Sample records for premixed calcium phosphate

  1. In Vivo Evaluation of an Injectable Premixed Radiopaque Calcium Phosphate Cement

    Directory of Open Access Journals (Sweden)

    Jonas Åberg

    2011-01-01

    Full Text Available In this work a radiopaque premixed calcium phosphate cement (pCPC has been developed and evaluated in vivo. Radiopacity was obtained by adding 0–40 % zirconia to the cement paste. The effects of zirconia on setting time, strength and radiopacity were evaluated. In the in vivo study a 2 by 3.5 mm cylindrical defect in a rat vertebrae was filled with either the pCPC, PMMA or bone chips. Nano-SPECT CT analysis was used to monitor osteoblast activity during bone regeneration. The study showed that by adding zirconia to the cement the setting time becomes longer and the compressive strength is reduced. All materials evaluated in the in vivo study filled the bone defect and there was a strong osteoblast activity at the injury site. In spite of the osteoblast activity, PMMA blocked bone healing and the bone chips group showed minimal new bone formation. At 12 weeks the pCPC was partially resorbed and replaced by new bone with good bone ingrowth. The radiopaque pCPC may be considered to be used for minimal invasive treatment of vertebral fractures since it has good handling, radiopacity and allows healing of cancellous bone in parallel with the resorption of the cement.

  2. Calcium phosphates for biomedical applications

    Directory of Open Access Journals (Sweden)

    Maria Canillas

    2017-05-01

    Full Text Available The history of calcium phosphates in the medicine field starts in 1769 when the first evidence of its existence in the bone tissue is discovered. Since then, the interest for calcium phosphates has increased among the scientific community. Their study has been developed in parallel with new advances in materials sciences, medicine or tissue engineering areas. Bone tissue engineering is the field where calcium phosphates have had a great importance. While the first bioceramics are selected according to bioinert, biocompatibility and mechanical properties with the aim to replace bone tissue damaged, calcium phosphates open the way to the bone tissue regeneration challenge. Nowadays, they are present in the majority of commercial products directed to repair or regenerate damaged bone tissue. Finally, in the last few decades, they have been suggested and studied as drug delivering devices and as vehicles of DNA and RNA for the future generation therapies.

  3. Calcium phosphates for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    Canillas, M.; Pena, P.; Aza, A.H. de; Rodriguez, M.A.

    2017-07-01

    The history of calcium phosphates in the medicine field starts in 1769 when the first evidence of its existence in the bone tissue is discovered. Since then, the interest for calcium phosphates has increased among the scientific community. Their study has been developed in parallel with new advances in materials sciences, medicine or tissue engineering areas. Bone tissue engineering is the field where calcium phosphates have had a great importance. While the first bioceramics are selected according to bioinert, biocompatibility and mechanical properties with the aim to replace bone tissue damaged, calcium phosphates open the way to the bone tissue regeneration challenge. Nowadays, they are present in the majority of commercial products directed to repair or regenerate damaged bone tissue. Finally, in the last few decades, they have been suggested and studied as drug delivering devices and as vehicles of DNA and RNA for the future generation therapies. (Author)

  4. Preparation of calcium phosphate paste

    International Nuclear Information System (INIS)

    Mohd Reusmaazran Yusof; Norzita Yaacob; Idris Besar; Che Seman Mahmood; Rusnah Mustafa

    2010-01-01

    Calcium phosphate paste were prepared by mixing between calcium sodium potassium phosphate, Ca 2 NaK (PO 4 ) 2 (CSPP) and monocalcium phosphate monohydrate, Ca(H 2 PO 4 ) 2 .H 2 O (MCPM). CSPP were obtained by reaction between calcium hydrogen phosphate (CaHPO 4 ), potassium carbonate (K 2 CO 3 ) and sodium carbonate (Na 2 CO 3 ) in solid state sintering process followed by quenching in air at 1000 degree Celsius. The paste was aging in simulated body fluid (SBF) for 0.5, 1, 3, 6, 12, 24, 48 hrs, 3, 7 and 14 days. The morphological investigation indicated the formation of apatite crystal were first growth after 24 hours. The obvious growth of apatite crystal was shown at 3 days. The obvious growth of apatite crystal was shown in 7 and 14 days indicated the prediction of paste would have rapid reaction with bone after implantation. (author)

  5. Application of Calcium Phosphate Materials in Dentistry

    Directory of Open Access Journals (Sweden)

    Jabr S. Al-Sanabani

    2013-01-01

    Full Text Available Calcium phosphate materials are similar to bone in composition and in having bioactive and osteoconductive properties. Calcium phosphate materials in different forms, as cements, composites, and coatings, are used in many medical and dental applications. This paper reviews the applications of these materials in dentistry. It presents a brief history, dental applications, and methods for improving their mechanical properties. Notable research is highlighted regarding (1 application of calcium phosphate into various fields in dentistry; (2 improving mechanical properties of calcium phosphate; (3 biomimetic process and functionally graded materials. This paper deals with most common types of the calcium phosphate materials such as hydroxyapatite and tricalcium phosphate which are currently used in dental and medical fields.

  6. Calcium phosphates: what is the evidence?

    Science.gov (United States)

    Larsson, Sune

    2010-03-01

    A number of different calcium phosphate compounds such as calcium phosphate cements and solid beta-tricalcium phosphate products have been introduced during the last decade. The chemical composition mimics the mineral phase of bone and as a result of this likeness, the materials seem to be remodeled as for normal bone through a cell-mediated process that involves osteoclastic activity. This is a major difference when compared with, for instance, calcium sulphate compounds that after implantation dissolve irrespective of the new bone formation rate. Calcium phosphates are highly biocompatible and in addition, they act as synthetic osteoconductive scaffolds after implantation in bone. When placed adjacent to bone, osteoid is formed directly on the surface of the calcium phosphate with no soft tissue interposed. Remodeling is slow and incomplete, but by adding more and larger pores, like in ultraporous beta-tricalcium phosphate, complete or nearly complete resorption can be achieved. The indications explored so far include filling of metaphyseal fracture voids or bone cysts, a volume expander in conjunction with inductive products, and as a carrier for various growth factors and antibiotics. Calcium phosphate compounds such as calcium phosphate cement and beta-tricalcium phosphate will most certainly be part of the future armamentarium when dealing with fracture treatment. It is reasonable to believe that we have so far only seen the beginning when it comes to clinical applications.

  7. Synthesis and characterization of porous calcium phosphate

    International Nuclear Information System (INIS)

    Granados C, F.; Serrano G, J.; Bonifacio M, J.

    2007-01-01

    The porous calcium phosphate was prepared by the continuous precipitation method using Ca(NO 3 ) 2 .4H 2 O and NH 4 H 2 PO 4 salts. The synthesized material was structurally and superficially characterized using the XRD, BET, IR TGA and SEM techniques. The obtained inorganic material was identified as calcium phosphate that presents a great specific area for what can be efficiently used as adsorbent material for adsorption studies in the radioactive wastes treatment present in aqueous solution. (Author)

  8. Kinetics of strontium sorption in calcium phosphate

    International Nuclear Information System (INIS)

    Bacic, S.; Komarov, V.F.; Vukovic, Z.

    1989-01-01

    Kinetics of strontium sorption by highly dispersed solids: tricalcium phosphate (Ca 3 (PO 4 ) 2 , TCP) and hydroxyapatite (Ca 5 (PO 4 ) 3 )H, HAP) were investigated. Analysis of sorption data was made taking into consideration composition and morphology of ultra micro particles. Conclusion is that the isomorphous strontium impurity is structurally sensitive element for calcium phosphate. It was determined that the beginning of strontium desorption corresponds to the beginning of transformation of the TCP - HAP (author)

  9. Calcium phosphate saturation in seawater around the Andaman Island

    Digital Repository Service at National Institute of Oceanography (India)

    Naik, S.; Reddy, C.V.G.

    Ionic product (IP) of calcium phosphate is calculated at some stations around Andaman Island. The depthwise variations of the ionic product of calcium phosphate seem to follow a normal trend with maximum saturation value between 100 to 200 m. Using...

  10. Electrosprayed calcium phosphate coatings for biomedical purposes.

    NARCIS (Netherlands)

    Leeuwenburgh, S.C.G.

    2006-01-01

    In this thesis, the suitability of the Electrostatic Spray Deposition (ESD) technique was studied for biomedical purposes, i.e., deposition of calcium phosphate (CaP) coatings onto titanium substrates. Using ESD, which is a simple and cheap deposition method for inorganic and organic coatings, it

  11. Serum Calcium, Inorganic Phosphates and some Haematological ...

    African Journals Online (AJOL)

    Objectives: Sickle cell disease has long been associated with bone deformities and pain. Mineral salts such as calcium and inorganic phosphate are critical in bone formation and metabolism. This investigation was designed to study the serum concentration of these minerals as well as some haematological parameters in ...

  12. Calcium phosphate ceramics in drug delivery

    Science.gov (United States)

    Bose, Susmita; Tarafder, Solaiman; Edgington, Joe; Bandyopadhyay, Amit

    2011-04-01

    Calcium phosphate (CaP) particulates, cements and scaffolds have attracted significant interest as drug delivery vehicles. CaP systems, including both hydroxyapaptite and tricalcium phosphates, possess variable stoichiometry, functionality and dissolution properties which make them suitable for cellular delivery. Their chemical similarity to bone and thus biocompatibility, as well as variable surface charge density contribute to their controlled release properties. Among specific research areas, nanoparticle size, morphology, surface area due to porosity, and chemistry controlled release kinetics are the most active. This article discusses CaP systems in their particulate, cements, and scaffold forms for drug, protein, and growth factor delivery toward orthopedic and dental applications.

  13. Electrosprayed calcium phosphate coatings for biomedical purposes.

    OpenAIRE

    Leeuwenburgh, S.C.G.

    2006-01-01

    In this thesis, the suitability of the Electrostatic Spray Deposition (ESD) technique was studied for biomedical purposes, i.e., deposition of calcium phosphate (CaP) coatings onto titanium substrates. Using ESD, which is a simple and cheap deposition method for inorganic and organic coatings, it was possible to obtain thin CaP layers with an extremely wide range of chemical and morphological characteristics. Various CaP phases and phase mixtures were deposited and a broad diversity of coatin...

  14. Calcium phosphate cement scaffolds with PLGA fibers.

    Science.gov (United States)

    Vasconcellos, Letícia Araújo; dos Santos, Luís Alberto

    2013-04-01

    The use of calcium phosphate-based biomaterials has revolutionized current orthopedics and dentistry in repairing damaged parts of the skeletal system. Among those biomaterials, the cement made of hydraulic grip calcium phosphate has attracted great interest due to its biocompatibility and hardening "in situ". However, these cements have low mechanical strength compared with the bones of the human body. In the present work, we have studied the attainment of calcium phosphate cement powders and their addition to poly (co-glycolide) (PLGA) fibers to increase mechanical properties of those cements. We have used a new method that obtains fibers by dripping different reagents. PLGA fibers were frozen after lyophilized. With this new method, which was patented, it was possible to obtain fibers and reinforcing matrix which furthered the increase of mechanical properties, thus allowing the attainment of more resistant materials. The obtained materials were used in the construction of composites and scaffolds for tissue growth, keeping a higher mechanical integrity. Copyright © 2012 Elsevier B.V. All rights reserved.

  15. Calcium phosphate saturation in the western Bay of Bengal

    Digital Repository Service at National Institute of Oceanography (India)

    Naik, S.; Reddy, C.V.G.

    Temperature, inorganic phosphate concentration and pH seem to be the major factors influencing the degree of saturation of calcium phosphate in sea water. Two water regions can be demarcated in the study area based on the saturation patterns...

  16. Preparation and characterization of bioceramics produced from calcium phosphate cements

    Energy Technology Data Exchange (ETDEWEB)

    Andriotis, O.; Katsamenis, O.L. [Department of Materials Science, University of Patras, 26504, Patras (Greece); Mouzakis, D.E. [Technological Educational Institute of Larisa, Department of Mechanical Engineering, T.E.I of Larissa, 411 10, Larissa (Greece); Bouropoulos, N. [Foundation for Research and Technology, Hellas, Institute of Chemical Engineering and High Temperature Chemical Processes, FORTH/ICE-HT, P.O. Box 1414, 26504 Rio Patras (Greece)

    2010-03-15

    The present work reports a method for preparing calcium phosphate ceramics by calcination of calcium phosphate cements composed mainly of calcium deficient hydroxyapatite (CDHA). It was found that hardened cements calcinied at temperatures from to 600 to 1300 C were transformed to tricalcium phosphates. Moreover the compressive strength was determined and porosity was estimated as a function of the calcination temperature. (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  17. Preparation of Porous Calcium Phosphate Bioceramic

    Institute of Scientific and Technical Information of China (English)

    2005-01-01

    Porous calcium phosphate ceramics were prepared by slip casting and molding method respectively. By these two different methods, different microstructures can be got. By slip casting method, the pore size was 100- 350μm and 20- 80μm; pores were opened, interconnected and ball-like; the grain size was 2- 4 μm.By molding method, the pore size was 100-500 μm and 1-10μm; the grain size was 2-8μm. By slip casting method regular and interconnected pores can be got. By molding method the porosity and strength can be adjusted easily.

  18. Hybrid calcium phosphate coatings for implants

    Science.gov (United States)

    Malchikhina, Alena I.; Shesterikov, Evgeny V.; Bolbasov, Evgeny N.; Ignatov, Viktor P.; Tverdokhlebov, Sergei I.

    2016-08-01

    Monophasic biomaterials cannot provide all the necessary functions of bones or other calcined tissues. It is necessary to create for cancer patients the multiphase materials with the structure and composition simulating the natural bone. Such materials are classified as hybrid, obtained by a combination of chemically different components. The paper presents the physical, chemical and biological studies of coatings produced by hybrid technologies (HT), which combine primer layer and calcium phosphate (CaP) coating. The first HT type combines the method of vacuum arc titanium primer layer deposition on a stainless steel substrate with the following micro-arc oxidation (MAO) in phosphoric acid solution with addition of calcium compounds to achieve high supersaturated state. MAO CaP coatings feature high porosity (2-8%, pore size 5-7 µm) and surface morphology with the thickness greater than 5 µm. The thickness of Ti primer layer is 5-40 µm. Amorphous MAO CaP coating micro-hardness was measured at maximum normal load Fmax = 300 mN. It was 3.1 ± 0.8 GPa, surface layer elasticity modulus E = 110 ± 20 GPa, roughness Ra = 0.9 ± 0.1 µm, Rz = 7.5 ± 0.2 µm, which is less than the titanium primer layer roughness. Hybrid MAO CaP coating is biocompatible, able to form calcium phosphates from supersaturated body fluid (SBF) solution and also stimulates osteoinduction processes. The second HT type includes the oxide layer formation by thermal oxidation and then CaP target radio frequency magnetron sputtering (RFMS). Oxide-RFMS CaP coating is a thin dense coating with good adhesion to the substrate material, which can be used for metal implants. The RFMS CaP coating has thickness 1.6 ± 0.1 µm and consists of main target elements calcium and phosphorus and Ca/P ratio 2.4. The second HT type can form calcium phosphates from SBF solution. In vivo study shows that hybrid RFMS CaP coating is biocompatible and produces fibrointegration processes.

  19. Development of a fully injectable calcium phosphate cement

    Indian Academy of Sciences (India)

    Permanent link: https://www.ias.ac.in/article/fulltext/boms/026/04/0415-0422. Keywords. Calcium phosphate cements; hydroxyapatite; bioceramics; bone substitute; orthopedic; dental. Abstract. A study on the development of a fully injectable calcium phosphate cement for orthopedic and dental applications is presented.

  20. Properties of calcium silicate-monobasic calcium phosphate materials for endodontics containing tantalum pentoxide and zirconium oxide.

    Science.gov (United States)

    Zamparini, Fausto; Siboni, Francesco; Prati, Carlo; Taddei, Paola; Gandolfi, Maria Giovanna

    2018-05-08

    The aim of the study was to evaluate chemical-physical properties and apatite-forming ability of three premixed calcium silicate materials containing monobasic calcium phosphate (CaH 4 P 2 O 8 ) bioceramic, tantalum pentoxide and zirconium oxide, recently marketed for endodontics (TotalFill BC-Sealer, BC-RRM-Paste, BC-RRM-Putty). Microchemical and micromorphological analyses, radiopacity, initial and final setting times, calcium release and alkalising activity were tested. The nucleation of calcium phosphates (CaPs) and/or apatite after 28 days ageing was evaluated by ESEM-EDX and micro-Raman spectroscopy. BC-Sealer and BC-RRM-Paste showed similar initial (23 h), prolonged final (52 h) setting times and good radiopacity (> 7 mm Al); BC-RRM-Putty showed fast initial (2 h) and final setting times (27 h) and excellent radiopacity (> 9 mm Al). All materials induced a marked alkalisation (pH 11-12) up to 28 days and showed the release of calcium ions throughout the entire test period (cumulative calcium release 641-806 ppm). After 28 days ageing, a well-distributed mineral layer was present on all samples surface; EDX demonstrated relevant calcium and phosphorous peaks. B-type carbonated apatite and calcite deposits were identified by micro-Raman spectroscopy on all the 28-day-aged samples; the deposit thickness was higher on BC-RRM-Paste and BC-RRM-Putty, in agreement with calcium release data. These materials met the required chemical and physical standards and released biologically relevant ions. The CaSi-CaH 4 P 2 O 8 system present in the materials provided Ca and OH ions release with marked abilities to nucleate a layer of B-type carbonated apatite favoured/accelerated by the bioceramic presence. The ability to nucleate apatite may lead many clinical advantages: In orthograde endodontics, it may improve the sealing ability by the deposition of CaPs at the material-root dentine interface, and in endodontic surgery, it could promote bone and

  1. Preparation and Characterization of Porous Calcium Phosphate Bioceramics

    Institute of Scientific and Technical Information of China (English)

    Honglian Dai; Xinyu Wang; Yinchao Han; Xin Jiang; Shipu Li

    2011-01-01

    β-tricalcium phosphate (β-TCP) powder and Na2O-CaO-MgO-P2O5 glass binder were synthesized and mixed, and then the biodegradable porous calcium phosphate ceramics were successfully prepared by foaming and sintering at 850℃. The as-prepared ceramics possess a high porosity with partial three-dimension interconnected macro- and micro-pores. As in vitro experiment testified, the calcium phosphate ceramics (CPCs) has good degradability.

  2. Effect of Casein Phosphopeptide-Amorphous Calcium Phosphate and Three Calcium Phosphate on Enamel Microhardness.

    Science.gov (United States)

    Haghgou, En Hr; Haghgoo, Roza; Roholahi, Mohamad R; Ghorbani, Zahra

    2017-07-01

    This study aims to investigate the effect of casein phos-phopeptide-amorphous calcium phosphate and three calcium phosphate (CPP-ACP and TCP) on increasing the microhardness of human enamel after induction of erosion. A total of 26 healthy human-impacted third molar teeth were chosen, and their hardness measured using a microhardness testing machine. The samples were immersed in Coca Cola (pH = 4.7) for 8 minutes. Then, micro-hardness was measured again, and these samples were randomly divided into four groups (two control groups and two experimental groups). (1) Negative control group: Artificial saliva was used for 10 minutes, (2) positive control group: Fluoride gel was used for 10 minutes, (3) β-TCP group: TCP was used for 10 minutes, (4) CCP-ACP group: CCP-ACP was used for 10 minutes. The final microhardness of those samples was measured, and the changes in microhardness of teeth within group and between groups were analyzed using the paired and analysis of variance tests respectively. Results were considered statistically significant at a level of p < 0.05. No significant difference was observed in microhard-ness between CPP-ACP group and TCP group (p = 0.368) during the time microhardness significantly dropped after soaking in soda. Casein phosphopeptide-amorphous calcium phosphate and TCP increased the microhardness of teeth. The increase in hardness in the TCP group was higher than in the CPP-ACP group, but this difference was not significant (p = 0.36). Casein phosphopeptide-amorphous calcium phosphate and TCP can affect the remineralization of erosive lesions.

  3. Fourier transform Raman spectroscopy of synthetic and biological calcium phosphates.

    Science.gov (United States)

    Sauer, G R; Zunic, W B; Durig, J R; Wuthier, R E

    1994-05-01

    Fourier-transform (FT) Raman spectroscopy was used to characterize the organic and mineral components of biological and synthetic calcium phosphate minerals. Raman spectroscopy provides information on biological minerals that is complimentary to more widely used infrared methodologies as some infrared-inactive vibrational modes are Raman-active. The application of FT-Raman technology has, for the first time, enabled the problems of high sample fluorescence and low signal-to-noise that are inherent in calcified tissues to be overcome. Raman spectra of calcium phosphates are dominated by a very strong band near 960 cm-1 that arises from the symmetric stretching mode (v1) of the phosphate group. Other Raman-active phosphate vibrational bands are seen at approximately 1075 (v3), 590 (v4), and 435 cm-1 (v2). Minerals containing acidic phosphate groups show additional vibrational modes. The different calcium phosphate mineral phases can be distinguished from one another by the relative positions and shapes of these bands in the Raman spectra. FT-Raman spectra of nascent, nonmineralized matrix vesicles (MV) show a distinct absence of the phosphate v1 band even though these structures are rich in calcium and phosphate. Similar results were seen with milk casein and synthetic Ca-phosphatidyl-serine-PO4 complexes. Hence, the phosphate and/or acidic phosphate ions in these noncrystalline biological calcium phosphates is in a molecular environment that differs from that in synthetic amorphous calcium phosphate. In MV, the first distinct mineral phase to form contained acidic phosphate bands similar to those seen in octacalcium phosphate. The mineral phase present in fully mineralized MV was much more apatitic, resembling that found in bones and teeth.(ABSTRACT TRUNCATED AT 250 WORDS)

  4. Removal of phosphate from solution by adsorption and precipitation of calcium phosphate onto monohydrocalcite.

    Science.gov (United States)

    Yagi, Shintaro; Fukushi, Keisuke

    2012-10-15

    The sorption behavior and mechanism of phosphate on monohydrocalcite (CaCO(3)·H(2)O: MHC) were examined using batch sorption experiments as a function of phosphate concentrations, ionic strengths, temperatures, and reaction times. The mode of PO(4) sorption is divisible into three processes depending on the phosphate loading. At low phosphate concentrations, phosphate is removed by coprecipitation of phosphate during the transformation of MHC to calcite. The sorption mode at the low-to-moderate phosphate concentrations is most likely an adsorption process because the sorption isotherm at the conditions can be fitted reasonably with the Langmuir equation. The rapid sorption kinetics at the conditions is also consistent with the adsorption reaction. The adsorption of phosphate on MHC depends strongly on ionic strength, but slightly on temperature. The maximum adsorption capacities of MHC obtained from the regression of the experimental data to the Langmuir equation are higher than those reported for stable calcium carbonate (calcite or aragonite) in any conditions. At high phosphate concentrations, the amount of sorption deviates from the Langmuir isotherm, which can fit the low-to-moderate phosphate concentrations. Speciation-saturation analyses of the reacted solutions at the conditions indicated that the solution compositions which deviate from the Langmuir equation are supersaturated with respect to a certain calcium phosphate. The obtained calcium phosphate is most likely amorphous calcium phosphate (Ca(3)(PO(4))(2)·xH(2)O). The formation of the calcium phosphate depends strongly on ionic strength, temperature, and reaction times. The solubility of MHC is higher than calcite and aragonite because of its metastability. Therefore, the higher solubility of MHC facilitates the formation of the calcium phosphates more than with calcite and aragonite. Copyright © 2012 Elsevier Inc. All rights reserved.

  5. Role of magnesium on the biomimetic deposition of calcium phosphate

    Science.gov (United States)

    Sarma, Bimal K.; Sarma, Bikash

    2016-10-01

    Biomimetic depositions of calcium phosphate (CaP) are carried out using simulated body fluid (SBF), calcifying solution and newly developed magnesium containing calcifying solution. Calcium phosphate has a rich phase diagram and is well known for its excellent biocompatibility and bioactivity. The most common phase is hydroxyapatite (HAp), an integral component of human bone and tooth, widely used in orthopedic and dental applications. In addition, calcium phosphate nanoparticles show promise for the targeted drug delivery. The doping of calcium phosphate by magnesium, zinc, strontium etc. can change the protein uptake by CaP nanocrystals. This work describes the role of magnesium on the nucleation and growth of CaP on Ti and its oxide substrates. X-ray diffraction studies confirm formation of HAp nanocrystals which closely resemble the structure of bone apatite when grown using SBF and calcifying solution. It has been observed that magnesium plays crucial role in the nucleation and growth of calcium phosphate. A low magnesium level enhances the crystallinity of HAp while higher magnesium content leads to the formation of amorphous calcium phosphate (ACP) phase. Interestingly, the deposition of ACP phase is rapid when magnesium ion concentration in the solution is 40% of calcium plus magnesium ions concentration. Moreover, high magnesium content alters the morphology of CaP films.

  6. A novel biphasic calcium phosphate derived from fish otoliths

    Science.gov (United States)

    Montañez-Supelano, N. D.; Sandoval-Amador, A.; Estupiñan-Durán, H. A.; Y Peña-Ballesteros, D.

    2017-12-01

    Calcium phosphates are bioceramics that have been widely used as bone substitutes because they encourage the formation of bone on their surface and can improve the healing of the bone. Hydroxyapatite HA (calcium/phosphorus ratio of 1.67) and tricalcium phosphate TCP (calcium/phosphorus ratio of 1.50) are the most common calcium phosphates. Natural materials have begun to be tested to make HA or TCP such as shells of cardiidae (family of mollusks) and eggshells. The calcium phosphate obtained has a high ability to precipitate apatite. In this work, the mixed phase ceramic of beta-Tri-calcium phosphate / hydroxyapatite (β-TCP/HA) was synthesized by aqueous precipitation from fish otoliths, which are monomineralic species composed of aragonite. Otoliths of the specie Plagioscion squamosissimus, commonly called the river croaker, were used. Techniques such as DRX, Raman spectroscopy and SEM-EDS were used to characterize the raw material and the obtained material. X-ray diffraction analysis revealed the presence of two crystalline phases of calcium phosphates with 86.2% crystallinity. SEM micrographs showed agglomeration of particles with porous structure and submicron particle sizes.

  7. Development of a fully injectable calcium phosphate cement for ...

    Indian Academy of Sciences (India)

    Unknown

    2003-01-27

    Jan 27, 2003 ... excellent alloplastic material for osseous augmentation because of the ... and basic calcium phosphate compounds on wetting with an aqueous ... ment of acute fracture of the radius through percutaneous administration of ...

  8. Biomimetic calcium phosphate coatings on recombinant spider silk fibres

    NARCIS (Netherlands)

    Yang, Liang; Hedhammar, My; Blom, Tobias; Leifer, Klaus; Johansson, Jan; Habibovic, Pamela; van Blitterswijk, Clemens

    2010-01-01

    Calcium phosphate ceramic coatings, applied on surfaces of metallic and polymeric biomaterials, can improve their performance in bone repair and regeneration. Spider silk is biocompatible, strong and elastic, and hence an attractive biomaterial for applications in connective tissue repair. Recently,

  9. A review paper on biomimetic calcium phosphate coatings

    NARCIS (Netherlands)

    Lin, X.; de Groot, K.; Wang, D.; Hu, Q.; Wismeijer, D.; Liu, Y.

    2015-01-01

    Biomimetic calcium phosphate coatings have been developed for bone regeneration and repair because of their biocompatibility, osteoconductivity, and easy preparation. They can be rendered osteoinductive by incorporating an osteogenic agent, such as bone morphogenetic protein 2 (BMP-2), into the

  10. Chemistry Misconceptions Associated with Understanding Calcium and Phosphate Homeostasis

    Science.gov (United States)

    Cliff, William H.

    2009-01-01

    Successful learning of many aspects in physiology depends on a meaningful understanding of fundamental chemistry concepts. Two conceptual diagnostic questions measured student understanding of the chemical equilibrium underlying calcium and phosphate homeostasis. One question assessed the ability to predict the change in phosphate concentration…

  11. Effect of humic substances on the precipitation of calcium phosphate

    Institute of Scientific and Technical Information of China (English)

    SONG Yong-hui; Hermann H. HAHN; Erhard HOFFMANN; Peter G. WEIDLER

    2006-01-01

    For phosphorus (P) recovery from wastewater, the effect of humic substances (HS) on the precipitation of calcium phosphate was studied. Batch experiments of calcium phosphate precipitation were undertaken with synthetic water that contained 20 mg/L phosphate (as P) and 20 mg/L HS (as dissolved organic carbon, DOC) at a constant pH value in the range of 8.0-10.0. The concentration variations of phosphate, calcium (Ca) and HS were measured in the precipitation process; the crystalline state and compositions of the precipitates were analysed by powder X-ray diffraction (XRD) and chemical methods, respectively. It showed that at solution pH 8.0, the precipitation rate and removal efficiency of phosphate were greatly reduced by HS, but at solution pH ≥9.0,the effect of HS was very small. The Ca consumption for the precipitation of phosphate increased when HS was added; HS was also removed from solution with the precipitation of calcium phosphate. At solution pH 8.0 and HS concentrations ≤ 3.5 mg/L, and at pH ≥ 9.0 and HS concentrations ≤ 10 mg/L, the final precipitates were proved to be hydroxyapatite (HAP) by XRD. The increases of solution pH value and initial Ca/P ratio helped reduce the influence of HS on the precipitation of phosphate.

  12. Characterization of cement calcium phosphate for use dental

    International Nuclear Information System (INIS)

    Barros, C.M.B.; Oliveira, S.V.; Silva, M.C.; Marques, J.B.; Fook, M.V.L.

    2011-01-01

    Calcium phosphates are interesting biological and medical attention due to its occurrence in different animal species and humans. Ceramics based on calcium phosphate in the form of implants or porous particulate materials, have proven to be suitable replacements for bone tissue when they are only subjected to small mechanical stresses. Was obtained research laboratory DEMA/UFCG a calcium phosphate phase. The goal is to characterize the material by X-ray diffraction (XRD) in order to analyze what the phases and infrared spectroscopy (FTIR) to identify the absorption bands of the bonding characteristic. Was identified by XRD phase present in the sample is hydroxyapatite Ca/P 1.67. In infrared spectroscopy has absorption bands characteristic of the phosphate group at 1032 cm1 region. (author)

  13. Investigation of calcium phosphate coatings for biomedical applications

    International Nuclear Information System (INIS)

    Yusof Abdullah; Idris Besar; Muhammad Jamal Md Isa; Mohamad Abd Razak; Hyzan Mohd Yusof

    1999-01-01

    Calcium phosphate is the main constituent of our bone and tooth minerals. The use of this bioactive material for coating implant such as artificial joint prosthesis, therefore, can promote biological fixation and enhance biocompatibility. Our initial work has been focused on the evaluation of experimental conditions of coating preparation and the effects of post-deposition calcium phosphate coatings on stainless steel substrates. The coating layers were produced by the precipitation technique and coatings were carried out in sol-gel by the dipping method. For comparison purposes a wet method was used to obtain a fine calcium phosphate ceramic powder for fabrication of microcrystal suspension used as a coating material. Scanning electron microscopy (SEM), energy dispersive microanalysis (EDS), energy dispersive x-ray fluorescence (EDXRF) and x-ray diffraction (XRD) were used to characterise the morphology, chemical composition and structure of the coatings. The results showed that the dip coating of stainless steel substrates using viscous solutions lead to the formation of porous calcium phosphate layers. These results suggested that fabrication of bioactive calcium phosphate coatings using this route offers significant advantages over the currently used methods due to considerably lower temperature process involved and may produce better result for substrates with complex shapes

  14. Calcium phosphate bioceramics prepared from wet chemically precipitated powders

    Directory of Open Access Journals (Sweden)

    Kristine Salma

    2010-03-01

    Full Text Available In this work calcium phosphates were synthesized by modified wet chemical precipitation route. Contrary to the conventional chemical precipitation route calcium hydroxide was homogenized with planetary mill. Milling calcium oxide and water in planetary ball mill as a first step of synthesis provides a highly dispersed calcium hydroxide suspension. The aim of this work was to study the influence of main processing parameters of wet chemical precipitation synthesis product and to control the morphology, phase and functional group composition and, consequently, thermal stability and microstructure of calcium phosphate bioceramics after thermal treatment. The results showed that it is possible to obtain calcium phosphates with different and reproducible phase compositions after thermal processing (hydroxyapatite [HAp], β-tricalcium phosphate [β-TCP] and HAp/β-TCP by modified wet-chemical precipitation route. The β-TCP phase content in sintered bioceramics samples is found to be highly dependent on the changes in technological parameters and it can be controlled with ending pH, synthesis temperature and thermal treatment. Pure, crystalline and highly thermally stable (up to 1300°C HAp bioceramics with homogenous grainy microstructure, grain size up to 200–250 nm and high open porosity can be successfully obtained by powder synthesized at elevated synthesis temperature of 70°C and stabilizing ending pH at 9.

  15. Calcium phosphate-based coatings on titanium and its alloys.

    Science.gov (United States)

    Narayanan, R; Seshadri, S K; Kwon, T Y; Kim, K H

    2008-04-01

    Use of titanium as biomaterial is possible because of its very favorable biocompatibility with living tissue. Titanium implants having calcium phosphate coatings on their surface show good fixation to the bone. This review covers briefly the requirements of typical biomaterials and narrowly focuses on the works on titanium. Calcium phosphate ceramics for use in implants are introduced and various methods of producing calcium phosphate coating on titanium substrates are elaborated. Advantages and disadvantages of each type of coating from the view point of process simplicity, cost-effectiveness, stability of the coatings, coating integration with the bone, cell behavior, and so forth are highlighted. Taking into account all these factors, the efficient method(s) of producing these coatings are indicated finally.

  16. Renal Control of Calcium, Phosphate, and Magnesium Homeostasis

    Science.gov (United States)

    Chonchol, Michel; Levi, Moshe

    2015-01-01

    Calcium, phosphate, and magnesium are multivalent cations that are important for many biologic and cellular functions. The kidneys play a central role in the homeostasis of these ions. Gastrointestinal absorption is balanced by renal excretion. When body stores of these ions decline significantly, gastrointestinal absorption, bone resorption, and renal tubular reabsorption increase to normalize their levels. Renal regulation of these ions occurs through glomerular filtration and tubular reabsorption and/or secretion and is therefore an important determinant of plasma ion concentration. Under physiologic conditions, the whole body balance of calcium, phosphate, and magnesium is maintained by fine adjustments of urinary excretion to equal the net intake. This review discusses how calcium, phosphate, and magnesium are handled by the kidneys. PMID:25287933

  17. Preparation and Characterization of Apatitic Biphasic Calcium Phosphate

    International Nuclear Information System (INIS)

    Thin Thin Nwe; Kyaw Naing; Khin Mar Tun; Nyunt Wynn

    2005-09-01

    The apatitic biphasic calcium phosphate (ABcp) consisting of hydroxyapatite (HA) and -tricalcium phosphate ( -Tcp) has been prepared by precipitation technique using slaked lime and orthophosphoric acid. The X-ray diffraction analysis of the product I (hydroxyapatite) revealed that ABcp was partially crystalline state. However, on heating at 800 C for 8 hrs, XRD pattern indicated a perfectly crystalline form of ABcp. This observation was supported by FT-IR measurement. The change in morphology regarding in the functional nature was infered by the shift in the FT-IR frequency. The optimization of the apatitic biphasic calcium phosphate was done by the variation of disodium hydrogen phosphate concentration, setting time, hardening time as well as compressive strength. The perpared cement may be used as an artificial substitution bone

  18. Optimization of calcium phosphate fine ceramic powders preparation

    Science.gov (United States)

    Sezanova, K.; Tepavitcharova, S.; Rabadjieva, D.; Gergulova, R.; Ilieva, R.

    2013-12-01

    The effect of biomimetic synthesis method, reaction medium and further precursor treatments on the chemical and phase composition, crystal size and morphology of calcium phosphates was examined. Nanosized calcium phosphate precursors were biomimetically precipitated by the method of continuous precipitation in three types of reaction media at pH 8: (i) SBF as an inorganic electrolyte system; (ii) organic (glycerine) modified SBF (volume ratio of 1:1); (iii) polymer (10 g/l xanthan gum or 10 g/l guar gum) modified SBF (volume ratio of 1:1). After maturation (24 h) the samples were lyophilized, calcinated at 300°C for 3 hours, and washed with water, followed by new gelation, lyophilization and step-wise (200, 400, 600, 800, and 1000°C, each for 3 hours) sintering. The reaction medium influenced the chemical composition and particle size but not the morphology of the calcium phosphate powders. In all studied cases bi-phase calcium phosphate fine powders with well-shaped spherical grains, consisting of β-tricalcium phosphate (β-TCP) and hydroxyapatite (HA) with a Ca/P ratio of 1.3 - 1.6 were obtained. The SBF modifiers decreased the particle size of the product in the sequence guar gum ˜ xanthan gum < glycerin < SBF medium.

  19. Relative biological activity of amorphous calcium and calcium-magnesium phosphates

    International Nuclear Information System (INIS)

    Silina, E.N.; Kunitsa, T.N.; Shuslikova, E.S.; Griggs, J.; Levchenko, L.V.; Karjaubaeva, R.A.; Sinyayev, V.A.

    2005-01-01

    Three amorphous calcium and calcium-magnesium phosphates that are close on composition to mineral basis of the bone tissues are compared on bioactivity in the given article. Properties of the hydrated substances produced from water solutions and their derivations, which are formed due to thermal treatment, are discussed here. As a detector of bioactivity was used microbial culture E-Coli. [author

  20. The effect of calcium phosphate-containing desensitizing agent on ...

    African Journals Online (AJOL)

    Objective: The aim of this study was to investigate the effect of calcium phosphate containing desensitizing pretreatments on the microtensile bond strength (MTBS) and microleakage of the multimode adhesive agent to dentin. Materials and Methods: In this study, twelve noncarious, freshly extracted human third molar teeth ...

  1. In vitro study on biomineralization of biphasic calcium phosphate ...

    Indian Academy of Sciences (India)

    In this study, we report the preparation of a bone graft material, having cylindrical shape, containing biphasic calcium phosphate (BCP), gelatin (G), chitosan (C) and Terminalia chebula (TC) extract. TC extract was used as a crosslinker that gives stability to bone graft when it is placed in SBF. The graft was stable in the SBF ...

  2. Injectable biphasic calcium phosphate cements as a potential bone substitute

    NARCIS (Netherlands)

    Sariibrahimoglu, K.; Wolke, J.G.C.; Leeuwenburgh, S.C.G.; Yubao, L.; Jansen, J.A.

    2014-01-01

    Apatitic calcium phosphate cements (CPCs) have been widely used as bone grafts due to their excellent osteoconductive properties, but the degradation properties are insufficient to stimulate bone healing in large bone defects. A novel approach to overcome the lack of degradability of apatitic CPC

  3. Structure and properties of silver-doped calcium phosphate ...

    Indian Academy of Sciences (India)

    Abstract. Stable and antimicrobial silver-doped calcium phosphate nanopowders were synthesized using sol–gel .... ical morphology of HAP/Ag nanoparticles with particle size ..... [40] Buckley J J, Lee A F, Olivi L and Wilson K 2010 J. Mater.

  4. Phase stability of silver particles embedded calcium phosphate ...

    Indian Academy of Sciences (India)

    Abstract. In this paper, we report the compositional variation-dependent phase stability of hydroxyapatite ... material along with other calcium phosphate bioceramics.3–5 ... Model U-3310). ... recorded using a Field Emissio scanning electron microscope .... the colour change of the silver-doped samples only after sin-.

  5. Osteoinduction of calcium phosphate biomaterials in small animals

    International Nuclear Information System (INIS)

    Cheng, Lijia; Shi, Yujun; Ye, Feng; Bu, Hong

    2013-01-01

    Although osteoinduction mechanism of calcium phosphate (CP) ceramics is still unclear, several essential properties have been reported, such as chemical composition, pore size and porosity, etc. In this study, calcium phosphate powder (Ca 3 (PO 4 ) 2 , CaP, group 1), biphasic calcium phosphate ceramic powder (BCP, group 2), and intact BCP rods (group 3) were implanted into leg muscles of mice and dorsal muscles of rabbits. One month and three months after implantation, samples were harvested for biological and histological analysis. New bone tissues were observed in 10/10 samples in group 1, 3/10 samples in group 2, and 9/10 samples in group 3 at 3rd month in mice, but not in rabbits. In vitro, human mesenchymal stem cells (hMSCs) were cultured with trace CaP and BCP powder, and osteogenic differentiation was observed at day 7. Our results suggested that chemical composition is the prerequisite in osteoinduction, and pore structure would contribute to more bone formation. - Highlights: ► Intrinsic osteoinduction of calcium phosphate biomaterials was observed implanted in muscles of mice. ► Biomaterials powder also has osteoinduction property. ► Osteogenic genes and protein could be detected by RT-PCR and Western blot in implanted biomaterials. ► Osteogenic phenomenon could be observed by electron microscopy. ► The chemical composition is the prerequisite in osteoinduction, and pore structure would contribute to more bone formation

  6. Biomimetic calcium phosphate coatings on recombinant spider silk fibres

    Energy Technology Data Exchange (ETDEWEB)

    Yang Liang; Habibovic, Pamela; Van Blitterswijk, Clemens A [Department of Tissue Regeneration, University of Twente, PO Box 217, 7500 AE Enschede (Netherlands); Hedhammar, My; Johansson, Jan [Department of Anatomy, Physiology and Biochemistry, Swedish University of Agricultural Sciences, the Biomedical Centre, Box 575, 751 23 Uppsala (Sweden); Blom, Tobias; Leifer, Klaus [Department of Engineering Sciences, Uppsala University, Box 534, S-751 21 Uppsala (Sweden)

    2010-08-01

    Calcium phosphate ceramic coatings, applied on surfaces of metallic and polymeric biomaterials, can improve their performance in bone repair and regeneration. Spider silk is biocompatible, strong and elastic, and hence an attractive biomaterial for applications in connective tissue repair. Recently, artificial spider silk, with mechanical and structural characteristics similar to those of native spider silk, has been produced from recombinant minispidroins. In the present study, supersaturated simulated body fluid was used to deposit calcium phosphate coatings on recombinant spider silk fibres. The mineralization process was followed in time using scanning electron microscopy equipped with an energy dispersive x-ray (EDX) detector and Raman spectroscope. Focused ion beam technology was used to produce a cross section of a coated fibre, which was further analysed by EDX. Preliminary in vitro experiments using a culture of bone marrow-derived human mesenchymal stem cells (hMSCs) on coated fibres were also performed. This study showed that recombinant spider silk fibres were successfully coated with a homogeneous and thick crystalline calcium phosphate layer. In the course of the mineralization process from modified simulated body fluid, sodium chloride crystals were first deposited on the silk surface, followed by the deposition of a calcium phosphate layer. The coated silk fibres supported the attachment and growth of hMSCs.

  7. Evaluation of Serum Calcium and Inorganic Phosphate Levels in ...

    African Journals Online (AJOL)

    The importance of calcium and inorganic phosphate in pregnancy cannot be overemphasized. Their adequacy or otherwise amongst pregnant and lactating women in Enugu metropolis receiving their routine antenatal supplements was the focus of this study. Two hundred subjects (forty in each trimester; forty lactating and ...

  8. Atomic structure of intracellular amorphous calcium phosphate deposits.

    Science.gov (United States)

    Betts, F; Blumenthal, N C; Posner, A S; Becker, G L; Lehninger, A L

    1975-06-01

    The radial distribution function calculated from x-ray diffraction of mineralized cytoplasmic structures isolated from the hepatopancreas of the blue crab (Callinectes sapidus) is very similar to that previously found for synthetic amorphous calcium phosphate. Both types of mineral apparently have only short-range atomic order, represented as a neutral ion cluster of about 10 A in longest dimension, whose probable composition is expressed by the formula Ca9(PO4)6. The minor differences observed are attributed to the presence in the biological mineral of significant amounts of Mg-2+ and ATP. Synthetic amorphous calcium phosphate in contact with a solution containing an amount of ATP equivalent to that of the biological mineral failed to undergo conversion to the thermodynamically more stable hydroxyapatite. The amorphous calcium phosphate of the cytoplasmic mineral granules is similarly stable, and does not undergo conversion to hydroxyapatite, presumably owing to the presence of ATP and Mg-2+, known in inhibitors of the conversion process. The physiological implications of mineral deposits consisting of stabilized calcium phosphate ion clusters are discussed.

  9. Osteoinduction of calcium phosphate biomaterials in small animals

    Energy Technology Data Exchange (ETDEWEB)

    Cheng, Lijia; Shi, Yujun [Key Laboratory of Transplant Engineering and Immunology, Ministry of Health, West China Hospital, Sichuan University, Chengdu (China); Ye, Feng [Department of Pathology, West China Hospital, Sichuan University, Chengdu, 610041 (China); Bu, Hong, E-mail: hongbu@scu.edu.cn [Key Laboratory of Transplant Engineering and Immunology, Ministry of Health, West China Hospital, Sichuan University, Chengdu (China); Department of Pathology, West China Hospital, Sichuan University, Chengdu, 610041 (China)

    2013-04-01

    Although osteoinduction mechanism of calcium phosphate (CP) ceramics is still unclear, several essential properties have been reported, such as chemical composition, pore size and porosity, etc. In this study, calcium phosphate powder (Ca{sub 3}(PO{sub 4}){sub 2}, CaP, group 1), biphasic calcium phosphate ceramic powder (BCP, group 2), and intact BCP rods (group 3) were implanted into leg muscles of mice and dorsal muscles of rabbits. One month and three months after implantation, samples were harvested for biological and histological analysis. New bone tissues were observed in 10/10 samples in group 1, 3/10 samples in group 2, and 9/10 samples in group 3 at 3rd month in mice, but not in rabbits. In vitro, human mesenchymal stem cells (hMSCs) were cultured with trace CaP and BCP powder, and osteogenic differentiation was observed at day 7. Our results suggested that chemical composition is the prerequisite in osteoinduction, and pore structure would contribute to more bone formation. - Highlights: ► Intrinsic osteoinduction of calcium phosphate biomaterials was observed implanted in muscles of mice. ► Biomaterials powder also has osteoinduction property. ► Osteogenic genes and protein could be detected by RT-PCR and Western blot in implanted biomaterials. ► Osteogenic phenomenon could be observed by electron microscopy. ► The chemical composition is the prerequisite in osteoinduction, and pore structure would contribute to more bone formation.

  10. Calcium phosphate implants coatings as carriers for BMP-2

    NARCIS (Netherlands)

    Liu, Y.; He, J.F.; Hunziker, E.B.

    2009-01-01

    The osteoconductivity of dental implants can be improved by coating them with a layer of calcium phosphate (CaP), which can be rendered osteoinductive by functionalizing it with an osteogenic agent, such as bone morphogenetic protein 2 (BMP-2). In the present study, we wished to compare the

  11. Biomimetic calcium phosphate coatings on recombinant spider silk fibres

    International Nuclear Information System (INIS)

    Yang Liang; Habibovic, Pamela; Van Blitterswijk, Clemens A; Hedhammar, My; Johansson, Jan; Blom, Tobias; Leifer, Klaus

    2010-01-01

    Calcium phosphate ceramic coatings, applied on surfaces of metallic and polymeric biomaterials, can improve their performance in bone repair and regeneration. Spider silk is biocompatible, strong and elastic, and hence an attractive biomaterial for applications in connective tissue repair. Recently, artificial spider silk, with mechanical and structural characteristics similar to those of native spider silk, has been produced from recombinant minispidroins. In the present study, supersaturated simulated body fluid was used to deposit calcium phosphate coatings on recombinant spider silk fibres. The mineralization process was followed in time using scanning electron microscopy equipped with an energy dispersive x-ray (EDX) detector and Raman spectroscope. Focused ion beam technology was used to produce a cross section of a coated fibre, which was further analysed by EDX. Preliminary in vitro experiments using a culture of bone marrow-derived human mesenchymal stem cells (hMSCs) on coated fibres were also performed. This study showed that recombinant spider silk fibres were successfully coated with a homogeneous and thick crystalline calcium phosphate layer. In the course of the mineralization process from modified simulated body fluid, sodium chloride crystals were first deposited on the silk surface, followed by the deposition of a calcium phosphate layer. The coated silk fibres supported the attachment and growth of hMSCs.

  12. Optimizing conditions for calcium phosphate mediated transient transfection

    Directory of Open Access Journals (Sweden)

    Ling Guo

    2017-03-01

    Conclusions: Calcium phosphate mediated transfection is the most low-cost approach to introduce recombinant DNA into culture cells. However, the utility of this procedure is limited in highly-differentiated cells. Here we describe the specific HBS-buffered saline, PH, glycerol shock, vortex strength, transfection medium, and particle concentrations conditions necessary to optimize this transfection method in highly differentiated cells.

  13. Amorphous calcium phosphate and its application in dentistry

    Directory of Open Access Journals (Sweden)

    Sun Wei-bin

    2011-07-01

    Full Text Available Abstract Amorphous Calcium Phosphate (ACP is an essential mineral phase formed in mineralized tissues and the first commercial product as artificial hydroxyapatite. ACP is unique among all forms of calcium phosphates in that it lacks long-range, periodic atomic scale order of crystalline calcium phosphates. The X-ray diffraction pattern is broad and diffuse with a maximum at 25 degree 2 theta, and no other different features compared with well-crystallized hydroxyapatite. Under electron microscopy, its morphological form is shown as small spheroidal particles in the scale of tenths nanometer. In aqueous media, ACP is easily transformed into crystalline phases such as octacalcium phosphate and apatite due to the growing of microcrystalline. It has been demonstrated that ACP has better osteoconductivity and biodegradability than tricalcium phosphate and hydroxyapatite in vivo. Moreover, it can increase alkaline phosphatase activities of mesoblasts, enhance cell proliferation and promote cell adhesion. The unique role of ACP during the formation of mineralized tissues makes it a promising candidate material for tissue repair and regeneration. ACP may also be a potential remineralizing agent in dental applications. Recently developed ACP-filled bioactive composites are believed to be effective anti-demineralizing/remineralizing agents for the preservation and repair of tooth structures. This review provides an overview of the development, structure, chemical composition, morphological characterization, phase transformation and biomedical application of ACP in dentistry.

  14. Biomimetic fabrication of antibacterial calcium phosphates mediated by polydopamine.

    Science.gov (United States)

    Forte, Lucia; Torricelli, Paola; Bonvicini, Francesca; Boanini, Elisa; Gentilomi, Giovanna Angela; Lusvardi, Gigliola; Della Bella, Elena; Fini, Milena; Vecchio Nepita, Edoardo; Bigi, Adriana

    2018-01-01

    In this work we developed new antibacterial composite materials using polydopamine (PDA) to trigger the deposition of silver nanoparticles (AgNPs) onto calcium phosphates, namely octacalcium phosphate (OCP) and α-tricalcium phosphate (αTCP). Functionalization of OCP and αTCP with a self-polymerized polydopamine layer was obtained by soaking the calcium phosphates in dopamine solution. The PDA surface of functionalized calcium phosphates (OCPd and αTCPd) promoted the deposition of AgNPs by reducing silver ions when soaked in a silver nitrate solution. The amount of deposited AgNPs can be modulated by varying the concentration of silver nitrate solution and the type of substrate. The results of in vitro tests carried out with osteoblast-like MG63 cells indicate that the combination of AgNPs with OCP provides more biocompatible materials than those obtained using αTCP as substrate. In particular, the study of osteoblast activity and differentiation was focused on the samples OCPdAg5 (silver content=8.2wt%) and αTCPdAg5 (silver content=4.7wt%), which did not show any cytotoxicity, and compared with those obtained on pure OCP and αTCP. The results demonstrate that the AgNPs loaded materials support osteoblast viability and differentiation, whereas they significantly inhibit the growth of relevant antibiotic-resistant pathogenic bacteria. Copyright © 2017 Elsevier Inc. All rights reserved.

  15. Calcium-phosphate-osteopontin particles for caries control

    DEFF Research Database (Denmark)

    Schlafer, Sebastian; Birkedal, Henrik; Olsen, Jakob

    2016-01-01

    Caries is caused by acid production in biofilms on dental surfaces. Preventing caries therefore involves control of microorganisms and/or the acid produced. Here, calcium-phosphate-osteopontin particles are presented as a new approach to caries control. The particles are made by co......-precipitation and designed to bind to bacteria in biofilms, impede biofilm build-up without killing the microflora, and release phosphate ions to buffer bacterial acid production if the pH decreases below 6. Analysis of biofilm formation and pH in a five-species biofilm model for dental caries showed that treatment......H always remained above 5.5. Hence, calcium-phosphate-osteopontin particles show potential for applications in caries control....

  16. Calcium-phosphate-osteopontin particles for caries control

    DEFF Research Database (Denmark)

    Schlafer, Sebastian

    Oftentimes caries lesions develop in protected sites that are difficult to access by self-performed mechanical tooth cleaning. At present, there is a growing interest in chemical adjuncts to mechanical procedures of oral hygiene that aim at biofilm control rather than biofilm eradication. Calcium......-phosphate-osteopontin particles are a new promising therapeutic approach to caries control. They are designed to bind to dental biofilms and interfere with biofilm build-up, lowering the bacterial burden on the tooth surface without affecting bacterial viability in the oral cavity. Moreover, they dissolve when pH in the biofilm...... drops to 6 or below and release buffering phosphate ions that stabilize biofilm pH above the critical level for enamel dissolution. With that twofold approach, calcium-phosphate-osteopontin particles may make a relevant contribution to clinical caries control....

  17. Synthesis and characterization of powders calcium phosphate for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, D.M.P. de; Prants, W.T.; Camargo, N.H.A.; Gemelli, E., E-mail: daniellapinheiro@gmail.com, E-mail: w_prants@hotmail.com, E-mail: dem2nhac@joinville.udesc.br, E-mail: dma2ec@joinville.udesc.br [Universidade do Estado de Santa Catarina (UDESC), Joinville, SC (Brazil). Centro de Ciencias Tecnologicas

    2009-07-01

    Scientists of different areas research the bioceramics as new materials to substitute parts of the human body. The bioceramics of the calcium phosphate have the advantage present similar chemical composition to the structure of the bony apatite of the human skeleton. In this study, calcium phosphate powder was synthesized chemically using the solution of phosphorus pentoxide (P{sub 2}O{sub 5}) and calcium oxide (CaO) necessary for molar Ca/P =1.67. These works aim the study of different thermal treatments, physics and of the microstructure properties. For characterization the bony matrix were used the techniques of: X-ray diffraction (DRX); Scanning Electronic Microscopy (SEM) and Differential Scanning Calorimetry (DSC). (author)

  18. Synthesis and characterization of powders calcium phosphate for biomedical applications

    International Nuclear Information System (INIS)

    Oliveira, D.M.P. de; Prants, W.T.; Camargo, N.H.A.; Gemelli, E.

    2009-01-01

    Scientists of different areas research the bioceramics as new materials to substitute parts of the human body. The bioceramics of the calcium phosphate have the advantage present similar chemical composition to the structure of the bony apatite of the human skeleton. In this study, calcium phosphate powder was synthesized chemically using the solution of phosphorus pentoxide (P 2 O 5 ) and calcium oxide (CaO) necessary for molar Ca/P =1.67. These works aim the study of different thermal treatments, physics and of the microstructure properties. For characterization the bony matrix were used the techniques of: X-ray diffraction (DRX); Scanning Electronic Microscopy (SEM) and Differential Scanning Calorimetry (DSC). (author)

  19. Comparative study on in vitro biocompatibility of synthetic octacalcium phosphate and calcium phosphate ceramics used clinically.

    Science.gov (United States)

    Morimoto, Shinji; Anada, Takahisa; Honda, Yoshitomo; Suzuki, Osamu

    2012-08-01

    The present study was designed to investigate the extent to which calcium phosphate bone substitute materials, including osteoconductive octacalcium phosphate (OCP), display cytotoxic and inflammatory responses based on their dissolution in vitro. Hydroxyapatite (HA) and β-tricalcium phosphate (β-TCP) ceramics, which are clinically used, as well as dicalcium phosphate dihydrate (DCPD) and synthesized OCP were compared. The materials were well characterized by chemical analysis, x-ray diffraction and Fourier transform infrared spectroscopy. Calcium and phosphate ion concentrations and the pH of culture media after immersion of the materials were determined. The colony forming rate of Chinese hamster lung fibroblasts was estimated with extraction of the materials. Proliferation of bone marrow stromal ST-2 cells and inflammatory cytokine TNF-α production by THP-1 cells grown on the material-coated plates were examined. The materials had characteristics that corresponded to those reported. DCPD was shown to dissolve the most in the culture media, with a marked increase in phosphate ion concentration and a reduction in pH. ST-2 cells proliferated well on the materials, with the exception of DCPD, which markedly inhibited cellular growth. The colony forming capacity was the lowest on DCPD, while that of the other calcium phosphates was not altered. In contrast, TNF-α was not detected even in cells grown on DCPD, suggesting that calcium phosphate materials are essentially non-inflammatory, while the solubility of the materials can affect osteoblastic and fibroblastic cellular attachment. These results indicate that OCP is biocompatible, which is similar to the materials used clinically, such as HA. Therefore, OCP could be clinically used as a biocompatible bone substitute material.

  20. Influence of calcium on ceramide-1-phosphate monolayers

    Directory of Open Access Journals (Sweden)

    Joana S. L. Oliveira

    2016-02-01

    Full Text Available Ceramide-1-phosphate (C1P plays an important role in several biological processes, being identified as a key regulator of many protein functions. For instance, it acts as a mediator of inflammatory responses. The mediation of the inflammation process happens due to the interaction of C1P with the C2 domain of cPLA2α, an effector protein that needs the presence of submicromolar concentrations of calcium ions. The aim of this study was to determine the phase behaviour and structural properties of C1P in the presence and absence of millimolar quantities of calcium in a well-defined pH environment. For that purpose, we used monomolecular films of C1P at the soft air/liquid interface with calcium ions in the subphase. The pH was varied to change the protonation degree of the C1P head group. We used surface pressure versus molecular area isotherms coupled with other monolayer techniques as Brewster angle microscopy (BAM, infrared reflection–absorption spectroscopy (IRRAS and grazing incidence X-ray diffraction (GIXD. The isotherms indicate that C1P monolayers are in a condensed state in the presence of calcium ions, regardless of the pH. At higher pH without calcium ions, the monolayer is in a liquid-expanded state due to repulsion between the negatively charged phosphate groups of the C1P molecules. When divalent calcium ions are added, they are able to bridge the highly charged phosphate groups, enhancing the regular arrangement of the head groups. Similar solidification of the monolayer structure can be seen in the presence of a 150 times larger concentration of monovalent sodium ions. Therefore, calcium ions have clearly a strong affinity for the phosphomonoester of C1P.

  1. Prediction of the Setting Properties of Calcium Phosphate Bone Cement

    Directory of Open Access Journals (Sweden)

    Seyed Mahmud Rabiee

    2012-01-01

    Full Text Available Setting properties of bone substitutes are improved using an injectable system. The injectable bone graft substitutes can be molded to the shape of the bone cavity and set in situ when injected. Such system is useful for surgical operation. The powder part of the injectable bone cement is included of β-tricalcium phosphate, calcium carbonate, and dicalcium phosphate and the liquid part contains poly ethylene glycol solution with different concentrations. In this way, prediction of the mechanical properties, setting times, and injectability helps to optimize the calcium phosphate bone cement properties. The objective of this study is development of three different adaptive neurofuzzy inference systems (ANFISs for estimation of compression strength, setting time, and injectability using the data generated based on experimental observations. The input parameters of models are polyethylene glycol percent and liquid/powder ratio. Comparison of the predicted values and measured data indicates that the ANFIS model has an acceptable performance to the estimation of calcium phosphate bone cement properties.

  2. Mechanism of calcium phosphates precipitation in liquid crystals

    International Nuclear Information System (INIS)

    Prelot, B.; Zemb, T.

    2004-04-01

    The possibility of using as a precursor an easily wet meso-porous powder would be a breakthrough in the preparation of nuclear waste storage ceramics. A concentrated solution containing ions to be stored would wet a dry powder and then, subjected to mild compression, lead to a micro-crystalline matrix of calcium phosphate at acceptable temperatures. Since no porous calcium phosphate different from calcined bone (patented) is described as porous precursor, we have compared the different synthesis routes towards meso-porous ceramics. First, we considered homogeneous precipitation of slats in water: using initially off-stoichiometry in reaction, micron-sized hydroxyapatite particles are produced with a specific surface up to 100 m 2 /g. Then, we consider the classical route of precipitation of an hybrid material in the miscibility gap of a phase diagram, when an hexagonal liquid crystal is used a matrix for precipitation. The surfactant family consists in single chain surfactants containing phosphates as head-group to poison the growing surface of calcium phosphate nano-domains. Since the reaction is still too brutal, we considered using a cat-anionic precursor material of controllable surface charge. For certain concentrations and molar ratios, a new structure not yet described in surfactant precipitation literature is observed: since the periodicity is lower than twice the chain length, a disordered constant curvature monolayer (instead of the classical cylinder of twice chain length diameter) of surfactant is implied. Finally, we have investigated synthesis routes implying slow dissolution of pre-formed calcium phosphate in an already existing hexagonal matrix. For all these routes of synthesis, micro-structural determinations using SAXS, WARS and BET are performed, with a special attention to comparison of the precipitation material, the matrix obtained with all elements present, and also the material obtained after calcinations. (authors)

  3. Mechanism of calcium phosphates precipitation in liquid crystals; Mecanisme de precipitation de phosphates de calcium dans des cristaux liquides

    Energy Technology Data Exchange (ETDEWEB)

    Prelot, B.; Zemb, T

    2004-04-01

    The possibility of using as a precursor an easily wet meso-porous powder would be a breakthrough in the preparation of nuclear waste storage ceramics. A concentrated solution containing ions to be stored would wet a dry powder and then, subjected to mild compression, lead to a micro-crystalline matrix of calcium phosphate at acceptable temperatures. Since no porous calcium phosphate different from calcined bone (patented) is described as porous precursor, we have compared the different synthesis routes towards meso-porous ceramics. First, we considered homogeneous precipitation of slats in water: using initially off-stoichiometry in reaction, micron-sized hydroxyapatite particles are produced with a specific surface up to 100 m{sup 2}/g. Then, we consider the classical route of precipitation of an hybrid material in the miscibility gap of a phase diagram, when an hexagonal liquid crystal is used a matrix for precipitation. The surfactant family consists in single chain surfactants containing phosphates as head-group to poison the growing surface of calcium phosphate nano-domains. Since the reaction is still too brutal, we considered using a cat-anionic precursor material of controllable surface charge. For certain concentrations and molar ratios, a new structure not yet described in surfactant precipitation literature is observed: since the periodicity is lower than twice the chain length, a disordered constant curvature monolayer (instead of the classical cylinder of twice chain length diameter) of surfactant is implied. Finally, we have investigated synthesis routes implying slow dissolution of pre-formed calcium phosphate in an already existing hexagonal matrix. For all these routes of synthesis, micro-structural determinations using SAXS, WARS and BET are performed, with a special attention to comparison of the precipitation material, the matrix obtained with all elements present, and also the material obtained after calcinations. (authors)

  4. The increasing of enamel calcium level after casein phosphopeptideamorphous calcium phosphate covering

    OpenAIRE

    Widyasri Prananingrum; Puguh Bayu Prabowo

    2012-01-01

    Background: Caries process is characterized by the presence of demineralization. Demineralization is caused by organic acids as a result of carbohydrate substrate fermentation. Remineralization is a natural repair process for non-cavitated lesions. Remineralization occurs if there are Ca2+ and PO43- ions in sufficient quantities. Casein-amorphous calcium phosphate phosphopeptide (CPP-ACP) is a paste material containing milk protein (casein), that actually contains minerals, such as calcium an...

  5. Synthesis of amorphous calcium phosphate using various types of cyclodextrins

    International Nuclear Information System (INIS)

    Li Yanbao; Wiliana, Tjandra; Tam, Kam C.

    2007-01-01

    Amorphous calcium phosphate (ACP) was synthesised in aqueous solution at room temperature using cyclodextrins. Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDX) and thermal analysis (DTA/TGA) were performed on the calcium phosphate precipitates obtained from solutions. We observed that only β-CD could stabilise the amorphous phase in the mother solution because of the lower solubility of β-CD in water and the ACP remained stable in aqueous solution for more than 24 h at room temperature. The ACP particle has an initial particle size of less than 40 nm, Ca/P molar ratio of 1.67 and β-CD absorbed on its surface. The mechanism for the stabilisation of ACP is proposed

  6. The influence of Sr content in calcium phosphate coatings

    International Nuclear Information System (INIS)

    Lindahl, Carl; Pujari-Palmer, Shiuli; Hoess, Andreas; Ott, Marjam; Engqvist, Håkan; Xia, Wei

    2015-01-01

    In this study calcium phosphate coatings with different amounts of strontium (Sr) were prepared using a biomineralization method. The incorporation of Sr changed the composition and morphology of coatings from plate-like to sphere-like morphology. Dissolution testing indicated that the solubility of the coatings increased with increased Sr concentration. Evaluation of extracts (with Sr concentrations ranging from 0 to 2.37 μg/mL) from the HA, 0.06Sr, 0.6Sr, and 1.2Sr coatings during in vitro cell cultures showed that Sr incorporation into coatings significantly enhanced the ALP activity in comparison to cells treated with control and HA eluted media. These findings show that calcium phosphate coatings could promote osteogenic differentiation even in a low amount of strontium. - Highlights: • Calcium phosphate coating doping with low Sr contents was prepared via a biomineralization process. • The solubility of the coatings increased with increased Sr concentration. • Present findings show the potential that Sr has on promoting osteogenic differentiation even in a low amount

  7. Hydrolytic conversion of amorphous calcium phosphate into apatite accompanied by sustained calcium and orthophosphate ions release

    Energy Technology Data Exchange (ETDEWEB)

    Niu, Xufeng, E-mail: nxf@buaa.edu.cn [Key Laboratory for Biomechanics and Mechanobiology of Ministry of Education, School of Biological Science and Medical Engineering, Beihang University, Beijing 100191 (China); BUAA Research Institute, Guangzhou 510530 (China); Research Institute of Beihang University in Shenzhen, Shenzhen 518057 (China); Chen, Siqian; Tian, Feng; Wang, Lizhen [Key Laboratory for Biomechanics and Mechanobiology of Ministry of Education, School of Biological Science and Medical Engineering, Beihang University, Beijing 100191 (China); Feng, Qingling [State Key Laboratory of New Ceramic and Fine Processing, Tsinghua University, Beijing 100084 (China); Fan, Yubo, E-mail: yubofan@buaa.edu.cn [Key Laboratory for Biomechanics and Mechanobiology of Ministry of Education, School of Biological Science and Medical Engineering, Beihang University, Beijing 100191 (China)

    2017-01-01

    The aim of this study is to investigate the calcium and orthophosphate ions release during the transformation of amorphous calcium phosphate (ACP) to hydroxyapatite (HA) in aqueous solution. The ACP is prepared by a wet chemical method and further immersed in the distilled water for various time points till 14 d. The release of calcium and orthophosphate ions is measured with calcium and phosphate colorimetric assay kits, respectively. The transition of ACP towards HA is detected by x-ray diffraction (XRD), transmission electron microscopy (TEM), and fourier transform infrared spectroscopy (FTIR). The results indicate that the morphological conversion of ACP to HA occurs within the first 9 h, whereas the calcium and orthophosphate ions releases last for over 7 d. Such sustained calcium and orthophosphate ions release is very useful for ACP as a candidate material for hard tissue regeneration. - Highlights: • ACP is prepared using a wet chemical method. • The conversion of crystal morphology and structure occurs mainly within the initial 9 h. • The calcium and orthophosphate ions release sustains over 14 d.

  8. Biomimetic coprecipitation of calcium phosphate and bovine serum albumin on titanium alloy

    NARCIS (Netherlands)

    Liu, Yuelian; Layrolle, Pierre; de Bruijn, Joost Dick; van Blitterswijk, Clemens; de Groot, K.

    2001-01-01

    Titanium alloy implants were precoated biomimetically with a thin and dense layer of calcium phosphate and then incubated either in a supersaturated solution of calcium phosphate or in phosphate-buffered saline, each containing bovine serum albumin (BSA) at various concentrations, under

  9. Calcium phosphate granulation in anaerobic treatment of black water: a new approach to phosphorus recovery

    NARCIS (Netherlands)

    Tervahauta, T.H.; Weijden, van der R.D.; Flemming, R.L.; Hernández, L.; Zeeman, G.; Buisman, C.J.N.

    2014-01-01

    Recovery of phosphorus from wastewater as calcium phosphate could diminish the need for mining of scarce phosphate rock resources. This study introduces a novel approach to phosphorus recovery by precipitation of calcium phosphate granules in anaerobic treatment of black water. The granules formed

  10. Effect of calcium carbonate on hardening, physicochemical properties, and in vitro degradation of injectable calcium phosphate cements.

    NARCIS (Netherlands)

    Sariibrahimoglu, K.; Leeuwenburgh, S.C.G.; Wolke, J.G.C.; Yubao, L.; Jansen, J.A.

    2012-01-01

    The main disadvantage of apatitic calcium phosphate cements (CPCs) is their slow degradation rate, which limits complete bone regeneration. Carbonate (CO(3)(2)(-)) is the common constituent of bone and it can be used to improve the degradability of the apatitic calcium phosphate ceramics. This study

  11. Kinetics of dissolution of calcium phosphate (Ca-P bioceramics

    Directory of Open Access Journals (Sweden)

    Lukas Brazda

    2008-06-01

    Full Text Available Hydroxyapatite (HAp and β-tricalcium phosphate (β-TCP are widely used bioceramics for surgical or dental applications. This paper is dealing with dissolution kinetics of synthetically prepared β-TCP and four types of HAp granules. Two groups of HAp, treated at different temperatures, each of them with two different granule sizes, were tested. Three corrosive solutions with different pH and simulated body fluid (SBF were used for immersing of the samples. Changes in concentrations of calcium and phosphate ions, pH level and weight changes of the samples were observed. It was found that presence of TRIS buffer enhanced dissolution rate of the β-TCP approximately two times. When exposed to SBF solution, calcium phosphate (most probably hydroxyapatite precipitation predominates over β-TCP dissolution. Results from HAp samples dissolution showed some unexpected findings. Neither heat treatment nor HAp particle size made any major differences in dissolution rate of the same mass of each HAp sample.

  12. Tailoring the structure of biphasic calcium phosphate via synthesis procedure

    Science.gov (United States)

    Mansour, S. F.; El-dek, S. I.; Ahmed, M. K.

    2017-12-01

    Nano calcium phosphate ceramics (CaPC) were synthesized using simple co-precipitation method at different preparation conditions. The selected Ca/P ratio with a variation of pH value lead to formation of dicalcium phosphate dihydrate (DCPD) at pH 5 and 6 while, hydroxyapatite (HAP) nano particles were formed at pH 9 and 12 at room temperature. The crystallite size was in the range of 15-55 nm depending on the obtained crystalline phase. The study displayed variation of decomposition depending on the annealing temperature. The significant note is the different transformation trend of each phase depending on the starting pH value. The HRTEM illustrated that the DCPD phase was formed as fibers with diameter around 4-6 nm, while HAP was formed in rod shape. The aspect ratio decreased from 6.6 at pH 9 to 4 at pH 12 which refer to the great influence of pH value on the morphology of calcium phosphates.

  13. Removal of radioactive waste waters by calcium phosphate precipitation

    International Nuclear Information System (INIS)

    Raicevic, S.; Vukovic, Z.; Mandic, M.

    1997-01-01

    The kinetics of removal of radioactive strontium by coprecipitation and sorption with amorphous calcium phosphate (ACP) which transformed into stable crystalline hydroxyapatite (HA) were investigated. The advantage of phosphate precipitation is a possibility not only for removal of radioactive strontium but also for incorporation of a strontium ion into stable structure of HA. calcium phosphate was precipitated from highly saturated solution by fast reagent mixing. Kinetic experiments were performed using strontium nitrate solution labeled with 8 5 Sr. The amount of radionuclide uptake by the solid phase was determined radiometrically at different time intervals. It was found that ACP phase firmly retains coprecipitated impurities up to 150 min, of reaction time when partial rejection of strontium into the solution occurred. In sorption experiments after prolonged time of equilibrium the firm incorporation of 8 5 Sr stable crystalline structure of HA was detected. The incorporation of 8 5 Sr into crystalline HA was analysed in detail in the paper /S. Raicevic, et. al., J. Radioanal. Nucl. Chem., Articles, Vol. 204, No 2, 1996/ (author)

  14. Calcium phosphate stabilization of fly ash with chloride extraction.

    Science.gov (United States)

    Nzihou, Ange; Sharrock, Patrick

    2002-01-01

    Municipal solid waste incinerator by products include fly ash and air pollution control residues. In order to transform these incinerator wastes into reusable mineral species, soluble alkali chlorides must be separated and toxic trace elements must be stabilized in insoluble form. We show that alkali chlorides can be extracted efficiently in an aqueous extraction step combining a calcium phosphate gel precipitation. In such a process, sodium and potassium chlorides are obtained free from calcium salts, and the trace metal ions are immobilized in the calcium phosphate matrix. Moderate calcination of the chemically treated fly ash leads to the formation of cristalline hydroxylapatite. Fly ash spiked with copper ions and treated by this process shows improved stability of metal ions. Leaching tests with water or EDTA reveal a significant drop in metal ion dissolution. Hydroxylapatite may trap toxic metals and also prevent their evaporation during thermal treatments. Incinerator fly ash together with air pollution control residues, treated by the combined chloride extraction and hydroxylapatite formation process may be considered safe to use as a mineral filler in value added products such as road base or cement blocks.

  15. Effect of the calcium to phosphorus ratio on the setting properties of calcium phosphate bone cements.

    Science.gov (United States)

    Vlad, M D; Gómez, S; Barracó, M; López, J; Fernández, E

    2012-09-01

    α-Tricalcium phosphate (α-TCP) has become the main reactant of most experimental and commercial ceramic bone cements. It has calcium-to-phosphorus (Ca/P) ratio of 1.50. The present study expands and reports on the microstructures and mechanical properties of calcium phosphate (CP) cements containing sintered monolithic reactants obtained in the interval 1.29 properties as well as on their microstructure and crystal phase evolution. The results showed that: (a) CP-cements made with reactants with Ca/P ratio other than 1.50 have longer setting and lower hardening properties; (b) CP-cements reactivity was clearly affected by the Ca/P ratio of the starting reactant; (c) reactants with Ca/P calcium pyrophosphate and α- and β-TCP. Similarly, reactants with Ca/P > 1.50 were composed of α-TCP, tetracalcium phosphate and hydroxyapatite; (d) only the reactant with Ca/P = 1.50 was monophasic and was made of α-TCP, which transformed during the setting into calcium deficient hydroxyapatite; (e) CP-cements developed different crystal microstructures with specific features depending on the Ca/P ratio of the starting reactant.

  16. Selective laser sintering of calcium phosphate materials for orthopedic implants

    Science.gov (United States)

    Lee, Goonhee

    Two technologies, Solid Freeform Fabrication (SFF) and bioceramics are combined in this work to prepare bone replacement implants with complex geometry. SFF has emerged as a crucial technique for rapid prototyping in the last decade. Selective Laser Sintering (SLS) is one of the established SFF manufacturing processes that can build three-dimensional objects directly from computer models without part-specific tooling or human intervention. Meanwhile, there have been great efforts to develop implantable materials that can assist in regeneration of bone defects and injuries. However, little attention has been focused in shaping bones from these materials. The main thrust of this research was to develop a process that can combine those two separate efforts. The specific objective of this research is to develop a process that can construct bone replacement material of complex geometry from synthetic calcium phosphate materials by using the SLS process. The achievement of this goal can have a significant impact on the quality of health care in the sense that complete custom-fit bone and tooth structures suitable for implantation can be prepared within 24--48 hours of receipt of geometric information obtained either from patient Computed Tomographic (CT) data, from Computer Aided Design (CAD) software or from other imaging systems such as Magnetic Resonance Imaging (MRI) and Holographic Laser Range Imaging (HLRI). In this research, two different processes have been developed. First is the SLS fabrication of porous bone implants. In this effort, systematic procedures have been established and calcium phosphate implants were successfully fabricated from various sources of geometric information. These efforts include material selection and preparation, SLS process parameter optimization, and development of post-processing techniques within the 48-hour time frame. Post-processing allows accurate control of geometry and of the chemistry of calcium phosphate, as well as

  17. The Transformation of Calcium Phosphate Bioceramics in Vivo

    Institute of Scientific and Technical Information of China (English)

    DAI Hong-lian; CAO Xian-ying; LI Xiao-xi; YAN Yu-hua; LI Shi-pu

    2003-01-01

    To study the transformation process of calcium phosphate bioceramic in vivo,biodegradable porous β-tricalcium phosphate ceramics (β-TCP) were used in this experiment. The materials (φ5×8mm) were implanted in the tibia of rabbits. The β-TCP ceramics with bone tissue were retrieved and treated for histology, and then observed by using a scanning electron microscope (SEM) and an electron probe X-ray microanalyzer (EMPA) every month. The results show that β-TCP ceramics bond to bone directly,new bones are forming and maturing with materials continuous degrading,and the materials are nearly replaced by the formed bone finally.Parts of the materials were degraded,absorpted and recrystallized,the others dispersped on the cancellous bone and the Haversian lamella with an irregular arrangement incorporating in bone formation directly by remodeling structure.

  18. Bioactivity of calcium phosphate bioceramic coating fabricated by laser cladding

    Science.gov (United States)

    Zhu, Yizhi; Liu, Qibin; Xu, Peng; Li, Long; Jiang, Haibing; Bai, Yang

    2016-05-01

    There were always strong expectations for suitable biomaterials used for bone regeneration. In this study, to improve the biocompatiblity of titanium alloy, calcium phosphate bioceramic coating was obtained by laser cladding technology. The microstructure, phases, bioactivity, cell differentiation, morphology and resorption lacunae were investigated by optical microscope (OM), x-ray diffraction (XRD), methyl thiazolyl tetrazolium (MTT) assay, tartrate-resistant acid phosphatase (TRAP) staining and scanning electronic microscope (SEM), respectively. The results show that bioceramic coating consists of three layers, which are a substrate, an alloyed layer and a ceramic layer. Bioactive phases of β-tricalcium phosphate (β-TCP) and hydroxyapatite (HA) were found in ceramic coating. Osteoclast precursors have excellent proliferation on the bioceramic surface. The bioceramics coating could be digested by osteoclasts, which led to the resorption lacunae formed on its surface. It revealed that the gradient bioceramic coating has an excellent bioactivity.

  19. Bioactivity of calcium phosphate bioceramic coating fabricated by laser cladding

    International Nuclear Information System (INIS)

    Zhu, Yizhi; Liu, Qibin; Xu, Peng; Li, Long; Jiang, Haibing; Bai, Yang

    2016-01-01

    There were always strong expectations for suitable biomaterials used for bone regeneration. In this study, to improve the biocompatiblity of titanium alloy, calcium phosphate bioceramic coating was obtained by laser cladding technology. The microstructure, phases, bioactivity, cell differentiation, morphology and resorption lacunae were investigated by optical microscope (OM), x-ray diffraction (XRD), methyl thiazolyl tetrazolium (MTT) assay, tartrate-resistant acid phosphatase (TRAP) staining and scanning electronic microscope (SEM), respectively. The results show that bioceramic coating consists of three layers, which are a substrate, an alloyed layer and a ceramic layer. Bioactive phases of β-tricalcium phosphate (β-TCP) and hydroxyapatite (HA) were found in ceramic coating. Osteoclast precursors have excellent proliferation on the bioceramic surface. The bioceramics coating could be digested by osteoclasts, which led to the resorption lacunae formed on its surface. It revealed that the gradient bioceramic coating has an excellent bioactivity. (letter)

  20. Formation of calcium phosphate layer on ceramics with different reactivities

    International Nuclear Information System (INIS)

    Ribeiro, C.; Rigo, E.C.S.; Sepulveda, P.; Bressiani, J.C.; Bressiani, A.H.A.

    2004-01-01

    Biphasic ceramic samples of different biological reactivity are prepared by using hydroxyapatite (HAp) and tricalcium phosphate (TCP) in various ratios. Different parameters for sintering in an air atmosphere furnace were defined after dilatometric studies. An increased densification with decreased TCP content was observed. The sintered bodies were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The dissolution kinetics and in vitro reactivity were investigated using simulated body fluid (SBF) at 37 deg. C for a maximum period of 3 weeks. The surfaces of the ceramics were analyzed by Fourier transform infrared spectroscopy (FTIR) and SEM in order to observe the formation of a calcium phosphate layer, which indicates the samples bioactivity. Dissolution in SBF demonstrated that layers with different kinetics on the samples surface were formed during the immersion period. The biphasic ceramics show bioactive behavior, even if the resorbable TCP is incorporated

  1. Mechanical properties of experimental composites with different calcium phosphates fillers.

    Science.gov (United States)

    Okulus, Zuzanna; Voelkel, Adam

    2017-09-01

    Calcium phosphates (CaPs)-containing composites have already shown good properties from the point of view of dental restorative materials. The purpose of this study was to examine the crucial mechanical properties of twelve hydroxyapatite- or tricalcium phosphate-filled composites. The raw and surface-treated forms of both CaP fillers were applied. As a reference materials two experimental glass-containing composites and one commercial dental restorative composite were applied. Nano-hardness, elastic modulus, compressive, flexural and diametral tensile strength of all studied materials were determined. Application of statistical methods (one-way analysis of variance and cluster agglomerative analysis) allowed for assessing the similarities between examined materials according to the values of studied parameters. The obtained results show that in almost all cases the mechanical properties of experimental CaPs-composites are comparable or even better than mechanical properties of examined reference materials. Copyright © 2017 Elsevier B.V. All rights reserved.

  2. Interactions of casein micelles with calcium phosphate particles.

    Science.gov (United States)

    Tercinier, Lucile; Ye, Aiqian; Anema, Skelte G; Singh, Anne; Singh, Harjinder

    2014-06-25

    Insoluble calcium phosphate particles, such as hydroxyapatite (HA), are often used in calcium-fortified milks as they are considered to be chemically unreactive. However, this study showed that there was an interaction between the casein micelles in milk and HA particles. The caseins in milk were shown to bind to the HA particles, with the relative proportions of bound β-casein, αS-casein, and κ-casein different from the proportions of the individual caseins present in milk. Transmission electron microscopy showed no evidence of intact casein micelles on the surface of the HA particles, which suggested that the casein micelles dissociated either before or during binding. The HA particles behaved as ion chelators, with the ability to bind the ions contained in the milk serum phase. Consequently, the depletion of the serum minerals disrupted the milk mineral equilibrium, resulting in dissociation of the casein micelles in milk.

  3. Preparation of DNA/Gold Nanoparticle Encapsulated in Calcium Phosphate

    Directory of Open Access Journals (Sweden)

    Tomoko Ito

    2011-01-01

    Full Text Available Biocompatible DNA/gold nanoparticle complex with a protective calcium phosphate (CaP coating was prepared by incubating DNA/gold nanoparticle complex coated by hyaluronic acid in SBF (simulated body fluid with a Ca concentration above 2 mM. The CaP-coated DNA complex was revealed to have high compatibility with cells and resistance against enzymatic degradation. By immersion in acetate buffer (pH 4.5, the CaP capsule released the contained DNA complex. This CaP capsule including a DNA complex is promising as a sustained-release system of DNA complexes for gene therapy.

  4. Photon absorption of calcium phosphate-based dental biomaterials

    International Nuclear Information System (INIS)

    Singh, V. P.; Badiger, N. M.; Tekin, H. O.; Kara, U.; Vega C, H. R.; Fernandes Z, M. A.

    2017-10-01

    Effective atomic number and mass energy absorption buildup factors for four calcium phosphate-based biomaterials used in dental treatments were calculated for 0.015 to 15 MeV photons. The mass energy absorption coefficients were calculated for 0.5 to 40 mean free paths of photons. In the energy region important for dental radiology the Zeff for all studied biomaterials are larger in comparison to larger energies. In x-rays for dental radiology and the energy absorption buildup factors are low, however CbMDI bio material shows a resonance at 80 keV. (Author)

  5. Microporous calcium phosphate ceramics driving osteogenesis through surface architecture.

    Science.gov (United States)

    Zhang, Jingwei; Barbieri, Davide; ten Hoopen, Hetty; de Bruijn, Joost D; van Blitterswijk, Clemens A; Yuan, Huipin

    2015-03-01

    The presence of micropores in calcium phosphate (CaP) ceramics has shown its important role in initiating inductive bone formation in ectopic sites. To investigate how microporous CaP ceramics trigger osteoinduction, we optimized two biphasic CaP ceramics (i.e., BCP-R and BCP-S) to have the same chemical composition, equivalent surface area per volume, comparable protein adsorption, similar ion (i.e., calcium and phosphate) exchange and the same surface mineralization potential, but different surface architecture. In particular, BCP-R had a surface roughness (Ra) of 325.4 ± 58.9 nm while for BCP-S it was 231.6 ± 35.7 nm. Ceramic blocks with crossing or noncrossing channels of 250, 500, 1000, and 2000 µm were implanted in paraspinal muscle of dogs for 12 weeks. The percentage of bone volume in the channels was not affected by the type of pores (i.e., crossing vs. closed) or their size, but it was greatly influenced by the ceramic type (i.e., BCP-R vs. BCP-S). Significantly, more bone was formed in the channels of BCP-R than in those of BCP-S. Since the two CaP ceramics differed only in their surface architecture, the results hereby demonstrate that microporous CaP ceramics may induce ectopic osteogenesis through surface architecture. © 2014 Wiley Periodicals, Inc.

  6. Nucleation, growth and evolution of calcium phosphate films on calcite.

    Science.gov (United States)

    Naidu, Sonia; Scherer, George W

    2014-12-01

    Marble, a stone composed of the mineral calcite, is subject to chemically induced weathering in nature due to its relatively high dissolution rate in acid rain. To protect monuments and sculpture from corrosion, we are investigating the application of thin layers of hydroxyapatite (HAP) onto marble. The motivation for using HAP is its low dissolution rate and crystal and lattice compatibility with calcite. A mild, wet chemical synthesis route, in which diammonium hydrogen phosphate salt was reacted with marble, alone and with cationic and anionic precursors under different reaction conditions, was used to produce inorganic HAP layers on marble. Nucleation and growth on the calcite substrate was studied, as well as metastable phase evolution, using scanning electron microscopy, grazing incidence X-ray diffraction, and atomic force microscopy. Film nucleation was enhanced by surface roughness. The rate of nucleation and the growth rate of the film increased with cationic (calcium) and anionic (carbonate) precursor additions. Calcium additions also influenced phase formation, introducing a metastable phase (octacalcium phosphate) and a different phase evolution sequence. Copyright © 2014 Elsevier Inc. All rights reserved.

  7. Microstructural investigation into calcium phosphate biomaterials by spatially resolved cathodoluminescence

    Energy Technology Data Exchange (ETDEWEB)

    Goetze, J.; Heimann, R.B.; Hildebrandt, H. [Freiberg Univ. of Mining and Technology (Germany). Dept. of Mineralogy; Gburek, U. [Wuerzburg Univ. (Germany). Dept. of Experimental Dentistry

    2001-02-01

    From cathodoluminescence (CL) investigations of synthetic and natural calcium phosphates it can be concluded that the CL of pure synthetic apatite is mainly characterized by intrinsic luminescence, whereas the luminescence of naturally occurring apatites is frequently activated by trace elements. CL revealed internal structures within plasma-sprayed hydroxyapatite coatings which were not discernible by SEM-BSE imaging. However, cathodoluminescence microscopy alone can presently not be used in every case to characterize synthetic calcium phosphate biomaterials because of the dominant intrinsic blue CL emission. In the future, optimum results will likely be achieved by using a combination of CL microscopy and spectroscopy with other spatially resolved analytical methods such as SEM-BSE, SEM-CL or micro-Raman spectroscopy. In the present study, different types of tetracalcium phosphate dental cements could be distinguished due to varying CL colours and CL spectra that are caused by a different content of impurity Mn. These results emphasize the advantages of spectral CL measurements for spatially resolved detection of trace elements in solids. (orig.) [German] Ergebnisse von Kathodolumineszenz- (KL-) Untersuchungen synthetischer und natuerlicher Apatite zeigen, dass die KL synthetischer Apatite vorrangig durch intrinsische Lumineszenz gekennzeichnet ist, waehrend die KL natuerlicher Apatite meist durch Spurenlemente aktiviert wird. Mittels KL koennen Internstrukturen in plasmagespritzten Hydroxylapatit-Schichten sichtbar gemacht werden, die im REM-BSE nicht nachweisbar sind. Allerdings kann die KL-Mikroskopie aufgrund der dominierenden blauen intrinsischen Lumineszenz gegenwaertig nicht als alleinige Untersuchungsmethode zur Charakterisierung von Calciumphosphat Biomaterialien eingesetzt werden. Optimale Resultate werden zukuenftig durch Kombination von KL-Mikrroskopie und -spektroskopie mit anderen ortsaufgeloesten analytischen Methoden wie REM-BSE, REM-KL oder Mikro

  8. Interaction between calcium and phosphate adsorption on goethite.

    Science.gov (United States)

    Rietra, R P; Hiemstra, T; van Riemsdijk, W H

    2001-08-15

    Quantitatively, little is known about the ion interaction processes that are responsible for the binding of phosphate in soil, water, and sediment, which determine the bioavailability and mobility of phosphate. Studies have shown that metal hydroxides are often responsible for the binding of PO4 in soils and sediments, but the binding behavior of PO4 in these systems often differs significantly from adsorption studies on metal hydroxides in laboratory. The interaction between PO4 and Ca adsorption was studied on goethite because Ca can influence the PO4 adsorption equilibria. Since adsorption interactions are very difficult to discriminate from precipitation reactions, conditions were chosen to prevent precipitation of Ca-PO4 solids. Adsorption experiments of PO4 and Ca, individually and in combination, show a strong interaction between adsorbed Ca and PO4 on goethite for conditions below the saturation index of apatite. It is shown that it is possible to predict the adsorption and interaction of PO4 and Ca on electrostatic arguments using the model parameter values derived from the single-ion systems and without invoking ternary complex formation or precipitation. The model enables the prediction of the Ca-PO4 interaction for environmentally relevant calcium and phosphate concentrations.

  9. Structure and properties of gadolinium loaded calcium phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Cuiling [Analytical and Testing Center, Southwest University of Science and Technology, Mianyang 621010 (China); State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials, Southwest University of Science and Technology, Mianyang 621010 (China); Liang, Xiaofeng, E-mail: XFLiang@swust.edu.cn [Analytical and Testing Center, Southwest University of Science and Technology, Mianyang 621010 (China); State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials, Southwest University of Science and Technology, Mianyang 621010 (China); Li, Haijian; Yu, Huijun; Li, Zhen [Analytical and Testing Center, Southwest University of Science and Technology, Mianyang 621010 (China); State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials, Southwest University of Science and Technology, Mianyang 621010 (China); Yang, Shiyuan [State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials, Southwest University of Science and Technology, Mianyang 621010 (China)

    2014-10-15

    The glass samples with composition xGd{sub 2}O{sub 3}–(50 − x)CaO–50P{sub 2}O{sub 5} (0 ⩽ x ⩽ 9 mol%) were prepared by the conventional melt quench method. The structure and properties of gadolinium loaded in calcium phosphate glasses were investigated using XRD, SEM, DTA, IR and Raman spectroscopy. The XRD and SEM analysis for the samples show that the majority of samples are amorphous, and crystallization occurs when the content of Gd{sub 2}O{sub 3} containing is up to 6 mol%. Two main crystalline phases, Ca{sub 2}P{sub 2}O{sub 7} and Gd{sub 3}(P{sub 2}O{sub 7}){sub 3}, are embedded in an amorphous matrix. IR and Raman data indicate that glass structure consists of predominantly metaphosphate (Q{sup 2}) units and the depolymerization of phosphate network with the addition of Gd{sub 2}O{sub 3}. Both the chemical durability and the glass transition temperature (T{sub g}) are improved with the increase of Gd{sub 2}O{sub 3}, which suggests that the Gd acts a role of strengthening the cross-links between the phosphate chains of the glass.

  10. Structure and properties of gadolinium loaded calcium phosphate glasses

    International Nuclear Information System (INIS)

    Wang, Cuiling; Liang, Xiaofeng; Li, Haijian; Yu, Huijun; Li, Zhen; Yang, Shiyuan

    2014-01-01

    The glass samples with composition xGd 2 O 3 –(50 − x)CaO–50P 2 O 5 (0 ⩽ x ⩽ 9 mol%) were prepared by the conventional melt quench method. The structure and properties of gadolinium loaded in calcium phosphate glasses were investigated using XRD, SEM, DTA, IR and Raman spectroscopy. The XRD and SEM analysis for the samples show that the majority of samples are amorphous, and crystallization occurs when the content of Gd 2 O 3 containing is up to 6 mol%. Two main crystalline phases, Ca 2 P 2 O 7 and Gd 3 (P 2 O 7 ) 3 , are embedded in an amorphous matrix. IR and Raman data indicate that glass structure consists of predominantly metaphosphate (Q 2 ) units and the depolymerization of phosphate network with the addition of Gd 2 O 3 . Both the chemical durability and the glass transition temperature (T g ) are improved with the increase of Gd 2 O 3 , which suggests that the Gd acts a role of strengthening the cross-links between the phosphate chains of the glass

  11. The increasing of enamel calcium level after casein phosphopeptideamorphous calcium phosphate covering

    Directory of Open Access Journals (Sweden)

    Widyasri Prananingrum

    2012-06-01

    Full Text Available Background: Caries process is characterized by the presence of demineralization. Demineralization is caused by organic acids as a result of carbohydrate substrate fermentation. Remineralization is a natural repair process for non-cavitated lesions. Remineralization occurs if there are Ca2+ and PO43- ions in sufficient quantities. Casein-amorphous calcium phosphate phosphopeptide (CPP-ACP is a paste material containing milk protein (casein, that actually contains minerals, such as calcium and phosphate. The casein ability to stabilize calcium phosphate and enhance mineral solubility and bioavailability confers upon CPP potential to be biological delivery vehicles for calcium and phosphate. Purpose: The aim of this study was to determine the calcium levels in tooth enamel after being covered with CPP-ACP 2 times a day for 3, 14 and 28 days. Methods: Sample were bovine incisors of 3 year old cows divided into 4 groups, namely group I as control group, group II, III and IV as treatment groups covered with CPP-ACP 2 times a day. All of those teeth were then immersed in artificial saliva. Group II was immersed for 3 days, while group III was immersed for 14 days, and group IV was immersed for 28 days. One drop of CPP-ACP was used to cover the entire labial surface of teeth. The measurement of the calcium levels was then conducted by using titration method. All data were analyzed by One- Way ANOVA test with 5% degree of confidence. Results: The results showed significant difference of the calcium levels in tooth enamel of those groups after covered with CPP-ACP 2 times a day for 3, 14 and 28 days (p = 0.001. There is also significant difference of the calcium levels in tooth enamel of those treatment groups and the control group (p = 0.001. Conclusion: The calcium levels of tooth enamel are increased after covered with CPP-ACP 2 times a day for 3, 14 and 28 days.Latar belakang: Proses terjadinya karies gigi ditandai oleh adanya demineralisasi

  12. Biocompatibility of calcium phosphate bone cement with optimised mechanical properties: an in vivo study.

    Science.gov (United States)

    Palmer, Iwan; Nelson, John; Schatton, Wolfgang; Dunne, Nicholas J; Buchanan, Fraser; Clarke, Susan A

    2016-12-01

    This work establishes the in vivo performance of modified calcium phosphate bone cements for vertebroplasty of spinal fractures using a lapine model. A non-modified calcium phosphate bone cement and collagen-calcium phosphate bone cements composites with enhanced mechanical properties, utilising either bovine collagen or collagen from a marine sponge, were compared to a commercial poly(methyl methacrylate) cement. Conical cement samples (8 mm height × 4 mm base diameter) were press-fit into distal femoral condyle defects in New Zealand White rabbits and assessed after 5 and 10 weeks. Bone apposition and tartrate-resistant acid phosphatase activity around cements were assessed. All implants were well tolerated, but bone apposition was higher on calcium phosphate bone cements than on poly(methyl methacrylate) cement. Incorporation of collagen showed no evidence of inflammatory or immune reactions. Presence of positive tartrate-resistant acid phosphatase staining within cracks formed in calcium phosphate bone cements suggested active osteoclasts were present within the implants and were actively remodelling within the cements. Bone growth was also observed within these cracks. These findings confirm the biological advantages of calcium phosphate bone cements over poly(methyl methacrylate) and, coupled with previous work on enhancement of mechanical properties through collagen incorporation, suggest collagen-calcium phosphate bone cement composite may offer an alternative to calcium phosphate bone cements in applications where low setting times and higher mechanical stability are important.

  13. The effects of excess calcium on the handling and mechanical properties of hydrothermal derived calcium phosphate bone cement

    Science.gov (United States)

    Razali, N. N.; Sukardi, M. A.; Sopyan, I.; Mel, M.; Salleh, H. M.; Rahman, M. M.

    2018-01-01

    The objective of this study is to determine the effects of excess calcium on the handling and mechanical properties of hydrothermal derived calcium phosphate cement (CPC) for bone filling applications. Hydroxyapatite powder was synthesized via hydrothermal method using calcium oxide, CaO and ammonium dihydrogen phosphate, NH4H2PO4 as the calcium and phosphorus precursors respectively. The effects of calcium excess were evaluated by varying the CaO content at 0, 5 and 15 mole %. The precursors were then refluxed in distilled water at 90-100°C and dried overnight until the calcium phosphate powder was formed. CPC was then produced by mixing the synthesized powder with distilled water at the powder-to-liquid (P/L) ratio of 1.5. The result from the morphological properties of CPC shows the increase in agglomeration and particles size with 5 mole % of calcium excess but decreased with 15 mole % of calcium excess in CPC. This result was in agreement with the compressive strength result where the CPC increased its strength with 5 mole % of calcium excess but reduced with 15 mole % of calcium excess. The excess in calcium precursor also significantly improved the setting time but reduced the injectability of CPC.

  14. Calcium phosphate nuclear materials: apatitic ceramics for separated wastes

    International Nuclear Information System (INIS)

    Carpena, J.; Lacout, J.L.

    2005-01-01

    Is it feasible to elaborate conditioning materials for separated high activity nuclear wastes, as actinides or fission products? Specific materials have been elaborated so that the waste is incorporated within the crystalline structure of the most stable calcium phosphate, i.e. apatite. This mineral is able to sustain high irradiation doses assuming a well chosen chemical composition. Mainly two different ways of synthesis have been developed to produce hard apatite ceramics that can be used to condition nuclear wastes. Here we present a data synthesis regarding the elaboration of these apatite nuclear materials that includes experiments on crystallo-chemistry, chemical analysis, leaching and irradiation tests performed for the past fifteen years. (authors)

  15. Structure and Degradation Behaviour of Calcium Phosphate Glasses

    International Nuclear Information System (INIS)

    Silva, A M B; Correia, R N; Fernandes, M H V; Oliveira, J M M

    2011-01-01

    Some studies have shown a relationship between glass structure and in vitro mineralization, generally associated with the rate of glass degradation, nature of released ions and subsequent Ca-P precipitation on glass surfaces when immersed in a Simulated Body Fluid (SBF). The knowledge of the ionic species distribution in glasses and of the involved bond strengths can be used to assess the in vitro behaviour of a glass. The role of ions such as silicon or titanium is of major importance for the development of new compositions and also for the control of glass degradation behaviour. A comparative study with two calcium phosphate glasses series was performed: Both glasses series - one with Si and another with Ti - include P 2 O 5 and alkaline earth ions in their compositions. Surface reactivity of glasses from the SiO 2 -containing system have been studied in SBF showing the precipitation of a Ca-P surface layer that increases with increasing MgO/CaO ratio. In glasses from the TiO 2 -containing series it is shown that the increase of TiO 2 contributes for the stabilization of the glass network thus allowing the control of their degradation rate when immersed in SBF. The relationship between structural features of these calcium-phosphate glasses and their degradation behaviour in SBF is discussed in terms of the structural role of Si and Ti ions. It is concluded that glasses with less interconnected species favour the Ca-P surface precipitation. The understanding of this relationship in synthetic physiological fluids is expected to allow the tailoring of glass degradation rates in complex biological systems.

  16. Characterization of a calcium phosphate cement based on alpha-tricalcium phosphate obtained by wet precipitation process

    International Nuclear Information System (INIS)

    Thurmer, M.B.; Diehl, C.E.; Vieira, R.S.; Coelho, W.T.G.; Santos, L.A.

    2012-01-01

    There are several systems of calcium phosphate cements being studied. Those based on alpha-tricalcium phosphate are of particular interest. After setting they produce calcium deficient hydroxyapatite similar to bone like hydroxyapatite. This work aims to obtain alpha-tricalcium phosphate powders by the wet precipitation process, using calcium nitrate and phosphoric acid as reagents. This powder was characterized by infrared spectroscopy, X-ray diffraction and particle size distribution. In order to prepare the calcium phosphate cement, the powder was mixed with an accelerator in an aqueous solution. The mechanical properties of the cement were assessed and it was evaluated by means of apparent density, X-ray diffraction and scanning electron microscopy. The described method produced crystalline alpha-tricalcium phosphate as the major phase. The calcium phosphate cement showed high values of compression strength (50 MPa). The soaking of the cement in a simulated body fluid (SBF) formed a layer of hydroxyapatite like crystals in the surface of the samples. (author)

  17. Inflammatory cell response to calcium phosphate biomaterial particles: an overview.

    Science.gov (United States)

    Velard, Frédéric; Braux, Julien; Amedee, Joëlle; Laquerriere, Patrice

    2013-02-01

    Bone is a metabolically active and highly organized tissue consisting of a mineral phase of hydroxyapatite (HA) and amorphous calcium phosphate (CaP) crystals deposited in an organic matrix. One objective of bone tissue engineering is to mimic the chemical and structural properties of this complex tissue. CaP ceramics, such as sintered HA and beta-tricalcium phosphate, are widely used as bone substitutes or prosthesis coatings because of their osteoconductive properties. These ceramic interactions with tissues induce a cell response that can be different according to the composition of the material. In this review, we discuss inflammatory cell responses to CaP materials to provide a comprehensive overview of mechanisms governing the integration or loosening of implants, which remains a major concern in tissue engineering. A focus on the effects of the functionalization of CaP biomaterials highlights potential ways to increase tissue integration and limit rejection processes. Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  18. Preparation and bioactivity of micro-arc oxidized calcium phosphate coatings

    International Nuclear Information System (INIS)

    Pan, Y.K.; Chen, C.Z.; Wang, D.G.; Lin, Z.Q.

    2013-01-01

    Calcium phosphate (CaP) coatings were prepared on ZK60 magnesium alloy by micro-arc oxidation (MAO) in electrolyte containing calcium acetate monohydrate (CH 3 COO) 2 Ca·H 2 O) and disodium hydrogen phosphate dodecahydrate (Na 2 HPO 4 ·12H 2 O). Scanning electron microscope (SEM), energy-dispersive X-ray spectrometry (EDX) and X-ray diffractometer (XRD) were employed to characterize the microstructure, elemental distribution and phase composition of the CaP coatings respectively. Simulated body fluid (SBF) immersion test was used to evaluate the coating degradability and bioactivity. After 30 days of SBF immersion, the CaP coatings effectively reduce the degradation rate. The surfaces of CaP coatings are covered by a new layer formed of numerous needle-like, spherical and columned calcium phosphates. SEM, EDX and XRD results suggest that these calcium phosphates are bioactive calcium phosphate phases such as hydroxyapatite (Ca 10 (PO 4 ) 6 (OH) 2 , HA) and calcium pyrophosphates (Ca 2 P 2 O 7 , CPP). The formation of these calcium phosphates indicates that the CaP coatings have bioactivity. - Highlights: • Bioactive CaP coatings are successfully formed on ZK60 magnesium alloy. • CaP coatings consist of MgO, MgF 2 , CaO, CaF 2 and Ca 3 (PO 4 ) 2 . • Needle-like, spherical and columned calcium phosphates formed in SBF. • CaP coatings exhibit bioactivity and low corrosion rate

  19. Silver-Doped Calcium Phosphate Bone Cements with Antibacterial Properties

    Directory of Open Access Journals (Sweden)

    J. V. Rau

    2016-04-01

    Full Text Available Calcium phosphate bone cements (CPCs with antibacterial properties are demanded for clinical applications. In this study, we demonstrated the use of a relatively simple processing route based on preparation of silver-doped CPCs (CPCs-Ag through the preparation of solid dispersed active powder phase. Real-time monitoring of structural transformations and kinetics of several CPCs-Ag formulations (Ag = 0 wt %, 0.6 wt % and 1.0 wt % was performed by the Energy Dispersive X-ray Diffraction technique. The partial conversion of β-tricalcium phosphate (TCP phase into the dicalcium phosphate dihydrate (DCPD took place in all the investigated cement systems. In the pristine cement powders, Ag in its metallic form was found, whereas for CPC-Ag 0.6 wt % and CPC-Ag 1.0 wt % cements, CaAg(PO33 was detected and Ag (met. was no longer present. The CPC-Ag 0 wt % cement exhibited a compressive strength of 6.5 ± 1.0 MPa, whereas for the doped cements (CPC-Ag 0.6 wt % and CPC-Ag 1.0 wt % the reduced values of the compressive strength 4.0 ± 1.0 and 1.5 ± 1.0 MPa, respectively, were detected. Silver-ion release from CPC-Ag 0.6 wt % and CPC-Ag 1.0 wt % cements, measured by the Atomic Emission Spectroscopy, corresponds to the average values of 25 µg/L and 43 µg/L, respectively, rising a plateau after 15 days. The results of the antibacterial test proved the inhibitory effect towards pathogenic Escherichia coli for both CPC-Ag 0.6 wt % and CPC-Ag 1.0 wt % cements, better performances being observed for the cement with a higher Ag-content.

  20. Reinforcement of calcium phosphate cement with multi-walled carbon nanotubes and bovine serum albumin for injectable bone substitute applications

    NARCIS (Netherlands)

    Chew, K.K.; Low, K.L.; Zein, S.H.S.; McPhail, D.; Gerhardt, L.C.; Roether, J.A.; Boccaccini, A.R.

    2011-01-01

    This paper presents the development of novel alternative injectable calcium phosphate cement (CPC) composites for orthopaedic applications. The new CPC composites comprise ß-tri-calcium phosphate (ß-TCP) and di-calcium phosphate anhydrous (DCPA) mixed with bovine serum albumin (BSA) and incorporated

  1. Development of a degradable cement of calcium phosphate and calcium sulfate composite for bone reconstruction

    International Nuclear Information System (INIS)

    Guo, H; Wei, J; Liu, C S

    2006-01-01

    A new type of composite bone cement was prepared and investigated by adding calcium sulfate (CS) to calcium phosphate cement (CPC). This composite cement can be handled as a paste and easily shaped into any contour, which can set within 5-20 min, the setting time largely depending on the liquid-solid (L/S) ratio; adding CS to CPC had little effect on the setting time of the composite cements. No obvious temperature increase and pH change were observed during setting and immersion in simulated body fluid (SBF). The compressive strength of the cement decreased with an increase in the content of CS. The degradation rate of the composite cements increased with time when the CS content was more than 20 wt%. Calcium deficient apatite could form on the surface of the composite cement because the release of calcium into SBF from the dissolution of CS and the apatite of the cement induced the new apatite formation; increasing the content of CS in the composite could improve the bioactivity of the composite cements. The results suggested that composite cement has a reasonable setting time, excellent degradability and suitable mechanical strength and bioactivity, which shows promising prospects for development as a clinical cement

  2. Interaction of bovine gallbladder mucin and calcium-binding protein: effects on calcium phosphate precipitation.

    Science.gov (United States)

    Afdhal, N H; Ostrow, J D; Koehler, R; Niu, N; Groen, A K; Veis, A; Nunes, D P; Offner, G D

    1995-11-01

    Gallstones consist of calcium salts and cholesterol crystals, arrayed on a matrix of gallbladder mucin (GBM), and regulatory proteins like calcium-binding protein (CBP). To determine if interactions between CBP and GBM follow a biomineralization scheme, their mutual binding and effects on CaHPO4 precipitation were studied. Binding of CBP to GBM was assessed by inhibition of the fluorescence of the complex of GBM with bis-1,8-anilinonaphthalene sulfonic acid (bis-ANS). The effects of the proteins on precipitation of CaHPO4 were assessed by nephelometry and gravimetry. Precipitates were analyzed for calcium, phosphate, and protein. CBP and bis-ANS competitively displaced each other from 30 binding sites on mucin, with a 1:1 stoichiometry and similar affinity. The rate of precipitation of CaHPO4 was retarded by mucin and CBP. Precipitate mass was unaffected by GBM alone but decreased with the addition of CBP. Complexing CBP with GBM abolished or moderated this latter effect, altered precipitate morphology, and changed the stoichiometric ratios of Ca to PO4 in the precipitates from 1:1 to 3:2. Mucin and CBP were incorporated into the precipitates. These studies suggest that the formation of calcium-containing gallstones is a biomineralization process regulated by both GBM and CBP.

  3. Preparation of in situ hardening composite microcarriers: Calcium phosphate cement combined with alginate for bone regeneration

    Science.gov (United States)

    Park, Jung-Hui; Lee, Eun-Jung; Knowles, Jonathan C

    2014-01-01

    Novel microcarriers consisting of calcium phosphate cement and alginate were prepared for use as three-dimensional scaffolds for the culture and expansion of cells that are effective for bone tissue engineering. The calcium phosphate cement-alginate composite microcarriers were produced by an emulsification of the composite aqueous solutions mixed at varying ratios (calcium phosphate cement powder/alginate solution = 0.8–1.2) in an oil bath and the subsequent in situ hardening of the compositions during spherodization. Moreover, a porous structure could be easily created in the solid microcarriers by soaking the produced microcarriers in water and a subsequent freeze-drying process. Bone mineral-like apatite nanocrystallites were shown to rapidly develop on the calcium phosphate cement–alginate microcarriers under moist conditions due to the conversion of the α-tricalcium phosphate phase in the calcium phosphate cement into a carbonate–hydroxyapatite. Osteoblastic cells cultured on the microspherical scaffolds were proven to be viable, with an active proliferative potential during 14 days of culture, and their osteogenic differentiation was confirmed by the determination of alkaline phosphatase activity. The in situ hardening calcium phosphate cement–alginate microcarriers developed herein may be used as potential three-dimensional scaffolds for cell delivery and tissue engineering of bone. PMID:23836845

  4. Dibasic calcium phosphate dihydrate, USP material compatibility with gamma radiation

    Science.gov (United States)

    Betancourt Quiles, Maritza

    Gamma radiation is a commonly used method to reduce the microbial bioburden in compatible materials when it is applied at appropriate dose levels. Gamma irradiation kills bacteria and mold by breaking down the organism’s DNA and inhibiting cell division. The purpose of this study is to determine the radiation dosage to be used to treat Dibasic Calcium Phosphate Dihydrate, USP (DCPD) and to evaluate its physicochemical effects if any, on this material. This material will be submitted to various doses of gamma radiation that were selected based on literature review and existing regulations that demonstrate that this method is effective to reduce or eliminate microbial bioburden in natural source and synthetic materials. Analytical testing was conducted to the DCPD exposed material in order to demonstrate that gamma radiation does not alter the physicochemical properties and material still acceptable for use in the manufacture of pharmaceutical products. The results obtained through this study were satisfactory and demonstrated that the gamma irradiation dosages from 5 to 30 kGy can be applied to DCPD without altering its physicochemical properties. These are supported by the Assay test data evaluation of lots tested before and after gamma irradiation implementation that show no significant statistical difference between irradiated and non irradiated assay results. The results of this study represent an achievement for the industry since they provide as an alternative the use of Gamma irradiation technology to control the microbial growth in DCPD.

  5. Incorporation of iodine into calcium phosphates with apatitic structure

    International Nuclear Information System (INIS)

    Coulon, Antoine

    2014-01-01

    In order to avoid the release of 129 I (long-lived intermediate-level waste) in the environment, we describe a novel material incorporating iodine under the form of iodate in a calcium phosphate based hydroxyapatite. This material is prepared by two synthetic processes: a wet precipitation route followed by a spark plasma sintering and a cementitious route. A high iodine content (with a maximum incorporation rate of 10 wt.%) is reached for both processes, by incorporation of the iodate in the apatitic structure. A monolith with relative density of 88.6% was obtained after shaping of the precipitated powders by spark plasma sintering. This material reveals satisfactory leaching properties, with an initial leaching rate in pure water at 50 C of 10 -2 g.m -2 .j -1 , and a residual leaching rate at 50 C of 10 -5 g.m -2 .j -1 in underground water of potential geological repositories. All in all, this material is a potential candidate for the conditioning of radioactive iodine. (author) [fr

  6. Biocompatibility of calcium phosphate bone cement with optimized mechanical properties.

    Science.gov (United States)

    Palmer, Iwan; Nelson, John; Schatton, Wolfgang; Dunne, Nicholas J; Buchanan, Fraser J; Clarke, Susan A

    2016-02-01

    The broad aim of this work was to investigate and optimize the properties of calcium phosphate bone cements (CPCs) for use in vertebroplasty to achieve effective primary fixation of spinal fractures. The incorporation of collagen, both bovine and from a marine sponge (Chondrosia reniformis), into a CPC was investigated. The biological properties of the CPC and collagen-CPC composites were assessed in vitro through the use of human bone marrow stromal cells. Cytotoxicity, proliferation, and osteoblastic differentiation were evaluated using lactate dehydrogenase, PicoGreen, and alkaline phosphatase activity assays, respectively. The addition of both types of collagen resulted in an increase in cytotoxicity, albeit not to a clinically relevant level. Cellular proliferation after 1, 7, and 14 days was unchanged. The osteogenic potential of the CPC was reduced through the addition of bovine collagen but remained unchanged in the case of the marine collagen. These findings, coupled with previous work showing that incorporation of marine collagen in this way can improve the physical properties of CPCs, suggest that such a composite may offer an alternative to CPCs in applications where low setting times and higher mechanical stability are important. © 2015 The Authors. Journal of Biomedical Materials Research Part B: Applied Biomaterials Published by Wiley Periodicals, Inc.

  7. Fabrication and characterization of calcium phosphate cement scaffolds

    International Nuclear Information System (INIS)

    Sousa, E. de; Motisuke, M.; Bertran, C.A.

    2011-01-01

    In Tissue Engineering, the need for scaffolds which are capable of guiding the organization, differentiation and growth of cells leading to the formation of new tissues is highly relevant. For the development of new scaffolds focused on bone tissue therapy, calcium phosphate cements (CPC) have great potential, because besides their resorbability, they present morphology and chemical composition similar to the bone mineral phase. Moreover, there are several processing techniques to produce ceramic scaffolds: polymeric sponge replication, incorporation of organic material into the ceramic powder, gelcasting, emulsion, among others. The aim of this work was to obtain CPCs scaffolds by using two techniques, emulsion and gelcasting. The scaffolds were characterized by their physical and mechanical properties and the crystalline phases formed after the setting reaction of cement were determined by X-ray diffraction. The samples obtained by both methods presented porosity between 61-65% and the microstructure consists of nearly spherical pores (d5o = 50-100 μm). The mechanical strength of the samples ranged from 5.5 to 1.5 MPa. The crystalline phases found were monetite (CaHPO 4 ) and brushite (CaHPO 4 2H 2 O). (author)

  8. Control of surface topography in biomimetic calcium phosphate coatings.

    Science.gov (United States)

    Costa, Daniel O; Allo, Bedilu A; Klassen, Robert; Hutter, Jeffrey L; Dixon, S Jeffrey; Rizkalla, Amin S

    2012-02-28

    The behavior of cells responsible for bone formation, osseointegration, and bone bonding in vivo are governed by both the surface chemistry and topography of scaffold matrices. Bone-like apatite coatings represent a promising method to improve the osteoconductivity and bonding of synthetic scaffold materials to mineralized tissues for regenerative procedures in orthopedics and dentistry. Polycaprolactone (PCL) films were coated with calcium phosphates (CaP) by incubation in simulated body fluid (SBF). We investigated the effect of SBF ion concentration and soaking time on the surface properties of the resulting apatite coatings. CaP coatings were examined by scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transform infrared spectrometry (FTIR), and energy dispersive X-ray spectrometry (EDX). Young's modulus (E(s)) was determined by nanoindentation, and surface roughness was assessed by atomic force microscopy (AFM) and mechanical stylus profilometry. CaP such as carbonate-substituted apatite were deposited onto PCL films. SEM and AFM images of the apatite coatings revealed an increase in topographical complexity and surface roughness with increasing ion concentration of SBF solutions. Young's moduli (E(s)) of various CaP coatings were not significantly different, regardless of the CaP phase or surface roughness. Thus, SBF with high ion concentrations may be used to coat synthetic polymers with CaP layers of different surface topography and roughness to improve the osteoconductivity and bone-bonding ability of the scaffold. © 2012 American Chemical Society

  9. Periodontal regeneration using a bilayered PLGA/calcium phosphate construct.

    Science.gov (United States)

    Carlo Reis, Emily C; Borges, Andréa P B; Araújo, Michel V F; Mendes, Vanessa C; Guan, Limin; Davies, John E

    2011-12-01

    The regeneration of tissues affected by periodontal disease is a complex process; it encompasses the formation of bone, cementum and periodontal ligament. We developed a semi-rigid PLGA (polylactide-co-glycolide acid)/CaP (calcium phosphate) bilayered biomaterial construct to promote periodontal regeneration, which has a continuous outer barrier membrane and an inner topographically complex component. Our experimental model compared periodontal prophylaxis alone with prophylaxis and biomaterial implantation in the treatment of class II furcation defects in dogs. Clinical evaluation, micro-computed tomography, histology and backscattered electron imaging were used for data analysis. Healing occurred uneventfully and bone volumetric values, trabecular number and trabecular thickness were all significantly greater in the treated group; while trabecular separation was significantly greater in the control group. New cementum, bone, and periodontal ligament with Sharpey fibre insertions were only seen in the treated group. Although periodontal regeneration has been reported elsewhere, the advantages of employing our bilayered PLGA + CaP construct are twofold: 1)it did not collapse into the defect; and, 2) its inner side was able to retain the blood clot throughout the buccal defect. The result was greater periodontal regeneration than has previously been reported with traditional flexible membranes. Copyright © 2011 Elsevier Ltd. All rights reserved.

  10. A randomised study to compare salivary pH, calcium, phosphate and calculus formation after using anticavity dentifrices containing Recaldent(®) and functionalized tri-calcium phosphate.

    Science.gov (United States)

    Sharma, Ena; Vishwanathamurthy, Ramesh Alampalli; Nadella, Manjari; Savitha, A N; Gundannavar, Gayatri; Hussain, M Ahad

    2012-10-01

    The aim of this study was to estimate the pH of saliva, concentration of calcium and inorganic phosphate, and calculus formation before and after usage of Recaldent(®) (GC Tooth Mousse Plus™), Functionalized Tricalcium Phosphate (3M ESPE ClinPro™ Tooth Crème) and standard dentifrice (Colgate dental cream). Randomized double-blind study. A total of 50 subjects were recruited, the subjects were assessed at their first visit, on the 21(st) day and on the 42(nd) day. At the first visit, scaling was carried out and oral hygiene instructions were given. After 21 days, the subjects were given coded dentifrices where the operator and the subjects both were unaware of the type of dentifrice. Clinical parameters assessed were Plaque index, Gingival index, and Calculus index. Salivary samples were obtained to measure calcium, phosphate levels, and pH at 21(st) day and 42(nd) day. ANOVA test, t-test, Mann-Whitney test, Kruskal-Wallis test. The mean salivary calcium level and mean salivary phosphate level were higher in Group III (functionalized tricalcium phosphate (3M ESPE ClinPro™ Tooth Creme) as compared to Group II (Recaldent(®) GC Tooth Mousse Plus™) and Group I (Colgate dental cream) on the 42(nd) day after using dentifrices, which was statistically significant. This showed that the usage of remineralizing dentifrices led to an increase in the salivary calcium, phosphate, and pH but it did not reach the level of super saturation of the ions caused by elevated pH which could lead to calculus formation. Thought here was a statistically significant increase in salivary calcium and phosphate level in all three groups from baseline to 42(nd) day, there was no calculus formation.

  11. Characterization of a silver-incorporated calcium phosphate film by RBS and its antimicrobial effects

    International Nuclear Information System (INIS)

    Han, I-H; Lee, I-S; Song, J-H; Lee, M-H; Park, J-C; Lee, G-H; Sun, X-D; Chung, S-M

    2007-01-01

    A thin calcium phosphate film was synthesized on both commercially pure Ti and Si wafers by electron beam evaporation of hydroxyapatite as an evaporant with simultaneous Ar ion beam bombardments. Silver was introduced into an ion-beam-assisted deposition of a calcium phosphate thin film for antimicrobial effect. The amount of incorporated silver ions was controlled by immersing calcium-phosphate-coated samples in different AgNO 3 concentrations, and Rutherford backscattering spectrometry (RBS) was employed to measure the amounts of substituted silver. The higher concentration of silver in the calcium phosphate film was more effective in reducing the bacteria of Escherichia coli ATCC 8739 and Streptococcus mutans OMZ 65 on contact with respect to controls

  12. Characterization of a silver-incorporated calcium phosphate film by RBS and its antimicrobial effects

    Energy Technology Data Exchange (ETDEWEB)

    Han, I-H [Institute of Physics and Applied Physics, and Atomic-Scale Surface Science Research Center, Yonsei University, Seou1 120-749 (Korea, Republic of); Lee, I-S [Institute of Physics and Applied Physics, and Atomic-Scale Surface Science Research Center, Yonsei University, Seou1 120-749 (Korea, Republic of); Song, J-H [Advanced Analysis Center, Korea Institute of Science and Technology, Seoul 136-791 (Korea, Republic of); Lee, M-H [Department of Medical Engineering, Yonsei University, Seoul 120-752 (Korea, Republic of); Park, J-C [Department of Medical Engineering, Yonsei University, Seoul 120-752 (Korea, Republic of); Lee, G-H [Korea Institute of Machinery and Materials, Chang-Won 641-010 (Korea, Republic of); Sun, X-D [Department of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China); Chung, S-M [Implantium Research Center, Seoul 135-879 (Korea, Republic of)

    2007-09-15

    A thin calcium phosphate film was synthesized on both commercially pure Ti and Si wafers by electron beam evaporation of hydroxyapatite as an evaporant with simultaneous Ar ion beam bombardments. Silver was introduced into an ion-beam-assisted deposition of a calcium phosphate thin film for antimicrobial effect. The amount of incorporated silver ions was controlled by immersing calcium-phosphate-coated samples in different AgNO{sub 3} concentrations, and Rutherford backscattering spectrometry (RBS) was employed to measure the amounts of substituted silver. The higher concentration of silver in the calcium phosphate film was more effective in reducing the bacteria of Escherichia coli ATCC 8739 and Streptococcus mutans OMZ 65 on contact with respect to controls.

  13. Drug Release Profile from Calcium-Induced Alginate-Phosphate Composite Gel Beads

    Directory of Open Access Journals (Sweden)

    Yoshifumi Murata

    2009-01-01

    Full Text Available Calcium-induced alginate-phosphate composite gel beads were prepared, and model drug release profiles were investigated in vitro. The formation of calcium phosphate in the alginate gel matrix was observed and did not affect the rheological properties of the hydrogel beads. X-ray diffraction patterns showed that the calcium phosphate does not exist in crystalline form in the matrix. The initial release amount and release rate of a water-soluble drug, diclofenac, from the alginate gel beads could be controlled by modifying the composition of the matrix with calcium phosphate. In contrast, the release profile was not affected by the modification for hydrocortisone, a drug only slightly soluble in water.

  14. Polyelectrolyte addition effect on the properties of setting hydraulic cements based on calcium phosphate

    International Nuclear Information System (INIS)

    Santos, Luis A. dos; Oliveira, Luci C. de; Rigo, Eliana C.S.; Boschi, Anselmo Ortega; Carrodeguas, Raul Gracia

    1997-01-01

    In the present work the effects of the addition of some poly electrolytes (sodium alginate and poly acrylic acid) on the solubility, crystalline phases, pH and mechanical strength under compression of three calcium phosphate cements were studied. (author)

  15. Production and characterization of setting hydraulic cements based on calcium phosphate

    International Nuclear Information System (INIS)

    Oliveira, Luci C. de; Rigo, Eliana C.S.; Santos, Luis A dos; Boschi, Anselmo Ortega; Carrodeguas, Raul G.

    1997-01-01

    Setting hydraulic cements based on calcium phosphate has risen great interest in scientific literature during recent years due to their total bio compatibility and to the fact that they harden 'in situ', providing easy handling and adaptation to the shape and dimensions of the defect which requires correction, differently from the predecessors, the calcium phosphate ceramics (Hydroxy apatite, β-tri calcium phosphate, biphasic, etc) in the shape of dense or porous blocks and grains. In the work, three calcium-phosphate cement compositions were studied. The resulting compositions were characterized according to the following aspects: setting times, pH, mechanical resistance, crystalline phases, microstructure and solubility in SBF (Simulated Body Fluid). The results show a potential use for the compositions. (author)

  16. RBS and XPS analyses of the composite calcium phosphate coatings for biomedical applications

    International Nuclear Information System (INIS)

    Ide-Ektessabi, Ari; Yamaguchi, Tetsuro; Tanaka, Yoshikazu

    2005-01-01

    The calcium phosphate coatings on metallic implants are widely used for biomedical applications. The calcium phosphate coatings require mechanical strength, strong adhesion to the metallic implants, chemical stability and low dissolution into the human body fluid for stable functioning in the corrosive environment of the human body. In this study, a novel approach for improving the calcium phosphate coatings is utilized by adding trace metallic element into the coatings. We focused on teeth enamel, which is the hardest calcium phosphate tissue in the human body. Zn concentration increases exponentially from the interior to the surface of the enamel. As the Zn concentration increases, so the local hardness increases. Our previous studies suggest that Zn has influence on the hardness and other properties of enamel, calcium phosphate tissue. Calcium phosphate coatings doped with Zn was fabricated and characterized. The atomic composition and chemical state were investigated by using Rutherford backscattering spectroscopy (RBS) and X-ray photoelectron spectrometer (XPS), respectively. Scratch test was also carried out for measuring the adhesion of the coatings

  17. Effects of calcium phosphate/chitosan composite on bone healing in rats: calcium phosphate induces osteon formation.

    Science.gov (United States)

    Fernández, Tulio; Olave, Gilberto; Valencia, Carlos H; Arce, Sandra; Quinn, Julian M W; Thouas, George A; Chen, Qi-Zhi

    2014-07-01

    Vascularization of an artificial graft represents one of the most significant challenges facing the field of bone tissue engineering. Over the past decade, strategies to vascularize artificial scaffolds have been intensively evaluated using osteoinductive calcium phosphate (CaP) biomaterials in animal models. In this work, we observed that CaP-based biomaterials implanted into rat calvarial defects showed remarkably accelerated formation and mineralization of new woven bone in defects in the initial stages, at a rate of ∼60 μm/day (0.8 mg/day), which was considerably higher than normal bone growth rates (several μm/day, 0.1 mg/day) in implant-free controls of the same age. Surprisingly, we also observed histological evidence of primary osteon formation, indicated by blood vessels in early-region fibrous tissue, which was encapsulated by lamellar osteocyte structures. These were later fully replaced by compact bone, indicating complete regeneration of calvarial bone. Thus, the CaP biomaterial used here is not only osteoinductive, but vasculogenic, and it may have contributed to the bone regeneration, despite an absence of osteons in normal rat calvaria. Further investigation will involve how this strategy can regulate formation of vascularized cortical bone such as by control of degradation rate, and use of models of long, dense bones, to more closely approximate repair of human cortical bone.

  18. Enzymatic pH control for biomimetic deposition of calcium phosphate coatings

    NARCIS (Netherlands)

    Nijhuis, A.W.G.; Nejadnik, M.R.; Nudelman, F.; Walboomers, X.F.; Riet, J. te; Habibovic, P.; Tahmasebi Birgani, Z.; Li, Y.; Bomans, P.H.; Jansen, J.A.; Sommerdijk, N.A.; Leeuwenburgh, S.C.G.

    2014-01-01

    The current study examines the enzymatic decomposition of urea into carbon dioxide and ammonia as a means to increase the pH during biomimetic deposition of calcium phosphate (CaP) onto implant surfaces. The kinetics of the enzymatically induced pH increase were studied by monitoring pH, calcium

  19. Calcium carbonate-calcium phosphate mixed cement compositions for bone reconstruction.

    Science.gov (United States)

    Combes, C; Bareille, R; Rey, C

    2006-11-01

    The feasibility of making calcium carbonate-calcium phosphate (CaCO(3)-CaP) mixed cements, comprising at least 40% (w/w) CaCO(3) in the dry powder ingredients, has been demonstrated. Several original cement compositions were obtained by mixing metastable crystalline CaCO(3) phases with metastable amorphous or crystalline CaP powders in aqueous medium. The cements set within at most 1 h at 37 degrees C in atmosphere saturated with water. The hardened cement is microporous and exhibits weak compressive strength. The setting reaction appeared to be essentially related to the formation of a highly carbonated nanocrystalline apatite phase by reaction of the metastable CaP phase with part or almost all of the metastable CaCO(3) phase. The recrystallization of metastable CaP varieties led to a final cement consisting of a highly carbonated poorly crystalline apatite analogous to bone mineral associated with various amounts of vaterite and/or aragonite. The presence of controlled amounts of CaCO(3) with a higher solubility than that of the apatite formed in the well-developed CaP cements might be of interest to increase resorption rates in biomedical cement and favors its replacement by bone tissue. Cytotoxicity testing revealed excellent cytocompatibility of CaCO(3)-CaP mixed cement compositions.

  20. Nano-sized calcium phosphate particles for periodontal gene therapy.

    Science.gov (United States)

    Elangovan, Satheesh; Jain, Shardool; Tsai, Pei-Chin; Margolis, Henry C; Amiji, Mansoor

    2013-01-01

    Growth factors such as platelet-derived growth factor (PDGF) have significantly enhanced periodontal therapy outcomes with a high degree of variability, mostly due to the lack of continual supply for a required period of time. One method to overcome this barrier is gene therapy. The aim of this in vitro study is to evaluate PDGF-B gene delivery in fibroblasts using nano-sized calcium phosphate particles (NCaPP) as vectors. NCaPP incorporating green fluorescent protein (NCaPP-GFP) and PDGF-B (NCaPP-PDGF-B) plasmids were synthesized using an established precipitation system and characterized using transmission electron microscopy and 1.2% agarose gel electrophoresis. Biocompatibility and transfection of the nanoplexes in fibroblasts were evaluated using cytotoxicity assay and florescence microscopy, respectively. Polymerase chain reaction and enzyme-linked immunosorbent assay were performed to evaluate PDGF-B transfection after different time points of treatments, and the functionality of PDGF-B transfection was evaluated using the cell proliferation assay. Synthesized NCaPP nanoplexes incorporating the genes of GFP and PDGF-B were spherical in shape and measured about 30 to 50 nm in diameter. Gel electrophoresis confirmed DNA incorporation and stability within the nanoplexes, and 3-(4,5-dimethylthiazol-2-yl)-5-(3-carboxymethoxyphenyl)-2-(4-sulfophenyl)-2H-tetrazolium reagent assay demonstrated their biocompatibility in fibroblasts. In vitro transfection studies revealed a higher and longer lasting transfection after NCaPP-PDGF-B treatment, which lasted up to 96 hours. Significantly enhanced fibroblast proliferation observed in NCaPP-PDGF-B-treated cells confirmed the functionality of these nanoplexes. NCaPP demonstrated higher levels of biocompatibility and efficiently transfected PDGF plasmids into fibroblasts under described in vitro conditions.

  1. Calcium phosphate cements with strontium halides as radiopacifiers.

    Science.gov (United States)

    López, Alejandro; Montazerolghaem, Maryam; Engqvist, Håkan; Ott, Marjam Karlsson; Persson, Cecilia

    2014-02-01

    High radiopacity is required to monitor the delivery and positioning of injectable implants. Inorganic nonsoluble radiopacifiers are typically used in nondegradable bone cements; however, their usefulness in resorbable cements is limited due to their low solubility. Strontium halides, except strontium fluoride, are ionic water-soluble compounds that possess potential as radiopacifiers. In this study, we compare the radiopacity, mechanical properties, composition, and cytotoxicity of radiopaque brushite cements prepared with strontium fluoride (SrF2 ), strontium chloride (SrCl2 ·6H2 O), strontium bromide (SrBr2 ), or strontium iodide (SrI2 ). Brushite cements containing 10 wt % SrCl2 ·6H2 O, SrBr2 , or SrI2 exhibited equal to or higher radiopacity than commercial radiopaque cements. Furthermore, the brushite crystal lattice in cements that contained the ionic radiopacifiers was larger than in unmodified cements and in cements that contained SrF2 , indicating strontium substitution. Despite the fact that the strontium halides increased the solubility of the cements and affected their mechanical properties, calcium phosphate cements containing SrCl2 ·6H2 O, SrBr2 , and SrI2 showed no significant differences in Saos-2 cell viability and proliferation with respect to the control. Strontium halides: SrCl2 ·6H2 O, SrBr2 , and SrI2 may be potential candidates as radiopacifiers in resorbable biomaterials although their in vivo biocompatibility, when incorporated into injectable implants, is yet to be assessed. Copyright © 2013 Wiley Periodicals, Inc.

  2. Coupling between phosphate and calcium homeostasis: a mathematical model.

    Science.gov (United States)

    Granjon, David; Bonny, Olivier; Edwards, Aurélie

    2017-12-01

    We developed a mathematical model of calcium (Ca) and phosphate (PO 4 ) homeostasis in the rat to elucidate the hormonal mechanisms that underlie the regulation of Ca and PO 4 balance. The model represents the exchanges of Ca and PO 4 between the intestine, plasma, kidneys, bone, and the intracellular compartment, and the formation of Ca-PO 4 -fetuin-A complexes. It accounts for the regulation of these fluxes by parathyroid hormone (PTH), vitamin D 3 , fibroblast growth factor 23, and Ca 2+ -sensing receptors. Our results suggest that the Ca and PO 4 homeostatic systems are robust enough to handle small perturbations in the production rate of either PTH or vitamin D 3 The model predicts that large perturbations in PTH or vitamin D 3 synthesis have a greater impact on the plasma concentration of Ca 2+ ([Ca 2+ ] p ) than on that of PO 4 ([PO 4 ] p ); due to negative feedback loops, [PO 4 ] p does not consistently increase when the production rate of PTH or vitamin D 3 is decreased. Our results also suggest that, following a large PO 4 infusion, the rapidly exchangeable pool in bone acts as a fast, transient storage PO 4 compartment (on the order of minutes), whereas the intracellular pool is able to store greater amounts of PO 4 over several hours. Moreover, a large PO 4 infusion rapidly lowers [Ca 2+ ] p owing to the formation of CaPO 4 complexes. A large Ca infusion, however, has a small impact on [PO 4 ] p , since a significant fraction of Ca binds to albumin. This mathematical model is the first to include all major regulatory factors of Ca and PO 4 homeostasis. Copyright © 2017 the American Physiological Society.

  3. Influence of whole-body irradiation on calcium and phosphate homeostasis in the rat

    International Nuclear Information System (INIS)

    Pento, J.T.; Kenny, A.D.

    1975-01-01

    Previous irradiation studies have revealed marked alterations in calcium metabolism. Moreover, the maintenance of calcium homeostasis with parathyroid hormone or calcium salts has been reported to reduce radiation lethality. Therefore, the present study was designed to evaluate the influence of irradiation on calcium homeostasis in the rat. Nine hundred rad of whole-body irradiation produced a significant depression of both plasma calcium and phosphate at 4 days postirradiation. This effect of irradiation was observed to be dose-dependent over a range of 600 to 1200 rad, and possibly related to irradiation-induced anorexia. The physiological significance of these observations is discussed

  4. Preparation and bioactivity of micro-arc oxidized calcium phosphate coatings

    Energy Technology Data Exchange (ETDEWEB)

    Pan, Y.K. [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Ji' nan, Shandong 250061 (China); School of Materials Science and Engineering, Shandong University, Ji' nan, Shandong 250061 (China); Chen, C.Z., E-mail: czchen@sdu.edu.cn [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Ji' nan, Shandong 250061 (China); School of Materials Science and Engineering, Shandong University, Ji' nan, Shandong 250061 (China); Wang, D.G.; Lin, Z.Q. [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Ji' nan, Shandong 250061 (China); School of Materials Science and Engineering, Shandong University, Ji' nan, Shandong 250061 (China)

    2013-09-16

    Calcium phosphate (CaP) coatings were prepared on ZK60 magnesium alloy by micro-arc oxidation (MAO) in electrolyte containing calcium acetate monohydrate (CH{sub 3}COO){sub 2}Ca·H{sub 2}O) and disodium hydrogen phosphate dodecahydrate (Na{sub 2}HPO{sub 4}·12H{sub 2}O). Scanning electron microscope (SEM), energy-dispersive X-ray spectrometry (EDX) and X-ray diffractometer (XRD) were employed to characterize the microstructure, elemental distribution and phase composition of the CaP coatings respectively. Simulated body fluid (SBF) immersion test was used to evaluate the coating degradability and bioactivity. After 30 days of SBF immersion, the CaP coatings effectively reduce the degradation rate. The surfaces of CaP coatings are covered by a new layer formed of numerous needle-like, spherical and columned calcium phosphates. SEM, EDX and XRD results suggest that these calcium phosphates are bioactive calcium phosphate phases such as hydroxyapatite (Ca{sub 10}(PO{sub 4}){sub 6}(OH){sub 2}, HA) and calcium pyrophosphates (Ca{sub 2}P{sub 2}O{sub 7}, CPP). The formation of these calcium phosphates indicates that the CaP coatings have bioactivity. - Highlights: • Bioactive CaP coatings are successfully formed on ZK60 magnesium alloy. • CaP coatings consist of MgO, MgF{sub 2}, CaO, CaF{sub 2} and Ca{sub 3}(PO{sub 4}){sub 2}. • Needle-like, spherical and columned calcium phosphates formed in SBF. • CaP coatings exhibit bioactivity and low corrosion rate.

  5. Calcium Overload Accelerates Phosphate-Induced Vascular Calcification Via Pit-1, but not the Calcium-Sensing Receptor.

    Science.gov (United States)

    Masumoto, Asuka; Sonou, Tomohiro; Ohya, Masaki; Yashiro, Mitsuru; Nakashima, Yuri; Okuda, Kouji; Iwashita, Yuko; Mima, Toru; Negi, Shigeo; Shigematsu, Takashi

    2017-07-01

    Vascular calcification (VC) is a risk factor of cardiovascular and all-cause mortality in patients with chronic kidney disease (CKD). CKD-mineral and bone metabolism disorder is an important problem in patients with renal failure. Abnormal levels of serum phosphate and calcium affect CKD-mineral and bone metabolism disorder and contribute to bone disease, VC, and cardiovascular disease. Hypercalcemia is a contributing factor in progression of VC in patients with CKD. However, the mechanisms of how calcium promotes intracellular calcification are still unclear. This study aimed to examine the mechanisms underlying calcium-induced calcification in a rat aortic tissue culture model. Aortic segments from 7-week-old male Sprague-Dawley rats were cultured in serum-supplemented medium for 10 days. We added high calcium (HiCa; calcium 3.0 mM) to high phosphate (HPi; phosphate 3.8 mM) medium to accelerate phosphate and calcium-induced VC. We used phosphonoformic acid and the calcimimetic R-568 to determine whether the mechanism of calcification involves Pit-1 or the calcium-sensing receptor. Medial VC was significantly augmented by HPi+HiCa medium compared with HPi alone (300%, p<0.05), and was associated with upregulation of Pit-1 protein. Pit-1 protein concentrations in HPi+HiCa medium were greater than those in HPi medium. Phosphonoformic acid completely negated the augmentation of medial VC induced by HPi+HiCa. R-568 had no additive direct effect on medial VC. These results indicated that exposure to HPi+HiCa accelerates medial VC, and this is mediated through Pit-1, not the calcium-sensing receptor.

  6. Mucins and calcium phosphate precipitates additively stimulate cholesterol crystallization

    NARCIS (Netherlands)

    van den Berg, A. A.; van Buul, J. D.; Tytgat, G. N.; Groen, A. K.; Ostrow, J. D.

    1998-01-01

    Human biliary mucin and calcium binding protein (CBP) influence formation of both calcium salt precipitates and cholesterol crystals and colocalize in the center of cholesterol gallstones. We investigated how physiological concentrations of these proteins regulate cholesterol crystallization in

  7. Synthesis of calcium phosphate hydrogel from waste incineration fly ash and bone powder

    International Nuclear Information System (INIS)

    Fukui, Kunihiro; Arimitsu, Naoki; Kidoguchi, Satoshi; Yamamoto, Tetsuya; Yoshida, Hideto

    2009-01-01

    Waste incineration fly ash and bone powder could be successfully recycled into calcium phosphate hydrogel, a type of fast proton conductor. Various properties of the intermediate and calcium phosphate hydrogel from them were characterized and compared with that from calcium carbonate reagent. It was found that the intermediate from the incineration fly ash and calcium phosphate glass was more brittle than that from bone powder and calcium carbonate reagent. The electric conductivity of crystallized hydrogel obtained from all raw materials increases exponentially with temperature. However, the crystallized hydrogel from incineration fly ash has lower electric conductivity and lower crystallinity than that from bone powder and the reagent. Moreover, the difference in electric conductivity between these crystallized hydrogels decreases with temperature. Compared with using the reagent as a raw material, bone powder provides a 25% reduction in the usage of H 3 PO 4 to acquire the crystallized hydrogel which has the highest conductivity. These experimental results suggest that the incineration fly ash and bone powder are useful calcium sources for the synthesis of calcium phosphate hydrogel

  8. Controlled adsorption and release onto calcium phosphates materials and drug delivery applications

    Directory of Open Access Journals (Sweden)

    Barroug A.

    2013-11-01

    Full Text Available The adsorptive properties of synthetic calcium phosphates analogous to bone mineral were examined with respect to cisplatin and risedronate, two biological active drugs; the uptake and release experiments were carried out under various conditions in order to understand the basic mechanism of interaction. The effect of temperature and solution composition were highlighted and discussed. The adsorption results obtained for the therapeutic agents demonstrated that, depending on the conditions investigated (nature of the sorbent, concentration range, ionic composition, temperature…, the shape of the isotherms is of Freundlich or Langmuir type. The adsorption is described as an ion-exchange process in dilute solutions, while the interaction appears to be reactive for concentrated solutions (dissolution of mineral ions from the apatite substrate and formation of soluble calcium complex and/or precipitation of calcium salts involving sorbate molecules. The information gained on the surface reactivity of calcium phosphate were exploited to associate an antibiotic to calcium phosphate cements for drug delivery applications. The specimens were obtained by combination of calcium phosphate and calcium carbonate powders upon mixing with water. The physicochemical properties of the paste were altered by the drug loading method (in the liquid or solid phase. Thus, a dose-dependent effect was noticed for the paste setting time, hardening and the release process.

  9. The Effect of Moderate Dietary Protein and Phosphate Restriction on Calcium-Phosphate Homeostasis in Healthy Older Cats.

    Science.gov (United States)

    Geddes, R F; Biourge, V; Chang, Y; Syme, H M; Elliott, J

    2016-09-01

    Dietary phosphate and protein restriction decreases plasma PTH and FGF-23 concentrations and improves survival time in azotemic cats, but has not been examined in cats that are not azotemic. Feeding a moderately protein- and phosphate-restricted diet decreases PTH and FGF-23 in healthy older cats and thereby slows progression to azotemic CKD. A total of 54 healthy, client-owned cats (≥ 9 years). Prospective double-blinded randomized placebo-controlled trial. Cats were assigned to test diet (protein 76 g/Mcal and phosphate 1.6 g/Mcal) or control diet (protein 86 g/Mcal and phosphate 2.6 g/Mcal) and monitored for 18 months. Changes in variables over time and effect of diet were assessed by linear mixed models. A total of 26 cats ate test diet and 28 cats ate control diet. There was a significant effect of diet on urinary fractional excretion of phosphate (P = 0.045), plasma PTH (P = 0.005), and ionized calcium concentrations (P = 0.018), but not plasma phosphate, FGF-23, or creatinine concentrations. Plasma PTH concentrations did not significantly change in cats fed the test diet (P = 0.62) but increased over time in cats fed the control diet (P = 0.001). There was no significant treatment effect of the test diet on development of azotemic CKD (3 of 26 (12%) test versus 3 of 28 (11%) control, odds ratio 1.09 (95% CI 0.13-8.94), P = 0.92). Feeding a moderately protein- and phosphate-restricted diet has effects on calcium-phosphate homeostasis in healthy older cats and is well tolerated. This might have an impact on renal function and could be useful in early chronic kidney disease. Copyright © 2016 The Authors. Journal of Veterinary Internal Medicine published by Wiley Periodicals, Inc. on behalf of the American College of Veterinary Internal Medicine.

  10. Biocompatible and colloidally stabilized mPEG-PE/calcium phosphate hybrid nanoparticles loaded with siRNAs targeting tumors

    OpenAIRE

    Gao, Pei; Zhang, Xiangyu; Wang, Hongzhi; Zhang, Qinghong; Li, He; Li, Yaogang; Duan, Yourong

    2015-01-01

    Calcium phosphate nanoparticles are safe and effective delivery vehicles for small interfering RNA (siRNA), as a result of their excellent biocompatibility. In this work, mPEG-PE (polyethylene glycol-L-?-phosphatidylethanolamine) was synthesized and used to prepare nanoparticles composed of mPEG-PE and calcium phosphate for siRNA delivery. Calcium phosphate and mPEG-PE formed the stable hybrid nanoparticles through self-assembly resulting from electrostatic interaction in water. The average s...

  11. Interaction between calcium and phosphate adsorption on goethite

    NARCIS (Netherlands)

    Rietra, R.P.J.J.; Hiemstra, T.; Riemsdijk, van W.H.

    2001-01-01

    Quantitatively, little is known about the ion interaction processes that are responsible for the binding of phosphate in soil, water, and sediment, which determine the bioavailability and mobility of phosphate. Studies have shown that metal hydroxides are often responsible for the binding of PO4 in

  12. Surface physical chemistry properties in coated bacterial cellulose membranes with calcium phosphate.

    Science.gov (United States)

    de Olyveira, Gabriel Molina; Basmaji, Pierre; Costa, Ligia Maria Manzine; Dos Santos, Márcio Luiz; Dos Santos Riccardi, Carla; Guastaldi, Fernando Pozzi Semeghini; Scarel-Caminaga, Raquel Mantuaneli; de Oliveira Capote, Ticiana Sidorenko; Pizoni, Elisabeth; Guastaldi, Antônio Carlos

    2017-06-01

    Bacterial cellulose has become established as a new biomaterial, and it can be used for medical applications. In addition, it has called attention due to the increasing interest in tissue engineering materials for wound care. In this work, the bacterial cellulose fermentation process was modified by the addition of chondroitin sulfate to the culture medium before the inoculation of the bacteria. The biomimetic process with heterogeneous calcium phosphate precipitation of biological interest was studied for the guided regeneration purposes on bacterial cellulose. FTIR results showed the incorporation of the chondroitin sulfate in the bacterial cellulose, SEM images confirmed the deposition of the calcium phosphate on the bacterial cellulose surface, XPS analysis showed a selective chemical group influences which change calcium phosphate deposition, besides, the calcium phosphate phase with different Ca/P ratios on bacterial cellulose surface influences wettability. XTT results concluded that these materials did not affect significantly in the cell viability, being non-cytotoxic. Thus, it was produced one biomaterial with the surface charge changes for calcium phosphate deposition, besides different wettability which builds new membranes for Guided Tissue Regeneration. Copyright © 2017 Elsevier B.V. All rights reserved.

  13. Sorption behavior of Zn(II) ions on synthetic apatitic calcium phosphates

    Science.gov (United States)

    Sebei, Haroun; Pham Minh, Doan; Nzihou, Ange; Sharrock, Patrick

    2015-12-01

    The synthesis, characterization and the reactivity of apatitic calcium phosphates (Ca-HA, chemical formula Ca10(PO4)6(OH)2) is reported. Calcium carbonate (CaCO3) and potassium dihydrogen orthophosphate (KH2PO4) were selected as economical starting materials for the synthesis of Ca-HA under atmospheric conditions. Monocalcium phosphate monohydrate (MCPM), dicalcium phosphate dihydrate (DCPD), and octacalcium phosphate pentahydrate (OCP) were identified as the main intermediates of the synthesis reaction. The product obtained after 48 h of reaction contains mainly low-crystalline Ca-HA and small amounts of other calcium phosphates such as octacalcium phosphate (OCP), B-type carbonate apatite (CAP), as well as unreacted calcium carbonate. This Ca-HA was found to be active for the removal of Zn2+ from an aqueous solution. Its sorption capacity reached up to 120 mg of Zn2+ per g of Ca-HA powder after 24 h of reaction. The monitoring of soluble Zn, Ca and P during the sorption experiment allowed characterizing the mechanism of Zn uptake. Dissolution-precipitation, ionic exchange and surface complexation are the three main mechanisms involved in the sorption processes. The contribution of these mechanisms is discussed in detail.

  14. Molecular mechanism of crystallization impacting calcium phosphate cements

    Energy Technology Data Exchange (ETDEWEB)

    Giocondi, J L; El-Dasher, B S; Nancollas, G H; Orme, C A

    2009-05-31

    theoretical modeling. The question changes from 'What types of molecules will inhibit brushite growth' to 'What type of molecule will interact with the [10-1]{sub Cc} step?' Similarly, to increase resorption rate, it would be most efficacious to target the slow moving [-100] step, perhaps by targeting the hydroxyl group which seem to stabilize this step compared to its otherwise similar mirror, [100]. In short, there are a number of opportunities where molecular scale imaging can provide new information that has the prospect to aid in optimizing calcium phosphate cements.

  15. Immobilization of calcium and phosphate ions improves the osteoconductivity of titanium implants

    International Nuclear Information System (INIS)

    Sunarso; Toita, Riki; Tsuru, Kanji; Ishikawa, Kunio

    2016-01-01

    In this work, to elevate weak osteoconductivity of titanium (Ti) implant, we prepared a Ti implant having both calcium and phosphate ions on its surface. To modify calcium and phosphate ions onto Ti, phosphate ions were first immobilized by treating the Ti with a NaH 2 PO 4 solution, followed by CaCl 2 treatment to immobilize calcium ions, which created the calcium and phosphate ions-modified Ti (Ca-P-Ti). X-ray photoelectron spectroscopy and thin-layer X-ray diffraction measurement confirmed that both phosphate and calcium ions were co-immobilized onto the Ti surface on the molecular level. Three-hour after seeding MC3T3-E1 murine pre-osteoblast cells on substrates, cell number on Ca-P-Ti was much larger than that of Ti and phosphate-modified Ti (P-Ti), but was similar to that of calcium-modified Ti (Ca-Ti). Also, MC3T3-E1 cells on Ca-P-Ti expressed larger amount of vinculin, a focal adhesion protein, than those on other substrates, probably resulting in larger cell size as well as greater cell proliferation on Ca-P-Ti than those on other substrates. Alkaline phosphatase activity of cells on Ca-P-Ti was greater than those on Ti and P-Ti, but was almost comparable to that of Ca-Ti. Moreover, the largest amount of bone-like nodule formation was observed on Ca-P-Ti. These results provide evidence that calcium and phosphate ions-co-immobilization onto Ti increased the osteoconductivity of Ti by stimulating the responses of pre-osteoblast cells. This simple modification would be promising technique for bone tissue implant including dental and orthopedic implants. - Highlights: • Phosphate and calcium ions have been successfully co-immobilize on Ti surface. • Co-immobilization of Ca and phosphate ions (Ca-P-Ti) did not alter the original surface morphology. • Ca-P-Ti significantly improved initial MC3T3-E1 cell adhesion. • Ca-P-Ti demonstrated remarkable cell proliferation, differentiation and mineralization. • Overall, Ca-P-Ti would be a promising bone

  16. Synthesis and characterization of nanostructured powders of hydroxyapatite and β-calcium phosphate

    Energy Technology Data Exchange (ETDEWEB)

    Prants, W.T.; Muller, D.T.; Orzechowski, L.G.; Feit, G.; Delima, S.A.; Camargo, N.H.A.; Gemelli, E., E-mail: w_prants@hotmail.com, E-mail: danielt_muller@yahoo.com.br, E-mail: sarahamindelima@hotmail.com, E-mail: dem2nhac@joinville.udesc.br, E-mail: gemelli@joinville.udesc.br [Universidade do Estado de Santa Catarina (UDESC), Joinville, SC (Brazil). Campus Universitario Prof. Avelino Marcante

    2009-07-01

    Biphasic calcium phosphate (BCP) bioceramics are composed in a general manner from a mixture between hydroxyapatite (HA), and β-calcium phosphate. In the recent years, the BCP bioceramics are pointed out in researches from regeneration and reconstitution in osseous tissue, in reason of their similar mineralogical characteristics of the human bone structure, as great biodegradation, absorption and formation of precocious osseous tissue. The biphasic materials (BCP) are detached for use in medical and dental application, as filling bone cavities, maxillofacial treatment, medicaments discharge for treatment cancerous osteomyelitis and antibiotics discharge related with orthopedic injuries reparation. The aim of this work focused in synthesis and characterization of hydroxyapatite and β-calcium phosphate. The presented results are related with the mineralogical characterization with X-ray diffraction, thermal behavior with Differential Scanning Calorimetry and Dilatometer. The Scanning Electronic Microscopy (SEM) was used to help in the morphological characterization of the nanostructured powders. (author)

  17. Synthesis and characterization of nanocomposite powders of calcium phosphate/titanium oxide for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    Delima, S.A.; Camargo, N.H.A.; Souza, J.C.P.; Gemelli, E., E-mail: sarahamindelima@hotmail.com, E-mail: dem2nhac@joinville.udesc.br, E-mail: souzajulio@joinville.udesc.br, E-mail: gemelli@joinville.udesc.br [Universidade do Estado de Santa Catarina (UDESC), Joinville, SC (Brazil). Centro de Ciencias Tecnologicas

    2009-07-01

    The nanostructured bioceramics of calcium phosphate are current themes of research and they are becoming important as bone matrix in regeneration of tissues in orthopedic and dental applications. Nanocomposite powders of calcium phosphate, reinforced with nanometric particles of titanium oxide, silica oxide and alumina oxid ealpha, are being widely studied because they offer new microstructures, nanostructures and interconnected microporosity with high superficial area of micropores that contribute to osteointegration and osteoinduction processes. This study is about the synthesis of nanocomposites powders of calcium phosphate reinforced with 1%, 2%, 3% and 5% in volume of titanium oxide and its characterization through the techniques of X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Differential Thermal Analysis (DTA), Thermogravimetry (TG) and Dilatometry. (author)

  18. Evaluation of growth of calcium phosphate ceramics on sintered Ti-Ca-P composites

    Energy Technology Data Exchange (ETDEWEB)

    Karanjai, Malobika [Centre for Nano Materials, International Advanced Research Centre for Powder Metallurgy and New Materials, Balapur P.O, Hyderabad - 500 005, Andhra Pradesh (India)], E-mail: malobika_k@rediffmail.com; Sundaresan, Ranganathan [Centre for Nano Materials, International Advanced Research Centre for Powder Metallurgy and New Materials, Balapur P.O, Hyderabad - 500 005, Andhra Pradesh (India); Mohan, Tallapragada Raja Rama; Kashyap, Bhagwati Prasad [Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Mumbai - 400 076, Maharashtra (India)

    2008-12-01

    Sintered Ti-Ca-P composites having in situ formed calcium phosphate phases developed by powder metallurgy processing were soaked for 28 days in simulated body fluid (SBF) with a pH of 7.4 at 37 deg. C and evaluated for the growth of calcium phosphate ceramics onto its surface. The composites were taken out once every 7 days and characterised using X-ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR) for evaluating the Ca-P growth. Based on the change in chemistry of the SBF and phase contents, a model has been proposed for mechanism of growth of calcium phosphate compounds on sintered Ti-Ca-P composites immersed in SBF.

  19. Synthesis and characterization of nanostructured powders of hydroxyapatite and β-calcium phosphate

    International Nuclear Information System (INIS)

    Prants, W.T.; Muller, D.T.; Orzechowski, L.G.; Feit, G.; Delima, S.A.; Camargo, N.H.A.; Gemelli, E.

    2009-01-01

    Biphasic calcium phosphate (BCP) bioceramics are composed in a general manner from a mixture between hydroxyapatite (HA), and β-calcium phosphate. In the recent years, the BCP bioceramics are pointed out in researches from regeneration and reconstitution in osseous tissue, in reason of their similar mineralogical characteristics of the human bone structure, as great biodegradation, absorption and formation of precocious osseous tissue. The biphasic materials (BCP) are detached for use in medical and dental application, as filling bone cavities, maxillofacial treatment, medicaments discharge for treatment cancerous osteomyelitis and antibiotics discharge related with orthopedic injuries reparation. The aim of this work focused in synthesis and characterization of hydroxyapatite and β-calcium phosphate. The presented results are related with the mineralogical characterization with X-ray diffraction, thermal behavior with Differential Scanning Calorimetry and Dilatometer. The Scanning Electronic Microscopy (SEM) was used to help in the morphological characterization of the nanostructured powders. (author)

  20. Calcium phosphate formation from sea urchin - (brissus latecarinatus via modified mechano-chemical (ultrasonic conversion method

    Directory of Open Access Journals (Sweden)

    R. Samur

    2013-07-01

    Full Text Available This study aims to produce apatite structures, such as hydroxyapatite (HA and fluorapatite (FA, from precursor calcium phosphates of biological origin, namely from sea urchin, with mechano-chemical stirring and hot-plating conversion method. The produced materials were heat treated at 800 °C for 4 hours. X-ray diffraction and scanning electron microscopy (SEM studies were conducted. Calcium phosphate phases were developed. The SEM images showed the formation of micro to nano-powders. The experimental results suggest that sea urchin, Brissus latecarinatus skeleton could be an alternative source for the production of various mono or biphasic calcium phosphates with simple and economic mechano-chemical (ultrasonic conversion method.

  1. Synthesis and characterization of nanocomposite powders of calcium phosphate/titanium oxide for biomedical applications

    International Nuclear Information System (INIS)

    Delima, S.A.; Camargo, N.H.A.; Souza, J.C.P.; Gemelli, E.

    2009-01-01

    The nanostructured bioceramics of calcium phosphate are current themes of research and they are becoming important as bone matrix in regeneration of tissues in orthopedic and dental applications. Nanocomposite powders of calcium phosphate, reinforced with nanometric particles of titanium oxide, silica oxide and alumina oxid ealpha, are being widely studied because they offer new microstructures, nanostructures and interconnected microporosity with high superficial area of micropores that contribute to osteointegration and osteoinduction processes. This study is about the synthesis of nanocomposites powders of calcium phosphate reinforced with 1%, 2%, 3% and 5% in volume of titanium oxide and its characterization through the techniques of X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Differential Thermal Analysis (DTA), Thermogravimetry (TG) and Dilatometry. (author)

  2. Uptake of CrO42- ions by Fe-treated tri-calcium phosphate

    International Nuclear Information System (INIS)

    Serrano G, J.; Ramirez S, J. L.; Bonifacio M, J.; Granados C, F.; Badillo A, V. E.

    2010-01-01

    CrO 4 2- ion adsorption of Fe-treated tri-calcium phosphate was studied by batch experiments as a function of contact time, initial concentration of metal ion and temperature. Adsorption results showed that at ph 5.5 and 1.0 x 10 -4 M chromium concentration the adsorption capacity of Fe-treated tri-calcium phosphate for CrO 4 2- ions was 7.10 x 10 -3 mmol/g. Chromium adsorption data on Fe-treated tri-calcium phosphate at various initial concentration fitted the Freundlich isotherm. By temperature studies the thermodynamic parameters ΔH 0 , ΔG 0 and ΔS 0 were estimated and the obtained results showed that the adsorption reaction was endothermic and spontaneous. (Author)

  3. Dental Composites with Calcium / Strontium Phosphates and Polylysine.

    Directory of Open Access Journals (Sweden)

    Piyaphong Panpisut

    Full Text Available This study developed light cured dental composites with added monocalcium phosphate monohydrate (MCPM, tristrontium phosphate (TSrP and antimicrobial polylysine (PLS. The aim was to produce composites that have enhanced water sorption induced expansion, can promote apatite precipitation and release polylysine.Experimental composite formulations consisted of light activated dimethacrylate monomers combined with 80 wt% powder. The powder phase contained a dental glass with and without PLS (2.5 wt% and/or reactive phosphate fillers (15 wt% TSrP and 10 wt% MCPM. The commercial composite, Z250, was used as a control. Monomer conversion and calculated polymerization shrinkage were assessed using FTIR. Subsequent mass or volume changes in water versus simulated body fluid (SBF were quantified using gravimetric studies. These were used, along with Raman and SEM, to assess apatite precipitation on the composite surface. PLS release was determined using UV spectroscopy. Furthermore, biaxial flexural strengths after 24 hours of SBF immersion were obtained.Monomer conversion of the composites decreased upon the addition of phosphate fillers (from 76 to 64% but was always higher than that of Z250 (54%. Phosphate addition increased water sorption induced expansion from 2 to 4% helping to balance the calculated polymerization shrinkage of ~ 3.4%. Phosphate addition promoted apatite precipitation from SBF. Polylysine increased the apatite layer thickness from ~ 10 to 20 μm after 4 weeks. The novel composites showed a burst release of PLS (3.7% followed by diffusion-controlled release irrespective of phosphate addition. PLS and phosphates decreased strength from 154 MPa on average by 17% and 18%, respectively. All formulations, however, had greater strength than the ISO 4049 requirement of > 80 MPa.The addition of MCPM with TSrP promoted hygroscopic expansion, and apatite formation. These properties are expected to help compensate polymerization shrinkage and

  4. Mechanical properties of calcium phosphate cements obtained by solution combustion synthesis

    Energy Technology Data Exchange (ETDEWEB)

    Volkmer, Tiago M.; Barreiro, Oscar; Souza, Vania Caldas; Santos, Luis Alberto dos, E-mail: tiagovolkmer@gmail.com, E-mail: oscarbafer@hotmail.com, E-mail: vania.souza@ufrgs.br, E-mail: luis.santos@ufrgs.br [Universidade Federal do Rio Grande do Sul (UFRS), Porto Alegre, RS (Brazil). Laboratorio de Biomateriais

    2009-07-01

    Bioceramics based on calcium phosphates, especially hydroxyapatite and tricalcium phosphates (TCP) are the most used biomaterials as bone substitutes. The objective of this work is to evaluate the mechanical properties of α-tricalcium phosphate (α-TCP) synthesized by the solution combustion method. The solution combustion synthesis (SCS) can be considered as faster and simpler as other methods, furthermore it allows the obtainment of high purity α-TCP. In the calcium phosphates (CPC), α-TCP reacts with water forming needle like HA, which restrain the movement of grains, increasing mechanical resistance. In the present paper the influence of particle size on mechanical properties of α-TCP cements were evaluated. The α-TCP powder were characterized by XRD, TEM, BET and laser diffraction to asses particle size while the CPC bodies by SEM, Arquimedes method and compression tests. Increasing the milling time, the particle size decreases, resulting in samples with less porosity and consequently with higher compression resistance. (author)

  5. Adsorption and release of amino acids mixture onto apatitic calcium phosphates analogous to bone mineral

    Science.gov (United States)

    El Rhilassi, A.; Mourabet, M.; El Boujaady, H.; Bennani-Ziatni, M.; Hamri, R. El; Taitai, A.

    2012-10-01

    Study focused on the interaction of adsorbate with poorly crystalline apatitic calcium phosphates analogous to bone mineral. Calcium phosphates prepared in water-ethanol medium at physiological temperature (37 °C) and neutral pH, their Ca/P ratio was between 1.33 and 1.67. Adsorbate used in this paper takes the mixture form of two essential amino acids L-lysine and DL-leucine which have respectively a character hydrophilic and hydrophobic. Adsorption and release are investigated experimentally; they are dependent on the phosphate type and on the nature of adsorbate L-lysine, DL-leucine and their mixture. Adsorption of mixture of amino acids on the apatitic calcium phosphates is influenced by the competition between the two amino acids: L-lysine and DL-leucine which exist in the medium reaction. The adsorption kinetics is very fast while the release kinetics is slow. The chemical composition of apatite has an influence on both adsorption and release. The interactions adsorbate-adsorbent are electrostatic type. Adsorption and release reactions of the amino acid mixture are explained by the existence of the hydrated surface layer of calcium phosphate apatite. The charged sbnd COOsbnd and sbnd NH3+ of adsorbates are the strongest groups that interact with the surface of apatites, the adsorption is mainly due to the electrostatic interaction between the groups sbnd COOsbnd of amino acids and calcium Ca2+ ions of the apatite. Comparative study of interactions between adsorbates (L-lysine, DL-leucine and their mixture) and apatitic calcium phosphates is carried out in vitro by using UV-vis and infrared spectroscopy IR techniques.

  6. Ossification Vesicles with Calcium Phosphate in the Eyes of the Insect Copium teucrii (Hemiptera: Tingidae

    Directory of Open Access Journals (Sweden)

    Javier Garcia-Guinea

    2011-01-01

    Full Text Available Arthropod eyes are built of repeating units named ommatidia. Each single ommatidium unit contains a cluster of photoreceptor cells surrounded by support cells and pigment cells. The insect Copium eye ommatidia include additional calcium-phosphate deposits, not described in insects to date, which can be examined today using a combined set of modern microscopy and spectroscopy techniques. Teucrium gnaphalodes L'Her plants, growing in central Spain, develop galls induced by Copium insects. A survey of C. teucrii adult specimens resulted in surprising environmental scanning electron microscopy (ESEM images, showing that their bright red eyes contain a calcium-phosphate mineralization. A complete survey of Copium eye specimens was performed by ESEM using energy-dispersive spectroscopy, backscattered electron detector and cathodoluminescence (CL probes, field emission scanning electron microscopy, micro-Raman spectroscopy, and confocal laser scanning microscopy in order to learn ommatidia features, such as chemical composition, molecular structure, cell membrane, and internal ommatidium eye fluids and calcium-phosphate distribution deposits. The CL panchromatic images distinguish between the calcium-phosphate ommatidium and calcium-phosphate setae, which are more apatite rich. They show Raman bands attributable to bone tissue apatite biomaterials, such as bone, collagen, lipids, and blood, i.e., peptides, amide-S, amide-II, amide-III, and cytochrome P-450scc. The chemical composition of both galls and leaves of T. gnaphalodes was determined by gas chromatography – mass spectrometry (GC-MS of their extracts. The spectrometric and microscopic images reveal that the calcium-phosphate mineralization is formed and constrained to Copium ommatidia, which are both matrix vesicles generating mixtures of apatite collagen and operational compound eyes of the insect.

  7. Reduced CSF leak in complete calvarial reconstructions of microvascular decompression craniectomies using calcium phosphate cement.

    Science.gov (United States)

    Eseonu, Chikezie I; Goodwin, C Rory; Zhou, Xin; Theodros, Debebe; Bender, Matthew T; Mathios, Dimitrios; Bettegowda, Chetan; Lim, Michael

    2015-12-01

    Calcium phosphate cement provides a biomaterial that can be used for calvarial reconstruction in a retrosigmoid craniectomy for microvascular decompression (MVD). This study evaluates the outcomes of postoperative CSF leak and wound infection for patients undergoing a complete cranioplasty using calcium phosphate cement versus incomplete cranioplasty using polyethylene titanium mesh following a retrosigmoid craniectomy for MVD. The authors evaluated 211 cases involving patients who underwent first-time retrosigmoid craniectomies performed by a single attending surgeon fortrigeminal neuralgia from October 2008 to June 2014. From this patient population, 111 patients underwent calvarial reconstruction after retrosigmoid craniectomy using polyethylene titanium mesh, and 100 patients had reconstructions using calcium phosphate cement. A Pearson's chi-square test was used to compare postoperative complications of CSF leak and wound infection in these 2 types of cranioplasties. The polyethylene titanium mesh group included 5 patients (4.5%) with postoperative CSF leak or pseudomeningocele and 3 patients (2.7%) with wound infections. In the calcium phosphate cement group, no patients had a CSF leak, and 2 patients (2%) had wound infections. This represented a statistically significant reduction of postoperative CSF leak in patients who underwent calcium phosphate reconstructions of their calvarial defect compared with those who underwent polyethylene titanium mesh reconstructions (p = 0.03). No significant difference was seen between the 2 groups in the number of patients with postoperative wound infections. Calcium phosphate cement provides a viable alternative biomaterial for calvarial reconstruction of retrosigmoid craniectomy defects in patients who have an MVD. The application of this material provides a biocompatible barrier that reduces the incidence of postoperative CSF leaks.

  8. Adsorption studies of phosphate ions on alginate- calcium ...

    African Journals Online (AJOL)

    user

    osmosis, electro dialysis, phytoremediation and phyto- extraction, ion-exchange .... occurred between functional groups of alginate and host material, that is, calcium .... metal ions using wheat based biosorbent; a review of the recent literature.

  9. Brittle and ductile adjustable cement derived from calcium phosphate cement/polyacrylic acid composites.

    Science.gov (United States)

    Chen, Wen-Cheng; Ju, Chien-Ping; Wang, Jen-Chyan; Hung, Chun-Cheng; Chern Lin, Jiin-Huey

    2008-12-01

    Bone filler has been used over the years in dental and biomedical applications. The present work is to characterize a non-dispersive, fast setting, modulus adjustable, high bioresorbable composite bone cement derived from calcium phosphate-based cement combined with polymer and binding agents. This cement, we hope, will not swell in simulated body fluid and keep the osteogenetic properties of the dry bone and avoid its disadvantages of being brittle. We developed a calcium phosphate cement (CPC) of tetracalcium phosphate/dicalcium phosphate anhydrous (TTCP/DCPA)-polyacrylic acid with tartaric acid, calcium fluoride additives and phosphate hardening solution. The results show that while composite, the hard-brittle properties of 25wt% polyacrylic acid are proportional to CPC and mixing with additives is the same as those of the CPC without polyacrylic acid added. With an increase of polyacrylic acid/CPC ratio, the 67wt% samples revealed ductile-tough properties and 100wt% samples kept ductile or elastic properties after 24h of immersion. The modulus range of this development was from 200 to 2600MPa after getting immersed in simulated body fluid for 24h. The TTCP/DCPA-polyacrylic acid based CPC demonstrates adjustable brittle/ductile strength during setting and after immersion, and the final reaction products consist of high bioresorbable monetite/brushite/calcium fluoride composite with polyacrylic acid.

  10. Biomimetic fabrication of calcium phosphate/chitosan nanohybrid composite in modified simulated body fluids

    Directory of Open Access Journals (Sweden)

    K. H. Park

    2017-01-01

    Full Text Available In this study, nucleation and growth of bone-like hydroxyapatite (HAp mineral in modified simulated body fluids (m-SBF were induced on chitosan (CS substrates, which were prepared by spin coating of chitosan on Ti substrate. The m-SBF showed a two fold increase in the concentrations of calcium and phosphate ions compared to SBF, and the post-NaOH treatment provided stabilization of the coatings. The calcium phosphate/chitosan composite prepared in m-SBF showed homogeneous distribution of approximately 350 nm-sized spherical clusters composed of octacalcium phosphate (OCP; Ca8H2(PO46·5H2O crystalline structure. Chitosan provided a control over the size of calcium phosphate prepared by immersion in m-SBF, and post-NaOH treatment supported the binding of calcium phosphate compound on the Ti surface. Post-NaOH treatment increased hydrophilicity and crystallinity of carbonate apatite, which increased its potential for biomedical application.

  11. Synthesis and characterization of porous calcium phosphate; Sintesis y caracterizacion del fosfato de calcio poroso

    Energy Technology Data Exchange (ETDEWEB)

    Granados C, F.; Serrano G, J.; Bonifacio M, J. [ININ, 52750 La Marquesa, Estado de Mexico (Mexico)]. e-mail: fgc@nuclear.inin.mx

    2007-07-01

    The porous calcium phosphate was prepared by the continuous precipitation method using Ca(NO{sub 3}){sub 2}.4H{sub 2}O and NH{sub 4}H{sub 2}PO{sub 4} salts. The synthesized material was structurally and superficially characterized using the XRD, BET, IR TGA and SEM techniques. The obtained inorganic material was identified as calcium phosphate that presents a great specific area for what can be efficiently used as adsorbent material for adsorption studies in the radioactive wastes treatment present in aqueous solution. (Author)

  12. Treatment of post-orthodontic white spot lesions with casein phosphopeptide-stabilised amorphous calcium phosphate

    DEFF Research Database (Denmark)

    Bröchner, Ann; Christensen, Carsten; Kristensen, Bjarne

    2010-01-01

    This study aims to investigate the effect of topical applications of 10% casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) on white spot lesions (WSL) detected after treatment with fixed orthodontic appliances. Sixty healthy adolescents with >/=1 clinically visible WSL at debonding were...... findings were largely reflected by the clinical scores. No side effects were reported. Topical treatment of white spot lesions after debonding of orthodontic appliances with a casein phosphopeptide-stabilised amorphous calcium phosphate agent resulted in significantly reduced fluorescence and a reduced...

  13. Bioactivity evaluation of commercial calcium phosphate-based bioceramics for bone regeneration

    Energy Technology Data Exchange (ETDEWEB)

    Borrós, S.; Mas, A.

    2016-11-01

    Calcium phosphate-based bioceramics constitute a great promise for bone tissue engineering as they chemically resemble to mammalian bone and teeth. Their use is a viable alternative for bone regeneration as it avoids the use of autografts and allografts, which usually involves immunogenic reactions and patient’s discomfort. This work evolves around the study of the bioactivity potential of different commercially available bone substitutes based in calcium phosphate through the characterization of their ionic exchangeability when immersed in simulated body fluid (SBF). (Author)

  14. Inhibition of calcium phosphate precipitation under environmentally-relevant conditions

    International Nuclear Information System (INIS)

    Cao Xinde; Harris, Willie G.; Josan, Manohardeep S.; Nair, Vimala D.

    2007-01-01

    Precipitation of Ca phosphates plays an important role in controlling P activity and availability in environmental systems. The purpose of this study was to determine inhibitory effects on Ca phosphate precipitation by Mg 2+ , SO 4 2- , CO 3 2- , humic acid, oxalic acid, biogenic Si, and Si-rich soil clay commonly found in soils, sediments, and waste streams. Precipitation rates were determined by measuring decrease of P concentration in solutions during the first 60 min; and precipitated solid phases identified using X-ray diffraction and electron microscopy. Poorly-crystalline hydroxyapatite (HAP: Ca 5 (PO 4 ) 3 OH) formed in control solutions over the experiment period of 24 h, following a second-order dependence on P concentration. Humic acid and Mg 2+ significantly inhibited formation of HAP, allowing formation of a more soluble amorphous Ca phosphate phase (ACP), and thus reducing the precipitation rate constants by 94-96%. Inhibition caused by Mg 2+ results from its incorporation into Ca phosphate precipitates, preventing formation of a well-crystalline phase. Humic acid likely suppressed Ca phosphate precipitation by adsorbing onto the newly-formed nuclei. Presence of oxalic acid resulted in almost complete inhibition of HAP precipitation due to preemptive Ca-oxalate formation. Carbonate substituted for phosphate, decreasing the crystallinity of HAP and thus reducing precipitation rate constant by 44%. Sulfate and Si-rich solids had less impact on formation of HAP; while they reduced precipitation in the early stage, they did not differ from the control after 24 h. Results indicate that components (e.g., Mg 2+ , humic acid) producing relatively soluble ACP are more likely to reduce P stability and precipitation rate of Ca phosphate in soils and sediments than are components (e.g., SO 4 2- , Si) that have less effect on the crystallinity

  15. Simultaneous in vivo determination of calcium and phosphate effective intestinal absorption in the rat

    International Nuclear Information System (INIS)

    Ladizesky, M.; Mautalen, C.A.; Cabrejas, M.; Degrossi, O.J.

    1978-01-01

    A description is given of a technique which allows a more precise assessment of the interrelation between calcium and phosphate transport systems. Rats were given an i.p. or oral dose of 47 Ca with 40 Ca as carrier and/or 32 P with 31 P as carrier. The animals were sacrificed and activities in body and excised gastrointestinal tract determined. The 1.28 MeV photopeak activity was measured for calcium 47, and phosphorus 32 activity was determined by measuring the Bremsstrahlung produced by this isotope in the rat's body in the 80 to 200 keV range. The rates of intestinal absorption of calcium and phosphate differed; there seemed to be no urinary excretion of the radioisotopes within 3 hours. The reciprocal influence of calcium and phosphate on the intestinal absorption was also studied. The technique is simple and allows the simultaneous in vivo measurement of the effective intestinal absorption of calcium and phosphate. (U.K.)

  16. The effect of organic ligands on the crystallinity of calcium phosphate

    Science.gov (United States)

    van der Houwen, Jacqueline A. M.; Cressey, Gordon; Cressey, Barbara A.; Valsami-Jones, Eugenia

    2003-03-01

    Calcium phosphate phases precipitated under critical supersaturation were identified and studied in detail using X-ray powder diffraction, electron probe microanalysis, infrared spectroscopy (IR) and transmission electron microscopy. These synthetic calcium phosphates formed by spontaneous precipitation at pH 7, 25°C and 0.1 M ionic strength (NaCl as the background electrolyte). The combination of several methods allowed detailed characterisation of the calcium phosphates. The purpose of the work was to assess the influence of carboxylate ligands, specifically acetate and citrate, on the quality of the calcium phosphate precipitate. All precipitates were identified as non-stoichiometric, calcium-deficient hydroxylapatites (HAPs), containing carbonate, HPO 42-, sodium and chloride impurities. No other phases were found to be present in any of the precipitates. The presence of citrate resulted in a decrease in crystal size and a higher degree of apatite lattice imperfection in the precipitated HAP. Furthermore, IR spectroscopy showed a higher amount of carbonate present in that HAP, compared with the ones formed in the control and acetate experiments. An additional absorption band, in the infrared spectrum of the HAP formed in the presence of citrate, was observed at 1570 cm -1; this is interpreted as carboxyl groups bound to HAP.

  17. Correlation between calcium and phosphate levels to calculus accumulation on coronary heart disease patients

    Science.gov (United States)

    Cahaya, Cindy; Masulili, Sri Lelyati C.; Lessang, Robert; Radi, Basuni

    2017-02-01

    Coronary Artery Disease (CAD) or Coronary Heart Disease (CHD) is a disease that happened because of blood flow being blocked by atherosclerosis. Atherosclerosis is a process of hardening of the arteries which characterized by thickening and loss of elasticity of the intimal layer of vascular wall, by lipid deposit. Periodontitis is a chronic multifactorial inflammatory disease caused by microorganism and characterized by progressive destruction of the tooth supporting apparatus leading to tooth loss. Many studies use saliva as a valuable source for clinically information, as an asset for early diagnosis, prognostic and reviewer for pascatherapy status. Dental calculus had happened as a consequence of saliva supersaturation by calcium and phosphate. Salivary flow rate and its composition influence the formation of calculus. Increasing salivary calcium levels is characteristic of periodontitis patients. An important hipotesis in Cardiology is chronic infections contribute in atherosclerosis. Objective: To analyse the correlation between calcium and phosphate levels in saliva to calculus accumulation on CHD patients. Result: Correlation analysis between salivary calcium levels with calculus accumulation in patients with CHD and non-CHD showed no significant p value, p=0.59 and p=0.518. Correlation analysis between salivary phosphate levels and calculus accumulation showed no significant p value, p=0.836 for CHD patients and p=0.484 for non-CHD patients. Conclusion: There are no correlation between calcium levels and phosphate levels with calculus accumulation in CHD patients. Further research need to be done.

  18. Magnesium substitution in the structure of orthopedic nanoparticles: A comparison between amorphous magnesium phosphates, calcium magnesium phosphates, and hydroxyapatites

    International Nuclear Information System (INIS)

    Nabiyouni, Maryam; Ren, Yufu; Bhaduri, Sarit B.

    2015-01-01

    As biocompatible materials, magnesium phosphates have received a lot of attention for orthopedic applications. During the last decade multiple studies have shown advantages for magnesium phosphate such as lack of cytotoxicity, biocompatibility, strong mechanical properties, and high biodegradability. The present study investigates the role of Mg +2 and Ca +2 ions in the structure of magnesium phosphate and calcium phosphate nanoparticles. To directly compare the effect of Mg +2 and Ca +2 ions on structure of nanoparticles and their biological behavior, three groups of nanoparticles including amorphous magnesium phosphates (AMPs) which release Mg +2 , calcium magnesium phosphates (CMPs) which release Mg +2 and Ca +2 , and hydroxyapatites (HAs) which release Ca +2 were studied. SEM, TEM, XRD, and FTIR were used to evaluate the morphology, crystallinity, and chemical properties of the particles. AMP particles were homogeneous nanospheres, whereas CMPs were combinations of heterogeneous nanorods and nanospheres, and HAs which contained heterogeneous nanosphere particles. Cell compatibility was monitored in all groups to determine the cytotoxicity effect of particles on studied MC3T3-E1 preosteoblasts. AMPs showed significantly higher attachment rate than the HAs after 1 day and both AMPs and CMPs showed significantly higher proliferation rate when compared to HAs after 7 days. Gene expression level of osteoblastic markers ALP, COL I, OCN, OPN, RUNX2 were monitored and they were normalized to GAPDH housekeeping gene. Beta actin expression level was monitored as the second housekeeping gene to confirm the accuracy of results. In general, AMPs and CMPs showed higher expression level of osteoblastic genes after 7 days which can further confirm the stimulating role of Mg + 2 and Ca +2 ions in increasing the proliferation rate, differentiation, and mineralization of MC3T3-E1 preosteoblasts. - Highlights: • Role of Mg 2+ and Ca 2+ ions in proliferation, and differentiation

  19. Preliminary characterization of calcium chemical environment in apatitic and non-apatitic calcium phosphates of biological interest by X-ray absorption spectroscopy

    International Nuclear Information System (INIS)

    Eichert, D.; Salome, M.; Banu, M.; Susini, J.; Rey, C.

    2005-01-01

    Several reports have mentioned the existence of non-apatitic environments of phosphate and carbonate ions in synthetic and biological poorly crystalline apatites. However there were no direct spectroscopic evidences for the existence of non-apatitic environment of calcium ions. X-ray Absorption Spectroscopy, at the K-edge of calcium, allows the discrimination between different calcium phosphates of biological interest despite great spectral similarities. A primary analysis of the spectra reveals the existence, in synthetic poorly crystalline apatites, of variable features related to the maturation stage of the sample and corresponding to the existence of non-apatitic environments of calcium ions. Although these features can also be found in several other calcium phosphate salts, and do not allow a clear identification of the ionic environments of calcium ions, they give a possibility to directly determine the maturity of poorly crystalline apatite from calcium X-ray Absorption Near Edge Structure spectra

  20. Non-viral bone morphogenetic protein 2 transfection of rat dental pulp stem cells using calcium phosphate nanoparticles as carriers.

    NARCIS (Netherlands)

    Yang, X.; Walboomers, X.F.; Dolder, J. van den; Yang, F.; Bian, Z.; Fan, M.; Jansen, J.A.

    2008-01-01

    Calcium phosphate nanoparticles have shown potential as non-viral vectors for gene delivery. The aim of this study was to induce bone morphogenetic protein (Bmp)2 transfection in rat dental pulp stem cells using calcium phosphate nanoparticles as a gene vector and then to evaluate the efficiency and

  1. Characterization of calcium phosphate powders originating from Phyllacanthus imperialis and Trochidae Infundibulum concavus marine shells

    International Nuclear Information System (INIS)

    Tămăşan, M.; Ozyegin, L.S.; Oktar, F.N.; Simon, V.

    2013-01-01

    The study reports the preparation and characterization of powders consisting of the different phases of calcium phosphates that were obtained from the naturally derived raw materials of sea-shell origins reacted with H 3 PO 4 . Species of sea origin, such as corals and nacres, attracted a special interest in bone tissue engineering area. Nacre shells are built up of calcium carbonate in aragonite form crystallized in an organic matrix. In this work two natural marine origin materials (shells of echinoderm Sputnik sea urchin — Phyllacanthus imperialis and Trochidae Infundibulum concavus mollusk) were involved in the developing powders of calcium phosphate based biomaterials (as raw materials for bone-scaffolds) by hotplate and ultrasound methods. Thermal analyses of the as-prepared materials were made for an assessment of the thermal behavior and heat treatment temperatures. Samples from both sea shells each of them prepared by the above mentioned methods were subjected to thermal treatments at 450 °C and 850 °C in order to evaluate the crystalline transformations of the calcium phosphate structures in the heating process. By X-ray diffraction analyses various calcium phosphate phases were identified. In Sputnik sea urchins originated samples were found predominantly brushite and calcite as a small secondary phase, while in Trochidae I. concavus samples mainly monetite and HA phases were identified. Thermal treatment at 850 °C resulted flat-plate whitlockite crystals — β-MgTCP [(Ca, Mg) 3 (PO 4 ) 2 ] for both samples regardless the preparation method (ultrasound or hotplate) or the targeted Ca/P molar ratio according with XRD patterns. Scanning electron microscopy and Fourier transformed infrared spectroscopy were involved more in the characterization of these materials and the good correlations of the results of these methods were made. - Highlights: ► Calcium phosphate powders are obtained from the crushed shells of 2 “marine” species and H 3 PO 4

  2. Characterization of calcium phosphate powders originating from Phyllacanthus imperialis and Trochidae Infundibulum concavus marine shells

    Energy Technology Data Exchange (ETDEWEB)

    Tămăşan, M., E-mail: monica.tamasan@phys.ubbcluj.ro [Babeş-Bolyai University, Faculty of Physics and Interdisciplinary Research Institute on Bio-Nano-Sciences, Cluj-Napoca (Romania); Ozyegin, L.S. [Marmara University, Istanbul (Turkey); Oktar, F.N. [Marmara University, Faculty of Engineering, Department of Bioengineering, Göztepe Campus, Kadıköy 34722, Istanbul (Turkey); Marmara University, School of Health Related Professions, Department of Medical Imaging Technics, Haydarpaşa Campus, Tıbbiye Street, 49, Üsküdar 34668, Istanbul (Turkey); Marmara University, Nanotechnology and Biomaterials Application and Research Centre, Göztepe Campus, Kadıköy 34722, Istanbul (Turkey); Simon, V. [Babeş-Bolyai University, Faculty of Physics and Interdisciplinary Research Institute on Bio-Nano-Sciences, Cluj-Napoca (Romania)

    2013-07-01

    The study reports the preparation and characterization of powders consisting of the different phases of calcium phosphates that were obtained from the naturally derived raw materials of sea-shell origins reacted with H{sub 3}PO{sub 4}. Species of sea origin, such as corals and nacres, attracted a special interest in bone tissue engineering area. Nacre shells are built up of calcium carbonate in aragonite form crystallized in an organic matrix. In this work two natural marine origin materials (shells of echinoderm Sputnik sea urchin — Phyllacanthus imperialis and Trochidae Infundibulum concavus mollusk) were involved in the developing powders of calcium phosphate based biomaterials (as raw materials for bone-scaffolds) by hotplate and ultrasound methods. Thermal analyses of the as-prepared materials were made for an assessment of the thermal behavior and heat treatment temperatures. Samples from both sea shells each of them prepared by the above mentioned methods were subjected to thermal treatments at 450 °C and 850 °C in order to evaluate the crystalline transformations of the calcium phosphate structures in the heating process. By X-ray diffraction analyses various calcium phosphate phases were identified. In Sputnik sea urchins originated samples were found predominantly brushite and calcite as a small secondary phase, while in Trochidae I. concavus samples mainly monetite and HA phases were identified. Thermal treatment at 850 °C resulted flat-plate whitlockite crystals — β-MgTCP [(Ca, Mg){sub 3} (PO{sub 4}){sub 2}] for both samples regardless the preparation method (ultrasound or hotplate) or the targeted Ca/P molar ratio according with XRD patterns. Scanning electron microscopy and Fourier transformed infrared spectroscopy were involved more in the characterization of these materials and the good correlations of the results of these methods were made. - Highlights: ► Calcium phosphate powders are obtained from the crushed shells of 2

  3. The calcium-paracaseinate-phosphate-complex under conditions similar to those in cheese

    NARCIS (Netherlands)

    Monib, A.M.M.F.

    1962-01-01

    The complex of calcium-paracaseinate-phosphate is the matrix substance of cheese. The changes it undergoes during maturing determines many characteristics of the finished product.

    The preliminary studies of the effect of pH and sodium chloride on the swelling and solubility of the

  4. Bioactivity and Surface Reactivity of RF-sputtered Calcium Phosphate Thin Films

    NARCIS (Netherlands)

    Wal, Edwin van der

    2003-01-01

    Calcium phosphates (CaP) are known to be bioactive, i.e. able to bond to bone. This makes CaPs very suitable to be aplied as thin coatings on bone-implants. In this work we studied the physicochemical behaviour of CaP coatings applied with radio frequency (RF) magnetron sputtering, a deposition

  5. Ectopic osteoid and bone formation by three calcium-phosphate ceramics in rats, rabbits and dogs

    NARCIS (Netherlands)

    Wang, Liao; Zhang, B.; Bao, Chongyun; Habibovic, Pamela; Hu, J.; Zhang, Xingdong

    2014-01-01

    Calcium phosphate ceramics with specific physicochemical properties have been shown to induce de novo bone formation upon ectopic implantation in a number of animal models. In this study we explored the influence of physicochemical properties as well as the animal species on material-induced ectopic

  6. In vivo performance of microstructured calcium phosphate formulated in novel water-free carriers

    NARCIS (Netherlands)

    Davison, N.L.; Yuan, Huipin; de Bruijn, Joost Dick; Barrere-de Groot, F.YF.

    2012-01-01

    Osteoinductive calcium phosphate (CaP) ceramics can be combined with polymeric carriers to make shapeable bone substitutes as an alternative to autologous bone; however, carriers containing water may degrade the ceramic surface microstructure, which is crucial to bone formation. In this study five

  7. Bone response adjacent to calcium phosphate electrostatic spray deposition coated implants: an experimental study in goats.

    NARCIS (Netherlands)

    Manders, P.J.D.; Wolke, J.G.C.; Jansen, J.A.

    2006-01-01

    BACKGROUND: A new technique to deposit calcium phosphate (CaP) coatings onto titanium substrates has been developed recently. This electrostatic spray deposition (ESD) technique seems to be very promising. It appears to have clinical advantages such as an inexpensive and simple set-up, high

  8. Simultaneous recovery of calcium phosphate granules and methane in anaerobic treatment of black water

    NARCIS (Netherlands)

    Cunha Costa, da J.M.R.; Tervahauta, T.; Weijden, van der R.D.; Hernández Leal, L.; Zeeman, G.; Buisman, C.J.N.

    2017-01-01

    Calcium phosphate (CaP) granules were discovered in the anaerobic treatment of vacuum collected black water (BW), using upflow anaerobic sludge blanket (UASB) technology. This allows simultaneous recovery of CaP granules and methane in the UASB reactor. However, the role of BW composition on CaP

  9. The effect of inorganic additives to calcium phosphate on in vitro behavior of osteoblasts and osteoclasts

    NARCIS (Netherlands)

    Yang, Liang; Perez-Amodio, Soledad; Barrère, F.; Everts, Vincent; van Blitterswijk, Clemens; Habibovic, Pamela

    2010-01-01

    This study describes a medium-throughput system based on deposition of calcium phosphate films in multi-well tissue culture plates that can be used to study the effect of inorganic additives on the behavior of osteoblasts and osteoclasts in a standardized manner. All tested elements, copper, zinc,

  10. The effects of inorganic additives to calcium phosphate on in vitro behavior of osteoblasts and osteoclasts

    NARCIS (Netherlands)

    Yang, L.; Perez-Amodio, S.; Barrere-de Groot, F.Y.F.; Everts, V.; van Blitterswijk, C.A.; Habibovic, P.

    2010-01-01

    This study describes a medium-throughput system based on deposition of calcium phosphate films in multi-well tissue culture plates that can be used to study the effect of inorganic additives on the behavior of osteoblasts and osteoclasts in a standardized manner. All tested elements, copper, zinc,

  11. Controlling surface microstructure of calcium phosphate ceramic from random to custom-design

    NARCIS (Netherlands)

    Wang, Liao; Luo, Xiaoman; Barbieri, D.; Bao, Chongyun; Yuan, Huipin

    2014-01-01

    Calcium phosphate ceramics have long been studied as bone graft substitutes due to their similarity with the mineral constitute of bone and teeth, excellent biocompatibility and bioactivity. Chemical composition, macrostructure and surface microstructure are believed to be important for the bone

  12. Variation of the bone forming ability with the physicochemical properties of calcium phosphate bone substitutes

    NARCIS (Netherlands)

    Duan, Rongquan; Barbieri, Davide; Luo, Xiaoman; Weng, Jie; Bao, Chongyun; De Bruijn, Joost D.; Yuan, Huipin

    2018-01-01

    Because of their bioactive properties and chemical similarity to the inorganic component of bone, calcium phosphate (CaP) materials are widely used for bone regeneration. Six commercially available CaP bone substitutes (Bio-Oss, Actifuse, Bi-Ostetic, MBCP, Vitoss and chronOs) as well as two

  13. A theranostic agent to enhance osteogenic and magnetic resonance imaging properties of calcium phosphate cements

    NARCIS (Netherlands)

    Ventura, M.; Sun, Y.; Cremers, S.; Borm, P.; Tahmasebi Birgani, Zeinab; Habibovic, Pamela; Heerschap, A.; van der Kraan, P.M.; Jansen, J.A.; Walboomers, X.F.

    2014-01-01

    With biomimetic biomaterials, like calcium phosphate cements (CPCs), non-invasive assessment of tissue regeneration is challenging. This study describes a theranostic agent (TA) to simultaneously enhance both imaging and osteogenic properties of such a bone substitute material. For this purpose,

  14. Dense and porous titanium substrates with a biomimetic calcium phosphate coating

    Energy Technology Data Exchange (ETDEWEB)

    Ribeiro, A.A., E-mail: aantunesr@yahoo.com.br [Powder Technology Laboratory, Materials Processing and Characterization Division, National Institute of Technology, No. 82 Venezuela Avenue, Room 602, 20081-312 Rio de Janeiro, RJ (Brazil); Balestra, R.M. [Powder Technology Laboratory, Materials Processing and Characterization Division, National Institute of Technology, No. 82 Venezuela Avenue, Room 602, 20081-312 Rio de Janeiro, RJ (Brazil); Rocha, M.N. [Metallurgical and Materials Engineering Program, COPPE, Federal University of Rio de Janeiro, P.O. Box 68505, 21941-972 Rio de Janeiro, RJ (Brazil); Peripolli, S.B. [Materials Metrology Division, National Institute of Metrology, Normalization and Quality, No. 50 Nossa Senhora das Gracas Street, Building 3, 25250-020 Duque de Caxias, RJ (Brazil); Andrade, M.C. [Polytechnic Institute of Rio de Janeiro, Rio de Janeiro State University, s/n, Alberto Rangel Street, 28630-050 Nova Friburgo, RJ (Brazil); Pereira, L.C. [Metallurgical and Materials Engineering Program, COPPE, Federal University of Rio de Janeiro, P.O. Box 68505, 21941-972 Rio de Janeiro, RJ (Brazil); Oliveira, M.V. [Powder Technology Laboratory, Materials Processing and Characterization Division, National Institute of Technology, No. 82 Venezuela Avenue, Room 602, 20081-312 Rio de Janeiro, RJ (Brazil)

    2013-01-15

    Highlights: Black-Right-Pointing-Pointer A biomimetic coating method with simplified solution is proposed. Black-Right-Pointing-Pointer Titanium substrates are submitted to chemical and heat treatments. Black-Right-Pointing-Pointer Titanium substrates are coated with biocompatible calcium phosphate phases. Black-Right-Pointing-Pointer The simplified solution shows potential to be applied as a coating technique. - Abstract: The present work studied a biomimetic method using a simplified solution (SS) with calcium and phosphorus ions for coating titanium substrates, in order to improve their bioactivity. Commercially pure titanium dense sheet, microporous and macroporous titanium samples, both produced by powder metallurgy, were treated in NaOH solution followed by heat-treating and immersed in SS for 7, 14 or 21 days. The samples characterization was performed by quantitative metallographic analysis, confocal scanning optical microscopy, scanning electron microscopy, energy dispersive spectroscopy and low angle X-ray diffraction. The results showed coatings with calcium phosphate precipitation in all samples, with globular or plate-like morphology, typical of hydroxyapatite and octacalcium phosphate, respectively, indicating that the solution (SS) has potential for coating titanium substrates. In addition, the different surfaces of substrates had an effect on the formed calcium phosphate phase and thickness of coatings, depending on the substrate type and imersion time in the simplified solution.

  15. Self-assembly of calcium phosphate nanoparticles into hollow spheres induced by dissolved amino acids

    NARCIS (Netherlands)

    Hagmeyer, D.; Ganesan, K.; Ruesing, J.; Schunk, D.; Mayer, C.; Dey, A.; Sommerdijk, N.A.J.M.; Epple, M.

    2011-01-01

    Nanoparticles of calcium phosphate assemble spontaneously within a few seconds into hollow spheres with a diameter around 200–300 nm in the presence of dissolved amino acids and dipeptides. The process of formation was followed by cryo-transmission electron microscopy (cryoTEM), proving their hollow

  16. Nano-scale study of the nucleation and growth of calcium phosphate coating

    NARCIS (Netherlands)

    Barrère, F.; Snel, M.M.E.; van Blitterswijk, Clemens; de Groot, K.; Layrolle, Pierre

    2004-01-01

    The nucleation and growth of a calcium phosphate (Ca-P) coating deposited on titanium implants from simulated body fluid was investigated by using atomic force microscopy (AFM) and environmental scanning electron microscopy (ESEM). Forty titanium alloy plates were assigned into two groups. One group

  17. Calcium phosphate coated eletrospun fiber matrices as scaffold for bone tissue engineering

    NARCIS (Netherlands)

    Nandakumar, A.; Yang, Liang; Habibovic, Pamela; van Blitterswijk, Clemens

    2010-01-01

    Electrospun polymeric scaffolds are used for various tissue engineering applications. In this study, we applied a biomimetic coating method to provide electrospun scaffolds from a block copolymer-poly(ethylene oxide terephthalate)−poly(buthylene terephthalate), with a calcium phosphate layer to

  18. In vitro and in vivo reactivity of porous, electrosprayed calcium phosphate coatings.

    NARCIS (Netherlands)

    Leeuwenburgh, S.C.G.; Wolke, J.G.C.; Siebers, M.C.; Schoonman, J.; Jansen, J.A.

    2006-01-01

    The dissolution and/or precipitation behaviour of porous calcium phosphate (CaP) coatings, deposited using electrostatic spray deposition (ESD), was investigated (a) in vitro after soaking in simulated body fluid (SBF) for several time periods (2, 4, 8, and 12 weeks), and (b) in vivo after

  19. Bioactivity tests of calcium phosphates with variant molar ratios of main components.

    Science.gov (United States)

    Pluta, Klaudia; Sobczak-Kupiec, Agnieszka; Półtorak, Olga; Malina, Dagmara; Tyliszczak, Bożena

    2018-03-09

    Calcium phosphates constitute attractive materials of biomedical applications. Among them particular attention is devoted to bioactive hydroxyapatite (HAp) and bioresorbable tricalcium phosphate (TCP) that possess ability to bind to living bones and can be used clinically as important bone substitutes. Notably, in vivo bone bioactivity can be predicted from apatite formation of bone immersed in SBF fluids. Thus, analyses of behavior of calcium phosphates immersed in various bio fluids are of great importance. Recently, stoichiometric HAp and TCP structures have been widely studied, whereas only limited number of publications have been devoted to analyses of nonstoichiometric calcium phosphates. Here, we report physicochemical analysis of natural and synthetic phosphates with variable Ca/P molar ratios. Subsequently attained structures were subjected to incubation in either artificial saliva or Ringer's fluids. Both pH and conductivity of such fluids were determined before and after incubation. Furthermore, the influence of the Ca/P values on such parameters was exemplified. Physicochemical analysis of received materials was performed by XRD and FT-IR characterization techniques. Their potential antibacterial activity and behavior in the presence of infectious microorganisms as Escherichia coli and Staphylococcus aureus was also evaluated. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part A, 2018. © 2018 Wiley Periodicals, Inc.

  20. Structure and properties of calcium iron phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Qian, Bin [School of Science, Southwest University of Science and Technology, Mianyang 621010 (China); Liang, Xiaofeng, E-mail: xfliangswust@gmail.com [Analytical and Testing Center, Southwest University of Science and Technology, Mianyang 621010 (China); School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621010 (China); Wang, Cuiling; Yang, Shiyuan [School of Materials Science and Engineering, Southwest University of Science and Technology, Mianyang 621010 (China)

    2013-11-15

    The structural properties of xCaO–(100 − x) (0.4Fe{sub 2}O{sub 3}–0.6P{sub 2}O{sub 5}) (x = 0, 10, 20, 30, 40, 50 mol%) glasses have been investigated by XRD, DTA, IR and Raman spectroscopy. XRD analysis has confirmed that the majority of samples are X-ray amorphous, and EDS analysis indicates that the glass matrix can accommodate ≈30 mol% CaO. IR and Raman spectra show that the glass structure consists predominantly of pyrophosphate (Q{sup 1}) units. IR spectra indicate that the phosphate network is depolymerized with the addition of CaO content. The density and glass transition temperature (T{sub g}) increase with increasing CaO content for the glasses. This behavior indicates that the addition of CaO improves the strength of the cross-links between the phosphate chains of the glass.

  1. Processing and properties of calcium phosphates bioceramics by hot isostatic pressing

    Directory of Open Access Journals (Sweden)

    Boilet Laurent

    2013-11-01

    Full Text Available Stoichiometric β-tricalcium phosphate (β-TCP, hydroxyapatite (HA and biphasic calcium phosphate (TCP/HA 60/40 %wt, BCP40 powders were synthesized by chemical precipitation of aqueous solutions of diammonium phosphate and calcium nitrate. After a calcination treatment and a milling step, powders were shaped by slip-casting. The sintering temperature effect on the density and the average grain size was investigated. By natural sintering, densities between 98 and 99.8% were obtained. Hot Isostatic Pressing (HIP treatment was carried out after a pre-sintering of these materials. Transparent or translucent samples were obtained, indicating a relative density very close to the theoretical value (>99.9%. Mechanical properties (three-point bending strength, fracture toughness, Young's modulus and Vickers hardness were measured on hipped materials with similar grain size (∼0.7μm.

  2. Calcium phosphate holmium-166 ceramic to addition in bone cement: synthesis and characterization

    Energy Technology Data Exchange (ETDEWEB)

    Donanzam, Blanda A.; Campos, Tarcisio P.R., E-mail: campos@nuclear.ufmg.b [Universidade do Federal de Minas Gerais (DEN/UFMG), Belo Horizonte, MG (Brazil). Escola de Engenharia. Dept. de Engenharia Nuclear; Dalmazio, Ilza; Valente, Eduardo S., E-mail: id@cdtn.b, E-mail: valente@cdtn.b [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2011-07-01

    Spine metastases are a common and painful complication of cancer. The treatment often consists of bone cement injection (vertebroplasty or kyphoplasty) within vertebral body for vertebrae stabilization, followed by external beam radiation therapy. Recently, researchers introduced the concept of radioactive bone cement for spine tumors therapy. Then, investigations about bioactive and radioactive materials became interesting. In this study, we present the synthesis of calcium phosphate incorporated holmium (CaP-Ho) via sol-gel technique, and its characterization by XRD, FT-IR, NA and SEM. Results showed a multiphasic bioceramic composed mainly of hydroxyapatite, {beta}-tricalcium phosphate, holmium phosphate and traces of calcium pyrophosphate. Furthermore, the nuclide Ho-166 was the major radioisotope produced. Despite that, the radioactive bioceramic CaP-{sup 166}Ho must be investigated in clinical trials to assure its efficacy and safety on spine tumors treatment (author)

  3. Calcium phosphate holmium-166 ceramic to addition in bone cement: synthesis and characterization

    International Nuclear Information System (INIS)

    Donanzam, Blanda A.; Campos, Tarcisio P.R.

    2011-01-01

    Spine metastases are a common and painful complication of cancer. The treatment often consists of bone cement injection (vertebroplasty or kyphoplasty) within vertebral body for vertebrae stabilization, followed by external beam radiation therapy. Recently, researchers introduced the concept of radioactive bone cement for spine tumors therapy. Then, investigations about bioactive and radioactive materials became interesting. In this study, we present the synthesis of calcium phosphate incorporated holmium (CaP-Ho) via sol-gel technique, and its characterization by XRD, FT-IR, NA and SEM. Results showed a multiphasic bioceramic composed mainly of hydroxyapatite, β-tricalcium phosphate, holmium phosphate and traces of calcium pyrophosphate. Furthermore, the nuclide Ho-166 was the major radioisotope produced. Despite that, the radioactive bioceramic CaP- 166 Ho must be investigated in clinical trials to assure its efficacy and safety on spine tumors treatment (author)

  4. Corrosion control of galvanized steel using a phosphate/calcium ion inhibitor mixture

    International Nuclear Information System (INIS)

    Zin, I.M.; Lyon, S.B.; Pokhmurskii, V.I.

    2003-01-01

    The corrosion inhibition of galvanized steel was studied in artificial acid rain solution using extracts of pigments normally used in organic coatings for corrosion control. It was established that a combination of zinc phosphate/molybdate and calcium ion exchange silica has a significant synergetic anticorrosion effect in the acid rain solution compared to the pigments used alone. Further, the charge transfer resistance of galvanized steel in acid rain solution saturated by the above pigment blend approaches that of strontium chromate in artificial acid rain solution. Use of the pigment blend was found to lead to development of a protective film, which is thought to be a complex mixture of calcium phosphates and zinc phosphate

  5. Extrusion-based, three-dimensional printing of calcium-phosphate scaffolds

    Science.gov (United States)

    Witek, Lukasz

    Small or large bone defects, can occur due to a variety of reasons: congenital disorders, infections, tumors, or traumas which can lead to significant disabilities. There is an assortment of bone grafting procedures, each having their own respective advantages and disadvantages and exhibiting certain essential characteristics. Among the available grafts, autogenous (autograft), allograft, xenograft, and alloplasts, all exhibit a minimum of two-thirds of the essential characteristics and have been proven useful in fully or partially repairing skeletal defects. However, different host-to-grafting material responses have been reported and should be taken into consideration when determining treatment options. A large range of physical and chemical properties can be achieved with calcium phosphate based materials, which possess two of the ideal characteristics for grafting procedures: osteoconduction and osseointegration. Calcium phosphate based scaffolds composed of hydroxyapatite (HA), beta-tri-calcium phosphate (beta-TCP), or a combination of both (HA/beta-TCP) were investigated as materials for three-dimensional printing process to create layer-by-layer structures for use as bone regeneration scaffolds. Different calcium-phosphate phases will result in different degrees of in vivo dissolution and/or cell-mediated resorption. There has been a growing interest in BCP because it has been shown that this material improves the formation of new bone inside the implanted scaffold. The literature indicates that the faster dissolution rate of ?-TCP would be greatly responsible of this enhancement. However, in vitro tests indicate that fast dissolution can decrease the mechanical strength of BCP scaffolds. Furthermore, studies reported that HA has higher mechanical strength and lower degradation rate than beta-TCP. Therefore, the HA/beta-TCP ratio is a key parameter controlling the performance of the scaffold for bone repair applications, since it determines degradation rate

  6. A novel biodegradable nicotinic acid/calcium phosphate composite coating on Mg-3Zn alloy

    Energy Technology Data Exchange (ETDEWEB)

    Song, Yingwei, E-mail: ywsong@imr.ac.cn; Shan, Dayong; Han, En-Hou

    2013-01-01

    A novel biodegradable composite coating is prepared to reduce the biodegradation rate of Mg-3Zn alloy. The Mg-3Zn substrate is first immersed into 0.02 mol L{sup -1} nicotinic acid (NA) solution, named as vitamin B{sub 3}, to obtain a pretreatment film, and then the electrodeposition of calcium phosphate coating with ultrasonic agitation is carried out on the NA pretreatment film to obtain a NA/calcium phosphate composite coating. Surface morphology is observed by scanning electron microscopy (SEM). Chemical composition is determined by X-ray diffraction (XRD) and EDX. Protection property of the coatings is evaluated by electrochemical tests. The biodegradable behavior is investigated by immersion tests. The results indicate that a thin but compact bottom layer can be obtained by NA pretreatment. The electrodeposition calcium phosphate coating consists of many flake particles and ultrasonic agitation can greatly improve the compactness of the coating. The composite coating is biodegradable and can reduce the biodegradation rate of Mg alloys in stimulated body fluid (SBF) for twenty times. The biodegradation process of the composite coating can be attributed to the gradual dissolution of the flake particles into chippings. - Highlights: Black-Right-Pointing-Pointer NA/calcium phosphate composite coating is prepared to protect Mg-3Zn alloy implant. Black-Right-Pointing-Pointer Nicotinic acid (vitamin B{sub 3}) is available to obtain a protective bottom film. Black-Right-Pointing-Pointer Ultrasonic agitation greatly improves the compactness of calcium phosphate coating. Black-Right-Pointing-Pointer The composite coating can reduce the biodegradation rate of Mg-3Zn twenty times. Black-Right-Pointing-Pointer The composite coating is biodegraded by the dissolution of flakes into chippings.

  7. Nanostructured silicate substituted calcium phosphate (NanoSiCaPs) nanoparticles — Efficient calcium phosphate based non-viral gene delivery systems

    Energy Technology Data Exchange (ETDEWEB)

    Shekhar, Sudhanshu [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Center for Complex Engineered Multifunctional Materials, University of Pittsburgh, Pittsburgh, PA 15261 (United States); McGowan Institute of Regenerative Medicine, University of Pittsburgh, PA 15261 (United States); Roy, Abhijit; Hong, Daeho [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Kumta, Prashant N., E-mail: pkumta@pitt.edu [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Department of Chemical Engineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Department of Mechanical Engineering and Materials Science, University of Pittsburgh, Pittsburgh, PA 15260 (United States); Center for Complex Engineered Multifunctional Materials, University of Pittsburgh, Pittsburgh, PA 15261 (United States); McGowan Institute of Regenerative Medicine, University of Pittsburgh, PA 15261 (United States)

    2016-12-01

    Nanostructured ceramic particles, particularly, nanoparticles of calcium phosphate (CaP) remain an attractive option among the various types of non-viral gene delivery vectors studied because of their safety, biocompatibility, biodegradability, and ease of handling as well as their adsorptive capacity for DNA. We have accordingly developed an enhanced version of nanostructured calcium phosphates (NanoCaPs), by substituting known amounts of silicate for phosphate in the hydroxyapatite (HA) lattice (NanoSiCaPs). Results indicate that in addition to the excellent transfection levels exhibited by un-substituted NanoCaPs alone in vitro, an additional 20–50% increase in transfection is observed for NanoCaPs containing 8.3–50 mol% silicate aptly called NanoSiCaPs, owing to its rapid dissolution properties enabling nanoparticles escaping the lysosomal degradation. However, high silicate substitution (> 50 mol%) resulted in a drastic decline in transfection as the synthesized NanoCaPs deviated far from the characteristic hydroxyapatite phase formed as evidenced by the materials characterization results. - Highlights: • Successful demonstration of nanostructured NanoSiCaPs formation • Demonstration of superior transfection of NanoSiCaPs contrasted to NanoCaPs • Silicate substitution leads to smaller aggregates of nanoparticle complexes. • Enhanced dissolution of NanoSiCaPs demonstrated • Faster NanoSiCaPs dissolution leads to escape of pDNA from lysosomal degradation.

  8. Yolk-Shell Porous Microspheres of Calcium Phosphate Prepared by Using Calcium L-Lactate and Adenosine 5'-Triphosphate Disodium Salt: Application in Protein/Drug Delivery.

    Science.gov (United States)

    Ding, Guan-Jun; Zhu, Ying-Jie; Qi, Chao; Sun, Tuan-Wei; Wu, Jin; Chen, Feng

    2015-06-26

    A facile and environmentally friendly approach has been developed to prepare yolk-shell porous microspheres of calcium phosphate by using calcium L-lactate pentahydrate (CL) as the calcium source and adenosine 5'-triphosphate disodium salt (ATP) as the phosphate source through the microwave-assisted hydrothermal method. The effects of the concentration of CL, the microwave hydrothermal temperature, and the time on the morphology and crystal phase of the product are investigated. The possible formation mechanism of yolk-shell porous microspheres of calcium phosphate is proposed. Hemoglobin from bovine red cells (Hb) and ibuprofen (IBU) are used to explore the application potential of yolk-shell porous microspheres of calcium phosphate in protein/drug loading and delivery. The experimental results indicate that the as-prepared yolk-shell porous microspheres of calcium phosphate have relatively high protein/drug loading capacity, sustained protein/drug release, favorable pH-responsive release behavior, and a high biocompatibility in the cytotoxicity test. Therefore, the yolk-shell porous microspheres of calcium phosphate have promising applications in various biomedical fields such as protein/drug delivery. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  9. Comparative study on in vivo response of porous calcium carbonate composite ceramic and biphasic calcium phosphate ceramic

    International Nuclear Information System (INIS)

    He, Fupo; Ren, Weiwei; Tian, Xiumei; Liu, Wei; Wu, Shanghua; Chen, Xiaoming

    2016-01-01

    In a previous study, robust calcium carbonate composite ceramics (CC/PG) were prepared by using phosphate-based glass (PG) as an additive, which showed good cell response. In the present study the in vivo response of porous CC/PG was compared to that of porous biphasic calcium phosphate ceramics (BCP), using a rabbit femoral critical-size grafting model. The materials degradation and bone formation processes were evaluated by general observation, X-ray radiography, micro-computed tomography, and histological examination. The results demonstrated excellent biocompatibility and osteoconductivity, and progressive degradation of CC/PG and BCP. Although the in vitro degradation rate of CC/PG was distinctly faster than that of BCP, at 4 week post-implantation, the bone generation and material degradation of CC/PG were less than those of BCP. Nevertheless, at postoperative week 8, the increment of bone formation and material degradation of CC/PG was pronouncedly larger than that of BCP. These results show that CC/PG is a potential resorbable bone graft aside from the traditional synthetic ones. - Highlights: • A calcium carbonate composite ceramic (CC/PG) was acquired. • The in vivo response of CC/PG and biphasic calcium phosphate (BCP) was compared. • CC/PG showed faster in vitro degradation rate compared to BCP. • CC/PG showed less in vivo degradation and bone formation than BCP at week 4. • CC/PG had larger increment of degradation and bone formation than BCP at week 8.

  10. Comparative study on in vivo response of porous calcium carbonate composite ceramic and biphasic calcium phosphate ceramic

    Energy Technology Data Exchange (ETDEWEB)

    He, Fupo, E-mail: fphebm@126.com [School of Electromechanical Engineering, Guangdong University of Technology, Guangzhou 510006 (China); Ren, Weiwei [School of Electromechanical Engineering, Guangdong University of Technology, Guangzhou 510006 (China); Tian, Xiumei [Department of Biomedical Engineering, School of Basic Sciences, Guangzhou Medical University, Guangzhou 510182 (China); Liu, Wei; Wu, Shanghua [School of Electromechanical Engineering, Guangdong University of Technology, Guangzhou 510006 (China); Chen, Xiaoming, E-mail: xmchenw@126.com [Department of Biomedical Engineering, School of Basic Sciences, Guangzhou Medical University, Guangzhou 510182 (China)

    2016-07-01

    In a previous study, robust calcium carbonate composite ceramics (CC/PG) were prepared by using phosphate-based glass (PG) as an additive, which showed good cell response. In the present study the in vivo response of porous CC/PG was compared to that of porous biphasic calcium phosphate ceramics (BCP), using a rabbit femoral critical-size grafting model. The materials degradation and bone formation processes were evaluated by general observation, X-ray radiography, micro-computed tomography, and histological examination. The results demonstrated excellent biocompatibility and osteoconductivity, and progressive degradation of CC/PG and BCP. Although the in vitro degradation rate of CC/PG was distinctly faster than that of BCP, at 4 week post-implantation, the bone generation and material degradation of CC/PG were less than those of BCP. Nevertheless, at postoperative week 8, the increment of bone formation and material degradation of CC/PG was pronouncedly larger than that of BCP. These results show that CC/PG is a potential resorbable bone graft aside from the traditional synthetic ones. - Highlights: • A calcium carbonate composite ceramic (CC/PG) was acquired. • The in vivo response of CC/PG and biphasic calcium phosphate (BCP) was compared. • CC/PG showed faster in vitro degradation rate compared to BCP. • CC/PG showed less in vivo degradation and bone formation than BCP at week 4. • CC/PG had larger increment of degradation and bone formation than BCP at week 8.

  11. Compression and rupture cycles as tools for compressibility characterization application to apatitic calcium phosphates

    Energy Technology Data Exchange (ETDEWEB)

    Pontier, C. [S.P.C.T.S., Faculte des Sciences, Limoges (France); G.E.F., Faculte de Pharmacie, Limoges (France); Viana, M.; Chulia, D. [G.E.F., Faculte de Pharmacie, Limoges (France); Champion, E.; Bernache-Assollant, D. [S.P.C.T.S., Faculte des Sciences, Limoges (France)

    2002-07-01

    Measurement of the cycles of compression and rupture helps to understand the phenomena occurring during compaction. Different parameters are deduced from the cycles, such as the packing of the material and energies used during compression. The ratio between the energy of rupture and the energy of compaction defines the efficacy of compaction of the materials. This technique is applied to ceramic materials using apatitic calcium phosphates with a Ca/P molar ratio of 1.5 (apatitic tricalcium phosphate and {beta}-tricalcium phosphate) and 1.667 (stoichiometric hydroxyapatite). The methodology uses a uniaxial instrumented press to plot the cycles of compaction and rupture. The results point out the good compaction and cohesion properties of apatitic tricalcium phosphate, compared to the other apatitic materials. (orig.)

  12. Interaction of adsorption of reactive yellow 4 from aqueous solutions onto synthesized calcium phosphate

    Directory of Open Access Journals (Sweden)

    H. El Boujaady

    2017-01-01

    Full Text Available The interaction of reactive yellow 4 with Apatitic Tricalcium Phosphate (PTCa has been investigated in aqueous medium to understand the mechanism of adsorption and explore the potentiality of this phosphate toward controlling pollution resulting from textile dyes. Transmission electron microscopy (TEM analysis demonstrates that the adsorbent is composed of needle-like nanoparticles and the SAED pattern exhibits spotted sharp and continuous rings that evidence polycrystalline grains. X-ray diffraction results showed that, the crystallinity of the dye decreased after interaction with RY4 indicatating incorporation of the dye into the micropores and macropores of the adsorbent. The results of Fourier transform infrared (FTIR spectroscopy indicate that the adsorption is due to the electrostatic interaction between the –SO3- groups of dye and the surface of the Phosphate. The desorption efficiency was very high at about 99.4%. The presence of calcium ions favored the adsorption of the dye, while the phosphate ions inhibited it.

  13. Hereditary deafness with hydrops and anomalous calcium phosphate deposits

    International Nuclear Information System (INIS)

    Johnsson, L.G.; Rouse, R.C.; Hawkins, J.E. Jr.; Kingsley, T.C.; Wright, C.G.

    1981-01-01

    The temporal bones from a 58-year-old white woman who had had hereditary congenital deafness were examined with the techniques of microdissection and surface preparations followed by sectioning of the modiolus. There was bilateral, almost total sensorineural degeneration, which also involved the saccule. The degeneration of the distal processes of the cochlear neurons in the osseous spiral lamina was almost complete, whereas numerous ganglion cells and proximal processes remained in the modiolus and the internal auditory canal. Severe cochleo-saccular hydrops was present in the left ear with Reissner's membrane bulging into the horizontal canal. X-ray diffraction and electron probe analysis were used to study the abnormal crystalline deposits in both ears. On the left side the saccular otoconia were composed of calcite, but the utricular macula was covered by a crust of apatite spherulites. More apatite occurred around the maculae and in the scala media. The cupulae were composed of apatite and octacalcium phosphate. On the right side the utricular otoconia were of normal calcite, but there was a deposit of apatite on the macula sacculi. The upper part of the scala media was completely filled by a deposit of apatite and octacalcium phosphate

  14. Hereditary deafness with hydrops and anomalous calcium phosphate deposits

    Energy Technology Data Exchange (ETDEWEB)

    Johnsson, L.G.; Rouse, R.C.; Hawkins, J.E. Jr.; Kingsley, T.C.; Wright, C.G.

    1981-11-01

    The temporal bones from a 58-year-old white woman who had had hereditary congenital deafness were examined with the techniques of microdissection and surface preparations followed by sectioning of the modiolus. There was bilateral, almost total sensorineural degeneration, which also involved the saccule. The degeneration of the distal processes of the cochlear neurons in the osseous spiral lamina was almost complete, whereas numerous ganglion cells and proximal processes remained in the modiolus and the internal auditory canal. Severe cochleo-saccular hydrops was present in the left ear with Reissner's membrane bulging into the horizontal canal. X-ray diffraction and electron probe analysis were used to study the abnormal crystalline deposits in both ears. On the left side the saccular otoconia were composed of calcite, but the utricular macula was covered by a crust of apatite spherulites. More apatite occurred around the maculae and in the scala media. The cupulae were composed of apatite and octacalcium phosphate. On the right side the utricular otoconia were of normal calcite, but there was a deposit of apatite on the macula sacculi. The upper part of the scala media was completely filled by a deposit of apatite and octacalcium phosphate.

  15. Effect of Fluoride, Casein Phosphopeptide–Amorphous Calcium Phosphate and Casein Phosphopeptide–Amorphous Calcium Phosphate Fluoride on Enamel Surface Microhardness After Microabrasion: An In Vitro Study

    Directory of Open Access Journals (Sweden)

    Ghazaleh Ahmadi Zenouz

    2016-03-01

    Full Text Available Objectives: This study aimed to assess the effect of applying casein phosphopeptide–amorphous calcium phosphate (CPP-ACP paste, casein phosphopeptide–amorphous calcium phosphate fluoride (CPP-ACPF paste and sodium fluoride gel on surface microhardness of enamel after microabrasion.Materials and Methods: Thirty freshly extracted human premolars were selected. All samples were subjected to hardness indentations made with the Vickers hardness machine and the average value was recorded as the initial surface microhardness. The specimens were then randomly divided into three groups (n=10 of CPP-ACPF, fluoride and CPP-ACP. The teeth were micro-abraded with Opalustre. Microhardness test was performed to assess the post-abrasion hardness. Three remineralization modalities were performed on samples of each group. The enamel surface microhardness measurements were performed. To compare the difference between groups, the rehardening and softening values were defined. One-way ANOVA and Tukey’s post hoc test at a significance level of 5% were used for statistical analysis.Results: The mean microhardness value (MMV had a significant decrease after microabrasion from baseline. The MMV had a significant increase after remineralization in all groups. The MMV of CPP-ACPF group was significantly more than that of fluoride group (P=0.027. The rehardening value of fluoride group was significantly more than that of other groups (P<0.001.Conclusion: All the remineralizing agents were effective for rehardening the enamel after microabrasion. The CPP-ACP and CPP-ACPF pastes are effective, but to a lesser extent than neutral sodium fluoride gel in remineralizing enamel surface. Incorporation of fluoride to CPP-ACP formulation does not provide any additional remineralizing potential.Keywords: Casein phosphopeptide-amorphous calcium phosphate nanocomplex; Enamel Microabrasion; Hardness; Sodium Fluoride

  16. Interaction of bovine gallbladder mucin and calcium-binding protein: effects on calcium phosphate precipitation

    NARCIS (Netherlands)

    Afdhal, N. H.; Ostrow, J. D.; Koehler, R.; Niu, N.; Groen, A. K.; Veis, A.; Nunes, D. P.; Offner, G. D.

    1995-01-01

    Gallstones consist of calcium salts and cholesterol crystals, arrayed on a matrix of gallbladder mucin (GBM), and regulatory proteins like calcium-binding protein (CBP). To determine if interactions between CBP and GBM follow a biomineralization scheme, their mutual binding and effects on CaHPO4

  17. Ectopic osteoid and bone formation by three calcium-phosphate ceramics in rats, rabbits and dogs.

    Directory of Open Access Journals (Sweden)

    Liao Wang

    Full Text Available Calcium phosphate ceramics with specific physicochemical properties have been shown to induce de novo bone formation upon ectopic implantation in a number of animal models. In this study we explored the influence of physicochemical properties as well as the animal species on material-induced ectopic bone formation. Three bioceramics were used for the study: phase-pure hydroxyapatite (HA sintered at 1200°C and two biphasic calcium phosphate (BCP ceramics, consisting of 60 wt.% HA and 40 wt.% TCP (β-Tricalcium phosphate, sintered at either 1100°C or 1200°C. 108 samples of each ceramic were intramuscularly implanted in dogs, rabbits, and rats for 6, 12, and 24 weeks respectively. Histological and histomorphometrical analyses illustrated that ectopic bone and/or osteoid tissue formation was most pronounced in BCP sintered at 1100°C and most limited in HA, independent of the animal model. Concerning the effect of animal species, ectopic bone formation reproducibly occurred in dogs, while in rabbits and rats, new tissue formation was mainly limited to osteoid. The results of this study confirmed that the incidence and the extent of material-induced bone formation are related to both the physicochemical properties of calcium phosphate ceramics and the animal model.

  18. Physicochemical Properties of Calcium Phosphate Based Coating on Gutta-Percha Root Canal Filling

    Directory of Open Access Journals (Sweden)

    Afaf Al-Haddad

    2015-01-01

    Full Text Available Dental Gutta-percha (GP is a polymer based standard root canal filling material that has been widely used in dentistry. However, it has an inadequate sealing ability and adhesion to root dentin. The aim of this study is to coat GP with a bioactive material to enhance its sealing ability and adhesion to the root sealer and subsequently to the root dentin. The choice of coating method is limited by the nature of GP as it requires a technique that is not governed by high temperatures or uses organic solvents. In this study, biomimetic coating technique using 1.5 Tas-simulated body fluids (SBF was employed to coat the treated GP cones. The coated samples were characterized using Fourier transform infrared spectroscopy (FTIR, X-ray Diffraction (XRD, and field emission scanning electron microscope (FESEM. The presence of hydroxyl, carbonate, and phosphate groups was detected by FTIR while the formation of hydroxyapatite (HA/calcium phosphate was confirmed with XRD. FESEM revealed uniform, thin, and crystalline HA calcium phosphate coating. The adhesion of the coating to the GP substrate was assessed with microscratch technique. It was viable with cohesive failure mode. In conclusion, Tas-SBF is able to coat pretreated GP cones with a crystalline apatitic calcium phosphate layer.

  19. Synthesis of some calcium phosphate crystals using the useful biomass for immobilization of microorganisms

    International Nuclear Information System (INIS)

    Kohiruimaki, T

    2011-01-01

    Three sources of biomass generated by primary industry were used as the raw material for the synthesis of calcium phosphate crystals. Phosphoric acid was extracted from burned rice chaff using a 30% nitric acid solution, while scallop shells and gypsum of plasterboard were used as calcium sources. The calcium phosphate crystals were synthesized by a method involving homogeneous precipitation, and the relationship between the composition and shape of the crystals and the pH at the time of the precipitation was investigated. Monetite crystals in a petal form with a diameter ranging from 0.1 to 2 μm were precipitated at pH 2.0, while granular apatite crystals with a mean diameter of 1 μm were precipitated at pH 6.0. We also investigated the ability of the synthesized calcium phosphate crystals to immobilize lactic acid bacteria for practical use in industrial bioreactor. It was determined that monetite crystals with a diameter of 2 μm had the highest ability to fix lactic acid bacteria. The population of lactic acid bacteria was estimated to exceed 1,300 bacteria per crystal surface of 50 μm 2 suggesting that these crystals may be of practical use in industrial fermenters.

  20. Complexation/encapsulation of green tea polyphenols in mixed calcium carbonate and phosphate micro-particles.

    Science.gov (United States)

    Elabbadi, Amal; Jeckelmann, Nicolas; Haefliger, Olivier P; Ouali, Lahoussine

    2011-01-01

    We used a double-jet mixer to encapsulate water-soluble polyphenols, green tea extract (GTE), with calcium-based inorganic materials. The device mixed calcium chloride solutions with a solution of carbonate and phosphate in the presence of a GTE solution, and formed micro-particles which capture the GTE molecules. The micro-particles were analysed by liquid chromatography coupled to tandem mass spectroscopy to determine the encapsulation yield and loading of the different GTE components. We established correlations between (1) the efficiency of the GTE encapsulation and the composition of the mixed anion solutions and (2) the protonation degree of the ions and the molar ratio of calcium cations and carbonate/phosphate anions. An optimal and reproducible GTE loading of about 40% with an encapsulation yield of 65% was observed for a carbonate/phosphate molar composition of 4 : 1. In addition, our experimental results showed that the process is selective and favours the encapsulation of gallated species which form stronger complexes with calcium cations.

  1. Investigation into the role of NaOH and calcium ions in the synthesis of calcium phosphate nanoshells

    Directory of Open Access Journals (Sweden)

    C. H. Yeo

    2012-03-01

    Full Text Available Calcium phosphate (CaP nanoshells were prepared using negatively charged liposomes (1,2-dioleoyl-sn-glycero-3-phosphate sodium salt (DOPA as a template by base titration synthesis at various concentrations of NaOH and calcium ions. The elemental composition, morphology, particle size, particle size distribution and zeta potential of the products were determined via various characterisation techniques, such as energy-dispersive X-ray spectrometry (EDX, transmission electron microscopy (TEM, dynamic light scattering (DLS, laser Doppler velocimetry (LDV and Fourier transform infrared spectroscopy (FTIR. The best results showed that stable spherical CaP nanoshells with a mean particle size of 197.5 ± 5.8 nm and a zeta potential of -34.5 ± 0.6 mV were successfully formed when 0.100 M sodium hydroxide (NaOH and 0.100 M calcium ions were used. Moreover, an optimal pH of 10.52 and a final Ca/P molar ratio of 0.97 were achieved under these conditions.

  2. Treatment of cows with parturient paresis using intravenous calcium and oral sodium phosphate.

    Science.gov (United States)

    Braun, U; Grob, D; Hässig, M

    2016-09-01

    The goal of this study was to investigate whether intravenous infusion of 1000 ml 40% calcium borogluconate combined with the oral adminstration of 500 g sodium phosphate leads to a better cure rate and longer-lasting normocalcaemia and normophosphataemia than standard intravenous treatment with 500 ml calcium borogluconate in cows with parturient paresis. Forty recumbent cows with hypocalcaemia and hypophosphataemia were alternately allocated to group A or B. Cows of both groups were treated intravenously with 500 ml 40% calcium borogluconate, and cows of group B additionally received another 500 ml calcium borogluconate via slow intravenous infusion and 500 g sodium phosphate administered via an orogastric tube. Thirty-two cows stood within 8 hours after the start of treatment and 8 did not; of the 32 cows that stood, 18 belonged to group A and 14 to group B (90% of group A vs. 70% of group B; P = 0.23). Seven cows relapsed; of these and the 8 that did not respond to initial treatment, 10 stood after two standard intravenous treatments. Downer cow syndrome occurred in 5 cows, 3 of which recovered after aggressive therapy. The overall cure rate did not differ significantly between groups A and B. Twelve (60%) cows of group A and 14 (70%) cows of group B were cured after a single treatment and of the remaining 14, 11 were cured after two or more treatments. Two downer cows were euthanized and one other died of heart failure during treatment. Serum calcium concentrations during the first eight hours after the start of treatment were significantly higher in group B than in group A, and oral sodium phosphate caused a significant and lasting increase in inorganic phosphate. More cows of group B than group A were cured after a single treatment (P > 0.05). These findings, although not statistically significant, are promising and should be verified using a larger number of cows.

  3. Modulating calcium phosphate formation using CO2 laser engineering of a polymeric material

    International Nuclear Information System (INIS)

    Waugh, D.G.; Lawrence, J.

    2012-01-01

    The use of simulated body fluid (SBF) is widely used as a screening technique to assess the ability of materials to promote calcium phosphate formation. This paper details the use of CO 2 laser surface treatment of nylon® 6,6 to modulate calcium phosphate formation following immersion in SBF for 14 days. Through white light interferometry (WLI) it was determined that the laser surface processing gave rise to maximum Ra and Sa parameters of 1.3 and 4.4 μm, respectively. The use of X-ray photoelectron spectroscopy (XPS) enabled a maximum increase in surface oxygen content of 5.6%at. to be identified. The laser-induced surface modifications gave rise to a modulation in the wettability characteristics such that the contact angle, θ, decreased for the whole area processed samples, as expected, and increased for the patterned samples. The increase in θ can be attributed to a transition in wetting nature to a mixed-state wetting regime. It was seen for all samples that calcium phosphate formed on each surface following 14 days. The largest increase in mass, Δg, owed to calcium phosphate formation, was brought about by the whole area processed sample irradiated with a fluence of 51 J cm −2 . No correlation between the calcium phosphate formation and the laser patterned surface properties was determined due to the likely affect of the mixed-state wetting regime. Strong correlations between θ, the surface energy parameters and the calcium phosphate formation for the whole area processed samples allow one to realize the potential for this surface treatment technique in predicting the bone forming ability of laser processed materials. - Highlights: ► Surface modifications brought about a modulation in the wetting of nylon 6,6. ► An increase in θ can be attributed to a mixed-state wetting regime. ► Laser surface treatment modulated the ability to promote apatite formation. ► Mixed-state wetting regime affected the promotion of uniform apatite formation.

  4. Modulating calcium phosphate formation using CO{sub 2} laser engineering of a polymeric material

    Energy Technology Data Exchange (ETDEWEB)

    Waugh, D.G., E-mail: Dwaugh@lincoln.ac.uk; Lawrence, J.

    2012-02-01

    The use of simulated body fluid (SBF) is widely used as a screening technique to assess the ability of materials to promote calcium phosphate formation. This paper details the use of CO{sub 2} laser surface treatment of nylon Registered-Sign 6,6 to modulate calcium phosphate formation following immersion in SBF for 14 days. Through white light interferometry (WLI) it was determined that the laser surface processing gave rise to maximum Ra and Sa parameters of 1.3 and 4.4 {mu}m, respectively. The use of X-ray photoelectron spectroscopy (XPS) enabled a maximum increase in surface oxygen content of 5.6%at. to be identified. The laser-induced surface modifications gave rise to a modulation in the wettability characteristics such that the contact angle, {theta}, decreased for the whole area processed samples, as expected, and increased for the patterned samples. The increase in {theta} can be attributed to a transition in wetting nature to a mixed-state wetting regime. It was seen for all samples that calcium phosphate formed on each surface following 14 days. The largest increase in mass, {Delta}g, owed to calcium phosphate formation, was brought about by the whole area processed sample irradiated with a fluence of 51 J cm{sup -2}. No correlation between the calcium phosphate formation and the laser patterned surface properties was determined due to the likely affect of the mixed-state wetting regime. Strong correlations between {theta}, the surface energy parameters and the calcium phosphate formation for the whole area processed samples allow one to realize the potential for this surface treatment technique in predicting the bone forming ability of laser processed materials. - Highlights: Black-Right-Pointing-Pointer Surface modifications brought about a modulation in the wetting of nylon 6,6. Black-Right-Pointing-Pointer An increase in {theta} can be attributed to a mixed-state wetting regime. Black-Right-Pointing-Pointer Laser surface treatment modulated the

  5. [Optimization of riboflavin sodium phosphate loading to calcium alginate floating microspheres by response surface methodology].

    Science.gov (United States)

    Zhang, An-yang; Fan, Tian-yuan

    2009-12-18

    To investigate the preparation, optimization and in vitro properties of riboflavin sodium phosphate floating microspheres. The floating microspheres composed of riboflavin sodium phosphate and calcium alginate were prepared using ion gelatin-oven drying method. The properties of the microspheres were investigated, including the buoyancy, release, appearance and entrapment efficiency. The formulation was optimized by response surface methodology (RSM). The optimized microspheres were round. The entrapment efficiency was 57.49%. All the microspheres could float on the artificial gastric juice over 8 hours. The release of the drug from the microspheres complied with Fick's diffusion.

  6. Thermal decomposition of calcium aluminium phosphate of Thies. [Vaporization of uranium and phosphorus pentoxide

    Energy Technology Data Exchange (ETDEWEB)

    Allaf, K; Rouanet, A

    1984-01-01

    This study is related to the work on beneficiation of raw phosphates by thermal processing (selective vaporization). More precisely it deals with the ability of a calcium-aluminium phosphate (ores from Thies) to vaporize selectively as phosphorus pentoxide and uranium contents. Experiments are performed on liquid samples at Tsub(f)

  7. Identification and quantitive analysis of calcium phosphate microparticles in intestinal tissue by nuclear microscopy

    International Nuclear Information System (INIS)

    Gomez-Morilla, Inmaculada; Thoree, Vinay; Powell, Jonathan J.; Kirkby, Karen J.; Grime, Geoffrey W.

    2006-01-01

    Microscopic particles (0.5-2 μm diameter), rich in calcium and phosphorus, are found in the lumen of the mid-distal gut of all mammals investigated, including humans, and these may play a role in immuno-surveillance and immune regulation of antigens from food and symbiotic bacteria that are contained in the gut. Whether these particles can cross in to tissue of the intestinal mucosa is unclear. If so, characterising their morphology and chemical composition is an important task in elucidating their function. The analysis of calcium phosphate in biological tissues has been approached in several ways including optical microscopy, scanning electron microscopy and, most recently in this work, with nuclear microscopy. In this paper, we describe the use of microPIXE and microRBS to locate these particles and to determine, accurately, the ratio of phosphorus to calcium using the information on sample thickness obtained from RBS to allow the PIXE ratios to be corrected. A commercial sample of hydroxy apatite was used to demonstrate accuracy and precision of the technique. Then, in a pilot study on intestinal tissue of mice, we demonstrated the presence of calcium phosphate microparticles, consistent with confocal microscopy observations, and we identified the average molar P:Ca molar ratio as 1.0. Further work will confirm the exact chemical speciation of these particles and will examine the influence of differing calcium containing diets on the formation of these microparticles

  8. Identification and quantitive analysis of calcium phosphate microparticles in intestinal tissue by nuclear microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Gomez-Morilla, Inmaculada [Advanced Technology Institute, University of Surrey, Guildford GU2 7XH (United Kingdom)]. E-mail: i.gomez-morilla@surrey.ac.uk; Thoree, Vinay [Gastrointestinal Laboratory, Rayne Institute, St. Thomas' Hospital, London SE1 7EH (United Kingdom); Powell, Jonathan J. [MRC Human Nutrition Research, Elsie Widdowson Laboratory, Fulbourn Road, Cambridge CB1 9NL (United Kingdom); Kirkby, Karen J. [Advanced Technology Institute, University of Surrey, Guildford GU2 7XH (United Kingdom); Grime, Geoffrey W. [Department of Physics, University of Surrey, GU2 7XH (United Kingdom)

    2006-08-15

    Microscopic particles (0.5-2 {mu}m diameter), rich in calcium and phosphorus, are found in the lumen of the mid-distal gut of all mammals investigated, including humans, and these may play a role in immuno-surveillance and immune regulation of antigens from food and symbiotic bacteria that are contained in the gut. Whether these particles can cross in to tissue of the intestinal mucosa is unclear. If so, characterising their morphology and chemical composition is an important task in elucidating their function. The analysis of calcium phosphate in biological tissues has been approached in several ways including optical microscopy, scanning electron microscopy and, most recently in this work, with nuclear microscopy. In this paper, we describe the use of microPIXE and microRBS to locate these particles and to determine, accurately, the ratio of phosphorus to calcium using the information on sample thickness obtained from RBS to allow the PIXE ratios to be corrected. A commercial sample of hydroxy apatite was used to demonstrate accuracy and precision of the technique. Then, in a pilot study on intestinal tissue of mice, we demonstrated the presence of calcium phosphate microparticles, consistent with confocal microscopy observations, and we identified the average molar P:Ca molar ratio as 1.0. Further work will confirm the exact chemical speciation of these particles and will examine the influence of differing calcium containing diets on the formation of these microparticles.

  9. Calcific tendinitis of the shoulder in basic calcium phosphate crystal deposition disease

    International Nuclear Information System (INIS)

    Scutellari, P.N.; Mazzilli, M.P.; Orzincolo, C.

    1986-01-01

    Basic calcium phosphate (BCP) crystal deposition can lead to periarticular collections associated with typical radiographic findings, most frequently observed in the shoulder. Moreover, these deposits may be revealed in other articular sites (i.e.,wrist, hand, foot, elbow, hip, etc.). Initially, the calcium deposits may appear poorly defined (cloudlike); sequently, they may reveal different patterns (linear, triangular or circular areas), changing in size, configuration and site. Adjacent bone may be normal, altough osteoporosis, cystic lesions and reactive sclerosis are reported. The radiographic appearance of calcifications will depend upon the exact location of the deposits in the specific tendon of the rotator cuff, the adjacent bursae and the soft tissues

  10. Preparation and Properties of Nanoparticles of Calcium Phosphates With Various Ca/P Ratios.

    Science.gov (United States)

    Sun, Limin; Chow, Laurence C; Frukhtbeyn, Stanislav A; Bonevich, John E

    2010-01-01

    This study aimed at preparing and studying the properties of nanoparticles of calcium phosphate (nCaP) with Ca/P ratios ranging from 1.0 to 1.67 using a spray-drying technique. Micro-structural analyses suggested that the nCaPs with Ca/P ratios of 1.67 to 1.33 were nano-sized amorphous calcium phosphate (ACP) containing varying amounts of acid phosphate and carbonate. The nCaP with Ca/P ratio of 1 contained only nano-sized low crystalline dicalcium phosphate (DCP). BET measurements of the nCaPs showed specific surface areas of (12 ± 2 to 50 ± 1) m(2)/g, corresponding to estimated equivalent spherical diameters of (38 to 172) nm. However, dynamic light scattering measurements revealed much larger particles of (380 ± 49 to 768 ± 111) nm, owing to agglomeration of the smaller primary nano particles as revealed by Scanning Electron Microscopy (SEM). Thermodynamic solubility measurements showed that the nCaPs with Ca/P ratio of 1.33 - 1.67 all have similar solubility behavior. The materials were more soluble than the crystalline hydroxyapatite (HA) at pH greater than about 4.7, and more soluble than β-tricalcium phosphate (β-TCP), octacalcium phosphate (OCP) and DCP at pH above 5.5. Their solubility approached that of α-tricalcium phosphate (α-TCP) at about pH 7. These nCaPs, which cannot be readily prepared by other currently available methods for nanoparticle preparation, have potential biomedical applications.

  11. Manufacturing of calcium phosphate scaffolds by pseudomorphic transformation of gypsum

    Energy Technology Data Exchange (ETDEWEB)

    Araujo Batista, H. de.; Batista Cardoso, M.; Sales Vasconcelos, A.; Vinicius Lia Fook, M.; Rodriguez Barbero, M. A.; Garcia Carrodeguas, R.

    2016-08-01

    Carbonated hydroxyapatite (CHAp) and β-tricalcium phosphate (β-TCP) have been employed for decades as constituents of scaffolds for bone regeneration because they chemically resemble bone mineral. In this study, the feasibility to manufacture CHAp/β-TCP scaffolds by pseudomorphic transformation of casted blocks of gypsum was investigated. The transformation was carried out by immersing the precursor gypsum block in 1 M (NH{sub 4}){sub 2}HPO{sub 4}/1.33 M NH{sub 4}OH solution with liquid/solid ratio of 10 mL/g and autoclaving at 120 degree centigrade and 203 kPa (2 atm) for 3 h at least. Neither shape nor dimensions significantly changed during transformation. The composition of scaffolds treated for 3 h was 70 wt.% CHAp and 30 wt.% β-TCP, and their compressive and diametral compressive strengths were 6.5 ± 0.7 and 5.3 ±0.7 MPa, respectively. By increasing the time of treatment to 6 h, the composition of the scaffold enriched in β-TCP (60 wt.% CHAp and 40 wt.% β-TCP) but its compressive and diametral compressive strengths were not significantly affected (6.7 ± 0.9 and 5.4 ± 0.6 MPa, respectively). On the basis of the results obtained, it was concluded that this route is a good approach to the manufacturing of biphasic (CHAp/β-TCP) scaffolds from previously shaped pieces of gypsum. (Author)

  12. Multiple prismatic calcium phosphate layers in the jaws of present-day sharks (Chondrichthyes; Selachii).

    Science.gov (United States)

    Dingerkus, G; Séret, B; Guilbert, E

    1991-01-15

    Jaws of large individuals, over 2 m in total length, of the shark species Carcharodon carcharias (great white shark) and Isurus oxyrinchus (mako shark) of the family Lamnidae, and Galeocerdo cuvieri (tiger shark) and Carcharhinus leucas (bull shark) of the family Carcharhinidae were found to have multiple, up to five, layers of prismatic calcium phosphate surrounding the cartilages. Smaller individuals of these species and other known species of living chondrichthyans have only one layer of prismatic calcium phosphate surrounding the cartilages, as also do most species of fossil chondrichthyans. Two exceptions are the fossil shark genera Xenacanthus and Tamiobatis. Where it is found in living forms, this multiple layered calcification does not appear to be phylogenetic, as it appears to be lacking in other lamnid and carcharhinid genera and species. Rather it appears to be functional, only appearing in larger individuals and species of these two groups, and hence may be necessary to strengthen the jaw cartilages of such individuals for biting.

  13. Investigation on the biomimetic influence of biopolymers on calcium phosphate precipitation-Part 1: Alginate

    International Nuclear Information System (INIS)

    Oliveira de Lima, Daniel; Gomes Aimoli, Cassiano; Beppu, Marisa Masumi

    2009-01-01

    The understanding of how macromocules act in precipitation of inorganic phases is the key knowledge that is needed to establish the foundation to mimic nature and produce materials with high mechanical modulus besides outstanding optical and thermal properties. This study investigated how addition of small amounts of alginate (7-70 ppm), that presents many carboxylic groups, affects phase distribution and morphology of calcium phosphates, obtained through precipitation and further submitted to calcination and sintering. The results lead to the conclusion that alginate action is dynamic, where alginate molecules act as templates to nucleation, and most of the biopolymer remains in solution even when all calcium phosphate has precipitated. However, despite the effect on phase composition being mainly related to the system's kinetics, alginate does present thermodynamic interaction with the precipitates. It is probable that it acts by reducing the free energy of nucleation, as in heterogeneous nucleation processes.

  14. Corrosion resistance of biomimetic calcium phosphate coatings on magnesium due to varying pretreatment time

    Energy Technology Data Exchange (ETDEWEB)

    Waterman, J., E-mail: jay.waterman@pg.canterbury.ac.nz [Department of Mechanical Engineering, University of Canterbury, Christchurch (New Zealand); Pietak, A. [Department of Anatomy and Structural Biology, University of Otago, Dunedin (New Zealand); Birbilis, N. [Department of Materials Engineering, Monash University (Australia); Woodfield, T. [Department of Mechanical Engineering, University of Canterbury, Christchurch (New Zealand); Department of Orthopaedic Surgery, University of Otago, Christchurch (New Zealand); Dias, G. [Department of Anatomy and Structural Biology, University of Otago, Dunedin (New Zealand); Staiger, M.P., E-mail: mark.staiger@canterbury.ac.nz [Department of Mechanical Engineering, University of Canterbury, Christchurch (New Zealand)

    2011-12-15

    Calcium phosphate coatings were prepared on magnesium substrates via a biomimetic coating process. The effects of a magnesium hydroxide pretreatment on the formation and the ultimate corrosion protection of the coatings were studied. The pretreatment layer was found to affect the amount of defects present in the coatings. Corrosion resistance of the coatings was studied in vitro using two simulated body fluids, 0.8% NaCl and Hanks solution. In NaCl, the resistance to corrosion of all samples decreases with time as corrosion proceeded through cracks and other defects in the coatings. Samples with no pretreatment displayed the highest corrosion resistance as these samples had the fewest defects in the coating. However, in Hanks solution, corrosion resistance increased with time due to additional nucleation of calcium phosphate from the fluid on to the substrate. In this solution, additional pretreatment time was beneficial to the overall corrosion resistance.

  15. Calcium phosphate nanoparticles as versatile carrier for small and large molecules across cell membranes

    Energy Technology Data Exchange (ETDEWEB)

    Sokolova, Viktoriya; Rotan, Olga; Klesing, Jan [University of Duisburg-Essen, Inorganic Chemistry and Center for Nanointegration Duisburg-Essen (CeNIDE) (Germany); Nalbant, Perihan [University of Duisburg-Essen, Faculty of Biology, Institute of Molecular Cell Biology (Germany); Buer, Jan; Knuschke, Torben; Westendorf, Astrid M. [University Hospital Essen, University of Duisburg-Essen, Institute of Medical Microbiology (Germany); Epple, Matthias, E-mail: matthias.epple@uni-due.de [University of Duisburg-Essen, Inorganic Chemistry and Center for Nanointegration Duisburg-Essen (CeNIDE) (Germany)

    2012-06-15

    The successful transport of molecules across the cell membrane is a key point in biology and medicine. In most cases, molecules alone cannot penetrate the cell membrane, therefore an efficient carrier is needed. Calcium phosphate nanoparticles (diameter: 100-250 nm, depending on the functionalization) were loaded with fluorescent oligonucleotides, peptide, proteins, antibodies, polymers or porphyrins and characterized by dynamic light scattering, nanoparticle tracking analysis and scanning electron microscopy. Any excess of molecules was removed by ultracentrifugation, and the dissolved molecules at the same concentration were used as control. The uptake of such fluorescence-labeled nanoparticles into HeLa cells was monitored by fluorescence microscopy and confocal laser scanning microscopy. Calcium phosphate nanoparticles were able to transport all molecules across the cell membrane, whereas the dissolved molecules alone were taken up only to a very small extent or even not at all.

  16. Calcium phosphate nanoparticles as versatile carrier for small and large molecules across cell membranes

    Science.gov (United States)

    Sokolova, Viktoriya; Rotan, Olga; Klesing, Jan; Nalbant, Perihan; Buer, Jan; Knuschke, Torben; Westendorf, Astrid M.; Epple, Matthias

    2012-06-01

    The successful transport of molecules across the cell membrane is a key point in biology and medicine. In most cases, molecules alone cannot penetrate the cell membrane, therefore an efficient carrier is needed. Calcium phosphate nanoparticles (diameter: 100-250 nm, depending on the functionalization) were loaded with fluorescent oligonucleotides, peptide, proteins, antibodies, polymers or porphyrins and characterized by dynamic light scattering, nanoparticle tracking analysis and scanning electron microscopy. Any excess of molecules was removed by ultracentrifugation, and the dissolved molecules at the same concentration were used as control. The uptake of such fluorescence-labeled nanoparticles into HeLa cells was monitored by fluorescence microscopy and confocal laser scanning microscopy. Calcium phosphate nanoparticles were able to transport all molecules across the cell membrane, whereas the dissolved molecules alone were taken up only to a very small extent or even not at all.

  17. Calcium phosphate nanoparticles as versatile carrier for small and large molecules across cell membranes

    International Nuclear Information System (INIS)

    Sokolova, Viktoriya; Rotan, Olga; Klesing, Jan; Nalbant, Perihan; Buer, Jan; Knuschke, Torben; Westendorf, Astrid M.; Epple, Matthias

    2012-01-01

    The successful transport of molecules across the cell membrane is a key point in biology and medicine. In most cases, molecules alone cannot penetrate the cell membrane, therefore an efficient carrier is needed. Calcium phosphate nanoparticles (diameter: 100–250 nm, depending on the functionalization) were loaded with fluorescent oligonucleotides, peptide, proteins, antibodies, polymers or porphyrins and characterized by dynamic light scattering, nanoparticle tracking analysis and scanning electron microscopy. Any excess of molecules was removed by ultracentrifugation, and the dissolved molecules at the same concentration were used as control. The uptake of such fluorescence-labeled nanoparticles into HeLa cells was monitored by fluorescence microscopy and confocal laser scanning microscopy. Calcium phosphate nanoparticles were able to transport all molecules across the cell membrane, whereas the dissolved molecules alone were taken up only to a very small extent or even not at all.

  18. Ph-activated nano-amorphous calcium phosphate-based cement to reduce dental enamel demineralization.

    Science.gov (United States)

    Melo, Mary A S; Weir, Michael D; Passos, Vanara F; Powers, Michael; Xu, Hockin H K

    2017-12-01

    Enamel demineralization is destructive, esthetically compromised, and costly complications for orthodontic patients. Nano-sized amorphous calcium phosphate (NACP) has been explored to address this challenge. The 20% NACP-loaded ortho-cement notably exhibited favorable behavior on reducing demineralization of enamel around brackets in a caries model designed to simulate the carious attack. The 20% NACP-loaded ortho-cement markedly promotes higher calcium and phosphate release at a low pH, and the mineral loss was almost two fold lower and carious lesion depth decreased the by 1/3. This novel approach is promising co-adjuvant route for prevention of dental caries dissemination in millions of patients under orthodontic treatment.

  19. Performance of phosphogypsum and calcium magnesium phosphate fertilizer for nitrogen conservation in pig manure composting.

    Science.gov (United States)

    Li, Yun; Luo, Wenhai; Li, Guoxue; Wang, Kun; Gong, Xiaoyan

    2018-02-01

    This study investigated the performance of phosphogypsum and calcium magnesium phosphate fertilizer for nitrogen conservation during pig manure composting with cornstalk as the bulking agent. Results show that phosphogypsum increased nitrous oxide (N 2 O) emission, but significantly reduced ammonia (NH 3 ) emission and thus enhanced the mineral and total nitrogen (TN) contents in compost. Although N 2 O emission could be reduced by adding calcium magnesium phosphate fertilizer, NH 3 emission was considerably increased, resulting in an increase in TN loss during composting. By blending these two additives, both NH 3 and N 2 O emissions could be mitigated, achieving effective nitrogen conservation in composting. More importantly, with the addition of 20% TN of the mixed composting materials, these two additives could synergistically improve the compost maturity and quality. Copyright © 2017 Elsevier Ltd. All rights reserved.

  20. Incorporation of casein phosphopeptide-amorphous calcium phosphate into a glass-ionomer cement.

    Science.gov (United States)

    Mazzaoui, S A; Burrow, M F; Tyas, M J; Dashper, S G; Eakins, D; Reynolds, E C

    2003-11-01

    Casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) nanocomplexes have been shown to prevent demineralization and promote remineralization of enamel subsurface lesions in animal and in situ caries models. The aim of this study was to determine the effect of incorporating CPP-ACP into a self-cured glass-ionomer cement (GIC). Incorporation of 1.56% w/w CPP-ACP into the GIC significantly increased microtensile bond strength (33%) and compressive strength (23%) and significantly enhanced the release of calcium, phosphate, and fluoride ions at neutral and acidic pH. MALDI mass spectrometry also showed casein phosphopeptides from the CPP-ACP nanocomplexes to be released. The release of CPP-ACP and fluoride from the CPP-ACP-containing GIC was associated with enhanced protection of the adjacent dentin during acid challenge in vitro.

  1. Studies on the mechanisms underlying the transfer of calcium and phosphate from bone to blood

    Energy Technology Data Exchange (ETDEWEB)

    Brommage, Jr., Robert J. [Univ. of Rochester, NY (United States)

    1978-01-01

    The skeleton is recognized as a crucial organ in the minute-to-minute regulation of the blood levels of calcium and phosphate. The fluxes of calcium and phosphate to and from bone greatly exceed the entry and exit of these ions occurring in the intestine and kidneys. Parathyroid hormone, calcitonin, and 1,25-dihydroxyvitamin D3 (1,25-(OH)2D3 are known to influence the transfer of calcium and phosphate from bone to blood. Three mechanisms have been proposed to explain the hormonal control of the calcium and phosphate effluxes from bone. The concept of a bone membrane maintaining a distinct bone extracellular fluid composition has led to the pump and pH gradient theories. An alternate solubilizer theory proposes that bone cells secrete a substance which increases the solubility of the bone mineral. The bone membrane concept was originally proposed to explain the presence of the apparent anomalously high concentrations of potassium in the bone extracellular fluid. However, the available evidence does not allow an unambiguous decision concerning the presence of a bone membrane. Calvarial lactate production was unaltered by 1,25-(OH)2D3 treatment and consequently 1,25-(OH)2D3 does not appear to promote the mobilization of bone mineral through a lactate-mediated pH gradient mechanism. 1,25-(OH)2D3 did increase the solubility of non-vital bone, clearly demonstrating that the solubilizer mechanism is at least partially responsible for the mobilization of bone mineral and the regulation of blood levels of calcium and phosphate. Vitamin D-deficient female rats fed a 0.2% calcium, 0.4% phosphorous diet and supplemented with daily injections of 0.75 pmole of 1,25-(OH)2D3 were shown to be capable of bearing young. When the injections of 1,25-(OH)2D3 were terminated at delivery, the dams and pups showed signs of vitamin D deficiency

  2. Effect of different calcium phosphate scaffold ratios on odontogenic differentiation of human dental pulp cells

    Energy Technology Data Exchange (ETDEWEB)

    AbdulQader, Sarah Talib [School of Dental Sciences, Universiti Sains Malaysia, 16150 Kubang Kerian, Kelantan (Malaysia); Department of Pedodontic and Preventive Dentistry, College of Dentistry, University of Baghdad, Baghdad (Iraq); Kannan, Thirumulu Ponnuraj, E-mail: kannan@usm.my [School of Dental Sciences, Universiti Sains Malaysia, 16150 Kubang Kerian, Kelantan (Malaysia); Human Genome Centre, School of Medical Sciences, Universiti Sains Malaysia, 16150 Kubang Kerian, Kelantan (Malaysia); Rahman, Ismail Ab [School of Dental Sciences, Universiti Sains Malaysia, 16150 Kubang Kerian, Kelantan (Malaysia); Ismail, Hanafi [School of Materials and Minerals Resource Engineering, Universiti Sains Malaysia, 14300 Penang (Malaysia); Mahmood, Zuliani [School of Dental Sciences, Universiti Sains Malaysia, 16150 Kubang Kerian, Kelantan (Malaysia)

    2015-04-01

    Calcium phosphate (CaP) scaffolds have been widely and successfully used with osteoblast cells for bone tissue regeneration. However, it is necessary to investigate the effects of these scaffolds on odontoblast cells' proliferation and differentiation for dentin tissue regeneration. In this study, three different hydroxyapatite (HA) to beta tricalcium phosphate (β-TCP) ratios of biphasic calcium phosphate (BCP) scaffolds, BCP20, BCP50, and BCP80, with a mean pore size of 300 μm and 65% porosity were prepared from phosphoric acid (H{sub 2}PO{sub 4}) and calcium carbonate (CaCO{sub 3}) sintered at 1000 °C for 2 h. The extracts of these scaffolds were assessed with regard to cell viability and differentiation of odontoblasts. The high alkalinity, more calcium, and phosphate ions released that were exhibited by BCP20 decreased the viability of human dental pulp cells (HDPCs) as compared to BCP50 and BCP80. However, the cells cultured with BCP20 extract expressed high alkaline phosphatase activity and high expression level of bone sialoprotein (BSP), dental matrix protein-1 (DMP-1), and dentin sialophosphoprotein (DSPP) genes as compared to that cultured with BCP50 and BCP80 extracts. The results highlighted the effect of different scaffold ratios on the cell microenvironment and demonstrated that BCP20 scaffold can support HDPC differentiation for dentin tissue regeneration. - Highlights: • BCPs of different HA/β-TCP ratios influence cell microenvironment. • BCP20 decreases cell viability of HDPCs as compared to BCP50 and BCP80. • HDPCs cultured with BCP20 express highest ALP activity. • HDPCs cultured with BCP20 up-regulate BSP, DMP-1 and DSPP gene expressions. • BCP20 can support HDPC differentiation for dentin tissue regeneration.

  3. The effect of calcium phosphate nanoparticles on hormone production and apoptosis in human granulosa cells

    Directory of Open Access Journals (Sweden)

    Gao Li

    2010-04-01

    Full Text Available Abstract Objectives Although many nanomaterials are being used in academia, industry and daily life, there is little understanding about the effects of nanoparticles on the reproductive health of vertebral animals, including human beings. An experimental study was therefore performed here to explore the effect of calcium phosphate nanoparticles on both steroid hormone production and apoptosis in human ovarian granulosa cells. Methods Calcium phosphate nanoparticles uptaking was evaluated by transmission electron microscopy (TEM. The cell cycle was assessed with propidium iodide-stained cells (distribution of cells in G0/G1, S, and G2/M phases by flow cytometry. The pattern of cell death (necrosis and apoptosis was analyzed by flow cytometry with annexin V-FITC/PI staining. The expression of mRNAs encoding P450scc, P450arom and StAR were determined by RT-PCR. Progesterone and estradiol levels were measured by radioimmunoassay. Results TEM results confirmed that calcium phosphate nanoparticles could enter into granulosa cells, and distributed in the membranate compartments, including lysosome and mitochondria and intracellular vesicles. The increased percentage of cells in S phase when cultured with nanoparticles indicated that there was an arrest at the checkpoint from phase S-to-G2/M (from 6.28 +/- 1.55% to 11.18 +/- 1.73%, p Conclusion Calcium phosphate nanoparticles interfered with cell cycle of cultured human ovarian granulosa cells thus increasing cell apoptosis. This pilot study suggested that effects of nanoparticles on ovarian function should be extensively investigated.

  4. Nanostructured calcium phosphate coatings on magnesium alloys: characterization and cytocompatibility with mesenchymal stem cells

    OpenAIRE

    Iskandar, Maria Emil; Aslani, Arash; Tian, Qiaomu; Liu, Huinan

    2015-01-01

    This article reports the deposition and characterization of nanostructured calcium phosphate (nCaP) on magnesium–yttrium alloy substrates and their cytocompatibility with bone marrow derived mesenchymal stem cells (BMSCs). The nCaP coatings were deposited on magnesium and magnesium–yttrium alloy substrates using proprietary transonic particle acceleration process for the dual purposes of modulating substrate degradation and BMSC adhesion. Surface morphology and feature size were analyzed usin...

  5. Effect of different calcium phosphate scaffold ratios on odontogenic differentiation of human dental pulp cells

    International Nuclear Information System (INIS)

    AbdulQader, Sarah Talib; Kannan, Thirumulu Ponnuraj; Rahman, Ismail Ab; Ismail, Hanafi; Mahmood, Zuliani

    2015-01-01

    Calcium phosphate (CaP) scaffolds have been widely and successfully used with osteoblast cells for bone tissue regeneration. However, it is necessary to investigate the effects of these scaffolds on odontoblast cells' proliferation and differentiation for dentin tissue regeneration. In this study, three different hydroxyapatite (HA) to beta tricalcium phosphate (β-TCP) ratios of biphasic calcium phosphate (BCP) scaffolds, BCP20, BCP50, and BCP80, with a mean pore size of 300 μm and 65% porosity were prepared from phosphoric acid (H 2 PO 4 ) and calcium carbonate (CaCO 3 ) sintered at 1000 °C for 2 h. The extracts of these scaffolds were assessed with regard to cell viability and differentiation of odontoblasts. The high alkalinity, more calcium, and phosphate ions released that were exhibited by BCP20 decreased the viability of human dental pulp cells (HDPCs) as compared to BCP50 and BCP80. However, the cells cultured with BCP20 extract expressed high alkaline phosphatase activity and high expression level of bone sialoprotein (BSP), dental matrix protein-1 (DMP-1), and dentin sialophosphoprotein (DSPP) genes as compared to that cultured with BCP50 and BCP80 extracts. The results highlighted the effect of different scaffold ratios on the cell microenvironment and demonstrated that BCP20 scaffold can support HDPC differentiation for dentin tissue regeneration. - Highlights: • BCPs of different HA/β-TCP ratios influence cell microenvironment. • BCP20 decreases cell viability of HDPCs as compared to BCP50 and BCP80. • HDPCs cultured with BCP20 express highest ALP activity. • HDPCs cultured with BCP20 up-regulate BSP, DMP-1 and DSPP gene expressions. • BCP20 can support HDPC differentiation for dentin tissue regeneration

  6. Polymer-Ceramic Composite Scaffolds: The Effect of Hydroxyapatite and β-tri-Calcium Phosphate

    OpenAIRE

    Boyang Huang; Guilherme Caetano; Cian Vyas; Jonny James Blaker; Carl Diver; Paulo Bártolo

    2018-01-01

    The design of bioactive scaffolds with improved mechanical and biological properties is an important topic of research. This paper investigates the use of polymer-ceramic composite scaffolds for bone tissue engineering. Different ceramic materials (hydroxyapatite (HA) and β-tri-calcium phosphate (TCP)) were mixed with poly-ε-caprolactone (PCL). Scaffolds with different material compositions were produced using an extrusion-based additive manufacturing system. The produced scaffolds were physi...

  7. Physicochemical Approach to Alkaline Flocculation of Chlorella vulgaris Induced by Calcium Phosphate Precipitates.

    Czech Academy of Sciences Publication Activity Database

    Brányiková, Irena; Filipenská, Monika; Urbanová, K.; Růžička, Marek; Pivokonský, Martin; Brányik, T.

    2018-01-01

    Roč. 166, 1 June (2018), s. 54-60 ISSN 0927-7765 R&D Projects: GA ČR(CZ) GA18-05007S Institutional support: RVO:67985858 ; RVO:67985874 Keywords : microalgae * calcium phosphate * precipitates * surface interactions Subject RIV: CI - Industrial Chemistry, Chemical Engineering; BK - Fluid Dynamics (UH-J) OBOR OECD: Chemical process engineering; Environmental sciences (social aspects to be 5.7) (UH-J) Impact factor: 3.887, year: 2016

  8. UV and X radiation effects on the stability of calcium halide phosphate phosphors. 2

    International Nuclear Information System (INIS)

    Tews, W.; Getter, R.; Kleemann, M.

    1983-01-01

    Sb(V) and Sb(III) concentrations in calcium halide phosphate phosphors have been investigated as a function of time of irradiation with near UV and X radiation. It was found that the reduction of both Sb(V) and Sb(III) to elemental Sb results in intensity losses. The reductions follow consecutive first-order kinetics and first-order kinetics, respectively

  9. Synthesis and Characterization of Calcium Phosphate Powders for Biomedical Applications by Plasma Spray Coating

    OpenAIRE

    Sasidharan Pillai, Rahul

    2015-01-01

    This PhD work mainly focus on the synthesis and characterization of calcium phosphate powders for plasma spray coating. The preparation of high temperature phase stabilized βTCP and HA/βTCP powders for plasma spray coating applications has been the topic of investigation. Nowadays plasma sprayed coatings are widely used for biomedical applications especially in the dental and orthopaedic implantation field. Previously Ti based alloys were widely used for the orthopaedic and dental implant ap...

  10. Calcium phosphate barrier for augmentation of bone in noncontained periodontal osseous defects: a novel approach.

    Science.gov (United States)

    Chopra, Aditi; Sivaraman, Karthik; Awataramaney, Tarun K

    2014-11-01

    The aim of this technique is to augment bone in non-contained osseous deformities using a unique self-sustaining calcium phosphate barrier. Bone has the inherent ability to regenerate completely if it is provided with a fracture space or an undisturbed enclosed scaffold. A secluded environment is essential as it provides a secured, sterile and stable wound system that regenerates lost bone by a process of osteopromotion. Reconstructive techniques using bone grafts and barrier membranes utilize this principle for augmentation of deficient bony sites by providing a closed environment that promotes clot stability, graft retention, and facilitates correct cell repopulation. However, in noncontained bone defects like one walled infrabony periodontal defect or sites with horizontal bone loss, regeneration of bone still remains an unrealistic situation since osseous topography at such sites does not favor membrane stability or bone grafts retention. This case report presents a promising technique to augment bone in areas with horizontal loss. Augmentation of bone in the interdental area with horizontal bone loss was accomplished by building a contained defect using a unique self sustaining calcium phosphate cement formulation. The calcium phosphate barrier stimulates the lost cortical plates and promotes graft retention and clot stability. At 6 months, there was a significant bone fill and trabecular formation in the interdental area and reduction in tooth mobility. This promising technique could prove to be a good alternative to the conventional approaches for treating osseous deformities. Calcium phosphate is a promising barrier graft for repair of noncontained periodontal osseous defect. This technique cues both the clinicians and manufacturers to develop moldable tissue engineered constructs for osseous repair.

  11. Calcium phosphate thin films enhance the response of human mesenchymal stem cells to nanostructured titanium surfaces

    Directory of Open Access Journals (Sweden)

    Mura M McCafferty

    2014-05-01

    Full Text Available The development of biomaterial surfaces possessing the topographical cues that can promote mesenchymal stem cell recruitment and, in particular, those capable of subsequently directing osteogenic differentiation is of increasing importance for the advancement of tissue engineering. While it is accepted that it is the interaction with specific nanoscale topography that induces mesenchymal stem cell differentiation, the potential for an attendant bioactive chemistry working in tandem with such nanoscale features to enhance this effect has not been considered to any great extent. This article presents a study of mesenchymal stem cell response to conformal bioactive calcium phosphate thin films sputter deposited onto a polycrystalline titanium nanostructured surface with proven capability to directly induce osteogenic differentiation in human bone marrow–derived mesenchymal stem cells. The sputter deposited surfaces supported high levels of human bone marrow–derived mesenchymal stem cell adherence and proliferation, as determined by DNA quantification. Furthermore, they were also found to be capable of directly promoting significant levels of osteogenic differentiation. Specifically, alkaline phosphatase activity, gene expression and immunocytochemical localisation of key osteogenic markers revealed that the nanostructured titanium surfaces and the bioactive calcium phosphate coatings could direct the differentiation towards an osteogenic lineage. Moreover, the addition of the calcium phosphate chemistry to the topographical profile of the titanium was found to induce increased human bone marrow–derived mesenchymal stem cell differentiation compared to that observed for either the titanium or calcium phosphate coating without an underlying nanostructure. Hence, the results presented here highlight that a clear benefit can be achieved from a surface engineering strategy that combines a defined surface topography with an attendant, conformal

  12. Hydroxyapatite and Other Calcium Phosphates for the Conservation of Cultural Heritage: A Review

    Science.gov (United States)

    2018-01-01

    The present paper reviews the methods and the performance of in situ formation of calcium phosphates (CaP) for the conservation of materials belonging to cultural heritage. The core idea is to form CaP (ideally hydroxyapatite, HAP, the most stable CaP at pH > 4) by reaction between the substrate and an aqueous solution of a phosphate salt. Initially proposed for the conservation of marble and limestone, the treatment has been explored for a variety of different substrates, including sandstones, sulphated stones, gypsum stuccoes, concrete, wall paintings, archaeological bones and paper. First, the studies aimed at identifying the best treatment conditions (e.g., nature and concentration of the phosphate precursor, solution pH, treatment duration, ionic and organic additions to the phosphate solution, mineralogical composition of the new CaP phases) are summarized. Then, the treatment performance on marble and limestone is reviewed, in terms of protective and consolidating effectiveness, compatibility (aesthetic, microstructural and physical) and durability. Some pilot applications in real case studies are also reported. Recent research aimed at extending the phosphate treatment to other substrates is then illustrated. Finally, the strengths of the phosphate treatment are summarized, in comparison with alternative products, and some aspects needing future research are outlined. PMID:29617322

  13. Hydroxyapatite and Other Calcium Phosphates for the Conservation of Cultural Heritage: A Review

    Directory of Open Access Journals (Sweden)

    Enrico Sassoni

    2018-04-01

    Full Text Available The present paper reviews the methods and the performance of in situ formation of calcium phosphates (CaP for the conservation of materials belonging to cultural heritage. The core idea is to form CaP (ideally hydroxyapatite, HAP, the most stable CaP at pH > 4 by reaction between the substrate and an aqueous solution of a phosphate salt. Initially proposed for the conservation of marble and limestone, the treatment has been explored for a variety of different substrates, including sandstones, sulphated stones, gypsum stuccoes, concrete, wall paintings, archaeological bones and paper. First, the studies aimed at identifying the best treatment conditions (e.g., nature and concentration of the phosphate precursor, solution pH, treatment duration, ionic and organic additions to the phosphate solution, mineralogical composition of the new CaP phases are summarized. Then, the treatment performance on marble and limestone is reviewed, in terms of protective and consolidating effectiveness, compatibility (aesthetic, microstructural and physical and durability. Some pilot applications in real case studies are also reported. Recent research aimed at extending the phosphate treatment to other substrates is then illustrated. Finally, the strengths of the phosphate treatment are summarized, in comparison with alternative products, and some aspects needing future research are outlined.

  14. Study of a hydraulic dicalcium phosphate dihydrate/calcium oxide-based cement for dental applications.

    Science.gov (United States)

    el-Briak, Hasna; Durand, Denis; Nurit, Josiane; Munier, Sylvie; Pauvert, Bernard; Boudeville, Phillipe

    2002-01-01

    By mixing CaHPO(4) x 2H(2)O (DCPD) and CaO with water or sodium phosphate buffers as liquid phase, a calcium phosphate cement was obtained. Its physical and mechanical properties, such as compressive strength, initial and final setting times, cohesion time, dough time, swelling time, dimensional and thermal behavior, and injectability were investigated by varying different parameters such as liquid to powder (L/P) ratio (0.35-0.7 ml g(-1)), molar calcium to phosphate (Ca/P) ratio (1.67-2.5) and the pH (4, 7, and 9) and the concentration (0-1 M) of the sodium phosphate buffer. The best results were obtained with the pH 7 sodium phosphate buffer at the concentration of 0.75 M. With this liquid phase, physical and mechanical properties depended on the Ca/P and L/P ratios, varying from 3 to 11 MPa (compressive strength), 6 to 10 min (initial setting time), 11 to 15 min (final setting time), 15 to 30 min (swelling time), 7 to 20 min (time of 100% injectability). The dough or working time was over 16 min. This cement expanded during its setting (1.2-5 % according to Ca/P and L/P ratios); this would allow a tight filling. Given the mechanical and rheological properties of this new DCPD/CaO-based cement, its use as root canal sealing material can be considered as classical calcium hydroxide or ZnO/eugenol-based pastes, without or with a gutta-percha point. Copyright 2002 Wiley Periodicals, Inc. J Biomed Mater Res (Appl Biomater) 63: 447-453, 2002

  15. Formation of calcium phosphates by vapour diffusion in highly concentrated ionic micro-droplets

    Energy Technology Data Exchange (ETDEWEB)

    Iafisco, M. [Alma Mater Studiorum Universita di Bologna, Dipartimento di Chimica ' ' G. Ciamician' ' , Via Selmi 2, 40126 Bologna (Italy); Universita del Piemonte Orientale, Dipartimento di Scienze Mediche, Via Solaroli 4, 28100 Novara (Italy); Delgado-Lopez, J.M.; Gomez-Morales, J.; Hernandez-Hernandez, M.A.; Rodriguez-Ruiz, I. [Laboratorio de Estudios Cristalograficos, IACT CSIC-UGR, Edificio Lopez Neyra, Avenida del Conocimiento, s/n 18100 Armilla (Spain); Roveri, N. [Alma Mater Studiorum Universita di Bologna, Dipartimento di Chimica ' ' G. Ciamician' ' , Via Selmi 2, 40126 Bologna (Italy)

    2011-08-15

    In this work we have used the sitting drop vapour diffusion technique, employing the ''crystallization mushroom '' to analyze the evolution of calcium phosphate crystallization in micro-droplets containing high initial concentrations of Ca{sup 2+} and HPO{sub 4}{sup 2-}. The decomposition of NH{sub 4}HCO{sub 3} solution produces vapours of NH{sub 3} and CO{sub 2} which diffuse through the droplets containing an aqueous solution of Ca(CH{sub 3}COO){sub 2} and (NH{sub 4}){sub 2}HPO{sub 4}. The result is the increase of pH by means of the diffusion of NH{sub 3} gas and the doping of the calcium phosphate with CO{sub 3}{sup 2-} ions by means of the diffusion of CO{sub 2} gas. The pH of the crystallization process is monitored and the precipitates at different times are characterized by XRD, FTIR, TGA, SEM and TEM techniques. The slow increase of pH and the high concentration of Ca{sup 2+} and HPO{sub 4}{sup 2-} in the droplets induce the crystallization of three calcium phosphate phases: dicalcium phosphate dihydrate (DCPD, brushite), octacalcium phosphate (OCP) and carbonate-hydroxyapatite (HA). The amount of HA nanocrystals with needle-like morphology and dimensions of about 100 nm, closely resembling the inorganic phase of bones, gradually increases, with the precipitation time up to 7 days, whereas the amount of DCPD, growing along the b axis, increases up to 3 days. Then, DCDP crystals start to hydrolyze yielding OCP nanoribbons and HA nanocrystals. (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  16. Preparation and Sustained-Release Property of Triblock Copolymer/Calcium Phosphate Nanocomposite as Nanocarrier for Hydrophobic Drug

    Directory of Open Access Journals (Sweden)

    Cao Shao-Wen

    2010-01-01

    Full Text Available Abstract The P123/ACP nanocomposite with sizes less than 100 nm consisting of triblock copolymer P123 and amorphous calcium phosphate (ACP has been prepared by using an aqueous solution containing CaCl2, (NH43PO4, and P123 at room temperature. The P123/ACP nanocomposite is used as the nanocarrier for hydrophobic drug ibuprofen, based on the combined advantages of both amphiphilic block copolymer and calcium phosphate delivery system. The P123/ACP nanocomposite has a much higher ibuprofen loading capacity (148 mg/g than the single-phase calcium phosphate nanostructures. The drug release percentage of the P123/ACP nanocomposite in simulated body fluid reaches about 100% in a period of 156 h, which is much slower than that of single-phase calcium phosphate nanostructures. It is expected that the P123/ACP nanocomposite is promising for the application in the controlled delivery of hydrophobic drugs.

  17. Cell response of calcium phosphate based ceramics, a bone substitute material

    Directory of Open Access Journals (Sweden)

    Juliana Marchi

    2013-01-01

    Full Text Available The aim of this study was to characterize calcium phosphate ceramics with different Ca/P ratios and evaluate cell response of these materials for use as a bone substitute. Bioceramics consisting of mixtures of hydroxyapatite (HAp and β-tricalcium phosphate (β-TCP powders in different proportions were pressed and sintered. The physical and chemical properties of these bioceramics were then characterized. Characterization of the biological properties of these materials was based on analysis of cell response using cultured fibroblasts. The number of cells attached to the samples was counted from SEM images of samples exposed to cell culture solution for different periods. These data were compared by analysis of variance (ANOVA complemented by the Tukey's test. The TCP sample had higher surface roughness and lower density. The adherence and growth of FMM1 cells on samples from all groups was studied. Even though the different calcium based ceramics exhibited properties which made them suitable as bone substitutes, those with higher levels of β-TCP revealed improved cell growth on their surfaces. These observations indicated two-phase calcium phosphate based materials with a β-TCP surface layer to be a promising bone substitute.

  18. Synthesis of Calcium Phosphate Composite Organogels by Using Emulsion Method for Dentine Occlusion Materials

    Science.gov (United States)

    Nopteeranupharp, C.; Akkarachaneeyakorn, K.; Songsasaen, A.

    2018-03-01

    Dentinal hypersensitivity (DH) is one of the most human’s problems caused by the erosion of enamel. There are many methods and materials to solve this problem. Calcium phosphate is an excellent alternative for curing this symptom because of its osteoconductivity, and biocompatibility properties. The low-cost and low-toxicity calcium phosphate nanogel was fabricated by using emulsion method and characterized by using TEM, EDX, and DLS techniques. The results showed that P123 (poly (ethylene oxide)19-block-Poly (propylene oxide)69-block-poly (ethylene oxide)19) has played a major role as template and gel formation, SDS was used as a surfactant to form water-in-oil emulsion nanodroplets with circle-like shape. Moreover, the ability of synthesised organogel to occlude the exposed dentine tubules was tested on the model of human’s dentine slices. The results showed that calcium phosphate composite organogel can be efficiently occluded on dentine slice, characterized by SEM technique, after 1 day.

  19. Cellular Performance Comparison of Biomimetic Calcium Phosphate Coating and Alkaline-Treated Titanium Surface

    Directory of Open Access Journals (Sweden)

    Xiaohua Yu

    2013-01-01

    Full Text Available The influence of biomimetic calcium phosphate coating on osteoblasts behavior in vitro is not well established yet. In this study, we investigated the behavior of osteoblastic rat osteosarcoma 17/2.8 cells (ROS17/2.8 on two groups of biomaterial surfaces: alkaline-treated titanium surface (ATT and biomimetic calcium phosphate coated ATT (CaP. The cell attachment, proliferation, differentiation, and morphology on these surfaces were extensively evaluated to reveal the impact of substrate surface on osteoblastic cell responses. It was found that the ROS17/2.8 cells cultured on the ATT surface had higher attachment and proliferation rates compared to those on the CaP surface. Our results also showed that the calcium phosphate coatings generated in this work have an inhibiting effect on osteoblast adhesion and further influenced the proliferation and differentiation of osteoblast compared to the ATT surface in vitro. Cells on the ATT surface also exhibited a higher alkaline phosphatase activity than on the CaP surface after two weeks of culture. Immunofluorescence staining and scanning electron microscopy results showed that the cells adhered and spread faster on the ATT surface than on the CaP surface. These results collectively suggested that substrate surface properties directly influence cell adhesion on different biomaterials, which would result in further influence on the cell proliferation and differentiation.

  20. Development of a Calcium Phosphate Nanocomposite for Fast Fluorogenic Detection of Bacteria

    Directory of Open Access Journals (Sweden)

    Claudio R. Martínez

    2014-09-01

    Full Text Available Current procedures for the detection and identification of bacterial infections are laborious, time-consuming, and require a high workload and well-equipped laboratories. Therefore the work presented herein developed a simple, fast, and low cost method for bacterial detection based on hydroxyapatite nanoparticles with a nutritive mixture and the fluorogenic substrate. Calcium phosphate ceramic nanoparticles were characterized and integrated with a nutritive mixture for the early detection of bacteria by visual as well as fluorescence spectroscopy techniques. The composite was obtained by combining calcium phosphate nanoparticles (Ca:P ratio, 1.33:1 with a nutritive mixture of protein hydrolysates and carbon sources, which promote fast bacterial multiplication, and the fluorogenic substrate 4-methylumbellipheryl-β-d-glucuronide (MUG. The composite had an average particle size of 173.2 nm and did not show antibacterial activity against Gram-negative or Gram-positive bacteria. After an Escherichia coli suspension was in contact with the composite for 60–90 min, fluorescence detected under UV light or by fluorescence spectrophotometer indicated the presence of bacteria. Intense fluorescence was observed after incubation for a maximum of 90 min. Thus, this calcium phosphate nanocomposite system may be useful as a model for the development of other nanoparticle composites for detection of early bacterial adhesion.

  1. Europium-doped amorphous calcium phosphate porous nanospheres: preparation and application as luminescent drug carriers

    Directory of Open Access Journals (Sweden)

    Zhang Kui-Hua

    2011-01-01

    Full Text Available Abstract Calcium phosphate is the most important inorganic constituent of biological tissues, and synthetic calcium phosphate has been widely used as biomaterials. In this study, a facile method has been developed for the fabrication of amorphous calcium phosphate (ACP/polylactide-block-monomethoxy(polyethyleneglycol hybrid nanoparticles and ACP porous nanospheres. Europium-doping is performed to enable photoluminescence (PL function of ACP porous nanospheres. A high specific surface area of the europium-doped ACP (Eu3+:ACP porous nanospheres is achieved (126.7 m2/g. PL properties of Eu3+:ACP porous nanospheres are investigated, and the most intense peak at 612 nm is observed at 5 mol% Eu3+ doping. In vitro cytotoxicity experiments indicate that the as-prepared Eu3+:ACP porous nanospheres are biocompatible. In vitro drug release experiments indicate that the ibuprofen-loaded Eu3+:ACP porous nanospheres show a slow and sustained drug release in simulated body fluid. We have found that the cumulative amount of released drug has a linear relationship with the natural logarithm of release time (ln(t. The Eu3+:ACP porous nanospheres are bioactive, and can transform to hydroxyapatite during drug release. The PL properties of drug-loaded nanocarriers before and after drug release are also investigated.

  2. Aptamer-Conjugated Calcium Phosphate Nanoparticles for Reducing Diabetes Risk via Retinol Binding Protein 4 Inhibition.

    Science.gov (United States)

    Torabi, Raheleh; Ghourchian, Hedayatollah; Amanlou, Massoud; Pasalar, Parvin

    2017-06-01

    Inhibition of the binding of retinol to its carrier, retinol binding protein 4, is a new strategy for treating type 2 diabetes; for this purpose, we have provided an aptamer-functionalized multishell calcium phosphate nanoparticle. First, calcium phosphate nanoparticles were synthesized and conjugated to the aptamer. The cytotoxicity of nanoparticles releases the process of aptamer from nanoparticles and their inhibition function of binding retinol to retinol binding protein 4. After synthesizing and characterizing the multishell calcium phosphate nanoparticles and observing the noncytotoxicity of conjugate, the optimum time (48 hours) and the pH (7.4) for releasing the aptamer from the nanoparticles was determined. The half-maximum inhibitory concentration (IC 50 ) value for inhibition of retinol binding to retinol binding protein 4 was 210 femtomolar (fmol). The results revealed that the aptamer could prevent connection between retinol and retinol binding protein 4 at a very low IC 50 value (210 fmol) compared to other reported inhibitors. It seems that this aptamer could be used as an efficient candidate not only for decreasing the insulin resistance in type 2 diabetes, but also for inhibiting the other retinol binding protein 4-related diseases. Copyright © 2017 Diabetes Canada. Published by Elsevier Inc. All rights reserved.

  3. Designing calcium phosphate-based bifunctional nanocapsules with bone-targeting properties

    Energy Technology Data Exchange (ETDEWEB)

    Khung, Yit-Lung; Bastari, Kelsen; Cho, Xing Ling; Yee, Wu Aik; Loo, Say Chye Joachim, E-mail: joachimloo@ntu.edu.sg [Nanyang Technological University, School of Materials Science and Engineering (Singapore)

    2012-06-15

    Using sodium dodecyl sulphate micelles as template, hollow-cored calcium phosphate nanocapsules were produced. The surfaces of the nanocapsule were subsequently silanised by a polyethylene glycol (PEG)-based silane with an N-hydroxysuccinimide ester end groups which permits for further attachment with bisphosphonates (BP). Characterisations of these nanocapsules were investigated using Field Emission Scanning Electron Microscopy (FESEM), Transmission Electron Microscopy, Fourier Transform Infra-Red Spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy and Dynamic Light Scattering. To further validate the bone-targeting potential, dentine discs were incubated with these functionalised nanocapsules. FESEM analysis showed that these surface-modified nanocapsules would bind strongly to dentine surfaces compared to non-functionalised nanocapsules. We envisage that respective components would give this construct a bifunctional attribute, whereby (1) the shell of the calcium phosphate nanocapsule would serve as biocompatible coating aiding in gradual osteoconduction, while (2) surface BP moieties, acting as targeting ligands, would provide the bone-targeting potential of these calcium phosphate nanocapsules.

  4. Designing calcium phosphate-based bifunctional nanocapsules with bone-targeting properties

    International Nuclear Information System (INIS)

    Khung, Yit-Lung; Bastari, Kelsen; Cho, Xing Ling; Yee, Wu Aik; Loo, Say Chye Joachim

    2012-01-01

    Using sodium dodecyl sulphate micelles as template, hollow-cored calcium phosphate nanocapsules were produced. The surfaces of the nanocapsule were subsequently silanised by a polyethylene glycol (PEG)-based silane with an N-hydroxysuccinimide ester end groups which permits for further attachment with bisphosphonates (BP). Characterisations of these nanocapsules were investigated using Field Emission Scanning Electron Microscopy (FESEM), Transmission Electron Microscopy, Fourier Transform Infra-Red Spectroscopy, X-ray diffraction, X-ray photoelectron spectroscopy and Dynamic Light Scattering. To further validate the bone-targeting potential, dentine discs were incubated with these functionalised nanocapsules. FESEM analysis showed that these surface-modified nanocapsules would bind strongly to dentine surfaces compared to non-functionalised nanocapsules. We envisage that respective components would give this construct a bifunctional attribute, whereby (1) the shell of the calcium phosphate nanocapsule would serve as biocompatible coating aiding in gradual osteoconduction, while (2) surface BP moieties, acting as targeting ligands, would provide the bone-targeting potential of these calcium phosphate nanocapsules.

  5. Biomimetic synthesis of modified calcium phosphate fine powders and their in vitro studies

    Energy Technology Data Exchange (ETDEWEB)

    Gergulova, R., E-mail: rumigg@yahoo.com; Tepavitcharova, S., E-mail: rumigg@yahoo.com; Rabadjieva, D., E-mail: rumigg@yahoo.com; Sezanova, K., E-mail: rumigg@yahoo.com; Ilieva, R., E-mail: rumigg@yahoo.com [Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, Acad. G. Bonchev Str., Bl. 11, 1113 Sofia (Bulgaria); Alexandrova, R.; Andonova-Lilova, B. [Institute of Experimental Morphology, Pathology and Anthropology with Museum, BAS, Acad. G. Bonchev Str., Bl. 25, Sofia (Bulgaria)

    2013-12-16

    Biomimetic approach and subsequent high-temperature treatment were used to synthesize ion modified calcium phosphate fine powders. Thus, using Simulated Body Fluid (SBF) as an ion modifier, a bi-phase mixture of ion modified β-tricalcium phosphate and hydroxyapatite (β-TCP + HA) was prepared. The use of SBF electrolyte solution enriched with Mg{sup 2+} or Zn{sup 2+} yielded monophase β-tricalcium phosphate additionally modified with Mg{sup 2+} or Zn{sup 2+} (Mg-β-TCP or Zn-β-TCP). The in vitro behavior of the prepared powders on cell viability and proliferation of murine BALB/c 3T3 fibroblasts and of human Lep 3 cells was studied by MTT test assays and Mosmann method after 72 h incubation. The relative cell viability was calculated.

  6. RF magnetron-sputtered coatings deposited from biphasic calcium phosphate targets for biomedical implant applications

    Directory of Open Access Journals (Sweden)

    K.A. Prosolov

    2017-09-01

    Full Text Available Bioactive calcium phosphate coatings were deposited by radio-frequency magnetron sputtering from biphasic targets of hydroxyapatite and tricalcium phosphate, sintered at different mass % ratios. According to Raman scattering and X-ray diffraction data, the deposited hydroxyapatite coatings have a disordered structure. High-temperature treatment of the coatings in air leads to a transformation of the quasi-amorphous structure into a crystalline one. A correlation has been observed between the increase in the Ca content in the coatings and a subsequent decrease in Ca in the biphasic targets after a series of deposition processes. It was proposed that the addition of tricalcium phosphate to the targets would led to a finer coating's surface topography with the average size of 78 nm for the structural elements.

  7. Elaboration de biocéramiques phosphocalciques Processing of calcium phosphate bioceramics

    Directory of Open Access Journals (Sweden)

    Champion Eric

    2013-11-01

    Full Text Available Les céramiques phosphocalciques (hydroxyapatite, phosphate tricalcique sont couramment utilisées comme implants synthétiques en substitution osseuse. Le développement de nouveaux implants céramiques aux performances accrues nécessite la maîtrise de nombreux paramètres chimiques et physiques intervenant dans leurs procédés d'élaboration : synthèse de poudres spécifiques, mise en forme d'architectures complexes contrôlées, frittage et fonctionnalisation. Cette contribution illustre à travers quelques exemples les travaux menés dans le domaine des procédés d'élaboration de ces biocéramiques phosphocalciques pour des applications en ingénierie des tissus osseux. Calcium phosphate ceramics (hydroxyapatite, tricalcium phosphate are commonly used as synthetic bone graft substitutes. The development of new ceramic implants with improved performances requires the mastering of many chemical and physical parameters involved in their processing: synthesis of specific powders, shaping of complex architectures, sintering and functionalization. This paper illustrates a few examples of the work in the field of processes of these calcium phosphate bioceramics for applications in bone tissue engineering.

  8. Chemical synthesis and characterization of magnesium substituted amorphous calcium phosphate (MG-ACP)

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Donghyun [Department of Biomedical Engineering, Chung-Ang University, 221 Heukseok-Dong, Dongjak-Gu, Seoul 156-756 (Korea, Republic of); Kumta, Prashant N., E-mail: pkumta@pitt.edu [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15260 (United States); Department of Mechanical Engineering and Materials Sceince, University of Pittsburgh, Pittsburgh, PA 15260 (United States); Department of Chemical and Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15260 (United States)

    2010-10-12

    Amorphous calcium phosphate (ACP) was synthesized by a simple aqueous precipitation using CaCl{sub 2} and Na{sub 3}PO{sub 4} in the presence of MgCl{sub 2} to ensure the formation of the ACP phase at room temperature. Magnesium substituted ACP phases corresponding to two different compositions representing the two most prominent calcium phosphate phases (hydroxyapatite: Ca + Mg/P = 1.67 and tricalcium phosphate: Ca + Mg/P = 1.5) were synthesized by this simple approach. Both compositions of ACP phases resulted in their transformation into {beta}-tricalcium phosphate upon heat treatment in air at 600 deg. C. X-ray diffraction (XRD), heat treatment, scanning electron microscopy (SEM), Fourier transform infrared (FT-IR) and Brunauer-Emmett-Teller (BET) analyses were used to characterize the phase, thermal stability, surface area, and morphology of the synthesized ACP powders corresponding to the two different nominal Ca/P compositions. Although it is known that {alpha}-TCP is the phase that appears upon heat treatment at 600 deg. C unsubstituted ACP, substitution of magnesium ion in ACP (both TCP and HA composition) stabilized the structure of {beta}-TCMP phase at 600 deg. C. Moreover, FT-IR analysis revealed that the ACP phase regardless of the composition, exhibited characteristic bands corresponding to that of HA, with the exception of the ACP corresponding to HA composition which exhibited a prominent OH vibrational mode.

  9. In vitro and in vivo study of commercial calcium phosphate cement HydroSet™.

    Science.gov (United States)

    Kent, Niall W; Blunn, Gordon; Karpukhina, Natalia; Davis, Graham; de Godoy, Roberta Ferro; Wilson, Rory M; Coathup, Melanie; Onwordi, Lyris; Quak, Wen Yu; Hill, Robert

    2018-01-01

    The commercial calcium phosphate cement, HydroSet™, was investigated in vitro, studying phase formation, compressive strength and setting time, followed by an ovine in vivo study to measure osseointegration, bone apposition and bone-to-graft contact. The X-ray diffraction and 31 P Magic Angle Spinning Nuclear Magnetic Resonance (MAS NMR) results showed the initial formation of octacalcium phosphate and hydroxyapatite at one hour. Over 7 days the octacalcium phosphate transformed to apatite, which was the only crystalline phase of the cement at 28 days. This apatite phase is thought to be a calcium deficient apatite. In the scanning electron microscopy, histological images of 12-week ovine in vivo results showed a high degree of osseointegration, 92.5%. Compressive strength comparisons between in vitro and in vivo measurements showed a dramatic difference between the in vitro measurements (highest 25.4 MPa) and in vivo (95 MPa), attributed to bone ingrowth into the cement in vivo. To the best of our knowledge this is the first time phase evolution of HydroSet™ and the properties studied in vitro complement the in vivo evaluation of the cement in a publication. The significance of the new finding of initial formation of octacalcium phosphate in this cement is discussed. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 21-30, 2018. © 2016 Wiley Periodicals, Inc.

  10. Pulsed electrodeposition for the synthesis of strontium-substituted calcium phosphate coatings with improved dissolution properties.

    Science.gov (United States)

    Drevet, Richard; Benhayoune, Hicham

    2013-10-01

    Strontium-substituted calcium phosphate coatings are synthesized by pulsed electrodeposition on titanium alloy (Ti6Al4V) substrates. Experimental conditions of the process are optimized in order to obtain a coating with a 5% atomic substitution of calcium by strontium which corresponds to the best observations on the osteoblast cells activity and on the osteoclast cells proliferation. The physical and chemical characterizations of the obtained coating are carried out by scanning electron microscopy associated to energy dispersive X-ray spectroscopy (EDXS) for X-ray microanalysis and the structural characterization of the coating is carried out by X-ray diffraction. The in vitro dissolution/precipitation properties of the coated substrates are investigated by immersion into Dulbecco's Modified Eagle Medium (DMEM) from 1h to 14 days. The calcium, phosphorus and strontium concentrations variations in the biological liquid are assessed by Induced Coupled Plasma - Atomic Emission Spectroscopy for each immersion time. The results show that under specific experimental conditions, the electrodeposition process is suitable to synthesize strontium-substituted calcium phosphate coatings. Moreover, the addition of hydrogen peroxide (H2O2) into the electrolytic solution used in the process allows us to observe a control of the strontium release during the immersion of the prosthetic materials into DMEM. © 2013.

  11. 25-Hydroxycholecalciferol as an antagonist of adverse corticosteroid effects on phosphate and calcium metabolism in man.

    Science.gov (United States)

    Nuti, R; Vattimo, A; Turchetti, V; Righi, G

    1984-10-01

    The present study was performed in 30 patients who needed steroid therapy: courses of triamcinolone or DTM 8-15 given orally lasted 30 days. In 15 of these patients glucoactive corticosteroids were administered in combination with 5 micrograms/day of 25OH-vitamin D3 (25OHD3). 47Calcium oral test and 99mTc-MDP kinetics, as an index of bone turnover, were performed at the beginning of the therapy and after 30 days. At the end of treatment a significant improvement of intestinal radiocalcium transport together with a decrease in bone turnover in the group of patients treated with 25OHD3 was observed. As it concerns plasma calcium level, inorganic phosphate, the urinary excretion of calcium, phosphate and hydroxyproline no significant difference between the two groups examined were noticed. These results indicate that the adverse effects of glucoactive corticosteroids on intestinal calcium transport and bone turnover may be counteracted by the combined administration of physiological doses of 25OHD3.

  12. Identification of the hydrate gel phases present in phosphate-modified calcium aluminate binders

    Energy Technology Data Exchange (ETDEWEB)

    Chavda, Mehul A.; Bernal, Susan A. [Department of Materials Science and Engineering, The University of Sheffield, Sheffield S1 3JD (United Kingdom); Apperley, David C. [Solid-State NMR Group, Department of Chemistry, Durham University, Durham DH1 3LE (United Kingdom); Kinoshita, Hajime [Department of Materials Science and Engineering, The University of Sheffield, Sheffield S1 3JD (United Kingdom); Provis, John L., E-mail: j.provis@sheffield.ac.uk [Department of Materials Science and Engineering, The University of Sheffield, Sheffield S1 3JD (United Kingdom)

    2015-04-15

    The conversion of hexagonal calcium aluminate hydrates to cubic phases in hydrated calcium aluminate cements (CAC) can involve undesirable porosity changes and loss of strength. Modification of CAC by phosphate addition avoids conversion, by altering the nature of the reaction products, yielding a stable amorphous gel instead of the usual crystalline hydrate products. Here, details of the environments of aluminium and phosphorus in this gel were elucidated using solid-state NMR and complementary techniques. Aluminium is identified in both octahedral and tetrahedral coordination states, and phosphorus is present in hydrous environments with varying, but mostly low, degrees of crosslinking. A {sup 31}P/{sup 27}Al rotational echo adiabatic passage double resonance (REAPDOR) experiment showed the existence of aluminium–phosphorus interactions, confirming the formation of a hydrated calcium aluminophosphate gel as a key component of the binding phase. This resolves previous disagreements in the literature regarding the nature of the disordered products forming in this system.

  13. Bone substitute material composition and morphology differentially modulate calcium and phosphate release through osteoclast-like cells.

    Science.gov (United States)

    Konermann, A; Staubwasser, M; Dirk, C; Keilig, L; Bourauel, C; Götz, W; Jäger, A; Reichert, C

    2014-04-01

    The aim of this study was to determine the material composition and cell-mediated remodelling of different calcium phosphate-based bone substitutes. Osteoclasts were cultivated on bone substitutes (Cerabone, Maxresorb, and NanoBone) for up to 5 days. Bafilomycin A1 addition served as the control. To determine cellular activity, the supernatant content of calcium and phosphate was measured by inductively coupled plasma optical emission spectrometry. Cells were visualized on the materials by scanning electron microscopy. Material composition and surface characteristics were assessed by energy-dispersive X-ray spectroscopy. Osteoclast-induced calcium and phosphate release was material-specific. Maxresorb exhibited the highest ion release to the medium (P = 0.034; calcium 40.25mg/l day 5, phosphate 102.08 mg/l day 5) and NanoBone the lowest (P = 0.021; calcium 8.43 mg/l day 5, phosphate 15.15 mg/l day 5); Cerabone was intermediate (P = 0.034; calcium 16.34 mg/l day 5, phosphate 30.6 mg/l day 5). All investigated materials showed unique resorption behaviours. The presented methodology provides a new perspective on the investigation of bone substitute biodegradation, maintaining the material-specific micro- and macrostructure. Copyright © 2013 International Association of Oral and Maxillofacial Surgeons. Published by Elsevier Ltd. All rights reserved.

  14. Osteoblast adhesion on novel machinable calcium phosphate/lanthanum phosphate composites for orthopedic applications.

    Science.gov (United States)

    Ergun, Celaletdin; Liu, Huinan; Webster, Thomas J

    2009-06-01

    Lanthanum phosphate (LaPO(4), LP) was combined with either hydroxyapatite (HA) or tricalcium phosphate (TCP) to form novel composites for orthopedic applications. In this study, these composites were prepared by wet chemistry synthesis and subsequent powder mixing. These HA/LP and TCP/LP composites were characterized in terms of phase stability and microstructure evolution during sintering using X-ray diffraction (XRD) and scanning electron microscopy (SEM). Their machinability was evaluated using a direct drilling test. For HA/LP composites, LP reacted with HA during sintering and formed a new phase, Ca(8)La(2)(PO(4))(6)O(2), as a reaction by-product. However, TCP/LP composites showed phase stability and the formation of a weak interface between TCP and LP machinability when sintered at 1100 degrees C, which is crucial for achieving desirable properties. Thus, these novel TCP/LP composites fulfilled the requirements for machinability, a key consideration for manufacturing orthopedic implants. Moreover, the biocompatibility of these novel LP composites was studied, for the first time, in this paper. In vitro cell culture tests demonstrated that the LP and its composites supported osteoblast (bone-forming cell) adhesion similar to natural bioceramics (such as HA and TCP). In conclusion, these novel LP composites should be further studied and developed for more effectively treating bone related diseases or injuries. 2008 Wiley Periodicals, Inc.

  15. In vitro degradation of calcium phosphates: Effect of multiscale porosity, textural properties and composition.

    Science.gov (United States)

    Diez-Escudero, A; Espanol, M; Beats, S; Ginebra, M-P

    2017-09-15

    The capacity of calcium phosphates to be replaced by bone is tightly linked to their resorbability. However, the relative importance of some textural parameters on their degradation behavior is still unclear. The present study aims to quantify the effect of composition, specific surface area (SSA), and porosity at various length scales (nano-, micro- and macroporosity) on the in vitro degradation of different calcium phosphates. Degradation studies were performed in an acidic medium to mimic the osteoclastic environment. Small degradations were found in samples with interconnected nano- and micropores with sizes below 3µm although they were highly porous (35-65%), with maximum weight loss of 8wt%. Biomimetic calcium deficient hydroxyapatite, with high SSA and low crystallinity, presented the highest degradation rates exceeding even the more soluble β-TCP. A dependence of degradation on SSA was indisputable when porosity and pore sizes were increased. The introduction of additional macroporosity with pore interconnections above 20µm significantly impacted degradation, more markedly in the substrates with high SSA (>15m 2 /g), whereas in sintered substrates with low SSA (calcium deficient hydroxyapatite did not increase its degradation rate. Overall, the study highlights the importance of textural properties, which can modulate or even outweigh the effect of other features such as the solubility of the compounds. The physicochemical features of calcium phosphates are crucial to tune biological events like resorption during bone remodeling. Understanding in vitro resorption can help to predict the in vivo behavior. Besides chemical composition, other parameters such as porosity and specific surface area have a strong influence on resorption. The complexity of isolating the contribution of each parameter lies in the close interrelation between them. In this work, a multiscale study was proposed to discern the extent to which each parameter influences degradation in

  16. Surface acidity of calcium phosphate and calcium hydroxyapatite: FTIR spectroscopic study of low-temperature CO adsorption

    International Nuclear Information System (INIS)

    Pekounov, Yassen; Chakarova, Kristina; Hadjiivanov, Konstantin

    2009-01-01

    The surface properties of calcium phosphate precursor (CP) and crystalline calcium hydroxyapatite (HA) prepared biomimetically have been studied by IR spectroscopy of adsorbed CO. Both samples are characterized by the absence of Bronsted acidity. Low-temperature CO adsorption on CP evacuated at 523 K leads to formation of only one family of Ca 2+ -CO species (2168 cm -1 ). The analysis indicates that the respective calcium ions on the surface are not isolated. Similar spectra were obtained with HA evacuated at 573 K. In this case, however, the Ca 2+ -CO band was detected at 2165 cm -1 due to enhanced lateral interaction between the adsorbed CO molecules. Another family of Ca 2+ sites (Ca 2+ -CO band at 2178 cm -1 ) was created after evacuation of the HA sample at 673 K. These sites were assumed to be a result of sample dehydroxylation. The results demonstrate the absence of any protonic acidity of the samples (i.e. P-OH surface groups) and weak electrostatic Lewis acidity caused by coordinatively unsaturated Ca 2+ cations.

  17. Dissolution and storage stability of nanostructured calcium carbonates and phosphates for nutrition

    Energy Technology Data Exchange (ETDEWEB)

    Posavec, Lidija; Knijnenburg, Jesper T. N., E-mail: jesper.knijnenburg@alumni.ethz.ch; Hilty, Florentine M. [ETH Zurich, Human Nutrition Laboratory, Institute of Food, Nutrition and Health, Department of Health Sciences and Technology (Switzerland); Krumeich, Frank; Pratsinis, Sotiris E. [ETH Zurich, Particle Technology Laboratory, Institute of Process Engineering, Department of Mechanical and Process Engineering (Switzerland); Zimmermann, Michael B. [ETH Zurich, Human Nutrition Laboratory, Institute of Food, Nutrition and Health, Department of Health Sciences and Technology (Switzerland)

    2016-10-15

    Rapid calcium (Ca) dissolution from nanostructured Ca phosphate and carbonate (CaCO{sub 3}) powders may allow them to be absorbed in much higher fraction in humans. Nanosized Ca phosphate and CaCO{sub 3} made by flame-assisted spray pyrolysis were characterized by nitrogen adsorption, X-ray diffraction (XRD), Raman spectroscopy, and transmission electron microscopy. As-prepared nanopowders contained both CaCO{sub 3} and CaO, but storing them under ambient conditions over 130 days resulted in a complete transformation into CaCO{sub 3}, with an increase in both crystal and particle sizes. The small particle size could be stabilized against such aging by cation (Mg, Zn, Sr) and anion (P) doping, with P and Mg being most effective. Calcium phosphate nanopowders made at Ca:P ≤ 1.5 were XRD amorphous and contained γ-Ca{sub 2}P{sub 2}O{sub 7} with increasing hydroxyapatite content at higher Ca:P. Aging of powders with Ca:P = 1.0 and 1.5 for over 500 days gradually increased particle size (but less than for CaCO{sub 3}) without a change in phase composition or crystallinity. In 0.01 M H{sub 3}PO{sub 4} calcium phosphate nanopowders dissolved ≈4 times more Ca than micronsized compounds and about twice more Ca than CaCO{sub 3} nanopowders, confirming that nanosizing and/or amorphous structuring sharply increases Ca powder dissolution. Because higher Ca solubility in vitro generally leads to greater absorption in vivo, these novel FASP-made Ca nanostructured compounds may prove useful for nutrition applications, including supplementation and/or food fortification.

  18. Dissolution and storage stability of nanostructured calcium carbonates and phosphates for nutrition

    Science.gov (United States)

    Posavec, Lidija; Knijnenburg, Jesper T. N.; Hilty, Florentine M.; Krumeich, Frank; Pratsinis, Sotiris E.; Zimmermann, Michael B.

    2016-10-01

    Rapid calcium (Ca) dissolution from nanostructured Ca phosphate and carbonate (CaCO3) powders may allow them to be absorbed in much higher fraction in humans. Nanosized Ca phosphate and CaCO3 made by flame-assisted spray pyrolysis were characterized by nitrogen adsorption, X-ray diffraction (XRD), Raman spectroscopy, and transmission electron microscopy. As-prepared nanopowders contained both CaCO3 and CaO, but storing them under ambient conditions over 130 days resulted in a complete transformation into CaCO3, with an increase in both crystal and particle sizes. The small particle size could be stabilized against such aging by cation (Mg, Zn, Sr) and anion (P) doping, with P and Mg being most effective. Calcium phosphate nanopowders made at Ca:P ≤ 1.5 were XRD amorphous and contained γ-Ca2P2O7 with increasing hydroxyapatite content at higher Ca:P. Aging of powders with Ca:P = 1.0 and 1.5 for over 500 days gradually increased particle size (but less than for CaCO3) without a change in phase composition or crystallinity. In 0.01 M H3PO4 calcium phosphate nanopowders dissolved ≈4 times more Ca than micronsized compounds and about twice more Ca than CaCO3 nanopowders, confirming that nanosizing and/or amorphous structuring sharply increases Ca powder dissolution. Because higher Ca solubility in vitro generally leads to greater absorption in vivo, these novel FASP-made Ca nanostructured compounds may prove useful for nutrition applications, including supplementation and/or food fortification.

  19. Dissolution and storage stability of nanostructured calcium carbonates and phosphates for nutrition

    International Nuclear Information System (INIS)

    Posavec, Lidija; Knijnenburg, Jesper T. N.; Hilty, Florentine M.; Krumeich, Frank; Pratsinis, Sotiris E.; Zimmermann, Michael B.

    2016-01-01

    Rapid calcium (Ca) dissolution from nanostructured Ca phosphate and carbonate (CaCO 3 ) powders may allow them to be absorbed in much higher fraction in humans. Nanosized Ca phosphate and CaCO 3 made by flame-assisted spray pyrolysis were characterized by nitrogen adsorption, X-ray diffraction (XRD), Raman spectroscopy, and transmission electron microscopy. As-prepared nanopowders contained both CaCO 3 and CaO, but storing them under ambient conditions over 130 days resulted in a complete transformation into CaCO 3 , with an increase in both crystal and particle sizes. The small particle size could be stabilized against such aging by cation (Mg, Zn, Sr) and anion (P) doping, with P and Mg being most effective. Calcium phosphate nanopowders made at Ca:P ≤ 1.5 were XRD amorphous and contained γ-Ca 2 P 2 O 7 with increasing hydroxyapatite content at higher Ca:P. Aging of powders with Ca:P = 1.0 and 1.5 for over 500 days gradually increased particle size (but less than for CaCO 3 ) without a change in phase composition or crystallinity. In 0.01 M H 3 PO 4 calcium phosphate nanopowders dissolved ≈4 times more Ca than micronsized compounds and about twice more Ca than CaCO 3 nanopowders, confirming that nanosizing and/or amorphous structuring sharply increases Ca powder dissolution. Because higher Ca solubility in vitro generally leads to greater absorption in vivo, these novel FASP-made Ca nanostructured compounds may prove useful for nutrition applications, including supplementation and/or food fortification.

  20. Glucose-6-phosphate reduces calcium accumulation in rat brain endoplasmic reticulum

    Directory of Open Access Journals (Sweden)

    Jeffrey Thomas Cole

    2012-04-01

    Full Text Available Brain cells expend large amounts of energy sequestering calcium (Ca2+, while loss of Ca2+ compartmentalization leads to cell damage or death. Upon cell entry, glucose is converted to glucose-6-phosphate (G6P, a parent substrate to several metabolic major pathways, including glycolysis. In several tissues, G6P alters the ability of the endoplasmic reticulum to sequester Ca2+. This led to the hypothesis that G6P regulates Ca2+ accumulation by acting as an endogenous ligand for sarco-endoplasmic reticulum calcium ATPase (SERCA. Whole brain ER microsomes were pooled from adult male Sprague-Dawley rats. Using radio-isotopic assays, 45Ca2+ accumulation was quantified following incubation with increasing amounts of G6P, in the presence or absence of thapsigargin, a potent SERCA inhibitor. To qualitatively assess SERCA activity, the simultaneous release of inorganic phosphate (Pi coupled with Ca2+ accumulation was quantified. Addition of G6P significantly and decreased Ca2+ accumulation in a dose-dependent fashion (1-10 mM. The reduction in Ca2+ accumulation was not significantly different that seen with addition of thapsigargin. Addition of glucose-1-phosphate or fructose-6-phosphate, or other glucose metabolic pathway intermediates, had no effect on Ca2+ accumulation. Further, the release of Pi was markedly decreased, indicating G6P-mediated SERCA inhibition as the responsible mechanism for reduced Ca2+ uptake. Simultaneous addition of thapsigargin and G6P did decrease inorganic phosphate in comparison to either treatment alone, which suggests that the two treatments have different mechanisms of action. Therefore, G6P may be a novel, endogenous regulator of SERCA activity. Additionally, pathological conditions observed during disease states that disrupt glucose homeostasis, may be attributable to Ca2+ dystasis caused by altered G6P regulation of SERCA activity

  1. Cooperation of phosphates and carboxylates controls calcium oxalate crystallization in ultrafiltered urine.

    Science.gov (United States)

    Grohe, Bernd; Chan, Brian P H; Sørensen, Esben S; Lajoie, Gilles; Goldberg, Harvey A; Hunter, Graeme K

    2011-10-01

    Osteopontin (OPN) is one of a group of proteins found in urine that are believed to limit the formation of kidney stones. In the present study, we investigate the roles of phosphate and carboxylate groups in the OPN-mediated modulation of calcium oxalate (CaOx), the principal mineral phase found in kidney stones. To this end, crystallization was induced by addition of CaOx solution to ultrafiltered human urine containing either human kidney OPN (kOPN; 7 consecutive carboxylates, 8 phosphates) or synthesized peptides corresponding to residues 65-80 (pSHDHMDDDDDDDDDGD; pOPAR) or 220-235 (pSHEpSTEQSDAIDpSAEK; P3) of rat bone OPN. Sequence 65-80 was also synthesized without the phosphate group (OPAR). Effects on calcium oxalate monohydrate (COM) and dihydrate (COD) formation were studied by scanning electron microscopy. We found that controls form large, partly intergrown COM platelets; COD was never observed. Adding any of the polyelectrolytes was sufficient to prevent intergrowth of COM platelets entirely, inhibiting formation of these platelets strongly, and inducing formation of the COD phase. Strongest effects on COM formation were found for pOPAR and OPAR followed by kOPN and then P3, showing that acidity and hydrophilicity are crucial in polyelectrolyte-affected COM crystallization. At higher concentrations, OPAR also inhibited COD formation, while P3, kOPN and, in particular, pOPAR promoted COD, a difference explainable by the variations of carboxylate and phosphate groups present in the molecules. Thus, we conclude that carboxylate groups play a primary role in inhibiting COM formation, but phosphate and carboxylate groups are both important in initiating and promoting COD formation.

  2. Plasma Calcium, Inorganic Phosphate and Magnesium During Hypocalcaemia Induced by a Standardized EDTA Infusion in Cows

    Directory of Open Access Journals (Sweden)

    Enemark JMD

    2001-06-01

    Full Text Available The intravenous Na2EDTA infusion technique allows effective specific chelation of circulating Ca2+ leading to a progressive hypocalcaemia. Methods previously used were not described in detail and results obtained by monitoring total and free ionic calcium were not comparable due to differences in sampling and analysis. This paper describes a standardized EDTA infusion technique that allowed comparison of the response of calcium, phosphorus and magnesium between 2 groups of experimental cows. The concentration of the Na2EDTA solution was 0.134 mol/l and the flow rate was standardized at 1.2 ml/kg per hour. Involuntary recumbency occurred when ionised calcium dropped to 0.39 – 0.52 mmol/l due to chelation. An initial fast drop of ionized calcium was observed during the first 20 min of infusion followed by a fluctuation leading to a further drop until recumbency. Pre-infusion [Ca2+] between tests does not correlate with the amount of EDTA required to induce involuntary recumbence. Total calcium concentration measured by atomic absorption remained almost constant during the first 100 min of infusion but declined gradually when the infusion was prolonged. The concentration of inorganic phosphate declined gradually in a fluctuating manner until recumbency. Magnesium concentration remained constant during infusion. Such electrolyte responses during infusion were comparable to those in spontaneous milk fever. The standardized infusion technique might be useful in future experimental studies.

  3. The efficiency of child formula dentifrices containing different calcium and phosphate compounds on artificial enamel caries.

    Science.gov (United States)

    Rirattanapong, Praphasri; Vongsavan, Kadkao; Saengsirinavin, Chavengkiat; Khumsub, Ploychompoo

    2016-01-01

    Fluoride toothpaste has been extensively used to prevent dental caries. However, the risk of fluorosis is concerning, especially in young children. Calcium phosphate has been an effective remineralizing agent and is present in commercial dental products, with no risk of fluorosis to users. This in vitro study aimed to compare the effects of different calcium phosphate compounds and fluoride-containing dentifrices on artificial caries in primary teeth. Fifty sound primary incisors were coated with nail varnish, leaving two 1 mm 2 windows on the labial surface before immersion in demineralizing solution for 96 hours to produce artificial enamel lesions. Subsequently, one window from each tooth was coated with nail varnish, and all 50 teeth were divided into five groups ( n = 10); group A - deionized water; group B - casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) paste (Tooth Mousse); group C - 500 ppm F (Colgate Spiderman ® ); group D - nonfluoridated toothpaste with triple calcium phosphate (Pureen ® ); and group E - tricalcium phosphate (TCP). Polarized light microscopy and Image-Pro ® Plus software were used to evaluate lesions. After a 7-day pH-cycle, mean lesion depths in groups A, B, C, D, and E had increased by 57.52 ± 10.66%, 33.28 ± 10.16%, 17.04 ± 4.76%, 32.51 ± 8.99%, and 21.76 ± 8.15%, respectively. All data were processed by the Statistical Package for the Social Sciences (version 16.0) software package. Comparison of percentage changes using one-way analysis of variance and Fisher's least squares difference tests at a 95% level of confidence demonstrated that group A was significantly different from the other groups ( P < 0.001). Lesions in groups B and D had a significant lesion progression when compared with groups C and E. All toothpastes in this study had the potential to delay the demineralization progression of artificial enamel caries in primary teeth. The fluoride 500 ppm and TCP toothpastes were equal in the deceleration of

  4. The Role of Poly(Aspartic Acid) in the Precipitation of Calcium Phosphate in Confinement.

    Science.gov (United States)

    Cantaert, Bram; Beniash, Elia; Meldrum, Fiona C

    2013-12-28

    Many questions remain regarding the formation of ultrathin hydroxapatite (HAP) crystals within the confines of collagen fibrils of bones. These structures form through the interplay of the collagen matrix and non-collagenous proteins, and in vitro mineralization studies employing poly(aspartic acid) (PAsp) as a mimic of the non-collagenous proteins have generated mineralized fibrils with structures comparable to their biogenic counterparts. In this article, we employ the nanoscale cylindrical pores perforating track-etch filtration membranes to investigate the role of PAsp in controlling the infiltration and crystallization of calcium phosphate (CaP) within confined volumes. Oriented polycrystalline HAP and non-oriented octacalcium phosphate (OCP) rods precipitated within the membrane pores via an amorphous calcium phosphate (ACP) precursor, where PAsp increased the proportion of OCP rods. Further, ACP crystallized faster within the membranes than in bulk solution when PAsp was present, suggesting that PAsp inhibits crystallization in solution, but promotes it when bound to a substrate. Finally, in contrast to the collagen system, PAsp reduced the yield of intra-membrane mineral and failed to enhance infiltration. This suggests that a specific interaction between the collagen matrix and ACP/PAsp precursor particles drives effective infiltration. Thus, while orientation of HAP crystals can be achieved by confinement alone, the chemistry of the collagen matrix is necessary for efficient mineralisation with CaP.

  5. In Situ Laser Coating of Calcium Phosphate on TC4 Surface for Enhancing Bioactivity

    Institute of Scientific and Technical Information of China (English)

    DENG Chi; WANG Yong; ZHANG Ya-ping; GAO Jia-cheng

    2007-01-01

    Titanium alloy has been a successful implant material owing to its excellent ratio of strength to weight,toughness, and bio-inert oxide surface. Significant progress has been made in improving the bioactivity of titanium alloy by coating its oxide surface with calcium phosphates. In the present study, in situ coating was reported on Ti6Al4V(TC4) surface with calcium phosphate (Ca-P) bioceramics synthesized and synchronously cladded by laser beam. This coating was grown by first preplacing directly the raw powders, which contain 80% of CaHPO4 ·2H2O, 20% of CaCO3, and dram of rare earth (RE), on the TC4 surfaces, and then exposing the surfaces to the laser beam with a power density of 12. 73-15.27 MW · m-2 and a scanning velocity of 10. 5 m/s. The resultant coating was characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD), thermogravimetric analysis and Different-thermal Scanning (TG-DSC), and Energy Dispersive X-ray Detection (EDX). The results show that these laser ceramics include hydroxyapatite (HA), tricalcium phosphate (TCP), Ca2P2O7, and other Ca-P phases, and the interface between the coating and the TC4 substrate has tighter fixation, in which the chemical bonding is approved. These laser hybrid coatings are useful in enhancing the bioactivity of titanium alloy surfaces.

  6. Synthesis and characterization of the aluminium phosphates modified with ammonium, calcium and molybdenum by hydrothermal method

    Directory of Open Access Journals (Sweden)

    Łuczka Kinga

    2016-06-01

    Full Text Available Synthesis and characterization of the aluminum phosphates modified with ammonium, calcium and molybdenum were conducted. The influence of process parameters (reactive pressure and molar ratios in the reaction mixture were studied. The contents of the individual components in the products were in the range of: 10.97–17.31 wt% Al, 2.65–13.32 wt% Ca, 0.70–3.11 wt% Mo, 4.36–8.38 wt% NH3, and 35.12–50.54 wt% P2O5. The materials obtained in the experiments were characterized by various physicochemical parameters. The absorption oil number was in the range from 67 to 89 of oil/100 g of product, the surface area was within the range of 4–76 m2/g, whereas the average particle size of products reached 282–370 nm. The Tafel tests revealed comparable anticorrosive properties of aluminum phosphates modified with ammonium, calcium, molybdenum in comparison with commercial phosphate.

  7. Influences of the steam sterilization on the properties of calcium phosphate porous bioceramics.

    Science.gov (United States)

    Li, Xiangfeng; Guo, Bo; Xiao, Yumei; Yuan, Tun; Fan, Yujiang; Zhang, Xingdong

    2016-01-01

    The influences of steam sterilization on the physicochemical properties of calcium phosphate (Ca-P) porous bioceramics, including β-tricalcium phosphate (β-TCP), biphasic calcium phosphate (BCP) and hydroxyapatite (HA) are investigated. After being steam sterilized in an autoclave (121 °C for 40 min), the porous bioceramics are dried and characterized. The steam sterilization has no obvious effects on the phase composition, thermal stability, pH value and dissolubility of β-TCP porous bioceramic, but changes its morphology and mechanical strength. Meanwhile, the steam sterilization leads to the significant changes of the morphology, phase composition, pH value and dissolubility of BCP porous bioceramic. The increase of dissolubility and mechanical strength, the decrease of pH value of the immersed solution and partial oriented growth of crystals are also observed in HA porous bioceramic after steam sterilization. These results indicate that the steam sterilization can result in different influences on the physicochemical properties of β-TCP, BCP and HA porous bioceramics, thus the application of the steam sterilization on the three kinds of Ca-P porous bioceramics should be considered carefully based on the above changed properties.

  8. Efficacy of tooth whitening with different calcium phosphate-based formulations.

    Science.gov (United States)

    Jin, Jian; Xu, Xiaohui; Lai, Guangyun; Kunzelmann, Karl-Heinz

    2013-08-01

    The aim of this in-vitro study was to evaluate the efficacy of tooth whitening using different calcium phosphate-based formulations. Teeth were treated with three different hydroxyapatite preparations at different concentrations and with two control preparations; each tooth was treated a total of three times. After application of the last material, hydrodynamic shear force was applied to mimic mechanical loading. After each treatment, tooth color was measured using a dental spectrophotometer, and the mean changes in L*a*b* values between different measurements were expressed as ∆E. The results indicated significant differences between the materials, but neither dose- nor time-dependent associations were found. The suspension containing tricalcium phosphate (10 wt%) showed the most obvious color change (∆E = 2.20 ± 0.90), while the suspension containing zinc-carbonate-apatite (20 wt%) showed the least obvious color change (∆E = 0.91 ± 0.50). Calcium phosphate-based formulations that can adhere to the enamel surface and contribute to tooth whitening have promising tooth-whitening potential. © 2013 Eur J Oral Sci.

  9. Injectable TEMPO-oxidized nanofibrillated cellulose/biphasic calcium phosphate hydrogel for bone regeneration.

    Science.gov (United States)

    Safwat, Engie; Hassan, Mohammad L; Saniour, Sayed; Zaki, Dalia Yehia; Eldeftar, Mervat; Saba, Dalia; Zazou, Mohamed

    2018-05-01

    Nanofibrillated cellulose, obtained from rice straw agricultural wastes was used as a substrate for the preparation of a new injectable and mineralized hydrogel for bone regeneration. Tetramethyl pyridine oxyl (TEMPO) oxidized nanofibrillated cellulose, was mineralized through the incorporation of a prepared and characterized biphasic calcium phosphate at a fixed ratio of 50 wt%. The TEMPO-oxidized rice straw nanofibrillated cellulose was characterized using transmission electron microscopy, Fourier transform infrared, and carboxylic content determination. The injectability and viscosity of the prepared hydrogel were evaluated using universal testing machine and rheometer testing, respectively. Cytotoxicity and alkaline phosphatase level tests on osteoblast like-cells for in vitro assessment of the biocompatibility were investigated. Results revealed that the isolated rice straw nanofibrillated cellulose is a nanocomposite of the cellulose nanofibers and silica nanoparticles. Rheological properties of the tested materials are suitable for use as injectable material and of nontoxic effect on osteoblast-like cells, as revealed by the positive alkaline phosphate assay. However, nanofibrillated cellulose/ biphasic calcium phosphate hydrogel showed higher cytotoxicity and lower bioactivity test results when compared to that of nanofibrillated cellulose.

  10. Feasibility of a tetracycline-binding method for detecting synovial fluid basic calcium phosphate crystals.

    Science.gov (United States)

    Rosenthal, Ann K; Fahey, Mark; Gohr, Claudia; Burner, Todd; Konon, Irina; Daft, Laureen; Mattson, Eric; Hirschmugl, Carol; Ryan, Lawrence M; Simkin, Peter

    2008-10-01

    Basic calcium phosphate (BCP) crystals are common components of osteoarthritis (OA) synovial fluid. Progress in understanding the role of these bioactive particles in clinical OA has been hampered by difficulties in their identification. Tetracyclines stain calcium phosphate mineral in bone. The aim of this study was to investigate whether tetracycline staining might be an additional or alternative method for identifying BCP crystals in synovial fluid. A drop of oxytetracycline was mixed with a drop of fluid containing synthetic or native BCP, calcium pyrophosphate dihydrate (CPPD), or monosodium urate (MSU) crystals and placed on a microscope slide. Stained and unstained crystals were examined by light microscopy, with and without a portable broad-spectrum ultraviolet (UV) pen light. A small set of characterized synovial fluid samples were compared by staining with alizarin red S and oxytetracycline. Synthetic BCP crystals in synovial fluid were quantified fluorimetrically using oxytetracycline. After oxytetracycline staining, synthetic and native BCP crystals appeared as fluorescent amorphous aggregates under UV light. Oxytetracycline did not stain CPPD or MSU crystals or other particulates. Oxytetracycline staining had fewer false-positive test results than did alizarin red S staining and could provide estimates of the quantities of synthetic BCP crystals in synovial fluid. With further validation, oxytetracycline staining may prove to be a useful adjunct or alternative to currently available methods for identifying BCP crystals in synovial fluid.

  11. Understanding the Biocompatibility of Sintered Calcium Phosphate with Ratio of [Ca]/[P] = 1.50

    Directory of Open Access Journals (Sweden)

    Feng-Lin Yen

    2012-01-01

    Full Text Available Biocompatibility of sintered calcium phosphate pellets with [Ca]/[P] = 1.50 was determined in this study. Calcium pyrophosphate (CPP phase formed on the sintered pellets immersed in a normal saline solution for 14 d at 37∘C. The intensities of hydroxyapatite (HA reflections in the X-ray diffraction (XRD patterns of the pellets were retrieved to as-sintered state. The pellet surface morphology shows that CPP crystallites were clearly present and make an amorphous calcium phosphate (ACP to discriminate against become to the area of slice join together. In addition, the intensities of the CPP reflections in the XRD patterns were the highest when the pellets were immersed for 28 d. When the CPP powders were extracted from the pellets after immersion in the solution for 14 d, the viability of 3T3 cells remained above 90% for culture times from 1 to 4 d. The pellet surface morphology observed using optical microscopy showed that the cells did not adhere to the bottom of the sintered pellets when cultured for 4 d; however, some CPP phase precipitates were formed, as confirmed by XRD. In consequence, the results suggest that the sintered HA powders are good materials for use in biomedical applications because of their good biocompatibility.

  12. Influences of ambient gases on the structure and the composition of calcium phosphate films prepared by pulsed laser deposition

    International Nuclear Information System (INIS)

    Kim, Hye-Lee; Kim, Young-Sun; Kim, Dae-Joon; Lee, Won-Jun; Han, Jung-Suk

    2006-01-01

    Calcium phosphate films were prepared by using a pulsed KrF-laser deposition (PLD) method with a hydroxyapatite target in various ambient gases, such as Ar, O 2 and H 2 O. The influence of the ambient gas on the properties of the deposited films was investigated. The chamber pressure and the substrate temperature were fixed at 0.25 Torr and 600 .deg. C, respectively. Calcium-rich amorphous calcium phosphate films were deposited with a low density in Ar due to the preferential resputtering of phosphorus from the growing film. In an O 2 ambient, the density and the Ca/P ratio of the films were similar to those of the target. However, the deposited film was amorphous calcium phosphate and did not contain OH - groups. Polycrystalline hydroxyapatite films can be deposited in a H 2 O ambient because a sufficient supply of OH - groups from the ambient gas is essential for the growth of a hydroxyapatite film.

  13. Effect of carbonate and phosphate ratios on the transformation of calcium orthophosphates

    Energy Technology Data Exchange (ETDEWEB)

    Eliassi, Mohammad Daoud, E-mail: eliassi2007@gmail.com [Key Laboratory of Arable Land Conservation (Middle and Lower Reaches of Yangtze River), Ministry of Agriculture, College of Resources and Environment, Huazhong Agricultural University, Wuhan 430070 (China); Zhao, Wei [State Key Laboratory of Soil Erosion and Dryland Farming on Loess Plateau, Institute of Soil and Water Conservation, Chinese Academy of Sciences, Yangling 712100 (China); Tan, Wen Feng, E-mail: wenfeng.tan@hotmail.com [Key Laboratory of Arable Land Conservation (Middle and Lower Reaches of Yangtze River), Ministry of Agriculture, College of Resources and Environment, Huazhong Agricultural University, Wuhan 430070 (China)

    2014-07-01

    Graphical abstract: Complexes among phosphate, carbonate and calcium have been prepared via a facile hydrothermal route. The synthesized product at the low (0.15) and the high (1.8) molar ratio of PO{sub 4}{sup 3−}/CO{sub 3}{sup 2−} is calcium phosphate hydrate and hydroxylapatite (HAp), respectively. Molar ratios of PO{sub 4}{sup 3−}/CO{sub 3}{sup 2−} are effective on the reduction of carbonate activity during the crystallization of HAp. - Highlights: • Formation of different complexes from CO{sub 3}{sup 2−}, PO{sub 4}{sup 3−} and Ca{sup 2+} solutions at 60 °C. • Molar ratios of PO{sub 4}{sup 3−}/CO{sub 3}{sup 2} cause changes in phase and size of synthesized products. • Addition of PO{sub 4}{sup 3} inhibited the activity of CO{sub 3}{sup 2−} during bound with Ca{sup 2+}. • The phase transformation was completed, when CO{sub 3}{sup 2−} peaks disappeared in FTIR. • PO{sub 4}{sup 3−}, CO{sub 3}{sup 2−} and Ca{sup 2+} distributed heterogeneously on the surface of precipitation. - Abstract: Complexes among phosphate, carbonate and calcium have been synthesized by a designed hydrothermal method. Effects of carbonate and phosphate ratios on the transformation of calcium-orthophosphates were investigated. With X-ray diffraction measurement the synthesized product at the low (0.15) and the high (1.8) molar ratio of PO{sub 4}{sup 3−}/CO{sub 3}{sup 2−} is calcium phosphate hydrate at pH 9.0, and hydroxylapatite (HAp) at pH 8.0, respectively. Fourier transform infrared spectroscopy of product at the high ratio (1.8) of PO{sub 4}{sup 3−}/CO{sub 3}{sup 2−} shows that the CO{sub 3}{sup 2−} peaks disappear, and the strong peaks at 1412 and 1460 cm{sup −1} are assigned to the vibrations of PO{sub 4}{sup 3−} in HAp. {sup 31}P nuclear magnetic resonance spectra of products at the low (0.15–0.6) to the high (1.2–1.8) ratios of PO{sub 4}{sup 3−}/CO{sub 3}{sup 2−} are obtained at 2.9 and 2.7 ppm, respectively. Molar ratios of PO

  14. Ultrastructural Analysis on the Osteogenesis and Transformation of Calcium Phosphate Ceramics in Vivo

    Institute of Scientific and Technical Information of China (English)

    Honglian DAI; Shipu LI; Yuhua YAN; Xianying CAO; Xuehui LU; Yang LENG

    2004-01-01

    To study the osteogenesis and transformation process of calcium phosphate bioceramic in vivo, biodegradable porous β-tricalcium phosphate ceramics (β-TCP, φ5×8 mm) were implanted in the tibia of rabbits. β-TCP ceramics with surrounding bone tissue were retrieved and observed by SEM, TEM and EPMA every month after implantation.The results showed that osteogenesis was active and β-TCP ceramics bonded to bones directly. The new bones were forming and maturing as materials were continuously degrading, and materials were finally replaced by new bone. Parts of the materials were degraded, absorbed and recrystallized, while the rest were dispersed to the spongy bone and the Haversian lamella in an irregular arrangement, becoming incorporated into bone formation directly by remodeling the structure. Some β-TCP crystals cleaved along its (001) rhombohedral plane and formed lath-like crystals in vivo.

  15. Effect of Sr2+AND Mg2+ IONS on electrochemical deposition of calcium phosphates

    Energy Technology Data Exchange (ETDEWEB)

    Correia, M.B.; Gualberto Junior, J.P.; Macedo, M.C.S.S.; Resende, C.X.; Santos, E.A. [Universidade Federal de Sergipe (UFS), SE (Brazil)

    2014-07-01

    The incorporation of Sr2+ and Mg2+ ions into apatite favors the mineralization process of the bone, besides it to prevent the osteoporosis. In this work, it was evaluated the individual effect of Sr2+ and Mg2+ ions in the electrochemical deposition process of calcium phosphate on metallic substrate. The electrodeposition was performed using a conventional three- electrode cell. The titanium sheets were immersed in the electrolyte containing Ca(NO3)2 and NH4H2PO4 and a potential of -0. 8 V was applied. The coatings were characterized by SEM and XRD. By XRD analysis was possible to identify octacalcium phosphate in the control sample. However, after the addition of Mg2+ ions the OCP becomes the secondary phase while the brushite showed as majoritary phase. On the other hand, the incorporation of Sr2+ ions stabilized the OCP phase. (author)

  16. Studying metal impurities (Mn2+, Cu2+, Fe3+) in calcium phosphates by electron paramagnetic resonance

    Science.gov (United States)

    Iskhakova, K.; Murzakhanov, F.; Mamin, G.; Putlyaev, V.; Klimashina, E.; Fadeeva, I.; Fomin, A.; Barinov, S.; Maltsev, A.; Bakhteev, S.; Yusupov, R.; Gafurov, M.; Orlinskii, S.

    2018-05-01

    Calcium phosphates (CaP) are exploited in many fields of science, including geology, chemistry, biology and medicine due to their abundance in the nature and presence in the living organism. Various analytical and biochemical methods are used for controlling their chemical content, structure, morphology, etc. Unfortunately, magnetic resonance techniques are usually not even considered as necessary tools for CaP inspection. Some aspects of application of the commercially realized electron paramagnetic resonance (EPR) approaches for characterization of CaP powders and ceramics (including the nanosized materails) such as hydroxyapatite and tricalcium phosphates of biogenic and synthetic origins containing intrinsic impurities or intentional dopants are demonstrated. The key features and advantages of the EPR techniques for CaP based materials characterization that could compliment the data obtained with the recognized analytical methods are pointed out.

  17. The Properties of Sintered Calcium Phosphate with [Ca]/[P] = 1.50

    Directory of Open Access Journals (Sweden)

    Moo-Chin Wang

    2012-10-01

    Full Text Available In order to obtain the properties of the sintered as-dried calcium phosphate with [Ca]/[P] = 1.50, the characteristics of sintered pellets have been investigated using X-ray diffraction (XRD, inductively coupled plasma-mass spectrometry (ICP-MS, Fourier-transform infrared (FT-IR spectra, Vickers hardness indentation and scanning electron microscopy (SEM. When the pellet samples were sintered between 700 °C and 1200 °C for 4 h, the hydroxyapatite (Ca10(PO46(OH2, HA still maintained the major phase, accompanied with the rhenanite (NaCaPO4 as the secondary phase and β-tricalcium phosphate (β-Ca3(PO42, β-TCP as the minor phases. In addition, the HA partially transformed to α-tricalcium phosphate (α-Ca3(PO42, α-TCP and tetracalcium phosphate (Ca4(PO42O, TTCP, when the pellet samples were sintered at 1300 °C and 1400 °C, respectively, for 4 h. The maximum density and Vickers Hardness (HV of sintered pellet samples were 2.85 g/cm3 (90.18% theoretical density (T.D. and 407, which appeared at 1200 °C and 900 °C, respectively.

  18. Synthesis of calcium phosphates and porous hydroxyapatite beads prepared by emulsion method

    Energy Technology Data Exchange (ETDEWEB)

    Chen, B.-H. [Faculty of Biotechnology, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 807, Taiwan (China); Chen, K.-I [Department of Electronics Engineering and Computer Science, Tung-Fang Institute of Technology, 100 Dungfang Road, Hunei, Kaohsiung, Taiwan (China); Ho, M.-L. [Department of Physiology, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Chen, H.-N. [Faculty of Medicinal and Applied Chemistry, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 807, Taiwan (China); Chen, W.-C. [Faculty of Dentistry, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Wang, C.-K. [Faculty of Medicinal and Applied Chemistry, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 807, Taiwan (China)], E-mail: ckwang@kmu.edu.tw

    2009-01-15

    Raw calcium phosphates were synthesized via a chemical reaction between 0.5 M orthophosphoric acid and 0.5 M calcium hydroxide. Hydroxyapatite (HAp), {beta}-tricalcium phosphate ({beta}-TCP) or biphase calcium phosphate (BCP) comprising HAp and {beta}-TCP were obtained by changing pH value, Ca/P ratio, and the addition of glycerol. The as-synthesized and heat-treated powders were analyzed by X-ray diffraction (XRD) and Fourier transformation infrared spectrometry (FTIR). Thermal stability of the pure apatite phase was obtained to be 1300 deg. C, while synthesis was done at the pH value of 10.0 with a Ca/P ratio of 2.0 and a temperature of 37 deg. C. Besides, the {beta}-TCP phase (with higher purity) was achieved at 800 deg. C, whose synthesis was done at pH 6.4 with a Ca/P ratio of 1.5 and a temperature of 37 deg. C. Therefore, the biphase bioceramics comprising of HAp and {beta}-TCP could be obtained, since it was manipulated suitably. The HAp raw material was subjected to a simple emulsion method for the preparation of porous beads. They should have the advantage of exhibiting higher adsorptive ability and osteoconductivity in comparison with the sintered dense apatite. Additionally, the porous beads of apatite were demonstrated to be non-toxic to cells, and should be suitable for the use as a scaffold of cultured bone and bone graft material, as well as for drug delivery systems.

  19. Dental plaque microcosm biofilm behavior on calcium phosphate nanocomposite with quaternary ammonium.

    Science.gov (United States)

    Cheng, Lei; Weir, Michael D; Zhang, Ke; Wu, Eric J; Xu, Sarah M; Zhou, Xuedong; Xu, Hockin H K

    2012-08-01

    Half of dental restorations fail in 10 years, with secondary caries as the main reason. Calcium phosphate composites could remineralize tooth lesions. The objectives of this study were to: (1) impart antibacterial activity to a composite with nanoparticles of amorphous calcium phosphate (NACP); and (2) investigate the effect of quaternary ammonium dimethacrylate (QADM) on mechanical and dental plaque microcosm biofilm properties for the first time. The NACP and glass particles were filled into a dental resin that contained bis(2-methacryloyloxy-ethyl) dimethyl-ammonium bromide, the QADM. NACP nanocomposites containing 0%, 7%, 14%, and 17.5% of QADM by mass, respectively, were photo-cured. A commercial composite with no antibacterial activity was used as control. Mechanical properties were measured in three-point flexure. A human saliva microcosm model was used to grow biofilms on composites. Live/dead assay, metabolic activity, colony-forming unit (CFU) counts, and lactic acid production of biofilms on the composites were measured. Increasing QADM mass fraction monotonically reduced the biofilm viability, CFU and lactic acid. Biofilms on NACP nanocomposite with 17.5% QADM had metabolic activity that was 30% that on a commercial composite control (pbacterial cells with normal short-rod shapes, while some cells on NACP-QADM nanocomposites disintegrated into pieces. Adding QADM to NACP did not decrease the composite strength and elastic modulus, which matched (p>0.1) those of a commercial composite without Ca-PO(4) or antibacterial activity. A dental plaque microcosm model was used to evaluate the novel NACP-QADM nanocomposite. The nanocomposite greatly reduced the biofilm viability, metabolic activity and lactic acid, while its mechanical properties matched those of a commercial composite. NACP-QADM nanocomposite with calcium phosphate fillers, good mechanical properties and a strong antibacterial activity may have potential for anti-biofilm and anti

  20. In-situ high temperature XRD of calcium phosphate biomaterial using DEHPA as the starting material

    International Nuclear Information System (INIS)

    Meor Yusoff Meor Sulaiman; Masliana Muslim

    2009-01-01

    A process to produce calcium phosphate biomaterial was done using an organic based phosphoric acid (DEHPA) as its starting material. The gel obtained from this reaction was used to study calcium phosphate transformation using in-situ XRD with temperature ranges from room temperature to 1300 degree C. The results obtained from this analysis show the following phase transformation: Gel β-Ca 2 P 2 O 7 β-TCP + HA α-TCP + HA, β-Ca 2 P 2 O 7 forms at 400 degree C and as we heat the sample at 1000 degree C peaks belonging to β- TCP and HA appears showing the transformation of the β-Ca 2 P 2 O 7 phase. When the sample is heated up further to 1200 degree C, β-TCP is transform into α-TCP. In the cold in-situ study, XRD analysis was performed on the sample from room temperature to -140 degree C. At room the XRD diffractogram shows the sample as an amorphous material and as the temperature was further lowered sharp peaks begins to form indicating that the material had becomes crystalline. The peaks were identified to be that calcium hydrogen phosphate (Ca(H 2 PO 4 ) 2 ) and this indicates that there is no hydroxyl group removal during the cooling process. The relative crystallinity values obtained for the different cooling temperatures show a slow exponential increase on the initial cooling of 0 to -100 degree C and at further cooling temperatures resulted fast and linear process. Also unlike the in-situ XRD analysis performs at high temperature no phase transformation occurred at this low temperature. (Author)

  1. Synthesis and characterization of Ag-containing calcium phosphates with various Ca/P ratios

    Energy Technology Data Exchange (ETDEWEB)

    Gokcekaya, Ozkan, E-mail: gokcekaya@dc.tohoku.ac.jp [Department of Materials Processing, Tohoku University, 6-6-02 Aza Aoba, Aramaki, Aoba-ku, Sendai, Miyagi 980-8579 (Japan); Ueda, Kyosuke; Narushima, Takayuki [Department of Materials Processing, Tohoku University, 6-6-02 Aza Aoba, Aramaki, Aoba-ku, Sendai, Miyagi 980-8579 (Japan); Ergun, Celaletdin [Faculty of Mechanical Engineering, Istanbul Technical University, 65 Inonu Street, Gumussuyu, Istanbul 34437 (Turkey)

    2015-08-01

    Ag-containing calcium phosphate (CaP) powders were synthesized by a precipitation method using aqueous solutions of calcium nitrate, silver nitrate, and ammonium phosphate. The powders were sintered at temperatures ranging from 1173 to 1473 K. The charged atomic ratios of (Ca + Ag)/P and Ag/(Ca + Ag) in solution were varied from 1.33 to 1.67 and from 0 to 0.30, respectively. The Ag content in the as-precipitated CaP powders increased with the charged Ag/(Ca + Ag) atomic ratio in solution and was lower than the charged Ag/(Ca + Ag) value. The as-precipitated CaP powders consisted of hydroxyapatite (HA) as the main phase. Ag nanoparticles were observed on the as-precipitated HA particles under all conditions of Ag addition. After the sintering, HA, β-TCP (tricalcium phosphate), α-TCP, and β-CPP (calcium pyrophosphate) were mainly detected as CaPs on the basis of the Ca/P atomic ratio of the as-precipitated powders. The addition of Ag stabilized the β-TCP phase, and the distribution of Ag in β-TCP was homogeneous. A metallic Ag phase coexisted with HA. The solubility of Ag in HA was estimated to be 0.0019–0.0061 (Ag/(Ca + Ag)) atomic ratio, which was lower than that in β-TCP (higher than 0.0536) and higher than that of β-CPP (below the detection limit of analyses). - Highlights: • The HA powders with Ag nanoparticles were synthesized by a precipitation method. • Metallic Ag particles were detected with the HA phase after sintering. • The distribution of Ag in β-TCP was homogeneous after sintering. • The addition of Ag stabilized the β-ΤCP phase. • β-TCP exhibited higher solubility of Ag than HA and β-CPP.

  2. Direct 3D powder printing of biphasic calcium phosphate scaffolds for substitution of complex bone defects

    International Nuclear Information System (INIS)

    Castilho, Miguel; Pires, Inês; Moseke, Claus; Ewald, Andrea; Gbureck, Uwe; Groll, Jürgen; Teßmar, Jörg; Vorndran, Elke

    2014-01-01

    The 3D printing technique based on cement powders is an excellent method for the fabrication of individual and complex bone substitutes even in the case of large defects. The outstanding bone remodeling capacity of biphasic calcium phosphates (BCPs) containing hydroxyapatite (HA) as well as tricalcium phosphate (TCP) in varying ratios makes the adaption of powder systems resulting in BCP materials to this fabrication technique a desirable aim. This study presents the synthesis and characterization of a novel powder system for the 3D printing process, intended for the production of complexly shaped BCP scaffolds by a hydraulic setting reaction of calcium carbonate and TCP with phosphoric acid. The HA/TCP ratio in the specimens could be tailored by the calcium/phosphate ratio of the starting powder. The scaffolds could be fabricated with a dimensional accuracy of >96.5% and a minimal macro pore size of 300 µm. Independent of the phase composition the printed specimens showed a microporosity of approximately 68%, while the compressive strength strongly depended on the chemical composition and increased with rising TCP content in the scaffolds to a maximum of 1.81 MPa. Post-treatment of the scaffolds with a polylactic-co-glycolic acid-solution enhanced the mechanical properties by a factor of 8. In vitro studies showed that all BCP scaffolds were cytocompatible and enhanced the cell viability as well as the cell proliferation, as compared with pure TCP. Cell proliferation is even better on BCP when compared to HA and cell viability is in a similar range on these materials. (paper)

  3. Co-crystallization of cholesterol and calcium phosphate as related to atherosclerosis

    Science.gov (United States)

    Hirsch, Danielle; Azoury, Reuven; Sarig, Sara

    1990-09-01

    Calcification of atherosclerotic plaques occurs very frequently and aggravates the disease. In biological systems, epitaxial relationships between crystal structures may be important in nucleating the deposit of a solid phase. The biologically preferred calcium phosphate species, apatite, and cholesterol crystal have structurally compatible crystallographic faces which allow epitaxial growth of one crystal upon another. The present study describes a new approach to explore, in vitro, the crystallization processes of calcium phosphate (CaP) with cholesterol (CS) and cholestanol (CN) which are related to atherosclerosis. Aqueous solutions containing calcium and phosphate ions or CaP crystals as hydroxyapatite were added into saturated ethanolic solutions of CS or CS and 10% CN. After precipitation, crystals were collected and analyzed by nuclear magnetic resonance (NMR), infra-red (IR), X-ray, scanning electron microscope (SEM-LINK), differential scanning calorimeter (DSC) and atomic absorption. The principal result is the well-formed crystals precipitation when an aqueous solution and CaP seed crystals were added to saturated solutions of CS and 10% CN. Cholesterol-cholestanol dihydrate (CC2W) crystals precipitated in the presence of CaP seeds were compared to the CC2W crystals obtained without the mineral compound. The results of this comparison indicate a special link between crystals of CaP and CC2W, and support the epitaxial relationship between the two kinds of crystals. The potential of CC2W crystals to be precipitated by CaP seed crystals prove likewise the possible significant role of the cholestanol metabolite in the process of cholesterol crystallization and calcification in the arteries.

  4. Synthesis and characterization of Ag-containing calcium phosphates with various Ca/P ratios

    International Nuclear Information System (INIS)

    Gokcekaya, Ozkan; Ueda, Kyosuke; Narushima, Takayuki; Ergun, Celaletdin

    2015-01-01

    Ag-containing calcium phosphate (CaP) powders were synthesized by a precipitation method using aqueous solutions of calcium nitrate, silver nitrate, and ammonium phosphate. The powders were sintered at temperatures ranging from 1173 to 1473 K. The charged atomic ratios of (Ca + Ag)/P and Ag/(Ca + Ag) in solution were varied from 1.33 to 1.67 and from 0 to 0.30, respectively. The Ag content in the as-precipitated CaP powders increased with the charged Ag/(Ca + Ag) atomic ratio in solution and was lower than the charged Ag/(Ca + Ag) value. The as-precipitated CaP powders consisted of hydroxyapatite (HA) as the main phase. Ag nanoparticles were observed on the as-precipitated HA particles under all conditions of Ag addition. After the sintering, HA, β-TCP (tricalcium phosphate), α-TCP, and β-CPP (calcium pyrophosphate) were mainly detected as CaPs on the basis of the Ca/P atomic ratio of the as-precipitated powders. The addition of Ag stabilized the β-TCP phase, and the distribution of Ag in β-TCP was homogeneous. A metallic Ag phase coexisted with HA. The solubility of Ag in HA was estimated to be 0.0019–0.0061 (Ag/(Ca + Ag)) atomic ratio, which was lower than that in β-TCP (higher than 0.0536) and higher than that of β-CPP (below the detection limit of analyses). - Highlights: • The HA powders with Ag nanoparticles were synthesized by a precipitation method. • Metallic Ag particles were detected with the HA phase after sintering. • The distribution of Ag in β-TCP was homogeneous after sintering. • The addition of Ag stabilized the β-ΤCP phase. • β-TCP exhibited higher solubility of Ag than HA and β-CPP

  5. CALCIUM, CREATININE AND URINARY PHOSPHATE/CREATININE RATIO CONCENTRATIONS IN NEONATES OF VARIOUS GESTATIONAL AGES

    Directory of Open Access Journals (Sweden)

    O. I. Fomina

    2014-01-01

    Full Text Available Objective: specify peculiarities of calcium and phosphates excretion in neonates of various gestational ages and types of feeding in neonatal period. Patients and methods. Calcium-creatinine (Ca/Cr and phosphate-creatinine (P/Cr ratio concentrations were determined in 96 healthy neonates of 38-40 weeks of gestational age and 146 premature infants of 28-37 weeks of gestational age of various types of feeding. Results. The Ca/Cr ratio concentration in healthy term infants in the early neonatal period amounted to 0.9-2.2 (median – 1.8, the P/Cr ratio concentration – 0.8-2.1 (median – 1.6. The Ca/Cr ratio concentration in premature infants (28-37 weeks of gestational age amounted to 0.9-2.4 (median – 1.9, which is comparable to this parameter’s value in term infants. The P/Cr ratio concentration amounted to 0.7-3.1 (median – 2.4, which exceeds this parameter’s value in term infants. The lesser the gestational age and birth weight, the higher the Ca/Cr and P/Cr ratio concentrations. The authors revealed hypercalciuria and hyperphosphaturia in premature infants with a very low body weight fed with specialized formulas. Conclusions. Use of specialized formulas in small premature infants (gestational age < 33 weeks with VLBW results in excessive calcium and phosphates excretion. It is reasonable to monitor their concentrations using a non-invasive and informative method of determining Ca/Cr and P/Cr ratios. Feeding of premature infants with BW > 1,500 g with breast milk only (in case of the mother’s adequate lactation allows avoiding hypercalciuria and hyperphosphaturia and preventing risk of a renal pathology. 

  6. Proliferation and differentiation of osteoblast-like MC3T3-E1 cells ons biomimetically and electrolytically deposited calcium phosphate coatings

    NARCIS (Netherlands)

    Wang, J.; de Boer, Jan; de Groot, K.

    2009-01-01

    Biomimetic and electrolytic deposition are versatile methods to prepare calcium phosphate coatings. In this article, we compared the effects of biomimetically deposited octacalcium phosphate and carbonate apatite coatings as well as electrolytically deposited carbonate apatite coating on the

  7. Effect of polydopamine on the biomimetic mineralization of mussel-inspired calcium phosphate cement in vitro

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Zongguang [Key Lab of Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031 (China); Qu, Shuxin, E-mail: qushuxin@swjtu.edu.cn [Key Lab of Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031 (China); Zheng, Xiaotong; Xiong, Xiong [Key Lab of Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031 (China); Fu, Rong; Tang, Kuangyun; Zhong, Zhendong [Department of Plastic Surgery, Academy of Medical Sciences and Sichuan Provincial People' s Hospital, Chengdu 610041 (China); Weng, Jie [Key Lab of Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031 (China)

    2014-11-01

    Inspired by the excellent adhesive property of mussel adhesive protein, we added polydopamine (PDA) to calcium phosphate cement (PDA–CPC) to enhance its compressive strength previously. The mineralization and mechanism on PDA–CPC were investigated by soaking it in simulated body fluid in this study. The results indicated that PDA promoted the conversion of dicalcium phosphate dihydrate and α-tricalcium phosphate to hydroxyapatite (HA) in the early stage but inhibited this conversion subsequently. PDA promoted the rapid mineralization on PDA–CPC to form a layer of nanoscale calcium phosphate (CaP) whereas there was no CaP formation on the control-CPC after 1 d of soaking. This layer of nanoscale CaP was similar to that of natural bone, which was always observed during soaking. X-ray photoelectron spectroscopy showed that the peak of C=O of PDA existed in the newly formed CaP on PDA–CPC, indicating the co-precipitation of CaP with PDA. Furthermore, the newly formed CaP on PDA–CPC was HA confirmed by transmission electron microscopy, which the newly formed HA was in association with PDA. Therefore, PDA increased the capacity of mineralization of CPC and induced the formation of nanoscale bone-like apatite on PDA–CPC. Thus, this provides the feasible route for surface modification on CPC. - Highlights: • Effect of polydopamine (PDA) on the in vitro mineralization of PDA-CPC was studied. • PDA promoted the rapid mineralization on PDA-CPC to form a nanoscale HA layer. • The precipitation of the nanoscale HA layer on PDA-CPC accompanied with PDA. • Polydopamine induced mineralization is feasible for surface modification of CaP.

  8. Alendronate-Eluting Biphasic Calcium Phosphate (BCP Scaffolds Stimulate Osteogenic Differentiation

    Directory of Open Access Journals (Sweden)

    Sung Eun Kim

    2015-01-01

    Full Text Available Biphasic calcium phosphate (BCP scaffolds have been widely used in orthopedic and dental fields as osteoconductive bone substitutes. However, BCP scaffolds are not satisfactory for the stimulation of osteogenic differentiation and maturation. To enhance osteogenic differentiation, we prepared alendronate- (ALN- eluting BCP scaffolds. The coating of ALN on BCP scaffolds was confirmed by scanning electron microscopy (FE-SEM, energy-dispersive X-ray spectroscopy (EDS, and attenuated total reflectance-Fourier transform infrared spectroscopy (ATR-FTIR. An in vitro release study showed that release of ALN from ALN-eluting BCP scaffolds was sustained for up to 28 days. In vitro results revealed that MG-63 cells grown on ALN-eluting BCP scaffolds exhibited increased ALP activity and calcium deposition and upregulated gene expression of Runx2, ALP, OCN, and OPN compared with the BCP scaffold alone. Therefore, this study suggests that ALN-eluting BCP scaffolds have the potential to effectively stimulate osteogenic differentiation.

  9. Microstructure of yttric calcium phosphate bioceramic coatings synthesized by laser cladding

    International Nuclear Information System (INIS)

    Wang Diangang; Chen Chuanzhong; Ma Jie; Lei Tingquan

    2007-01-01

    The yttric calcium phosphate (CaP) coatings were in situ prepared on pure titanium substrate by laser cladding. The morphologies and phases constitution of CaP coatings were studied by electron probe microanalysis, X-ray diffraction and so on. The bonding state between the coating and the substrate is fine metallurgical combination, and the addition of yttria can fine the structure and increase the tensile strength of the coatings. The X-ray result shows that the coating is composed of the phases of HA, α-Ca 2 P 2 O 7 , β-Ca 2 P 2 O 7 and CaTiO 3

  10. [Osteogenic activity of porous calcium phosphate ceramics fabricated by rapid prototyping].

    Science.gov (United States)

    He, Chenguang; Zhao, Li; Lin, Liulan; Gu, Huijie; Zhou, Heng; Cui, Lei

    2010-07-01

    Calcium phosphate bioceramics has a broad application prospect because of good biocompatibility, but porous scaffolds with complex shape can not be prepared by the traditional methods. To fabricate porous calcium phosphate ceramics by rapid prototyping and to investigate the in vitro osteogenic activities. The porous calcium phosphate ceramics was fabricated by rapid prototyping. The bone marrow mesenchymal stem cells (BMSCs) were isolated from bone marrow of Beagle canine, and the 3rd passage BMSCs were seeded onto the porous ceramics. The cell/ceramics composite cultured in osteogenic medium were taken as the experimental group (group A) and the cell/ceramics composite cultured in growth medium were taken as the control group (group B). Meanwhile, the cells seeded on the culture plate were cultured in osteogenic medium or growth medium respectively as positive control (group C) or negative control (group D). After 1, 3, and 7 days of culture, the cell proliferation and osteogenic differentiation on the porous ceramics were evaluated by DNA quantitative analysis, histochemical staining and alkaline phosphatase (ALP) activity. After DiO fluorescent dye, the cell adhesion, growth, and proliferation on the porous ceramics were also observed by confocal laser scanning microscope (CLSM). DNA quantitative analysis results showed that the number of BMSCs in all groups increased continuously with time. Plateau phase was not obvious in groups A and B, but it was clearly observed in groups C and D. The CLSM observation indicated that the activity of BMSCs was good and the cells spread extensively, showing good adhesion and proliferation on the porous calcium phosphate ceramics prepared by rapid prototyping. ALP quantitative analysis results showed that the stain of cells on the ceramics became deeper and deeper with time in groups A and B, the staining degree in group A were stronger than that in group B. There was no significant difference in the change of the ALP activity

  11. Nano-sized calcium phosphate (CaP) carriers for non-viral gene deilvery

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Donghyun, E-mail: dhlee@cau.ac.kr [Department of Biomedical Engineering, Division of Integrative Engineering, Chung-Ang University, 221 Heukseok-Dong, Dongjak-Gu, Seoul 156-756 (Korea, Republic of); Upadhye, Kalpesh [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15260 (United States); Kumta, Prashant N., E-mail: pkumta@pitt.edu [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15260 (United States); Department of Mechanical Engineering and Materials Sceince, University of Pittsburgh, Pittsburgh, PA 15260 (United States); Department of Chemical and Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15260 (United States); Center for Complex Engineered Multifunctional Materials, University of Pittsburgh, Pittsburgh, PA 15261 (United States)

    2012-02-25

    Highlights: Black-Right-Pointing-Pointer Nanostructured calcium phosphates (NanoCaPs): comprehensive review. Black-Right-Pointing-Pointer Non viral gene delivery mechanisms: detailed mechanisms are outlined. Black-Right-Pointing-Pointer Barriers to non-viral gene delivery: detailed barriers are discussed. - Abstract: Gene therapy has garnered much interest due to the potential for curing multiple inherited and/or increases in the acquired diseases. As a result, there has been intense activity from multiple research groups for developing effective delivery methods and carriers, which is a critical step in advancing gene delivery technologies. In order for the carriers to effectively deliver the genetic payloads, multiple extracellular and intracellular barriers need to be overcome. Although overcoming these challenges to improve the effectiveness is critical, the development of safe gene delivery agents is even more vital to assure its use in clinical applications. The development of safe and effective strategies has therefore been a major challenge impeding gene therapy progress. In this regard, calcium phosphate (CaP) based nano-particles has been considered as one of the candidate non-viral gene delivery vehicles, but has been plagued by inconsistent and low transfection efficiencies limiting its progress. There has been major research effort to improve the consistency and effectiveness of CaP based vectors. Currently, it is therefore thought that by controlling the various synthesis factors such as Ca/P ratio, mode of mixing, and type of calcium phosphate phase, such variability and inefficiency could be modulated. This review attempts to provide a comprehensive analysis of the current research activity in the development of CaP based ceramic and polymer-ceramic hybrid systems for non-viral gene delivery. Preliminary transfection results of hydroxyapatite (HA or NanoCaPs), amorphous calcium phosphate (ACP) and brushite phases are also compared to assess the

  12. Physical–chemical and biological behavior of an amorphous calcium phosphate thin film produced by RF-magnetron sputtering

    International Nuclear Information System (INIS)

    Santos, Euler A. dos; Moldovan, Simona; Mateescu, Mihaela; Faerber, Jacques; Acosta, Manuel; Pelletier, Hervé; Anselme, Karine; Werckmann, Jacques

    2012-01-01

    This work evaluates the thermal reactivity and the biological reactivity of an amorphous calcium phosphate thin film produced by radio frequency (RF) magnetron sputtering onto titanium substrates. The analyses showed that the sputtering conditions used in this work led to the deposition of an amorphous calcium phosphate. The thermal treatment of this amorphous coating in the presence of H 2 O and CO 2 promoted the formation of a carbonated HA crystalline coating with the entrance of CO 3 2− ions into the hydroxyl HA lattice. When immersed in culture medium, the amorphous and carbonated coatings exhibited a remarkable instability. The presence of proteins increased the dissolution process, which was confirmed by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) analyses. Moreover, the carbonated HA coating induced precipitation independently of the presence of proteins under dynamic conditions. Despite this surface instability, this reactive calcium phosphate significantly improved the cellular behavior. The cell proliferation was higher on the Ticp than on the calcium phosphate coatings, but the two coatings increased cellular spreading and stress fiber formation. In this sense, the presence of reactive calcium phosphate coatings can stimulate cellular behavior. - Highlights: ► Functionalization of Ti with reactive CaP thin film by RF-magnetron sputtering. ► De-hydroxylation facilitating the insertion of CO 3 2− into the HA lattice. ► High surface reactivity in the presence of culture medium. ► Cell behavior improved by the presence of reactive films.

  13. A biomimetic strategy to form calcium phosphate crystals on type I collagen substrate

    Energy Technology Data Exchange (ETDEWEB)

    Xu Zhang [Department of Restorative Dentistry, Faculty of Dentistry, National University of Singapore, 5 Lower Kent Ridge Road 119074, Singapore (Singapore); Neoh, Koon Gee [Department of Chemical and Biomolecular Engineering, National University of Singapore, Kent Ridge 119260, Singapore (Singapore); Kishen, Anil, E-mail: anil.kishen@utoronto.ca [Discipline of Endodontics, Faculty of Dentistry, University of Toronto, 124 Edward Street, Toronto, ON (Canada)

    2010-07-20

    Objective: The aim of this study is to induce mineralization of collagen by introducing phosphate groups onto type I collagen from eggshell membrane (ESM) by treating with sodium trimetaphosphate (STMP). This strategy is based on the hypothesis that phosphate groups introduced on collagen can mimic the nucleating role of phosphorylated non-collagenous proteins bound to collagen for inducing mineralization in natural hard tissue. Method: The collagen membrane was phosphorylated by treating it with a solution of STMP and saturated calcium hydroxide. The phosphorylated collagen was subsequently exposed to a mineralization solution and the pattern of mineralization on the surface of phosphorylated collagen substrate was analyzed. Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), field emission electron microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and microhardness test were used to characterize the collagen substrate and the pattern of minerals formed on the collagen surface. Results: The FTIR and EDX results indicated that the phosphate groups were incorporated onto the collagen surface by treatment with STMP. During the mineralization process, the plate-like mineral, octacalcium phosphate (OCP), which was initially formed on the surface of ESM, was later transformed into needle-like hydroxyapatite (HAP) as indicated by the SEM, FESEM, EDX and XRD findings. The microhardness test displayed significant increase in the Knoop hardness number of the mineralized collagen. Conclusions: Phosphate groups can be introduced onto type I collagen surface by treating it with STMP and such phosphorylated collagen can induce the mineralization of type I collagen.

  14. Calcium phosphate-PEG-insulin-casein (CAPIC) particles as oral delivery systems for insulin.

    Science.gov (United States)

    Morçöl, T; Nagappan, P; Nerenbaum, L; Mitchell, A; Bell, S J D

    2004-06-11

    An oral delivery system for insulin was developed and functional activity was tested in a non-obese diabetic (NOD) mice model. Calcium phosphate particles containing insulin was synthesized in the presence of PEG-3350 and modified by aggregating the particles with caseins to obtain the calcium phosphate-PEG-insulin-casein (CAPIC) oral insulin delivery system. Single doses of CAPIC formulation were tested in NOD mice under fasting or fed conditions to evaluate the glycemic activity. The blood glucose levels were monitored every 1-2h for 12h following the treatments using an ACCU CHECK blood glucose monitoring system. Orally administered and subcutaneously injected free insulin solution served as controls in the study. Based on the results obtained we propose that: (1). the biological activity of insulin is preserved in CAPIC formulation; (2). insulin in CAPIC formulations, but not the free insulin, displays a prolonged hypoglycemic effect after oral administration to diabetic mice; (3). CAPIC formulation protects insulin from degradation while passing through the acidic environment of the GI track until it is released in the less acidic environment of the intestines where it can be absorbed in its biologically active form; (4). CAPIC formulation represents a new and unique oral delivery system for insulin and other macromolecules.

  15. A histological evaluation on osteogenesis and resorption of methotrexate-loaded calcium phosphate cement in vivo

    Energy Technology Data Exchange (ETDEWEB)

    Li Dong; Yang Zhiping; Li Xin; Li Zhenfeng; Li Jianmin [Department of Orthopedics, Qilu Hospital of Shandong University, Shandong (China); Yang Jingyan, E-mail: yangzhiping@medmail.com.c [Department of Pathology, 2nd Affiliated Hospital of Shandong University, Shandong (China)

    2010-04-15

    In this study, we investigated the resorption of in vivo methotrexate-loaded calcium phosphate cement (MTX-CPC) implants and their effect on osteogenesis. MTX-CPC implants containing 1% methotrexate (MTX) (weight/weight) were preset and implanted into the femoral condyle of rabbits. Calcium phosphate cement (CPC) without MTX was used as the control. The femurs were harvested at day 1 and at 1, 3 and 6 months after implantation and radiological examination were performed. Decalcified sections were examined by hematoxylin and eosin (HE) staining, alkaline phosphatase (ALPase) immunohistochemistry and tartrate-resistant acid phosphatase (TRAPase) enzyme histochemistry. Then, we performed histomorphometric analysis, including determination of the percentage of newly formed bone and osteoblast and osteoclast counts. The results indicated that MTX-CPC implants were biocompatible, biodegradable and osteoconducive. However, MTX release from the implantation site inhibited osteogenesis in the initial period; this inhibition weakened with time, and no difference was observed between CPC and MTX-CPC at 6 months after implantation. Hence, MTX-CPC is an excellent material for filling defects and can be used for preparing effective drug delivery systems to achieve local control of invasive bone tumors.

  16. Mixed zirconia calcium phosphate coatings for dental implants: Tailoring coating stability and bioactivity potential

    International Nuclear Information System (INIS)

    Pardun, Karoline; Treccani, Laura; Volkmann, Eike; Streckbein, Philipp; Heiss, Christian; Destri, Giovanni Li; Marletta, Giovanni; Rezwan, Kurosch

    2015-01-01

    Enhanced coating stability and adhesion are essential for long-term success of orthopedic and dental implants. In this study, the effect of coating composition on mechanical, physico-chemical and biological properties of coated zirconia specimens is investigated. Zirconia discs and dental screw implants are coated using the wet powder spraying (WPS) technique. The coatings are obtained by mixing yttria-stabilized zirconia (TZ) and hydroxyapatite (HA) in various ratios while a pure HA coating served as reference material. Scanning electron microscopy (SEM) and optical profilometer analysis confirm a similar coating morphology and roughness for all studied coatings, whereas the coating stability can be tailored with composition and is probed by insertion and dissections experiments in bovine bone with coated zirconia screw implants. An increasing content of calcium phosphate (CP) resulted in a decrease of mechanical and chemical stability, while the bioactivity increased in simulated body fluid (SBF). In vitro experiments with human osteoblast cells (HOB) revealed that the cells grew well on all samples but are affected by dissolution behavior of the studied coatings. This work demonstrates the overall good mechanical strength, the excellent interfacial bonding and the bioactivity potential of coatings with higher TZ contents, which provide a highly interesting coating for dental implants. - Highlights: • Different ratios of zirconia (TZ) and calcium phosphate (CP) were deposited on zirconia substrates. • Enhancement of TZ content in mixed coatings increased coating stability. • Enhancement of CP content in mixed coatings increased bioactivity. • All tested coating compositions were non-toxic

  17. Amorphous Calcium Phosphate Formation and Aggregation Process Revealed by Light Scattering Techniques

    Directory of Open Access Journals (Sweden)

    Vida Čadež

    2018-06-01

    Full Text Available Amorphous calcium phosphate (ACP attracts attention as a precursor of crystalline calcium phosphates (CaPs formation in vitro and in vivo as well as due to its excellent biological properties. Its formation can be considered to be an aggregation process. Although aggregation of ACP is of interest for both gaining a fundamental understanding of biominerals formation and in the synthesis of novel materials, it has still not been investigated in detail. In this work, the ACP aggregation was followed by two widely applied techniques suitable for following nanoparticles aggregation in general: dynamic light scattering (DLS and laser diffraction (LD. In addition, the ACP formation was followed by potentiometric measurements and formed precipitates were characterized by Fourier transform infrared spectroscopy (FTIR, powder X-ray diffraction (PXRD, transmission electron microscopy (TEM, and atomic force microscopy (AFM. The results showed that aggregation of ACP particles is a process which from the earliest stages simultaneously takes place at wide length scales, from nanometers to micrometers, leading to a highly polydisperse precipitation system, with polydispersity and vol. % of larger aggregates increasing with concentration. Obtained results provide insight into developing a way of regulating ACP and consequently CaP formation by controlling aggregation on the scale of interest.

  18. Synthesis of biphasic calcium phosphate containing nanostructured films by micro arc oxidation on magnesium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Seyfoori, A., E-mail: klm.1985@yahoo.com [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, 16846-13114 Tehran (Iran, Islamic Republic of); National Cell Bank, Pasteur Institute of Iran, 13164 Tehran (Iran, Islamic Republic of); Mirdamadi, Sh.; Seyedraoufi, Z.S.; Khavandi, A. [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, 16846-13114 Tehran (Iran, Islamic Republic of); Aliofkhazraei, M. [Department of Materials Engineering, Faculty of Engineering, Tarbiat Modares University, 14115-143 Tehran (Iran, Islamic Republic of)

    2013-10-01

    The present research reports the synthesis of an innovative nanostructured composite film containing biphasic calcium phosphate (BCP) by the micro arc oxidation (MAO) method on AZ31 magnesium alloy. Nanometric structure of the used hydroxyapatite powder and the coatings were characterized by means of transmission and field-emission scanning electron microscope, respectively. Electrochemical behaviors of the pure MAO and nanocomposite films were also evaluated by electrochemical impedance spectroscopy and potentiodynamic polarization tests in simulated body fluid (SBF) environment. The results showed higher corrosion resistance of nanocomposite film compared to pure MAO coating, which was related to the blocking feature of the nanoparticles from the diffusing of the corrosive medium through the substrate. In addition, by immersing the specimens in simulated body fluid, greater apatite forming ability of the nanocomposite coating was proved. - Highlights: • Synthesis of innovative biphasic calcium phosphate containing nanostructured films via micro arc oxidation. • Nanocomposite film has lower degradation rate than pure MAO film. • Greater apatite forming ability for nanocomposite coating compared with pure MAO film is obtained.

  19. Biomimetic nanoparticles with polynucleotide and PEG mixed-monolayers enhance calcium phosphate mineralization

    Energy Technology Data Exchange (ETDEWEB)

    Vasconcellos, Kayla B.; McHugh, Sean M.; Dapsis, Katherine J.; Petty, Alexander R.; Gerdon, Aren E., E-mail: gerdoar@emmanuel.edu [Emmanuel College (United States)

    2013-09-15

    Biomineralization of hydroxyapatite (Ca{sub 10}(PO{sub 4}){sub 6}(OH){sub 2}) is of significant importance in biomedical applications such as bone and dental repair, and biomimetic control of mineral formation may lead to more effective restorative procedures. Gold nanoparticles are functional scaffolds on which to assemble multi-component monolayers capable of mimicking protein activity in the templated synthesis of calcium phosphate. The goal of this research was to explore nanoparticle templates with mixed-monolayers of uncharged polar polyethylene glycol (PEG) molecules and highly charged polynucleotide and amino acid molecules in their ability to influence mineralization rates and mineral particle size and morphology. This research demonstrates through time-resolved optical density and dynamic light scattering measurements that the combination of tiopronin, PEG, and DNA presented on a nanoparticle surface decreases nanoparticle aggregation from 59 to 21 nm solvated radius, increases mineralization kinetics from 1.5 Multiplication-Sign 10{sup -3} to 3.1 Multiplication-Sign 10{sup -3} OD/min, and decreases mineral particle size from 685 to 442 nm average radius. FT-IR and TEM data demonstrate that mineralized material, while initially amorphous, transforms to a semi-crystalline material when guided by template interactions. This demonstrates that surface-tailored monolayer protected cluster scaffolds are successful and controllable mineralization templates with further potential for biomedical applications involving calcium phosphate and other biomaterials.

  20. Microwave-Assisted Hydrothermal Rapid Synthesis of Calcium Phosphates: Structural Control and Application in Protein Adsorption.

    Science.gov (United States)

    Cai, Zhu-Yun; Peng, Fan; Zi, Yun-Peng; Chen, Feng; Qian, Qi-Rong

    2015-07-31

    Synthetic calcium phosphate (CaP)-based materials have attracted much attention in the biomedical field. In this study, we have investigated the effect of pH values on CaP nanostructures prepared using a microwave-assisted hydrothermal method. The hierarchical nanosheet-assembled hydroxyapatite (HAP) nanostructure was prepared under weak acidic conditions (pH 5), while the HAP nanorod was prepared under neutral (pH 7) and weak alkali (pH 9) condition. However, when the pH value increases to 11, a mixed product of HAP nanorod and tri-calcium phosphate nanoparticle was obtained. The results indicated that the pH value of the initial reaction solution played an important role in the phase and structure of the CaP. Furthermore, the protein adsorption and release performance of the as-prepared CaP nanostructures were investigated by using hemoglobin (Hb) as a model protein. The sample that was prepared at pH = 11 and consisted of mixed morphologies of nanorods and nanoprisms showed a higher Hb protein adsorption capacity than the sample prepared at pH 5, which could be explained by its smaller size and dispersed structure. The results revealed the relatively high protein adsorption capacity of the as-prepared CaP nanostructures, which show promise for applications in various biomedical fields such as drug delivery and protein adsorption.

  1. Microwave-Assisted Hydrothermal Rapid Synthesis of Calcium Phosphates: Structural Control and Application in Protein Adsorption

    Directory of Open Access Journals (Sweden)

    Zhu-Yun Cai

    2015-07-01

    Full Text Available Synthetic calcium phosphate (CaP-based materials have attracted much attention in the biomedical field. In this study, we have investigated the effect of pH values on CaP nanostructures prepared using a microwave-assisted hydrothermal method. The hierarchical nanosheet-assembled hydroxyapatite (HAP nanostructure was prepared under weak acidic conditions (pH 5, while the HAP nanorod was prepared under neutral (pH 7 and weak alkali (pH 9 condition. However, when the pH value increases to 11, a mixed product of HAP nanorod and tri-calcium phosphate nanoparticle was obtained. The results indicated that the pH value of the initial reaction solution played an important role in the phase and structure of the CaP. Furthermore, the protein adsorption and release performance of the as-prepared CaP nanostructures were investigated by using hemoglobin (Hb as a model protein. The sample that was prepared at pH = 11 and consisted of mixed morphologies of nanorods and nanoprisms showed a higher Hb protein adsorption capacity than the sample prepared at pH 5, which could be explained by its smaller size and dispersed structure. The results revealed the relatively high protein adsorption capacity of the as-prepared CaP nanostructures, which show promise for applications in various biomedical fields such as drug delivery and protein adsorption.

  2. Synthesis of biphasic calcium phosphate containing nanostructured films by micro arc oxidation on magnesium alloy

    International Nuclear Information System (INIS)

    Seyfoori, A.; Mirdamadi, Sh.; Seyedraoufi, Z.S.; Khavandi, A.; Aliofkhazraei, M.

    2013-01-01

    The present research reports the synthesis of an innovative nanostructured composite film containing biphasic calcium phosphate (BCP) by the micro arc oxidation (MAO) method on AZ31 magnesium alloy. Nanometric structure of the used hydroxyapatite powder and the coatings were characterized by means of transmission and field-emission scanning electron microscope, respectively. Electrochemical behaviors of the pure MAO and nanocomposite films were also evaluated by electrochemical impedance spectroscopy and potentiodynamic polarization tests in simulated body fluid (SBF) environment. The results showed higher corrosion resistance of nanocomposite film compared to pure MAO coating, which was related to the blocking feature of the nanoparticles from the diffusing of the corrosive medium through the substrate. In addition, by immersing the specimens in simulated body fluid, greater apatite forming ability of the nanocomposite coating was proved. - Highlights: • Synthesis of innovative biphasic calcium phosphate containing nanostructured films via micro arc oxidation. • Nanocomposite film has lower degradation rate than pure MAO film. • Greater apatite forming ability for nanocomposite coating compared with pure MAO film is obtained

  3. Polyaspartic Acid Concentration Controls the Rate of Calcium Phosphate Nanorod Formation in High Concentration Systems

    Energy Technology Data Exchange (ETDEWEB)

    Krogstad, Daniel V. [Biosystems and; Wang, Dongbo [Biosystems and; Lin-Gibson, Sheng [Biosystems and

    2017-08-31

    Polyelectrolytes are known to greatly affect calcium phosphate (CaP) mineralization. The reaction kinetics as well as the CaP phase, morphology and aggregation state depend on the relative concentrations of the polyelectrolyte and the inorganic ions in a complex, nonlinear manner. This study examines the structural evolution and kinetics of polyaspartic acid (pAsp) directed CaP mineralization at high concentrations of polyelectrolytes, calcium, and total phosphate (19–30 mg/mL pAsp, 50–100 mM Ca2+, Ca/P = 2). Using a novel combination of characterization techniques including cryogenic transmission electron microscopy (cryo-TEM), spectrophotometry, X-ray total scattering pair distribution function analysis, and attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), it was determined that the CaP mineralization occurred over four transition steps. The steps include the formation of aggregates of pAsp stabilized CaP spherical nanoparticles (sNP), crystallization of sNP, oriented attachment of the sNP into nanorods, and further crystallization of the nanorods. The intermediate aggregate sizes and the reaction kinetics were found to be highly polymer concentration dependent while the sizes of the particles were not concentration dependent. This study demonstrates the complex role of pAsp in controlling the mechanism as well as the kinetics of CaP mineralization.

  4. Effective atomic numbers (Z_e_f_f) of based calcium phosphate biomaterials: a comparative study

    International Nuclear Information System (INIS)

    Fernandes Zenobio, Madelon Aparecida; Gonçalves Zenobio, Elton; Silva, Teógenes Augusto da; Socorro Nogueira, Maria do

    2016-01-01

    This study determined the interaction of radiation parameters of four biomaterials as attenuators to measure the transmitted X-rays spectra, the mass attenuation coefficient and the effective atomic number by spectrometric system comprising the CdTe detector. The biomaterial BioOss"® presented smaller mean energy than the other biomaterials. The μ/ρ and Z_e_f_f of the biomaterials showed their dependence on photon energy. The data obtained from analytical methods of x-ray spectra, µ/ρ and Z_e_f_f_, using biomaterials as attenuators, demonstrated that these materials could be used as substitutes for dentin, enamel and bone. Further, they are determinants for the characterization of the radiation in tissues or equivalent materials. - Highlights: • Measure of the transmitted x-rays spectra using based calcium phosphate biomaterials as attenuators. • Determination effective atomic number using four dental biomaterials. • Determination of the mass attenuation coefficient (µ/ρ) of the biomaterials samples calculated by the WinXCOM software. • Determination of the chemical composition of calcium phosphate biomaterials.

  5. Preparation and characterization of a novel injectable strontium-containing calcium phosphate cement with collagen

    Directory of Open Access Journals (Sweden)

    Zhou Ziqiang

    2015-07-01

    Full Text Available Purpose: To develop a novel injectable strontium-containing calcium phosphate cement with collagen. Methods: A novel calcium phosphate bone cement (CPC was prepared with the addition of strontium element, collagenⅠ, and modified starch; the injectability, solidification time, microstructure, phase composition, compressive strength, anti-collapsibility and histological properties of material were evaluated. Results: The results showed that the material could be injected with an excellent performance; the modified starch significantly improved the anti-washout property of cement; with the liquid to solid ratio of 0.3, the largest compressive strength of cement was obtained (48.0 MPa ± 2.3 MPa; histological examination of repair tissue showed that the bone was repaired after 16 weeks; the degradation of cement was consistent with the new bone growth. Conclusion: A novel injectable collagen-strontium-containing CPC with excellent compressive strength and suitable setting time was prepared, with addition of modified starch. The CPC showed a good antiwashout property and the degradation time of the cement met with the new bone growing. This material is supposed to be used in orthopedic and maxillofacial surgery for bone defects.

  6. Chapter 9: Model Systems for Formation and Dissolution of Calcium Phosphate Minerals

    Energy Technology Data Exchange (ETDEWEB)

    Orme, C A; Giocondi, J L

    2006-07-29

    Calcium phosphates are the mineral component of bones and teeth. As such there is great interest in understanding the physical mechanisms that underlie their growth, dissolution, and phase stability. Control is often achieved at the cellular level by the manipulation of solution states and the use of crystal growth modulators such as peptides or other organic molecules. This chapter begins with a discussion of solution speciation in body fluids and relates this to important crystal growth parameters such as the supersaturation, pH, ionic strength and the ratio of calcium to phosphate activities. We then discuss the use of scanning probe microscopy as a tool to measure surface kinetics of mineral surfaces evolving in simplified solutions. The two primary themes that we will touch on are the use of microenvironments that temporally evolve the solution state to control growth and dissolution; and the use of various growth modifiers that interact with the solution species or with mineral surfaces to shift growth away from the lowest energy facetted forms. The study of synthetic minerals in simplified solution lays the foundation for understand mineralization process in more complex environments found in the body.

  7. Mixed zirconia calcium phosphate coatings for dental implants: Tailoring coating stability and bioactivity potential

    Energy Technology Data Exchange (ETDEWEB)

    Pardun, Karoline [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany); Treccani, Laura, E-mail: treccani@uni-bremen.de [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany); Volkmann, Eike [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany); Streckbein, Philipp [University Hospital, Justus-Liebig-University Giessen, Department of Cranio-Maxillo-Facial Surgery, Klinikstrasse 33, 35385 Giessen (Germany); Heiss, Christian [University Hospital of Giessen-Marburg, Department of Trauma Surgery, Rudolf-Buchheim-Strasse 7, 35385 Giessen, Germany, (Germany); Laboratory of Experimental Surgery, Kerkraderstrasse 9, 35392 Giessen (Germany); Destri, Giovanni Li; Marletta, Giovanni [Laboratory for Molecular Surfaces and Nanotechnology (LAMSUN), Department of Chemistry, University of Catania and CSGI, Viale A. Doria 6, 95125 Catania (Italy); Rezwan, Kurosch [University of Bremen, Advanced Ceramics, Am Biologischen Garten 2, 28359 Bremen (Germany)

    2015-03-01

    Enhanced coating stability and adhesion are essential for long-term success of orthopedic and dental implants. In this study, the effect of coating composition on mechanical, physico-chemical and biological properties of coated zirconia specimens is investigated. Zirconia discs and dental screw implants are coated using the wet powder spraying (WPS) technique. The coatings are obtained by mixing yttria-stabilized zirconia (TZ) and hydroxyapatite (HA) in various ratios while a pure HA coating served as reference material. Scanning electron microscopy (SEM) and optical profilometer analysis confirm a similar coating morphology and roughness for all studied coatings, whereas the coating stability can be tailored with composition and is probed by insertion and dissections experiments in bovine bone with coated zirconia screw implants. An increasing content of calcium phosphate (CP) resulted in a decrease of mechanical and chemical stability, while the bioactivity increased in simulated body fluid (SBF). In vitro experiments with human osteoblast cells (HOB) revealed that the cells grew well on all samples but are affected by dissolution behavior of the studied coatings. This work demonstrates the overall good mechanical strength, the excellent interfacial bonding and the bioactivity potential of coatings with higher TZ contents, which provide a highly interesting coating for dental implants. - Highlights: • Different ratios of zirconia (TZ) and calcium phosphate (CP) were deposited on zirconia substrates. • Enhancement of TZ content in mixed coatings increased coating stability. • Enhancement of CP content in mixed coatings increased bioactivity. • All tested coating compositions were non-toxic.

  8. Design and characterization of calcium phosphate ceramic scaffolds for bone tissue engineering.

    Science.gov (United States)

    Denry, Isabelle; Kuhn, Liisa T

    2016-01-01

    Our goal is to review design strategies for the fabrication of calcium phosphate ceramic scaffolds (CPS), in light of their transient role in bone tissue engineering and associated requirements for effective bone regeneration. We examine the various design options available to meet mechanical and biological requirements of CPS and later focus on the importance of proper characterization of CPS in terms of architecture, mechanical properties and time-sensitive properties such as biodegradability. Finally, relationships between in vitro versus in vivo testing are addressed, with an attempt to highlight reliable performance predictors. A combinatory design strategy should be used with CPS, taking into consideration 3D architecture, adequate surface chemistry and topography, all of which are needed to promote bone formation. CPS represent the media of choice for delivery of osteogenic factors and anti-infectives. Non-osteoblast mediated mineral deposition can confound in vitro osteogenesis testing of CPS and therefore the expression of a variety of proteins or genes including collagen type I, bone sialoprotein and osteocalcin should be confirmed in addition to increased mineral content. CPS are a superior scaffold material for bone regeneration because they actively promote osteogenesis. Biodegradability of CPS via calcium and phosphate release represents a unique asset. Structural control of CPS at the macro, micro and nanoscale and their combination with cells and polymeric materials is likely to lead to significant developments in bone tissue engineering. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  9. Water-Soluble Cellulose Derivatives Are Sustainable Additives for Biomimetic Calcium Phosphate Mineralization

    Directory of Open Access Journals (Sweden)

    Andreas Taubert

    2016-10-01

    Full Text Available The effect of cellulose-based polyelectrolytes on biomimetic calcium phosphate mineralization is described. Three cellulose derivatives, a polyanion, a polycation, and a polyzwitterion were used as additives. Scanning electron microscopy, X-ray diffraction, IR and Raman spectroscopy show that, depending on the composition of the starting solution, hydroxyapatite or brushite precipitates form. Infrared and Raman spectroscopy also show that significant amounts of nitrate ions are incorporated in the precipitates. Energy dispersive X-ray spectroscopy shows that the Ca/P ratio varies throughout the samples and resembles that of other bioinspired calcium phosphate hybrid materials. Elemental analysis shows that the carbon (i.e., polymer contents reach 10% in some samples, clearly illustrating the formation of a true hybrid material. Overall, the data indicate that a higher polymer concentration in the reaction mixture favors the formation of polymer-enriched materials, while lower polymer concentrations or high precursor concentrations favor the formation of products that are closely related to the control samples precipitated in the absence of polymer. The results thus highlight the potential of (water-soluble cellulose derivatives for the synthesis and design of bioinspired and bio-based hybrid materials.

  10. Biomimetic nanoparticles with polynucleotide and PEG mixed-monolayers enhance calcium phosphate mineralization

    Science.gov (United States)

    Vasconcellos, Kayla B.; McHugh, Sean M.; Dapsis, Katherine J.; Petty, Alexander R.; Gerdon, Aren E.

    2013-09-01

    Biomineralization of hydroxyapatite (Ca10(PO4)6(OH)2) is of significant importance in biomedical applications such as bone and dental repair, and biomimetic control of mineral formation may lead to more effective restorative procedures. Gold nanoparticles are functional scaffolds on which to assemble multi-component monolayers capable of mimicking protein activity in the templated synthesis of calcium phosphate. The goal of this research was to explore nanoparticle templates with mixed-monolayers of uncharged polar polyethylene glycol (PEG) molecules and highly charged polynucleotide and amino acid molecules in their ability to influence mineralization rates and mineral particle size and morphology. This research demonstrates through time-resolved optical density and dynamic light scattering measurements that the combination of tiopronin, PEG, and DNA presented on a nanoparticle surface decreases nanoparticle aggregation from 59 to 21 nm solvated radius, increases mineralization kinetics from 1.5 × 10-3 to 3.1 × 10-3 OD/min, and decreases mineral particle size from 685 to 442 nm average radius. FT-IR and TEM data demonstrate that mineralized material, while initially amorphous, transforms to a semi-crystalline material when guided by template interactions. This demonstrates that surface-tailored monolayer protected cluster scaffolds are successful and controllable mineralization templates with further potential for biomedical applications involving calcium phosphate and other biomaterials.

  11. Preparation, Physical-Chemical Characterization, and Cytocompatibility of Polymeric Calcium Phosphate Cements

    Directory of Open Access Journals (Sweden)

    Rania M. Khashaba

    2011-01-01

    Full Text Available Aim. Physicochemical mechanical and in vitro biological properties of novel formulations of polymeric calcium phosphate cements (CPCs were investigated. Methods. Monocalcium phosphate, calcium oxide, and synthetic hydroxyapatite were combined with either modified polyacrylic acid, light activated polyalkenoic acid, or polymethyl vinyl ether maleic acid to obtain Types I, II, and III CPCs. Setting time, compressive and diametral strength of CPCs was compared with zinc polycarboxylate cement (control. Specimens were characterized using X-ray diffraction, scanning electron microscopy, and infrared spectroscopy. In vitro cytotoxicity of CPCs and control was assessed. Results. X-ray diffraction analysis showed hydroxyapatite, monetite, and brushite. Acid-base reaction was confirmed by the appearance of stretching peaks in IR spectra of set cements. SEM revealed rod-like crystals and platy crystals. Setting time of cements was 5–12 min. Type III showed significantly higher strength values compared to control. Type III yielded high biocompatibility. Conclusions. Type III CPCs show promise for dental applications.

  12. Obtain ceramic porous alumina-zirconia by replica method calcium phosphate coated

    International Nuclear Information System (INIS)

    Silva, A.D.R.; Rigoli, W.R.; Osiro, Denise; Pallone, E.M.J.A.

    2016-01-01

    Biomaterials used in bone replacement, including porous bioceramics, are often used as support structure for bone formation and repair. The porous bioceramics are used because present features as biocompatibility, high porosity and pore morphology that confer adequate mechanical strength and induce bone growth. In this work were obtained porous specimens of alumina containing 5% by inclusion of volume of zirconia produced by the replica method. The porous specimens had its surface chemically treated with phosphoric acid and were coated with calcium phosphate. The coating was performed using the biomimetic method during 14 days and an initial pH of 6.1. The porous specimens were characterized using the follow techniques: porosity, axial compression tests, microtomography, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD) and pH measurements SBF solution. The results showed specimens with suitable pore morphology for application as biomaterial, and even a reduced time of incubation favored the calcium phosphate phases formation on the material surfaces. (author)

  13. A new synthetic granular calcium phosphate compound induces new bone in a sinus lift rabbit model.

    Science.gov (United States)

    Trbakovic, Amela; Hedenqvist, Patricia; Mellgren, Torbjörn; Ley, Cecilia; Hilborn, Jöns; Ossipov, Dmitri; Ekman, Stina; Johansson, Carina B; Jensen-Waern, Marianne; Thor, Andreas

    2018-03-01

    The aim of this study was to investigate if a synthetic granular calcium phosphate compound (CPC) and a composite bisphosphonate-linked hyaluronic acid-calcium phosphate hydrogel (HABP·CaP) induced similar or more amount of bone as bovine mineral in a modified sinus lift rabbit model. Eighteen adult male New Zeeland White rabbits, received randomly one of the two test materials on a random side of the face, and bovine mineral as control on the contralateral side. In a sinus lift, the sinus mucosa was elevated and a titanium mini-implant was placed in the alveolar bone. Augmentation material (CPC, HABP·CaP or bovine bone) was applied in the space around the implant. The rabbits were euthanized three months after surgery and qualitative and histomorphometric evaluation were conducted. Histomorphometric evaluation included three different regions of interest (ROIs) and the bone to implant contact on each installed implant. Qualitative assessment (p = <.05), histomorphometric evaluations (p = < .01), and implant incorporation (p = <.05) showed that CPC and bovine mineral induced similar amount of bone and more than the HABP·CaP hydrogel. CPC induced similar amount of bone as bovine mineral and both materials induced more bone than HABP·CaP hydrogel. The CPC is suggested as a synthetic alternative for augmentations in the maxillofacial area. Copyright © 2017 Elsevier Ltd. All rights reserved.

  14. Uptake of the proteins HTRA1 and HTRA2 by cells mediated by calcium phosphate nanoparticles

    Directory of Open Access Journals (Sweden)

    Olga Rotan

    2017-02-01

    Full Text Available The efficient intracellular delivery of (biomolecules into living cells remains a challenge in biomedicine. Many biomolecules and synthetic drugs are not able to cross the cell membrane, which is a problem if an intracellular mode of action is desired, for example, with a nuclear receptor. Calcium phosphate nanoparticles can serve as carriers for small and large biomolecules as well as for synthetic compounds. The nanoparticles were prepared and colloidally stabilized with either polyethyleneimine (PEI; cationic nanoparticles or carboxymethyl cellulose (CMC; anionic nanoparticles and loaded with defined amounts of the fluorescently labelled proteins HTRA1, HTRA2, and BSA. The nanoparticles were purified by ultracentrifugation and characterized by dynamic light scattering and scanning electron microscopy. Various cell types (HeLa, MG-63, THP-1, and hMSC were incubated with fluorescently labelled proteins alone or with protein-loaded cationic and anionic nanoparticles. The cellular uptake was followed by light and fluorescence microscopy, confocal laser scanning microscopy (CLSM, and flow cytometry. All proteins were readily transported into the cells by cationic calcium phosphate nanoparticles. Notably, only HTRA1 was able to penetrate the cell membrane of MG-63 cells in dissolved form. However, the application of endocytosis inhibitors revealed that the uptake pathway was different for dissolved HTRA1 and HTRA1-loaded nanoparticles.

  15. Uptake of CrO{sub 4}{sup 2-} ions by Fe-treated tri-calcium phosphate

    Energy Technology Data Exchange (ETDEWEB)

    Serrano G, J.; Ramirez S, J. L.; Bonifacio M, J.; Granados C, F.; Badillo A, V. E., E-mail: juan.serrano@inin.gob.m [ININ, Carretera Mexico-Toluca s/n, 52750 Ocoyoacac, Estado de Mexico (Mexico)

    2010-07-01

    CrO{sub 4}{sup 2-} ion adsorption of Fe-treated tri-calcium phosphate was studied by batch experiments as a function of contact time, initial concentration of metal ion and temperature. Adsorption results showed that at ph 5.5 and 1.0 x 10{sup -4} M chromium concentration the adsorption capacity of Fe-treated tri-calcium phosphate for CrO{sub 4}{sup 2-} ions was 7.10 x 10{sup -3} mmol/g. Chromium adsorption data on Fe-treated tri-calcium phosphate at various initial concentration fitted the Freundlich isotherm. By temperature studies the thermodynamic parameters {Delta}H{sup 0}, {Delta}G{sup 0} and {Delta}S{sup 0} were estimated and the obtained results showed that the adsorption reaction was endothermic and spontaneous. (Author)

  16. Calcium-Phosphate-Osteopontin Particles Reduce Biofilm Formation and pH Drops in in situ-Grown Dental Biofilms

    DEFF Research Database (Denmark)

    Schlafer, Sebastian; Ibsen, Casper Jon Steenberg; Birkedal, Henrik

    2017-01-01

    This 2-period crossover study investigated the effect of calcium-phosphate-osteopontin particles on biofilm formation and pH in 48-h biofilms grown in situ. Bovine milk osteopontin is a highly phosphorylated glycoprotein that has been shown to interfere with bacterial adhesion to salivary......-coated surfaces. Calcium-phosphate-osteopontin particles have been shown to reduce biofilm formation and pH drops in a 5-species laboratory model of dental biofilm without affecting bacterial viability. Here, smooth surface biofilms from 10 individuals were treated ex vivo 6 times/day for 30 min with either...... calcium-phosphate-osteopontin particles or sterile saline. After growth, the amount of biofilm formed was determined by confocal microscopy, and pH drops upon exposure to glucose were monitored using confocal-microscopy-based pH ratiometry. A total of 160 biofilms were analysed. No adverse effects...

  17. Topography of calcium phosphate ceramics regulates primary cilia length and TGF receptor recruitment associated with osteogenesis.

    Science.gov (United States)

    Zhang, Jingwei; Dalbay, Melis T; Luo, Xiaoman; Vrij, Erik; Barbieri, Davide; Moroni, Lorenzo; de Bruijn, Joost D; van Blitterswijk, Clemens A; Chapple, J Paul; Knight, Martin M; Yuan, Huipin

    2017-07-15

    The surface topography of synthetic biomaterials is known to play a role in material-driven osteogenesis. Recent studies show that TGFβ signalling also initiates osteogenic differentiation. TGFβ signalling requires the recruitment of TGFβ receptors (TGFβR) to the primary cilia. In this study, we hypothesize that the surface topography of calcium phosphate ceramics regulates stem cell morphology, primary cilia structure and TGFβR recruitment to the cilium associated with osteogenic differentiation. We developed a 2D system using two types of tricalcium phosphate (TCP) ceramic discs with identical chemistry. One sample had a surface topography at micron-scale (TCP-B, with a bigger surface structure dimension) whilst the other had a surface topography at submicron scale (TCP-S, with a smaller surface structure dimension). In the absence of osteogenic differentiation factors, human bone marrow stromal cells (hBMSCs) were more spread on TCP-S than on TCP-B with alterations in actin organization and increased primary cilia prevalence and length. The cilia elongation on TCP-S was similar to that observed on glass in the presence of osteogenic media and was followed by recruitment of transforming growth factor-β RII (p-TGFβ RII) to the cilia axoneme. This was associated with enhanced osteogenic differentiation of hBMSCs on TCP-S, as shown by alkaline phosphatase activity and gene expression for key osteogenic markers in the absence of additional osteogenic growth factors. Similarly, in vivo after a 12-week intramuscular implantation in dogs, TCP-S induced bone formation while TCP-B did not. It is most likely that the surface topography of calcium phosphate ceramics regulates primary cilia length and ciliary recruitment of p-TGFβ RII associated with osteogenesis and bone formation. This bioengineering control of osteogenesis via primary cilia modulation may represent a new type of biomaterial-based ciliotherapy for orthopedic, dental and maxillofacial surgery

  18. Short-term in vivo evaluation of zinc-containing calcium phosphate using a normalized procedure

    Energy Technology Data Exchange (ETDEWEB)

    Calasans-Maia, Monica, E-mail: monicacalasansmaia@gmail.com [Dental Clinical Research Center, Dentistry School, Fluminense Federal University, Niteroi, Rio de Janeiro (Brazil); Calasans-Maia, José, E-mail: josecalasans@gmail.com [Dental Clinical Research Center, Dentistry School, Fluminense Federal University, Niteroi, Rio de Janeiro (Brazil); Santos, Silvia, E-mail: silviaquimica@gmail.com [LABIOMAT, Brazilian Center for Physics Research, CBPF, Rio de Janeiro (Brazil); Mavropoulos, Elena, E-mail: elena@cbpf.br [LABIOMAT, Brazilian Center for Physics Research, CBPF, Rio de Janeiro (Brazil); Farina, Marcos, E-mail: mfarina@anato.ufrj.br [Institute of Biomedical Sciences, Federal University of Rio de Janeiro, Rio de Janeiro (Brazil); Lima, Inayá, E-mail: inayacorrea@gmail.com [Nuclear Instrumentation Laboratory, Nuclear Engineering Program, COPPE, Federal University of Rio de Janeiro, Rio de Janeiro (Brazil); Lopes, Ricardo Tadeu [Nuclear Instrumentation Laboratory, Nuclear Engineering Program, COPPE, Federal University of Rio de Janeiro, Rio de Janeiro (Brazil); Rossi, Alexandre, E-mail: rossi@cbpf.br [LABIOMAT, Brazilian Center for Physics Research, CBPF, Rio de Janeiro (Brazil); Granjeiro, José Mauro, E-mail: jmgranjeiro@gmail.com [Dental Clinical Research Center, Dentistry School, Fluminense Federal University, Niteroi, Rio de Janeiro (Brazil); Bioengineering Division, National Institute of Metrology, Quality and Technology, Duque de Caxias, Rio de Janeiro (Brazil)

    2014-08-01

    The effect of zinc-substituted calcium phosphate (CaP) on bone osteogenesis was evaluated using an in vivo normalized ISO 10993-6 protocol. Zinc-containing hydroxyapatite (ZnHA) powder with 0.3% by wt zinc (experimental group) and stoichiometric hydroxyapatite (control group) were shaped into cylindrical implants (2 × 6 mm) and were sintered at 1000 °C. Thermal treatment transformed the ZnHA cylinder into a biphasic implant that was composed of Zn-substituted HA and Zn-substituted β-tricalcium phosphate (ZnHA/βZnTCP); the hydroxyapatite cylinder was a highly crystalline and poorly soluble HA implant. In vivo tests were performed in New Zealand White rabbits by implanting two cylinders of ZnHA/βZnTCP in the left tibia and two cylinders of HA in the right tibia for 7, 14 and 28 days. Incorporation of 0.3% by wt zinc into CaP increased the rate of Zn release to the biological medium. Microfluorescence analyses (μXRF-SR) using synchrotron radiation suggested that some of the Zn released from the biomaterial was incorporated into new bone near the implanted region. In contrast with previous studies, histomorphometric analysis did not show significant differences between the newly formed bone around ZnHA/βZnTCP and HA due to the dissolution profile of Zn-doped CaP. Despite the great potential of Zn-containing CaP matrices for future use in bone regeneration, additional in vivo studies must be conducted to explain the mobility of zinc at the CaP surface and its interactions with a biological medium. - Highlights: • We produced a hydroxyapatite containing a low concentration (0.3 wt.%) of zinc. • The biomaterial underwent characterization before and after in vivo implant. • In vivo tests were performed according to ISO 10993-6. • Zinc-containing calcium phosphate promotes osteoconduction and bone regeneration. • Zinc-containing calcium phosphate may be useful for clinical applications.

  19. Short-term in vivo evaluation of zinc-containing calcium phosphate using a normalized procedure

    International Nuclear Information System (INIS)

    Calasans-Maia, Monica; Calasans-Maia, José; Santos, Silvia; Mavropoulos, Elena; Farina, Marcos; Lima, Inayá; Lopes, Ricardo Tadeu; Rossi, Alexandre; Granjeiro, José Mauro

    2014-01-01

    The effect of zinc-substituted calcium phosphate (CaP) on bone osteogenesis was evaluated using an in vivo normalized ISO 10993-6 protocol. Zinc-containing hydroxyapatite (ZnHA) powder with 0.3% by wt zinc (experimental group) and stoichiometric hydroxyapatite (control group) were shaped into cylindrical implants (2 × 6 mm) and were sintered at 1000 °C. Thermal treatment transformed the ZnHA cylinder into a biphasic implant that was composed of Zn-substituted HA and Zn-substituted β-tricalcium phosphate (ZnHA/βZnTCP); the hydroxyapatite cylinder was a highly crystalline and poorly soluble HA implant. In vivo tests were performed in New Zealand White rabbits by implanting two cylinders of ZnHA/βZnTCP in the left tibia and two cylinders of HA in the right tibia for 7, 14 and 28 days. Incorporation of 0.3% by wt zinc into CaP increased the rate of Zn release to the biological medium. Microfluorescence analyses (μXRF-SR) using synchrotron radiation suggested that some of the Zn released from the biomaterial was incorporated into new bone near the implanted region. In contrast with previous studies, histomorphometric analysis did not show significant differences between the newly formed bone around ZnHA/βZnTCP and HA due to the dissolution profile of Zn-doped CaP. Despite the great potential of Zn-containing CaP matrices for future use in bone regeneration, additional in vivo studies must be conducted to explain the mobility of zinc at the CaP surface and its interactions with a biological medium. - Highlights: • We produced a hydroxyapatite containing a low concentration (0.3 wt.%) of zinc. • The biomaterial underwent characterization before and after in vivo implant. • In vivo tests were performed according to ISO 10993-6. • Zinc-containing calcium phosphate promotes osteoconduction and bone regeneration. • Zinc-containing calcium phosphate may be useful for clinical applications

  20. Influence of surface microstructure and chemistry on osteoinduction and osteoclastogenesis by biphasic calcium phosphate discs

    Directory of Open Access Journals (Sweden)

    NL Davison

    2015-06-01

    Full Text Available It has been reported that surface microstructural dimensions can influence the osteoinductivity of calcium phosphates (CaPs, and osteoclasts may play a role in this process. We hypothesised that surface structural dimensions of ≤ 1 μm trigger osteoinduction and osteoclast formation irrespective of macrostructure (e.g., concavities, interconnected macropores, interparticle space or surface chemistry. To test this, planar discs made of biphasic calcium phosphate (BCP: 80 % hydroxyapatite, 20 % tricalcium phosphate were prepared with different surface structural dimensions – either ~ 1 μm (BCP1150 or ~ 2-4 μm (BCP1300 – and no macropores or concavities. A third material was made by sputter coating BCP1150 with titanium (BCP1150Ti, thereby changing its surface chemistry but preserving its surface structure and chemical reactivity. After intramuscular implantation in 5 dogs for 12 weeks, BCP1150 formed ectopic bone in 4 out of 5 samples, BCP1150Ti formed ectopic bone in 3 out of 5 samples, and BCP1300 formed no ectopic bone in any of the 5 samples. In vivo, large multinucleated osteoclast-like cells densely colonised BCP1150, smaller osteoclast-like cells formed on BCP1150Ti, and osteoclast-like cells scarcely formed on BCP1300. In vitro, RAW264.7 cells cultured on the surface of BCP1150 and BCP1150Ti in the presence of osteoclast differentiation factor RANKL (receptor activator for NF-κB ligand proliferated then differentiated into multinucleated osteoclast-like cells with positive tartrate resistant acid phosphatase (TRAP activity. However, cell proliferation, fusion, and TRAP activity were all significantly inhibited on BCP1300. These results indicate that of the material parameters tested – namely, surface microstructure, macrostructure, and surface chemistry – microstructural dimensions are critical in promoting osteoclastogenesis and triggering ectopic bone formation.

  1. Porous hydroxyapatite and biphasic calcium phosphate ceramics promote ectopic osteoblast differentiation from mesenchymal stem cells

    Energy Technology Data Exchange (ETDEWEB)

    Zhang Lingli; Fan Hongsong; Zhang Xingdong [National Engineering Research Center for Biomaterials, Sichuan University, Chengdu, Sichuan 610064 (China); Hanagata, Nobutaka; Ikoma, Toshiyuki [Biomaterials Center, National Institute for Materials Science, Tsukuba, Ibaraki 305-0047 (Japan); Maeda, Megumi; Minowa, Takashi, E-mail: HANAGATA.Nobutaka@nims.go.j [Nanotechnology Innovation Center, National Institute for Materials Science, Tsukuba, Ibaraki 305-0047 (Japan)

    2009-04-15

    Because calcium phosphate (Ca-P) ceramics have been used as bone substitutes, it is necessary to investigate what effects the ceramics have on osteoblast maturation. We prepared three types of Ca-P ceramics with different Ca-P ratios, i.e. hydroxyapatite (HA), beta-tricalcium phosphate ({beta}-TCP), and biphasic calcium phosphate (BCP) ceramics with dense-smooth and porous structures. Comprehensive gene expression microarray analysis of mouse osteoblast-like cells cultured on these ceramics revealed that porous Ca-P ceramics considerably affected the gene expression profiles, having a higher potential for osteoblast maturation. In the in vivo study that followed, porous Ca-P ceramics were implanted into rat skeletal muscle. Sixteen weeks after the implantation, more alkaline-phosphatase-positive cells were observed in the pores of hydroxyapatite and BCP, and the expression of the osteocalcin gene (an osteoblast-specific marker) in tissue grown in pores was also higher in hydroxyapatite and BCP than in {beta}-TCP. In the pores of any Ca-P ceramics, 16 weeks after the implantation, we detected the expressions of marker genes of the early differentiation stage of chondrocytes and the complete differentiation stage of adipocytes, which originate from mesenchymal stem cells, as well as osteoblasts. These marker gene expressions were not observed in the muscle tissue surrounding the implanted Ca-P ceramics. These observations indicate that porous hydroxyapatite and BCP had a greater potential for promoting the differentiation of mesenchymal stem cells into osteoblasts than {beta}-TCP.

  2. A New Type of Biphasic Calcium Phosphate Cement as a Gentamicin Carrier for Osteomyelitis

    Directory of Open Access Journals (Sweden)

    Wen-Yu Su

    2013-01-01

    Full Text Available Osteomyelitis therapy is a long-term and inconvenient procedure for a patient. Antibiotic-loaded bone cements are both a complementary and alternative treatment option to intravenous antibiotic therapy for the treatment of osteomyelitis. In the current study, the biphasic calcium phosphate cement (CPC, called α-TCP/HAP (α-tricalcium phosphate/hydroxyapatite biphasic cement, was prepared as an antibiotics carrier for osteomyelitis. The developed biphasic cement with a microstructure of α-TCP surrounding the HAP has a fast setting time which will fulfill the clinical demand. The X-ray diffraction and Fourier transform infrared spectrometry analyses showed the final phase to be HAP, the basic bone mineral, after setting for a period of time. Scanning electron microscopy revealed a porous structure with particle sizes of a few micrometers. The addition of gentamicin in α-TCP/HAP would delay the transition of α-TCP but would not change the final-phase HAP. The gentamicin-loaded α-TCP/HAP supplies high doses of the antibiotic during the initial 24 hours when they are soaked in phosphate buffer solution (PBS. Thereafter, a slower drug release is produced, supplying minimum inhibitory concentration until the end of the experiment (30 days. Studies of growth inhibition of Staphylococcus aureus and Pseudomonas aeruginosa in culture indicated that gentamicin released after 30 days from α-TCP/HAP biphasic cement retained antibacterial activity.

  3. Continuous cellularization of calcium phosphate hybrid scaffolds induced by plasma polymer activation

    International Nuclear Information System (INIS)

    Bergemann, Claudia; Cornelsen, Matthias; Quade, Antje; Laube, Thorsten; Schnabelrauch, Matthias; Rebl, Henrike; Weißmann, Volker; Seitz, Hermann; Nebe, Barbara

    2016-01-01

    The generation of hybrid materials based on β-tricalcium phosphate (TCP) and various biodegradable polymers like poly(L-lactide-co-D,L-lactide) (PLA) represents a common approach to overcoming the disadvantages of pure TCP devices. These disadvantages lie in TCP's mechanical properties, such as brittleness. The positive characteristic of PLA — improvement of compressive strength of calcium phosphate scaffolds – is diametrically opposed to its cell attractiveness. Therefore, the objective of this work was to optimize osteoblast migration and cellularization inside a three-dimensionally (3D) printed, PLA polymer stabilized TCP hybrid scaffold by a plasma polymer process depositing amino groups via allylamine. MG-63 osteoblastic cells inside the 10 mm hybrid scaffold were dynamically cultivated for 14 days in a 3D model system integrated in a perfusion reactor. The whole TCP/PLA hybrid scaffold was continuously colonized due to plasma polymerized allylamine activation inducing the migration potential of osteoblasts. - Highlights: • Mechanical stabilization of β-tricalcium phosphate scaffolds by PLA infiltration • Hybrid scaffolds with higher cell attraction due to plasma polymerized allylamine • 3D perfusion in vitro model for observation of cell migration inside scaffolds • Enhanced cell migration within plasma polymer coated TCP hybrid scaffolds

  4. Continuous cellularization of calcium phosphate hybrid scaffolds induced by plasma polymer activation

    Energy Technology Data Exchange (ETDEWEB)

    Bergemann, Claudia [University Medical Center Rostock, Cell Biology, Schillingallee 69, D-18057 Rostock (Germany); Cornelsen, Matthias [University of Rostock, Fluid Technology and Microfluidics, Justus-von-Liebig Weg 6, D-18059 Rostock (Germany); Quade, Antje [Leibniz-Institute for Plasma Science and Technology (INP), Felix-Hausdorff-Str. 2, D-17489 Greifswald (Germany); Laube, Thorsten; Schnabelrauch, Matthias [INNOVENT e.V., Biomaterials Department, Pruessingstrasse 27B, D-07745 Jena (Germany); Rebl, Henrike [University Medical Center Rostock, Cell Biology, Schillingallee 69, D-18057 Rostock (Germany); Weißmann, Volker [Institute for Polymer Technologies (IPT) e.V., Alter Holzhafen 19, D-23966 Wismar (Germany); Seitz, Hermann [University of Rostock, Fluid Technology and Microfluidics, Justus-von-Liebig Weg 6, D-18059 Rostock (Germany); Nebe, Barbara, E-mail: barbara.nebe@med.uni-rostock.de [University Medical Center Rostock, Cell Biology, Schillingallee 69, D-18057 Rostock (Germany)

    2016-02-01

    The generation of hybrid materials based on β-tricalcium phosphate (TCP) and various biodegradable polymers like poly(L-lactide-co-D,L-lactide) (PLA) represents a common approach to overcoming the disadvantages of pure TCP devices. These disadvantages lie in TCP's mechanical properties, such as brittleness. The positive characteristic of PLA — improvement of compressive strength of calcium phosphate scaffolds – is diametrically opposed to its cell attractiveness. Therefore, the objective of this work was to optimize osteoblast migration and cellularization inside a three-dimensionally (3D) printed, PLA polymer stabilized TCP hybrid scaffold by a plasma polymer process depositing amino groups via allylamine. MG-63 osteoblastic cells inside the 10 mm hybrid scaffold were dynamically cultivated for 14 days in a 3D model system integrated in a perfusion reactor. The whole TCP/PLA hybrid scaffold was continuously colonized due to plasma polymerized allylamine activation inducing the migration potential of osteoblasts. - Highlights: • Mechanical stabilization of β-tricalcium phosphate scaffolds by PLA infiltration • Hybrid scaffolds with higher cell attraction due to plasma polymerized allylamine • 3D perfusion in vitro model for observation of cell migration inside scaffolds • Enhanced cell migration within plasma polymer coated TCP hybrid scaffolds.

  5. Development of novel strontium containing bioactive glass based calcium phosphate cement.

    Science.gov (United States)

    D'Onofrio, A; Kent, N W; Shahdad, S A; Hill, R G

    2016-06-01

    The aim of this study was to investigate the effect on properties of increasing strontium substitution for calcium in bioactive glasses used as precursors for novel calcium phosphate cements. Glasses were produced by progressively substituting strontium for calcium. Cements were prepared by mixing the glass powder with Ca(H2PO4)2 powder with a 2.5% solution of Na2HPO4. Setting times and compressive strength were measured after 1h, 1 day, 7 days and 28 days immersion in Tris buffer solution. X-ray diffraction (XRD), Fourier transform infrared spectroscopy and radiopacity were measured and crystal morphology was assessed using scanning electron microscopy. A correlation between the phases formed, morphology of the crystallites, setting time and compressive strength were analyzed. Setting time increased proportionally with strontium substitution in the glass up to 25%, whereas for higher substitutions it decreased. Compressive strength showed a maximum value of 12.5MPa and was strongly influenced by the interlocking of the crystals and their morphology. XRD showed that the presence of strontium influenced the crystal phases formed. Octacalcium phosphate (Ca8H2(PO4)6·5H2O, OCP) was the main phase present after 1h and 1 day whereas after 28 days OCP was completely transformed to strontium-containing hydroxyapatite (SrxCa(10-x)(PO4)6(OH)2, SrHA). Radiopacity increased proportionally to strontium substitution in the glass. A novel method to develop a bone substitute forming in vitro SrHA as a final product by using a bioactive glass as a precursor was shown. These novel injectable bioactive glass cements are promising materials for dental and orthopedic applications. Further in vivo characterizations are being conducted. Copyright © 2016 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  6. Ectopic bone formation in bone marrow stem cell seeded calcium phosphate scaffolds as compared to autograft and (cell seeded allograft

    Directory of Open Access Journals (Sweden)

    J O Eniwumide

    2007-08-01

    Full Text Available Improvements to current therapeutic strategies are needed for the treatment of skeletal defects. Bone tissue engineering offers potential advantages to these strategies. In this study, ectopic bone formation in a range of scaffolds was assessed. Vital autograft and devitalised allograft served as controls and the experimental groups comprised autologous bone marrow derived stem cell seeded allograft, biphasic calcium phosphate (BCP and tricalcium phosphate (TCP, respectively. All implants were implanted in the back muscle of adult Dutch milk goats for 12 weeks. Micro-computed tomography (µCT analysis and histomorphometry was performed to evaluate and quantify ectopic bone formation. In good agreement, both µCT and histomorphometric analysis demonstrated a significant increase in bone formation by cell-seeded calcium phosphate scaffolds as compared to the autograft, allograft and cell-seeded allograft implants. An extensive resorption of the autograft, allograft and cell-seeded allograft implants was observed by histology and confirmed by histomorphometry. Cell-seeded TCP implants also showed distinct signs of degradation with histomorphometry and µCT, while the degradation of the cell-seeded BCP implants was negligible. These results indicate that cell-seeded calcium phosphate scaffolds are superior to autograft, allograft or cell-seeded allograft in terms of bone formation at ectopic implantation sites. In addition, the usefulness of µCT for the efficient and non-destructive analysis of mineralised bone and calcium phosphate scaffold was demonstrated.

  7. Association of salivary calcium, phosphate, pH and flow rate on oral health: A study on 90 subjects.

    Science.gov (United States)

    Fiyaz, Mohamed; Ramesh, Amitha; Ramalingam, Karthikeyan; Thomas, Biju; Shetty, Sucheta; Prakash, Prashanth

    2013-07-01

    This study was designed to compare inorganic salivary calcium, phosphate, flow rate and pH of un-stimulated saliva and oral hygiene of healthy subjects, patients with periodontitis and dental caries and to correlate salivary calcium level with the number of intact teeth. The present study consisted of 90 patients aged between 18 and 55 years and were divided into three groups, periodontitis, dental caries and controls. Oral hygiene index-simplified, probing pocket depth, clinical attachment level and number of teeth present, teeth with active carious lesions were recorded. Salivary flow rate and pH was recorded and subjected to biochemical investigation. Estimation of inorganic calcium and phosphate was performed by colorimetric method. Results showed statistically significant increase in salivary inorganic calcium and phosphate levels, poor oral hygiene status, pH and salivary flow rate in patients with periodontitis when compared with dental caries group and controls. Individuals who have increased salivary inorganic calcium, phosphate, pH, flow rate and maintain poor oral hygiene could be at a higher risk for developing periodontitis and may have less dental caries and more number of intact teeth.

  8. Assessment of salivary calcium, phosphate, magnesium, pH, and flow rate in healthy subjects, periodontitis, and dental caries.

    Science.gov (United States)

    Rajesh, K S; Zareena; Hegde, Shashikanth; Arun Kumar, M S

    2015-01-01

    This study was conducted to estimate and compare inorganic salivary calcium, phosphate, magnesium, salivary flow rate, and pH of unstimulated saliva and oral hygiene status of healthy subjects, subjects with periodontitis and dental caries, and to correlate salivary calcium level with number of intact teeth. The study population consisted of 48 systemically healthy subjects in the age group of 18-55 years, which was further divided into three groups: healthy, periodontitis, and dental caries. Oral hygiene index-simplified, probing pocket depth, clinical attachment level, the number of intact teeth, and active carious lesions were recorded. Estimation of inorganic salivary calcium, phosphate, and magnesium was performed spectrophotometrically using Vitros 5.1 FS. Statistical analysis was performed using the one-way analysis of variance test at 5% significance level. There was a statistically significant increase in inorganic salivary calcium, phosphate, pH, flow rate, and poor oral hygiene status in periodontitis group compared to dental caries and healthy group. Subjects with increased inorganic salivary calcium, phosphate, pH, flow rate, and poor oral hygiene are at a higher risk of developing periodontitis. Since there is increased remineralization potential, these subjects have more number of intact teeth compared to the dental caries group.

  9. Assessment of salivary calcium, phosphate, magnesium, pH, and flow rate in healthy subjects, periodontitis, and dental caries

    Directory of Open Access Journals (Sweden)

    K S Rajesh

    2015-01-01

    Full Text Available Aim: This study was conducted to estimate and compare inorganic salivary calcium, phosphate, magnesium, salivary flow rate, and pH of unstimulated saliva and oral hygiene status of healthy subjects, subjects with periodontitis and dental caries, and to correlate salivary calcium level with number of intact teeth. Materials and Methods: The study population consisted of 48 systemically healthy subjects in the age group of 18-55 years, which was further divided into three groups: healthy, periodontitis, and dental caries. Oral hygiene index-simplified, probing pocket depth, clinical attachment level, the number of intact teeth, and active carious lesions were recorded. Estimation of inorganic salivary calcium, phosphate, and magnesium was performed spectrophotometrically using Vitros 5.1 FS. Statistical analysis was performed using the one-way analysis of variance test at 5% significance level. Results: There was a statistically significant increase in inorganic salivary calcium, phosphate, pH, flow rate, and poor oral hygiene status in periodontitis group compared to dental caries and healthy group. Conclusion: Subjects with increased inorganic salivary calcium, phosphate, pH, flow rate, and poor oral hygiene are at a higher risk of developing periodontitis. Since there is increased remineralization potential, these subjects have more number of intact teeth compared to the dental caries group.

  10. Enhancement of biodegradation and osseointegration of poly(ε-caprolactone)/calcium phosphate ceramic composite screws for osteofixation using calcium sulfate.

    Science.gov (United States)

    Wu, Chang-Chin; Hsu, Li-Ho; Tsai, Yuh-Feng; Sumi, Shoichiro; Yang, Kai-Chiang

    2016-04-04

    Internal fixation devices, which can stabilize and realign fractured bone, are widely used in fracture management. In this paper, a biodegradable composite fixator, composed of poly(ε-caprolactone), calcium phosphate ceramic and calcium sulfate (PCL/CPC/CS), is developed. The composition of CS, which has a high dissolution rate, was expected to create a porous structure to improve osteofixation to the composite fixator. PCL, PCL/CPC, and PCL/CPC/CS samples were prepared and their physical properties were characterized in vitro. In vivo performance of the composite screws was verified in the distal femurs of rabbits. Results showed that the PCL/CPC/CS composite had a higher compressive strength (28.55 ± 3.32 MPa) in comparison with that of PCL (20.64 ± 1.81 MPa) (p < 0.05). A larger amount of apatite was formed on PCL/CPC/CS than on PCL/CPC, while no apatite was found on PCL after simulated body fluid immersion. In addition, PCL/CPC/CS composites also had a faster in vitro degradation rate (13.05 ± 3.42% in weight loss) relative to PCL (1.79 ± 0.23%) and PCL/CPC (4.32 ± 2.18%) (p < 0.001). In animal studies, PCL/CPC/CS screws showed a greater volume loss than that of PCL or PCL/CPC at 24 weeks post-implantation. Under micro-computerized tomography observation, animals with PCL/CPC/CS implants had better osseointegration in terms of the structural parameters of the distal metaphysis, including trabecular number, trabecular spacing, and connectivity density, than the PCL screw. This study reveals that the addition of CS accelerates the biodegradation and enhanced apatite formation of the PCL/CPC composite screw. This osteoconductive PCL/CPC/CS is a good candidate material for internal fixation devices.

  11. Osteogenic activity of cyclodextrin-encapsulated doxycycline in a calcium phosphate PCL and PLGA composite

    Energy Technology Data Exchange (ETDEWEB)

    Trajano, V.C.C.; Costa, K.J.R. [Restorative Dentistry Department, Faculty of Dentistry, Universidade Federal de Minas Gerais, Av. Antônio Carlos, 6627, CEP: 31270-901 Belo Horizonte, Minas Gerais (Brazil); Lanza, C.R.M. [Department of Oral Clinical, Surgery and Pathology, Faculty of Dentistry, Universidade Federal de Minas Gerais, Av. Antônio Carlos, 6627, CEP: 31270-901 Belo Horizonte, Minas Gerais (Brazil); Sinisterra, R.D. [Chemistry Department, ICEX, Universidade Federal de Minas Gerais, Av. Antônio Carlos, 6627, CEP: 31270-901 Belo Horizonte, Minas Gerais (Brazil); Cortés, M.E., E-mail: mecortes@ufmg.br [Restorative Dentistry Department, Faculty of Dentistry, Universidade Federal de Minas Gerais, Av. Antônio Carlos, 6627, CEP: 31270-901 Belo Horizonte, Minas Gerais (Brazil)

    2016-07-01

    Composites of biodegradable polymers and calcium phosphate are bioactive and flexible, and have been proposed for use in tissue engineering and bone regeneration. When associated with the broad-spectrum antibiotic doxycycline (DOX), they could favor antimicrobial action and enhance the action of osteogenic composites. Composites of polycaprolactone (PCL), poly(lactic-co-glycolic acid) (PLGA), and a bioceramic of biphasic calcium phosphate Osteosynt® (BCP) were loaded with DOX encapsulated in β-cyclodextrin (βCD) and were evaluated for effects on osteoblastic cell cultures. The DOX/βCD composite was prepared with a double mixing method. Osteoblast viability was assessed with methyl tetrazolium (MTT) assays after 1 day, 7 day, and 14 days of composite exposure; alkaline phosphatase (AP) activity and collagen production were evaluated after 7 days and 14 days, and mineral nodule formation after 14 days. Composite structures were evaluated by scanning electron microscopy (SEM). Osteoblasts exposed to the composite containing 25 μg/mL DOX/βCD had increased cell proliferation (p < 0.05) compared to control osteoblast cultures at all experimental time points, reaching a maximum in the second week. AP activity and collagen secretion levels were also elevated in osteoblasts exposed to the DOX/βCD composite (p < 0.05 vs. controls) and reached a maximum after 14 days. These results were corroborated by Von Kossa test results, which showed strong formation of mineralization nodules during the same time period. SEM of the composite material revealed a surface topography with pore sizes suitable for growing osteoblasts. Together, these results suggest that osteoblasts are viable, proliferative, and osteogenic in the presence of a DOX/βCD-containing BCP ceramic composite. - Highlights: • Doxycycline encapsulated in β-cyclodextrin was incorpored into a polycaprolactone - poly(lactic-co-glycolic acid) - calcium phosphate • Composite’s scaffold carrying doxycycline

  12. Calcium Phosphate as a Key Material for Socially Responsible Tissue Engineering

    Directory of Open Access Journals (Sweden)

    Vuk Uskoković

    2016-06-01

    Full Text Available Socially responsible technologies are designed while taking into consideration the socioeconomic, geopolitical and environmental limitations of regions in which they will be implemented. In the medical context, this involves making therapeutic platforms more accessible and affordable to patients in poor regions of the world wherein a given disease is endemic. This often necessitates going against the reigning trend of making therapeutic nanoparticles ever more structurally complex and expensive. However, studies aimed at simplifying materials and formulations while maintaining the functionality and therapeutic response of their more complex counterparts seldom provoke a significant interest in the scientific community. In this review we demonstrate that such compositional simplifications are meaningful when it comes to the design of a solution for osteomyelitis, a disease that is in its natural, non-postoperative form particularly prevalent in the underdeveloped parts of the world wherein poverty, poor sanitary conditions, and chronically compromised defense lines of the immune system are the norm. We show that calcium phosphate nanoparticles, which are inexpensive to make, could be chemically designed to possess the same functionality as a hypothetic mixture additionally composed of: (a a bone growth factor; (b an antibiotic for prophylactic or anti-infective purposes; (c a bisphosphonate as an antiresorptive compound; (d a viral vector to enable the intracellular delivery of therapeutics; (e a luminescent dye; (f a radiographic component; (g an imaging contrast agent; (h a magnetic domain; and (i polymers as viscous components enabling the injectability of the material and acting as carriers for the sustained release of a drug. In particular, calcium phosphates could: (a produce tunable drug release profiles; (b take the form of viscous and injectable, self-setting pastes; (c be naturally osteo-inductive and inhibitory for osteoclastogenesis

  13. The calcium phosphate coating of soy lecithin nanoemulsion with performance in stability and as an oxygen carrier

    Science.gov (United States)

    Han, Kyu B.

    This work studied the relationship between surfactant, oil, and water, by building ternary phase diagrams, the goal of which was to identify the oil-in-water phase composition. The resulting nano-sized emulsion was coated with dicalcium phosphate by utilizing the ionic affinity between calcium ions and the emulsion surface. Since the desired function of the particle is as an oxygen carrier, the particle stability, oxygen capacity, and oxygen release rate were investigated. The first step in the process was to construct ternary phase diagrams with 1,2-dioleoyl-sn-glycero-3-phosphate (DOPA) and soy derived lecithin. The results showed that the lecithin surfactant formed an oil-in-water phase region that was 36 times greater than that of DOPA. With the desired phase composition set, the lecithin emulsion was extruded, resulting in a well-dispersed nanosized particle. A pH titration study of the emulsion found an optimized calcium phosphate coating condition at pH 8.8, at which, the calcium ion had a greater affinity for the emulsion surface than phosphate. A Hill plot was used to show calcium cooperativeness on the emulsion surface which suggested one calcium ion binds to one lecithin molecule. The lecithin emulsion particles were then coated with calcium phosphate using a layering technique that allowed for careful control of the coating thickness. The overall particle hydrodynamic radius was consistent with the growth of the calcium phosphate coating, from 8 nm to 28 nm. This observation was further supported with cryo-TEM measurements. The stability of the coated emulsion was tested in conditions that simulate practical thermal, physical, and time-dependent conditions. Throughout the tests, the coated emulsion exhibited a constant mono-dispersed particle size, while the uncoated emulsion size fluctuated greatly and exhibited increased polydispersion. The fast mixing method with the stopped-flow apparatus was employed to test the product as an oxygen carrier, and it

  14. Synthesis and characterization of nanosized calcium phosphates by flame spray pyrolysis, and their effect on osteogenic differentiation of stem cells

    Energy Technology Data Exchange (ETDEWEB)

    Ataol, Sibel; Tezcaner, Ayşen [Middle East Technical University, Department of Biomedical Engineering (Turkey); Duygulu, Ozgur [TUBITAK Marmara Research Center, Materials Institute (Turkey); Keskin, Dilek [Middle East Technical University, Department of Biomedical Engineering (Turkey); Machin, Nesrin E., E-mail: nesrinmachin@gmail.com [Kocaeli University, Department of Chemical Engineering (Turkey)

    2015-02-15

    The present study evaluates the synthesis of biocompatible osteoconductive and osteoinductive nano calcium phosphate (CaP) particles by industrially applied, aerosol-derived flame spray pyrolysis method for biomedical field. Calcium phosphate nanoparticles were produced in a range of calcium-to-phosphorus ratio, (1.20–2.19) in order to analyze the morphology and crystallinity changes, and to test the bioactivity of particles. The characterization results confirmed that nanometer-sized, spherical calcium phosphate particles were produced. The average primary particle size was determined as 23 nm by counting more than 500 particles in TEM pictures. XRD patterns, HRTEM, SAED, and SEM analyses revealed the amorphous nature of the as-prepared nano calcium phosphate particles at low Ca/P ratios. Increases in the specific surface area and crystallinity were observed with the increasing Ca/P ratio. TGA–DTA analysis showed that the thermally stable crystal phases formed after 700 °C. Cell culture studies were conducted with urine-derived stem cells that possess the characteristics of mesenchymal stem cells. Synthesized amorphous nanoparticles did not have cytotoxic effect at 5–50 μg/ml concentration range. Cells treated with the as-prepared nanoparticles had higher alkaline phosphatase (ALP) enzyme activity than control cells, indicating osteogenic differentiation of cells. A slight decrease in ALP activity of cells treated with two highest Ca:P ratios at 50 μg/ml concentration was observed at day 7. The findings suggest that calcium phosphate nanoparticles produced in this work have a potential to be used as biomaterials in biomedical applications.

  15. Synthesis and characterization of nanosized calcium phosphates by flame spray pyrolysis, and their effect on osteogenic differentiation of stem cells

    Science.gov (United States)

    Ataol, Sibel; Tezcaner, Ayşen; Duygulu, Ozgur; Keskin, Dilek; Machin, Nesrin E.

    2015-02-01

    The present study evaluates the synthesis of biocompatible osteoconductive and osteoinductive nano calcium phosphate (CaP) particles by industrially applied, aerosol-derived flame spray pyrolysis method for biomedical field. Calcium phosphate nanoparticles were produced in a range of calcium-to-phosphorus ratio, (1.20-2.19) in order to analyze the morphology and crystallinity changes, and to test the bioactivity of particles. The characterization results confirmed that nanometer-sized, spherical calcium phosphate particles were produced. The average primary particle size was determined as 23 nm by counting more than 500 particles in TEM pictures. XRD patterns, HRTEM, SAED, and SEM analyses revealed the amorphous nature of the as-prepared nano calcium phosphate particles at low Ca/P ratios. Increases in the specific surface area and crystallinity were observed with the increasing Ca/P ratio. TGA-DTA analysis showed that the thermally stable crystal phases formed after 700 °C. Cell culture studies were conducted with urine-derived stem cells that possess the characteristics of mesenchymal stem cells. Synthesized amorphous nanoparticles did not have cytotoxic effect at 5-50 μg/ml concentration range. Cells treated with the as-prepared nanoparticles had higher alkaline phosphatase (ALP) enzyme activity than control cells, indicating osteogenic differentiation of cells. A slight decrease in ALP activity of cells treated with two highest Ca:P ratios at 50 μg/ml concentration was observed at day 7. The findings suggest that calcium phosphate nanoparticles produced in this work have a potential to be used as biomaterials in biomedical applications.

  16. Thermally stimulated luminescence and electron paramagnetic resonance studies on uranium doped calcium phosphate

    CERN Document Server

    Natarajan, V; Veeraraghavan, R; Sastry, M D

    2003-01-01

    Thermally stimulated luminescence (TSL) and electron paramagnetic resonance (EPR) studies on uranium doped calcium phosphate yielded mechanistic information on the observed glow peaks at 365, 410 and 450 K. TSL spectral studies of the glow peaks showed that UO sub 2 sup 2 sup + acts as the luminescent center. Electron paramagnetic resonance studies on gamma-irradiated samples revealed that the predominant radiation induced centers are H sup 0 , PO sub 4 sup 2 sup - , PO sub 3 sup 2 sup - and O sup - ion. Studies on the temperature dependence studies of the EPR spectra of samples annealed to different temperatures indicate the role of H sup 0 and PO sub 4 sup 2 sup - ions in the main glow peak at 410 K.

  17. Influence of calcium phosphate nanoparticles, Piriformospora indica and Glomus mosseae on growth of Zea mays

    International Nuclear Information System (INIS)

    Rane, Mansi; Bawskar, Manisha; Rathod, Dnyaneshwar; Nagaonkar, Dipali; Rai, Mahendra

    2015-01-01

    In this study, the arbuscular mycorrhizal fungus (G. mosseae) and endosymbiont (P. indica) colonized Zea mays were treated with calcium phosphate nanoparticles (CaPNPs) and evaluated for their plant growth promotion efficiency. It was observed that CaPNPs in combination with both G. mosseae and P. indica are more potent plant growth promoter than independent combinations of CaPNPs + G. mosseae, CaPNPs + P. indica or CaPNPs alone. The fluorimetric studies of treated plants revealed that CaPNPs alone and in combination with P. indica can enhance vitality of Zea mays by improving chlorophyll a content and performance index of treated plants. Hence, we conclude that CaPNPs exhibit synergistic growth promotion, root proliferation and vitality improvement properties along with endosymbiotic and arbuscular mycorrhizal fungi, which after further field trials can be developed as a cost-effective nanofertilizer with pronounced efficiency. (paper)

  18. Addition of 1, 2 and 3% in mass of sodium alginate in calcium phosphate cement

    International Nuclear Information System (INIS)

    Coelho, W.T.; Fernandes, J.M.; Vieira, R.S.; Thurmer, M.B.; Santos, L.A.

    2011-01-01

    The calcium phosphate cement (CFC) are bone substitutes with great potential for use in orthopedics, traumatology and dentistry because of their biocompatibility, bioactivity, osteoconductivity and osteotransdutivity, and a paste that can be easily molded and placed into the surgical site. However, CFCs have low mechanical strength, which equals the maximum mechanical strength of trabecular bone. Aiming to evaluate the strength and time to handle a CFC phase composed mainly of alpha were added to sodium alginate (1%, 2% and 3% wt) and an accelerator handle in an aqueous medium. The cement powder was mixed with liquid takes 2 minutes and resigned in specimens and assessed for apparent density and porosity by the Archimedes method, X-ray diffraction and mechanical strength. We noticed a significant increase in mechanical properties of cement added sodium alginate. (author)

  19. Polymer-Ceramic Composite Scaffolds: The Effect of Hydroxyapatite and β-tri-Calcium Phosphate

    Directory of Open Access Journals (Sweden)

    Boyang Huang

    2018-01-01

    Full Text Available The design of bioactive scaffolds with improved mechanical and biological properties is an important topic of research. This paper investigates the use of polymer-ceramic composite scaffolds for bone tissue engineering. Different ceramic materials (hydroxyapatite (HA and β-tri-calcium phosphate (TCP were mixed with poly-ε-caprolactone (PCL. Scaffolds with different material compositions were produced using an extrusion-based additive manufacturing system. The produced scaffolds were physically and chemically assessed, considering mechanical, wettability, scanning electron microscopy and thermal gravimetric tests. Cell viability, attachment and proliferation tests were performed using human adipose derived stem cells (hADSCs. Results show that scaffolds containing HA present better biological properties and TCP scaffolds present improved mechanical properties. It was also possible to observe that the addition of ceramic particles had no effect on the wettability of the scaffolds.

  20. 3D printing of mineral-polymer bone substitutes based on sodium alginate and calcium phosphate.

    Science.gov (United States)

    Egorov, Aleksey A; Fedotov, Alexander Yu; Mironov, Anton V; Komlev, Vladimir S; Popov, Vladimir K; Zobkov, Yury V

    2016-01-01

    We demonstrate a relatively simple route for three-dimensional (3D) printing of complex-shaped biocompatible structures based on sodium alginate and calcium phosphate (CP) for bone tissue engineering. The fabrication of 3D composite structures was performed through the synthesis of inorganic particles within a biopolymer macromolecular network during 3D printing process. The formation of a new CP phase was studied through X-ray diffraction, Fourier transform infrared spectroscopy and scanning electron microscopy. Both the phase composition and the diameter of the CP particles depend on the concentration of a liquid component (i.e., the "ink"). The 3D printed structures were fabricated and found to have large interconnected porous systems (mean diameter ≈800 μm) and were found to possess compressive strengths from 0.45 to 1.0 MPa. This new approach can be effectively applied for fabrication of biocompatible scaffolds for bone tissue engineering constructions.

  1. Polymer-Ceramic Composite Scaffolds: The Effect of Hydroxyapatite and β-tri-Calcium Phosphate.

    Science.gov (United States)

    Huang, Boyang; Caetano, Guilherme; Vyas, Cian; Blaker, Jonny James; Diver, Carl; Bártolo, Paulo

    2018-01-14

    The design of bioactive scaffolds with improved mechanical and biological properties is an important topic of research. This paper investigates the use of polymer-ceramic composite scaffolds for bone tissue engineering. Different ceramic materials (hydroxyapatite (HA) and β-tri-calcium phosphate (TCP)) were mixed with poly-ε-caprolactone (PCL). Scaffolds with different material compositions were produced using an extrusion-based additive manufacturing system. The produced scaffolds were physically and chemically assessed, considering mechanical, wettability, scanning electron microscopy and thermal gravimetric tests. Cell viability, attachment and proliferation tests were performed using human adipose derived stem cells (hADSCs). Results show that scaffolds containing HA present better biological properties and TCP scaffolds present improved mechanical properties. It was also possible to observe that the addition of ceramic particles had no effect on the wettability of the scaffolds.

  2. Evolution of the magnesium incorporated amorphous calcium phosphate to nano-crystallized hydroxyapatite in alkaline solution

    Science.gov (United States)

    Zhang, Xiao-Juan; Lin, Dong-Yang; Yan, Xiao-Hui; Wang, Xiao-Xiang

    2011-12-01

    A homogeneous amorphous calcium phosphate (ACP) coating containing magnesium was achieved on titanium substrates by electrochemical deposition (ECD). Its amorphous structure is confirmed by transmission electron microscope (TEM) together with grazing reflection absorption infrared spectroscopy (IR) spectrometer. In the images of high-resolution transmission electron microscope (HRTEM), the ACP spheres are assembled by nano-particles with the diameter of 5-10 nm. In the alkaline environment, nucleation of hydroxyapatite (HAP) occurs on the surfaces of ACP spheres. By consuming the Ca and PO 4 ions inside the ACP spheres, the HAP nuclei grow outward. Confirmed by TEM, the ACP spheres converse to hollow HAP spheres composed of HAP nano-needles. The coating is finally constructed by the HAP nano-needles, which are themselves aggregated by numerous nano-particles.

  3. Basic calcium phosphate crystal-induced Egr-1 expression stimulates mitogenesis in human fibroblasts

    International Nuclear Information System (INIS)

    Zeng, Xiao R.; Sun Yubo; Wenger, Leonor; Cheung, Herman S.

    2005-01-01

    Previously, we have reported that basic calcium phosphate (BCP) crystals stimulate mitogenesis and synthesis of matrix metalloproteinases in cultured human foreskin and synovial fibroblasts. However, the detailed mechanisms involved are still unclear. In the present study, using RT-PCR and Egr-1 promoter analysis we showed that BCP crystals could stimulate early growth response gene Egr-1 transcription through a PKCα-dependent p44/p42 MAPK pathway. Using a retrovirus gene expression system (Clontech) to overexpress Egr-1 in human fibroblast BJ-1 cells resulted in promotion of mitogenesis measured either by MTT cell proliferation analysis or by direct cell counting. The results demonstrate that Egr-1 may play a key role in mediating BCP crystal-induced synovial fibroblast mitogenesis

  4. Microstructure of yttric calcium phosphate bioceramic coatings synthesized by laser cladding

    Energy Technology Data Exchange (ETDEWEB)

    Wang Diangang [School of Materials Science and Engineering, Shandong University, Jinan 250061 (China); Chen Chuanzhong [School of Materials Science and Engineering, Shandong University, Jinan 250061 (China)]. E-mail: czchen@sdu.edu.cn; Ma Jie [School of Materials Science and Engineering, Shandong University, Jinan 250061 (China); Lei Tingquan [School of Materials Science and Engineering, Shandong University, Jinan 250061 (China); School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China)

    2007-02-15

    The yttric calcium phosphate (CaP) coatings were in situ prepared on pure titanium substrate by laser cladding. The morphologies and phases constitution of CaP coatings were studied by electron probe microanalysis, X-ray diffraction and so on. The bonding state between the coating and the substrate is fine metallurgical combination, and the addition of yttria can fine the structure and increase the tensile strength of the coatings. The X-ray result shows that the coating is composed of the phases of HA, {alpha}-Ca{sub 2}P{sub 2}O{sub 7}, {beta}-Ca{sub 2}P{sub 2}O{sub 7} and CaTiO{sub 3}.

  5. UV and X radiation effects on the stability of calcium halide phosphate phosphors. 1

    International Nuclear Information System (INIS)

    Tews, W.

    1983-01-01

    Intensity losses of several calcium halide phosphate phosphors have been investigated as a function of the time of irradiation with near UV and X radiation. The results show that antimony-containing foreign phases increase such losses. The directly excited manganese centre emission is much more lowered than the sensitized one. Detrimental effects of the 185 nm UV radiation are observable not only in the first minutes of irradiation but also over considerably extended periods. The sensitization effect caused by irradiation in different gases depends on the phosphor, especially on the content of antimony, and can be explained by the sorption of gaseous impurities at the phosphor surface so that the diffusion of photochemical reaction products from the surface is inhibited

  6. 3D printing of mineral–polymer bone substitutes based on sodium alginate and calcium phosphate

    Directory of Open Access Journals (Sweden)

    Aleksey A. Egorov

    2016-11-01

    Full Text Available We demonstrate a relatively simple route for three-dimensional (3D printing of complex-shaped biocompatible structures based on sodium alginate and calcium phosphate (CP for bone tissue engineering. The fabrication of 3D composite structures was performed through the synthesis of inorganic particles within a biopolymer macromolecular network during 3D printing process. The formation of a new CP phase was studied through X-ray diffraction, Fourier transform infrared spectroscopy and scanning electron microscopy. Both the phase composition and the diameter of the CP particles depend on the concentration of a liquid component (i.e., the “ink”. The 3D printed structures were fabricated and found to have large interconnected porous systems (mean diameter ≈800 μm and were found to possess compressive strengths from 0.45 to 1.0 MPa. This new approach can be effectively applied for fabrication of biocompatible scaffolds for bone tissue engineering constructions.

  7. Structural characterization and mechanical performance of calcium phosphate scaffolds and natural bones: a comparative study.

    Science.gov (United States)

    Fuentes, Elena; Sáenz de Viteri, Virginia; Igartua, Amaya; Martinetti, Roberta; Dolcini, Laura; Barandika, Gotzone

    2010-01-01

    The knowledge of the mechanical response of bones and their substitutes is pertinent to numerous medical problems. Understanding the effects of mechanical influence on the body is the first step toward developing innovative treatment and rehabilitation concepts for orthopedic disorders. This was a comparative study of 5 synthetic scaffolds based on porous calcium phosphates and natural bones, with regard to their microstructural, chemical, and mechanical characterizations. The structural and chemical characterizations of the scaffolds were examined by means of X-ray diffraction, scanning electron microscopy, and X-ray spectroscopy analysis. The mechanical characterization of bones and bone graft biomaterials was carried out through compression tests using samples with noncomplex geometry. Analysis of the chemical composition, surface features, porosity, and compressive strength indicates that hydroxyapatite-based materials and trabecular bone have similar properties.

  8. Antimicrobial peptides on calcium phosphate-coated titanium for the prevention of implant-associated infections

    DEFF Research Database (Denmark)

    Kazemzadeh-Narbat, Mehdi; Kindrachuk, Jason; Duan, Ke

    2010-01-01

    of this study was to develop a technique that enables the loading and local delivery of a unique group of cationic antimicrobial peptides (AMP) through implant surfaces. A thin layer of micro-porous calcium phosphate (CaP) coating was processed by electrolytic deposition onto the surface of titanium as the drug......Prevention of implant-associated infections has been one of the main challenges in orthopaedic surgery. This challenge is further complicated by the concern over the development of antibiotic resistance as a result of using traditional antibiotics for infection prophylaxis. The objective......) bacteria with 106-fold reductions of both bacterial strains within 30 min as assessed by measuring colony-forming units (CFU). Repeated CFU assays on the same CaP-Tet213 specimen demonstrated retention of antimicrobial activity by the CaP-Tet213 surfaces through four test cycles. The susceptibility...

  9. Modifications on the properties of a calcium phosphate cement by additions of sodium alginate

    International Nuclear Information System (INIS)

    Coelho, W.T.; Fernandes, J.M.; Vieira, R.S.; Thurmer, M.B.; Santos, L.A.

    2012-01-01

    The Calcium Phosphate Cement (CPC) are bone substitutes with great potential for use in orthopedics, traumatology and dentistry due to its biocompatibility, bioactivity and osteoconductivity, and form a paste that can be easily shaped and placed into the surgical site. However, CPCs have low mechanical strength, which equals the maximum mechanical strength of trabecular bone. In order to assess the strength and time to handle a CPC composed primarily of alpha phase, were added sodium alginate (1%, 2% and 3% wt) and an accelerator in an aqueous solution. The cement powder was mixed with liquid of setting, shaped into specimens and evaluated for apparent density and porosity by Archimedes method, X-ray diffraction and compressive strength. A significant increase in compressive strength by adding sodium alginate was verified. (author)

  10. Production of calcium phosphate coating by laser ablation for biomedical applications

    International Nuclear Information System (INIS)

    Mayor, M.B.; Arias, J.L.; Garcia-Sanz, F.J.; Pou, J.; Leon, B.; Perez-Amor, M.

    1998-01-01

    Apatitic calcium phosphates are used as coating to improve the fixation of orthopaedic and dental implants. The commercial technique to produce these coatings (plasma-spray) shows some problems of adherence and control of their physicochemical properties. In this communication laser ablation is presented as a solution to overcome these problems. The ablation system consists in a vacuum chamber filled with water vapour up to the desired pressure. The laser beam of an ArF excimer laser is focused on a hydroxyapatite target, and the coating is deposited on a substrate parallel to the target maintained at certain temperature. The physicochemical properties of the material were analysed by Fourier transformed infrared spectroscopy (FT-IR) X ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive X ray spectroscopy (EDX). Taking into account these results, two types of coatings were choose to asses their bio compatibility in vitro. (Author) 15 refs

  11. Calcium phosphate glass-ceramics for bioactive coating on a β-titanium alloy

    International Nuclear Information System (INIS)

    Kasuga, T.; Nogami, M.; Niinomi, M.

    2003-01-01

    The formation of a porous coating is the decisive feature for the bio-compatibility of silica-free calcium phosphate glass ceramics on alloy surfaces like the β-Ti structured Ti-29Nb-13Ta-4.6Zr used in this work. The ceramic composition is highly important: 50CaO-40P 2 O 5 -7Na 2 O-3TiO 2 glass powder produces a pore-free coating unable to bind hydroxyapatite, whereas 60CaO-30P 2 O 5 -7Na 2 O-3TiO 2 glass incorporates pores from which a crystalline hydroxyapatite phase can grow over the surface from simulated body fluid (see Figure). (Abstract Copyright [2003], Wiley Periodicals, Inc.)

  12. Calcium phosphate glass-ceramics for bioactive coating on a {beta}-titanium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Kasuga, T.; Nogami, M. [Graduate School of Engineering, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, Nagoya 466-8555 (Japan); Niinomi, M. [Department of Production Systems Engineering, Toyohashi University of Technology, Tenpaku-cho, Toyohashi 441-8580 (Japan)

    2003-07-01

    The formation of a porous coating is the decisive feature for the bio-compatibility of silica-free calcium phosphate glass ceramics on alloy surfaces like the {beta}-Ti structured Ti-29Nb-13Ta-4.6Zr used in this work. The ceramic composition is highly important: 50CaO-40P{sub 2}O{sub 5}-7Na{sub 2}O-3TiO{sub 2} glass powder produces a pore-free coating unable to bind hydroxyapatite, whereas 60CaO-30P{sub 2}O{sub 5}-7Na{sub 2}O-3TiO{sub 2} glass incorporates pores from which a crystalline hydroxyapatite phase can grow over the surface from simulated body fluid (see Figure). (Abstract Copyright [2003], Wiley Periodicals, Inc.)

  13. Structural characterization of pure and doped calcium phosphate bioceramics prepared by simple solid state method

    International Nuclear Information System (INIS)

    Ahmed, S.; Kabir, H.; Nigar, F.

    2011-01-01

    Calcium Phosphate based bioceramic materials, in pure and doped forms have been successfully synthesized from egg shells by using solid-state method for the first time. Considering the diverse role of zinc and fluoride in biological functions, these two ions were chosen to develop the substituted bioceramic materials. Structural characterizations of these developed bioceramics were performed by using FTIR, XRD, SEM and EDS techniques. The results revealed that the fluoride doped apatite was formed in single phase containing hydroxyapatite while pure and Zinc doped apatites contained -TCP with hydroxyapatite. Experimental results and the crystallographic parameters matched well with the literature values indicating that the present experimental protocol favoured the formation of the desired bioceramics. However, to synthesize the (Ca (PO)) based bioceramic materials, such a simple solid-state approach would obviously be very helpful, not only in making the process economically feasible, but also in creating an effective material recycling technology for waste-management. (author)

  14. Monolithic calcium phosphate/poly(lactic acid) composite versus calcium phosphate-coated poly(lactic acid) for support of osteogenic differentiation of human mesenchymal stromal cells.

    Science.gov (United States)

    Tahmasebi Birgani, Zeinab; van Blitterswijk, Clemens A; Habibovic, Pamela

    2016-03-01

    Calcium phosphates (CaPs), extensively used synthetic bone graft substitutes, are often combined with other materials with the aim to overcome issues related to poor mechanical properties of most CaP ceramics. Thin ceramic coatings on metallic implants and polymer-ceramic composites are examples of such hybrid materials. Both the properties of the CaP used and the method of incorporation into a hybrid structure are determinant for the bioactivity of the final construct. In the present study, a monolithic composite comprising nano-sized CaP and poly(lactic acid) (PLA) and a CaP-coated PLA were comparatively investigated for their ability to support proliferation and osteogenic differentiation of bone marrow-derived human mesenchymal stromal cells (hMSCs). Both, the PLA/CaP composite, produced using physical mixing and extrusion and CaP-coated PLA, resulting from a biomimetic coating process at near-physiological conditions, supported proliferation of hMSCs with highest rates at PLA/CaP composite. Enzymatic alkaline phosphatase activity as well as the mRNA expression of bone morphogenetic protein-2, osteopontin and osteocalcin were higher on the composite and coated polymer as compared to the PLA control, while no significant differences were observed between the two methods of combining CaP and PLA. The results of this study confirmed the importance of CaP in osteogenic differentiation while the exact properties and the method of incorporation into the hybrid material played a less prominent role.

  15. Effects of Stirring and Fluid Perfusion on the In Vitro Degradation of Calcium Phosphate Cement/PLGA Composites

    NARCIS (Netherlands)

    An, J.; Leeuwenburgh, S.C.G.; Wolke, J.G.C.; Jansen, J.A.

    2015-01-01

    In vitro degradation rates of calcium phosphate bioceramics are investigated using a large variation of soaking protocols that do not all match the dynamic conditions of the perfused physiological environment. Therefore, we studied the effect of stirring and fluid perfusion on the in vitro

  16. Comparison of the adjuvant activity of aluminum hydroxide and calcium phosphate on the antibody response towards Bothrops asper snake venom.

    Science.gov (United States)

    Olmedo, Hidekel; Herrera, María; Rojas, Leonardo; Villalta, Mauren; Vargas, Mariángela; Leiguez, Elbio; Teixeira, Catarina; Estrada, Ricardo; Gutiérrez, José María; León, Guillermo; Montero, Mavis L

    2014-01-01

    The adjuvanticity of aluminum hydroxide and calcium phosphate on the antibody response in mice towards the venom of the snake Bothrops asper was studied. It was found that, in vitro, most of the venom proteins are similarly adsorbed by both mineral salts, with the exception of some basic phospholipases A2, which are better adsorbed by calcium phosphate. After injection, the adjuvants promoted a slow release of the venom, as judged by the lack of acute toxicity when lethal doses of venom were administered to mice. Leukocyte recruitment induced by the venom was enhanced when it was adsorbed on both mineral salts; however, venom adsorbed on calcium phosphate induced a higher antibody response towards all tested HPLC fractions of the venom. On the other hand, co-precipitation of venom with calcium phosphate was the best strategy for increasing: (1) the capacity of the salt to couple venom proteins in vitro; (2) the venom ability to induce leukocyte recruitment; (3) phagocytosis by macrophages; and (4) a host antibody response. These findings suggest that the chemical nature is not the only one determining factor of the adjuvant activity of mineral salts.

  17. Comparison of xenogenic bone bioimplant and calcium phosphate granules on experimental femoral bone defect healing in rabbits

    Directory of Open Access Journals (Sweden)

    GH Mousavi

    2012-05-01

    Full Text Available Rebuilding and renovation of lost bone whether because of physiologic or pathologic factors was one of the surgeons’ motivations from the past. Osteogenesis of decalcified bone induced by growth factors contained in it. This study is to assay probability effect of decalcified bone and calcium phosphate granules on osteogenesis which is made in experimental flaw and it is as a laboratory pattern in rabbit femur.This experimental study is made on 15 male rabbits. Animals were divided randomly into 3 groups (control and treatments.After induction of general anesthesia, 2 holes in size of 2 mm in diameter was made using a dental bit in femur width to medullary channel. After surgery, the control group left untreated and decalcified bones was placed in group 2 and calcium phosphate granules were placed in group 3. Histopathological and histomorphometrical studies for evaluation of bone healing were carried out in experimental rats, which were euthanized after 45 days of the experiment using hematoxylin-eosin (H&E staining method.In control group, defect seemed to be filled with woven bone and bone marrow spaces and in spite of a poor osteogenic activity. In calcium phosphate group, young bone trabeculas increased in number and bone trabeculas more organized. Histomorphometric results, observed that calcium phosphate granules has significant effect on bone healing than decalcified and control groups.

  18. Calcium-Phosphate-Osteopontin Particles Reduce Biofilm Formation and pH Drops in in situ Grown Dental Biofilms.

    Science.gov (United States)

    Schlafer, Sebastian; Ibsen, Casper J S; Birkedal, Henrik; Nyvad, Bente

    2017-01-01

    This 2-period crossover study investigated the effect of calcium-phosphate-osteopontin particles on biofilm formation and pH in 48-h biofilms grown in situ. Bovine milk osteopontin is a highly phosphorylated glycoprotein that has been shown to interfere with bacterial adhesion to salivary-coated surfaces. Calcium-phosphate-osteopontin particles have been shown to reduce biofilm formation and pH drops in a 5-species laboratory model of dental biofilm without affecting bacterial viability. Here, smooth surface biofilms from 10 individuals were treated ex vivo 6 times/day for 30 min with either calcium-phosphate-osteopontin particles or sterile saline. After growth, the amount of biofilm formed was determined by confocal microscopy, and pH drops upon exposure to glucose were monitored using confocal-microscopy-based pH ratiometry. A total of 160 biofilms were analysed. No adverse effects of repeated ex vivo treatment with calcium-phosphate-osteopontin particles were observed. Particle treatment resulted in a 32% lower amount of biofilm formed (p Biofilm pH was significantly higher upon particle treatment, both shortly after the addition of glucose and after 30 min of incubation with glucose (p biofilms as well as the remineralizing potential of the particles. © 2016 S. Karger AG, Basel.

  19. Effect of calcium phosphate coating crystallinity and implant surface roughness on differentiation of rat bone marrow cells.

    NARCIS (Netherlands)

    Brugge, P.J. ter; Wolke, J.G.C.; Jansen, J.A.

    2002-01-01

    In this study, we examined the effect of calcium phosphate (Ca-P) coating crystallinity and of surface roughness on growth and differentiation of osteogenic cells. Grit-blasted titanium substrates were provided with Ca-P coatings of different crystallinities. Rat bone marrow (RBM) cells were

  20. Increased acellular and cellular surface mineralization induced by nanogrooves in combination with a calcium-phosphate coating.

    NARCIS (Netherlands)

    Klymov, A.; Song, J.; Cai, X; Riet, J. te; Leeuwenburgh, S.C.; Jansen, J.A.; Walboomers, X.F.

    2016-01-01

    The current work evaluated the influence of nanoscale surface-topographies in combination with a calcium phosphate (CaP) coating on acellular and cellular surface mineralization. Four groups of substrates were produced, including smooth, grooved (940nm pitch, 430nm groove width, 185nm depth), smooth

  1. Effect of pH and phosphate on calcium carbonate polymorphs precipitated at near-freezing temperature

    NARCIS (Netherlands)

    Hu, Yu-Bin; Wolthers, Mariëtte; Wolf-Gladrow, Dieter A.; Nehrke, Gernot

    2015-01-01

    The effects of pH and phosphate on the precipitation of calcium carbonate polymorphs from aqueous solution were investigated. Experiments were carried out at near-freezing temperature and two different pH conditions (pH 13.4 and 9.0). At each pH condition, solutions having different concentrations

  2. Bulk physicochemical, interconnectivity, and mechanical properties of calcium phosphate cements-fibrin glue composites for bone substitute applications

    NARCIS (Netherlands)

    Lopez-Heredia, M.A.; Pattipeilohy, J.; Hsu, S.; Grykien, M.; Weijden, B. van der; Leeuwenburgh, S.C.G.; Salmon, P.; Wolke, J.G.C.; Jansen, J.A.

    2013-01-01

    Calcium phosphate cements (CPCs) and fibrin glue (FG) are used for surgical applications. Their combination is promising to create bone substitutes able to promote cell attachment and bone remodeling. This study proposes a novel approach to create CPC-FG composites by simultaneous CPC setting and FG

  3. Revealing the nanostructure of calcium phosphate coatings using HRTEM/FIB techniques

    International Nuclear Information System (INIS)

    Solla, E.L.; Rodríguez-González, B.; Aguiar, H.; Rodríguez-Valencia, C.; Serra, J.; González, P.

    2016-01-01

    Herein, we report on the micro- and nanostructure of the calcium phosphate coating produced by pulsed laser deposition (PLD), using focused ion beam (FIB) lamella sample preparation and transmission electron microscopy (TEM) as the characterization technique. The initial selected area electron diffraction (SAED) data demonstrated the presence of hydroxyapatite (HA) over any other possible calcium phosphate crystalline structure and the polycrystalline nature of the coating. Moreover, the SAED analyses showed clear textured ring patterns coherent with the presence of a preferred orientation in the HA nano-crystal growth. The SAED data also indicated that the coating appears to be textured in the 〈002〉 crystalline direction. Dark-field images obtained using 002 as the working reflection showed a clear oriented crystal growth in columns, from bottom to top. These columns have a peculiar arrangement of nano-crystals since, in some cases, the preferred orientation appears to start at a certain distance from the substrate. Direct d-spacing measurements on high-resolution TEM images provided further proof of the presence of an HA nano-crystal structure. The reported data may be of interest in the future to adjust the microstructure of the HA coatings. - Highlights: •The FIB lift-out technique allows a very site-specific sample preparation method for HRTEM analysis. •It also permits a fast assessment of the HA coating thickness and elemental composition (EDS). •The coatings exhibit a nano-crystalline nature, with a texturing effect along the 002 planes. •PLD is suitable for the production of crystalline c-axis oriented hydroxyapatite coatings. •The crystalline HA phase in the PLD coating is very similar to the present in bone.

  4. Revealing the nanostructure of calcium phosphate coatings using HRTEM/FIB techniques

    Energy Technology Data Exchange (ETDEWEB)

    Solla, E.L., E-mail: esolla@uvigo.es [Servicio de Microscopía Electrónica, CACTI, University of Vigo, Campus As Lagoas-Marcosende, 36310 Vigo (Spain); Rodríguez-González, B. [Servicio de Microscopía Electrónica, CACTI, University of Vigo, Campus As Lagoas-Marcosende, 36310 Vigo (Spain); Aguiar, H.; Rodríguez-Valencia, C.; Serra, J.; González, P. [Applied Physics Department, School of Industrial Engineering, University of Vigo, Campus As Lagoas-Marcosende, 36310 Vigo (Spain)

    2016-12-15

    Herein, we report on the micro- and nanostructure of the calcium phosphate coating produced by pulsed laser deposition (PLD), using focused ion beam (FIB) lamella sample preparation and transmission electron microscopy (TEM) as the characterization technique. The initial selected area electron diffraction (SAED) data demonstrated the presence of hydroxyapatite (HA) over any other possible calcium phosphate crystalline structure and the polycrystalline nature of the coating. Moreover, the SAED analyses showed clear textured ring patterns coherent with the presence of a preferred orientation in the HA nano-crystal growth. The SAED data also indicated that the coating appears to be textured in the 〈002〉 crystalline direction. Dark-field images obtained using 002 as the working reflection showed a clear oriented crystal growth in columns, from bottom to top. These columns have a peculiar arrangement of nano-crystals since, in some cases, the preferred orientation appears to start at a certain distance from the substrate. Direct d-spacing measurements on high-resolution TEM images provided further proof of the presence of an HA nano-crystal structure. The reported data may be of interest in the future to adjust the microstructure of the HA coatings. - Highlights: •The FIB lift-out technique allows a very site-specific sample preparation method for HRTEM analysis. •It also permits a fast assessment of the HA coating thickness and elemental composition (EDS). •The coatings exhibit a nano-crystalline nature, with a texturing effect along the 002 planes. •PLD is suitable for the production of crystalline c-axis oriented hydroxyapatite coatings. •The crystalline HA phase in the PLD coating is very similar to the present in bone.

  5. Investigation of duty cycle effect on corrosion properties of electrodeposited calcium phosphate coatings

    Energy Technology Data Exchange (ETDEWEB)

    Azem, Funda Ak, E-mail: funda.ak@deu.edu.tr [Dokuz Eylul University, Faculty of Engineering, Department of Metallurgical and Materials Engineering, Buca, 35390 Izmir (Turkey); Delice, Tulay Koc, E-mail: tulaykocdelice@gmail.com [Dokuz Eylul University, The Graduate School of Natural and Applied Sciences, Buca, 35390 Izmir (Turkey); Ungan, Guler, E-mail: gulerungan@hotmail.com [Es Group, Izmir (Turkey); Cakir, Ahmet, E-mail: ahmet.cakir@deu.edu.tr [Dokuz Eylul University, Faculty of Engineering, Department of Metallurgical and Materials Engineering, Buca, 35390 Izmir (Turkey)

    2016-11-01

    The bioceramic calcium phosphate (CaP) is frequently used for improving bone fixation in titanium medical implants and thus increasing lifetime of the implant. It is known that the application of CaP coatings on metallic implant devices offers the possibility of combining the strength of the metals and the bioactivity of the ceramic materials. Many different techniques are available for producing CaP coatings. Electrochemical deposition method is widely used because of its ease of operation parameters, low temperature requirement, reproducibility and suitability for coating complex structures. This technique allows obtaining CaP coatings which promote bone in growth during the first healing period leading to permanent fixation. Electrochemical pulse technique is an alternative to calcium phosphate deposition techniques usually employed to cover orthopedic or dental titanium implant surfaces. Additionally, pulse electrodeposition technique can produce more uniform and denser CaP coatings on metallic implants. In this study, CaP based coatings were produced by electrochemical pulse technique on Ti6Al4V substrates. The resulting CaP deposits were investigated by means of X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). Corrosion properties of the CaP coatings were also investigated. The results showed that various duty cycle ranges have remarkably effect on morphology, crystallinity and corrosion properties of the produced CaP coatings. - Highlights: • Electrodeposited CaP based coating were produced by pulse deposition technique. • The pulsed electrodeposited coatings produced under 30% and 50% duty cycles were exhibited better corrosion resistance. • Produced coatings consist of irregular flake-like structure and compact network with fine needles.

  6. Characterization of nickel-doped biphasic calcium phosphate/graphene nanoplatelet composites for biomedical application

    International Nuclear Information System (INIS)

    Baradaran, S.; Moghaddam, E.; Nasiri-Tabrizi, Bahman; Basirun, W.J.; Mehrali, M.; Sookhakian, M.; Hamdi, M.; Alias, Y.

    2015-01-01

    The effect of the addition of an ionic dopant to calcium phosphates for biomedical applications requires specific research due to the essential roles played in such processes. In the present study, the mechanical and biological properties of Ni-doped hydroxyapatite (HA) and Ni-doped HA mixed with graphene nanoplatelets (GNPs) were evaluated. Ni (3 wt.% and 6 wt.%)-doped HA was synthesized using a continuous precipitation method and calcined at 900 °C for 1 h. The GNP (0.5–2 wt.%)-reinforced 6% Ni-doped HA (Ni6) composite was prepared using rotary ball milling for 15 h. The sintering process was performed using hot isostatic pressing at processing conditions of 1150 °C and 160 MPa with a 1-h holding time. The results indicated that the phase compositions and structural features of the products were noticeably affected by the Ni and GNPs. The mechanical properties of Ni6 and 1.5Ni6 were increased by 55% and 75% in hardness, 59% and 163% in fracture toughness and 120% and 85% in elastic modulus compared with monolithic HA, respectively. The in-vitro biological behavior was investigated using h-FOB osteoblast cells in 1, 3 and 5 days of culture. Based on the osteoblast results, the cytotoxicity of the products was indeed affected by the Ni doping. In addition, the effect of GNPs on the growth and proliferation of osteoblast cells was investigated in Ni6 composites containing different ratios of GNPs, where 1.5 wt.% was the optimum value. - Highlights: • Ni doped biphasic calcium phosphate/graphene nanoplatelets composite was investigated. • Mechanical and biological properties were evaluated. • Phase compositions and structural features were influenced noticeably by the Ni and GNPs. • The cytotoxicity of the Ni was improved with the addition of GNPs

  7. Development of macroporous calcium phosphate scaffold processed via microwave rapid drying

    Energy Technology Data Exchange (ETDEWEB)

    Jamuna-Thevi, K., E-mail: jamuna@sirim.my [Advanced Materials Research Centre (AMREC), SIRIM Berhad, Lot 34, Jalan Hi-Tech 2/3, Kulim Hi-Tech Park, 09000 Kulim, Kedah (Malaysia); Zakaria, F.A. [Advanced Materials Research Centre (AMREC), SIRIM Berhad, Lot 34, Jalan Hi-Tech 2/3, Kulim Hi-Tech Park, 09000 Kulim, Kedah (Malaysia); Othman, R. [Materials and Mineral Resources Engineering, Engineering Campus, Universiti Sains Malaysia, Seri Ampangan, 14300 Nibong Tebal, Penang (Malaysia); Muhamad, S. [Bioassay Unit, Herbal Medicine Research Centre (HMRC), Institute for Medical Research (IMR), Jalan Pahang, 50588 Kuala Lumpur (Malaysia)

    2009-06-01

    Porous hydroxyapatite (HA) scaffold has great potential in bone tissue engineering applications. A new method to fabricate macroporous calcium phosphate (CP) scaffold via microwave irradiation, followed by conventional sintering to form HA scaffold was developed. Incorporation of trisodium citrate dihydrate and citric acid in the CP mixture gave macroporous scaffolds upon microwave rapid drying. In this work, a mixture of {beta}-tricalcium phosphate ({beta}-TCP), calcium carbonate (CaCO{sub 3}), trisodium citrate dihydrate, citric acid and double distilled de-ionised water (DDI) was exposed to microwave radiation to form a macroporous structure. Based on gross eye examinations, addition of trisodium citrate at 30 and 40 wt.% in the CP mixture ({beta}-TCP and CaCO{sub 3}) without citric acid indicates increasing order of pore volume where the highest porosity yield was observed at 40 wt.% of trisodium citrate addition and the pore size was detected at several millimeters. Therefore, optimization of pore size was performed by adding 3-7 wt.% of citric acid in the CP mixture which was separately mixed with 30 and 40 wt.% of trisodium citrate for comparison purposes. Fabricated scaffolds were calcined at 600 deg. C and washed with DDI water to remove the sodium hydroxycarbonate and sintered at 1250 deg. C to form HA phase as confirmed in the X-ray diffraction (XRD) results. Based on Archimedes method, HA scaffolds prepared from 40 wt.% of trisodium citrate with 3-7 wt.% of citric acid added CP mixture have an open and interconnected porous structure ranging from 51 to 53 vol.% and observation using Scanning electron microscope (SEM) showed the pore size distribution between 100 and 500 {mu}m. The cytotoxicity tests revealed that the porous HA scaffolds have no cytotoxic potential on MG63 osteoblast-like cells which might allow for their use as biomaterials.

  8. Characterization of nickel-doped biphasic calcium phosphate/graphene nanoplatelet composites for biomedical application

    Energy Technology Data Exchange (ETDEWEB)

    Baradaran, S., E-mail: saeid_baradaran@yahoo.com [Department of Mechanical Engineering, Faculty of Engineering, University of Malaya, 50603 Kuala Lumpur (Malaysia); Moghaddam, E. [Tropical Infectious Diseases Research and Education Centre, Department of Medical Microbiology, Faculty of Medicine, University of Malaya, 50603 Kuala Lumpur (Malaysia); Nasiri-Tabrizi, Bahman, E-mail: bahman_nasiri@hotmail.com [Advanced Materials Research Center, Materials Engineering Department, Najafabad Branch, Islamic Azad University, Isfahan (Iran, Islamic Republic of); Basirun, W.J. [Department of Chemistry, Faculty of Science, University of Malaya, Kuala Lumpur 50603 (Malaysia); Institute of Nanotechnology& Catalysis Research (NanoCat), University Malaya, 50603 Kuala Lumpur (Malaysia); Mehrali, M. [Department of Mechanical Engineering, Faculty of Engineering, University of Malaya, 50603 Kuala Lumpur (Malaysia); Department of Biomedical Engineering, Faculty of Engineering, University of Malaya, Kuala Lumpur 50603 (Malaysia); Sookhakian, M. [Department of Physics, Faculty of Science, University of Malaya, Kuala Lumpur 50603 (Malaysia); Hamdi, M. [Center of Advanced Manufacturing and Material Processing, University of Malaya, 50603 Kuala Lumpur (Malaysia); Alias, Y. [Department of Chemistry, Faculty of Science, University of Malaya, Kuala Lumpur 50603 (Malaysia)

    2015-04-01

    The effect of the addition of an ionic dopant to calcium phosphates for biomedical applications requires specific research due to the essential roles played in such processes. In the present study, the mechanical and biological properties of Ni-doped hydroxyapatite (HA) and Ni-doped HA mixed with graphene nanoplatelets (GNPs) were evaluated. Ni (3 wt.% and 6 wt.%)-doped HA was synthesized using a continuous precipitation method and calcined at 900 °C for 1 h. The GNP (0.5–2 wt.%)-reinforced 6% Ni-doped HA (Ni6) composite was prepared using rotary ball milling for 15 h. The sintering process was performed using hot isostatic pressing at processing conditions of 1150 °C and 160 MPa with a 1-h holding time. The results indicated that the phase compositions and structural features of the products were noticeably affected by the Ni and GNPs. The mechanical properties of Ni6 and 1.5Ni6 were increased by 55% and 75% in hardness, 59% and 163% in fracture toughness and 120% and 85% in elastic modulus compared with monolithic HA, respectively. The in-vitro biological behavior was investigated using h-FOB osteoblast cells in 1, 3 and 5 days of culture. Based on the osteoblast results, the cytotoxicity of the products was indeed affected by the Ni doping. In addition, the effect of GNPs on the growth and proliferation of osteoblast cells was investigated in Ni6 composites containing different ratios of GNPs, where 1.5 wt.% was the optimum value. - Highlights: • Ni doped biphasic calcium phosphate/graphene nanoplatelets composite was investigated. • Mechanical and biological properties were evaluated. • Phase compositions and structural features were influenced noticeably by the Ni and GNPs. • The cytotoxicity of the Ni was improved with the addition of GNPs.

  9. Structure-Composition-Property Relationships in Polymeric Amorphous Calcium Phosphate-Based Dental Composites

    Directory of Open Access Journals (Sweden)

    Drago Skrtic

    2009-11-01

    Full Text Available Our studies of amorphous calcium phosphate (ACP-based materials over the last decade have yielded bioactive polymeric composites capable of protecting teeth from demineralization or even regenerating lost tooth mineral. The anti-cariogenic/remineralizing potential of these ACP composites originates from their propensity, when exposed to the oral environment, to release in a sustained manner sufficient levels of mineral-forming calcium and phosphate ions to promote formation of stable apatitic tooth mineral. However, the less than optimal ACP filler/resin matrix cohesion, excessive polymerization shrinkage and water sorption of these experimental materials can adversely affect their physicochemical and mechanical properties, and, ultimately, limit their lifespan. This study demonstrates the effects of chemical structure and composition of the methacrylate monomers used to form the matrix phase of composites on degree of vinyl conversion (DVC and water sorption of both copolymers and composites and the release of mineral ions from the composites. Modification of ACP surface via introducing cations and/or polymers ab initio during filler synthesis failed to yield mechanically improved composites. However, moderate improvement in composite’s mechanical stability without compromising its remineralization potential was achieved by silanization and/or milling of ACP filler. Using ethoxylated bisphenol A dimethacrylate or urethane dimethacrylate as base monomers and adding moderate amounts of hydrophilic 2-hydroxyethyl methacrylate or its isomer ethyl-α-hydroxymethacrylate appears to be a promising route to maximize the remineralizing ability of the filler while maintaining high DVC. Exploration of the structure/composition/property relationships of ACP fillers and polymer matrices is complex but essential for achieving a better understanding of the fundamental mechanisms that govern dissolution/re-precipitation of bioactive ACP fillers, and

  10. Corrosion Behavior of PEO Coatings Formed on AZ31 Alloy in Phosphate-Based Electrolytes with Calcium Acetate Additive

    Science.gov (United States)

    Ziyaei, E.; Atapour, M.; Edris, H.; Hakimizad, A.

    2017-07-01

    The PEO coating started on magnesium AZ31 using a unipolar DC power source. The coating was generated in the electrolyte based on Na3PO4·12H2O and KOH with calcium acetate as additive. The x-ray diffraction method showed some phases containing calcium and phosphate, which was created in the presence of additive. Also, the EDS tests of the sample's surfaces proved the existence of calcium on the surface. Based on the electrochemical tests results, the most corrosion resistance belongs to the sample with calcium acetate additive. In fact, the results of the EIS tests showed the coating with calcium acetate has the highest resistance but the lowest capacitance. However, this state belongs to the surface morphology, the lower porosity, and surface chemical composition.

  11. Human bone marrow stem cell-encapsulating calcium phosphate scaffolds for bone repair

    Science.gov (United States)

    Weir, Michael D.; Xu, Hockin H.K.

    2010-01-01

    Due to its injectability and excellent osteoconductivity, calcium phosphate cement (CPC) is highly promising for orthopedic applications. However, a literature search revealed no report on human bone marrow mesenchymal stem cell (hBMSC) encapsulation in CPC for bone tissue engineering. The aim of this study was to encapsulate hBMSCs in alginate hydrogel beads and then incorporate them into CPC, CPC–chitosan and CPC–chitosan–fiber scaffolds. Chitosan and degradable fibers were used to mechanically reinforce the scaffolds. After 21 days, that the percentage of live cells and the cell density of hBMSCs inside CPC-based constructs matched those in alginate without CPC, indicating that the CPC setting reaction did not harm the hBMSCs. Alkaline phosphate activity increased by 8-fold after 14 days. Mineral staining, scanning electron microscopy and X-ray diffraction confirmed that apatitic mineral was deposited by the cells. The amount of hBMSC-synthesized mineral in CPC–chitosan–fiber matched that in CPC without chitosan and fibers. Hence, adding chitosan and fibers, which reinforced the CPC, did not compromise hBMSC osteodifferentiation and mineral synthesis. In conclusion, hBMSCs were encapsulated in CPC and CPC–chitosan–fiber scaffolds for the first time. The encapsulated cells remained viable, osteodifferentiated and synthesized bone minerals. These self-setting, hBMSC-encapsulating CPC-based constructs may be promising for bone tissue engineering applications. PMID:20451676

  12. Three dimensional biphasic calcium phosphate nanocomposites for load bearing bioactive bone grafts

    Energy Technology Data Exchange (ETDEWEB)

    Garai, Subhadra, E-mail: subha@nmlindia.org; Sinha, Arvind

    2016-02-01

    Mimicking matrix mediated bio-mineralization process, three dimensional blocks of biphasic calcium phosphate (BCP, hydroxyapatite (HA) and β-tricalcium phosphate (TCP)) nanocomposites, having three different stoichiometries have been synthesized for possible application as load bearing synthetic bone graft or scaffolds. Biphasic blocks with three weight ratios of 20:80, 25:75 and 30:70 of HA and TCP respectively have been synthesized. Detailed structural and chemical characterization of the samples revealed a strong dependence of porosity and mechanical properties on the stoichiometry of biphasic blocks. Effect of physiological medium on the microstructure and mechanical properties of the three different blocks has also been studied. Bioactivity of the BCP block, exhibiting highest compressive strength in air as well as in physiological medium, has been evaluated through adhesion, proliferation and differentiation of mesenchymal stem cells using different markers. - Highlights: • Developed a process for the synthesis of load bearing 3d- biphasic nanocomposites. • Synthesized nanocomposites exhibited in vitro osteoconductivity and osteoinductivity for bone marrow mesenchymal cells. • Developed process is a matrix mediated biomimetic one.

  13. A study of strontium doped calcium phosphate coatings on AZ31

    International Nuclear Information System (INIS)

    Singh, Satish S.; Roy, Abhijit; Lee, Boeun E.; Ohodnicki, John; Loghmanian, Autrine; Banerjee, Ipsita; Kumta, Prashant N.

    2014-01-01

    Calcium phosphate (CaP) coatings have been studied to tailor the uncontrolled non-uniform corrosion of Mg based alloys while simultaneously enhancing bioactivity. The use of immersion techniques to deposit CaP coatings is attractive due to the ability of the approach to coat complex structures. In the current study, AZ31 substrates were subjected to various pretreatment conditions prior to depositing Sr 2+ doped and undoped CaP coatings. It was hypothesized that the bioactivity and corrosion protection of CaP coatings could be improved by doping with Sr 2+ . Heat treatment to elevated temperatures resulted in the diffusion of alloying elements, Mg and Zn, into the pretreated layer. Sr 2+ doped and undoped CaP coatings formed on the pretreated substrates consisted of biphasic mixtures of β-tricalcium phosphate (β-TCP) and hydroxyapatite (HA). Electrochemical corrosion experiments indicated that the extent of Sr 2+ doping and pretreatment both influenced the corrosion protection. Cytotoxicity was evaluated with MC3T3-E1 mouse preosteoblasts and human mesenchymal stem cells (hMSCs). For both cell types, proliferation decreased upon increasing the Sr 2+ concentration. However, both osteogenic gene and protein expression significantly increased upon increasing Sr 2+ concentration. These results suggest that Sr 2+ doped coatings are capable of promoting osteogenic differentiation on degradable Mg alloys, while also enhancing corrosion protection, in comparison to undoped CaP coatings

  14. Crystal Analysis of Multi Phase Calcium Phosphate Nanoparticles Containing Different amount of Magnesium

    Science.gov (United States)

    Gozalian, Afsaneh; Behnamghader, Ali Asghar; Moshkforoush, Arash

    In this study, Mg doped hydroxyapatite [(Ca, Mg)10(PO4)6(OH)2] and β-tricalcium phosphate nanoparticles were synthesized via sol gel method. Triethyl phosphite, calcium nitrate tetrahydrate and magnesium nitrate hexahydrate were used as P, Ca and Mg precursors. The ratio of (Ca+Mg)/P and the amount of magnesium (x) were kept constant at 1.67 and ranging x = 0 up to 3 in molecular formula of Ca10-xMgx (PO4)6(OH)2, respectively. Phase composition and chemical structure were performed using X-ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FT-IR). Phase percentages, crystallite size, degree of crystallinity and lattice parameters were investigated. The presence of magnesium led to form the Mg doped tricalcium phosphate (β-TCMP) and Mg doped hydroxyapatite (Mg-HA). Based on the results of this study, lattice parameters, degree of crystallinity and crystallite size decreased with magnesium content. In addition, with increasing magnesium content, the amount of CaO phase decreased whereas the amount of MgO phase increased significantly. Obtained results can be used for new biomaterials design.

  15. Thermal spraying of functionally graded calcium phosphate coatings for biomedical implants

    Science.gov (United States)

    Wang, Y.; Khor, K. A.; Cheang, P.

    1998-03-01

    Biomedical requirements in a prosthesis are often complex and diverse in nature. Biomaterials for implants have to display a wide range of adaptability to suit the various stages of the bio-integration process of any foreign material into the human body. Often, a combination of materials is needed. The preparation of a functionally graded bioceramic coating composed of essentially calcium phosphate compounds is explored. The coating is graded in accordance to adhesive strength, bioactivity, and bioresorbability. The bond coat on the Ti-6Al-4V stub is deposited with a particle range of the hydroxyapatite (HA) that will provide a high adhesive strength and bioactivity but have poor bioresorption properties. The top coat, however, is composed of predominantly α-tricalcium phosphate (α-TCP) that is highly bioresorbable. This arrangement has the propensity of allowing accelerated bio-integration of the coating by the body tissues as the top layer is rapidly resorbed, leaving the more bioactive intermediate layer to facilitate the much needed bioactive properties for proper osteoconduction. The processing steps and problems are highlighted, as well as the results of post-spray heat treatment.

  16. Osseoconductive and Corrosion-Inhibiting Plasma-Sprayed Calcium Phosphate Coatings for Metallic Medical Implants

    Directory of Open Access Journals (Sweden)

    Robert B. Heimann

    2017-11-01

    Full Text Available During the last several decades, research into bioceramic coatings for medical implants has emerged as a hot topic among materials scientists and clinical practitioners alike. In particular, today, calcium phosphate-based bioceramic materials are ubiquitously used in clinical applications to coat the stems of metallic endoprosthetic hips as well as the surfaces of dental root implants. Such implants frequently consist of titanium alloys, CoCrMo alloy, or austenitic surgical stainless steels, and aim at replacing lost body parts or restoring functions to diseased or damaged tissues of the human body. In addition, besides such inherently corrosion-resistant metals, increasingly, biodegradable metals such as magnesium alloys are being researched for osseosynthetic devices and coronary stents both of which are intended to remain in the human body for only a short time. Biocompatible coatings provide not only vital biological functions by supporting osseoconductivity but may serve also to protect the metallic parts of implants from corrosion in the aggressive metabolic environment. Moreover, the essential properties of hydroxylapatite-based bioceramic coatings including their in vitro alteration in contact with simulated body fluids will be addressed in this current review paper. In addition, a paradigmatic shift is suggested towards the development of transition metal-substituted calcium hexa-orthophosphates with the NaSiCON (Na superionic conductor structure to be used for implant coatings with superior degradation resistance in the corrosive body environment and with pronounced ionic conductivity that might be utilized in novel devices for electrical bone growth stimulation.

  17. Electrochemical deposition mechanism of calcium phosphate coating in dilute Ca-P electrolyte system

    Energy Technology Data Exchange (ETDEWEB)

    Hu Ren [State Key Laboratory of Physical Chemistry of Solid Surfaces and Department of Chemistry, CNRS Laboratoire International Associe XiamENS, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen, Fujian 361005 (China); Department of Biology, College of Life Science, Xiamen University, Xiamen, Fujian 361005 (China); Lin Changjian, E-mail: cjlin@xmu.edu.cn [State Key Laboratory of Physical Chemistry of Solid Surfaces and Department of Chemistry, CNRS Laboratoire International Associe XiamENS, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen, Fujian 361005 (China); Shi Haiyan; Wang Hui [State Key Laboratory of Physical Chemistry of Solid Surfaces and Department of Chemistry, CNRS Laboratoire International Associe XiamENS, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen, Fujian 361005 (China)

    2009-06-15

    In this work, the electrochemical deposition behavior of calcium phosphate coating from an aqueous electrolyte containing very dilute calcium and phosphorus species (Ca-P) was studied. The effects of three process parameters, i.e. temperature, current density and duration, were systematically investigated and the underlying mechanism was thoroughly analyzed. It was observed that the coating is mainly composed of hydroxyapatite (HA) in a wide range of temperature and current densities. The temperature had a significant effect on the deposition velocity. An apparent activation energy of 174.9 kJ mol{sup -1} was subsequently derived, indicating the mass-transfer control mechanism for the coating formation. The current density was identified to be an important parameter for structure controllability. The results of DR-FTIR/Raman spectroscopic studies of the initial deposition phase strongly suggested that the HA coating was instantaneously and directly precipitated on the substrate; neither induction period nor precursor was detected in this dilute Ca-P electrolyte system. Finally, a phase diagram of the Ca-P electrolyte system was constructed, which offered a thermodynamic reason for the direct single-phase HA precipitation observed only in this system, but not in conventional concentrated systems.

  18. Electrochemical deposition mechanism of calcium phosphate coating in dilute Ca-P electrolyte system

    International Nuclear Information System (INIS)

    Hu Ren; Lin Changjian; Shi Haiyan; Wang Hui

    2009-01-01

    In this work, the electrochemical deposition behavior of calcium phosphate coating from an aqueous electrolyte containing very dilute calcium and phosphorus species (Ca-P) was studied. The effects of three process parameters, i.e. temperature, current density and duration, were systematically investigated and the underlying mechanism was thoroughly analyzed. It was observed that the coating is mainly composed of hydroxyapatite (HA) in a wide range of temperature and current densities. The temperature had a significant effect on the deposition velocity. An apparent activation energy of 174.9 kJ mol -1 was subsequently derived, indicating the mass-transfer control mechanism for the coating formation. The current density was identified to be an important parameter for structure controllability. The results of DR-FTIR/Raman spectroscopic studies of the initial deposition phase strongly suggested that the HA coating was instantaneously and directly precipitated on the substrate; neither induction period nor precursor was detected in this dilute Ca-P electrolyte system. Finally, a phase diagram of the Ca-P electrolyte system was constructed, which offered a thermodynamic reason for the direct single-phase HA precipitation observed only in this system, but not in conventional concentrated systems.

  19. Synthesis, characterization and antimicrobial activity of the micro/nano structured biogenic silver doped calcium phosphate

    Science.gov (United States)

    Supraja, N.; Prasad, T. N. V. K. V.; David, Ernest

    2016-01-01

    Scale formation in PVC pipelines reduces the water flow efficiency and enhances microbial contamination. A bio-based composite material comprising of silver doped calcium phosphate (Cp-Ag) was synthesized using a simple technique (photo catalysis) and herein, we report for the first time on preparation and evaluation of the antimicrobial efficacy of silver doped calcite extracted from the scale in drinking water pipe lines. Five concentrations of silver doped calcite materials viz,5, 10, 15, 20 and 25 ppm were prepared using chemical ammonia mediated synthetic method. The material Cp-Ag was characterized by using the techniques UV-Visible spectroscopy, X-ray diffraction, Fourier transform infrared spectroscopy, Scanning electron microscopy, Raman spectroscopy, Thermo gravimetric analysis, X-ray photo electron spectroscopy (XPS), Nuclear magnetic resonance spectrometer and X-ray flouresence microscopy (XRF). Typical rhombohedral structure of the silver doped calcite was observed. XRF and XPS studies confirmed the presence of both calcium and silver in the composite material (Cp-Ag). The silver doped calcite material exhibited enhanced inhibition against Escherichia coli and staphylococcus aureus (Kirby-Bauer discs diffusion assay) which is also dependent on the concentration of the Cp-Ag material.

  20. Calcium carbonate phosphate binding ion exchange filtration and accelerated denitrification improve public health standards and combat eutrophication in aquatic ecosystems.

    Science.gov (United States)

    Yanamadala, Vijay

    2005-01-01

    Cultural eutrophication, the process by which a lake becomes rich in dissolved nutrients as a result of point and nonpoint pollutant sources, is a major cause of the loss of natural lake ecosystems throughout the world. The process occurs naturally in all lakes, but phosphate-rich nutrient runoff from sources such as storm drains and agricultural runoff is a major cause of excess phosphate-induced eutrophication. Especially in Madrona Marsh, one of the last remaining vernal marshes in the greater Los Angeles area, California, cultural eutrophication has become a major problem. In this study, calcium carbonate was found to be an excellent phosphate binder, reducing up to 70% of the phosphates in a given sample of water, and it posed relatively negligent ecological repercussions. This study involved the testing of this principle in both the laboratory and the real ecosystem. A calcium carbonate lacing procedure was first carried out to determine its efficacy in Madrona Marsh. Through this, ammonia was found to interfere with the solubility of calcium carbonate and therefore to be a hindrance to the reduction of phosphate. Therefore, various approaches for reduction of ammonia were tested, including aeration, use of fiber growth media, and plants, mainly Caulerpa verticellata, chosen for it hardiness, primarily in an attempt to increase population of Nitrobacter and Nitrosomonas. All were successful in moderately reducing ammonia levels. In addition, soil sampling, sediment analysis, microscopic plant analysis, microorganism and macroinvertebrate identification, and rate law formulations were conducted. The effect of phosphate and ammonia reduction on the populations of enterobacteria was also an important focus of this experiment. Varying concentrations of phosphate, ammonia, and calcium carbonate in conjunction with phosphate were tested in Madrona Marsh to determine their effects on the populations of enteropathogens on nonspecific blood agar, MacConkey agar, and

  1. First-Row Transition Metal Doping in Calcium Phosphate Bioceramics: A Detailed Crystallographic Study

    Directory of Open Access Journals (Sweden)

    Guillaume Renaudin

    2017-01-01

    Full Text Available Doped calcium phosphate bioceramics are promising materials for bone repair surgery because of their chemical resemblance to the mineral constituent of bone. Among these materials, BCP samples composed of hydroxyapatite (Ca10(PO46(OH2 and β-TCP (Ca3(PO42 present a mineral analogy with the nano-multi-substituted hydroxyapatite bio-mineral part of bones. At the same time, doping can be used to tune the biological properties of these ceramics. This paper presents a general overview of the doping mechanisms of BCP samples using cations from the first-row transition metals (from manganese to zinc, with respect to the applied sintering temperature. The results enable the preparation of doped synthetic BCP that can be used to tailor biological properties, in particular by tuning the release amounts upon interaction with biological fluids. Intermediate sintering temperatures stabilize the doping elements in the more soluble β-TCP phase, which favors quick and easy release upon integration in the biological environment, whereas higher sintering temperatures locate the doping elements in the weakly soluble HAp phase, enabling a slow and continuous supply of the bio-inspired properties. An interstitial doping mechanism in the HAp hexagonal channel is observed for the six investigated cations (Mn2+, Fe3+, Co2+, Ni2+, Cu2+ and Zn2+ with specific characteristics involving a shift away from the center of the hexagonal channel (Fe3+, Co2+, cationic oxidation (Mn3+, Co3+, and also cationic reduction (Cu+. The complete crystallochemical study highlights a complex HAp doping mechanism, mainly realized by an interstitial process combined with calcium substitution for the larger cations of the series leading to potentially calcium deficient HAp.

  2. Micropore-induced capillarity enhances bone distribution in vivo in biphasic calcium phosphate scaffolds.

    Science.gov (United States)

    Rustom, Laurence E; Boudou, Thomas; Lou, Siyu; Pignot-Paintrand, Isabelle; Nemke, Brett W; Lu, Yan; Markel, Mark D; Picart, Catherine; Wagoner Johnson, Amy J

    2016-10-15

    The increasing demand for bone repair solutions calls for the development of efficacious bone scaffolds. Biphasic calcium phosphate (BCP) scaffolds with both macropores and micropores (MP) have improved healing compared to those with macropores and no micropores (NMP), but the role of micropores is unclear. Here, we evaluate capillarity induced by micropores as a mechanism that can affect bone growth in vivo. Three groups of cylindrical scaffolds were implanted in pig mandibles for three weeks: MP were implanted either dry (MP-Dry), or after submersion in phosphate buffered saline, which fills pores with fluid and therefore suppresses micropore-induced capillarity (MP-Wet); NMP were implanted dry. The amount and distribution of bone in the scaffolds were quantified using micro-computed tomography. MP-Dry had a more homogeneous bone distribution than MP-Wet, although the average bone volume fraction, BVF‾, was not significantly different for these two groups (0.45±0.03 and 0.37±0.03, respectively). There was no significant difference in the radial bone distribution of NMP and MP-Wet, but the BVF‾, of NMP was significantly lower among the three groups (0.25±0.02). These results suggest that micropore-induced capillarity enhances bone regeneration by improving the homogeneity of bone distribution in BCP scaffolds. The explicit design and use of capillarity in bone scaffolds may lead to more effective treatments of large and complex bone defects. The increasing demand for bone repair calls for more efficacious bone scaffolds and calcium phosphate-based materials are considered suitable for this application. Macropores (>100μm) are necessary for bone ingrowth and vascularization. However, studies have shown that microporosity (micropore-induced capillarity had the potential to enhance bone growth in vivo. This work illustrates the positive effects of capillarity on bone regeneration in vivo; it demonstrates that micropore-induced capillarity significantly

  3. Nano clay-enhanced calcium phosphate cements and hydrogels for biomedical applications

    Science.gov (United States)

    Jammalamadaka, Udayabhanu

    Biomaterials are used as templates for drug delivery, scaffolds in tissue engineering, grafts in surgeries, and support for tissue regeneration. Novel biomaterial composites are needed to meet multifaceted requirements of compatibility, ease of fabrication and controlled drug delivery. Currently used biomaterials in orthopedics surgeries suffer limitations in toxicity and preventing infections. Polymethyl methacrylate (PMMA) used as bone cement suffers from limitations of thermal necrosis and monomer toxicity calls for development of better cementing biomaterials. A biodegradable/bioresorbable cement with good mechanical properties is needed to address this short coming. Metal implants used in fixing fractures or total joint replacement needs improvements in preventing biofilm formation and better tissue integration. This research addressed the above mentioned research gaps by formulating novel biomaterial composites. Calcium phosphate cements are the alternative bone cements that are bioresorbable and promote tissue integration. These cements lack sufficient mechanical strengths to be used in load bearing sites. The addition of nanoparticles is hypothesized to improve the mechanical properties without inducing toxicity to the tissue. This hypothesis was tested by evaluating compression and flexural strengths in addition to cytocompatibility tests. Results indicate that addition of nano-clay particles (halloysites nanotubes) improved the compressive strength and osteoinductive properties of calcium phosphate cements. To address the research need of preventing implant failure due to infection and aseptic loosening, novel coatings are needed. Hydrogels are well establish for their ability to mimic in vivo environment, promote cell viability and as drug delivery vehicles. Use of composites of hydrogels and drug-loaded nanoparticles to prevent infection was evaluated. Cytocompatibility results indicate good cell viability. Antibacterial results show sustained release

  4. Calcium phosphate granules in the hepatopancreas of the blue crab Callinectes sapidus.

    Science.gov (United States)

    Becker, G L; Chen, C H; Greenawalt, J W; Lehninger, A L

    1974-05-01

    The hepatopancreas of the adult male blue crab Callinectes sapidus in intermolt was found to contain substantial amounts of calcium, magnesium, and inorganic phosphorus, averaging about 260, 20, and 250 microg-atoms per g wet tissue, respectively, accounting for over 10% of the tissue dry weight. Electron microscopy of the intact tissue showed three qualitatively different granular structures having electron densities suggestive of high mineral content. After fractionation of the tissue using centrifugal techniques, almost 95% of the total mineral was found to reside in a heavy, nonmitochondrial particulate fraction(s). The bulk of the low-speed pellet consisted of relatively dense, roughly spherical granules 1-5 microm in diameter, which could be considerably purified by repeated suspension in water and low-speed sedimentation. In the electron microscope the isolated granules appeared basically similar to one of the three characteristic types of electron-dense granules seen in the intact tissue. Although the freshly isolated granules lost approximately 50% of their wet weight when dried at 105 degrees C, only 10% more was lost upon dry ashing at 450 degrees C, suggesting a fairly low content of organic material. Chemical analysis revealed calcium, magnesium, and inorganic phosphate at 5.7, 2.1, and 4.4 microg-atoms per mg dried granules, respectively, accounting for 69% of the dry weight of the fraction. By specific enzymatic assays, the freshly isolated granules were found to contain ATP, ADP, and AMP at levels of 0.13, 0.03, and 0.01 micromol/mg, or 8% of their total dry weight. The remainder of the total phosphorus contributed an additional 3%, whereas carbonate, citrate, oxalate, and protein each constituted no more than 1%. The mineral granules of the crab hepatopancreas appear to function as storage forms of calcium and phosphate during the intermolt period. This tissue appears promising as a model for study of the cellular events associated with biological

  5. Kinetic identification of an intracellular calcium compartment sensitive to phosphate and dinitrophenol in intact isolated rabbit aorta

    International Nuclear Information System (INIS)

    Hai, C.M.; Phair, R.D.

    1986-01-01

    Previous work from this laboratory revealed the presence of at least three distinct intracellular calcium compartments in intact segments of rabbit aorta. In this study one of these intracellular compartments is shown to be sensitive to dinitrophenol and to increased extracellular phosphate. Intact aortic segments were loaded with 45 Ca in bicarbonate-buffered physiologic salt solution for 1 hour, and then transferred to a flow-through chamber perfused with physiologic salt solution. Effluent from the chamber was collected for 8 hours, and 45 Ca efflux curves were analyzed using compartmental analysis. When aortic segments were loaded and washed out in dinitrophenol, the slowest component of the efflux curve was less prominent; in high phosphate it was more prominent. The rate constant changes required to account for these data were primarily in the exchange between the cytosolic and slowest intracellular calcium compartment, suggesting that the slowest calcium compartment resolved during the 8-hour washout was mitochondrial. This compartment contained 5.4 +/- 3.2 nmol calcium/g wet wt. tissue. The calcium flux across its membranes was 0.32 +/- 0.04 nmol min-1g-1. Because this flux is much smaller than the plasma-membrane calcium flux, we suggest that, in normal physiological circumstances, plasma-membrane extrusion is more important for the removal of Ca from the smooth muscle cytosol than is uptake into this slow intracellular compartment

  6. Synthesis, characterization, and in-vitro cytocompatibility of amorphous β-tri-calcium magnesium phosphate ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Satish S., E-mail: sss42@pitt.edu [Department of Chemical & Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Roy, Abhijit, E-mail: abr20@pitt.edu [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Lee, Boeun, E-mail: bol11@pitt.edu [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Banerjee, Ipsita [Department of Chemical & Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Kumta, Prashant N., E-mail: pkumta@pitt.edu [Department of Chemical & Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Center for Craniofacial Regeneration, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Department of Mechanical Engineering and Materials Science, University of Pittsburgh, PA 15261 (United States)

    2016-10-01

    Biphasic mixtures of crystalline β-tricalcium magnesium phosphate (β-TCMP) and an amorphous calcium magnesium phosphate have been synthesized and reported to support enhanced hMSC differentiation in comparison to β-tricalcium phosphate (β-TCP) due to the release of increased amounts of bioactive ions. In the current study, completely amorphous β-TCMP has been synthesized which is capable of releasing increased amounts of Mg{sup 2+} and PO{sub 4}{sup 3−} ions, rather than a biphasic mixture as earlier reported. The amorphous phase formed was observed to crystallize between temperatures of 400–600 °C. The scaffolds prepared with amorphous β-TCMP were capable of supporting enhanced hMSC proliferation and differentiation in comparison to commercially available β-TCP. However, a similar gene expression of mature osteoblast markers, OCN and COL-1, in comparison to biphasic β-TCMP was observed. To further study the role of Mg{sup 2+} and PO{sub 4}{sup 3−} ions in regulating hMSC osteogenic differentiation, the capability of hMSCs to mineralize in growth media supplemented with Mg{sup 2+} and PO{sub 4}{sup 3−} ions was studied. Interestingly, 5 mM PO{sub 4}{sup 3−} supported mineralization while the addition of 5 mM Mg{sup 2+} to 5 mM PO{sub 4}{sup 3−} inhibited mineralization. It was therefore concluded that the release of Ca{sup 2+} ions from β-TCMP scaffolds also plays a role in regulating osteogenic differentiation on these scaffolds and it is noted that further work is required to more accurately determine the exact role of Mg{sup 2+} in regulating hMSC osteogenic differentiation. - Highlights: • Synthesis of amorphous Mg containing beta tricalcium phosphate ceramics • Amorphous beta TCMP supports enhanced hMSC proliferation and differentiation. • Amorphous beta TCMP shows comparable OCN and COL-1 expression to biphasic TCMP. • Presence of 5 mM Mg{sup 2+} and PO{sub 4}{sup 3−} ions in growth media inhibits hMSC mineralization.

  7. In-situ observation of the transformation of amorphous calcium phosphate to crystalline hydroxyapatite

    Science.gov (United States)

    Stammeier, Jessica; Hippler, Dorothee; Mavromatis, Vasileios; Sacher, Stephan; Dietzel, Martin

    2016-04-01

    Amorphous calcium phosphate (Ca3(PO4)2*nH2O; ACP) is often a precursor phase of the mineral (hydroxy-) apatite (Ca5(PO4)3(OH)) that can be formed in natural settings during both authigenic and biogenic mineral formation. Particularly, in the biomineralization process of fish tissue, ACP has shown to be an important transient phase. In solution ACP rapidly transforms into the crystalline phase. The transformation rate highly depends on the physico-chemical conditions of the solution: Ca & P availability, pH and temperature. In natural settings Ca can be provided by different sources: from (1) seawater, (2) porewater, or (3) diagenetically-altered carbonates, whereas local supersaturation of P can be induced by microbial activity. In this study, we performed phosphate precipitation experiments in order to monitor the transformation process of the ACP to crystalline hydroxyapatite (HAP) using in-situ Raman spectroscopy. During the experiments the temperature was kept constant at 20.0 ± 0.01 ° C and pH at 9 ± 0.1. 50 ml of 0.3 CaCl 2H2O was titrated at a rate of 5 ml/min to an equal volume of 0.2 M Na2HPO4. The pH was kept constant by titration of 1 M NaOH. During the experiment samples were taken from the solution and instantly filtered. The obtained solid samples were lyophilized and analyzed with XRD, ATR and SEM. The respective solution samples were analyzed using ion chromatography and ICP OES, coupling the spectroscopic data with detailed solution chemistry data. We observed transformation of ACP to HAP to occur within 14 hours, illustrated in a clear peak shift in Raman spectra from 950 cm-1 to 960 cm-1. The obtained results are discussed in the aspects of distribution of major elements during the formation of phosphates and/or the diagenetic alteration of carbonates to phosphates in geologic settings. Financial support by DFG-FG 736 and NAWI Graz is kindly acknowledged.

  8. Difference in surface reactions between titanium and zirconium in Hanks' solution to elucidate mechanism of calcium phosphate formation on titanium using XPS and cathodic polarization

    International Nuclear Information System (INIS)

    Tsutsumi, Y.; Nishimura, D.; Doi, H.; Nomura, N.; Hanawa, T.

    2009-01-01

    Titanium and zirconium were immersed in Hanks' solution with and without calcium and phosphate ions, and the surfaces were characterized with X-ray photoelectron spectroscopy (XPS) to determine the mechanism of calcium phosphate formation on titanium in simulated body fluids and in a living body. In addition, they were cathodically polarized in the above solutions. XPS characterization and cathodic polarization revealed differences in the surface properties in the ability of calcium phosphate formation between titanium and zirconium. The surface oxide film on titanium is not completely oxidized and is relatively reactive; that on zirconium is more passive and protective than that on titanium. Neither calcium nor phosphate stably exists alone on titanium, and calcium phosphate is naturally formed on it; calcium phosphate formed on titanium is stable and protective. On the other hand, calcium is never incorporated on zirconium, while zirconium phosphate, which is easily formed on zirconium, is highly stable and protective. Our study presents new information regarding the surface property of titanium and demonstrates that the characteristics of titanium and zirconium may be applied to various medical devices and new surface modification techniques.

  9. Influences of ambient gases on the structure and the composition of calcium phosphate films prepared by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Hye-Lee; Kim, Young-Sun; Kim, Dae-Joon; Lee, Won-Jun [Sejong University, Seoul (Korea, Republic of); Han, Jung-Suk [Seoul National University, Seoul (Korea, Republic of)

    2006-11-15

    Calcium phosphate films were prepared by using a pulsed KrF-laser deposition (PLD) method with a hydroxyapatite target in various ambient gases, such as Ar, O{sub 2} and H{sub 2}O. The influence of the ambient gas on the properties of the deposited films was investigated. The chamber pressure and the substrate temperature were fixed at 0.25 Torr and 600 .deg. C, respectively. Calcium-rich amorphous calcium phosphate films were deposited with a low density in Ar due to the preferential resputtering of phosphorus from the growing film. In an O{sub 2} ambient, the density and the Ca/P ratio of the films were similar to those of the target. However, the deposited film was amorphous calcium phosphate and did not contain OH{sup -} groups. Polycrystalline hydroxyapatite films can be deposited in a H{sub 2}O ambient because a sufficient supply of OH{sup -} groups from the ambient gas is essential for the growth of a hydroxyapatite film.

  10. Influence of colloidal calcium phosphate level on the microstructure and rheological properties of rennet-induced skim milk gels

    DEFF Research Database (Denmark)

    Koutina, Glykeria; Knudsen, Jes Christian; Andersen, Ulf

    2015-01-01

    lactose, to obtain varying levels of micellar calcium and phosphorus but constant value of pH, serum and free calcium, and serum phosphorus. Bovine chymosin was added to the skim milk samples after dialysis and microstructural and rheological properties during gel formation were recorded at 30°C. Samples......Colloidal calcium phosphate is an essential part of casein micelles and being responsible for their stability. Different mineralization of casein micelles was obtained by acidification of skim milk to pH 6.5, 6.0 or 5.5, followed by a dialysis method, using simulated milk ultrafiltrate without...... after dialysis needed approximately 30min after the addition of chymosin to form rennet gels. In addition, low micellar calcium and phosphorus values were both found to correlate with slightly less time for the gels to be formed. This information highlights the importance of CCP in the primary phase...

  11. Study of hMSC proliferation and differentiation on Mg and Mg–Sr containing biphasic β-tricalcium phosphate and amorphous calcium phosphate ceramics

    International Nuclear Information System (INIS)

    Singh, Satish S.; Roy, Abhijit; Lee, Boeun; Kumta, Prashant N.

    2016-01-01

    Biphasic mixtures of either Mg"2"+ or combined Mg"2"+ and Sr"2"+ cation substituted β-tricalcium phosphate (β-TCP) and amorphous calcium phosphate (ACP) were prepared using a low temperature chemical phosphatizing and hydrolysis reaction approach. Scaffolds prepared using the cation substituted calcium phosphates were capable of supporting similar levels of human mesenchymal stem cell proliferation in comparison to commercially available β-TCP. The concentrations of Mg"2"+, Sr"2"+, and PO_4"3"− released from these scaffolds were also within the ranges desired from previous reports to support both hMSC proliferation and osteogenic differentiation. Interestingly, hMSCs cultured directly on scaffolds prepared with only Mg"2"+ substituted β-TCP were capable of supporting statistically significantly increased alkaline phosphatase activity, osteopontin, and osteoprotegerin expression in comparison to all compositions containing both Mg"2"+ and Sr"2"+, and commercially available β-TCP. hMSCs cultured in the presence of scaffold extracts also exhibited similar trends in the expression of osteogenic markers as was observed during direct culture. Therefore, it was concluded that the enhanced differentiation observed was due to the release of bioactive ions rather than the surface microstructure. The role of these ions on transforming growth factor-β and bone morphogenic protein signaling was also evaluated using a PCR array. It was concluded that the release of these ions may support enhanced differentiation through SMAD dependent TGF-β and BMP signaling. - Highlights: • Synthesis of Mg and Mg-Sr containing biphasic beta tricalcium phosphate ceramics • Magnesium substitution influences ALP activity compared to strontium content. • Solution extract plays a more dominant role on hMSC differentiation. • Direct and indirect Mg and Mg-Sr TCP culture show similar OPG and OPN expression.

  12. Study of hMSC proliferation and differentiation on Mg and Mg–Sr containing biphasic β-tricalcium phosphate and amorphous calcium phosphate ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Satish S., E-mail: sss42@pitt.edu [Department of Chemical & Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Roy, Abhijit, E-mail: abr20@pitt.edu [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Lee, Boeun [Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Kumta, Prashant N., E-mail: pkumta@pitt.edu [Department of Chemical & Petroleum Engineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Center for Craniofacial Regeneration, University of Pittsburgh, Pittsburgh, PA 15261 (United States); Department of Mechanical Engineering and Materials Science, University of Pittsburgh, PA 15261 (United States)

    2016-07-01

    Biphasic mixtures of either Mg{sup 2+} or combined Mg{sup 2+} and Sr{sup 2+} cation substituted β-tricalcium phosphate (β-TCP) and amorphous calcium phosphate (ACP) were prepared using a low temperature chemical phosphatizing and hydrolysis reaction approach. Scaffolds prepared using the cation substituted calcium phosphates were capable of supporting similar levels of human mesenchymal stem cell proliferation in comparison to commercially available β-TCP. The concentrations of Mg{sup 2+}, Sr{sup 2+}, and PO{sub 4}{sup 3−} released from these scaffolds were also within the ranges desired from previous reports to support both hMSC proliferation and osteogenic differentiation. Interestingly, hMSCs cultured directly on scaffolds prepared with only Mg{sup 2+} substituted β-TCP were capable of supporting statistically significantly increased alkaline phosphatase activity, osteopontin, and osteoprotegerin expression in comparison to all compositions containing both Mg{sup 2+} and Sr{sup 2+}, and commercially available β-TCP. hMSCs cultured in the presence of scaffold extracts also exhibited similar trends in the expression of osteogenic markers as was observed during direct culture. Therefore, it was concluded that the enhanced differentiation observed was due to the release of bioactive ions rather than the surface microstructure. The role of these ions on transforming growth factor-β and bone morphogenic protein signaling was also evaluated using a PCR array. It was concluded that the release of these ions may support enhanced differentiation through SMAD dependent TGF-β and BMP signaling. - Highlights: • Synthesis of Mg and Mg-Sr containing biphasic beta tricalcium phosphate ceramics • Magnesium substitution influences ALP activity compared to strontium content. • Solution extract plays a more dominant role on hMSC differentiation. • Direct and indirect Mg and Mg-Sr TCP culture show similar OPG and OPN expression.

  13. Effects of inorganic phosphate and ADP on calcium handling by the sarcoplasmic reticulum in rat skinned cardiac muscles.

    Science.gov (United States)

    Xiang, J Z; Kentish, J C

    1995-03-01

    The aim was to investigate whether, and how, increases in inorganic phosphate (Pi) and ADP, similar to those occurring intracellularly during early myocardial ischaemia, affect the calcium handling of the sarcoplasmic reticulum. Rat ventricular trabeculae were permeabilised with saponin. The physiological process of calcium induced calcium release (CICR) from the muscle sarcoplasmic reticulum was triggered via flash photolysis of the "caged Ca2+", nitr-5. Alternatively, calcium release was induced by rapid application of caffeine to give an estimate of sarcoplasmic reticular calcium loading. The initial rate of sarcoplasmic reticular calcium pumping was also assessed by photolysis of caged ATP at saturating [Ca2+]. Myoplasmic [Ca2+] (using fluo-3) and isometric force were measured. Pi (2-20 mM) significantly depressed the magnitude of CICR and the associated force transient. Sarcoplasmic reticular calcium loading was inhibited even more than CICR by Pi, suggesting that reduced calcium loading could account for all of the inhibitory effect of Pi on CICR and that Pi may slightly activate the calcium release mechanism. The reduced sarcoplasmic reticular calcium loading seemed to be due to a fall in the free energy of ATP hydrolysis (delta GATP) available for the calcium pump, since equal decreases in delta GATP produced by adding both Pi and ADP in various ratios caused similar falls in the calcium loading of the sarcoplasmic reticulum. The caged ATP experiments indicated that Pi (20 mM) did not affect the rate constant of sarcoplasmic reticular calcium uptake. ADP (10 mM) alone, or with 1 mM Pi, inhibited calcium loading. In spite of this, ADP (10 mM) did not alter CICR and, when 1 mM Pi was added, ADP increased CICR above control. An increase in intracellular Pi reduces sarcoplasmic reticular calcium loading and thus depresses the CICR. This could be an important contributing factor in the hypoxic or ischaemic contractile failure of the myocardium. However the

  14. Calcification mechanism and bony bonding studies of calcium carbonate and composite aluminosilicate/calcium phosphate applied as biomaterials by using radioactivation methods

    International Nuclear Information System (INIS)

    Oudadesse, H.; Derrien, A.C.; Lucas-Girot, A.; Martin, S.; Cathelieau, G.

    2007-01-01

    Bony grafts are used as a filling biomaterial for defective bone. The introduction of new range of synthetic materials offers to surgeons additional possibilities to avoid virus transmission risks by using natural grafts in bony surgery. In this work, two materials, synthetic calcium carbonate and composite aluminosilicate/calcium phosphate were synthesized by an original method and experimented 'in vivo' as biomaterials for bony filling. Extracted biopsies were studied by several physico chemical and biological methods. The aim was to evaluate the kinetic resorption and bioconsolidation of these materials. We focused on the bioconsolidation between implant and bone by realising cartographies from the implant to the bone and on the calcification mechanism by determination of the origin of Ca and Sr responsible of the neo-formed bone. Neutron activation analysis (NAA), radiotracers 45 Ca* and 85 Sr* and proton-induced X-ray emission (PIXE) were used. Concerning the synthetic calcium carbonate, results show that twelve months after implantation, the mineral composition of implant becomes similar to that of the mature bone. The neoformed bone is composed with Ca and Sr coming from the organism when the Ca and Sr of the implant were progressively eliminated. Concerning the composite geopolymer/calcium phosphate, PIXE and histological studies reveal the intimate links between the bone and the implant starting with the first month after implantation. (author)

  15. Response of stem cells from different origins to biphasic calcium phosphate bioceramics.

    Science.gov (United States)

    Lobo, Sonja E; Glickman, Robert; da Silva, Wagner N; Arinzeh, Treena L; Kerkis, Irina

    2015-08-01

    Biphasic calcium phosphate (BCP) bioceramics have been successfully applied in a broad variety of presentation forms and with different ratios of hydroxyapatite (HA) and β-tricalcium phosphate (β-TCP). BCPs have been loaded with stem cells from different origins for bone tissue engineering purposes, but evidence of stem cell behavior on different compositions (various HA/β-TCP ratios) and physical features of BCPs is limited. We compared the adhesion, proliferation, viability and osteogenic potential of human mesenchymal stem cells (MSCs) on granular BCPs with equal HA/β-TCP ratio of diverse particle sizes and on porous blocks which had different chemical compositions. In addition, the osteogenic differentiation of MSCs was compared to adipose-derived (ADSC) and dental pulp (DPSC) stem cells, as well as to pre-osteoblasts on a particulate BCP. MSCs growing on granular BCPs demonstrated increased number as compared to MSCs growing on blocks. Cells proliferated to a greater extent on small granular BCPs, while large granular BCPs and blocks promoted cell differentiation. Surprisingly, the expression of genes involved in osteogenesis was upregulated in MSCs on bioceramics in basal medium which indicates that BCPs may have osteoinductive potential. This was confirmed with the upregulation of osteochondrogenic markers, at different time points, when stem cells from various tissues were grown on the BCP. This study demonstrates that BCPs, depending on their physical features and chemical composition, modulate stem cell behavior, and that stem cells from different origins are inherently distinct in their gene expression profile and can be triggered toward osteochondrogenic fate by BCPs.

  16. EFFECT OF ACTIVE ACCUMULATION OF CALCIUM AND PHOSPHATE IONS ON THE STRUCTURE OF RAT LIVER MITOCHONDRIA

    Science.gov (United States)

    Greenawalt, John W.; Rossi, Carlo S.; Lehninger, Albert L.

    1964-01-01

    Rat liver mitochondria allowed to accumulate maximal amounts of Ca++ and HPO4 = ions from the suspending medium in vitro during respiration have a considerably higher specific gravity than normal mitochondria and may be easily separated from the latter by isopycnic centrifugation in density gradients of sucrose or cesium chloride. When the mitochondria are allowed to accumulate less than maximal amounts of Ca++ and HPO4 = from the medium, they have intermediate specific gravities which are roughly proportional to their content of calcium phosphate. Maximally "loaded" mitochondria are relatively homogeneous with respect to specific gravity. Correlated biochemical and electron microscopic studies show that Ca++-loaded mitochondria contain numerous dense granules, of which some 85 per cent are over 500 A in diameter. These granules are electron-opaque not only following fixation and staining with heavy metal reagents, but also following fixation with formaldehyde, demonstrating that the characteristic granules in Ca++-loaded mitochondria have intrinsic electron-opacity. The dense granules are almost always located within the inner compartment of the mitochondria and not in the space between the inner and outer membranes. They are frequently located at or near the cristae and they often show electron-transparent "cores." Such granules appear to be made up of clusters of smaller dense particles, but preliminary x-ray diffraction analysis and electron diffraction studies have revealed no evidence of crystallinity in the deposits. The electron-opaque granules decrease in number when the Ca++-loaded mitochondria are incubated with 2,4-dinitrophenol; simultaneously there is discharge of Ca++ and phosphate from the mitochondria into the medium. PMID:14228516

  17. Effects of calcium-phosphate topography on osteoblast mechanobiology determined using a cytodetacher

    International Nuclear Information System (INIS)

    Yang, Shih-Ping; Yang, Chyun-Yu; Lee, Tzer-Min; Lui, Truan-Sheng

    2012-01-01

    The Human fetal osteoblast (hFOB) cell morphology, adhesion force, and proliferation on a calcium-phosphate (Ca-P) micropattern surface were investigated and the mechanobiology was investigated by a cytodetachment test. Ca-P-coated groove patterns with 3.0-μm-deep grooves (C3), 4.5-μm-deep grooves (C4), and 5.5-μm-deep grooves (C5) were produced on silicon wafers using photolithography and wet etching techniques. The grooved substrates were coated with a 200-nm-thick layer of titanium (bond coat) and a 200-nm-thick layer of calcium phosphate (top coat) using a sputtering system. Smooth Ca-P-coated Si wafers were used as control surfaces. Analysis of the scanning electron microscopy observations shows that cells on the Ca-P micropattern showed spreading and elongation. The MTT (3-(4, 5-dimethylthiazol-2-yl)-2, 5-diphenyltetrazolium bromide) assay indicated that C3 and C4 specimens had a significantly higher number of cells than did the control group after 5- and 15-day cultures. The cyto-compatibility of specimens was quantitatively evaluated using a cytodetacher, which directly measures the detachment shear force of an individual cell to the substrate. After 30-min culture, the cell adhesion forces were 38.4 nN for the smooth specimen, 140.8 nN for C3, 124.2 nN for C4, and 67.1 nN for C5. The results indicate that the cell adhesion force is influenced by cell shape and the Ca-P grooved patterns affect the cell shape and cytoskeletal structure, thus influence cell proliferation and cell adhesion force. The cytodetachment test with nanonewton resolution is a sensitive method for studying cell–biomaterial interaction. - Highlights: ► We fabricate different sizes of bioceramic groove surfaces which control the cell physiology. ► The mechanobiology was investigated by a cytodetachment test. ► The narrow size Ca-P micropatterns have better biocompatibility. ► The cytodetachment test with nanonewton resolution is a sensitive method for studying cell

  18. The use of physiological solutions or media in calcium phosphate synthesis and processing.

    Science.gov (United States)

    Tas, A Cuneyt

    2014-05-01

    This review examined the literature to spot uses, if any, of physiological solutions/media for the in situ synthesis of calcium phosphates (CaP) under processing conditions (i.e. temperature, pH, concentration of inorganic ions present in media) mimicking those prevalent in the human hard tissue environments. There happens to be a variety of aqueous solutions or media developed for different purposes; sometimes they have been named as physiological saline, isotonic solution, cell culture solution, metastable CaP solution, supersaturated calcification solution, simulated body fluid or even dialysate solution (for dialysis patients). Most of the time such solutions were not used as the aqueous medium to perform the biomimetic synthesis of calcium phosphates, and their use was usually limited to the in vitro testing of synthetic biomaterials. This review illustrates that only a limited number of research studies used physiological solutions or media such as Earle's balanced salt solution, Bachra et al. solutions or Tris-buffered simulated body fluid solution containing 27mM HCO3(-) for synthesizing CaP, and these studies have consistently reported the formation of X-ray-amorphous CaP nanopowders instead of Ap-CaP or stoichiometric hydroxyapatite (HA, Ca10(PO4)6(OH)2) at 37°C and pH 7.4. By relying on the published articles, this review highlights the significance of the use of aqueous solutions containing 0.8-1.5 mMMg(2+), 22-27mM HCO3(-), 142-145mM Na(+), 5-5.8mM K(+), 103-133mM Cl(-), 1.8-3.75mM Ca(2+), and 0.8-1.67mM HPO4(2-), which essentially mimic the composition and the overall ionic strength of the human extracellular fluid (ECF), in forming the nanospheres of X-ray-amorphous CaP. Copyright © 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  19. Antibacterial activity and ion release of bonding agent containing amorphous calcium phosphate nanoparticles.

    Science.gov (United States)

    Chen, Chen; Weir, Michael D; Cheng, Lei; Lin, Nancy J; Lin-Gibson, Sheng; Chow, Laurence C; Zhou, Xuedong; Xu, Hockin H K

    2014-08-01

    Recurrent caries at the margins is a primary reason for restoration failure. The objectives of this study were to develop bonding agent with the double benefits of antibacterial and remineralizing capabilities, to investigate the effects of NACP filler level and solution pH on Ca and P ion release from adhesive, and to examine the antibacterial and dentin bond properties. Nanoparticles of amorphous calcium phosphate (NACP) and a quaternary ammonium monomer (dimethylaminododecyl methacrylate, DMADDM) were synthesized. Scotchbond Multi-Purpose (SBMP) primer and adhesive served as control. DMADDM was incorporated into primer and adhesive at 5% by mass. NACP was incorporated into adhesive at filler mass fractions of 10%, 20%, 30% and 40%. A dental plaque microcosm biofilm model was used to test the antibacterial bonding agents. Calcium (Ca) and phosphate (P) ion releases from the cured adhesive samples were measured vs. filler level and solution pH of 7, 5.5 and 4. Adding 5% DMADDM and 10-40% NACP into bonding agent, and water-aging for 28 days, did not affect dentin bond strength, compared to SBMP control at 1 day (p>0.1). Adding DMADDM into bonding agent substantially decreased the biofilm metabolic activity and lactic acid production. Total microorganisms, total streptococci, and mutans streptococci were greatly reduced for bonding agents containing DMADDM. Increasing NACP filler level from 10% to 40% in adhesive increased the Ca and P ion release by an order of magnitude. Decreasing solution pH from 7 to 4 increased the ion release from adhesive by 6-10 folds. Bonding agents containing antibacterial DMADDM and remineralizer NACP were formulated to have Ca and P ion release, which increased with NACP filler level from 10% to 40% in adhesive. NACP adhesive was "smart" and dramatically increased the ion release at cariogenic pH 4, when these ions would be most-needed to inhibit caries. Therefore, bonding agent containing DMADDM and NACP may be promising to inhibit

  20. Calcium phosphate cement as a "barrier-graft" for the treatment of human periodontal intraosseous defects

    Directory of Open Access Journals (Sweden)

    Rajesh J

    2009-01-01

    Full Text Available Background : Calcium phosphate cements (CPC are apparently good candidates for periodontal treatment by virtue of their biocompatibility, mouldability and osteoconductivity. However, the clinical efficacy in this regard has not been established. This study is aimed at the evaluation of the efficacy of a formulation of CPC in healing human periodontal intraosseous defects in comparison with hydroxyapatite ceramic granules. Materials and Methods : In this clinical study, 60 patients with periodontal defects were divided into 2 test groups and 1 control group. The defect sites in the test groups were repaired with CPC and hydroxyapatite ceramic granules (HAG. Debridement alone was given in the control group. The progress was assessed at 3, 6, 9 and 12 months observation intervals through soft tissue parameters (probing depth, attachment level and gingival recession. Results: CPC showed significantly better outcome. Probing depth reduction values of CPC, HAG and Control at 6 months were 5.40 ± 1.43, 3.75 ± 1.71 and 2.90 ± 1.48, and those at 12 months were 6.20 ± 1.80, 4.5 ± 1.91 and 2.95 ± 1.73. Clinical attachment gain values of CPC, HAG and Control at 6 months were 5.15 ± 1.50, 3.45 ± 1.96 and 2.25 ± 1.52, and those at 12 months were 5.80 ± 2.02, 3.55 ± 2.06 and 2.30 ± 1.78, In both cases the P value was < 0.001 showing high significance. The gingival recession over 12 months, for the CPC group is lesser than that in the HAG group and the value for the control group is marginally higher than both. Soft-tissue measurements were appended by postoperative radiographs and surgical re-entry in selected cases. Conclusions: Calcium phosphate cement is found to be significantly better than hydroxyapatite ceramic granules. The material could be considered as a "barrier-graft".

  1. The development and characterization of a primarily mineral calcium phosphate - poly(epsilon-caprolactone) biocomposite

    Science.gov (United States)

    Dunkley, Ian Robert

    Orthopaedic reconstruction often involves the surgical introduction of structural implants that provide for rigid fixation, skeletal stabilization, and bone integration. The high stresses incurred by these implanted devices have historically limited material choices to metallic and select polymeric formulations. While mechanical requirements are achieved, these non-degradable materials do not participate actively in the remodeling of the skeleton and present the possibility of long-term failure or rejection. This is particularly relevant in cervical fusion, an orthopaedic procedure to treat damaged, degenerative or diseased intervertebral discs. A significant improvement on the available synthetic bone replacement/regeneration options for implants to treat these conditions in the cervical spine may be achieved with the development of primarily mineral biocomposites comprised of a bioactive ceramic matrix reinforced with a biodegradable polymer. Such a biocomposite may be engineered to possess the clinically required mechanical properties of a particular application, while maintaining the ability to be remodeled completely by the body. A biocomposite of Si-doped calcium phosphate (Si-CaP) and poly(epsilon-caprolactone) (PCL) was developed for application as such a synthetic bone material for potential use as a fusion device in the cervical spine. In this thesis, a method by which high mineral content Si-CaP/PCL biocomposites with interpenetrating matrices of mineral and polymer phases may be prepared will be demonstrated, in addition to the effects of the various preparation parameters on the biocomposite density, porosity and mechanical properties. This new technique by which dense, primarily ceramic Si-CaP/PCL biocomposites were prepared, allowed for the incorporation of mineral contents ranging between 45-97vol%. Polymer infiltration, accomplished solely by passive capillary uptake over several days, was found to be capable of fully infiltrating the microporosity

  2. In vitro assessments of experimental NaF dentifrices containing a prospective calcium phosphate technology.

    Science.gov (United States)

    Karlinsey, Robert L; Mackey, Allen C; Stookey, George K; Pfarrer, Aaron M

    2009-06-01

    To determine the fluoride dose response of experimental NaF dentifrices containing a prospective calcium phosphate technology, along with the corresponding relative enamel and dentin abrasion values. 3 mm diameter bovine enamel specimens were mounted, ground and polished, and softened in a carbopol-lactic acid solution (pH = 5.0) for 36 hours at 37 degrees C. Specimens were then measured for baseline Vickers microhardness and stratified (N = 18, mean VHN = 33) into eight groups. These groups consisted of a placebo paste, four test dentifrices (A, B, C, D) with three of the four (A, B, C) containing a promising calcium phosphate ingredient, Crest Cavity Protection, MI Paste Plus, and PreviDent Booster 5000. The groups were cycled in a lesion reversal pH cycling model consisting of four 2-minute treatment periods (diluted 1:3 with DI water) and one 4-hour acid challenge (carbopol-lactic acid, pH = 5.0) per day. Between these events, specimens were immersed in artificial saliva (pH = 7.0). After 20 days of cycling, the specimens were microdrilled and analyzed for fluoride content, and also measured for Vickers surface microhardness after 10 and 20 days of cycling and after a 2-hour and 16-hour post-cycle acid challenge (carbopol-lactic acid, pH = 5.0). Separately, relative dentin and enamel abrasion (RDA and REA) were performed using the ADA recommended radiotracer method. A fluoride dose response was observed for the test dentifrices after 10 and 20 days of pH cycling, with test dentifrice C promoting the highest remineralization among the groups while both the MI Paste Plus and PreviDent systems provide the least remineralization (one-way ANOVA, SNK, P dentin (one-way ANOVA, SNK, P < 0.05). Altogether, these data show the developmental test dentifrices demonstrate a fluoride dose response and show great promise in remineralizing white-spot enamel lesions relative to MI Paste Plus and PreviDent.

  3. Casein phosphopeptide-amorphous calcium phosphate and shear bond strength of adhesives to primary teeth enamel.

    Science.gov (United States)

    Farokh Gisovar, Elham; Hedayati, Nassim; Shadman, Niloofar; Shafiee, Leila

    2015-02-01

    CPP-ACP (Phosphopeptide-Amorphous Calcium Phosphate) has an important role in caries prevention in pediatric patients. This study was done, because of the great use of CPP-ACP and the need for restoration for teeth treated with CPP-ACP as well as the importance of shear bond strength of adhesives in the success of restorations. This study aimed to evaluate the effect of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) on shear bond strength of dental adhesives to enamel of primary teeth molars. This in vitro study was conducted on 180 extracted primary molars. They were randomly divided into 6 groups and each group was divided into 2 subgroups (treated with CPP-ACP and untreated). In subgroups with CPP-ACP, enamel was treated with CPP-ACP paste 1 h/d for 5 days. Types of adhesives that were evaluated in this study were Tetric N-Bond, AdheSE, AdheSE One F, single Bond 2, SE Bond, and Adper Prompt L-Pop. Shear bond strength was tested with a universal testing machine and mode of failure was evaluated under stereomicroscope. Data were analyzed by T test, 2-way analysis of variance (ANOVA), Tukey and Fisher exact test using SPSS18. P adhesive systems to enamel of primary teeth treated and untreated with CPP-ACP showed no significant difference (P > 0.05). Mode of failure in all groups regardless of CPP-ACP administration was mainly adhesive type. Our results indicated that CPP-ACP did not affect shear bond strength of studied adhesives to primary teeth enamel. To have a successful and durable composite restoration, having a high strength bonding is essential. Considering the wide use of CPP-ACP in preventing tooth decay and the role of adhesive shear bond strength (SBS) in success of composite restoration, we conducted the present study to evaluate the effect of CPP-ACP on the SBS of adhesives to primary teeth enamel.

  4. Wollastonite nanofiber–doped self-setting calcium phosphate bioactive cement for bone tissue regeneration

    Directory of Open Access Journals (Sweden)

    Guo H

    2012-07-01

    Full Text Available Han Guo,1,2 Jie Wei,2 Wenhua Song,2 Shan Zhang,2 Yonggang Yan,3 Changsheng Liu,2 Tiqiao Xiao11Shanghai Synchrotron Radiation Facility, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai, People's Republic of China; 2Key Laboratory for Ultrafine Materials of Ministry of Education, East China University of Science and Technology, Shanghai, People's Republic of China; 3School of Physical Science and Technology, Sichuan University, Chengdu, People's Republic of ChinaAbstract: The purpose of this study was to synthesize a self-setting bioactive cement by incorporation of wollastonite nanofibers (WNFs into calcium phosphate cement (CPC. The composition, morphology, setting time, compressive strength, hydrophilicity, and degradation of WNF-doped CPC (wnf-CPC were investigated. Scanning electron microscopy, Fourier transform infrared spectroscopy, X-ray diffraction, and inductively coupled plasma atomic emission spectroscopy were utilized. Additionally, methyl-thiazolyl-tetrazolium bromide assay, scanning electron microscopy, inductively coupled plasma atomic emission spectroscopy, and histological evaluation were used to study the cell and tissue responses to wnf-CPC, both in vitro and in vivo. The results confirmed that the addition of WNFs into CPC had no obvious effect on the setting time or the compressive strength of wnf-CPC, provided the WNF amount was not more than 10 wt%. However, the hydrophilicity and degradability of wnf-CPC were significantly improved by the addition of WNFs – this was because of the change of microstructure caused by the WNFs. The preferred dissolution of WNFs caused the formation of microporosity in wnf-CPC when soaked in tris hydrochloride solution. The microporosity enlarged the surface area of the wnf-CPC and so promoted degradation of the wnf-CPC when in contact with liquid. In addition, MG-63 cell attachment and proliferation on the wnf-CPC were superior to that on the CPC, indicating that

  5. Why Basic Calcium Phosphate Crystals Should Be Targeted In the Treatment of Osteoarthritis

    Directory of Open Access Journals (Sweden)

    Claire-Louise Murphy

    2014-07-01

    Full Text Available Osteoarthritis (OA is the most common form of arthritis and results in significant social, psychological, and economic costs. It is characterised by progressive cartilage loss, bone remodelling, osteophyte formation, and synovial inflammation with resultant joint pain and disability. Since OA affects the entire joint, it is not surprising that there has been difficulty developing an effective targeted treatment. Treatments available for structural disease modification are limited. Current options appear to mostly reduce symptoms. Basic calcium phosphate (BCP crystals represent a potential therapeutic target in OA; they have been found in 100% of knee and hip cartilages removed at joint replacement. Intra-articular BCP crystals are associated with large joint effusions and dissolution of intra-articular structures, synovial proliferation, and marked degeneration as assessed by diagnostic imaging. While BCP deposition has been considered by many to be simply a consequence of advanced OA, there is substantial evidence to support BCP crystal deposition as an active pathogenic mediator of OA. BCP crystals exhibit a multiplicity of biologic effects in vitro including the ability to stimulate mitogenesis and prostaglandin, cytokine, and matrix metalloproteinase (MMP synthesis in a number of cell types including macrophages, synovial fibroblasts, and chondrocytes. BCP crystals also contribute to inflammation in OA through direct interaction with the innate immune system. Intra-articular BCP crystals can elicit synovial inflammation and cartilage degradation in mice in vivo . Although intra-articular BCP crystals are difficult to detect at the bedside, advances in modern technology should allow improved identification and quantitation of BCP crystals. Our article focuses on why basic calcium crystals are important in the pathogenesis of OA. There is ample evidence that BCP crystals should be explored as a therapeutic target in OA.

  6. Biomimetic calcium phosphate coating of additively manufactured porous CoCr implants

    Energy Technology Data Exchange (ETDEWEB)

    Lindahl, Carl [BIOMATCELL Vinn Excellence Center of Biomaterials and Cell Therapy, Gothenburg (Sweden); Department of Engineering Sciences, Ångstrom Laboratory, Uppsala University, Uppsala (Sweden); Xia, Wei, E-mail: wei.xia@angstrom.uu.se [BIOMATCELL Vinn Excellence Center of Biomaterials and Cell Therapy, Gothenburg (Sweden); Department of Engineering Sciences, Ångstrom Laboratory, Uppsala University, Uppsala (Sweden); Engqvist, Håkan [BIOMATCELL Vinn Excellence Center of Biomaterials and Cell Therapy, Gothenburg (Sweden); Department of Engineering Sciences, Ångstrom Laboratory, Uppsala University, Uppsala (Sweden); Snis, Anders [BIOMATCELL Vinn Excellence Center of Biomaterials and Cell Therapy, Gothenburg (Sweden); Arcam AB, Krokslätts Fabriker 27 A, SE-431 37 Mölndal (Sweden); Lausmaa, Jukka [BIOMATCELL Vinn Excellence Center of Biomaterials and Cell Therapy, Gothenburg (Sweden); Department of Chemistry, Materials and Surfaces, SP Technical Research Institute of Sweden, Borås (Sweden); Palmquist, Anders [BIOMATCELL Vinn Excellence Center of Biomaterials and Cell Therapy, Gothenburg (Sweden); Department of Biomaterials, Sahlgrenska Academy at the University of Gothenburg, Gothenburg (Sweden)

    2015-10-30

    Highlights: • A route for coating complex shaped electron beam melted implants is presented. • Biomimetic HA coatings were deposited on CoCr alloys using a solution method. • Deposited biomimetic coating was partially crystalline, slightly calcium deficient. • Coating morphology was plate-like with crystallites forming roundish flowers. • Present coating procedure could be useful for porous implants made by EBM. - Abstract: The aim of this work was to study the feasibility to use a biomimetic method to prepare biomimetic hydroxyapatite (HA) coatings on CoCr substrates with short soaking times and to characterize the properties of such coatings. A second objective was to investigate if the coatings could be applied to porous CoCr implants manufactured by electron beam melting (EBM). The coating was prepared by immersing the pretreated CoCr substrates and EBM implants into the phosphate-buffered solution with Ca{sup 2+} in sealed plastic bottles, kept at 60 °C for 3 days. The formed coating was partially crystalline, slightly calcium deficient and composed of plate-like crystallites forming roundish flowers in the size range of 300–500 nm. Cross-section imaging showed a thickness of 300–500 nm. In addition, dissolution tests in Tris–HCl up to 28 days showed that a substantial amount of the coating had dissolved, however, undergoing only minor morphological changes. A uniform coating was formed within the porous network of the additive manufactured implants having similar thickness and morphology as for the flat samples. In conclusion, the present coating procedure allows coatings to be formed on CoCr and could be used for complex shaped, porous implants made by additive manufacturing.

  7. Biomimetic calcium phosphate coating of additively manufactured porous CoCr implants

    International Nuclear Information System (INIS)

    Lindahl, Carl; Xia, Wei; Engqvist, Håkan; Snis, Anders; Lausmaa, Jukka; Palmquist, Anders

    2015-01-01

    Highlights: • A route for coating complex shaped electron beam melted implants is presented. • Biomimetic HA coatings were deposited on CoCr alloys using a solution method. • Deposited biomimetic coating was partially crystalline, slightly calcium deficient. • Coating morphology was plate-like with crystallites forming roundish flowers. • Present coating procedure could be useful for porous implants made by EBM. - Abstract: The aim of this work was to study the feasibility to use a biomimetic method to prepare biomimetic hydroxyapatite (HA) coatings on CoCr substrates with short soaking times and to characterize the properties of such coatings. A second objective was to investigate if the coatings could be applied to porous CoCr implants manufactured by electron beam melting (EBM). The coating was prepared by immersing the pretreated CoCr substrates and EBM implants into the phosphate-buffered solution with Ca"2"+ in sealed plastic bottles, kept at 60 °C for 3 days. The formed coating was partially crystalline, slightly calcium deficient and composed of plate-like crystallites forming roundish flowers in the size range of 300–500 nm. Cross-section imaging showed a thickness of 300–500 nm. In addition, dissolution tests in Tris–HCl up to 28 days showed that a substantial amount of the coating had dissolved, however, undergoing only minor morphological changes. A uniform coating was formed within the porous network of the additive manufactured implants having similar thickness and morphology as for the flat samples. In conclusion, the present coating procedure allows coatings to be formed on CoCr and could be used for complex shaped, porous implants made by additive manufacturing.

  8. Dual mode antibacterial activity of ion substituted calcium phosphate nanocarriers for bone infections

    Directory of Open Access Journals (Sweden)

    Sampath Kumar eT.S.

    2015-05-01

    Full Text Available Nanotechnology has tremendous potential for the management of infectious diseases caused by multi-drug resistant (MDR bacteria, through the development of newer antibacterial materials and efficient modes of antibiotic delivery. Calcium phosphate (CaP bioceramics are commonly used as bone substitutes due to their similarity to bone mineral and are widely researched upon for the treatment of bone infections associated with bone loss. CaPs can be used as local antibiotic delivery agents for bone infections and can be substituted with antibacterial ions in their crystal structure to have a wide spectrum, sustained antibacterial activity even against drug resistant bacteria. In the present work, a dual mode antibiotic delivery system with antibacterial ion substituted calcium deficient hydroxyapatite (CDHA nanoparticles has been developed. Antibacterial ions such as zinc, silver and strontium have been incorporated into CDHA at concentrations of 6 at. %, 0.25-0.75 at. % and 2.5-7.5 at. % respectively. The samples were found to be phase pure, acicular nanoparticles of length 40-50 nm and width 5-6 nm approximately. The loading and release profile of doxycycline, a commonly used antibiotic, was studied from the nanocarriers. The drug release was studied for five days and the release profile was influenced by the ion concentrations. The release of antibacterial ions was studied over a period of 21 days. The ion substituted CDHA samples were tested for antibacterial efficacy on S.aureus and E.coli by MIC/MBC studies and time-kill assay. AgCDHA and ZnCDHA showed high antibacterial activity against both bacteria while SrCDHA was weakly active against S.aureus. Present study shows that the antibiotic release can provide the initial high antibacterial activity and the sustained ion release can provide a long-term antibacterial activity. Such dual mode antibiotic and antibacterial ion release offers an efficient and potent way to treat an incumbent drug

  9. Synthesis and characterization of amino acid-functionalized calcium phosphate nanoparticles for siRNA delivery.

    Science.gov (United States)

    Bakan, Feray; Kara, Goknur; Cokol Cakmak, Melike; Cokol, Murat; Denkbas, Emir Baki

    2017-10-01

    Small interfering RNAs (siRNA) are short nucleic acid fragments of about 20-27 nucleotides, which can inhibit the expression of specific genes. siRNA based RNAi technology has emerged as a promising method for the treatment of a variety of diseases. However, a major limitation in the therapeutic use of siRNA is its rapid degradation in plasma and cellular cytoplasm, resulting in short half-life. In addition, as siRNA molecules cannot penetrate into the cell efficiently, it is required to use a carrier system for its delivery. In this work, chemically and morphologically different calcium phosphate (CaP) nanoparticles, including spherical-like hydroxyapatite (HA-s), needle-like hydroxyapatite (HA-n) and calcium deficient hydroxyapatite (CDHA) nanoparticles were synthesized by the sol-gel technique and the effects of particle characteristics on the binding capacity of siRNA were investigated. In order to enhance the gene loading efficiency, the nanoparticles were functionalized with arginine and the morphological and their structural characteristics were analyzed. The addition of arginine did not significantly change the particle sizes; however, it provided a significantly increased binding of siRNA for all types of CaP nanoparticles, as revealed by spectrophotometric measurements analysis. Arginine functionalized HA-n nanoparticles showed the best binding behavior with siRNA among the other nanoparticles due to its high, positive zeta potential (+18.8mV) and high surface area of Ca ++ rich "c" plane. MTT cytotoxicity assays demonstrated that all the nanoparticles tested herein were biocompatible. Our results suggest that high siRNA entrapment in each of the three modified non-toxic CaP nanoparticles make them promising candidates as a non-viral vector for delivering therapeutic siRNA molecules to treat cancer. Copyright © 2017 Elsevier B.V. All rights reserved.

  10. Mechanical characterization and ion release of bioactive dental composites containing calcium phosphate particles.

    Science.gov (United States)

    Natale, Livia C; Rodrigues, Marcela C; Alania, Yvette; Chiari, Marina D S; Boaro, Leticia C C; Cotrim, Marycel; Vega, Oscar; Braga, Roberto R

    2018-08-01

    to verify the effect of the addition of dicalcium phosphate dihydrate (DCPD) particles functionalized with di- or triethylene glycol dimethacrylate (DEGDMA or TEGDMA) on the degree of conversion (DC), post-gel shrinkage (PS), mechanical properties, and ion release of experimental composites. Four composites were prepared containing a BisGMA/TEGDMA matrix and 60 vol% of fillers. The positive control contained only barium glass fillers, while in the other composites 15 vol% of the barium was replaced by DCPD. Besides the functionalized particles, non-functionalized DCPD was also tested. DC after 24 h (n = 3) was determined by FTIR spectroscopy. The strain gage method was used to obtain PS 5 min after photoactivation (n = 5). Flexural strength and modulus (n = 10) were calculated based on the biaxial flexural test results, after specimen storage for 24 h or 60 days in water. The same storage times were used for fracture toughness testing (FT, n = 10). Calcium and phosphate release up to 60 days was quantified by ICP-OES (n = 3). Data were analyzed by ANOVA/Tukey test (alpha: 5%). Composites containing functionalized DCPD presented higher DC than the control (p composites (p composite with DEGDMA-functionalized DCPD presented fracture strength similar to the control, while for flexural modulus only the composite with TEGDMA-functionalized particles was lower than the control (p composites containing DCPD was higher than the control after 60 days (p composite with non-functionalized DCPD at 15 days and no significant reductions were observed for composites with functionalized DCPD during the observation period (p composites, phosphate release was higher at 15 days than in the subsequent periods, and no difference among them was recorded at 45 and 60 days (p composite with DEGDMA-functionalized particles was the only material with strength similar to the control after 60 days in water; however, it also presented the highest

  11. Colorimetric determination of selenium in mineral premixes .

    Science.gov (United States)

    Hurlbut, J A; Burkepile, R G; Geisler, C A; Kijak, P J; Rummel, N G

    1997-01-01

    A method is described for determination of sodium selenite or sodium selenate in mineral-based premixes. It is based on the formation of intense-yellow piazselenol by Se(IV) and 3,3'-diaminobenzidine. Mineral premixes typically contain calcium carbonate as a base material and magnesium carbonate, silicon dioxide, and iron(III) oxide as minor components or additives. In this method, the premix is digested briefly in nitric acid, diluted with water, and filtered to remove any Iron(III) oxide. Ethylenediaminetetraacetic acid and HCl are added to the filtrate, which is heated to near boiling for 1 h to convert any selenate to selenite. After heating, the solution is buffered between pH 2 and 3 with NaOH and formic acid and treated with NH2OH and EDTA; any Se present forms a complex with 3,3'-diaminobenzidine at 60 degrees C. The solution is made basic with NH4OH, and the piazselenol is extracted into toluene. The absorbance of the complex in dried toluene is measured at 420 nm. The method was validated independently by 2 laboratories. Samples analyzed included calcium carbonate fortified with 100, 200, and 300 micrograms Se in the form of sodium selenite or sodium selenate, a calcium carbonate premix containing sodium selenite, a calcium carbonate premix containing sodium selenate, and a commercial premix; 5 replicates of each sample type were analyzed by each laboratory. Average recoveries ranged from 89 to 109% with coefficients of variation from 1.2 to 13.6%.

  12. Effect of Poly(Vinyl Alcohol) Addition on the Properties of Hydrothermal Derived Calcium Phosphate Cement for Bone Filling Materials

    Science.gov (United States)

    Razali, N. N.; Sopyan, I.; Mel, M.; Salleh, H. M.; Rahman, M. M.; Singh, R.

    2017-06-01

    The effect of addition of poly(vinyl alcohol) on hydrothermal derived calcium phosphate cement has been studied. The precursors used to prepare the cement were calcium oxide (CaO) and ammonium dihydrogen phosphate (NH4H2PO4); the reaction was conducted in water at 80-100°C. To improve properties of CPC, poly(vinyl alcohol) (PVA) of 1wt% and 2wt% was added to the liquid phase of CPC and the results were compared to CPC without PVA addition. The addition of PVA was proved to bring remarkable effects on cohesion, setting time and mechanical strength of CPC which make it suitable physically for injectable bone filler applications.

  13. A Short Overview on the Biomedical Applications of Silica, Alumina and Calcium Phosphate-based Nanostructured Materials.

    Science.gov (United States)

    Ellahioui, Younes; Prashar, Sanjiv; Gómez-Ruiz, Santiago

    2016-01-01

    This article reviews the use of silica, alumina and calcium phosphate-based nanostructured materials with biomedical applications. A short introduction on the use of the materials in Science, Nanotechnology and Health is included followed by a revision of each of the selected materials. A description of the principal synthetic methods used in the preparation of the materials in nanostructured form is included. The most widely used applications in biomedicine are reviewed including, for example drug-delivery, bone regeneration, imaging, sensoring amongst others. Finally, a short description of the toxicity and cytotoxicity associated with each of the materials of this revision is presented. This short literature revision serves to demonstrate the very promising future ahead of nanosystems based on silica, alumina and calcium phosphate for biological and biomedical applications.

  14. Microwave assisted synthesis and characterization of magnesium substituted calcium phosphate bioceramics

    Energy Technology Data Exchange (ETDEWEB)

    Khan, Nida Iqbal [Interdisciplinary Research Centre in Biomedical Materials, COMSATS Institute of Information Technology, M. A. Jinnah Campus, Defence Road, Off Raiwind Road, Lahore (Pakistan); Medical Implant Technology Group (MEDITEG), Faculty of Bioscience and Medical Engineering, Universiti Teknologi Malaysia, 81310 Skudai, Johor Darul Takzim (Malaysia); Ijaz, Kashif; Zahid, Muniza; Khan, Abdul S. [Interdisciplinary Research Centre in Biomedical Materials, COMSATS Institute of Information Technology, M. A. Jinnah Campus, Defence Road, Off Raiwind Road, Lahore (Pakistan); Abdul Kadir, Mohammed Rafiq [Medical Implant Technology Group (MEDITEG), Faculty of Bioscience and Medical Engineering, Universiti Teknologi Malaysia, 81310 Skudai, Johor Darul Takzim (Malaysia); Hussain, Rafaqat [Department of Chemistry, Faculty of Science, Universiti Teknologi Malaysia, Skudai, Johore (Malaysia); Anis-ur-Rehman [Department of Physics, COMSATS Institute of Information Technology, Chakshahzad Campus, Islamabad (Pakistan); Darr, Jawwad A. [Clean Materials Technology Group, Department of Chemistry, University College London, Christopher Ingold Laboratories, 20 Gordon Street, London WC1H 0AJ (United Kingdom); Ihtesham-ur-Rehman [The Kroto Research Institute, North Campus, University of Sheffield, Broad Lane, Sheffield S3 7HQ (United Kingdom); Chaudhry, Aqif A., E-mail: aqifanwar@ciitlahore.edu.pk [Interdisciplinary Research Centre in Biomedical Materials, COMSATS Institute of Information Technology, M. A. Jinnah Campus, Defence Road, Off Raiwind Road, Lahore (Pakistan)

    2015-11-01

    Hydroxyapatite is used extensively in hard tissue repair due to its biocompatibility and similarity to biological apatite, the mineral component of bone. It differs subtly in composition from biological apatite which contains other ions such as magnesium, zinc, carbonate and silicon (believed to play biological roles). Traditional methods of hydroxyapatite synthesis are time consuming and require strict reaction parameter control. This paper outlines synthesis of magnesium substituted hydroxyapatite using simple microwave irradiation of precipitated suspensions. Microwave irradiation resulted in a drastic decrease in ageing times of amorphous apatitic phases. Time taken to synthesize hydroxyapatite (which remained stable upon heat treatment at 900 °C for 1 h) reduced twelve folds (to 2 h) as compared to traditionally required times. The effects of increasing magnesium concentration in the precursors on particle size, surface area, phase-purity, agglomeration and thermal stability, were observed using scanning electron microscopy, BET surface area analysis, X-ray diffraction and photo acoustic Fourier transform infra-red spectroscopy. Porous agglomerates were obtained after a brief heat-treatment (1 h) at 900 °C. - Highlights: • Microwave irradiation of suspensions of calcium phosphates accelerated maturation. • Reactions took 2 h to complete as compared to 18 h required traditionally. • Magnesium contents higher than 1 wt.% lead to the presence of non-apatitic phases. • Agglomerates with micron and sub-micron porosity were obtained after heat-treatment.

  15. The Effect of Reduced Graphene Oxide-Coated Biphasic Calcium Phosphate Bone Graft Material on Osteogenesis.

    Science.gov (United States)

    Kim, Jeong-Woo; Shin, Yong Cheol; Lee, Jin-Ju; Bae, Eun-Bin; Jeon, Young-Chan; Jeong, Chang-Mo; Yun, Mi-Jung; Lee, So-Hyoun; Han, Dong-Wook; Huh, Jung-Bo

    2017-08-08

    This study was conducted to evaluate the effect of biphasic calcium phosphate (BCP) coated with reduced graphene oxide (rGO) as bone graft materials on bone regeneration. The rGO-coated BCP bone graft material was fabricatied by mixing rGO and BCP at various concentrations. The surface charge of rGO-coated BCP was measured to be -14.43 mV, which formed a static electrostatic interaction. Cell viabilities were significantly diminished at higher concentrations of ≥100 μg/mL. The calvarial defects of 48 rats were implanted rGO-coated BCPs at a weight ratio of 2:1000 (rGO2), 4:1000 (rGO4), and 10:1000 (rGO10), repectively. BCP was used as a control group. The micro-CT and histological analysis were performed to evaluate new bone formation at 2 and 8 weeks after surgery. The results showed that the new bone volume (mm³) was significantly higher in the experimental groups than in the control group. Histological analysis showed that new bone areas (%) were significantly higher in the rGO2 and rGO10 than in the control, and significantly higher in rGO4 than in the rGO2 and rGO10. Conclusively, the rGO-coated BCP was found to be effective on osteogenesis and the concentration of the composite was an important factor.

  16. Synthesis of calcium hydrogen phosphate and hydroxyapatite coating on SS316 substrate through pulsed electrodeposition

    Energy Technology Data Exchange (ETDEWEB)

    Chakraborty, Rajib, E-mail: rajibju4@gmail.com [Department of Mechanical Engineering, Indian Institute of Technology Kharagpur, Kharagpur 721302 (India); Sengupta, Srijan [Department of Metallurgical and Materials Engineering, Indian Institute of Technology Kharagpur, Kharagpur 721302 (India); Saha, Partha [Department of Mechanical Engineering, Indian Institute of Technology Kharagpur, Kharagpur 721302 (India); Das, Karabi; Das, Siddhartha [Department of Metallurgical and Materials Engineering, Indian Institute of Technology Kharagpur, Kharagpur 721302 (India)

    2016-12-01

    The orthopaedic implants for human body are generally made of different biomaterials like stainless steels or Ti based alloys. However, it has been found that from surface properties point of view, none of these materials is attractive for fast tissue or cell growth on the surface of implant. This is one of the most important criteria to assure quick bonding between implant and body tissues vis-à-vis minimum recovery time for the patient. Keeping in view of the above facts, this work involves the pulsed electro-deposition coating of biocompatible hydroxyapatite and its group compounds from a diluted bath of calcium and phosphate salt at various current densities over the biomaterial sheet of SS316. SEM study confirms different morphologies of the coatings at different current densities. Characterization techniques like X-ray diffraction, SEM with EDX and FTIR have been used to confirm the phase and percentage quantity of hydroxyapatite compound in the depositions. This coating can serve as a medium for faster tissue growth over the metallic implants. - Highlights: • Composite coatings of CaHPO{sub 4} and hydroxyapatite for biomedical application through pulsed electro-deposition. • Achieved optimum phase composition in view of crystallinity of both the phases. • Overall coating crystallinity of around 70% in view better bio compatibility. • In cyclic voltammetry it is observed that the deposition reaction is completely irreversible. • The deposited coating consists of nano-crystalline hydroxyapatite similar to human bone; which exhibits better bio-compatibility.

  17. Improving the packing density of calcium phosphate coating on a magnesium alloy for enhanced degradation resistance.

    Science.gov (United States)

    Kannan, M Bobby

    2013-05-01

    In this study, an attempt was made to improve the packing density of calcium phosphate (CaP) coating on a magnesium alloy by tailoring the coating solution for enhanced degradation resistance of the alloy for implant applications. An organic solvent, ethanol, was added to the coating solution to decrease the conductivity of the coating solution so that hydrogen bubble formation/bursting reduces during the CaP coating process. Experimental results confirmed that ethanol addition to the coating solution reduces the conductivity of the solution and also decreases the hydrogen evolution/bubble bursting. In vitro electrochemical experiments, that is, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization showed that CaP coating produced in 30% (v/v) ethanol containing coating solution (3E) exhibits significantly higher degradation resistance (i.e., ~50% higher polarization resistance and ~60% lower corrosion current) than the aqueous solution coating. Scanning electron microscope (SEM) analysis of the coatings revealed that the packing of 3E coating was denser than that of aqueous coating, which can be attributed to the lower hydrogen evolution in the former than in the latter. Further increase in the ethanol content in the coating solution was not beneficial; in fact, the coating produced in 70% (v/v) ethanol containing solution (7E) showed degradation resistance much inferior to that of the aqueous coating, which is due to low thickness of 7E coating. Copyright © 2012 Wiley Periodicals, Inc.

  18. Solution combustion synthesis of calcium phosphate particles for controlled release of bovine serum albumin

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Junfeng, E-mail: daidai02304@163.com [School of Chemistry and Materials Engineering, Changshu Institute of Technology, Changshu (China); Jiangsu Laboratory of Advanced Functional Materials, Changshu Institute of Technology, Changshu (China); Zhao, Junjie; Qian, Yu; Zhang, Xiali; Zhou, Feifei; Zhang, Hong [School of Chemistry and Materials Engineering, Changshu Institute of Technology, Changshu (China); Lu, Hongbin [National Laboratory of Solid State Microstructures, College of Engineering and Applied Sciences, Nanjing University, Nanjing (China); Chen, JianHua; Wang, XuHong [School of Chemistry and Materials Engineering, Changshu Institute of Technology, Changshu (China); Jiangsu Laboratory of Advanced Functional Materials, Changshu Institute of Technology, Changshu (China); Yu, Wencong [School of Chemistry and Materials Engineering, Changshu Institute of Technology, Changshu (China)

    2015-05-01

    Four different phase compositions of calcium phosphate (CaP) particles were prepared via a solution combustion method. X-ray diffraction (XRD) and Rietveld analysis results revealed that the variations in the nominal Ca/P (molar) ratios were found to provide a favorable control in the different proportions of CaP materials. Bovine serum albumin (BSA) was used as a model protein to study the loading and release behavior. The release profile indicated that the BSA release rates depended on the phase compositions of the CaP particles, and showed an order of TCP-BSA > BCP-1-BSA > BCP-2-BSA > HA-BSA. The results suggested that the BSA protein release rate can be controlled by varying the phase compositions of CaP carriers. Moreover, the release process involved two stages: firstly surface diffusion via ion exchange and secondly intraparticle diffusion. - Highlights: • Solution combustion method was an efficient way to produced CaP powders. • Ca/P (molar) ratios provided a favorable control in the different proportions of phase composition. • BSA release rate varied depending on the phase composition of the CaP particles. • Two kinetic models were chosen to simulate the release kinetics of the drugs from CaP carriers.

  19. Physicochemical properties and biocompatibility of chitosan oligosaccharide/gelatin/calcium phosphate hybrid cements

    Energy Technology Data Exchange (ETDEWEB)

    Chiang, Ting-Yi [Department of Dental Laboratory Technology, Central Taiwan University of Science and Technology, Taichung 406, Taiwan (China); Ho, Chia-Che [Institute of Oral Biology and Biomaterials Science, Chung-Shan Medical University, Taichung 402, Taiwan (China); Chen, David Chan-Hen [Institute of Veterinary Microbiology, National Chung-Hsing University, Taichung 402, Taiwan (China); Lai, Meng-Heng [Institute of Oral Biology and Biomaterials Science, Chung-Shan Medical University, Taichung 402, Taiwan (China); Ding, Shinn-Jyh, E-mail: sjding@csmu.edu.tw [Institute of Oral Biology and Biomaterials Science, Chung-Shan Medical University, Taichung 402, Taiwan (China); Department of Dentistry, Chung-Shan Medical University Hospital, Taichung 402, Taiwan (China)

    2010-04-15

    A bone substitute material was developed consisting of a chitosan oligosaccharide (COS) solution in a liquid phase and gelatin (GLT) containing calcium phosphate powder in a solid phase. The physicochemical and biocompatible properties of the hybrid cements were evaluated. The addition of COS to cement did not affect the setting time or diametral tensile strength of the hybrid cements, whereas GLT significantly prolonged the setting time and decreased the strength slightly. The setting reaction was inhibited by the addition of GLT to the initial mixture, but not by COS. However, the presence of GLT appreciably improved the anti-washout properties of the hybrid cement compared with COS. COS may promote the cement's biocompatibility as an approximate twofold increase in cell proliferation for 10% COS-containing cements was observed on day 3 as compared with the controls. The combination of GLT and COS was chosen due to the benefits achieved from several synergistic effects and for their clinical applications. Cement with 5% GLT and 10% COS may be a better choice among cements in terms of anti-washout properties and biological activity.

  20. Amiloride-enhanced gene transfection of octa-arginine functionalized calcium phosphate nanoparticles.

    Directory of Open Access Journals (Sweden)

    Juan Ramón Vanegas Sáenz

    Full Text Available Nanoparticles represent promising gene delivery systems in biomedicine to facilitate prolonged gene expression with low toxicity compared to viral vectors. Specifically, nanoparticles of calcium phosphate (nCaP, the main inorganic component of human bone, exhibit high biocompatibility and good biodegradability and have been reported to have high affinity for protein or DNA, having thus been used as gene transfer vectors. On the other hand, Octa-arginine (R8, which has a high permeability to cell membrane, has been reported to improve intracellular delivery systems. Here, we present an optimized method for nCaP-mediated gene delivery using an octa-arginine (R8-functionalized nCaP vector containing a marker or functional gene construct. nCaP particle size was between 220-580 nm in diameter and all R8-functionalized nCaPs carried a positive charge. R8 concentration significantly improved nCaP transfection efficiency with high cell compatibility in human mesenchymal stem cells (hMSC and human osteoblasts (hOB in particular, suggesting nCaPs as a good option for non-viral vector gene delivery. Furthermore, pre-treatment with different endocytosis inhibitors identified that the endocytic pathway differed among cell lines and functionalized nanoparticles, with amiloride increasing transfection efficiency of R8-functionalized nCaPs in hMSC and hOB.

  1. Growth and characterization of calcium hydrogen phosphate dihydrate crystals from single diffusion gel technique

    Energy Technology Data Exchange (ETDEWEB)

    Rajendran, K.; Dale Keefe, C. [Department of Chemistry, Cape Breton University, Sydney, Nova Scotia (Canada)

    2010-09-15

    Calcium hydrogen phosphate dihydrate (CaHPO{sub 4}.2H{sub 2}O, CHPD) a dissolved mineral in urine is known to cause renal or bladder stones in both human and animals. Growth of CHPD or brushite using sodium metasilicate gel techniques followed by light and polarizing microscopic studies revealed its structural and morphological details. Crystal identity by powder x-ray diffraction confirmed the FT-IR and FT-Raman spectroscopic techniques as alternate methods for fast analysis of brushite crystals which could form as one type of renal stones. P-O-P asymmetric stretchings in both FT-IR (987.2, 874.1 and 792 cm{sup -1}) and FT-Raman (986.3 cm{sup -1}, 1057.6 cm{sup -1} and 875.2 cm{sup -1}) were found as characteristics of brushite crystals. Differential Scanning Calorimetry (DSC) analysis revealed brushite crystallization purity using gel method by studying their endothermic peaks. This study incorporated a multidisciplinary approach in characterizing CHPD crystals grown in vitro to help formulate prevention or dissolution strategy in controlling urinary stone growth. Initial studies with 0.2 M citric acid ions as controlling agent in the nucleation of brushite crystals further support the presented approach. (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  2. Calcium Phosphate Bioceramics: A Review of Their History, Structure, Properties, Coating Technologies and Biomedical Applications

    Science.gov (United States)

    Eliaz, Noam; Metoki, Noah

    2017-01-01

    Calcium phosphate (CaP) bioceramics are widely used in the field of bone regeneration, both in orthopedics and in dentistry, due to their good biocompatibility, osseointegration and osteoconduction. The aim of this article is to review the history, structure, properties and clinical applications of these materials, whether they are in the form of bone cements, paste, scaffolds, or coatings. Major analytical techniques for characterization of CaPs, in vitro and in vivo tests, and the requirements of the US Food and Drug Administration (FDA) and international standards from CaP coatings on orthopedic and dental endosseous implants, are also summarized, along with the possible effect of sterilization on these materials. CaP coating technologies are summarized, with a focus on electrochemical processes. Theories on the formation of transient precursor phases in biomineralization, the dissolution and reprecipitation as bone of CaPs are discussed. A wide variety of CaPs are presented, from the individual phases to nano-CaP, biphasic and triphasic CaP formulations, composite CaP coatings and cements, functionally graded materials (FGMs), and antibacterial CaPs. We conclude by foreseeing the future of CaPs. PMID:28772697

  3. Lithium doped calcium phosphate cement maintains physical mechanical properties and promotes osteoblast proliferation and differentiation.

    Science.gov (United States)

    Li, Li; Wang, Renchong; Li, Baichuan; Liang, Wei; Pan, Haobo; Cui, Xu; Tang, Jingli; Li, Bing

    2017-07-01

    Calcium phosphate cement (CPC) has been widely used in bone tissue repairing due to its physical mechanical properties and biocompatibility. Addition of trace element to CPC has shown promising evidence to improve the physical properties and biological activities of CPC. Lithium (Li) has effect on osteoblast proliferation and differentiation. In this study, we incorporated Li to CPC and examined the physical properties of Li/CPC and its effect on osteoblast proliferation and differentiation. We found that Li doped CPC maintained similar setting time, pore size distribution, compressive strength, composition, and morphology as CPC without Li. Additionally, Li doped CPC improved osteoblast proliferation and differentiation significantly compared to CPC without Li. To our knowledge, our results, for the first time, show that Li doped CPC has beneficial effect on osteoblast in cell culture while keeps the excellent physical-mechanical properties of CPC. This study will lead to potential application of Li doped CPC in bone tissue engineering. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 944-952, 2017. © 2016 Wiley Periodicals, Inc.

  4. The decreased of Streptococcus Mutans growth after topical application of phosphopeptide amorphous calcium phosphate paste

    Directory of Open Access Journals (Sweden)

    Tika Faradina Araf

    2011-07-01

    Full Text Available Casein Phosphopeptide-Amorphous Calcium Phosphate (CPP-ACP paste is a topical application substance that consisted of a series of milk derivative peptide as a result of phosphorylation and has an antibacterial activity. The objective of this research was to find out the difference of Streptococcus mutans growth before and after CPP-ACP paste given topically to child's teeth. The method of the research was a quasi-experiment. Research samples were 10 students of MI Al Falah Islamic Boarding School, Jatinangor, West Jawa Indonesia and collected with purposive sampling technique. This research used dental plaque from child's teeth before and after applicated by CPP-ACP paste. The plaque was cultivated in selective media Tryptone Yeast Cysteine Sucrose Bacitracin (TYCSB with repeated twice. Streptococcus mutans colony in TYCSB were counted by Stuart colony counter and statistically analyzed based on paired t-test. The results showed the average of Streptococcus mutans growth before applicated CPP-ACP paste was 57.05, whereas after applicated CPP-ACP paste for 1 days was 9.4; for 3 days was 2.85, and for 14 days was 1.7 colony. The research concluded that there was a decrease of Streptococcus mutans growth in isolate plaque after CPP-ACP paste topically given to child's teeth.

  5. Np(V)O2+ sorption on hydroxyapatite-effect of calcium and phosphate anions

    International Nuclear Information System (INIS)

    Thakur, P.; Choppin, G.R.; Moore, R.C.

    2006-01-01

    The sorption of NpO 2 + from aqueous solution on hydroxyapatite was studied as a function of the amount of sorbent, initial NpO 2 + concentration, ionic strength and pcH. The hydroxyapatite was characterized by SEM, EDS, XRD, FT-IR and ICP-MS measurements. At ionic strengths of 0.10 to 5.00 M NaClO 4 , the sorption increased with increased pcH to a maximum between pcH 8-8.5, then decreased as the pcH increased. The kinetics of NpO 2 + sorption on hydroxyapatite followed Lagergren first order kinetics. The temperature dependence of sorption was small in the range of 273-283 K, but increased more sharply at higher temperatures of 298-333 K. The heat of sorption of NpO 2 + was endothermic and the free energy values were exothermic indicating large, positive entropy. The activation energy for the sorption process was calculated to be 29.52 ± 1.2 kJ/mole. The effect of calcium and phosphate on NpO 2 + sorption was studied as a function of concentration and pcH. (orig.)

  6. Photoacoustic spectroscopy applied to the optical characterization of calcium phosphates for biomedical use

    Energy Technology Data Exchange (ETDEWEB)

    Mendez G, M. [ESFM-IPN, 07738 Mexico D.F. (Mexico); Cruz O, A. [CINVESTAV, Dept. of Physics, 07360 Mexico D.F. (Mexico)

    2007-07-01

    Full text: Photoacoustic Spectroscopy (PAS), based on the Rosencwaig and Gersho model, has been used for thermal and optical characterization of diverse materials. The use of PAS has become an important tool because is a nondestructive and no contact analytical technique. Furthermore its use to measure optical absorption spectra has advantages over the usual transmission measurements due to important features as the fact that scattered light does not disturb the measurements significantly and also the sample don't need to be prepared to have good quality surfaces. Then the optical properties of biological samples can be easily investigated with this technique. In the present study PAS is applied to obtain the optical absorption spectra of hydroxyapatite (HAp) [Ca{sub 10} (PO{sub 4} ){sub 6} (OH ){sub 2}] and bioactive calcium phosphates. The spectra of these samples ranged from 300 to 800 nm. All samples were prepared in a power form with particle size < 741m. Complementary studies X-ray diffraction and EDC were performed. (Author)

  7. 3D Printing of Calcium Phosphate Ceramics for Bone Tissue Engineering and Drug Delivery.

    Science.gov (United States)

    Trombetta, Ryan; Inzana, Jason A; Schwarz, Edward M; Kates, Stephen L; Awad, Hani A

    2017-01-01

    Additive manufacturing, also known as 3D printing, has emerged over the past 3 decades as a disruptive technology for rapid prototyping and manufacturing. Vat polymerization, powder bed fusion, material extrusion, and binder jetting are distinct technologies of additive manufacturing, which have been used in a wide variety of fields, including biomedical research and tissue engineering. The ability to print biocompatible, patient-specific geometries with controlled macro- and micro-pores, and to incorporate cells, drugs and proteins has made 3D-printing ideal for orthopaedic applications, such as bone grafting. Herein, we performed a systematic review examining the fabrication of calcium phosphate (CaP) ceramics by 3D printing, their biocompatibility in vitro, and their bone regenerative potential in vivo, as well as their use in localized delivery of bioactive molecules or cells. Understanding the advantages and limitations of the different 3D printing approaches, CaP materials, and bioactive additives through critical evaluation of in vitro and in vivo evidence of efficacy is essential for developing new classes of bone graft substitutes that can perform as well as autografts and allografts or even surpass the performance of these clinical standards.

  8. Calcium phosphate coating containing silver shows high antibacterial activity and low cytotoxicity and inhibits bacterial adhesion

    Energy Technology Data Exchange (ETDEWEB)

    Ando, Yoshiki, E-mail: andoy@jmmc.jp [Division of Microbiology, Department of Pathology and Microbiology, Faculty of Medicine, Saga University, 5-1-1 Nabeshima, Saga 849-8501 (Japan); Research Department, Japan Medical Materials Corporation, Uemura Nissei Bldg.9F 3-3-31 Miyahara, Yodogawa-ku, Osaka 532-0003 (Japan); Miyamoto, Hiroshi [Division of Microbiology, Department of Pathology and Microbiology, Faculty of Medicine, Saga University, 5-1-1 Nabeshima, Saga 849-8501 (Japan); Noda, Iwao; Sakurai, Nobuko [Research Department, Japan Medical Materials Corporation, Uemura Nissei Bldg.9F 3-3-31 Miyahara, Yodogawa-ku, Osaka 532-0003 (Japan); Akiyama, Tomonori [Division of Microbiology, Department of Pathology and Microbiology, Faculty of Medicine, Saga University, 5-1-1 Nabeshima, Saga 849-8501 (Japan); Yonekura, Yutaka; Shimazaki, Takafumi; Miyazaki, Masaki; Mawatari, Masaaki; Hotokebuchi, Takao [Department of Orthopaedic Surgery, Faculty of Medicine, Saga University, 5-1-1 Nabeshima, Saga 849-8501 (Japan)

    2010-01-01

    Surgical site infection is one of the serious complications of orthopedic implants. In order to reduce the incidence of implant-associated infections, we developed a novel coating technology of calcium phosphate (CP) containing silver (Ag), designated Ag-CP coating, using a thermal spraying technique. In this study, we evaluated the antibacterial efficacy and biological safety of this coating. In vitro antibacterial activity tests showed that the growths of Escherichia coli, Staphylococcus aureus and methicillin-resistant S. aureus (MRSA) are completely suppressed on Ag-CP coating. In vitro bacterial adherence tests revealed that the number of adherent bacteria on the surface of this coating is significantly less (p < 0.02) than that on the surface of the CP coating. Moreover, the Ag-CP coating completely inhibits MRSA adhesion [<10 colony-forming units (CFU)] when 10{sup 2} CFU MRSA is inoculated. On the other hand, V79 Chinese hamster lung cells were found to grow on the Ag-CP coating as well as on the CP coating in a cytotoxicity test. These results indicate that the Ag-CP coating on the surface of orthopedic implants exhibits antibacterial activity and inhibits bacterial adhesion without cytotoxicity.

  9. 3D Printing of Calcium Phosphate Ceramics for Bone Tissue Engineering and Drug Delivery

    Science.gov (United States)

    Trombetta, Ryan; Inzana, Jason A.; Schwarz, Edward M.; Kates, Stephen L.; Awad, Hani A.

    2016-01-01

    Additive manufacturing, also known as 3D printing, has emerged over the past 3 decades as a disruptive technology for rapid prototyping and manufacturing. Vat polymerization, powder bed fusion, material extrusion, and binder jetting are distinct technologies of additive manufacturing, which have been used in a wide variety of fields, including biomedical research and tissue engineering. The ability to print biocompatible, patient-specific geometries with controlled macro- and micropores, and to incorporate cells, drugs and proteins has made 3D-printing ideal for orthopaedic applications, such as bone grafting. Herein, we performed a systematic review examining the fabrication of calcium phosphate (CaP) ceramics by 3D printing, their biocompatibility in vitro, and their bone regenerative potential in vivo, as well as their use in localized delivery of bioactive molecules or cells. Understanding the advantages and limitations of the different 3D printing approaches, CaP materials, and bioactive additives through critical evaluation of in vitro and in vivo evidence of efficacy is essential for developing new classes of bone graft substitutes that can perform as well as autografts and allografts or even surpass the performance of these clinical standards. PMID:27324800

  10. Injection laryngoplasty using BIOPEX calcium phosphate cement. The Sanokousei General Hospital experience

    International Nuclear Information System (INIS)

    Okubo, Keisuke; Shinnabe, Akihiro; Saito, Koichiro; Shiotani, Akihiro

    2008-01-01

    The calcium phosphate bone paste BIOPEX is an injectable material developed as a bone replacement that hardens into a hydroxylapatite block after injection. BIOPEX offers many advantages as a material for injection laryngoplasty: it induces little foreign-material reaction, is minimally absorbed, and is easy to prepare in the OR. Between 2004 and 2007, 14 patients, including 13 with vocal fold paralysis and 1 with severe atrophy of the vocal folds, were treated with BIOPEX-injection laryngoplasty at Sanokousei General Hospital. The injection of BIOPEX is usually performed through a direct laryngoscopy under general anesthesia, and no adverse effects were observed in any of the cases. A postoperative three-dimensional CT revealed successful injection of the BIOPEX into the paraglottic space in all cases. BIOPEX is minimally absorbed over long time periods, and this procedure results in a dramatic improvement of glottic function immediately after surgery. We consider this operative technique, which aims at medialization of the vocal fold by injection of a sclerotic agent into the lateral side of the vocal fold, as 'type I thyroplasty from inside the laryngeal framework.' (author)

  11. Biological influence of Ca/P ratio on calcium phosphate coatings by sol-gel processing.

    Science.gov (United States)

    Catauro, M; Papale, F; Sapio, L; Naviglio, S

    2016-08-01

    The objective of this work has been to develop low temperature sol-gel glass coatings to modify the substrate surface and to evaluate their bioactivity and biocompatibility. Glasses, based on SiO2·CaO·P2O5, were synthesized by the sol-gel technique using tetraethyl orthosilicate, calcium nitrate tetrahydrate and triethyl phosphate as precursors of SiO2, CaO and P2O5, respectively. Those materials, still in the sol phase, have been used to coat substrates by means of the dip-coating technique. Attenuated total reflectance Fourier transform infrared (ATR-FTIR) has been used for characterize coatings and a microstructural analysis has been obtained using scanning electron microscopy (SEM). The potential applications of the coatings in the biomedical field were evaluated by bioactivity and biocompatibility tests. The coated substrate was immersed in simulated body fluid (SBF) for 21days and the hydroxyapatite deposition on its surface was subsequently evaluated via SEM-EDXS analysis, as an index of bone-bonding capability. In order to study the cell behavior and response to our silica based materials, prepared via the sol-gel method, with various Ca/P ratio and coating substrate, we have used the human osteoblast-like U2OS cell line. Copyright © 2016 Elsevier B.V. All rights reserved.

  12. Determination of calcium to phosphate elemental ratio in natural hydroxypatite using LIBS

    Science.gov (United States)

    Mazalan, Elham; Chaudhary, Kashif; Haider, Zuhaib; Hadi, Siti Fatimah Abd; Ali, Jalil

    2018-05-01

    In this work, laser induced breakdown spectroscopy (LIBS) is employed for determination of calcium to phosphate (Ca/P) ratio in hydroxyapatite (HA) extracted from animal bones. HA was extracted from the biological bones of lamb, bovine, and fish separately. Fresh bones were boiled in deuterium-depleted water (DDW) for 4 hours and immersed it in acetone for 15 hours followed by drying process in the oven. Dried bones were heated at 600 °C and crushed into powder form which was then mixed with potassium bromide (KBr) in a known quantity. The mixture for each sample was palletized into pellets of identical mass using a hydraulic press. The palletized samples of HA extracted from the bones were ablated with 10 ns Q-switched Nd-YAG laser pulses having an energy of 320 mJ/pulse. The optical emissions produced from the laser induced plasma were recorded. Ca and P emission lines are identified and the Ca/P is calculated. Ca/P ratio by LIBS analysis has been verified by EDX measurements and are found in good agreement.

  13. In Vitro Evaluation of Dentin Tubule Occlusion for Novel Calcium Lactate Phosphate (CLP Paste

    Directory of Open Access Journals (Sweden)

    Jen-Chang Yang

    2017-02-01

    Full Text Available Introduction: The objective of this in vitro study is to evaluate the effective and long-term occlusion of dentinal tubules using a novel calcium lactate phosphate (CLP based desensitizing agent. Methods: Dentin disks (n = 9 were pre-etched using 1 M lactic acid for 30 s and individually treated with Colgate® Pro-Relief™ paste, CLP paste, and double distilled water (ddH2O by a rubber-cupped handpiece. Dentin disks were analyzed under optical micrographs for pre-treatment, directly after treatment, and 14 days post-treatment. One-way ANOVA and post-hoc Tukey’s test were used to determine whether there were any statistically significant differences in dentinal tubule diameter. Results: A significant decrease occurred in the mean tubule diameter for dentin disks treated with CLP paste. A decrease was observed from 3.52 ± 0.83 µm to 2.62 ± 0.42 µm right after treatment, further decreasing to 1.71 ± 0.45 µm after immersion in artificial saliva for 14 days (p < 0.05. Conclusions: The results suggest that the CLP based desensitizing paste has remineralization properties and provides instant and lasting effectiveness in dentinal tubule occlusion.

  14. Interaction Of Calcium Phosphate Nanoparticles With Human Chorionic Gonadotropin Modifies Secondary And Tertiary Protein Structure

    Directory of Open Access Journals (Sweden)

    Al-Hakeim Hussein K

    2015-12-01

    Full Text Available Calcium phosphate nanoparticles (CaPNP have good biocompatibility and bioactivity inside human body. In this study, the interaction between CaPNP and human chorionic gonadotropin (hCG was analyzed to determine the changes in the protein structure in the presence of CaPNP and the quantity of protein adsorbed on the CaPNP surface. The results showed a significant adsorption of hCG on the CaPNP nanoparticle surface. The optimal fit was achieved using the Sips isotherm equation with a maximum adsorption capacity of 68.23 µg/mg. The thermodynamic parameters, including ∆H° and ∆G°, of the adsorption process are positive, whereas ∆S° is negative. The circular dichroism results of the adsorption of hCG on CaPNP showed the changes in its secondary structure; such changes include the decomposition of α-helix strand and the increase in β-pleated sheet and random coil percentages. Fluorescence study indicated minimal changes in the tertiary structure near the microenvironment of the aromatic amino acids such as tyrosine and phenyl alanine caused by the interaction forces between the CaPNP and hCG protein. The desorption process showed that the quantity of the hCG desorbed significantly increases as temperature increases, which indicates the weak forces between hCG and the surface.

  15. Calcium phosphate coated Keratin-PCL scaffolds for potential bone tissue regeneration.

    Science.gov (United States)

    Zhao, Xinxin; Lui, Yuan Siang; Choo, Caleb Kai Chuen; Sow, Wan Ting; Huang, Charlotte Liwen; Ng, Kee Woei; Tan, Lay Poh; Loo, Joachim Say Chye

    2015-04-01

    The incorporation of hydroxyapatite (HA) nanoparticles within or on the surface of electrospun polymeric scaffolds is a popular approach for bone tissue engineering. However, the fabrication of osteoconductive composite scaffolds via benign processing conditions still remains a major challenge to date. In this work, a new method was developed to achieve a uniform coating of calcium phosphate (CaP) onto electrospun keratin-polycaprolactone composites (Keratin-PCL). Keratin within PCL was crosslinked to decrease its solubility, before coating of CaP. A homogeneous coating was achieved within a short time frame (~10min) by immersing the scaffolds into Ca(2+) and (PO4)(3-) solutions separately. Results showed that the incorporation of keratin into PCL scaffolds not only provided nucleation sites for Ca(2+) adsorption and subsequent homogeneous CaP surface deposition, but also facilitated cell-matrix interactions. An improvement in the mechanical strength of the resultant composite scaffold, as compared to other conventional coating methods, was also observed. This approach of developing a biocompatible bone tissue engineering scaffold would be adopted for further in vitro osteogenic differentiation studies in the future. Copyright © 2015 Elsevier B.V. All rights reserved.

  16. Gold nanoparticles in injectable calcium phosphate cement enhance osteogenic differentiation of human dental pulp stem cells.

    Science.gov (United States)

    Xia, Yang; Chen, Huimin; Zhang, Feimin; Bao, Chongyun; Weir, Michael D; Reynolds, Mark A; Ma, Junqing; Gu, Ning; Xu, Hockin H K

    2018-01-01

    In this study, a novel calcium phosphate cement containing gold nanoparticles (GNP-CPC) was developed. Its osteogenic induction ability on human dental pulp stem cells (hDPSCs) was investigated for the first time. The incorporation of GNPs improved hDPSCs behavior on CPC, including better cell adhesion (about 2-fold increase in cell spreading) and proliferation, and enhanced osteogenic differentiation (about 2-3-fold increase at 14 days). GNPs endow CPC with micro-nano-structure, thus improving surface properties for cell adhesion and subsequent behaviors. In addition, GNPs released from GNP-CPC were internalized by hDPSCs, as verified by transmission electron microscopy (TEM), thus enhancing cell functions. The culture media containing GNPs enhanced the cellular activities of hDPSCs. This result was consistent with and supported the osteogenic induction results of GNP-CPC. In conclusion, GNP-CPC significantly enhanced the osteogenic functions of hDPSCs. GNPs are promising to modify CPC with nanotopography and work as bioactive additives thus enhance bone regeneration. Copyright © 2017 Elsevier Inc. All rights reserved.

  17. Structural studies of calcium phosphate doped with titanium and zirconium obtained by high-energy mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Silva, C C; Sombra, A S B [Telecommunications and Materials Science and Engineering Laboratory (LOCEM), Physics Department, Federal University of Ceara, Campus do Pii, Postal Code 6030, 60455-760, Fortaleza-Ceara (Brazil)], E-mail: sombra@fisica.ufc.br

    2009-12-15

    In this paper, we present a new variation of the solid-state procedure on the synthesis of bioceramics with titanium (CapTi) and zirconium (CapZr), considering that zirconium (ZrO{sub 2}) and titanium oxide (TiO{sub 2}) are strengthening agents, due to their superb force and fracture toughness. The high efficiency of the calcination process opens a new way of producing commercial amounts of nanocrystalline bioceramics. In this work, a new variation of the solid-state procedure method was used to produce nanocrystalline powders of titanium and zirconium, using two different experimental chemical routes: CapTi: Ca(H{sub 2}PO{sub 4}){sub 2}+TiO{sub 2} and CapZr: Ca(H{sub 2}PO{sub 4}){sub 2}+ZrO{sub 2}. The powders were submitted to calcination processes (CapTic and CapZrc) at 800, 900 and 1000 deg. C. The calcium titanium phosphate phase, CaTi{sub 4}P{sub 6}O{sub 24}, was obtained in the CapTic reaction and the calcium zirconium phosphate, CaZr{sub 4}P{sub 6}O{sub 24}, was obtained in the CapZrc reaction. The obtained ceramics were characterized by x-ray powder diffraction (XRD), infrared (IR) spectroscopy, Raman scattering spectroscopy (RSS) and scanning electron microscopy (SEM) analysis. This method was compared with the milling process (CapTim and CapZrm), where in the last process the melting is not necessary and the powder obtained is nanocrystalline. The calcium titanium phosphate phase, CaTi{sub 4}P{sub 6}O{sub 24}, was obtained in the reaction CapTim, but in CapZrm the formation of any calcium phosphate phase even after 15 h of dry mechanical alloying was not observed.

  18. Determination of the Ca/P ratio in calcium phosphates during the precipitation of hydroxyapatite using X-ray diffractometry

    Directory of Open Access Journals (Sweden)

    Zoltan Z. Zyman

    2013-06-01

    Full Text Available The applicability of the X-ray powder diffraction method to the determination of phase composition and Ca/P ratio in precipitates during the nitrous wet synthesis of hydroxyapatite (HA has been shown. The plotted dependences of the phase composition and the Ca/P ratio on the synthesis time can be used as initial data for the development of new and simple processing routes of calcium phosphate ceramics based on HA of any desired composition.

  19. Assessment of bone healing ability of calcium phosphate cements loaded with platelet lysate in rat calvarial defects.

    Science.gov (United States)

    Babo, Pedro S; Carvalho, Pedro P; Santo, Vítor E; Faria, Susana; Gomes, Manuela E; Reis, Rui L

    2016-11-01

    Injectable calcium phosphate cements have been used as a valid alternative to autologous bone grafts for bone augmentation with the additional advantage of enabling minimally invasive implantation procedures and for perfectly fitting the tissue defect. Nevertheless, they have low biodegradability and lack adequate biochemical signaling to promote bone healing and remodeling. In previous in vitro studies, we observed that the incorporation of platelet lysate directly into the cement paste or loaded in hyaluronic acid microspheres allowed to modulate the cement degradation and the in vitro expression of osteogenic markers in seeded human adipose derived stem cells. The present study aimed at investigating the possible effect of this system in new bone formation when implanted in calvarial bilateral defects in rats. Different formulations were assessed, namely plain calcium phosphate cements, calcium phosphate cements loaded with human platelet lysate, hybrid injectable formulations composed of the calcium phosphate cement incorporating hyaluronin acid non-loaded microparticles (20% hyaluronin acid) or with particles loaded with platelet lysate. The degradability and new bone regrowth were evaluated in terms of mineral volume in the defect, measured by micro-computed tomography and histomorphometric analysis upon 4, 8 and 12 weeks of implantation. We observed that the incorporation of hyaluronin acid microspheres induced an overly rapid cement degradation, impairing the osteoconductive properties of the cement composites. Moreover, the incorporation of platelet lysate induced higher bone healing than the materials without platelet lysate, up to four weeks after surgery. Nevertheless, this effect was not found to be significant when compared to the one observed in the sham-treated group. © The Author(s) 2016.

  20. Characterization of calcium, phosphate and peroxide interactions in activation of mitochondrial swelling using derivative of the swelling curves

    Czech Academy of Sciences Publication Activity Database

    Drahota, Zdeněk; Endlicher, R.; Staňková, P.; Rychtrmoc, D.; Milerová, Marie; Červinková, Z.

    2012-01-01

    Roč. 44, č. 3 (2012), s. 309-315 ISSN 0145-479X R&D Projects: GA MZd(CZ) NT12370 Grant - others:GA ČR(CZ) GP305/09/P145 Institutional support: RVO:67985823 Keywords : mitochondrial swelling * mitochondrial permeability transition pore * Calcium, phosphate and peroxide interactions Subject RIV: FG - Pediatrics Impact factor: 1.604, year: 2012

  1. Production and characterization of setting hydraulic cements based on calcium phosphate; Obtencao e caracterizacao de cimentos de fosfato de calcio de pega hidraulica

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, Luci C. de; Rigo, Eliana C.S.; Santos, Luis A dos; Boschi, Anselmo Ortega [Sao Carlos Univ., SP (Brazil). Dept. de Engenharia de Materiais; Carrodeguas, Raul G. [Universidad de La Habana, Habana (Cuba). Centro de Biomateriales

    1997-12-31

    Setting hydraulic cements based on calcium phosphate has risen great interest in scientific literature during recent years due to their total bio compatibility and to the fact that they harden `in situ`, providing easy handling and adaptation to the shape and dimensions of the defect which requires correction, differently from the predecessors, the calcium phosphate ceramics (Hydroxy apatite, {beta}-tri calcium phosphate, biphasic, etc) in the shape of dense or porous blocks and grains. In the work, three calcium-phosphate cement compositions were studied. The resulting compositions were characterized according to the following aspects: setting times, pH, mechanical resistance, crystalline phases, microstructure and solubility in SBF (Simulated Body Fluid). The results show a potential use for the compositions. (author) 6 figs., 4 tabs.

  2. Three dimensional printed calcium phosphate and poly(caprolactone) composites with improved mechanical properties and preserved microstructure.

    Science.gov (United States)

    Vella, Joseph B; Trombetta, Ryan P; Hoffman, Michael D; Inzana, Jason; Awad, Hani; Benoit, Danielle S W

    2018-03-01

    Biphasic calcium phosphate scaffolds formed via three dimensional (3D) printing technology to exhibit porosity and chemical resorbability to promote osseointegration often lack the strength and toughness required to withstand loading in bone tissue engineering applications. Herein, sintering and CaP:poly(caprolactone) (PCL) composite formation were explored to improve 3D printed scaffold strength and toughness. Hydroxyapatite and α-tricalcium phosphate (α-TCP) biphasic calcium powders were printed using phosphoric acid binder, which generated monetite and hydroxyapatite scaffolds. Upon sintering, evolution of β-TCP was observed along with an increase in flexural strength and modulus but no effect on fracture toughness was observed. Furthermore, scaffold porosity increased with sintering. Additionally, two techniques of PCL composite formation were employed: postprint precipitation and 3D print codeposition to further augment scaffold mechanical properties. While both techniques significantly improved flexural strength, flexural modulus, and fracture toughness under most conditions explored, precipitation yielded more substantial increases in these properties, which is attributed to better continuity of the PCL phase. However, precipitation also compromised surface porosity due to PCL passivation of the calcium phosphate surface, which may subsequently hinder scaffold integration and bone regeneration. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 106A: 663-672, 2018. © 2017 Wiley Periodicals, Inc.

  3. Potentiostatic pulse-deposition of calcium phosphate on magnesium alloy for temporary implant applications--an in vitro corrosion study.

    Science.gov (United States)

    Kannan, M Bobby; Wallipa, O

    2013-03-01

    In this study, a magnesium alloy (AZ91) was coated with calcium phosphate using potentiostatic pulse-potential and constant-potential methods and the in vitro corrosion behaviour of the coated samples was compared with the bare metal. In vitro corrosion studies were carried out using electrochemical impedance spectroscopy and potentiodynamic polarization in simulated body fluid (SBF) at 37 °C. Calcium phosphate coatings enhanced the corrosion resistance of the alloy, however, the pulse-potential coating performed better than the constant-potential coating. The pulse-potential coating exhibited ~3 times higher polarization resistance than that of the constant-potential coating. The corrosion current density obtained from the potentiodynamic polarization curves was significantly less (~60%) for the pulse-deposition coating as compared to the constant-potential coating. Post-corrosion analysis revealed only slight corrosion on the pulse-potential coating, whereas the constant-potential coating exhibited a large number of corrosion particles attached to the coating. The better in vitro corrosion performance of the pulse-potential coating can be attributed to the closely packed calcium phosphate particles. Copyright © 2012 Elsevier B.V. All rights reserved.

  4. Preliminary research on a novel bioactive silicon doped calcium phosphate coating on AZ31 magnesium alloy via electrodeposition

    Energy Technology Data Exchange (ETDEWEB)

    Qiu, Xun [Department of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094 (China); Institute of Metal Research, Chinese Academy of Science, Shenyang 110016 (China); Wan, Peng, E-mail: pwan@imr.ac.cn [Institute of Metal Research, Chinese Academy of Science, Shenyang 110016 (China); Tan, LiLi [Institute of Metal Research, Chinese Academy of Science, Shenyang 110016 (China); Fan, XinMin [Department of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094 (China); Yang, Ke [Institute of Metal Research, Chinese Academy of Science, Shenyang 110016 (China)

    2014-03-01

    A silicon doped calcium phosphate coating was obtained successfully on AZ31 alloy substrate via pulse electrodeposition. A novel dual-layer structure was observed with a porous lamellar-like and outer block-like apatite layer. In vitro immersion tests were adopted in simulated body fluid within 28 days of immersion. Slow degradation rate obtained from weight loss was observed for the Si-doped Ca–P coating, which was also consistent with the results of electrochemical experiments showing an enhanced corrosion resistance for the coating. Further formation of an apatite-like layer on the surface after immersion proved better integrity and biomineralization performance of the coating. Biological characterization was carried out for viability, proliferation and differentiation of MG63 osteoblast-like cells. The coating showed a good cell growth and an enhanced cell proliferation. Moreover, an increased activity of osteogenic marker ALP was found. All the results demonstrated that the Si-doped calcium phosphate was perspective to be used as a coating for magnesium alloy implants to control the degradation rate and enhance the bioactivity, which would facilitate the rapidity of bone tissue repair. - Highlights: • A Si-doped calcium phosphate coating was achieved via pulse ED on AZ31 alloy. • The coating was composed of a porous lamellar-like layer and outer block-like apatite. • The coating showed slow degradation rate and better biomineralization property. • The coating improved cell proliferation and activity of osteogenic marker ALP.

  5. Preliminary research on a novel bioactive silicon doped calcium phosphate coating on AZ31 magnesium alloy via electrodeposition

    International Nuclear Information System (INIS)

    Qiu, Xun; Wan, Peng; Tan, LiLi; Fan, XinMin; Yang, Ke

    2014-01-01

    A silicon doped calcium phosphate coating was obtained successfully on AZ31 alloy substrate via pulse electrodeposition. A novel dual-layer structure was observed with a porous lamellar-like and outer block-like apatite layer. In vitro immersion tests were adopted in simulated body fluid within 28 days of immersion. Slow degradation rate obtained from weight loss was observed for the Si-doped Ca–P coating, which was also consistent with the results of electrochemical experiments showing an enhanced corrosion resistance for the coating. Further formation of an apatite-like layer on the surface after immersion proved better integrity and biomineralization performance of the coating. Biological characterization was carried out for viability, proliferation and differentiation of MG63 osteoblast-like cells. The coating showed a good cell growth and an enhanced cell proliferation. Moreover, an increased activity of osteogenic marker ALP was found. All the results demonstrated that the Si-doped calcium phosphate was perspective to be used as a coating for magnesium alloy implants to control the degradation rate and enhance the bioactivity, which would facilitate the rapidity of bone tissue repair. - Highlights: • A Si-doped calcium phosphate coating was achieved via pulse ED on AZ31 alloy. • The coating was composed of a porous lamellar-like layer and outer block-like apatite. • The coating showed slow degradation rate and better biomineralization property. • The coating improved cell proliferation and activity of osteogenic marker ALP

  6. The fabrication of nanocomposites via calcium phosphate formation on gelatin–chitosan network and the gelatin influence on the properties of biphasic composites

    International Nuclear Information System (INIS)

    Babaei, Zahra; Jahanshahi, Mohsen; Rabiee, Sayed Mahmood

    2013-01-01

    A novel biodegradable polymer–ceramic nanocomposite which consisted of gelatin (Gel), chitosan (CS), and calcium phosphate (CaP) nanoparticles was prepared based on in situ preparation method. The fabricated biocomposites were characterized by FTIR, X-ray diffraction (XRD), transmission electron microscopy (TEM) as well as scanning electron microscope with X-ray elemental analysis (SEM-EDX). The characterization results confirmed that the crystalline calcium phosphate nanoparticles were mineralized in polymeric matrix and the interaction between Ca2+ in calcium phosphate and functional groups in polymers molecular chains was formed. XRD result showed that in addition to hydroxyapatite (HA), Brushite (BR) and tricalcium phosphate (β-TCP) particles also were formed due to lack of complete penetration of the basic solution into the polymeric matrix. However, SEM image indicated that the polymeric matrix has the controlling role in the particle size of calcium phosphate. The size of particles in three component composites was about 100 nm while in two component composites proved to be more in μm size. TEM observation supported SEM results and showed that the three component composites have calcium phosphate nanoparticles. The elastic modulus and compressive strength of the composites were also improved by the employment of gelatin and chitosan together, which can make them more beneficial for surgical applications. - Highlights: ► A new type of calcium phosphate nanocomposites consisted chitosan and gelatin as polymeric matrix was obtained via in situ precipitation method. ► The formed particles into the polymeric matrix are hydroxyapatite, Brushite and β-tricalcium phosphate. ► The polymer concentration is a predominant factor for inhibiting nucleation and growth of calcium phosphate particles as the particles size was also decreased by increasing the amount of polymeric phase. ► The nano particles formed in three component composites and micro particles

  7. Effect of surface modification of nanofibres with glutamic acid peptide on calcium phosphate nucleation and osteogenic differentiation of marrow stromal cells.

    Science.gov (United States)

    Karaman, Ozan; Kumar, Ankur; Moeinzadeh, Seyedsina; He, Xuezhong; Cui, Tong; Jabbari, Esmaiel

    2016-02-01

    Biomineralization is mediated by extracellular matrix (ECM) proteins with amino acid sequences rich in glutamic acid. The objective of this study was to investigate the effect of calcium phosphate deposition on aligned nanofibres surface-modified with a glutamic acid peptide on osteogenic differentiation of rat marrow stromal cells. Blend of EEGGC peptide (GLU) conjugated low molecular weight polylactide (PLA) and high molecular weight poly(lactide-co-glycolide) (PLGA) was electrospun to form aligned nanofibres (GLU-NF). The GLU-NF microsheets were incubated in a modified simulated body fluid for nucleation of calcium phosphate crystals on the fibre surface. To achieve a high calcium phosphate to fibre ratio, a layer-by-layer approach was used to improve diffusion of calcium and phosphate ions inside the microsheets. Based on dissipative particle dynamics simulation of PLGA/PLA-GLU fibres, > 80% of GLU peptide was localized to the fibre surface. Calcium phosphate to fibre ratios as high as 200%, between those of cancellous (160%) and cortical (310%) bone, was obtained with the layer-by-layer approach. The extent of osteogenic differentiation and mineralization of marrow stromal cells seeded on GLU-NF microsheets was directly related to the amount of calcium phosphate deposition on the fibres prior to cell seeding. Expression of osteogenic markers osteopontin, alkaline phosphatase (ALP), osteocalcin and type 1 collagen increased gradually with calcium phosphate deposition on GLU-NF microsheets. Results demonstrate that surface modification of aligned synthetic nanofibres with EEGGC peptide dramatically affects nucleation and growth of calcium phosphate crystals on the fibres leading to increased osteogenic differentiation of marrow stromal cells and mineralization. Copyright © 2013 John Wiley & Sons, Ltd.

  8. Osteogenic and antimicrobial nanoparticulate calcium phosphate and poly-(D,L-lactide-co-glycolide) powders for the treatment of osteomyelitis

    International Nuclear Information System (INIS)

    Uskoković, Vuk; Hoover, Charles; Vukomanović, Marija; Uskoković, Dragan P.; Desai, Tejal A.

    2013-01-01

    Development of a material for simultaneous sustained and localized delivery of antibiotics and induction of spontaneous regeneration of hard tissues affected by osteomyelitis stands for an important clinical need. In this work, a comparative analysis of the bacterial and osteoblastic cell response to two different nanoparticulate carriers of clindamycin, an antibiotic commonly prescribed in the treatment of bone infection, one composed of calcium phosphate and the other comprising poly-(D,L-lactide-co-glycolide)-coated calcium phosphate, was carried out. Three different non-cytotoxic phases of calcium phosphate, exhibiting dissolution and drug release profiles in the range of one week to two months to one year, respectively, were included in the analysis: monetite, amorphous calcium phosphate and hydroxyapatite. Spherical morphologies and narrow size distribution of both types of nanopowders were confirmed in transmission and scanning electron microscopic analyses. The antibiotic-containing powders exhibited sustained drug release contingent upon the degradation rate of the carrier. Assessment of the antibacterial performance of the antibiotic-encapsulated powders against Staphylococcus aureus, the most common pathogen isolated from infected bone, yielded satisfactory results both in broths and on blood agar plates for all the analyzed powders. In contrast, no cytotoxic behavior was detected upon the incubation of the antibiotic powders with the osteoblastic MC3T3-E1 cell line for up to three weeks. The cells were shown to engage in a close contact with the antibiotic-containing particles, irrespective of their internal or surface phase composition, polymeric or mineral. At the same time, both types of particles upregulated the expression of osteogenic markers osteocalcin, osteopontin, Runx2 and protocollagen type I, suggesting their ability to promote osteogenesis and enhance remineralization of the infected site in addition to eliminating the bacterial source of

  9. An inorganic electroluminescent device using calcium phosphate doped with Eu{sup 3+} as the luminescent layer

    Energy Technology Data Exchange (ETDEWEB)

    Koide, Takuhiro [Department of Chemistry and Chemical Engineering, Yamagata University, 4-3-16 Jonan, Yonezawa-shi, Yamagata 992-8510 (Japan); Ito, Michimasa [Tokai Rika Co. Ltd., 3-260 Toyota, Oguchi-cho, Niwa-gun, Aichi 480-0195 (Japan); Kawai, Takahiro [Department of Biochemical Engineering, Yamagata University, 4-3-16 Jonan, Yonezawa-shi, Yamagata 992-8510 (Japan); Matsushima, Yuta, E-mail: ymatsush@yz.yamagata-u.ac.jp [Department of Chemistry and Chemical Engineering, Yamagata University, 4-3-16 Jonan, Yonezawa-shi, Yamagata 992-8510 (Japan)

    2013-03-20

    Highlights: ► A thin film electroluminescent device was fabricated with a calcium phosphate as the light emitting layer. ► The light emitting layer was formed on the BaTiO{sub 3} disk by a spray pyrolysis method. ► Among the examined calcium phosphates, β-Ca{sub 3}(PO{sub 4}){sub 2}:Eu{sup 3+} showed the best photo- and electroluminescent properties. -- Abstract: In this work, the availability of calcium phosphates for the light emitting layer of a thin-film electroluminescent (TFEL) device was investigated. The goal of this work was to develop an electronic device with ordinary materials such as a calcium phosphate, the principal ingredient of the skeleton of the vertebrate. Compositions of 2CaO·P{sub 2}O{sub 5} (Ca{sub 2}P{sub 2}O{sub 7}), 3CaO·P{sub 2}O{sub 5} (Ca{sub 3}(PO{sub 4}){sub 2}) and 4CaO·P{sub 2}O{sub 5} (Ca{sub 4}O(PO{sub 4}){sub 2}) were examined as the candidates for the light emitting layer. Before composing the TFEL device, the photoluminescence (PL) properties of the three compositions were investigated in the powder form to evaluate the performance as the light emitting layer. Among the examined calcium phosphates, Eu-doped β-Ca{sub 3}(PO{sub 4}){sub 2} showed the best PL properties. It showed typical red-emission from Eu{sup 3+}. The PL intensity was enhanced with the heat-treatment temperature and the optimal temperature was 1250 °C. Then, a TFEL device was prepared by a spray pyrolysis method with the β-Ca{sub 3}(PO{sub 4}){sub 2}:Eu{sup 3+} phosphor layer on a BaTiO{sub 3} disk. The TFEL device exhibited the red emission originating in Eu{sup 3+} at 610 nm under applying alternating voltage. Different from the power sample, the intensity of EL decreased with the heat-treatment temperature from 1000 to 1250 °C. The deterioration of EL at the higher temperatures was attributed to chemical interaction between the phosphor layer and the BaTiO{sub 3} disk.

  10. Osteogenic and antimicrobial nanoparticulate calcium phosphate and poly-(D,L-lactide-co-glycolide) powders for the treatment of osteomyelitis

    Energy Technology Data Exchange (ETDEWEB)

    Uskoković, Vuk, E-mail: vuk21@yahoo.com [Therapeutic Micro and Nanotechnology Laboratory, Department of Bioengineering and Therapeutic Sciences, University of California, San Francisco, CA (United States); Hoover, Charles [Department of Cell and Tissue Biology, University of California, San Francisco, CA (United States); Vukomanović, Marija [Institute of Technical Sciences, Serbian Academy of Sciences and Arts, Belgrade (Serbia); Advanced Materials Department, Jožef Stefan Institute, Ljubljana (Slovenia); Uskoković, Dragan P. [Institute of Technical Sciences, Serbian Academy of Sciences and Arts, Belgrade (Serbia); Desai, Tejal A. [Therapeutic Micro and Nanotechnology Laboratory, Department of Bioengineering and Therapeutic Sciences, University of California, San Francisco, CA (United States)

    2013-08-01

    Development of a material for simultaneous sustained and localized delivery of antibiotics and induction of spontaneous regeneration of hard tissues affected by osteomyelitis stands for an important clinical need. In this work, a comparative analysis of the bacterial and osteoblastic cell response to two different nanoparticulate carriers of clindamycin, an antibiotic commonly prescribed in the treatment of bone infection, one composed of calcium phosphate and the other comprising poly-(D,L-lactide-co-glycolide)-coated calcium phosphate, was carried out. Three different non-cytotoxic phases of calcium phosphate, exhibiting dissolution and drug release profiles in the range of one week to two months to one year, respectively, were included in the analysis: monetite, amorphous calcium phosphate and hydroxyapatite. Spherical morphologies and narrow size distribution of both types of nanopowders were confirmed in transmission and scanning electron microscopic analyses. The antibiotic-containing powders exhibited sustained drug release contingent upon the degradation rate of the carrier. Assessment of the antibacterial performance of the antibiotic-encapsulated powders against Staphylococcus aureus, the most common pathogen isolated from infected bone, yielded satisfactory results both in broths and on blood agar plates for all the analyzed powders. In contrast, no cytotoxic behavior was detected upon the incubation of the antibiotic powders with the osteoblastic MC3T3-E1 cell line for up to three weeks. The cells were shown to engage in a close contact with the antibiotic-containing particles, irrespective of their internal or surface phase composition, polymeric or mineral. At the same time, both types of particles upregulated the expression of osteogenic markers osteocalcin, osteopontin, Runx2 and protocollagen type I, suggesting their ability to promote osteogenesis and enhance remineralization of the infected site in addition to eliminating the bacterial source of

  11. Cells responding to surface structure of calcium phosphate ceramics for bone regeneration.

    Science.gov (United States)

    Zhang, Jingwei; Sun, Lanying; Luo, Xiaoman; Barbieri, Davide; de Bruijn, Joost D; van Blitterswijk, Clemens A; Moroni, Lorenzo; Yuan, Huipin

    2017-11-01

    Surface structure largely affects the inductive bone-forming potential of calcium phosphate (CaP) ceramics in ectopic sites and bone regeneration in critical-sized bone defects. Surface-dependent osteogenic differentiation of bone marrow stromal cells (BMSCs) partially explained the improved bone-forming ability of submicron surface structured CaP ceramics. In this study, we investigated the possible influence of surface structure on different bone-related cells, which may potentially participate in the process of improved bone formation in CaP ceramics. Besides BMSCs, the response of human brain vascular pericytes (HBVP), C2C12 (osteogenic inducible cells), MC3T3-E1 (osteogenic precursors), SV-HFO (pre-osteoblasts), MG63 (osteoblasts) and SAOS-2 (mature osteoblasts) to the surface structure was evaluated in terms of cell proliferation, osteogenic differentiation and gene expression. The cells were cultured on tricalcium phosphate (TCP) ceramics with either micron-scaled surface structure (TCP-B) or submicron-scaled surface structure (TCP-S) for up to 14 days, followed by DNA, alkaline phosphatase (ALP) and quantitative polymerase chain reaction gene assays. HBVP were not sensitive to surface structure with respect to cell proliferation and osteogenic differentiation, but had downregulated angiogenesis-related gene expression (i.e. vascular endothelial growth factor) on TCP-S. Without additional osteogenic inducing factors, submicron-scaled surface structure enhanced ALP activity and osteocalcin gene expression of human (h)BMSCs and C2C12 cells, favoured the proliferation of MC3T3-E1, MG63 and SAOS-2, and increased ALP activity of MC3T3-E1 and SV-HFO. The results herein indicate that cells with osteogenic potency (either osteogenic inducible cells or osteogenic cells) could be sensitive to surface structure and responded to osteoinductive submicron-structured CaP ceramics in cell proliferation, ALP production or osteogenic gene expression, which favour bone

  12. Calcium-phosphate and parathyroid intradialytic profiles: A potential aid for tailoring the dialysate calcium content of patients on different hemodialysis schedules.

    Science.gov (United States)

    Ferraresi, Martina; Pia, Anna; Guzzo, Gabriella; Vigotti, Federica Neve; Mongilardi, Elena; Nazha, Marta; Aroasio, Emiliano; Gonella, Cinzia; Avagnina, Paolo; Piccoli, Giorgina Barbara

    2015-10-01

    Severe hyperparathyroidism is a challenge on hemodialysis. The definition of dialysate calcium (Ca) is a pending issue with renewed importance in cases of individualized dialysis schedules and of portable home dialysis machines with low-flow dialysate. Direct measurement of calcium mass transfer is complex and is imprecisely reflected by differences in start-to-end of dialysis Ca levels. The study was performed in a dialysis unit dedicated to home hemodialysis and to critical patients with wide use of daily and tailored schedules. The Ca-phosphate (P)-parathyroid hormone (PTH) profile includes creatinine, urea, total and ionized Ca, albumin, sodium, potassium, P, PTH levels at start, mid, and end of dialysis. "Severe" secondary hyperparathyroidism was defined as PTH > 300 pg/mL for ≥3 months. Four schedules were tested: conventional dialysis (polysulfone dialyzer 1.8-2.1 m(2) ), with dialysate Ca 1.5 or 1.75 mmol/L, NxStage (Ca 1.5 mmol/L), and NxStage plus intradialytic Ca infusion. Dosages of vitamin D, calcium, phosphate binders, and Ca mimetic agents were adjusted monthly. Eighty Ca-P-PTH profiles were collected in 12 patients. Serum phosphate was efficiently reduced by all techniques. No differences in start-to-end PTH and Ca levels on dialysis were observed in patients with PTH levels dialysis on all schedules except on Nxstage (P dialysis, in "severe" secondary hyperparathyroid patients in order to increase the therapeutic potentials of the new dialysis techniques. © 2015 International Society for Hemodialysis.

  13. Strontium hydroxyapatite and strontium carbonate as templates for the precipitation of calcium-phosphates in the absence and presence of fluoride

    Science.gov (United States)

    Sternitzke, Vanessa; Janousch, Markus; Heeb, Michèle B.; Hering, Janet G.; Johnson, C. Annette

    2014-06-01

    The heterogeneous precipitation of calcium-phosphates on calcium hydroxyapatite (Ca10(PO4)6(OH)2 or HAP) in the presence and absence of fluoride is important in the formation of bone and teeth, protection against tooth decay, dental and skeletal fluorosis and defluoridation of drinking water. Strontium hydroxyapatite (Sr10(PO4)6(OH)2 or SrHAP) and strontium carbonate (SrCO3) were used as calcium-free seed templates in precipitation experiments conducted with varying initial calcium-to-phosphate (Ca/P) or calcium-to-phosphate-to-fluoride (Ca/P/F) ratios. Suspensions of SrHAP or SrCO3 seed templates (which were calcium-limited for both templates and phosphate-limited in the case of SrCO3) were reacted at pH 7.3 (25 °C) over 3 days. The resulting solids were examined with Scanning Transmission Electron Microscopy (STEM), X-ray Diffraction (XRD), Fourier Transform Infrared (FTIR), and X-ray Photoelectron Spectroscopy (XPS), X-ray Absorption Near Edge Structure (XANES), and Extended X-ray Absorption Fine Structure spectroscopy (EXAFS). Calcium apatite was the predominant phase identified by all techniques independent of the added Ca/P ratios and of the presence of fluoride. It was not possible to make an unambiguous distinction between HAP and fluorapatite (Ca10(PO4)6F2, FAP). The apatite was calcium-deficient and probably contained some strontium.

  14. Mg substituted apatite coating from alkali conversion of acidic calcium phosphate

    Energy Technology Data Exchange (ETDEWEB)

    Navarro da Rocha, Daniel, E-mail: dnr.navarro@gmail.com [Military Institute of Engineering-IME, Pça. Gen. Tiburcio, 80, P. Vermelha, Urca, Rio de Janeiro, R.J. (Brazil); Cruz, Leila Rosa de Oliveira [Military Institute of Engineering-IME, Pça. Gen. Tiburcio, 80, P. Vermelha, Urca, Rio de Janeiro, R.J. (Brazil); Campos, José Brant de [Rio de Janeiro State University - UERJ, Rio de Janeiro, R.J. (Brazil); Marçal, Rubens L. Santana Blazutti [Military Institute of Engineering-IME, Pça. Gen. Tiburcio, 80, P. Vermelha, Urca, Rio de Janeiro, R.J. (Brazil); Mijares, Dindo Q.; Coelho, Paulo G. [Department of Biomaterials and Biomimetics, New York University College of Dentistry (NYU), New York, NY (United States); Prado da Silva, Marcelo H. [Military Institute of Engineering-IME, Pça. Gen. Tiburcio, 80, P. Vermelha, Urca, Rio de Janeiro, R.J. (Brazil)

    2017-01-01

    In this work, two solutions were developed: the first, rich in Ca{sup 2+}, PO{sub 4}{sup 3−} ions and the second, rich in Ca{sup 2+}, PO{sub 4}{sup 3−} and Mg{sup 2+}, defined as Mg-modified precursor solution. For each Mg-modified precursor solution, the concentrations of Mg{sup 2+} ions were progressively increased by 5%, 10% and 15%wt. The aims of this research were to investigate the influence of magnesium ions substitution in calcium phosphate coatings on titanium surface and to evaluate these coatings by bioactivity assay in McCoy culture medium. The obtained coatings were characterized by X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) analysis, and the presence of Mg ions was confirmed by the inductively coupled plasma atomic emission spectroscopy (ICP) analysis. In vitro bioactivity assay in McCoy culture medium showed bioactivity after 14 days in incubation for the HA and 10% Mg-monetite coatings. The high chemical stability of Mg-HA coatings was verified by the bioactivity assays, and no bone-like apatite deposition, characteristic of bioactivity, was observed for Mg-HA coatings, for the time period used in this study. - Highlights: • The presence of Mg ions influenced the final apatite phase present in the produced coatings. • A lower efficiency in heterogeneous deposition and an exposure of Ti substrate in 5% Mg-monetite coatings was soon verified. • McCoy culture medium was effective in predicting the coatings bioactivity.

  15. Biological influence of Ca/P ratio on calcium phosphate coatings by sol-gel processing

    Energy Technology Data Exchange (ETDEWEB)

    Catauro, M., E-mail: michelina.catauro@unina2.it [Department of Industrial and Information Engineering, Second University of Naples, Via Roma 29 (Italy); Papale, F. [Department of Industrial and Information Engineering, Second University of Naples, Via Roma 29 (Italy); Sapio, L.; Naviglio, S. [Department of Biochemistry, Biophysics and General Pathology, Second University of Naples, Via L. De Crecchio 7, 80138 Naples (Italy)

    2016-08-01

    The objective of this work has been to develop low temperature sol-gel glass coatings to modify the substrate surface and to evaluate their bioactivity and biocompatibility. Glasses, based on SiO{sub 2}·CaO·P{sub 2}O{sub 5}, were synthesized by the sol-gel technique using tetraethyl orthosilicate, calcium nitrate tetrahydrate and triethyl phosphate as precursors of SiO{sub 2}, CaO and P{sub 2}O{sub 5}, respectively. Those materials, still in the sol phase, have been used to coat substrates by means of the dip-coating technique. Attenuated total reflectance Fourier transform infrared (ATR-FTIR) has been used for characterize coatings and a microstructural analysis has been obtained using scanning electron microscopy (SEM). The potential applications of the coatings in the biomedical field were evaluated by bioactivity and biocompatibility tests. The coated substrate was immersed in simulated body fluid (SBF) for 21 days and the hydroxyapatite deposition on its surface was subsequently evaluated via SEM-EDXS analysis, as an index of bone-bonding capability. In order to study the cell behavior and response to our silica based materials, prepared via the sol-gel method, with various Ca/P ratio and coating substrate, we have used the human osteoblast-like U2OS cell line. - Highlights: • Coatings consisting of SiO{sub 2}·CaO·P{sub 2}O{sub 5} glasses were prepared via sol-gel dip coating. • Ca/P molar ratio affects the film morphology and biocompatibility. • Higher cell proliferation was found in response to higher Ca/P ratios coatings. • A growth cell proliferation inhibition was observed in response to lower Ca/P ratio.

  16. Effectiveness of a baking soda toothpaste delivering calcium and phosphate in reducing dentinal hypersensitivity.

    Science.gov (United States)

    Ghassemi, A; Hooper, W; Winston, A E; Sowinski, J; Bowman, J; Sharma, N

    2009-01-01

    The purpose of this controlled clinical trial was to determine the effectiveness and safety of a single-phase dentifrice that delivers calcium, phosphate, and fluoride to the tooth surface (Arm & Hammer Enamel Care for Sensitive Teeth toothpaste, United Kingdom) in reducing dentinal hypersensitivity. Two-hundred and eight qualifying subjects were randomly assigned to either the Enamel Care dentifrice group or a control dentifrice group, and brushed twice daily with their assigned dentifrice for eight weeks. Pain/discomfort in response to a thermal stimulus was assessed at baseline, week 4, and week 8 using a Visual Analogue Scale (VAS; primary outcome variable) and the Schiff Thermal Sensitivity Scale (STSS; secondary outcome variable). After eight weeks, volunteers from the Enamel Care group were switched to the control dentifrice and participated in a second eight-week study to determine the degree of persistence of pain reduction. Both groups had statistically significant VAS score reductions from baseline at weeks 4 and 8, with mean VAS scores in the Enamel Care group decreasing by 45.6% at week 4 and 61.1% at week 8 (p < 0.0001). Enamel Care was statistically significantly more effective than the control at weeks 4 and 8, with respective mean VAS reductions of 63% (p < 0.0001) and 33% (p = 0.0004) greater than the control. Consistent with the VAS score results, the Enamel Care group had respective statistically significant STSS score reductions of 77% and 58% greater than the control group (p < 0.0001). The reductions in dentinal hypersensitivity seen in the Enamel Care group at week 8 persisted for an additional eight weeks, during which the subjects discontinued use of Enamel Care and brushed with the control dentifrice. Enamel Care for Sensitive Teeth toothpaste (United Kingdom) is an effective dentifrice for the management of dentinal hypersensitivity, and its efficacy persists for a least eight weeks following discontinued product use.

  17. Synthesis, characterization and in vitro behavior of nanostructured diopside/biphasic calcium phosphate scaffolds

    Energy Technology Data Exchange (ETDEWEB)

    Ramezani, Samira; Emadi, Rahmatollah; Kharaziha, Mahshid [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Tavangarian, Fariborz, E-mail: f_tavangarian@yahoo.com [Mechanical Engineering Program, School of Science, Engineering and Technology, Penn State Harrisburg, Middletown, PA 17057 (United States)

    2017-01-15

    A significant challenge in bone tissue engineering is the development of 3D constructs serving as scaffolds to fill bone defects, support osteoblasts, and promote bone regeneration. In this paper, highly porous (∼79%) nanostructured diopside/biphasic calcium phosphate (BCP) scaffolds with interconnected porosity were developed using various diopside contents via space holder method. X-ray diffraction (XRD), transmission electron microscopy (TEM) and scanning electron microscopy (SEM) techniques were utilized to evaluate different samples. Furthermore, the effects of scaffold composition on mechanical properties, bioactivity, biodegradability, and cytotoxicity were studied as well. The results showed that the produced scaffolds had an average pore size and density of 200–340 μm and 2.5 ± 0.3–1.8 ± 0.3 gr/cm{sup 3}, respectively, depending on the diopside content. Besides, increasing the diopside content of scaffolds from 0 to 15 wt% enhanced the bioactivity, biodegradability, and compressive strength from 1.2 ± 0.2 to 3.2 ± 0.3 MPa, respectively. In addition, MTT assay also confirmed that the BCP15 scaffold (containing 15 wt% diopside) significantly promoted cell viability and cell adhesion compared to BCP0 scaffold. Overall, our study suggests that nanostructured diopside/BCP scaffolds with improved biological and mechanical properties could potentially be used for bone tissue engineering application. - Highlights: • Highly porous (∼79%) scaffolds were synthesized by space holder method. • Adding diopside nanopowder reduced the average pore size of the scaffolds. • Diopside increased the compressive strength of the scaffolds by three-times. • Nanostructured diopside/BCP scaffolds significantly promoted cell viability. • The nanostructured composite scaffold of BCP15 is cell-friendly.

  18. Electrochemically assisted co-deposition of calcium phosphate/collagen coatings on carbon/carbon composites

    Energy Technology Data Exchange (ETDEWEB)

    Zhao Xueni [C/C Composites Technology Research Center, State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi' an, Shaanxi 710072 (China); Hu Tao [C/C Composites Technology Research Center, State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi' an, Shaanxi 710072 (China); Department of Cardiology, Xijing Hospital, Fourth Military Medical University, Xi' an, Shaanxi 710032 (China); Li Hejun, E-mail: lihejun@nwpu.edu.cn [C/C Composites Technology Research Center, State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi' an, Shaanxi 710072 (China); Chen Mengdi; Cao Sheng; Zhang Leilei [C/C Composites Technology Research Center, State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi' an, Shaanxi 710072 (China); Hou Xianghui [Department of Mechanical, Materials and Manufacturing Engineering, University of Nottingham, University Park, Nottingham NG7 2RD (United Kingdom)

    2011-02-01

    Calcium phosphate (CaP)/collagen coatings were prepared on the surface of carbon/carbon (C/C) composites by electrochemically assisted co-deposition technique. The effects of collagen concentration in the electrolyte on morphology, structure and composition of the coatings were systematically investigated using scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier transformed infrared (FTIR) spectroscopy and X-ray photoelectron spectroscopy (XPS). The adhesive strength of the coatings was also evaluated by scratch tests and tensile bond tests. It was demonstrated that the coatings of three-dimensional collagen network structure was formed on the C/C composites from the electrolyte containing collagen. The surface of the collagen network was covered by uniform CaP aggregates. The coatings were actually composites of CaP and collagen. Hydroxyapatite (HA) was a favorable composition in the coatings with the increase of the collagen concentration in the electrolyte. The formed collagen network increased the cohesive and adhesive strength of the coatings. The adhesive strength between the coatings and substrates increased as the collagen concentration in the electrolyte increased. The coatings prepared at the collagen concentration of 500 mg/L in the electrolyte were not scraped off until the applied load reached 32.0 {+-} 2.2 N and the average tensile adhesive strength of the coatings was 4.83 {+-} 0.71 MPa. After C/C coated with composite coatings (500 mg/L) being immersed in a 10{sup -3} M Ca (OH){sub 2} solution at 30-33 deg. C for 96 h, nano-structured HA/collagen coatings similar to the natural human bone were obtained on the C/C.

  19. A self-setting iPSMSC-alginate-calcium phosphate paste for bone tissue engineering.

    Science.gov (United States)

    Wang, Ping; Song, Yang; Weir, Michael D; Sun, Jinyu; Zhao, Liang; Simon, Carl G; Xu, Hockin H K

    2016-02-01

    Calcium phosphate cements (CPCs) are promising for dental and craniofacial repairs. The objectives of this study were to: (1) develop an injectable cell delivery system based on encapsulation of induced pluripotent stem cell-derived mesenchymal stem cells (iPSMSCs) in microbeads; (2) develop a novel tissue engineered construct by dispersing iPSMSC-microbeads in CPC to investigate bone regeneration in an animal model for the first time. iPSMSCs were pre-osteoinduced for 2 weeks (OS-iPSMSCs), or transduced with bone morphogenetic protein-2 (BMP2-iPSMSCs). Cells were encapsulated in fast-degradable alginate microbeads. Microbeads were mixed with CPC paste and filled into cranial defects in nude rats. Four groups were tested: (1) CPC-microbeads without cells (CPC control); (2) CPC-micr