WorldWideScience

Sample records for pitting corrosion inhibition

  1. Initiation and inhibition of pitting corrosion on reinforcing steel under natural corrosion conditions

    Energy Technology Data Exchange (ETDEWEB)

    Abd El Wanees, S., E-mail: s_wanees@yahoo.com [Chemistry Department, Faculty of Science, University of Tabuk, Tabuk (Saudi Arabia); Chemistry Department, Faculty of Science, Zagazig University, Zagazig 44519 (Egypt); Bahgat Radwan, A. [Center for Advanced Materials, Qatar University, Doha 2713 (Qatar); Alsharif, M.A. [Chemistry Department, Faculty of Science, University of Tabuk, Tabuk (Saudi Arabia); Abd El Haleem, S.M. [Chemistry Department, Faculty of Science, Zagazig University, Zagazig 44519 (Egypt)

    2017-04-01

    Initiation and inhibition of pitting corrosion on reinforcing steel in saturated, naturally aerated Ca(OH){sub 2} solutions, under natural corrosion conditions, are followed through measurements of corrosion current, electrochemical impedance spectroscopy and SEM investigation. Induction period for pit initiation and limiting corrosion current for pit propagation are found to depend on aggressive salt anion and cation-types, as well as, concentration. Ammonium chlorides and sulfates are more corrosive than the corresponding sodium salts. Benzotriazole and two of its derivatives are found to be good inhibitors for pitting corrosion of reinforcing steel. Adsorption of these compounds follows a Langmuir adsorption isotherm. The thermodynamic functions ΔE{sup ∗}, ΔH{sup ∗} and ΔS{sup ∗} for pitting corrosion processes in the absence and presence of inhibitor are calculated and discussed. - Highlights: • Cl{sup −} and SO{sub 4} {sup 2-} induce pitting corrosion on passive reinforcing steel. • Initiation and propagation of pitting depend on cation and anion types. • Inhibition is based on adsorption according to Langmuir isotherm.

  2. Inhibition of Copper Pitting Corrosion in Aggressive Potable Waters

    Directory of Open Access Journals (Sweden)

    Emily Sarver

    2012-01-01

    Full Text Available Copper pitting corrosion can lead to premature plumbing failures, and can be caused by aggressive potable waters characterized by high pH, free chlorine residual and low alkalinity. In such waters and under continuous flow, certain inhibitors including phosphate, silica or natural organic matter may greatly reduce pitting occurrence. In the current work, 1 mg/L phosphate (as P completely prevented initiation of pits, and 5 mg/L silica (as Si significantly decelerated pitting. However, much lower doses of these inhibitors had little benefit and actually accelerated the rate of attack in some cases. Effects of organic matter were dependent on both the type (e.g., natural versus ozonated humic substances and dosage. Dose-response effects of free chlorine and alkalinity were also investigated. Based on electrochemical data, pits initiated more rapidly with increased free chlorine, but even moderate levels of chlorine (~0.4 mg/L eventually caused severe pitting. High alkalinity decreased pit propagation rates but did not prevent pit formation.

  3. Corrosion and inhibition of stainless steel pitting corrosion in alkaline medium and the effect of Cl- and Br- anions

    International Nuclear Information System (INIS)

    Refaey, S.A.M.; Taha, F.; El-Malak, A.M. Abd

    2005-01-01

    The effect of carbonate anion on the pitting corrosion and inhibition behavior of stainless steel samples (304L SS and 316L SS) has been studied using potentiodynamic and scanning electron microscope (SEM) techniques. The effect of concentration of CO 3 2- ions, pH, potential scanning rate and the composition of stainless steel are discussed. Additions of Cl - and Br - ions into the carbonate solution increase the anodic dissolution of stainless steel and decrease its pitting corrosion resistance. The effect of CO 3 2- anion on the inhibition of chloride and bromide pitting corrosion of the two stainless steel types has been studied also. Pitting corrosion decrease with the increasing of sodium carbonate concentration, i.e. increases the resistance of stainless steels towards the chloride and bromide pitting corrosion. This inhibition effect argued to formation of [Fe,Cr]CO 3 film caused by preferential adsorption of the CO 3 2- ion, leading to instantaneous repair of weak sites for pit nucleation

  4. Inhibiting pitting corrosion in carbon steel exposed to dilute radioactive waste slurries

    International Nuclear Information System (INIS)

    Zapp, P.E.; Hobbs, D.T.

    1991-01-01

    Dilute caustic high-level radioactive waste slurries can induce pitting corrosion in carbon steel. Cyclic potentiodynamic polarization tests were conducted in simulated and actual waste solutions to determine minimum concentrations of sodium nitrate which inhibit pitting in ASTM A537 class 1 steel exposed to these solutions. Susceptibility to pitting was assessed through microscopic inspection of specimens and inspection of polarization scans. Long-term coupon immersion tests were conducted to verify the nitrite concentrations established by the cyclic potentiodynamic polarization tests. The minimum effective nitrite concentration is expressed as a function of the waste nitrate concentration and temperature

  5. Pitting corrosion inhibition of aluminum 2024 by Bacillus biofilms secreting polyaspartate or gamma-polyglutamate.

    Science.gov (United States)

    Ornek, D; Jayaraman, A; Syrett, B C; Hsu, C-H; Mansfeld, F B; Wood, T K

    2002-04-01

    Pitting corrosion of aluminum 2024 in Luria Bertani medium was reduced by the secretion of anionic peptides by engineered and natural Bacillus biofilms and was studied in continuous reactors using electrochemical impedance spectroscopy. Compared to sterile controls, pitting was reduced dramatically by the presence of the biofilms. The secretion of a 20 amino acid polyaspartate peptide by an engineered Bacillus subtilis WB600/pBE92-Asp biofilm slightly reduced the corrosion rate of the passive aluminum alloy at pH 6.5; however, the secretion of gamma-polyglutamate by a Bacillus licheniformis biofilm reduced the corrosion rate by 90% (compared to the B. subtilis WB600/pBE92 biofilm which did not secrete polyaspartate or gamma-polyglutamate). The corrosion potential ( E(corr)) of aluminum 2024 was increased by about 0.15-0.44 V due to the formation of B. subtilis and B. licheniformis biofilms as compared to sterile controls. The increase of E(corr) and the observed prevention of pitting indicate that the pitting potential ( E(pit)) had increased. This result and the further decrease of corrosion rates for the passive aluminum alloy suggest that the rate of the anodic metal dissolution reaction was reduced by an inhibitor produced by the biofilms. Purified gamma-polyglutamate also decreased the corrosion rates of aluminum 2024.

  6. Electrochemical analysis of the corrosion inhibition effect of trypsin complex on the pitting corrosion of 420 martensitic stainless steel in 2M H2SO4 solution.

    Science.gov (United States)

    Loto, Roland Tolulope

    2018-01-01

    Inhibition effect of trypsin complex (TC) on the pitting corrosion of martensitic stainless steel (type 420) in 1M H2SO4 solution was studied with potentiodynamic polarization, open circuit potential measurement and optical microscopy. TC reduced the corrosion rate of the steel with maximum inhibition efficiency of 80.75%. Corrosion potential shifted anodically due to the electrochemical action of TC. The pitting potential increased from 1.088VAg/AgCl (3M) at 0% TC to 1.365VAg/AgCl(3M) at 4% TC. TC shifts the open circuit corrosion potential from -0.270s at 0% TC concentration to -0.255V at 5% TC. The compound completely adsorbed onto the steel according to Langmuir, Frumkin and Temkin isotherms. ATF-FTIR spectroscopy confirmed the inhibition mode to be through surface coverage. Thermodynamic calculations showed physisorption molecular interaction. Corrosion pits are present on the uninhibited 420 morphology in comparison to TC inhibited surface which slightly deteriorated.

  7. pitting corrosion susceptibility pitting corrosion susceptibility of aisi

    African Journals Online (AJOL)

    eobe

    2DEPARTMENT OF MECHANICAL ENGINEERING, UNIVERSITY OF BENIN, BENIN- CITY, EDO STATE, NIGERIA. E-mail addresses: ... fluids and aggressive chemicals. Pitting corrosion ... the kitchen, food manufacturing and dispensing and.

  8. Pitting corrosion of zirconium in aqueous solution

    International Nuclear Information System (INIS)

    El Shayeb, H.A.; Abd El Wahab, F.M.; Abd Elk Meguid, E.A.

    1994-01-01

    The open circuit potentials of the Zr electrode are followed as a function of time in various aqueous solutions till attainment of steady state values.The results are discussed on the basis of oxide film thickening and repair. Pitting corrosion of Zr was examined in chloride solutions using the potentiodynamic technique. The effect of some inorganic and organic additives was also investigated for inhibiting the pitting corrosion of Zr and the relative performance is presented and discussed. (author). 21 refs., 6 figs., 1 tab

  9. Stochastic modeling of pitting corrosion: A new model for initiation and growth of multiple corrosion pits

    International Nuclear Information System (INIS)

    Valor, A.; Caleyo, F.; Alfonso, L.; Rivas, D.; Hallen, J.M.

    2007-01-01

    In this work, a new stochastic model capable of simulating pitting corrosion is developed and validated. Pitting corrosion is modeled as the combination of two stochastic processes: pit initiation and pit growth. Pit generation is modeled as a nonhomogeneous Poisson process, in which induction time for pit initiation is simulated as the realization of a Weibull process. In this way, the exponential and Weibull distributions can be considered as the possible distributions for pit initiation time. Pit growth is simulated using a nonhomogeneous Markov process. Extreme value statistics is used to find the distribution of maximum pit depths resulting from the combination of the initiation and growth processes for multiple pits. The proposed model is validated using several published experiments on pitting corrosion. It is capable of reproducing the experimental observations with higher quality than the stochastic models available in the literature for pitting corrosion

  10. Stochastic modeling of pitting corrosion: A new model for initiation and growth of multiple corrosion pits

    Energy Technology Data Exchange (ETDEWEB)

    Valor, A. [Facultad de Fisica, Universidad de La Habana, San Lazaro y L, Vedado, 10400 Havana (Cuba); Caleyo, F. [Departamento de Ingenieria, Metalurgica, IPN-ESIQIE, UPALM Edif. 7, Zacatenco, Mexico DF 07738 (Mexico)]. E-mail: fcaleyo@gmail.com; Alfonso, L. [Departamento de Ingenieria, Metalurgica, IPN-ESIQIE, UPALM Edif. 7, Zacatenco, Mexico DF 07738 (Mexico); Rivas, D. [Departamento de Ingenieria, Metalurgica, IPN-ESIQIE, UPALM Edif. 7, Zacatenco, Mexico DF 07738 (Mexico); Hallen, J.M. [Departamento de Ingenieria, Metalurgica, IPN-ESIQIE, UPALM Edif. 7, Zacatenco, Mexico DF 07738 (Mexico)

    2007-02-15

    In this work, a new stochastic model capable of simulating pitting corrosion is developed and validated. Pitting corrosion is modeled as the combination of two stochastic processes: pit initiation and pit growth. Pit generation is modeled as a nonhomogeneous Poisson process, in which induction time for pit initiation is simulated as the realization of a Weibull process. In this way, the exponential and Weibull distributions can be considered as the possible distributions for pit initiation time. Pit growth is simulated using a nonhomogeneous Markov process. Extreme value statistics is used to find the distribution of maximum pit depths resulting from the combination of the initiation and growth processes for multiple pits. The proposed model is validated using several published experiments on pitting corrosion. It is capable of reproducing the experimental observations with higher quality than the stochastic models available in the literature for pitting corrosion.

  11. Corrosion inhibition

    Energy Technology Data Exchange (ETDEWEB)

    Fisher, A O

    1965-12-29

    An acid corrosion-inhibiting composition consists essentially of a sugar, and an alkali metal salt selected from the group consisting of iodides and bromides. The weight ratio of the sugar to the alkali metal salt is between 2:1 and about 20,000:1. Also, a corrosion- inhibited phosphoric acid composition comprising at least about 20 wt% of phosphoric acid and between about 0.1 wt% and about 10 wt% of molasses, and between about 0.0005 wt% and about 1 wt% of potassium iodide. The weight ratio of molasses to iodide is greater than about 2:1. (11 claims)

  12. Pitting corrosion on a copper canister

    International Nuclear Information System (INIS)

    Hermansson, H.P.; Beverskog, B.

    1996-02-01

    It is demonstrated that normal pitting can occur during oxidizing conditions in the repository. It is also concluded that a new theory for pitting corrosion has to be developed, as the present theory is not in accordance with all practical and experimental observations. A special variant of pitting, based on the growth of sulfide whiskers, is suggested to occur during reducing conditions. However, such a mechanism needs to be demonstrated experimentally. A simple calculational model of canister corrosion was developed based on the results of this study. 69 refs, 3 figs

  13. Pitting corrosion of copper. Further model studies

    International Nuclear Information System (INIS)

    Taxen, C.

    2002-08-01

    The work presented in this report is a continuation and expansion of a previous study. The aim of the work is to provide background information about pitting corrosion of copper for a safety analysis of copper canisters for final deposition of radioactive waste. A mathematical model for the propagation of corrosion pits is used to estimate the conditions required for stationary propagation of a localised anodic corrosion process. The model uses equilibrium data for copper and its corrosion products and parameters for the aqueous mass transport of dissolved species. In the present work we have, in the model, used a more extensive set of aqueous and solid compounds and equilibrium data from a different source. The potential dependence of pitting in waters with different compositions is studied in greater detail. More waters have been studied and single parameter variations in the composition of the water have been studied over wider ranges of concentration. The conclusions drawn in the previous study are not contradicted by the present results. However, the combined effect of potential and water composition on the possibility of pitting corrosion is more complex than was realised. In the previous study we found what seemed to be a continuous aggravation of a pitting situation by increasing potentials. The present results indicate that pitting corrosion can take place only over a certain potential range and that there is an upper potential limit for pitting as well as a lower. A sensitivity analysis indicates that the model gives meaningful predictions of the minimum pitting potential also when relatively large errors in the input parameters are allowed for

  14. COPPER PITTING CORROSION: A CASE STUDY

    Science.gov (United States)

    Localized or pitting corrosion of copper pipes used in household drinking-water plumbing is a problem for many water utilities and their customers. Extreme attack can lead to pinhole water leaks that may result in water damage, mold growth, and costly repairs. Water quality has b...

  15. Ultrasonic monitoring of pitting corrosion

    Science.gov (United States)

    Jarvis, A. J. C.; Cegla, F. B.; Bazaz, H.; Lozev, M.

    2013-01-01

    Exposure to corrosive substances in high temperature environments can cause damage accumulation in structural steels, particularly in the chemical and petrochemical industries. The interaction mechanisms are complex and varied; however initial damage propagation often manifests itself in the form of localized areas of increased material loss. Recent development of an ultrasonic wall thickness monitoring sensor capable of withstanding temperatures in excess of 500°C has allowed permanent monitoring within such hostile environments, providing information on how the shape of a pulse which has reflected from a corroding surface can change over time. Reconstructing localized corrosion depth and position may be possible by tracking such changes in reflected pulse shape, providing extra information on the state of the backwall and whether process conditions should be altered to increase plant life. This paper aims to experimentally investigate the effect certain localized features have on reflected pulse shape by `growing' artificial defects into the backwall while wall thickness is monitored using the sensor. The size and complexity of the three dimensional scattering problem lead to the development of a semi-analytical simulation based on the distributed point source method (DPSM) which is capable of simulating pulse reflection from complex surfaces measuring approximately 17×10λ Comparison to experimental results show that amplitude changes are predicted to within approximately 1dB and that pulse shape changes are accurately modelled. All experiments were carried out at room temperature, measurements at high temperature will be studied in the future.

  16. Pitting corrosion resistant austenite stainless steel

    Science.gov (United States)

    van Rooyen, D.; Bandy, R.

    A pitting corrosion resistant austenite stainless steel comprises 17 to 28 wt. % chromium, 15 to 26 wt. % nickel, 5 to 8 wt. % molybdenum, and 0.3 to 0.5 wt. % nitrogen, the balance being iron, unavoidable impurities, minor additions made in the normal course of melting and casting alloys of this type, and may optionally include up to 10 wt. % of manganese, up to 5 wt. % of silicon, and up to 0.08 wt. % of carbon.

  17. Markov Chain Models for the Stochastic Modeling of Pitting Corrosion

    OpenAIRE

    Valor, A.; Caleyo, F.; Alfonso, L.; Velázquez, J. C.; Hallen, J. M.

    2013-01-01

    The stochastic nature of pitting corrosion of metallic structures has been widely recognized. It is assumed that this kind of deterioration retains no memory of the past, so only the current state of the damage influences its future development. This characteristic allows pitting corrosion to be categorized as a Markov process. In this paper, two different models of pitting corrosion, developed using Markov chains, are presented. Firstly, a continuous-time, nonhomogeneous linear growth (pure ...

  18. Influence of Pitting Corrosion on Fatigue and Corrosion Fatigue of Ship and Offshore Structures, Part II: Load - Pit - Crack Interaction

    Directory of Open Access Journals (Sweden)

    Jakubowski Marek

    2015-09-01

    Full Text Available In the paper has been discussed influence of stresses on general corrosion rate and corrosion pit nucleation rate and growth , whose presence has been questioned by some authors but accepted by most of them. Influence of roughness of pit walls on fatigue life of a plate suffering pit corrosion and presence of the so called „ non-damaging” pits which never lead to initiation of fatigue crack, has been presented. Possibility of prediction of pit-to-crack transition moment by two different ways, i.e. considering a pit a stress concentrator or an equivalent crack, has been analyzed. Also, influence of statistical distribution of depth of corrosion pits as well as anticorrosion protection on fatigue and corrosion fatigue has been described.

  19. Research process of nondestructive testing pitting corrosion in metal material

    Directory of Open Access Journals (Sweden)

    Bo ZHANG

    2017-12-01

    Full Text Available Pitting corrosion directly affects the usability and service life of metal material, so the effective nondestructive testing and evaluation on pitting corrosion is of great significance for fatigue life prediction because of data supporting. The features of pitting corrosion are elaborated, and the relation between the pitting corrosion parameters and fatigue performance is pointed out. Through introducing the fundamental principles of pitting corrosion including mainly magnetic flux leakage inspection, pulsed eddy current and guided waves, the research status of nondestructive testing technology for pitting corrosion is summarized, and the key steps of nondestructive testing technologies are compared and analyzed from the theoretical model, signal processing to industrial applications. Based on the analysis of the signal processing specificity of different nondestructive testing technologies in detecting pitting corrosion, the visualization combined with image processing and signal analysis are indicated as the critical problems of accurate extraction of pitting defect information and quantitative characterization for pitting corrosion. The study on non-contact nondestructive testing technologies is important for improving the detection precision and its application in industries.

  20. Pitting corrosion as a mixed system: coupled deterministic-probabilistic simulation of pit growth

    Science.gov (United States)

    Ibrahim, Israr B. M.; Fonna, S.; Pidaparti, R.

    2018-05-01

    Stochastic behavior of pitting corrosion poses a unique challenge in its computational analysis. However, it also stems from electrochemical activity causing general corrosion. In this paper, a framework for corrosion pit growth simulation based on the coupling of the Cellular Automaton (CA) and Boundary Element Methods (BEM) is presented. The framework assumes that pitting corrosion is controlled by electrochemical activity inside the pit cavity. The BEM provides the prediction of electrochemical activity given the geometrical data and polarization curves, while the CA is used to simulate the evolution of pit shapes based on electrochemical activity provided by BEM. To demonstrate the methodology, a sample case of local corrosion cells formed in pitting corrosion with varied dimensions and polarization functions is considered. Results show certain shapes tend to grow in certain types of environments. Some pit shapes appear to pose a higher risk by being potentially significant stress raisers or potentially increasing the rate of corrosion under the surface. Furthermore, these pits are comparable to commonly observed pit shapes in general corrosion environments.

  1. Markov Chain Models for the Stochastic Modeling of Pitting Corrosion

    Directory of Open Access Journals (Sweden)

    A. Valor

    2013-01-01

    Full Text Available The stochastic nature of pitting corrosion of metallic structures has been widely recognized. It is assumed that this kind of deterioration retains no memory of the past, so only the current state of the damage influences its future development. This characteristic allows pitting corrosion to be categorized as a Markov process. In this paper, two different models of pitting corrosion, developed using Markov chains, are presented. Firstly, a continuous-time, nonhomogeneous linear growth (pure birth Markov process is used to model external pitting corrosion in underground pipelines. A closed-form solution of the system of Kolmogorov's forward equations is used to describe the transition probability function in a discrete pit depth space. The transition probability function is identified by correlating the stochastic pit depth mean with the empirical deterministic mean. In the second model, the distribution of maximum pit depths in a pitting experiment is successfully modeled after the combination of two stochastic processes: pit initiation and pit growth. Pit generation is modeled as a nonhomogeneous Poisson process, in which induction time is simulated as the realization of a Weibull process. Pit growth is simulated using a nonhomogeneous Markov process. An analytical solution of Kolmogorov's system of equations is also found for the transition probabilities from the first Markov state. Extreme value statistics is employed to find the distribution of maximum pit depths.

  2. Statistical characterization of pitting corrosion process and life prediction

    International Nuclear Information System (INIS)

    Sheikh, A.K.; Younas, M.

    1995-01-01

    In order to prevent corrosion failures of machines and structures, it is desirable to know in advance when the corrosion damage will take place, and appropriate measures are needed to mitigate the damage. The corrosion predictions are needed both at development as well as operational stage of machines and structures. There are several forms of corrosion process through which varying degrees of damage can occur. Under certain conditions these corrosion processes at alone and in other set of conditions, several of these processes may occur simultaneously. For a certain type of machine elements and structures, such as gears, bearing, tubes, pipelines, containers, storage tanks etc., are particularly prone to pitting corrosion which is an insidious form of corrosion. The corrosion predictions are usually based on experimental results obtained from test coupons and/or field experiences of similar machines or parts of a structure. Considerable scatter is observed in corrosion processes. The probabilities nature and kinetics of pitting process makes in necessary to use statistical method to forecast the residual life of machine of structures. The focus of this paper is to characterization pitting as a time-dependent random process, and using this characterization the prediction of life to reach a critical level of pitting damage can be made. Using several data sets from literature on pitting corrosion, the extreme value modeling of pitting corrosion process, the evolution of the extreme value distribution in time, and their relationship to the reliability of machines and structure are explained. (author)

  3. PITTING CORROSION OF STAINLESS STEEL AT THE VARIOUS SURFACE TREATMENT

    Directory of Open Access Journals (Sweden)

    Viera Zatkalíková

    2011-09-01

    Full Text Available The stainless steel surface treatment is very important with regard to its pitting corrosion susceptibility. An effect of various types surfacing on pitting corrosion resistance of AISI 304stainless steel is investigated in this work. The samples of the tested material are turned, blasted, peened, grinded and a half of them are pickled to achieve higher purity of surfaces and better quality of passive film. Eight types of different finished surfaces are tested by electrochemical and immersion tests to determine corrosion behaviour in conditions where pitting is evoked by controlled potential and second by solution with high redox potential. By this way the effect of mechanical and chemical surface treatment on the resistance to pitting corrosion, character, size and shape of pits are compared in the conditions of different mechanisms of corrosion process.

  4. Markov chain modelling of pitting corrosion in underground pipelines

    Energy Technology Data Exchange (ETDEWEB)

    Caleyo, F. [Departamento de Ingenieri' a Metalurgica, ESIQIE, IPN, UPALM Edif. 7, Zacatenco, Mexico D. F. 07738 (Mexico)], E-mail: fcaleyo@gmail.com; Velazquez, J.C. [Departamento de Ingenieri' a Metalurgica, ESIQIE, IPN, UPALM Edif. 7, Zacatenco, Mexico D. F. 07738 (Mexico); Valor, A. [Facultad de Fisica, Universidad de La Habana, San Lazaro y L, Vedado, 10400 La Habana (Cuba); Hallen, J.M. [Departamento de Ingenieri' a Metalurgica, ESIQIE, IPN, UPALM Edif. 7, Zacatenco, Mexico D. F. 07738 (Mexico)

    2009-09-15

    A continuous-time, non-homogenous linear growth (pure birth) Markov process has been used to model external pitting corrosion in underground pipelines. The closed form solution of Kolmogorov's forward equations for this type of Markov process is used to describe the transition probability function in a discrete pit depth space. The identification of the transition probability function can be achieved by correlating the stochastic pit depth mean with the deterministic mean obtained experimentally. Monte-Carlo simulations previously reported have been used to predict the time evolution of the mean value of the pit depth distribution for different soil textural classes. The simulated distributions have been used to create an empirical Markov chain-based stochastic model for predicting the evolution of pitting corrosion depth and rate distributions from the observed properties of the soil. The proposed model has also been applied to pitting corrosion data from pipeline repeated in-line inspections and laboratory immersion experiments.

  5. Markov chain modelling of pitting corrosion in underground pipelines

    International Nuclear Information System (INIS)

    Caleyo, F.; Velazquez, J.C.; Valor, A.; Hallen, J.M.

    2009-01-01

    A continuous-time, non-homogenous linear growth (pure birth) Markov process has been used to model external pitting corrosion in underground pipelines. The closed form solution of Kolmogorov's forward equations for this type of Markov process is used to describe the transition probability function in a discrete pit depth space. The identification of the transition probability function can be achieved by correlating the stochastic pit depth mean with the deterministic mean obtained experimentally. Monte-Carlo simulations previously reported have been used to predict the time evolution of the mean value of the pit depth distribution for different soil textural classes. The simulated distributions have been used to create an empirical Markov chain-based stochastic model for predicting the evolution of pitting corrosion depth and rate distributions from the observed properties of the soil. The proposed model has also been applied to pitting corrosion data from pipeline repeated in-line inspections and laboratory immersion experiments.

  6. Pitting by corrosion in aluminium and Al-6201 alloy

    International Nuclear Information System (INIS)

    Vera, R.; Schrebler, R.; Layana, G.; Orellana, F.; Olguin, A.

    1998-01-01

    The susceptibility of pure aluminum 6201 alloy to pitting was investigated in sodium chloride solutions through determination of the corrosion, repassivation and pitting potentials. Potentiodynamic polarization including scratching techniques were employed being also determined the type and relative amount of corrosion damage to the metals. The morphology of the attach was determined using scanning electrons microscopy (SEM). The results showed a similar performance for aluminum 6201 alloy and aluminum. It was also observed that an increase in chloride concentration resulted in a decrease in the corrosion, pitting and repassivation potentials of both materials. (Author) 19 refs

  7. Pitting corrosion of copper. An equilibrium - mass transport study

    International Nuclear Information System (INIS)

    Taxen, C.

    2002-08-01

    A mathematical model for the propagation of corrosion pits is described and used to calculate the potentials below which copper is immune to pitting. The model uses equilibrium data and diffusion coefficients and calculates the stationary concentration profiles of 26 aqueous species from the bulk water outside a corrosion pit to the site of the metal dissolution. Precipitation of oxides and salts of copper is considered. Studied conditions include water compositions from tap waters to seawater at the temperatures 25 deg C and 75 deg C. Carbonate and sulphate are aggressive towards copper because of complex formation with divalent copper. Carbonate is less aggressive in a corrosion pit than outside at the pH of the bulk. Carbonate carries acidity out from the pit, favours oxide formation and may prevent the initiation of acidic corrosion pits. The concentration profiles are used to estimate the maximum propagation rates for a corrosion pit. A high potential is found to be the most important factor for the rate of propagation. The levels of potential copper can sustain, as corrosion potentials are discussed in terms of the stability of cuprous oxide as a cathode material for oxygen reduction relative to non-conducting cupric phases

  8. Pitting corrosion of copper. An equilibrium - mass transport study

    Energy Technology Data Exchange (ETDEWEB)

    Taxen, C. [Swedish Corrosion Inst., Stockholm (Sweden)

    2002-08-01

    A mathematical model for the propagation of corrosion pits is described and used to calculate the potentials below which copper is immune to pitting. The model uses equilibrium data and diffusion coefficients and calculates the stationary concentration profiles of 26 aqueous species from the bulk water outside a corrosion pit to the site of the metal dissolution. Precipitation of oxides and salts of copper is considered. Studied conditions include water compositions from tap waters to seawater at the temperatures 25 deg C and 75 deg C. Carbonate and sulphate are aggressive towards copper because of complex formation with divalent copper. Carbonate is less aggressive in a corrosion pit than outside at the pH of the bulk. Carbonate carries acidity out from the pit, favours oxide formation and may prevent the initiation of acidic corrosion pits. The concentration profiles are used to estimate the maximum propagation rates for a corrosion pit. A high potential is found to be the most important factor for the rate of propagation. The levels of potential copper can sustain, as corrosion potentials are discussed in terms of the stability of cuprous oxide as a cathode material for oxygen reduction relative to non-conducting cupric phases.

  9. Inhibition of aluminum corrosion using Opuntia extract

    International Nuclear Information System (INIS)

    El-Etre, A.Y.

    2003-01-01

    The inhibitive action of the mucilage extracted from the modified stems of prickly pears, toward acid corrosion of aluminum, is tested using weight loss, thermometry, hydrogen evolution and polarization techniques. It was found that the extract acts as a good corrosion inhibitor for aluminum corrosion in 2.0 M HCl solution. The inhibition action of the extract was discussed in view of Langmuir adsorption isotherm. It was found that the adsorption of the extract on aluminum surface is a spontaneous process. The inhibition efficiency (IE) increases as the extract concentration is increased. The effect of temperature on the IE was studied. It was found that the presence of extract increases the activation energy of the corrosion reaction. Moreover, the thermodynamic parameters of the adsorption process were calculated. It was found also that the Opuntia extract provides a good protection to aluminum against pitting corrosion in chloride ion containing solutions

  10. Improving pitting corrosion resistance of aluminum by anodizing process

    International Nuclear Information System (INIS)

    John, P.; Khan, I.U.

    2013-01-01

    Summary: Anodizing of aluminum was studied in sulphuric/citric/boric acid electrolyte system to improve pitting corrosion resistance. Maximum oxide film thickness was obtained using 5% sulphuric acid, 3% citric acid and 0.5% boric acid electrolyte composition. The corrosion resistance of aluminum sample was determined to find the effectiveness of oxide coating by potentiodynamic polarization test. The surface morphology of aluminum samples was investigated using scanning electron microscope (SEM) before and after corrosion test. It was found that the coated aluminum sample obtained by anodizing in sulphuric/citric/boric acid electrolyte system exhibited better pitting corrosion resistance with no significant difference in surface morphology. (author)

  11. Pitting corrosion of copper. An equilibrium - mass transport study

    Energy Technology Data Exchange (ETDEWEB)

    Taxen, C

    1996-11-01

    A mathematical model for the propagation of corrosion pits on copper is described. The model is used to predict the potentials below which copper is immune to pitting. The criteria used for immunity against pitting is that the volume of the cuprous oxide formed at the site of the metal oxidation at the bottom of a corrosion pit must be smaller than the volume of the oxidised metal. Equal volumes would give a complete coverage of the metal in a pit by adherent cuprous oxide and propagation would not be possible. For potentials where copper is not immune to pitting an estimate of the maximum growth rate is given. The model uses equilibrium data and diffusion coefficients and calculates the stationary concentration profiles from the bulk water outside a corrosion pit to the site of the metal dissolution at the bottom a corrosion pit. Precipitation of oxides as well as of basic salts of copper is considered. A total of 26 aqueous species are considered in waters with compositions ranging from those of tap waters to that of sea water. Calculations are made for the temperatures 25 deg C and 75 deg C. 38 refs, 60 figs, 17 tabs

  12. Pitting Corrosion Topography Characteristics and Evolution Laws of LC4 Aluminum Alloy in Service Environment

    Directory of Open Access Journals (Sweden)

    LIU Zhiguo

    2017-08-01

    Full Text Available Aircraft aluminum alloy is easy to initiate pitting corrosion in the service environment, the pitting corrosion topography characteristics could directly affect the fatigue mechanical property of structure material. In order to obtain the pitting corrosion topography characteristics of LC4 aluminum alloy in the service environment, the accelerated corrosion test was carried out along the accelerated corrosion test environment spectrum which imitated the service environment spectrum, and the corrosion topography characteristic parameters of corrosion pit depth H,corrosion pit surface length L and corrosion pit surface width W were defined respectively. During the corrosion test process,the three parameters of typical corrosion pit were successively measured in different equivalent corrosion years for obtaining the corrosion pit damage size data, then the data were analysed through the statistics method and fractal theory. Further more in order to gain the pit topography characteristics in the same equivalent corrosion year and the topography evolution laws during different equivalent corrosion years were gained. The analysis results indicate that LC4 aluminum alloy corrosion pit topography characteristics in the service environment include the following:firstly, the pit topography characteristic parameters conform to the lognormal distributions in the same equivalent corrosion years; secondly,the pit topography characteristic parameters gradually reflect the fractal feature in accordance with the equivalent corrosion year increment, and the pits tend to be shallow, long and moderate wide topography character.

  13. Influence of remanent magnetization on pitting corrosion in pipeline steel

    Energy Technology Data Exchange (ETDEWEB)

    Espina-Hernandez, J. H. [ESIME Zacatenco, SEPI Electronica Instituto Politecnico Nacional Mexico, D. F. (Mexico); Caleyo, F.; Hallen, J. M. [DIM-ESIQIE, Instituto Politecnico Nacional Mexico D. F. (Mexico); Lopez-Montenegro, A.; Perez-Baruch, E. [Pemex Exploracion y Produccion, Region Sur Villahermosa, Tabasco (Mexico)

    2010-07-01

    Statistical studies performed in Mexico indicate that leakage due to external pitting corrosion is the most likely cause of failure of buried pipelines. When pipelines are inspected with the magnetic flux leakage (MFL) technology, which is routinely used, the magnetization level of every part of the pipeline changes as the MFL tool travels through it. Remanent magnetization stays in the pipeline wall after inspection, at levels that may differ from a point to the next. This paper studies the influence of the magnetic field on pitting corrosion. Experiments were carried out on grade 52 steel under a level of remanent magnetization and other laboratory conditions that imitated the conditions of a pipeline after an MLF inspection. Non-magnetized control samples and magnetized samples were subjected to pitting by immersion in a solution containing chlorine and sulfide ions for seven days, and then inspected with optical microscopy. Results show that the magnetic field in the pipeline wall significantly increases pitting corrosion.

  14. Effect of microcrystallization on pitting corrosion of pure aluminium

    International Nuclear Information System (INIS)

    Meng Guozhe; Wei Liyan; Zhang Tao; Shao Yawei; Wang Fuhui; Dong Chaofang; Li Xiaogang

    2009-01-01

    A microcrystalline aluminium film with grain size of about 400 nm was prepared by magnetron sputtering technique. Its corrosion behaviour was investigated in NaCl containing acidic solution by means of potentiodynamic polarization curves and electrochemical noise (EN). The polarization results indicated that the corrosion potential of the sample shifted towards more positive direction, while its corrosion current density decreased compared with that of pure coarse-grain Al. The EN analysis based on stochastic model demonstrated that there existed two kinds of effect of microcrystallization on the pitting behaviour of pure aluminium: (1) the rate of pit initiation is accelerated, (2) the pit growth process was impeded. This leads to the enhancement of pitting resistance for the microcrystallized aluminium.

  15. Plastics for corrosion inhibition

    CERN Document Server

    Goldade, Victor A; Makarevich, Anna V; Kestelman, Vladimir N

    2005-01-01

    The development of polymer composites containing inhibitors of metal corrosion is an important endeavour in modern materials science and technology. Corrosion inhibitors can be located in a polymer matrix in the solid, liquid or gaseous phase. This book details the thermodynamic principles for selecting these components, their compatibility and their effectiveness. The various mechanisms of metal protection – barrier, inhibiting and electromechanical – are considered, as are the conflicting requirements placed on the structure of the combined material. Two main classes of inhibited materials (structural and films/coatings) are described in detail. Examples are given of structural plastics used in friction units subjected to mechano-chemical wear and of polymer films/coatings for protecting metal objects against corrosion.

  16. Corrosion pit depth extreme value prediction from limited inspection data

    International Nuclear Information System (INIS)

    Najjar, D.; Bigerelle, M.; Iost, A.; Bourdeau, L.; Guillou, D.

    2004-01-01

    Passive alloys like stainless steels are prone to localized corrosion in chlorides containing environments. The greater the depth of the localized corrosion phenomenon, the more dramatic the related damage that can lead to a structure weakening by fast perforation. In practical situations, because measurements are time consuming and expensive, the challenge is usually to predict the maximum pit depth that could be found in a large scale installation from the processing of a limited inspection data. As far as the parent distribution of pit depths is assumed to be of exponential type, the most successful method was found in the application of the statistical extreme-value analysis developed by Gumbel. This study aims to present a new and alternative methodology to the Gumbel approach with a view towards accurately estimating the maximum pit depth observed on a ferritic stainless steel AISI 409 subjected to an accelerated corrosion test (ECC1) used in automotive industry. This methodology consists in characterising and modelling both the morphology of pits and the statistical distribution of their depths from a limited inspection dataset. The heart of the data processing is based on the combination of two recent statistical methods that avoid making any choice about the type of the theoretical underlying parent distribution of pit depths: the Generalized Lambda Distribution (GLD) is used to model the distribution of pit depths and the Bootstrap technique to determine a confidence interval on the maximum pit depth. (authors)

  17. Stochastic models for predicting pitting corrosion damage of HLRW containers

    International Nuclear Information System (INIS)

    Henshall, G.A.

    1991-10-01

    Stochastic models for predicting aqueous pitting corrosion damage of high-level radioactive-waste containers are described. These models could be used to predict the time required for the first pit to penetrate a container and the increase in the number of breaches at later times, both of which would be useful in the repository system performance analysis. Monte Carlo implementations of the stochastic models are described, and predictions of induction time, survival probability and pit depth distributions are presented. These results suggest that the pit nucleation probability decreases with exposure time and that pit growth may be a stochastic process. The advantages and disadvantages of the stochastic approach, methods for modeling the effects of environment, and plans for future work are discussed

  18. THE IMPACT OF PHOSPHATE ON COPPER PITTING CORROSION

    Science.gov (United States)

    Pinhole leaks caused by extensive localized or pitting corrosion of copper pipes is a problem for many homeowners. Pinhole water leaks may result in water damage, mold growth, and costly repairs. A large water system in Florida has been addressing a widespread pinhole leak proble...

  19. COPPER PITTING CORROSION AND PINHOLE LEAKS: A CASE STUDY

    Science.gov (United States)

    Localized corrosion, or "pitting", of copper drinking water pipe continues is a problem for many water utilities and their customers. Extreme attack leads to pinhole leaks that can potentially lead to water damage, mold growth, and costly repairs for the homeowners, as well as th...

  20. Electrochemical tests for pitting and crevice corrosion susceptibility

    International Nuclear Information System (INIS)

    Postlethwaite, J.

    1983-01-01

    Passive metals are being considered as container materials for the disposal of nuclear waste by deep burial. Localized corrosion is a potential problem and electrochemical techniques have an important role in the assessment of the susceptibility of these container materials to crevice and pitting corrosion. This paper critically reviews both the theoretical background and the experimental details of the electrochemical test methods presently used in both industrial and scientific studies of localized corrosion in both halide and non-halide solutions and identifies those areas where theory and experimental behaviour are in agreement and those areas for which there is neither well established theory nor an experimental test method

  1. The use of different techniques for determination of pitting corrosion potential of austenitic stainless steel

    International Nuclear Information System (INIS)

    Eskelinen, P.; Forsen, O.; Onnela, J.; Ylaesaari, S.; Haenninen, H.

    1992-01-01

    Three different techniques for pitting corrosion potential measurement on austenitic stainless steel (Fe18Cr10Ni) were compared: conventional polarization method, a new Avesta electrochemical corrosion measurement cell and a scratch technique. Special attention was paid to the effects of crevice corrosion during pitting corrosion potential measurement and to their elimination. Development of a rapid test technique for reliable pitting corrosion potential determination was aimed at and resulted from comparison of the different techniques

  2. Influence of increasing phosphate/silikate contents on the pitting and general corrosion of galvanized steel tubing and the corrosion of copper in warm water mixed installation systems

    International Nuclear Information System (INIS)

    Ehreke, J.; Stichel, W.

    1989-01-01

    In hot tap water (65 0 C) the influence of a mixture of phosphate/silicate inhibitor on the general, the pitting and the galvanic corrosion of galvanized steel tubes and the general corrosion of copper in mixed installations of both metals was investigated. Increasing concentration of inhibitors descreases the general corrosion rate of galvanized steel and copper. A worth mentioning reduction of pitting and galvanic corrosion of steel could be reached only with high concentrations of 5 mg/l P 2 O 5 and 30 mg/l SiO 2 . Galvannealed tubes are much more sensitive to pitting corrosion than galvanized ones. Referring to this they could not be inhibited. (orig.) [de

  3. Pitting and stress corrosion cracking of stainless steel

    Science.gov (United States)

    Saithala, Janardhan R.

    An investigation has been performed to determine the pitting resistance of stainless steels and stress corrosion cracking of super duplex stainless steels in water containing chloride ions from 25 - 170°C. The steels studied are 12% Cr, FV520B, FV566, 304L, Uranus65, 2205, Ferallium Alloy 255, and Zeron 100. All these commercial materials used in very significant industrial applications and suffer from pitting and stress corrosion failures. The design of a new experimental setup using an autoclave enabled potentiodynamic polarisation experiments and slow strain rate tests in dilute environments to be conducted at elevated temperatures. The corrosion potentials were controlled using a three electrode cell with computer controlled potentiostat.The experimental programme to determine pitting potentials was designed to simulate the service conditions experienced in most industrial plants and develop mathematical model equations to help a design engineer in material selection decision. Stress corrosion resistance of recently developed Zeron100 was evaluated in dilute environments to propose a mechanism in chloride solutions at high' temperatures useful for the nuclear and power generation industry. Results have shown the significance of the composition of alloying elements across a wide range of stainless steels and its influence on pitting. Nitrogen and molybdenum added to modern duplex stainless steels was found to be unstable at higher temperatures. The fractographic results obtained using the scanning electron microscope (SEM) has given insight in the initiation of pitting in modem duplex and super duplex stainless steels. A mathematical model has been proposed to predict pitting in stainless steels based on the effect of environmental factors (temperature, chloride concentration, and chemical composition). An attempt has been made to identify the mechanism of SCC in Zeron100 super duplex stainless steel.The proposed empirical models have shown good correlation

  4. Numerical Investigation on Stress Concentration of Tension Steel Bars with One or Two Corrosion Pits

    Directory of Open Access Journals (Sweden)

    Jian Hou

    2015-01-01

    Full Text Available Pitting corrosion has been observed in steel bars of existing reinforced concrete (RC structures in different erosion environments and has been identified as a potential origin for fatigue crack nucleation. In the present study, under uniaxial tension loading, stress distribution in the steel bars with one or two semiellipsoidal corrosion pits has systematically been investigated by conducting a series of three-dimensional semiellipsoidal pitted models. Based on the finite element analyses, it is shown that stress concentration factor (SCF increases linearly with increasing pit aspect ratio (a/b and increases nonlinearly with increasing pit relative depth (a/R for single corrosion pit problem. For double corrosion pits problem, the SCF decreases nonlinearly with increasing angle of two transverse pits (θ. The interaction of two longitudinal pits can be ignored in the calculation of SCF even if the distance of two pits (d is very small.

  5. Fokker-Planck modeling of pitting corrosion in underground pipelines

    Energy Technology Data Exchange (ETDEWEB)

    Camacho, Eliana Nogueira [Risco Ambiental Engenharia, Rio de Janeiro, RJ (Brazil); Melo, Paulo F. Frutuoso e [Coordenacao dos Programas de Pos-Graduacao de Engenharia (COPPE/UFRJ), Rio de Janeiro, RJ (Brazil). Programa de Engenharia Nuclear; Saldanha, Pedro Luiz C. [Comissao Nacional de Energia Nuclear (CGRC/CNEN), Rio de Janeiro, RJ (Brazil). Coordenacao Geral de Reatores e Ciclo do Combustivel; Silva, Edson de Pinho da [Universidade Federal Rural do Rio de Janeiro (UFRRJ), Seropedica, RJ (Brazil). Dept. of Physics

    2011-07-01

    Full text: The stochastic nature of pitting corrosion has been recognized since the 1930s. It has been learned that this damage retains no memory of its past. Instead, the future state is determined only by the knowledge of its present state. This Markovian property that underlies the stochastic process governing pitting corrosion has been explored as a discrete Markovian process by many authors since the beginning of the 1990s for underground pipelines of the oil and gas industries and nuclear power plants. Corrosion is a genuine continuous time and space state Markovian process, so to model it as a discrete time and/or state space is an approximation to the problem. Markovian chains approaches, with an increasing number of states, could involve a large number of parameters, the transition rates between states, to be experimentally determined. Besides, such an increase in the number of states produces matrices with huge dimensions leading to time-consuming computational solutions. Recent approaches involving Markovian discrete process have overcome those difficulties but, on the other hand, a large number of soil and pipe stochastic variables have to be known. In this work we propose a continuous time and space state approach to the evolution of pit corrosion depths in underground pipelines. In order to illustrate the application of the model for defect depth growth a combination of real life data and Monte Carlo simulation was used. The process is described by a Fokker-Planck equation. The Fokker-Planck equation is completely determined by the knowledge of two functions known as the drift and diffusion coefficients. In this work we also show that those functions can be estimated from corrosion depth data from in-line inspections. Some particular forms of drift and diffusion coefficients lead to particular Fokker-Planck equations for which analytical solutions are known, as is the case for the Wiener process, the Ornstein-Uhlenbeck process and the Brownian motion

  6. Markov chain model helps predict pitting corrosion depth and rate in underground pipelines

    Energy Technology Data Exchange (ETDEWEB)

    Caleyo, F.; Velazquez, J.C.; Hallen, J. M. [ESIQIE, Instituto Politecnico Nacional, Mexico D. F. (Mexico); Esquivel-Amezcua, A. [PEMEX PEP Region Sur, Villahermosa, Tabasco (Mexico); Valor, A. [Universidad de la Habana, Vedado, La Habana (Cuba)

    2010-07-01

    Recent reports place pipeline corrosion costs in North America at seven billion dollars per year. Pitting corrosion causes the higher percentage of failures among other corrosion mechanisms. This has motivated multiple modelling studies to be focused on corrosion pitting of underground pipelines. In this study, a continuous-time, non-homogenous pure birth Markov chain serves to model external pitting corrosion in buried pipelines. The analytical solution of Kolmogorov's forward equations for this type of Markov process gives the transition probability function in a discrete space of pit depths. The transition probability function can be completely identified by making a correlation between the stochastic pit depth mean and the deterministic mean obtained experimentally. The model proposed in this study can be applied to pitting corrosion data from repeated in-line pipeline inspections. Case studies presented in this work show how pipeline inspection and maintenance planning can be improved by using the proposed Markovian model for pitting corrosion.

  7. The resistance of titanium to pitting, microbially induced corrosion and corrosion in unsaturated conditions

    Energy Technology Data Exchange (ETDEWEB)

    Shoesmith, D W; Ikeda, B M

    1997-04-01

    Titanium and its alloys (Grades-2, -12, -16) are candidate materials for Canadian nuclear waste containers on the basis of their apparent immunity to many localized corrosion processes. This simplifies markedly the effort needed to justify the use of these materials and to develop models to predict the lifetimes of containers. Here we review the pitting, microbially influenced corrosion (MIC), and corrosion under unsaturated conditions, of titanium. For all these processes, the properties of the passive oxide film are paramount in determining the metal`s resistance to corrosion. A review of these oxide properties is included and the conditions to which the metal must be exposed if localized corrosion is to occur are defined. Since these conditions cannot be achieved under Canadian waste vault conditions, it can be concluded that pitting and MIC will not occur and that corrosion under unsaturated conditions is extremely unlikely. (author) 114 refs., 1 tab., 18 figs.

  8. The resistance of titanium to pitting, microbially induced corrosion and corrosion in unsaturated conditions

    International Nuclear Information System (INIS)

    Shoesmith, D.W.; Ikeda, B.M.

    1997-04-01

    Titanium and its alloys (Grades-2, -12, -16) are candidate materials for Canadian nuclear waste containers on the basis of their apparent immunity to many localized corrosion processes. This simplifies markedly the effort needed to justify the use of these materials and to develop models to predict the lifetimes of containers. Here we review the pitting, microbially influenced corrosion (MIC), and corrosion under unsaturated conditions, of titanium. For all these processes, the properties of the passive oxide film are paramount in determining the metal's resistance to corrosion. A review of these oxide properties is included and the conditions to which the metal must be exposed if localized corrosion is to occur are defined. Since these conditions cannot be achieved under Canadian waste vault conditions, it can be concluded that pitting and MIC will not occur and that corrosion under unsaturated conditions is extremely unlikely. (author)

  9. Mechanism of Pitting Corrosion Prevention by Nitrite in Carbon Steel Exposed to Dilute Salt Solutions

    International Nuclear Information System (INIS)

    Zapp, Philip E.; Zee, John W. van

    2002-01-01

    The research has developed a broad fundamental understanding of the inhibition action of nitrite ions in preventing nitrate pitting corrosion of carbon steel tanks containing high-level radioactive waste. This fundamental understanding can be applied to specific situations during waste removal for permanent disposition and waste tank closure to ensure that the tanks are maintained safely. The results of the research provide the insight necessary to develop solutions that prevent further degradation

  10. Dependence of Crystallographic Orientation on Pitting Corrosion Behavior of Ni-Fe-Cr Alloy 028

    Science.gov (United States)

    Zhang, LiNa; Szpunar, Jerzy A.; Dong, JianXin; Ojo, Olanrewaju A.; Wang, Xu

    2018-03-01

    The influence of crystallographic orientation on the pitting corrosion behavior of Ni-Fe-Cr alloy 028 was studied using a combination of X-ray diffraction (XRD), electron backscatter diffraction (EBSD), potentiodynamic polarization technique, and atomic force microscopy (AFM). The results show that there is anisotropy of pitting corrosion that strongly depends on crystallographic orientation of the surface plane. The distribution of pit density in a standard stereographic triangle indicates that the crystallographic planes close to {100} are more prone to pitting corrosion compared to planes {110} and {111}. The surface energy calculation of (001) and (111) shows that the plane with a high atomic packing density has a low surface energy with concomitant strong resistance to pitting corrosion. A correlation function between crystallographic orientation and pitting corrosion susceptibility suggests a method that not only predicts the pitting resistance of known textured materials, but also could help to improve corrosion resistance by controlling material texture.

  11. Pitting Corrosion Susceptibility of AISI 301 Stainless Steel in ...

    African Journals Online (AJOL)

    The susceptibility of austenitic (AISI 301) stainless steel to pitting corrosion was evaluated in sodium chloride (NaCl) solutions - 0.1M, 0.2M, 0.3M, 0.5M and 0.7M and 1.0M. Tensile tests and microscopic examinations were performed on samples prepared from the steel after exposure in the various environments.

  12. Detection of simulated pitting corrosion and noises in crude oil storage tank by acoustic emission

    International Nuclear Information System (INIS)

    Shukri Mohd; Latif, N.A.; Azhar Mohd Sinin; Mohamad Daud; Abd Nasir Ibrahim

    2008-01-01

    The damage mechanisms associated with crude oil storage tanks can be complex and varied and include pitting corrosion due to presence of species such as sulphate reducing bacteria. Acoustic Emission (AE) could be used to characterise the pitting corrosion signal in crude oil storage tanks but it is extremely difficult to simulate the pitting corrosion in the laboratory using crude oil as electrolyte because crude oil is considered as non corrosive medium. In this study, induced current have been introduced onto a surface ASTM 516 steel as an electrical source to simulate the electrical noise produced during pitting corrosion process and AE sensor have been used to detect this current. It is found that AE system could detect AE signal release during current induction this current and is expected that if the exact simulation of the current magnitude produced during pitting corrosion process is made available, AE characterisation of pitting corrosion in such tank could be made possible. (Author)

  13. Pitting corrosion of Al and Al-Cu alloys by ClO4- ions in neutral sulphate solutions

    International Nuclear Information System (INIS)

    Amin, Mohammed A.; Abd El Rehim, Sayed S.; Moussa, S.O.; Ellithy, Abdallah S.

    2008-01-01

    The influence of various concentrations of NaClO 4 , as a pitting corrosion agent, on the corrosion behaviour of pure Al, and two Al-Cu alloys, namely (Al + 2.5 wt% Cu) and (Al + 7 wt% Cu) alloys in 1.0 M Na 2 SO 4 solution was investigated by potentiodynamic polarization and potentiostatic techniques at 25 deg. C. Measurements were conducted under the influence of various experimental conditions, complemented by ex situ energy dispersive X-ray (EDX) and scanning electron microscopy (SEM) examinations of the electrode surface. In free perchlorate sulphate solutions, for the three Al samples, the anodic polarization exhibits an active/passive transition. The active dissolution region involves an anodic peak (peak A) which is assigned to the formation of Al 2 O 3 passive film on the electrode surface. The passive region extends up to 1500 mV with almost constant current density (j pass ) without exhibiting a critical breakdown potential or showing any evidence of pitting attack. For the three Al samples, addition of ClO 4 - ions to the sulphate solution stimulates their active anodic dissolution and tends to induce pitting corrosion within the oxide passive region. Pitting corrosion was confirmed by SEM examination of the electrode surface. The pitting potential decreases with increasing ClO 4 - ion concentration indicating a decrease in pitting corrosion resistance. The susceptibility of the three Al samples towards pitting corrosion decreases in the order: Al > (Al + 2.5 wt% Cu) alloy > (Al + 7 wt% Cu) alloy. Potentiostatic measurements showed that the rate of pitting initiation increases with increasing ClO 4 - ion concentration and applied step anodic potential, while it decreases with increasing %Cu in the Al samples. The inhibitive effect of SO 4 2- ions was also discussed

  14. Investigation of the pitting corrosion of low carbon steel containers

    International Nuclear Information System (INIS)

    Mughabghab, S.F.; Sullivan, T.M.

    1988-01-01

    The present study was undertaken because the prediction of the degradation rate of low carbon steel contains over long time frames is one of the crucial elements in the development of a source term model for low-level shallow land burial. The principal data base considered is that of the NBS corrosion measurements of ferrous materials buried in the ground for periods of up to 18 years. In this investigation, the maximum penetration in mils, hm, due to pitting corrosion was found to conform closely to the relation h m = kt n where it is the exposure time of the sample in years, κ is the pitting parameter in mil/(years) n , and n > O is a parameter related to the aeration property of the soil. The central objective of the present investigation is the determination of the dependence of the pitting parameters κ and n on the soil properties. The result of a detailed linear correlation analysis of κ on one hand, the pH value and the resistivity of the soil on the other hand revealed that κ is principally influenced by the pH value of the soil. The resistivity of the soil is found to play a minor role

  15. A mathematical model of crevice and pitting corrosion

    International Nuclear Information System (INIS)

    Sharland, S.M.; Tasker, P.W.

    1985-09-01

    A predictive and self-consistent mathematical model incorporating the electrochemical, chemical and ionic migration processes characterising crevice and pitting corrosion is described. The model predicts full details of the steady-state solution chemistry and electrode kinetics (and hence metal penetration rates) within the corrosion cavities as functions of the many parameters on which these depend such as external electrode potential and crevice dimensions. The crevice is modelled as a parallel-sided slot filled with a dilute sodium chloride solution. Corrosion in both one and two directions is considered. The model includes a solid hydroxide precipitation reaction and assesses the effect on the corrosion rates of consequent changes in the chemical and physical environment within the crevice. A time stepping method is developed for the study of the progression of the corrosion with a precipitation reaction included and is applied to a restricted range of parameters. The applicability of this method is justified in relation to the physical and mathematical approximations made during the construction of the model. (author)

  16. The effect of notches and pits on corrosion fatigue strength

    Science.gov (United States)

    Tatner, Ian

    An investigation has been undertaken to examine the fatigue behaviour of two martensitic steels in air and aggressive environments. The steels studied are, 18% Ni marageing steel and FV520B, the later being a stainless steel turbine blade material and the former being a marageing steel that suffers general corrosion in mild environments. Both steels were heat treated to give similar tensile strength.The design and manufacture of an autoclave allowed push-pull fatigue tests to be conducted in aggressive environments at elevated temperatures.Corrosion potential was monitored using a three electrode cell and was controlled during testing. Base-line fatigue tests were conducted with a range of constant corrosion potentials, using both notched and plain FV520B specimens. In addition fatigue tests with pulsed corrosion potential were performed to asses the effect of transient corrosion conditions on the corrosion fatigue strength. The pulsed tests were designed to simulate service transients in the oxygen content and general chemical hostility in the condensing steam environment during start-up and shut down of the steam turbine.Post test examination of fractured samples was performed using Scanning Electron Microscopy (SEM) and optical microscope techniques. The fractography results were used to quantify microstructural and fracture features of the steels.A model based on the size and geometry of the initial corrosion pitting has been proposed to asses the fatigue life of FV520B in an aggressive environment.The effect of pitting on the corrosion fatigue strength of FV520B has been modelled using linear elastic fracture mechanics (LEFM) type approach. The model has shown a good correlation between predicted fatigue lives with experimental results.The results suggest that the fatigue life is governed by the mechanical stress concentrating effect of the pits rather than the electrochemical damage caused by the environment.Finite Element Analysis (FEA) of the notch allowed

  17. Copper Tube Pitting in Santa Fe Municipal Water Caused by Microbial Induced Corrosion.

    Science.gov (United States)

    Burleigh, Thomas D; Gierke, Casey G; Fredj, Narjes; Boston, Penelope J

    2014-06-05

    Many copper water lines for municipal drinking water in Santa Fe, New Mexico USA, have developed pinhole leaks. The pitting matches the description of Type I pitting of copper, which has historically been attributed to water chemistry and to contaminants on the copper tubing surface. However, more recent studies attribute copper pitting to microbial induced corrosion (MIC). In order to test for microbes, the copper tubing was fixed in hexamethyldisilazane (HMDS), then the tops of the corrosion mounds were broken open, and the interior of the corrosion pits were examined with scanning electron microscopy (SEM). The analysis found that microbes resembling actinobacteria were deep inside the pits and wedged between the crystallographic planes of the corroded copper grains. The presence of actinobacteria confirms the possibility that the cause of this pitting corrosion was MIC. This observation provides better understanding and new methods for preventing the pitting of copper tubing in municipal water.

  18. Copper Tube Pitting in Santa Fe Municipal Water Caused by Microbial Induced Corrosion

    Directory of Open Access Journals (Sweden)

    Thomas D. Burleigh

    2014-06-01

    Full Text Available Many copper water lines for municipal drinking water in Santa Fe, New Mexico USA, have developed pinhole leaks. The pitting matches the description of Type I pitting of copper, which has historically been attributed to water chemistry and to contaminants on the copper tubing surface. However, more recent studies attribute copper pitting to microbial induced corrosion (MIC. In order to test for microbes, the copper tubing was fixed in hexamethyldisilazane (HMDS, then the tops of the corrosion mounds were broken open, and the interior of the corrosion pits were examined with scanning electron microscopy (SEM. The analysis found that microbes resembling actinobacteria were deep inside the pits and wedged between the crystallographic planes of the corroded copper grains. The presence of actinobacteria confirms the possibility that the cause of this pitting corrosion was MIC. This observation provides better understanding and new methods for preventing the pitting of copper tubing in municipal water.

  19. Influence of cracks and pitting corrosion on residual ultimate strength of stiffened plates

    Directory of Open Access Journals (Sweden)

    ZHANG Jing

    2018-02-01

    Full Text Available [Objectives] Ships and offshore platforms serve in the harsh sea environment for a long time. Cracks and pitting corrosion will occur in such a structure and the damage will affect its ultimate strength.[Methods] To investigate the influence of cracks and pitting corrosion on ultimate bearing capacity, the ultimate strength of a structure under axial compression is studied by using a nonlinear finite element. The mesh size of a stiffened plate with cracks and pitting corrosion is first discussed. Then the influence of the relative positions of cracks and pitting corrosion, number of corrosion points and crack length impact on the residual ultimate strength of damaged stiffened plates is discussed via a series of calculations.[Results] The results indicate that the increase in crack length and pitting corrosion significantly decreases the ultimate strength of a stiffened plate. [Conclusions] This provides a useful reference for designing and maintaining ships and offshore structures in their life cycles.

  20. Investigation of Stress Concentration and Casing Strength Degradation Caused by Corrosion Pits

    Directory of Open Access Journals (Sweden)

    Wei Yan

    2016-01-01

    Full Text Available Downhole casing and tubing are subjected to corrosion in many cases because of the exposure to corrosive environment. A more serious problem is that pitting corrosion occurs in the casing inner surface. Meanwhile, downhole strings are subjected to various forms of mechanical loads, for example, internal pressure load, external collapse load, or both. These loads acting on the corrosion pits will cause stress concentration and degrade the casing strength. Thus, it is essential to evaluate the stress concentration degree reasonably. The SCF (stress concentration factor is usually used to characterize the degree of stress concentration induced by corrosion pits. This paper presented a comparison on the SCFs regarding the analytical method for a single pit and experimental method for double pits. The results show that the SCF of a single pit depends mainly on the depth of the corrosion pit; however, the SCF of the double pits strongly depends on the pits distance. A correction factor of 1.3 was recommended in the double pits SCF prediction model.

  1. Simulation of Fatigue Crack Initiation at Corrosion Pits With EDM Notches

    Science.gov (United States)

    Smith, Stephen W.; Newman, John A.; Piascik, Robert S.

    2003-01-01

    Uniaxial fatigue tests were conducted to compare the fatigue life of laboratory produced corrosion pits, similar to those observed in the shuttle main landing gear wheel bolt-hole, and an electro-discharged-machined (EDM) flaw. EDM Jaws are used to simulate corrosion pits during shuttle wheel (dynamometer) testing. The aluminum alloy, (AA 7050) laboratory fatigue tests were conducted to simulate the local stress level contained in the wheel bolt-hole. Under this high local stress condition, the EDM notch produced a fatigue life similar to test specimens containing corrosion pits of similar size. Based on the laboratory fatigue test results, the EDM Jaw (semi-circular disc shaped) produces a local stress state similar to corrosion pits and can be used to simulate a corrosion pit during the shuttle wheel dynamometer tests.

  2. Perchlorate reduction during electrochemically induced pitting corrosion of zero-valent titanium (ZVT)

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Chunwoo, E-mail: clee@doosanhydro.com [Department of Research and Development, Doosan Hydro Technology, Inc, Tampa, FL 33619 (United States); Batchelor, Bill [Zachry Department of Civil Engineering, Texas A and M University, College Station, TX 77840 (United States); Park, Sung Hyuk [Environmental and Engineering Research Team, GS Engineering and Construction Research Institute, Youngin, Kyunggi-do 449-831 (Korea, Republic of); Han, Dong Suk; Abdel-Wahab, Ahmed [Chemical Engineering Program, Texas A and M University at Qatar, Education City, Doha, PO Box 23874 (Qatar); Kramer, Timothy A.

    2011-12-15

    Highlights: Black-Right-Pointing-Pointer ZVT is oxidized during electrochemically induced pitting corrosion to produce reactive soluble species. Black-Right-Pointing-Pointer Perchlorate is effectively reduced to chloride by soluble titanium species. Black-Right-Pointing-Pointer Solution pH and surface area of ZVT showed negligible effects on rates of perchlorate reduction. - Abstract: Zero-valent metals and ionic metal species are a popular reagent for the abatement of contaminants in drinking water and groundwater and perchlorate is a contaminant of increasing concern. However, perchlorate degradation using commonly used reductants such as zero-valent metals and soluble reduced metal species is kinetically limited. Titanium in the zero-valent and soluble states has a high thermodynamic potential to reduce perchlorate. Here we show that perchlorate is effectively reduced to chloride by soluble titanium species in a system where the surface oxide film is removed from ZVT and ZVT is oxidized during electrochemically induced pitting corrosion to produce reactive soluble species. The pitting potential of ZVT was measured as 12.77 {+-} 0.04 V (SHE) for a 100 mM solution of perchlorate. The rate of perchlorate reduction was independent of the imposed potential as long as the potential was maintained above the pitting potential, but it was proportional to the applied current. Solution pH and surface area of ZVT electrodes showed negligible effects on rates of perchlorate reduction. Although perchlorate is effectively reduced during electrochemically induced corrosion of ZVT, this process may not be immediately applicable to perchlorate treatment due to the high potentials needed to produce active reductants, the amount of titanium consumed, the inhibition of perchlorate removal by chloride, and oxidation of chloride to chlorine.

  3. Perchlorate reduction during electrochemically induced pitting corrosion of zero-valent titanium (ZVT)

    International Nuclear Information System (INIS)

    Lee, Chunwoo; Batchelor, Bill; Park, Sung Hyuk; Han, Dong Suk; Abdel-Wahab, Ahmed; Kramer, Timothy A.

    2011-01-01

    Highlights: ► ZVT is oxidized during electrochemically induced pitting corrosion to produce reactive soluble species. ► Perchlorate is effectively reduced to chloride by soluble titanium species. ► Solution pH and surface area of ZVT showed negligible effects on rates of perchlorate reduction. - Abstract: Zero-valent metals and ionic metal species are a popular reagent for the abatement of contaminants in drinking water and groundwater and perchlorate is a contaminant of increasing concern. However, perchlorate degradation using commonly used reductants such as zero-valent metals and soluble reduced metal species is kinetically limited. Titanium in the zero-valent and soluble states has a high thermodynamic potential to reduce perchlorate. Here we show that perchlorate is effectively reduced to chloride by soluble titanium species in a system where the surface oxide film is removed from ZVT and ZVT is oxidized during electrochemically induced pitting corrosion to produce reactive soluble species. The pitting potential of ZVT was measured as 12.77 ± 0.04 V (SHE) for a 100 mM solution of perchlorate. The rate of perchlorate reduction was independent of the imposed potential as long as the potential was maintained above the pitting potential, but it was proportional to the applied current. Solution pH and surface area of ZVT electrodes showed negligible effects on rates of perchlorate reduction. Although perchlorate is effectively reduced during electrochemically induced corrosion of ZVT, this process may not be immediately applicable to perchlorate treatment due to the high potentials needed to produce active reductants, the amount of titanium consumed, the inhibition of perchlorate removal by chloride, and oxidation of chloride to chlorine.

  4. Effect of chloride concentration and pH on pitting corrosion of waste package container materials

    International Nuclear Information System (INIS)

    Roy, A.K.; Fleming, D.L.; Gordon, S.R.

    1996-12-01

    Electrochemical cyclic potentiodynamic polarization experiments were performed on several candidate waste package container materials to evaluate their susceptibility to pitting corrosion at 90 degrees C in aqueous environments relevant to the potential underground high-level nuclear waste repository. Results indicate that of all the materials tested, Alloy C-22 and Ti Grade-12 exhibited the maximum corrosion resistance, showing no pitting or observable corrosion in any environment tested. Efforts were also made to study the effect of chloride ion concentration and pH on the measured corrosion potential (Ecorr), critical pitting and protection potential values

  5. Effect of heat treatment on pitting corrosion of austenitic Cr-Ni-Mo steels in sodium chloride solution

    International Nuclear Information System (INIS)

    Stefec, R.; Franz, F.; Holecek, A.

    1979-01-01

    The pitting corrosion resistance of Cr17Ni12Mo2,5 type steel under potentiostatic polarization in a sodium chloride solution is adversely affected by previous annealing. The data obtained were systematically dependent on annealing temperature, time and surface roughness. The corrosion current, the number of pits or the mean area of pit opening and the corrosion rate within the pits were increased by previous annealing at 550 to 750 0 C for 1-100 hrs. The highest corrosion rate estimated corresponded to heat treatments provoking severe sensitization to intergranular corrosion. The paercentage area of corrosion pit openings and the estimated pit penetration rates were several times higher for as-machined than for polished surfaces. It can be assumed that pitting corrosion is little affected by the carbon content and that molybdenum depletion of grain-boundary zones is responsible for the reduced pitting resistance of annealed steels. (orig./HP) [de

  6. Study of pitting corrosion in line-pipe steel under the influence of remanent magnetization

    Energy Technology Data Exchange (ETDEWEB)

    Espina-Hernandez, J H; Caleyo, F; Hallen, J M [Instituto Politecnico Nacional (IPN), Zacatenco (Mexico)

    2009-07-01

    The influence of remanent magnetization on pitting corrosion in line-pipe steels is studied. Pitting corrosion experiments have been carried out on samples of an API 5L grade 52 steel under a magnetization level of the same order of magnitude of the remanent magnetization in the pipeline wall after in-line inspection based on magnetic flux leakage. The samples were magnetized using rings of the same grade as the investigated steel. Immediately after magnetization, the investigated samples were subjected to pitting by immersing them in a solution containing dissolved Cl{sup -} and SO{sup 2-}{sub 4} and ions. The pitting experiments were conducted during a seven days period. The pit depth distribution and the maximum pit depth in each sample were recorded and used to conduct extreme value analyses of the pitting process in magnetized and non-magnetized control samples. The statistical assessment of the pitting corrosion data collected during this study shows that the magnetic field reduces the average depth of the pit population and also the extreme pit depth values that can be predicted from the maximum values observed in the magnetized samples in comparison with to the non-magnetized control samples. Scanning electron microscopy observations show that the magnetic field alters the pit morphology by increasing the pit mouth opening. (author)

  7. The influence of the cathodic process on the interpretation of electrochemical noise signals arising from pitting corrosion of stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Klapper, Helmuth Sarmiento [Federal Institute for Materials Research and Testing, Unter den Eichen 87, 12205 Berlin (Germany)], E-mail: Helmuth.sarmiento-klapper@bam.de; Goellner, Joachim [Otto von Guericke University Magdeburg, P.O. Box 4120, Magdeburg (Germany); Heyn, Andreas [Federal Institute for Materials Research and Testing, Unter den Eichen 87, 12205 Berlin (Germany); Otto von Guericke University Magdeburg, P.O. Box 4120, Magdeburg (Germany)

    2010-04-15

    The use of electrochemical noise (EN) measurements for the investigation and monitoring of corrosion has allowed many interesting advances in the corrosion science in recent years. A special advantage of EN measurements includes the possibility to detect and study the early stages of localized corrosion. Nevertheless, the understanding of the electrochemical information included in the EN signal is actually very limited. The role of the cathodic process on the EN signals remains uncertain and has not been sufficiently investigated to date. Thus, an accurate understanding of the influence of the cathodic process on the EN signal is still lacking. On the basis of different kinetics of the oxygen reduction it was established that the anodic amplitude of transients arising from pitting corrosion on stainless steel can be decreased by the corresponding electron consumption of the cathodic process. Therefore, the stronger the electron consumption, the weaker the anodic amplitude of the EN signal becomes. EN signals arising from pitting corrosion on stainless steel can be measured because the cathodic process is inhibited by the passive layer. This was confirmed by means of EN measurements under cathodic polarisation. Since the cathodic process plays a decisive role on the form of transients arising from pitting corrosion, its influence must be considered in the evaluation and interpretation of the EN signals.

  8. Graphene: corrosion-inhibiting coating.

    Science.gov (United States)

    Prasai, Dhiraj; Tuberquia, Juan Carlos; Harl, Robert R; Jennings, G Kane; Rogers, Bridget R; Bolotin, Kirill I

    2012-02-28

    We report the use of atomically thin layers of graphene as a protective coating that inhibits corrosion of underlying metals. Here, we employ electrochemical methods to study the corrosion inhibition of copper and nickel by either growing graphene on these metals, or by mechanically transferring multilayer graphene onto them. Cyclic voltammetry measurements reveal that the graphene coating effectively suppresses metal oxidation and oxygen reduction. Electrochemical impedance spectroscopy measurements suggest that while graphene itself is not damaged, the metal under it is corroded at cracks in the graphene film. Finally, we use Tafel analysis to quantify the corrosion rates of samples with and without graphene coatings. These results indicate that copper films coated with graphene grown via chemical vapor deposition are corroded 7 times slower in an aerated Na(2)SO(4) solution as compared to the corrosion rate of bare copper. Tafel analysis reveals that nickel with a multilayer graphene film grown on it corrodes 20 times slower while nickel surfaces coated with four layers of mechanically transferred graphene corrode 4 times slower than bare nickel. These findings establish graphene as the thinnest known corrosion-protecting coating.

  9. Pitting corrosion and crevice corrosion of an advanced chromium-based stainless steel

    International Nuclear Information System (INIS)

    Kohler, M.

    1999-01-01

    Alloy 33 is a (wt. %) 33 Cr-32Fe-31Ni-1.6Mo-0.6CU-0.4N austenitic stainless steel combining high yield strength of min. 380 N/mm 2 (55 KSI) with high resistance to local corrosion and superior resistance to stress corrosion cracking. Ranking the material according to its PRE (pitting resistance equivalent) value, the new alloy fits in between the advanced 6% Mo superaustenitics and the nickel-base Alloy 625 but due to the balanced chemical composition the alloy shows a lot less sensitivity to segregation in the base material as well as in welded structures. It is recommended to weld the material with matching filler. The critical pitting temperature of such joints in the 10% FeCl 3 · 6H 2 O solution is reduced by only 10 C in comparison to the base material. Corrosion tests in artificial seawater (20 g/l Cl - ) with additions of chloride up to 37 g/l as well as in a NaCl-CaCl 2 , solution with 62 g/l Cl - --revealed that the critical pitting temperature does not differentiate from the 6% Mo austenitic steel Alloy 926. With respect to crevice corrosion the depassivation pH value has been determined in 1 M NaCl solution according to Crolet and again there was no difference between Alloy 33 and Alloy 926. SCC tests performed on Alloy 33 in the solution annealed condition as well as after heavy cold work up to R PO,2 ∼ 1,100--1,200 N/mm 2 (160--174 KSI) indicate the high resistance to stress corrosion cracking in hot sodium chloride solutions

  10. Pitting Corrosion of Ni3(Si,Ti Intermetallic Compound at Various Chloride Concentrations

    Directory of Open Access Journals (Sweden)

    Gadang Priyotomo

    2013-10-01

    Full Text Available The pitting corrosion of Ni3(Si,Ti intermetallic compound was investigated as function of chloride concentration by using electrochemical method and scanning electron microscope in sodium chloride solutions at 293 K.  In addition, the pitting corrosion of type C276 alloy was also studied under the same experimental condition for comparison.  The pitting potential obtained for the intermetallic compound decreased with increasing chloride concentration.  The specific pitting potential and pitting potential of Ni3(Si,Ti were lower than those of C276 alloy, which means that the pitting corrosion resistance of C276 alloy was higher than that of Ni3(Si,Ti.

  11. Failure Analysis of End Grain Attack and Pit Corrosion in 316L Stainless Steel Pipe

    Energy Technology Data Exchange (ETDEWEB)

    Baek, Un Bong; Nam, Sung Hoon [Korea Research Institute of Standards and Science, Daejeon (Korea, Republic of); Choe, Byung Hak; Shim, Jong Hun [Gangneung-Wonju National University, Gangneung (Korea, Republic of); Lee, Jin Hee [Oil and Gas Technology SK E and C, Junggu (Korea, Republic of); Kim, Eui Soo [National Forensic Service, Wonju (Korea, Republic of)

    2015-01-15

    The aim of this paper was to analyze the cause of surface cracks and pit corrosion on 316L pipe. An End Grain Attack (EGA) as a kind of pit mechanism was conducted on the pipe surface. The early stage of the EGA may come from under-deposit of caustic-water formation compositions like Na+, K+, Ca+, and Mg+ etc. The under-deposit corrosion is caused by the corrosion layer on the pipe surface followed by crevice corrosion due to accumulation of Cl‒ or S‒ composition between the corrosion layer and the pipe surface. In the early stage, the EGA occurred in all grain boundaries beneath the under-deposit corrosion. In the later stage of EGA, almost all the early attacked grain boundaries stopped at a limited depth of about 10 µm. Meanwhile, only the smallest number of the attacked boundaries progressed into the pipe as pit corrosion and resulted in leak failure.

  12. Testing of intergranular and pitting corrosion in sensitized welded joints of austenitic stainless steel

    Directory of Open Access Journals (Sweden)

    Bore V. Jegdic

    2017-06-01

    Full Text Available Pitting corrosion resistance and intergranular corrosion of the austenitic stainless steel X5Cr Ni18-10 were tested on the base metal, heat affected zone and weld metal. Testing of pitting corrosion was performed by the potentiodynamic polarization method, while testing of intergranular corrosion was performed by the method of electrochemical potentiokinetic reactivation with double loop. The base metal was completely resistant to intergranular corrosion, while the heat affected zone showed a slight susceptibility to intergranular corrosion. Indicators of pitting corrosion resistance for the weld metal and the base metal were very similar, but their values are significantly higher than the values for the heat affected zone. This was caused by reduction of the chromium concentration in the grain boundary areas in the heat affected zone, even though the carbon content in the examined stainless steel is low (0.04 wt. % C.

  13. Pitting Corrosion Behavior of 304 SS and 316 SS Alloys in Aqueous Chloride and Bromide Solutions

    Directory of Open Access Journals (Sweden)

    Ibtehal Kareem Shakir

    2018-01-01

    Full Text Available The importance of the present work falls on the pitting corrosion behavior investigation of 304 SS and 316 SS alloys in 3.5 wt% of aqueous solution bearing with chloride and bromide anion at different solutions temperature range starting from (20-50oC due to the pitting corrosion tremendous effect on the economic, safety and materials loss due to leakage. The impact of solution temperatures on the pitting corrosion resistance at 3.5wt% (NaCl and NaBr solutions for the 304 SS and 316 SS has been investigated utilizing the cyclic polarization techniques at the potential range -400 to1000 mV vs. SCE at 40 mV/sec scan rate followed by the surface characterization employing Scanning Electron Microscope. The results show that a significant decline in the pitting corrosion potential Ep values of both stainless steel alloys in chloride and bromide solution during temperature increase attributed to the pitting corrosion potential decreased arises from the modification of the passive film properties. The surface examination using optical microscope and scanning electron microscope prove the occurring of higher pitting density over 304 SS in chloride solution than that observed in bromide solution with a non-circular lacy cover pitfall out at the center and falls inside the pits hall in comparison to the isolated circular lacy cover pit formed on 316 SS in 3.5wt% NaBr solution at 50 oC.

  14. Pitting corrosion of Inconel 600 in chloride and sulfate solutions at low temperature

    International Nuclear Information System (INIS)

    Chang Mingyu; Yu Geping

    1993-01-01

    Pitting corrosion of Inconel 600 was examined in chloride and sulfate solutions through usage of potentiodynamic polarization techniques. The effects of chloride and sulfate concentration were investigated in the range of 0.0001 to 0.1 M. Increasing chloride concentrations resulted in active shifts of the pit nucleation potential. Immunity to pitting corrosion was evident at a chloride level below 0.005 M. Increasing sulfate concentrations resulted in improved pitting resistance of Inconel 600 in chloride solutions. Detrimental effects associated with pitting were evident with low-level sulfate being added to dilute chloride media. The density of pits increased with increasing chloride concentrations or temperature between room temperature and 70 C. Systematic trends for the depth of pits were not evident. The observations of pitting corrosion in open immersion were consistent with those in polarization methods. Corrosion products contained in the pits were enriched in nickel, chromium and iron with a small amount of titanium and silicon. The enrichment of chlorine or sulfur was still, however, not found. (orig.)

  15. A numerical study of under-deposit pitting corrosion in sour petroleum pipelines

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Z.; Sand, K.W.; Teevens, P.J. [Broadsword Corrosion Engineering Ltd., Calgary, AB (Canada)

    2010-07-01

    Insufficient fluid velocity in petroleum pipelines can lead to the deposit of sand, corrosion products, and non-corrosion products on the pipe's metal surface, which in turn can lead to pitting corrosion. There is currently no reliable means of detecting and preventing the pitting process. This paper presented a computerized simulation tool that used the finite element method to model mass transfer-governed internal pitting corrosion under solids deposition in sour petroleum pipelines. The computational domain consisted of a hemispherical pit and a thin stagnant solution film under a surface deposit. The moving mesh method was used to track pitting growth. A Poisson equation was used to determine aqueous path migration of ions. Pitting corrosion rates were estimated using the Nernst-Planck equation. The model was used to predict the effects of different operating parameters on pitting corrosion rates. The model can be used to develop pigging and in-line-inspection (ILI) procedures. 35 refs., 2 tabs., 16 figs.

  16. A predictive approach to fitness-for-service assessment of pitting corrosion

    International Nuclear Information System (INIS)

    Shekari, Elahe; Khan, Faisal; Ahmed, Salim

    2016-01-01

    Pitting corrosion is a localized corrosion that often causes leak and failure of process components. The aim of this work is to present a new fitness-for-service (FFS) assessment methodology for process equipment to track and predict pitting corrosion. In this methodology, pit density is modeled using a non-homogenous Poisson process and induction time for pit initiation is simulated as the realization of a Weibull process. The non-homogenous Markov process is used to estimate maximum pit depth, considering that only the current state of the damage influences its future development. Subsequently, the distributions of the operating pressure and the estimated burst pressure of the defected component are integrated with Monte Carlo simulations and First Order Second Moment (FOSM) method to calculate the reliability index and probability of failure. This methodology provides a more realistic failure assessment and enables consideration of uncertainty associated with estimating pit characteristics. The practical application of the proposed model is demonstrated using a piping case study. - Highlights: • A new model to estimate maximum pit depth and pit density as two main pit characteristics. • Integrating maximum pit depth with failure analysis considering allowable pressure of defected component. • Time dependent failure analysis to determine the remaining life.

  17. Pitting Corrosion Behaviour of New Corrosion-Resistant Reinforcement Bars in Chloride-Containing Concrete Pore Solution.

    Science.gov (United States)

    Jiang, Jin-Yang; Liu, Yao; Chu, Hong-Yan; Wang, Danqian; Ma, Han; Sun, Wei

    2017-08-04

    In this study, the pitting behaviour of a new corrosion-resistant alloy steel (CR) is compared to that of low-carbon steel (LC) in a simulated concrete pore solution with a chloride concentration of 5 mol/L. The electrochemical behaviour of the bars was characterised using linear polarisation resistance (LPR) and electrochemical impedance spectroscopy (EIS). The pitting profiles were detected by reflective digital holographic microscopy (DHM), scanning electron microscopy (SEM), and the chemical components produced in the pitting process were analysed by X-ray energy dispersive spectroscopy (EDS). The results show that the CR bars have a higher resistance to pitting corrosion than the LC bars. This is primarily because of the periodic occurrence of metastable pitting during pitting development. Compared to the pitting process in the LC bars, the pitting depth grows slowly in the CR bars, which greatly reduces the risk of pitting. The possible reason for this result is that the capability of the CR bars to heal the passivation film helps to restore the metastable pits to the passivation state.

  18. Laser surface melting of 304 stainless steel for pitting corrosion resistance improvement

    CSIR Research Space (South Africa)

    Seleka, TS

    2006-11-01

    Full Text Available optical emission spectroscopy (GDOES) was utilized for chemical analysis. Changes in hardness were observed by using a Vickers microhardness tester. Pitting corrosion tests on laser treated and untreated samples were conducted according to ASTM G48...

  19. Probability distribution of pitting corrosion depth and rate in underground pipelines: A Monte Carlo study

    International Nuclear Information System (INIS)

    Caleyo, F.; Velazquez, J.C.; Valor, A.; Hallen, J.M.

    2009-01-01

    The probability distributions of external-corrosion pit depth and pit growth rate were investigated in underground pipelines using Monte Carlo simulations. The study combines a predictive pit growth model developed by the authors with the observed distributions of the model variables in a range of soils. Depending on the pipeline age, any of the three maximal extreme value distributions, i.e. Weibull, Frechet or Gumbel, can arise as the best fit to the pitting depth and rate data. The Frechet distribution best fits the corrosion data for long exposure periods. This can be explained by considering the long-term stabilization of the diffusion-controlled pit growth. The findings of the study provide reliability analysts with accurate information regarding the stochastic characteristics of the pitting damage in underground pipelines.

  20. Probability distribution of pitting corrosion depth and rate in underground pipelines: A Monte Carlo study

    Energy Technology Data Exchange (ETDEWEB)

    Caleyo, F. [Departamento de Ingenieria Metalurgica, ESIQIE, IPN, UPALM Edif. 7, Zacatenco, 07738 Mexico, D.F. (Mexico)], E-mail: fcaleyo@gmail.com; Velazquez, J.C. [Departamento de Ingenieria Metalurgica, ESIQIE, IPN, UPALM Edif. 7, Zacatenco, 07738 Mexico, D.F. (Mexico); Valor, A. [Facultad de Fisica, Universidad de La Habana, San Lazaro y L, Vedado, 10400, La Habana (Cuba); Hallen, J.M. [Departamento de Ingenieria Metalurgica, ESIQIE, IPN, UPALM Edif. 7, Zacatenco, 07738 Mexico, D.F. (Mexico)

    2009-09-15

    The probability distributions of external-corrosion pit depth and pit growth rate were investigated in underground pipelines using Monte Carlo simulations. The study combines a predictive pit growth model developed by the authors with the observed distributions of the model variables in a range of soils. Depending on the pipeline age, any of the three maximal extreme value distributions, i.e. Weibull, Frechet or Gumbel, can arise as the best fit to the pitting depth and rate data. The Frechet distribution best fits the corrosion data for long exposure periods. This can be explained by considering the long-term stabilization of the diffusion-controlled pit growth. The findings of the study provide reliability analysts with accurate information regarding the stochastic characteristics of the pitting damage in underground pipelines.

  1. Stochastic modeling of pitting corrosion in underground pipelines using Markov chains

    Energy Technology Data Exchange (ETDEWEB)

    Velazquez, J.C.; Caleyo, F.; Hallen, J.M.; Araujo, J.E. [Instituto Politecnico Nacional (IPN), Mexico D.F. (Mexico). Escuela Superior de Ingenieria Quimica e Industrias Extractivas (ESIQIE); Valor, A. [Universidad de La Habana, La Habana (Cuba)

    2009-07-01

    A non-homogenous, linear growth (pure birth) Markov process, with discrete states in continuous time, has been used to model external pitting corrosion in underground pipelines. The transition probability function for the pit depth is obtained from the analytical solution of the forward Kolmogorov equations for this process. The parameters of the transition probability function between depth states can be identified from the observed time evolution of the mean of the pit depth distribution. Monte Carlo simulations were used to predict the time evolution of the mean value of the pit depth distribution in soils with different physicochemical characteristics. The simulated distributions have been used to create an empirical Markov-chain-based stochastic model for predicting the evolution of pitting corrosion from the observed properties of the soil in contact with the pipeline. Real- life case studies, involving simulated and measured pit depth distributions are presented to illustrate the application of the proposed Markov chains model. (author)

  2. Numerical Simulation of Interactions between Corrosion Pits on Stainless Steel under Loading Conditions

    International Nuclear Information System (INIS)

    Wang, Haitao; Han, En-Hou

    2017-01-01

    The interactions between corrosion pits on stainless steel under loading conditions are studied by using a cellular automata model coupled with finite element method at a mesoscopic scale. The cellular automata model focuses on a metal/film/electrolyte system, including anodic dissolution, passivation, diffusion of hydrogen ions and salt film hydrolysis. The Chopard block algorithm is used to improve the diffusion simulation efficiency. The finite element method is used to calculate the stress concentration on the pit surface during pit growth, and the effect of local stress and strain on anodic current is obtained by using the Gutman model, which is used as the boundary conditions of the cellular automata model. The transient current characteristics of the interactions between corrosion pits under different simulation factors including the breakdown of the passive film at the pit mouth and the diffusion of hydrogen ions are analyzed. The analysis of the pit stability product shows that the simulation results are close to the experimental conclusions.

  3. Numerical Simulation of Interactions between Corrosion Pits on Stainless Steel under Loading Conditions

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Haitao; Han, En-Hou [Chinese Academy of Sciences, Shenyang (China)

    2017-04-15

    The interactions between corrosion pits on stainless steel under loading conditions are studied by using a cellular automata model coupled with finite element method at a mesoscopic scale. The cellular automata model focuses on a metal/film/electrolyte system, including anodic dissolution, passivation, diffusion of hydrogen ions and salt film hydrolysis. The Chopard block algorithm is used to improve the diffusion simulation efficiency. The finite element method is used to calculate the stress concentration on the pit surface during pit growth, and the effect of local stress and strain on anodic current is obtained by using the Gutman model, which is used as the boundary conditions of the cellular automata model. The transient current characteristics of the interactions between corrosion pits under different simulation factors including the breakdown of the passive film at the pit mouth and the diffusion of hydrogen ions are analyzed. The analysis of the pit stability product shows that the simulation results are close to the experimental conclusions.

  4. Effects of pH and chloride concentration on pitting corrosion of AA6061 aluminum alloy

    International Nuclear Information System (INIS)

    Zaid, B.; Saidi, D.; Benzaid, A.; Hadji, S.

    2008-01-01

    Effects of pH solution and chloride (Cl - ) ion concentration on the corrosion behaviour of alloy AA6061 immersed in aqueous solutions of NaCl have been investigated using measurements of weight loss, potentiodynamic polarisation, linear polarisation, cyclic polarisation experiment combined with open circuit potential transient technique and optical or scanning electron microscopy. The corrosion behaviour of the AA6061 aluminum alloy was found to be dependant on the pH and chloride concentration [NaCl] of solution. In acidic or slightly neutral solutions, general and pitting corrosion occurred simultaneously. In contrast, exposure to alkaline solutions results in general corrosion. Experience revealed that the alloy AA6061 was susceptible to pitting corrosion in all chloride solution of concentration ranging between 0.003 wt% and 5.5 wt% NaCl and an increase in the chloride concentration slightly shifted both the pitting E pit and corrosion E cor potentials to more active values. In function of the conditions of treatment, the sheets of the alloy AA6061 undergo two types of localised corrosion process, leading to the formation of hemispherical and crystallographic pits. Polarisation resistance measurements in acidic (pH = 2) and alkaline chloride solutions (pH = 12) which are in good agreement with those of weight loss, show that the corrosion kinetic is minimised in slightly neutral solutions (pH = 6)

  5. Effects of cold working on the pitting corrosion behavior s of AISI 304 stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Jung, Kee Min; Kim, Jong Soo; Kim, Young Jun; Kwon, Houk Sang [KAIST, Daejon (Korea, Republic of)

    2015-12-15

    These microstructural changes by cold working can lead improvement of mechanical properties, however from a corrosion resistant point of view, the effects of cold working on the corrosion resistance of stainless steel have been argued. Several studies has been focused on the influence of cold working on the localized corrosion resistance of stainless steels. However, the opinions about the role of cold working on the localized corrosion resistance are highly in consistence. Some studies report that the pitting potential of austenitic stainless steels decreased with cold working level, on the other hands, other studies claimed that the pitting resistance was increased by cold working. Therefore it is necessary to verify how cold working affects pitting corrosion behavior of austenitic stainless steels. In the present work, the influence of cold working on the localized corrosion of AISI 304stainless steel in the neutral chloride solution was studied based on point defect model (PDM). The fraction of deformation-induced martensite was linearly increased with cold rolling level. Through cold rolling, the pitting potential was decreased, the metastable pitting event density was significantly increased and the repassivation potential was decreased. The overall localized corrosion resistance was decreased with cold working, however cold working level increased from 30 % to 50 %, localized corrosion resistance was recovered. The accumulated cation vacancy generates a void at metal/film interface, therefore film breakdown accelerates for cold worked alloys.

  6. Effects of cold working on the pitting corrosion behavior s of AISI 304 stainless steels

    International Nuclear Information System (INIS)

    Jung, Kee Min; Kim, Jong Soo; Kim, Young Jun; Kwon, Houk Sang

    2015-01-01

    These microstructural changes by cold working can lead improvement of mechanical properties, however from a corrosion resistant point of view, the effects of cold working on the corrosion resistance of stainless steel have been argued. Several studies has been focused on the influence of cold working on the localized corrosion resistance of stainless steels. However, the opinions about the role of cold working on the localized corrosion resistance are highly in consistence. Some studies report that the pitting potential of austenitic stainless steels decreased with cold working level, on the other hands, other studies claimed that the pitting resistance was increased by cold working. Therefore it is necessary to verify how cold working affects pitting corrosion behavior of austenitic stainless steels. In the present work, the influence of cold working on the localized corrosion of AISI 304stainless steel in the neutral chloride solution was studied based on point defect model (PDM). The fraction of deformation-induced martensite was linearly increased with cold rolling level. Through cold rolling, the pitting potential was decreased, the metastable pitting event density was significantly increased and the repassivation potential was decreased. The overall localized corrosion resistance was decreased with cold working, however cold working level increased from 30 % to 50 %, localized corrosion resistance was recovered. The accumulated cation vacancy generates a void at metal/film interface, therefore film breakdown accelerates for cold worked alloys

  7. Application of spectral analysis of the electrochemical noise to the investigation of aluminium alloy pitting corrosion

    International Nuclear Information System (INIS)

    Bataillon, Christian

    1987-01-01

    The objective of this research is to decode (at least partially) the nature of the information contained in the electrochemical noise associated with the pitting corrosion phenomenon in aluminium alloys. After a general presentation of aluminium and its alloys and a report of a bibliographical study on the electrochemical noise, the author gives an overview of a theoretical approach of stochastic phenomena, and of an experimental approach. Then, the experimental investigation of the electrochemical noise in the case of pitting corrosion leads to a noise control law, to a study of the structure of pitting growth, and to the elaboration of a procedure of assessment of spectral characteristics of this noise. The author reports a systematic study of the electrochemical noise with respect to the parameters of the control law. Results allow a quantitative characterization of pitting corrosion resistance of the studied alloys, notably by using the kinetic aspect of pitting growth and the structure of pitting corrosion. The author discusses the physicochemical nature of random fluctuations which build up the noise. He proposes a more precise explanation of phenomena related to initiation and propagation of pitting corrosion on aluminium alloys in marine environment [fr

  8. Stochastic approach to pitting-corrosion-extreme modelling in low-carbon steel

    Energy Technology Data Exchange (ETDEWEB)

    Valor, A. [Facultad de Fisica, Universidad de La Habana, San Lazaro y L, Vedado 10400, La Habana (Cuba); Caleyo, F. [Departamento de Ingenieria Metalurgica, IPN-ESIQIE, UPALM Edif. 7, Zacatenco, Mexico DF 07738 (Mexico)], E-mail: fcaleyo@gmail.com; Rivas, D.; Hallen, J.M. [Departamento de Ingenieria Metalurgica, IPN-ESIQIE, UPALM Edif. 7, Zacatenco, Mexico DF 07738 (Mexico)

    2010-03-15

    A stochastic model previously developed by the authors using Markov chains has been improved in the light of new experimental evidence. The new model has been successfully applied to reproduce the time evolution of extreme pitting corrosion depths in low-carbon steel. The model is shown to provide a better physical understanding of the pitting process.

  9. Stochastic approach to pitting-corrosion-extreme modelling in low-carbon steel

    International Nuclear Information System (INIS)

    Valor, A.; Caleyo, F.; Rivas, D.; Hallen, J.M.

    2010-01-01

    A stochastic model previously developed by the authors using Markov chains has been improved in the light of new experimental evidence. The new model has been successfully applied to reproduce the time evolution of extreme pitting corrosion depths in low-carbon steel. The model is shown to provide a better physical understanding of the pitting process.

  10. Probabilistic models for steel corrosion loss and pitting of marine infrastructure

    International Nuclear Information System (INIS)

    Melchers, R.E.; Jeffrey, R.J.

    2008-01-01

    With the increasing emphasis on attempting to retain in service ageing infrastructure models for the description and prediction of corrosion losses and for maximum pit depth are of increasing interest. In most cases assessment and prediction will be done in a probabilistic risk assessment framework and this then requires probabilistic corrosion models. Recently, novel models for corrosion loss and maximum pit depth under marine immersion conditions have been developed. The models show that both corrosion loss and pit depth progress in a non-linear fashion with increased exposure time and do so in a non-monotonic manner as a result of the controlling corrosion process changing from oxidation to being influenced by bacterial action. For engineers the importance of this lies in the fact that conventional 'corrosion rates' have no validity, particularly for the long-term corrosion effects as relevant to deteriorated infrastructure. The models are consistent with corrosion science principles as well as current understanding of the considerable influence of bacterial processes on corrosion loss and pitting. The considerable practical implications of this are described

  11. Microstructure and pitting corrosion of 13CrNiMo weld metals

    International Nuclear Information System (INIS)

    Bilmes, P.D.; Llorente, C.L.; Saire Huaman, L.; Gassa, L.M.; Gervasi, C.A.

    2006-01-01

    Cyclic potentiodynamic measurements and scanning electron microscopy were used to analyze susceptibility to pitting corrosion of 13CrNiMo weld metals. In order to carry out a critical assessment of the influence of microstructural factors on localized corrosion, different heat treatments were applied to the alloys under investigation. Volume fractions of austenite in tempered conditions as well as the amount and size of precipitated carbides strongly affect pitting resistance. Characteristic potentials (pitting potential and repassivation potential) increase according to the retained austenite content. Results can be discussed in terms of a model that describes the structural refinement resulting from a double-tempering procedure

  12. Pitting Corrosion of Ni3(Si,Ti+4Al Intermetallic Compound at Various Chloride Concentrations

    Directory of Open Access Journals (Sweden)

    Gadang Priyotomo

    2014-04-01

    Full Text Available The pitting corrosion of Ni3(Si,Ti with 4 at% Al consisting of two regions of a Ni3(Si,Ti single-phase of L12 structure and two phases of L12 and fcc Niss was investigated as function of chloride concentrations by using electrochemical method, scanning electron microscope and energy dispersive X-Ray spectroscopy in neutral sodium chloride solutions at 293 K.  In addition, the pitting corrosion of Ni3(Si,Ti and  type C276 alloy were also studied under the same experimental condition for comparison.  The pitting potential obtained for the Ni3(Si,Ti with 4 at%Al decreased with increasing chloride concentration.  The specific pitting potential and pitting potential of Ni3(Si,Ti with 4at%, Ni3(Si,Ti and C276 were the lowest, the moderate and the highest, respectively, which means that the pitting corrosion resistance of Ni3(Si,Ti was higher than Ni3(Si,Ti with 4at% Al, but lower than that of C276.  A critical chloride concentration of Ni3(Si,Ti with 4at% Al was found to be lower than that of Ni3(Si,Ti.  The Pitting corrosion of Ni3(Si,Ti with 4at% Al occurred in the two phase mixture (L12 + Niss.

  13. Mechanism of pitting corrosion protection of metals and alloys in new-generation water treatment plants

    Directory of Open Access Journals (Sweden)

    Grachev Vladimir

    2017-01-01

    Full Text Available In this article authors set out a principle of pitting corrosion protection, suggested a new class of multilayer materials with high corrosion resistance. They substantiated the choice of the layers for the multilayer material designed for exploitation in oxidizing and non-oxidizing environment. The sphere of application of the multilyer materials was defined.

  14. Influence of the filler material on the pitting corrosion in welded duplex stainless

    International Nuclear Information System (INIS)

    Munez, C. J.; Utrilla, M. V.; Urena, A.; Otero, E.

    2007-01-01

    In this work, it has been studied the pitting corrosion resistance of welding duplex stainless steel 2205. Unions were made by GMAW process with different fillers: duplex ER 2209 and two austenitic (ER 316LSi and ER 308LSi). the microstructure obtained with the duplex ER 2209 filler is similar to the duplex 2205 base material, but the unions produced with the austenitic fillers cause a decrease of the phases relationα/γ. To evaluate the influence of the filler on the weld, the pitting corrosion resistance was determined by electrochemical critical pitting temperature test (TCP) and the mechanical properties by the hardness. The phases imbalance produced for the dissimilar fillers bring out a variation of the pitting corrosion resistance and the mechanical properties. (Author)

  15. Pitting corrosion of friction stir welded aluminum alloy thick plate in alkaline chloride solution

    International Nuclear Information System (INIS)

    Xu Weifeng; Liu Jinhe; Zhu Hongqiang

    2010-01-01

    The pitting corrosion of different positions (Top, Middle and Bottom) of weld nugget zone (WNZ) along thickness plate in friction stir welded 2219-O aluminum alloy in alkaline chloride solution was investigated by using open circuit potential, cyclic polarization, scanning electron microscopy and atomic force microscope. The results indicate that the material presents significant passivation, the top has highest corrosion potential, pitting potential and re-passivation potential compared with the bottom and base material. With the increase of traverse speed from 60 to 100 mm/min or rotary speed from 500 to 600 rpm, the corrosion resistance decreases.

  16. CHROMATE INHIBITION OF THE LOCALIZED CORROSION OF ALUMINUM: MEASUREMENTS OF ELECTROCHEMICAL TRANSIENTS

    International Nuclear Information System (INIS)

    SASAKI, K.; ISAACS, H.S.

    2001-01-01

    We investigated the inhibition by chromate ions of the localized corrosion of aluminum by electrochemical transient measurements. In agreement with other work, the measurements demonstrated that chromate is a cathodic inhibitor for aluminum in open circuit. The reduction of hexavalent chromium to trivalent chromium is assumed to take place on catalyzed sites of the surface. The resulting products inhibit oxygen reduction reactions at these sites, thereby retarding pitting corrosion

  17. Prediction of microsegregation and pitting corrosion resistance of austenitic stainless steel welds by modelling

    Energy Technology Data Exchange (ETDEWEB)

    Vilpas, M. [VTT Manufacturing Technology, Espoo (Finland). Materials and Structural Integrity

    1999-07-01

    The present study focuses on the ability of several computer models to accurately predict the solidification, microsegregation and pitting corrosion resistance of austenitic stainless steel weld metals. Emphasis was given to modelling the effect of welding speed on solute redistribution and ultimately to the prediction of weld pitting corrosion resistance. Calculations were experimentally verified by applying autogenous GTA- and laser processes over the welding speed range of 0.1 to 5 m/min for several austenitic stainless steel grades. Analytical and computer aided models were applied and linked together for modelling the solidification behaviour of welds. The combined use of macroscopic and microscopic modelling is a unique feature of this work. This procedure made it possible to demonstrate the effect of weld pool shape and the resulting solidification parameters on microsegregation and pitting corrosion resistance. Microscopic models were also used separately to study the role of welding speed and solidification mode in the development of microsegregation and pitting corrosion resistance. These investigations demonstrate that the macroscopic model can be implemented to predict solidification parameters that agree well with experimentally measured values. The linked macro-micro modelling was also able to accurately predict segregation profiles and CPT-temperatures obtained from experiments. The macro-micro simulations clearly showed the major roles of weld composition and welding speed in determining segregation and pitting corrosion resistance while the effect of weld shape variations remained negligible. The microscopic dendrite tip and interdendritic models were applied to welds with good agreement with measured segregation profiles. Simulations predicted that weld inhomogeneity can be substantially decreased with increasing welding speed resulting in a corresponding improvement in the weld pitting corrosion resistance. In the case of primary austenitic

  18. Influence of microstructure and elemental partitioning on pitting corrosion resistance of duplex stainless steel welding joints

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Zhiqiang; Jing, Hongyang [School of Materials Science and Engineering, Tianjin University, Tianjin 300350 (China); Tianjin Key Laboratory of Advanced Joining Technology, Tianjin 300350 (China); Xu, Lianyong, E-mail: xulianyong@tju.edu.cn [School of Materials Science and Engineering, Tianjin University, Tianjin 300350 (China); Tianjin Key Laboratory of Advanced Joining Technology, Tianjin 300350 (China); Han, Yongdian; Zhao, Lei [School of Materials Science and Engineering, Tianjin University, Tianjin 300350 (China); Tianjin Key Laboratory of Advanced Joining Technology, Tianjin 300350 (China); Zhang, Jianli [Welding laboratory, Offshore Oil Engineering (Qing Dao) Company, Qing Dao 266520 (China)

    2017-02-01

    Highlights: • N{sub 2}-supplemented shielding gas promoted nitrogen solid-solution in the austenite. • Secondary austenite had higher Ni but lower Cr and Mo than primary austenite. • Pitting corrosion preferentially occurred at secondary austenite and Cr{sub 2}N. • Adding N{sub 2} in shielding gas improved pitting corrosion resistance of GTAW joint. • E2209T{sub 1} weld metal had very poor pitting corrosion resistance due to inclusions. - Abstract: The influences of microstructure and elemental partitioning on pitting corrosion resistance of duplex stainless steel joints welded by gas tungsten arc welding (GTAW) and flux-cored arc welding (FCAW) with different shielding gas compositions were studied by optical microscopy, electron backscatter diffraction, scanning electron microscopy, transmission electron microscopy, energy dispersive spectroscopy, electron probe microanalysis, and potentiostatic and potentiodynamic polarization methods The adding 2% N{sub 2} in shielding gas facilitated primary austenite formation in GTAW weld metal (WM) and suppressed Cr{sub 2}N precipitation in GTAW weld root. In the HAZ, the banded microstructure disappeared while the coarse ferrite grains maintained same orientation as the banded ferrite in the BM. In the WM, the ferrite had one single orientation throughout a grain, whereas several families of austenite appeared. The austenite both in BM and WM enriched in Ni and nitrogen, while Cr and Mo were concentrated in the ferrite and thus no element showed clear dendritic distribution in the WM (ER2209 and E2209T{sub 1}). In addition, the secondary austenite had higher Ni content but lower Cr and Mo content than the primary austenite. The N{sub 2}-supplemented shielding gas promoted nitrogen solid-solution in the primary and secondary austenite. Furthermore, the secondary austenite had relatively lower pitting resistance equivalent number (PREN) than the ferrite and primary austenite, thereby resulting in its preferential

  19. Pitting Corrosion of Ni3(Si,Ti+2Cr Intermetallic Compound at Various Chloride Concentrations

    Directory of Open Access Journals (Sweden)

    Gadang Priyotomo

    2014-05-01

    Full Text Available The pitting corrosion of Ni3(Si,Ti with 2 at% Cr containing two regions of a Ni3(Si,Ti single-phase of L12 structure and a mixture phase of of (L12 +Niss was investigated as function of chloride concentrations by using a polarization method, scanning electron microscope and energy dispersive X-Ray spectroscopy in neutral sodium chloride solutions at 293 K.  The pitting corrosion of Ni3(Si,Ti with and without the addition of aluminium and type C276 alloy were also studied under the same experimental condition for the comparison.  The pitting potential obtained for the Ni3(Si,Ti with 2 at% Cr decreased with increasing chloride concentration.  The specific pitting potentials and the pitting potentials were decreased in the order of C276 alloy > Ni3(Si,Ti > Ni3(Si,Ti + 2Cr > Ni3(Si,Ti + 4Al, which means that the pitting corrosion resistance of Ni3(Si,Ti with 2 at% Cr was higher than Ni3(Si,Ti with 4 at% Al, but lower than that of Ni3(Si,Ti.  A critical chloride concentration of Ni3(Si,Ti with 2 at% Cr was found to be higher than that of Ni3(Si,Ti with at% Al. In addition, the presence of high concentration for oxygen indicates the occurrence of pit formation.

  20. Resistance to pitting corrosion in ferritic and austenitic/ferritic steels

    International Nuclear Information System (INIS)

    De Bouvier, O.

    1995-01-01

    Stainless steel tubes carrying raw water are potentially vulnerable to pitting corrosion. With a view to minimizing the corrosion risk in the river-water-cooled condensers at PWR power plant, a study was conducted to determine initiation conditions and incubation durations for pitting corrosion in stagnant water. As a result, condenser tubes in Z2 CI 18 (439) or Z2 CT 18-10 (304L) steels were phased out in favour of Z2 CND 16-32 (316L) stainless steel. The same question can be yield for other applications and especially for all types of exchangers for use in electrical applications. This study sought to assess alternative methods for estimating pitting corrosion, and to check the results of these methods against the actual behaviour of studied steels. The study covered ferritic steels (439, 444, 290Mo), austenitic steel (316L) and austenitic/ferritic steels (Uranus 35N, 45N, 47N, 52N). Two approaches were adopted: laboratory tests to compare pitting corrosion risks on different materials, and tests for characterizing the behaviour of steels exposed to river water. The study begins with a laboratory tests that yield an arbitrary parameter for quantifying pitting corrosion resistance. One method involves measuring the pitting temperature in an aggressive ferric chloride solution. Other methods measure the pitting potential, either statistically (Multipit method) or deterministically (polarization curve). We then go on to discuss tests under simulated life-like conditions, involving repeated immersions in water from the Seine. (author). 9 refs., 13 figs, 9 tabs

  1. Mechanism of pitting corrosion prevention by nitrite in carbon steel exposed to dilute salt solutions. 1998 annual progress report

    International Nuclear Information System (INIS)

    Zapp, P.E.; Zee, J. van.

    1998-01-01

    'The overall goal of this project is to develop a fundamental understanding of the role of nitrite in preventing the breakdown of protective oxide(s) on carbon steel and the onset of pitting. Pitting corrosion of carbon steel exposed to dilute alkaline salt solutions can be induced by nitrate, sulfate, and chloride ions and is prevented by sufficient concentration of nitrite. A significant example of this material/electrolyte system is the storage and processing of DOE''s high-level radioactive liquid waste in carbon steel tanks. Added nitrite in the waste has a considerable downstream impact on the immobilization of the waste in a stable glass form. Waste tank integrity and glass production efficiency may benefit from the fundamental understanding of nitrite''s role in preventing pitting. This report summarizes progress after approximately six months of effort in this three-year EMSP project. Initial experimental and theoretical work has focused on the electrochemical behavior of carbon steel in simplified non-radioactive solutions that simulate complex dilute radioactive waste solutions. These solutions contain corrosion-inducing species such as nitrate and chloride and the corrosion-inhibiting nitrite at moderately alkaline pHs. The electrochemical behavior of interest here is that of the open-circuit potential of the steel specimen at equilibrium in the experimental electrolyte and the measures of the steel''s passivity and passivity breakdown.'

  2. Corrosion Resistance and Pitting Behaviour of Low-Carbon High-Mn Steels in Chloride Solution

    Directory of Open Access Journals (Sweden)

    Grajcar A.

    2016-06-01

    Full Text Available Corrosion resistance of the X4MnSiAlNbTi27-4-2 and X6MnSiAlNbTi26-3-3 type austenitic steels, after hot deformation as well as after cold rolling, were evaluated in 3.5% NaCl solution using potentiodynamic polarization tests. A type of nonmetallic inclusions and their pitting corrosion behaviour were investigated. Additionally, the effect of cold deformation on the corrosion resistance of high-Mn steels was studied. The SEM micrographs revealed that corrosion damage formed in both investigated steels is characterized by various shapes and an irregular distribution at the metallic matrix, independently on the steel state (thermomechanically treated or cold worked. Corrosion pits are generated both in grain interiors, grain boundaries and along the deformation bands. Moreover, corrosion damage is stronger in cold deformed steels in comparison to the thermomechanically treated specimens. EDS analysis revealed that corrosion pits preferentially nucleated on MnS and AlN inclusions or complex oxysulphides. The morphology of corrosion damage in 3.5% NaCl supports the data registered in potentiodynamic tests.

  3. Correlation between evolution of inclusions and pitting corrosion in 304 stainless steel with yttrium addition.

    Science.gov (United States)

    Shi, Weining; Yang, Shufeng; Li, Jingshe

    2018-03-19

    Effects of the evolution of inclusions on the pitting corrosion resistance of 304 stainless steel with different contents of the rare-earth element yttrium (Y) were studied using thermodynamic calculations, accelerated immersion tests, and electrochemical measurements. The experimental results showed that regular Y 2 O 3 inclusions demonstrated the best pitting resistance, followed in sequence by (Al,Mn)O inclusions, the composite inclusions, and irregular Y 2 O 3 inclusions. The pitting resistance first decreased, then increased, and then decreased again with increasing Y content, because sulfide inclusions were easily generated when the Y content was low and YN inclusions were easily generated at higher Y contents. The best pitting corrosion resistance was obtained for 304 stainless steel with addition of 0.019% Y.

  4. Role of heat tint on pitting corrosion of 304 austenitic stainless steel in chloride environment

    Energy Technology Data Exchange (ETDEWEB)

    Elshawesh, F.; Elhoud, A. [Petroleum Research Center, P. O. Box 6431, Tripoli (Libyan Arab Jamahiriya)

    2004-07-01

    The effect of simulated heat tint produced by air oxidation at a wide range of temperatures 200, 400, 600, 800 and 1050 deg. C on pitting potential of 304 austenitic stainless steel was studied in environment of different chloride concentration. It was found that the heat tint effect depends on the heating temperature. The most effective heat tint was that produced at the high temperature up to 1050 deg. C and hence less pitting potential and low corrosion resistance. In order to improve the surface pitting corrosion resistance, acid pickling of hydrochloric acid was applied at different time and temperatures of 15 and 60 min, room temperature and 60 deg. C, respectively. Improvement in pitting potential was achieved as the pickling time and temperature increase. This is can be attributed to the removal of depleted chromium oxide film produced during the heat tint. (authors)

  5. Evidence of the pitting corrosion induced embrittlement of the structural steel SAE 8620

    International Nuclear Information System (INIS)

    Atanazio Filho, Nelson do Nascimento; Mansur, Tanius Rodrigues; Rabello, Emerson Giovani

    2007-01-01

    The influence of an aggressive environment (NaCl 3.5% aerated solution) on fatigue crack initiation and crack growth behavior were studied. This study comprised corrosion fatigue tests using specimens of SAE 8620 steel. The decreasing cyclic frequency (60 Hz to 11.7 Hz) effect on corrosion fatigue crack initiation behavior was examined. The tests carried out under rotating-bending loading conditions at 11.7 Hz (700 rpm), showed that pitting corrosion caused by anodic attack was responsible for corrosion fatigue crack initiation (author)

  6. Pitting corrosion in austenitic stainless steel water tanks of hotel trains

    International Nuclear Information System (INIS)

    Moreno, D. A.; Garcia, A. M.; Ranninger, C.; Molina, B.

    2011-01-01

    The water storage tanks of hotel trains suffered pitting corrosion. To identify the cause, the tanks were subjected to a detailed metallographic study and the chemical composition of the austenitic stainless steels used in their construction was determined. Both the tank water and the corrosion products were further examined by physicochemical and microbiological testing. Corrosion was shown to be related to an incompatibility between the chloride content of the water and the base and filler metals of the tanks. These findings formed the basis of recommendations aimed at the prevention and control of corrosion in such tanks. (Author) 18 refs.

  7. Microstructure and pitting corrosion of friction stir welded joints in 2219-O aluminum alloy thick plate

    International Nuclear Information System (INIS)

    Xu Weifeng; Liu Jinhe

    2009-01-01

    Effect of welding parameters on the microstructure and pitting corrosion of different positions along the thickness of weld nugget zone in friction stir welded 2219-O aluminum alloy plate was investigated using scanning electron microscopy (SEM), polarization experiment and electrochemical impedance tests (EIS). It was found that the material presents significant passivation and the top has best corrosion resistance compared to the bottom and base material. Corrosion resistance decreases with the increase of traverse speed from 60 to 100 mm/min at rotary speed 400 rpm. Corrosion resistance at rotary speed 600 rpm is lower than that at 500 rpm.

  8. Studies in pitting corrosion on archaeological bronzes. Copper

    International Nuclear Information System (INIS)

    Bresle, Aa.; Saers, J.; Arrhenius, B.

    1983-01-01

    Copper has been proposed as a canister material for use in the long-term storage of radioactive waste from nuclear power reactors. The storage period has been set to at least 100 000 years, during which time the copper cylinders must remain intact so that the contained waste has no possibility of leaking out. In this work, the pitting factor in archaelogical copper objects have been determined. The absolute values of the pitting factor obtained are generally very low. In the case of the most thoroughly studied material the pitting factor is only slightly more than three units. Nor does the native copper, with a presumed burial period of about 8000 years, exhibit particularly high values. In summary, it can therefore be concluded that the present study does not provide support for the assumption of extremely high pitting factors in copper-base material that has been buried for periods of several millenia. (G.B.)

  9. Influence of microstructure and elemental partitioning on pitting corrosion resistance of duplex stainless steel welding joints

    Science.gov (United States)

    Zhang, Zhiqiang; Jing, Hongyang; Xu, Lianyong; Han, Yongdian; Zhao, Lei; Zhang, Jianli

    2017-02-01

    The influences of microstructure and elemental partitioning on pitting corrosion resistance of duplex stainless steel joints welded by gas tungsten arc welding (GTAW) and flux-cored arc welding (FCAW) with different shielding gas compositions were studied by optical microscopy, electron backscatter diffraction, scanning electron microscopy, transmission electron microscopy, energy dispersive spectroscopy, electron probe microanalysis, and potentiostatic and potentiodynamic polarization methods The adding 2% N2 in shielding gas facilitated primary austenite formation in GTAW weld metal (WM) and suppressed Cr2N precipitation in GTAW weld root. In the HAZ, the banded microstructure disappeared while the coarse ferrite grains maintained same orientation as the banded ferrite in the BM. In the WM, the ferrite had one single orientation throughout a grain, whereas several families of austenite appeared. The austenite both in BM and WM enriched in Ni and nitro`gen, while Cr and Mo were concentrated in the ferrite and thus no element showed clear dendritic distribution in the WM (ER2209 and E2209T1). In addition, the secondary austenite had higher Ni content but lower Cr and Mo content than the primary austenite. The N2-supplemented shielding gas promoted nitrogen solid-solution in the primary and secondary austenite. Furthermore, the secondary austenite had relatively lower pitting resistance equivalent number (PREN) than the ferrite and primary austenite, thereby resulting in its preferential corrosion. The Cr2N precipitation led to relatively poor resistance to pitting corrosion in three HAZs and pure Ar shielding GTAW weld root. The N2-supplemented shielding gas improved pitting corrosion resistance of GTAW joint by increasing PREN of secondary austenite and suppressing Cr2N precipitation. In addition, the FCAW WM had much poorer resistance to pitting corrosion than the GTAW WM due to many O-Ti-Si-Mn inclusions. In the BM, since the austenite with lower PREN compared

  10. The effect of precipitated carbides on the pitting corrosion of 304 stainless steel

    International Nuclear Information System (INIS)

    Kwak, Jai-Hyun; Kim, Kwan-Hun

    1985-01-01

    In order to investigate the relation between the pitting corrosion and precipitated carbides, the heat treatment of specimens was carried out in two ways: Solution treatment and carbides precipitation treatment. The experiment was focused on the polarization curves of specimens immersed in HCL solution and on the microscopic analysis of the corroded specimens through a potentiodynamic method. It was found out that the intergranular and pitting corrosion occurred remarkably in 0.1N and 1N KCL solution when carbides were precipitated around the grain boundary of the 304 stain steel. The intergranular corrosion was noticed in the region of passivation and the pitting was prominent in the region of passivation break-down. The distribution of pits on the solution treated 304 stainless steel was random, while that of pits on carbides precipitated specimen was concentrated around the grain boundary in 0.1N and 1N HCL solution. It was ascertained that the pitting resistance of the solution treated 304 stainless steel was better than that of carbides precipitated specimen. (Author)

  11. Near-field microwave detection of corrosion precursor pitting under thin dielectric coatings in metallic substrate

    International Nuclear Information System (INIS)

    Hughes, D.; Zoughi, R.; Austin, R.; Wood, N.; Engelbart, R.

    2003-01-01

    Detection of corrosion precursor pitting on metallic surfaces under various coatings and on bare metal is of keen interest in evaluation of aircraft fuselage. Near-field microwave nondestructive testing methods, utilizing open-ended rectangular waveguides and coaxial probes, have been used extensively for detection of surface flaws in metals, both on bare metal and under a dielectric coating. This paper presents the preliminary results of using microwave techniques to detect corrosion precursor pitting under paint and primer, applique and on bare metal. Machined pits of 500 μm diameter were detected using open-ended rectangular waveguides at V-Band under paint and primer and applique, and on bare metal. Using coaxial probes, machined pits with diameters down to 150 μm on bare metal were also detected. Relative pit size and density were shown on a corrosion-pitted sample using open-ended rectangular waveguides at frequencies of 35 GHz to 70 GHz. The use of Boeing's MAUS TM scanning systems provided improved results by alleviating standoff variation and scanning artifact. Typical results of this investigation are also presented

  12. Pitting corrosion susceptibility study of zirconium alloys in the presence of the chloride ions

    International Nuclear Information System (INIS)

    Radulescu, M.; Pirvan, I.; Velciu, L.

    1997-01-01

    Pitting corrosion mechanism is specific to metal/aggressive environment systems. The influence of both components of the process was thoroughly investigated. After reviewing the principal steps of the pitting corrosion and of the electrochemical reactions associated, there were presented the physico-chemical methods used for the determination of the corrosion pitting parameters completed with the metallographic techniques of investigation of the attacked surfaces. Reported are the results of determinations of the pit initiation (E np ) and pit passivation (E pp ) potentials in the systems Zy-4 (Zr)/ Cl - provided from the following solutions: HCl, FeCl 3 , NaCl and LiCl. In the case of the last two solutions, the measurements were carried out also in the range of alkaline pH values. It was also determined the dependence of E np and E pp potential on the Cl - ions concentration in NaCl and HCl solutions, and also the reaction order 'n' in presence of several chloride concentration. Finally, on the basis of the experimental data, we established the kinetic characteristics specific to different steps of pitting. (authors)

  13. Spatial statistics of pitting corrosion patterning: Quadrat counts and the non-homogeneous Poisson process

    International Nuclear Information System (INIS)

    Lopez de la Cruz, J.; Gutierrez, M.A.

    2008-01-01

    This paper presents a stochastic analysis of spatial point patterns as effect of localized pitting corrosion. The Quadrat Counts method is studied with two empirical pit patterns. The results are dependent on the quadrat size and bias is introduced when empty quadrats are accounted for the analysis. The spatially inhomogeneous Poisson process is used to improve the performance of the Quadrat Counts method. The latter combines Quadrat Counts with distance-based statistics in the analysis of pit patterns. The Inter-Event and the Nearest-Neighbour statistics are here implemented in order to compare their results. Further, the treatment of patterns in irregular domains is discussed

  14. Pitting corrosion and structural reliability of corroding RC structures: Experimental data and probabilistic analysis

    International Nuclear Information System (INIS)

    Stewart, Mark G.; Al-Harthy, Ali

    2008-01-01

    A stochastic analysis is developed to assess the temporal and spatial variability of pitting corrosion on the reliability of corroding reinforced concrete (RC) structures. The structure considered herein is a singly reinforced RC beam with Y16 or Y27 reinforcing bars. Experimental data obtained from corrosion tests are used to characterise the probability distribution of pit depth. The RC beam is discretised into a series of small elements and maximum pit depths are generated for each reinforcing steel bar in each element. The loss of cross-sectional area, reduction in yield strength and reduction in flexural resistance are then inferred. The analysis considers various member spans, loading ratios, bar diameters and numbers of bars in a given cross-section, and moment diagrams. It was found that the maximum corrosion loss in a reinforcing bar conditional on beam collapse was no more than 16%. The probabilities of failure considering spatial variability of pitting corrosion were up to 200% higher than probabilities of failure obtained from a non-spatial analysis after 50 years of corrosion. This shows the importance of considering spatial variability in a structural reliability analysis for deteriorating structures, particularly for corroding RC beams in flexure

  15. Effect of Equal-Channel Angular Pressing on Pitting Corrosion of Pure Aluminum

    Directory of Open Access Journals (Sweden)

    Injoon Son

    2012-01-01

    Full Text Available The effect of equal-channel angular pressing (ECAP on the pitting corrosion of pure Al was investigated using electrochemical techniques in solutions containing 0.1 m mol·dm−3 of Na2SO4 and 8.46 mol·dm−3 of NaCl (300 ppm Cl− and followed by surface analysis. The potential for pitting corrosion of pure Al was clearly shifted in the noble direction by the ECAP process indicating that this process improves resistance to pitting corrosion. The time dependence of corrosion potential and the anodic potential at 1 A·m−2 revealed that the rate of formation of Al oxide films increased due to a decrease in the grain size of the Al after ECAP. Since there exists a negligible amount of impurity precipitates in pure Al, the improvement in pitting corrosion resistance of pure Al by ECAP appears to be attributable to an increase in the rate of formation of Al oxide films.

  16. Analysis on the stress corrosion crack inception based on pit shape and size of the FV520B tensile specimen

    Science.gov (United States)

    Xiang, Longhao; Pan, Juyi; Chen, Songying

    2018-06-01

    The influence of pit shape and size on local stress concentration in the tensile specimen and the stress corrosion cracks inception was studied by employing the element remove technique. The maximum stress located in the bottom of pit on FV520B tensile specimen. The location of maximum strain was near the mouth of the pit or the shoulder and plastic strain existed in this region. Stress concentration factor and plastic deformation on four different geometrical shape pits of hemisphere, semi-ellipsoid, bullet and butterfly were numerically investigated, respectively. The simulation results showed that butterfly pit got the biggest stress concentration factor. The plastic strain rate during pit growth was in the sensitivity range of stress corrosion cracks inception, indicating that stress corrosion cracks were more likely to nucleate near the pit tip or the shoulder.

  17. A Statistical Study on the Effect of Hydrostatic Pressure on Metastable Pitting Corrosion of X70 Pipeline Steel.

    Science.gov (United States)

    Yang, Zixuan; Kan, Bo; Li, Jinxu; Qiao, Lijie; Volinsky, Alex A; Su, Yanjing

    2017-11-14

    Hydrostatic pressure effects on pitting initiation and propagation in X70 steel are investigated by evaluating metastable pitting probability using electrochemical methods and immersion corrosion tests in containing chlorine ion solution. Potentiodynamic tests indicated that hydrostatic pressure can decrease the breakdown potential and lead to a reduced transpassivity region. Metastable test results revealed that hydrostatic pressure can increase metastable pitting formation frequency and promote stabilization of metastable pitting growth. Electrochemical impedance spectroscopy (EIS) results indicate that Hydrostatic pressure decreases the charge transfer resistance and increases the dissolution rate within the cavities. Corrosion test results also indicated that pitting initiation and propagation are accelerated by hydrostatic pressure. Result validity was verified by evaluating metastable pitting to predict pitting corrosion resistance.

  18. A generic statistical methodology to predict the maximum pit depth of a localized corrosion process

    International Nuclear Information System (INIS)

    Jarrah, A.; Bigerelle, M.; Guillemot, G.; Najjar, D.; Iost, A.; Nianga, J.-M.

    2011-01-01

    Highlights: → We propose a methodology to predict the maximum pit depth in a corrosion process. → Generalized Lambda Distribution and the Computer Based Bootstrap Method are combined. → GLD fit a large variety of distributions both in their central and tail regions. → Minimum thickness preventing perforation can be estimated with a safety margin. → Considering its applications, this new approach can help to size industrial pieces. - Abstract: This paper outlines a new methodology to predict accurately the maximum pit depth related to a localized corrosion process. It combines two statistical methods: the Generalized Lambda Distribution (GLD), to determine a model of distribution fitting with the experimental frequency distribution of depths, and the Computer Based Bootstrap Method (CBBM), to generate simulated distributions equivalent to the experimental one. In comparison with conventionally established statistical methods that are restricted to the use of inferred distributions constrained by specific mathematical assumptions, the major advantage of the methodology presented in this paper is that both the GLD and the CBBM enable a statistical treatment of the experimental data without making any preconceived choice neither on the unknown theoretical parent underlying distribution of pit depth which characterizes the global corrosion phenomenon nor on the unknown associated theoretical extreme value distribution which characterizes the deepest pits. Considering an experimental distribution of depths of pits produced on an aluminium sample, estimations of maximum pit depth using a GLD model are compared to similar estimations based on usual Gumbel and Generalized Extreme Value (GEV) methods proposed in the corrosion engineering literature. The GLD approach is shown having smaller bias and dispersion in the estimation of the maximum pit depth than the Gumbel approach both for its realization and mean. This leads to comparing the GLD approach to the GEV one

  19. Crack Initiation and Growth Behavior at Corrosion Pit in 2024-T3 Aluminum Alloy

    Science.gov (United States)

    2014-09-01

    concepts of fracture mechanics. Corrosion crack initiation or growth can develop when exposed to continuous or intermittent humid environment during...act as nucleation sites. For many materials of the structure such as Al, steel the growth of fatigue cracks from corrosion pit stands legitimate...critical or rather threshold values below which the nucleation of fatigue crack is not possible [6]. Under certain conditions that prevail on

  20. Review and Study of Physics Driven Pitting Corrosion Modeling in 2024-T3 Aluminum Alloys (Postprint)

    Science.gov (United States)

    2015-05-01

    aluminum subjected to pitting corrosion under fatigue conditions ”, Journal of Aircraft, Vol. 46, No. 4, pp. 1253-1259 Wei, R.P. (2001) “A model for...and material microstructure applied to corrosion and fatigue of aluminum and steel alloys”, Engineering Fracture Mechanics , Vol. 76, pp. 695-708 Wei...Fatigue Behavior of Aluminum Alloy 7075 -T6: Modeling and Experimental Studies", Materials Science and Engineering: A, vol. 297, Issue: 1-2, 15, pp. 223

  1. IMPACT OF WATER CHEMISTRY ON LOCALIZED CORROSION OF COPPER PITTING

    Science.gov (United States)

    This project will help identify what waters are problematic in causing the corrosion of copper pipes and improve understanding of how water distribution leads to corrosion. This project will also focus on the prevention of pinhole leaks and how to reverse them once they occur. ...

  2. A preliminary investigation of the initiation of pitting corrosion in austenitic stainless steels and nickel-based alloys

    International Nuclear Information System (INIS)

    Higginson, A.

    1984-01-01

    Pitting corrosion in a number of austenitic stainless steels and nickel-based alloys that differ widely in their resistance to corrosion was studed by electrochemical and electron-optical techniques. The effect of contamination of the sulphuric acid electrolyte by chloride ions was also investigated. Preliminary results for the surface analysis of samples of 316 stainless steel by Auger electron spectroscopy are presented, and suggestions are included for further application of this technique to the examination of pitting corrosion. A comprehensive review of the literature concerning the initiation of pitting corrosion is included

  3. Corrosion inhibition by lithium zinc phosphate pigment

    International Nuclear Information System (INIS)

    Alibakhshi, E.; Ghasemi, E.; Mahdavian, M.

    2013-01-01

    Highlights: •Synthesis of lithium zinc phosphate (LZP) by chemical co-precipitation method. •Corrosion inhibition activity of pigments compare with zinc phosphate (ZP). •LZP showed superior corrosion inhibition effect in EIS measurements. •Evaluation of adhesion strength and dispersion stability. -- Abstract: Lithium zinc phosphate (LZP) has been synthesized through a co-precipitation process and characterized by XRD and IR spectroscopy. The inhibitive performances of this pigment for corrosion of mild steel have been discussed in comparison with the zinc phosphate (ZP) in the pigment extract solution by means of EIS and in the epoxy coating by means of salt spray. The EIS and salt spray results revealed the superior corrosion inhibitive effect of LZP compared to ZP. Moreover, adhesion strength and dispersion stability of the pigmented epoxy coating showed the advantage of LZP compared to ZP

  4. Electrochemical study of corrosion inhibition of stainless steel in phosphoric medium

    Energy Technology Data Exchange (ETDEWEB)

    Hnini, K.; Chtaini, A. [Laboratoire d' Electrochimie et de Bio Corrosion, Faculte des Sciences et Techniques, Beni-Mellal (Morocco); Khouili, M.; Elbouadili, A. [Laboratoire de Chimie Organique et Analytique, Faculte des Sciences et Techniques, Beni-Mellal (Morocco)

    2004-07-01

    The corrosion of metals represents a terrible waste of both natural resources and money, the failure of some stainless steel resulting from pitting corrosion is some times considered a technological problem, consequently, much effort has been expended in attempting to understand and overcome the corrosion therefore, many stainless steel/ environment combinations have been studied. The use of heterocyclic compounds as inhibitors is one of the most practical methods for protection against corrosion in acidic media. In continuation of our work on development of macrocyclic compounds as corrosion inhibitors we report in our study the corrosion inhibiting behaviour of organic compound Methoxy-2-Allyl-4 Phenol (MAP) containing coordinating and conjugation groups, at three forms (natural, polymerized and chemically treated) on the corrosion of stainless steel in phosphoric acid. This study focused on the comparison for corrosion inhibition proprieties of these different applications using potentiodynamic polarization, electrochemical impedance spectroscopy and SEM. The specimen was evaluated to determine change in his corrosion potential and resistance polarization; These MAP products have exhibited corrosion inhibition by maintaining a high resistance polarization (low corrosion rate) in each application. These results reveal that this compound is efficient inhibitor in all forms; the most inhibition efficiency is obtained with polymerized form. To further evaluate the test data, the steel surfaces were analyzed using scanning electron microscopy, SEM observations of surface treated concrete confirmed presence of inhibitor on the steel surfaces. (authors)

  5. The kinetics of pitting corrosion of carbon steel

    International Nuclear Information System (INIS)

    Marsh, G.P.; Taylor, K.J.; Sooi, Z.

    1988-02-01

    The development of an improved statistical method for analysing pit growth data to take account of the difference in area of laboratory specimens and full sized high level nuclear waste containers is described. Statistical analysis of data from pit growth experiments with large area (460 cm 2 ) plates of BS 4360 steel have indicated that the depth distributions correlate most closely with a limited distribution function. This correlation implies that previous statistical analyses to estimate the maximum pit depths in full size containers, which were made using unlimited distribution functions, will be pessimistic. An evaluation of the maximum feasible pitting period based on estimating the period during which the oxygen diffusion flux is sufficient to stabilise a passive film on carbon steel containers has indicated that this is of the order of 125 years rather than the full 1000 year container life. The estimate is sensitive to the value of the leakage current assumed to flow through the passive film, and therefore work is planned to measure this accurately in relevant granitic environments. (author)

  6. Scanning Probe Investigation of Pitting Corrosion on Aluminum 5083 H131

    Science.gov (United States)

    2014-05-01

    245–254. 10. Dolic, N.; Malina, J.; Begic Hadzipasic, A. Pit Nucleation on As-Cast Aluminum Alloy AW-5083 in 0.01M NaCl. Journal of Mining and...R. A.; Stratmann, M. Application of a Kelvin Microprobe to the Corrosion in Humid Atmospheres. J. Electrochem Soc. 1991, 138 (1), 55–61. 15

  7. Pitting Corrosion of Copper in Waters with High pH and Low Alkalinity

    Science.gov (United States)

    Localized or pitting corrosion of copper pipes used in household drinking-water plumbing is a problem for many water utilities and their customers. Extreme attack can lead to pinhole water leaks that may result in water damage, mold growth, and costly repairs. Water quality has b...

  8. Tungsten ion implantation of aluminum for improved resistance to pitting corrosion -- electrochemical testing results

    International Nuclear Information System (INIS)

    Smith, P.P.; Buchanan, R.A.; Williams, J.M.

    1995-01-01

    The greatly accelerated localized corrosion of aluminum in salt solutions has been observed and combated for many years. The susceptibility to pitting attack has been linked to the presence of chloride ions in the solution. Alloying additions to aluminum for improved corrosion resistance are restricted due to its limited solubility for passivating species such as chromium and molybdenum. However, many recent attempts to produce non-equilibrium alloys with these and other species, both through sputtering techniques and by rapid solidification, have met with very promising pitting resistance enhancements. The most dramatic increase in passivity is demonstrated by a thin co-sputtered film of Al and 9 atomic percent W, in which the pitting potential is increased by 2600 m V relative to pure Al. Recent efforts to extrapolate the promising W-Al thin film results to a bulk aluminum alloy using tungsten ion implantation are discussed here

  9. Effects of heat input on pitting corrosion in super duplex stainless steel weld metals

    Science.gov (United States)

    Shin, Yong taek; Shin, Hak soo; Lee, Hae woo

    2012-12-01

    Due to the difference in reheating effects depending on the heat input of subsequent weld passes, the microstructure of the weld metal varies between acicular type austenite and a mixture of polygonal type and grain boundary mixed austenite. These microstructural changes may affect the corrosion properties of duplex stainless steel welds. This result indicates that the pitting resistance of the weld can be strongly influenced by the morphology of the secondary austenite phase. In particular, the ferrite phase adjacent to the acicular type austenite phase shows a lower Pitting Resistance Equivalent (PRE) value of 25.3, due to its lower chromium and molybdenum contents, whereas the secondary austenite phase maintains a higher PRE value of more than 38. Therefore, it can be inferred that the pitting corrosion is mainly due to the formation of ferrite phase with a much lower PRE value.

  10. Inhibition of the Cu65/Zn35 brass corrosion by natural extract of Camellia sinensis

    International Nuclear Information System (INIS)

    Ramde, Tambi; Rossi, Stefano; Zanella, Caterina

    2014-01-01

    In this work, the corrosion inhibition of brass was studied using natural plant extract, Camellia sinensis, in 0.1 M Na2SO4 solutions with pH 7 and pH 4. Electrochemical techniques (potentiodynamic polarization, electrochemical impedance spectroscopy) and scanning electron microscopy (SEM) were applied to study the brass corrosion behavior in presence and absence of the extract. The results indicated that the extract is a very effective corrosion inhibitor for brass corrosion process in both the acidic and neutral media by virtue of adsorption. The inhibition effect increases by time as demonstrated by the EIS monitoring for 120 h. In the blank solution the corrosion process leads to the formation of a dark oxide patina at pH 7 and induces localized corrosion morphology at pH 4. The extract presence can avoid both the dark patina and the pits formation.

  11. Inhibition of the Cu65/Zn35 brass corrosion by natural extract of Camellia sinensis

    Energy Technology Data Exchange (ETDEWEB)

    Ramde, Tambi, E-mail: t_ramde@univ-ouaga.bf [Equipe Chimie Physique et Electrochimie, Laboratoire de Chimie Moléculaire et des Matériaux, Université de Ouagadougou, 03 BP 7021 Ouagadougou 03 (Burkina Faso); Department of Industrial Engineering, University of Trento, via Sommarive 9, 38123 Trento (Italy); Rossi, Stefano; Zanella, Caterina [Department of Industrial Engineering, University of Trento, via Sommarive 9, 38123 Trento (Italy)

    2014-07-01

    In this work, the corrosion inhibition of brass was studied using natural plant extract, Camellia sinensis, in 0.1 M Na2SO4 solutions with pH 7 and pH 4. Electrochemical techniques (potentiodynamic polarization, electrochemical impedance spectroscopy) and scanning electron microscopy (SEM) were applied to study the brass corrosion behavior in presence and absence of the extract. The results indicated that the extract is a very effective corrosion inhibitor for brass corrosion process in both the acidic and neutral media by virtue of adsorption. The inhibition effect increases by time as demonstrated by the EIS monitoring for 120 h. In the blank solution the corrosion process leads to the formation of a dark oxide patina at pH 7 and induces localized corrosion morphology at pH 4. The extract presence can avoid both the dark patina and the pits formation.

  12. Exfoliation Corrosion and Pitting Corrosion and Their Role in Fatigue Predictive Modeling: State-of-the-Art Review

    Directory of Open Access Journals (Sweden)

    David W. Hoeppner

    2012-01-01

    Full Text Available Intergranular attack (IG and exfoliation corrosion (EC have a detrimental impact on the structural integrity of aircraft structures of all types. Understanding the mechanisms and methods for dealing with these processes and with corrosion in general has been and is critical to the safety of critical components of aircraft. Discussion of cases where IG attack and exfoliation caused issues in structural integrity in aircraft in operational fleets is presented herein along with a much more detailed presentation of the issues involved in dealing with corrosion of aircraft. Issues of corrosion and fatigue related to the structural integrity of aging aircraft are introduced herein. Mechanisms of pitting nucleation are discussed which include adsorption-induced, ion migration-penetration, and chemicomechanical film breakdown theories. In addition, pitting corrosion (PC fatigue models are presented as well as a critical assessment of their application to aircraft structures and materials. Finally environmental effects on short crack behavior of materials are discussed, and a compilation of definitions related to corrosion and fatigue are presented.

  13. ANALYSIS OF PITTING CORROSION ON AN INCONEL 718 ALLOY SUBMITTED TO AGING HEAT TREATMENT

    Directory of Open Access Journals (Sweden)

    Felipe Rocha Caliari

    2014-10-01

    Full Text Available Inconel 718 is one of the most important superalloys, and it is mainly used in the aerospace field on account of its high mechanical strength, good resistance to fatigue and creep, good corrosion resistance and ability to operate continuously at elevated temperatures. In this work the resistance to pitting corrosion of a superalloy, Inconel 718, is analyzed before and after double aging heat treatment. The used heat treatment increases the creep resistance of the alloy, which usually is used up to 0.6 Tm. Samples were subjected to pitting corrosion tests in chloride-containing aqueous solution, according to ASTM-F746-04 and the procedure described by Yashiro et al. The results of these trials show that after heat treatment the superalloy presents higher corrosion resistance, i.e., the pitting corrosion currents of the as received surfaces are about 6 (six times bigger (~0.15 mA than those of double aged surfaces (~0.025 mA.

  14. Pitting corrosion resistance of high alloy OCTG in ferric chloride solution

    International Nuclear Information System (INIS)

    Masamura, K.; Yamamoto, S.; Matsushima, I.

    1986-01-01

    The effects of alloying elements and precipitated phases on the corrosion rate of high alloy OCTG in the ferric chloride solution have been evaluated. The corrosion rate of Fe-Cr-Ni-Mo alloys without precipitated phases, e.g. carbides and sigma phase, can be estimated from the composition using the following equation: log(C.R.)=-0.144xPRE-7690/(273+T)+28.6 where C.R. is the corrosion rate in g/m/sup 2//hr; PRE is Cr+3Mo+16N in percent and T is the test temperature in 0 C. The activation energies of the ferric chloride test are almost the same regardless of PRE or Ni content when no detrimental phase precipitates. When carbides or the sigma phase precipitate, the corrosion rate is higher and the activation energy is lowered. This suggests that secondary phases give preferential sites for initiation of pitting corrosion

  15. Evaluation of aluminum pit corrosion in oak ridge research reactor pool by quantitative imaging and thermodynamic modeling

    International Nuclear Information System (INIS)

    Jang, Ping-Rey; Arunkumar, Rangaswami; Lindner, Jeffrey S.; Long, Zhiling; Mott, Melissa A.; Okhuysen, Walter P.; Monts, David L.; Su, Yi; Kirk, Paula G.; Ettien, John

    2007-01-01

    The Oak Ridge Research Reactor (ORRR) was operated as an isotope production and irradiation facility from March 1958 until March 1987. The US Department of Energy permanently shut down and removed the fuel from the ORRR in 1987. The water level must be maintained in the ORRR pool as shielding for radioactive components still located in the pool. The U.S. Department of Energy's Office of Environmental Management (DOE EM) needs to decontaminate and demolish the ORRR as part of the Oak Ridge cleanup program. In February 2004, increased pit corrosion was noted in the pool's 6 mm (1/4'')-thick aluminum liner in the section nearest where the radioactive components are stored. If pit corrosion has significantly penetrated the aluminum liner, then DOE EM must accelerate its decontaminating and decommissioning (D and D) efforts or look for alternatives for shielding the irradiated components. The goal of Mississippi State University's Institute for Clean Energy Technology (ICET) was to provide a determination of the extent and depth of corrosion and to conduct thermodynamic modeling to determine how further corrosion can be inhibited. Results from the work will facilitate ORNL in making reliable disposition decisions. ICET's inspection approach was to quantitatively estimate the amount of corrosion by using Fourier - transform profilometry (FTP). FTP is a non-contact 3- D shape measurement technique. By projecting a fringe pattern onto a target surface and observing its deformation due to surface irregularities from a different view angle, the system is capable of determining the height (depth) distribution of the target surface, thus reproducing the profile of the target accurately. ICET has previously demonstrated that its FTP system can quantitatively estimate the volume and depth of removed and residual material to high accuracy. The results of our successful initial deployment of a submergible FTP system into the ORRR pool are reported here as are initial thermodynamic

  16. Pitting corrosion protection of low nickel stainless steel

    Indian Academy of Sciences (India)

    The corrosion protective properties of PANi and PoPD coatings on LN SS in 0.5 M NaCl were evaluated using potentiodynamic polarization and electrochemical impedance spectroscopic (EIS) techniques. The potentiodynamic polarization and electrochemical impedance spectroscopic results indicate that the PoPD ...

  17. On the detection of corrosion pit interactions using two-dimensional spectral analysis

    International Nuclear Information System (INIS)

    Jarrah, Adil; Nianga, Jean-Marie; Iost, Alain; Guillemot, Gildas; Najjar, Denis

    2010-01-01

    A statistical methodology for detecting pits interactions based on a two-dimensional spectral analysis is presented. This method can be used as a tool for the exploratory analysis of spatial point patterns and can be advanced as an alternative of classical methods based on distance. One of the major advantages of the spectral analysis approach over the use of classical methods is its ability to reveal more details about the spatial structure like the scale for which pits corrosion can be considered as independent. Furthermore, directional components of pattern can be investigated. The method is validated in a first time using numerical simulations on random, regular and aggregated structures. The density of pits, used in the numerical simulations, corresponds to that assessed from a corroded aluminium sheet. In a second time, this method is applied to verify the independence of the corrosion pits observed on the aforementioned aluminium sheet before applying the Gumbel theory to determine the maximum pit depth. Indeed, the property of independence is a prerequisite of the Gumbel theory which is one of the most frequently used in the field of safety and reliability.

  18. Effects of rare earth metals addition on the resistance to pitting corrosion of super duplex stainless steel - Part 1

    International Nuclear Information System (INIS)

    Kim, Soon-Tae; Jeon, Soon-Hyeok; Lee, In-Sung; Park, Yong-Soo

    2010-01-01

    To elucidate the effects of rare earth metals addition on the resistance to pitting corrosion of super duplex stainless steel, a metallographic examination, potentiodynamic and potentiostatic polarization tests, a SEM-EDS and a SAM analysis of inclusion, austenite phase and ferrite phase were conducted. The addition of rare earth metals to the base alloy led to the formation of (Mn, Cr, Si, Al, Ce) oxides and (Mn, Cr, Si, Ce) oxides, which improved the resistance to pitting corrosion and caused a decrease in the preferential interface areas for the initiation of the pitting corrosion.

  19. Statistical study by digitalized image analysis of pitting corrosion of an AISI 304 type stainless steel in chloride environment

    International Nuclear Information System (INIS)

    Lacome, Isabelle

    1994-01-01

    This research thesis addresses the pitting corrosion of an AISI 304-type stainless steel in chloride environment, a phenomenon which is generally considered as comprising two main steps: pit initiation with local degradation of the passive film, and pit growth. By using a technique of analysis of digitalized images, the process is observed in situ and both steps are monitored. A statistical study of the initiation of all the noticed pits is performed. After a bibliographical survey on the pitting corrosion process, its mechanisms and the influence of different parameters, the author presents the studied material and the experimental methods, reports the investigation of the pitting corrosion process in potentiostatic mode over a wide range of potentials in order to study all the types of pits, discusses the influence of potential on pit initiation and growth, reports the study of the influence of hydrodynamic conditions and of ageing in solution on the different parameters, reports the analysis of passive films by photoelectron spectroscopy, and the study of the influence of an inhibitor (molybdate ions) on both steps of pitting corrosion [fr

  20. A point defect model for the general and pitting corrosion on iron-oxide-electrolyte interface deduced from current oscillations

    CERN Document Server

    Pagitsas, M; Sazou, D

    2003-01-01

    Analysis of the passive-active oscillatory region of the Fe-0.75 M H sub 2 SO sub 4 system, perturbed by adding small amounts of halide species, allow the distinction between pitting and general corrosion. Complex periodic and aperiodic current oscillations characterize pitting corrosion whereas monoperiodic oscillations of a relaxation type indicate general corrosion. A point defect model (PDM) is considered for the microscopic description of the growth and breakdown of the iron oxide film. The physicochemical processes leading to different types of corrosion can be clarified in terms of the PDM. Occupation of an anion vacancy by a halide ion results in the localized attack of the passive oxide and pitting corrosion. On the other hand, the formation of surface soluble iron complexes is related to the uniform dissolution of the passive oxide and general corrosion.

  1. A study on the initiation of pitting corrosion in carbon steel in chloride-containing media using scanning electrochemical probes

    International Nuclear Information System (INIS)

    Lin Bin; Hu Ronggang; Ye Chenqing; Li Yan; Lin Changjian

    2010-01-01

    Scanning electrochemical probes of corrosion potential and chloride ions were developed for the in situ monitoring of localized corrosion processes of reinforcing steel in NaCl-containing solution. The results indicated that the chloride ions (Cl - ) preferentially adsorbed and accumulated at the imperfect/defective sites, resulting in initiation and propagation of pitting corrosion on the reinforcing steel surface. An electron microprobe analyzer (EMPA) was used to examine the corrosion morphology and elemental distribution at the corroded location to investigate the origins of the preferential Cl - adsorption and pitting corrosion. By combining the in situ and ex situ images, we concluded that manganese sulfide inclusions in reinforcing steel are the most susceptible defects to pitting corrosion in chloride-containing solution.

  2. Pitting corrosion behaviour study of aluminium matrix composites (A3xx.x/SiCp)

    International Nuclear Information System (INIS)

    Pardo, A.; Merino, M. C.; Merino, S.; Lopez, M. D.; Viejo, F.; Carboneras, M.; Arrabal, R.

    2004-01-01

    The influence of the SiCp proportion on the pitting corrosion of A3xx.x/SiC/xxp composites was studies by means of potenciodinamic polarization and double cyclic polarization in saline environment at 25 degree centigrade A360/SiC/xxp matrix does not contain copper, whereas the A380/SiC/xxp matric contains 1,39-1,44 wt %Cu. The kinetic study was carried out by gravimetric measurements. The nature of corrosion products was analysed by low angle XRD and Scanning Electron Microscopy (SEM). The corrosion is due to nucleation and growth of Al 2 O 3 -3H 2 O on the material surface. The corrosion increases with the reinforcement proportion, chloride concentration and copper content. (Author) 10 refs

  3. The role of nitrogen in improving pitting corrosion resistance of high-alloy austenitic and duplex stainless steel welds

    International Nuclear Information System (INIS)

    Vilpas, M.; Haenninen, H.

    1999-01-01

    The effects of nitrogen alloyed shielding gas on weld nitrogen content and pitting corrosion resistance of super austenitic (6%Mo) and super duplex stainless steels have been studied with special emphasis on microsegregation behaviour of Cr, Mo and N. The measurements performed with the 6%Mo steel indicate that all these elements segregate interdendritically in the fully austenitic weld metal. With nitrogen addition to the shielding gas the enrichment of nitrogen to the interdendritic regions is more pronounced than to the dendrite cores due to which the pitting corrosion resistance of the dendrite cores increases only marginally. In the super duplex steel welds nitrogen enriches in austenite increasing its pitting corrosion resistance more effectively. In these welds the pitting corrosion resistance of the ferrite phase remains lower. (orig.)

  4. Crevice corrosion ampersand pitting of high-level waste containers: integration of deterministic ampersand probabilistic models

    International Nuclear Information System (INIS)

    Farmer, J.C.; McCright, R.D.

    1997-01-01

    A key component of the Engineered Barrier System (EBS) being designed for containment of spent-fuel and high-level waste at the proposed geological repository at Yucca Mountain, Nevada is a two-layer canister. In this particular design, the inner barrier is made of a corrosion resistant material (CRM) such as Alloy 625 or C-22, while the outer barrier is made of a corrosion-allowance material (CAM) such as carbon steel or Monel 400. An integrated predictive model is being developed to account for the effects of localized environmental conditions in the CRM-CAM crevice on the initiation and propagation of pits through the CRM

  5. CREVICE CORROSION and PITTING OF HIGH-LEVEL WASTE CONTAINERS: INTEGRATION OF DETERMINISTIC and PROBABILISTIC MODELS

    International Nuclear Information System (INIS)

    JOSEPH C. FARMER AND R. DANIEL MCCRIGHT

    1997-01-01

    A key component of the Engineered Barrier System (EBS) being designed for containment of spent-fuel and high-level waste at the proposed geological repository at Yucca Mountain, Nevada is a two-layer canister. In this particular design, the inner barrier is made of a corrosion resistant material (CRM) such as Alloy 625 or C-22, while the outer barrier is made of a corrosion-allowance material (CAM) such as carbon steel or Monel 400. An integrated predictive model is being developed to account for the effects of localized environmental conditions in the CRM-CAM crevice on the initiation and propagation of pits through the CRM

  6. Activation of aluminum as an effective reducing agent by pitting corrosion for wet-chemical synthesis.

    Science.gov (United States)

    Li, Wei; Cochell, Thomas; Manthiram, Arumugam

    2013-01-01

    Metallic aluminum (Al) is of interest as a reducing agent because of its low standard reduction potential. However, its surface is invariably covered with a dense aluminum oxide film, which prevents its effective use as a reducing agent in wet-chemical synthesis. Pitting corrosion, known as an undesired reaction destroying Al and is enhanced by anions such as F⁻, Cl⁻, and Br⁻ in aqueous solutions, is applied here for the first time to activate Al as a reducing agent for wet-chemical synthesis of a diverse array of metals and alloys. Specifically, we demonstrate the synthesis of highly dispersed palladium nanoparticles on carbon black with stabilizers and the intermetallic Cu₂Sb/C, which are promising candidates, respectively, for fuel cell catalysts and lithium-ion battery anodes. Atomic hydrogen, an intermediate during the pitting corrosion of Al in protonic solvents (e.g., water and ethylene glycol), is validated as the actual reducing agent.

  7. Uniform and pitting corrosion events induced by SCN- anions on Al alloys surfaces and the effect of UV light

    International Nuclear Information System (INIS)

    Amin, Mohammed A.

    2011-01-01

    The influence of the alloying elements on the uniform and pitting corrosion processes of Al-6061, Al-4.5%Cu, Al-7.5%Cu, Al-6%Si and Al-12%Si alloys was studied in 0.50 M KSCN solution at 25 o C. Open-circuit potential, Tafel polarization, linear polarization resistance (LPR) and ICP-AES measurements were used to study the uniform corrosion process on the surfaces of the tested alloys. Cyclic polarization, potentiostatic current-time transients and impedance techniques were employed for pitting corrosion studies. Obtained results were compared with pure Al. Passivation kinetics of the tested Al samples were also studied as a function of applied potential, [SCN - ] and sample composition by means of potentiostatic current transients. The induction time, after which the growth of stable pits occurs, decreased with increasing applied potential and [SCN - ]. Regarding to uniform corrosion, alloyed Cu was found to enhance the corrosion rate, while alloyed Si suppressed it. Alloying elements of the tested samples diminished pitting attack to an extent depending on the percentage of the alloying element in the sample. Among the investigated materials, Al-Si alloys exhibited the highest corrosion resistance towards uniform and pitting corrosion processes in KSCN solutions. The passive and dissolution behaviour of Al was also studied under the conditions of continuous illumination (300-450 nm) based on cyclic polarization and potentiostatic techniques. The incident photons had a little influence on pit initiation and a marked effect on pit growth. These explained in terms of a photo-induced modification of the passive film formed on the anode surface, which render it more resistant to pitting. The effects of UV photons energy and period of illumination on the morphology of the pitted surfaces were also studied.

  8. Pitting corrosion of 304 stainless steel in an activated carbon filter

    OpenAIRE

    Martins, J.I.; Martins, C.M.B.

    2016-01-01

    Water leakages of an orange color were found in the cross welding zone and barrel of an activated carbon filter used in a wastewater treatment plant. The analysis of the chloride content in the plant flowsheet showed that the equipment was subjected to unsuited chloride concentration for 304 stainless steel resistance to pitting corrosion. The inside shows holes distributed randomly from about 20 cm above the welding zone to the lower outlet port of the equipment. The rehabilitation of the eq...

  9. Microstructure and pitting corrosion of shielded metal arc welded high nitrogen stainless steel

    Directory of Open Access Journals (Sweden)

    Raffi Mohammed

    2015-09-01

    Full Text Available The present work is aimed at studying the microstructure and pitting corrosion behaviour of shielded metal arc welded high nitrogen steel made of Cromang-N electrode. Basis for selecting this electrode is to increase the solubility of nitrogen in weld metal due to high chromium and manganese content. Microscopic studies were carried out using optical microscopy (OM and field emission scanning electron microscopy (FESEM. Energy back scattered diffraction (EBSD method was used to determine the phase analysis, grain size and orientation image mapping. Potentio-dynamic polarization testing was carried out to study the pitting corrosion resistance in aerated 3.5% NaCl environment using a GillAC electrochemical system. The investigation results showed that the selected Cr–Mn–N type electrode resulted in a maximum reduction in delta-ferrite and improvement in pitting corrosion resistance of the weld zone was attributed to the coarse austenite grains owing to the reduction in active sites of the austenite/delta ferrite interface and the decrease in galvanic interaction between austenite and delta-ferrite.

  10. A stochastic analysis of the effect of hydrostatic pressure on the pit corrosion of Fe-20Cr alloy

    International Nuclear Information System (INIS)

    Zhang Tao; Yang Yange; Shao Yawei; Meng, Guozhe; Wang, Fuhui

    2009-01-01

    The effect of hydrostatic pressure on the pit corrosion behavior of Fe-20Cr alloy was investigated in 3.5% NaCl solution by means of potentiodynamic polarization and potentiostatic technology, and the experiment data was analyzed based on stochastic theory. With the increase of hydrostatic pressure, the pit corrosion resistance of Fe-20Cr alloy was deteriorated, which was distinguished by the decrease of critical pit potential (E cirt ) and the increase of passive current density. The results also demonstrated that there exist two effects of hydrostatic pressure on the corrosion behavior of Fe-20Cr alloy: (1) the pit generation rate was evidently increased compared to that under lower hydrostatic pressure, and the metastable pits become faster and larger. However, it seemed that pit generation mechanism shows no hydrostatic pressure dependence; (2) the probability of pit growth increased with the increase of hydrostatic pressure, which implied that the metastable pit on Fe-20Cr alloy exhibited higher probability to become larger pit cavity during shorter time interval than that under lower hydrostatic pressure.

  11. Pitting Corrosion of the Resistance Welding Joints of Stainless Steel Ventilation Grille Operated in Swimming Pool Environment

    Directory of Open Access Journals (Sweden)

    Mirosław Szala

    2018-01-01

    Full Text Available This work focuses on the pitting corrosion of ventilation grilles operated in swimming pool environments. The ventilation grille was made by resistance welding of stainless steel rods. Based on the macroscopic and microscopic examinations, the mechanism of the pitting corrosion was confirmed. Chemical composition microanalysis of sediments as well as base metal using scanning electron microscopy and energy-dispersive spectroscopy (SEM-EDS method was carried out. The weldments did not meet the operating conditions of the swimming pool environment. The wear due to the pitting corrosion was identified in heat affected zones of stainless steel weldment and was more severe than the corrosion of base metal. The low quality finish of the joints and influence of the welding process on the weld metal microstructure lead to accelerated deposition of corrosion effecting elements such as chlorine.

  12. Corrosion Chemistry in Inhibited HDA.

    Science.gov (United States)

    1980-11-30

    which are likely to resemble authentic Modified HDA corrosion products, and reactions of a range of metal fluorides with difluorphosphoric acid have i...Introduction 10 (b) Solutions of HF in nitric acid and in HDA 10 (c) Solutions of PF5 in HDA 10 (d) Solutions of HPO 2 F2 in HDA 15 (e) Solutions of...of metals with HPO F in HDA 2 2 solution. 166 Iron. 166 Nickel. 166 (c) Reactions of metal fluorides with difluorophosphoric acid . 169 B-FeF 3.3H 2 0

  13. Effect of Adenine Concentration on the Corrosion Inhibition of Aisi ...

    African Journals Online (AJOL)

    This gave a surface coverage of 0.8956 and corrosion penetration rate of 0.022132mm/yr. Hence, the best adenine concentration for the corrosion inhibition of alloys 304L in 1.0M sulphuric acid solution to obtain optimum inhibition efficiency is 0.011M. Keywords: Corrosion, AISI 304L Steel, Inhibition efficiency, Degree of ...

  14. Pitting and Stress Corrosion Cracking Susceptibility of Nanostructured Al-Mg Alloys in Natural and Artificial Environments

    Science.gov (United States)

    Sharma, Mala M.; Ziemian, Constance W.

    2008-12-01

    The stress corrosion cracking (SCC) behavior of two developmental nanocrystalline 5083 alloys with varied composition and processing conditions was studied. The results were compared to a commercial aluminum AA 5083 (H111) alloy. The pitting densities, size and depths, and residual tensile strengths were measured after alternate immersion in artificial seawater and atmospheric exposure under different loading conditions. Optical and scanning electron microscopy (SEM) with EDX was used to analyze the fracture surfaces of failed specimen after removal at selected intervals and tensile testing. One of the nanostructured Al-Mg alloys exhibited significantly superior pitting resistance when compared to conventional microstructured AA 5083. Under conditions where pitting corrosion showed up as local tunnels toward phase inclusions, transgranular cracking was observed, whereas under conditions when pitting corrosion evolved along grain boundaries, intergranular cracking inside the pit was observed. Pit initiation resistance of the nano alloys appears to be better than that of the conventional alloys. However, long-term pit propagation is a concern and warrants further study. The objective of this investigation was to obtain information regarding the role that ultra-fine microstructures play in their degradation in marine environments and to provide insight into the corrosion mechanisms and damage processes of these alloys.

  15. A Study on Microstructure Change and Pitting Corrosion Resistance of Ferritic Stainless Steel Weldment According to Nb Contents

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jong-Min; Shin, Yong-Taek; Lee, Sang-Hwa; Lee, Jun-Hee; Lee, Hae-Woo [Dong-A University, Busan (Korea, Republic of); Lee, Sung-Riong [Kangwon National University, ChunCheon (Korea, Republic of); Kim, Soon-Ho [Silla University, Busan (Korea, Republic of)

    2014-01-15

    This paper identified the effects of Nb on microstructure. Also, it has studied on uniform and pitting corrosion resistance in a ferritic stainless steel weld metal of the automobile exhaust system. We fabricated 3 flux cored wires designed with 0-1.0 wt% Nb and performed Flux Cored Arc Welding. We observed the microstructure with the SEM/EDS and EBSD. To evaluate the uniform and pitting corrosion resistance, we performed a potentiodynamic polarization test in 0.2 M H{sub 2}SO{sub 4} and 0.1, 0.3, 0.5 M NaCl. As a result of the tests, we found that as the amount of addition of Nb rose, the amount of Cr-carbide fell. The microstructure became more refined. The specimen with 1.0%Nb added had the highest uniform and pitting corrosion resistance. After the pitting corrosion test, a pit was formed at the grain boundary that has no addition of Nb. In addition, in the specimen with added Nb, pits were formed at the inclusions.

  16. Effect of cold-rolling on pitting corrosion of 304 austenitic stainless steel

    International Nuclear Information System (INIS)

    Peguet, L.; Malki, B.; Baroux, B.

    2004-01-01

    Full text of publication follows: This paper deals with a not very often investigated topic on relation between cold-working and stainless steels localized corrosion resistance. It is devoted to the study of the cold-rolling effects on the pitting corrosion behavior of a 304 stainless steel grade in chloride containing aqueous electrolytes. It focus particularly on the analysis of metastable pitting transients observed at Open Circuit Potential using an experimental protocol including two identical working electrodes connected through a zero-impedance. As received the used specimens were heat-treated at 1100 C for 30 s and cold-rolled at 10%, 20%, 30% up to a final reduction pass of 70% inducing a large amount of α'-martensite. Then, current-potential fluctuations measurements were performed at OCP in NaCl 0.1 M + FeCl 3 2.10 -4 M containing aqueous solution during 24 h from the immersion time. As expected, a detrimental effect on corrosion behavior induced by cold rolling has been confirmed. Surprisingly, this is a nonlinear effect as a function of cold-rolling rate which controverts the hypothesis that strain induced martensite is the principal factor to explain this kind of sensibilizing. In particular, the results show a maximum of the metastable pits initiation frequency at 20% of cold-rolling rate. Moreover, the passive film/electrochemical double layer resistance and capacity deduced from the transients study show an analog nonlinear behavior. So, the transfer resistance show a minimum around 10-20% of cold-rolling rate where one can assume an increase of the electrons transfer kinetics through the interface. Conversely, the interfacial capacity is the highest at 20% of cold-rolling rate. Finally, It is expected a combined effect of the cold-rolled induced martensite and the dislocations arrangement via the mechano-chemical theory discussed by Gutman. (authors)

  17. Effects of Alloyed Carbon on the General Corrosion and the Pitting Corrosion Behavior of FeCrMnN Stainless Steels

    Energy Technology Data Exchange (ETDEWEB)

    Ha, Heon-Young; Lee, Tae-Ho; Kim, Sung-Joon [Korea Institute of Materials Science, Changwon (Korea, Republic of)

    2011-10-15

    The effects of alloyed carbon on the pitting corrosion, the general corrosion, and the passivity behavior of Fe{sub 1}8Cr{sub 1}0Mn{sub 0}.4Nx{sub C} (x=0 ⁓ 0.38 wt%) alloys were investigated by various electrochemical methods and XPS analysis. The alloyed carbon increased the general corrosion resistance of the FeCrMnN matrix. Carbon enhanced the corrosion potential, reduced the metal dissolution rate, and accelerated the hydrogen evolution reaction rate in various acidic solutions. In addition, carbon promoted the pitting corrosion resistance of the matrix in a chloride solution. The alloyed carbon in the matrix increased the chromium content in the passive film, and thus the passive film became more protective.

  18. An investigation on the effect of bleaching environment on pitting corrosion and trans-passive dissolution of 316 stainless steel

    International Nuclear Information System (INIS)

    Moayed, M.H.; Golestanipour, M.

    2004-01-01

    Pitting corrosion and trans-passive dissolution of 316 stainless steel in solution containing five percent of commercial bleaching liquid was investigated by employing potentiodynamic polarization method and recording corrosion potential during immersion. Today commercial bleaching liquids are widely used as cleaner additives, therefore, those house appliances made from stainless steels are in contact with aqueous solution containing bleaching liquid. This may cause sever localized corrosion and trans-passive dissolution. In order to investigate the possibility of trans-passive dissolution of stainless steel by bleaching liquid, potentiodynamic polarization and recording variation of corrosion potential of specimens were carried out in 0.2 M Na 2 SO 4 solution containing 5 %wt. commercial bleaching liquid. A 500 mV drop in trans-passive potential and also instantaneously ennobling corrosion potential revealed the possibility of trans-passive dissolution due to oxidizing effect of the species such as free chlorine and its derivatives in bleaching liquid. Evaluation of the occurrence of localized corrosion at the presence of Cl - and bleaching liquid was investigated by similar electrochemical experiments in 0.2 M Na 2 SO 4 + 0.4M NaCl containing 5%wt. bleaching solution. Initiation of stable pitting at potentials lower than trans-passive potential as well as sharp increasing of corrosion potential in this environment demonstrates the possibility of pitting corrosion. (authors)

  19. In-situ monitoring of pitting corrosion on vertically positioned 304 stainless steel by analyzing acoustic-emission energy parameter

    International Nuclear Information System (INIS)

    Wu, Kaige; Jung, Woo-Sang; Byeon, Jai-Won

    2016-01-01

    Highlights: • Pitting process in vertically positioned 304 SS is investigated by AE energy. • Gravity-influenced elongated pit, crack and rupture of pit cover were observed. • Hydrogen bubble evolution and pit covers rupturing were separately monitored by AE. • Four stages of AE energy were correlated with observed pitting mechanism. - Abstract: The acoustic emission (AE) energy was analyzed to monitor the pitting process on a vertically positioned 304-stainless steel. The gravity-dependent morphology of the elongated corrosion pits was observed. A scatter plot of the duration and energy indicated two AE clusters with different energy levels. There was a time delay after the detection of the low-energy hydrogen-bubble signals. Subsequently, high-energy signals were observed, whose AE source was attributed to large-scale cracks formed during the rupture of the elongated pit cover. An in-situ analysis of the AE energy evolution provided detailed insights into the corrosion process in relation to the specimen position.

  20. LabVIEW 2010 Computer Vision Platform Based Virtual Instrument and Its Application for Pitting Corrosion Study.

    Science.gov (United States)

    Ramos, Rogelio; Zlatev, Roumen; Valdez, Benjamin; Stoytcheva, Margarita; Carrillo, Mónica; García, Juan-Francisco

    2013-01-01

    A virtual instrumentation (VI) system called VI localized corrosion image analyzer (LCIA) based on LabVIEW 2010 was developed allowing rapid automatic and subjective error-free determination of the pits number on large sized corroded specimens. The VI LCIA controls synchronously the digital microscope image taking and its analysis, finally resulting in a map file containing the coordinates of the detected probable pits containing zones on the investigated specimen. The pits area, traverse length, and density are also determined by the VI using binary large objects (blobs) analysis. The resulting map file can be used further by a scanning vibrating electrode technique (SVET) system for rapid (one pass) "true/false" SVET check of the probable zones only passing through the pit's centers avoiding thus the entire specimen scan. A complete SVET scan over the already proved "true" zones could determine the corrosion rate in any of the zones.

  1. Influence of Step Annealing Temperature on the Microstructure and Pitting Corrosion Resistance of SDSS UNS S32760 Welds

    Science.gov (United States)

    Yousefieh, M.; Shamanian, M.; Saatchi, A.

    2011-12-01

    In the present work, the influence of step annealing heat treatment on the microstructure and pitting corrosion resistance of super duplex stainless steel UNS S32760 welds have been investigated. The pitting corrosion resistance in chloride solution was evaluated by potentiostatic measurements. The results showed that step annealing treatments in the temperature ranging from 550 to 1000 °C resulted in a precipitation of sigma phase and Cr2N along the ferrite/austenite and ferrite/ferrite boundaries. At this temperature range, the metastable pits mainly nucleated around the precipitates formed in the grain boundary and ferrite phase. Above 1050 °C, the microstructure contains only austenite and ferrite phases. At this condition, the critical pitting temperature of samples successfully arrived to the highest value obtained in this study.

  2. Effect of Annealing on the Pitting Corrosion Resistance of Anodized Aluminum-Magnesium Alloy Processed by Equal Channel Angular Pressing

    Energy Technology Data Exchange (ETDEWEB)

    Son, In Joon; Nakano, Hiroaki; Oue, Satoshi; Fukushima, Hisaaki; Horita, Zenji [Kyushu University, Fukuoka (Japan); Kobayashi, Shigeo [Kyushu Sangyo University, Fukuoka (Japan)

    2007-12-15

    The effect of annealing on the pitting corrosion resistance of anodized Al-Mg alloy (AA5052) processed by equal-channel angular pressing (ECAP) was investigated by electrochemical techniques in a solution containing 0.2 mol/L of AlCl{sub 3} and also by surface analysis. The Al-Mg alloy was annealed at a fixed temperature between 473 and 573 K for 120 min in air after ECAP. Anodizing was conducted for 40 min at 100-400 A/m{sup 2} at 293 K in a solution containing 1.53 mol/L of H{sub 2}SO{sub 4} and 0.0185 mol/L of Al{sub 2}(SO{sub 4}){sub 3}. The internal stress generated in anodic oxide films during anodization was measured with a strain gauge to clarify the effect of ECAP on the pitting corrosion resistance of anodized Al-Mg alloy. The time required to initiate the pitting corrosion of anodized Al-Mg alloy was shorter in samples subjected to ECAP, indicating that ECAP decreased the pitting corrosion resistance. however, the pitting corrosion resistance was greatly improved by annealing after ECAP. The time required to initiate pitting corrosion increased with increasing annealing temperature. The strain gauge attached to Al-Mg alloy revealed that the internal stress present in the anodic oxide films was compressive stress, and that the stress was larger with ECAP than without. The compressive internal stress gradually decreased with increasing annealing temperature. Scanning electron microscopy showed that cracks occurred in the anodic oxide film on Al-Mg alloy during initial corrosion and that the cracks were larger with ECAP than without. The ECAP process of severe plastic deformation produces large internal stresses in the Al-Mg alloy: the stresses remain in the anodic oxide films, increasing the likelihood of cracks. it is assumed that the pitting corrosion is promoted by these cracks as a result of the higher internal stress resulting from ECAP. The improvement in the pitting corrosion resistance of anodized AlMg alloy as a result of annealing appears to be

  3. Effect of Annealing on the Pitting Corrosion Resistance of Anodized Aluminum-Magnesium Alloy Processed by Equal Channel Angular Pressing

    International Nuclear Information System (INIS)

    Son, In Joon; Nakano, Hiroaki; Oue, Satoshi; Fukushima, Hisaaki; Horita, Zenji; Kobayashi, Shigeo

    2007-01-01

    The effect of annealing on the pitting corrosion resistance of anodized Al-Mg alloy (AA5052) processed by equal-channel angular pressing (ECAP) was investigated by electrochemical techniques in a solution containing 0.2 mol/L of AlCl 3 and also by surface analysis. The Al-Mg alloy was annealed at a fixed temperature between 473 and 573 K for 120 min in air after ECAP. Anodizing was conducted for 40 min at 100-400 A/m 2 at 293 K in a solution containing 1.53 mol/L of H 2 SO 4 and 0.0185 mol/L of Al 2 (SO 4 ) 3 . The internal stress generated in anodic oxide films during anodization was measured with a strain gauge to clarify the effect of ECAP on the pitting corrosion resistance of anodized Al-Mg alloy. The time required to initiate the pitting corrosion of anodized Al-Mg alloy was shorter in samples subjected to ECAP, indicating that ECAP decreased the pitting corrosion resistance. however, the pitting corrosion resistance was greatly improved by annealing after ECAP. The time required to initiate pitting corrosion increased with increasing annealing temperature. The strain gauge attached to Al-Mg alloy revealed that the internal stress present in the anodic oxide films was compressive stress, and that the stress was larger with ECAP than without. The compressive internal stress gradually decreased with increasing annealing temperature. Scanning electron microscopy showed that cracks occurred in the anodic oxide film on Al-Mg alloy during initial corrosion and that the cracks were larger with ECAP than without. The ECAP process of severe plastic deformation produces large internal stresses in the Al-Mg alloy: the stresses remain in the anodic oxide films, increasing the likelihood of cracks. it is assumed that the pitting corrosion is promoted by these cracks as a result of the higher internal stress resulting from ECAP. The improvement in the pitting corrosion resistance of anodized AlMg alloy as a result of annealing appears to be attributable to a decrease in

  4. Pitting corrosion of lead in sodium carbonate solutions containing NO3- ions

    International Nuclear Information System (INIS)

    Amin, Mohammed A.; Abdel Rehim, Sayed S.

    2004-01-01

    Pitting corrosion of Pb in Na 2 CO 3 solutions (pH=10.8) containing NaNO 3 as a pitting corrosion agent has been studied using potentiodynamic anodic polarization, cyclic voltammetry and chronoamperometry techniques, complemented with scanning electron microscopy (SEM) examinations of the electrode surface. In the absence of NO 3 - , the anodic voltammetric response exhibits three anodic peaks prior to oxygen evolution. The first anodic peak A 1 corresponds to the formation of PbCO 3 layer and soluble Pb 2+ species in solution. The second anodic peak A 2 is due to the formation of PbO beneath the carbonate layer. Peak A 2 is followed by a wide passive region which extends up to the appearance of the third anodic peak A 3 . The later is related to the formation of PbO 2 . Addition of NO 3 - to the carbonate solution stimulates the anodic dissolution through peaks A 1 and A 2 and breaks down the dual passive layer prior to peak A 3 . The breakdown potential decreases with an increase in nitrate concentration, temperature and electrode rotation rate, but increases with an increase in carbonate concentration and potential scan rate. Successive cycling leads to a progressive increase in breakdown potential. The current/time transients show that the incubation time for passivity breakdown decreases with increasing the applied anodic potential, nitrate concentration and temperature

  5. Examination of the metastable and stable pitting corrosion of aluminum modified with carbon by ion beam techniques

    International Nuclear Information System (INIS)

    Lensch, O.; Enders, B.; Knecht, J.; Ensinger, W.

    2001-01-01

    It is well known that aluminum and aluminum alloys are sensitive to pitting corrosion when exposed to aqueous solutions containing aggressive anions like halides. The destructive nature of pitting is due to its high local dissolution rates at electrode potentials above the so-called pitting potential U p . Recently, it has been realized that also at potentials below U p , in the passive and cathodic regions and around the free corrosion potential, anodic current transients appear which have been attributed to metastable pitting events. For the purpose of full characterization of the pitting behavior, a program routine has been developed where the occurrence frequency, lifetime and rate of metastable pitting events are extracted from potentiostatic current/time-measurements depending on the electrode potential. The routine has been applied to measurements of carbon modified pure aluminum. Carbon modifications were done with carbon evaporation and carbon sputtering under concurrent argon ion bombardment. The results are discussed in terms of the applied modification technique, their parameters and their effects on the corrosion protection ability of aluminum modified by carbon

  6. Advances in local mechano-electro chemistry for detecting pitting corrosion in duplex stainless steels

    International Nuclear Information System (INIS)

    Mary, N.

    2004-11-01

    A lot of studies have been carried out on the influence of a plastic deformation on the electrochemical behaviour of stainless steels. But, very few works have mentioned the role of the elastic or residual deformations. Nevertheless, these works reveal at the macroscopic scale the preponderant role of these deformations in the localized corrosion processes. The aim of this work is then to correlate the surface mechanical state to the local electrochemical behaviour of an austeno-ferritic stainless steel. The macroscopic mechanical behaviour of this steel (UNS S31803) has been at first determined by x-ray diffraction. The different domains of elastic and plastic behaviour have then been defined for each phase during tensile tests experiments. These results and the conventional pitting tests show the role of the residual stresses on the starting of the pitting. In complement to X-ray diffraction, a numerical approach has been used in order to determine the local mechanical state at the surface of the material. The coupling of the numerical simulation to local electrochemical measurements by the electrochemical microcell technology has allowed to define mechano-electrochemical criteria which control the starting of the pitting to the austenite-ferrite interfaces. (O.M.)

  7. Initiation, Propagation, and Mitigation of Aluminum and Chlorine Induced Pitting Corrosion

    OpenAIRE

    Marshall, Becki Jean

    2004-01-01

    Previous research by Rushing et al. (2002) identified key factors contributing to the formation of pinhole leaks in copper plumbing. These factors included high chlorine, pH levels and the presence of aluminum solids. Experiments were conducted to 1) examine the interplay between these constituents, 2) confirm that the water was aggressive enough to eat a hole through a pipe, 3) examine phosphate inhibition, and 4) try to determine the scope of this pitting problem in other distribution sy...

  8. Effects of sulfur addition on pitting corrosion and machinability behavior of super duplex stainless steel containing rare earth metals: Part 2

    International Nuclear Information System (INIS)

    Jeon, Soon-Hyeok; Kim, Soon-Tae; Lee, In-Sung; Park, Yong-Soo

    2010-01-01

    Research highlights: → The mechanisms on the effects of rare earth metals (REM) and sulfur (S) additions on the initiation and propagation of pitting corrosion and machinabillity of a super duplex stainless steel (SDSS) were elucidated → It was found that, in consideration of the ratio of lifetime (the resistance to pitting corrosion) to cost (machining and raw material), a costly austenitic stainless steel with high Ni , medium Mo and low N can be replaced by the high S and REM added SDSS with 7 wt.% Ni-4 wt% Mo-0.3 wt.% N → The resistance to pitting corrosion of the tested super duplex stainless steel was affected by the type of inclusions, the preferential interface areas between inclusions and the substrate, and the PREN difference between the γ-phase and the α-phase for the initiation and propagation of the pitting corrosion. - Abstract: To elucidate the effects of sulfur addition on pitting corrosion and machinability behavior of alloys containing rare earth metals, a potentiostatic polarization test, a critical pitting temperature test, a SEM-EDS analysis of inclusions, and a tool life test were conducted. As sulfur content increased, the resistance to pitting corrosion decreased due to the formation of numerous manganese sulfides deteriorating the corrosion resistance and an increase in the preferential interface areas for the initiation of the pitting corrosion. With an increase in sulfur content, the tool life increased due to the lubricating films of manganese sulfides adhering to tool surface.

  9. Corrosion

    Science.gov (United States)

    Slabaugh, W. H.

    1974-01-01

    Presents some materials for use in demonstration and experimentation of corrosion processes, including corrosion stimulation and inhibition. Indicates that basic concepts of electrochemistry, crystal structure, and kinetics can be extended to practical chemistry through corrosion explanation. (CC)

  10. Inhibition of Bio corrosion of steel coupon by sulphate reducing ...

    African Journals Online (AJOL)

    ADOWIE PERE

    Inhibition of Bio corrosion of steel coupon by sulphate reducing bacteria and Iron oxidizing bacteria using .... Ethanol for 24 h. The extract was ... with distilled water to get a zero reading from the meter before .... Ethanol extract of musa species peels as a green corrosion ... Eco friendly extract of banana peel as corrosion ...

  11. Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment

    Directory of Open Access Journals (Sweden)

    Liwei Wang

    2018-03-01

    Full Text Available Influence of alternating current (AC on pitting corrosion and stress corrosion cracking (SCC behavior of X70 pipeline steel in the near-neutral pH environment under cathodic protection (CP was investigated. Both corrosion and SCC are inhibited by −0.775 VSCE CP without AC interference. With the superimposition of AC current (1–10 mA/cm2, the direct current (DC potential shifts negatively under the CP of −0.775 VSCE and the cathodic DC current decreases and shifts to the anodic direction. Under the CP potential of −0.95 VSCE and −1.2 VSCE, the applied AC current promotes the cathodic reaction and leads to the positive shift of DC potential and increase of cathodic current. Local anodic dissolution occurs attributing to the generated anodic current transients in the positive half-cycle of the AC current, resulting in the initiation of corrosion pits (0.6–2 μm in diameter. AC enhances the SCC susceptibility of X70 steel under −0.775 VSCE CP, attributing to the promotion of anodic dissolution and hydrogen evolution. Even an AC current as low as 1 mA/cm2 can enhance the SCC susceptibility.

  12. Comparative Studies on Microstructure, Mechanical and Pitting Corrosion of Post Weld Heat Treated IN718 Superalloy GTA and EB Welds

    Science.gov (United States)

    Dilkush; Mohammed, Raffi; Madhusudhan Reddy, G.; Srinivasa Rao, K.

    2018-03-01

    In the present study, an attempt has been made to weld Inconel 718 nickel-base superalloy (IN718 alloy) using gas tungsten arc welding (GTAW) and electron beam welding (EBW) processes. Both the weldments were subjected to post-weld heat treatment condition as follows -980°C / 20 min followed by direct aging condition (DA) as 720°C/8 h/FC followed by 620°C/8 h/AC. The GTA and EB welds of IN718 alloy were compared in two conditions as-received and 980STA conditions. Welds were characterized to observe mechanical properties, pitting corrosion resistance by correlating with observed microstructures. The rate of higher cooling ranges, the fusion zone of EBW exhibited discrete and relative finer lave phases whereas the higher niobium existed laves with coarser structure were observed in GTAW. The significant dissolution of laves were observed at 980STA of EBW. Due to these effects, the EBW of IN718 alloy showed the higher mechanical properties than GTAW. The electrochemical potentiostatic etch test was carried out in 3.5wt% sodium chloride (NaCl) solution to study the pitting corrosion behaviour of the welds. Results of the present investigation established that mechanical properties and pitting corrosion behaviour are significantly better in post weld heat treated condition. The comparative studies showed that the better combination of mechanical properties and pitting corrosion resistance were obtained in 980STA condition of EBW than GTAW.

  13. Experimental and quantum chemical studies on corrosion inhibition ...

    Indian Academy of Sciences (India)

    Abstract. The corrosion inhibition effect of fluconazole (FLU) was investigated on steel in 1 M hydrochloric acid solution. Weight loss measurements and atomic force microscope analysis were utilized to investigate the corrosion inhibition properties and film formation behaviour of FLU. Quantum chemical approach was also ...

  14. Experimental and quantum chemical studies on corrosion inhibition

    Indian Academy of Sciences (India)

    The corrosion inhibition effect of fluconazole (FLU) was investigated on steel in 1 M hydrochloric acid solution. Weight loss measurements and atomic force microscope analysis were utilized to investigate the corrosion inhibition properties and film formation behaviour of FLU. Quantum chemical approach was also used to ...

  15. Surface monitoring for pitting evolution into uniform corrosion on Cu-Ni-Zn ternary alloy in alkaline chloride solution: ex-situ LCM and in-situ SECM

    Science.gov (United States)

    Kong, Decheng; Dong, Chaofang; Zheng, Zhaoran; Mao, Feixiong; Xu, Aoni; Ni, Xiaoqing; Man, Cheng; Yao, Jizheng; Xiao, Kui; Li, Xiaogang

    2018-05-01

    The evolution of the corrosion process on Cu-Ni-Zn alloy in alkaline chloride solution was investigated by in-situ scanning electrochemical microscopy, X-ray photoelectron spectroscopy, and ex-situ laser confocal microscopy, and the effects of ambient temperature and polarization time were also discussed. The results demonstrated a higher pitting nucleation rate and lower pit growth rate at low temperature. The ratio of pit depth to mouth diameter decreased with increasing pit volume and temperature, indicating that pits preferentially propagate in the horizontal direction rather than the vertical direction owing to the presence of corrosion products and deposited copper. The surface current was uniform and stabilized at approximately 2.2 nA during the passive stage, whereas the current increased after the pits were formed with the maximum approaching 3 nA. Increasing the temperature led to an increase in porous corrosion products (CuO, Zn(OH)2, and Ni(OH)2) and significantly increased the rate of transition from pitting to uniform corrosion. Dezincification corrosion was detected by energy dispersive spectrometry, and a mechanism for pitting transition into uniform corrosion induced by dezincification at the grain boundaries is proposed.

  16. Corrosion Inhibition of High Speed Steel by Biopolymer HPMC Derivatives

    Directory of Open Access Journals (Sweden)

    Shih-Chen Shi

    2016-07-01

    Full Text Available The corrosion inhibition characteristics of the derivatives of biopolymer hydroxypropyl methylcellulose (HPMC, hydroxypropyl methylcellulose phthalate (HPMCP, and hydroxypropyl methylcellulose acetate succinate (HPMCAS film are investigated. Based on electrochemical impedance spectroscopic measurements and potentiodynamic polarization, the corrosion inhibition performance of high speed steel coated with HPMC derivatives is evaluated. The Nyquist plot and Tafel polarization demonstrate promising anti-corrosion performance of HPMC and HPMCP. With increasing film thickness, both materials reveal improvement in corrosion inhibition. Moreover, because of a hydrophobic surface and lower moisture content, HPMCP shows better anti-corrosion performance than HPMCAS. The study is of certain importance for designing green corrosion inhibitors of high speed steel surfaces by the use of biopolymer derivatives.

  17. Magnesium microelectrode corrosion product transport modelling in relation to chloride induced pitting

    International Nuclear Information System (INIS)

    Burrows, R.; Cook, A.; Stevens, N.P.C.

    2012-09-01

    The high magnesium alloy Magnox is used as a fuel clad for the UK gas cooled, graphite moderated reactors of the same name. The fuel is metallic uranium (typically natural enrichment), so a low neutron absorption cross-section clad is required. Following discharge from reactor, spent fuel is stored in water, which acts as an effective heat transfer medium and biological shield. The chemistry of these ponds is carefully controlled to ensure that the Magnox clad remains in a passive state. This is primarily through the maintenance of a high pH and very low anion concentration. Of particular concern is the presence of chloride ions as even very low levels may allow localised corrosion to initiate. Although extensive work has been undertaken historically considering the behaviour of Magnox clad and the acceptable storage envelopes, the challenges of ageing plant and aspirations for accelerated decommissioning give value to further understanding of the corrosion mechanisms of this material. Recently, electrochemical techniques have been employed to characterise performance in a variety of chemistries and microelectrodes have been produced which have shown characteristics of salt film corrosion at moderate chloride concentrations under polarisation. A characteristic of the electrochemical response observed during the mass transport limited (potential independent) salt film regime has been periodic transients which correspond to emission of microscopic hydrogen bubbles from the microelectrode cavity. A simple finite element multi-physics model has been employed to assist in understanding the dominant processes of corrosion product transport away from a magnesium electrode surface which is dissolving under a salt film and this shows that characteristic transients observed in electrochemical tests may be simulated with reasonable agreement by consideration of convection from laminar flow around hydrogen micro-bubbles in the pit cavity combined with aqueous diffusion in the

  18. Pitting Corrosion Within Bioreactors for Space Cell-Culture Contaminated by Paenibacillus glucanolyticus, a Case Report

    Science.gov (United States)

    Barravecchia, Ivana; Cesari, Chiara De; Pyankova, Olga V.; Scebba, Francesca; Mascherpa, Marco Carlo; Vecchione, Alessandra; Tavanti, Arianna; Tedeschi, Lorena; Angeloni, Debora

    2018-02-01

    Performing cell biology experiments in space imposes the use of hardware that essentially allows fluid exchange in a contained environment. Given the technical and logistical peculiarities, the limited opportunities and the high cost of access to space, a great effort during mission preparation of scientific studies is devoted to preventing loss of the experiment. The European Space Agency (ESA) requires, at the end of the preparation phase, the execution of an Experiment Sequence Test (EST), a dry-run version of the space experiment to check all procedures. At conclusion of the EST of our experiment `ENDO' (ESA ILSRA-2009-1026), we found pitting corrosion of metal parts and biofilm formation within the cell-culture devices. The subsequent chemical (spectral assays), instrumental (OGP SmartScope) and microbiological (MALDI-TOF, 16S rRNA gene sequencing) investigations allowed the identification in contaminated material of Paenibacillus glucanolyticus, a ubiquitous, aerobic, facultative anaerobic, endospore forming, acid-producing, Gram-positive microorganism. A concurrence of P. glucanolyticus contamination and galvanic corrosion determined massive fouling, rust precipitation and damage to cells and cell-culture devices being, to our knowledge, the association between this microbe and corrosion never reported before in literature. As a consequence of the episode a critical procedure of experiment set up, i.e. hardware sterilization, was modified. The ENDO experiment was successfully launched to the International Space Station on September 2nd 2015 and returned to the PI laboratory on September 13th, with all cell culture samples in optimal condition.

  19. Pitting Corrosion Within Bioreactors for Space Cell-Culture Contaminated by Paenibacillus glucanolyticus, a Case Report

    Science.gov (United States)

    Barravecchia, Ivana; Cesari, Chiara De; Pyankova, Olga V.; Scebba, Francesca; Mascherpa, Marco Carlo; Vecchione, Alessandra; Tavanti, Arianna; Tedeschi, Lorena; Angeloni, Debora

    2018-05-01

    Performing cell biology experiments in space imposes the use of hardware that essentially allows fluid exchange in a contained environment. Given the technical and logistical peculiarities, the limited opportunities and the high cost of access to space, a great effort during mission preparation of scientific studies is devoted to preventing loss of the experiment. The European Space Agency (ESA) requires, at the end of the preparation phase, the execution of an Experiment Sequence Test (EST), a dry-run version of the space experiment to check all procedures. At conclusion of the EST of our experiment `ENDO' (ESA ILSRA-2009-1026), we found pitting corrosion of metal parts and biofilm formation within the cell-culture devices. The subsequent chemical (spectral assays), instrumental (OGP SmartScope) and microbiological (MALDI-TOF, 16S rRNA gene sequencing) investigations allowed the identification in contaminated material of Paenibacillus glucanolyticus, a ubiquitous, aerobic, facultative anaerobic, endospore forming, acid-producing, Gram-positive microorganism. A concurrence of P. glucanolyticus contamination and galvanic corrosion determined massive fouling, rust precipitation and damage to cells and cell-culture devices being, to our knowledge, the association between this microbe and corrosion never reported before in literature. As a consequence of the episode a critical procedure of experiment set up, i.e. hardware sterilization, was modified. The ENDO experiment was successfully launched to the International Space Station on September 2nd 2015 and returned to the PI laboratory on September 13th, with all cell culture samples in optimal condition.

  20. Modeling pitting corrosion damage of high-level radioactive-waste containers, with emphasis on the stochastic approach

    Energy Technology Data Exchange (ETDEWEB)

    Henshall, G.A.; Halsey, W.G.; Clarke, W.L.; McCright, R.D.

    1993-01-01

    Recent efforts to identify methods of modeling pitting corrosion damage of high-level radioactive-waste containers are described. The need to develop models that can provide information useful to higher level system performance assessment models is emphasized, and examples of how this could be accomplished are described. Work to date has focused upon physically-based phenomenological stochastic models of pit initiation and growth. These models may provide a way to distill information from mechanistic theories in a way that provides the necessary information to the less detailed performance assessment models. Monte Carlo implementations of the stochastic theory have resulted in simulations that are, at least qualitatively, consistent with a wide variety of experimental data. The effects of environment on pitting corrosion have been included in the model using a set of simple phenomenological equations relating the parameters of the stochastic model to key environmental variables. The results suggest that stochastic models might be useful for extrapolating accelerated test data and for predicting the effects of changes in the environment on pit initiation and growth. Preliminary ideas for integrating pitting models with performance assessment models are discussed. These ideas include improving the concept of container ``failure``, and the use of ``rules-of-thumb`` to take information from the detailed process models and provide it to the higher level system and subsystem models. Finally, directions for future work are described, with emphasis on additional experimental work since it is an integral part of the modeling process.

  1. Modeling pitting corrosion damage of high-level radioactive-waste containers, with emphasis on the stochastic approach

    International Nuclear Information System (INIS)

    Henshall, G.A.; Halsey, W.G.; Clarke, W.L.; McCright, R.D.

    1993-01-01

    Recent efforts to identify methods of modeling pitting corrosion damage of high-level radioactive-waste containers are described. The need to develop models that can provide information useful to higher level system performance assessment models is emphasized, and examples of how this could be accomplished are described. Work to date has focused upon physically-based phenomenological stochastic models of pit initiation and growth. These models may provide a way to distill information from mechanistic theories in a way that provides the necessary information to the less detailed performance assessment models. Monte Carlo implementations of the stochastic theory have resulted in simulations that are, at least qualitatively, consistent with a wide variety of experimental data. The effects of environment on pitting corrosion have been included in the model using a set of simple phenomenological equations relating the parameters of the stochastic model to key environmental variables. The results suggest that stochastic models might be useful for extrapolating accelerated test data and for predicting the effects of changes in the environment on pit initiation and growth. Preliminary ideas for integrating pitting models with performance assessment models are discussed. These ideas include improving the concept of container ''failure'', and the use of ''rules-of-thumb'' to take information from the detailed process models and provide it to the higher level system and subsystem models. Finally, directions for future work are described, with emphasis on additional experimental work since it is an integral part of the modeling process

  2. Aspects of the effects of temperature and electrolyte composition on pitting corrosion of stainless steel in dairy fluids

    Energy Technology Data Exchange (ETDEWEB)

    Perrin, F.X. [Toulon Univ., 83 - La Garde (France). Lab. de Chimie Appliquee; Girard, H.; Pagetti, J. [Universite de Franche-Comte, Besancon (France). Lab. de Corrosion et Traitments de Surfaces; Daufin, G. [INRA, Rennes (France). Lab. de Recherches de Technologie Laitiere

    2001-08-01

    The pitting corrosion resistance of 304L stainless steel in dairy fluids (milks, wheys, soya juice and peptidic fluids) was studied using electrochemical measurements. The effects of temperature, chloride content and other components of the fluids was particularly investigated. In the range 30- 70 C, the pitting potential in whole milk E{sub p} is related to the temperature by the relation ln(E{sub p} + 100) = aT{sup -1} + b. Above 70 C, a further phenomenon adds to the common activation effect of temperature. Heat induced conformational changes (denaturation) of the proteins were believed to explain such a behaviour. A typical linear relationship was found between E{sub p} and the logarithm of chloride concentration. All fluids are well represented by a single relationship. Therefore, the buffering capacity of casein micelles in milks do not significantly change the pitting resistance of the oxide film. In dairy industry, the corrosion risk is usually estimated from the difference between the pitting potential and the potential of a gold electrode (E{sub g}). It is noteworthy that the pitting risk decreases when temperature increases in the temperature range 50-90 C. Such a trend was due to the strong decrease in dissolved oxygen above 50 C. Besides, in aggressive peptidic solutions, the resistance of the passive film to localized attack is directly related to the Cr, Mo and N alloy content of stainless steel. (orig.)

  3. Studies on microstructure, mechanical and pitting corrosion behaviour of similar and dissimilar stainless steel gas tungsten arc welds

    Science.gov (United States)

    Mohammed, Raffi; Dilkush; Srinivasa Rao, K.; Madhusudhan Reddy, G.

    2018-03-01

    In the present study, an attempt has been made to weld dissimilar alloys of 5mm thick plates i.e., austenitic stainless steel (316L) and duplex stainless steel (2205) and compared with that of similar welds. Welds are made with conventional gas tungsten arc welding (GTAW) process with two different filler wires namely i.e., 309L and 2209. Welds were characterized using optical microscopy to observe the microstructural changes and correlate with mechanical properties using hardness, tensile and impact testing. Potentio-dynamic polarization studies were carried out to observe the pitting corrosion behaviour in different regions of the welds. Results of the present study established that change in filler wire composition resulted in microstructural variation in all the welds with different morphology of ferrite and austenite. Welds made with 2209 filler showed plate like widmanstatten austenite (WA) nucleated at grain boundaries. Compared to similar stainless steel welds inferior mechanical properties was observed in dissimilar stainless steel welds. Pitting corrosion resistance is observed to be low for dissimilar stainless steel welds when compared to similar stainless steel welds. Overall study showed that similar duplex stainless steel welds having favorable microstructure and resulted in better mechanical properties and corrosion resistance. Relatively dissimilar stainless steel welds made with 309L filler obtained optimum combination of mechanical properties and pitting corrosion resistance when compared to 2209 filler and is recommended for industrial practice.

  4. Inhibitive Behaviour of Corrosion of Aluminium Alloy in NaCl by Mangrove Tannin

    International Nuclear Information System (INIS)

    Solhan Yahya; Afidah Abdul Rahim; Affaizza Mohd Shah; Rohana Adnan

    2011-01-01

    Anticorrosion potential of mangrove tannins on aluminium alloys AA6061 in NaCl solution has been studied using potentiodynamic polarisation method and scanning electron microscopy (SEM). The study was carried out in different pH of corrosive medium in the absence and presence of various concentrations of tannin. The corrosion inhibition behaviour of the mangrove tannin on AA6061 aluminium alloy corrosion was found to be dependant on the pH of NaCl solution. Our results showed that the inhibition efficiency increased with increasing tannins concentration in chloride solution at pH 6. Treatment of aluminium alloy 6061 with all concentrations of mangrove tannins reduced the current density, thus decreased the corrosion rate. Tannins behaved as mixed inhibitors at pH 6 and reduction in current density predominantly affected in cathodic reaction. Meanwhile, at pH 12, addition of tannins shifted the corrosion potential to more cathodic potentials and a passivating effect was observed in anodic potentials. SEM studies have shown that the addition of tannins in chloride solution at pH 12 reduced the surface degradation and the formation of pits. (author)

  5. Inhibition of anodic corrosion of aluminium cathode current collector on recharging in lithium imide electrolytes

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Xianming; Yasukawa, Eiki; Mori, Shoichiro [Tsukuba Research Center, Mitsubishi Chemical Corp., Ibaraki (Japan)

    2000-07-01

    Pitting corrosion of aluminum as cathode current collector for lithium rechargeable batteries was found to take place at potential positive of 3.5 V in 1 mol dm {sup -3} LiN(SO{sub 2}CF{sub 3}){sub 2} /EC + DME (1:1) electrolyte. The corrosion mechanism of aluminum in the presence of LiN(SO{sub 2}CF{sub 3}){sub 2} was proposed, and three methods were deduced to inhibit the aluminum corrosion based on this mechanism. As a result, an additive of lithium salts based on perfluorinated inorganic anions, especially LiPF{sub 6}, was found to inhibit the aluminum corrosion to a certain extent by forming a protective film on aluminum surface. The oxidation stability of aluminum in LiN(SO{sub 2}CF{sub 3}){sub 2} -containing electrolytes depended strongly on the solvent structure. The ether solvents such as tetrahydrofuran (THF) and dimethoxyethane (DME) were effective in preventing aluminum corrosion due to their low dielectric constants. Furthermore, LiN(SO{sub 2}C{sub 2}F{sub 5}){sub 2} salt with a larger anion than that of LiN(SO{sub 2}CF{sub 3}){sub 2} was evaluated and good oxidation stability of aluminum was obtained regardless of the kind of solvents. (Author)

  6. Lean duplex stainless steels-The role of molybdenum in pitting corrosion of concrete reinforcement studied with industrial and laboratory castings

    Energy Technology Data Exchange (ETDEWEB)

    Mesquita, T.J. [LEPMI, UMR5279CNRS, Grenoble INP, Universite de Savoie, Universite Joseph Fourier, BP 75, 38402 St Martin d' Heres (France); CRU Ugitech, Av Paul Girod 73400 Ugine (France); Chauveau, E.; Mantel, M. [CRU Ugitech, Av Paul Girod 73400 Ugine (France); Kinsman, N. [International Molybdenum Association, IMOA W4 4JE London (United Kingdom); Roche, V. [LEPMI, UMR5279CNRS, Grenoble INP, Universite de Savoie, Universite Joseph Fourier, BP 75, 38402 St Martin d' Heres (France); Nogueira, R.P., E-mail: ricardo.nogueira@grenoble-inp.fr [LEPMI, UMR5279CNRS, Grenoble INP, Universite de Savoie, Universite Joseph Fourier, BP 75, 38402 St Martin d' Heres (France)

    2012-02-15

    Highlights: Black-Right-Pointing-Pointer Mo influence on corrosion of DSS was studied with industrial and laboratory heats. Black-Right-Pointing-Pointer Beneficial effect of Mo was associated with ferrite corrosion resistance. Black-Right-Pointing-Pointer Mo-species in the alkaline solution did not improve pit resistance. Black-Right-Pointing-Pointer Mo role in DSS under alkaline conditions was ascribed to its presence in oxide film. - Abstract: The influence of Mo addition on pitting corrosion resistance of lean duplex stainless steels is not clearly understood in alkaline chloride conditions even if this element is widely recognized to increase corrosion resistance in acidic and neutral environments. This work aims to study the effect of Mo on pitting corrosion of lean duplex stainless steels in synthetic concrete pore solutions simulating degraded concrete. Results are discussed with respect to the influence of Mo on pitting potential for two industrial alloys in chloride rich and carbonated solution simulating concrete pore environments. To establish the real effect of Mo addition on lean duplex corrosion and passivation properties, two specific laboratory lean duplex alloys, for which the only difference is strictly the Mo content, are also studied. Mo presented a strong positive influence on the pitting corrosion resistance of industrial and laboratory lean duplex stainless steels in all studied chloride-rich solutions, but its effect is as less pronounced as the pH increases. In presence of Mo, pitting initiates and propagates preferentially in the austenitic phase at high temperature.

  7. INHIBITION OF CORROSION OF ZINC IN (HNO3 + HCl) ACID ...

    African Journals Online (AJOL)

    2015-05-01

    May 1, 2015 ... corrosion inhibitor for zinc in phosphoric acid. Vashi et al.[8-9] studied the corrosion inhibition of zinc in (HNO3 + H2SO4) and (HNO3 + H3PO4) binary acid mixture by aniline. In the present work, the role of aniline as inhibitor for corrosion of zinc in (HNO3 + HCl) binary acid mixture has been reported. 2.

  8. Nanosecond laser surface modification of AISI 304L stainless steel: Influence the beam overlap on pitting corrosion resistance

    International Nuclear Information System (INIS)

    Pacquentin, Wilfried; Caron, Nadège; Oltra, Roland

    2014-01-01

    Surface modifications of AISI 304L stainless steel by laser surface melting (LSM) were investigated using a nanosecond pulsed laser-fibre doped by ytterbium at different overlaps. The objective was to study the change in the corrosion properties induced by the treatment of the outer-surface of the stainless steel without modification of the bulk material. Different analytical techniques such as scanning electron microscopy (SEM), X-ray diffraction (XRD), and glow discharge optical emission spectrometry (GDOES) were used to characterize the laser-melted surface. The corrosion resistance was evaluated in a chloride solution at room temperature by electrochemical tests. The results showed that the crystallographic structure, the chemical composition, the properties of the induced oxide layer and consequently the pitting corrosion resistance strongly depend on the overlap rate. The most efficient laser parameters led to an increase of the pitting potential by more than 300 mV, corresponding to a quite important improvement of the corrosion resistance. This latter was correlated to chromium enrichment (47 wt.%) at the surface of the stainless steel and the induced absence of martensite and ferrite phases. However, these structural and chemical modifications were not sufficient to explain the change in corrosion behaviour: defects and adhesion of the surface oxide layer must have been taken into consideration.

  9. Improvement of pitting corrosion resistance of AISI 304L stainless steel by nano-pulsed laser surface melting

    International Nuclear Information System (INIS)

    Pacquentin, W.; Blanc, C.; Caron, N.; Thro, P.Y.; Cheniere, A.; Tabarant, M.; Moutiers, G.; Miserque, F.; Plouzennec, H.; Oltra, R.

    2013-01-01

    The stainless steel 304L is widely used, however, in particular conditions, it may be sensitive to pitting corrosion. Nano-pulsed laser surface melting is a surface treatment which allows improving the corrosion resistance of this steel. This treatment consists in focusing a laser beam on the surface of the material, involving its quite immediately melting through a few microns depth, then an ultra-fast solidification occurs with cooling rate about 1011 K/s. The laser parameters control the modifications of the physico-chemical properties. In particular, we studied the influence of the impacts overlap of an ytterbium laser-fiber on the corrosion resistance of a 304L stainless steel in conditions of an aerated and agitated solution of NaCl (concentration of 30 g/L). We obtained an increase of the pitting potential of 220 mV, highlighting an improvement of the corrosion resistance. The study of the chemical and structural modifications is not enough to explain the improvement of the corrosion resistance. Other phenomena must be taken into account, as the quality of the oxide layer, in terms of physico-chemical and mechanical properties. (authors)

  10. The effect of sulphite on crevice corrosion and pitting on various steels in 0.5 M sodium chloride

    International Nuclear Information System (INIS)

    Hemmingsen, T.; Nielsen, L.V.; Maahn, E.

    1992-01-01

    A carbon steel, st 37, and two stainless steels, AISI 304 SS and AISI 316 SS were exposed to 0.5 M NaCl with 10 mM sulphite under anaerobic conditions. The sulphite ions may, under these conditions, be reduced to sulphide ions, and cause pitting or crevice corrosion. Electrochemical and bottle-test experiments were done to determine the effect of the sulphite addition. These effects were highly dependant on the pH

  11. The resistance of austenitic stainless steels to pitting corrosion in simulated BFS/OPC pore waters containing thiosulphate ions

    International Nuclear Information System (INIS)

    Betts, A.J.; Newman, R.C.

    1989-06-01

    Current plans for the disposal of intermediate-level nuclear waste involve the use of austenitic stainless steel drums. The immediate environment seen by both the inner and outer surfaces of these drums will be alkaline, as a consequence of the encasement of both the drum and its contents in concrete. Normally there would be no risk of localized corrosion of the steel in this situation, but a possible complication is introduced by the use of blast-furnace slag (BFS) to decrease the permeability of the concrete. Metal sulphides in the BFS react with air and water to yield thiosulphate ions, which are known to be corrosive towards stainless steels in environments of near-neutral pH. This research was carried out to study the effects of thiosulphate at alkaline pH, simulating the concrete environment. Types 304L and 316L stainless steel have been tested for pitting corrosion resistance in simulated BFS/Ordinary Portland Cement pore waters of pH 10-13, at 20 o C and 50 o C. The results show that the 316L steel is essentially immune to pitting. The 304L steel shows some pitting at the higher temperature, especially at the higher chloride concentrations, but only at pH values of less than 12, which would require serious deterioration of the cement matrix. (author)

  12. Inhibition Effect of Deanol on Mild Steel Corrosion in Dilute ...

    African Journals Online (AJOL)

    NICOLAAS

    2014-06-23

    Jun 23, 2014 ... allows for extensive use as the material of construction in petro- leum industries .... steel specimens was investigated after mass-loss analysis ..... Ogbuliec, Inhibition of pseudo-anaerobic corrosion of oil pipeline steel in ...

  13. Pitting corrosion of copper in aqueous solutions containing phosphonic acid as an inhibitor. Hosuhon san wo inhibita toshite fukumu suiyoekichu ni okeru do no koshiku ni tsuite

    Energy Technology Data Exchange (ETDEWEB)

    Yamada, Y. (Muroran Univ., Hokkaido (Japan). Graduate School); Seri, O.; Tagashira, K. (Muroran Univ., Hokkaido (Japan)); Nagata, K. (Sumitomo Light Metal Co. Ltd., Tokyo (Japan). Technical Research Lab.)

    1993-09-15

    Phosphonic acid-based inhibitors that are poured into cooling water for copper-tube circulation systems for open heat-accumulators were studied on their influence on pitting corrosion of copper. Amino trimethylene phosphonic acid (ATMP) dissolved into distilled water to 50 ppm was used for the immersion corrosion test. The corrosion-proof effect of additives such as ZnSO4, benzotriazole (BTA) was tested too. 0.5 mm thick phosphate-treated copper plates with a hole of 5 mm in diameter were used as test specimens. Pitting corrosion on the copper plate occurred when ATMP, BTA and ZnSO4 coexisted. It was proved that SO4 [sup 2-] is essential since Na2SO4 in stead of ZnSO4 induced also corrosion. The pitting took place when 0.6 ppm or more of SO4 [sup 2-] was present in a BTA-added ATMP solution. It was observed that the pitting is prone to occur with increase of SO4 [sup 2-] and the number of pitting increases. The following relationship is established when pitting corrosion occurs; E[sub b] [le] E[sub corr], where the former is a potential value at which current density shows a steep increase and the latter is an average value of spontaneous electrode potential showing a plateau. 8 refs., 11 figs., 1 tab.

  14. Abstraction of Models for Pitting and Crevice Corrosion of Drip Shield and Waste Package Outer Barrier

    International Nuclear Information System (INIS)

    Mon, K.

    2001-01-01

    This analyses and models report (AMR) was conducted in response to written work direction (CRWMS M and O 1999a). ICN 01 of this AMR was developed following guidelines provided in TWP-MGR-MD-000004 REV 01, ''Technical Work Plan for: Integrated Management of Technical Product Input Department'' (BSC 2001, Addendum B). The purpose and scope of this AMR is to review and analyze upstream process-level models (CRWMS M and O 2000a and CRWMS M and O 2000b) and information relevant to pitting and crevice corrosion degradation of waste package outer barrier (Alloy 22) and drip shield (Titanium Grade 7) materials, and to develop abstractions of the important processes in a form that is suitable for input to the WAPDEG analysis for long-term degradation of waste package outer barrier and drip shield in the repository. The abstraction is developed in a manner that ensures consistency with the process-level models and information and captures the essential behavior of the processes represented. Also considered in the model abstraction are the probably range of exposure conditions in emplacement drifts and local exposure conditions on drip shield and waste package surfaces. The approach, method, and assumptions that are employed in the model abstraction are documented and justified

  15. Abstraction of Models for Pitting and Crevice Corrosion of Drip Shield and Waste Package Outer Barrier

    Energy Technology Data Exchange (ETDEWEB)

    K. Mon

    2001-08-29

    This analyses and models report (AMR) was conducted in response to written work direction (CRWMS M and O 1999a). ICN 01 of this AMR was developed following guidelines provided in TWP-MGR-MD-000004 REV 01, ''Technical Work Plan for: Integrated Management of Technical Product Input Department'' (BSC 2001, Addendum B). The purpose and scope of this AMR is to review and analyze upstream process-level models (CRWMS M and O 2000a and CRWMS M and O 2000b) and information relevant to pitting and crevice corrosion degradation of waste package outer barrier (Alloy 22) and drip shield (Titanium Grade 7) materials, and to develop abstractions of the important processes in a form that is suitable for input to the WAPDEG analysis for long-term degradation of waste package outer barrier and drip shield in the repository. The abstraction is developed in a manner that ensures consistency with the process-level models and information and captures the essential behavior of the processes represented. Also considered in the model abstraction are the probably range of exposure conditions in emplacement drifts and local exposure conditions on drip shield and waste package surfaces. The approach, method, and assumptions that are employed in the model abstraction are documented and justified.

  16. Effect of pH and chloride on the micro-mechanism of pitting corrosion for high strength pipeline steel in aerated NaCl solutions

    International Nuclear Information System (INIS)

    Wang, Yafei; Cheng, Guangxu; Wu, Wei; Qiao, Qiao; Li, Yun; Li, Xiufeng

    2015-01-01

    Highlights: • Pitting behavior of X80 steel in aerated NaCl solutions is studied systematically. • Unique large pit morphology is observed in neutral/acidic NaCl solutions. • In low pH solutions, pit will propagate in the horizontal direction, leading to the shallow shape of pitting morphology; in high pH solutions, the pit sizes are much smaller. • Film growth, which is dependent on the pH and chloride concentration, has great influence on the cathodic reaction by affecting oxygen diffusion process. - Abstract: The pitting corrosion mechanism of high strength pipeline steel in aerated NaCl solutions with different pH and chloride content was investigated, using potentiodynamic polarization, electrochemical impedance spectroscopy (EIS) and scanning electron microscope (SEM). The pitting behavior in alkaline solutions was found to be significantly different from that in neutral and acidic solutions. Electrochemical results and SEM images indicate that the product film formed on the steel surface results in different corrosion behavior in an alkaline solution. SEM images show that pH and chloride concentration in the bulk solution have a great influence on the pitting morphology. Unique large pit morphology due to corrosion in neutral/acidic solutions with 0.05 mol/L NaCl was observed. The relationship between solution pH and the effect of chloride concentration is also discussed

  17. Axenic aerobic biofilms inhibit corrosion of copper and aluminum.

    Science.gov (United States)

    Jayaraman, A; Ornek, D; Duarte, D A; Lee, C C; Mansfeld, F B; Wood, T K

    1999-11-01

    The corrosion behavior of unalloyed copper and aluminum alloy 2024 in modified Baar's medium has been studied with continuous reactors using electrochemical impedance spectroscopy. An axenic aerobic biofilm of either Pseudomonas fragi K or Bacillus brevis 18 was able to lessen corrosion as evidenced by a consistent 20-fold increase in the low-frequency impedance value of copper as well as by a consistent four- to seven-fold increase in the polarization resistance of aluminum 2024 after six days exposure compared to sterile controls. This is the first report of axenic aerobic biofilms inhibiting generalized corrosion of copper and aluminum. Addition of the representative sulfate-reducing bacterium (SRB) Desulfovibrio vulgaris (to simulate consortia corrosion behavior) to either the P. fragi K or B. brevis 18 protective biofilm on copper increased the corrosion to that of the sterile control unless antibiotic (ampicillin) was added to inhibit the growth of SRB in the biofilm.

  18. Resistance of Incoloy 800 steam generator tube to pitting corrosion in PWR secondary water at 250°C

    International Nuclear Information System (INIS)

    Schvartzman, Mônica M.A.M.; Albuquerque, Adriana Silva de; Esteves, Luiza; Rabello, Emerson G.; Mansur, Fábio Abud

    2017-01-01

    The steam generator (SG) is one of the main components of a PWR, so the performance of this type of nuclear power plant depends to a large extent on the trouble-free operation of SGs. Its degradation significantly affects the overall plant performance. Alloy 800NG (Incoloy® 800) is a nickel-iron-chromium alloy used for steam generator tubes in PWRs due to their high strength, good workability and resistance to corrosion. This behavior is attributed to the protective oxide film formed on the metal surface by contact with the high temperature pressurized water. However, chloride is one of major SG impurities that cause the breakdown of the passive film and initiate localized corrosion in passive metals as Alloy 800NG. The aim of this study is to provide information about the pitting corrosion behavior of the Incoloy® 800 steam generator tube under normal secondary circuit parameters (250 deg C and 5 MPa) and abnormal conditions of operation (presence of chloride ions in the secondary water). For this, optical microscopy, XRD and EDS analysis and electrochemical tests have been carried out under simulated PWR secondary water operating conditions. The susceptibility to pitting corrosion was evaluated using electrochemical tests and the oxide layer formed on material was examined by means of scanning electron microscopy (SEM) and energy dispersive X-ray spectrometer (EDS) analyses. (author)

  19. Resistance of Incoloy 800 steam generator tube to pitting corrosion in PWR secondary water at 250°C

    Energy Technology Data Exchange (ETDEWEB)

    Schvartzman, Mônica M.A.M. [Pontifícia Universidade Católica de Minas Gerais (PUC-Minas), Belo Horizonte, MG (Brazil); Albuquerque, Adriana Silva de; Esteves, Luiza; Rabello, Emerson G.; Mansur, Fábio Abud, E-mail: monicacdtn@gmail.com, E-mail: asa@cdtn.br, E-mail: luiza.esteves@cdtn.br, E-mail: egr@cdtn.br, E-mail: fametalurgica@gmail.com [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2017-07-01

    The steam generator (SG) is one of the main components of a PWR, so the performance of this type of nuclear power plant depends to a large extent on the trouble-free operation of SGs. Its degradation significantly affects the overall plant performance. Alloy 800NG (Incoloy® 800) is a nickel-iron-chromium alloy used for steam generator tubes in PWRs due to their high strength, good workability and resistance to corrosion. This behavior is attributed to the protective oxide film formed on the metal surface by contact with the high temperature pressurized water. However, chloride is one of major SG impurities that cause the breakdown of the passive film and initiate localized corrosion in passive metals as Alloy 800NG. The aim of this study is to provide information about the pitting corrosion behavior of the Incoloy® 800 steam generator tube under normal secondary circuit parameters (250 deg C and 5 MPa) and abnormal conditions of operation (presence of chloride ions in the secondary water). For this, optical microscopy, XRD and EDS analysis and electrochemical tests have been carried out under simulated PWR secondary water operating conditions. The susceptibility to pitting corrosion was evaluated using electrochemical tests and the oxide layer formed on material was examined by means of scanning electron microscopy (SEM) and energy dispersive X-ray spectrometer (EDS) analyses. (author)

  20. TRANSITIONS IN ELECTROCHEMICAL NOISE DURING PITTING CORROSION OF ALUMINUM IN CHLORIDE ENVIRONMENTS

    International Nuclear Information System (INIS)

    SASAKI, K.; ISAACS, H.S.; LEVY, P.W.

    2001-01-01

    Aluminum, in a chloride containing solutions close to its pitting potential, shows vigorous fluctuations in current and potential. Measurements have been made of the freely corroding potential, and the currents between interconnected electrodes. It is shown that there is a transition in the behavior of the transients. The transition occurs when multiple active pits are present and electrochemical communication occurs between them. The major source of current and potential transients is the growth process in the active pits rather than meta-stable pitting at the passive surface

  1. TRANSITIONS IN ELECTROCHEMICAL NOISE DURING PITTING CORROSION OF ALUMINUM IN CHLORIDE ENVIRONMENTS.

    Energy Technology Data Exchange (ETDEWEB)

    SASAKI,K.; ISAACS,H.S.; LEVY,P.W.

    2001-09-02

    Aluminum, in a chloride containing solutions close to its pitting potential, shows vigorous fluctuations in current and potential. Measurements have been made of the freely corroding potential, and the currents between interconnected electrodes. It is shown that there is a transition in the behavior of the transients. The transition occurs when multiple active pits are present and electrochemical communication occurs between them. The major source of current and potential transients is the growth process in the active pits rather than meta-stable pitting at the passive surface.

  2. A phenomenological approach to simulating the evolution of radioactive-waste container damage due to pitting corrosion

    International Nuclear Information System (INIS)

    Henshall, G.A.

    1995-01-01

    The damage to high-level radioactive-waste containers by pitting corrosion is an important design and performance assessment consideration. It is desirable to calculate the evolution of the pit depth distribution, not just the time required for initial penetration of the containers, so that the area available for advective of diffusive release of radionuclides through the container can be estimated. A phenomenological approach for computing the time evolution of these distributions is presented which combines elements of the deterministic and stochastic aspects of pit growth. The consistency of this approach with the mechanisms believed to control the evolution of the pit depth distribution is discussed. Qualitative comparisons of preliminary model predictions with a variety of experimental data from the literature are shown to be generally favorable. The sensitivity of the simulated distributions to changes in the input parameters is discussed. Finally, the results of the current model are compared to those of existing approaches based on extreme-value statistics, particularly regarding the extrapolation of laboratory data to large exposed surface areas

  3. Corrosion inhibition of mild steel by Capsicum annuum fruit paste

    Directory of Open Access Journals (Sweden)

    Chandan M. Reddy

    2016-09-01

    Full Text Available The anti-corrosive property of Capsicum annuum fruit paste (CFP on mild steel was investigated. Weight loss and SEM analysis showed that the aqueous and ethanolic solutions of CFP exhibits excellent corrosion inhibition in 2 M HCl. Contact angle, surface atomic composition and FTIR studies verified the presence of an organic film on the mild steel surface. The FTIR spectra also indicated the formation of active compound-Fe complex. CFP thus shows potential as an inexpensive environment friendly corrosion inhibitor for mild steel.

  4. Corrosion inhibition of brass by aliphatic amines

    International Nuclear Information System (INIS)

    Taha, K. K.; Sheshadri, B. S; Ahmed, M. F.

    2005-01-01

    Aliphatic amines hexylamine (HCA), octylamine (OCA) and decylamine (DCA) have been used as corrosion inhibitors for (70/30) brass in 0.I M HCIO 4 . The inhibitor efficiency (%P) calculated using weight loss, Tafel extrapolation, linear polarization and impedance methods was found to be in the order DCA> OCA> HCA. These adsorb on brass surface following bockris-swinkels' isotherm. DCA, OCA and HCA displaced 4, 3 and 2 molecules of water from interface respectively. Displacement of water molecules brought a great reorganization of double layer at the interface. These amines during corrosion form complexes with dissolved zinc and copper ions.(Author)

  5. Effect of Welding Process on Microstructure, Mechanical and Pitting Corrosion Behaviour of 2205 Duplex Stainless Steel Welds

    Science.gov (United States)

    Mohammed, Raffi; Madhusudhan Reddy, G.; Srinivasa Rao, K.

    2018-03-01

    An attempt has been made to weld 2205 Duplex stainless steel of 6mm thick plate using conventional gas tungsten arc welding (GTAW) and activated gas tungsten arc welding (A- GTAW) process using silica powder as activated flux. Present work is aimed at studying the effect of welding process on depth of penetration, width of weld zone of 2205 duplex stainless steel. It also aims to observe the microstructural changes and its effect on mechanical properties and pitting corrosion resistance of 2205 duplex stainless steel welds. Metallography is done to observe the microstructural changes of the welds using image analyzer attached to the optical microscopy. Hardness studies, tensile and ductility bend tests were evaluated for mechanical properties. Potentio-dynamic polarization studies were carried out using a basic GillAC electro-chemical system in 3.5% NaCl solution to observe the pitting corrosion behaviour. Results of the present investigation established that increased depth of penetration and reduction of weld width in a single pass by activated GTAW with the application of SiO2 flux was observed when compared with conventional GTAW process. It may be attributed to the arc constriction effect. Microstructure of the weld zones for both the welds is observed to be having combination of austenite and delta ferrite. Grain boundary austenite (GBA) with Widmanstatten-type austenite (WA) of plate-like feature was nucleated from the grain boundaries in the weld zone of A-GTAW process. Mechanical properties are relatively low in activated GTAW process and are attributed to changes in microstructural morphology of austenite. Improved pitting corrosion resistance was observed for the welds made with A-GTAW process.

  6. Non Destructive Testing Measurement for Monitoring Pitting Corrosion using Dcp Techniques

    International Nuclear Information System (INIS)

    Atlam, A.; Omar, A.A.; Habashy, M.; Waheed, A.F.; Shafy, M.

    2010-01-01

    A repeatable monitoring of pit from in accessible side of a welded side of a structure is one of the hurdles in field of NT. The present work uses the DC potential drop measuring system for evaluating the response of pits in the weld joins to be detected by DC potential drop measurements. Weld joint of type 304L stainless steel welded with 308L was tested. Selected pits in different zones of the weld joint were detected by optical microscopy. The PD test shows difference in potential between pitted and non-pitted weld joints ranging from 1.3 in BM to 1.7 in HAZ. The capability of present monitoring process can be extended to evaluate the reduction in thickness for the case of thick stainless steel structure

  7. SCC life estimation based on cracks initiated from the corrosion pits of bolting material SCM435 used in steam turbine

    International Nuclear Information System (INIS)

    Itoh, Hitomi; Ochi, Mayumi; Fujiwara, Isao; Momoo, Takashi

    2003-01-01

    Life estimation was performed for the stress corrosion cracking (SCC) that occurs in deaerated and wet hot pure steam at the bottoms of the threads of bolts made of SCM435 (equivalent to AISI 4137) used in steam turbine. SCC is believed to occur when corrosion pits are formed and grow to critical size, after which SCC is initiated and cracks propagate until the critical fracture toughness value is reached. Calculations were performed using laboratory and field data. The results showed that, for a 40mm diameter bolt with 0.2% offset strength of 820MPa, the critical crack depth for straight-front cracks was 5.4mm. The SCC life depends on the lubricant used; the SCC life estimated from this value is approximately 70,000 hours when graphite is used as a lubricant. (author)

  8. The application of ion-exchanged clay as corrosion inhibiting pigments in organic coatings

    Science.gov (United States)

    Chrisanti, Santi

    High strength aluminum alloys are used in aerospace industry and are normally coated to prevent corrosion. The corrosion protection of the coatings is mainly provided by pigmented-primer layer. Strontium chromate pigments are widely used, but they are toxic and carcinogenic. The objective of the current study is to develop and characterize the ion exchange compounds bentonite and hydrotalcite as corrosion inhibiting pigments. These compounds were synthesized with different cations and anions, and were used either alone or in mixtures as particulate additive in organic coatings. In coating applications as well as bulk solution, the inhibitor release mechanism is based on ion exchange. To evaluate corrosion inhibition, pigments extract solutions were used in potentiodynamic polarization as well as electrochemical impedance spectroscopy (EIS) experiments on bare aluminum alloy 2024-T3. Cathodic polarization showed that zinc- and cerium-containing filtrate solutions modestly inhibited cathodic current density. These solutions also decreased the extent of pitting damage formed on the surface, as compared to uninhibited 0.5 M NaCl solution. Pigments were also added as primer additives, and painted on AA2024-T3. The coated panels were then subjected to salt spray exposure testing. The possibility of sensing inhibitor exhaustion by means of X-ray diffraction interrogation of the pigment in a coating is demonstrated and discussed on cerium bentonite-pigmented coatings. Although cerium bentonite-pigmented coatings did not show behavior indicative of self-healing, the combination of bentonite and hydrotalcite that released Ce3+, Zn 2+, and PO43- showed potent scribe protection even after 3000 h exposure in salt spray. Promising self-healing was also demonstrated by pigments that consisted of decavanadate-hydrotalcite and zinc pyrovanadate, as indicated by a shiny scribed area after 1000h exposure in salt spray. When these pigments are used, blistering is minimized.

  9. Pitting corrosion resistance of a novel duplex alloy steel in alkali-activated slag extract in the presence of chloride ions

    Science.gov (United States)

    Shi, Jin-jie; Ming, Jing; Liu, Xin

    2017-10-01

    In this study, two types of reinforcing steels (conventional low-carbon steel and a novel duplex alloy steel with Cr and Mo) were exposed to chloride-contaminated extract solutions (ordinary Portland cement (OPC) extract and alkali-activated slag (AAS) extract) to investigate their pitting corrosion resistance. The results confirm that the pitting corrosion resistance of the alloy steel is much higher than that of the low-carbon steel in both extract solutions with various NaCl concentrations. Moreover, for each type of steel, the AAS extract contributes to a higher pitting corrosion resistance compared with the OPC extract in the presence of chloride ions, likely because of the formation of flocculent precipitates on the steel surface.

  10. Electrochemical investigations of the resistance of Inconel 600, Incoloy 800, and Type 347 stainless steel to pitting corrosion in faulted PWR secondary water at 150 to 250 C

    International Nuclear Information System (INIS)

    Hickling, J.; Wieling, N.

    1981-01-01

    Determinations of critical pitting potentials were carried out at temperatures of 150, 200, and 250 C on three corrosion resistant alloys important in the construction of nuclear steam generators. The results are assessed in terms of the effects on pitting resistance of chloride (as NaCl) and phosphate (as Na/sub 2/ HPO/sub 4/) contents of the water and test temperature. A comparison of material behavior was obtained for each set of test conditions. 18 refs

  11. Bacillus sp. Acting as Dual Role for Corrosion Induction and Corrosion Inhibition with Carbon Steel (CS

    Directory of Open Access Journals (Sweden)

    Santosh K. Karn

    2017-10-01

    Full Text Available Present work investigated the role of five different bacteria species as a corrosion inducer as well as corrosion inhibitor with carbon steel (CS. We observed the ability of different bacteria species on the metal surface attachment, biofilm formation, and determined Peroxidase, Catalase enzyme activity in the detached biofilm from the CS surface. We found that each strain has diverse conduct for surface attachment like DS1 3.3, DS2 2.5, DS3 4.3, DS4 4.0, and DS5 4.71 log cfu/cm2 and for biofilm 8.3 log cfu/cm2. The enzyme Peroxidase, Catalase was found in huge concentration inside the biofilm Peroxidase was maximum for DS4 36.0 U/ml and least for DS3 19.54 U/ml. Whereas, Catalase was highest for DS4, DS5 70.14 U/ml and least 57.2 U/ml for DS2. Scanning electron microscopy (SEM was conducted to examine the biofilm and electrochemical impedance spectroscopy (EIS were utilized to observe corrosion in the presence of bacteria. The electrochemical results confirmed that DS1, DS3, DS4, and DS5 strains have statistically significant MIC-factors (Microbially Influenced Corrosion of 5.46, 8.51, 2.36, and 1.04, while DS2 protective effect factor of 0.89. Weight reduction results with carbon steel likewise supports that corrosion was initiated by DS1 and DS3, while DS2 and DS5 have no any impact though with DS4 we watched less weight reduction however assumed no role in the corrosion. We established the relation of Peroxidase enzyme activity of the isolates. DS1, DS3 and having Peroxidase in the range 22.18, 19.54 U/ml which induce the corrosion whereas DS2 and DS5 having 28.57 and 27.0 U/ml has no any effect and DS4 36 U/ml has inhibitory effect, increasing concentration inhibiting the corrosion. For Catalase DS1, DS3 have 67.28, 61.57 U/ml which induce corrosion while DS2 and DS5 57.71 and 59.14 U/ml also has no effect whereas DS4 70.14 U/ml can inhibit corrosion. Results clearly express that in a specific range both enzymes can induce the corrosion

  12. Compatibility in the Ustilago maydis-maize interaction requires inhibition of host cysteine proteases by the fungal effector Pit2.

    Directory of Open Access Journals (Sweden)

    André N Mueller

    2013-02-01

    Full Text Available The basidiomycete Ustilago maydis causes smut disease in maize, with large plant tumors being formed as the most prominent disease symptoms. During all steps of infection, U. maydis depends on a biotrophic interaction, which requires an efficient suppression of plant immunity. In a previous study, we identified the secreted effector protein Pit2, which is essential for maintenance of biotrophy and induction of tumors. Deletion mutants for pit2 successfully penetrate host cells but elicit various defense responses, which stops further fungal proliferation. We now show that Pit2 functions as an inhibitor of a set of apoplastic maize cysteine proteases, whose activity is directly linked with salicylic-acid-associated plant defenses. Consequently, protease inhibition by Pit2 is required for U. maydis virulence. Sequence comparisons with Pit2 orthologs from related smut fungi identified a conserved sequence motif. Mutation of this sequence caused loss of Pit2 function. Consequently, expression of the mutated protein in U. maydis could not restore virulence of the pit2 deletion mutant, indicating that the protease inhibition by Pit2 is essential for fungal virulence. Moreover, synthetic peptides of the conserved sequence motif showed full activity as protease inhibitor, which identifies this domain as a new, minimal protease inhibitor domain in plant-pathogenic fungi.

  13. Research on corrosion mechanism of suspension insulator steel foot of direct current system and measures for corrosion inhibition

    Science.gov (United States)

    Chen, He; Yang, Yueguang; Su, Guolei; Wang, Xiaoqing; Zhang, Hourong; Sun, Xiaoyu; Fan, Youping

    2017-09-01

    There are increasingly serious electrocorrosion phenomena on insulator hardware caused by direct current transmission due to the wide-range popularization of extra high voltage direct current transmission engineering in our country. Steel foot corrosion is the main corrosion for insulators on positive polarity side of transmission lines. On one hand, the corrosion leads to the tapering off of steel foot diameter, having a direct influence on mechanical property of insulators; on the other hand, in condition of corrosion on steel foot wrapped in porcelain ware, the volume of the corrosion product is at least 50% more than that of the original steel foot, leading to bursting of porcelain ware, threatening safe operation of transmission lines. Therefore, it is necessary to conduct research on the phenomenon and propose feasible measures for corrosion inhibition. Starting with the corrosion mechanism, this article proposes two measures for corrosion inhibition, and verifies the inhibition effect in laboratory conditions, providing reference for application in engineering.

  14. Influence of Welding Process and Post Weld Heat Treatment on Microstructure and Pitting Corrosion Behavior of Dissimilar Aluminium Alloy Welds

    Science.gov (United States)

    Venkata Ramana, V. S. N.; Mohammed, Raffi; Madhusudhan Reddy, G.; Srinivasa Rao, K.

    2018-03-01

    Welding of dissimilar Aluminum alloy welds is becoming important in aerospace, shipbuilding and defence applications. In the present work, an attempt has been made to weld dissimilar aluminium alloys using conventional gas tungsten arc welding (GTAW) and friction stir welding (FSW) processes. An attempt was also made to study the effect of post weld heat treatment (T4 condition) on microstructure and pitting corrosion behaviour of these welds. Results of the present investigation established the differences in microstructures of the base metals in T4 condition and in annealed conditions. It is evident that the thickness of the PMZ is relatively more on AA2014 side than that of AA6061 side. In FS welds, lamellar like shear bands are well noticed on the top of the stir zone. The concentration profile of dissimilar friction stir weld in T4 condition revealed that no diffusion has taken place at the interface. Poor Hardness is observed in all regions of FS welds compared to that of GTA welds. Pitting corrosion resistance of the dissimilar FS welds in all regions was improved by post weld heat treatment.

  15. Effect of Aging on Precipitation Behavior and Pitting Corrosion Resistance of SAF2906 Super Duplex Stainless Steel

    Science.gov (United States)

    Li, Jianchun; Li, Guoping; Liang, Wei; Han, Peide; Wang, Hongxia

    2017-09-01

    The effect of aging temperature and holding time on the precipitation of secondary phases and pitting corrosion resistance of SAF2906 super duplex stainless steel was examined. Chromium nitride and σ phase were observed to preferentially precipitate at the ferrite/austenite interface. An amount of nitrides was also observed within the ferrite grain. The precipitation of chromium nitride occurred before the σ phase. The increase in aging temperature and holding time did not affect the concentration of the nitrides but increased the area fraction of the σ phase at a faster rate. The Cr2N precipitation in SAF2906 is more evident than that of the other duplex stainless steels. The variation tendency of the precipitation concentrations is primarily consistent with the prediction results of Thermo-Calc software. The electrochemical results showed that Cr2N and σ phase significantly reduced the pitting potential. Scanning electron microscope observations revealed that pits appear mainly in regions adjacent to sigma phase and Cr2N.

  16. Synergistic Effect on Corrosion Inhibition Efficiency of Ginger Affinale Extract in Controlling Corrosion of Mild Steel in Acid Medium

    International Nuclear Information System (INIS)

    Subramanian, Ananth Kumar; Arumugam, Sankar; Mallaiya, Kumaravel; Subramaniam, Rameshkumar

    2013-01-01

    The corrosion inhibition nature of Ginger affinale extract for the corrosion of mild steel in 0.5N H 2 SO 4 was investigated using weight loss, electrochemical impedance and potentiodynamic polarization methods. The results revealed that Ginger affinale extract acts as a good corrosion inhibitor in 0.5N H 2 SO 4 medium. The inhibition efficiency increased with an increase in inhibitor concentration. The inhibition could be attributed to the adsorption of the inhibitor on the steel surface

  17. High temperature solution-nitriding and low-temperature nitriding of AISI 316: Effect on pitting potential and crevice corrosion performance

    DEFF Research Database (Denmark)

    Bottoli, Federico; Jellesen, Morten Stendahl; Christiansen, Thomas Lundin

    2018-01-01

    in a 0.1M NaCl solution and crevice corrosion immersion tests in 3wt% FeCl3 solution were studied before and after the bulk and surface treatments.Nitrogen addition in the bulk proved to have a beneficial effect on the pitting resistance of the alloy. The formation of a zone of expanded austenite...... at the material surface through low-temperature nitriding resulted in a considerable improvement of the pitting potential and the crevice corrosion performance of the steels....

  18. Corrosion inhibition behavior of Ketosulfone for Zinc in acidic medium

    African Journals Online (AJOL)

    The corrosion inhibition behavior of Ketosulfone for zinc is investigated by polarization and AC-impedance techniques at 303-333K. The Tafel plots indicates that the Ketosulfone is a mixed type inhibitor. The interaction between metal and inhibitor is explained by Langmuir adsorption isotherm. DG0ads andDH0ads value ...

  19. Corrosion inhibition and adsorption characteristics of camel foot ...

    African Journals Online (AJOL)

    Inhibitive performance of Camel foot (Piliostigma thonningii) leave extract was investigated on corrosion of mild steel in 1.5M hydrochloric at different temperature (25oC to 60oC) using weight loss and hydrogen evolution measurement. Phytochemical screening was carried out on the extract and characterized with Gas ...

  20. A SIMPLE APPROACH TO ASSESSING COPPER PITTING CORROSION TENDENCIES AND DEVELOPING CONTROL STRATEGIES

    Science.gov (United States)

    Localized corrosion of copper premise plumbing in drinking water distribution systems can lead to pinhole leaks, which are a growing problem for many homeowners. Despite the fact that water quality is an important factor associated with localized copper corrosion, definitive appr...

  1. Crack Initiation and Growth Behavior at Corrosion Pit in 7075-T6 High Strength Aluminum Alloy

    Science.gov (United States)

    2013-06-01

    brass, etc.) have a very small impact in the aerospace industry. In other words, their usage is limited in aerospace systems, which at present are...rolling direction of the material has a profound impact on the growth of the pits. The pits have anisotropy and the largest dimension occurs along the...referred to as H13 . This is a specimen that was previously prepared by Sabelkin. Table 3.3: Specifications for the uni-axial test specimens. ∆K values are

  2. Inhibition of the ultrasonic microjet-pits on the carbon steel in the particles-water mixtures

    Science.gov (United States)

    Yan, Dayun; Wang, Jiadao; Liu, Fengbin

    2015-07-01

    In the incubation period of ultrasonic cavitation, due to the impact of microjets on the material surface, the needle-like microjet-pits are formed. Because the formation of microjet-pits relates with the evolution of cavitation erosion on engineering materials, corresponding study will promote the understanding on the mechanism of cavitation erosion. However, little study on the microjet-pits has been carried out, especially in the particles-water mixture. In this study, we firstly demonstrated the microjet-pits on the carbon steel would be significantly inhibited by Al particles in water. Such inhibition effect indicated that particular particles might not only provide growth sites for cavitation bubbles but also affect the collapse of cavitation bubbles near a solid surface. Our study deepened the understanding on the ultrasonic cavitation erosion in the particles-water mixture.

  3. Inhibition of the ultrasonic microjet-pits on the carbon steel in the particles-water mixtures

    Directory of Open Access Journals (Sweden)

    Dayun Yan

    2015-07-01

    Full Text Available In the incubation period of ultrasonic cavitation, due to the impact of microjets on the material surface, the needle-like microjet-pits are formed. Because the formation of microjet-pits relates with the evolution of cavitation erosion on engineering materials, corresponding study will promote the understanding on the mechanism of cavitation erosion. However, little study on the microjet-pits has been carried out, especially in the particles-water mixture. In this study, we firstly demonstrated the microjet-pits on the carbon steel would be significantly inhibited by Al particles in water. Such inhibition effect indicated that particular particles might not only provide growth sites for cavitation bubbles but also affect the collapse of cavitation bubbles near a solid surface. Our study deepened the understanding on the ultrasonic cavitation erosion in the particles-water mixture.

  4. A probabilistic physics-of-failure model for prognostic health management of structures subject to pitting and corrosion-fatigue

    International Nuclear Information System (INIS)

    Chookah, M.; Nuhi, M.; Modarres, M.

    2011-01-01

    A combined probabilistic physics-of-failure-based model for pitting and corrosion-fatigue degradation mechanisms is proposed to estimate the reliability of structures and to perform prognosis and health management. A mechanistic superposition model for corrosion-fatigue mechanism was used as a benchmark model to propose the simple model. The proposed model describes the degradation of the structures as a function of physical and critical environmental stresses, such as amplitude and frequency of mechanical loads (for example caused by the internal piping pressure) and the concentration of corrosive chemical agents. The parameters of the proposed model are represented by the probability density functions and estimated through a Bayesian approach based on the data taken from the experiments performed as part of this research. For demonstrating applications, the proposed model provides prognostic information about the reliability of aging of structures and is helpful in developing inspection and replacement strategies. - Highlights: ► We model an inventory system under static–dynamic uncertainty strategy. ► The demand is stochastic and non-stationary. ► The optimal ordering policy is proven to be a base stock policy. ► A solution algorithm for finding an optimal solution is provided. ► Two heuristics developed produce high quality solutions and scale-up efficiently.

  5. Investigating pitting in X65 carbon steel using potentiostatic polarisation

    Science.gov (United States)

    Mohammed, Sikiru; Hua, Yong; Barker, R.; Neville, A.

    2017-11-01

    Although pitting corrosion in passive materials is generally well understood, the growth of surface pits in actively-corroding materials has received much less attention to date and remains poorly understood. One of the key challenges which exists is repeatedly and reliably generating surface pits in a practical time-frame in the absence of deformation and/or residual stress so that studies on pit propagation and healing can be performed. Another pertinent issue is how to evaluate pitting while addressing general corrosion in low carbon steel. In this work, potentiostatic polarisation was employed to induce corrosion pits (free from deformation or residual stress) on actively corroding X65 carbon steel. The influence of applied potential (50 mV, 100 mV and 150 mV vs open circuit potential) was investigated over 24 h in a CO2-saturated, 3.5 wt.% NaCl solution at 30 °C and pH 3.8. Scanning electron microscopy (SEM) was utilised to examine pits, while surface profilometry was conducted to measure pit depth as a function of applied potential over the range considered. Analyses of light pitting (up to 120 μm) revealed that pit depth increased linearly with increase in applied potential. This paper relates total pit volume (measured using white light interferometry) to dissipated charge or total mass loss (using the current response for potentiostatic polarisation in conjunction with Faraday's law). By controlling the potential of the surface (anodic) the extent of pitting and general corrosion could be controlled. This allowed pits to be evaluated for their ability to continue to propagate after the potentiostatic technique was employed. Linear growth from a depth of 70 μm at pH 3.8, 80 °C was demonstrated. The technique offers promise for the study of inhibition of pitting.

  6. Phosphate ions as inhibiting agents for copper corrosion in chlorinated tap water

    Energy Technology Data Exchange (ETDEWEB)

    Yohai, L. [División Electroquímica y Corrosión, INTEMA, CONICET, UNMdP, Juan B. Justo 4302, B7608FDQ Mar del Plata (Argentina); Schreiner, W.H. [Laboratório de Superfícies e Interfases, Departamento de Física, Universidade Federal do Paraná, 81531-990 Curitiba, PR (Brazil); Vázquez, M., E-mail: mvazquez@fi.mdp.edu.ar [División Electroquímica y Corrosión, INTEMA, CONICET, UNMdP, Juan B. Justo 4302, B7608FDQ Mar del Plata (Argentina); Valcarce, M.B. [División Electroquímica y Corrosión, INTEMA, CONICET, UNMdP, Juan B. Justo 4302, B7608FDQ Mar del Plata (Argentina)

    2013-05-15

    PO{sub 4}{sup 3−} ions as corrosion inhibitor were investigated on copper in tap water in the presence of NaClO. The inhibitor was evaluated by electrochemical techniques and weight loss tests. Raman spectroscopy and X-ray photoelectron spectroscopy were used to study the passive layer. In inhibited tap water, the passive layer is thick and compact if NaClO is present. Weight-loss tests showed the inhibition of uniform dissolution and no pitting attack. When adding NaClO, Cu{sub 3}(PO{sub 4}){sub 2} is incorporated to the passive film. Thus, phosphate ions are effective as inhibitors for copper in tap water, even when using high dosages of biocides. - Highlights: ► Changes in the copper corrosion after adding phosphate to tap water were analyzed. ► When NaClO and phosphates are present, Cu{sub 3}(PO{sub 4}){sub 2} participates of the surface film. ► In the absence of biocide the surface film contains a mixture of Cu{sub 2}O, CuO and Cu(OH){sub 2}. ► PO{sub 4}{sup 3−} is an effective inhibitor for Cu in tap water containing high NaClO dosages.

  7. Phosphate ions as inhibiting agents for copper corrosion in chlorinated tap water

    International Nuclear Information System (INIS)

    Yohai, L.; Schreiner, W.H.; Vázquez, M.; Valcarce, M.B.

    2013-01-01

    PO 4 3− ions as corrosion inhibitor were investigated on copper in tap water in the presence of NaClO. The inhibitor was evaluated by electrochemical techniques and weight loss tests. Raman spectroscopy and X-ray photoelectron spectroscopy were used to study the passive layer. In inhibited tap water, the passive layer is thick and compact if NaClO is present. Weight-loss tests showed the inhibition of uniform dissolution and no pitting attack. When adding NaClO, Cu 3 (PO 4 ) 2 is incorporated to the passive film. Thus, phosphate ions are effective as inhibitors for copper in tap water, even when using high dosages of biocides. - Highlights: ► Changes in the copper corrosion after adding phosphate to tap water were analyzed. ► When NaClO and phosphates are present, Cu 3 (PO 4 ) 2 participates of the surface film. ► In the absence of biocide the surface film contains a mixture of Cu 2 O, CuO and Cu(OH) 2 . ► PO 4 3− is an effective inhibitor for Cu in tap water containing high NaClO dosages

  8. Electrochemical polarization measurements on pitting corrosion susceptibility of nickel-rich Alloy 825

    International Nuclear Information System (INIS)

    McCright, R.D.; Fleming, D.L.

    1991-10-01

    Alloy 825 contains approximately 40% Ni, 30% Fe, 20% Cr, 3.5% Mo, 2% Cu, and 1% Ti. Alloy 825 has a number of performance features that make it attractive as a candidate material for nuclear waste containers. However, under certain environmental conditions Alloy 825 is susceptible to localized forms of corrosion, and the focus of this paper is determination of those conditions. Electrochemical polarization was used to determine the critical potential for passive film breakdown, a process which leads to localized corrosion attack. Results indicated that quite high levels of chloride ion concentrations coupled with low pH are required to lower the critical potential to approach the corrosion potential

  9. XPS and Auger investigation of mechanisms affecting corrosion inhibition of metals

    International Nuclear Information System (INIS)

    Holmes, R.M.; Surman, D.J.

    1989-01-01

    Atmospheric corrosion of metal surfaces need not be extremely obvious to cause extensive damage to many products. Very small corrosion pits and spots can cause defects in critical copper sources, often resulting in the catastrophic failure of complete electronic assemblies. Microscopic corrosion in steel can lead to the complete failure of subsequently added coatings or furnishings, the automotive industry has become aware. In addition, corrosion at its earliest stages can initiate other corrosion at a later date, resulting in inferior finishings or coatings. A major interest in atmospheric corrosion is in the mechanism by which the initial corrosion initiated and propagated. The initial phase involves the attack of the very other surface layers, hence it is difficult to observe with conventional techniques such as SEM/EDX. This paper presents some of the results obtained by both Auger electron spectroscopy and x- ray photoelectron spectroscopy, of steel and copper samples exposed to corrosive materials under controlled conditions

  10. Standard test methods for pitting and crevice corrosion resistance of stainless steels and related alloys by use of ferric Chloride solution

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2003-01-01

    1.1 These test methods cover procedures for the determination of the resistance of stainless steels and related alloys to pitting and crevice corrosion (see Terminology G 15) when exposed to oxidizing chloride environments. Six procedures are described and identified as Methods A, B, C, D, E, and F. 1.1.1 Method A—Ferric chloride pitting test. 1.1.2 Method B—Ferric chloride crevice test. 1.1.3 Method C—Critical pitting temperature test for nickel-base and chromium-bearing alloys. 1.1.4 Method D—Critical crevice temperature test for nickel-base and chromium-bearing alloys. 1.1.5 Method E—Critical pitting temperature test for stainless steels. 1.1.6 Method F—Critical crevice temperature test for stainless steels. 1.2 Method A is designed to determine the relative pitting resistance of stainless steels and nickel-base, chromium-bearing alloys, whereas Method B can be used for determining both the pitting and crevice corrosion resistance of these alloys. Methods C, D, E and F allow for a rankin...

  11. In situ AFM study of pitting corrosion and corrosion under strain on a 304L stainless steel

    International Nuclear Information System (INIS)

    Martin, F.A.; Cousty, J.; Masson, J-L.; Bataillon, C.

    2004-01-01

    Our study is centred on surface localised corrosion under strain of a standard stainless steel (304L). The interest we take in these corrosion phenomena is led by the general misunderstanding of its primary initiation steps. The goal of this study is to determine precisely the relationships between local geometrical defects (grain boundaries, dislocation lines, etc) or chemical defects (inclusions) with the preferential sites of corrosion on the strained material. By combining three techniques at the same time: Atomic Force Microscopy, an electrochemical cell and a traction plate, we can observe in situ the effect of localised stress and deformation on the sample surface exposed to a corrosive solution. We managed to build an original set-up compatible with all the requirements of these three different techniques. Furthermore, we prepared the surface of our sample as flat as possible to decrease at maximum the topographical noise in order to observe the smallest defect on the surface. By using a colloidal suspension of SiO 2 , we obtained surfaces with a typical corrugation (RMS) of about 1 A for areas of at least 1 μm 2 . Our experimental study has been organised in two primary investigations: - In situ study of the morphology evolution of the surface under a corrosive chloride solution (borate buffer with NaCl salt). The influence of time, NaCl concentration, and potential was investigated; - In situ exploration of a 304L strained surface. It revealed the first stages of the surface plastic evolutions like activation of sliding dislocations, materialized by parallel steps of about 2 nm high in the same grain. The secondary sliding plane systems were also noticeable for higher deformation rates. Recent results concerning in situ AFM observation of corroded surfaces under strain in a chloride media will be presented. (authors)

  12. In situ AFM study of pitting corrosion and corrosion under strain on a 304L stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Martin, F.A. [CEA de Saclay, DRECAM/SPCSI, 91191 Gif-sur-Yvette cedex (France); Cousty, J.; Masson, J-L. [CEA de Saclay, DRECAM/SPCSI, 91191 Gif-sur-Yvette cedex (France); Bataillon, C. [CEA de Saclay, DEN/DPC/LECA, 91191 Gif-sur-Yvette cedex (France)

    2004-07-01

    Our study is centred on surface localised corrosion under strain of a standard stainless steel (304L). The interest we take in these corrosion phenomena is led by the general misunderstanding of its primary initiation steps. The goal of this study is to determine precisely the relationships between local geometrical defects (grain boundaries, dislocation lines, etc) or chemical defects (inclusions) with the preferential sites of corrosion on the strained material. By combining three techniques at the same time: Atomic Force Microscopy, an electrochemical cell and a traction plate, we can observe in situ the effect of localised stress and deformation on the sample surface exposed to a corrosive solution. We managed to build an original set-up compatible with all the requirements of these three different techniques. Furthermore, we prepared the surface of our sample as flat as possible to decrease at maximum the topographical noise in order to observe the smallest defect on the surface. By using a colloidal suspension of SiO{sub 2}, we obtained surfaces with a typical corrugation (RMS) of about 1 A for areas of at least 1 {mu}m{sup 2}. Our experimental study has been organised in two primary investigations: - In situ study of the morphology evolution of the surface under a corrosive chloride solution (borate buffer with NaCl salt). The influence of time, NaCl concentration, and potential was investigated; - In situ exploration of a 304L strained surface. It revealed the first stages of the surface plastic evolutions like activation of sliding dislocations, materialized by parallel steps of about 2 nm high in the same grain. The secondary sliding plane systems were also noticeable for higher deformation rates. Recent results concerning in situ AFM observation of corroded surfaces under strain in a chloride media will be presented. (authors)

  13. The effect of inhibitor sodium nitrate on pitting corrosion of dissimilar material weldment joint of stainless steel AISI 304 and mild steel SS 400

    Energy Technology Data Exchange (ETDEWEB)

    Hilca, B. R., E-mail: bangkithilca@yahoo.com; Triyono, E-mail: triyonomesin@uns.ac.id [Mechanical Engineering Department, Sebelas Maret University, Surakarta 57126 (Indonesia)

    2016-03-29

    This study experimentally evaluated the effect of Sodium Nitrate inhibitor (NaNO{sub 3}) of 0.1%, 0.3%, and 0.5% on NaCl 3.5% toward pitting corrosion of dissimilar metal welding joint between stainless steel AISI 304 and mild steel SS 400. Electrochemical corrosion was tested using potentiodynamic polarization. Further the Scanning Electron Microscope (SEM) conducted to analyze the specimen. Chemical composition analysis used Energy Dispersive X-ray Spectrometry (EDS). The highest efficiency of sodium nitrate for ER 308 attained 63.8% and 64.89%for ER 309L. The specimen surface which observed through SEM showed decrease of pitting corrosion respectively with the addition of sodium nitrate content as inhibitor.

  14. Corrosion inhibition of powder metallurgy Mg by fluoride treatments.

    Science.gov (United States)

    Pereda, M D; Alonso, C; Burgos-Asperilla, L; del Valle, J A; Ruano, O A; Perez, P; Fernández Lorenzo de Mele, M A

    2010-05-01

    Pure Mg has been proposed as a potential degradable biomaterial to avoid both the disadvantages of non-degradable internal fixation implants and the use of alloying elements that may be toxic. However, it shows excessively high corrosion rate and insufficient yield strength. The effects of reinforcing Mg by a powder metallurgy (PM) route and the application of biocompatible corrosion inhibitors (immersion in 0.1 and 1M KF solution treatments, 0.1M FST and 1M FST, respectively) were analyzed in order to improve Mg mechanical and corrosion resistance, respectively. Open circuit potential measurements, polarization techniques (PT), scanning electrochemical microscopy (SECM) and electrochemical impedance spectroscopy (EIS) were performed to evaluate its corrosion behavior. SECM showed that the local current of attacked areas decreased during the F(-) treatments. The corrosion inhibitory action of 0.1M FST and 1M FST in phosphate buffered solution was assessed by PT and EIS. Under the experimental conditions assayed, 0.1M FST revealed better performance. X-ray photoelectron spectroscopy, energy dispersive X-ray and X-ray diffraction analyses of Mg(PM) with 0.1M FST showed the presence of KMgF(3) crystals on the surface while a MgF(2) film was detected for 1M FST. After fluoride inhibition treatments, promising results were observed for Mg(PM) as degradable metallic biomaterial due to its higher yield strength and lower initial corrosion rate than untreated Mg, as well as a progressive loss of the protective characteristics of the F(-)-containing film which ensures the gradual degradation process. Copyright (c) 2009 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  15. Inhibition of stress corrosion cracking of alloy AA8090 T-8171 by addition of rare earth salts

    International Nuclear Information System (INIS)

    Davo, B.; Conde, A.; Damborenea, J.J. de

    2005-01-01

    Aluminium-lithium alloys are suitable for aeronautical purposes because of their good mechanical properties and high damage tolerance. Although these alloys are less susceptible to stress corrosion cracking than conventional alloys, Al-Li-Cu-Mg alloy (8090-T8171) still experiences this problem in a NaCl + H 2 O 2 solution. In this work it has been demonstrated that the addition of 10,000 ppm of CeCl 3 to the medium inhibits the stress corrosion cracking of 8090 alloy by precipitation of cerium oxides/hydroxides. The deposition of these compounds on the alloy surface decreases the pit density and slows the crack growth through the grain boundaries by hindering the anodic dissolution of T phases

  16. Corrosion Inhibition of Mild Steel in Seawater using Jatropha Stem

    Directory of Open Access Journals (Sweden)

    Olawale Olamide

    2016-10-01

    Full Text Available The present work investigate the inhibition of Jatropha Stem Extract (JSE in sea water using mild steel coupons of dimension 5 × 5 × 0.5 cm. The cupons were immersed in test solutions of sea water and varied concentrations of extracts of 0.1g/l to 0.9g/l was used. The functional groups of the compounds was analyzed using an FTIR. The results showed that as the concentration of the extract increases, there was a reduction in the corrosion rates. Furthermore, as the extract concentrations increased from 0.1g/l to 0.4g/l at 48hrs exposure time, the weight loss decreased by 14.3% in the medium. However, the Jatropha Stem Extract was absorbed on the substrate surface to inhibit corrosion, the morphology of phases formed from the scanning Electron Microscopy examination confirmed this trend. Hence, JSE is a good and safe inhibitor in sea water solution. The FT-IR results also indicates the presence of active corrosion inhibitor present in the Jatropha Stem.

  17. Adsorption and corrosion inhibiting effect of riboflavin on Q235 mild steel corrosion in acidic environments

    Energy Technology Data Exchange (ETDEWEB)

    Chidiebere, Maduabuchi A. [Institute of Metal Research, Chinese Academy of Sciences, 62 Wencui Rd, Shenyang 110016 (China); Electrochemistry and Materials Science Research Laboratory, Department of Chemistry, Federal University of Technology Owerri, PMB 1526 Owerri (Nigeria); Oguzie, Emeka E. [Electrochemistry and Materials Science Research Laboratory, Department of Chemistry, Federal University of Technology Owerri, PMB 1526 Owerri (Nigeria); Liu, Li [Institute of Metal Research, Chinese Academy of Sciences, 62 Wencui Rd, Shenyang 110016 (China); Li, Ying, E-mail: liying@imr.ac.cn [Institute of Metal Research, Chinese Academy of Sciences, 62 Wencui Rd, Shenyang 110016 (China); Wang, Fuhui [Institute of Metal Research, Chinese Academy of Sciences, 62 Wencui Rd, Shenyang 110016 (China)

    2015-04-15

    The inhibiting effect of Riboflavin (RF) on Q235 mild steel corrosion in 1 M HCl and 0.5 M H{sub 2}SO{sub 4} at 30 °C temperature was investigated using electrochemical techniques (electrochemical impedance spectroscopy and potentiodynamic polarization). The obtained results revealed that RF inhibited the corrosion reaction in both acidic solutions. Maximum inhibition efficiency values in 1 M HCl and 0.5 M H{sub 2}SO{sub 4} were 83.9% and 71.4%, respectively, obtained for 0.0012 M RF. Polarization data showed RF to be a mixed-type inhibitor, while EIS results revealed that the RF species adsorbed on the metal surface. The adsorption of RF followed Langmuir adsorption isotherm. Atomic force microscopy (AFM), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM) studies confirmed the formation of a protective layer adsorbed on the steel surface. Quantum chemical calculations were used to correlate the inhibition ability of RF with its electronic structural parameters. - Highlights: • The inhibitory mechanism was influenced by the nature of acid anions. • RF has reasonable inhibition effect especially in 1 M HCl solution. • Polarization studies showed that RF functioned as a mixed type inhibitor. • Improved surface morphology was observed in the presence of RF.

  18. Electrochemical evaluation of under-deposit corrosion and its inhibition using the wire beam electrode method

    Energy Technology Data Exchange (ETDEWEB)

    Tan Yongjun, E-mail: yj.tan@curtin.edu.a [Western Australian Corrosion Research Group, Department of Chemistry, Curtin University, GPO Box U1987, Perth (Australia); Fwu, Young; Bhardwaj, Kriti [Western Australian Corrosion Research Group, Department of Chemistry, Curtin University, GPO Box U1987, Perth (Australia)

    2011-04-15

    Research highlights: A new experiment method for evaluating under-deposit corrosion and its inhibitors. Under-deposit corrosion did not occur in a CO{sub 2} saturated pure brine solution. Inhibitor imidazoline addition and O{sub 2} contamination initiated under-deposit corrosion. Inhibitor imidazoline reduced general corrosion but enhanced localised corrosion. - Abstract: A new experimental method has been applied to evaluate under-deposit corrosion and its inhibition by means of an electrochemically integrated multi-electrode array, namely the wire beam electrode (WBE). Maps showing galvanic current and corrosion potential distributions were measured from a WBE surface that was partially covered by sand. Under-deposit corrosion did not occur during the exposure of the WBE to carbon dioxide saturated brine under ambient temperature. The introduction of corrosion inhibitor imidazoline and oxygen into the brine was found to significantly affect the patterns and rates of corrosion, leading to the initiation of under-deposit corrosion over the WBE.

  19. Corrosion behavior and pitting susceptibility of in-situ Ti-based metallic glass matrix composites in 3.5 wt.% NaCl solutions

    Science.gov (United States)

    Xu, K. K.; Lan, A. D.; Yang, H. J.; Han, P. D.; Qiao, J. W.

    2017-11-01

    The Ti62Zr12V13Cu4Be9, Ti58Zr16V10Cu4Be12, Ti46Zr20V12Cu5Be17, and Ti40Zr24V12Cu5Be19 metallic glass matrix composites (MGMCs) were prepared by copper mould casting. The corrosion resistance and the pitting susceptibility of Ti-based MGMCs were tested on their cross-sectional areas in 3.5 wt.% NaCl solutions by potentiodynamic polarization measurements. The composites with lower Ti contents (Ti40Zr24V12Cu5Be19 and Ti46Zr20V12Cu5Be17) exhibit a low resistance to the chloride induced pitting and local corrosion. The preferential dissolution of amorphous matrix is explained by the high chemical reactivity of beryllium element compared to that of stable dendrites and by the detected lower Ti and V contents. However, fairly good passivity was found in the composite with higher Ti contents (Ti62Zr12V13Cu4Be9). XPS measurements revealed that protective Ti-enriched oxide film was formed on the composite surface, additionally, lower content of beryllium element in amorphous matrix hinder the selective corrosion of amorphous matrix. The assessment of experimental observation leads to a proposed corrosion mechanism involving selective dissolution of amorphous matrix and chloride induced pitting process.

  20. Synergistic Effect on Corrosion Inhibition Efficiency of Ginger Affinale Extract in Controlling Corrosion of Mild Steel in Acid Medium

    Energy Technology Data Exchange (ETDEWEB)

    Subramanian, Ananth Kumar; Arumugam, Sankar [Kandaswami Kandar' s College, Namakkal (India); Mallaiya, Kumaravel; Subramaniam, Rameshkumar [PSG College of Technology Peelamedu, Coimbatore (India)

    2013-12-15

    The corrosion inhibition nature of Ginger affinale extract for the corrosion of mild steel in 0.5N H{sub 2}SO{sub 4} was investigated using weight loss, electrochemical impedance and potentiodynamic polarization methods. The results revealed that Ginger affinale extract acts as a good corrosion inhibitor in 0.5N H{sub 2}SO{sub 4} medium. The inhibition efficiency increased with an increase in inhibitor concentration. The inhibition could be attributed to the adsorption of the inhibitor on the steel surface.

  1. Corrosion inhibition of aluminum 6063 using some pharmaceutical compounds

    International Nuclear Information System (INIS)

    Fouda, A.S.; Al-Sarawy, A.A.; Ahmed, F.Sh.; El-Abbasy, H.M.

    2009-01-01

    The corrosion inhibition characteristics of some pharmaceutical compounds on aluminum 6063 in 0.5 mol l -1 H 3 PO 4 has been studied using weight loss and galvanostatic polarization techniques. Results showed that the inhibition occurs through adsorption of the inhibitor molecules on the metal surface. The inhibition efficiency increased with increasing inhibitor concentration, but decreased with increasing temperature. The adsorption of first group pharmaceutical compounds on the metal surface is found to obey Frumkin's adsorption isotherm, but the adsorption of second group pharmaceutical compounds is found to obey Temkin's adsorption isotherm. Thermodynamic parameters for adsorption process were determined. Galvanostatic polarization studies showed that first and second groups' pharmaceutical compounds are mixed-type inhibitors and the results obtained from the two techniques are in good agreement

  2. Density-functional theory investigation of Al pitting corrosion in electrolyte containing chloride ions

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Min [National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083 (China); Jin, Ying, E-mail: yjin@ustb.edu.cn [National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083 (China); Zhang, Chuanhui [National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083 (China); Leygraf, Christofer [Division of Surface and Corrosion Science, Department of Chemistry, KTH Royal Institute of Technology, SE-10044 Stockholm (Sweden); Wen, Lei [National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083 (China)

    2015-12-01

    Highlights: • Cl{sup −} led to the elongation of Al−O bond and the weakened binding between Al layers in scenario i. • Al−O interaction weakened whereas an intensive hybridization peak at −0.18 Ha between Al-3p with Cl-3p showed in scenario ii. • Substructures such as AlCl{sub 3} and Al{sub 2}Cl{sub 5} formed in scenario iii when the Cl{sup −} coverage was larger than 2/3 ML of a monolayer. - Abstract: The behavior of chloride ions (Cl{sup −}) and oxygen species (the oxygen atom, O or molecular oxygen, O{sub 2}) on Al(1 1 1) surface has been studied by density functional theory calculations in order to deepen the molecular understanding of fundamental processes leading to pitting of aluminum (Al). The adsorption behavior of individual species, Cl{sup −}, O atom and O{sub 2} was determined first. Subsequently, three possible scenarios in different pitting stages were modeled exploring the repassivation and dissolution of Al in neutral electrolyte containing Cl{sup −}. In scenario i, it was found that Cl{sup −} can hardly destroy even an O-monolayer on Al(1 1 1) surface, however may lead to the elongation of Al−O bond and the weakened binding between the first Al layer and subsequent Al layers. Both O{sub 2} and Cl{sup −} were simultaneously introduced onto Al(1 1 1) in scenario ii. The result showed a weakened Al−O interaction and an intensive hybridization peak at −0.18 Ha between Al-3p with Cl-3p suggesting insufficient repassivation behavior of Al under this condition. Finally, scenario iii mimicked different local environmental conditions in pits formed on Al. At low coverage of Cl{sup −}, chloride ions had little effect on surface relaxation. The interaction among chloride ions and Al surface became stronger as Cl{sup −} coverage increased. Surface Al atoms dissolved gradually and substructures such as AlCl{sub 3} and Al{sub 2}Cl{sub 5} formed when the coverage was larger than 2/3 ML of a monolayer.

  3. Comparison of susceptibility to pitting corrosion of AA2024-T4, AA7075-T651 and AA7475-T761 aluminium alloys in neutral chloride solutions using electrochemical noise analysis

    International Nuclear Information System (INIS)

    Na, Kyung-Hwan; Pyun, Su-Il

    2008-01-01

    The susceptibility to pitting corrosion of AA2024-T4, AA7075-T651 and AA7475-T761 aluminium alloys was investigated in aqueous neutral chloride solution for the purpose of comparison using electrochemical noise measurement. The experimentally measured electrochemical noises were analysed based upon the combined stochastic theory and shot-noise theory using the Weibull distribution function. From the occurrence of two linear regions on one Weibull probability plot, it was suggested that there existed two stochastic processes of uniform corrosion and pitting corrosion; pitting corrosion was distinguished from uniform corrosion in terms of the frequency of events in the stochastic analysis. Accordingly, the present analysis method allowed us to investigate pitting corrosion independently. The susceptibility to pitting corrosion was appropriately evaluated by determining pit embryo formation rate in the stochastic analysis. The susceptibility was decreased in the following order: AA2024-T4 (the naturally aged condition), AA7475-T761 (the overaged condition) and AA7075-T651 (the near-peak-aged condition)

  4. Study on the Synthesis and Corrosion Inhibition Performance of Mannich-Modified Imidazoline

    Directory of Open Access Journals (Sweden)

    Xiangjun Kong

    2016-07-01

    Full Text Available A novel Mannich-modified imidazoline (MMI as cationic emulsifier was synthesised for corrosion harm reduction, through three steps — acylation, cyclization, and Mannich reaction. The surface activity was characterized by determination of surface tensions and critical micelle concentration (CMC. The corrosion inhibition performance of five types of steels in the simulated corrosion solution in the presence of the MMI was investigated by static weight loss tests. The results showed that the MMI had good surface activities, with CMC of 19.8 μg g−1 and surface tension of 36.4 mN m−1. The corrosion test results indicated that the corrosion rates of different materials were decreased significantly, and degrees of corrosion inhibition were always higher than 80.0 %. The main inhibition mechanism was most likely due to the adsorption of the corrosion inhibitor on the steel surface, leading to the prevention of corrosion medium from the metal surface.

  5. Novel package for inhibition of aluminium corrosion in alkaline solutions

    International Nuclear Information System (INIS)

    Abdel-Gaber, A.M.; Khamis, E.; Abo-Eldahab, H.; Adeel, Sh.

    2010-01-01

    Inhibition of aluminium corrosion in 2 M sodium hydroxide solution by a package composed of the cationic surfactant cetyl trimethyl ammonium bromide (CTAB) and lupine seed extract has been investigated employing different electrochemical techniques and chemical gasometry measurements. Potentiodynamic polarization curve measurements showed that lupine seed extract controls both the anodic dissolution of aluminium and the hydrogen gas evolved at the cathodic sites of aluminium surface. Nyquist plots showed two capacitive semicircles in the high and low frequency regions separated by an inductive loop at intermediate frequencies. The inductive loop may be explained by the occurrence of adsorbed intermediates on the surface. A proposed equivalent circuit was used to analyse the impedance spectra for aluminium in NaOH solutions. The corrosion inhibition data have been analysed using different isotherms. The results showed excellent agreement between the kinetic-thermodynamic model and Flory-Huggins isotherm. Gasometry measurements showed that the Inhibitive effect of the surfactant increases at a composition around its critical micelle concentration (cmc). The presence of both the surfactant and lupine seed extract did not indicate synergistic action between them. The mode of adsorption of the surfactant molecules corresponding to their structure is also discussed.

  6. Novel package for inhibition of aluminium corrosion in alkaline solutions

    Energy Technology Data Exchange (ETDEWEB)

    Abdel-Gaber, A.M., E-mail: ashrafmoustafa@yahoo.com [Chemistry Department, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt); Khamis, E.; Abo-Eldahab, H.; Adeel, Sh. [Chemistry Department, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt)

    2010-11-01

    Inhibition of aluminium corrosion in 2 M sodium hydroxide solution by a package composed of the cationic surfactant cetyl trimethyl ammonium bromide (CTAB) and lupine seed extract has been investigated employing different electrochemical techniques and chemical gasometry measurements. Potentiodynamic polarization curve measurements showed that lupine seed extract controls both the anodic dissolution of aluminium and the hydrogen gas evolved at the cathodic sites of aluminium surface. Nyquist plots showed two capacitive semicircles in the high and low frequency regions separated by an inductive loop at intermediate frequencies. The inductive loop may be explained by the occurrence of adsorbed intermediates on the surface. A proposed equivalent circuit was used to analyse the impedance spectra for aluminium in NaOH solutions. The corrosion inhibition data have been analysed using different isotherms. The results showed excellent agreement between the kinetic-thermodynamic model and Flory-Huggins isotherm. Gasometry measurements showed that the Inhibitive effect of the surfactant increases at a composition around its critical micelle concentration (cmc). The presence of both the surfactant and lupine seed extract did not indicate synergistic action between them. The mode of adsorption of the surfactant molecules corresponding to their structure is also discussed.

  7. CORROSION INHIBITION OF ALUMINUM ALLOY 3SR IN HCl BY POLYVINYLPYRROLIDONE AND POLYACRYLAMIDE: EFFECT OF MOLECULAR STRUCTURE ON INHIBITION EFFICIENCY

    OpenAIRE

    S. A. UMOREN

    2009-01-01

    The inhibitive performance of two water soluble polymers–polyacrylamide (PA) and polyvinylpyrrolidone (PVP) on the corrosion behavior of aluminum alloy 3SR in HCl solution was investigated using weight loss, hydrogen evolution, and thermometric methods at 30–60°C. Results obtained indicate that both polymers inhibited acid-induced corrosion of aluminum at the temperatures studied. PVP was found to be a better corrosion inhibitor than PA. All measurements from the three techniques show that in...

  8. Pitting corrosion studies on nitrogen implanted 316L SS for biomedical applications

    International Nuclear Information System (INIS)

    Subbaiyan, M.; Veerabadran, K.M.; Thampi, N.S.; Kanwar Krishnan; Kamachi Mudali, U.; Dayal, R.K.

    1997-01-01

    Traditionally, human bone fracture and defects have been corrected using metal and alloy fixing devices. Austenitic stainless steels (such as 316L alloy studied here) are favoured because of low cost, compared to titanium alloys, ease of fabrication and fair corrosion resistance. Localized attack on 316l stainless steel, however, results in iron, chromium and nickel ions leaching into surrounding body fluids. This study reports on the successful use of nitrogen ion implantation into 316lSS to evaluate the optimum dose needed to minimise this localised attack, in a physiological saline solution. (UK)

  9. Inhibitory effect of konjac glucomanan on pitting corrosion of AA5052 aluminium alloy in NaCl solution.

    Science.gov (United States)

    Zhang, Kegui; Yang, Wenzhong; Xu, Bin; Chen, Yun; Yin, Xiaoshuang; Liu, Ying; Zuo, Huanzhen

    2018-05-01

    A natural carbohydrate polymer, konjac glucomanan, has been extracted from commercial product and studied as a green corrosion inhibitor for AA5052 aluminium alloy in 3.5 wt% NaCl solution by high-performance gel permeation chromatography (GPC), thermo gravimetric analysis (TGA), Fourier-transform infrared (FT-IR) spectra, electrochemical measurement and surface characterization techniques. The results of GPC measurements suggest the weight-average molecular weight and the number-average molecular weight of KGM with 98.2% purity are 1.61 × 10 5  g/mol and 1.54 × 10 5  g/mol, respectively. Potentiodynamic polarization curves show konjac glucomanan behaves as a mixed-type inhibitor with dominant anodic effect and that its maximum efficiency at 200 ppm is 94%. Electrochemical impedance spectroscopy (EIS) studies reveal the resistance of oxide film is approximately two orders of magnitude greater than the resistance of adsorbed inhibitor layer and that they both increase with KGM concentration. Moreover, in-situ electrochemical noise (EN) detection demonstrates that the growth and propagation stages of the pitting corrosion germinating on metal surface are blocked by polysaccharide additive, which is confirmed by the surface analysis of aluminium alloy using scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and Raman spectroscopy. At last, it is found that the addition of KGM makes it harder for water droplet containing NaCl to wet the metallic substrate. Copyright © 2018 Elsevier Inc. All rights reserved.

  10. Corrosion Inhibition by Sodium Gluconate-Zn2+-DTPMP System

    Directory of Open Access Journals (Sweden)

    P. Manjula

    2009-01-01

    Full Text Available The inhibition efficiency of a phosphonic acid, Diethylene Triamine Pentamethylene Phosphonic acid (DTPMP in controlling corrosion of carbon steel immersed in an aqueous solution containing 60 ppm of Cl- has been evaluated by weight loss method in the absence and presence of Zn2+. The formulation consisting of DTPMP and Zn2+ has excellent inhibition efficiency (IE. A synergistic effect is noticed between Zn2+ and DTPMP. Addition of sodium gluconate (SG enhances the IE of Zn2+ and DTPMP system. The DTPMP-Zn2+-SG system function as a mixed inhibitor as revealed by polarization study. AC impedance spectrum, optical and atomic force micrographs reveal the formation of a protective film on the metal surface. FTIR spectra reveal that the protective film consists of Fe2+-DTPMP complex, Fe2+-SG complex and Zn(OH2.

  11. Some investigations on the pitting attack of magnesium and its alloys; Contribution a l'etude de la corrosion par piqures du magnesium et de ses alliages

    Energy Technology Data Exchange (ETDEWEB)

    Blanchet, J [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1964-03-01

    The pitting attack of magnesium and its alloys has been studied by means of potentio-kinetic polarisation curves; the following parameters have been considered: structural state and composition of the metal, chloride concentration and pH of the medium. The electrochemical data obtained demonstrate that when pH = 12, a localized corrosion might appear as soon as a 10{sup -3} M NaCl concentration is reached; on the other hand, when pH = 13, a much higher concentration (five times) has no effect. In the same conditions, the coupling of magnesium with various noble materials (graphite, platinum, 18/10 stainless steel) also dramatically increases its susceptibility to pitting, but only when chloride ions are present in the solution. Usual corrosion tests have confirmed these electrochemical results. A micrographic study of the pits has shown that their morphology is connected with the metallurgical state of the specimens. (author) [French] La corrosion par piqures du magnesium est etudiee a l'aide des courbes de polarisation potentiocinetiques en fonction des parametres suivants etat structural et composition du metal, concentration en chlorure et pH de la solution. De ces mesures electrochimiques on deduit qu'a pH 12, des la concentration 10{sup -3} M en NaCl, il existe un risque de corrosion localisee, tandis qu'a pH 13 une concentration cinq fois plus forte doit etre sans effet. Dans les memes conditions on montre que le couplage du magnesium avec differents elements nobles (graphite, platine, acier inoxydable 18/10) accroit fortement sa susceptibilite a l'attaque par piqures, excepte dans les solutions exemptes d'ions chlorures. Des essais classiques de corrosion dans les differentes solutions envisagees precedemment confirment les resultats de cette etude electrochimique. L'examen micrographique des piqures montre que leur morphologie est liee a l'etat metallurgique des echantillons. (auteur)

  12. Pitting corrosion behaviour study of aluminium matrix composites (A3xx.x/SiCp); Estudio del comportamiento a la corrosion por picadura de materiales compuestos de matriz de aluminio (A3xx.x/SiCp)

    Energy Technology Data Exchange (ETDEWEB)

    Pardo, A.; Merino, M. C.; Merino, S.; Lopez, M. D.; Viejo, F.; Carboneras, M.; Arrabal, R.

    2004-07-01

    The influence of the SiCp proportion on the pitting corrosion of A3xx.x/SiC/xxp composites was studies by means of potenciodinamic polarization and double cyclic polarization in saline environment at 25 degree centigree A360/SiC/xxp matrix does not contain copper, whereas the A380/SiC/xxp matric contains 1,39-1,44 wt %Cu. The kinetic study was carried out by gravimetric measurements. The nature of corrosion products was analysed by low angle XRD and Scanning Electron Microscopy (SEM). The corrosion is due to nucleation and growth of Al{sub 2}O{sub 3}-3H{sub 2}O on the material surface. The corrosion increases with the reinforcement proportion, chloride concentration and copper content. (Author) 10 refs.

  13. Corrosion Inhibition and Adsorption Properties of Ethanolic Extract of Calotropis for Corrosion of Aluminium in Acidic Media

    OpenAIRE

    Sudesh Kumar; Suraj Prakash Mathur

    2013-01-01

    The corrosion inhibition of aluminium in sulfuric acid solution in the presence of different plant parts, namely, leaves, latex, and fruit was studied using weight loss method and thermometric method. The ethanolic extracts of Calotropis procera and Calotropis gigantea act as an inhibitor in the acid environment. The inhibition efficiency increases with increase in inhibitor concentration. The plant parts inhibit aluminium, and inhibition is attributed, due to the adsorption of the plant part...

  14. Dictionary corrosion and corrosion control

    International Nuclear Information System (INIS)

    1985-01-01

    This dictionary has 13000 entries in both languages. Keywords and extensive accompanying information simplify the choice of word for the user. The following topics are covered: Theoretical principles of corrosion; Corrosion of the metals and alloys most frequently used in engineering. Types of corrosion - (chemical-, electro-chemical, biological corrosion); forms of corrosion (superficial, pitting, selective, intercrystalline and stress corrosion; vibrational corrosion cracking); erosion and cavitation. Methods of corrosion control (material selection, temporary corrosion protection media, paint and plastics coatings, electro-chemical coatings, corrosion prevention by treatment of the corrosive media); Corrosion testing methods. (orig./HP) [de

  15. Improving the Corrosion Inhibitive Strength of Sodium Sulphite in Hydrogen Cyanide Solution Using Sodium Benzoate

    OpenAIRE

    Muhammed Olawale Hakeem AMUDA; Olusegun Olusoji SOREMEKUN; Olakunle Wasiu SUBAIR; Atinuke OLADOYE

    2008-01-01

    The improvement in the inhibitive strength of sodium sulphite on corrosion of mild steel in hydrogen cyanide by adding sodium benzoate in regulated volume was investigated using the fundamental weight loss measurement.500 ppm concentration inhibitive mixtures of sodium benzoate and sodium sulphite in three different volume ratios (5/15, 10/10, 15/5) were formulated and studied for corrosion rate in 200ml hydrogen cyanide fluid. Result obtained indicates that the corrosion rate of mild steel i...

  16. Inhibition of Corrosion of Zinc in (HNO 3 + HCl) acid mixture by ...

    African Journals Online (AJOL)

    Corrosion of Zinc metal in (HNO3 + HCl) binary acid mixture and inhibition efficiency of aniline has been studied by weight loss method and polarization technique. Corrosion rate increases with the concentration of acid mixture and the temperature. Inhibition efficiency (I.E.) of aniline increases with the concentration of ...

  17. Corrosion Inhibition of Carbon Steel in HCl Solution by Some Plant Extracts

    Directory of Open Access Journals (Sweden)

    Ambrish Singh

    2012-01-01

    Full Text Available The strict environmental legislations and increasing ecological awareness among scientists have led to the development of “green” alternatives to mitigate corrosion. In the present work, literature on green corrosion inhibitors has been reviewed, and the salient features of our work on green corrosion inhibitors have been highlighted. Among the studied leaves, extract Andrographis paniculata showed better inhibition performance (98% than the other leaves extract. Strychnos nuxvomica showed better inhibition (98% than the other seed extracts. Moringa oleifera is reflected as a good corrosion inhibitor of mild steel in 1 M HCl with 98% inhibition efficiency among the studied fruits extract. Bacopa monnieri showed its maximum inhibition performance to be 95% at 600 ppm among the investigated stem extracts. All the reported plant extracts were found to inhibit the corrosion of mild steel in acid media.

  18. Inhibition of mild steel corrosion using Jatropha Curcas leaf extract

    Directory of Open Access Journals (Sweden)

    OLORUNFEMI MICHAEL AJAYI

    2014-05-01

    Full Text Available Jatropha Curcas leaf was investigated as a green inhibitor on the degradation of mild steel in 4 M HCl and 4 M H2SO4 aqueous solutions using gasometric technique. Mild steel coupons of dimension 2 × 1.5 cm were immersed in test solutions of uninhibited acid and also those with extract concentrations of 4 ml, 6 ml, 8 ml and 10 ml at 30 oC, for up to 30 minutes. The results showed that as the concentration of the extract increases, there was reduction in the corrosion rate. As the extract concentration increased from 4 ml to 10 ml at 30 minutes exposure, the volume of hydrogen gas evolved decreased from 19.1 cm3 to 11.2 cm3 in H2SO4 medium, while it reduced to 5 cm3 from 9 cm3 in HCl medium. Also, the metal surface-phytoconstituent interaction mechanism showed that 6 minutes is the best exposure time for the adsorption of the extract in both acidic media. The Jatropha Curcas leaf extract was adsorbed on the mild steel surface to inhibit corrosion, while the experimental data obtained at 30 minutes exposure in both acidic media were well fitted with the Langmuir adsorption isotherm. Hence, Jatropha Curcas leaf extract is a good and safe inhibitor in both acidic solutions.

  19. Laser shock peening without coating induced residual stress distribution, wettability characteristics and enhanced pitting corrosion resistance of austenitic stainless steel

    Science.gov (United States)

    Prabhakaran, S.; Kulkarni, Aniket; Vasanth, G.; Kalainathan, S.; Shukla, Pratik; Vasudevan, Vijay K.

    2018-01-01

    Low energy laser shock peening without coating (LSPwC) was conducted on AISI 304 austenitic stainless steel specimens with varying pulse densities or overlapping. Highest magnitude of compressive residual stress (CRS) was achieved for an optimized pulse density of 2500 pulses/cm2 (75% overlapping). The 2-D and 3-D topographical analysis were indicative of the fact that controlled roughening of the surface was achieved after the LSPwC process. After the LSPwC process, the hydrophilic unpeened surface was converted into the hydrophobic surface, thus decreasing the wettability characteristics of the surface. The X-ray diffraction (XRD) results reveal that there is a beginning of the martensite transformation and the rise in the intensity value of the peaks after LSPwC indicates the presence of compressive residual stresses induced in the specimen. The optical microscope and high-resolution transmission electron microscope results provided evidence of grain refinement and deformation induced refinement features such as multidirectional mechanical twinning, dislocations lines, micro shear cells and stacking faults in the near and sub-surface areas. The average hardness value of the LSPwC specimens was found to be increased by 28% more than the untreated specimen. The potentiodynamic polarization revealed that there was a considerable amount of increase in the pitting corrosion resistance after the LSPwC process, thus, supporting to extend the fatigue life of the specimen. The electrochemical impedance spectroscopic (EIS) analysis depicts that the LSPwC process supports the formation of the strong passivation layer in 3.5% NaCl solution.

  20. In-situ Raman and X-ray photoelectron spectroscopic studies on the pitting corrosion of modified 9Cr-1Mo steel in neutral chloride solution

    Science.gov (United States)

    Ramya, S.; Nanda Gopala Krishna, D.; Mudali, U. Kamachi

    2018-01-01

    In-situ Raman and X-ray photoelectron spectroscopic studies were performed for the identification of native and corroded surface oxide layers of modified 9Cr-1Mo steel. The Raman data obtained for native oxide layer of modified 9Cr-1Mo steel revealed that it was mainly composed of oxides of Fe and Cr. The presence of alloying element Mo was found to be less significant in the native oxide film. The oxides of Cr were dominant at the surface and were found to be decreasing closer to metal/oxide layer interface. The changes in the chemical composition of the native films upon in-situ pitting during potentiostatic polarization experiment were characterized by in-situ Raman analysis. The corrosion products of potentiostatically polarized modified 9Cr-1Mo steel was composed of dominant Fe (III) phases viz., γ- Fe2O3, α and γ - FeOOH along with the oxides of chromium. The results from Raman analysis were corroborated with the XPS experiments on as received and pitted samples of modified 9Cr-1Mo steel specimens. It was observed that the oxides of Cr and Mo contributed for the stability of the surface layer by forming Cr2O3 and MoO3. Also, the study attempted to find out the intermediate corrosion products inside the metastable pits to account for the pseudo passive behavior of modified 9Cr-1Mo steel in 0.1 M NaCl solution.

  1. Friction welding of a nickel free high nitrogen steel: influence of forge force on microstructure, mechanical properties and pitting corrosion resistance

    Directory of Open Access Journals (Sweden)

    Mrityunjoy Hazra

    2014-01-01

    Full Text Available In the present work, nickel free high nitrogen austenitic stainless steel specimens were joined by continuous drive friction welding process by varying the amount of forge (upsetting force and keeping other friction welding parameters such as friction force, burn-off, upset time and speed of rotation as constant at appropriate levels. The joint characterization studies include microstructural examination and evaluation of mechanical (micro-hardness, impact toughness and tensile and pitting corrosion behaviour. The integrity of the joint, as determined by the optical microscopy was very high and no crack and area of incomplete bonding were observed. Welds exhibited poor Charpy impact toughness than the parent material. Toughness for friction weld specimens decreased with increase in forge force. The tensile properties of all the welds were almost the same (irrespective of the value of the applied forge force and inferior to those of the parent material. The joints failed in the weld region for all the weld specimens. Weldments exhibited lower pitting corrosion resistance than the parent material and the corrosion resistance of the weld specimens was found to decrease with increase in forge force.

  2. Synergy between molybdenum and nitrogen on the pitting corrosion and passive film resistance of austenitic stainless steels as a pH-dependent effect

    International Nuclear Information System (INIS)

    Loable, Carole; Viçosa, Isadora N.; Mesquita, Thiago J.; Mantel, Marc; Nogueira, Ricardo P.; Berthomé, Gregory; Chauveau, Eric; Roche, Virginie

    2017-01-01

    This paper brings up some insights upon the pH dependence of the synergistic effect of Mo and N on the localized corrosion resistance of austenitic stainless steels. The objective of this work is to study the synergetic effect of Mo and N additions on corrosion and passive film properties of austenitic grades. A comparison between Mo containing (3 wt% Mo); Mo and N containing (3 wt% Mo and 0.1% N) and free Mo or free Mo and N grades of highly controlled laboratory heats was done considering their localized corrosion resistance and oxide film formation in different aggressive conditions, from neutral to alkaline pH. The passive layer was characterized by EIS and XPS analyses. The combined effect of Mo and N on the pitting potential was confirmed to be synergistic, and not just the addition of their individual effects. Moreover, this effect was found to be pH-dependent, being very positive in acid to neutral conditions whereas it was almost inexistent in high pH. - Highlights: • Laboratory austenitic stainless steels with Mo and/or N were tested. • Mo and N acted synergistically to improve pitting resistance. • Synergistic effect is pH-dependent. • N clearly enhanced the repassivation of austenitic SS in presence of Mo.

  3. Synergy between molybdenum and nitrogen on the pitting corrosion and passive film resistance of austenitic stainless steels as a pH-dependent effect

    Energy Technology Data Exchange (ETDEWEB)

    Loable, Carole, E-mail: carole.loable@lepmi.grenoble-inp.fr [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France); Dep. Eng. Quimica, Instituto Superior Técnico-Universidade de Lisboa, Av. Rovisco Pais, 1049 001 Lisbon (Portugal); Viçosa, Isadora N., E-mail: inogueira@poli.ufrj.br [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France); Mesquita, Thiago J., E-mail: Thiago.mesquita@total.com [CRU Ugitech, Avenue Paul Girod, 73403 Ugine Cedex (France); Mantel, Marc, E-mail: Marc.Mantel@ugitech.com [CRU Ugitech, Avenue Paul Girod, 73403 Ugine Cedex (France); Université Grenoble Alpes, SIMAP, F-38000 Grenoble (France); CNRS, SIMAP, F-38000 Grenoble (France); Nogueira, Ricardo P., E-mail: rnogueira@pi.ac.ae [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France); Department of Chemical Engineering, The Petroleum Institute, P.O. Box 2533, Abu Dhabi (United Arab Emirates); Berthomé, Gregory, E-mail: gregory.berthome@simap.grenoble-inp.fr [Université Grenoble Alpes, SIMAP, F-38000 Grenoble (France); CNRS, SIMAP, F-38000 Grenoble (France); Chauveau, Eric, E-mail: eric.chauveau@ugitech.fr [Department of Chemical Engineering, The Petroleum Institute, P.O. Box 2533, Abu Dhabi (United Arab Emirates); Roche, Virginie, E-mail: virginie.roche@lepmi.grenoble-inp.fr [Univ. Grenoble Alpes, LEPMI, F-38000 Grenoble (France); CNRS, LEPMI, F-38000 Grenoble (France)

    2017-01-15

    This paper brings up some insights upon the pH dependence of the synergistic effect of Mo and N on the localized corrosion resistance of austenitic stainless steels. The objective of this work is to study the synergetic effect of Mo and N additions on corrosion and passive film properties of austenitic grades. A comparison between Mo containing (3 wt% Mo); Mo and N containing (3 wt% Mo and 0.1% N) and free Mo or free Mo and N grades of highly controlled laboratory heats was done considering their localized corrosion resistance and oxide film formation in different aggressive conditions, from neutral to alkaline pH. The passive layer was characterized by EIS and XPS analyses. The combined effect of Mo and N on the pitting potential was confirmed to be synergistic, and not just the addition of their individual effects. Moreover, this effect was found to be pH-dependent, being very positive in acid to neutral conditions whereas it was almost inexistent in high pH. - Highlights: • Laboratory austenitic stainless steels with Mo and/or N were tested. • Mo and N acted synergistically to improve pitting resistance. • Synergistic effect is pH-dependent. • N clearly enhanced the repassivation of austenitic SS in presence of Mo.

  4. The Effect of Shielding N{sub 2} gas on The Pitting Corrosion of Seal-welded Super Austenitic Stainless Steel by Autogenous Welding

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Ki Tae; Kim, Young Sik [Andong National University, Andong (Korea, Republic of); Chang, Hyun Young [KEPCO Engineering and Construction Company, Gimcheon (Korea, Republic of)

    2017-04-15

    Many research efforts on the effect of nitrogen on the corrosion resistance of stainless steels have been reported, but little research has been conducted on the effect of nitrogen for the weldment of stainless steels by the seal-weld method. Therefore, this work focused on the determining the corrosion resistance of tube/tube sheet mock-up specimen for sea water condensers, and elucidating the effect of shielding nitrogen gas on its resistance. The pitting corrosion of autogenously welded specimen propagated preferentially along the dendritic structure. Regardless of the percent of shielding nitrogen gas, the analyzed nitrogen contents were very much lower than that of the bulk specimen. This can be arisen because the nitrogen in shielding gas may partly dissolve into the weldment, but simultaneously during the welding process, nitrogen in the alloy may escape into the atmosphere. However, the pitting resistance equivalent number (PREN) of the interdendrite area was higher than that of the dendrite arm, regardless of the shielding gas percent; and the PREN of the interdendrite area was higher than that of the base metal; the PREN of the dendrite arm was lower than that of the base metal because of the formation of (Cr, Mo) rich phases by welding.

  5. Corrosion Inhibition of Aluminium in Acid Media By Citrullus Colocynthis Extract

    OpenAIRE

    Chauhan, Rajkiran; Garg, Urvija; Tak, R. K.

    2011-01-01

    Inhibition of corrosion of aluminium in acid solution by methanol extract of Citrullus colocynthis plant has been studied using mass loss and thermometric measurements. It has been found that the plant extract act as a good corrosion inhibitor for aluminium in all concentrations of sulphuric and hydrochloric acid solution. The inhibition action depends on the concentration of acid and inhibitor. Results for mass loss and thermometric measurement indicate that inhibition efficiency increase wi...

  6. Inhibition of Aluminium Corrosion in Hydrochloric Acid Using Nizoral and the Effect of Iodide Ion Addition

    OpenAIRE

    I. B. Obot; N. O. Obi-Egbedi

    2010-01-01

    The effect of nizoral (NZR) on the corrosion inhibition of aluminium alloy AA 1060 in 2 M HCl solution was investigated using the mylius thermometric technique. Results of the study revealed that nizoral acts as corrosion inhibitor for aluminium in the acidic medium. In general, at constant acid concentration, the inhibition efficiency increases with increase in the inhibitor concentration. The addition of KI to the inhibitor enhanced the inhibition efficiency to a considerable extent. The ad...

  7. Chemical treatment of zinc surface and its corrosion inhibition studies

    Indian Academy of Sciences (India)

    WINTEC

    Department of PG Studies and Research in Chemistry, School of Chemical Sciences, Kuvempu University, ... cations and is mainly used for the corrosion protection of ... provide a greater resistance to corrosion, but when exposed to humid ...

  8. Study of the pitting and repassiv,tion corrosion potential of zicaloy-4 halides solutions at 250C and several pH

    International Nuclear Information System (INIS)

    Gardiazabal, J.I.; Cordova, R.; Gomez, H.; Layana, G.; Schrebler, R.

    1987-01-01

    The electrochemical behaviour of Zircaloy-4 electrode in chloride, bromide and iodide acid solution was investigated at 25 0 C employing stationary, quasi-stationary and potentiodynamic techniques. The results show that the pitting and repassivation potentials are independent on pH but both are dependent on halice concentration, following linear relation ships in these cases. It is also possible to correlate the pitting potential with the ionic radius of the anions, allowing thus to establish an order in their agressive properties. This order was extrapolated for fluoride ion and further experimental measurements show that the corrosion potential of Zircaloy-4 in acid or neutra solution of this ion (which undergoes active dissolution) is coincident with that predicted from the Ep v/s ionic radius determined for the other halides. (Author) [pt

  9. Synergistic Effect of Potassium Iodide on Corrosion Inhibition of Mild ...

    African Journals Online (AJOL)

    MICHAEL

    fruticans' wurmb extract on corrosion of mild steel in 0.1M and 0.5M HCl have been investigated using weight loss methods. ... efficient ways of combating the corrosion of metals. Among other ..... chloride ion on cold rolled steel corrosion.

  10. The Inhibition of Aluminum Corrosion in Sulfuric Acid by Poly(1-vinyl-3-alkyl-imidazolium Hexafluorophosphate

    Directory of Open Access Journals (Sweden)

    Paulina Arellanes-Lozada

    2014-08-01

    Full Text Available Compounds of poly(ionic liquids (PILs, derived from imidazole with different alkylic chain lengths located in the third position of the imidazolium ring (poly(1-vinyl-3-dodecyl-imidazolium (PImC12, poly(1-vinyl-3-octylimidazolium (PImC8 and poly(1-vinyl-3-butylimidazolium (PImC4 hexafluorophosphate were synthesized. These compounds were tested as corrosion inhibitors on aluminum alloy AA6061 in diluted sulfuric acid (0.1–1 M H2SO4 by weight loss tests, polarization resistance measurements and inductively coupled plasma optical emission spectroscopy. Langmuir’s isotherms suggested film formation on bare alloy while standard free energy indicated inhibition by a physisorption process. However, compound efficiencies as inhibitors ranked low (PImC12 > PImC8 > PImC4 to reach 61% for PImC12 in highly diluted acidic solution. Apparently, the high mobility of sulfates favored their adsorption in comparison to PILs. The surface film displayed general corrosion, and pitting occurred as a consequence of PILs’ partial inhibition along with a continuous dissolution of defective patchy film on formation. A slight improvement in efficiency was displayed by compounds having high molecular weight and a long alkyl chain, as a consequence of steric hindrance and PIL interactions.

  11. The Inhibition of Aluminum Corrosion in Sulfuric Acid by Poly(1-vinyl-3-alkyl-imidazolium Hexafluorophosphate).

    Science.gov (United States)

    Arellanes-Lozada, Paulina; Olivares-Xometl, Octavio; Guzmán-Lucero, Diego; Likhanova, Natalya V; Domínguez-Aguilar, Marco A; Lijanova, Irina V; Arce-Estrada, Elsa

    2014-08-07

    Compounds of poly(ionic liquid)s (PILs), derived from imidazole with different alkylic chain lengths located in the third position of the imidazolium ring (poly(1-vinyl-3-dodecyl-imidazolium) (PImC 12 ), poly(1-vinyl-3-octylimidazolium) (PImC₈) and poly(1-vinyl-3-butylimidazolium) (PImC₄) hexafluorophosphate) were synthesized. These compounds were tested as corrosion inhibitors on aluminum alloy AA6061 in diluted sulfuric acid (0.1-1 M H₂SO₄) by weight loss tests, polarization resistance measurements and inductively coupled plasma optical emission spectroscopy. Langmuir's isotherms suggested film formation on bare alloy while standard free energy indicated inhibition by a physisorption process. However, compound efficiencies as inhibitors ranked low (PImC 12 > PImC₈ > PImC₄) to reach 61% for PImC 12 in highly diluted acidic solution. Apparently, the high mobility of sulfates favored their adsorption in comparison to PILs. The surface film displayed general corrosion, and pitting occurred as a consequence of PILs' partial inhibition along with a continuous dissolution of defective patchy film on formation. A slight improvement in efficiency was displayed by compounds having high molecular weight and a long alkyl chain, as a consequence of steric hindrance and PIL interactions.

  12. Corrosion polarization behaviour and inhibition of S40977 stainless steel in benzosulfonazole/3 M H2SO4 solution

    Directory of Open Access Journals (Sweden)

    Roland Tolulope Loto

    2017-12-01

    Full Text Available Benzosulfonazole was evaluated for its corrosion inhibition effect on S40977 stainless steel in 3 M H2SO4 solution through potentiodynamic polarization, open circuit potential measurement, optical microscopy and IR spectroscopy. Results obtained showed the effective performance of the compound with values of 77.33%–88.32% inhibition efficiency, at 0.25%–1.25% inhibitor concentration from electrochemical analysis. Corrosion potential value decreased from −0.359 V to −0.306 V upon addition of the compound at 0.25% concentration, which decreased progressively to −0.278 at 1.25% concentration. Identified functional groups of alcohols, phenols, amines, amides, carboxylic acids, aliphatic amines, esters and ethers within the compound completely adsorbed onto the steel from analysis of the adsorption spectra while others decreased in intensity due to partial adsorption. Thermodynamic calculations showed the cationic adsorption to be through chemisorption mechanism according to Langmuir, Freundlich and Temkin adsorption isotherms. Micro-analytical images showed a severely corroded morphology with corrosion pits in the absence of benzosulfonazole which contrast the images obtained with the inhibitor addition. The compound was determined to be mixed type inhibition. Keywords: Corrosion, Inhibitor, Benzosulfonazole, Sulphuric acid

  13. Corrosion Inhibition of AISI/SAE Steel in a Marine Environment

    Directory of Open Access Journals (Sweden)

    Fatai Olufemi ARAMIDE

    2009-12-01

    Full Text Available Effect of Sodium nitrite as a corrosion inhibitor of mild steel in sea water wasinvestigated, using the conventional weight loss method. Differentpercentages of sodium nitrite were used from 0% to 10% in sea water.Samples of mild steel were exposed to these corrosive media and the weightloss was calculated at intervals of 120 hours, 168 hours, 208 hours, 256 hours,304 hours and 352 hours. It was observed that corrosion rate increases withtime of exposure to the corrosive medium (inhibited or non-inhibited and thatsodium nitrite can be used to retards the corrosion rate of mild steel if theappropriate concentration is used in sea water. It was concluded that theoptimum percentage of sodium nitrate in sea water that gives the optimumcorrosion inhibition of mild steel is 4%.

  14. Influence of reinforcement proportion and matrix composition on pitting corrosion behaviour of cast aluminium matrix composites (A3xx.x/SiCp)

    International Nuclear Information System (INIS)

    Pardo, A.; Merino, M.C.; Merino, S.; Viejo, F.; Carboneras, M.; Arrabal, R.

    2005-01-01

    The influence of silicon carbide (SiCp) proportion and matrix composition on four aluminium metal matrix composites (A360/SiC/10p, A360/SiC/20p, A380/SiC/10p, A380/SiC/20p) immersed in 1-3.5 wt% NaCl at 22 deg C was investigated by potentiodynamic polarization. The kinetics of the corrosion process was studied on the basis of gravimetric measurements. The nature of corrosion products was analysed by scanning electron microscopy (SEM) and low angle X-ray diffraction (XRD). The corrosion damage in Al/SiCp composites was caused by pitting attack and by nucleation and growth of Al 2 O 3 . 3H 2 O on the material surface. The main attack nucleation sites were the interface region between the matrix and the reinforcement particles. The corrosion process was influenced more by the concentration of alloy elements in the matrix than by the proportion of SiCp reinforcement and saline concentration

  15. Influence of reinforcement proportion and matrix composition on pitting corrosion behaviour of cast aluminium matrix composites (A3xx.x/SiCp)

    Energy Technology Data Exchange (ETDEWEB)

    Pardo, A. [Departamento de Ciencia de Materiales, Facultad de Quimica, Universidad Complutense, 28040 Madrid (Spain)]. E-mail: anpardo@quim.ucm.es; Merino, M.C. [Departamento de Ciencia de Materiales, Facultad de Quimica, Universidad Complutense, 28040 Madrid (Spain); Merino, S. [Departamento de Tecnologia Industrial, Universidad Alfonso X El Sabio, 28691, Villanueva de la Canada, Madrid (Spain); Viejo, F. [Departamento de Ciencia de Materiales, Facultad de Quimica, Universidad Complutense, 28040 Madrid (Spain); Carboneras, M. [Departamento de Ciencia de Materiales, Facultad de Quimica, Universidad Complutense, 28040 Madrid (Spain); Arrabal, R. [Departamento de Ciencia de Materiales, Facultad de Quimica, Universidad Complutense, 28040 Madrid (Spain)

    2005-07-01

    The influence of silicon carbide (SiCp) proportion and matrix composition on four aluminium metal matrix composites (A360/SiC/10p, A360/SiC/20p, A380/SiC/10p, A380/SiC/20p) immersed in 1-3.5 wt% NaCl at 22 deg C was investigated by potentiodynamic polarization. The kinetics of the corrosion process was studied on the basis of gravimetric measurements. The nature of corrosion products was analysed by scanning electron microscopy (SEM) and low angle X-ray diffraction (XRD). The corrosion damage in Al/SiCp composites was caused by pitting attack and by nucleation and growth of Al{sub 2}O{sub 3} . 3H{sub 2}O on the material surface. The main attack nucleation sites were the interface region between the matrix and the reinforcement particles. The corrosion process was influenced more by the concentration of alloy elements in the matrix than by the proportion of SiCp reinforcement and saline concentration.

  16. Corrosion Inhibition and Adsorption Characteristics of Tarivid on Mild Steel in H2SO4

    Directory of Open Access Journals (Sweden)

    N. O. Eddy

    2010-01-01

    Full Text Available The corrosion inhibition and adsorption characteristics of (+/--9-fluoro-2,3-dihydro-3-methyl-10-(4-methyl-1-piperazinyl-7-oxo-7H-pyrido[1,2,3-de]-1,4-benzoxazine-6-carboxylic acid (Tarivid on the corrosion of mild steel has been studied using thermometric and gasometric methods. The study reveals that tarivid inhibits the corrosion of mild steel in H2SO4. The values of inhibition efficiency of tarivid were found to increase as its concentration increased but decreased with increase in temperature. Activation energies of the inhibited corrosion of mild steel ranged from 39.05 to 50.61 kJ/mol. Values of enthalpy change and free energy of adsorption were negative which indicated exothermic and spontaneous adsorption process. Physical adsorption mechanism is proposed from the obtained kinetic and thermodynamic parameters. Langmuir adsorption isotherm model is obeyed from the fit of the experimental data.

  17. Comparison Of Metal Corrosion Inhibition By Gravimetric And Linear Polarization Resistance Methods

    OpenAIRE

    Banerji, Shankha

    1992-01-01

    Studies were conducted to evaluate the effectiveness of various dosages of the selected silicate and phosphate compounds applied for corrosion inhibition of cast iron, copper, lead, and galvanized steel specimens. The compounds selected for study were zinc polyphosphate (Calgon C-39), zinc orthophosphate (Virchem V-931), sodium metasilicate and glassy silicate. The effectiveness of these compounds for corrosion inhibition were studied under differing water quality conditions using gravimetric...

  18. Corrosion Inhibition of Aluminium by Treculia Africana Leaves Extract in Acid Medium

    OpenAIRE

    Ejikeme, P.M.; Umana, S.G.; Onukwuli, O.D.

    2012-01-01

    The inhibitive effect of Treculia Africana leaves extract (TALE) in the corrosion of aluminium in HCl solution was studied using weight loss and thermometric methods at 30-60 °C. The results showed that TALE acted as a corrosion inhibitor of aluminium in HCl. Inhibition efficiency increased with increase in TALE concentration, but decreased with increase in temperature. TALE interaction with the metal surface was found to obey Freundlich and El-Awady adsorption isotherms. The obtained heats o...

  19. Image analysis of corrosion pit initiation on ASTM type A240 stainless steel and ASTM type A 1008 carbon steel

    Science.gov (United States)

    Nine, H. M. Zulker

    The adversity of metallic corrosion is of growing concern to industrial engineers and scientists. Corrosion attacks metal surface and causes structural as well as direct and indirect economic losses. Multiple corrosion monitoring tools are available although those are time-consuming and costly. Due to the availability of image capturing devices in today's world, image based corrosion control technique is a unique innovation. By setting up stainless steel SS 304 and low carbon steel QD 1008 panels in distilled water, half-saturated sodium chloride and saturated sodium chloride solutions and subsequent RGB image analysis in Matlab, in this research, a simple and cost-effective corrosion measurement tool has identified and investigated. Additionally, the open circuit potential and electrochemical impedance spectroscopy results have been compared with RGB analysis to gratify the corrosion. Additionally, to understand the importance of ambiguity in crisis communication, the communication process between Union Carbide and Indian Government regarding the Bhopal incident in 1984 was analyzed.

  20. Inhibition Effect of Deanol on Mild Steel Corrosion in Dilute ...

    African Journals Online (AJOL)

    NICOLAAS

    2014-06-23

    Jun 23, 2014 ... The influence of deanol on the corrosion behaviour of mild steel in dilute sulphuric acid with sodium ... the formation of a complex precipitate of protective film, which ... silicon carbide abrasive papers of 80, 120, 220, 800 and 1000 grit ...... ions in sulphuric acid on the corrosion behaviour of stainless steel,.

  1. Method for inhibiting corrosion of nickel-containing alloys

    Science.gov (United States)

    DeVan, J.H.; Selle, J.E.

    Nickel-containing alloys are protected against corrosion by contacting the alloy with a molten alkali metal having dissolved therein aluminum, silicon or manganese to cause the formation of a corrosion-resistant intermetallic layer. Components can be protected by applying the coating after an apparatus is assembled.

  2. Improving the Corrosion Inhibitive Strength of Sodium Sulphite in Hydrogen Cyanide Solution Using Sodium Benzoate

    Directory of Open Access Journals (Sweden)

    Muhammed Olawale Hakeem AMUDA

    2008-12-01

    Full Text Available The improvement in the inhibitive strength of sodium sulphite on corrosion of mild steel in hydrogen cyanide by adding sodium benzoate in regulated volume was investigated using the fundamental weight loss measurement.500 ppm concentration inhibitive mixtures of sodium benzoate and sodium sulphite in three different volume ratios (5/15, 10/10, 15/5 were formulated and studied for corrosion rate in 200ml hydrogen cyanide fluid. Result obtained indicates that the corrosion rate of mild steel in hydrogen cyanide in the presence of sodium benzoate/sodium sulphite inhibitive mixtures range 0.322mmpy to 1.1269mmpy across the three volumetric ratios considered. The 15ml5ml sodium benzoatesodium sulphite mixture had the best average corrosion rate of 0.5123mmpy.The corrosion rate followed reducing pattern after the first 200 hours of immersion. The average corrosion rate in the sodium benzoate / sodium sulphite mixture is less than the rate in sodium sulphite and the mixture is only effective after long time exposure.It is concluded that adding sodium benzoate to sodium sulphite in the volumetric ratio 155ml improves the inhibitive strength of sodium sulphite on the corrosion of mild steel in hydrogen cyanide environment.

  3. The Corrosion Inhibition Characteristics of Sodium Nitrite Using an On-line Corrosion Rate Measurement System

    International Nuclear Information System (INIS)

    Park, Mal-Yong; Kang, Dae-Jin; Moon, Jeon-Soo

    2015-01-01

    An on-line corrosion rate measurement system was developed using a personal computer, a data acquisition board and program, and a 2-electrode corrosion probe. Reliability of the developed system was confirmed with through comparison test. With this system, the effect of sodium nitrite (NaNO 2 ) as a corrosion inhibitor were studied on iron and aluminum brass that were immersed in sodium chloride (NaCl) solution. Corrosion rate was measured based on the linear polarization resistance method. The corrosion rates of aluminum brass and iron in 1% NaCl solutions were measured to be 0.290 mm per year (mmpy) and 0.2134 mmpy, respectively. With the addition of 200 ppm of NO 2 - , the corrosion rates decreased to 0.0470 mmpy and 0.0254 mmpy. The addition of NO 2 - caused a decrease in corrosion rates of both aluminum brass and iron, yet the NO 2 - acted as a more effective corrosion inhibitor for iron. than aluminum brass

  4. Electrochemical investigation of the properties of Co doped ZnO nanoparticle as a corrosion inhibitive pigment for modifying corrosion resistance of the epoxy coating

    International Nuclear Information System (INIS)

    Rostami, M.; Rasouli, S.; Ramezanzadeh, B.; Askari, A.

    2014-01-01

    Highlights: • Corrosion inhibitive pigment based on ZnOCo was synthesized through combustion method. • Doping ZnO nanoparticle with Co enhanced its inhibition properties considerably. • ZnOCo nanoparticle could enhance corrosion protective performance of epoxy coating. • Co doped ZnO nanoparticles behaved as efficient barrier and inhibitive pigment. - Abstract: Co doped ZnO nanoparticles were synthesized by combustion method. Then, the epoxy nanocomposites were prepared using various amounts of nanoparticles. Salt spray and electrochemical impedance spectroscopy (EIS) were used in order to investigate the corrosion inhibition effects of nanoparticles on the steel substrate. The morphology and composition of the films precipitated on the steel surface were investigated by scanning electron microscope (SEM) and energy dispersive spectroscopy. Results revealed that the corrosion inhibition properties of ZnO nanoparticle were significantly enhanced after doping with Co. Moreover, Co doped ZnO nanoparticles enhanced the corrosion resistance of the epoxy coating effectively

  5. Inhibition of Weld Corrosion in Flowing Brines Containing Carbon Dioxide

    OpenAIRE

    Alawadhi, Khaled

    2009-01-01

    The aim of this research was to study the effectiveness of a typical oilfield corrosion inhibitor, which is considered to be a green inhibitor (non toxic to the environment) in controlling internal corrosion of welded X65 pipeline steel in brines saturated with carbon dioxide at one bar pressure, under dynamic flowing conditions, over a range of temperatures. Several experimental configurations were used ranging from a simple flat plate design to a novel rotating cylinder electrode, to all...

  6. Less-Toxic Coatings for Inhibiting Corrosion of Aluminum

    Science.gov (United States)

    Minevski, Zoran; Clarke, Eric; Eylem, Cahit; Maxey, Jason; Nelson, Carl

    2003-01-01

    Two recently invented families of conversion- coating processes have been found to be effective in reducing or preventing corrosion of aluminum alloys. These processes offer less-toxic alternatives to prior conversion-coating processes that are highly effective but have fallen out of favor because they generate chromate wastes, which are toxic and carcinogenic. Specimens subjected to these processes were found to perform well in standard salt-fog corrosion tests.

  7. Application of electrochemical frequency modulation for monitoring corrosion and corrosion inhibition of iron by some indole derivatives in molar hydrochloric acid

    International Nuclear Information System (INIS)

    Khaled, K.F.

    2008-01-01

    The corrosion inhibition effect of four indole derivatives, namely indole (IND), benzotriazole (BTA), benzothiazole (BSA) and benzoimidazole (BIA), have been used as possible corrosion inhibitors for pure iron in 1 M HCl. In this study, electrochemical frequency modulation, EFM was used as an effective method for corrosion rate determination in corrosion inhibition studies. By using EFM measurements, corrosion current density was determined without prior knowledge of Tafel slopes. Corrosion rates obtained using EFM, were compared to that obtained from other chemical and electrochemical techniques. The results obtained from EFM, EIS, Tafel and weight loss measurements were in good agreement. Tafel polarization measurements show that indole derivatives are cathodic-type inhibitors. Molecular simulation studies were applied to optimize the adsorption structures of indole derivatives. The inhibitor/iron/solvent interfaces were simulated and the adsorption energies of these inhibitors were calculated. Quantum chemical calculations have been performed and several quantum chemical indices were calculated and correlated with the corresponding inhibition efficiencies

  8. PITTING CORROSION IN EROSIVE CONDITION OF AGED 550°C CU10NI-3AL-1,3FE ALLOY IN 0,01 M NA2 SO4

    Directory of Open Access Journals (Sweden)

    Rodrigo Nascimento Liberto

    2012-09-01

    Full Text Available This study evaluates the effect of aging at 550°C on pitting corrosion of Cu10Ni-3Al-1.3Fe alloy, after potentiodynamic polarization test in 0.01 M Na2 SO4 in erosive condition. Cold rolled sheet specimens were solution treated at 900°C for 1 hour, and aged at 550°C until 1,032 hours. The investigation was carried out by potentiodynamic polarization in electrolyte consisted of 0.01 M Na2 SO4 with 10 wt. (% of Al2 O3 abrasive particles. After the polarization tests, specimens were analyzed by optical microscopy and scanning electron microscopy techniques to examine the morphology of the corroded regions. Result show that all samples present a passivity break potential (Eq that characterizes the initiation of pitting corrosion. However, it is not observed any significant change in the value of passivity break potential as a function of aging time. The mechanism of pitting corrosion in the studied alloys can be the passivity breakdown by the action of sulfate ion, followed by growth of pit by galvanic action or dissolution of the copper in cupric and cuprous ions and membrane formation of cuprous oxide over the pit

  9. Inhibition study of additives towards the corrosion of ferrous metal in palm biodiesel

    International Nuclear Information System (INIS)

    Fazal, M.A.; Sazzad, B.S.; Haseeb, A.S.M.A.; Masjuki, H.H.

    2016-01-01

    Highlights: • TBA doped biodiesel exhibits fairly good corrosion inhibition efficiency. • TBA forms nitrogen-containing layer on metal surface and protects the corrosion. • Materials exposed to TBA doped biodiesel show less surface roughness. - Abstract: Some efforts have already been given by other researchers to characterize the corrosion behavior of different metals in biodiesel. However, there is very limited information on its remedial measure. Therefore, this study investigates the effects of tert-butylamine (TBA), benzotriazole (BTA), butylate-dhydroxytoluene (BHT), and pyrogallol (PY) on the corrosion of cast iron (CI) and low carbon steel (LCS) through an immersion test in palm biodiesel (B100) at 300 K. Result shows that TBA-doped biodiesel exhibits fairly good corrosion-inhibiting properties for materials exposed to B100. Inhibition efficiency of TBA is found to be 86.54% and 86.71% for CI and LCS, respectively which is far better than other tested additives in this study. The high inhibition efficiency could be attributed to the dominant physical adsorption of N-containing compound which creates a protective layer over the metal surface and prevents corrosion.

  10. Inhibition of Aluminium Corrosion in Hydrochloric Acid Using Nizoral and the Effect of Iodide Ion Addition

    Directory of Open Access Journals (Sweden)

    I. B. Obot

    2010-01-01

    Full Text Available The effect of nizoral (NZR on the corrosion inhibition of aluminium alloy AA 1060 in 2 M HCl solution was investigated using the mylius thermometric technique. Results of the study revealed that nizoral acts as corrosion inhibitor for aluminium in the acidic medium. In general, at constant acid concentration, the inhibition efficiency increases with increase in the inhibitor concentration. The addition of KI to the inhibitor enhanced the inhibition efficiency to a considerable extent. The adsorption of nizoral onto the aluminium surface was found to obey the Fruendlich adsorption isotherm. The value of the free energy for the adsorption process shows that the process is spontaneous.

  11. Inhibiting Effect of Nicotinic Acid Hydrazide on Corrosion of Aluminum and Mild Steel in Acidic Medium

    Energy Technology Data Exchange (ETDEWEB)

    Bhat, J. Ishwara [Mangalore Univ., Karnataka (India); Alva, Vijaya D. P. [Shree Devi Institute of Technology, Karnataka (India)

    2014-02-15

    The corrosion behavior of aluminum and mild steel in hydrochloric acid medium was studied using a nicotinic acid hydrazide as inhibitor by potentiodynamic polarization, electrochemical impedance spectroscopy technique and gravimetric methods. The effects of inhibitor concentration and temperature were investigated. The experimental results suggested, nicotinic acid hydrazide is a good corrosion inhibitor for both aluminum and mild steel in hydrochloric acid medium and the inhibition efficiency increased with increase in the inhibitor concentration. The polarization studies revealed that nicotinic acid hydrazide exhibits mixed type of inhibition. The inhibition was assumed to occur via adsorption of the inhibitor molecules on the aluminum and mild steel surface and inhibits corrosion by blocking the reaction sites on the surface of aluminum.

  12. Corrosion Inhibition of Aluminium in Acid Media By Citrullus Colocynthis Extract

    Directory of Open Access Journals (Sweden)

    Rajkiran Chauhan

    2011-01-01

    Full Text Available Inhibition of corrosion of aluminium in acid solution by methanol extract of Citrullus colocynthis plant has been studied using mass loss and thermometric measurements. It has been found that the plant extract act as a good corrosion inhibitor for aluminium in all concentrations of sulphuric and hydrochloric acid solution. The inhibition action depends on the concentration of acid and inhibitor. Results for mass loss and thermometric measurement indicate that inhibition efficiency increase with increasing inhibitor concentration. The inhibition action of the plant extract is discussed in view of Langmuir adsorption isotherm. It has been observed that the adsorption of the extract on aluminium surface is a spontaneous process. The plant extract provides a good protection to aluminium against corrosion.

  13. Inhibiting Effect of Nicotinic Acid Hydrazide on Corrosion of Aluminum and Mild Steel in Acidic Medium

    International Nuclear Information System (INIS)

    Bhat, J. Ishwara; Alva, Vijaya D. P.

    2014-01-01

    The corrosion behavior of aluminum and mild steel in hydrochloric acid medium was studied using a nicotinic acid hydrazide as inhibitor by potentiodynamic polarization, electrochemical impedance spectroscopy technique and gravimetric methods. The effects of inhibitor concentration and temperature were investigated. The experimental results suggested, nicotinic acid hydrazide is a good corrosion inhibitor for both aluminum and mild steel in hydrochloric acid medium and the inhibition efficiency increased with increase in the inhibitor concentration. The polarization studies revealed that nicotinic acid hydrazide exhibits mixed type of inhibition. The inhibition was assumed to occur via adsorption of the inhibitor molecules on the aluminum and mild steel surface and inhibits corrosion by blocking the reaction sites on the surface of aluminum

  14. Inorganic Corrosion-Inhibitive Pigments for High-Temperature Alkali-activated Well Casing Foam Cement

    Energy Technology Data Exchange (ETDEWEB)

    Sugama, T. [Brookhaven National Lab. (BNL), Upton, NY (United States); Pyatina, T. [Brookhaven National Lab. (BNL), Upton, NY (United States)

    2014-11-14

    This study evaluates inorganic pigments for improving carbon steel (CS) brine-corrosion protection by the sodium metasilicate-activated calcium aluminate cement/Fly Ash blend at 300°C. Calcium borosilicate (CBS) and zinc phosphate, significantly improved CS corrosion-protection by decreasing cement’s permeability for corrosive ions and inhibiting anodic corrosion. An amorphous Na2O-Al2O3-SiO2-H2O phase tightly attached to CS surface formed at 300oC in CBS-modified cement pore solution. The corrosion rate of the CS covered with this phase was nearly 4-fold lower than in the case of nonmodified cement pore solution where the major phase formed on the surface of CS was crystalline analcime.

  15. Inorganic Corrosion-Inhibitive Pigments for High-Temperature Alkali-activated Well Casing Foam Cement

    Energy Technology Data Exchange (ETDEWEB)

    Sugama, T. [Brookhaven National Lab. (BNL), Upton, NY (United States); Pyatina, T. [Brookhaven National Lab. (BNL), Upton, NY (United States)

    2014-11-01

    This study evaluates inorganic pigments for improving carbon steel (CS) brine-corrosion protection by the sodium metasilicate-activated calcium aluminate cement/Fly Ash blend at 300°C. Calcium borosilicate (CBS) and zinc phosphate, significantly improved CS corrosion-protection by decreasing cement’s permeability for corrosive ions and inhibiting anodic corrosion. An amorphous Na2O-Al2O3-SiO2-H2O phase tightly attached to CS surface formed at 300oC in CBS-modified cement pore solution. The corrosion rate of the CS covered with this phase was nearly 4-fold lower than in the case of nonmodified cement pore solution where the major phase formed on the surface of CS was crystalline analcime.

  16. Corrosion Inhibition of the Galvanic Couple Copper-Carbon Steel in Reverse Osmosis Water

    Directory of Open Access Journals (Sweden)

    Irene Carrillo

    2011-01-01

    Full Text Available The purpose of this paper is to evaluate the electrochemical behaviour of corrosion inhibition of the copper-carbon steel galvanic couple (Cu-CS, exposed to reverse osmosis water (RO used for rinsing of heat exchangers for heavy duty machinery, during manufacture. Molybdate and nitrite salts were utilized to evaluate the inhibition behaviour under galvanic couple conditions. Cu-CS couple was used as working electrodes to measure open circuit potential (OCP, potentiodynamic polarization (PP, and electrochemical impedance spectroscopy (EIS. The surface conditions were characterized by scanning electron microscopy (SEM and electron dispersive X-ray spectroscopy (EDS. The most effective concentration ratio between molybdate and nitrite corrosion inhibitors was determined. The morphological study indicated molybdate deposition on the anodic sites of the galvanic couple. The design of molybdate-based corrosion inhibitor developed in the present work should be applied to control galvanic corrosion of the Cu-CS couple during cleaning in the manufacture of heat exchangers.

  17. Controlled Release from Core-Shell Nanoporous Silica Particles for Corrosion Inhibition of Aluminum Alloys

    Directory of Open Access Journals (Sweden)

    Xingmao Jiang

    2011-01-01

    Full Text Available Cerium (Ce corrosion inhibitors were encapsulated into hexagonally ordered nanoporous silica particles via single-step aerosol-assisted self-assembly. The core/shell structured particles are effective for corrosion inhibition of aluminum alloy AA2024-T3. Numerical simulation proved that the core-shell nanostructure delays the release process. The effective diffusion coefficient elucidated from release data for monodisperse particles in water was 1.0×10−14 m2s for Ce3+ compared to 2.5×10−13 m2s for NaCl. The pore size, pore surface chemistry, and the inhibitor solubility are crucial factors for the application. Microporous hydrophobic particles encapsulating a less soluble corrosion inhibitor are desirable for long-term corrosion inhibition.

  18. Controlled Release from Core-Shell Nano porous Silica Particles for Corrosion Inhibition of Aluminum Alloys

    International Nuclear Information System (INIS)

    Jiang, X.; Rathod, Sh.; Shah, P.; Brinker, C.J.; Jiang, X.; Jiang, Y.; Liu, N.; Xu, H.; Brinker, C.J.

    2011-01-01

    Cerium (Ce) corrosion inhibitors were encapsulated into hexagonally ordered nanoporous silica particles via single-step aerosol-assisted self-assembly. The core/shell structured particles are effective for corrosion inhibition of aluminum alloy AA2024-T3. Numerical simulation proved that the core-shell nanostructure delays the release process. The effective diffusion coefficient elucidated from release data for monodisperse particles in water was 1.0x10-14 m 2 s for Ce 3+ compared to 2.5x10-13 m 2 s for NaCl. The pore size, pore surface chemistry, and the inhibitor solubility are crucial factors for the application. Microporous hydrophobic particles encapsulating a less soluble corrosion inhibitor are desirable for long-term corrosion inhibition.

  19. Investigation on synergism of composite additives for zinc corrosion inhibition in alkaline solution

    Energy Technology Data Exchange (ETDEWEB)

    Zhou Hebing [School of Materials Science and Engineering, South China University of Technology, Guangzhou 510641 (China); Key Laboratory of Electrochemical Technology on Energy Storage and Power Generation of Guangdong Higher Education Institutes, South China Normal University, Guangzhou 510006 (China); Engineering Research Center of Materials and Technology for Electrochemical Energy Storage (Ministry of Education), South China Normal University, Guangzhou 510006 (China); Huang Qiming; Liang Man; Lv Dongsheng; Xu Mengqing; Li Hong [Key Laboratory of Electrochemical Technology on Energy Storage and Power Generation of Guangdong Higher Education Institutes, South China Normal University, Guangzhou 510006 (China); Engineering Research Center of Materials and Technology for Electrochemical Energy Storage (Ministry of Education), South China Normal University, Guangzhou 510006 (China); Li Weishan, E-mail: liwsh@scnu.edu.cn [School of Materials Science and Engineering, South China University of Technology, Guangzhou 510641 (China); Key Laboratory of Electrochemical Technology on Energy Storage and Power Generation of Guangdong Higher Education Institutes, South China Normal University, Guangzhou 510006 (China); Engineering Research Center of Materials and Technology for Electrochemical Energy Storage (Ministry of Education), South China Normal University, Guangzhou 510006 (China)

    2011-07-15

    Highlights: {yields} An kind of environmentally benign organic composite additives is used firstly. {yields} The corrosion of zinc is inhibited used the organic compound as additive. {yields} The rate performance of the battery used the organic compound as additive is improved. {yields} The synergism of composite additives for zinc corrosion inhibition is investigated. - Abstract: The synergism of imidazole (IMZ) and poly(ethylene glycol) 600 (PEG) for zinc corrosion inhibition in 3 mol L{sup -1} KOH solution was investigated using a combination of electrochemical and gravimetric methods, and the surface morphology of the zinc was observed by scanning electron microscopy. It is found that there is a synergistic effect between IMZ and PEG for the zinc corrosion inhibition. The difference in molecular structure, ring for IMZ and chain for PEG, and in binding atoms with zinc, nitrogen in IMZ and oxygen in PEG, contributes to this synergistic effect. IMZ inhibits zinc corrosion by mainly depressing the anodic reaction, whereas PEG by depressing the cathodic reaction. The storage performance of the zinc-manganese dioxide batteries using IMZ and/or PEG as inhibitors was determined by discharge test, with a comparison of the battery using mercury as the inhibitor. The battery containing 0.05% IMZ + 0.05% PEG exhibits better performance than the mercury-containing battery, especially when discharged at high rate.

  20. Effects of Tungsten on the Precipitation Kinetics of Secondary Phases and the Associated Susceptibility to Pitting Corrosion in Duplex Stainless Steels

    International Nuclear Information System (INIS)

    Park, Chan Jin; Kwon, Hyuk Sang

    2006-01-01

    Effects of tungsten (W) on the precipitation kinetics of secondary phases and the associated resistance to pitting corrosion of 25% Cr duplex stainless steels were investigated through microstructural and electrochemical noise analyses. With the partial substitution of W for Mo in duplex stainless steel, the potential and current noises of the alloy were significantly decreased in chloride solution due to retardation of the σ phase precipitation. The preferential precipitation of the χ phase in the W-containing alloy during the early period of aging contributed to retarding the precipitation of the σ phase by depleting W and Mo along grain boundaries. In addition, the retardation of the nucleation and growth of the σ phase in the W-containing alloy appears to be attributed to the inherently low diffusivity of W compared with that of Mo

  1. Corrosion Inhibition of Mild Steel in Hydrochloric Acid by Sodium Lauryl Sulfate (SLS

    Directory of Open Access Journals (Sweden)

    Atul Kumar

    2008-01-01

    Full Text Available Effect of Sodium Lauryl Sulfate (SLS, a surfactant on corrosion of mild steel in 1 M hydrochloric acid was studied using three techniques namely: weight loss, electrochemical polarization and metallurgical research microscopy. Results obtained reveal that SLS is good inhibitor and shows very good corrosion inhibition efficiency (IE. The IE was found to vary with concentration of inhibitor and temperature. The electrochemical polarization result revealed that SLS is anodic in nature.

  2. Corrosion Inhibition of Mild Steel in Hydrochloric Acid by Sodium Lauryl Sulfate (SLS)

    OpenAIRE

    Atul Kumar

    2008-01-01

    Effect of Sodium Lauryl Sulfate (SLS), a surfactant on corrosion of mild steel in 1 M hydrochloric acid was studied using three techniques namely: weight loss, electrochemical polarization and metallurgical research microscopy. Results obtained reveal that SLS is good inhibitor and shows very good corrosion inhibition efficiency (IE). The IE was found to vary with concentration of inhibitor and temperature. The electrochemical polarization result revealed that SLS is anodic in nature.

  3. ELECTROCHEMICAL STUDIES FOR CORROSION INHIBITION OF MILD STEEL BY CHRYSOPHYLLUM ALBIDUM EXTRACT

    OpenAIRE

    Akoma Chigozie S.; Osarolube Eziaku; Abumere O. E.

    2018-01-01

    The corrosion behavior of mild steel in carbonated drinks produced by Nigerian Breweries (Fanta, Sprite and Coke) was studied in the presence and absence of an eco-friendly inhibitor, Chrysophyllum albidum using Potentiodynamic polarization technique at 25 °C. Results showed that Chrysophyllum albidum reduced the current density (icorr), which in turn means that the corrosion rate was reduced significantly. The inhibition efficiency was found to be 93%, 78.6% and 87.5% for Fanta, Sprite and C...

  4. Corrosion Inhibition of Cold-rolled Low Carbon Steel with Pulse Fiber Laser Ablation in Water

    Science.gov (United States)

    Chan, Sze Ney; Wong, Wai Yin; Walvekar, Rashmi; Kadhum, Abdul Amir H.; Khalid, Mohammad; Lim, Kean Long

    2018-04-01

    This study aims at the use of a fiber laser for modifying the surface properties of cold-rolled low carbon steel via a pulse laser ablation technique in water. The effect on the corrosion behavior of the fiber laser-treated metal surface was investigated in NaCl and HCl environments. Electrochemical tests showed significant improvement in the corrosion resistance of the laser-treated sample in NaCl, with an increase in open-circuit potential (OCP) from - 0.65 to - 0.60 V and an inhibition efficiency of 89.22% as obtained from the impedance study. Such improvement was less significant in an acidic environment. Lower corrosion rates of 20.9 mpy and 5.819 × 103 mpy were obtained for the laser-treated samples in neutral and acidic electrolytes, respectively, than the corrosion rates obtained for the as-received samples (33.2 mpy and 11.98 × 103 mpy). Morphological analysis indicated a passive film built by spherical grains of regular size on the metal surface after laser treatment. The corrosion inhibition effects in NaCl were evident by the nonexistence of the common corrosion products of lepidocrocite and crystalline structures that were seen on as-received samples; only polyhedral crystals with micrograins grown on them were seen covering the laser-treated surface. Therefore, the laser treatment using a fiber laser source improved the corrosion resistance of cold-rolled low carbon steel.

  5. Effect of nickel and MnS inclusions in the metal on the pitting corrosion of low-carbon stainless steels

    International Nuclear Information System (INIS)

    Frejman, L.I.; Nguen, The Dong; Volkov, D.E.; Konnov, Yu.P.

    1986-01-01

    The resistance to pitting corrosion of steels on the 03Kh17-03Kh18 base containing up to 20 % Ni at different levels of S and Mn impurities contamination is investigated. It is shown that up to 50 % of nickel introduced into ordinary steels with 5-6 % Ni is spent to compensate the resistance decrease caused by MnS inclusions. Full compensation is not attained even in the 10-20 %. Ni range in which nickel practically does not affect the resistance of neither ordinary, nor pure (without MnS) steels. Titanium introduction into ordinary steel on the Kh22N6 base permits to surpass the level of 03Kh17N3 pure steel resistance and attain the level of 03Kh17N6 pure steel almost by all characteristics (including passivated characteristics in sulfuric acid) besides pitting repassivity. In this property pure steels with Ni >or approx. 3 % surpass even the molybdenum containing 03Kh21NbM2T ordinary steel though they by far concede by passivation in sulfuric acid

  6. Investigation on Aging σ-Phase Precipitation Kinetics and Pitting Corrosion of 22 Pct Cr Economical Duplex Stainless Steel with Mn Addition

    Science.gov (United States)

    Yang, Yinhui; Qian, Hao

    2018-05-01

    The influence of Mn addition on σ-phase precipitation kinetics and pitting corrosion of Fe-22Cr-1.9Ni-2.3Mo-0.2N-xMn low nickel type duplex stainless steel was investigated by medium- and high-temperature aging treatments of 600 °C and 800 °C. The microstructure analysis showed that the fine rod-shaped and coarsening dendritelike σ-phase precipitates formed at 600 °C and 800 °C, respectively, and the precipitate growth with the higher temperature was accelerated due to the partition of Mn, but Mn is not a strong σ-phase forming element like Cr, Mo during aging treatment at these two temperatures. At an early aging time of 800 °C, more precipitated nuclei with more Mn addition promote refinement of σ precipitates in later aging time. The kinetic behavior at 600 °C and 800 °C is related to diffusion-controlled growth of σ phase, and the σ-phase nucleation and growth are enhanced with more Mn addition and higher aging temperature due to a faster Mn diffusion rate. The difference in precipitation morphology for two aging temperatures was attributed to the different nucleation modes caused by kinetics parameter n variation. Increasing the aging temperature from 600 °C to 800 °C increased the susceptibility to pitting with higher Mn addition due to faster σ-phase precipitation kinetics.

  7. Corrosion Inhibition in the Secondary Cooling System of ETRR-2, Egypt

    International Nuclear Information System (INIS)

    Aly, A.H.; Gad, M.M.A.; Abdel-Karim, R.; Abdel-Salam, O.F.

    2003-01-01

    The second Egyptian research reactor (ETRR-2) is a light water type of 22 MW thermal power. Proper cooling water treatment is necessary to set the water chemical characteristics within a specified window to avoid or minimize corrosion problems, scale formation, fouling, and microbiological contamination. Selection of a proper and economic corrosion inhibitor is of great importance. This selection depends, among other factors, on the availability as well as cost. The corrosion behaviour of water of ETRR-2 site and its inhibition by different inhibitors was studied in a special test rig designed for this purpose. Sodium salts of polyphosphate, phosphate, molybdate, and tungstate were used to treat and qualify the cooling water. Results showed that the corrosion resistance of the test material depends on both type and concentration of the applied inhibitor. Using 30-ppm tungstate, molybdate, and phosphate (as anodic inhibitors) reduced the corrosion rate, and inhibitor efficiencies of about 97% 86%, and 68% were achieved respectively. Accordingly, sodium tungstate could be ranked as the best anodic inhibitor used followed by molybdate. Sodium phosphate could be ranked as the least efficient one. Adding the same concentration of sodium polyphosphate (as a cathodic inhibitor) yields almost the same inhibition efficiency as tungstate type. However, at higher concentration(40 ppm), an inhibition efficiency of 100% was obtained, Which corresponds to almost zero-corrosion rate

  8. Evolution of the corrosion process of AA 2024-T3 in an alkaline NaCl solution with sodium dodecylbenzenesulfonate and lanthanum chloride inhibitors

    International Nuclear Information System (INIS)

    Zhou, Biner; Wang, Yishan; Zuo, Yu

    2015-01-01

    Highlights: • Inhibition effect of LaCl 3 and SDBS for AA 2024 in NaCl solution (pH 10) was studied. • At the beginning the active polarization behavior of the alloy changed to passivation. • The passive behavior gradually disappeared with time and pitting happened at S-phases. • The compounded inhibitors showed good inhibition but cannot totally inhibit pitting. • The adsorption of SDBS played the key role for inhibition to the corrosion process. - Abstract: The evolution of the corrosion process of AA 2024-T3 in 0.58 g L −1 NaCl solution (pH 10) with sodium dodecylbenzenesulfonate (SDBS) and lanthanum chloride inhibitors was studied with electrochemical and surface analysis methods. With the addition of the compounded LaCl 3 and SDBS inhibitors, in the early stage the polarization behavior of AA 2024-T3 changed from active corrosion to passivation, and both the general corrosion and pitting corrosion were inhibited. However, with the immersion time extended, the passive behavior gradually disappeared and pitting happened at the Cu-rich phases. After 24 h immersion, the compounded inhibitors still showed good inhibition for general corrosion, but the polarization curve again presented the characteristic similar to active polarization. The compounded inhibitors also inhibited the pitting corrosion to some extent. The acting mechanism of the inhibitors SDBS and La 3 Cl on the corrosion process of AA 2024-T3 in the test solution was discussed.

  9. Mechanistic studies of carbon steel corrosion inhibition by cashew ...

    African Journals Online (AJOL)

    The phenoxide, R-Ar-O- ions from the CNSL inhibitor were found to be responsible for the reduction of the corrosion rate of the carbon steel. Also, it was observed that the surface charge of the carbon steel electrodes was positive with respect to the solutions containing CNSL inhibitor. It is likely that the mechanism of the ...

  10. Inhibition Effect of Deanol on Mild Steel Corrosion in Dilute ...

    African Journals Online (AJOL)

    The influence of deanol on the corrosion behaviour of mild steel in dilute sulphuric acid with sodium chloride addition was studied by means of mass-loss, potentiodynamic polarization, electrode potential monitoring, scanning electron microscopy and statistical analysis. Results show that deanol performed excellently with ...

  11. Stochastic theory of fatigue corrosion

    Science.gov (United States)

    Hu, Haiyun

    1999-10-01

    A stochastic theory of corrosion has been constructed. The stochastic equations are described giving the transportation corrosion rate and fluctuation corrosion coefficient. In addition the pit diameter distribution function, the average pit diameter and the most probable pit diameter including other related empirical formula have been derived. In order to clarify the effect of stress range on the initiation and growth behaviour of pitting corrosion, round smooth specimen were tested under cyclic loading in 3.5% NaCl solution.

  12. A comparative study of leaves extracts for corrosion inhibition effect on aluminium alloy in alkaline medium

    Directory of Open Access Journals (Sweden)

    Namrata Chaubey

    2017-12-01

    Full Text Available This paper deals with the comparative inhibition study of some plants leaves extract namely Cannabis sativa (CS, Rauwolfia serpentina (RS, Cymbopogon citratus (CC, Annona squamosa (AS and Adhatoda vasica (AV on the corrosion of aluminium alloy (AA in 1 M NaOH. The corrosion tests were performance by using gravimetric, electrochemical impedance spectroscopy (EIS, potentiodynamic polarization and linear polarization resistance (LPR techniques. RS showed maximum inhibition efficiency (η%, 97% at 0.2 g L−1. Potentiodynamic polarization curves justified that all the inhibitors are mixed-type. Surface morphology of AA is carried by scanning electron microscopy (SEM and atomic force microscopy (AFM.

  13. Enhancing pitting corrosion resistance of AlxCrFe1.5MnNi0.5 high-entropy alloys by anodic treatment in sulfuric acid

    International Nuclear Information System (INIS)

    Lee, C.P.; Chen, Y.Y.; Hsu, C.Y.; Yeh, J.W.; Shih, H.C.

    2008-01-01

    High-entropy alloys are a newly developed family of multi-component alloys that comprise various major alloying elements. Each element in the alloy system is present in between 5 and 35 at.%. The crystal structures and physical properties of high-entropy alloys differ completely from those of conventional alloys. The electrochemical impedance spectra (EIS) of the Al x CrFe 1.5 MnNi 0.5 (x = 0, 0.3, 0.5) alloys, obtained in 0.1 M HCl solution, clearly revealed that the corrosion resistance values were determined to increase from 21 to 34 Ωcm 2 as the aluminum content increased from 0 to 0.5 mol, and were markedly lower than that of 304 stainless steel (243 Ωcm 2 ). At passive potential, the corresponding current declined with the anodizing time accounting, causing passivity by the growth of the multi-component anodized film in H 2 SO 4 solution. X-ray photoelectron spectroscopy (XPS) analyses revealed that the surface of anodized Al 0.3 CrFe 1.5 MnNi 0.5 alloy formed aluminum and chromium oxide film which was the main passivating compound on the alloy. This anodic treatment increased the corrosion resistance in the EIS measurements of the CrFe 1.5 MnNi 0.5 and Al 0.3 CrFe 1.5 MnNi 0.5 alloys by two orders of magnitude. Accordingly, the anodic treatment of the Al x CrFe 1.5 MnNi 0.5 alloys optimized their surface structures and minimized their susceptibility to pitting corrosion

  14. Effect of Rice Straw Extract and Alkali Lignin on the Corrosion Inhibition of Carbon Steel

    International Nuclear Information System (INIS)

    Rabiahtul Zulkafli; Norinsan Kamil Othman; Irman Abdul Rahman; Azman Jalar

    2014-01-01

    A paddy residue based corrosion inhibitor was prepared by treating finely powdered rice straw with aqueous ethanol under acid catalyst (0.01 M H 2 SO 4 ). Commercial alkali lignin was obtained from Sigma-Aldrich. Prior to the corrosion test, the extraction yield and alkali lignin was characterized via FTIR to determine the functional group. The effect of paddy residue extract and commercial alkali lignin on the corrosion inhibition of carbon steel in 1 M HCl was investigated through the weight loss method, potentiodynamic polarization technique and scanning electron microscopy (SEM). The corrosion inhibition efficiency of the extract and alkali lignin at different immersion times (3 h, 24 h and 42 h) was evaluated. The results show that the paddy waste extract exhibited lesser weight loss of carbon steel in the acidic medium in comparison to the commercial alkali lignin, suggesting that the paddy residue extract is more effective than the commercial alkali lignin in terms of its corrosion inhibition properties. The results obtained proves that the extract from paddy residue could serve as an effective inhibitor for carbon steel in acidic mediums. (author)

  15. Adsorption and inhibitive properties of Tryptophan on low alloy steel corrosion in acidic media

    Directory of Open Access Journals (Sweden)

    Hesham T.M. Abdel-Fatah

    2017-02-01

    Corrosion inhibition was studied using electrochemical methods (electrochemical impedance spectroscopy; EIS and the new technique electrochemical frequency modulation; EFM and weight loss measurements. The influence of inhibitor concentration, solution temperature, and immersion time on the corrosion resistance of low alloy steel (LAS has been investigated. Trp proved to be a very good inhibitor for low alloy steel acid corrosion. EFM measurements showed that Trp is a mixed type inhibitor. Trp behaved better in 0.6 M HCl than in 0.6 M HSO3NH2. Moreover, it was found that the inhibition efficiency increased with increasing inhibitor concentration, while a decrease was detected with the rise of temperature and immersion time. The associated activation energy (Ea has been determined. The values of Ea indicate that the type of adsorption of Trp on the steel surface in both acids belongs to physical adsorption. The adsorption process was tested using Temkin adsorption isotherm.

  16. Corrosion inhibition efficiency of linear alkyl benzene derivatives for carbon steel pipelines in 1M HCl

    Directory of Open Access Journals (Sweden)

    A.M. Al-Sabagh

    2011-06-01

    Full Text Available Linear alkyl benzene sulfonic acid (L and three of its ester derivatives (L1, L2, L3 were prepared, followed by quaternization of these esters (L1Q, L2Q, L3Q. The corrosion inhibition effect on carbon steel in 1 M HCl was studied using weight loss and potentiodynamic polarization measurements. The adsorption of the inhibitors on carbon steel surface obeyed the Langmuir’s adsorption isotherm. The associated activation energy of corrosion and other thermodynamic parameters such as enthalpy (ΔH∗, entropy (ΔS∗ of activation, adsorption–desorption equilibrium constant (Kads, standard free energy of adsorption (ΔGoads, heat (ΔHoads, and entropy of adsorption (ΔSoads were calculated to elaborate the corrosion inhibition mechanism.

  17. Corrosion inhibition of magnesium heated in wet air, by surface fluoridation; Inhibition de la corrosion du magnesium chauffe dans l'air humide, par fluoruration superficielle

    Energy Technology Data Exchange (ETDEWEB)

    Caillat, R; Darras, R; Leclercq, D [Commissariat a l' Energie Atomique, Saclay (France).Centre d' Etudes Nucleaires

    1960-07-01

    The maximum temperature (350 deg. C) of magnesium corrosion resistance in wet air may be raised to 490-500 deg. C by the formation of a superficial fluoride film. This can be obtained by two different ways: either by addition of hydrofluoric acid to the corroding medium in a very small proportion such as 0,003 mg/litre; at atmospheric pressure, or by dipping the magnesium in a dilute aqueous solution of nitric and hydrofluoric acids at room temperature before exposing it to the corroding atmosphere. In both cases the corrosion inhibition is effective over a very long time, even several thousand hours. (author) [French] La temperature limite (350 deg. C) de resistance du magnesium a la corrosion par l'air humide, peut etre elevee jusque 490-500 deg. C par la formation d'une couche fluoruree superficielle. Deux procedes permettent d'obtenir ce resultat: l'atmosphere corrodante peut etre additionnee d'acide fluorhydrique a une concentration aussi faible que 0,003 mg/litre, a la pression atmospherique, ou bien le magnesium peut etre traite a froid, avant exposition a la corrosion, dans une solution aqueuse diluee d'acides nitrique et fluorhydrique. Dans les deux cas, la protection est assuree, meme pour de tres longues durees d'exposition: plusieurs milliers d'heures. (auteur)

  18. Corrosion inhibition of magnesium heated in wet air, by surface fluoridation; Inhibition de la corrosion du magnesium chauffe dans l'air humide, par fluoruration superficielle

    Energy Technology Data Exchange (ETDEWEB)

    Caillat, R.; Darras, R.; Leclercq, D. [Commissariat a l' Energie Atomique, Saclay (France).Centre d' Etudes Nucleaires

    1960-07-01

    The maximum temperature (350 deg. C) of magnesium corrosion resistance in wet air may be raised to 490-500 deg. C by the formation of a superficial fluoride film. This can be obtained by two different ways: either by addition of hydrofluoric acid to the corroding medium in a very small proportion such as 0,003 mg/litre; at atmospheric pressure, or by dipping the magnesium in a dilute aqueous solution of nitric and hydrofluoric acids at room temperature before exposing it to the corroding atmosphere. In both cases the corrosion inhibition is effective over a very long time, even several thousand hours. (author) [French] La temperature limite (350 deg. C) de resistance du magnesium a la corrosion par l'air humide, peut etre elevee jusque 490-500 deg. C par la formation d'une couche fluoruree superficielle. Deux procedes permettent d'obtenir ce resultat: l'atmosphere corrodante peut etre additionnee d'acide fluorhydrique a une concentration aussi faible que 0,003 mg/litre, a la pression atmospherique, ou bien le magnesium peut etre traite a froid, avant exposition a la corrosion, dans une solution aqueuse diluee d'acides nitrique et fluorhydrique. Dans les deux cas, la protection est assuree, meme pour de tres longues durees d'exposition: plusieurs milliers d'heures. (auteur)

  19. Corrosion Inhibition of Aluminium by Capparis deciduas in Acidic Media

    Directory of Open Access Journals (Sweden)

    P. Arora

    2007-01-01

    Full Text Available The inhibition efficiency of ethanolic extract of different parts of Capparis deciduas (Ker in acidic medium has been evaluated by mass loss and thermometric methods. Values of inhibition efficiency obtained from the two methods are in good agreement and are dependent upon the concentration of inhibitor and acid.

  20. Corrosion Inhibition of Aluminium by Capparis deciduas in Acidic Media

    OpenAIRE

    P. Arora; S. Kumar; M. K. Sharma; S. P. Mathur

    2007-01-01

    The inhibition efficiency of ethanolic extract of different parts of Capparis deciduas (Ker) in acidic medium has been evaluated by mass loss and thermometric methods. Values of inhibition efficiency obtained from the two methods are in good agreement and are dependent upon the concentration of inhibitor and acid.

  1. Inhibition of salt precipitation, corrosion and corrosion fatigue of steel in neutral environments

    International Nuclear Information System (INIS)

    Mikhajlovskij, V.Ya.; Slobodyan, Z.V.; Soprunyuk, N.G.; Ivanov, A.M.

    1983-01-01

    Processes of salt precipitation, corrosion under dynamic and static conditions, are studied as well as corrosion fatigue of 20 and 40Kh steels in neutral aqueous media without and with the addition of compounds of several classes. The solution of calcium bicarbonate with the initial concentration [Ca(HCO 3 ) 2 ]=1.3 g/l and 3% NaCl solution in distilled water are used for investigation. The effectiveness index of salt precipitation inhibitor is determined by the change in the rate of calcium bicarbonate transformation into carbonate. The combination of results obtained permits to make the conclusion that tripolyphosphate and pyrophosphoric acid are rather perspective inhibitors of complex effect with low protective concentrations

  2. The initial stage of pitting corrosion on coated steels investigated by photon rupture in chloride containing solutions

    International Nuclear Information System (INIS)

    Sakairi, M.; Uchida, Y.; Itabashi, K.; Takahashi, H.

    2005-01-01

    A photon rupture method, film removal by a focused pulse of pulsed Nd-YAG laser beam irradiation, has been developed to enable oxide film stripping at extremely high rates without contamination from the film removal tools. In the present study, Zn-55mass%Al alloy and Al-9mass%Si alloy-coated steel specimens covered with protective nitrocellulose film were irradiated with a focused pulse of a pulsed Nd-YAG laser beam at a constant potential in 0.5 kmol m -3 H 3 BO 3 -0.05 kmol m -3 Na 2 B 4 O 7 (pH = 7.4) with 0.01 kmol m -3 of chloride ions to investigate the initial stage of localized corrosion. At low potentials, oxide films on both coated alloys were reformed after the nitrocellulose films were removed by this method. The oxide film formation kinetics follows an inverse logarithmic law, in agreement with Cabrera-Mott theory. However, at high potentials, localized corrosion producing corrosion products occurs at the area where nitrocellulose film was removed. Nevertheless, when the applied potential is less noble, the dissolution current of the Zn-55mass%Al-coated steel samples is higher than that of Al-9mass%Si-coated samples

  3. The initial stage of pitting corrosion on coated steels investigated by photon rupture in chloride containing solutions

    Energy Technology Data Exchange (ETDEWEB)

    Sakairi, M. [Research Group of Interface Control Engineering Molecular Chemistry, Graduate School of Engineering, Hokkaido University, Kita 13, Nishi 8, Kita-ku, Sapporo 060-8628 (Japan)]. E-mail: msakairi@elechem1-mc.eng.hokudai.ac.jp; Uchida, Y. [Research Group of Interface Control Engineering Molecular Chemistry, Graduate School of Engineering, Hokkaido University, Kita 13, Nishi 8, Kita-ku, Sapporo 060-8628 (Japan); Itabashi, K. [NTT DoCoMo Hokkaido Inc., Kita 1, Nishi 14, Chuou-ku, Sapporo 060-0001 (Japan); Takahashi, H. [Research Group of Interface Control Engineering Molecular Chemistry, Graduate School of Engineering, Hokkaido University, Kita 13, Nishi 8, Kita-ku, Sapporo 060-8628 (Japan)

    2005-10-01

    A photon rupture method, film removal by a focused pulse of pulsed Nd-YAG laser beam irradiation, has been developed to enable oxide film stripping at extremely high rates without contamination from the film removal tools. In the present study, Zn-55mass%Al alloy and Al-9mass%Si alloy-coated steel specimens covered with protective nitrocellulose film were irradiated with a focused pulse of a pulsed Nd-YAG laser beam at a constant potential in 0.5 kmol m{sup -3} H{sub 3}BO{sub 3}-0.05 kmol m{sup -3} Na{sub 2}B{sub 4}O{sub 7} (pH = 7.4) with 0.01 kmol m{sup -3} of chloride ions to investigate the initial stage of localized corrosion. At low potentials, oxide films on both coated alloys were reformed after the nitrocellulose films were removed by this method. The oxide film formation kinetics follows an inverse logarithmic law, in agreement with Cabrera-Mott theory. However, at high potentials, localized corrosion producing corrosion products occurs at the area where nitrocellulose film was removed. Nevertheless, when the applied potential is less noble, the dissolution current of the Zn-55mass%Al-coated steel samples is higher than that of Al-9mass%Si-coated samples.

  4. Corrosion inhibition performance of imidazolium ionic liquids and their influence on surface ferrous carbonate layer formation

    Science.gov (United States)

    Yang, Dongrui

    Corrosion inhibitors as effective anti-corrosion applications were widely studied and drawn much attention in both academe and industrial area. In this work, a systematic work, including inhibitors selection, anti-corrosion property and characterization, influence on scale formation, testing system design and so on, were reported. The corrosion inhibition performance of four imidazolium ionic liquids in carbon dioxide saturated NaCl solution was investigated by using electrochemical and surface analysis technologies. The four compounds are 1-ethyl-3-methylimidazolium chloride (a), 1-butyl-3-methylimidazolium chloride (b), 1-hexyl-3-methylimidazolium chloride (c), 1-decyl-3-methylimidazolium chloride (d). Under the testing conditions, compound d showed the highest inhibition efficiency and selected as the main object of further study. As a selected representative formula, 1-decyl-3-methylimidazolium chloride was studied in detail about its corrosion inhibition performance on mild steel in carbon dioxide saturated NaCl brine at pH 3.8 and 6.8. Electrochemical and surface analysis techniques were used to characterize the specimen corrosion process during the immersion in the blank and inhibiting solutions. The precorrosion of specimen surface showed significant and different influences on the anti-corrosion property of DMICL at pH 3.8 and 6.8. The corrosion inhibition efficiency (IE) was calculated based on parameters obtained from electrochemical techniques; the achieved IE was higher than 98% at the 25th hour for the steel with a well-polished surface at pH 3.8. The fitting parameters obtained from electrochemical data helped to account for the interfacial changes. As proved in previous research, 1-decyl-3-methylimidazolium chloride could be used as good corrosion inhibitors under certain conditions. However, under other conditions, such chemicals, as well as other species in oil transporting system, could be a factor influencing the evolution of protective surface

  5. Organic-inorganic nanosystems designed for multiple metal corrosion inhibition

    Science.gov (United States)

    Stockley, Robert

    This research focuses on the refinement and discovery of environmentally friendly coatings of metals with increased durability and longer lifetimes as the goal. In the pursuit of an ideal, such as environmentally friendly coatings or "green chemistry," there are many obstacles that must be overcome. This is particularly true in the case of protecting magnesium and its alloys. The relatively low open circuit potential of magnesium makes it highly susceptible to galvanic corrosion when in contact with other metals. It is also easily oxidized when exposed to air or humid conditions and forms a loose hydroxide/oxide layer (Mg(OH)2/MgO). However, for all of its problems, the advantages to using magnesium far outweigh the disadvantages; if and only if, its natural tendency to corrode can be adequately controlled. Magnesium has a high strength to weight ratio, similar to that of glass, making it ideal for a vast array of commercial applications. Magnesium has a high electromagnetic shielding effect (-52.34 dB at 2.45/ GHz for AZ31), making it applicable not only to aircraft instrumentation, but structure as well, due to its low density (d = 1.48 g/cm3). The list of applications for magnesium and its alloys is extensive. Our research has provided insights into the prevention of magnesium corrosion and the applications of "green chemistry" to a metal used across a multitude of industries. Specifically, excellent results were obtained for the electrochemical impedance spectroscopy of LZ91 (magnesium alloy) which demonstrated an impedance of 1.0 x 1010 Ohms to 1.0 x 1011 Ohms. These results suggest our coatings display a pure capacitance behavior in the Bode plot. According to ASTM B117 testing (salt fog testing) the coating on LZ91 panels reached 120 hours, a period considered to be the equivalent of five years of real world conditions, without appreciable corrosion. The possible mechanism for this corrosion protection will also be discussed. These advancements are

  6. Iron corrosion inhibition by phosphonate complexes of rare earth metals

    International Nuclear Information System (INIS)

    Kuznetsov, Yu.I.; Raskol'nikov, A.F.; Starobinskaya, I.V.; Alekseev, V.N.

    1993-01-01

    Capability is shown of trivalent rare earth nitrilotrimethylphosphonates (R= Ce, Pr, Nd, Eu, Lu, Y) to retard steel corrosion in soft water due to the formation of slightly soluble hydroxides on steel surface. The protective film is produced as a result of electrophilic substitution of nascent iron cations for rare earth ions in near the surface layer. The introduction of rare earth cations into the protective film is ascertained by Auger spectroscopy in combination with the argon spraying. A quantitative interrelation between the protective effectiveness and solubility product of rare earth hydroxides is revealed

  7. Inhibition of the corrosion of mild steel in hydrochloric acid by isatin ...

    African Journals Online (AJOL)

    The inhibition of corrosion of mild steel in hydrochloric acid by isatin glycine (ING) and isatin (IN) at 30-60 oC and concentrations of 0.0001 M to 0.0005 M was studied via weight loss method. At the highest inhibitor concentration studied ING exhibited inhibition efficiency of 87% while IN exhibited 84% at 60 oC. A chemical ...

  8. Corrosion inhibition of carbon steel XC70 in H 2 SO 4 solution by ...

    African Journals Online (AJOL)

    In this work, we studied the efficiency of corrosion inhibition of carbon steel XC70 in H2SO4 0.5 M aqueous solution using ferrocenyl derivatives synthesized in our laboratory, this compound is: 3-(ferrocenylmethylamine)benzonitrile. The inhibitory potential of this compound was determined by electrochemical techniques ...

  9. Corrosion inhibition properties of pyrazolylindolenine compounds on copper surface in acidic media

    Directory of Open Access Journals (Sweden)

    Ebadi Mehdi

    2012-12-01

    Full Text Available Abstract Background The corrosion inhibition performance of pyrazolylindolenine compounds, namely 4-(3,3-dimethyl-3H-indol-2-yl-pyrazole-1-carbothioamide (InPzTAm, 4-(3,3-dimethyl-3H-indol-2-yl-1H-pyrazole-1-carbothiohydrazide (InPzTH and 3,3-dimethyl-2-(1-phenyl-1H-pyrazol-4-yl-3H-indole (InPzPh, on copper in 1M HCl solution is investigated by electrochemical impedance spectroscopy (EIS, open circuit potential (OCP and linear scan voltammetry (LSV techniques. Results The results show that the corrosion rate of copper is diminished by the compounds with the inhibition strength in the order of: InPzTAm> InPzTH > InPzPh. The corrosion inhibition efficiencies for the three inhibitors are 94.0, 91.4 and 79.3, for InPzTAm, InPzTH and InPzPh respectively with the same inhibitor concentration (2 mM. Conclusion From the EIS, OCP and LSV results it was concluded that pyrazolylindolenine compounds with S-atom (with an amine group have illustrated better corrosion inhibition performance compared to hydrazine and phenyl group.

  10. Effect of Benzamide on the Corrosion Inhibition of Mild Steel in ...

    African Journals Online (AJOL)

    NICOLAAS

    2SO4 was studied at .... The structure and chemistry of benzamide is expected to give .... corrosion inhibition of mild steel in the sulphuric acid strength ... tion and formation of a compact barrier film on the metal elec- .... metal–acid interface.

  11. Boiler and steam generator corrosion: Nuclear power plants. (Latest citations from the NTIS Bibliographic database). Published Search

    International Nuclear Information System (INIS)

    1993-09-01

    The bibliography contains citations concerning corrosion effects, mechanisms, detection, and inhibition in nuclear powered steam generators. Pitting, stress corrosion cracking, and crevice corrosion studies performed on the water side and hot gas side of the heat exchanger tubes and support structures are presented. Water treatment, corrosion monitoring, chemical cleaning, and descaling methods are considered. Fossil fuel fired boilers are examined in a separate bibliography. (Contains a minimum of 138 citations and includes a subject term index and title list.)

  12. EIS study on corrosion and scale processes and their inhibition in cooling system media

    Energy Technology Data Exchange (ETDEWEB)

    Marin-Cruz, J. [Universidad Autonoma Metropolitana, Departamento de Quimica, Apdo. Postal 55-534, 09340 Mexico, DF (Mexico) and Instituto Mexicano del Petroleo, Coordinacion de Ingenieria Molecular, Competencia de Quimica Aplicada, Eje Central Lazaro Cardenas No. 152, CP 07730, DF (Mexico)]. E-mail: jmarin@imp.mx; Cabrera-Sierra, R. [Universidad Autonoma Metropolitana, Departamento de Quimica, Apdo. Postal 55-534, 09340 Mexico, DF (Mexico); Escuela Superior de Ingenieria Quimica e Industrias Extractivas (ESIQIE-IPN), Departamento de Metalurgia, UPALM Zacatenco AP 75-874, CP 07338, DF (Mexico); Pech-Canul, M.A. [Departamento de Fisica Aplicada, Centro de Investigacion y de Estudios, Avanzados del IPN, AP 73 Cordemex, CP 97310, Merida, Yucatan (Mexico); Gonzalez, I. [Universidad Autonoma Metropolitana, Departamento de Quimica, Apdo. Postal 55-534, 09340 Mexico, DF (Mexico)]. E-mail: igm@xanum.uam.mx

    2006-01-20

    A study of the carbon steel/cooling water interface was carried out using electrochemical impedance spectroscopy (EIS). EIS spectra reveal that a layer of corrosion and scale products forms naturally and evolves with the immersion time modifying the carbon steel/cooling water interface and giving rise to corrosion and scale processes. In addition, the nature of the layer formed on the metal was found to depend on the inhibitor used. It was established that the corrosion inhibitor (hydroxyphosphonoacetic acid (HPA)) chelates with Ca(II) ion generating a layer with resistive properties that provides good protection against corrosion. In contrast, the scale inhibitor (1-hydroxy-ethane-1,1-diphosphonic acid (HEDP)) is incorporated into the calcium carbonate crystals at the surface, modifying the structure and diminishing scale formation in the surface; this additive additionally inhibited corrosion. These observations were supported by scanning electronic microscopy (SEM) and corroborate previous studies performed by other techniques on HPA and HEDP. Finally, a synergistic effect was observed between these inhibitors that provides good protection to steel against corrosion and scaling in cooling media.

  13. EIS study on corrosion and scale processes and their inhibition in cooling system media

    International Nuclear Information System (INIS)

    Marin-Cruz, J.; Cabrera-Sierra, R.; Pech-Canul, M.A.; Gonzalez, I.

    2006-01-01

    A study of the carbon steel/cooling water interface was carried out using electrochemical impedance spectroscopy (EIS). EIS spectra reveal that a layer of corrosion and scale products forms naturally and evolves with the immersion time modifying the carbon steel/cooling water interface and giving rise to corrosion and scale processes. In addition, the nature of the layer formed on the metal was found to depend on the inhibitor used. It was established that the corrosion inhibitor (hydroxyphosphonoacetic acid (HPA)) chelates with Ca(II) ion generating a layer with resistive properties that provides good protection against corrosion. In contrast, the scale inhibitor (1-hydroxy-ethane-1,1-diphosphonic acid (HEDP)) is incorporated into the calcium carbonate crystals at the surface, modifying the structure and diminishing scale formation in the surface; this additive additionally inhibited corrosion. These observations were supported by scanning electronic microscopy (SEM) and corroborate previous studies performed by other techniques on HPA and HEDP. Finally, a synergistic effect was observed between these inhibitors that provides good protection to steel against corrosion and scaling in cooling media

  14. Environmentally safe corrosion inhibition of Mg-Al-Zn alloy in chloride free neutral solutions by amino acids

    Energy Technology Data Exchange (ETDEWEB)

    Helal, N.H. [Chemistry Department, Faculty of Science, Fayoum University, Fayoum (Egypt); Badawy, W.A., E-mail: wbadawy@cu.edu.eg [Chemistry Department, Faculty of Science, Cairo University, 12 613 Giza (Egypt)

    2011-07-30

    Highlights: > Phenyl alanine at a concentration of 2 x 10{sup -3} mol dm{sup -3} gives 93% corrosion inhibition efficiency for the corrosion of the Mg-Al-Zn alloy. > The corrosion inhibition process is based on the adsorption of the amino acid molecules on the active sites of the alloy surface by physical adsorption mechanism. > The adsorption free energy was 15.72 kJ mol{sup -1}. - Abstract: The corrosion inhibition of Mg-Al-Zn alloy was investigated in stagnant naturally aerated chloride free neutral solutions using amino acids as environmentally safe corrosion inhibitors. The corrosion rate was calculated in the absence and presence of the corrosion inhibitor using the polarization technique and electrochemical impedance spectroscopy. The experimental impedance data were fitted to theoretical data according to a proposed electronic circuit model to explain the behavior of the alloy/electrolyte interface under different conditions. The corrosion inhibition process was found to depend on the adsorption of the amino acid molecules on the metal surface. Phenyl alanine has shown remarkably high corrosion inhibition efficiency up to 93% at a concentration of 2 x 10{sup -3} mol dm{sup -3}. The corrosion inhibition efficiency was found to depend on the concentration of the amino acid and its structure. The mechanism of the corrosion inhibition process was discussed and different adsorption isotherms were investigated. The free energy of the adsorption process was calculated for the adsorption of different amino acids on the Mg-Al-Zn alloy and the obtained values reveal a physical adsorption of the inhibitor molecules on the alloy surface.

  15. Contribution to the study of the electrochemical behaviour of titanium and of its industrial shores in sulphuric environment. Characteristics of their resistance to pitting corrosion in neutral and acid halogenous environment

    International Nuclear Information System (INIS)

    Petit, Jacques-Alain

    1975-01-01

    After a presentation of the general metallurgical, physical, and corrosion resistance characteristics of titanium and of its alloys, this research thesis presents the experimental means, discusses the influence of experimental conditions on the assessment of the electrochemical behaviour of titanium and of its alloys. It reports an investigation of the cathodic behaviour of non-alloyed titanium and notably the hydrogen release kinetics in a concentrated acid environment. It discusses the influence of alloy composition on their cathodic behaviour, addresses the anodic behaviour of titanium and of its alloys in sulphuric environment, and the pitting corrosion of titanium and of its alloys in an acid and neutral halogenous environment [fr

  16. Automated Methods Of Corrosion Measurements

    DEFF Research Database (Denmark)

    Bech-Nielsen, Gregers; Andersen, Jens Enevold Thaulov; Reeve, John Ch

    1997-01-01

    The chapter describes the following automated measurements: Corrosion Measurements by Titration, Imaging Corrosion by Scanning Probe Microscopy, Critical Pitting Temperature and Application of the Electrochemical Hydrogen Permeation Cell.......The chapter describes the following automated measurements: Corrosion Measurements by Titration, Imaging Corrosion by Scanning Probe Microscopy, Critical Pitting Temperature and Application of the Electrochemical Hydrogen Permeation Cell....

  17. Studies on the impact, detection, and control of microbiology influenced corrosion related to pitting failures in the Russian oil and gas industry. Final CRADA report.

    Energy Technology Data Exchange (ETDEWEB)

    Ehst, D.

    2006-09-30

    The objectives of the Project are: (1) to design effective anti-corrosion preparations (biocides, inhibitors, penetrants and their combinations) for gas- and oil-exploration industries; (2) to study a possibility of development of environmentally beneficial ('green') biocides and inhibitors of the new generation; (3) to develop chemical and microbiological methods of monitoring of sites at risk of corrosion; and (4) to evaluate potentialities in terms of technology, raw materials and material and technical basis to set up a production of effective anti-corrosion preparations of new generation in Russia. During the four years of the project 228 compounds and formulations were synthesized and studied in respect to their corrosion inhibiting activity. A series of compounds which were according to the Bubble tests more efficient (by a factor of 10-100) than the reference inhibitor SXT-1102, some possessing the similar activity or slightly better activity than new inhibitor ??-1154? (company ONDEO/Nalco). Two synthetic routes for the synthesis of mercaptopyrimidines as perspective corrosion inhibitors were developed. Mercaptopyrimidine derivatives can be obtained in one or two steps from cheap and easily available precursors. The cost for their synthesis is not high and can be further reduced after the optimization of the production processes. A new approach for lignin utilization was proposed. Water-soluble derivative of lignin can by transformed to corrosion protective layer by its electropolymerization on a steel surface. Varying lignosulfonates from different sources, as well as conditions of electrooxidation we proved, that drop in current at high anodic potentials is due to electropolymerization of lignin derivative at steel electrode surface. The electropolymerization potential can be sufficiently decreased by an increase in ionic strength of the growing solution. The lignosulfonate electropolymerization led to the considerable corrosion protection

  18. Inhibition Effect of 1-Butyl-4-Methylpyridinium Tetrafluoroborate on the Corrosion of Copper in Phosphate Solutions

    OpenAIRE

    Scendo, M.; Uznanska, J.

    2011-01-01

    The influence of the concentration of 1-Butyl-4-methylpyridinium tetrafluoroborate (4MBPBF4) as ionic liquid (IL) on the corrosion of copper in 0.5 M P O 4 3 − solutions of pH 2 and 4 was studied. The research involved electrochemical polarization method, and scanning electron microscopy (SEM) technique. The results obtained showed that the inhibition efficiency of corrosion of copper increases with an increase in the concentration of 4MBPBF4 but decreases with increasing temperature. The the...

  19. Corrosion inhibition of magnesium heated in wet air, by surface fluoridation

    International Nuclear Information System (INIS)

    Caillat, R.; Darras, R.; Leclercq, D.

    1960-01-01

    The maximum temperature (350 deg. C) of magnesium corrosion resistance in wet air may be raised to 490-500 deg. C by the formation of a superficial fluoride film. This can be obtained by two different ways: either by addition of hydrofluoric acid to the corroding medium in a very small proportion such as 0,003 mg/litre; at atmospheric pressure, or by dipping the magnesium in a dilute aqueous solution of nitric and hydrofluoric acids at room temperature before exposing it to the corroding atmosphere. In both cases the corrosion inhibition is effective over a very long time, even several thousand hours. (author) [fr

  20. Thermometric Study of Inhibition of Aluminium Corrosion in Hydrochloric Acid Solution

    OpenAIRE

    Al Gaber, A.S. [امينة سلطان الجابر; Seliman, S. A.; Mourad, M.

    1997-01-01

    The use of 6- amino - 4- (4-phenyl)-l,4- dihydro -3- methylpyrano [2,3- c] pyrazole -5- carbonitrile and some related compounds as corrosion inhibitors for aluminium in 2 M HCl solution was studied by the thermometric method. The results indicate that the additives reduce the corrosion rate via weak adsorption through the cationic oxygen of the pyran ring. They act as mixed inhibitors and their adsorption was found to obey Frumkin's isotherm. The inhibition efficiency of the additives is rela...

  1. Development of a functionalized coating for inhibition of marine corrosion and biofouling

    Science.gov (United States)

    Gittens, Jeanette Elizabeth

    The financial loss incurred by corrosion of metals in the marine environment has led to a need to develop effective, economic and environmentally friendly methods of protection. Traditional methods of counteracting the development of surface biofilms and biofouling within aqueous environments have involved implementing chemical biocides, often with a deleterious effect on non-target organisms. Sol gel coating technology offers a convenient route for immobilizing functional additives, such as inhibitors or, in the case of this study, biologically active microorganisms. Paenibacillus polymyxa biofilms inhibit the corrosion of metal substrates and this strain has the advantage of forming endospores can withstand the solvent and acid concentrations required in sol-gel formulation. Encapsulation of viable P. polymyxa endospores within the sol-gel matrix allowed germination on exposure to nutrients, when germinating endospores and vegetative cells were seen after fluorescence microscopy to be distributed throughout the coating. Laboratory electrochemical impedance tests were used to characterize the corrosion behaviour of the endospore-containing (biotic) sol-gel coating in comparison to an abiotic (no endospores) sol-gel only coating and one containing non-viable (killed) endospores. The technology enabled manipulation of the sol-gel formulation and the method of application to produce biotic sol-gel with enhanced corrosion inhibition properties on aluminium alloy. Field trials in a marine environment confirmed the corrosion protecting properties of the biotic coating and that the biotic coatings inhibited macroscopic biofouling for at least 29 weeks relative to the controls without encapsulated live endospores. Production of polymyxin by the encapsulated bacteria, which was proposed as a mechanism by which they inhibit MIC, was less than 1 mug per ml and below the threshold of detection by liquid chromatography mass spectrometry and antimicrobial bioassay. Microcosm

  2. Corrosion Inhibition and Adsorption Behavior of Clove Oil on Iron in Acidic Medium

    Directory of Open Access Journals (Sweden)

    Archana Saxena

    2012-01-01

    Full Text Available Corrosion behavior of iron in hydrochloric acid solution was studied using weight loss as well Scanning electron microscopy study without and with clove oil. The percentage inhibition efficiency increases with increasing clove oil concentration. All the data revel that the oil acts as an excellent inhibitor for the corrosion of iron in HCl solution. Thermodynamic, kinetic parameters and equilibrium constant for adsorption process were calculated from the experimental data. The adsorption of clove oil on experimental metals was found to follow the Langmuir adsorption isotherm at all the concentration studies. Scanning electron microscope (SEM, investigations also indicate that clove oil greatly lowers the dissolution currents.

  3. Evaluation of the inhibitive effect of some plant extracts on the acid corrosion of mild steel

    International Nuclear Information System (INIS)

    Oguzie, Emeka E.

    2008-01-01

    Corrosion inhibition of mild steel in 2 M HCl and 1 M H 2 SO 4 by extracts of selected plants was investigated using a gasometric technique at temperatures of 30 and 60 deg. C. The studied plants materials include leaf extracts Occimum viridis (OV), Telferia occidentalis (TO), Azadirachta indica (AI) and Hibiscus sabdariffa (HS) as well as extracts from the seeds of Garcinia kola (GK). The results indicate that all the extracts inhibited the corrosion process in both acid media by virtue of adsorption and inhibition efficiency improved with concentration. Synergistic effects increased the inhibition efficiency in the presence of halide additives. Inhibition mechanisms were deduced from the temperature dependence of the inhibition efficiency as well as from assessment of kinetic and activation parameters that govern the processes. Comparative analysis of the inhibitor adsorption behaviour in 2 M HCl and 1 M H 2 SO 4 as well as the effects of temperature and halide additives suggest that both protonated and molecular species could be responsible for the inhibiting action of the extracts

  4. Evaluation of the inhibitive effect of some plant extracts on the acid corrosion of mild steel

    Energy Technology Data Exchange (ETDEWEB)

    Oguzie, Emeka E. [Electrochemistry and Materials Science Research Laboratory, Department of Chemistry, Federal University of Technology, PMB 1526, Owerri (Nigeria)], E-mail: oguziemeka@yahoo.com

    2008-11-15

    Corrosion inhibition of mild steel in 2 M HCl and 1 M H{sub 2}SO{sub 4} by extracts of selected plants was investigated using a gasometric technique at temperatures of 30 and 60 deg. C. The studied plants materials include leaf extracts Occimum viridis (OV), Telferia occidentalis (TO), Azadirachta indica (AI) and Hibiscus sabdariffa (HS) as well as extracts from the seeds of Garcinia kola (GK). The results indicate that all the extracts inhibited the corrosion process in both acid media by virtue of adsorption and inhibition efficiency improved with concentration. Synergistic effects increased the inhibition efficiency in the presence of halide additives. Inhibition mechanisms were deduced from the temperature dependence of the inhibition efficiency as well as from assessment of kinetic and activation parameters that govern the processes. Comparative analysis of the inhibitor adsorption behaviour in 2 M HCl and 1 M H{sub 2}SO{sub 4} as well as the effects of temperature and halide additives suggest that both protonated and molecular species could be responsible for the inhibiting action of the extracts.

  5. Inhibition effect of fatty amides with secondary compound on carbon steel corrosion in hydrodynamic condition

    Science.gov (United States)

    Ibrahim, I. M.; Jai, J.; Daud, M.; Hashim, Md A.

    2018-03-01

    The inhibition effect demonstrates an increase in the inhibition performance in presence of a secondary compound in the inhibited solution. This study introduces fatty amides as corrosion inhibitor and oxygen scavenger, namely, sodium sulphite as a secondary compound. The main objective is to determine the synergistic inhibition effect of a system by using fatty amides together with sodium sulphite in hydrodynamic condition. The synergistic inhibition of fatty amides and sodium sulphite on corrosion of carbon steel in 3.5 wt% sodium chloride solution had been studied using linear polarization resistance method and scanning electron microscope (SEM) with energy dispersive X-ray spectroscopy (EDX). Electrochemical measurement was carried out using rotating cylinder electrode at different flow regimes (static, laminar, transition and turbulent). Linear polarization resistance experiments showed the changes in polarization resistance when the rotation speed increased. It found that, by addition of fatty amides together with sodium sulphite in test solution, the inhibition efficiency increased when rotation speed increased. The results collected from LPR experiment correlated with results from SEM-EDX. The results showed inhibition efficiency of system was enhanced when fatty amides and oxygen scavengers were present together.

  6. Inhibition Effect of 1-Butyl-4-Methylpyridinium Tetrafluoroborate on the Corrosion of Copper in Phosphate Solutions

    Directory of Open Access Journals (Sweden)

    M. Scendo

    2011-01-01

    Full Text Available The influence of the concentration of 1-Butyl-4-methylpyridinium tetrafluoroborate (4MBPBF4 as ionic liquid (IL on the corrosion of copper in 0.5 M PO43− solutions of pH 2 and 4 was studied. The research involved electrochemical polarization method, and scanning electron microscopy (SEM technique. The results obtained showed that the inhibition efficiency of corrosion of copper increases with an increase in the concentration of 4MBPBF4 but decreases with increasing temperature. The thermodynamic functions of corrosion analysis and adsorptive behavior of 4MBPBF4 were carried out. During the test, the adsorption of the inhibitor on the copper surface in the phosphate solutions was found to obey the Langmuir adsorption isotherm and had a physical mechanism.

  7. Standard test method for initial screening of corrosion inhibiting admixtures for steel in concrete

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2007-01-01

    1.1 This test method covers a procedure for determining the effects of chemical admixtures on the corrosion of metals in concrete. This test method can be used to evaluate materials intended to inhibit chloride-induced corrosion of steel in concrete. It can also be used to evaluate the corrosivity of admixtures by themselves or in a chloride environment. This test is not applicable for emulsions. 1.2 &solely-SI-units; 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

  8. Electrodeposited Organic Layers Formed from Aryl Diazonium Salts for Inhibition of Copper Corrosion

    Directory of Open Access Journals (Sweden)

    Ana Chira

    2017-02-01

    Full Text Available Copper substrates deposed on a gold screen-printed electrode were covered with different aryl diazonium salts by electrodeposition at 0.25 mA for 30 or 300 s. Seven compounds were investigated: 4-aminophenylacetic acid, 4-aminophenethyl alcohol, 4-fluoroaniline, 4-(heptadecafluorooctylaniline, 4-aminoantipyrine, 4-(4-aminophenylbutyric acid and 3,4,5-trimethoxyaniline. Quantitative monitoring of the electrodeposition process was carried out by electrogravimetry using quartz crystal microbalance (QCM. The electrodeposited mass varies between 26 ng/cm2 for 4-fluoroaniline formed during 30 s to 442 ng/cm2 for 4-phenylbutyric acid formed during 300 s. The corrosion inhibition properties of aryl-modified layers have been studied in buffer citrate with pH = 3 or 3.5% NaCl solutions using electrochemical noise (ECN and Tafel potentiodynamic polarization measurements. A corrosion inhibiting efficiency up to 90% was found. The highest corrosion inhibition was obtained for 4-(4-aminophenylbutyric acid and the lowest for 4-fluoroaniline. A relation between the inhibition efficiency and the chemical nature of the substituents in the protective layer was found.

  9. Electrodeposited Organic Layers Formed from Aryl Diazonium Salts for Inhibition of Copper Corrosion.

    Science.gov (United States)

    Chira, Ana; Bucur, Bogdan; Radu, Gabriel-Lucian

    2017-02-28

    Copper substrates deposed on a gold screen-printed electrode were covered with different aryl diazonium salts by electrodeposition at 0.25 mA for 30 or 300 s. Seven compounds were investigated: 4-aminophenylacetic acid, 4-aminophenethyl alcohol, 4-fluoroaniline, 4-(heptadecafluorooctyl)aniline, 4-aminoantipyrine, 4-(4-aminophenyl)butyric acid and 3,4,5-trimethoxyaniline. Quantitative monitoring of the electrodeposition process was carried out by electrogravimetry using quartz crystal microbalance (QCM). The electrodeposited mass varies between 26 ng/cm² for 4-fluoroaniline formed during 30 s to 442 ng/cm² for 4-phenylbutyric acid formed during 300 s. The corrosion inhibition properties of aryl-modified layers have been studied in buffer citrate with pH = 3 or 3.5% NaCl solutions using electrochemical noise (ECN) and Tafel potentiodynamic polarization measurements. A corrosion inhibiting efficiency up to 90% was found. The highest corrosion inhibition was obtained for 4-(4-aminophenyl)butyric acid and the lowest for 4-fluoroaniline. A relation between the inhibition efficiency and the chemical nature of the substituents in the protective layer was found.

  10. Corrosion inhibition of 7000 series aluminium alloys with cerium diphenyl phosphate

    Energy Technology Data Exchange (ETDEWEB)

    Hill, Julie-Anne [Department of Materials Engineering and Australian Centre of Excellence for Electromaterials Science, Wellington Rd, Monash University, Clayton, Victoria (Australia); Markley, Tracey [Department of Materials Engineering and Australian Centre of Excellence for Electromaterials Science, Wellington Rd, Monash University, Clayton, Victoria (Australia); CSIRO, Division of Materials Science and Technology, Clayton, Victoria (Australia); Forsyth, Maria, E-mail: maria.forsyth@deakin.edu.au [Department of Materials Engineering and Australian Centre of Excellence for Electromaterials Science, Wellington Rd, Monash University, Clayton, Victoria (Australia); Howlett, Patrick C. [Department of Materials Engineering and Australian Centre of Excellence for Electromaterials Science, Wellington Rd, Monash University, Clayton, Victoria (Australia); Hinton, Bruce R.W. [Department of Materials Engineering and Australian Centre of Excellence for Electromaterials Science, Wellington Rd, Monash University, Clayton, Victoria (Australia); Defence Science and Technology Organisation, Melbourne, Victoria (Australia)

    2011-02-03

    Graphical abstract: Scanning electron micrographs of microtomed surface shows pristine surface free of corrosion related 'mud cracking' inset for an inhibited AA7050 specimen when only 150 ppm Ce(dpp)3 is present in 0.1 M NaCl solution. Display Omitted Research highlights: > The thin film of hydrolysis products of Ce(dpp)3 and aluminium oxide is proposed to cause the inhibition. > The film consists of discrete Ce rich particles and a thin film over the matrix of Ce, P and Al oxides. > Discrete deposition of Ce is specifically influenced by Cu rich intermetallics. - Abstract: Cerium diphenyl phosphate (Ce(dpp){sub 3}) has previously been shown to be a strong corrosion inhibitor for aluminium-copper magnesium alloy AA2024-T3 and AA7075 in chloride solutions. Surface characterisation including SEM and ToF-SIMS coupled with electrochemical impedance spectroscopy (EIS) measurements are used to propose a mechanism of corrosion inhibition which appears to involve the formation of a complex oxide film of aluminium and cerium also incorporating the organophosphate component. The formation of a thin complex film consisting of hydrolysis products of the Ce(dpp){sub 3} compound and aluminium oxide is proposed to lead to the observed inhibition. SEM analysis shows that some intermetallics favour the creation of thicker deposits predominantly containing cerium oxide compounds.

  11. Long-term corrosion inhibition mechanism of microarc oxidation coated AZ31 Mg alloys for biomedical applications

    International Nuclear Information System (INIS)

    Gu, Yanhong; Bandopadhyay, Sukumar; Chen, Cheng-fu; Ning, Chengyun; Guo, Yuanjun

    2013-01-01

    Highlights: ► The corrosion behavior is significantly affected by the long-term immersion. ► The degradation is inhibited due to the corrosion product layer. ► The corrosion resistance is enhanced by optimized MAO electrolyte concentrations. ► The corrosion inhibition mechanism is presented by a Flash animation. - Abstract: This paper addresses the long-term corrosion behavior of microarc oxidation coated Mg alloys immersed in simulated body fluid for 28 days. The coatings on AZ31 Mg alloys were produced in the electrolyte of sodium phosphate (Na 3 PO 4 ) at the concentration of 20 g/L, 30 g/L and 40 g/L, respectively. Scanning electron microscope (SEM) and optical micrograph were used to observe the microstructure of the samples before and after corrosion. The composition of the MAO coating and corrosion products were determined by X-Ray Diffraction (XRD). Corrosion product identification showed that hydroxyapatite (HA) was formed on the surface of the corroded samples. The ratio of Ca/P in HA determined by the X-ray Fluorescence (XRF) technique showed that HA is an acceptable biocompatible implant material. The potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) were employed to characterize the corrosion rate and the electrochemical impedance. The corrosion resistance of the coated Mg alloys can be enhanced by optimizing the electrolyte concentrations for fabricating samples, and is enhanced after immersing the coated samples in simulated body fluid for more than 14 days. The enhanced corrosion resistance after long-term immersion is attributed to a corrosion product layer formed on the sample surface. The inhibition mechanism of the corrosion process is discussed and presented with an animation

  12. Inhibition properties of self-assembled corrosion inhibitor talloil diethylenetriamine imidazoline for mild steel corrosion in chloride solution saturated with carbon dioxide

    International Nuclear Information System (INIS)

    Jevremović, Ivana; Singer, Marc; Nešić, Srđan; Mišković-Stanković, Vesna

    2013-01-01

    Highlights: •Corrosion inhibitor talloil diethylenetriamine imidazoline effectively protects mild steel from CO 2 corrosion. •Quartz crystal microbalance measurements were used to the investigate kinetics of corrosion inhibitor adsorption. •Adsorption of talloil diethylenetriamine imidazoline can be described by Langmuir adsorption isotherm. -- Abstract: The inhibition effect of talloil diethylenetriamine imidazoline (TOFA/DETA imidazoline) on corrosion of mild steel in chloride solutions saturated with CO 2 was investigated by weight loss measurements (WL) and atomic force microscopy (AFM). Adsorption mechanism and kinetics of self-assembled (TOFA/DETA imidazoline) monolayers formation on gold were studied using the quartz crystal microbalance measurements (QCM). WL and AFM results demonstrated that TOFA/DETA imidazoline can effectively protect mild steel surface from corrosion. QCM measurements shown that the adsorption of TOFA/DETA imidazoline onto gold follows Langmuir adsorption isotherm and further investigation of the adsorption process will be carried out on a corroding metal surface

  13. Synergistic Effect of Molybdate and Monoethanolamine on Corrosion Inhibition of Ductile Cast Iron in Tap Water

    Energy Technology Data Exchange (ETDEWEB)

    Kim, K. T.; Kim, Y. S. [Andong National University, Andong (Korea, Republic of); Chang, H. Y.; Lim, B. T.; Park, H. B. [KEPCO Engineering and Construction Company, Gimcheon (Korea, Republic of)

    2017-02-15

    A synergistic effect was observed in the combination of nitrite and ethanolamines. Ethanolamine is one of the representative organic corrosion inhibitors and can be categorized as adsorption type. However, nitrosamines can form when amines mix with sodium nitrite. Since nitrosamine is a carcinogen, the co-addition of nitrite and ethanolamine will be not practical, and thus, a non-toxic combination of inhibitors shall be needed. In order to maximize the effect of monoethanolamine, we focused on the addition of molybdate. Molybdate has been used to alternate the addition of chromate, but it showed insufficient oxidizing power relative to corrosion inhibitors. This work evaluated the synergistic effect of the co-addition of molybdate and monoethanolamine, and its corrosion mechanism was elucidated. A high concentration of molybdate or monoethanolamine was needed to inhibit the corrosion of ductile cast iron in tap water, but in the case of the co-addition of molybdate and monoethanolamine, a synergistic effect was observed. This synergistic effect could be attributed to the molybdate that partly oxidizes the metallic surface and the monoethanolamine that is simultaneously adsorbed on the graphite surface. This adsorbed layer then acts as the barrier layer that mitigates galvanic corrosion between the graphite and the matrix.

  14. A study of the inhibition of iron corrosion in HCl solutions by some amino acids

    International Nuclear Information System (INIS)

    Amin, Mohammed A.; Khaled, K.F.; Mohsen, Q.; Arida, H.A.

    2010-01-01

    The performance of three selected amino acids, namely alanine (Ala), cysteine (Cys) and S-methyl cysteine (S-MCys) as safe corrosion inhibitors for iron in aerated stagnant 1.0 M HCl solutions was evaluated by Tafel polarization and impedance measurements. Results indicate that Ala acts mainly as a cathodic inhibitor, while Cys and S-MCys function as mixed-type inhibitors. Cys, which contains a mercapto group in its molecular structure, was the most effective among the inhibitors tested, while Ala was less effective than S-MCys. The low inhibition efficiency recorded for S-MCys compared with that of Cys was attributed to steric effects caused by the substituent methyl on the mercapto group. Electrochemical frequency modulation (EFM) technique and inductively coupled plasma atomic emission spectrometry (ICP-AES), were also applied to make accurate determination of corrosion rates. Validation of the Tafel extrapolation method for measuring corrosion rates was tested. Rates of corrosion rates (in μm y -1 ) obtained from Tafel extrapolation method are in good agreement with those measured using EFM and ICP methods. Some theoretical studies, including molecular dynamics (MD) and density functional theory (DFT), were also employed to establish the correlation between the structure (molecular and electronic) of the three tested inhibitors and the inhibition efficiency. Adsorption via hydrogen bonding was discussed here based on some theoretical studies. Experimental and theoretical results were in good agreement.

  15. Inhibition of Mild Steel Corrosion in Hydrochloric Acid Solution by New Coumarin

    Directory of Open Access Journals (Sweden)

    Abdul Amir H. Kadhum

    2014-06-01

    Full Text Available A new coumarin derivative, N,N′-((2E,2′E-2,2′-(1,4-phenylenebis (methanylylidenebis(hydrazinecarbonothioylbis(2-oxo-2H-chromene-3-carboxamide PMBH, was synthesized and its chemical structure was elucidated and confirmed using spectroscopic techniques (Infrared spectroscopy IR, Proton nuclear  magnetic resonance, 1H-NMR and carbon-13 nuclear magnetic resonance 13C-NMR. The corrosion inhibition effect of PMBH on mild steel in 1.0 M HCl was investigated using corrosion potential (ECORR, potentiodynamic polarization, electrochemical impedance spectroscopy (EIS, and electrochemical frequency modulation (EFM measurements. The obtained results indicated that PMBH has promising inhibitive effects on the corrosion of mild steel in 1.0 M HCl across all of the conditions examined. Scanning electron microscopy (SEM was used to investigate the morphology of the mild steel before and after immersion in 1.0 M HCl solution containing 0.5 mM of PMBH. Surface analysis revealed improvement of corrosion resistance in presence of PMBH.

  16. Inhibition of Mild Steel Corrosion in Hydrochloric Acid Solution by New Coumarin

    Science.gov (United States)

    Kadhum, Abdul Amir H.; Mohamad, Abu Bakar; Hammed, Leiqaa A.; Al-Amiery, Ahmed A.; San, Ng Hooi; Musa, Ahmed Y.

    2014-01-01

    A new coumarin derivative, N,N′-((2E,2′E)-2,2′-(1,4-phenylenebis(methanylylidene))bis(hydrazinecarbonothioyl))bis(2-oxo-2H-chromene-3-carboxamide) PMBH, was synthesized and its chemical structure was elucidated and confirmed using spectroscopic techniques (Infrared spectroscopy IR, Proton nuclear magnetic resonance, 1H-NMR and carbon-13 nuclear magnetic resonance 13C-NMR). The corrosion inhibition effect of PMBH on mild steel in 1.0 M HCl was investigated using corrosion potential (ECORR), potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and electrochemical frequency modulation (EFM) measurements. The obtained results indicated that PMBH has promising inhibitive effects on the corrosion of mild steel in 1.0 M HCl across all of the conditions examined. Scanning electron microscopy (SEM) was used to investigate the morphology of the mild steel before and after immersion in 1.0 M HCl solution containing 0.5 mM of PMBH. Surface analysis revealed improvement of corrosion resistance in presence of PMBH. PMID:28788680

  17. Single pit propagation on austenitic stainless steel

    International Nuclear Information System (INIS)

    Heurtault, Stephane

    2016-01-01

    The electrochemical characterization of metastable events such as pitting corrosion of stainless steel in chloride electrolyte remains complex because many individual processes may occur simultaneously on the alloy surface. To overcome these difficulties, an experimental setup, the flow micro-device, has been developed to achieve the initiation of a single pit and to propagate the single pit in three dimensions. In this work, we take advantage of such a device in order to revisit the pitting process on a 316L stainless steel in a chloride - sulphate bulk. In a first step, the time evolution of the pit geometry (depth, radius) and the chemical evolution of the pit solution investigated using in situ Raman spectroscopy have shown that the pit depth propagation depends on the formation of a metal chloride and sulphate gel in the pit solution, and is controlled by the metallic cations diffusion from the pit bottom to the pit mouth. The pit radius growth is defined by the initial surface de-passivation, by the presence of a pit cover and by the gel development in the solution. all of these phenomena are function of applied potential and chemical composition of the solution. In a last step, it was demonstrated that a critical chloride concentration is needed in order to maintain the pit propagation. This critical concentration slightly increases with the pit depth. From statistical analysis performed on identical experiments, a zone diagram showing the pit stability as a function of the chloride concentration and the pit dimensions was built. (author) [fr

  18. Some observations on pitting corrosion in the zircaloy cladding of fuel pins irradiated in a PWR loop

    International Nuclear Information System (INIS)

    Linde, A. van der; Letsch, A.C.; Hornsveld, E.M.

    1978-11-01

    A three-pins, zircaloy-4 clad, sphere-pac bundle was irradiated in a 280 0 C PWR loop in the HFR at Petten during 131 effective full power days to a bundle average burnup of 0.84 % FIMA. The pins contained a mixture of 61.5 w/o of 1050 μm (U,Pu) 0 2 spheres, 18.5 w/o of 115 μm UO 2 spheres and 20.0 w/o of 2 spheres. The as-fabricated smear density of the vibratory compacted mixture was 81-85 % T.D. The pressure of the pin filling gas was 1 bar helium for pin 306 and 25 bar helium for the pins 308 and 309. The cladding was zircaloy-4 tubing, stress relieved for 4 hours at 540 0 C, with an inner diameter of 9.30 mm and a wall thickness of 0.73 mm. Exposure of the pins in the loop started in the as-pickled, degreased surface condition. The pins operated at an average heat rating of 335 W/cm and at a peak rating of 620 W/cm. The end-of -life peak rating was 425 W/cm. Unfavourable water chemistry conditions of the coolant during the last weeks of the irradition, in particular low NH 3 concentrations resulting in low pH values, caused the deposition of heavy crud layers on the pin surfaces. This crud layer caused a small cladding defect in pin 306 at the axial position of the peak heat rating. The zircaloy-4 wall failed by complete oxidation, which started at and progressed from the outer, coolant side, surface. Immediately after the detection of fission product activity in the loop water, the irradiation of the bundle was terminated. Microscopic investigations on cross sections of the pins 306 and 309 revealed the presence of oxide pits at the outer surface of the zircalloy-4 wall

  19. Corrosion Inhibition Study of Al-Cu-Ni Alloy in Simulated Sea-Water ...

    African Journals Online (AJOL)

    A study on the inhibition of Al-Cu-Ni alloy in simulated sea-water environment was investigated using Sodium Chromate as inhibitor. The inhibitor concentration was varied as control, 0.25, 0.5, 1.0, 1.5 and 2.0 Molar. Al-Cu-Ni alloy was sand cast into cylindrical bars of 20 mm x 300 mm dimension. The corrosion of the ...

  20. Effect of Ethanolamines on Corrosion Inhibition of Ductile Cast Iron in Nitrite Containing Solutions

    International Nuclear Information System (INIS)

    Kim, K. T.; Kim, Y. S.; Chang, H. Y.; Lim, B. T.; Park, H. B.

    2016-01-01

    In this work, synergistic corrosion inhibition effect of nitrite and 3 kinds of ethanolamines on ductile cast iron using chemical and electrochemical methods was evaluated. This work attempts to clarify the synergistic effect of nitrite and ethanolamines. The effects of single addition of TEA, DEA, and MEA, and mixed addition of nitrite plus TEA, DEA or MEA on the corrosion inhibition of ductile cast iron in a tap water were evaluated. A huge amount of single addition of ethanolamine was needed. However, the synergistic effect by mixed addition was observed regardless of the combination of nitrite and triethanolamines, but their effects increased in a series of MEA + nitrite > DEA + nitrite > TEA + nitrite. This tendency of synergistic effect was attributed to the film properties and polar effect; TEA addition couldn't form the film showing high film resistance and semiconductive properties, but DEA or MEA could build the film having relatively high film resistance and n-type semiconductive properties. Moreover, it can be explained that this behaviour was closely related to electron attractive group within the ethanolamines, and thus corrosion inhibition power depends upon the number of the electron attractive group of MEA, DEA, and TEA.

  1. Inhibitive action of some plant extracts on the corrosion of steel in acidic media

    Energy Technology Data Exchange (ETDEWEB)

    Abdel-Gaber, A.M. [Department of Chemistry, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt)]. E-mail: ashrafmoustafa@yahoo.com; Abd-El-Nabey, B.A. [Department of Chemistry, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt); Sidahmed, I.M. [Department of Chemistry, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt); El-Zayady, A.M. [Department of Chemistry, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt); Saadawy, M. [Department of Chemistry, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt)

    2006-09-15

    The effect of extracts of Chamomile (Chamaemelum mixtum L.), Halfabar (Cymbopogon proximus), Black cumin (Nigella sativa L.), and Kidney bean (Phaseolus vulgaris L.) plants on the corrosion of steel in aqueous 1 M sulphuric acid were investigated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization techniques. EIS measurements showed that the dissolution process of steel occurs under activation control. Potentiodynamic polarization curves indicated that the plant extracts behave as mixed-type inhibitors. The corrosion rates of steel and the inhibition efficiencies of the extracts were calculated. The results obtained show that the extract solution of the plant could serve as an effective inhibitor for the corrosion of steel in sulphuric acid media. Inhibition was found to increase with increasing concentration of the plant extract up to a critical concentration. The inhibitive actions of plant extracts are discussed on the basis of adsorption of stable complex at the steel surface. Theoretical fitting of different isotherms, Langmuir, Flory-Huggins, and the kinetic-thermodynamic model, were tested to clarify the nature of adsorption.

  2. Effect of Ethanolamines on Corrosion Inhibition of Ductile Cast Iron in Nitrite Containing Solutions

    Energy Technology Data Exchange (ETDEWEB)

    Kim, K. T.; Kim, Y. S. [Andong National University, Andong (Korea, Republic of); Chang, H. Y.; Lim, B. T.; Park, H. B. [KEPCO Engineering and Construction Company, Gimcheon (Korea, Republic of)

    2016-08-15

    In this work, synergistic corrosion inhibition effect of nitrite and 3 kinds of ethanolamines on ductile cast iron using chemical and electrochemical methods was evaluated. This work attempts to clarify the synergistic effect of nitrite and ethanolamines. The effects of single addition of TEA, DEA, and MEA, and mixed addition of nitrite plus TEA, DEA or MEA on the corrosion inhibition of ductile cast iron in a tap water were evaluated. A huge amount of single addition of ethanolamine was needed. However, the synergistic effect by mixed addition was observed regardless of the combination of nitrite and triethanolamines, but their effects increased in a series of MEA + nitrite > DEA + nitrite > TEA + nitrite. This tendency of synergistic effect was attributed to the film properties and polar effect; TEA addition couldn't form the film showing high film resistance and semiconductive properties, but DEA or MEA could build the film having relatively high film resistance and n-type semiconductive properties. Moreover, it can be explained that this behaviour was closely related to electron attractive group within the ethanolamines, and thus corrosion inhibition power depends upon the number of the electron attractive group of MEA, DEA, and TEA.

  3. A Theoretical Model for Metal Corrosion Degradation

    Directory of Open Access Journals (Sweden)

    David V. Svintradze

    2010-01-01

    Full Text Available Many aluminum and stainless steel alloys contain thin oxide layers on the metal surface which greatly reduce the corrosion rate. Pitting corrosion, a result of localized breakdown of such films, results in accelerated dissolution of the underlying metal through pits. Many researchers have studied pitting corrosion for several decades and the exact governing equation for corrosion pit degradation has not been obtained. In this study, the governing equation for corrosion degradation due to pitting corrosion behavior was derived from solid-state physics and some solutions and simulations are presented and discussed.

  4. INHIBITION EFFECT OF FLAVONOID EXTRACT OF Euphorbia Guyoniana ON THE CORROSION OF MILD STEEL IN H2SO4 MEDIUM

    OpenAIRE

    S. Chihi; N. Gherraf; B. Alabed; S. Hameurlain

    2009-01-01

    The influence of flavonoids extracts of three parts of Euphorbia Guyoniana towards the corrosion of type API 5L X52 steel in 15% H2SO4 has been evaluated by weight loss method and polarization technique. The results showed that extracts are a good inhibitors for API 5L X52 steel in this medium. The corrosion inhibition efficiency increases on increasing plant extracts concentration. The inhibition is attributed to the adsorption of the surface of the metal. Potentiodynamic polarization result...

  5. Inhibition of Corrosion of Carbon Steel in 3.5% NaCl Solution by Myrmecodia Pendans Extract

    Directory of Open Access Journals (Sweden)

    Atria Pradityana

    2016-01-01

    Full Text Available Inhibitor is a substance that is added to the corrosive media to inhibit corrosion rate. Organic inhibitors are preferred to inorganic ones since they are environmentally friendly. One of the organic compounds which is rarely reported as a corrosion inhibitor is Myrmecodia Pendans. The organic compounds can be adsorbed on the metal surface and block the active surface to reduce the rate of corrosion. In this study, the used pipe was carbon steel API 5L Grade B with 3.5% NaCl solution as the corrosion medium. The objective of this research was to analyze the inhibition mechanism Myrmecodia Pendans towards carbon steel in a corrosion medium. Concentration variations of extract Myrmecodia Pendans were 0–500 ppm. Fourier Transform Infrared (FTIR was used for chemical characterization of Myrmecodia Pendans. Polarization and Electrochemical Impedance Spectroscopy (EIS were used to measure the corrosion rate and behaviour. From the electrochemical measurements, it was found that the addition of 400 mg/L inhibitor gave the highest inhibition efficiency. Myrmecodia Pendans acted as a corrosion inhibitor by forming a thin layer on the metal surface.

  6. Corrosion inhibition of nickel in H2SO4 solution by alanine

    International Nuclear Information System (INIS)

    Hamed, E.; Abd El-REhim, S.S.; El-Shahat, M.F.; Shaltot, A.M.

    2012-01-01

    Highlights: ► Corrosion of Ni in 1 M H 2 SO 4 in the absence and the presence of alanine. ► Alanine acts as a moderate mixed type inhibitor. ► Physical adsorption of alanine and formation of protective film are on Ni surface. ► Addition of KI improves the inhibition efficiency (synergistic effect). ► EFM technique is in reasonably good agreement with the different techniques used. - Abstract: The effect of alanine, as a safe inhibitor, was studied by measuring the corrosion of Ni in aerated and stagnant 1 M H 2 SO 4 solution (pH ∼0.2). Measurements were performed under various conditions using potentiodynamic polarization, electrochemical impedance spectroscopy (EIS) and the new electrochemical frequency modulation (EFM) methods. The obtained results showed that the addition of alanine alone gives a moderate inhibition and acts as an anodic-type inhibitor. The inhibition is due to physical adsorption of alanine on the metal surface. The inhibition efficiency enhances with increasing alanine concentration and immersion time but decreases with rise in temperature. The apparent activation energy, E a , is higher in the presence than in the absence of alanine. Addition of I − ions greatly improves the inhibition efficiency of alanine. The synergistic effect is due to enhanced adsorption of alanine cations by chemisorbed I − anions on the metal surface. The results obtained from polarization, EIS and EFM techniques are in good agreement indicating that EFM method can be used successfully for monitoring corrosion rate of Ni in H 2 SO 4 solution with and without alanine.

  7. Note: Inhibiting bottleneck corrosion in electrical calcium tests for ultra-barrier measurements

    Energy Technology Data Exchange (ETDEWEB)

    Nehm, F., E-mail: frederik.nehm@iapp.de; Müller-Meskamp, L.; Klumbies, H.; Leo, K. [Institut für Angewandte Photophysik, Technische Universität Dresden, George-Bähr-Straße 1, 01069 Dresden (Germany)

    2015-12-15

    A major failure mechanism is identified in electrical calcium corrosion tests for quality assessment of high-end application moisture barriers. Accelerated calcium corrosion is found at the calcium/electrode junction, leading to an electrical bottleneck. This causes test failure not related to overall calcium loss. The likely cause is a difference in electrochemical potential between the aluminum electrodes and the calcium sensor, resulting in a corrosion element. As a solution, a thin, full-area copper layer is introduced below the calcium, shifting the corrosion element to the calcium/copper junction and inhibiting bottleneck degradation. Using the copper layer improves the level of sensitivity for the water vapor transmission rate (WVTR) by over one order of magnitude. Thin-film encapsulated samples with 20 nm of atomic layer deposited alumina barriers this way exhibit WVTRs of 6 × 10{sup −5} g(H{sub 2}O)/m{sup 2}/d at 38 °C, 90% relative humidity.

  8. Electrochemical and surface analysis studies on corrosion inhibition of Q235 steel by imidazoline derivative against CO2 corrosion

    International Nuclear Information System (INIS)

    Wang, B.; Du, M.; Zhang, J.; Gao, C.J.

    2011-01-01

    Research highlights: → The TAI inhibitor showed peak-value-phenomenon due to the change of adsorption mode. → The adsorption of TAI inhibitor made the PZC shift toward positive direction. → The adsorption film occurred by forming coordination bonds between heteroatom and Fe. → Bigger adhesive force owing to hydrophobic interaction was detected in TAI solution. → The long range-repulsive force reduced by screening effect of surface charges of TAI. - Abstract: The inhibition performance of a newly synthesized thioureido imidazoline inhibitor (TAI) in CO 2 corrosion was studied by using electrochemical impedance spectroscopy (EIS), atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). Results show that the values of inhibition efficiency show peak-value-phenomenon at concentration of 0.15 mmol dm -3 owing to the change of adsorption mode. The adsorption of protonated TAI molecules on the negatively charged steel surface makes the potential of zero charge (PZC) shift to positive direction, and the long-range electrostatic exclusive forces between AFM tip and sample surface are reduced by screening effect of surface charges.

  9. Synthesis and corrosion inhibition application of NATN on mild steel surface in acidic media complemented with DFT studies

    Science.gov (United States)

    Al-Baghdadi, Shaimaa B.; Hashim, Fanar G.; Salam, Ahmed Q.; Abed, Talib K.; Gaaz, Tayser Sumer; Al-Amiery, Ahmed A.; Kadhum, Abdul Amir H.; Reda, Khalid S.; Ahmed, Wahab K.

    2018-03-01

    The corrosion inhibition effectiveness of thiosemicarbazide compound, namely 3-nitro-5-(2-amino-1,3,4-thiadiazolyl)nitrobenzene (NATN), on mild steel in 1 M hydrochloric acid media has been investigated by weight loss technique. The results exhibit that the corrosion ratio of mild steel was reduced regarding to adding NATN. The corrosion inhibition rate for the NATN was 92.3% at the highest investigated NATN concentration. From the weight loss results it could be concluded that NATN with sulfur, nitrogen and oxygen atoms has clarified best corrosion inhibition achievement comparing to 3,5-dinitrobenzoic acid. Regarding to theoretical studies, DFT was employee to figured geometrical structure and electronic characteristics on NATN. The investigation have been extensive to the HOMO and LUMO analysis to evaluate the energy gap, Ionization potential, Electron Affinity, Global Hardness, Chemical Potential, Electrophilicity, Electronegativity and Polarizability.

  10. Synthesis and corrosion inhibition application of NATN on mild steel surface in acidic media complemented with DFT studies

    Directory of Open Access Journals (Sweden)

    Shaimaa B. Al-Baghdadi

    2018-03-01

    Full Text Available The corrosion inhibition effectiveness of thiosemicarbazide compound, namely 3-nitro-5-(2-amino-1,3,4-thiadiazolylnitrobenzene (NATN, on mild steel in 1 M hydrochloric acid media has been investigated by weight loss technique. The results exhibit that the corrosion ratio of mild steel was reduced regarding to adding NATN. The corrosion inhibition rate for the NATN was 92.3% at the highest investigated NATN concentration. From the weight loss results it could be concluded that NATN with sulfur, nitrogen and oxygen atoms has clarified best corrosion inhibition achievement comparing to 3,5-dinitrobenzoic acid. Regarding to theoretical studies, DFT was employee to figured geometrical structure and electronic characteristics on NATN. The investigation have been extensive to the HOMO and LUMO analysis to evaluate the energy gap, Ionization potential, Electron Affinity, Global Hardness, Chemical Potential, Electrophilicity, Electronegativity and Polarizability. Keywords: NATN, Mild steel, Weight loss, Dinitrobenzoic acid

  11. Kinetics of Corrosion Inhibition of Aluminum in Acidic Media by Water-Soluble Natural Polymeric Pectates as Anionic Polyelectrolyte Inhibitors.

    Science.gov (United States)

    Hassan, Refat M; Zaafarany, Ishaq A

    2013-06-17

    Corrosion inhibition of aluminum (Al) in hydrochloric acid by anionic polyeletrolyte pectates (PEC) as a water-soluble natural polymer polysaccharide has been studied using both gasometric and weight loss techniques. The results drawn from these two techniques are comparable and exhibit negligible differences. The inhibition efficiency was found to increase with increasing inhibitor concentration and decrease with increasing temperature. The inhibition action of PEC on Al metal surface was found to obey the Freundlich isotherm. Factors such as the concentration and geometrical structure of the inhibitor, concentration of the corrosive medium, and temperature affecting the corrosion rates were examined. The kinetic parameters were evaluated and a suitable corrosion mechanism consistent with the kinetic results is discussed in the paper.

  12. Kinetics of Corrosion Inhibition of Aluminum in Acidic Media by Water-Soluble Natural Polymeric Pectates as Anionic Polyelectrolyte Inhibitors

    Directory of Open Access Journals (Sweden)

    Refat M. Hassan

    2013-06-01

    Full Text Available Corrosion inhibition of aluminum (Al in hydrochloric acid by anionic polyeletrolyte pectates (PEC as a water-soluble natural polymer polysaccharide has been studied using both gasometric and weight loss techniques. The results drawn from these two techniques are comparable and exhibit negligible differences. The inhibition efficiency was found to increase with increasing inhibitor concentration and decrease with increasing temperature. The inhibition action of PEC on Al metal surface was found to obey the Freundlich isotherm. Factors such as the concentration and geometrical structure of the inhibitor, concentration of the corrosive medium, and temperature affecting the corrosion rates were examined. The kinetic parameters were evaluated and a suitable corrosion mechanism consistent with the kinetic results is discussed in the paper.

  13. Inhibition of Mild Steel Corrosion in Sulfuric Acid Solution by New Schiff Base

    Directory of Open Access Journals (Sweden)

    Ahmed A. Al-Amiery

    2014-01-01

    Full Text Available The efficiency of Schiff base derived from 4-aminoantipyrine, namely 2-(1,5-dimethyl-4-(2-methylbenzylideneamino-2-phenyl-1H-pyrazol-3(2H-ylidene hydrazinecarbothioamide as a corrosion inhibitor on mild steel in 1.0 M H2SO4 was investigated using electrochemical impedance spectroscopy (EIS, potentiodynamic polarization (PD and electrochemical frequently modulation (EFM in addition to the adsorption isotherm, corrosion kinetic parameters and scanning electron microscopy (SEM. The results showed that this inhibitor behaved as a good corrosion inhibitor, even at low concentration, with a mean efficiency of 93% and, also, a reduction of the inhibition efficiency as the solution temperature increases. A polarization technique and EIS were tested for different concentrations and different temperatures to reveal that this compound is adsorbed on the mild steel, therefore blocking the active sites, and the adsorption follows the Langmuir adsorption isotherm model. The excellent inhibition effectiveness of 2-(1,5-dimethyl-4-(2-methylbenzylideneamino-2-phenyl-1H-pyrazol-3(2H-ylidenehydrazinecarbothioamide was also verified by scanning electron microscope (SEM.

  14. Corrosion Inhibition of Q235A Steel in Acid Medium Using Isatin Derivatives: A Qsar Study

    International Nuclear Information System (INIS)

    Abdo M Al-Fakih; Madzlan Aziz; Abdo M Al-Fakih; Abdallah, H.H.; Hasmerya Maarof; Rosmahaida Jamaludin; Bishir Usman

    2016-01-01

    Quantitative Structure-Activity Relationship (QSAR) study was performed on 10 isatin derivatives which were reportedly used as corrosion inhibitors. Dragon software was used to calculate the molecular descriptors. Partial least square (PLS) method was used to run the regression analysis between the descriptors and the corrosion inhibition efficiencies (IE) of the inhibitors. A predictive QSAR model was developed with a correlation coefficient (r 2 cal ) of 0.9676. The model validity was assessed through internal and external validation. The results show that cross-validation regression coefficient (r 2 cv ) and prediction regression coefficient (r 2 pred ) are 0.8163 and 0.9189, respectively. The model was used to predict the IE for ten isatin derivatives. The results confirm a good stability and predictive ability of the model. Dragon-based descriptors provide a very good description of the corrosion inhibition properties of the inhibitors. The results of the QSAR study were found to be consistent with the experimental data. (author)

  15. Inhibition of Mild Steel Corrosion in Sulfuric Acid Solution by New Schiff Base

    Science.gov (United States)

    Al-Amiery, Ahmed A.; Kadhum, Abdul Amir H.; Kadihum, Abdulhadi; Mohamad, Abu Bakar; How, Chong K.; Junaedi, Sutiana

    2014-01-01

    The efficiency of Schiff base derived from 4-aminoantipyrine, namely 2-(1,5-dimethyl-4-(2-methylbenzylidene)amino)-2-phenyl-1H-pyrazol-3(2H)-ylidene) hydrazinecarbothioamide as a corrosion inhibitor on mild steel in 1.0 M H2SO4 was investigated using electrochemical impedance spectroscopy (EIS), potentiodynamic polarization (PD) and electrochemical frequently modulation (EFM) in addition to the adsorption isotherm, corrosion kinetic parameters and scanning electron microscopy (SEM). The results showed that this inhibitor behaved as a good corrosion inhibitor, even at low concentration, with a mean efficiency of 93% and, also, a reduction of the inhibition efficiency as the solution temperature increases. A polarization technique and EIS were tested for different concentrations and different temperatures to reveal that this compound is adsorbed on the mild steel, therefore blocking the active sites, and the adsorption follows the Langmuir adsorption isotherm model. The excellent inhibition effectiveness of 2-(1,5-dimethyl-4-(2-methylbenzylidene)amino)-2-phenyl-1H-pyrazol-3(2H)-ylidene)hydrazinecarbothioamide was also verified by scanning electron microscope (SEM). PMID:28788488

  16. Corrosion inhibition studies in support of the long term storage of AGR fuel

    Energy Technology Data Exchange (ETDEWEB)

    Standring, P [Sellafield Limited (United Kingdom)

    2012-07-01

    Thorp Receipt and Storage (at Sellafield, UK) is currently being investigated as a bridging solution for the storage of AGR fuel pending the out-come of a national review into spent fuel management. AGR spent fuel is known to be susceptible to corrosion through inter-granular attack. To avoid this, the chosen storage regime for AGR fuel is sodium hydroxide dosed pond water to pH 11.4; now 22 years of operating experience. The conversion of TR and S will require a phased transition. During this transition sodium hydroxide cannot be used due to materials compatibility issues. Alternative corrosion inhibitors have been investigated as an interim measure and sodium nitrate has been selected as a suitable candidate. The efficiency of sodium nitrate to inhibit propagating inter-granular attack of active AGR materials has yet to be established. In the longer term sodium hydroxide will be deployed along with a move to a closed loop pond water management system. Given that carbon dioxide is known to be absorbed by sodium hydroxide dosed water and can affect fuel integrity, in the case of Magnox fuel, there is a need to establish its impact on AGR fuel. The objectives are: To establish the impact of carbonate on AGR fuel corrosion; To establish the efficiency of sodium nitrate to inhibit propagating inter-granular attack of irradiated AGR materials.

  17. Inhibiting effects of some oxadiazole derivatives on the corrosion of mild steel in perchloric acid solution

    International Nuclear Information System (INIS)

    Lebrini, Mounim; Bentiss, Fouad; Vezin, Herve; Lagrenee, Michel

    2005-01-01

    The efficiency of 3,5-bis(n-pyridyl)-1,3,4-oxadiazole (n-POX, n = 1, 2, 3), as corrosion inhibitors for mild steel in 1 M perchloric acid (HClO 4 ) have been determined by weight loss measurements and electrochemical studies. The results show that these inhibitors revealed a good corrosion inhibition even at very low concentrations. Comparison of results among those obtained by the studied oxadiazoles shows that 3-POX was the best inhibitor. Polarisation curves indicate that n-pyridyl substituted-1,3,4-oxadiazoles are mixed type inhibitors in 1 M HClO 4 . The adsorption of these inhibitors follows a Langmuir isotherm model. The electronic properties of n-POX, obtained using the AM1 semi-empirical quantum chemical approach, were correlated with their experimental efficiencies using the linear resistance model (LR)

  18. Studies on the Inhibition of Mild Steel Corrosion by Rauvolfia serpentina in Acid Media

    Science.gov (United States)

    Bothi Raja, P.; Sethuraman, M. G.

    2010-07-01

    Alkaloid extract of Rauvolfia serpentina was tested as corrosion inhibitor for mild steel in 1 M HCl and H2SO4 using weight loss method at three different temperatures, viz., 303, 313, and 323 K, potentiodynamic polarization, electrochemical impedance spectroscopy and scanning electron microscope (SEM) studies. It is evident from the results of this study that R. serpentina effectively inhibits the corrosion in both the acids through adsorption process following Tempkin adsorption isotherm. The protection efficiency increased with increase in inhibitor concentration and temperature. Free energy of adsorption calculated from the temperature studies also revealed the chemisorption. The mixed mode of action exhibited by the inhibitor was confirmed by the polarization studies while SEM analysis substantiated the formation of protective layer over the mild steel surface.

  19. Corrosion Inhibition of Copper-nickel Alloy: Experimental and Theoretical Studies

    Energy Technology Data Exchange (ETDEWEB)

    Khadom, Anees A. [Univ. of Daiyla, Baquba (Iran, Islamic Republic of); Yaro, Aprael S. [Univ. of Baghdad, Aljadreaa (Iran, Islamic Republic of); Musa, Ahmed Y.; Mohamad, Abu Bakar; Kadhum, Abdul Amir H. [UniversitiKebangsaan Malaysia, Bangi (Malaysia)

    2012-08-15

    The corrosion inhibition of copper-nickel alloy by Ethylenediamine (EDA) and Diethylenetriamine (DETA) in 1.5M HCl has been investigated by weight loss technique at different temperatures. Maximum value of inhibitor efficiency was 75% at 35 .deg. C and 0.2 M inhibitor concentration EDA, while the lower value was 4% at 35 .deg. C and 0.01 M inhibitor concentration DETA. Two mathematical models were used to represent the corrosion rate data, second order polynomial model and exponential model respectively. Nonlinear regression analysis showed that the first model was better than the second model with high correlation coefficient. The reactivity of studied inhibitors was analyzed through theoretical calculations based on density functional theory (DFT). The results showed that the reactive sites were located on the nitrogen (N1, N2 and N4) atoms.

  20. Experimental and Theoretical Studies on Corrosion Inhibition of Niobium and Tantalum Surfaces by Carboxylated Graphene Oxide

    Directory of Open Access Journals (Sweden)

    Valbonë Mehmeti

    2018-05-01

    Full Text Available The corrosion of two different metals, niobium and tantalum, in aqueous sulfuric acid solution has been studied in the presence and absence of carboxylated graphene oxide. Potentiodynamic measurements indicate that this nanomaterial inhibits corrosion due to its adsorption on the metal surfaces. The adsorbed layer of carboxylated graphene hinders two electrochemical reactions: the oxidation of the metal and the transport of metal ions from the metal to the solution but also hydrogen evolution reaction by acting as a protective barrier. The adsorption behavior at the molecular level of the carboxylated graphene oxide with respect to Nb, NbO, Ta, and TaO (111 surfaces is also investigated using Molecular Dynamic and Monte Carlo calculations.

  1. CORROSION INHIBITIVE PROPERTIES OF EXTRACT OF JATROPHA CURCAS LEAVES ON MILD STEEL IN HYDROCHLORIC ACID ENVIRONMENT

    Directory of Open Access Journals (Sweden)

    J. Odusote

    2016-09-01

    Full Text Available Jatropha curcas leaves extract was tested as a green corrosion inhibitor for mild steel in aqueous hydrochloric acid solution using gravimetric and thermometric techniques. The results reveal that the inhibition efficiency vary with concentration of the leaf extract and the time of immersion. Maximum inhibition efficiency was found to be 95.92% in 2M HCl with 0.5 g/l concentration of the extract in gravimetric method, while 87.04% was obtained in thermometric method. The inhibiting effect was attributed to the presence of alkaloids, flavonoids, saponins, tannins and phenol in the extract. The adsorption processes of the Jatropha curcas leaves extract onto the mild steel is consistent with the assumptions of Langmuir isotherm model and also found to be spontaneous. From the results, a physical adsorption mechanism is proposed for the adsorption of Jatropha curcas leaves extract onto mild steel surface.

  2. Inhibiting effects of imidazole on copper corrosion in 1 M HNO3 solution

    International Nuclear Information System (INIS)

    Lee, Woo-Jin

    2003-01-01

    The present work deals with the inhibiting effects of imidazole on the pure copper (Cu) corrosion in 1 M HNO 3 solution analysing potentiodynamic polarisation curves, potentiostatic anodic current transient, AC impedance spectra and X-ray photoelectron spectra (XPS). By adding imidazole to HNO 3 solution, the polarisation curves showed decrease in the corrosion current and the cathodic current, suggesting that imidazole acts as an effective cathodic inhibitor to Cu corrosion. From the measured anodic current transients, it is inferred that the protective Cu-imidazole complex film is simultaneously formed with the Cu oxide in the presence of imidazole during the early stage of the anodic polarisation. Analysis of the AC impedance spectra revealed that the values of the charge transfer resistance R ct obtained in imidazole-containing HNO 3 solution were greater than that value in imidazole-free one and at the same time steadily increased with immersion time to the constant value. Contrarily, the capacitance value was abruptly lowered from the double layer capacitance C dl to the complex film capacitance C cf in the progress of immersion time. Furthermore, the Warburg coefficient σ value for the ion diffusion through the complex film was observed to increase with immersion time. This means that the Cu(N-OH) complex film becomes thicker during immersion in the HNO 3 solution with imidazole through the inward growth of the N-rich outer layer to the O-rich inner layer, as well validated by XPS. Based upon the experimental results, it is suggested that the Cu corrosion in 1 M HNO 3 solution is efficiently inhibited with the addition of imidazole by retarding both the charge transfer on cathodic sites of the Cu surface in the early stage of immersion time and the subsequent ion diffusion through the steadily growing complex film

  3. Towards lightweight nanocomposite coatings for corrosion inhibition: Graphene, carbon nanotubes, and nanostructured magnesium as case studies

    Science.gov (United States)

    Dennis, Robert Vincent, III

    The field of nanocomposites is a burgeoning area of research due to the interest in the remarkable properties which can be achieved through their use in a variety of applications, including corrosion resistant coatings. Lightweighting is of increasing importance in the world today due to the ever growing push towards energy efficiency and the green movement and in recent years there has been a vast amount of research performed in the area of developing lightweight nanocomposites for corrosion inhibition. Many new composite materials have been developed through the use of newly developed nanomaterials (including carbonaceous and metallic constituents) and their specialized incorporation in the coating matrix materials. We start with a general review on the development of hybrid nanostructured composites for corrosion protection of base metals from a sustainability perspective in Chapter 1. This review demonstrates the ever swelling requirements for a paradigm shift in the way that we protect metals against corrosion due to the costs and environmental concerns that exist with currently used technology. In Chapter 2, we delve into the much required understanding of graphene oxide and reduced graphene oxide through near-edge X-ray absorption fine structure (NEXAFS) spectroscopy measurements to elucidate information about the electronic structure upon incorporation of nitrogen within the structure. For successful integration of the carbonaceous nanomaterials into a composite coating, a full swath of knowledge is necessary. Within this work we have shown that upon chemical defunctionalization of graphene oxide to reduced graphene oxide by means of hydrazine treatment, nitrogen is incorporated into the structure in the form of a pyrazole ring. In Chapter 3, we demonstrate that by way of in situ polymerization, graphene and multiwalled carbon nanotubes can be incorporated within a polymer (polyetherimide, PEI) matrix. Two systems have been developed including graphene and

  4. Adsorption properties and inhibition of mild steel corrosion in sulphuric acid solution by ketoconazole: Experimental and theoretical investigation

    Energy Technology Data Exchange (ETDEWEB)

    Obot, I.B. [Department of Chemistry, Faculty of Science, University of Uyo, P.M.B. 1017, Uyo, Akwa Ibom State (Nigeria)], E-mail: proffoime@yahoo.com; Obi-Egbedi, N.O. [Department of Chemistry, University of Ibadan, Ibadan (Nigeria)

    2010-01-15

    Ketoconazole (KCZ) has been evaluated as a corrosion inhibitor for mild steel in aerated 0.1 M H{sub 2}SO{sub 4} by gravimetric method. The effect of KCZ on the corrosion rate was determined at various temperatures and concentrations. The inhibition efficiency increases with increase in inhibitor concentration but decrease with rise in temperature. Adsorption followed the Langmuir isotherm with negative values of {delta}G{sub ads}{sup 0}, suggesting a stable and a spontaneous inhibition process. Quantum chemical approach was further used to calculate some electronic properties of the molecule in order to ascertain any correlation between the inhibitive effect and molecular structure of ketoconazole.

  5. Synergistic inhibition between o-phenanthroline and chloride ion for steel corrosion in sulphuric acid

    International Nuclear Information System (INIS)

    Li Xueming; Tang Libin; Li Lin; Mu Guannan; Liu Guangheng

    2006-01-01

    The corrosion inhibition of cold rolled steel in 0.5 M sulphuric acid in the presence of o-phenanthroline and sodium chloride (NaCl) has been investigated by using weight loss and electrochemical techniques. The experimental data suggest that the inhibition efficiency increases with increasing NaCl concentration in the presence of 0.0002 M o-phenanthroline, but decreases with increasing temperature. A synergistic effect is observed when o-phenanthroline and chloride ions are used together to prevent cold rolled steel corrosion in 0.5 M sulphuric acid. The polarization curves showed that the complex of o-phenanthroline and NaCl acts as a mixed type inhibitor. The experimental results suggested that the presence of chloride ions in the solution stabilized the adsorption of o-phenanthroline molecules on the metal surface and improved the inhibition efficiency of o-phenanthroline. The adsorption of the complex accords with the Langmuir adsorption isotherm. Some thermodynamic parameters such as adsorption heat, adsorption entropy and adsorption free energy have been calculated by employing thermodynamic equations. Kinetic parameters such as apparent activation energy and pre-exponential factor have been calculated and discussed

  6. Synthesis, characterization and corrosion inhibition efficiency of N-(4-(Morpholinomethyl Carbamoyl Phenyl Furan-2-Carboxamide

    Directory of Open Access Journals (Sweden)

    N. Zulfareen

    2016-01-01

    Full Text Available A mannich base namely N-(4-(Morpholinomethyl Carbamoyl Phenyl Furan-2-Carboxamide (MFC was synthesized and characterized by FT-IR, 1H NMR, and 13C NMR. The molecular weight of MFC was confirmed by LC-MS. The inhibition effect of MFC on brass in 1 M HCl medium has been investigated by weight loss measurement, potentiodynamic polarization, electrochemical impedance spectroscopy (EIS and cyclic voltametry (CV. Thermodynamic parameters such as free energy, entropy and enthalpy were calculated to describe the mechanism of corrosion inhibitor. The inhibition efficiency of MFC increases with increase in concentration and temperature ranges from 30 °C to 60 °C. Polarization measurements indicated that MFC acts as a mixed type corrosion inhibitor. AC impedance indicates that Rct value increases with increase in the concentration of inhibitor. CV reveals that the oxidation of the copper is controlled by the addition of inhibitor on the brass metal. Surface analysis using scanning electron microscope (SEM shows a significant morphological improvement on the brass surface with the addition of the inhibitor. The adsorption of MFC on brass obeys Langmuir adsorption isotherm. The molecular structure of MFC was distorted to quantum chemical indices using density functional theory (DFT which indicates that the inhibition efficiency of MFC is closely related to quantum parameters.

  7. Electrochemical and spectroscopic evidences of corrosion inhibition of bronze by a triazole derivative

    International Nuclear Information System (INIS)

    Dermaj, A.; Hajjaji, N.; Joiret, S.; Rahmouni, K.; Srhiri, A.; Takenouti, H.; Vivier, V.

    2007-01-01

    The electrochemical behavior of the bronze (Cu-8Sn in wt%) was investigated in 3% NaCl aqueous solution, in presence and in absence of a corrosion inhibitor, the 3-phenyl-1,2,4-triazole-5-thione (PTS). The inhibiting effect of the PTS was evidenced for concentrations higher than 1 mM for the cathodic process whereas its effect was clearly seen with a concentration as low as 0.1 mM for the anodic process. A significant positive shift of the corrosion potential was also observed, and its inhibiting effect increased with both its concentration and the immersion time of the sample. From voltammetry and electrochemical impedance spectroscopy experiments, the inhibiting efficiency of the PTS was found to be in the 94-99% range for 1 mM concentration. Scanning electron microscopy and X-ray energy dispersion analysis of the specimen surface show the presence of sulphur on the surface. Raman micro-spectrometry study confirms the protective effect of the PTS in aqueous solution through three types of interactions with the electrode, namely the adsorption of the inhibitor in a flat configuration, the formation of copper-thiol molecules, and when copper is released, the formation of a polymeric complex

  8. Influence of poly(aminoquinone) on corrosion inhibition of iron in acid media

    Science.gov (United States)

    Jeyaprabha, C.; Sathiyanarayanan, S.; Phani, K. L. N.; Venkatachari, G.

    2005-11-01

    The inhibitor performance of chemically synthesized water soluble poly(aminoquinone) (PAQ) on iron corrosion in 0.5 M sulphuric acid was studied in relation to inhibitor concentration using potentiodynamic polarization and electrochemical impedance spectroscopy measurements. On comparing the inhibition performance of PAQ with that of the monomer o-phenylenediamine (OPD), the OPD gave an efficiency of 80% for 1000 ppm while it was 90% for 100 ppm of PAQ. PAQ was found to be a mixed inhibitor. Besides, PAQ was able to improve the passivation tendency of iron in 0.5 M H 2SO 4 markedly.

  9. Organic compounds as corrosion inhibitors for mild steel in acidic media: correlation between inhibition efficiency and chemical structure

    Energy Technology Data Exchange (ETDEWEB)

    Elias, Elizandra C.S.; Chrisman, Erika C.A.N. [Universidade Federal do Rio de Janeiro (UFRJ), Rio de Janeiro, RJ (Brazil). Escola de Quimica

    2009-12-19

    The use of inhibitors for mild steels corrosion control which are in contact with aggressive environment is an accepted practice in acid treatment of oil-wells. Organic compounds have been studied to evaluate their corrosion inhibition potential. Film-forming corrosion inhibitors, commonly used to protect oil-field equipment, can be absorbed on the steel surface to give structurally ordered layers. Therefore, the electrons should act as an important role for this adsorption. Studies reveal that organic compounds show significant inhibition efficiency. For this purpose, their molecules should contain N, O and S heteroatoms in various functional groups, long hydrocarbon linear or branched radical and anion and cation active components. However, most of these compounds are not only expensive but also toxic to living beings. According to the 'Green Chemistry' rules, corrosion inhibitors based on organic compounds should be cheap, with low toxicity and have high inhibition efficiency. In this study, the effects of some organic compounds with different groups such as amide, ether, phenyldiamine, anime and aminophenol on the corrosion behavior of mild steel in acidic media have been investigated. The experimental data were obtained by gravimetric measurements. The results show that these compounds reveal a promising corrosion inhibition where phenyldiamine is the most efficient. The effect of molecular structure on the corrosion inhibition efficiency was investigated by semi-empirical quantum chemical calculations. The electronic properties such as highest occupied molecular orbital (HOMO), lowest unoccupied molecular orbital (LUMO) energy levels, and LUMO-HOMO energy gap orbital density were calculated. The relations between the inhibition efficiency and some quantum parameters are discussed and correlations are proposed. The highest values for the HOMO densities were found in the vicinity nitrogen atom, indicating that it is the most probable adsorption center

  10. Inhibition effect of phosphorus-based chemicals on corrosion of carbon steel in secondary-treated municipal wastewater.

    Science.gov (United States)

    Shen, Zhanhui; Ren, Hongqiang; Xu, Ke; Geng, Jinju; Ding, Lili

    2013-01-01

    Secondary-treated municipal wastewater (MWW) could supply a viable alternative water resource for cooling water systems. Inorganic salts in the concentrated cooling water pose a great challenge to corrosion control chemicals. In this study, the inhibition effect of 1-hydroxy ethylidene-1,1-diphosphonic acid (HEDP), trimethylene phosphonic acid (ATMP) and 2-phosphonobutane-1,2,4-tricarboxylic acid (PBTCA) on corrosion of carbon steel in secondary-treated MWW was investigated by the means of potentiodynamic polarization and electrochemical impedance spectroscopy. The inhibition effect increased with increasing concentration of inhibitors. The corrosion rates of carbon steel were 1.5, 0.8, 0.2 and 0.5 mm a(-1) for blank, HEDP, ATMP and PBTCA samples at 50 mg L(-1), respectively. The phosphorus-based chemicals could adsorb onto the surface of the carbon steel electrode, form a coat of protective film and then protect the carbon steel from corrosion in the test solution.

  11. Hydrodynamic Effect on the Inhibition for the Flow Accelerated Corrosion of an Elbow

    Energy Technology Data Exchange (ETDEWEB)

    Zeng, L.; Zhang, G. A.; Guo, X. P. [Huazhong University of Science and Technology, Wuhan (China)

    2017-02-15

    The inhibition effect of thioureido imidazoline inhibitor (TAI) for flow accelerated corrosion (FAC) at different locations for an X65 carbon steel elbow was studied by array electrode and computational fluid dynamics (CFD) simulations. The distribution of the inhibition efficiency measured by electrochemical impedance spectroscopy (EIS) is in good accordance with the distribution of the hydrodynamic parameters at the elbow. The inhibition efficiencies at the outer wall are higher than those at the inner wall meaning that the lower inhibition efficiency is associated with a higher flow velocity, shear stress, and turbulent kinetic energy at the inner wall of the elbow, as well as secondary flow at the elbow rather than the mass transport of inhibitor molecules. Compared to the static condition, the inhibition efficiency of TAI for FAC was relatively low. It is also due to a drastic turbulence flow and high wall shear stress during the FAC test, which prevents the adsorption of inhibitor and/or damages the adsorbed inhibitor film.

  12. Quantum chemical studies on the corrosion inhibition of some sulphonamides on mild steel in acidic medium

    International Nuclear Information System (INIS)

    Arslan, Taner; Kandemirli, Fatma; Ebenso, Eno E.; Love, Ian; Alemu, Hailemichael

    2009-01-01

    Quantum chemical calculations using the density functional theory (DFT) and some semi-empirical methods were performed on four sulphonamides (sulfaguanidine, sulfamethazine, sulfamethoxazole and sulfadiazine) used as corrosion inhibitors for mild steel in acidic medium to determine the relationship between molecular structure and their inhibition efficiencies. The results of the quantum chemical calculations and experimental %IE were subjected to correlation analysis and indicate that their inhibition effect are closely related to E HOMO , E LUMO , hardness, polarizability, dipole moment and charges. The %IE increased with increase in the E HOMO and decrease in E HOMO - E LUMO . The negative sign of the E HOMO values and other kinetic and thermodynamic parameters indicates that the data obtained support physical adsorption mechanism

  13. Inhibition of corrosion of carbon steel by heptane sulphonic acid – Zn2+ system

    Directory of Open Access Journals (Sweden)

    C. MARY ANBARAS

    2012-03-01

    Full Text Available Corrosion inhibition of carbon steel in dam water by sodium heptane sulphonate (SHS and zinc ion system was investigated using weight loss and potentiodynamic polarization methods. Results of weight loss method indicated that inhibition efficiency (IE increased as the inhibitor concentration increased. A synergistic effect existed between SHS and Zn2+. The influence of sodium potassium tartrate (SPT on the IE of the SHS-Zn2+ system was evaluated. As the immersion period increased, the IE decreased. Polarization study revealed that SHS-Zn2+ system functioned as a cathodic inhibitor. AC impedance spectra revealed that a protective film was formed on the metal surface. The nature of the metal surface was analyzed by FTIR spectra, SEM and AFM analyses.

  14. The Inhibition Effect of Potassium Iodide on the Corrosion of Pure Iron in Sulphuric Acid

    Directory of Open Access Journals (Sweden)

    Tarik Attar

    2014-01-01

    Full Text Available The use of inorganic inhibitors as an alternative to organic compounds is based on the possibility of degradation of organic compounds with time and temperature. The inhibition effect of potassium iodide on the corrosion of pure iron in 0.5 M H2SO4 has been studied by weight loss. It has been observed from the results that the inhibition efficiency (IE% of KI increases from 82.17% to 97.51% with the increase in inhibitor concentration from 1·10−4 to 2·10−3 M. The apparent activation energy (Ea and the equilibrium constant of adsorption (Kads were calculated. The adsorption of the inhibitor on the pure iron surface is in agreement with Langmuir adsorption isotherm.

  15. Inhibition of mild steel corrosion in acid solution by Pheniramine drug: Experimental and theoretical study

    Energy Technology Data Exchange (ETDEWEB)

    Ahamad, Ishtiaque [Department of Applied Chemistry, Institute of Technology, Banaras Hindu University, Varanasi 221 005 (India); Prasad, Rajendra [Department of Chemistry, SGB Amravati University, Amravati 444 602 (India); Quraishi, M.A., E-mail: maquraishi@rediffmail.co [Department of Applied Chemistry, Institute of Technology, Banaras Hindu University, Varanasi 221 005 (India)

    2010-09-15

    Inhibition of mild steel corrosion in 1 M HCl solution by Pheniramine drug was studied using weight loss, electrochemical impedance spectroscopy, linear polarization resistance, and potentiodynamic polarization measurements. The values of activation energy (E{sub a}) and different thermodynamic parameters such as adsorption equilibrium constant (K{sub ads}), free energy of adsorption ({Delta}G{sub ads}{sup o}), adsorption enthalpy ({Delta}H{sub ads}{sup o}) and adsorption entropy ({Delta}S{sub ads}{sup o}) were calculated and discussed. The adsorption process of studied drug on mild steel surface obeys the Langmuir adsorption isotherm. Potentiodynamic polarization measurements showed that Pheniramine is mixed-type inhibitor. Further, theoretical calculations were carried out and relations between computed parameters and experimental inhibition efficiency were discussed.

  16. Inhibition of mild steel corrosion in acid solution by Pheniramine drug: Experimental and theoretical study

    International Nuclear Information System (INIS)

    Ahamad, Ishtiaque; Prasad, Rajendra; Quraishi, M.A.

    2010-01-01

    Inhibition of mild steel corrosion in 1 M HCl solution by Pheniramine drug was studied using weight loss, electrochemical impedance spectroscopy, linear polarization resistance, and potentiodynamic polarization measurements. The values of activation energy (E a ) and different thermodynamic parameters such as adsorption equilibrium constant (K ads ), free energy of adsorption (ΔG ads o ), adsorption enthalpy (ΔH ads o ) and adsorption entropy (ΔS ads o ) were calculated and discussed. The adsorption process of studied drug on mild steel surface obeys the Langmuir adsorption isotherm. Potentiodynamic polarization measurements showed that Pheniramine is mixed-type inhibitor. Further, theoretical calculations were carried out and relations between computed parameters and experimental inhibition efficiency were discussed.

  17. Structural, theoretical and corrosion inhibition studies on some transition metal complexes derived from heterocyclic system

    Science.gov (United States)

    Gupta, Shraddha Rani; Mourya, Punita; Singh, M. M.; Singh, Vinod P.

    2017-06-01

    A Schiff base, (E)-N‧-((1H-indol-3-yl)methylene)-2-aminobenzohydrazide (Iabh) and its Mn(II), Co(II), Ni(II), Cu(II) and Zn(II) complexes have been synthesized. These compounds have been characterized by different physico-chemical and spectroscopic tools (UV-Vis, IR, NMR and ESI-Mass). The molecular structure of Iabh is determined by single crystal X-ray diffraction technique. The ligand Iabh displays E-configuration about the >Cdbnd N- bond. The structure of ligand is stabilized by intra-molecular H-bonding. In all the metal complexes the ligand coordinates through azomethine-N and carbonyl-O resulting a distorted octahedral geometry for Mn(II), Co(II) and Cu(II) complexes in which chloride ions occupy axial positions. Ni(II) and Zn(II) complexes, however, form 4-coordinate distorted square planer and tetrahedral geometry around metal ion, respectively. The structures of the complexes have been satisfactorily modeled by calculations based on density functional theory (DFT) and time dependent-DFT (TD-DFT). The corrosion inhibition study of the compounds have been performed against mild steel in 0.5 M H2SO4 solution at 298 K by using weight loss, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). They show appreciable corrosion inhibition property.

  18. Inhibition of microbial concrete corrosion by Acidithiobacillus thiooxidans with functionalised zeolite-A coating.

    Science.gov (United States)

    Haile, Tesfaalem; Nakhla, George

    2009-01-01

    The inhibition of the corrosive action of Acidithiobacillus thiooxidans on concrete specimens coated by functionalised zeolite-A containing 14% zinc and 5% silver by weight was studied. Uncoated concrete specimens, epoxy-coated concrete specimens (EP), and functionalised zeolite-A coated concrete specimens with epoxy to zeolite weight ratios of 3:1 (Z1), 2:2 (Z2) and 1:3 (Z3) were studied. Specimens were characterised by x-ray powder diffraction and field emission scanning electron microscopy for the identification of corrosion products and morphological changes. Biomass growth at the conclusion of the 32-day experiments was 4, 179 and 193 mg volatile suspended solids g(-1) sulphur for the uncoated, EP and Z1 specimens, whereas that of Z2 and Z3 were negligible. In the uncoated, EP and Z1 specimens, sulphate production rates were 0.83, 9.1 and 8.8 mM SO(4)(2-) day(-1) and the specific growth rates, mu, were 0.14, 0.57 and 0.47 day(-1), respectively. The corresponding values for Z2 and Z3 were negligible due to their bacterial inhibition characteristics.

  19. Electrochemical evaluation of inhibition efficiency of ciprofloxacin on the corrosion of copper in acid media

    Energy Technology Data Exchange (ETDEWEB)

    Thanapackiam, P. [Department of Chemistry, Coimbatore Institute of Technology, Coimbatore, Tamilnadu, 641 014 (India); Rameshkumar, Subramaniam [Department of Chemistry, Sri Vasavi College, Erode, Tamilnadu, 638 316 (India); Subramanian, S.S. [Department of Chemistry, PSG College of Technology, Coimbatore, Tamilnadu, 641 004 (India); Mallaiya, Kumaravel, E-mail: mkvteam.research@gmail.com [Department of Chemistry, PSG College of Technology, Coimbatore, Tamilnadu, 641 004 (India)

    2016-05-01

    The inhibition efficiency of ciprofloxacin on the corrosion of copper was studied in 1.0MHNO{sub 3} and 0.5MH{sub 2}SO{sub 4} solutions by electrochemical impedance spectroscopy and potentiodynamic polarization techniques. The corrosion inhibition action of ciprofloxacin was observed to be of mixed type in both the acid media, but with more of a cathodic nature. The experimental data were found to fit well with the Langmuir adsorption isotherm. The thermodynamic parameters such as adsorption equilibrium constant(K{sub ads}), free energy of adsorption(ΔG{sub ads}), activation energy(E{sub a}) and potential of zero charge(PZC) showed that the adsorption of ciprofloxacin onto copper surface involves both physisorption and chemisorption. - Highlights: • The inhibitor efficiency increases with increase in ciprofloxacin concentration. • Polarization measurements show that ciprofloxacin acts as a mixed type inhibitor. • The adsorption of the inhibitor on copper surface follows Langmuir adsorption isotherm. • The negative values of ΔG{sub ads} indicates that the adsorption is spontaneous and exothermic.

  20. Corrosion inhibition of Eleusine aegyptiaca and Croton rottleri leaf extracts on cast iron surface in 1 M HCl medium

    International Nuclear Information System (INIS)

    Rajeswari, Velayutham; Kesavan, Devarayan; Gopiraman, Mayakrishnan; Viswanathamurthi, Periasamy; Poonkuzhali, Kaliyaperumal; Palvannan, Thayumanavan

    2014-01-01

    Graphical abstract: - Highlights: • Eleusine aegyptiaca and Croton rottleri are commonly available, less-toxic and eco-friendly inhibitors for cast iron corrosion. • The active constituents present in extracts adsorbed on the iron surface to inhibit the acidic corrosion. • The higher values of E a and ΔH * point out the higher inhibition efficiency noticed for the inhibitors. • Weight loss methods at various temperature and spectral data provides evidence for adsorption mechanism of inhibitors. - Abstract: The adsorption and corrosion inhibition activities of Eleusine aegyptiaca (E. aegyptiaca) and Croton rottleri (C. rottleri) leaf extracts on cast iron corrosion in 1 M hydrochloric acid solution were studied first time by weight loss and electrochemical techniques viz., Tafel polarization and electrochemical impedance spectroscopy. The results obtained from the weight loss and electrochemical methods showed that the inhibition efficiency increased with inhibitor concentrations. It was found that the extracts acted as mixed-type inhibitors. The addition of halide additives (KCl, KBr, and KI) on the inhibition efficiency has also been investigated. The adsorption of the inhibitors on cast iron surface both in the presence and absence of halides follows the Langmuir adsorption isotherm model. The inhibiting nature of the inhibitors was supported by FT-IR, UV–vis, Wide-angle X-ray diffraction and SEM methods

  1. Corrosion and corrosion fatigue of airframe aluminum alloys

    Science.gov (United States)

    Chen, G. S.; Gao, M.; Harlow, D. G.; Wei, R. P.

    1994-01-01

    Localized corrosion and corrosion fatigue crack nucleation and growth are recognized as degradation mechanisms that effect the durability and integrity of commercial transport aircraft. Mechanically based understanding is needed to aid the development of effective methodologies for assessing durability and integrity of airframe components. As a part of the methodology development, experiments on pitting corrosion, and on corrosion fatigue crack nucleation and early growth from these pits were conducted. Pitting was found to be associated with constituent particles in the alloys and pit growth often involved coalescence of individual particle-nucleated pits, both laterally and in depth. Fatigue cracks typically nucleated from one of the larger pits that formed by a cluster of particles. The size of pit at which fatigue crack nucleates is a function of stress level and fatigue loading frequency. The experimental results are summarized, and their implications on service performance and life prediction are discussed.

  2. INHIBITION EFFECT OF FLAVONOID EXTRACT OF Euphorbia Guyoniana ON THE CORROSION OF MILD STEEL IN H2SO4 MEDIUM

    Directory of Open Access Journals (Sweden)

    S. Chihi

    2009-08-01

    Full Text Available The influence of flavonoids extracts of three parts of Euphorbia Guyoniana towards the corrosion of type API 5L X52 steel in 15% H2SO4 has been evaluated by weight loss method and polarization technique. The results showed that extracts are a good inhibitors for API 5L X52 steel in this medium. The corrosion inhibition efficiency increases on increasing plant extracts concentration. The inhibition is attributed to the adsorption of the surface of the metal. Potentiodynamic polarization results revealed that the studied inhibitors behave as a mixed type.

  3. The jet impingement cell: A valuable device for investigating CO{sub 2} corrosion

    Energy Technology Data Exchange (ETDEWEB)

    Kinsella, Brian; John, Douglas; Bailey, Stuart; De Marco, Roland [Western Australian Corrosion Research Group, School of Applied Chemistry, Curtin University of Technology, GPO Box U1987, Perth WA, 6845 (Australia)

    2004-07-01

    The jet impingement cell (JIC) is a valuable technique for the investigation of carbon dioxide corrosion of steel and its inhibition under high flow conditions or high wall shear stress. Despite the use of the JIC in corrosion testing laboratories not a great deal has been published on the design and calibration of these cells. In the evaluation of corrosion inhibitors, the type of corrosion and relative performance of the inhibitors depends on the metallurgy of the steel used to manufacture electrodes and measure the corrosion rate. This paper covers aspects of cell design and the determination of mass transfer and wall shear stress at electrodes used in the cell. The performance of different generic type corrosion inhibitors and their affect on the type of corrosion (i.e, uniform, pitting and crevice corrosion) is shown and discussed. (authors)

  4. Corrosion inhibition of mild steel in acidic media using newly synthesized heterocyclic organic molecules: Correlation between inhibition efficiency and chemical structure

    Energy Technology Data Exchange (ETDEWEB)

    Ouici, H. B., E-mail: ouici.houari@yahoo.fr; Guendouzi, A., E-mail: guendouzzi@yahoo.fr [Departement of Chimistry, Faculty of Sciences, University of Saïda (Algeria); Benali, O. [Department of Biology, Faculty of Science, University of Saida (Algeria)

    2015-03-30

    The corrosion inhibition of mild steel in 5% HCl solutions by some new synthesized organic compounds namely 3-(2-methoxyphenyl) 5-mercapto-1. 2. 4-triazole (2-MMT), 3-(3-methoxyphenyl) 5-mercapto-1. 2. 4-triazole (3-MMT) and 3-(2-hydroxyphenyl) 5-mercapto-1. 2. 4-triazole (2-HMT) was investigated using weight loss and potentiostatic polarization techniques. These measurements reveal that the inhibition efficiency obtained by these compounds increased by increasing their concentration. The inhibition efficiency follows the order 2-MMT >3-MMT >2-HMT. Polarization studies show that these compounds are of the mixed type but dominantly act as a cathodic inhibitors for mild steel in 5% HCl solutions. These inhibitors function through adsorption following Langmuir isotherm. Activation energy and Gibbs free energy for adsorption of inhibitors are calculated. Molecular modeling has been conducted to correlate the corrosion inhibition properties with the calculated quantum chemical parameters.

  5. Influence of molecular packing on the corrosion inhibition properties of self-assembled octadecyltrichlorosilane monolayers on silicon

    International Nuclear Information System (INIS)

    Hsieh, Shuchen; Chao, Wei-Jay; Lin, Pei-Ying; Hsieh, Chiung-Wen

    2014-01-01

    Highlights: •Molecular packing plays an important role in determining SAM film properties. •Loose-packed OTS monolayers on silicon were corroded by exposure to KMnO 4 . •Dense-packed OTS SAM films exhibited excellent corrosion protection efficacy. -- Abstract: The corrosion inhibition properties of octadecyltrichlorosilane (OTS) self-assembled monolayers (SAMs) on silicon were investigated. Atomic force microscopy (AFM), X-ray photoelectron spectroscopy (XPS), contact angle (CA), and lateral force microscopy (LFM) were used to determine the OTS film formation time, packing density, and corrosion protection efficacy. The OTS films reached adsorption saturation after 15 s; however, the molecular density continued to increase up to 24 h. The films were exposed to the strong oxidant KMnO 4 , and while 15-s film samples exhibited corrosion after a 1 min exposure, samples with films grown for 24 h were protected even after 24 h

  6. Inhibition treatment of the corrosion of lead artefacts in atmospheric conditions and by acetic acid vapour: use of sodium decanoate

    International Nuclear Information System (INIS)

    Rocca, E.; Rapin, C.; Mirambet, F.

    2004-01-01

    The efficiency of linear sodium decanoate, CH 3 (CH 2 ) 8 COONa (noted NaC 10 ), as corrosion inhibitor of lead was determined by electrochemical techniques in two corrosive mediums: ASTM D1384 standard water and acetic acid-enriched solutions. Best results were obtained with 0.05 mol l -1 of NaC 10 solution. In these conditions, the inhibition efficiency can be estimated of 99.9%. The corrosion inhibition effect was confirmed by cyclic atmospheric tests in a climatic chamber in two different conditions: water saturated vapour, and acid acetic enriched vapour simulating the atmosphere in the wooden displays in museums. Surface analyses by SEM and X-ray diffraction indicate that the metal protection is due to the formation of a protective layer mainly composed of lead decanoate Pb(C 10 ) 2 (metallic soap). This inhibition treatment was applied on objects of metallic cultural heritage: gallo-roman sarcophagus in lead. Electrochemical methods confirm the efficiency of treatment on archaeological materials. In conclusion, this inhibitor treatment seems to be very promising against the atmospheric corrosion and the corrosion by organic acid vapour in museums

  7. Application of Moessbauer spectroscopy to the study of tannins inhibition of iron and steel corrosion

    Energy Technology Data Exchange (ETDEWEB)

    Jaen, Juan A., E-mail: jjaen@ancon.up.ac.pa [Universidad de Panama, CITEN, Depto. de Quimica Fisica (Panama); Obaldia, J. De; Rodriguez, M. V. [Universidad de Panama, Escuela de Quimica, Facultad de Ciencias Naturales, Exactas y Tecnologia (Panama)

    2011-11-15

    The inhibitory effect of tannins was investigated using, among others, potentiodynamic polarizations and Moessbauer spectroscopy. These techniques confirmed that the nature, pH and concentration of tannic solution are of upmost importance in the inhibitory properties of the solutions. It is observed that at low tannin concentration or pH, both, hydrolizable and condensed tannins, effectively inhibit iron corrosion, due to the redox properties of tannins. At pH Almost-Equal-To 0, Moessbauer spectra of the frozen aqueous solutions of iron(III) with the tannin solutions showed that iron is in the form of a monomeric species [Fe(H{sub 2}O){sub 6}]{sup 3 + }, without coordination with the functional hydroxyl groups of the tannins. The suspended material consisted of amorphous ferric oxide and oxyhydroxides, though with quebracho tannin partly resulted in complex formation and in an iron (II) species from a redox process. Other tannins, such as chestnut hydrolysable tannins, do not complex iron at this low pH. Tannins react at high concentrations or pH (3 and 5) to form insoluble blue-black amorphous complexes of mono-and bis-type tannate complexes, with a relative amount of the bis-ferric tannate generally increasing with pH. Some Fe{sup 2 + } in the form of hydrated polymeric ferrous tannate could be obtained. At pH 7, a partially hydrolyzed ferric tannate complex was also formed. The latter two phases do not provide corrosion protection. Tannin solutions at natural pH react with electrodeposited iron films (approx. 6 {mu}m) to obtain products consisting only on the catecholate mono-complex of ferric tannate. Some aspects of the mechanism of tannins protection against corrosion are discussed.

  8. Corrosion inhibition by inorganic cationic inhibitors on the high strength alumunium alloy, 2024-T3

    Science.gov (United States)

    Chilukuri, Anusha

    The toxicity and carcinogenic nature of chromates has led to the investigation of environmentally friendly compounds that offer good corrosion resistance to AA 2024-T3. Among the candidate inhibitors are rare earth metal cationic (REM) and zinc compounds, which have received much of attention over the past two decades. A comparative study on the corrosion inhibition caused by rare earth metal cations, Ce3+, Pr3+, La3+ and Zn2+ cations on the alloy was done. Cathodic polarization showed that these inhibitor ions suppress the oxygen reduction reaction (ORR) to varying extents with Zn2+ providing the best inhibition. Pr3+ exhibited windows of concentration (100-300 ppm) in which the corrosion rate is minimum; similar to the Ce3+ cation. Scanning Electron Microscopy (SEM) studies showed that the mechanism of inhibition of the Pr3+ ion is also similar to that of the Ce3+ ion. Potentiodynamic polarization experiments after 30 min immersion time showed greatest suppression of oxygen reduction reaction in neutral chloride solutions (pH 7), which reached a maximum at a Zn2+ ion concentration of 5 mM. Anodic polarization experiments after 30 min immersion time, showed no anodic inhibition by the inhibitor in any concentration (0.1 mM - 10 mM) and at any pH. However, anodic polarization of samples immersed after longer immersion times (upto 4 days) in mildly acidic Zn2+ (pH 4) solutions showed significant reduction in anodic kinetics indicating that zinc also acts as a “slow anodic inhibitor”. In contrast to the polarization experiments, coupons exposed to inhibited acidic solutions at pH 4 showed complete suppression of dissolution of Al2CuMg particles compared to zinc-free solutions in the SEM studies. Samples exposed in pH 4 Zn2+-bearing solution exhibited highest polarization resistance which was also observed to increase with time. In deaerated solutions, the inhibition by Zn2+ at pH 4 is not observed as strongly. The ability to make the interfacial electrolyte

  9. Method of inhibiting concentration of radioactive corrosion products in cooling water or nuclear power plants

    International Nuclear Information System (INIS)

    Takabayashi, Jun-ichi; Hishida, Mamoru; Ishikura, Takeshi.

    1979-01-01

    Purpose: To suppress the increase in the concentration of the radioactive corrosion products in cooling water, which increase is accompanied by the transference of the corrosion products activated and accumulated in the core due to dissolution and exfoliation into the core water, and inhibit the flowing of said products out of the core and the diffusion thereof into the cooling system, thereby to prevent the accumulation of said products in the cooling system and prevent radioactive contaminations. Method: In a nuclear power plant of a BWR type light water reactor, when the temperature of the pile water is t 0 C, hydrogen is injected in cooling water in a period of time from immediately before starting of the drive stopping operation of the nuclear power plant to immediately after the termination of restarting operation, whereby the concentration of hydrogen in the reactor water through said period is maintained at a value more than 2exp (0.013 t) cm 3 N.T.P./kg H 2 O. (Aizawa, K.)

  10. Relationships between chemical compositions, microstructure, and corrosion properties in molybdenum ion implanted aluminum

    International Nuclear Information System (INIS)

    Kim, S.

    1986-01-01

    This thesis compares the corrosion properties of Al annealed after implantation with selected Mo concentrations to those of as-implanted Al with same Mo level and to pure Al. The principal results in this investigation are the improvement in the pitting corrosion resistance for Al implanted with Mo relative to pure Al in both the as-implanted and as-implanted-annealed state. The corrosion properties were related to the microstructures and chemical profiles in the surface-modified-regions. Potentiodynamic measurements indicate that stability of various species on the surface controls corrosion behavior in the Al-Mo system. Dual energy Mo implant procedure was used to produce a relatively thick ion implanted layer. The processing parameters were selected to produce specimen containing a continuous Al 12 Mo film with two different microstructures in the annealed material. The most improved pitting corrosion resistance was achieved in an as-implanted alloy which was implanted at 95 keV and then at 25 keV. This alloy was very resistant to pitting corrosion in a neutral aqueous solution containing 0.1 M chloride ion. Surface chemical analysis by Auger electron spectroscopy indicates that the role of Mo in inhibiting pitting corrosion is related to the formation of stable Mo oxide film

  11. The role of acid anion on the inhibition of the acidic corrosion of steel by lupine extract

    Energy Technology Data Exchange (ETDEWEB)

    Abdel-Gaber, A.M. [Chemistry Department, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt)], E-mail: ashrafmoustafa@yahoo.com; Abd-El-Nabey, B.A.; Saadawy, M. [Chemistry Department, Faculty of Science, Alexandria University, Ibrahimia, P.O. Box 426, Alexandria 21321 (Egypt)

    2009-05-15

    The inhibitive effect of lupine (Lupinous albus L.) extract on the corrosion of steel in aqueous solution of 1 M sulphuric and 2 M hydrochloric acids was investigated by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) techniques. Potentiodynamic polarization curves indicated that the lupine extract acts as a mixed-type inhibitor. EIS measurements showed that the dissolution process is under activation control. The inhibition efficiency of the extract obtained from impedance and polarization measurements was in a good agreement and was found to increase with increasing concentration of the extract. The obtained results showed that, the lupine extract could serve as an effective inhibitor for the corrosion of steel in acid media and the extract was more effective in case of hydrochloric acid. Theoretical fitting of the corrosion data to the kinetic-thermodynamic model was tested to show the nature of adsorption.

  12. The inhibition performance of long-chain alkyl-substituted benzimidazole derivatives for corrosion of mild steel in HCl

    International Nuclear Information System (INIS)

    Zhang, Dongqin; Tang, Yongming; Qi, Sijun; Dong, Dawei; Cang, Hui; Lu, Gang

    2016-01-01

    Highlights: • Inhibition performance of long-chain alkyl-substituted benzimidazole. • Benzimidazole segment donating electrons to metal surface. • Non-polar long chain enhancing inhibition by the barrier effect. • Molecular form of DBI more tightly adsorbs on the steel than its protonated form. - Abstract: The corrosion inhibition of a new benzimidazole derivative, 6-(dodecyloxy)-1H-benzo[d]imidazole (DBI), for mild steel in 1 M HCl was investigated in this paper. Computational chemistry was performed to explore the adsorption of DBI on metal surface. Inhibition performance of DBI is attributed to both the direct interaction of benzimidazole segment with iron surface and the barrier effect of the non-polar long chain against aggressive solution. Compared to the protonated form, the molecular form of DBI could more tightly interact with iron surface. These results show that the long-chain alkyl-substituted benzimidazole derivative is of great potential application as corrosion inhibitor.

  13. The Inhibitive Action Of Sodium Soya Sulphonate Towards The Corrosion Of Aluminium In Hydrochloric Acid

    OpenAIRE

    Mourad, M. Y.; Mead, A. I.; Seliman, S. A.

    1993-01-01

    The dissolution of aluminium in 2M hydrochloric acid in the presence of sodium soya sulphonate (SSS) as corrosion inhibitor has been studied using hydrogen evolution and thermometric methods. The two methods gave consistent results. The results obtained indicate that the inhibitive effect of the sulphonated mixture relates to chemisorption mechanism on the metal surface via the n electrons in the double bonds. تمت دراسة ذوبان الألمونيوم في محلول 2 مولارى من حمض الهيدروكلوريك في وجود سلفونا...

  14. Corrosion of the reinforcing steel in the inhibited sawdust concrete construction

    International Nuclear Information System (INIS)

    Kobuliev, Z.V.

    2005-01-01

    In the article described the way of protection of the reinforcing steel in sawdust concrete construction by adding to inhibited sawdust concrete mixture containing nitrate-nitride calcium chloride (NNCC) and (NH 4 ) 2 Cr 2 O 7 , also NaNO 2 + NaNO 3 +NH 4 Cl and CaCl 2 +(NH 4 ) 2 +Cr 2 . There is determined, that the use of these additives increase strength properties of sawdust concrete at 28 day to 40-55% in comparison with sawdust concrete containing CaCl 2 , and decrease its corrosion-resistance activity, and provided reliability under condition of double excess of inhibitor ions (NO 2- , Cr 2 O 7- ) in comparison with ions (Cl-)

  15. Corrosion of API 5L B and X52 in crude oil/water/gas mixtures

    Energy Technology Data Exchange (ETDEWEB)

    Perdomo, J J; Gonzalez, J J; Viloria, A; De Veer, H; De Abreu, Y

    2000-02-01

    Laboratory and field tests were conducted to evaluate the corrosion behavior of API 5L grade B and X52 steels using Furrial's crude oil in the presence of water and gas containing carbon dioxide (CO{sub 2}) and hydrogen sulfide (H{sub 2}S). The results suggest that the corrosiveness of this crude oil/water/gas mixture is not detrimental to either steel. However, pitting corrosion was observed. The low general corrosion rates measured were attributed to the natural inhibiting properties of the crude oil.

  16. Corrosion of API 5L B and X52 in crude oil/water/gas mixtures

    Energy Technology Data Exchange (ETDEWEB)

    Perdomo, J.J.; Gonzalez, J.J.; Viloria, A.; De Veer, H.; De Abreu, Y.

    2000-02-01

    Laboratory and field tests were conducted to evaluate the corrosion behavior of API 5L grade B and X52 steels using Furrial's crude oil in the presence of water and gas containing carbon dioxide (CO{sub 2}) and hydrogen sulfide (H{sub 2}S). The results suggest that the corrosiveness of this crude oil/water/gas mixture is not detrimental to either steel. However, pitting corrosion was observed. The low general corrosion rates measured were attributed to the natural inhibiting properties of the crude oil.

  17. Synthesis, characterization and corrosion inhibition properties of benzamide-2-chloro-4-nitrobenzoic acid and anthranilic acid-2-chloro-4-nitrobenzoic acid for mild steel corrosion in acidic medium

    Science.gov (United States)

    Pandey, Archana; Verma, Chandrabhan; Singh, B.; Ebenso, Eno E.

    2018-03-01

    The present study deals with the synthesis of two new compounds namely, benzamide - 2-chloro-4-nitrobenzoic acid (BENCNBA) and anthranilic acid-2-chloro-4-nitrobenzoic acid (AACNBA) using solid phase reactions. The phase diagram studies revealed that formation of the investigated compounds occurs in 1:1 molar ratio. The synthesized compounds were characterized using several spectral techniques such as FT-IR, 1H and 13C NMR, UV-Vis, powder X-ray diffraction (PXRD). Single crystal XRD (SCXRD) study showed that both BENCNBA and AACNBA compounds crystallize in triclinic crystal system with P-1 space group. Further, the presence of intermolecular hydrogen bonding between the constituent components was also supported by single crystal X-ray diffraction (SCXRD) method. Heat of mixing, entropy of fusion, roughness parameter, interfacial energy and excess thermodynamic functions have also been computed using the enthalpy of fusion values derived from differential scanning calorimeter (DSC) study. The inhibition effect of BENCNBA and AACNBA on the mild steel corrosion in hydrochloric acid solution was tested using electrochemical methods. Electrochemical impedance spectroscopy (EIS) study revealed that both BENCNBA and AACNBA behaved as interface corrosion inhibitors and showed maximum inhibition efficiencies of 95.71% and 96.42%, respectively at 400 ppm (1.23 × 10-3 M) concentration. Potentiodynamic polarization (PDP) measurements suggested that BENCNBA and AACNBA acted as mixed type corrosion inhibitors. EIS and PDP results showed that BENCNBA and AACNBA act as efficient corrosion inhibitors for mild steel and their inhibition efficiencies enhances on increasing their concentrations.

  18. Influence of liquid surface segregation on the pitting corrosion behavior of semi-solid metal high pressure die cast alloy F357

    CSIR Research Space (South Africa)

    Moller, H

    2009-01-01

    Full Text Available Cl aqueous solution. It is shown that pitting attack occurs preferentially in the eutectic regions at the interface between silicon particles and the alpha phase in the eutectic. Since the surface liquid segregation layer consists of mainly eutectic...

  19. Corrosion Inhibiting Mechanism of Nitrite Ion on the Passivation of Carbon Steel and Ductile Cast Iron for Nuclear Power Plants

    Directory of Open Access Journals (Sweden)

    K. T. Kim

    2015-01-01

    Full Text Available While NaNO2 addition can greatly inhibit the corrosion of carbon steel and ductile cast iron, in order to improve the similar corrosion resistance, ca. 100 times more NaNO2 addition is needed for ductile cast iron compared to carbon steel. A corrosion and inhibition mechanism is proposed whereby NO2- ion is added to oxidize. The NO2- ion can be reduced to nitrogen compounds and these compounds may be absorbed on the surface of graphite. Therefore, since nitrite ion needs to oxidize the surface of matrix and needs to passivate the galvanic corroded area and since it is absorbed on the surface of graphite, a greater amount of corrosion inhibitor needs to be added to ductile cast iron compared to carbon steel. The passive film of carbon steel and ductile cast iron, formed by NaNO2 addition showed N-type semiconductive properties and its resistance, is increased; the passive current density is thus decreased and the corrosion rate is then lowered. In addition, the film is mainly composed of iron oxide due to the oxidation by NO2- ion; however, regardless of the alloys, nitrogen compounds (not nitrite were detected at the outermost surface but were not incorporated in the inner oxide.

  20. A Revisit to the Corrosion Inhibition of Aluminum in Aqueous Alkaline Solutions by Water-Soluble Alginates and Pectates as Anionic Polyelectrolyte Inhibitors

    Directory of Open Access Journals (Sweden)

    Refat Hassan

    2013-01-01

    Full Text Available The corrosion behavior of aluminum (Al in alkaline media in presence of some natural polymer inhibitors has been reinvestigated. The inhibition action of the tested inhibitors was found to obey both Langmuir and Freundlich isotherms models. The inhibition efficiency was found to increase with increasing the inhibitors concentration and decrease with increasing the temperature, suggesting physical adsorption mechanism. Factors such as the concentration and geometrical structure of the inhibitor, concentration of the corrosive medium, and temperature affecting the corrosion rates were examined. The kinetic parameters were evaluated, and a suitable corrosion mechanism consistent with the kinetic results obtained is suggested and discussed.

  1. Application of calculated NMR parameters, aromaticity indices and wavefunction properties for evaluation of corrosion inhibition efficiency of pyrazine inhibitors

    Science.gov (United States)

    Behzadi, Hadi; Manzetti, Sergio; Dargahi, Maryam; Roonasi, Payman; Khalilnia, Zahra

    2018-01-01

    In light of the importance of developing novel corrosion inhibitors, a series of quantum chemical calculations were carried out to evaluate 15N chemical shielding CS tensors as well as aromaticity indexes including NICS, HOMA, FLU, and PDI of three pyrazine derivatives, 2-methylpyrazine (MP), 2-aminopyrazine (AP) and 2-amino-5-bromopyrazine (ABP). The NICS parameters have been shown in previous studies to be paramount to the prediction of anti-corrosion properties, and have been combined here with HOMA, FLU and PDI and detailed wavefunction analysis to determine the effects from bromination and methylation on pyrazine. The results show that the electron density around the nitrogens, represented by CS tensors, can be good indicators of anti-corrosion efficiency. Additionally, the NICS, FLU and PDI, as aromaticity indicators of molecule, are well correlated with experimental corrosion inhibition efficiencies of the studied inhibitors. Bader sampling and detailed wavefunction analysis shows that the major effects from bromination on the pyrazine derivatives affect the Laplacian of the electron density of the ring, delocalizing the aromatic electrons of the carbon atoms into lone pairs and increasing polarization of the Laplacian values. This feature is well agreement with empirical studies, which show that ABP is the most efficient anti-corrosion compound followed by AP and MP, a property which can be attributed and predicted by derivation of the Laplacian of the electron density of the ring nuclei. This study shows the importance of devising DFT methods for development of new corrosion inhibitors, and the strength of electronic and nuclear analysis, and depicts most importantly how corrosion inhibitors composed of aromatic moieties may be modified to increase anti-corrosive properties.

  2. Corrosion and protection of magnesium alloys

    Energy Technology Data Exchange (ETDEWEB)

    Ghali, E. [Laval Univ., Quebec City, PQ (Canada). Dept. of Mining and Metallurgy

    2000-07-01

    The oxide film on magnesium offers considerable surface protection in rural and some industrial environments and the corrosion rate lies between that of aluminum and low carbon steels. Galvanic coupling of magnesium alloys, high impurity content such as Ni, Fe, Cu and surface contamination are detrimental for corrosion resistance of magnesium alloys. Alloying elements can form secondary particles which are noble to the Mg matrix, thereby facilitating corrosion, or enrich the corrosion product thereby possibly inhibiting the corrosion rate. Bimetallic corrosion resistance can be increased by fluxless melt protection, choice of compatible alloys, insulating materials, and new high-purity alloys. Magnesium is relatively insensible to oxygen concentration. Pitting, corrosion in the crevices, filiform corrosion are observed. Granular corrosion of magnesium alloys is possible due to the cathodic grain-boundary constituent. More homogeneous microstructures tend to improve corrosion resistance. Under fatigue loading conditions, microcrack initiation in Mg alloys is related to slip in preferentially oriented grains. Coating that exclude the corrosive environments can provide the primary defense against corrosion fatigue. Magnesium alloys that contain neither aluminum nor zinc are the most SCC resistant. Compressive surface residual stresses as that created by short peening increase SCC resistance. Cathodic polarization or cladding with a SCC resistant sheet alloy are good alternatives. Effective corrosion prevention for magnesium alloy components and assemblies should start at the design stage. Selective surface preparation, chemical treatment and coatings are recommended. Oil application, wax coating, anodizing, electroplating, and painting are possible alternatives. Recently, it is found that a magnesium hydride layer, created on the magnesium surface by cathodic charging in aqueous solution is a good base for painting. (orig.)

  3. The effect of temperature and concentration on the corrosion inhibition mechanism of an amphiphilic amido-amine in CO2 saturated solution

    OpenAIRE

    Desimone, Paula Mariela; Gordillo, Gabriel Jorge; Simison, Silvia Noemi

    2017-01-01

    The corrosion inhibition mechanism of the N-[2-[(2-aminoethyl)amino]ethyl]-9-octadecenamide on mild steel surface in CO2-saturated 5% NaCl solution has been studied. The inhibition efficiency decreases with increasing temperature. Adsorption of the inhibitor studied is found to follow the Frumkin adsorption isotherm. EIS results show that the mechanism of its corrosion inhibition at concentrations higher than critical micelle concentration is by forming a protective porous bi-layer. The a...

  4. Study on Corrosion Inhibition Efficiency of Stem Alkaloid Extract of Different Varieties of Holy Basil on Aluminium in HCl Solution

    Energy Technology Data Exchange (ETDEWEB)

    Kumpawat, Nutan; Chaturvedi, Alok; Upadhyay, R. K. [Synthetic and Surface Science Laboratory, Ajmer (India)

    2012-08-15

    Corrosion inhibition efficiencies of holy basil on Al in HCl solution were studied by weight loss and thermometric methods in presence and in absence of stem extract of three different varieties of holy basil viz. ocimum basilicum (E{sub B}), ocimum canum (E{sub C}) and ocimum sanctum (E{sub S}). Inhibition efficiency increases with the increasing concentration of stem extract and decreases with increases in acid strength. Results show that all varieties under study are good corrosion inhibitors, among which, E{sub B} is most effective. Maximum inhibition efficiency was found 97.09% in 0.5N HCl solution with 0.6% stem extract. The Langmuir adsorption isotherm indicates that surface coverage also increases with increasing in the concentration of extract of stem in HCl solution.

  5. Study on Corrosion Inhibition Efficiency of Stem Alkaloid Extract of Different Varieties of Holy Basil on Aluminium in HCl Solution

    International Nuclear Information System (INIS)

    Kumpawat, Nutan; Chaturvedi, Alok; Upadhyay, R. K.

    2012-01-01

    Corrosion inhibition efficiencies of holy basil on Al in HCl solution were studied by weight loss and thermometric methods in presence and in absence of stem extract of three different varieties of holy basil viz. ocimum basilicum (E B ), ocimum canum (E C ) and ocimum sanctum (E S ). Inhibition efficiency increases with the increasing concentration of stem extract and decreases with increases in acid strength. Results show that all varieties under study are good corrosion inhibitors, among which, E B is most effective. Maximum inhibition efficiency was found 97.09% in 0.5N HCl solution with 0.6% stem extract. The Langmuir adsorption isotherm indicates that surface coverage also increases with increasing in the concentration of extract of stem in HCl solution

  6. Inhibition of copper corrosion in sodium chloride solution by the self-assembled monolayer of sodium diethyldithiocarbamate

    Energy Technology Data Exchange (ETDEWEB)

    Liao, Q.Q., E-mail: liaoqq1971@yahoo.com.c [Key Lab of Shanghai Colleges and Universities for Electric Power Corrosion Control and Applied Electrochemistry, Shanghai Engineering Research Center of Energy - Saving in Heat Exchange Systems, Shanghai University of Electric Power, Shanghai 200090 (China); Yue, Z.W.; Yang, D. [Key Lab of Shanghai Colleges and Universities for Electric Power Corrosion Control and Applied Electrochemistry, Shanghai Engineering Research Center of Energy - Saving in Heat Exchange Systems, Shanghai University of Electric Power, Shanghai 200090 (China); Wang, Z.H. [Department of Chemistry, Tongji University, Shanghai 200092 (China); Li, Z.H. [Department of Chemistry, Fudan University, Shanghai 200433 (China); Ge, H.H. [Key Lab of Shanghai Colleges and Universities for Electric Power Corrosion Control and Applied Electrochemistry, Shanghai Engineering Research Center of Energy - Saving in Heat Exchange Systems, Shanghai University of Electric Power, Shanghai 200090 (China); Li, Y.J. [Department of Chemistry, Tongji University, Shanghai 200092 (China)

    2011-05-15

    Research highlights: DDTC is of low toxicity. DDTC SAM had good corrosion inhibition effects on copper in 3% NaCl solution. DDTC SAM was chemisorbed on copper surface by its S atoms. - Abstract: Sodium diethyldithiocarbamate (DDTC) self-assembled monolayer (SAM) on copper surface has been investigated by SERS and EDS and the results show that DDTC SAM is chemisorbed on copper surface by its S atoms with tilted orientation. Corrosion inhibition ability of DDTC SAM was measured in 3% NaCl solution using electrochemical methods. The impedance results indicate that the maximum inhibition efficiency of DDTC SAM can reach 99%. Quantum chemical calculations show that DDTC has relatively small {Delta}E between HOMO and LUMO and large negative charge in its two sulfur atoms, which facilitates the formation of a DDTC SAM on copper surface.

  7. Inhibition of the corrosion of steel in hydrochloric acid solution by some organic molecules containing the methylthiophenyl moiety

    International Nuclear Information System (INIS)

    Nataraja, S.E.; Venkatesha, T.V.; Manjunatha, K.; Poojary, Boja; Pavithra, M.K.; Tandon, H.C.

    2011-01-01

    Highlights: → Acid corrosion inhibition. → Work in small concentration. → Effective at higher temperature. → Effect of different functional groups, cyclisation and aromaticity. - Abstract: The corrosion inhibition effect of 2-[4-(methylthio) phenyl] acetohydrazide (HYD), 2-{[4-(methylthio) phenyl] acetyl} hydrazinecarbothioamide (TAD) and 5-[4-(methylthio) benzyl]-4H-1,2,4-triazole-3-thiol (TRD) on steel in 1.0 M HCl was investigated by mass loss and electrochemical methods. The effect of concentration, temperature and immersion time was studied. The results indicated that the compounds are efficient, mixed type and pursue Flory-Huggins adsorption isotherm. The inhibition efficiency at lower concentration of inhibitor decreased with temperature while at higher concentration, it is retained and the calculated free energy attributes this to comprehensive adsorption. The efficiency stands in the order TRD > TAD > HYD and is confirmed by the Quantum studies.

  8. Modelling and Optimization of Corrosion Inhibition of Mild Steel in Phosphoric Acid by Red Pomegranate Peels Aqueous Extract

    Directory of Open Access Journals (Sweden)

    Khalid Hamid Rashid

    2011-11-01

    Full Text Available Taguchi experimental design (TED is applied to find the optimum effectiveness of aqueous Red Pomegranate Peel (RPP extract as a green inhibitor for the corrosion of mild steel in 2M H3PO4 solution. The Taguchi methodology has been used to study the effects of changing, temperature, RPP concentration and contact period, at three levels. Weight-loss measurements were designed by construction a L9 orthogonal arrangement of experiments. Results of the efficiencies of inhibition were embraced for the signal to noise proportion & investigation of variance (ANOVA. The results were further processed with a MINITAB-17 software package to find the optimal conditions for inhibitor usage. Second order polynomial model was used for experimental data fitting. Optimum conditions for achieving the maximum corrosion inhibition efficiency are obtained from optimizing the above model and are found as follow: 39.66 °C temperature of acidic media, 38.29 ml/L inhibitor concentration and 2.95 h contact period. Results demonstrated that rate of corrosion was increased with temperature increasing & decreasing inhibitor concentration. It was concluded that the Taguchi design was adequately useful in the optimization of operating parameters and that RPP sufficiently inhibited the corrosion of steel at the range of variables studied.

  9. Inhibition of the corrosion of mild steel in hydrochloric acid by isatin and isatin glycine

    Directory of Open Access Journals (Sweden)

    B.I. Ita

    2006-12-01

    Full Text Available The inhibition of corrosion of mild steel in hydrochloric acid by isatin glycine (ING and isatin (IN at 30-60 oC and concentrations of 0.0001 M to 0.0005 M was studied via weight loss method. At the highest inhibitor concentration studied ING exhibited inhibition efficiency of 87% while IN exhibited 84% at 60 oC. A chemical adsorption mechanism was proposed on the basis of the temperature effect and obtained average activation energy values of 143.9 kJ/mol for ING and 118.5 kJ/mol for IN. The two inhibitors were confirmed to obey the Langmuir adsorption isotherm equation at the concentrations studied. Also a first-order type of mechanism was proposed from the kinetic treatment of the result. The difference in the inhibitory properties of the inhibitors was explained in terms of the difference in their molecular structures and solubility rather than difference in molecular weights alone.

  10. Risk Based Corrosion Studies at SRS

    International Nuclear Information System (INIS)

    Hoffman, E.

    2010-01-01

    TYPE I and II (ASTM 285-B) - Experienced stress corrosion cracking (SCC), 2 have been closed; 22 scheduled for closure by 2017, and No active leak sites today. TYPE III (ASTM A516-70 and A537 Class I) - Post-fabrication relief of weld residual stresses, Improved resistance to SCC and brittle fracture, No leakage history, and Receives new waste. The objectives are to utilize statistical methods to reduce conservatism in current chemistry control program; and express nitrite inhibitor limits in terms of pitting risk on waste tank steel. Conclusions are: (1) A statistically designed experimental study has been undertaken to improve the effectiveness of the minimum nitrite concentrations to inhibit pitting corrosion; (2) Mixture/amount model supports that pitting depends on the ratio of aggressive to inhibitive anions, as well as the concentration of each species; (3) Secondary aggressive species, Cl - and SO 4 2- , significantly effect the corrosion response; and (4) Results support the reduction of the chemistry control nitrite inhibitor concentrations in the regime of 0.8-1.0 M nitrate.

  11. Uniform Corrosion and General Dissolution of Aluminum Alloys 2024-T3, 6061-T6, and 7075-T6

    Science.gov (United States)

    Huang, I.-Wen

    Uniform corrosion and general dissolution of aluminum alloys was not as well-studied in the past, although it was known for causing significant amount of weight loss. This work comprises four chapters to understand uniform corrosion of aluminum alloys 2024-T3, 6061-T6, and 7075-T6. A preliminary weight loss experiment was performed for distinguishing corrosion induced weight loss attributed to uniform corrosion and pitting corrosion. The result suggested that uniform corrosion generated a greater mass loss than pitting corrosion. First, to understand uniform corrosion mechanism and kinetics in different environments, a series of static immersion tests in NaCl solutions were performed to provide quantitative measurement of uniform corrosion. Thereafter, uniform corrosion development as a function of temperature, pH, Cl-, and time was investigated to understand the influence of environmental factors. Faster uniform corrosion rate has been found at lower temperature (20 and 40°C) than at higher temperature (60 and 80°C) due to accelerated corrosion product formation at high temperatures inhibiting corrosion reactions. Electrochemical tests including along with scanning electron microscopy (SEM) were utilized to study the temperature effect. Second, in order to further understand the uniform corrosion influence on pit growth kinetics, a long term exposures for 180 days in both immersion and ASTM-B117 test were performed. Uniform corrosion induced surface recession was found to have limited impact on pit geometry regardless of exposure methods. It was also found that the competition for limited cathodic current from uniform corrosion the primary rate limiting factor for pit growth. Very large pits were found after uniform corrosion growth reached a plateau due to corrosion product coverage. Also, optical microscopy and focused ion beam (FIB) imaging has provided more insights of distinctive pitting geometry and subsurface damages found from immersion samples and B117

  12. Scanning reference electrode techniques in localized corrosion

    International Nuclear Information System (INIS)

    Isaacs, H.S.; Vyas, B.

    1979-04-01

    The principles, advantages, and implementations of scanning reference electrode techniques are reviewed. Data related to pitting, intergranular corrosion, welds and stress corrosion cracking are presented. The technique locates the position of localized corrosion and can be used to monitor the development of corrosion and changes in the corrosion rate under a wide range of conditions

  13. Microstructural evolution and pitting resistance of annealed lean duplex stainless steel UNS S32304

    International Nuclear Information System (INIS)

    Zhang Ziying; Han Dong; Jiang Yiming; Shi Chong; Li Jin

    2012-01-01

    Highlights: ► The relationship between pitting corrosion resistance and annealing temperature for UNS S32304 was systemically studied. ► The specimens annealed at 1080 °C for 1 h, quenched in water exhibit the best pitting corrosion resistance. ► The relationship between microstructural evolution and pitting resistance of annealed UNS S32304 was discussed in detail. ► The pitting corrosion resistance is consistent with pitting resistance equivalent number of weaker phase for UNS S32304 alloy. - Abstract: The effect of annealing temperature in the range from 1000 to 1200 °C on the pitting corrosion behavior of duplex stainless steel UNS S32304 was investigated by the potentiodynamic polarization and potentiostatic critical pitting temperature techniques. The microstructural evolution and pit morphologies were studied using a scanning electron microscopy with energy dispersive X-ray spectroscopy. The results demonstrated that the nucleation of metastable pits transformed from austenite phase to ferrite phase with the increasing annealing temperature. As the annealing temperature increased, the pitting corrosion resistance firstly increased and then decreased. The highest pitting corrosion resistance was obtained at 1080 °C with the highest critical pitting temperature value and pitting nucleation resistance. The results could be well explained by the microstructural evolution of ferrite and austenite phases induced by annealing treatment.

  14. Study of Temperature Effect on the Corrosion Inhibition of C38 Carbon Steel Using Amino-tris(Methylenephosphonic Acid in Hydrochloric Acid Solution

    Directory of Open Access Journals (Sweden)

    Najoua Labjar

    2011-01-01

    Full Text Available Tafel polarization method was used to assess the corrosion inhibitive and adsorption behaviours of amino-tris(methylenephosphonic acid (ATMP for C38 carbon steel in 1 M HCl solution in the temperature range from 30 to 60∘C. It was shown that the corrosion inhibition efficiency was found to increase with increase in ATMP concentration but decreased with temperature, which is suggestive of physical adsorption mechanism. The adsorption of the ATMP onto the C38 steel surface was found to follow Langmuir adsorption isotherm model. The corrosion inhibition mechanism was further corroborated by the values of kinetic and thermodynamic parameters obtained from the experimental data.

  15. Impact of saline aquifer water on surface and shallow pit corrosion of martensitic stainless steels during exposure to CO2 environment (CCS)

    Science.gov (United States)

    Pfennig, Anja; Kranzmann, Axel

    2018-05-01

    Pipe steels suitable for carbon capture and storage technology (CCS) require resistance against the corrosive environment of a potential CCS-site, e.g. heat, pressure, salinity of the aquifer, CO2-partial pressure. Samples of different mild and high alloyed stainless injection-pipe steels partially heat treated: 42CrMo4, X20Cr13, X46Cr13, X35CrMo4 as well as X5CrNiCuNb16-4 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CO2-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. Main corrosion products are FeCO3 and FeOOH. Corrosion rates obtained at 100 bar are generally much lower than those measured at ambient pressure. Highest surface corrosion rates are 0.8 mm/year for 42CrMo4 and lowest 0.01 mm/year for X5CrNiCuNb16-4 in the vapour phase at ambient pressure. At 100 bar the highest corrosion rates are 0.01 mm/year for 42CrMo4, X20Cr13 (liquid phase), X46Cr13 and less than 0.01 mm/year for X35CrMo4 and X5CrNiCuNb16-4 after 8000 h of exposure with no regard to atmosphere. Martensitic microstructure offers good corrosion resistance.

  16. Corrosion inhibition of carbon steel in acidic medium by orange peel extract and its main antioxidant compounds

    International Nuclear Information System (INIS)

    M’hiri, Nouha; Veys-Renaux, Delphine; Rocca, Emmanuel; Ioannou, Irina; Boudhrioua, Nourhéne Mihoubi; Ghoul, Mohamed

    2016-01-01

    Highlights: • Catechol and derived functions are responsible for flavonoids antioxidant activity. • Antioxidant activity of adsorbed molecules explains cathodic inhibition. • Orange peel extract inhibition is enhanced by the precipitation of a covering film. - Abstract: Chemical compounds of orange peel extracts were identified and their antioxidant activities were determined. The inhibiting effect on acidic steel corrosion brought by the extract and selected antioxidant compounds (neohesperidin, naringin, ascorbic acid) was evaluated separately by electrochemical methods. Whatever the extract concentration, a significant inhibition is observed, whereas selected antioxidant compounds show only a slight effect. Both electrochemical impedance spectroscopy results and scanning electron microscopy observations after immersion reveal that the inhibiting efficiency of orange peel extract is not only due to the antioxidant activity of its compounds but also to the precipitation of a surface film.

  17. Vapor Space Corrosion Testing Simulating The Environment Of Hanford Double Shell Tanks

    Energy Technology Data Exchange (ETDEWEB)

    Wiersma, B. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL); Gray, J. R. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL); Garcia-Diaz, B. L. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL); Murphy, T. H. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL); Hicks, K. R. [Savannah River Site (SRS), Aiken, SC (United States). Savannah River National Lab. (SRNL)

    2014-01-30

    As part of an integrated program to better understand corrosion in the high level waste tanks, Hanford has been investigating corrosion at the liquid/air interface (LAI) and at higher areas in the tank vapor space. This current research evaluated localized corrosion in the vapor space over Hanford double shell tank simulants to assess the impact of ammonia and new minimum nitrite concentration limits, which are part of the broader corrosion chemistry limits. The findings from this study showed that the presence of ammonia gas (550 ppm) in the vapor space is sufficient to reduce corrosion over the short-term (i.e. four months) for a Hanford waste chemistry (SY102 High Nitrate). These findings are in agreement with previous studies at both Hanford and SRS which showed ammonia gas in the vapor space to be inhibitive. The presence of ammonia in electrochemical test solution, however, was insufficient to inhibit against pitting corrosion. The effect of the ammonia appears to be a function of the waste chemistry and may have more significant effects in waste with low nitrite concentrations. Since high levels of ammonia were found beneficial in previous studies, additional testing is recommended to assess the necessary minimum concentration for protection of carbon steel. The new minimum R value of 0.15 was found to be insufficient to prevent pitting corrosion in the vapor space. The pitting that occurred, however, did not progress over the four-month test. Pits appeared to stop growing, which would indicate that pitting might not progress through wall.

  18. Enhancing pitting corrosion resistance of Al{sub x}CrFe{sub 1.5}MnNi{sub 0.5} high-entropy alloys by anodic treatment in sulfuric acid

    Energy Technology Data Exchange (ETDEWEB)

    Lee, C.P.; Chen, Y.Y.; Hsu, C.Y.; Yeh, J.W. [Department of Materials Science and Engineering, National Tsing Hua University, Hsinchu 300, Taiwan (China); Shih, H.C. [Department of Materials Science and Engineering, National Tsing Hua University, Hsinchu 300, Taiwan (China); Institute of Materials Science and Nanotechnology, Chinese Culture University, Taipei 111, Taiwan (China)], E-mail: hcshih@mx.nthu.edu.tw

    2008-12-01

    High-entropy alloys are a newly developed family of multi-component alloys that comprise various major alloying elements. Each element in the alloy system is present in between 5 and 35 at.%. The crystal structures and physical properties of high-entropy alloys differ completely from those of conventional alloys. The electrochemical impedance spectra (EIS) of the Al{sub x}CrFe{sub 1.5}MnNi{sub 0.5} (x = 0, 0.3, 0.5) alloys, obtained in 0.1 M HCl solution, clearly revealed that the corrosion resistance values were determined to increase from 21 to 34 {omega}cm{sup 2} as the aluminum content increased from 0 to 0.5 mol, and were markedly lower than that of 304 stainless steel (243 {omega}cm{sup 2}). At passive potential, the corresponding current declined with the anodizing time accounting, causing passivity by the growth of the multi-component anodized film in H{sub 2}SO{sub 4} solution. X-ray photoelectron spectroscopy (XPS) analyses revealed that the surface of anodized Al{sub 0.3}CrFe{sub 1.5}MnNi{sub 0.5} alloy formed aluminum and chromium oxide film which was the main passivating compound on the alloy. This anodic treatment increased the corrosion resistance in the EIS measurements of the CrFe{sub 1.5}MnNi{sub 0.5} and Al{sub 0.3}CrFe{sub 1.5}MnNi{sub 0.5} alloys by two orders of magnitude. Accordingly, the anodic treatment of the Al{sub x}CrFe{sub 1.5}MnNi{sub 0.5} alloys optimized their surface structures and minimized their susceptibility to pitting corrosion.

  19. On the inhibition of mild steel corrosion by 4-amino-5-phenyl-4H-1, 2, 4-trizole-3-thiol

    International Nuclear Information System (INIS)

    Musa, Ahmed Y.; Kadhum, Abdul Amir H.; Mohamad, Abu Bakar; Takriff, Mohd Sobri; Daud, Abdul Razak; Kamarudin, Siti Kartom

    2010-01-01

    The corrosion inhibition of mild steel in a 2.5 M H 2 SO 4 solution by 4-amino-5-phenyl-4H-1, 2, 4-trizole-3-thiol (APTT) was studied at different temperatures, utilising open circuit potential, potentiodynamic and impedance measurements. The results indicate that APTT performed as an excellent mixed-type inhibitor for mild steel corrosion in a 2.5 M H 2 SO 4 solution and that the inhibition efficiencies increased with the inhibitor concentration but decreased proportionally with temperature. The kinetic and thermodynamic parameters for adsorption of APTT on the mild steel surface were calculated. A chemisorption mechanism of APTT molecules on the mild steel surface was proposed based on the thermodynamic adsorption parameters.

  20. Biosynthesis of silver nanoparticles using Sida acuta extract for antimicrobial actions and corrosion inhibition potential.

    Science.gov (United States)

    Idrees, Muhammad; Batool, Saima; Kalsoom, Tanzila; Raina, Sadaf; Sharif, Hafiz Muhammad Adeel; Yasmeen, Summera

    2018-02-12

    Nanotechnology exhibits a multidisciplinary area and gained interests for researchers. Nanoparticles produced via physical and chemical methods affects ecosystem drastically. Green synthesis is the charming technique that is inexpensive and safe for the environment. This study aimed to explore the antibacterial actions of as-synthesized silver nanoparticles (Ag-NPs) against Escherichia coli, Staphylococcus aureus and Streptococcus faecalis. Also, the anti-corrosion actions confirmed that the Ag-NPs proved as good inhibitors. In this way, Ag-NPs were prepared via biosynthesis technique by consuming the ground leaves and stem of 'Sida acuta' as a capping agent. The Ag-NPs were formed by irradiation of the aqueous solution of silver nitrate (AgNO 3 ) with extract of S. acuta stem and leaves. The as-synthesized reaction mixture of Ag-NPs was found to exhibit an absorbance band at 446-447 nm, by an UV/VIS spectrophotometer, which is a characteristic of Ag-NPs due to the surface plasmon resonance absorption band. The X-ray diffraction and transmission electron microscopy (TEM) were used for the confirmation of Ag-NPs' variety dimension, morphology and dispersion. The infrared spectra confirmed the bio-fabrication of the Ag-NPs displayed the existence of conceivable functional groups responsible for the bio-reduction and capping. The antimicrobial actions were measured and the zone of inhibition was compared with standard antibiotics.

  1. Superhydrophobic and superoleophobic surface by electrodeposition on magnesium alloy substrate: Wettability and corrosion inhibition.

    Science.gov (United States)

    Liu, Yan; Li, Shuyi; Wang, Yaming; Wang, Huiyuan; Gao, Ke; Han, Zhiwu; Ren, Luquan

    2016-09-15

    Superamphiphobic (both superhydrophobic and superoleophobic) surfaces have attracted great interests in the fundamental research and practical application. This research successfully fabricated the superamphiphobic surfaces by combining the nickel plating process and modification with perfluorocaprylic acid. The cooperation of hierarchical micro-nano structures and perfluorocaprylic acid with low surface energy plays an important role in the formation of superamphiphobic surfaces. The contact angles of water/oil have reached up to 160.2±1°/152.4±1°, respectively. Contrast with bare substrate, the electrochemical measurements of superamphiphobic surfaces, not only the EIS measurement, but also potentiodynamic polarization curves, all revealed that, the surface corrosion inhibition was improved significantly. Moreover, superamphiphobic surfaces exhibited superior stability in the solutions with a large pH range, also could maintain excellent performance after storing for a long time in the air. This method is easy, feasible and effective, and could be used to fabricate large-area mutli-functional surface. Such a technique will develop a new approach to fabricate superamphiphobic surfaces on different engineering materials. Copyright © 2016 Elsevier Inc. All rights reserved.

  2. Inhibitive Effect of Butyltin Trichloride on Dissolution and Localized Corrosion of Aluminium in Sodium Hydroxide and Hydrochloric Acid

    OpenAIRE

    Mourad, M.Y.; Ibrahim, E.H.; Seliman, S.A.

    1990-01-01

    The dissolution of aluminium in sodium hydroxide and hydrochloric acid in the presence of butyltin trichloride as corrosion inhibitor has been studied by hydrogen evolution and thermometric methods. Experimental findings indicate that the inhibition effect of butyltin trichloride takes place through an adsorption mechanism following the Frumkin's isotherm. Butyltin trichloride acts as a weakly adsorbed inhibitor in NaOH and as a strongly adsorbed inhibitor in hydrochloric acid medium. Wile...

  3. Evaluation of Corrosion Inhibition of Mild Steel in 1 M Hydrochloric Acid Solution by Mollugo cerviana

    Directory of Open Access Journals (Sweden)

    P. Arockiasamy

    2014-01-01

    Full Text Available The inhibiting effect of methanolic extract of Mollugo cerviana plant on the corrosion of mild steel in 1 M HCl solution has been investigated by different techniques like potentiodynamic polarization, electrochemical impedance spectroscopy, and weight loss methods for five different concentrations of plant extract ranging from 25 to 1000 mg/L. The results indicated that the corrosion inhibition efficiency increased on increasing plant extract concentration till 500 mg/L and decreased on further increasing concentration. The extract was a mixed type inhibitor with the optimum inhibition concentration of 500 mg/L in potentiodynamic polarization. The adsorption of the plant extract on the mild steel surface was found to obey Langmuir adsorption isotherm. Surface analysis was also carried out to find out the surface morphology of the mild steel in the presence and in the absence of the inhibitor to find out its efficiency. The obtained results showed that the Mollugo cerviana extract acts as a good inhibitor for the corrosion of mild steel in 1 M HCl solution.

  4. Corrosion of PWR steam generators

    International Nuclear Information System (INIS)

    Garnsey, R.

    1979-01-01

    Some designs of pressurized water reactor (PWR) steam generators have experienced a variety of corrosion problems which include stress corrosion cracking, tube thinning, pitting, fatigue, erosion-corrosion and support plate corrosion resulting in 'denting'. Large international research programmes have been mounted to investigate the phenomena. The operational experience is reviewed and mechanisms which have been proposed to explain the corrosion damage are presented. The implications for design development and for boiler and feedwater control are discussed. (author)

  5. Synergistic Effect of Azadirachta Indica Extract and Iodide Ions on the Corrosion Inhibition of Aluminium in Acid Media

    Energy Technology Data Exchange (ETDEWEB)

    Arab, S. T.; Al- Turkustani, A. M.; Al- Dhahiri, R. H. [King Abd El- Aziz University, Jeddah (Saudi Arabia)

    2008-06-15

    The synergistic action caused by iodide ions on the corrosion inhibition of aluminium (Al) in 0.5 M HCl in the presence of Azadirachta Indica (AZI) plant extract has been investigated using potintiodynamic polarization and impedance techniques. It is found that AZI extract inhibits the corrosion of aluminium in 0.5 M HCl. The inhibition efficiency increases with the increase in AZI extract concentration, until 24% v/v of AZI extract, then Inh.% is decreased with father increase in AZI extract concentration. The adsorption of this extract in the studied concentration is found to obey Frewendlish adsorption isotherm. The addition of iodide ions enhances the inhibition efficiency to a considerable extent. The increase in Inh.% values in presence of fixed concentration of iodide ions indicates that AZI extract forms an insoluble complex at lower AZI extract concentrations by undergoing a joint adsorption. But at higher concentrations of AZI extract, competitive adsorption is found between iodide ions and the formed complex leading to less Inh.%. The Inh.% decreased in presence of iodide ions with AZI extract than in presence of AZI extract alone at all studied iodide concentrations. The synergism parameter S {sub θ} is defined and calculated from surface coverage values. This parameter in the case of AZI extract is found to be more than unity, indicating that the enhanced inhibition efficiency caused by the addition of iodide ions.

  6. Inhibition of mild steel corrosion in acidic medium using synthetic and naturally occurring polymers and synergistic halide additives

    Energy Technology Data Exchange (ETDEWEB)

    Umoren, S.A. [Department of Chemistry, Faculty of Science, University of Uyo, P.M.B 1017 Uyo (Nigeria)], E-mail: saviourumoren@yahoo.com; Ogbobe, O.; Igwe, I.O. [Department of Polymer and Textile Engineering, School of Engineering and Engineering Technology, Federal University of Technology, P.M.B. 1526 Owerri (Nigeria); Ebenso, E.E. [Department of Chemistry and Chemical Technology, National University of Lesotho, P. O. Roma180, Lesotho (South Africa)

    2008-07-15

    The corrosion inhibition of mild steel in H{sub 2}SO{sub 4} in the presence of gum arabic (GA) (naturally occurring polymer) and polyethylene glycol (PEG) (synthetic polymer) was studied using weight loss, hydrogen evolution and thermometric methods at 30-60 deg. C. PEG was found to be a better inhibitor for mild steel corrosion in acidic medium than GA. The effect of addition of halides (KCl, KBr and KI) was also studied. Results obtained showed that inhibition efficiency (I%) increased with increase in GA and PEG concentration, addition of halides and with increase in temperature. Increase in inhibition efficiency (I%) and degree of surface coverage ({theta}) was found to follow the trend Cl{sup -} < Br{sup -} < I{sup -} which indicates that the radii and electronegativity of the halide ions play a significant role in the adsorption process. GA and PEG alone and in combination with halides were found to obey Temkin adsorption isotherm. Phenomenon of chemical adsorption is proposed from the trend of inhibition efficiency with temperature and values {delta}G{sub ads}{sup 0} obtained. The synergism parameter, S{sub I} evaluated is found to be greater than unity indicating that the enhanced inhibition efficiency caused by the addition of halides is only due to synergism.

  7. Synergistic effect of halide ions on the corrosion inhibition of aluminium in H2SO4 using 2-acetylphenothiazine

    International Nuclear Information System (INIS)

    Ebenso, E.E.

    2003-01-01

    The corrosion inhibition of aluminium in H 2 SO 4 in the presence of 2-acetylphenothiazine (2APTZ) at temperature range of 30-60 deg. C was studied using the weight loss and thermometric techniques. The effect of addition of halides (KCl, KBr, KI) is also reported. The inhibition efficiency (I, %) increased with increase in concentration of 2APTZ. The addition of the halides increased the inhibition efficiency to a considerable extent. The temperature increased the corrosion rate and inhibition efficiency in the range 30-60 deg. C in the absence and presence of the inhibitor and halides. Phenomenon of chemical adsorption is proposed. Flory-Huggins adsorption isotherm equation was obeyed at all the concentrations studied. The decrease in inhibition efficiency (and surface coverage values) was found to be in the order I - >Br - >Cl - which clearly indicates that the radii and the electronegativity of halides play a significant role in the adsorption process. All the data acquired reveal that 2APTZ acts as an inhibitor in the acid environment from the two techniques used. The synergistic effect of 2APTZ and halide ions is discussed

  8. Optic Nerve Pit

    Science.gov (United States)

    ... Conditions Frequently Asked Questions Español Condiciones Chinese Conditions Optic Nerve Pit What is optic nerve pit? An optic nerve pit is a ... may be seen in both eyes. How is optic pit diagnosed? If the pit is not affecting ...

  9. Corrosion Inhibition on SAE 1010 Steel by Nanoscale Exopolysaccharides Coatings Determined by Electrochemical and Surface Characterization

    Science.gov (United States)

    Plating, painting and the application of enamel are the most common anti-corrosion treatments. They are effective by providing a barrier of corrosion resistant material between the damaging environment and the structural material. Coatings start failing rapidly if scratched or damaged because a co...

  10. Inhibition of pH fronts in corrosion cells due to the formation of cerium hydroxide

    NARCIS (Netherlands)

    Soestbergen, M. van; Erich, S.J.F.; Huinink, H.P.; Adan, O.C.G.

    2013-01-01

    The effect of cerium-based corrosion inhibitors on the pH front between the alkaline cathode and acidic anode in corrosion cells has been studied. The cerium component of these inhibitors can affect the pH front since it precipitates in an alkaline environment as cerium hydroxide, which is important

  11. Some observations about the Incoloy 800 corrosion

    International Nuclear Information System (INIS)

    Baptista, W.; Sathler, L.; Mattos, O.R.

    1985-01-01

    The chemical and electrochemical characteristics of synthetic solutions similar to those inside the occluded cell corrosion - OCC (pitting, cracks from stress corrosion) of incoloy 800, 25 0 C are studied. (E.G.) [pt

  12. Pit formation on stainless steel surfaces pre-treated with biosurfactants produced by Pseudomonas fluorescens

    International Nuclear Information System (INIS)

    Dagbert, Catherine; Meylheuc, Thierry; Bellon-Fontaine, Marie-Noelle

    2008-01-01

    Today, it is widely established that the surface tension of water can be reduced by some microorganisms capable of synthesizing surface-active compounds called biosurfactants (BS). BS characteristics depend on the microorganism that produces them and therefore, on the microorganism culture conditions. Some studies on chemical surfactants have shown that the adsorption of surface-active compounds plays a major role in corrosion; indeed they are used as a good corrosion inhibition tool. The purpose of this study was first, to estimate the importance and behavior of the stainless steels passive film on the adsorption of BS, produced by the Gram negative bacteria Pseudomonas fluorescens, and secondly, to study the impact of these treatments on the pitting corrosion. In this paper, the galvanostatic polarization technique, used as accelerated method for determining the characteristic pit potentials on stainless steels, is examined. Pit growth, shape and cover formation were also observed. The surface topography of the corroded specimens was investigated using field emission scanning electron microscopy (FESEM)

  13. Pit formation on stainless steel surfaces pre-treated with biosurfactants produced by Pseudomonas fluorescens

    Energy Technology Data Exchange (ETDEWEB)

    Dagbert, Catherine [ECP-LGPM, Grande Voie des Vignes, 92295 Chatenay-Malabry (France)], E-mail: catherine.dagbert@ecp.fr; Meylheuc, Thierry; Bellon-Fontaine, Marie-Noelle [INRA, UMR 763 Bioadhesion et Hygiene des Materiaux, F-91300 Massy (France); AGROPARISTECH, UMR 763 Bioadhesion et Hygiene des Materiaux, F-91300 Massy (France)

    2008-12-01

    Today, it is widely established that the surface tension of water can be reduced by some microorganisms capable of synthesizing surface-active compounds called biosurfactants (BS). BS characteristics depend on the microorganism that produces them and therefore, on the microorganism culture conditions. Some studies on chemical surfactants have shown that the adsorption of surface-active compounds plays a major role in corrosion; indeed they are used as a good corrosion inhibition tool. The purpose of this study was first, to estimate the importance and behavior of the stainless steels passive film on the adsorption of BS, produced by the Gram negative bacteria Pseudomonas fluorescens, and secondly, to study the impact of these treatments on the pitting corrosion. In this paper, the galvanostatic polarization technique, used as accelerated method for determining the characteristic pit potentials on stainless steels, is examined. Pit growth, shape and cover formation were also observed. The surface topography of the corroded specimens was investigated using field emission scanning electron microscopy (FESEM)

  14. Kinetics of corrosion inhibition of aluminum in acidic media by water-soluble natural polymeric chondroitin-4-sulfate as anionic polyelectrolyte inhibitor.

    Science.gov (United States)

    Hassan, Refat M; Ibrahim, Samia M; Takagi, Hideo D; Sayed, Suzan A

    2018-07-15

    Corrosion inhibition of aluminum (Al) in hydrochloric acid by anionic polyelectrolyte chondroitin-4-sulfate (CS) polysaccharide has been studied using both gasometrical and weight-loss techniques. The results drawn from these two techniques are comparable and exhibit negligible differences. The inhibition efficiency was found to increase with increasing the inhibitor concentration and decreased with increasing temperature. The inhibition action of CS on Al metal surface was found to obey both of Langmuir and Freundlich isotherms. The factors affecting the corrosion rates such as the concentration and geometrical structure of the inhibitor, concentration of the corrosive medium, and the temperature were examined. The kinetic parameters were evaluated and a suitable corrosion mechanism consistent with the results obtained is discussed. Copyright © 2018. Published by Elsevier Ltd.

  15. Inhibitive effect of N,N'-Dimethylaminoethanol on carbon steel corrosion in neutral sodium chloride solution, at different temperatures

    Directory of Open Access Journals (Sweden)

    Hassoune Mohammed

    2018-01-01

    Full Text Available The inhibition of carbon steel corrosion in neutral sodium chloride solution by N,N'- Dimethylaminoethanol (DMEA, at different temperatures, was investigated using weight loss, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS techniques. The results obtained confirm that DMEA is a good organic corrosion inhibitor for carbon steel in 0.5M of NaCl (concentration encountered in the Mediterranean seawater, over the whole range of temperatures studied. The inhibition efficiency (IE% increases with increasing DMEA concentration; it reaches highest value for a concentration around 0.125 mol.L-1. Potentiodynamic polarization data show that, the compound studied in this research predominantly act as anodic-type inhibitor. The EIS study reveals that the addition of DMEA decreases the corrosion rate of carbon steel in neutral sodium chloride solution, due to the fact that the inhibitor molecules are strongly adsorbed on the active sites following Langmuir isotherm, thus leading to the formation of a stable protective film on the steel surface which is able to keep the metal/solution interface in a passive state. Furthermore, the values of the activation parameters, i.e. ΔHa and Ea obtained in this study indicate that the adsorption process of DMEA is endothermic and could be mainly attributed to chemisorption, respectively.

  16. Synergistic Effect of L-Methionine and KI on Copper Corrosion Inhibition in HNO3 (1M

    Directory of Open Access Journals (Sweden)

    Amel SEDIK

    2014-05-01

    Full Text Available L-Methionine (L-Met efficiency as a non-toxic corrosion inhibitor for copper in 1M HNO3 has been studied by using electrochemical impedance spectroscopy (EIS and potentiodynamic polarization. Copper corrosion rate significant decrease was observed in the presence of L-Met at 10-4M. The Obtained Results from potentiodynamic polarization and impedance measurements are in good agreement. L-Methionine adsorption on copper surface follows Langmuir isotherm. L-Met free energy adsorption on copper (-30 KJ mol-1 reveals an inhibition strong physical adsorption on copper surface. In order to evaluate the L-Met effect, L-Met and iodide ion’synergistic effect was used to prevent copper corrosion in nitric acid. It was found that inhibitor efficiency (IE reached 98.27 % in 1M solution containing 10-4M L-Met and 10- 3 M KI. The synergistic effect was attributed to iodide ions adsorption on copper surface, which facilitated the L-Met adsorption and an inhibitive film formation.

  17. A comparative study of the corrosion inhibition of mild steel in sulphuric acid by 4,4-dimethyloxazolidine-2-thione

    International Nuclear Information System (INIS)

    Musa, Ahmed Y.; Kadhum, Abdul Amir H.; Mohamad, Abu Bakar; Daud, Abdul Razak; Takriff, Mohd Sobri; Kamarudin, Siti Kartom

    2009-01-01

    The corrosion protection of mild steel in a 2.5 M H 2 SO 4 solution by 4,4-dimethyloxazolidine-2-thione (DMT) was studied at different temperatures by measuring changes in open circuit potential (OCP), potentiodynamic polarisation and electrochemical impedance spectroscopy (EIS). Corrosion current densities calculated from EIS data were comparable to those obtained from polarisation measurements. Results showed that DMT inhibited mild steel corrosion in a 2.5 M H 2 SO 4 solution and indicated that the inhibition efficiencies increased with the concentration of inhibitor, but decreased proportionally with temperature. Polarisation curves showed that DMT is a mixed-type inhibitor. Changes in impedance parameters suggested the adsorption of DMT on the mild steel surface, leading to the formation of protective films. The DMT adsorption on the mild steel surface followed the Langmuir adsorption isotherm. The kinetic and thermodynamic parameters for dissolution and adsorption were investigated. Comprehensive adsorption (physisorption and chemisorption) of the inhibitor molecules on the mild steel surface was suggested based on the thermodynamic adsorption parameters.

  18. The Synergistic Effect of Iodide and Sodium Nitrite on the Corrosion Inhibition of Mild Steel in Bicarbonate–Chloride Solution

    Directory of Open Access Journals (Sweden)

    Gaius Debi Eyu

    2016-10-01

    Full Text Available The effect of potassium iodide (KI and sodium nitrite (NaNO2 inhibitor on the corrosion inhibition of mild steel in chloride bicarbonate solution has been studied using electrochemical techniques. Potentiodynamic polarisation data suggest that, when used in combination, KI and NaNO2 function together to inhibit reactions at both the anode and the cathode, but predominantly anodic. KI/NO2− concentration ratios varied from 2:1 to 2:5; inhibition efficiency was optimized for a ratio of 1:1. The surface morphology and corrosion products were analysed using scanning electron microscopy (SEM and X-ray diffractometry (XRD. The latter shows that the addition of I− to NO2 facilitates the formation of a passivating oxide (γ-Fe2O3 as compared to NO2− alone, decreasing the rate of metal dissolution observed in electrochemical testing. The synergistic effect of KI/NO2− inhibition was enhanced under the dynamic conditions associated with testing in a rotating disc electrode.

  19. Understanding the corrosion inhibition of carbon steel and copper in sulphuric acid medium by amino acids using electrochemical techniques allied to molecular modelling methods

    International Nuclear Information System (INIS)

    Mendonça, Glaydson L.F.; Costa, Stefane N.; Freire, Valder N.; Casciano, Paulo N.S.; Correia, Adriana N.; Lima-Neto, Pedro de

    2017-01-01

    Highlights: • Corrosion inhibition of carbon steel and of copper by the amino acids was studied. • Inhibition efficiencies were experimentally achieved by electrochemical impedance. • DFT and Monte Carlo methods allowed correlating molecular properties with inhibition efficiency. • The corrosion inhibition followed the electron donation the electron-back donations process. - Abstract: Six amino acids were evaluated as corrosion inhibitors for carbon steel and copper in 0.5 mol L"−"1 H_2SO_4 solution by potentiodynamic polarization and electrochemical impedance techniques allied to Density Functional Theory (DFT) and Monte Carlo computations The corrosion inhibitor rankings were: Arg > Gln > Asn > Met > Cys > Ser, for copper, and Met > Cys > Ser > Arg > Gln > Asn, for carbon steel. The DFT approach failed to explain the corrosion inhibition rating based on the HOMO and LUMO energies of the isolated amino acid molecules, while the simpler classical Monte Carlo approach, performed considering the interaction energies between the corrosion inhibitor and the metallic substrate, was successful.

  20. Detection and spatial characterization of carbon steel pitting corrosion in anaerobic sulpho-genic medium; Detection et caracterisation spatiale de la corrosion localisee des aciers au carbone en milieu anaerobie sulfurogene

    Energy Technology Data Exchange (ETDEWEB)

    Festy, D.; Forest, B. [Institut francais de Recherche pour l' Exploitation de la Mer - IFREMER, Centre de Brest, Service Materiaux et Structures, 29 - Plouzane (France); Keddam, M.; Monfort Moros, N.; Tribollet, B. [UPR 15 du CNRS Lab. de Physique des Liquides et Electrochimie, 75 - Paris (France); Marchal, R.; Monfort Moros, N. [Institut Francais du Petrole (IFP), Div. Chimie et Physico-Chimie Appliquee, Dept. Microbiologie, 92 - Rueil-Malmaison (France)

    2002-07-01

    The bio-film developing on carbon steel surfaces in anaerobic condition may induce localised corrosion. To be able to better understand this type of bio-corrosion, this piper presents a new electrochemical technique, which has been developed in collaboration between IFREMER and the Laboratory for liquid physic and electrochemistry. Focussed on local aspect of this phenomenon, the described technique enables surface torrent density mapping to be performed and anodic or cathodic zones to be identified. A double micro-electrode probe is placed closed to the steel simple surface and potential difference between them is measured. This value is directly connected to ohmic drop within electrolyte and consequently, to local torrent. By scanning the substrate surface, local torrent repartition is visualized and one tan detect and characterise Localised corrosion attacks. After presenting the technique and the calibration procedure, a bio-corrosion phenomenon induced by stripping a bio-film at a carbon steel simple surface is analysed by successively drawing localised torrent maps, included biocide efficiency assessment. (authors)

  1. Corrosion inhibition of Armco iron by 2-mercaptobenzimidazole in sodium chloride 3% media

    International Nuclear Information System (INIS)

    Amar, H.; Tounsi, A.; Makayssi, A.; Derja, A.; Benzakour, J.; Outzourhit, A.

    2007-01-01

    The effect of 2-mercaptobenzimidazole (2MBI) on the corrosion of Armco iron in NaCl media has been investigated in relation to the concentration of the inhibitor by various corrosion monitoring techniques. Surface morphology was studied by scanning electron microscopy (SEM). Results obtained revealed that 2MBI is a good anodic inhibitor. The addition of increasing concentrations of 2MBI moves the corrosion potential towards positive values and reduces the corrosion rate. EIS results show that the changes in the impedance parameters (R t and C dl ) with concentrations of 2MBI is indicative of the adsorption of these molecules leading to the formation of a protective layer on iron surface. The adsorption of this compound is also found to obey Langmuir's adsorption isotherm in NaCl

  2. Design of nanocoatings by in situ phosphatizing reagent catalyzed polysilsesquioxane for corrosion inhibition and adhesion promotion on metal alloys

    Science.gov (United States)

    Henderson, Kimberly B.

    When a metal reacts with oxygen and water, a redox reaction happens, which will cause corrosion. Current surface pretreatment for inhibiting corrosion on metal alloys is a phosphate conversion bath. The phosphate conversion bath will generate a phosphate-chromate layer to adhere strongly to a metal substrate. However, it is toxic and unfriendly to the environment. Our group proposed an innovative coating that contains a phosphate component (ISPR-In-situ Phosphatizing Reagent) within a protective coating. The ISPR coating will form a bound phosphate layer on the metal surface acting as the corrosion barrier and enhancing adhesion into the metal surface; moreover, it is low in cost and non-toxic. Within this dissertation, there are four projects that investigate design of ISPR nanocoatings for the use of corrosion inhibition and adhesion promotion. Surface modification and adjusting concentrations of materials with the different formulations are explored. The first project focuses on the adhesion enhancement of a coating created by modifying the surface of an aluminum panel. Secondly, the next project will discuss and present the use of three rare earth element formulations as a replacement for phosphate conversion coatings on magnesium alloy, AZ61. The third project is the design of a nanocoating by using heat dissipating materials to fill in small vacant spaces in the ISPR network coating on various metal alloys. The last project, studies the strategic selection of incorporating metal components into ISPR network by the reduction potential values on several different alloys. Many methods of analysis are used; SEM, TEM, ASTM B117, ASTM D1308, ASTM D3359, EIS, and thickness probe. It was found that the addition of ISPR in the nanocoatings dramatically improves the vitality of metal alloys and these results will be presented during this dissertation.

  3. The synergistic inhibitive effect and some quantum chemical parameters of 2,3-diaminonaphthalene and iodide ions on the hydrochloric acid corrosion of aluminium

    International Nuclear Information System (INIS)

    Obot, I.B.; Obi-Egbedi, N.O.; Umoren, S.A.

    2009-01-01

    The effect of iodide ions on the inhibitive performance of 2,3-diaminonaphthalene (2,3-DAN) in 1 M HCl for aluminium corrosion has been studied using hydrogen evolution (gasometry) measurements at 30 and 40 deg. C. Results obtained showed that the presence of 2,3-DAN molecules in the corrosive medium (1 M HCl solution) inhibits the corrosion process of aluminium and as the concentration of 2,3-DAN increases the inhibition efficiency also increased at the studied temperatures. A synergistic effect was observed between KI and 2,3-DAN. The experimental results suggest that the presence of iodide ions in the solutions stabilized the adsorption of 2,3-DAN molecules on the metal surfaces and, therefore improve the inhibition efficiency of 2,3-DAN. Phenomenon of physical adsorption is proposed for the inhibition and the process followed the Freundlich adsorption isotherm. The activation energy (E a ), heat of adsorption (Q ads ) and free energy of adsorption for the corrosion process (ΔG ads ) have been evaluated at the different temperatures and the values support the results obtained. Some quantum chemical parameters and the Mulliken charge densities for 2,3-diaminonaphthalene were calculated by the AM1 Semi-empirical method to provide further insight into the mechanism of inhibition of the corrosion process

  4. Corrosion of pure magnesium under thin electrolyte layers

    International Nuclear Information System (INIS)

    Zhang Tao; Chen Chongmu; Shao Yawei; Meng Guozhe; Wang Fuhui; Li Xiaogang; Dong Chaofang

    2008-01-01

    The corrosion behavior of pure magnesium was investigated by means of cathodic polarization curve, electrochemical impedance spectroscopy (EIS) and electrochemical noise (EN) under aerated and deaerated thin electrolyte layers (TEL) with various thicknesses. Based on shot noise theory and stochastic theory, the EN results were quantitatively analyzed by using the Weibull and Gumbel distribution function, respectively. The results show that the cathodic process of pure magnesium under thin electrolyte layer was dominated by hydrogen reduction. With the decreasing of thin electrolyte layer thickness, cathodic process was retarded slightly while the anodic process was inhibited significantly, which indicated that both the cathodic and anodic process were inhibited in the presence of oxygen. The absence of oxygen decreased the corrosion resistance of pure magnesium in case of thin electrolyte layer. The corrosion was more localized under thin electrolyte layer than that in bulk solution. The results also demonstrate that there exist two kinds of effects for thin electrolyte layer on the corrosion behavior of pure magnesium: (1) the rate of pit initiation was evidently retarded compared to that in bulk solution; (2) the probability of pit growth oppositely increased. The corrosion model of pure magnesium under thin electrolyte layer was suggested in the paper

  5. Experimental and theoretical investigation on corrosion inhibition of AA5052 aluminium alloy by L-cysteine in alkaline solution

    International Nuclear Information System (INIS)

    Wang, Dapeng; Gao, Lixin; Zhang, Daquan; Yang, Dong; Wang, Hongxia; Lin, Tong

    2016-01-01

    The corrosion inhibition of L-cysteine on AA5052 aluminium alloy in 4 mol/L NaOH solution was investigated by hydrogen gas evolution experiment, polarisation curve, galvanostatic discharge, electrochemical impedance spectroscopy measurements and quantum chemical calculations. The adsorption of L-cysteine on aluminium alloy surface obeyed the amended Langmuir's adsorption isotherm. The polarisation curves indicated that L-cysteine acted as a cathodic inhibitor to inhibit cathodic reaction. The inhibition mechanism was dominated by the geometric covering effect. The galvanostatic discharge shows that the additives restrain the hydrogen evolution and increase the anodic utilization rate. Quantum chemical calculations indicated that L-cysteine molecules mainly interacted with on the carboxyl groups on the aluminium alloy surface. A strong hybridization occurred between the s-orbital and p-orbital of reactive sites in the L-cysteine molecule and the sp-orbital of Aluminium. - Highlights: • L-cysteine was used as corrosion inhibitor for Al alloy in alkaline solution. • Adsorption of L-cysteine on Al alloy surface obeyed the amended Langmuir's isotherm. • L-cysteine molecules interacted with the carboxyl groups on the Al alloy surface. • A strong orbital hybridization occurred between the reactive sites in L-cysteine and Al.

  6. Corrosion inhibition of iron in 0.5 mol L-1 H2SO4 by halide ions

    Directory of Open Access Journals (Sweden)

    Jeyaprabha C.

    2006-01-01

    Full Text Available The inhibition effect of halide ions such as iodide, bromide and chloride ions on the corrosion of iron in 0.5 mol L-1 H2SO4 and the adsorption behaviour of these ions on the electrode surface have been studied by polarization and impedance methods. It has been found that the inhibition of nearly 90% has been observed for iodide ions at 2.5 10-3 mol L-1, for bromide ions at 10 10-3 mol L-1 and 80% for chloride ions at 2.5 10-3 mol L-1. The inhibition effect is increased with increase of halide ions concentration in the case of I- and Br- ions, whereas it has decreased in the case of Cl- ion at concentrations higher than 5 10-3 mol L-1. The double layer capacitance values have decreased considerably in the presence of halide ions which indicate that these anions are adsorbed on iron at the corrosion potential.

  7. Experimental and theoretical investigation on corrosion inhibition of AA5052 aluminium alloy by L-cysteine in alkaline solution

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Dapeng; Gao, Lixin [School of Environmental and Chemical Engineering, Shanghai University of Electric Power, Shanghai 200090 (China); Zhang, Daquan, E-mail: zhangdaquan@shiep.edu.cn [School of Environmental and Chemical Engineering, Shanghai University of Electric Power, Shanghai 200090 (China); Yang, Dong [School of Environmental and Chemical Engineering, Shanghai University of Electric Power, Shanghai 200090 (China); Wang, Hongxia; Lin, Tong [Institute for Frontier Materials, Deakin University, Geelong, VIC 3216 (Australia)

    2016-02-01

    The corrosion inhibition of L-cysteine on AA5052 aluminium alloy in 4 mol/L NaOH solution was investigated by hydrogen gas evolution experiment, polarisation curve, galvanostatic discharge, electrochemical impedance spectroscopy measurements and quantum chemical calculations. The adsorption of L-cysteine on aluminium alloy surface obeyed the amended Langmuir's adsorption isotherm. The polarisation curves indicated that L-cysteine acted as a cathodic inhibitor to inhibit cathodic reaction. The inhibition mechanism was dominated by the geometric covering effect. The galvanostatic discharge shows that the additives restrain the hydrogen evolution and increase the anodic utilization rate. Quantum chemical calculations indicated that L-cysteine molecules mainly interacted with on the carboxyl groups on the aluminium alloy surface. A strong hybridization occurred between the s-orbital and p-orbital of reactive sites in the L-cysteine molecule and the sp-orbital of Aluminium. - Highlights: • L-cysteine was used as corrosion inhibitor for Al alloy in alkaline solution. • Adsorption of L-cysteine on Al alloy surface obeyed the amended Langmuir's isotherm. • L-cysteine molecules interacted with the carboxyl groups on the Al alloy surface. • A strong orbital hybridization occurred between the reactive sites in L-cysteine and Al.

  8. Corrosion inhibition of iota-carrageenan natural polymer on aluminum in presence of zwitterion mediator in HCl media

    International Nuclear Information System (INIS)

    Fares, Mohammad M.; Maayta, A.K.; Al-Mustafa, Jamil A.

    2012-01-01

    Highlights: ► Inhibition of Al by ι-carrageenan in the presence of zwitterion mediator was investigated. ► Considerable improvement in inhibition efficiency observed in the presence of zwitterion mediator. ► Coherent physical adsorption layer was evidenced by kinetic and thermodynamic parameters. ► Small but consistent fractured island layers observed after acid exposure as revealed by SEM images. - Abstract: ι-Carrageenan a natural polymer has been used as corrosion inhibitor of aluminum in presence of pefloxacin mesylate, acting as zwitterionic mediator, in acidic medium. Considerable improvement in inhibition efficiency occurred in the presence of the mediator. Activation energy of corrosion and other thermodynamic parameters such as standard free energy, standard enthalpy, and standard entropy of the adsorption process revealed better and well-ordered physical adsorption layers in presence of pefloxacin. Adsorption isotherms in absence or presence of pefloxacin mediator appropriately fit in the Langmuir isotherms. The scanning electron microscope (SEM) images demonstrated smooth, glossy, and relatively coherent adsorption layers of the inhibitor on the metal surface in aqueous solution. After the exposure to 2.0 M HCl for 2 h, a smaller but consistent regular shaped fractured layer is obtained.

  9. Launch Pad Coatings for Smart Corrosion Control

    Science.gov (United States)

    Calle, Luz M.; Hintze, Paul E.; Bucherl, Cori N.; Li, Wenyan; Buhrow, Jerry W.; Curran, Jerome P.; Whitten, Mary C.

    2010-01-01

    Corrosion is the degradation of a material as a result of its interaction with the environment. The environment at the KSC launch pads has been documented by ASM International (formerly American Society for Metals) as the most corrosive in the US. The 70 tons of highly corrosive hydrochloric acid that are generated by the solid rocket boosters during a launch exacerbate the corrosiveness of the environment at the pads. Numerous failures at the pads are caused by the pitting of stainless steels, rebar corrosion, and the degradation of concrete. Corrosion control of launch pad structures relies on the use of coatings selected from the qualified products list (QPL) of the NASA Standard 5008A for Protective Coating of Carbon Steel, Stainless Steel, and Aluminum on Launch Structures, Facilities, and Ground Support Equipment. This standard was developed to establish uniform engineering practices and methods and to ensure the inclusion of essential criteria in the coating of ground support equipment (GSE) and facilities used by or for NASA. This standard is applicable to GSE and facilities that support space vehicle or payload programs or projects and to critical facilities at all NASA locations worldwide. Environmental regulation changes have dramatically reduced the production, handling, use, and availability of conventional protective coatings for application to KSC launch structures and ground support equipment. Current attrition rate of qualified KSC coatings will drastically limit the number of commercial off the shelf (COTS) products available for the Constellation Program (CxP) ground operations (GO). CxP GO identified corrosion detection and control technologies as a critical, initial capability technology need for ground processing of Ares I and Ares V to meet Constellation Architecture Requirements Document (CARD) CxP 70000 operability requirements for reduced ground processing complexity, streamlined integrated testing, and operations phase affordability

  10. Investigation of adsorption and inhibitive effect of acid red GRE (183 dye on the corrosion of carbon steel in hydrochloric acid media

    Directory of Open Access Journals (Sweden)

    M. Abd El-raouf

    2015-09-01

    Full Text Available The adsorption and corrosion inhibitive effect of acid red GRE (183 dye on carbon steel alloy in 1 M HCl solutions was studied using various techniques. Results of weight loss, Tafel polarization measurements and electrochemical impedance spectroscopy (EIS techniques show that this compound has fairly good inhibiting properties for steel corrosion in acidic bath; with efficiency around 96% at a concentration of 50 ppm. The inhibition is of a mixed anodic–cathodic nature. Factors affecting the corrosion process have been calculated and discussed. Acid red GRE (183 dye was shown to be an inhibitor in the acidic corrosion. Inhibition efficiency increased with acid red GRE (183 dye concentration but decreased with rise in temperature, corrosion inhibition is attributed to the adsorption of acid red GRE (183 dye on the carbon steel surface via a physical adsorption mechanism. Langmuir isotherm is found to provide an accurate description of the adsorption behavior of the investigated azo compound. The nature of the protective film was investigated using SEM and EDX techniques.

  11. Corrosion/95 conference papers

    International Nuclear Information System (INIS)

    Anon.

    1995-01-01

    The papers in this conference represent the latest technological advances in corrosion control and prevention. The following subject areas are covered: cathodic protection in natural waters; materials for fossil fuel combustion and conversion systems; modern problems in atmospheric corrosion; innovative ideas for controlling the decaying infrastructure; deposits and their effects on corrosion in industry; volatile high temperature and non aqueous corrosion inhibitors; corrosion of light-weight and precoated metals for automotive application; refining industry corrosion; corrosion in pulp and paper industry; arctic/cold weather corrosion; materials selection for waste incinerators and associated equipment; corrosion measurement technology; environmental cracking of materials; advancing technology in the coating industry; corrosion in gas treating; green inhibition; recent advances in corrosion control of rail equipment; velocity effects and erosion corrosion in oil and gas production; marine corrosion; corrosion of materials in nuclear systems; underground corrosion control; corrosion in potable and industrial water systems in buildings and its impact on environmental compliance; deposit related boiler tube failures; boiler systems monitoring and control; recent developments and experiences in reactive metals; microbiologically influenced corrosion; corrosion and corrosion control for steel reinforced concrete; international symposium on the use of 12 and 13 Cr stainless steels in oil and gas production environments; subsea corrosion /erosion monitoring in production facilities; fiberglass reinforced pipe and tubulars in oilfield service; corrosion control technology in power transmission and distribution; mechanisms and methods of scale and deposit control; closing the loop -- results oriented cooling system monitoring and control; and minimization of aqueous discharge

  12. Effect of Ti3+ ion on the Corrosion Behavior of Alloy 600

    International Nuclear Information System (INIS)

    Lee, Chang Bong; Lim, Han Gwi; Kim, Bok Hee; Kim, Ki Ju

    1999-01-01

    Alloy 600 has been widely used as a steam generator tubing material in pressurized water reactors(PWRs) nuclear power plants. Corrosion of steam generator tubing mainly occurs on the secondary water side. The purpose of this work is primarily concerned with examining the effect of Ti 3+ ion concentrations on the corrosion behavior of the Alloy 600 steam generator tubing material. Corrosion behavior of the Alloy 600 steam generator tubing material was studied in aqueous solutions with varying Ti 3+ ion concentration at room temperature. Potentiodynamic and potentiostatic polarization techniques were used to determine the corrosion and pitting potentials for the Alloy 600 test material. The addition of Ti 3+ ion to 1000ppm, showed inhibition effect on the corrosion of Alloy 600. But the corrosion of Alloy 600 was accelerated when the concentration of Ti 3+ ion exceeded 1000ppm, it is assumed that the effect of general corrosion of Alloy 600 is more sensitive than pitting corrosion. It is considered that the passive film which was formed on the Alloy 600 surface in the 100ppm Ti 3+ ion containing solution is mainly consisted of TiO 2

  13. Dictionary corrosion and corrosion control. English-German/German-English. Fachwoerterbuch Korrosion und Korrosionsschutz. Englisch-Deutsch/Deutsch-Englisch

    Energy Technology Data Exchange (ETDEWEB)

    1985-01-01

    This dictionary has 13000 entries in both languages. Keywords and extensive accompanying information simplify the choice of word for the user. The following topics are covered: Theoretical principles of corrosion; Corrosion of the metals and alloys most frequently used in engineering. Types of corrosion - (chemical-, electro-chemical, biological corrosion); forms of corrosion (superficial, pitting, selective, intercrystalline and stress corrosion; vibrational corrosion cracking); erosion and cavitation. Methods of corrosion control (material selection, temporary corrosion protection media, paint and plastics coatings, electro-chemical coatings, corrosion prevention by treatment of the corrosive media); Corrosion testing methods.

  14. Evaluation of the susceptibility to pitting corrosion of steel api 5L x42 exposed to solutions containing chloride ions and CO{sub 2} by electrochemical noise measurements; Evaluacion de la susceptibilidad a la corrosion por picado del acero api 5l x42 expuesto a un ambiente con cloruros y CO{sub 2} mediante la tecnica de ruido electroquimico

    Energy Technology Data Exchange (ETDEWEB)

    Pena-Ballesteros, D.; Rodriguez-Vanegas, N.; Anteliz, C.; Sarmiento Klapper, H.

    2011-07-01

    The concentration of chloride ions and the partial pressure of CO{sub 2} play an important role in the degradation of low-carbon steels used for the construction of pipelines in oil and gas industry. In order to evaluate the susceptibility of carbon steel API 5L X42 to pitting corrosion electrochemical noise and linear polarization resistance measurements were carried out in aqueous solutions containing chloride ions and CO{sub 2}. The concentration of chloride ions was varied between, 10000 and 18000 ppm, and the CO{sub 2} partial pressure between 10 psi and 18 psi. Experimental results pointed out that the formation of protective layer, consisting mainly of FeCO{sub 3}, depends on the partial pressure of CO{sub 2} in the system. Nevertheless, the stability of this layer was considerably affected by increasing the concentration of chloride ions causing that localized corrosion has taken place in some areas of the surface of API 5L X42, which were detected by electrochemical noise technique. (Author) 10 refs.

  15. Exploratory shaft liner corrosion estimate

    International Nuclear Information System (INIS)

    Duncan, D.R.

    1985-10-01

    An estimate of expected corrosion degradation during the 100-year design life of the Exploratory Shaft (ES) is presented. The basis for the estimate is a brief literature survey of corrosion data, in addition to data taken by the Basalt Waste Isolation Project. The scope of the study is expected corrosion environment of the ES, the corrosion modes of general corrosion, pitting and crevice corrosion, dissimilar metal corrosion, and environmentally assisted cracking. The expected internal and external environment of the shaft liner is described in detail and estimated effects of each corrosion mode are given. The maximum amount of general corrosion degradation was estimated to be 70 mils at the exterior and 48 mils at the interior, at the shaft bottom. Corrosion at welds or mechanical joints could be significant, dependent on design. After a final determination of corrosion allowance has been established by the project it will be added to the design criteria. 10 refs., 6 figs., 5 tabs

  16. Corrosion Inhibition of Aluminium using 3-Hydroxy flavone in the Presence of Quarternary Ammonium Salts in NaOH Medium

    International Nuclear Information System (INIS)

    Princey, J. Morris; Nagarajan, Prabavathi

    2012-01-01

    The anticorrosive effect of 3-Hydroxyflavone (3HF) in combination with quarternary ammonium bromide and iodide salts (QAB and QAI) for aluminium corrosion in NaOH medium was studied at the temperature range of 303K-323K using weight loss study, potentiodynamic polarization study and impedance spectroscopic measurements. The results revealed that the inhibition efficiency increases with the inhibitor concentration and it further increases on the addition of quarternary ammonium bromide and iodide salts. The enhanced inhibition efficiency of the inhibitor in the presence of quarternary ammonium salts may be due to synergistic effect. The adsorption process of 3HF on the aluminium surface obeys Langmuir's adsorption isotherm. The mechanism of adsorption is further supported by Scanning Electron Microscopic study (SEM)

  17. Inhibition effect of 4-amino-antipyrine on the corrosion of copper in 3 wt.% NaCl solution

    Energy Technology Data Exchange (ETDEWEB)

    Hong Song; Chen Wen; Luo Hongqun [Key Laboratory of Eco-environments in Three Gorges Reservoir Region (Ministry of Education), School of Chemistry and Chemical Engineering, Southwest University, Chongqing 400715 (China); Li Nianbing, E-mail: linb@swu.edu.cn [Key Laboratory of Eco-environments in Three Gorges Reservoir Region (Ministry of Education), School of Chemistry and Chemical Engineering, Southwest University, Chongqing 400715 (China)

    2012-04-15

    Highlights: Black-Right-Pointing-Pointer 4-Amino-antipyrine (AAP) has inhibition behaviour for copper corrosion in 3.0 wt.% NaCl. Black-Right-Pointing-Pointer AAP acted as a mixed-type inhibitor with anodic predominance. Black-Right-Pointing-Pointer Adsorption of AAP on the copper surface obeys the Langmuir isotherm. Black-Right-Pointing-Pointer Quantum chemical calculations were applied to explain the experimental results. - Abstract: The effect of 4-amino-antipyrine (AAP) on the corrosion of copper in 3.0 wt.% NaCl was investigated using weight loss, potentiodynamic polarisation, and electrochemical impedance spectroscopy. The results revealed that AAP acts as a mixed-type inhibitor with more pronounced effect on anodic domain and the inhibition efficiency decreases with increasing the temperature. The adsorption of AAP was found to obey the Langmuir isotherm. Surface characterisation was performed using scanning electron microscope and Fourier transform infrared spectrometer. Quantum chemical calculations show that AAP has large negative charge in nitrogen and oxygen atoms, which facilitates the adsorption of AAP on the copper surface.

  18. Summary of model to account for inhibition of CAM corrosion by porous ceramic coating

    Energy Technology Data Exchange (ETDEWEB)

    Hopper, R., LLNL

    1998-03-31

    Corrosion occurs during five characteristic periods or regimes. These are summarized below. For more detailed discussion, see the attached Memorandum by Robert Hopper entitled `Ceramic Barrier Performance Model, Version 1.0, Description of Initial PA Input` and dated March 30, 1998.

  19. Corrosion inhibition of aluminum with a series of aniline monomeric surfactants and their analog polymers in 0.5 M HCl solution

    Directory of Open Access Journals (Sweden)

    M.M. El-Deeb

    2015-07-01

    Full Text Available The inhibition effect of 3-(12-sodiumsulfonate dodecyloxy aniline monomeric surfactant (MC12 and its analog polymer Poly 3-(dodecyloxy sulfonic acid aniline (PC12 on the corrosion of aluminum in 0.5 M HCl solution was investigated using weight loss and potentiodynamic polarization techniques. The presence of these two compounds in 0.5 M HCl inhibits the corrosion of aluminum without modifying the mechanism of corrosion process. It was found that these inhibitors act as mixed-type inhibitors with anodic predominance as well as the inhibition efficiency increases with increasing inhibitor concentration, but decreases with raising temperature. Langmuir and Frumkin adsorption isotherms fit well with the experimental data. Thermodynamic functions for both dissolution and adsorption processes were determined. The obtained results from weight loss and potentiodynamic polarization techniques are in good agreement with contact angle measurements.

  20. Pattern recognition model to estimate intergranular stress corrosion cracking (IGSCC) at crevices and pit sites of 304 SS in BWR environments

    Energy Technology Data Exchange (ETDEWEB)

    Urquidi-Macdonald, Mirna [Penn State University, 212 Earth-Engineering Science Building, University Park, PA 16801 (United States)

    2004-07-01

    Many publications have shown that crack growth rates (CGR) due to intergranular stress corrosion cracking (IGSCC) of metals is dependent on many parameters related to the manufacturing process of the steel and the environment to which the steel is exposed. Those parameters include, but are not restricted to, the concentration of chloride, fluoride, nitrates, and sulfates, pH, fluid velocity, electrochemical potential (ECP), electrolyte conductivity, stress and sensitization applied to the steel during its production and use. It is not well established how combinations of each of these parameters impact the CGR. Many different models and beliefs have been published, resulting in predictions that sometimes disagree with experimental observations. To some extent, the models are the closest to the nature of IGSCC, however, there is not a model that fully describes the entire range of observations, due to the difficulty of the problem. Among the models, the Fracture Environment Model, developed by Macdonald et al., is the most physico-chemical model, accounting for experimental observations in a wide range of environments or ECPs. In this work, we collected experimental data on BWR environments and designed a data mining pattern recognition model to learn from that data. The model was used to generate CGR estimations as a function of ECP on a BWR environment. The results of the predictive model were compared to the Fracture Environment Model predictions. The results from those two models are very close to the experimental observations of the area corresponding to creep and IGSCC controlled by diffusion. At more negative ECPs than the potential corresponding to creep, the pattern recognition predicts an increase of CGR with decreasing ECP, while the Fracture Environment Model predicts the opposite. The results of this comparison confirm that the pattern recognition model covers 3 phenomena: hydrogen embrittlement at very negative ECP, creep at intermediate ECP, and IGSCC

  1. Pattern recognition model to estimate intergranular stress corrosion cracking (IGSCC) at crevices and pit sites of 304 SS in BWR environments

    International Nuclear Information System (INIS)

    Urquidi-Macdonald, Mirna

    2004-01-01

    Many publications have shown that crack growth rates (CGR) due to intergranular stress corrosion cracking (IGSCC) of metals is dependent on many parameters related to the manufacturing process of the steel and the environment to which the steel is exposed. Those parameters include, but are not restricted to, the concentration of chloride, fluoride, nitrates, and sulfates, pH, fluid velocity, electrochemical potential (ECP), electrolyte conductivity, stress and sensitization applied to the steel during its production and use. It is not well established how combinations of each of these parameters impact the CGR. Many different models and beliefs have been published, resulting in predictions that sometimes disagree with experimental observations. To some extent, the models are the closest to the nature of IGSCC, however, there is not a model that fully describes the entire range of observations, due to the difficulty of the problem. Among the models, the Fracture Environment Model, developed by Macdonald et al., is the most physico-chemical model, accounting for experimental observations in a wide range of environments or ECPs. In this work, we collected experimental data on BWR environments and designed a data mining pattern recognition model to learn from that data. The model was used to generate CGR estimations as a function of ECP on a BWR environment. The results of the predictive model were compared to the Fracture Environment Model predictions. The results from those two models are very close to the experimental observations of the area corresponding to creep and IGSCC controlled by diffusion. At more negative ECPs than the potential corresponding to creep, the pattern recognition predicts an increase of CGR with decreasing ECP, while the Fracture Environment Model predicts the opposite. The results of this comparison confirm that the pattern recognition model covers 3 phenomena: hydrogen embrittlement at very negative ECP, creep at intermediate ECP, and IGSCC

  2. Corrosion Monitoring System

    Energy Technology Data Exchange (ETDEWEB)

    Dr. Russ Braunling

    2004-10-31

    The Corrosion Monitoring System (CMS) program developed and demonstrated a continuously on-line system that provides real-time corrosion information. The program focused on detecting pitting corrosion in its early stages. A new invention called the Intelligent Ultrasonic Probe (IUP) was patented on the program. The IUP uses ultrasonic guided waves to detect small defects and a Synthetic Aperture Focusing Technique (SAFT) algorithm to provide an image of the pits. Testing of the CMS demonstrated the capability to detect pits with dimensionality in the sub-millimeter range. The CMS was tested in both the laboratory and in a pulp and paper industrial plant. The system is capable of monitoring the plant from a remote location using the internet.

  3. Inhibition of stress corrosion cracking of alloy 600 in 10% NaOH solutions with and with lead oxide at 315 C

    International Nuclear Information System (INIS)

    Hur, D.H.; Kim, J.S.; Baek, J.S.; Kim, J.G.

    2002-01-01

    Alloy 600 steam generator tube materials have experienced various degradations by corrosion such as stress corrosion cracking (SCC) on the inner and outer diameter surface of tube, intergranular attack and pitting, and by mechanical damage such as fretting-wear and fatigue. These tube degradations not only increase the costs for tube inspection, maintenance and repair but also reduce the operation safety and the efficiency of plants. Therefore, the methodologies have been extensively developed to mitigate them. The addition of inhibitors to the coolant is a feasible method to mitigate tube degradations in operating plants. In this paper, a new inhibitor is proposed to mitigate the secondary side stress corrosion cracking of alloy 600 tubes. The effect of inhibitors on the electrochemical behavior and the stress corrosion cracking resistance of alloy 600 was evaluated in 10% sodium hydroxide solution with and without lead oxide at 315 C. The specimens of a C-ring type for stress corrosion cracking test were polarized at 150 mV above the corrosion potential for 120 hours without and with inhibitors such as titanium oxide, titanium boride, cerium boride. The chemical compositions of the films formed on the crack tip in the C-ring specimens were analyzed using a scanning Auger electron spectroscopy. The cerium boride, the most effective inhibitors, was observed to decrease the crack propagation rate more than a factor of three compared with that obtained in pure 10% NaOH solution. Furthermore, no SCC was observed in lead contaminated 10% NaOH solution by the addition of the cerium boride. (authors)

  4. Comparative analysis of adsorption and corrosion inhibitive properties of ethanol extract of Dialium Guineense leaves for mild steel in 0.5 M HCl

    OpenAIRE

    Shola Elijah Adeniji; Bamigbola Abiola Akindehinde

    2018-01-01

    Adsorption and corrosion inhibitive properties of ethanol extract of Dialium guineense leaves for mild steel in 0.5M HCl was studied using the gravimetric method. The results showed that the ethanol extract of Dialium guineense leaves is a good corrosion inhibitor for mild steel in 0.5 M HCl. The inhibition efficiency was found to increase with increase in the concentration of ethanol extract of Dialium guineense leaves up to the maximum of 92 %, but at the same time it decreased as the tempe...

  5. An overview of NiTi shape memory alloy: Corrosion resistance and antibacterial inhibition for dental application

    Energy Technology Data Exchange (ETDEWEB)

    Fadlallah, Sahar A., E-mail: sahar.fadlallah@yahoo.com [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia); Chemistry Department, Faculty of Science, Cairo University, Cairo (Egypt); El-Bagoury, Nader [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia); Casting Technology Lab., Manufacturing Technology Dept., CMRDI, P.O. Box 87, Helwan, Cairo (Egypt); Gad El-Rab, Sanaa M.F. [Biotechnology Department, Faculty of Science, Taif University, Taif (Saudi Arabia); Botany Department, Faculty of Science, Asuit University, Asuit (Egypt); Ahmed, Rasha A. [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia); Forensic Chemistry Laboratories, Medico Legal Department, Ministry of Justice, Cairo (Egypt); El-Ousamii, Ghaida [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia)

    2014-01-15

    Highlights: • Evaluate the corrosion resistance of NiTi alloy by using electrochemical techniques. • Estimate the Antibacterial inhibition rate of NiTi alloy. • Assessment the mechanical properties of NiTi from the hardness measurements. • Comparsion the microstructures of cast NiTi with Ti, this indicate the role of Ni to change the behavior of alloy in oral environment. • Advise drinking green tea in small quantities in small quantities in the event of present NiTi alloy in the oral cavity. • Recommendation to use NiTi for dental application. -- Abstract: Nowadays, Nickel–titanium nearly equiatomic is considered as one of the best biomaterials. The aim of the present work deals with the evolution of the electrochemical behavior of NiTi in simulated oral environment. The hardness, microstructures corrosion resistance and antibacterial performance of NiTi alloy were compared with pure titanium. The hardness of NiTi is twice the hardness of pure titanium. Electrochemical techniques were used to detect the corrosion resistance of both biomaterials in Hank’s solution containing (−)-epigallocatechin gallate (EGCG) which used to simulate the oral environment. In the physiological solution selected for the present study, the impedance spectroscopy (EIS) results showed that EGCG sharply increase the corrosion resistance of NiTi from 129 kΩ cm{sup 2} to 1.10 T Ω cm{sup 2} while slowly increase the corrosion resistance of pure titanium from 9.4 kΩ cm{sup 2} to 11.3 kΩ cm{sup 2} during the duration time of immersion at 37 °C. The plate-counting method was used to evaluate the antibacterial performance against Staphylococcus aureus (ATCC 6538). Among the two specimens of biomaterials studied, the antibacterial performance results revealed that the NiTi alloy is better than the pure titanium. The morphology and chemical structure of NiTi and Ti samples were systematically investigated by scanning electron microscope (SEM) and energy dispersive X

  6. An overview of NiTi shape memory alloy: Corrosion resistance and antibacterial inhibition for dental application

    International Nuclear Information System (INIS)

    Fadlallah, Sahar A.; El-Bagoury, Nader; Gad El-Rab, Sanaa M.F.; Ahmed, Rasha A.; El-Ousamii, Ghaida

    2014-01-01

    Highlights: • Evaluate the corrosion resistance of NiTi alloy by using electrochemical techniques. • Estimate the Antibacterial inhibition rate of NiTi alloy. • Assessment the mechanical properties of NiTi from the hardness measurements. • Comparsion the microstructures of cast NiTi with Ti, this indicate the role of Ni to change the behavior of alloy in oral environment. • Advise drinking green tea in small quantities in small quantities in the event of present NiTi alloy in the oral cavity. • Recommendation to use NiTi for dental application. -- Abstract: Nowadays, Nickel–titanium nearly equiatomic is considered as one of the best biomaterials. The aim of the present work deals with the evolution of the electrochemical behavior of NiTi in simulated oral environment. The hardness, microstructures corrosion resistance and antibacterial performance of NiTi alloy were compared with pure titanium. The hardness of NiTi is twice the hardness of pure titanium. Electrochemical techniques were used to detect the corrosion resistance of both biomaterials in Hank’s solution containing (−)-epigallocatechin gallate (EGCG) which used to simulate the oral environment. In the physiological solution selected for the present study, the impedance spectroscopy (EIS) results showed that EGCG sharply increase the corrosion resistance of NiTi from 129 kΩ cm 2 to 1.10 T Ω cm 2 while slowly increase the corrosion resistance of pure titanium from 9.4 kΩ cm 2 to 11.3 kΩ cm 2 during the duration time of immersion at 37 °C. The plate-counting method was used to evaluate the antibacterial performance against Staphylococcus aureus (ATCC 6538). Among the two specimens of biomaterials studied, the antibacterial performance results revealed that the NiTi alloy is better than the pure titanium. The morphology and chemical structure of NiTi and Ti samples were systematically investigated by scanning electron microscope (SEM) and energy dispersive X-ray analysis (EDX). The

  7. Inhibition of intergranular stress corrosion cracking of sensitized type 304 stainless steel. Annual report

    International Nuclear Information System (INIS)

    Brown, B.F.

    1977-01-01

    The effectiveness of various inhibitors in mitigating stress corrosion cracking of stainless steel in hot aqueous environment was evaluated. The inhibitors studied were of three types: poly-oxy-anions, organic competitive absorbers, and simple cations; the corrosive medium was 4M NaCl acidified with H 2 SO 4 to ph of about 2.3. The following conclusions were reached: pH does not affect cracking kinetics in a sensitive way; cracking time is highly dependent on chloride concentrations; poly-oxy-anions do not perform well; organics offer some possibilities as inhibitors; cationic additives can have effects varying from trivial to total suppression of cracking--behavior is both cation and concentration dependent. 2 figures, 5 tables

  8. Electrochemical assessing corrosion inhibiting effects of zinc aluminum polyphosphate (ZAPP) as a modified zinc phosphate pigment

    International Nuclear Information System (INIS)

    Naderi, R.; Attar, M.M.

    2008-01-01

    Undesirable anti-corrosion performance of zinc phosphate pigment, the classical chromate replacement, has led researchers to take modification into account. Polyphosphate-based anti-corrosion pigments as a result of modification of zinc orthophosphate have been found to function much more efficiently. This study aimed to evaluate performance of steel samples immersed in 3.5% NaCl aqueous solution-containing zinc aluminum polyphosphate (ZAPP) pigment extract compared to those involving conventional zinc phosphate (ZP) pigment extract and also no pigment (blank) using electrochemical tests such as electrochemical impedance spectroscopy (EIS) and linear polarization (LP) as well as surface analysis. Impedance spectra and polarization curves revealed two different trends, showing the superiority of ZAPP pigment. Based on the results of scanning electron microscopy (SEM) and energy dispersive X-ray analysis (EDX), presence of a precipitated layer on the surface was confirmed when steel sample was immersed into the solution-containing ZAPP

  9. Inhibition de corrosion des échangeurs thermiques en aluminium et ...

    African Journals Online (AJOL)

    Ainsi, on peut trouver dans un même circuit de chauffage central la chaudière en aluminium, la tuyauterie en cuivre et les radiateurs en fonte, acier ou aluminium et aussi des matériaux polymères. Nous décrivons un nouvel inhibiteur de corrosion spécifiquement conçu pour protéger les circuits de chauffage central dans ...

  10. Inhibition de corrosion des échangeurs thermiques en aluminium et ...

    African Journals Online (AJOL)

    L'introduction de haute technologie dans l'industrie de chauffage central a été accompagnée avec des nouveaux problèmes de corrosion liés aux concepts modernes tels que la condensation et le choix des matériaux. Ainsi, on peut trouver dans un même circuit de chauffage central la chaudière en aluminium, la tuyauterie ...

  11. Osseoconductive and Corrosion-Inhibiting Plasma-Sprayed Calcium Phosphate Coatings for Metallic Medical Implants

    Directory of Open Access Journals (Sweden)

    Robert B. Heimann

    2017-11-01

    Full Text Available During the last several decades, research into bioceramic coatings for medical implants has emerged as a hot topic among materials scientists and clinical practitioners alike. In particular, today, calcium phosphate-based bioceramic materials are ubiquitously used in clinical applications to coat the stems of metallic endoprosthetic hips as well as the surfaces of dental root implants. Such implants frequently consist of titanium alloys, CoCrMo alloy, or austenitic surgical stainless steels, and aim at replacing lost body parts or restoring functions to diseased or damaged tissues of the human body. In addition, besides such inherently corrosion-resistant metals, increasingly, biodegradable metals such as magnesium alloys are being researched for osseosynthetic devices and coronary stents both of which are intended to remain in the human body for only a short time. Biocompatible coatings provide not only vital biological functions by supporting osseoconductivity but may serve also to protect the metallic parts of implants from corrosion in the aggressive metabolic environment. Moreover, the essential properties of hydroxylapatite-based bioceramic coatings including their in vitro alteration in contact with simulated body fluids will be addressed in this current review paper. In addition, a paradigmatic shift is suggested towards the development of transition metal-substituted calcium hexa-orthophosphates with the NaSiCON (Na superionic conductor structure to be used for implant coatings with superior degradation resistance in the corrosive body environment and with pronounced ionic conductivity that might be utilized in novel devices for electrical bone growth stimulation.

  12. Surface coverage and corrosion inhibition effect of Rosmarinus officinalis and zinc oxide on the electrochemical performance of low carbon steel in dilute acid solutions

    Directory of Open Access Journals (Sweden)

    Roland Tolulope Loto

    2018-03-01

    Full Text Available Electrochemical analysis of the corrosion inhibition and surface protection properties of the combined admixture of Rosmarinus officinalis and zinc oxide on low carbon steel in 1 M HCl and H2SO4 solution was studied by potentiodynamic polarization, open circuit potential measurement, optical microscopy and ATR-FTIR spectroscopy. Results obtained confirmed the compound to be more effective in HCl solution, with optimal inhibition efficiencies of 93.26% in HCl and 87.7% in H2SO4 acid solutions with mixed type inhibition behavior in both acids. The compound shifts the corrosion potential values of the steel cathodically in HCl and anodically in H2SO4 signifying specific corrosion inhibition behavior without applied potential. Identified functional groups of alcohols, phenols, 1°, 2° amines, amides, carbonyls (general, esters, saturated aliphatic, carboxylic acids, ethers, aliphatic amines, alkenes, aromatics, alkyl halides and alkynes within the compound completely adsorbed onto the steel forming a protective covering. Thermodynamic calculations showed physisorption molecular interaction with the steel’s surface according to Langmuir and Frumkin adsorption isotherms. Optical microscopy images of the inhibited and uninhibited steels contrast each other with steel specimens from HCl solution showing a better morphology. Keywords: Corrosion, Inhibitor, Adsorption, Steel, Acid

  13. A Bayesian approach to modeling and predicting pitting flaws in steam generator tubes

    International Nuclear Information System (INIS)

    Yuan, X.-X.; Mao, D.; Pandey, M.D.

    2009-01-01

    Steam generators in nuclear power plants have experienced varying degrees of under-deposit pitting corrosion. A probabilistic model to accurately predict pitting damage is necessary for effective life-cycle management of steam generators. This paper presents an advanced probabilistic model of pitting corrosion characterizing the inherent randomness of the pitting process and measurement uncertainties of the in-service inspection (ISI) data obtained from eddy current (EC) inspections. A Markov chain Monte Carlo simulation-based Bayesian method, enhanced by a data augmentation technique, is developed for estimating the model parameters. The proposed model is able to predict the actual pit number, the actual pit depth as well as the maximum pit depth, which is the main interest of the pitting corrosion model. The study also reveals the significance of inspection uncertainties in the modeling of pitting flaws using the ISI data: Without considering the probability-of-detection issues and measurement errors, the leakage risk resulted from the pitting corrosion would be under-estimated, despite the fact that the actual pit depth would usually be over-estimated.

  14. Corrosion of Metal-Matrix Composites with Aluminium Alloy Substrate

    Directory of Open Access Journals (Sweden)

    B. Bobic

    2010-03-01

    Full Text Available The corrosion behaviour of MMCs with aluminium alloy matrix was presented. The corrosion characteristics of boron-, graphite-, silicon carbide-, alumina- and mica- reinforced aluminium MMCs were reviewed. The reinforcing phase influence on MMCs corrosion rate as well as on various corrosion forms (galvanic, pitting, stress corrosion cracking, corrosion fatique, tribocorrosion was discussed. Some corrosion protection methods of aluminium based MMCs were described

  15. Corrosion inhibition of mild steel in 1 M HCl solution by henna extract: A comparative study of the inhibition by henna and its constituents (Lawsone, Gallic acid, α-D-Glucose and Tannic acid)

    International Nuclear Information System (INIS)

    Ostovari, A.; Hoseinieh, S.M.; Peikari, M.; Shadizadeh, S.R.; Hashemi, S.J.

    2009-01-01

    The inhibitive action of henna extract (Lawsonia inermis) and its main constituents (lawsone, gallic acid, α-D-Glucose and tannic acid) on corrosion of mild steel in 1 M HCl solution was investigated through electrochemical techniques and surface analysis (SEM/EDS). Polarization measurements indicate that all the examined compounds act as a mixed inhibitor and inhibition efficiency increases with inhibitor concentration. Maximum inhibition efficiency (92.06%) is obtained at 1.2 g/l henna extract. Inhibition efficiency increases in the order: lawsone > henna extract > gallic acid > α-D-Glucose > tannic acid. Also, inhibition mechanism and thermodynamic parameters are discussed.

  16. Corrosion inhibition of mild steel in 1 M HCl solution by henna extract: A comparative study of the inhibition by henna and its constituents (Lawsone, Gallic acid, {alpha}-D-Glucose and Tannic acid)

    Energy Technology Data Exchange (ETDEWEB)

    Ostovari, A. [Technical Inspection Engineering Department, Petroleum University of Technology, Abadan (Iran, Islamic Republic of)], E-mail: A.Ostovari@gmail.com; Hoseinieh, S.M.; Peikari, M. [Technical Inspection Engineering Department, Petroleum University of Technology, Abadan (Iran, Islamic Republic of); Shadizadeh, S.R. [Petroleum Engineering Department, Petroleum University of Technology, Abadan (Iran, Islamic Republic of); Hashemi, S.J. [Technical Inspection Engineering Department, Petroleum University of Technology, Abadan (Iran, Islamic Republic of)

    2009-09-15

    The inhibitive action of henna extract (Lawsonia inermis) and its main constituents (lawsone, gallic acid, {alpha}-D-Glucose and tannic acid) on corrosion of mild steel in 1 M HCl solution was investigated through electrochemical techniques and surface analysis (SEM/EDS). Polarization measurements indicate that all the examined compounds act as a mixed inhibitor and inhibition efficiency increases with inhibitor concentration. Maximum inhibition efficiency (92.06%) is obtained at 1.2 g/l henna extract. Inhibition efficiency increases in the order: lawsone > henna extract > gallic acid > {alpha}-D-Glucose > tannic acid. Also, inhibition mechanism and thermodynamic parameters are discussed.

  17. Inhibition Effects of a Synthesized Novel 4-Aminoantipyrine Derivative on the Corrosion of Mild Steel in Hydrochloric Acid Solution together with Quantum Chemical Studies

    Directory of Open Access Journals (Sweden)

    Abu Bakar Mohamad

    2013-06-01

    Full Text Available 1,5-Dimethyl-4-((2-methylbenzylideneamino-2-phenyl-1H-pyrazol-3(2H-one (DMPO was synthesized to be evaluated as a corrosion inhibitor. The corrosion inhibitory effects of DMPO on mild steel in 1.0 M HCl were investigated using electrochemical impedance spectroscopy (EIS, potentiodynamic polarization, open circuit potential (OCP and electrochemical frequency modulation (EFM. The results showed that DMPO inhibited mild steel corrosion in acid solution and indicated that the inhibition efficiency increased with increasing inhibitor concentration. Changes in the impedance parameters suggested an adsorption of DMPO onto the mild steel surface, leading to the formation of protective films. The novel synthesized corrosion inhibitor was characterized using UV-Vis, FT-IR and NMR spectral analyses. Electronic properties such as highest occupied molecular orbital energy, lowest unoccupied molecular orbital energy (EHOMO and ELUMO, respectively and dipole moment (μ were calculated and discussed. The results showed that the corrosion inhibition efficiency increased with an increase in the EHOMO values but with a decrease in the ELUMO value.

  18. Experimental and theoretical investigations on the inhibition of mild steel corrosion in the ground water medium using newly synthesised bipodal and tripodal imidazole derivatives

    Energy Technology Data Exchange (ETDEWEB)

    Gopi, D., E-mail: dhanaraj_gopi@yahoo.com [Department of Chemistry, Periyar University, Salem 636 011, Tamilnadu (India); Centre for Nanoscience and Nanotechnology, Periyar University, Salem 636 011, Tamilnadu (India); Sherif, El-Sayed M. [Center of Excellence for Research in Engineering Materials (CEREM), Advanced Manufacturing Institute, King Saud University, P.O. Box 800, Al-Riyadh 11421 (Saudi Arabia); Electrochemistry and Corrosion Laboratory, Department of Physical Chemistry, National Research Centre (NRC), Dokki, 12622 Cairo (Egypt); Surendiran, M. [Department of Chemistry, Periyar University, Salem 636 011, Tamilnadu (India); Jothi, M.; Kumaradhas, P. [Department of Physics, Periyar University, Salem 636 011, Tamilnadu (India); Kavitha, L. [Department of Physics, School of Basic and Applied Sciences, Central University of Tamilnadu, Thiruvarur 610 101, Tamilnadu (India)

    2014-10-15

    Two new imidazole derivatives, namely 1,4-bis(N-imidazolylmethyl)-2-5-dimethoxybenzene (BIDM) and 1,3,5-tris(N-imidazolylmethyl)-2,4,6-trimethoxybenzene (TITM), were synthesised and their effects on the inhibition of mild steel corrosion in ground water medium are reported. The study was carried out using gravimetric and electrochemical techniques in order to determine the corrosion inhibition efficiencies of the bipodal and tripodal structured imidazoles. Further, the quantum chemical calculations using density functional theory (DFT) gave a profound insight into the inhibitory action mechanism of BIDM and TITM and their calculation parameters, such as E{sub HOMO}, E{sub LUMO} and ΔE were in good agreement with the results of the experimental studies. BIDM and TITM exhibited lowest corrosion current densities of circa 7.5 μA cm{sup −2} and 4.1 μAcm{sup −2} at the optimum concentrations of 0.67 and 0.49 mM, respectively. All measurements thus confirmed that both BIDM and TITM behaved as good inhibitors for mild steel corrosion in ground water medium. - Highlights: • Synthesis of new imidazole derivatives-BIDM(bipodal) and TITM(tripodal) inhibitors. • Gravimetric analysis to investigate mild steel corrosion inhibition in ground water. • Electrochemical characterizations to substantiate results of weight loss method. • Quantum studies to analyse the chemical behavior, structure and substituent effect.

  19. Inhibition Effects of a Synthesized Novel 4-Aminoantipyrine Derivative on the Corrosion of Mild Steel in Hydrochloric Acid Solution together with Quantum Chemical Studies

    Science.gov (United States)

    Junaedi, Sutiana; Al-Amiery, Ahmed A.; Kadihum, Abdulhadi; Kadhum, Abdul Amir H.; Mohamad, Abu Bakar

    2013-01-01

    1,5-Dimethyl-4-((2-methylbenzylidene)amino)-2-phenyl-1H-pyrazol-3(2H)-one (DMPO) was synthesized to be evaluated as a corrosion inhibitor. The corrosion inhibitory effects of DMPO on mild steel in 1.0 M HCl were investigated using electrochemical impedance spectroscopy (EIS), potentiodynamic polarization, open circuit potential (OCP) and electrochemical frequency modulation (EFM). The results showed that DMPO inhibited mild steel corrosion in acid solution and indicated that the inhibition efficiency increased with increasing inhibitor concentration. Changes in the impedance parameters suggested an adsorption of DMPO onto the mild steel surface, leading to the formation of protective films. The novel synthesized corrosion inhibitor was characterized using UV-Vis, FT-IR and NMR spectral analyses. Electronic properties such as highest occupied molecular orbital energy, lowest unoccupied molecular orbital energy (EHOMO and ELUMO, respectively) and dipole moment (μ) were calculated and discussed. The results showed that the corrosion inhibition efficiency increased with an increase in the EHOMO values but with a decrease in the ELUMO value. PMID:23736696

  20. Experimental and theoretical investigations on the inhibition of mild steel corrosion in the ground water medium using newly synthesised bipodal and tripodal imidazole derivatives

    International Nuclear Information System (INIS)

    Gopi, D.; Sherif, El-Sayed M.; Surendiran, M.; Jothi, M.; Kumaradhas, P.; Kavitha, L.

    2014-01-01

    Two new imidazole derivatives, namely 1,4-bis(N-imidazolylmethyl)-2-5-dimethoxybenzene (BIDM) and 1,3,5-tris(N-imidazolylmethyl)-2,4,6-trimethoxybenzene (TITM), were synthesised and their effects on the inhibition of mild steel corrosion in ground water medium are reported. The study was carried out using gravimetric and electrochemical techniques in order to determine the corrosion inhibition efficiencies of the bipodal and tripodal structured imidazoles. Further, the quantum chemical calculations using density functional theory (DFT) gave a profound insight into the inhibitory action mechanism of BIDM and TITM and their calculation parameters, such as E HOMO , E LUMO and ΔE were in good agreement with the results of the experimental studies. BIDM and TITM exhibited lowest corrosion current densities of circa 7.5 μA cm −2 and 4.1 μAcm −2 at the optimum concentrations of 0.67 and 0.49 mM, respectively. All measurements thus confirmed that both BIDM and TITM behaved as good inhibitors for mild steel corrosion in ground water medium. - Highlights: • Synthesis of new imidazole derivatives-BIDM(bipodal) and TITM(tripodal) inhibitors. • Gravimetric analysis to investigate mild steel corrosion inhibition in ground water. • Electrochemical characterizations to substantiate results of weight loss method. • Quantum studies to analyse the chemical behavior, structure and substituent effect