Dimensional stability of wood-plastic composites reinforced with potassium methyl siliconate modified fiber and sawdust made from beetle-killed trees

Science.gov (United States)

Cheng Piao; Zhiyong Cai; Nicole M. Stark; Charles J. Montezun

2014-01-01

Wood fromtwovarieties of beetle-killed trees was used to fabricate wood–plastic composites. Loblolly pine and lodgepole pine beetle-killed trees were defibrated mechanically and thermomechanically, respectively, into fiber. Fiber and sawdust produced from the trees were modified with potassium methyl siliconate (PMS) and injection-molded into fiber/sawdust reinforced...

Tensile strength characteristics of polypropylene composites reinforced with stone groundwood fibers from softwood

OpenAIRE

López, Joan Pere; Méndez González, José Alberto; Espinach Orús, Xavier; Julián Pérez, Fernando; Mutjé Pujol, Pere; Vilaseca Morera, Fabiola

2012-01-01

The behavior of stone groundwood / polypropylene injection-molded composites was evaluated with and without coupling agent. Stone groundwood (SGW) is a fibrous material commonly prepared in a high yield process and mainly used for papermaking applications. In this work, the use of SGW fibers was explored as a reinforcing element of polypropylene (PP) composites. The surface charge density of the composite components was evaluated, as well as the fiber’s length and diameter inside the composit...

Some Chemical Compositional Changes in Miscanthus and White Oak Sawdust Samples during Torrefaction

Directory of Open Access Journals (Sweden)

J. Richard Hess

2012-10-01

Full Text Available Torrefaction tests on miscanthus and white oak sawdust were conducted in a bubbling sand bed reactor to see the effect of temperature and residence time on the chemical composition. Process conditions for miscanthus and white oak sawdust were 250–350 °C for 30–120 min and 220–270 °C for 30 min, respectively. Torrefaction of miscanthus at 250 °C and a residence time of 30 min resulted in a significant decrease in moisture—about 82.68%—but the other components—hydrogen, nitrogen, sulfur, and volatiles—changed only marginally. Increasing torrefaction temperatures to 350 °C with a residence time of 120 min further reduced the moisture content to 0.54%, with a significant decrease in the hydrogen, nitrogen, and volatiles by 58.29%, 14.28%, and 70.45%, respectively. Regression equations developed for the moisture, hydrogen, nitrogen, and volatile content of the samples with respect to torrefaction temperature and time have adequately described the changes in chemical composition based on R2 values of >0.82. Surface plots based on the regression equation indicate that torrefaction temperatures of 280–350 °C with residence times of 30–120 min can help reduce moisture, nitrogen, and volatile content from 1.13% to 0.6%, 0.27% to 0.23%, and 79% to 23%, with respect to initial values. Trends of chemical compositional changes in white oak sawdust are similar to miscanthus. Torrefaction temperatures of 270 °C and a 30 min residence time reduced the moisture, volatiles, hydrogen, and nitrogen content by about 79%, 17.88%, 20%, and 5.88%, respectively, whereas the carbon content increased by about 3.5%.

Development and characterisation of injection moulded, all-polypropylene composites

Directory of Open Access Journals (Sweden)

A. Kmetty

2013-02-01

Full Text Available In this work, all-polypropylene composites (all-PP composites were manufactured by injection moulding. Prior to injection moulding, pre-impregnated pellets were prepared by a three-step process (filament winding, compression moulding and pelletizing. A highly oriented polypropylene multifilament was used as the reinforcement material, and a random polypropylene copolymer (with ethylene was used as the matrix material. Plaque specimens were injection moulded from the pellets with either a film gate or a fan gate. The compression moulded sheets and injection moulding plaques were characterised by shrinkage tests, static tensile tests, dynamic mechanical analysis and falling weight impact tests; the fibre distribution and fibre/matrix adhesion were analysed with light microscopy and scanning electron microscopy. The results showed that with increasing fibre content, both the yield stress and the perforation energy significantly increased. Of the two types of gates used, the fan gate caused the mechanical properties of the plaque specimens to become more homogeneous (i.e., the differences in behaviour parallel and perpendicular to the flow direction became negligible.

Kenaf/PP and EFB/PP: Effect of fibre loading on the mechanical properties of polypropylene composites

Science.gov (United States)

Anuar, N. I. S.; Zakaria, S.; Harun, J.; Wang, C.

2017-07-01

Kenaf and empty fruit bunch (EFB) fibre which are the important natural fibres in Malaysia were studied as nonwoven polymer composites. The effect of fibre loading on kenaf polypropylene and EFB polypropylene nonwoven composite was studied at different mixture ratio. Kenaf polypropylene nonwoven composite (KPNC) and EFB polypropylene nonwoven composite (EPNC) were prepared by carding and needle-punching techniques, followed by a compression moulding at 6 mm thickness. This study was conducted to identify the optimum fibre loading of nonwoven polypropylene composite and their effect on the mechanical strength. The study was designed at 40%, 50%, 60% and 70% of fibre content in nonwoven mat and composite. The tensile strength, flexural strength and compression strength were tested to evaluate the composite mechanical properties. It was found that the mechanical properties for both kenaf and EFB nonwoven composites were influenced by the fibre content. KPNC showed higher mechanical strength than EPNC. The highest flexural strength was obtained at 60% KPNC and the lowest value was showed by 40% EPNC. The tensile and flexural strength for both KPNC and EPNC decreased after the fibre loading of 60%.

Kenaf Fibre Reinforced Polypropylene Composites: Effect of Cyclic Immersion on Tensile Properties

Directory of Open Access Journals (Sweden)

W. H. Haniffah

2015-01-01

Full Text Available This research studied the degradation of tensile properties of kenaf fibre reinforced polypropylene composites due to cyclic immersion into two different solutions, as well as comparison of the developed composites’ tensile properties under continuous and cyclic immersion. Composites with 40% and 60% fibre loadings were immersed in tap water and bleach for 4 cycles. Each cycle consisted of 3 days of immersion and 4 days of conditioning in room temperature (28°C and 55% humidity. The tensile strength and modulus of composites were affected by fibre composition, type of liquid of immersion, and number of cycles. The number of immersion cycles and conditioning caused degradation to tensile strength and modulus of kenaf fibre reinforced polypropylene composites. Continuous and cyclic immersion in bleach caused tensile strength of the composites to differ significantly whereas, for tensile modulus, the difference was insignificant in any immersion and fibre loadings. However, continuous immersion in the bleach reduced the tensile strength of composites more compared to cyclic immersion. These preliminary results suggest further evaluation of the suitability of kenaf fibre reinforced polypropylene composites for potential bathroom application where the composites will be exposed to water/liquid in cyclic manner due to discontinuous usage of bathroom.

Property Relationship in Organosilanes and Nanotubes Filled Polypropylene Hybrid Composites

Directory of Open Access Journals (Sweden)

Alejandra J. Monsiváis-Barrón

2014-10-01

Full Text Available Polypropylene composites with different filler contents were prepared by creating a masterbatch containing 3 wt%. filler. A variety of silanol groups were used to synthetized three compounds in different media trough a sol-gel process with acetic acid, formic acid and ammonium hydroxide as catalysts. Besides, four different nanotubular fillers were also used to analyze their behavior and compare it with the effect caused by the silanol groups. These tubular structures comprise: unmodified halloysite, carbon nanotubes and functionalized halloysite and carbon nanotubes. Morphological characterization in SEM and STEM/TEM showed dispersion in the polypropylene matrix. According to TGA and DSC measurements thermal behavior remain similar for all the composites. Mechanical test in tension demonstrate that modulus of the composites increases for all samples with a major impact for materials containing silanol groups synthetized in formic acid. Rheological measurements show a significantly increment in viscosity for samples containing unmodified and modified carbon nanotubes. No difference was found for samples containing silanol groups and halloysite when compared to neat polypropylene. Finally, the oxygen transmission rate increased for all samples showing high barrier properties only for samples containing natural and functionalized halloysite nanotubes.

Property Relationship in Organosilanes and Nanotubes Filled Polypropylene Hybrid Composites.

Science.gov (United States)

Monsiváis-Barrón, Alejandra J; Bonilla-Rios, Jaime; Sánchez-Fernández, Antonio

2014-10-20

Polypropylene composites with different filler contents were prepared by creating a masterbatch containing 3 wt%. filler. A variety of silanol groups were used to synthetized three compounds in different media trough a sol-gel process with acetic acid, formic acid and ammonium hydroxide as catalysts. Besides, four different nanotubular fillers were also used to analyze their behavior and compare it with the effect caused by the silanol groups. These tubular structures comprise: unmodified halloysite, carbon nanotubes and functionalized halloysite and carbon nanotubes. Morphological characterization in SEM and STEM/TEM showed dispersion in the polypropylene matrix. According to TGA and DSC measurements thermal behavior remain similar for all the composites. Mechanical test in tension demonstrate that modulus of the composites increases for all samples with a major impact for materials containing silanol groups synthetized in formic acid. Rheological measurements show a significantly increment in viscosity for samples containing unmodified and modified carbon nanotubes. No difference was found for samples containing silanol groups and halloysite when compared to neat polypropylene. Finally, the oxygen transmission rate increased for all samples showing high barrier properties only for samples containing natural and functionalized halloysite nanotubes.

Properties analysis of tensile strength, crystallinity degree and microstructure of polymer composite polypropylene-sand

International Nuclear Information System (INIS)

Sudirman; Karo-Karo, Aloma; Ari-Handayani; Bambang-Sugeng; Rukihati; Mashuri

2004-01-01

Materials modification base on polymer toward polymer composite is needed by addition of filler. Mechanical properties such as tensile strength, crystallinity degree and microstructure of polymer composite based on polypropylene with sand filler have been investigated. In this work, the polymer composite has been made by mixing the matrix of polypropylene melt flow 2 (PP MF2) or polypropylene melt flow 10 (PP MF 10) with sand filler in a labo plastomill. The composition of sand filler was varied to 10, 30, 40 and 50 % v/v, a then the composite were casted to the film sheets form. The sheets were characterized mechanically i.e tensile strength, crystallinity degree and microstructure. The result showed that the tensile strength decreased by increasing the volume fraction of sand filler, in accordance with microstructure investigation that the matrix area under zone plastic deformation (more cracks), while the filler experienced elastic deformation, so that the strength mechanism of filler did not achieved with expectation (Danusso and Tieghi theory). For filler more than 30 % of volume fraction, the tensile strength of polypropylene melt flow 10 (PP MF 10) was greater than that polypropylene melt flow 2 (PP MF2). It was caused by plasticities in PP MF 10. The tensile strength of PP MF2 was greater than that PP MF 10 for volume fraction of sand filler less than 30 %. It was caused by PP MF2 to be have more degree of crystallinity

Flexural creep behaviour of jute polypropylene composites

Science.gov (United States)

Chandekar, Harichandra; Chaudhari, Vikas

2016-09-01

Present study is about the flexural creep behaviour of jute fabric reinforced polypropylene (Jute-PP) composites. The PP sheet and alkali treated jute fabric is stacked alternately and hot pressed in compression molding machine to get Jute-PP composite laminate. The flexural creep study is carried out on dynamic mechanical analyzer. The creep behaviour of the composite is modeled using four-parameter Burgers model. Short-term accelerated creep testing is conducted which is later used to predict long term creep behaviour. The feasibility of the construction of a master curve using the time-temperature superposition (TTS) principle to predict long term creep behavior of unreinforced PP and Jute-PP composite is investigated.

Susceptibility to scratch surface damage of wollastonite- and talc-containing polypropylene micrometric composites

International Nuclear Information System (INIS)

Hadal, R.; Dasari, A.; Rohrmann, J.; Misra, R.D.K.

2004-01-01

The paper describes the effect of wollastonite and talc on the scratch deformation behavior of low and high crystallinity polypropylenes under identical test conditions. The vertical resolution of atomic force microscopy and lateral resolution of scanning electron microscopy is utilized to examine the characteristics of scratch damage. Contrary to the expectations that high crystallinity and stiffness of polypropylene composites should increase resistance to scratch deformation, the susceptibility to mechanical deformation depends on bonding of mineral particles to the polymer matrix. Scratch deformed regions in neat polypropylenes were free of voids and grooves, while reinforced-polypropylenes exhibited voids and debonding/detachment of filler particles. The severity of plastic deformation in reinforced polypropylenes is a function of debonding/detachment of mineral particles, which is comparatively more for talc-reinforced polypropylenes than wollastonite-reinforced polypropylenes because of the layered structure of talc that encourages delamination. Usage of coating and coupling agents improved the resistance to scratch deformation by promoting adhesion and bonding between the reinforcement and matrix

Bio-composites fabricated by sandwiching sisal fibers with polypropylene (PP)

Energy Technology Data Exchange (ETDEWEB)

Sosiati, H., E-mail: hsosiati@gmail.com [Nanomaterials Research Group, LPPT Universitas Gadjah Mada (Indonesia); Nahyudin, A., E-mail: ahmadnahyudin@yahoo.co.id; Fauzi, I., E-mail: ikhsannurfauzi@gmail.com; Wijayanti, D. A., E-mail: wijayantidwiastuti@gmail.com [Department of Physics, Faculty of Mathematics and Natural Sciences, Gadjah Mada University (Indonesia); Triyana, K., E-mail: triyana@ugm.ac.id [Nanomaterials Research Group, LPPT Universitas Gadjah Mada (Indonesia); Department of Physics, Faculty of Mathematics and Natural Sciences, Gadjah Mada University (Indonesia)

2016-04-19

Sisal fibers reinforced polypropylene (PP) composites were successfully fabricated using sandwiching sisal fibers with PP sheets. The ratio of fiber and polymer matrix was 50:50 (wt. %). Untreated short and long sisal fibers, and alkali treated short sisal fibers in 6% NaOH at 100°C for 1 and 3 h were used as reinforcement or fillers. A small amount (3 wt. %) of maleic anhydride grafted polypropylene (MAPP) was added as a coupling agent. Scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) spectroscopy were used to characterize the surface morphology and chemical composition of the fibers, respectively. Flexural test of sisal/PP composites was done according to ASTM D 790-02. The results showed that flexural strength of untreated long fiber reinforced composite is much higher than that of the untreated and alkali treated short fibers reinforced composites with and without the addition of MAPP. Alkalization related to fiber surface modification, fiber length/fiber orientation and a composite fabrication technique are important factors in contributing to the fiber distribution within the matrix, the bonding between the fiber and the matrix and the enhancement of flexural strength of the bio-composite.

Bio-composites fabricated by sandwiching sisal fibers with polypropylene (PP)

International Nuclear Information System (INIS)

Sosiati, H.; Nahyudin, A.; Fauzi, I.; Wijayanti, D. A.; Triyana, K.

2016-01-01

Sisal fibers reinforced polypropylene (PP) composites were successfully fabricated using sandwiching sisal fibers with PP sheets. The ratio of fiber and polymer matrix was 50:50 (wt. %). Untreated short and long sisal fibers, and alkali treated short sisal fibers in 6% NaOH at 100°C for 1 and 3 h were used as reinforcement or fillers. A small amount (3 wt. %) of maleic anhydride grafted polypropylene (MAPP) was added as a coupling agent. Scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) spectroscopy were used to characterize the surface morphology and chemical composition of the fibers, respectively. Flexural test of sisal/PP composites was done according to ASTM D 790-02. The results showed that flexural strength of untreated long fiber reinforced composite is much higher than that of the untreated and alkali treated short fibers reinforced composites with and without the addition of MAPP. Alkalization related to fiber surface modification, fiber length/fiber orientation and a composite fabrication technique are important factors in contributing to the fiber distribution within the matrix, the bonding between the fiber and the matrix and the enhancement of flexural strength of the bio-composite.

Bio-composites fabricated by sandwiching sisal fibers with polypropylene (PP)

Science.gov (United States)

Sosiati, H.; Nahyudin, A.; Fauzi, I.; Wijayanti, D. A.; Triyana, K.

2016-04-01

Sisal fibers reinforced polypropylene (PP) composites were successfully fabricated using sandwiching sisal fibers with PP sheets. The ratio of fiber and polymer matrix was 50:50 (wt. %). Untreated short and long sisal fibers, and alkali treated short sisal fibers in 6% NaOH at 100°C for 1 and 3 h were used as reinforcement or fillers. A small amount (3 wt. %) of maleic anhydride grafted polypropylene (MAPP) was added as a coupling agent. Scanning electron microscopy (SEM) and Fourier transform infrared (FTIR) spectroscopy were used to characterize the surface morphology and chemical composition of the fibers, respectively. Flexural test of sisal/PP composites was done according to ASTM D 790-02. The results showed that flexural strength of untreated long fiber reinforced composite is much higher than that of the untreated and alkali treated short fibers reinforced composites with and without the addition of MAPP. Alkalization related to fiber surface modification, fiber length/fiber orientation and a composite fabrication technique are important factors in contributing to the fiber distribution within the matrix, the bonding between the fiber and the matrix and the enhancement of flexural strength of the bio-composite.

A novel approach in organic waste utilization through biochar addition in wood/polypropylene composites

Energy Technology Data Exchange (ETDEWEB)

Das, Oisik [Department of Civil and Environmental Engineering, University of Auckland, Auckland 1142 (New Zealand); Sarmah, Ajit K., E-mail: a.sarmah@auckland.ac.nz [Department of Civil and Environmental Engineering, University of Auckland, Auckland 1142 (New Zealand); Bhattacharyya, Debes [Department of Mechanical Engineering, Center for Advanced Composite Materials, University of Auckland, Auckland 1142 (New Zealand)

2015-04-15

Highlights: • Biochar made from waste wood was added with wood polypropylene composites. • 24% biochar gave the best mechanical properties. • 6% biochar had no effect on physico-mechanical properties of composites. • Coupling agent remained unreacted in composites having higher amount of biochar. - Abstract: In an attempt to concurrently address the issues related to landfill gas emission and utilization of organic wastes, a relatively novel idea is introduced to develop biocomposites where biochar made from pyrolysis of waste wood (Pinus radiata) is added with the same wood, plastic/polymer (polypropylene) and maleated anhydride polypropylene (MAPP). Experiments were conducted by manufacturing wood and polypropylene composites (WPCs) mixed with 6 wt%, 12 wt%, 18 wt%, 24 wt%, and 30 wt% biochar. Though 6 wt% addition had similar properties to that of the control (composite without biochar), increasing biochar content to 24 wt% improved the composite’s tensile/flexural strengths and moduli. The biochar, having high surface area due to fine particles and being highly carbonised, acted as reinforcing filler in the biocomposite. Composites having 12 wt% and 18 wt% of biochar were found to be the most ductile and thermally stable, respectively. This study demonstrates that, WPCs added with biochar has good potential to mitigate wastes while simultaneously producing biocomposites having properties that might be suited for various end applications.

A novel approach in organic waste utilization through biochar addition in wood/polypropylene composites

International Nuclear Information System (INIS)

Das, Oisik; Sarmah, Ajit K.; Bhattacharyya, Debes

2015-01-01

Highlights: • Biochar made from waste wood was added with wood polypropylene composites. • 24% biochar gave the best mechanical properties. • 6% biochar had no effect on physico-mechanical properties of composites. • Coupling agent remained unreacted in composites having higher amount of biochar. - Abstract: In an attempt to concurrently address the issues related to landfill gas emission and utilization of organic wastes, a relatively novel idea is introduced to develop biocomposites where biochar made from pyrolysis of waste wood (Pinus radiata) is added with the same wood, plastic/polymer (polypropylene) and maleated anhydride polypropylene (MAPP). Experiments were conducted by manufacturing wood and polypropylene composites (WPCs) mixed with 6 wt%, 12 wt%, 18 wt%, 24 wt%, and 30 wt% biochar. Though 6 wt% addition had similar properties to that of the control (composite without biochar), increasing biochar content to 24 wt% improved the composite’s tensile/flexural strengths and moduli. The biochar, having high surface area due to fine particles and being highly carbonised, acted as reinforcing filler in the biocomposite. Composites having 12 wt% and 18 wt% of biochar were found to be the most ductile and thermally stable, respectively. This study demonstrates that, WPCs added with biochar has good potential to mitigate wastes while simultaneously producing biocomposites having properties that might be suited for various end applications

Effect of particles size on mechanical properties of polypropylene particulate composites

Czech Academy of Sciences Publication Activity Database

Nezbedová, E.; Krčma, F.; Majer, Z.; Hutař, Pavel

2016-01-01

Roč. 7, č. 5 (2016), s. 690-699 ISSN 1757-9864 Institutional support: RVO:68081723 Keywords : Morphology * Mechanical properties * Numerical simulation * Polypropylene particulate composite s * Plasma surface treatment Subject RIV: JI - Composite Material s www.emeraldinsight.com/1757-9864.htm

Quality improvement of pyrolysis oil from waste rubber by adding sawdust

International Nuclear Information System (INIS)

Wang, Wen-liang; Chang, Jian-min; Cai, Li-ping; Shi, Sheldon Q.

2014-01-01

Highlights: • Rubber-pyrolysis oil is difficult to be fuel due to high proportion of PAHs. • The efficiency of pyrolysis was increased as the percentage of sawdust increased. • The adding of sawdust improved pyrolysis oil quality by reducing the PAHs content. • Adding sawdust reduced nitrogen/sulfur in oil and was easier to convert to diesel. - Abstract: This work was aimed at improving the pyrolysis oil quality of waste rubber by adding larch sawdust. Using a 1 kg/h stainless pyrolysis reactor, the contents of sawdust in rubber were gradually increased from 0%, 50%, 100% and 200% (wt%) during the pyrolysis process. Using a thermo-gravimetric (TG) analyzer coupled with Fourier transform infrared (FTIR) analysis of evolving products (TG–FTIR), the weight loss characteristics of the heat under different mixtures of sawdust/rubber were observed. Using the pyrolysis–gas chromatography (GC)–mass spectrometry (Py–GC/MS), the vapors from the pyrolysis processes were collected and the compositions of the vapors were examined. During the pyrolysis process, the recovery of the pyrolysis gas and its composition were measured in-situ at a reaction temperature of 450 °C and a retaining time of 1.2 s. The results indicated that the efficiency of pyrolysis was increased and the residual carbon was reduced as the percentage of sawdust increased. The adding of sawdust significantly improved the pyrolysis oil quality by reducing the polycyclic aromatic hydrocarbons (PAHs) and nitrogen and sulfur compounds contents, resulting in an improvement in the combustion efficiency of the pyrolysis oil

Quality improvement of pyrolysis oil from waste rubber by adding sawdust

Energy Technology Data Exchange (ETDEWEB)

Wang, Wen-liang [MOE Key Laboratory of Wooden Material Science and Application, College of Material Science and Technology, Wood Science and Technology, Beijing Forestry University, 100083 Beijing (China); Chang, Jian-min, E-mail: cjianmin@bjfu.edu.cn [MOE Key Laboratory of Wooden Material Science and Application, College of Material Science and Technology, Wood Science and Technology, Beijing Forestry University, 100083 Beijing (China); Cai, Li-ping [Mechanical and Energy Engineering Department, University of North Texas, 3940 N. Elm, Denton 72076, TX (United States); Shi, Sheldon Q., E-mail: Sheldon.Shi@unt.edu [Mechanical and Energy Engineering Department, University of North Texas, 3940 N. Elm, Denton 72076, TX (United States)

2014-12-15

Highlights: • Rubber-pyrolysis oil is difficult to be fuel due to high proportion of PAHs. • The efficiency of pyrolysis was increased as the percentage of sawdust increased. • The adding of sawdust improved pyrolysis oil quality by reducing the PAHs content. • Adding sawdust reduced nitrogen/sulfur in oil and was easier to convert to diesel. - Abstract: This work was aimed at improving the pyrolysis oil quality of waste rubber by adding larch sawdust. Using a 1 kg/h stainless pyrolysis reactor, the contents of sawdust in rubber were gradually increased from 0%, 50%, 100% and 200% (wt%) during the pyrolysis process. Using a thermo-gravimetric (TG) analyzer coupled with Fourier transform infrared (FTIR) analysis of evolving products (TG–FTIR), the weight loss characteristics of the heat under different mixtures of sawdust/rubber were observed. Using the pyrolysis–gas chromatography (GC)–mass spectrometry (Py–GC/MS), the vapors from the pyrolysis processes were collected and the compositions of the vapors were examined. During the pyrolysis process, the recovery of the pyrolysis gas and its composition were measured in-situ at a reaction temperature of 450 °C and a retaining time of 1.2 s. The results indicated that the efficiency of pyrolysis was increased and the residual carbon was reduced as the percentage of sawdust increased. The adding of sawdust significantly improved the pyrolysis oil quality by reducing the polycyclic aromatic hydrocarbons (PAHs) and nitrogen and sulfur compounds contents, resulting in an improvement in the combustion efficiency of the pyrolysis oil.

Coir fiber reinforced polypropylene composite panel for automotive interior applications

Science.gov (United States)

Nadir Ayrilmis; Songklod Jarusombuti; Vallayuth Fueangvivat; Piyawade Bauchongkol; Robert H. White

2011-01-01

In this study, physical, mechanical, and flammability properties of coconut fiber reinforced polypropylene (PP) composite panels were evaluated. Four levels of the coir fiber content (40, 50, 60, and 70 % based on the composition by weight) were mixed with the PP powder and a coupling agent, 3 wt % maleic anhydride grafted PP (MAPP) powder. The water resistance and the...

Dynamic Mechanical and Thermal Properties of Bagasse/Glass Fiber/Polypropylene Hybrid Composites

Directory of Open Access Journals (Sweden)

Mehdi Roohani

2016-06-01

Full Text Available This work aims to evaluate the thermal and dynamic mechanical properties of bagasse/glass fiber/polypropylene hybrid composites. Composites were prepared by the melt compounding method and their properties were characterized by differential scanning calorimetry (DSC and dynamic mechanical analysis (DMA. DSC results found that with incorporation of bagasse and glass fiber the melting temperature (Tm and the crystallisation temperature (Tc shift to higher temperatures and the degree of crystallinity (Xc increase. These findings suggest that the fibers played the role of a nucleating agent in composites. Dynamic mechanical analysis indicated that by the incorporation of bagasse and glass fiber into polypropylene, the storage modulus ( and the loss modulus ( increase whereas the mechanical loss factor (tanδ decrease. To assess the effect of reinforcement with increasing temperature, the effectiveness coefficient C was calculated at different temperature ranges and revealed that, at the elevated temperatures, improvement of mechanical properties due to the presence of fibers was more noticeable. The fiber-matrix adhesion efficiency determined by calculating of adhesion factor A in terms of the relative damping of the composite (tan δc and the polymer (tan δpand volume fraction of the fibers (Фf. Calculated adhesion factor A values indicated that by adding glass fiber to bagasse/polypropylene system, the fiber-matrix adhesion improve. Hybrid composite containing 25% bagasse and 15% glass fiber showed better fiber-matrix adhesion.

Evaluation of Properties of Unidirectional Hemp/Polypropylene Composites: Influence of Fiber Content and Fiber/Matrix Interface Variables

DEFF Research Database (Denmark)

Plackett, David; Løgstrup Andersen, Tom; Lilholt, Hans

2002-01-01

Flament-wound textile hemp yarn was used in combination with unmodified or maleated polypropylene (PP) films to produce plates of unidirectional composites.......Flament-wound textile hemp yarn was used in combination with unmodified or maleated polypropylene (PP) films to produce plates of unidirectional composites....

Recycling of asbestos tailings used as reinforcing fillers in polypropylene based composites.

Science.gov (United States)

Zhai, Wensi; Wang, Yao; Deng, Yuan; Gao, Hongli; Lin, Zhen; Li, Mao

2014-04-15

In this work, asbestos tailings were recycled and used as reinforcing fillers to enhance the mechanical properties of polypropylene (PP). A silane coupling agent was used to chemically modify the asbestos tailings to increase the compatibility between asbestos tailings and polypropylene matrix. Both raw and chemically treated asbestos tailings with different loading levels (from 3 to 30 wt%) were utilized to fabricate composites. Mechanical properties of these composites have been investigated by dynamic mechanical analysis, tensile test and notched impact test. Results showed that hybridization of asbestos tailings in the composites enhanced the mechanical properties of neat PP evidently, and treated asbestos tailings/PP composites yielded even better mechanical properties compared with those of raw asbestos tailings/PP composites. This recycling method of asbestos tailings not only reduces disposal costs and avoids secondary pollution but also produces a new PP-based composite material with enhanced mechanical properties. Copyright © 2014 Elsevier B.V. All rights reserved.

Spatially Resolved Characterization of Cellulose Nanocrystal-Polypropylene Composite by Confocal Raman Microscopy

Science.gov (United States)

Umesh P. Agarwal; Ronald Sabo; Richard S. Reiner; Craig M. Clemons; Alan W. Rudie

2012-01-01

Raman spectroscopy was used to analyze cellulose nanocrystal (CNC)–polypropylene (PP) composites and to investigate the spatial distribution of CNCs in extruded composite filaments. Three composites were made from two forms of nanocellulose (CNCs from wood pulp and the nanoscale fraction of microcrystalline cellulose) and two of the three composites investigated used...

Analysis of Nanodomain Composition in High-Impact Polypropylene by Atomic Force Microscopy-Infrared.

Science.gov (United States)

Tang, Fuguang; Bao, Peite; Su, Zhaohui

2016-05-03

In this paper, compositions of nanodomains in a commercial high-impact polypropylene (HIPP) were investigated by an atomic force microscopy-infrared (AFM-IR) technique. An AFM-IR quantitative analysis method was established for the first time, which was then employed to analyze the polyethylene content in the nanoscopic domains of the rubber particles dispersed in the polypropylene matrix. It was found that the polyethylene content in the matrix was close to zero and was high in the rubbery intermediate layers, both as expected. However, the major component of the rigid cores of the rubber particles was found to be polypropylene rather than polyethylene, contrary to what was previously believed. The finding provides new insight into the complicated structure of HIPPs, and the AFM-IR quantitative method reported here offers a useful tool for assessing compositions of nanoscopic domains in complex polymeric systems.

Interfacial enhancement of polypropylene composites modified with sorbitol derivatives and siloxane-silsesquioxane resin

Science.gov (United States)

Dobrzyńska-Mizera, Monika; Dutkiewicz, Michał; Sterzyński, Tomasz; Di Lorenzo, Maria Laura

2015-12-01

Composites based on polypropylene (iPP) modified with a sorbitol derivative (NX8000) and siloxane-silsesquioxane resin (SiOPh) containing maleated polypropylene (MAPP) as compatibilizer were prepared by melt extrusion. Calorimetric investigations were carried out using differential scanning calorimetry (DSC), whereas the morphological and mechanical properties were investigated by scanning electron microscopy (SEM) and static tensile tests. DSC measurements revealed no influence of SiOPh and a slight effect of MAPP addition on the crystallization kinetics of polypropylene. Additionally, the introduction of MAPP into the iPP+NX8000+SiOPh composites increased plastic properties of the samples. All the above was attributed to the compatibilizing effect of MAPP which improved interfacial adhesion between iPP, NX8000 and SiOPh. This phenomenon was also confirmed by the SEM images illustrating more homogenous distribution of the filler in the compatibilized samples.

Morphology and properties of recycled polypropylene/bamboo fibers composites

International Nuclear Information System (INIS)

Phuong, Nguyen Tri; Guinault, Alain; Sollogoub, Cyrille; Chuong, Bui

2011-01-01

Polypropylene (PP) is among the most widely used thermoplastics in many industrial fields. However, like other recycled polymers, its properties usually decrease after recycling process and sometimes are degraded to poor properties level for direct re-employment. The recycled products, in general, need to be reinforced to have competitive properties. Short bamboo fibers (BF) have been added in a recycled PP (RPP) with and without compatibilizer type maleic anhydride polypropylene (MAPP). Several properties of composite materials, such as helium gas permeability and mechanical properties before and after ageing in water, were examined. The effects of bamboo fiber content and fiber chemical treatment have been also investigated. We showed that the helium permeability increases if fiber content is higher than 30% because of a poor adhesion between untreated bamboo fiber and polymer matrix. The composites reinforced by acetylated bamboo fibers show better helium permeability due to grafting of acetyl groups onto cellulose fibers surface and thus improves compatibility between bamboo fibers and matrix, which has been shown by microscopic observations. Besides, mechanical properties of composite decrease with ageing in water but the effect is less pronounced with low bamboo fiber content.

Thermal analysis of polypropylene modified by gamma irradiation composites under outdoor conditions

International Nuclear Information System (INIS)

Komatsu, Luiz G.H.; Oliani, Washington L.; Lugao, Ademar B.; Parra, Duclerc F.

2015-01-01

This work reports the influence of the clay in the degradation process of the HMSPP.The polypropylene (PP) was irradiated under acetylene atmosphere in gamma irradiation source ( 60 Co) to obtain the HMSPP (high melt strength polypropylene). Composites of HMSPP were processed in twin-screw extruder with clay Cloisite 20A and Maleic Anhydride (PP-g-MA) as coupling agent. The obtained composites were exposed under outdoor conditions for 6 months. The ageing effects were characterized by Differential Scanning Calorimetry (DSC), Thermogravimetry Analysis (TGA). Chemical oxidation was evaluated by Carbonyl Index (IC) through infrared Spectroscopy (FT-IR). The results showed correlation between carbonyl index and ageing time. (author)

Thermal analysis of polypropylene modified by gamma irradiation composites under outdoor conditions

Energy Technology Data Exchange (ETDEWEB)

Komatsu, Luiz G.H.; Oliani, Washington L.; Lugao, Ademar B.; Parra, Duclerc F., E-mail: dfparra@ipen.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

2015-07-01

This work reports the influence of the clay in the degradation process of the HMSPP.The polypropylene (PP) was irradiated under acetylene atmosphere in gamma irradiation source ({sup 60}Co) to obtain the HMSPP (high melt strength polypropylene). Composites of HMSPP were processed in twin-screw extruder with clay Cloisite 20A and Maleic Anhydride (PP-g-MA) as coupling agent. The obtained composites were exposed under outdoor conditions for 6 months. The ageing effects were characterized by Differential Scanning Calorimetry (DSC), Thermogravimetry Analysis (TGA). Chemical oxidation was evaluated by Carbonyl Index (IC) through infrared Spectroscopy (FT-IR). The results showed correlation between carbonyl index and ageing time. (author)

Thermal degradation and tensile strength of sansevieria trifasciata-polypropylene composites

Science.gov (United States)

Abral, H.; Kenedy, E.

2015-07-01

The paper exhibits thermal degradation and tensile strength of Sansevieria Trifasciata (ST) fibers and polypropylene (PP) composites. Thermal degradation of ST fibers PP composites was conducted by using thermogravimetry (TGA) instrument, meanwhile tensile strength of the composite was done by using tensile equipment. The results show that the thermal resistance of ST fibers PP composites was higher than that of virgin PP only. Increases in volume fraction of fibers in the composites enhance the tensile strength. Scanning Electron Microscope (SEM) observation exhibits good interface bonding between ST fibers and PP matrix.

Thermal degradation and tensile strength of sansevieria trifasciata-polypropylene composites

International Nuclear Information System (INIS)

Abral, H; Kenedy, E

2015-01-01

The paper exhibits thermal degradation and tensile strength of Sansevieria Trifasciata (ST) fibers and polypropylene (PP) composites. Thermal degradation of ST fibers PP composites was conducted by using thermogravimetry (TGA) instrument, meanwhile tensile strength of the composite was done by using tensile equipment. The results show that the thermal resistance of ST fibers PP composites was higher than that of virgin PP only. Increases in volume fraction of fibers in the composites enhance the tensile strength. Scanning Electron Microscope (SEM) observation exhibits good interface bonding between ST fibers and PP matrix. (paper)

Stone-ground wood pulp-reinforced polypropylene composites: Water uptake and thermal properties

Directory of Open Access Journals (Sweden)

Joan Pere López

2012-11-01

Full Text Available Two of the drawbacks of using natural-based composites in industrial applications are thermal instability and water uptake capacity. In this work, mechanical wood pulp was used to reinforce polypropylene at a level of 20 to 50 wt. %. Composites were mixed by means of a Brabender internal mixer for both non-coupled and coupled formulations. Differential scanning calorimetry (DSC and thermogravimetric analysis (TGA were used to determine the thermal properties of the composites. The water uptake behavior was evaluated by immersion of the composites in water until an equilibrium state was reached. Results of water absorption tests revealed that the amount of water absorption was clearly dependent upon the fiber content. The coupled composites showed lower water absorption compared to the uncoupled composites. The incorporation of mechanical wood pulp into the polypropylene matrix produced a clear nucleating effect by increasing the crystallinity degree of the polymer and also increasing the temperature of polymer degradation. The maximum degradation temperature for stone ground wood pulp–reinforced composites was in the range of 330 to 345 ºC.

Surface modification and micromechanical properties of jute fiber mat reinforced polypropylene composites

Directory of Open Access Journals (Sweden)

2007-05-01

Full Text Available A new treating method using sodium hydroxide (NaOH and Maleic anhydride-grafted polypropylene (MPP emulsion was introduced to treat jute fiber mat in order to enhance the performance of jute/polypropylene (PP composite prepared by film stacking method. The surface modifications of jute fiber mat have been found to be very effective in improving the fiber-matrix adhesion. It was shown that treatments changed not only the surface topography but also the distribution of diameter and strength for the jute fibers, which was analyzed by using a two-parameter Weibull distribution model. Consequently, the interfacial shear strength, flexural and tensile strength of the composites all increased, but the impact strength decreased slightly. These results have demonstrated a new approach to use natural materials to enhance the mechanical performances of composites.

Evaluation of the thermal properties of polypropylene reinforced with palm fibers composites

International Nuclear Information System (INIS)

Capri, M.R.; Santana, L.C.; Mulinari, D.R.

2016-01-01

The aim of this study was to characterize polypropylene reinforced with palm composites. Of this form, it was studied physical and chemical modifications of the in nature fibers, washed with hot water and mercerized. The composites of polypropylene reinforced with 5%, 10% and 20% (wt /wt) in nature fibers and mercerized were evaluated thermally. The fibers were characterized by SEM XRD and TGA / DSC techniques. Results revealed that the mercerized fibers presented higher crystallinity when compared to others, as well as increased roughness, facilitating interlacing with the reinforcement matrix. Thermal studies of the fibers showed that the mercerization caused displacement curves paragraph higher temperatures. The composites reinforced with treated fibers presented largest temperatures and enthalpies of degradation. The content of fiber influenced in enthalpy degradation and reduction in fusion temperature. (author)

Study of Tensile Properties and Deflection Temperature of Polypropylene/Subang Pineapple Leaf Fiber Composites

Science.gov (United States)

Hafizhah, R.; Juwono, A. L.; Roseno, S.

2017-05-01

The development of eco-friendly composites has been increasing in the past four decades because the requirement of eco-friendly materials has been increasing. Indonesia has a lot of natural fiber resources and, pineapple leaf fiber is one of those fibers. This study aimed to determine the influence of weight fraction of pineapple leaf fibers, that were grown at Subang, to the tensile properties and the deflection temperature of polypropylene/Subang pineapple leaf fiber composites. Pineapple leaf fibers were pretreated by alkalization, while polypropylene pellets, as the matrix, were extruded into sheets. Hot press method was used to fabricate the composites. The results of the tensile test and Heat Deflection Temperature (HDT) test showed that the composites that contained of 30 wt.% pineapple leaf fiber was the best composite. The values of tensile strength, modulus of elasticity and deflection temperature were (64.04 ± 3.91) MPa; (3.98 ± 0.55) GPa and (156.05 ± 1.77) °C respectively, in which increased 187.36%, 198.60%, 264.72% respectively from the pristine polypropylene. The results of the observation on the fracture surfaces showed that the failure modes were fiber breakage and matrix failure.

Irradiation and processing of oil palm empty fruit bunch fibres - polypropylene composites

International Nuclear Information System (INIS)

Khairul Zaman Mohd Dahlan; Syarifah Hanisah Syed Abdul Aziz

2000-01-01

In this study, polypropylene was blended with oil palm empty fruit bunch fibres at a ratio of 60 to 40 by weight, respectively. Trimethylolpropane triacrylate (TMPTA) was used as the crosslinking agent. Homopolymer Polypropylene of MFI 14.0 and EFB fibres of 0.5 -1.0 mm sizes were used through out the experiment. Processing parameters such as temperature, rotor speed and processing time were optimized. Modes of irradiation were established to determine the optimum properties of the composites. The mechanical properties of the composite such as tensile strength, tensile modulus, flexural strength and flexural modulus were measured. The results indicate that temperature, 185 degree C, with a rotor speed of 40 rpm and 9 minutes processing time are sufficient to produce the optimum mechanical properties of PP/EFB composite. Modes of adding TMPTA into the blend and modes of irradiation also have influenced the properties of the composites

Tough and Reinforced Polypropylene/Kaolin Composites using Modified Kaolin

Science.gov (United States)

Yao, J. L.; Zhu, H. X.; Qi, Y. B.; Guo, M. J.; Hu, Q.; Gao, L.

2018-05-01

Polypropylene (PP)/kaolin composites have been prepared by filling modified kaolin with diethylenetriaminepentaacetic acid (DTPA) into the PP matrix. The surface modification of kaolin particles effectively improves the compatibility between kaolin and PP matrix. It is conducive for uniform dispersion of inorganic particles in the matrix, and enhances the mechanical performance of the composites. Compared with plain kaolin, the mechanical properties of the modified composites exhibit higher tensile strength, bending strength, impact strength and melt index simultaneously. The DTPA modification of kaolin overall enhances the mechanical properties of PP composites. It meets the requirements in various applications, and makes the modified experiment interesting in modern teaching.

Influence of Sawdust Bio-filler on the Tensile, Flexural, and Impact Properties of Mangifera Indica Leaf Stalk Fibre Reinforced Polyester Composites

Directory of Open Access Journals (Sweden)

Heckadka Srinivas Shenoy

2018-01-01

Full Text Available The need to have biodegradable composites is aloft in today’s market as they are environment friendly and are also easy to fabricate. In this study, mangifera indica leaf stalk fibres were used as reinforcement along with saw dust as bio-filler material. Unsaturated isophthalic polyester resin was used as the matrix. The fibres were treated with 6 % vol. NaOH and neutralized with 3 % vol. of dilute HCl. Treatment of sawdust fillers was done by using 2% vol. NaOH solution. Hand layup method and compression moulding technique was used to fabricate the composite laminates. Specimens for evaluating the mechanical properties were prepared by using water jet machining. The results indicated an increase in tensile, flexural and impact strength of composites with addition of sawdust upto 3%. Further addition of the bio-filler resulted in decrease of mechanical properties.

Quality improvement of pyrolysis oil from waste rubber by adding sawdust.

Science.gov (United States)

Wang, Wen-liang; Chang, Jian-min; Cai, Li-ping; Shi, Sheldon Q

2014-12-01

This work was aimed at improving the pyrolysis oil quality of waste rubber by adding larch sawdust. Using a 1 kg/h stainless pyrolysis reactor, the contents of sawdust in rubber were gradually increased from 0%, 50%, 100% and 200% (wt%) during the pyrolysis process. Using a thermo-gravimetric (TG) analyzer coupled with Fourier transform infrared (FTIR) analysis of evolving products (TG-FTIR), the weight loss characteristics of the heat under different mixtures of sawdust/rubber were observed. Using the pyrolysis-gas chromatography (GC)-mass spectrometry (Py-GC/MS), the vapors from the pyrolysis processes were collected and the compositions of the vapors were examined. During the pyrolysis process, the recovery of the pyrolysis gas and its composition were measured in-situ at a reaction temperature of 450 °C and a retaining time of 1.2s. The results indicated that the efficiency of pyrolysis was increased and the residual carbon was reduced as the percentage of sawdust increased. The adding of sawdust significantly improved the pyrolysis oil quality by reducing the polycyclic aromatic hydrocarbons (PAHs) and nitrogen and sulfur compounds contents, resulting in an improvement in the combustion efficiency of the pyrolysis oil. Copyright © 2014 Elsevier Ltd. All rights reserved.

Studies on improvement of mechanical properties of Kenaf-reinforced polypropylene composites

International Nuclear Information System (INIS)

Sarifah Hanisah Syed Abd Aziz; Khairul Zaman Mohd Dahlan

2006-01-01

At present, research in composite materials is being directed at using natural fibres instead of synthetic fibres. Kenaf which is extensively grown in the Far East including Malaysia, has been identified as a bast (stem) fibre with significant market potential. In this work, long and random kenaf fibres were used in the as-received condition and alkalized with a 0.06 M NaOH solution. They were combined with polypropylene thin sheets, sandwiched between layers of kenaf fibres and hot-pressed to form natural fibre composites. The mechanical properties of the composites were investigated to observe the effect of fibre alignment, fibre treatment, the addition of coupling agent and pre-irradiation method used. A general trend was observed whereby alkalized and long fibre composites gave higher flexural modulus and flexural strength compared with random mat and untreated fibres. The long fibre composites also gave a higher work of fracture. However, the correlation between fibre surface treatment and the work of fracture was less clear. The addition of coupling agent at 1% showed a slight improvement on the mechanical performance of the composites whereas pre-irradiation on the polypropylene pellets and fibres before the composite is manufactured showed significant improvement on the mechanical properties. However, the method of moulding used need to be improved to optimize the performance of the composites. (Author)

Wood Sawdust/Natural Rubber Ecocomposites Cross-Linked by Electron Beam Irradiation

Directory of Open Access Journals (Sweden)

Elena Manaila

2016-06-01

Full Text Available The obtaining and characterization of some polymeric eco-composites based on wood sawdust and natural rubber is presented. The natural rubber was cross-linked using the electron beam irradiation. The irradiation doses were of 75, 150, 300 and 600 kGy and the concentrations of wood sawdust were of 10 and 20 phr, respectively. As a result of wood sawdust adding, the physical and mechanical properties such as hardness, modulus at 100% elongation and tensile strength, showed significant improvements. The presence of wood sawdust fibers has a reinforcing effect on natural rubber, similar or better than of mineral fillers. An increase in the irradiation dose leads to the increasing of cross-link density, which is reflected in the improvement of hardness, modulus at 100% elongation and tensile strength of blends. The cross-linking rates, appreciated using the Flory-Rehner equation, have increased with the amount of wood sawdust in blends and with the irradiation dose. Even if the gel fraction values have varied irregularly with the amount of wood sawdust and irradiation dose it was over 90% for all blends, except for the samples without wood sawdust irradiated with 75 kGy. The water uptake increased with increasing of fiber content and decreased with the irradiation dose.

Benzothiazole sulfide compatibilized polypropylene/halloysite nanotubes composites

Energy Technology Data Exchange (ETDEWEB)

Liu Mingxian [Department of Polymer Materials and Engineering, South China University of Technology, Guangzhou 510640 (China); Guo Baochun, E-mail: psbcguo@scut.edu.cn [Department of Polymer Materials and Engineering, South China University of Technology, Guangzhou 510640 (China); Lei Yanda; Du Mingliang; Jia Demin [Department of Polymer Materials and Engineering, South China University of Technology, Guangzhou 510640 (China)

2009-02-15

Clay-philic benzothiazole sulfide, capable of donating electrons, is grafted onto polypropylene (PP) backbones when N-cyclohexyl-2-benzothiazole sulfonamide (CBS), a commonly used accelerator in the tire industry, is included in the processing of PP/halloysite nanotubes (HNTs) composites. CBS decomposes at elevated temperature and yields benzothiazole sulfide radicals, which react with the PP polymeric free radicals generated during the processing of the composites. On the other hand, the benzothiazole group of CBS is reactive to HNTs via electron transferring. The compatibilization between HNTs and PP is thus realized via interfacial grafting and electron transferring mechanism. The interfacial interactions in the compatibilized systems were fully characterized. Compared with the control sample, the dispersion of HNTs and the interfacial bonding are enhanced substantially in the compatibilized composites. The significantly improved mechanical properties and thermal properties of benzothiazole sulfide compatibilized PP/HNTs composites are correlated to the enhanced interfacial property. The present work demonstrates a novel interfacial design via interfacial grafting/electron transferring for the compatibilization of PP/clay composites.

Chapter 1.4: Spatially Resolved Characterization of CNC-Polypropylene composite by Confocal Raman Microscopy

Science.gov (United States)

Umesh Agarwal; Ronald Sabo; Richard Reiner; Craig Clemons; Alan Rudie

2013-01-01

Raman spectroscopy was used to analyze cellulose nanocrystal (CNC)-polypropylene (PP) composites and to investigate the spatial distribution of CNCs in extruded composite filaments. Three composites were made from two forms of nanocellulose (CNCs from wood pulp and the nanoscale fraction of microcrystalline cellulose), and two of the three composites...

Bio-composites based on polypropylene reinforced with Almond Shells particles: Mechanical and thermal properties

International Nuclear Information System (INIS)

Essabir, H.; Nekhlaoui, S.; Malha, M.; Bensalah, M.O.; Arrakhiz, F.Z.; Qaiss, A.; Bouhfid, R.

2013-01-01

Highlights: • Almond Shells (ASs) particles have been used as reinforcement in polypropylene matrix. • The SEBS-g-MA has been used to improve the adhesion between matrix and particles. • The mechanical and thermal properties of the composite have been improved by the AS. - Abstract: In this work, Almond Shells (ASs) particles are used as reinforcement in a thermoplastic matrix as polypropylene (PP). Composites containing Almond Shells (ASs) particles with and without compatibilizer (maleic anhydride grafted polypropylene; SEBS-g-MA) for various particle content (5, 10, 15, 20, 25, 30 wt.%) was investigated by means of studying their mechanical, thermal and rheological properties. The composites were prepared in a twin-screw extruder and assessed by means of X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), tensile testing and Dynamic Mechanical Analysis (DMA). Results show a clear improvement in mechanical and rheological properties from the use of Almond Shells particles in the matrix without and with maleic anhydride compatibilizer, corresponding to a gain in Young’s modulus of 56.2% and 35% respectively, at 30 wt.% particle loading. Thermal analysis revealed that incorporation of particle in the composites resulted in increase in the initial thermal decomposition temperatures

Topological and thermal properties of polypropylene composites based on oil palm biomass

Energy Technology Data Exchange (ETDEWEB)

Bhat, A. H., E-mail: aamir.bhat@petronas.com.my, E-mail: anie-yal88@yahoo.com; Dasan, Y. K., E-mail: aamir.bhat@petronas.com.my, E-mail: anie-yal88@yahoo.com [Department of Fundamental and Applied Sciences, Universiti Teknologi Petronas, 31750 Perak (Malaysia)

2014-10-24

Roughness on pristine and polymer composite surfaces is of enormous practical importance for polymer applications. This study deals with the use of varying quantity of oil palm ash as a nanofiller in a polypropylene based matrix. The oil palm ash sample was preprocessed to break the particles into small diameter by using ultra sonication before using microfluidizer for further deduction in size and homogenization. The oil palm ash was made to undergo many passes through the microfluidizer for fine distribution of particles. Polypropylene based composites containing different loading percentage oil palm ash was granulated by twin screw extruder and then injection molded. The surface morphology of the OPA passed through microfluidizer was analyzed by Tapping Mode - Atomic Force Microscopy (TMAFM). Thermal analysis results showed an increase in the activation energy values. The thermal stability of the composite samples showed improvement as compared to the virgin polymer as corroborated by the on-set degradation temperatures and the temperatures at which 50% degradation occurred.

Topological and thermal properties of polypropylene composites based on oil palm biomass

International Nuclear Information System (INIS)

Bhat, A. H.; Dasan, Y. K.

2014-01-01

Roughness on pristine and polymer composite surfaces is of enormous practical importance for polymer applications. This study deals with the use of varying quantity of oil palm ash as a nanofiller in a polypropylene based matrix. The oil palm ash sample was preprocessed to break the particles into small diameter by using ultra sonication before using microfluidizer for further deduction in size and homogenization. The oil palm ash was made to undergo many passes through the microfluidizer for fine distribution of particles. Polypropylene based composites containing different loading percentage oil palm ash was granulated by twin screw extruder and then injection molded. The surface morphology of the OPA passed through microfluidizer was analyzed by Tapping Mode - Atomic Force Microscopy (TMAFM). Thermal analysis results showed an increase in the activation energy values. The thermal stability of the composite samples showed improvement as compared to the virgin polymer as corroborated by the on-set degradation temperatures and the temperatures at which 50% degradation occurred

Physicochemical Study of Irradiated polypropylene/Organo :Modified Montmorillonite Composites by Using Electron Beam Irradiation Technique

International Nuclear Information System (INIS)

Hassan, M.S.

2008-01-01

Polypropylene/ Organo modified montmorillonite composites (PP/ OMMT) were prepared by melt blending with a twin screw extruder. The thermal properties by thermo gravimetric analysis (TGA), the dispersion of OMMT of macromolecules by X-ray diffraction (XRD), mechanical properties and the morphology by scanning electron microscopy (SEM) were investigated. The effect of electron beam irradiation on these properties was also studied. The results showed an intercalation between the silicate layers and the PP polymer matrix. The (PP/ OMMT) composites exhibit higher thermal stability and lower mechanical properties than pure polypropylene

Analysis and optimization of machining parameters of laser cutting for polypropylene composite

Science.gov (United States)

Deepa, A.; Padmanabhan, K.; Kuppan, P.

2017-11-01

Present works explains about machining of self-reinforced Polypropylene composite fabricated using hot compaction method. The objective of the experiment is to find optimum machining parameters for Polypropylene (PP). Laser power and Machining speed were the parameters considered in response to tensile test and Flexure test. Taguchi method is used for experimentation. Grey Relational Analysis (GRA) is used for multiple process parameter optimization. ANOVA (Analysis of Variance) is used to find impact for process parameter. Polypropylene has got the great application in various fields like, it is used in the form of foam in model aircraft and other radio-controlled vehicles, thin sheets (∼2-20μm) used as a dielectric, PP is also used in piping system, it is also been used in hernia and pelvic organ repair or protect new herrnis in the same location.

Effect of boron and phosphate compounds on physical, mechanical, and fire properties of wood-polypropylene composites

Science.gov (United States)

Nadir Ayrilmis; Turgay Akbulut; Turker Dundar; Robert H. White; Fatih Mengeloglu; Umit Buyuksari; Zeki Candan; Erkan Avci

2012-01-01

Physical, mechanical, and fire properties of the injection-molded wood flour/polypropylene composites incorporated with different contents of boron compounds; borax/boric acid and zinc borate, and phosphate compounds; mono and diammonium phosphates were investigated. The effect of the coupling agent content, maleic anhydride-grafted polypropylene, on the properties of...

Switchgrass (Panicum virgatum L.) as a reinforcing fibre in polypropylene composites

NARCIS (Netherlands)

Oever, van den M.J.A.; Elbersen, H.W.; Keijsers, E.R.P.; Gosselink, R.J.A.; Klerk-Engels, de B.

2003-01-01

In this study the switchgrass (Panicum virgatum L.), a biomass crop being developed in North America and Europe, was tested as a stiffening and reinforcing agent in polypropylene (PP) composites with and without maleic anhydride grafted PP (MAPP) as a compatibiliser and to evaluate the effect of

Effect of ionizing radiation on polypropylene composites reinforced with coconut fibers

Energy Technology Data Exchange (ETDEWEB)

Miranda, Leila F.; Pereira, Nilson C.; Faldini, Sonia B.; Masson, Terezinha J.; Silveira, Luiz H., E-mail: lfmiranda@sti.com.b [Universidade Presbiteriana Mackenzie, Sao Paulo, SP (Brazil). Escola de Engenharia. Curso de Engenharia de Materiais; Silva, Leonardo G. de Andrade e, E-mail: lgasilva@ipen.b [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

2009-07-01

The use of the polymeric composite materials has been increasing but these materials have environmental problems related to the discard. To reduce the discard deleterious effect, coconuts, sisal, as well as sugar cane pulp natural based fiber have been studied to replace the synthetic ones. These fibers embedded in a polymeric matrix plays a similar role as the synthetic ones, in terms of mechanical and thermal properties. The natural fibers are environmentally friendly, easy to recycle and biodegradable. The aim of this work is the study of ionizing radiation effects on the properties of recycled polypropylene composites, reinforced with 10%, 15% and 20% of the coconut fibers, using as coupling agent a substance based on maleic anhydride (MAPP) graphitized polypropylene. The samples were molded by injection, irradiated and submitted to thermal and mechanical tests. The mechanical properties (hardness, impact strength and tensile strength), temperature of thermal distortion (HDT) and Vicat softening temperature of the non irradiated and irradiated composites were determined. The irradiation doses were of 30, 50 and 100kGy in a gamma cell. Regarding the thermal and mechanical properties of non-irradiated samples, the incorporation of coconut fibers to polypropylene resulted in a decrease of impact strength, tensile strength and Vicat softening temperature as well as in an increase in hardness and HDT. This result indicates that the coconut fibers do not act like a reinforcement agent but as biodegradable filler. In the irradiated samples, it was observed a decrease in the impact strength, tensile strength, HDT, and thermal distortion temperature and an increase in the hardness and tensile strength. The Vicat softening temperature shows no change. (author)

Effect of ionizing radiation on polypropylene composites reinforced with coconut fibers

International Nuclear Information System (INIS)

Miranda, Leila F.; Pereira, Nilson C.; Faldini, Sonia B.; Masson, Terezinha J.; Silveira, Luiz H.

2009-01-01

The use of the polymeric composite materials has been increasing but these materials have environmental problems related to the discard. To reduce the discard deleterious effect, coconuts, sisal, as well as sugar cane pulp natural based fiber have been studied to replace the synthetic ones. These fibers embedded in a polymeric matrix plays a similar role as the synthetic ones, in terms of mechanical and thermal properties. The natural fibers are environmentally friendly, easy to recycle and biodegradable. The aim of this work is the study of ionizing radiation effects on the properties of recycled polypropylene composites, reinforced with 10%, 15% and 20% of the coconut fibers, using as coupling agent a substance based on maleic anhydride (MAPP) graphitized polypropylene. The samples were molded by injection, irradiated and submitted to thermal and mechanical tests. The mechanical properties (hardness, impact strength and tensile strength), temperature of thermal distortion (HDT) and Vicat softening temperature of the non irradiated and irradiated composites were determined. The irradiation doses were of 30, 50 and 100kGy in a gamma cell. Regarding the thermal and mechanical properties of non-irradiated samples, the incorporation of coconut fibers to polypropylene resulted in a decrease of impact strength, tensile strength and Vicat softening temperature as well as in an increase in hardness and HDT. This result indicates that the coconut fibers do not act like a reinforcement agent but as biodegradable filler. In the irradiated samples, it was observed a decrease in the impact strength, tensile strength, HDT, and thermal distortion temperature and an increase in the hardness and tensile strength. The Vicat softening temperature shows no change. (author)

Investigating the influence of alkalization on the mechanical and water absorption properties of coconut and sponge fibers reinforced polypropylene composites

Directory of Open Access Journals (Sweden)

Okikiola Ganiu AGBABIAKA

2014-11-01

Full Text Available Natural fibers are products made from renewable agricultural and forestry feedstock, which can include wood, grasses, and crops, as well as wastes and residues. There are two primary ways these fibers are used: to create polymers or as reinforcement and filler. Thermoplastic polymer may be reinforced or filled using natural fibers such as coir, sponge, hemp, flax, or sisal. This paper focused on the influence of alkalization (NaOH treatment on the mechanical and water absorption properties of selected natural fibers (coconut and sponge fibers reinforced polypropylene composites. In this study, coconut and sponge fiber were extracted from its husk by soaking them in water and was dried before it was cut into 10mm length. Those fibers were chemically treated with sodium hydroxide (NaOH in a shaking water bath before it was used as reinforcement in polypropylene composite. The reinforced polypropylene composite was produced by dispersing the coconut fibers randomly in the polypropylene before it was fabricated in a compression molding machine where the composite was produced. The fiber content used were; 2%wt, 4%wt, 6%wt, 8%wt and 10%wt. Tensile and flexural properties was observed from universal testing machine while water absorption test was carried out on the samples for seven (7 days. It was observed that the influence of NaOH treatment highly enhanced the Flexural and water absorption properties of sponge fiber reinforced polypropylene composites than coconut fiber reinforced composite samples.

PEG-template for surface modification of zeolite: A convenient material to the design of polypropylene based composite for packaging films

Directory of Open Access Journals (Sweden)

S. Toommee

2018-06-01

Full Text Available Zeolite was successfully modified by conventional synthetic route. Polyethylene glycol was employed for surface modification of zeolite. The surface of zeolite exhibited therefore hydrophobic properties. Less than 5 wt% of modified zeolites with uniform size and shape were integrated into polypropylene matrix. Mechanical properties of composite exhibited the similar trend compare to neat polypropylene. Oxygen transmission rate and water vapor transmission rate were evaluated and it exhibited the strong potential to be a good candidate material in active packaging. Keywords: Zeolite, Composite, Polypropylene, Packaging, PEG-template

Wear resistance of polypropylene-SiC composite

Science.gov (United States)

Abenojar, J.; Enciso, B.; Martínez, MA; Velasco, F.

2017-05-01

In this work, the wear resistance of thermoplastic composites with a high amount of ceramic is evaluated. Composites made of polypropylene (PP) and silicon carbide (SiC) powder at 50 wt% were used with the final objective of manufacturing ablative materials. This is the first part of a project studying the wear resistance and the mechanical properties of those composites, to be used in applications like habitat industry. In theory, the exposure to high temperature of ablative materials involves the elimination of thermal energy by the sacrifice of surface polymer. In our case, PP will act as a heat sink, up to the reaction temperature (melting or sublimation), where endothermic chemical decomposition into charred material and gaseous products occurs. As the surface is eroded, it is formed a SiC like-foam with improved insulation performance. Composites were produced by extrusion and hot compression. The wear characterization was performed by pin-on-disk test. Wear test was carried out under standard ASTM G99. The parameters were 120 rpm speed, 15 N load, a alumina ball with 6 mm as pin and 1000 m sliding distance. The tracks were also observed by opto-digital microscope.

Wear resistance of polypropylene-SiC composite

International Nuclear Information System (INIS)

Abenojar, J; Enciso, B; Martínez, MA; Velasco, F

2017-01-01

In this work, the wear resistance of thermoplastic composites with a high amount of ceramic is evaluated. Composites made of polypropylene (PP) and silicon carbide (SiC) powder at 50 wt% were used with the final objective of manufacturing ablative materials. This is the first part of a project studying the wear resistance and the mechanical properties of those composites, to be used in applications like habitat industry. In theory, the exposure to high temperature of ablative materials involves the elimination of thermal energy by the sacrifice of surface polymer. In our case, PP will act as a heat sink, up to the reaction temperature (melting or sublimation), where endothermic chemical decomposition into charred material and gaseous products occurs. As the surface is eroded, it is formed a SiC like-foam with improved insulation performance. Composites were produced by extrusion and hot compression. The wear characterization was performed by pin-on-disk test. Wear test was carried out under standard ASTM G99. The parameters were 120 rpm speed, 15 N load, a alumina ball with 6 mm as pin and 1000 m sliding distance. The tracks were also observed by opto-digital microscope. (paper)

Evaluation of the acquirement of nano composites of polypropylene and a bentonite organophilized by different methodologies

International Nuclear Information System (INIS)

Paiva, Lucilene B. de; Morales, Ana R.; Branciforti, Marcia C.; Bretas, Rosario E.S.

2009-01-01

This work describes the organophilization of an argentinean sodium bentonite with a quaternary ammo nium salt, by two methodologies: cation exchange in aqueous dispersion and intercalation in semi-solid medium. The modified samples were used in the preparation of nano composites, with polypropylene as a matrix and polypropylene-graft-maleic anhydride as a coupling agent, through melt intercalation by using a twin-screw micro extruder. The organophilic bentonites were characterized by the swelling capacity test in water and in xylene and by X-ray diffraction, and the nano composites were characterized by X-ray diffraction and transmission electronic microscopy. The results showed that were obtained nano composites with structures partially intercalated and exfoliated. (author)

Application Waste Sawdust as Mixed Polyurethane Insulation in Traditional Cold Storage of Fishing Vessel

Directory of Open Access Journals (Sweden)

Sutopo Purwono Fitri

2017-03-01

Full Text Available In the process of fishing it takes some supplies such as fishing equipment, instrumentation and storage of fish. The traditional fishermen of their fishing days fishing usually only bring ice cubes. Solid plastic polyurethane foam is a mixture solution of polyols and isocyanates, commonly used as an insulating material storage. From the observation waste generated being sawmill sawdust per spindle with diameter of 30 cm and a length of 1 m with 5 times sawmill, Saws 0.8 cm thick produced 0.0088 m³ / burnable logs only discarded. Therefore takes thermal conductivity test to review mixture of sawdust and polyurethane comparison with variations different dosing. Maximum disposals sawdust can be done is 40% of the total volume of material mixture, polyurethane and sawdust because composite material (sawdust-polyurethane can not be bond with good so easy slab separately from origin form. Thermal Conductivity insulating good and economical on disposals 40% wood flour (0.05252 W / m°C and is able to maintain a 2 kg of ice crystals melt up perfect on 34 hours. Operating profits economical from 4,8 m³insulation composite application with obtained Rp 4.486.000 compared with 100% Polyurethane Insulation Manufacture.

Synthesis and characterization of polypropylene/jigsaw wood ash composite

International Nuclear Information System (INIS)

Sudirman; Karo Karo, Aloma; Gunawan, Indra; Handayani, Ari; Hertinvyana, Evi

2002-01-01

The composite of polypropylene (PP) polymer with jigsaw wood ash as filler is the alternative composite material. The dispersion of the filler in the composite is random with the jigsaw wood ash composition of 10,30, and 50% by volume. The characterization of composite are done to measure its mechanical properties, physical properties and microstructure by using XRD and SEM. From this research, it is concluded that increasing filler content of the composite will decrease its mechanical and physical properties. The comparation of different composites are found that tensile strength of PP MF 10 is higher 4.24% compared with PP MF 2 as a matrix. It is also found that melting temperature of PP MF 10 is higher 4.09% compared with PP MF 2 as a matrices and the decomposition temperature different is 0.17%. The degree of crystallinity of composite with PP MF 10 as a matrices is 2.55% higher compared with PP MF 2. The higher degree of crystallinity is increasing the tensile strength

Mechanical and thermal properties of polypropylene composites with curaua fibre irradiated with gamma radiation

International Nuclear Information System (INIS)

Egute, Nayara S.; Forster, Pedro L.; Parra, Duclerc F.; Fermino, Danilo M.; Santana, Sebastiao; Lugao, Ademar B.

2009-01-01

Thermal and mechanical behavior of polypropylene with curaua fibre composites were investigated. The treatment of the curaua fibres was processed in alkaline solution (10% wt NaOH). A coupling agent was used (maleic anhydride) to increase the adhesion of the fibre/matrix interface. This composite was irradiated with gamma source in the doses of 5, 15 and 30 kGy and the adhesion between the fibres and the polymeric matrix was monitored to observe probable changes. The thermal behavior was evaluated using differential scanning calorimetry (DSC) and Thermogravimetry (TGA). The mechanical behavior was evaluated using tensile strength in comparison with non-reinforced polypropylene resin. The morphology of the composite fracture surface was observed using scanning electron microscopy (SEM). There were no significant changes in the thermal properties neither in the adhesion of irradiated fibres at doses of 5, 15 and 30 kGy of gamma radiation. (author)

Mechanical performance of hemp fiber polypropylene composites at different operating temperatures

Science.gov (United States)

Mehdi Tajvidi; Nazanin Motie; Ghonche Rassam; Robert H. Falk; Colin Felton

2010-01-01

In order to quantify the effect of temperature on the mechanical properties of hemp fiber polypropylene composites, formulations containing 25% and 40% (by weight) hemp fiber were produced and tested at three representative temperatures of 256, 296, and 336 K. Flexural, tensile, and impact tests, as well as dynamic mechanical analysis, were performed and the reduction...

Effect of polypropylene maleic anhydride (PPMAH) on mechanical and morphological properties of polypropylene (PP)/recycled acrylonitrile butadiene rubber (NBRr)/empty fruit bunch (EFB) composites

Science.gov (United States)

Othman, Nurul Syazwani; Santiagoo, Ragunathan; Abdillahi, Khalid Mohamed; Ismail, Hanafi

2017-07-01

The fabrication of polypropylene (PP)/ recycled acrylonitrile butadiene rubber (NBRr)/ empty fruit bunch (EFB) composites were investigated. The effects of polypropylene maleic anhydride (PPMAH) as a compatibilizer on the mechanical and morphological properties of PP/NBRr/EFB composites were studied. Composites were prepared through melt mixing using heated two roll mill at 180 °C for 9 minutes and rotor speed of 15 rpm. NBRr loading were varied from 0 to 60 phr and PPMAH was fixed for 5 phr. The composites were moulded into a 1 mm thin sheet using hot press machine and then cut into dumbbell shape. The mechanical and morphological properties of composites were examined using universal tensile machine (UTM) and scanning electron microscope (SEM), respectively. Tensile strength and Young's modulus of PP/NBRr/EFB composites decreased with increasing NBRr loading, whilst increasing the elongation at break. However, PPMAH compatibilized composites have resulted 27% to 40% and 25% to 42% higher tensile strength and Young's modulus, respectively, higher compared to uncompatibilized composites. This was due to the better adhesion between PP/NBRr matrices and EFB filler with the presence of maleic anhydride moieties. From the morphological study, the micrograph of PPMAH compatibilized composites has proved the well bonded and good attachments of EFB filler with PP/NBRr matrices which results better tensile strength to the PP/NBRr/EFB composites.

Flow-induced solidification of high-impact polypropylene copolymer compositions : morphological and mechanical effects

NARCIS (Netherlands)

Drongelen, van M.; Gahleitner, M.; Spoelstra, A.B.; Govaert, L.E.; Peters, G.W.M.

2015-01-01

Polypropylene-based impact copolymers are a complex composition of matrix material, a dispersed phase and many optional modifiers. The final heterophasic morphology of such systems is influenced significantly by the processing step, adding an additional level of complexity to understanding the

Monotonic and cyclic responses of impact polypropylene and continuous glass fiber-reinforced impact polypropylene composites at different strain rates

KAUST Repository

Yudhanto, Arief

2016-03-08

Impact copolymer polypropylene (IPP), a blend of isotactic polypropylene and ethylene-propylene rubber, and its continuous glass fiber composite form (glass fiber-reinforced impact polypropylene, GFIPP) are promising materials for impact-prone automotive structures. However, basic mechanical properties and corresponding damage of IPP and GFIPP at different rates, which are of keen interest in the material development stage and numerical tool validation, have not been reported. Here, we applied monotonic and cyclic tensile loads to IPP and GFIPP at different strain rates (0.001/s, 0.01/s and 0.1/s) to study the mechanical properties, failure modes and the damage parameters. We used monotonic and cyclic tests to obtain mechanical properties and define damage parameters, respectively. We also used scanning electron microscopy (SEM) images to visualize the failure mode. We found that IPP generally exhibits brittle fracture (with relatively low failure strain of 2.69-3.74%) and viscoelastic-viscoplastic behavior. GFIPP [90]8 is generally insensitive to strain rate due to localized damage initiation mostly in the matrix phase leading to catastrophic transverse failure. In contrast, GFIPP [±45]s is sensitive to the strain rate as indicated by the change in shear modulus, shear strength and failure mode.

Impact of Surface Modification and Nanoparticle on Sisal Fiber Reinforced Polypropylene Nano composites

International Nuclear Information System (INIS)

Ibrahim, I. D.; Jamiru, T.; Sadiku, E. R.; Agwuncha, S. Ch.; Kupolati, W. K.

2016-01-01

The use of plant fibers, polymer, and nanoparticles for composite has gained global attention, especially in the packaging, automobile, aviation, building, and construction industries. Nano composites materials are currently in use as a replacement for traditional materials due to their superior properties, such as high strength-to-weight ratio, cost effectiveness, and environmental friendliness. Sisal fiber (SF) was treated with 5% NaOH for 2 hours at 70"°C. A mixed blend of sisal fiber and recycled polypropylene (rPP) was produced at four different fiber loadings: 10, 20, 30, and 40 wt.%, while nano clay was added at 1, 3, and 5 wt.%. Maleic anhydride grafted polypropylene (MAPP) was used as the compatibilizer for all composites prepared except the untreated sisal fibers. The characterization results showed that the fiber treatment, addition of MAPP, and nano clay improved the mechanical properties and thermal stability and reduced water absorption of the SF/rPP nano composites. The tensile strength, tensile modulus, and impact strength increased by 32.80, 37.62, and 5.48%, respectively, when compared to the untreated SF/rPP composites. Water absorption was reduced due to the treatment of fiber and the incorporation of MAPP and nano clay.

Use of softwood sawdust to amend reclaimed soils - a progress report

International Nuclear Information System (INIS)

Bossenberry, T.; Chollak, D.; Walker, G.; Evans, D. S.; Wilson, J. J.

1997-01-01

Updating a report presented at the 1996 annual meeting, these authors reported on an experiment on a 12 hectare site near Bonnyville in northeastern Alberta involving the addition of softwood sawdust, manure and inorganic fertilizers to the clay-rich stoney, glacial till parent material characterized by thin organic-poor cover and low nutrient composition. A nearby site of approximately the same size has been reclaimed using more conventional reclamation methods. The site with the added sawdust progressed slowly during spring and early summer, but more favorably with growing conditions in late 1996. It eventually resulted in better plant cover dominated by clover species with a late catching of grasses as understory vegetation. The conventionally treated site progressed more quickly with better production of both clovers and grasses. In 1997 the sawdust-added site accelerated with better and more consistent plant coverage and a better grass to clover ratio. The sawdust-amended topsoil profile remained stable, had good moisture retention and continued to be well drained and uncompacted. The overall assessment is that amended topsoils provide a short term physical and textural improvement to clay-rich soils and a longer term source of organic material. Therefore sawdust addition is particularly useful in remediating soils where topsoil quality is poor or insufficient for conventional reclamation

Electromagnetic shielding of polypyrrole-sawdust composites: polypyrrole globules and nanotubes

Czech Academy of Sciences Publication Activity Database

Babayan, V.; Kazantseva, N. E.; Moučka, R.; Stejskal, Jaroslav

2017-01-01

Roč. 24, č. 8 (2017), s. 3445-3451 ISSN 0969-0239 R&D Projects: GA ČR(CZ) GA16-02787S Institutional support: RVO:61389013 Keywords : wood sawdust * conducting polymer * nanotubes Subject RIV: CD - Macromolecular Chemistry OBOR OECD: Polymer science Impact factor: 3.417, year: 2016

Evaluation of Mechanical Property of Carbon Fiber/Polypropylene Composite According to Carbon Fiber Surface Treatment

International Nuclear Information System (INIS)

Han, Song Hee; Oh, Hyun Ju; Kim, Seong Su

2013-01-01

In this study, the mechanical properties of a carbon fiber/polypropylene composite were evaluated according to the carbon fiber surface treatment. Carbon fiber surface treatments such as silane coupling agents and plasma treatment were performed to enhance the interfacial strength between carbon fibers and polypropylene. The treated carbon fiber surface was characterized by XP S, Sem, and single-filament tensile test. The interlaminar shear strength (Ilks) of the composite with respect to the surface treatment was determined by a short beam shear test. The test results showed that the Ilks of the plasma-treated specimen increased with the treatment time. The Ilks of the specimen treated with a silane coupling agent after plasma treatment increased by 48.7% compared to that of the untreated specimen

Mechanical Properties and Weathering Behavior of Polypropylene-Hemp Shives Composites

Directory of Open Access Journals (Sweden)

Marcel Ionel Popa

2013-01-01

Full Text Available This paper presents the obtaining and the characterization of composites with polypropylene matrix and hemp shives as filler in different ratios and containing poly(propylene-co maleic anhydride (MAH-PP 3% wt as compatibility agent. The weathering behavior of the composite enclosing 60% hemp shives, performed after the exposure to UV radiations at different exposure times, was evaluated. The changes in the chemical and morphological structures were investigated by FT-IR and RAMAN spectroscopies and AFM microscopy. The mechanical characteristics of the composites were determined before and after an artificial aging process, and they are within the limits of the values reported for polyolefin-based composites and materials with natural fillers. During the accelerated weathering process, the correlation between the chemical degradation of the main components of the composite and the modification of the mechanical properties after the process of aging has been observed.

Application of waste bulk moulded composite (BMC) as a filler for isotactic polypropylene composites.

Science.gov (United States)

Barczewski, Mateusz; Matykiewicz, Danuta; Andrzejewski, Jacek; Skórczewska, Katarzyna

2016-05-01

The aim of this study was to produce isotactic polypropylene based composites filled with waste thermosetting bulk moulded composite (BMC). The influence of BMC waste addition (5, 10, 20 wt%) on composites structure and properties was investigated. Moreover, additional studies of chemical treatment of the filler were prepared. Modification of BMC waste by calcium stearate (CaSt) powder allows to assess the possibility of the production of composites with better dispersion of the filler and more uniform properties. The mechanical, processing, and thermal properties, as well as structural investigations were examined by means of static tensile test, Dynstat impact strength test, differential scanning calorimetry (DSC), wide angle X-ray scattering (WAXS), melt flow index (MFI) and scanning electron microscopy (SEM). Developed composites with different amounts of non-reactive filler exhibited satisfactory thermal and mechanical properties. Moreover, application of the low cost modifier (CaSt) allows to obtain composites with better dispersion of the filler and improved processability.

The carbonaceous concrete based on sawdust

Directory of Open Access Journals (Sweden)

BELOUSOVA Elena Sergeevna

2015-06-01

Full Text Available Today there are many requirements for strength, ecology and economy of produced concretes. The authors of the paper study attenuation of electromagnetic radiation of carbonaceous powders in the concrete composition. Carbon black was selected as a carbon powder for addition in concrete composition. Carbon black is a nanomaterial with disoriented structure of particles (average size is about 50 nm. The composition of the carbon black contains at least 90 wt.% amorphous carbon, more than 5 wt. % chemisorbed oxygen and about 4 wt.% of impurities. Materials with the addition of carbon black have electrical conductivity due to the high content of carbon. These materials are able to absorb electromagnetic radiation. For cement composition with addition of carbon black (more than 30 wt. % and water transmission coefficient of electromagnetic radiation is about –10 dB, for cement composition with 20 wt. % of carbon black the reflection coefficient is –8 dB in the frequency range 8–12 GHz. The concretes with a saturated aqueous solution of calcium chloride and 10% of carbon black possess minimal reflection coefficient (–14... –8 dB. Electromagnetic radiation shielding of concrete with the addition of sawdust was investigated. The concrete with sawdust (40 wt. % impregnated with an aqueous solution with carbon black has the reflection coefficient less than –8 dB and transmission coefficient –40 dB in the frequency range 8–12 GHz. These concretes can be used for creation of a shielded room with the technical equipment for information processing to prevent data leakage through the compromising emanations and crosstalk.

Fatigue mechanisms in unidirectional glass-fibre-reinforced polypropylene

DEFF Research Database (Denmark)

Gamstedt, E.K.; Berglund, L.A.; Peijs, T.

1999-01-01

Polypropylene (PP) and polypropylene modified with maleic anhydride (MA-PP) reinforced by continuous longitudinal glass fibres have been investigated. The most prominent effect of the modification with maleic anhydride in the composite is a stronger fibre/matrix interface. The effects of interfac......Polypropylene (PP) and polypropylene modified with maleic anhydride (MA-PP) reinforced by continuous longitudinal glass fibres have been investigated. The most prominent effect of the modification with maleic anhydride in the composite is a stronger fibre/matrix interface. The effects...... of interfacial strength on fatigue performance and on the underlying micromechanisms have been studied for these composite systems. Tension-tension fatigue tests (R = 0.1) were carried out on 0 degrees glass-fibre/PP and glass-fibre/ MA-PP coupons. The macroscopic fatigue behaviour was characterized in terms...

Coir dust reinforced recycled polypropylene composites; Compositos de polipropileno reciclado e po de coco

Energy Technology Data Exchange (ETDEWEB)

Santos, Bianca B. dos; Costa, Marysilvia F. da; Thire, Rossana M. da S.M., E-mail: bianca@metalmat.ufrj.br [Universidade Federal do Rio de Janeiro (UFRJ), Rio de Janeiro, RJ (Brazil)

2015-07-01

The environmental impacts caused by disposed plastics encourage the search for new alternatives. Recycling polymers leads to the degradation of their mechanical properties, which can be modified by the addition of fillers. In this paper, recycled polypropylene from plastic cups with 2%, 5% and 10% of coir dust were produced with and without the addition of additives. These composites were characterized by tensile tests, X-ray diffraction, differential scanning calorimetry and scanning electron microscopy on the fracture surface. It was verified the effectiveness of the addition of coir dust in improving the elasticity modulus of recycled polypropylene besides the effectiveness of additives used in promoting the adhesion of the powder to the matrix. However, higher levels of coir dust caused the appearance of air bubbles inside the material, which contributed to its embrittlement. The addition of coir dust promoted a decrease in the degree of polypropylene crystallinity. (author)

Mechanical properties of unidirectional and randomly oriented kenaf bast fibre composites using polypropylene resin matrix

International Nuclear Information System (INIS)

Sharifah Hanisah Syed Abd Aziz; Khairul Zaman Mohd Dahlan

2004-01-01

Fibres are known to confer strength and rigidity to the weak and brittle matrix and currently, research in composite materials is being directed at using natural fibers instead of synthetic fibres. In this work long and random kenaf fibers were used in the as-received condition and alkalized with a 0.06M NaOH solution. They were combined with polypropylene thin sheets and hot-pressed to form natural fibre composites. The mechanical properties of the composites were investigated to observe the effect of fibre alignment, fibre treatment, and the method of moulding technique used. A general trend was observed whereby alkalized and long fibre composites give higher flexural modulus and flexural strength compared with random mat and untreated fibres. The long fibre composites also gave a higher work of fracture. However, the correlation between fibre surface treatment and the work of fracture was less clear. The method of moulding used also need to be improved to optimize the performance of the composites manufactured as the overall mechanical test result showed some irregularities. Pre-irradiation on the polypropylene pellets before the composite is manufactured will be considered as one of the mechanism in enhancing the mechanical performance of the composites in future work. (Author)

Mechanical, Thermal Degradation, and Flammability Studies on Surface Modified Sisal Fiber Reinforced Recycled Polypropylene Composites

Directory of Open Access Journals (Sweden)

Arun Kumar Gupta

2012-01-01

Full Text Available The effect of surface treated sisal fiber on the mechanical, thermal, flammability, and morphological properties of sisal fiber (SF reinforced recycled polypropylene (RPP composites was investigated. The surface of sisal fiber was modified with different chemical reagent such as silane, glycidyl methacrylate (GMA, and O-hydroxybenzene diazonium chloride (OBDC to improve the compatibility with the matrix polymer. The experimental results revealed an improvement in the tensile strength to 11%, 20%, and 31.36% and impact strength to 78.72%, 77%, and 81% for silane, GMA, and OBDC treated sisal fiber reinforced recycled Polypropylene (RPP/SF composites, respectively, as compared to RPP. The thermogravimetric analysis (TGA, differential scanning calorimeter (DSC, and heat deflection temperature (HDT results revealed improved thermal stability as compared with RPP. The flammability behaviour of silane, GMA, and OBDC treated SF/RPP composites was studied by the horizontal burning rate by UL-94. The morphological analysis through scanning electron micrograph (SEM supports improves surface interaction between fiber surface and polymer matrix.

Ag2S deposited on oxidized polypropylene as composite material for solar light absorption

NARCIS (Netherlands)

Krylovaa, V.; Milbrat, Alexander; Embrachts, A.; Baltrusaitis, Jonas

2014-01-01

Thin film metal chalcogenides are superior solar light absorbers and can be combined into a functional material when deposited on polymeric substrates. Ag2S composite materials were synthesized on oxidized polypropylene using chemical bath deposition method and their properties were explored using

Burnout synergic or inhibiting effects in combustion assays of coal/sawdust blends

Energy Technology Data Exchange (ETDEWEB)

Ximena Garcia; Ximena Matus; Claudia Ulloa; Alfredo L. Gordon [University of Concepcion, Concepcion (Chile). Dept. of Chemical Engineering

2007-07-01

Characterization of chars and charcoal and combustion assays of coal/ pine sawdust blends were carried on to evaluate the burnout, under conditions similar to those found in pulverized coal combustion. A drop tube furnace (DTF) was used to generate chars from three coals of different rank (Bitsch, a lignite; Lemington, a bituminous HV coal; and LD, a semianthracite) and charcoal from sawdust (S). Burning profiles, as well as morphological and optical characterization of these chars were obtained and discussed. Pulverized samples of pure constituents and sawdust/coal blends (5, 10 and 20%wt of S) were burned in the DTF reactor. Samples of combustion residues were collected for characterization. Depending on blend composition and the rank of the coal being blended, positive and negative deviations with respect to the expected weighted average value of the burnout were measured. This behavior is related both, to the duration of the step by which simultaneous burning of char and charcoal take place, and to the sawdust content in the blend. The optical analysis of combustion residues supports this conclusion. 7 refs., 6 figs., 3 tabs.

Characterization of wood plastic composites made from landfill-derived plastic and sawdust: Volatile compounds and olfactometric analysis

International Nuclear Information System (INIS)

Félix, Juliana S.; Domeño, Celia; Nerín, Cristina

2013-01-01

Graphical abstract: This work details the characterization of VOCs of WPC, produced from residual materials which would have landfills as current destination, and evaluates their odor profile. Highlights: ► More than 140 volatile compounds were identified in raw materials and WPC products. ► Markers were related to the thermal degradation, sawdust or coupling agents. ► WPC prototype showed a characteristic odor profile of burnt, sweet and wax-like. ► Aldehydes, carboxylic acids, ketones and phenols were odor descriptors of WPC. - Abstract: Application of wood plastic composites (WPCs) obtained from recycled materials initially intended for landfill is usually limited by their composition, mainly focused on release of volatile organic compounds (VOCs) which could affect quality or human safety. The study of the VOCs released by a material is a requirement for new composite materials. Characterization and quantification of VOCs of several WPC produced with low density polyethylene (LDPE) and polyethylene/ethylene vinyl acetate (PE/EVA) films and sawdust were carried out, in each stage of production, by solid phase microextraction in headspace mode (HS-SPME) and gas chromatography–mass spectrometry (GC–MS). An odor profile was also obtained by HS-SPME and GC–MS coupled with olfactometry analysis. More than 140 compounds were observed in the raw materials and WPC samples. Some quantified compounds were considered WPC markers such as furfural, 2-methoxyphenol, N-methylphthalimide and 2,4-di-tert-butylphenol. Hexanoic acid, acetic acid, 2-methoxyphenol, acetylfuran, diacetyl, and aldehydes were the most important odorants. None of the VOCs were found to affect human safety for use of the WPC

Characterization of wood plastic composites made from landfill-derived plastic and sawdust: Volatile compounds and olfactometric analysis

Energy Technology Data Exchange (ETDEWEB)

Félix, Juliana S., E-mail: jfelix@unizar.es [Department of Analytical Chemistry, I3A, EINA, University of Zaragoza (UNIZAR), Zaragoza 50018 (Spain); Domeño, Celia, E-mail: cdomeno@unizar.es [Department of Analytical Chemistry, I3A, EINA, University of Zaragoza (UNIZAR), Zaragoza 50018 (Spain); Nerín, Cristina, E-mail: cnerin@unizar.es [Department of Analytical Chemistry, I3A, EINA, University of Zaragoza (UNIZAR), Zaragoza 50018 (Spain)

2013-03-15

Graphical abstract: This work details the characterization of VOCs of WPC, produced from residual materials which would have landfills as current destination, and evaluates their odor profile. Highlights: ► More than 140 volatile compounds were identified in raw materials and WPC products. ► Markers were related to the thermal degradation, sawdust or coupling agents. ► WPC prototype showed a characteristic odor profile of burnt, sweet and wax-like. ► Aldehydes, carboxylic acids, ketones and phenols were odor descriptors of WPC. - Abstract: Application of wood plastic composites (WPCs) obtained from recycled materials initially intended for landfill is usually limited by their composition, mainly focused on release of volatile organic compounds (VOCs) which could affect quality or human safety. The study of the VOCs released by a material is a requirement for new composite materials. Characterization and quantification of VOCs of several WPC produced with low density polyethylene (LDPE) and polyethylene/ethylene vinyl acetate (PE/EVA) films and sawdust were carried out, in each stage of production, by solid phase microextraction in headspace mode (HS-SPME) and gas chromatography–mass spectrometry (GC–MS). An odor profile was also obtained by HS-SPME and GC–MS coupled with olfactometry analysis. More than 140 compounds were observed in the raw materials and WPC samples. Some quantified compounds were considered WPC markers such as furfural, 2-methoxyphenol, N-methylphthalimide and 2,4-di-tert-butylphenol. Hexanoic acid, acetic acid, 2-methoxyphenol, acetylfuran, diacetyl, and aldehydes were the most important odorants. None of the VOCs were found to affect human safety for use of the WPC.

Effect of gamma radiation on the performance of jute fabrics-reinforced polypropylene composites

Energy Technology Data Exchange (ETDEWEB)

Haydaruzzaman [Department of Physics, Jahangirnagar University, Savar, Dhaka (Bangladesh); Khan, Ruhul A. [Radiation and Polymer Chemistry Laboratory, Institute of Nuclear Science and Technology, Bangladesh Atomic Energy Commission, G. P.O. Box 3787, Dhaka 1000 (Bangladesh); Khan, Mubarak A. [Radiation and Polymer Chemistry Laboratory, Institute of Nuclear Science and Technology, Bangladesh Atomic Energy Commission, G. P.O. Box 3787, Dhaka 1000 (Bangladesh)], E-mail: makhan.inst@gmail.com; Khan, A.H.; Hossain, M.A. [Department of Physics, Jahangirnagar University, Savar, Dhaka (Bangladesh)

2009-11-15

Jute fabrics-reinforced polypropylene (PP) composites (50% fiber) were prepared by compression molding. Composites were fabricated with non-irradiated jute fabrics/non-irradiated PP (C-0), non-irradiated jute fabrics/irradiated PP (C-1), irradiated jute fabrics/non-irradiated PP (C-2) and irradiated jute fabrics/irradiated PP (C-3). It was found that C-3 composite performed the best mechanical properties over other composites. Total radiation dose varied from 250-1000 krad and composites made of using 500 krad showed the best results. The optimized values (C-3 composites) for tensile strength (TS), bending strength (BS) and impact strength (IS) were found to be 63 MPa, 73 MPa and 2.93 kJ/m{sup 2}, respectively.

Electron beam processing of rubber wood fibers - polypropylene composites. Effects of reactive additives on the physical and mechanical properties

International Nuclear Information System (INIS)

Nor Yuziah Mohd Yunus; Jalaluddin Harun; Khairul Zaman

2000-01-01

The purpose of this study is to determine the suitability of producing agro-fiber reinforced plastic composite (agro-FRPC) from rubber wood fiber blended in polypropylene matrix. The effects of varying fiber dimension and fiber content on the physical and mechanical properties of the composite were evaluated to provide an insight into the fiber matrix adhesion. The effects of reactive additives on the physical and mechanical properties of the composite were evaluated which provides the insight on the reinforcement of the composite. Rubber wood fiber used in this study is currently being used in the manufacturing of medium density fiber (MDF) board. Two sizes of rubber wood fiber were used i.e. 0.5-1.0 mm and 1.0-2.0 mm. Homopolymer polypropylene of MFI 14.0 was used as a matrix. The irradiation work was carried out using electron beam accelerator, 3.0 MeV, 3.0 mA. Various types of reactive additives (RA) with mono-functional, di-functional, tri-functional and oligomer were applied in the blend. For comparison, a conventional chemical cross-linking using two types of maleated polypropylene, MPA (Mw=9,000) and PMAP (Mw=220,000) were also performed. (author)

Electron beam processing of rubber wood fibers - polypropylene composites. Effects of reactive additives on the physical and mechanical properties

Energy Technology Data Exchange (ETDEWEB)

Nor Yuziah Mohd Yunus; Jalaluddin Harun [Universiti Putra Malaysia, Selangor Darul Ehsan (Malaysia); Khairul Zaman [Malaysian Institute for Nuclear Technology Research (MINT), Selangor Darul Ehsan (Malaysia)

2000-07-01

The purpose of this study is to determine the suitability of producing agro-fiber reinforced plastic composite (agro-FRPC) from rubber wood fiber blended in polypropylene matrix. The effects of varying fiber dimension and fiber content on the physical and mechanical properties of the composite were evaluated to provide an insight into the fiber matrix adhesion. The effects of reactive additives on the physical and mechanical properties of the composite were evaluated which provides the insight on the reinforcement of the composite. Rubber wood fiber used in this study is currently being used in the manufacturing of medium density fiber (MDF) board. Two sizes of rubber wood fiber were used i.e. 0.5-1.0 mm and 1.0-2.0 mm. Homopolymer polypropylene of MFI 14.0 was used as a matrix. The irradiation work was carried out using electron beam accelerator, 3.0 MeV, 3.0 mA. Various types of reactive additives (RA) with mono-functional, di-functional, tri-functional and oligomer were applied in the blend. For comparison, a conventional chemical cross-linking using two types of maleated polypropylene, MPA (Mw=9,000) and PMAP (Mw=220,000) were also performed. (author)

Radiation resistant modified polypropylene

International Nuclear Information System (INIS)

Bojarski, J.; Zimek, Z.

1997-01-01

Radiation technology for production of radiation resistant polypropylene for medical use has been presented. The method consists in radiation induced copolymerization of polypropylene with ethylene and addition of small amount of copolymer of polyethylene and vinyl acetate. The material of proposed composition has a very good mechanical properties and elevated radiation resistivity decided on possibility of radiosterilization of products made of this material and designed for medical use. 3 figs, 3 tabs

Short Jute Fiber Reinforced Polypropylene Composites: Effect of Nonhalogenated Fire Retardants

Directory of Open Access Journals (Sweden)

Sk. Sharfuddin Chestee

2017-01-01

Full Text Available Short jute fiber reinforced polypropylene (PP composites were prepared using a single screw extrusion moulding. Jute fiber content in the composites is optimized with the extent of mechanical properties, and composites with 20% jute show higher mechanical properties. Dissimilar concentrations of several fire retardants (FRs, such as magnesium oxide (MO, aluminum oxide (AO, and phosphoric acid (PA, were used in the composites. The addition of MO, AO, and PA improved the fire retardancy properties (ignition time, flame height, and total firing time of the composites. Ignition time for 30% MO, flame height for 30% PA, and total firing time for 20% MO content composites showed good results which were 8 sec, 1 inch, and 268 sec, respectively. Mechanical properties (tensile strength, tensile modulus, bending strength, bending modulus, and elongation at break, degradation properties (soil test, weathering test, and percentage of weight loss, and water uptake were studied.

Fabrication and characterization of jute fabrics reinforced polypropylene-based composites: effects of ionizing radiation and disaccharide (sucrose)

Science.gov (United States)

Sahadat Hossain, Md.; Uddin, Muhammad B.; Razzak, Md.; Sarwaruddin Chowdhury, A. M.; Khan, Ruhul A.

2017-12-01

Composites were prepared successfully by compression molding technique using jute fabrics (reinforcing agent) and polypropylene (matrix). Jute fabrics were treated with disaccharide (sucrose) solution and composites were fabricated with the treated fabric and polypropylene. The fiber content of the prepared composites was 40% by weight. It was found that the sucrose (2% solution) decreased the tensile strength (TS) and elongation at break about 6% and 37%, respectively, but tensile modulus and impact strength improved about 27% and 32%, respectively. When gamma radiation was applied through the untreated and treated composites the mechanical properties were improved much higher in non-treated Jute/PP-based composites than that of sucrose treated composites. For 5.0 kGy gamma dose the highest mechanical properties were observed for non-treated composites. At 5.0 kGy gamma dose the improvement of TS was 14% and 2% for non-treated and sucrose treated composites, respectively. The water uptake property of the sucrose treated composites was performed up to 10 days and composites absorbed 18% water. The functional groups of the both composites were analyzed by Fourier transform infrared spectroscopy machine. The scanning electron microscopic images of the both composites were taken for the surface and fiber adhesion analysis.

Rice straw addition as sawdust substitution in oyster mushroom (Pleurotus ostreatus) planted media

Science.gov (United States)

Utami, Christine Pamardining; Susilawati, Puspita Ratna

2017-08-01

Oyster mushroom is favorite by the people because of the high nutrients. The oyster mushroom cultivation usually using sawdust. The availability of sawdust become difficult to find. It makes difficulties of mushroom cultivation. Rice straw as an agricultural waste can be used as planted media of oyster mushroom because they contain much nutrition needed to the mushroom growth. The aims of this research were to analysis the influence of rice straw addition in a baglog as planted media and to analysis the concentration of rice straw addition which can substitute sawdust in planted media of oyster mushroom. This research used 4 treatment of sawdust and rice straw ratio K = 75 % : 0 %, P1 = 60 % : 15 %, P2 = 40 % : 35 %, P3 = 15 % : 60 %. The same material composition of all baglog was bran 20%, chalk 5%, and water 70%. The parameters used in this research were wet weight, dry weight, moisture content and number of the mushroom fruit body. Data analysis was used ANOVA test with 1 factorial. The results of this research based on statistical analysis showed that there was no influence of rice straw addition in a planted media on the oyster mushroomgrowth. 15% : 60% was the concentrationof rice straw additionwhich can substitute the sawdust in planted media of oyster mushroom.

Study of the rice husk ash utilization as filler polypropylene matrix and ionization radiation effect on this composite

International Nuclear Information System (INIS)

Alfaro, Eduardo de Faria

2010-01-01

In the first step of this work, it was evaluated the possibility of using rice husk ash as a filler in polypropylene (PP) making a comparison with talc which is the most used mineral filler in polymers. This comparison was made by using polypropylene with 20% rice husk ash as well as polypropylene with 20% talc measuring their properties. Despite the properties of the PP with 20% rice husk ash decreased compared with the composite of polypropylene with 20% talc it can be said that the rice husk ash can be used as filler for or other utilization less noble of PP . This way it is being given a destination for this residue that it is disposable in the environment contributing to its preservation, moreover reducing the product cost. This work had also as an aim to study the ionizing radiation effect in the properties of these composites. It was used the coupling agent, maleic anhydride , to verify a best sample homogenization. According to the results it can be said that PP is a semicrystalline polymer, and so it has its morphology modified when exposed to the irradiation process. This fact is due to the scission mechanisms of the polymeric chains which it is in compliance to the literature. (author)

The influence of irradiated wood filler on some properties of polypropylene - wood composites

Directory of Open Access Journals (Sweden)

Điporović-Momčilović Milanka

2007-01-01

Full Text Available The problem of compatibility between the wood filler and thermoplastic matrix is of essential importance in composite production. Numerous methods have been developed for increasing this compatibility, which is still representing a challenging objective of composite research throughout the world. The research into these methods is primarily directed towards their efficiency from the viewpoint of the composite performance and their economical acceptability. The latter is of particular importance for the composite production in the developing countries with respect to the shortage of the corresponding funds. With this respect, the utilization of ionizing radiation might have considerable advantages. In this research, the beech wood flour was irradiated by a dose of 10 kGy of 60Co gamma rays for purpose of provoking the changes by the ionizing effect. The effects of ionizing radiation upon the properties of wood particles have been examined by IR spectroscopy and by determination of contents of hydroxyl groups in wood by acetylating as an indirect method. All these methods have been expected to reveal the chemical effects of the applied radiation treatment. The irradiated and the control wood flour were used in order to produce the samples of composite with polypropylene. The polypropylene-wood flour (PP-WF composites were produced with 40% of wood particles having fraction size 0.3 mm. The melt-blended composites were modified with amido-acrylic acid (AMACA as a new coupling agent synthesized for this propose in amount of 6 wt.% (based on wood filler and successively with 0.05 wt.% (based on PP of organic peroxide during mixing step. The composites containing coupling agents showed superior mechanical properties, compared to the untreated one. The highest extent of improvement of tensile was achieved in PP-WFl composites modified with AMACA coupling agent.

Woodflour as Reinforcement of Polypropylene

Directory of Open Access Journals (Sweden)

José Cláudio Caraschi

2002-10-01

Full Text Available The effect of the filler content and size, as well as accelerated aging on the mechanical properties of polypropylene composites reinforced with woodflour (WF/PP were evaluated. The composites were prepared by the extrusion of polypropylene with woodflour (Pinus elliotti based on following ratios: 15, 25 and 40 wt% with two different granulometries. The specimens were injection molded according to ASTM standards. The composite properties did not show significant differences as a function of the filler granulometry. We also observed that by increasing the filler content, both the mechanical properties and the melt flow index (MFI decreased, and the elasticity modulus, hardness and density increased. Concerning the accelerated aging, the composite presented a reduction in tensile properties. The results showed that the composite properties are extremely favorable when compared to other commercial systems reinforced by inorganic fillers.

Modelling of polypropylene fibre-matrix composites using finite element analysis

Directory of Open Access Journals (Sweden)

2009-01-01

Full Text Available Polypropylene (PP fibre-matrix composites previously prepared and studied experimentally were modelled using finite element analysis (FEA in this work. FEA confirmed that fibre content and composition controlled stress distribution in all-PP composites. The stress concentration at the fibre-matrix interface became greater with less fibre content. Variations in fibre composition were more significant in higher stress regions of the composites. When fibre modulus increased, the stress concentration at the fibres decreased and the shear stress at the fibre-matrix interface became more intense. The ratio between matrix modulus and fibre modulus was important, as was the interfacial stress in reducing premature interfacial failure and increasing mechanical properties. The model demonstrated that with low fibre concentration, there were insufficient fibres to distribute the applied stress. Under these conditions the matrix yielded when the applied stress reached the matrix yield stress, resulting in increased fibre axial stress. When the fibre content was high, there was matrix depletion and stress transfer was inefficient. The predictions of the FEA model were consistent with experimental and published data.

Effects of consolidation process on microstructure and mechanical properties of commingled glass/polypropylene composites

International Nuclear Information System (INIS)

Tufail, M.; Long, A.C.; Rudd, C.D.

2001-01-01

The thermal history of a thermoplastic composite material during forming and consolidation is critical to the quality of the component. Attempts to process outside the normal melt region will result in incomplete consolidation and voidage. Clearly then, the preheat phase plays a key role in successful processing. Too low a preheat temperature results in insufficient matrix flow while, if the temperature is increased too much, degradation of the matrix occurs, again resulting in poor quality of the composite. In particular polypropylene has poor chemical (oxidative) resistance, and oxidative degradation reduces the average molecular weight of the materials. If excessive, this can result in a dramatic reduction in mechanical properties. Flat plaques of braided, commingled glass/polypropylene yarn were produced to examine these effects using both isothermal and non-isothermal consolidation. Woven plaques were also produced from commingled yarn in a similar fashion as control samples in order to identify any effects specific to the braiding process. This paper describes the effect of heating and stamping cycles on the properties of these composites, concentrating on the effects of temperature, heating time and compaction rate. (author)

Bioprospecting of powdered pineapple rind as an organic supplement of composted sawdust for Pleurotus ostreatus mushroom cultivation.

Science.gov (United States)

Narh Mensah, Deborah L; Addo, Peter; Dzomeku, Matilda; Obodai, Mary

2018-03-01

Pineapple rind is a by-product of the pineapple processing industry and contains nutrients and other compounds which must be utilized as a bioresource for socio-economic benefits while preventing the potential problems of improper agroindustrial biomass disposal methods. Pleurotus ostreatus is an edible oyster mushroom with medicinal properties and can be cultivated on various agroindustrial biomass, including sawdust containing supplements. Pineapple rind was powdered and used as a supplement of composted sawdust at 2%, 5%, 10%, 12%, 15%, and 20% (w/w) on dry weight basis. A control treatment consisted of composted sawdust supplemented with rice bran at 12% (the most utilized composition in Ghana). P. ostreatus strain EM-1 was cultivated on these treatments. Factors investigated included the spawn run period, yield, fruiting body weight and size, biological efficiency, and nutritional composition (proximate composition and Copper, Zinc and Lead content) of fruiting bodies harvested from selected high-yielding treatments and the control treatment. Full colonization of all treatments occurred by the 34th day of incubation. Enhanced yield, fruiting body weight and size, and biological efficiency were generally recorded with supplementation at lower concentrations (2% and 5%) compared to treatments supplemented at higher concentrations. There was also a supplement concentration-dependent alteration of the nutritional composition of the mushroom. Powdered pineapple rind can be utilized as an organic supplement at relatively low concentrations in composted sawdust for P. ostreatus strain EM-1 cultivation. The use of lower concentrations of powdered pineapple rind in composted sawdust is advantageous as relatively less input will be required to produce higher P. ostreatus strain EM-1 yields. Utilization of pineapple rind for mushroom cultivation will extend the pineapple plant value chain, intensify mushroom production in a sustainable way, and minimize agricultural

Study of the effect of ionizing radiation on composites of wood flour in polypropylene matrix using barium titanate as coupling agent

International Nuclear Information System (INIS)

Ulloa, Maritza Eliza Perez

2007-01-01

The purpose of this work was to study the effects of ionizing radiation on the properties of wood flour composites in polypropylene matrix, using barium titanate as a coupling agent and the reactive monomer tripropylene glycol diacrylate (TPDGA). An electron accelerator was used in the study as the radiation source. The physical properties of virgin compounds and of the polypropylene/wood flour composite, with and without barium titanate and TPDGA addition, were investigated. The composites were developed from the load treatment, which first consisted of incorporating additives to the wood flour reinforcement and after that, the fusion process of polypropylene and composite mixing in a 'calander'. Subsequently, the samples to be irradiated and submitted to thermal and mechanical assays were molded by injection. The mechanical properties (hardness, impact resistance and molten fluidity index (MFI)), as well as the thermal properties (HDT and Vicat) of the composites were determined. The investigated compositions consisted of polypropylene/wood flour, polypropylene/wood flour with barium titanate and polypropylene/wood flour with barium titanate and TPDGA, using different wood flour concentrations of 10 por cent, 15 por cent and 20 por cent in the polypropylene matrix. The samples were separated in groups and irradiated to doses of 10 kGy and 20 kGy in the samples of the essays of traction. Besides these doses, it was also used doses of 15 kGy and 25 kGy to be observed the behavior of the sample of the sample due to the increase of the radiation. These doses were chosen to show that with low doses the composite material presents reticulation, what represents a viable commercial option. There was a reduction of the flow rate for the composites containing wood flour, being this reduction more effective in the presence of TiBa. The superficial treatment using TPDGA monomer influence in the composite samples because it acted as a plastic additive becoming the sample

Rheological properties of polypropylene nanocomposites

International Nuclear Information System (INIS)

Oliveira, Camila F. de P.; Demarquette, Nicole R.

2009-01-01

In this work, composites of polypropylene with a master batch to obtain clay containing nano composites were obtained. The materials were characterized by X ray diffraction, small angle X-ray scattering and by rheological analysis. (author)

Electromagnetic interference shielding effectiveness of polypropylene/conducting fiber composites

International Nuclear Information System (INIS)

Lee, Pyoung-Chan; Kim, Bo-Ram; Jeoung, Sun Kyoung; Kim, Yeung Keun

2016-01-01

Electromagnetic released from the automotive electronic parts is harmful to human body. Electromagnetic interference (EMT) shielding refers to the reflection and/or adsorption of electromagnetic radiation by a material, which thereby acts as a shield against the penetration of the radiation through the shield. Polypropylene (PP)/conductive micro fiber composites containing various fiber contents and fiber length were injection-molded. The effect of fiber content and length on electrical properties of the composites was studied by electrical resistivity and EMT shielding measurements. The through-plane electrical conductivity and dielectric permittivity were obtained by measuring dielectric properties. The EMT shielding effectiveness (SE) was investigated by using S-parameter in the range of 100 ~ 1500 MHz. Reflection, absorption and multiple-reflection are the EMT attenuation mechanisms. From the measurement of S-Parameters, the absorption coefficient, reflection coefficient, and the shielding efficiency of the materials were calculated. The EMT SE of PP/conducing fiber composites is 40 dB over a wide frequency range up to 1.5 GHz, which is higher than that of PP/talc composite used automotive parts, viz. 0 dB.

Removal of light petroleum hydrocarbons from water sources using polypropylene and titanium dioxide nano-composite

Directory of Open Access Journals (Sweden)

H. Karyab

2016-08-01

Full Text Available Background: Petroleum hydrocarbons are the most important pollutants which threat human health and aquatics. Adsorbents are one of the common equipment in water pollution management; however, their applications have been associated with limitations. Objective: To evaluate the potential of polypropylene/titanium dioxide Nano-composite in adsorption of light petroleum hydrocarbons from water sources. Methods: This experimental study was conducted at school of health, Qazvin University of Medical Sciences in 2014-15. Activation of polypropylene fibers, with 1 cm length and 300 microns diameters, was achieved with wet heating. To synthesize of nano-composite the fibers were coated with nano-titanium dioxide with 20 nm diameter. The sonication was performed at 26 kHz and 100 W of power in 40ºc. The morphology of the fractured surfaces of impact specimens was examined by FESEM. The adsorption rate of petrol and gasoline, as surrogate of TPH, was evaluated in different retention time within polyamide mesh aperture diameter of 250 nm. Average of TPH adsorbing, per unit weight of adsorbent, were analyzed with analysis of variance and Scheffe post hoc tests. Findings: The FESEM micrographs showed that the dispersion of the nano-Tio2 particles was relatively good and only few aggregations exist. The maximum adsorption capacity of petrol and gasoline was obtained in 30 minute. The adsorption rate of gasoline was 6.49±0.10 g/g and oil was 7.01±0.13 g/g. Conclusion: According to the results and in comparison with commercial imported adsorbents, the synthesized Nano-composite had favorable performance. The results show that the polypropylene/Tio2 Nano-composite can be used effectively in light petroleum hydrocarbons removal from polluted water sources.

Isotactic polypropylene/carbon nanotube composites prepared by latex technology. Thermal analysis of carbon nanotube-induced nucleation

NARCIS (Netherlands)

Miltner, H.E.; Grossiord, N.; Lu, K.; Loos, J.; Koning, C.E.; Van Mele, B.

2008-01-01

During nonisothermal crystallization of highly dispersed polypropylene/carbon nanotube (CNT) composites, considerable heterogeneous nucleation is observed to an extent scaling with the CNT surface area. Saturation occurs at higher loadings, reaching a plateau value for the crystallization onset

Polypropylene Nano composites Obtained by In Situ Polymerization Using Metallocenes Catalyst: Influence of the Nanoparticles on the Final Polymer Morphology

International Nuclear Information System (INIS)

Zapata, P.; Quijada, R.

2012-01-01

Polypropylene nano composites containing silica nanospheres based on the sol-gel methods were produced via in situ polymerization using a rac-Et(Ind) 2 ZrCl 2 /methylaluminoxane (MAO) system. Two different routes were used depending on the interaction between the silica nanoparticles with the catalytic system. In route 1 the nanoparticles were added together with the catalytic system (rac-Et(Ind) 2 ZrCl 2 )/(MAO) directly into the reactor, and in route 2 the metallocenes rac-Et(Ind) 2 ZrCl 2 was supported on silica nanospheres pretreated with (MAO). SEM images show that when the nanospheres were added by both routes, they were replicated in the final polymer particle morphology; this phenomenon was more pronounced for PP obtained by route 2. The polypropylene (PP) nano composites obtained by both routes had a slightly higher percent crystallinity and crystallinity temperatures than pure PP. Transmission electron microscopy (TEM) images show that the nanospheres were well dispersed into the polypropylene matrix, particularly in the nano composites obtained by the support system (route 2).

Studies on Poly(propylene fumarate-co-caprolactone diol Thermoset Composites towards the Development of Biodegradable Bone Fixation Devices

Directory of Open Access Journals (Sweden)

M. Jayabalan

2009-01-01

Full Text Available The effect of reinforcement in the cross-linked poly(propylene fumarate-co-caprolactone diol thermoset composites based on Kevlar fibres and hydroxyapatite was studied. Cross-linked poly(propylene fumarate-co-caprolactone diol was also studied without any reinforcement for comparison. The reinforcing fibre acts as a barrier for the curing reaction leading to longer setting time and lesser cross-link density. The fibre and HA reinforced composites have almost the same compressive strength. Nonreinforced material undergoes greater degree of swelling. Among the reinforced materials, the hydroxyapatite reinforced composite has a much higher swelling percentage than the fibre reinforced one. The studies on in vitro degradation of the cured materials reveal hydrolytic degradation in Ringer's solution and PBS medium during aging. All the three materials are found to swell initially in Ringer's solution and PBS medium during aging and then undergo gradual degradation. Compression properties of these cross-linked composites increase with aging; HA reinforced composite has the highest compressive strength and compressive modulus, whereas the aged fibre-reinforced composite has the least compressive strength and modulus.

Studies on Poly(propylene fumarate-co-caprolactone diol) Thermoset Composites towards the Development of Biodegradable Bone Fixation Devices.

Science.gov (United States)

Jayabalan, M

2009-01-01

The effect of reinforcement in the cross-linked poly(propylene fumarate-co-caprolactone diol) thermoset composites based on Kevlar fibres and hydroxyapatite was studied. Cross-linked poly(propylene fumarate-co-caprolactone diol) was also studied without any reinforcement for comparison. The reinforcing fibre acts as a barrier for the curing reaction leading to longer setting time and lesser cross-link density. The fibre and HA reinforced composites have almost the same compressive strength. Nonreinforced material undergoes greater degree of swelling. Among the reinforced materials, the hydroxyapatite reinforced composite has a much higher swelling percentage than the fibre reinforced one. The studies on in vitro degradation of the cured materials reveal hydrolytic degradation in Ringer's solution and PBS medium during aging. All the three materials are found to swell initially in Ringer's solution and PBS medium during aging and then undergo gradual degradation. Compression properties of these cross-linked composites increase with aging; HA reinforced composite has the highest compressive strength and compressive modulus, whereas the aged fibre-reinforced composite has the least compressive strength and modulus.

Radiation-modified blends of the basis of polyethylene terephthalate and polypropylene

International Nuclear Information System (INIS)

Mery-Meri, R.; Revyakin, O.; Zicans, J.

2000-01-01

The binary composite systems on the basis of post-consumer poly-(ethylene terephthalate) and polypropylene have been investigated. Mechanical properties of the compositions were studied in detail in order to expand the application possibilities of tested binary composites. Structural changes of the poly (ethylene terephthalate) / polypropylene blends depending on the concentration of the components were investigated also. Additionally, the optimum processing conditions were established. Particular attention was paid to study the influence of the ionizing γ-radiation on the structural and mechanical properties of the composition systems tested. The magnitude of the adsorbed dose od γ-radiation was established to affect differently the structure of poly(ethylene terephalate) and polypropylene. At small absorbed doses (50 kGy) crosslinking of the polymer was observed for both poly(ethylene terephthalate) and polypropylene resulting in the increase of some mechanical properties of pure materials as well of their compositions, whereas the absorbed dose of 300 kGy caused the destruction of the tested materials. It is important to mention that the rate of radiation-chemical destruction of polypropylene is higher than poly(ethylene terephthalate) destruction rate. (author)

Cyclic viscoelastoplasticity of polypropylene/nanoclay composites

DEFF Research Database (Denmark)

Drozdov, A.; Christiansen, Jesper de Claville

2012-01-01

Observations are reported on isotactic polypropylene/organically modified nanoclay hybrids with concentrations of filler ranging from 0 to 5 wt.% in cyclic tensile tests with a stress–controlled program (oscillations between various maximum stresses and the zero minimum stress). A pronounced effe...

Mechanical Properties of Isotactic Polypropylene Modified with Thermoplastic Potato Starch

Science.gov (United States)

Knitter, M.; Dobrzyńska-Mizera, M.

2015-05-01

In this paper selected mechanical properties of isotactic polypropylene (iPP) modified with potato starch have been presented. Thermoplastic starch (TPS) used as a modifier in the study was produced from potato starch modified with glycerol. Isotactic polypropylene/thermoplastic potato starch composites (iPP/TPS) that contained 10, 30, 50 wt.% of modified starch were examined using dynamic mechanical-thermal analysis, static tensile, Brinell hardness, and Charpy impact test. The studies indicated a distinct influence of a filler content on the mechanical properties of composites in comparison with non-modified polypropylene.

Pulse NMR-spectroscopy of structural changes of chemically modified polypropylene

International Nuclear Information System (INIS)

Gafarov, A.M.; Galibeev, S.S.; Kochnev, A.M.; Sukhanov, P.P.; Arkhireev, V.P.

2004-01-01

The structure of polypropylene compositions is studied by the method of pulse NMR-spectroscopy. The polypropylene compositions are derived by means of the modification by multicomponent systems. The analysis of relaxation times in a wide temperature range is carried out. Character of changes going on at a level of supermolecular structures is described. It is shown that the amplifications that manifest themselves under the polypropylene modification by the mixtures based on 2,4-tolyilendiisocyanate and e-caprolactam, are related to the change in the intermolecular interaction and formation of a more ordered polymer structure. (authors)

Acid hydrolysis of hemicelluloses in beech sawdust

Energy Technology Data Exchange (ETDEWEB)

Hojnos, J

1977-01-01

The hemicellulose of beechwood consists mainly of 4-O-methylglucuronoxylan, 92.4 to 94.4% of which is selectively hydrolyzed to D-xylose (1) by exposing moist beechwood sawdust to HCl (g) at 50/sup 0/ for 50 min. The prepn. of 1 in 85.6% yield from beechwood sawdust can also be carried out by heating it at 140/sup 0/ for 70 to 100 min in 3 to 4.5% H/sub 2/SO/sub 3/ soln. Dry SO/sub 2/(g) does not hydrolyze beechwood sawdust.

Synthesis And Thermal Characterization Of Polypropylene ...

African Journals Online (AJOL)

The present work investigates the heat transfer and specifically, thermal conductivity, diffusivity and specific heat in Aluminium composite materials. The composites were obtained by mixing polypropylene (PP) with oxidized Aluminium (Al) under various volume fractions. Two sizes of filler are used in the sample composite ...

Polypropylene /Aspen/ liquid polybutadienes composites: maximization of impact strength, tensile and modulus by statistical experimental design

Czech Academy of Sciences Publication Activity Database

Kokta, B. V.; Fortelný, Ivan; Kruliš, Zdeněk; Horák, Zdeněk; Michálková, Danuše

2005-01-01

Roč. 99, - (2005), s. 10-11 ISSN 0009-2770. [International Conference on Polymeric Materials in Automotive , Slovak Rubber Conference /17./. 10.5.2005-12.5.2005, Bratislava] Institutional research plan: CEZ:AV0Z40500505 Keywords : polypropylene * Aspen-PP composite Subject RIV: CD - Macromolecular Chemistry

Improving the utilization of beech sawdust by sheep

International Nuclear Information System (INIS)

Zelenak, I.; Boda, K.; Jalc, D.; Lenart, J.; Kmet, V.; Havassy, I.; Kosta, K.

1991-01-01

Defibration following treatment with 1% H 2 SO 4 as an impregnation agent increased the in vitro dry matter (DM) digestibility of beech sawdust to 59.5%. Digestibilities of barley straw, wheat straw, maize stover and bagasse were also increased through defibration without prior chemical treatment. Increased DM degradability was also reflected in better digestibility of fibre components and volatile fatty acids (VFA) production. The inclusion of treated beech sawdust in the diet at levels of up to 20% had no negative effect on lamb performance. Studies with 15 N labelled urea did not show clear positive effect on nitrogen utilization when sheep were fed the treated beech sawdust. Immobilized cellulase and the addition of branched-chain VFA significantly increased the in vitro degradation of treated beech sawdust. Methanol extract of treated beech sawdust had an inhibitory effect on the growth of Streptococus bovis and Lactobacillus plantarum and reduced in vitro fermentation of rumen fluid. (author). 15 refs, 3 figs, 10 tabs

Bio composites from polypropylene/ clay/eva polymers and kenaf natural fiber

International Nuclear Information System (INIS)

Siti Hasnah Kamarudin; Khalina Abdan; Bernard Maringgal; Wan Mohd Zin Wan Yunus

2009-01-01

Full text: There is an increasing need to investigate more environmental friendly, sustainable materials to replace existing materials as industry attempts to lessen dependence on petroleum based fuels and products. The natural fiber composites offer specific properties comparable to those of conventional fiber composites. In this experiment, mixing process of polymer/nano clay composites from polypropylene, organo clay and ethylene vinyl acetate were prepared using a Brabender twin screw compounder. The composites sheets were then laminated with kenaf fibers and subjected to hot and cold press machine to form a bio composite. The mechanical properties such as flexural and impact strength are compare favourably between polymers reinforced kenaf fiber and polymers without kenaf fiber. In addition, various analysis techniques were used to characterize the dispersion and the properties of nano composites, using scanning electron micrograph (SEM), differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). These results suggest that kenaf fibers are a viable alternative to inorganic mineral-based reinforcing fibers as long as the right processing conditions are used and they are used in applications where the higher water absorption is not critical. (author)

Characterization of Polypropylene Green Composites Reinforced by Cellulose Fibers Extracted from Rice Straw

Directory of Open Access Journals (Sweden)

Ngo Dinh Vu

2018-01-01

Full Text Available Polypropylene (PP based green composites containing 10, 20, 30, 40 and 50 wt% of cellulose fibers (CFs which were extracted from rice straw were successfully prepared by melt blend method. The CFs washed with H2O2 after alkaline extraction showed lower water absorption than that not washed with H2O2. The thermal, mechanical, and biodegradation properties of composites were also investigated. The 10% weight loss temperature of the composites was decreased with the increasing CFs content, but all the composites showed over 300°C. Young’s modulus and flexural properties of PP were improved by blending PP with CFs. The pure PP showed no degradability, but the PP/CFs composites degraded from about 3 to 23 wt%, depending on CFs content after being buried in soil for 50 days. These PP/CFs composites with high thermal, mechanical properties and biodegradability may be useful as green composite materials for various environmental fields.

Studying nanostructure gradients in injection-molded polypropylene/montmorillonite composites by microbeam small-angle x-ray scattering

DEFF Research Database (Denmark)

Stribeck, Norbert; Schneider, Konrad; Zeinolebadi, Ahmad

2014-01-01

The core–shell structure in oriented cylindrical rods of polypropylene (PP) and nanoclay composites (NCs) from PP and montmorillonite (MMT) is studied by microbeam small-angle x-ray scattering (SAXS). The structure of neat PP is almost homogeneous across the rod showing regular semicrystalline......-shaped phyllosilicate filler particles....

PEG-template for surface modification of zeolite: A convenient material to the design of polypropylene based composite for packaging films

Science.gov (United States)

Toommee, S.; Pratumpong, P.

2018-06-01

Zeolite was successfully modified by conventional synthetic route. Polyethylene glycol was employed for surface modification of zeolite. The surface of zeolite exhibited therefore hydrophobic properties. Less than 5 wt% of modified zeolites with uniform size and shape were integrated into polypropylene matrix. Mechanical properties of composite exhibited the similar trend compare to neat polypropylene. Oxygen transmission rate and water vapor transmission rate were evaluated and it exhibited the strong potential to be a good candidate material in active packaging.

The influence of filler surface modification on mechanical and material properties of layered double hydroxide -containing polypropylene composites

CSIR Research Space (South Africa)

Moyo, Lumbidzani

2017-03-01

Full Text Available The processing and properties of layered double hydroxides (LDHs)-containing polypropylene (PP) composites have been studied extensively. However, no detailed studies have reported on how stearic acid (SA)-intercalated and SA-coated LDHs influence...

Flammability of polypropylene/organoclay nanocomposites

International Nuclear Information System (INIS)

Alves, Tatianny Soares; Barbosa, Renata; Carvalho, Laura Hecker de; Canedo, Eduardo Luis

2014-01-01

The flammabilities of nanocomposites made with three polypropylene grades (homo and copolymers) with 5 wt % of organoclay (Cloisite 20A), 5 or 15 wt % of maleated polypropylene as compatibilizer, and 0, 0.5 or 1 wt % of cis-13-docosenamide (Erucamide) as co-intercalant, were studied using the horizontal burning test UL94HB. Masterbatches prepared in an internal mixer were diluted in the polypropylene matrix using a corotating twin-screw extruder, with different screw configurations and operating at 240 or 480 rpm. Results indicate that the high burning rate of the composites was not affected by the processing conditions. For all formulations was observed a significant reduction in smoke release, lack of dripping and the formation of a char surface layer, that protected the core of the samples. (author)

Influence of the chemical modification and content of the clay on the mechanical properties of polypropylene and national bentonite composites

International Nuclear Information System (INIS)

Libano, Elaine V.D.G.; Pacheco, Elen B.A.V.; Visconte, Leila L.Y.

2011-01-01

The polypropylene/national clay composite was prepared by melt intercalation in a counter-rotating twin screw extruder, using bentonite as filler either in the natural (BENT) form or modified with the ammonium salt, cetyltrimethylammonium chloride (BENT-org). The clay was used in 1, 3 and 5%w. The influence of the modification and content of clay on the mechanical properties of this system was analysed. The analyses of infrared spectroscopy (FTIR) and X-ray diffraction (XRD) showed that clay organophilization did occur. The tensile modulus and the tensile strength at the yield point were not affected by chemical modification (BENT and BENT-org) or clay content. On the other hand, it was evidenced that the elongation at the yield point decreased with the addition of BENT and BENT-org to polypropylene. According to the thermogravimetric results, it was evidenced that the incorporation of clay into polypropylene improved thermal stability of the polymer in the composites with 5%w of BENT and 3 and 5%w of BENT-org. (author)

Preparation of Polypropylene/Montmorillonite Nanocomposites Using Ionizing Radiation

International Nuclear Information System (INIS)

Güven, Olgun; Zengin, Fatma

2011-01-01

Polymer/clay nanocomposites are new generation materials that bring significant changes in mechanical, thermal and permeation properties of base polymers by low clay loading. In this study, polypropylene/montmorillonite nanocomposites were prepared by melt intercalation method by using batch type mixer. Two polypropylene samples with different melt flow indexes are used as the matrix, maleic anhydride grafted polypropylene (PP-g-MAH), and polypropylene granules oxidized by radiation/ozone are used as compatibilizer and unmodified clay (Na + montmorillonite, MMT) as the filler. Aim of this study is to examine the effect of different compatibilizers in the mechanical properties of polypropylene composite. Firstly, PP/clay samples were prepared and the effect of clay was examined, then 5, 10, 20kGy oxidized/degraded polypropylenes were used as compatibilizer and, 10 kGy was determined to be the most suitable irradiation dose for the best compatibilizing effect. Polypropylene granules were ozonated until they contained carbonyl groups equivalent to 10kGy oxidized PP, which was checked by FTIR-ATR spectroscopy. UV-visible reflectance measurements were also made on film samples and no significant changes were observed in visible region. Nano structures of some nanocomposites were characterized by PALS (Positron Annihilation Lifetime Spectroscopy) where it was observed that the addition of clay decreased the number of free volume holes and free volume hole radia. The dispersion state of MMT within polymer matrix was analyzed by XRD (X-ray diffraction). Tensile tests were made and the effect of the addition of clay and compatibilizers investigated. At low melt flow index PP, 1% MMT of PP/10kGyPP/MMT nanocomposite showed an increase in E-modulus 26% and in tensile strength 8% as compared to those of pristine PP. In conclusion radiation degraded (chain scissioned and oxidized) PP has been found to show very good compatibilizing effect for the natural montmorillonite/polypropylene

Preparation of Polypropylene/Montmorillonite Nanocomposites Using Ionizing Radiation

Energy Technology Data Exchange (ETDEWEB)

Güven, Olgun; Zengin, Fatma

2011-07-01

Polymer/clay nanocomposites are new generation materials that bring significant changes in mechanical, thermal and permeation properties of base polymers by low clay loading. In this study, polypropylene/montmorillonite nanocomposites were prepared by melt intercalation method by using batch type mixer. Two polypropylene samples with different melt flow indexes are used as the matrix, maleic anhydride grafted polypropylene (PP-g-MAH), and polypropylene granules oxidized by radiation/ozone are used as compatibilizer and unmodified clay (Na{sup +} montmorillonite, MMT) as the filler. Aim of this study is to examine the effect of different compatibilizers in the mechanical properties of polypropylene composite. Firstly, PP/clay samples were prepared and the effect of clay was examined, then 5, 10, 20kGy oxidized/degraded polypropylenes were used as compatibilizer and, 10 kGy was determined to be the most suitable irradiation dose for the best compatibilizing effect. Polypropylene granules were ozonated until they contained carbonyl groups equivalent to 10kGy oxidized PP, which was checked by FTIR-ATR spectroscopy. UV-visible reflectance measurements were also made on film samples and no significant changes were observed in visible region. Nano structures of some nanocomposites were characterized by PALS (Positron Annihilation Lifetime Spectroscopy) where it was observed that the addition of clay decreased the number of free volume holes and free volume hole radia. The dispersion state of MMT within polymer matrix was analyzed by XRD (X-ray diffraction). Tensile tests were made and the effect of the addition of clay and compatibilizers investigated. At low melt flow index PP, 1% MMT of PP/10kGyPP/MMT nanocomposite showed an increase in E-modulus 26% and in tensile strength 8% as compared to those of pristine PP. In conclusion radiation degraded (chain scissioned and oxidized) PP has been found to show very good compatibilizing effect for the natural montmorillonite/polypropylene

Experimental study of co-pyrolysis of polyethylene/sawdust mixtures

Directory of Open Access Journals (Sweden)

Berrueco Cesar

2004-01-01

Full Text Available A study of the behavior of the thermal decomposition of mixtures of biomass and thermoplastics, such as polyethylene, is of interest for processes for the thermal recovery of industrial and urban wastes such as pyrolysis or gasification. No solid residue is formed during the thermal degradation of pure polyethylene. However, the addition of biomass, which generates char can vary the product distribution and increase the heating value of the gas obtained. A study of the thermal degradation of pine sawdust, polyethylene and mixtures of polyethylene and pine sawdust has been carried out in a fluidized bed reactor. Experiments were carried out at five different temperatures: 640, 685, 730, 780, and 850 ºC. The yields and composition of the derived oil, wax, and gas were determined. The addition of polyethylene increases the gas production and decreases the production of waxes and liquids for the different temperatures tested. The main gases produced from the co-pyrolysis process were, at low temperatures, carbon monoxide ethylene, carbon dioxide, propylene, butadiene, methane and pentadiene while at high temperatures the gas composition changed drastically, the main components being carbon monoxide (more than 33 wt.%, ethylene, methane benzene and hydrogen. The analysis of the liquid fraction shows a decrease of the concentration of oxygenated and aliphatic compounds.

In vivo assessment of an industrial waste product as a feed additive in dairy cows: Effects of larch (Larix decidua L.) sawdust on blood parameters and milk composition.

Science.gov (United States)

Tedesco, D; Garavaglia, L; Spagnuolo, M S; Pferschy-Wenzig, E M; Bauer, R; Franz, C

2015-12-01

When larch (Larix spp.) is processed in the wood industry, the sawdust is currently disposed of as waste or used as combustible material, even though it is rich in biologically active compounds. In this study the effect of larch sawdust supplementation on blood parameters as well as milk composition was examined in healthy mid-lactating dairy cows. Twenty-four multiparous Italian Friesian dairy cows were assigned to groups receiving either 300 g/day/cow of larch sawdust or a control diet, and treatments were continued for a 20 day period. Milk parameters were unaffected by treatment. A lower plasma total protein concentration was observed and can be attributed to a decrease in globulin concentration. A lower plasma urea concentration was also detected in the larch group. Moreover, biomarkers of liver function were influenced by the treatment. Total bilirubin was lower in larch-treated animals, and cholesterol tended to be lower. In addition, an interaction between day and treatment was observed for very low density lipoprotein. The concentration of other parameters, including reactive oxygen metabolites, superoxide dismutase, glutathione peroxidase and nitrotyrosine, did not differ between treatments. The observed benefits, together with the good palatability, make larch sawdust a promising candidate for the development of beneficial feed supplements for livestock. Further studies will be useful, particularly to evaluate its efficacy in different health conditions. Copyright © 2015 Elsevier Ltd. All rights reserved.

Evaluation of the environmental aging and mechanical properties of the polypropylene/sugarcane bagasse composites

International Nuclear Information System (INIS)

Paiva, Rayane Lima de Moura; Mulinari, Daniella Regina

2013-01-01

Polypropylene (PP) reinforced with fibers from sugarcane bagasse composites in different proportions were prepared. Also environmental aging was conducted for the composites and their mechanical properties determined. The results showed that chemical treatment caused changes in color and chemical composition of the fibers, removing impurities and amorphous constituents such as lignin and hemicellulose, techniques of FTIR, X-ray diffraction and scanning electron microscopy confirmed these data. Also, it was observed that addition of natural fiber in PP matrix provided an improvement in the mechanical properties materials. The weathering test revealed a slight mass gain after 75 days, but it was clear that the inclusion of fibers has a higher mass gain compared to pure PP. (author)

Pre-irradiation technique for processing of oil palm fruit bunch fibers - polypropylene composites

International Nuclear Information System (INIS)

Khairul Zaman Dahlan; Manarpaac, G.A.; Harun Jalaluddin

2002-01-01

Researches on oil palm empty fruit bunch (EFB) fibers and thermoplastic composites have been carried out by many workers in the last decade. The main focus was to enhance the properties of the resultant composites in view of the incompatibility of the two components. Thus, efforts have been made to enhance their properties by using coupling agents, treating the fibers and modifying the matrices. In this study, the effects of electron beam (EB) irradiation and some reactive additives (RAs) on the mechanical properties of EFB-PP (polypropylene) composites were evaluated. Different modes of irradiation were investigated. Mono, di and tri functional of monomers of RAs were used. irradiating PP alone, compared to irradiating the EFB fibers or irradiating both components, gave optimum properties for EFB-PP composites. Further, improvements of the properties of the composites were achieved with the addition of RAs with TMPTA (trymethylol propane triacrylate) giving the optimum results. (Author)

Effects of Particle Size and Surface Chemistry on the Dispersion of Graphite Nanoplates in Polypropylene Composites

Directory of Open Access Journals (Sweden)

Raquel M. Santos

2018-02-01

Full Text Available Carbon nanoparticles tend to form agglomerates with considerable cohesive strength, depending on particle morphology and chemistry, thus presenting different dispersion challenges. The present work studies the dispersion of three types of graphite nanoplates (GnP with different flake sizes and bulk densities in a polypropylene melt, using a prototype extensional mixer under comparable hydrodynamic stresses. The nanoparticles were also chemically functionalized by covalent bonding polymer molecules to their surface, and the dispersion of the functionalized GnP was studied. The effects of stress relaxation on dispersion were also analyzed. Samples were removed along the mixer length, and characterized by microscopy and dielectric spectroscopy. A lower dispersion rate was observed for GnP with larger surface area and higher bulk density. Significant re-agglomeration was observed for all materials when the deformation rate was reduced. The polypropylene-functionalized GnP, characterized by increased compatibility with the polymer matrix, showed similar dispersion effects, albeit presenting slightly higher dispersion levels. All the composites exhibit dielectric behavior, however, the alternate current (AC conductivity is systematically higher for the composites with larger flake GnP.

Effects of the cooling rate on the shear behavior of continuous glass fiber/impact polypropylene composites (GF-IPP)

KAUST Repository

Wafai, Husam

2016-09-20

Fiber-reinforced composites with improved dissipation of energy during impact loading have recently been developed based on a polypropylene copolymer commonly called impact polypropylene (IPP). Composites made of IPP reinforced with glass fibers (GF) are particularly attractive to the automotive industry due to their low cost and good impact resistance. In such composites, the cooling rate varies depending on processing techniques and manufacturing choices. Here, we study the effects of the cooling rate of GF-IPP composites on shear behavior, which is critical in impact applications, using [±45]s monotonic and cyclic (load/unload) tensile specimens. The specimens were manufactured under a wide range of cooling rates (3 °C/min, 22 °C/min, 500–1000 °C/min). Mainly dominated by the properties of the matrix, the global shear behavior of GF-IPP composites differed considerably with respect to the cooling rate. However, the performance of the fiber-matrix interface (chemically modified) appeared to be unaffected by the range of cooling rates used in this study. We found that the cooling rate has a minor effect on the rate of damage accumulation, while it strongly modifies the shear-activated rate-dependant viscoelastic behavior. © 2016 Elsevier Ltd

Melt rheological properties of natural fiber-reinforced polypropylene

Science.gov (United States)

Jarrod J. Schemenauer; Tim A. Osswald; Anand R. Sanadi; Daniel F. Caulfield

2000-01-01

The melt viscosities and mechanical properties of 3 different natural fiber-polypropylene composites were investigated. Coir (coconut), jute, and kenaf fibers were compounded with polypropylene at 30% by weight content. A capillary rheometer was used to evaluate melt viscosity. The power-law model parameters are reported over a shear rate range between 100 to 1000 s–1...

Flexure and impact properties of glass fiber reinforced nylon 6-polypropylene composites

Science.gov (United States)

Kusaseh, N. M.; Nuruzzaman, D. M.; Ismail, N. M.; Hamedon, Z.; Azhari, A.; Iqbal, A. K. M. A.

2018-03-01

In recent years, polymer composites are rapidly developing and replacing the metals or alloys in numerous engineering applications. These polymer composites are the topic of interests in industrial applications such as automotive and aerospace industries. In the present research study, glass fiber (GF) reinforced nylon 6 (PA6)-polypropylene (PP) composite specimens were prepared successfully using injection molding process. Test specimens of five different compositions such as, 70%PA6+30%PP, 65%PA6+30%PP+5%GF, 60%PA6+30%PP+10%GF, 55%PA6+30%PP+15%GF and 50%PA6+30%PP+20%GF were prepared. In the experiments, flexure and impact tests were carried out. The obtained results revealed that flexure and impact properties of the polymer composites were significantly influenced by the glass fiber content. Results showed that flexural strength is low for pure polymer blend and flexural strength of GF reinforced composite increases gradually with the increase in glass fiber content. Test results also revealed that the impact strength of 70%PA6+30%PP is the highest and 55%PA6+30%PP+15%GF composite shows moderate impact strength. On the other hand, 50%PA6+30%PP+20%GF composite shows low toughness or reduced impact strength.

Effect of compatibilizer, bamboo fiber size and content on the mechanical properties of PP-g-MA compatibilized polypropylene/bamboo fiber composites

International Nuclear Information System (INIS)

Caranti, Lilian R.A.; Bonse, Baltus C.; Costa, Ricardo A. da

2011-01-01

The contemporary need for ecological preservation is a challenge to the realms of science to develop environmentally sustainable materials and processes. Research on composites reinforced with natural cellulosic fibers seeks to meet that need. An investigation was performed on the mechanical and thermal behavior of a composite comprising a polypropylene thermoplastic matrix and bamboo fibers (Phyllostachys Edulis). Interfacial adhesion between the two materials was achieved by the addition of compatibilizer maleic anhydride grafted polypropylene PPg- MA. An investigation was carried out with 8 compositions by varying the average fiber size (lower level = 0.94 mm and upper level = 2.19 mm), fiber content (20 and 40 weight %) and compatibilizer PP-g-MA (1 and 4 weight %). The mechanical behavior of the composites was studied by carrying out tensile, flexural, impact and fatigue tests. Thermal behavior was investigated by heat deflection temperature tests. Crystallinity was measured by means of X Ray diffraction and fractured surfaces were observed and analyzed by scanning electron microscopy. (author)

THE IMPACT OF FRESH SAWDUST AND DRY PIG MANURE PRODUCED ON SAWDUST BEDDING APPLICATION ON THE NUTRIENTS MOBILITY IN SOIL AND SUGAR BEET YIELD

Directory of Open Access Journals (Sweden)

Peter Kováčik

2013-07-01

Full Text Available The objective of the pot trial carried out at the area of the Slovak University of Agriculture in Nitra was to determine the impact of dry pig manure produced on the sawdust bedding and sawdust litter on the level of nutrients’ mobility in the soil and sugar beet yield. The achieved results showed that one month after the sawdust and manure application to the soil, the contents of mobile nutrients (Nan, P, K, Ca, Mg in soil were lower than in the control unfertilized treatment. The sawdust litter immobilized nutrients more considerably than manure. Four months after the manure application into soil, its immobilization effect was not evident. On the contrary, the manure increased the mobile nutrients content in soil. In the second year of experiment the immobilization effect of sawdust litter was proved even four months after its application into soil. The application of manure increased considerably the beet root yield. The maximum root yield was determined in the treatment where the highest dose of manure was applied. The minimum root yield was detected in the treatment where the highest dose of sawdust litter was applied.

Thermal Conductivity Performance of Polypropylene Composites Filled with Polydopamine-Functionalized Hexagonal Boron Nitride.

Science.gov (United States)

Chen, Lin; Xu, Hong-Fei; He, Shao-Jian; Du, Yi-Hang; Yu, Nan-Jie; Du, Xiao-Ze; Lin, Jun; Nazarenko, Sergei

2017-01-01

Mussel-inspired approach was attempted to non-covalently functionalize the surfaces of boron nitride (BN) with self-polymerized dopamine coatings in order to reduce the interfacial thermal barrier and enhance the thermal conductivity of BN-containing composites. Compared to the polypropylene (PP) composites filled with pristine BN at the same filler content, thermal conductivity was much higher for those filled with both functionalized BN (f-BN) and maleic anhydride grafted PP (PP-g-ma) due to the improved filler dispersion and better interfacial filler-matrix compatibility, which facilitated the development of more thermal paths. Theoretical models were also applied to predict the composite thermal conductivity in which the Nielsen model was found to fit well with the experimental results, and the estimated effective aspect ratio of fillers well corresponded to the degree of filler aggregation as observed in the morphological study.

Composite TiO2/hydrocarbon plasma polymer films prepared by magnetron sputtering of TiO2 and poly(propylene)

Czech Academy of Sciences Publication Activity Database

Drabik, M.; Hanuš, J.; Kousal, J.; Choukourov, A.; Biederman, H.; Slavínská, D.; Macková, Anna; Pešička, J.

2007-01-01

Roč. 4, č. 6 (2007), s. 654-663 ISSN 1612-8850 Institutional research plan: CEZ:AV0Z10480505 Keywords : composite thin films * magnetron * poly(propylene) (PP) Subject RIV: BE - Theoretical Physics Impact factor: 2.132, year: 2007

Effect of Particle Size on Mechanical Properties of Sawdust-High Density Polyethylene Composites under Various Strain Rates

Directory of Open Access Journals (Sweden)

Haliza Jaya

2016-06-01

Full Text Available There is a need to understand the effect of wood particle size, as it affects the characteristics of wood-based composites. This study considers the effect of wood particle size relative to the dynamic behavior of wood composites. The compression Split Hopkinson Pressure Bar (SHPB was introduced to execute dynamic compression testing at the strain rate of 650 s-1, 900 s-1, and 1100 s-1, whereas a conventional universal testing machine (UTM was used to perform static compression testing at the strain rate of 0.1 s-1, 0.01 s-1, and 0.001 s-1 for four different particle sizes (63 µm, 125 µm, 250 µm, and 500 µm. The results showed that mechanical properties of composites were positively affected by the particle sizes, where the smallest particle size gave the highest values compared to the others. Moreover, the particle size also affected the rate sensitivity and the thermal activation volume of sawdust/HDPE, where smaller particles resulted in lower rate sensitivity. For the post-damage analysis, the applied strain rates influenced deformation behavior differently for all particle sizes of the specimens. In a fractographic analysis under dynamic loading, the composites with large particles experienced severe catastrophic deformation and damages compared to the smaller particles.

The effect of modified ijuk fibers to crystallinity of polypropylene composite

Science.gov (United States)

Prabowo, I.; Nur Pratama, J.; Chalid, M.

2017-07-01

Nowadays, plastics becomes concern associated with its degradation and environmental issues. It has led studies to develop an environmental-friendly material. To minimize the impact of those problems, recently the usage of natural fibers as a filler are introduced because of biodegradability and availability. The promising natural fiber is “ijuk” fiber from Arenga pinnata plant as a filler and polypropylene (PP) polymer as a matrix. Unfortunately, the natural fibers and polymers have the different properties on which polymers are polar while natural fibers are non-polar so that reducing the compatibility and resulting the poor crystallinity. To enhance the compatibility and crystallinity, ijuk fibers were prepared by multistage treatments including alkalinization with 5 and 10% sodium hydroxide (NaOH), oxidation with 3 and 6% sodium hypochlorite (NaClO) and hydrolysis with 20% sulphuric acid (H2SO4) in sequences. The purposes of multistage treatments are to remove the components such as lignin, wax, hemicellulose, to cause an oxidative fragmentation of remaining lignin and to annihilate the amorphous parts respectively. Fourier-Transform Infrared (FTIR) confirms the compatibility meanwhile Differential Scanning Calorimetry (DSC) reveals the crystallinity and Scanning Electron Microscope (SEM) displays surface morphology of polypropylene. The experiments were revealing that the effects of “ijuk” fibers by the multistage treatments of 5 and 10% NaOH resulting the crystallinity of polypropylene around 31.2 and 27.64% respectively compared to the crystallinity before adding the “ijuk” fibers for 16.8%. It indicates that the entire treatments increasing the compatibility and crystallinity of polypropylene. In addition, the use of 5% NaOH offers the better crystallinity than non-treated polypropylene. The experiments conclude that by adding alkalinized “ijuk” fibers of multistage treatments can increase the compatibility and crystallinity of polypropylene.

Effect of Nanosilica Filled Polyurethane Composite Coating on Polypropylene Substrate

Directory of Open Access Journals (Sweden)

Yern Chee Ching

2013-01-01

Full Text Available Acrylic based polyurethane (PU coatings with various amounts of nanosilica contents were prepared using solution casting method. The nanosilica (SiO2 particles used are around 16 nm in diameter. The friction and wear test was conducted using the reciprocating wear testing machine. The tests were performed at rotary speed of 100 rpm and 200 rpm with load of 0.1 kg to 0.4 kg under 1 N interval. The effect of the PU/nano-SiO2 composite coating on friction and wear behavior of polypropylene substrate was investigated and compared. The worn surface of coating film layer after testing was investigated by using an optical microscope. The introduction of PU/nanosilica composite coating containing 3 wt% of nano-SiO2 content gives the lowest friction coefficient and wear rate to PP substrate. Both the friction and wear rate of PP substrate coated with >3 wt% of nano-SiO2 filled PU coating would increase with the increasing of applied load and sliding time.

Effect of processing conditions on the mechanical properties of polypropylene/bentonite nano composites

International Nuclear Information System (INIS)

Alves, Tatianny S.; Cipriano, Pamela B.; Lira, Vanize F.; Canedo, Eduardo L.; Carvalho, Laura H. de

2009-01-01

This work dealt with the effect of processing conditions on the properties of polypropylene/bentonite compounds, using natural clay and an organoclay prepared with hexadecyl trimethyl ammonium bromide. Compounds with 1% clay were prepared by melt compounding in a single-screw extruder and in a counter-rotating twin-screw extruder, and characterized x-ray diffraction; tensile and impact mechanical tests. X ray diffraction results on clays and compounds show that the surfactant was incorporated within the clay galleries and that intercalated nano composites were obtained with the organoclay processed in either the single or the twin-screw extruder. The data also indicated that, without the addition of a compatibilizer, no significant variation of mechanical properties was observed for the composites processed in either extruder. (author)

Synthesis and application of a ternary composite of clay, saw-dust and peanut husks in heavy metal adsorption.

Science.gov (United States)

Mungondori, Henry H; Mtetwa, Sandile; Tichagwa, Lilian; Katwire, David M; Nyamukamba, Pardon

2017-05-01

The adsorption of a multi-component system of ferrous, chromium, copper, nickel and lead on single, binary and ternary composites was studied. The aim of the study was to investigate whether a ternary composite of clay, peanut husks (PH) and saw-dust (SD) exhibited a higher adsorption capacity than that of a binary system of clay and SD as well as a single component adsorbent of PH alone. The materials were used in their raw state without any chemical modifications. This was done to retain the cost effective aspect of the naturally occurring adsorbents. The adsorption capacities of the ternary composite for the heavy metals Fe 2+ , Cr 3+ , Cu 2+ , Ni 2+ and Pb 2+ were 41.7 mg/g, 40.0 mg/g, 25.5 mg/g, 41.5 mg/g and 39.0 mg/g, respectively. It was found that the ternary composite exhibited excellent and enhanced adsorption capacity compared with both a binary and single adsorbent for the heavy metals Fe 2+ , Ni 2+ and Cr 3+ . Characterization of the ternary composites was done using Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and thermogravimetric analysis (TGA). Kinetic models and adsorption isotherms were also studied. The pseudo second order kinetic model and the Langmuir adsorption isotherm best described the adsorption mechanisms for the ternary composite towards each of the heavy metal ions.

Analysis physical properties of composites polymer from cocofiber and polypropylene plastic waste with maleic anhydrate as crosslinking agent

Science.gov (United States)

Pelita, E.; Hidayani, T. R.; Akbar, A.

2017-07-01

This research was conducted with the aim to produce composites polymer with polypropylene plastic waste materials and cocofiber which aims to produce wood replacement material in the home furnishings industry. This research was conducted with several stages. The first stage is the process of soaking coco fiber with detergent to remove oil and 2% NaOH. The second stage is to combine the polypropylene plastic waste with cocofiber is a chemical bond, modification by adding maleic anhydride as a crosslinking agent and benzoyl peroxide as an initiator each as much as 1%. Mixing materials done by reflux method using xylene solvent. In this study, carried out a wide range of weight variation of coco fiber are added to the 10, 20, 30, 40 and 50%. The third stage is a polymer composite molding process using hot press at a temperature of 158°C. The results of polymer composites Showed optimum condition on the addition of 40% cocofiber with supple tensile strength value of 90.800 kgf /cm2 and value of elongation break at 3.6726 x 104 (kgf/cm2), melting point at 160.02°C, burning point 463.43°C, residue of TGA is 19%, the density of 0.84 g/mL. From these data, conclude that the resulting polymer composites meet the SNI 03-2105-2006 about ordinary composite polymer and polymer composite structural type 8 regular types from 17.5 to 10.5.

Influence of Rubber Powders on Foaming Behavior and Mechanical Properties of Foamed Polypropylene Composites

Directory of Open Access Journals (Sweden)

HE Yue

2017-02-01

Full Text Available Polypropylene/rubber powders composites with different kinds of rubber powders were foamed by injection molding machine equipped with volume-adjustable cavity. The effect of dispersity of rubber powders and crystallization behavior of composites on the foaming behavior and mechanical properties was investigated. The results show that the addition of rubber powders can improve the cell structure of foamed PP with fine and uniform cell distribution. And cell density and size of PP/PP-MAH/NBR foams are 7.64×106cell/cm3 and 29.78μm respectively, which are the best among these foams. Combining cell structures with mechanical properties, notch impact strength of PP/PP-MAH/CNBR composites increases approximately by 2.2 times while tensile strength is reduced just by 26% compared with those of the pure PP. This indicates that PP/PP-MAH/CNBR composites are ideal foamed materials.

Pretreatment of sawdust and its hydrolysis with immobilised enzymes

International Nuclear Information System (INIS)

Kumakura, M.; Kaetsu, I.

1988-01-01

The pretreatment of sawdust by radiation and its hydrolysis with immobilised cellulase were studied. The sawdust was irradiated with a number of different irradiation doses and crushed with two kinds of crusher; pulveriser and ball mill. In ball-mill crushing, the crushing time to get a fine powder was reduced by radiation treatment and the conversion yield of cellulose to glucose in the enzyme hydrolysis was increased. It was found that sawdust pretreated by radiation and subsequent crushing was efficiently hydrolysed by immobilised cellulase which itself was obtained by a radiation polymerisation technique. (author)

Effect of fibre treatment using fluorosilane on Sansevieria Trifasciata/Polypropylene composite

Science.gov (United States)

Aref, Yanzur Mohd; Baharum, Azizah

2018-04-01

Recently, there is an increasing interest in the development of wood-plastic composites (WPC) due to their advantages such as wide availability, low cost, environment friendliness and sustainability. However, some major factors limiting the large scales production of WPC including the tendency of natural fibres to absorb water and the poor compatibility between fibre and matrix. In this study, we investigated the effectiveness of natural fibre treatment using fluorosilane in imparting hydrophobicity to the polypropylene (PP) matrix composite reinforced with Sansevieria Trifasciata (ST) fibres. ST fibres are subjected to silane treatment with 1H,1H,2H,2H-perfluorooctyltriethoxsysilane (POTS) at 1, 3 and 5% for a period of 2 hours. Influence of POTS treatment on the physical and mechanical properties of composites was studied to determine the optimum condition of silane treatment. The water contact angle (WCA) of WPC increased after POTS treatment where the highest value of 115° was shown by 3% POTS treated ST/PP composite. Based on mechanical properties results, incorporation of POTS treated ST fibre improves the mechanical properties with the enhancement of flexural and impact strength. The treatment with 3% POTS revealed statistically higher flexural strength and modulus compared to 1 and 5%. The water absorption test of ST/PP composites also gives the best result for 3% POTS treatment with 20.90% water uptake.

The effect of alkaline treatment and fiber orientation on impact resistant of bio-composites Sansevieria trifasciata fiber/polypropylene as automotive components material

Science.gov (United States)

Shieddieque, Apang Djafar; Mardiyati, Suratman, Rochim; Widyanto, Bambang

2018-04-01

The increasing amount of car usage is causing an escalated amount of fuel consumption and CO2 emission. It implicates demand for the automotive industry to increase the efficiency of their products, One of the most effective ways to solve the issue is to find green weight light material for the interior automotive component. The Aim of this research was to investigate the effect of alkaline treatment and fiber orientation on the impact resistant of material bio- composite sansevieiria trifasciata fiber/Polypropylene. In this research, bio-composites sansevieria trifasciata fiber/Polypropylene was prepared with random fiber orientation and unidirectional orientation by using a hot press method with pressure 140 Bar and temperature 240°C. Fiber was taken from Sansevieria trifasciata by using mechanical retting. In this study, Sansevieria fiber was given alkaline treatment (mercerization) with NaOH 3% (w/w) solution at temperature 100°C for an hour. The fraction of fiber volume that were used in this experiment are 0%, 5%, 10%, and 15%. The impact test was conducted based on ASTM D 6110 - 04, and the fracture analysis was investigated by scanning electron microscope (SEM). The best result of impact toughness and fracture analysis were achieved by bio composite untreated and unidirectional sansevieria trifasciata fiber/Polypropylene with fiber volume fraction of 15%, which was 48.092kJ/m2 for impact resistant. As compared to the impact toughness standard, which needed for interior automotive component, the impact toughness of sansevieria trifasciata fiber/Polypropylene has fulfilled the standard of the interior material automotive industry. Therefore, this material can be potentially used as materials on the car exterior component.

Abdominal wall hernia repair with a composite ePTFE/polypropylene mesh: clinical outcome and quality of life in 152 patients

DEFF Research Database (Denmark)

Iversen, E; Lykke, Anna; Hensler, M

2010-01-01

No consensus has yet been reached regarding the optimal mesh for the repair of small ventral hernias. A composite polytetrafluoroethylene/polypropylene mesh (Ventralex(®)) is designed for this purpose, and this paper reports its use in a larger series of patients....

The Usage Of Nutshell In The Production of Polypropylene Based on Polymer Composite Panels

Directory of Open Access Journals (Sweden)

Selçuk Akbaş

2013-04-01

Full Text Available Natural fibers have been commonly utilized to reinforced materials for many years. Recently due to advantages of natural fibers such as low cost, high physical and mechanical resistance are produced plastic-composite materials by mixing various proportions. In addition, plastic composites are used natural fibers include agricultural wastes (wheat straw, rice straw, hemp fiber, shells of various dry fruits, etc.. In this study, polymer composites were manufactured using waste nutshell flour as filler and polypropylene (PP as polymer matrix. The nutshell-PP composites were manufactured via extrusion and compression methods. The final product tested to determine their tensile, flexural, impact strength properties as well as some physical features such as thickness swelling and water absorptions. The best results were obtained composites containing 30% nutshell flour. In addition, composites which were produced nutshell provided the values of ASTM D6662 standard. The data collected in our country which waste a large portion of nutshell allows for the evaluation of the production polymer composites. The incorporation of nutshell flour feasible to produce plastic composites when appropriate formulations were used. As a result hazelnut shell which was considered agricultural waste can be utilized in polymer composite production.

Radiation resistant modified polypropylene; Polipropylen modyfikowany odporny radiacyjnie

Energy Technology Data Exchange (ETDEWEB)

Bojarski, J; Zimek, Z [Institute of Nuclear Chemistry and Technology, Warsaw (Poland)

1997-10-01

Radiation technology for production of radiation resistant polypropylene for medical use has been presented. The method consists in radiation induced copolymerization of polypropylene with ethylene and addition of small amount of copolymer of polyethylene and vinyl acetate. The material of proposed composition has a very good mechanical properties and elevated radiation resistivity decided on possibility of radiosterilization of products made of this material and designed for medical use. 3 figs, 3 tabs.

Impact of chemical treatments on the mechanical and water absorption properties of coconut fibre (Cocos nucifera reinforced polypropylene composites

Directory of Open Access Journals (Sweden)

Isiaka O. OLADELE

2016-07-01

Full Text Available In this work, chemically treated coconut fibres were used to reinforce Homopolymer Polypropylene in order to ascertain the effect of the treatments on the mechanical and water absorption properties of the composites produced. Coconut fibre was first extracted from its husk by soaking it in water and was dried before it was cut into 10 mm lengths. It was then chemically treated in alkali solution of sodium hydroxide (NaOH and potassium hydroxide (KOH in a shaker water bath. The treated coconut fibres were used as reinforcements in polypropylene matrix to produce composites of varied fibre weight contents; 2, 4, 6, 8 and 10 wt.%. Tensile and flexural properties were investigated using universal testing machine while water absorption test was carried out on the samples for 7 days. It was observed from the results that, NaOH treated samples gave the best tensile properties while KOH treated samples gave the best flexural and water repellent properties.

Flat-pressed wood plastic composites from sawdust and recycled polyethylene terephthalate (PET): physical and mechanical properties.

Science.gov (United States)

Rahman, Khandkar-Siddikur; Islam, Md Nazrul; Rahman, Md Mushfiqur; Hannan, Md Obaidullah; Dungani, Rudi; Khalil, Hps Abdul

2013-01-01

This study deals with the fabrication of composite matrix from saw dust (SD) and recycled polyethylene terephthalate (PET) at different ratio (w/w) by flat-pressed method. The wood plastic composites (WPCs) were made with a thickness of 6 mm after mixing the saw dust and PET in a rotary type blender followed by flat press process. Physical i.e., density, moisture content (MC), water absorption (WA) and thickness swelling (TS), and mechanical properties i.e., Modulus of Elasticity (MOE) and Modulus of Rupture (MOR) were assessed as a function of mixing ratios according to the ASTM D-1037 standard. WA and TS were measured after 24 hours of immersion in water at 25, 50 and 75°C temperature. It was found that density decreased 18.3% when SD content increased from 40% to 70% into the matix. WA and TS increased when the PET content decreased in the matrix and the testing water temperature increased. MOE and MOR were reached to maximum for the fabricated composites (2008.34 and 27.08 N/mm(2), respectively) when the SD content were only 40%. The results indicated that the fabrication of WPCs from sawdust and PET would technically feasible; however, the use of additives like coupling agents could further enhance the properties of WPCs.

Electrical resistivity and thermal properties of compatibilized multi-walled carbon nanotube/polypropylene composites

Directory of Open Access Journals (Sweden)

A. Szentes

2012-06-01

Full Text Available The electrical resistivity and thermal properties of multi-walled carbon nanotube/polypropylene (MWCNT/PP composites have been investigated in the presence of coupling agents applied for improving the compatibility between the nanotubes and the polymer. A novel olefin-maleic-anhydride copolymer and an olefin-maleic-anhydride copolymer based derivative have been used as compatibilizers to achieve better dispersion of MWCNTs in the polymer matrix. The composites have been produced by extrusion followed by injection moulding. They contained different amounts of MWCNTs (0.5, 2, 3 and 5 wt% and coupling agent to enhance the interactions between the carbon nanotubes and the polymer. The electrical resistivity of the composites has been investigated by impedance spectroscopy, whereas their thermal properties have been determined using a thermal analyzer operating on the basis of the periodic thermal perturbation method. Rheological properties, BET-area and adsorption-desorption isotherms have been determined. Dispersion of MWCNTs in the polymer has been studied by scanning electron microscopy (SEM.

Briquetting of coal fines and sawdust. Part 1: binder and briquetting-parameters evaluations

Energy Technology Data Exchange (ETDEWEB)

D. Taulbee; D.P. Patil; Rick Q. Honaker; B.K. Parekh [University of Kentucky, Lexington, KY (United States). Center for Applied Energy Research

2009-01-15

Various technical and economic aspects relating to the briquetting of fine coal with sawdust have been evaluated with the results for two segments of that study presented here: binder and briquetting-parameter evaluations. Approximately 50 potential binder formulations were subjected to a series of screening evaluations to identify three formulations that were the most cost effective for briquetting fine coal with sawdust. Two of the binders, guar gum and wheat starch, were selected as most suitable for the pulverized coal market while the third formulation, lignosulfonate/lime, was targeted for the stoker market. Following binder selection, a number of briquetting parameters including binder and sawdust concentration, sawdust type, briquetting pressure and dwell time, coal and sawdust particle size, clay content, moisture content, and cure temperature and cure time were evaluated. Briquetting pressure and dwell time have the least impact while binder and sawdust concentrations, sawdust type, and curing conditions exerted the greatest influence on briquette quality. 7 refs.

Development of new baked bricks based on clay and sawdust

Directory of Open Access Journals (Sweden)

Benjeddou Omrane

2018-01-01

Full Text Available Current research in the field of building materials is oriented towards the recovery of waste to ensure the lightening of certain building elements and energy saving. The objective of this study is to produce a new bricks by adding sawdust to clay mixtures. The first part of this experimental work consists on detremining the proper manufacturing process and cooking diagram for these new bricks. In the second part, the effect of the maximum cooking temperature, the firing phase time's of the bricks and the sawdust prportion on the physical and mechanical properties of the new bricks have been studied. The studied properties are the absorption ratio, the unit weight and the compressive strength. The results showed that the addition of an increasing amount of sawdust tends to modify the physical and mechanical properties of the cooked samples. The presence of sawdust reduces the number of connections between the clay grains and produces a lighter, more absorbent and less resistant material. Finally, the results showed that the manufacture of bricks based on sawdust is possible.

Polypropylene compositional evolution under 3.5 MeV He+ ion irradiation

Science.gov (United States)

Abdesselam, M.; Muller, D.; Djebara, M.; Chami, A. C.; Montgomery, P.

2012-05-01

A helium beam at 3.5 MeV was used to induce damage in thin polypropylene film of 5.1 μm in thickness. The fluence ranges from 2 × 1012 to 3.5 × 1015 cm-2. The evolution of the atomic composition (C and H) as a function of the fluence was investigated in situ by forward elastic scattering (C(α, α)C) and hydrogen elastic recoil detection (H(α, H)α), respectively. The helium beam was used at the same time for irradiation and analysis. In respect to the high sensitivity of the polypropylene to radiation damage, the beam current was kept at very low intensity of 0.5 nA. The mass loss becomes significant above a fluence of ˜5 × 1013 He+ cm-2. The carbon depletion levels off at a fluence of ˜5 × 1014 He+ cm-2 approximately while hydrogen loss continues to be present along the whole of the studied fluence range. The final carbon and hydrogen losses, at the highest fluence, are around 17% and 48% of their initial contents, respectively. Satisfactory fits to the release curves have been obtained in the framework of the bulk molecular recombination model (BMR). The deduced hydrogen and carbon release cross sections are 7.8 and 65.2 × 10-16 cm2, respectively. A comparison with our previous measurements of polyethylene terephthalate (PET) film irradiated with 3.7 MeV He+ beam is made.

Development of plasma-treated polypropylene nonwoven-based composites for high-performance lithium-ion battery separators

International Nuclear Information System (INIS)

Li, Xiaofei; He, Jinlin; Wu, Dazhao; Zhang, Mingzu; Meng, Juwen; Ni, Peihong

2015-01-01

Graphical abstract: A composite separator based on plasma-treated fluorinated polypropylene (PP) nonwoven, poly(vinylidene fluoride-co-hexafluoropropylene) (PVdF-HFP) and SiO 2 nanoparticles exhibiting enhanced thermal stability, ionic conductivity and electrochemical properties. Display Omitted -- Highlights: •Fluorinated segments are introduced on the surface of PP nonwoven through plasma treatment. •The obtained composite separators exhibit better physical and electrochemical properties. •The capacity of half-cell with composite separator keeps above 150 mA h g −1 after 100 charge–discharge cycles. -- Abstract: Separators have drawn substantial attention because of their important role in achieving the safety and good electrochemical performance of lithium-ion batteries. In this study, we report a new type of composite membrane prepared by a combination of fluorinated polypropylene (PP) nonwoven fabric, poly(vinylidene fluoride-co-hexafluoropropylene) (PVdF-HFP) and SiO 2 nanoparticles. 2, 2, 3, 3, 4, 4, 5, 5-Octafluoropentyl methacrylate (OFPMA) is first grafted on the surface of PP nonwoven by plasma treatment to improve the nonwoven’s adhesion with PVdF-HFP. Two kinds of composite separators have been prepared by using the different PP nonwovens together with PVdF-HFP and SiO 2 nanoparticles. They were separately designated as PHS for commercially raw PP nonwoven system and PHS-n for OFPMA-modified PP nonwoven systems (n means plasma treatment time). The morphology, electrolyte uptake, ionic conductivity and electrochemical properties of the composite separators have been analyzed by scanning electron microscope (SEM) analysis, impedance measurement, charge-discharge cycle and C-rate tests, respectively. The results indicate that PHS-10 composite separator using the modified PP nonwoven treated by plasma for 10 min exhibits much better properties than PHS separator, including an improved mechanical property, thermal stability, electrolyte uptake

Lignocellulose nanofibers prepared by ionic liquid pretreatment and subsequent mechanical nanofibrillation of bagasse powder: Application to esterified bagasse/polypropylene composites.

Science.gov (United States)

Ninomiya, Kazuaki; Abe, Megumi; Tsukegi, Takayuki; Kuroda, Kosuke; Tsuge, Yota; Ogino, Chiaki; Taki, Kentaro; Taima, Tetsuya; Saito, Joji; Kimizu, Mitsugu; Uzawa, Kiyoshi; Takahashi, Kenji

2018-02-15

In the present study, we examined the efficacy of choline acetate (ChOAc, a cholinium ionic liquid))-assisted pretreatment of bagasse powder for subsequent mechanical nanofibrillation to produce lignocellulose nanofibers. Bagasse sample with ChOAc pretreatment and subsequent nanofibrillation (ChOAc/NF-bagasse) was prepared and compared to untreated control bagasse sample (control bagasse), bagasse sample with nanofibrillation only (NF-bagasse) and with ChOAc pretreatment only (ChOAc-bagasse). The specific surface area was 0.83m 2 /g, 3.1m 2 /g, 6.3m 2 /g, and 32m 2 /g for the control bagasse, ChOAc-bagasse, NF-bagasse, and the ChOAc/NF-bagasse, respectively. Esterified bagasse/polypropylene composites were prepared using the bagasse samples. ChOAc/NF-bagasse exhibited the best dispersion in the composites. The tensile toughness of the composites was 0.52J/cm 3 , 0.73J/cm 3 , 0.92J/cm 3 , and 1.29J/cm 3 for the composites prepared using control bagasse, ChOAc-bagasse, NF-bagasse, and ChOAc/NF-bagasse, respectively. Therefore, ChOAc pretreatment and subsequent nanofibrillation of bagasse powder resulted in enhanced tensile toughness of esterified bagasse/polypropylene composites. Copyright © 2017 Elsevier Ltd. All rights reserved.

Corrosion of the reinforcing steel in the inhibited sawdust concrete construction

International Nuclear Information System (INIS)

Kobuliev, Z.V.

2005-01-01

In the article described the way of protection of the reinforcing steel in sawdust concrete construction by adding to inhibited sawdust concrete mixture containing nitrate-nitride calcium chloride (NNCC) and (NH 4 ) 2 Cr 2 O 7 , also NaNO 2 + NaNO 3 +NH 4 Cl and CaCl 2 +(NH 4 ) 2 +Cr 2 . There is determined, that the use of these additives increase strength properties of sawdust concrete at 28 day to 40-55% in comparison with sawdust concrete containing CaCl 2 , and decrease its corrosion-resistance activity, and provided reliability under condition of double excess of inhibitor ions (NO 2- , Cr 2 O 7- ) in comparison with ions (Cl-)

Adsorption of heavy metal ions by sawdust of deciduous trees

International Nuclear Information System (INIS)

Bozic, D.; Stankovic, V.; Gorgievski, M.; Bogdanovic, G.; Kovacevic, R.

2009-01-01

The adsorption of heavy metal ions from synthetic solutions was performed using sawdust of beech, linden and poplar trees. The adsorption depends on the process time, pH of the solution, type of ions, initial concentration of metals and the sawdust concentration in suspension. The kinetics of adsorption was relatively fast, reaching equilibrium for less than 20 min. The adsorption equilibrium follows Langmuir adsorption model. The ion exchange mechanism was confirmed assuming that the alkali-earth metals from the adsorbent are substituted by heavy metal ions and protons. On lowering the initial pH, the adsorption capacity decreased, achieving a zero value at a pH close to unity. The maximum adsorption capacity (7-8 mg g -1 of sawdust) was achieved at a pH between 3.5 and 5 for all the studied kinds of sawdust. The initial concentration of the adsorbate and the concentration of sawdust strongly affect the process. No influence of particles size was evidenced. A degree of adsorption higher than 80% can be achieved for Cu 2+ ions but it is very low for Fe 2+ ions, not exceeding 10%.

Mechanical and thermal properties of bio-composites based on polypropylene reinforced with Nut-shells of Argan particles

International Nuclear Information System (INIS)

Essabir, H.; Hilali, E.; Elgharad, A.; El Minor, H.; Imad, A.; Elamraoui, A.; Al Gaoudi, O.

2013-01-01

Highlights: ► Nuts-shells of Argan particles are used as reinforcement in thermoplastic matrix. ► Particles are homogeneously dispersed and distributed within PP matrix. ► Mechanical and thermal characterization of the composite are applied. ► Particles–matrix adhesion was assured by the use of a SBS compatibilizer. - Abstract: This study treats the combined effects of both particle sizes and particle loading on the mechanical and thermal properties of polypropylene (PP) composites reinforced with Nut-shells of Argan (NA) particles. Three range sizes of particles were used in the presence of a polypropylene matrix grafted with 8 wt.% of a linear block copolymer based on styrene and butadiene coupling agent, to improve adhesion between the particles and the matrix. The composites were prepared through melt-blending using an internal mixer and the tensile specimens were prepared using a hot press molding machine. Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectroscopy (FT-IR), Thermo Gravimetric Analysis (TGA), Differential Thermal Analysis (DTA) and tensile tests were employed to characterize the composites at 10, 15, 20 and 25 wt.% particle contents. Results show a clear improvement in Young’s modulus from the use of particles when compared to the neat PP, a gain of 42.65%, 26.7% and 2.9% at 20 wt.% particle loading, for particle range 1, 2 and 3, respectively. In addition a notable increase in the Young’s modulus was observed when decrease the particle size. The thermal stability of composites exhibits a slight decrease (256–230 °C) with particles loading from 10 to 25 wt.%, against neat PP (258 °C)

Study on the Properties of Microcapsulated Chlorocyclophosphazene Polypropylene Composites%三聚氯化磷腈微胶囊阻燃剂/聚丙烯复合材料的性能研究

Institute of Scientific and Technical Information of China (English)

刘亚青; 赵贵哲

2007-01-01

Microcapsulated chlorocyclophosphazenes were synthesized, and then microcapsulated chlorocyclophosphazene/polypropylene(PP) composites were prepared.The results showed that microcapsulated chlorocyclophosphazene had good high thermal stability through thermogravimetric analysis (TGA).The flammability and mechanical properties of microcapsulated chlorocyclophosphazene/polypropylene composites were investigated by limiting oxygen index experiment, UL 94V flame retardancy test, cone calorimetry, tensile experiment, and impact test, respectively.It was shown that the microcapsulated chlorocyclophosphazene/PP composites had better tensile strength, impact strength, flame retardant properties and smoke suppress properties compared with chlorocyclophosphazene/PP composites.

Polypropylene compositional evolution under 3.5 MeV He+ ion irradiation

International Nuclear Information System (INIS)

Abdesselam, M.; Muller, D.; Djebara, M.; Chami, A.C.; Montgomery, P.

2012-01-01

A helium beam at 3.5 MeV was used to induce damage in thin polypropylene film of 5.1 μm in thickness. The fluence ranges from 2 × 10 12 to 3.5 × 10 15 cm −2 . The evolution of the atomic composition (C and H) as a function of the fluence was investigated in situ by forward elastic scattering (C(α, α)C) and hydrogen elastic recoil detection (H(α, H)α), respectively. The helium beam was used at the same time for irradiation and analysis. In respect to the high sensitivity of the polypropylene to radiation damage, the beam current was kept at very low intensity of 0.5 nA. The mass loss becomes significant above a fluence of ∼5 × 10 13 He + cm −2 . The carbon depletion levels off at a fluence of ∼5 × 10 14 He + cm −2 approximately while hydrogen loss continues to be present along the whole of the studied fluence range. The final carbon and hydrogen losses, at the highest fluence, are around 17% and 48% of their initial contents, respectively. Satisfactory fits to the release curves have been obtained in the framework of the bulk molecular recombination model (BMR). The deduced hydrogen and carbon release cross sections are 7.8 and 65.2 × 10 −16 cm 2 , respectively. A comparison with our previous measurements of polyethylene terephthalate (PET) film irradiated with 3.7 MeV He + beam is made.

STRUCTURAL EVOLUTION AND COMPOSITION CHANGE IN THE SURFACE REGION OF POLYPROPYLENE/CLAY NANOCOMPOSITES ANNEALED AT HIGH TEMPERATURES

Institute of Scientific and Technical Information of China (English)

唐涛

2009-01-01

A model experiment was done to clear the formation mechanism of protective layers during combustion of polypropylene(PP)/organically modified montmorillonite(OMMT) nanocomposites.The investigation was focused on the effects of annealing temperature on the structural changes and protective layer formation.The decomposition of OMMT and degradation of PP/OMMT nanocomposites were characterized by means of thermogravimetric analysis(TGA).The structural evolution and composition change in the surface region of...

Structural interpretations of deformation and fracture behavior of polypropylene/multi-walled carbon nanotube composites

International Nuclear Information System (INIS)

Ganss, Martin; Satapathy, Bhabani K.; Thunga, Mahendra; Weidisch, Roland; Poetschke, Petra; Jehnichen, Dieter

2008-01-01

The deformation and crack resistance behavior of polypropylene (PP) multi-walled carbon nanotube (MWNT) composites have been studied and their interrelation to the structural attributes studied by transmission electron microscopy (TEM), atomic force microscopy (AFM), scanning electron microscopy (SEM), wide-angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC) and polarization light microscopy has been discussed. The composites were produced from industrial available MWNT by extrusion melt-mixing and injection-molding. In stress-strain measurements a strong increase in the yield stress and the Young's modulus at low MWNT contents has been observed, which was attributed to an efficient load transfer between the carbon nanotubes and polypropylene matrix through a good polymer-nanotube adhesion as indicated by SEM. The extent of enhancement in mechanical properties above 1.5 wt.% of MWNT decreased due to an apparently increased tendency of clustering of carbon nanotubes. Several theoretical models have been taken into account to explain the mechanical properties and to demonstrate the applicability of such models to the system under investigation. The crack resistance behavior has been studied with the essential work of fracture (EWF) approach based on post-yield fracture mechanics (PYFM) concept. A maximum in the non-essential work of fracture was observed at 0.5 wt.% MWNT demonstrating enhanced toughness compared to pure PP, followed by a sharp decline as the MWNT content was increased to 1.5 wt.% reveals a ductile-to-semi-ductile transition. Studies on the kinetics of crack propagation aspects have revealed a qualitative picture of the nature of such a transition in the fracture modes

Emissions of volatile hydrocarbons (VOC) during drying of sawdust; Utslaepp av laettflyktiga kolvaeten vid torkning av biobraenslen

Energy Technology Data Exchange (ETDEWEB)

Granstroem, Karin

2001-08-01

In the project 'Emissions of volatile hydrocarbons (VOC) during drying of sawdust' the identity, amount and composition of monoterpenes found in the drying medium of a fluidized bed drier drying sawdust from Norwegian spruce and Scotch pine has been determined. The energy efficiency of the drier has also been measured. The aim of this project was to reduce both emissions and energy required for drying, to minimize environmental and health hazards, and make drying more competitive. This would help our primary target group - small scale saw mills - to make use of the sawdust produced as a by- product by making pellets and briquettes. If the VOC remains in the sawdust its energy content will improve and therefore also its value as a fuel. The sawdust was dried to different moisture levels in a spouted bed drier at atmospheric pressure, using either recirculating or not recirculating drying medium with temperatures 140, 170 or 200 deg C. The emissions of VOC were measured using a flame ionization detector (FID) and the nature of the emissions analyzed with a gas chromatograph with mass spectrometric detector (GC-MS). The GC-MS data is reported as emitted substance per oven dry weight (odw). Experiments show that terpenes do not leave the sawdust in great amounts until it is dried to a moisture content (water/total weight) below 10%. When sawdust is dried to a predetermined moisture level, the terpene emissions increase when warmer incoming drying medium is used. The monoterpenes found in greatest amount are a-pinene, b-pinene, 3-carene, limonene and myrcene. y-terpinene was detected in emissions from pine but not from spruce. The relative amounts of different monoterpenes did not vary significantly with post-drying moisture content, but drying medium of higher temperature caused an increase in the relative amount of less volatile monoterpenes. The FID data is reported as concentration of VOC in the drying medium, and as weight VOC per odw. The concentration

Photo-oxidative degradation of TiO{sub 2}/polypropylene films

Energy Technology Data Exchange (ETDEWEB)

García-Montelongo, X.L. [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Martínez-de la Cruz, A., E-mail: azael70@yahoo.com.mx [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Vázquez-Rodríguez, S. [Facultad de Ingeniería Mecánica y Eléctrica, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico); Torres-Martínez, Leticia M. [Facultad de Ingeniería Civil, Universidad Autónoma de Nuevo León, Ciudad Universitaria, C.P. 66451 San Nicolás de los Garza, N.L. (Mexico)

2014-03-01

Graphical abstract: - Highlights: • Photo-oxidative degradation of polypropylene is accelerated by TiO{sub 2} incorporation. • Weight loss, FTIR, SEM and GPC shown high degree of degradation of polypropylene. • A mechanism of the photo-degradation of polypropylene by TiO{sub 2} is proposed. - Abstract: Photo-oxidative degradation of polypropylene films with TiO{sub 2} nanoparticles incorporated was studied in a chamber of weathering with Xenon lamps as irradiation source. TiO{sub 2} powder with crystalline structure of anatase was synthesized by thermal treatments at 400 and 500 °C starting from a precursor material obtained by sol–gel method. Composites of TiO{sub 2}/polypropylene were prepared with 0.1, 0.5 and 1.0 wt% of TiO{sub 2}. The mixture of components was performed using a twin screw extruder, the resulting material was pelletized by mechanical fragmenting and then hot-pressed in order to form polypropylene films with TiO{sub 2} dispersed homogeneously. Photo-oxidative degradation process was followed by visual inspection, weight loss of films, scanning electron microscopy (SEM), infrared spectroscopy with Fourier transformed (FTIR), and gel permeation chromatography (GPC)

A study on flexural and water absorption of surface modified rice husk flour/E-glass/polypropylene hybrid composite

Science.gov (United States)

Rassiah, K.; Sin, T. W.; Ismail, M. Z.

2016-10-01

This work is to study the effects of rice husk (RH)/E-Glass (EG)/polypropylene (PP) hybrid composites in terms of flexural and water absorption properties. The tests conducted are the flexural test and also the water absorption test using two types of water: distilled and sea water. The hybrid composites are prepared with various ratios of fibre weight fractions and the rice husk is treated using 2% Sodium Hydroxide (NaOH) to improve interaction and adhesion between the non-polar matrix and the polar lignocellulosic fibres. It was found that the content of rice husk/E-Glass fillers affected the structural integrity and flexural properties of hybrid composites. In addition, a higher ratio of rice husk contributes to higher water absorption in the hybrid composites.

Highly Conductive 3D Segregated Graphene Architecture in Polypropylene Composite with Efficient EMI Shielding

Directory of Open Access Journals (Sweden)

Fakhr E. Alam

2017-12-01

Full Text Available The extensive use of electronic equipment in modern life causes potential electromagnetic pollution harmful to human health. Therefore, it is of great significance to enhance the electrical conductivity of polymers, which are widely used in electronic components, to screen out electromagnetic waves. The fabrication of graphene/polymer composites has attracted much attention in recent years due to the excellent electrical properties of graphene. However, the uniform distribution of graphene nanoplatelets (GNPs in a non-polar polymer matrix like polypropylene (PP still remains a challenge, resulting in the limited improvement of electrical conductivity of PP-based composites achieved to date. Here, we propose a single-step approach to prepare GNPs/PP composites embedded with a segregated architecture of GNPs by coating PP particles with GNPs, followed by hot-pressing. As a result, the electrical conductivity of 10 wt % GNPs-loaded composites reaches 10.86 S·cm−1, which is ≈7 times higher than that of the composites made by the melt-blending process. Accordingly, a high electromagnetic interference shielding effectiveness (EMI SE of 19.3 dB can be achieved. Our method is green, low-cost, and scalable to develop 3D GNPs architecture in a polymer matrix, providing a versatile composite material suitable for use in electronics, aerospace, and automotive industries.

Saccharification of delignified sawdust from 20 different trees in the ...

African Journals Online (AJOL)

USER

volumes of almost 104 000 m3 sawdust (Aina, 2006) are incinerated, burnt or accumulated on the banks of the. Lagos Lagoon where the ocean tide and waves washes these wood residuals into the lagoon causing water pollution (Akparta and Ekundayo, 1983). Sawdust clogs water ways and it enhances the germination of ...

Influence of Interleaved Films on the Mechanical Properties of Carbon Fiber Fabric/Polypropylene Thermoplastic Composites

Directory of Open Access Journals (Sweden)

Jong Won Kim

2016-05-01

Full Text Available A laminated composite was produced using a thermoplastic prepreg by inserting an interleaved film with the same type of matrix as the prepreg during the lay-up process to improve the low interlaminar properties, which is a known weakness of laminated composites. Carbon fiber fabric (CFF and polypropylene (PP were used to manufacture the thermoplastic prepregs. Eight prepregs were used to produce the laminated composites. Interleaved films with different thicknesses were inserted into each prepreg. The physical properties of the composite, such as thickness, density, fiber volume fraction (Vf, and void content (Vc, were examined. The tensile strength, flexural strength, interlaminar shear strength (ILSS, impact property, and scanning electron microscopy (SEM were used to characterize the mechanical properties. Compared to the composite without any inserted interleaved film, as the thickness of the inserted interleaved resin film was increased, Vc decreased by 51.45%. At the same time, however, the tensile strength decreased by 8.75%. Flexural strength increased by 3.79% and flexural modulus decreased by 15.02%. Interlaminar shear strength increased by 11.05% and impact strength increased by 15.38%. Fracture toughness of the laminated composite was improved due to insertion of interleaved film.

Influence of Interleaved Films on the Mechanical Properties of Carbon Fiber Fabric/Polypropylene Thermoplastic Composites.

Science.gov (United States)

Kim, Jong Won; Lee, Joon Seok

2016-05-06

A laminated composite was produced using a thermoplastic prepreg by inserting an interleaved film with the same type of matrix as the prepreg during the lay-up process to improve the low interlaminar properties, which is a known weakness of laminated composites. Carbon fiber fabric (CFF) and polypropylene (PP) were used to manufacture the thermoplastic prepregs. Eight prepregs were used to produce the laminated composites. Interleaved films with different thicknesses were inserted into each prepreg. The physical properties of the composite, such as thickness, density, fiber volume fraction ( V f ), and void content ( V c ), were examined. The tensile strength, flexural strength, interlaminar shear strength (ILSS), impact property, and scanning electron microscopy (SEM) were used to characterize the mechanical properties. Compared to the composite without any inserted interleaved film, as the thickness of the inserted interleaved resin film was increased, V c decreased by 51.45%. At the same time, however, the tensile strength decreased by 8.75%. Flexural strength increased by 3.79% and flexural modulus decreased by 15.02%. Interlaminar shear strength increased by 11.05% and impact strength increased by 15.38%. Fracture toughness of the laminated composite was improved due to insertion of interleaved film.

Thermal and mechanical properties of polypropylene/titanium dioxide nanocomposite fibers

International Nuclear Information System (INIS)

Esthappan, Saisy Kudilil; Kuttappan, Suma Kumbamala; Joseph, Rani

2012-01-01

Highlights: ► Wet synthesis method was used for the synthesis of TiO 2 nano particles. ► Mechanical properties of polypropylene fibers were increased by the addition of TiO 2 nanoparticles. ► Thermal stability of polypropylene fiber was improved significantly by the addition of TiO 2 nano particles. ► TiO 2 nanoparticles dispersed well in polypropylene fibers. -- Abstract: Titanium dioxide nanoparticles were prepared by wet synthesis method and characterized by transmission electron microscopy and X-ray diffraction studies. The nanotitanium dioxide then used to prepare polypropylene/titanium dioxide composites by melt mixing method. It was then made into fibers by melt spinning and subsequent drawing. Mechanical properties of the fibers were studied using Favimat tensile testing machine with a load cell of 1200 cN capacity. Thermal behavior of the fibers was studied using differential scanning calorimetry and thermogravimetric analysis. Scanning electron microscope studies were used to investigate the titanium dioxide surface morphology and crosssection of the fiber. Mechanical properties of the polypropylene fiber was improved by the addition of titanium dioxide nanoparticles. Incorporation of nanoparticles improves the thermal stability of polypropylene. Differential scanning calorimetric studies revealed an improvement in crystallinity was observed by the addition of titanium dioxide nanoparticles.

Alumina/Phenolphthalein Polyetherketone Ceramic Composite Polypropylene Separator Film for Lithium Ion Power Batteries

International Nuclear Information System (INIS)

Wang, Jing; Hu, Zhiyu; Yin, Xiunan; Li, Yunchao; Huo, Hong; Zhou, Jianjun; Li, Lin

2015-01-01

Highlights: • PEK-C (T g : ∼230 °C) was used as binder to prepare ceramic coated composite PP separator. • The composite PP separator was stable and showed low thermal shrinkage in the electrolyte solvent. • The composite PP separator was helpful for high current density discharge. • The composite PP separator improved the safety performance of the coin cells. - Abstract: One way to obtain the lithium ion power battery with better safety performance was to increase the thermal shrinkage resistance of the separator at higher temperature. Phenolphthalein polyetherketone (PEK-C) is a polymer that can withstand high temperature to about 230 °C. Here, we developed a new Al 2 O 3 coated composite polypropylene (PP) separator with PEK-C as binder. The coating layer was formed on the surface of the PP separator and both ceramic particles and binder did not infiltrated into the separator along the thickness direction. The composite separator with 4 μm coating layer provided balanced permeability and thermal shrinkage properties. The composite separator was stable at the electrochemical window for lithium ion battery. The coin cells with composite separator showed better charge/discharge performance than that of the cells with the PP separator. It seemed that the composite separator was helpful for high current density discharge. Also, the battery safety performance test had verified that the Al 2 O 3 coated composite separator with PEK-C as binder had truly improved the safety performance of the coin cells. So, the newly developed Al 2 O 3 coated composite PP separator was a promising safety product for lithium ion power batteries with high energy density

Study of microcellular injection-molded polypropylene/waste ground rubber tire powder blend

International Nuclear Information System (INIS)

Xin, Zhen Xiang; Zhang, Zhen Xiu; Pal, Kaushik; Byeon, Jong Ung; Lee, Sung Hyo; Kim, Jin Kuk

2010-01-01

Microcellular polypropylene/waste ground rubber tire powder blend processing was performed on an injection-molding machine with a chemical foaming agent. The molded samples produced based on the design of experiments (DOE) matrices were subjected to tensile testing and scanning electron microscope (SEM) analyses. Molding conditions and waste ground rubber tire (WGRT) powder have been found to have profound effects on the cell structures and mechanical properties of polypropylene (PP) and waste ground rubber tire powder composite samples. The result shows that microcellular PP/WGRT blend samples exhibit smaller cell size and higher cell density compare with polypropylene resin. Among the molding parameters studied, chemical foaming agent weight percentage has the most significant effect on cell size, cell density, and tensile strength. The results also suggest that tensile strength of microcellular PP/WGRT composites is sensitive to weight reduction, and skin thickness.

Effects of gamma irradiation on polypropylene, polypropylene + high density polyethylene and polypropylene + high density polyethylene + wood flour

Energy Technology Data Exchange (ETDEWEB)

Reyes, J.; Albano, C.; Davidson, E.; Poleo, R. [Universidad Central de Venezuela, Caracas (Venezuela). Escuela de Quimica; Gonzalez, J.; Ichazo, M. [Universidad Simon Bolivar, Dept. de Mecanica, Caracas (Venezuela); Chipara, M. [Research Institute for Electrotechnics, Bucharest (Romania)

2001-04-01

The effect of the gamma-irradiation on the mechanical properties of the composites, Polypropylene (PP), PP+high density Polyethylene (HDPE), PP+ HDPE+wood flour, where HDPE is virgin and recycled, was studied. This paper discusses the behavior of the composites after exposure to various doses of gamma irradiation (1-7 MRads) in the presence of oxygen. The dependence of mechanical properties on the integral dose for a constant dose rate of 0.48 MRads/h confirms the influence of the irradiation. Strong effects on the elongation at break and break strength is noticed. The mathematical analysis suggests for the PP+r-HDPE a bimolecular process of the elongation at break. On the order hand, for the PP+HDPE a complex process is represented for a three exponential equation. (orig.)

Effects of gamma irradiation on polypropylene, polypropylene + high density polyethylene and polypropylene + high density polyethylene + wood flour

International Nuclear Information System (INIS)

Reyes, J.; Albano, C.; Davidson, E.; Poleo, R.; Chipara, M.

2001-01-01

The effect of the gamma-irradiation on the mechanical properties of the composites, Polypropylene (PP), PP+high density Polyethylene (HDPE), PP+ HDPE+wood flour, where HDPE is virgin and recycled, was studied. This paper discusses the behavior of the composites after exposure to various doses of gamma irradiation (1-7 MRads) in the presence of oxygen. The dependence of mechanical properties on the integral dose for a constant dose rate of 0.48 MRads/h confirms the influence of the irradiation. Strong effects on the elongation at break and break strength is noticed. The mathematical analysis suggests for the PP+r-HDPE a bimolecular process of the elongation at break. On the order hand, for the PP+HDPE a complex process is represented for a three exponential equation. (orig.)

Polypropylene compositional evolution under 3.5 MeV He{sup +} ion irradiation

Energy Technology Data Exchange (ETDEWEB)

Abdesselam, M., E-mail: abdesselam_m@yahoo.fr [Faculte de Physique, USTHB, BP32, El Alia, 16111 BEZ (Algeria); Muller, D. [InESS, UMR7163, 23 rue du Loess, BP20, F-67037 Strasbourg Cedex 02 (France); Djebara, M.; Chami, A.C. [Faculte de Physique, USTHB, BP32, El Alia, 16111 BEZ (Algeria); Montgomery, P. [InESS, UMR7163, 23 rue du Loess, BP20, F-67037 Strasbourg Cedex 02 (France)

2012-05-01

A helium beam at 3.5 MeV was used to induce damage in thin polypropylene film of 5.1 {mu}m in thickness. The fluence ranges from 2 Multiplication-Sign 10{sup 12} to 3.5 Multiplication-Sign 10{sup 15} cm{sup -2}. The evolution of the atomic composition (C and H) as a function of the fluence was investigated in situ by forward elastic scattering (C({alpha}, {alpha})C) and hydrogen elastic recoil detection (H({alpha}, H){alpha}), respectively. The helium beam was used at the same time for irradiation and analysis. In respect to the high sensitivity of the polypropylene to radiation damage, the beam current was kept at very low intensity of 0.5 nA. The mass loss becomes significant above a fluence of {approx}5 Multiplication-Sign 10{sup 13} He{sup +} cm{sup -2}. The carbon depletion levels off at a fluence of {approx}5 Multiplication-Sign 10{sup 14} He{sup +} cm{sup -2} approximately while hydrogen loss continues to be present along the whole of the studied fluence range. The final carbon and hydrogen losses, at the highest fluence, are around 17% and 48% of their initial contents, respectively. Satisfactory fits to the release curves have been obtained in the framework of the bulk molecular recombination model (BMR). The deduced hydrogen and carbon release cross sections are 7.8 and 65.2 Multiplication-Sign 10{sup -16} cm{sup 2}, respectively. A comparison with our previous measurements of polyethylene terephthalate (PET) film irradiated with 3.7 MeV He{sup +} beam is made.

Influence of nonmetals recycled from waste printed circuit boards on flexural properties and fracture behavior of polypropylene composites

International Nuclear Information System (INIS)

Zheng Yanhong; Shen Zhigang; Cai Chujiang; Ma Shulin; Xing Yushan

2009-01-01

Flexural strength and flexural modulus of the composites can be successfully improved by filling nonmetals recycled from waste printed circuit boards (PCBs) into polypropylene (PP). By using scanning electron microscopy (SEM), the influence of nonmetals on fracture behavior of PP composites is investigated by in situ flexural test. Observation results show that the particles can effectively lead to mass micro cracks instead of the breaking crack. The process of the crack initiation, propagation and fiber breakage dissipate a great amount of energy. As a result, the flexural properties of the composites can be reinforced significantly. Results of the in situ SEM observation and analysis to the dynamic flexural process supply effective test evidence for the reinforcing mechanism of the nonmetals/PP composites on the basis of the energy dissipation theory

Modification of polypropylene with radiation-treated wood fiber

International Nuclear Information System (INIS)

Czvikovszky, T.; Tapolcai, I.

1983-01-01

The dispersed wood material is used not only as filler for thermosetting polymers but also as a new type of fibrous additive for thermoplastics e.g. polypropylene. Benefit of this additive (filler or reinforcement) is determined by the coupling between the wood and the synthetic resin. Fibrous, dispersed wood material was preirradiated in air, treated with vinyl monomer containing polyester resin and then mixed in polypropylene. Processability of such thermoplastic blends as well as reactivity of the mixed components were followed by measuring energy, absorbed during the kneading of the melt. The vinylmonomer vinylmonomer - polyester additive, activated at higher temperature by the radiation-formed peroxy groups on the wood fiber, results in good processability of the thermoplastic blend, and gives interesting mechanical properties. Calandering, extrusion, pressmoulding and mechanical testing demonstrated good workability and practical value of the polypropylene composite material containing radiation-treated wood fiber. (author)

Preparation of immobilized growing cells and enzymatic hydrolysis of sawdust

International Nuclear Information System (INIS)

Kumakura, M.; Kaetsu, I.

1984-01-01

Trichoderma reesei cells were immobilized by radiation polymerization using porous materials such as non-woven material and sawdust, and the enzymatic hydrolysis of sawdust with the enzyme solution from the immobilized growing cells was studied. The filter paper activity, which shows the magnitude of cellulase production in the immobilized cells, was comparable with that in the intact cells. The filter paper activity was affected by addition concentration of monomer and porous materials. The cells in the immobilized cells grew to be adhered on the surface of the fibrous polymers. Sawdust, which was pretreated by irradiation technique, was effectively hydrolyzed with the enzyme solution resulting from the culture of the immobilized cells, in which the glucose yield increased increasing the culture time of the immobilized cells. (author)

Antimicrobial Carvacrol-Containing Polypropylene Films: Composition, Structure and Function

Directory of Open Access Journals (Sweden)

Max Krepker

2018-01-01

Full Text Available Significant research has been directed toward the incorporation of bioactive plant extracts or essential oils (EOs into polymers to endow the latter with antimicrobial functionality. EOs offer a unique combination of having broad antimicrobial activity from a natural source, generally recognized as safe (GRAS recognition in the US, and a volatile nature. However, their volatility also presents a major challenge in their incorporation into polymers by conventional high-temperature-processing techniques. Herein, antimicrobial polypropylene (PP cast films were produced by incorporating carvacrol (a model EO or carvacrol, loaded into halloysite nanotubes (HNTs, via melt compounding. We studied the composition-structure-property relationships in these systems, focusing on the effect of carvacrol on the composition of the films, the PP crystalline phase and its morphology and the films’ mechanical and antimicrobial properties. For the first time, molecular dynamics simulations were applied to reveal the complex interactions between the components of these carvacrol-containing systems. We show that strong molecular interactions between PP and carvacrol minimize the loss of this highly-volatile EO during high-temperature polymer processing, enabling semi-industrial scale production. The resulting films exhibit outstanding antimicrobial properties against model microorganisms (Escherichia coli and Alternaria alternata. The PP/(HNTs-carvacrol nanocomposite films, containing the carvacrol-loaded HNTs, display a higher level of crystalline order, superior mechanical properties and prolonged release of carvacrol, in comparison to PP/carvacrol blends. These properties are ascribed to the role of HNTs in these nanocomposites and their effect on the PP matrix and retained carvacrol content.

Composting of organically amended/treated hardwood and softwood sawdust

International Nuclear Information System (INIS)

Takyi-Lartey, Rita

2015-07-01

Sawdust is a major waste produced by the wood industry. Adding value to sawdust through composting is one of the surest means by which environmental pollution could be minimized. About 500 kg of softwood and hardwood sawdust were separately mixed with mucuna leaves and kitchen waste in the ratio of 3:1:1 on weight basis and heaped using effluent from abattoir to develop composts. Objectives of the study were to monitor changes in the physico-chemical properties, NH4"+ ‒ N, NO3"‒ ‒ N, C:N ratio, minerals N, K, P, microbial load and toxic elements in the composts during a 12 week period. Germination test was also done to evaluate the stability and maturity of the composts developed. Degradation of softwood sawdust compost (SSC) was better in the mesophilic phase while that of hardwood sawdust compost (HSC) occurred in the thermophilic phase. Thus, significantly higher amount of the organic material in SSC was decomposed during the period as compared to HSC. Also, greater percentage of the nitrogen in the initial material of SSC was converted into plant-available inorganic nitrogen (NH4"+ and NO3"‒) than was achieved in HSC. Hence, most of the mineral nitrogen in HSC that was converted was lost, probably in the thermophilic phase. On the contrary, the amount of organic nitrogen contained in the finished composts of both SSC and HSC were adequately good for application to the soil. Additionally, concentrations of pathogenic microorganisms in SSC and HSC products were within acceptable limits in terms of toxicity on growing plants. The softwood sawdust compost was relatively more stable as compared to HSC under the experimental conditions. Concentrations of heavy metals in both SSC and HSC were also within acceptable limits that would cause no toxicity to plants. Also, moisture contents in both SSC and HSC were within the good range (40 - 60%) required for a good compost. Thus both SSC and HSC produced were of good quality. Further research targeting specific

Mechanical Properties of Nanofilled Polypropylene Composites

Directory of Open Access Journals (Sweden)

Cristina-Elisabeta PELIN

2015-06-01

Full Text Available The paper presents a study concerning mechanical performance of thermoplastic nanocomposites based on isotactic polypropylene matrix, nanofilled with montmorillonite modified with quaternary ammonium salt and carboxyl functionalized carbon nanotubes, respectively, added in the same concentration relative to the matrix. The nanofilled and single polymer materials were obtained by simple melt compounding through extrusion process followed by injection molding into specific shape specimens for mechanical testing of the samples. Mechanical properties were evaluated by tensile and 3 point bending tests. In terms of modulus of elasticity, the results showed overall positive effects concerning the effect of nanofiller addition to the thermoplastic polymer. The fracture cross section of the tested specimens was characterized by FT-IR spectroscopy and SEM microscopy.

The Use Of Sawdust As An Alternative Source Of Energy For ...

African Journals Online (AJOL)

This paper presents the reports on the utilization of sawdust stove as a way of ameliorating the effect of perennial fuel crisis in Nigeria on domestic cooking and a means of reducing deforestation and subsequent desertification. The performance of the sawdust stove, in terms of cooking duration and specific fuel consumption ...

Comparison of the mechanical properties between carbon nanotube and nanocrystalline cellulose polypropylene based nano-composites

International Nuclear Information System (INIS)

Huang, Jun; Rodrigue, Denis

2015-01-01

Highlights: • SWCNT and NCC can effectively improve the mechanical properties of nano-composites. • SWCNT is more effective than NCC to increase modulus and strength. • Longer NCC is more effective to improve the mechanical properties of nano-composites. • It is more economic to use NCC than SWCNT to improve mechanical properties. - Abstract: Using beam and tetrahedron elements to simulate nanocrystalline cellulose (NCC), single wall carbon nanotube (SWCNT) and polypropylene (PP), finite element method (FEM) is used to predict the mechanical properties of nano-composites. The bending, shear and torsion behaviors of nano-composites are especially investigated due to the limited amount of information in the present literature. First, mixed method (MM) and FEM are used to compare the bending stiffness of NCC/PP and SWCNT/PP composites. Second, based on mechanics of materials, the shear moduli of both types of nano-composites are obtained. Finally, fixing the number of fibers and for different volume contents, four NCC lengths are used to determine the mechanical properties of the composites. The bending and shearing performances are also compared between NCC and SWCNT based composites. In all cases, the elastic–plastic analyses are carried out and the stress or strain distributions for specific regions are also investigated. From all the results obtained, an economic analysis shows that NCC is more interesting than SWCNT to reinforce PP

Evaluation of elevated temperature influence on mechanical properties of a commercial unrefined bagasse fiber-polypropylene composite

Directory of Open Access Journals (Sweden)

Foroogh Dastoorian

2014-11-01

Full Text Available An experimental investigation was conducted to evaluate the effect of elevated temperatures, ranging from room temperature to 80oC, on mechanical characteristics of a commercial bagasse fiber/polypropylene composite. The test results were used to determine the temperature dependencies of the mechanical properties of the studied composite material at temperatures up to 80°C in order to develop temperature adjustment factors for the use in structural applications. The results have shown that as temperature increases, the material become more ductile due to increased plastic deformation gets lower stiffness and fails at higher strains. The resulted adjustment factors were different for each loading mode and the results also have indicated that the influence of elevated temperatures on values of modulus was higher than that on strengths.

Two-fold sustainability – Adobe with sawdust as partial sand replacement

Science.gov (United States)

Jokhio, Gul A.; Syed Mohsin, Sharifah M.; Gul, Yasmeen

2018-04-01

Adobe is a material that is economic, environment friendly, and provides better indoor air quality. The material required for the preparation of adobe include clay, sand, and sometimes straw or other organic materials. These materials do not require industrial processing or transportation, however, sand mining has been recently posing a threat to the environment. Therefore, to enhance the existing sustainability of adobe, sand can be partially or fully replaced by other waste materials. This approach will not only solve the problem of excessive sand mining, it will also address the issue of waste management. Sawdust is one such waste material that can be used to partially replace sand in Adobe. This paper presents the results of compressive and flexural test carried out on Adobe samples with partial sand replacement by sawdust. The results show that about 4% sand replacement by volume produces higher compressive strength, whereas the flexural strength reduces with the use of sawdust. However, since flexural strength is not a critical property for adobe, it is concluded that replacing sand with sawdust by about 4% of volume will be beneficial.

Performance and Characteristics of a Cyclone Gasifier for Gasification of Sawdust

Science.gov (United States)

Azman Miskam, Muhamad; Zainal, Z. A.; Idroas, M. Y.

The performance and characteristics of a cyclone gasifier for gasification of sawdust has been studied and evaluated. The system applied a technique to gasify sawdust through the concept of cyclonic motion driven by air injected at atmospheric pressure. This study covers the results obtained for gasification of ground sawdust from local furniture industries with size distribution ranging from 0.25 to 1 mm. It was found that the typical wall temperature for initiating stable gasification process was about 400°C. The heating value of producer gas was about 3.9 MJ m-3 that is sufficient for stable combustion in a dual-fuel engine generator. The highest thermal output from the cyclone gasifier was 57.35 kWT. The highest value of mass conversion efficiency and enthalpy balance were 60 and 98.7%, respectively. The highest efficiency of the cyclone gasifier obtained was 73.4% and this compares well with other researchers. The study has identified the optimum operational condition for gasifying sawdust in a cyclone gasifier and made conclusions as to how the steady gasification process can be achieved.

Cleanup Verification Package for the 118-F-5 PNL Sawdust Pit

International Nuclear Information System (INIS)

Habel, L.D.

2008-01-01

This cleanup verification package documents completion of remedial action, sampling activities, and compliance with cleanup criteria for the 118-F-5 Burial Ground, the PNL (Pacific Northwest Laboratory) Sawdust Pit. The 118-F-5 Burial Ground was an unlined trench that received radioactive sawdust from the floors of animal pens in the 100-F Experimental Animal Farm

A Combined Self-Consistent Method to Estimate the Effective Properties of Polypropylene/Calcium Carbonate Composites

Directory of Open Access Journals (Sweden)

Zhongqiang Xiong

2018-01-01

Full Text Available In this work, trying to avoid difficulty of application due to the irregular filler shapes in experiments, self-consistent and differential self-consistent methods were combined to obtain a decoupled equation. The combined method suggests a tenor γ independent of filler-contents being an important connection between high and low filler-contents. On one hand, the constant parameter can be calculated by Eshelby’s inclusion theory or the Mori–Tanaka method to predict effective properties of composites coinciding with its hypothesis. On the other hand, the parameter can be calculated with several experimental results to estimate the effective properties of prepared composites of other different contents. In addition, an evaluation index σ f ′ of the interactional strength between matrix and fillers is proposed based on experiments. In experiments, a hyper-dispersant was synthesized to prepare polypropylene/calcium carbonate (PP/CaCO3 composites up to 70 wt % of filler-content with dispersion, whose dosage was only 5 wt % of the CaCO3 contents. Based on several verifications, it is hoped that the combined self-consistent method is valid for other two-phase composites in experiments with the same application progress as in this work.

Ecotoxicity and fungal deterioration of recycled polypropylene/wood composites: effect of wood content and coupling.

Science.gov (United States)

Sudár, András; López, María J; Keledi, Gergely; Vargas-García, M Carmen; Suárez-Estrella, Francisca; Moreno, Joaquín; Burgstaller, Christoph; Pukánszky, Béla

2013-09-01

Recycled polypropylene (rPP) was recovered from an industrial shredder and composites were prepared with a relatively wide range of wood content and with two coupling agents, a maleated PP (MAPP) and a maleated ethylene-propylene-diene elastomer (MAEPDM). The mechanical properties of the composites showed that the coupling agents change structure only slightly, but interfacial adhesion quite drastically. The durability of the materials was determined by exposing them to a range of fungi and, ecotoxicity was studied on the aquatic organism Vibrio fischeri. The composites generally exhibit low acute toxicity, with values below the levels considered to have direct ecotoxic effect on aquatic ecosystems (deterioration proved that wood facilitates fungal colonization. Fungi caused slight mass loss (below 3%) but it was not correlated with substantial deterioration in material properties. MAPP seems to be beneficial in the retention of mechanical properties during fungal attack. rPP/wood composites can be considered non-ecotoxic and quite durable, but the influence of wood content on resistance to fungal attack must be taken into account for materials intended for applications requiring long-term outdoor exposure. Copyright © 2013 Elsevier Ltd. All rights reserved.

Comparative studies of Titanium Dioxide and Zinc Oxide as a potential filler in Polypropylene reinforced rice husk composite

Science.gov (United States)

Awang, M.; Mohd, W. R. Wan

2018-04-01

Arising global environmental issues have triggered the search of new products and processes that are compatible with the environment while maintaining novel properties of materials. In this work, green composites containing rice husk (RH), polypropylene (PP), and incorporated with two different fillers namely titanium dioxide (TiO2) and zinc oxide (ZnO) were prepared using an internal mixer and were injected into desired specimen by using an injection molding method. Mechanical properties of the composite were studied using Instron universal testing machine with load cell of 30kN capacity. Morphological of tensile fractured surface of composites was observed using scanning electron microscopy (SEM). The results show that the composites with the addition of TiO2 gave an excellent mechanical properties than the composites filled with ZnO. Furthermore, morphological image of PP/RH/TiO2 also shows a good interaction occurred between polymer matrix and RH particles as compared to that of PP/RH/ZnO.

EFFECT OF SEA WATER ON THE STRENGTH OF POROUS CONCRETE CONTAINING PORTLAND COMPOSITE CEMENT AND MICROFILAMENT POLYPROPYLENE FIBER

OpenAIRE

TJARONGE, M.W

2011-01-01

The aim of this research is to study the influence of sea water on the strength of porous concrete containing Portland Composite cement and micro monofilament polypropylene fibre. The specimens of porous concrete were immersed in the sea water up to 28 days. The compressive strength test and flexural strength test were carried out at 3, 7 and 28 days in order to investigate the strength development. The test result indicated that the strength of porous concrete can develop in t...

Genome Regions Associated with Functional Performance of Soybean Stem Fibers in Polypropylene Thermoplastic Composites.

Directory of Open Access Journals (Sweden)

Yarmilla Reinprecht

Full Text Available Plant fibers can be used to produce composite materials for automobile parts, thus reducing plastic used in their manufacture, overall vehicle weight and fuel consumption when they replace mineral fillers and glass fibers. Soybean stem residues are, potentially, significant sources of inexpensive, renewable and biodegradable natural fibers, but are not curretly used for biocomposite production due to the functional properties of their fibers in composites being unknown. The current study was initiated to investigate the effects of plant genotype on the performance characteristics of soybean stem fibers when incorporated into a polypropylene (PP matrix using a selective phenotyping approach. Fibers from 50 lines of a recombinant inbred line population (169 RILs grown in different environments were incorporated into PP at 20% (wt/wt by extrusion. Test samples were injection molded and characterized for their mechanical properties. The performance of stem fibers in the composites was significantly affected by genotype and environment. Fibers from different genotypes had significantly different chemical compositions, thus composites prepared with these fibers displayed different physical properties. This study demonstrates that thermoplastic composites with soybean stem-derived fibers have mechanical properties that are equivalent or better than wheat straw fiber composites currently being used for manufacturing interior automotive parts. The addition of soybean stem residues improved flexural, tensile and impact properties of the composites. Furthermore, by linkage and in silico mapping we identified genomic regions to which quantitative trait loci (QTL for compositional and functional properties of soybean stem fibers in thermoplastic composites, as well as genes for cell wall synthesis, were co-localized. These results may lead to the development of high value uses for soybean stem residue.

Lignocellulosic micro/nanofibers from wood sawdust applied to recycled fibers for the production of paper bags.

Science.gov (United States)

Tarrés, Quim; Pellicer, Neus; Balea, Ana; Merayo, Noemi; Negro, Carlos; Blanco, Angeles; Delgado-Aguilar, Marc; Mutjé, Pere

2017-12-01

In the present work, lignocellulosic micro/nanofibers (LCMNF) were produced from pine sawdust. For that, pine sawdust was submitted to alkali treatment and subsequent bleaching stages, tailoring its chemical composition with the purpose of obtaining effective LCMNF. The obtained LCMNF were characterized and incorporated to recycled cardboard boxes with the purpose of producing recycled paper. The obtained results showed that it was possible to obtain LCMNF with the same reinforcing potential than those cellulose nanofibers (CNF) prepared by oxidative or other chemical methods In fact, the obtained papers increased the breaking length of recycled cardboard from 3338m to 5347m, being a value significantly higher than the requirements to produce paper bags. Overall, the studied strategies could allow a significant reduction of paper basis weight, with the consequent material saving and, thus, contribution to the environment. Copyright © 2017 Elsevier B.V. All rights reserved.

Effect of surface modified kaolin on properties of polypropylene grafted maleic anhydride

Science.gov (United States)

Yang, Ni; Zhang, Zuo-Cai; Ma, Ning; Liu, Huan-Li; Zhan, Xue-Qing; Li, Bing; Gao, Wei; Tsai, Fang-Chang; Jiang, Tao; Chang, Chang-Jung; Chiang, Tai-Chin; Shi, Dean

To achieve reinforcement of mechanical and thermal performances of polypropylene (PP) product, this work aimed at fabrication of surface modified kaolin (M-kaolin) filled polypropylene grafted maleic anhydride (PP-g-MAH) composites with varying contents of fillers and investigation of their mechanical and thermal properties. And the prepared PP-g-MAH/M-kaolin composites were characterized by means of Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and thermogravimetric analysis (TGA). Fracture analysis by SEM showed M-kaolin particles were well dispersed in the PP-g-MAH matrix. Mechanical behaviors were determined by tensile strength, tensile strain at break and impact strength analysis. Impact strength of PP-g-MAH/2 wt% M-kaolin composites was improved up to 30% comparing with unfilled composites. Thermostability had been found enhanced when M-kaolin added. The results revealed PP-g-MAH/M-kaolin composites showed the optimal thermal and mechanical properties when 2 wt% of M-kaolin was added.

Detection of changes in fuel quality during storage of sawdust from pine and spruce by using gas chromatography - Mass spectrometry (GC-MS) and VIS-NIR-spectroscopy

Energy Technology Data Exchange (ETDEWEB)

Arshadi, Mehrdad; Nilsson, David; Geladi, Paul (Unit of Biomass Technology and Chemistry, Swedish Univ. of Agricultural Sciences, SE-904 03 Umeaa (Sweden)). e-mail: mehrdad.arshadi@btk.slu.se

2008-10-15

Fuel pellets made of sawdust represent a renewable energy source for heat production. The raw material comes from sawmills and sawdust is used in the pellet mills and for reasons of logistics there is a need for storage of large quantities of the raw material. Long-term storage induces changes in the sawdust and therefore processing parameters for pellets production have to be adapted. This makes knowledge of storage time or maturity necessary. Two examples of experimental studies are presented: An industrial storage of pine and spruce sawdust was carried out over a period of 16 weeks in order to monitor the changes in the quality of sawdust during storage. Samples were taken out every week and all samples were analysed by VIS-NIR spectroscopy while some samples were analysed by GC-MS for their composition of fatty- and resin acids. The resulting data were subjected to multivariate data analysis. GC-MS data showed the difference between pine and spruce sawdust and the influence of maturity. This maturity effect could be associated with the decrease in fatty- and resin acids due to auto oxidative reactions. Multivariate analysis of the VIS-NIR data showed a major effect due to maturity associated with a colour change and also weaker effects of fatty- and resin acids differences. PLS regression was used to predict the storage time with RMSEP values between 10 and 15 days. However, since weather conditions, precipitation and seasonal variation have high influence on the speed of maturing of sawdust it will be necessary to continuously determine the degree of maturity. A second similar study is used as a complementary way of corroborating the results of the first one

Mechanical and thermal properties of polypropylene (PP) composites filled with modified shell waste

Energy Technology Data Exchange (ETDEWEB)

Yao, Z.T., E-mail: sxyzt@126.com [College of Materials Science and Environmental Engineering, Hangzhou Dianzi University, Hangzhou 310018 (China); Chen, T. [Department of Ocean Science and Engineering, Zhejiang University, Hangzhou 310058 (China); Li, H.Y. [Zhoushan Ocean Research Institute, Zhejiang University, Zhoushan 316021 (China); Xia, M.S., E-mail: msxia@zju.edu.cn [Department of Ocean Science and Engineering, Zhejiang University, Hangzhou 310058 (China); Ye, Y.; Zheng, H. [Department of Ocean Science and Engineering, Zhejiang University, Hangzhou 310058 (China)

2013-11-15

Highlights: • Adding modified shell powder could significantly increase the properties of PP. • The modified shell powder could act as a nucleating agent in PP matrix. • The modified shell powder has a potential to be used as a bio-filler. -- Abstract: Shell waste, with its high content of calcium carbonate (CaCO{sub 3}) plus organic matrix, has a potential to be used as a bio-filler. In this work, shell waste was modified by furfural and then incorporated to reinforce polypropylene (PP). The shell waste and modified powder were characterized by means of X-ray diffraction (XRD), scanning electron microscopy equipped with an energy dispersive spectrometer (SEM-EDS), X-ray photoelectronic spectroscopy (XPS), and Fourier transformed infrared spectroscopy (FTIR). The mechanical and thermal properties of neat PP and PP composites were investigated as well. Thermal gravimetric (TG) analyses confirmed the reinforcing role of modified powder in PP composites. The mechanical properties studied showed that adding modified powder could significantly increase the impact strength, elongation at break point and flexural modulus of composites. The maximum incorporation content could reach 15 wt.% with a good balance between toughness and stiffness of PP composites. Differential scanning calorimetry (DSC) results showed that the modified powder could act as a nucleating agent and thus increase the crystallization temperature of PP. Polarized optical microscopy (POM) observation also indicated that the introduction of modified powder could promote the heterogeneous nucleation of PP matrix.

Irradiation of isotactic polypropylene and polypropylene/ethylene-propylene (diene-monomer) blends

NARCIS (Netherlands)

Gisbergen, van J.G.M.; Meijerink, J.I.; Overbergh, N.; Kleintjes, L.; Lemstra, P.J.

1989-01-01

The influence of electron beam irradiation on rheological properties and morphology of polypropylene and polypropylene/ethylene-propylene rubber blends was studied. Electron beam irradiation of isotactic PP causes pronounced chain scission (degradation) at dosis = 100 kGy. Melt viscosity can be

Melamine-formaldehyde microcapsules filled sappan dye modified polypropylene composites: encapsulation and thermal properties

Science.gov (United States)

Phanyawong, Suphitcha; Siengchin, Suchart; Parameswaranpillai, Jyotishkumar; Asawapirom, Udom; Polpanich, Duangporn

2018-01-01

Sappan dye, a natural dye extracted from sappan wood is widely used in cosmetics, textile dyeing and as food additives. However, it was recognized that natural dyes cannot withstand high temperature. In this study, a protective coating of melamine-formaldehyde shell material was applied over the sappan dye to improve its thermal stability. The percentage of sappan dye used in the microencapsulation was 30, 40, 50, 60 and 70 wt%. The color, shape, size, and thermal stability of sappan dye microcapsules were investigated. It was found that increasing amount of sappan dye content in the microcapsules decreased the particle size. Thermal analysis reveals that the melamine-formaldehyde resin served as an efficient protective shell for sappan dye. Besides, 30 wt% sappan dye microcapsules with different weight percent (1, 3 and 5 wt%) of sappan dye was used as modifier for polypropylene (PP). All the prepared composites are red in color which supports the thermal stability of the microcapsules. The changes in crystallinity and melting behavior of PP by the addition of microcapsules were studied in detail by differential scanning calorimetry. Thermogravimetric studies showed that the thermal stability of PP composites increased by the addition of microcapsules.

Density-independent algorithm for sensing moisture content of sawdust based on reflection measurements

Science.gov (United States)

A density-independent algorithm for moisture content determination in sawdust, based on a one-port reflection measurement technique is proposed for the first time. Performance of this algorithm is demonstrated through measurement of the dielectric properties of sawdust with an open-ended haft-mode s...

Effect of combined extrusion parameters on mechanical properties of basalt fiber-reinforced plastics based on polypropylene

Science.gov (United States)

Bashtannik, P. I.; Ovcharenko, V. G.; Boot, Yu. A.

1997-11-01

Basalt fibers are efficient reinforcing fillers for polypropylene because they increase both the mechanical and the tribotechnical properties of composites. Basalt fibers can compete with traditional fillers (glass and asbestos fibers) of polypropylene with respect to technological, economic, and toxic properties. The effect of technological parameters of producing polypropylene-based basalt fiber-reinforced plastics (BFRPs) by combined extrusion on their mechanical properties has been investigated. The extrusion temperature was found to be the main parameter determining the mechanical properties of the BFRPs. With temperature growth from 180 to 240°C, the residual length of the basalt fibers in the composite, as well as the adhesive strength of the polymer-fiber system, increased, while the composite defectiveness decreased. The tensile strength and elastic modulus increased from 35 to 42 MPa and 3.2 to 4.2 GPa, respectively. At the same time, the growth in composite solidity led to its higher brittleness. Thus, a higher temperature of extrusion allows us to produce materials which can be subjected to tensile and bending loads, while the materials produced at a lower temperature of extrusion are impact stable. The effect of the gap size between the extruder body and moving disks on the mechanical properties of the BFRPs is less significant than that of temperature. An increase of the gap size from 2 to 8 mm improves the impregnation quality of the fibers, but the extruder productivity diminishes. The possibility of controling the properties of reinforced polypropylene by varying the technological parameters of combined extrusion is shown. The polypropylene-based BFRPs produced by the proposed method surpass the properties of glass and asbestos fiber-reinforced plastics.

The method of polymer compositions manufacturing on the base of polypropylene[Radiation processing]; Sposob wytwarzania kompozycji polimerow na bazie polipropylenu

Energy Technology Data Exchange (ETDEWEB)

Zimek, Z; Bulhak, Z; Bojarski, J; Stachowicz, W [Warsaw (Poland); Mirkowski, K [Legionowo (Poland)

1966-06-28

The method of manufacturing of radiation resistant polymer composition of medical quality have been proposed. The raw material consisted of polypropylene homopolymer with propylene-ethylene copolymer, ethylene-vinyl acetate copolymer and polystyrene suspension have been mixed and extruded during heating at 190-270{sup o}C. Then obtained mixture have been granulated. The material structure with microagglomerates is responsible for elevated radiation resistance of material being destinated for medical devices production and radiosterilization.

Electrical and dielectric properties of foam injection-molded polypropylene/multiwalled carbon nanotube composites

Energy Technology Data Exchange (ETDEWEB)

Ameli, A.; Nofar, M.; Saniei, M.; Hossieny, N.; Park, C. B. [Microcellular Plastics Manufacturing Laboratory, Department of Mechanical and Industrial Engineering, University of Toronto, 5 King’s College Road, Toronto, Ontario, Canada M5S 3G8 (Canada); Pötschke, P. [Leibniz-Institut für Polymerforschung Dresden e.V. (IPF), Hohe Strasse 6, D-01069 Dresden (Germany)

2015-05-22

A combination of high dielectric permittivity (ε′) and low dielectric loss (tan δ) is required for charge storage applications. In percolative systems such as conductive polymer composites, however, obtaining high ε′ and low tan δ is very challenging due to the sharp insulation-conduction transition near the threshold region. Due to the particular arrangement of conductive fillers induced by both foaming and injection molding processes, they may address this issue. Therefore, this work evaluates the application of foam injection molding process in fabricating polymer nanocomposites for energy storage. Polypropylene-multiwalled carbon nanotubes (PP-MWCNT) composites were prepared by melt mixing and foamed in an injection molding process. Electrical conductivity (σ), ε′ and tan δ were then characterized. Also, scanning and transmission electron microscopy (SEM and TEM) was used to investigate the carbon nanotube’s arrangement as well as cellular morphology. The results showed that foam injection-molded composites exhibited highly superior dielectric properties to those of solid counterparts. For instance, foamed samples had ε′=68.3 and tan δ =0.05 (at 1.25 vol.% MWCNT), as opposed to ε′=17.8 and tan δ=0.04 in solid samples (at 2.56 vol.% MWCNT). The results of this work reveal that high performance dielectric nanocomposites can be developed using foam injection molding technologies for charge storage applications.

[Quantification of Wood Flour and Polypropylene in Chinese Fir/Polypropylene Composites by FTIR].

Science.gov (United States)

Lao, Wan-li; Li, Gai-yun; Zhou, Qun; Qin, Te-fu

2015-06-01

The ratio of wood and plastic in Wood Plastic Composites (WPCss) influences quality and price, but traditional thermochemical methods cannot rapidly and accurately quantify the ratio of wood/PP in WPCss. This paper was addressed to investigate the feasibility of quantifying the wood flour content and plastic content in WPCss by Fourier Transform Infrared (FTIR) spectroscopy. With Chinese fir, polypropylene (PP) and other additives as raw materials, 13 WPCs samples with different wood flour contents, ranging from 9.8% to 61.5%, were prepared by modifying wood flour, mixing materials and extrusion pelletizing. The samples were analyzed by FTIR with the KBr pellets technique. The absorption peaks of WPCss at 1059, 1 033 and 1 740 cm(-1) are considered as characteristic of Chinese fir, and the absorption peaks at 1 377, 2 839 and 841 cm(-1) are typical of PP by comparing the spectra of WPCss with that of Chinese fir, PP and other additives. The relationship between the wood flour content, PP content in WPCss and their characteristic IR peaks height ratio was established. The results show that there is a strong linear correlation between the wood flour content in WPCss and I1 059/l 1 377/I1 033, /I1377, R2 are 0.992 and 0.993 respectively; there is a high linear correlation between the PP content in WPCss and I1 377/I1 740, I2 839 /I1 740 R2 are 0.985 and 0.981, respectively. Quantitative methods of the wood flour content and PP content in WPCss by FTIR were developed, the predictive equations of the wood flour content in WPCss are y = 53.297x-9. 107 and y = 55.922x-10.238, the predictive equations of the PP content in WPCss are y = 6.828 5x+5.403 6 and y = 8.719 7x+3.295 8. The results of the accuracy test and precision test show that the method has strong repeatability and high accuracy. The average prediction relative deviations of the wood flour content and PP content in WPCss are about 5%. The prediction accuracy has been improved remarkably, compared to

Biodegradation of Polypropylene Nonwovens

Science.gov (United States)

Keene, Brandi Nechelle

The primary aim of the current research is to document the biodegradation of polypropylene nonwovens and filament under composting environments. To accelerate the biodegradat ion, pre-treatments and additives were incorporated into polypropylene filaments and nonwovens. The initial phase (Chapter 2) of the project studied the biodegradation of untreated polypropylene with/without pro-oxidants in two types of composting systems. Normal composting, which involved incubation of samples in food waste, had little effect on the mechanical properties of additive-free spunbond nonwovens in to comparison prooxidant containing spunbond nonwovens which were affected significantly. Modified composting which includes the burial of samples with food and compressed air, the polypropylene spunbond nonwovens with/without pro-oxidants displayed an extreme loss in mechanical properties and cracking on the surface cracking. Because the untreated spunbond nonwovens did not completely decompose, the next phase of the project examined the pre-treatment of gamma-irradiation or thermal aging prior to composting. After exposure to gamma-irradiation and thermal aging, polypropylene is subjected to oxidative degradation in the presence of air and during storage after irradiat ion. Similar to photo-oxidation, the mechanism of gamma radiation and thermal oxidative degradation is fundamentally free radical in nature. In Chapter 3, the compostability of thermal aged spunbond polypropylene nonwovens with/without pro-oxidant additives. The FTIR spectrum confirmed oxidat ion of the polypropylene nonwovens with/without additives. Cracking on both the pro-oxidant and control spunbond nonwovens was showed by SEM imaging. Spunbond polypropylene nonwovens with/without pro-oxidants were also preirradiated by gamma rays followed by composting. Nonwovens with/without pro-oxidants were severely degraded by gamma-irradiation after up to 20 kGy exposure as explained in Chapter 4. Furthermore (Chapter 5), gamma

Assessment of extrusion-sonication process on flame retardant polypropylene by rheological characterization

Directory of Open Access Journals (Sweden)

Guadalupe Sanchez-Olivares

2016-05-01

Full Text Available In this work, the rheological behavior of flame retardant polypropylene composites produced by two methods: 1 twin-screw extrusion and 2 ultrasound application combined with a static mixer die single-screw extrusion is analyzed in detail; results are related to the morphology of the composites. The flame retardant polymer composites are composed of a polypropylene matrix, an intumescent flame retardant system and functionalized clay. Scanning electron microscopy revealed that the combination of the static mixer die and on-line sonication reduced particle size and improved the dispersion and distribution of the intumescent additives in the polypropylene matrix at the micrometric level. From linear viscoelastic properties, the Han, Cole-Cole and van Gurp-Palmen diagrams characterized the improved particle dispersion of the flame retardant additives. Two well-defined rheological behaviors were observed in these diagrams. These behaviors are independent on clay presence and concentration. In fact, the ultrasound device generates a 3D highly interconnected structure similar to a co-continuous pattern observed in polymer blends as evidenced by rheological measurements. This improvement in the dispersion and distribution of the additives is attributed to the combined effect of the static mixer die and on-line sonication that allowed reducing the additive content while achieving the optimum classification UL94-V0.

Mechanical and thermal properties of polymer composite based on natural fibers: Moroccan hemp fibers/polypropylene

International Nuclear Information System (INIS)

Elkhaoulani, A.; Arrakhiz, F.Z.; Benmoussa, K.; Bouhfid, R.; Qaiss, A.

2013-01-01

Highlights: ► Moroccan hemp fibers are used as reinforcement in thermoplastic matrix. ► Moroccan hemp fiber was alkali treated to remove waxes and noncellulosic component. ► Fiber–matrix adhesion was assured by the use of a SEBS-g-MA as a compatibilizer. - Abstract: Moroccan hemp is a cellulosic fiber obtained from the north of Morocco. Their use as reinforcement in thermoplastic matrix composite requires a knowledge of their morphology and structure. In this paper the Moroccan hemp fiber was alkali treated to remove waxes and noncellulosic surface components. Fiber/matrix adhesion was assured by the use of a styrene-(ethylene-butene)-styrene three-block copolymer grafted with maleic anhydride (SEBS-g-MA) as a compatibilizer. Scanning electron microscopy (SEM), Fourier transforms infrared spectroscopy (FT-IR), Thermogravimetric analysis (TGA), tensile and torsional tests were carried out for hemp fibers polypropylene composite and the compatibilized composite at different fiber content. Thus, the binary composite PP/hemp fibers (Alk) and ternary system with maleic anhydride indicate clearly an improved adhesion of the fiber to the matrix as results of the good interaction at the interface. A gain of 50% on the Young’s modulus of PP/hemp 25 wt.% without coupling agent and 74% on the PP/hemp 20 wt.% composite with the coupling agent were found. Tensile strength curve shows a remarkable stabilization when the coupling agent was used

Poly(lauryl acrylate) and poly(stearyl acrylate) grafted multiwalled carbon nanotubes for polypropylene composites

DEFF Research Database (Denmark)

Daugaard, Anders Egede; Jankova Atanasova, Katja; Hvilsted, Søren

2014-01-01

Two new polymer grafts on an industrial grade multiwalled carbon nanotube (MWCNT) were prepared through a non-oxidative pathway employing controlled free radical polymerization for surface initiated polymer grafting. After photochemical introduction of an ATRP initiator onto the MWCNT......, polymerizations of lauryl or stearyl acrylate were performed, resulting in two novel polymer modifications on the MWCNT (poly(lauryl acrylate) or poly(stearyl acrylate)). The method was found to give time dependent loading of polymers as a function of time (up to 38 wt% for both acrylates), and showed a plateau...... in loading after 12 h of polymerization. The modified nanomaterials were melt mixed into polypropylene composites with very low filler loading (0.3 wt%), whereafter both the thermal and electrical properties were investigated by DSC and dielectric resonance spectroscopy. The electrical properties were found...

Cedrela odorata L. PRODUCTION IN A RAW SAWDUST SUBSTRATE IN TECHNICIAN SYSTEM AT TECPAN DE GALEANA, GUERRERO, MEXICO

Directory of Open Access Journals (Sweden)

José Justo Mateo-Sánchez

2011-01-01

Full Text Available Nursery high quality plants production by using expensive commercial substrates (peat moss, perlite, vermiculite decreases profits; this is the main reason to search alternative production substrates. Pine sawdust is a sub product of forestry industry cheap and available in forest areas. In recent years it has been used as a substrateproviding good results. In this study it was evaluated the effect of different sawdust mixtures on Cedrela odorata L. plant growth in a technician system in forest nursery under shade cloth covered. A completely randomized experimental design was used with eleven substrate components combinations (sawdust + peat moss-perlite-vermiculite mixtures ranging from 0% to 100% each. After three and a half months morphological variables were measured so as some quality indexes in seedlings. The largest diameter was obtained by the mixture of 70% sawdust + 30% peat moss mix-vermiculite-perlite. The highest in height by using the mixture 80% sawdust + 20% peat moss - vermiculite – perlite mixture. The highest leaves dry weight corresponded to 90 % sawdust + 10% peat moss-vermiculite-perlite mixture. However the highest root weight and total dry weight values occurred in 60% sawdust + 40% peat moss – perlite - vermiculite mixture. As for the height-diameter ratio (slenderness index, the best value is obtained a mixture of 80% sawdust + 20% peat moss, perlite, vermiculite. According to Dickson Quality Index (DQI, used to predict the plant field surviving, the highest value was obtained for the 60% sawdust + 40% peat moss-perlite-vermiculite mixture.

Raman structural study of melt-mixed blends of isotactic polypropylene with polyethylene of various densities

Science.gov (United States)

Prokhorov, K. A.; Nikolaeva, G. Yu; Sagitova, E. A.; Pashinin, P. P.; Guseva, M. A.; Shklyaruk, B. F.; Gerasin, V. A.

2018-04-01

We report a Raman structural study of melt-mixed blends of isotactic polypropylene with two grades of polyethylene: linear high-density and branched low-density polyethylenes. Raman methods, which had been suggested for the analysis of neat polyethylene and isotactic polypropylene, were modified in this study for quantitative analysis of polyethylene/polypropylene blends. We revealed the dependence of the degree of crystallinity and conformational composition of macromolecules in the blends on relative content of the blend components and preparation conditions (quenching or annealing). We suggested a simple Raman method for evaluation of the relative content of the components in polyethylene/polypropylene blends. The degree of crystallinity of our samples, evaluated by Raman spectroscopy, is in good agreement with the results of analysis by differential scanning calorimetry.

Effects of electron beam radiation dose on the compatibilization behaviour in recycled polypropylene/microcrystalline cellulose composites

Science.gov (United States)

Samat, N.; Motsidi, S. N. R.; Lazim, N. H. M.

2018-01-01

The purpose of this research was to evaluate the influence of dose level of electron beam on the compatibilization behavior of recycled polypropylene (rPP) in rPP/microcrystalline cellulose (MCC) composites. Initially, the rPP was irradiated with various dose of electron beam (5 kGy up to 250 kGy) which then mixed with unirradiated rPP (u-rPP) at a ratio of 30:70 respectively. The composites were prepared by incorporating a series wt% of MCC fibers into rPP (u-rPP : i-rPP) using extruder and finally moulded with an injection moulding machine. The compatibility behavior of irradiated rPP (i-rPP) were analysed with mechanical tensile and thermal methods. The results of mechanical analysis showed great improvement in tensile modulus but an increase in radiation dosage gradually decreased this property. Nevertheless, the tensile strength exhibited a minor effect. The thermal stability of composites is lowered with increase in the absorbed dose, more significantly at higher content of MCC. Fracture surface observations reveal adhesion between the cellulose and rPP matrix.

Bond Characteristics of Macro Polypropylene Fiber in Cementitious Composites Containing Nanosilica and Styrene Butadiene Latex Polymer

Directory of Open Access Journals (Sweden)

Jae-Woong Han

2015-01-01

Full Text Available This study evaluated the bond properties of polypropylene (PP fiber in plain cementitious composites (PCCs and styrene butadiene latex polymer cementitious composites (LCCs at different nanosilica contents. The bond tests were evaluated according to JCI SF-8, in which the contents of nanosilica in the cement were 0, 2, 4, 6, 8, and 10 wt%, based on cement weight. The addition of nanosilica significantly affected the bond properties between macro PP fiber and cementitious composites. For PCCs, the addition of 0–2 wt% nanosilica enhanced bond strength and interface toughness, whereas the addition of 4 wt% or more reduced bond strength and interface toughness. The bond strength and interfacial toughness of LCCs also increased with the addition of up to 6% nanosilica. The analysis of the relative bond strength showed that the addition of nanosilica affects the bond properties of both PCC and LCC. This result was confirmed via microstructural analysis of the macro PP fiber surface after the bond tests, which revealed an increase in scratches due to frictional forces and fiber tearing.

Rheological and mechanical properties of polypropylene prepared with multi-walled carbon nanotube masterbatch.

Science.gov (United States)

Shim, Young-Sun; Park, Soo-Jin

2012-07-01

In this study, the effects of polypropylene-grafted maleic-anhydride-treated multi-walled carbon nanotubes (PP-MWNTs) on the viscoelastic behaviors and mechanical properties of a polypropylene-(PP)-based composite system were examined. The PP-MWNT/PP composites were prepared via melt mixing with a 3:1 ratio of PP-g-MA and acid-treated MWNTs at 220 degrees C. The surface characteristics of the PP-MWNTs were confirmed via Fourier transform infrared (FTIR) spectroscopy and transmission electron microscopy (TEM). The viscoelastic behavior and mechanical properties of the PP-MWNT/PP composites were confirmed using a rheometer and an ultimate testing machine (UTM). The storage and loss moduli increased with increasing PP-MWNT content. The critical intensity stress factor (K(IC)) of the PP-MWNT/PP composites at high filler loading was also higher than that of the MWNT/PP composites. In conclusion, the viscoelastic behavior and mechanical properties of MWNT/PP can be improved by grafting MWNTs to PP-g-MA.

Mechanism of enhanced performance on a hybrid direct carbon fuel cell using sawdust biofuels

Science.gov (United States)

Li, Shuangbin; Jiang, Cairong; Liu, Juan; Tao, Haoliang; Meng, Xie; Connor, Paul; Hui, Jianing; Wang, Shaorong; Ma, Jianjun; Irvine, John T. S.

2018-04-01

Biomass is expected to play a significant role in power generation in the near future. With the uprising of carbon fuel cells, hybrid direct carbon fuel cells (HDCFCs) show its intrinsic and incomparable advantages in the generation of clean energy with higher efficiency. In this study, two types of biomass treated by physical sieve and pyrolysis from raw sawdust are investigated on an anode-supported HDCFC. The structure and thermal analysis indicate that raw sawdust has well-formed cellulose I phase with very low ash. Electrochemical performance behaviors for sieved and pyrolyzed sawdust combined with various weight ratios of carbonate are compared in N2 and CO2 purge gas. The results show that the power output of sieved sawdust with 789 mWcm-2 is superior to that of pyrolyzed sawdust in CO2 flowing, as well as in N2 flowing. The anode reaction mechanism for the discrepancy of two fuels is explained and the emphasis is also placed on the modified oxygen-reduction cycle mechanism of catalytic effects of Li2CO3 and K2CO3 salts in promoting cell performance.

Modelling of Creep and Stress Relaxation Test of a Polypropylene Microfibre by Using Fraction-Exponential Kernel

Directory of Open Access Journals (Sweden)

Andrea Sorzia

2016-01-01

Full Text Available A tensile test until breakage and a creep and relaxation test on a polypropylene fibre are carried out and the resulting creep and stress relaxation curves are fit by a model adopting a fraction-exponential kernel in the viscoelastic operator. The models using fraction-exponential functions are simpler than the complex ones obtained from combination of dashpots and springs and, furthermore, are suitable for fitting experimental data with good approximation allowing, at the same time, obtaining inverse Laplace transform in closed form. Therefore, the viscoelastic response of polypropylene fibres can be modelled straightforwardly through analytical methods. Addition of polypropylene fibres greatly improves the tensile strength of composite materials with concrete matrix. The proposed analytical model can be employed for simulating the mechanical behaviour of composite materials with embedded viscoelastic fibres.

Effect of porous zeolite on temperature-dependent physical properties of polypropylene/octadecane (PP/OD composite films

Directory of Open Access Journals (Sweden)

D. Kim

2018-07-01

Full Text Available Polymeric materials with temperature-dependent gas permeabilities using a phase change material are designed and their applicability as a packaging system investigated. Polypropylene/octadecane/zeolite (PP/OD/ZL composite films were prepared via extrusion process. ZL was used as a filler to enhance the dispersion and interfacial interaction between the OD and the PP originating from different flowabilities during the extrusion process. (FTIR and (WAXD analyses showed that the incorporation of ZL increased the interfacial interaction between PP and OD, resultantly enhancing the thermal stability, mechanical properties, and the oxygen transmittance rate and mechanical properties after contact with food simulants and thermal treatment. When the temperature was elevated from 10 to 30 °C, oxygen and water vapor transmittance rate of the composite films increased sharply because of the influence of the OD content. It was surmised that temperaturedependent permeation jump caused by increasing of segmental mobility of OD phase and converting the crystalline structure to an amorphous one of OD phase in the composite films. However, the permeation jump in the composite films was weakened as the ZL content increased. These results are related to changes in the interfacial interaction and crystallinity in the composite films due to the addition of ZL.

Effect of secondary air injection on the combustion efficiency of sawdust in a fluidized bed combustor

Directory of Open Access Journals (Sweden)

K. V. N. Srinivasa Rao

2008-03-01

Full Text Available Agricultural wastes like bagasse, paddy husks, sawdust and groundnut shells can be effectively used as fuels for fluidized bed combustion; otherwise these biomass fuels are difficult to handle due to high moisture and fines content. In the present work the possibility of using sawdust in the fluidized bed combustor, related combustion efficiencies and problems encountered in the combustion process are discussed. The temperature profiles for sawdust with an increase in fluidizing velocity along the vertical height above the distributor plate indicate that considerable burning of fuel particles is taking place in the freeboard zone rather than complete burning within the bed. Therefore, an enlarged disengagement section is provided to improve the combustion of fines. The temperature profiles along the bed height are observed at different feed rates. The feed rate of sawdust corresponding to the maximum possible temperature was observed to be 10.2 kg/h. It is observed that 50-60% excess air is optimal for reducing carbon loss during the burning of sawdust. The maximum possible combustion efficiency with sawdust is 99.2% and is observed with 65% excess air.

Smart Natural Fiber Reinforced Plastic (NFRP) Composites Based On Recycled Polypropylene in The Presence Kaolin

Science.gov (United States)

Suharty, N. S.; Ismail, H.; Diharjo, K.; Handayani, D. S.; Lestari, W. A.

2017-07-01

Composites contain double filler material which act as reinforcement and flame retardants of recycled polypropylene (rPP)/kaolin(Kao)/palm oil empty bunch fiber (PEBF) have been succesfully prepared. The composites were synthesized through reactively solution method, using coupling agent PP-g-AA and compatibilizer DVB. The effect of double filler [Kao/PEBF] were investigated flexural strength (FS), inflammability, and morphology. Mechanical testing result in accordance to ASTM D790, the FS of rPP/DVB/PP-g-AA/Kao+ZB/PEBF composite was 48% higher than that of rPP matrix. Moreover, flexural modulus (FM) was significantly improved by 56% as compared to that of rPP matrix. The scanning electron images (SEM) shown good dispersion of [Ka/PEBF] and good filler-matrix interaction. The inflammability testing result which is tested using ASTM D635, showed that the flame resistance of rPP/DVB/PP-g-AA/Kao+ZB/PEBF composite was improve by increasing of time to ignition (TTI) about 857% and burning rate (BR) decreasing to 66% compared to the raw material rPP matrix. In the same time, the addition of 20% (w/w) PEBF as a second filler to form rPP/DVB/PP-g-AA/Kao+ZB/PEBF composites (F5) is able to increase: the FS by 17.5%, the FM by 19%, the TTI by 7.6% and the BR by 3.7% compared to the composite without PEBF (F2).

Radiopasteurization of sawdust media used in propagation of mushrooms

International Nuclear Information System (INIS)

Ito, Hitoshi; Sato, Tomotaro

1975-01-01

In our country, cultivation of mushrooms such as Pleurotus ostreatus, Kuehneromyces nameko, and Lentinus edodes (Cortinellus shiitake) are expanding, and has reached considerable amounts. These mushrooms are cultivated generally on decaying logs of broad leaf trees. Recently, these mushrooms are also cultivated artificially on the sawdust-media containing rice bran and other nutrient in the room of which temperature is controlled. However, these artificial culture media must be germicidated for 2 or 6 hours at 100 to 120 0 C before inoculation of mushroom spawn. In this study, attempts were made to cultivate Pleurotus ostreatus on the sawdust-media pasteurized by ionizing radiation. Inhibition of mushrooms growth were caused mainly by multiplication of Citrobacter and Fusarium, and these organisms were eliminated by a dose of 0.5 Mrad gamma irradiation. A surprising result was that many of sawdust media subjected to 0.5, 1.0 and 2.0 Mrad increased mycelial growth rates more than heat treatments, and also mushroom yields were enhanced. The multiplication of remaining microorganisms such as Bacillus and yeasts after irradiation with a dose of 0.5 Mrad or 1.0 Mrad did not inhibit the mycelial growth of mushrooms. (auth.)

Tuning the nano/micro-structure and properties of melt-processed ternary composites of polypropylene/ethylene vinyl acetate blend and nanoclay: The influence of kinetic and thermodynamic parameters

CSIR Research Space (South Africa)

Mofokeng, Tladi G

2017-09-01

Full Text Available The present study reports the dependence of the nano/micro-structure and properties of polypropylene (PP)/ethylene vinyl acetate (EVA)/nanoclay ternary composites on the kinetics and thermodynamics of the melt-mixing process. The size of dispersed...

Dye removal from wastewater using activated carbon developed from sawdust: adsorption equilibrium and kinetics.

Science.gov (United States)

Malik, P K

2004-09-10

Mahogany sawdust was used to develop an effective carbon adsorbent. This adsorbent was employed for the removal of direct dyes from spent textile dyeing wastewater. The experimental data were analysed by the Langmuir and Freundlich models of adsorption. Equilibrium data fitted well with the Langmuir model. The rates of adsorption were found to conform to the pseudo-second-order kinetics with good correlation. The equilibrium adsorption capacity of the sawdust carbon was determined with the Langmuir equation as well as the pseudo-second-order rate equation and found to be >300 mg dye per gram of the adsorbent. The most ideal pH for adsorption of direct dyes onto sawdust carbon was found to be 3 and below. The results indicate that the Mahogany sawdust carbon could be employed as a low cost alternative to commercial activated carbon in the removal of dyes from wastewater.

Thermo-chemical pretreatment and enzymatic hydrolysis for enhancing saccharification of catalpa sawdust.

Science.gov (United States)

Jin, Shuguang; Zhang, Guangming; Zhang, Panyue; Li, Fan; Fan, Shiyang; Li, Juan

2016-04-01

To improve the reducing sugar production from catalpa sawdust, thermo-chemical pretreatments were examined and the chemicals used including NaOH, Ca(OH)2, H2SO4, and HCl. The hemicellulose solubilization and cellulose crystallinity index (CrI) were significantly increased after thermo-alkaline pretreatments, and the thermo-Ca(OH)2 pretreatment showed the best improvement for reducing sugar production comparing to other three pretreatments. The conditions of thermo-Ca(OH)2 pretreatment and enzymatic hydrolysis were systematically optimized. Under the optimal conditions, the reducing sugar yield increased by 1185.7% comparing to the control. This study indicates that the thermo-Ca(OH)2 pretreatment is ideal for the saccharification of catalpa sawdust and that catalpa sawdust is a promising raw material for biofuel. Copyright © 2016 Elsevier Ltd. All rights reserved.

Arsenic Removal from Aqueous Solutions Using Modified and Unmodified Oak Sawdust

Directory of Open Access Journals (Sweden)

Ali Reza Rahmani

2016-01-01

Full Text Available In this research, oak sawdust, in both modified and unmodified forms, was used as an economical and low-cost material for the removal of arsenic from aqueous solutions. For this purpose, arsenic synthetic samples were prepared using NaAsO2 in distilled water and the effects of pH, adsorbent dosage, contact time, and initial As(V concentration were investigated on As(V adsorption using the adsorbents prepared. The results showed that modified sawdust achieved the highest efficiency (>91% over a contact time of 60 min and at pH 7 when the adsorbent dosage was 4gr/L and the initial As(V concentration was 150 µg/L. The data from both adsorbents fitted well to the Langmuir isotherm. Under optimum conditions (an initial As(V concentration of 150 µg/L and optimal absorption pH, contact time, and adsorbent dosage, maximum As(V removal efficiencies were 93.85% and 91.034% with the modified  and unmodified sawdust adsorbents, respectively. Given the availability and low cost of the adsorbent used and the high removal efficiency obtained at  lower adsorbent dosages and contact times, the modified oak sawdust may be recommended as an effective adsorbent for the removal of arsenic (v from aqueous solutions, especially since it requires no need for pH modification.

Flammability of polypropylene/organoclay nanocomposites; Inflamabilidade de nanocompositos de polipropileno/argila organofilica

Energy Technology Data Exchange (ETDEWEB)

Alves, Tatianny Soares; Barbosa, Renata [Universidade Federal do Piaui (UFPI), Teresina (Brazil); Carvalho, Laura Hecker de [Universidade Federal de Campina Grande (UFCG), PB (Brazil); Canedo, Eduardo Luis [Instituto de Tecnologia de Pernambuco, Recife (Brazil)

2014-11-01

The flammabilities of nanocomposites made with three polypropylene grades (homo and copolymers) with 5 wt % of organoclay (Cloisite 20A), 5 or 15 wt % of maleated polypropylene as compatibilizer, and 0, 0.5 or 1 wt % of cis-13-docosenamide (Erucamide) as co-intercalant, were studied using the horizontal burning test UL94HB. Masterbatches prepared in an internal mixer were diluted in the polypropylene matrix using a corotating twin-screw extruder, with different screw configurations and operating at 240 or 480 rpm. Results indicate that the high burning rate of the composites was not affected by the processing conditions. For all formulations was observed a significant reduction in smoke release, lack of dripping and the formation of a char surface layer, that protected the core of the samples. (author)

Jute fiber reinforced polypropylene produced by continuous extrusion compounding. Part 1. Processing and ageing properties

NARCIS (Netherlands)

Oever, van den M.J.A.; Snijder, M.H.B.

2008-01-01

This article addresses the processing and ageing properties of jute fiber reinforced polypropylene (PP) composites. The composite has been manufactured by a continuous extrusion process and results in free flowing composite granules, comprising up to 50 weight percent (wt %) jute fiber in PP. These

Modification of bentonite clay and application on polypropylene nano composites

International Nuclear Information System (INIS)

Oliveira, Akidauana D.B.; Rodrigues, Andre W.B.; Agrawal, Pankaj; Araujo, Edcleide M.; Melo, Tomas J.A.

2009-01-01

This work consisted on the modification of Brasgel PA clay with ionic surfactant Praepagen WB and its incorporation into polypropylene. The results of infrared and DR-X was showed that the intercalation of surfactant in the clay and the incorporation of organoclay in PP matrix resulted in the formation of an intercalated structure. The impact strength of PP increased with the incorporation of organoclay. (author)

Optimization of the pretreatment of Prosopis nigra sawdust for the production of fermentable sugars

Directory of Open Access Journals (Sweden)

Eliana P. Dagnino

2013-02-01

Full Text Available The black carob tree (Prosopis nigra is a particularly valued species in Chaco, Argentina on account of its hard wood. Finding a use for the sawdust, the main industrial residue of wood, could be useful within the furniture industry of any country in the tropics seeking to apply the biorefinery concept. For the conversion of wood carbohydrates to bioethanol, a pretreatment stage is necessary. The objective of this work was to find the acid pretreatment conditions that maximize the extraction of xylose with minimum degradation, while maximizing the concentration of glucans in the pretreated solid to obtain better enzymatic accessibility, using black carob tree sawdust as the raw material. The optimization was carried out by use of a central composite design (CCD with two independent variables: the concentration of the sulfuric acid solution and the heating time. Optimal enzymatic hydrolysis occurred at the mean values of the tested acid solution concentration (1.2% and after shorter heating times (10.2 min. The concentration of sugars after the enzymatic hydrolysis of the pretreated solid over a time period of 72 h was three times higher than the untreated solid.

Role of carbon nanotubes (CNTs) in improving wear properties of polypropylene (PP) in dry sliding condition

International Nuclear Information System (INIS)

Ashok Gandhi, R.; Palanikumar, K.; Ragunath, B.K.; Paulo Davim, J.

2013-01-01

Highlights: ► Role of carbon nanotubes (CNTs) on wear behaviour of polypropylene (PP) is evaluated. ► Effect of applied pressure and composition against a steel counter face is investigated. ► Microstructure and worn surfaces of samples are observed by scanning electron microscope. ► The wear phenomenon has been discussed based on wear losses and worn surfaces. ► The coefficient of friction (μ) and sliding time for PP and PP/CNT blend is investigated. - Abstract: Polymers are widely used for sliding couples against metals and other materials. Polypropylene is a polymer used in variety of applications includes packaging, laboratory equipments, automotive components, etc. Polypropylene is often desirable automotive material due to its low cost, colorability, chemical resistance and UV stability. In addition the range of potential polypropylene uses is nearly unlimited through the use of modifiers, additives and fillers. In the present work, the sliding wear of polypropylene (PP) and carbon nanotube (CNT) blends are evaluated as a function of applied load and composition against a steel counter face in dry condition. The addition of CNT in PP in wear performance is investigated and presented in detail. Microstructure and worn surfaces of samples were observed by scanning electron microscope. The wear phenomenon has been discussed based on wear losses and worn surfaces

Nitrous oxide flux from landfill leachate-sawdust nitrogenous compost

International Nuclear Information System (INIS)

Hui, C.H.; So, M.K.; Lee, C.M.; Chan, G.Y.S.

2003-01-01

Composted nitrogenous waste has the potential to produce excessive amounts of nitrous oxide (N 2 O), a potent greenhouse gas that also contributes to stratospheric ozone depletion. In this laboratory study, sawdust was irrigated with varying amounts of landfill leachate with high NH 4 + -N content (3950 mg l -1 ). Physicochemical properties, including the amount of N 2 O produced, were monitored during the composting process over 28 days. A rapid decline in NH 4 + -N in the first 4 days and increasing NO 3 - -N for 11 days was followed by lower but stabilized levels of available-N, even with repeated leachate irrigation. Less than 0.03% of the leachate-applied N was lost as N 2 O. Higher leachate applications as much as tripled N 2 O production, but this represented a lesser proportion overall of the total nitrogen. Addition of glucose to the composting process had no significant effect on N 2 O production. The derived sawdust-leachate compost supported healthy growth of Sesbania rostrata. It is concluded that compost can be produced from sawdust irrigated with landfill leachate without substantial emission of N 2 O, although excessive flux of N 2 O remains about high application rates over longer time periods. (Author)

Recycling effects on the rheological and thermomechanical properties of polypropylene-based composites

International Nuclear Information System (INIS)

Bahlouli, Nadia; Pessey, Daniel; Raveyre, Claude; Guillet, Jacques; Ahzi, Said; Dahoun, Abdessalam; Hiver, Jean Marie

2012-01-01

Highlights: → Recycling effect on high impact PP with or without talc for automotive industries. → Rheological/mechanical tests, effect of molecular weight, deformation and damage. → Embrittlement of the amorphous matrix by chain scissions and growth of cavitation. → Better stability for talc filled HiPP, but decreased failure stress. → Interfaces talc/PP matrix and EPDM droplets/PP matrix are degraded. -- Abstract: As recycled materials are increasingly used in design of structural components, it is necessary to understand the effect of recycling on the properties and durability of these materials. In this work, the recycling effects on two high impact polypropylenes (HiPP) are studied. The recycling process was simulated by performing several extrusion runs with the same material in order to get a better understanding of the multi recycling effects. These effects were identified not only on the molecular weight and the rheological properties but also on the mechanical properties and the deformation mechanisms. The volume strain has been also measured as a damage indicator in the studied polymers. For both materials, the analysis of the different results showed that the rheological and the mechanical properties were affected by the thermomechanical recycling process. In particular, this process led to the decrease of the molecular weight, the decrease of the failure stress and the decrease of the impact energy. Moreover, Scanning Electronic Micoscopy (SEM) pictures showed a modification of the deformation process due to the embrittlement of the amorphous matrix by the chain scission and by cavitation. Moreover, a better stability for talc filled HiPP was observed but a decrease of the failure stress was obtained because the interfaces talc/polypropylene (PP) matrix and ethylene propylene diene monomer (EPDM) droplets/PP matrix were degraded. Indeed, the knowledge of the molecular characteristics as well as the rheological and mechanical properties of

COMPARATIVE STUDIES OF PHYSICAL CHARACTERISTICS OF RAW AND MODIFIED SAWDUST FOR THEIR USE AS ADSORBENTS FOR REMOVAL OF ACID DYE

Directory of Open Access Journals (Sweden)

Jivan Singh

2011-05-01

Full Text Available The present paper aims to investigate the physical characteristics of sawdust relative to its use as an adsorbent for removal of an acid dye (Orange G from aqueous solutions. The raw sawdust was sieved to have a uniform size and was activated by sulphuric acid by refluxing the content at 60 oC for 4 h. Surface morphology and surface functional groups of both raw and modified sawdust samples were investigated by Scanning Electron Microscope (SEM, Energy Dispersive X-ray Analysis (EDX, Fourier Transformation Infrared (FTIR, and elemental analysis. All these analyses displayed significant change in the structure of the sawdust. The data obtained from batch adsorption experiments for the removal of the selected dye confirmed that adsorption characteristics of the modified sawdust were better than those of raw sawdust.

Effect of Nano-clay on Rheological and Extrusion Foaming Process of a Block-Copolymerized Polypropylene

Directory of Open Access Journals (Sweden)

Wang Mingyi

2016-01-01

Full Text Available The effects of nano-clay and the corresponding coupling agent maleic anhydride grafted polypropylene (PP-g-MAH on thermal properties, rheological properties and extrusion foaming process of a block-copolymerized polypropylene (B-PP were studied. Supercritical CO2 (SC CO2 was used as the foaming agent with a concentration of 5wt%. Each step of foamed B-PP/ PP-g-MAH/ nano-clay composites processing is addressed, including mixing of the composites, manufacture of the composites, foaming process of the composites and characterization of the cell structure. The results showed that incorporation of nano-clay and PP-g-MAH caused reduced melt strength and complex viscosity of B-PP. However, the heterogeneous nucleation induced by nano-clay and PP-g-MAH improved the maximum foaming expansion ratio and cell-population density of B-PP foam.

Stabilization of soft clayey soils with sawdust ashes

Directory of Open Access Journals (Sweden)

Karim Hussein

2018-01-01

Full Text Available The problems of soft clayey soils are taken in considerations by many Iraqi geologists and civil engineers, because about 35% of the Iraqi clay soils (especially southern Iraq are weak. Thus, it is necessary to improve the properties of such soils for road construction by means of using of various stabilizers such as sawdust ash. The main goal of the present study is to stabilize soft clay models with sawdust ash (SDA additive using different percentages (0, 2, 4, 6, 8 and 10% by dry weight of soil. The results revealed that the additive has adverse effects on the property of soil indices by increasing its liquid limit and plasticity index due to clay content. The mixture of sawdust ashes with soft clay soils improves most other physical and mechanical properties of the soil, as expressed by a general reduction in specific gravity and maximum dry density (MDD, as well as a reduction in the compression coefficients (Cc and Cr with an increase in SDA content. While increasing the optimum moisture content (OMC and the undrained shear strength (cu with the increase in SDA content. The stabilized soils (with 4 and 10% ash content resulted in low CBR values (1.6-1.2% which can be used as sub-base. The SDA can be considered as a cheap and acceptable stabilizing agent in road construction for improving most of the geotechnical properties of the soft clayey soil.

Dielectric and thermal properties of isotactic polypropylene/hexagonal boron nitride composites for high-frequency applications

International Nuclear Information System (INIS)

Takahashi, Susumu; Imai, Yusuke; Kan, Akinori; Hotta, Yuji; Ogawa, Hirotaka

2014-01-01

Highlights: • The degree of orientation of the hBN could be controlled by the fabrication process. • The dielectric constants of composites ranged between 2.25 and 3.39. • The dielectric loss of composites was on the order of 10 −4 for all compositions. • The thermal conductivity were improved by controlling orientation of hBN. - Abstract: Dielectric composites aimed for high frequency applications were prepared by using anisotropic hexagonal boron nitride (hBN) particles as a fillers and isotactic polypropylene (iPP) as polymer matrix. Dielectric and thermal properties of the composites were studied, focusing on the filler orientation in the plate-shape specimens and filler concentration up to 40 vol%. The degree of orientation of the filler was controlled by the composite fabrication process. Hot-pressing gave relatively random orientation of the filler in the matrix, while injection molding induced a high orientation. Dielectric constant (ε r ) of the composites ranged between 2.25 and 3.39. The estimation of ε r based on the Bruggeman mixing model agreed well with the measured value. Low dielectric losses (tan δ) at microwave frequencies, on the order of 10 −4 , were obtained for all the compositions. Through-thickness thermal conductivity (k) of the hot-pressed samples showed a drastic increase with increasing the filler concentration, reaching up to 2.1 W/m K at 40 vol% of hBN. The filler concentration dependence of k was less significant for the injection molded composites. In-plane thermal expansion was almost independent on the filler orientation, while the coefficient of thermal expansion for the thickness direction of the hot-pressed sample was reduced to approximately half of the injection molded counterpart. These differences in thermal conductivity and thermal expansion are thought to arise from the difference in hBN filler orientation

Development of Particleboard from Waste Styrofoam and Sawdust

African Journals Online (AJOL)

OLUWASOGO

in a chosen solvent, and properly mixed with sawdust by simple mechanical stirring, using hand lay-up process in ... achieved. Various organic and/or inorganic binders have been ... was hampered by the high viscosity of the resulting resin.

Structural characterization and mechanical properties of polypropylene reinforced natural fibers

Science.gov (United States)

Karim, M. A. A.; Zaman, I.; Rozlan, S. A. M.; Berhanuddin, N. I. C.; Manshoor, B.; Mustapha, M. S.; Khalid, A.; Chan, S. W.

2017-10-01

Recently the development of natural fiber composite instead of synthetics fiber has lead to eco-friendly product manufacturing to meet various applications in the field of automotive, construction and manufacturing. The use of natural fibers offer an alternative to the reinforcing fibers because of their good mechanical properties, low density, renewability, and biodegradability. In this present research, the effects of maleic anhydride polypropylene (MAPP) on the mechanical properties and material characterization behaviour of kenaf fiber and coir fiber reinforced polypropylene were investigated. Different fractions of composites with 10wt%, 20wt% and 30wt% fiber content were prepared by using brabender mixer at 190°C. The 3wt% MAPP was added during the mixing. The composites were subsequently molded with injection molding to prepare the test specimens. The mechanical properties of the samples were investigated according to ISO 527 to determine the tensile strength and modulus. These results were also confirmed by the SEM machine observations of fracture surface of composites and FTIR analysis of the chemical structure. As the results, the presence of MAPP helps increasing the mechanical properties of both fibers and 30wt% kenaf fiber with 3wt% MAPP gives the best result compare to others.

Mechanical properties of thermoplastic composites reinforced with Entada Mannii fibre

Directory of Open Access Journals (Sweden)

Oluwayomi BALOGUN

2017-06-01

Full Text Available The mechanical properties and fracture mechanisms of thermoplastic composites reinforced with Entada mannii fibres was investigated. Polypropylene reinforced with 1, 3, 5, and 7 wt% KOH treated and untreated Entada mannii fibres were processed using a compression moulding machine. The tensile properties, impact strength, and flexural properties of the composites were evaluated while the tensile fracture surface morphology was examined using scanning electron microscopy. The results show that reinforcing polypropylene with Entada mannii fibres resulted in improvement of the tensile strength and elastic modulus. This improvement is remarkable for 5 wt% KOH treated Entada mannii fibre reinforced composites by 28 % increase as compared with the unreinforced polypropylene. The composites reinforced with Entada mannii fibres also had impact strength values of 70 % higher than the unreinforced polypropylene. However, the polypropylene reinforced with 5 and 7wt% KOH treated fibres exhibited significantly higher flexural strength and Young’s modulus by 53% and 52% increase as compared with the unreinforced polypropylene. The fracture surface of the polypropylene composites reinforced with untreated Entada mannii fibres were characterized by fibre debonding, fibre pull-out and matrix yielding while less voids and fibre pull-outs are observed in the composites reinforced with KOH treated Entada mannii fibres. v

Various compositions containing organic substrates to produce Eugenia uniflora L. seedlings

Directory of Open Access Journals (Sweden)

Licielo Romero Vieira

2015-09-01

Full Text Available The use of substrates formulated with agro-industrial residues, such as coconut shell fiber, sawdust, and carbonized rice husk, is among the sustainable alternatives to decrease the production costs of seedlings of plant species. This study aimed to evaluate the use of various substrates for obtaining high quality Eugenia uniflora L. seedlings. The experiment was conducted at the Federal University of Pampa (UNIPAMPA – Campus in São Gabriel, Rio Grande do Sul, Brazil, by sowing directly into 200 cm3 polypropylene tubes, testing various substrates (50% commercial substrate Plantmax® + 50% rice husk; commercial substrate Plantmax®; 50% commercial substrate Plantmax® + 50% coconut shell fiber; and 50% commercial substrate Plantmax® + 50% sawdust. Every 3 days, the number of emerged seedlings was evaluated and, after 180 days, the following morphological features were analyzed: shoot height, stem diameter, number of leaves, root and total fresh weight, shoot, root, and total dry weight, and Dickson’s quality index. The results indicate that all substrates were suitable for Eugenia uniflora emergence, but that containing 50% commercial substrate Plantmax® + 50% sawdust provided a delay in the emergence of this Myrtaceae; also, substrates containing 50% commercial substrate Plantmax® + 50% husk rice and 50% commercial substrate Plantmax® + 50% coconut shell fiber showed to be satisfactory for the growth of Eugenia uniflora seedlings.

Spray-Dried Cellulose Nanofibril-Reinforced Polypropylene Composites for Extrusion-Based Additive Manufacturing: Nonisothermal Crystallization Kinetics and Thermal Expansion

Directory of Open Access Journals (Sweden)

Lu Wang

2018-02-01

Full Text Available Isotactic polypropylene (iPP is a versatile polymer. It accounts for the second-largest polymer consumption worldwide. However, iPP is difficult to 3D print via extrusion-based processing. This is attributable to its rapid crystallization rate. In this study, spray-dried cellulose nanofibrils (SDCNF and maleic anhydride polypropylene (MAPP were investigated to reveal their effects on the nonisothermal crystallization kinetics and thermal expansion of iPP. SDCNF at 3 wt % and 30 wt % accelerated the crystallization rate of iPP, while SDCNF at 10 wt % retarded the crystallization rate by restricting crystal growth and moderately increasing the nucleation density of iPP. Additionally, adding MAPP into iPP/SDCNF composites accelerated the crystallization rate of iPP. The effective activation energy of iPP increased when more than 10 wt % SDCNF was added. Scanning electron microscopy and polarized light microscopy results indicated that high SDCNF content led to a reduced gap size among SDCNF, which hindered the iPP crystal growth. The coefficient of thermal expansion of iPP/SDCNF10% was 11.7% lower than the neat iPP. In summary, SDCNF, at 10 wt %, can be used to reduce the warping of iPP during extrusion-based additive manufacturing.

Calcined clay lightweight ceramics made with wood sawdust and sodium silicate

Energy Technology Data Exchange (ETDEWEB)

Santis, Bruno Carlos de; Rossignolo, Joao Adriano, E-mail: desantis.bruno@gmail.com [Universidade de Sao Paulo (USP), Pirassununga, SP (Brazil); Morelli, Marcio Raymundo [Universidade Federal de Sao Carlos (UFSCar), SP (Brazil). Departamento de Engenharia de Materiais

2016-11-15

This paper aims to study the influence of including wood sawdust and sodium silicate in the production process of calcined clay lightweight ceramics. In the production process first, a sample used by a company that produces ceramic products in Brazil was collected. The sample was analysed by techniques of liquidity (LL) and plasticity (LP) limits, particle size analysis, specific mass, X-ray diffraction (XRD) and X ray fluorescence spectrometry (XRF). From the clay, specimens of pure clay and mixtures with wood sawdust (10%, 20% and 30% by mass) and sodium silicate were produced and fired at a temperature of 900 deg C. These specimens were submitted to tests of water absorption, porosity, specific mass and compressive strength. Results of this research indicate that the incorporation of wood sawdust and sodium silicate in the ceramic paste specimens can be useful to make calcined clay lightweight ceramics with special characteristics (low values of water absorption and specific mass and high values of compressive strength), which could be used to produce calcined clay lightweight aggregates to be used in structural concrete. (author)

Synthesis and characterization of polypropylene/graphite nano composite preparation for in situ polymerization

International Nuclear Information System (INIS)

Montagna, L.S.; Fim, F. de C.; Galland, G.B.

2010-01-01

This paper presents the synthesis of polypropylene/graphite nanocomposites through in situ polymerization, using the metallocene catalyst C 20 H 16 Cl 2 Zr (dichloro(rac-ethylenebis(indenyl))zircon(IV)). The graphite nanosheets in nano dimensions were added to the polymer matrix in percentages of 0.6;1.0;4.2;4.8 and 6.0% (w/w). The TEM images indicated that the thickness of graphite nanosheets ranged from 4 to 60 nm and by means of XRD analysis it was observed that the physical and chemical treatment did not destroyed the graphite layers. The presence of nanosheets did not decrease the catalytic activity of the nanocomposites. TEM images and XRD analysis of nanocomposites showed a good dispersion of the graphite nanosheets in the polypropylene matrix. (author)

Fire retardancy assessment of polypropylene composite filed with nano clay prepared from Iraqi bentonite

Science.gov (United States)

Kareem Salih, Watheq

2018-05-01

Fire retardants have an extraordinary importance because of their role in saving the people, property and reducing the damages and minimizing the dangers resulting from fires and burning of polymeric composites which are used in different civil and industrial fields. The work in this paper can be divided into two main stages. In first one nano-clay was manufactured from Iraqi bentonite and it was characterized using AFM, XRD, XRF, SEM, and BET. The AFM test showed the particle size of prepared nano clay was about 99.25 nm. In the second stage, polypropylene/nano clay composites at three low loading percents (0%,2%,4%,6%) were formulated via twin screw extruder. The fire retardancy tests included burning rate according to ASTM:D-635 and maximum flame height of flame according to ASTM:D-3014. Besides, the mechanical tests and thermal behavior of prepared samples were investigated. The results showed that (4%) of nano-clay had the maximum fire retardancy and while at (2%) loading, the maximum value of tensile strength and Yong modulus were obtained. The maximum heat of fusion was recorded for 6% nano clay sample. The final results assessment confirmed on the possibility of using low loadings of prepared nano clay to improve the fire retardancy, mechanical and thermal properties successfully.

Evaluation of mechanical properties and durability performance of HDPE-wood composites

Energy Technology Data Exchange (ETDEWEB)

Tazi, M.; Erchiqui, F. [Engineering department, Université de Quebec en Abitibi-Témiscamingue (Canada); Kaddami, H. [Université Caddi Ayad Marrakech, Laboratoire ’LCO2MC’, B.P. 549, Marrakech 40000, Maroc (Morocco); Bouazara, M. [Mechanical department, Université de Québec à Chicoutimi Canada (Canada); Poaty, B. [Technology Center of industrial residuals, QC Canada (Canada)

2015-05-22

The objective of this work is to evaluate the mechanical properties and durability performance of bio-composite materials made from sawdust and thermoplastic polymer (HDPE). For the preparation of the composites, sawdust in different proportions with Maleic Anhydride grafted Polyethylene (MAPE) as the coupling agent was used. The thermal and mechanical properties were successively characterized. The results indicate that adding wood fillers to a polymer matrix increases the degree of crystallinity and improves the tensile strength and ductility of composites. On the contrary, resistance to water absorption decreases as a function of the wood fillers. Scanning electron microscopy (SEM) was used to analyze morphological structure alteration when exposed to intense weathering. The biodegradability of bio-composites up to 97 days was also investigated; the results indicate that, by increasing the filler content, the amount of weight loss increased as well. In other words, even though the addition of sawdust to thermoplastic polymer improves the mechanical performance of a composite material, it also accelerates the biodegradation rate of the composite. An optimum amount of filler content might compromise the effect of biodegradation and mechanical properties of composite materials.

Evaluation of mechanical properties and durability performance of HDPE-wood composites

International Nuclear Information System (INIS)

Tazi, M.; Erchiqui, F.; Kaddami, H.; Bouazara, M.; Poaty, B.

2015-01-01

The objective of this work is to evaluate the mechanical properties and durability performance of bio-composite materials made from sawdust and thermoplastic polymer (HDPE). For the preparation of the composites, sawdust in different proportions with Maleic Anhydride grafted Polyethylene (MAPE) as the coupling agent was used. The thermal and mechanical properties were successively characterized. The results indicate that adding wood fillers to a polymer matrix increases the degree of crystallinity and improves the tensile strength and ductility of composites. On the contrary, resistance to water absorption decreases as a function of the wood fillers. Scanning electron microscopy (SEM) was used to analyze morphological structure alteration when exposed to intense weathering. The biodegradability of bio-composites up to 97 days was also investigated; the results indicate that, by increasing the filler content, the amount of weight loss increased as well. In other words, even though the addition of sawdust to thermoplastic polymer improves the mechanical performance of a composite material, it also accelerates the biodegradation rate of the composite. An optimum amount of filler content might compromise the effect of biodegradation and mechanical properties of composite materials

Effect of Pin Geometry on the Mechanical Strength of Friction-Stir-Welded Polypropylene Composite Plates

Science.gov (United States)

Kordestani, F.; Ashenai Ghasemi, F.; Arab, N. B. M.

2017-09-01

Friction stir welding (FSW) is a solid-state welding process, which has successfully been applied in aerospace and automotive industries for joining materials. The friction stir tool is the key element in the FSW process. In this study, the effect of four different tool pin geometries on the mechanical properties of two types of polypropylene composite plates, with 30% glass and carbon fiber, respectively, were investigated. For this purpose, four pins of different geometry, namely, a threaded-tapered pin, square pin, four-flute threaded pin, and threaded-tapered pin with a chamfer were made and used to carry out the butt welding of 5-mm-thick plates. The standard tensile and Izod impact tests were performed to evaluate the tensile strength and impact toughness of welded specimens. The results indicated that the threaded-tapered pin with a chamfer produced welds with a better surface appearance and higher tensile and impact strengths. The tests also showed that, with the threaded-tapered pin with a chamfer, the impact strength of the glass- and carbon-fiber composite welds were about 40 and 50%, respectively, of that of the base materials.

Study of the effect of ionizing radiation on composites of wood flour in polypropylene matrix using barium titanate as coupling agent; Estudo do efeito da radiacao ionizante em compositos de polipropileno/po de madeira usando titanato de bario como agente de acoplagem

Energy Technology Data Exchange (ETDEWEB)

Ulloa, Maritza Eliza Perez

2007-07-01

The purpose of this work was to study the effects of ionizing radiation on the properties of wood flour composites in polypropylene matrix, using barium titanate as a coupling agent and the reactive monomer tripropylene glycol diacrylate (TPDGA). An electron accelerator was used in the study as the radiation source. The physical properties of virgin compounds and of the polypropylene/wood flour composite, with and without barium titanate and TPDGA addition, were investigated. The composites were developed from the load treatment, which first consisted of incorporating additives to the wood flour reinforcement and after that, the fusion process of polypropylene and composite mixing in a 'calander'. Subsequently, the samples to be irradiated and submitted to thermal and mechanical assays were molded by injection. The mechanical properties (hardness, impact resistance and molten fluidity index (MFI)), as well as the thermal properties (HDT and Vicat) of the composites were determined. The investigated compositions consisted of polypropylene/wood flour, polypropylene/wood flour with barium titanate and polypropylene/wood flour with barium titanate and TPDGA, using different wood flour concentrations of 10 por cent, 15 por cent and 20 por cent in the polypropylene matrix. The samples were separated in groups and irradiated to doses of 10 kGy and 20 kGy in the samples of the essays of traction. Besides these doses, it was also used doses of 15 kGy and 25 kGy to be observed the behavior of the sample of the sample due to the increase of the radiation. These doses were chosen to show that with low doses the composite material presents reticulation, what represents a viable commercial option. There was a reduction of the flow rate for the composites containing wood flour, being this reduction more effective in the presence of TiBa. The superficial treatment using TPDGA monomer influence in the composite samples because it acted as a plastic additive becoming the

Influence of the elastomeric polypropylene addition on the properties of commercial metallocenic polypropylene

Directory of Open Access Journals (Sweden)

Marques Maria de Fátima V.

2001-01-01

Full Text Available Polypropylene with special properties can be obtained by metallocenic catalysts. These catalytic systems represent the beginning of a new age in polyolefins technology. In this work, the influence of the addition of a syndiotactic polypropylene (s-PP on the processability and mechanical properties of a commercial isotactic polypropylene (i-PP obtained by metallocenic catalysts was evaluated. Increasing addition of s-PP promoted better processability, with an increase in the impact strength and a decrease in the stress at break. A reduction of the crystallinity in the polymeric blends was verified. The more significant influence of the s-PP addition was observed for the mi-PP, compared to the ZNi-PP.

Utilization of Delignified Sawdust as Raw Material of Biogas Production

Directory of Open Access Journals (Sweden)

Zumalla Asfarina

2018-01-01

Full Text Available Biogas is one alternative to replace the irreplaceable energy source that has begun to diminish its existence. The raw materials for biogas manufacture are renewable biomass, usually using plantation waste, agriculture, and livestock. Using biogas can also reduce environmental pollution. One of the agricultural waste that has great potential to become the raw material of biogas is teak sawdust. Wood processing industry in Indonesia quite a lot, but wood has a high lignosesluosa content, so it needs the right method to process it. With the delignification of lignin levels on teak sawdust will decrease. Wood sawdust is soaked using NaOH for 1, 2, 3, and 4 days with 4% w / v concentration. The lowest lignin and hemicellulose content was 25.79% and 87.9% in pretreatment for 4 days, while the highest cellulose level was 57, 34%. The accumulated volume of biogas at 1 day pretreatment, ie 709 ml / g TS. Gcms shows the enlarged peak area of methanamine, N-methyl from before pretreatment. The fastest biogas formation (λ in 4 days pretreatment, 1.60403 days and the largest constant A and U variables at 1 day were 914.5903 ml / g TS and 34.59765 ml / g TS.

Rheological properties of molten flax- and Tencel"®-polypropylene composites: Influence of fiber morphology and concentration

International Nuclear Information System (INIS)

Abdennadher, Ahmed; Vincent, Michel; Budtova, Tatiana

2016-01-01

The rheological properties of short fiber reinforced polypropylene were investigated. Flax and Tencel"® are two cellulose based fibers used in this study. Flax fibers are extracted from the bast of plants. They are composed of thin elementary fibers and rigid thick bundles made of elementary fibers “glued” together. Tencel"® is a man-made cellulosic fiber spun from cellulose solution, with a uniform diameter, thin, and flexible. First, fiber dimensions before and after compounding were analyzed. Both types of fibers were broken during compounding. Flax shows larger length and diameter than Tencel"®, but aspect ratio of flax is smaller. The reason is that after compounding flax remained in bundles. Dynamic viscosity, elastic and viscous moduli were studied as a function of fiber type, concentration (from 0 to 30 wt. %), and composite temperature (from 180 to 200 °C). All Tencel"®-based composites showed higher apparent yield stress, viscosity, and moduli compared to flax-based composites at the same fiber concentrations. The results are analyzed in terms of the influence of fiber type, aspect ratio, and flexibility. The importance of considering fiber morphology is demonstrated as far as it controls fiber flexibility and fiber-fiber interactions

Performance comparison of sand and fine sawdust vermifilters in treating concentrated grey water for urban poor.

Science.gov (United States)

Adugna, Amare T; Andrianisa, Harinaivo A; Konate, Yacouba; Ndiaye, Awa; Maiga, Amadou H

2015-01-01

A comparative investigation was conducted for 10 months with sand and fine sawdust vermifilters and a control unit to treat concentrated grey water generated from a poor urban household in Ouagadougou, Burkina Faso. Each of the filters was made up of cylindrical DN200-PVC pipes and filled with 10 cm of gravel at the bottom. On top of the gravel layer, filter 1 (fully sand, F1) was completed with 40 cm of sand and 10 cm of fine sawdust, filter 2 (partially sand, F2) with 20 cm of sand and 30 cm of fine sawdust, respectively, and filter 3 (fully sawdust, F3) and 4 (control, F4) with 50 cm of fine sawdust only. Two hundred Eudrilus eugeniae earthworms were inoculated in each of the vermifilters. The vermifiltration system was supplied with grey water four times per day at a hydraulic loading rate of 64 L/m(2)/day on a batch basis. The removal efficiencies of biological oxygen demand, total chemical oxygen demand, and dissolved chemical oxygen demand (dCOD) by the vermifilters were 25-30% higher than the control, but little differences were observed in terms of total suspended solids and coliform removal efficiencies. Though there was no significant difference in the performance of the three vermifilters (p > 0.05), except for dCOD removal efficiency, the lifespan of F2 and F3 was longer than that of F1. Therefore, fine sawdust can substitute sand as a filter medium in vermifilters.

Spinning, drawing and physical properties of polypropylene nanocomposite fibers with fumed nanosilica

Czech Academy of Sciences Publication Activity Database

Dabrowska, I.; Fambri, L.; Pegoretti, A.; Šlouf, Miroslav; Vacková, Taťana; Kolarik, J.

2015-01-01

Roč. 9, č. 3 (2015), s. 277-290 ISSN 1788-618X R&D Projects: GA ČR(CZ) GA14-17921S Institutional support: RVO:61389013 Keywords : polypropylene * fibers * nanocomposites Subject RIV: JI - Composite Materials Impact factor: 2.965, year: 2015

OPTIMIZATION OF PROCESS PARAMETERS FOR ENHANCED MECHANICAL PROPERTIES OF POLYPROPYLENE TERNARY NANOCOMPOSITES

Directory of Open Access Journals (Sweden)

Oladipupo Olaosebikan Ogunleye

2015-02-01

Full Text Available Preparation of Polypropylene ternary nanocomposites (PPTN was accomplished by blending multiwall carbon nanotube (MWCNT in polypropylene/clay binary system using a melt intercalation method. The effects of MWCNT loadings (A, melting temperature (B and mixing speed (C were investigated and optimized using central composite design. The analysis of the fitted cubic model clearly indicated that A and B were the main factors influencing the tensile properties at a fixed value of C. However, the analysis of variance showed that the interactions between the process parameters, such as; AB, AC, AB2, A2B and ABC, were highly significant on both tensile strength and Young’s modulus enhancement, while no interaction is significant in all models considered for elongation. The established optimal conditions gave 0.17%, 165 °C, and 120 rpm for A, B and C, respectively. These conditions yielded a percentage increase of 57 and 63% for tensile strength and Young’s modulus respectively compared to the virgin Polypropylene used.

The Effect of Size and Crumb Rubber Composition as a Filler with Compatibilizer Pp-G-Ma in Polypropylene Blends and Sir-20 Compound on Mechanical and Thermal Properties

Directory of Open Access Journals (Sweden)

Erna Frida

2013-04-01

Full Text Available Having been researched the development of thermoplastic elastomer material of polypropylene and natural rubber SIR-20 compound with Crumb Rubber as the filler. Reinforced polypropylene with size 60 mesh with 1 mm, and the composition of the Crumb rubber (30, 40, and 50 wt%. Observed mechanical properties are tensile strength, fracture elongation, Young's modulus, tear strength and impact strength. Thermal properties are analyzed by DSC and DTA/TGA. It is acquired that for the size of 60 mesh crumb rubber tensile strength, fracture elongation, Young’s modulus, tear strength and impact strength are bigger than 1mm size. The addition of 60 mesh crumb rubber increases but it decreases by adding of 50 weight%. While for crumb rubber 1 mm tensile strength, fracture elongation, tear strength and impact strength decreas. Based on analysis of DSC that the addition of crumb rubber does not make a difference boiling point significantly between samples containing crumb rubber and polypropylene Analysis TGA/DTA to an increase in enthalpy and decomposition temperature with the addition of crumb rubber used and thermal stability.

Environmental Particle Emissions due to Automated Drilling of Polypropylene Composites and Nanocomposites Reinforced with Talc, Montmorillonite and Wollastonite

Science.gov (United States)

Starost, K.; Frijns, E.; Laer, J. V.; Faisal, N.; Egizabal, A.; Elizextea, C.; Nelissen, I.; Blazquez, M.; Njuguna, J.

2017-05-01

In this study, the effect on nanoparticle emissions due to drilling on Polypropylene (PP) reinforced with 20% talc, 5% montmorillonite (MMT) and 5% Wollastonite (WO) is investigated. The study is the first to explore the nanoparticle release from WO and talc reinforced composites and compares the results to previously researched MMT. With 5% WO, equivalent tensile properties with a 10 % weight reduction were obtained relative to the reference 20% talc sample. The materials were fabricated through injection moulding. The nanorelease studies were undertaken using the controlled drilling methodology for nanoparticle exposure assessment developed within the European Commission funded SIRENA Life 11 ENV/ES/506 project. Measurements were taken using CPC and DMS50 equipment for real-time characterization and measurements. The particle number concentration (of particles <1000nm) and particle size distribution (4.87nm - 562.34nm) of the particles emitted during drilling were evaluated to investigate the effect of the silicate fillers on the particles released. The nano-filled samples exhibited a 33% decrease (MMT sample) or a 30% increase (WO sample) on the average particle number concentration released in comparison to the neat polypropylene sample. The size distribution data displayed a substantial percentage of the particles released from the PP, PP/WO and PP/MMT samples to be between 5-20nm, whereas the PP/talc sample emitted larger particle diameters.

Nuclear magnetic resonance study of the effect of the addition of clay on polypropylene

International Nuclear Information System (INIS)

Nogueira, Regina F.; San Gil, Rosane A.S.; Tavares, Maria Ines B.

2001-01-01

Polypropylene (PP) samples and polypropylene (PP)/clay (M) composite prepared by melting mixing have been characterized by solution and solid state nuclear magnetic resonance spectroscopy (NMR). The monomer sequences distribution and the influence of time and temperature of mechanical mix on the modifications in the PP structure were investigated by 13 C solution NMR. The solid state NMR investigation showed that the 13 C routine spectra such as MAS and CPMAS allowed obtaining information on the molecular domains of chains, and also permits to evaluate the domains mobility. 29 Si and 27 Al solid state NMR were used to characterize the clay and the PP/M composite samples. The results showed that the heating and friction in the range of temperature and time used in the sample preparation did not affect the distribution of configurational sequence in the PP chains. The effect of clay in the PP/M composite structure could be detected, using both 13 C solution and in 29 Si solid state NMR spectra. (author)

Carbothermal Upgrading of the Awaso Bauxite Ore using Sawdust ...

African Journals Online (AJOL)

Michael

2016-12-02

Dec 2, 2016 ... Bauxite Ore using Sawdust and Coconut Shells as Reductant”, Ghana Mining Journal, Vol. 16, No. 2, pp ... The fruit is consumed locally, producing greater volumes .... made into paste by drop-wise addition of water. The paste ...

Effect of the interfacial adhesion on the tensile and impact properties of carbon fiber reinforced polypropylene matrices

Directory of Open Access Journals (Sweden)

Clara Leal Nogueira

2005-03-01

Full Text Available Thermoplastic composites have been applied in a wide variety of industrial products, showing recently a great potential to be used in aeronautical field. The objectives of this work were to evaluate the fiber/matrix interface of carbon fiber reinforced polypropylene-based matrices after tensile and impact tests and also to compare the mechanical test results of the manufactured laminates. The laminates were prepared by stacking carbon fiber fabric style Plain Weave (CF and films of four different polypropylene matrices, described as (a polypropylene-PP, (b polypropylene-polyethylene copolymer-PP-PE, (c PP-PE with an interfacial compatibilizer-AM1 and (d PP-PE containing an elastomeric modifier-AM2. The composites were processed using hot compression molding. The mechanical testing results showed that the CF-AM1 laminate family presented the lowest impact strength and the highest tensile strength values when compared to the other laminates. SEM analysis observations of both tensile and impact fractured specimens of the CF-PP/PE-AM1 specimens revealed a stronger fiber/matrix interface. The CF-PP/PE-AM2 laminate showed a lower tensile strength and higher impact strength values when compared to the CF-PP/PE-AM1 one. PP-PE and PP laminates presented the lowest impact strength values.

Styrene-butadiene-styrene copolymer compatibilized carbon black/polypropylene/polystyrene composites with tunable morphology, electrical conduction and rheological stabilities.

Science.gov (United States)

Song, Yihu; Xu, Chunfeng; Zheng, Qiang

2014-04-21

We report a facile kinetic strategy in combination with styrene-butadiene-styrene (SBS) copolymer compatibilizers for preparing carbon black (CB) filled immiscible polypropylene (PP)/polystyrene (PS) (1/1) blends with finely tuned morphologies and show the important role of location and migration of CB nanoparticles in determining the electrical conductivity and rheological behaviour of the composites. A novel method of mixing a SBS/CB (5/3) masterbatch with the polymers allowed producing composites with CB aggregates dispersed partially in the unfavorable PP phase and partially in the PP side of the interface to exhibit diverse phase connectivity and electrical conductivity depending on the compounding sequences. A cocontinuous morphology with CB enrichment along the interface was formed in the composite prepared by mixing the SBS/CB masterbatch with the premixed PP/PS blend, giving rise to a highest electrical conductivity and dynamic moduli at low frequencies. On the other hand, mixing the masterbatch with one and then with another polymer yielded droplet (PS)-in-matrix (filled PP) composites. The composites underwent phase coalescence and CB redistribution accompanied by marked dynamic electrical conduction and modulus percolations as a function of time during thermal annealing at 180 °C. The composites with the initial droplet-in-matrix morphology progressed anomalously into the cocontinuous morphology, reflecting a common mechanism being fairly nonspecific for understanding the processing of filled multicomponent composites with tailored performances of general concern.

Liquid nitrogen pretreatment of eucalyptus sawdust and rice hull for enhanced enzymatic saccharification.

Science.gov (United States)

Castoldi, Rafael; Correa, Vanesa G; de Morais, Gutierrez Rodrigues; de Souza, Cristina G M; Bracht, Adelar; Peralta, Rosely A; Peralta-Muniz Moreira, Regina F; Peralta, Rosane M

2017-01-01

In this work, liquid nitrogen was used for the first time in the pretreatment of plant biomasses for purposes of enzymatic saccharification. After treatment (cryocrushing), the initial rates of the enzymatic hydrolysis of eucalyptus sawdust and rice hull were increased more than ten-fold. Cryocrushing did not modify significantly the contents of cellulose, hemicellulose and lignin in both eucalyptus sawdust and rice hulls. However, substantial disorganization of the lignocellulosic materials in consequence of the pretreatment could be observed by electron microscopy. Cryocrushing was highly efficient in improving the saccharification of the holocellulose component of the plant biomasses (from 4.3% to 54.1% for eucalyptus sawdust and from 3.9% to 40.6% for rice hull). It is important to emphasize that it consists in a simple operation with low requirements of water and chemicals, no corrosion, no release of products such as soluble phenolics, furfural and hydroxymethylfurfural and no waste generation. Copyright © 2016 Elsevier Ltd. All rights reserved.

Electrical conductivity and physical changes of functionalized carbon nanotube/graphite/stainless steel (SS316L/polypropylene composites immersed in an acidic solution

Directory of Open Access Journals (Sweden)

Hendra Suherman

2018-02-01

Full Text Available Chemical functionalization of carbon nanotubes (CNTs and graphite (G was performed to improve their adhesion to a metal powder (SS316L and a polypropylene (PP matrix. A conductive pathway was thus formed to utilize the high electrical conductivity of the SS316L for conductive polymer composites (CPCs applications. The rheological properties of the feedstock mixture were measured, and samples were formed by injection molding. Fourier transform infrared spectroscopy indicated the existence of functional groups generated by chemical wet oxidation. Only feedstock mixtures containing more than 28 vol% of the PP composite showed a shear rate (102 s -1 to 105 s -1 , shear viscosity (10 Pa·s to 103 Pa·s, and flow behavior index (n<1 suitable for injection molding. The functionalized composites exhibited improved electrical and mechanical properties over the as-produced composites. The functionalized composites containing 28 vol% PP obtained an electrical conductivity of 6 S/m, compared to 0.5 S/m for the as-produced composites.

Radiation crosslinking of polypropylene

International Nuclear Information System (INIS)

Nojiri, A.; Sawasaki, T.

1984-01-01

The radiation crosslinking of polypropylene with several kinds of polyfunctional monomers has been examined, and it has been clarified that the enhanced crosslinking may be classified into two types. In particular, the irradiation crosslinking process of polypropylene containing a polyfunctional monomer having an acryloyloxy group giving a specific gel - dose curve has been studied by infrared absorption spectrum and oxygen absorptivity measurement in comparison with the non-enhanced system. (author)

The effects of H2SO4 and NaOH solutions on irradiated sawdust for ethanol production

International Nuclear Information System (INIS)

Lina, M.R.; Susiana; Siagian, E.G.

1988-01-01

The research of gamma irradiated sawdust, which were added H2SO4 and NaOH solutions on fermentation process for ethanol production was investigated. Irradiation doses used were : 0 and 200 kGy, while H2SO4 and NaOH solutions had concentrations of 0,1 and 2% (v/v) and (b/v), with a ratio of sawdust weight and solution volume = 1:3. Fine powder of sawdust with a mesh of 60, was hydrolysed by enzyme (cellulase), S.cerevisiae was a yeast used for fermentation process and fermentation time was 4 hours. From the experimental results showed that irradiation doses up to 200 kGy, could increase the ethanol concentration from sawdust fermentation signivicantly (P= . Irradiation treatment, addition of the solutions and its interaction could not influence the total carbohydrate before and after fermentation. (author). 9 refs, 2 figs, 6 tabs

Development of Antibacterial Composite Films Based on Isotactic Polypropylene and Coated ZnO Particles for Active Food Packaging

Directory of Open Access Journals (Sweden)

Clara Silvestre

2016-01-01

Full Text Available This study was aimed at developing new films based on isotactic polypropylene (iPP for food packaging applications using zinc oxide (ZnO with submicron dimension particles obtained by spray pyrolysis. To improve compatibility with iPP, the ZnO particles were coated with stearic acid (ZnOc. Composites based on iPP with 2 wt % and 5 wt % of ZnOc were prepared in a twin-screw extruder and then filmed by a calender. The effect of ZnOc on the properties of iPP were assessed and compared with those obtained in previous study on iPP/ZnO and iPP/iPPgMA/ZnO. For all composites, a homogeneous distribution and dispersion of ZnOc was obtained indicating that the coating with stearic acid of the ZnO particles reduces the surface polarity mismatch between iPP and ZnO. The iPP/ZnOc composite films have relevant zinc oxide with respect to E. coli, higher thermal stability and improved mechanical and impact properties than the pure polymer and the composites iPP/ZnO and iPP/iPPgMA/ZnO. This study demonstrated that iPP/ZnOc films are suitable materials for potential application in the active packaging field.

The radiation degradation of polypropylene

International Nuclear Information System (INIS)

De Hollain, G.

1977-04-01

Polypropylene is used extensively in the manufacture of disposable medical devices because of its superior properties. Unfortunately this polymer does not lend itself well to radiation sterilization, undergoing serious degradation which affects the mechanical properties of the polymer. In this paper the effects of radiation on the mechanical and physical properties of polypropylene are discussed. A programme of research to minimize the radiation degradation of this polymer through the addition of crosslinking agents to counteract the radiation degradation is proposed. It is furthermore proposed that a process of annealing of the irradiated polymer be investigated in order to minimize the post-irradiation degradation of the polypropylene [af

Biosorption of Acid Dye in Single and Multidye Systems onto Sawdust of Locust Bean (Parkia biglobosa Tree

Directory of Open Access Journals (Sweden)

Abdur-Rahim Adebisi Giwa

2016-01-01

Full Text Available Properties of raw sawdust of Parkia biglobosa, as a biosorbent for the removal of Acid Blue 161 dye in single, binary, and ternary dye systems with Rhodamine B and Methylene Blue dyes in aqueous solution, were investigated. The sawdust was characterized using Scanning Electron Microscopy, Fourier Transform Infrared spectrophotometry, X-ray diffraction, and pH point of zero charge. Batch adsorption experiments were carried out to determine the equilibrium characteristics, thermodynamics, and kinetics of the sorption processes. The data obtained were subjected to various isotherm and kinetics equations. The results showed that the adsorption processes were described by different isotherm models depending on the composition of the system; they were all spontaneous (ΔG ranges from −0.72 to −5.36 kJ/mol and endothermic (range of ΔH is 11.37–26.31 kJ/mol and with increased randomness with ΔS values of 55.55 and 98.78 J·mol/K for single and ternary systems, respectively. Pseudo-second-order kinetics model gave better fit for all the sorption systems studied irrespective of the differences in composition, with the initial and overall rate constants higher for the mixtures than for the single system (6.76 g·mg−1min−1. The presence of Rhodamine B and Methylene Blue had a synergetic effect on the maximum monolayer capacity of the adsorbent for Acid Blue 161 dye.

The lignin pyrolysis composition and pyrolysis products of palm kernel shell, wheat straw, and pine sawdust

International Nuclear Information System (INIS)

Chang, Guozhang; Huang, Yanqin; Xie, Jianjun; Yang, Huikai; Liu, Huacai; Yin, Xiuli; Wu, Chuangzhi

2016-01-01

Highlights: • The primarily pyrolysis composition of PKS lignin was p-hydroxyphenyl unit. • Higher phenol yield and lower gas energy yield were obtained from PKS pyrolysis. • PKS produced more bio-oil and biochar than WS and PS from pyrolysis at 650–850 °C. • PKS-char had poorer gasification reactivity due to higher ordering carbon degree. - Abstract: The lignin monomer composition of palm kernel shell (PKS) was characterized using pyrolysis-gas chromatography/mass spectrometry (Py-GC/MS), and the characteristics and distributions of products obtained from PKS pyrolysis were investigated using Py-GC/MS, GC, and a specially designed pyrolysis apparatus. The gasification reactivity of PKS biochar was also characterized using thermogravimetry (TG) and Raman spectroscopy. All the results were compared with those obtained from wheat straw (WS) and pine sawdust (PS). The results showed that PKS lignin is primarily composed of p-hydroxyphenyl structural units, while WS and PS lignins are mainly made up of guaiacyl units. Both the mass and energy yields of non-condensable gases from PKS pyrolysis were lower than those obtained from WS and PS pyrolysis at 650–850 °C, owing to the lower volatile content (75.21%) and lack of methoxy groups in PKS. Compared with WS and PS, higher bio-oil productivity was observed during PKS pyrolysis. Phenols were the main component of PKS bio-oil from pyrolysis at 500 °C, and the phenol content of PKS bio-oil (13.49%) was higher than in WS bio-oil (1.62%) and PS bio-oil (0.55%). A higher yield of biochar (on an ash-free basis) was also obtained from PKS pyrolysis. Because of its greater relative degree of ordered carbon, PKS biochar exhibited lower in situ reactivity during CO_2 or H_2O gasification than WS and PS biochars. A longer residence time and addition of steam were found to be beneficial during PKS biochar gasification.

Production of ethanol from cellulose (sawdust)

OpenAIRE

Otulugbu, Kingsley

2012-01-01

The production of ethanol from food such as corn, cassava etc. is the most predominate way of producing ethanol. This has led to a shortage in food, inbalance in food chain, increased food price and indirect land use. This thesis thus explores using another feed for the production of ethanol- hence ethanol from cellulose. Sawdust was used to carry out the experiment from the production of ethanol and two methods were considered: SHF (Separate Hydrolysis and Fermentation) and SSF (Simultaneous...

Emissions of Sesquiterpenes from Spruce Sawdust During Drying

International Nuclear Information System (INIS)

Granstroem, K.M.

2006-01-01

Large amounts of sawdust are dried for production of particleboard and Pellets. During processing of wood (i.e. drying, densification), volatile organic compounds are emitted. These contribute in the presence of nitrogen oxides and sunlight to the formation of ground level ozone and other harmful photo-oxidants. In this study sesquiterpene emissions from the drying of fresh Norway Spruce (Picea abies) sawdust in a continuous spouted bed steam dryer at 140-200 deg C have been investigated, and patterns of covariation between sesquiterpene emissions and drying parameters elucidated. Sesquiterpene emissions was about 20% of the monoterpene emissions. Drying in 200 deg C caused markedly larger sesquiterpene emissions than in 140 deg C or 170 deg C. Whereas a change in moisture content had no notable effect on the amount of sesquiterpenes emitted at high wood moisture contents (25-40%), the sesquiterpene emissions increased considerably as drying proceeded at low wood moisture contents (5-15%). While it has long been known that monoterpenes are a dominant VOC emitted during processing of wood, this study shows that sesquiterpenes are of considerable importance

Interactions of coal gangue and pine sawdust during combustion of their blends studied using differential thermogravimetric analysis.

Science.gov (United States)

Zhang, Yuanyuan; Zhang, Zhezi; Zhu, Mingming; Cheng, Fangqin; Zhang, Dongke

2016-08-01

The interactions between coal gangue and pine sawdust during the combustion process were studied using thermogravimetric analysis. The effect of the blending ratio, oxygen concentration and heating rate on the weight loss (TG) and differential thermogravimetric (TGA) profiles was examined. The TG and DTG curves of the blends were not additives of those of the individual materials, suggesting that interactions between coal gangue and pine sawdust had occurred during the combustion, especially in the temperature range of 400-600°C. Kinetic analysis confirmed that the combustion of coal gangue, pine sawdust and their blends was chemical reaction controlled. Further analysis revealed that the interactions between coal gangue and pine sawdust were primarily due to thermal effects rather than structural changes, with the thermal inertia of coal gangue dominating over the behaviour of the blends. The interactions decreased with decreasing the coal gangue ratio in the blend, oxygen concentration and heating rate. Copyright © 2016 Elsevier Ltd. All rights reserved.

PREPARATION AND CHARACTERIZATION OF COMPOSITES COMPRISING MODIFIED HARDWOOD AND WOOD POLYMERS/POLY(VINYL CHLORIDE

Directory of Open Access Journals (Sweden)

Ruxanda Bodîrlău

Full Text Available Chemical modification of hardwood sawdust from ash-tree species was carried out with a solution of maleic anhydride in acetone. Wood polymers, lignin, and cellulose were isolated from the wood sawdust and modified by the same method. Samples were characterized by Fourier transform infrared spectroscopy (FTIR, providing evidence that maleic anhydride esterifies the free hydroxyl groups of the wood polymer components. Composites comprising chemically modified wood sawdust and wood polymers (cellulose, lignin-as variable weight percentages-, and poly (vinyl chloride were obtained and further characterized by using FTIR spectroscopy and scanning electron microscopy (SEM. The thermal behavior of composites was investigated by using the thermogravimetric analysis (TGA. In all cases, thermal properties were affected by fillers addition.

Influence of polymer swelling and dissolution into food simulants on the release of graphene nanoplates and carbon nanotubes from poly(lactic) acid and polypropylene composite films

OpenAIRE

Velichkova, Hristiana; Petrova, Ivanka; Kotsilkov, Stanislav; Ivanov, Evgeni; Vitanov, Nikolay K.; Kotsilkova, Rumiana

2017-01-01

The study compared the effects of swelling and dissolution of a matrix polymer by food simulants on the release of graphene nanoplates (GNPs) and multiwall carbon nanotubes (MWCNTs) from poly(lactic) acid (PLA) and polypropylene (PP) composite films. The total migration was determined gravimetrically in the ethanol and acetic acid food simulants at different time and temperature conditions, while migrants were detected by laser diffraction analysis and transmission electron microscopy. Swelli...

Permeation Tests on Polypropylene Fiber Materials

Science.gov (United States)

2018-03-16

Permeation Tests on Polypropylene Fiber Materials Brandy J. White Martin H. Moore Brian J. Melde Laboratory for the Study of Molecular Interfacial...ABSTRACT Permeation Tests on Polypropylene Fiber Materials Brandy J. White, Martin H. Moore, Brian J. Melde Center for Bio/Molecular Science

Green aqueous surface modification of polypropylene for novel polymer nanocomposites.

Science.gov (United States)

Thakur, Vijay Kumar; Vennerberg, Danny; Kessler, Michael R

2014-06-25

Polypropylene is one of the most widely used commercial commodity polymers; among many other applications, it is used for electronic and structural applications. Despite its commercial importance, the hydrophobic nature of polypropylene limits its successful application in some fields, in particular for the preparation of polymer nanocomposites. Here, a facile, plasma-assisted, biomimetic, environmentally friendly method was developed to enhance the interfacial interactions in polymer nanocomposites by modifying the surface of polypropylene. Plasma treated polypropylene was surface-modified with polydopamine (PDA) in an aqueous medium without employing other chemicals. The surface modification strategy used here was based on the easy self-polymerization and strong adhesion characteristics of dopamine (DA) under ambient laboratory conditions. The changes in surface characteristics of polypropylene were investigated using FTIR, TGA, and Raman spectroscopy. Subsequently, the surface modified polypropylene was used as the matrix to prepare SiO2-reinforced polymer nanocomposites. These nanocomposites demonstrated superior properties compared to nanocomposites prepared using pristine polypropylene. This simple, environmentally friendly, green method of modifying polypropylene indicated that polydopamine-functionalized polypropylene is a promising material for various high-performance applications.

Heat Energy From Value-Added Sawdust Briquettes Of Albizia Zygia ...

African Journals Online (AJOL)

Choice-Academy

... physical properties between the sawdust briquettes and the solid wood of the same species were carried out. The results ... kerosene and cooking gas in Nigeria, draw attention to the .... between the physical properties of solid wood used for ...

Scavenging behaviour of meranti sawdust in the removal of methylene blue from aqueous solution

International Nuclear Information System (INIS)

Ahmad, A.; Rafatullah, M.; Sulaiman, O.; Ibrahim, M.H.; Hashim, R.

2009-01-01

Meranti (Philippine mahogany) sawdust, an inexpensive material, showed strong scavenging behaviour through adsorption for the removal of methylene blue (MB) from aqueous solution. Batch studies were performed to evaluate and optimize the effects of various parameters such as contact time, pH, initial dye concentrations and adsorbent dosage. Langmuir, Freundlich and Temkin isotherms were used to analyze the equilibrium data at different temperatures. The experimental data fitted well with the Langmuir adsorption isotherm, indicating thereby the mono layer adsorption of the dye. The monolayer sorption capacity of meranti sawdust for MB was found to be 120.48, 117.64, 149.25 and 158.73 mg/g at 30, 40, 50 and 60 deg. C, respectively. Thermodynamic calculations showed that the MB adsorption process is endothermic and spontaneous in nature. Kinetic studies showed that the adsorption followed a pseudo-second-order kinetic model. The results indicated that the meranti sawdust could be an alternative material in place of more costly adsorbents used for dye removal.

Assessment of hydrothermal carbonization and coupling washing with torrefaction of bamboo sawdust for biofuels production.

Science.gov (United States)

Zhang, Shuping; Su, Yinhai; Xu, Dan; Zhu, Shuguang; Zhang, Houlei; Liu, Xinzhi

2018-06-01

Two kinds of biofuels were produced and compared from hydrothermal carbonization (HTC) and coupling washing with torrefaction (CWT) processes of bamboo sawdust in this study. The mass and energy yields, mass energy density, fuel properties, structural characterizations, combustion behavior and ash behavior during combustion process were investigated. Significant increases in the carbon contents resulted in the improvement of mass energy density and fuel properties of biofuels obtained. Both HTC and CWT improved the safety of the biofuels during the process of handling, storing and transportation. The ash-related issues of the biofuels were significantly mitigated and combustion behavior was remarkably improved after HTC and CWT processes of bamboo sawdust. In general, both HTC and CWT processes are suitable to produce biofuels with high fuel quality from bamboo sawdust. Copyright © 2018 Elsevier Ltd. All rights reserved.

Effects of sawdust and organo mineral fertilizer and their residual effect on the yield of maize on degrades soil

International Nuclear Information System (INIS)

Dania, S.O.; Fagbola, O.; Isitekhale, H.H.E.

2012-01-01

Conventional mineral fertilizer alone cannot sustain arable crop production in soil which top layer has been eroded hence it is necessary to employ the application of organic base fertilizer. A greenhouse experiment was conducted to investigate the effects of sawdust, organo mineral fertilizer and their residual effects on the growth and yield of maize. Organo mineral fertilizer is the combination of organic manure and mineral fertilizer. Simulated degraded soil was used and the experimental design was a 2 x 2 x 3 factorial in a completely randomized design with three replicates. The factors investigated were: two levels of organo mineral fertilizer (with and without), two levels of soil amendment (with and without sawdust) and three levels of application methods. The methods of organo mineral fertilizer used were ring, subsurface and mixed methods. The amendment of soil to sawdust was ratio 1:1 by volume. The growth and yield of maize was significantly (p = 0.05) higher in non-amended soil with OMF under different application methods compared to soil amended with sawdust with or without OMF application. Ring method of application of OMF in non-amended soil significantly increased the growth and yield of maize compared to other methods of OMF application. The residual effect of OMF and sawdust on the growth and yield of maize was significantly higher in non-amended soil with OMF under different application methods compared to soil amended with sawdust. Addition of sawdust to soil does not improve the growth and yield of maize with or without OMF and under different application methods. Organo mineral fertilizer using ring and subsurface application methods has a beneficial effect in improving the growth and yield of maize in degraded soil where the top layer has been eroded. (author)

Effects of sawdust and organo mineral fertilizer and their residual effect on the yield of maize on degraded soil

International Nuclear Information System (INIS)

Dania, S.O.; Fagbola, O.

2012-01-01

Conventional mineral fertilizer alone cannot sustain arable crop production in soil which top layer has been eroded hence it is necessary to employ the application of organic base fertilizer. A greenhouse experiment was conducted to investigate the effects of sawdust, organo mineral fertilizer and their residual effects on the growth and yield of maize. Organo mineral fertilizer is the combination of organic manure and mineral fertilizer. Simulated degraded soil was used and the experimental design was a 2 x 2 x 3 factorial in a completely randomized design with three replicates. The factors investigated were: two levels of organo mineral fertilizer (with and without), two levels of soil amendment (with and without sawdust) and three levels of application methods. The methods of organo mineral fertilizer used were ring, subsurface and mixed methods. The amendment of soil to sawdust was ratio 1: 1 by volume. The growth and yield of maize was significantly (p = 0.05) higher in non-amended soil with OMF under different application methods compared to soil amended with sawdust with or without OMF application. Ring method of application of OMF in non-amended soil significantly increased the growth and yield of maize compared to other methods of OMF application. The residual effect of OMF and sawdust on the growth and yield of maize was significantly higher in non-amended soil with OMF under different application methods compared to soil amended with sawdust. Addition of sawdust to soil does not improve the growth and yield of maize with or without OMF and under different application methods. Organo mineral fertilizer using ring and subsurface application methods has a beneficial effect in improving the growth and yield of maize in degraded soil where the top layer has been eroded. (author)

Amendment of crude oil contaminated soil with sawdust and ...

African Journals Online (AJOL)

GRACE

2006-05-02

May 2, 2006 ... Akonye LA, Onwudiwe IO (2004). Potential for Sawdust and. Chromolaena leaves as soil amendments for plants growth in an oil polluted soil. Niger Delta Biologia 4: 50-60. Chen ZS Lee DY (1997). Evaluation of remediation technique on two. Cadmiun polluted soil contaminated with metals. North word.

GEOTECHNICAL CHARACTERISTICS OF LATERITIC SOIL STABILIZED WITH SAWDUST ASH-LIME MIXTURES

Directory of Open Access Journals (Sweden)

Emeka Segun Nnochiri

2017-04-01

Full Text Available This study assesses the geotechnical characteristics of lateritic soil and sawdust ash lime (SDAL mixtures. Preliminary tests were carried out on the natural soil sample for identification and classification purposes. The sawdust was mixed with lime for stabilization in the ratio 2:1. This mixture was thereafter added to the lateritic soil in varying proportions of 2, 4, 6, 8 and 10% by weight of soil. Addition of SDAL increased values of Optimum Moisture Content (OMC from 17.0% at 0% SDAL to 26.5% at 10% SDAL by weight of soil, also, values of Maximum Dry Density (MDD decreased from 2040 kg/m3 at 0% SDAL to 1415 kg/m3 at 10% SDAL. Values of Unconfined Compressive Strength (UCS increased from 38.58 kN/m2 at 0% SDAL to highest value of 129.63 kN/m2 at 6% SDAL. The values of liquid limits and plasticity index of the soil were effectively reduced with the addition of the SDAL, from 54.0% at 0% SDAL to 49.0% at 10% SDAL and from 13.7% at 0% SDAL to 12.5% at 10% SDAL respectively. It was therefore concluded that the sawdust ash lime (SDAL mixture can serve as a cheap soil stabilizing agent for poor lateritic soil.

Antifriction basalt-plastics based on polypropylene

Science.gov (United States)

Bashtannik, P. I.; Ovcharenko, V. G.

1997-05-01

A study is made of the dependence of the mechanical and friction-engineering properties of polypropylene reinforced with basalt fibers on the viscosity of the polymer matrix. It is established that the main factors that determine the mechanical properties of the plastics are the quality of impregnation of the fibers by the binder and the residual length of the reinforcing filler in the composite after extrusion and injection molding. The material that was developed has a low friction coefficient and low rate of wear within a relatively brood range of friction conditions. The basalt-plastics can be used in the rubbing parts of machines and mechanisms subjected to dry friction.

Sono-chemical synthesis of cellulose nanocrystals from wood sawdust using Acid hydrolysis.

Science.gov (United States)

Shaheen, Th I; Emam, Hossam E

2018-02-01

Cellulose nanocrystal (CNC) is a unique material obtained from naturally occurring cellulose fibers. Owing to their mechanical, optical, chemical, and rheological properties, CNC gained significant interest. Herein, we investigate the potential of commercially non-recyclable wood waste, in particular, sawdust as a new resource for CNC. Isolation of CNC from sawdust was conducted as per acid hydrolysis which induced by ultrasonication technique. Thus, sawdust after being alkali delignified prior sodium chlorite bleaching, was subjected to sulfuric acid with concentration of 65% (w/w) at 60 ° C for 60min. After complete reaction, CNC were collected by centrifugation followed by dialyzing against water and finally dried via using lyophilization technique. The CNC yield attained values of 15% from purified sawdust. Acid hydrolysis mechanism exactly referred that, the amorphous regions along with thinner as well as shorter crystallites spreaded throughout the cellulose structure are digested by the acid leaving CNC suspension. The latter was freeze-dried to produce CNC powder. A thorough investigation pertaining to nanostructural characteristics of CNC was performed. These characteristics were monitored using TEM, SEM, AFM, XRD and FTIR spectra for following the changes in functionality. Based on the results obtained, the combination of sonication and chemical treatment was great effective in extraction of CNC with the average dimensions (diameter×length) of 35.2±7.4nm×238.7±81.2nm as confirmed from TEM. Whilst, the XRD study confirmed the crystal structure of CNC is obeyed cellulose type I with crystallinity index ∼90%. Cellulose nanocrystals are nominated as the best candidate within the range studied in the area of reinforcement by virtue of their salient textural features. Copyright © 2017 Elsevier B.V. All rights reserved.

Morphology of Thermoplastic Elastomers:Stereoblock Polypropylene

Energy Technology Data Exchange (ETDEWEB)

Pople, John A

2002-08-06

The morphologies of low-density (0.86 g/cm{sup 3}), elastomeric polypropylene (ePP) derived from bis(2-arylindenyl) hafnium dichloride were investigated using a combination of polarized optical microscopy (OM), differential scanning calorimetry (DSC), wide angle X-ray scattering (WAXS), Fourier transform infrared (FT-IR) spectroscopy, and tapping mode atomic force microscopy (TMAFM). These low-crystallinity polypropylenes, when crystallized isothermally from the melt, exhibit morphologies reminiscent of classical semi-crystalline polymers. The presence of lamellae, cross-hatching, hedrites, and spherulites was revealed by high resolution TM-AFM. These elastomeric polypropylenes can be fractionated into components of different average tacticities and crystallinities, but similar molecular mass. The analysis of the morphologies of all of the fractions revealed both large hierarchical structures and cross-hatching typical of the {alpha}-modification of crystalline isotactic polypropylene for all but the lowest crystalline ether soluble fraction. Evidence for high-melting crystals in all of the fractions are most consistent with a stereoblock microstructure of atactic and isotactic sequences.

Characteristics of Sawdust and Cocopeat Beddings, and Their Usefulness According to the Fan and Pen Location for Rearing Hanwoo Cattle.

Science.gov (United States)

Ahn, Gyu Chul; Jang, Sun Sik; Lee, Kang Yeon; Kwak, Wan Sup; Oh, Young Kyun; Park, Keun Kyu

2016-03-01

This study was designed to examine the characteristics of sawdust and cocopeat bedding materials, including physicochemical properties (Exp. I) and on-farm trial (Exp. II). In Exp. I, the proportion of particle size was in the order of sawdust> cocopeat India>cocopeat Vietnam (pcocopeat Vietnam>sawdust (pfan (blowing 2.00 m/s) and no fan treatments, and feed bunk side (FB) and water supply side (WS) within a pen (4.5 m, width×9.0 m, length). Beddings were replaced with fresh bedding materials when moisture concentrations were over 65%. No interactions among treatments were detected for moisture concentration and increment rates, and ammonia concentrations, but a significant effect was observed (pfan than with fan. Moisture concentrations and increment rate within a pen were also higher (pfan-FB and sawdust-fan-FB were replaced with fresh bedding material between 4 to 5 experimental weeks. The ammonia concentrations and pH of beddings were not significantly different among treatments. Therefore, using cocopeat bedding with a blowing fan can extend twice the bedding utilization period, and WS within a pen showed twice the bedding-life compared to FB. Despite the outstanding characteristics of cocopeat compared with sawdust, using cocopeat as an alternative for sawdust bedding is not recommended for cattle management, considering it has 4.4 times higher bedding cost and a dust production problem.

Determination of the efficiency of sawdust and coco fiber used as Biofilter for pollutant removal for the treatment of wastewater

Directory of Open Access Journals (Sweden)

Jimmy Vicente Reyes

2016-09-01

Full Text Available Water is a resource used by mankind for industrial and domestic needs, which once used, is discharged into the public sewer system or septic tanks. This project proposes an ecological alternative for the treatment of wastewater from domestic use named Biofilter, which is built of living material (worms and inert material (chip and gravel, which filters the wastewater; the biological filter has shown high efficiency in the removal of organic matter and pathogens. The field work was carried out with experimental biological filters, to ascertain the best composition of inert material, different variants were used. Two experimental Biofilters, one using sawdust and the other coco fiber were used in the treatment of domestic wastewater; treated samples from each reactor were subjected to laboratory analysis. The analysis and interpretation of results showed that the Biofilter using sawdust removed 53.53 % of pollutants and is outside the required norm for wastewater treatment and the Biofilter using coco fiber removed 82.37 % of contaminants and is within the Environmental Quality Norm and Effluent Discharge: Water Resource.

Influence of Sawdust as an Aggregate in the Production of Interlocking Pavers

Directory of Open Access Journals (Sweden)

Olayiwola Olaleye AJALA

2017-03-01

Full Text Available The study was conducted to determine the effect of incorporating sawdust into the production of interlocking pavers. Sawdust, stone dust, cement and sharp-sand were combined in different mixing ratios of 2:4:2:0, 2:3:2:1, 2:2:2:2, 3:1:2:2 and 0:3:2:3 respectively with five replicates of each treatment. The interlocking pavers produced were tested for weight, density, hardness, compressive and impact strength. The Analysis of Variance was conducted to test the significance of the strength properties of the pavers produced. The results showed that pavers produced with mixing ratio 0:3:2:3 has the highest mean density and mean compressive strength at 1.58kg/m3 and 4.72N/mm2 respectively, closely followed by ratio 2:2:2:2 which has the highest mean impact strength at 4.39J, compressive strength of 3.26N/mm2 , hardness of 1.70kg and mean density of 1.20kg/m3 . However there is no significant difference in the interlocking pavers’ degree of resistance to abrasion (hardness. It can be concluded that optimum replacement of aggregates exists in ratio 2:2:2:2 where 25% of sawdust can be utilized in each unit of interlocking paver.

Study of the rice husk ash utilization as filler polypropylene matrix and ionization radiation effect on this composite; Estudos da utilizacao da cinza de casca de arroz como carga em matriz de polipropileno e do efeito da radiacao ionizante sobre este composito

Energy Technology Data Exchange (ETDEWEB)

Alfaro, Eduardo de Faria

2010-07-01

In the first step of this work, it was evaluated the possibility of using rice husk ash as a filler in polypropylene (PP) making a comparison with talc which is the most used mineral filler in polymers. This comparison was made by using polypropylene with 20% rice husk ash as well as polypropylene with 20% talc measuring their properties. Despite the properties of the PP with 20% rice husk ash decreased compared with the composite of polypropylene with 20% talc it can be said that the rice husk ash can be used as filler for or other utilization less noble of PP . This way it is being given a destination for this residue that it is disposable in the environment contributing to its preservation, moreover reducing the product cost. This work had also as an aim to study the ionizing radiation effect in the properties of these composites. It was used the coupling agent, maleic anhydride , to verify a best sample homogenization. According to the results it can be said that PP is a semicrystalline polymer, and so it has its morphology modified when exposed to the irradiation process. This fact is due to the scission mechanisms of the polymeric chains which it is in compliance to the literature. (author)

Controlled drug release from a novel injectable biodegradable microsphere/scaffold composite based on poly(propylene fumarate).

Science.gov (United States)

Kempen, Diederik H R; Lu, Lichun; Kim, Choll; Zhu, Xun; Dhert, Wouter J A; Currier, Bradford L; Yaszemski, Michael J

2006-04-01

The ideal biomaterial for the repair of bone defects is expected to have good mechanical properties, be fabricated easily into a desired shape, support cell attachment, allow controlled release of bioactive factors to induce bone formation, and biodegrade into nontoxic products to permit natural bone formation and remodeling. The synthetic polymer poly(propylene fumarate) (PPF) holds great promise as such a biomaterial. In previous work we developed poly(DL-lactic-co-glycolic acid) (PLGA) and PPF microspheres for the controlled delivery of bioactive molecules. This study presents an approach to incorporate these microspheres into an injectable, porous PPF scaffold. Model drug Texas red dextran (TRD) was encapsulated into biodegradable PLGA and PPF microspheres at 2 microg/mg microsphere. Five porous composite formulations were fabricated via a gas foaming technique by combining the injectable PPF paste with the PLGA or PPF microspheres at 100 or 250 mg microsphere per composite formulation, or a control aqueous TRD solution (200 microg per composite). All scaffolds had an interconnected pore network with an average porosity of 64.8 +/- 3.6%. The presence of microspheres in the composite scaffolds was confirmed by scanning electron microscopy and confocal microscopy. The composite scaffolds exhibited a sustained release of the model drug for at least 28 days and had minimal burst release during the initial phase of release, as compared to drug release from microspheres alone. The compressive moduli of the scaffolds were between 2.4 and 26.2 MPa after fabrication, and between 14.9 and 62.8 MPa after 28 days in PBS. The scaffolds containing PPF microspheres exhibited a significantly higher initial compressive modulus than those containing PLGA microspheres. Increasing the amount of microspheres in the composites was found to significantly decrease the initial compressive modulus. The novel injectable PPF-based microsphere/scaffold composites developed in this study

Thermal Properties, Structure and Morphology of Graphene Reinforced Polyethylene Terephthalate/ Polypropylene Nano composites

International Nuclear Information System (INIS)

Inuwa, I.M.; Hassan, A.; Shamsudin, S.A.

2014-01-01

In this work the thermal properties, structure and morphology of a blend of polyethylene terephthalate (PET) and polypropylene (PP) reinforced with graphene nano platelets (GNP) were investigated. A blend of PET/ PP (70/ 30 weight percent) compatibilized with styrene-ethylene-butylene-styrene grafted maleic anhydride triblock copolymer (10 phr) were fabricated by melt extrusion process in a twin screw extruder. The effective thermal conductivity of the nano composites increased as a function of the GNP concentration. More than 80 % increase in effective thermal conductivity was observed for the 7 phr reinforced sample compared to the neat blend. This observation was attributed to the development interconnected GNP sheets which formed heat conductive bridges that are suitable for maximum heat transfer. However, in the case of thermal stability which is a function of dispersibility of GNP in polymer matrix, the maximum increase was observed at 3 phr GNP loading which could be attributed to the uniform dispersion of GNPs in the matrix. It is explained that the GNP nano fillers migrated to the surface of matrix forming an effective oxygen barrier due to char formation. Morphological studies revealed uniform dispersion graphene in the polymer matrix at 3 phr GNP loading along with isolated instances of exfoliation of the graphene layers. (author)

Nanocomposites of polypropylene and organophilic clay: X ray diffraction, absorption infrared spectroscopy with fourier transform and water vapor permeation

International Nuclear Information System (INIS)

Morelli, Fernanda C.; Ruvolo Filho, Adhemar

2010-01-01

In this work nano composites were prepared from polypropylene, graft polypropylene with maleic anhydride as compatibilizer and organophilic montmorillonite Cloisite 20A with concentrations of 1.5, 2.5, 5.0 and 7.5% clay. The mixture was made in the melt state using a twin screw extruder. The materials were characterized by X ray diffraction, infrared spectroscopy with Fourier transform and analysis of water vapor permeation. The results of X ray diffraction and absorption infrared spectroscopy indicates the formation of nano composites with structures probably exfoliate and or intercalated for concentrations of 1.5 and 2.5% clay, and provided a marked decrease in the water permeability, corroborating with other analyses. (author)

Influence of alkaline treatment and fiber loading on the physical and mechanical properties of kenaf/polypropylene composites for variety of applications☆

Institute of Scientific and Technical Information of China (English)

Majid Niaz Akhtar; Abu Bakar Sulong; M.K. Fadzly Radzi; N.F. Ismail; M.R. Raza; Norhamidi Muhamad; Muhammad Azhar Khan

2017-01-01

Due to current trend and increasing interest towards natural based fiber products, Kenaf (Hibiscus cannabinus) fibers have been used for the developments of many products. Therefore, Kenaf fiber-reinforced composites have been widely used in engineering and industrial applications. The present work deals with the fabricating and characterization of untreated and treated kenaf/polypropylene (PP)-reinforced composites. Composites of PP reinforced with treated and untreated kenaf fibers were fabricated using the injection molding technique. Different fiber loadings of 10, 20, 30, 40, 50 wt%treated and untreated kenaf composites were also prepared. X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy and thermo gravimetric analysis (TGA) were performed on the treated, untreated kenaf fibers and kenaf/PP composites. Moreover, the alkaline-treated kenaf composites exhibit better physical, morphological, and mechanical properties because of the compatibility of kenaf with PP. However, variations in tensile and flexural properties depend on treatment and kenaf fiber contents. The percentage increase in the mechanical properties of the treated kenaf/PP composites relative to that of PP was also measured. In addition, 40 wt%kenaf fiber loading resulted in higher mechanical properties. By contrast, kenaf/PP composite with 50%fiber loading was not successfully prepared because of improper mixing and the burning of kenaf fibers in the PP matrix. To conclude, 40%kenaf/PP composites with superior physical and mechanical properties may be used in variety of applications such as automotive, sports, construction, animal bedding, and mass production industries.

A comparison of sawdust and wood shavings as litter materials for ...

African Journals Online (AJOL)

-Amponsem, A Osei-Somuah. Abstract. The suitability of sawdust as litter material for broilers was assessed by comparing broiler performance on it with performance on wood shavings in a 49-day trial. Criteria for assessment included body ...

Effect of Multiwalled Carbon Nanotubes on the Mechanical Properties of Carbon Fiber-Reinforced Polyamide-6/Polypropylene Composites for Lightweight Automotive Parts

Directory of Open Access Journals (Sweden)

Huu-Duc Nguyen-Tran

2018-03-01

Full Text Available The development of lightweight automotive parts is an important issue for improving the efficiency of vehicles. Polymer composites have been widely applied to reduce weight and improve mechanical properties by mixing polymers with carbon fibers, glass fibers, and carbon nanotubes. Polypropylene (PP has been added to carbon fiber-reinforced nylon-6 (CF/PA6 composite to achieve further weight reduction and water resistance. However, the mechanical properties were reduced by the addition of PP. In this research, multiwalled carbon nanotubes (CNTs were added to compensate for the reduced mechanical properties experienced when adding PP. Tensile testing and bending tests were carried out to evaluate the mechanical properties. A small amount of CNTs improved the mechanical properties of carbon fiber-reinforced PA6/PP composites. For example, the density of CF/PA6 was reduced from 1.214 to 1.131 g/cm3 (6.8% by adding 30 wt % PP, and the tensile strength of 30 wt % PP composite was improved from 168 to 173 MPa (3.0% by adding 0.5 wt % CNTs with small increase of density (1.135 g/cm3. The developed composite will be widely used for lightweight automotive parts with improved mechanical properties.

Effects of Polypropylene Orientation on Mechanical and Heat Seal Properties of Polymer-Aluminum-Polymer Composite Films for Pouch Lithium-Ion Batteries

Directory of Open Access Journals (Sweden)

Fangxinyu Zeng

2018-01-01

Full Text Available In this study, polyamide-aluminum foil-polypropylene (PA-Al-PP composite films with different orientation status of the PP layer were prepared, and their morphology, tensile, peeling and heat seal behavior were studied. The comparative study of tensile and fracture behaviors of single-layer film of PA, Al and PP, as well as the composite films of PA-Al, PP-Al and PA-Al-PP revealed that in PA-Al-PP composite film, the PA layer with the highest tensile strength can share the tensile stress from the Al layer during stretching, while the PP layer with the lowest tensile strength can prevent further development of the small cracks on boundary of the Al layer during stretching. Moreover, the study of heat seal behavior suggested that both the orientation status and the heat seal conditions were important factors in determining the heat seal strength (HSS and failure behavior of the sample. Four failure types were observed, and a clear correspondence between HSS and failure types was found. The results also elucidated that for the composite film, only in the cases where the tensile stress was efficiently released by each layer during HSS measurement could the composite film exhibit desired high HSS that was even higher than its tensile strength.

Selective laser vaporization of polypropylene sutures and mesh

Science.gov (United States)

Burks, David; Rosenbury, Sarah B.; Kennelly, Michael J.; Fried, Nathaniel M.

2012-02-01

Complications from polypropylene mesh after surgery for female stress urinary incontinence (SUI) may require tedious surgical revision and removal of mesh materials with risk of damage to healthy adjacent tissue. This study explores selective laser vaporization of polypropylene suture/mesh materials commonly used in SUI. A compact, 7 Watt, 647-nm, red diode laser was operated with a radiant exposure of 81 J/cm2, pulse duration of 100 ms, and 1.0-mm-diameter laser spot. The 647-nm wavelength was selected because its absorption by water, hemoglobin, and other major tissue chromophores is low, while polypropylene absorption is high. Laser vaporization of ~200-μm-diameter polypropylene suture/mesh strands, in contact with fresh urinary tissue samples, ex vivo, was performed. Non-contact temperature mapping of the suture/mesh samples with a thermal camera was also conducted. Photoselective vaporization of polypropylene suture and mesh using a single laser pulse was achieved with peak temperatures of 180 and 232 °C, respectively. In control (safety) studies, direct laser irradiation of tissue alone resulted in only a 1 °C temperature increase. Selective laser vaporization of polypropylene suture/mesh materials is feasible without significant thermal damage to tissue. This technique may be useful for SUI procedures requiring surgical revision.

Origin of toughness in .beta.-polypropylene: the effect of molecular mobility in the amorphous phase

Czech Academy of Sciences Publication Activity Database

Policianová, Olivia; Hodan, Jiří; Brus, Jiří; Kotek, Jiří

2015-01-01

Roč. 60, 9 March (2015), s. 107-114 ISSN 0032-3861 R&D Projects: GA ČR(CZ) GA13-29009S Institutional support: RVO:61389013 Keywords : isotactic polypropylene * β-modification * toughness Subject RIV: JI - Composite Materials Impact factor: 3.586, year: 2015

Polypropylene fumarate/phloroglucinol triglycidyl methacrylate blend for use as partially biodegradable orthopaedic cement.

Science.gov (United States)

Jayabalan, M; Thomas, V; Rajesh, P N

2001-10-01

Polypropylene fumarate/phloroglucinol triglycidyl methacrylate oligomeric blend-based bone cement was studied. Higher the percentage of phloroglucinol triglycidyl methacrylate, lesser the setting time. An optimum setting time could be arrived with 50:50 blend composition of the two oligomers. Composite cement of 50:50 blend prepared with hydroxyapatite granules of particle size 125 microm binds bovine rib bones. The tensile strength of this adhesive bond was found to be 1.11 kPa. The thermal studies suggest the onset of cross-linking reaction in the cured blend if the blend is heated. The absence of softening endotherm in the cured blend shows the thermosetting-like amorphous nature of blend system, which may restrict the changes in creep properties. The in vitro biodegradation studies reveal possible association of calcium ions with negatively charged units of degrading polymer chain resulting in slow down of degradation. Relatively slow degradation was observed in Ringer's solution. The study reveals the potential use of polypropylene fumarate/phloroglucinol triglycidyl methacrylate as partially degradable polymeric cement for orthopaedic applications.

Mechanical properties, morphology and thermal degradation of a biocomposite of polypropylene and curaua fibers: coupling agent effect

Directory of Open Access Journals (Sweden)

Barbara Mano

2013-01-01

Full Text Available Biocomposites of polymers with vegetal fibers have a broad spectrum of applications due to their high specific properties in comparison to their counterparts made with fiberglass. Polypropylene, PP, composites with curaua fiber compatibilized with different concentrations of maleic anhydride grafted polypropylene, PP-g-MA, were characterized according to their mechanical properties, morphologies and thermal stabilities in oxidative and inert atmospheres. The composites were prepared by single screw extrusion and injection molded specimens were used for testing. The composite with 20 wt % of curaua fiber with and without compatibilizer presented improved mechanical properties compared to pure PP. The use of PP-g-MA as a compatibilizer significantly increased fiber/matrix adhesion, however, the mechanical properties were only slightly improved in comparison with composites without compatibilizer. We observed an improvement in thermal stability of the composites, compared to that expected from the weighted average of the individual components, both under inert and oxidative atmospheres. Furthermore, the thermal stability improved under inert atmosphere as a function of the concentration of compatibilizer. In this situation, indeed, there was a different shift of the weight loss processes owing to the presence of the compatibilizer.

Plasma modification of polypropylene surfaces and its alloying with styrene in situ

Energy Technology Data Exchange (ETDEWEB)

Ma Guiqiu, E-mail: magq@tju.edu.cn [School of Materials Science and Engineering, Tianjin Key Laboratory of Composite and Functional Materials, Tianjin University, Tianjin, 300072 (China); Liu Ben; Li Chen; Huang Dinghai; Sheng Jing [School of Materials Science and Engineering, Tianjin Key Laboratory of Composite and Functional Materials, Tianjin University, Tianjin, 300072 (China)

2012-01-15

The treatment of polypropylene surfaces has been studied by dielectric barrier discharges plasma of Ar. The structure and morphology of polypropylene surfaces of Ar plasma modification are characterized by X-ray photoelectron spectroscopy, Fourier transform infrared spectrometers and scanning electron microscope. The modified by plasma treatment of iPP (isotactic polypropylene) surface properties have been examined in a determination of free radicals. The modified active surfaces of polypropylene can induce grafting copolymerization of styrene onto polypropylene. The structure of grafting copolymer is characterized and the grafting percent of styrene onto polypropylene is calculated. The homopolymer of styrene can be formed under grafting copolymerization of styrene onto polypropylene, which follows that the alloying of polypropylene with styrene is achieved in situ.

Combination of sawdust from teak wood and rice husk activated carbon as adsorbent of Pb(II) ion and its analysis using solid-phase spectrophotometry (sps)

Science.gov (United States)

Saputro, S.; Mahardiani, L.; Wulandari, D. A.

2018-03-01

This research aimed to know the usage of sawdust of teak wood and rice husk waste as Pb (II) ion adsorbents in simulated liquid waste, the combined optimum mass required adsorbent to adsorb Pb(II) ion, the sensitivity of the solid-phase spectrophotometry (sps) method in determining the decrease of Pb (II) metal ion levels in the μg/L level. This research was conducted by experimental method in laboratory. Adsorbents used in this study were charcoal of sawdust sawdust activated using 15% ZnCl2 solution and activated rice husk using 2 N NaOH solution. The adsorption processes of sawdust and rice husk with Pb(II) solution was done by variation of mass combination with a ratio of 1: 0; 0: 1; 1: 1; 1: 2; and 2: 1. Analysis of Pb(II) ion concentration using SPS and characterization of sawdust and rice husk adsorbent ads using FTIR. The results showed that activated charcoal from sawdust of teak wood and rice husks can be used as Pb (II) metal ion adsorbents with adsorption capacity of 0.86 μg/L, charcoal from sawdust of teak wood and rice husk adsorbent with a combination of optimum mass contact of sawdust and rice husk is 2:1 as much as 3 grams can adsorb 42.80 μg/L. Solid-phase spectophotometry is a sensitive method for analysis of concentration decreasing levels of Pb(II) ion, after it was absorbed by sawdust of teak wood and rice husk with high sensitivity and has the limit of detection (LOD) of 0.06 μg/L.

Extraction of Micro- and Nano-Fibrils from Nylon 6/Polypropylene Grafted with Maleic Anhydride/Polypropylene Blended Films

Directory of Open Access Journals (Sweden)

E. Bagheban Kochak

2013-01-01

Full Text Available Atechnical feasibility study has been conducted on production of nano- and micro-fibrils from nylon 6/polypropylene grafted with maleic anhydride/polypropylene blended films. Fibrils are prepared in four consecutive steps.In the first step the polymers melt blended in an extruder with and without compatibilizers to produce chips; in the second step films are extruded from polymer blends chips, in the third step films are cold drawn with different draw ratios at room temperature and in the forth step fibrils are extracted by Soxhlet extraction with formic acid as solvent for nylon 6.  The films and fibrils were examined by scanning electron microscope and FTIR spectroscopy. It is found that the polypropylene dispersed phase deforms and coalesces into elongated fibrils during drawing  operation. The  fibrils’ diameters in the blends containing compatibilizer are more uniform and are smaller than those from films without compatibilizers. The thinnest polypropylene fibril observed has a diameter around 300 nm with the aspect ratio above 150. The stress-elongation curves show three distinctive regions, elastic, yield and hardening-leading to breakage. The elastic region is short and follows by necking and yield, i.e., elongation without increase in load. The hardening region is accompanied by the increase in the slope. The deformations of the polypropylene particles are noticed during the last regions of the extension; the fibril deformations seem to be more severe during breakage.

Montmorillonite clay/polypropylene (HMSPP) nanocomposites: evaluation of thermal and mechanical properties

International Nuclear Information System (INIS)

Komatsu, L.G.H.; Oliani, W.L.; Lugao, A.B.; Parra, D.F.

2014-01-01

The evaluation of HMSPP (high melt strength polypropylene) properties in nanocomposites was done in composites of 0.1; 1; 3; 5; 10 wt% of Cloisite 20A clay. The PP-g-MA (polypropylene graft maleic anhydride) was the compatibilizer agent in the process of extrusion in twin-screw. Mechanical tests performed in the nanocomposites with higher clay content showed higher values of rupture in 5 and 10 wt% of Cloisite. The thermal properties were evaluate utilizing Calorimetry Differential Exploratory (DSC) and in the sample of 10 wt% of Cloisite were observed increase of the melting temperature and increase of crystallinity. The morphology was investigated by the Scanning Electron Microscopy (SEM) and Fourier Transformed Infrared (FTIR), in which the sample with lower clay amount, 1 wt% of Cloisite showed better dispersion of the clay. X-Ray Diffraction reported the clay intercalation in the sample with 5 wt% of clay. (author)

Development of polypropylene (PP)/bentonite organoclay nanocomposites; Desenvolvimento de nanocompositos de polipropileno/argila bentonitica organofilica

Energy Technology Data Exchange (ETDEWEB)

Oliveira, Carlos Ivan Ribeiro de; Rocha, Marisa Cristina Guimaraes; Verly, Jessica, E-mail: carlosivanr@gmail.com [Universidade do Estado do Rio de Janeiro (UERJ), Nova Friburgo, RJ (Brazil). Instituto Politecnico; Silva, Ana Lucia Nazareth da [Universidade Federal do Rio de Janeiro (UFRJ), RJ (Brazil). Instituto de Macromoleculas Professora Eloisa Mano; Bertolino, Luiz Carlos [Centro de Tecnologia Mineral (CETEM), Rio de Janeiro, RJ (Brazil)

2016-07-01

In recent years, a significant number of studies on polymer/clay nanocomposites has been developed due to the improved properties these materials have compared to those of the conventional composites. Among the various clays used for preparing nanocomposites, the bentonite clays have been the most widely used. In this context, the aim of this work is to develop polypropylene/organoclay nanocomposites based on deposits of bentonite clays recently discovered in Cubati, PB. The composites were prepared in a twin screw extruder. The structural characterization of the produced materials indicated a possible intercalation of the polymer chains between the layers of the organoclay. The results of impact strength showed that the addition of clay as well as the initial addition of clay and compatibilizer decreased the impact strength of polypropylene. The Young's modulus and tensile strength of the polymer were not significantly affected by the filler addition. However, an increase of the elongation at break was observed. (author)

Influence of alkaline treatment and fiber loading on the physical and mechanical properties of kenaf/polypropylene composites for variety of applications

Institute of Scientific and Technical Information of China (English)

Majid Niaz Akhtar; Abu Bakar Sulong; M.K.Fadzly Radzi; N.F.Ismail; M.R.Raza; Norhamidi Muhamad; Muhammad Azhar Khan

2016-01-01

Due to current trend and increasing interest towards natural based fiber products,Kenaf (Hibiscus cannabinus) fibers have been used for the developments of many products.Therefore,Kenaf fiber-reinforced composites have been widely used in engineering and industrial applications.The present work deals with the fabricating and characterization of untreated and treated kenaf/polypropylene (PP)-reinforced composites.Composites of PP reinforced with treated and untreated kenaf fibers were fabricated using the injection molding technique.Different fiber loadings of 10,20,30,40,50 wt％ treated and untreated kenaf composites were also prepared.Xray diffraction (XRD),scanning electron microscopy (SEM),Fourier transform infrared (FTIR) spectroscopy and thermo gravimetric analysis (TGA) were performed on the treated,untreated kenaf fibers and kenaf/PP composites.Moreover,the alkaline-treated kenaf composites exhibit better physical,morphological,and mechanical properties because of the compatibility of kenaf with PP.However,variations in tensile and flexural properties depend on treatment and kenaf fiber contents.The percentage increase in the mechanical properties of the treated kenaf/PP composites relative to that of PP was also measured.In addition,40 wt％kenaf fiber loading resulted in higher mechanical properties.By contrast,kenaf/PP composite with 50％ fiber loading was not successfully prepared because of improper mixing and the burning of kenaf fibers in the PP matrix.To conclude,40％ kenaf/PP composites with superior physical and mechanical properties may be used in variety of applications such as automotive,sports,construction,animal bedding,and mass production industries.

Influence of alkaline treatment and fiber loading on the physical and mechanical properties of kenaf/polypropylene composites for variety of applications

Directory of Open Access Journals (Sweden)

Majid Niaz Akhtar

2016-12-01

Full Text Available Due to current trend and increasing interest towards natural based fiber products, Kenaf (Hibiscus cannabinus fibers have been used for the developments of many products. Therefore, Kenaf fiber-reinforced composites have been widely used in engineering and industrial applications. The present work deals with the fabricating and characterization of untreated and treated kenaf/polypropylene (PP-reinforced composites. Composites of PP reinforced with treated and untreated kenaf fibers were fabricated using the injection molding technique. Different fiber loadings of 10, 20, 30, 40, 50 wt% treated and untreated kenaf composites were also prepared. X-ray diffraction (XRD, scanning electron microscopy (SEM, Fourier transform infrared (FTIR spectroscopy and thermo gravimetric analysis (TGA were performed on the treated, untreated kenaf fibers and kenaf/PP composites. Moreover, the alkaline-treated kenaf composites exhibit better physical, morphological, and mechanical properties because of the compatibility of kenaf with PP. However, variations in tensile and flexural properties depend on treatment and kenaf fiber contents. The percentage increase in the mechanical properties of the treated kenaf/PP composites relative to that of PP was also measured. In addition, 40 wt% kenaf fiber loading resulted in higher mechanical properties. By contrast, kenaf/PP composite with 50% fiber loading was not successfully prepared because of improper mixing and the burning of kenaf fibers in the PP matrix. To conclude, 40% kenaf/PP composites with superior physical and mechanical properties may be used in variety of applications such as automotive, sports, construction, animal bedding, and mass production industries.

Effect of Mesoporous Silica and Hydroxyapatite Nanoparticles on the Tensile and Dynamic Mechanical Thermal Properties of Polypropylene and Polypropylene Foam

Directory of Open Access Journals (Sweden)

Alireza Albooyeh

2014-12-01

Full Text Available The main purpose of this paper is the experimental study on the tensile and dynamic - mechanical thermal properties of polypropylene (PP and polypropylene foam reinforced with mesoporous silica (MCM-41, hydroxyapatite (HA and the composite of mesoporous silica and hydroxyapatite (MCM41-HA nanoparticles. Nanocomposites and nanocomposite foams containing PP, maleic anhydride grafted polypropylene, different nanoparticles and chemical blowing agent (for foam samples are mixed using the melt-compounding technique in a twin-screw extruder. The results of the tests show that at the same nanoparticles content, all the nanofillers cause better mechanical properties than neat PP and PP foam. Also, due to the porous structure of the foam samples, these samples have the higher damping characteristics and lower tensile properties than the solid samples. Because of higher rigidity and higher strength of HA nanoparticles, the greatest increase in modulus and tensile strength occurs by adding these nanoparticles to neat PP and PP foam. The highest damping factor is obtained by adding MCM-41-HA nanoparticles to PP and PP foam, because of the porous nature of the MCM-41 particles which were reinforced by HA particles. The results of differential scanning calorimetry show that the addition of different nanoparticles does not have any significant effect on crystallinity and melting behavior of PP. Scanning electron microscopy images show that the nanomaterials were fine and uniformly dispersed within the polymer matrix. Furthermore, the addition of different nanoparticles to PP foam causes to increase the cell density, to reduce the cell sizes and to improve the cell sizes distribution. In this respect, the lowest cell sizes and the highest cell density are created by adding HA and MCM41-HA  nanopaticles to PP foams.

Preparation, characterization and properties of nano-hydroxyapatite/polypropylene carbonate biocomposite

Energy Technology Data Exchange (ETDEWEB)

Liao, Jianguo, E-mail: liaojianguo10@hpu.edu.cn [School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000 (China); Li, Yanqun [School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000 (China); Zou, Qin [Analytical & Testing Center, Sichuan University, Chengdu 610064 (China); Duan, Xingze; Yang, Zhengpeng; Xie, Yufen [School of Materials Science and Engineering, Henan Polytechnic University, Jiaozuo 454000 (China); Liu, Haohuai [School of Chemistry and Chemical Engineering, Analytical and Testing Center, Guangzhou University, Guangzhou 510006 (China)

2016-06-01

The combination of nano-hydroxyapatite (n-HA) and polypropylene carbonate (PPC) was used to make a composite materials by a coprecipitation method. The physical and chemical properties of the composite were tested. Scanning electron microscope (SEM) observation indicated that the biomimetic n-HA crystals were uniformly distributed in the polymer matrix. As the n-HA content increased in the composite, the fracture mechanism of the composites changes from gliding fracture to gliding and brittle fracture. Furthermore, the chemical interaction between inorganic n-HA and polypropylene carbonate was also investigated and discussed in detail. The hydrogen bonds might be formed between –OH/CO{sub 3}{sup 2−} of n-HA crystal and the ester group (–COO–) of PPC. The tensile strength of n-HA/PPC (40/60) was similar to that of the cancellous bone, and reached ca 58 MPa. The osteoblasts were cultured for up to 7 days, and then the adhesion and proliferation of osteoblasts were measured by Methyl thiazolyl tetrazolium (MTT) colorimetry assay and SEM. The cells proliferated, grew normally in fusiform shape and well attached. The in vitro test confirmed that the n-HA/PPC composites were biocompatible and showed undetectable negative effect on osteoblasts. In vivo implantation of the composite in New Zealand white rabbits was performed. It can stimulate the growth of a new bone, and at the same time the material begins to degrade. These results suggested that the composite may be suitable for the reparation or replacement of bone defects and possessed the potential for clinical applications. - Graphical abstract: SEM micrographs of the induced osteoblasts cultured on the n-HA/PC (40/60) composite. After 2 day cell culture (a), after 4 days (b) hematoxylin/eosin-stained sections of n-HA/PPC (40/60) composite materials. In the photos, M denotes n-HA/PPC (40/60) composite materials, B denotes bone, while NB denotes newly formed bone tissue. - Highlights: • A novel method, co

Suppressing immature house and stable flies in outdoor calf hutches with sand, gravel, and sawdust bedding.

Science.gov (United States)

Schmidtmann, E T

1991-11-01

Sand, gravel, sawdust, and pine shavings were used as bedding in outdoor calf hutches and compared with straw relative to the density of immature (maggot) house flies, Musca domestica, and stable flies, Stomoxys calcitrans. In 6-wk field trials, average densities of house and stable fly maggots in concrete mix sand ranged from only .3 to 1.6 and 0 to .1 maggots/L, respectively; pea size gravel bedding also strongly suppressed densities from less than .1 to .3 and less than .1 to .1 maggots/L, respectively. These densities represent reductions of 76 to greater than 99% relative to straw bedding, but both sand and gravel compacted and became soiled with calf feces, which resulted in unacceptable bedding sanitation and foul odors. Densities of house and stable fly maggots in pine shavings did not differ from those in straw bedding. Nevertheless, in sawdust bedding, maggot density was limited to averages of 1.4 to 8.3 house and 9.8 to 11.8 stable fly maggots/L; this represented reductions of 45 to 91% relative to straw. In a follow-up trial, house and stable fly maggot densities in sawdust averaged 11.3 and 43.9 maggots/L, respectively, reductions of 77 and 46%. These findings suggest that bedding calf hutches with sawdust during warm weather can be useful as an ecologically sound approach to controlling muscoid fly populations on dairy farms.

Comparative study on microwave and conventional hydrothermal pretreatment of bamboo sawdust: Hydrochar properties and its pyrolysis behaviors

International Nuclear Information System (INIS)

Dai, Leilei; He, Chao; Wang, Yunpu; Liu, Yuhuan; Yu, Zhenting; Zhou, Yue; Fan, Liangliang; Duan, Dengle

2017-01-01

Highlights: • Two pretreatments affect differently the hydrochar properties and its pyrolysis behaviors. • Hydrochar by conventional hydrothermal pretreatment shows higher thermal stability. • Microwave hydrothermal pretreatment removes more acetyl. • Hydrochar by microwave hydrothermal pretreatment produces more glucopyranose and less acids. - Abstract: Comparative study on microwave and conventional hydrothermal pretreatment of bamboo sawdust was carried out in this study. Microwave and conventional hydrothermal pretreatment both improved the hydrochar properties and its pyrolysis behaviors. Proximate and elemental analyses show that the properties of hydrochar from microwave hydrothermal pretreatment are better than conventional hydrothermal pretreatment in terms of calorific value and oxygen content except for 150 °C. Microwave hydrothermal pretreatment removes more acetyl groups in hemicellulose compared to conventional hydrothermal pretreatment, which may be attributed to the hot spot effect of microwave irradiation. The peaks of thermogravimetric and derivative thermogravimetric curves of pretreated samples always shifted to higher temperature region. Also, the conventional hydrothermal pretreated samples are more thermally stable than those by microwave heating. In addition, the glucopyranose content in pyrolysis vapors of microwave hydrothermal pretreated bamboo sawdust (190 °C) was 9.82% higher than that from conventional hydrothermal pretreated bamboo sawdust. However, the acids content from microwave hydrothermal pretreated bamboo sawdust (150 °C) was 4.12% lower. In this regard, microwave hydrothermal pretreatment is more suitable for upgrading the pyrolysis oil quality than conventional hydrothermal pretreatment.

Briquetting of coal fines and sawdust - effect of particle-size distribution

Energy Technology Data Exchange (ETDEWEB)

Patil, D.P.; Taulbee, D.; Parekh, B.K.; Honaker, R. [University of Kentucky, Lexington, KY (United States). Center for Applied Energy Research

2009-07-01

The coal industry usually discards fine-size (-150 microns) coal because of its high-moisture content and handling problems. One avenue for utilization is to either pelletize or briquette this material. However, industry has not adopted this route due in large part to significant drying and binder costs. In an effort to reduce these costs, compacting and briquetting studies were conducted to determine the effect of combining a coarse (1.18x0.15mm) spiral separator product with a fine coal flotation product (-150microns), with and without adding sawdust. Maximizing the packing density of the coal and wood waste mixture could potentially reduce the binder requirement by minimizing the void space as well as reducing shipping costs. Accordingly, work reported here focused on evaluating the impact of the particle-size distribution of different blends of fine and coarse coal, with and without sawdust and/or binder. The modified Proctor density of compacted blends along with the porosity and compressive strengths of briquettes made from each blend were determined. For the coal-only blends, the packing density was maximized by a relatively high (70% to 80%) coarse coal content. However, the packing density did not correlate with the compressive strength of the briquette that instead maximized with 100% fine flotation coal and continuously decreased as higher proportions of coarse coal were added. Similar compaction and compressive-strength results were obtained with mixtures of sawdust and varying proportions of coarse and fine coal. With the addition of a binder, the highest strengths were no longer obtained with 100% fine coal but instead maximized between 20% and 50% coarse coal addition depending on how long the briquettes were cured.

Development of bio/blood compatible polypropylene through low pressure nitrogen plasma surface modification

International Nuclear Information System (INIS)

Gomathi, N.; Rajasekar, R.; Babu, R. Rajesh; Mishra, Debasish; Neogi, S.

2012-01-01

Surface modification of polypropylene by nitrogen containing plasma was performed in this work in order to improve the wettability which resulted in enhanced biocompatibility and blood compatibility. Various nitrogen containing functional groups as well as oxygen containing functional groups were found to be incorporated to the polymer surface during plasma treatment and post plasma reaction respectively. Wettability of the polymers was evaluated by static contact angle measurement to show the improvement in hydrophilicity of plasma treated polypropylene. Cross linking and surface modification were reported to be dominating in the case of nitrogen plasma treatment compared to degradation. The effect of various process variables namely power, pressure, flow rate and treatment time on surface energy and weight loss was studied at various levels according to the central composite design of response surface methodology (RSM). Except pressure the other variables resulted in increased weight loss due to etching whereas with increasing pressure weight loss was found to increase and then decrease. The effect of process variables on surface morphology of polymers was evaluated by Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). Well spread fibroblast cells on nitrogen plasma treated polypropylene due to the presence of CO, NH 2+ and NH + was observed. Reduced platelet adhesion and increased partial thromboplastin time evidenced the increased blood compatibility. - Highlights: ► Improved biocompatibility and blood compatibility of polypropylene. ► Nitrogen plasma surface modification. ► Maintaining a balance between polar group incorporation and weight loss due to etching. ► Optimization of process conditions by response surface methodology.

Enhancement of mechanical properties and interfacial adhesion by chemical odification of natural fibre reinforced polypropylene composites

CSIR Research Space (South Africa)

Erasmus, E

2008-11-01

Full Text Available with the polymer matrix. Therefore, the constituents need to be chemically modified to enhancing adhesion between fibre and polymer matrix. The aim of this work is to improve the interfacial adhesion between the polypropylene matrix and the natural fibre...

Pyrolysis Process and Characteristics of Products from Sawdust Briquettes

Directory of Open Access Journals (Sweden)

Hua Yang

2016-01-01

Full Text Available The pyrolysis of briquettes made from biomass is an available and economic technological route for the production of briquette charcoal, but by-products (tar and gas cannot be brought into full utilization, leading to the waste of resources and the addition of environmental concerns. Temperature is the most important parameter that affects the distributions and properties of briquette charcoal. This work investigated the three kinds of products of the pyrolysis of sawdust briquette in a fixed bed across a wide temperature range (250 to 950 °C. The purpose of this experiment was to study the pyrolysis process and the properties of the resulting products (briquette charcoal, liquid, and gas of sawdust briquettes and explore the optimum operating temperature to generate good quality briquette charcoal, liquid, and gaseous products simultaneously. According to the results, the optimum pyrolysis temperature range was 450 to 650 °C, for which the briquette charcoal produced within this range had the highest calorific value (2,9.14 to 30.21 MJ/kg. Meanwhile, the liquid product is considered to be useful for liquid fuels or valuable chemical materials, and the low heating value of the gaseous product was 11.79 to 14.85 MJ/Nm3 in this temperature range.

New fillers in the synthesis of polypropylene nano composites with Ziegler-Natta catalysts

International Nuclear Information System (INIS)

Rosa, Jeferson L.S.; Silva, Marcelo C.V.; Marques, Maria F.V.

2011-01-01

In this study, Ziegler-Natta catalysts bi-supported on MgCl 2 and natural clays were prepared in order to synthesize polypropylene nanocomposites. The employed clays were bentonite, as reference, as well as halloysite, vermiculite and mica. Propylene polymerizations were carried out using those catalysts and the properties of the obtained materials were analyzed using techniques of thermogravimetric analysis X-ray diffraction, dynamic mechanical thermal analysis e scanning electronic microscopy. Results showed the production of nanocomposites with higher thermal degradation temperature. (author)

Synthesis and characterization of CNTs using polypropylene waste as precursor

Energy Technology Data Exchange (ETDEWEB)

Bajad, Ganesh S. [Department of Chemical Engineering, Visvesvaraya National Institute of Technology, Nagpur 440010 (India); Tiwari, Saurabh K. [Department of Chemical Engineering, Indian Institute of Technology Bombay, Powai, Mumbai 400076 (India); Vijayakumar, R.P., E-mail: vijayakumarrp@che.vnit.ac.in [Department of Chemical Engineering, Visvesvaraya National Institute of Technology, Nagpur 440010 (India)

2015-04-15

Graphical abstract: - Highlights: • A facile method for producing CNTs from polypropylene waste is proposed. • Optimization of Ni/Mo mole ratio using RSM suggests the adequacy of cubic model. • Process parameters were optimized by RSM using Box–Behnken four factorial design. • Maximum desirability of one suggested that 514% of CNTs would yield over Ni{sub 4}Mo{sub 0.2}MgO{sub 1}. • Increase in Ni/Mo ratio from 0.5 to 20, inner diameter of CNTs decreases from 25 to 2 nm. - Abstract: We study the synthesis of MWCNTs using polypropylene waste as a precursor and Ni/Mo/MgO as a catalyst by the combustion technique. Molar ratios of Ni, Mo and MgO in the Ni/Mo/MgO catalyst were optimized using response surface methodology (RSM) to obtain the maximum yield of CNTs. The mole ratio 4/0.2/1 was found to yield more carbon product. Further, process parameters such as combustion temperature, combustion time, polymer and catalyst weight were optimized by RSM using Box–Behnken three-level and four-factorial design. The best possible combination of process parameters (combustion time of 10 min, combustion temperature of 800 °C, polymer weight of 5 g and catalyst weight of 150 mg) for maximum yield of CNTs was obtained. HRTEM indicates that the diameter of CNTs depends on the catalyst composition used for the synthesis of CNTs. The results of the study indicate a facile method for producing CNTs from polypropylene waste.

Synthesis and characterization of CNTs using polypropylene waste as precursor

International Nuclear Information System (INIS)

Bajad, Ganesh S.; Tiwari, Saurabh K.; Vijayakumar, R.P.

2015-01-01

Graphical abstract: - Highlights: • A facile method for producing CNTs from polypropylene waste is proposed. • Optimization of Ni/Mo mole ratio using RSM suggests the adequacy of cubic model. • Process parameters were optimized by RSM using Box–Behnken four factorial design. • Maximum desirability of one suggested that 514% of CNTs would yield over Ni 4 Mo 0.2 MgO 1 . • Increase in Ni/Mo ratio from 0.5 to 20, inner diameter of CNTs decreases from 25 to 2 nm. - Abstract: We study the synthesis of MWCNTs using polypropylene waste as a precursor and Ni/Mo/MgO as a catalyst by the combustion technique. Molar ratios of Ni, Mo and MgO in the Ni/Mo/MgO catalyst were optimized using response surface methodology (RSM) to obtain the maximum yield of CNTs. The mole ratio 4/0.2/1 was found to yield more carbon product. Further, process parameters such as combustion temperature, combustion time, polymer and catalyst weight were optimized by RSM using Box–Behnken three-level and four-factorial design. The best possible combination of process parameters (combustion time of 10 min, combustion temperature of 800 °C, polymer weight of 5 g and catalyst weight of 150 mg) for maximum yield of CNTs was obtained. HRTEM indicates that the diameter of CNTs depends on the catalyst composition used for the synthesis of CNTs. The results of the study indicate a facile method for producing CNTs from polypropylene waste

Research on mechanical properties of carbon fiber /polyamide reinforced PP composites

Science.gov (United States)

Chen, Xinghui; Yu, Qiang; Liu, Lixia; Ji, Wenhua; Yang, Li; Fan, Dongli

2017-10-01

The polyamide composites reinforced by carbon fiber/polypropylene are produced by injection molding processing. The flow abilities and mechanical properties of the CF/PA/PP composite materials are studied by the fusion index instrument and the universal testing machine. The results show that with the content of carbon fiber/polyamide increase, the impact breaking strength and the tensile property of the composite materials increase, which is instructive to the actual injection production of polypropylene products.

Formation of CuxS Layers on Polypropylene Sulfurized by Molten Sulfur

Directory of Open Access Journals (Sweden)

Rasa ALABURDAITĖ

2011-11-01

Full Text Available The processes of formation of electrically conductive layers of copper sulfides CuxS by the sorption-diffusion method on polypropylene (PP using molten sulfur as sulfurizing agent was investigated. The amount of sorbed sulfur increased with the increase of the duration of treatment. Copper sulfide layers were formed on the surface of polypropylene after the treatment of sulfurized polymer with Cu(II/I salt solution. The amount of copper sulfide in layer increased with the increase of treatment duration in copper salt solution. XRD spectra of PP films treated for 3 min with molten sulfur and then with Cu(II/I salt solution for the different time showed that the copper sulfide phases, mostly digenite, Cu2-xS and a-chalcocite, Cu2S were formed in the layers. Electromotive force measurement results confirmed the composition of formed CuxS layers on PP. The phase composition of layers also changed after the annealing. The value of electrical resistance of copper sulfide layers on PP varied from 20 W/cm2 to 80 W/cm2 and after annealing at 80 °C - in the interval of 10 W/cm2 - 60 W/cm2.http://dx.doi.org/10.5755/j01.ms.17.4.776

Evaluation of the environmental aging and mechanical properties of the polypropylene/sugarcane bagasse composites; Avaliacao do envelhecimento ambiental e das propriedades mecanicas dos compositos de polipropileno/bagaco de cana-de-acucar

Energy Technology Data Exchange (ETDEWEB)

Paiva, Rayane Lima de Moura; Mulinari, Daniella Regina [Centro Universitario de Volta Redonda (UNIFOA), Volta Redonda, RJ (Brazil)

2013-06-15

Polypropylene (PP) reinforced with fibers from sugarcane bagasse composites in different proportions were prepared. Also environmental aging was conducted for the composites and their mechanical properties determined. The results showed that chemical treatment caused changes in color and chemical composition of the fibers, removing impurities and amorphous constituents such as lignin and hemicellulose, techniques of FTIR, X-ray diffraction and scanning electron microscopy confirmed these data. Also, it was observed that addition of natural fiber in PP matrix provided an improvement in the mechanical properties materials. The weathering test revealed a slight mass gain after 75 days, but it was clear that the inclusion of fibers has a higher mass gain compared to pure PP. (author)

Numerical modeling of pyrolysis of sawdust in a packed bed

Energy Technology Data Exchange (ETDEWEB)

Meng, Qingmin; Chen, Xiaoping [Southeast Univ., Nanjing (China). School of Energy and Environment

2013-07-01

An unsteady, one-dimensional mathematical model has been developed to describe the pyrolysis of sawdust in a packed bed. The sawdust bed was pyrolyzed using the hot gas and an electric heater outside the bed as the source of energy. The developed model includes mass, momentum and energy conservations of gas and solid within the bed. The gas flow in the bed is modeled using Darcy's law for fluid through a porous medium. The heat transfer model includes heat conduction inside the bed and convection between the bed and the hot gas. The kinetic model consists of primary pyrolysis reaction. A finite volume fully implicit scheme is employed for solving the heat and mass transfer model equations. A Runge-Kutta fourth order method is used for the chemical kinetics model equations. The model predictions of mass loss history and temperature were validated with published experimental results, showing a good agreement. The effects of inlet temperature on the pyrolysis process have been analyzed with model simulation. A sensitivity analysis using the model suggests that the predictions could be improved by considering the second reaction which could generate volatile flowing in the void.

Abaca fibre reinforced PP composites and comparison with jute and flax fibre PP composites

Directory of Open Access Journals (Sweden)

2007-11-01

Full Text Available Abaca fibre reinforced PP composites were fabricated with different fibre loadings (20, 30, 40, 50wt% and in some cases 35 and 45 wt%. Flax and jute fibre reinforced PP composites were also fabricated with 30 wt% fibre loading. The mechanical properties, odour emission and structure properties were investigated for those composites. Tensile, flexural and Charpy impact strengths were found to increase for fibre loadings up to 40 wt% and then decreased. Falling weight impact tests were also carried out and the same tendency was observed. Owing to the addition of coupling agent (maleated polypropylene -MAH-PP, the tensile, flexural and falling weight impact properties were found to increase in between 30 to 80% for different fibre loadings. When comparing jute and flax fibre composites with abaca fibre composites, jute fibre composites provided best tensile properties but abaca fibre polypropylene composites were shown to provide best notch Charpy and falling weight impact properties. Odours released by flax fibre composites were smaller than jute and abaca fibre composites.

Autoclaved Sand-Lime Products with a Polypropylene Mesh

Science.gov (United States)

Kostrzewa, Paulina; Stępień, Anna

2017-10-01

The paper presents the results of the research on modifications of silicate bricks with a polypropylene mesh and their influence on physical, mechanical and microstructural properties of such bricks. The main goal of the paper was to determine effects of the polypropylene mesh on sand-lime product parameters. The analysis has focused on compressive strength, water absorption, bulk density and structural features of the material. The obtained product is characterized by improved basic performance characteristics compared to traditional silicate products. Using the polypropylene mesh increased compressive strength by 25% while decreasing the product density. The modified products retain their form and do not disintegrate after losing their bearing capacity.

Microstructural evolution during tensile deformation of polypropylenes

International Nuclear Information System (INIS)

Dasari, A.; Rohrmann, J.; Misra, R.D.K.

2003-01-01

Tensile deformation processes occurring at varying strain rates in high and low crystallinity polypropylenes and ethylene-propylene di-block copolymers have been investigated by scanning electron microscopy. This is examined for both long and short chain polymeric materials. The deformation processes in different polymeric materials show striking dissimilarities in spite of the common propylene matrix. Additionally, the deformation behavior of long and their respective short chain polymers was different. Deformation mechanisms include crazing/tearing, wedging, ductile ploughing, fibrillation, and brittle fracture. The different modes of deformation are depicted in the form of strain rate-strain diagrams. At a constant strain rate, the strain to fracture follows the sequence: high crystallinity polypropylenes< low crystallinity polypropylenes< ethylene-propylene di-block copolymers, indicative of the trend in resistance to plastic deformation

Removal of Cd(II) and Pb(II) ions, from aqueous solutions, by adsorption onto sawdust of Pinus sylvestris

International Nuclear Information System (INIS)

Taty-Costodes, V. Christian; Fauduet, Henri; Porte, Catherine; Delacroix, Alain

2003-01-01

Fixation of heavy metal ions (Cd(II) and Pb(II)) onto sawdust of Pinus sylvestris is presented in this paper. Batch experiments were conducted to study the main parameters such as adsorbent concentration, initial adsorbate concentration, contact time, kinetic, pH solution, and stirring velocity on the sorption of Cd(II) and Pb(II) by sawdust of P. sylvestris. Kinetic aspects are studied in order to develop a model which can describe the process of adsorption on sawdust. The equilibrium of a solution between liquid and solid phases is described by Langmuir model. Scanning electronic microscopy (SEM) coupled with energy dispersive X-ray analysis (EDAX) and X-ray photoelectron spectroscopy (XPS) shows that the process is controlled by a porous diffusion with ion-exchange. The capacity of the metal ions to bind onto the biomass was 96% for Cd(II), and 98% for Pb(II). The sorption followed a pseudo-second-order kinetics. The adsorption of these heavy metals ions increased with the pH and reached a maximum at a 5.5 value. From these results, it can be concluded that the sawdust of P. sylvestris could be a good adsorbent for the metal ions coming from aqueous solutions. Moreover, this material could also be used for purification of water before rejection into the natural environment

Utilization of poplar wood sawdust for heavy metals removal from model solutions

Directory of Open Access Journals (Sweden)

Demcak Stefan

2017-06-01

Full Text Available Some kinds of natural organic materials have a potential for removal of heavy metal ions from wastewater. It is well known that cellulosic waste materials or by-products can be used as cheap adsorbents in chemical treatment process. In this paper, poplar wood sawdust were used for removal of Cu(II, Zn(II and Fe(II ions from model solutions with using the static and dynamic adsorption experiments. Infrared spectrometry of poplar wood sawdust confirmed the presence of the functional groups which correspond with hemicelluloses, cellulose and lignin. At static adsorption was achieved approximately of 80 % efficiency for all treated model solutions. Similar efficiency of the adsorption processes was reached after 5 min at dynamic condition. The highest efficiency of Cu(II removal (98 % was observed after 30 min of dynamic adsorption. Changes of pH values confirmed a mechanism of ion exchange on the beginning of the adsorption process.

Dissolution of South African Eucalyptus sawdust wood in [Emim][OAc]/Co-solvent mixtures

CSIR Research Space (South Africa)

Tywabi, Zikhona

2017-03-01

Full Text Available The paper presents a method of obtaining wood cellulose by dissolution of eucalyptus sawdust in a mixture of ionic liquid (IL) 1-ethyl-3-methylimidazolium acetate [Emim][OAc] together with co-solvents; dimethylformamide (DMF) and dimethylsulphoxide...

Effect of ultraviolet radiation (300-400 nanometers) on polypropylene

International Nuclear Information System (INIS)

Lerman, S.

1983-01-01

Polypropylene discs and shavings were exposed to simulated ambient ultraviolet (UV) radiation (lambda 300-400 nm) for a period equivalent to at least two years of wear within the eye, assuming the eye to be exposed to ambient UV radiation for four hours per day at 1 mW/cm2. The polypropylene and the incubation media were measured by several forms of optical spectroscopy, and there was no photochemical change in either. Where polypropylene discs were exposed to a very high level of UV radiation (greater than 500 W/cm2), they became brittle and discolored within five to ten days. This level of exposure, however, was equivalent to a total of over 20 million joules/cm2, which is at least one million times levels for expected ambient UV exposure to polypropylene within the eye

Thermal properties of light-weight concrete with waste polypropylene aggregate

Science.gov (United States)

Záleská, Martina; Pokorný, Jaroslav; Pavlíková, Milena; Pavlík, Zbyšek

2017-07-01

Thermal properties of a sustainable light-weight concrete incorporating high volume of waste polypropylene as partial substitution of natural aggregate were studied in the paper. Glass fiber reinforced polypropylene (GFPP), a by-product of PP tubes production, partially substituted fine natural silica aggregate in 10, 20, 30, 40, and 50 mass%. In order to quantify the effect of GFPP use on concrete properties, a reference concrete mix without plastic waste was studied as well. For the applied GFPP, bulk density, matrix density, and particle size distribution were measured. Specific attention was paid to thermal transport and storage properties of GFPP that were examined in dependence on compaction time. For the developed light-weight concrete, thermal properties were accessed using transient impulse technique, whereas the measurement was done in dependence on moisture content, from the dry state to fully water saturated state. Additionally, the investigated thermal properties were plotted as function of porosity. The tested light-weight concrete was found to be prospective construction material possessing improved thermal insulation function. Moreover, the reuse of waste plastics in concrete composition was beneficial both from the environmental and financial point of view considering plastics low biodegradability and safe disposal.

Graft copolimerization of hydrophilic monomers onto irradiated polypropylene fibers

International Nuclear Information System (INIS)

Sundardi, F.

1978-01-01

A method of graft copolymerization of hydrophilic monomers, such as 1-vinyl-2-pyrrolidone, acrylonitrile, acrylic acid, and acrylamide, onto irradiated polypropylene fibers has been studied. γ ray as well as electron beam were employed for the irradiation processes. Graft-copolymerization kinetics and the properties of grafted fibers have been investigated. Moisture regain, dyes absorption, and melting point of the grafted fibers were found to increase with the increasing of the degree of grafting. Polypropylene for 1-vinyl-2-pyrrolidone grafted fibers showed excellent dye absorption for almost all kinds of dyes such as direct, basic, acid, reactive, disper, and naphthol dyes. However, for polypropylene acrylic acid grafted fibers, the colorfastness to washing was found to be unsatisfactory. The colorfastness to washing for polypropylene 1-vinyl-2-pyrrolidone grafted fibers was found to be fairly good for certain types of dyes such as vat and naphthol dyes. (author)

The effects of normal paraffins mobilizers on irradiated polypropylene

International Nuclear Information System (INIS)

Chen Wenxiu; Gao Ling

1995-01-01

The n-paraffins blended with polypropylene (PP) as mobilizer had been investigated. The effectiveness of mobilizer (n-paraffins) on irradiated polypropylene is dependent on the molecular weight of mobilizer and its content on polypropylene. The n-docosame (n-C 22 ) possesses the best effectiveness of radiation tolerance on PP among the mobilizer paraffins: n-decane (n-C 10 ), n-hexadecane (n-C 16 ), n-docosane (n-C 22 ) and n-hexatriacontane (n-C 36 ). The 2% (w/w) content of a given mobilizer is the most effective at reducing the embrittlement of irradiated PP as evidenced by the elongation at break. The physical properties of polypropylene with mobilizers such as density, Young's modulus, the Fraction of free volume and the weight swelling ratio in p-xylene at room temperature were measured. Above phenomena are related with the constructive of blended PP and demonstrated by its physical properties

Preliminary study on antifungal effect of commercial essential oils against white rot fungi

Science.gov (United States)

Khalid, Nurul Izzaty; Baharum, Azizah; Daud, Fauzi

2015-09-01

Protecting and preserving wood plastic composite from deterioration caused by fungal attack is a high challenge issue to cater nowadays. The objective of this study was to carry out a screening test towards antifungal effect of essential oil and to investigate the potential of raw materials that will be used as basic material for manufacturing wood plastic composite against white rot fungi. Essential oils from four types of natural products comprising cinnamon, lemongrass, lavender and geranium have been screened for their ability to inhibit five types of white rot fungi species which are Lentinus squarrosulus, Pleuorotus pulmonarius, Lentinus sp., Pleuorotus sajor-caju and Lignosus rhinocerus. The antifungal evaluation showed that no inhibitory effect against tested white rot fungi since the mycelia completely filled the plates. From the observation, mycelia of L. squarrosulus, P. pulmonarius and Lentinus sp. were found to filled the surface of falcon tubes with rubber sawdust after 15 days. Mycelia of L. squarrosulus and P. pulmonarius also were found to completely covered the surface of media that contain polypropylene and maleic anhydride grafted polypropylene on it. Therefore, this report proved that the main materials that will be applicable in manufacturing of wood plastic composite had potential to be degraded by this type of fungal attack.

SHS synthesis of Si-SiC composite powders using Mg and reactants from industrial waste

Science.gov (United States)

Chanadee, Tawat

2017-11-01

Si-SiC composite powders were synthesized by self-propagating high-temperature synthesis (SHS) using reactants of fly ash-based silica, sawdust-based activated carbon, and magnesium. Fly ash-based silica and sawdust-based activated carbon were prepared from coal mining fly ash and Para rubber-wood sawdust, respectively. The work investigated the effects of the synthesis atmosphere (air and Ar) on the phase and morphology of the SHS products. The SHS product was leached by a two-step acid leaching processes, to obtain the Si-SiC composite powder. The SHS product and SHS product after leaching were characterized by X-ray diffractometry, scanning electron microscopy and energy dispersive X-ray spectrometry. The results indicated that the SHS product synthesized in air consisted of Si, SiC, MgO, and intermediate phases (SiO2, Mg, Mg2SiO4, Mg2Si), whereas the SHS product synthesized in Ar consisted of Si, SiC, MgO and a little Mg2SiO4. The SiC content in the leached-SHS product was higher when Ar was used as the synthesis atmosphere. As well as affecting the purity, the synthesis atmospheres also affected the average crystalline sizes of the products. The crystalline size of the product synthesized in Ar was smaller than that of the product synthesized in air. All of the results showed that fly ash and sawdust could be effective waste-material reactants for the synthesis of Si-SiC composite powders.

Effect of modified polypropylene on the interfacial bonding of polymer–aluminum laminated films

International Nuclear Information System (INIS)

Liang, Chang-Sheng; Lv, Zhong-Fei; Bo, Yang; Cui, Jia-Yang; Xu, Shi-Ai

2015-01-01

Highlights: • Aluminium-polymer composite packing material with high T-peel strength was prepared. • Polypropylene was grafted by acrylic acid, glycidyl methacrylate, maleic anhydride. • Grafted polypropylene greatly improved the T-peel strength. • Chemical bonding plays an important role in improving the adhesion strength. - Abstract: The interfacial bonding between functionalized polymers and chromate–phosphate treated aluminum (Al) foil were investigated in this study. Glycidyl methacrylate (GMA), acrylic acid (AA) and maleic anhydride (MAH) were grafted onto polypropylene (PP) to improve its adhesion strength with the treated Al foil. The interfacial peel strength was evaluated by the T-peel test, and the results showed that modification of PP resulted in a significant improvement in the interfacial peel strength from 1 N/15 mm for pure PP to 10–14 N/15 mm for the modified PP. The surface chemistry, topography and surface energy of the modified PP and Al foil after peeling were characterized by time-of-flight secondary ion mass spectrometry (TOF-SIMS), X-ray photoelectron spectroscopy (XPS), attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), scanning electron microscopy (SEM) and contact angle measurement. The treated Al foil could react with the functional groups of PP, resulting in the formation of new carboxylates. The new chemical bonding rather than the mechanical interlocking contributed to the improvement of adhesion strength

Alternatives for composting Caribbean Pine sawdust (Pinus caribaea in the wood industry Refocosta S. A., in the municipality of Villanueva, Casanare, Colombia

Directory of Open Access Journals (Sweden)

Mónica Bibiana Sarmiento Oviedo

2011-10-01

Full Text Available Given the day-to-day accumulation of sawdust, a byproduct of the milling process of the Pinus caribaea species in the Wood industry of Refocosta, a composting process was tested in three treatments with different nitrogen sources (urea, industrial palm oil sludge, cattle dung and it was compared with composted pine bark and sawdust exposed to the weather. To assess possible inhibition of the substrates, the fresh biomass and germination of Zea maize and Acacia mangium was measured. Seedlings of Pinus caribaea, eucalyptus Pellita and Acacia Mangium were transplanted, and two months later the stem length, strength and survival were assessed. There were differences between maize and Acacia mangium and a lower germination and biomass in the substrates, sawdust and bark exposed to the weather and without composting were observed. The vigor and stem length were significantly better in composted bark, substrate which is currently used in the vivarium of Refocosta to produce seedlings; the sawdust-based substrates showed marked deficits (red colors, necrosis and stunting.

Strength of biodegradable polypropylene tapes filled with a modified starch

Science.gov (United States)

Vinidiktova, N. S.; Ermolovich, O. A.; Goldade, V. A.; Pinchuk, L. S.

2006-05-01

The possibility of creating composite materials with high deformation and strength characteristics based on polypropylene (PP) and a natural polysaccharide in the form of a modified starch (MS) has been studied. The modified starch is shown to interact chemically with functional groups of PP, thereby positively affecting the physicomechanical properties, structure, and water absorption properties of films and oriented flat fibers based on starch-filled PP. The strength characteristics of both oriented and unoriented composites are 1.5-2.0 times as high as those of the initial PP. The water absorption ability of the materials varies symbatically with content of MS, which points to the dominant contribution of interactions at the PP-MS interface. The introduction of MS into synthetic polymers offers a possibility of producing new ecologically safe materials with high strength characteristics.

Polypropylene and polycarbonate radiosterilization: effects on the stress resistance

International Nuclear Information System (INIS)

Musico Filho, W.; Terence, M.C.; Guedes, S.M.L.; Araujo, E.S. de

1994-01-01

The gamma radiation effect on polymer sterilization used in the fabrication of medical supplies, national polycarbonate and polypropylene, was studied in function of the tensile strength. During the polycarbonate irradiation occur the scission of polymer chain and the crosslinking/scission of the polypropylene, but in the sterilization dose, 25 kGy, does not occur expressive changes in the tensile strength. After the polypropylene sterilization the tensile strength continues increasing as consequence of the crosslinking. Since the sixth day the oxidation reaction predominates as consequence of the radical migration to the amorphous region. (author). 7 refs, 6 figs

A Comprehensive Study of the Polypropylene Fiber Reinforced Fly Ash Based Geopolymer

DEFF Research Database (Denmark)

Ranjbar, Navid; Mehrali, Mehdi; Behnia, Arash

2016-01-01

and long term impacts of different volume percentages of polypropylene fiber (PPF) reinforcement on fly ash based geopolymer composites. Different characteristics of the composite were compared at fresh state by flow measurement and hardened state by variation of shrinkage over time to assess the response...... of composites under flexural and compressive load conditions. The fiber-matrix interface, fiber surface and toughening mechanisms were assessed using field emission scan electron microscopy (FESEM) and atomic force microscopy (AFM). The results show that incorporation of PPF up to 3 wt % into the geopolymer......As a cementitious material, geopolymers show a high quasi-brittle behavior and a relatively low fracture energy. To overcome such a weakness, incorporation of fibers to a brittle matrix is a well-known technique to enhance the flexural properties. This study comprehensively evaluates the short...

The effect of halloysite modification combined with in situ matrix modifications on the structure and properties of polypropylene/halloysite nanocomposites

Czech Academy of Sciences Publication Activity Database

Khunova, V.; Kristóf, J.; Kelnar, Ivan; Dybal, Jiří

2013-01-01

Roč. 7, č. 5 (2013), s. 471-479 ISSN 1788-618X R&D Projects: GA AV ČR IAA200500904 Institutional support: RVO:61389013 Keywords : nanocomposites * polypropylene * halloysite Subject RIV: JI - Composite Materials Impact factor: 2.953, year: 2013

Polypropylene/graphite nanocomposites by in situ polymerization

International Nuclear Information System (INIS)

Milani, Marceo A.; Galland, Giselda B.; Quijada, Raul

2011-01-01

This work presents the synthesis of nanocomposites of polypropylene/graphite by in situ polymerization using metallocene catalyst and graphene nanosheets. Initially was analyzed which of the metallocene catalysts rac-Et(Ind) 2 ZrCl 2 or rac-Me 2 Si(Ind) 2 ZrCl 2 produces polypropylene with mechanical properties more relevant. Then it were performed the in situ polymerization reactions to obtain the nanocomposites. The polymeric materials were characterized by XRD, DSC, GPC and DMTA. (author)

Phenolic Content and Antioxidant Capacity of Essential Oil Obtained from Sawdust of Chamaecyparis obtusa by Microwave-Assisted Hydrodistillation

Directory of Open Access Journals (Sweden)

Vivek K. Bajpai

2013-01-01

Full Text Available Reactive oxygen species and free radicals play a major role in food deterioration. Current research is directed towards finding naturally occurring antioxidants of plant origin. In the present study, the chemical composition analysis of the essential oil obtained from sawdust of Chamaecyparis obtusa (COEO was conducted by gas chromatography coupled with mass spectroscopy (GC-MS. Further, the phenolic content and antioxidant capacity of the COEO were investigated using different radical scavenging assays. The COEO obtained from the dried sawdust material using a microwave-assisted hydrodistillation technique resulted in the determination of 46 different compounds by GC-MS analysis, representing 98.94 % of total oil content. The COEO was characterised by the presence of mono- and sesquiterpene hydrocarbons, oxygenated mono- and sesquiterpenes, steroids, diterpenes and indole derivatives. At the highest tested concentration range, the COEO showed antioxidant capacity, i.e. the inhibition of DPPH, nitric oxide, superoxide and hydroxyl radicals of 80.16, 82.93, 72.99 and 71.62 %, respectively. Moreover, the COEO displayed concentration-dependent reducing power ability and remarkable inhibitory effect on ferric ion-induced lipid peroxidation in bovine brain extract. In addition, the COEO yielded (6.13±0.05 mg of gallic acid per g of dry mass. The present study confirms that the C. obtusa essential oil has potent antioxidant, lipid peroxidation inhibition and radical scavenging abilities; therefore, it might be used as a natural antioxidant to prevent food deterioration.

Comparative Effects of MMT Clay Modified with Two Different Cationic Surfactants on the Thermal and Rheological Properties of Polypropylene Nanocomposites

Directory of Open Access Journals (Sweden)

Meshal Al-Samhan

2017-01-01

Full Text Available Polypropylene montmorillonite (MMT nanocomposites were prepared by melt blending using two different organoclays modified with imidazolium and alkylammonium surfactants. The imidazolium and ammonium modified organoclays were characterized by the FTIR and SEM analysis. The effect of organic clay (MMT on the physical properties of polypropylene was evaluated, thermal and rheological properties with different filler weight percentage. Differential scanning calorimetric results showed that imidazolium modified clay (IMMT exhibits low melting temperature compared to the ammonium modified clay (AMMT. The crystallinity analysis showed that crystallization improved in all nanocomposites irrespective of surface modification; the thermogravimetric analysis showed that the imidazolium modified polymer composites are more thermally stable than conventional ammonium modified composites. The Transmission Electron Microscopy (TEM analyses indicated that the PP-IMMT composites displayed exfoliated morphologies compared with the intercalated structure in PP-AMMT, and the rheological analysis at 180°C showed an enhancement in the viscoelastic properties as the clay concentration increases. The melt viscosity, crossover modulus, and relaxation times were comparable for both the surface modified composites with two different cations. The imidazolium based surfactant was found to be an effective organic modification for MMT to prepare thermally stable PP/MMT nanocomposites.

Functionalization of Silica Nanoparticles for Polypropylene Nanocomposite Applications

Directory of Open Access Journals (Sweden)

Diego Bracho

2012-01-01

Full Text Available Synthetic silica nanospheres of 20 and 100 nm diameter were produced via the sol-gel method to be used as filler in polypropylene (PP composites. Modification of the silica surface was further performed by reaction with organic chlorosilanes in order to improve the particles interaction with the hydrophobic polyolefin matrix. These nanoparticles were characterized using transmission electronic microscopy (TEM, elemental analysis, thermogravimetric analysis (TGA, and solid-state nuclear magnetic resonance (NMR spectroscopy. For unmodified silica, it was found that the 20 nm particles have a greater effect on both mechanical and barrier properties of the polymeric composite. In particular, at 30 wt%, Young's modulus increases by 70%, whereas water vapor permeability (WVP increases by a factor of 6. Surface modification of the 100 nm particles doubles the value of the composite breaking strain compared to unmodified particles without affecting Young's modulus, while 20 nm modified particles presented a slight increase on both Young's modulus and breaking strain. Modified 100 nm particles showed a higher WVP compared to the unmodified particles, probably due to interparticle condensation during the modification step. Our results show that the addition of nanoparticles on the composite properties depends on both particle size and surface modifications.

2-hydroxyethyl methacrylate composite - polypropylene mesh for preventing peritoneal adhesions in female dogs Compósito 2-hidroxietil dimetacrilato-tela de polipropileno para prevenção de aderências peritoneais em cadelas

Directory of Open Access Journals (Sweden)

Marcelo Seixo de Brito e Silva

2010-08-01

Full Text Available PURPOSE: To evaluate whether the lining facing the visceral side of polypropylene mesh made with 2-hydroxyethyl methacrylate (p(HEMA hydrogel could avoid peritoneal adhesion in female dogs. METHODS: Eight animals (group PP had a polypropylene mesh implanted to correct a defect in the rectal abdominal muscle, whereas in the other group (group PH the polypropylene mesh was coated with p(HEMA composite on the surface facing the peritoneal area. RESULTS: Adhesions were observed on the mesh in 62.5% of the PP group. In the PH group adhesions were present only on the suture lines. CONCLUSION: p(HEMA hydrogel was well tolerated and effective in avoiding visceral and omental adhesions on the surface of the polypropylene mesh.OBJETIVO: Avaliar se o revestimento da face visceral de uma tela de polipropileno com 2-hidroxietil dimetacrilato (p(HEMA poderia evitar aderências peritoniais em cadelas. MÉTODOS: Em oito animais (Grupo PP foram implantadas telas de polipropileno para correção de um defeito do músculo reto abdominal, enquanto em outro grupo (Grupo PH fez-se a implantação de uma tela de polipropileno cuja face peritonial foi revestida por 2-hidroxietil dimetacrilato (p(HEMA. RESULTADOS: Foram observados 62,5% de aderências peritoniais sobre a tela nos animais do Grupo PP, enquanto que no Grupo PH estas não ocorreram, exceto sobre a linha se sutura. CONCLUSÃO: O hidrogel de p(HEMA foi bem tolerado pelos animais e mostrou-se efetivo na prevenção das aderências viscerais e omentais sobre a tela de polipropileno.

Comparison of polypropylene and silicone Ahmed Glaucoma Valves.

Science.gov (United States)

Ishida, Kyoko; Netland, Peter A; Costa, Vital P; Shiroma, Lineu; Khan, Baseer; Ahmed, Iqbal Ike K

2006-08-01

To evaluate and compare the clinical outcomes after implantation of the silicone plate and the polypropylene plate Ahmed Glaucoma Valves. Prospective, multicenter, comparative series. A total of 132 patients with uncontrolled glaucoma were treated with either the silicone or polypropylene Ahmed Glaucoma Valve implant. Success was defined according to 2 criteria: (1) intraocular pressure (IOP) of 6 mmHg or more or 21 mmHg or less, and (2) IOP reduction of at least 30% relative to preoperative values. Eyes requiring further glaucoma surgery, including cyclophotocoagulation, or showing loss of light perception were classified as failures. Average follow-up was 12.8 months (range, 6-30 months) for the silicone plate group and 14.5 months (range, 6-30 months) for the polypropylene plate group (P = 0.063). At the last follow-up examination, the mean IOP was 13.8+/-3.9 mmHg and 17.3+/-6.5 mmHg (PAhmed Glaucoma Valve (model FP7) showed improved IOP reduction compared with the polypropylene (model S2) implant. Differences observed in mean IOP, success rate, and complications suggest that plate material may influence clinical outcome.

Additive manufacturing with polypropylene microfibers.

Science.gov (United States)

Haigh, Jodie N; Dargaville, Tim R; Dalton, Paul D

2017-08-01

The additive manufacturing of small diameter polypropylene microfibers is described, achieved using a technique termed melt electrospinning writing. Sequential fiber layering, which is important for accurate three-dimensional fabrication, was achieved with the smallest fiber diameter of 16.4±0.2μm obtained. The collector speed, temperature and melt flow rate to the nozzle were optimized for quality and minimal fiber pulsing. Of particular importance to the success of this method is appropriate heating of the collector plate, so that the electrostatically drawn filament adheres during the direct-writing process. By demonstrating the direct-writing of polypropylene, new applications exploiting the favorable mechanical, stability and biocompatible properties of this polymer are envisaged. Copyright © 2017. Published by Elsevier B.V.

Radiation-induced grafting of acrylic acid onto polypropylene film and its biodegradability

Science.gov (United States)

Mandal, Dev K.; Bhunia, Haripada; Bajpai, Pramod K.; Chaudhari, C. V.; Dubey, K. A.; Varshney, L.

2016-06-01

Polypropylene based commodity polyolefins are widely used in packaging, manufacturing, electrical, pharmaceutical and other applications. The aim of the present work is to study the effect of grafting of acrylic acid on the biodegradability of acrylic acid grafted polypropylene. The effect of different conditions showed that grafting percentage increased with increase in monomer concentration, radiation dose and inhibitor concentration but decreased with increase in radiation dose rate. The maximum grafting of 159.4% could be achieved at optimum conditions. The structure of grafted polypropylene films at different degree of grafting was characterized by EDS, FTIR, TGA, DSC, SEM and XRD. EDS studies showed that the increase in acrylic acid grafting percentage increased the hydrophilicity of the grafted films. FTIR studies indicated the presence of acrylic acid on the surface of polypropylene film. TGA studies revealed that thermal stability decreased with increase in grafting percentage. DSC studies showed that melting temperature and crystallinity of the grafted polypropylene films lower than polypropylene film. SEM studies indicated that increase in acrylic acid grafting percentage increased the wrinkles in the grafted films. The maximum biodegradability could be achieved to 6.85% for 90.5% grafting. This suggested that microorganisms present in the compost could biodegrade acrylic acid grafted polypropylene.

Effect of nanosilica particles on polypropylene polymer modified asphalt mixture performance

Directory of Open Access Journals (Sweden)

Nura Bala

2018-06-01

Full Text Available The current study was conducted to investigate the effect of nanosilica particles on the performance characteristics of polymer modified asphalt binders. In this study, control 80/100 binder were modified with polypropylene polymer and nanosilica particles at concentration of 0%–4%. Both nanosilica particles and polypropylene polymer were added by weight of total bitumen content. The asphalt performance tests flexural four point beam fatigue test, indirect tensile strength, indirect tensile stiffness modulus and draindown tests are conducted to evaluate the effect of nanosilica particles. The results of the study shows that nanosilica particles improves the fatigue properties of polypropylene polymer modified binder. This indicates that nanosilica particles have significant effect on improving the performance properties of polymer modified binders. Also, the result reveals that thermoplastic polymer polypropylene with nanosilica particles when used as bitumen modifiers improve the performance and durability of asphalt mixtures. Keywords: Polypropylene, Fatigue cracking, Stiffness modulus, Modified asphalt, Draindown

Polypropylene Track Membranes for Mikro and Ultrafiltration of Chemically Aggressive Agents

CERN Document Server

Kravets, L I; Apel, P Yu

2000-01-01

A production process for track membranes on the basis of chemically resistant polymer polypropylene has been developed. Research in all stages of the formation of the polypropylene track membranes has been conducted: the main principles of the process of chemical etching of polypropylene irradiated with accelerated ions have been investigated, the most effective structure of the etchant for a selective etching of the heavy ion tracks has been selected, the parameters of etching have been optimized. A method for sensibilization of latent tracks in polypropylene by effect of solvents has been developed. It helps to reach a significant increase in etching selectivity. A method for destruction of an absorbed chromocontaining layer on the surface of polypropylene track membranes formed during etching has been elaborated. Experimental samples of the membranes for micro and ultrafiltration have been obtained and their properties have been studied in course of their exploitation in chemically aggressive agents. For t...

Synergistic effects of iron powder on intumescent flame retardant polypropylene system

Directory of Open Access Journals (Sweden)

2009-06-01

Full Text Available The effects of iron powder as a synergistic agent on the flame retardancy of intumescent flame retardant polypropylene composites (IFR-PP were studied. The thermogravimetric analysis (TGA and cone calorimeter (CONE were used to evaluate the synergistic effects of iron powder (Fe. The TGA data showed that Fe could enhance the thermal stability of the IFR-PP systems at high temperature and effectively increase the char residue formation. The CONE results revealed that Fe and IFR could clearly change the decomposition behavior of PP and form a char layer on the surface of the composites, consequently resulting in efficient reduction of the flammability parameters, such as heat release rate (HRR, mass loss (ML, Mass loss rate (MLR, total heat release (THR, carbon monoxide and so on. Thus, a suitable amount of Fe plays a synergistic effect in the flame retardancy of IFR composites.

STRUCTURAL EVOLUTION AND COMPOSITION CHANGE IN THE SURFACE REGION OF POLYPROPYLENE/CLAY NANOCOMPOSITES ANNEALED AT HIGH TEMPERATURES

Institute of Scientific and Technical Information of China (English)

Zhe Wang; Rong-jun Song; Xiao-hua Du; Xiao-yu Meng; Zhi-wei Jiang; Tao Tang

2009-01-01

A model experiment was done to clear the formation mechanism of protective layers during combustion of polypropylene (PP)/organically modified montmorillonite (OMMT) nanocomposites. The investigation was focused on the effects of annealing temperature on the structural changes and protective layer formation. The decomposition of OMMT and degradation of PP/OMMT nanocomposites were characterized by means of thermogravimetric analysis (TGA). The structural evolution and composition change in the surface region of PP/OMMT nanocomposites during heating were monitored by means of X-ray photoelectron spectroscopy (XPS), ATR-FTIR and field emission scanning electron microscopy (FESEM). The results showed that the formation of the carbonaceous silicate barrier in the surface region of PP/OMMT nanocomposites resulted from the following three processes: (1) The formation of strong acid sites on the MMT sheets, which could promote the degradation of PP and the carbonization of its degradation products; (2) The gases and gas bubbles formed by decomposition of the surfactant and degradation of PP, which pushed the molten sample to the surface; (3) The degradation of PP and the carbonization of the degradation products, which led to accumulation of MMT sheets tightly linked by the char in the surface region.

Physical and dielectric properties of irradiated polypropylene and poly(ethylene terephthalate)

International Nuclear Information System (INIS)

Kita, H.; Okamoto, K.

1986-01-01

The effect of high-energy electron irradiation in air and in nitrogen on the physical and dielectric properties of polypropylene and poly(ethylene terephthalate) has been studied by measurements of electric strength, dielectric constant, dissipation factor, tensile strength, gel fraction and molecular weight distribution. Electric strength of polypropylene was improved by irradiation, while dielectric properties of poly(ethylene terephthalate) were virtually unaffected by irradiation of 1.0-20 Mrad. Possible mechanisms for increasing electric strength are discussed from the point of view of degradation and oxidation taking place simultaneously with crosslinking of polypropylene. The maximum dose level to improve the electric strength of polypropylene is determined to be about 5 Mrad. (author)

Co-60 gamma radiation assisted diffusion of iodine in polypropylene

Energy Technology Data Exchange (ETDEWEB)

Mathakari, N.L.; Bhoraskar, V.N. [Microtron Accelerator Laboratory, Department of Physics, University of Pune, Pune, Maharashtra 411007 (India); Dhole, S.D., E-mail: sanjay@physics.unipune.ernet.i [Microtron Accelerator Laboratory, Department of Physics, University of Pune, Pune, Maharashtra 411007 (India)

2010-09-15

Thin films of polypropylene having dimensions 50 mm x 15 mm x 350 {mu}m were immersed in 1 N iodine solution and then irradiated with Co-60 gamma radiation for the periods of 48, 96 and 144 h at the doses varying from 14.4 to 43.2 kGy. The films were also kept immersed in iodine solution for similar periods but without irradiation. Furthermore, the films were also directly-irradiated with Co-60 gamma radiation for similar periods and doses. The radiation-iodinated, plain-iodinated and directly-irradiated samples were characterized by using various techniques such as weight gain EDS, SEM, FTIR, UV-visible spectroscopy, contact angle and XRD. Weight gain, EDS and SEM collectively reveal that gamma irradiation enhances iodine intake in polypropylene. FTIR, EDS and contact angle measurements indicate that presence of iodine during irradiation resists radiation induced carbonylation of polypropylene. FTIR also shows presence of HOI (Hypoiodous acid) species instead of expected C-I bonds. UV-visible analysis unambiguously shows that presence of iodine enhances radiation induced band gap reduction process of polypropylene. XRD indicates that iodine decreases the crystallinity of polypropylene.

A new constitutive model for prediction of impact rates response of polypropylene

Directory of Open Access Journals (Sweden)

Buckley C.P.

2012-08-01

Full Text Available This paper proposes a new constitutive model for predicting the impact rates response of polypropylene. Impact rates, as used here, refer to strain rates greater than 1000 1/s. The model is a physically based, three-dimensional constitutive model which incorporates the contributions of the amorphous, crystalline, pseudo-amorphous and entanglement networks to the constitutive response of polypropylene. The model mathematics is based on the well-known Glass-Rubber model originally developed for glassy polymers but the arguments have herein been extended to semi-crystalline polymers. In order to predict the impact rates behaviour of polypropylene, the model exploits the well-known framework of multiple processes yielding of polymers. This work argues that two dominant viscoelastic relaxation processes – the alpha- and beta-processes – can be associated with the yield responses of polypropylene observed at low-rate-dominant and impact-rates dominant loading regimes. Compression test data on polypropylene have been used to validate the model. The study has found that the model predicts quite well the experimentally observed nonlinear rate-dependent impact response of polypropylene.

ENERGY CONVERSION FROM WOODY BIOMASS STUFF: POSSIBLE MANUFACTURE OF BRIQUETTED CHARCOAL FROM SAWMILL-GENERATED SAWDUST

Directory of Open Access Journals (Sweden)

Han Roliadi

2006-07-01

Full Text Available There are three dominant kinds of wood industries in Indonesia which consume huge amount of  wood materials as well as generate considerable amount of  woody waste stuffs, i.e. sawmills, plywood, and pulp/paper. For the two latest industries, their wastes to great extent have been reutilized in the remanufacturing process, or burnt under controlled condition to supplement their energy needs in the corresponding factories, thereby greatly alleviating environmental negative impacts.  However, wastes from sawmills (especially sawdust still often pose a serious environmental threat, since they as of this occasion are merely dumped on sites, discarded to the stream, or merely burnt, hence inflicting dreadful stream as well as air pollutions. One way to remedy those inconveniences is by converting the sawdust into useful product, i.e. briquetted charcoal, as has been experimentally tried. The charcoal was at first prepared by carbonizing the sawdust wastes containing a mixture of the ones altogether from the sawing of seven particular Indonesia's wood species, and afterwards was shaped into the briquette employing various concentrations of starch binder at two levels (3.0 and 5.0 % and also various hydraulic pressures (1.0, 2.5, and 5.0 kg/cm2.  Further, the effect of those variations was examined on the yield and qualities of the resulting briquetted charcoal. The results revealed that the most satisfactory yield and qualities of the briquetted sawdustcharcoal were acquired at 3 % starch binder concentration with 5.0 kg/cm2 hydraulic pressure. As such, the briquette qualities were as follows: density at 0.60 gram/cm3, tensile strength 15.27 kg/cm2, moisture content 2.58 %, volatile matter 23.35 %, ash content 4.10 %, fixed carbon 72.55 %, and calorific value 5,426 cal/gram. Those qualities revealed that the experimented briquetted sawdust charcoal could be conveniently used as biomass-derived fuel.

Effects of Aeration of Sawdust Cultivation Bags on Hyphal Growth of Lentinula edodes.

Science.gov (United States)

Lee, Hwa-Yong; Ham, Eun-Ju; Yoo, Young-Jin; Kim, Eui-Sung; Shim, Kyu-Kwang; Kim, Myung-Kon; Koo, Chang-Duck

2012-09-01

The effects of aeration through lid filters on the hyphal growth of Lentinula edodes (oak mushroom) in sawdust cultivation bags were investigated. The aeration treatment levels were traditional 27 mm hole cotton plugs, cotton balls and combinations of seven hole sizes × two hole positions (up and under) in the lids covering plastic bags containing 1.4 kg sawdust medium at 63% moisture that had been autoclaved for one hour and inoculated with sawdust spawn of L. edodes strain 921. Aeration treatment effects were measured based on the CO(2) concentration at the 15th wk, as well as the hyphal growth rate and degree of weight loss of bags every 14 days for 15 wk. In bags with traditional cotton plugs, the CO(2) concentration was 3.8 ± 1.3%, daily mean hyphal growth was 2.3 ± 0.6 mm and daily mean weight loss was 0.84 ± 0.26 g. In the bags with 15 mm diameter holes, the CO(2) concentration was 6.0 ± 1.6%, daily hyphal growth was 2.8 ± 0.2 mm and daily weight loss was 0.86 ± 0.4 g. The bags with 15 mm holes had a higher CO(2) concentration and lower water loss than bags with other hole sizes, but the hyphal growth was not significantly different from that of other bags. The weight loss of bags increased proportionally relative to the lid hole sizes. Taken together, these results indicate that traditional cotton plugs are economically efficient, but 15 mm hole lids are the most efficient at maintaining hyphal growth and controlling water loss while allowing CO(2) emissions.

Sawdust and fruit residues of Central Amazonian for Panus strigellus spawn’s production Serragem e resíduos de frutos da Amazônia Central para produção de semente-inóculo de Panus strigellus

Directory of Open Access Journals (Sweden)

Ruby Vargas-Isla

2012-06-01

Full Text Available

The objective of this work was to perform a screening of residues of forest species of the Central Amazon to prepare spawn of the edible mushroom Panus strigellus. Sawdust substrates from 11 forest species were tested. Then supplementation with beer yeast, cereal bran and regional fruit residues in sawdust:supplementation relation (5:1 and 10:1 were evaluated. Mycelial growth of P. strigellus occurred in all the substrates composed of the Amazonian forests species, suggesting that all have potential for use in spawn formulation and/or cultivation of this edible mushroom. Among these species the substrate formulated with Simarouba amara sawdust promoted higher mycelial growth (P<0.05. The formulation of S. amara supplemented with Astrocaryum aculeatum fruit shell bran (10:1 presented the best supplementation alternative among regional fruit residues. Three types of packaging for spawn preparation were evaluated, and the polypropylene sack (32×45 cm was considered the most appropriate. Simarouba amara sawdust and A. aculeatum fruit shell are readily available in the North region, and the results demonstrating that these residues might substitute Eucalyptus sp. sawdust and rice bran, commonly used in the South and Southeast of Brazil for mushroom spawn production.

doi: 10.4336/2012.pfb.32.70.07

Neste trabalho objetivou-se realizar uma triagem de resíduos de espécies florestais da Amazônia Central para o preparo da semente-inóculo do cogumelo comestível Panus strigellus. Foram testados substratos de serragem de 11 espécies florestais. Em seguida, suplementação com levedura de cerveja, farelos de cereais e resíduos de frutas regionais foram avaliados na relação serragem:suplemento (5:1 e 10:1. O crescimento micelial de P. strigellus ocorreu em todos os substratos formulados com espécies florestais da Amazônia, apresentando potencial de uso na formulação da semente-inóculo e/ou cultivo deste fungo comestível. Entre

Thermal degradation kinetics and estimation of lifetime of radiation grafted polypropylene films

International Nuclear Information System (INIS)

Mandal, Dev K.; Bhunia, Haripada; Bajpai, Pramod K.; Bhalla, Vinod Kumar

2017-01-01

In this research work, thermal stability and degradation behavior of acrylic acid grafted polypropylene (PP-g-PAAc) films were investigated by using thermogravimetric (TGA) analysis at four different heating rates 5, 10, 15 and 20 °C/min over a temperature range of 40–550 °C in nitrogen atmosphere. The kinetic parameters namely activation energy (E a ), reaction order (n) and frequency factor (Z) were calculated by three multiple heating rate methods. The thermal stability of PP-g-PAAc films is found to decrease with increase in degree of grafting. The TGA data and thermal kinetic parameters were also used to predict the lifetime of grafted PP films. The estimated lifetime of neat PP as well as grafted PP decreased with increase in temperature by all the three methods. Studies also indicated that E a and lifetime of PP-g-PAAc films decreased with increase in degree of grafting, which may also be helpful in biodegradation of grafted PP films. - Highlights: • Thermal stability of grafted polypropylene films have been observed lower than for neat polypropylene film. • Multiple heating rate methods have been used for determination of activation energy. • Activation energies of grafted polypropylene films were lower than polypropylene film. • The lifetimes of grafted polypropylene films were shorter than for neat polypropylene film.

Determination of Partition Coefficients of Selected Model Migrants between Polyethylene and Polypropylene and Nanocomposite Polypropylene

Directory of Open Access Journals (Sweden)

Pablo Otero-Pazos

2016-01-01

Full Text Available Studies on nanoparticles have focused the attention of the researchers because they can produce nanocomposites that exhibit unexpected hybrid properties. Polymeric materials are commonly used in food packaging, but from the standpoint of food safety, one of the main concerns on the use of these materials is the potential migration of low molecular substances from the packaging into the food. The key parameters of this phenomenon are the diffusion and partition coefficients. Studies on migration from food packaging with nanomaterials are very scarce. This study is focused on the determination of partition coefficients of different model migrants between the low-density polyethylene (LDPE and polypropylene (PP and between LDPE and nanocomposite polypropylene (naPP. The results show that the incorporation of nanoparticles in polypropylene increases the mass transport of model migrants from LDPE to naPP. This quantity of migrants absorbed into PP and naPP depends partially on the nature of the polymer and slightly on the chemical features of the migrant. Relation (RPP/naPP between partition coefficient KLDPE/PP and partition coefficient KLDPE/naPP at 60°C and 80°C shows that only BHT at 60°C has a RPP/naPP less than 1. On the other hand, bisphenol A has the highest RPP/naPP with approximately 50 times more.

Novel polypropylene biocomposites reinforced with carbon nanotubes and hydroxyapatite nanorods for bone replacements

Energy Technology Data Exchange (ETDEWEB)

Liao, Cheng Zhu; Li, Kai [Department of Physics and Materials Science, City University of Hong Kong, Tat Chee Avenue, Kowloon (Hong Kong); Wong, Hoi Man; Tong, Wing Yin; Yeung, Kelvin Wai Kwok [Department of Orthopedics and Traumatology, The University of Hong Kong (Hong Kong); Tjong, Sie Chin, E-mail: aptjong@cityu.edu.hk [Department of Physics and Materials Science, City University of Hong Kong, Tat Chee Avenue, Kowloon (Hong Kong)

2013-04-01

Multi-walled carbon nanotubes (MWNTs) of 0.1 and 0.3 wt.% and hydoxyapatite nanorods (nHAs) of 8–20 wt.% were incorporated into polypropylene (PP) to form biocomposites using melt-compounding and injection molding techniques. The structural, mechanical, thermal and in vitro cell responses of the PP/MWNT–nHA hybrids were investigated. Tensile and impact tests demonstrated that the MWNT additions are beneficial in enhancing the stiffness, tensile strength and impact toughness of the PP/nHA nanocomposites. According to thermal analysis, the nHA and MWNT fillers were found to be very effective to improve dimensional and thermal stability of PP. The results of osteoblast cell cultivation and dimethyl thiazolyl diphenyl tetrazolium (MTT) tests showed that the PP/MWNT–nHA nanocomposites are biocompatible. Such novel PP/MWNT–nHA hybrids are considered to be potential biomaterials for making orthopedic bone implants. - Highlights: ► Multiwalled carbon nanotubes (MWNTs) and hydroxyapatite nanorods (nHA) are used as hybrid fillers to reinforce polypropylene. ► MWNT additions are beneficial in enhancing tensile strength and stiffness of PP/nHA composites. ► Hybridizing MWNT with nHA fillers enhance thermal and dimensional stability of PP significantly. ► Hybridizing MWNT with nHA greatly enhance osteoblast adhesion and proliferation. ► PP/MWNT–nHA composites show attractive applications as load-bearing materials in orthopedics.

Development of more friendly food packaging materials base on polypropylene through blending with polylacticacid

Science.gov (United States)

Setiawan, Achmad Hanafi; Aulia, Fauzan

2017-01-01

The commonly food packaging materials today is used a thin layer plastic or film, which is made of a synthetic polymer, such as polypropylene (PP). However, the use of these polymers has a negative impact on the environment, because the synthetic polymer is difficult to degrade naturally by the biotic components such as micro-organisms decomposers and abiotic components such as the sunshine. The use of the biodegradable polymeric material will reduce the use of synthetic polymer products, thereby reducing plastic waste pollution at relatively low cost, it is expected to produce positive effects both for the environment and in terms of economy. PLA is a biodegradable polymer that can be substituted totally or partially to synthetic polymers as far as could fulfill the main function of packaging in the protection and preservation of food. Increasing PLA content in polypropylene blend will affect to the increasing in its water absorption and also its biodegradable. 20% PLA may the optimum composition of poly-blend for food packaging.

A Comprehensive Study of the Polypropylene Fiber Reinforced Fly Ash Based Geopolymer.

Directory of Open Access Journals (Sweden)

Navid Ranjbar

Full Text Available As a cementitious material, geopolymers show a high quasi-brittle behavior and a relatively low fracture energy. To overcome such a weakness, incorporation of fibers to a brittle matrix is a well-known technique to enhance the flexural properties. This study comprehensively evaluates the short and long term impacts of different volume percentages of polypropylene fiber (PPF reinforcement on fly ash based geopolymer composites. Different characteristics of the composite were compared at fresh state by flow measurement and hardened state by variation of shrinkage over time to assess the response of composites under flexural and compressive load conditions. The fiber-matrix interface, fiber surface and toughening mechanisms were assessed using field emission scan electron microscopy (FESEM and atomic force microscopy (AFM. The results show that incorporation of PPF up to 3 wt % into the geopolymer paste reduces the shrinkage and enhances the energy absorption of the composites. While, it might reduce the ultimate flexural and compressive strength of the material depending on fiber content.

Radiation modification and interaction mechanism of polypropylene and polyethylene by protons and electrons

International Nuclear Information System (INIS)

Wang Guanghou

1988-10-01

A systematic investigation of radiation effects on isotactic polypropylene (PP) and low-density polyethylene (PE) films by protons and electrons is reported. Electrons can make polyethylene cross-linked and polypropylene crached while protons can improve the PP mechanical properties and deteriorate polyethylene with increasing the irradiation dose. The structural analysis shows that conversion between α and β phases occurs and the crystallinity remains constant in the electron-irradiated polypropylene whereas the network structure is formed by allyl-type radicals in the e - -irradiated polyethylene. The infrared spectra indicate that conformational changes have taken place in the polypropylene under proton bombardment, such as the transition from an ordered to a disordered state in the crystalline region, the formation of double bonds as well as trans-conformations. This leads to the cross-linking between macromolecules of polypropylene at the proper irradiation doses, thus enhancing its mechanical properties. The cross-linking of polypropylene by proton bombardment observed and its properties may have some potential applications

THE FTIR STUDIES OF PHOTO-OXIDATIVE DEGRADATION OF POLYPROPYLENE

Institute of Scientific and Technical Information of China (English)

WEN Zaiqing; HU Xingzhou; SHEN Deyan

1988-01-01

The photo-oxidative degradation process of polypropylene film containing iron ions was investigated via FTIR and absorbance substraction technique. It is shown that the iron ions play an important role in the decomposition of hydroperoxide and the increase of the degradation rate of polypropylene film. Theamorphous region of PP film undergoes degradation prior to the crystalline one.

Processing of Polypropylene-Organic Montmorillonite Nanocomposite by Equal Channel Multiangular Extrusion

Directory of Open Access Journals (Sweden)

V. A. Beloshenko

2016-01-01

Full Text Available By the example of polypropylene-organic montmorillonite composite (PP-OMMT, the abilities of the method of equal channel multiangular extrusion have been studied with respect to the modification of the structure and the properties of polymeric nanocomposites. With using X-ray structure analysis, TEM, DSC, and dilatometry, it has been demonstrated that this kind of processing provides an additional intercalation of the polymer into OMMT tactoids with the succeeding exfoliation and facilitates an increase in the aspect ratio, the degree of platelet orientation, the crystalline lamellar thickness, and a decrease in the dispersion of the crystallite thickness, as well as the formation of biaxial orientation of the OMMT and PP crystals. The observed structure rearrangements determine enhanced microhardness, ductility, and the heat distortion temperature of the PP-OMMT composite.

Application to refrigerator plastics by mechanical recycling from polypropylene in waste-appliances

International Nuclear Information System (INIS)

Ha, Kyung Ho; Kim, Moon Saeng

2012-01-01

Highlights: → Polypropylene is mechanically recycled from waste-appliances. → Recycled polypropylene (RPP) is impact enhanced polypropylene with ethylene-propylene rubber (EPR). → Performance evaluation shows that RPP is applicable to refrigerator plastics. -- Abstract: For the application to refrigerator plastics by mechanical recycling from polypropylene (PP) in waste-appliances, it needs to identify the degradation and heterogeneity of recycled polypropylene (RPP). It is applicable the thermal analysis such as differential scanning calorimetry (DSC), thermo-gravimetric analysis (TGA), spectroscopic analysis such as Fourier Transform Infrared (FTIR) and morphological analysis such as scanning electronic microscope (SEM). The analysis results show that RPP from waste-appliances is the polyethylene (PE) and polypropylene (PP) copolymer enhanced impact property (Impact-PP) and it is possible to apply refrigerator plastics with good impact property at low temperature. Finally, the performance evaluation of RPP is estimated by Gel Permeation Chromatography (GPC) analysis and is performed by the various mechanical and physical testing methods. It shows that RPP has relatively high molecular weight and balanced properties with strength and toughness. It is expected that RPP by the mechanical recycling from waste-appliances will have about 50% cost-merit.

A study on the trans-crystallisation behaviour of flax fibre reinforced polypropylene composites and effect on mechanical properties

NARCIS (Netherlands)

George, J.; Garkhail, S.K.; Wieland, B.; Peijs, A.A.J.M.; Mattoso, L.H.C.

2000-01-01

The effect of flax fiber reinforcement on crystn. behavior of polypropylene (PP) was investigated using a hot-stage optical microscope. To follow the crystn. kinetics, cooling rate and crystn. temps. were varied. Flax fibers with different processing history e.g. green flax, Duralin flax, alkali and

Flame Retardancy and Mechanical Properties of Kenaf Filled Polypropylene (PP) Containing Ammonium Polyphosphate (APP)

International Nuclear Information System (INIS)

Atikah Ismail; Azman Hassan; Aznizam Abu Bakar; Jawaid, M.

2013-01-01

The effects of ammonium polyphosphate (APP) as flame retardant and kenaf as fillers on flammability, thermal and mechanical properties of polypropylene (PP) composites were determined. Test specimens were prepared by using a co-rotating twin screw extruder for the compounding process followed by injection molding. The flame retardancy of the composites was determined by using limiting oxygen index (LOI) test. Addition of flame retardant into kenaf-PP composites significantly increased the LOI values that indicated the improvement of flame retardancy. Thermogravimetric analysis was done to examine the thermal stability of the composites. The addition of kenaf fiber in PP composites decreased the thermal stability significantly but the influence of APP on thermal properties of the kenaf-filled PP composites was not significant. The flexural strength and modulus of composites increased with the addition of APP into kenaf filled PP composite. The addition of APP into kenaf filled PP causes increase in the impact strength while increasing the APP content in the kenaf filled PP composite show decrease in impact strength. (author)

Total Phenolics, Flavonoids, Tannin Contents and Antioxidant Properties of Pleurotus ostreatus Cultivated on Different Wastes and Sawdust

Directory of Open Access Journals (Sweden)

Ayşenur Yılmaz

2017-01-01

Full Text Available In this study, the usage possibilities of some agro-industrial wastes such as; peanut wastes, potatoes farm wastes, walnut and orange tree sawdust in Pleurotus ostreatus cultivation were investigated and total phenolic, flavonoid, condensed tannin content and antioxidant properties of these methanolic mushroom extracts were examined. For the determination of the total phenolic contents, the Folin-Ciocalteau procedure was used. The content of total flavonoid present in the methanolic extracts was measured using a spectrophotometric assay. Condensed tannins were determined according to the method by Julkunen-Tıtto. The antioxidant capacity was determined using ferric reducing antioxidant power (FRAP and free radical scavenging activity of DPPH. The highest total phenolic content (2.672 ± 0.003 mg GAE/g was found in mushroom cultivated on walnut sawdust. The highest condensed tannin (1.011 ± 0.088 CE mg/g and ferric reducing antioxidant power (FRAP (12.332 ± 0.017 μmol FeSO4.7H2O/g were observed in the same mushroom extract. The highest total flavonoid and free radical scavenging activity of DPPH were found in extract of mushroom cultivated on potatoes handle. Bioactive properties of P. ostreatus cultivated on walnut tree sawdust were generally exhibited remarkable results.

Application of Glass Fiber Waste Polypropylene Aggregate in Lightweight Concrete – thermal properties

Science.gov (United States)

Citek, D.; Rehacek, S.; Pavlik, Z.; Kolisko, J.; Dobias, D.; Pavlikova, M.

2018-03-01

Actual paper focus on thermal properties of a sustainable lightweight concrete incorporating high volume of waste polypropylene aggregate as partial substitution of natural aggregate. In presented experiments a glass fiber reinforced polypropylene (GFPP) which is a by-product of PP tubes production, partially substituted fine natural silica aggregate in 10, 20, 30, 40 and 50 mass %. Results were compared with a reference concrete mix without plastic waste in order to quantify the effect of GFPP use on concrete properties. Main material physical parameters were studied (bulk density, matrix density without air content, and particle size distribution). Especially a thermal transport and storage properties of GFPP were examined in dependence on compaction time. For the developed lightweight concrete, thermal properties were accessed using transient impulse technique, where the measurement was done in dependence on moisture content (from the fully water saturated state to dry state). It was found that the tested lightweight concrete should be prospective construction material possessing improved thermal insulation function and the reuse of waste plastics in concrete composition was beneficial both from the environmental and financial point of view.

Study of modified polypropylene nanocomposites by gamma irradiation with addition of cloisite clay

International Nuclear Information System (INIS)

Komatsu, Luiz G.H.; Oliani, Washington L.; Parra, Duclerc F.; Lugao, Ademar B.

2011-01-01

Nanomaterials, and, in particular, nanoreinforcements for polymer composites have been the subject of intense research, development and commercialization. Clay-containing polymeric nanocomposites (CPNCs) are used as either functional or structural materials, large-volume CPNCs with a commodity or engineering polymer as the matrix, where the mechanical behavior is the main concern (followed by gas-vapor barrier properties, flammability, etc.). This work concerns to the study of the mechanical, thermal and morphological behavior nanocomposite, (HMSPP) Polypropylene High Melt Strength (obtained at dose of 12.5 kGy) and addition of 5 and 10 wt% of organoclay with Cloisite 20A nanocomposite. Agent compatibilizer polypropylene-graft, (PP-g-AM) was added at 3% concentration and the clay was dispersed through melt intercalation technique using a twin-screw extruder). We observed an increase in traction rupture. The mechanical behavior was evaluated by strength, the thermal behavior were evaluated by the technique of differential scanning calorimetry, the morphology of the nanocomposites was studied by scanning electron microscopy, melt flow index and Fourier transformed infrared spectroscopy in nanocomposites Cloisite 20 A at 10% wt. (author)

Enzymatic saccharification and structural properties of industrial wood sawdust: Recycled ionic liquids pretreatments

International Nuclear Information System (INIS)

Auxenfans, Thomas; Buchoux, Sébastien; Larcher, Dominique; Husson, Gérard; Husson, Eric; Sarazin, Catherine

2014-01-01

Highlights: • 1-Ethyl-3-metylimidazolium acetate is an effective catalyst for pretreatment of hardwood and softwood sawdust. • Regeneration of cellulosic fraction from ionic liquid is discussed. • 1-Ethyl-3-methylimidazolium acetate can be reused at least 7 times without loss of its efficiency. • Removal of extractives and lignin with slight cellulose and xylan losses were observed. • Better cellulase accessibility to cellulose thanks to the expansion of the powder and the creation of a large porous volume. - Abstract: Wood residues constitute a promising challenge for biochemical processing into bioethanol and chemicals with competitive costs. Here, we report the impacts of pretreatments in a hydrophilic ionic liquid ([C2mim][OAc]), onto the physicochemical properties and enzymatic saccharification of softwood (spruce) and hardwood (oak) sawdust. Enzymatic saccharification of IL- pretreated sawdust is significantly increased (up to 7 times) when compared to untreated ones. Methanol, ethanol or water can be used as polar anti-solvent for the recovery of a cellulose rich fraction after dissolution in IL (i.e regeneration step) without any effect on enzymatic saccharification. Chemical, textural and structural modifications possibly induced by the IL pretreatments have been investigated through various means (Infra-red spectroscopy, NMR, X-ray diffraction) in order to correlate the observed modifications in enzymatic saccharification. This mild pretreatment seemed to mainly act in a breakdown of lignocellulosic organization leading to better cellulase accessibility to cellulose thanks to the expansion of the powder and the creation of a large porous volume (5 times more apparent porous volume). Partial removal of lignin and extractives may also contribute to the best enzymatic performances. The recyclability and reuse up to 7 times of [C2mim][OAc] is shown without the need of strictly anhydrous conditions and any alteration of the pretreatment

Preparation of Highly Porous Binderless Active Carbon Monoliths from Waste Aspen Sawdust

Directory of Open Access Journals (Sweden)

Dawei Li

2014-01-01

Full Text Available Waste aspen sawdust was used as a precursor to prepare binderless active carbon monoliths (ACMs with high porosities. The ACMs were prepared by activation with H3PO4 at different activation temperatures (500 to 700 °C and retention times (1 to 3 h. Their morphologies, yields, textural properties, and microcrystalline structures were investigated using scanning electron microscopy (SEM, an analytical balance, N2 adsorption/desorption techniques, and X-ray diffraction (XRD. The results indicated that waste aspen sawdust could be successfully converted into highly porous binderless ACMs. The apparent specific surface area (SSA and yield of ACMs were in the range of 688 to 951 m2/g and 26.6 to 36.2%, respectively. Highly microporous ACMs with a micropore percentage of 91.1%, apparent specific surface area of 951 m2/g, pore volume of 0.481 mL/g, and bulk density of 0.56 g/mL could be produced by activation at 700 °C for 1 h. Increasing the activation temperature or retention time increased the specific surface area, pore volume, and turbostratic degree, but decreased the yield.

The Effectiveness of Polydimethylsiloxane (PDMS) and Hexamethyldisiloxane (HMDSO) As Compatibilizer on the Preparation of Betel Nut Fiber (BNF) and Polypropylene (PP) /Polystyrene (PS) Wood Composites

International Nuclear Information System (INIS)

Nurul Izzaty Khalid; Azizah Baharum; Siti Sarah Ramli; Siti Norhana Mohd Nor

2014-01-01

This research was carried out to investigate the effectiveness of polydimethylsiloxane (PDMS) and hexamethyldisiloxane (HMDSO) as compatibilizing agent in producing wood composites of betel nut fiber/ polypropylene (BNF/ PP) and betel nut fiber/ polystyrene (BNF/ PS). Wood composite was prepared by blending 40 % of matrix polymer and 60 % of treated and untreated BNF using internal mixer Brabender Plasticoder at 170 degree Celsius with 50 rpm rotor speed for 13 minutes. The treatment was done prior to blending the materials by immersing the BNF in PDMS and HMDSO solutions with 1 %, 3 % and 5 % of concentrations for 24 hours. The effects of 1 % HMDSO treatment on BNF/ PP composite contributed to high flexure strength and impact strength which are 19.2 MPa and 7.9 kJ/M2 respectively while the percentage of water absorption showed the minimum value of 6.7%. The impact strength of BNF/ PS composite treated with 3% HMDSO showed maximum value that is 4.7 kJ/ M 2 and minimum percentage of water absorption, 6.8 %. However, the flexure strength of untreated BNF/ PS composite is higher than treated BNF/ PS composite with value of 4.7 MPa. The morphology of treated BNF/ PP composites from SEM micrographs showed better interface interaction between fibers and matrices. FTIR spectra showed the presence of siloxane groups such as Si-O, Si-CH 3 , Si-(CH 3 ) and Si(CH 3 ) as a result of HMDSO and PDMS treatment. Based on the characterization analysis, HMDSO treated composite of BNF/ PP showed more effective interfacial interaction between BNF and matrices. (author)

Improvement of radiation resistance of polypropylene by blending with polyethylene and polystyrene

International Nuclear Information System (INIS)

Al Aji, Z.

2001-01-01

The use of polypropylene in production of medical component and packaging materials makes it an interesting material for applied research. Since the use of ethylene oxide for sterilization of medical components will be forbidden in the next future because of its carcinogens effect. Therefore, another alternative sterilization methods are required. The use of Gamma radiation is already established for sterilization of some medical components, this technique causes change in the physical mechanical properties of polypropylene, which makes the addition of stabilizers necessary. In this work, blends of domestically used polymers, polypropylene, linear low-density polyethylene, and polystyrene/butadiene were prepared in order to improve the radiation resistance of polypropylene; naphthalene was also used as an additive

Bioremediation of contaminated mixtures of desert mining soil and sawdust with fuel oil by aerated in-vessel composting in the Atacama Region (Chile)

International Nuclear Information System (INIS)

Godoy-Faundez, Alex; Antizar-Ladislao, Blanca; Reyes-Bozo, Lorenzo; Camano, Andres; Saez-Navarrete, Cesar

2008-01-01

Since early 1900s, with the beginning of mining operations and especially in the last decade, small, although repetitive spills of fuel oil had occurred frequently in the Chilean mining desert industry during reparation and maintenance of machinery, as well as casual accidents. Normally, soils and sawdust had been used as cheap readily available sorbent materials of spills of fuel oil, consisting of complex mixtures of aliphatic and aromatic hydrocarbons. Chilean legislation considers these fuel oil contaminated mixtures of soil and sawdust as hazardous wastes, and thus they must be contained. It remains unknown whether it would be feasible to clean-up Chilean desert soils with high salinity and metal content, historically polluted with different commercial fuel oil, and contained during years. Thus, this study evaluated the feasibility of aerated in-vessel composting at a laboratory scale as a bioremediation technology to clean-up contaminated desert mining soils (fuel concentration > 50,000 mg kg -1 ) and sawdust (fuel concentration > 225,000 mg kg -1 ) in the Atacama Region. The composting reactors were operated using five soil to sawdust ratios (S:SD, 1:0, 3:1, 1:1, 1:3, 0:1, on a dry weight basis) under mesophilic temperatures (30-40 deg. C), constant moisture content (MC, 50%) and continuous aeration (16 l min -1 ) during 56 days. Fuel oil concentration and physico-chemical changes in the composting reactors were monitored following standard procedures. The highest (59%) and the lowest (35%) contaminant removals were observed in the contaminated sawdust and contaminated soil reactors after 56 days of treatment, respectively. The S:SD ratio, time of treatment and interaction between both factors had a significant effect (p < 0.050) on the contaminant removal. The results of this research indicate that bioremediation of an aged contaminated mixture of desert mining soil and sawdust with fuel oil is feasible. This study recommends a S:SD ratio 1:3 and a correct

Bioremediation of contaminated mixtures of desert mining soil and sawdust with fuel oil by aerated in-vessel composting in the Atacama Region (Chile).

Science.gov (United States)

Godoy-Faúndez, Alex; Antizar-Ladislao, Blanca; Reyes-Bozo, Lorenzo; Camaño, Andrés; Sáez-Navarrete, César

2008-03-01

Since early 1900s, with the beginning of mining operations and especially in the last decade, small, although repetitive spills of fuel oil had occurred frequently in the Chilean mining desert industry during reparation and maintenance of machinery, as well as casual accidents. Normally, soils and sawdust had been used as cheap readily available sorbent materials of spills of fuel oil, consisting of complex mixtures of aliphatic and aromatic hydrocarbons. Chilean legislation considers these fuel oil contaminated mixtures of soil and sawdust as hazardous wastes, and thus they must be contained. It remains unknown whether it would be feasible to clean-up Chilean desert soils with high salinity and metal content, historically polluted with different commercial fuel oil, and contained during years. Thus, this study evaluated the feasibility of aerated in-vessel composting at a laboratory scale as a bioremediation technology to clean-up contaminated desert mining soils (fuel concentration>50,000 mg kg(-1)) and sawdust (fuel concentration>225,000 mg kg(-1)) in the Atacama Region. The composting reactors were operated using five soil to sawdust ratios (S:SD, 1:0, 3:1, 1:1, 1:3, 0:1, on a dry weight basis) under mesophilic temperatures (30-40 degrees C), constant moisture content (MC, 50%) and continuous aeration (16 l min(-1)) during 56 days. Fuel oil concentration and physico-chemical changes in the composting reactors were monitored following standard procedures. The highest (59%) and the lowest (35%) contaminant removals were observed in the contaminated sawdust and contaminated soil reactors after 56 days of treatment, respectively. The S:SD ratio, time of treatment and interaction between both factors had a significant effect (pcontaminant removal. The results of this research indicate that bioremediation of an aged contaminated mixture of desert mining soil and sawdust with fuel oil is feasible. This study recommends a S:SD ratio 1:3 and a correct nutrient balance

Tribological performance of paddy straw reinforced polypropylene (PSRP and unidirectional glass-pultruded-kenaf (UGPK composites

Directory of Open Access Journals (Sweden)

R.M. Nasir

2014-06-01

Full Text Available In standard preparation and fabrication of natural-fibre embedded composites, 5 wt. % of natural fibre is enough to strengthen and homogenized in parental matrix as the mechanical strength was observed to increase by more than 25% of pure matrix. Hence, paddy straw and kenaf has been a potential candidate in northern region of Malaysia due to its abundance and easily replenished. A unidirectional glass-pultruded-kenaf (UGPK and paddy straws reinforced polypropylene (PSRP was studied focusing on its tribological performance. Meanwhile, friction and wear properties were examined using pin-on-disc machine under ambient temperature with dry contact condition. The tests were conducted at various sliding velocities (1.178-2.749m/s and applied normal loads (9.82-19.64N. The results showed that specific wear rate and friction coefficient decreased with increasing applied normal load and sliding velocity, but the applied normal load was more influential. The coefficient of friction ranges from 0.5 to 4 and wear rate varies from 0.5 to 4 x 10-5 mm3/Nm for PSRP. The friction coefficient of UGPK is within a range of 2.76 to 4.54 at the given test parameters while its wear rate ranging from 0.8 to 1.79 x 10-5mm3/Nm. The failure mode observed during the test was micro-buckling and followed by splitting while fiber-matrix interfacial failure occurred.

Continuous Fixed-Bed Column Study and Adsorption Modeling: Removal of Lead Ion from Aqueous Solution by Charcoal Originated from Chemical Carbonization of Rubber Wood Sawdust

Directory of Open Access Journals (Sweden)

Swarup Biswas

2015-01-01

Full Text Available The efficiency of chemically carbonized rubber wood sawdust for the removal of lead ion from the aqueous stream was investigated by column process. Chemically carbonized rubber wood sawdust was prepared by treating the sawdust with H2SO4 and HNO3. Maximum removal of lead ion in column process was found as 38.56 mg/g. The effects of operating parameters such as flow rate, bed depth, concentration, and pH were studied in column mode. Experimental data confirmed that the adsorption capacity increased with the increasing inlet concentration and bed depth and decreased with increasing flow rate. Thomas, Yoon-Nelson, and Adams-Bohart models were used to analyze the column experimental data and the relationship between operating parameters. Chemically carbonized rubber wood sawdust was characterized by using Fourier transform infrared spectroscopy. Scanning electron microscope was also utilized for morphological analysis of the adsorbent. Furthermore X-ray fluorescence spectrum analysis and energy dispersive X-ray spectroscopy were also used for the confirmation of lead adsorption process.

Reinforced poly(propylene oxide)- a very soft and extensible dielectric electroactive polymer

DEFF Research Database (Denmark)

Goswami, Kaustav; Galantini, F.; Mazurek, Piotr Stanislaw

2013-01-01

Poly(propylene oxide) (PPO), a novel soft elastomeric material, and its composites were investigated as a new dielectric electroactive polymer (EAP). The PPO networks were obtained from thiol-ene chemistry by photochemical crosslinking of ,!-diallyl PPO with a tetra-functional thiol. The elastomer...... was reinforced with hexamethylenedisilazane treated fumed silica to improve the mechanical properties of PPO. The mechanical properties of PPO and composites thereof were investigated by shear rheology and stress–strain measurements. It was found that incorporation of silica particles improved the stability...... of the otherwise mechanically weak pure PPO network. Dielectric spectroscopy revealed high relative dielectric permittivity of PPO at 103 Hz of 5.6. The relative permittivity was decreased slightly upon addition of fillers, but remained higher than the commonly used acrylic EAP material VHB4910...

Effect of coupling agent on durian skin fibre nanocomposite reinforced polypropylene

Science.gov (United States)

Siti Nur E'zzati, M. A.; Anuar, H.; Siti Munirah Salimah, A. R.

2018-01-01

This paper reports on the development of a composite-based natural fiber to reduce the reliance on petroleum-based product in order to amplify environmental awareness. The production of Durian Skin Nanofiber (DSNF) was conducted using biological fermentation method via rhizopus oryzae in order to obtain the nano dimension of the particle size. Polypropylene (PP) and DSNF were produced using Haake internal mixer via melt blending technique. The significant effect of maleic anhydride grafted polypropylene (MAPP) on the properties of PP/DSNF nanocomposite was investigated to study its mechanical properties which are tensile strength and thermal stability using thermogravimetric (TGA) and differential scanning analysis (DSC). The tensile property of PP nanocomposites increased from 33 MPa to 38 MPa with the presence of MAPP. The addition of MAPP also increased the thermal stability of PP/DSNF nanocomposite where the char residue increased by 52%. Besides that, the thermal degradation of PP/DSNF and PP/DSNF-MAPP were higher than PP where they exerted higher amount of weight loss at an elevated temperature. The percentage of crystallinity, %Xc, of PP nanocomposites improved with the addition of MAPP by 35% based on the differential scanning calorimetry (DSC) result. The SEM analysis showed that the PP/DSNF-MAPP exerts ductile fracture while PP/DSNF exerts brittle fracture.

Morphological, viscoelastic and mechanical characterization of polypropylene/exfoliated graphite nanocomposites

Energy Technology Data Exchange (ETDEWEB)

Ferreira, Creusa Iara; Oliveira, Ricardo Vinicius Bof de; Mauler, Raquel Santos, E-mail: raquel.mauler@ufrgs.br [Universidade Federal do Rio Grande do Sul (PGCIMAT/IQ/UFRGS), Porto Alegre, RS (Brazil); Bianchi, Otavio [Universidade de Caxias do Sul (PGMAT/CCET/UCS), RS (Brazil); Oviedo, Mauro Alfredo Soto [Braskem S/A, Rio de Janeiro, RJ (Brazil)

2013-07-01

The viscoelastic, mechanical and morphological properties of polypropylene/exfoliated graphite nanocomposites with different contents of nanofiller were investigated. According to transmission electron microscopy results, the nanofiller particles were homogeneously dispersed in the matrix. The rheological properties indicated that incorporation of graphite improved the matrix stiffness and had a reinforcing effect. Exfoliated graphite had a weak interaction with the polypropylene. The behavior of the nanocomposites was similar to that of polypropylene in terms of the interfacial detachment inferred from the transmission electron microscopy images and of their G' (storage) and G' (loss) moduli, and viscosity. The mechanical properties of the nanocomposites compared to the matrix improved significantly for the flexural and storage moduli with little loss of impact strength. (author)

Compositional analysis of nitrile terminated poly(propylene imine) dendrimers by high-performance liquid chromatography combined with electrospray mass spectrometry

NARCIS (Netherlands)

van der Wal, S; Mengerink, Y; Brackman, JC; de Brabander, EMM; Jeronimus-Stratingh, CM; Bruins, AP

1998-01-01

Separation methods for nitrile terminated poly(propylene imine) dendrimers were developed to monitor and optimize their large scale production. Detailed analyses of defects within a dendrimer generation were performed by HPLC at alkaline pH (sodium hydroxide) on a polymer-based column or at neutral

High strain rate behaviour of polypropylene microfoams

Science.gov (United States)

Gómez-del Río, T.; Garrido, M. A.; Rodríguez, J.; Arencón, D.; Martínez, A. B.

2012-08-01

Microcellular materials such as polypropylene foams are often used in protective applications and passive safety for packaging (electronic components, aeronautical structures, food, etc.) or personal safety (helmets, knee-pads, etc.). In such applications the foams which are used are often designed to absorb the maximum energy and are generally subjected to severe loadings involving high strain rates. The manufacture process to obtain polymeric microcellular foams is based on the polymer saturation with a supercritical gas, at high temperature and pressure. This method presents several advantages over the conventional injection moulding techniques which make it industrially feasible. However, the effect of processing conditions such as blowing agent, concentration and microfoaming time and/or temperature on the microstructure of the resulting microcellular polymer (density, cell size and geometry) is not yet set up. The compressive mechanical behaviour of several microcellular polypropylene foams has been investigated over a wide range of strain rates (0.001 to 3000 s-1) in order to show the effects of the processing parameters and strain rate on the mechanical properties. High strain rate tests were performed using a Split Hopkinson Pressure Bar apparatus (SHPB). Polypropylene and polyethylene-ethylene block copolymer foams of various densities were considered.

Antioxidant action in irradiated polypropylene studied by ultraviolet spectroscopy

International Nuclear Information System (INIS)

Milosavljevic, B.H.; Novakovic, Lj.

1999-01-01

Ultraviolet spectrum of 0.2 mm thick film of polypropylene containing 0.5% ORGANOX 1010 showed that in the sample prepared by slow cooling about 15% of the antioxidant reacted during the preparation process. The difference in turbidity between the samples obtained in the slow and the fast cooling process is attributed to the degree of crystallinity, which is in agreement with the DSC data. Very pronounced effects of the oxygen concentration and the degree of crystallinity on antioxidant uptake in irradiated polypropylene films were observed and discussed. It was also shown that a Febetron 707 pulsed electron accelerator is capable of producing both the single pulse dose (50 kGy) and the dose rate (2.5 TGy/s) large enough to enable a comparison of dose rate effects and LET effects in the study of the antioxidant reactions in polypropylene

Evaluation of bolted connections in wood-plastic composites

Science.gov (United States)

Arnandha, Yudhi; Satyarno, Iman; Awaludin, Ali; Irawati, Inggar Septia; Ihsan, Muhamad; Wijanarko, Felyx Biondy; William, Mahdinur, Fardhani, Arfiati

2017-03-01

Wood-plastic composite (WPC) is a relatively new material that consists of sawdust and plastic polymer using the extrusion process. Due to its attributes such as low water content, low maintenance, UV durability and being fungi and termite resistant. Nowadays, WPC has already been produced in Indonesia using sawdust from local wood such as Albizia (Paraserianthes falcataria) and Teak (Tectona grandis). Moreover preliminary studies about the physical and mechanical WPC board from Albizia sawdust and HDPE plastic have been carried out. Based on these studies, WPC has a high shear strength around 25-30 MPa higher than its original wood shear strength. This paper was a part of the research in evaluating WPC as potential sheathing in a shear wall system. Since still little is known about connection behavior in WPC using Indonesian local wood, this study evaluated the connection for both of these two types of wood-plastic composite. WPC board from Albizia sawdust will be projected as shear wall sheathing and WPC stud from Teak sawdust projected to be shear wall frame. For this study, the embedding strength for both WPC was determined according to ASTM D 5764 standard, using two types of bolts (stainless bolt and standard bolt) with several diameters as variation (6 mm, 8 mm, 10 and 12 mm). Hence, dowel-bearing test under fastened condition conducted accordance to ASTM D5652, hereby the yield strength then compared with the prediction yield strength from European Yield Model (EYM). According to both single and double shear connection, it can be concluded that yield strength from the EYM method tended to under-predict the 5% diameter offset yield than the actual yield strength from the test. The yield strength itself increase with the increase of bolt diameter. For single shear connection, the highest yield strength was 12 mm standard bolt around 9732 N, slightly higher than stainless bolt around 9393 N. Whereby for double shear connection, the highest yield strength was

Mathematical Determination of Thermal Load for Fluidised Bed Furnaces Using Sawdust

Directory of Open Access Journals (Sweden)

Antonescu Nicolae

2014-06-01

Full Text Available For technical applications, a physical model capable of predicting the particle evolution in the burning process along its trajectory through the furnace is very useful. There are two major demands: all the thermo-dynamic processes that describe the particle burning process must be accounted and the model must be written in such equation terms to allow the intervention for parameter settings and particle definition. The computations were performed for the following parameters: furnace average temperature between 700 and 1200 °C, size of the sawdust particle from 4 to 6 mm and fix carbon ignition between 500 and 900 °C. The values obtained for the characteristic parameters of the burning process ranged from 30 to 60 [kg/(h·m3] for the gravimetrical burning speed WGh and from 150 to 280 [kW/m3] for the volumetric thermal load of the furnace QV. The main conclusion was that the calculus results are in good agreement with the experimental data from the pilot installations and the real-case measurements in the sawdust working boiler furnaces or pre-burning chambers. Another very important conclusion is that the process speed variation, when the furnace temperature changes, confirms the thermo-kinetic predictions, namely that the burning process speed decreases when the furnace temperature increases.

Reinforced poly(propylene oxide): a very soft and extensible dielectric electroactive polymer

International Nuclear Information System (INIS)

Goswami, K; Mazurek, P; Daugaard, A E; Skov, A L; Galantini, F; Gallone, G

2013-01-01

Poly(propylene oxide) (PPO), a novel soft elastomeric material, and its composites were investigated as a new dielectric electroactive polymer (EAP). The PPO networks were obtained from thiol-ene chemistry by photochemical crosslinking of α,ω-diallyl PPO with a tetra-functional thiol. The elastomer was reinforced with hexamethylenedisilazane treated fumed silica to improve the mechanical properties of PPO. The mechanical properties of PPO and composites thereof were investigated by shear rheology and stress–strain measurements. It was found that incorporation of silica particles improved the stability of the otherwise mechanically weak pure PPO network. Dielectric spectroscopy revealed high relative dielectric permittivity of PPO at 10 3 Hz of 5.6. The relative permittivity was decreased slightly upon addition of fillers, but remained higher than the commonly used acrylic EAP material VHB4910. The electromechanical actuation performance of both PPO and its composites showed properties as good as VHB4910 and a lower viscous loss. (paper)

Co-pyrolysis behavior of fermentation residues with woody sawdust by thermogravimetric analysis and a vacuum reactor.

Science.gov (United States)

Zheng, Yan; Zhang, Yimin; Xu, Jingna; Li, Xiayang; Charles Xu, Chunbao

2017-12-01

This study aimed at cost-effective utilization of fermentation residues (FR) from biogas project for bio-energy via co-pyrolysis of FR and woody sawdust (WS). In this study, a vacuum reactor was used to study the pyrolysis behaviors of individual and blend samples of FR and WS. Obvious synergistic effects were observed, resulting in a lower char yield but a higher gas yield. The presence of woody sawdust promoted the devolatilization of FR, and improved the syngas (H 2 and CO) content in the gaseous products. Compared to those of the char from pyrolysis of individual feedstock, co-pyrolysis of FR and WS in the vacuum reactor promoted the cracking reactions of large aromatic rings, enlarged the surface area and reduced the oxygenated groups of the resulted char. Copyright © 2017 Elsevier Ltd. All rights reserved.

Production of the oxidation-resistant polypropylene track membranes

International Nuclear Information System (INIS)

Kravets, L.I.; Dmitriev, S.N.; Apel, P.Y.

1999-01-01

This paper describes results of the method of manufacturing the polypropylene track membranes produced by physicochemical treatment under irradiation of accelerated heavy ions of polymer films. The developed method allows to produce membranes 0.1 - 0.2 μm in diameter and more with an improved structural and physicochemical properties. Poly-propylene track membranes of a novel sample are characterized by high homogeneity of pore sizes in magnitude, considerable mechanical strength, advanced thermal stability and resistance to oxidation in aggressive media. It opens new fields for their usage

Hofmeister effect of salt mixtures on thermo-responsive poly(propylene oxide)

DEFF Research Database (Denmark)

Moghaddam, Saeed Zajforoushan; Thormann, Esben

2015-01-01

of aqueous solutions of poly(propylene oxide) is affected by mixtures of ions with different location in the Hofmeister series. Our results show that the Hofmeister effects of pure salt species are not always linearly additive and that the relative effect of some ions can be reversed depending...... on the composition of the salt mixture as well as by the absolute and relative concentration of the different species. We suggest that these results can lead to a better understanding of the potential role of the Hofmeister effect in regulation of biological processes, which does always take place in salt mixtures...... rather than solutions containing just single salt species....

Morphological, viscoelastic and mechanical characterization of polypropylene/exfoliated graphite nanocomposites

Directory of Open Access Journals (Sweden)

Creusa Iara Ferreira

2013-01-01

Full Text Available The viscoelastic, mechanical and morphological properties of polypropylene/exfoliated graphite nanocomposites with different contents of nanofiller were investigated. According to transmission electron microscopy results, the nanofiller particles were homogeneously dispersed in the matrix. The rheological properties indicated that incorporation of graphite improved the matrix stiffness and had a reinforcing effect. Exfoliated graphite had a weak interaction with the polypropylene. The behavior of the nanocomposites was similar to that of polypropylene in terms of the interfacial detachment inferred from the transmission electron microscopy images and of their G' (storage and G'' (loss moduli, and viscosity. The mechanical properties of the nanocomposites compared to the matrix improved significantly for the flexural and storage moduli with little loss of impact strength.

Morphological, viscoelastic and mechanical characterization of polypropylene/exfoliated graphite nanocomposites

Energy Technology Data Exchange (ETDEWEB)

Ferreira, Creusa Iara; Oliveira, Ricardo Vinicius Bof de; Mauler, Raquel Santos, E-mail: raquel.mauler@ufrgs.br [Universidade Federal do Rio Grande do Sul (PGCIMAT/IQ/UFRGS), Porto Alegre, RS (Brazil); Bianchi, Otavio [Universidade de Caxias do Sul (PGMAT/CCET/UCS), RS (Brazil); Oviedo, Mauro Alfredo Soto [Braskem S/A, Rio de Janeiro, RJ (Brazil)

2013-07-01

The viscoelastic, mechanical and morphological properties of polypropylene/exfoliated graphite nanocomposites with different contents of nanofiller were investigated. According to transmission electron microscopy results, the nanofiller particles were homogeneously dispersed in the matrix. The rheological properties indicated that incorporation of graphite improved the matrix stiffness and had a reinforcing effect. Exfoliated graphite had a weak interaction with the polypropylene. The behavior of the nanocomposites was similar to that of polypropylene in terms of the interfacial detachment inferred from the transmission electron microscopy images and of their G' (storage) and G' (loss) moduli, and viscosity. The mechanical properties of the nanocomposites compared to the matrix improved significantly for the flexural and storage moduli with little loss of impact strength. (author)

Technical assessment of three layered cement-bonded boards produced from wastepaper and sawdust

International Nuclear Information System (INIS)

Fuwape, Joseph Adeola; Fabiyi, James Sunday; Osuntuyi, Edward Olusola

2007-01-01

The technical properties of three layered cement-bonded boards (CBBs) made from wastepaper and sawdust were investigated. The CBBs were produced at three density levels of 1000, 1200 and 1300 kg/m 3 and at four cement/particle ratios of 2.0:1, 2.5:1, 3.0:1 and 3.5:1 on a weight to weight basis. The technical properties evaluated were modulus of rupture (MOR), modulus of elasticity (MOE), water absorption (WA) and thickness swelling (TS). The MOR values ranged from 4.85 to 11.69 MPa and MOE values ranged from 2.80 to 5.57 GPa. The mean values of WA and TS after 24 h of water soaking of the CBBs ranged from 18.18% to 40.49% and 3.55% to 12.13%, respectively. MOR and MOE of the CBBs increased with increase in board density, but MOR decreased with the increase in cement/particle ratio. On the other hand, WA and TS decreased with increase in board density and cement/particle ratio. CBBs produced from wastepaper and sawdust at cement/particle ratios of 3.0:1 and 3.5:1 are suitable for building construction such as paneling, ceiling and partitioning

Thermochemical properties of cellulose acetate blends with acetosolv and sawdust lignin: A comparative study.

Science.gov (United States)

Peredo, Karol; Escobar, Danilo; Vega-Lara, Johana; Berg, Alex; Pereira, Miguel

2016-02-01

Sawdust (SD) and cotton-lignin blends (CLB) were acetylated and the effect of lignin type and content on thermoplastic properties of the acetate produced was studied. The lignin in samples did not significantly affect the degree of acetylation. An increase in acetyl groups of 1-3% was observed in acetylated SD (ASD) unlike acetylated CLB (ACLB). Thermogravimetric analysis showed two thermal degradation zones; one at 190-200°C and the other at 330-370°C. The early degradation in ASD corresponds to galactoglucomannans while that in ACLB corresponds to the low-molecular-weight lignin. The second degradation is due to decomposition of cellulose acetate and high-molecular-weight lignin. DSC analysis showed homogeneous behaviour in ASD with only one glass transition temperature (Tg) at 170-180°C, unlike ACLB that showed two Tgs at 170-180°C. Sawdust acetylation, taking advantage of its residual lignin, showed higher reactivity and miscibility as compared to the same material produced by adding previously extracted lignin on cotton. Copyright © 2015 Elsevier B.V. All rights reserved.

Synthesis and characterization of kaolin with polystyrene via in-situ polymerization and their application on polypropylene

International Nuclear Information System (INIS)

Zhao, Songfang; Qiu, Shangchang; Zheng, Yuying; Cheng, Lei; Guo, Yong

2011-01-01

To improve both the mechanical and thermal properties of kaolin/polypropylene (PP) composites, kaolin was modified by using 3-(trimethoxysilyl) propylmethacrylate (YDH-570) as a coupling agent to form polymerizable particle. Styrene was radically polymerized through the immobilized vinyl using benzoyl peroxide (BPO) as an initiator. Fourier transform-infrared (FTIR) spectroscopy, particle size distribution, X-ray diffraction (XRD) and thermo-gravimetric analysis (TGA) well demonstrated that the kaolin-polystyrene particles were successfully synthesized via in-situ polymerization. While the modified kaolin and raw kaolin were introduced into the PP matrix, it could be concluded that modified kaolin/PP composites have better mechanical and thermal properties than raw kaolin/PP composites, and these improvements were attributed to the desirable dispersion of kaolin in PP matrix.

High-voltage pulsed life of multistressed polypropylene capacitor dielectric

International Nuclear Information System (INIS)

Laghari, J.R.

1992-01-01

High-voltage polypropylene capacitors were aged under singular as well as simultaneous multiple stresses (electrical, thermal, and radiation) at the University of Buffalo's 2 MW thermal nuclear reactor. These stresses were combined neutron-gamma radiation with a total dose of 1.6 x 10 6 rad, electrical stress at 40 V rms /μm, and thermal stress at 90 degrees C. After exposure, the polypropylene dielectric was tested for life (number of pulses to fail) under high-voltage high-repetition-rate (100 pps) pulses. Pulsed life data were also compared with ac life data. Results show that radiation stress causes the most degradation in life, either acting alone or in combination with other stresses. The largest reduction in life occurs when polypropylene is aged under simultaneous multiple stresses (electrical, thermal, and radiation). In this paper, it is shown that pulsed life can be equivalently compared with ac life

PLASTIC SHRINKAGE CONTROLLING EFFECT BY POLYPROPYLENE SHORT FIBER WITH HYDROPHILY

Science.gov (United States)

Hosoda, Akira; Sadatsuki, Yoshitomo; Oshima, Akihiro; Ishii, Akina; Tsubaki, Tatsuya

The aim of this research is to clarify the mechanism of controlling plastic shrinkage crack by adding small amout of synthetic short fiber, and to propose optimum polypropylene short fiber to control plastic shrinkage crack. In this research, the effect of the hydrophily of polypropylene fiber was investigated in the amount of plastic shrinkage of mortar, total area of plastic shrinkage crack, and bond properties between fiber and mortar. The plastic shrinkage test of morar was conducted under high temperature, low relative humidity, and constant wind velocity. When polypropylene fiber had hydrophily, the amount of plastic shrinkage of mortar was restrained, which was because cement paste in morar was captured by hydrophilic fiber and then bleeding of mortar was restrained. With hydrophily, plastic shrinkage of mortar was restrained and bridging effect was improved due to better bond, which led to remarkable reduction of plastic shrinkage crack. Based on experimental results, the way of developing optimum polypropylene short fiber for actual construction was proposed. The fiber should have large hydrophily and small diameter, and should be used in as small amount as possible in order not to disturb workability of concrete.

Sensitivity of the polypropylene to the strain rate: experiments and modeling

International Nuclear Information System (INIS)

Abdul-Latif, A.; Aboura, Z.; Mosleh, L.

2002-01-01

, i.e. to describe the elastic-viscoplastic behavior of the polypropylene for other loading paths which did not use during the identification process. Finally, the obtained model being devoted to describe the stress-strain behavior of the polypropylene, is able to fairly well reproduce the strain rate dependent deformation of such a material under several loading conditions (uniaxial tensile load at different strain rates, strain rate jumping and relaxation phenomenon). It is important to keep in mind that the final objective will be to model the damaged behavior of women fibbers glass composite materials with thermoplastic matrix

High strain rate behaviour of polypropylene microfoams

Directory of Open Access Journals (Sweden)

Martínez A.B.

2012-08-01

Full Text Available Microcellular materials such as polypropylene foams are often used in protective applications and passive safety for packaging (electronic components, aeronautical structures, food, etc. or personal safety (helmets, knee-pads, etc.. In such applications the foams which are used are often designed to absorb the maximum energy and are generally subjected to severe loadings involving high strain rates. The manufacture process to obtain polymeric microcellular foams is based on the polymer saturation with a supercritical gas, at high temperature and pressure. This method presents several advantages over the conventional injection moulding techniques which make it industrially feasible. However, the effect of processing conditions such as blowing agent, concentration and microfoaming time and/or temperature on the microstructure of the resulting microcellular polymer (density, cell size and geometry is not yet set up. The compressive mechanical behaviour of several microcellular polypropylene foams has been investigated over a wide range of strain rates (0.001 to 3000 s−1 in order to show the effects of the processing parameters and strain rate on the mechanical properties. High strain rate tests were performed using a Split Hopkinson Pressure Bar apparatus (SHPB. Polypropylene and polyethylene-ethylene block copolymer foams of various densities were considered.

Polypropylene reinforced with organophilic clay and brazilian nut fibers

International Nuclear Information System (INIS)

Rocha-Gomes, L.V.; Mondelo-Garcia, F.J.; Vaccioli, K.; Valera, S.T.; Silva-Valenzuela, M.G.; Valenzuela-Diaz, F.R.

2014-01-01

Polymer nanocomposites have been shown to possess better properties when compared with traditional composites. This study aims to investigate the effects of the addition of organophilic clay and Brazilian nut fiber on the polypropylene (PP). First, 5%, 10% and 20% PP/compatibilizer maleic anhydride (PP-g-MA) by weight was added to Pure PP, respectively. From the results, 5% PP-g-MA was defined for preparing the nanocomposites. Samples were prepared containing 5% PP / PP-g-MA reinforced with 5% organophilic Brazilian smectite clay and 5%, 10% and 15% Brazilian nut fiber. Specimens were tested for tensile strength and impact. The materials were characterized by laser diffraction particle size and X-ray diffraction, and the nanocomposites, by mechanical strength and impact. The best result was obtained by inserting 15% fiber. (author)

Highest recorded electrical conductivity and microstructure in polypropylene-carbon nanotubes composites and the effect of carbon nanofibers addition

Science.gov (United States)

Ramírez-Herrera, C. A.; Pérez-González, J.; Solorza-Feria, O.; Romero-Partida, N.; Flores-Vela, A.; Cabañas-Moreno, J. G.

2018-04-01

In the last decade, numerous investigations have been devoted to the preparation of polypropylene-multiwalled carbon nanotubes (PP/MWCNT) nanocomposites having enhanced properties, and in particular, high electrical conductivities (> 1 S cm-1). The present work establishes that the highest electrical conductivity in PP/MWCNT nanocomposites is limited by the amount of nanofiller content which can be incorporated in the polymer matrix, namely, about 20 wt%. This concentration of MWCNT in PP leads to a maximum electrical conductivity slightly lower than 8 S cm-1, but only by assuring an adequate combination of dispersion and spatial distribution of the carbon nanotubes. The realization of such an optimal microstructure depends on the characteristics of the production process of the PP/MWCNT nanocomposites; in our experiments, involving composite fabrication by melt mixing and hot pressing, a second re-processing cycle is shown to increase the electrical conductivity values by up to two orders of magnitude, depending on the MWCNT content of the nanocomposite. A modest increase of the highest electrical conductivity obtained in nanocomposites with 21.5 wt% MWCNT content has been produced by the combined use of carbon nanofibers (CNF) and MWCNT, so that the total nanofiller content was increased to 30 wt% in the nanocomposite with PP—15 wt% MWCNT—15 wt%CNF.

Effect of atmospheric pressure plasma treatment condition on adhesion of ramie fibers to polypropylene for composite

Energy Technology Data Exchange (ETDEWEB)

Li, Ying [College of Material and Textile Engineering, Jiaxing University, Jiaxing 314033 (China); Center for Plasma-Aided Manufacturing, Madison, WI 53706 (United States); School of Human Ecology, University of Wisconsin-Madison, Madison, WI 53706 (United States); Manolache, Sorin [Center for Plasma-Aided Manufacturing, Madison, WI 53706 (United States); US Forest Products Laboratory, Madison, WI 53726 (United States); Qiu, Yiping, E-mail: ypqiu@dhu.edu.cn [College of Textiles, Donghua University, Shanghai 201620 (China); Sarmadi, Majid, E-mail: majidsar@wisc.edu [Center for Plasma-Aided Manufacturing, Madison, WI 53706 (United States); School of Human Ecology, University of Wisconsin-Madison, Madison, WI 53706 (United States); Materials Science Program, University of Wisconsin-Madison, Madison, WI 53706 (United States)

2016-02-28

Graphical abstract: - Highlights: • The continuous ethanol flow technique can successfully modify ramie fiber surface with an increase in IFSS value up to 50%. • Response surface methodology was applied to design the plasma treatment parameters for ramie fiber modification. • The ethanol flow rate was the most influential treatment parameter in plasma modification process. - Abstract: In order to improve the interfacial adhesion between hydrophilic ramie fibers and hydrophobic polypropylene (PP) matrices, ramie fibers are modified by atmospheric pressure dielectric barrier discharge (DBD) plasma with our continuous ethanol flow technique in helium environment. A central composite design of experiments with different plasma processing parameter combinations (treatment current, treatment time and ethanol flow rate) is applied to find the most influential parameter and to obtain the best modification effect. Field emission scanning electron microscope (SEM) shows the roughened surfaces of ramie fibers from the treated groups due to plasma etching effect. Dynamic contact angle analysis (DCAA) demonstrates that the wettability of the treated fibers drastically decreases. Microbond pullout test shows that the interfacial shear strength (IFSS) between treated ramie fibers and PP matrices increases significantly. Residual gas analysis (RGA) confirms the creation of ethyl groups during plasma treatment. This study shows that our continuous ethanol flow technique is effective in the plasma modification process, during which the ethanol flow rate is the most influential parameter but all parameters have simultaneous influence on plasma modification effect of ramie fibers.

Stabilization of polypropylene, polypropylene blends with poly (styrene-b-(ethylene-co-butylene)-b-styrene) under irradiation: A comparative investigation

International Nuclear Information System (INIS)

Luan Shifang; Yang Huawei; Shi Hengchong; Zhao Jie; Wang Jianwei; Yin Jinghua

2011-01-01

The aim of this paper is to investigate the stabilization of polypropylene in the poly (styrene-b-(ethylene-co-butylene)-b-styrene) (SEBS)/polypropylene (PP) blends under irradiation with respect to PP. The PP films, SEBS/PP films were subjected to electron beam irradiation and characterized by wide angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), gel permeation chromatography (GPC), and dynamic mechanical thermal analysis (DMTA). It demonstrated that upon irradiation, the molecular weight of PP had a pronounced decrease due to the major chain scission, and the minor chain cross-linking or chain branching occurred at the higher irradiation dose. Stabilization of PP was improved in the presence of SEBS, exhibiting an enhanced irradiation resistance.

Stabilization of polypropylene, polypropylene blends with poly (styrene-b-(ethylene-co-butylene)-b-styrene) under irradiation: A comparative investigation

Energy Technology Data Exchange (ETDEWEB)

Luan Shifang; Yang Huawei; Shi Hengchong; Zhao Jie [State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China); Wang Jianwei [Shandong Weigao Group Medical Polymer Company Limited, Weihai 264209 (China); Yin Jinghua, E-mail: yinjh@ciac.jl.c [State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China)

2011-01-15

The aim of this paper is to investigate the stabilization of polypropylene in the poly (styrene-b-(ethylene-co-butylene)-b-styrene) (SEBS)/polypropylene (PP) blends under irradiation with respect to PP. The PP films, SEBS/PP films were subjected to electron beam irradiation and characterized by wide angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), gel permeation chromatography (GPC), and dynamic mechanical thermal analysis (DMTA). It demonstrated that upon irradiation, the molecular weight of PP had a pronounced decrease due to the major chain scission, and the minor chain cross-linking or chain branching occurred at the higher irradiation dose. Stabilization of PP was improved in the presence of SEBS, exhibiting an enhanced irradiation resistance.

METHANE DRY REFORMING OVER Ni SUPPORTED ON PINE SAWDUST ACTIVATED CARBON: EFFECTS OF SUPPORT SURFACE PROPERTIES AND METAL LOADING

Directory of Open Access Journals (Sweden)

Rafael García

2015-05-01

Full Text Available The influence of metal loading and support surface functional groups (SFG on methane dry reforming (MDR over Ni catalysts supported on pine-sawdust derived activated carbon were studied. Using pine sawdust as the catalyst support precursor, the smallest variety and lowest concentration of SFG led to best Ni dispersion and highest catalytic activity, which increased with Ni loading up to 3 Ni atoms nm-2. At higher Ni loading, the formation of large metal aggregates was observed, consistent with a lower "apparen" surface area and a decrease in catalytic activity. The H2/CO ratio rose with increasing reaction temperature, indicating that increasingly important side reactions were taking place in addition to MDR.

Crescimento micelial de Pleurotus ostreatus em resíduo de Simarouba amara Mycelial growth of Pleurotus ostreatus in Simarouba amara sawdust

Directory of Open Access Journals (Sweden)

Ceci Sales-Campos

2008-11-01

Full Text Available O objetivo deste trabalho foi avaliar o crescimento micelial do cogumelo Pleurotus ostreatus, cultivado na serragem da espécie madeireira Simarouba amara. Avaliaram-se: o efeito das temperaturas de 22, 25, 27, 30 e 35ºC sobre o crescimento micelial de P. ostreatus, nos meios malte-ágar 3% e SDA-MA (infusão da serragem de S. amara, enriquecida com farelo de soja-dextrose-ágar; e o crescimento micelial em substrato de cultivo de serragem de S. amara, com e sem suplementação de farelo de soja, a 25 e 30ºC. O melhor desenvolvimento de P. ostreatus ocorreu em meio malte-ágar 3% a 25ºC. A suplementação de farelo de soja na serragem de S. amara favorece o crescimento micelial.The objective of this work was to assess the mycelial growth of oyster mushroom (Pleurotus ostreatus cultivated in sawdust of Simarouba amara. Evaluations were made for the effect of temperatures 22, 25, 27, 30 and 35ºC on the mycelial growth of P. ostreatus in 3% malt-agar and SDA-MA (infusion of S. amara sawdust, enriched with soybean meal-dextrose-agar media; and the mycelial growth in cultivation substrate of S. amara sawdust, with and without supplementation of soybean meal, at 25 and 30ºC. The best development of P. ostreatus was in 3% malt-agar medium at 25ºC. Soybean meal supplementation on S. amara sawdust promoted mycelial growth.

Antioxidant Potential of Lingzhi or Reishi Medicinal Mushroom, Ganoderma lucidum (Higher Basidiomycetes) Cultivated on Artocarpus heterophyllus Sawdust Substrate in India.

Science.gov (United States)

Rani, P; Lal, Merlin Rajesh; Maheshwari, Uma; Krishnan, Sreeram

2015-01-01

The artificial cultivation of Ganoderma lucidum (MTCC1039) using Artocarpus heterophyllus as sawdust substrate was optimized and free radical scavenging activities of the generated fruiting bodies were investigated. The choice of A. heterophyllus as substrate was due to its easy availability in South India. Sawdust supplemented with dextrose medium yielded better spawn hyphae and early fruiting body initiation (15 days). The biological yield obtained was 42.06 ± 2.14 g/packet and the biological efficiency was 8.41 ± 0.48%. Both aqueous and methanolic extracts of fruiting body were analyzed for radical scavenging activity. Methanolic extract showed maximum scavenging activity for 1,1-diphenyl-2-picrylhydrazyl (IC50 = 290 μg/ml) and 2,2'-azino-bis(3-ethylbenzothiazoline- 6-sulphonic acid (IC50 = 580 μg/ml), whereas aqueous extract had better scavenging for ferric reducing antioxidant power (IC50 = 5 μg/ml). Total phenolic content and total antioxidant capacity were significantly higher in methanolic extract (p < 0.01). A positive correlation existed between the phenolic content and antioxidant activity. Our results indicated that fruiting bodies of G. lucidum cultivated in sawdust medium possess antioxidant property, which can be exploited for therapeutic application.

Influence of injection temperatures and fiberglass compositions on mechanical properties of polypropylene

Science.gov (United States)

Keey, Tony Tiew Chun; Azuddin, M.

2017-06-01

Injection molding process appears to be one of the most suitable mass and cost efficiency manufacturing processes for polymeric parts nowadays due to its high efficiency of large scale production. When down-scaling the products and components, the limits of conventional injection molding process are reached. These constraints had initiated the development of conventional injection molding process into a new era of micro injection molding technology. In this study, fiberglass reinforced polypropylenes (PP) with various glass fiber percentage materials were used. The study start with fabrication of micro tensile specimens at three different injection temperature, 260°C, 270°C and 280°C for different percentage by weight of fiberglass reinforced PP. Then evaluate the effects of various injection temperatures on the tensile properties of micro tensile specimens. Different percentage by weight of fiberglass reinforced PP were tested as well and it was found that 20% fiberglass reinforced PP possessed the greatest percentage increase of tensile strength with increasing temperatures.

Application of gas chromatography to the investigations on polypropylene radiolysis

International Nuclear Information System (INIS)

Zagorski, Z.P.; Gluszewski, W.

2006-01-01

Refinement of the gas chromatography (GC) instrumental approach permitted not only improvement of investigation in basic research, but also development of a new kind of polypropylene blends, more suitable for the production of medical devices and radiation sterilization. It has been shown, that using the GC method not only methane and carbon dioxide can be measured, but also the consumption of oxygen which reacts with free radicals on the polypropylene chain

Effect of polybutenes on mechanical and physical properties of polypropylene

International Nuclear Information System (INIS)

Nascimento, Uedson A. do; Timoteo, Gustavo Arante V.; Rabello, Marcelo S.

2009-01-01

This study investigated the effect of polybutene (PIB) of molecular weights ranging from 480 the 1.600 g/mol in polypropylene homopolymer. Compositions with 0, 3, 5 and 7% of PIB were prepared in internal mixer and compression moulded. The properties evaluated were: tensile strength, scanning electron microscopy (SEM), FTIR, X-ray diffraction (XRD) and melt flow index (IF). The results of mechanical tests showed that the presence of the plasticizer reduced the tensile strength, elastic modulus and hardness. The analysis of XRD showed a drop in the degree of crystallinity of PP/PIB blends. The micrographs obtained by SEM did not reveal the occurrence of the phase separation. The IF analysis confirm the effect of PIB as internal lubricant's, by increasing the rate of flow. (author)

DESIGNING AND OPPORTUNITY FUEL WITH BIOMASS AND TIRE-DERIVED FUEL FOR COFIRING AT WILLOW ISLAND GENERATING STATION AND COFIRING SAWDUST WITH COAL AT ALBRIGHT GENERATING STATION

Energy Technology Data Exchange (ETDEWEB)

K. Payette; D. Tillman

2004-06-01

During the period July 1, 2000-March 31, 2004, Allegheny Energy Supply Co., LLC (Allegheny) conducted an extensive demonstration of woody biomass cofiring at its Willow Island and Albright Generating Stations. This demonstration, cofunded by USDOE and Allegheny, and supported by the Biomass Interest Group (BIG) of EPRI, evaluated the impacts of sawdust cofiring in both cyclone boilers and tangentially-fired pulverized coal boilers. The cofiring in the cyclone boiler--Willow Island Generating Station Unit No.2--evaluated the impacts of sawdust alone, and sawdust blended with tire-derived fuel. The biomass was blended with the coal on its way to the combustion system. The cofiring in the pulverized coal boiler--Albright Generating Station--evaluated the impact of cofiring on emissions of oxides of nitrogen (NO{sub x}) when the sawdust was injected separately into the furnace. The demonstration of woody biomass cofiring involved design, construction, and testing at each site. The results addressed impacts associated with operational issues--capacity, efficiency, and operability--as well as formation and control of airborne emissions such as NO{sub x}, sulfur dioxide (SO{sub 2}2), opacity, and mercury. The results of this extensive program are detailed in this report.

Optimization of microwave-assisted rubberwood sawdust based activated carbon preparation conditions for methylene blue removal

Science.gov (United States)

Khasri, Azduwin; Ahmad, Mohd Azmier

2017-10-01

Optimum preparation conditions of rubberwood sawdust based activated carbon (RSAC) for methylene blue (MB) dye removal was studied. RSAC was produced by applying physiochemical activation method by using potassium hydroxide as a chemical agent which accompanied by carbon dioxide gasification under microwave heating. The effects of microwave power, irradiation time and impregnation ratio on two types of responses namely MB removal and RSAC yield using the center composite design (CCD) were also included in this study. The preparation variables correlation for responses was developed by two quadratic models. Optimum preparation conditions of RSAC were obtained at microwave power, irradiation time and IR of 354 W, 4.5 minutes and 0.98, respectively, which resulted MB removal and yield of 83.79% and 28%, respectively. The average pore diameter, surface area and total pore volume of optimized RSAC were 4.12 nm, 796.33 m2/g and 0.4219 cm3/g, respectively. This sample was found to has well-developed pores on its surface and can be a promising adsorbent for MB removal from aqueous solution.

Study of mechanical, rheological and thermal properties of nanocomposite HMSPP (high melt strength polypropylene) with Brazilian bentonite

International Nuclear Information System (INIS)

Fermino, Danilo Marin

2011-01-01

This work concerns to the study of the mechanical, thermal and rheological behavior of the nano composite HMSPP - Polypropylene High Melt Strength (obtained at a dose of 12.5 kGy) and a bentonite clay Brazilian Paraiba, known as 'Chocolate' in concentrations of 5 and 10% by weight, comparison of to one American Clay, Cloisite 20A nanocomposite was done. Agent compatibilizer polypropylene-graft, known as maleic anhydride (PP-g-AM) was addict 3% concentration thought technique melt intercalation using a twin-screw extruder and the specimens were prepared by injection process. The mechanical behavior was evaluated by strength, flexural strength and impact tests. The thermal behavior was evaluated by the techniques of differential scanning calorimetry (DSC) and thermogravimetry (TGM). The rheological behavior was evaluated in rheometer. The morphology of the nanocomposites was studied by the technique of scanning electron microscopy (SEM). The organophilic bentonite and the nanocomposites were characterized by X-ray diffraction (XRD) and infrared (FTIR). (author)

On clarification of haze in polypropylene

NARCIS (Netherlands)

Bernland, K.; Goossens, J.G.P.; Smith, P.; Tervoort, T.A.

2016-01-01

The mechanism of reducing light scattering in isotactic polypropylene (i-PP), through the addition of so-called clarifying agents, is studied with small-angle light scattering (SALS) and scanning electron microscopy (SEM). The clarifying agents used in this study depict monotectic phase behavior

Impact of clay mineral, wood sawdust or root organic matter on the bacterial and fungal community structures in two aged PAH-contaminated soils.

Science.gov (United States)

Cébron, Aurélie; Beguiristain, Thierry; Bongoua-Devisme, Jeanne; Denonfoux, Jérémie; Faure, Pierre; Lorgeoux, Catherine; Ouvrard, Stéphanie; Parisot, Nicolas; Peyret, Pierre; Leyval, Corinne

2015-09-01

The high organic pollutant concentration of aged polycyclic aromatic hydrocarbon (PAH)-contaminated wasteland soils is highly recalcitrant to biodegradation due to its very low bioavailability. In such soils, the microbial community is well adapted to the pollution, but the microbial activity is limited by nutrient availability. Management strategies could be applied to modify the soil microbial functioning as well as the PAH contamination through various amendment types. The impact of amendment with clay minerals (montmorillonite), wood sawdust and organic matter plant roots on microbial community structure was investigated on two aged PAH-contaminated soils both in laboratory and 1-year on-site pot experiments. Total PAH content (sum of 16 PAHs of the US-EPA list) and polar polycyclic aromatic compounds (pPAC) were monitored as well as the available PAH fraction using the Tenax method. The bacterial and fungal community structures were monitored using fingerprinting thermal gradient gel electrophoresis (TTGE) method. The abundance of bacteria (16S rRNA genes), fungi (18S rRNA genes) and PAH degraders (PAH-ring hydroxylating dioxygenase and catechol dioxygenase genes) was followed through qPCR assays. Although the treatments did not modify the total and available PAH content, the microbial community density, structure and the PAH degradation potential changed when fresh organic matter was provided as sawdust and under rhizosphere influence, while the clay mineral only increased the percentage of catechol-1,2-dioxygenase genes. The abundance of bacteria and fungi and the percentage of fungi relative to bacteria were enhanced in soil samples supplemented with wood sawdust and in the plant rhizospheric soils. Two distinct fungal populations developed in the two soils supplemented with sawdust, i.e. fungi related to Chaetomium and Neurospora genera and Brachyconidiellopsis and Pseudallescheria genera, in H and NM soils respectively. Wood sawdust amendment favoured the

Anomalous behavior of secondary dielectric relaxation in polypropylene glycols

Energy Technology Data Exchange (ETDEWEB)

Grzybowska, K; Grzybowski, A; Ziolo, J; Rzoska, S J; Paluch, M [Institute of Physics, Silesian University, Uniwersytecka 4, 40-007 Katowice (Poland)

2007-09-19

A surprising slow down in the dielectric secondary {gamma}-relaxation with temperature increasing near the glass transition is confirmed for several polypropylene glycols. The peculiar behavior diminishes as the molecular weight grows. The minimal model (Dyre and Olsen 2003 Phys. Rev. Lett. 91 155703) is applied successfully to describe the temperature dependences of the {gamma}-relaxation times. The minimal model parameters are analyzed for different molecular weights. A molecular explanation of the {gamma}-process anomaly for polypropylene glycols is proposed on the basis of the minimal model prediction.

Rearing Xyleborus volvulus (Coleoptera: Curculionidae) on Media Containing Sawdust from Avocado or Silkbay, With or Without Raffaelea lauricola (Ophiostomatales: Ophiostomataceae).

Science.gov (United States)

Menocal, Octavio; Cruz, Luisa F; Kendra, Paul E; Crane, Jonathan H; Ploetz, Randy C; Carrillo, Daniel

2017-12-08

Like other ambrosia beetles, Xyleborus volvulus Fabricius (Coleoptera: Curculionidae) lives in a mutualistic symbiotic relationship with fungi that serve as food source. Until recently, X. volvulus was not considered a pest, and none of its symbionts were considered plant pathogens. However, recent reports of an association between X. volvulus and Raffaelea lauricola T.C. Harr., Fraedrich & Aghayeva (Ophiostomatales: Ophiostomataceae), the cause of the laurel wilt disease of avocado (Persea americana Mill. [Laurales: Lauraceae]), and its potential role as vector of the pathogen merit further investigation. The objective of this study was to evaluate three artificial media containing sawdust obtained from avocado or silkbay (Persea humilis Nash) for laboratory rearing of X. volvulus. The effect of R. lauricola in the media on the beetle's reproduction was also evaluated. Of the three media, the one with the lowest content of sawdust and intermediate water content provided the best conditions for rearing X. volvulus. Reproduction on this medium was not affected by the sawdust species or the presence of R. lauricola. On the other two media, there was a significant interaction between sawdust species and R. lauricola. The presence of R. lauricola generally had a negative effect on brood production. There was limited colonization of the mycangia of X. volvulus by R. lauricola on media inoculated with the pathogen. From galleries formed within the best medium, there was 50% recovery of R. lauricola, but recovery was much less from the other two media. Here, we report the best artificial substrate currently known for X. volvulus. © The Authors 2017. Published by Oxford University Press on behalf of Entomological Society of America. All rights reserved. For permissions, please e-mail: journals.permissions@oup.com.

Influence of MCM-41 particle on mechanical and morphological behavior of polypropylene

International Nuclear Information System (INIS)

Wang Na; Shao Yawei; Shi Zhaoxin; Zhang Jing; Li Hongwei

2008-01-01

This study investigates the effects of different types of nanoparticles and amount of nanoparticles on morphology and mechanical performance of polypropylene (PP) composites. Three different types of nanoparticles, namely mesoporous MCM-41 (without template), mesoporous MCM-41 (with template), and mesoporous MCM-41, whose pore channels were filled with different flexible polymer inside the pore channels with the aid of supercritical CO 2 are considered. PP composites containing (0.5-5 wt.%) mesoporous MCM-41 were prepared by compounding. The tensile properties of the composites determined as a function of the filler loading and the different types of nanoparticles are found to vary with the different interface between different fillers and the matrix. The results of tensile tests showed that different flexible polymer filled mesoporous MCM-41 nanoparticles could simultaneously provide PP with strengthening and toughening effects at rather low filler content (0.5 wt.%). Scanning electron microscopy studies revealed a good dispersion of the MCM-41-S-PMMA and MCM-41-S-PS particles in the PP matrix and the enhancement of the interface between PP and MCM-41 are obtained

Combination of artificial neural network and genetic algorithm method for modeling of methylene blue adsorption onto wood sawdust from water samples.

Science.gov (United States)

Khajeh, Mostafa; Sarafraz-Yazdi, Ali; Natavan, Zahra Bameri

2016-03-01

The aim of this research was to develop a low price and environmentally friendly adsorbent with abundant of source to remove methylene blue (MB) from water samples. Sawdust solid-phase extraction coupled with high-performance liquid chromatography was used for the extraction and determination of MB. In this study, an experimental data-based artificial neural network model is constructed to describe the performance of sawdust solid-phase extraction method for various operating conditions. The pH, time, amount of sawdust, and temperature were the input variables, while the percentage of extraction of MB was the output. The optimum operating condition was then determined by genetic algorithm method. The optimized conditions were obtained as follows: 11.5, 22.0 min, 0.3 g, and 26.0°C for pH of the solution, extraction time, amount of adsorbent, and temperature, respectively. Under these optimum conditions, the detection limit and relative standard deviation were 0.067 μg L(-1) and <2.4%, respectively. The Langmuir and Freundlich adsorption models were applied to describe the isotherm constant and for the removal and determination of MB from water samples. © The Author(s) 2013.

Determination of effective moisture diffusivity and drying kinetics for poplar sawdust by thermogravimetric analysis under isothermal condition.

Science.gov (United States)

Chen, Dengyu; Zheng, Yan; Zhu, Xifeng

2012-03-01

The current study presents a thermogravimetric method to determine the effective moisture diffusivity and drying kinetics of biomass. Drying experiments on poplar sawdust were performed at four temperatures (60, 70, 80, and 90°C) by a thermogravimetric analyzer (TGA). The major assumption in experimentally determining effective diffusivity by Fick's diffusion equation is that drying is mass transfer limited and temperature remains isothermal during drying. The results indicated that TGA could well achieve these determining conditions. The drying process of sawdust mostly took place in the falling rate period. Midilli-Kucuk model showed the best fit for all experimental data. The effective diffusivity values changed from 9.38 × 10(-10)m(2)/s to 1.38 × 10(-9)m(2)/s within the given temperature range, and the activation energy was calculated to be 12.3 kJ/mol. Copyright © 2011 Elsevier Ltd. All rights reserved.

Quality evaluation of polypropylene packaged corn yogurt during storage

Science.gov (United States)

Aini, Nur; Prihananto, V.; Sustriawan, B.; Astuti, Y.; Maulina, M. R.

2018-01-01

Packaging is an important factor to control the process of quality decrease of any food product, including to determine the shelf life. The objective of this study was to determine changes quality of corn yogurt packaged using polypropylene. The method were using was package yogurt polypropylene, then it was stored in a refrigerator at 5, 10, or 15°C during 21 days. The yogurt was analysed every 7 days over a 21-day period. The results indicate that protein content decreased during storage, while the lactic acid bacteria, total acid, pH, viscosity, and total solids were increased. At the end of storage, the amount of lactic acid bacteria still fulfil the minimum requirements of a probiotic food, with a count of 6.407 log CFU/g. Overal scoring by panelist (scores ranged from 0 to 5) have a 4.78 at the beginning of storage. By the 21st day of storage, yogurt was packaging using transparent polypropylene having a score of 3.85, and that stored in opaque white packaging having a value of 3.95.

Degradation of Polypropylene Membranes Applied in Membrane Distillation Crystallizer

Directory of Open Access Journals (Sweden)

Marek Gryta

2016-03-01

Full Text Available The studies on the resistance to degradation of capillary polypropylene membranes assembled in a membrane crystallizer were performed. The supersaturation state of salt was achieved by evaporation of water from the NaCl saturated solutions using membrane distillation process. A high feed temperature (363 K was used in order to enhance the degradation effects and to shorten the test times. Salt crystallization was carried out by the application of batch or fluidized bed crystallizer. A significant membrane scaling was observed regardless of the method of realized crystallization. The SEM-EDS, DSC, and FTIR methods were used for investigations of polypropylene degradation. The salt crystallization onto the membrane surface accelerated polypropylene degradation. Due to a polymer degradation, the presence of carbonyl groups on the membranes’ surface was identified. Besides the changes in the chemical structure a significant mechanical damage of the membranes, mainly caused by the internal scaling, was also found. As a result, the membranes were severely damaged after 150 h of process operation. A high level of salt rejection was maintained despite damage to the external membrane surface.

USE OF SAWDUST OF PINE (Pinnus patula AS A SOURCE OF FIBER IN DIETS FOR SHEEP IN FEEDLOTS

Directory of Open Access Journals (Sweden)

Cándido Enrique Guerra medina

2010-02-01

Full Text Available Rations for sheep include 5 to 40 % of fibrous sources that can be used as cereal straws, alternate sources of oak or pine sawdust have been used; however its effectiveness has not been researched in depth. With the objective of using an alternative source of fiber in diets for sheep in feedlots, two treatments were assessed for four periods of 14 days each. There were two treatments, one with 30 % pine sawdust (SD and another with 30 % corn straw  (CS. The variables evaluated were average daily gain (ADG, dry matter intake (DMI, ruminal pH, concentration of volatile fatty acids (VFA, and concentration of ammonia. A Completely Randomized Design was used and the data were analyzed using the procedure of repeated measurements. The ADG, concentration of propionic acid, and the average ruminal pH was higher (p

Resterilized Polypropylene Mesh for Inguinal Hernia Repair

African Journals Online (AJOL)

2018-04-19

Apr 19, 2018 ... Conclusion: The use of sterilized polypropylene mesh for the repair of inguinal ... and nonabsorbable materials to reduce the tissue–mesh. INTRODUCTION ... which we have been practicing in our center since we introduced ...

Surface treated polypropylene (PP) fibres for reinforced concrete

Energy Technology Data Exchange (ETDEWEB)

López-Buendía, Angel M., E-mail: buendia@uv.es [AIDICO Technological Institute of Construction, Benjamin Franklin 17, 46380 Paterna, Valencia (Spain); Romero-Sánchez, María Dolores [AIDICO Technological Institute of Construction, Marble Technical Unit, Camí de Castella 4, 03660 Novelda. Alicante (Spain); Climent, Verónica [Lafarge Cementos, Polígono Sepes, Isaac Newton s/n, 46500 Sagunto, Valencia (Spain); Guillem, Celia [AIDICO Technological Institute of Construction, Marble Technical Unit, Camí de Castella 4, 03660 Novelda. Alicante (Spain)

2013-12-15

Surface treatments on a polypropylene (PP) fibre have contributed to the improvement of fibre/concrete adhesion in fibre-reinforced concrete. The treatments to the PP fibre were characterized by contact angle measurements, ATR-IR and XPS to analyse chemical alterations. The surface topography and fibre/concrete interaction were analysed by several microscopic techniques, namely optical petrographic, and scanning electron microscopy. Treatment modified the surface chemistry and topography of the fibre by introducing sodium moieties and created additional fibre surface roughness. Modifications in the fibre surface led to an increase in the adhesion properties between the treated fibres and concrete and an improvement in the mechanical properties of the fibre-reinforced concrete composite as compared to the concrete containing untreated PP fibres. Compatibility with the concrete and increased roughness and mineral surface was also improved by nucleated portlandite and ettringite mineral association anchored on the alkaline PP fibre surface, which is induced during treatment.

Fabrication of polypropylene/silver nanocomposites for biocidal applications

Energy Technology Data Exchange (ETDEWEB)

Oliani, Washington Luiz, E-mail: washoliani@usp.br [Nuclear and Energy Research Institute, IPEN-CNEN/SP, Av. Prof. Lineu Prestes, 2242 – Cidade Universitária – CEP, 05508-000 São Paulo (Brazil); Parra, Duclerc Fernandes; Komatsu, Luiz Gustavo Hiroki [Nuclear and Energy Research Institute, IPEN-CNEN/SP, Av. Prof. Lineu Prestes, 2242 – Cidade Universitária – CEP, 05508-000 São Paulo (Brazil); Lincopan, Nilton [Department of Microbiology, Institute of Biomedical Sciences, University of Sao Paulo, 05508-000, São Paulo (Brazil); Department of Clinical Analysis, School of Pharmacy, University of São Paulo, 05508-000, São Paulo (Brazil); Rangari, Vijaya Kumar [Department of Materials Science and Engineering, Tuskegee University, AL 36088 (United States); Lugao, Ademar Benevolo [Nuclear and Energy Research Institute, IPEN-CNEN/SP, Av. Prof. Lineu Prestes, 2242 – Cidade Universitária – CEP, 05508-000 São Paulo (Brazil)

2017-06-01

This paper presents a study on biocidal effect of polymer nanocomposite films of gamma irradiated polypropylene (PP) and silver nanoparticles. The modified polypropylene was obtained from isotactic polypropylene (iPP) in pellets form by irradiation with gamma rays in the presence of acetylene. A new morphology with long chain branching of PP and distinct rheology is obtained by this process. The blend of 50/50 wt% neat PP and PP modified by gamma radiation were further mixed using a twin screw extruder. The AgNPs were infused into this polymer blend at different concentrations of: 0.1%; 0.25%; 0.5%; 1.0%; 1.0% (PVP), 2.0% and 4.0% by wt%. These polymer nanocomposites were characterized by Raman spectroscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), thermogravimetric analysis (TG), differential scanning calorimetry (DSC), X-ray diffraction (XRD), transmission electron microscopy (TEM), cytotoxicity test and Kirby-Bauer disk diffusion techniques. The bactericidal effect of Pseudomonas aeruginosa (P. aeruginosa) and Staphylococcus aureus (S. aureus) were assessed in detail. - Highlights: • PP film was obtained from iPP in pellets form by γ rays with acetylene and AgNPs • Bactericidal effect of P aeruginosa and S aureus were assessed.

Mechanical properties of polypropylene/calcium carbonate nanocomposites

Directory of Open Access Journals (Sweden)

Daniel Eiras

2009-01-01

Full Text Available The aim of this work was to study the influence of calcium carbonate nanoparticles in both tensile and impact mechanical properties of a polypropylene homopolymer. Four compositions of PP/CaCO3 nanocomposites were prepared in a co-rotational twin screw extruder machine with calcium carbonate content of 3, 5, 7 and 10 wt. (% The tests included SEM analyzes together with EDS analyzer and FTIR spectroscopy for calcium carbonate, tensile and impact tests for PP and the nanocomposites. The results showed an increase in PP elastic modulus and a little increase in yield stress. Brittle-to-ductile transition temperature was reduced and the impact resistance increased with the addition of nanoparticles. From the stress-strain curves we determined the occurrence of debonding process before yielding leading to stress softening. Debonding stress was determined from stress-strain curves corresponding to stress in 1% strain. We concluded that the tensile properties depend on the surface contact area of nanoparticles and on their dispersion. Finally we believe that the toughening was due to the formation of diffuse shear because of debonding process.

The research on the interfacial compatibility of polypropylene composite filled with surface treated carbon fiber

International Nuclear Information System (INIS)

Li, J.

2009-01-01

Dielectric barrier discharges (DBD) in ambient air are used on carbon fiber to improve the fiber surface activity. Carbon fibers with length of 75 μm are placed into the plasma configuration. The interaction between modified carbon fibers and polypropylene (PP) was studied by three-point bending (TPB) test. The chemical changes induced by the treatments on carbon fiber surface are examined using X-ray photoelectron spectroscopy (XPS). XPS results reveal that the carbon fiber modified with the DBD at atmospheric pressure show a significant increase in oxygen and nitrogen concentration. These results demonstrate that the surface of the carbon fiber is more active and hydrophilic after plasma treatments using a DBD operating in ambient air.

Production of bio-oil via hydrothermal liquefaction of birch sawdust

International Nuclear Information System (INIS)

Malins, Kristaps

2017-01-01

Highlights: • NaOH has significant impact on hydrothermal liquefaction of birch sawdust. • High yield of bio-oil (54.1%) was obtained under developed optimal conditions. • Compounds in bio-oil have appropriate chemical structure for hydrocarbon synthesis. • The yield of marketable solid residue with potential for industrial application was 7.1%. • Solid residue has high calorific value (29.8 MJ/kg) and C content (74.6 wt.%). - Abstract: The effect of weight ratio of plywood manufacturing by-product birch sawdust (BS) to water (1/2–1/8), reaction temperature (200–340 °C), initial H 2 pressure (0–10 MPa), residence time (5–90 min), catalysts amount (0.25–7.0 wt.%) and type (FeSO 4 , ZnSO 4 , NiSO 4 , Raney-nickel, Ni65%/SiO 2 −Al 2 O 3 , Na 2 CO 3 and NaOH) on hydrothermal liquefaction of BS was investigated. High yield of bio-oil (54.1%) with calorific value (CV) 24.9 MJ/kg under developed optimal experimental conditions in the presence of NaOH (5 wt.%) utilizing weight ratio of BS to water 1/4, residence time 5 min, mixing speed 250 rpm at 300 °C without pressurized particular inert gas or H 2 atmosphere was achieved. Compounds in bio-oil analyzed by gas chromatography-mass spectrometry (GC-MS) have suitable chemical structures for conversion into renewable hydrocarbons. Marketable solid residue (SR) with yield 7.1%, high CV (29.8 MJ/kg) and perspective characteristics for industrial application was obtained. Produced gas in process analyzed by gas chromatography-thermal conductivity detector (GC–TCD) contains 60.1 vol.% of CO 2 .

The effects of gamma radiation and electron beam on the mechanical properties of polypropylene dominant natural rubber blend

International Nuclear Information System (INIS)

Mar Mar Oo; Khairul Zaman; Tin Hlaing

2001-01-01

The effects of irradiation, with dose ranging from 20 to 100 kGy on the mechanical properties of polypropylene and natural rubber blends (PP/NR blends) were investigated. Crosslinking of the PP/NR blends proved to play a major role in the improvement of the mechanical properties of the blend. The results also revealed that the blend composition the enhancement in properties depend on the irradiation dose and on the concentration of the crosslinking agent. (author)

Carbon ion irradiation induced surface modification of polypropylene

International Nuclear Information System (INIS)

Saha, A.; Chakraborty, V.; Dutta, R.K.; Chintalapudi, S.N.

2001-01-01

Polypropylene was irradiated with 12 C ions of 3.6 and 5.4 MeV energies in the fluence range of 5x10 13 -5x10 14 ions/cm 2 using 3 MV tandem accelerator. Ion penetration was limited to a few microns and surface modifications were investigated by scanning electron microscopy. At the lowest ion fluence only blister formation of various sizes (1-6 μm) were observed, but at higher fluence (1x10 14 ions/cm 2 ) a three-dimensional network structure was found to form. A gradual degradation in the network structure was observed with further increase in the ion fluence. The dose dependence of the changes on surface morphology of polypropylene is discussed

Carbon ion irradiation induced surface modification of polypropylene

Energy Technology Data Exchange (ETDEWEB)

Saha, A. E-mail: abhijit@alpha.iuc.res.in; Chakraborty, V.; Dutta, R.K.; Chintalapudi, S.N

2001-12-01

Polypropylene was irradiated with {sup 12}C ions of 3.6 and 5.4 MeV energies in the fluence range of 5x10{sup 13}-5x10{sup 14} ions/cm{sup 2} using 3 MV tandem accelerator. Ion penetration was limited to a few microns and surface modifications were investigated by scanning electron microscopy. At the lowest ion fluence only blister formation of various sizes (1-6 {mu}m) were observed, but at higher fluence (1x10{sup 14} ions/cm{sup 2}) a three-dimensional network structure was found to form. A gradual degradation in the network structure was observed with further increase in the ion fluence. The dose dependence of the changes on surface morphology of polypropylene is discussed.

Modification of low density polyethylene, isostatic polypropylene and their blends by gamma radiation

International Nuclear Information System (INIS)

Santos Rosa, D. dos

1991-01-01

The effects of the gamma radiation (of a 60 Co source), over low density polyethylene, isostatic polypropylene and their blends of low density polyethylene / polypropylene were studied. The structures modifications were attended by infrared spectrometry (IV), differential scanning calorimeter (DSC), strain-strain measurement, density measurement and scanning electron microscope (SEM). (author)

Sorption of polluting metal ions on a palm tree frond sawdust studied by the means of modified carbon paste electrodes.

Science.gov (United States)

Nouacer, Sana; Hazourli, Sabir; Despas, Christelle; Hébrant, Marc

2015-11-01

Water remediation by adsorption of the metal ions on a low cost sorbent is the frame of the present study. The metal ions adsorption properties of sawdust of palm tree fronds (PTF sawdust) are investigated by both equilibrium measurements and modified carbon paste electrode. The ability to adsorb Cu(II), Cr(VI) and As(III) in significant quantities is demonstrated. Carbon paste electrodes modified by incorporation of PTF sawdust (PTF-CPE) or, for comparison, an organically modified silica for the detection of copper(II) are investigated in term of sensitivity, estimation of number of possible reuses, repeatability and interference effect. A detection limit for Cu(II) analysis of 1.0×10(-8) M has been achieved after 5 min preconcentration and a single PTF-CPE can be used for up to 10 preconcentration-analysis-regeneration cycles. The relative standard deviation (n=9) for the determination of a 10(-6) M Cu(II) solution (pH=5) was about 26%. The effects of Ca(II), As(III) and Cr(VI) on the copper detection are investigated: calcium ions were shown to compete with copper on the same adsorption sites, arsenic(III) has no effect on the copper detection whereas chromium(VI) was shown to enhance the copper detection. Copyright © 2015 Elsevier B.V. All rights reserved.

Effects of Sawdust and Rice husk Additives on Physical Properties of Ceramic Filter

OpenAIRE

Majid. Muhi Shukur; Mohsin Abbas Aswad; Saba Mohamed Bader

2017-01-01

Two processes were employed for forming, specifically,  slip casting and semi-dry press were used to manufacture ceramic filters from local raw materials, red clay and combustible materials  (sawdust and rice husk). Different proportions of additives were used as pores forming agents to create porosity in ceramic filter. Dried filters  were fired at temperature to 1000°C.   It was found that the forming technique and additives have great effect on the physical properties of the produced ...

Mechanical properties of the weld line defect in micro injection molding for various nano filled polypropylene composites

International Nuclear Information System (INIS)

Xie Lei; Ziegmann, Gerhard

2011-01-01

is increased to 30%, the E modulus and tensile strength of micro weld line were increased again compared with the low loading level. → Finally, an empirical prediction equation for micro injection molded weld line strength of nano PP composites was proposed for higher nano filler loading fraction than 10 wt%. - Abstract: The nano filled functional polymer materials have been widely processed with micro injection molding technology for micro electromechanical systems (MEMS) fabrication. As the unfavorable defect in micro injection molding parts, weld line brings reduced mechanical and physical properties, especially for nano filled composites. In this study, polypropylene (PP) was compounded respectively with carbon nano fibers (CNFs) and TiO 2 nano particles at various weight fractions (10, 20, 30, 35 wt%) through co-screws internal mixing. The morphological, thermal and rheological properties of nano composites were characterized by wider angle X-ray diffraction (WXRD), different scanning calorimeter (DSC) and high pressure capillary rheometer. Additionally, under the constant setting of injection molding process parameters in injection molding machine, micro tensile samples with weld lines for each nano filled PP composite were produced. The tensile tests were served as the characterizing method for weld line mechanical properties. The results show that when the CNFs is filled higher than 10 wt%, the tensile strength of samples with weld lines made of nano composites become lower than neat PP. While the raising CNFs content contributes to the improved E modulus of micro injection molded weld lines. Additionally, with the increasing fraction of CNFs in PP, the weld line area's elongation percent is decreased. Whereas for case of TiO 2 , the 10 wt% is the threshold for micro injection molded weld line tensile strength turning from decrease trend to increase. The same as CNFs, elongation of micro weld line samples were in general lower than neat PP as well, due to

Effect of Mixing Process on Polypropylene Modified Bituminous Concrete Mix Properties

OpenAIRE

Noor Zainab Habib; Ibrahim Kamaruddin; Madzalan Napiah; Isa Mohd Tan

2011-01-01

This paper presents a research conducted to investigate the effect of mixing process on polypropylene (PP) modified bitumen mixed with well graded aggregate to form modified bituminous concrete mix. Two mode of mixing, namely dry and wet with different concentration of polymer polypropylene was used with 80/100 pen bitumen, to evaluate the bituminous concrete mix properties. Three percentages of polymer varying from 1-3% by the weight of bitumen was used in this study. Three mixes namely cont...

Influence of electron beam Irradiation on PP/Piassava fiber composite prepared by melt extrusion process

International Nuclear Information System (INIS)

Gomes, Michelle G.; Ferreira, Maiara S.; Oliveira, Rene R.; Silva, Valquiria A.; Teixeira, Jaciele G.; Moura, Esperidiana A.B.

2013-01-01

In the latest years, the interest for the use of natural fibers in materials composites polymeric has increased significantly due to their environmental and technological advantages. Piassava fibers (Attalea funifera) have been used as reinforcement in the matrix of thermoplastic and thermoset polymers. In the present work (20%, in mass), piassava fibers with particle sizes equal or smaller than 250 μm were incorporated in the polypropylene matrix (PP) no irradiated and polypropylene matrix containing 10 % and 30 % of polypropylene treated by electron-beam radiation at 40 kGy (PP/PPi/Piassava). The composites PP/Piassava and PP/PPi/Piassava were prepared by using a twin screw extruder, followed by injection molding. The composite material samples obtained were treated by electron-beam radiation at 40 kGy, using a 1.5 MeV electron beam accelerator, at room temperature, in presence of air. After irradiation treatment, the irradiated and non-irradiated specimens tests samples were submitted to thermo-mechanical tests, melt flow index (MFI), sol-gel analysis, X-Ray diffraction (XRD) and scanning electron microscopy (SEM). (author)

A novel test method for quantifying surface tack of polypropylene compound surfaces

Directory of Open Access Journals (Sweden)

2011-11-01

Full Text Available While adhesiveness is required for polymer surfaces in special applications, tacky surfaces are generally undesirable in many applications like automotive interior parts. The tackiness of polymer surface results from a combination of composition and additivation, and it can change significantly in natural or accelerated ageing. Since there is no established, uniform method to characterize surface tack, the major focus of the present work was on the development of an objective quantification method. A setup having a soft die tip attached to a standard tensile tester was developed aiming for correlation to the human sense of touch. Three different model thermoplastic polyolefin (TPO compound formulations based on a high-impact isotactic polypropylene (iPP composition with varying amounts and types of anti-scratch additives were used for these investigations. As the surface tack phenomenon is related to ageing and weathering, the material’s examination was also performed after various intervals of weathering. The developed method allows a fast assessment of the effect of polymer composition variations and different additive formulations on surface tack and gives identical rankings as the standardized haptic panel.

Mechanical and rheological response of polypropylene/boehmite nanocomposites

CSIR Research Space (South Africa)

Pedrazzoli, D

2014-01-01

Full Text Available In this work the influence of synthetic boehmite alumina (BA) nanoparticles with various surface treatments on the morphology, crystallization behavior and mechanical properties of polypropylene copolymer (PP) nanocomposites was studied...

Effect of processing conditions on the mechanical and thermal properties of high-impact polypropylene nanocomposites

Energy Technology Data Exchange (ETDEWEB)

Furlan, L G [Federal Institute of Rio Grande do Sul, IFRS, Campus Restinga, Estrada Joao Antonio da Silveira, 351, Porto Alegre 91790-400 (Brazil); Ferreira, C I; Dal Castel, C; Santos, K S; Mello, A C.E. [Chemistry Institute, Federal University of Rio Grande do Sul, UFRGS, Av. Bento Goncalves, 9500, Porto Alegre 91501-970 (Brazil); Liberman, S A; Oviedo, M A.S. [Braskem S.A., III Polo Petroquimico, Via Oeste, Lote 5, Triunfo 95853-000 (Brazil); Mauler, R.S., E-mail: mauler@iq.ufrgs.br [Chemistry Institute, Federal University of Rio Grande do Sul, UFRGS, Av. Bento Goncalves, 9500, Porto Alegre 91501-970 (Brazil)

2011-08-25

Highlights: {yields} Polypropylene montmorillonite (PP-MMT) produced at different processing conditions. {yields} Polypropylene Nanocomposites with higher increase on impact resistance. {yields} Higher enhancement on mechanical properties. - Abstract: Polypropylene montmorillonite (PP-MMT) nanocomposites have been prepared by using a co-rotating twin screw extruder. The effects of processing conditions at fixed clay content (5 wt%) on polymer properties were investigated by means of transmission electron microscopy (TEM), flexural modulus, izod impact, dynamic mechanical analysis (DMA), and differential scanning calorimetry (DSC). It was noticed that the morphology and the mechanical properties of polypropylene nanocomposites were affected by different screw shear configuration. The results showed that the higher enhancement on mechanical properties was obtained by medium shear intensity profile instead of high configuration. An exceptional increase (maximum of 282%) on impact resistance was observed.

Effect of processing conditions on the mechanical and thermal properties of high-impact polypropylene nanocomposites

International Nuclear Information System (INIS)

Furlan, L.G.; Ferreira, C.I.; Dal Castel, C.; Santos, K.S.; Mello, A.C.E.; Liberman, S.A.; Oviedo, M.A.S.; Mauler, R.S.

2011-01-01

Highlights: → Polypropylene montmorillonite (PP-MMT) produced at different processing conditions. → Polypropylene Nanocomposites with higher increase on impact resistance. → Higher enhancement on mechanical properties. - Abstract: Polypropylene montmorillonite (PP-MMT) nanocomposites have been prepared by using a co-rotating twin screw extruder. The effects of processing conditions at fixed clay content (5 wt%) on polymer properties were investigated by means of transmission electron microscopy (TEM), flexural modulus, izod impact, dynamic mechanical analysis (DMA), and differential scanning calorimetry (DSC). It was noticed that the morphology and the mechanical properties of polypropylene nanocomposites were affected by different screw shear configuration. The results showed that the higher enhancement on mechanical properties was obtained by medium shear intensity profile instead of high configuration. An exceptional increase (maximum of 282%) on impact resistance was observed.

Study of gel formation in polypropylene modified by gamma irradiation

International Nuclear Information System (INIS)

Oliani, W.L.; Parra, D.F.; Fermino, D.M.; Lima, L.F.C.P.; Lugao, A.B.; Riella, H.G.

2010-01-01

The linearity of the chains of iPP (isotactic polypropylene) confers to this, low melt strength. This fact limits the use of iPP in processes that demand high stretching. The graft of branches confers improvements in its extensional viscosity, resulting in Polypropylene with High Melt Strength (HMS-PP). Preparation process of the HMS-PP, included iPP in pellets, conditioned in plastic container containing acetylene under pressure of 110 kPa and radiation with γ source of 60 Co in the doses of 5, 12.5 and 20 kGy. The gel fraction of the samples was determined by the extraction of soluble components in xylene under boiling for 12 hours at 138 deg C. The soluble part of the samples was decanted with the total volatilization of the xylene to the room temperature (25 deg C) and deposition in glass blades. These samples had been characterized by Optic Microscopy, Scanning Electron Microscopy and Infrared Spectroscopy. In this study of the morphology, we obtained the formation of gel and microgel of polypropylene with higher incidence in HMS-PP 20 kGy. (author)

Comparative effect of steam and gamma irradiation sterilization of sawdust compost on the yield, nutrient and shelf-life of Pleurotus ostreatus (Jacq. Ex.Fr) Kummer stored in two different packaging materials

International Nuclear Information System (INIS)

Kortei, J. N. K.

2015-06-01

The conventional method of decontamination of the spawn substrate sorghum and compost of 'wawa' (Triplochiton scleroxylon) sawdust by the use of steam sterilization has attendant problems. In this thesis the possibility of using gamma radiation to decontaminate sorghum based spawn substrate and the compost before cultivation of the fruit bodies was determined as well as its effectiveness on selected nutritional, physical and organoleptic properties of the fruit bodies. A survey was carried out using the rapid appraisal method to determine the existing methods of sterilization, use of gamma radiation in food preservation, preference of mushrooms in Ghana by consumers and nutritional and medicinal attributes of the mushroom. The resident mycoflora in the sorghum grains and 'wawa' sawdust as well as in the fresh and dry fruitbodies of P. ostreatus was determined by using Standard Decimal Series Dilution technique on two media (Cooke's and DRBC). At the end of the prescribed incubation period of the compost bags, the following parameters were determined: surface mycelia density and contamination, total number of fruit bodies, number of primordial formed, total yield, Biological Efficiency, mycelia growth rate, average stipe length, average cap diameter and mushroom size at each dose applied. The bacterial loads were determined by the conventional microbiological techniques and identification was by the use of the API 20E system. The D IO dose requirement for reduction of fungi and Baccillus cereus were also carried out on the preserved fresh and dry mushroom using Fricke Dosimetry. To ascertain the influence of the different combinations of radiation and steam treatments and packaging material on the nutritional quality of the sporophore formed, proximate analysis and mineral elements composition (Na, Ca, K, P, N, Fe, Zn, Cu, Mg, Pb) were determined by using the International Standard Methods in the Mushroom Industry. Dry curves showing the

Functionalization of silica nanoparticles for polypropylene nanocomposites applications

International Nuclear Information System (INIS)

Bracho, Diego; Palza, Humberto; Quijada, Raul; Dougnac, Vivianne

2011-01-01

Synthetic silica nanospheres of different diameters produced via the sol-gel method were used in order to enhance the barrier properties of the polypropylene-silica nanocomposites. Modification of the silica surface by reaction with organic chlorosilanes was performed in order to improve the particles interaction with the polypropylene matrix and its dispersion. Unmodified and modified silica nanoparticles were characterized using electronic microscopy (TEM), elemental analysis, thermo gravimetric analysis (TGA), and solid state nuclear magnetic resonance (NMR) spectroscopy. Preliminary permeability tests of the polymer-silica nanocomposite films showed no significant change at low particles load (3 wt%) regardless its size or surface functionality, mainly because of the low aspect ratio of the silica nanospheres. However, it is expected that at a higher concentration of silica particles differences will be observed. (author)

Surface modification of polypropylene membrane by polyethylene glycol graft polymerization

Energy Technology Data Exchange (ETDEWEB)

Abednejad, Atiye Sadat, E-mail: atiyeabednejad@gmail.com [Department of Biomedical Engineering, Faculty of New Sciences and Technologies, University of Tehran, P.O. Box 14395-1561, Tehran (Iran, Islamic Republic of); Amoabediny, Ghasem [Department of Life Science Engineering, Faculty of New Sciences and Technologies, University of Tehran, P.O. Box 14395-1561, Tehran (Iran, Islamic Republic of); Research Center for New Technologies in Life Science Engineering, University of Tehran, P.O. Box 63894-14179, Tehran (Iran, Islamic Republic of); Ghaee, Azadeh [Department of Biomedical Engineering, Faculty of New Sciences and Technologies, University of Tehran, P.O. Box 14395-1561, Tehran (Iran, Islamic Republic of)

2014-09-01

Polypropylene hollow fiber microporous membranes have been used in a wide range of applications, including blood oxygenator. The hydrophobic feature of the polypropylene surface causes membrane fouling. To minimize fouling, a modification consisting of three steps: surface activation in H{sub 2} and O{sub 2} plasma, membrane immersion in polyethylene glycol (PEG) and plasma graft polymerization was performed. The membranes were characterized by contact angle measurement, Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), tensile test, scanning electron microscopy (SEM) and atomic force microscopy (AFM). Oxygen transfer of modified membranes was also tested. The stability of grafted PEG was measured in water and in phosphate buffer saline (PBS) at 37 °C. Blood compatibility of modified surfaces was evaluated by the platelet adhesion method. Water contact angel reduction from 110° to 72° demonstrates the enhanced hydrophilicity, and XPS results verify the presence of oxygenated functional groups due to the peak existence in 286 eV as a result of PEG grafting. The results clearly indicate that plasma graft-polymerization of PEG is an effective way for antifouling improvement of polypropylene membranes. Also, the results show that oxygen transfer changes in PEG grafted membranes are not significant. - Highlights: • H{sub 2} and O{sub 2} plasma graft polymerization of PEG on polypropylene membrane was carried out. • Changes in surface properties were investigated by FTIR, XPS, SEM, and AFM. • Surface wettability enhanced as a result of poly ethylene glycol grafting. • PEG grafting degree increase causes reduction of fouling and adhesion.

Storing of Extracts in Polypropylene Microcentrifuge Tubes Yields Contaminant Peak During Ultra-flow Liquid Chromatographic Analysis

OpenAIRE

Kshirsagar, Parthraj R.; Hegde, Harsha; Pai, Sandeep R.

2016-01-01

Background and Aim: This study was designed to understand the effect of storage in polypropylene microcentrifuge tubes and glass vials during ultra-flow liquid chromatographic (UFLC) analysis. Materials and Methods: One ml of methanol was placed in polypropylene microcentrifuge tubes (PP material, Autoclavable) and glass vials (Borosilicate) separately for 1, 2, 4, 8, 10, 20, 40, and 80 days intervals stored at ?4?C. Results: Contaminant peak was detected in methanol stored in polypropylene m...

Morphology and crystalline-phase-dependent electrical insulating properties in tailored polypropylene for HVDC cables

Science.gov (United States)

Zha, Jun-Wei; Yan, Hong-Da; Li, Wei-Kang; Dang, Zhi-Min

2016-11-01

Polypropylene (PP) has become one promising material to potentially replace the cross-link polyethylene used for high voltage direct current cables. Besides the isotactic polypropylene, the block polypropylene (b-PP) and random polypropylene (r-PP) can be synthesized through the copolymerization of ethylene and propylene molecules. In this letter, the effect of morphology and crystalline phases on the insulating electrical properties of PP was investigated. It was found that the introduction of polyethylene monomer resulted in the formation of β and γ phases in b-PP and r-PP. The results from the characteristic trap energy levels indicated that the β and γ phases could induce deep electron traps which enable to capture the carriers. And the space charge accumulation was obviously suppressed. Besides, the decreased electrical conductivity was observed in b-PP and r-PP. It is attributed to the existence of deep traps which can effectively reduce the carrier mobility and density in materials.

An in-depth analysis of the physico-mechanical properties imparted by agricultural fibers and food processing residues in polypropylene biocomposites

Science.gov (United States)

Murdy, Rachel Campbell; Mak, Michelle; Misra, Manjusri; Mohanty, Amar K.

2015-05-01

The use of agricultural and food processing residues as potential reinforcements in plastics has been extensively studied. However, there is a large variation in the mechanical performance of agricultural fiber-based biocomposites due to different processing materials and parameters. An in-depth comparison of the resulting effect of the agricultural filler on the matrix is often not possible given the discrepancy in processing conditions. This study seeks to determine the intrinsic properties of agricultural fibers and food processing residues for their use in polypropylene biocomposites based on a standardization of experimental design. The effect of 25wt% loading of miscanthus, fall-and spring-harvest switchgrass, wheat straw, oat hull, soy hull, soy stalk, hemp and flax on the physico-mechanical properties of polypropylene biocomposites was investigated. The addition of fiber led to an improvement in flexural strength, flexural modulus, and tensile modulus, and a general decrease in tensile strength at yield, elongation at break and Izod impact strength. Scanning electron microscopy highlighted the interfacial adhesion, orientation and distribution of the fibers within the matrix, confirming that fiber length and dispersion within the matrix are positively correlated with mechanical properties. The crystallization of the polypropylene phase and a compositional analysis of the agricultural fibers and processing residues were also compared to offer insight into the effect of the filler's intrinsic properties on the resulting material performance.

An in-depth analysis of the physico-mechanical properties imparted by agricultural fibers and food processing residues in polypropylene biocomposites

International Nuclear Information System (INIS)

Murdy, Rachel Campbell; Mak, Michelle; Misra, Manjusri; Mohanty, Amar K.

2015-01-01

The use of agricultural and food processing residues as potential reinforcements in plastics has been extensively studied. However, there is a large variation in the mechanical performance of agricultural fiber-based biocomposites due to different processing materials and parameters. An in-depth comparison of the resulting effect of the agricultural filler on the matrix is often not possible given the discrepancy in processing conditions. This study seeks to determine the intrinsic properties of agricultural fibers and food processing residues for their use in polypropylene biocomposites based on a standardization of experimental design. The effect of 25wt% loading of miscanthus, fall-and spring-harvest switchgrass, wheat straw, oat hull, soy hull, soy stalk, hemp and flax on the physico-mechanical properties of polypropylene biocomposites was investigated. The addition of fiber led to an improvement in flexural strength, flexural modulus, and tensile modulus, and a general decrease in tensile strength at yield, elongation at break and Izod impact strength. Scanning electron microscopy highlighted the interfacial adhesion, orientation and distribution of the fibers within the matrix, confirming that fiber length and dispersion within the matrix are positively correlated with mechanical properties. The crystallization of the polypropylene phase and a compositional analysis of the agricultural fibers and processing residues were also compared to offer insight into the effect of the filler’s intrinsic properties on the resulting material performance

An in-depth analysis of the physico-mechanical properties imparted by agricultural fibers and food processing residues in polypropylene biocomposites

Energy Technology Data Exchange (ETDEWEB)

Murdy, Rachel Campbell; Mak, Michelle [Bioproducts Discovery and Development Centre, Department of Plant Agriculture, Crop Science Building, University of Guelph, Guelph, ON N1G 2W1 (Canada); Misra, Manjusri; Mohanty, Amar K. [Bioproducts Discovery and Development Centre, Department of Plant Agriculture, Crop Science Building, University of Guelph, Guelph, ON N1G 2W1 (Canada); School of Engineering, Thornbrough Building, University of Guelph, ON N1G 2W1 (Canada)

2015-05-22

The use of agricultural and food processing residues as potential reinforcements in plastics has been extensively studied. However, there is a large variation in the mechanical performance of agricultural fiber-based biocomposites due to different processing materials and parameters. An in-depth comparison of the resulting effect of the agricultural filler on the matrix is often not possible given the discrepancy in processing conditions. This study seeks to determine the intrinsic properties of agricultural fibers and food processing residues for their use in polypropylene biocomposites based on a standardization of experimental design. The effect of 25wt% loading of miscanthus, fall-and spring-harvest switchgrass, wheat straw, oat hull, soy hull, soy stalk, hemp and flax on the physico-mechanical properties of polypropylene biocomposites was investigated. The addition of fiber led to an improvement in flexural strength, flexural modulus, and tensile modulus, and a general decrease in tensile strength at yield, elongation at break and Izod impact strength. Scanning electron microscopy highlighted the interfacial adhesion, orientation and distribution of the fibers within the matrix, confirming that fiber length and dispersion within the matrix are positively correlated with mechanical properties. The crystallization of the polypropylene phase and a compositional analysis of the agricultural fibers and processing residues were also compared to offer insight into the effect of the filler’s intrinsic properties on the resulting material performance.