Automated Plasma Spray (APS) process feasibility study: Plasma spray process development and evaluation

Science.gov (United States)

Fetheroff, C. W.; Derkacs, T.; Matay, I. M.

1979-01-01

An automated plasma spray (APS) process was developed to apply two layer (NiCrAlY and ZrO2-12Y2O3) thermal-barrier coatings to aircraft gas turbine engine blade airfoils. The APS process hardware consists of four subsystems: a mechanical blade positioner incorporating two interlaced six-degree-of-freedom assemblies; a noncoherent optical metrology subsystem; a microprocessor-based adaptive system controller; and commercial plasma spray equipment. Over fifty JT9D first stage turbine blades specimens were coated with the APS process in preliminary checkout and evaluation studies. The best of the preliminary specimens achieved an overall coating thickness uniformity of + or - 53 micrometers, much better than is achievable manually. Factors limiting this performance were identified and process modifications were initiated accordingly. Comparative evaluations of coating thickness uniformity for manually sprayed and APS coated specimens were initiated. One of the preliminary evaluation specimens was subjected to a torch test and metallographic evaluation.

Dielectric Strontium Zirconate Sprayed by a Plasma Torch.

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Sedláček, J.; Janata, Marek

2017-01-01

Roč. 10, č. 4 (2017), s. 225-230 ISSN 2008-2134 Institutional support: RVO:61389021 Keywords : Plasma spraying * Electrical properties * Strontium Zirconate * Insulators Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass OBOR OECD: Ceramics www.pccc.icrc.ac.ir/Articles/18/1/18/1010/

Post-treatment of Plasma-Sprayed Amorphous Ceramic Coatings by Spark Plasma Sintering

Science.gov (United States)

Chraska, T.; Pala, Z.; Mušálek, R.; Medřický, J.; Vilémová, M.

2015-04-01

Alumina-zirconia ceramic material has been plasma sprayed using a water-stabilized plasma torch to produce free standing coatings. The as-sprayed coatings have very low porosity and are mostly amorphous. The amorphous material crystallizes at temperatures above 900 °C. A spark plasma sintering apparatus has been used to heat the as-sprayed samples to temperatures above 900 °C to induce crystallization, while at the same time, a uniaxial pressure of 80 MPa has been applied to their surface. After such post-treatment, the ceramic samples are crystalline and have very low open porosity. The post-treated material exhibits high hardness and significantly increased flexural strength. The post-treated samples have a microstructure that is best described as nanocomposite with the very small crystallites embedded in an amorphous matrix.

Fabrication of copper-based anodes via atmosphoric plasma spraying techniques

Science.gov (United States)

Lu, Chun [Monroeville, PA

2012-04-24

A fuel electrode anode (18) for a solid oxide fuel cell is made by presenting a solid oxide fuel cell having an electrolyte surface (15), mixing copper powder with solid oxide electrolyte in a mixing step (24, 44) to provide a spray feedstock (30,50) which is fed into a plasma jet (32, 52) of a plasma torch to melt the spray feed stock and propel it onto an electrolyte surface (34, 54) where the spray feed stock flattens into lamellae layer upon solidification, where the layer (38, 59) is an anode coating with greater than 35 vol. % based on solids volume.

The Influence of Anode Inner Contour on Atmospheric DC Plasma Spraying Process

Directory of Open Access Journals (Sweden)

Kui Wen

2017-01-01

Full Text Available In thermal plasma spraying process, anode nozzle is one of the most important components of plasma torch. Its inner contour controls the characteristics of plasma arc/jet, determining the motion and heating behaviors of the in-flight particles and hence influencing the coating quality. In this study, the effects of anode inner contour, standard cylindrical nozzle, and cone-shaped Laval nozzle with conical shape diverging exit (CSL nozzle on the arc voltage, net power, thermal efficiency, plasma jet characteristics, in-flight particle behaviors, and coating properties have been systematically investigated under atmospheric plasma spraying conditions. The results show that the cylindrical nozzle has a higher arc voltage, net power, and thermal efficiency, as well as the higher plasma temperature and velocity at the torch exit, while the CSL nozzle has a higher measured temperature of plasma jet. The variation trends of the plasma jet characteristics for the two nozzles are comparable under various spraying parameters. The in-flight particle with smaller velocity of CSL nozzle has a higher measured temperature and melting fraction. As a result, the coating density and adhesive strength of CSL nozzle are lower than those of cylindrical nozzle, but the deposition efficiency is greatly improved.

Characteristics of a Novel Water Plasma Torch

International Nuclear Information System (INIS)

Guo-Hua, Ni; Yue-Dong, Meng; Cheng, Cheng; Yan, Lan

2010-01-01

Relying on heat generated by plasma arc heating liquid water into steam as a swirl gas, a water plasma torch has the distinctive steam generation structure, which has various applications such as in the treatment of organic waste and hydrogen production for fuel cells in future vehicles. The operational features of the water plasma torch and water phase change process in the discharge chamber are investigated based on the temporal evolution of the voltage and current. The optical emission spectrum measurement shows that the water molecule in the plasma is decomposed into H, OH and O radicals. As the electrodes do not require water-cooling, the thermal efficiency of the torch is very high, which is confirmed by analytical calculation and experimental measurement

Characterization of plasma sprayed NiCrAlY-Yttria stabilized zirconia coatings

International Nuclear Information System (INIS)

Bhave, V.S.; Rakhasia, R.H.; Tripathy, P.K.; Hubli, R.C.; Sengupta, P.; Bhanumurthy; Satpute, R.U.; Sreekumar, K.P.; Thiyagarajan, T.K.; Padmanabhan, P.V.A.

2004-01-01

Plasma sprayed coatings of yttria stabilized zirconia are used in many advanced technologies for thermal and chemical barrier applications. Development and characterization of NiCrAlY-yttria stabilized zirconia duplex coatings on Inconel substrates is reported in this paper. Plasma spraying was carried out using the 40 kW atmospheric plasma spray facility at the Laser and Plasma Technology Division, BARC. A bond coat of NiCrAlY was deposited on Inconel substrates and yttria stabilized zirconia (YSZ) was deposited over the bond coat. The coatings have been characterized by x-ray diffraction and EPMA. It is observed that the coating characteristics are affected by the input power to the torch. (author)

Modelling of arc behaviour inside a F4 APS torch

International Nuclear Information System (INIS)

Ramachandran, K; Marques, J-L; Vassen, R; Stoever, D

2006-01-01

The plasma arc inside the F4 torch used for atmospheric plasma spraying is characterized by means of analytical and numerical methods. A simplified analytical model is formulated to understand the physical behaviour of the plasma arc. A three-dimensional numerical model is developed to simulate the realistic plasma arc flow inside the torch. At a given torch power and gas flow rate, possible combinations of the arc core radius and arc length are predicted. The thermodynamic principle of minimum entropy production is used to determine the combination of arc core radius and arc length, which corresponds to the actual physical situation of the arc inside the torch. The effect of arc current and gas flow rate on the plasma arc characteristics is clarified. The effect of hydrogen content in the plasma gas on its velocity and temperature profiles at the nozzle exit is shown. Predicted torch efficiencies are comparable to measured ones. The results of the numerical model are similar to that an analytical model. Previously published experimental and numerical results support part of the present results

On reactive suspension plasma spraying of calcium titanate

OpenAIRE

Kotlan, J. (Jiří); Pala, Z. (Zdeněk); Mušálek, R. (Radek); Ctibor, P. (Pavel)

2016-01-01

This study shows possibility of preparation of calcium titanate powder and coatings by reactive suspension plasma spraying. Suspension of mixture of calcium carbonate (CaCO3) and titanium dioxide (TiO2) powders in ethanol was fed into hybrid plasma torch with a DC-arc stabilized by a water–argon mixture (WSP-H 500). Various feeding distances and angles were used in order to optimize suspension feeding conditions. In the next step, the coatings were deposited on stainless steel substrates and ...

Power supply controlled for plasma torch generation

International Nuclear Information System (INIS)

Diaz Z, S.

1996-01-01

The high density of energy furnished by thermal plasma is profited in a wide range of applications, such as those related with welding fusion, spray coating and at the present in waste destruction. The waste destruction by plasma is a very attractive process because the remaining products are formed by inert glassy grains and non-toxic gases. The main characteristics of thermal plasmas are presented in this work. Techniques based on power electronics are utilized to achieve a good performance in thermal plasma generation. This work shown the design and construction of three phase control system for electric supply of thermal plasma torch, with 250 kw of capacity, as a part of the project named 'Destruction of hazard wastes by thermal plasma' actually working in the Instituto Nacional de Investigaciones Nucleares (ININ). The characteristics of thermal plasma and its generation are treated in the first chapter. The A C controllers by thyristors applied in three phase arrays are described in the chapter II, talking into account the power transformer, rectifiers bank and aliasing coil. The chapter III is dedicated in the design of the trigger module which controls the plasma current by varying the trigger angle of the SCR's; the protection and isolating unit are also presented in this chapter. The results and conclusions are discussed in chapter IV. (Author)

Three-dimensional modelling of a dc non-transferred arc plasma torch

International Nuclear Information System (INIS)

Li Heping; Chen Xi

2001-01-01

Three-dimensional (3D) modelling results are presented concerning a direct current (dc) non-transferred arc plasma torch with axisymmetrical geometrical configuration and axisymmetrical boundary conditions. It is shown that the arc is locally attached at the anode surface of the plasma torch, and the heat transfer and plasma flow within the torch are of 3D features. The predicted arc root location at the anode surface and arc voltage of the torch are very consistent with corresponding experimental results. (author)

An evaluation of the electric arc spray and (HPPS) processes for the manufacturing of high power plasma spraying MCrAIY coatings

Science.gov (United States)

Sacriste, D.; Goubot, N.; Dhers, J.; Ducos, M.; Vardelle, A.

2001-06-01

The high power plasma torch (PlazJet) can be used to spray refractory ceramics with high spray rates and deposition efficiency. It can provide dense and hard coating with high bond strengths. When manufacturing thermal barrier coatings, the PlazJet gun is well adapted to spraying the ceramic top coat but not the MCrAIY materials that are used as bond coat. Arc spraying can compete with plasma spraying for metallic coatings since cored wires can be used to spray alloys and composites. In addition, the high production rate of arc spraying enables a significant decrease in coating cost. This paper discusses the performances of the PlazJet gun, and a twin-wire are spray system, and compares the properties and cost of MCrAIY coatings made with these two processes. For arc spraying, the use of air or nitrogen as atomizing gas is also investigated.

Carbon dioxide elimination and regeneration of resources in a microwave plasma torch

International Nuclear Information System (INIS)

Uhm, Han S.; Kwak, Hyoung S.; Hong, Yong C.

2016-01-01

Carbon dioxide gas as a working gas produces a stable plasma-torch by making use of 2.45 GHz microwaves. The temperature of the torch flame is measured by making use of optical spectroscopy and a thermocouple device. Two distinctive regions are exhibited, a bright, whitish region of a high-temperature zone and a bluish, dimmer region of a relatively low-temperature zone. The bright, whitish region is a typical torch based on plasma species where an analytical investigation indicates dissociation of a substantial fraction of carbon dioxide molecules, forming carbon monoxides and oxygen atoms. The emission profiles of the oxygen atoms and the carbon monoxide molecules confirm the theoretical predictions of carbon dioxide disintegration in the torch. Various hydrocarbon materials may be introduced into the carbon dioxide torch, regenerating new resources and reducing carbon dioxide concentration in the torch. As an example, coal powders in the carbon dioxide torch are converted into carbon monoxide according to the reaction of CO_2 + C → 2CO, reducing a substantial amount of carbon dioxide concentration in the torch. In this regards, the microwave plasma torch may be one of the best ways of converting the carbon dioxides into useful new materials. - Highlights: • Carbon dioxide gas produces a plasma-torch by making use of 2.45 GHz microwaves. • The temperature measurement of torch flame by optical spectroscopy. • Disintegration of carbon dioxide into carbon monoxide and oxygen atom. • Emission profiles of carbon monoxide confirm disintegration theory. • Conversion of carbon dioxide into carbon monoxide in the plasma torch. - This article presents carbon-dioxide plasma torch operated by microwaves and its applications to regeneration of new resources, eliminating carbon dioxide molecules.

Operational features and air plasma characteristics of a thermal plasma torch with hollow electrodes

International Nuclear Information System (INIS)

Hur, Min; Kim, Keun Su; Hong, Sang Hee

2003-01-01

The operational features and thermal plasma characteristics of a plasma torch with hollow electrodes are investigated based on their dependence on input current, gas flow rate and electrode diameter when air is used as a plasma gas. A plasma torch with a hollow cathode and anode has been designed and fabricated, and the arc voltages and thermal efficiencies are measured from its discharge. The newly modified similarity criteria are derived from the measured data related to torch performances. From the fact that these criteria successfully describe both the arc voltage and thermal efficiency behaviour of the torch, depending on its operating and geometrical parameters, it is proved that they can be usefully applied to the design and operation of high power torches. For the numerical modelling of the interior region of the torch, a cold flow analysis is employed along with a simplified balance equation of the Lorentz and gas dynamic drag forces in order to determine a cathode spot position on the cathode surface. The validity of this method is confirmed by comparison of the calculated and measured net powers. As a practically useful result of this analysis, carried out through this numerical and experimental work, it is suggested that low input current, high gas flow rate and relatively large electrode diameter are more favourable as appropriate operating conditions of the torch for the efficient treatment of hazardous organic wastes

Positioning system of a torch used in thermal spray coatings applications

Directory of Open Access Journals (Sweden)

Edgar Absalón Torres-Barahona

2016-07-01

Full Text Available This paper presents the design, construction and performance evaluation of a positioning system used for the deposition of coatings with molten particles, by using a torch CastoDyn Ds 8000 thermal spray with oxyacetylene combustion. The design has been done with parameters obtained in the laboratory of materials of the Universidad Pedagógica y Tecnológica de Colombia, and the information determined from the evaluation of the device, allows to control the main process variables as the projection distance, flow powder, torch speed and rotation speed of the sample holder; this has been seen in coatings made in application tests zirconia / nickel on a carbon steel substrate and analyzed with Scanning Electron Microscopy - SEM.

Decontamination of biological warfare agents by a microwave plasma torch

International Nuclear Information System (INIS)

Lai, Wilson; Lai, Henry; Kuo, Spencer P.; Tarasenko, Olga; Levon, Kalle

2005-01-01

A portable arc-seeded microwave plasma torch running stably with airflow is described and applied for the decontamination of biological warfare agents. Emission spectroscopy of the plasma torch indicated that this torch produced an abundance of reactive atomic oxygen that could effectively oxidize biological agents. Bacillus cereus was chosen as a simulant of Bacillus anthracis spores for biological agent in the decontamination experiments. Decontamination was performed with the airflow rate of 0.393 l/s, corresponding to a maximum concentration of atomic oxygen produced by the torch. The experimental results showed that all spores were killed in less than 8 s at 3 cm distance, 12 s at 4 cm distance, and 16 s at 5 cm distance away from the nozzle of the torch

Feasibility of suspension spraying of yttria-stabilized zirconia with water-stabilized plasma torch

Czech Academy of Sciences Publication Activity Database

Mušálek, Radek; Bertolissi, Gabriele; Medřický, J.; Kotlan, Jiří; Pala, Zdeněk; Curry, N.

2015-01-01

Roč. 268, April (2015), s. 58-62 ISSN 0257-8972. [Rencontres Internationales de la Projection Thermique/6./. Limoges, 11.12.2013-13.12.2013] R&D Projects: GA ČR(CZ) GPP108/12/P552 Institutional support: RVO:61389021 Keywords : Thermal spray coating * Suspension spray ing * Thermal barrier coating * Water-stabilized plasma * High enthalpy plasma Subject RIV: JK - Corrosion ; Surface Treatment of Materials Impact factor: 2.139, year: 2015 http://www.sciencedirect.com/science/article/pii/S025789721400680X

Development of suspension plasma sprayed alumina coatings with high enthalpy plasma torch

Czech Academy of Sciences Publication Activity Database

Tesař, Tomáš; Mušálek, Radek; Medřický, Jan; Kotlan, Jiří; Lukáč, František; Pala, Zdeněk; Ctibor, Pavel; Chráska, Tomáš; Houdková, Š.; Rimal, V.; Curry, N.

2017-01-01

Roč. 325, September (2017), s. 277-288 ISSN 0257-8972 R&D Projects: GA ČR GA15-12145S Institutional support: RVO:61389021 Keywords : Suspension plasma spraying * Aluminium oxide * Mechanical properties * Hardness * Adhesion * Wear resistance Subject RIV: JK - Corrosion ; Surface Treatment of Materials OBOR OECD: Coating and films Impact factor: 2.589, year: 2016 http://www.sciencedirect.com/science/article/pii/S0257897217306424

Plasma Spray-Physical Vapor Deposition (PS-PVD) of Ceramics for Protective Coatings

Science.gov (United States)

Harder, Bryan J.; Zhu, Dongming

2011-01-01

In order to generate advanced multilayer thermal and environmental protection systems, a new deposition process is needed to bridge the gap between conventional plasma spray, which produces relatively thick coatings on the order of 125-250 microns, and conventional vapor phase processes such as electron beam physical vapor deposition (EB-PVD) which are limited by relatively slow deposition rates, high investment costs, and coating material vapor pressure requirements. The use of Plasma Spray - Physical Vapor Deposition (PS-PVD) processing fills this gap and allows thin (deposited and multilayer coatings of less than 100 microns to be generated with the flexibility to tailor microstructures by changing processing conditions. Coatings of yttria-stabilized zirconia (YSZ) were applied to NiCrAlY bond coated superalloy substrates using the PS-PVD coater at NASA Glenn Research Center. A design-of-experiments was used to examine the effects of process variables (Ar/He plasma gas ratio, the total plasma gas flow, and the torch current) on chamber pressure and torch power. Coating thickness, phase and microstructure were evaluated for each set of deposition conditions. Low chamber pressures and high power were shown to increase coating thickness and create columnar-like structures. Likewise, high chamber pressures and low power had lower growth rates, but resulted in flatter, more homogeneous layers

Development and Use of the Dual-Mode Plasma Torch

International Nuclear Information System (INIS)

Womack, R.; Shuey, M.

2002-01-01

After several years of development, a commercially available high-temperature treatment system has been developed and installed that treats heterogeneous low-level radioactive waste. High temperature plasma processing, unique torch design and operating features make it feasible to achieve a volume reduced, permanent, high integrity waste form while eliminating the personnel exposure and costs associated with conventional sorting, characterizing and handling. Plasma technology can also be used to treat previous conditioned waste packages that no longer meet the current acceptance criteria for final disposal. Plasma treatment can result, in many cases, in a substantial volume reduction, which lowers the final disposal costs. This paper covers the recently patented dual mode plasma torch design(1), the lessons learned that fostered its development and the advantages it brings to radioactive waste processing. This paper also provides current full scale Plasma Arc Centrifugal Treatment (PACT) project status and how the dual mode torch is being used in the PACT system

Numerical simulation of a novel non-transferred arc plasma torch operating with nitrogen

International Nuclear Information System (INIS)

Hiremath, Gavisiddayya; Kandasamy, Ramachandran; Ganesh, Ravi

2015-01-01

High power plasma torches with higher electro-thermal efficiency are required for industrial applications. To increase the plasma power and electrothermal efficiency, conventional torches are being modified to operate with molecular gases such as air and nitrogen. Since increasing arc current enhances the heat loss to the anode, torches are being developed to operate under high voltage and low current. The plasma flow dynamics and electromagnetic coupling with plasma flow inside the torch etc. are highly complex and knowledge on the same is required to develop high torches with higher efficiency. Unfortunately detailed experimentation on the same is very difficult. Numerical modeling and simulation is one of the best tools to understand the physics involved in such complex processes. A 2D numerical model is developed to simulate the characteristics of the plasma inside the torch. Though plasma is not in local thermodynamic equilibrium (LTE) close to the electrodes, LTE is assumed everywhere in the plasma to avoid complex and time consuming calculations. Other valid assumptions used in the model are plasma flow is optically thin, laminar and incompressible. Flow, energy and electromagnetic equations are solved with appropriate boundary conditions and volume sources using SIMPLE algorithm with finite volume method. Temperature dependent thermophysical properties of nitrogen are used for the simulations. Simulations are carried out for different experimental conditions. The effects of arc current, gas flow rate of plasma generating gas and sheath gas injected above the bottom anode on the arc voltage, electrothermal efficiency of the torch, plasma temperature and plasma velocity are simulated. Predicted results are compared with experimental results. (author)

Carbon dioxide elimination and regeneration of resources in a microwave plasma torch.

Science.gov (United States)

Uhm, Han S; Kwak, Hyoung S; Hong, Yong C

2016-04-01

Carbon dioxide gas as a working gas produces a stable plasma-torch by making use of 2.45 GHz microwaves. The temperature of the torch flame is measured by making use of optical spectroscopy and a thermocouple device. Two distinctive regions are exhibited, a bright, whitish region of a high-temperature zone and a bluish, dimmer region of a relatively low-temperature zone. The bright, whitish region is a typical torch based on plasma species where an analytical investigation indicates dissociation of a substantial fraction of carbon dioxide molecules, forming carbon monoxides and oxygen atoms. The emission profiles of the oxygen atoms and the carbon monoxide molecules confirm the theoretical predictions of carbon dioxide disintegration in the torch. Various hydrocarbon materials may be introduced into the carbon dioxide torch, regenerating new resources and reducing carbon dioxide concentration in the torch. As an example, coal powders in the carbon dioxide torch are converted into carbon monoxide according to the reaction of CO2 + C → 2CO, reducing a substantial amount of carbon dioxide concentration in the torch. In this regards, the microwave plasma torch may be one of the best ways of converting the carbon dioxides into useful new materials. Copyright © 2015 Elsevier Ltd. All rights reserved.

Design and test of a large plasma torch for environmental recycling

International Nuclear Information System (INIS)

Tuszewski, M.

1996-01-01

A 2.5-inch inductive plasma torch has been tested with up to 600 kW rf power and with argon, nitrogen, and oxygen gases. A complete power balance is obtained from electrical, thermal, and radiation measurements. These data indicate that torch efficiencies of up to 30% are obtained with molecular gases, while efficiencies around 15% are obtained with argon. The efficiencies obtained with molecular gases almost triple earlier torch efficiencies and confirm substantially the predictions of a torch model developed during a previous CRADA. Torch efficiencies of up to 50% could be obtained in future tests with an improved rf power supply, with steam gas, and with larger torch dimensions. Future applications of the Plasma Energy Recycle and Conversion (PERC) process could include the high explosives of DOE's nuclear weapons, chemical and biological remediation, and the treatment and volume reduction of radioactive mixed waste

Melting characteristics of a plasma torch melter according to the waste feeding method

International Nuclear Information System (INIS)

Kim, T. W.; Choi, J. R.; Park, S. C.; Lu, C. S.; Park, J. K.; Hwang, T. W.; Shin, S. W.

2001-01-01

By using a batch type plasma torch melting system, continuous feeding and melting tests of non-combustible waste were executed. Using the results, the establishment of a heat transfer model and its verification were executed; the characteristics of the molten slag, exhaust gas, fly dust, volatilization of Cs, and leaching of slag were analyzed. In order to establish the heat transfer mode, the followings were considered; the electrical energy supplied to the plasma torch, the absorbed energy to the plasma torch for generating the plasma gas, the absorbed energy to the cooling water of the plasma torch, the energy supplied to the melter from the plasma gas by radiant heat, the energy loss through the exhaust gas, the waste melting energy, and the heating energy of an inner crucible and the melter. The concrete and soil were melted for the verification of the model. The waste was fed through waste feeder by the amount of 0.5kg or 1kg that was calculated by using the model. The experiment for the verification resulted in that the model was fitted well until the melter was heated sufficiently. If the electrical energy of 128kW were supplied to the plasma torch, energy balance of the plasma melting system was calculated with the model: the absorbed energy to the plasma torch for generating the plasma gas (27kW), the absorbed energy to the cooling water of the plasma torch (0∼ 36kW), the energy loss through the exhaust gas (5 ∼ 8kW), the waste melting energy (14kW), and the heating energy of an inner crucible and the melter (82 ∼ 43kW)

Novel Prospects for Plasma Spray-Physical Vapor Deposition of Columnar Thermal Barrier Coatings

Science.gov (United States)

Anwaar, Aleem; Wei, Lianglinag; Guo, Qian; Zhang, Baopeng; Guo, Hongbo

2017-12-01

Plasma spray-physical vapor deposition (PS-PVD) is an emerging coating technique that can produce columnar thermal barrier coatings from vapor phase. Feedstock treatment at the start of its trajectory in the plasma torch nozzle is important for such vapor-phase deposition. This study describes the effects of the plasma composition (Ar/He) on the plasma characteristics, plasma-particle interaction, and particle dynamics at different points spatially distributed inside the plasma torch nozzle. The results of calculations show that increasing the fraction of argon in the plasma gas mixture enhances the momentum and heat flow between the plasma and injected feedstock. For the plasma gas combination of 45Ar/45He, the total enthalpy transferred to a representative powder particle inside the plasma torch nozzle is highest ( 9828 kJ/kg). Moreover, due to the properties of the plasma, the contribution of the cylindrical throat, i.e., from the feed injection point (FIP) to the start of divergence (SOD), to the total transferred energy is 69%. The carrier gas flow for different plasma gas mixtures was also investigated by optical emission spectroscopy (OES) measurements of zirconium emissions. Yttria-stabilized zirconia (YSZ) coating microstructures were produced when using selected plasma gas compositions and corresponding carrier gas flows; structural morphologies were found to be in good agreement with OES and theoretical predictions. Quasicolumnar microstructure was obtained with porosity of 15% when applying the plasma composition of 45Ar/45He.

Controlling Microstructure of Yttria-Stabilized Zirconia Prepared from Suspensions and Solutions by Plasma Spraying with High Feed Rates.

Czech Academy of Sciences Publication Activity Database

Mušálek, Radek; Medřický, Jan; Tesař, Tomáš; Kotlan, Jiří; Pala, Zdeněk; Lukáč, František; Illková, Ksenia; Hlína, Michal; Chráska, Tomáš; Sokołowski, P.; Curry, N.

2017-01-01

Roč. 26, č. 8 (2017), s. 1787-1803 ISSN 1059-9630 R&D Projects: GA ČR GA15-12145S Institutional support: RVO:61389021 Keywords : hybrid plasma torch * microstructure * solution * precursor spraying * suspension spraying * thermal barrier * coatings (TBCs) * water-stabilized plasma * yttria-stabilized zirconia (YSZ) Subject RIV: JK - Corrosion ; Surface Treatment of Materials OBOR OECD: Coating and films Impact factor: 1.488, year: 2016 https://link.springer.com/ article /10.1007/s11666-017-0622-x

Comparative analysis of turbulent effects on thermal plasma characteristics inside the plasma torches with rod- and well-type cathodes

International Nuclear Information System (INIS)

Hur, Min; Hong, Sang Hee

2002-01-01

The thermal plasma characteristics inside the two non-transferred plasma torches with rod-type cathode (RTC) and well-type cathode (WTC) are analysed in conjunction with turbulent effects on them in the atmospheric-pressure conditions. A control volume method and a modified semi-implicit pressure linked equations revised algorithm are used for solving the governing equations, i.e. conservation equations of mass, momentum, and energy together with a current continuity equation for arc discharge. A cold flow analysis is introduced to find the cathode spot position in the WTC torch, and both the laminar and turbulent models are employed to gain a physical insight into the turbulent effects on the thermal plasma characteristics produced inside the two torches. The numerical analysis for an RTC torch shows that slightly different values of plasma temperature and velocity between the laminar and turbulent calculations occur and the radial temperature profiles are constricted at the axis with increasing the gas flow rate, and that the large turbulent viscosities appear mostly near the anode wall. These calculated results indicate that the turbulent effects on the thermal plasma characteristics are very weak in the whole discharge region inside the RTC torch. On the other hand, the calculated results of the two numerical simulations for a WTC torch present that the significantly different values of plasma characteristics between the two models appear in the whole torch region and the plasma temperatures decrease with increasing the gas flow rate because the relatively strong turbulent effects are prevailing in the entire interior region of the WTC torch. From the comparisons of plasma net powers calculated and measured in this work, the turbulent modelling turns out to provide the more accurately calculated results close to the measured ones compared with the laminar one, especially for the torch with WTC. This is because the turbulent effects are considerably strong in

Calculation of DC Arc Plasma Torch Voltage- Current Characteristics Based on Steebeck Model

International Nuclear Information System (INIS)

Gnedenko, V.G.; Ivanov, A.A.; Pereslavtsev, A.V.; Tresviatsky, S.S.

2006-01-01

The work is devoted to the problem of the determination of plasma torches parameters and power sources parameters (working voltage and current of plasma torch) at the predesigning stage. The sequence of calculation of voltage-current characteristics of DC arc plasma torch is proposed. It is shown that the simple Steenbeck model of arc discharge in cylindrical channel makes it possible to carry out this calculation. The results of the calculation are confirmed by the experiments

Recent Developments in Suspension Plasma Sprayed Titanium Oxide and Hydroxyapatite Coatings

Science.gov (United States)

Jaworski, R.; Pawlowski, L.; Pierlot, C.; Roudet, F.; Kozerski, S.; Petit, F.

2010-01-01

The paper aims at reviewing of the recent studies related to the development of suspension plasma sprayed TiO2 and Ca5(PO4)3OH (hydroxyapatite, HA) coatings as well as their multilayer composites obtained onto stainless steel, titanium and aluminum substrates. The total thickness of the coatings was in the range 10 to 150 μm. The suspensions on the base of distilled water, ethanol and their mixtures were formulated with the use of fine commercial TiO2 pigment crystallized as rutile and HA milled from commercial spray-dried powder or synthesized from calcium nitrate and ammonium phosphate in an optimized reaction. The powder was crystallized as hydroxyapatite. Pneumatic and peristaltic pump liquid feeders were applied. The injection of suspension to the plasma jet was studied carefully with the use of an atomizer injector or a continuous stream one. The injectors were placed outside or inside of the anode-nozzle of the SG-100 plasma torch. The stream of liquid was tested under angle right or slightly backwards with regard to the torch axis. The sprayed deposits were submitted to the phase analysis by the use of x-ray diffraction. The content of anatase and rutile was calculated in the titanium oxide deposits as well as the content of the decomposition phases in the hydroxyapatite ones. The micro-Raman spectroscopy was used to visualize the area of appearance of some phases. Scratch test enabled to characterize the adhesion of the deposits, their microhardness and friction coefficient. The electric properties including electron emission, impedance spectroscopy, and dielectric properties of some coatings were equally tested.

A comprehensive study of different gases in inductively coupled plasma torch operating at one atmosphere

International Nuclear Information System (INIS)

Punjabi, Sangeeta B.; Joshi, N. K.; Mangalvedekar, H. A.; Lande, B. K.; Das, A. K.; Kothari, D. C.

2012-01-01

A numerical study is done to understand the possible operating regimes of RF-ICP torch (3 MHz, 50 kW) using different gases for plasma formation at atmospheric pressure. A two dimensional numerical simulation of RF-ICP torch using argon, nitrogen, oxygen, and air as plasma gas has been investigated using computational fluid dynamic (CFD) software fluent (c) . The operating parameters varied here are central gas flow, sheath gas flow, RF-power dissipated in plasma, and plasma gas. The temperature contours, flow field, axial, and radial velocity profiles were investigated under different operating conditions. The plasma resistance, inductance of the torch, and the heat distribution for various plasma gases have also been investigated. The plasma impedance of ICP torch varies with different operating parameters and plays an important role for RF oscillator design and power coupling. These studies will be useful to decide the design criteria for ICP torches required for different material processing applications.

Characteristics of a 30 Km plasma torch

International Nuclear Information System (INIS)

Busnardo Neto, J.; Rodrigues, V.A.; Boeckelmann, H.K.; Sakanaka, P.H.

1987-01-01

Plasma torches are important for countries with a high hydroelectric energy supply as is the case of Brazil. Indeed a 1.5 million dollar program is in its early stages at COSIPA with a view of substitution of fossil fuels in Brazilian steel mills. The first step in this program is the development of a 1.5 MW torch to preheat steel ladles (120 tons of molten metal). At UNICAMP a 30 kW torch for heating air using scaling law techniques was built. The current, voltage and efficiency were measured over a wide range of parameters and the results yield the expected VαI -0.3 law. This torch was used to preheat a foundry ladle (100 kg of metal). The final desired temperatures (300-400 0 C externally, 1300 0 C internally) were obtained in thirty minutes. Higher temperatures can be obtained with less power of an insulating material is used. The results were confirmed with a computer simulation program which integrates in time the heat conduction equations. (author) [pt

Optical plasma torch electron bunch generation in plasma wakefield accelerators

Directory of Open Access Journals (Sweden)

G. Wittig

2015-08-01

Full Text Available A novel, flexible method of witness electron bunch generation in plasma wakefield accelerators is described. A quasistationary plasma region is ignited by a focused laser pulse prior to the arrival of the plasma wave. This localized, shapeable optical plasma torch causes a strong distortion of the plasma blowout during passage of the electron driver bunch, leading to collective alteration of plasma electron trajectories and to controlled injection. This optically steered injection is more flexible and faster when compared to hydrodynamically controlled gas density transition injection methods.

Characterisation of plasmas produced by the "Torche a Injection Axiale"

NARCIS (Netherlands)

Jonkers, J.; Selen, L.J.M.; Mullen, van der J.J.A.M.; Regt, de J.M.; Timmermans, E.A.H.; Schram, D.C.

1996-01-01

Summary form only given. The Torche a Injection Axiale (TIA), i.e. torch with axial gas injection, was developed by the group of Moisan in 1993. We report on the investigations on two different kind of plasmas created by the TIA: one with helium and the other with argon as main gas. Using absolute

Characterisation of plasmas produced by the "Torche a Injection Axciale"

NARCIS (Netherlands)

Jonkers, J.; Selen, L.J.M.; Mullen, van der J.J.A.M.; Regt, de J.M.; Timmermans, E.A.H.; Schram, D.C.

1996-01-01

Summary form only given. The Torche a Injection Axiale (TIA), i.e. torch with axial gas injection, was developed by the group of Moisan in 1993. We report on the investigations on two different kind of plasmas created by the TIA: one with helium and the other with argon as main gas. Using absolute

Experimental investigation of gas heating and dissociation in a microwave plasma torch at atmospheric pressure

International Nuclear Information System (INIS)

Su, Liu; Kumar, Rajneesh; Ogungbesan, Babajide; Sassi, Mohamed

2014-01-01

Highlights: • Atmospheric-pressure microwave plasma torch. • Gas heating and dissociation. • Parametric studies of plasma operating conditions. • Local thermal equilibrium plasma. - Abstract: Experimental investigations are made to understand gas heating and dissociation in a microwave (MW) plasma torch at atmospheric pressure. The MW induced plasma torch operates at 2.45 GHz frequency and up to 2 kW power. Three different gas mixtures are injected in the form of axial flow and swirl flow in a quartz tube plasma torch to experimentally investigate the MW plasma to gas energy transfer. Air–argon, air–air and air–nitrogen plasmas are formed and their operational ranges are determined in terms of gas flow rates and MW power. Visual observations, optical emission spectroscopy and K-type thermocouple measurements are used to characterize the plasma. The study reveals that the plasma structure is highly dependent on the carrier gas type, gas flow rate, and MW power. However, the plasma gas temperature is shown not to vary much with these parameters. Further spectral and analytical analysis show that the plasma is in thermal equilibrium and presents very good energy coupling between the microwave power and gas heating and dissociation. The MW plasma torch outlet temperature is also measured and found to be suitable for many thermal heating and chemical dissociation applications

Surface Modification of Metals using Plasma Torch

International Nuclear Information System (INIS)

Hassan, A.

2009-01-01

Low temperature plasma nitriding of 304L stainless steel is performed using a home made low power direct-current plasma torch. Plasma nitriding is carried out in temperature range of 300-550 degree C for 1 to 4 hours, in various N 2 H 2 gas mixture ratios at about 5 Torr pressure and torch power 300 Watts. The effect of treatment time, temperature and working gas composition on the microstructure and mechanical properties of plasma nitrided surface layers is investigated. The microstructure, phase composition and micro hardness profile of the nitrided surface layers are characterized by optical microscopy, scanning electron microscope (SEM), X-ray diffraction (XRD) and Vickers micro hardness tester. The results show that plasma treatment for 14 h over a temperature range of 300 - 550 degree C yields nitride case depth of 20 - 50 μm and the hardness of the nitrided layer is in the range of 700-1250 HV. Plasma nitriding of stainless steel samples at about 475 degree C in 70 % of nitrogen admixed with hydrogen at 5 torr shows the maximum increase of hardness 1220 HV which is about four times that of untreated layers. The XRD pattern confirmed the formation of an expanded austenite .N phase, due to the nitrogen incorporation into original lattice and forms supersaturated face center cubic phase. In addition preliminary results for aluminum nitriding is also shown

Advanced oxide powders processing based on cascade plasma

International Nuclear Information System (INIS)

Solonenko, O P; Smirnov, A V

2014-01-01

Analysis of the potential advantages offered to thermal spraying and powder processing by the implementation of plasma torches with inter-electrode insert (IEI) or, in other words, cascade plasma torches (CPTs) is presented. The paper provides evidence that the modular designed single cathode CPT helps eliminate the following major disadvantages of conventional plasma torches: plasma parameters drifting, 1-5 kHz pulsing of plasma flow, as well as excessive erosion of electrodes. More stable plasma results in higher quality, homogeneity and reproducibility of plasma sprayed coatings and powders treated. In addition, CPT offers an extremely wide operating window, which allows better control of plasma parameters, particle dwell time and, consequently, particle temperature and velocity within a wide range by generating high enthalpy quasi-laminar plasmas, medium enthalpy transient plasmas, as well as relatively low enthalpy turbulent plasmas. Stable operation, flexibility with plasma gases as well as wide operating window of CPT should help significantly improve the existing plasma spraying processes and coatings, and also help develop new advanced technologies

Optimization of steam-vortex plasma-torch start-up

Science.gov (United States)

Mikhailov, B. I.

2011-12-01

We propose a new optimal method of steam-vortex plasma-torches start-up; this method completely prevents the danger of water steam condensation in the arc chamber and all undesirable consequences of it.

Characterizing Suspension Plasma Spray Coating Formation Dynamics through Curvature Measurements

Science.gov (United States)

Chidambaram Seshadri, Ramachandran; Dwivedi, Gopal; Viswanathan, Vaishak; Sampath, Sanjay

2016-12-01

Suspension plasma spraying (SPS) enables the production of variety of microstructures with unique mechanical and thermal properties. In SPS, a liquid carrier (ethanol/water) is used to transport the sub-micrometric feedstock into the plasma jet. Considering complex deposition dynamics of SPS technique, there is a need to better understand the relationships among spray conditions, ensuing particle behavior, deposition stress evolution and resultant properties. In this study, submicron yttria-stabilized zirconia particles suspended in ethanol were sprayed using a cascaded arc plasma torch. The stresses generated during the deposition of the layers (termed evolving stress) were monitored via the change in curvature of the substrate measured using an in situ measurement apparatus. Depending on the deposition conditions, coating microstructures ranged from feathery porous to dense/cracked deposits. The evolving stresses and modulus were correlated with the observed microstructures and visualized via process maps. Post-deposition bi-layer curvature measurement via low temperature thermal cycling was carried out to quantify the thermo-elastic response of different coatings. Lastly, preliminary data on furnace cycle durability of different coating microstructures were evaluated. This integrated study involving in situ diagnostics and ex situ characterization along with process maps provides a framework to describe coating formation mechanisms, process parametrics and microstructure description.

The Influence of Process Equipment on the Properties of Suspension Plasma Sprayed Yttria-Stabilized Zirconia Coatings

Science.gov (United States)

Marr, Michael; Waldbillig, David; Kesler, Olivera

2013-03-01

Suspension plasma-sprayed YSZ coatings were deposited at lab-scale and production-type facilities to investigate the effect of process equipment on coating properties. The target application for these coatings is solid oxide fuel cell (SOFC) electrolytes; hence, dense microstructures with low permeability values were preferred. Both facilities had the same torch but different suspension feeding systems, torch robots, and substrate holders. The lab-scale facility had higher torch-substrate relative speeds compared with the production-type facility. On porous stainless steel substrates, permeabilities and microstructures were comparable for coatings from both facilities, and no segmentation cracks were observed. Coating permeability was further reduced by increasing substrate temperatures during deposition or reducing suspension feed rates. On SOFC cathode substrates, coatings made in the production-type facility had higher permeabilities and more segmentation cracks compared with coatings made in the lab-scale facility. Increased cracking in coatings from the production-type facility was likely caused mainly by its lower torch-substrate relative speed.

Chromatic monitoring of dc plasma torches: The latest developments

Czech Academy of Sciences Publication Activity Database

Djakov, B. E.; Enikov, R.; Oliver, D.H.; Hrabovský, Milan; Kopecký, Vladimír

2006-01-01

Roč. 3, č. 2 (2006), s. 170-173 ISSN 1612-8850 R&D Projects: GA ČR(CZ) GA202/05/0669 Institutional research plan: CEZ:AV0Z20430508 Keywords : chromatic monitoring * on-line control * plasma jet * plasma torch * powder Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 2.298, year: 2006

Generator of the low-temperature heterogeneous plasma flow

Science.gov (United States)

Yusupov, D. I.; Gadzhiev, M. Kh; Tyuftyaev, A. S.; Chinnov, V. F.; Sargsyan, M. A.

2018-01-01

A generator of low-temperature dc plasma with an expanding channel of an output electrode for gas-thermal spraying was designed and constructed. The delivery of the sprayed powder into the cathode and anode arc-binding zones or into the plasma jet below the anode binding was realized. The electrophysical characteristics of both the plasma torch and the heterogeneous plasma flow with Al2O3 powder are studied. It is shown that the current-voltage characteristic (CVC) of a plasma torch depends on the gas flow rate. If the flow rate varies from 1 to 3 g/s, the falling CVC becomes gradually increasing. The speed and temperature of the sprayed powder are determined.

Cell treatment and surface functionalization using a miniature atmospheric pressure glow discharge plasma torch

International Nuclear Information System (INIS)

Yonson, S; Coulombe, S; Leveille, V; Leask, R L

2006-01-01

A miniature atmospheric pressure glow discharge plasma torch was used to detach cells from a polystyrene Petri dish. The detached cells were successfully transplanted to a second dish and a proliferation assay showed the transplanted cells continued to grow. Propidium iodide diffused into the cells, suggesting that the cell membrane had been permeabilized, yet the cells remained viable 24 h after treatment. In separate experiments, hydrophobic, bacteriological grade polystyrene Petri dishes were functionalized. The plasma treatment reduced the contact angle from 93 0 to 35 0 , and promoted cell adhesion. Two different torch nozzles, 500 μm and 150 μm in internal diameter, were used in the surface functionalization experiments. The width of the tracks functionalized by the torch, as visualized by cell adhesion, was approximately twice the inside diameter of the nozzle. These results indicate that the miniature plasma torch could be used in biological micropatterning, as it does not use chemicals like the present photolithographic techniques. Due to its small size and manouvrability, the torch also has the ability to pattern complex 3D surfaces

On the atomic state densities of plasmas produced by the "torch a injection axiale"

NARCIS (Netherlands)

Jonkers, J.; Vos, H.P.C.; Mullen, van der J.J.A.M.; Timmermans, E.A.H.

1996-01-01

The atomic state densities of helium and argon plasmas produced by the microwave driven plasma torch called the "torche à injection axiale" are presented. They are obtained by absolute line intensity measurements of the excited states and by applying the ideal gas law to the ground state. It will be

Power supply controlled for plasma torch generation; Fuente de alimentacion controlada para la generacion de un plasma

Energy Technology Data Exchange (ETDEWEB)

Diaz Z, S

1997-12-31

The high density of energy furnished by thermal plasma is profited in a wide range of applications, such as those related with welding fusion, spray coating and at the present in waste destruction. The waste destruction by plasma is a very attractive process because the remaining products are formed by inert glassy grains and non-toxic gases. The main characteristics of thermal plasmas are presented in this work. Techniques based on power electronics are utilized to achieve a good performance in thermal plasma generation. This work shown the design and construction of three phase control system for electric supply of thermal plasma torch, with 250 kw of capacity, as a part of the project named `Destruction of hazard wastes by thermal plasma` actually working in the Instituto Nacional de Investigaciones Nucleares (ININ). The characteristics of thermal plasma and its generation are treated in the first chapter. The A C controllers by thyristors applied in three phase arrays are described in the chapter II, talking into account the power transformer, rectifiers bank and aliasing coil. The chapter III is dedicated in the design of the trigger module which controls the plasma current by varying the trigger angle of the SCR`s; the protection and isolating unit are also presented in this chapter. The results and conclusions are discussed in chapter IV. (Author).

Supersonic Plasma Spray Deposition of CoNiCrAlY Coatings on Ti-6Al-4V Alloy

Science.gov (United States)

Caliari, F. R.; Miranda, F. S.; Reis, D. A. P.; Essiptchouk, A. M.; Filho, G. P.

2017-06-01

Plasma spray is a versatile technology used for production of environmental and thermal barrier coatings, mainly in the aerospace, gas turbine, and automotive industries, with potential application in the renewable energy industry. New plasma spray technologies have been developed recently to produce high-quality coatings as an alternative to the costly low-pressure plasma-spray process. In this work, we studied the properties of as-sprayed CoNiCrAlY coatings deposited on Ti-6Al-4V substrate with smooth surface ( R a = 0.8 μm) by means of a plasma torch operating in supersonic regime at atmospheric pressure. The CoNiCrAlY coatings were evaluated in terms of their surface roughness, microstructure, instrumented indentation, and phase content. Static and dynamic depositions were investigated to examine their effect on coating characteristics. Results show that the substrate surface velocity has a major influence on the coating properties. The sprayed CoNiCrAlY coatings exhibit low roughness ( R a of 5.7 μm), low porosity (0.8%), excellent mechanical properties ( H it = 6.1 GPa, E it = 155 GPa), and elevated interface toughness (2.4 MPa m1/2).

Numerical simulation of a DC double anode arc plasma torch

International Nuclear Information System (INIS)

Chen Lunjiang; Tang Deli; Zhu Hailong

2012-01-01

A 2D axisymmetric numerical simulation of DC double anode plasma torch was done by the computational fluid dynamics (CFD) software FLUENT to improve the efficiency of the waste treatment, which is on the basis of the magnetic fluid dynamics (MHD) theory and uses the method of magnetic vector potential, and the simulation method is based on SIMPLE algorithm. The temperature and speed distributions of the plasma, and so on were obtained. The results show that the temperature of plasma decreases with increasing the axial distance, and increases with increasing the amplitude of the arc current. The velocity first increases and then decreases with the axial distance increase, and increase with the arc current increase. The temperature and the speed at the export of the plasma torch both decrease when the radial distance increases. Those results are in agreement with the experimental results. (authors)

Research on electric and thermal characteristics of plasma torch based on similarity theory

International Nuclear Information System (INIS)

Cheng Changming; Tang Deli; Lan Wei

2007-01-01

Configuration and working principle of a DC non-transferred plasma torch have been introduced. Based on similarity theory, connections between the electric-thermal characteristics and operational parameter such as flowing gas rate and arc power have been investigated. Calculation and experiment are compared. The results indicate that the calculation results are in agreement with experimental ones. The formulas can be used for plasma torch improvement and optimization. (authors)

Enthalpy probe measurements and three-dimensional modelling on air plasma jets generated by a non-transferred plasma torch with hollow electrodes

International Nuclear Information System (INIS)

Kim, Keun Su; Park, Jin Myung; Choi, Sooseok; Kim, Jongin; Hong, Sang Hee

2008-01-01

Thermal flow characteristics of air plasma jets generated by a non-transferred plasma torch with hollow electrodes are experimentally and numerically investigated in order to provide more reliable scientific and technical information, which has been insufficient for their practical applications to material and environmental industries. In this work, a thermal plasma torch of hollow electrode type is first designed and fabricated, and similarity criteria for predicting operational conditions for the scale-up to high-power torches are derived from the arc voltage characteristics measured with various operating and geometry conditions of the torch. The thermal flow characteristics of air plasma jets ejected from the torch are measured by enthalpy probe diagnostics and turn out to have relatively low temperatures of around 3000-7000 K, but show features of other unique properties, such as high energy flux, broad high temperature region and long plasma jet with moderate axial velocity, which are promising for their applications to material syntheses and hazardous waste treatments. Such high enthalpy at a relatively low temperature of air thermal plasma compared with the argon one is due to the high thermal energy residing in the vibrational and rotational states and oxygen dissociation, besides the translational states in monatomic gases such as argon. It is expected that this high specific enthalpy of the air plasma will enable material and environmental industries to treat a large amount of precursors and waste materials effectively at a lower temperature for a longer residence time by the low plasma velocity. It is also found from the measurements that the turbulence intensity influenced by the size of the electrode diameter has a significant effect on the axial and radial profiles of plasma jet properties and that a longer plasma jet is more readily achievable with a larger electrode diameter reducing the turbulence intensity in the external region of the torch. In

Evaporation of Droplets in Plasma Spray-Physical Vapor Deposition Based on Energy Compensation Between Self-Cooling and Plasma Heat Transfer

Science.gov (United States)

Liu, Mei-Jun; Zhang, Meng; Zhang, Qiang; Yang, Guan-Jun; Li, Cheng-Xin; Li, Chang-Jiu

2017-10-01

In the plasma spray-physical vapor deposition process (PS-PVD), there is no obvious heating to the feedstock powders due to the free molecular flow condition of the open plasma jet. However, this is in contrast to recent experiments in which the molten droplets are transformed into vapor atoms in the open plasma jet. In this work, to better understand the heating process of feedstock powders in the open plasma jet of PS-PVD, an evaporation model of molten ZrO2 is established by examining the heat and mass transfer process of molten ZrO2. The results reveal that the heat flux in PS-PVD open plasma jet (about 106 W/m2) is smaller than that in the plasma torch nozzle (about 108 W/m2). However, the flying distance of molten ZrO2 in the open plasma jet is much longer than that in the plasma torch nozzle, so the heating in the open plasma jet cannot be ignored. The results of the evaporation model show that the molten ZrO2 can be partly evaporated by self-cooling, whereas the molten ZrO2 with a diameter <0.28 μm and an initial temperature of 3247 K can be completely evaporated within the axial distance of 450 mm by heat transfer.

Strontium Zirconate TBC Sprayed by a High Feed-Rate Water-Stabilized Plasma Torch.

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Nevrlá, Barbara; Čížek, Jan; Lukáč, František

2017-01-01

Roč. 26, č. 8 (2017), s. 1804-1809 ISSN 1059-9630 R&D Projects: GA TA ČR(CZ) TE02000011 Institutional support: RVO:61389021 Keywords : adhesion * plasma spraying * strontium zirconate * thermal insulator Subject RIV: JK - Corrosion ; Surface Treatment of Materials OBOR OECD: Coating and films Impact factor: 1.488, year: 2016 https://link.springer.com/article/10.1007/s11666-017-0641-7

The microstructural studies of suspension plasma sprayed zirconia coatings with the use of high-energy plasma torches

Czech Academy of Sciences Publication Activity Database

Sokołowski, P.; Nylen, P.; Mušálek, Radek; Łatka, L.; Kozerski, S.; Dietrich, D.; Lampke, T.; Pawłowski, L.

2017-01-01

Roč. 318, May (2017), s. 250-261 ISSN 0257-8972. [International Meeting on Thermal Spraying (RIPT)/7./. Limoges, 09.12.2015-11.12.2015] R&D Projects: GA ČR GA15-12145S Institutional support: RVO:61389021 Keywords : Water-stabilized plasma (WSP) * Gas-stabilized plasma (GSP) * Suspension injection * Columnar microstructure * Two-zones microstructure * Electron backscatter diffraction Subject RIV: JK - Corrosion ; Surface Treatment of Materials OBOR OECD: Coating and films Impact factor: 2.589, year: 2016 http://www.sciencedirect.com/science/article/pii/S0257897217302645

Spectroscopic determination of temperatures in plasmas generated by arc torches

Czech Academy of Sciences Publication Activity Database

Mašláni, Alan; Sember, Viktor; Hrabovský, Milan

2017-01-01

Roč. 133, July (2017), s. 14-20 ISSN 0584-8547 R&D Projects: GA ČR(CZ) GA15-19444S Institutional support: RVO:61389021 Keywords : Arc plasma torch * Optical emission spectroscopy * Temperature * Boltzmann plot Subject RIV: BL - Plasma and Gas Discharge Physics OBOR OECD: Fluids and plasma physics (including surface physics) Impact factor: 3.241, year: 2016

Application of Steenbeck's minimum principle for three-dimensional modelling of DC arc plasma torches

International Nuclear Information System (INIS)

Li Heping; Pfender, E; Chen, Xi

2003-01-01

In this paper, physical/mathematical models for the three-dimensional, quasi-steady modelling of the plasma flow and heat transfer inside a non-transferred DC arc plasma torch are described in detail. The Steenbeck's minimum principle (Finkelnburg W and Maecker H 1956 Electric arcs and thermal plasmas Encyclopedia of Physics vol XXII (Berlin: Springer)) is employed to determine the axial position of the anode arc-root at the anode surface. This principle postulates a minimum arc voltage for a given arc current, working gas flow rate, and torch configuration. The modelling results show that the temperature and flow fields inside the DC non-transferred arc plasma torch show significant three-dimensional features. The predicted anode arc-root attachment position and the arc shape by employing Steenbeck's minimum principle are reasonably consistent with experimental observations. The thermal efficiency and the torch power distribution are also calculated in this paper. The results show that the thermal efficiency of the torch always ranges from 30% to 45%, i.e. more than half of the total power input is taken away by the cathode and anode cooling water. The special heat transfer mechanisms at the plasma-anode interface, such as electron condensation, electron enthalpy and radiative heat transfer from the bulk plasma to the anode inner surface, are taken into account in this paper. The calculated results show that besides convective heat transfer, the contributions of electron condensation, electron enthalpy and radiation to the anode heat transfer are also important (∼30% for parameter range of interest in this paper). Additional effects, such as the non-local thermodynamic equilibrium plasma state near the electrodes, the transient phenomena, etc, need to be considered in future physical/mathematical models, including corresponding measurements

Fast tomographic measurements of temperature in an air plasma cutting torch

Czech Academy of Sciences Publication Activity Database

Hlína, Jan; Šonský, Jiří; Gruber, Jan; Cressault, Y.

2016-01-01

Roč. 49, č. 10 (2016), č. článku 105202. ISSN 0022-3727 Institutional support: RVO:61388998 Keywords : air plasma * cutting torch * tomography Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 2.588, year: 2016

Method and Process Development of Advanced Atmospheric Plasma Spraying for Thermal Barrier Coatings

Science.gov (United States)

Mihm, Sebastian; Duda, Thomas; Gruner, Heiko; Thomas, Georg; Dzur, Birger

2012-06-01

Over the last few years, global economic growth has triggered a dramatic increase in the demand for resources, resulting in steady rise in prices for energy and raw materials. In the gas turbine manufacturing sector, process optimizations of cost-intensive production steps involve a heightened potential of savings and form the basis for securing future competitive advantages in the market. In this context, the atmospheric plasma spraying (APS) process for thermal barrier coatings (TBC) has been optimized. A constraint for the optimization of the APS coating process is the use of the existing coating equipment. Furthermore, the current coating quality and characteristics must not change so as to avoid new qualification and testing. Using experience in APS and empirically gained data, the process optimization plan included the variation of e.g. the plasma gas composition and flow-rate, the electrical power, the arrangement and angle of the powder injectors in relation to the plasma jet, the grain size distribution of the spray powder and the plasma torch movement procedures such as spray distance, offset and iteration. In particular, plasma properties (enthalpy, velocity and temperature), powder injection conditions (injection point, injection speed, grain size and distribution) and the coating lamination (coating pattern and spraying distance) are examined. The optimized process and resulting coating were compared to the current situation using several diagnostic methods. The improved process significantly reduces costs and achieves the requirement of comparable coating quality. Furthermore, a contribution was made towards better comprehension of the APS of ceramics and the definition of a better method for future process developments.

Determination of plasma velocity from light fluctuations in a cutting torch

International Nuclear Information System (INIS)

Prevosto, L.; Mancinelli, B.; Kelly, H.

2009-01-01

Measurements of plasma velocities in a 30 A high energy density cutting torch are reported. The velocity diagnostic is based on the analysis of the light fluctuations emitted by the arc which are assumed to propagate with the flow velocity. These light fluctuations originate from plasma temperature and plasma density fluctuations mainly due to hydrodynamic instabilities. Fast photodiodes are employed as the light sensors. The arc core velocity was obtained from spectrally filtered light fluctuations measurements using a band-pass filter to detect light emission fluctuations emitted only from the arc axis. Maximum plasma jet velocities of 5000 m s -1 close to the nozzle exit and about 2000 m s -1 close to the anode were found. The obtained velocity values are in good agreement with those values predicted by a numerical code for a similar torch to that employed in this work.

ELECTRIC PROBE INVESTIGATION OF ARC ANODE REGION IN PLASMA TORCH

Czech Academy of Sciences Publication Activity Database

Chumak, Oleksiy; Hrabovský, Milan; Kavka, Tetyana

2006-01-01

Roč. 10, č. 4 (2006), s. 515-524 ISSN 1093-3611. [High technology plasma processes. Saint-Petersburg, 27.5.2006-4.6.2006] R&D Projects: GA ČR GA202/05/0669 Institutional research plan: CEZ:AV0Z20430508 Keywords : plasma torch * arc * anode attachment * restrike * electric probes Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 0.343, year: 2006

Single-shot Thomson scattering on argon plasmas created by the Microwave Plasma Torch; evidence for a new plasma class

NARCIS (Netherlands)

Mullen, van der J.J.A.M.; Sande, van de M.J.; Vries, de N.; Broks, B.H.P.; Iordanova, E.I.; Gamero, A.; Torres, J.; Sola, A.

2007-01-01

To determine the fine-structure size of plasmas created by a Microwave Plasma Torch (MPT), single-shot Thomson scattering (TS) measurements were performed. The aim was to find a solution for the long-standing discrepancy between experiments and Global Plasma Models (GPMs). Since these GPMs are based

Arc root dynamics in high power plasma torches – Evidence of ...

Indian Academy of Sciences (India)

Two of the major causes of erratic and poor performance of a variety of thermal plasma processes are currently identified as the fluctuations arising out of the arc root movement on the electrodes inside the plasma torch and the fluid dynamic instabilities arising out of entrainment of the air into the plasma jet. This paper ...

An analytical methodology to predict the coating characteristics of plasma-sprayed ceramic powders

International Nuclear Information System (INIS)

Varacalle, D.J. Jr.

1990-01-01

Experimental and analytical studies have been conducted at the Idaho National Engineering Laboratory (INEL) to investigate gas, particle, and coating dynamics in the plasma spray process. Nine experiments were conducted using a Taguchi statistical parametric approach. The thermal plasma produced by the commercial plasma spray torch and the related plasma/particle interaction were then numerically modeled from the cathode tip to varied standoff distances in the free plume for the nine experiments, which ranged in power from 28 to 43 kW. The flow and temperature fields in the plasma were solved using the governing conservation equations with suitable boundary conditions. This information was then used as boundary conditions to solve the plasma/particle interaction problem for the nine experiments. The particle dynamics (10- to 75-μm particles) for a yttria-stabilized zirconia powder were then simulated by computer. Particle morphology is discussed with respect to the changes in the process parameters. The predicted temperature and velocity of the zirconia particles were then used as initial conditions to a coating dynamics code. The code predicts the thickness and porosity of the zirconia coatings for the specific process parameters. The predicted coating characteristics exhibit reasonable correlation with the actual characteristics obtained from the Taguchi experimental studies. 12 refs., 7 figs., 6 tabs

Characterization of Ni-YSZ anodes for solid oxide fuel cells fabricated by solution precursor plasma spraying with axial feedstock injection

Science.gov (United States)

Metcalfe, Craig; Lay-Grindler, Elisa; Kesler, Olivera

2014-02-01

Nickel and yttria-stabilized zirconia (YSZ) anodes were fabricated by solution precursor plasma spraying (SPPS) and incorporated into metal-supported solid oxide fuel cells (SOFC). A power density of 0.45 W cm-2 at 0.7 V and a peak power density of 0.52 W cm-2 at 750 °C in humidified H2 was obtained, which are the first performance results reported for an SOFC having an anode fabricated by SPPS. The effects of solution composition, plasma gas composition, and stand-off distance on the composition of the deposited Ni-YSZ coatings by SPPS were evaluated. It was found that the addition of citric acid to the aqueous solution delayed re-solidification of NiO particles, improving the deposition efficiency and coating adhesion. The composition of the deposited coatings was found to vary with torch power. Increasing torch power led to coatings with decreasing Ni content, as a result of Ni vaporizing in-flight at stand-off distances less than 60 mm from the torch nozzle exit.

Oxygen Plasma Treatment of Rubber Surface by the Atmospheric Pressure Cold Plasma Torch

DEFF Research Database (Denmark)

Lee, Bong-ju; Kusano, Yukihiro; Kato, Nobuko

1997-01-01

adhesive. The adhesion property was improved by treatment of the rubber compound with plasma containing oxygen radicals. Physical and chemical changes of the rubber surface as a result of the plasma treatment were analyzed by field emission scanning electron microscopy (FE-SEM) and fourier transform......A new application of the atmospheric cold plasma torch has been investigated. Namely, the surface treatment of an air-exposed vulcanized rubber compound. The effect of plasma treatment was evaluated by the bondability of the treated rubber compound with another rubber compound using a polyurethane...

The Efficiency of Quartz Particles Evaporation in the Argon Plasma Flow of the RF Inductively Coupled Plasma Torch

Directory of Open Access Journals (Sweden)

Yu. M. Grishin

2017-01-01

Full Text Available Owing to high-power density and high-purity plasma, a RF inductively coupled plasma torch (ICPT is widely used both in research laboratory and in industry. The potential RF ICPT application areas are powders spheroidisation, waste treatment, thermal spraying, etc.In the last decade the investigation was focused on the treatment processes of quartz into polycrystalline silicon. An analysis of these results has shown that the increasing productivity and producing high-purity silicon can be achieved only when using the electrodeless radio-frequency induction plasma torches and in case the optimum conditions for evaporation of SiO2solid particles are realized.Optimization of the RF ICPT design and power parameters calls for a wide range of computational studies. In spite of the fact that to date a large number of efforts to calculate the evaporation efficiency of powder materials have been made, a number of issues, as applied to the problem of obtaining silicon, require further research.In this paper, we present the results of a two-dimensional numerical simulation of the heating and evaporation of quartz particles in the RF ICPT channel with axial flow of gases. The main aim is to determine how the axial position of the central tube (through which the particles are injected into the discharge zone, the dispersion of the quartz powder, the amplitude of the discharge current (and, respectively, flow regimes impact on the evaporation efficiency of quartz particles.The paper presented the numerical modeling results of heating and evaporation processes of quartz particles supplied by transporting gas to the RF ICPT channel with axial gas flow (argon. Defined the impact of the axial position of the central tube, the plasma flow regime, the discharge current, the flow rate of transporting gas, and other parameters on the evaporation efficiency of quartz particles.It is shown that the evaporation efficiency of particles reaches its maximum when their

Schlieren Technique Applied to Magnetohydrodynamic Generator Plasma Torch

Science.gov (United States)

Chopra, Nirbhav; Pearcy, Jacob; Jaworski, Michael

2017-10-01

Magnetohydrodynamic (MHD) generators are a promising augmentation to current hydrocarbon based combustion schemes for creating electrical power. In recent years, interest in MHD generators has been revitalized due to advances in a number of technologies such as superconducting magnets, solid-state power electronics and materials science as well as changing economics associated with carbon capture, utilization, and sequestration. We use a multi-wavelength schlieren imaging system to evaluate electron density independently of gas density in a plasma torch under conditions relevant to MHD generators. The sensitivity and resolution of the optical system are evaluated alongside the development of an automated analysis and calibration program in Python. Preliminary analysis shows spatial resolutions less than 1mm and measures an electron density of ne = 1 ×1016 cm-3 in an atmospheric microwave torch. Work supported by DOE contract DE-AC02-09CH11466.

Contribution of a portable air plasma torch to rapid blood coagulation as a method of preventing bleeding

International Nuclear Information System (INIS)

Kuo, S P; Chen, C Y; Fan, H W; Tarasenko, O; Scott, A; Lahiani, M; Alusta, P; Chang, J; Popovic, S; Drake, J D; Nikolic, M

2009-01-01

The effectiveness and mechanism of a low temperature air plasma torch in clotting blood are explored. Both blood droplets and smeared blood samples were used in the tests. The treated droplet samples reveal how blood clotting depends on the distance at which the torch operated, and for how long the droplets have been exposed to the torch. Microscopy and cell count of smeared blood samples shed light on dependencies of erythrocyte and platelet counts on torch distance and exposure time. With an increase of torch distance, the platelet count of treated blood samples increases but is less than that of the control. The flux of reactive atomic oxygen (RAO) and the degree of blood clotting decreased. With an increase of exposure time, platelet count of treated samples decreased, while the degree of clot increased. The correlation among these dependencies and published data support a blood clotting mechanism that RAO as well as other likely reactive oxygen species generated by the plasma torch activate erythrocyte-platelets interactions and induces blood coagulation.

Determination of trace amounts of boron in steel by high frequency plasma torch spectrometry

International Nuclear Information System (INIS)

Akiyoshi, Takanori; Tsukamoto, Takako

1978-01-01

Trace amount of boron in steel were determined by means of emission spectrometry using high frequency plasma torch. The sensitivity of this method depended on the kind of solvent used, and methyl alcohol gave the best sensitivity. The determination limit of boron in methanol was 0.002 μg/ml. The established method utilized the high sensibility of the plasma torch and the easy distillation of boron in methanol as trimethyl-borate (B(OCH 3 ) 3 ). The sample was dissolved by acids and dehydrated by hot H 2 SO 4 and H 3 Po 4 . After cooling and addition of methanol (60 ml), the solution was distilled to obtain 40 ml of the distillate. The amount of boron in the distillate was determined by the intensity of the spectral line of B 2497.73 A excited by plasma torch. This method was rapid and accurate, particularly in determining trace amounts of boron and the determination range of boron in steel was 0.2 to 150 ppm. This method was also appliciable to stainless steels and other alloys. (auth.)

Melting experiment on concrete waste using a hollow type plasma torch mounted on furnace

International Nuclear Information System (INIS)

Moon, Y. P.; Kim, T. W.; Kim, H. S.; Shin, S. U.; Lee, M. C.

2000-01-01

A furnace coupled with a hollow type plasma torch was manufactured and installed in order to develop a volume reduction technology for non-combustible radioactive waste using plasma. A melting test with 10kg of concrete waste was carried out for the evaluation of melting characteristics in the non-transferred operation mode for 20 minutes with the melter. Feeded concrete was completely melted. However, the molten bath was not easily discharged because of its high viscosity. It was found that some molten slag spat from the molten bath was coated on the surface of torch which was mounted vertically inside furnace

Characterisation of plasmas produced by the "torche à injection axiale"

NARCIS (Netherlands)

Jonkers, J.; Selen, L.J.M.; Mullen, van der J.J.A.M.; Timmermans, E.A.H.; Schram, D.C.; Fauchais, P.

1997-01-01

Two different kinds of plasmas created by the microwave driven Torche a' Injection Axiale (TIA) are investigated: one with helium and the other with argon as the main gas. By using abs. line intensity measurements, the densities of the excited states are detd. Applying the ideal gas law gives the

Dynamic behaviour of dc double anode plasma torch at atmospheric pressure

International Nuclear Information System (INIS)

Tu, X; Cheron, B G; Yan, J H; Cen, K F

2007-01-01

An original dc double anode plasma torch which provides a long-time and highly stable atmospheric plasma jet has been devised for the purpose of hazardous waste treatment. The arc fluctuations and dynamic behaviour of the argon and argon-nitrogen plasma jets under different operating conditions have been investigated by means of classical tools, such as the statistic method, fast Fourier transform (FFT) and correlation analysis. In our experiments, the takeover mode is identified as the fluctuation characteristic of the argon plasma jet while the restrike mode is typical in the argon-nitrogen plasma dynamic behaviour. In the case of pure argon, the FFT and correlation calculation results of electrical signals exhibit the only characteristic frequency of 150 Hz, which originates from the torch power and is independent of any change in the operating conditions. It indicates that the nature of fluctuations in an argon plasma jet is mainly induced by the undulation of the tri-phase rectified power supply. In contrast, besides the same low frequency bulk fluctuation, the dynamic behaviour of the argon-nitrogen plasma jet at high frequency (4.1 kHz) is ascribed to the rapid motion of both arc roots on the anode surface. In addition, it is found that each arc root attachment is rather diffused than located at a fixed position on the anode wall in the argon plasma jet, while constricted arc roots occur when nitrogen is added into argon as the plasma working gas

Wastes vitrification by plasma torch: study of a glass formulation compatible with a wide range of B wastes; Vitrification des dechets par torche a plasma: recherche d'une formulation de verre compatible avec un large eventail de dechets B

Energy Technology Data Exchange (ETDEWEB)

Poitou, S.; Richaud, D.; Fiquet, O.; Gramondi, P.; Massit, H. [CEA Cadarache, Dept. d' Entreposage et de Stockage des Dechets, 13 - Saint-Paul-lez-Durance (France)

2001-07-01

Within the context of radioactive waste management, CEA has equipped itself with a 'PLASMARC' device. The central element of this device is a plasma torch treatment furnace. It has been implemented and validated for the vitrification of low level radioactive wastes. Meanwhile, the plasma torch presents potentially interests for immobilizing under an inert form in vitreous matrices, B wastes which are generally divided and of complex chemical composition. The application of this process to this type of wastes has been studied here. The obtained results show that with the plasma torch it is possible to make glasses with a high amount of silicon and aluminium oxide and which are adapted to the treatment / packaging of the B wastes. (O.M.)

High quality ceramic coatings sprayed by high efficiency hypersonic plasma spraying gun

International Nuclear Information System (INIS)

Zhu Sheng; Xu Binshi; Yao JiuKun

2005-01-01

This paper introduced the structure of the high efficiency hypersonic plasma spraying gun and the effects of hypersonic plasma jet on the sprayed particles. The optimised spraying process parameters for several ceramic powders such as Al 2 O 3 , Cr 2 O 3 , ZrO 2 , Cr 3 C 2 and Co-WC were listed. The properties and microstructure of the sprayed ceramic coatings were investigated. Nano Al 2 O 3 -TiO 2 ceramic coating sprayed by using the high efficiency hypersonic plasma spraying was also studied. Compared with the conventional air plasma spraying, high efficiency hypersonic plasma spraying improves greatly the ceramic coatings quality but at low cost. (orig.)

Wastes vitrification by plasma torch: study of a glass formulation compatible with a wide range of B wastes

International Nuclear Information System (INIS)

Poitou, S.; Richaud, D.; Fiquet, O.; Gramondi, P.; Massit, H.

2001-01-01

Within the context of radioactive waste management, CEA has equipped itself with a 'PLASMARC' device. The central element of this device is a plasma torch treatment furnace. It has been implemented and validated for the vitrification of low level radioactive wastes. Meanwhile, the plasma torch presents potentially interests for immobilizing under an inert form in vitreous matrices, B wastes which are generally divided and of complex chemical composition. The application of this process to this type of wastes has been studied here. The obtained results show that with the plasma torch it is possible to make glasses with a high amount of silicon and aluminium oxide and which are adapted to the treatment / packaging of the B wastes. (O.M.)

Flexible small size radiofrequency plasma torch for Tokamak wall cleaning

International Nuclear Information System (INIS)

Eusebiu-Rosini Ionita; Luciu, I.; Dinescu, G.; Grisolia, Ch.

2006-01-01

Tritium accumulation in walls is a limiting factor in efficient long term operation of fusion machines. A number of detritiation techniques are under study, like laser, discharge, flash lamp based cleaning. One of the encountered difficulties is the limited access of the detritiation tool in narrow spaces, as in divertor region, inter-tiles or inside castellated gaps, where in fact an enhanced co-deposition and tritium trapping were observed. This contribution addresses the problem of elaboration of plasma torch as a tool appropriate for stimulating detritiation and removal of co-deposited layers in such spaces. The requirements imposed to the plasma torch source were related to the compatibility with inside torus operation: small diameter in order to permit access in narrow spaces, reasonable power, large range of working pressures from vacuum to atmosphere, closed loop cooling, flexibility in order to allow scanning and mounting on a robotic arm. The approached design is based on a radiofrequency discharge constricted to burn in a closed space between an active radiofrequency electrode and a grounded nozzle, from where plasma expands outside as a directional beam. The found solutions have led to a flexible hand held source working stable up to 300 W injected power and consisting of a cylindrical body of 20 mm diameter including the external water jacket embracing the discharge and an inside cooling circuit. The electrical characterization of the radiofrequency discharge sustaining the expanded plasma was performed and the domain of stable source operation in terms of power, current, pressure, argon mass flow rate is presented and discussed. The plasma beam size presents a strong dependence on pressure: the plasma length decreases from 200 mm to 20 mm, when pressure increases from vacuum to atmospheric, depending on power and mass flow rate. The ionized gas temperature, as indicated by a thermocouple head inserted in expansion in the nozzle proximity fall in the

Fabrication of High-Temperature Heat Exchangers by Plasma Spraying Exterior Skins on Nickel Foams

Science.gov (United States)

Hafeez, P.; Yugeswaran, S.; Chandra, S.; Mostaghimi, J.; Coyle, T. W.

2016-06-01

Thermal-sprayed heat exchangers were tested at high temperatures (750 °C), and their performances were compared to the foam heat exchangers made by brazing Inconel sheets to their surface. Nickel foil was brazed to the exterior surface of 10-mm-thick layers of 10 and 40 PPI nickel foam. A plasma torch was used to spray an Inconel coating on the surface of the foil. A burner test rig was built to produce hot combustion gases that flowed over exposed face of the heat exchanger. Cooling air flowed through the foam heat exchanger at rates of up to 200 SLPM. Surface temperature and air inlet/exit temperature were measured. Heat transfer to air flowing through the foam was significantly higher for the thermally sprayed heat exchangers than for the brazed heat exchangers. On an average, thermally sprayed heat exchangers show 36% higher heat transfer than conventionally brazed foam heat exchangers. At low flow rates, the convective resistance is large (~4 × 10-2 m2 K/W), and the effect of thermal contact resistance is negligible. At higher flow rates, the convective resistance decreases (~2 × 10-3 m2 K/W), and the lower contact resistance of the thermally sprayed heat exchanger provides better performance than the brazed heat exchangers.

Platelet-cooled plasma arc torch. Final report

International Nuclear Information System (INIS)

1995-10-01

In this 12-month program sponsored by the DOE Morgantown Energy Technology Center, Aerojet designed, fabricated, and tested six platelet cooled electrodes for a Retech 75T (90 MW) plasma arc torch capable of processing mixed radioactive waste. Two of the electrodes with gas injection through the electrode wall demonstrated between eight and forty times the life of conventional water cooled electrodes. If a similar life increase can be produced in a 1 Mw size electrode, then electrodes possessing thousands, rather than hundreds, of hours of life will be available to DOE for potential application to mixed radioactive waste processing

Direct solution introduction using conventional nebulizers with a short torch for plasma mass spectrometry

International Nuclear Information System (INIS)

Westphal, Craig S.; Montaser, Akbar

2006-01-01

A new torch, a shortened version of a standard demountable torch, is proposed for facilitating direct injection of liquid samples into an inductively coupled plasma mass spectrometer using conventional and micro-pneumatic nebulizers. The proposed arrangement reduces the cost of the direct injector nebulizer by a factor of 5, typically from $2000 to $400, although a different torch is required. The analytical performance of the high efficiency nebulizer-short torch arrangement is compared to that obtained with the direct injection high efficiency nebulizer interfaced to the conventional torch. Optimum operating conditions for the high efficiency nebulizer-short torch arrangement are generally similar to those of the direct injection high efficiency nebulizer: high RF power (1500 W), low nebulizer gas flow rates (0.09 L/min) and low solution uptake rates (5-85 μL/min). Sensitivity with the high efficiency nebulizer-short torch system at 85 μL/min is improved by a factor of 2.4 on average compared to the direct injection high efficiency nebulizer, while precision values (%RSD) and detection limits are generally comparable or slightly degraded (on average by a factor of 1.7), respectively. Sensitivity is also better at lower solution uptake rates (5 μL/min) by factors ranging from 2 ( 82 Se) to 7 ( 59 Co) compared to the direct injection high efficiency nebulizer. Additionally, the %RSD values are better at 5 μL/min, ranging from 3.5% to 6.0% for the high efficiency nebulizer-short torch combination compared to 4.7 to 9.1% for the direct injection high efficiency nebulizer. The utility of the high efficiency nebulizer-short torch arrangement is demonstrated through the microscale flow injection analysis of Cr-DNA adducts and the analysis of four certified reference materials (Lyphochek urine metals control, SRM 1515: Apple Leaves, SRM 1570a: Spinach Leaves, SRM 1577b: Bovine Liver). Peak to peak precision values (N = 3) for the microscale flow injection analysis

Enhancement of the life of refractories through the operational experience of plasma torch melter

Energy Technology Data Exchange (ETDEWEB)

Moon, Young Pyo [Technology Institute, Korea Radioactive waste Agency (KORAD), Daejeon (Korea, Republic of); Choi, Jaang Young [Chungnam National University, Daejeon (Korea, Republic of)

2016-06-15

The properties of wastes for melting need to be considered to minimize the maintenance of refractory and to discharge the molten slags smoothly from a plasma torch melter. When the nonflammable wastes from nuclear facilities such as concrete debris, glass, sand, etc., are melted, they become acid slags with low basicity since the chemical composition has much more acid oxides than basic oxides. A molten slag does not have good characteristics of discharge and is mainly responsible for the refractory erosion due to its low liquidity. In case of a stationary plasma torch melter with a slant tapping port on the wall, a fixed amount of molten slags remains inside of tapping hole as well as the melter inside after tapping out. Nonmetallic slags keep the temperature higher than melting point of metal because metallic slags located on the bottom of melter by specific gravity difference are simultaneously melted when dual mode plasma torch operates in transferred mode. In order to minimize the refractory erosion, the compatible refractories are selected considering the temperature inside the melter and the melting behavior of slags whether to contact or noncontact with molten slags. An acidic refractory shall not be installed in adjacent to a basic refractory for the resistibility against corrosion.

Non-combustible waste vitrification with plasma torch melter.

Science.gov (United States)

Park, J K; Moon, Y P; Park, B C; Song, M J; Ko, K S; Cho, J M

2001-05-01

Non-combustible radioactive wastes generated from Nuclear Power Plants (NPPs) are composed of concrete, glass, asbestos, metal, sand, soil, spent filters, etc. The melting tests for concrete, glass, sand, and spent filters were carried out using a 60 kW plasma torch system. The surrogate wastes were prepared for the tests. Non-radioactive Co and Cs were added to the surrogates in order to simulate the radioactive waste. Several kinds of surrogate prepared by their own mixture or by single waste were melted with the plasma torch system to produce glassy waste forms. The characteristics of glassy waste forms were examined for the volume reduction factor (VRF) and the leach rate. The VRFs were estimated through the density measurement of the surrogates and the glassy waste forms, and were turned out to be 1.2-2.4. The EPA (Environmental Protection Agency) Toxicity Characteristic Leaching Procedure (TCLP) was used to determine the leach resistance for As, Ba, Hg, Pb, Cd, Cr, Se, Co, and Cs. The leaching index was calculated using the total content of each element in both the waste forms and the leachant. The TCLP tests resulted in that the leach rates for all elements except Co and Cs were lower than those of the Universal Treatment Standard (UTS) limits. There were no UTS limits for Co and Cs, and their leach rate & index from the experiments were resulted in around 10 times higher than those of other elements.

Diagnostics of an rf induction plasma torch with the aid of a magnetic probe

International Nuclear Information System (INIS)

Shamim, A.; Wooding, E.R.

1978-01-01

Estimates of a plasma temperature, electrical conductivity, and torch efficiency have been made from simple measurements made on the plasma and on the rf supply. Measurements were made with the aid of a simple magnetic probe and a pickup coil. Estimates are also made of the heating-coil constants

Production of nitric oxide using a microwave plasma torch and its application to fungal cell differentiation

International Nuclear Information System (INIS)

Na, Young Ho; Kang, Min-Ho; Cho, Guang Sup; Choi, Eun Ha; Park, Gyungsoon; Uhm, Han Sup; Kumar, Naresh

2015-01-01

The generation of nitric oxide by a microwave plasma torch is proposed for its application to cell differentiation. A microwave plasma torch was developed based on basic kinetic theory. The analytical theory indicates that nitric oxide density is nearly proportional to oxygen molecular density and that the high-temperature flame is an effective means of generating nitric oxide. Experimental data pertaining to nitric oxide production are presented in terms of the oxygen input in units of cubic centimeters per minute. The apparent length of the torch flame increases as the oxygen input increases. The various levels of nitric oxide are observed depending on the flow rate of nitrogen gas, the mole fraction of oxygen gas, and the microwave power. In order to evaluate the potential of nitric oxide as an activator of cell differentiation, we applied nitric oxide generated from the microwave plasma torch to a model microbial cell (Neurospora crassa: non-pathogenic fungus). Germination and hyphal differentiation of fungal cells were not dramatically changed but there was a significant increase in spore formation after treatment with nitric oxide. In addition, the expression level of a sporulation related gene acon-3 was significantly elevated after 24 h upon nitric oxide treatment. Increase in the level of nitric oxide, nitrite and nitrate in water after nitric oxide treatment seems to be responsible for activation of fungal sporulation. Our results suggest that nitric oxide generated by plasma can be used as a possible activator of cell differentiation and development. (paper)

Removal of volatile organic compounds by a high pressure microwave plasma torch

International Nuclear Information System (INIS)

Rubio, S.J.; Quintero, M.C.; Rodero, A.; Alvarez, R.

2004-01-01

A helium microwave plasma torch was studied and optimised as a destruction system of volatile organic compounds. Attention was focused on trichloroethylene as a prototypical volatile organic compound, which is used technologically and which poses known health risks. The dependence of the destruction efficiency on the plasma conditions was obtained for different values of trichloroethylene concentrations. The results show a destruction and removal efficiency greater than 99.999% (Authors)

Permeability and Microstructure of Suspension Plasma-Sprayed YSZ Electrolytes for SOFCs on Various Substrates

Science.gov (United States)

Marr, Michael; Kesler, Olivera

2012-12-01

Yttria-stabilized zirconia electrolyte coatings for solid oxide fuel cells were deposited by suspension plasma spraying using a range of spray conditions and a variety of substrates, including finely structured porous stainless steel disks and cathode layers on stainless steel supports. Electrolyte permeability values and trends were found to be highly dependent on which substrate was used. The most gas-tight electrolyte coatings were those deposited directly on the porous metal disks. With this substrate, permeability was reduced by increasing the torch power and reducing the stand-off distance to produce dense coating microstructures. On the substrates with cathodes, electrolyte permeability was reduced by increasing the stand-off distance, which reduced the formation of segmentation cracks and regions of aligned and concentrated porosity. The formation mechanisms of the various permeability-related coating features are discussed and strategies for reducing permeability are presented. The dependences of electrolyte deposition efficiency and surface roughness on process conditions and substrate properties are also presented.

The influence of nitrogen entrainment on argon plasmas created by the 'Torche à Injection Axiale' (TIA)

NARCIS (Netherlands)

Jonkers, J.; Hartgers, A.; Selen, L.J.M.; Mullen, van der J.J.A.M.; Schram, D.C.

1999-01-01

When a plasma is sustained in the open air, nitrogen will diffuse into the plasma. Especially for plasmas sustained by the `Torche à Injection Axiale' (TIA) this appears to be the case, since this turbulent jet draws gases from the surroundings. In the argon plasma the entrained nitrogen is probably

Influence of non-equilibrium effects on plasma property functions in hybrid water-argon plasma torch

Czech Academy of Sciences Publication Activity Database

Křenek, Petr; Hrabovský, Milan

2010-01-01

Roč. 14, 1-2 (2010), s. 95-100 ISSN 1093-3611. [European High Temperature Plasma Processes (HTPP)/10th./. Patras (Patras University), 07.07.2008-11.07.2008] R&D Projects: GA ČR GA202/08/1084 Institutional research plan: CEZ:AV0Z20430508 Keywords : Thermal plasma * material properties * non-equlibrium phenomena * dc arc torch Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 0.189, year: 2010 http://www.begellhouse.com/journals/57d172397126f956,227c67f42b79464a,5bbc4c7760b4b6cb.html

Study of Multi-Function Micro-Plasma Spraying Technology

International Nuclear Information System (INIS)

Wang Liuying; Wang Hangong; Hua Shaochun; Cao Xiaoping

2007-01-01

A multi-functional micro-arc plasma spraying system was developed according to aerodynamics and plasma spray theory. The soft switch IGBT (Insulated Gate Bipolar Transistor) invert technique, micro-computer control technique, convergent-divergent nozzle structure and axial powder feeding techniques have been adopted in the design of the micro-arc plasma spraying system. It is not only characterized by a small volume, a light weight, highly accurate control, high deposition efficiency and high reliability, but also has multi-functions in plasma spraying, welding and quenching. The experimental results showed that the system can produce a supersonic flame at a low power, spray Al 2 O 3 particles at an average speed up to 430 m/s, and make nanostructured AT13 coatings with an average bonding strength of 42.7 MPa. Compared to conventional 9M plasma spraying with a higher power, the coatings with almost the same properties as those by conventional plasma spray can be deposited by multi-functional micro-arc plasma spraying with a lower power plasma arc due to an improved power supply design, spray gun structure and powder feeding method. Moreover, this system is suitable for working with thin parts and undertaking on site repairs, and as a result, the application of plasma spraying will be greatly extended

Departure from Local Thermodynamic Equilibrium in argon plasmas sustained in a Torche à Injection Axiale sur Guide d'Ondes

International Nuclear Information System (INIS)

Rincón, R.; Muñoz, J.; Calzada, M.D.

2015-01-01

Plasma torches are suitable plasma sources for a wide range of applications. The capability of these discharges to produce processes like sample excitation or decomposition of molecules inside them depends on the density of the plasma species and their energies (temperatures). The relation between these parameters determines the specific state of thermodynamic equilibrium in the discharge. Thus, the understanding of plasma possibilities for application purposes is related to the knowledge of the plasma thermodynamic equilibrium degree. In this paper a discussion about the equilibrium state for Ar plasmas generated by using a Torche à Injection Axiale sur Guide d'Ondes, TIAGO device, is presented. Emission spectroscopy techniques were used to measure gas temperature and electron density at the exit of the nozzle torch and along the dart. Boltzmann-plots as well as b p parameters were calculated to characterize the type and degree of departure from partial Local Saha Equilibrium (pLSE). This study indicates that the closer situation to Local Thermodynamic Equilibrium (LTE) of the plasma corresponds to larger Ar flows which highlights the importance of the nitrogen (atmosphere surrounding the plasma) in the kinetics of Ar-TIAGO discharges. - Highlights: • Discharges sustained in Ar using a TIAGO Torch show a significant departure from Local Thermodynamic Equilibrium. • Nitrogen entrance from surrounding air highly influences Thermodynamic Equilibrium. • Departure from LTE has been studied by means of Boltzmann plots and b p parameters. • The discharge is ionizing at the nozzle exit plasma, while along the dart it becomes recombining

Low-pressure water-cooled inductively coupled plasma torch

Science.gov (United States)

Seliskar, Carl J.; Warner, David K.

1988-12-27

An inductively coupled plasma torch is provided which comprises an inner tube, including a sample injection port to which the sample to be tested is supplied and comprising an enlarged central portion in which the plasma flame is confined; an outer tube surrounding the inner tube and containing water therein for cooling the inner tube, the outer tube including a water inlet port to which water is supplied and a water outlet port spaced from the water inlet port and from which water is removed after flowing through the outer tube; and an r.f. induction coil for inducing the plasma in the gas passing into the tube through the sample injection port. The sample injection port comprises a capillary tube including a reduced diameter orifice, projecting into the lower end of the inner tube. The water inlet is located at the lower end of the outer tube and the r.f. heating coil is disposed around the outer tube above and adjacent to the water inlet.

Aerosol measurements from plasma torch cuts on stainless steel, carbon steel, and aluminum

International Nuclear Information System (INIS)

Novick, V.J.; Brodrick, C.J.; Crawford, S.; Nasiatka, J.; Pierucci, K.; Reyes, V.; Sambrook, J.; Wrobel, S.; Yeary, J.

1996-01-01

The main purpose of this project is to quantify aerosol particle size and generation rates produced by a plasma torch whencutting stainless steel, carbon steel and aluminum. the plasma torch is a common cutting tool used in the dismantling of nuclear facilities. Eventually, other cutting tools will be characterized and the information will be compiled in a user guide to aid in theplanning of both D ampersand D and other cutting operations. The data will be taken from controlled laboratory experiments on uncontaminated metals and field samples taken during D ampersand D operations at ANL nuclear facilities. The plasma torch data was collected from laboratory cutting tests conducted inside of a closed, filtered chamber. The particle size distributions were determined by isokinetically sampling the exhaust duct using a cascade impactor. Cuts on different thicknesses showed there was no observable dependence of the aerosol quantity produced as a function of material thickness for carbon steel. However, data for both stainless steel and aluminum revealed that the aerosol mass produced for these materials appear to have some dependance on thickness, with thinner materials producing tmore aerosols. The results of the laboratory cutting tests show that most measured particle size distributions are bimodal with one mode at about 0.2 μm and the other at about 10 μm. The average Mass Median Aerodynamic Diameters (MMAD's) for these tests are 0.36 ±0.08 μm for stainless steel, 0.48 ±0.17μm for aluminum and 0.52±0.12 μm for carbon steel

Optimizing Thermoelectric Properties of In Situ Plasma-Spray-Synthesized Sub-stoichiometric TiO2-x Deposits

Science.gov (United States)

Lee, Hwasoo; Seshadri, Ramachandran Chidambaram; Pala, Zdenek; Sampath, Sanjay

2018-06-01

In this article, an attempt has been made to relate the thermoelectric properties of thermal spray deposits of sub-stoichiometric titania to process-induced phase and microstructural variances. The TiO2-x deposits were formed through the in situ reaction of the TiO1.9 or TiO1.7 feedstock within the high-temperature plasma flame and manipulated via varying the amounts of hydrogen fed into in the thermal plasma. Changes in the flow rates of H2 in the plasma plume greatly affected the in-flight particle behavior and composition of the deposits. For reference, a high-velocity oxy-fuel spray torch was also used to deposit the two varieties of feedstocks. Refinements to the representation of the in-flight particle characteristics derived via single particle and ensemble diagnostic methods are proposed using the group parameters (melting index and kinetic energy). The results show that depending on the value of the melting index, there is an inverse proportional relationship between electrical conductivity and Seebeck coefficient, whereas thermal conductivity has a directly proportional relationship with the electrical conductivity. Retention of the original phase and reduced decomposition is beneficial to retain the high Seebeck coefficient or the high electrical conductivity in the TiO2 system.

Radio-frequency plasma spraying of ceramics

International Nuclear Information System (INIS)

Okada, T.; Hamatani, H.; Yoshida, T.

1989-01-01

This study was aimed at developing a novel spraying process using a radio-frequency (rf) plasma. Experiments of Al 2 O 3 and ZrO 2 - 8 wt% Y 2 O 3 spraying showed that the initial powder size was the most important parameter for depositing dense coatings. The optimum powder sizes of Al 2 O 3 and ZrO 2 - 8 wt% Y 2 O 3 were considered to be around 100 and 80 μm, respectively. The use of such large-size powders compared with those used by conventional dc plasma spraying made it possible to deposit adherent ceramics coatings of 150 to 300 μm on as-rolled SS304 substrates. It was also shown that low particle velocity of about 10 m/s, which is peculiar to rf plasma spraying, was sufficient for particle deformation, though it imposed a severe limitation on the substrate position. These experimental results prove that rf plasma spraying is an effective process and a strong candidate to open new fields of spraying applications

Effects of Atomization Injection on Nanoparticle Processing in Suspension Plasma Spray

Directory of Open Access Journals (Sweden)

Hong-bing Xiong

2016-05-01

Full Text Available Liquid atomization is applied in nanostructure dense coating technology to inject suspended nano-size powder materials into a suspension plasma spray (SPS torch. This paper presents the effects of the atomization parameters on the nanoparticle processing. A numerical model was developed to simulate the dynamic behaviors of the suspension droplets, the solid nanoparticles or agglomerates, as well as the interactions between them and the plasma gas. The plasma gas was calculated as compressible, multi-component, turbulent jet flow in Eulerian scheme. The droplets and the solid particles were calculated as discrete Lagrangian entities, being tracked through the spray process. The motion and thermal histories of the particles were given in this paper and their release and melting status were observed. The key parameters of atomization, including droplet size, injection angle and velocity were also analyzed. The study revealed that the nanoparticle processing in SPS preferred small droplets with better atomization and less aggregation from suspension preparation. The injection angle and velocity influenced the nanoparticle release percentage. Small angle and low initial velocity might have more nanoparticles released. Besides, the melting percentage of nanoparticles and agglomerates were studied, and the critical droplet diameter to ensure solid melting was drawn. Results showed that most released nanoparticles were well melted, but the agglomerates might be totally melted, partially melted, or even not melted at all, mainly depending on the agglomerate size. For better coating quality, the suspension droplet size should be limited to a critical droplet diameter, which was inversely proportional to the cubic root of weight content, for given critical agglomerate diameter of being totally melted.

Characterization of a segmented plasma torch assisted High Heat Flux (HHF) system for performance evaluation of plasma facing components in fusion devices

International Nuclear Information System (INIS)

Ngangom, Aomoa; Sarmah, Trinayan; Sah, Puspa; Kakati, Mayur; Ghosh, Joydeep

2015-01-01

A wide variety of high heat and particle flux test facilities are being used by the fusion community to evaluate the thermal performance of plasma facing materials/components, which includes electron beam, ion beam, neutral beam and thermal plasma assisted sources. In addition to simulate heat loads, plasma sources have the additional advantage of reproducing exact fusion plasma like conditions, in terms of plasma density, temperature and particle flux. At CPP-IPR, Assam, we have developed a high heat and particle flux facility using a DC, non-transferred, segmented thermal plasma torch system, which can produce a constricted, stabilized plasma jet with high ion density. In this system, the plasma torch exhausts into a low pressure chamber containing the materials to be irradiated, which produces an expanded plasma jet with more uniform profiles, compared to plasma torches operated at atmospheric pressure. The heat flux of the plasma beam was studied by using circular calorimeters of different diameters (2 and 3 cm) for different input power (5-55 kW). The effect of the change in gas (argon) flow rate and mixing of gases (argon + hydrogen) was also studied. The heat profile of the plasma beam was also studied by using a pipe calorimeter. From this, the radial heat flux was calculated by using Abel inversion. It is seen that the required heat flux of 10 MW/m 2 is achievable in our system for pure argon plasma as well as for plasma with gas mixtures. The plasma parameters like the temperature, density and the beam velocity were studied by using optical emission spectroscopy. For this, a McPherson made 1.33 meter focal length spectrometer; model number 209, was used. A plane grating with 1800 g/mm was used which gave a spectral resolution of 0.007 nm. A detailed characterization with respect to these plasma parameters for different gas (argon) flow rate and mixing of gases (argon+hydrogen) for different input power will be presented in this paper. The plasma

Plasma spraying process of disperse carbides for spraying and facing

International Nuclear Information System (INIS)

Blinkov, I.V.; Vishnevetskaya, I.A.; Kostyukovich, T.G.; Ostapovich, A.O.

1989-01-01

A possibility to metallize carbides in plasma of impulsing capacitor discharge is considered. Powders granulation occurs during plasma spraying process, ceramic core being completely capped. X-ray phase and chemical analyses of coatings did not show considerable changes of carbon content in carbides before and after plasma processing. This distinguishes the process of carbides metallization in impulsing plasma from the similar processing in arc and high-frequency plasma generator. Use of powder composites produced in the impulsing capacitor discharge, for plasma spraying and laser facing permits 2-3 times increasing wear resistance of the surface layer as against the coatings produced from mechanical powders mixtures

The dissociation of NZP (Ca{sub 0.5}Sr{sub 0.5}Zr{sub 4}P{sub 6}O{sub 24}) during plasma spraying[Sodium Zirconium Phosphate

Energy Technology Data Exchange (ETDEWEB)

Trice, R.W.; Brewer, L.N.; Faber, K.T.

2000-04-01

Sodium zirconium phosphate (NaZr{sub 2}P{sub 3}O{sub 12} or NZP) was first systematically evaluated in the early 1980s by Roy and co-workers, who demonstrated its extremely low coefficient of thermal expansion (CTE). It was later shown that other group IA and IIA atoms can be ionically substituted into the NZP crystal structure to adjust the CTE. As a result of their low and tailorable CTEs, NZP's have potential use as a protective coating for silicon-based ceramics and carbon-carbon composites. One technique for the application of ceramic coatings employs plasma-spraying. In this process, powders are injected into a plasma flame, melted, and propelled onto a substrate. The resulting coating microstructure is typically composed of thin lamellae (from each melted particle) stacked on top of one another during each pass of the torch. In the current research, NZP has been plasma-sprayed using the recently patented small particle plasma-spray process. The microstructure was then analyzed using transmission electron microscopy and x-ray diffraction to identify the phases in the complex coating that resulted.

Plasma sprayed Nd-Fe-B permanent magnets

International Nuclear Information System (INIS)

Willson, M.; Bauser, S.; Liu, S.; Huang, M.

2003-01-01

This study demonstrated that the plasma spray deposition method is an alternative process for producing Nd-Fe-B magnets in addition to the two existing principal processes: the powder metallurgy process for producing sintered Nd-Fe-B magnets and the melt spinning process for bonded Nd-Fe-B magnets. Plasma spray is a potentially better process for producing magnetic parts with complicated shape, large area, thin thickness, small dimension, or unusual geometry. High intrinsic coercivity greater than 15 kOe was readily obtained for Nd 16 Dy 1 Fe 76 B 7 even in the as-deposited condition when the substrate was preheated. The plasma spray process contains only three steps: melting, crushing, and plasma spray, which is much simpler than the powder metallurgy and melt spinning processes. Without preheating the substrate, the coercivity was usually very low (∼0.1 kOe) in the as-deposited condition and it increased to 10 to >15 kOe after anneal. Evidence of magnetocrystalline anisotropy was observed in plasma sprayed Nd 15 Dy 1 Fe 77 B 7 magnets when the substrate was not preheated. It is believed that a crystal texture was developed during the plasma spray as a result of the existence of a temperature gradient in the solidifying melt

Influence of spray parameters on the microstructure and mechanical properties of gas-tunnel plasma sprayed hydroxyapatite coatings

International Nuclear Information System (INIS)

Morks, M.F.; Kobayashi, Akira

2007-01-01

For biomedical applications, hydroxyapatite (HA) coatings were deposited on 304 stainless steel substrate by using a gas tunnel type plasma spraying process. The influences of spraying distances and plasma arc currents on the microstructure, hardness and adhesion properties of HA coatings were investigated. Microstructure observation by SEM showed that HA coatings sprayed at low plasma power have a porous structure and poor hardness. HA coatings sprayed at high plasma power and short spraying distance are characterized by good adhesion and low porosity with dense structure. Hardness increased for HA coatings sprayed at shorter spraying distance and higher plasma power, mainly due to the formation of dense coatings

Plasma sprayed samarium--cobalt permanent magnets

International Nuclear Information System (INIS)

Willson, M.C.; Janowiecki, R.J.

1975-01-01

Samarium--cobalt permanent magnets were fabricated by arc plasma spraying. This process involves the injection of relatively coarse powder particles into a high-temperature gas for melting and spraying onto a substrate. The technique is being investigated as an economical method for fabricating cobalt--rare earth magnets for advanced traveling wave tubes and cross-field amplifiers. Plasma spraying permits deposition of material at high rates over large areas with optional direct bonding to the substrate, and offers the ability to fabricate magnets in a variety of shapes and sizes. Isotropic magnets were produced with high coercivity and good reproducibility in magnetic properties. Post-spray thermal treatments were used to enhance the magnetic properties of sprayed deposits. Samarium--cobalt magnets, sprayed from samarium-rich powder and subjected to post-spray heat treatment, displayed energy products in excess of 9 million gauss-oersteds and coercive forces of approximately 6000 oersteds. Bar magnet arrays were constructed by depositing magnets on ceramic substrates. (auth)

Plasma sprayed samarium--cobalt permanent magnets

International Nuclear Information System (INIS)

Willson, M.C.; Janowiecki, R.J.

1975-01-01

Samarium--Co permanent magnets were fabricated by arc plasma spraying. This process involves the injection of relatively coarse powder particles into a high temperature gas for melting and spraying onto a substrate. The technique is being investigated as an economical method for fabricating Co--rare earth magnets for advanced traveling wave tubes and cross-field amplifiers. Plasma spraying permits deposition of material at high rates over large areas with optional direct bonding to the substrate, and offers the ability to fabricate magnets in a variety of shapes and sizes. Isotropic magnets were produced with high coercivity and good reproducibility in magnetic properties. Post-spray thermal treatments were used to enhance the magnetic properties of sprayed deposits. Samarium--Co magnets, sprayed from Sm-rich powder and subjected to post-spray heat treatment, displayed energy products in excess of 9 million G-Oe and coercive forces of approximately 6000 Oe. Bar magnet arrays were constructed by depositing magnets on ceramic substrates

Characterization of gas tunnel type plasma sprayed hydroxyapatite-nanostructure titania composite coatings

Science.gov (United States)

Yugeswaran, S.; Kobayashi, A.; Ucisik, A. Hikmet; Subramanian, B.

2015-08-01

Hydroxyapatite (HA) can be coated onto metal implants as a ceramic biocompatible coating to bridge the growth between implants and human tissue. Meanwhile many efforts have been made to improve the mechanical properties of the HA coatings without affecting its bioactivity. In the present study, nanostructure titania (TiO2) was mixed with HA powder and HA-nanostructure TiO2 composite coatings were produced by gas tunnel type plasma spraying torch under optimized spraying conditions. For this purpose, composition of 10 wt% TiO2 + 90 wt% HA, 20 wt% TiO2 + 80 wt% HA and 30 wt% TiO2 + 70 wt% HA were selected as the feedstock materials. The phase, microstructure and mechanical properties of the coatings were characterized. The obtained results validated that the increase in weight percentage of nanostructure TiO2 in HA coating significantly increased the microhardness, adhesive strength and wear resistance of the coatings. Analysis of the in vitro bioactivity and cytocompatibility of the coatings were done using conventional simulated body fluid (c-SBF) solution and cultured green fluorescent protein (GFP) labeled marrow stromal cells (MSCs) respectively. The bioactivity results revealed that the composite coating has bio-active surface with good cytocompatibility.

Influence of a transverse magnetic field on arc root movements in a dc plasma torch: Diamagnetic effect of arc column

International Nuclear Information System (INIS)

Kim, Keun Su

2009-01-01

The effect of a transverse magnetic field on the anodic arc root movement inside a dc plasma torch has been investigated. The arc voltage fluctuation, which represents the degree of the arc instability, was reduced to 28.6% of the original value and the high frequency components in the voltage signal also decreased in their magnitudes. The inherent arc instability in a dc thermal plasma torch seems to be suppressed by a diamagnetic effect of the arc column. Furthermore, the measured voltage wave forms indicated that the arc root attachment mode would be controllable by a transverse magnetic field

Comparative study of two- and three-dimensional modeling on arc discharge phenomena inside a thermal plasma torch with hollow electrodes

International Nuclear Information System (INIS)

Kim, Keun Su; Park, Jin Myung; Choi, Sooseok; Kim, Jongin; Hong, Sang Hee

2008-01-01

A comparative study between two- and three-dimensional (2D and 3D) modeling is carried out on arc discharge phenomena inside a thermal plasma torch with hollow electrodes, in order to evaluate the effects of arc root configuration characterized by either 2D annular or 3D highly localized attachment on the electrode surface. For this purpose, a more precise 3D transient model has been developed by taking account of 3D arc current distribution and arc root rotation. The 3D simulation results apparently reveal that the 3D arc root attachment brings about the inherent 3D and turbulence nature of plasma fields inside the torch. It is also found that the constricted arc column near the vortex chamber plays an important role in heating and acceleration of injected arc gases by concentrating arc currents on the axis of the hollow electrodes. The inherent 3D nature of arc discharge is well preserved inside the cathode region, while these 3D features slowly diminish behind the vortex chamber where the turbulent flow begins to be developed in the anode region. Based on the present simulation results, it is noted that the mixing effects of the strong turbulent flow on the heat and mass transfer are mainly responsible for the gradual relaxation of the 3D structures of plasma fields into the 2D axisymmetric ones that eventually appear in the anode region near the torch exit. From a detailed comparison of the 3D results with the 2D ones, the arc root configuration seems to have a significant effect on the heat transfer to the electrode surfaces interacting with the turbulent plasma flow. That is, in the 2D simulation based on an axisymmetric stationary model, the turbulence phenomena are fairly underestimated and the amount of heat transferred to the cold anode wall is calculated to be smaller than that obtained in the 3D simulation. For the validation of the numerical simulations, calculated plasma temperatures and axial velocities are compared with experimentally measured ones

Development of a 30 kW Inductively Coupled Plasma Torch Facility for Advanced Aerospace Material Investigations

Science.gov (United States)

2012-02-21

Mac MEDIA. Nature & Type: Identification: SOFTWARE . Name: Microsoft Word 2010 KEY WORDS LANGUAGE CODE ENG APPROVAL. Plasma torch, ground...15. P. F. Barbante, “Accurate and Efficient Modeling of High Temperature Non- equilibrium Air Flows,” Ph.D. Thesis, Univ. Libre de Bruxelles

Nanostructured Photocatalytic TiO2 Coating Deposited by Suspension Plasma Spraying with Different Injection Positions

Science.gov (United States)

Liu, Xuezhang; Wen, Kui; Deng, Chunming; Yang, Kun; Deng, Changguang; Liu, Min; Zhou, Kesong

2018-02-01

High plasma power is beneficial for the deposition efficiency and adhesive strength of suspension-sprayed photocatalytic TiO2 coatings, but it confronts two challenges: one is the reduced activity due to the critical phase transformation of anatase into rutile, and the other is fragmented droplets which cannot be easily injected into the plasma core. Here, TiO2 coatings were deposited at high plasma power and the position of suspension injection was varied with the guidance of numerical simulation. The simulation was based on a realistic three-dimensional time-dependent numerical model that included the inside and outside of torch regions. Scanning electron microscopy was performed to study the microstructure of the TiO2 coatings, whereas x-ray diffraction was adopted to analyze phase composition. Meanwhile, photocatalytic activities of the manufactured TiO2 coatings were evaluated by the degradation of an aqueous solution of methylene blue dye. Fragmented droplets were uniformly injected into the plasma jet, and the solidification pathway of melting particles was modified by varying the position of suspension injection. A nanostructured TiO2 coating with 93.9% anatase content was obtained at high plasma power (48.1 kW), and the adhesive coating bonding to stainless steel exhibited the desired photocatalytic activity.

Hydrogen permeation properties of plasma-sprayed tungsten

International Nuclear Information System (INIS)

Anderl, R.A.; Pawelko, R.J.; Hankins, M.R.; Longhurst, G.R.; Neiser, R.A.

1994-01-01

Tungsten has been proposed as a plasma-facing component material for advanced fusion facilities. This paper reports on laboratory-scale studies that were done to assess the hydrogen permeation properties of plasma-sprayed tungsten for such applications. The work entailed deuterium permeation measurements for plasma-sprayed (PS) tungsten coatings, sputter-deposited (SP) tungsten coatings, and steel substrate material using a mass-analyzed, 3 keV D + 3 ion beam with fluxes of similar 6.5x10 19 D/m 2 s. Extensive characterization analyses for the plasma-sprayed tungsten coatings were made using Auger spectrometry and scanning electron microscopy (SEM). Observed permeation rates through composite PS-tungsten/steel specimens were several orders of magnitude below the permeation levels observed for SP-tungsten/steel composite specimens and pure steel specimens. Characterization analyses indicated that the plasma-sprayed tungsten coating had a nonhomogeneous microstructure that consisted of splats with columnar solidification, partially-melted particles with grain boundaries, and void regions. Reduced permeation levels can be attributed to the complex microstructure and a substantial surface-connected porosity. ((orig.))

Hydrogen permeation properties of plasma-sprayed tungsten

Energy Technology Data Exchange (ETDEWEB)

Anderl, R.A. (Idaho National Engineering Lab., EG and G Idaho Inc., Idaho Falls, ID (United States)); Pawelko, R.J. (Idaho National Engineering Lab., EG and G Idaho Inc., Idaho Falls, ID (United States)); Hankins, M.R. (Idaho National Engineering Lab., EG and G Idaho Inc., Idaho Falls, ID (United States)); Longhurst, G.R. (Idaho National Engineering Lab., EG and G Idaho Inc., Idaho Falls, ID (United States)); Neiser, R.A. (Sandia National Laboratories, Albuquerque, NM 87185 (United States))

1994-09-01

Tungsten has been proposed as a plasma-facing component material for advanced fusion facilities. This paper reports on laboratory-scale studies that were done to assess the hydrogen permeation properties of plasma-sprayed tungsten for such applications. The work entailed deuterium permeation measurements for plasma-sprayed (PS) tungsten coatings, sputter-deposited (SP) tungsten coatings, and steel substrate material using a mass-analyzed, 3 keV D[sup +][sub 3] ion beam with fluxes of similar 6.5x10[sup 19] D/m[sup 2] s. Extensive characterization analyses for the plasma-sprayed tungsten coatings were made using Auger spectrometry and scanning electron microscopy (SEM). Observed permeation rates through composite PS-tungsten/steel specimens were several orders of magnitude below the permeation levels observed for SP-tungsten/steel composite specimens and pure steel specimens. Characterization analyses indicated that the plasma-sprayed tungsten coating had a nonhomogeneous microstructure that consisted of splats with columnar solidification, partially-melted particles with grain boundaries, and void regions. Reduced permeation levels can be attributed to the complex microstructure and a substantial surface-connected porosity. ((orig.))

Atmospheric-pressure plasma technology

International Nuclear Information System (INIS)

Kogelschatz, U

2004-01-01

Major industrial plasma processes operating close to atmospheric pressure are discussed. Applications of thermal plasmas include electric arc furnaces and plasma torches for generation of powders, for spraying refractory materials, for cutting and welding and for destruction of hazardous waste. Other applications include miniature circuit breakers and electrical discharge machining. Non-equilibrium cold plasmas at atmospheric pressure are obtained in corona discharges used in electrostatic precipitators and in dielectric-barrier discharges used for generation of ozone, for pollution control and for surface treatment. More recent applications include UV excimer lamps, mercury-free fluorescent lamps and flat plasma displays

Plasma sprayed coatings on crankshaft used steels

Science.gov (United States)

Mahu, G.; Munteanu, C.; Istrate, B.; Benchea, M.

2017-08-01

Plasma spray coatings may be an alternative to conventional heat treatment of main journals and crankpins of the crankshaft. The applications of plasma coatings are various and present multiple advantages compared to electric arc wire spraying or flame spraying. The study examines the layers sprayed with the following powders: Cr3C2- 25(Ni 20Cr), Al2O3- 13TiO2, Cr2O3-SiO2- TiO2 on the surface of steels used in the construction of a crankshaft (C45). The plasma spray coatings were made with the Spray wizard 9MCE facility at atmospheric pressure. The samples were analyzed in terms of micro and morphological using optical microscopy, scanning electron microscopy and X-ray diffraction. Wear tests on samples that have undergone simulates extreme working conditions of the crankshafts. In order to emphasize adherence to the base material sprayed layer, were carried out tests of microscratches and micro-indentation. Results have showed a relatively compact morphological aspect given by the successive coatings with splat-like specific structures. Following the microscratch analysis it can be concluded that Al2O3-13TiO2 coating has a higher purpose in terms of hardness compared to Cr3C2-(Ni 20Cr) and Cr2O3-SiO2- TiO2 powders. Thermal coatings of the deposited powders have increased the mechanical properties of the material. The results stand to confirm that plasma sprayed Al2O3-13TiO2 powder is in fact a efficient solution for preventing mechanical wear, even with a faulty lubrication system.

Detection, in real time, of metallic pollutants present in the industrial atmospheric effluents by inductively coupled plasma torch; Detection, en temps reel, d'elements metalliques presents dans les rejets atmospheriques industriels par torche a plasma a couplage inductif

Energy Technology Data Exchange (ETDEWEB)

Vacher, D.

2001-12-15

This work is devoted to the development of a process of detection in real time of metallic pollutants present in industrial atmospheric effluents. The method of measurement is the atomic spectrometry of emission coupled to an ICP torch (Inductively coupled Plasma). The technology of the fluidized beds is used as system of introduction of the metallic particles into the ICP torch, the interest of the principle of detection resting on the stamping from the usual procedure of calibration of the analytical system. The results are presented in two parts. The first relates to the diagnosis of plasmas formed with various mixtures of N{sub 2}/O{sub 2} which one corresponds to pure air, the second presents the setting process of detection in real time starting from the intensities ratios of the spectral lines of the metallic element with those of the plasma-producing element (argon or pure air) The study of the diagnosis of plasmas made up of mixtures N{sub 2}/O{sub 2} relates to the determination of the atomic excitation temperature from the spectral lines of the copper element and the evaluation of the thermal disequilibrium q Te/Th. This last is obtained by considering the mass enthalpy of various mixtures N{sub 2}/O{sub 2}. The existence of a small thermal disequilibrium is highlighted. The study of detection in real time by ICP torch, without calibration of the system, is based on three points: - spectroscopic data processing to determine the values of the intensities ratios of spectral lines; - the insertion of the intensities ratios and the characteristics of plasma (argon or pure air) into a calculation code of plasma composition; - the comparison of the mass flux values of the metallic pollutants, in real time, obtained by experiments with those resulting from the elutriation calculation, term which defines the phenomenon of entrainment of the particles out of the fluidized bed. The results made it possible to show the similarity of the analytical system response

How to increase the hydrophobicity of PTFE surfaces using an r.f. atmospheric-pressure plasma torch

NARCIS (Netherlands)

Carbone, E.A.D.; Boucher, N.; Sferrazza, M.; Reniers, F.

2010-01-01

An experimental investigation of the surface modification of polytetrafluoroethylene (PTFE) by an Ar and Ar/O2 plasma created with an atmospheric-pressure radio frequency (r.f.) torch is presented here. The surfaces were analyzed by atomic force microscopy (AFM), XPS and water contact angle (WCA) to

Comparison of solidity and fractal dimension of plasma sprayed splat with different spreading morphologies

Energy Technology Data Exchange (ETDEWEB)

Chen, Shu-ying; Ma, Guo-zheng, E-mail: magz0209@163.com; Wang, Hai-dou, E-mail: wanghaidou@aliyun.com.cn; He, Peng-fei; Liu, Ming; Wang, Hai-jun; Xu, Bin-shi

2017-07-01

Highlights: • The solidification mechanism of the plasma sprayed droplets deposited on substrate preheated with different temperature was discussed. • The solidified morphology of individual splat was detected by image analysis method. • The fractal dimension, solidity, area and perimeter, were employed to characterize the morphology of the splat. • The typical solidification modes of Fe-based alloy droplet could be divided into three types, namely, flower-like splat, splashed splat and disk-like splat, which may be attributed the differences of solidification rate of the droplets and adsorption on the substrates. - Abstract: The paper deals with the quantitative characterization of spreading morphologies of plasma sprayed Fe-based alloy droplets deposited on mirror polished steels with different preheated temperature. The plasma torch was utilized as heat producer. The influence of substrate temperature on the solidification mechanism of molten droplets was investigated. The image analysis method (IMA) was employed to identify single splat from the field emission scanning electron microscope (FE-SEM) morphology. The result shows that the substrate preheated temperature has a significant effect on the flattening behavior of molten droplets. With the increment of substrate temperature, the solidification mode of splat changes from flower-like and splashed splat to disk-like splat due to the modification of wettability and cooling velocity between molten droplet and substrate. Compared with area and perimeter, both fractal dimension (FD) and solidity could separately detect the solidification mode of splat to a certain extent, while the FD seems to be more excellent in characterizing irregular morphology of splat in contrast with solidity. However, the combination of FD and solidity is more efficient in classifying solidification mode of splat.

Radio frequency induction plasma spraying of molybdenum

International Nuclear Information System (INIS)

Jiang Xianliang

2003-01-01

Radio frequency (RF) induction plasma was used to make free-standing deposition of molybdenum (Mo). The phenomena of particle melting, flattening, and stacking were investigated. The effect of process parameters such as plasma power, chamber pressure, and spray distance on the phenomena mentioned above was studied. Scanning electron microscopy (SEM) was used to analyze the plasma-processed powder, splats formed, and deposits obtained. Experimental results show that less Mo particles are spheroidized when compared to the number of spheroidized tungsten (W) particles at the same powder feed rate under the same plasma spray condition. Molten Mo particles can be sufficiently flattened on substrate. The influence of the process parameters on the flattening behavior is not significant. Mo deposit is not as dense as W deposit, due to the splash and low impact of molten Mo particles. Oxidation of the Mo powder with a large particle size is not evident under the low pressure plasma spray

Research of Plasma Spraying Process on Aluminum-Magnesium Alloy

Directory of Open Access Journals (Sweden)

Patricija Kavaliauskaitė

2016-04-01

Full Text Available The article examines plasma sprayed 95Ni-5Al coatings on alu-minum-magnesium (Mg ≈ 2,6‒3,6 % alloy substrate. Alumi-num-magnesium samples prior spraying were prepared with mechanical treatment (blasting with Al2O3. 95Ni-5Al coatings on aluminum-magnesium alloys were sprayed with different parameters of process and coating‘s thickness, porosity, micro-hardness and microstructure were evaluated. Also numerical simulations in electric and magnetic phenomena of plasma spray-ing were carried out.

Abatement of fluorinated compounds using a 2.45 GHz microwave plasma torch with a reverse vortex plasma reactor

Energy Technology Data Exchange (ETDEWEB)

Kim, J.H.; Cho, C.H.; Shin, D.H. [Plasma Technology Research Center, National Fusion Research Institute, 814-2 Oxikdo-dong, Gunsan-city, Jeollabuk-do (Korea, Republic of); Hong, Y.C., E-mail: ychong@nfri.re.kr [Plasma Technology Research Center, National Fusion Research Institute, 814-2 Oxikdo-dong, Gunsan-city, Jeollabuk-do (Korea, Republic of); Shin, Y.W. [Plasma Technology Research Center, National Fusion Research Institute, 814-2 Oxikdo-dong, Gunsan-city, Jeollabuk-do (Korea, Republic of); School of Advanced Green Energy and Environments, Handong Global University, Heunghae-eup, Buk-gu, Pohang-city, Gyeongbuk (Korea, Republic of)

2015-08-30

Highlights: • We developed a microwave plasma torch with reverse vortex reactor (RVR). • We calculated a volume fraction and temperature distribution of discharge gas and waste. • The performance of reverse vortex reactor increased from 29% to 43% than conventional vortex reactor. - Abstract: Abatement of fluorinated compounds (FCs) used in semiconductor and display industries has received an attention due to the increasingly stricter regulation on their emission. We have developed a 2.45 GHz microwave plasma torch with reverse vortex reactor (RVR). In order to design a reverse vortex plasma reactor, we calculated a volume fraction and temperature distribution of discharge gas and waste gas in RVR by ANSYS CFX of computational fluid dynamics (CFD) simulation code. Abatement experiments have been performed with respect to SF{sub 6}, NF{sub 3} by varying plasma power and N{sub 2} flow rates, and FCs concentration. Detailed experiments were conducted on the abatement of NF{sub 3} and SF{sub 6} in terms of destruction and removal efficiency (DRE) using Fourier transform infrared (FTIR). The DRE of 99.9% for NF{sub 3} was achieved without an additive gas at the N{sub 2} flow rate of 150 liter per minute (L/min) by applying a microwave power of 6 kW with RVR. Also, a DRE of SF{sub 6} was 99.99% at the N{sub 2} flow rate of 60 L/min using an applied microwave power of 6 kW. The performance of reverse vortex reactor increased about 43% of NF{sub 3} and 29% of SF{sub 6} abatements results definition by decomposition energy per liter more than conventional vortex reactor.

Hydrogen permeation properties of plasma-sprayed tungsten*1

Science.gov (United States)

Anderl, R. A.; Pawelko, R. J.; Hankins, M. R.; Longhurst, G. R.; Neiser, R. A.

1994-09-01

Tungsten has been proposed as a plasma-facing component material for advanced fusion facilities. This paper reports on laboratory-scale studies that were done to assess the hydrogen permeation properties of plasma-sprayed tungsten for such applications. The work entailed deuterium permeation measurements for plasma-sprayed (PS) tungsten coatings, sputter-deposited (SP) tungsten coatings, and steel substrate material using a mass-analyzed, 3 keV D 3+ ion beam with fluxes of ˜6.5 × 10 19 D/m 2 s. Extensive characterization analyses for the plasma-sprayed tungsten coatings were made using Auger spectrometry and scanning electron microscopy (SEM). Observed permeation rates through composite PS-tungsten/steel specimens were several orders of magnitude below the permeation levels observed for SP-tungsten/steel composite specimens and pure steel specimens. Characterization analyses indicated that the plasma-sprayed tungsten coating had a nonhomogeneous microstructure that consisted of splats with columnar solidification, partially-melted particles with grain boundaries, and void regions. Reduced permeation levels can be attributed to the complex microstructure and a substantial surface-connected porosity.

Alignment Fixtures For Vacuum-Plasma-Spray Gun

Science.gov (United States)

Woodford, William H.; Mckechnie, Timothy N.; Power, Christopher A.; Daniel, Ronald L., Jr.

1993-01-01

Fixtures for alignment of vacuum-plasma-spray guns built. Each fixture designed to fit specific gun and holds small, battery-powered laser on centerline of gun. Laser beam projects small red dot where centerline intersects surface of workpiece to be sprayed. After laser beam positioned on surface of workpiece, fixture removed from gun and spraying proceeds.

Low pressure plasma spray deposition of W-Ni-Fe alloy

International Nuclear Information System (INIS)

Mutasim, Z.Z.; Smith, R.W.

1991-01-01

The production of net shape refractory metal structural preforms are increasing in importance in chemical processing, defense and aerospace applications. Conventional methods become limited for refractory metal processing due to the high melting temperatures and fabrication difficulties. Plasma spray forming, a high temperature process, has been shown to be capable of refractory metal powder consolidation in net shape products. The research reported here has evaluated this method for the deposition of heavy tungsten alloys. Plasma Melted Rapidly Solidified (PMRS) W 8%Ni-2%Fe refractory metal powders were spray formed using vacuum plasma spray (VPS) process and produced 99% dense, fine grain and homogeneous microstructures. In this paper plasma operating parameters (plasma arc gas type and flowrate plasma gun nozzle size and spray distance) were studied and their effects on deposit's density and microstructure are reported

Twin carbon arc torch | Skelskey | SINET: Ethiopian Journal of Science

African Journals Online (AJOL)

... and applied to brazing and heating in order to offer an alternative to the much more expensive oxyacetylene torch and to the usually environmentally degrading use of charcoal. SINET: Ethiopian Journal of Science Vol. 24, No. 1 (June 2001), pp. 133-138. Key words/phrases: Arc, brazing, carbon electrode, plasma, torch ...

Model of the macrostructure formation of plasma sprayed coatings

International Nuclear Information System (INIS)

Gnedovets, A.G.; Kalita, V.I.

2007-01-01

A 3D discrete ballistic model of plasma sprayed coatings structure formation is presented. The effect of a spraying angle on porous macrostructure of coatings is investigated by numerical computations.Computer simulation results as well as experimental data show that at a sputtering angle less than 45 deg the mechanism of surface relief formation is changed and the relief consists of valleys and ridges under such conditions of plasma spraying [ru

Understanding plasma spraying process and characteristics of DC-arc plasma gun (PJ-100

Directory of Open Access Journals (Sweden)

Jovana Ružić

2012-12-01

Full Text Available The thermal spray processes are a group of coating processes used to apply metallic or non-metallic coatings. In these processes energy sources are used to heat the coating material (in the form of powder, wire, or rod form to a molten or semi-molten state and accelerated towards a prepared surface by either carrier gases or atomization jets. In plasma spraying process, the spraying material is generally in the form of powder and requires a carrier gas to feed the powder into the plasma jet, which is passing between the hot cathode and the cylindrical nozzle-shaped anode. The design of DC plasma gun (PJ - 100 is designed and manufactured in Serbia. Plasma spaying process, the powder injection with the heat, momentum and mass transfers between particles and plasma jet, and the latest developments related to the production of DC plasma gun are described in this article.

Plasma sprayed thermoregulating coatings

International Nuclear Information System (INIS)

Kudinov, V.V.; Puzanov, A.A.; Zambrzhitskij, A.P.; Soboleva, V.V.

1979-01-01

Shown is the possibility of plasma spraying application for thermoregulating coating formation. Given are test results of service properties of BeO, Al 2 O 2 plasma coatings on the substrates of the MA2-1 magnesium alloy. Described is a device for studying durability of coating optical parameters under ultraviolet irradiation in deep vacuum. Dynamics of absorption coefficient, growth caused by an increase in absorption centers amount under such irradiation is investigated

Excess of L-Alanine in Amino Acids Synthesized in a Plasma Torch Generated by a Hypervelocity Meteorite Impact Reproduced in the Laboratory

Science.gov (United States)

Managadze, George G.; Engle, Michael H.; Getty, Stephanie A.; Wurz, Peter; Brinckerhoff, William B.; Shokolov, Anatoly; Sholin, Gennady; Terent'ev, Sergey A.; Chumikov, Alexander E.; Skalkin, Alexander S

2016-01-01

We present a laboratory reproduction of hypervelocity impacts of a carbon containing meteorite on a mineral substance representative of planetary surfaces. The physical conditions of the resulting impact plasma torch provide favorable conditions for abiogenic synthesis of protein amino acids: We identified glycine and alanine, and in smaller quantities serine, in the produced material. Moreover, we observe breaking of alanine mirror symmetry with L excess, which coincides with the bioorganic world. Therefore the selection of L-amino acids for the formation of proteins for living matter could have been the result from plasma processes occurring during the impact meteorites on the surface. This indicates that the plasma torch from meteorite impacts could play an important role in the formation of biomolecular homochirality. Thus, meteorite impacts possibly were the initial stage of this process and promoted conditions for the emergence of a living matter.

Development & characterization of alumina coating by atmospheric plasma spraying

Science.gov (United States)

Sebastian, Jobin; Scaria, Abyson; Kurian, Don George

2018-03-01

Ceramic coatings are applied on metals to prevent them from oxidation and corrosion at room as well as elevated temperatures. The service environment, mechanisms of protection, chemical and mechanical compatibility, application method, control of coating quality and ability of the coating to be repaired are the factors that need to be considered while selecting the required coating. The coatings based on oxide materials provides high degree of thermal insulation and protection against oxidation at high temperatures for the underlying substrate materials. These coatings are usually applied by the flame or plasma spraying methods. The surface cleanliness needs to be ensured before spraying. Abrasive blasting can be used to provide the required surface roughness for good adhesion between the substrate and the coating. A pre bond coat like Nickel Chromium can be applied on to the substrate material before spraying the oxide coating to avoid chances of poor adhesion between the oxide coating and the metallic substrate. Plasma spraying produces oxide coatings of greater density, higher hardness, and smooth surface finish than that of the flame spraying process Inert gas is often used for generation of plasma gas so as to avoid the oxidation of the substrate material. The work focuses to develop, characterize and optimize the parameters used in Al2O3 coating on transition stainless steel substrate material for minimizing the wear rate and maximizing the leak tightness using plasma spray process. The experiment is designed using Taguchi’s L9 orthogonal array. The parameters that are to be optimized are plasma voltage, spraying distance and the cooling jet pressure. The characterization techniques includes micro-hardness and porosity tests followed by Grey relational analysis of the results.

Plasma-spraying synthesis of high-performance photocatalytic TiO2 coatings

International Nuclear Information System (INIS)

Takahashi, Yasuo; Maeda, Masakatsu; Ohmori, Akira; Shibata, Yoshitaka; Miyano, Yasuyuki; Murai, Kensuke

2014-01-01

Anatase (A-) TiO 2 is a photocatalytic material that can decompose air-pollutants, acetaldehyde, bacteria, and so on. In this study, three kinds of powder (A-TiO 2 without HAp, TiO 2 + 10mass%HAp, and TiO 2 +30mass%HAp, where HAp is hydroxyapatite and PBS is polybutylene succinate) were plasma sprayed on biodegradable PBS substrates. HAp powder was mixed with A-TiO 2 powder by spray granulation in order to facilitate adsorption of acetaldehyde and bacteria. The crystal structure was almost completely maintained during the plasma spray process. HAp enhanced the decomposition of acetaldehyde and bacteria by promoting adsorption. A 10mass% HAp content was the most effective for decomposing acetaldehyde when plasma preheating of the PBS was not carried out before the plasma spraying. The plasma preheating of PBS increased the yield rate of the spray process and facilitated the decomposition of acetaldehyde by A-TiO 2 coatings without HAp. HAp addition improved photocatalytic sterilization when plasma preheating of the PBS was performed

Automatic targeting of plasma spray gun

Science.gov (United States)

Abbatiello, Leonard A.; Neal, Richard E.

1978-01-01

A means for monitoring the material portion in the flame of a plasma spray gun during spraying operations is provided. A collimated detector, sensitive to certain wavelengths of light emission, is used to locate the centroid of the material with each pass of the gun. The response from the detector is then relayed to the gun controller to be used to automatically realign the gun.

Automatic targeting of plasma spray gun

International Nuclear Information System (INIS)

Abbatiello, L.A.; Neal, R.E.

1978-01-01

A means for monitoring the material portion in the flame of a plasma spray gun during spraying operations is described. A collimated detector, sensitive to certain wavelengths of light emission, is used to locate the centroid of the material with each pass of the gun. The response from the detector is then relayed to the gun controller to be used to automatically realign the gun

Mathematical modelling of powder material motion and transportation in high-temperature flow core during plasma coatings application

Science.gov (United States)

Bogdanovich, V. I.; Giorbelidze, M. G.

2018-03-01

A problem of mathematical modelling of powder material motion and transportation in gas thermal flow core has been addressed. Undertaken studies indicate significant impact on dynamics of motion of sprayed particles of phenomenological law for drag coefficient and accounting momentum loss of a plasma jet upon acceleration of these particles and their diameter. It is determined that at great dispersion of spraying particles, they reach detail surface at different velocity and significant particles separation takes place at spraying spot. According to the results of mathematical modelling, requirements for admissible dispersion of diameters of particles used for spraying have been formulated. Research has also allowed reducing separation of particles at the spraying spot due to the selection of the method of powder feed to the anode channel of the plasma torch.

The effect of hydrogen on B4C coatings fabrication in inductively coupled plasma torch

Directory of Open Access Journals (Sweden)

Q. J. Guo

2018-02-01

Full Text Available Boron carbide (B4C coatings are prepared by an RF inductively coupled plasma (ICP torch with different amounts of hydrogen introduced into the sheath gas. The effects of the added hydrogen on the characteristics of the plasma are diagnosed by optical emission spectroscopy and high speed photography. The effects on the melting of B4C particles in the plasma are studied by scanning electron microscopy (SEM. The microstructure of the B4C coatings was determined with SEM imaging and x-ray diffraction analysis. The results show that adding hydrogen to the sheath gas leads to plasma contraction, which results in higher gas temperature of plasma. It also enhances B4C particles spheroidizing and improves the compactness of B4C coatings. Plasma processing does not change the main phase of boron carbide. The obtained results on B4C coatings on Cu substrates allows for improving the B4C coatings fabrication process.

Direct morphological comparison of vacuum plasma sprayed and detonation gun sprayed hydroxyapatite coatings for orthopaedic applications.

Science.gov (United States)

Gledhill, H C; Turner, I G; Doyle, C

1999-02-01

Hydroxyapatite coatings on titanium substrates were produced using two thermal spray techniques vacuum plasma spraying and detonation gun spraying. X-ray diffraction was used to compare crystallinity and residual stresses in the coatings. Porosity was measured using optical microscopy in conjunction with an image analysis system. Scanning electron microscopy and surface roughness measurements were used to characterise the surface morphologies of the coatings. The vacuum plasma sprayed coatings were found to have a lower residual stress, a higher crystallinity and a higher level of porosity than the detonation gun coatings. It is concluded that consideration needs to be given to the significance of such variations within the clinical context.

Plasma technology

International Nuclear Information System (INIS)

Drouet, M.G.

1984-03-01

IREQ was contracted by the Canadian Electrical Association to review plasma technology and assess the potential for application of this technology in Canada. A team of experts in the various aspects of this technology was assembled and each team member was asked to contribute to this report on the applications of plasma pertinent to his or her particular field of expertise. The following areas were examined in detail: iron, steel and strategic-metals production; surface treatment by spraying; welding and cutting; chemical processing; drying; and low-temperature treatment. A large market for the penetration of electricity has been identified. To build up confidence in the technology, support should be provided for selected R and D projects, plasma torch demonstrations at full power, and large-scale plasma process testing

Electroform/Plasma-Spray Laminates for X-Ray Optics

Science.gov (United States)

Ulmer, Melville P.; Graham, Michael; Vaynman, Semyon

2007-01-01

Electroform/plasma-spray laminates have shown promise as lightweight, strong, low-thermal-expansion components for xray optics. The basic idea is to exploit both (1) the well-established art of fabrication of optical components by replication and (2) plasma spraying as a means of reinforcing a thin replica optic with one or more backing layer(s) having tailorable thermomechanical properties. In x-ray optics as in other applications, replication reduces the time and cost of fabrication because grinding and polishing can be limited to a few thick masters, from which many lightweight replicas can thereafter be made. The first step in the fabrication of a component of the type in question is to make a replica optic by electroforming a thin layer of nickel on a master. Through proper control of the electroforming process conditions, it is possible to minimize residual stress and, hence, to minimize distortion in the replica. Next, a powder comprising ceramic particles coated with a metal compatible with the electroformed nickel is plasma-sprayed onto the backside of the nickel replica. Then through several repetitions and variations of the preceding steps or perhaps a small compressive stress, alternating layers of electroformed nickel and plasma-sprayed metal-coated ceramic powder are deposited. The thicknesses of the layers and the composition of the metal-coated ceramic powder are chosen to optimize the strength, areal mass density, and toughness of the finished component. An important benefit of using both electroforming and plasma spraying is the possibility of balancing stresses to a minimum level, which could be zero or perhaps a small net compressive stress designed to enhance the function of the component in its intended application.

Plasma sprayed alumina-titania coatings

International Nuclear Information System (INIS)

Steeper, T.J.; Rotolico, A.J.; Nerz, J.E.; Riggs, W.L. II; Varacalle, D.J. Jr.; Wilson, G.C.

1992-01-01

This paper presents an experimental study of the air plasma spraying (APS) of alumina-titania powder using argon-hydrogen working gases. This powder system is being used in the fabrication of heater tubes that emulate nuclear fuel tubes for use in thermal-hydraulic testing. Experiments were conducted using a Taguchi fractional-factorial design parametric study. Operating parameters were varied around the typical spray parameters in a systematic design of experiments in order to display the range of plasma processing conditions and their effect on the resultant coatings. The coatings were characterized by hardness and electrical tests, surface profilometry, image analysis, optical metallography, and x-ray diffraction. Coating qualities are discussed with respect to dielectric strength, hardness, porosity, surface roughness, deposition efficiency, and microstructure. attempts are made to correlate the features of the coatings with the changes in operating parameters

Plasma Sprayed Hydroxyapatite Coatings: Influence of Spraying Power on Microstructure

International Nuclear Information System (INIS)

Mohd, S. M.; Abd, M. Z.; Abd, A. N.

2010-01-01

The plasma sprayed hydroxyapatite (HA) coatings are used on metallic implants to enhance the bonding between the implant and bone in human body. The coating process was implemented at different spraying power for each spraying condition. The coatings formed from a rapid solidification of molten and partly molten particles that impact on the surface of substrate at high velocity and high temperature. The study was concentrated on different spraying power that is between 23 to 31 kW. The effect of different power on the coatings microstructure was investigated using scanning electron microscope (SEM) and phase composition was evaluated using X-ray diffraction (XRD) analysis. The coatings surface morphology showed distribution of molten, partially melted particles and some micro-cracks. The produced coatings were found to be porous as observed from the cross-sectional morphology. The coatings XRD results indicated the presence of crystalline phase of HA and each of the patterns was similar to the initial powder. Regardless of different spraying power, all the coatings were having similar XRD patterns.

Microstructural Effects and Properties of Non-line-of-Sight Coating Processing via Plasma Spray-Physical Vapor Deposition

Science.gov (United States)

Harder, Bryan J.; Zhu, Dongming; Schmitt, Michael P.; Wolfe, Douglas E.

2017-08-01

Plasma spray-physical vapor deposition (PS-PVD) is a unique processing method that bridges the gap between conventional thermal spray and vapor phase methods, and enables highly tailorable coatings composed of a variety of materials in thin, dense layers or columnar microstructures with modification of the processing conditions. The strengths of this processing technique are material and microstructural flexibility, deposition speed, and potential for non-line-of-sight (NLOS) capability by vaporization of the feedstock material. The NLOS capability of PS-PVD is investigated here using yttria-stabilized zirconia and gadolinium zirconate, which are materials of interest for turbine engine applications. PS-PVD coatings were applied to static cylindrical substrates approximately 6-19 mm in diameter to study the coating morphology as a function of angle. In addition, coatings were deposited on flat substrates under various impingement configurations. Impingement angle had significant effects on the deposition mode, and microscopy of coatings indicated that there was a shift in the deposition mode at approximately 90° from incidence on the cylindrical samples, which may indicate the onset of more turbulent flow and PVD-like growth. Coatings deposited at non-perpendicular angles exhibited a higher density and nearly a 2× improvement in erosion performance when compared to coatings deposited with the torch normal to the surface.

WELDING TORCH

Science.gov (United States)

Correy, T.B.

1961-10-01

A welding torch into which water and inert gas are piped separately for cooling and for providing a suitable gaseous atmosphere is described. A welding electrode is clamped in the torch by a removable collet sleeve and a removable collet head. Replacement of the sleeve and head with larger or smaller sleeve and head permits a larger or smaller welding electrode to be substituted on the torch. (AEC)

Production of press moulds by plasma spray forming process

International Nuclear Information System (INIS)

Borisov, Y.; Myakota, I.; Polyakov, S.

2001-01-01

Plasma spray forming process for production of press moulds which are used for manufacture of articles from plastics was developed. The press moulds were produced by plasma spraying of Cu-Al-Fe-alloy powder on surface of a master model. The master models were made from non-metallic materials with heat resistance below 70 C (wood, gypsum etc). Double cooling system which provides for a control of surface model temperature and quenching conditions of sprayed material was designed. It made possible on the one hand to support model surface temperature below 70 C and on the other hand to provide for temperature conditions of martensite transformation in Cu-Al-system with a fixation of metastable ductile α + β 1 -phase. This allowed to decrease residual stresses in sprayed layer (up to 0,5-2,5 MPa), to increase microhardness of the coating material (up to 1200-1800 MPa) and its ductility (σ B = 70-105 MPa, δ = 6-12 %). This plasma spray forming process makes possible to spray thick layers (5-20 mm and more) without their cracking and deformation. The process is used for a production of press moulds which are applied in shoes industry, for fabrication of toys, souvenirs etc. (author)

D. C. plasma-sprayed coatings of nano-structured alumina-titania-silica

CERN Document Server

Jiang Xian Liang

2002-01-01

nano-crystalline powders of omega(Al sub 2 O sub 3) = 95%, omega(TiO sub 2) = 3%, and omega(SiO sub 2) = 2%, were reprocessed into agglomerated particles for plasma spraying, by using consecutive steps of ball milling, slurry forming, spray drying, and heat treatment. D.C. plasma was used to spray the agglomerated nano-crystalline powders, and resultant coatings were deposited on the substrate of stainless steel. Scanning electron microscopy (SEM) was used to examine the morphology of the agglomerated powders and the cross section of the alumina-titania-silica coatings. Experimental results show that the agglomerated nano-crystalline particles are spherical, with a size from (10-90) mu m. The flow ability of the nano-crystalline powders is greatly improved after the reprocessing. The coatings deposited by the plasma spraying are mainly of nano-structure. Unlike conventional plasma-sprayed coatings, no laminar layer could be found in the nano-structured coatings. Although the nano-structured coatings have a lo...

Plasma spheroidization of iron powders in a non-transferred DC thermal plasma jet

International Nuclear Information System (INIS)

Kumar, S.; Selvarajan, V.

2008-01-01

In this paper, the results of plasma spheroidization of iron powders using a DC non-transferred plasma spray torch are presented. The morphology of the processed powders was characterized through scanning electron microscopy (SEM) and optical microscopy (OM). The percentages of spheroidized powders were calculated by the shape factors such as the Irregularity Parameter (IP) and Roundness (RN). A maximum of 83% of spheroidization can be achieved. The spheroidization results are compared with the theoretical estimation and they are found to be in good agreement. The phase composition of the spheroidized powder was analyzed by XRD. The effect of plasma jet temperature and plasma gas flow rate on spheroidization is discussed. At low plasma gas flow rates and at high plasma jet temperatures, the percentage of spheroidization is high

Plasma spraying of cerium-doped YAG

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Kubát, J.; Pala, Zdeněk; Nevrlá, Barbara

2014-01-01

Roč. 29, č. 19 (2014), s. 2344-2351 ISSN 0884-2914 R&D Projects: GA ČR(CZ) GAP108/12/1872 Institutional support: RVO:61389021 Keywords : plasma spraying * water-stabilized plasma Subject RIV: JK - Corrosion ; Surface Treatment of Materials Impact factor: 1.647, year: 2014 http://dx.doi.org/10.1557/jmr.2014.251

Molybdenum plasma spray powder, process for producing said powder, and coating made therefrom

International Nuclear Information System (INIS)

Lafferty, W.D.; Cheney, R.F.; Pierce, R.H.

1979-01-01

Plasma spray powders of molybdenum particles containing 0.5 to 15 weight percent oxygen and obtained by reacting molybdenum particles with oxygen or oxides in a plasma, form plasma spray coatings exhibiting hardness comparable to flame sprayed coatings formed from molybdenum wire and plasma coatings of molybdenum powders. Such oxygen rich molybdenum powders may be used to form wear resistant coatings, such as for piston rings. (author)

Research Into Ni-Cr-Si-B Coating Sprayed Onto Aluminium Substrate Using the Method of Plasma Spray

Directory of Open Access Journals (Sweden)

Raimonda Lukauskaitė

2013-02-01

Full Text Available The article deals with Ni base coatings deposited on aluminium substrate applying the method of plasma spray. The purpose of the conducted research is to improve the physical and mechanical properties of coatings on the surface of aluminium alloy work pieces. Spraying on aluminium alloys encounters serious problems, and therefore this work analyses the ways to make the situation more favourable. Before spraying, the surfaces of substrates were modified employing chemical and mechanical pre-treatment methods. The aim of pre-treating aluminium alloys was to remove oxide layers from the aluminium surface. Coating microstructures and porosity were characterised applying optical microscopy. Differences in the roughness of pre-treated surfaces have been determined referring to profilometry. The paper investigates the influence of the adhesion of plasma spray coatings on aluminium surface pretreatment. Microhardness technique was applied for measuring the hardness of coatings. The study also describes and compares the mechanical properties of Ni base coatings deposited on different pre-treated aluminium substrates using plasma spray.Article in Lithuanian

Research Into Ni-Cr-Si-B Coating Sprayed Onto Aluminium Substrate Using the Method of Plasma Spray

Directory of Open Access Journals (Sweden)

Raimonda Lukauskaitė

2012-12-01

Full Text Available The article deals with Ni base coatings deposited on aluminium substrate applying the method of plasma spray. The purpose of the conducted research is to improve the physical and mechanical properties of coatings on the surface of aluminium alloy work pieces. Spraying on aluminium alloys encounters serious problems, and therefore this work analyses the ways to make the situation more favourable. Before spraying, the surfaces of substrates were modified employing chemical and mechanical pre-treatment methods. The aim of pre-treating aluminium alloys was to remove oxide layers from the aluminium surface. Coating microstructures and porosity were characterised applying optical microscopy. Differences in the roughness of pre-treated surfaces have been determined referring to profilometry. The paper investigates the influence of the adhesion of plasma spray coatings on aluminium surface pretreatment. Microhardness technique was applied for measuring the hardness of coatings. The study also describes and compares the mechanical properties of Ni base coatings deposited on different pre-treated aluminium substrates using plasma spray.Article in Lithuanian

Plasma-sprayed tantalum/alumina cermets

International Nuclear Information System (INIS)

Kramer, C.M.

1977-12-01

Cermets of tantalum and alumina were fabricated by plasma spraying, with the amount of alumina varied from 0 to 65 percent (by volume). Each of four compositions was then measured for tensile strength, elastic modulus, and coefficient of thermal expansion. In general, strength and strain to failure decreased with increasing alumina content: 62 MPa for 100 percent Ta to 19 MPa for 35 v percent Ta. A maximum of 0.1 percent strain was observed for the sprayed 100 percent Ta specimens. The coefficient of thermal expansion measured for the pure Ta was 6.2 (10 -6 )/K

Plasma spraying of bioactive glass-ceramics containing bovine bone

Directory of Open Access Journals (Sweden)

Annamária Dobrádi

2017-06-01

Full Text Available Natural bone derived glass-ceramics are promising biomaterials for implants. However, due to their price and weak mechanical properties they are preferably applied as coatings on load bearing implants. This paper describes result obtained by plasma spraying of bioactive glass-ceramics containing natural bone onto selected implant materials, such as stainless steel, alumina, and titanium alloy. Adhesion of plasma sprayed coating was tested by computed X-ray tomography and SEM of cross sections. The results showed defect free interface between the coating and substrate, without cracks or gaps. Dissolution rate of the coating in simulated body fluid (SBF was readily controlled by the bone additives (phase composition, as well as microstructure. The SBF treatment of the plasma sprayed coating did not influence the boundary between the coating and substrate.

Comparative study of laminar and turbulent flow model with different operating parameters for radio frequency-inductively coupled plasma torch working at 3  MHz frequency at atmospheric pressure

International Nuclear Information System (INIS)

Punjabi, Sangeeta B.; Sahasrabudhe, S. N.; Das, A. K.; Joshi, N. K.; Mangalvedekar, H. A.; Kothari, D. C.

2014-01-01

This paper provides 2D comparative study of results obtained using laminar and turbulent flow model for RF (radio frequency) Inductively Coupled Plasma (ICP) torch. The study was done for the RF-ICP torch operating at 50 kW DC power and 3 MHz frequency located at BARC. The numerical modeling for this RF-ICP torch is done using ANSYS software with the developed User Defined Function. A comparative study is done between laminar and turbulent flow model to investigate how temperature and flow fields change when using different operating conditions such as (a) swirl and no swirl velocity for sheath gas flow rate, (b) variation in sheath gas flow rate, and (c) variation in plasma gas flow rate. These studies will be useful for different material processing applications

Process maps for plasma spray: Part 1: Plasma-particle interactions

International Nuclear Information System (INIS)

Gilmore, Delwyn L.; Neiser, Richard A. Jr.; Wan, Yuepeng; Sampath, Sanjay

2000-01-01

This is the first paper of a two part series based on an integrated study carried out at Sandia National Laboratories and the State University of New York at Stony Brook. The aim of the study is to develop a more fundamental understanding of plasma-particle interactions, droplet-substrate interactions, deposit formation dynamics and microstructural development as well as final deposit properties. The purpose is to create models that can be used to link processing to performance. Process maps have been developed for air plasma spray of molybdenum. Experimental work was done to investigate the importance of such spray parameters as gun current, auxiliary gas flow, and powder carrier gas flow. In-flight particle diameters, temperatures, and velocities were measured in various areas of the spray plume. Samples were produced for analysis of microstructures and properties. An empirical model was developed, relating the input parameters to the in-flight particle characteristics. Multi-dimensional numerical simulations of the plasma gas flow field and in-flight particles under different operating conditions were also performed. In addition to the parameters which were experimentally investigated, the effect of particle injection velocity was also considered. The simulation results were found to be in good general agreement with the experimental data

X-ray structural analysis of plasma sprayed europium oxide

Energy Technology Data Exchange (ETDEWEB)

Gorshkov, B.N.; Loskutov, V.S.; Gavrish, A.A.; Shakh, G.E.

1981-12-01

An X-ray structure microanalysis is made for europium oxide powder produced by sintering and plasmic spheroidization for plasma spraying. The technique of concern is shown not to alter chemical composition of the powder. It is stated that a rise in the plasma jet enthalpy while spraying does not result in dissociation of europium oxide and its interaction with the plasma flux. The coating (to 15.2 kWxs/g) is found to have only a high-temperature (monoclinic) europium oxide phase and there appears a low-temperature (cubic) phase with a subsequent increase in the enthalpy. The plasma jet enthalpy increasing the grain size and the crystal lattice c parameter of the sprayed europium oxide are shown to decrease; the a parameter reduces with an enthalpy growth to 16.2 kW s/g and then smoothly increases with the enthalpy further growth. It is noticed that the europium oxide coating does not interact with an aluminium D16 alloy substrate.

D. C. plasma-sprayed coatings of nano-structured alumina-titania-silica

International Nuclear Information System (INIS)

Jiang Xianliang

2002-01-01

nano-crystalline powders of ω(Al 2 O 3 ) = 95%, ω(TiO 2 ) = 3%, and ω(SiO 2 ) = 2%, were reprocessed into agglomerated particles for plasma spraying, by using consecutive steps of ball milling, slurry forming, spray drying, and heat treatment. D.C. plasma was used to spray the agglomerated nano-crystalline powders, and resultant coatings were deposited on the substrate of stainless steel. Scanning electron microscopy (SEM) was used to examine the morphology of the agglomerated powders and the cross section of the alumina-titania-silica coatings. Experimental results show that the agglomerated nano-crystalline particles are spherical, with a size from (10-90) μm. The flow ability of the nano-crystalline powders is greatly improved after the reprocessing. The coatings deposited by the plasma spraying are mainly of nano-structure. Unlike conventional plasma-sprayed coatings, no laminar layer could be found in the nano-structured coatings. Although the nano-structured coatings have a lower microhardness than conventional microstructured coatings, the toughness of the nano-structured ceramic coatings is significantly improved

Consolidation of tungsten disilicide by plasma spraying

Czech Academy of Sciences Publication Activity Database

Brožek, Vlastimil; Ctibor, Pavel; Matějíček, Jiří; Rohan, Pavel; Janča, J.

2007-01-01

Roč. 52, č. 3 (2007), s. 311-320 ISSN 0001-7043 R&D Projects: GA ČR(CZ) GA104/05/0540 Institutional research plan: CEZ:AV0Z20430508 Keywords : Water stabilized plasma * tungsten disilicide * plasma deposition * thermal spray coatings Subject RIV: JJ - Other Materials

Preparation and Characterization of Plasma-Sprayed Ultrafine Chromium Oxide Coatings

International Nuclear Information System (INIS)

Lin Feng; Jiang Xianliang; Yu Yueguang; Zeng Keli; Ren Xianjing; Li Zhenduo

2007-01-01

Ultrafine chromium oxide coatings were prepared by plasma spraying with ultrafine feedstock. Processing parameters of plasma spraying were optimized. Optical microscope (OM) was used to observe the microstructure of the ultrafine chromium oxide coatings. Scanning electron microscopy (SEM) was used to observe the morphology and particle size of ultrafine powder feedstock as well as to examine the microstructure of the chromium oxide coating. In addition, hardness and bonding strength of the ultrafine chromium oxide coatings were measured. The results showed that the optimized plasma spraying parameters were suitable for ultrafine chromium oxide coating and the properties and microstructure of the optimized ultrafine chromium oxide coating were superior compared to conventional chromium oxide wear resistant coatings

Thermal plasma spheroidization and spray deposition of barium titanate powder and characterization of the plasma sprayable powder

Energy Technology Data Exchange (ETDEWEB)

Pakseresht, A.H., E-mail: amirh_pak@yahoo.com [Department of Ceramics, Materials and Energy Research Center, P.O. Box 31787-316, Karaj (Iran, Islamic Republic of); Rahimipour, M.R. [Department of Ceramics, Materials and Energy Research Center, P.O. Box 31787-316, Karaj (Iran, Islamic Republic of); Vaezi, M.R. [Department of Nanotechnology and Advanced Materials, Materials and Energy Research Center, P.O. Box 31787-316, Karaj (Iran, Islamic Republic of); Salehi, M. [Department of Materials Engineering, Isfahan University of Technology, P.O. Box 84156-83111, Isfahan (Iran, Islamic Republic of)

2016-04-15

In this paper, atmospheric plasma spray method was used to produce dense plasma sprayable powder and thick barium titanate film. In this regard, the commercially feedstock powders were granulated and spheroidized by the organic binder and the thermal spray process, respectively. Scanning electron microscopy was used to investigate the microstructure of the produced powders and the final deposits. X-ray diffraction was also implemented to characterize phase of the sprayed powder. The results indicated that spheroidized powder had suitable flowability as well as high density. The micro-hardness of the film produced by the sprayed powders was higher than that of the film deposited by the irregular granules. Additionally, relative permittivity of the films was increased by decreasing the defects from 160 to 293 for film deposited using spheroidized powder. The reduction in the relative permittivity of deposits, in comparison with the bulk material, was due to the existence of common defects in the thermal spray process. - Highlights: • We prepare sprayable BaTiO{sub 3} powder with no or less inside voids for plasma spray application for first time. • The sprayable powder has good flow characteristics and high density. • Powder spheroidization via plasma spray improves the hardness and dielectric properties of the deposited film.

Thermal plasma spheroidization and spray deposition of barium titanate powder and characterization of the plasma sprayable powder

International Nuclear Information System (INIS)

Pakseresht, A.H.; Rahimipour, M.R.; Vaezi, M.R.; Salehi, M.

2016-01-01

In this paper, atmospheric plasma spray method was used to produce dense plasma sprayable powder and thick barium titanate film. In this regard, the commercially feedstock powders were granulated and spheroidized by the organic binder and the thermal spray process, respectively. Scanning electron microscopy was used to investigate the microstructure of the produced powders and the final deposits. X-ray diffraction was also implemented to characterize phase of the sprayed powder. The results indicated that spheroidized powder had suitable flowability as well as high density. The micro-hardness of the film produced by the sprayed powders was higher than that of the film deposited by the irregular granules. Additionally, relative permittivity of the films was increased by decreasing the defects from 160 to 293 for film deposited using spheroidized powder. The reduction in the relative permittivity of deposits, in comparison with the bulk material, was due to the existence of common defects in the thermal spray process. - Highlights: • We prepare sprayable BaTiO_3 powder with no or less inside voids for plasma spray application for first time. • The sprayable powder has good flow characteristics and high density. • Powder spheroidization via plasma spray improves the hardness and dielectric properties of the deposited film.

Study of technical, environmental and economic assessment of the process of waste gasification by plasma torch of PlascoEnergy Group - Report

International Nuclear Information System (INIS)

Kunegel, Andre

2009-10-01

This study aims at assessing technical, environmental and economic performance of a technology developed by PlascoEnergy Group in its application to French household and similar wastes, at analysing PlascoEnergy project for their processing in a city of southern France, and at providing a global analysis of the appropriateness of plasma torch technologies to the gasification of these wastes, of other wastes to be defined, biomass and so on. After a presentation of the technology and a reference to a demonstrator project in Ottawa, the report presents the PlascoEnergy Company, the French installation and its differences with the demonstration project. Based on documents provided by PlascoEnergy, it reports an analysis of various critical points (waste preparation, gasification, waste introduction, waste movements in the oven, hot air recovery, gasification performance, syngas processing, engines, valorisation and removal of solid residues). Performance of the Ottawa plant are presented and commented. The use of the plasma torch technology in waste processing is described

Evaluation of an inductively-coupled plasma with an extended-sleeve torch as an atomization cell for laser-excited fluorescence spectrometry.

Science.gov (United States)

Kosinski, M A; Uchida, H; Winefordner, J D

1983-05-01

An inductively-coupled plasma (ICP) with an extended-sleeve torch has been evaluated as an atomization cell for laser-excited fluorescence spectrometry. Limits of detection for 20 lines are given. The detection power is almost equivalent to that obtained by excitation with a hollow-cathode lamp. Interelement effects and spectral interferences are discussed.

Proceedings of the 16th symposium on plasma physics and technology

International Nuclear Information System (INIS)

1993-01-01

Among 53 papers collected in the proceedings, 28 papers deal with the theory and modelling (8 papers), experimental research (11 papers) and diagnostics of high-temperature plasmas. These include lower hybrid current drive in tokamaks, plasma heating by electron beams, laser plasma interaction and z-pinch experiments. In the diagnostic papers, attention is mostly paid to X-ray and optical plasma spectroscopy and to advanced Langmuir probe diagnostics. The remaining papers discuss low-temperature plasmas and their applications. In this group, 8 papers deal with low-pressure electric discharges, 5 papers with high-pressure arcs, glidarcs and plasma torches, and 12 papers with various plasma technology topics, such as thin film deposition, plasma spraying and plasma chemistry. (J.U.)

Ceramic plasma-sprayed coating of melting crucibles for casting metal fuel slugs

International Nuclear Information System (INIS)

Kim, Ki Hwan; Lee, Chong Tak; Lee, Chan Bock; Fielding, R.S.; Kennedy, J.R.

2013-01-01

Thermal cycling and melt reaction studies of ceramic coatings plasma-sprayed on Nb substrates were carried out to evaluate the performance of barrier coatings for metallic fuel casting applications. Thermal cycling tests of the ceramic plasma-sprayed coatings to 1450 °C showed that HfN, TiC, ZrC, and Y 2 O 3 coating had good cycling characteristics with few interconnected cracks even after 20 cycles. Interaction studies by 1550 °C melt dipping tests of the plasma-sprayed coatings also indicated that HfN and Y 2 O 3 do not form significant reaction layer between U–20 wt.% Zr melt and the coating layer. Plasma-sprayed Y 2 O 3 coating exhibited the most promising characteristics among HfN, TiC, ZrC, and Y 2 O 3 coating

ZrO2 coatings on stainless steel by aerosol thermal spraying

International Nuclear Information System (INIS)

Di Giampaolo, A.R.; Reveron, H.; Ruiz, H.; Poirier, T.; Lira, J.

1998-01-01

Zirconia coatings, with a wide range of thickness (1 to 80 μ) have been obtained by spraying a ZrO 2 sol with an oxyacetylenic flame, on stainless steel substrates. The sol was prepared by mixing Zr-n-propoxide and acetic acid in order to obtain a zirconium oxyacetate precipitate, which was filtrated, washed with 1-propanol, dryed and subjected to an hydrothermal treatment. A new sol-gel based ceramic deposition process , aerosol thermal spraying was developed based on previous thermal spray work. A compressed air spray gun was used to produce a fine aerosol flow which was injected in the flame of the thermal spray torch and deposited on polished and sand blasted substrates. This original technique allows simultaneous spraying, drying and partial sintering of the zirconia nanometric particles. The maximum working temperature necessary to yield a resistant coating is 1000 deg C. This method produced crack-free homogeneous layers of monoclinic ZrO 2 with good adhesion to the substrate and low porosity, as shown by X-ray diffraction and scanning electron microscopy. Oxidation test, carried out by heat treatments in air atmosphere at 800 deg C indicated good protection, mainly for low thickness coatings deposited in polished substrates. This original deposition technique offers several advantages when compared with classical thermal spraying techniques, such as plasma spraying. Copyright (1998) AD-TECH - International Foundation for the Advancement of Technology Ltd

3D-simulation of residual stresses in TBC plasma sprayed coating

International Nuclear Information System (INIS)

Kundas, S.; Kashko, T.; Hurevich, V.E.; Lugscheider, E.; Hayn, G. von; Ilyuschenko, A.

2001-01-01

Thermal barrier coatings (TBC) are used in gas turbine technology in order to protect against overheating of the nickel alloy turbine blades. This coatings allows to increase turbine inlet temperatures and improve their efficiency. Plasma spraying processes are widely used since several years in thermal barrier coating technology. Although the plasma spraying process of TBC's is largely successful, a fundamental understanding of the process parameters influencing the TBC microstructure and mechanical properties is necessary. But this investigation has received much less attention so they could lead to considerable advances in performance of plasma sprayed thermal barrier coatings. The main reason of this mate is difficulties in experimental investigation of high temperature and high velocity process. One of the most effective ways to accelerate the process optimization is the application of computer simulation for the modeling of plasma spraying. This enables the achievement of a maximum of information about the investigated process by carrying out a minimum number of experiments. The main problem of plasma spray TBC coatings is crack information during the deposition process and coating cooling. The reasons for this are quenched and residual stresses in the coating-substrate system, and peculiarities of TBC coating properties. The problem of deposition and solidification of plasma sprayed coatings have received little attention to date and remains one of the unintelligible parts of process. A fundamental understanding of heat transfer in the coating-substrate system and particles deformation processes are, however, critical for the prediction of the microstructural characteristics of the deposited coatings, the understanding of the mechanisms involved in formation of thermal stresses and defects (cracks, debonding etc.). (author)

Comparison of a high temperature torch integrated sample introduction system with a desolvation system for the analysis of microsamples through inductively coupled plasma mass spectrometry

Science.gov (United States)

Sánchez, Raquel; Cañabate, Águeda; Bresson, Carole; Chartier, Frédéric; Isnard, Hélène; Maestre, Salvador; Nonell, Anthony; Todolí, José-Luis

2017-03-01

This work describes for the first time the comparison of the analytical performances obtained with a high temperature torch integrated sample introduction system (hTISIS) against those found with a commercially available desolvation system (APEX) associated with inductively coupled plasma mass spectrometry (ICP-MS). A double pass spray chamber was taken as the reference system. Similar detection limits and sensitivities were obtained in continuous injection mode at low liquid flow rates for the APEX and hTISIS operating at high temperatures. In contrast, in the air-segmented injection mode, the detection limits obtained with hTISIS at high temperatures were up to 12 times lower than those found for the APEX. Regarding memory effects, wash out times were shorter in continuous mode and peaks were narrower in air segmented mode for the hTISIS as compared to the APEX. Non spectral interferences (matrix effects) were studied with 10% nitric acid, 2% methanol, for an ICP multielemental solution and a hydro-organic matrix containing 70% (v/v) acetonitrile in water, 15 mmol L- 1 ammonium acetate and 0.5% formic acid containing lanthanide complexes. In all the cases, matrix effects were less severe for the hTISIS operating at 200 °C and the APEX than for the double pass spray chamber. Finally, two spiked reference materials (sea water and Antartic krill) were analyzed. The hTISIS operating at 200 °C gave the best results compared to those obtained with the APEX and the double pass spray chamber. In conclusion, despite the simplicity of the hTISIS, it provided, at low liquid flow rates, results similar to or better than those obtained with the by other sample introduction systems.

Metallurgy and properties of plasma spray formed materials

Science.gov (United States)

Mckechnie, T. N.; Liaw, Y. K.; Zimmerman, F. R.; Poorman, R. M.

1992-01-01

Understanding the fundamental metallurgy of vacuum plasma spray formed materials is the key to enhancing and developing full material properties. Investigations have shown that the microstructure of plasma sprayed materials must evolve from a powder splat morphology to a recrystallized grain structure to assure high strength and ductility. A fully, or near fully, dense material that exhibits a powder splat morphology will perform as a brittle material compared to a recrystallized grain structure for the same amount of porosity. Metallurgy and material properties of nickel, iron, and copper base alloys will be presented and correlated to microstructure.

New generation of plasma-sprayed mullite coatings on silicon carbide

Science.gov (United States)

Lee, Kang N.; Miller, Robert A.; Jacobson, Nathan S.

1995-01-01

Mullite is promising as a protective coating for silicon-based ceramics in aggressive high-temperature environments. Conventionally plasma-sprayed mullite on SiC tends to crack and debond on thermal cycling. It is shown that this behavior is due to the presence of amorphous mullite in the conventionally sprayed mullite. Heating the SiC substrate during the plasma spraying eliminated the amorphous phase and produced coatings with dramatically improved properties. The new coating exhibits excellent adherence and crack resistance under thermal cycling between room temperature and 1000 to 1400 C. Preliminary tests showed good resistance to Na2CO3-induced hot corrosion.

Mechanical Properties of Plasma Sprayed Alumina Coatings

Czech Academy of Sciences Publication Activity Database

Kovářík, O.; Nohava, Jiří; Siegel, J.

2003-01-01

Roč. 48, č. 2 (2003), s. 129-145 ISSN 0001-7043 R&D Projects: GA ČR GA106/01/0094 Institutional research plan: CEZ:AV0Z2043910 Keywords : plasma sprayed alumina coatings, fatigue test, metalography, fractography, residual stress, microhardness, Young's modulus , four-point bending Subject RIV: BL - Plasma and Gas Discharge Physics

Vacuum-plasma-sprayed silicon coatings

International Nuclear Information System (INIS)

Varacalle, D.J. Jr.; Herman, H.; Bancke, G.A.; Burchell, T.D.; Romanoski, G.R.

1991-01-01

Vacuum plasma spraying produces well-bonded dense stress-free coatings for a variety of materials on a wide range of substrates. The process is used in many industries for the excellent wear, corrosion resistance and high temperature behavior of the fabricated coatings. In this study, silicon metal was deposited on graphite to study the feasibility of preventing corrosion and oxidation of graphite components for nuclear reactors. Operating parameters were varied in a Taguchi design of experiments to display the range of the plasma processing conditions and their effect on the measured coating characteristics. The coating attributes evaluated were thickness, porosity, microhardness and phase content. This paper discusses the influence of the processing parameters on as-sprayed coating qualities. The paper also discusses the effect of thermal cycling on silicon samples in an inert helium atmosphere. The diffraction spectrum for a sample that experienced a 1600degC temperature cycle indicated that more than 99% of the coating transformed to β-SiC. The silicon coatings protected the graphite substrates from oxidation in one experiment. (orig.)

Ultrasonic technique for measuring porosity of plasma-sprayed alumina coatings

Science.gov (United States)

Parthasarathi, S.; Tittmann, B. R.; Onesto, E. J.

1997-12-01

Porosity is an important factor in plasma-sprayed coatings, especially ceramic coatings. Excessive poros-ity can adversely affect the performance of the coated component in various ways. An ultrasonic nonde-structive measurement technique has been developed to measure porosity in plasma-sprayed alumina coatings. The technique is generic and can be extended to other ceramic coating systems. To test the tech-nique, freestanding alumina coatings with varying levels of porosity were fabricated via plasma spray. Samples with varying porosity, obtained through innovative fabrication techniques, were used to gener-ate a calibration curve. The ultrasonic velocity in the low-frequency range was found to be dependent on the density of freestanding coatings (measured via Archimedian techniques). This dependence is the basis of the development of a technique to measure the density of coatings.

Advanced Microstructural Study of Suspension Plasma Sprayed Hydroxyapatite Coatings

Science.gov (United States)

Podlesak, Harry; Pawlowski, Lech; D'Haese, Romain; Laureyns, Jacky; Lampke, Thomas; Bellayer, Severine

2010-03-01

Fine, home-synthesized, hydroxyapatite powder was formulated with water and alcohol to obtain a suspension used to plasma spray coatings onto a titanium substrate. The deposition process was optimized using statistical design of 2 n experiments with two variables: spray distance and electric power input to plasma. X-ray diffraction (XRD) was used to determine quantitatively the phase composition of obtained deposits. Raman microscopy and electron probe microanalysis (EPMA) enabled localization of the phases in different positions of the coating cross sections. Transmission electron microscopic (TEM) study associated with energy-dispersive x-ray spectroscopy (EDS) enabled visualization and analysis of a two-zone microstructure. One zone contained crystals of hydroxyapatite, tetracalcium phosphate, and a phase rich in calcium oxide. This zone included lamellas, usually observed in thermally sprayed coatings. The other zone contained fine hydroxyapatite grains that correspond to nanometric and submicrometric solids from the suspension that were agglomerated and sintered in the cold regions of plasma jet and on the substrate.

Particle melting and particle/plasma interactions in DC and RF plasmas: a modeling study. (Volumes I and II)

International Nuclear Information System (INIS)

Wei, D.Y.C.

1987-01-01

Integral process models were developed to predict particle melting in both DC and RF plasmas. Specifically, a numerical model has been developed to predict the temperature history of particles injected in a low pressure DC plasma jet. The temperature and velocity fields of the plasma jet are predicted as a free jet by solving the parabolized Navier-Stokes equations using a spatial marching scheme. Correction factors were introduced to take into account non continuum effects encountered in the low pressure environment. The plasma jet profiles as well as the particle/plasma interactions under different jet pressure ratios (from underexpanded to overexpanded) were investigated. The flow and temperature fields in the RF plasma torch are calculated using the axisymmetric Navier-Stokes equations based on the primitive variables, along with pseudo two-dimensional electromagnetic field equations. Particle trajectories and heat transfer characteristics in both DC and RF plasmas are calculated using predicted plasma jet profiles. Particle melting efficiencies in both DC and RF plasmas are evaluated and compared using model alloy systems. Based on the theoretical considerations, an alternative route of plasma spraying process (hybrid plasma spraying process) is proposed. An evaluation of particle melting in hybrid plasma jets had indicated that further improvement in deposit properties could be made

A study of the solid and gaseous products generated by a dc plasma torch under coal and steam injection

International Nuclear Information System (INIS)

Beuthe, T.G.; Chang, J.S.; Irons, G.A.; Lu, W.K.; Berezin, A.A.; Chu, E.Y.

1988-01-01

In this work, the solid and gaseous products generated by a DC plasma torch under simultaneous coal powder and supersaturated steam injection are examined. A range of steam (0.75[g/min]) and coal powder (0-10[g/min]) were injected into the hot argon plasma and the product gases were analyzed by gas chromatographic techniques, an optical multichannel analyzer and infrared CO and CO/sub 2/ analyzers. The solid product generated by the present process was analyzed using neutron activation analysis and scanning electron microscopy. Results indicate that the most common product constituents consisted of simple compounds such as carbon dioxide, carbon monoxide, hydrogen, oxygen and nitrogen. Detailed analysis using infra-red analyzers and gas chromatographic techniques showed that the product gas contained significant amounts of H/sub 2/(--2[%], CO(0.5-4.5[%]) and CO/sub 2/(0.5-1.0[%]) gases, where approximately 80 (%) was still argon gas. Evidence was found of slight amounts of OH, but no significant amount of CH/sub 2/ compounds were detected. The energy yields of the CO/sub 2/ and CO production rates were in the range of 4-10 and 5-25 [g/kWhr] respectively. The produced gas CO:CO/sub 2/ concentration ratio was approximately in the order of 10. Neutron activation analysis shows that the solid product generated in the present process is significantly different from the ash produced by a conventional coal fired furnace. The overall concentrations of trace oxides are significantly lower in the solid product than in conventional ash, tending to support the hypothesis that the solid product is a coke rather than an ash. The conditions in the plasma torch also seem to favour the removal of Ca, S and Si oxides from the coal. Downstream temperature analysis indicates the product gas can be heated from 600 to 1500(K) depending on the torch operating conditions and injectant flowrates

PLASMA SPRAYING OF REFRACTORY CERMETS BY THE WATER-STABILIZED SPRAY (WSP®) SYSTEM

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Brožek, V.; Cheong, D.-I.; Chráska, Pavel

2009-01-01

Roč. 54, č. 3 (2009), s. 241-253 ISSN 0001-7043 Institutional research plan: CEZ:AV0Z20430508 Keywords : Plasma spraying * cermet coatings * microhardness * zirconium carbide * tungsten Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass

Plasma-sprayed titanium coating to polyetheretherketone improves the bone-implant interface.

Science.gov (United States)

Walsh, William R; Bertollo, Nicky; Christou, Chrisopher; Schaffner, Dominik; Mobbs, Ralph J

2015-05-01

Rapid and stable fixation at the bone-implant interface would be regarded as one of the primary goals to achieve clinical efficacy, regardless of the surgical site. Although mechanical and physical properties of polyetheretherketone (PEEK) provide advantages for implant devices, the hydrophobic nature and the lack of direct bone contact remains a limitation. To examine the effects of a plasma-sprayed titanium coated PEEK on the mechanical and histologic properties at the bone-implant interface. A preclinical laboratory study. Polyetheretherketone and plasma-sprayed titanium coated PEEK implants (Ti-bond; Spinal Elements, Carlsbad, CA, USA) were placed in a line-to-line manner in cortical bone and in a press-fit manner in cancellous bone of adult sheep using an established ovine model. Shear strength was assessed in the cortical sites at 4 and 12 weeks, whereas histology was performed in cortical and cancellous sites at both time points. The titanium coating dramatically improved the shear strength at the bone-implant interface at 4 weeks and continued to improve with time compared with PEEK. Direct bone ongrowth in cancellous and cortical sites can be achieved using a plasma-sprayed titanium coating on PEEK. Direct bone to implant bonding can be achieved on PEEK in spite of its hydrophobic nature using a plasma-sprayed titanium coating. The plasma-sprayed titanium coating improved mechanical properties in the cortical sites and the histology in cortical and cancellous sites. Copyright © 2015 Elsevier Inc. All rights reserved.

Plasma transferred arc surface modification of atmospheric plasma sprayed ceramic coatings

Energy Technology Data Exchange (ETDEWEB)

Ulutan, Mustafa; Kilicay, Koray; Kaya, Esad; Bayar, Ismail [Dept. of Mechanical Engineering, Eskisehir Osmangazi University, Eskisehir (Turkmenistan)

2016-08-15

In this study, a 90MnCrV8 steel surface was coated with aluminum oxide and chromium oxide powders through the Atmospheric plasma spray (APS) and Plasma transferred arc (PTA) methods. The effects of PTA surface melting on the microstructure, hardness, and wear behavior were investigated. The microstructures of plasma-sprayed and modified layers were characterized by Optical microscopy (OM), Scanning electron microscopy (SEM) and Energy dispersive X-ray spectroscopy (EDS). The dry-sliding wear properties of the samples were determined through the ball-on-disk wear test method. Voids, cracks, and nonhomogeneous regions were observed in the microstructure of the APS ceramic-coated surface. These microstructure defects were eliminated by the PTA welding process. The microhardness of the samples was increased. Significant reductions in wear rate were observed after the PTA surface modification. The wear resistance of ceramic coatings increased 7 to 12 times compared to that of the substrate material.

Current transfer in dc non-transferred arc plasma torches

International Nuclear Information System (INIS)

Ghorui, S; Sahasrabudhe, S N; Das, A K

2010-01-01

Fundamentals of current transfer to the anodes in dc non-transferred arc plasma torches are investigated. Specially designed anodes made of three mutually isolated sections and external dc axial magnetic fields of various strengths are utilized to explore the conditions for different diffused and constricted attachments of the arc with the anode. A number of new facts are revealed in the exercise. Under constricted attachment, formation of arc root takes place. Spontaneous and magnetically induced movements of the arc root, their dependence on the arc current and the strength of the external magnetic field, most probable arc root velocity, variation of the root velocity with strength of the applied magnetic field, the effect of swirl on the rotational speed of the arc root are some of the important features investigated. Two new techniques are introduced: one for measurement of the arc root diameter and the other for determination of the negative electric field in the boundary layer over the anode. While the first one exploits the rigid column behaviour of the arcs, the second one utilizes the shooting back of the residual electrons over an arc spot. Sample calculations are provided.

Numerical Coupling of the Particulate Phase to the Plasma Phase in Modeling of Multi-Arc Plasma Spraying

International Nuclear Information System (INIS)

Bobzin, K.; Öte, M.

2017-01-01

Inherent to Euler-Lagrange formulation, which can be used in order to describe the particle behavior in plasma spraying, particle in-flight characteristics are determined by calculating the impulse, heat and mass transfer between the plasma jet and individual powder particles. Based on the assumption that the influence of the particulate phase on the fluid phase is insignificant, impulse, heat and mass transfer from particles to the plasma jet can be neglected using the so-called numerical approach of “one-way coupling”. On the other hand, so-called “two-way coupling” considers the two-sided transfer between both phases. The former is a common simplification used in the literature to describe the plasma-particle interaction in thermal spraying. This study focuses on the significance of this simplification on the calculated results and shows that the use of this simplification leads to significant errors in calculated plasma and particle in-flight characteristics in three-cathode plasma spraying process. (paper)

Sensing Properties of Multiwalled Carbon Nanotubes Grown in MW Plasma Torch: Electronic and Electrochemical Behavior, Gas Sensing, Field Emission, IR Absorption

Directory of Open Access Journals (Sweden)

Petra Majzlíková

2015-01-01

Full Text Available Vertically aligned multi-walled carbon nanotubes (VA-MWCNTs with an average diameter below 80 nm and a thickness of the uniform VA-MWCNT layer of about 16 µm were grown in microwave plasma torch and tested for selected functional properties. IR absorption important for a construction of bolometers was studied by Fourier transform infrared spectroscopy. Basic electrochemical characterization was performed by cyclic voltammetry. Comparing the obtained results with the standard or MWCNT‑modified screen-printed electrodes, the prepared VA-MWCNT electrodes indicated their high potential for the construction of electrochemical sensors. Resistive CNT gas sensor revealed a good sensitivity to ammonia taking into account room temperature operation. Field emission detected from CNTs was suitable for the pressure sensing application based on the measurement of emission current in the diode structure with bending diaphragm. The advantages of microwave plasma torch growth of CNTs, i.e., fast processing and versatility of the process, can be therefore fully exploited for the integration of surface-bound grown CNTs into various sensing structures.

Suspension plasma sprayed composite coating using amorphous powder feedstock

International Nuclear Information System (INIS)

Chen Dianying; Jordan, Eric H.; Gell, Maurice

2009-01-01

Al 2 O 3 -ZrO 2 composite coatings were deposited by the suspension plasma spray process using molecularly mixed amorphous powders. X-ray diffraction (XRD) analysis shows that the as-sprayed coating is composed of α-Al 2 O 3 and tetragonal ZrO 2 phases with grain sizes of 26 nm and 18 nm, respectively. The as-sprayed coating has 93% density with a hardness of 9.9 GPa. Heat treatment of the as-sprayed coating reveals that the Al 2 O 3 and ZrO 2 phases are homogeneously distributed in the composite coating

DEVELOPMENT OF WEAR RESISTANT COATINGS FORMED BY PLASMA SPRAYING OF ALLOY Ni–Fe–Cr–Si–B–C SYSTEM REINFORCED WITH CERAMICS Al2O3

Directory of Open Access Journals (Sweden)

A. S. Kalinichenko

2016-01-01

Full Text Available . Creating a functionally oriented, including nanostructured, anti-friction materials and coatings with qualitatively new complex of service properties is an important scientific and practical problem. In particular, for the cable industry it is urgent task of ensuring the high performance properties of fast deteriorating stretching and supporting rollers. Working surfaces of these parts operate under practically dry friction conditions with constantly updated material of stretching wire. Plasma spraying is one of the widely used methods of surface engineering to create wear resistant coatings and which is characterized with process flexibility and the ability to create coatings using various materials and alloys including composite ones. The installation UPU-3D with the PP-25 plasma torch was used for plasma spraying. The thickness of the sprayed layer was 0.8–1.1 mm. As a material for the deposition of composite coatings a powder mixture of self-fluxing nickel alloy PG-HN80SR4 (system Ni–Fe–Cr–Si–B–C and a neutral oxide ceramics Al2O3 was used. The amount of ceramics varied from 15 to 33 %. This ceramic oxide was selected due to the desire to reduce coatings’ costs while providing high durability. Carried out phase and microstructural studies have shown when ceramics was added in an amount more than 20 % a formation of conglomerates formed by not melted alumina particles often was observed. These conglomerates serve as crack formation centers in the coating. The phase composition of the coatings practically does not depend on the content of ceramics compounds. Tribological tests have shown that the best results were obtained when the content of the oxide ceramic in the coating was in the range from 15 to 20 %.

Current Progress in Solution Precursor Plasma Spraying of Cermets: A Review

Directory of Open Access Journals (Sweden)

Romnick Unabia

2018-06-01

Full Text Available Ceramic and metal composites, known also as cermets, may considerably improve many material properties with regards to that of initial components. Hence, cermets are frequently applied in many technological fields. Among many processes which can be employed for cermet manufacturing, thermal spraying is one of the most frequently used. Conventional plasma spraying of powders is a popular and cost-effective manufacturing process. One of its most recent innovations, called solution precursor plasma spraying (SPPS, is an emerging coating deposition method which uses homogeneously mixed solution precursors as a feedstock. The technique enables a single-step deposition avoiding the powder preparation procedures. The nanostructured coatings developed by SPPS increasingly find a place in the field of surface engineering. The present review shows the recent progress in the fabrication of cermets using SPPS. The influence of starting solution precursors, such as their chemistry, concentration, and solvents used, to the micro-structural characteristics of cermet coatings is discussed. The effect of the operational plasma spray process parameters such as solution injection mode to the deposition process and coatings’ microstructure is also presented. Moreover, the advantages of the SPPS process and its drawbacks compared to the conventional powder plasma spraying process are discussed. Finally, some applications of SPPS cermet coatings are presented to understand the potential of the process.

Characterization of metal-supported axial injection plasma sprayed solid oxide fuel cells with aqueous suspension plasma sprayed electrolyte layers

Science.gov (United States)

Waldbillig, D.; Kesler, O.

A method for manufacturing metal-supported SOFCs with atmospheric plasma spraying (APS) is presented, making use of aqueous suspension feedstock for the electrolyte layer and dry powder feedstock for the anode and cathode layers. The cathode layer was deposited first directly onto a metal support, in order to minimize contact resistance, and to allow the introduction of added porosity. The electrolyte layers produced by suspension plasma spraying (SPS) were characterized in terms of thickness, permeability, and microstructure, and the impact of substrate morphology on electrolyte properties was investigated. Fuel cells produced by APS were electrochemically tested at temperatures ranging from 650 to 750 °C. The substrate morphology had little effect on open circuit voltage, but substrates with finer porosity resulted in lower kinetic losses in the fuel cell polarization.

Characterization of metal-supported axial injection plasma sprayed solid oxide fuel cells with aqueous suspension plasma sprayed electrolyte layers

Energy Technology Data Exchange (ETDEWEB)

Waldbillig, D. [University of British Columbia, Department of Materials Engineering, 309-6350 Stores Road, Vancouver, BC (Canada); Kesler, O. [University of Toronto, Department of Mechanical and Industrial Engineering, 5 King' s College Road, Toronto, Ontario (Canada)

2009-06-15

A method for manufacturing metal-supported SOFCs with atmospheric plasma spraying (APS) is presented, making use of aqueous suspension feedstock for the electrolyte layer and dry powder feedstock for the anode and cathode layers. The cathode layer was deposited first directly onto a metal support, in order to minimize contact resistance, and to allow the introduction of added porosity. The electrolyte layers produced by suspension plasma spraying (SPS) were characterized in terms of thickness, permeability, and microstructure, and the impact of substrate morphology on electrolyte properties was investigated. Fuel cells produced by APS were electrochemically tested at temperatures ranging from 650 to 750 C. The substrate morphology had little effect on open circuit voltage, but substrates with finer porosity resulted in lower kinetic losses in the fuel cell polarization. (author)

Development of Process for Plasma Spray:Case Study for Molybdenum

Czech Academy of Sciences Publication Activity Database

Sampath, S.; Jiang, X.; Kulkarni, A.; Matějíček, Jiří; Gilmore, D. L.; Neiser, R. A.

2003-01-01

Roč. 348, 1-2 (2003), s. 54-66 ISSN 0921-5093 Grant - others:NSF(US) DMR9632570 Institutional research plan: CEZ:AV0Z2043910 Keywords : process maps, plasma spray, thermal spray Subject RIV: JG - Metallurgy Impact factor: 1.365, year: 2003

Very low pressure plasma sprayed yttria-stabilized zirconia coating using a low-energy plasma gun

International Nuclear Information System (INIS)

Zhu, Lin; Zhang, Nannan; Bolot, Rodolphe; Planche, Marie-Pierre; Liao, Hanlin; Coddet, Christian

2011-01-01

In the present study, a more economical low-energy plasma source was used to perform a very low pressure plasma-spray (VLPPS) process. The plasma-jet properties were analyzed by means of optical emission spectroscopy (OES). Moreover, yttria-stabilized zirconia coating (YSZ) was elaborated by a F100 low-power plasma gun under working pressure of 1 mbar, and the substrate specimens were partially shadowed by a baffle-plate during plasma spraying for obtaining different coating microstructures. Based on the SEM observation, a column-like grain coating was deposited by pure vapor deposition at the shadowed region, whereas, in the unshadowed region, the coating exhibited a binary microstructure which was formed by a mixed deposition of melted particles and evaporated particles. The mechanical properties of the coating were also well under investigation. (orig.)

Synthesis and Characterization of Calcium Phosphate Powders for Biomedical Applications by Plasma Spray Coating

OpenAIRE

Sasidharan Pillai, Rahul

2015-01-01

This PhD work mainly focus on the synthesis and characterization of calcium phosphate powders for plasma spray coating. The preparation of high temperature phase stabilized βTCP and HA/βTCP powders for plasma spray coating applications has been the topic of investigation. Nowadays plasma sprayed coatings are widely used for biomedical applications especially in the dental and orthopaedic implantation field. Previously Ti based alloys were widely used for the orthopaedic and dental implant ap...

Dismantling of JPDR reactor internals by underwater plasma arc cutting technique using robotic manipulator

International Nuclear Information System (INIS)

Yokota, M.

1988-01-01

The actual dismantling of JPDR started on December 4, 1986. As of now, equipment that surrounds the reactor has mostly been removed to provide working space in reactor containment prior to the dismantling of reactor internals. Some reactor internals have been successfully dismantled using the underwater arc cutting system with a robotic manipulator during the period of January to March 1988. The cutting system is composed of an underwater plasma arc cutting device and a robotic manipulator. The cut off reactor internals were core spray block, feedwater sparger and stabilizers for fuel upper grid tube. The plasma arc cutting device was developed to dismantle the reactor internals underwater. It mainly consists of a plasma torch, power and gas supply systems for the torch, and by-product treatment systems. It has the cutting ability of 130 mm thickness stainless steel underwater. The robotic manipulator has seven degrees of freedom of movement, enabling it to move in almost the same way as the arm of a human being. The arm of the robot is mounted on a supporting device which is suspended by three chains from the support structure set on a service floor. A plasma torch is griped by the robotic hand; its position to the structure to be cut is controlled from a remote control room, about 100 meters outside the reactor containment

Aligned, plasma sprayed SmCo5 deposits

International Nuclear Information System (INIS)

Kumar, K.; Das, D.

1986-01-01

Highly aligned SmCo 5 deposits were produced using plasma spraying. c-axis alignment, normal to the plane of the deposit, was achieved by depositing the Sm-Co alloys on steel substrates maintained at high temperatures. The substrates were heated by the plasma flame to obtain the high temperatures. The attainment of a range of substrate temperatures was made possible through control over the geometry of the substrate

Dielectric properties of plasma sprayed silicates

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Sedláček, J.; Neufuss, Karel; Dubský, Jiří; Chráska, Pavel

-, č. 31 (2005), s. 315-321 ISSN 0272-8842 R&D Projects: GA ČR(CZ) GA202/03/0708 Institutional research plan: CEZ:AV0Z20430508 Keywords : Optical microscopy * electrical properties * silicates * insulators * plasma spraying Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 0.702, year: 2005

Inductively coupled plasma torch efficiency at atmospheric pressure for organo-chlorine liquid waste removal: Chloroform destruction in oxidative conditions

Energy Technology Data Exchange (ETDEWEB)

Kamgang-Youbi, Georges, E-mail: kamyougeo@yahoo.fr [French Atomic Commission-CEA, Marcoule-DTCD/SCDV/LPIC, BP 17171, 30207 Bagnols-Sur-Cèze Cedex (France); Department of Inorganic Chemistry, The University of Yaounde I, P.O Box, 812 Yaounde (Cameroon); Poizot, Karine; Lemont, Florent [French Atomic Commission-CEA, Marcoule-DTCD/SCDV/LPIC, BP 17171, 30207 Bagnols-Sur-Cèze Cedex (France)

2013-01-15

Highlights: ► Inductively plasma torch is used for the decomposition of organochlorine molecule. ► We examine the impact of liquid water substitution by oxygen gas as oxidant. ► Complete and safe decomposition is achieved with the presence of oxygen. ► The energy efficiency and capabilities of process are better with O{sub 2} than H{sub 2}O. -- Abstract: The performance of a plasma reactor for the degradation of chlorinated hydrocarbon waste is reported. Chloroform was used as a target for a recently patented destruction process based using an inductive plasma torch. Liquid waste was directly injected axially into the argon plasma with a supplied power of ∼4 kW in the presence of oxygen as oxidant and carrier gas. Decomposition was performed at CHCl{sub 3} feed rates up to 400 g h{sup −1} with different oxygen/waste molar ratios, chloroform destruction was obtained with at least 99% efficiency and the energy efficiency reached 100 g kWh{sup −1}. The conversion end products were identified and assayed by online FTIR spectroscopy (CO{sub 2}, HCl and H{sub 2}O) and redox titration (Cl{sub 2}). Considering phosgene as representative of toxic compounds, only very small quantities of toxics were released (<1 g h{sup −1}) even with high waste feed rates. The experimental results were very close to the equilibrium composition predicted by thermodynamic calculations. At the bottom of the reactor, the chlorinated acids were successfully trapped in a scrubber and transformed into mineral salts, hence, only CO{sub 2} and H{sub 2}O have been found in the final off-gases composition.

Corrosion performance of atmospheric plasma sprayed alumina coatings on AZ31B magnesium alloy under immersion environment

OpenAIRE

D. Thirumalaikumarasamy; K. Shanmugam; V. Balasubramanian

2014-01-01

Plasma sprayed ceramic coatings are successfully used in many industrial applications, where high wear and corrosion resistance with thermal insulation are required. The alumina powders were plasma sprayed on AZ31B magnesium alloy with three different plasma spraying parameters. In the present work, the influence of plasma spray parameters on the corrosion behavior of the coatings was investigated. The corrosion behavior of the coated samples was evaluated by immersion corrosion test in 3.5 w...

HfC plasma coating of C/C composites

International Nuclear Information System (INIS)

Boncoeur, M.; Schnedecker, G.; Lulewicz, J.D.

1992-01-01

The surface properties of C/C composites such as hardness and corrosion or erosion resistance can be modified by a ceramic coating applied by plasma torch. The technique of plasma spraying in controlled temperature and atmosphere, that was developed and patented by the CEA, makes it possible to apply coatings to the majority of metals and ceramics without affecting the characteristics of the composite. An example of hard deposit of HfC on a C/C composite is described. The characteristics of the deposit and of the bonding with the C/C composite were studied before and after a heat treatment under vacuum for 2 hours at 1000 C. 2 refs

Effect of laser induced plasma ignition timing and location on Diesel spray combustion

International Nuclear Information System (INIS)

Pastor, José V.; García-Oliver, José M.; García, Antonio; Pinotti, Mattia

2017-01-01

Highlights: • Laser plasma ignition is applied to a direct injection Diesel spray, compared with auto-ignition. • Critical local fuel/air ratio for LIP provoked ignition is obtained. • The LIP system is able to stabilize Diesel combustion compared to auto-ignition cases. • Varying LIP position along spray axis directly affects Ignition-delay. • Premixed combustion is reduced both by varying position and delay of the LIP ignition system. - Abstract: An experimental study about the influence of the local conditions at the ignition location on combustion development of a direct injection spray is carried out in an optical engine. A laser induced plasma ignition system has been used to force the spray ignition, allowing comparison of combustion’s evolution and stability with the case of conventional autoignition on the Diesel fuel in terms of ignition delay, rate of heat release, spray penetration and soot location evolution. The local equivalence ratio variation along the spray axis during the injection process was determined with a 1D spray model, previously calibrated and validated. Upper equivalence ratios limits for the ignition event of a direct injected Diesel spray, both in terms of ignition success possibilities and stability of the phenomena, could been determined thanks to application of the laser plasma ignition system. In all laser plasma induced ignition cases, heat release was found to be higher than for the autoignition reference cases, and it was found to be linked to a decrease of ignition delay, with the premixed peak in the rate of heat release curve progressively disappearing as the ignition delay time gets shorter. Ignition delay has been analyzed as a function of the laser position, too. It was found that ignition delay increases for plasma positions closer to the nozzle, indicating that the amount of energy introduced by the laser induced plasma is not the only parameter affecting combustion initiation, but local equivalence ratio

Dielectric and mechanical properties of plasma-sprayed olivine

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Neufuss, Karel; Pala, Zdeněk; Kotlan, Jiří; Soumar, J.

2015-01-01

Roč. 67, č. 2 (2015), s. 600-616 ISSN 1221-1451. [International Conference on Plasma Physics and Applications/16./. Magurele, Bucharest, 20.06.2013-25.06.2013] Institutional support: RVO:61389021 Keywords : olivine * plasma spraying * dielectric properties Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 1.367, year: 2015 www.infim.ro/rrp

The spray-drying process is sufficient to inactivate infectious porcine epidemic diarrhea virus in plasma.

Science.gov (United States)

Gerber, Priscilla F; Xiao, Chao-Ting; Chen, Qi; Zhang, Jianqiang; Halbur, Patrick G; Opriessnig, Tanja

2014-11-07

Porcine epidemic diarrhea virus (PEDV) is considered an emergent pathogen associated with high economic losses in many pig rearing areas. Recently it has been suggested that PEDV could be transmitted to naïve pig populations through inclusion of spray-dried porcine plasma (SDPP) into the nursery diet which led to a ban of SDPP in several areas in North America and Europe. To determine the effect of spray-drying on PEDV infectivity, 3-week-old pigs were intragastrically inoculated with (1) raw porcine plasma spiked with PEDV (RAW-PEDV-CONTROL), (2) porcine plasma spiked with PEDV and then spray dried (SD-PEDV-CONTROL), (3) raw plasma from PEDV infected pigs (RAW-SICK), (4) spray-dried plasma from PEDV infected pigs (SD-SICK), or (5) spray-dried plasma from PEDV negative pigs (SD-NEG-CONTROL). For the spray-drying process, a tabletop spray-dryer with industry-like settings for inlet and outlet temperatures was used. In the RAW-PEDV-CONTROL group, PEDV RNA was present in feces at day post infection (dpi) 3 and the pigs seroconverted by dpi 14. In contrast, PEDV RNA in feces was not detected in any of the pigs in the other groups including the SD-PEDV-CONTROL group and none of the pigs had seroconverted by termination of the project at dpi 28. This work provides direct evidence that the experimental spray-drying process used in this study was effective in inactivating infectious PEDV in the plasma. Additionally, plasma collected from PEDV infected pigs at peak disease did not contain infectious PEDV. These findings suggest that the risk for PEDV transmission through commercially produced SDPP is minimal. Copyright © 2014 Elsevier B.V. All rights reserved.

Characterization of plasma sprayed beryllium ITER first wall mockups

Energy Technology Data Exchange (ETDEWEB)

Castro, R.G.; Vaidya, R.U.; Hollis, K.J. [Los Alamos National Lab., NM (United States). Material Science and Technology Div.

1998-01-01

ITER first wall beryllium mockups, which were fabricated by vacuum plasma spraying the beryllium armor, have survived 3000 thermal fatigue cycles at 1 MW/m{sup 2} without damage during high heat flux testing at the Plasma Materials Test Facility at Sandia National Laboratory in New Mexico. The thermal and mechanical properties of the plasma sprayed beryllium armor have been characterized. Results are reported on the chemical composition of the beryllium armor in the as-deposited condition, the through thickness and normal to the through thickness thermal conductivity and thermal expansion, the four-point bend flexure strength and edge-notch fracture toughness of the beryllium armor, the bond strength between the beryllium armor and the underlying heat sink material, and ultrasonic C-scans of the Be/heat sink interface. (author)

Characterization of Plasma Sprayed Beryllium ITER First Wall Mockups

International Nuclear Information System (INIS)

Castro, Richard G.; Vaidya, Rajendra U.; Hollis, Kendall J.

1997-10-01

ITER first wall beryllium mockups, which were fabricated by vacuum plasma spraying the beryllium armor, have survived 3000 thermal fatigue cycles at 1 MW/sq m without damage during high heat flux testing at the Plasma Materials Test Facility at Sandia National Laboratory in New Mexico. The thermal and mechanical properties of the plasma sprayed beryllium armor have been characterized. Results are reported on the chemical composition of the beryllium armor in the as-deposited condition, the through thickness and normal to the through thickness thermal conductivity and thermal expansion, the four-point bend flexure strength and edge-notch fracture toughness of the beryllium armor, the bond strength between the beryllium armor and the underlying heat sink material, and ultrasonic C-scans of the Be/heat sink interface

Comparison of W–TiC composite coatings fabricated by atmospheric plasma spraying and supersonic atmospheric plasma spraying

International Nuclear Information System (INIS)

Hou, Qing Yu; Luo, Lai Ma; Huang, Zhen Yi; Wang, Ping; Ding, Ting Ting; Wu, Yu Cheng

2016-01-01

Highlights: • W–TiC composite coatings were fabricated by APS and SAPS technologies. • TiC had filling effect on pores and coating/fixing effect on un-melted particles. • Porosity and oxygen content in SAPS coating were lower than that in APS coating. • Thermal conductivity of SAPS coating was higher than that of APS coating. • SAPS coating has better ability to resist to elastic fracture than APS coating does. - Abstract: Tungsten coatings with 1.5 wt.% TiC (W/TiC) were fabricated by atmospheric plasma spraying (APS) and supersonic atmospheric plasma spraying (SAPS) techniques, respectively. The results showed that the typical lamellar structure of plasma spraying and columnar crystalline grains formed in the coatings. Pores located mainly at lamellar gaps in association with oxidation were also observed. TiC phase, distributed at lamellar gaps filled the gaps; and that distributed around un-melted tungsten particles and splashed debris coated the particles or debris that were linked with the TiC at lamellar gaps. The coating and linking of the retained TiC phase prevented the tungsten particles to come off from the coatings. The porosity and the oxygen content of the SAPS-W/TiC were lower than those of the APS-W/TiC coating. The mechanical response of the coatings was strongly dependent on the H/E* ratio (H and E* are the hardness and effective Young’s modulus, respectively). The SAPS-W/TiC coating with a higher H/E* ratio had a better ability to resist to elastic fracture and better fracture toughness as compared with the APS-W/TiC coating with a smaller H/E* ratio. The thermal conductivity of the SAPS-W/TiC coating was greater than that of the APS-W/TiC coating.

Plasma sprayed and electrospark deposited zirconium metal diffusion barrier coatings

International Nuclear Information System (INIS)

Hollis, Kendall J.; Pena, Maria I.

2010-01-01

Zirconium metal coatings applied by plasma spraying and electrospark deposition (ESD) have been investigated for use as diffusion barrier coatings on low enrichment uranium fuel for research nuclear reactors. The coatings have been applied to both stainless steel as a surrogate and to simulated nuclear fuel uranium-molybdenum alloy substrates. Deposition parameter development accompanied by coating characterization has been performed. The structure of the plasma sprayed coating was shown to vary with transferred arc current during deposition. The structure of ESD coatings was shown to vary with the capacitance of the deposition equipment.

Gaseous material capacity of open plasma jet in plasma spray-physical vapor deposition process

Science.gov (United States)

Liu, Mei-Jun; Zhang, Meng; Zhang, Qiang; Yang, Guan-Jun; Li, Cheng-Xin; Li, Chang-Jiu

2018-01-01

Plasma spray-physical vapor deposition (PS-PVD) process, emerging as a highly efficient hybrid approach, is based on two powerful technologies of both plasma spray and physical vapor deposition. The maximum production rate is affected by the material feed rate apparently, but it is determined by the material vapor capacity of transporting plasma actually and essentially. In order to realize high production rate, the gaseous material capacity of plasma jet must be fundamentally understood. In this study, the thermal characteristics of plasma were measured by optical emission spectrometry. The results show that the open plasma jet is in the local thermal equilibrium due to a typical electron number density from 2.1 × 1015 to 3.1 × 1015 cm-3. In this condition, the temperature of gaseous zirconia can be equal to the plasma temperature. A model was developed to obtain the vapor pressure of gaseous ZrO2 molecules as a two dimensional map of jet axis and radial position corresponding to different average plasma temperatures. The overall gaseous material capacity of open plasma jet, take zirconia for example, was further established. This approach on evaluating material capacity in plasma jet would shed light on the process optimization towards both depositing columnar coating and a high production rate of PS-PVD.

Erosion protection of carbon-epoxy composites by plasma-sprayed coatings

International Nuclear Information System (INIS)

Alonso, F.; Fagoaga, I.; Oregui, P.

1991-01-01

This paper deals with the production of plasma-sprayed erosion-resistant coatings on carbon-fibre - epoxy composites, and the study of their erosion behaviour. The heat sensitivity of the composite substrate requires a specific spraying procedure in order to avoid its degradation. In addition, several bonding layers were studied to allow spraying of the protective coatings. Two different functional coatings were sprayed onto an aluminium-glass bonding layer, a WC-12Co cermet and an Al 2 O 3 ceramic oxide. The microstructure and properties of these coatings were studied and their erosion behaviour determined experimentally in an erosion-testing device. (orig.)

Plasma Sprayed Tungsten-based Coatings and their Usage in Edge Plasma Region of Tokamaks

Czech Academy of Sciences Publication Activity Database

Matějíček, Jiří; Weinzettl, Vladimír; Dufková, Edita; Piffl, Vojtěch; Peřina, Vratislav

2006-01-01

Roč. 51, č. 2 (2006), s. 179-191 ISSN 0001-7043 Grant - others:Evropská unie EFDA Task TW-5-TVM-PSW (EU – Euratom) Institutional research plan: CEZ:AV0Z20430508; CEZ:AV0Z10480505 Keywords : plasma sprayed coatings * fusion * plasma facing components * tungsten * tokamak Subject RIV: BL - Plasma and Gas Discharge Physics

Spectroscopic diagnostics of industrial plasmas

International Nuclear Information System (INIS)

Joshi, N.K.

2004-01-01

Plasmas play key role in modern industry and are being used for processing micro electronic circuits to the destruction of toxic waste. Characterization of industrial plasmas which includes both 'thermal plasmas' and non-equilibrium plasmas or 'cold plasmas' in industrial environment offers quite a challenge. Numerous diagnostic techniques have been developed for the measurement of these partially ionized plasma and/or particulate parameters. The 'simple' non-invasive spectroscopic methods for characterization of industrial plasmas will be discussed in detail in this paper. The excitation temperature in thermal (DC/RF) plasma jets has been determined using atomic Boltzmann technique. The central axis temperature of thermal plasma jets in a spray torch can be determined using modified atomic Boltzmann technique with out using Abel inversion. The Stark broadening of H β and Ar-I (430 nm) lines have been used to determine the electron number density in thermal plasma jets. In low-pressure non-equilibrium argon plasma, electron temperature has been measured using the Corona model from the ratio of line intensities of atomic and ionic transitions. (author)

The development of beryllium plasma spray technology for the International Thermonuclear Experimental Reactor (ITER)

International Nuclear Information System (INIS)

Castro, R.G.; Elliott, K.E.; Hollis, K.J.; Watson, R.D.

1999-01-01

Over the past five years, four international parties, which include the European Communities, Japan, the Russian Federation and the United States, have been collaborating on the design and development of the International Thermonuclear Experimental Reactor (ITER), the next generation magnetic fusion energy device. During the ITER Engineering Design Activity (EDA), beryllium plasma spray technology was investigated by Los Alamos National Laboratory as a method for fabricating and repairing and the beryllium first wall surface of the ITER tokamak. Significant progress has been made in developing beryllium plasma spraying technology for this application. Information will be presented on the research performed to improve the thermal properties of plasma sprayed beryllium coatings and a method that was developed for cleaning and preparing the surface of beryllium prior to depositing plasma sprayed beryllium coatings. Results of high heat flux testing of the beryllium coatings using electron beam simulated ITER conditions will also be presented

Simple microwave plasma source at atmospheric pressure

International Nuclear Information System (INIS)

Kim, Jeong H.; Hong, Yong C.; Kim, Hyoung S.; Uhm, Han S.

2003-01-01

We have developed a thermal plasma source operating without electrodes. One electrodeless torch is the microwave plasma-torch, which can produce plasmas in large quantities. We can generate plasma at an atmospheric pressure by marking use of the same magnetrons used as commercial microwave ovens. Most of the magnetrons are operated at the frequency of 2.45 GHz; the magnetron power microwave is about 1kW. Electromagnetic waves from the magnetrons propagate through a shorted waveguide. Plasma was generated under a resonant condition, by an auxiliary ignition system. The plasma is stabilized by vortex stabilization. Also, a high-power and high-efficiency microwave plasma-torch has been operated in air by combining two microwave plasma sources with 1kW, 2.45 GHz. They are arranged in series to generate a high-power plasma flame. The second torch adds all its power to the plasma flame of the first torch. Basically, electromagnetic waves in the waveguide were studied by a High Frequency Structure Simulator (HFSS) code and preliminary experiments were conducted

Plasma spraying of refractory metals and refractory hard materials. State of the art

International Nuclear Information System (INIS)

Eschnauer, H.; Lugscheider, E.; Jaeger, D.

1989-01-01

Suitable spraying processes for manufacturing refractory metals, refractory hard materials as well as spray materials with refractory components are the VPS- and IPS-spraying techniques. The advantages of these special spraying process variations are described. The reactive spraying materials are systematically organized. The characteristical properties used in purpose of improving the substrate surfaces are explained. Finally some examples of the latest results of research concerning plasma spraying of reactive materials are shown. 16 refs., 10 figs. (Author)

Plasma sprayed alumina coatings for radiation detector development

Indian Academy of Sciences (India)

A mechanical as well as metallurgical bonding is necessary. 3. Applications ... Here the feasibility of using metallic components that were plasma spray- ... To study the electrical insulation, integrity of ceramic coating etc, tests were carried out.

Calcium titanate (CaTiO{sub 3}) dielectrics prepared by plasma spray and post-deposition thermal treatment

Energy Technology Data Exchange (ETDEWEB)

Ctibor, Pavel [Materials Engineering Department, Institute of Plasma Physics ASCR, v.v.i., Za Slovankou 3, Prague 8 (Czech Republic); Kotlan, Jiri, E-mail: kotlan@ipp.cas.cz [Materials Engineering Department, Institute of Plasma Physics ASCR, v.v.i., Za Slovankou 3, Prague 8 (Czech Republic); Department of Electrotechnology, Faculty of Electrical Engineering, Czech Technical University in Prague, Technicka 2, Prague 6 (Czech Republic); Pala, Zdenek [Materials Engineering Department, Institute of Plasma Physics ASCR, v.v.i., Za Slovankou 3, Prague 8 (Czech Republic); Sedlacek, Josef [Department of Electrotechnology, Faculty of Electrical Engineering, Czech Technical University in Prague, Technicka 2, Prague 6 (Czech Republic); Hajkova, Zuzana; Grygar, Tomas Matys [Institute of Inorganic Chemistry ASCR, v.v.i., Husinec-Rez 1001, Rez (Czech Republic)

2015-12-15

Highlights: • Calcium titanate was sprayed by two different plasma spray systems. • Significant improvement of dielectric properties after annealing was observed. • Calcium titanate self-supporting parts can be fabricated by plasma spraying. - Abstract: This paper studies calcium titanate (CaTiO{sub 3}) dielectrics prepared by plasma spray technology. A water stabilized plasma gun (WSP) as well as a widely used gas stabilized plasma gun (GSP) were employed in this study to deposit three sample sets at different spray conditions. Prepared specimens were annealed in air at atmospheric pressure for 2 h at various temperatures from 530 to 1170 °C. X-ray diffraction (XRD), Raman spectroscopy and porosity measurements were used for sample characterization. Dielectric spectroscopy was applied to obtain relative permittivity, conductivity and loss factor frequency dependence. Band gap energy was estimated from reflectance measurements. The work is focused on the explanation of changes in microstructure and properties of a plasma sprayed deposit after thermal annealing. Obtained results show significant improvement of dielectric properties after thermal annealing.

3D static and time-dependent modelling of a dc transferred arc twin torch system

International Nuclear Information System (INIS)

Colombo, V; Ghedini, E; Boselli, M; Sanibondi, P; Concetti, A

2011-01-01

The transferred arc plasma torch device consists of two electrodes generating a plasma arc sustained by means of an electric current flowing through the body of the discharge. Modelling works investigating transferred electric arc discharges generated between two suspended metallic electrodes, in the so-called twin torch configuration, are scarce. The discharge generated by this particular plasma source configuration is characterized by a complex shape and fluid dynamics and needs a 3D description in order to be realistically predicted. The extended discharge length that goes from the tungsten pencil cathode to the flat copper anode without any particular confinement wall and the fluid dynamics and magnetic forces acting on the arc may induce an unsteady behaviour. In order to capture the dynamic behaviour of a twin torch discharge, a 3D time-dependent plasma arc model has been developed using a customized commercial code FLUENT form in both local thermodynamic equilibrium (LTE) and non-LTE. A two temperature (2T) model has been developed taking into account only the thermal non-equilibrium effects in argon plasma. The main differences between LTE and 2T models' results concern the increased extension of the horizontal section of the discharge and the predicted reduced (of about 60-80 V) voltage drop between the electrodes when using a 2T model.

Sintering of Fine Particles in Suspension Plasma Sprayed Coatings

Directory of Open Access Journals (Sweden)

Leszek Latka

2010-07-01

Full Text Available Suspension plasma spraying is a process that enables the production of finely grained nanometric or submicrometric coatings. The suspensions are formulated with the use of fine powder particles in water or alcohol with some additives. Subsequently, the suspension is injected into plasma jet and the liquid additives evaporate. The remaining fine solids are molten and subsequently agglomerate or remain solid, depending on their trajectory in the plasma jet. The coating’s microstructure results from these two groups of particles arriving on a substrate or previously deposited coating. Previous experimental studies carried out for plasma sprayed titanium oxide and hydroxyapatite coatings enabled us to observe either a finely grained microstructure or, when a different suspension injection mode was used, to distinguish two zones in the microstructure. These two zones correspond to the dense zone formed from well molten particles, and the agglomerated zone formed from fine solid particles that arrive on the substrate in a solid state. The present paper focuses on the experimental and theoretical analysis of the formation process of the agglomerated zone. The experimental section establishes the heat flux supplied to the coating during deposition. In order to achieve this, calorimetric measurements were made by applying experimental conditions simulating the real coatings’ growth. The heat flux was measured to be in the range from 0.08 to 0.5 MW/m2,depending on the experimental conditions. The theoretical section analyzes the sintering during the coating’s growth, which concerns the fine particles arriving on the substrate in the solid state. The models of volume, grain boundary and surface diffusion were analyzed and adapted to the size and chemistry of the grains, temperature and time scales corresponding to the suspension plasma spraying conditions. The model of surface diffusion was found to best describe the sintering during suspension

Simulated experiment for elimination of chemical and biological warfare agents by making use of microwave plasma torch

International Nuclear Information System (INIS)

Hong, Yong C.; Kim, Jeong H.; Uhm, Han S.

2004-01-01

The threat of chemical and biological warfare agents in a domestic terrorist attack and in military conflict is increasing worldwide. Elimination and decontamination of chemical and biological warfare (CBW) agents are immediately required after such an attack. Simulated experiment for elimination of CBW agents by making use of atmospheric-pressure microwave plasma torches is carried out. Elimination of biological warfare agents indicated by the vitrification or burnout of sewage sludge powders and decomposition of toluene gas as a chemical agent stimulant are presented. A detailed characterization for the elimination of the simulant chemicals using Fourier transform infrared and gas chromatography is also presented

Simulated experiment for elimination of chemical and biological warfare agents by making use of microwave plasma torch

Science.gov (United States)

Hong, Yong C.; Kim, Jeong H.; Uhm, Han S.

2004-02-01

The threat of chemical and biological warfare agents in a domestic terrorist attack and in military conflict is increasing worldwide. Elimination and decontamination of chemical and biological warfare (CBW) agents are immediately required after such an attack. Simulated experiment for elimination of CBW agents by making use of atmospheric-pressure microwave plasma torches is carried out. Elimination of biological warfare agents indicated by the vitrification or burnout of sewage sludge powders and decomposition of toluene gas as a chemical agent stimulant are presented. A detailed characterization for the elimination of the simulant chemicals using Fourier transform infrared and gas chromatography is also presented.

Behaviour of plasma spray coatings under disruption simulation

International Nuclear Information System (INIS)

Brossa, F.; Rigon, G.; Looman, B.

1988-01-01

The behaviour of metallic and ceramic protective coatings under disruption simulations was studied correlating the damage with their physical and structural parameters. Plasma Spray (PS) and Vacuum Plasma Spray (VPS) were the techniques used for the production of the coatings. W-5% Re was selected for divertor plates, and TiC, TiO 2 , Al 2 O 3 , low-Z ceramic materials for the first wall protection on 316 SS, Cu and Al as substrates. An electron beam gun was used to simulate the plasma disruptions. The tests were carried out from 0.6 to 6 MJ/m 2 . The thermal effects were studied by metallographic and EDXA analysis. The damage was observed comparing the degree of protection provided by each coating to discover the minimum thickness necessary to prevent the underlying material from melting. Good protective coatings must have a high melting point, great porosity and low thermal conductivity. Such coatings act as thermal barriers, increasing the surface temperature and radiating back large parts of the energy. (orig.)

The Influence of Nanodispersed Modifiers on the Structure and Properties of Plasma-Sprayed Coatings

Directory of Open Access Journals (Sweden)

Igor V. Smirnov

2017-10-01

Full Text Available Background. Currently, plasma-sprayed coatings are widely used to protect machine parts operating under conditions of high loads and temperatures, abrasive wear and exposure to corrosive media. Objective. The aim of the paper is to improve the physico-mechanical characteristics of plasma-sprayed coatings by modification of nano-sized particles of TiO2 oxides compounds. Methods. Experimental studies of corrosion resistance, microhardness, adhesion strength and residual stresses of plasma-sprayed coatings based on the oxide aluminum ceramic powder with the addition of nanodisperse TiO2 powder were conducted. Results. It is found that addition of TiO2 nanodisperse modifier to the oxide aluminum ceramic powder composition leads to corrosion resistance increase 2.8 times in a 10 % hydrochloric acid solution. The adhesive strength of ceramic nanomodified coatings is increased by 15–20 %. Conclusions. The positive influence of nanodispersed powders on the physico-mechanical and tribological characteristics of plasma-sprayed coatings is established.

Laser treatment of plasma sprayed HA coatings

NARCIS (Netherlands)

Khor, KA; Vreeling, A; Dong, ZL; Cheang, P

1999-01-01

Laser treatment was conducted on plasma sprayed hydroxyapatite (HA) coatings using a Nd-YAG pulse laser. Various laser parameters were investigated. The results showed that the HA surface melted when an energy level of greater than or equal to 2 J and a spot size of 2 mm was employed during

The influence of pore formers on the microstructure of plasma-sprayed NiO-YSZ anodes

Science.gov (United States)

Poon, Michael; Kesler, Olivera

2012-07-01

Four types of pore formers: high-density polyethylene (HDPE), polyether-ether-ketone (PEEK), mesocarbon-microbead (MCMB) carbon powder, and baking flour, are processed and characterized, then incorporated with NiO-YSZ nano-agglomerate powder to produce plasma sprayed SOFC anode coatings. Scanning electron microscopy (SEM) of the coating microstructure, gas permeability measurements, and porosity determinations by image analysis are used to evaluate the effectiveness of each potential pore former powder. Under the spray conditions studied, the flour and MCMB pore former powders are effective as plasma sprayed pore formers, increasing the permeability of the coatings by factors of four and two, respectively, compared to a similarly sprayed NiO-YSZ coating without pore formers. The HDPE powder is unable to survive the plasma spray process and does not contribute to the final coating porosity. The PEEK pore former, though ineffective with the current powder characteristics and spray parameters, exhibits the highest relative deposition efficiency and the most favorable thermal characteristics.

A study on the effect of heat treatment on electrical properties of plasma sprayed YSZ

International Nuclear Information System (INIS)

Elshikh, S.S.M.

2012-01-01

Free standing samples of plasma sprayed (PS) zirconia partially stabilized with yettria (YSZ) were prepared with two machines of plasma spray deposition (Triplex gun- 100 kw, F-4 gun 64 kw) have different electrical power and spraying parameters, which produced different microstructures; contain different amounts and varieties of pores and micro-cracks.The study included heat treatment of samples at 1200 degree C for 1 h, 5 h, 10 h, 100 h and 500 h, to study the changes in macrostructure (pores and micro-cracks) which affect the electrical conductivity.The electrical properties (resistively, electrical conductivity) of plasma sprayed ZrO 2 stabilized by 8 wt. % Y 2 O 3 samples were determined by using electrical impedance spectroscopy (IS). Specimen's microstructure was examined by optical microscopy. By measuring electrical properties and connected porosity percent of the coatings obtained under various spraying conditions, it would be possible to select the optimum spraying condition to spray coatings which have high efficiency at high temperature.The results showed that the electrical conductivity of (YSZ) samples after heat treatment increased by a rate of (20%-30%) as compared to that of as sprayed.

Measurement of the non-thermal properties of a low pressure spraying plasma by electric and spectroscopic methods

International Nuclear Information System (INIS)

Jung, Yong Ho

2003-02-01

For the case of an atmospheric plasma, the local thermodynamic equilibrium (LTE) model can be applied to plasmas at a nozzle entrance and to those on the axis of the plasma flame, but it is not easy to justify applying the LTE model to off-center plasma and to a low-pressure spraying plasma. Although the energy distribution of the electrons is assumed to be Maxwellian for the most of spraying plasmas, the non-Maxwellian distribution is possible for the case of low-pressure spaying plasma and edge plasma of atmospheric spraying plasma. In this work, the non-Maxwellian distribution of electrons was measured by using an electric probe installed on the fast scanning probe system, and non-LTE effects were measured by using the optical emission spectroscopy system. Distribution of the electrons of a low-pressure spraying plasma is observed not as Maxwellian but as bi-Maxwellian by the measurement of the single probe. Bi-Maxwellian distribution appears in the edge of a low pressure spraying plasma and seems to be due to the reduction of the collisonality by the drastic variation of the plasma density. Non-LTE characteristics of a low-pressure spraying plasma can be deuced from the measured results of the optical emission spectroscopy and is analyzed by the collisional radiative equilibrium (CRE) model, where the Maxwellian and the non-Maxwellian distributions are assumed for comparison. For the electron temperature, the results from optical emission spectroscopy were similar to the results from the single probe (3∼5 % in error)

A study on the particle melting by plasma spraying

International Nuclear Information System (INIS)

Jung, In Ha; Ji, C. G.; Bae, S. O.; Yoon, J. H.; Kwon, H. I.

2001-12-01

As a preliminary study for fabricating a thick and dense free standing type deposit, powder melting studies were carried out. Various morphologies and sizes of powder having the same chemical compositions were applied in particle melting experiments with varying systematic parameters. Through the study of powder melting by inductively coupled plasma, we can conclude as followings: Argon-hydrogen plasma gas with a higher plasma power gave good quality of splats and shown a higher density with a higher build-up rate. Reproducibility of the experiments appeared in the range of 99%. Degree of particle melting and its density just before impinging played a predominant role in the density of a deposit. Chamber pressure has an effect on degree of deformation of the splats, i.e. on the particle momentum. Completely melted particle showed a high deformation appearance. Build-up rate had a relation with a fraction of the fully melted particle, and this also closely associates with productivity and economical efficiency. For increasing the fraction of the fully melted particle, either increasing the power or limiting the particle size was recommended. Mean pore size and its distribution of a deposit seemed to have a relation with a viscosity of the melted powder, i.e. particle temperature, and also with a chamber pressure and spraying distances. Particle temperature may be governed by a plasma power, plasma gas property, probe position, and spraying distance in the present experimental range. Some results might be appeared with mutual interactions of the effects, for example, particle residence time and momentum with chamber pressure, particle temperature with chamber pressure, spraying distance and its size

A study on the particle melting by plasma spraying

Energy Technology Data Exchange (ETDEWEB)

Jung, In Ha; Ji, C. G.; Bae, S. O.; Yoon, J. H.; Kwon, H. I

2001-12-01

As a preliminary study for fabricating a thick and dense free standing type deposit, powder melting studies were carried out. Various morphologies and sizes of powder having the same chemical compositions were applied in particle melting experiments with varying systematic parameters. Through the study of powder melting by inductively coupled plasma, we can conclude as followings: Argon-hydrogen plasma gas with a higher plasma power gave good quality of splats and shown a higher density with a higher build-up rate. Reproducibility of the experiments appeared in the range of 99%. Degree of particle melting and its density just before impinging played a predominant role in the density of a deposit. Chamber pressure has an effect on degree of deformation of the splats, i.e. on the particle momentum. Completely melted particle showed a high deformation appearance. Build-up rate had a relation with a fraction of the fully melted particle, and this also closely associates with productivity and economical efficiency. For increasing the fraction of the fully melted particle, either increasing the power or limiting the particle size was recommended. Mean pore size and its distribution of a deposit seemed to have a relation with a viscosity of the melted powder, i.e. particle temperature, and also with a chamber pressure and spraying distances. Particle temperature may be governed by a plasma power, plasma gas property, probe position, and spraying distance in the present experimental range. Some results might be appeared with mutual interactions of the effects, for example, particle residence time and momentum with chamber pressure, particle temperature with chamber pressure, spraying distance and its size.

Supersonic induction plasma jet modeling

International Nuclear Information System (INIS)

Selezneva, S.E.; Boulos, M.I.

2001-01-01

Numerical simulations have been applied to study the argon plasma flow downstream of the induction plasma torch. It is shown that by means of the convergent-divergent nozzle adjustment and chamber pressure reduction, a supersonic plasma jet can be obtained. We investigate the supersonic and a more traditional subsonic plasma jets impinging onto a normal substrate. Comparing to the subsonic jet, the supersonic one is narrower and much faster. Near-substrate velocity and temperature boundary layers are thinner, so the heat flux near the stagnation point is higher in the supersonic jet. The supersonic plasma jet is characterized by the electron overpopulation and the domination of the recombination over the dissociation, resulting into the heating of the electron gas. Because of these processes, the supersonic induction plasma permits to separate spatially different functions (dissociation and ionization, transport and deposition) and to optimize each of them. The considered configuration can be advantageous in some industrial applications, such as plasma-assisted chemical vapor deposition of diamond and polymer-like films and in plasma spraying of nanoscaled powders

Evaluation of Plasma Spray hydroxy Apatite Coatings on Metallic Materials

International Nuclear Information System (INIS)

Take, S.; Mitsul, K.; Kasahara, M.; Sawal, R.; Izawa, S.; Nakayama, M.; Itoi, Y.

2007-01-01

Biocompatible Hydroxy apatite (HAp) coatings on metallic substrate by plasma spray techniques have been developed. Long-term credibility of plasma spray HAp coatings has been evaluated in physiological saline by electrochemical measurements. It was found that the corrosion resistance of SUS316L based HAp/Ti combined coatings was excellent even after more than 10 weeks long-term immersion. It was shown that postal heat treatment improved both the crystallinity and corrosion resistance of HAp. By lowering cooling rate during heat treatment process, less cracks produced in HAp coating layer, which lead to higher credibility of HAp during immersion in physiological saline. The ICP results showed that the dissolution level of substrate metallic ions was low and HAp coatings produced in this research can be acceptable as biocompatible materials. Also, the concentration of dissolved ions from HAp coatings with postal heat treatment was lower compared to those from samples without postal heat treatment. The adherence of HAp coatings with Ti substrate and other mechanical properties were also assessed by three-point bending test. The poor adhesion of HAp coating to titanium substrate can be improved by introducing a plasma spray titanium intermediate layer

Influence of Bondcoat Spray Process on Lifetime of Suspension Plasma-Sprayed Thermal Barrier Coatings

Science.gov (United States)

Gupta, M.; Markocsan, N.; Li, X.-H.; Östergren, L.

2018-01-01

Development of thermal barrier coatings (TBCs) manufactured by suspension plasma spraying (SPS) is of high commercial interest as SPS has been shown capable of producing highly porous columnar microstructures similar to the conventionally used electron beam-physical vapor deposition. However, lifetime of SPS coatings needs to be improved further to be used in commercial applications. The bondcoat microstructure as well as topcoat-bondcoat interface topography affects the TBC lifetime significantly. The objective of this work was to investigate the influence of different bondcoat deposition processes for SPS topcoats. In this work, a NiCoCrAlY bondcoat deposited by high velocity air fuel (HVAF) was compared to commercial vacuum plasma-sprayed NiCoCrAlY and PtAl diffusion bondcoats. All bondcoat variations were prepared with and without grit blasting the bondcoat surface. SPS was used to deposit the topcoats on all samples using the same spray parameters. Lifetime of these samples was examined by thermal cyclic fatigue testing. Isothermal heat treatment was performed to study bondcoat oxidation over time. The effect of bondcoat deposition process and interface topography on lifetime in each case has been discussed. The results show that HVAF could be a suitable process for bondcoat deposition in SPS TBCs.

Investigation on the suitability of plasma sprayed Fe-Cr-Al coatings as tritium permeation barrier

International Nuclear Information System (INIS)

Fazio, C.; Serra, E.; Benamati, G.

1999-01-01

Results on the fabrication of a tritium permeation barrier by spraying Fe-Cr-Al powders are described. The sprayed coatings were deposited at temperatures below the A c1 temperature of the ferritic-martensitic steel substrate and no post-deposition heat treatment was applied. The aim of the investigation was the determination of the efficiency of the coatings to act as tritium permeation barrier. Metallurgical investigations as well as hydrogen isotope permeation measurements were carried out onto the produced coatings. The depositions were performed on ferritic-martensitic steels by means of three types of spray techniques: high velocity oxy fuel, air plasma spray and vacuum plasma spray. (orig.)

Transformation kinetics in plasma-sprayed barium- and strontium-doped aluminosilicate (BSAS)

International Nuclear Information System (INIS)

Harder, B.J.; Faber, K.T.

2010-01-01

The hexacelsian-to-celsian phase transformation in Ba 1-x Sr x Al 2 Si 2 O 8 is of interest for environmental barrier coating applications. Plasma-sprayed microstructures were heat treated above 1100 o C and the kinetics of the hexacelsian-to-celsian transformation were quantified. Activation energies for bulk and crushed materials were determined to be ∼340 and ∼500 kJ mol -1 , respectively. X-ray diffraction and electron backscattered diffraction were used to establish how plasma spraying barium- and strontium-doped aluminosilicate effectively reduces the energy required for its transformation.

Plasma sprayed coatings on mild steel split moulds for uranium casting

International Nuclear Information System (INIS)

Sreekumar, K.P.; Padmanaban, P.V.A.; Venkatramani, N.; Singh, S.P.; Saha, D.P.; Date, V.G.

2002-01-01

High velocity high temperature plasma jets are used to deposit metals and ceramics on metallic substrates for oxidation and corrosion protection applications. Plasma sprayed ceramic coatings on metallic substrates are also used to prevent its reaction with molten metals. Metal-alumina duplex coatings on mild steel split moulds have been developed and successfully used for casting of uranium. Techno-economics of the coated moulds against the conventional graphite moulds are a major advantage. Mild steel moulds of 600 mm long and 75 mm in diameter have been plasma spray coated with alumina over a bond coat of molybdenum. In-plant tests showed an increase in number of castings per mould compared to the commonly used graphite moulds. (author)

Aspects of industrial production of solid electrolyte fuel cells (SOFC) by thermal spraying technology; Aspekte industrieller Fertigung von Festelektrolyt-Brennstoffzellen (SOFC) mittels thermischer Beschichtungsverfahren

Energy Technology Data Exchange (ETDEWEB)

Weckmann, Hannes

2010-07-01

was applied significantly higher charge transfer resistance of up to 1,7 M{omega}cm{sup 2} could be demonstrated at layer thicknesses between 20 {mu}m and 117 {mu}m. In the further course of the thesis an online controller was developed for the VPS process based on insitu process diagnostic systems in order to reproducibly produce thermal sprayed functional layers. In pretests the process diagnostic system Accuraspray appeared to be cable of identifying changes in the process by detecting particle properties in the spray torch. In order to serve as a knowledge base for the controller the plasma spraying process was successfully modelled as correlation between machine parameters, spray torch- und layer properties by using artificial neural networks (ANN). The ability for the generalization as well as the accuracy of the model was improved further by measures such as active learning (additional experiments at poorly represented regions) and the combination of several models with different network architectures as an ensemble (mixture of experts). Based on the artificial neural network model, an online process controller was developed, which manipulates major process parameters in case of a deviation in order to get back to the initial state. The ability of the prototype controller could be demonstrated successfully in most cases. (orig.)

Microstructure and mechanical properties of plasma sprayed HA/YSZ/Ti-6Al-4V composite coatings.

Science.gov (United States)

Khor, K A; Gu, Y W; Pan, D; Cheang, P

2004-08-01

Plasma sprayed hydroxyapatite (HA) coatings on titanium alloy substrate have been used extensively due to their excellent biocompatibility and osteoconductivity. However, the erratic bond strength between HA and Ti alloy has raised concern over the long-term reliability of the implant. In this paper, HA/yttria stabilized zirconia (YSZ)/Ti-6Al-4V composite coatings that possess superior mechanical properties to conventional plasma sprayed HA coatings were developed. Ti-6Al-4V powders coated with fine YSZ and HA particles were prepared through a unique ceramic slurry mixing method. The so-formed composite powder was employed as feedstock for plasma spraying of the HA/YSZ/Ti-6Al-4V coatings. The influence of net plasma energy, plasma spray standoff distance, and post-spray heat treatment on microstructure, phase composition and mechanical properties were investigated. Results showed that coatings prepared with the optimum plasma sprayed condition showed a well-defined splat structure. HA/YSZ/Ti-6Al-4V solid solution was formed during plasma spraying which was beneficial for the improvement of mechanical properties. There was no evidence of Ti oxidation from the successful processing of YSZ and HA coated Ti-6Al-4V composite powders. Small amount of CaO apart from HA, ZrO(2) and Ti was present in the composite coatings. The microhardness, Young's modulus, fracture toughness, and bond strength increased significantly with the addition of YSZ. Post-spray heat treatment at 600 degrees C and 700 degrees C for up to 12h was found to further improve the mechanical properties of coatings. After the post-spray heat treatment, 17.6% increment in Young's modulus (E) and 16.3% increment in Vicker's hardness were achieved. The strengthening mechanisms of HA/YSZ/Ti-6Al-4V composite coatings were related to the dispersion strengthening by homogeneous distribution of YSZ particles in the matrix, the good mechanical properties of Ti-6Al-4V and the formation of solid solution among HA

Langmuir probe diagnostics of an atmospheric pressure, vortex-stabilized nitrogen plasma jet

Energy Technology Data Exchange (ETDEWEB)

Prevosto, L.; Mancinelli, B. R. [Grupo de Descargas Electricas, Departamento Ingenieria Electromecanica, Facultad Regional Venado Tuerto (UTN), Laprida 651, (2600) Venado Tuerto, Santa Fe (Argentina); Kelly, H. [Grupo de Descargas Electricas, Departamento Ingenieria Electromecanica, Facultad Regional Venado Tuerto (UTN), Laprida 651, (2600) Venado Tuerto, Santa Fe (Argentina) and Instituto de Fisica del Plasma (CONICET), Departamento de Fisica, Facultad de Ciencias Exactas y Naturales UBA Ciudad Universitaria Pab. I, (1428) Buenos Aires (Argentina)

2012-09-15

Langmuir probe measurements in an atmospheric pressure direct current (dc) plasma jet are reported. Sweeping probes were used. The experiment was carried out using a dc non-transferred arc torch with a rod-type cathode and an anode of 5 mm diameter. The torch was operated at a nominal power level of 15 kW with a nitrogen flow rate of 25 Nl min{sup -1}. A flat ion saturation region was found in the current-voltage curve of the probe. The ion saturation current to a cylindrical probe in a high-pressure non local thermal equilibrium (LTE) plasma was modeled. Thermal effects and ionization/recombination processes inside the probe perturbed region were taken into account. Averaged radial profiles of the electron and heavy particle temperatures as well as the electron density were obtained. An electron temperature around 11 000 K, a heavy particle temperature around 9500 K and an electron density of about 4 Multiplication-Sign 10{sup 22} m{sup -3}, were found at the jet centre at 3.5 mm downstream from the torch exit. Large deviations from kinetic equilibrium were found throughout the plasma jet. The electron and heavy particle temperature profiles showed good agreement with those reported in the literature by using spectroscopic techniques. It was also found that the temperature radial profile based on LTE was very close to that of the electrons. The calculations have shown that this method is particularly useful for studying spraying-type plasma jets characterized by electron temperatures in the range 9000-14 000 K.

Antibacterial characteristics of thermal plasma spray system.

Science.gov (United States)

Goudarzi, M; Saviz, Sh; Ghoranneviss, M; Salar Elahi, A

2018-03-15

The objective of this study is to investigate antibacterial characteristics of a thermal plasma spray system. For this purpose, copper powder was coated on a handmade atmospheric plasma spraying system made by the stainless steel 316 substrate, which is preheated at different temperatures before spraying. A number of deposition characteristics such as antibacterial characteristics, adhesion strength and hardness of coating, was investigated. All of the spray parameters are fixed except the substrate temperature. The chemical composition was analyzed by X-ray diffraction (XRD). A scanning electron microscopy (SEM) and back scattering electron microscopy (BSE) were used to show the coating microstructure, its thickness and also the powder micrograph. The energy dispersive X-ray spectroscopy (EDX) was used to analyze the coating particles. Hardness of the deposition was examined by Vickers tester (HV0.1). Its adhesion strength was declared by cross cut tester (TQC). In addition, the percentage of bactericidal coating was evidenced with Staphylococcus aurous and Escherichia coli bacteria. Study results show that as the substrates temperature increases, the number of splats in the shape of pancake increases, the greatness and percentage of the deposition porosity both decrease. The increment of the substrate temperature leads to more oxidation and makes thicker dendrites on the splat. The enhancement of the substrate temperature also enlarges thickness and efficiency of coating. The interesting results are that antibacterial properties of coatings against the Escherichia coli are more than Staphylococcus aurous bacteria. However the bactericidal percentage of the coatings against Staphylococcus aurous and Escherichia coli bacteria roughly does not change with increasing the substrate temperature. Furthermore, by increment of the substrate temperature, coatings with both high adhesion and hardness are obtained. Accordingly, the temperature of substrate can be an

Molybdenum disilicide composites produced by plasma spraying

International Nuclear Information System (INIS)

Castro, R.G.; Hollis, K.J.; Kung, H.H.; Bartlett, A.H.

1998-01-01

The intermetallic compound, molybdenum disilicide (MoSi 2 ) is being considered for high temperature structural applications because of its high melting point and superior oxidation resistance at elevated temperatures. The lack of high temperature strength, creep resistance and low temperature ductility has hindered its progress for structural applications. Plasma spraying of coatings and structural components of MoSi 2 -based composites offers an exciting processing alternative to conventional powder processing methods due to superior flexibility and the ability to tailor properties. Laminate, discontinuous and in situ reinforced composites have been produced with secondary reinforcements of Ta, Al 2 O 3 , SiC, Si 3 N 4 and Mo 5 Si 3 . Laminate composites, in particular, have been shown to improve the damage tolerance of MoSi 2 during high temperature melting operations. A review of research which as been performed at Los Alamos National Laboratory on plasma spraying of MoSi 2 -based composites to improve low temperature fracture toughness, thermal shock resistance, high temperature strength and creep resistance will be discussed

Corrosion performance of atmospheric plasma sprayed alumina coatings on AZ31B magnesium alloy under immersion environment

Directory of Open Access Journals (Sweden)

D. Thirumalaikumarasamy

2014-12-01

Full Text Available Plasma sprayed ceramic coatings are successfully used in many industrial applications, where high wear and corrosion resistance with thermal insulation are required. The alumina powders were plasma sprayed on AZ31B magnesium alloy with three different plasma spraying parameters. In the present work, the influence of plasma spray parameters on the corrosion behavior of the coatings was investigated. The corrosion behavior of the coated samples was evaluated by immersion corrosion test in 3.5 wt% NaCl solution. Empirical relationship was established to predict the corrosion rate of plasma sprayed alumina coatings by incorporating process parameters. The experiments were conducted based on a three factor, five-level, central composite rotatable design matrix. The developed relationship can be effectively used to predict the corrosion rate of alumina coatings at 95% confidence level. The results indicate that the input power has the greatest influence on corrosion rate, followed by stand-off distance and powder feed rate.

Investigating Tribological Characteristics of HVOF Sprayed AISI 316 Stainless Steel Coating by Pulsed Plasma Nitriding

Science.gov (United States)

Mindivan, H.

2018-01-01

In this study, surface modification of aluminum alloy using High-Velocity Oxygen Fuel (HVOF) thermal spray and pulsed plasma nitriding processes was investigated. AISI 316 stainless steel coating on 1050 aluminum alloy substrate by HVOF process was pulsed plasma nitrided at 793 K under 0.00025 MPa pressure for 43200 s in a gas mixture of 75 % N2 and 25 % H2. The results showed that the pulse plasma nitriding process produced a surface layer with CrN, iron nitrides (Fe3N, Fe4N) and expanded austenite (γN). The pulsed plasma nitrided HVOF-sprayed coating showed higher surface hardness, lower wear rate and coefficient of friction than the untreated HVOF-sprayed one.

Mueller matrix polarimetry on plasma sprayed thermal barrier coatings for porosity measurement.

Science.gov (United States)

Luo, David A; Barraza, Enrique T; Kudenov, Michael W

2017-12-10

Yttria-stabilized zirconia (YSZ) is the most widely used material for thermal plasma sprayed thermal barrier coatings (TBCs) used to protect gas turbine engine parts in demanding operation environments. The superior material properties of YSZ coatings are related to their internal porosity level. By quantifying the porosity level, tighter control on the spraying process can be achieved to produce reliable coatings. Currently, destructive measurement methods are widely used to measure the porosity level. In this paper, we describe a novel nondestructive approach that is applicable to classify the porosity level of plasma sprayed YSZ TBCs via Mueller matrix polarimetry. A rotating retarder Mueller matrix polarimeter was used to measure the polarization properties of the plasma sprayed YSZ coatings with different porosity levels. From these measurements, it was determined that a sample's measured depolarization ratio is dependent on the sample's surface roughness and porosity level. To this end, we correlate the depolarization ratio with the samples' surface roughness, as measured by a contact profilometer, as well as the total porosity level, in percentage measured using a micrograph and stereological analysis. With the use of this technique, a full-field and rapid measurement of porosity level can be achieved.

Plasma devices for hydrocarbon reformation

KAUST Repository

Cha, Min Suk

2017-02-16

Plasma devices for hydrocarbon reformation are provided. Methods of using the devices for hydrocarbon reformation are also provided. The devices can include a liquid container to receive a hydrocarbon source, and a plasma torch configured to be submerged in the liquid. The plasma plume from the plasma torch can cause reformation of the hydrocarbon. The device can use a variety of plasma torches that can be arranged in a variety of positions in the liquid container. The devices can be used for the reformation of gaseous hydrocarbons and/or liquid hydrocarbons. The reformation can produce methane, lower hydrocarbons, higher hydrocarbons, hydrogen gas, water, carbon dioxide, carbon monoxide, or a combination thereof.

Solution precursor plasma deposition of nanostructured ZnO coatings

International Nuclear Information System (INIS)

Tummala, Raghavender; Guduru, Ramesh K.; Mohanty, Pravansu S.

2011-01-01

Highlights: → The solution precursor route employed is an inexpensive process with capability to produce large scale coatings at fast rates on mass scale production. → It is highly capable of developing tailorable nanostructures. → This technique can be employed to spray the coatings on any kind of substrates including polymers. → The ZnO coatings developed via solution precursor plasma spray process have good electrical conductivity and reflectivity properties in spite of possessing large amount of particulate boundaries, porosity and nanostructured grains. -- Abstract: Zinc oxide (ZnO) is a wide band gap semiconducting material that has various applications including optical, electronic, biomedical and corrosion protection. It is usually synthesized via processing routes, such as vapor deposition techniques, sol-gel, spray pyrolysis and thermal spray of pre-synthesized ZnO powders. Cheaper and faster synthesis techniques are of technological importance due to increased demand in alternative energy applications. Here, we report synthesis of nanostructured ZnO coatings directly from a solution precursor in a single step using plasma spray technique. Nanostructured ZnO coatings were deposited from the solution precursor prepared using zinc acetate and water/isopropanol. An axial liquid atomizer was employed in a DC plasma spray torch to create fine droplets of precursor for faster thermal treatment in the plasma plume to form ZnO. Microstructures of coatings revealed ultrafine particulate agglomerates. X-ray diffraction confirmed polycrystalline nature and hexagonal Wurtzite crystal structure of the coatings. Transmission electron microscopy studies showed fine grains in the range of 10-40 nm. Observed optical transmittance (∼65-80%) and reflectivity (∼65-70%) in the visible spectrum, and electrical resistivity (48.5-50.1 mΩ cm) of ZnO coatings are attributed to ultrafine particulate morphology of the coatings.

Solution precursor plasma deposition of nanostructured ZnO coatings

Energy Technology Data Exchange (ETDEWEB)

Tummala, Raghavender [Department of Mechanical Engineering, University of Michigan - Dearborn, MI 48128 (United States); Guduru, Ramesh K., E-mail: rkguduru@umich.edu [Department of Mechanical Engineering, University of Michigan - Dearborn, MI 48128 (United States); Mohanty, Pravansu S. [Department of Mechanical Engineering, University of Michigan - Dearborn, MI 48128 (United States)

2011-08-15

Highlights: {yields} The solution precursor route employed is an inexpensive process with capability to produce large scale coatings at fast rates on mass scale production. {yields} It is highly capable of developing tailorable nanostructures. {yields} This technique can be employed to spray the coatings on any kind of substrates including polymers. {yields} The ZnO coatings developed via solution precursor plasma spray process have good electrical conductivity and reflectivity properties in spite of possessing large amount of particulate boundaries, porosity and nanostructured grains. -- Abstract: Zinc oxide (ZnO) is a wide band gap semiconducting material that has various applications including optical, electronic, biomedical and corrosion protection. It is usually synthesized via processing routes, such as vapor deposition techniques, sol-gel, spray pyrolysis and thermal spray of pre-synthesized ZnO powders. Cheaper and faster synthesis techniques are of technological importance due to increased demand in alternative energy applications. Here, we report synthesis of nanostructured ZnO coatings directly from a solution precursor in a single step using plasma spray technique. Nanostructured ZnO coatings were deposited from the solution precursor prepared using zinc acetate and water/isopropanol. An axial liquid atomizer was employed in a DC plasma spray torch to create fine droplets of precursor for faster thermal treatment in the plasma plume to form ZnO. Microstructures of coatings revealed ultrafine particulate agglomerates. X-ray diffraction confirmed polycrystalline nature and hexagonal Wurtzite crystal structure of the coatings. Transmission electron microscopy studies showed fine grains in the range of 10-40 nm. Observed optical transmittance ({approx}65-80%) and reflectivity ({approx}65-70%) in the visible spectrum, and electrical resistivity (48.5-50.1 m{Omega} cm) of ZnO coatings are attributed to ultrafine particulate morphology of the coatings.

Ceramic Materials Selection of Fuel Crucibles based on Plasma Spray Coating for SFR

Energy Technology Data Exchange (ETDEWEB)

Song, Hoon; Kim, Jonghwan; Kim, Hyungtae; Ko, Youngmo; Woo, Yoonmyung; Oh, Seokjin; Kim, Kihwan; Lee, Chanbock [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

2012-07-01

The plasma-sprayed coating can provide the crucible with a denser, more friable coating layer, compared with the more friable coating layer formed by slurry-coating, which was used to prevent the interaction between melt and crucibles. Plasma-sprayed coatings are consolidated by mechanical interlocking of the molten particles impacting on the substrate and are dense by the heat applied by the plasma. The increased coating density is advantageous because it should not require frequent re coating and U-Zr melt penetration through the protective layer is more difficult in a dense coating than in a porous coating. In this study, we used Vacuum Plasma Spray method to investigate permanent coatings for re-usable crucibles for melting and casting of metallic fuel onto niobium substrates. Niobium was selected as a substrate because of its refractory nature and the coefficient of thermal expansion is similar to that of many of the candidate materials. After the HfC, ZrC, TiC, TaC, Y{sub 2}O{sub 3}, and 8% YSZ coatings were applied the resulting microstructure and chemical compositions was characterized to find the optimum process conditions for coating. Thermal plasma-sprayed coatings of refractory materials can be applied to develop a re-usable crucible coating for metallic fuel, such as the U-Zr alloy proposed for sodium cooled fast reactors.

Effect of Bauxite addition on Adhesion Strength and Surface Roughness of Fly ash based Plasma Sprayed Coatings

Science.gov (United States)

Bhuyan, S. K.; Samal, S.; Pattnaik, D.; Sahu, A.; Swain, B.; Thiyagarajan, T. K.; Mishra, S. C.

2018-03-01

The environment is being contaminated with advancement of new technology, day by day. One of the primary sources for this contamination is the industrial waste. Industrialization is the prime reason behind the prosperity of any country to meet the materialistic demand. To run the industries, a huge amount of (electric) power is needed and hence need for thermal power plants to serve the purpose. In present scenario, coal fired thermal power plants are set up which generates a huge quantity of Fly ash. Consumption of industrial waste (Fly ash), continually a major concern for human race. In recent years, fly ash is being utilized for various purposes i.e. making bricks, mine reclamation, production of cements etc. The presence of Silica and Alumina in fly ash makes it useful for thermal barrier applications also. The plasma spray technology has the advantage of being able to process any types of metal/ceramic mineral, low-grade-ore minerals etc. to make value-added products and also to deposit ceramics, metals and a combination of these to deposit composite coatings with desired microstructure and required properties on a range of substrate materials. The present work focuses on utilization of fly ash mixing with bauxite (ore mineral) for a high valued application. Fly ash with 10 and 20% bauxite addition is used to deposit plasma spray overlay coatings at different power levels (10-20kW) on aluminum and mild steel substrates. Adhesion strength and surface roughness of the coatings are evaluated. Phase composition analysis of the coatings were done using X-ray diffraction analysis. Surface morphology of the coatings was studied using a scanning electron microscope (SEM). Maximum adhesion strength of 4.924 MPa is obtained for the composition fly ash and bauxite (10%), coated on mild steel at 16kW torch power level. The surface roughness (Ra) of the coatings is found to vary between 10.0102 to 17.2341 micron.

Atmospheric Plasma Spraying Low-Temperature Cathode Materials for Solid Oxide Fuel Cells

Science.gov (United States)

Harris, J.; Kesler, O.

2010-01-01

Atmospheric plasma spraying (APS) is attractive for manufacturing solid oxide fuel cells (SOFCs) because it allows functional layers to be built rapidly with controlled microstructures. The technique allows SOFCs that operate at low temperatures (500-700 °C) to be fabricated by spraying directly onto robust and inexpensive metallic supports. However, standard cathode materials used in commercial SOFCs exhibit high polarization resistances at low operating temperatures. Therefore, alternative cathode materials with high performance at low temperatures are essential to facilitate the use of metallic supports. Coatings of lanthanum strontium cobalt ferrite (LSCF) were fabricated on steel substrates using axial-injection APS. The thickness and microstructure of the coating layers were evaluated, and x-ray diffraction analysis was performed on the coatings to detect material decomposition and the formation of undesired phases in the plasma. These results determined the envelope of plasma spray parameters in which coatings of LSCF can be manufactured, and the range of conditions in which composite cathode coatings could potentially be manufactured.

Plasma spraying of zirconium carbide – hafnium carbide – tungsten cermets

Czech Academy of Sciences Publication Activity Database

Brožek, Vlastimil; Ctibor, Pavel; Cheong, D.-I.; Yang, S.-H.

2009-01-01

Roč. 9, č. 1 (2009), s. 49-64 ISSN 1335-8987 Institutional research plan: CEZ:AV0Z20430508 Keywords : Plasma spraying * cermet coatings * microhardness * zirconium carbide * hafnium carbide * tungsten * water stabilized plasma Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass

Induction plasma-sprayed photocatalytically active titania coatings and their characterisation by micro-Raman spectroscopy

Czech Academy of Sciences Publication Activity Database

Burlacov, I.; Jirkovský, Jaromír; Muller, M.; Heimann, R. B.

2006-01-01

Roč. 201, 1-2 (2006), s. 255-264 ISSN 0257-8972 Grant - others:European Communities(XE) EVKI-2002-30025 Institutional research plan: CEZ:AV0Z40400503 Source of funding: R - rámcový projekt EK Keywords : titania (anatase) coatings * induction plasma spraying * suspension plasma spraying * Raman spectroscopy Subject RIV: CG - Electrochemistry Impact factor: 1.559, year: 2006

Stainless steel coatings produced through atmospheric plasma spraying study of in flight powder behavior and coating structure

International Nuclear Information System (INIS)

Denoirjean, A.; Denoirjean, P.; Fauchais, P.; Labbe, J.C.; Khan, A.A.

2005-01-01

The Stainless Steel coatings deposited through Atmospheric Plasma Spraying over mild steel surface present an interest from commercial point of view, especially for the applications where corrosion resistance or inertness towards severe environment is required. Atmospheric Plasma Spraying is fast and relatively less expensive choice as compared to Vacuum Plasma Spraying, the only limitation being the extremely reactive nature of metallic powders used. A study of the behaviour of metallic powders within an Atmospheric Plasma Jet is presented in view of better understanding and eventual improvement in coating properties. Metallic powder particles show very interesting features when individual particles are collected after passing them through a DC Blown Arc Thermal Plasma Jet under Atmospheric Pressure. The spraying was carried out under air which makes the significance of these results even more interesting from the industrial point of view. Proper control of Spraying Parameters can help produce Stainless Steel coatings of reasonably low porosity and a typical lamellar microstructure. The results of SEM, AFM and XRD are discussed. A strange oxidation phenomenon under highly non equilibrium conditions is observed. (author)

Heat-Treated TiO2 Plasma Spray Deposition for Bioactivity Improvement in Ti-6Al-4V Alloy

Science.gov (United States)

Kumari, Renu; Majumdar, Jyotsna Dutta

2017-12-01

In the present study, titanium di-oxide (TiO2) coating has been developed on Ti-6Al-4V substrate by plasma spray deposition. Followed by plasma spraying, heat treatment of the sprayed sample has been carried out by isothermally holding it at 823 K (550 °C) for 2 h. Microstructural analysis shows the presence of porosity and unmelted particles on the as-sprayed surface, the area fraction of which reduces after heat treatment. X-ray diffraction analysis shows the phase transformation from anatase (in precursor powder) to rutile (in as-sprayed coating and the same after heat treatment). There is an improvement in nano-hardness, "Young's modulus" and wear resistance in plasma-sprayed TiO2 coating (as-sprayed as well as post-heat-treated condition) as compared to as-received Ti-6Al-4V, though post-heat treatment offers a superior hardness, "young's modulus" and wear resistance as compared to as-sprayed coating. The corrosion behavior in "hank's solution" shows decrease in corrosion resistance after plasma spraying and post-heat treatment as compared to as-received substrate. A significant decrease in contact angle and improvement in bioactivity (in terms of apatite deposition) were observed in TiO2-coated surface as compared to as-received Ti-6Al-4V.

Acoustic signature analysis of the interaction between a dc plasma jet and a suspension liquid jet

International Nuclear Information System (INIS)

Rat, V; Coudert, J F

2009-01-01

Suspension plasma spraying allows forming finely structured coatings by injecting suspensions of ceramic particles within a dc plasma jet. The electric arc motion in dc plasma torch is the main acoustic source which is modified by the injection of suspension. The analyses of cross-correlations between the arc voltage and the acoustic signal show a decrease in time propagations due to local cooling of the plasma jet when injecting suspensions. Moreover, power spectra highlight acoustic amplifications below a certain frequency threshold and attenuations above. A simplified model of the frequency acoustic response of a two-phase vaporizing mixture is used to interpret experimental measurements. These acoustic effects are due to the dynamics of thermal transfers between vaporizing liquid and plasma.

dc-plasma-sprayed electronic-tube device

Science.gov (United States)

Meek, T.T.

1982-01-29

An electronic tube and associated circuitry which is produced by dc plasma arc spraying techniques is described. The process is carried out in a single step automated process whereby both active and passive devices are produced at very low cost. The circuitry is extremely reliable and is capable of functioning in both high radiation and high temperature environments. The size of the electronic tubes produced are more than an order of magnitude smaller than conventional electronic tubes.

Process development for synthesis and plasma spray deposition of LaPO4 and YPO4 for nuclear applications

International Nuclear Information System (INIS)

Chakravarthy, Y.; Sreekumar, K.P.; Jayakumar, S.; Thiyagarajan, T.K.; Ananthapadmanabhan, P.V.; Das, A.K.; Gantayet, L.M.; Krishnan, K.

2009-01-01

Rare earth phosphates are geologically very stable and considered as potential matrix material for nuclear waste disposal and also for many high temperature thermal barrier and corrosion barrier applications involving molten metals. This paper focuses on developmental studies related to synthesis, thermal stability and plasma spray deposition of LaPO 4 and YPO 4 . The rare earth phosphates were synthesized by chemical method from their respective oxide materials using ortho phosphoric acid. The as-precipitated powders were converted to thermal spray grade powder by compaction, sintering and crushing. Thermal stability of these phosphates up to their melting point was determined by arc plasma melting, followed by X-ray diffraction. Results indicate that LaPO 4 and YPO 4 melt congruently without decomposition. Plasma spray deposition was carried out using the in-house 40 kW atmospheric plasma spray system. Adherent coatings could be deposited on various substrates by optimizing the plasma spray parameters. (author)

Deposition of porous cathodes using plasma spray technique for reduced-temperature SOFCs

Energy Technology Data Exchange (ETDEWEB)

Jankovic, J.; Hui, S.; Roller, J.; Kesler, O.; Xie, Y.; Maric, R.; Ghosh, D. [National Research Council of Canada, Vancouver, BC (Canada). Inst. for Fuel Cell Innovation

2005-07-01

Current techniques for Solid Oxide Fuel Cell (SOFC) materials deposition are often expensive and time-consuming. Plasma-spraying techniques provide higher deposition rates, short processing times and control over porosity and composition during deposition. Optimum plasma spraying for lanthanum based cathode materials were discussed. Plasma-spraying was used to deposit cathode materials onto ceramic and stainless steel substrates to obtain highly porous structures. Lanthanum cathode materials with composition of La{sub 0.6}Sr{sub 0.4}C{sub 0.2}Fe{sub 0.8}O{sub 3} were employed in the powder form. The powder was prepared from powder precursors with different power formers and binder levels, or from produced single-phase lanthanum powders. The (La{sub 0.8}Sr{sub 0.2}){sub 0.98}MnO{sub 3} cathode material was also processed for comparison purposes. The deposition process was developed to obtain coatings with good bond strength, porosity, film thickness and residual stresses. The phase and microstructure of deposited materials were characterized using X-Ray Diffraction and Scanning Electron Microscopy (SEM). It was concluded that good flow of the powder precursors is achieved by spraying 50-100 um particle size powders and using vibrating feeders. Further processing of the spraying powders was recommended. It was noted that oxide precursors showed greater reactivity among the precursors. The best precursor reactivity and coating morphology was obtained using 40 volume per cent of graphite pore former, incorporated into the precursor mixture during wet ball milling. It was concluded that higher power levels and larger distances between the plasma gun and the substrate result in coatings with the highest porosities and best phase compositions. 5 refs., 1 tab., 6 figs.

Study, analysis and design of plasma torch for the elimination of hospital wastes in Chile

International Nuclear Information System (INIS)

Diaz Ramirez, Ximena Jesus

2014-01-01

Within the field of new technologies in industry, the use of plasma is notable for its high speed of expansion and development. Currently one of its uses is the elimination of waste as it allows to avoid problems such as the formation of airborne byproducts and hazardous solids that represent a serious problem for the environment and human health. Plasma, when it is at extreme temperatures above 3,000 Celsius, causes inorganic waste to disintegrate and to vitrify on a solid residue while organic waste is converted into gases. Unlike any other thermal treatment of waste (incineration, gasification, pyrolysis, etc.) and because it is not a combustion process, but atomization of matter, no pollutant emissions into the atmosphere (dioxins and similar) or ash, there are only simple gases and an inert solid completely vitrified that can be used in the construction, for the obtaining of urban furniture, as decorative element, for example. The project proposes to develop an experimental device, laboratory plasma torch, to investigate its application in the reduction of hospital waste. It is expected to model, design and construct an experimental device that produces a plasma jet, whose temperature is adequate to perform hospital waste treatments at the laboratory level. The main objective of the project is to contribute to the generation of knowledge in the field of hospital waste reduction through the use of technological applications of plasmas, generating the necessary research for the study of art and technological development at the experimental level in the indicated field

Spray-dried plasma and fresh frozen plasma modulate permeability and inflammation in vitro in vascular endothelial cells

NARCIS (Netherlands)

Wataha, K.; Menge, T.; Deng, X.; Shah, A.; Bode, A.; Holcomb, J.B.; Potter, D.; Kozar, R.; Spinella, P.C.; Pati, S.

2013-01-01

BACKGROUND: After major traumatic injury, patients often require multiple transfusions of fresh frozen plasma (FFP) to correct coagulopathy and to reduce bleeding. A spray-dried plasma (SDP) product has several logistical benefits over FFP use in trauma patients with coagulopathy. These benefits

Oxidation Behavior of Titanium Carbonitride Coating Deposited by Atmospheric Plasma Spray Synthesis

Science.gov (United States)

Zhu, Lin; He, Jining; Yan, Dianran; Liao, Hanlin; Zhang, Nannan

2017-10-01

As a high-hardness and anti-frictional material, titanium carbonitride (TiCN) thick coatings or thin films are increasingly being used in many industrial fields. In the present study, TiCN coatings were obtained by atmospheric plasma spray synthesis or reactive plasma spray. In order to promote the reaction between the Ti particles and reactive gases, a home-made gas tunnel was mounted on a conventional plasma gun to perform the spray process. The oxidation behavior of the TiCN coatings under different temperatures in static air was carefully investigated. As a result, when the temperature was over 700 °C, the coatings suffered from serious oxidation, and finally they were entirely oxidized to the TiO2 phase at 1100 °C. The principal oxidation mechanism was clarified, indicating that the oxygen can permeate into the defects and react with TiCN at high temperatures. In addition, concerning the use of a TiCN coating in high-temperature conditions, the microhardness of the oxidized coatings at different treatment temperatures was also evaluated.

Deposition of Composite LSCF-SDC and SSC-SDC Cathodes by Axial-Injection Plasma Spraying

Science.gov (United States)

Harris, Jeffrey; Qureshi, Musab; Kesler, Olivera

2012-06-01

The performance of solid oxide fuel cell cathodes can be improved by increasing the number of electrochemical reaction sites, by controlling microstructures, or by using composite materials that consist of an ionic conductor and a mixed ionic and electronic conductor. LSCF (La0.6Sr0.4Co0.2Fe0.8O3-δ) and SSC (Sm0.5Sr0.5CoO3) cathodes were manufactured by axial-injection atmospheric plasma spraying, and composite cathodes were fabricated by mixing SDC (Ce0.8Sm0.2O1.9) into the feedstock powders. The plasma power was varied by changing the proportion of nitrogen in the plasma gas. The microstructures of cathodes produced with different plasma powers were characterized by scanning electron microscopy and gas permeation measurements. The deposition efficiencies of these cathodes were calculated based on the mass of the sprayed cathode. Particle surface temperatures were measured in-flight to enhance understanding of the relationship between spray parameters, microstructure, and deposition efficiency.

Plasma spraying of hard magnetic coatings based on Sm-Co alloys

International Nuclear Information System (INIS)

KrasnoyarskiyRabochiy prospect, Krasnoyarsk, 660014 (Russian Federation))" data-affiliation=" (Siberian State Aerospace University named after Academician M.F. Reshetnev 31 KrasnoyarskiyRabochiy prospect, Krasnoyarsk, 660014 (Russian Federation))" >Saunin, V N; KrasnoyarskiyRabochiy prospect, Krasnoyarsk, 660014 (Russian Federation))" data-affiliation=" (Siberian State Aerospace University named after Academician M.F. Reshetnev 31 KrasnoyarskiyRabochiy prospect, Krasnoyarsk, 660014 (Russian Federation))" >Telegin, S V

2015-01-01

Our research is focused on the formation of hard magnetic coatings by plasma spraying an arc-melted Sm-Co powder. We have studied basic magnetic characteristics depending on the components ratio in the alloy. A sample with a 40 wt.% Sm coating exhibits the highest coercive force (63 kOe) as compared to near-to-zero coercive force in the starting powder. X-ray structure analysis of the starting alloy and the coating reveals that the amount of SmCo 5 phase in the sprayed coating increases occupying up to 2/3 of the sample. We have also studied temperature dependence of the coating and have been able to obtain plasma sprayed permanent magnets operating within the temperature range from -100 to +500 °C. The technique used does not involve any additional thermal treatment and allows a coating to be formed right on the magnetic conductor surface irrespective of the conductor geometry

Effects of RF plasma treatment on spray-pyrolyzed copper oxide films on silicon substrates

Science.gov (United States)

Madera, Rozen Grace B.; Martinez, Melanie M.; Vasquez, Magdaleno R., Jr.

2018-01-01

The effects of radio-frequency (RF) argon (Ar) plasma treatment on the structural, morphological, electrical and compositional properties of the spray-pyrolyzed p-type copper oxide films on n-type (100) silicon (Si) substrates were investigated. The films were successfully synthesized using 0.3 M copper acetate monohydrate sprayed on precut Si substrates maintained at 350 °C. X-ray diffraction revealed cupric oxide (CuO) with a monoclinic structure. An apparent improvement in crystallinity was realized after Ar plasma treatment, attributed to the removal of residues contaminating the surface. Scanning electron microscope images showed agglomerated monoclinic grains and revealed a reduction in size upon plasma exposure induced by the sputtering effect. The current-voltage characteristics of CuO/Si showed a rectifying behavior after Ar plasma exposure with an increase in turn-on voltage. Four-point probe measurements revealed a decrease in sheet resistance after plasma irradiation. Fourier transform infrared spectral analyses also showed O-H and C-O bands on the films. This work was able to produce CuO thin films via spray pyrolysis on Si substrates and enhancement in their properties by applying postdeposition Ar plasma treatment.

Creep behavior of the titanium alloy with zirconia plasma sprayed coating

International Nuclear Information System (INIS)

Reis, D.A.P.; Moura Neto, C.; Couto, A.A.

2009-01-01

The proposal of this research has been the study of the plasma spayed coating on creep of the Ti-6Al-4V, focusing on the determination of the experimental parameters related to the first and second creep stages. Yttria (8 wt %) stabilized zirconia (YSZ) (Metco 204B-NS) with CoNiCrAlY ( AMDRY 995C) has been plasma sprayed coated on Ti-6Al-4V substrate. Creep tests with constant load had been done on Ti-6Al-4V coated samples, the stress level was from 250 to 319 MPa at 600 deg C. Highest values of t p and the decrease of the second stage rate had shown a better creep resistance on coated sample. Results indicate that the coated sample was greater than uncoated sample, thus the plasma sprayed coating prevent the sample oxidation efficiently. (author)

Laser induced plasma methodology for ignition control in direct injection sprays

International Nuclear Information System (INIS)

Pastor, José V.; García-Oliver, José M.; García, Antonio; Pinotti, Mattia

2016-01-01

Highlights: • Laser Induced Plasma Ignition system is designed and applied to a Diesel Spray. • A method for quantification of the system effectiveness and reliability is proposed. • The ignition system is optimized in atmospheric and engine-like conditions. • Higher system effectiveness is reached with higher ambient density. • The system is able to stabilize Diesel combustion compared to auto-ignition cases. - Abstract: New combustion modes for internal combustion engines represent one of the main fields of investigation for emissions control in transportation Industry. However, the implementation of lean fuel mixture condition and low temperature combustion in real engines is limited by different unsolved practical issues. To achieve an appropriate combustion phasing and cycle-to-cycle control of the process, the laser plasma ignition system arises as a valid alternative to the traditional electrical spark ignition system. This paper proposes a methodology to set-up and optimize a laser induced plasma ignition system that allows ensuring reliability through the quantification of the system effectiveness in the plasma generation and positional stability, in order to reach optimal ignition performance. For this purpose, experimental tests have been carried out in an optical test rig. At first the system has been optimized in an atmospheric environment, based on the statistical analysis of the plasma records taken with a high speed camera to evaluate the induction effectiveness and consequently regulate and control the system settings. The same optimization method has then been applied under engine-like conditions, analyzing the effect of thermodynamic ambient conditions on the plasma induction success and repeatability, which have shown to depend mainly on ambient density. Once optimized for selected engine conditions, the laser plasma induction system has been used to ignite a direct injection Diesel spray, and to compare the evolution of combustion

Thin films by metal-organic precursor plasma spray

International Nuclear Information System (INIS)

Schulz, Douglas L.; Sailer, Robert A.; Payne, Scott; Leach, James; Molz, Ronald J.

2009-01-01

While most plasma spray routes to coatings utilize solids as the precursor feedstock, metal-organic precursor plasma spray (MOPPS) is an area that the authors have investigated recently as a novel route to thin film materials. Very thin films are possible via MOPPS and the technology offers the possibility of forming graded structures by metering the liquid feed. The current work employs metal-organic compounds that are liquids at standard temperature-pressure conditions. In addition, these complexes contain chemical functionality that allows straightforward thermolytic transformation to targeted phases of interest. Toward that end, aluminum 3,5-heptanedionate (Al(hd) 3 ), triethylsilane (HSi(C 2 H 5 ) 3 or HSiEt 3 ), and titanium tetrakisdiethylamide (Ti(N(C 2 H 5 ) 2 ) 4 or Ti(NEt 2 ) 4 ) were employed as precursors to aluminum oxide, silicon carbide, and titanium nitride, respectively. In all instances, the liquids contain metal-heteroatom bonds envisioned to provide atomic concentrations of the appropriate reagents at the film growth surface, thus promoting phase formation (e.g., Si-C bond in triethylsilane, Ti-N bond in titanium amide, etc.). Films were deposited using a Sulzer Metco TriplexPro-200 plasma spray system under various experimental conditions using design of experiment principles. Film compositions were analyzed by glazing incidence x-ray diffraction and elemental determination by x-ray spectroscopy. MOPPS films from HSiEt 3 showed the formation of SiC phase but Al(hd) 3 -derived films were amorphous. The Ti(NEt 2 ) 4 precursor gave MOPPS films that appear to consist of nanosized splats of TiOCN with spheres of TiO 2 anatase. While all films in this study suffered from poor adhesion, it is anticipated that the use of heated substrates will aid in the formation of dense, adherent films.

Short torch design for direct liquid sample introduction using conventional and micro-nebulizers for plasma spectrometry

Science.gov (United States)

Montaser, Akbar [Potomac, MD; Westphal, Craig S [Landenberg, PA; Kahen, Kaveh [Montgomery Village, MD; Rutkowski, William F [Arlington, VA

2008-01-08

An apparatus and method for providing direct liquid sample introduction using a nebulizer are provided. The apparatus and method include a short torch having an inner tube and an outer tube, and an elongated adapter having a cavity for receiving the nebulizer and positioning a nozzle tip of the nebulizer a predetermined distance from a tip of the outer tube of the short torch. The predetermined distance is preferably about 2-5 mm.

Production of ceramic formed parts by means of plasma spraying

International Nuclear Information System (INIS)

Kirner, K.

1989-01-01

Open and closed pipes and tubes, nozzles and crucibles, conical parts and other molded articles of ceramic materials such as aluminium oxide, magnesium-aluminium spinel, zirconium oxide, zirconium silicate and special ceramics can be fabricated by spray application to a core which is afterwards removed. Because at the same time these are mainly high temperature materials and high temperature application areas, plasma spraying is preferred. The process and examples of application are described, the advantages and disadvantages are pointed out. (orig.) [de

Preparation and in vitro evaluation of plasma-sprayed bioactive akermanite coatings

International Nuclear Information System (INIS)

Yi, Deliang; Wu, Chengtie; Chang, Jiang; Ma, Xubing; Ji, Heng; Zheng, Xuebin

2012-01-01

Bioactive ceramic coatings on titanium (Ti) alloys play an important role in orthopedic applications. In this study, akermanite (Ca 2 MgSi 2 O 7 ) bioactive coatings are prepared through a plasma spraying technique. The bonding strength between the coatings and Ti-6Al-4V substrates is around 38.7–42.2 MPa, which is higher than that of plasma sprayed hydroxyapatite (HA) coatings reported previously. The prepared akermanite coatings reveal a distinct apatite-mineralization ability in simulated body fluid. Furthermore, akermanite coatings support the attachment and proliferation of rabbit bone marrow mesenchymal stem cells (BMSCs). The proliferation rate of BMSCs on akermanite coatings is obviously higher than that on HA coatings. (paper)

Nanostructure of plasma-sprayed hydroxyapatite coating

International Nuclear Information System (INIS)

Suvorova, E.I.; Klechkovskaya, V.V.; Bobrovsky, V.V.; Khamchukov, Yu.D.; Klubovich, V.V.

2003-01-01

Calcium phosphate coatings were studied by high-resolution transmission microscopy, microdiffraction, and X-ray energy-dispersive spectroscopy. Coatings were prepared by spraying hydroxyapatite targets onto copper, nickel, and chromium substrates and onto NaCl and BaF 2 single crystals in an argon plasma at a gas pressure of ∼1 Pa; the sputter power was about 200 W; and the RF-generator frequency was 13.56 MHz. Under the conditions used, thin layers of nanocrystalline hydroxyapatite were formed regardless of the nature of the substrate

On reactive suspension plasma spraying of calcium titanate

Czech Academy of Sciences Publication Activity Database

Kotlan, Jiří; Pala, Zdeněk; Mušálek, Radek; Ctibor, Pavel

2016-01-01

Roč. 42, č. 3 (2016), s. 4607-4615 ISSN 0272-8842 R&D Projects: GA ČR GA15-12145S Institutional support: RVO:61389021 Keywords : Suspensions * X-raymethods * Perovskites * Substrates * Suspension plasma spraying Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 2.986, year: 2016 http://www.sciencedirect.com/science/article/pii/S0272884215022646

Heavy duty plasma spray gun

International Nuclear Information System (INIS)

Irons, G.C.; Klein, J.F.; Lander, R.D.; Thompson, H.C.; Trapani, R.D.

1984-01-01

A heavy duty plasma spray gun for extended industrial service is disclosed. The gun includes a gas distribution member made of a material having a coefficient of expansion different from that of the parts surrounding it. The gas distribution member is forcibly urged by a resilient member such as a coiled spring against a seal so as to assure the plasma gas is introduced into the gun arc in a manner only defined by the gas distribution member. The gun has liquid cooling for the nozzle (anode) and the cathode. Double seals are provided between the coolant and the arc region and a vent is provided between the seals which provides an indication when a seal has failed. Some parts of the gun are electrically isolated from others by an intermediate member which is formed as a sandwich of two rigid metal face pieces and an insulator disposed between them. The metal face pieces provide a rigid body to attach the remaining parts in proper alignment therewith

Phase stabilization in plasma sprayed BaTiO3

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Seiner, Hanuš; Sedláček, J.; Pala, Zdeněk; Vaněk, Přemysl

2013-01-01

Roč. 39, č. 5 (2013), s. 5039-5048 ISSN 0272-8842 R&D Projects: GA ČR(CZ) GA101/09/0702 Institutional support: RVO:61389021 ; RVO:61388998 ; RVO:68378271 Keywords : Spectroscopy * BaTiO3 * Plasma spraying * Spark plasma sintering Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass; BJ - Thermodynamics (UT-L); JH - Ceramics, Fire-Resistant Materials and Glass (FZU-D) Impact factor: 2.086, year: 2013 http://www.sciencedirect.com/science/article/pii/S0272884212013582

Method for atmospheric pressure reactive atom plasma processing for surface modification

Science.gov (United States)

Carr, Jeffrey W [Livermore, CA

2009-09-22

Reactive atom plasma processing can be used to shape, polish, planarize and clean the surfaces of difficult materials with minimal subsurface damage. The apparatus and methods use a plasma torch, such as a conventional ICP torch. The workpiece and plasma torch are moved with respect to each other, whether by translating and/or rotating the workpiece, the plasma, or both. The plasma discharge from the torch can be used to shape, planarize, polish, and/or clean the surface of the workpiece, as well as to thin the workpiece. The processing may cause minimal or no damage to the workpiece underneath the surface, and may involve removing material from the surface of the workpiece.

Systematic Investigation on the Influence of Spray Parameters on the Mechanical Properties of Atmospheric Plasma-Sprayed YSZ Coatings

Science.gov (United States)

Mutter, Markus; Mauer, Georg; Mücke, Robert; Guillon, Olivier; Vaßen, Robert

2018-04-01

In the atmospheric plasma spray (APS) process, micro-sized ceramic powder is injected into a thermal plasma where it is rapidly heated and propelled toward the substrate. The coating formation is characterized by the subsequent impingement of a large number of more or less molten particles forming the so-called splats and eventually the coating. In this study, a systematic investigation on the influence of selected spray parameters on the coating microstructure and the coating properties was conducted. The investigation thereby comprised the coating porosity, the elastic modulus, and the residual stress evolution within the coating. The melting status of the particles at the impingement on the substrate in combination with the substrate surface condition is crucial for the coating formation. Single splats were collected on mirror-polished substrates for selected spray conditions and evaluated by identifying different types of splats (ideal, distorted, weakly bonded, and partially molten) and their relative fractions. In a previous study, these splat types were evaluated in terms of their effect on the above-mentioned coating properties. The particle melting status, which serves as a measure for the particle spreading behavior, was determined by in-flight particle temperature measurements and correlated to the coating properties. It was found that the gun power and the spray distance have a strong effect on the investigated coating properties, whereas the feed rate and the cooling show minor influence.

Development of Carbon-14 Waste Destruction and Recovery System Using AC Plasma Torch Technology Final Report CRADA No. TC02108.0

Energy Technology Data Exchange (ETDEWEB)

Althouse, P. [Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States); McKannay, R. H. [Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)

2017-08-15

This was a collaborative effort between Lawrence Livermore National Security, LLC as manager and operator of Lawrence Livermore National Laboratory (LLNL) and ISOFLEX USA (ISOFLEX), to 1) develop and test a prototype waste destruction system ("System") using AC plasma torch technology to break down and drastically reduce the volume of Carbon-14 (C-14) contaminated medical laboratory wastes while satisfying all environmental regulations, and 2) develop and demonstrate methods for recovering 99%+ of the carbon including the C-14 allowing for possible re-use as a tagging and labeling tool in the biomedical industry.

Nonlinear Stress-Strain Behavior of Plasma Sprayed Ceramic Coatings

Czech Academy of Sciences Publication Activity Database

Nohava, Jiří; Kroupa, František

2005-01-01

Roč. 50, č. 3 (2005), s. 251-262 ISSN 0001-7043 R&D Projects: GA AV ČR KSK1010104 Institutional research plan: CEZ:AV0Z20430508 Keywords : plasma spraying * ceramic coatings * Young’s modulus * nonlinear behavior * microcracks Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass

DEVELOPMENT OF COMPLEX EQUIPMENT FOR PLASMA SPRAY CERAMIC COATINGS

Directory of Open Access Journals (Sweden)

V. V. Okovity

2017-01-01

Full Text Available Develop a set equipment for plasma forming ceramic coatings. The article presents characteristics and parameters of the developed complex equipment for formation of plasma ceramic coatings as well as results of its testing. Methods of research is based on studies of structural elements composite plasma coatings system ZrO2 – Y2O3  obtained  using  developed complex equipment. One of the most effective ways to protect the components from high temperature corrosion and oxidation is formation on the surface of plasma thermal barrier coatings. For thermal barrier coating has very strict requirements: сharacterized by a smooth change of physico-mechanical properties (porosity, microhardness, elastic modulus in the cross section of the metal substrate to the outer ceramic layer; to withstand multiple cycles of thermal cycling from room temperature to the operating temperature; to maintain gastightness under operating conditions and thus ensure a sufficiently high level of adhesive strength. For realization of new technological schemes applying thermal barrier coatings with high operational characteristics was developed, patented and manufactured a range of new equipment. The experiments show that authors developed PBG-1 plasmatron and powder feeder PPBG-04 have at least 2–3 times the service life during the deposition of ceramic materials compared to the standard equipment of the company "Plasma-Technik", by changing the structure of the cathode-anode plasma torch assembly and construction of the delivery unit of the feeder to facilitate the uniform supply of the powder into the plasma jet and the best of his penetration. The result is better plasma coatings with improved operational characteristics: adhesion strength is increased to 1.3–2 times, material utilization in 1.5–1.6 times microhardness 1.2–1.4 times the porosity is reduced by 2–2.5 times.

Kinematic Optimization of Robot Trajectories for Thermal Spray Coating Application

Science.gov (United States)

Deng, Sihao; Liang, Hong; Cai, Zhenhua; Liao, Hanlin; Montavon, Ghislain

2014-12-01

Industrial robots are widely used in the field of thermal spray nowadays. Due to their characteristics of high-accuracy and programmable flexibility, spraying on complex geometrical workpieces can be realized in the equipped spray room. However, in some cases, the robots cannot guarantee the process parameters defined by the robot movement, such as the scanning trajectory, spray angle, relative speed between the torch and the substrate, etc., which have distinct influences on heat and mass transfer during the generation of any thermally sprayed coatings. In this study, an investigation on the robot kinematics was proposed to find the rules of motion in a common case. The results showed that the motion behavior of each axis of robot permits to identify the motion problems in the trajectory. This approach allows to optimize the robot trajectory generation in a limited working envelop. It also minimizes the influence of robot performance to achieve a more constant relative scanning speed which is represented as a key parameter in thermal spraying.

Plasma spraying of Fe-Cr-Al alloy powder

Czech Academy of Sciences Publication Activity Database

Voleník, Karel; Leitner, J.; Kolman, Blahoslav Jan; Písačka, Jan; Schneeweiss, Oldřich

2008-01-01

Roč. 46, č. 1 (2008), s. 17-25 ISSN 0023-432X R&D Projects: GA AV ČR IAA1041404 Institutional research plan: CEZ:AV0Z20430508; CEZ:AV0Z20410507 Keywords : Fe-Cr-Al alloy powder * plasma spraying * oxidation * vaporization * composition changes Subject RIV: JK - Corrosion ; Surface Treatment of Materials Impact factor: 1.345, year: 2007

Preventing Clogging In A Vacuum Plasma Spray Gun

Science.gov (United States)

Krotz, Phillip D.; Daniel, Ronald L., Jr.; Davis, William M.

1994-01-01

Modification of powder-injection ports enables lengthy, high-temperature deposition operations. Graphite inserts prevent clogging of ports through which copper powder injected into vacuum plasma spray (VPS) gun. Graphite liners eliminate need to spend production time refurbishing VPS gun, reducing cost of production and increasing productivity. Concept also applied to other material systems used for net-shape fabrication via VPS.

Effect of substrate and cathode parameters on the properties of suspension plasma sprayed solid oxide fuel cell electrolytes

Energy Technology Data Exchange (ETDEWEB)

Waldbillig, D.; Tang, Z.; Burgess, A. [British Columbia Univ., Vancouver, BC (Canada); Kesler, O. [Toronto Univ., ON (Canada)

2008-07-01

An axial injection suspension plasma spray system has been used to produce layers of fully stabilized yttriastabilized zirconia (YSZ) that could be used as solid oxide fuel cell (SOFC) electrolytes. Suspension plasma spraying is a promising technique for the rapid production of coatings with fine microstructures and controlled porosity without requiring a post-deposition heat treatment. This new manufacturing technique to produce SOFC active layers requires the build up of a number of different plasma sprayed SOFC functional layers (cathode, electrolyte and anode) sequentially on top of each other. To understand the influence of the substrate and previouslydeposited coating layers on subsequent coating layer properties, YSZ layers were deposited on top of plasma sprayed composite lanthanum strontium manganite (LSM)/YSZ cathode layers that were first deposited on porous ferritic stainless steel substrates. Three layer half cells consisting of the porous steel substrate, composite cathode, and suspension plasma sprayed electrolyte layer were then characterized. A systematic study was performed in order to investigate the effect of parameters such as substrate and cathode layer roughness, substrate surface pore size, and cathode microstructure and thickness on electrolyte deposition efficiency, cathode and electrolyte permeability, and layer microstructure. (orig.)

Properties of plasma flames sustained by microwaves and burning hydrocarbon fuels

International Nuclear Information System (INIS)

Hong, Yong Cheol; Uhm, Han Sup

2006-01-01

Plasma flames made of atmospheric microwave plasma and a fuel-burning flame were presented and their properties were investigated experimentally. The plasma flame generator consists of a fuel injector and a plasma flame exit connected in series to a microwave plasma torch. The plasma flames are sustained by injecting hydrocarbon fuels into a microwave plasma torch in air discharge. The microwave plasma torch in the plasma flame system can burn a hydrocarbon fuel by high-temperature plasma and high atomic oxygen density, decomposing the hydrogen and carbon containing fuel. We present the visual observations of the sustained plasma flames and measure the gas temperature using a thermocouple device in terms of the gas-fuel mixture and flow rate. The plasma flame volume of the hydrocarbon fuel burners was more than approximately 30-50 times that of the torch plasma. While the temperature of the torch plasma flame was only 868 K at a measurement point, that of the diesel microwave plasma flame with the addition of 0.019 lpm diesel and 30 lpm oxygen increased drastically to about 2280 K. Preliminary experiments for methane plasma flame were also carried out, measuring the temperature profiles of flames along the radial and axial directions. Finally, we investigated the influence of the microwave plasma on combustion flame by observing and comparing OH molecular spectra for the methane plasma flame and methane flame only

High temperature tribological properties of plasma-sprayed metallic coatings containing ceramic particles

International Nuclear Information System (INIS)

Dallaire, S.; Legoux, J.G.

1995-01-01

For sealing a moving metal component with a dense silica-based ceramic pre-heated at 800 C, coatings with a low coefficient of friction and moderate wear loss are required. As reported previously, plasma-sprayed coatings containing solid lubricants could reduce sliding wear in high-temperature applications. Plasma-sprayed metal-based coatings containing ceramic particles have been considered for high temperature sealing. Selected metal powders (NiCoCrAlY, CuNi, CuNiIn, Ag, Cu) and ceramic particles (boron nitride, Zeta-B ceramic) were agglomerated to form suitable spray powders. Plasma-sprayed composite coatings and reference materials were tested in a modified pin-on-disc apparatus in which the stationary disc consisted of a dense silica-based ceramic piece initially heated at 800 C and allowed to cool down during tests. The influence of single exposure and repeated contacts with a dense silica-based ceramic material pre-heated to 800 C on the coefficient of friction, wear loss and damage to the ceramic piece was evaluated. Being submitted to a single exposure at high temperature, coatings containing malleable metals such as indium, silver and copper performed well. The outstanding tribological characteristics of the copper-Zeta-B ceramic coating was attributed to the formation of a glazed layer on the surface of this coating which lasted over exposures to high temperature. This glazed layer, composed of fine oxidation products, provided a smooth and polished surface and helped maintaining the coefficient of friction low

Functionally Graded Materials using Plasma Spray with Nano Structured Ceramic

International Nuclear Information System (INIS)

Sioh, E L; Tok, A I Y

2013-01-01

In this paper, nano structured FGM was fabricated using DC plasma spray technique. Nano structured and micro structured powder were used as the feeding powder with steel substrate. The spray parameters was optimized and characterisation of nano-ceramic FGM and micro-ceramic FGM were done using bending test and micro-hardness test. Experimental results have shown that the nano-structured FGM exhibit 20% improvement flexure strength and 10% in hardness. A comparison was made between sintered micro ceramic tile and nano ceramic FGM using simple drop test method.

The structure and thermal properties of plasma-sprayed beryllium for the International Thermonuclear Experimental Reactor (ITER)

International Nuclear Information System (INIS)

Castro, R.G.; Bartlett, A.; Elliott, K.E.; Hollis, K.J.

1996-01-01

Plasma spraying is being studied for in situ repair of damaged Be and W plasma facing surfaces for ITER, the next generation magnetic fusion energy device, and is also being considered for fabricating Be and W plasma-facing components for the first wall of ITER. Investigators at LANL's Beryllium Atomization and Thermal Spray Facility have concentrated on investigating the structure-property relation between as-deposited microstructures of plasma sprayed Be coatings and resulting thermal properties. In this study, the effect of initial substrate temperature on resulting thermal diffusivity of Be coatings and the thermal diffusivity at the coating/Be substrate interface (interface thermal resistance) was investigated. Results show that initial Be substrate temperatures above 600 C can improve the thermal diffusivity of the Be coatings and minimize any thermal resistance at the interface between the Be coating and Be substrate

The effect of processing parameters on plasma sprayed beryllium for fusion applications

International Nuclear Information System (INIS)

Castro, R.G.; Stanek, P.W.; Jacobson, L.A.; Cowgill, D.F.; Snead, L.L.

1993-01-01

Plasma spraying is being investigated as a potential coating technique for applying thin (0.1--5mm) layers of beryllium on plasma facing surfaces of blanket modules in ITER and also as an in-situ repair technique for repairing eroded beryllium surfaces in high heat flux divertor regions. High density spray deposits (>98% of theoretical density) of beryllium will be required in order to maximize the thermal conductivity of the beryllium coatings. A preliminary investigation was done to determine the effect of various processing parameters (particle size, particle morphology, secondary gas additions and reduced chamber pressure) on the as-deposited density of beryllium. The deposits were made using spherical beryllium feedstock powder which was produced by centrifugal atomization at Los Alamos National Laboratory (LANL). Improvements in the as-deposited densities and deposit efficiencies of the beryllium spray deposits will be discussed along with the corresponding thermal conductivity and outgassing behavior of these deposits

The effect of processing parameters on plasma sprayed beryllium for fusion applications

International Nuclear Information System (INIS)

Castro, R.G.; Stanek, P.W.; Jacobson, L.W.; Cowgill, D.F.

1993-01-01

Plasma spraying is being investigated as a potential coating technique for applying thin (0.1-5mm) layers of beryllium on plasma facing surfaces of blanket modules in ITER and also as an in-situ repair technique for repairing eroded beryllium surfaces in high heat flux divertor regions. High density spray deposits (>98% of theoretical density) of beryllium will be required in order to maximize the thermal conductivity of the beryllium coatings. A preliminary investigation was done to determine the effect of various processing parameters (particle size, particle morphology, secondary gas additions and reduced chamber pressure) on the as-deposited density of beryllium. The deposits were made using spherical beryllium feedstock powder which was produced by centrifugal atomization at Los Alamos National Laboratory (LANL). Improvements in the as-deposited densities and deposit efficiencies of the beryllium spray deposits will be discussed along with the corresponding thermal conductivity and outgassing behavior of these deposits. (orig.)

Plasma vitrification program for radioactive waste treatment

International Nuclear Information System (INIS)

Hung, Tsungmin; Tzeng, Chinchin; Kuo, Pingchun

1998-01-01

In order to treat radioactive wastes effectively and solve storage problems, INER has developed the plasma arc technology and plasma process for various waste forms for several years. The plasma vitrification program is commenced via different developing stages through nine years. It includes (a) development of non-transferred DC plasma torch, (b) establishment of a lab-scale plasma system with home-made 100kW non-transferred DC plasma torch, (c) testing of plasma vitrification of simulated radioactive wastes, (d) establishment of a transferred DC plasma torch delivering output power more than 800 kW, (e) study of NOx reduction process for the plasma furnace, (f) development of a pilot-scale plasma melting furnace to verify the vitrification process, and (g) constructing a plasma furnace facility in INER. The final goal of the program is to establish a plasma processing plant with capacity of 250 kg/hr to treat the low-level radioactive wastes generated from INER itself and domestic institutes due to isotope applications. (author)

Studies on Nanocrystalline TiN Coatings Prepared by Reactive Plasma Spraying

Directory of Open Access Journals (Sweden)

Dong Yanchun

2008-01-01

Full Text Available Titanium nitride (TiN coatings with nanostructure were prepared on the surface of 45 steel (Fe-0.45%C via reactive plasma spraying (denoted as RPS Ti powders using spraying gun with self-made reactive chamber. The microstructural characterization, phases constitute, grain size, microhardness, and wear resistance of TiN coatings were systematically investigated. The grain size was obtained through calculation using the Scherrer formula and observed by TEM. The results of X-ray diffraction and electron diffraction indicated that the TiN is main phase of the TiN coating. The forming mechanism of the nano-TiN was characterized by analyzing the SEM morphologies of surface of TiN coating and TiN drops sprayed on the surface of glass, and observing the temperature and velocity of plasma jet using Spray Watch. The tribological properties of the coating under nonlubricated condition were tested and compared with those of the AISI M2 high-speed steel and Al2O3 coating. The results have shown that the RPS TiN coating presents better wear resistance than the M2 high-speed steel and Al2O3 coating under nonlubricated condition. The microhardness of the cross-section and longitudinal section of the TiN coating was tested. The highest hardness of the cross-section of TiN coating is 1735.43HV100 g.

Development of process maps for plasma spray: case study for molybdenum

International Nuclear Information System (INIS)

Sampath, S.; Jiang, X.; Kulkarni, A.; Matejicek, J.; Gilmore, D.L.; Neiser, R.A.

2003-01-01

A schematic representation referred to as 'process maps' examines the role of process variables on the properties of plasma-sprayed coatings. Process maps have been developed for air plasma spraying of molybdenum. Experimental work was done to investigate the importance of such spray parameters as gun current, primary gas flow, auxiliary gas flow, and powder carrier gas flow. In-flight particle temperatures and velocities were measured and diameters estimated in various areas of the spray plume. Empirical models were developed relating the input parameters to the in-flight particle characteristics. Molybdenum splats and coatings were produced at three distinct process conditions identified from the first-order process map experiments. In addition, substrate surface temperature during deposition was treated as a variable. Within the tested range, modulus, hardness and thermal conductivity increases with particle velocity, while oxygen content and porosity decreases. Increasing substrate deposition temperature resulted in dramatic improvement in coating thermal conductivity and modulus, while simultaneously increasing coating oxide content. Indentation reveals improved fracture resistance for the coatings prepared at higher substrate temperature. Residual stress was significantly affected by substrate temperature, although not to a great extent by particle conditions within the investigated parameter range. Coatings prepared at high substrate temperature with high-energy particles suffered considerably less damage in a wear test. The mechanisms behind these changes are discussed within the context relational maps, which have been proposed

Tungsten oxide coatings deposited by plasma spray using powder and solution precursor for detection of nitrogen dioxide gas

Energy Technology Data Exchange (ETDEWEB)

Zhang, Chao, E-mail: zhangc@yzu.edu.cn [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); Wang, Jie [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); Geng, Xin [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); College of Chemistry and Chemical Engineering, Yangzhou University, Yangzhou 225002 (China)

2016-05-25

Increasing attention has been paid on preparation methods for resistive-type gas sensors based on semiconductor metal oxides. In this work, tungsten oxide (WO{sub 3}) coatings were prepared on alumina substrates and used as gas sensitive layers. The coatings were deposited by atmospheric plasma spray using powder, solution precursor, or a combination of both. Tungsten oxide powder through a powder port and ammonium tungstate aqueous solution through a liquid port were injected into plasma stream respectively or together to deposit WO{sub 3} coatings. Phase structures in the coatings were characterized by X-ray diffraction analyzer. The field-emission scanning electron microscopy images confirmed that the coatings were in microstructure, nanostructure or micro-nanostructure. The sensing properties of the sensors based on the coatings exposed to 1 ppm nitrogen dioxide gas were characterized in a home-made instrument. Sensing properties of the coatings were compared and discussed. The influences of gas humidity and working temperature on the sensor responses were further studied. - Highlights: • Porous gas sensitive coatings were deposited by plasma spray using powder and solution precursor. • Crystallized WO{sub 3} were obtained through hybrid plasma spray plus a pre-conditioned step. • Plasma power had an important influence on coating microstructure. • The particle size of atmospheric plasma-sprayed microstructured coating was stable. • Solution precursor plasma-sprayed WO{sub 3} coatings had nanostructure and showed good responses to 1 ppm NO{sub 2}.

Metastable phases in yttrium oxide plasma spray deposits and their effect on coating properties

International Nuclear Information System (INIS)

Gourlaouen, V.; Schnedecker, G.; Boncoeur, M.; Lejus, A.M.; Collongues, R.

1993-01-01

Yttrium oxide coatings were obtained by plasma spray. Structural investigations on these deposits show that, due to the drastic conditions of this technique, a minor monoclinic B phase is formed in the neighborhood of the major cubic C form. The authors discuss here the influence of different plasma spray parameters on the amount of the B phase formed. They describe also the main properties of Y 2 O 3 B and C phases in these deposits such as structural characteristics, thermal stability and mechanical behavior

Cavitation Erosion of Plasma -sprayed Coatings

International Nuclear Information System (INIS)

Kim, J. J.; Park, J. S.; Jeon, S. B.

1991-01-01

Tungsten Carbide, chromium carbide and chromium oxide coatings were obtained on a 304 stainless steel substrate by plasma spraying technique. The coated samples were exposed to cavitation generated in distilled water by a 20KHz ultrasonic horn. The results of investigation reveal that all the samples tested are significantly eroded even within ten minutes of exposure, indicative of a short incubation period. The eroded surfaces can be characterized as having large pits and flat smooth areas. The latter may be associated with the poor cohesive strength of the coatings, which leads to the failures between individual lamellae

Plasma-Sprayed Titanium Patterns for Enhancing Early Cell Responses

Science.gov (United States)

Shi, Yunqi; Xie, Youtao; Pan, Houhua; Zheng, Xuebin; Huang, Liping; Ji, Fang; Li, Kai

2016-06-01

Titanium coating has been widely used as a biocompatible metal in biomedical applications. However, the early cell responses and long-term fixation of titanium implants are not satisfied. To obviate these defects, in this paper, micro-post arrays with various widths (150-1000 μm) and intervals (100-300 μm) were fabricated on the titanium substrate by template-assisted plasma spraying technology. In vitro cell culture experiments showed that MC3T3-E1 cells exhibited significantly higher osteogenic differentiation as well as slightly improved adhesion and proliferation on the micro-patterned coatings compared with the traditional one. The cell number on the pattern with 1000 µm width reached 130% after 6 days of incubation, and the expressions of osteopontin (OPN) as well as osteocalcin (OC) were doubled. No obvious difference was found in cell adhesion on various size patterns. The present micro-patterned coatings proposed a new modification method for the traditional plasma spraying technology to enhance the early cell responses and convenience for the bone in-growth.

Characterization of Fe-based alloy coating deposited by supersonic plasma spraying

International Nuclear Information System (INIS)

Piao, Zhong-yu; Xu, Bin-shi; Wang, Hai-dou; Wen, Dong-hui

2013-01-01

Highlights: • Fe-based coating exhibited few oxides, high density and bond strength. • Amorphous/nanocrystalline phases were found in the coating. • Formation mechanism of excellent coating was investigated. -- Abstract: The objective of the present study is to characterize the Fe-based alloy coating deposited by the supersonic plasma spraying process. The condition of the melting particles was in situ monitored. The microstructure of the coating was examined by scanning electron microscope and high resolution transmission electron microscope. The phase composition was examined by X-ray diffraction. The microhardness and porosity were also measured, respectively. Results show the prepared coatings have excellent properties, such as few oxides, high microhardness and a low porosity amount. At the same time, a mass of amorphous/nanocrystalline phases was found in the coating. The mechanism of the formation of amorphous/nanocrystalline phases was investigated. The appropriate material composition of spraying material and flash set process of plasma spraying are the key factors. Moreover, the mechanism for oxidation resistance is also investigated, where the separation between melting metal and oxygen by the formation of SiO 2 films is the key factor

Wet Slurry Abrasion Tests of Ceramic Coatings Deposited by Water-Stabilized Plasma Spraying

Czech Academy of Sciences Publication Activity Database

Nohava, Jiří

2003-01-01

Roč. 48, č. 2 (2003), s. 203-214 ISSN 0001-7043 R&D Projects: GA ČR GA106/01/0094 Institutional research plan: CEZ:AV0Z2043910 Keywords : plasma spraying, wear resistence, ceramic coating Subject RIV: BL - Plasma and Gas Discharge Physics

Bond strength of plasma sprayed ceramic coatings on phosphate steels

Czech Academy of Sciences Publication Activity Database

Pokorný, P.; Mastný, L.; Sýkora, V.; Pala, Zdeněk; Brožek, Vlastimil

2015-01-01

Roč. 54, č. 2 (2015), s. 411-414 ISSN 0543-5846 R&D Projects: GA ČR(CZ) GAP108/12/1872 Institutional support: RVO:61389021 Keywords : phosphating * plasma spraying * ceramic coatings * corrosion * bond strength Subject RIV: CA - Inorganic Chemistry Impact factor: 0.959, year: 2014

Analysis of bauxite by inductively coupled plasma-atomic emission spectroscopy

Science.gov (United States)

Barnes, Ramon M.; Mahanti, Himansu S.

Methods are described for the analysis of bauxite by inductively coupled plasma (ICP) emission spectroscopy. Bauxite samples were dissolved either in HCl, HNO 3, and HF at 160°C in all-PTFE bomb or fused with NaOH. Spectral lines were selected after examination of experimental wavelength scans at each potential analyte wavelength. Limits of detection, background equivalent concentration, and analytical figures of merit were established. The accuracy of the method was confirmed by determining 17 elements in NBS-SRM bauxite samples. Silicon in HF solutions was analyzed using a modified ICP torch with a graphite injector tube, an inert nebulizer using PTFE capillary tubes, and a PTFE spray chamber.

Atmospheric plasma sprayed (APS) coatings of Al2O3-TiO2 system for photocatalytic application.

Science.gov (United States)

Stengl, V; Ageorges, H; Ctibor, P; Murafa, N

2009-05-01

The goal of this study is to examine the photocatalytic ability of coatings produced by atmospheric plasma spraying (APS). The plasma gun used is a common gas-stabilized plasma gun (GSP) working with a d.c. current and a mixture of argon and hydrogen as plasma-forming gas. The TiO(2) powders are particles of about 100 nm which were agglomerated to a mean size of about 55 mum, suitable for spraying. Composition of the commercial powder is 13 wt% of TiO(2) in Al(2)O(3), whereas also in-house prepared powder with the same nominal composition but with agglomerated TiO(2) and conventional fused and crushed Al(2)O(3) was sprayed. The feedstock materials used for this purpose are alpha-alumina and anatase titanium dioxide. The coatings are analyzed by scanning electron microscopy (SEM), energy dispersion probe (EDS) and X-ray diffraction. Photocatalytic degradation of acetone is quantified for various coatings. All plasma sprayed coatings show a lamellar structure on cross section, as typical for this process. Anatase titania from feedstock powder is converted into rutile titania and alpha-alumina partly to gamma-alumina. Coatings are proven to catalyse the acetone decomposition when irradiated by UV rays.

Dielectric properties of plasma sprayed silicates subjected to additional annealing

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Sedláček, J.; Nevrlá, Barbara; Neufuss, Karel

2017-01-01

Roč. 10, č. 2 (2017), s. 105-114 ISSN 2008-2134 Institutional support: RVO:61389021 Keywords : Annealing * Dielectric properties * Plasma spraying * Silicates * Electrical properties * Insulators Subject RIV: JK - Corrosion ; Surface Treatment of Materials OBOR OECD: Coating and films http://pccc.icrc.ac.ir/Articles/1/18/990/

Determination of elastic modulus and residual stress of plasma-sprayed tungsten coating on steel substrate

Science.gov (United States)

You, J. H.; Höschen, T.; Lindig, S.

2006-01-01

Plasma-sprayed tungsten, which is a candidate material for the first wall armour, shows a porous, heterogeneous microstructure. Due to its characteristic morphology, the properties are significantly different from those of its dense bulk material. Measurements of the elastic modulus of this coating have not been reported in the literature. In this work Young's modulus of highly porous plasma-sprayed tungsten coatings deposited on steel (F82H) substrates was measured. For the fabrication of the coating system the vacuum plasma-spray process was applied. Measurements were performed by means of three-point and four-point bending tests. The obtained modulus values ranged from 53 to 57 GPa. These values could be confirmed by the test result of a detached coating strip, which was 54 GPa. The applied methods produced consistent results regardless of testing configurations and specimen sizes. The errors were less than 1%. Residual stress of the coating was also estimated.

Determination of elastic modulus and residual stress of plasma-sprayed tungsten coating on steel substrate

International Nuclear Information System (INIS)

You, J.H.; Hoeschen, T.; Lindig, S.

2006-01-01

Plasma-sprayed tungsten, which is a candidate material for the first wall armour, shows a porous, heterogeneous microstructure. Due to its characteristic morphology, the properties are significantly different from those of its dense bulk material. Measurements of the elastic modulus of this coating have not been reported in the literature. In this work Young's modulus of highly porous plasma-sprayed tungsten coatings deposited on steel (F82H) substrates was measured. For the fabrication of the coating system the vacuum plasma-spray process was applied. Measurements were performed by means of three-point and four-point bending tests. The obtained modulus values ranged from 53 to 57 GPa. These values could be confirmed by the test result of a detached coating strip, which was 54 GPa. The applied methods produced consistent results regardless of testing configurations and specimen sizes. The errors were less than 1%. Residual stress of the coating was also estimated

A review of fusion torch applications

International Nuclear Information System (INIS)

Eastlund, B.J.; Gough, W.C.

1983-01-01

The Fusion Torch is a concept developed in 1968 to propose the investigation of non-electrical uses of the flux of particle and electromagnetic radiation capable of being produced from a fusion plasma (leakage). The proposed applications include direct recycling of material, the use of electromagnetic radiation to produce H 2 fuel and novel methods of heat transfer. The purpose of this paper is to review progress, and to discuss ideas that have resulted from new magnetic containment concepts. The practicality of the Fusion Torch concept for direct recycling with D-T fuel cycles was questioned because of neutron-activation. Since 1968, low neutron fusion reactions have received serious consideration. The economics of adding applications features to a fusion reactor must be studied in relation to specific reactor designs. Calculations are presented to illustrate the large advantages applications could offer for low Q, high circulating power systems such as mirrors, small Tokamaks and linear pinches. Little advantage is predicated for high Q, high thermal efficiency systems typified by large Tokamaks. The production of fuels such as H 2 has received study using high temperature electrolysis, radiation chemistry, and thermochemical cycles. Ore reduction using differential ionization is also described. A summary of applications areas are presented along with ideas on the potential of large scale use of such systems

Performance Testing of Suspension Plasma Sprayed Thermal Barrier Coatings Produced with Varied Suspension Parameters

Directory of Open Access Journals (Sweden)

Nicholas Curry

2015-07-01

Full Text Available Suspension plasma spraying has become an emerging technology for the production of thermal barrier coatings for the gas turbine industry. Presently, though commercial systems for coating production are available, coatings remain in the development stage. Suitable suspension parameters for coating production remain an outstanding question and the influence of suspension properties on the final coatings is not well known. For this study, a number of suspensions were produced with varied solid loadings, powder size distributions and solvents. Suspensions were sprayed onto superalloy substrates coated with high velocity air fuel (HVAF -sprayed bond coats. Plasma spray parameters were selected to generate columnar structures based on previous experiments and were maintained at constant to discover the influence of the suspension behavior on coating microstructures. Testing of the produced thermal barrier coating (TBC systems has included thermal cyclic fatigue testing and thermal conductivity analysis. Pore size distribution has been characterized by mercury infiltration porosimetry. Results show a strong influence of suspension viscosity and surface tension on the microstructure of the produced coatings.

Phase Formation Control in Plasma Sprayed Alumina–Chromia Coatings

Czech Academy of Sciences Publication Activity Database

Dubský, Jiří; Chráska, Pavel; Kolman, Blahoslav Jan; Stahr, C.Ch.; Berger, L.-M.

2011-01-01

Roč. 55, č. 3 (2011), s. 294-300 ISSN 0862-5468 R&D Projects: GA ČR GA106/08/1240 Institutional research plan: CEZ:AV0Z20430508 Keywords : Alumina * Chromia * Plasma spraying * Phase stabilization Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 0.382, year: 2011 http://www.ceramics-silikaty.cz/2011/2011_03_294.htm

Computational image analysis of Suspension Plasma Sprayed YSZ coatings

Directory of Open Access Journals (Sweden)

Michalak Monika

2017-01-01

Full Text Available The paper presents the computational studies of microstructure- and topography- related features of suspension plasma sprayed (SPS coatings of yttria-stabilized zirconia (YSZ. The study mainly covers the porosity assessment, provided by ImageJ software analysis. The influence of boundary conditions, defined by: (i circularity and (ii size limits, on the computed values of porosity is also investigated. Additionally, the digital topography evaluation is performed: confocal laser scanning microscope (CLSM and scanning electron microscope (SEM operating in Shape from Shading (SFS mode measure surface roughness of deposited coatings. Computed values of porosity and roughness are referred to the variables of the spraying process, which influence the morphology of coatings and determines the possible fields of their applications.

The effect of YBa2Cu3O7-x powder characteristics on thick coatings prepared by atmospheric plasma spraying

International Nuclear Information System (INIS)

Georgiopoulos, E.; Tsetsekou, A.

2000-01-01

The development of superconducting YBa 2 Cu 3 O 7-x plasma sprayed coatings on metal substrates can be very useful for applications such as targets for thin-film deposition techniques (sputtering, laser ablation, ion assisted deposition) or magnetic shielding, due to the brittle nature of bulk superconductors. The plasma spraying technique is very flexible and can be used for manufacturing components with a large variety of geometries. This technique requires the use of powders with good rheological characteristics. In this study, YBa 2 Cu 3 O 7-x powders were produced by using the conventional solid-state reaction route and also by spray drying a solution of nitrate precursors. Both powders, as well as mixtures of them, were plasma sprayed to develop coatings on stainless-steel substrates, with the aim of studying the effect of the feedstock powder characteristics on the coating properties. It was found that by optimizing the plasma spraying conditions, good quality coatings could be obtained. However, the powder morphology and homogeneity significantly affect the coating quality. More homogeneous powders lead to better results, the spray-dried powder being the best because of its enhanced rheological properties and good morphology. (author)

Structure and property evaluation of a vacuum plasma sprayed nanostructured tungsten-hafnium carbide bulk composite

NARCIS (Netherlands)

Rea, K. E.; Viswanathan, V.; Kruize, A.; De Hosson, J. Th. M.; O'Dell, S.; McKechnie, T.; Rajagopalan, S.; Vaidyanathan, R.; Seal, S.; O’Dell, S.

2008-01-01

Vacuum plasma spray (VPS) forming of tungsten-based metal matrix nanocomposites (MMCs) has shown to be a cost effective and time saving method for the formation of bulk monolithic nanostructured then no-mechanical components. Spray drying of powder feedstock appears to have a significant effect on

NUMERICAL MODELING OF STRESSES NEAR THE SURFACE IN THE INGOT OF CIRCULAR SECTION, CRYSTALLIZABLE AT CIRCULAR TORCH SECONDARY COOLING

Directory of Open Access Journals (Sweden)

A. N. Chichko

2004-01-01

Full Text Available The results of computer calculations of the stresses, generated in outside layer of ingot of steel 20 of circular section with diameter 300 mm, in application to one of the industrial technological schemas of RUP “BMZ”, are presented. The segments of compressive and tensile stresses formation along the length of ingot are determined and the principal possibility of production of continuously cast slug of circular section at circular-torch spray cooling is shown.

Effect of plasma spraying modes on material properties of internal combustion engine cylinder liners

Science.gov (United States)

Timokhova, O. M.; Burmistrova, O. N.; Sirina, E. A.; Timokhov, R. S.

2018-03-01

The paper analyses different methods of remanufacturing worn-out machine parts in order to get the best performance characteristics. One of the most promising of them is a plasma spraying method. The mathematical models presented in the paper are intended to anticipate the results of plasma spraying, its effect on the properties of the material of internal combustion engine cylinder liners under repair. The experimental data and research results have been computer processed with Statistica 10.0 software package. The pare correlation coefficient values (R) and F-statistic criterion are given to confirm the statistical properties and adequacy of obtained regression equations.

Steam torch plasma modelling

Czech Academy of Sciences Publication Activity Database

Jeništa, Jiří

2017-01-01

Roč. 37, č. 3 (2017), s. 653-687 ISSN 0272-4324 R&D Projects: GA ČR(CZ) GA15-19444S Institutional support: RVO:61389021 Keywords : Arc * Evaporation * Mass flow rate * Water-vortex stabilization * Net emission coefficients * Partial characteristics * Local thermodynamic equilibrium Subject RIV: BL - Plasma and Gas Discharge Physics OBOR OECD: Fluids and plasma physics (including surface physics) Impact factor: 2.355, year: 2016 http://link.springer.com/article/10.1007/s11090-017-9789-7

Prediction and optimization of process variables to maximize the Young's modulus of plasma sprayed alumina coatings on AZ31B magnesium alloy

Directory of Open Access Journals (Sweden)

D. Thirumalaikumarasamy

2017-03-01

Full Text Available Like other manufacturing techniques, plasma spraying has also a non-linear behavior because of the contribution of many coating variables. This characteristic results in finding optimal factor combination difficult. Subsequently, the issue can be solved through effective and strategic statistical procedures integrated with systematic experimental data. Plasma spray parameters such as power, stand-off distance and powder feed rate have significant influence on coating characteristics like Young's modulus. This paper presents the use of statistical techniques in specifically response surface methodology (RSM, analysis of variance, and regression analysis to develop empirical relationship to predict Young's modulus of plasma-sprayed alumina coatings. The developed empirical relationships can be effectively used to predict Young's modulus of plasma-sprayed alumina coatings at 95% confidence level. Response graphs and contour plots were constructed to identify the optimum plasma spray parameters to attain maximum Young's modulus in alumina coatings. A linear regression relationship was established between porosity and Young's modulus of the alumina coatings.

Plasma-sprayed CaTiSiO5 ceramic coating on Ti-6Al-4V with excellent bonding strength, stability and cellular bioactivity

Science.gov (United States)

Wu, Chengtie; Ramaswamy, Yogambha; Liu, Xuanyong; Wang, Guocheng; Zreiqat, Hala

2008-01-01

Novel Ca-Si-Ti-based sphene (CaTiSiO5) ceramics possess excellent chemical stability and cytocompatibility. The aim of this study was to prepare sphene coating on titanium alloy (Ti-6Al-4V) for orthopaedic applications using the plasma spray method. The phase composition, surface and interface microstructure, coating thickness, surface roughness and bonding strength of the plasma-sprayed sphene coating were analysed using X-ray diffraction, scanning electron microscopy, atomic force microscopy and the standard mechanical testing of the American Society for Testing and Materials, respectively. The results indicated that sphene coating was obtained with a uniform and dense microstructure at the interface of the Ti-6Al-4V surface and the thickness and surface roughness of the coating were approximately 150 and 10 μm, respectively. Plasma-sprayed sphene coating on Ti-6Al-4V possessed a significantly improved bonding strength and chemical stability compared with plasma-sprayed hydroxyapatite (HAp) coating. Plasma-sprayed sphene coating supported human osteoblast-like cell (HOB) attachment and significantly enhanced HOB proliferation and differentiation compared with plasma-sprayed HAp coating and uncoated Ti-6Al-4V. Taken together, plasma-sprayed sphene coating on Ti-6Al-4V possessed excellent bonding strength, chemical stability and cellular bioactivity, indicating its potential application for orthopaedic implants. PMID:18664431

Dielectric properties and vacancy-like defects in plasma-sprayed barium titanate.

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Čížek, J.; Sedláček, J.; Lukáč, František

2017-01-01

Roč. 100, č. 7 (2017), s. 2972-2983 ISSN 0002-7820 Institutional support: RVO:61389021 Keywords : barium titanate * plasma spraying * vacancies Subject RIV: JH - Ceramic s, Fire-Resistant Materials and Glass OBOR OECD: Ceramic s Impact factor: 2.841, year: 2016

Structural and photoluminescence properties of silicon nanowires extracted by means of a centrifugation process from plasma torch synthesized silicon nanopowder

Science.gov (United States)

Le Borgne, Vincent; Agati, Marta; Boninelli, Simona; Castrucci, Paola; De Crescenzi, Maurizio; Dolbec, Richard; El Khakani, My Ali

2017-07-01

We report on a method for the extraction of silicon nanowires (SiNWs) from the by-product of a plasma torch based spheroidization process of silicon. This by-product is a nanopowder which consists of a mixture of SiNWs and silicon particles. By optimizing a centrifugation based process, we were able to extract substantial amounts of highly pure Si nanomaterials (mainly SiNWs and Si nanospheres (SiNSs)). While the purified SiNWs were found to have typical outer diameters in the 10-15 nm range and lengths of up to several μm, the SiNSs have external diameters in the 10-100 nm range. Interestingly, the SiNWs are found to have a thinner Si core (2-5 nm diam.) and an outer silicon oxide shell (with a typical thickness of ˜5-10 nm). High resolution transmission electron microscopy (HRTEM) observations revealed that many SiNWs have a continuous cylindrical core, whereas others feature a discontinuous core consisting of a chain of Si nanocrystals forming a sort of ‘chaplet-like’ structures. These plasma-torch-produced SiNWs are highly pure with no trace of any metal catalyst, suggesting that they mostly form through SiO-catalyzed growth scheme rather than from metal-catalyzed path. The extracted Si nanostructures are shown to exhibit a strong photoluminescence (PL) which is found to blue-shift from 950 to 680 nm as the core size of the Si nanostructures decreases from ˜5 to ˜3 nm. This near IR-visible PL is shown to originate from quantum confinement (QC) in Si nanostructures. Consistently, the sizes of the Si nanocrystals directly determined from HRTEM images corroborate well with those expected by QC theory.

Superhydrophobic Ceramic Coatings by Solution Precursor Plasma Spray

Science.gov (United States)

Cai, Yuxuan

Superhydrophobic surfaces exhibit superior water repellent properties, and they have remarkable potential to improve current energy infrastructure. Substantial research has been performed on the production of superhydrophobic coatings. However, superhydrophobic coatings have not yet been adopted in many industries where potential applications exist due to the limited durability of the coating materials and the complex and costly fabrication processes. Here presented a novel coating technique to manufacture ceramic superhydrophobic coatings rapidly and economically. A rare earth oxide (REO) was selected as the coating material due to its hydrophobic nature and strong mechanical properties, and deposited on stainless steel substrates by solution precursor plasma spray (SPPS). The as-sprayed coating demonstrated a hierarchically structured coating topography, which closely resembles superhydrophobic surfaces in nature. Compared to smooth REO surfaces, the SPPS superhydrophobic coating improved the water contact angle by as much as 65° after vacuum treatment at 1 Pa for 48 hours.

The influence of substrate temperature and spraying distance on the properties of plasma sprayed tungsten and steel coatings deposited in a shrouding chamber

Czech Academy of Sciences Publication Activity Database

Matějíček, Jiří; Vilémová, Monika; Nevrlá, Barbara; Kocmanová, Lenka; Veverka, Jakub; Halasová, Martina; Hadraba, Hynek

2017-01-01

Roč. 318, May (2017), s. 217-223 ISSN 0257-8972. [International Meeting on Thermal Spraying (RIPT)/7./. Limoges, 09.12.2015-11.12.2015] R&D Projects: GA ČR GB14-36566G EU Projects: European Commission(XE) 633053 - EUROfusion Institutional support: RVO:61389021 ; RVO:68081723 Keywords : Tungsten * Steel * Atmospheric plasma spraying * Shrouding * Substrate temperature * Fusion reactor materials * Plasma facing components Subject RIV: JK - Corrosion ; Surface Treatment of Materials; JK - Corrosion ; Surface Treatment of Materials (UFM-A) OBOR OECD: Coating and films; Coating and films (UFM-A) Impact factor: 2.589, year: 2016 http://www.sciencedirect.com/science/ article /pii/S0257897216310520

Deposition of titanium nitride layers by electric arc – Reactive plasma spraying method

International Nuclear Information System (INIS)

Şerban, Viorel-Aurel; Roşu, Radu Alexandru; Bucur, Alexandra Ioana; Pascu, Doru Romulus

2013-01-01

Highlights: ► Titanium nitride layers deposited by electric arc – reactive plasma spraying method. ► Deposition of titanium nitride layers on C45 steel at different spraying distances. ► Characterization of the coatings hardness as function of the spraying distances. ► Determination of the corrosion behavior of titanium nitride layers obtained. - Abstract: Titanium nitride (TiN) is a ceramic material which possesses high mechanical properties, being often used in order to cover cutting tools, thus increasing their lifetime, and also for covering components which are working in corrosive environments. The paper presents the experimental results on deposition of titanium nitride coatings by a new combined method (reactive plasma spraying and electric arc thermal spraying). In this way the advantages of each method in part are combined, obtaining improved quality coatings in the same time achieving high productivity. Commercially pure titanium wire and C45 steel as substrate were used for experiments. X-ray diffraction analysis shows that the deposited coatings are composed of titanium nitride (TiN, Ti 2 N) and small amounts of Ti 3 O. The microstructure of the deposited layers, investigated both by optical and scanning electron microscopy, shows that the coatings are dense, compact, without cracks and with low porosity. Vickers microhardness of the coatings presents maximum values of 912 HV0.1. The corrosion tests in 3%NaCl solution show that the deposited layers have a high corrosion resistance compared to unalloyed steel substrate.

Synthesis of mullite-based coatings from alumina and zircon powder mixtures by plasma spraying and laser remelting

International Nuclear Information System (INIS)

Hazra, S.; Das, J.; Bandyopadhyay, P.P.

2015-01-01

A mechanical mixture of alumina and pulverized zircon sand in 3:2 M ratio has been plasma sprayed to obtain mullite coating. Thereafter, the top layer of the coating has been remelted using laser. The presence of a mullite phase in the as-sprayed and laser remelted coatings has been confirmed qualitatively using X-ray diffraction. Both as-sprayed and laser remelted coatings have been characterized for their microstructure, hardness and porosity. The ultrafine grain structure of the coating produced by rapid quenching has been analyzed using transmission electron microscope. Presence of a mullite phase in the coatings has also been confirmed using small angle electron diffraction. Laser remelting has resulted in an appreciable reduction in porosity and increase in hardness in the coatings. - Highlights: • Mullite has been produced by plasma spraying of alumina–zircon powder mixture. • As sprayed coating shows good integrity. • Laser remelting reduced porosity and increased coating hardness

Synthesis of mullite-based coatings from alumina and zircon powder mixtures by plasma spraying and laser remelting

Energy Technology Data Exchange (ETDEWEB)

Hazra, S. [Integrated Test Range, Chandipur, Balasore, Odisha 756025 (India); Das, J. [Department of Metallurgical and Materials Engineering, IIT Kharagpur, 721302 (India); Bandyopadhyay, P.P., E-mail: ppb@mech.iitkgp.ernet.in [Department of Mechanical Engineering, IIT Kharagpur, 721302 (India)

2015-03-15

A mechanical mixture of alumina and pulverized zircon sand in 3:2 M ratio has been plasma sprayed to obtain mullite coating. Thereafter, the top layer of the coating has been remelted using laser. The presence of a mullite phase in the as-sprayed and laser remelted coatings has been confirmed qualitatively using X-ray diffraction. Both as-sprayed and laser remelted coatings have been characterized for their microstructure, hardness and porosity. The ultrafine grain structure of the coating produced by rapid quenching has been analyzed using transmission electron microscope. Presence of a mullite phase in the coatings has also been confirmed using small angle electron diffraction. Laser remelting has resulted in an appreciable reduction in porosity and increase in hardness in the coatings. - Highlights: • Mullite has been produced by plasma spraying of alumina–zircon powder mixture. • As sprayed coating shows good integrity. • Laser remelting reduced porosity and increased coating hardness.

Plasma-Sprayed Fine-grained Zirconium Silicate and Its Dielectric Properties.

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Pala, Zdeněk; Nevrlá, Barbara; Neufuss, Karel

2017-01-01

Roč. 26, č. 5 (2017), s. 2388-2393 ISSN 1059-9495 R&D Projects: GA ČR GB14-36566G Institutional support: RVO:61389021 Keywords : electrical properties * insulators * plasma spraying * silica-substituted zirconia * zircon Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass OBOR OECD: Ceramics Impact factor: 1.331, year: 2016

The TORCH time-of-flight detector

Energy Technology Data Exchange (ETDEWEB)

Harnew, N., E-mail: Neville.Harnew@physics.ox.ac.uk [University of Oxford, Denys Wilkinson Building, 1 Keble Road, Oxford OX1 3RH (United Kingdom); Brook, N. [University College London, Department of Physics & Astronomy, Gower Street, London WC1E 6BT (United Kingdom); Castillo García, L. [CERN, PH Department, CH-1211 Geneva 23 (Switzerland); Laboratory for High Energy Physics, Ecole Polytechnique Fédérale de Lausanne, CH-1015 Lausanne (Switzerland); Cussans, D. [H.H. Wills Physics Laboratory, University of Bristol, Bristol BS8 1TL (United Kingdom); Föhl, K.; Forty, R.; Frei, C. [CERN, PH Department, CH-1211 Geneva 23 (Switzerland); Gao, R. [University of Oxford, Denys Wilkinson Building, 1 Keble Road, Oxford OX1 3RH (United Kingdom); Gys, T.; Piedigrossi, D. [CERN, PH Department, CH-1211 Geneva 23 (Switzerland); Rademacker, J.; Ros Garcia, A.; Dijk, M. van [H.H. Wills Physics Laboratory, University of Bristol, Bristol BS8 1TL (United Kingdom)

2016-07-11

The TORCH time-of-flight detector is being developed to provide particle identification between 2 and 10 GeV/c momentum over a flight distance of 10 m. TORCH is designed for large-area coverage, up to 30 m{sup 2}, and has a DIRC-like construction. The goal is to achieve a 15 ps time-of-flight resolution per incident particle by combining arrival times from multiple Cherenkov photons produced within quartz radiator plates of 10 mm thickness. A four-year R&D programme is underway with an industrial partner (Photek, UK) to produce 53×53 mm{sup 2} Micro-Channel Plate (MCP) detectors for the TORCH application. The MCP-PMT will provide a timing accuracy of 40 ps per photon and it will have a lifetime of up to at least 5 Ccm{sup −2} of integrated anode charge by utilizing an Atomic Layer Deposition (ALD) coating. The MCP will be read out using charge division with customised electronics incorporating the NINO chipset. Laboratory results on prototype MCPs are presented. The construction of a prototype TORCH module and its simulated performance are also described.

Evaluating microhardness of plasma sprayed Al2O3 coatings using Vickers indentation technique

International Nuclear Information System (INIS)

Yin Zhijian; Tao Shunyan; Zhou Xiaming; Ding Chuanxian

2007-01-01

In this work, the microhardness of plasma sprayed Al 2 O 3 coatings was evaluated using the Vickers indentation technique, and the effects of measurement direction, location and applied loads were investigated. The measured data sets were then statistically analysed employing the Weibull distribution to evaluate their variability within the coatings. It was found that the Vickers hardness (VHN) increases with decreasing applied indenter load, which can be explained in terms of Kick's law and the Meyer index k of 1.93, as well as relating to the microstructural characteristics of plasma sprayed coatings and the elastic recovery taking place during indentation. In addition, VHN, measured on the cross section of coatings, was obviously higher than that on its top surface. The obtained Weibull modulus and variation coefficient indicate that the VHN was less variable when measured at a higher applied load and on the cross section of coating. The obvious dependence of the VHN on the specific indentation location within through-thickness direction was also realized. These phenomena described above in this work were related to the special microstructure and high anisotropic behaviour of plasma sprayed coatings

The Influence of Spray Parameters on the Characteristics of Hydroxyapatite In-Flight Particles, Splats and Coatings by Micro-plasma Spraying

Science.gov (United States)

Liu, Xiao-mei; He, Ding-yong; Wang, Yi-ming; Zhou, Zheng; Wang, Guo-hong; Tan, Zhen; Wang, Zeng-jie

2018-04-01

Hydroxyapatite (HA) is one of the most important bioceramic materials used in medical implants. The structure of HA coatings is closely related to their manufacturing process. In the present study, HA coatings were deposited on Ti-6Al-4V substrate by micro-plasma spraying. Results show that three distinct HA coatings could be obtained by changing the spraying power from 0.5 to 1.0 kW and spraying stand-off distance from 60 to 110 mm: (1) high crystallinity (93.3%) coatings with porous structure, (2) high crystallinity coatings (86%) with columnar structure, (3) higher amorphous calcium phosphate (ACP, 50%) coatings with dense structure. The in-flight particles melting state and splat topography was analyzed to better understand the formation mechanism of three distinct HA coatings. Results show that HA coatings sprayed at low spraying power and short stand-off distance exhibit high crystallinity and porosity is attributed to the presence of partially melted particles. High crystallinity HA coatings with (002) crystallographic texture could be deposited due to the complete melting of the in-flight particles and low cooling rate of the disk shape splats under higher spraying power and shorter SOD. However, splashed shape splats with relative high cooling can be provided by increasing SOD, which leads to the formation of ACP.

Hydroxyapatite coatings deposited by liquid precursor plasma spraying: controlled dense and porous microstructures and osteoblastic cell responses

International Nuclear Information System (INIS)

Huang Yi; Song Lei; Liu Xiaoguang; Xiao Yanfeng; Wu Yao; Chen Jiyong; Wu Fang; Gu Zhongwei

2010-01-01

Hydroxyapatite coatings were deposited on Ti-6Al-4V substrates by a novel plasma spraying process, the liquid precursor plasma spraying (LPPS) process. X-ray diffraction results showed that the coatings obtained by the LPPS process were mainly composed of hydroxyapatite. The LPPS process also showed excellent control on the coating microstructure, and both nearly fully dense and highly porous hydroxyapatite coatings were obtained by simply adjusting the solid content of the hydroxyapatite liquid precursor. Scanning electron microscope observations indicated that the porous hydroxyapatite coatings had pore size in the range of 10-200 μm and an average porosity of 48.26 ± 0.10%. The osteoblastic cell responses to the dense and porous hydroxyapatite coatings were evaluated with human osteoblastic cell MG-63, in respect of the cell morphology, proliferation and differentiation, with the hydroxyapatite coatings deposited by the atmospheric plasma spraying (APS) process as control. The cell experiment results indicated that the heat-treated LPPS coatings with a porous structure showed the best cell proliferation and differentiation among all the hydroxyapatite coatings. Our results suggest that the LPPS process is a promising plasma spraying technique for fabricating hydroxyapatite coatings with a controllable microstructure, which has great potential in bone repair and replacement applications.

Strategies to improve the adhesion of rubbers to adhesives by means of plasma surface modification

Science.gov (United States)

Martín-Martínez, J. M.; Romero-Sánchez, M. D.

2006-05-01

The surface modifications produced by treatment of a synthetic sulfur vulcanized styrene-butadiene rubber with oxidizing (oxygen, air, carbon dioxide) and non oxidizing (nitrogen, argon) RF low pressure plasmas, and by treatment with atmospheric plasma torch have been assessed by ATR-IR and XPS spectroscopy, SEM, and contact angle measurements. The effectiveness of the low pressure plasma treatment depended on the gas atmosphere used to generate the plasma. A lack of relationship between surface polarity and wettability, and peel strength values was obtained, likely due to the cohesive failure in the rubber obtained in the adhesive joints. In general, acceptable adhesion values of plasma treated rubber were obtained for all plasmas, except for nitrogen plasma treatment during 15 minutes due to the creation of low molecular weight moieties on the outermost rubber layer. A toluene wiping of the N{2 } plasma treated rubber surface for 15 min removed those moieties and increased adhesion was obtained. On the other hand, the treatment of the rubber with atmospheric pressure by means of a plasma torch was proposed. The wettability of the rubber was improved by decreasing the rubber-plasma torch distance and by increasing the duration because a partial removal of paraffin wax from the rubber surface was produced. The rubber surface was oxidized by the plasma torch treatment, and the longer the duration of the plasma torch treatment, the higher the degree of surface oxidation (mainly creation of C O moieties). However, although the rubber surface was effectively modified by the plasma torch treatment, the adhesion was not greatly improved, due to the migration of paraffin wax to the treated rubber-polyurethane adhesive interface once the adhesive joint was produced. On the other hand, the extended treatment with plasma torch facilitated the migration of zinc stearate to the rubber-adhesive interface, also contributing to deteriorate the adhesion in greater extent. Finally

Plasma Spraying and Characterization of Chromium Carbide-Nickel Chromium Coatings

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Prantnerová, M.

2016-01-01

Roč. 9, č. 4 (2016), s. 281-290, č. článku PCCC-2016-09-16-339. ISSN 2008-2134 Institutional support: RVO:61389021 Keywords : Plasma spraying * Chromium carbide * Slurry abrasion * Dry rubber wheel test * Friction * Microhardness Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass http://www.pccc.icrc.ac.ir/?xid=0113010121000001804&id=976

Dual wire welding torch and method

Science.gov (United States)

Diez, Fernando Martinez; Stump, Kevin S.; Ludewig, Howard W.; Kilty, Alan L.; Robinson, Matthew M.; Egland, Keith M.

2009-04-28

A welding torch includes a nozzle with a first welding wire guide configured to orient a first welding wire in a first welding wire orientation, and a second welding wire guide configured to orient a second welding wire in a second welding wire orientation that is non-coplanar and divergent with respect to the first welding wire orientation. A method of welding includes moving a welding torch with respect to a workpiece joint to be welded. During moving the welding torch, a first welding wire is fed through a first welding wire guide defining a first welding wire orientation and a second welding wire is fed through a second welding wire guide defining a second welding wire orientation that is divergent and non-coplanar with respect to the first welding wire orientation.

Testing of Flame Sprayed Al2O3 Matrix Coatings Containing TiO2

Directory of Open Access Journals (Sweden)

Czupryński A.

2016-09-01

Full Text Available The paper presents the results of the properties of flame sprayed ceramic coatings using oxide ceramic materials coating of a powdered aluminium oxide (Al2O3 matrix with 3% titanium oxide (TiO2 applied to unalloyed S235JR grade structural steel. A primer consisting of a metallic Ni-Al-Mo based powder has been applied to plates with dimensions of 5×200×300 mm and front surfaces of Ø40×50 mm cylinders. Flame spraying of primer coating was made using a RotoTec 80 torch, and an external coating was made with a CastoDyn DS 8000 torch. Evaluation of the coating properties was conducted using metallographic testing, phase composition research, measurement of microhardness, substrate coating adhesion (acc. to EN 582:1996 standard, erosion wear resistance (acc. to ASTM G76-95 standard, and abrasive wear resistance (acc. to ASTM G65 standard and thermal impact. The testing performed has demonstrated that flame spraying with 97% Al2O3 powder containing 3% TiO2 performed in a range of parameters allows for obtaining high-quality ceramic coatings with thickness up to ca. 500 µm on a steel base. Spray coating possesses a structure consisting mainly of aluminium oxide and a small amount of NiAl10O16 and NiAl32O49 phases. The bonding primer coat sprayed with the Ni-Al-Mo powder to the steel substrate and external coating sprayed with the 97% Al2O3 powder with 3% TiO2 addition demonstrates mechanical bonding characteristics. The coating is characterized by a high adhesion to the base amounting to 6.5 MPa. Average hardness of the external coating is ca. 780 HV. The obtained coatings are characterized by high erosion and abrasive wear resistance and the resistance to effects of cyclic thermal shock.

[Determination of sodium, magnesium, calcium, lithium and strontium in natural mineral drinking water by microwave plasma torch spectrometer with nebulization sample introduction system].

Science.gov (United States)

Zhou, Wei; Xiong, Hai-long; Feng, Guo-dong; Yu, Ai-min; Chen, Huan-wen

2014-06-01

The microwave plasma torch (MPT) was used as the emission light source. Aqueous samples were introduced with a nebulizer and a desolvation system. A method for the determination of Na, Mg, Ca, Li and Sr in natural mineral drinking water by argon microwave plasma torch spectrometer (ArMPT spectrometer) was established. The effects of microwave power, flow rate of carrier gas and support gas were investigated in detail and these parameters were optimized. Under the optimized condition, the experiments for the determination of Na, Mg, Ca, Li and Sr in 11 kinds of bottled mineral drinking water were carried out by ArMPT spectrometer. The limit-of-detection (LOD) of Na, Mg, Ca, Li and Sr was found to be 4.4, 21, 56, 11 and 84 μg x mL(-1), respectively. Relative standard deviation (n = 6) was in the range of 1.30%-5.45% and standard addition recoveries were in the range of 84.6%-98.5%. MPT spectrometer was simpler, more convenient and of lower cost as compared to ICP unit. MPT spectrometer demonstrated its rapid analysis speed, accuracy, sensitivity and simultaneous multi element analysis ability during the analysis process. The results showed that MPT spectrometer was suitable for metal elements detection for natural mineral drinking water. This approach provides not only one way for resisting the illegal dealings, but also a security for the quality of drinking water. Moreover, the usability of MPT spectrometer in the field of food security; drug safety; clinical diagnostic is promised.

Optical study of plasma sprayed hydroxyapatite coatings deposited at different spray distance

Science.gov (United States)

Belka, R.; Kowalski, S.; Żórawski, W.

2017-08-01

Series of hydroxyapatite (HA) coatings deposited on titanium substrate at different spray (plasma gun to workpiece) distance were investigated. The optical methods as dark field confocal microscopy, Raman/PL and UV-VIS spectroscopy were used for study the influence of deposition process on structural degradation of HA precursor. The hydroxyl group concentration was investigated by study the OH mode intensity in the Raman spectra. Optical absorption coefficients at near UV region were analyzed by Diffuse Reflectance Spectroscopy. PL intensity observed during Raman measurement was also considered as relation to defects concentration and degradation level. It was confirmed the different gunsubstrate distance has a great impact on structure of deposited HA ceramics.

The change of NiCrBSi alloys’ phase composition after plasma spraying

Directory of Open Access Journals (Sweden)

A. Dudek

2008-08-01

Full Text Available Material for investigations was NiCrBSi powder for components’ coatings which improve their corrosion resistance as well as resistance to friction wear and erosion. Plasma spraying method was used to produce a coating with thickness of 300 μm on low-alloy steel which was then remelted with the base material. Using X-ray quality analysis, phase composition was determined for: NiCrBSi powder, obtained coating and the alloyed surface layer. Crystallinity degree was also calculated for NiCrBSi layer sprayed on the base material.

Plasma sprayed rutile titania-nanosilver antibacterial coatings

Energy Technology Data Exchange (ETDEWEB)

Gao, Jinjin [Key Lab of Inorganic Coating Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); Zhao, Chengjian [National Key Laboratory of Human Factors Engineering, Department of ECLSS, China Astronaut Researching and Training Center, Beijing, 100094 (China); Zhou, Jingfang [Ian Wark Research Institute, University of South Australia, Mawson Lakes Campus, Mawson Lakes, SA, 5095 (Australia); Li, Chunxia [National Key Laboratory of Human Factors Engineering, Department of ECLSS, China Astronaut Researching and Training Center, Beijing, 100094 (China); Shao, Yiran; Shi, Chao [Key Lab of Inorganic Coating Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); Zhu, Yingchun, E-mail: yzhu@mail.sic.ac.cn [Key Lab of Inorganic Coating Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China)

2015-11-15

Graphical abstract: - Highlights: • TiO{sub 2}/Ag feedstock powders containing 1–10,000 ppm silver nanoparticles were double sintered and deposited by plasma spray. • TiO{sub 2}/Ag coatings were composed of pure rutile phase and homogeneously-distributed metallic silver. • TiO{sub 2}/Ag coatings with more than 10 ppm silver nanoparticles exhibited strong antibacterial activity against E. coli and S. aureus. - Abstract: Rutile titania (TiO{sub 2}) coatings have superior mechanical properties and excellent stability that make them preferential candidates for various applications. In order to prevent infection arising from bacteria, significant efforts have been focused on antibacterial TiO{sub 2} coatings. In the study, titania-nanosilver (TiO{sub 2}/Ag) coatings with five different kinds of weight percentages of silver nanoparticles (AgNPs) were prepared by plasma spray. The feedstock powders, which had a composition of rutile TiO{sub 2} powders containing 1–10,000 ppm AgNPs, were double sintered and deposited on stainless steel substrates with optimized spraying parameters. X-Ray diffraction and scanning electron microscopy were used to analysize the phase composition and surface morphology of TiO{sub 2}/Ag powders and coatings. Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) were employed to examine the antibacterial activity of the as-prepared coatings by bacterial counting method. The results showed that silver existed homogeneously in the TiO{sub 2}/Ag coatings and no crystalline changed happened in the TiO{sub 2} structure. The reduction ratios on the TiO{sub 2}/Ag coatings with 10 ppm AgNPs were as high as 94.8% and 95.6% for E. coli and S. aureus, respectively, and the TiO{sub 2}/Ag coatings with 100–1000 ppm AgNPs exhibited 100% bactericidal activity against E. coli and S. aureus, which indicated the TiO{sub 2}/Ag coatings with more than 10 ppm AgNPs had strong antibacterial activity. Moreover, the main factors influencing the

Plasma sprayed rutile titania-nanosilver antibacterial coatings

International Nuclear Information System (INIS)

Gao, Jinjin; Zhao, Chengjian; Zhou, Jingfang; Li, Chunxia; Shao, Yiran; Shi, Chao; Zhu, Yingchun

2015-01-01

Graphical abstract: - Highlights: • TiO_2/Ag feedstock powders containing 1–10,000 ppm silver nanoparticles were double sintered and deposited by plasma spray. • TiO_2/Ag coatings were composed of pure rutile phase and homogeneously-distributed metallic silver. • TiO_2/Ag coatings with more than 10 ppm silver nanoparticles exhibited strong antibacterial activity against E. coli and S. aureus. - Abstract: Rutile titania (TiO_2) coatings have superior mechanical properties and excellent stability that make them preferential candidates for various applications. In order to prevent infection arising from bacteria, significant efforts have been focused on antibacterial TiO_2 coatings. In the study, titania-nanosilver (TiO_2/Ag) coatings with five different kinds of weight percentages of silver nanoparticles (AgNPs) were prepared by plasma spray. The feedstock powders, which had a composition of rutile TiO_2 powders containing 1–10,000 ppm AgNPs, were double sintered and deposited on stainless steel substrates with optimized spraying parameters. X-Ray diffraction and scanning electron microscopy were used to analysize the phase composition and surface morphology of TiO_2/Ag powders and coatings. Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) were employed to examine the antibacterial activity of the as-prepared coatings by bacterial counting method. The results showed that silver existed homogeneously in the TiO_2/Ag coatings and no crystalline changed happened in the TiO_2 structure. The reduction ratios on the TiO_2/Ag coatings with 10 ppm AgNPs were as high as 94.8% and 95.6% for E. coli and S. aureus, respectively, and the TiO_2/Ag coatings with 100–1000 ppm AgNPs exhibited 100% bactericidal activity against E. coli and S. aureus, which indicated the TiO_2/Ag coatings with more than 10 ppm AgNPs had strong antibacterial activity. Moreover, the main factors influencing the antibacterial properties of TiO_2/Ag coatings were discussed with

Fuel Retention Improvement at High Temperatures in Tungsten-Uranium Dioxide Dispersion Fuel Elements by Plasma-Spray Cladding

Science.gov (United States)

Grisaffe, Salvatore J.; Caves, Robert M.

1964-01-01

An investigation was undertaken to determine the feasibility of depositing integrally bonded plasma-sprayed tungsten coatings onto 80-volume-percent tungsten - 20-volume-percent uranium dioxide composites. These composites were face clad with thin tungsten foil to inhibit uranium dioxide loss at elevated temperatures, but loss at the unclad edges was still significant. By preheating the composite substrates to approximately 3700 degrees F in a nitrogen environment, metallurgically bonded tungsten coatings could be obtained directly by plasma spraying. Furthermore, even though these coatings were thin and somewhat porous, they greatly inhibited the loss of uranium dioxide. For example, a specimen that was face clad but had no edge cladding lost 5.8 percent uranium dioxide after 2 hours at 4750 dgrees F in flowing hydrogen. A similar specimen with plasma-spray-coated edges, however, lost only 0.75 percent uranium dioxide under the same testing conditions.

Thermal analysis of HNPF spent fuel shipping container in torch environments

International Nuclear Information System (INIS)

Eggers, P.E.; Crawford, H.L.; Trujillo, A.A.; Pope, R.B.; Yoshimura, H.R.

1980-01-01

A thermal analysis of a modified HNPF cask has been performed to predict cask temperatures in simulated torch fire environments. A portion of this analysis also provided a basis for the modifications leading to the design of external cooling fins, a pressure relief valve system, a spent fuel torch fire analyses will provide comparison with experimentally measured temperatures of the HNPF cask, in torch fire environments, which will be obtained in the future. Scope of this study was analytical in nature and involved the use of a computer-based heat transfer analysis methods. Product of this study is the prediction of cask temperatures and internal pressures under normal and torch-fire accident conditions. This study also involved an analysis of the torch fire literature in order to develop an empirically based thermal model for the torch environment. 8 figures, 3 tables

The structure, properties and performance of plasma-sprayed beryllium for fusion applications

International Nuclear Information System (INIS)

Castro, R.G.; Stanek, P.W.; Elliott, K.E.

1995-01-01

Plasma-spray technology is under investigation as a method for producing high thermal conductivity beryllium coatings for use in magnetic fusion applications. Recent investigations have focused on optimizing the plasma-spray process for depositing beryllium coatings on damaged beryllium surfaces. Of particular interest has been optimizing the processing parameters to maximize the through-thickness thermal conductivity of the beryllium coatings. Experimental results will be reported on the use of secondary H 2 gas additions to improve the melting of the beryllium powder and transferred-arc cleaning to improve the bonding between the beryllium coatings and the underlying surface. Information will also be presented on thermal fatigue tests which were done on beryllium coated ISX-B beryllium limiter tiles using 10 sec cycle times with 60 sec cooldowns and an International Thermonuclear Experimental Reactor (ITER) relevant divertor heat flux slightly in excess of 5 MW/m 2

[Atomic/ionic fluorescence in microwave plasma torch discharge with excitation of high current and microsecond pulsed hollow cathode lamp: Ca atomic/ionic fluorescence spectrometry].

Science.gov (United States)

Gong, Zhen-bin; Liang, Feng; Yang, Peng-yuan; Jin, Qin-han; Huang, Ben-li

2002-02-01

A system of atomic and ionic fluorescence spectrometry in microwave plasma torch (MPT) discharge excited by high current microsecond pulsed hollow cathode lamp (HCMP HCL) has been developed. The operation conditions for Ca atomic and ionic fluorescence spectrometry have been optimized. Compared with atomic fluorescence spectrometry (AFS) in argon microwave induced plasma (MIP) and MPT with the excitation of direct current and conventional pulsed HCL, the system with HCMP HCL excitation can improve AFS and ionic fluorescence spectrometry (IFS) detection limits in MPT atomizer and ionizer. Detection limits (3 sigma) with HCMP HCL-MPT-AFS/IFS are 10.1 ng.mL-1 for Ca I 422.7 nm, 14.6 ng.mL-1 for Ca II 393.4 nm, and 37.4 ng.mL-1 for Ca II 396.8 nm, respectively.

Computer simulation of ZrO2 + 8 % Y2O3 and Al2O3 powder particles heating under plasma spraying

International Nuclear Information System (INIS)

Smurov, I.; Gusarov, A.; Hurevich, V.; Kundas, S.; Kashko, T.

2001-01-01

The optimization of plasma spraying processes and investigation of the influence of different parameters and variables on particle trajectories, final temperature distributions and velocities were the aim of this study. A mathematical model for simulation of powder particle heating and acceleration in a plasma jet with particle evaporation and diameter reduction is developed. The choice of the evaporation model strongly depends on the pressure of surrounded gas, for low and atmospheric pressures models were developed. A software with a database for material properties was developed, the first allows to conduct simulation of plasma spraying and contains several models for simulating the different stages of plasma spraying, providing a common interface and access to the database for all the models. The input or output data can be represented as ordinary graphic, distributed diagram or by special way, i.e. animation of particle moving and heating in plasma jet, diagram of phase changing etc. By using this program the process of stabilized zirconium oxide and aluminium oxide coating plasma spraying was simulated. (nevyjel)

Dietary specific antibodies in spray-dried immune plasma prevent enterotoxigenic Escherichia coli F4 (ETEC) post weaning in diarrhoea in piglets

NARCIS (Netherlands)

Niewold, T.A.; Dijk, van A.D.J.; Geenen, P.L.; Roodink, H.; Margry, R.; Meulen, van der J.

2007-01-01

In order to establish the mechanism of spray dried plasma powder (SDPP) in improving pig health and performance, a diet containing either 8% SDPP, spray dried immune plasma powder (SDIPP), or control protein (soybean and whey) ration was fed to piglets in an experimental model of enterotoxigenic

Tribological Behavior of Plasma-Sprayed Al2O3-20 wt.%TiO2 Coating

Science.gov (United States)

Cui, Shiyu; Miao, Qiang; Liang, Wenping; Zhang, Zhigang; Xu, Yi; Ren, Beilei

2017-05-01

Al2O3-20 wt.% TiO2 ceramic coatings were deposited on the surface of Grade D steel by plasma spraying of commercially available powders. The phases and the microstructures of the coatings were investigated by x-ray diffraction and scanning electron microscopy, respectively. The Al2O3-20 wt.% TiO2 composite coating exhibited a typical inter-lamellar structure consisting of the γ-Al2O3 and the Al2TiO5 phases. The dry sliding wear behavior of the coating was examined at 20 °C using a ball-on-disk wear tester. The plasma-sprayed coating showed a low wear rate ( 4.5 × 10-6 mm3 N-1 m-1), which was matrix ( 283.3 × 10-6 mm3 N-1 m-1), under a load of 15 N. In addition, the tribological behavior of the plasma-sprayed coating was analyzed by examining the microstructure after the wear tests. It was found that delamination of the Al2TiO5 phase was the main cause of the wear during the sliding wear tests. A suitable model was used to simulate the wear mechanism of the coating.

A comparative study of tribological behavior of plasma and D-gun sprayed coatings under different wear modes

International Nuclear Information System (INIS)

Sundararajan, G.; Rao, D.S.; Prasad, K.U.M.; Joshi, S.V.

1998-01-01

In recent years, thermal sprayed protective coatings have gained widespread acceptance for a variety of industrial applications. A vast majority of these applications involve the use of thermal sprayed coatings to combat wear. While plasma spraying is the most versatile variant of all the thermal spray processes, the detonation gun (D-gun) coatings have been a novelty until recently because of their proprietary nature. The present study is aimed at comparing the tribological behavior of coatings deposited using the two above techniques by focusing on some popular coating materials that are widely adopted for wear resistant applications, namely, WC-12% Co, Al 2 O 3 , and Cr 3 C 2 -NiCr. To enable a comprehensive comparison of the above indicated thermal spray techniques as well as coating materials, the deposited coatings were extensively characterized employing microstructural evaluation, microhardness measurements, and XRD analysis for phase constitution. The behavior of these coatings under different wear modes was also evaluated by determining their tribological performance when subjected to solid particle erosion tests, rubber wheel sand abrasion tests, and pin-on-disk sliding wear tests. Among all the coating materials studied, D-gun sprayed WC-12% Co, in general, yields the best performance under different modes of wear, whereas plasma sprayed Al 2 O 3 shows least wear resistance to every wear mode

The detailed analysis of the spray time effects of the aluminium coating using self-generated atmospheric plasma spray system on the microstructure and corrosion behaviour

Directory of Open Access Journals (Sweden)

Sh. Khandanjou

Full Text Available In the present paper our aim is to investigate the effect of the spray time of the aluminium coated layers on the microstructure and corrosion behaviour. For this purpose we use the self-generated atmospheric plasma spray system for coating of aluminium on the carbon steel substrate. The different thicknesses of coating are created. To evaluate this effect we use the several analyses such as X-ray diffraction, scanning electron microscope, Micro hardness analysis by Vickers method, Adhesion strength analysis and electrochemical polarization test. The results are very interesting and show that due to low porosity, thicker layers are more homogeneous. The nanoparticles are observed in the thicker layers. The micro hardness tests show that the thicker layers have the better micro hardness value. Next, the adhesion strength tests illustrate that the highest adhesion strength are for longer spray times. On the other hand, the corrosion resistance behaviour of the coating is investigated by electrochemical polarization test. It is shown that the corrosion resistance increases by increasing the thickness due to low percentage of porosity. Keywords: Plasma spray, Thickness, Aluminium, Micro hardness, Corrosion resistance

Fabrication of MgAl2O4 spinel/niobium laminar composites by plasma spraying

International Nuclear Information System (INIS)

Boncoeur, M.; Lochet, N.; Miomandre, F.; Schnedecker, G.

1994-01-01

The feasibility of plasma spray manufacturing of laminar ceramic matrix composites made of alternate thin layers of a ceramic oxide and a metal is demonstrated with a composite made of 7 layers, each 0.2 mm thick, of MgAl 2 O 4 spinel and niobium. Microstructure and mechanical characteristics have been studied with both as-sprayed and heat-treated under vacuum at 1400 C conditions. It is shown that the as-sprayed composite is brittle but becomes pseudo-plastic after heat treatment. These laminar composites are very attractive for the manufacturing of large surface, few millimeter thick components. (from authors). 4 figs., 4 refs

Thermal Conductivity Analysis and Lifetime Testing of Suspension Plasma-Sprayed Thermal Barrier Coatings

Directory of Open Access Journals (Sweden)

Nicholas Curry

2014-08-01

Full Text Available Suspension plasma spraying (SPS has become an interesting method for the production of thermal barrier coatings for gas turbine components. The development of the SPS process has led to structures with segmented vertical cracks or column-like structures that can imitate strain-tolerant air plasma spraying (APS or electron beam physical vapor deposition (EB-PVD coatings. Additionally, SPS coatings can have lower thermal conductivity than EB-PVD coatings, while also being easier to produce. The combination of similar or improved properties with a potential for lower production costs makes SPS of great interest to the gas turbine industry. This study compares a number of SPS thermal barrier coatings (TBCs with vertical cracks or column-like structures with the reference of segmented APS coatings. The primary focus has been on lifetime testing of these new coating systems. Samples were tested in thermo-cyclic fatigue at temperatures of 1100 °C for 1 h cycles. Additional testing was performed to assess thermal shock performance and erosion resistance. Thermal conductivity was also assessed for samples in their as-sprayed state, and the microstructures were investigated using SEM.

Microstructure and Properties of Plasma Sprayed Lead Zirconate Titanate (PZT) Ceramics

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Pala, Zdeněk; Boldyryeva, Hanna; Sedláček, J.; Kmetík, Viliam

2012-01-01

Roč. 2, č. 2 (2012), s. 64-75 ISSN 2079-6412 R&D Projects: GA TA ČR TA01010878 Institutional research plan: CEZ:AV0Z20430508 Keywords : plasma spraying * electroceramics * PZT * phase composition * permittivity Subject RIV: JK - Corrosion ; Surface Treatment of Materials http://www.mdpi.com/2079-6412/2/2/64

Thermal response of plasma sprayed tungsten coating to high heat flux

International Nuclear Information System (INIS)

Liu, X.; Yang, L.; Tamura, S.; Tokunaga, K.; Yoshida, N.; Noda, N.; Xu, Z.

2004-01-01

In order to investigate the thermal response of tungsten coating on carbon and copper substrates by vacuum plasma spray (VPS) or inert gas plasma spray (IPS), annealing and cyclic heat load experiments of these coatings were conducted. It is indicated that the multi-layered tungsten and rhenium interface of VPS-W/CFC failed to act as a diffusion barrier at elevated temperature and tungsten carbides were developed after 1 h incubation time when annealing temperature was higher than 1600 deg. C. IPS-W/Cu and W/C without an intermediate bonding layer were failed by the detachment of the tungsten coating at 900 and 1200 deg. C annealing for several hours, respectively. Cyclic heat load of electron beam with 35 MW/m 2 and 3-s pulse duration indicated that IPS-W/Cu samples failed with local detachment of the tungsten coating within 200 cycles and IPS-W/C showed local cracks by 300 cycles, but VPS-W/CFC withstood 1000 cycles without visible damages. However, crack creation and propagation in VPS-W/CFC were also observed under higher heat load

Modelling of thermal removal of tars in a high temperature stage fed by a plasma torch

International Nuclear Information System (INIS)

Fourcault, A.; Marias, F.; Michon, U.

2010-01-01

The thermal degradation of tars in a chamber fed by a non-transferred plasma torch is theoretically examined in this study. The input of this reactor is a product gas coming from a gasification unit with a temperature of about 800 o C. According to literature, naphthalene and toluene are chosen as model compounds to represent the behaviour of their classes. According to this choice and to the data available in the literature, a reaction pathway for the thermal degradation of tars and its associated kinetics are proposed in this study. This mechanism is introduced in a CSTR model in order to check the influence of the operating parameters of the reactor on the degradation efficiency. These computations clearly show that a complete conversion of toluene (>99.9%) and an important conversion of naphthalene (96.7%) can be reached in the reactor, with concentration levels compatible with the further use of gas engines for electricity production. This theoretical study requires to be validated by comparison with experimental results.

Modelling of thermal removal of tars in a high temperature stage fed by a plasma torch

Energy Technology Data Exchange (ETDEWEB)

Fourcault, A. [Laboratoire Thermique Energetique et Procedes, LaTEP-ENSGTI, rue Jules Ferry, BP 7511, 64075 Pau Cedex (France); Europlasma, 21 rue Daugere, 33520 Bruges (France); Marias, F. [Laboratoire Thermique Energetique et Procedes, LaTEP-ENSGTI, rue Jules Ferry, BP 7511, 64075 Pau Cedex (France); Michon, U. [Europlasma, 21 rue Daugere, 33520 Bruges (France)

2010-09-15

The thermal degradation of tars in a chamber fed by a non-transferred plasma torch is theoretically examined in this study. The input of this reactor is a product gas coming from a gasification unit with a temperature of about 800 C. According to literature, naphthalene and toluene are chosen as model compounds to represent the behaviour of their classes. According to this choice and to the data available in the literature, a reaction pathway for the thermal degradation of tars and its associated kinetics are proposed in this study. This mechanism is introduced in a CSTR model in order to check the influence of the operating parameters of the reactor on the degradation efficiency. These computations clearly show that a complete conversion of toluene (>99.9%) and an important conversion of naphthalene (96.7%) can be reached in the reactor, with concentration levels compatible with the further use of gas engines for electricity production. This theoretical study requires to be validated by comparison with experimental results. (author)

Fabrication of gas turbine water-cooled composite nozzle and bucket hardware employing plasma spray process

Science.gov (United States)

Schilke, Peter W.; Muth, Myron C.; Schilling, William F.; Rairden, III, John R.

1983-01-01

In the method for fabrication of water-cooled composite nozzle and bucket hardware for high temperature gas turbines, a high thermal conductivity copper alloy is applied, employing a high velocity/low pressure (HV/LP) plasma arc spraying process, to an assembly comprising a structural framework of copper alloy or a nickel-based super alloy, or combination of the two, and overlying cooling tubes. The copper alloy is plamsa sprayed to a coating thickness sufficient to completely cover the cooling tubes, and to allow for machining back of the copper alloy to create a smooth surface having a thickness of from 0.010 inch (0.254 mm) to 0.150 inch (3.18 mm) or more. The layer of copper applied by the plasma spraying has no continuous porosity, and advantageously may readily be employed to sustain a pressure differential during hot isostatic pressing (HIP) bonding of the overall structure to enhance bonding by solid state diffusion between the component parts of the structure.

Deposition of Lanthanum Strontium Cobalt Ferrite (LSCF) Using Suspension Plasma Spraying for Oxygen Transport Membrane Applications

Science.gov (United States)

Fan, E. S. C.; Kesler, O.

2015-08-01

Suspension plasma spray deposition was utilized to fabricate dense lanthanum strontium cobalt ferrite oxygen separation membranes (OSMs) on porous metal substrates for mechanical support. The as-sprayed membranes had negligible and/or reversible material decomposition. At the longer stand-off distance (80 mm), smooth and dense membranes could be manufactured using a plasma with power below approximately 81 kW. Moreover, a membrane of 55 μm was observed to have very low gas leakage rates desirable for OSM applications. This thickness could potentially be decreased further to improve oxygen diffusion by using metal substrates with finer surface pores.

Argon Shrouded Plasma Spraying of Tantalum over Titanium for Corrosion Protection in Fluorinated Nitric Acid Media

Science.gov (United States)

Vetrivendan, E.; Jayaraj, J.; Ningshen, S.; Mallika, C.; Kamachi Mudali, U.

2018-02-01

Argon shrouded plasma spraying (ASPS) was used to deposit a Ta coating on commercially pure Ti (CP-Ti) under inert argon, for dissolver vessel application in the aqueous spent fuels reprocessing plant with high plutonium content. Oxidation during plasma spraying was minimized by shrouding argon system. Porosity and oxide content were controlled by optimizing the spraying parameters, to obtain a uniform and dense Ta coating. The Ta particle temperature and velocity were optimized by judiciously controlling the spray parameters, using a spray diagnostic charge-coupled device camera. The corrosion resistance of the Ta coatings developed by ASPS was investigated by electrochemical studies in 11.5 M HNO3 and 11.5 M HNO3 + 0.05 M NaF. Similarly, the durability of the ASPS Ta coating/substrate was evaluated as per ASTM A262 Practice-C test in boiling nitric acid and fluorinated nitric acid for 240 h. The ASPS Ta coating exhibited higher corrosion resistance than the CP-Ti substrate, as evident from electrochemical studies, and low corrosion rate with excellent coating stability in boiling nitric, and fluorinated nitric acid. The results of the present study revealed that tantalum coating by ASPS is a promising strategy for improving the corrosion resistance in the highly corrosive reprocessing environment.

Oxy-gasoline torch. Innovative technology summary report

International Nuclear Information System (INIS)

1998-12-01

Under the deactivation and decommissioning (D and D) Implementation Plan of the US Department of Energy's (DOE) Fernald Environmental Management Project (FEMP), non-recyclable process components and debris that are removed from buildings undergoing D and D are disposed of in an on-site disposal facility (OSDF). Critical to the design and operation of the FEMP's OSDF are provisions to protect against subsidence of the OSDF's cap. Subsidence of the cap could occur if void spaces within the OSDF were to collapse under the overburden of debris and the OSDF cap. Subsidence may create significant depressions in the OSDF's cap in which rainwater could collect and eventually seep into the OSDF. To minimize voids in the FEMP's OSDF, large metallic components are cut into smaller segments that can be arranged more compactly when placed in the OSDF. Component segmentation using an oxy-acetylene cutting torch was the baseline approach used by the FEMP's D and D contractor on Plant 1, Babcock and Wilcox (B and W) Services, Inc., for the dismantlement and size-reduction of large metal components. Although this technology has performed satisfactorily, improvements are sought in the areas of productivity, airborne contamination, safety, and cost. This demonstration investigated the feasibility of using an oxy-gasoline torch as an alternative to the baseline oxy-acetylene torch for segmenting D and D components. This report provides a comparative analysis of the cost and performance of the baseline oxy-acetylene torch currently used by B and W Services, Inc., and the innovative oxy-gasoline torch

Properties of tungsten coating deposited onto copper by high-speed atmospheric plasma spraying

Energy Technology Data Exchange (ETDEWEB)

Huang Jianjun, E-mail: huangjj@szu.edu.cn [Applied Low Temperature Plasma Laboratory, College of Physics Science and Technology, Shenzhen University, Shenzhen 518060 (China); Wang Fan; Liu Ying; Jiang Shishou; Wang Xisheng; Qi Bing; Gao Liang [Applied Low Temperature Plasma Laboratory, College of Physics Science and Technology, Shenzhen University, Shenzhen 518060 (China)

2011-07-01

Tungsten (W) coatings were fabricated on copper (Cu) by high-speed atmospheric plasma spray (HAPS) technique. The properties of the porosity, oxygen content, bonding strength and microhardness were measured. The results obtained indicated that the HAPS-W coating showed good properties particularly in terms of porosity and oxygen content. The porosity of the HAPS-W coating was 2.3% and the distribution of pore size diameter was mainly concentrated in the range of 0.01-1 {mu}m. The oxygen content of the coating measured by means of Nitrogen/Oxygen Determinator was about 0.10 wt.%. These initial results suggest that the HAPS-W coating has achieved the reported properties of the vacuum plasma spray (VPS) W coating. Compared with VPS, HAPS-W technique could provide a convenient and low cost way to obtain adequate W coatings for fusion applications.

Fluctuation-Coupling of Cathode Cavity Pressure and Arc Voltage in a dc Plasma Torch with a Long Inter-Electrode Channel at Reduced Pressure

International Nuclear Information System (INIS)

Cao Jin-Wen; Huang He-Ji; Pan Wen-Xia

2014-01-01

Fluctuations of cathode cavity pressure and arc voltage are observed experimentally in a dc plasma torch with a long inter-electrode channel. The results show that they have the same frequency of around 4 kHz under typical experimental conditions. The observed phase difference between the pressure and the voltage, which is influenced by the path length between the pressure sensor and the cathode cavity, varies with different input powers. Combined with numerical simulation, the position of the pressure perturbation origin is estimated, and the results show that it is located at 0.01–0.05 m upstream of the inter-electrode channel outlet

Structure and properties of plasma sprayed BaTiO3 coatings

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Ageorges, H.; Sedláček, J.; Čtvrtlík, Radim

2010-01-01

Roč. 36, č. 7 (2010), s. 2155-2162 ISSN 0272-8842 R&D Projects: GA AV ČR KAN301370701 Institutional research plan: CEZ:AV0Z20430508; CEZ:AV0Z10100522 Keywords : Cermet * plasma spraying * microstructure * elastic modulus * wear resistance Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 1.471, year: 2010

Microstructure and mechanical properties of plasma sprayed Al2O3 – 13%TiO2 Ceramic Coating

Directory of Open Access Journals (Sweden)

Wahab Juyana A

2017-01-01

Full Text Available This paper focused on the effect of deposition conditions on the microstructural and mechanical properties of the ceramic coating. In this study, Al2O3 – 13%TiO2 coated mild steel were prepared by using atmospheric plasma spray technology with different plasma power ranging from 25 kW to 40 kW. The as-sprayed coatings consist of γ-Al2O3 phase as the major phase and small amount of the titania phase existed in the coating structure. High degree of fully melted region was observed in the surface morphology for the coating sprayed with high plasma power, which lead to the high hardness and low percentage of porosity. In this study, nanoindentation test was carried out to investigate mechanical properties of the coating and the results showed that the coatings possess high elastic behaviour, which beneficial in engineering practice.

In vitro fatigue behaviour of vacuum plasma and detonation gun sprayed hydroxyapatite coatings.

Science.gov (United States)

Gledhill, H C; Turner, I G; Doyle, C

2001-06-01

The fatigue behaviour of vacuum plasma sprayed (VPS) and detonation gun sprayed (DGUN) hydroxyapatite coatings on titanium substrates has been compared in air and in buffered Ringer's solution. There was an increase in the surface microcracking and bulk porosity of both types of coating tested in air. After 1 million cycles in Ringer's solution the VPS coatings had completely delaminated from their substrates. In contrast the DGUN coatings retained their integrity when tested up to 10 million cycles but were beginning to show signs of delamination at the interface.

[Atomic/ionic fluorescence in microwave plasma torch discharge excited by high current microsecond pulsed hollow cathode lamp-europium atomic/ionic fluorescence spectrometry].

Science.gov (United States)

Gong, Z; Liang, F; Yang, P; Jin, Q; Huang, B

1999-06-01

Eu atomic and ionic fluorescence spectrometry in microwave plasma torch discharge excited by high current microsecond pulsed hollow cathode lamp (HCMP HCL-MPT AFS/IFS) was studied. Operating conditions were optimized. The best detection limits for AFS and IFS obtained with a desolvated ultrasonic nebulization system were 42.0 ng/mL for Eu I 462.7 nm and 21.8 ng/mL for Eu II 381.97 nm, respectively, both were better than those given by the instruction manual of a Baird ICP AFS-2000 spectrometer using pneumatic concentric nebulizer with desolvation for AFS, but were significantly higher than those obtained by using the Baird spectrometer with a mini-monochromator and a ultrasonic nebulzer system.

XPS and bioactivity study of the bisphosphonate pamidronate adsorbed onto plasma sprayed hydroxyapatite coatings

International Nuclear Information System (INIS)

McLeod, Kate; Kumar, Sunil; Smart, Roger St.C.; Dutta, Naba; Voelcker, Nicolas H.; Anderson, Gail I.; Sekel, Ron

2006-01-01

This paper reports the use of X-ray photoelectron spectroscopy (XPS) to investigate bisphosphonate (BP) adsorption onto plasma sprayed hydroxyapatite (HA) coatings commonly used for orthopaedic implants. BPs exhibit high binding affinity for the calcium present in HA and hence can be adsorbed onto HA-coated implants to exploit their beneficial properties for improved bone growth at the implant interface. A rigorous XPS analysis of pamidronate, a commonly used nitrogenous BP, adsorbed onto plasma sprayed HA-coated cobalt-chromium substrates has been carried out, aimed at: (a) confirming the adsorption of this BP onto HA; (b) studying the BP diffusion profile in the HA coating by employing the technique of XPS depth profiling; (c) confirming the bioactivity of the adsorbed BP. XPS spectra of plasma sprayed HA-coated discs exposed to a 10 mM aqueous BP solution (pamidronate) for periods of 1, 2 and 24 h showed nitrogen and phosphorous photoelectron signals corresponding to the BP, confirming its adsorption onto the HA substrate. XPS depth profiling of the 2 h BP-exposed HA discs showed penetration of the BP into the HA matrix to depths of at least 260 nm. The bioactivity of the adsorbed BP was confirmed by the observed inhibition of osteoclast (bone resorbing) cell activity. In comparison to the HA sample, the HA sample with adsorbed BP exhibited a 25-fold decrease in primary osteoclast cells

Velocities of gas and plasmas from real time holographic interferograms

International Nuclear Information System (INIS)

Deason, V.A.; Reynolds, L.D.; McIlwain, M.E.

1985-01-01

A truly noninvasive measurement technique for plasma velocity has not been demonstrated. Plasma velocities have been inferred using laser Doppler anemometry or photographic analysis of the position of smoke or small particles. This paper describes an alternate method based on the refractive index change created in a plasma by a gaseous probe material injected into the plasma. This disturbance of the refractive index can be monitored using interferometry. A multipass real time holographic interferometry system was used to follow the changes of the interferometric pattern, and the data was recorded using high speed cinematography. A transparent model of an industrial plasma torch was employed in these studies, and a number of different types of trace gas materials were used to track the plasma flow. Using a combination of multipass interferometry and a laser line absorbing gas, sufficient interferometric sensitivity was obtained to determine plasma velocities in the 100 m/s range. Based on these results, a working plasma torch was constructed. Further studies are planned using this torch and actual plasmas

Development and evaluation of suspension plasma sprayed yttria stabilized zirconia coatings as thermal barriers

Science.gov (United States)

van Every, Kent J.

The insulating effects from thermal barrier coatings (TBCs) in gas turbine engines allow for increased operational efficiencies and longer service lifetimes. Consequently, improving TBCs can lead to enhanced gas turbine engine performance. This study was conducted to investigate if yttria-stabilized zirconia (YSZ) coatings, the standard industrial choice for TBCs, produced from nano-sized powder could provide better thermal insulation than current commericial YSZ coatings generated using micron-sized powders. The coatings for this research were made via the recently developed suspension plasma spraying (SPS) process. With SPS, powders are suspended in a solvent containing dispersing agents; the suspension is then injected directly into a plasma flow that evaporates the solvent and melts the powder while transporting it to the substrate. Although related to the industrial TBC production method of air plasma spraying (APS), SPS has two important differences---the ability to spray sub-micron diameter ceramic particles, and the ability to alloy the particles with chemicals dissolved in the solvent. These aspects of SPS were employed to generate a series of coatings from suspensions containing ˜100 nm diameter YSZ powder particles, some of which were alloyed with neodymium and ytterbium ions from the solvent. The SPS coatings contained columnar structures not observed in APS TBCs; thus, a theory was developed to explain the formation of these features. The thermal conductivity of the coatings was tested to evaluate the effects of these unique microstructures and the effects of the alloying process. The results for samples in the as-sprayed and heat-treated conditions were compared to conventional YSZ TBCs. This comparison showed that, relative to APS YSZ coatings, the unalloyed SPS samples typically exhibited higher as-sprayed and lower heat-treated thermal conductivities. All thermal conductivity values for the alloyed samples were lower than conventional YSZ TBCs

Temperature of thermal plasma jets: A time resolved approach

Energy Technology Data Exchange (ETDEWEB)

Sahasrabudhe, S N; Joshi, N K; Barve, D N; Ghorui, S; Tiwari, N; Das, A K, E-mail: sns@barc.gov.i [Laser and Plasma Technology Division, Bhabha Atomic Research Centre, Mumbai - 400 094 (India)

2010-02-01

Boltzmann Plot method is routinely used for temperature measurement of thermal plasma jets emanating from plasma torches. Here, it is implicitly assumed that the plasma jet is 'steady' in time. However, most of the experimenters do not take into account the variations due to ripple in the high current DC power supplies used to run plasma torches. If a 3-phase transductor type of power supply is used, then the ripple frequency is 150 Hz and if 3- phase SCR based power supply is used, then the ripple frequency is 300 Hz. The electrical power fed to plasma torch varies at ripple frequency. In time scale, it is about 3.3 to 6.7 ms for one cycle of ripple and it is much larger than the arc root movement times which are within 0.2 ms. Fast photography of plasma jets shows that the luminosity of plasma jet also varies exactly like the ripple in the power supply voltage and thus with the power. Intensity of line radiations varies nonlinearly with the instantaneous power fed to the torch and the simple time average of line intensities taken for calculation of temperature is not appropriate. In this paper, these variations and their effect on temperature determination are discussed and a method to get appropriate data is suggested. With a small adaptation discussed here, this method can be used to get temperature profile of plasma jet within a short time.

Plasma sprayed TiC coatings for first wall protection in fusion devices

International Nuclear Information System (INIS)

Groot, P.; Laan, J.G. van der; Laas, L.; Mack, M.; Dvorak, M.

1989-01-01

For protection of plasma facing components in nuclear fusion devices thick titanium carbide coatings are being developed. Coatings have been produced by plasma spraying at atmospheric pressure (APS) and low pressure (LPPS) and analyzed with respect to microstructure and chemical composition. Thermo-mechanical evaluation has been performed by applying short pulse laser heat flux tests. The influence of coating thickness and porosity on the resistance to spalling by thermal shocks appears to be more important than aspects of chemical composition. (author)

Plasma-Sprayed Hydroxylapatite-Based Coatings: Chemical, Mechanical, Microstructural, and Biomedical Properties

Science.gov (United States)

Heimann, Robert B.

2016-06-01

This contribution discusses salient properties and functions of hydroxylapatite (HA)-based plasma-sprayed coatings, including the effect on biomedical efficacy of coating thickness, phase composition and distribution, amorphicity and crystallinity, porosity and surface roughness, cohesion and adhesion, micro- and nano-structured surface morphology, and residual coating stresses. In addition, it will provide details of the thermal alteration that HA particles undergo in the extremely hot plasma jet that leads to dehydroxylated phases such as oxyhydroxylapatite (OHA) and oxyapatite (OA) as well as thermal decomposition products such as tri-(TCP) and tetracalcium phosphates (TTCP), and quenched phases such as amorphous calcium phosphate (ACP). The contribution will further explain the role of ACP during the in vitro interaction of the as-deposited coatings with simulated body fluid resembling the composition of extracellular fluid (ECF) as well as the in vivo responses of coatings to the ECF and the host tissue, respectively. Finally, it will briefly describe performance profiles required to fulfill biological functions of osteoconductive bioceramic coatings designed to improve osseointegration of hip endoprostheses and dental root implants. In large parts, the content of this contribution is a targeted review of work done by the author and his students and coworkers over the last two decades. In addition, it is considered a stepping stone toward a standard operation procedure aimed at depositing plasma-sprayed bioceramic implant coatings with optimum properties.

Temperature dependence of bending strength for plasma sprayed zirconia coating; Plasuma yosha zirconia himaku no magetsuyosa no ondo izonsei

Energy Technology Data Exchange (ETDEWEB)

Arai, M.; Sakuma, T. [Central Research Inst. of Electric Power Industry, Tokyo (Japan)] Mizutani, T. [Tokyo Inst. of Tech. (Japan)] Kishimoto, K. [Tokyo Inst. of Tech. (Japan). Faculty of Engineering] Saito, M. [Toshiba Corp. (Japan). Heavy Apparatus Engineering Lab.

1998-02-01

Plasma sprayed zirconia applying to the thermal barrier coating in gas turbine has been developing for protecting the hot parts such as blades and nozzles from high-temperature enviroments. In this paper, four point bending tests under various temperature conditions are conducted on plasma sprayed zirconia and its mechanical properties are examined. Results show that the bending strength at room temperature for plasma sprayed zirconia is much lower than that of sintered zirconia and is decreased with the increase in temperature. However, Weibull modulus at each temperature is relatively large and the dispersion of bending strength is very small in comparison with that of sintered zirconia. It is also clarified by the SEM observations of fracture surface that many defects such as debonding and microcrack are responsible for the lower bending strength. 9 refs., 8 figs., 1 tab.

A comparative physico-chemical study of chlorapatite and hydroxyapatite: from powders to plasma sprayed thin coatings.

Science.gov (United States)

Demnati, I; Grossin, D; Combes, C; Parco, M; Braceras, I; Rey, C

2012-10-01

Due to their bioactivity and osteoconductivity, hydroxyapatite (HA) plasma sprayed coatings have been widely developed for orthopedic uses. However, the thermodynamic instability of HA leads frequently to a mixture of phases which limit the functional durability of the coating. This study investigates the plasma spraying of chlorapatite (ClA) powder, known to melt without decomposition, onto pure titanium substrates using a low energy plasma spray system (LEPS). Pure ClA powder was prepared by a solid gas reaction at 950 °C and thermogravimetric analysis showed the good thermal stability of ClA powder in the range 30-1400 °C compared to that of the HA powder. Characterization of ClA coating showed that ClA had a very high crystalline ratio and no other crystalline phase was detected in the coating. HA and ClA coatings composition, microstructure and in vitro bioactivity potential were studied, compared and discussed. In vitro SBF test on HA and ClA coatings revealed the formation of a poorly crystalline apatite on the coating surface suggesting that we could expect a good osteoconductivity especially for the ClA coating prepared by the LEPS system.

Investigation of Plasma Spray Coatings as an Alternative to Hard Chrome Plating on Internal Surfaces

National Research Council Canada - National Science Library

Legg, Keith O; Sartwell, Bruce D; Legoux, Jean-Gabriel; Nestler, Montia; Dambra, Christopher; Wang, Daming; Quets, John; Natishan, Paul; Bretz, Philip; Devereaux, Jon

2006-01-01

.... This document constitutes the final report on an investigation of deposition of coatings using miniature plasma spray guns that could replace hard chromium on internal surfaces where conventional...

Controlling of Nitriding Process on Reactive Plasma Spraying of Al Particles

International Nuclear Information System (INIS)

Shahien, Mohammed; Yamada, Motohiro; Yasui, Toshiaki; Fukumoto, Masahiro

2011-01-01

Reactive plasma spraying (RPS) has been considered as a promising technology for in-situ formation of aluminum nitride (AlN) thermally sprayed coatings. To fabricate thick A lN coatings in RPS process, controlling and improving the in-flight nitriding reaction of Al particles is required. In this study, it was possible to control the nitriding reaction by using ammonium chloride (NH 4 Cl) powders. Thick and dense AlN coating (more than 300 μm thickness) was successfully fabricated with small addition of NH 4 Cl powders. Thus, addition of NH 4 Cl prevented the Al aggregation by changing the reaction pathway to a mild way with no explosive mode (relatively low heating rates) and it acts as a catalyst, nitrogen source and diluent agent.

Influence of Microstructure on Thermal Properties of Axial Suspension Plasma-Sprayed YSZ Thermal Barrier Coatings

Czech Academy of Sciences Publication Activity Database

Ganvir, A.; Curry, N.; Markocsan, N.; Nylen, P.; Joshi, S.; Vilémová, Monika; Pala, Zdeněk

2016-01-01

Roč. 25, 1-2 (2016), s. 202-212 ISSN 1059-9630. [ITSC 2015: International Thermal Spray Conference and Exposition. Long Beach, California, 11.05.2015-14.05.2015] Institutional support: RVO:61389021 Keywords : axial injection * column ar microstructure * porosity * suspension plasma spraying * thermal conductivity * thermal diffusivity Subject RIV: JK - Corrosion ; Surface Treatment of Materials Impact factor: 1.488, year: 2016 http://link.springer.com/article/10.1007%2Fs11666-015-0355-7

Finite element analysis of residual stress in plasma-sprayed ceramic

International Nuclear Information System (INIS)

Mullen, R.L.; Hendricks, R.C.; McDonald, G.

1985-01-01

Residual stress in a ZrO 2 -Y 2 O 3 ceramic coating resulting from the plasma spraying operation is calculated. The calculations were done using the finite element method. Both thermal and mechanical analysis were performed. The resulting residual stress field was compared to the measurements obtained by Hendricks and McDonald. Reasonable agreement between the predicted and measured moment occurred. However, the resulting stress field is not in pure bending

Application and research of special waste plasma disposal technology

International Nuclear Information System (INIS)

Lan Wei

2007-12-01

The basic concept of plasma and the principle of waste hot plasma disposal technology are simply introduced. Several sides of application and research of solid waste plasma disposal technology are sumed up. Compared to the common technology, the advantages of waste hot plasma disposal technology manifest further. It becomes one of the most prospective and the most attended high tech disposal technology in particular kind of waste disposal field. The article also simply introduces some experiment results in Southwest Institute of Physics and some work on the side of importation, absorption, digestion, development of foreign plasma torch technology and researching new power sources for plasma torch. (authors)

Thermal plasma spraying for SOFCs: Applications, potential advantages, and challenges

Energy Technology Data Exchange (ETDEWEB)

Hui, Rob; Wang, Zhenwei; Jankovic, Jasna; Yick, Sing; Maric, Radenka; Ghosh, Dave [National Research Council Institute for Fuel Cell Innovation, 4250 Wesbrook Mall, Vancouver, BC V6T 1W5 (Canada); Kesler, Olivera [National Research Council Institute for Fuel Cell Innovation, 4250 Wesbrook Mall, Vancouver, BC V6T 1W5 (Canada); Department of Mechanical Engineering, University of British Columbia, 2054-6250 Applied Science Lane, Vancouver, BC V6T 1Z4 (Canada); Rose, Lars [National Research Council Institute for Fuel Cell Innovation, 4250 Wesbrook Mall, Vancouver, BC V6T 1W5 (Canada); Department of Materials Engineering, University of British Columbia, 309-6350 Stores Road, Vancouver, BC V6T 1Z4 (Canada)

2007-07-10

In this article, the applications, potential advantages, and challenges of thermal plasma spray (PS) processing for nanopowder production and cell fabrication of solid oxide fuel cells (SOFCs) are reviewed. PS processing creates sufficiently high temperatures to melt all materials fed into the plasma. The heated material can either be quenched into oxide powders or deposited as coatings. This technique has been applied to directly deposit functional layers as well as nanopowder for SOFCs application. In particularly, low melting point and highly active electrodes can be directly fabricated on zirconia-based electrolytes. This is a simple processing technique that does not require the use of organic solvents, offering the opportunity for flexible adjustment of process parameters, and significant time saving in production of the cell and cost reduction compared with tape casting, screen printing and sintering processing steps. Most importantly, PS processing shows strong potential to enable the deposition of metal-supported SOFCs through the integrated fabrication of membrane-electrode assemblies (MEA) on porous metallic substrates with consecutive deposition steps. On the other hand, the application of PS processing to produce SOFCs faces some challenges, such as insufficient porosity of the electrodes, the difficulty of obtaining a thin (<10 {mu}m) and dense electrolyte layer. Fed with H{sub 2} as the fuel gas and oxygen as the oxidant gas, the plasma sprayed cell reached high power densities of 770 mW cm{sup -2} at 900 C and 430 mW cm{sup -2} at 800 C at a cell voltage of 0.7 V. (author)

C_1_8-attached membrane funnel-based spray ionization mass spectrometry for quantification of anti-diabetic drug from human plasma

International Nuclear Information System (INIS)

Li, Wan; Chen, Xiangfeng; Wong, Y.-L. Elaine; Hung, Y.-L. Winnie; Wang, Ze; Deng, Liulin; Dominic Chan, T.-W.

2016-01-01

In this work, sorbent-attached membrane funnel-based spray ionization mass spectrometry was explored for quantitative analysis of anti-diabetic drugs spiked in human plasma. C_1_8-attached membrane funnel was fabricated for in situ extraction and clean-up to alleviate matrix suppression effect in the ionization process. Repaglinide was used as a target analyte of anti-diabetic drugs. Under optimal working conditions, good linearity (R"2 > 0.99) was obtained in the concentration range of 1–100 ng mL"−"1. The method detection limit of target drugs spiked in the human plasma was around 0.30 ng mL"−"1. Through the application of an isotope-labeled internal standard, the signal fluctuation caused by residual background matrices was largely alleviated and the precision of measurement (RSD) was below 15%. The recovery of repaglinide for 5, 25, and 100 ng mL"−"1 of spiked human plasma matrixes ranged from 87% to 112%. The developed method was successfully applied to determine repaglinide in plasma volunteers who orally received a dose of drug association. Our results demonstrated that membrane funnel-based spray is a simple and sensitive method for rapid screening analysis of complex biological samples. - Highlights: • Sorbent attached membrane funnel based spray platform was used for drug determination in human plasma. • The matrix suppression effect of human plasma was largely eliminated. • The method was applied to determine repaglinide in plasma volunteers. • Membrane funnel-based spray is promising for analysis of biological samples.

Interaction of plasma-sprayed YBa/sub y/Cu/sub 3/0/sub x/ coatings with alumina substrates

Energy Technology Data Exchange (ETDEWEB)

Moreau, C; Parent, L; Dallaire, S; Champagne, B

1989-01-01

Superconducting YBa/sub 2/Cu/sub 3/O/sub x/ coatings can be obtained by plasma spraying. Since the as-sprayed coatings do not have an appropriate crystalline structure and are not superconducting, a thermal treatment must be done for crystallizing them in the appropriate YBa/sub 2/Cu/sub 3/O/sub x/ phase. During heat treatment, reactions between the substrate and coating occur and in some cases, may prevent superconducting properties to be obtained. In the present study, YBa/sub 2/Cu/sub 3/O sub/x/ coatings have been deposited on alumina substrates by plasma spraying and heat treated under flowing oxygen at 950/sup 0/C for different periods of time. The modification in coating microstructure has been investigated after different heat treatments. A degradation mechanism of superconducting coatings is proposed. 14 refs., 7 figs., 2 tabs.

Structure and properties of plasma sprayed BaTiO(3) coatings: Spray parameters versus structure and photocatalytic activity

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Ageorges, H.; Štengl, Václav; Murafa, Nataliya; Píš, I.; Zahoranová, T.; Nehasil, V.; Pala, Zdeněk

2011-01-01

Roč. 37, č. 7 (2011), s. 2561-2567 ISSN 0272-8842 R&D Projects: GA AV ČR IAAX00430803 Institutional research plan: CEZ:AV0Z20430508; CEZ:AV0Z40320502 Keywords : Spectroscopy * Optical properties * BaTiO3 * Plasma spraying * Photocatalysis Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 1.751, year: 2011 http://www.sciencedirect.com/science/article/pii/S0272884211002173

Failure Analysis of Multilayered Suspension Plasma-Sprayed Thermal Barrier Coatings for Gas Turbine Applications

Science.gov (United States)

Gupta, M.; Markocsan, N.; Rocchio-Heller, R.; Liu, J.; Li, X.-H.; Östergren, L.

2018-02-01

Improvement in the performance of thermal barrier coatings (TBCs) is one of the key objectives for further development of gas turbine applications. The material most commonly used as TBC topcoat is yttria-stabilized zirconia (YSZ). However, the usage of YSZ is limited by the operating temperature range which in turn restricts the engine efficiency. Materials such as pyrochlores, perovskites, rare earth garnets are suitable candidates which could replace YSZ as they exhibit lower thermal conductivity and higher phase stability at elevated temperatures. The objective of this work was to investigate different multilayered TBCs consisting of advanced topcoat materials fabricated by suspension plasma spraying (SPS). The investigated topcoat materials were YSZ, dysprosia-stabilized zirconia, gadolinium zirconate, and ceria-yttria-stabilized zirconia. All topcoats were deposited by TriplexPro-210TM plasma spray gun and radial injection of suspension. Lifetime of these samples was examined by thermal cyclic fatigue and thermal shock testing. Microstructure analysis of as-sprayed and failed specimens was performed with scanning electron microscope. The failure mechanisms in each case have been discussed in this article. The results show that SPS could be a promising route to produce multilayered TBCs for high-temperature applications.

Thermophysical properties of YSZ and YCeSZ suspension plasma sprayed coatings having different microstructures

Czech Academy of Sciences Publication Activity Database

Sokołowski, P.; Björklund, S.; Mušálek, Radek; Candidato, Jr., R.T.; Pawłowski, L.; Nait-Ali, B.; Smith, D.

2017-01-01

Roč. 318, May (2017), s. 28-38 ISSN 0257-8972. [International Meeting on Thermal Spraying (RIPT)/7./. Limoges, 09.12.2015-11.12.2015] R&D Projects: GA ČR GA15-12145S Institutional support: RVO:61389021 Keywords : Thermal Barrier Coatings (TBC) * Suspension Plasma Spraying * Thermal conductivity * Specific heat * Thermal dilatation * Response function method Subject RIV: JK - Corrosion ; Surface Treatment of Materials OBOR OECD: Coating and films Impact factor: 2.589, year: 2016 http://www.sciencedirect.com/science/article/pii/S0257897217302086

Role of process conditions on the microstructure, stoichiometry and functional performance of atmospheric plasma sprayed La(Sr)MnO3 coatings

Science.gov (United States)

Han, Su Jung; Chen, Yikai; Sampath, Sanjay

2014-08-01

Strontium doped lanthanum manganite (LSM) perovskite coatings were produced via atmospheric plasma spray technique to examine their applicability as electrically conductive coatings to protect chromium-poisoning of cathode side metallic interconnects in solid oxide fuel cells. Various plasma spray process conditions were manipulated including plasma power, total gas flow and content of H2 in the plasma gas in order to understand their effects on coating properties as well as efficacy as a protectant against Cr-poisoning. In-flight temperatures and velocities of spray particles were monitored for the various plasma spray conditions enabling assessment of thermal and kinetic energies of LSM particles. As anticipated, coating density improves with increasing thermal and/or kinetic energies of the LSM particles. However, the LSM particles also experienced significant phase decomposition at higher thermal exposure and longer residence time conditions. Due to preferential loss of oxygen and manganese, La2O3 phase is also formed under certain processing regimes. The resultant mixed-phase coating is ineffective both from electrical transport and as a protective coating for the metallic interconnect. Concomitantly, coatings with limited decomposition show excellent conductivity and protection characteristics demonstrating the need for mechanism driven process optimization for these functional oxide coatings.

Novel Approach in the Use of Plasma Spray: Preparation of Bulk Titanium for Bone Augmentations

Directory of Open Access Journals (Sweden)

Michaela Fousova

2017-08-01

Full Text Available Thermal plasma spray is a common, well-established technology used in various application fields. Nevertheless, in our work, this technology was employed in a completely new way; for the preparation of bulk titanium. The aim was to produce titanium with properties similar to human bone to be used for bone augmentations. Titanium rods sprayed on a thin substrate wire exerted a porosity of about 15%, which yielded a significant decrease of Young′s modulus to the bone range and provided rugged topography for enhanced biological fixation. For the first verification of the suitability of the selected approach, tests of the mechanical properties in terms of compression, bending, and impact were carried out, the surface was characterized, and its compatibility with bone cells was studied. While preserving a high enough compressive strength of 628 MPa, the elastic modulus reached 11.6 GPa, thus preventing a stress-shielding effect, a generally known problem of implantable metals. U-2 OS and Saos-2 cells derived from bone osteosarcoma grown on the plasma-sprayed surface showed good viability.

Plasma arc and cold crucible furnace vitrification for medium level waste: a review

International Nuclear Information System (INIS)

Poitou, S.; Fiquet, O.; Bourdeloie, C.; Gramondi, P.; Rebollo, F.; Girold, C.; Charvillat, J.P.; Boen, R.; Jouan, A.; Ladirat, C.; Nabot, J.P.; Ochem, D.; Baronnet, J.M.

2001-01-01

Initially developed for high-level waste reprocessing, several vitrification processes have been under study since the 80's at the French Atomic Energy Commission (CEA) for other waste categories. According to the French law concerning waste management research passed on December 30, 1991, vitrification may be applied to mixed medium-level waste. A review of processes developed at CEA is presented: cold crucible furnace heated by induced current, refractory furnace heated by nitrogen transferred arc plasma torch, and coupling of cold crucible furnace with oxygen transferred plasma arc twin torch. Furthermore, gas post-combustion has been studied with an oxygen non-transferred plasma torch. (authors)

Relationship Between Particle and Plasma Properties and Coating Characteristics of Samaria-Doped Ceria Prepared by Atmospheric Plasma Spraying for Use in Solid Oxide Fuel Cells

Science.gov (United States)

Cuglietta, Mark; Kesler, Olivera

2012-06-01

Samaria-doped ceria (SDC) has become a promising material for the fabrication of high-performance, intermediate-temperature solid oxide fuel cells (SOFCs). In this study, the in-flight characteristics, such as particle velocity and surface temperature, of spray-dried SDC agglomerates were measured and correlated to the resulting microstructures of SDC coatings fabricated using atmospheric plasma spraying, a manufacturing technique with the capability of producing full cells in minutes. Plasmas containing argon, nitrogen and hydrogen led to particle surface temperatures higher than those in plasmas containing only argon and nitrogen. A threshold temperature for the successful deposition of SDC on porous stainless steel substrates was calculated to be 2570 °C. Coating porosity was found to be linked to average particle temperature, suggesting that plasma conditions leading to lower particle temperatures may be most suitable for fabricating porous SOFC electrode layers.

Structure and mechanical properties of plasma sprayed coatings of titania and alumina

Czech Academy of Sciences Publication Activity Database

Ctibor, Pavel; Boháč, Petr; Stranyánek, Martin; Čtvrtlík, Radim

2006-01-01

Roč. 26, č. 16 (2006), s. 3509-3514 ISSN 0955-2219 Institutional research plan: CEZ:AV0Z20430508; CEZ:AV0Z10100523 Keywords : Plasma spraying * Optical microscopy * Mechanical properties * TiO2 * Al2O3 Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass Impact factor: 1.576, year: 2006

In Situ Fabrication of AlN Coating by Reactive Plasma Spraying of Al/AlN Powder

Directory of Open Access Journals (Sweden)

Mohammed Shahien

2011-10-01

Full Text Available Reactive plasma spraying is a promising technology for the in situ formation of aluminum nitride (AlN coatings. Recently, it became possible to fabricate cubic-AlN-(c-AlN based coatings through reactive plasma spraying of Al powder in an ambient atmosphere. However, it was difficult to fabricate a coating with high AlN content and suitable thickness due to the coalescence of the Al particles. In this study, the influence of using AlN additive (h-AlN to increase the AlN content of the coating and improve the reaction process was investigated. The simple mixing of Al and AlN powders was not suitable for fabricating AlN coatings through reactive plasma spraying. However, it was possible to prepare a homogenously mixed, agglomerated and dispersed Al/AlN mixture (which enabled in-flight interaction between the powder and the surrounding plasma by wet-mixing in a planetary mill. Increasing the AlN content in the mixture prevented coalescence and increased the nitride content gradually. Using 30 to 40 wt% AlN was sufficient to fabricate a thick (more than 200 µm AlN coating with high hardness (approximately 1000 Hv. The AlN additive prevented the coalescence of Al metal and enhanced post-deposition nitriding through N₂ plasma irradiation by allowing the nitriding species in the plasma to impinge on a larger Al surface area. Using AlN as a feedstock additive was found to be a suitable method for fabricating AlN coatings by reactive plasma spraying. Moreover, the fabricated coatings consist of hexagonal (h-AlN, c-AlN (rock-salt and zinc-blend phases and certain oxides: aluminum oxynitride (Al₅O₆N, cubic sphalerite Al₂₃O₂₇N₅ (ALON and Al₂O₃. The zinc-blend c-AlN and ALON phases were attributed to the transformation of the h-AlN feedstock during the reactive plasma spraying. Thus, the zinc-blend c