  1. Extrusion and properties of lead zirconate titanate piezoelectric ceramics

    DEFF Research Database (Denmark)

    Cai, S.; Millar, C.E.; Pedersen, L.

    1997-01-01

    The purpose of this work was to develop a procedure for fabricating electroceramic actuators with good piezoelectric properties. The preparation of lead zirconate titanate (PZT) piezoelectric ceramic rods and tubes by extrusion processing is described. The microstructure of extrudates was investi......The purpose of this work was to develop a procedure for fabricating electroceramic actuators with good piezoelectric properties. The preparation of lead zirconate titanate (PZT) piezoelectric ceramic rods and tubes by extrusion processing is described. The microstructure of extrudates...

  2. Evolution of bias field and offset piezoelectric coefficient in bulk lead zirconate titanate with fatigue

    International Nuclear Information System (INIS)

    Zhang Yong; Baturin, Ivan S.; Aulbach, Emil; Lupascu, Doru C.; Kholkin, Andrei L.; Shur, Vladimir Ya.; Roedel, Juergen

    2005-01-01

    Hysteresis loops of the piezoelectric coefficient, d 33 =f(E 3 ), are measured on virgin and fatigued lead zirconate titanate ceramics. Four parameters are directly extracted from the measurements: internal bias field E b , offset piezoelectric coefficient d offset , coercive field E c , and remnant piezoelectric coefficient d r . The reduction in d r displays the decreasing switchable polarization with fatigue cycling. E b and d offset are found to be linearly related. After thermal annealing, both offsets disappear, while the increase in E c and the reduction in d r withstand annealing. The microscopic entities responsible for the offsets are less stable than those for reduced switching

  3. Evolution of transverse piezoelectric response of lead zirconate titanate ceramics under hydrostatic pressure

    International Nuclear Information System (INIS)

    Li Fei; Xu Zhuo; Wei Xiaoyong; Gao Junjie; Zhang, Chonghui; Yao Xi; Jin Li

    2009-01-01

    The piezoelectric properties of 31-mode resonators of lead zirconate titanate ceramics under hydrostatic pressure from 0.1 to 325 MPa were evaluated by a fitting method, in which mechanical loss was taken into account. Our results based on the fitting method showed a hydrostatic pressure independent tendency of the piezoelectric coefficient and the electromechanical coupling factor because the adopted PZT ceramic can be considered as a linear system in our experiment, while two misleading tendencies of piezoelectric coefficient were obtained based on the resonance method when ignoring the contribution of the mechanical loss. (fast track communication)

  4. Cross-poling textures in a lead zirconate titanate piezoelectric material

    International Nuclear Information System (INIS)

    Wan, Shan; Bowman, Keith J.

    2000-01-01

    Tetragonal ferroelectric materials are polarized to induce the anisotropy necessary for the piezoelectric effect. This poling of the material is inherently an orientation process. Pole figure texture measurements of poling and cross-poling in a lead zirconate titanate Navy VI material show domain motion. The resulting axisymmetric and three-dimensional textures demonstrate the contribution of 90 degree sign domain motion to piezoelectricity. Cross-poling results in strong orientations with lower applied fields than in the initial poling steps. (c) 2000 Materials Research Society

  5. Compact piezoelectric micromotor with a single bulk lead zirconate titanate stator

    Science.gov (United States)

    Yan, Liang; Lan, Hua; Jiao, Zongxia; Chen, Chin-Yin; Chen, I.-Ming

    2013-04-01

    The advance of micro/nanotechnology promotes the development of micromotors in recent years. In this article, a compact piezoelectric ultrasonic micromotor with a single bulk lead zirconate titanate stator is proposed. A traveling wave is generated by superposition of bending modes with 90° phase difference excited by d15 inverse piezoelectric effects. The operating principle simplifies the system structure significantly, and provides a miniaturization solution. A research prototype with the size of 0.75× 0.75×1.55 mm is developed. It can produce start-up torque of 0.27μNmand maximum speed of 2760 r/min at 14RMS.

  6. Piezoelectric Lead Zirconate Titanate (PZT) Ring Shaped Contour-Mode MEMS Resonators

    Science.gov (United States)

    Kasambe, P. V.; Asgaonkar, V. V.; Bangera, A. D.; Lokre, A. S.; Rathod, S. S.; Bhoir, D. V.

    2018-02-01

    Flexibility in setting fundamental frequency of resonator independent of its motional resistance is one of the desired criteria in micro-electromechanical (MEMS) resonator design. It is observed that ring-shaped piezoelectric contour-mode MEMS resonators satisfy this design criterion than in case of rectangular plate MEMS resonators. Also ring-shaped contour-mode piezoelectric MEMS resonator has an advantage that its fundamental frequency is defined by in-plane dimensions, but they show variation of fundamental frequency with different Platinum (Pt) thickness referred as change in ratio of fNEW /fO . This paper presents the effects of variation in geometrical parameters and change in piezoelectric material on the resonant frequencies of Platinum piezoelectric-Aluminium ring-shaped contour-mode MEMS resonators and its electrical parameters. The proposed structure with Lead Zirconate Titanate (PZT) as the piezoelectric material was observed to be a piezoelectric material with minimal change in fundamental resonant frequency due to Platinum thickness variation. This structure was also found to exhibit extremely low motional resistance of 0.03 Ω as compared to the 31-35 Ω range obtained when using AlN as the piezoelectric material. CoventorWare 10 is used for the design, simulation and corresponding analysis of resonators which is Finite Element Method (FEM) analysis and design tool for MEMS devices.

  7. Unexpectedly high piezoelectricity of Sm-doped lead zirconate titanate in the Curie point region.

    Science.gov (United States)

    Seshadri, Shruti B; Nolan, Michelle M; Tutuncu, Goknur; Forrester, Jennifer S; Sapper, Eva; Esteves, Giovanni; Granzow, Torsten; Thomas, Pam A; Nino, Juan C; Rojac, Tadej; Jones, Jacob L

    2018-03-07

    Large piezoelectric coefficients in polycrystalline lead zirconate titanate (PZT) are traditionally achieved through compositional design using a combination of chemical substitution with a donor dopant and adjustment of the zirconium to titanium compositional ratio to meet the morphotropic phase boundary (MPB). In this work, a different route to large piezoelectricity is demonstrated. Results reveal unexpectedly high piezoelectric coefficients at elevated temperatures and compositions far from the MPB. At temperatures near the Curie point, doping with 2 at% Sm results in exceptionally large piezoelectric coefficients of up to 915 pm/V. This value is approximately twice those of other donor dopants (e.g., 477 pm/V for Nb and 435 pm/V for La). Structural changes during the phase transitions of Sm-doped PZT show a pseudo-cubic phase forming ≈50 °C below the Curie temperature. Possible origins of these effects are discussed and the high piezoelectricity is posited to be due to extrinsic effects. The enhancement of the mechanism at elevated temperatures is attributed to the coexistence of tetragonal and pseudo-cubic phases, which enables strain accommodation during electromechanical deformation and interphase boundary motion. This work provides insight into possible routes for designing high performance piezoelectrics which are alternatives to traditional methods relying on MPB compositions.

  8. Conformable amplified lead zirconate titanate sensors with enhanced piezoelectric response for cutaneous pressure monitoring.

    Science.gov (United States)

    Dagdeviren, Canan; Su, Yewang; Joe, Pauline; Yona, Raissa; Liu, Yuhao; Kim, Yun-Soung; Huang, YongAn; Damadoran, Anoop R; Xia, Jing; Martin, Lane W; Huang, Yonggang; Rogers, John A

    2014-08-05

    The ability to measure subtle changes in arterial pressure using devices mounted on the skin can be valuable for monitoring vital signs in emergency care, detecting the early onset of cardiovascular disease and continuously assessing health status. Conventional technologies are well suited for use in traditional clinical settings, but cannot be easily adapted for sustained use during daily activities. Here we introduce a conformal device that avoids these limitations. Ultrathin inorganic piezoelectric and semiconductor materials on elastomer substrates enable amplified, low hysteresis measurements of pressure on the skin, with high levels of sensitivity (~0.005 Pa) and fast response times (~0.1 ms). Experimental and theoretical studies reveal enhanced piezoelectric responses in lead zirconate titanate that follow from integration on soft supports as well as engineering behaviours of the associated devices. Calibrated measurements of pressure variations of blood flow in near-surface arteries demonstrate capabilities for measuring radial artery augmentation index and pulse pressure velocity.

  9. Determination of temperature dependence of piezoelectric coefficients matrix of lead zirconate titanate ceramics by quasi-static and resonance method

    International Nuclear Information System (INIS)

    Li Fei; Xu Zhuo; Wei Xiaoyong; Yao Xi

    2009-01-01

    The piezoelectric coefficients (d 33 , -d 31 , d 15 , g 33 , -g 31 , g 15 ) of soft and hard lead zirconate titanate ceramics were measured by the quasi-static and resonance methods, at temperatures from 20 to 300 0 C. The results showed that the piezoelectric coefficients d 33 , -d 31 and d 15 obtained by these two methods increased with increasing temperature for both hard and soft PZT ceramics, while the piezoelectric coefficients g 33 , -g 31 and g 15 decreased with increasing temperature for both hard and soft PZT ceramics. In this paper, the observed results were also discussed in terms of intrinsic and extrinsic contributions to piezoelectric response.

  10. Ferroelectric and Piezoelectric properties of (111) oriented lanthanum modified lead zirconate titanate film

    International Nuclear Information System (INIS)

    Dutta, Soma; Antony Jeyaseelan, A.; Sruthi, S.

    2014-01-01

    Lanthanum modified lead zirconate titanate (PLZT) thick film with molecular formula of Pb 0.92 La 0.08 (Zr 0.52 Ti 0.48 ) 0.98 O 3 was grown preferentially along (111) direction on Pt/SiO 2 /Si (platinum/silicon oxide/silicon) substrate by spin coating of chemical solution. The directional growth of the film was facilitated by platinum (Pt) (111) template and rapid thermal annealing. X-ray diffraction pattern and atomic force microscopy revealed the preferential growth of the PLZT film. The film was characterized for ferroelectric and detailed piezoelectric properties in a parallel plate capacitor (metal–PLZT–metal) configuration. Ferroelectric characterization of the film showed saturated hysteresis loop with remanent polarization and coercive electric field values of 10.14 μC/cm 2 and 42 kV/cm, respectively, at an applied field of 300 kV/cm. Longitudinal piezoelectric coefficient (d 33,f ) was measured by employing converse piezoelectric effect where electrical charge response and displacement were measured with electrical voltage excitation on the sample electrodes. The effective transverse piezoelectric coefficient (e 31,f ) was derived from charge measurement with an applied mechanical excitation strain by using the four point bending method. d 33,f and e 31,f coefficients of PLZT films were found to be 380 pm/V and − 0.831 C/m 2 respectively. - Highlights: • PLZT (111) film is prepared by spin coating of chemical sol on Pt (111) template. • Piezoelectric d 33 value (380 pm/V) of PLZT film is found 20% higher than PZT. • Transverse piezocoefficient e 31,f of PLZT film is reported for the first time

  11. Ferroelectric and Piezoelectric properties of (111) oriented lanthanum modified lead zirconate titanate film

    Energy Technology Data Exchange (ETDEWEB)

    Dutta, Soma, E-mail: som@nal.res.in; Antony Jeyaseelan, A.; Sruthi, S.

    2014-07-01

    Lanthanum modified lead zirconate titanate (PLZT) thick film with molecular formula of Pb{sub 0.92}La{sub 0.08}(Zr{sub 0.52}Ti{sub 0.48}){sub 0.98}O{sub 3} was grown preferentially along (111) direction on Pt/SiO{sub 2}/Si (platinum/silicon oxide/silicon) substrate by spin coating of chemical solution. The directional growth of the film was facilitated by platinum (Pt) (111) template and rapid thermal annealing. X-ray diffraction pattern and atomic force microscopy revealed the preferential growth of the PLZT film. The film was characterized for ferroelectric and detailed piezoelectric properties in a parallel plate capacitor (metal–PLZT–metal) configuration. Ferroelectric characterization of the film showed saturated hysteresis loop with remanent polarization and coercive electric field values of 10.14 μC/cm{sup 2} and 42 kV/cm, respectively, at an applied field of 300 kV/cm. Longitudinal piezoelectric coefficient (d{sub 33,f}) was measured by employing converse piezoelectric effect where electrical charge response and displacement were measured with electrical voltage excitation on the sample electrodes. The effective transverse piezoelectric coefficient (e{sub 31,f}) was derived from charge measurement with an applied mechanical excitation strain by using the four point bending method. d{sub 33,f} and e{sub 31,f} coefficients of PLZT films were found to be 380 pm/V and − 0.831 C/m{sup 2} respectively. - Highlights: • PLZT (111) film is prepared by spin coating of chemical sol on Pt (111) template. • Piezoelectric d{sub 33} value (380 pm/V) of PLZT film is found 20% higher than PZT. • Transverse piezocoefficient e{sub 31,f} of PLZT film is reported for the first time.

  12. Piezoelectric and dielectric performance of poled lead zirconate titanate subjected to electric cyclic fatigue

    Science.gov (United States)

    Wang, Hong; Matsunaga, Tadashi; Lin, Hua-Tay; Mottern, Alexander M.

    2012-02-01

    Poled lead zirconate titanate (PZT) material as a single-layer plate was tested using a piezodilatometer under electric cyclic loading in both unipolar and bipolar modes. Its responses were evaluated using unipolar and bipolar measurements on the same setup. The mechanical strain and charge density loops exhibited various variations when the material was cycled for more than 108 cycles. The various quantities including loop amplitude, hysteresis, switchable polarization, and coercive field were characterized accordingly under the corresponding measurement conditions. At the same time, the offset polarization and bias electric field of the material were observed to be changed and the trend was found to be related to the measurement conditions also. Finally, the piezoelectric and dielectric coefficients were analyzed and their implications for the application of interest have been discussed.

  13. Piezoelectric and dielectric performance of poled lead zirconate titanate subjected to electric cyclic fatigue

    International Nuclear Information System (INIS)

    Wang, Hong; Matsunaga, Tadashi; Lin, Hua-Tay; Mottern, Alexander M

    2012-01-01

    Poled lead zirconate titanate (PZT) material as a single-layer plate was tested using a piezodilatometer under electric cyclic loading in both unipolar and bipolar modes. Its responses were evaluated using unipolar and bipolar measurements on the same setup. The mechanical strain and charge density loops exhibited various variations when the material was cycled for more than 10 8 cycles. The various quantities including loop amplitude, hysteresis, switchable polarization, and coercive field were characterized accordingly under the corresponding measurement conditions. At the same time, the offset polarization and bias electric field of the material were observed to be changed and the trend was found to be related to the measurement conditions also. Finally, the piezoelectric and dielectric coefficients were analyzed and their implications for the application of interest have been discussed. (paper)

  14. Research on output signal of piezoelectric lead zirconate titanate detector using Monte Carlo method

    Energy Technology Data Exchange (ETDEWEB)

    Takechi, Seiji, E-mail: takechi@elec.eng.osaka-cu.ac.jp [Graduate School of Engineering, Osaka City University, Osaka 558-8585 (Japan); Mitsuhashi, Tomoaki; Miura, Yoshinori [Graduate School of Engineering, Osaka City University, Osaka 558-8585 (Japan); Miyachi, Takashi; Kobayashi, Masanori; Okudaira, Osamu [Planetary Exploration Research Center, Chiba Institute of Technology, Narashino, Chiba 275-0016 (Japan); Shibata, Hiromi [The Institute of Scientific and Industrial Research, Osaka University, Ibaraki, Osaka 567-0047 (Japan); Fujii, Masayuki [Famscience Co., Ltd., Tsukubamirai, Ibaraki 300-2435 (Japan); Okada, Nagaya [Honda Electronics Co., Ltd., Toyohashi, Aichi 441-3193 (Japan); Murakami, Takeshi; Uchihori, Yukio [National Institute of Radiological Sciences, Chiba 263-8555 (Japan)

    2017-06-21

    The response of a radiation detector fabricated from piezoelectric lead zirconate titanate (PZT) was studied. The response signal due to a single 400 MeV/n xenon (Xe) ion was assumed to have a simple form that was composed of two variables, the amplitude and time constant. These variables were estimated by comparing two output waveforms obtained from a computer simulation and an experiment on Xe beam irradiation. Their values appeared to be dependent on the beam intensity. - Highlights: • The performance of PZT detector was studied by irradiation of a 400 MeV/n Xe beam. • Monte Carlo simulation was used to examine the formation process of the output. • The response signal due to a single Xe ion was assumed to have a simple form. • The form was composed of two variables, the amplitude and time constant. • These variables appeared to be dependent on the beam intensity.

  15. Output characteristics of piezoelectric lead zirconate titanate detector using high-energy heavy-ion beam

    International Nuclear Information System (INIS)

    Takechi, Seiji; Sekiguchi, Masahiro; Miyachi, Takashi; Kobayashi, Masanori; Hattori, Maki; Okudaira, Osamu; Shibata, Hiromi; Fujii, Masayuki; Okada, Nagaya; Murakami, Takeshi; Uchihori, Yukio

    2014-01-01

    A radiation detector fabricated using piezoelectric lead zirconate titanate (PZT) has been studied by irradiating it with a 400 MeV/n xenon (Xe) beam. The beam diameter was controlled to change the irradiation conditions. It was found that the magnitude of the output observed from the PZT detector may be related to the number of Xe ions per unit area per unit time within the limits of the experimental conditions. -- Highlights: • The performance of PZT detector was studied by irradiation of a 400 MeV/n Xe beam. • The beam diameter was controlled to change the irradiation conditions. • By the control, the number of Xe ions per one pulse was changed from ∼500 to ∼1500. • The output of the PZT detector was not always larger with more intense beam. • The energy of Xe ions per unit area per unit time may determine the output

  16. Development of a stress sensor based on the piezoelectric lead zirconate titanate for impact stress measurement

    Science.gov (United States)

    Liu, Yiming; Xu, Bin; Li, Lifei; Li, Bing

    2012-04-01

    The measurement of stress of concrete structures under impact loading and other strong dynamic loadings is crucial for the monitoring of health and damage detection. Due to its main advantages including availability, extremely high rigidity, high natural frequency, wide measuring range, high stability, high reproducibility, high linearity and wide operating temperature range, piezoelectric (Lead Zirconate Titanate, PZT) ceramic materials has been a widely used smart material for both sensing and actuation for monitoring and control in engineering structures. In this paper, a kind of stress sensor based on piezoelectric ceramics for impact stress measuring of concrete structures is developed. Because the PZT is fragile, in order to employ it for the health monitoring of concrete structures, special handling and treatment should be taken to protect the PZT and to make it survive and work properly in concrete. The commercially available PZT patch with lead wires is first applied with an insulation coating to prevent water and moisture damage, and then is packaged by jacketing it by two small precasted cylinder concrete blocks with enough strength to form a smart aggregate (SA). The employed PZT patch has a dimension of 10mm x 10mm x 0.3mm. In order to calibrate the PZT based stress sensor for impact stress measuring, a dropping hammer was designed and calibration test on the sensitivity of the proposed transducer was carried out with an industry charge amplifier. The voltage output of the stress sensor and the impact force under different free falling heights and impact mass were recorded with a high sampling rate data acquisition system. Based on the test measurements, the sensibility of the PZT based stress sensor was determined. Results show that the output of the PZT based stress sensor is proportional to the stress level and the repeatability of the measurement is very good. The self-made piezoelectric stress sensor can be easily embedded in concrete and provide

  17. Transverse piezoelectric coefficient measurement of flexible lead zirconate titanate thin films

    Energy Technology Data Exchange (ETDEWEB)

    Dufay, T.; Guiffard, B.; Seveno, R. [LUNAM Université, Université de Nantes, IETR (Institut d' Électronique et de Télécommunications de Rennes), UMR CNRS 6164, 2 rue de la Houssinière, BP 92208, 44322 Nantes Cedex 3 (France); Thomas, J.-C. [LUNAM Université, Université de Nantes-École Centrale Nantes, GeM (Institut de Recherche en Génie Civil et Ingénierie Mécanique), UMR CNRS 6183, 2 rue de la Houssinière, BP 92208, 44322 Nantes Cedex 3 (France)

    2015-05-28

    Highly flexible lead zirconate titanate, Pb(Zr,Ti)O{sub 3} (PZT), thin films have been realized by modified sol-gel process. The transverse piezoelectric coefficient d{sub 31} was determined from the tip displacement of bending-mode actuators made of PZT cantilever deposited onto bare or RuO{sub 2} coated aluminium substrate (16 μm thick). The influence of the thickness of ruthenium dioxide RuO{sub 2} and PZT layers was investigated for Pb(Zr{sub 0.57}Ti{sub 0.43})O{sub 3}. The modification of Zr/Ti ratio from 40/60 to 60/40 was done for 3 μm thick PZT thin films onto aluminium (Al) and Al/RuO{sub 2} substrates. A laser vibrometer was used to measure the beam displacement under controlled electric field. The experimental results were fitted in order to find the piezoelectric coefficient. Very large tip deflections of about 1 mm under low voltage (∼8 V) were measured for every cantilevers at the resonance frequency (∼180 Hz). For a given Zr/Ti ratio of 58/42, it was found that the addition of a 40 nm thick RuO{sub 2} interfacial layer between the aluminium substrate and the PZT layer induces a remarkable increase of the d{sub 31} coefficient by a factor of 2.7, thus corresponding to a maximal d{sub 31} value of 33 pC/N. These results make the recently developed PZT/Al thin films very attractive for both low frequency bending mode actuating applications and vibrating energy harvesting.

  18. Determination of temperature dependence of piezoelectric coefficients matrix of lead zirconate titanate ceramics by quasi-static and resonance method

    Energy Technology Data Exchange (ETDEWEB)

    Li Fei; Xu Zhuo; Wei Xiaoyong; Yao Xi, E-mail: lifei1216@gmail.co [Electronic Materials Research Laboratory, Key Laboratory of the Ministry of Education, Xi' an Jiaotong University, Xi' an 710049 (China)

    2009-05-07

    The piezoelectric coefficients (d{sub 33}, -d{sub 31}, d{sub 15}, g{sub 33}, -g{sub 31}, g{sub 15}) of soft and hard lead zirconate titanate ceramics were measured by the quasi-static and resonance methods, at temperatures from 20 to 300 {sup 0}C. The results showed that the piezoelectric coefficients d{sub 33}, -d{sub 31} and d{sub 15} obtained by these two methods increased with increasing temperature for both hard and soft PZT ceramics, while the piezoelectric coefficients g{sub 33}, -g{sub 31} and g{sub 15} decreased with increasing temperature for both hard and soft PZT ceramics. In this paper, the observed results were also discussed in terms of intrinsic and extrinsic contributions to piezoelectric response.

  19. Generation of electrical energy using lead zirconate titanate (PZT-5A) piezoelectric material: Analytical, numerical and experimental verifications

    Energy Technology Data Exchange (ETDEWEB)

    Butt, Zubair; Ahmad, Nasir [Dept. of Mechanical, Mechatronics and Manufacturing Engineering, UET Lahore, Faisalabad Campus, Lahore (Pakistan); Pasha, Riffat Asim; Qayyum, Faisal; Anjum, Zeeshan [Dept. of Mechanical Engineering, University of Engineering and Technology, Taxila (Pakistan); Elahi, Hassan [Northwestern Polytechnical University, Xian (China)

    2016-08-15

    Energy harvesting is the process of attaining energy from the external sources and transforming it into usable electrical energy. An analytical model of piezoelectric energy harvester has been developed to determine the output voltage across an electrical circuit when it is forced to undergo a base excitation. This model gives an easy approach to design and investigate the behavior of piezoelectric material. Numerical simulations have been carried out to determine the effect of frequency and loading on a Lead zirconate titanate (PZT-5A) piezoelectric material. It has been observed that the output voltage from the harvester increases when loading increases whereas its resonance frequency decreases. The analytical results were found to be in good agreement with the experimental and numerical simulation results.

  20. Fabrication and characterization of thick-film piezoelectric lead zirconate titanate ceramic resonators by tape-casting.

    Science.gov (United States)

    Qin, Lifeng; Sun, Yingying; Wang, Qing-Ming; Zhong, Youliang; Ou, Ming; Jiang, Zhishui; Tian, Wei

    2012-12-01

    In this paper, thick-film piezoelectric lead zirconate titanate (PZT) ceramic resonators with thicknesses down to tens of micrometers have been fabricated by tape-casting processing. PZT ceramic resonators with composition near the morphotropic phase boundary and with different dopants added were prepared for piezoelectric transducer applications. Material property characterization for these thick-film PZT resonators is essential for device design and applications. For the property characterization, a recently developed normalized electrical impedance spectrum method was used to determine the electromechanical coefficient and the complex piezoelectric, elastic, and dielectric coefficients from the electrical measurement of resonators using thick films. In this work, nine PZT thick-film resonators have been fabricated and characterized, and two different types of resonators, namely thickness longitudinal and transverse modes, were used for material property characterization. The results were compared with those determined by the IEEE standard method, and they agreed well. It was found that depending on the PZT formulation and dopants, the relative permittivities ε(T)(33)/ε(0) measured at 2 kHz for these thick-films are in the range of 1527 to 4829, piezoelectric stress constants (e(33) in the range of 15 to 26 C/m(2), piezoelectric strain constants (d(31)) in the range of -169 × 10(-12) C/N to -314 × 10(-12) C/N, electromechanical coupling coefficients (k(t)) in the range of 0.48 to 0.53, and k(31) in the range of 0.35 to 0.38. The characterization results shows tape-casting processing can be used to fabricate high-quality PZT thick-film resonators, and the extracted material constants can be used to for device design and application.

  1. Fabrication and energy harvesting characteristics of unimorph piezoelectric cantilever generators with interdigitated electrode lead zirconate titanate laminates

    Science.gov (United States)

    Lee, Min-seon; Yun, Ji-sun; Park, Woon-ik; Hong, Youn-woo; Cho, Jeong-ho; Paik, Jong-hoo; Park, Yong Ho; Son, Chun-myung; Jeong, Young Hun

    2017-12-01

    Interdigitated electrode (IDE) unimorph piezoelectric cantilever generators (UPCGs) were fabricated and their energy harvesting characteristics were investigated. A hard lead zirconate titanate (PZT) material with a high mechanical quality factor (Q m) of 1280 was used for the active piezoelectric film of the IDE UPCGs. Two different laminated IDE UPCGs were prepared; one has Ag/Pd interdigitated electrode (IDE) formed only on the top and bottom PZT sheets (D-IDE), while the other has Ag/Pd IDE on all of the PZT sheets (M-IDE). Cofiring was conducted at 1050 °C for 2 h for PZT laminates with IDEs. The fabricated IDE UPCGs exhibited power densities of 50.4 µW/cm3 for the D-IDE and 820 µW/cm3 for the M-IDE. The UPCG with the M-IDE exhibited a higher performance than that with the D-IDE. Specifically, a significantly enhanced normalized power factor of 670 µW/(g2·cm3) was found at 118 Hz across 100 kΩ.

  2. Pulsed laser deposition of piezoelectric lead zirconate titanate thin films maintaining a post-CMOS compatible thermal budget

    Science.gov (United States)

    Schatz, A.; Pantel, D.; Hanemann, T.

    2017-09-01

    Integration of lead zirconate titanate (Pb[Zrx,Ti1-x]O3 - PZT) thin films on complementary metal-oxide semiconductor substrates (CMOS) is difficult due to the usually high crystallization temperature of the piezoelectric perovskite PZT phase, which harms the CMOS circuits. In this work, a wafer-scale pulsed laser deposition tool was used to grow 1 μm thick PZT thin films on 150 mm diameter silicon wafers. Three different routes towards a post-CMOS compatible deposition process were investigated, maintaining a post-CMOS compatible thermal budget limit of 445 °C for 1 h (or 420 °C for 6 h). By crystallizing the perovskite LaNiO3 seed layer at 445 °C, the PZT deposition temperature can be lowered to below 400 °C, yielding a transverse piezoelectric coefficient e31,f of -9.3 C/m2. With the same procedure, applying a slightly higher PZT deposition temperature of 420 °C, an e31,f of -10.3 C/m2 can be reached. The low leakage current density of below 3 × 10-6 A/cm2 at 200 kV/cm allows for application of the post-CMOS compatible PZT thin films in low power micro-electro-mechanical-systems actuators.

  3. A Piezoelectric MEMS Microphone Based on Lead Zirconate Titanate (PZT) Thim Films

    National Research Council Canada - National Science Library

    Polcawich, Ronald

    2004-01-01

    .... A piezoelectric-based microphone can provide a solution to these requirements, since it offers the ability to passively sense without the power requirements of condenser or piezoresistive microphone counterparts...

  4. Strongly Enhanced Piezoelectric Response in Lead Zirconate Titanate Films with Vertically Aligned Columnar Grains

    Science.gov (United States)

    2017-01-01

    Pb(Zr0.52Ti0.48)O3 (PZT) films with (001) orientation were deposited on Pt(111)/Ti/SiO2/Si(100) substrates using pulsed laser deposition. Variation of the laser pulse rate during the deposition of the PZT films was found to play a key role in the control of the microstructure and to change strongly the piezoelectric response of the thin film. The film deposited at low pulse rate has a denser columnar microstructure, which improves the transverse piezoelectric coefficient (d31f) and ferroelectric remanent polarization (Pr), whereas the less densely packed columnar grains in the film deposited at high pulse rates give rise to a significantly higher longitudinal piezoelectric coefficient (d33f) value. The effect of film thickness on the ferroelectric and piezoelectric properties of the PZT films was also investigated. With increasing film thickness, the grain column diameter gradually increases, and also the average Pr and d33f values become larger. The largest piezoelectric coefficient of d33f = 408 pm V–1 was found for a 4-μm film thickness. From a series of films in the thickness range 0.5–5 μm, the z-position dependence of the piezoelectric coefficient could be deduced. A local maximum value of 600 pm V–1 was deduced in the 3.5–4.5 μm section of the thickest films. The dependence of the film properties on film thickness is attributed to the decreasing effect of the clamping constraint imposed by the substrate and the increasing spatial separation between the grains with increasing film thickness. PMID:28247756

  5. Contribution of the irreversible displacement of domain walls to the piezoelectric effect in barium titanate and lead zirconate titanate ceramics

    CERN Document Server

    Damjanovic, D

    1997-01-01

    The contribution from the irreversible displacement of non-180 deg domain walls to the direct longitudinal piezoelectric d sub 3 sub 3 coefficient of BaTiO sub 3 and Pb(Zr, Ti)O sub 3 ceramics was determined quantitatively by using the Rayleigh law. Effects of the crystal structure and microstructure of the ceramics as well as the external d.c. pressure on the domain wall contribution to d sub 3 sub 3 were examined. In barium titanate, this domain wall contribution is large (up to 35% of the total d sub 3 sub 3 , under the experimental conditions used) and dependent on the external d.c. pressure in coarse grained ceramics, and much smaller and independent of the external d.c. pressure in fine-grained samples. The presence of internal stresses in fine-grained ceramics could account for the observed behaviour. The analysis shows that the domain-wall contribution to the d sub 3 sub 3 in lead zirconate titanate ceramics is large in compositions close to the morphotropic phase boundary that contain a mixture of te...

  6. Pressure tuning of the morphotropic phase boundary in piezoelectric lead zirconate titanate

    International Nuclear Information System (INIS)

    Rouquette, J.; Haines, J.; Bornand, V.; Pintard, M.; Papet, Ph.; Bousquet, C.; Konczewicz, L.; Gorelli, F. A.; Hull, S.

    2004-01-01

    Titanium-rich PZT solid solutions were studied under high pressure by neutron and x-ray diffraction, Raman spectroscopy and dielectric measurements. The results show that high pressure stabilizes the ferroelectric monoclinic phases, which are proposed to be responsible for the high piezoelectric properties characteristic of the morphotropic composition PbZr 0.52 Ti 0.48 O 3 . Pressure may thus be used to tune the morphotropic phase boundary in the composition-pressure plane to include a wide range of titanium-rich PZT compositions

  7. Effect Of Electric Field Induced Texture On The Properties Of Piezoelectric Lead Zirconate Titanate

    International Nuclear Information System (INIS)

    Alkoy, S.

    2010-01-01

    Texturing a polycrystalline piezoelectric ceramic provide single-crystal like properties without experiencing any difficulties of single crystal growth process. This study reports a method to obtain texture in PbZr 0 .5Ti 0 .5O 3 ceramics by application of an electric field during gelation of a gelcast slurry. Gelcasting provides a means to lock the particles aligned under the application of a high electric field via gelation and this alignment in green body was retained after sintering. Monomer, cross linker and dispersant were dissolved in DI water and PZT powder was dispersed in this premix. Iniator and catalyzer were added to the slurry. An electric field was applied to the slurry for 30 min during gelation. XRD pattern of sintered samples indicates that PZT develops a tetragonal symmetry as a result of E-field applied during gelation. Dielectric constants and piezoelectric d 3 3 coefficients along and perpendicular to E-field are 1070 and 450 and 390 and 280 pC/N, respectively.

  8. Lead-free piezoelectric (K,Na)NbO3-based ceramic with planar-mode coupling coefficient comparable to that of conventional lead zirconate titanate

    Science.gov (United States)

    Ohbayashi, Kazushige; Matsuoka, Takayuki; Kitamura, Kazuaki; Yamada, Hideto; Hishida, Tomoko; Yamazaki, Masato

    2017-06-01

    We developed a (K,Na)NbO3-based lead-free piezoelectric ceramic with a KTiNbO5 system, (K1- x Na x )0.86Ca0.04Li0.02Nb0.85O3-δ-K0.85Ti0.85Nb1.15O5-BaZrO3-Fe2O3-MgO (K1- x N x N-NTK-FM). K1- x N x N-NTK-FM ceramic exhibits a very dense microstructure and a coupling coefficient of k p = 0.59, which is almost comparable to that of conventional lead zirconate titanate (PZT). The (K,Na)NbO3-based ceramic has the Γ15 mode for a wide x range. The nanodomains of orthorhombic (K,Na)NbO3 with the M3 mode coexist within the tetragonal Γ15 mode (K,Na)NbO3 matrix. Successive phase transition cannot occur with increasing x. The maximum k p is observed at approximately the minimum x required to generate the M3 mode phase. Unlike the behavior at the morphotropic phase boundary (MPB) in PZT, the characteristics of K1- x N x N-NTK-FM ceramic in this region changed moderately. This gentle phase transition seems to be a relaxor, although the diffuseness degree is not in line with this hypothesis. Furthermore, piezoelectric properties change from “soft” to “hard” upon the M3 mode phase aggregation.

  9. Electrophoretic growth of lead zirconate titanate nanorods

    Energy Technology Data Exchange (ETDEWEB)

    Limmer, S.J.; Seraji, S.; Forbess, M.J.; Wu Yun; Chou, T.P.; Nguyen, C.; Cao Guozhong [Washington Univ., Seattle, WA (United States). Dept. of Materials Science and Engineering

    2001-08-16

    Nanorods of lead zirconate titanate (PZT)-a ferro- and piezoelectric material-up to 10 {mu}m in length and 70 to 150 nm in diameter are produced by sol-gel electrophoresis of PZT in a track-etched polycarbonate membrane, which is used as a template. (orig.)

  10. Acoustic response of piezoelectric lead-zirconate-titanate to a 400MeV/n xenon beam

    CERN Document Server

    Miyachi, T; Ito, H

    2003-01-01

    Characteristics of lead-zirconate-titanate (PZT) elements were studied by directly irradiating them with a 400 MeV/n Xe beam. The elements were sensitive to 10 sup 4 Xe ions and their output amplitudes were proportional to the beam intensity. An ensemble of those output amplitudes displayed a Bragg-curve-like response towards the range of 400 MeV/n Xe ion. We discuss the potential of PZT elements as a radiation detector and their application to high-intensity and high-energy detectors. (author)

  11. Lead-Free Piezoelectrics

    CERN Document Server

    Nahm, Sahn

    2012-01-01

    Ecological restrictions in many parts of the world are demanding the elimination of Pb from all consumer items. At this moment in the piezoelectric ceramics industry, there is no issue of more importance than the transition to lead-free materials. The goal of Lead-Free Piezoelectrics is to provide a comprehensive overview of the fundamentals and developments in the field of lead-free materials and products to leading researchers in the world. The text presents chapters on demonstrated applications of the lead-free materials, which will allow readers to conceptualize the present possibilities and will be useful for both students and professionals conducting research on ferroelectrics, piezoelectrics, smart materials, lead-free materials, and a variety of applications including sensors, actuators, ultrasonic transducers and energy harvesters.

  12. Soft mode of lead zirconate

    International Nuclear Information System (INIS)

    Pan'ko, G.F.; Prisedskij, V.V.; Klimov, V.V.

    1983-01-01

    Anisotropic diffusional scattering of electrons on PbZrO 3 crystal in the temperature range of phase transition has been recorded. As a result of its analysis it has been established that in lead zirconate the rotational vibrational mode G 25 plays the role of soft mode. The experiment is carried out using PbZrO 3 monocrystals in translucent electron microscope EhM-200, operating in the regime of microdiffraction at accelerating voltage of 150 kV and beam current 50 μA; sample preparation is realized using the method of shearing and fragmentation

  13. Quantitative analysis method for niobium in lead zirconate titanate

    International Nuclear Information System (INIS)

    Hara, Hideo; Hashimoto, Toshio

    1986-01-01

    Lead zirconate titanate (PZT) is a strong dielectric ceramic having piezoelectric and pyroelectric properties, and is used most as a piezoelectric material. Also it is a main component of lead lanthanum zirconate titanate (PLZT), which is a typical electrical-optical conversion element. Since these have been developed, the various electronic parts utilizing the piezoelectric characteristics have been put in practical use. The characteristics can be set up by changing the composition of PZT and the kinds and amount of additives. Among the additives, niobium has the action to make metallic ion vacancy in crystals, and by the formation of this vacancy, to ease the movement of domain walls in crystal grains, and to increase resistivity. Accordingly, it is necessary to accurately determine the niobium content for the research and development, quality control and process control. The quantitative analysis methods for niobium used so far have respective demerits, therefore, the authors examined the quantitative analysis of niobium in PZT by using an inductively coupled plasma emission spectro-analysis apparatus which has remarkably developed recently. As the result, the method of dissolving a specimen with hydrochloric acid and hydrofluoric acid, and masking unstable lead with ethylene diamine tetraacetic acid 2 sodium and fluoride ions with boric acid was established. The apparatus, reagents, the experiment and the results are reported. (Kako, I.)

  14. Fractal cluster modeling of the fatigue behavior of lead zirconate titanate

    OpenAIRE

    Priya, Shashank; Kim, Hyeoung Woo; Ryu, Jungho; Uchino, Kenji; Viehland, Dwight D.

    2002-01-01

    The fatigue behavior of lead zirconate titanate ceramics (PZT) has been studied under electrical and mechanical drives. Piezoelectric fatigue was studied using a mechanical method. Under ac mechanical drive, hard and soft PZTs showed an increase in the longitudinal piezoelectric constant at short times, reaching a maximum at intermediate times. Systematic investigations were performed to characterize the electrical fatigue behavior. A decrease in the magnitude of the remanent polarization was...

  15. F-center mechanism of long-term relaxation in lead zirconate-titanate-based piezoelectric ceramics. 1. After-heating relaxation

    Directory of Open Access Journals (Sweden)

    V. M. Ishchuk

    2015-12-01

    The oxygen vacancies-based model for description of the long-time relaxation processes is suggested. The model takes into account oxygen vacancies on the sample’s surface ends, their conversion into F+- and F0-centers under external effects (due to the liberation of the pyroelectric charge and subsequent relaxation of these centers into the simple oxygen vacancies after the actions termination. The initial sample’s state is electroneutrality one. F-center formation leads to the violation of the original sample’s electroneutrality, and generates DC electric field into the sample. Relaxation of F-centers is accompanied by decreasing of electric field, induced by them, and dielectric constant relaxation as consequent effect.

  16. Development, Characterization and Piezoelectric Fatigue Behavior of Lead-Free Perovskite Piezoelectric Ceramics

    Science.gov (United States)

    Patterson, Eric Andrew

    Much recent research has focused on the development lead-free perovskite piezoelectrics as environmentally compatible alternatives to lead zirconate titanate (PZT). Two main categories of lead free perovskite piezoelectric ceramic systems were investigated as potential replacements to lead zirconate titanate (PZT) for actuator devices. First, solid solutions based on Li, Ta, and Sb modified (K0.5Na0.5)NbO3 (KNN) lead-free perovskite systems were created using standard solid state methods. Secondly, Bi-based materials a variety of compositions were explored for (1-x)(Bi 0.5Na0.5)TiO3-xBi(Zn0.5Ti0.5)O 3 (BNT-BZT) and Bi(Zn0.5Ti0.5)O3-(Bi 0.5K0.5)TiO3-(Bi0.5Na0.5)TiO 3 (BZT-BKT-BNT). It was shown that when BNT-BKT is combined with increasing concentrations of Bi(Zn1/2i1/2)O3 (BZT), a transition from normal ferroelectric behavior to a material with large electric field induced strains was observed. The higher BZT containing compositions are characterized by large hysteretic strains(> 0.3%) with no negative strains that might indicate domain switching. This work summarizes and analyzes the fatigue behavior of the new generation of Pb-free piezoelectric materials. In piezoelectric materials, fatigue is observed as a degradation in the electromechanical properties under the application of a bipolar or unipolar cyclic electrical load. In Pb-based materials such as lead zirconate titanate (PZT), fatigue has been studied in great depth for both bulk and thin film applications. In PZT, fatigue can result from microcracking or electrode effects (especially in thin films). Ultimately, however, it is electronic and ionic point defects that are the most influential mechanism. Therefore, this work also analyzes the fatigue characteristics of bulk polycrystalline ceramics of the modified-KNN and BNT-BKT-BZT compositions developed. The defect chemistry that underpins the fatigue behavior will be examined and the results will be compared to the existing body of work on PZT. It will

  17. Investigation of the effect of temperature on aging behavior of Fe-doped lead zirconate titanate

    Science.gov (United States)

    Promsawat, Napatporn; Promsawat, Methee; Janphuang, Pattanaphong; Marungsri, Boonruang; Luo, Zhenhua; Pojprapai, Soodkhet

    The aging degradation behavior of Fe-doped Lead zirconate titanate (PZT) subjected to different heat-treated temperatures was investigated over 1000h. The aging degradation in the piezoelectric properties of PZT was indicated by the decrease in piezoelectric charge coefficient, electric field-induced strain and remanent polarization. It was found that the aging degradation became more pronounced at temperature above 50% of the PZT’s Curie temperature. A mathematical model based on the linear logarithmic stretched exponential function was applied to explain the aging behavior. A qualitative aging model based on polar macrodomain switchability was proposed.

  18. Lead-free piezoelectric transducers for vibration-based energy harvesting devices

    Energy Technology Data Exchange (ETDEWEB)

    Roescher, Mark

    2011-11-15

    Future applications like piezoelectric energy harvesters in addition with increasing environmental awareness ultimately demand novel sophisticated material systems in the field of piezoelectrics as an alternative to the long-established system lead-zirconate-titanate. In this publication state-of-the-art microgenerators have been designed to possess nonlinear Duffing oscillator characteristics. It is shown by measurement and simulation that lead-zirconate-titanate may hence no longer be the first choice in material selection for a piezoelectric microgenerator. Polyvinylidene fluoride has been integrated in a piezoelectric microgenerator and identified as an extraordinarily promising material system for transducer applications being highly insusceptible to stretching induced material failure. Finally, a fundamentally new chemical synthesis approach has been developed for the fabrication of potassium-sodium-niobate films that may also be suitable for other complex oxides.

  19. Fracture mechanisms in lead zirconate titanate ceramics

    International Nuclear Information System (INIS)

    Freiman, S.W.; Chuck, L.; Mecholsky, J.J.; Shelleman, D.L.

    1986-01-01

    Lead Zirconate Titanate (PZT) ceramics can be formed over a wide range of PbTiO 3 /PbZrO 3 ratios and exist in a number of crystal structures. This study involved the use of various fracture mechanics techniques to determine critical fracture toughness, K /SUB IC/ , as a function of composition, microstructure, temperature, and electrical and thermal history. The results of these experiments indicate that variations in K /SUB IC/ are related to phase transformations in the material as well as to other toughening mechanisms such as twinning and microcracking. In addition, the strength and fracture toughness of selected PZT ceramics were determined using specimens in which a crack was introduced by a Vicker's hardness indentor. The variation of K /SUB IC/ with composition and microstructure was related to the extent of twin-crack interaction. Comparison of the plot of strength as a function of indentation load with that predicted from indentation fracture models indicates the presence of internal stresses which contribute to failure. The magnitude of these internal stresses has been correlated with electrical properties of the ceramic. Fractographic analysis was used to determine the magnitude of internal stresses in specimens failing from ''natural flaws.''

  20. Finite element analysis of vibration energy harvesting using lead-free piezoelectric materials: A comparative study

    Directory of Open Access Journals (Sweden)

    Anuruddh Kumar

    2014-06-01

    Full Text Available In this article, the performance of various piezoelectric materials is simulated for the unimorph cantilever-type piezoelectric energy harvester. The finite element method (FEM is used to model the piezolaminated unimorph cantilever structure. The first-order shear deformation theory (FSDT and linear piezoelectric theory are implemented in finite element simulations. The genetic algorithm (GA optimization approach is carried out to optimize the structural parameters of mechanical energy-based energy harvester for maximum power density and power output. The numerical simulation demonstrates the performance of lead-free piezoelectric materials in unimorph cantilever-based energy harvester. The lead-free piezoelectric material K0.5Na0.5NbO3-LiSbO3-CaTiO3 (2 wt.% has demonstrated maximum mean power and maximum mean power density for piezoelectric energy harvester in the ambient frequency range of 90–110 Hz. Overall, the lead-free piezoelectric materials of K0.5Na0.5NbO3-LiSbO3 (KNN-LS family have shown better performance than the conventional lead-based piezoelectric material lead zirconate titanate (PZT in the context of piezoelectric energy harvesting devices.

  1. Structural and electrical properties of Nd ion modified lead zirconate titanate nanopowders and ceramics

    International Nuclear Information System (INIS)

    Da-Wei, Wang; De-Qing, Zhang; Quan-Liang, Zhao; Hong-Mei, Liu; Zhi-Ying, Wang; Mao-Sheng, Cao; Jie, Yuan

    2009-01-01

    A modified sol-gel method is used for synthesizing Nd ion doped lead zirconate titanate nanopowders Pb 1–3x/2 Nd x Zr 0.52 Ti 0.48 O 3 (PNZT) in an ethylene glycol system with zirconium nitrate as zirconium source. The results show that it is critical to add lead acetate after the reaction of zirconium nitrate with tetrabutyl titanate in the ethylene glycol system for preparing PNZT with an exact fraction of titanium content. It has been observed that the dopant of excess Nd ions can effectively improve the sintered densification and activity of the PNZT ceramics. Piezoelectric, dielectric and ferroelectric properties of the PNZT ceramics are remarkably enhanced as compared with those of monolithic lead zirconate titanate (PZT). Especially, the supreme values of piezoelectric constant (d 33 ) and dielectric constant ( element of ) for the PNZT are both about two times that of the monolithic PZT and moreover, the remnant polarization (P r ) also increases by 30%. According to the analysis of the structures and properties, we attribute the improvement in electrical properties to the lead vacancies caused by the doping of Nd ions

  2. Fatigue responses of lead zirconate titanate stacks under semibipolar electric cycling with mechanical preload

    Science.gov (United States)

    Wang, Hong; Cooper, Thomas A.; Lin, Hua-Tay; Wereszczak, Andrew A.

    2010-10-01

    Lead zirconate titanate (PZT) stacks that had an interdigital internal electrode configuration were tested to more than 108 cycles. A 100 Hz semibipolar sine wave with a field range of +4.5/-0.9 kV/mm was used in cycling with a concurrently-applied 20 MPa preload. Significant reductions in piezoelectric and dielectric responses were observed during the cycling depending on the measuring condition. Extensive partial discharges were also observed. These surface events resulted in the erosion of external electrode and the exposure of internal electrodes. Sections prepared by sequential polishing technique revealed a variety of damage mechanisms including delaminations, pores, and etch grooves. The scale of damage was correlated with the degree of fatigue-induced reduction in piezoelectric and dielectric responses. The results from this study demonstrate the feasibility of using a semibipolar mode to drive a PZT stack under a mechanical preload and illustrate the potential fatigue and damages of the stack in service.

  3. Fatigue studies in compensated bulk lead zirconate titanate

    International Nuclear Information System (INIS)

    Verdier, Cyril; Morrison, Finlay D.; Lupascu, Doru C.; Scott, James F.

    2005-01-01

    Impedance analysis studies were carried out on compensated bulk lead zirconate titanate samples. Fatigue is concomitant with the onset of dielectric loss. This is shown to be dominantly due to an irreversibly modified near-surface layer that can be polished off. The highly compensated nature of these samples minimizes the role of oxygen vacancies

  4. Pyroelectricity versus conductivity in soft lead zirconate titanate (PZT) ceramics

    NARCIS (Netherlands)

    Kamel, T.M.; With, de G.

    2007-01-01

    The electrical behavior of modified soft lead zirconate titanate (PZT) ceramics has been studied as a function of temperature at different direct current (dc) electric fields and grain sizes. As ferroelectrics, such as PZT, are highly polarizable materials, poling, depolarization, and electric

  5. High Performance Lead--free Piezoelectric Materials

    OpenAIRE

    Gupta, Shashaank

    2013-01-01

    Piezoelectric materials find applications in number of devices requiring inter-conversion of mechanical and electrical energy.  These devices include different types of sensors, actuators and energy harvesting devices. A number of lead-based perovskite compositions (PZT, PMN-PT, PZN-PT etc.) have dominated the field in last few decades owing to their giant piezoresponse and convenient application relevant tunability. With increasing environmental concerns, in the last one decade, focus has be...

  6. On the use of non-MPB lead zirconium titanate (PZT) granules for piezoelectric ceramic–polymer sensorial composites

    NARCIS (Netherlands)

    Shaji Karapuzha, A.; Kunnamkuzhakkal James, N.; van der Zwaag, S.; Groen, W.A.

    2016-01-01

    Modern flexible and sensitive sensors based on polymer–ceramic composites employ lead zirconate titanate (PZT) granulates having the morphotropic phase boundary (MPB) composition as the piezo active ingredient, as this composition gives the best properties in fully ceramic piezoelectric sensors.

  7. On the use of non-MPB lead zirconium titanate (PZT) granules for piezoelectric ceramic–polymer sensorial composites

    NARCIS (Netherlands)

    Shaji Karapuzha, A.; Zwaag, S. van der; Groen, W.A.

    2016-01-01

    Modern flexible and sensitive sensors based on polymer–ceramic composites employ lead zirconate titanate (PZT) granulates having the morphotropic phase boundary (MPB) composition as the piezo active ingredient, as this composition gives the best properties in fully ceramic piezoelectric sensors. In

  8. Electronically droplet energy harvesting using piezoelectric cantilevers

    KAUST Repository

    Al Ahmad, Mahmoud Al; Jabbour, Ghassan E.

    2012-01-01

    A report is presented on free falling droplet energy harvesting using piezoelectric cantilevers. The harvester incorporates a multimorph clamped-free cantilever which is composed of five layers of lead zirconate titanate piezoelectric thick films

  9. Differential lead retention in zircons: implications for nuclear waste containment.

    Science.gov (United States)

    Gentry, R V; Sworski, T J; McKown, H S; Smith, D H; Eby, R E; Christie, W H

    1982-04-16

    An innovative ultrasensitive technique was used for lead isotopic analysis of individual zircons extracted from granite core samples at depths of 960, 2170, 2900, 3930, and 4310 meters. The results show that lead, a relatively mobile element compared to the nuclear waste-related actinides uranium and thorium, has been highly retained at elevated temperatures (105 degrees to 313 degrees C) under conditions relevant to the burial of synthetic rock waste containers in deep granite holes.

  10. Characterization and microstructure of porous lead zirconate titanate ...

    Indian Academy of Sciences (India)

    Unknown

    need to have porous piezoelectric materials. These can be made by combining a PZT ceramic with a passive polymer or air phase. These materials greatly extend the range of properties offered by conventional PZT ceramics. More- over, porosity in the materials could reduce the effective acoustical impedance leading to an ...

  11. Theoretical modeling of infrared spectra of twinned lead zirconate

    Czech Academy of Sciences Publication Activity Database

    Dočekalová, Zuzana; Pasciak, Marek; Hlinka, Jiří

    2017-01-01

    Roč. 90, č. 1 (2017), s. 17-23 ISSN 0141-1594 R&D Projects: GA ČR GA15-04121S Institutional support: RVO:68378271 Keywords : domains * IR spectroscopy * dielectric permittivity * lead zirconate * shell model * Born effective charge Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 1.060, year: 2016

  12. Microwave-assisted hydrothermal synthesis of lead zirconate fine powders

    Directory of Open Access Journals (Sweden)

    Apinpus Rujiwatra

    2011-01-01

    Full Text Available A rapid synthesis of lead zirconate fine powders by microwave-assisted hydrothermal technique is reported. The influences of type of lead precursor, concentration of potassium hydroxide mineraliser, applied microwave power and irradiation time are described. The synthesised powders were characterised by powder X-ray diffraction, field emission scanning electron microscopy, energy-dispersive X-ray spectroscopic microanalysis and light scattering technique. The merits of the microwave application in reducing reaction time and improving particle mono-dispersion and size uniformity as well as the drawbacks, viz. low purity of the desired phase and increasing demand of mineraliser, are discussed in relation to conventional heating method.

  13. Phase transformations in lead zirconate-titanate doped with lanthanum

    Energy Technology Data Exchange (ETDEWEB)

    Ishchuk, V M; Morozov, E M

    1979-07-01

    Presented are the results of studies on the character of phase transitions of the lead-lanthanum zirconate-titanate (LLZT) system. The replacement of lead by lanthanum leads to the expansion of the region of antisegnetoelectric (ASE) states of solid solutions of lead zirconate-titanate (LZT) in the direction of PbTiO/sub 3/ concentration growth. An intermediate region is revealed between segnetoelectric (SE) and ASE states, material properties in which depend on their prehistory: annealed samples are in the ASE state, whereas the application of electric field exceeding some critical value induces the SE state. A family of phase diagrams obtained at consequent replacement of lead by lanthanum permits to identify phase states in any series of LLZT with a constant ratio of Zr:Ti, in the x/65/35 series in particular. Thermally depolarized state of materials of this series at x<6.5 is shown to be antisegnetoelectric at all the temperatures below the Curie point Tsub(c), and heating causes phase transition of ASE..-->..PE (paraelectric state) at Tsub(c). Polarized samples being heated, a successiveness of phase transitions of SE..-->..ASE takes place at T/sub 0/, and that of ASE reversible PE at Tsub(C) (Tsub(0)..ASE phase transition in the LZT system.

  14. Substrate clamping effects on irreversible domain wall dynamics in lead zirconate titanate thin films.

    Science.gov (United States)

    Griggio, F; Jesse, S; Kumar, A; Ovchinnikov, O; Kim, H; Jackson, T N; Damjanovic, D; Kalinin, S V; Trolier-McKinstry, S

    2012-04-13

    The role of long-range strain interactions on domain wall dynamics is explored through macroscopic and local measurements of nonlinear behavior in mechanically clamped and released polycrystalline lead zirconate-titanate (PZT) films. Released films show a dramatic change in the global dielectric nonlinearity and its frequency dependence as a function of mechanical clamping. Furthermore, we observe a transition from strong clustering of the nonlinear response for the clamped case to almost uniform nonlinearity for the released film. This behavior is ascribed to increased mobility of domain walls. These results suggest the dominant role of collective strain interactions mediated by the local and global mechanical boundary conditions on the domain wall dynamics. The work presented in this Letter demonstrates that measurements on clamped films may considerably underestimate the piezoelectric coefficients and coupling constants of released structures used in microelectromechanical systems, energy harvesting systems, and microrobots.

  15. Dielectric behaviors of lead zirconate titanate ceramics with coplanar electrodes

    International Nuclear Information System (INIS)

    Wang, Y.; Cheng, Y.L.; Zhang, Y.W.; Chan, H.L.W.; Choy, C.L.

    2003-01-01

    This paper reports on the dielectric behaviors of lead zirconate titanate (PZT) capacitors with coplanar electrodes. Usually a ferroelectric device has a metal-ferroelectric-metal configuration (parallel plate capacitor); when both the electrodes are on one side of a ceramic to form a coplanar capacitor, different dielectric behaviors will be anticipated because of the change in the distribution of the test field inside the dielectrics. This paper describes how the capacitance and dielectric loss of PZT-based coplanar capacitors change with electrode distance, area and test frequency

  16. Potassium Sodium Niobate-Based Lead-Free Piezoelectric Multilayer Ceramics Co-Fired with Nickel Electrodes

    Directory of Open Access Journals (Sweden)

    Shinichiro Kawada

    2015-11-01

    Full Text Available Although lead-free piezoelectric ceramics have been extensively studied, many problems must still be overcome before they are suitable for practical use. One of the main problems is fabricating a multilayer structure, and one solution attracting growing interest is the use of lead-free multilayer piezoelectric ceramics. The paper reviews work that has been done by the authors on lead-free alkali niobate-based multilayer piezoelectric ceramics co-fired with nickel inner electrodes. Nickel inner electrodes have many advantages, such as high electromigration resistance, high interfacial strength with ceramics, and greater cost effectiveness than silver palladium inner electrodes. However, widely used lead zirconate titanate-based ceramics cannot be co-fired with nickel inner electrodes, and silver palladium inner electrodes are usually used for lead zirconate titanate-based piezoelectric ceramics. A possible alternative is lead-free ceramics co-fired with nickel inner electrodes. We have thus been developing lead-free alkali niobate-based multilayer ceramics co-fired with nickel inner electrodes. The normalized electric-field-induced thickness strain (Smax/Emax of a representative alkali niobate-based multilayer ceramic structure with nickel inner electrodes was 360 pm/V, where Smax denotes the maximum strain and Emax denotes the maximum electric field. This value is about half that for the lead zirconate titanate-based ceramics that are widely used. However, a comparable value can be obtained by stacking more ceramic layers with smaller thicknesses. In the paper, the compositional design and process used to co-fire lead-free ceramics with nickel inner electrodes are introduced, and their piezoelectric properties and reliabilities are shown. Recent advances are introduced, and future development is discussed.

  17. Review and Perspectives of Aurivillius Structures as a Lead-Free Piezoelectric System

    Directory of Open Access Journals (Sweden)

    Alberto Moure

    2018-01-01

    Full Text Available According to the EU-Directives 2002/95/EC, 2002/96/EC, lead-based piezoceramics must be substituted in the future with more environmentally friendly alternatives, only when a reliable alternative is found. This is why an increasing interest has grown in the research community to find lead free piezoelectric materials that fulfil the requirements for this substitution. Different families of compounds have been shown to be possible candidates for this use, such as bismuth and niobates based perovskites, pyrochlores, etc. However, a material with piezoelectric coefficients similar to those of PZT (lead zirconate titanate, Pb[ZrxTi1-x]O3 has not been yet found. Besides, each of these families has its specific characteristics in terms of remnant polarization, coercive field or application temperature. Thus, the choice of each material should be made according to the specific needs of the application. In this sense, Aurivillius-type structure materials (also known as Bismuth Layered Structure Ferroelectrics, BLSF can take advantage of their specific properties for uses as Lead Free Piezoelectric systems. Some of them have a high Curie temperature, which make them good candidates to be used as high temperature piezoelectrics; high coercive fields, which facilitates their use as actuators; or a high switching fatigue resistance, which can be useful for future applications as Ferroelectric Random Access Memories (FERAM.

  18. Preparation of lead titanate zirconate from metal citrates

    International Nuclear Information System (INIS)

    Bastos, C.M.R.

    1994-01-01

    Lead titanate zirconate (PZT) preparation from its metal constituent citrates have been investigated. Metal citrates were obtained by forced precipitation using a dehydration alcohol mixture. Salt solutions of lead nitrate and octahydrated zirconyl chloride, and titanium tetrachloride were treated separately with citric acid and ammonium hydroxide. Zirconium, titanium and lead oxides resulted from thermal decomposition of corresponding citrates at 500 0 C, 450 0 C and 250 0 C, respectively. Lead titanate (PT) and lead zirconate (P Z) were obtained by calcining at 450 0 C and 500 0 C, respectively, after adequate heating of citrates mechanically mixed in ethyl ether. PZT samples were obtained with different starting stoichiometry. Rhombohedral PZT-1 53/47 sample was prepared from co precipitating zirconyl ammonium and ammonium lead citrates in presence of ethanolic titanium oxide dispersion, and calcinating at 800 0 C. Rhombohedral PZT-q 52/48 sample was obtained from heating at 500 0 C for 2 hours a mixture of metal citrates coprecipitated by dehydration mixture of acetone-ethanol-formic acid (2:1:0,06). Tetragonal PZT-m stoichiometry 53/47 sample were obtained by calcining at after 600 0 C for 2 hours after heating a mechanically mixed metal citrates. PT phase arose at 400 0 C. PZT-m powders obtained in a range of 400 0 C-800 0 C were isostatically pressed, and sintered at 1100 0 C and 1200 0 C in saturated Pb O atmosphere. Rhombohedral sintered PZT was obtained with 7,78 g.cm -3 at 1200 0 C. (author). 123 refs, 53 figs, 32 tabs

  19. Two-stage model of development of heterogeneous uranium-lead systems in zircon

    International Nuclear Information System (INIS)

    Mel'nikov, N.N.; Zevchenkov, O.A.

    1985-01-01

    Behaviour of isotope systems of multiphase zircons at their two-stage distortion is considered. The results of calculations testify to the fact that linear correlations on the diagram with concordance can be explained including two-stage discovery of U-Pb systems of cogenetic zircons if zircon is considered physically heterogeneous and losing in its different part different ratios of accumulated radiogenic lead. ''Metamorphism ages'' obtained by these two-stage opening zircons are intermediate, and they not have geochronological significance while ''crystallization ages'' remain rather close to real ones. Two-stage opening zircons in some cases can be diagnosed by discordance of their crystal component

  20. Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

    International Nuclear Information System (INIS)

    Wang, Hong; Lee, Sung-Min; Wang, James L.; Lin, Hua-Tay

    2014-01-01

    Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10 8 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines

  1. Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

    Science.gov (United States)

    Wang, Hong; Lee, Sung-Min; Wang, James L.; Lin, Hua-Tay

    2014-12-01

    Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 108 cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines.

  2. Fatigue of extracted lead zirconate titanate multilayer actuators under unipolar high field electric cycling

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hong, E-mail: wangh@ornl.gov; Lee, Sung-Min; Wang, James L. [Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831 (United States); Lin, Hua-Tay [School of Mechanical and Electronic Engineering, Guangdong University of Technology, Guangzhou, 510006 (China)

    2014-12-21

    Testing of large prototype lead zirconate titanate (PZT) stacks presents substantial technical challenges to electronic testing systems, so an alternative approach that uses subunits extracted from prototypes has been pursued. Extracted 10-layer and 20-layer plate specimens were subjected to an electric cycle test under an electric field of 3.0/0.0 kV/mm, 100 Hz to 10{sup 8} cycles. The effects of measurement field level and stack size (number of PZT layers) on the fatigue responses of piezoelectric and dielectric coefficients were observed. On-line monitoring permitted examination of the fatigue response of the PZT stacks. The fatigue rate (based on on-line monitoring) and the fatigue index (based on the conductance spectrum from impedance measurement or small signal measurement) were developed to quantify the fatigue status of the PZT stacks. The controlling fatigue mechanism was analyzed against the fatigue observations. The data presented can serve as input to design optimization of PZT stacks and to operation optimization in critical applications, such as piezoelectric fuel injectors in heavy-duty diesel engines.

  3. Progress in engineering high strain lead-free piezoelectric ceramics

    International Nuclear Information System (INIS)

    Leontsev, Serhiy O; Eitel, Richard E

    2010-01-01

    Environmental concerns are strongly driving the need to replace the lead-based piezoelectric materials currently employed as multilayer actuators. The current review describes both compositional and structural engineering approaches to achieve enhanced piezoelectric properties in lead-free materials. The review of the compositional engineering approach focuses on compositional tuning of the properties and phase behavior in three promising families of lead-free perovskite ferroelectrics: the titanate, alkaline niobate and bismuth perovskites and their solid solutions. The 'structural engineering' approaches focus instead on optimization of microstructural features including grain size, grain orientation or texture, ferroelectric domain size and electrical bias field as potential paths to induce large piezoelectric properties in lead-free piezoceramics. It is suggested that a combination of both compositional and novel structural engineering approaches will be required in order to realize viable lead-free alternatives to current lead-based materials for piezoelectric actuator applications. (topical review)

  4. Progress in engineering high strain lead-free piezoelectric ceramics

    Science.gov (United States)

    Leontsev, Serhiy O; Eitel, Richard E

    2010-01-01

    Environmental concerns are strongly driving the need to replace the lead-based piezoelectric materials currently employed as multilayer actuators. The current review describes both compositional and structural engineering approaches to achieve enhanced piezoelectric properties in lead-free materials. The review of the compositional engineering approach focuses on compositional tuning of the properties and phase behavior in three promising families of lead-free perovskite ferroelectrics: the titanate, alkaline niobate and bismuth perovskites and their solid solutions. The ‘structural engineering’ approaches focus instead on optimization of microstructural features including grain size, grain orientation or texture, ferroelectric domain size and electrical bias field as potential paths to induce large piezoelectric properties in lead-free piezoceramics. It is suggested that a combination of both compositional and novel structural engineering approaches will be required in order to realize viable lead-free alternatives to current lead-based materials for piezoelectric actuator applications. PMID:27877343

  5. Mechanical and dielectric characterization of lead zirconate titanate(PZT)/polyurethane(PU) thin film composite for energy harvesting

    Science.gov (United States)

    Aboubakr, S.; Rguiti, M.; Hajjaji, A.; Eddiai, A.; Courtois, C.; d'Astorg, S.

    2014-04-01

    The Lead Zirconate titanate (PZT) ceramic is known by its piezoelectric feature, but also by its stiffness, the use of a composite based on a polyurethane (PU) matrix charged by a piezoelectric material, enable to generate a large deformation of the material, therefore harvesting more energy. This new material will provide a competitive alternative and low cost manufacturing technology of autonomous systems (smart clothes, car seat, boat sail, flag ...). A thin film of the PZT/PU composite was prepared using up to 80 vol. % of ceramic. Due to the dielectric nature of the PZT, inclusions of this one in a PU matrix raises the permittivity of the composite, on other hand this latter seems to decline at high frequencies.

  6. Lead zirconate titanate nanoscale patterning by ultraviolet-based lithography lift-off technique for nano-electromechanical system applications.

    Science.gov (United States)

    Guillon, Samuel; Saya, Daisuke; Mazenq, Laurent; Costecalde, Jean; Rèmiens, Denis; Soyer, Caroline; Nicu, Liviu

    2012-09-01

    The advantage of using lead zirconate titanate (PbZr(0.54)Ti(0.46)O(3)) ceramics as an active material in nanoelectromechanical systems (NEMS) comes from its relatively high piezoelectric coefficients. However, its integration within a technological process is limited by the difficulty of structuring this material with submicrometer resolution at the wafer scale. In this work, we develop a specific patterning method based on optical lithography coupled with a dual-layer resist process. The main objective is to obtain sub-micrometer features by lifting off a 100-nm-thick PZT layer while preserving the material's piezoelectric properties. A subsequent result of the developed method is the ability to stack several layers with a lateral resolution of few tens of nanometers, which is mandatory for the fabrication of NEMS with integrated actuation and read-out capabilities.

  7. Ferroelastic domain switching fatigue in lead zirconate titanate ceramics

    International Nuclear Information System (INIS)

    Pojprapai, Soodkhet; Jones, Jacob L.; Studer, Andrew J.; Russell, Jennifer; Valanoor, Nagarajan; Hoffman, Mark

    2008-01-01

    The influence of the frequency and amplitude of cyclic mechanical loading on soft, tetragonal lead zirconate titanate (PZT) ceramics was investigated via neutron diffraction. Intensity change in the {2 0 0} reflections provided quantitative measurements of domain switching behavior, domain texture and the strain resulting from domain switching. The results are explained using a viscoelasticity model. It was found that the magnitude of applied stress affects the level of strain accumulated, while its frequency affects the time taken for the strain to reach saturation. Furthermore, markedly different behaviors are exhibited by poled and unpoled samples. For samples loaded under identical conditions, the frequency effect is more pronounced in unpoled samples and the accumulated ferroelastic strain is greater in poled samples

  8. Ferroelectric devices using lead zirconate titanate (PZT) nanoparticles.

    Science.gov (United States)

    Paik, Young Hun; Kojori, Hossein Shokri; Kim, Sung Jin

    2016-02-19

    We successfully demonstrate the synthesis of lead zirconate titanate nanoparticles (PZT NPs) and a ferroelectric device using the synthesized PZT NPs. The crystalline structure and the size of the nanocrystals are studied using x-ray diffraction and transmission electron microscopy, respectively. We observe PZT NPs and this result matches dynamic light scattering measurements. A solution-based low-temperature process is used to fabricate PZT NP-based devices on an indium tin oxide substrate. The fabricated ferroelectric devices are characterized using various optical and electrical measurements and we verify ferroelectric properties including ferroelectric hysteresis and the ferroelectric photovoltaic effect. Our approach enables low-temperature solution-based processes that could be used for various applications. To the best of our knowledge, this low-temperature solution processed ferroelectric device using PZT NPs is the first successful demonstration of its kind.

  9. New phase transitions in lead zirconate-titanate

    International Nuclear Information System (INIS)

    Ishchuk, V.M.; Morozov, E.M.; Klimov, V.V.

    1977-01-01

    Processes of disordering are considered in the paraelectric phase of lead zirconate-titanate. Te investigations were carried out on poly- and single-crystal specimens of the composition PbZrsub(1-x)Tisub(x)O 3 (0< x(<=)0.5). The results are presented of measurements of the temperature dependence of the dielectric constant and the dependence of the polarization on the temperature and the electric field. Anomaly is observed of the investigated characteristics above the Curie point due to a first-type phase transition. The results are interpreted within the framework of the model proposed by Coms, Lambert, and Guiniot, according to which this transition is due to the disordering of chains of unit cells existing above the Curie point

  10. Characterisation of glass matrix composites reinforced with lead zirconate titanate particles

    International Nuclear Information System (INIS)

    Cannillo, Valeria; Manfredini, Tiziano; Montorsi, Monia; Tavoni, Francesca; Minay, Emma J.; Boccaccini, Aldo R.

    2005-01-01

    A new type of glass matrix composite reinforced with ferroelectric particulate secondary phase was investigated. Samples containing lead zirconate titanate (PZT) particles in a silicate lead glass were fabricated. Various sintering strategies were tested in order to optimise the processing route. The densest samples were obtained by hot-pressing. The composites were characterized by means of SEM observations, X-ray diffraction, differential thermal analysis and Vickers indentations. In order to get a deeper insight into the thermo-mechanical behaviour of the material, a FEM based numerical model was prepared and applied. In particular, the crack-particle interaction was assessed and thus possible toughening mechanisms were investigated. By means of the numerical modelling supported by SEM observations, traditional toughening mechanisms (e.g. crack deflection, particle debonding) were ruled out. Since the experimentally measured indentation fracture toughness of the composite is significantly higher than that of the unreinforced glass, the findings suggest that a new toughening mechanism may be active, based on the piezoelectric effect

  11. LEAD-FREE BNKT PIEZOELECTRIC ACTUATOR

    Directory of Open Access Journals (Sweden)

    A. Moosavi

    2016-03-01

    Full Text Available An actuator is a device that converts input energy into mechanical energy. According to various types of input energy, various actuators have been advanced. Displacement in the electromagnetic, hydraulic and pneumatic actuators achieve by moving a piston via electromagnetic force or pressure, however the piezoelectric actuator (piezoceramic plates displace directly. Therefore, accuracy and speed in the piezoelectric device are higher than other types of actuators. In the present work, the high-field electromechanical response of high-quality (1−x(Bi 0.5Na0.5TiO3–x(Bi0.5K0.5TiO3 samples abbreviated to BNKTx with x = 0.18, 0.20, 0.22 and 0.24 ceramic materials across its MPB was investigated. The piezoelectrics and actuation characteristics were characterized. Ourresults indicate that x = 0.20, indeed, constitutes the best choice for the MPB composition in the system. Maximum of remanent polarization (37.5 μC cm−2 was obtained for x=0.20. High-field electromechanical responses were also obtained for BNKT0.20 samples. This material exhibited giant field induced strains of 0.13% under 1 kV mm -1 at room temperature.

  12. Improvement of conditions for ceramics sintering on the base of lead zirconate-titanate

    International Nuclear Information System (INIS)

    Glinchuk, M.D.; Kim, P.V.; Bykov, I.P.; Lyashchenko, A.B.

    1989-01-01

    Lead zirconate-titanate powders of different graininess are studied for their phase composition. The finest grains of the powder consist of lead zirconate-titanate with the rhombohedral structure. Grains of 3-5 μm size are a mixture of lead zirconate-titanate and lead titanate, the latter exceeding 50% (by weight) causes the effect of anomalous expansion in the process of sintering. Control of the technological parameters of the synthesis permits producing powder with favourable correlation of the above phases and grain sizes. Sintering of such a powder induces no effect of the anomalous expansion with an increased density of the product attained

  13. Molten salt synthesis of lead lanthanum zirconate titanate ceramic powders

    International Nuclear Information System (INIS)

    Cai Zongying; Xing Xianran; Li Lu; Xu Yeming

    2008-01-01

    Lead lanthanum zirconate titanate (Pb 0.95 La 0.03 )(Zr 0.52 Ti 0.48 )O 3 (PLZT) was synthesized by one step molten salt method with the starting materials of PbC 2 O 4 , La 2 O 3 , ZrO(NO 3 ) 2 .2H 2 O and TiO 2 in the NaCl-KCl eutectic mixtures in the temperature range of 700-1000 deg. C. The single phase of (Pb 0.95 La 0.03 )(Zr 0.52 Ti 0.48 )O 3 powders was prepared at a temperature as low as 850 deg. C for 5 h. The effects of process parameters, such as soaking temperature and time, salt species, and the amount of flux with respect to the starting materials were investigated. The growth process of the PLZT particles in the molten salt undergoes a transition from a diffusion controlled mechanism to an interfacial reaction controlled mechanism at 900 deg. C

  14. Non-aqueous electrochemical deposition of lead zirconate titanate films for flexible sensor applications

    Science.gov (United States)

    Joseph, Sherin; Kumar, A. V. Ramesh; John, Reji

    2017-11-01

    Lead zirconate titanate (PZT) is one of the most important piezoelectric materials widely used for underwater sensors. However, PZTs are hard and non-compliant and hence there is an overwhelming attention devoted toward making it flexible by preparing films on flexible substrates by different routes. In this work, the electrochemical deposition of composition controlled PZT films over flexible stainless steel (SS) foil substrates using non-aqueous electrolyte dimethyl sulphoxide (DMSO) was carried out. Effects of various key parameters involved in electrochemical deposition process such as current density and time of deposition were studied. It was found that a current density of 25 mA/cm2 for 5 min gave a good film. The morphology and topography evaluation of the films was carried out by scanning electron microscopy (SEM) and atomic force microscopy (AFM), respectively, which showed a uniform morphology with a surface roughness of 2 nm. The PZT phase formation was studied using X-ray diffraction (XRD) and corroborated with Raman spectroscopic studies. The dielectric constant, dielectric loss, hysteresis and I-V characteristics of the film was evaluated.

  15. Dynamic magnetoelectric effects in bulk and layered composites of cobalt zinc ferrite and lead zirconate titanate

    Energy Technology Data Exchange (ETDEWEB)

    Srinivasan, G.; Hayes, R.; DeVreugd, C.P. [Oakland University, Physics Department, Rochester, MI (United States); Laletsin, V.M.; Paddubnaya, N. [National Academy of Sciences, Institute of Technical Acoustics, Vitebsk (Belarus)

    2005-02-01

    Low-frequency magnetoelectric (ME) coupling is investigated in bulk samples and multilayers of cobalt zinc ferrite, Co{sub 1-x}Zn{sub x}Fe{sub 2}O{sub 4} (x=0-0.6), and lead zirconate titanate. In bulk samples, the transverse and longitudinal couplings are weak and of equal magnitude. A substantial strengthening of ME interactions is evident in layered structures, with the ME voltage coefficient a factor of 10-30 higher than in bulk samples. Important findings of our studies of layered composites are as follows. (i) The transverse coupling is stronger than the longitudinal coupling. (ii) The strength of ME interactions is dependent on Zn substitution, with a maximum for x=0.4. (iii) A weak coupling exists at the ferromagnetic-piezoelectric interface, as revealed by an analysis of the volume and static magnetic field dependence of ME voltage coefficients. (iv) The interface coupling k increases with Zn substitution and the k versus x profile shows a maximum centered at x=0.4. (v) The Zn-assisted enhancement can be attributed to efficient magneto-mechanical coupling in the ferrite. (orig.)

  16. Current—voltage characteristics of lead zirconate titanate/nickel bilayered hollow cylindrical magnetoelectric composites

    International Nuclear Information System (INIS)

    De-An, Pan; Shen-Gen, Zhang; Jian-Jun, Tian; Li-Jie, Qiao; Jun-Sai, Sun; Volinsky, Alex A.

    2010-01-01

    Current–voltage measurements obtained from lead zirconate titanate/nickel bilayered hollow cylindrical magnetoelectric composite showed that a sinusoidal current applied to the copper coil wrapped around the hollow cylinder circumference induces voltage across the lead zirconate titanate layer thickness. The current–voltage coefficient and the maximum induced voltage in lead zirconate titanate at 1 kHz and resonance (60.1 kHz) frequencies increased linearly with the number of the coil turns and the applied current. The resonance frequency corresponds to the electromechanical resonance frequency. The current–voltage coefficient can be significantly improved by optimizing the magnetoelectric structure geometry and/or increasing the number of coil turns. Hollow cylindrical lead zirconate titanate/nickel structures can be potentially used as current sensors. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  17. Real-Time Salmonella Detection Using Lead Zirconate Titanate-Titanium Microcantilevers

    National Research Council Canada - National Science Library

    McGovern, John-Paul; Shih, Wan Y; Shih, Wei-Heng; Sergi, Mauro; Chaiken, Irwin

    2005-01-01

    .... We have developed and investigated the use of a lead zirconate titanate - titanium (PZT-Ti) microcantilever for in situ detection of the common food- and water-born pathogen, Salmonella typhimurium...

  18. Structure and high-piezoelectricity in lead oxide solid solutions

    NARCIS (Netherlands)

    Noheda, B.

    2002-01-01

    A review of the recent advances in the understanding of piezoelectricity in lead oxide solid solutions is presented, giving special attention to the structural aspects. It has now become clear that the very high electromechanical response in these materials is directly related to the existence of

  19. Metalorganic solution deposition of lead zirconate titanate films onto an additively manufactured Ni-based superalloy

    International Nuclear Information System (INIS)

    Patel, T.; Khassaf, H.; Vijayan, S.; Bassiri-Gharb, N.; Aindow, M.; Alpay, S.P.; Hebert, R.J.

    2017-01-01

    Recent advances in additive manufacturing of high-temperature alloys for structural aerospace applications has led to interest in integrating additional functionality into such parts. Lead zirconate titanate (PZT) is a prototypical ferroelectric ceramic used as the electro-active material in many piezoelectric sensors and actuators. In this study, 300 nm thick PbZr_0_._2Ti_0_._8O_3 (PZT 20/80) films were grown using metalorganic solution deposition onto additively manufactured substrates of Inconel 718. The microstructures of the films and the nature of the film/substrate interfaces were characterized using a combination of X-ray diffraction and electron microscopy techniques. Electrical measurements were performed to determine the ferroelectric, dielectric, and conductive responses of the PZT films. Our findings show that the PZT films exhibit robust ferroelectricity characterized by well-defined polarization-applied electric field (P-E) hysteresis loops. The samples display internal bias of up to ∼40 kV/cm. The room temperature remnant polarization and the small signal dielectric permittivity are ∼70 μC/cm"2 and 205, respectively. The dielectric loss (tan δ) and the leakage current at 1 kHz are 9% and 1 nA at 1 V, respectively. We attribute the internal bias observed in the hysteresis loops and the overall large dielectric losses to the presence of an intermediate oxide layer at the PZT/Inconel interface, which forms during the high temperature crystallization of the ferroelectric film. These results show that it is possible to grow functional oxides with promising electrical properties onto additively manufactured metallic substrates.

  20. Dielectric and electrical properties of gadolinium-modified lead-zirconate-titanate system

    International Nuclear Information System (INIS)

    Panigrahi, S.C.; Das, Piyush R.; Parida, B.N.; Padhee, R.; Choudhary, R.N.P.

    2014-01-01

    Highlights: • Gadolinium modified PZT have very good dielectric and ferroelectric properties. • The impedance analysis of shows grain and grain boundary phenomena. • Electrical properties of the compounds show very good transport properties. • Piezoelectric coefficient of the samples have higher values. - Abstract: The gadolinium (Gd) modified lead zirconate titanate (PbZr,TiO 3 ) ceramics with Zr/Ti = 48/52 (i.e., near morphotropic phase boundary (MPB)) in a general chemical formula Pb 1−x Gd x (Zr 0.48 Ti 0.52 ) 1−x/4 O 3 (PGZT; x = 0, 0.07, 0.10 and 0.12) have been synthesized using a high-temperature solid-state reaction method. Preliminary structural analysis using X-ray powder diffraction (XRD) shows the formation of a single-phase tetragonal structure of the compounds. Detailed studies of dielectric parameters of PGZT exhibit the diffuse phase transition but non-relaxor characteristics in the material for the higher concentration of gadolinium. The ac conductivity spectra of PGZT are found to obey Jonscher’s universal power law. The electrical impedance parameters of PGZT (near MPB) were obtained in a wide range of temperature (25–500 °C) and frequency (1–1000 kHz) using complex impedance spectroscopy (CIS) technique. Detailed analysis of these parameters shows that bulk (grain) and grain boundary resistance have significant effect on the total impedance of the materials. Temperature dependence of hysteresis characteristics of PGZT confirms that the phase transition parameter of the material is strongly affected by the substitution of Gd at the Pb-sites

  1. Piezoelectric Active Humidity Sensors Based on Lead-Free NaNbO3 Piezoelectric Nanofibers

    Directory of Open Access Journals (Sweden)

    Li Gu

    2016-06-01

    Full Text Available The development of micro-/nano-scaled energy harvesters and the self-powered sensor system has attracted great attention due to the miniaturization and integration of the micro-device. In this work, lead-free NaNbO3 piezoelectric nanofibers with a monoclinic perovskite structure were synthesized by the far-field electrospinning method. The flexible active humidity sensors were fabricated by transferring the nanofibers from silicon to a soft polymer substrate. The sensors exhibited outstanding piezoelectric energy-harvesting performance with output voltage up to 2 V during the vibration process. The output voltage generated by the NaNbO3 sensors exhibited a negative correlation with the environmental humidity varying from 5% to 80%, where the peak-to-peak value of the output voltage generated by the sensors decreased from 0.40 to 0.07 V. The sensor also exhibited a short response time, good selectively against ethanol steam, and great temperature stability. The piezoelectric active humidity sensing property could be attributed to the increased leakage current in the NaNbO3 nanofibers, which was generated due to proton hopping among the H3O+ groups in the absorbed H2O layers under the driving force of the piezoelectric potential.

  2. Elution of lead from lead zirconate titanate ceramics to acid rain

    Science.gov (United States)

    Tsurumi, Takaaki; Takezawa, Shuhei; Hoshina, Takuya; Takeda, Hiroaki

    2017-10-01

    The amount of lead that eluted from lead zirconate titanate (PZT) ceramics to artificial acid rain was evaluated. Four kinds of PZT ceramics, namely, pure PZT at MPB composition, CuO-added PZT, PZT with 10 mol % substitution of Ba for Pb, and CuO-added PZT with 10 mol % substitution of Ba for Pb, were used as samples of the elution test. These PZT ceramics of 8 mm2 and 1.1-1.2 mm thickness were suspended in 300 ml of H2SO4 solution of pH 4.0. The concentration of lead eluted from PZT was in the range from 0.2 to 0.8 ppm. It was found that both liquid phase formation by the addition of CuO and the substitution of Ba for Pb were effective to reduce the amount of lead that eluted. By fitting the leaching out curve with a classical equation, a master curve assuming no sampling effect was obtained. The lead concentration evaluated from the amount of lead that eluted from a commercial PZT plate to H2SO4 solution of pH 5.3 was almost the same as the limit in city water. It is concluded that PZT is not harmful to health and the environment and the amount of lead that eluted from PZT can be controlled by modifying PZT composition.

  3. Piezoelectric Ceramics Characterization

    National Research Council Canada - National Science Library

    Jordan, T

    2001-01-01

    ... the behavior of a piezoelectric material. We have attempted to cover the most common measurement methods as well as introduce parameters of interest. Excellent sources for more in-depth coverage of specific topics can be found in the bibliography. In most cases, we refer to lead zirconate titanate (PZT) to illustrate some of the concepts since it is the most widely used and studied piezoelectric ceramic to date.

  4. Experimental Determination of Effect of Variable Resistance on Lead ZirconateTitanate (PZT-5A4Eunder various Thermal and Frequency Conditions

    Directory of Open Access Journals (Sweden)

    Hassan Elahi

    2014-12-01

    Full Text Available A specially designed apparatus and circuit working on the principle of inverse piezoelectricity due to the effect of polarization was used to find the relationship between resistance and peak to peak voltage of Lead Zirconate Titanate (PZT-5A4E by shocking it at variable frequencies and at variable resistances under various thermal conditions within Curie temperature limit using equivalent circuit method. It was found that by increasing temperature, peak to peak voltage increases and similarly by increasing frequency, peak to peak voltage decreases and with the increase in resistance peak to peak voltage decreases.

  5. Effect of multi-layered bottom electrodes on the orientation of strontium-doped lead zirconate titanate thin films

    Energy Technology Data Exchange (ETDEWEB)

    Bhaskaran, M. [Microelectronics and Materials Technology Centre, School of Electrical and Computer Engineering, RMIT University, GPO Box 2476V, Melbourne, Victoria 3001 (Australia)], E-mail: madhu.bhaskaran@gmail.com; Sriram, S. [Microelectronics and Materials Technology Centre, School of Electrical and Computer Engineering, RMIT University, GPO Box 2476V, Melbourne, Victoria 3001 (Australia); Mitchell, D.R.G.; Short, K.T. [Institute of Materials Engineering, Australian Nuclear Science and Technology Organisation (ANSTO), PMB 1, Menai, New South Wales 2234 (Australia); Holland, A.S. [Microelectronics and Materials Technology Centre, School of Electrical and Computer Engineering, RMIT University, GPO Box 2476V, Melbourne, Victoria 3001 (Australia)

    2008-09-30

    This article discusses the results from X-ray diffraction (XRD) analysis of piezoelectric strontium-doped lead zirconate titanate (PSZT) thin films deposited on multi-layer coatings on silicon. The films were deposited by RF magnetron sputtering on a metal coated substrate. The aim was to exploit the pronounced piezoelectric effect that is theoretically expected normal to the substrate. This work highlighted the influence that the bottom electrode architecture exerts on the final crystalline orientation of the deposited thin films. A number of bottom electrode architectures were used, with the uppermost metal layer on which PSZT was deposited being gold or platinum. The XRD analysis revealed that the unit cell of the PSZT thin films deposited on gold and on platinum were deformed, relative to expected unit cell dimensions. Experimental results have been used to estimate the unit cell parameters. The XRD results were then indexed based on these unit cell parameters. The choice and the thickness of the intermediate adhesion layers influenced the relative intensity, and in some cases, the presence of perovskite peaks. In some cases, undesirable reactions between the bottom electrode layers were observed, and layer architectures to overcome these reactions are also discussed.

  6. Crystallographic changes in lead zirconate titanate due to neutron irradiation

    Directory of Open Access Journals (Sweden)

    Alexandra Henriques

    2014-11-01

    Full Text Available Piezoelectric and ferroelectric materials are useful as the active element in non-destructive monitoring devices for high-radiation areas. Here, crystallographic structural refinement (i.e., the Rietveld method is used to quantify the type and extent of structural changes in PbZr0.5Ti0.5O3 after exposure to a 1 MeV equivalent neutron fluence of 1.7 × 1015 neutrons/cm2. The results show a measurable decrease in the occupancy of Pb and O due to irradiation, with O vacancies in the tetragonal phase being created preferentially on one of the two O sites. The results demonstrate a method by which the effects of radiation on crystallographic structure may be investigated.

  7. Piezoelectric transducer array microspeaker

    KAUST Repository

    Carreno, Armando Arpys Arevalo; Conchouso Gonzalez, David; Castro, David; Kosel, Jü rgen; Foulds, Ian G.

    2016-01-01

    contains 2n piezoelectric transducer membranes, where “n” is the bit number. Every element of the array has a circular shape structure. The membrane is made out four layers: 300nm of platinum for the bottom electrode, 250nm or lead zirconate titanate (PZT

  8. A poling study on lead zirconate titanate composition

    International Nuclear Information System (INIS)

    Bryant, P.J.

    1992-01-01

    Ceramics produced by the conventional mixed oxide route are dual phased. Because the titania and zirconia are not perfectly homogenized, some parts of the ceramic are more tetragonal (titanium rich) and other parts more rhombohedral (zirconium rich). This inhomogeneity means that some domains can be more easily poled than others. Lastly, the density and porosity can affect the poling process if the flaw density becomes such that the breakdown voltage is exceeded by the required poling voltage. The phase boundary determined by most dielectric and piezoelectric measurements is significantly removed from the 44% titanium content determined by neutron diffraction. The indicators that are most consistent with this value are the minimum in the poling efficiency curve and the shape of the dissipative factor curve. The reason for the discrepancy appears to be related to the broad coexistence region of the two phases and the differing poling efficiencies of each phase. It has been established that different poling temperature profiles can substantially modify the observed properties. Such behaviour is again related to the inhomogeneity of the ceramic and the presence of the two phases. 4 refs., 5 figs

  9. Anisotropic dielectric response of lead zirconate crystals in the terahertz and infrared range at low temperature

    Czech Academy of Sciences Publication Activity Database

    Ostapchuk, Tetyana; Kadlec, Christelle; Kužel, Petr; Kroupa, Jan; Železný, Vladimír; Hlinka, Jiří; Petzelt, Jan; Dec, J.

    2014-01-01

    Roč. 87, 10-11 (2014), s. 1129-1137 ISSN 0141-1594 R&D Projects: GA ČR GA13-15110S Institutional support: RVO:68378271 Keywords : antiferroelectrics * infrared and terahertz spectroscopy * lead zirconate * phonons * complex dielectric permittivity Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.954, year: 2014

  10. Piezoelectric transducer array microspeaker

    KAUST Repository

    Carreno, Armando Arpys Arevalo

    2016-12-19

    In this paper we present the fabrication and characterization of a piezoelectric micro-speaker. The speaker is an array of micro-machined piezoelectric membranes, fabricated on silicon wafer using advanced micro-machining techniques. Each array contains 2n piezoelectric transducer membranes, where “n” is the bit number. Every element of the array has a circular shape structure. The membrane is made out four layers: 300nm of platinum for the bottom electrode, 250nm or lead zirconate titanate (PZT), a top electrode of 300nm and a structural layer of 50

  11. In situ synchrotron diffraction of lead-zirconate-titanate at its morphotropic phase boundary

    International Nuclear Information System (INIS)

    Schoenau, K.A.

    2008-01-01

    Ferroelectric lead zirconate titanate ceramics (PZT,Pb(Zr x Ti 1-x )O 3 ) find in industry intensifiedly applications as piezoactors. Their largest macroscopic strain under electric field they show in the region of the morphotropic phase boundary (MPB), the transition region between the Ti rich tetragonal and the Zr rich structure. The structure of PZT at the MPB was controversially discussed since the detection of a monoclinic intermediate phase by Noheda et al. [Appl. Phys. Lett.,74(14), 2059(1999)], whereby into the considerations the domain structure of the material not entered, which however is essentially responsible for the reaction under electric field. In order to understand the domain structure of PZT under electric field and to study possible causes for the fatigue behaviour of the material under bipolar cycling a bridge must be built between macroscopic and local structure. For this at the measuring place B2 of the Hasylab, Hamburg, synchrotron X-ray powder diffractometry was in situ performed under different sample environments in transmission geometry, which was correlated with transmission-electron-microscopical studies and electron spin resonance. Samples with compositions over the whole MPB were beside temperature-dependent measurements measured at room temperature in high resolution and under applied electric field. Furthermore for studies under electric field at elevated temperatures a special E-field furnace was constructed. It could be shown the large piezoelectric reaction of PZT at its MPB is strongly correlated with a diminishment of the domain structure, which simulates in X-ray diffraction a lower symmetric phase. The stability range of the nanodomains with temperature and electric field reflects in the switching behaviour of the matter and by the detection of a relaxor behavior of the nanodomain structure for the first time a direct comparison with relaxoceramics is possible. The varying stress conditions within the sample influence

  12. KNN–NTK composite lead-free piezoelectric ceramic

    Energy Technology Data Exchange (ETDEWEB)

    Matsuoka, T., E-mail: ta-matsuoka@mg.ngkntk.co.jp; Kozuka, H.; Kitamura, K.; Yamada, H.; Kurahashi, T.; Yamazaki, M.; Ohbayashi, K. [NGK SPARK PLUG Co., Ltd., 2808 Iwasaki, Komaki, Aichi 485-8510 (Japan)

    2014-10-21

    A (K,Na)NbO₃-based lead-free piezoelectric ceramic was successfully densified. It exhibited an enhanced electromechanical coupling factor of kₚ=0.52, a piezoelectric constant d₃₃=252 pC/N, and a frequency constant Nₚ=3170 Hz m because of the incorporation of an elaborate secondary phase composed primarily of KTiNbO₅. The ceramic's nominal composition was 0.92K₀.₄₂Na₀.₄₄Ca₀.₀₄Li₀.₀₂Nb₀.₈₅O₃–0.047K₀.₈₅Ti₀.₈₅Nb₁.₁₅O₅–0.023BaZrO₃ –0.0017Co₃O₄–0.002Fe₂O₃–0.005ZnO, abbreviated herein as KNN–NTK composite. The KNN–NTK ceramic exhibited a dense microstructure with few microvoids which significantly degraded its piezoelectric properties. Elemental maps recorded using transmission electron microscopy with energy-dispersive X-ray spectroscopy (TEM–EDS) revealed regions of high concentrations of Co and Zn inside the NTK phase. In addition, X-ray diffraction patterns confirmed that a small portion of the NTK phase was converted into K₂(Ti,Nb,Co,Zn)₆O₁₃ or CoZnTiO₄ by a possible reaction between Co and Zn solutes and the NTK phase during a programmed sintering schedule. TEM studies also clarified a distortion around the KNN/NTK interfaces. Such an NTK phase filled voids between KNN particles, resulting in an improved chemical stability of the KNN ceramic. The manufacturing process was subsequently scaled to 100 kg per batch for granulated ceramic powder using a spray-drying technique. The properties of the KNN–NTK composite ceramic produced using the scaled-up method were confirmed to be identical to those of the ceramic prepared by conventional solid-state reaction sintering. Consequently, slight changes in the NTK phase composition and the distortion around the KNN/NTK interfaces affected the KNN–NTK composite ceramic's piezoelectric characteristics.

  13. Lead zirconate (PbZrO3 embedded in natural rubber as electroactive elastomer composites

    Directory of Open Access Journals (Sweden)

    Anuvat Sirivat

    2014-11-01

    Full Text Available Perovskite lead zirconate (PbZrO3 was synthesized in an orthorhombic form at a temperature below the Curie temperature, TC. The orthorhombic form is a noncentrosymmetric structure which is capable of spontaneous polarization. Fourier transform infrared (FTIR spectra and X-ray diffraction (XRD patterns confirm the successful synthesis of the lead zirconate; and scanning electron microscopy (SEM micrographs indicate that PbZrO3 particles are moderately dispersed in the natural rubber (NR matrix. Without an electrical field, the particles merely act as a ferroelectric filler, which can absorb and store additional stress. Under an electrical field, particle-induced dipole moments are generated, leading to interparticle interaction and a substantial increase in the storage modulus. At a small amount of lead zirconate particulates present in the natural rubber matrix, at a volume fraction of 0.007306, the electrical conductivity increases dramatically by nearly two orders of magnitude at the electrical frequency of 500 kHz.

  14. Structural Contribution to the Ferroelectric Fatigue in Lead Zirconate Titanate (PZT) Ceramics

    OpenAIRE

    Hinterstein , Manuel; Rouquette , Jerome; Haines , J; Papet , Ph; Glaum , Julia; Knapp , Michael; Eckert , J; Hoffman , M

    2014-01-01

    International audience; Many ferroelectric devices are based on doped lead zirconate titanate (PZT) ceramics with compositions near the morphotropic phase boundary (MPB), at which the relevant material's properties approach their maximum. Based on a synchrotron x-ray diffraction study of MPB PZT, bulk fatigue is unambiguously found to arise from a less effective field induced tetragonal-to-monoclinic transformation, at which the degradation of the polarization flipping is detected by a less i...

  15. Fatigue and failure responses of lead zirconate titanate multilayer actuator under unipolar high-field electric cycling

    Science.gov (United States)

    Zeng, Fan Wen; Wang, Hong; Lin, Hua-Tay

    2013-07-01

    Lead zirconate titanate (PZT) multilayer actuators with an interdigital electrode design were studied under high electric fields (3 and 6 kV/mm) in a unipolar cycling mode. A 100 Hz sine wave was used in cycling. Five specimens tested under 6 kV/mm failed from 3.8 × 105 to 7 × 105 cycles, whereas three other specimens tested under 3 kV/mm were found to be still functional after 108 cycles. Variations in piezoelectric and dielectric responses of the tested specimens were observed during the fatigue test, depending on the measuring and cycling conditions. Selected fatigued and damaged actuators were characterized using an impedance analyzer or small signal measurement. Furthermore, involved fatigue and failure mechanisms were investigated using scanning acoustic microscope and scanning electron microscope. The extensive cracks and porous regions were revealed across the PZT layers on the cross sections of a failed actuator. The results from this study have demonstrated that the high-field cycling can accelerate the fatigue of PZT stacks as long as the partial discharge is controlled. The small signal measurement can also be integrated into the large signal measurement to characterize the fatigue response of PZT stacks in a more comprehensive basis. The former can further serve as an experimental method to test and monitor the behavior of PZT stacks.

  16. Structural contribution to the ferroelectric fatigue in lead zirconate titanate ceramics

    Science.gov (United States)

    Hinterstein, M.; Rouquette, J.; Haines, J.; Papet, Ph.; Glaum, J.; Knapp, M.; Eckert, J.; Hoffman, M.

    2014-09-01

    Many ferroelectric devices are based on doped lead zirconate titanate (PZT) ceramics with compositions near the morphotropic phase boundary (MPB), at which the relevant material's properties approach their maximum. Based on a synchrotron x-ray diffraction study of MPB PZT, bulk fatigue is unambiguously found to arise from a less effective field induced tetragonal-to-monoclinic transformation, at which the degradation of the polarization flipping is detected by a less intense and more diffuse anomaly in the atomic displacement parameter of lead. The time dependence of the ferroelectric response on a structural level down to 250 μs confirms this interpretation in the time scale of the piezolectric strain response.

  17. Characterization of lead zirconate titanate (PZT)--indium tin oxide (ITO) thin film interface

    International Nuclear Information System (INIS)

    Sreenivas, K.; Sayer, M.; Laursen, T.; Whitton, J.L.; Pascual, R.; Johnson, D.J.; Amm, D.T.

    1990-01-01

    In this paper the interface between ultrathin sputtered lead zirconate titanate (PZT) films and a conductive electrode (indium tin oxide-ITO) is investigated. Structural and compositional changes at the PZT-ITO interface have been examined by surface analysis and depth profiling techniques of glancing angle x-ray diffraction, Rutherford backscattering (RBS), SIMS, Auger electron spectroscopy (AES), and elastic recoil detection analysis (ERDA). Studies indicate significant interdiffusion of lead into the underlying ITP layer and glass substrate with a large amount of residual stress at the interface. Influence of such compositional deviations at the interface is correlated to an observed thickness dependence in the dielectric properties of PZT films

  18. Fabrication and Characterization of Aligned Flexible Lead-Free Piezoelectric Nanofibers for Wearable Device Applications

    Directory of Open Access Journals (Sweden)

    Sang Hyun Ji

    2018-03-01

    Full Text Available Flexible lead-free piezoelectric nanofibers, based on BNT-ST (0.78Bi0.5Na0.5TiO3-0.22SrTiO3 ceramic and poly(vinylidene fluoride-trifluoroethylene (PVDF-TrFE copolymers, were fabricated by an electrospinning method and the effects of the degree of alignment in the nanofibers on the piezoelectric characteristics were investigated. The microstructure of the lead-free piezoelectric nanofibers was observed by field emission scanning electron microscope (FE-SEM and the orientation was analyzed by fast Fourier transform (FFT images. X-ray diffraction (XRD analysis confirmed that the phase was not changed by the electrospinning process and maintained a perovskite phase. Polarization-electric field (P-E loops and piezoresponse force microscopy (PFM were used to investigate the piezoelectric properties of the piezoelectric nanofibers, according to the degree of alignment—the well aligned piezoelectric nanofibers had higher piezoelectric properties. Furthermore, the output voltage of the aligned lead-free piezoelectric nanofibers was measured according to the vibration frequency and the bending motion and the aligned piezoelectric nanofibers with a collector rotation speed of 1500 rpm performed the best.

  19. Ceramic piezoelectric materials

    International Nuclear Information System (INIS)

    Kaszuwara, W.

    2004-01-01

    Ceramic piezoelectric materials conert reversibility electric energy into mechanical energy. In the presence of electric field piezoelectric materials exhibit deformations up to 0.15% (for single crystals up to 1.7%). The deformation energy is in the range of 10 2 - 10 3 J/m 3 and working frequency can reach 10 5 Hz. Ceramic piezoelectric materials find applications in many modern disciplines such as: automatics, micromanipulation, measuring techniques, medical diagnostics and many others. Among the variety of ceramic piezoelectric materials the most important appear to be ferroelectric materials such as lead zirconate titanate so called PZT ceramics. Ceramic piezoelectric materials can be processed by methods widely applied for standard ceramics, i.e. starting from simple precursors e.g. oxides. Application of sol-gel method has also been reported. Substantial drawback for many applications of piezoelectric ceramics is their brittleness, thus much effort is currently being put in the development of piezoelectric composite materials. Other important research directions in the field of ceramic piezoelectric materials composite development of lead free materials, which can exhibit properties similar to the PZT ceramics. Among other directions one has to state processing of single crystals and materials having texture or gradient structure. (author)

  20. Anisotropy of domain switching in prepoled lead titanate zirconate ceramics under multiaxial electrical loading

    Science.gov (United States)

    Liu, Yuan-Ming; Li, Fa-Xin; Fang, Dai-Ning

    2007-01-01

    The authors report an observation of anisotropic domain switching process in prepoled lead titanate zirconate (PZT) ceramics under multiaxial electrical loading. Prepoled PZT blocks were obliquely cut to apply an electric field at discrete angles θ (0°-180°) to the initial poling direction. Both the coercive field and switchable polarization are found to decrease significantly when sinθ increases from zero to unity. The measured strain curves show that most domains that accomplished 180° domain switching actually experienced two successive 90° switching. The oriented domain texture after poling plus the induced nonuniform stress are used to explain the observed domain switching anisotropy.

  1. Dynamic fatigue on repolarization of lead zirconate-titanate base ceramics with various ferroelectric hardness

    International Nuclear Information System (INIS)

    Gavrilyachenko, V.G.; Semenchev, A.F.; Sklyarova, E.N.; Kuznetsova, E.M.

    2006-01-01

    One studied experimentally changes of the residual polarization in lead zirconate-titanate base ceramics with various ferroelectric hardness under the effect of a strong varying field. The twinning and untwinning of crystallites accompanying repolarization is assumed to be the basic mechanism of propagation of the crystalline structure defects governing the fatigue rates of the ferroelectric-soft ceramics. In ferroelectric-hard ceramics crystallites the stable configurations of mechanical twins, the result of the secondary twinning, are formed when the hysteresis loop is formed. At repolarization in the mentioned structures one observes no motion of the twin boundaries, and the fatigue rates are low ones [ru

  2. TOPICAL REVIEW: Progress in engineering high strain lead-free piezoelectric ceramics

    Science.gov (United States)

    Leontsev, Serhiy O.; Eitel, Richard E.

    2010-08-01

    Environmental concerns are strongly driving the need to replace the lead-based piezoelectric materials currently employed as multilayer actuators. The current review describes both compositional and structural engineering approaches to achieve enhanced piezoelectric properties in lead-free materials. The review of the compositional engineering approach focuses on compositional tuning of the properties and phase behavior in three promising families of lead-free perovskite ferroelectrics: the titanate, alkaline niobate and bismuth perovskites and their solid solutions. The 'structural engineering' approaches focus instead on optimization of microstructural features including grain size, grain orientation or texture, ferroelectric domain size and electrical bias field as potential paths to induce large piezoelectric properties in lead-free piezoceramics. It is suggested that a combination of both compositional and novel structural engineering approaches will be required in order to realize viable lead-free alternatives to current lead-based materials for piezoelectric actuator applications.

  3. Effect of dielectrophoretic structuring on piezoelectric and pyroelectric properties of lead titanate-epoxy composites

    NARCIS (Netherlands)

    Khanbareh, H.; Zwaag, S. van der; Groen, W.A.

    2014-01-01

    Functional granular composites of lead titanate particles in an epoxy matrix prepared by dielectrophoresis show enhanced dielectric, piezoelectric and pyroelectric properties compared to 0-3 composites for different ceramic volume content from 10% to 50%. Two structuring parameters, the

  4. Thickness dependence of the poling and current-voltage characteristics of paint films made up of lead zirconate titanate ceramic powder and epoxy resin

    Science.gov (United States)

    Egusa, Shigenori; Iwasawa, Naozumi

    1995-11-01

    A specially prepared paint made up of lead zirconate titanate (PZT) ceramic powder and epoxy resin was coated on an aluminum plate and was cured at room temperature, thus forming the paint film of 25-300 μm thickness with a PZT volume fraction of 53%. The paint film was then poled at room temperature, and the poling behavior was determined by measuring the piezoelectric activity as a function of poling field. The poling behavior shows that the piezoelectric activity obtained at a given poling field increases with an increase in the film thickness from 25 to 300 μm. The current-voltage characteristic of the paint film, on the other hand, shows that the increase in the film thickness leads not only to an increase in the magnitude of the current density at a given electric field but also to an increase in the critical electric field at which the transition from the ohmic to space-charge-limited conduction takes place. This fact indicates that the amount of the space charge of electrons injected into the paint film decreases as the film thickness increases. Furthermore, comparison of the current-voltage characteristic of the paint film with that of a pure epoxy film reveals that the space charge is accumulated largely at the interface between the PZT and epoxy phases in the paint film. On the basis of this finding, a model is developed for the poling behavior of the paint film by taking into account a possible effect of the space-charge accumulation and a broad distribution of the electric field in the PZT phase. This model is shown to give an excellent fit to the experimental data of the piezoelectric activity obtained here as a function of poling field and film thickness.

  5. Phase structure and piezoelectric properties of Li-modified NKLN lead-free piezoelectric ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Sin-Woong; Lee, Sung-Chan; Kim, Min-Soo; Jeong, Soon-Jong; Kim, In-Sung; Song, Jae-Sung [Korea Electrotechnology Research Institute, Changwon (Korea, Republic of)

    2012-09-15

    Through the low-temperature sintering method, a sintered body with excellent characteristics was produced in an eco-friendly niobate-based piezoelectric ceramic, whose application was low in expectation due to poor sinterability. Li{sub 2}CO{sub 3} was added in excess to (Na{sub 0.49}K{sub 0.45}Li{sub 0.06})NbO{sub 3}, and ceramics were manufactured using a commercial sintering method. Then, the sinterability and the piezoelectric properties of the specimens containing varying amounts of Li{sub 2}CO{sub 3} were investigated. The microstructure demonstrated the typical abnormal grain growth tendencies with the addition of Li{sub 2}CO{sub 3}, and this was explained through changes in the critical driving force in the interface reaction-controlled nucleation and growth theory. When the specimen had been sintered at 1000 .deg. C for 4 hours in air after the addition of 1.5 mol% Li{sub 2}CO{sub 3}, the sintered body showed outstanding characteristics with a piezoelectric coefficient of 180 pC/N, an electromechanical coupling coefficient of 0.32, and a dielectric constant of 975. These results showed that eco-friendly niobate-based ceramics, whose use in applications was expected to be difficult in spite of their excellent properties, could be used to produce piezoelectric materials with outstanding properties through a commercial low-temperature sintering method using additives.

  6. Phase structure and piezoelectric properties of Li-modified NKLN lead-free piezoelectric ceramics

    International Nuclear Information System (INIS)

    Kim, Sin-Woong; Lee, Sung-Chan; Kim, Min-Soo; Jeong, Soon-Jong; Kim, In-Sung; Song, Jae-Sung

    2012-01-01

    Through the low-temperature sintering method, a sintered body with excellent characteristics was produced in an eco-friendly niobate-based piezoelectric ceramic, whose application was low in expectation due to poor sinterability. Li 2 CO 3 was added in excess to (Na 0.49 K 0.45 Li 0.06 )NbO 3 , and ceramics were manufactured using a commercial sintering method. Then, the sinterability and the piezoelectric properties of the specimens containing varying amounts of Li 2 CO 3 were investigated. The microstructure demonstrated the typical abnormal grain growth tendencies with the addition of Li 2 CO 3 , and this was explained through changes in the critical driving force in the interface reaction-controlled nucleation and growth theory. When the specimen had been sintered at 1000 .deg. C for 4 hours in air after the addition of 1.5 mol% Li 2 CO 3 , the sintered body showed outstanding characteristics with a piezoelectric coefficient of 180 pC/N, an electromechanical coupling coefficient of 0.32, and a dielectric constant of 975. These results showed that eco-friendly niobate-based ceramics, whose use in applications was expected to be difficult in spite of their excellent properties, could be used to produce piezoelectric materials with outstanding properties through a commercial low-temperature sintering method using additives.

  7. Advances in Lead-Free Piezoelectric Materials for Sensors and Actuators

    Directory of Open Access Journals (Sweden)

    Jacob L. Jones

    2010-03-01

    Full Text Available Piezoelectrics have widespread use in today’s sensor and actuator technologies. However, most commercially available piezoelectric materials, e.g., Pb [ZrxTi1-x] O3 (PZT,are comprised of more than 60 weight percent lead (Pb. Dueto its harmful effects, there is a strong impetus to identify new lead-free replacement materials with comparable properties to those of PZT. This review highlights recent developments in several lead-free piezoelectric materials including BaTiO3, Na0.5Bi0.5TiO3, K0.5Bi0.5TiO3, Na0.5K0.5NbO3, and their solid solutions. The factors that contribute to strong piezoelectric behavior are described and a summary of the properties for the various systems is provided.

  8. Ultrahigh Piezoelectric Properties in Textured (K,Na)NbO3 -Based Lead-Free Ceramics.

    Science.gov (United States)

    Li, Peng; Zhai, Jiwei; Shen, Bo; Zhang, Shujun; Li, Xiaolong; Zhu, Fangyuan; Zhang, Xingmin

    2018-02-01

    High-performance lead-free piezoelectric materials are in great demand for next-generation electronic devices to meet the requirement of environmentally sustainable society. Here, ultrahigh piezoelectric properties with piezoelectric coefficients (d 33 ≈700 pC N -1 , d 33 * ≈980 pm V -1 ) and planar electromechanical coupling factor (k p ≈76%) are achieved in highly textured (K,Na)NbO 3 (KNN)-based ceramics. The excellent piezoelectric properties can be explained by the strong anisotropic feature, optimized engineered domain configuration in the textured ceramics, and facilitated polarization rotation induced by the intermediate phase. In addition, the nanodomain structures with decreased domain wall energy and increased domain wall mobility also contribute to the ultrahigh piezoelectric properties. This work not only demonstrates the tremendous potential of KNN-based ceramics to replace lead-based piezoelectrics but also provides a good strategy to design high-performance piezoelectrics by controlling appropriate phase and crystallographic orientation. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  9. Influence of crystal phases on electro-optic properties of epitaxially grown lanthanum-modified lead zirconate titanate films

    Science.gov (United States)

    Masuda, Shin; Seki, Atsushi; Masuda, Yoichiro

    2010-02-01

    We describe here how we have improved the crystal qualities and controlled the crystal phase of the lanthanum-modified lead zirconate titanate (PLZT) film without changing the composition ratio using an oxygen-pressure crystallization process. A PLZT film deposited on a SrTiO3 substrate with the largest electro-optic (EO) coefficient of 498 pm/V has been achieved by controlling the crystal phase of the film. Additionally, a fatigue-free lead zirconate titanate (PZT) capacitor with platinum electrodes has been realized by reducing the oxygen vacancies in the films.

  10. Comparison of chemical solution deposition systems for the fabrication of lead zirconate titanate thin films

    International Nuclear Information System (INIS)

    Lecarpentier, F.; Daglish, M.; Kemmitt, T.

    2001-01-01

    Ferroelectric thin films of lead zirconate titanate Pb(Zr x Ti 1-x )O 3 (PZT) were prepared from five chemical solution deposition (CSD) systems, namely methoxyethanol, citrate, diol, acetic acid and triethanolamine. Physical characteristics of the solutions, processing parameters and physical and electrical properties of the films were used to assess the relative advantages and disadvantages of the different chemical systems. All the CSD systems decomposed to produce single phase perovskite PZT at temperatures above 650 deg C. Thin film deposition was influenced by the specific characteristics of each system such as wetting on the substrate and viscosity. Distinct precursor effects on the thin film crystallinity and electrical performance were revealed. The diol route yielded films with the highest crystallite size, highest permittivity and lowest loss tangent. The relative permittivity exhibited by films made by the other routes were 25% to 35% lower at equivalent thicknesses. Copyright (2001) The Australian Ceramic Society

  11. Electrical fatigue behaviour in lead zirconate titanate: an experimental and theoretical study

    International Nuclear Information System (INIS)

    Bhattacharyya, Mainak; Arockiarajan, A

    2013-01-01

    A systematic investigation on electrical fatigue in lead zirconate titanate (PZT) is carried out for different loading frequencies. Experiments are conducted up to 10 6 cycles to measure the electrical displacement and longitudinal strain on bulk ceramics in the bipolar mode with large electrical loading conditions. A simplified macroscopic model based on physical mechanisms of domain switching is developed to predict the non-linear behaviour. In this model, the volume fraction of a domain is used as the internal variable by considering the mechanisms of domain nucleation and propagation (domain wall movement). The measured material properties at different fatigue cycles are incorporated into the switching model as damage parameters and the classical strain versus electric field and electric displacement versus electric field curves are simulated. Comparison between the experiments and simulations shows that the proposed model can reproduce the characteristics of non-linear as well as fatigue responses. (paper)

  12. Fatigue-free lead zirconate titanate-based capacitors for nonvolatile memories

    International Nuclear Information System (INIS)

    Shannigrahi, S. R.; Jang, Hyun M.

    2001-01-01

    The development of lead zirconate titanate (PZT)-based capacitors has been a long time goal of ferroelectric random access memories (FRAM). However, PZT-based perovskites with common platinum (Pt) electrodes have suffered from a significant reduction of the remanent polarization (P r ) after a certain number of read/write cycles (electrical fatigue). We now report the development of fatigue-free lanthanum-modified PZT capacitors using common Pt electrodes. The capacitors fabricated at 580 o C by applying a PZT seed layer exhibited fatigue-free behavior up to 6.5 x 10 10 switching cycles, a quite stable charge retention profile with time, and comparatively high P r values, all of which assure their suitability for practical FRAM applications. Copyright 2001 American Institute of Physics

  13. Electrical fatigue behaviour in lead zirconate titanate: an experimental and theoretical study

    Science.gov (United States)

    Bhattacharyya, Mainak; Arockiarajan, A.

    2013-08-01

    A systematic investigation on electrical fatigue in lead zirconate titanate (PZT) is carried out for different loading frequencies. Experiments are conducted up to 106 cycles to measure the electrical displacement and longitudinal strain on bulk ceramics in the bipolar mode with large electrical loading conditions. A simplified macroscopic model based on physical mechanisms of domain switching is developed to predict the non-linear behaviour. In this model, the volume fraction of a domain is used as the internal variable by considering the mechanisms of domain nucleation and propagation (domain wall movement). The measured material properties at different fatigue cycles are incorporated into the switching model as damage parameters and the classical strain versus electric field and electric displacement versus electric field curves are simulated. Comparison between the experiments and simulations shows that the proposed model can reproduce the characteristics of non-linear as well as fatigue responses.

  14. Surface bond contraction and its effect on the nanometric sized lead zirconate titanate

    International Nuclear Information System (INIS)

    Haitao Huang; Sun, Chang Q.; Hing, Peter

    2000-01-01

    The grain size effect of lead zirconate titanate PbZr 1-x Ti x O 3 (PZT, x≥0.6) caused by surface bond contraction has been investigated by using the Landau-Ginsburg-Devonshire (LGD) phenomenological theory. It has been shown that, due to the surface bond contraction, both the Curie temperature and the spontaneous polarization of tetragonal PZT decrease with decreasing grain size. These effects become more significant when the grain size is in the nanometre range. A dielectric anomaly appears with decreasing grain size, which corresponds to a size dependent phase transformation. The ferroelectric critical size below which a loss of ferroelectricity will happen is estimated from the results obtained. (author). Letter-to-the-editor

  15. Piezoelectricity

    CERN Document Server

    Lubitz, Karl

    2008-01-01

    Piezoelectric materials play a key role in an innovative market. Advances in applications derive from new materials and their development, as well as to new market requirements. This report elucidates these developments by a broad spectrum of examples, comprising ultrasound in medicine and defence industry, and frequency control.

  16. Finite Element Study on Acoustic Energy Harvesting Using Lead-Free Piezoelectric Ceramics

    Science.gov (United States)

    Kumar, Anuruddh; Sharma, Anshul; Kumar, Rajeev; Vaish, Rahul

    2018-02-01

    In this article, a numerical investigation is performed for ambient acoustic energy harvesting at a low-frequency acoustic signal. A model of a quarter-wavelength resonator with a rectangular cross section is constructed, and piezoelectric-laminated bimorph plates are placed inside the system. Finite element modeling is implemented to numerically formulate the piezoelectric energy harvester. With the application of acoustic pressure at the open end of the resonator, amplified acoustic pressure inside the tube vibrates the piezolaminated bimorphs inside the tube, thus generating electric potential on the piezoelectric layers. To generate higher voltage and power in the acoustic harvester, multiple piezolaminated plates are positioned inside the resonator. The lead-free piezoelectric material K0.475Na0.475Li0.05 (Nb0.92Ta0.05Sb0.03)O3 (KNLNTS) is laminated on the host structure as a layer of piezoelectric material for the acoustic energy harvester. With the application of an acoustic sound pressure of 1 dB at the opening of the tube, a maximum output voltage of 16.3 V is measured at the first natural frequency, while the maximum power calculated is 0.033 mW. Maximum voltage is obtained when five piezoelectric bimorphs are place inside the resonator. At the second natural frequency, the maximum voltage measured is 8.40 V, obtained when eight piezoelectric bimorphs are placed inside the resonator, and the maximum power calculated is 0.020 mW.

  17. Patterning lead zirconate titanate nanostructures at sub-200-nm resolution by soft confocal imprint lithography and nanotransfer molding

    NARCIS (Netherlands)

    Khan, Sajid; Göbel, Ole; Blank, David H.A.; ten Elshof, Johan E.

    2009-01-01

    Patterned sol-gel-derived lead zirconate titanate (PZT) thin films with lateral resolutions down to 100 nm on silicon are reported. Both an imprint and a transfer-molding method were employed. The formed patterns after annealing were characterized with scanning electron microscopy, atomic force

  18. Wafer-scale integration of piezoelectric actuation capabilities in nanoelectromechanical systems resonators

    OpenAIRE

    DEZEST, Denis; MATHIEU, Fabrice; MAZENQ, Laurent; SOYER, Caroline; COSTECALDE, Jean; REMIENS, Denis; THOMAS, Olivier; DEÜ, Jean-François; NICU, Liviu

    2013-01-01

    In this work, we demonstrate the integration of piezoelectric actuation means on arrays of nanocantilevers at the wafer scale. We use lead titanate zirconate (PZT) as piezoelectric material mainly because of its excellent actuation properties even when geometrically constrained at extreme scale

  19. Lead-free LiNbO3 nanowire-based nanocomposite for piezoelectric power generation

    Science.gov (United States)

    2014-01-01

    In a flexible nanocomposite-based nanogenerator, in which piezoelectric nanostructures are mixed with polymers, important parameters to increase the output power include using long nanowires with high piezoelectricity and decreasing the dielectric constant of the nanocomposite. Here, we report on piezoelectric power generation from a lead-free LiNbO3 nanowire-based nanocomposite. Through ion exchange of ultra-long Na2Nb2O6-H2O nanowires, we synthesized long (approximately 50 μm in length) single-crystalline LiNbO3 nanowires having a high piezoelectric coefficient (d33 approximately 25 pmV-1). By blending LiNbO3 nanowires with poly(dimethylsiloxane) (PDMS) polymer (volume ratio 1:100), we fabricated a flexible nanocomposite nanogenerator having a low dielectric constant (approximately 2.7). The nanogenerator generated stable electric power, even under excessive strain conditions (approximately 105 cycles). The different piezoelectric coefficients of d33 and d31 for LiNbO3 may have resulted in generated voltage and current for the e33 geometry that were 20 and 100 times larger than those for the e31 geometry, respectively. This study suggests the importance of the blending ratio and strain geometry for higher output-power generation in a piezoelectric nanocomposite-based nanogenerator. PACS 77.65.-j; 77.84.-s; 73.21.Hb PMID:24386884

  20. Orientation of rapid thermally annealed lead zirconate titanate thin films on (111) Pt substrate

    International Nuclear Information System (INIS)

    Brooks, K.G.; Reaney, I.M.; Klissurska, R.; Huang, Y.; Bursill, L.A.; Setter, N.

    1994-01-01

    The nucleation, growth and orientation of lead zirconate titanate thin films prepared from organometallic precursor solutions by spin coating on (111) oriented platinum substrates and crystallized by rapid thermal annealing was investigated. The effects of pyrolysis temperature, post-pyrolysis thermal treatments, excess lead addition, and Nb dopant substitution are reported. The use of post pyrolysis oxygen anneals at temperatures in the regime of 350-450 deg C was found to strongly effect the kinetics of subsequent amorphous-pyrochlore perovskite crystallization by rapid thermal annealing. It has also allowed films of reproducible microstructure and textures (both (100) and (111)) to be prepared by rapid thermal annealing. It is suggested that such anneals and pyrolysis temperature affect the oxygen concentration/average Pb valence in the amorphous films prior to annealing. The changes in Pb valence state then affect the stability of the transient pyrochlore phase and thus the kinetics of perovskite crystallization. Nb dopant was also found to influence the crystallization kinetics. 28 refs., 18 figs

  1. Synthesis and characterization of lead zirconate titanate powders obtained by the oxidant peroxo method

    Energy Technology Data Exchange (ETDEWEB)

    Camargo, Emerson R. [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Department of Chemistry, UFSCar-Federal University of Sao Carlos, Rod. Washington Luis km 235, CP 676, Sao Carlos SP, 13565-905 (Brazil)], E-mail: camargo@ufscar.br; Leite, Edson R. [LIEC-Laboratorio Interdisciplinar de Eletroquimica e Ceramica, Department of Chemistry, UFSCar-Federal University of Sao Carlos, Rod. Washington Luis km 235, CP 676, Sao Carlos SP, 13565-905 (Brazil)], E-mail: derl@power.ufscar.br; Longo, Elson [Department of Biochemistry, Chemistry Institute of Araraquara, UNESP, Sao Paulo State University Rua Francisco Degni, CP 355 Araraquara SP, 14801-907 Brazil (Brazil)], E-mail: elson@iq.unesp.br

    2009-02-05

    Lead zirconate titanate (PbZr{sub 1-x}Ti{sub x}O{sub 3}) was synthesized by the 'oxidant peroxo method (OPM)' with 'x' between 0.25 and 0.50. Titanium metal was dissolved into a hydrogen peroxide/ammonia aqueous solution, followed by the addition of lead and zirconium nitrate solution. The amorphous precipitated precursor obtained was crystallized by heat treatment between 400 and 1000 deg. C. Images of transmission microscopy showed spherical particles with average diameter between 20 and 60 nm, and the presence of necks between particles treated at 700 deg. C. All of the unpressed powders were characterized by X-ray diffractometry and FT-Raman spectroscopy. Powder samples with 'x' up to 0.35 showed rhombohedral structure when treated at temperatures higher than 500 deg. C, and tetragonal structure when 'x' was higher than 0.40. Analysis of XRD and Raman spectroscopy of the precursor powders showed amorphous-like structures, however powders treated at 400 deg. C showed a structure identified as an intermediate pyrochlore phase, independently of the Zr and Ti mole ratio.

  2. Synthesis and characterization of lead zirconate titanate powders obtained by the oxidant peroxo method

    International Nuclear Information System (INIS)

    Camargo, Emerson R.; Leite, Edson R.; Longo, Elson

    2009-01-01

    Lead zirconate titanate (PbZr 1-x Ti x O 3 ) was synthesized by the 'oxidant peroxo method (OPM)' with 'x' between 0.25 and 0.50. Titanium metal was dissolved into a hydrogen peroxide/ammonia aqueous solution, followed by the addition of lead and zirconium nitrate solution. The amorphous precipitated precursor obtained was crystallized by heat treatment between 400 and 1000 deg. C. Images of transmission microscopy showed spherical particles with average diameter between 20 and 60 nm, and the presence of necks between particles treated at 700 deg. C. All of the unpressed powders were characterized by X-ray diffractometry and FT-Raman spectroscopy. Powder samples with 'x' up to 0.35 showed rhombohedral structure when treated at temperatures higher than 500 deg. C, and tetragonal structure when 'x' was higher than 0.40. Analysis of XRD and Raman spectroscopy of the precursor powders showed amorphous-like structures, however powders treated at 400 deg. C showed a structure identified as an intermediate pyrochlore phase, independently of the Zr and Ti mole ratio

  3. Characterisation of lead barium zirconate thin films for utilisation of the electrocaloric effect

    Energy Technology Data Exchange (ETDEWEB)

    Shaw, C.P., E-mail: c.p.shaw@cranfield.ac.uk [Surface Engineering and Nanotechnology Institute, Manufacturing and Materials Department, Cranfield University, Cranfield, Bedfordshire MK43 0AL (United Kingdom); Zhang, Qi, E-mail: q.zhang@cranfield.ac.uk [Surface Engineering and Nanotechnology Institute, Manufacturing and Materials Department, Cranfield University, Cranfield, Bedfordshire MK43 0AL (United Kingdom); Correia, T.M., E-mail: Tatiana.correia@ktn-uk.org [Knowledge Transfer Network (United Kingdom); Weaver, P.M., E-mail: paul.weaver@innotecuk.com [InotekUK (United Kingdom)

    2016-08-01

    Characterisation of a composition of Lead Barium Zirconate thin films deposited by a spin coating sol-gel process onto platinised silicon substrates has been undertaken to investigate a potential application utilising the reported electrocaloric properties of the material. Xray diffraction studies revealed that above 700 °C the presence of pyrochlore phase was replaced by ferroelectric phase but the identification of antiferroelectric phases previously reported could not be identified. Wet etching of the films produced an insoluble residue containing only evidence of zirconium out of the original three metals, which resembled a skeletal structure similar to the original rosette morphology of the annealed films. Elemental analysis of the annealed films using EDX indicated a non-target Pb:Ba:Zr ratio, which suggested a reduced Zr content of the films. “Solution-like” rather than “sol-like” nature of the spin coated sol and phase boundary proximity are proposed for reported observations, and a mechanism is proposed to account for the unusual observed trend in dielectric constant. - Highlights: • Characterisation of sol-gel deposited Lead barium zirconnate films. • Absence of previously reported antiferroelectric phase. • Identification of proposed non-PBZ phase. • Anomalous increase in film capacitance with thickness interpreted.

  4. Electronically droplet energy harvesting using piezoelectric cantilevers

    KAUST Repository

    Al Ahmad, Mahmoud Al

    2012-01-01

    A report is presented on free falling droplet energy harvesting using piezoelectric cantilevers. The harvester incorporates a multimorph clamped-free cantilever which is composed of five layers of lead zirconate titanate piezoelectric thick films. During the impact, the droplet kinetic energy is transferred into the form of mechanical stress forcing the piezoelectric structure to vibrate. Experimental results show energy of 0.3 μJ per droplet. The scenario of moderate falling drop intensity, i.e. 230 drops per second, yields a total energy of 400 μJ. © 2012 The Institution of Engineering and Technology.

  5. Develop techniques for ion implantation of PLZT [lead-lanthanum-zirconate-titanate] for adaptive optics

    International Nuclear Information System (INIS)

    Batishko, C.R.; Brimhall, J.L.; Pawlewicz, W.T.; Stahl, K.A.; Toburen, L.H.

    1987-09-01

    Research was conducted at Pacific Northwest Laboratory to develop high photosensitivity adaptive optical elements utilizing ion implanted lanthanum-doped lead-zirconate-titanate (PLZT). One centimeter square samples were prepared by implanting ferroelectric and anti-ferroelectric PLZT with a variety of species or combinations of species. These included Ne, O, Ni, Ne/Cr, Ne/Al, Ne/Ni, Ne/O, and Ni/O, at a variety of energies and fluences. An indium-tin oxide (ITO) electrode coating was designed to give a balance of high conductivity and optical transmission at near uv to near ir wavelengths. Samples were characterized for photosensitivity; implanted layer thickness, index of refraction, and density; electrode (ITO) conductivity; and in some cases, residual stress curvature. Thin film anti-ferroelectric PLZT was deposited in a preliminary experiment. The structure was amorphous with x-ray diffraction showing the beginnings of a structure at substrate temperatures of approximately 550 0 C. This report summarizes the research and provides a sampling of the data taken during the report period

  6. Effect of compositional variations in the lead lanthanum zirconate stannate titanate system on electrical properties

    International Nuclear Information System (INIS)

    Markowski, K.; Park, S.E.; Yoshikawa, Shoko; Cross, L.E.

    1996-01-01

    The purpose of this work was to evaluate the effect of compositional modifications on the electrical properties of lead lanthanum zirconate stannate titanate (PLZST) ceramics, as well as to examine their electrically induced phase-change behavior. Variations in the Ti:Sn ratio were evaluated. Increased Ti 4+ content produced the following: decreased switching field, related to an increased antiferroelectric-ferroelectric (AFE-FE) transition temperature; constant hysteresis (ΔE) correlated with a constant temperature of the maximum dielectric constant (T max ); a sharper dielectric-constant maximum peak; and increased room-temperature dielectric constant (K). Variations in the Zr:Sn ratio also were evaluated. Increased Zr 4+ content produced the following: increased hysteresis with increased T max , decreased maximum dielectric constant, and decreased switching field with increased AFE-FE transition temperature (T AFE-FE ). From these results, with respect to compositional modifications, the AFE-FE switching field (E AFE-FE ) and ΔE were observed to be dependent strongly on T AFE-FE and T max , respectively. Negligible change existed in the strain achievable at the switching field, which remained constant for all compositions at ∼0.16%. The significance of this research was the ability demonstrated to tailor the properties of phase-change materials through compositional modifications

  7. Chemical solution deposited BaPbO3 buffer layers for lead zirconate titanate ferroelectric films

    International Nuclear Information System (INIS)

    Tseng, T.-K.; Wu, J.-M.

    2005-01-01

    Conductive perovskite BaPbO 3 (BPO) films have been prepared successfully by chemical solution deposition method through spin-coating on Pt/Ti/SiO 2 /Si substrates. The choice of baking temperature is a key factor on the development of conducting BPO perovskite phase. When the baking temperature is higher than 350 deg. C, the BPO films contain a high content of BaCO 3 phase after annealing at temperatures higher than 500 deg. C. If the baking temperature is chosen lower than 300 deg. C, such as 200 deg. C, the annealed BPO films consist mostly of perovskite with only traces of BaCO 3 . Choosing 200 deg. C as the baking temperature, the BPO films developed single perovskite phase at temperatures as low as 550 deg. C. The perovskite BPO phase is stable in the range of 550-650 deg. C and the measured sheet resistance of the BPO films is about 2-3 Ω/square. The perovskite BPO film as a buffer layer provides improvement in electric properties of lead zirconate titanate films

  8. Modification of surface texture by grinding and polishing lead zirconate titanate ceramics

    International Nuclear Information System (INIS)

    Cheng, S.; Lloyd, I.K.

    1992-01-01

    This paper reports that grinding and polishing affected the orientation of 90 degrees domains at the surface of lead zirconate titanate (PZT) ceramics. This was quantified by using changes in the intensity ratio of the (002) and (200) X-ray reflections. Grinding unpoled PZT with 600-grit SiC paper gave X-ray intensity ratios similar to those of poled material. This implies that 90 degrees domain realignments had occurred in the near surface region probed by the X-rays. Grinding poled samples with 600-grit SiC further increased the X-ray intensity ratio beyond that caused by poling, indicating that additional surface reorientation of 90 degrees domains had occurred. The effects of diamond polishing depended on the size of the diamond particles. The use of 6-μm diamond had no effect on the (002)/(200) intensity ratio of either poled or unpoled samples, while polishing with 15- or 45-μm diamond significantly enhanced the 90 degrees domain rotation. In unpoled samples, the increase in the X-ray intensity ratio then approached that induced by poling or grinding with 600-grit SiC paper. While the observed increase in X-ray intensity ratio upon grinding is attributed to the rotation of 90 degrees domains, the simultaneous formation of 180 degrees domains appears to minimize or reduce the increase in electrical polarization

  9. Crystallization of sol-gel derived lead zirconate titanate thin films in argon and oxygen atmospheres

    International Nuclear Information System (INIS)

    Bursill, L.A.

    1994-01-01

    Electron diffraction and high-resolution electron microscopic techniques are applied to reveal the mechanisms of crystallization of 75 nm thin films of ferroelectric lead-zirconate-titanate (PZT). Sol-gel methods, followed by pyrolysis at 350 deg C, were used to provide a common starting point after which a variety of rapid-thermal annealing (RTA) experiments in the temperature range 400-700 deg C were made in argon, oxygen and nitrogen/hydrogen atmospheres. The results are interpreted in terms of the crystal chemical analysis, which points out that partial pressure of oxygen and heating rate are important experimental parameters which must be controlled if ferroelectric perovskite-type Pb 2 ZrTiO 6 , rather than pyrochlore-type Pb 2 ZrTiO 6+x , where O < X < 1 or -1 < X < O, is to be obtained after the RTA step. Thus significant improvements in the crystallization of perovskite-type PZT were clearly demonstrated by using argon atmospheres for the RTA step. The results have significance for the production of high-quality ferroelectric thin films, with improved switching and fatigue characteristics, since even small amounts of the pyrochlore phase prove detrimental for these properties. 18 refs., 1 tab., 10 figs

  10. Effect of bipolar electric fatigue on polarization switching in lead-zirconate-titanate ceramics

    Science.gov (United States)

    Zhukov, Sergey; Fedosov, Sergey; Glaum, Julia; Granzow, Torsten; Genenko, Yuri A.; von Seggern, Heinz

    2010-07-01

    From comparison of experimental results on polarization switching in fresh and electrically fatigued lead-zirconate-titanate (PZT) over a wide range of applied fields and switching times it is concluded that fatigue alters the local field distribution inside the sample due to the generation of discrete defects, such as voids and cracks. Such defects have a strong influence on the overall electric field distribution by their shape and dielectric permittivity. On this hypothesis, a new phenomenological model of polarization switching in fatigued PZT is proposed. The model assumes that the fatigued sample can be composed of different local regions which exhibit different field strengths but otherwise can be considered as unfatigued. Consequently the temporal response of a fatigued sample is assumed to be the superposition of the field-dependent temporal responses of unfatigued samples weighted by their respective volume fraction. A certain part of the volume is excluded from the overall switching process due to the domain pinning even at earlier stages of fatigue, which can be recovered by annealing. Suitability of the proposed model is demonstrated by a good correlation between experimental and calculated data for differently fatigued samples. Plausible cause of the formation of such regions is the generation of defects such as microcracks and the change in electrical properties at imperfections such as pores or voids.

  11. Crystallization of sol-gel derived lead zirconate titanate thin films in argon and oxygen atmospheres

    Energy Technology Data Exchange (ETDEWEB)

    Bursill, L A [Melbourne Univ., Parkville, VIC (Australia). School of Physics; Brooks, K G [Ecole Polytechnique Federale, Lausanne (Switzerland)

    1994-12-31

    Electron diffraction and high-resolution electron microscopic techniques are applied to reveal the mechanisms of crystallization of 75 nm thin films of ferroelectric lead-zirconate-titanate (PZT). Sol-gel methods, followed by pyrolysis at 350 deg C, were used to provide a common starting point after which a variety of rapid-thermal annealing (RTA) experiments in the temperature range 400-700 deg C were made in argon, oxygen and nitrogen/hydrogen atmospheres. The results are interpreted in terms of the crystal chemical analysis, which points out that partial pressure of oxygen and heating rate are important experimental parameters which must be controlled if ferroelectric perovskite-type Pb{sub 2}ZrTiO{sub 6}, rather than pyrochlore-type Pb{sub 2}ZrTiO{sub 6+x}, where O < X < 1 or -1 < X < O, is to be obtained after the RTA step. Thus significant improvements in the crystallization of perovskite-type PZT were clearly demonstrated by using argon atmospheres for the RTA step. The results have significance for the production of high-quality ferroelectric thin films, with improved switching and fatigue characteristics, since even small amounts of the pyrochlore phase prove detrimental for these properties. 18 refs., 1 tab., 10 figs.

  12. The Effect of Acceptor and Donor Doping on Oxygen Vacancy Concentrations in Lead Zirconate Titanate (PZT).

    Science.gov (United States)

    Slouka, Christoph; Kainz, Theresa; Navickas, Edvinas; Walch, Gregor; Hutter, Herbert; Reichmann, Klaus; Fleig, Jürgen

    2016-11-22

    The different properties of acceptor-doped (hard) and donor-doped (soft) lead zirconate titanate (PZT) ceramics are often attributed to different amounts of oxygen vacancies introduced by the dopant. Acceptor doping is believed to cause high oxygen vacancy concentrations, while donors are expected to strongly suppress their amount. In this study, La 3+ donor-doped, Fe 3+ acceptor-doped and La 3+ /Fe 3+ -co-doped PZT samples were investigated by oxygen tracer exchange and electrochemical impedance spectroscopy in order to analyse the effect of doping on oxygen vacancy concentrations. Relative changes in the tracer diffusion coefficients for different doping and quantitative relations between defect concentrations allowed estimates of oxygen vacancy concentrations. Donor doping does not completely suppress the formation of oxygen vacancies; rather, it concentrates them in the grain boundary region. Acceptor doping enhances the amount of oxygen vacancies but estimates suggest that bulk concentrations are still in the ppm range, even for 1% acceptor doping. Trapped holes might thus considerably contribute to the charge balancing of the acceptor dopants. This could also be of relevance in understanding the properties of hard and soft PZT.

  13. The Effect of Acceptor and Donor Doping on Oxygen Vacancy Concentrations in Lead Zirconate Titanate (PZT

    Directory of Open Access Journals (Sweden)

    Christoph Slouka

    2016-11-01

    Full Text Available The different properties of acceptor-doped (hard and donor-doped (soft lead zirconate titanate (PZT ceramics are often attributed to different amounts of oxygen vacancies introduced by the dopant. Acceptor doping is believed to cause high oxygen vacancy concentrations, while donors are expected to strongly suppress their amount. In this study, La3+ donor-doped, Fe3+ acceptor-doped and La3+/Fe3+-co-doped PZT samples were investigated by oxygen tracer exchange and electrochemical impedance spectroscopy in order to analyse the effect of doping on oxygen vacancy concentrations. Relative changes in the tracer diffusion coefficients for different doping and quantitative relations between defect concentrations allowed estimates of oxygen vacancy concentrations. Donor doping does not completely suppress the formation of oxygen vacancies; rather, it concentrates them in the grain boundary region. Acceptor doping enhances the amount of oxygen vacancies but estimates suggest that bulk concentrations are still in the ppm range, even for 1% acceptor doping. Trapped holes might thus considerably contribute to the charge balancing of the acceptor dopants. This could also be of relevance in understanding the properties of hard and soft PZT.

  14. Adhesion strength of lead zirconate titanate sol-gel thin films

    Energy Technology Data Exchange (ETDEWEB)

    Berfield, Thomas A., E-mail: tom.berfield@louisville.edu [Department of Mechanical Engineering, University of Louisville, Louisville, KY 40292 (United States); Kitey, Rajesh [Department of Aerospace Engineering, Indian Institute of Technology Kanpur, Kanpur (India); Kandula, Soma S. [Intel Corporation, Portland, OR (United States)

    2016-01-01

    The adhesion strength between a thin film and substrate is often the critical parameter that controls the initiation as well as the mode of film failure. In this work, a laser-based spallation method is used to determine the adhesion strength of “as deposited” lead zirconate titanate (PZT) sol-gel thin films on the two functionally different substrates. For the first case, PZT sol-gel film is deposited onto bare Si/SiO{sub 2} substrates via spin casting. The extremely high adhesion strength between the film and the substrate necessitated an additional platinum mass superlayer to be deposited on top of the PZT film in order to induce interfacial failure. For the superlayer film system, a hybrid experimental/numerical method is employed for determining the substrate/film interfacial strength, quantified to be in the range of 460–480 MPa. A second substrate variation with lower adhesion strength is also prepared by applying a self-assembled octadecyltrichlorosilane (ODS) monolayer to the Si/SiO{sub 2} substrate prior to the film deposition. For the monolayer-coated substrate case, the adhesion strength is observed to be significantly lower (54.7 MPa) when compared to the earlier case. - Highlights: • A non-contact laser spallation method is used to determine PZT film adhesion. • A mediated self-assembled monolayer is shown to greatly reduce interface strength. • Adhesion strength for even well-bonded thin films was found using a superlayer.

  15. Investigation of the additive induced doping effects in gelcast soft lead zirconate titanate ceramics

    International Nuclear Information System (INIS)

    Guo Dong; Cai Kai; Li Longtu; Gui Zhilun

    2009-01-01

    Due to the high sensitivity of the electrical properties of electronic ceramics to various factors, knowledge about the possible influence of the processing procedure on their electrical performance is critical for applying a new technique to the fabrication of the materials. In this study, various electrical parameters, complex impedance spectra, ferroelectric hysteresis loops, and microstructures of soft lead zirconate titanate (PZT) ceramics formed by the gelcasting technique from suspensions with various dispersants were investigated in comparison with those of the conventional dry pressed ones. We found that the sodium ion, which is the main cation in many commercial surfactants, exhibited obvious hard doping effects; thus causing deteriorated performance of the gelcast PZT ceramics. While a certain impurity ion introduced by a dispersant was also found to induce soft doping characteristics and improve the electrical performance of the materials. The results suggest that the doping effects of the metal ions or impurities introduced by the dispersants, or other additives, should be generally considered for applying a wet processing technique to forming multicomponent electronic ceramics.

  16. Raman analysis of ferroelectric switching in niobium-doped lead zirconate titanate thin films

    International Nuclear Information System (INIS)

    Ferrari, P.; Ramos-Moore, E.; Guitar, M.A.; Cabrera, A.L.

    2014-01-01

    Characteristic Raman vibration modes of niobium-doped lead zirconate titanate (PNZT) are studied as a function of ferroelectric domain switching. The microstructure of PNZT is characterized by scanning electron microscopy and X-ray diffraction. Ferroelectric switching is achieved by applying voltages between the top (Au) and bottom (Pt) electrodes, while acquiring the Raman spectra in situ. Vibrational active modes associated with paraelectric and ferroelectric phases are identified after measuring above and below the ferroelectric Curie temperature, respectively. Changes in the relative intensities of the Raman peaks are observed as a function of the switching voltage. The peak area associated with the ferroelectric modes is analyzed as a function of the applied voltage within one ferroelectric polarization loop, showing local maxima around the coercive voltage. This behavior can be understood in terms of the correlation between vibrational and structural properties, since ferroelectric switching modifies the interaction between the body-centered atom (Zr, Ti or Nb) and the Pb–O lattice. - Highlights: • Electric fields induce structural distortions on ferroelectric perovskites. • Ferroelectric capacitor was fabricated to perform hysteresis loops. • Raman analysis was performed in situ during ferroelectric switching. • Raman modes show hysteresis and inflections around the coercive voltages. • Data can be understood in terms of vibrational–structural correlations

  17. Wafer scale lead zirconate titanate film preparation by sol-gel method using stress balance layer

    International Nuclear Information System (INIS)

    Lu Jian; Kobayashi, Takeshi; Yi Zhang; Maeda, Ryutaro; Mihara, Takashi

    2006-01-01

    In this paper, platinum/titanium (Pt/Ti) film was introduced as a residual stress balance layer into wafer scale thick lead zirconate titanate (PZT) film fabrication by sol-gel method. The stress developing in PZT film's bottom electrode as well as in PZT film itself during deposition were analyzed; the wafer curvatures, PZT crystallizations and PZT electric properties before and after using Pt/Ti stress balance layer were studied and compared. It was found that this layer is effective to balance the residual stress in PZT film's bottom electrode induced by thermal expansion coefficient mismatch and Ti diffusion, thus can notably reduce the curvature of 4-in. wafer from - 40.5 μm to - 12.9 μm after PZT film deposition. This stress balance layer was also found effective to avoid the PZT film cracking even when annealed by rapid thermal annealing with heating-rate up to 10.5 deg. C/s. According to X-ray diffraction analysis and electric properties characterization, crack-free uniform 1-μm-thick PZT film with preferred pervoskite (001) orientation, excellent dielectric constant, as high as 1310, and excellent remanent polarization, as high as 39.8 μC/cm 2 , can be obtained on 4-in. wafer

  18. Flexible Piezoelectric Touch Sensor by Alignment of Lead-Free Alkaline Niobate Microcubes in PDMS

    NARCIS (Netherlands)

    Deutz, D.B.; Mascarenhas, N.T.; Schelen, J.B.J.; de Leeuw, D.M.; van der Zwaag, S.; Groen, W.A.

    2017-01-01

    A highly sensitive, lead-free, and flexible piezoelectric touch sensor is reported based on composite films of alkaline niobate K0.485Na0.485Li0.03NbO3 (KNLN) powders aligned in a polydimethylsiloxane (PDMS) matrix. KNLN powder is fabricated by

  19. Synthesis, by alkaline fusion of zirconia from zirconite: characterization and preparation of lead zirconate-titanate

    International Nuclear Information System (INIS)

    Zaghete, M.A.

    1985-01-01

    Zirconium oxide was prepared from zirconite by alkaline fusion. The purity of zirconia was determined by atomic absorption spectroscopy and was found to be 99,94 wt%. In order to prepare en unglomerated and dry hidrous zirconia powder it was used alcohol and acetone for washing and gel suspension; control of the drying rate; and control of the atmosphere and temperature of the oven. The physical characteristics of the hidrous zirconia powder were determined after calcining in several conditions. The zirconia obtained by calcining at 800 0 C during 5 hours (13,9m 2 /g) was used with titanium oxide (7,6m 2 /g and lead oxide (0,6m 2 /g) to prepare a lead zirconate-titanate (PZT) with composition Pb(Zr 0,5 Ti 0,5 O 3 . Two different procedures were used to obtain high densits PZT pellets: in the first procedure the misture of the oxide powder with above composition were reacted at 850 0 C for 4 hours. Then the powder was pressed and sintered at 1200 0 C during 4 and 6 hours; in the second procedure the mixture of unreacted oxide were pressed in pellets and then reacted at 850 0 C during 4 hours and sintered at 1200 0 C during 4 and 6 hours. The apparent density of the sintered pellets were determined By mercury displacement and ranged from 7,25 to 7,39 g/cm 3 for the compacts obtained by the second procedure and from 8,08 to 8,10g/cm 3 for the compacts obtained by the first procedure. The microstructure observed by scanning electron microscopy showed that sintered compact obtained by the first procedure has a more homogeneous size distribution when compared with samples obtained be the second procedure. (author) [pt

  20. On the valency state of radiogenic lead in zircon and its consequences

    DEFF Research Database (Denmark)

    Kramers, J.; Frei, Robert; Newville, M.

    2009-01-01

    nucleus comes to rest. Further, a zircon grain, being small, should remain highly oxidizing in its interior by the constant loss of ß-particles, maintaining the 4+ state of radiogenic Pb. From its effective ion radius, similar to that of Zr4+, and its charge, Pb4+ has to be compatible in the zircon...... not resemble that of PbO2. The arguments why radiogenic Pb should be tetravalent are based on analogies with studies relating to the tetravalent state of 234Th and the hexavalent state of 234U, which show that a-recoil in silicates generates a strongly oxidizing environment at the site where the recoiling......-recoil damaged sites could be leached out by any electrolyte solution that reduces it to the divalent state, making it both incompatible and soluble. Thus, discordia can be generated in weathering. The curious observation that discordant Archaean zircon suites generally define trends to lower intercepts at up...

  1. Microwave emission from lead zirconate titanate induced by impulsive mechanical load

    Energy Technology Data Exchange (ETDEWEB)

    Aman, A., E-mail: alexander.aman@ovgu.de [Department of Engineering, Brandenburg University of Applied Science, 14470 Brandenburg an derHavel (Germany); Packaging Group, Institute of Micro- and Sensorsytems, Otto-von-Guericke University, Universitätsplatz 2, 39106 Magdeburg (Germany); Majcherek, S. [Packaging Group, Institute of Micro- and Sensorsytems, Otto-von-Guericke University, Universitätsplatz 2, 39106 Magdeburg (Germany); Hirsch, S. [Department of Engineering, Brandenburg University of Applied Science, 14470 Brandenburg an derHavel (Germany); Schmidt, B. [Chair of Micorsystem Technology, Institute of Micro- and Sensorsytems, Otto-von-Guericke University, Universitätsplatz 2, 39106 Magdeburg (Germany)

    2015-10-28

    This paper focuses on microwave emission from Lead zirconate titanate Pb [Zr{sub x}Ti{sub 1−x}] O{sub 3} (PZT) induced by mechanical stressing. The mechanical stress was initiated by impact of a sharp tungsten indenter on the upper surface of PZT ceramic. The sequences of microwave and current impulses, which flew from indenter to electric ground, were detected simultaneously. The voltage between the upper and lower surface of ceramic was measured to obtain the behavior of mechanical force acting on ceramic during the impact. It was found that the amplitude, form, and frequency of measured microwave impulses were different by compression and restitution phase of impact. Two different mechanisms of electron emission, responsible for microwave impulse generation, were proposed based on the dissimilar impulse behavior. The field emission from tungsten indenter is dominant during compression, whereas ferroemission dominates during restitution phase. Indeed, it was observed that the direction of the current flow, i.e., sign of current impulses is changed by transitions from compression to restitution phase of impact. The observed dissimilar behavior of microwave impulses, caused by increasing and decreasing applied force, can be used to calculate the contact time and behavior of mechanical force during mechanical impact on ceramic surface. It is shown that the generation of microwave impulses exhibits high reproducibility, impulse intensity, a low damping factor, and high mechanical failure resistance. Based on these microwave emission properties of PZT, the development of new type of stress sensor with spatial resolution of few microns becomes possible.

  2. Reduction of etching damage in lead-zirconate-titanate thin films with inductively coupled plasma

    International Nuclear Information System (INIS)

    Lim, Kyu-Tae; Kim, Kyoung-Tae; Kim, Dong-Pyo; Kim, Chang-Il

    2003-01-01

    In this work, we etched lead-zirconate-titanate (PZT) films with various additive gases (O 2 and Ar) in Cl 2 /CF 4 plasmas, while mixing ratio was fixed at 8/2. After the etching, the plasma induced damages are characterized in terms of hysteresis curves, leakage current, retention properties, and switching polarization. When the electrical properties of PZT etched in O 2 or Ar added to Cl 2 /CF 4 were compared, the value of remanent polarization in O 2 added to Cl 2 /CF 4 plasma is higher than that in Ar added plasma. The maximum etch rate of the PZT thin films was 145 nm/min for 30% Ar added Cl 2 /CF 4 gas having mixing ratio of 8/2 and 110 nm/min for 10% O 2 added to that same gas mixture. In order to recover the ferroelectric properties of the PZT thin films after etching, we annealed the etched PZT thin films at 550 deg. C in an O 2 atmosphere for 10 min. From the hysteresis curves, leakage current, retention property, and switching polarization, the reduction of the etching damage and the recovery via the annealing turned out to be more effective when O 2 was added to Cl 2 /CF 4 than Ar. X-ray diffraction showed that the structural damage was lower when O 2 was added to Cl 2 /CF 4 and the improvement in the ferroelectric properties of the annealed samples was consistent with the increased intensities of the (100) and the (200) PZT peaks

  3. Study of samarium modified lead zirconate titanate and nickel zinc ferrite composite system

    Energy Technology Data Exchange (ETDEWEB)

    Rani, Rekha [Department of Physics, SD PG College, Panipat 132103 (India); School of Physics and Materials Science, Thapar University, Patiala 147004 (India); Juneja, J.K., E-mail: jk_juneja@yahoo.com [Department of Physics, Hindu College, Sonepat 131001 (India); Singh, Sangeeta [Department of Physics, GVM Girls College, Sonepat 131001 (India); Raina, K.K. [School of Physics and Materials Science, Thapar University, Patiala 147004 (India); Prakash, Chandra [Solid State Physics Laboratory, Timarpur, Delhi 110054 (India)

    2015-03-15

    In the present work, composites of samarium substituted lead zirconate titanate and nickel zinc ferrite with compositional formula 0.95Pb{sub 1−3x/2} Sm{sub x}Zr{sub 0.65}Ti{sub 0.35}O{sub 3}–0.05Ni{sub 0.8}Zn{sub 0.2}Fe{sub 2}O{sub 4} (x=0, 0.01, 0.02 and 0.03) were prepared by the conventional solid state route. X-ray diffraction analysis was carried out to confirm the coexistence of individual phases. Microstructural study was done by using scanning electron microscope. Dielectric constant and loss were studied as a function of temperature and frequency. To study ferroelectric and magnetic properties of the composite samples, corresponding P–E and M–H hysteresis loops were recorded. Change in magnetic properties of electrically poled composite sample (x=0.02) was studied to confirm the magnetoelectric (ME) coupling. ME coefficient (dE/dH) of the samples (x=0 and 0.02) was measured as a function of DC magnetic field. - Highlights: • We are reporting the effect of Sm substitution on PZT–NiZn ferrite composites. • Observation of both P–E and M–H loops confirms ferroelectric and magnetic ordering. • With Sm substitution, significant improvement in properties was observed. • Increase in magnetization for electrically poled sample is evidence of ME coupling. • Electric polarization is generated by applying magnetic field.

  4. Piezoelectric effect in polarized and electrically depolarized ferrotextures

    International Nuclear Information System (INIS)

    Luchaninov, A.G.; Shil'nikov, A.V.; Shuvalov, L.A.

    1999-01-01

    Piezoelectric moduli were calculated for ferroelectric textures in the states with the greatest possible (in terms of symmetry) polarization and the zero polarization (obtained from the former by electrical depolarization). The calculations were performed for the textures of crystals of the classes 2, 3, 4, 6, mm2, 3m, 4mm,and 6mm. The experimental results for lead zirconate-titanate- and barium-titanate-based piezoelectric ceramic are reported

  5. Lead-free piezoelectrics based on potassium-sodium niobate with giant d(33).

    Science.gov (United States)

    Zhang, Binyu; Wu, Jiagang; Cheng, Xiaojing; Wang, Xiaopeng; Xiao, Dingquan; Zhu, Jianguo; Wang, Xiangjian; Lou, Xiaojie

    2013-08-28

    High-performance lead-free piezoelectrics (d33 > 400 pC/N) based on 0.96(K0.5Na0.5)0.95Li0.05Nb1-xSbxO3-0.04BaZrO3 with the rhombohedral-tetragonal (R-T) phase boundary have been designed and prepared. The R-T phase boundary lies the composition range of 0.04 ≤ x ≤ 0.07, and the dielectric and piezoelectric properties of the ceramics with the compositions near the phase boundary are significantly enhanced. In addition, the ceramic with x = 0.07 has a giant d33 of ~425 pC/N, which is comparable to that (~416 pC/N) of textured KNN-based ceramics (Saito, Y.; Takao, H.; Tani, T.; Nonoyama, T.; Takatori, K.; Homma, T.; Nagaya, T.; Nakamura, M. Nature 2004, 432, 84). The underlying physical mechanisms for enhanced piezoelectric properties are addressed. We believe that the material system is the most promising lead-free piezoelectric candidates for the practical applications.

  6. The effect of calcining temperature on the properties of 0-3 piezoelectric composites of PZT and a liquid crystalline thermosetting polymer

    NARCIS (Netherlands)

    Ende, D.A. van den; Groen, W.A.; Zwaag, S. van der

    2011-01-01

    We report on the optimisation of a recently developed high performance 0-3 piezoelectric composite comprising of the piezoelectric Lead Zirconate Titanate (PZT) powder and a liquid crystalline thermosetting matrix polymer (LCT). The matrix polymer is a liquid crystalline polymer comprising of an

  7. Effect of polarization fatigue on the Rayleigh coefficients of ferroelectric lead zirconate titanate thin films: Experimental evidence and implications

    Science.gov (United States)

    Lou, X. J.; Zhang, H. J.; Luo, Z. D.; Zhang, F. P.; Liu, Y.; Liu, Q. D.; Fang, A. P.; Dkhil, B.; Zhang, M.; Ren, X. B.; He, H. L.

    2014-09-01

    The effect of polarization fatigue on the Rayleigh coefficients of ferroelectric lead zirconate titanate (PZT) thin film was systematically investigated. It was found that electrical fatigue strongly affects the Rayleigh behaviour of the PZT film. Both the reversible and irreversible Rayleigh coefficients decrease with increasing the number of switching cycles. This phenomenon is attributed to the growth of an interfacial degraded layer between the electrode and the film during electrical cycling. The methodology used in this work could serve as an alternative way for evaluating the fatigue endurance and degradation in dielectric properties of ferroelectric thin-film devices during applications.

  8. Preparation and piezoelectric properties of (K0.5Na0.5)NbO3 lead-free piezoelectric ceramics with pressure-less sintering

    International Nuclear Information System (INIS)

    Du Hongliang; Li Zhimin; Tang Fusheng; Qu Shaobo; Pei Zhibin; Zhou Wancheng

    2006-01-01

    Lead-free piezoelectric ceramics (K 0.5 Na 0.5 )NbO 3 (abbreviated as KNN) with the relative density of 97.6% have been synthesized by press-less sintering owing to the careful control of processing conditions. The phase structure of KNN ceramics with different sintering temperature and heating rate was analyzed. Results show that the pure perovskite phase with orthorhombic symmetry is in all ceramics specimens. The effect of heating rate and sintering temperature on microstructure and piezoelectric properties of KNN ceramics was investigated. The densification behavior and piezoelectric properties of KNN ceramics were enhanced by improving heating rate and sintering temperature. Pure KNN ceramics sintered at 1120 deg. C with heating rate of 5 deg. C/min showed optimized densification and piezoelectric properties (ρ = 4.4 g/cm 3 , d 33 = 120 pC/N -1 , k p = 0.40 and T c = 400 deg. C). The results show that KNN is a promising candidate for lead-free piezoelectric ceramics

  9. Polarization Switching and Light-Enhanced Piezoelectricity in Lead Halide Perovskites.

    Science.gov (United States)

    Coll, Mariona; Gomez, Andrés; Mas-Marza, Elena; Almora, Osbel; Garcia-Belmonte, Germà; Campoy-Quiles, Mariano; Bisquert, Juan

    2015-04-16

    We investigate the ferroelectric properties of photovoltaic methylammonium lead halide CH3NH3PbI3 perovskite using piezoelectric force microscopy (PFM) and macroscopic polarization methods. The electric polarization is clearly observed by amplitude and phase hysteresis loops. However, the polarization loop decreases as the frequency is lowered, persisting for a short time only, in the one second regime, indicating that CH3NH3PbI3 does not exhibit permanent polarization at room temperature. This result is confirmed by macroscopic polarization measurement based on a standard capacitive method. We have observed a strong increase of piezoelectric response under illumination, consistent with the previously reported giant photoinduced dielectric constant at low frequencies. We speculate that an intrinsic charge transfer photoinduced dipole in the perovskite cage may lie at the origin of this effect.

  10. Texturation of lead-free BaTiO3-based piezoelectric ceramics

    OpenAIRE

    Ngueteu-Kamlo , A; Levassort , F; Pham Thi , M; Marchet , Pascal

    2014-01-01

    International audience; Nowadays, piezoelectric ceramics are integrated in a wide range of devices, in particular in ultrasonic applications (underwater sonar systems, medical imaging, non-destructive testing…). Most of them use Pb(Zr,Ti)O3 (PZT). However, due to health care and environmental problems, lead content must be reduced in such applications [1]. Recent reviews demonstrated that few lead-free materials families can be considered: the alkaline-niobates (K0.5Na0.5NbO3), the alkaline-b...

  11. Nanoscale characterization and local piezoelectric properties of lead-free KNN-LT-LS thin films

    Science.gov (United States)

    Abazari, M.; Choi, T.; Cheong, S.-W.; Safari, A.

    2010-01-01

    We report the observation of domain structure and piezoelectric properties of pure and Mn-doped (K0.44,Na0.52,Li0.04)(Nb0.84,Ta0.1,Sb0.06)O3 (KNN-LT-LS) thin films on SrTiO3 substrates. It is revealed that, using piezoresponse force microscopy, ferroelectric domain structure in such 500 nm thin films comprised of primarily 180° domains. This was in accordance with the tetragonal structure of the films, confirmed by relative permittivity measurements and x-ray diffraction patterns. Effective piezoelectric coefficient (d33) of the films were calculated using piezoelectric displacement curves and shown to be ~53 pm V-1 for pure KNN-LT-LS thin films. This value is among the highest values reported for an epitaxial lead-free thin film and shows a great potential for KNN-LT-LS to serve as an alternative to PZT thin films in future applications.

  12. Nanoscale characterization and local piezoelectric properties of lead-free KNN-LT-LS thin films

    Energy Technology Data Exchange (ETDEWEB)

    Abazari, M; Safari, A [Glenn Howatt Electroceramics Laboratories, Department of Materials Science and Engineering, Rutgers-The state University of New Jersey, Piscataway, NJ 08854 (United States); Choi, T; Cheong, S-W [Rutgers Center for Emergent Materials, Department of Physics and Astronomy, Rutgers-The state University of New Jersey, Piscataway, NJ 08854 (United States)

    2010-01-20

    We report the observation of domain structure and piezoelectric properties of pure and Mn-doped (K{sub 0.44},Na{sub 0.52},Li{sub 0.04})(Nb{sub 0.84},Ta{sub 0.1},Sb{sub 0.06})O{sub 3} (KNN-LT-LS) thin films on SrTiO{sub 3} substrates. It is revealed that, using piezoresponse force microscopy, ferroelectric domain structure in such 500 nm thin films comprised of primarily 180{sup 0} domains. This was in accordance with the tetragonal structure of the films, confirmed by relative permittivity measurements and x-ray diffraction patterns. Effective piezoelectric coefficient (d{sub 33}) of the films were calculated using piezoelectric displacement curves and shown to be {approx}53 pm V{sup -1} for pure KNN-LT-LS thin films. This value is among the highest values reported for an epitaxial lead-free thin film and shows a great potential for KNN-LT-LS to serve as an alternative to PZT thin films in future applications.

  13. Lead-free piezoelectric KNN-BZ-BNT films with a vertical morphotropic phase boundary

    Directory of Open Access Journals (Sweden)

    Wen Chen

    2015-07-01

    Full Text Available The lead-free piezoelectric 0.915K0.5Na0.5NbO3-0.075BaZrO3-0.01Bi0.5Na0.5TiO3 (0.915KNN-0.075BZ-0.01BNT films were prepared by a chemical solution deposition method. The films possess a pure rhomobohedral perovskite phase and a dense surface without crack. The temperature-dependent dielectric properties of the specimens manifest that only phase transition from ferroelectric to paraelectric phase occurred and the Curie temperature is 217 oC. The temperature stability of ferroelectric phase was also supported by the stable piezoelectric properties of the films. These results suggest that the slope of the morphotropic phase boundary (MPB for the solid solution formed with the KNN and BZ in the films should be vertical. The voltage-induced polarization switching, and a distinct piezo-response suggested that the 0.915 KNN-0.075BZ-0.01BNT films show good piezoelectric properties.

  14. Electrical properties and temperature stability of a new kind of lead-free piezoelectric ceramics

    International Nuclear Information System (INIS)

    Wang Yuanyu; Wu Jiagang; Xiao Dingquan; Zhang Bin; Wu Wenjuan; Shi Wei; Zhu Jianguo

    2008-01-01

    0.995[(K 0.50 Na 0.50 ) 0.94 Li 0.06 ]NbO 3 -0.005AETiO 3 (AE=Ca, Sr, Mg, Ba) lead-free piezoelectric ceramics were prepared by normal sintering. The effects of the AETiO 3 and poling temperature on the electrical properties of the ceramics were carefully studied, and the temperature stability of the electrical properties of the ceramics was also investigated. The experimental results show that the ceramics with Li and CaTiO 3 possess the pure phase, Li and AETiO 3 improves the electrical properties of the pure (K 0.50 Na 0.50 )NbO 3 ceramics, the poling temperature near tetragonal and orthorhombic phase transition will enhance the piezoelectric properties of the ceramics and the KNLN-CT ceramics exhibit good temperature stability of electrical properties for tetragonal and orthorhombic phase transition below room temperature. The KNLN-CT ceramics exhibit relatively good properties: d 33 = 172 pC N -1 , k p = 0.43, tan δ = 0.032, ε r = 771 and T c = 465 deg. C. As a result, the KNLN-CT ceramic is promising candidate material for piezoelectric devices.

  15. Preparation of lead titanate zirconate from metal citrates; Preparacao do titanato zirconato de chumbo a partir dos citratos metalicos

    Energy Technology Data Exchange (ETDEWEB)

    Bastos, C M.R.

    1994-12-31

    Lead titanate zirconate (PZT) preparation from its metal constituent citrates have been investigated. Metal citrates were obtained by forced precipitation using a dehydration alcohol mixture. Salt solutions of lead nitrate and octahydrated zirconyl chloride, and titanium tetrachloride were treated separately with citric acid and ammonium hydroxide. Zirconium, titanium and lead oxides resulted from thermal decomposition of corresponding citrates at 500{sup 0} C, 450{sup 0} C and 250{sup 0} C, respectively. Lead titanate (PT) and lead zirconate (P Z) were obtained by calcining at 450{sup 0} C and 500{sup 0} C, respectively, after adequate heating of citrates mechanically mixed in ethyl ether. PZT samples were obtained with different starting stoichiometry. Rhombohedral PZT-1 53/47 sample was prepared from co precipitating zirconyl ammonium and ammonium lead citrates in presence of ethanolic titanium oxide dispersion, and calcinating at 800{sup 0} C. Rhombohedral PZT-q 52/48 sample was obtained from heating at 500{sup 0} C for 2 hours a mixture of metal citrates coprecipitated by dehydration mixture of acetone-ethanol-formic acid (2:1:0,06). Tetragonal PZT-m stoichiometry 53/47 sample were obtained by calcining at after 600{sup 0} C for 2 hours after heating a mechanically mixed metal citrates. PT phase arose at 400{sup 0} C. PZT-m powders obtained in a range of 400{sup 0} C-800{sup 0} C were isostatically pressed, and sintered at 1100{sup 0} C and 1200{sup 0} C in saturated Pb O atmosphere. Rhombohedral sintered PZT was obtained with 7,78 g.cm{sup -3} at 1200{sup 0} C. (author). 123 refs, 53 figs, 32 tabs.

  16. Giant piezoelectricity in potassium-sodium niobate lead-free ceramics.

    Science.gov (United States)

    Wang, Xiaopeng; Wu, Jiagang; Xiao, Dingquan; Zhu, Jianguo; Cheng, Xiaojing; Zheng, Ting; Zhang, Binyu; Lou, Xiaojie; Wang, Xiangjian

    2014-02-19

    Environment protection and human health concern is the driving force to eliminate the lead from commercial piezoelectric materials. In 2004, Saito et al. [ Saito et al., Nature , 2004 , 432 , 84 . ] developed an alkali niobate-based perovskite solid solution with a peak piezoelectric constant d33 of 416 pC/N when prepared in the textured polycrystalline form, intriguing the enthusiasm of developing high-performance lead-free piezoceramics. Although much attention has been paid on the alkali niobate-based system in the past ten years, no significant breakthrough in its d33 has yet been attained. Here, we report an alkali niobate-based lead-free piezoceramic with the largest d33 of ∼490 pC/N ever reported so far using conventional solid-state method. In addition, this material system also exhibits excellent integrated performance with d33∼390-490 pC/N and TC∼217-304 °C by optimizing the compositions. This giant d33 of the alkali niobate-based lead-free piezoceramics is ascribed to not only the construction of a new rhombohedral-tetragonal phase boundary but also enhanced dielectric and ferroelectric properties. Our finding may pave the way for "lead-free at last".

  17. Effect of Polymer Matrix on the Structure and Electric Properties of Piezoelectric Lead Zirconatetitanate/Polymer Composites

    Directory of Open Access Journals (Sweden)

    Rui Li

    2017-08-01

    Full Text Available Piezoelectric lead zirconatetitanate (PZT/polymer composites were prepared by two typical polymer matrixes using the hot-press method. The micromorphology, microstructure, dielectric properties, and piezoelectric properties of the PZT/polymer composites were characterized and investigated. The results showed that when the condition of frequency is 103 Hz, the dielectric and piezoelectric properties of PZT/poly(vinylidene fluoride were both better than that of PZT/polyvinyl chloride (PVC. When the volume fraction of PZT was 50%, PZT/PVDF prepared by the hot-press method had better comprehensive electric property.

  18. Lead-free piezoelectric materials and ultrasonic transducers for medical imaging

    Directory of Open Access Journals (Sweden)

    Elaheh Taghaddos

    2015-06-01

    Full Text Available Piezoelectric materials have been vastly used in ultrasonic transducers for medical imaging. In this paper, firstly, the most promising lead-free compositions with perovskite structure for medical imaging applications have been reviewed. The electromechanical properties of various lead-free ceramics, composites, and single crystals based on barium titanate, bismuth sodium titanate, potassium sodium niobate, and lithium niobate are presented. Then, fundamental principles and design considerations of ultrasonic transducers are briefly described. Finally, recent developments in lead-free ultrasonic probes are discussed and their acoustic performance is compared to lead-based transducers. Focused transducers with different beam focusing methods such as lens focusing and mechanical shaping are explained. Additionally, acoustic characteristics of lead-free probes including the pulse-echo results as well as their imaging capabilities for various applications such as phantom imaging, in vitro intravascular ultrasound imaging of swine aorta, and in vivo or ex vivo imaging of human eyes and skin are reviewed.

  19. Thickness effect on the structure, grain size, and local piezoresponse of self-polarized lead lanthanum zirconate titanate thin films

    Energy Technology Data Exchange (ETDEWEB)

    Melo, M.; Araújo, E. B., E-mail: eudes@dfq.feis.unesp.br [Departamento de Física e Química, Faculdade de Engenharia de Ilha Solteira, UNESP—Univ. Estadual Paulista, 15385-000 Ilha Solteira, SP (Brazil); Shvartsman, V. V. [Institute for Materials Science, University Duisburg-Essen, 45141 Essen (Germany); Shur, V. Ya. [Institute of Natural Sciences, Ural Federal University, 620000 Ekaterinburg (Russian Federation); Kholkin, A. L. [Institute of Natural Sciences, Ural Federal University, 620000 Ekaterinburg (Russian Federation); Department of Physics and CICECO—Aveiro Institute of Materials, University of Aveiro, 3810-193 Aveiro (Portugal)

    2016-08-07

    Polycrystalline lanthanum lead zirconate titanate (PLZT) thin films were deposited on Pt/TiO{sub 2}/SiO{sub 2}/Si substrates to study the effects of the thickness and grain size on their structural and piezoresponse properties at nanoscale. Thinner PLZT films show a slight (100)-orientation tendency that tends to random orientation for the thicker film, while microstrain and crystallite size increases almost linearly with increasing thickness. Piezoresponse force microscopy and autocorrelation function technique were used to demonstrate the existence of local self-polarization effect and to study the thickness dependence of correlation length. The obtained results ruled out the bulk mechanisms and suggest that Schottky barriers near the film-substrate are likely responsible for a build-in electric field in the films. Larger correlation length evidence that this build-in field increases the number of coexisting polarization directions in larger grains leading to an alignment of macrodomains in thinner films.

  20. Dynamic processes of domain switching in lead zirconate titanate under cyclic mechanical loading by in situ neutron diffraction

    International Nuclear Information System (INIS)

    Pojprapai, Soodkhet; Luo, Zhenhua; Clausen, Bjorn; Vogel, Sven C.; Brown, Donald W.; Russel, Jennifer; Hoffman, Mark

    2010-01-01

    The performance of ferroelectric ceramics is governed by the ability of domains to switch. A decrease in the switching ability can lead to degradation of the materials and failure of ferroelectric devices. In this work the dynamic properties of domain reorientation are studied. In situ time-of-flight neutron diffraction is used to probe the evolution of ferroelastic domain texture under mechanical cyclic loading in bulk lead zirconate titanate ceramics. The high sensitivity of neutron diffraction to lattice strain is exploited to precisely analyze the change of domain texture and strain through a full-pattern Rietveld method. These results are then used to construct a viscoelastic model, which explains the correlation between macroscopic phenomena (i.e. creep and recovered deformation) and microscopic dynamic behavior (i.e. ferroelastic switching, lattice strain).

  1. The determination of major and some minor constituents in lead zirconate-titanate compositions by x-ray fluorescence and atomic absorption spectrometry

    NARCIS (Netherlands)

    van Willigen, J.H.H.G.; Kruidhof, H.; Dahmen, E.A.M.F.

    1972-01-01

    An accurate X-ray fluorescence spectrometric method is described for the determination of lead, zirconium and titanium in lead zirconate-titanate ceramics. Careful matching of samples and standards by a borax fusion method resulted in a relative standard deviation of about 0.2% for the major

  2. Ultrasonic Transducer Fabricated Using Lead-Free BFO-BTO+Mn Piezoelectric 1-3 Composite

    Directory of Open Access Journals (Sweden)

    Yan Chen

    2015-05-01

    Full Text Available Mn-doped 0.7BiFeO3-0.3BaTiO3 (BFO-0.3BTO+Mn 1% mol lead-free piezoelectric ceramic were fabricated by traditional solid state reaction. The phase structure, microstructure, and ferroelectric properties were investigated. Additionally, lead-free 1–3 composites with 60% volume fraction of BFO-BTO+Mn ceramic were fabricated for ultrasonic transducer applications by a conventional dice-and-fill method. The BFO-BTO+Mn 1-3 composite has a higher electromechanical coupling coefficient (kt = 46.4% and lower acoustic impedance (Za ~ 18 MRayls compared with that of the ceramic. Based on this, lead-free piezoelectric ceramic composite, single element ultrasonic transducer with a center frequency of 2.54 MHz has been fabricated and characterized. The single element transducer exhibits good performance with a broad bandwidth of 53%. The insertion loss of the transducer was about 33.5 dB.

  3. Damage-free patterning of ferroelectric lead zirconate titanate thin films for microelectromechanical systems via contact printing

    Science.gov (United States)

    Welsh, Aaron

    This thesis describes the utilization and optimization of the soft lithographic technique, microcontact printing, to additively pattern ferroelectric lead zirconate titanate (PZT) thin films for application in microelectromechanical systems (MEMS). For this purpose, the solution wetting, pattern transfer, printing dynamics, stamp/substrate configurations, and processing damages were optimized for incorporation of PZT thin films into a bio-mass sensor application. This patterning technique transfers liquid ceramic precursors onto a device stack in a desired configuration either through pattern definition in the stamp, substrate or both surfaces. It was determined that for ideal transfer of the pattern from the stamp to the substrate surface, wetting between the solution and the printing surface is paramount. To this end, polyurethane-based stamp surfaces were shown to be wet uniformly by polar solutions. Patterned stamp surfaces revealed that printing from raised features onto flat substrates could be accomplished with a minimum feature size of 5 mum. Films patterned by printing as a function of thickness (0.1 to 1 mum) showed analogous functional properties to continuous films that were not patterned. Specifically, 1 mum thick PZT printed features had a relative permittivity of 1050 +/- 10 and a loss tangent of 2.0 +/- 0.4 % at 10 kHz; remanent polarization was 30 +/- 0.4 muC/cm 2 and the coercive field was 45 +/- 1 kV/cm; and a piezoelectric coefficient e31,f of -7 +/- 0.4 C/m2. No pinching in the minor hysteresis loops or splitting of the first order reversal curve (FORC) distributions was observed. Non-uniform distribution of the solution over the printed area becomes more problematic as feature size is decreased. This resulted in solutions printed from 5 mum wide raised features exhibiting a parabolic shape with sidewall angles of ˜ 1 degree. As an alternative, printing solutions from recesses in the stamp surface resulted in more uniform solution thickness

  4. Transmission electron microscopy investigation of the microstructural mechanisms for the piezoelectricity in lead-free perovskite ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Ma, Cheng [Iowa State Univ., Ames, IA (United States)

    2012-01-01

    Lead-free materials with superior piezoelectricity are in increasingly urgent demand in the current century, because the industrial standard Pb(Zr,Ti)O3-based piezoelectrics, which contain over 60 weight% of the toxic element lead, pose severe environmental hazards. Although significant research efforts have been devoted in the past decade, no effective lead-free substitute for Pb(Zr,Ti)O3 has been identified yet. One of the primary hindrances to the development of lead-free piezoelectrics lies in the ignorance of the microstructural mechanism for the electric-field-induced strains in the currently existing compositions. In this dissertation, the microstructural origin for the high piezoelectricity in (1-x)(Bi1/2Na1/2)TiO3-xBaTiO3 [(1-x)BNT-xBT], the most widely studied lead-free piezoelectric system, has been elucidated.

  5. Effect of oxygen partial pressure on texture development in lead zirconate titanate thin films processed from metalorganic precursors

    International Nuclear Information System (INIS)

    Norton, Jarrod L.; Liedl, Gerald L.; Slamovich, Elliott B.

    1999-01-01

    Metalorganic liquid precursors were used to examine the effects of processing atmosphere on texture development in oriented Pb(Zr 0.60 Ti 0.40 )O 3 thin films. After removal of organic ligands via pyrolysis, the films were heated at 25 degree sign C/min in a 5% H 2 /Ar atmosphere until a switching temperature, after which the atmosphere was switched to pure oxygen. The films were heated to a maximum temperature of 650 degree sign C with switching temperatures ranging from 450 to 600 degree sign C. The degree of (111) orientation in the lead zirconate titanate (PZT) films increased with increasing switching temperature, resulting in highly textured (111) PZT films. These results suggest that atmosphere control plays a significant role in texture development during rapid thermal processing. (c) 1999 Materials Research Society

  6. Fracture mechanisms in ferroelectric-ferroelastic lead zirconate titanate (Zr:Ti = 0.54:0.46) ceramics

    International Nuclear Information System (INIS)

    Mehta, K.; Virkar, A.V.

    1990-01-01

    Fracture toughness, K IC , of a single-phase commercial lead zirconate titanate (PZT) ceramic of tetragonal structure was measured using the single edge notched beam method above and below the Curie temperature. Domain switching (poling) under electrical and mechanical loading was examined using x-ray diffraction. Surface grinding, electrical poling, and mechanical poling caused crystallographic texture. Similar texture, indicative of domain switching, was also observed on fracture surfaces of some samples fractured at room temperature. At room temperature, the highest K IC measured was 1.85 MPa · m 1/2 , while above the Curie temperature it was about 1.0 MPa · m 1/2 . Cracks emanating from Vickers indents in poled samples were different in the poling and the transverse directions. The difference in crack sizes is explained on the basis of domain switching during crack growth. These results indicate that ferroelastic domain switching (twinning) is a viable toughening mechanism in the PZT materials tested

  7. Improvement of fatigue resistance for multilayer lead zirconate titanate (PZT)-based ceramic actuators by external mechanical loads

    Science.gov (United States)

    Yang, Gang; Yue, Zhenxing; Ji, Ye; Chu, Xiangcheng; Li, Longtu

    2008-12-01

    The influence of external compressive loads, applied along a direction perpendicular to polarization, on fatigue behaviors of multilayer lead zirconate titanate (PZT)-based ceramic actuators was investigated. Under no external mechanical load, a normal fatigue behavior was observed, demonstrating that both switching polarization (Pswitching) and remnant polarization (Pr) progressively decreased with increasing switching cycles due to domain pinning by charge point defects. However, an anomalous enhancement in both switching and remnant polarizations was observed upon application of the external compressive loads. After 5×106 cycles of polarization switching, Pswitching and Pr increase by about 13% and 6% at 40 MPa, respectively, while Pswitching and Pr increase by about 11% and 21% at 60 MPa, respectively. The improvement of fatigue resistance can be attributed to non-180° domain switching and suppression of microcracking, triggered by external mechanical loads.

  8. Grain growth kinetics and electrical properties of lanthanum modified lead zirconate titanate (9/65/35) based ferroelectric ceramics

    International Nuclear Information System (INIS)

    Roca, R. Alvarez; Guerrero, F.; Botero, E. R.; Garcia, D.; Eiras, J. A.; Guerra, J. D. S.

    2009-01-01

    The influence of the microstructural characteristics on the dielectric and electrical properties has been investigated for Nd 3+ doped lanthanum modified lead zirconate titanate ferroelectric ceramics, obtained by the conventional solid-state reaction method, by taking into account different sintering conditions. The grain growth mechanism has been investigated and a cubic-type grain growth law was observed for samples with grain size varying from 1.00 up to 2.35 μm. The porosity and grain size dependences of the phase transition parameters, such as the maximum dielectric permittivity and its corresponding temperature (ε m and T m , respectively) were also investigated. The ac conductivity analyses followed the universal Jonscher law. The behavior of the frequency exponent (s) was analyzed through the correlated barrier hopping model. Both ac and dc conductivity results have been correlated with the observed microstructural features

  9. Piezoelectric Lead Zirconium Titanate Composite Touch Sensors for Integration with Flexible OLED Technology

    NARCIS (Netherlands)

    Deutz, D.B.; Tempelman, E.; Zwaag, S. van der; Groen, W.A.

    2015-01-01

    To enable the design of more intuitive product user interfaces, the prospects of matching piezoelectric touch sensors with flexible organic light emitting diode (OLED) technology are investigated. Low stiffness piezoelectric composite sensors, combining piezoelectric Pb(Zr,Ti)O3 powder with a

  10. Piezoelectric Materials Synthesized by the Hydrothermal Method and Their Applications

    Directory of Open Access Journals (Sweden)

    Takeshi Morita

    2010-12-01

    Full Text Available Synthesis by the hydrothermal method has various advantages, including low reaction temperature, three-dimensional substrate availability, and automatic polarization alignment during the process. In this review, powder synthesis, the fabrication of piezoelectric thin films, and their applications are introduced. A polycrystalline lead zirconate titanate (PZT thin film was applied to a micro ultrasonic motor, and an epitaxial lead titanate (PbTiO3 thin film was estimated as a ferroelectric data storage medium. Ferroelectric and piezoelectric properties were successfully obtained for epitaxial PbTiO3 films. As lead-free piezoelectric powders, KNbO3 and NaNbO3 powders were synthesized by the hydrothermal method and sintered together to form (K,NaNbO3 ceramics, from which reasonable piezoelectric performance was achieved.

  11. High aspect ratio lead zirconate titanate tube structures: I. Template assisted fabrication - vacuum infiltration method

    Directory of Open Access Journals (Sweden)

    Vladimír Kovaľ

    2012-03-01

    Full Text Available Polycrystalline Pb(Zr0.52Ti0.48O3 (PZT microtubes are fabricated by a vacuum infiltration method. The method is based on repeated infiltration of precursor solution into macroporous silicon (Si templates at a sub-atmospheric pressure. The pyrolyzed PZT tubes of a 2-µm outer diameter, extending to over 30 µm in length were released from the template using a selective isotropic-pulsed XeF2 reactive ion etching of silicon. Free-standing microtubes, partially anchored at the bottom of the Si template, were then crystallized in pure oxygen atmosphere at 750 °C for 2 min using a rapid thermal annealer. The perovskite phase of the final PZT tubes was confirmed by X-ray diffraction (XRD analysis. The XRD spectrum also revealed a small amount of the pyrochlore phase in the structure and signs of possible fluoride contamination caused most likely by the XeF2 etching process. The surface morphology was examined using scanning electron microscopy. It was demonstrated that the whole surface of the pore walls was conformally coated during the repeated infiltration of templates, resulting in straight tubes with closed tips formed on the opposite ends as replicas of the pore bottoms. These high aspect ratio ferroelectric structures are suggested as building units for developing miniaturized electronic devices, such as memory storage (DRAM trenched capacitors, piezoelectric scanners and actuators, and are of fundamental value for the theory of ferroelectricity in systems with low dimensionality.

  12. An equivalent dipole analysis of PZT ceramics and lead-free piezoelectric single crystals

    Directory of Open Access Journals (Sweden)

    Andrew J. Bell

    2016-06-01

    Full Text Available The recently proposed Equivalent Dipole Model for describing the electromechanical properties of ionic solids in terms of 3 ions and 2 bonds has been applied to PZT ceramics and lead-free single crystal piezoelectric materials, providing analysis in terms of an effective ionic charge and the asymmetry of the interatomic force constants. For PZT it is shown that, as a function of composition across the morphotropic phase boundary, the dominant bond compliance peaks at 52% ZrO2. The stiffer of the two bonds shows little composition dependence with no anomaly at the phase boundary. The effective charge has a maximum value at 50% ZrO2, decreasing across the phase boundary region, but becoming constant in the rhombohedral phase. The single crystals confirm that both the asymmetry in the force constants and the magnitude of effective charge are equally important in determining the values of the piezoelectric charge coefficient and the electromechanical coupling coefficient. Both are apparently temperature dependent, increasing markedly on approaching the Curie temperature.

  13. Development of a Flexible Lead-Free Piezoelectric Transducer for Health Monitoring in the Space Environment

    Directory of Open Access Journals (Sweden)

    Marco Laurenti

    2015-11-01

    Full Text Available In this work we report on the fabrication process for the development of a flexible piezopolymeric transducer for health monitoring applications, based on lead-free, piezoelectric zinc oxide (ZnO thin films. All the selected materials are compatible with the space environment and were deposited by the RF magnetron sputtering technique at room temperature, in view of preserving the total flexibility of the structures, which is an important requirement to guarantee coupling with cylindrical fuel tanks whose integrity we want to monitor. The overall transducer architecture was made of a c-axis-oriented ZnO thin film coupled to a pair of flexible Polyimide foils coated with gold (Au electrodes. The fabrication process started with the deposition of the bottom electrode on Polyimide foils. The ZnO thin film and the top electrode were then deposited onto the Au/Polyimide substrates. Both the electrodes and ZnO layer were properly patterned by wet-chemical etching and optical lithography. The assembly of the final structure was then obtained by gluing the upper and lower Polyimide foils with an epoxy resin capable of guaranteeing low outgassing levels, as well as adequate thermal and electrical insulation of the transducers. The piezoelectric behavior of the prototypes was confirmed and evaluated by measuring the mechanical displacement induced from the application of an external voltage.

  14. An equivalent dipole analysis of PZT ceramics and lead-free piezoelectric single crystals

    Science.gov (United States)

    Bell, Andrew J.

    2016-04-01

    The recently proposed Equivalent Dipole Model for describing the electromechanical properties of ionic solids in terms of 3 ions and 2 bonds has been applied to PZT ceramics and lead-free single crystal piezoelectric materials, providing analysis in terms of an effective ionic charge and the asymmetry of the interatomic force constants. For PZT it is shown that, as a function of composition across the morphotropic phase boundary, the dominant bond compliance peaks at 52% ZrO2. The stiffer of the two bonds shows little composition dependence with no anomaly at the phase boundary. The effective charge has a maximum value at 50% ZrO2, decreasing across the phase boundary region, but becoming constant in the rhombohedral phase. The single crystals confirm that both the asymmetry in the force constants and the magnitude of effective charge are equally important in determining the values of the piezoelectric charge coefficient and the electromechanical coupling coefficient. Both are apparently temperature dependent, increasing markedly on approaching the Curie temperature.

  15. Using the methods of radiospectroscopy (EPR, NMR) to study the nature of the defect structure of solid solutions based on lead zirconate titanate (PZT)

    Czech Academy of Sciences Publication Activity Database

    Bykov, I. P.; Zagorodniy, A.Y.; Yurchenko, L.P.; Korduban, A.M.; Nejezchleb, K.; Trachevsky, V.V.; Dimza, V.; Jastrabík, Lubomír; Dejneka, Alexandr

    2014-01-01

    Roč. 61, č. 8 (2014), 1379-1385 ISSN 0885-3010 R&D Projects: GA TA ČR TA01010517; GA ČR GAP108/12/1941 Institutional support: RVO:68378271 Keywords : lead zirconate titanate ( PZT ) * EPR * NMR * XPS spectroscopy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.512, year: 2014

  16. Fatigue and retention properties of shape memory piezoelectric actuator with non-180° domain switching

    International Nuclear Information System (INIS)

    Kadota, Y; Morita, T

    2012-01-01

    A shape memory piezoelectric actuator can maintain a piezoelectric displacement without an operating voltage. It has two stable strain states at zero voltage: a poled state and a depoled state. The driving principle of the shape memory piezoelectric actuator is based on reorientation of the non-180° domains in the ferroelectric materials. In this study, a unimorph shape memory piezoelectric actuator with a soft lead zirconate titanate was fabricated. The fatigue and retention properties of this shape memory piezoelectric actuator were investigated. The fatigue behavior of the actuator in the early stages is considered to be closely related to the domain stabilization process. Continuous cycle fatigue tests revealed that the shape memory piezoelectric actuator continues to operate even after 10 6 cycles. Retention measurements revealed that the depoled state of the actuator was more stable than the poled state. The drift in the actuator displacement over one year was estimated to be less than 10% of the initial shape memory displacement. (paper)

  17. Towards a digital sound reconstruction MEMS device: Characterization of a single PZT based piezoelectric actuator

    KAUST Repository

    Carreno, Armando Arpys Arevalo; Conchouso Gonzalez, David; Castro, David; Jaber, Nizar; Younis, Mohammad I.; Foulds, Ian G.

    2015-01-01

    of acoustic actuators. These actuators consist of a flexible membrane fabricated using polyimide, which is actuated using a Lead-Zirconate-Titanate (PZT) piezoelectric ceramic layer working in the d31 actuation mode. The dimensions of the membrane are of 1mm

  18. Ferroelectric and piezoelectric properties of epitaxial PZT films and devices on silicon

    NARCIS (Netherlands)

    Nguyen, Duc Minh

    2010-01-01

    In this thesis, the integration of lead zirconate titanate Pb(Zr,Ti)O3 (PZT) thin films into piezoelectric microelectromechanical systems (MEMS) based on silicon is studied. In these structures, all epitaxial oxide layers (thin film/electrode/buffer-layer(s)) were deposited by pulsed laser

  19. Shear wave propagation in piezoelectric-piezoelectric composite layered structure

    Directory of Open Access Journals (Sweden)

    Anshu Mli Gaur

    Full Text Available The propagation behavior of shear wave in piezoelectric composite structure is investigated by two layer model presented in this approach. The composite structure comprises of piezoelectric layers of two different materials bonded alternatively. Dispersion equations are derived for propagation along the direction normal to the layering and in direction of layering. It has been revealed that thickness and elastic constants have significant influence on propagation behavior of shear wave. The phase velocity and wave number is numerically calculated for alternative layer of Polyvinylidene Difluoride (PVDF and Lead Zirconate Titanate (PZT-5H in composite layered structure. The analysis carried out in this paper evaluates the effect of volume fraction on the phase velocity of shear wave.

  20. Pressure, temperature, and electric field dependence of phase transformations in niobium modified 95/5 lead zirconate titanate

    Energy Technology Data Exchange (ETDEWEB)

    Dong, Wen D.; Carlos Valadez, J.; Gallagher, John A.; Jo, Hwan R.; Lynch, Christopher S., E-mail: cslynch@seas.ucla.edu [Department of Mechanical and Aerospace Engineering, The University of California, Los Angeles, 420 Westwood Plaza, Los Angeles, California 90095 (United States); Sahul, Raffi; Hackenberger, Wes [TRS Technologies, 2820 East College Avenue, State College, Pennsylvania 16801 (United States)

    2015-06-28

    Ceramic niobium modified 95/5 lead zirconate-lead titanate (PZT) undergoes a pressure induced ferroelectric to antiferroelectric phase transformation accompanied by an elimination of polarization and a volume reduction. Electric field and temperature drive the reverse transformation from the antiferroelectric to ferroelectric phase. The phase transformation was monitored under pressure, temperature, and electric field loading. Pressures and temperatures were varied in discrete steps from 0 MPa to 500 MPa and 25 °C to 125 °C, respectively. Cyclic bipolar electric fields were applied with peak amplitudes of up to 6 MV m{sup −1} at each pressure and temperature combination. The resulting electric displacement–electric field hysteresis loops were open “D” shaped at low pressure, characteristic of soft ferroelectric PZT. Just below the phase transformation pressure, the hysteresis loops took on an “S” shape, which split into a double hysteresis loop just above the phase transformation pressure. Far above the phase transformation pressure, when the applied electric field is insufficient to drive an antiferroelectric to ferroelectric phase transformation, the hysteresis loops collapse to linear dielectric behavior. Phase stability maps were generated from the experimental data at each of the temperature steps and used to form a three dimensional pressure–temperature–electric field phase diagram.

  1. Dielectric and piezoelectric properties of lead-free (Bi,Na)TiO3-based thin films

    Science.gov (United States)

    Abazari, M.; Safari, A.; Bharadwaja, S. S. N.; Trolier-McKinstry, S.

    2010-02-01

    Dielectric and piezoelectric properties of morphotropic phase boundary (Bi,Na)TiO3-(Bi,K)TiO3-BaTiO3 epitaxial thin films deposited on SrRuO3 coated SrTiO3 substrates were reported. Thin films of 350 nm thickness exhibited small signal dielectric permittivity and loss tangent values of 750 and 0.15, respectively, at 1 kHz. Ferroelectric hysteresis measurements indicated a remanent polarization value of 30 μC/cm2 with a coercive field of 85-100 kV/cm. The thin film transverse piezoelectric coefficient (e31,f) of these films after poling at 600 kV/cm was found to be -2.2 C/m2. The results indicate that these BNT-based thin films are a potential candidate for lead-free piezoelectric devices.

  2. Voltage control of a magnetization easy axis in piezoelectric/ferromagnetic hybrid films

    International Nuclear Information System (INIS)

    Kim, Sang-Koog; Lee, Jeong-Won; Shin, Sung-Chul; Song, Han Wook; Lee, Chang Ho; No, Kwangsoo

    2003-01-01

    We have established a spontaneous magnetization-axis switching in ferromagnetic films by applying a low voltage to a piezoelectric layer in a newly developed hybrid system comprised of the ferromagnetic and piezoelectric films. The magnetization easy axis along which a spontaneous magnetization is oriented, is readily switchable by a voltage without applying an external magnetic field through both the inverse magnetostrictive and piezoelectric effects of CoPd and lead-zirconate-titanate alloy films, respectively. This challenging work provides a new way into the memory writing as well as storage means of ultrahigh bit densities in nonvolatile magnetic random access memory

  3. High Discharge Energy Density at Low Electric Field Using an Aligned Titanium Dioxide/Lead Zirconate Titanate Nanowire Array.

    Science.gov (United States)

    Zhang, Dou; Liu, Weiwei; Guo, Ru; Zhou, Kechao; Luo, Hang

    2018-02-01

    Polymer-based capacitors with high energy density have attracted significant attention in recent years due to their wide range of potential applications in electronic devices. However, the obtained high energy density is predominantly dependent on high applied electric field, e.g., 400-600 kV mm -1 , which may bring more challenges relating to the failure probability. Here, a simple two-step method for synthesizing titanium dioxide/lead zirconate titanate nanowire arrays is exploited and a demonstration of their ability to achieve high discharge energy density capacitors for low operating voltage applications is provided. A high discharge energy density of 6.9 J cm -3 is achieved at low electric fields, i.e., 143 kV mm -1 , which is attributed to the high relative permittivity of 218.9 at 1 kHz and high polarization of 23.35 µC cm -2 at this electric field. The discharge energy density obtained in this work is the highest known for a ceramic/polymer nanocomposite at such a low electric field. The novel nanowire arrays used in this work are applicable to a wide range of fields, such as energy harvesting, energy storage, and photocatalysis.

  4. Effects of Thickness, Pulse Duration, and Size of Strip Electrode on Ferroelectric Electron Emission of Lead Zirconate Titanate Films

    Science.gov (United States)

    Yaseen, Muhammad; Ren, Wei; Chen, Xiaofeng; Feng, Yujun; Shi, Peng; Wu, Xiaoqing

    2018-02-01

    Sol-gel-derived lead zirconate titanate (PZT) thin-film emitters with thickness up to 9.8 μm have been prepared on Pt/TiO2/SiO2/Si wafer via chemical solution deposition with/without polyvinylpyrrolidone (PVP) modification, and the relationship between the film thickness and electron emission investigated. Notable electron emission was observed on application of a trigger voltage of 120 V for PZT film with thickness of 1.1 μm. Increasing the film thickness decreased the threshold field to initiate electron emission for non-PVP-modified films. In contrast, the electron emission behavior of PVP-modified films did not show significant dependence on film thickness, probably due to their porous structure. The emission current increased with decreasing strip width and space between strips. Furthermore, it was observed that increasing the duration of the applied pulse increased the magnitude of the emission current. The stray field on the PZT film thickness was also calculated and found to increase with increasing ferroelectric sample thickness. The PZT emitters were found to be fatigue free up to 105 emission cycles. Saturated emission current of around 25 mA to 30 mA was achieved for the electrode pattern used in this work.

  5. Bath temperature effect on magnetoelectric performance of Ni-lead zirconate titanate-Ni laminated composites synthesized by electroless deposition

    Energy Technology Data Exchange (ETDEWEB)

    Wu, W. [College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016 (China); Wang, Y.G., E-mail: yingang.wang@nuaa.edu.c [College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016 (China); Bi, K. [College of Materials Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016 (China)

    2011-03-15

    Magnetoelectric (ME) Ni-lead zirconate titanate-Ni laminated composites have been prepared by electroless deposition at various bath temperatures. The structure of the Ni layers deposited at various bath temperatures was characterized by X-ray diffraction, and microstructures were investigated by transmission electron microscopy. The magnetostrictive coefficients were measured by means of a resistance strain gauge. The transverse ME voltage coefficient {alpha}{sub E,31} was measured with the magnetic field applied parallel to the sample plane. The deposition rate of Ni increases with bath temperature. Ni layer with smaller grain size is obtained at higher bath temperature and shows higher piezomagnetic coefficient, promoting the ME effect of corresponding laminated composites. It is advantageous to increase the bath temperature, while trying to avoid the breaking of bath constituents. - Research Highlights: Laminated composites without interlayer are prepared by electroless deposition. Bath temperature affects the grain size of the deposited Ni layers. Higher bath temperature is beneficial to obtain stronger ME response.

  6. Influence of poling on far-infrared response of lead zirconate titanate ceramics

    Czech Academy of Sciences Publication Activity Database

    Simon, E.; Hlinka, Jiří; Kamba, Stanislav; Gregora, Ivan; Erhart, J.

    2009-01-01

    Roč. 106, č. 7 (2009), 074104/1-074104/5 ISSN 0021-8979 R&D Projects: GA AV ČR KAN301370701; GA MŠk ME08109; GA ČR GA202/06/0411 Institutional research plan: CEZ:AV0Z10100520 Keywords : ceramics * dielectric polarisation * infrared spectra * lead compounds * phonons Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.072, year: 2009

  7. Effect of ultraviolet light on fatigue of lead zirconate titanate thin-film capacitors

    Science.gov (United States)

    Lee, J.; Esayan, S.; Safari, A.; Ramesh, R.

    1994-07-01

    Fatigue of Pb(Zr0.52Ti0.48)O3 (PZT) thin-film capacitors was studied under UV light (He-Cd laser, λ=325 nm). The remanent polarization of the PZT film capacitors increased upon light illumination. Fatigue resistance was also improved under UV light. During fatigue test, the change in polarization of PZT films upon UV light illumination increased gradually with cycling. These results were examined within the framework of the polarization screening model, which is suggested as an essential process for fatigue. This leads to a conclusion that more charged defects are involved in the fatigue process through internal screening of polarization.

  8. Defect enhanced optic and electro-optic properties of lead zirconate titanate thin films

    Directory of Open Access Journals (Sweden)

    M. M. Zhu

    2011-12-01

    Full Text Available Pb(Zr1-xTixO3 (PZT thin films near phase morphotropic phase boundary were deposited on (Pb0.86La0.14TiO3-coated glass by radio frequency sputtering. A retrieved analysis shows that the lattice parameters of the as-grown PZT thin films were similar to that of monoclinic PZT structure. Moreover, the PZT thin films possessed refractive index as high as 2.504 in TE model and 2.431 in TM model. The as-grown PZT thin film had one strong absorption peak at 632.6 nm, which attributed to lead deficiency by quantitative XPS analysis. From the attractive properties achieved, electro-optic and photovoltaic characteristic of the films were carried out.

  9. Electric field tuning of magnetism in heterostructure of yttrium iron garnet film/lead magnesium niobate-lead zirconate titanate ceramic

    Science.gov (United States)

    Lian, Jianyun; Ponchel, Freddy; Tiercelin, Nicolas; Chen, Ying; Rémiens, Denis; Lasri, Tuami; Wang, Genshui; Pernod, Philippe; Zhang, Wenbin; Dong, Xianlin

    2018-04-01

    In this paper, the converse magnetoelectric (CME) effect by electric field tuning of magnetization in an original heterostructure composed of a polycrystalline yttrium iron garnet (YIG) film and a lead magnesium niobate-lead zirconate titanate (PMN-PZT) ceramic is presented. The magnetic performances of the YIG films with different thicknesses under a DC electric field applied to the PMN-PZT ceramics and a bias magnetic field are investigated. All the magnetization-electric field curves are found to be in good agreement with the butterfly like strain curve of the PMN-PZT ceramic. Both the sharp deformation of about 2.5‰ of PMN-PZT and the easy magnetization switching of YIG are proposed to be the reasons for the strongest CME interaction in the composite at the small electric coercive field of PMN-PZT (4.1 kV/cm) and the small magnetic coercive field of YIG (20 Oe) where the magnetic susceptibility reaches its maximum value. A remarkable CME coefficient of 3.1 × 10-7 s/m is obtained in the system with a 600 nm-thick YIG film. This heterostructure combining multiferroics and partially magnetized ferrite concepts is able to operate under a small or even in the absence of an external bias magnetic field and is more compact and power efficient than the traditional magnetoelectric devices.

  10. Dynamic pyroelectric response of composite based on ferroelectric copolymer of poly(vinylidene fluoride-trifluoroethylene) and ferroelectric ceramics of barium lead zirconate titanate

    Energy Technology Data Exchange (ETDEWEB)

    Solnyshkin, A.V. [Tver State University, Department of Condensed Matter Physics, Tver (Russian Federation); National Research University ' ' MIET' ' , Department of Intellectual Technical Systems, Zelenograd, Moscow (Russian Federation); Morsakov, I.M.; Bogomolov, A.A. [Tver State University, Department of Condensed Matter Physics, Tver (Russian Federation); Belov, A.N.; Vorobiev, M.I.; Shevyakov, V.I.; Silibin, M.V. [National Research University ' ' MIET' ' , Department of Intellectual Technical Systems, Zelenograd, Moscow (Russian Federation); Shvartsman, V.V. [University of Duisburg-Essen, Institute for Materials Science, Essen (Germany)

    2015-10-15

    In this work, pyroelectric properties of composite films on the basis of poly(vinylidene fluoride-trifluoroethylene) copolymer with a various level of ferroelectric ceramics inclusions of barium lead zirconate titanate solid solution were investigated by the dynamic method. The composite films were prepared by the solvent cast method. The unusual spike-like dynamic response with a quasi-stationary component was observed. It is supposed that composite films may be effectively used for pyroelectric applications. (orig.)

  11. A polarized Raman study of the relaxor and ferroelectric states of La-modified lead zirconate titanate ceramics

    International Nuclear Information System (INIS)

    El Marssi, M.; Farhi, R.; Viehland, D.

    1997-01-01

    Lanthanum modified lead zirconate titanate ceramics with La/Zr/Ti ratios of 6/40/60, 12/40/60, 5/65/35, and 9/65/35 have been studied by polarized Raman scattering. In the two former (tetragonal-type) compositions, selection rules were rather well defined and allowed an assignment of the Raman lines at lower temperature. These selection rules disappeared for 6/40/60 but remained for 12/40/60 even at higher temperatures. The behavior of the two latter (rhombohedral-type compositions) was quite different. No assignment of lines could be done. In addition, the spectra recorded in parallel and crossed polarizations were almost identical for 5/65/35 regardless of temperature. A very smeared paraelectric to ferroelectric transition was evidenced by Raman intensity measurements for this composition. On the contrary, selection rules were always present for the relaxor composition 9/65/35 which were similar to those for 12/40/60 and 6/40/60. This suggests that both tetragonal and rhombohedral-type local polar order is present for 9/65/35. The spectra of the field induced ferroelectric phase for 9/65/35 revealed no selection rules, similar to 5/65/35. This is attributed to the onset of only medium range ferroelectric order. Finally, Raman spectra recorded on powders of every composition did not reveal any selection rules, suggesting that intergranular effects might play a significant role in the behavior of these materials. copyright 1997 American Institute of Physics

  12. X-ray and neutron scattering on disordered nanosize clusters: a case study of lead-zirconate-titanate solid solutions

    Energy Technology Data Exchange (ETDEWEB)

    Frantti, Johannes; Fujioka, Yukari [Finnish Research and Engineering, Helsinki (Finland)

    2015-04-01

    Defects and frequently used defect models of solids are reviewed. Signatures for identifying the disorder from x-ray and neutron scattering data are given. To give illustrative examples how technologically important defects contribute to x-ray and neutron scattering numerical method able to treat non-periodical solids possessing several simultaneous defect types is given for simulating scattering in nanosize disordered clusters. The approach takes particle size, shape, and defects into account and isolates element specific signals. As a case study a statistical approximation model for lead-zirconate titanate [Pb(Zr{sub x}Ti{sub 1-x})O{sub 3}, PZT] is introduced. PZT is a material possessing several defect types, including substitutional, displacement and surface defects. Spatial composition variation is taken into account by introducing a model in which the edge lengths of each cell depend on the distribution of Zr and Ti ions in the cluster. Spatially varying edge lengths and angles is referred to as microstrain. The model is applied to compute the scattering from ellipsoid shaped PZT clusters and to simulate the structural changes as a function of average composition. Two-phase co-existence range, the so called morphotropic phase boundary composition is given correctly. The composition at which the rhombohedral and tetragonal cells are equally abundant was x ∼ 0.51. Selected x-ray and neutron Bragg reflection intensities and line shapes were simulated. Examples of the effect of size and shape of the scattering clusters on diffraction patterns are given and the particle dimensions, computed through Scherrer equation, are compared with the exact cluster dimensions. Scattering from two types of 180 domains in spherical particles, one type assigned to Ti-rich PZT and the second to the MPB and Zr-rich PZT, is computed. We show how the method can be used for modelling polarization reversal. (copyright 2015 by WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  13. Piezoelectric and ferroelectric properties of lead-free niobium-rich potassium lithium tantalate niobate single crystals

    Energy Technology Data Exchange (ETDEWEB)

    Li, Jun, E-mail: lijuna@hit.edu.cn [Department of Physics, Harbin Institute of Technology, Harbin 150001 (China); Li, Yang [Department of chemistry, Harbin Institute of Technology, Harbin 150001 (China); Zhou, Zhongxiang [Department of Physics, Harbin Institute of Technology, Harbin 150001 (China); Guo, Ruyan; Bhalla, Amar S. [Multifunctional Electronic Materials and Device Research Lab, Department of Electrical and Computer Engineering, The University of Texas at San Antonio, San Antonio 78249 (United States)

    2014-01-01

    Graphical abstract: - Highlights: • Lead-free K{sub 0.95}Li{sub 0.05}Ta{sub 1−x}Nb{sub x}O{sub 3} single crystals were grown using the top-seeded melt growth method. • The piezoelectric and ferroelectric properties of as-grown crystals were systematically investigated. • The piezoelectric properties are very attractive, e.g. for x = 0.60 composition, k{sub t} ≈ 70%, k{sub 31} ≈ 70%, k{sub 33} ≈ 77%, d{sub 31} ≈ 230 pC/N, d{sub 33} ≈ 600 pC/N. • The coercive fields of P–E hysteresis loops are quite small, about or less than 1 kV/mm. - Abstract: Lead-free potassium lithium tantalate niobate single crystals with the composition of K{sub 0.95}Li{sub 0.05}Ta{sub 1−x}Nb{sub x}O{sub 3} (abbreviated as KLTN, x = 0.51, 0.60, 0.69, 0.78) were grown using the top-seeded melt growth method. Their piezoelectric and ferroelectric properties in as-grown crystals have been systematically investigated. The phase transitions and Curie temperatures were determined from dielectric and pyroelectric measurements. Piezoelectric coefficients and electromechanical coupling factors in thickness mode, length-extensional mode and longitudinal mode were obtained. The piezoelectric properties are very attractive, e.g. for x = 0.60 composition, k{sub t} ≈ 70%, k{sub 31} ≈ 70%, k{sub 33} ≈ 77%, d{sub 31} ≈ 230 pC/N, d{sub 33} ≈ 600 pC/N are comparable to the lead-based PZT composition. The polarization versus electric field hysteresis loops show saturated shapes. In short, lead-free niobium-rich KLTN system possesses comparable properties to those in important lead-based piezoelectric material nowadays.

  14. Growth and characterization of lead-free (K,Na)NbO3-based piezoelectric single crystals

    International Nuclear Information System (INIS)

    Liu, Hairui

    2016-01-01

    Lead-free piezoelectric materials have received increasing attention in the last decade, driven by environmental issues and health concerns. Of considerable interest is the (K,Na)NbO 3 (KNN)-based system, which possesses a relatively high Curie temperature and good piezoelectric properties. Abundant publications on KNN-based polycrystalline ceramics increased the interest in studying their single-crystalline form, based on two major concerns. The first concern refers to the negative role of grain interactions on the electromechanical response. The second concern deals with domain engineering. The relationship between external electric field direction, crystallographic orientation, and spontaneous polarization vectors for a specific structure can be more readily established in single crystals and thus offers a pathway for an in-depth understanding of fundamental mechanism and potential applications. The exciting enhancement of both piezoelectric and ferroelectric response in lead-based single crystals also encourages the further exploration of KNN-based piezoelectric crystals, as they possess the same perovskite structure. The main goal of this thesis is to find possible approaches for improved electromechanical properties in KNN-based piezoelectric single crystals. In Chapter 2, the current development of KNN-based single crystals as piezoelectrics is reviewed, following a short introduction of fundamental knowledge on piezoelectrics and ferroelectrics. Both submerged-seed solution growth and top-seeded solution growth techniques were employed to produce single crystals, as described detailed in Chapter 3. Emphasis is subsequently placed on issues of the crystal growth process, effective methods to enhance electrical properties, and crystallographic orientation-dependent electrical properties in Li-, Ta-, and/or Sb-substituted KNN single crystals. The main conclusions from the crystal growth aspect are presented in Chapter 4 and can be summarized as follows: (i

  15. Growth and characterization of lead-free (K,Na)NbO{sub 3}-based piezoelectric single crystals

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Hairui

    2016-10-19

    Lead-free piezoelectric materials have received increasing attention in the last decade, driven by environmental issues and health concerns. Of considerable interest is the (K,Na)NbO{sub 3} (KNN)-based system, which possesses a relatively high Curie temperature and good piezoelectric properties. Abundant publications on KNN-based polycrystalline ceramics increased the interest in studying their single-crystalline form, based on two major concerns. The first concern refers to the negative role of grain interactions on the electromechanical response. The second concern deals with domain engineering. The relationship between external electric field direction, crystallographic orientation, and spontaneous polarization vectors for a specific structure can be more readily established in single crystals and thus offers a pathway for an in-depth understanding of fundamental mechanism and potential applications. The exciting enhancement of both piezoelectric and ferroelectric response in lead-based single crystals also encourages the further exploration of KNN-based piezoelectric crystals, as they possess the same perovskite structure. The main goal of this thesis is to find possible approaches for improved electromechanical properties in KNN-based piezoelectric single crystals. In Chapter 2, the current development of KNN-based single crystals as piezoelectrics is reviewed, following a short introduction of fundamental knowledge on piezoelectrics and ferroelectrics. Both submerged-seed solution growth and top-seeded solution growth techniques were employed to produce single crystals, as described detailed in Chapter 3. Emphasis is subsequently placed on issues of the crystal growth process, effective methods to enhance electrical properties, and crystallographic orientation-dependent electrical properties in Li-, Ta-, and/or Sb-substituted KNN single crystals. The main conclusions from the crystal growth aspect are presented in Chapter 4 and can be summarized as follows

  16. Evaluation of electromechanical coupling parameters of piezoelectric materials by using piezoelectric cantilever with coplanar electrode structure in quasi-stasis.

    Science.gov (United States)

    Zheng, Xuejun; Zhu, Yuankun; Liu, Xun; Liu, Jing; Zhang, Yong; Chen, Jianguo

    2014-02-01

    Based on Timoshenko beam theory, a principle model is proposed to establish the relationship between electric charge and excitation acceleration, and in quasi-stasis we apply the direct piezoelectric effect of multilayer cantilever with coplanar electrode structure to evaluate the piezoelectric strain coefficient d15 and electromechanical coupling coefficient k15. They are measured as 678 pC/N and 0.74 for the commercial piezoelectric ceramic lead zirconate titanate (PZT-51) bulk specimen and 656 pC/N and 0.63 for the lead magnesium niobate (PMN) bulk specimen, and they are in agreement with the calibration and simulation values. The maximum of relative errors is less than 4.2%, so the proposed method is reliable and convenient.

  17. PZT/PLZT - elastomer composites with improved piezoelectric voltage coefficient

    Science.gov (United States)

    Harikrishnan, K.; Bavbande, D. V.; Mohan, Dhirendra; Manoharan, B.; Prasad, M. R. S.; Kalyanakrishnan, G.

    2018-02-01

    Lead Zirconate Titanate (PZT) and Lanthanum-modified Lead Zirconate Titanate (PLZT) ceramic sensor materials are widely used because of their excellent piezoelectric coefficients. These materials are brittle, high density and have low achievable piezoelectric voltage coefficients. The density of the sintered ceramics shall be reduced by burnable polymeric sponge method. The achievable porosity level in this case is nearly 60 - 90%. However, the porous ceramic structure with 3-3 connectivity produced by this method is very fragile in nature. The strength of the porous structure is improved with Sylgard®-184 (silicone elastomer) by vacuum impregnation method maintaining the dynamic vacuum level in the range of -650 mm Hg. The elastomer Sylgard®-184 is having low density, low dielectric constant and high compliance (as a resultant stiffness of the composites is increased). To obtain a net dipole moment, the impregnated ceramic composites were subjected to poling treatment with varying conditions of D.C. field and temperature. The properties of the poled PZT/PLZT - elastomer composites were characterized with LCR meter for measuring the dielectric constant values (k), d33 meter used for measuring piezo-electric charge coefficient values (d33) and piezo-electric voltage coefficient (g33) values which were derived from d33 values. The voltage coefficient (g33) values of these composites are increased by 10 fold as compared to the conventional solid ceramics demonstrates that it is possible to fabricate a conformable detector.

  18. Wafer-scale growth of highly textured piezoelectric thin films by pulsed laser deposition for micro-scale sensors and actuators

    Science.gov (United States)

    Nguyen, M. D.; Tiggelaar, R.; Aukes, T.; Rijnders, G.; Roelof, G.

    2017-11-01

    Piezoelectric lead-zirconate-titanate (PZT) thin films were deposited on 4-inch (111)Pt/Ti/SiO2/Si(001) wafers using large-area pulsed laser deposition (PLD). This study was focused on the homogeneity in film thickness, microstructure, ferroelectric and piezoelectric properties of PZT thin films. The results indicated that the highly textured (001)-oriented PZT thin films with wafer-scale thickness homogeneity (990 nm ± 0.8%) were obtained. The films were fabricated into piezoelectric cantilevers through a MEMS microfabrication process. The measured longitudinal piezoelectric coefficient (d 33f = 210 pm/V ± 1.6%) and piezoelectric transverse coefficient (e 31f = -18.8 C/m2 ± 2.8%) were high and homogeneity across wafers. The high piezoelectric properties on Si wafers will extend industrial application of PZT thin films and further development of piezoMEMS.

  19. Giant Piezoelectricity and High Curie Temperature in Nanostructured Alkali Niobate Lead-Free Piezoceramics through Phase Coexistence.

    Science.gov (United States)

    Wu, Bo; Wu, Haijun; Wu, Jiagang; Xiao, Dingquan; Zhu, Jianguo; Pennycook, Stephen J

    2016-11-30

    Because of growing environmental concerns, the development of lead-free piezoelectric materials with enhanced properties has become of great interest. Here, we report a giant piezoelectric coefficient (d 33 ) of 550 pC/N and a high Curie temperature (T C ) of 237 °C in (1-x-y)K 1-w Na w Nb 1-z Sb z O 3- xBiFeO 3- yBi 0.5 Na 0.5 ZrO 3 (KN w NS z -xBF-yBNZ) ceramics by optimizing x, y, z, and w. Atomic-resolution polarization mapping by Z-contrast imaging reveals the intimate coexistence of rhombohedral (R) and tetragonal (T) phases inside nanodomains, that is, a structural origin for the R-T phase boundary in the present KNN system. Hence, the physical origin of high piezoelectric performance can be attributed to a nearly vanishing polarization anisotropy and thus low domain wall energy, facilitating easy polarization rotation between different states under an external field.

  20. Dielectric properties of composite based on ferroelectric copolymer of poly(vinylidene fluoride-trifluoroethylene and ferroelectric ceramics of barium lead zirconate titanate

    Directory of Open Access Journals (Sweden)

    A. V. Solnyshkin

    2017-10-01

    Full Text Available A study of dielectric properties of composite films on the base of poly(vinylidene fluoride-trifluoroethylene copolymer P(VDF-TrFE and ferroelectric ceramics of barium lead zirconate titanate (BPZT solid solution is presented in this work. The composite films containing up to 50 vol.% of BPZT grains with size ∼1μm were prepared by the solvent cast method. Frequency dependences of real and imaginary components of the complex permittivity were determined. The concentration dependence of the dielectric constant was discussed.

  1. Phase transition characteristics and associated piezoelectricity of potassium-sodium niobate lead-free ceramics.

    Science.gov (United States)

    Wang, Yuanyu; Hu, Liang; Zhang, Qilong; Yang, Hui

    2015-08-14

    To achieve high piezoelectric activity and a wide sintering temperature range, the ceramic system concerning (1 - x)(K(0.48)Na(0.52))(Nb(0.96)Sb(0.04))O(3)-x[Bi(0.5)(Na(0.7)Ag(0.3))(0.5)](0.90) Zn(0.10)ZrO(3) was designed, and the rhombohedral-tetragonal (R-T) phase boundary can drive a high d(33). Phase transition characteristics as well as their effects on the electrical properties were investigated systematically. The R-T coexistence phase boundary (0.04 ≤ x ≤ 0.05) can be driven via modification with BNAZZ, and has been confirmed by XRD and temperature-dependent dielectric constants as well as Raman analysis, and the ceramics possess enhanced piezoelectric properties (d(33) ∼ 425 pC N(-1) and k(p) ∼ 0.43) and a high unipolar strain (∼0.3%). In addition, a wide sintering temperature range of 1050-1080 °C can warrant a large d(33) of 400-430 pC N(-1), which can benefit practical applications. As a result, the addition of BNAZZ is an effective method to improve the electrical properties (piezoelectricity and strain) and sintering behavior of potassium-sodium niobate ceramics.

  2. Effect of poling process on piezoelectric properties of BCZT - 0.08 wt.% CeO{sub 2} lead-free ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Chandrakala, E.; Praveen, J. Paul; Das, Dibakar, E-mail: ddse@uohyd.ernet.in [School of Engineering Sciences & Technology, University of Hyderabad, Hyderabad 500046 (India)

    2016-05-06

    The properties of lead free piezoelectric materials can be tuned by suitable doping in the A and B sites of the perovskite structure. In the present study, cerium has been identified as a dopant to investigate the piezoelectric properties of lead-free BCZT system. BCZT – 0.08 wt.%CeO{sub 2} lead-free ceramics have been synthesized using sol-gel technique and the effects of CeO{sub 2} dopant on their phase structure and piezoelectric properties were investigated systematically. Poling conditions, such as temperature, electric field, and poling time have been optimized to get enhanced piezoelectric response. The optimized poling conditions (50°C, 3Ec and 30min) resulted in high piezoelectric charge coefficient d{sub 33} ~ 670pC/N, high electromechanical coupling coefficient k{sub p} ~ 60% and piezoelectric voltage coefficient g{sub 33} ~ 14 mV.m/N for BCZT – 0.08wt.% CeO{sub 2} ceramics.

  3. Stress engineering for the design of morphotropic phase boundary in piezoelectric material

    Energy Technology Data Exchange (ETDEWEB)

    Ohno, Tomoya, E-mail: ohno@mail.kitami-it.ac.jp [Department of Materials Science, Kitami Institute of Technology, 165 Kouen-cho, Kitami 090-8507 (Japan); Yanagida, Hiroshi; Maekawa, Kentaroh [Department of Materials Science, Kitami Institute of Technology, 165 Kouen-cho, Kitami 090-8507 (Japan); Arai, Takashi; Sakamoto, Naonori; Wakiya, Naoki; Suzuki, Hisao [Graduate School of Science and Technology, Shizuoka University, 3-5-1 Johoku, Hamamatsu, Shizuoka 432-8561 (Japan); Satoh, Shigeo [Graduate School of Science and Engineering, Ibaragi University, 4-12-1 Nakanarusawa-cho, Hitachi, Ibaragi 316-0033 (Japan); Matsuda, Takeshi [Department of Materials Science, Kitami Institute of Technology, 165 Kouen-cho, Kitami 090-8507 (Japan)

    2015-06-30

    Alkoxide-derived lead zirconate titanate thin films having Zr/Ti = 50/50 to 60/40 compositions with different residual stress conditions were deposited on a Si wafer to clarify the effects of the residual stress on the morphotropic phase boundary shift. The residual stress condition was controlled to − 0.1 to − 0.9 GPa by the design of the buffer layer structure on the Si wafer. Results show that the maximum effective piezoelectric constant d{sub 33} was obtained at 58/42 composition under − 0.9 GPa compressive residual stress condition. Moreover, the MPB composition shifted linearly to Zr-rich phase with increasing compressive residual stress. - Highlights: • The residual stress in lead zirconate titanate film on silicon was controlled. • The maximum residual stress in lead zirconate titanate film was − 0.9 GPa. • The morphotropic phase boundary shifted to zirconium rich phase by the strain.

  4. Correlation between the structure and the piezoelectric properties of lead-free (K,Na,Li)(Nb,Ta,Sb)O3 ceramics studied by XRD and Raman spectroscopy.

    Science.gov (United States)

    Rubio-Marcos, Fernando; Marchet, Pascal; Romero, Juan José; Fernández, Jose F

    2011-09-01

    This article reviews on the use of Raman spectroscopy for the study of (K,Na,Li)(Nb,Ta,Sb)O(3) lead-free piezoceramics. Currently, this material appears to be one of the most interesting and promising alternatives to the well-known PZT piezoelectric materials. In this work, we prepare piezoceramics with different stoichiometries and study their structural, ferroelectric, and piezoelectric properties. By using both Raman spectroscopy and X-ray diffraction, we establish a direct correlation between the structure and the properties. The results demonstrate that the wavenumber of the A(1g) vibration is proportional to the tetragonality, the remnant polarization, and the piezoelectric coefficients of these materials. Thus, Raman spectroscopy appears as a very useful technique for a fast evaluation of the crystalline structure and the ferroelectric/ piezoelectric properties.

  5. Misfit strain-film thickness phase diagrams and related electromechanical properties of epitaxial ultra-thin lead zirconate titanate films

    Energy Technology Data Exchange (ETDEWEB)

    Qiu, Q.Y.; Mahjoub, R. [School of Materials Science and Engineering, University of New South Wales, Sydney, NSW 2052 (Australia); Alpay, S.P. [Materials Science and Engineering Program and Institute of Materials Science, University of Connecticut, Storrs, CT 06269 (United States); Nagarajan, V., E-mail: nagarajan@unsw.edu.au [School of Materials Science and Engineering, University of New South Wales, Sydney, NSW 2052 (Australia)

    2010-02-15

    The phase stability of ultra-thin (0 0 1) oriented ferroelectric PbZr{sub 1-x}Ti{sub x}O{sub 3} (PZT) epitaxial thin films as a function of the film composition, film thickness, and the misfit strain is analyzed using a non-linear Landau-Ginzburg-Devonshire thermodynamic model taking into account the electrical and mechanical boundary conditions. The theoretical formalism incorporates the role of the depolarization field as well as the possibility of the relaxation of in-plane strains via the formation of microstructural features such as misfit dislocations at the growth temperature and ferroelastic polydomain patterns below the paraelectric-ferroelectric phase transformation temperature. Film thickness-misfit strain phase diagrams are developed for PZT films with four different compositions (x = 1, 0.9, 0.8 and 0.7) as a function of the film thickness. The results show that the so-called rotational r-phase appears in a very narrow range of misfit strain and thickness of the film. Furthermore, the in-plane and out-of-plane dielectric permittivities {epsilon}{sub 11} and {epsilon}{sub 33}, as well as the out-of-plane piezoelectric coefficients d{sub 33} for the PZT thin films, are computed as a function of misfit strain, taking into account substrate-induced clamping. The model reveals that previously predicted ultrahigh piezoelectric coefficients due to misfit-strain-induced phase transitions are practically achievable only in an extremely narrow range of film thickness, composition and misfit strain parameter space. We also show that the dielectric and piezoelectric properties of epitaxial ferroelectric films can be tailored through strain engineering and microstructural optimization.

  6. Bismuth Sodium Titanate Based Materials for Piezoelectric Actuators.

    Science.gov (United States)

    Reichmann, Klaus; Feteira, Antonio; Li, Ming

    2015-12-04

    The ban of lead in many electronic products and the expectation that, sooner or later, this ban will include the currently exempt piezoelectric ceramics based on Lead-Zirconate-Titanate has motivated many research groups to look for lead-free substitutes. After a short overview on different classes of lead-free piezoelectric ceramics with large strain, this review will focus on Bismuth-Sodium-Titanate and its solid solutions. These compounds exhibit extraordinarily high strain, due to a field induced phase transition, which makes them attractive for actuator applications. The structural features of these materials and the origin of the field-induced strain will be revised. Technologies for texturing, which increases the useable strain, will be introduced. Finally, the features that are relevant for the application of these materials in a multilayer design will be summarized.

  7. Fabrication of high-power piezoelectric transformers using lead-free ceramics for application in electronic ballasts.

    Science.gov (United States)

    Yang, Song-Ling; Chen, Shih-Ming; Tsai, Cheng-Che; Hong, Cheng-Shong; Chu, Sheng-Yuan

    2013-02-01

    CuO is doped into (Na(0.5)K(0.5))NbO(3) (NKN) ceramics to improve the piezoelectric properties and thus obtain a piezoelectric transformer (PT) with high output power. In X-ray diffraction patterns, the diffraction angles of the CuO-doped NKN ceramics shift to lower values because of an expansion of the lattice volume, thus inducing oxygen vacancies and enhancing the mechanical quality factor. A homogeneous microstructure is obtained when NKN is subjected to CuO doping, leading to improved electrical properties. PTs with different electrode areas are fabricated using the CuO-doped NKN ceramics. Considering the efficiency, voltage gain, and temperature rise of PTs at a load resistance of 1 kΩ, PTs with an electrode with an inner diameter of 15 mm are combined with the circuit design for driving a 13-W T5 fluorescent lamp. A temperature rise of 6°C and a total efficiency of 82.4% (PT and circuit) are obtained using the present PTs.

  8. Large Piezoelectric Strain with Superior Thermal Stability and Excellent Fatigue Resistance of Lead-Free Potassium Sodium Niobate-Based Grain Orientation-Controlled Ceramics.

    Science.gov (United States)

    Quan, Yi; Ren, Wei; Niu, Gang; Wang, Lingyan; Zhao, Jinyan; Zhang, Nan; Liu, Ming; Ye, Zuo-Guang; Liu, Liqiang; Karaki, Tomoaki

    2018-03-19

    Environment-friendly lead-free piezoelectric materials with high piezoelectric response and high stability in a wide temperature range are urgently needed for various applications. In this work, grain orientation-controlled (with a 90% ⟨001⟩ c -oriented texture) (K,Na)NbO 3 -based ceramics with a large piezoelectric response ( d 33 *) = 505 pm V -1 and a high Curie temperature ( T C ) of 247 °C have been developed. Such a high d 33 * value varies by less than 5% from 30 to 180 °C, showing a superior thermal stability. Furthermore, the high piezoelectricity exhibits an excellent fatigue resistance with the d 33 * value decreasing within only by 6% at a field of 20 kV cm -1 up to 10 7 cycles. These exceptional properties can be attributed to the vertical morphotropic phase boundary and the highly ⟨001⟩ c -oriented textured ceramic microstructure. These results open a pathway to promote lead-free piezoelectric ceramics as a viable alternative to lead-based piezoceramics for various practical applications, such as actuators, transducers, sensors, and acoustic devices, in a wide temperature range.

  9. Growth of Ca, Zr co-doped BaTiO3 lead-free ferroelectric single crystal and its room-temperature piezoelectricity

    Directory of Open Access Journals (Sweden)

    Donglin Liu

    2017-09-01

    Full Text Available Lead-free Ca, Zr co-doped BaTiO3 (BCZT single crystal with a dimension up to 2mm×2mm×2mm was grown by a spontaneous nucleation technique using KF as the flux. The composition of the studied single crystal was defined to be Ba0.798Ca0.202Zr0.006Ti0.994O3, corresponding to a tetragonal phase at room temperature. The oriented single crystal exhibited a quasi-static piezoelectric constant of approximately 232 pC/N. The effective piezoelectric coefficient d33* of the single domain crystal obtained under a unipolar electric field of 35 kV/cm was 179 pm/V. Rayleigh analysis was used to identify the intrinsic and extrinsic contributions to the room-temperature piezoelectricity of BCZT single crystal. The extrinsic contribution was estimated up to 40% due to the irreversible domain wall movement. Furthermore a sixth-order polynomial of Landau expansion was employed to analyze the intrinsic contribution to piezoelectricity of BCZT single crystal. The large energy barriers inhibited polarization rotations, leading to the relatively low piezoelectricity.

  10. Role of sintering time, crystalline phases and symmetry in the piezoelectric properties of lead-free KNN-modified ceramics

    International Nuclear Information System (INIS)

    Rubio-Marcos, F.; Marchet, P.; Merle-Mejean, T.; Fernandez, J.F.

    2010-01-01

    Lead-free KNN-modified piezoceramics of the system (Li,Na,K)(Nb,Ta,Sb)O 3 were prepared by conventional solid-state sintering. The X-ray diffraction patterns revealed a perovskite phase, together with some minor secondary phase, which was assigned to K 3 LiNb 6 O 17 , tetragonal tungsten-bronze (TTB). A structural evolution toward a pure tetragonal structure with the increasing sintering time was observed, associated with the decrease of TTB phase. A correlation between higher tetragonality and higher piezoelectric response was clearly evidenced. Contrary to the case of the LiTaO 3 modified KNN, very large abnormal grains with TTB structure were not detected. As a consequence, the simultaneous modification by tantalum and antimony seems to induce during sintering a different behaviour from the one of LiTaO 3 modified KNN.

  11. Role of sintering time, crystalline phases and symmetry in the piezoelectric properties of lead-free KNN-modified ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Rubio-Marcos, F., E-mail: frmarcos@icv.csic.es [Electroceramic Department, Instituto de Ceramica y Vidrio, CSIC, Kelsen 5, 28049 Madrid (Spain); Marchet, P.; Merle-Mejean, T. [SPCTS, UMR 6638 CNRS, Universite de Limoges, 123, Av. A. Thomas, 87060 Limoges (France); Fernandez, J.F. [Electroceramic Department, Instituto de Ceramica y Vidrio, CSIC, Kelsen 5, 28049 Madrid (Spain)

    2010-09-01

    Lead-free KNN-modified piezoceramics of the system (Li,Na,K)(Nb,Ta,Sb)O{sub 3} were prepared by conventional solid-state sintering. The X-ray diffraction patterns revealed a perovskite phase, together with some minor secondary phase, which was assigned to K{sub 3}LiNb{sub 6}O{sub 17}, tetragonal tungsten-bronze (TTB). A structural evolution toward a pure tetragonal structure with the increasing sintering time was observed, associated with the decrease of TTB phase. A correlation between higher tetragonality and higher piezoelectric response was clearly evidenced. Contrary to the case of the LiTaO{sub 3} modified KNN, very large abnormal grains with TTB structure were not detected. As a consequence, the simultaneous modification by tantalum and antimony seems to induce during sintering a different behaviour from the one of LiTaO{sub 3} modified KNN.

  12. Dielectric and piezoelectric properties of BiFeO3 modified Bi0.5Na0.5TiO3-Bi0.5K0.5TiO3 lead-free piezoelectric ceramics

    International Nuclear Information System (INIS)

    Zhou Changrong; Liu Xinyu; Li Weizhou

    2008-01-01

    The (0.82 - x)Bi 0.5 Na 0.5 TiO 3 -0.18Bi 0.5 K 0.5 TiO 3 -xBiFeO 3 (x = 0-0.07) lead-free piezoelectric ceramics were fabricated by a conventional solid-state reaction method and the effect of BiFeO 3 addition on microstructure and electrical properties of the ceramics was investigated. The specimens with x ≤ 0.05 maintained a rhombohedral-tetragonal phase coexistence and changed into a rhombohedral phase when x > 0.05 in crystal structure. The addition of BiFeO 3 caused a promoted grain growth. All the specimens reveal a low-frequency dielectric dispersion in the frequency range of 40-1 MHz. The piezoelectric constant d 33 and the electromechanical coupling factor k p show an obvious improvement by the addition of small amount of BiFeO 3 , which shows optimum values of d 33 = 170 pC/N and k p = 0.366 at x = 0.03. Contrary to the enhancement of piezoelectric properties, Q m decreases with increasing BiFeO 3 content. The mechanisms of intrinsic and extrinsic contributions to the dielectric and piezoelectric responses have been proposed. Intrinsic contributions are from the relative ion/cation shift that preserves the ferroelectric crystal structure. The remaining extrinsic contributions are from the domain-wall motion and point defects

  13. Control of piezoelectricity in amino acids by supramolecular packing.

    Science.gov (United States)

    Guerin, Sarah; Stapleton, Aimee; Chovan, Drahomir; Mouras, Rabah; Gleeson, Matthew; McKeown, Cian; Noor, Mohamed Radzi; Silien, Christophe; Rhen, Fernando M F; Kholkin, Andrei L; Liu, Ning; Soulimane, Tewfik; Tofail, Syed A M; Thompson, Damien

    2018-02-01

    Piezoelectricity, the linear relationship between stress and induced electrical charge, has attracted recent interest due to its manifestation in biological molecules such as synthetic polypeptides or amino acid crystals, including gamma (γ) glycine. It has also been demonstrated in bone, collagen, elastin and the synthetic bone mineral hydroxyapatite. Piezoelectric coefficients exhibited by these biological materials are generally low, typically in the range of 0.1-10 pm V -1 , limiting technological applications. Guided by quantum mechanical calculations we have measured a high shear piezoelectricity (178 pm V -1 ) in the amino acid crystal beta (β) glycine, which is of similar magnitude to barium titanate or lead zirconate titanate. Our calculations show that the high piezoelectric coefficients originate from an efficient packing of the molecules along certain crystallographic planes and directions. The highest predicted piezoelectric voltage constant for β-glycine crystals is 8 V mN -1 , which is an order of magnitude larger than the voltage generated by any currently used ceramic or polymer.

  14. Control of piezoelectricity in amino acids by supramolecular packing

    Science.gov (United States)

    Guerin, Sarah; Stapleton, Aimee; Chovan, Drahomir; Mouras, Rabah; Gleeson, Matthew; McKeown, Cian; Noor, Mohamed Radzi; Silien, Christophe; Rhen, Fernando M. F.; Kholkin, Andrei L.; Liu, Ning; Soulimane, Tewfik; Tofail, Syed A. M.; Thompson, Damien

    2018-02-01

    Piezoelectricity, the linear relationship between stress and induced electrical charge, has attracted recent interest due to its manifestation in biological molecules such as synthetic polypeptides or amino acid crystals, including gamma (γ) glycine. It has also been demonstrated in bone, collagen, elastin and the synthetic bone mineral hydroxyapatite. Piezoelectric coefficients exhibited by these biological materials are generally low, typically in the range of 0.1-10 pm V-1, limiting technological applications. Guided by quantum mechanical calculations we have measured a high shear piezoelectricity (178 pm V-1) in the amino acid crystal beta (β) glycine, which is of similar magnitude to barium titanate or lead zirconate titanate. Our calculations show that the high piezoelectric coefficients originate from an efficient packing of the molecules along certain crystallographic planes and directions. The highest predicted piezoelectric voltage constant for β-glycine crystals is 8 V mN-1, which is an order of magnitude larger than the voltage generated by any currently used ceramic or polymer.

  15. PLZT-based photovoltaic Piezoelectric Transformer with light feedback

    Energy Technology Data Exchange (ETDEWEB)

    Kozielski, L [University of Silesia, Dep. Materials Sc, 2, Sniezna St. Sosnowiec, 41-200 Poland (Poland); Adamczyk, M [University of Silesia, Institute Phys., 4, Uniwersytecka St. Katowice, 40-007 Poland (Poland); Erhart, J, E-mail: lucjan.kozielski@us.edu.pl [Technical University of Liberec, Studencka St. 2, CZ-461 17 Liberec (Czech Republic)

    2011-10-29

    Piezoelectric Transformer (PT) converts an electrical AC input voltage into ultrasonic vibrations and reconverts back to an output as AC voltage. Hard lead zirconate titanate (PZT) ceramics is typically used for fabrications of such devices. In case of lanthaniun ion La{sup 3+} addition in PZT solid solution we can achieve piezoelectric ceramics with good transparency exhibiting both optical Pockels and Kerr effects. Values of these coefficients in the PLZT system are much bigger than in LiNbO{sub 3} or SBN single crystals. Among the various PLZT compositions 8/65/35, near the morphotropic boundary, exhibit large electrooptic effect and thus have found applications in light shutters and displays. In the present study we have investigated radial mode piezoelectric transformer based on optically transparent PLZT8/65/35 ceramics. The effect of the UV light generated photovoltage and photostriction on the efficiency and voltage step-up ratio of piezoelectric transformer have been demonstrated. Novel functions of this device is proposed by superimposing two sophistically coupled effects of piezoelectricity and photostriction.

  16. Identification of elastic, dielectric, and piezoelectric constants in piezoceramic disks.

    Science.gov (United States)

    Perez, Nicolas; Andrade, Marco A B; Buiochi, Flavio; Adamowski, Julio C

    2010-12-01

    Three-dimensional modeling of piezoelectric devices requires a precise knowledge of piezoelectric material parameters. The commonly used piezoelectric materials belong to the 6mm symmetry class, which have ten independent constants. In this work, a methodology to obtain precise material constants over a wide frequency band through finite element analysis of a piezoceramic disk is presented. Given an experimental electrical impedance curve and a first estimate for the piezoelectric material properties, the objective is to find the material properties that minimize the difference between the electrical impedance calculated by the finite element method and that obtained experimentally by an electrical impedance analyzer. The methodology consists of four basic steps: experimental measurement, identification of vibration modes and their sensitivity to material constants, a preliminary identification algorithm, and final refinement of the material constants using an optimization algorithm. The application of the methodology is exemplified using a hard lead zirconate titanate piezoceramic. The same methodology is applied to a soft piezoceramic. The errors in the identification of each parameter are statistically estimated in both cases, and are less than 0.6% for elastic constants, and less than 6.3% for dielectric and piezoelectric constants.

  17. Electromechanical-Traffic Model of Compression-Based Piezoelectric Energy Harvesting

    Directory of Open Access Journals (Sweden)

    Kok B.C.

    2016-01-01

    Full Text Available Piezoelectric energy harvesting has advantages over other alternative sources due to its large power density, ease of applications, and capability to be fabricated at different scales: macro, micro, and nano. This paper presents an electromechanical-traffic model for roadway compression-based piezoelectric energy harvesting system. A two-degree-of-freedom (2-DOF electromechanical model has been developed for the piezoelectric energy harvesting unit to define its performance in power generation under a number of external excitations on road surface. Lead Zirconate Titanate (PZT-5H is selected as the piezoelectric material to be used in this paper due to its high Piezoelectric Charge Constant (d and Piezoelectric Voltage Constant (g values. The main source of vibration energy that has been considered in this paper is the moving vehicle on the road. The effect of various frequencies on possible generated power caused by different vibration characteristics of moving vehicle has been studied. A single unit of circle-shape Piezoelectric Cymbal Transducer (PCT with diameter of 32 mm and thickness of 0.3 mm be able to generate about 0.12 mW and 13 mW of electric power under 4 Hz and 20 Hz of excitation, respectively. The estimated power to be generated for multiple arrays of PCT is approximately 150 kW/ km. Thus, the developed electromechanical-traffic model has enormous potential to be used in estimating the macro scale of roadway power generation system.

  18. BiFeO3-doped (Na0.5K0.5NbO3 lead-free piezoelectric ceramics

    Directory of Open Access Journals (Sweden)

    Xueyi Sun et al

    2008-01-01

    Full Text Available Lead-free piezoelectric ceramics (1−x(Na0.5K0.5NbO3-xBiFeO3 (x=0~0.07 were synthesized by the solid-state reaction. Differential scanning calorimetry (DSC measurements revealed that an increase in the amount of BiFeO3 dopant resulted in a decrease in the orthorhombic-tetragonal and tetragonal-cubic phase transition temperature of the material. One percent BiFeO3 additive suppressed grain growth, which not only benefits the sintering of ceramics but also enhances the piezoelectric and ferroelectric properties, where d33=145pC/N, kp=0.31, Qm=80, Pr=11.3 μC cm−2 and Ec=16.5 kV cm−1. As xBF>0.01, both piezoelectric and ferroelectric properties decreased rapidly with an increasing amount of dopant.

  19. Using the methods of radiospectroscopy (EPR, NMR) to study the nature of the defect structure of solid solutions based on lead zirconate titanate (PZT).

    Science.gov (United States)

    Bykov, Igor; Zagorodniy, Yuriy; Yurchenko, Lesya; Korduban, Alexander; Nejezchleb, Karel; Trachevsky, Vladimir; Dimza, Vilnis; Jastrabik, Lubomir; Dejneka, Alexander

    2014-08-01

    The nature of intrinsic and impurity point defects in lead zirconate titanate (PZT) ceramics has been explored. Using electron paramagnetic resonance (EPR), nuclear magnetic resonance (NMR), and X-ray photoelectron spectroscopy (XPS) methods, several impurity sites have been identified in the materials, including the Fe(3+)-oxygen vacancy (VO) complex and Pb ions. Both of these centers are incorporated into the PZT lattice. The Fe(3+) –VО paramagnetic complex serves as a sensitive probe of the local crystal field in the ceramic; the symmetry of this defect roughly correlates with PZT phase diagram as the composition is varied from PbTiO3 to PbZrO3. NMR spectra (207)Pb in PbTiO3, PbZrO3, and PZT with iron content from 0 to 0.4 wt% showed that increasing the iron concentration leads to a distortion of the crystal structure and to improvement of the electrophysical parameters of the piezoceramics. This is due to the formation of a phase which has a higher symmetry, but at high concentrations of iron (>0.4 wt%), it leads to sharp degradation of electrophysical parameters.

  20. Piezoelectric ultrasonic micromotor with 1.5 mm diameter.

    Science.gov (United States)

    Dong, Shuxiang; Lim, Siak P; Lee, Kwork H; Zhang, Jingdong; Lim, Leong C; Uchino, Kenji

    2003-04-01

    A piezoelectric ultrasonic micromotor has been developed using a lead zirconate titanate (PZT) ceramic/metal composite tube stator that was 1.5 mm in diameter and 7 mm in length. The micromotor was operated in its first bending vibration mode (approximately 70 kHz), producing speeds from hundreds to over 2000 rpm in both rotational directions. The maximum torque-output was 45 microN-m, which is far superior to previous PZT thin film-based micromotors. This micromotor showed good reliability and stability for more than 300 hours of continued operation.

  1. Three-dimensional micro electromechanical system piezoelectric ultrasound transducer

    Science.gov (United States)

    Hajati, Arman; Latev, Dimitre; Gardner, Deane; Hajati, Azadeh; Imai, Darren; Torrey, Marc; Schoeppler, Martin

    2012-12-01

    Here we present the design and experimental acoustic test data for an ultrasound transducer technology based on a combination of micromachined dome-shaped piezoelectric resonators arranged in a flexible architecture. Our high performance niobium-doped lead zirconate titanate film is implemented in three-dimensional dome-shaped structures, which form the basic resonating cells. Adjustable frequency response is realized by mixing these basic cells and modifying their dimensions by lithography. Improved characteristics such as high sensitivity, adjustable wide-bandwidth frequency response, low transmit voltage compatible with ordinary integrated circuitry, low electrical impedance well matched to coaxial cabling, and intrinsic acoustic impedance match to water are demonstrated.

  2. Determination of the reduced matrix of the piezoelectric, dielectric, and elastic material constants for a piezoelectric material with C∞ symmetry.

    Science.gov (United States)

    Sherrit, Stewart; Masys, Tony J; Wiederick, Harvey D; Mukherjee, Binu K

    2011-09-01

    We present a procedure for determining the reduced piezoelectric, dielectric, and elastic coefficients for a C(∞) material, including losses, from a single disk sample. Measurements have been made on a Navy III lead zirconate titanate (PZT) ceramic sample and the reduced matrix of coefficients for this material is presented. In addition, we present the transform equations, in reduced matrix form, to other consistent material constant sets. We discuss the propagation of errors in going from one material data set to another and look at the limitations inherent in direct calculations of other useful coefficients from the data.

  3. Energy harvesting from vibration using a piezoelectric membrane

    Energy Technology Data Exchange (ETDEWEB)

    Ericka, M.; Vasic, D.; Costa, F.; Tliba, S. [Ecole Normale Superieure de Cachan, Systemes et Applications des Technologies de l' Information et de l' Energie (SATIE, UMR 8029), 94 - Cachan (France); Poulin, G. [Ecole Nationale Superieure d' Ingenieurs Electriciens de Grenoble, Laboratoire d' Automatique de Grenoble, 38 (France)

    2005-09-01

    In this paper we investigate the capability of harvesting the electric energy from mechanical vibrations in a dynamic environment through a piezoelectric membrane transducer. This transducer consists of 2 layers lead zirconate titanate (PZT)/brass, the brass layer is embedded over the whole circumference by epoxy adhesive. A very small vibration gives a consequent deformation of the membrane which generates electric energy. Due to the impedance matrices connecting the efforts and flows of the membrane, we have established the dynamic electric equivalent circuit of the transducer. In a first study and in order to validate theoretical results, we performed experiments with a vibrating machine moving a macroscopic 25 mm diameter piezoelectric membrane. A power of 1.8 mW was generated at the resonance frequency (2.58 kHz) across a 56 k{omega} optimal resistor and for a 2 g acceleration. (authors)

  4. Large displacement vertical translational actuator based on piezoelectric thin films.

    Science.gov (United States)

    Qiu, Zhen; Pulskamp, Jeffrey S; Lin, Xianke; Rhee, Choong-Ho; Wang, Thomas; Polcawich, Ronald G; Oldham, Kenn

    2010-07-01

    A novel vertical translational microactuator based on thin-film piezoelectric actuation is presented, using a set of four compound bend-up/bend-down unimorphs to produce translational motion of a moving platform or stage. The actuation material is a chemical-solution deposited lead-zirconate-titanate (PZT) thin film. Prototype designs have shown as much as 120 μ m of static displacement, with 80-90 μ m displacements being typical, using four 920 μ m long by 70 μ m legs. Analytical models are presented that accurately describe nonlinear behavior in both static and dynamic operation of prototype stages when the dependence of piezoelectric coefficients on voltage is known. Resonance of the system is observed at a frequency of 200 Hz. The large displacement and high bandwidth of the actuators at low-voltage and low-power levels should make them useful to a variety of optical applications, including endoscopic microscopy.

  5. Converse flexoelectric effect in comb electrode piezoelectric microbeam

    Energy Technology Data Exchange (ETDEWEB)

    Shen, Zhiyuan, E-mail: shenyuan675603@gmail.com [School of Mechanical and Aerospace Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798 Singapore (Singapore); Chen, Wei [Microelectronics Centre, School of Electrical and Electronic Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798 Singapore (Singapore)

    2012-04-09

    We demonstrate the converse flexoelectric effect in a lead zirconate titanate microbeam. The fringe electric field of a comb electrode induces converse flexoelectric responses in uniformly poled and depoled beams. The simulated electric field distribution shows that bending of the beam is induced by piezoelectric and μ{sub 11}, μ{sub 12} flexoelectric coefficients. Simulations indicate that piezoelectric displacement occurs in different directions in the two opposite poled samples while flexoelectric displacement remains the same. This finding is verified by the displacement measurement results. -- Highlights: ► We demonstrate the converse flexoelectric effect in a PZT microbeam. ► Beams with upward and downward poling states are fabricated by MEMS technique. ► Converse flexoelectric deformation is induced by the fringe field. ► Electric field distribution is calculated by finite element analysis. ► The simulation results are verified by impedance and displacement measurements.

  6. Piezoelectric ribbons printed onto rubber for flexible energy conversion.

    Science.gov (United States)

    Qi, Yi; Jafferis, Noah T; Lyons, Kenneth; Lee, Christine M; Ahmad, Habib; McAlpine, Michael C

    2010-02-10

    The development of a method for integrating highly efficient energy conversion materials onto stretchable, biocompatible rubbers could yield breakthroughs in implantable or wearable energy harvesting systems. Being electromechanically coupled, piezoelectric crystals represent a particularly interesting subset of smart materials that function as sensors/actuators, bioMEMS devices, and energy converters. Yet, the crystallization of these materials generally requires high temperatures for maximally efficient performance, rendering them incompatible with temperature-sensitive plastics and rubbers. Here, we overcome these limitations by presenting a scalable and parallel process for transferring crystalline piezoelectric nanothick ribbons of lead zirconate titanate from host substrates onto flexible rubbers over macroscopic areas. Fundamental characterization of the ribbons by piezo-force microscopy indicates that their electromechanical energy conversion metrics are among the highest reported on a flexible medium. The excellent performance of the piezo-ribbon assemblies coupled with stretchable, biocompatible rubber may enable a host of exciting avenues in fundamental research and novel applications.

  7. Effect of MnO2, Bi2O3, and ZnO additions on the electrical properties of lead zirconate titanate piezo ceramics

    International Nuclear Information System (INIS)

    Klimov, V.V.; Selikova, N.I.; Bronnikov, A.N.

    2006-01-01

    The effect of manganese dioxide additions on the electrical properties of lead zirconate titanate (PZT) piezo ceramics has been investigated. The results demonstrate that, taken alone, manganese dioxide does not ensure the formation of hard PZT. The valence state of manganese in the piezo ceramics is shown to be 4+ if no other dopants are present and 3+ if manganese is introduced in combination with Bi and Zn. Microstructural examination indicates that the grain size of the singly doped ceramics is 5-15 μm, while that of the codoped ceramics is 1-3 μm. The polarization current curves of the piezo ceramics containing manganese, bismuth, and zinc oxides have extra maxima, which points to significant internal fields. The manganese is shown to reside at grain boundaries. The conclusion is made that it is the composition of Mn-containing intergranular phases, rather than the presence of manganese ions, that plays a key role in the formation of hard piezo ceramics [ru

  8. The effect of thai glutinous rice starch on the synthesis of lead zirconate (PbZrO3) nanofibers via the electrospinning method.

    Science.gov (United States)

    Nawanil, Chanisa; Vittayakorn, Wanwilai; Muanghua, Rangson; Niemcharoen, Surasak; Prachayawarakorn, Jutarat; Vittayakorn, Naratip

    2013-05-01

    This study synthesized blended lead zirconate (PbZrO3;PZ)/poly(ethylene oxide)(PEO)/Glutinous rice starch (GRS) nanofibers by the electrospinning method. A number of parameters such as the ratio between PEO and GRS and calcination temperature have been studied. The as-spun PZ/PEO/GRS composite and PZ fibers were characterized by TG-DTA, X-ray diffraction, FT-IR and SEM, respectively. SEM results showed that smooth and continuous fibers were obtained at the volume ratio of 10:2:1, PZ/PEO/GRS. After calcination of the as-spun PZ/PEO/GRS composite nanofibers at 650 degrees C for 4 h, PZ nanofibers with perovskite structure were obtained successfully. The fibers had a uniform and smooth surface without grain boundaries. However, when the calcination temperature increased to 750 degrees C and 850 degrees C, the fiber represented a necklace-like structure with grain boundaries arranged by grain to grain unit cell clusters.

  9. A piezoelectric transformer

    Science.gov (United States)

    Won, C. C.

    1993-01-01

    This work describes a modeling and design method whereby a piezoelectric system is formulated by two sets of second-order equations, one for the mechanical system, and the other for the electrical system, coupled through the piezoelectric effect. The solution to this electromechanical coupled system gives a physical interpretation of the piezoelectric effect as a piezoelectric transformer that is a part of the piezoelectric system, which transfers the applied mechanical force into a force-controlled current source, and short circuit mechanical compliance into capacitance. It also transfers the voltage source into a voltage-controlled relative velocity input, and free motional capacitance into mechanical compliance. The formulation and interpretation simplify the modeling of smart structures and lead to physical insight that aids the designer. Due to its physical realization, the smart structural system can be unconditional stable and effectively control responses. This new concept has been demonstrated in three numerical examples for a simple piezoelectric system.

  10. Towards a digital sound reconstruction MEMS device: Characterization of a single PZT based piezoelectric actuator

    KAUST Repository

    Carreno, Armando Arpys Arevalo

    2015-04-01

    In this paper we report the fabrication and characterization of a single piezoelectric actuator for digital sound reconstruction. This work is the first step towards the implementation of a true digital micro-loudspeaker by means of an array of acoustic actuators. These actuators consist of a flexible membrane fabricated using polyimide, which is actuated using a Lead-Zirconate-Titanate (PZT) piezoelectric ceramic layer working in the d31 actuation mode. The dimensions of the membrane are of 1mm diameter and 4μm in thickness, which is capable of being symmetrically actuated in both upward and downward directions, due to the back etch step releasing the membrane. Our electrical characterization shows an improvement in the polarization of the piezoelectric material after its final etch patterning step, and our mechanical characterization shows the natural modes of resonance of the stacked membrane. © 2015 IEEE.

  11. Structural and electrical characterization of PZT on gold for micromachined piezoelectric membranes

    International Nuclear Information System (INIS)

    Robinson, M.C.; Morris, D.J.; Hayenga, P.D.; Cho, J.H.; Richards, C.D.; Richards, R.F.; Bahr, D.F.

    2006-01-01

    Piezoelectric membranes have been fabricated that incorporate a gold bottom electrode with an adhesion layer of titanium-tungsten (10:90 wt. %). For solution-deposited acetic acid based lead zirconate titanate (HoAc-PZT) with a Zr:Ti ratio of 40:60, the film's average piezoelectric coefficient, e 31 , is -5.31 C/m 2 , with a dielectric constant of 814 at 200 Hz, which is similar to values for platinum bottom electrodes. The PZT structure remains columnar on both types of bottom electrodes. Initial fabrication attempts resulted in cracking that initiated in the PZT layer of the structure. X-ray photoelectron spectroscopy was utilized to establish how processing affects diffusion throughout the composite membrane structure. Crack-free membranes were fabricated and tested. This paper discusses the performance properties and piezoelectric fatigue results for these membranes. (orig.)

  12. Enhanced ferroelectric and piezoelectric properties in La-modified PZT ceramics

    Science.gov (United States)

    Kour, P.; Pradhan, S. K.; Kumar, Pawan; Sinha, S. K.; Kar, Manoranjan

    2016-06-01

    The effect of lanthanum (La) doping on ferroelectric and piezoelectric properties of lead zirconate titanate (PZT) sample has been investigated. Pb1- x La x Zr0.52Ti0.48O3 ceramics with x = 0.00, 0.02, 0.04, 0.06 and 0.10 were prepared by the sol-gel technique. Raman and Fourier transforms infrared spectroscopy have been employed to understand the structural modification due to ionic size mismatch. Raman spectra show the existence of both rhombohedral and tetragonal crystal symmetries. It also shows the dielectric relaxation with increase in La concentration in the sample. The increase in lattice strain due to La doping increases the remnant polarization and coercive field. The linear piezoelectric coefficient increases with the increase in La concentration. It reveals that La-substituted PZT is a better candidate for piezoelectric sensor applications as compared to that of PZT.

  13. Study on the piezoelectric behavior and structural changes of strontium doped PZT

    International Nuclear Information System (INIS)

    Silva, M.S. da; Lemos, L.; Souza, E.F.; Cavalheiro, A.A.; Longo, E.; Zaghete, M.A.

    2014-01-01

    Lead zirconate titanate, with Zr/Ti ratio of 53/47 was prepared by the polymeric precursor method. The powders were doped with 0.0, 0.2, 0.4 and 0.6 mol% of Sr 2+ and the effects of Sr 2+ additions on piezoelectric properties and on the phase constitution were investigated by XRD. The percentages of tetragonal and rhombohedral phases were calculated through Rietveld refinement. The results indicated that addition of Sr 2+ ions in the amount of 0.4 mol% in the ceramic structure maximally increase the values of piezoelectric parameter to d 33 = 289 μC/N and K p = 0.43. The values found for the piezoelectric properties were among the highest at the concentration of 0.4 mol% of strontium and this composition showed the highest structural change from the rhombohedral to the tetragonal phase perovskita. (author)

  14. Effects of improved process for CuO-doped NKN lead-free ceramics on high-power piezoelectric transformers.

    Science.gov (United States)

    Yang, Song-Ling; Tsai, Cheng-Che; Liou, Yi-Cheng; Hong, Cheng-Shong; Li, Bing-Jing; Chu, Sheng-Yuan

    2011-12-01

    In this paper, the effects of the electrical proper- ties of CuO-doped (Na(0.5)K(0.5))NbO(3) (NKN) ceramics prepared separately using the B-site oxide precursor method (BO method) and conventional mixed-oxide method (MO method) on high-power piezoelectric transformers (PTs) were investigated. The performances of PTs made with these two substrates were compared. Experimental results showed that the output power and temperature stability of PTs could be enhanced because of the lower resonant impedance of the ceramics prepared using the BO method. In addition, the output power of PTs was more affected by the resonant impedance than by the mechanical quality factor (Q(m)) of the ceramics. The PTs fabricated with ceramics prepared using the BO method showed a high efficiency of more than 94% and a maximum output power of 8.98 W (power density: 18.3 W/cm(3)) with temperature increase of 3°C under the optimum load resistance (5 kΩ) and an input voltage of 150 V(pp). This output power of the lead-free disk-type PTs is the best reported so far.

  15. Fabrication of lead-free piezoelectric Li2CO3-added (Ba,Ca)(Ti,Sn)O3 ceramics under controlled low oxygen partial pressure and their properties

    Science.gov (United States)

    Noritake, Kouta; Sakamoto, Wataru; Yuitoo, Isamu; Takeuchi, Teruaki; Hayashi, Koichiro; Yogo, Toshinobu

    2018-02-01

    Reduction-resistant lead-free (Ba,Ca)(Ti,Sn)O3 piezoceramics with high piezoelectric constants were fabricated by optimizing the amount of Li2CO3 added. Oxygen partial pressure was controlled during the sintering of (Ba,Ca)(Ti,Sn)O3 ceramics in a reducing atmosphere using H2-CO2 gas. Enhanced grain growth and a high-polarization state after poling treatment were achieved by adding Li2CO3. Optimizing the amount of Li2CO3 added to (Ba0.95Ca0.05)(Ti0.95Sn0.05)O3 ceramics sintered under a low oxygen partial pressure resulted in improved piezoelectric properties while maintaining the high sintered density. The prepared Li2CO3-added ceramic samples had homogeneous microstructures with a uniform dispersion of each major constituent element. However, the residual Li content in the 3 mol % Li2CO3-added (Ba0.95Ca0.05)(Ti0.95Sn0.05)O3 ceramics after sintering was less than 0.3 mol %. Sintered bodies of this ceramic prepared in a CO2 (1.5%)-H2 (0.3%)/Ar reducing atmosphere (PO2 = 10-8 atm at 1350 °C), exhibited sufficient electrical resistivity and a piezoelectric constant (d 33) exceeding 500 pC/N. The piezoelectric properties of this nonreducible ceramic were comparable or superior to those of the same ceramic sintered in air.

  16. Electroactive properties of flexible piezoelectric composites

    Directory of Open Access Journals (Sweden)

    Sakamoto Walter Katsumi

    2001-01-01

    Full Text Available A flexible piezoelectric composite with 0-3 connectivity, made from Lead Zirconate Titanate (PZT powder and vegetable-based polyurethane (PU, was doped with small amount of semiconductor powder. As a result a composite with 0-0-3 connectivity was obtained. The nature of absorption and steady state electrical conduction and the dielectric behaviour have been studied for this ceramic/polymer composite. The dielectric loss processes of the composite were observed to be dominated by those the polymer. Adding a semiconductor phase in the composite the electrical conductivity can be controlled and a continuous electric flux path could be created between the PZT grains. This composite may be poled at low voltage and in shorter time compared with composites without a conductive phase.

  17. Toward a unified description of nonlinearity and frequency dispersion of piezoelectric and dielectric responses in Pb(Zr,Ti)O3

    International Nuclear Information System (INIS)

    Damjanovic, D.; Bharadwaja, S.S.N.; Setter, N.

    2005-01-01

    A phenomenological approach is proposed describing both nonlinearity and frequency dispersion in dielectric and piezoelectric properties of lead zirconate titanate, Pb(Zr,Ti)O 3 (PZT), thin films and ceramics. The approach couples the frequency dependent response in form of the power law, 1/ω β , with the rate-independent nonlinear response described by the Rayleigh law. The main experimental trends are well described by the model

  18. A concept for the development of piezoceramic materials based on lead zirconate titanate (PZT). Part 2; Ein Entwicklungskonzept piezokeramischer Werkstoffe auf der Basis von Bleizirkonattitanat (PZT). Teil 2

    Energy Technology Data Exchange (ETDEWEB)

    Helke, G. [CeramTec AG, Lauf a.d. Pegnitz (Germany)

    2002-07-01

    Piezoceramic ceramics based on Lead Zircontate Titanate (PZT) show - within a relatively close Zr/Ti ratio range (close to the ratio 0.5/0.5) - extreme values for remanent polarization P{sub r} and the dielectric coefficient {epsilon}{sub 33}{sup {tau}}/{epsilon}{sub 0} as well as their corresponding piezoelectric coefficients. Remanent polarization P{sub t} can be directly correlated to the structural parameter {delta} (spontaneous deformation) and the domain mobility {eta}. PZT modification results from the substitution of isovalent or heterovalent ions, thereby taking ion radii and valency at the A and B sites of the perovskite-type lattice under consideration. The substitution of specific ions is the process used to develop new piezoceramic materials which is mainly applied to determine the values of specific parameters corresponding to technical requirements. (orig.) [German] Piezoelektrische Keramiken auf der Basis von Bleizirkonattitanat (PZT) weisen in einem relativ engen Bereich des Zr/Ti-Verhaeltnisses (nahe dem Verhaeltnis 0,5/0,5). Extremwerte der remanenten Polarisation P{sub r} und der Dielektrizitaetskonstanten {epsilon}{sub 33}{sup {tau}}/{epsilon}{sub 0} sowie der von ihnen abhaengigen piezoelektrischen Kenngroessen auf. Die remanente Polarisation P{sub r} laesst sich unmittelbar dem Strukturparameter {delta} (spontane Deformation) und der Domaenenbeweglichkeit {eta} zuordnen. Die Modifikation von PZT erfolgt durch Substitution isovalenter oder heterovalenter Ionen unter Beruecksichtigung von Ionenradien und -wertigkeit auf A- und B-Plaetzen des Perowskigitters. Die Substitution bestimmter Ionen ist das Verfahren zur Schaffung neuer piezokeramischer Werkstoffe und wird insbesondere zur Einstellung der Werte einzelner Kenngroessen auf einem bestimmten Niveau entsprechend den technischen Anforderungen angewendet. (orig.)

  19. A concept for the development of piezoceramic materials based on lead zirconate titanate (PZT). Part 1; Ein Entwicklungskonzept piezokeramischer Werkstoffe auf der Basis von Gleizirkonattitanat (PZT). Teil 1

    Energy Technology Data Exchange (ETDEWEB)

    Helke, G. [CeramTec AG, Lauf a.d. Pegnitz (Germany)

    2002-07-01

    Piezoceramic ceramics based on Lead Zircontate Titanate (PZT) show - within a relatively close Zr/Ti ratio range (close to the ratio 0.5/0.5) - extreme values for remanent polarization P{sub r} and the dielectric coefficient {epsilon}{sub 33}{sup {tau}}/{epsilon}{sub 0} as well as their corresponding piezoelectric coefficients. Remanent polarization P{sub t} can be directly correlated to the structural parameter {delta} (spontaneous deformation) and the domain mobility {eta}. PZT modification results from the substitution of isovalent or heterovalent ions, thereby taking ion radii and valency at the A and B sites of the perovskite-type lattice under consideration. The substitution of specific ions is the process used to develop new piezoceramic materials which is mainly applied to determine the values of specific parameters corresponding to technical requirements. (orig.) [German] Piezoelektrische Keramiken auf der Basis von Bleizirkonattitanat (PZT) weisen in einem relativ engen Bereich des Zr/Ti-Verhaeltnisses (nahe dem Verhaeltnis 0,5/0,5). Extremwerte der remanenten Polarisation P{sub r} und der Dielektrizitaetskonstanten {epsilon}{sub 33}{sup {tau}}/{epsilon}{sub 0} sowie der von ihnen abhaengigen piezoelektrischen Kenngroessen auf. Die remanente Polarisation P{sub r} laesst sich unmittelbar dem Strukturparameter {delta} (spontane Deformation) und der Domaenenbeweglichkeit {eta} zuordnen. Die Modifikation von PZT erfolgt durch Substitution isovalenter oder heterovalenter Ionen unter Beruecksichtigung von Ionenradien und -wertigkeit auf A- und B-Plaetzen des Perowskigitters. Die Substitution bestimmter Ionen ist das Verfahren zur Schaffung neuer piezokeramischer Werkstoffe und wird insbesondere zur Einstellung der Werte einzelner Kenngroessen auf einem bestimmten Niveau entsprechend den technischen Anforderungen angewendet. (orig.)

  20. Effect of electrical and mechanical poling history on domain orientation and piezoelectric properties of soft and hard PZT ceramics

    International Nuclear Information System (INIS)

    Marsilius, Mie; Granzow, Torsten; Jones, Jacob L

    2011-01-01

    The superior piezoelectric properties of all polycrystalline ferroelectrics are based on the extent of non-180 0 domain wall motion under electrical and mechanical poling loads. To distinguish between 180 0 and non-180 0 domain wall motion in a soft-doped and a hard-doped lead zirconate titanate (PZT) ceramic, domain texture measurements were performed using x-ray and neutron diffraction after different loading procedures. Comparing the results to measurements of the remanent strain and piezoelectric coefficient allowed the differentiation between different microstructural contributions to the macroscopic parameters. Both types of ceramic showed similar behavior under electric field, but the hard-doped material was more susceptible to mechanical load. A considerable fraction of the piezoelectric coefficient originated from poling by the preferred orientation of 180 0 domains.

  1. Effect of electrical and mechanical poling history on domain orientation and piezoelectric properties of soft and hard PZT ceramics

    Science.gov (United States)

    Marsilius, Mie; Granzow, Torsten; Jones, Jacob L.

    2011-02-01

    The superior piezoelectric properties of all polycrystalline ferroelectrics are based on the extent of non-180° domain wall motion under electrical and mechanical poling loads. To distinguish between 180° and non-180° domain wall motion in a soft-doped and a hard-doped lead zirconate titanate (PZT) ceramic, domain texture measurements were performed using x-ray and neutron diffraction after different loading procedures. Comparing the results to measurements of the remanent strain and piezoelectric coefficient allowed the differentiation between different microstructural contributions to the macroscopic parameters. Both types of ceramic showed similar behavior under electric field, but the hard-doped material was more susceptible to mechanical load. A considerable fraction of the piezoelectric coefficient originated from poling by the preferred orientation of 180° domains.

  2. X-ray diffraction measurement of residual stress in sol-gel grown lead zirconate titanate thick films on nickel-based super alloy substrate

    Energy Technology Data Exchange (ETDEWEB)

    Hoshyarmanesh, Hamidreza; Nehzat, Naser; Salehi, Mehdi [Isfahan University of Technology, Isfahan (Iran, Islamic Republic of); Ghodsi, Mojtaba [Sultan Qaboos University, Muscat (Oman)

    2015-02-15

    Residual compressive stress of Pb(Zr{sub 0.52}Ti{sub 0.48})O{sub 3} thick films was investigated using residual strains derived from X-ray diffraction patterns. Sin{sup 2}ψ method was applied for the 5, 10 and 15 μm sol-gel derived thick films annealed at 700 .deg. C for 1 hr as high frequency structural health monitoring square-shape transducers of 10 x10 mm, deposited onto the curved nickel-based super alloy substrates. A triaxial model was proposed based on piezoelectric constitutive equations, and Bragg's law at a large diffraction angle (∼89°) was utilized considering the electromechanical coupling factor as well as elastic, dielectric and piezoelectric constants. Thickness variations led to a significant change in residual stress magnitudes delineated from more-accurate triaxial model compared to small angle plane-stress results not considering the piezoelectric coupling effects.

  3. Uranium-lead dating of hydrothermal zircon and monazite from the Sin Quyen Fe-Cu-REE-Au-(U) deposit, northwestern Vietnam

    Science.gov (United States)

    Li, Xiao-Chun; Zhou, Mei-Fu; Chen, Wei Terry; Zhao, Xin-Fu; Tran, MyDung

    2018-03-01

    The Sin Quyen deposit in northwestern Vietnam contains economic concentrations of Cu, Au and LREE, and sub-economic concentration of U. In this deposit, massive and banded replacement ores are hosted in Neoproterozoic metapelite. The paragenetic sequence includes sodic alteration (stage I), calcic-potassic alteration and associated Fe-REE-(U) mineralization (stage II), Cu-Au mineralization (stage III), and sulfide-(quartz-carbonate) veins (stage IV). The Sin Quyen deposit experienced an extensive post-ore metamorphic overprint, which makes it difficult to precisely determine the mineralization age. In this study, zircon and monazite U-Pb geochronometers and the Rb-Sr isochron method are used to constrain the timing of mineralization. Zircon grains in the ore are closely intergrown or texturally associated with hydrothermal minerals of stage II (e.g., garnet, allanite, and hedenbergite). They may contain primary fluid inclusions and display irregular zoning in cathodoluminescence (CL) images. Zircon grains are rich in U (688 to 2902 ppm) and poor in Th (0.2 to 2.9 ppm). Their δ18OV-SMOW values range from 11.9 to 14.0‰, higher than those of typical magmatic zircon. These textural and compositional features imply that zircon precipitated from 18O- and U-rich hydrothermal fluids, coeval with the minerals of stage II. Monazite occurs in close association with stage II magnetite and allanite and has low contents of Th (<2700 ppm), indicative of a hydrothermal origin. Hydrothermal zircon and monazite have indistinguishable U-Pb ages of 841 ± 12 and 836 ± 18 Ma, respectively, representing the timing of Fe-REE mineralization. There is no direct isotopic constraint on the timing of the Cu-Au mineralization, but geological observations suggest that the Cu-Au and Fe-REE ores most likely formed within a single evolved hydrothermal process. In the plot of 87Rb/86Sr vs. 87Sr/86Sr, the composition of bulk-ore and biotite separates from ore lie along a reference line for 30 Ma

  4. High-displacement spiral piezoelectric actuators

    Science.gov (United States)

    Mohammadi, F.; Kholkin, A. L.; Jadidian, B.; Safari, A.

    1999-10-01

    A high-displacement piezoelectric actuator, employing spiral geometry of a curved piezoelectric strip is described. The monolithic actuators are fabricated using a layered manufacturing technique, fused deposition of ceramics, which is capable of prototyping electroceramic components with complex shapes. The spiral actuators (2-3 cm in diameter) consisted of 4-5 turns of a lead zirconate titanate ceramic strip with an effective length up to 28 cm. The width was varied from 0.9 to 1.75 mm with a height of 3 mm. When driven by the electric field applied across the width of the spiral wall, the tip of the actuator was found to displace in both radial and tangential directions. The tangential displacement of the tip was about 210 μm under the field of 5 kV/cm. Both the displacement and resonant frequency of the spirals could be tailored by changing the effective length and wall width. The blocking force of the actuator in tangential direction was about 1 N under the field of 5 kV/cm. These properties are advantageous for high-displacement low-force applications where bimorph or monomorph actuators are currently employed.

  5. PZT Thin Film Piezoelectric Traveling Wave Motor

    Science.gov (United States)

    Shen, Dexin; Zhang, Baoan; Yang, Genqing; Jiao, Jiwei; Lu, Jianguo; Wang, Weiyuan

    1995-01-01

    With the development of micro-electro-mechanical systems (MEMS), its various applications are attracting more and more attention. Among MEMS, micro motors, electrostatic and electromagnetic, are the typical and important ones. As an alternative approach, the piezoelectric traveling wave micro motor, based on thin film material and integrated circuit technologies, circumvents many of the drawbacks of the above mentioned two types of motors and displays distinct advantages. In this paper we report on a lead-zirconate-titanate (PZT) piezoelectric thin film traveling wave motor. The PZT film with a thickness of 150 micrometers and a diameter of 8 mm was first deposited onto a metal substrate as the stator material. Then, eight sections were patterned to form the stator electrodes. The rotor had an 8 kHz frequency power supply. The rotation speed of the motor is 100 rpm. The relationship of the friction between the stator and the rotor and the structure of the rotor on rotation were also studied.

  6. Direct strain energy harvesting in automobile tires using piezoelectric PZT–polymer composites

    International Nuclear Information System (INIS)

    Van den Ende, D A; Van de Wiel, H J; Groen, W A; Van der Zwaag, S

    2012-01-01

    Direct piezoelectric strain energy harvesting can be used to power wireless autonomous sensors in environments where low frequency, high strains are present, such as in automobile tires during operation. However, these high strains place stringent demands on the materials with respect to mechanical failure or depolarization, especially at elevated temperatures. In this work, three kinds of ceramic–polymer composite piezoelectric materials were evaluated and compared against state-of-the-art piezoelectric materials. The new composites are unstructured and structured composites containing granular lead zirconate titanate (PZT) particles or PZT fibers in a polyurethane matrix. The composites were used to build energy harvesting patches which were attached to a tire and tested under simulated rolling conditions. The energy density of the piezoelectric ceramic–polymer composite materials is initially not as high as that of the reference materials (a macro-fiber composite and a polyvinylidene fluoride polymer). However, the area normalized power output of the composites after temperature and strain cycling is comparable to that of the reference devices because the piezoelectric ceramic–polymer composites did not degrade during operation. (paper)

  7. Piezoelectric Flexible LCP-PZT Composites for Sensor Applications at Elevated Temperatures

    Science.gov (United States)

    Tolvanen, Jarkko; Hannu, Jari; Juuti, Jari; Jantunen, Heli

    2018-03-01

    In this paper fabrication of piezoelectric ceramic-polymer composites is demonstrated via filament extrusion enabling cost-efficient large-scale production of highly bendable pressure sensors feasible for elevated temperatures. These composites are fabricated by utilizing environmentally resistant and stable liquid crystal polymer matrix with addition of lead zirconate titanate at loading levels of 30 vol%. These composites, of approximately 0.99 mm thick and length of > 50 cm, achieved excellent bendability with minimum bending radius of 6.6 cm. The maximum piezoelectric coefficients d33 and g33 of the composites were > 14 pC/N and > 108 mVm/N at pressure < 10 kPa. In all cases, the piezoelectric charge coefficient (d33) of the composites decreased as a function of pressure. Also, piezoelectric coefficient (d33) further decreased in the case of increased frequency press-release cycle sand pre-stress levels by approximately 37-50%. However, the obtained results provide tools for fabricating novel piezoelectric sensors in highly efficient way for environments with elevated temperatures.

  8. Piezoelectric valve

    Science.gov (United States)

    Petrenko, Serhiy Fedorovich

    2013-01-15

    A motorized valve has a housing having an inlet and an outlet to be connected to a pipeline, a saddle connected with the housing, a turn plug having a rod, the turn plug cooperating with the saddle, and a drive for turning the valve body and formed as a piezoelectric drive, the piezoelectric drive including a piezoelectric generator of radially directed standing acoustic waves, which is connected with the housing and is connectable with a pulse current source, and a rotor operatively connected with the piezoelectric generator and kinematically connected with the rod of the turn plug so as to turn the turn plug when the rotor is actuated by the piezoelectric generator.

  9. Correlation of electron backscatter diffraction and piezoresponse force microscopy for the nanoscale characterization of ferroelectric domains in polycrystalline lead zirconate titanate

    Science.gov (United States)

    Burnett, T. L.; Weaver, P. M.; Blackburn, J. F.; Stewart, M.; Cain, M. G.

    2010-08-01

    The functional properties of ferroelectric ceramic bulk or thin film materials are strongly influenced by their nanostructure, crystallographic orientation, and structural geometry. In this paper, we show how, by combining textural analysis, through electron backscattered diffraction, with piezoresponse force microscopy, quantitative measurements of the piezoelectric properties can be made at a scale of 25 nm, smaller than the domain size. The combined technique is used to obtain data on the domain-resolved effective single crystal piezoelectric response of individual crystallites in Pb(Zr0.4Ti0.6)O3 ceramics. The results offer insight into the science of domain engineering and provide a tool for the future development of new nanostructured ferroelectric materials for memory, nanoactuators, and sensors based on magnetoelectric multiferroics.

  10. Superior piezoelectric composite films: taking advantage of carbon nanomaterials.

    Science.gov (United States)

    Saber, Nasser; Araby, Sherif; Meng, Qingshi; Hsu, Hung-Yao; Yan, Cheng; Azari, Sara; Lee, Sang-Heon; Xu, Yanan; Ma, Jun; Yu, Sirong

    2014-01-31

    Piezoelectric composites comprising an active phase of ferroelectric ceramic and a polymer matrix have recently found numerous sensory applications. However, it remains a major challenge to further improve their electromechanical response for advanced applications such as precision control and monitoring systems. We here investigated the incorporation of graphene platelets (GnPs) and multi-walled carbon nanotubes (MWNTs), each with various weight fractions, into PZT (lead zirconate titanate)/epoxy composites to produce three-phase nanocomposites. The nanocomposite films show markedly improved piezoelectric coefficients and electromechanical responses (50%) besides an enhancement of ~200% in stiffness. The carbon nanomaterials strengthened the impact of electric field on the PZT particles by appropriately raising the electrical conductivity of the epoxy. GnPs have been proved to be far more promising in improving the poling behavior and dynamic response than MWNTs. The superior dynamic sensitivity of GnP-reinforced composite may be caused by the GnPs' high load transfer efficiency arising from their two-dimensional geometry and good compatibility with the matrix. The reduced acoustic impedance mismatch resulting from the improved thermal conductance may also contribute to the higher sensitivity of GnP-reinforced composite. This research pointed out the potential of employing GnPs to develop highly sensitive piezoelectric composites for sensing applications.

  11. Superior piezoelectric composite films: taking advantage of carbon nanomaterials

    International Nuclear Information System (INIS)

    Saber, Nasser; Araby, Sherif; Meng, Qingshi; Hsu, Hung-Yao; Lee, Sang-Heon; Ma, Jun; Yan, Cheng; Xu, Yanan; Azari, Sara; Yu, Sirong

    2014-01-01

    Piezoelectric composites comprising an active phase of ferroelectric ceramic and a polymer matrix have recently found numerous sensory applications. However, it remains a major challenge to further improve their electromechanical response for advanced applications such as precision control and monitoring systems. We here investigated the incorporation of graphene platelets (GnPs) and multi-walled carbon nanotubes (MWNTs), each with various weight fractions, into PZT (lead zirconate titanate)/epoxy composites to produce three-phase nanocomposites. The nanocomposite films show markedly improved piezoelectric coefficients and electromechanical responses (50%) besides an enhancement of ∼200% in stiffness. The carbon nanomaterials strengthened the impact of electric field on the PZT particles by appropriately raising the electrical conductivity of the epoxy. GnPs have been proved to be far more promising in improving the poling behavior and dynamic response than MWNTs. The superior dynamic sensitivity of GnP-reinforced composite may be caused by the GnPs’ high load transfer efficiency arising from their two-dimensional geometry and good compatibility with the matrix. The reduced acoustic impedance mismatch resulting from the improved thermal conductance may also contribute to the higher sensitivity of GnP-reinforced composite. This research pointed out the potential of employing GnPs to develop highly sensitive piezoelectric composites for sensing applications. (paper)

  12. Triple degree-of-freedom piezoelectric ultrasonic micromotor via flexural-axial coupled vibration.

    Science.gov (United States)

    Khoo, Ter Fong; Dang, Dinh Huy; Friend, James; Oetomo, Denny; Yeo, Leslie

    2009-08-01

    Actuators remain a limiting factor in robotics, especially in microrobotics where the power density of actuators is a problem. A 3 x 3 x 8.7 mm 3-axis piezoelectric ultrasonic micromotor system is described here in an effort to help solve this problem. Formed from 4 bulk lead zirconate titanate (PZT) thickness-polarized elements placed around the periphery of a rectangular rod, the stator is designed to combine axial and flexural vibrations in a way that permits rotation of a hardened steel ball as a rotor about an arbitrary axis. A simple prototype of the micromotor was found to produce at least a rotation speed of 10.4 rad/s with 4 microN-m torque about all 3 orthogonal directions at an excitation frequency of about 221 kHz, demonstrating the feasibility of a 3 degree-of-freedom millimeter-scale piezoelectric motor.

  13. Effect of material constants on power output in piezoelectric vibration-based generators.

    Science.gov (United States)

    Takeda, Hiroaki; Mihara, Kensuke; Yoshimura, Tomohiro; Hoshina, Takuya; Tsurumi, Takaaki

    2011-09-01

    A possible power output estimation based on material constants in piezoelectric vibration-based generators is proposed. A modified equivalent circuit model of the generator was built and was validated by the measurement results in the generator fabricated using potassium sodium niobate-based and lead zirconate titanate (PZT) ceramics. Subsequently, generators with the same structure using other PZT-based and bismuth-layered structure ferroelectrics ceramics were fabricated and tested. The power outputs of these generators were expressed as a linear functions of the term composed of electromechanical coupling coefficients k(sys)(2) and mechanical quality factors Q*(m) of the generator. The relationship between device constants (k(sys)(2) and Q*(m)) and material constants (k(31)(2) and Q(m)) was clarified. Estimation of the power output using material constants is demonstrated and the appropriate piezoelectric material for the generator is suggested.

  14. Dual-enhancement of ferro-/piezoelectric and photoluminescent performance in Pr{sup 3+} doped (K{sub 0.5}Na{sub 0.5})NbO{sub 3} lead-free ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Wei, Yongbin; Jia, Yanmin, E-mail: wuzheng@zjnu.cn, E-mail: ymjia@zjnu.edu.cn; Wu, Jiang; Shen, Yichao [Department of Physics, Zhejiang Normal University, Jinhua 321004 (China); Wu, Zheng, E-mail: wuzheng@zjnu.cn, E-mail: ymjia@zjnu.edu.cn [College of Geography and Environmental Sciences, Zhejiang Normal University, Jinhua 321004 (China); Luo, Haosu [Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 201800 (China)

    2014-07-28

    A mutual enhancement action between the ferro-/piezoelectric polarization and the photoluminescent performance of rare earth Pr{sup 3+} doped (K{sub 0.5}Na{sub 0.5})NbO{sub 3} (KNN) lead-free ceramics is reported. After Pr{sup 3+} doping, the KNN ceramics exhibit the maximum enhancement of ∼1.2 times in the ferroelectric remanent polarization strength and ∼1.25 times in the piezoelectric coefficient d{sub 33}, respectively. Furthermore, after undergoing a ferro-/piezoelectric polarization treatment, the maximum enhancement of ∼1.3 times in photoluminescence (PL) was observed in the poled 0.3% Pr{sup 3+} doped sample. After the trivalent Pr{sup 3+} unequivalently substituting the univalent (K{sub 0.5}Na{sub 0.5}){sup +}, A-sites ionic vacancies will occur to maintain charge neutrality, which may reduce the inner stress and ease the domain wall motions, yielding to the enhancement in ferro-/piezoelectric performance. The polarization-induced enhancement in PL is attributed to the decrease of crystal symmetry abound the Pr{sup 3+} ions after polarization. The dual-enhancement of the ferro-/piezoelectric and photoluminescent performance makes the Pr{sup 3+} doped KNN ceramic hopeful for piezoelectric/luminescent multifunctional devices.

  15. Recent developments in piezoelectric ceramic materials and deterioration of their properties

    International Nuclear Information System (INIS)

    Pasha, R.A.; Khan, M.Z.

    2006-01-01

    There has been growing interest in recent years in piezoelectric ceramic materials because of their excellent dielectric, sensing, actuating and efficient process control applications. Lead Zirconate Titanate (PZT), Barium Titanate (BaTi O/sub 3/) and Lead Metaniobate (PbNb/sub 2/ O/sub 6/) and PVDF Polymers and generally favored as smart sensing materials. These materials are being used in critical engineering systems and smart structure. Fatigue failure due to electrical and thermal shocking is a major issue in degradation of these materials. Lot of work has been done in this area but still various issues need to investigate. Recent developments and current issues in piezoelectric materials and deterioration of their properties in different working conditions are discussed. The development of Finite Element codes incorporating smart material element has provided an opportunity to solve some practical problems. The new piezoelectric finite element capability available in some commercial package like ANSYS makes it convenient to perform static dynamic and thermal analysis for the fully coupled piezoelectric and structural response. Researchers have a great scope to uncover the various properties of these smart materials in different environmental conditions. In present work an overall review of the title is presented. (author)

  16. Strong and anisotropic magnetoelectricity in composites of magnetostrictive Ni and solid-state grown lead-free piezoelectric BZT–BCT single crystals

    Directory of Open Access Journals (Sweden)

    Haribabu Palneedi

    2017-03-01

    Full Text Available Aimed at developing lead-free magnetoelectric (ME composites with performances as good as lead (Pb-based ones, this study employed (001 and (011 oriented 82BaTiO3-10BaZrO3-8CaTiO3 (BZT–BCT piezoelectric single crystals, fabricated by the cost-effective solid-state single crystal growth (SSCG method, in combination with inexpensive, magnetostrictive base metal Nickel (Ni. The off-resonance, direct ME coupling in the prepared Ni/BZT–BCT/Ni laminate composites was found to be strongly dependent on the crystallographic orientation of the BZT–BCT single crystals, as well as the applied magnetic field direction. Larger and anisotropic ME voltage coefficients were observed for the composite made using the (011 oriented BZT–BCT single crystal. The optimized ME coupling of 1 V/cm Oe was obtained from the Ni/(011 BZT–BCT single crystal/Ni composite, in the d32 mode of the single crystal, when a magnetic field was applied along its [100] direction. This performance is similar to that reported for the Ni/Pb(Mg1/3Nb2/3O3-Pb(Zr,TiO3 (PMN–PZT single crystal/Ni, but larger than that obtained from the Ni/Pb(Zr,TiO3 ceramic/Ni composites. The results of this work demonstrate that the use of lead-free piezoelectric single crystals with special orientations permits the selection of desired anisotropic properties, enabling the realization of customized ME effects in composites.

  17. Disk-type piezoelectric transformer of a Na0.5K0.5NbO3–CuNb2O6 lead-free ceramic for driving T5 fluorescent lamp

    International Nuclear Information System (INIS)

    Yang, Ming-Ru; Chu, Sheng-Yuan; Chan, I.-Hao; Yang, Song-Ling

    2012-01-01

    Highlights: ► CuNb 2 O 6 dopants were doped into NKN ceramics not only improved the density but also exhibited superior piezoelectric characteristic, temperature stability of resonance frequency. ► Lead-free NKN-01CN piezoelectric transformer was simplified as an equivalent circuit and analyzed using MATLAB. ► An 8W T5 fluorescent lamp was successfully driven by the NKN-01CN piezoelectric transformer. - Abstract: Lead-free (Na 0.5 K 0.5 )NbO 3 (NKN) ceramics doped with 1 mol% CuNb 2 O 6 (CN) ceramics were prepared using the conventional mixed oxide method, with a sintering temperature of 1075 °C. Microstructural analyses of the NKN–01CN ceramics were carried out and compared, using X-ray diffraction (XRD). NKN–01CN ceramics sintered at 1075 °C not only exhibited excellent ‘hard’ piezoelectric properties of k p = 40%, k t = 45%, k 33 = 57%, a ferroelectric property of E c = 23 kV/cm, and an extraordinarily high mechanical quality factor (Q m ) of 1933 but also showed excellent stability with temperature (TCF = −154 ppm/°C). The piezoelectric transformer was simplified, using an equivalent circuit, and analyzed, using MATLAB; the simulation data agreed well with the experimental results. An efficiency of 95.7% was achieved for the NKN–01CN piezoelectric transformer with load resistance of 20 kΩ. An 8 W T5 fluorescent lamp was successfully driven by the NKN–01CN piezoelectric transformer.

  18. Figure of merit comparison of PP-based electret and PVDF-based piezoelectric polymer energy harvesters

    Science.gov (United States)

    Mrlík, M.; Leadenham, S.; AlMaadeed, M. A.; Erturk, A.

    2016-04-01

    The harvesting of mechanical strain and kinetic energy has received great attention over the past two decades in order to power wireless electronic components such as those used in passive and active monitoring applications. Piezoelectric ceramics, such as PZT (lead zirconate titanate), constitute the most commonly used electromechanical interface in vibration energy harvesters. However, there are applications in which piezoelectric ceramics cannot be used due to their low allowable curvature and brittle nature. Soft polymer PVDF (polyvinylidene fluoride) is arguably the most popular non-ceramic soft piezoelectric energy harvester material for such scenarios. Another type of polymer that has received less attention is PP (polypropylene) for electret-based energy harvesting using the thickness mode (33- mode). This work presents figure of merit comparison of PP versus PVDF for off-resonant energy harvesting in thickness mode operation, revealing substantial advantage of PP over PVDF. For thickness mode energy harvesting scenarios (e.g. dynamic compression) at reasonable ambient vibration frequencies, the figure of merit for the maximum power output is proportional to the square of the effective piezoelectric strain constant divided by the effective permittivity constant. Under optimal conditions and for the same volume, it is shown that PP can generate more than two orders of magnitude larger electrical power as compared to PVDF due to the larger effective piezoelectric strain constant and lower permittivity of the former.

  19. Low sintering temperature and high piezoelectric properties of Li-doped (Ba,Ca)(Ti,Zr)O3 lead-free ceramics

    International Nuclear Information System (INIS)

    Chen, Xiaoming; Ruan, Xuezheng; Zhao, Kunyun; He, Xueqing; Zeng, Jiangtao; Li, Yongsheng; Zheng, Liaoying; Park, Chul Hong; Li, Guorong

    2015-01-01

    Highlights: • Li-doped Ba 0.85 Ca 0.15 Ti 0.9 Zr 0.1 O 3 (BCZT) lead-free piezoceramics were prepared by the two-step synthesis and solid-state reaction method. • Their sintering temperature decreases from about 1540 °C down to about 1400 °C. • With the proper addition of Li, the densities and grain sizes of ceramics increase. • The ceramics not only have the characteristics of hard piezoceramics but also possesses the features of soft piezoceramics at low sintering temperature. - Abstract: Li-doped Ba 0.85 Ca 0.15 Ti 0.9 Zr 0.1 O 3 (BCZT) lead-free piezoelectric ceramics were prepared by the two-step synthesis and the solid-state reaction method. The density and grain size of ceramics sufficiently increases by Li-doped sintering aid, and their sintering temperature decreases from about 1540 °C down to about 1400 °C. X-ray diffraction reveals that the phase structure of Li-doped BCTZ ceramics is changed with the sintering temperature, which is consistent with their phase transition observed by the temperature-dependent dielectric curves. The well-poled Li-doped BCZT ceramics show a high piezoelectric constant d 33 (512 pC/N) and a planar electromechanical coupling factor k p (0.49), which have the characteristics of soft Pb(Zr,Ti)O 3 (PZT) piezoceramic, on the other hand, the mechanical quality factor Q m is about 190, which possesses the features of hard PZT piezoceramics. The enhanced properties of the Li-doped BCZT are explained by the combination of Li-doped effect and sintering effect on the microstructure and the phase transition around room temperature

  20. Longitudinal-bending mode micromotor using multilayer piezoelectric actuator.

    Science.gov (United States)

    Yao, K; Koc, B; Uchino, K

    2001-07-01

    Longitudinal-bending mode ultrasonic motors with a diameter of 3 mm were fabricated using stacked multilayer piezoelectric actuators, which were self-developed from hard lead zirconate titanate (PZT) ceramic. A bending vibration was converted from a longitudinal vibration with a longitudinal-bending coupler. The motors could be bidirectionally operated by changing driving frequency. Their starting and braking torque were analyzed based on the transient velocity response. With a load of moment of inertia 2.5 x 10(-7) kgm2, the motor showed a maximum starting torque of 127.5 microNm. The braking torque proved to be a constant independent on the motor's driving conditions and was roughly equivalent to the maximum starting torque achievable with our micromotors.

  1. Dielectric and piezoelectric properties of percolative three-phase piezoelectric polymer composites

    Science.gov (United States)

    Sundar, Udhay

    Three-phase piezoelectric bulk composites were fabricated using a mix and cast method. The composites were comprised of lead zirconate titanate (PZT), aluminum (Al) and an epoxy matrix. The volume fraction of the PZT and Al were varied from 0.1 to 0.3 and 0.0 to 0.17, respectively. The influences of three entities on piezoelectric and dielectric properties: inclusion of an electrically conductive filler (Al), poling process (contact and Corona) and Al surface treatment, were observed. The piezoelectric strain coefficient, d33, effective dielectric constant, epsilon r, capacitance, C, and resistivity were measured and compared according to poling process, volume fraction of constituent phases and Al surface treatment. The maximum values of d33 were 3.475 and 1.0 pC/N for Corona and contact poled samples respectively, for samples with volume fractions of 0.40 and 0.13 of PZT and Al (surface treated) respectively. Also, the maximum dielectric constant for the surface treated Al samples was 411 for volume fractions of 0.40 and 0.13 for PZT and Al respectively. The percolation threshold was observed to occur at an Al volume fraction of 0.13. The composites achieved a percolated state for Al volume fractions >0.13 for both contact and corona poled samples. In addition, a comparative time study was conducted to examine the influence of surface treatment processing time of Al particles. The effectiveness of the surface treatment, sample morphology and composition was observed with the aid of SEM and EDS images. These images were correlated with piezoelectric and dielectric properties. PZT-epoxy-aluminum thick films (200 mum) were also fabricated using a two-step spin coat deposition and annealing method. The PZT volume fraction were varied from 0.2, 0.3 and 0.4, wherein the Aluminum volume fraction was varied from 0.1 to 0.17 for each PZT volume fraction, respectively. The two-step process included spin coating the first layer at 500 RPM for 30 seconds, and the second

  2. UV laser micromachining of piezoelectric ceramic using a pulsed Nd:YAG laser

    International Nuclear Information System (INIS)

    Zeng, D.W.; Xie, C.S.; Li, K.; Chan, H.L.W.; Choy, C.L.; Yung, K.C.

    2004-01-01

    UV laser (λ=355 nm) ablation of piezoelectric lead zirconate titanate (PZT) ceramics in air has been investigated under different laser parameters. It has been found that there is a critical pulse number (N=750). When the pulse number is smaller than the critical value, the ablation rate decreases with increasing pulse number. Beyond the critical value, the ablation rate becomes constant. The ablation rate and concentrations of O, Zr and Ti on the ablated surface increase with the laser fluence, while the Pb concentration decreases due to the selective evaporation of PbO. The loss of the Pb results in the formation of a metastable pyrochlore phase. ZrO 2 was detected by XPS in the ablated zone. Also, the concentrations of the pyrochlore phase and ZrO 2 increase with increasing laser fluence. These results clearly indicate that the chemical composition and phase structure in the ablated zone strongly depend on the laser fluence. The piezoelectric properties of the cut PZT ceramic samples completely disappear due to the loss of the Pb and the existence of the pyrochlore phase. After these samples were annealed at 1150 C for 1 h in a PbO-controlled atmosphere, their phase structure and piezoelectric properties were recovered again. Finally, 1-3 and concentric-ring 2-2 PZT/epoxy composites were fabricated by UV laser micromachining and their thickness modes were measured by impedance spectrum analysis and a d 33 meter. Both composites show high piezoelectric properties. (orig.)

  3. First-principles calculation of the effects of Li-doping on the structure and piezoelectricity of (K0.5Na0.5)NbO3 lead-free ceramics.

    Science.gov (United States)

    Yang, D; Wei, L L; Chao, X L; Yang, Z P; Zhou, X Y

    2016-03-21

    The crystal structures of the lead-free piezoelectric ceramics (K0.5Na0.5)NbO3 and (K0.5Na0.5)0.94Li0.06NbO3 prepared by a solid-state method were investigated using first-principles calculations. The calculated values of piezoelectricity were in good agreement with the experimental data. We found that the primary contribution to piezoelectricity in this material comes from the hybridization of the O 2p and Nb 4d orbitals, which causes a change in the Nb-O bond length and the distortion of the Nb-O octahedral structure. Analysis of the band structure and the total density of states revealed that Li-doped (K0.5Na0.5)NbO3 enhances hybridization of the O 2p and Nb 4d orbitals. This hybridization enhancement further reduces the Nb-O1 bond length and enhances the distortion of the Nb-O octahedron along the [001] direction, which may be the main reason for the improvement of the piezoelectric properties. In addition, the piezoelectric coefficients are calculated here, which show the same trend as the experimental results.

  4. Room temperature large self-biased magnetoelectric effect in non-lead based piezoelectric and magnetostrictive (0−3) particulate composite system

    International Nuclear Information System (INIS)

    Kumari, Mukesh; Prakash, Chandra; Chatterjee, Ratnamala

    2017-01-01

    In this work, room temperature magnetoelectric properties of (0−3) particulate composites of non lead based piezoelectric BNTKNNLTS [0.97(Bi 0.5 Na 0.5 TiO 3 )–0.03(K 0.47 Na 0.47 Li 0.06 Nb 0.74 Sb 0.06 Ta 0.2 O 3 ) and magnetostrictive CZFMO (Co 0.6 Zn 0.4 Fe 1.7 Mn 0.3 O 4 ) are presented. Composite samples of (1-x)(BNTKNNLTS)-x(CZFMO) , with x=0.1 and 0.5, are synthesized by solid state reaction route. X-ray diffraction confirms the single phase formation of parent phases and the presence of two phases in the composites. Similar sintering conditions of the two individual components lead to optimal ferroelectric and ferromagnetic properties in the composites. A large self-biased magnetoelectric (ME) coupling ~74 mV/cm.Oe for the sample with x=0.1 (measured in longitudinally magnetized-transversely polarized configuration) is observed at room temperature. - Highlights: • Modified BNT-CFO based (0−3) particulate composites have been synthesized. • Similar sintering conditions of two components lead to optimal multiferroicity. • A large self-biased ME coupling ~74 mV/cm. Oe is obtained at room temperature.

  5. Enhanced piezoelectricity in (1 -x)Bi1.05Fe1-yAyO3-xBaTiO3 lead-free ceramics: site engineering and wide phase boundary region.

    Science.gov (United States)

    Zheng, Ting; Jiang, Zhenggen; Wu, Jiagang

    2016-07-28

    Site engineering has been employed to modulate the piezoelectric activity of high temperature (1 -x)Bi1.05Fe1-yScyO3-xBaTiO3 lead-free ceramics fabricated by a conventional solid-state method together with a quenching technique. The effects of x and y content on the phase structure, microstructure, and electrical properties have been investigated in detail. A wide rhombohedral (R) to pseudo-cubic (C) phase boundary was formed in the ceramics with x = 0.30 and 0 ≤y≤ 0.07, thus leading to enhanced piezoelectricity (d33 = 120-180 pC N(-1)), ferroelectricity (Pr = 19-22 μC cm(-2)) and a high Curie temperature (TC = 478-520 °C). In addition, the influence of different element substitutions for Fe(3+) on phase structure and electrical behavior was also investigated. Improved piezoelectricity (d33 = 160-180 pC N(-1)) and saturated P-E loops can be simultaneously achieved in the ceramics with A = Sc, Ga, and Al due to the R-C phase boundary. As a result, site engineering may be an efficient way to modulate the piezoelectricity of BiFeO3-BaTiO3 lead-free ceramics.

  6. Piezoelectric displacement in ceramics

    International Nuclear Information System (INIS)

    Stewart, M.; Cain, M.; Gee, M.

    1999-01-01

    This Good Practice Guide is intended to aid a user to perform displacement measurements on piezoelectric ceramic materials such as PZT (lead zirconium titanate) in either monolithic or multilayer form. The various measurement issues that the user must consider are addressed, and good measurement practise is described for the four most suitable methods. (author)

  7. Reliable Piezoelectricity in Bilayer WSe2 for Piezoelectric Nanogenerators.

    Science.gov (United States)

    Lee, Ju-Hyuck; Park, Jae Young; Cho, Eun Bi; Kim, Tae Yun; Han, Sang A; Kim, Tae-Ho; Liu, Yanan; Kim, Sung Kyun; Roh, Chang Jae; Yoon, Hong-Joon; Ryu, Hanjun; Seung, Wanchul; Lee, Jong Seok; Lee, Jaichan; Kim, Sang-Woo

    2017-08-01

    Recently, piezoelectricity has been observed in 2D atomically thin materials, such as hexagonal-boron nitride, graphene, and transition metal dichalcogenides (TMDs). Specifically, exfoliated monolayer MoS 2 exhibits a high piezoelectricity that is comparable to that of traditional piezoelectric materials. However, monolayer TMD materials are not regarded as suitable for actual piezoelectric devices due to their insufficient mechanical durability for sustained operation while Bernal-stacked bilayer TMD materials lose noncentrosymmetry and consequently piezoelectricity. Here, it is shown that WSe 2 bilayers fabricated via turbostratic stacking have reliable piezoelectric properties that cannot be obtained from a mechanically exfoliated WSe 2 bilayer with Bernal stacking. Turbostratic stacking refers to the transfer of each chemical vapor deposition (CVD)-grown WSe 2 monolayer to allow for an increase in degrees of freedom in the bilayer symmetry, leading to noncentrosymmetry in the bilayers. In contrast, CVD-grown WSe 2 bilayers exhibit very weak piezoelectricity because of the energetics and crystallographic orientation. The flexible piezoelectric WSe 2 bilayers exhibit a prominent mechanical durability of up to 0.95% of strain as well as reliable energy harvesting performance, which is adequate to drive a small liquid crystal display without external energy sources, in contrast to monolayer WSe 2 for which the device performance becomes degraded above a strain of 0.63%. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  8. Going back in time with zircon

    International Nuclear Information System (INIS)

    Burger, A.; Faurie, J.

    1978-01-01

    Uranium-lead age dating, with zircon as the agent is the most recent advance in exploring rocks and minerals to define their stratigraphic sequence. The authors believe it will have a tremendous effect on the accurate mapping of the earth's mineral resources, including those of Antartica; indeed, even of the moon

  9. Study of the microstructure and the hardness of PZT piezoelectric ceramics types I and III used in electro acoustic transducers; Estudo da microestrutura e da microdureza das ceramicas piezoeletricas tipos PZT I e III utilizadas em transdutores eletroacusticos

    Energy Technology Data Exchange (ETDEWEB)

    Cabral, Ricardo de Freitas; Itaboray, Lucas Mendes; Santos, Anna Paula de Oliveira [Centro Universitario de Volta Redonda (UNIFOA), Volta Redonda, RJ (Brazil)

    2015-12-15

    The field of electronic processing of the ceramic piezoelectric type imported powdered led to the production of ceramics with 97% of theoretical density, homogeneous microstructure with great potential for applications in piezoelectric devices such as electro acoustic transducers. However, the production of electronic ceramics National piezoelectric type is not yet able to have as raw material zirconate titanate Lead (PZT) 100% made in Brazil. Thus, this is used for supply of domestic production, the zirconium oxide. In this work, both post PZT types I and III, imported, were uniaxially pressed at 70 MPa and sintered at 1200 and 1250 deg C for 3 hours. Hardness measurements were performed by micro indentation, X-ray diffraction analysis and Scanning Electron Microscopy. The hardness of PZT I was 393 HV. (author)

  10. Low sintering temperature and high piezoelectric properties of Li-doped (Ba,Ca)(Ti,Zr)O{sub 3} lead-free ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Xiaoming [Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); University of Chinese Academy of Sciences, Beijing 100039 (China); School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237 (China); Ruan, Xuezheng; Zhao, Kunyun [Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); He, Xueqing [School of Materials and Metallurgy, Northeastern University, Shenyang 110004 (China); Zeng, Jiangtao, E-mail: zjt@mail.sic.ac.cn [Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); Li, Yongsheng [School of Materials Science and Engineering, East China University of Science and Technology, Shanghai 200237 (China); Zheng, Liaoying [Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); Park, Chul Hong [Department of Physics Education, Pusan National University, Pusan 609735 (Korea, Republic of); Li, Guorong [Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China)

    2015-05-25

    Highlights: • Li-doped Ba{sub 0.85}Ca{sub 0.15}Ti{sub 0.9}Zr{sub 0.1}O{sub 3} (BCZT) lead-free piezoceramics were prepared by the two-step synthesis and solid-state reaction method. • Their sintering temperature decreases from about 1540 °C down to about 1400 °C. • With the proper addition of Li, the densities and grain sizes of ceramics increase. • The ceramics not only have the characteristics of hard piezoceramics but also possesses the features of soft piezoceramics at low sintering temperature. - Abstract: Li-doped Ba{sub 0.85}Ca{sub 0.15}Ti{sub 0.9}Zr{sub 0.1}O{sub 3} (BCZT) lead-free piezoelectric ceramics were prepared by the two-step synthesis and the solid-state reaction method. The density and grain size of ceramics sufficiently increases by Li-doped sintering aid, and their sintering temperature decreases from about 1540 °C down to about 1400 °C. X-ray diffraction reveals that the phase structure of Li-doped BCTZ ceramics is changed with the sintering temperature, which is consistent with their phase transition observed by the temperature-dependent dielectric curves. The well-poled Li-doped BCZT ceramics show a high piezoelectric constant d{sub 33} (512 pC/N) and a planar electromechanical coupling factor k{sub p} (0.49), which have the characteristics of soft Pb(Zr,Ti)O{sub 3} (PZT) piezoceramic, on the other hand, the mechanical quality factor Q{sub m} is about 190, which possesses the features of hard PZT piezoceramics. The enhanced properties of the Li-doped BCZT are explained by the combination of Li-doped effect and sintering effect on the microstructure and the phase transition around room temperature.

  11. Enhanced pyroelectric and piezoelectric properties of PZT with aligned porosity for energy harvesting applications.

    Science.gov (United States)

    Zhang, Yan; Xie, Mengying; Roscow, James; Bao, Yinxiang; Zhou, Kechao; Zhang, Dou; Bowen, Chris R

    2017-04-14

    This paper demonstrates the significant benefits of exploiting highly aligned porosity in piezoelectric and pyroelectric materials for improved energy harvesting performance. Porous lead zirconate (PZT) ceramics with aligned pore channels and varying fractions of porosity were manufactured in a water-based suspension using freeze-casting. The aligned porous PZT ceramics were characterized in detail for both piezoelectric and pyroelectric properties and their energy harvesting performance figures of merit were assessed parallel and perpendicular to the freezing direction. As a result of the introduction of porosity into the ceramic microstructure, high piezoelectric and pyroelectric harvesting figures of merits were achieved for porous freeze-cast PZT compared to dense PZT due to the reduced permittivity and volume specific heat capacity. Experimental results were compared to parallel and series analytical models with good agreement and the PZT with porosity aligned parallel to the freezing direction exhibited the highest piezoelectric and pyroelectric harvesting response; this was a result of the enhanced interconnectivity of the ferroelectric material along the poling direction and reduced fraction of unpoled material that leads to a higher polarization. A complete thermal energy harvesting system, composed of a parallel-aligned PZT harvester element and an AC/DC converter, was successfully demonstrated by charging a storage capacitor. The maximum energy density generated by the 60 vol% porous parallel-connected PZT when subjected to thermal oscillations was 1653 μJ cm -3 , which was 374% higher than that of the dense PZT with an energy density of 446 μJ cm -3 . The results are beneficial for the design and manufacture of high performance porous pyroelectric and piezoelectric materials in devices for energy harvesting and sensor applications.

  12. Soft pneumatic actuator skin with piezoelectric sensors for vibrotactile feedback

    Directory of Open Access Journals (Sweden)

    Harshal Arun Sonar

    2016-01-01

    Full Text Available The latest wearable technologies demand more intuitive and sophisticated interfaces for communication, sensing, and feedback closer to the body. Evidently, such interfaces require flexibility and conformity without losing their functionality even on rigid surfaces. Although there has been various research efforts in creating tactile feedback to improve various haptic interfaces and master-slave manipulators, we are yet to see a comprehensive device that can both supply vibratory actuation and tactile sensing. This paper describes a soft pneumatic actuator (SPA based, SPA-skin prototype that allows bidirectional tactile information transfer to facilitate simpler and responsive wearable interface. We describe the design and fabrication of a 1.4 mm-thick vibratory SPA - skin that is integrated with piezoelectric sensors. We examine in detail the mechanical performance compared to the SPA model and the sensitivity of the sensors for the application in vibrotactile feedback. Experimental findings show that this ultra-thin SPA and the unique integration process of the discrete lead zirconate titanate (PZT based piezoelectric sensors achieve high resolution of soft contact sensing as well as accurate control on vibrotactile feedback by closing the control loop.

  13. In-situ poling and structurization of piezoelectric particulate composites.

    Science.gov (United States)

    Khanbareh, H; van der Zwaag, S; Groen, W A

    2017-11-01

    Composites of lead zirconate titanate particles in an epoxy matrix are prepared in the form of 0-3 and quasi 1-3 with different ceramic volume contents from 10% to 50%. Two different processing routes are tested. Firstly a conventional dielectrophoretic structuring is used to induce a chain-like particle configuration, followed by curing the matrix and poling at a high temperature and under a high voltage. Secondly a simultaneous combination of dielectrophoresis and poling is applied at room temperature while the polymer is in the liquid state followed by subsequent curing. This new processing route is practiced in an uncured thermoset system while the polymer matrix still possess a relatively high electrical conductivity. Composites with different degrees of alignment are produced by altering the magnitude of the applied electric field. A significant improvement in piezoelectric properties of quasi 1-3 composites can be achieved by a combination of dielectrophoretic alignment of the ceramic particles and poling process. It has been observed that the degree of structuring as well as the functional properties of the in-situ structured and poled composites enhance significantly compared to those of the conventionally manufactured structured composites. Improving the alignment quality enhances the piezoelectric properties of the particulate composites.

  14. Determination of the piezoelectric properties of fine scale PZT fibres

    Energy Technology Data Exchange (ETDEWEB)

    Nelson, L.J.; Bowen, C.R. [Bath Univ. (United Kingdom). Dept. of Engineering and Applied Science

    2002-07-01

    Finite element (FE) modelling is used to determine the effect of fibre volume fraction, aspect ratio and polymer matrix stiffness on the d{sub 33} coefficients of 1-3 connectivity piezoelectric fibre composites. The aim is to use these observations as a means of determining the d{sub 33} of fine scale lead zirconate titanate (PZT) fibres. Results from a 1-D analytical model fit well with FE predictions for low aspect ratios. Two commercially available PZT-5A fibres, produced via the viscous suspension spinning process (VSSP) and an extrusion process, were fabricated into 1-3 composites with varying fibre volume fractions. The composite d{sub 33} measurements are compared to the model predictions and used to determine the d{sub 33} coefficients of the fibers. The d{sub 33} of the VSSP fibres and extruded fibres is measured as 365 pCN{sup -1} and 235 pCN{sup -1} respectively using this method. The large difference in the piezoelectric coefficients is possibly linked to the grain size and porosity, which is examined using scanning electron microscopy. (orig.)

  15. Room temperature large self-biased magnetoelectric effect in non-lead based piezoelectric and magnetostrictive (0−3) particulate composite system

    Energy Technology Data Exchange (ETDEWEB)

    Kumari, Mukesh [Magnetics & Advanced Ceramics Laboratory, Indian Institute of Technology, Delhi-110016 India (India); Prakash, Chandra [Solid State Physics Laboratory Timarpur, Delhi-110054 India (India); Chatterjee, Ratnamala, E-mail: rmala@physics.iitd.ac.in [Magnetics & Advanced Ceramics Laboratory, Indian Institute of Technology, Delhi-110016 India (India)

    2017-05-01

    In this work, room temperature magnetoelectric properties of (0−3) particulate composites of non lead based piezoelectric BNTKNNLTS [0.97(Bi{sub 0.5}Na{sub 0.5}TiO{sub 3})–0.03(K{sub 0.47}Na{sub 0.47}Li{sub 0.06}Nb{sub 0.74}Sb{sub 0.06}Ta{sub 0.2}O{sub 3}) and magnetostrictive CZFMO (Co{sub 0.6}Zn{sub 0.4}Fe{sub 1.7}Mn{sub 0.3}O{sub 4}) are presented. Composite samples of (1-x)(BNTKNNLTS)-x(CZFMO){sub ,} with x=0.1 and 0.5, are synthesized by solid state reaction route. X-ray diffraction confirms the single phase formation of parent phases and the presence of two phases in the composites. Similar sintering conditions of the two individual components lead to optimal ferroelectric and ferromagnetic properties in the composites. A large self-biased magnetoelectric (ME) coupling ~74 mV/cm.Oe for the sample with x=0.1 (measured in longitudinally magnetized-transversely polarized configuration) is observed at room temperature. - Highlights: • Modified BNT-CFO based (0−3) particulate composites have been synthesized. • Similar sintering conditions of two components lead to optimal multiferroicity. • A large self-biased ME coupling ~74 mV/cm. Oe is obtained at room temperature.

  16. Morphotropic NaNbO{sub 3}-BaTiO{sub 3}-CaZrO{sub 3} lead-free ceramics with temperature-insensitive piezoelectric properties

    Energy Technology Data Exchange (ETDEWEB)

    Zuo, Ruzhong, E-mail: piezolab@hfut.edu.cn, E-mail: rzzuo@hotmail.com; Qi, He; Fu, Jian [Institute of Electro Ceramics and Devices, School of Materials Science and Engineering, Hefei University of Technology, Hefei, 230009 (China)

    2016-07-11

    A morphotropic NaNbO{sub 3}-based lead-free ceramic was reported to have temperature-insensitive piezoelectric and electromechanical properties (d{sub 33} = 231 pC/N, k{sub p} = 35%, T{sub c} = 148 °C, and low-hysteresis strain ∼0.15%) in a relatively wide temperature range. This was fundamentally ascribed to the finding of a composition-axis vertical morphotropic phase boundary in which coexisting ferroelectric phases are only compositionally driven and thermally insensitive. Both phase coexistence and nano-scaled domain morphology deserved well enhanced electrical properties, as evidenced by means of synchrotron x-ray diffraction and transmission electron microscopy. Our study suggests that the current lead-free ceramic would be a very promising piezoelectric material for actuator and sensor applications.

  17. Evolution of phase structure and giant strain at low driving fields in Bi-based lead-free incipient piezoelectrics

    International Nuclear Information System (INIS)

    Maqbool, Adnan; Hussain, Ali; Malik, Rizwan Ahmed; Rahman, Jamil Ur; Zaman, Arif; Song, Tae Kwon; Kim, Won-Jeong; Kim, Myong-Ho

    2015-01-01

    Graphical abstract: - Highlights: • Nb-doped BNBT–SZ ceramics were prepared by conventional solid state method. • A giant normalized strain of 825 pm/V at 4 kV/mm was achieved. • A large strain of 0.20% triggered at a relatively low field of 3 kV/mm. • Highest strain obtained in BNT-based ceramics at such a low driving field. • Ferroelectric to ergodic-relaxor phase transition occurred with Nb-doping. - Abstract: Lead-free 0.99[(Bi 0.5 Na 0.5 ) 0.935 Ba 0.065 Ti (1–x) Nb x O 3 ]–0.01SrZrO 3 (BNBTNb100x–SZ, with Nb100x = 0–1) ceramics were prepared by the conventional mixed oxide route. X-ray diffraction and Raman scattering was utilized for the structural evolution of Nb-modified BNBT–SZ ceramics at average and short-scale localized structure. Temperature dependent dielectric properties showed ferroelectric–ergodic relaxor (FE–ER) transition in Nb-modified BNBT–SZ ceramics by producing a significant disruption of the long-range FE order. A giant normalized strain of 825 pm/V at 4 kV/mm was achieved at Nb1.0. Interestingly, at a relatively low applied field of 3 kV/mm, the Nb0.75 sample displayed a large electric field-induced strain (EFIS) response of 0.20%, which is highest value obtained in non-textured lead-free BNT-based ceramics at such low driving field. The structural distortion induced by doping and electric poling is correlated with the dielectric, ferroelectric and EFIS response, and the evolution of giant strain was ascribed to reversible field induced phase transition from ER–FE phase

  18. Design, Modeling and Optimization of a Piezoelectric Pressure Sensor based on a Thin-Film PZT Membrane Containing Nanocrystalline Powders

    Directory of Open Access Journals (Sweden)

    Vahid MOHAMMADI

    2009-11-01

    Full Text Available In this paper fabrication of a 0-3 ceramic/ceramic composite lead zirconate titanate, Pb(Zr0.52Ti0.48O3 thin film has been presented and then a pressure sensor based on multilayer thin-film PZT diaphragm contain of Lead Zirconate Titanate nanocrystalline powders was designed, modeled and optimized. Dynamics characteristics of this multilayer diaphragm have been investigated by ANSYS® FE software. By this simulation the effective parameters of the multilayer PZT diaphragm for improving the performance of a pressure sensor in different ranges of pressure are optimized. The optimized thickness ratio of PZT layer to SiO2 was given in the paper to obtain the maximum deflection of the multilayer thin-film PZT diaphragm. A 0-3 ceramic/ceramic composite lead zirconate titanate, Pb(Zr0.52Ti0.48O3 film has been developed to fabricate the pressure sensor by a hybrid sol gel process. PZT nanopowders fabricated via conventional sol gel method and uniformly dispersed in PZT precursor solution by an attrition mill. XRD analysis shows that perovskite structure would be formed due to the presence of a significant amount of ceramic nanopowders. This texture has a good effect on piezoelectric properties of perovskite structure. The film forms a strongly bonded network and less shrinkage occurs, so the films do not crack during process. Also the aspect ratio through this process would be increased. SEM micrographs indicated that PZT films were uniform, crack free and have a composite microstructure and a piezoelectric coefficient d31 of -40 pC.N-1 and d33 ranged from 50pm.N-1 to 60pm.N-1.

  19. Highly selective piezoelectric sensor for lead(II) based on the lead-catalyzed release of gold nanoparticles from a self-assembled nanosurface

    International Nuclear Information System (INIS)

    Xie, Yunfeng; Jin, Yulong; Huang, Yanyan; Liu, Guoquan; Zhao, Rui

    2014-01-01

    A novel quartz crystal microbalance (QCM) sensor has been developed for highly selective and sensitive detection of Pb 2+ by exploiting the catalytic effect of Pb 2+ ions on the leaching of gold nanoparticles from the surface of a QCM sensor. The use of self-assembled gold nanoparticles (AuNPs) strongly enlarges the size of the interface and thus amplifies the analytical response resulting from the loss of mass. This results in a very low detection limit for Pb 2+ (30 nM). The high selectivity is demonstrated by studying the effect of potentially interfering ions both in the absence and presence of Pb 2+ ions. This simple and well reproducible sensor was applied to the determination of lead in the spiked drinking water. This work provides a novel strategy for fabricating QCM sensors towards Pb 2+ in real samples. (author)

  20. X-band EPR studies of ferroelectric lead titanate (PT), piezoelectric lead magnesium niobate (PMN), and PMN/PT powders at 10 and 85 K

    International Nuclear Information System (INIS)

    Huang, J.; Fitzgerald, J.J.; Chasteen, N.D.

    1998-01-01

    X-band EPR spectra of lead titanate (PT) and lead magnesium niobate (PMN) powders prepared by different synthetic methods and a PMN/PT powder of the composition 0.9 PMN/01 PT were obtained at 85 and 10 K. Several EPR signals due to adventitious Fe 3+ ion impurities, a signal due to the Ti 3+ ion, and a signal due to the Pb 3+ ion are observed for PT, PMN, and PMN/PT powders. The EPR signals observed at g = 2.0 and 6.0 are assigned to Fe 3+ ions in the B-sites of the perovskite lattice structure of lad titanate with axial symmetry. The EPR signals observed at g = 1.99 and 4.25 are assigned to Fe 3+ ions in the B-sites of the perovskite lattice structure of PMN and 0.9 PMN/0.1 PT materials with cubic and rhombic symmetries, respectively. The sharp EPR signal observed at g = 1.94 is assigned to Ti 3= ion for PT and 0.9 PMN/0.1 PT powders. In addition, a broader EPR signal at g = 2.28--2.30 for PMN obtained by the molten salt method is assigned to axial Pb 3+ ion sites in this PMN material. EPR results obtained here for the e 3+ ions in the B-sites of the PMN materials, in particular, suggest that both cubic and rhombic symmetry sites corresponding to a range of Nb(OMg) x (ONb) 6-x site configurations exist in the PMN. These EPR results indicate that PMN likely exists with partial B-site cation (Mg/Nb) ordering in the perovskite lattice structure

  1. Nonlinear vibration analysis of the high-efficiency compressive-mode piezoelectric energy harvester

    Science.gov (United States)

    Yang, Zhengbao; Zu, Jean

    2015-04-01

    Power source is critical to achieve independent and autonomous operations of electronic mobile devices. The vibration-based energy harvesting is extensively studied recently, and recognized as a promising technology to realize inexhaustible power supply for small-scale electronics. Among various approaches, the piezoelectric energy harvesting has gained the most attention due to its high conversion efficiency and simple configurations. However, most of piezoelectric energy harvesters (PEHs) to date are based on bending-beam structures and can only generate limited power with a narrow working bandwidth. The insufficient electric output has greatly impeded their practical applications. In this paper, we present an innovative lead zirconate titanate (PZT) energy harvester, named high-efficiency compressive-mode piezoelectric energy harvester (HC-PEH), to enhance the performance of energy harvesters. A theoretical model was developed analytically, and solved numerically to study the nonlinear characteristics of the HC-PEH. The results estimated by the developed model agree well with the experimental data from the fabricated prototype. The HC-PEH shows strong nonlinear responses, favorable working bandwidth and superior power output. Under a weak excitation of 0.3 g (g = 9.8 m/s2), a maximum power output 30 mW is generated at 22 Hz, which is about ten times better than current energy harvesters. The HC-PEH demonstrates the capability of generating enough power for most of wireless sensors.

  2. Piezo-generated charge mapping revealed through direct piezoelectric force microscopy.

    Science.gov (United States)

    Gomez, A; Gich, M; Carretero-Genevrier, A; Puig, T; Obradors, X

    2017-10-24

    While piezoelectric and ferroelectric materials play a key role in many everyday applications, there are still a number of open questions related to their physics. To enhance our understanding of piezoelectrics and ferroelectrics, nanoscale characterization is essential. Here, we develop an atomic force microscopy based mode that obtains a direct quantitative analysis of the piezoelectric coefficient d 33 . We report nanoscale images of piezogenerated charge in a thick single crystal of periodically poled lithium niobate (PPLN), a bismuth ferrite (BiFO 3 ) thin film, and lead zirconate titanate (PZT) by applying a force and recording the current produced by these materials. The quantification of d 33 coefficients for PPLN (14 ± 3 pC per N) and BFO (43 ± 6 pC per N) is in agreement with the values reported in the literature. Even stronger evidence of the reliability of the method is provided by an equally accurate measurement of the significantly larger d 33 of PZT.

  3. In situ 2D diffraction as a tool to characterize ferroelectric and piezoelectric thin films

    Science.gov (United States)

    Khamidy, N. I.; Kovacova, V.; Bernasconi, A.; Le Rhun, G.; Vaxelaire, N.

    2017-08-01

    In this paper the application of 2D x-ray diffraction (XRD2) as a technique to characterize in situ during electrical cycling the properties of a ferroelectric and piezoelectric thin film is discussed. XRD2 is one type of XRD on which a 2D detector is used instead of a point detector. This technique enables simultaneous recording of many sample information in a much shorter time compared to conventional XRD. The discussion is focused especially on the data processing technique of the huge data acquired. The methodology to calculate an effective piezoelectric coefficient, analyze the phase and texture, and estimate the domain size and shape is described in this paper. This methodology is then applied to a lead zirconate titanate (PZT) thin film at the morphotropic phase boundary (MPB) composition (i.e. Pb[Zr0.52Ti0.48]O3) with a preferred orientation of (1 0 0). The in situ XRD2 characterization was conducted in the European synchrotron radiation facility (ESRF) in Grenoble, France. Since a high-energy beam with vertical resolution as small as 100 nm was used, a cross-sectional scan of the sample was performed over the entire thickness of the film. From these experimental results, a better understanding on the piezoelectricity phenomena in PZT thin film at MPB composition were achieved, providing original feedback between the elaboration processes and functional properties of the film.

  4. The effects of sintering behavior on piezoelectric properties of porous PZT ceramics for hydrophone application

    International Nuclear Information System (INIS)

    Zeng Tao; Dong Xianlin; Chen Heng; Wang Yonglin

    2006-01-01

    Porous lead zirconate titanate (PZT) ceramics were fabricated by adding polymethyl methacrylate (PMMA) and the effects of sintering behavior on their microstructure and piezoelectric properties were investigated. The porosity of PZT ceramics decreased with an increase in the sintering temperature at a fixed PMMA addition. The dielectric constant (ε), longitudinal piezoelectric coefficient (d 33 ) and hydrostatic figures of merit (d h g h ) of 34% porous PZT ceramics increased with an increase in sintering temperature from 1050 to 1300 deg. C. When sintered at 1300 deg. C, longitudinal piezoelectric coefficient of 34% porous PZT ceramic was very close to that of 95% dense PZT ceramics, while the hydrostatic figures of merit of 34% porous PZT ceramics is about fifteen times more than that of 95% dense PZT ceramics. Compared with PZT-polymer composites, the dielectric constant of 34% porous PZT sintered at 1300 deg. C is much higher, which can be more efficient to resist the interference in receiving sensitivities caused by loading effect of the cable

  5. Two-Dimensional Lead(II) Halide-Based Hybrid Perovskites Templated by Acene Alkylamines: Crystal Structures, Optical Properties, and Piezoelectricity.

    Science.gov (United States)

    Du, Ke-Zhao; Tu, Qing; Zhang, Xu; Han, Qiwei; Liu, Jie; Zauscher, Stefan; Mitzi, David B

    2017-08-07

    A series of two-dimensional (2D) hybrid organic-inorganic perovskite (HOIP) crystals, based on acene alkylamine cations (i.e., phenylmethylammonium (PMA), 2-phenylethylammonium (PEA), 1-(2-naphthyl)methanammonium (NMA), and 2-(2-naphthyl)ethanammonium (NEA)) and lead(II) halide (i.e., PbX 4 2- , X = Cl, Br, and I) frameworks, and their corresponding thin films were fabricated and examined for structure-property relationship. Several new or redetermined crystal structures are reported, including those for (NEA) 2 PbI 4 , (NEA) 2 PbBr 4 , (NMA) 2 PbBr 4 , (PMA) 2 PbBr 4 , and (PEA) 2 PbI 4 . Non-centrosymmetric structures from among these 2D HOIPs were confirmed by piezoresponse force microscopy-especially noteworthy is the structure of (PMA) 2 PbBr 4 , which was previously reported as centrosymmetric. Examination of the impact of organic cation and inorganic layer choice on the exciton absorption/emission properties, among the set of compounds considered, reveals that perovskite layer distortion (i.e., Pb-I-Pb bond angle between adjacent PbI 6 octahedra) has a more global effect on the exciton properties than octahedral distortion (i.e., variation of I-Pb-I bond angles and discrepancy among Pb-I bond lengths within each PbI 6 octahedron). In addition to the characteristic sharp exciton emission for each perovskite, (PMA) 2 PbCl 4 , (PEA) 2 PbCl 4 , (NMA) 2 PbCl 4 , and (PMA) 2 PbBr 4 exhibit separate, broad "white" emission in the long wavelength range. Piezoelectric compounds identified from these 2D HOIPs may be considered for future piezoresponse-type energy or electronic applications.

  6. Mechanical bending strength of (Bi0.5Na0.5 TiO3-based lead-Free piezoelectric ceramics

    Directory of Open Access Journals (Sweden)

    Hiroaki Takahashi

    2017-09-01

    Full Text Available (Bi0.5Na0.5TiO3 [BNT] is expected as one of candidate lead-free materials because these ceramics show relatively good high-power piezoelectric properties. In this study, we tried to understand the bending strength and fracture behavior of the BNT-based ceramics. To measure the bending strength, a three-point bending test on the basis of JIS was conducted using 12.0 × 4.0 × 1.0 mm3 specimens. An average bending strength, σA, of pure BNT ceramics sintered at 1100 °C for 2, 12 and 24 h were 217, 195 and 187 MPa, respectively. It is cleared that the σA increased with decreasing the sintering time, (grain size and pore size. We also investigated the bending strength of Nb2O5 doped BNT ceramics [BNT-Nb x, x = 0.05 ∼ 1.5 wt%] and MnCO3 doped BNT ceramics [BNT-Mn x, x = 0.5 and 1.0 wt%]. Values of the σA of BNT-Nb 0.5 and BNT-Mn 0.5 were 222, and 188 MPa, respectively. It is clarified that soft dopants (Nb can improve the bending strength of BNT-based ceramics. Additionally, hot-pressed BNT [HP-BNT] were sintered at 1050 °C for 5 h, and the σA of HP-BNT was 245 MPa.

  7. A nanoscale piezoelectric transformer for low-voltage transistors.

    Science.gov (United States)

    Agarwal, Sapan; Yablonovitch, Eli

    2014-11-12

    A novel piezoelectric voltage transformer for low-voltage transistors is proposed. Placing a piezoelectric transformer on the gate of a field-effect transistor results in the piezoelectric transformer field-effect transistor that can switch at significantly lower voltages than a conventional transistor. The piezoelectric transformer operates by using one piezoelectric to squeeze another piezoelectric to generate a higher output voltage than the input voltage. Multiple piezoelectrics can be used to squeeze a single piezoelectric layer to generate an even higher voltage amplification. Coupled electrical and mechanical modeling in COMSOL predicts a 12.5× voltage amplification for a six-layer piezoelectric transformer. This would lead to more than a 150× reduction in the power needed for communications.

  8. Applications of Piezoelectric Ceramics

    Indian Academy of Sciences (India)

    Applications of Piezoelectric Ceramics. Piezoelectric Actuators. Nano and Micropositioners. Vibration Control Systems. Computer Printers. Piezoelectric Transformers,Voltage Generators, Spark Plugs, Ultrasonic Motors,. Ultrasonic Generators and Sensors. Sonars, Medical Diagnostic. Computer Memories. NVFRAM ...

  9. ALKALI FUSION OF ROSETTA ZIRCON

    International Nuclear Information System (INIS)

    DAHER, A.

    2008-01-01

    The decomposition of Rosetta zircon by fusion with different types of alkalis has been investigated. These alkalis include sodium hydroxide, potassium hydroxide and eutectic mixture of both. The influences of the reaction temperature, zircon to alkalis ratio, fusion time and the stirring of the reactant on the fusion reaction have been evaluated. The obtained results favour the decomposition of zircon with the eutectic alkalis mixture by a decomposition efficiency of 96% obtained at 500 0 C after one hour

  10. Investigation of structural, ferroelectric, piezoelectric and dielectric properties of Ba0.92Ca0.08TiO3-BaTi0.96Zr0.04O3 lead-free electroceramics

    Science.gov (United States)

    Keswani, Bhavna C.; Patil, S. I.; Kolekar, Y. D.

    2018-04-01

    Lead free ferroelectric with composition 0.55Ba0.92Ca0.08TiO3-0.45BaTi0.96Zr0.04O3 (BCT8-BZT4) was synthesized by solid state reaction method and investigated their structural, ferroelectric, piezoelectric and dielectric properties. X-ray diffraction analysis shows that BCT8-BZT4 ceramic possess both tetragonal (space group P4mm) and orthorhombic (space group Amm2) crystal structure which was further confirmed from Raman spectra spectroscopy. The micronized grains were observed from scanning electron micrographs while the presence of polarization-electric field hysteresis loop confirms ferroelectric nature of BCT8-BZT4 ceramic. Higher values of maximum polarization (Pmax = 22.27 μC/cm2), remnant polarization (Pr = 11.61 μC/cm2), coercive electric field (Ec = 4.77 kV/cm) and direct piezoelectric coefficient (d33) approximately 185 pC/N were observed. The real part of dielectric constant with frequency shows the usual dielectric dispersion behaviour at RT. The observed properties show that the lead free BCT8-BZT4 ceramic is suitable for ferroelectric memory device, piezoelectric sensor, capacitor, etc. applications.

  11. Oxygen diffusion in zircon

    Science.gov (United States)

    Watson, E. B.; Cherniak, D. J.

    1997-05-01

    Oxygen diffusion in natural, non-metamict zircon was characterized under both dry and water-present conditions at temperatures ranging from 765°C to 1500°C. Dry experiments were performed at atmospheric pressure by encapsulating polished zircon samples with a fine powder of 18O-enriched quartz and annealing the sealed capsules in air. Hydrothermal runs were conducted in cold-seal pressure vessels (7-70 MPa) or a piston cylinder apparatus (400-1000 MPa) on zircon samples encapsulated with both 18O-enriched quartz and 18O water. Diffusive-uptake profiles of 18O were measured in all samples with a particle accelerator, using the 18O(p, α) 15N reaction. For dry experimental conditions at 1100-1500°C, the resulting oxygen diffusivities (24 in all) are well described by: D dry (m 2/s) = 1.33 × 10 -4exp(-53920/T) There is no suggestion of diffusive anisotropy. Under wet conditions at 925°C, oxygen diffusion shows little or no dependence upon P H 2O in the range 7-1000 MPa, and is insensitive to total pressure as well. The results of 27 wet experiments at 767-1160°C and 7-1000 MPa can be described a single Arrhenius relationship: D wet (m 2/s) = 5.5 × 10 -12exp(-25280/T) The insensitivity of oxygen diffusion to P H 2O means that applications to geologic problems can be pursued knowing only whether the system of interest was 'wet' (i.e., P H 2O > 7MPa ) or 'dry'. Under dry conditions (presumably rare in the crust), zircons are extremely retentive of their oxygen isotopic signatures, to the extent that δ 18O would be perturbed at the center of a 200 μm zircon only during an extraordinarily hot and protracted event (e.g., 65 Ma at 900°C). Under wet conditions, δ 18O may or may not be retained in the central regions of individual crystals, cores or overgrowth rims, depending upon the specific thermal history of the system.

  12. Optimal design of robust piezoelectric unimorph microgrippers

    DEFF Research Database (Denmark)

    Ruiz, David; Díaz-Molina, Alex; Sigmund, Ole

    2018-01-01

    Topology optimization can be used to design piezoelectric actuators by simultaneous design of host structure and polarization profile. Subsequent micro-scale fabrication leads us to overcome important manufacturing limitations: difficulties in placing a piezoelectric layer on both top and bottom...

  13. Experiments to Demonstrate Piezoelectric and Pyroelectric Effects

    Science.gov (United States)

    Erhart, Jirí

    2013-01-01

    Piezoelectric and pyroelectric materials are used in many current applications. The purpose of this paper is to explain the basic properties of pyroelectric and piezoelectric effects and demonstrate them in simple experiments. Pyroelectricity is presented on lead zirconium titanate (PZT) ceramics as an electric charge generated by the temperature…

  14. Tailored piezoelectric thin films for energy harvester

    NARCIS (Netherlands)

    Wan, X.

    2013-01-01

    Piezoelectric materials are excellent materials to transfer mechanical energy into electrical energy, which can be stored and used to power other devices. PiezoMEMS is a good way to combine silicon wafer processing and piezoelectric thin film technology and lead to a variety of miniaturized and

  15. High-Throughput Investigation of a Lead-Free AlN-Based Piezoelectric Material, (Mg,Hf)xAl1-xN.

    Science.gov (United States)

    Nguyen, Hung H; Oguchi, Hiroyuki; Van Minh, Le; Kuwano, Hiroki

    2017-06-12

    We conducted a high-throughput investigation of the fundamental properties of (Mg,Hf) x Al 1-x N thin films (0 piezoelectric materials. For the high-throughput investigation, we prepared composition-gradient (Mg,Hf) x Al 1-x N films grown on a Si(100) substrate at 600 °C by cosputtering AlN and MgHf targets. To measure the properties of the various compositions at different positions within a single sample, we used characterization techniques with spatial resolution. X-ray diffraction (XRD) with a beam spot diameter of 1.0 mm verified that Mg and Hf had substituted into the Al sites and caused an elongation of the c-axis of AlN from 5.00 Å for x = 0 to 5.11 Å for x = 0.24. In addition, the uniaxial crystal orientation and high crystallinity required for piezoelectric materials to be used as application devices were confirmed. The piezoelectric response microscope indicated that this c-axis elongation increased the piezoelectric coefficient almost linearly from 1.48 pm/V for x = 0 to 5.19 pm/V for x = 0.24. The dielectric constants of (Mg,Hf) x Al 1-x N were investigated using parallel plate capacitor structures with ∼0.07 mm 2 electrodes and showed a slight increase by substitution. These results verified that (Mg,Hf) x Al 1-x N is a promising material for piezoelectric-based application devices, especially for vibrational energy harvesters.

  16. Piezoelectric properties and diffusion phase transition around PPT of La-doped (Na{sub 0.52}K{sub 0.44}Li{sub 0.04}) Nb{sub 0.8}Ta{sub 0.2}O{sub 3} lead-free piezoelectric ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Wenlong, E-mail: yangwenlong1983@163.com; Wang, Li; Li, Haidong; Han, Junsheng; Xiu, Hanjiang; Zhou, Zhongxiang

    2016-10-01

    Lead-free ceramics (Na{sub 0.52}K{sub 0.44}Li{sub 0.04}){sub 1−3x}La{sub x}Nb{sub 0.8}Ta{sub 0.2}O{sub 3} (KNLNT-Lax, x=0.00, 0.25, 0.5, 0.75, 1.00, 1.25 mol%) as non-polluting materials were prepared by solid state reaction method. The structure, piezoelectric proprieties and temperature stability of KNLNT ceramic with different La doping concentrations were investigated. The results show a transition from orthorhombic-tetragonal mix phase to tetragonal single phase with the variation of La{sup 3+} concentrations. The SEM micrographs of surface and fractured surface show a dense microstructure with few micropores. The La-doped KNLTN ceramic will be an alternative candidate contributes to excellent piezoelectric properties, which are found in the 0.75 mol% La-doped KNLNT ceramics, with d{sub 33}=215pC/N, k{sub p}=42.8%and Q{sub m}=89. It has been remarkably improved that the temperature stability of KNLTN-Lax piezoelectric properties at room temperature, and the dielectric relaxation can be observed obviously. The mechanism of La doping was analyzed in terms of valence compensation and polymorphic phase transition (PPT) diffusion. The orthorhombic-tetragonal phase transition around room temperature and the relaxation transition were considered contributing to the excellent piezoelectric performance and improved temperature stability of La{sup 3+}-doped KNLTN.

  17. A process chain for integrating piezoelectric transducers into aluminum die castings to generate smart lightweight structures

    Directory of Open Access Journals (Sweden)

    Stefan Stein

    al., [7]. The modules are made of low temperature cofired ceramic (LTCC tapes with an embedded lead zirconate titanate (PZT plate and are manufactured in multilayer technique. For joining conducting copper (Cu wires with the electrode structure of the LPM, a novel laser drop on demand wire bonding method (LDB is applied, which is based on the melting of a spherical CuSn12 braze preform with a liquidus temperature Tliquid of 989.9 °C (Deutsches Kupfer-Institut Düsseldorf, [8] providing sufficient thermal stability for a subsequent casting process. Keywords: Active noise reduction, Laser assisted wire bonding, Smart structures, Piezoelectric transducers, Die casting, Lightweight design

  18. Dielectric, Piezoelectric, and Vibration Properties of the LiF-Doped (Ba0.95Ca0.05(Ti0.93Sn0.07O3 Lead-Free Piezoceramic Sheets

    Directory of Open Access Journals (Sweden)

    Chien-Min Cheng

    2018-01-01

    Full Text Available By the conventional solid state reaction method, a small amount of lithium fluoride (LiF was used as the sintering promoter to improve the sintering and piezoelectric characteristics of (Ba0.95Ca0.05(Ti0.93Sn0.07O3 (BCTS lead-free piezoceramic sheets. Using X-ray diffraction (XRD and a scanning electron microscope (SEM, the inferences of the crystalline and surface microstructures were obtained and analyzed. Then, the impedance analyzer and d33-meter were used to measure the dielectric and piezoelectric characteristics. In this study, the optimum sintering temperature of the BCTS sheets decreased from 1450 °C to 1390 °C due to LiF doping. For the 0.07 wt % LiF-doped BCTS sheets sintered at 1390 °C, the piezoelectric constant (d33 is 413 pC/N, the electric–mechanical coupling coefficient (kp is 47.5%, the dielectric loss (tan δ is 3.9%, and the dielectric constant (εr is 8100, which are all close to or even better than that of the pure undoped BCTS ceramics. The Curie temperature also improved, from 85 °C for pure BCTS to 140 °C for BCTS–0.07 LiF sheets. Furthermore, by using the vibration system and fixing 1.5 g tip mass at the end of the sheets, as the vibration frequency is 20 Hz, the proposed piezoelectric ceramic sheets also reveal a good energy harvesting performance at the maximum output peak voltage of 4.6 V, which is large enough and can be applied in modern low-power electronic products.

  19. Three-degree-of-freedom ultrasonic motor using a 5-mm-diameter piezoelectric ceramic tube.

    Science.gov (United States)

    Mingsen Guo; Junhui Hu; Hua Zhu; Chunsheng Zhao; Shuxiang Dong

    2013-07-01

    A small three-degree-of-freedom ultrasonic motor has been developed using a simple piezoelectric lead zirconate titanate (PZT)-tube stator (OD 5 mm, ID 3 mm, length 15 mm). The stator drives a ball-rotor into rotational motion around one of three orthogonal (x-, y-, and z-) axes by combing the first longitudinal and second bending vibration modes. A motor prototype was fabricated and characterized; its performance was superior to those of previous motors made with a PZT ceramic/metal composite stator of comparable size. The method for further improving the performance was discussed. The motor can be further miniaturized and it has potential to be applied to medical microrobots, endoscopes or micro laparoscopic devices, and cell manipulation devices.

  20. Ferroelectric and dielectric properties of Sr2-x(Na, K)xBi4Ti5O18 lead-free piezoelectric ceramics

    International Nuclear Information System (INIS)

    Chen Qian; Xu Zhijun; Chu Ruiqing; Hao Jigong; Zhang Yanjie; Li Guorong; Yin Qingrui

    2010-01-01

    (Na, K)-doped Sr 2 Bi 4 Ti 5 O 18 (SBTi) bismuth layer structure ferroelectric ceramics were prepared by the solid-state reaction method. Pure bismuth-layered structural Sr 2-x (Na, K) x Bi 4 Ti 5 O 18 (x=0.1, 0.2, 0.3, and 0.4) ceramics with uniform grain size were obtained in this work. The effects of (Na, K)-doping on the dielectric, ferroelectric and piezoelectric properties of SBTi ceramics were investigated. Results showed that (Na, K)-doping caused the Curie temperature of SBTi ceramics to shift to higher temperature and enhanced the ferroelectric and piezoelectric properties. At x=0.2, the ceramics exhibited optimum properties with d 33 =20 pC/N, P r =10.3 μC/cm 2 , and T c =324 o C.

  1. Piezoelectric Motors, an Overview

    OpenAIRE

    Karl Spanner; Burhanettin Koc

    2016-01-01

    Piezoelectric motors are used in many industrial and commercial applications. Various piezoelectric motors are available in the market. All of the piezoelectric motors use the inverse piezoelectric effect, where microscopically small oscillatory motions are converted into continuous or stepping rotary or linear motions. Methods of obtaining long moving distance have various drive and functional principles that make these motors categorized into three groups: resonance-drive (piezoelectric ult...

  2. Industrial approach to piezoelectric damping of large fighter aircraft components

    Science.gov (United States)

    Simpson, John; Schweiger, Johannes

    1998-06-01

    Different concepts to damp structural vibrations of the vertical tail of fighter aircraft are reported. The various requirements for a vertical tail bias an integrated approach for the design. Several active vibrations suppression concepts had been investigated during the preparatory phase of a research program shared by Daimler-Benz Aerospace Military Aircraft (Dasa), Daimler-Benz Forschung (DBF) and Deutsche Forschungsandstalt fuer Luftund Raumfahrt (DLR). Now in the main phase of the programme, four concepts were finally chosen: two concepts with aerodynamic control surfaces and two concepts with piezoelectric components. One piezo concept approach will be described rigorously, the other concepts are briefly addressed. In the Dasa concept, thin surface piezo actuators are set out carefully to flatten the dynamic portion of the combined static and dynamic maximum bending moment loading case directly in the shell structure. The second piezo concept by DLR involves pre-loaded lead zirconate titanate (PZT)-block actuators at host structure fixtures. To this end a research apparatus was designed and built as a full scale simplified fin box with carbon fiber reinformed plastic skins and an aluminium stringer-rib substructure restrained by relevant aircraft fixtures. It constitutes a benchmark 3D-structural impedance. The engineering design incorporates 7kg of PZT surface actuators. The structural system then should be excited to more than 15mm tip displacement amplitude. This prepares the final step to total A/C integration. Typical analysis methods using cyclic thermal analogies adapted to induced load levels are compared. Commercial approaches leading onto basic state space model interpretation wrt. actuator sizing and positioning, structural integrity constraints, FE-validation and testing are described. Both piezoelectric strategies are aimed at straight open-loop performance related to concept weight penalty and input electric power. The required actuators, power

  3. FABRICATION AND MECHANICAL PROPERTIES OF Na0.5Bi0.5TiO3–BaTiO3 LEAD-FREE PIEZOELECTRIC CERAMICS

    Directory of Open Access Journals (Sweden)

    PAN YUSONG

    2014-03-01

    Full Text Available Piezoelectric ceramics with 0.94Na0.5Bi0.5TO3–0.06BaTiO3 compositions were fabricated by solid state mixed oxide method and sintered at different temperatures varying from 1050°C to 1150°C to obtain dense ceramics. Phase analysis using X-ray diffraction showed tetragonal perovskite structure of Na0.5Bi0.5TO3 with no BaTiO3 peak detected. The SEM observation revealed that the crystal grain size of the piezoelectric ceramics is on the nano-size dimensions under all the sintering temperature. The study on the compressive mechanical characteristics showed that the compressive strength of the 0.94Na0.5Bi0.5TO3–0.06BaTiO3 piezoelectric ceramics increases with the rise of sintering temperature and sintering time. The change behavior of the compressive strength with the rise of cold pressure presents increasing firstly and then decreases.

  4. Preparation and electrical properties of Bi0.5Na0.5TiO3-BaTiO3-KNbO3 lead-free piezoelectric ceramics

    International Nuclear Information System (INIS)

    Ni Haimin; Luo Laihui; Li Weiping; Zhu Yuejin; Luo Haosu

    2011-01-01

    Research highlights: → Bi 0.47 Na 0.47 Ba 0.06 TiO 3 -KNbO 3 ceramics exhibit excellent piezoelectric properties. → The optimized properties of the ceramics: d 33 = 195 pC/N; k t = 58.9; Q m = 113; E c = 19.5 kV/cm. → KNbO 3 has diffused into the Bi 0.47 Na 0.47 Ba 0.06 TiO 3 lattices to form a new solid solution. → Macro-micro domain switching occurs at depolarization temperature T d . - Abstract: Lead-free (1 - x)Bi 0.47 Na 0.47 Ba 0.06 TiO 3 -xKNbO 3 (BNBT-xKN, x = 0-0.08) ceramics were prepared by ordinary ceramic sintering technique. The piezoelectric, dielectric and ferroelectric properties of the ceramics are investigated and discussed. The results of X-ray diffraction (XRD) indicate that KNbO 3 (KN) has diffused into Bi 0.47 Na 0.47 Ba 0.06 TiO 3 (BNBT) lattices to form a solid solution with a pure perovskite structure. Moderate additive of KN (x ≤ 0.02) in BNBT-xKN ceramics enhance their piezoelectric and ferroelectric properties. Three dielectric anomaly peaks are observed in BNBT-0.00KN, BNBT-0.01KN and BNBT-0.02KN ceramics. With the increment of KN in BNBT-xKN ceramics, the dielectric anomaly peaks shift to lower temperature. BNBT-0.01KN ceramic exhibits excellent piezoelectric properties and strong ferroelectricity: piezoelectric coefficient, d 33 = 195 pC/N; electromechanical coupling factor, k t = 58.9 and k p = 29.3%; mechanical quality factor, Q m = 113; remnant polarization, P r = 41.8 μC/cm 2 ; coercive field, E c = 19.5 kV/cm.

  5. Point defects in crystalline zircon (zirconium silicate), ZrSiO4: electron paramagnetic resonance studies

    Science.gov (United States)

    Tennant, W. C.; Claridge, R. F. C.; Walsby, C. J.; Lees, N. S.

    This article outlines the present state of knowledge of paramagnetic defects in crystalline zircon as obtained mainly, but not exclusively, from electron paramagnetic resonance (EPR) studies in crystalline zircon (zirconium silicate, ZrSiO4). The emphasis is on single-crystal studies where, in principle, unambiguous analysis is possible. Firstly, the crystallography of zircon is presented. Secondly, the relationships between available crystal-site symmetries and the symmetries of observed paramagnetic species in zircon, and how these observations lead to unambiguous assignments of point-group symmetries for particular paramagnetic species are detailed. Next, spin-Hamiltonian (SH) analysis is discussed with emphasis on the symmetry relationships that necessarily exist amongst the Laue classes of the crystal sites in zircon, the paramagnetic species occupying those sites and the SH itself. The final sections of the article then survey the results of EPR studies on zircon over the period 1960-2002.

  6. A brief review of Ba(Ti0.8Zr0.2)O3-(Ba0.7Ca0.3)TiO3 based lead-free piezoelectric ceramics: Past, present and future perspectives

    Science.gov (United States)

    Zhang, Yong; Sun, Huajun; Chen, Wen

    2018-03-01

    As one kind of most crucial and emerging lead-free piezoelectric systems, Ba(Ti0.8Zr0.2)O3-(Ba0.7Ca0.3)TiO3 (BCZT) based lead-free piezoceramics have attracted worldwide attention in recent years. Much progress has been made, however, a summary which covers both the recent progress and the remained problems is urgently needed to further push this field forward. In this review, a brief background of the development of BCZT based lead-free piezoceramics was illustrated firstly. Then, the internal mechanism for the high piezoelectric response would be elaborated. Current research status was discussed in detail in the third section. Various strategies including: (1) Using distinct synthesis routes, (2) adopting different sintering techniques, (3) doping with foreign ions and/or second components, (4) grain size control, were exploited to improve the comprehensive performance and in turn broaden their application areas. In this part, some recently representative works were touched in detail and several existing problems were pointed out. Last, some critical comments (some thoughts related to the potential and future development of BCZT system) were given based on the current research status and existing problems. All in all, this review is devoted to summarizing the milestones in the past, classifying selected recent works and analyzing the prospects of BCZT based ceramics. It can be expected that, this first review that concentrates on BCZT based ceramics obviously would provide useful guidance for the research community.

  7. Ferroelectric and piezoelectric properties of lead-free BaTiO{sub 3} doped Bi{sub 0.5}Na{sub 0.5}TiO{sub 3} thin films from metal-organic solution deposition

    Energy Technology Data Exchange (ETDEWEB)

    Acharya, Susant Kumar [Division of Advanced Materials Engineering, Hydrogen and Fuel Cell Research Center, Chonbuk National University, Jeonju 561-756 (Korea, Republic of); Department of Semiconductor Science and Technology, Basic Research Laboratory (BRL), Semiconductor Physics Research Center (SPRC), Chonbuk National University, Jeonju 561-756 (Korea, Republic of); Lee, Sang-Kwon; Hyung, Jung-Hwan [Department of Semiconductor Science and Technology, Basic Research Laboratory (BRL), Semiconductor Physics Research Center (SPRC), Chonbuk National University, Jeonju 561-756 (Korea, Republic of); Yang, Yun-Ho; Kim, Bok-Hee [Division of Advanced Materials Engineering, Hydrogen and Fuel Cell Research Center, Chonbuk National University, Jeonju 561-756 (Korea, Republic of); Ahn, Byung-Guk, E-mail: bkahn@jbnu.ac.kr [Division of Advanced Materials Engineering, Hydrogen and Fuel Cell Research Center, Chonbuk National University, Jeonju 561-756 (Korea, Republic of)

    2012-11-05

    Highlights: Black-Right-Pointing-Pointer Lead-free BNT-BT thin films from an optimized metal-organic solution deposition. Black-Right-Pointing-Pointer Phase and microstructure evolution with annealing temperature. Black-Right-Pointing-Pointer A relatively low leakage current density. Black-Right-Pointing-Pointer Good dielectric constant of 613 at a frequency of 1 kHz. Black-Right-Pointing-Pointer High remanent polarization and piezoelectric constant comparable to PZT thin films. - Abstract: Lead-free 0.94Bi{sub 0.5}Na{sub 0.5}TiO{sub 3}-0.06BaTiO{sub 3} (BNT-BT) piezoelectric thin films were prepared by metal-organic solution deposition onto a Pt/Ti/SiO{sub 2}/Si substrate. A dense and well crystallized thin film with a perovskite phase was obtained by annealing these films at 700 Degree-Sign C. Atomic force microscopy showed that these films were smooth and crack-free with an average grain size on the order of 200 nm. Thin films of 356 nm thickness exhibited a small signal dielectric constant and a loss tangent at 1 kHz of 613 and 0.044, respectively. Ferroelectric hysteresis measurements indicated a remanent polarization value of 21.5 {mu}C/cm{sup 2} with a coercive field of 164.5 kV/cm. The leakage current density of the thin film was 4.08 Multiplication-Sign 10{sup -4} A/cm{sup 2} at an applied electric field of 200 kV/cm. A typical butterfly-shaped piezoresponse loop was observed and the effective piezoelectric coefficient (d{sub 33}) of the BNT-BT thin film was approximately 51.6 pm/V.

  8. Polymorphic phase transition dependence of piezoelectric properties in (K0.5Na0.5)NbO3-(Bi0.5K0.5)TiO3 lead-free ceramics

    International Nuclear Information System (INIS)

    Du Hongliang; Zhou Wancheng; Luo Fa; Zhu Dongmei; Qu Shaobo; Li Ye; Pei Zhibin

    2008-01-01

    Lead-free ceramics (1 - x)(K 0.5 Na 0.5 )NbO 3 -x(Bi 0.5 K 0.5 )TiO 3 [(1 - x)KNN-xBKT] were synthesized by conventional solid-state sintering. The phase structure, microstructure and electrical properties of (1 - x)KNN-xBKT ceramics were investigated. At room temperature, the polymorphic phase transition (from the orthorhombic to the tetragonal phase) (PPT) was identified at x = 0.02 by the analysis of x-ray diffraction patterns and dielectric spectroscopy. Enhanced electrical properties (d 33 = 251 pC N -1 , k p = 0.49, k t = 0.50, ε 33 T / ε 0 =1260, tan δ = 0.03 and T C = 376 deg. C) were obtained in the ceramics with x = 0.02 owing to the formation of the PPT at 70 deg. C and the selection of an optimum poling temperature. The related mechanisms for high piezoelectric properties in (1 - x)KNN-xBKT (x = 0.02) ceramics were discussed. In addition, the results confirmed that the selection of the optimum poling temperature was an effective way to further improve the piezoelectric properties of KNN-based ceramics. The enhanced properties were comparable to those of hard Pb(Zr, Ti)O 3 ceramics and indicated that the (1 - x)KNN-xBKT (x = 0.02) ceramic was a promising lead-free piezoelectric candidate material for actuator and transducer applications

  9. Experimental investigation into the effect of substrate clamping on the piezoelectric behaviour of thick-film PZT elements

    Energy Technology Data Exchange (ETDEWEB)

    Torah, R N; Beeby, S P; White, N M [Department of Electronics and Computer Science, University of Southampton, SO17 1BJ (United Kingdom)

    2004-04-07

    This paper details an experimental investigation of the clamping effect associated with thick-film piezoelectric elements printed on a substrate. The clamping effect reduces the measured piezoelectric coefficient, d{sub 33}, of the film. This reduction is due to the influence of the d{sub 31} component in the film when a deformation of the structure occurs, by either the direct or indirect piezoelectric effect. Theoretical analysis shows a reduction in the measured d{sub 33} of 62%, i.e. a standard bulk lead zirconate titanate (PZT)-5H sample with a manufacturer specified d{sub 33} of 593pC/N would fall to 227.8pC/N. To confirm this effect, the d{sub 33} coefficients of five thin bulk PZT-5H samples of 220 {mu}m thickness were measured before and after their attachment to a metallized 96% alumina substrate. The experimental results show a reduction in d{sub 33} of 74% from 529pC/N to 139pC/N. The theoretical analysis was then applied to existing University of Southampton thick-film devices. It is estimated that the measured d{sub 33} value of 131pC/N of the thick-film devices is the equivalent of an unconstrained d{sub 33} of 345pC/N.

  10. Electrode-shaping for the excitation and detection of permitted arbitrary modes in arbitrary geometries in piezoelectric resonators.

    Science.gov (United States)

    Pulskamp, Jeffrey S; Bedair, Sarah S; Polcawich, Ronald G; Smith, Gabriel L; Martin, Joel; Power, Brian; Bhave, Sunil A

    2012-05-01

    This paper reports theoretical analysis and experimental results on a numerical electrode shaping design technique that permits the excitation of arbitrary modes in arbitrary geometries for piezoelectric resonators, for those modes permitted to exist by the nonzero piezoelectric coefficients and electrode configuration. The technique directly determines optimal electrode shapes by assessing the local suitability of excitation and detection electrode placement on two-port resonators without the need for iterative numerical techniques. The technique is demonstrated in 61 different electrode designs in lead zirconate titanate (PZT) thin film on silicon RF micro electro-mechanical system (MEMS) plate, beam, ring, and disc resonators for out-of-plane flexural and various contour modes up to 200 MHz. The average squared effective electromechanical coupling factor for the designs was 0.54%, approximately equivalent to the theoretical maximum value of 0.53% for a fully electroded length-extensional mode beam resonator comprised of the same composite. The average improvement in S(21) for the electrode-shaped designs was 14.6 dB with a maximum improvement of 44.3 dB. Through this piezoelectric electrodeshaping technique, 95% of the designs showed a reduction in insertion loss.

  11. Orthotropic Piezoelectricity in 2D Nanocellulose.

    Science.gov (United States)

    García, Y; Ruiz-Blanco, Yasser B; Marrero-Ponce, Yovani; Sotomayor-Torres, C M

    2016-10-06

    The control of electromechanical responses within bonding regions is essential to face frontier challenges in nanotechnologies, such as molecular electronics and biotechnology. Here, we present Iβ-nanocellulose as a potentially new orthotropic 2D piezoelectric crystal. The predicted in-layer piezoelectricity is originated on a sui-generis hydrogen bonds pattern. Upon this fact and by using a combination of ab-initio and ad-hoc models, we introduce a description of electrical profiles along chemical bonds. Such developments lead to obtain a rationale for modelling the extended piezoelectric effect originated within bond scales. The order of magnitude estimated for the 2D Iβ-nanocellulose piezoelectric response, ~pm V -1 , ranks this material at the level of currently used piezoelectric energy generators and new artificial 2D designs. Such finding would be crucial for developing alternative materials to drive emerging nanotechnologies.

  12. Orthotropic Piezoelectricity in 2D Nanocellulose

    Science.gov (United States)

    García, Y.; Ruiz-Blanco, Yasser B.; Marrero-Ponce, Yovani; Sotomayor-Torres, C. M.

    2016-10-01

    The control of electromechanical responses within bonding regions is essential to face frontier challenges in nanotechnologies, such as molecular electronics and biotechnology. Here, we present Iβ-nanocellulose as a potentially new orthotropic 2D piezoelectric crystal. The predicted in-layer piezoelectricity is originated on a sui-generis hydrogen bonds pattern. Upon this fact and by using a combination of ab-initio and ad-hoc models, we introduce a description of electrical profiles along chemical bonds. Such developments lead to obtain a rationale for modelling the extended piezoelectric effect originated within bond scales. The order of magnitude estimated for the 2D Iβ-nanocellulose piezoelectric response, ~pm V-1, ranks this material at the level of currently used piezoelectric energy generators and new artificial 2D designs. Such finding would be crucial for developing alternative materials to drive emerging nanotechnologies.

  13. Phase segregation and dielectric, ferroelectric, and piezoelectric properties of MgO-doped NBT-BT lead-free ferroelecric ceramics

    Science.gov (United States)

    Liu, Gang; Wang, Ziyang; Zhang, Leiyang; Shi, Wenjing; Jing, Jiayi; Chen, Yi; Liu, Hongbo; Yan, Yan

    2018-03-01

    MgO doped NBT-BT ceramics were prepared by the conventional electroceramic processing. The effects of MgO on the phase, microstructures and electrical properties of NBT-BT ceramics were systematically investigated. When doping content is more than 1%, a second phase appeared, which has great effect on dielectric, ferroelectric, and piezoelectric properties, such as the T F-R peak weakened, moved to the higher temperature, and eventually disappeared. When the doping content is above 1.5%, the ceramic samples show a strong relaxation. The detailed analysis and discussion can be found within this study.

  14. A process chain for integrating piezoelectric transducers into aluminum die castings to generate smart lightweight structures

    Science.gov (United States)

    Stein, Stefan; Wedler, Jonathan; Rhein, Sebastian; Schmidt, Michael; Körner, Carolin; Michaelis, Alexander; Gebhardt, Sylvia

    modules are made of low temperature cofired ceramic (LTCC) tapes with an embedded lead zirconate titanate (PZT) plate and are manufactured in multilayer technique. For joining conducting copper (Cu) wires with the electrode structure of the LPM, a novel laser drop on demand wire bonding method (LDB) is applied, which is based on the melting of a spherical CuSn12 braze preform with a liquidus temperature Tliquid of 989.9 °C (Deutsches Kupfer-Institut Düsseldorf, [8]) providing sufficient thermal stability for a subsequent casting process.

  15. An improved resonantly driven piezoelectric gas pump

    International Nuclear Information System (INIS)

    Wu, Yue; Liu, Yong; Liu, Jianfang; Jiao, Xiaoyang; Yang, Zhigang; Wang, Long

    2013-01-01

    Piezoelectric pumps have the potential to be used in a variety of applications, such as in air circulation and compression. However, piezoelectric membrane pumps do not have enough driving capacity, and the heat induced during the direct contact between the driving part and the gas medium cannot be dissipated smoothly. When the gas is blocked, the piezoelectric vibrator generates heat quickly, which may eventually lead to damage. Resonantly driven piezoelectric stack pumps have high performance but no price advantage. In this situation, a novel, resonantly driven piezoelectric gas pump with annular bimorph as the driver is presented. In the study, the working principle of the novel pump was analyzed, the vibration mechanics model was determined, and the displacement amplified theory was studied. The outcome indicates that the displacement amplification factor is related with the original displacement provided by the piezoelectric bimorph. In addition, the displacement amplification effect is related to the stiffness of the spring lamination, adjustment spring, and piezoelectric vibrator, as well as to the systematic damping factor and the driving frequency. The experimental prototypes of the proposed pump were designed, and the displacement amplification effect and gas output performance were measured. At 70 V of sinusoidal AC driving voltage, the improved pump amplified the piezoelectric vibrator displacement by 4.2 times, the maximum gas output flow rate reached 1685 ml/min, and the temperature of the bimorph remained normal after 2000 hours of operation when the gas medium was blocked.

  16. Preparation and electrical properties of MoO{sub 3}-modified SrBi{sub 2}Nb{sub 2}O{sub 9}-based lead-free piezoelectric ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Yao, Zhongran, E-mail: ruiqingchu@sohu.com [College of Materials Science and Engineering, Liaocheng University, Liaocheng 252059 (China); Chu, Ruiqing, E-mail: rqchu@lcu.edu.cn [College of Materials Science and Engineering, Liaocheng University, Liaocheng 252059 (China); Xu, Zhijun; Hao, Jigong; Wei, Denghu; Cheng, Renfei [College of Materials Science and Engineering, Liaocheng University, Liaocheng 252059 (China); Li, Guorong [The State Key Lab of High Performance Ceramics and Superfinemicrostructure, Shanghai Institute of Ceramics, Chinese Academy of Science, Shanghai 200050 (China)

    2016-05-05

    Lead-free piezoelectric ceramics, SrBi{sub 2}(Nb{sub 1-x}Mo{sub x}){sub 2}O{sub 9} (SBNM-x), were prepared by a conventional solid-state reaction method. The crystal structure, microstructure and electrical properties were systematically investigated. The X-ray diffraction analysis suggested that the substitution formed layered perovskite structure. Plate-like morphology of the grains which is characteristic for layer-structure Aurivillius compounds was clearly observed for all the samples. The excellent electrical properties (e.g., d{sub 33}∼18 pC/N, 2P{sub r}∼20.34 μC/cm{sup 2}) and a high Curie temperature (e.g., T{sub c}∼458 °C) are simultaneously obtained in the ceramics with x = 0.12. Additionally, thermal annealing studies indicated that piezoelectric constant (d{sub 33}) of SBNM-0.12 ceramic remains almost unchanged (16 pC/N, only decrease by 12%) at temperatures below 400 °C, demonstrating that the Mo-modified SBN-based ceramics are the promising candidates for high-temperature applications. - Highlights: • Higher valent cation Mo{sup 6+} substituted for B-site Nb{sup 5+} in the perovskite layers ions. • The piezoelectric constant (d{sub 33}) of SrBi{sub 2}Nb{sub 2}O{sub 9} ceramic is increased to be 18 pC/N. • The remnant polarization (2P{sub r}) of SrBi{sub 2}Nb{sub 2}O{sub 9} ceramic is increased to be 20.34 μC cm{sup −2}. • SBNM-x ceramics show good temperature stability for high temperature applications.

  17. Design, fabrication, and properties of 2-2 connectivity cement/polymer based piezoelectric composites with varied piezoelectric phase distribution

    International Nuclear Information System (INIS)

    Dongyu, Xu; Xin, Cheng; Shifeng, Huang; Banerjee, Sourav

    2014-01-01

    The laminated 2-2 connectivity cement/polymer based piezoelectric composites with varied piezoelectric phase distribution were fabricated by employing Lead Zirconium Titanate ceramic as active phase, and mixture of cement powder, epoxy resin, and hardener as matrix phase with a mass proportion of 4:4:1. The dielectric, piezoelectric, and electromechanical coupling properties of the composites were studied. The composites with large total volume fraction of piezoelectric phase have large piezoelectric strain constant and relative permittivity, and the piezoelectric and dielectric properties of the composites are independent of the dimensional variations of the piezoelectric ceramic layer. The composites with small total volume fraction of piezoelectric phase have large piezoelectric voltage constant, but also large dielectric loss. The composite with gradually increased dimension of piezoelectric ceramic layer has the smallest dielectric loss, and that with the gradually increased dimension of matrix layer has the largest piezoelectric voltage constant. The novel piezoelectric composites show potential applications in fabricating ultrasonic transducers with varied surface vibration amplitude of the transducer

  18. A review on one dimensional perovskite nanocrystals for piezoelectric applications

    Directory of Open Access Journals (Sweden)

    Li-Qian Cheng

    2016-03-01

    Full Text Available In recent years, one-dimensional piezoelectric nanomaterials have become a research topic of interest because of their special morphology and excellent piezoelectric properties. This article presents a short review on one dimensional perovskite piezoelectric materials in different systems including Pb(Zr,TiO3, BaTiO3 and (K,NaNbO3 (KNN. We emphasize KNN as a promising lead-free piezoelectric compound with a high Curie temperature and high piezoelectric properties and describe its synthesis and characterization. In particular, details are presented for nanoscale piezoelectricity characterization of a single KNN nanocrystal by piezoresponse force microscopy. Finally, this review describes recent progress in applications based on one dimensional piezoelectric nanostructures with a focus on energy harvesting composite materials.

  19. Ferroelectric and impedance response of lead-free (B/sub o.5/N/sub 0.5/)TiO/sub 3/-BaZrO/sub 3/ piezoelectric ceramics

    International Nuclear Information System (INIS)

    Rehman, J. U.; Hussain, A.; Maqbool, A.; Kim, J. S.; Song, T. K.; Lee, J. H.; Kim, W. J.; Kim, M. H.

    2013-01-01

    Lead-free piezoelectric (0.96B/sub 0.5/N/sub 0.5/TiO/sub 3/)-0.04BaZrO/sub 3/ (BNT-BZ4) was synthesized by using a solid-state reaction method. SEM micrograph shows dense microstructure. X-ray diffraction (XRD) indicated the formation of a BNB-BZ4 single phase having pseudocubic symmetry. A maximum value of remnant polarization (30 meuC/cm2) and piezoelectric constant (112 pC/N) was observed for BNT-BZ4 ceramic. The temperature dependences of the dielectric properties of BNT-BZ4 were investigated in the temperature range of 25-600 degree C at various frequencies (0.1 Hz-1 MHz). The maximum dielectric constant value (epsilonr) reaches a highest value of 4046 (at 10 kHz). The electrical properties were investigated by using complex impedance spectroscopy and provided better understanding of relaxation process. (author)

  20. Structure and electrical properties of (1 − x) (Na0.5Bi0.5)0.94Ba0.06TiO3–x BiAlO3 lead-free piezoelectric ceramics

    International Nuclear Information System (INIS)

    Fu, Peng; Xu, Zhijun; Chu, Ruiqing; Wu, Xueyan; Li, Wei; Li, Xiaodong

    2013-01-01

    Highlights: ► (1 − x) BNBT6–x BA ceramics were prepared by solid-state reaction method. ► Electrical properties of BNBT6 ceramics are improved by the addition of BA. ► (1 − x) BNBT6 - x BA ceramics at x = 0.0225 have the best electrical properties. - Abstract: (1 − x) (Na 0.5 Bi 0.5 ) 0.94 Ba 0.06 TiO 3 –x BiAlO 3 ((1 − x) BNBT6–x BA) lead-free piezoelectric ceramics were synthesized by conventional solid-state processes. Effects of BiAlO 3 (BA) on the structure and electrical properties of (Na 0.5 Bi 0.5 ) 0.94 Ba 0.06 TiO 3 (BNBT6) ceramics were investigated. X-ray diffraction (XRD) data shows that (1 − x) BNBT6–x BA ceramics form the pure perovskite phases, and the ceramics have the morphotropic phase boundary (MPB) when x r = 42.5 μC/cm 2 ), the highest piezoelectric coefficient (d 33 = 204 pC/N), the highest planar coupling factor (k p = 0.3292), the highest dielectric constant (ε r = 1687) and higher mechanical quality factor (Q m = 112)

  1. Piezoelectric drive circuit

    Science.gov (United States)

    Treu, C.A. Jr.

    1999-08-31

    A piezoelectric motor drive circuit is provided which utilizes the piezoelectric elements as oscillators and a Meacham half-bridge approach to develop feedback from the motor ground circuit to produce a signal to drive amplifiers to power the motor. The circuit automatically compensates for shifts in harmonic frequency of the piezoelectric elements due to pressure and temperature changes. 7 figs.

  2. Multifunctional Electroactive Nanocomposites Based on Piezoelectric Boron Nitride Nanotubes

    Science.gov (United States)

    Kang, Jin Ho; Sauti, Godfrey; Park, Cheol; Yamakov, Vesselin I.; Wise, Kristopher E.; Lowther, Sharon E.; Fay, Catharine C.; Thibeault, Sheila A.; Bryant, Robert G.

    2015-01-01

    Space exploration missions require sensors and devices capable of stable operation in harsh environments such as those that include high thermal fluctuation, atomic oxygen, and high-energy ionizing radiation. However, conventional or state-of-the-art electroactive materials like lead zirconate titanate, poly(vinylidene fluoride), and carbon nanotube (CNT)-doped polyimides have limitations on use in those extreme applications. Theoretical studies have shown that boron nitride nanotubes (BNNTs) have strength-to-weight ratios comparable to those of CNTs, excellent high-temperature stability (to 800 C in air), large electroactive characteristics, and excellent neutron radiation shielding capability. In this study, we demonstrated the experimental electroactive characteristics of BNNTs in novel multifunctional electroactive nanocomposites. Upon application of an external electric field, the 2 wt % BNNT/polyimide composite was found to exhibit electroactive strain composed of a superposition of linear piezoelectric and nonlinear electrostrictive components. When the BNNTs were aligned by stretching the 2 wt % BNNT/polyimide composite, electroactive characteristics increased by about 460% compared to the nonstretched sample. An all-nanotube actuator consisting of a BNNT buckypaper layer between two single-walled carbon nanotube buck-paper electrode layers was found to have much larger electroactive properties. The additional neutron radiation shielding properties and ultraviolet/visible/near-infrared optical properties of the BNNT composites make them excellent candidates for use in the extreme environments of space missions. utilizing the unique characteristics of BNNTs.

  3. Piezoelectric Driving of Vibration Conveyors: An Experimental Assessment

    Directory of Open Access Journals (Sweden)

    Emerson Bastos de Albuquerque

    2013-07-01

    Full Text Available Vibratory feeders or vibratory conveyors have been widely used for the transport and orientation of individual parts and bulk materials in many branches of industrial activity. From the designer’s standpoint, the current endeavor is to conceive efficient vibratory feeders, satisfying constraints of power consumption, vibration transmission and noise emission. Moreover, the interest in the reduction of maintenance cost is always present. In this context, this paper investigates experimentally the concept of vibratory conveying based on the use of piezoelectric materials for motion generation. A small-size prototype of a linear conveyor, in which lead-zirconate-titanate (PZT patches are bonded to the resilient elements, is described. One of the main design goals is that the prototype is intended to be fed directly from the electric network, aiming at avoiding the use of electronic equipment for driving. To comply with this feature and, at the same time, enable to adjust the transport velocity, a mechanical device has been conceived in such a way that the first natural frequency of the conveyor can be changed. It is shown that the transport velocity is determined by the proximity between the excitation frequency and the first natural frequency of the conveyor. The experimental tests performed to characterize the dynamic behavior of the prototype are described and the range of transport velocities is determined.

  4. Piezoelectric Driving of Vibration Conveyors: An Experimental Assessment

    Science.gov (United States)

    Rade, Domingos Alves; de Albuquerque, Emerson Bastos; Figueira, Leandro Chaves; Carvalho, João Carlos Mendes

    2013-01-01

    Vibratory feeders or vibratory conveyors have been widely used for the transport and orientation of individual parts and bulk materials in many branches of industrial activity. From the designer's standpoint, the current endeavor is to conceive efficient vibratory feeders, satisfying constraints of power consumption, vibration transmission and noise emission. Moreover, the interest in the reduction of maintenance cost is always present. In this context, this paper investigates experimentally the concept of vibratory conveying based on the use of piezoelectric materials for motion generation. A small-size prototype of a linear conveyor, in which lead-zirconate-titanate (PZT) patches are bonded to the resilient elements, is described. One of the main design goals is that the prototype is intended to be fed directly from the electric network, aiming at avoiding the use of electronic equipment for driving. To comply with this feature and, at the same time, enable to adjust the transport velocity, a mechanical device has been conceived in such a way that the first natural frequency of the conveyor can be changed. It is shown that the transport velocity is determined by the proximity between the excitation frequency and the first natural frequency of the conveyor. The experimental tests performed to characterize the dynamic behavior of the prototype are described and the range of transport velocities is determined. PMID:23867743

  5. Improving yield of PZT piezoelectric devices on glass substrates

    Science.gov (United States)

    Johnson-Wilke, Raegan L.; Wilke, Rudeger H. T.; Cotroneo, Vincenzo; Davis, William N.; Reid, Paul B.; Schwartz, Daniel A.; Trolier-McKinstry, Susan

    2012-10-01

    The proposed SMART-X telescope includes adaptive optics systems that use piezoelectric lead zirconate titanate (PZT) films deposited on flexible glass substrates. Several processing constraints are imposed by current designs: the crystallization temperature must be kept below 550 °C, the total stress in the film must be minimized, and the yield on 1 cm2 actuator elements should be work, RF magnetron sputtering was used to deposit films since chemical solution deposition (CSD) led to warping of large area flexible glass substrates. A PZT 52/48 film that wasdeposited at 4 mTorr and annealed at 550 °C for 24 hours showed no detectable levels of either PbO or pyrochlore second phases. Large area electrodes (1cm x 1 cm) were deposited on 4" glass substrates. Initially, the yield of the devices was low, however, two methods were employed to increase the yield to near 100 %. The first method included a more rigorous cleaning to improve the continuity of the Pt bottom electrode. The second method was to apply 3 V DC across the capacitor structure to burn out regions of defective PZT. The result of this latter method essentially removed conducting filaments in the PZT but left the bulk of the material undamaged. By combining these two methods, the yield on the large area electrodes improved from < 10% to nearly 100%.

  6. Piezoelectric Ceramics of the (1 − x)Bi0.50Na0.50TiO3–xBa0.90Ca0.10TiO3 Lead-Free Solid Solution: Chemical Shift of the Morphotropic Phase Boundary, a Case Study for x = 0.06

    Science.gov (United States)

    Vivar-Ocampo, Rodrigo; Pardo, Lorena; Ávila, David; Morán, Emilio; González, Amador M.; Bucio, Lauro; Villafuerte-Castrejón, María-Elena

    2017-01-01

    Research and development of lead-free piezoelectric materials are still the hottest topics in the field of piezoelectricity. One of the most promising lead-free family of compounds to replace lead zirconate–titanate for actuators is that of Bi0.50Na0.50TiO3 (BNT) based solid solutions. The pseudo-binary (1 − x)Bi0.50Na0.50TiO3–xBa1 − yCayTiO3 system has been proposed for high temperature capacitors and not yet fully explored as piezoelectric material. In this work, the solid solution with x = 0.06 and y = 0.10 was obtained by two different synthesis routes: solid state and Pechini, aiming at using reduced temperatures, both in synthesis (<800 °C) and sintering (<1150 °C), while maintaining appropriated piezoelectric performance. Crystal structure, ceramic grain size, and morphology depend on the synthesis route and were analyzed by X-ray diffraction, together with scanning and transmission electron microscopy. The effects of processing and ceramic microstructure on the structural, dielectric, ferroelectric, and piezoelectric properties were discussed in terms of a shift of the Morphotropic Phase Boundary, chemically induced by the synthesis route. PMID:28773096

  7. A novel ultra-planar, long-stroke and low-voltage piezoelectric micromirror

    Science.gov (United States)

    Bakke, Thor; Vogl, Andreas; Żero, Oleg; Tyholdt, Frode; Johansen, Ib-Rune; Wang, Dag

    2010-06-01

    A novel piston-type micromirror with a stroke of up to 20 µm at 20 V formed out of a silicon-on-insulator wafer with integrated piezoelectric actuators was designed, fabricated and characterized. The peak-to-valley planarity of a 2 mm diameter mirror was better than 15 nm, and tip-to-tip tilt upon actuation less than 30 nm. A resonance frequency of 9.8 kHz was measured. Analytical and finite element models were developed and compared to measurements. The design is based on a silicon-on-insulator wafer where the circular mirror is formed out of the handle silicon, thus forming a thick, highly rigid and ultra-planar mirror surface. The mirror plate is connected to a supporting frame through a membrane formed out of the device silicon layer. A piezoelectric actuator made of lead-zirconate-titanate (PZT) thin film is structured on top of the membrane, providing mirror deflection by deformation of the membrane. Two actuator designs were tested: one with a single ring and the other with a double ring providing bidirectional movement of the mirror. The fabricated mirrors were characterized by white light interferometry to determine the static and temporal response as well as mirror planarity.

  8. Piezoelectric Materials Under Natural and Man-Made Radiation: The Potential for Direct Radiation Detection

    Science.gov (United States)

    Wart, Megan; Simpson, Evan; Flaska, Marek

    2018-01-01

    Radiation detection systems used for monitoring long term waste storage need to be compact, rugged, and have low or no power requirements. By using piezoelectric materials it may be possible to create a reliable self-powered radiation detection system. To determine the feasibility of this approach, the electrical signal response of the piezoelectric materials to radiation must be characterized. To do so, an experimental geometry has been designed and a neutron source has been chosen as described in this paper, which will be used to irradiate a uranium foil for producing fission fragments. These future experiments will be aimed at finding the threshold of exposure of lead zirconate titanate (PZT) plates needed to produce and electrical signal. Based on the proposed experimental geometry the thermal neutron beam-line at the Breazeale Reactor at The Pennsylvania State University will be used as the neutron source. The uranium foil and neutron source will be able to supply a maximum flux of 1.5e5 fission fragments/second*cm2 to each of the PZT plates.

  9. Optimization of electrode geometry and piezoelectric layer thickness of a deformable mirror

    Directory of Open Access Journals (Sweden)

    Nováková Kateřina

    2013-05-01

    Full Text Available Deformable mirrors are the most commonly used wavefront correctors in adaptive optics systems. Nowadays, many applications of adaptive optics to astronomical telescopes, high power laser systems, and similar fast response optical devices require large diameter deformable mirrors with a fast response time and high actuator stroke. In order to satisfy such requirements, deformable mirrors based on piezoelectric layer composite structures have become a subject of intense scientific research during last two decades. In this paper, we present an optimization of several geometric parameters of a deformable mirror that consists of a nickel reflective layer deposited on top of a thin lead zirconate titanate (PZT piezoelectric disk. Honeycomb structure of gold electrodes is deposited on the bottom of the PZT layer. The analysis of the optimal thickness ratio between the PZT and nickel layers is performed to get the maximum actuator stroke using the finite element method. The effect of inter-electrode distance on the actuator stroke and influence function is investigated. Applicability and manufacturing issues are discussed.

  10. Piezoelectric Materials Under Natural and Man-Made Radiation: The Potential for Direct Radiation Detection

    Directory of Open Access Journals (Sweden)

    Wart Megan

    2018-01-01

    Full Text Available Radiation detection systems used for monitoring long term waste storage need to be compact, rugged, and have low or no power requirements. By using piezoelectric materials it may be possible to create a reliable self-powered radiation detection system. To determine the feasibility of this approach, the electrical signal response of the piezoelectric materials to radiation must be characterized. To do so, an experimental geometry has been designed and a neutron source has been chosen as described in this paper, which will be used to irradiate a uranium foil for producing fission fragments. These future experiments will be aimed at finding the threshold of exposure of lead zirconate titanate (PZT plates needed to produce and electrical signal. Based on the proposed experimental geometry the thermal neutron beam-line at the Breazeale Reactor at The Pennsylvania State University will be used as the neutron source. The uranium foil and neutron source will be able to supply a maximum flux of 1.5e5 fission fragments/second*cm2 to each of the PZT plates.

  11. Modelling of magneto-acoustic resonance in ferrite-piezoelectric bilayers

    Energy Technology Data Exchange (ETDEWEB)

    Bichurin, M I; Petrov, V M; Averkin, S V; Filippov, A V [Institute for Electronic Information Systems, Novgorod State University, Veliky Novgorod 173003 (Russian Federation); Liverts, E [Department of Physics, Ben-Gurion University of the Negev, Beersheva 84105 (Israel); Mandal, S; Srinivasan, G [Physics Department, Oakland University, Rochester, MI 48309 (United States)

    2009-11-07

    A model is discussed for magnetoelectric (ME) effects in a single-crystal ferrite-piezoelectric bilayer on a substrate. The specific focus is on coupling at magneto-acoustic resonance (MAR) at the coincidence of ferromagnetic resonance in the ferrite and thickness modes of the electromechanical resonance in the piezoelectric. The clamping effect of the substrate has been considered in determining the ME voltage coefficient and applied to a model system of a bilayer of lead zirconate titanate (PZT) and yttrium iron garnet (YIG) on a gadolinium gallium garnet substrate. The theory predicts a giant ME effect at MAR due to interaction and transfer of energy between elastic modes and the uniform precession spin-wave mode. It is shown that the ME coupling strength decreases with increasing substrate thickness. Estimates for YIG-PZT for nominal film parameters predict MAR at 5 GHz and ME coefficients on the order of 5-70 V cm{sup -1} Oe{sup -1}. The phenomenon is of importance for the realization of multifunctional ME sensors and transducers operating at microwave frequencies.

  12. Piezoelectric and dielectric characterization of corona and contact poled PZT-epoxy-MWCNT bulk composites

    Science.gov (United States)

    Banerjee, S.; Cook-Chennault, K. A.; Du, W.; Sundar, U.; Halim, H.; Tang, A.

    2016-11-01

    Three-phase lead zirconate titanate (PZT, PbZr0.52Ti0.48O3)-epoxy-multi-walled carbon nanotube (MWCNT) bulk composites were prepared, where the volume fraction of PZT was held constant at 30%, while the volume fraction of the MWCNTs was varied from 1.0%-10%. The samples were poled using either a parallel plate contact or contactless (corona) poling technique. The piezoelectric strain coefficient (d33), dielectric constant (ɛ), and dielectric loss tangent (tan δ) of the samples were measured at 110 Hz, and compared as a function of poling technique and volume fraction of MWCNTs. The highest values for dielectric constant and piezoelectric strain coefficients were 465.82 and 18.87 pC/N for MWCNT volume fractions of 10% and 6%, respectively. These values were obtained for samples that were poled using the corona contactless method. The impedance and dielectric spectra of the composites were recorded over a frequency range of 100 Hz-20 MHz. The impedance values observed for parallel-plate contact poled samples are higher than that of corona poled composites. The fractured surface morphology and distribution of the PZT particles and MWCNTs were observed with the aid of electron dispersion spectroscopy and a scanning electron microscope. The surface morphology of the MWCNTs was observed with the aid of a field emission transmission electron microscope.

  13. Engineered piezoelectricity in graphene.

    Science.gov (United States)

    Ong, Mitchell T; Reed, Evan J

    2012-02-28

    We discover that piezoelectric effects can be engineered into nonpiezoelectric graphene through the selective surface adsorption of atoms. Our calculations show that doping a single sheet of graphene with atoms on one side results in the generation of piezoelectricity by breaking inversion symmetry. Despite their 2D nature, piezoelectric magnitudes are found to be comparable to those in 3D piezoelectric materials. Our results elucidate a designer piezoelectric phenomenon, unique to the nanoscale, that has potential to bring dynamical control to nanoscale electromechanical devices.

  14. Giant strain with ultra-low hysteresis and high temperature stability in grain oriented lead-free K0.5Bi0.5TiO3-BaTiO3-Na0.5Bi0.5TiO3 piezoelectric materials.

    Science.gov (United States)

    Maurya, Deepam; Zhou, Yuan; Wang, Yaojin; Yan, Yongke; Li, Jiefang; Viehland, Dwight; Priya, Shashank

    2015-02-26

    We synthesized grain-oriented lead-free piezoelectric materials in (K0.5Bi0.5TiO3-BaTiO3-xNa0.5Bi0.5TiO3 (KBT-BT-NBT) system with high degree of texturing along the [001]c (c-cubic) crystallographic orientation. We demonstrate giant field induced strain (~0.48%) with an ultra-low hysteresis along with enhanced piezoelectric response (d33 ~ 190pC/N) and high temperature stability (~160°C). Transmission electron microscopy (TEM) and piezoresponse force microscopy (PFM) results demonstrate smaller size highly ordered domain structure in grain-oriented specimen relative to the conventional polycrystalline ceramics. The grain oriented specimens exhibited a high degree of non-180° domain switching, in comparison to the randomly axed ones. These results indicate the effective solution to the lead-free piezoelectric materials.

  15. Piezoelectric Motors, an Overview

    Directory of Open Access Journals (Sweden)

    Karl Spanner

    2016-02-01

    Full Text Available Piezoelectric motors are used in many industrial and commercial applications. Various piezoelectric motors are available in the market. All of the piezoelectric motors use the inverse piezoelectric effect, where microscopically small oscillatory motions are converted into continuous or stepping rotary or linear motions. Methods of obtaining long moving distance have various drive and functional principles that make these motors categorized into three groups: resonance-drive (piezoelectric ultrasonic motors, inertia-drive, and piezo-walk-drive. In this review, a comprehensive summary of piezoelectric motors, with their classification from initial idea to recent progress, is presented. This review also includes some of the industrial and commercial applications of piezoelectric motors that are presently available in the market as actuators.

  16. Clamping effect on the piezoelectric responses of screen-printed low temperature PZT/Polymer films on flexible substrates

    Science.gov (United States)

    Almusallam, A.; Yang, K.; Zhu, D.; Torah, R. N.; Komolafe, A.; Tudor, J.; Beeby, S. P.

    2015-11-01

    This paper introduces a new flexible lead zirconate titanate (PZT)/polymer composite material that can be screen-printed onto fabrics and flexible substrates, and investigates the clamping effect of these substrates on the characterization of the piezoelectric material. Experimental results showed that the optimum blend of PZT/polymer binder with a weight ratio of 12:1 provides a dielectric constant of 146. The measured value of the piezoelectric coefficient d33 was found to depend on the substrate used. Measured d33clp values of 70, 40, 36 pC N-1 were obtained from the optimum formulation printed on Polyester-cotton with an interface layer, Kapton and alumina substrates, respectively. The variation in the measured d33clp values occurs because of the effect of the mechanical boundary conditions of the substrate. The piezoelectric film is mechanically bonded to the surface of the substrate and this constrains the film in the plane of the substrate (the 1-direction). This constraint means that the perpendicular forces (applied in the 3-direction) used to measure d33 introduce a strain in the 1-direction that produces a charge of the opposite polarity to that induced by the d33 effect. This is due to the negative sign of the d31 coefficient and has the effect of reducing the measured d33 value. Theoretical and experimental investigations confirm a reduction of 13%, 50% and 55% in the estimated freestanding d33fs values (80 pC N-1) on Polyester-cotton, Kapton and alumina substrates, respectively. These results demonstrate the effect of the boundary conditions of the substrate/PZT interface on the piezoelectric response of the PZT/polymer film and in particular the reduced effect of fabric substrates due to their lowered stiffness.

  17. New design for inertial piezoelectric motors

    Science.gov (United States)

    Liu, Lige; Ge, Weifeng; Meng, Wenjie; Hou, Yubin; Zhang, Jing; Lu, Qingyou

    2018-03-01

    We have designed, implemented, and tested a novel inertial piezoelectric motor (IPM) that is the first IPM to have controllable total friction force, which means that it sticks with large total friction forces and slips with severely reduced total friction forces. This allows the IPM to work with greater robustness and produce a larger output force at a lower threshold voltage while also providing higher rigidity. This is a new IPM design that means that the total friction force can be dramatically reduced or even canceled where necessary by pushing the clamping points at the ends of a piezoelectric tube that contains the sliding shaft inside it in the opposite directions during piezoelectric deformation. Therefore, when the shaft is propelled forward by another exterior piezoelectric tube, the inner piezoelectric tube can deform to reduce the total friction force acting on the shaft instantly and cause more effective stepping movement of the shaft. While our new IPM requires the addition of another piezoelectric tube, which leads to an increase in volume of 120% when compared with traditional IPMs, the average step size has increased by more than 400% and the threshold voltage has decreased by more than 50 V. The improvement in performance is far more significant than the increase in volume. This enhanced performance will allow the proposed IPM to work under large load conditions where a simple and powerful piezoelectric motor is needed.

  18. Dielectric and piezoelectric characteristics of lead-free Bi{sub 0.5}(Na{sub 0.84}K{sub 0.16}){sub 0.5}TiO{sub 3} ceramics substituted with Sr

    Energy Technology Data Exchange (ETDEWEB)

    Yoo, Juhyun [Department of Electrical Engineering, Semyung University Jechon, Chungbuk, 390-711 (Korea, Republic of); Oh, Dongon [Sunny Electronics Corporation, Chungju, 380-240 (Korea, Republic of); Jeong, Yeongho [Korea Electric Power Research Institute, Yusung-Gu, Taejon 305-380 (Korea, Republic of); Hong, Jaeil [Department of Electricity, Dongseoul Tech. Jr. College, 255 Soo Jung-Ku, Sung Nam (Korea, Republic of); Jung, Moonyoung [Department of Earth Resources and Environmental Geotechnics Engineering, Semyung University Jechon, Chungbuk, 390-711 (Korea, Republic of)

    2004-11-01

    In this study, lead-free Bi{sub 0.5}(Na{sub 0.84}K{sub 0.16}){sub 0.5}TiO{sub 3} ceramics were fabricated with the variations of Sr substitution and their dielectric and piezoelectric characteristics were investigated. Through the analysis of XRD diffraction pattern and SEM, crystal structure and microstructure were evaluated. With the increasing amount of Sr substitution, dielectric constant linearly increased at the rate of about 90 per 1 mol% and Curie temperature decreased slightly. Also, the temperature dependence curve of dielectric constant moved leftward. At 4 mol% Sr substitution, T{sub c} of 292C, k{sub p} of 34.3%, k{sub t} of 45.32%, and d{sub 33} of 185 pC/N were obtained, respectively.

  19. Direct Chlorination of Zircon Sand

    International Nuclear Information System (INIS)

    Dwiretnani Sudjoko; Budi Sulistyo; Pristi Hartati; Sunardjo

    2002-01-01

    It was investigated the direct chlorination of zircon sand in a unit chlorination equipment. The process was in semi batch. The product gas was scrubbed in aqueous NaOH. It was search the influence of time, ratio of reactant and size of particle sand to the concentration of Zr and Si in the product. From these research it was found that as the times, ratio of reactant increased, the concentration of Zr increased, but the concentration of Si decreased, while as grain size of zircon sand decreased the concentration of Zr decreased, but the concentration of Si increased. (author)

  20. Enhanced temperature stability and quality factor with Hf substitution for Sn and MnO2 doping of (Ba0.97Ca0.03(Ti0.96Sn0.04O3 lead-free piezoelectric ceramics with high Curie temperature

    Directory of Open Access Journals (Sweden)

    Cheng-Che Tsai

    2016-12-01

    Full Text Available In this work, the process of two-stage modifications for (Ba0.97Ca0.03(Ti0.96Sn0.04-xHfxO3 (BCTS4-100xH100x ceramics was studied. The trade-off composition was obtained by Hf substitution for Sn and MnO2 doping (two-stage modification which improves the temperature stability and piezoelectric properties. The phase structure ratio, microstructure, and dielectric, piezoelectric, ferroelectric, and temperature stability properties were systematically investigated. Results showed that BCTS4-100xH100x piezoelectric ceramics with x=0.035 had a relatively high Curie temperature (TC of about 112 °C, a piezoelectric charge constant (d33 of 313 pC/N, an electromechanical coupling factor (kp of 0.49, a mechanical quality factor (Qm of 122, and a remnant polarization (Pr of 19μC/cm2. In addition, the temperature stability of the resonant frequency (fr, kp, and aging d33 could be tuned via Hf content. Good piezoelectric temperature stability (up to 110 °C was found with x =0.035. BCTS0.5H3.5 + a mol% Mn (BCTSH + a Mn piezoelectric ceramics with a = 2 had a high TC of about 123 °C, kp ∼ 0.39, d33 ∼ 230 pC/N, Qm ∼ 341, and high temperature stability due to the produced oxygen vacancies. This mechanism can be depicted using the complex impedance analysis associated with a valence compensation model on electric properties. Two-stage modification for lead-free (Ba0.97Ca0.03(Ti0.96Sn0.04O3 ceramics suitably adjusts the compositions for applications in piezoelectric motors and actuators.

  1. Phase transition and piezoelectric properties of K0.48Na0.52NbO3-LiTa0.5Nb0.5O3-NaNbO3 lead-free ceramics

    International Nuclear Information System (INIS)

    Gao Feng; Liu Liangliang; Xu Bei; Cao Xiao; Deng Zhenqi; Tian Changsheng

    2011-01-01

    Highlights: → The evolution of the crystal structure for the new phase K 3 Li 2 Nb 5 O 15 was described. → The dielectric relaxor behavior would be strengthened by increasing plate-like NN. → k p and d 33 decrease with increasing amount of plate-like NN. → 0.01-0.03 mol of plate-like NN is a proper content for texturing ceramics by RTGG. - Abstract: Plate-like NaNbO 3 (NN) particles were used as the raw material to fabricate (1 - x)[0.93 K 0.48 Na 0.52 Nb O 3 -0.07Li(Ta 0.5 Nb 0.5 )O 3 ]-xNaNbO 3 lead-free piezoelectric ceramics using a conventional ceramic process. The effects of NN on the crystal structure and piezoelectric properties of the ceramics were investigated. The results of X-ray diffraction suggest that the perovskite phase coexists with the K 3 Li 2 Nb 5 O 15 phase, and the tilting of the oxygen octahedron is probably responsible for the evolution of the tungsten-bronze-typed K 3 Li 2 Nb 5 O 15 phase. The Curie temperature (T C ) is shifted to lower temperature with increasing NN content. (1 - x)[0.93 K 0.48 Na 0.52 NbO 3 -0.07Li(Ta 0.5 Nb 0.5 )O 3 ]-xNaNbO 3 ceramics show obvious dielectric relaxor characteristics for x > 0.03, and the relaxor behavior of ceramics is strengthened by increasing NN content. Both the electromechanical coupling factor (k p ) and the piezoelectric constant (d 33 ) decrease with increasing amounts of NN. 0.01-0.03 mol of plate-like NaNbO 3 in 0.93 K 0.48 Na 0.52 NbO 3 -0.07Li(Ta 0.5 Nb 0.5 )O 3 gives the optimum content for preparing textured ceramics by the RTGG method.

  2. The giant piezoelectric effect: electric field induced monoclinic phase or piezoelectric distortion of the rhombohedral parent?

    International Nuclear Information System (INIS)

    Kisi, E H; Piltz, R O; Forrester, J S; Howard, C J

    2003-01-01

    Lead zinc niobate-lead titanate (PZN-PT) single crystals show very large piezoelectric strains for electric fields applied along the unit cell edges e.g. [001] R . It has been widely reported that this effect is caused by an electric field induced phase transition from rhombohedral (R3m) to monoclinic (Cm or Pm) symmetry in an essentially continuous manner. Group theoretical analysis using the computer program ISOTROPY indicates phase transitions between R3m and Cm (or Pm) must be discontinuous under Landau theory. An analysis of the symmetry of a strained unit cell in R3m and a simple expansion of the piezoelectric strain equation indicate that the piezoelectric distortion due to an electric field along a cell edge in rhombohedral perovskite-based ferroelectrics is intrinsically monoclinic (Cm), even for infinitesimal electric fields. PZN-PT crystals have up to nine times the elastic compliance of other piezoelectric perovskites and it might be expected that the piezoelectric strains are also very large. A field induced phase transition is therefore indistinguishable from the piezoelectric distortion and is neither sufficient nor necessary to understand the large piezoelectric response of PZN-PT

  3. Anomalous piezoelectricity in two-dimensional graphene nitride nanosheets.

    Science.gov (United States)

    Zelisko, Matthew; Hanlumyuang, Yuranan; Yang, Shubin; Liu, Yuanming; Lei, Chihou; Li, Jiangyu; Ajayan, Pulickel M; Sharma, Pradeep

    2014-06-27

    Piezoelectricity is a unique property of materials that permits the conversion of mechanical stimuli into electrical and vice versa. On the basis of crystal symmetry considerations, pristine carbon nitride (C3N4) in its various forms is non-piezoelectric. Here we find clear evidence via piezoresponse force microscopy and quantum mechanical calculations that both atomically thin and layered graphitic carbon nitride, or graphene nitride, nanosheets exhibit anomalous piezoelectricity. Insights from ab inito calculations indicate that the emergence of piezoelectricity in this material is due to the fact that a stable phase of graphene nitride nanosheet is riddled with regularly spaced triangular holes. These non-centrosymmetric pores, and the universal presence of flexoelectricity in all dielectrics, lead to the manifestation of the apparent and experimentally verified piezoelectric response. Quantitatively, an e11 piezoelectric coefficient of 0.758 C m(-2) is predicted for C3N4 superlattice, significantly larger than that of the commonly compared α-quartz.

  4. Modelling, fabrication, and characterization for improved piezoelectric energy harvesters

    Science.gov (United States)

    Alomari, Almuatasim Ali

    The ambitious goal of this dissertation is to contribute its share to the scientific researchers and academic community by demonstrate a versatile study on energy harvesting via smart materials. Smart materials are amongst the current production modes which generate clean and green energy. The advantages of smart materials include ferroelectric, piezoelectric, and pyroelectric ceramics and composites in materials science and technology of the 21 st century are inconceivable. Their most current applications include conventional sensors, actuators, batteries replacement, and switch. Further, Piezoelectricity is the accumulation of electrical charges as a result of applying mechanical stress on certain type of materials such as crystals, DNA, and protein, where pyro-electricity is the accumulation of electrical charges from ambient environment from temperature gauges or fluctuations. In an incessant effort to increase the performance of smart materials devices researchers in both academic and industrial communities in field of green energy have suggested many techniques and procedures to increase the power generation capability and enhance the bandwidth of thermal and vibration energy harvesters. In this study, the EulerBernoulli beam Theory, lumped parameter model (LPM), and chain matrix method were applied on various design and structure shape of smart materials to find the output electrical parameters. The modeling and simulation investigations are accomplished using MATLAB program and COMSOL Multiphysics software. A low-cost fabrication technique, of polyvinyl-dine difluoride (PVDF) with different amount of Lead Zirconate Titanate (PZT), Lead Magnesium Niobate-Lead Titanate (PMN-PT), and Multi-walled Carbon Nanotubes (MWCNT) are introduced in this study as well. Later, the (Paint/ PZT) fabricated nanocomposites was tested for dielectric constants over a wide frequency range at different temperatures. It was observed that the composites with higher concentrations

  5. Enhanced pyroelectric and piezoelectric properties of PZT with aligned porosity for energy harvesting applications† †Electronic supplementary information (ESI) available. See DOI: 10.1039/c7ta00967d Click here for additional data file.

    Science.gov (United States)

    Zhang, Yan; Xie, Mengying; Roscow, James; Bao, Yinxiang; Zhou, Kechao

    2017-01-01

    This paper demonstrates the significant benefits of exploiting highly aligned porosity in piezoelectric and pyroelectric materials for improved energy harvesting performance. Porous lead zirconate (PZT) ceramics with aligned pore channels and varying fractions of porosity were manufactured in a water-based suspension using freeze-casting. The aligned porous PZT ceramics were characterized in detail for both piezoelectric and pyroelectric properties and their energy harvesting performance figures of merit were assessed parallel and perpendicular to the freezing direction. As a result of the introduction of porosity into the ceramic microstructure, high piezoelectric and pyroelectric harvesting figures of merits were achieved for porous freeze-cast PZT compared to dense PZT due to the reduced permittivity and volume specific heat capacity. Experimental results were compared to parallel and series analytical models with good agreement and the PZT with porosity aligned parallel to the freezing direction exhibited the highest piezoelectric and pyroelectric harvesting response; this was a result of the enhanced interconnectivity of the ferroelectric material along the poling direction and reduced fraction of unpoled material that leads to a higher polarization. A complete thermal energy harvesting system, composed of a parallel-aligned PZT harvester element and an AC/DC converter, was successfully demonstrated by charging a storage capacitor. The maximum energy density generated by the 60 vol% porous parallel-connected PZT when subjected to thermal oscillations was 1653 μJ cm–3, which was 374% higher than that of the dense PZT with an energy density of 446 μJ cm–3. The results are beneficial for the design and manufacture of high performance porous pyroelectric and piezoelectric materials in devices for energy harvesting and sensor applications. PMID:28580142

  6. Radioactivity in the zircon industry

    International Nuclear Information System (INIS)

    Selby, J.H.

    2002-01-01

    In a presentation from the Zircon Industry, it was shown that zircon sand contains significant concentrations of uranium, 3,500 to 4,500 Bq/kg, and thorium, 400 to 600 Bq/kg. Deposits mainly occur in South Africa, Australia, India and the USA. The mining is done by dredging or by just shoveling the sand onto trucks. The separation could be done by dry or wet concentration. Also the milling could be by dry or wet processes. The dry process has the highest risk of dust generation. The maximum potential annual dose for the milling process has been assessed to be about 5mSv. Measurements from South Africa and Australia indicate lower doses, 0.2 to 1 mSv/y

  7. Developing Zircon as a Probe of Planetary Impact History

    Science.gov (United States)

    Wielicki, Matthew

    2014-12-01

    The identification of Meteor Crater in Arizona as an extraterrestrial impact by Eugene Shoemaker provided the first evidence of this geologic phenomenon and opened the door to a new field of research that has eventually lead to the identification of over ~150 terrestrial impact structures. Subsequently impacts have been evoked in the formation of the moon, delivery of volatiles and bio-precursors to early Earth, creation of habitats for the earliest life and, in more recent times, major mass extinction events. However, understanding the impact flux to the Earth-Moon system has been complicated by the constant weathering and erosion at Earth's surface and the complex nature of impactite samples such that only a hand full of terrestrial craters have been accurately and precisely dated. Currently 40Ar/39Ar step-heating analysis of impactite samples is commonly used to infer impact ages but can be problematic due to the presence of relic clasts, incomplete 40Ar outgassing or excess 40Ar, and recoil and shock effects. The work presented here attempts to develop zircon geochronology to probe planetary impact histories as an alternative to current methods and provides another tool by which to constrain the bolide flux to the Earth-Moon system. Zircon has become the premier geo-chronometer in earth science and geochemical investigation of Hadean zircon from Western Australia has challenged the long-standing, popular conception that the near-surface Hadean Earth was an uninhabitable and hellish world; Zircons may preserve environmental information regarding their formation and thus provide a rare window into conditions on early Earth. Isotopic and petrologic analyses of these ancient grains have been interpreted to suggest that early Earth was more habitable than previously envisioned, with water oceans, continental crust, and possibly even plate tectonics. The Hadean is also suspected to be a time of major planetary bombardment however identifying impact signatures within

  8. Design and fabrication of a piezoelectric mode 2 sensor based on optical modulated liquid crystal and spiropyran

    International Nuclear Information System (INIS)

    Chen, Kuan-Ting; Lee, Chih-Kung; Chang, Chin-Kai; Kuo, Hui-Lung

    2011-01-01

    In this paper, we propose an innovative photoelectric material made of a mixture of liquid crystal and spiropyran which can be used to tailor the performance of piezoelectric sensors. The impedance variation of this photoelectric material can be controlled using different ultraviolet (UV) irradiation times. We found that the impedance of the liquid crystal–spiropyran mixture remains stable after the UV irradiation. Results showed that UV irradiation at 180 s resulted in the lowest mixture impedance. It appears that the electrical properties of the mixture have great potential to modulate a piezoelectric system since UV irradiation can be used to tailor the impedance of a photosensitive electrode made of a liquid crystal–spiropyran sensor for PZT (i.e. lead zirconate titanate) modal actuator/sensor applications. The main innovation of this paper is the demonstration of a new approach towards producing a positive and negative bias voltage in different regions of a sensor by using UV illumination for different time periods. A one-dimensional mode 2 sensor for a cantilever beam was designed and tested to verify the validity of this innovative approach. Since UV illumination can be changed in situ or in real time, this research also represents the creation of an optically defined/tailored modal sensor. In the future, a two-dimensional optical modal control could also be obtained using the method demonstrated

  9. Fission track dating of zircon: a multichronometer

    International Nuclear Information System (INIS)

    Carpena, J.

    1992-01-01

    Scattering in Fission Track ages of zircons of a single rock is possible when they present morphological and geochemical variations, if the greatest care is not taken in the choice of the etching conditions and the counting of tracks. The Fission Track study of two heterogeneous populations of zircons from the Mont Blanc granite and from the Gran Paradiso gneisses allows to show that zircon may work as a multichronometer

  10. Lead-free (K0.5Na0.5)NbO3 thin films by pulsed laser deposition driving MEMS-based piezoelectric cantilevers

    NARCIS (Netherlands)

    Nguyen, Duc Minh; Dekkers, Jan M.; Houwman, Evert Pieter; Vu, H.T.; Vu, Hung N.; Rijnders, Augustinus J.H.M.

    2016-01-01

    Thin film capacitors of the lead-free (K0.5Na0.5)NbO3 (KNN) with (100) orientation were grown on Pt/Ti/SiO2/SOI (silicon-on-insulator) substrates by pulsed laser deposition. The films are pure phases and do not show other crystal orientations. The remnant polarization Pr, saturation polarization

  11. Piezoelectric cantilever sensors

    Science.gov (United States)

    Shih, Wan Y. (Inventor); Shih, Wei-Heng (Inventor); Shen, Zuyan (Inventor)

    2008-01-01

    A piezoelectric cantilever with a non-piezoelectric, or piezoelectric tip useful as mass and viscosity sensors. The change in the cantilever mass can be accurately quantified by monitoring a resonance frequency shift of the cantilever. For bio-detection, antibodies or other specific receptors of target antigens may be immobilized on the cantilever surface, preferably on the non-piezoelectric tip. For chemical detection, high surface-area selective absorbent materials are coated on the cantilever tip. Binding of the target antigens or analytes to the cantilever surface increases the cantilever mass. Detection of target antigens or analytes is achieved by monitoring the cantilever's resonance frequency and determining the resonance frequency shift that is due to the mass of the adsorbed target antigens on the cantilever surface. The use of a piezoelectric unimorph cantilever allows both electrical actuation and electrical sensing. Incorporating a non-piezoelectric tip (14) enhances the sensitivity of the sensor. In addition, the piezoelectric cantilever can withstand damping in highly viscous liquids and can be used as a viscosity sensor in wide viscosity range.

  12. Impedance-based structural health monitoring of additive manufactured structures with embedded piezoelectric wafers

    Science.gov (United States)

    Scheyer, Austin G.; Anton, Steven R.

    2017-04-01

    Embedding sensors within additive manufactured (AM) structures gives the ability to develop smart structures that are capable of monitoring the mechanical health of a system. AM provides an opportunity to embed sensors within a structure during the manufacturing process. One major limitation of AM technology is the ability to verify the geometric and material properties of fabricated structures. Over the past several years, the electromechanical impedance (EMI) method for structural health monitoring (SHM) has been proven to be an effective method for sensing damage in structurers. The EMI method utilizes the coupling between the electrical and mechanical properties of a piezoelectric transducer to detect a change in the dynamic response of a structure. A piezoelectric device, usually a lead zirconate titanate (PZT) ceramic wafer, is bonded to a structure and the electrical impedance is measured across as range of frequencies. A change in the electrical impedance is directly correlated to changes made to the mechanical condition of the structure. In this work, the EMI method is employed on piezoelectric transducers embedded inside AM parts to evaluate the feasibility of performing SHM on parts fabricated using additive manufacturing. The fused deposition modeling (FDM) method is used to print specimens for this feasibility study. The specimens are printed from polylactic acid (PLA) in the shape of a beam with an embedded monolithic piezoelectric ceramic disc. The specimen is mounted as a cantilever while impedance measurements are taken using an HP 4194A impedance analyzer. Both destructive and nondestructive damage is simulated in the specimens by adding an end mass and drilling a hole near the free end of the cantilever, respectively. The Root Mean Square Deviation (RMSD) method is utilized as a metric for quantifying damage to the system. In an effort to determine a threshold for RMSD, the values are calculated for the variation associated with taking multiple

  13. Phase transitions and optical characterization of lead-free piezoelectric (K0.5Na0.5)0.96Li0.04(Nb 0.8Ta0.2)O3 thin films

    KAUST Repository

    Yao, Yingbang

    2013-06-01

    Lead-free piezoelectric thin films, (K0.5Na0.5) 0.96Li0.04(Nb0.8Ta0.2)O 3, were epitaxially grown on MgO(001) and Nb-doped SrTiO 3(001) substrates using pulsed laser deposition. The optimum deposition temperature was found to be 600 C. Two types of in-plane orientations were observed in the films depending on the substrates used. The transmittance and photoluminescence spectra as well as the dielectric and ferroelectric properties of the films were measured. The measured band-gap energy was found to be decreased with the deposition temperature. The dielectric constant decreased from 550 to 300 as the frequency increased from 100 Hz to 1 MHz. The measured remnant polarization and coercive field were 4 μC/cm2 and 68 kV/cm, respectively. The phase transitions of the films were studied by Raman spectroscopy. Two distinct anomalies originating from the cubic-to-tetragonal (TC-T ~ 300 C) and tetragonal-to-orthorhombic (TT-O ~ 120 C) phase transitions were observed. Our results show that Raman spectroscopy is a powerful tool in identifying the phase transitions in ferroelectric thin films. © 2013 Elsevier B.V.

  14. Preparation and characterization of Mn-doped Li{sub 0.06}(Na{sub 0.5}K{sub 0.5}){sub 0.94}NbO{sub 3} lead-free piezoelectric ceramics with surface sol-gel coatings

    Energy Technology Data Exchange (ETDEWEB)

    Yoo, Ae Ri; Lee, Seong Eui; Lee, Hee Chul [Korea Polytechnic University, Shiheung (Korea, Republic of)

    2014-08-15

    This study investigated the effects of Mn doping and sol-gel surface coating on the structural and the electrical properties of lead-free Li{sub 0.06}(K{sub 0.5}Na{sub 0.5}){sub 0.94}NbO{sub 3}(LNKN) ceramics in disc form for use as eco-friendly piezoelectric devices. The 1-mol% Mn-doped LNKN ceramic showed a relatively high piezoelectric constant owing to its high density in the case of its being annealed at a temperature of 1010 .deg. C. A Mn-doped LNKN sol-gel solution with the same composition as that of the ceramics was spin-coated and sintered on both sides of the ceramic surfaces to acquire improved electrical properties. The sol-gel surface coating could play a decisive role in filling the pores, resulting in flat and stable interfaces between the electrodes and the piezoelectric elements. As a result, the highest piezoelectric constant, d{sub 33}, of 173 pC/N could be obtained for the Mn-doped LNKN ceramics with 420-nm-thick sol-gel surface coatings.

  15. Phase structure, dielectric, and piezoelectric properties of (K{sub 0.94-x}Na{sub x}Li{sub 0.06})(Nb{sub 0.94}Sb{sub 0.06})O{sub 3} lead-free ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Fu, Lingling; Lin, Dunmin; Zheng, Qiaoji; Wu, Xiaochun; Xu, Chenggang [College of Chemistry and Materials Science, and Visual Computing and Virtual Reality Key Laboratory of Sichuan Province, Sichuan Normal University, Chengdu 610066 (China)

    2012-11-15

    Lead-free piezoelectric ceramics (K{sub 0.94-x}Na{sub x}Li{sub 0.06})(Nb{sub 0.94}Sb{sub 0.06})O{sub 3} have been fabricated by a conventional ceramic technique and the effects of K{sup +}/Na{sup +} ratio on the structure and piezoelectric properties of the ceramics have been studied. All the ceramics possess a pure perovskite structure. The coexistence of tetragonal and orthorhombic phases is formed at room temperature in the ceramics with 0.45 {<=} x {<=} 0.55. The tetragonal-orthorhombic phase-transition temperature T{sub O-T} decreases from 110 to 54 C with x increasing from 0.35 to 0.55 and then increases from 84 to 144 C with x further increasing from 0.6 to 0.7, while the Curie temperature T{sub C} deceases from 388 to 348 C with x increasing from 0.35 to 0.70. Because of the coexistence of the two phases near room temperature, the ceramics with x = 0.50 exhibit the optimum piezoelectric properties: d{sub 33} = 230 pC/N and k{sub p} = 49%. The ceramics possess good time stability of piezoelectric properties. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  16. Notes on Piezoelectricity

    Energy Technology Data Exchange (ETDEWEB)

    Redondo, Antonio [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

    2016-02-03

    These notes provide a pedagogical discussion of the physics of piezoelectricity. The exposition starts with a brief analysis of the classical (continuum) theory of piezoelectric phenomena in solids. The main subject of the notes is, however, a quantum mechanical analysis. We first derive the Frohlich Hamiltonian as part of the description of the electron-phonon interaction. The results of this analysis are then employed to derive the equations of piezoelectricity. A couple of examples with the zinc blende and and wurtzite structures are presented at the end

  17. Perfect zircon for rock dating no fairy tale

    International Nuclear Information System (INIS)

    Anon

    2000-01-01

    The scheme used to date rocks is based on the radioactive decay of uranium. Minute traces of uranium locked inside the zircon crystals have been decaying over aeons, producing lead. Scientists know that the decay occurs at a fixed rate and how quickly it happens. By measuring the relative amounts of uranium and lead encased in the crystals, scientists can determine how old the rock is. But sometimes lead is lost from zircon crystals via processes such as weathering (if the rocks were exposed on the surface) or deformation and metamorphism (if the rocks had crystallised deep in the earth and been subjected to high temperatures and pressure). Hence the special nature of the Temora rocks- a 417 million years old zirconium-containing rock which have been partially exposed in recent times in a remote paddock in NSW, Australia. SHRIMP dating was used for initial tests on the Temora rocks. Then, in December last year, the sample was sent to the world-recognised authority, Canada's Royal Ontario Museum, for independent analysis and dating via chemical decomposition. The museum confirmed the near perfect quality of the zircon and its age

  18. Zircon's Archean of the Ural

    International Nuclear Information System (INIS)

    Krasnobaev, A.A.; Cherednichenko, N.V.

    2005-01-01

    The age of zircons from metamorphic rocks of the Taratashsky complex located on the Western slope of the South Urals was determined by the methods of U-Pb isotope dating. The age values obtained suggest a two-stage model of the complex evolution at early stages of its existence. The age of 2913±133 mln. years identifies the age of granulite metamorphism, while the age 2127±65 mln. years indicates the period of the most intensive transformations of the rocks within the complex, which were accompanied by occurrence of high-temperature diaphthorites [ru

  19. Preparation and properties of calcium zirconate

    International Nuclear Information System (INIS)

    Dudek, M.; Bucko, M.; Rog, G.

    2001-01-01

    Dense samples of calcium zirconate were prepared. Electrical conductivity of the samples were measured in the temperature range 873 - 1273 K by both the d.c. four probe and the impedance spectroscopy methods. Calcium zirconate with small excess of calcium oxide appeared to be oxygen ion conductor. It was applied as an electrolyte in solid-state galvanic cells. (author)

  20. High-throughput density functional calculations to optimize properties and interfacial chemistry of piezoelectric materials

    Science.gov (United States)

    Barr, Jordan A.; Lin, Fang-Yin; Ashton, Michael; Hennig, Richard G.; Sinnott, Susan B.

    2018-02-01

    High-throughput density functional theory calculations are conducted to search through 1572 A B O3 compounds to find a potential replacement material for lead zirconate titanate (PZT) that exhibits the same excellent piezoelectric properties as PZT and lacks both its use of the toxic element lead (Pb) and the formation of secondary alloy phases with platinum (Pt) electrodes. The first screening criterion employed a search through the Materials Project database to find A -B combinations that do not form ternary compounds with Pt. The second screening criterion aimed to eliminate potential candidates through first-principles calculations of their electronic structure, in which compounds with a band gap of 0.25 eV or higher were retained. Third, thermodynamic stability calculations were used to compare the candidates in a Pt environment to compounds already calculated to be stable within the Materials Project. Formation energies below or equal to 100 meV/atom were considered to be thermodynamically stable. The fourth screening criterion employed lattice misfit to identify those candidate perovskites that have low misfit with the Pt electrode and high misfit of potential secondary phases that can be formed when Pt alloys with the different A and B components. To aid in the final analysis, dynamic stability calculations were used to determine those perovskites that have dynamic instabilities that favor the ferroelectric distortion. Analysis of the data finds three perovskites warranting further investigation: CsNb O3 , RbNb O3 , and CsTa O3 .

  1. Energy collection via Piezoelectricity

    International Nuclear Information System (INIS)

    Kumar, Ch Naveen

    2015-01-01

    In the present days, wireless data transmission techniques are commonly used in electronic devices. For powering them connection needs to be made to the power supply through wires else power may be supplied from batteries. Batteries require charging, replacement and other maintenance efforts. So, some alternative methods need to be developed to keep the batteries full time charged and to avoid the need of any consumable external energy source to charge the batteries. Mechanical energy harvesting utilizes piezoelectric components where deformations produced by different means are directly converted to electrical charge via piezoelectric effect. The proposed work in this research recommends Piezoelectricity as a alternate energy source. The motive is to obtain a pollution-free energy source and to utilize and optimize the energy being wasted. Current work also illustrates the working principle of piezoelectric crystal and various sources of vibration for the crystal. (paper)

  2. Piezoelectric MEMS resonators

    CERN Document Server

    Piazza, Gianluca

    2017-01-01

    This book introduces piezoelectric microelectromechanical (pMEMS) resonators to a broad audience by reviewing design techniques including use of finite element modeling, testing and qualification of resonators, and fabrication and large scale manufacturing techniques to help inspire future research and entrepreneurial activities in pMEMS. The authors discuss the most exciting developments in the area of materials and devices for the making of piezoelectric MEMS resonators, and offer direct examples of the technical challenges that need to be overcome in order to commercialize these types of devices. Some of the topics covered include: Widely-used piezoelectric materials, as well as materials in which there is emerging interest Principle of operation and design approaches for the making of flexural, contour-mode, thickness-mode, and shear-mode piezoelectric resonators, and examples of practical implementation of these devices Large scale manufacturing approaches, with a focus on the practical aspects associate...

  3. Zircon-rutile-ilmenite froth flotation process

    International Nuclear Information System (INIS)

    Schmidt, R.; Denham, D.L. Jr.

    1992-01-01

    This patent describes a method for separating a mixture of minerals comprising at least zircon, ilmenite and rutile. It comprises adding an acid solution to the mixture to acidify to a pH of between about 2.0 and 6.0; adding starch to the mixture to depress the ilmenite and the rutile; adding a source of fluoride ions to the mixture to provide a negative surface charge on the zircon surface to activate the zircon; adding an amine cationic collector to the mixture to float the activated zircon; subjecting the mixture containing the added acid solution, the fluoride ions, the starch and the cationic collector, to froth flotation; and withdrawing a float product comprising the zircon and a sink product comprising the ilmenite and rutile

  4. Piezoelectric Energy Harvesting Solutions

    Science.gov (United States)

    Caliò, Renato; Rongala, Udaya Bhaskar; Camboni, Domenico; Milazzo, Mario; Stefanini, Cesare; de Petris, Gianluca; Oddo, Calogero Maria

    2014-01-01

    This paper reviews the state of the art in piezoelectric energy harvesting. It presents the basics of piezoelectricity and discusses materials choice. The work places emphasis on material operating modes and device configurations, from resonant to non-resonant devices and also to rotational solutions. The reviewed literature is compared based on power density and bandwidth. Lastly, the question of power conversion is addressed by reviewing various circuit solutions. PMID:24618725

  5. Laminated piezoelectric transformer

    Science.gov (United States)

    Vazquez Carazo, Alfredo (Inventor)

    2006-01-01

    A laminated piezoelectric transformer is provided using the longitudinal vibration modes for step-up voltage conversion applications. The input portions are polarized to deform in a longitudinal plane and are bonded to an output portion. The deformation of the input portions is mechanically coupled to the output portion, which deforms in the same longitudinal direction relative to the input portion. The output portion is polarized in the thickness direction relative its electrodes, and piezoelectrically generates a stepped-up output voltage.

  6. Stretchable piezoelectric nanocomposite generator.

    Science.gov (United States)

    Park, Kwi-Il; Jeong, Chang Kyu; Kim, Na Kyung; Lee, Keon Jae

    2016-01-01

    Piezoelectric energy conversion that generate electric energy from ambient mechanical and vibrational movements is promising energy harvesting technology because it can use more accessible energy resources than other renewable natural energy. In particular, flexible and stretchable piezoelectric energy harvesters which can harvest the tiny biomechanical motions inside human body into electricity properly facilitate not only the self-powered energy system for flexible and wearable electronics but also sensitive piezoelectric sensors for motion detectors and in vivo diagnosis kits. Since the piezoelectric ZnO nanowires (NWs)-based energy harvesters (nanogenerators) were proposed in 2006, many researchers have attempted the nanogenerator by using the various fabrication process such as nanowire growth, electrospinning, and transfer techniques with piezoelectric materials including polyvinylidene fluoride (PVDF) polymer and perovskite ceramics. In 2012, the composite-based nanogenerators were developed using simple, low-cost, and scalable methods to overcome the significant issues with previously-reported energy harvester, such as insufficient output performance and size limitation. This review paper provides a brief overview of flexible and stretchable piezoelectric nanocomposite generator for realizing the self-powered energy system with development history, power performance, and applications.

  7. Gd2O3 doped 0.82Bi0.5Na0.5TiO3–0.18Bi0.5K0.5TiO3 lead-free piezoelectric ceramics

    International Nuclear Information System (INIS)

    Fu, Peng; Xu, Zhijun; Chu, Ruiqing; Li, Wei; Wang, Wei; Liu, Yong

    2012-01-01

    Highlights: ► Gd 2 O 3 doped BNKT18 piezoelectric ceramics were designed and prepared. ► The electrical properties of the BNKT18 ceramics are improved with the addition of Gd 2 O 3 . ► The BNKT18 ceramics doped with 0.4 wt.% Gd 2 O 3 has better electrical properties. -- Abstract: Gd 2 O 3 (0–0.8 wt.%)-doped 0.82Bi 0.5 Na 0.5 TiO 3 –0.18Bi 0.5 K 0.5 TiO 3 (BNKT18) lead-free piezoelectric ceramics were synthesized by a conventional solid-state process. The effects of Gd 2 O 3 on the microstructure, the dielectric, ferroelectric and piezoelectric properties were investigated. X-ray diffraction (XRD) data shows that Gd 2 O 3 in an amount of 0.2–0.8 wt.% can diffuse into the lattice of BNKT18 ceramics and form a pure perovskite phase. Scanning electron microscope (SEM) images indicate that the grain size of BNKT18 ceramics decreases with the increase of Gd 2 O 3 content; in addition, all the modified ceramics have a clear grain boundary and a uniformly distributed grain size. At room temperature, the ferroelectric and piezoelectric properties of the BNKT18 ceramics have been improved with the addition of Gd 2 O 3 , and the BNKT18 ceramics doped with 0.4 wt.% Gd 2 O 3 have the highest piezoelectric constant (d 33 = 137 pC/N), highest relative dielectric constant (ε r = 1023) and lower dissipation factor (tan δ = 0.044) at a frequency of 10 kHz. The BNKT18 ceramics doped with 0.2 wt.% Gd 2 O 3 have the highest planar coupling factor (k p = 0.2463).

  8. Enthalpy of formation of zircon

    International Nuclear Information System (INIS)

    Ellison, A.J.G.; Navrotsky, A.

    1992-01-01

    Using high-temperature solution calorimetry in molt 2PbO · B 2 O 3 , the enthalpy of reaction of the formation of zircon, ZrSiO 4 , from its constituent oxides has been determined: Δ 4 H 977 (ZrSiO 4 ) = -27.9 (±1.9) kJ/mol. With previously reported data for the heat contents of ZrO 2 SiO 2 and ZrSiO 4 and standard-state enthalpies of formation of ZrO 2 and SiO 2 , we obtain Δ f H 298 degrees. (ZrSiO 4 ) = -2034.2 (±3.1) kJ/mol and Δ t G 298 degrees (ZrSiO 4 ) = -1919.8 kJ/mol. The free energy value is in excellent agreement with a range previously estimated from solid-state reaction equilibria. At higher temperature also the data are in close agreement with existing data, though the data sets diverge somewhat with increasing T. In this paper the limitations of the data for predicting the breakdown temperature of zircon into its constituent oxides are discussed

  9. The effects of embedded piezoelectric fiber composite sensors on the structural integrity of glass-fiber–epoxy composite laminate

    International Nuclear Information System (INIS)

    Konka, Hari P; Wahab, M A; Lian, K

    2012-01-01

    Piezoelectric fiber composite sensors (PFCSs) made from micro-sized lead zirconate titanate (PZT) fibers have many advantages over the traditional bulk PZT sensors for embedded sensor applications. PFCSs as embedded sensors will be an ideal choice to continuously monitor the stress/strain levels and health conditions of composite structures. PFCSs are highly flexible, easily embeddable, have high compatibility with composite structures, and also provides manufacturing flexibility. This research is focused on examining the effects of embedding PFCS sensors (macro-fiber composite (MFC) and piezoelectric fiber composite (PFC)) on the structural integrity of glass-fiber–epoxy composite laminates. The strengths of composite materials with embedded PFCSs and conventional PZT sensors were compared, and the advantages of PFCS sensors over PZTs were demonstrated. Initially a numerical simulation study is performed to understand the local stress/strain field near the embedded sensor region inside a composite specimen. High stress concentration regions were observed near the embedded sensor corner edge. Using PFCS leads to a reduction of 56% in longitudinal stress concentration and 38% in transverse stress concentration, when compared to using the conventional PZTs as embedded sensors. In-plane tensile, in-plane tension–tension fatigue, and short beam strength tests are performed to evaluate the strengths/behavior of the composite specimens containing embedded PFCS. From the tensile test it is observed that embedding PFCS and PZT sensors in the composite structures leads to a reduction in ultimate strength by 3 and 6% respectively. From the fatigue test results it is concluded that both embedded PFCS and PZT sensors do not have a significant effect on the fatigue behavior of the composite specimens. From the short beam strength test it is found that embedding PFCS and PZT sensors leads to a reduction in shear strength by 7 and 15% respectively. Overall the pure PZT

  10. The effects of embedded piezoelectric fiber composite sensors on the structural integrity of glass-fiber-epoxy composite laminate

    Science.gov (United States)

    Konka, Hari P.; Wahab, M. A.; Lian, K.

    2012-01-01

    Piezoelectric fiber composite sensors (PFCSs) made from micro-sized lead zirconate titanate (PZT) fibers have many advantages over the traditional bulk PZT sensors for embedded sensor applications. PFCSs as embedded sensors will be an ideal choice to continuously monitor the stress/strain levels and health conditions of composite structures. PFCSs are highly flexible, easily embeddable, have high compatibility with composite structures, and also provides manufacturing flexibility. This research is focused on examining the effects of embedding PFCS sensors (macro-fiber composite (MFC) and piezoelectric fiber composite (PFC)) on the structural integrity of glass-fiber-epoxy composite laminates. The strengths of composite materials with embedded PFCSs and conventional PZT sensors were compared, and the advantages of PFCS sensors over PZTs were demonstrated. Initially a numerical simulation study is performed to understand the local stress/strain field near the embedded sensor region inside a composite specimen. High stress concentration regions were observed near the embedded sensor corner edge. Using PFCS leads to a reduction of 56% in longitudinal stress concentration and 38% in transverse stress concentration, when compared to using the conventional PZTs as embedded sensors. In-plane tensile, in-plane tension-tension fatigue, and short beam strength tests are performed to evaluate the strengths/behavior of the composite specimens containing embedded PFCS. From the tensile test it is observed that embedding PFCS and PZT sensors in the composite structures leads to a reduction in ultimate strength by 3 and 6% respectively. From the fatigue test results it is concluded that both embedded PFCS and PZT sensors do not have a significant effect on the fatigue behavior of the composite specimens. From the short beam strength test it is found that embedding PFCS and PZT sensors leads to a reduction in shear strength by 7 and 15% respectively. Overall the pure PZT sensors

  11. Inflight dissociation of zircon in air plasma

    Energy Technology Data Exchange (ETDEWEB)

    Yugeswaran, S; Selvarajan, V [Bharathiar University, Coimbatore 641046 (India); Ananthapadmanabhan, P V; Thiyagarajan, T K [Laser and Plasma Technology Division, Bhabha Atomic Research Centre, Mumbai - 400 085 (India); Nair, Janardhanan [Ion Arc Technologies Pvt Ltd, Coimbatore (India)

    2010-02-01

    Thermal dissociation of zircon can be conveniently carried out in a plasma reactor, which is characterized by high temperature, high energy density and high quench rate. Zirconia is recovered from this partially dissociated zircon by alkali leaching. Dissociation of zircon has been conventionally carried out in argon gas, which is expensive. The present paper reports experimental results on thermal dissociation of zircon in air plasma medium. Process simulation for 'inflight' dissociation of zircon in air plasma medium is also presented. The experimental system consists of a central hollow graphite electrode, which acts as the cathode and a graphite anode. The material to be processed is fed centrally through the cathode. The unique feature of the system is that it uses air as the working gas to generate the thermal plasma. The system has been used to study in-flight dissociation of zircon in the thermal plasma jet. Dissociation was carried out over 10-25 kW power range. Results of the study indicate that complete dissociation of zircon to ZrO{sub 2} and silica could be accomplished at 25 kW in air plasma.

  12. Inflight dissociation of zircon in air plasma

    International Nuclear Information System (INIS)

    Yugeswaran, S; Selvarajan, V; Ananthapadmanabhan, P V; Thiyagarajan, T K; Nair, Janardhanan

    2010-01-01

    Thermal dissociation of zircon can be conveniently carried out in a plasma reactor, which is characterized by high temperature, high energy density and high quench rate. Zirconia is recovered from this partially dissociated zircon by alkali leaching. Dissociation of zircon has been conventionally carried out in argon gas, which is expensive. The present paper reports experimental results on thermal dissociation of zircon in air plasma medium. Process simulation for 'inflight' dissociation of zircon in air plasma medium is also presented. The experimental system consists of a central hollow graphite electrode, which acts as the cathode and a graphite anode. The material to be processed is fed centrally through the cathode. The unique feature of the system is that it uses air as the working gas to generate the thermal plasma. The system has been used to study in-flight dissociation of zircon in the thermal plasma jet. Dissociation was carried out over 10-25 kW power range. Results of the study indicate that complete dissociation of zircon to ZrO 2 and silica could be accomplished at 25 kW in air plasma.

  13. Effect of composition on electrical properties of lead-free Bi{sub 0.5}(Na{sub 0.80}K{sub 0.20}){sub 0.5}TiO{sub 3}-(Ba{sub 0.98}Nd{sub 0.02})TiO{sub 3} piezoelectric ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Jaita, Pharatree [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Watcharapasorn, Anucha; Jiansirisomboon, Sukanda [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand)

    2013-07-14

    Lead-free piezoelectric ceramics with the composition of (1-x)Bi{sub 0.5}(Na{sub 0.80}K{sub 0.20}){sub 0.5}TiO{sub 3}-x(Ba{sub 0.98}Nd{sub 0.02})TiO{sub 3} or (1-x) BNKT-xBNdT (with x = 0-0.20 mol fraction) have been synthesized by a conventional mixed-oxide method. The compositional dependence of phase structure and electrical properties of the ceramics were systemically studied. The optimum sintering temperature of all BNKT-BNdT ceramics was found to be 1125 Degree-Sign C. X-ray diffraction pattern suggested that BNdT effectively diffused into BNKT lattice during sintering to form a solid solution with a perovskite structure. Scanning electron micrographs showed a slight reduction of grain size when BNdT was added. It was found that BNKT-0.10BNdT ceramic exhibited optimum electrical properties ({epsilon}{sub r} = 1716, tan{delta} = 0.0701, T{sub c} = 327 Degree-Sign C, and d{sub 33} = 211 pC/N), suggesting that this composition has a potential to be one of a promising lead-free piezoelectric candidate for dielectric and piezoelectric applications.

  14. Measurement of effective piezoelectric coefficients of PZT thin films for energy harvesting application with interdigitated electrodes.

    Science.gov (United States)

    Chidambaram, Nachiappan; Mazzalai, Andrea; Muralt, Paul

    2012-08-01

    Interdigitated electrode (IDE) systems with lead zirconate titanate (PZT) thin films play an increasingly important role for two reasons: first, such a configuration generates higher voltages than parallel plate capacitor-type electrode (PPE) structures, and second, the application of an electric field leads to a compressive stress component in addition to the overall stress state, unlike a PPE structure, which results in tensile stress component. Because ceramics tend to crack at relatively moderate tensile stresses, this means that IDEs have a lower risk of cracking than PPEs. For these reasons, IDE systems are ideal for energy harvesting of vibration energy, and for actuators. Systematic investigations of PZT films with IDE systems have not yet been undertaken. In this work, we present results on the evaluation of the in-plane piezoelectric coefficients with IDE systems. Additionally, we also propose a simple and measurable figure of merit (FOM) to analyze and evaluate the relevant piezoelectric parameter for harvesting efficiency without the need to fabricate the energy harvesting device. Idealized effective coefficients e(IDE) and h(IDE) are derived, showing its composite nature with about one-third contribution of the transverse effect, and about two-thirds contribution of the longitudinal effect in the case of a PZT film deposited on a (100)-oriented silicon wafer with the in-plane electric field along one of the Si directions. Randomly oriented 1-μm-thick PZT 53/47 film deposited by a sol-gel technique, was evaluated and yielded an effective coefficient e(IDE) of 15 C·m(-2). Our FOM is the product between effective e and h coefficient representing twice the electrical energy density stored in the piezoelectric film per unit strain deformation (both for IDE and PPE systems). Assuming homogeneous fields between the fingers, and neglecting the contribution from below the electrode fingers, the FOM for IDE structures with larger electrode gap is derived to be

  15. Beneficiation of low grade zircon concentrate

    International Nuclear Information System (INIS)

    Rehim, A.A.

    1976-01-01

    The zircon concentrate obtained from black sands, contains considerable amount of rutile and some ilmenite. It is necessary to separate these minerals before the metallurgical processing of zircon, as otherwise the zirconium products obtained will be contaminated with large amount of titanium. The present work explores the possibility of purification of zircon from rutile and other minerals by flotation. Effective separation can be obtained by selective flotation using oleic acid and liquid glass in alkaline medium or sodium silicon fluoride in weak acidic medium. (author)

  16. Refractory Materials of Zirconate. Part 2: Synthesis and some properties of strontium, zirconate, calcium zirconate and barium zirconate

    Science.gov (United States)

    Okubo, Tsutomo; Yonemochi, Osamu; Nakamura, Kazuo; Maeda, Minoru

    1988-01-01

    Chemical compounds SrZrO3, CaZrO3, and BaZrO3 were synthesized by solid reaction and arc fusion, and their properties examined. Results were as follows: (1) in the synthesis of CaZrO3 by solid reaction, ZrO2 solid solution with cubic form was produced, which then changed into CaZrO3; (2) the BaZrO3 was a cubic form and did not show any transformation, while SrZrO3 and CaZrO3 with an orthorhombic form transformed to a cubic form at high temperature; and (3) the solubility of BaZrO3 in acid and its vaporization rate at a high temperature were greater than those of zirconates.

  17. Computational and Experimental Insight Into Single-Molecule Piezoelectric Materials

    Science.gov (United States)

    Marvin, Christopher Wayne

    Piezoelectric materials allow for the harvesting of ambient waste energy from the environment. Producing lightweight, highly responsive materials is a challenge for this type of material, requiring polymer, foam, or bio-inspired materials. In this dissertation, I explore the origin of the piezoelectric effect in single molecules through density functional theory (DFT), analyze the piezoresponse of bio-inspired peptidic materials through the use of atomic and piezoresponse force microscopy (AFM and PFM), and develop a novel class of materials combining flexible polyurethane foams and non-piezoelectric, polar dopants. For the DFT calculations, functional group, regiochemical, and heteroatom derivatives of [6]helicene were examined for their influence on the piezoelectric response. An aza[6]helicene derivative was found to have a piezoelectric response (108 pm/V) comparable to ceramics such as lead zirconium titanate (200+ pm/V). These computed materials have the possibility to compete with current field-leading piezomaterials such as lead zirconium titanate (PZT), zinc oxide (ZnO), and polyvinylidene difluoride (PVDF) and its derivatives. The use of AFM/PFM allows for the demonstration of the piezoelectric effect of the selfassembled monolayer (SAM) peptidic systems. Through PFM, the influence that the helicity and sequence of the peptide has on the overall response of the molecule can be analyzed. Finally, development of a novel class of piezoelectrics, the foam-based materials, expands the current understanding of the qualities required for a piezoelectric material from ceramic and rigid materials to more flexible, organic materials. Through the exploration of these novel types of piezoelectric materials, new design rules and figures of merit have been developed.

  18. Piezoelectric effects in biomaterials

    International Nuclear Information System (INIS)

    Zimmerman, R.L.

    1976-03-01

    Precision methods have been developed for the simultaneous measurement of the complex piezoelectric stress constants and the electric conduction and polarization currents. Samples of Collagen, keratin, and chitin are prepared and measured in such a way to optimize the determination of the position and orientation of the electric dipole moments. The temperature and the hydration state of the samples are varied during the measurement of the piezoelectric constants in an effort to understand the role of water in biological material. Above 40 0 C, the inherent piezolectricity is enhanced by the water of hydration, in contrast to the more easily understood reduction observed at lower temperatures. Gelatin, which has no inherent piezoelectricity, displays a piezoelectricity proportional to the currents of conduction and polarization. An analysis of the new effect shows that it is a measure of the variation of the resistivity with deformation (d rho/dS - rho) in the same way that the electric field induced piezoelectricity is a measure of the variation of the dielectric constant with deformation (dk/dS + k). Both are sensitive to electric dipole relaxation effects. (Author) [pt

  19. The giant piezoelectric effect: electric field induced monoclinic phase or piezoelectric distortion of the rhombohedral parent?

    CERN Document Server

    Kisi, E H; Forrester, J S; Howard, C J

    2003-01-01

    Lead zinc niobate-lead titanate (PZN-PT) single crystals show very large piezoelectric strains for electric fields applied along the unit cell edges e.g. [001] sub R. It has been widely reported that this effect is caused by an electric field induced phase transition from rhombohedral (R3m) to monoclinic (Cm or Pm) symmetry in an essentially continuous manner. Group theoretical analysis using the computer program ISOTROPY indicates phase transitions between R3m and Cm (or Pm) must be discontinuous under Landau theory. An analysis of the symmetry of a strained unit cell in R3m and a simple expansion of the piezoelectric strain equation indicate that the piezoelectric distortion due to an electric field along a cell edge in rhombohedral perovskite-based ferroelectrics is intrinsically monoclinic (Cm), even for infinitesimal electric fields. PZN-PT crystals have up to nine times the elastic compliance of other piezoelectric perovskites and it might be expected that the piezoelectric strains are also very large. ...

  20. Strong piezoelectricity in single-layer graphene deposited on SiO2 grating substrates.

    Science.gov (United States)

    da Cunha Rodrigues, Gonçalo; Zelenovskiy, Pavel; Romanyuk, Konstantin; Luchkin, Sergey; Kopelevich, Yakov; Kholkin, Andrei

    2015-06-25

    Electromechanical response of materials is a key property for various applications ranging from actuators to sophisticated nanoelectromechanical systems. Here electromechanical properties of the single-layer graphene transferred onto SiO2 calibration grating substrates is studied via piezoresponse force microscopy and confocal Raman spectroscopy. The correlation of mechanical strains in graphene layer with the substrate morphology is established via Raman mapping. Apparent vertical piezoresponse from the single-layer graphene supported by underlying SiO2 structure is observed by piezoresponse force microscopy. The calculated vertical piezocoefficient is about 1.4 nm V(-1), that is, much higher than that of the conventional piezoelectric materials such as lead zirconate titanate and comparable to that of relaxor single crystals. The observed piezoresponse and achieved strain in graphene are associated with the chemical interaction of graphene's carbon atoms with the oxygen from underlying SiO2. The results provide a basis for future applications of graphene layers for sensing, actuating and energy harvesting.

  1. Damage detection monitoring applications in self-healing concrete structures using embedded piezoelectric transducers and recovery

    International Nuclear Information System (INIS)

    Karaiskos, G; Tsangouri, E; Aggelis, D G; Van Hemelrijck, D; Deraemaeker, A

    2015-01-01

    The ageing, operational and ambient loadings have a great impact in the operational and maintenance cost of concrete structures. Their service life prolongation is of utmost importance and this can be efficiently achieved by using reliable and low-cost monitoring and self-healing techniques. In the present study, the ultrasonic pulse velocity (UPV) method using embedded small-size and low-cost piezoelectric PZT (lead zirconate titanate) ceramic transducers in concrete with self-healing properties is implemented for monitoring not only the setting and hardening phases of concrete since casting time, but also for the detection of damage initiation, propagation and recovery of integrity after healing. A couple of small-scale notched unreinforced concrete beams are subjected to mode-I fracture through three-point bending tests. After a 24-hour healing agent curing period, the beams are reloaded using the same loading scenario. The results demonstrate the excellent performance of the proposed monitoring technique during the hydration, damage generation and recovery periods. (paper)

  2. Study of V-OTDR stability for dynamic strain measurement in piezoelectric vibration

    Science.gov (United States)

    Ren, Meiqi; Lu, Ping; Chen, Liang; Bao, Xiaoyi

    2016-09-01

    In a phase-sensitive optical-time domain reflectometry (Φ-OTDR) system, the challenge for dynamic strain measurement lies in large intensity fluctuations from trace to trace. The intensity fluctuation caused by stochastic characteristics of Rayleigh backscattering sets detection limit for the minimum strength of vibration measurement and causes the large measurement uncertainty. Thus, a trace-to-trace correlation coefficient is introduced to quantify intensity fluctuation of Φ-OTDR traces and stability of the sensor system theoretically and experimentally. A novel approach of measuring dynamic strain induced by various driving voltages of lead zirconate titanate (PZT) in Φ-OTDR is also demonstrated. Piezoelectric vibration signals are evaluated through analyzing peak values of fast Fourier transform spectra at the fundamental frequency and high-order harmonics based on Bessel functions. High trace-to-trace correlation coefficients varying from 0.824 to 0.967 among 100 measurements are obtained in experimental results, showing the good stability of our sensor system, as well as small uncertainty of measured peak values.

  3. Displacement and resonance behaviors of a piezoelectric diaphragm driven by a double-sided spiral electrode

    KAUST Repository

    Shen, Zhiyuan

    2012-04-03

    This paper presents the design of a lead zirconate titanate (PZT) diaphragm actuated by double-sided patterned electrodes. Au/Cr electrodes were deposited on bulk PZT wafers by sputtering while patterned by a lift-off process. SU-8 thick film was used to form the structural layer. Double-spiral electrode induced in-plane poling and piezoelectric elongation are converted to an out-of-plane displacement due to the confined boundary condition. The influence of different drive configurations and electrode parameters on deflection has been calculated by finite element methods (FEM) using a uniform field model. Impedance and quasi-static displacement spectra of the diaphragm were measured after poling. Adouble-sided patterned electrode diaphragm can be actuated by more drive configurations than a single-sided one. Compared with a single-sided electrode drive, a double-sided out-of-phase drive configuration increases the coupling coefficient of the fundamental resonance from 7.6% to 11.8%. The displacement response of the diaphragm increases from 2.6 to 8.6nmV 1. Configurations including the electric field component perpendicular to the poling direction can stimulate shear modes of the diaphragm. © 2012 IOP Publishing Ltd.

  4. Piezoelectric paints as one approach to smart structural materials with health-monitoring capabilities

    Science.gov (United States)

    Egusa, Shigenori; Iwasawa, Naozumi

    1998-08-01

    Piezoelectric paints have a potential to change a conventional structural material into an intelligent material system with health-monitoring capabilities such as vibration sensing and damage detection. Such paints were prepared using lead zirconate titanate (PZT) ceramic powder as a pigment and epoxy resin as a binder. The obtained paints were coated on aluminum test specimens, and were cured at room temperature or at 150 0964-1726/7/4/002/img5, thus forming the paint films having different thicknesses of 25-300 0964-1726/7/4/002/img6. These films were then poled at room temperature, and were evaluated with regard to the sensitivities as vibration and acoustic emission sensors in the frequency ranges of 0-250 Hz and 0-1.0 MHz, respectively. This paper mainly describes the effects of the film thickness and the cure temperature on the poling behavior of the PZT/epoxy paint film. This paper describes also the application of the paint film as a vibration modal sensor integrated into a structural material.

  5. Intraoral conversion of occlusal force to electricity and magnetism by biting of piezoelectric elements.

    Science.gov (United States)

    Kameda, Takashi; Ohkuma, Kazuo; Sano, Natsuki; Ogura, Hideo; Terada, Kazuto

    2012-01-01

    Very weak electrical, magnetic and ultrasound signal stimulations are known to promote the formation, metabolism, restoration and stability of bone and surrounding tissues after treatment and operations. We have therefore investigated the possibility of intraoral generation of electricity and magnetism by occlusal force in an in vitro study. Biting bimorph piezoelectric elements with lead zirconate titanate (PZT) using dental models generated appropriate magnetism for bone formation, i. e. 0.5-0.6 gauss, and lower electric currents and higher voltages, i. e. 2.0-6.0 μA at 10-22 V (appropriate levels are 30 μA and 1.25 V), as observed by a universal testing machine. The electric currents and voltages could be changed using amplifier circuits. These results show that intraoral generation of electricity and magnetism is possible and could provide post-operative stabilization and activation of treated areas of bone and the surrounding tissues directly and/or indirectly by electrical, magnetic and ultrasound stimulation, which could accelerate healing.

  6. A fatigue test method for Pb(Zr,Ti)O3 thin films by using MEMS-based self-sensitive piezoelectric microcantilevers

    Science.gov (United States)

    Kobayashi, T.; Maeda, R.; Itoh, T.

    2008-11-01

    In the present study, we propose a new method for the fatigue test of lead zirconate titanate (PZT) thin films for MEMS devices by using self-sensitive piezoelectric microcantilevers developed in our previous study. We have deposited PZT thin films on SOI wafers and fabricated the microcantilevers through the MEMS microfabrication process. In the self-sensitive piezoelectric microcantilevers, the PZT thin films are separated in order to act as an actuator and a sensor. The fatigue characteristic of the PZT thin films can be evaluated by measuring the output voltage of the sensor as a function of time. When a sine wave of 20 Vpp and a dc bias of 10 V were applied to the PZT thin films for an actuator, the output voltage of the sensor fell down after 107 fatigue cycles. We have also investigated the influence of amplitude of the actuation sine wave and dc bias on the fatigue of the PZT thin films by using the proposed fatigue test method.

  7. A fatigue test method for Pb(Zr,Ti)O3 thin films by using MEMS-based self-sensitive piezoelectric microcantilevers

    International Nuclear Information System (INIS)

    Kobayashi, T; Maeda, R; Itoh, T

    2008-01-01

    In the present study, we propose a new method for the fatigue test of lead zirconate titanate (PZT) thin films for MEMS devices by using self-sensitive piezoelectric microcantilevers developed in our previous study. We have deposited PZT thin films on SOI wafers and fabricated the microcantilevers through the MEMS microfabrication process. In the self-sensitive piezoelectric microcantilevers, the PZT thin films are separated in order to act as an actuator and a sensor. The fatigue characteristic of the PZT thin films can be evaluated by measuring the output voltage of the sensor as a function of time. When a sine wave of 20 V pp and a dc bias of 10 V were applied to the PZT thin films for an actuator, the output voltage of the sensor fell down after 10 7 fatigue cycles. We have also investigated the influence of amplitude of the actuation sine wave and dc bias on the fatigue of the PZT thin films by using the proposed fatigue test method

  8. Piezoelectric ceramic (PZT) modulates axonal guidance growth of rat cortical neurons via RhoA, Rac1, and Cdc42 pathways.

    Science.gov (United States)

    Wen, Jianqiang; Liu, Meili

    2014-03-01

    Electrical stimulation is critical for axonal connection, which can stimulate axonal migration and deformation to promote axonal growth in the nervous system. Netrin-1, an axonal guidance cue, can also promote axonal guidance growth, but the molecular mechanism of axonal guidance growth under indirect electric stimulation is still unknown. We investigated the molecular mechanism of axonal guidance growth under piezoelectric ceramic lead zirconate titanate (PZT) stimulation in the primary cultured cortical neurons. PZT induced marked axonal elongation. Moreover, PZT activated the excitatory postsynaptic currents (EPSCs) by increasing the frequency and amplitude of EPSCs of the cortical neurons in patch clamp assay. PZT downregulated the expression of Netrin-1 and its receptor Deleted in Colorectal Cancer (DCC). Rho GTPase signaling is involved in interactions of Netrin-1 and DCC. PZT activated RhoA. Dramatic decrease of Cdc42 and Rac1 was also observed after PZT treatment. RhoA inhibitor Clostridium botulinum C3 exoenzyme (C3-Exo) prevented the PZT-induced downregulation of Netrin-1 and DCC. We suggest that PZT can promote axonal guidance growth by downregulation of Netrin-1 and DCC to mediate axonal repulsive responses via the Rho GTPase signaling pathway. Obviously, piezoelectric materials may provide a new approach for axonal recovery and be beneficial for clinical therapy in the future.

  9. Rate dependent direct inverse hysteresis compensation of piezoelectric micro-actuator used in dual-stage hard disk drive head positioning system.

    Science.gov (United States)

    Rahman, Md Arifur; Al Mamun, Abdullah; Yao, Kui

    2015-08-01

    The head positioning servo system in hard disk drive is implemented nowadays using a dual-stage actuator—the primary stage consisting of a voice coil motor actuator providing long range motion and the secondary stage controlling the position of the read/write head with fine resolution. Piezoelectric micro-actuator made of lead zirconate titanate (PZT) has been a popular choice for the secondary stage. However, PZT micro-actuator exhibits hysteresis—an inherent nonlinear characteristic of piezoelectric material. The advantage expected from using the secondary micro-actuator is somewhat lost by the hysteresis of the micro-actuator that contributes to tracking error. Hysteresis nonlinearity adversely affects the performance and, if not compensated, may cause inaccuracy and oscillation in the response. Compensation of hysteresis is therefore an important aspect for designing head-positioning servo system. This paper presents a new rate dependent model of hysteresis along with rigorous analysis and identification of the model. Parameters of the model are found using particle swarm optimization. Direct inverse of the proposed rate-dependent generalized Prandtl-Ishlinskii model is used as the hysteresis compensator. Effectiveness of the overall solution is underscored through experimental results.

  10. Peritubular dentin lacks piezoelectricity.

    Science.gov (United States)

    Habelitz, S; Rodriguez, B J; Marshall, S J; Marshall, G W; Kalinin, S V; Gruverman, A

    2007-09-01

    Dentin is a mesenchymal tissue, and, as such, is based on a collagenous matrix that is reinforced by apatite mineral. Collagen fibrils show piezoelectricity, a phenomenon that is used by piezoresponse force microscopy (PFM) to obtain high-resolution images. We applied PFM to image human dentin with 10-nm resolution, and to test the hypothesis that zones of piezoactivity, indicating the presence of collagen fibrils, can be distinguished in dentin. Piezoelectricity was observed by PFM in the dentin intertubular matrix, while the peritubular dentin remained without response. High-resolution imaging of chemically treated intertubular dentin attributed the piezoelectric effect to individual collagen fibrils that differed in the signal strength, depending on the fibril orientation. This study supports the hypothesis that peritubular dentin is a non-collagenous tissue and is thus an exception among mineralized tissues that derive from the mesenchyme.

  11. Piezoelectric energy harvesting

    Energy Technology Data Exchange (ETDEWEB)

    Howells, Christopher A [Power Technology Branch, US Army, CERDEC, C2D, Ft. Belvoir, VA 22060-5816 (United States)

    2009-07-15

    Piezoelectric materials can be used to convert oscillatory mechanical energy into electrical energy. This technology, together with innovative mechanical coupling designs, can form the basis for harvesting energy from mechanical motion. Piezoelectric energy can be harvested to convert walking motion from the human body into electrical power. Recently four proof-of-concept Heel Strike Units were developed where each unit is essentially a small electric generator that utilizes piezoelectric elements to convert mechanical motion into electrical power in the form factor of the heel of a boot. The results of the testing and evaluation and the performance of this small electric generator are presented. The generator's conversion of mechanical motion into electrical power, the processes it goes through to produce useable power and commercial applications of the Heel Strike electric generator are discussed. (author)

  12. Piezoelectric wave motor

    Science.gov (United States)

    Yerganian, Simon Scott

    2001-07-17

    A piezoelectric motor having a stator in which piezoelectric elements are contained in slots formed in the stator transverse to the desired wave motion. When an electric field is imposed on the elements, deformation of the elements imposes a force perpendicular to the sides of the slot, deforming the stator. Appropriate frequency and phase shifting of the electric field will produce a wave in the stator and motion in a rotor. In a preferred aspect, the piezoelectric elements are configured so that deformation of the elements in direction of an imposed electric field, generally referred to as the d.sub.33 direction, is utilized to produce wave motion in the stator. In a further aspect, the elements are compressed into the slots so as to minimize tensile stresses on the elements in use.

  13. Piezoelectric energy harvesting

    International Nuclear Information System (INIS)

    Howells, Christopher A

    2009-01-01

    Piezoelectric materials can be used to convert oscillatory mechanical energy into electrical energy. This technology, together with innovative mechanical coupling designs, can form the basis for harvesting energy from mechanical motion. Piezoelectric energy can be harvested to convert walking motion from the human body into electrical power. Recently four proof-of-concept Heel Strike Units were developed where each unit is essentially a small electric generator that utilizes piezoelectric elements to convert mechanical motion into electrical power in the form factor of the heel of a boot. The results of the testing and evaluation and the performance of this small electric generator are presented. The generator's conversion of mechanical motion into electrical power, the processes it goes through to produce useable power and commercial applications of the Heel Strike electric generator are discussed.

  14. Piezoelectricity in polymers

    International Nuclear Information System (INIS)

    Kepler, R.G.; Anderson, R.A.

    1980-01-01

    Piezoelectricity and related properties of polymers are reviewed. After presenting a historical overview of the field, the mathematical basis of piezo- and pyroelectricity is summarized. We show how the experimentally measured quantities are related to the changes in polarization and point out the serious inequlity between direct and converse piezoelectric coefficients in polymers. Theoretical models of the various origins of piezo- and pyroelectricity, which include piezoelectricity due to inhomogeneous material properties and strains, are reviewed. Relaxational effects are also considered. Experimental techniques are examined and the results for different materials are presented. Because of the considerable work in recent years polyimylidene fluoride, this polymer receives the majority of the attention. The numerous applications of piezo-and pyroelectric polymers are mentioned. This article concludes with a discussion of the possible role of piezo- and pyroelectricity in biological system

  15. Piezoelectric Accelerometers Development

    DEFF Research Database (Denmark)

    Liu, Bin; Bang, Lisbet Fogh

    1999-01-01

    The paper describes the development of piezoelectric accelerometers using Finite Element (FE) approach. Brüel & Kjær Accelerometer Type 8325 is chosen as an example to illustrate the advanced accelerometer development procedure. The deviation between simulated results and measured results of Type...... 8325 are below 6%. It is proved that the specifications of the accelerometer can be effectively predicted using the FE method, especially when modifications of the accelerometer are required. The development process of piezoelectric accelerometers in Brüel & Kjær is becoming more efficient...

  16. Piezoelectric accelerometeres development

    DEFF Research Database (Denmark)

    Liu, Bin

    1999-01-01

    The paper describes the development of piezoelectric accelerometers using Finite Element (FE) approach. Brüel & Kjær Accelerometer Type 8325 is chosen as an example to illustrate the advanced accelerometer development procedure. The deviation between simulated results and measured results of Type...... 8325 are below 6%. It is proved that the specifications of the accelerometer can be effectively predicted using the FE method, especially when modifications of the accelerometer are required. The development process of piezoelectric accelerometers in Brüel & Kjær is becoming more efficient....

  17. A theory of piezoelectric laminates

    International Nuclear Information System (INIS)

    Giangreco, E.

    1997-01-01

    A theory of piezoelectric laminates is rationally derived from the three-dimensional Voigt theory of piezoelectricity. The present theory is a generalization to piezoelectric laminates of the Reissner-Mindlin-type layer-wise theory of elastic laminates. Both a differential formulation and a variational formulation of the piezoelectric laminate problem are presented. The proposed theory is adopted in the analysis of simple problems, in order to verify its effectiveness. The results it provides turn out to be in good agreement with the results supplied by the Voigt theory of piezoelectricity

  18. Induced piezoelectricity in isotropic biomaterial.

    Science.gov (United States)

    Zimmerman, R L

    1976-01-01

    Isotropic material can be made to exhibit piezoelectric effects by the application of a constant electric field. For insulators, the piezoelectric strain constant is proportional to the applied electric field and for semiconductors, an additional out-of-phase component of piezoelectricity is proportional to the electric current density in the sample. The two induced coefficients are proportional to the strain-dependent dielectric constant (depsilon/dS + epsilon) and resistivity (drho/dS - rho), respectively. The latter is more important at frequencies such that rhoepsilonomega less than 1, often the case in biopolymers.Signals from induced piezoelectricity in nature may be larger than those from true piezoelectricity. PMID:990389

  19. Strong piezoelectricity in (1 - x)(K0.4Na0.6)(Nb0.96Sb0.04)O3-xBi0.5K0.5Zr1-ySnyO3 lead-free binary system: identification and role of multiphase coexistence.

    Science.gov (United States)

    Zheng, Ting; Wu, Jiagang; Xiao, Dingquan; Zhu, Jianguo; Wang, Xiangjian; Xin, Lipeng; Lou, Xiaojie

    2015-03-18

    Here we report a strong piezoelectric activity in (1 - x)(K0.4Na0.6)(Nb0.96Sb0.04)O3-xBi0.5K0.5Zr1-ySnyO3 lead-free ceramics by designing different phase boundaries. The phase boundaries concerning rhombohedral-orthorhombic-tetragonal (R-O-T) and rhombohedral-tetragonal (R-T) multiphase coexistence were attained by changing BKZS and Sn contents and then were identified by the X-ray diffraction patterns as well as temperature-dependent permittivity and ν1 Raman modes associated with BO6 perovskite octahedron. A high strain (strain = 0.21-0.28% and d33* = 707-880 pm/V) and a strong piezoelectric coefficient (d33 = 415-460 pC/N) were shown in the ceramics located at the multiphase coexistence region. The reported results of this work are superior to that (d33* ∼ 570 pm/V and d33 ∼ 416 pC/N) of the textured (K,Na,Li)(Nb,Ta,Sb)O3 ceramics [Nature 2004, 432, 84]. We believe that the material system of this work will become one of the most promising candidates for piezoelectric actuators.

  20. Effects of MnO{sub 2} doping on structure, dielectric and piezoelectric properties of 0.825NaNbO{sub 3}-0.175Ba{sub 0.6}(Bi{sub 0.5}K{sub 0.5}){sub 0.4}TiO{sub 3} lead-free ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Fan, Ximing; Lin, Dunmin; Zheng, Qiaoji; Sun, Hailing; Wan, Yang; Wu, Xiaochun [College of Chemistry and Materials Science, and Visual Computing and Virtual Reality Key Laboratory of Sichuan Province, Sichuan Normal University, Chengdu 610066 (China); Wu, Lang [State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials, Southwest University of Science and Technology, Mianyang 621010 (China)

    2012-12-15

    Lead-free ceramics 0.825NaNbO{sub 3}-0.175Ba{sub 0.6}(Bi{sub 0.5}K{sub 0.5}){sub 0.4}TiO{sub 3} + xmol% MnO{sub 2} were prepared by an ordinary sintering technique and the effects of MnO{sub 2} doping on the structure, dielectric, and piezoelectric properties of the ceramics were studied. The ceramics with perovskite structure are transformed from tetragonal to pseudocubic phases by increasing the doping level of MnO{sub 2}. After the addition of MnO{sub 2}, the Curie temperature T{sub C} of the ceramics decreases and the ferroelectric-paraelectric phase transition at T{sub C} becomes more diffusive. Because of the donor and acceptor doping effects of Mn ions simultaneously, the piezoelectric constant d{sub 33}, electromechanical coupling coefficient k{sub p}, relative permittivity {epsilon}{sub r}, and mechanical quality factor Q{sub m} are enhanced considerably after the addition of 1 mol% MnO{sub 2}. The ceramic with 1 mol% MnO{sub 2} doping possesses the optimum piezoelectricity (d{sub 33} = 131 pC/N and k{sub p} = 21.8%) and relatively high Q{sub m} = 627. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  1. Subperiosteal preparation using a new piezoelectric device: a histological examination

    OpenAIRE

    Stoetzer, Marcus; Magel, Anja; Kampmann, Andreas; Lemound, Juliana; Gellrich, Nils-Claudius; von See, Constantin

    2014-01-01

    Introduction: Subperiosteal preparation using a periosteal elevator leads to disturbances of local immunohistochemistry and periosteal histology due to a microtrauma. Usually soft-tissue damage can be considerably reduced by using piezoelectric technology. For this reason, the effects of a novel piezoelectric device on immunohistochemistry and periosteal histology were examined and compared to conventional preparation of the periosteum using a periosteal elevator.Material and methods: Lewis...

  2. Effect of pressure on Zircon's (ZrSiO4) Raman active modes: a first-principles study

    Science.gov (United States)

    Sheremetyeva, Natalya; Cherniak, Daniele; Watson, Bruce; Meunier, Vincent

    Zircon is a mineral commonly found in the Earth crust. Its remarkable properties have given rise to considerable attention. This includes possible inclusion of radioactive elements in natural samples, which allows for geochronological investigations. Subsequently, Zircon was proposed as possible host material for radioactive waste management. Internal radiation damage in zircon leads to the destruction of its crystal structure (an effect known as metamictization) which is subject to ongoing research. Recently, the effect of pressure and temperature on synthetic zircon has been analyzed experimentally using Raman spectroscopy which led to the calibration of zircon as a pressure sensor in diamond-anvil cell experiments. While there have been a number of theoretical studies, the effect of pressure on the Raman active modes of zircon has not been investigated theoretically. Here we present a first-principles pressure calibration of the Raman active modes in Zircon employing density-functional theory (DFT). We find excellent quantitative agreement of the slopes ∂ω / ∂P with the experimental ones and are able to rationalize the ω vs. P behavior based on the details of the vibrational modes.

  3. Determination of temperature dependency of material parameters for lead-free alkali niobate piezoceramics by the inverse method

    Directory of Open Access Journals (Sweden)

    K. Ogo

    2016-06-01

    Full Text Available Sodium potassium niobate (NKN piezoceramics have been paid much attention as lead-free piezoelectric materials in high temperature devices because of their high Curie temperature. The temperature dependency of their material parameters, however, has not been determined in detail up to now. For this purpose, we exploit the so-called Inverse Method denoting a simulation-based characterization approach. Compared with other characterization methods, the Inverse Method requires only one sample shape of the piezoceramic material and has further decisive advantages. The identification of material parameters showed that NKN is mechanically softer in shear direction compared with lead zirconate titanate (PZT at room temperature. The temperature dependency of the material parameters of NKN was evaluated in the temperature range from 30 °C to 150 °C. As a result, we figured out that dielectric constants and piezoelectric constants show a monotonous and isotropic increment with increasing temperature. On the other hand, elastic stiffness constant c 44 E of NKN significantly decreased in contrast to other elastic stiffness constants. It could be revealed that the decrement of c 44 E is associated with an orthorhombic-tetragonal phase transition. Furthermore, ratio of elastic compliance constants s 44 E / s 33 E exhibited similar temperature dependent behavior to the ratio of piezoelectric constants d15/d33. It is suspected that mechanical softness in shear direction is one origin of the large piezoelectric shear mode of NKN. Our results show that NKN are suitable for high temperature devices, and that the Inverse Method should be a helpful approach to characterize material parameters under their practical operating conditions for NKN.

  4. Dielectric and piezoelectric properties of neodymium oxide doped ...

    Indian Academy of Sciences (India)

    Unknown

    Abstract. The dielectric and electromechanical properties of lead zirconate titanate [Pb(Zr, Ti)O3] ceramic added with neodymium oxide have been systematically studied employing the vector impedance spectroscopic. (VIS) technique. The specimens were prepared using the mixed oxide route by adding different mol% of.

  5. Auxetic piezoelectric energy harvesters for increased electric power output

    Directory of Open Access Journals (Sweden)

    Qiang Li

    2017-01-01

    Full Text Available This letter presents a piezoelectric bimorph with auxetic (negative Poisson’s ratio behaviors for increased power output in vibration energy harvesting. The piezoelectric bimorph comprises a 2D auxetic substrate sandwiched between two piezoelectric layers. The auxetic substrate is capable of introducing auxetic behaviors and thus increasing the transverse stress in the piezoelectric layers when the bimorph is subjected to a longitudinal stretching load. As a result, both 31- and 32-modes are simultaneously exploited to generate electric power, leading to an increased power output. The increasing power output principle was theoretically analyzed and verified by finite element (FE modelling. The FE modelling results showed that the auxetic substrate can increase the transverse stress of a bimorph by 16.7 times. The average power generated by the auxetic bimorph is 2.76 times of that generated by a conventional bimorph.

  6. Detrital Zircons Split Sibumasu in East Gondwana

    Science.gov (United States)

    Zhang, X.; Chung, S. L.

    2017-12-01

    It is widely accepted that Sibumasu developed as a united terrane and originated from NW Australian margin in East Gondwana. Here we report new detrital zircon U-Pb-Hf isotopic data from Sumatra that, in combination with literature data, challenge and refute the above long-held view. In particular, the East and West Sumatra terranes share nearly identical Precambrian to Paleozoic detrital zircon age distributions and Hf isotopes, indicating a common provenance/origin for them. The Sumatra detrital zircons exhibit a prominent population of ca. 1170-1070 Ma, indistinguishable from those of the Lhasa and West Burma terranes, with detritus most probably sourcing from western Australia. By contrast, Sibuma (Sibumasu excluding Sumatra) detrital zircons display a prevailing population of ca. 980-935 Ma, strongly resembling those of the western Qiangtang terrane, with detrital materials most likely derived from Greater India and Himalayas. Such markedly distinct detrital zircon age profiles between Sumatra and Sibuma require disparate sources/origin for them, provoking disintegration of the widely-adopted, but outdated, term Sibumasu and thus inviting a new configuration of East Gondwana in the early Paleozoic, with Sumatra and West Burma lying outboard the Lhasa terrane in the NW Australian margin and Sibuma situated in the northern Greater Indian margin. More future investigations are needed to establish the precise rifting and drifting histories of Sumatra and Sibuma, as two separated terranes, during the breakup of Gondwana.

  7. U-Pb dating by zircon dissolution method using chemical abrasion

    Energy Technology Data Exchange (ETDEWEB)

    Takehara, Lucy, E-mail: lucytakehara@gmail.com.br [Servico Geologico do Brasil (CPRM), Brasilia, DF (Brazil); Chemale Junior, Farid [Universidade de Brasilia (UnB), Brasilia, DF (Brazil). Inst. de Geociencias. Lab. de Geocronologia; Hartmann, Leo A. [Universidade Federal do Rio Grande do Sul (UFRS), Porto Alegre, RS (Brazil). Inst. de Geociencias; Dussin, Ivo A.; Kawashita, Koji [Universidade de Sao Paulo (USP), SP, (Brazil). Centro de Pesquisa Geocronologicas

    2012-06-15

    Chemical abrasion was carried out on zircons grains of the Temora II standard for U-Pb dating prior to analyses using in situ Laser Ablation-Multi Collector Ion Coupled Plasma Mass Spectrometer (LA-ICPMS) followed by the Isotope Dissolution Thermal Ionization Mass Spectrometer (ID-TIMS) method. The proposed methodology was herein applied in order to reduce primarily the effects of secondary Pb loss, the presence of common lead and/or silicate impurities. Nine Temora II zircon grains were analyzed by the laser ablation method yielding an age of 418.3 +- 4.3 Ma. Zircon grains of a same population were separated for chemical abrasion before dissolution and mass spectrometry analyses. Six fractions of them were separated for isotope dissolution using {sup 235}U-{sup 205}Pb mixed spike after we have checked and assured the laboratory conditions of low blank values for total Pb of less than 2 pg/g. The obtained U-Pb zircon age by the ID-TIMS method was 415.7 +- 1.8 Ma (error 0.43 %) based on four successful determinations. The results are consistent with the published ages for the Temora diorite (Temora I - 416.75 +- 1.3 Ma; Temora II - 416.78 +- 0.33 Ma) and established as 416 +- 0.33 Ma. The technique is thus recommended for high precision U-Pb zircon analyses (error < 1 %), mainly for high resolution stratigraphic studies of Phanerozoic sequences. (author)

  8. Applied and theoretical study of textural and structural evolution of pure and doped zircon powders

    International Nuclear Information System (INIS)

    Methivier, A.

    1992-02-01

    Using different preparation methods, undoped zircon constituted of quadratic and monoclinic phases, and quadratic phase zircon doped with lanthanum, magnesium or silicon were obtained and characterized. An applied kinetic study of the influence of the gaseous phase, and of the doping on pre-sintering shows an accelerating effect of water vapour, an important stabilization effect of lanthanum or silicon additions and a little effect of magnesium additions. This kinetic study leads to a model giving two parallel types of matter transport: one using water vapour catalytic effect, and the other oxygen diffusion

  9. Non linear effects in piezoelectric materials

    Directory of Open Access Journals (Sweden)

    Gonnard, P.

    2002-02-01

    Full Text Available The static and dynamic non-linear behaviours of a soft and a hard zirconate titanate composition are investigated in this paper as a function of electrical and mechanical fields. The calculated Rayleigh coefficients show that they are similar for the permittivity ε T33 and the piezoelectric constant and nul for the voltage constant d33 and the compliance at zero D (D = dielectric displacement. A non-linear electromechanical equivalent circuit is built up with components proportional to D. Finally an extended model to non-Rayleigh type behaviours is proposed.

    Los comportamientos no lineales estáticos y dinámicos de composiciones blandas y duras de titanato circonato de plomo se investigan en este trabajo en función de campos eléctricos y mecánicos. Los coeficientes de Rayleigh calculados son similares para la permitividad εT33 y la constantes piezoléctrica d33 y nulos para la constante g33 y la complianza a D cero (D=desplazamiento dieléctrico. Se construye un circuito electromecánico no lineal equivalente con componentes proporcionales a D. Finalmente se propone un modelo extendido a comportamientos de tipo no-Rayleigh.

  10. Effect of ZnO-B{sub 2}O{sub 3} addition on the dielectric and the piezoelectric properties of lead-free (Na{sub 0.525}K{sub 0.443}Li{sub 0.037})(Nb{sub 0.883}Sb{sub 0.08}Ta{sub 0.037})O{sub 3} ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Kim, You-Seok; Yoo, Ju-Hyun [Semyung University, Jecheon (Korea, Republic of)

    2014-12-15

    (Na{sub 0.525}K{sub 0.443}Li{sub 0.037})(Nb{sub 0.883}Sb{sub 0.08}Ta{sub 0.037})O{sub 3} + x wt% ZnO-B{sub 2}O{sub 3} (NKLNST + x ZnO-B{sub 2}O{sub 3}) lead-free piezoelectric ceramics were prepared via a conventional solid-state reaction for various values of x = 0, 0.3, 0.6, 0.9, 1.2; then, the dielectric and the piezoelectric properties of these ceramics were investigated. A pure perovskite structure and a small secondary phase were observed in the X-ray diffraction patterns. For the 0.3-wt% ZnO-B{sub 2}O{sub 3} specimen, a density of ρ = 4.537 g/cm{sup 3}, an electromechanical coupling factor of k{sub P} = 0.432, a mechanical quality factor of Q{sub m} = 96, and piezoelectric constant of d{sub 33} = 209 pC/N were found to be optimal. These results indicate that the material with this composition is a promising candidate for use in a lead-free piezoelectric device.

  11. Piezoelectric Transformers: An Historical Review

    OpenAIRE

    Alfredo Vazquez Carazo

    2016-01-01

    Piezoelectric transformers (PTs) are solid-state devices that transform electrical energy into electrical energy by means of a mechanical vibration. These devices are manufactured using piezoelectric materials that are driven at resonance. With appropriate design and circuitry, it is possible to step up and step down the voltages between the input and output sections of the piezoelectric transformer, without making use of magnetic materials and obtaining excellent conversion efficiencies. The...

  12. High Temperature Piezoelectric Drill

    Science.gov (United States)

    Bao, Xiaoqi; Bar-Cohen, Yoseph; Sherrit, Stewart; Badescu, Mircea; Shrout, Tom

    2012-01-01

    Venus is one of the planets in the solar systems that are considered for potential future exploration missions. It has extreme environment where the average temperature is 460 deg C and its ambient pressure is about 90 atm. Since the existing actuation technology cannot maintain functionality under the harsh conditions of Venus, it is a challenge to perform sampling and other tasks that require the use of moving parts. Specifically, the currently available electromagnetic actuators are limited in their ability to produce sufficiently high stroke, torque, or force. In contrast, advances in developing electro-mechanical materials (such as piezoelectric and electrostrictive) have enabled potential actuation capabilities that can be used to support such missions. Taking advantage of these materials, we developed a piezoelectric actuated drill that operates at the temperature range up to 500 deg C and the mechanism is based on the Ultrasonic/Sonic Drill/Corer (USDC) configuration. The detailed results of our study are presented in this paper

  13. Black branes as piezoelectrics.

    Science.gov (United States)

    Armas, Jay; Gath, Jakob; Obers, Niels A

    2012-12-14

    We find a realization of linear electroelasticity theory in gravitational physics by uncovering a new response coefficient of charged black branes, exhibiting their piezoelectric behavior. Taking charged dilatonic black strings as an example and using the blackfold approach we measure their elastic and piezolectric moduli. We also use our results to draw predictions about the equilibrium condition of charged dilatonic black rings in dimensions higher than six.

  14. Biodegradable Piezoelectric Force Sensor.

    Science.gov (United States)

    Curry, Eli J; Ke, Kai; Chorsi, Meysam T; Wrobel, Kinga S; Miller, Albert N; Patel, Avi; Kim, Insoo; Feng, Jianlin; Yue, Lixia; Wu, Qian; Kuo, Chia-Ling; Lo, Kevin W-H; Laurencin, Cato T; Ilies, Horea; Purohit, Prashant K; Nguyen, Thanh D

    2018-01-30

    Measuring vital physiological pressures is important for monitoring health status, preventing the buildup of dangerous internal forces in impaired organs, and enabling novel approaches of using mechanical stimulation for tissue regeneration. Pressure sensors are often required to be implanted and directly integrated with native soft biological systems. Therefore, the devices should be flexible and at the same time biodegradable to avoid invasive removal surgery that can damage directly interfaced tissues. Despite recent achievements in degradable electronic devices, there is still a tremendous need to develop a force sensor which only relies on safe medical materials and requires no complex fabrication process to provide accurate information on important biophysiological forces. Here, we present a strategy for material processing, electromechanical analysis, device fabrication, and assessment of a piezoelectric Poly-l-lactide (PLLA) polymer to create a biodegradable, biocompatible piezoelectric force sensor, which only employs medical materials used commonly in Food and Drug Administration-approved implants, for the monitoring of biological forces. We show the sensor can precisely measure pressures in a wide range of 0-18 kPa and sustain a reliable performance for a period of 4 d in an aqueous environment. We also demonstrate this PLLA piezoelectric sensor can be implanted inside the abdominal cavity of a mouse to monitor the pressure of diaphragmatic contraction. This piezoelectric sensor offers an appealing alternative to present biodegradable electronic devices for the monitoring of intraorgan pressures. The sensor can be integrated with tissues and organs, forming self-sensing bionic systems to enable many exciting applications in regenerative medicine, drug delivery, and medical devices.

  15. Density variation and piezoelectric properties of Ba(Ti1−xSnx)O3 ...

    Indian Academy of Sciences (India)

    diffraction method showed single phase perovskite structure. The density ... piezoelectric ceramics to replace toxic lead based materi- als. Among several groups ... electric field dependence of the material which leads to dif- ficulty in controlling ...

  16. Fission track dating of kimberlitic zircons

    International Nuclear Information System (INIS)

    Haggerty, S.E.

    1983-01-01

    The only reliable method for dating kimberlites at present is the lengthy and specialized hydrothermal procedure that extracts 206 Pb and 238 U from low-uranium zircons. This paper describes a second successful method by fission track dating of large single-crystal zircons, 1.0-1.5 cm in dimension. The use of large crystals overcomes the limitations imposed in conventional fission track analysis which utilizes crushed fragments. Low track densities, optical track dispersion, and the random orientation of polished surfaces in the etch and irradiation cycle are effectively overcome. Fission track ages of zircons from five African kimberlites are reported, from the Kimberley Pool (90.0 +- 6.5 m.y.), Orapa (87.4 +- 5.7 and 92.4 +- 6.1 m.y.), Nzega (51.1 +- 3.8 m.y.), Koffiefontein (90.9 +- 8.2 m.y.), and Val do Queve (133.4 +- 11.5 m.y.). In addition we report the first radiometric ages (707.9 +- 59.6 and 705.5 +- 61.0 m.y.) of crustal zircons from kimberlites in northwest Liberia. The fission track ages agree well with earlier age estimates. Most of the zircons examined in this study are zoned with respect to uranium but linear correlations are established (by regression analysis) between zones of variable uranium content, and within zones of constant uranium content (by analysis of variance). Concordance between the fission track method and the U/Pb technique is established and we concluded that track fading from thermal annealing has not taken place. Kimberlitic zircons dated in this study, therefore, record the time of eruption. (orig.)

  17. Micromechanics approach to the magnetoelectric properties of laminate and fibrous piezoelectric/magnetostrictive composites

    International Nuclear Information System (INIS)

    Huang Haitao; Zhou, L.M.

    2004-01-01

    We use a micromechanics approach to study the magnetoelectric (ME) properties of the piezoelectric/magnetostrictive composite with a 2-2 laminate structure and a 3-1 fibrous structure. It is found that the 3-1 composite has a higher ME coefficient than the 2-2 one, if the volume ratio of piezoelectric material is the same. The reason is that the 3-1 fibrous composite makes use of the longitudinal piezoelectric response and the piezoelectric voltage constant g 33 is 2-3 times that of g 31 . Generally, a smaller volume ratio of the piezoelectric material will generate a higher ME response. The tensile stress at the piezoelectric/magnetostrictive interface of the 3-1 fibrous composite, however, could be high enough to induce plastic deformation or microcracks, which leads to a ME coefficient lower than the theoretically predicted one

  18. U-Pb dating of zircons from the Modra Massif granodiorite of the Low Carpathians and from porphyroid of the Lower Paleozolic of the Spis-Gemer ore Mountains (Western Carpathians)

    International Nuclear Information System (INIS)

    Shcherbak, N.P.; Bartitskij, E.N.; Mitskevitch, N.Yu.; Stepanyuk, L.M.

    1988-01-01

    The method of radioisotope dating based on the ratio of uranium isotopes and lead isotopes was used to date certain rocks and zircon which they contain in the area of the Low Carpathians and the Spis-Gemer ore mountains. Zircon separated from tonalite is ca 320 million years old, zircon from porphyroid about 403 million years old. The obtained data serve to clarify the geological development of the studied area. (M.D.). 2 figs., 2 tabs., 17 refs

  19. Finding the "true" age: ways to read high-precision U-Pb zircon dates

    Science.gov (United States)

    Schaltegger, U.; Schoene, B.; Ovtcharova, M.; Sell, B. K.; Broderick, C. A.; Wotzlaw, J.

    2011-12-01

    Refined U-Pb dating techniques, applying an empirical chemical abrasion treatment prior to analysis [1], and using a precisely calibrated double isotope Pb, U EARTHTIME tracer solution, have led to an unprecedented two problems: (A) Post-crystallization Pb loss from decay damaged areas is considered to be mitigated by applying chemical abrasion techniques. The success of such treatment can, however, not be assumed a priori. The following examples demonstrate that youngest zircons are not biased by lead loss but represent close-to-youngest zircon growth: (i) coincidence of youngest zircon dates with co-magmatic titanite in tonalite; (ii) coincidence with statistically equivalent clusters of 206Pb/238U dates from zircon in residual melts of cogenetic mafic magmas; (iii) youngest zircons in ash beds of sedimentary sequences do not violate the stratigraphic superposition, whereas conventional statistical interpretation (mean or median values) does; (iv) results of published inter-laboratory cross-calibration tests using chemical abrasion on natural zircon crystals of the same sample arrive at the same 206Pb/238U result within case of single, significantly younger dates (>3 sigma), and are common in many pre-Triassic and hydrothermally altered rocks. (B) Pre-eruptive/pre-intrusive growth is found to be the main reason for scattered zircon ages in igneous rocks. Zircons crystallizing from the final magma batch are called autocrystic [3]. Autocrystic growth will happen in a moving or stagnant magma shortly before or after the rheological lockup by the crystals. Last crystallizing zircons in the interstitial melt may therefore postdate emplacement of the magma. The range of 206Pb/238U ages may yield a time frame for the cooling of a given magma batch, which could be added to quantitative thermal models of magma emplacement and cooling. Hf isotopes and trace elements of the dated zircon are used to trace the nature of the dated grains [4], specifically for identification of

  20. Piezoelectric properties of lead-free submicron-structured (Bi0.5Na0.5)0.94Ba0.06TiO3 ceramics from nanopowders

    International Nuclear Information System (INIS)

    Pardo, Lorena; García, Alvaro; Brebøl, Klaus; Mercadelli, Elisa; Galassi, Carmen

    2010-01-01

    Submicron-structured (Bi 0.5 Na 0.5 ) 0.94 Ba 0.06 TiO 3 (BNBT6) ceramics were obtained from nanometric powder synthesized by sol–gel auto-combustion at 500 °C. Hot-pressing at low temperatures and a combination of this with recrystallization, still moderate in order to reduce the loss of volatile elements, have been tested. Material properties, including all losses, were determined at the resonances of thin discs using Alemany et al software. Ceramics hot-pressed at 700–800 °C for 2 h have a pseudo-cubic structure, a grain size of a few hundred nanometers and are homogeneous. Both their crystal structure and the lack of sintering prevent their poling. For ceramics hot-pressed at 950 °C for 3 h, Bi or Bi 0.5 Na 0.5 loss, together with low piezoelectric properties (d 33 = 60 pC N −1 , k p = 8.3% and k t = 9.5%), was observed. Recrystallization at 1000 °C-1 h of ceramics hot-pressed at 700 and 800 °C for 2 h keeps the submicron structure, reduces porosity and prevents off-stoichiometry. Mechanical and piezoelectric losses are also reduced and coupling factors increased (k p = 24.6%, k t = 36.4%). The best piezoelectric coefficient obtained in these ceramics (d 33 = 143 pC N −1 ) is comparable with those reported for coarse-grained ceramics

  1. Piezoelectric Nanotube Array for Broadband High-Frequency Ultrasonic Transducer.

    Science.gov (United States)

    Liew, Weng Heng; Yao, Kui; Chen, Shuting; Tay, Francis Eng Hock

    2018-03-01

    Piezoelectric materials are vital in determining ultrasonic transducer and imaging performance as they offer the function for conversion between mechanical and electrical energy. Ultrasonic transducers with high-frequency operation suffer from performance degradation and fabrication difficulty of the demanded piezoelectric materials. Hence, we propose 1-D polymeric piezoelectric nanostructure with controlled nanoscale features to overcome the technical limitations of high-frequency ultrasonic transducers. For the first time, we demonstrate the integration of a well-aligned piezoelectric nanotube array to produce a high-frequency ultrasonic transducer with outstanding performance. We find that nanoconfinement-induced polarization orientation and unique nanotube structure lead to significantly improved piezoelectric and ultrasonic transducing performance over the conventional piezoelectric thin film. A large bandwidth, 126% (-6 dB), is achieved at high center frequency, 108 MHz. Transmission sensitivity of nanotube array is found to be 46% higher than that of the monolithic thin film transducer attributed to the improved electromechanical coupling effectiveness and impedance match. We further demonstrate high-resolution scanning, ultrasonic imaging, and photoacoustic imaging using the obtained nanotube array transducers, which is valuable for biomedical imaging applications in the future.

  2. Raman study of lead zirconate titanate under uniaxial stress

    International Nuclear Information System (INIS)

    Tallant, David R.; Simpson, Regina L.; Grazier, J. Mark; Zeuch, David H.; Olson, Walter R.; Tuttle, Bruce A.

    2000-01-01

    The authors used micro-Raman spectroscopy to monitor the ferroelectric (FE) to antiferroelectric (AFE) phase transition in PZT ceramic bars during the application of uniaxial stress. They designed and constructed a simple loading device, which can apply sufficient uniaxial force to transform reasonably large ceramic bars while being small enough to fit on the mechanical stage of the microscope used for Raman analysis. Raman spectra of individual grains in ceramic PZT bars were obtained as the stress on the bar was increased in increments. At the same time gauges attached to the PZT bar recorded axial and lateral strains induced by the applied stress. The Raman spectra were used to calculate an FE coordinate, which is related to the fraction of FE phase present. The authors present data showing changes in the FE coordinates of individual PZT grains and correlate these changes to stress-strain data, which plot the macroscopic evolution of the FE-to-AFE transformation. Their data indicates that the FE-to-AFE transformation does not occur simultaneously for all PZT grains but that grains react individually to local conditions

  3. Multiple soft-mode vibrations of lead zirconate

    Czech Academy of Sciences Publication Activity Database

    Hlinka, Jiří; Ostapchuk, Tetyana; Buixaderas, Elena; Kadlec, Christelle; Kužel, Petr; Gregora, Ivan; Kroupa, Jan; Savinov, Maxim; Klíč, Antonín; Drahokoupil, Jan; Etxebarria, I.; Dec, J.

    2014-01-01

    Roč. 112, č. 19 (2014), "197601-1"-"197601-5" ISSN 0031-9007 R&D Projects: GA ČR GA13-15110S Institutional support: RVO:68378271 Keywords : antiferroelectric * soft mode * polarized spectra Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 7.512, year: 2014

  4. Mechanism of electric fatigue crack growth in lead zirconate titanate

    International Nuclear Information System (INIS)

    Westram, Ilona; Oates, William S.; Lupascu, Doru C.; Roedel, Juergen; Lynch, Christopher S.

    2007-01-01

    A series of experiments was performed with through-thickness cracks in ferroelectric double cantilever beam (DCB) specimens. Cyclic electric fields of different amplitudes were applied which resulted in cyclic crack propagation perpendicular to the electric field direction. Crack propagation was observed optically and three regimes were identified: a pop-in from a notch, steady-state crack growth and a decrease of the crack growth rate with increasing cycle number. Crack growth only occurred if the applied field exceeded the coercive field strength of the material. Furthermore, the crack extended during each field reversal and the crack growth rate increased with increasing field. Based on the experimental observations, a mechanistic understanding was developed and contrasted with a nonlinear finite element analysis which quantified the stress intensity in the DCB specimens. The driving forces for crack formation at the notch and subsequent fatigue crack growth were computed based on the distribution of residual stresses due to ferroelectric switching. The finite element results are in good agreement with the experimental observations and support the proposed mechanism

  5. Ionic and electronic conductivity in lead-zirconate-titanate (PZT)

    NARCIS (Netherlands)

    Boukamp, Bernard A.; Pham thi ngoc mai, P.T.N.M.; Blank, David H.A.; Bouwmeester, Henricus J.M.

    2004-01-01

    Accurate impedance measurements on differently sized samples of lead–zirconate–titanate (PbZr0.53Ti0.47O3, PZT) have been analyzed with a CNLS procedure, resulting in the separation of the ionic and electronic conductivities over a temperature range from f150 to 630 jC. At 603 jC the electronic

  6. Calculations for Piezoelectric Ultrasonic Transducers

    DEFF Research Database (Denmark)

    Jensen, Henrik

    1986-01-01

    Analysis of piezoelectric ultrasonic transducers implies a solution of a boundary value problem, for a boay which consists of different materials, including a piezoelectric part. The problem is dynamic at frequencies, where a typical wavelength is somewhat less than the size of the body. Radiation...

  7. A review of the structure-property relationships in lead-free piezoelectric (1−x)Na{sub 0.5}Bi{sub 0.5}TiO{sub 3}–(x)BaTiO{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    McQuade, Ryan R.; Dolgos, Michelle R., E-mail: Michelle.Dolgos@oregonstate.edu

    2016-10-15

    Piezoelectric materials are increasingly being investigated for energy harvesting applications where (1−x)Na{sub 0.5}Bi{sub 0.5}TiO{sub 3}–(x)BaTiO{sub 3} (NBT-BT) is an important lead-free piezoelectric material with potential to be used as an actuator in energy harvesting devices. Much effort has been put into modifying NBT-BT to tune the properties for specific applications, but there is currently no consensus regarding the structure-property relationships in this material, making targeted, rational design a major challenge. In this review, we will summarize the current body of knowledge of NBT-BT and discuss contradicting studies, unresolved problems, and future directions in the field. - Graphical abstract: This review of (1−x)Na{sub 0.5}Bi{sub 0.5}TiO{sub 3}–(x)BaTiO{sub 3} (NBT-BT) summarizes the large body of literature regarding the structure-property relationships of this complex material. We highlight structural studies of the average and local structures of both unpoled and poled samples of NBT-BT at its morphotropic phase boundary and discuss them in context of the observed piezoelectric properties. - Highlights: • Local and average structure of NBT-BT at morphotropic phase boundary is reviewed. • Average structure of poled and unpoled samples of NBT-BT is discussed. • Structure-property relationships in NBT-BT and future directions are summarized.

  8. Geochemical fingerprints and pebbles zircon geochronology

    Indian Academy of Sciences (India)

    Home; Journals; Journal of Earth System Science; Volume 125; Issue 7. Geochemical fingerprints and pebbles zircon geochronology: Implications for the provenance and tectonic setting of Lower Cretaceous sediments in the Zhucheng Basin (Jiaodong peninsula, North China). Jin-Long Ni Jun-Lai Liu Xiao-Ling Tang ...

  9. Nanogeochronology of discordant zircon measured by atom probe microscopy of Pb-enriched dislocation loops

    Science.gov (United States)

    Peterman, Emily M.; Reddy, Steven M.; Saxey, David W.; Snoeyenbos, David R.; Rickard, William D. A.; Fougerouse, Denis; Kylander-Clark, Andrew R. C.

    2016-01-01

    Isotopic discordance is a common feature in zircon that can lead to an erroneous age determination, and it is attributed to the mobilization and escape of radiogenic Pb during its post-crystallization geological evolution. The degree of isotopic discordance measured at analytical scales of ~10 μm often differs among adjacent analysis locations, indicating heterogeneous distributions of Pb at shorter length scales. We use atom probe microscopy to establish the nature of these sites and the mechanisms by which they form. We show that the nanoscale distribution of Pb in a ~2.1 billion year old discordant zircon that was metamorphosed c. 150 million years ago is defined by two distinct Pb reservoirs. Despite overall Pb loss during peak metamorphic conditions, the atom probe data indicate that a component of radiogenic Pb was trapped in 10-nm dislocation loops that formed during the annealing of radiation damage associated with the metamorphic event. A second Pb component, found outside the dislocation loops, represents homogeneous accumulation of radiogenic Pb in the zircon matrix after metamorphism. The 207Pb/206Pb ratios measured from eight dislocation loops are equivalent within uncertainty and yield an age consistent with the original crystallization age of the zircon, as determined by laser ablation spot analysis. Our results provide a specific mechanism for the trapping and retention of radiogenic Pb during metamorphism and confirm that isotopic discordance in this zircon is characterized by discrete nanoscale reservoirs of Pb that record different isotopic compositions and yield age data consistent with distinct geological events. These data may provide a framework for interpreting discordance in zircon as the heterogeneous distribution of discrete radiogenic Pb populations, each yielding geologically meaningful ages. PMID:27617295

  10. High-Temperature Piezoelectric Sensing

    Directory of Open Access Journals (Sweden)

    Xiaoning Jiang

    2013-12-01

    Full Text Available Piezoelectric sensing is of increasing interest for high-temperature applications in aerospace, automotive, power plants and material processing due to its low cost, compact sensor size and simple signal conditioning, in comparison with other high-temperature sensing techniques. This paper presented an overview of high-temperature piezoelectric sensing techniques. Firstly, different types of high-temperature piezoelectric single crystals, electrode materials, and their pros and cons are discussed. Secondly, recent work on high-temperature piezoelectric sensors including accelerometer, surface acoustic wave sensor, ultrasound transducer, acoustic emission sensor, gas sensor, and pressure sensor for temperatures up to 1,250 °C were reviewed. Finally, discussions of existing challenges and future work for high-temperature piezoelectric sensing are presented.

  11. A Piezoelectric Shear Stress Sensor

    Science.gov (United States)

    Kim, Taeyang; Saini, Aditya; Kim, Jinwook; Gopalarathnam, Ashok; Zhu, Yong; Palmieri, Frank L.; Wohl, Christopher J.; Jiang, Xiaoning

    2016-01-01

    In this paper, a piezoelectric sensor with a floating element was developed for shear stress measurement. The piezoelectric sensor was designed to detect the pure shear stress suppressing effects of normal stress generated from the vortex lift-up by applying opposite poling vectors to the: piezoelectric elements. The sensor was first calibrated in the lab by applying shear forces and it showed high sensitivity to shear stress (=91.3 +/- 2.1 pC/Pa) due to the high piezoelectric coefficients of PMN-33%PT (d31=-1330 pC/N). The sensor also showed almost no sensitivity to normal stress (less than 1.2 pC/Pa) because of the electromechanical symmetry of the device. The usable frequency range of the sensor is 0-800 Hz. Keywords: Piezoelectric sensor, shear stress, floating element, electromechanical symmetry

  12. Piezoelectric Transformers: An Historical Review

    Directory of Open Access Journals (Sweden)

    Alfredo Vazquez Carazo

    2016-04-01

    Full Text Available Piezoelectric transformers (PTs are solid-state devices that transform electrical energy into electrical energy by means of a mechanical vibration. These devices are manufactured using piezoelectric materials that are driven at resonance. With appropriate design and circuitry, it is possible to step up and step down the voltages between the input and output sections of the piezoelectric transformer, without making use of magnetic materials and obtaining excellent conversion efficiencies. The initial concept of a piezoelectric ceramic transformer was proposed by Charles A. Rosen in 1954. Since then, the evolution of piezoelectric transformers through history has been linked to the relevant work of some excellent researchers as well as to the evolution in materials, manufacturing processes, and driving circuit techniques. This paper summarizes the historical evolution of the technology.

  13. Ti-in-zircon thermometry: applications and limitations

    Science.gov (United States)

    Fu, Bin; Page, F. Zeb; Cavosie, Aaron J.; Fournelle, John; Kita, Noriko T.; Lackey, Jade Star; Wilde, Simon A.; Valley, John W.

    2008-08-01

    The titanium concentrations of 484 zircons with U-Pb ages of ˜1 Ma to 4.4 Ga were measured by ion microprobe. Samples come from 45 different igneous rocks (365 zircons), as well as zircon megacrysts (84) from kimberlite, Early Archean detrital zircons (32), and zircon reference materials (3). Samples were chosen to represent a large range of igneous rock compositions. Most of the zircons contain less than 20 ppm Ti. Apparent temperatures for zircon crystallization were calculated using the Ti-in-zircon thermometer (Watson et al. 2006, Contrib Mineral Petrol 151:413-433) without making corrections for reduced oxide activities (e.g., TiO2 or SiO2), or variable pressure. Average apparent Ti-in-zircon temperatures range from 500° to 850°C, and are lower than either zircon saturation temperatures (for granitic rocks) or predicted crystallization temperatures of evolved melts (˜15% melt residue for mafic rocks). Temperatures average: 653 ± 124°C (2 standard deviations, 60 zircons) for felsic to intermediate igneous rocks, 758 ± 111°C (261 zircons) for mafic rocks, and 758 ± 98°C (84 zircons) for mantle megacrysts from kimberlite. Individually, the effects of reduced a_{TiO2} or a_{SiO2}, variable pressure, deviations from Henry’s Law, and subsolidus Ti exchange are insufficient to explain the seemingly low temperatures for zircon crystallization in igneous rocks. MELTs calculations show that mafic magmas can evolve to hydrous melts with significantly lower crystallization temperature for the last 10-15% melt residue than that of the main rock. While some magmatic zircons surely form in such late hydrous melts, low apparent temperatures are found in zircons that are included within phenocrysts or glass showing that those zircons are not from evolved residue melts. Intracrystalline variability in Ti concentration, in excess of analytical precision, is observed for nearly all zircons that were analyzed more than once. However, there is no systematic change in Ti

  14. Lead-free piezoceramics.

    Science.gov (United States)

    Saito, Yasuyoshi; Takao, Hisaaki; Tani, Toshihiko; Nonoyama, Tatsuhiko; Takatori, Kazumasa; Homma, Takahiko; Nagaya, Toshiatsu; Nakamura, Masaya

    2004-11-04

    Lead has recently been expelled from many commercial applications and materials (for example, from solder, glass and pottery glaze) owing to concerns regarding its toxicity. Lead zirconium titanate (PZT) ceramics are high-performance piezoelectric materials, which are widely used in sensors, actuators and other electronic devices; they contain more than 60 weight per cent lead. Although there has been a concerted effort to develop lead-free piezoelectric ceramics, no effective alternative to PZT has yet been found. Here we report a lead-free piezoelectric ceramic with an electric-field-induced strain comparable to typical actuator-grade PZT. We achieved this through the combination of the discovery of a morphotropic phase boundary in an alkaline niobate-based perovskite solid solution, and the development of a processing route leading to highly textured polycrystals. The ceramic exhibits a piezoelectric constant d33 (the induced charge per unit force applied in the same direction) of above 300 picocoulombs per newton (pC N(-1)), and texturing the material leads to a peak d33 of 416 pC N(-1). The textured material also exhibits temperature-independent field-induced strain characteristics.

  15. Nanostructured piezoelectric energy harvesters

    CERN Document Server

    Briscoe, Joe

    2014-01-01

    This book covers a range of devices that use piezoelectricity to convert mechanical deformation into electrical energy and relates their output capabilities to a range of potential applications. Starting with a description of the fundamental principles and properties of piezo- and ferroelectric materials, where applications of bulk materials are well established, the book shows how nanostructures of these materials are being developed for energy harvesting applications. The authors show how a nanostructured device can be produced, and put in context some of the approaches that are being invest

  16. Sulfur in zircons: A new window into melt chemistry

    Science.gov (United States)

    Tang, H.; Bell, E. A.; Boehnke, P.; Barboni, M.; Harrison, T. M.

    2017-12-01

    The abundance and isotopic composition of sulfur are important tools for exploring the photochemistry of the atmosphere, the thermal history of mantle and igneous rocks, and ancient metabolic processes on the early Earth. Because the oldest terrestrial samples are zircons, we developed a new in-situ procedure to analyze the sulfur content of zircons using the CAMECA ims 1290 at UCLA. We analyzed zircons from three metaluminous/I-type granites (reduced and oxidized Peninsular range and Elba), which exhibit low sulfur abundance with the average of 0.5ppm, and one peraluminous/S-type zircon (Strathbogie Range), which shows an elevated sulfur level with the average of 1.5ppm. Additionally, we found that sulfur content ranges between 0.4 and 2.3 ppm in young volcanic zircons (St. Lucia). Our analyses of zircons from the Jack Hills, Western Australia, whose ages range between 3.4 and 4.1 Ga, show a variety of sulfur contents. Three out of the ten zircons are consistent with the sulfur contents of S-type zircons; the rest have low sulfur contents, which are similar to those of I-type zircons. The high sulfur content in some of these Jack Hills zircons can be interpreted as indicating their origin in either a S-type granite or a volcanic reservoir. We favor the former interpretation since the Ti-in-zircon temperatures of our Jack Hills zircons is lower than those of volcanic zircons. Future work will be undertaken to develop a systematic understanding of the relationship between melt volatile content, melt chemistry, and zircon sulfur content.

  17. Critical Role of Monoclinic Polarization Rotation in High-Performance Perovskite Piezoelectric Materials.

    Science.gov (United States)

    Liu, Hui; Chen, Jun; Fan, Longlong; Ren, Yang; Pan, Zhao; Lalitha, K V; Rödel, Jürgen; Xing, Xianran

    2017-07-07

    High-performance piezoelectric materials constantly attract interest for both technological applications and fundamental research. The understanding of the origin of the high-performance piezoelectric property remains a challenge mainly due to the lack of direct experimental evidence. We perform in situ high-energy x-ray diffraction combined with 2D geometry scattering technology to reveal the underlying mechanism for the perovskite-type lead-based high-performance piezoelectric materials. The direct structural evidence reveals that the electric-field-driven continuous polarization rotation within the monoclinic plane plays a critical role to achieve the giant piezoelectric response. An intrinsic relationship between the crystal structure and piezoelectric performance in perovskite ferroelectrics has been established: A strong tendency of electric-field-driven polarization rotation generates peak piezoelectric performance and vice versa. Furthermore, the monoclinic M_{A} structure is the key feature to superior piezoelectric properties as compared to other structures such as monoclinic M_{B}, rhombohedral, and tetragonal. A high piezoelectric response originates from intrinsic lattice strain, but little from extrinsic domain switching. The present results will facilitate designing high-performance perovskite piezoelectric materials by enhancing the intrinsic lattice contribution with easy and continuous polarization rotation.

  18. Hybrid Piezoelectric/Fiber-Optic Sensor Sheets

    Science.gov (United States)

    Lin, Mark; Qing, Xinlin

    2004-01-01

    Hybrid piezoelectric/fiber-optic (HyPFO) sensor sheets are undergoing development. They are intended for use in nondestructive evaluation and long-term monitoring of the integrity of diverse structures, including aerospace, aeronautical, automotive, and large stationary ones. It is anticipated that the further development and subsequent commercialization of the HyPFO sensor systems will lead to economic benefits in the form of increased safety, reduction of life-cycle costs through real-time structural monitoring, increased structural reliability, reduction of maintenance costs, and increased readiness for service. The concept of a HyPFO sensor sheet is a generalization of the concept of a SMART Layer(TradeMark), which is a patented device that comprises a thin dielectric film containing an embedded network of distributed piezoelectric actuator/sensors. Such a device can be mounted on the surface of a metallic structure or embedded inside a composite-material structure during fabrication of the structure. There is has been substantial interest in incorporating sensors other than piezoelectric ones into SMART Layer(TradeMark) networks: in particular, because of the popularity of the use of fiber-optic sensors for monitoring the "health" of structures in recent years, it was decided to incorporate fiber-optic sensors, giving rise to the concept of HyPFO devices.

  19. Enhanced piezoelectric properties in vanadium-modified lead-free (K{sub 0.485}Na{sub 0.5}Li{sub 0.015})(Nb{sub 0.88}Ta{sub 0.1}V{sub 0.02})O{sub 3} ceramics prepared from nanopowders

    Energy Technology Data Exchange (ETDEWEB)

    Gaur, Roopam; Dhingra, Apurva; Pal, Soham; Chandramani Singh, K., E-mail: kongbam@gmail.com

    2015-03-15

    Highlights: • (K{sub 0.485}Na{sub 0.5}Li{sub 0.015})(Nb{sub 0.9−x}Ta{sub 0.1}V{sub x}) O{sub 3}(x = 0, 0.01, 0.02, 0.03) ceramics were prepared. • These ceramics were synthesized from 35-nm powders. • Density, microstrain, crystallite size, tetragonality were high at x = 0.02. • Dielectric, ferroelectric and piezoelectric properties were enhanced at x = 0.02. • The increased properties are attributed to crystal structure and microstructure. - Abstract: Enhancing the piezoelectric properties of lead-free piezoceramics like alkaline niobate system has been an important research topic in our search for an alternative to widely used but highly toxic lead-based PZT piezoceramics system. In the present study, lead-free alkaline niobate-based compositions (K{sub 0.485}Na{sub 0.5}Li{sub 0.015})(Nb{sub 0.9−x}Ta{sub 0.1}V{sub x})O{sub 3} (x = 0, 0.01, 0.02 and 0.03) were synthesized using conventional solid state reaction method. Nanocrystalline powders of these compositions, produced by high energy ball milling, were sintered at 1050 °C for 4 h to produce corresponding ceramics. Increasing V{sup 5+} content in the ceramics from x = 0 to 0.02 results in a gradual increase in the room temperature dielectric constant (ε{sub r}) from 1185 to 1336, remnant polarization (P{sub r}) from 13.4 μC/cm{sup 2} to 17.1 μC/cm{sup 2}, electromechanical coupling factor (k{sub p}) from 0.37 to 0.40, and piezoelectric charge constant (d{sub 33}) from 156 pC/N to 185 pC/N. Further increase in x to 0.03 lowers these values to 1082, 13.4 μC/cm{sup 2}, 0.36 and 128 pC/N respectively. Correspondingly, the coercive field (E{sub c}) first shows a gradual decline from 8.5 kV/cm to 7.9 kV/cm and then a rise to 9.2 kV/cm, as x increases from 0 to 0.02 and then to 0.03. The enhancement of piezoelectric properties in (K{sub 0.485}Na{sub 0.5}Li{sub 0.015})(Nb{sub 0.88}Ta{sub 0.1}V{sub 0.02})O{sub 3} ceramics is attributed to the associated higher values of density, tetragonality and

  20. Radial Field Piezoelectric Diaphragms

    Science.gov (United States)

    Bryant, R. G.; Effinger, R. T., IV; Copeland, B. M., Jr.

    2002-01-01

    A series of active piezoelectric diaphragms were fabricated and patterned with several geometrically defined Inter-Circulating Electrodes "ICE" and Interdigitated Ring Electrodes "ICE". When a voltage potential is applied to the electrodes, the result is a radially distributed electric field that mechanically strains the piezoceramic along the Z-axis (perpendicular to the applied electric field). Unlike other piezoelectric bender actuators, these Radial Field Diaphragms (RFDs) strain concentrically yet afford high displacements (several times that of the equivalent Unimorph) while maintaining a constant circumference. One of the more intriguing aspects is that the radial strain field reverses itself along the radius of the RFD while the tangential strain remains relatively constant. The result is a Z-deflection that has a conical profile. This paper covers the fabrication and characterization of the 5 cm. (2 in.) diaphragms as a function of poling field strength, ceramic thickness, electrode type and line spacing, as well as the surface topography, the resulting strain field and displacement as a function of applied voltage at low frequencies. The unique features of these RFDs include the ability to be clamped about their perimeter with little or no change in displacement, the environmentally insulated packaging, and a highly repeatable fabrication process that uses commodity materials.

  1. Piezoelectric trace vapor calibrator

    International Nuclear Information System (INIS)

    Verkouteren, R. Michael; Gillen, Greg; Taylor, David W.

    2006-01-01

    The design and performance of a vapor generator for calibration and testing of trace chemical sensors are described. The device utilizes piezoelectric ink-jet nozzles to dispense and vaporize precisely known amounts of analyte solutions as monodisperse droplets onto a hot ceramic surface, where the generated vapors are mixed with air before exiting the device. Injected droplets are monitored by microscope with strobed illumination, and the reproducibility of droplet volumes is optimized by adjustment of piezoelectric wave form parameters. Complete vaporization of the droplets occurs only across a 10 deg. C window within the transition boiling regime of the solvent, and the minimum and maximum rates of trace analyte that may be injected and evaporated are determined by thermodynamic principles and empirical observations of droplet formation and stability. By varying solution concentrations, droplet injection rates, air flow, and the number of active nozzles, the system is designed to deliver--on demand--continuous vapor concentrations across more than six orders of magnitude (nominally 290 fg/l to 1.05 μg/l). Vapor pulses containing femtogram to microgram quantities of analyte may also be generated. Calibrated ranges of three explosive vapors at ng/l levels were generated by the device and directly measured by ion mobility spectrometry (IMS). These data demonstrate expected linear trends within the limited working range of the IMS detector and also exhibit subtle nonlinear behavior from the IMS measurement process

  2. Piezoelectric effect in strained quantum wells

    International Nuclear Information System (INIS)

    Dang, L.S.; Andre, R.; Cibert, J.

    1995-01-01

    This paper describes some physical aspects of the piezoelectric effect which takes place in strained semiconductor heterostructures grown along a polar axis. First we show how piezoelectric fields can be accurately measured by optical spectroscopy. Then we discuss about the origin of the non-linear piezoelectric effect reported recently for CdTe, and maybe for InAs as well. Finally we compare excitonic effects in piezoelectric and non-piezoelectric quantum wells. (orig.)

  3. Apollo 12 breccia 12013: Impact-induced partial Pb loss in zircon and its implications for lunar geochronology

    Science.gov (United States)

    Thiessen, F.; Nemchin, A. A.; Snape, J. F.; Bellucci, J. J.; Whitehouse, M. J.

    2018-06-01

    Apollo 12 breccia 12013 is composed of two portions, one grey in colour, the other black. The grey portion of the breccia consists mainly of felsite thought to have formed during a single crystallisation event, while the black part is characterized by presence of lithic fragments of noritic rocks and individual plagioclase crystals. In this study, U-Pb analyses of Ca-phosphate and zircon grains were conducted in both portions of the breccia. The zircon grains within the grey portion yielded a large range of ages (4154 ± 7 to 4308 ± 6 Ma, 2σ) and show decreasing U and Th concentrations within the younger grains. Moreover, some grains exhibit recrystallisation features and potentially formation of neoblasts. The latter process requires high temperatures above 1600-1700 °C leading to the decomposition of the primary zircon grain and subsequent formation of new zircon occurring as neoblasts. As a result of the high temperatures, the U-Pb system of the remaining original zircon grains was most likely open for Pb diffusion causing partial resetting and the observed range of 207Pb/206Pb ages. The event that led to the Pb loss in zircon could potentially be dated by the U-Pb system in Ca-phosphates, which have a weighted average 207Pb/206Pb age across both lithologies of 3924 ± 3 Ma (95% conf.). This age is identical within error to the combined average 207Pb/206Pb age of 3926 ± 2 Ma that was previously obtained from Ca-phosphates within Apollo 14 breccias, zircon grains in Apollo 12 impact melt breccias, and the lunar meteorite SaU 169. This age was interpreted to date the Imbrium impact. The zircon grains located within the black portion of the breccia yielded a similar range of ages (4123 ± 13 to 4328 ± 14 Ma, 2σ) to those in the grey portion. Given the brecciated nature of this part of the sample, the interpretation of these ages as representing igneous crystallisation or resetting by impact events remains ambiguous since there is no direct link to their

  4. Sensing capabilities of piezoelectric wafer active sensors in extreme nuclear environment

    Science.gov (United States)

    Faisal Haider, Mohammad; Lin, Bin; Yu, Lingyu; Giurgiutiu, Victor

    2017-04-01

    There is considerable demand for structural health monitoring (SHM) at locations where there are substantial radiation fields such as nuclear reactor components, dry cask storage canister, irradiated fuel assemblies, etc. Piezoelectric wafer active sensors (PWAS) have been emerged as one of the major SHM sensing technologies. In order to use PWAS to perform SHM in nuclear environment, radiation influence on sensor and sensing capability needs to be investigated to assure the reliability of the PWAS based method. Radiation may cause degradation or even complete failure of sensors. Gamma radiation is one of the major radiation sources near the nuclear source. Therefore, experimental investigation was completed on the gamma radiation endurance of piezoelectric sensors. The irradiation test was done in a Co-60 Gamma Irradiator. Lead Zirconate Titanate (PZT) and Gallium Orthophosphate (GaPO4) PWAS were exposed under gamma radiation at 100 Gy/hr rate for 20 hours. Electro-mechanical (E/M) admittance signatures and electrical capacitance were measured to evaluate the PWAS performance before and after every 4 hours exposure to gamma radiation. PWAS were kept at room temperature for 6 days after each 4 hours radiation exposure to investigate the effect of time on PWAS by gamma radiation. It was found that, PZT-PWAS show variation in resonance frequency for both in plane and thickness mode E/M admittance. Where, the changes in resonance amplitudes are larger for PZT-PWAS. GaPO4-PWAS E/M impedance/admittance spectra don't show any reasonable change after gamma irradiation. A degradation behavior of electrical properties in the PZT-PWAS was observed. Capacitance value of PZT-PWAS decreases from 3.2 nF to 3.07 nF after exposing to gamma radiation for 20 hours at 100Gy/hour. This degradation behavior of electrical properties may be explained by the pinning of domain walls by some radiation induced effect. GaPO4-PWAS doesn't show reasonable degradation in electrical properties

  5. A top-crossover-to-bottom addressed segmented annular array using piezoelectric micromachined ultrasonic transducers

    Science.gov (United States)

    Jung, Joontaek; Lee, Wonjun; Kang, Woojin; Hong, Hyeryung; Yuen Song, Hi; Oh, Inn-yeal; Park, Chul Soon; Choi, Hongsoo

    2015-11-01

    We design and fabricate segmented annular arrays (SAAs) using piezoelectric micromachined ultrasonic transducers (pMUTs) to demonstrate the feasibility of acoustic focusing of ultrasound. The fabricated SAAs have 25 concentric top-electrode signal lines and eight bottom-electrodes for grounding to enable electronic steering of selectively grouped ultrasonic transducers from 2393 pMUT elements. Each element in the array is connected by top-crossover-to-bottom metal bridges, which reduce the parasitic capacitance. Circular-shaped pMUT elements, 120 μm in diameter, are fabricated using 1 μm-thick sol-gel lead zirconate titanate on a silicon wafer. To utilize the high-density pMUT array, a deep reactive ion etching process is used for anisotropic silicon etching to realize the transducer membranes. The resonant frequency and effective coupling coefficient of the elements, measured with an impedance analyzer, yields 1.517 MHz and 1.29%, respectively, in air. The SAAs using pMUTs are packaged on a printed circuit board and coated with parylene C for acoustic intensity measurements in water. The ultrasound generated by each segmented array is focused on a selected point in space. When a 5 Vpp, 1.5 MHz square wave is applied, the maximum spatial peak temporal average intensity ({{I}\\text{spta}} ) is found to be 79 mW cm-2 5 mm from the SAAs’ surface without beamforming. The beam widths (-3 dB) of ultrasonic radiation patterns in the elevation and azimuth directions are recorded as 3 and 3.4 mm, respectively. The results successfully show the feasibility of focusing ultrasound on a small area with SAAs using pMUTs.

  6. Zircon U-Pb ages of Guyana greenstone-gneiss terrane

    Energy Technology Data Exchange (ETDEWEB)

    Gibbs, A.K. (Cornell Univ., Ithaca, NY (USA)); Olszewski, W.J. Jr. (New Hampshire Univ., Durham (USA))

    1982-04-01

    Isotopic U-Pb studies of zircons collected from weathered metagreywackes of the Barama-Mazaruni Supergroup of northern Guyana, South America, demonstrate an age of origin of ca. 2250 Ma. This is the best estimate for the age of the associated metavolcanic rocks. Zircons from weathered gneiss of the Bartica complex, adjacent to the volcanic-sedimentary belts, yield a similar age. The contiguous greenstone-gneiss terrane of eastern Venezuela is also of similar age and comparable greenstone-gneiss terranes of eastern Suriname and French Guiana are probably also of this age. Continental crust formation of a style closely comparable to that of the Canadian Archean occurred on a very widespread scale in the Lower Proterozoic of the Guiana shield. The lead losses from the weathered zircons are comparable to those from zircons from fresh rock from the adjacent terrane of Venezuela, and the advantages of field concentration from numerous saprolite exposures warrant use of such material in future geochronological studies of the region.

  7. Zirconium oxide obtainment from brazilian zircon concentrate

    International Nuclear Information System (INIS)

    Ribeiro, S.; Martins, A.H.

    1991-01-01

    This work presents the experimental results of studies about alkaline melting, acid leaching and sulfation steps for obtention of zirconium oxide and partially stabilized zirconia by yttrium and rare-earth coprecipitation in chlorine medium, starting from the brazilian zircon concentrate. Using statistical methods of factorial design and the Packett-Burman approach, the results are discussed and the optimal conditions of the production steps were determined. (author)

  8. Archean inheritance in zircon from late Paleozoic granites from the Avalon zone of southeastern New England: an African connection

    Science.gov (United States)

    Zartman, R.E.; Don, Hermes O.

    1987-01-01

    In southeastern New England the Narragansett Pier Granite locally intrudes Carboniferous metasedimentary rocks of the Narragansett basin, and yields a monazite UPb Permian emplacement age of 273 ?? 2 Ma. Zircon from the Narragansett Pier Granite contains a minor but detectable amount of an older, inherited component, and shows modern loss of lead. Zircon from the late-stage, aplitic Westerly Granite exhibits a more pronounced lead inheritance -permitting the inherited component to be identified as Late Archean. Such old relict zircon has not been previously recognized in Proterozoic to Paleozoic igneous rocks in New England, and may be restricted to late Paleozoic rocks of the Avalon zone. We suggest that the Archean crustal component reflects an African connection, in which old Archean crust was underplated to the Avalon zone microplate in the late Paleozoic during collision of Gondwanaland with Avalonia. ?? 1987.

  9. Thermoluminescence of zircon: a kinetic model

    CERN Document Server

    Turkin, A A; Vainshtein, D I; Hartog, H W D

    2003-01-01

    The mineral zircon, ZrSiO sub 4 , belongs to a class of promising materials for geochronometry by means of thermoluminescence (TL) dating. The development of a reliable and reproducible method for TL dating with zircon requires detailed knowledge of the processes taking place during exposure to ionizing radiation, long-term storage, annealing at moderate temperatures and heating at a constant rate (TL measurements). To understand these processes one needs a kinetic model of TL. This paper is devoted to the construction of such a model. The goal is to study the qualitative behaviour of the system and to determine the parameters and processes controlling TL phenomena of zircon. The model considers the following processes: (i) Filling of electron and hole traps at the excitation stage as a function of the dose rate and the dose for both (low dose rate) natural and (high dose rate) laboratory irradiation. (ii) Time dependence of TL fading in samples irradiated under laboratory conditions. (iii) Short time anneali...

  10. Domain wall motion and electromechanical strain in lead-free piezoelectrics: Insight from the model system (1 − x)Ba(Zr{sub 0.2}Ti{sub 0.8})O{sub 3}–x(Ba{sub 0.7}Ca{sub 0.3})TiO{sub 3} using in situ high-energy X-ray diffraction during application of electric fields

    Energy Technology Data Exchange (ETDEWEB)

    Tutuncu, Goknur [Department of Materials Science and Engineering, University of Florida, Gainesville, Florida 32611 (United States); Li, Binzhi [Department of Chemical Engineering and Materials Science, University of California, Davis, Davis, California 95616 (United States); Bowman, Keith [Illinois Institute of Technology, Armour College of Engineering, Chicago, Illinois 60616 (United States); School of Materials Engineering, Purdue University, West Lafayette, Indiana 47907 (United States); Jones, Jacob L., E-mail: JacobJones@ncsu.edu [Department of Materials Science and Engineering, North Carolina State University, Raleigh, North Carolina 27695 (United States)

    2014-04-14

    The piezoelectric compositions (1 − x)Ba(Zr{sub 0.2}Ti{sub 0.8})O{sub 3}–x(Ba{sub 0.7}Ca{sub 0.3})TiO{sub 3} (BZT-xBCT) span a model lead-free morphotropic phase boundary (MPB) between room temperature rhombohedral and tetragonal phases at approximately x = 0.5. In the present work, in situ X-ray diffraction measurements during electric field application are used to elucidate the origin of electromechanical strain in several compositions spanning the tetragonal compositional range 0.6 ≤ x ≤ 0.9. As BCT concentration decreases towards the MPB, the tetragonal distortion (given by c/a-1) decreases concomitantly with an increase in 90° domain wall motion. The increase in observed macroscopic strain is predominantly attributed to the increased contribution from 90° domain wall motion. The results demonstrate that domain wall motion is a significant factor in achieving high strain and piezoelectric coefficients in lead-free polycrystalline piezoelectrics.

  11. Torsion sensing based on patterned piezoelectric beams

    Science.gov (United States)

    Cha, Youngsu; You, Hangil

    2018-03-01

    In this study, we investigated the sensing characteristics of piezoelectric beams under torsional loads. We used partially patterned piezoelectric beams to sense torsion. In particular, the piezoelectric patches are located symmetrically with respect to the line of the shear center of the beam. The patterned piezoelectric beam is modeled as a slender beam, and its electrical responses are obtained by piezoelectric electromechanical equations. To validate the modeling framework, experiments are performed using a setup that forces pure torsional deformation. Three different geometric configurations of the patterned piezoelectric layer are used for the experiments. The frequency and amplitude of the forced torsional load are systematically varied in order to study the behavior of the piezoelectric sensor. Experimental results demonstrate that two voltage outputs of the piezoelectric beam are approximately out of phase with identical amplitude. Moreover, the length of the piezoelectric layers has a significant influence on the sensing properties. Our theoretical predictions using the model support the experimental findings.

  12. Piezoelectric and mechanical properties of structured PZT-epoxy composites

    NARCIS (Netherlands)

    James, N.K.; Ende, D.A. van den; Lafont, U.; Zwaag, S. van der; Groen, W.A.

    2013-01-01

    Structured lead zirconium titanate (PZT)-epoxy composites are prepared by dielectrophoresis. The piezoelectric and dielectric properties of the composites as a function of PZT volume fraction are investigated and compared with the corresponding unstructured composites. The effect of poling voltage

  13. Piezoelectric and mechanical properties of structured PZT–epoxy composites

    NARCIS (Netherlands)

    Kunnamkuzhakkal James, N.; Van den Ende, D.; Lafont, U.; Van der Zwaag, S.; Groen, W.A.

    2013-01-01

    Structured lead zirconium titanate (PZT)–epoxy composites are prepared by dielectrophoresis. The piezoelectric and dielectric properties of the composites as a function of PZT volume fraction are investigated and compared with the corresponding unstructured composites. The effect of poling voltage

  14. Structural, dielectric and piezoelectric study of Ca-, Zr-modified ...

    Indian Academy of Sciences (India)

    Home; Journals; Bulletin of Materials Science; Volume 40; Issue 5. Structural, dielectric and piezoelectric study of Ca-, Zr-modified BaTiO 3 lead-free ceramics. H MSOUNI A TACHAFINE M EL AATMANI D FASQUELLE J C CARRU M EL HAMMIOUI M RGUITI A ZEGZOUTI A OUTZOURHIT M DAOUD. Volume 40 Issue 5 ...

  15. Structural Origins of Silk Piezoelectricity.

    Science.gov (United States)

    Yucel, Tuna; Cebe, Peggy; Kaplan, David L

    2011-02-22

    Uniaxially oriented, piezoelectric silk films were prepared by a two-step method that involved: (1) air drying aqueous, regenerated silk fibroin solutions into films, and (2) drawing the silk films to a desired draw ratio. The utility of two different drawing techniques, zone drawing and water immersion drawing were investigated for processing the silk for piezoelectric studies. Silk films zone drawn to a ratio of λ= 2.7 displayed relatively high dynamic shear piezoelectric coefficients of d(14) = -1.5 pC/N, corresponding to over two orders of magnitude increase in d(14) due to film drawing. A strong correlation was observed between the increase in the silk II, β-sheet content with increasing draw ratio measured by FTIR spectroscopy (C(β)∝ e(2.5) (λ)), the concomitant increasing degree of orientation of β-sheet crystals detected via WAXD (FWHM = 0.22° for λ= 2.7), and the improvement in silk piezoelectricity (d(14)∝ e(2.4) (λ)). Water immersion drawing led to a predominantly silk I structure with a low degree of orientation (FWHM = 75°) and a much weaker piezoelectric response compared to zone drawing. Similarly, increasing the β-sheet crystallinity without inducing crystal alignment, e.g. by methanol treatment, did not result in a significant enhancement of silk piezoelectricity. Overall, a combination of a high degree of silk II, β-sheet crystallinity and crystalline orientation are prerequisites for a strong piezoelectric effect in silk. Further understanding of the structural origins of silk piezoelectricity will provide important options for future biotechnological and biomedical applications of this protein.

  16. Mid-1970's imbalance in zircon supply and demand

    International Nuclear Information System (INIS)

    Van Gordon, D.V.; Collins, R.E.

    1975-01-01

    Mining and the historical development of the zircon market are briefly reviewed. Causes of the fluctuations in the zircon demand and supply and in the price are discussed. Possible adjustments (such as substitution of other materials in the steel foundry) are listed. Future uses of zircon will probably be limited to those which can justify high prices and those for which there are no substitutes. (DLC)

  17. Subperiosteal preparation using a new piezoelectric device: a histological examination

    Directory of Open Access Journals (Sweden)

    Stoetzer, Marcus

    2014-12-01

    Full Text Available Introduction: Subperiosteal preparation using a periosteal elevator leads to disturbances of local immunohistochemistry and periosteal histology due to a microtrauma. Usually soft-tissue damage can be considerably reduced by using piezoelectric technology. For this reason, the effects of a novel piezoelectric device on immunohistochemistry and periosteal histology were examined and compared to conventional preparation of the periosteum using a periosteal elevator.Material and methods: Lewis rats were randomly assigned to one of five groups (n=50. Subperiosteal preparation was performed using either a piezoelectric device or a periosteal elevator. Immunohistochemical and histological analyses were performed immediately after preparation as well as three and eight days postoperatively. A statistical analysis of the histological colouring was performed offline using analysis of variance (ANOVA on ranks (p<0.05. Results: At all times, immunohistochemical and histological analysis demonstrated a significantly more homogenous tissue structure in the group of rats that underwent piezosurgery than in the group of rats that underwent treatment with a periosteal elevator.Conclusion: The use of a piezoelectric device for subperiosteal preparation is associated with more harmonious immunohistochemical and histological results for the periosteum than the use of a conventional periosteal elevator. As a result, piezoelectric devices can be expected to have a positive effect primarily on soft tissue, in particular of the periosteal as well as on surrounding tissues.

  18. Piezoelectric Vibration Damping Study for Rotating Composite Fan Blades

    Science.gov (United States)

    Min, James B.; Duffy, Kirsten P.; Choi, Benjamin B.; Provenza, Andrew J.; Kray, Nicholas

    2012-01-01

    Resonant vibrations of aircraft engine blades cause blade fatigue problems in engines, which can lead to thicker and aerodynamically lower performing blade designs, increasing engine weight, fuel burn, and maintenance costs. In order to mitigate undesirable blade vibration levels, active piezoelectric vibration control has been investigated, potentially enabling thinner blade designs for higher performing blades and minimizing blade fatigue problems. While the piezoelectric damping idea has been investigated by other researchers over the years, very little study has been done including rotational effects. The present study attempts to fill this void. The particular objectives of this study were: (a) to develop and analyze a multiphysics piezoelectric finite element composite blade model for harmonic forced vibration response analysis coupled with a tuned RLC circuit for rotating engine blade conditions, (b) to validate a numerical model with experimental test data, and (c) to achieve a cost-effective numerical modeling capability which enables simulation of rotating blades within the NASA Glenn Research Center (GRC) Dynamic Spin Rig Facility. A numerical and experimental study for rotating piezoelectric composite subscale fan blades was performed. It was also proved that the proposed numerical method is feasible and effective when applied to the rotating blade base excitation model. The experimental test and multiphysics finite element modeling technique described in this paper show that piezoelectric vibration damping can significantly reduce vibrations of aircraft engine composite fan blades.

  19. Unified treatment of coupled optical and acoustic phonons in piezoelectric cubic materials

    DEFF Research Database (Denmark)

    Willatzen, Morten; Wang, Zhong Lin

    2015-01-01

    A unified treatment of coupled optical and acoustic phonons in piezoelectric cubic materials is presented whereby the lattice displacement vector and the internal ionic displacement vector are found simultaneously. It is shown that phonon couplings exist in pairs only; either between the electric...... piezoelectricity in a cubic structured material slab. First, it is shown that isolated optical phonon modes generally cannot exist in piezoelectric cubic slabs. Second, we prove that confined acousto-optical phonon modes only exist for a discrete set of in-plane wave numbers in piezoelectric cubic slabs. Third...... potential and the lattice displacement coordinate perpendicular to the phonon wave vector or between the two other lattice displacement components. The former leads to coupled acousto-optical phonons by virtue of the piezoelectric effect. We then establish three new conjectures that entirely stem from...

  20. A mechatronic power boosting design for piezoelectric generators

    International Nuclear Information System (INIS)

    Liu, Haili; Liang, Junrui; Ge, Cong

    2015-01-01

    It was shown that the piezoelectric power generation can be boosted by using the synchronized switch power conditioning circuits. This letter reports a self-powered and self-sensing mechatronic design in substitute of the auxiliary electronics towards a compact and universal synchronized switch solution. The design criteria are derived based on the conceptual waveforms and a two-degree-of-freedom analytical model. Experimental result shows that, compared to the standard bridge rectifier interface, the mechatronic design leads to an extra 111% increase of generated power from the prototyped piezoelectric generator under the same deflection magnitude excitation. The proposed design has introduced a valuable physical insight of electromechanical synergy towards the improvement of piezoelectric power generation

  1. A mechatronic power boosting design for piezoelectric generators

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Haili; Liang, Junrui, E-mail: liangjr@shanghaitech.edu.cn; Ge, Cong [School of Information Science and Technology, ShanghaiTech University, No. 8 Building, 319 Yueyang Road, Shanghai 200031 (China)

    2015-10-05

    It was shown that the piezoelectric power generation can be boosted by using the synchronized switch power conditioning circuits. This letter reports a self-powered and self-sensing mechatronic design in substitute of the auxiliary electronics towards a compact and universal synchronized switch solution. The design criteria are derived based on the conceptual waveforms and a two-degree-of-freedom analytical model. Experimental result shows that, compared to the standard bridge rectifier interface, the mechatronic design leads to an extra 111% increase of generated power from the prototyped piezoelectric generator under the same deflection magnitude excitation. The proposed design has introduced a valuable physical insight of electromechanical synergy towards the improvement of piezoelectric power generation.

  2. Thermal diffusivity of samarium-gadolinium zirconate solid solutions

    International Nuclear Information System (INIS)

    Pan, W.; Wan, C.L.; Xu, Q.; Wang, J.D.; Qu, Z.X.

    2007-01-01

    We synthesized samarium-gadolinium zirconate solid solutions and determined their thermal diffusivities, Young's moduli and thermal expansion coefficients, which are very important for their application in thermal barrier coatings. Samarium-gadolinium zirconate solid solutions have extremely low thermal diffusivity between 20 and 600 deg. C. The solid solutions have lower Young's moduli and higher thermal expansion coefficients than those of pure samarium and gadolinium zirconates. This combination of characteristics is promising for the application of samarium and gadolinium zirconates in gas turbines. The mechanism of phonon scattering by point defects is discussed

  3. Role of zircon in tracing crustal growth and recycling

    Science.gov (United States)

    Compston, W.; Williams, I. S.; Armstrong, R. A.; Claoue-Long, J. C.; Kinny, P. D.; Foster, J. J.; Kroener, A.; Pidgeon, R. T.; Myers, J. S.

    Single crystal ion probe ages of zircons is discussed, which allow much better time resolution compared to other geochronological methods, although the technique is not without problems. Rocks from two areas that contain composite zircon populations, including true magmatic zircons as well as a variety of xenocrystic types are described. It is often difficult to distinguish these; xenocrystic zircons, for example, cannot always be identified on the basis of morphology alone. Additional evidence is needed before making age interpretations. Evidence is also presented of zircon growth long after the original time of crystallization, in some cases apparently at temperatures less than 300 C. The spectacular discovery of 4.1 to 4.2 Ga detrital zircons in metaquartzites from the Mount Narryer area of Western Australia is described. Similar zircons with ages as old as 4276 Ma have been found in the nearby Jack Hills area. The source areas or parent lithologies of these zircons have not yet been determined, but the author expects that they may be unrecognized or buried antecedents of the K rich Narryer gneisses. U or Th concentrations of zircon cannot be used to discriminate between felsic and mafic source rocks.

  4. Influence of some additions on zircon synthesis and its properties

    International Nuclear Information System (INIS)

    Goryacheva, Z.E.; Poplevina, O.G.; Suvorov, S.A.; Toropov, A.N.

    1978-01-01

    Kinetics of zircon synthesis from pure ZrO 2 and SiO 2 is studied in the presence of additions of magnesium, calcium and rare earth oxides. The addition introduction accelerates zircon formation, its yield reaching 97% at 1600 deg C. Constants of zircon formation reaction rate are determined in the presence of additions of various oxides. It is shown that synthetic zircon surpasses the natural one in tensile and density properties at similar thermostability. It is stable to the effect of molten alkaline borosilicate glass and does not polute it

  5. Annealing effects on cathodoluminescence of zircon

    Science.gov (United States)

    Tsuchiya, Y.; Nishido, H.; Noumi, Y.

    2011-12-01

    U-Pb zircon dating (e. g., SHRIMP) is an important tool to interpret a history of the minerals at a micrometer-scale, where cathodoluminescence (CL) imaging allows us to recognize internal zones and domains with different chemical compositions and structural disorder at high spatial resolution. The CL of zircon is attributed by various types of emission centers, which are extrinsic ones such as REE impurities and intrinsic ones such as structural defects. Metamictization resulted from radiation damage to the lattice by alpha particles from the decay of U and Th mostly causes an effect on the CL features of zircon as a defect center. However, slightly radiation-damaged zircon, which is almost nondetectable by XRD, has not been characterized using CL method. In this study, annealing effects on CL of zircon has been investigated to clarify a recovery process of the damaged lattice at low radiation dose. A single crystal of zircon from Malawi was selected for CL measurements. It contains HfO2: 2.30 w.t %, U: 241 ppm and Th: 177 ppm. Two plate samples perpendicular to c and a axes were prepared for annealing experiments during 12 hours from room temperature to 1400 degree C. Color CL images were captured using a cold-cathode microscope (Luminoscope: Nuclide ELM-3R). CL spectral measurements were conducted using an SEM (JEOL: JSM-5410) combined with a grating monochromator (Oxford: Mono CL2) to measure CL spectra ranging from 300 to 800 nm in 1 nm steps with a temperature controlled stage. The dispersed CL was collected by a photoncounting method using a photomultiplier tube (Hamamatsu: R2228) and converted to digital data. All CL spectra were corrected for the total instrumental response. Spectral analysis reveals an anisotropy of the CL emission bands related to intrinsic defect center in blue region, radiation-induced defect center from 500 to 700 nm, and trivalent Dy impurity center at 480 and 580 nm, but their relative intensities are almost constant. CL on the

  6. Testing the reliability of information extracted from ancient zircon

    Science.gov (United States)

    Kielman, Ross; Whitehouse, Martin; Nemchin, Alexander

    2015-04-01

    Studies combining zircon U-Pb chronology, trace element distribution as well as O and Hf isotope systematics are a powerful way to gain understanding of the processes shaping Earth's evolution, especially in detrital populations where constraints from the original host are missing. Such studies of the Hadean detrital zircon population abundant in sedimentary rocks in Western Australia have involved analysis of an unusually large number of individual grains, but also highlighted potential problems with the approach, only apparent when multiple analyses are obtained from individual grains. A common feature of the Hadean as well as many early Archaean zircon populations is their apparent inhomogeneity, which reduces confidence in conclusions based on studies combining chemistry and isotopic characteristics of zircon. In order to test the reliability of information extracted from early Earth zircon, we report results from one of the first in-depth multi-method study of zircon from a relatively simple early Archean magmatic rock, used as an analogue to ancient detrital zircon. The approach involves making multiple SIMS analyses in individual grains in order to be comparable to the most advanced studies of detrital zircon populations. The investigated sample is a relatively undeformed, non-migmatitic ca. 3.8 Ga tonalite collected a few kms south of the Isua Greenstone Belt, southwest Greenland. Extracted zircon grains can be combined into three different groups based on the behavior of their U-Pb systems: (i) grains that show internally consistent and concordant ages and define an average age of 3805±15 Ma, taken to be the age of the rock, (ii) grains that are distributed close to the concordia line, but with significant variability between multiple analyses, suggesting an ancient Pb loss and (iii) grains that have multiple analyses distributed along a discordia pointing towards a zero intercept, indicating geologically recent Pb-loss. This overall behavior has

  7. (De)coupled zircon metamictization, radiation damage, and He diffusivity

    Science.gov (United States)

    Ault, A. K.; Guenthner, W.; Reiners, P. W.; Moser, A. C.; Miller, G. H.; Refsnider, K. A.

    2017-12-01

    We develop and apply a new protocol for targeting crystals for the zircon (U-Th)/He (He) thermochronometry to maximize effective U (eU) and corresponding closure temperature variability to develop zircon He date-eU correlations observed in some datasets. Our approach exploits visual proxies for radiation damage accumulation (metamictization) during zircon selection. We show that by purposefully targeting a spectrum of zircon textures from pristine to metamict grains, it is possible to generate broad eU variation in suites of zircon from a single sample and zircon He date-eU-metamictization trends that can be exploited to resolve increasingly complex thermal histories. We present plane light photographs, eU concentration, and zircon He results from 59 individual zircons from nine crystalline rock samples. Six of the nine samples come from exposed Proterozoic granitoids on SE Baffin Island, Canada; Boulder Creek, CO; Sandia Mountains, NM; and Mecca Hills, CA. We report data from three Archean Baffin samples to compare with the Proterozoic Baffin sample date-eU-metamictization trend. In each Proterozoic sample, target zircons display a spectrum of metamictization from pristine, transparent crystals to purple-brown, translucent grains. Progressive loss of transparency and increase in discoloration consistently corresponds to an increase in eU in all samples. Individual zircon eU varies from 89-1885 ppm and, within each sample, the total eU spread is 538 ppm to 1374 ppm. For any given eU value, the Archean zircon appear comparatively more metamict than the Proterozoic Baffin grains and samples collectively define a 1681 ppm range in eU, with more restrictive intrasample eU spreads (199-1120 ppm). Proterozoic samples from Baffin, Sandia, and Front Range yield negative zircon He date-eU correlations with intrasample date ranges of 90-783 Ma. Increasing eU and younger dates correspond with increasing metamictization. In contrast, all three Proterozoic Mecca Hills samples

  8. Piezoelectrically Initiated Pyrotechnic Igniter

    Science.gov (United States)

    Quince, Asia; Dutton, Maureen; Hicks, Robert; Burnham, Karen

    2013-01-01

    This innovation consists of a pyrotechnic initiator and piezoelectric initiation system. The device will be capable of being initiated mechanically; resisting initiation by EMF, RF, and EMI (electromagnetic field, radio frequency, and electromagnetic interference, respectively); and initiating in water environments and space environments. Current devices of this nature are initiated by the mechanical action of a firing pin against a primer. Primers historically are prone to failure. These failures are commonly known as misfires or hang-fires. In many cases, the primer shows the dent where the firing pin struck the primer, but the primer failed to fire. In devices such as "T" handles, which are commonly used to initiate the blowout of canopies, loss of function of the device may result in loss of crew. In devices such as flares or smoke generators, failure can result in failure to spot a downed pilot. The piezoelectrically initiated ignition system consists of a pyrotechnic device that plugs into a mechanical system (activator), which on activation, generates a high-voltage spark. The activator, when released, will strike a stack of electrically linked piezo crystals, generating a high-voltage, low-amperage current that is then conducted to the pyro-initiator. Within the initiator, an electrode releases a spark that passes through a pyrotechnic first-fire mixture, causing it to combust. The combustion of the first-fire initiates a primary pyrotechnic or explosive powder. If used in a "T" handle, the primary would ramp the speed of burn up to the speed of sound, generating a shock wave that would cause a high explosive to go "high order." In a flare or smoke generator, the secondary would produce the heat necessary to ignite the pyrotechnic mixture. The piezo activator subsystem is redundant in that a second stack of crystals would be struck at the same time with the same activation force, doubling the probability of a first strike spark generation. If the first

  9. Disc piezoelectric ceramic transformers.

    Science.gov (United States)

    Erhart, Jirií; Půlpán, Petr; Doleček, Roman; Psota, Pavel; Lédl, Vít

    2013-08-01

    In this contribution, we present our study on disc-shaped and homogeneously poled piezoelectric ceramic transformers working in planar-extensional vibration modes. Transformers are designed with electrodes divided into wedge, axisymmetrical ring-dot, moonie, smile, or yin-yang segments. Transformation ratio, efficiency, and input and output impedances were measured for low-power signals. Transformer efficiency and transformation ratio were measured as a function of frequency and impedance load in the secondary circuit. Optimum impedance for the maximum efficiency has been found. Maximum efficiency and no-load transformation ratio can reach almost 100% and 52 for the fundamental resonance of ring-dot transformers and 98% and 67 for the second resonance of 2-segment wedge transformers. Maximum efficiency was reached at optimum impedance, which is in the range from 500 Ω to 10 kΩ, depending on the electrode pattern and size. Fundamental vibration mode and its overtones were further studied using frequency-modulated digital holographic interferometry and by the finite element method. Complementary information has been obtained by the infrared camera visualization of surface temperature profiles at higher driving power.

  10. Bar piezoelectric ceramic transformers.

    Science.gov (United States)

    Erhart, Jiří; Pulpan, Půlpán; Rusin, Luboš

    2013-07-01

    Bar-shaped piezoelectric ceramic transformers (PTs) working in the longitudinal vibration mode (k31 mode) were studied. Two types of the transformer were designed--one with the electrode divided into two segments of different length, and one with the electrodes divided into three symmetrical segments. Parameters of studied transformers such as efficiency, transformation ratio, and input and output impedances were measured. An analytical model was developed for PT parameter calculation for both two- and three-segment PTs. Neither type of bar PT exhibited very high efficiency (maximum 72% for three-segment PT design) at a relatively high transformation ratio (it is 4 for two-segment PT and 2 for three-segment PT at the fundamental resonance mode). The optimum resistive loads were 20 and 10 kΩ for two- and three-segment PT designs for the fundamental resonance, respectively, and about one order of magnitude smaller for the higher overtone (i.e., 2 kΩ and 500 Ω, respectively). The no-load transformation ratio was less than 27 (maximum for two-segment electrode PT design). The optimum input electrode aspect ratios (0.48 for three-segment PT and 0.63 for two-segment PT) were calculated numerically under no-load conditions.

  11. Structured Piezoelectric Composites: Materials and Applications

    OpenAIRE

    Van den Ende, D.A.

    2012-01-01

    The piezoelectric effect, which causes a material to generate a voltage when it deforms, is very suitable for making integrated sensors, and (micro-) generators. However, conventional piezoelectric materials are either brittle ceramics or certain polymers with a low thermal stability, which limits their practical application to certain specific fields. Piezoelectric composites, which contain an active piezoelectric (ceramic) phase in a robust polymer matrix, can potentially have better proper...

  12. Silica-calcium zirconate nanocomposite, studying its thermal

    Indian Academy of Sciences (India)

    Silica–calcium zirconate nanocomposite was prepared in a two-step procedure. First, nanocalcium zirconate was synthesized by the modified sol–gel method; then, silica was added to the prepared sol and the resulting product was calcined at 700–1000° C. Dilatometric measurements were performed to determine the ...

  13. Natural radioactivity and radon specific exhalation rate of zircon sands

    International Nuclear Information System (INIS)

    Righi, S.; Verita, S.; Bruzzi, L.; Albertazzi, A.

    2006-01-01

    The study focuses on the radon emanation from zircon sands and their derivatives, which are widely used in many sectors of industry. In particular, the results obtained by experimental measurements on samples of zircon sands and zircon flours commonly used in Italian ceramic industries are reported. Zircon sands contain a significant concentration of natural radioactivity because Th and U may substitute zirconium in the zircon crystal lattice. The relevant routes of exposure of workers to T.E.N.O.R.M. from zircon materials are external radiation and internal exposure, either by inhalation of aerosols in dusty working conditions or by inhalation of radon in workplaces. The main objective of this investigation is to provide experimental data able to better calculate the internal exposure of workers due to radon inhalation. Zircon samples were surveyed for natural radioactivity, radon specific exhalation rate and emanation fraction. Measurements of radioactivity concentration were carried out using γ-spectrometry. Methods used for determining radon consisted in determining the 222 Rn activity accumulated in a vessel after a given accumulation build-up time. The average activity concentrations of 238 U and 232 Th in samples result about 2600 and 550 Bq kg-1, respectively; these concentrations are significantly higher than the world average noticed in soils, rocks and Earth crust. The 222 Rn specific exhalation rates result very low probably due to the low porosity of the material and the consequent difficulty for radon to be released from the zircon crystal lattice. (author)

  14. Thermal effects on domain orientation of tetragonal piezoelectrics

    Science.gov (United States)

    Chang, Wonyoung

    Thermal effects on electrical poling or mechanical grinding induced texture in tetragonal lead zirconate titanate (PZT) and lead titanate (PT) have been investigated using ex situ and in situ X-ray diffraction (XRD) with an area detector. According to previous results using ex situ XRD, domain configurations of poled samples after heat-treatment at or higher than the Curie temperature (TC) are similar to that of unpoled samples showing random domain distributions. The texture parameter called multiples of a random distribution (MRD) gradually decreases with increasing depoling temperature. On the other hand, using in situ XRD measurements, it was found that the MRD maximum for soft PZT initially increases with temperature up to approximately 100°C and then falls to unity at temperatures approaching the TC, whereas the MRD of hard PZT and PT initially undergoes a smaller increase or no change. Mechanical strain energy has an apparent effect on domain wall mobility. In contrast with previous results on electrical poling, mechanically-ground PT and soft PZT materials retained strong ferroelastic textures during thermal cycling, even after excursions to temperatures slightly above the TC . For the ground PT, it was found that repeated cycling above T C results in changes in both peak intensity and peak position, whereas the ground soft PZT undergoes the decrease in intensity of the (002) reflection after the first cycle of heating. Residual stresses in the surface region from grinding resulted in domain wall motion and the retention of textures in annealed samples. The research in this thesis demonstrates that the magnitude of loading applied to the sample surface, the speed used for grinding, or the grit size, can greatly affect the grinding induced damage zone and the depoling behavior of piezoelectric ceramics. Among the possible effects of grinding conditions on surface textures, one of particular interest is the effect of mechanical stresses produced during

  15. Auto-regenerative thermoluminescence dating using zircon inclusions

    International Nuclear Information System (INIS)

    Templer, R.H.

    1993-01-01

    Fired ceramics containing zircon inclusions have been dated by allowing the zircons to regenerate their own thermoluminescence (TL) signal, hence auto-regenerative TL dating. The technique is conceptually straightforward. One first measures the TL accrued since the last heating of the material. The zircon grains are then stored for six months and the TL signal regenerated through self-irradiation is measured. Since the internal dose-rate for zircon is dominated by the internal component the age of the sample is simply given by the ratio of the natural to auto-regenerated signal times the laboratory storage period. The technique, however, requires the measurement of a very small auto-regenerated signal, which introduces a number of experimental and physical complications. The methods for overcoming these problems and successfully dating zircons by auto-regeneration are described. (Author)

  16. Phase coexistence in ferroelectric solid solutions: Formation of monoclinic phase with enhanced piezoelectricity

    Directory of Open Access Journals (Sweden)

    Xiaoyan Lu

    2016-10-01

    Full Text Available Phase morphology and corresponding piezoelectricity in ferroelectric solid solutions were studied by using a phenomenological theory with the consideration of phase coexistence. Results have shown that phases with similar energy potentials can coexist, thus induce interfacial stresses which lead to the formation of adaptive monoclinic phases. A new tetragonal-like monoclinic to rhombohedral-like monoclinic phase transition was predicted in a shear stress state. Enhanced piezoelectricity can be achieved by manipulating the stress state close to a critical stress field. Phase coexistence is universal in ferroelectric solid solutions and may provide a way to optimize ultra-fine structures and proper stress states to achieve ultrahigh piezoelectricity.

  17. Piezoelectric nanomaterials for biomedical applications

    CERN Document Server

    Menciassi, Arianna

    2012-01-01

    Nanoscale structures and materials have been explored in many biological applications because of their novel and impressive physical and chemical properties. Such properties allow remarkable opportunities to study and interact with complex biological processes. This book analyses the state of the art of piezoelectric nanomaterials and introduces their applications in the biomedical field. Despite their impressive potentials, piezoelectric materials have not yet received significant attention for bio-applications. This book shows that the exploitation of piezoelectric nanoparticles in nanomedicine is possible and realistic, and their impressive physical properties can be useful for several applications, ranging from sensors and transducers for the detection of biomolecules to “sensible” substrates for tissue engineering or cell stimulation.

  18. Exceptionally High Piezoelectric Coefficient and Low Strain Hysteresis in Grain-Oriented (Ba, Ca)(Ti, Zr)O3 through Integrating Crystallographic Texture and Domain Engineering.

    Science.gov (United States)

    Liu, Yingchun; Chang, Yunfei; Li, Fei; Yang, Bin; Sun, Yuan; Wu, Jie; Zhang, Shantao; Wang, Ruixue; Cao, Wenwu

    2017-09-06

    Both low strain hysteresis and high piezoelectric performance are required for practical applications in precisely controlled piezoelectric devices and systems. Unfortunately, enhanced piezoelectric properties were usually obtained with the presence of a large strain hysteresis in BaTiO 3 (BT)-based piezoceramics. In this work, we propose to integrate crystallographic texturing and domain engineering strategies into BT-based ceramics to resolve this challenge. [001] c grain-oriented (Ba 0.94 Ca 0.06 )(Ti 0.95 Zr 0.05 )O 3 (BCTZ) ceramics with a texture degree as high as 98.6% were synthesized by templated grain growth. A very high piezoelectric coefficient (d 33 ) of 755 pC/N, and an extremely large piezoelectric strain coefficient (d 33 * = 2027 pm/V) along with an ultralow strain hysteresis (H s ) of 4.1% were simultaneously achieved in BT-based systems for the first time, which are among the best values ever reported on both lead-free and lead-based piezoceramics. The exceptionally high piezoelectric response is mainly from the reversible contribution, and can be ascribed to the piezoelectric anisotropy, the favorable domain configuration, and the formation of smaller sized domains in the BCTZ textured ceramics. This study paves a new pathway to develop lead-free piezoelectrics with both low strain hysteresis and high piezoelectric coefficient. More importantly, it represents a very exciting discovery with potential application of BT-based ceramics in high-precision piezoelectric actuators.

  19. Are there impact-formed zircons in the Hadean record?

    Science.gov (United States)

    Wielicki, M. M.; Lu, X.; Bell, E. A.; Schmitt, A. K.; Harrison, T. M.

    2008-12-01

    Detrital Hadean zircons from the Jack Hills, Western Australia, show a remarkable cluster of crystallization temperatures at 680±25°C. This is particularly surprising as a simple model relating rock composition and Zr concentration predicts that a very broad spectrum of crystallization temperatures (ca. 650°C to 1000°C) with a median value of 780°C, would result from impact melting of the Earth's surface. Magmatic fractionation would tend to increase the aforementioned values. Given the predicted high rate of impacts during the Hadean, the absence of such a population in the Jack Hills zircons could signal a profound sampling problem, a hint of a history much different than previously supposed, or our lack of understanding of zircon formation due to impact related processes. We have begun to examine the latter issue by investigating the crystallization temperatures of zircons formed in melt sheets preserved in the geologic record. The Sudbury Igneous Complex, formed at 1850±3 Ma within the second largest impact crater on Earth, includes two igneous units termed the Black and Felsic Norites. Examination of zircons from each by SIMS confirms their crystallization age at 1847.3±2.2 Ma and yields Ti-in-zircon temperatures of 720°C and 750°C, respectively. This is consistent with that predicted from zircon saturation systematics. A statistical test indicates that the combined norite population is distinct from the Hadean temperature distribution. Thus the question arises: where are the Hadean zircons expected to have formed at >780°C via impact processes? Similar analysis is being pursued for zircons from the Vredefort Impact Structure, South Africa, which should provide further information on impact-formed zircon temperature spectra.

  20. Microfabricated Bulk Piezoelectric Transformers

    Science.gov (United States)

    Barham, Oliver M.

    Piezoelectric voltage transformers (PTs) can be used to transform an input voltage into a different, required output voltage needed in electronic and electro- mechanical systems, among other varied uses. On the macro scale, they have been commercialized in electronics powering consumer laptop liquid crystal displays, and compete with an older, more prevalent technology, inductive electromagnetic volt- age transformers (EMTs). The present work investigates PTs on smaller size scales that are currently in the academic research sphere, with an eye towards applications including micro-robotics and other small-scale electronic and electromechanical sys- tems. PTs and EMTs are compared on the basis of power and energy density, with PTs trending towards higher values of power and energy density, comparatively, indicating their suitability for small-scale systems. Among PT topologies, bulk disc-type PTs, operating in their fundamental radial extension mode, and free-free beam PTs, operating in their fundamental length extensional mode, are good can- didates for microfabrication and are considered here. Analytical modeling based on the Extended Hamilton Method is used to predict device performance and integrate mechanical tethering as a boundary condition. This model differs from previous PT models in that the electric enthalpy is used to derive constituent equations of motion with Hamilton's Method, and therefore this approach is also more generally applica- ble to other piezoelectric systems outside of the present work. Prototype devices are microfabricated using a two mask process consisting of traditional photolithography combined with micropowder blasting, and are tested with various output electri- cal loads. 4mm diameter tethered disc PTs on the order of .002cm. 3 , two orders smaller than the bulk PT literature, had the followingperformance: a prototype with electrode area ratio (input area / output area) = 1 had peak gain of 2.3 (+/- 0.1), efficiency of 33 (+/- 0

  1. Laser-Assisted Atom Probe Tomography of Deformed Minerals: A Zircon Case Study.

    Science.gov (United States)

    La Fontaine, Alexandre; Piazolo, Sandra; Trimby, Patrick; Yang, Limei; Cairney, Julie M

    2017-04-01

    The application of atom probe tomography to the study of minerals is a rapidly growing area. Picosecond-pulsed, ultraviolet laser (UV-355 nm) assisted atom probe tomography has been used to analyze trace element mobility within dislocations and low-angle boundaries in plastically deformed specimens of the nonconductive mineral zircon (ZrSiO4), a key material to date the earth's geological events. Here we discuss important experimental aspects inherent in the atom probe tomography investigation of this important mineral, providing insights into the challenges in atom probe tomography characterization of minerals as a whole. We studied the influence of atom probe tomography analysis parameters on features of the mass spectra, such as the thermal tail, as well as the overall data quality. Three zircon samples with different uranium and lead content were analyzed, and particular attention was paid to ion identification in the mass spectra and detection limits of the key trace elements, lead and uranium. We also discuss the correlative use of electron backscattered diffraction in a scanning electron microscope to map the deformation in the zircon grains, and the combined use of transmission Kikuchi diffraction and focused ion beam sample preparation to assist preparation of the final atom probe tip.

  2. Electronics for Piezoelectric Smart Structures

    Science.gov (United States)

    Warkentin, D. J.; Tani, J.

    1997-01-01

    This paper briefly presents work addressing some of the basic considerations for the electronic components used in smart structures incorporating piezoelectric elements. After general remarks on the application of piezoelectric elements to the problem of structural vibration control, three main topics are described. Work to date on the development of techniques for embedding electronic components within structural parts is presented, followed by a description of the power flow and dissipation requirements of those components. Finally current work on the development of electronic circuits for use in an 'active wall' for acoustic noise is introduced.

  3. Relaxor-PT Single Crystal Piezoelectric Sensors

    Directory of Open Access Journals (Sweden)

    Xiaoning Jiang

    2014-07-01

    Full Text Available Relaxor-PbTiO3 piezoelectric single crystals have been widely used in a broad range of electromechanical devices, including piezoelectric sensors, actuators, and transducers. This paper reviews the unique properties of these single crystals for piezoelectric sensors. Design, fabrication and characterization of various relaxor-PT single crystal piezoelectric sensors and their applications are presented and compared with their piezoelectric ceramic counterparts. Newly applicable fields and future trends of relaxor-PT sensors are also suggested in this review paper.

  4. Fatigue life characterization for piezoelectric macrofiber composites

    International Nuclear Information System (INIS)

    A Henslee, Isaac; Miller, David A; Tempero, Tyler

    2012-01-01

    In an effort to aid the investigation into lightweight and reliable materials for actuator design, a study was developed to characterize the temperature-dependent lifetime performance of a piezoelectric macrofiber composite (MFC). MFCs are thin rectangular patches of polyimide film, epoxy and a single layer of rectangular lead zirconium titanate (PZT) fibers. In this study, the useful life of the MFC is characterized to determine the effect of temperature on the performance of the composite as it is fatigued by cyclic piezoelectric excitation. The test specimen consists of the MFC laminated to a cantilevered stainless steel beam. Beam strain and tip displacement measurements are used as a basis for determining the performance of the MFC as it is cyclically actuated under various operating temperatures. The temperature of the beam laminate is held constant and then cycled to failure, or 250 million cycles, in order to determine the useful life of the MFC over a temperature range from − 15 to 145 °C. The results of the experiments show a strong temperature dependence of the operational life for the MFC. Damage inside the composite was identified through in situ visual inspection and during post-test microstructural observation; however, no degradation in operational performance was identified as it was cyclically actuated up to the point of failure, regardless of temperature or actuation cycle number. (paper)

  5. Fatigue life characterization for piezoelectric macrofiber composites

    Science.gov (United States)

    Henslee, Isaac A.; Miller, David A.; Tempero, Tyler

    2012-10-01

    In an effort to aid the investigation into lightweight and reliable materials for actuator design, a study was developed to characterize the temperature-dependent lifetime performance of a piezoelectric macrofiber composite (MFC). MFCs are thin rectangular patches of polyimide film, epoxy and a single layer of rectangular lead zirconium titanate (PZT) fibers. In this study, the useful life of the MFC is characterized to determine the effect of temperature on the performance of the composite as it is fatigued by cyclic piezoelectric excitation. The test specimen consists of the MFC laminated to a cantilevered stainless steel beam. Beam strain and tip displacement measurements are used as a basis for determining the performance of the MFC as it is cyclically actuated under various operating temperatures. The temperature of the beam laminate is held constant and then cycled to failure, or 250 million cycles, in order to determine the useful life of the MFC over a temperature range from - 15 to 145 °C. The results of the experiments show a strong temperature dependence of the operational life for the MFC. Damage inside the composite was identified through in situ visual inspection and during post-test microstructural observation; however, no degradation in operational performance was identified as it was cyclically actuated up to the point of failure, regardless of temperature or actuation cycle number.

  6. Nanoscale piezoelectric vibration energy harvester design

    Science.gov (United States)

    Foruzande, Hamid Reza; Hajnayeb, Ali; Yaghootian, Amin

    2017-09-01

    Development of new nanoscale devices has increased the demand for new types of small-scale energy resources such as ambient vibrations energy harvesters. Among the vibration energy harvesters, piezoelectric energy harvesters (PEHs) can be easily miniaturized and fabricated in micro and nano scales. This change in the dimensions of a PEH leads to a change in its governing equations of motion, and consequently, the predicted harvested energy comparing to a macroscale PEH. In this research, effects of small scale dimensions on the nonlinear vibration and harvested voltage of a nanoscale PEH is studied. The PEH is modeled as a cantilever piezoelectric bimorph nanobeam with a tip mass, using the Euler-Bernoulli beam theory in conjunction with Hamilton's principle. A harmonic base excitation is applied as a model of the ambient vibrations. The nonlocal elasticity theory is used to consider the size effects in the developed model. The derived equations of motion are discretized using the assumed-modes method and solved using the method of multiple scales. Sensitivity analysis for the effect of different parameters of the system in addition to size effects is conducted. The results show the significance of nonlocal elasticity theory in the prediction of system dynamic nonlinear behavior. It is also observed that neglecting the size effects results in lower estimates of the PEH vibration amplitudes. The results pave the way for designing new nanoscale sensors in addition to PEHs.

  7. Elastic properties of spherically anisotropic piezoelectric composites

    International Nuclear Information System (INIS)

    En-Bo, Wei; Guo-Qing, Gu; Ying-Ming, Poon

    2010-01-01

    Effective elastic properties of spherically anisotropic piezoelectric composites, whose spherically anisotropic piezoelectric inclusions are embedded in an infinite non-piezoelectric matrix, are theoretically investigated. Analytical solutions for the elastic displacements and the electric potentials under a uniform external strain are derived exactly. Taking into account of the coupling effects of elasticity, permittivity and piezoelectricity, the formula is derived for estimating the effective elastic properties based on the average field theory in the dilute limit. An elastic response mechanism is revealed, in which the effective elastic properties increase as inclusion piezoelectric properties increase and inclusion dielectric properties decrease. Moreover, a piezoelectric response mechanism, of which the effective piezoelectric response vanishes due to the symmetry of spherically anisotropic composite, is also disclosed. (condensed matter: structure, thermal and mechanical properties)

  8. A multi-feature integration method for fatigue crack detection and crack length estimation in riveted lap joints using Lamb waves

    Data.gov (United States)

    National Aeronautics and Space Administration — This paper presents an experimental study of damage detection and quantification in riveted lap joints. Embedded lead zirconate titanate piezoelectric (PZT) ceramic...

  9. BIOMINERALOGICAL INVESTIGATION OF APATITE PIEZOELECTRICITY

    Directory of Open Access Journals (Sweden)

    M. Pawlikowski

    2016-01-01

    Full Text Available Investigation of apatite piezoelectricity was conducted in order to assess piezoelectric properties of bone. In the first stage, mineralogical analysis of different apatite crystals, regarding their purity and fitness for the experiments was performed. After the crystals had been chosen, 0.8 mm-thick plates were cut, perpendicular and parallel to the crystallographic Z axis. The plates were then polished and dusted with gold. Electrodes were attached to the opposite surfaces of the plates with conductive glue. So prepared plates were hooked up to the EEG machine used for measuring electrical activity in the brain. The plates were then gently tapped to observe and register currents generated in them. Acquired data was processed by subtracting from the resulting graphs those generated by a hand movement, without tapping the plate. Results indicate that apatite plates have weak piezoelectric properties. Observed phenomenon may be translated to bone apatite, which would explain, at least partially, piezoelectric properties of bone. Acquired results suggest that there is a relation between the mechanical workload of bones (bone apatite and theirelectrical properties. Considering the massive internal surface of bones, they may be treated as a kind of internal “antenna” reacting not only to mechanical stimuli, but to changes in electromagnetic field as well. Observed phenomena no doubt significantly influence the biological processes occurring in bones and the whole human body.

  10. Cylindrical Piezoelectric Fiber Composite Actuators

    Science.gov (United States)

    Allison, Sidney G.; Shams, Qamar A.; Fox, Robert L.

    2008-01-01

    The use of piezoelectric devices has become widespread since Pierre and Jacques Curie discovered the piezoelectric effect in 1880. Examples of current applications of piezoelectric devices include ultrasonic transducers, micro-positioning devices, buzzers, strain sensors, and clocks. The invention of such lightweight, relatively inexpensive piezoceramic-fiber-composite actuators as macro fiber composite (MFC) actuators has made it possible to obtain strains and displacements greater than those that could be generated by prior actuators based on monolithic piezoceramic sheet materials. MFC actuators are flat, flexible actuators designed for bonding to structures to apply or detect strains. Bonding multiple layers of MFC actuators together could increase force capability, but not strain or displacement capability. Cylindrical piezoelectric fiber composite (CPFC) actuators have been invented as alternatives to MFC actuators for applications in which greater forces and/or strains or displacements may be required. In essence, a CPFC actuator is an MFC or other piezoceramic fiber composite actuator fabricated in a cylindrical instead of its conventional flat shape. Cylindrical is used here in the general sense, encompassing shapes that can have circular, elliptical, rectangular or other cross-sectional shapes in the planes perpendicular to their longitudinal axes.

  11. V-stack piezoelectric actuator

    Science.gov (United States)

    Ardelean, Emil V.; Clark, Robert L.

    2001-07-01

    Aeroelastic control of wings by means of a distributed, trailing-edge control surface is of interest with regards to maneuvers, gust alleviation, and flutter suppression. The use of high energy density, piezoelectric materials as motors provides an appealing solution to this problem. A comparative analysis of the state of the art actuators is currently being conducted. A new piezoelectric actuator design is presented. This actuator meets the requirements for trailing edge flap actuation in both stroke and force. It is compact, simple, sturdy, and leverages stroke geometrically with minimum force penalties while displaying linearity over a wide range of stroke. The V-Stack Piezoelectric Actuator, consists of a base, a lever, two piezoelectric stacks, and a pre-tensioning element. The work is performed alternately by the two stacks, placed on both sides of the lever. Pre-tensioning can be readily applied using a torque wrench, obviating the need for elastic elements and this is for the benefit of the stiffness of the actuator. The characteristics of the actuator are easily modified by changing the base or the stacks. A prototype was constructed and tested experimentally to validate the theoretical model.

  12. PZT piezoelectric films on glass for Gen-X imaging

    Science.gov (United States)

    Wilke, Rudeger H. T.; Trolier-McKinstry, Susan; Reid, Paul B.; Schwartz, Daniel A.

    2010-09-01

    The proposed adaptive optics system for the Gen-X telescope uses piezoelectric lead zirconate titanate (PZT) films deposited on flexible glass substrates. The low softening transition of the glass substrates imposes several processing challenges that require the development of new approaches to deposit high quality PZT thin films. Synthesis and optimization of chemical solution deposited 1 μm thick films of PbZr0.52Ti0.48O3 on small area (1 in2) and large area (16 in2) Pt/Ti/glass substrates has been performed. In order to avoid warping of the glass at temperatures typically used to crystallize PZT films ({700°C), a lower temperature, two-step crystallization process was employed. An {80 nm thick seed layer of PbZr0.30Ti0.70O3 was deposited to promote the growth of the perovskite phase. After the deposition of the seed layer, the films were annealed in a rapid thermal annealing (RTA) furnace at 550°C for 3 minutes to nucleate the perovskite phase. This was followed by isothermal annealing at 550°C for 1 hour to complete crystallization. For the subsequent PbZr0.52Ti0.48O3 layers, the same RTA protocol was performed, with the isothermal crystallization implemented following the deposition of three PbZr0.52Ti0.48O3 spin-coated layers. Over the frequency range of 1 kHz to 100 kHz, films exhibit relative permittivity values near 800 with loss tangents below 0.07. Hysteresis loops show low levels of imprint with coercive fields of 40-50 kV/cm in the forward direction and 50-70 kV/cm in the reverse direction. The remanent polarization varied from 25-35 μC/cm2 and e31,f values were approximately -5.0 C/m2. In scaling up the growth procedure to large area films, where warping becomes more pronounced due to the increased size of the substrate, the pyrolysis and crystallization conditions were performed in a box furnace to improve the temperature uniformity. By depositing films on both sides of the glass substrate, the tensile stresses are balanced, providing a

  13. Circuit for Driving Piezoelectric Transducers

    Science.gov (United States)

    Randall, David P.; Chapsky, Jacob

    2009-01-01

    The figure schematically depicts an oscillator circuit for driving a piezoelectric transducer to excite vibrations in a mechanical structure. The circuit was designed and built to satisfy application-specific requirements to drive a selected one of 16 such transducers at a regulated amplitude and frequency chosen to optimize the amount of work performed by the transducer and to compensate for both (1) temporal variations of the resonance frequency and damping time of each transducer and (2) initially unknown differences among the resonance frequencies and damping times of different transducers. In other words, the circuit is designed to adjust itself to optimize the performance of whichever transducer is selected at any given time. The basic design concept may be adaptable to other applications that involve the use of piezoelectric transducers in ultrasonic cleaners and other apparatuses in which high-frequency mechanical drives are utilized. This circuit includes three resistor-capacitor networks that, together with the selected piezoelectric transducer, constitute a band-pass filter having a peak response at a frequency of about 2 kHz, which is approximately the resonance frequency of the piezoelectric transducers. Gain for generating oscillations is provided by a power hybrid operational amplifier (U1). A junction field-effect transistor (Q1) in combination with a resistor (R4) is used as a voltage-variable resistor to control the magnitude of the oscillation. The voltage-variable resistor is part of a feedback control loop: Part of the output of the oscillator is rectified and filtered for use as a slow negative feedback to the gate of Q1 to keep the output amplitude constant. The response of this control loop is much slower than 2 kHz and, therefore, does not introduce significant distortion of the oscillator output, which is a fairly clean sine wave. The positive AC feedback needed to sustain oscillations is derived from sampling the current through the

  14. Pengaruh Temperatur, Waktu, dan Aditif Dalam Pembuatan Zircon Micronized

    Directory of Open Access Journals (Sweden)

    Sajima

    2017-05-01

    Full Text Available Research on temperature, time and additives effects on milling process in micronized-zircon production has been conducted. The production of zircon micronized started from sorting process on mining products then followed by beneficiation, roasting, leaching, dryng and milling processes. The results showed that the optimum conditions of the roasting process was at the temperature of 425 °C, in 25 minutes and using 4% additives. In these conditions, micronized zircon (2 µm obtained as much as 92.10% in10 minutes milling time.

  15. Enhanced active piezoelectric 0-3 nanocomposites fabricated through electrospun nanowires

    International Nuclear Information System (INIS)

    Feenstra, Joel; Sodano, Henry A.

    2008-01-01

    The use of monolithic piezoceramic materials in sensing and actuation applications has become quite common over the past decade. However, these materials have several properties that limit their application in practical systems. These materials are very brittle due to the ceramic nature of the monolithic material, making them vulnerable to accidental breakage during handling and bonding procedures. In addition, they have very poor ability to conform to curved surfaces and result in large add-on mass associated with using a typically lead-based ceramic. These limitations have motivated the development of alternative methods of applying the piezoceramic material, including piezoceramic fiber composites and piezoelectric 0-3 composites (also known as piezoelectric paint). Piezoelectric paint is desirable because it can be spayed or painted on and can be used with abnormal surfaces. However, the piezoelectric paint developed in prior studies has resulted in low coupling, limiting its application. In order to increase the coupling of the piezoelectric paint, this effort has investigated the use of piezoelectric nanowires rather than spherical piezoelectric particle, which are difficult to strain when embedded in a polymer matrix. The piezoceramic wires were electrospun from a barium titanate (BaTiO 3 ) sol gel to produce fibers with 500-1000 nm diameters and subsequently calcinated to acquire perovskite BaTiO 3 . An active nanocomposite paint was formed using the resulting piezoelectric wires and was compared to the same paint with piezoelectric nanoparticles. The results show that the piezoceramic wires produce 0-3 nanocomposites with as high as 300% increase in electromechanical coupling

  16. Transformations to granular zircon revealed: Twinning, reidite, and ZrO2 in shocked zircon from Meteor Crater (Arizona, USA)

    Science.gov (United States)

    Cavosie, Aaron; Timms, Nicholas E.; Erickson, Timmons M.; Hagerty, Justin J.; Hörz, Friedrich

    2016-01-01

    Granular zircon in impact environments has long been recognized but remains poorly understood due to lack of experimental data to identify mechanisms involved in its genesis. Meteor Crater in Arizona (United States) contains abundant evidence of shock metamorphism, including shocked quartz, the high pressure polymorphs coesite and stishovite, diaplectic SiO2 glass, and lechatelierite (fused SiO2). Here we report the presence of granular zircon, a new shocked mineral discovery at Meteor Crater, that preserve critical orientation evidence of specific transformations that occurred during its formation at extreme impact conditions. The zircon grains occur as aggregates of sub-µm neoblasts in highly shocked Coconino Formation Sandstone (CFS) comprised of lechatelierite. Electron backscatter diffraction shows that each grain consists of multiple domains, some with boundaries disoriented by 65°, a known {112} shock-twin orientation. Other domains have crystallographic c-axes in alignment with {110} of neighboring domains, consistent with the former presence of the high pressure ZrSiO4 polymorph reidite. Additionally, nearly all zircon preserve ZrO2 + SiO2, providing evidence of partial dissociation. The genesis of CFS granular zircon started with detrital zircon that experienced shock-twinning and reidite formation from 20 to 30 GPa, ultimately yielding a phase that retained crystallographic memory; this phase subsequently recrystallized to systematically oriented zircon neoblasts, and in some areas partially dissociated to ZrO2. The lechatelierite matrix, experimentally constrained to form at >2000 °C, provided an ultra high-temperature environment for zircon dissociation (~1670 °C) and neoblast formation. The capacity of granular zircon to preserve a cumulative P-T record has not been recognized previously, and provides a new method for retrieving histories of impact-related mineral transformations in the crust at conditions far beyond which most rocks melt.

  17. Late cenozoic magmatism in the South Patagonian batholith: SHRIMP U-Pb zircon age evidence

    International Nuclear Information System (INIS)

    Fanning, C.M; Herve, F; Pankhurst, R.J; Thomson, S; Faundez, V

    2001-01-01

    The North Patagonian Batholith (NPB) has a zonal age pattern which includes a well defined belt of Miocene and Mio-Pliocene plutons in its central portion (Pankhurst et al., 1999) which are spatially, and probably genetically related to the Liquine-Ofqui Fault Zone. Previous geochronological studies in the Southern Patagonian Batholith (SPB), as summarized by Bruce et al. (1991), have yielded 9 late Cenozoic K-Ar or Ar-Ar ages out of a total of 116 age determinations. None of these young ages correspond to U-Pb determinations on zircons, and some of the young ages correspond to satellite plutons east of the SPB proper, such as the Torres del Paine intrusion. In this paper we present the first late Cenozoic SHRIMP U-Pb zircon ages in the area of the SPB. The morphology of the analysed zircon crystals is described and leads to some inferences on the methodology and on the geological interpretation of the obtained ages (au)

  18. Depositional history of a condensed shallow marine reservoir succession: stratigraphy and detrital zircon geochronology of the Jurassic Sto Formation, Barents Sea

    Czech Academy of Sciences Publication Activity Database

    Klausen, T. G.; Müller, R.; Sláma, Jiří; Olaussen, S.; Rismyhr, B.; Helland-Hansen, W.

    2018-01-01

    Roč. 175, č. 1 (2018), s. 130-145 ISSN 0016-7649 Institutional support: RVO:67985831 Keywords : binary alloys * deposition * erosion * geochronology * lead * lead alloys * sea level * silicate minerals * uranium alloys * zircon Subject RIV: DB - Geology ; Mineralogy OBOR OECD: Geology Impact factor: 3.037, year: 2016

  19. Displacement and resonance behaviors of a piezoelectric diaphragm driven by a double-sided spiral electrode

    KAUST Repository

    Shen, Zhiyuan; Olfatnia, Mohammad; Miao, Jianmin; Wang, Zhihong

    2012-01-01

    This paper presents the design of a lead zirconate titanate (PZT) diaphragm actuated by double-sided patterned electrodes. Au/Cr electrodes were deposited on bulk PZT wafers by sputtering while patterned by a lift-off process. SU-8 thick film

  20. Novel Mechano-Luminescent Sensors Based on Piezoelectric/Electroluminescent Composites

    Directory of Open Access Journals (Sweden)

    Yunzhang Fang

    2011-04-01

    Full Text Available A high-sensitivity mechano-luminescent sensor was fabricated on the basis of piezoelectric/electroluminescent composites. The working principle of this mechano-luminescent sensor was elucidated by analyzing the relationship between the piezoelectric-induced charges and the electroluminescent effects. When a stress is applied on the piezoelectric layer, electrical charges will be induced at both the top and bottom sides of the piezoelectric layer. The induced electrical charges will lead to a light output from the electroluminescent layer, thus producing a mechano-luminescence effect. By increasing the vibration strength or frequency applied, the mechano-luminescence output can be obviously enhanced. Mechano-luminescence sensors have potential in smart stress-to-light devices, such as foot-stress-distribution-diagnosis systems and dynamic-load-monitors for bridge hanging cables.