Effect of Alkyl Phenol from Cashew Nutshell Liquid on Mechanical and Dry Sliding Wear Behavior of Epoxy Resin

Directory of Open Access Journals (Sweden)

Rajesh Panda

2015-05-01

Full Text Available A phenalkamine made from the reaction of alkyl phenol from cashew nutshell liquid (CSNL and polyamine was added at three different weight percentages (30%, 40%, and 50% as a diglycidyl ether of bisphenol A (DGEBA epoxy hardener. This curing agent was compared to a traditional polyamine epoxy hardener. It was observed that an increase in phenalkamine concentration resulted in considerable improvement to impact strength and elongation, which ultimately translated to better wear resistance of the cured epoxy compound. Lancaster–Ratner correlations between mechanical and wear resistance properties were found to be linear. Optical microscope observations were used to understand the wear mechanisms of the cured epoxy materials.

Selective defunctionalization by TiO2 of monomeric phenolics from lignin pyrolysis into simple phenols.

Science.gov (United States)

Mante, Ofei D; Rodriguez, Jose A; Babu, Suresh P

2013-11-01

This study is focused on defunctionalizing monomeric phenolics from lignin into simple phenols for applications such as phenol/formaldehyde resins, epoxidized novolacs, adhesives and binders. Towards this goal, Titanium dioxide (TiO2) was used to selectively remove hydroxyl, methoxy, carbonyl and carboxyl functionalities from the monomeric phenolic compounds from lignin to produce mainly phenol, cresols and xylenols. The results showed that anatase TiO2 was more selective and active compared to rutile TiO2. Catechols were found to be the most reactive phenolics and 4-ethylguaiacol the least reactive with anatase TiO2. An overall conversion of about 87% of the phenolics was achieved at 550°C with a catalyst-to-feed ratio of 5 w/w. Over 97% conversion of phenolics is achievable at moderate temperatures (550°C or ≤ 600°C) and a moderate catalyst-to-feed ratio of 6.5:1. The reactivity of catechols on TiO2 suggests that titania is a promising catalyst in the removal of hydroxyl moiety. Published by Elsevier Ltd.

High-capacitance supercapacitors using nitrogen-decorated porous carbon derived from novolac resin containing peptide linkage

Energy Technology Data Exchange (ETDEWEB)

Kim, Yong Jung [Institute of Carbon Science and Technology, Shinshu University, 4-17-1 Wakasato, Nagano 380-8553 (Japan); Jang, In Young; Park, Ki Chul; Jung, Yong Chae; Oka, Takuyuki [Department of Electric and Electronic Engineering, Faculty of Engineering, Shinshu University, 4-17-1 Wakasato, Nagano 380-8553 (Japan); Iinou, Satoshi [MEFS, Co. Ltd. Choei Nagano, Higasiguchi Bldg, 2F, 1000-1 Gentakubo, Kurita, Nagano 380-0921 (Japan); Komori, Yasuhiro; Kozutsumi, Toshihiko; Hashiba, Takashi [SHOWA HIGHPOLYMER, Co., Ltd. 1021 Tomizuka-cho, Isesaki-City, Gunma 372-0833 (Japan); Kim, Yoong Ahm, E-mail: yak@endomoribu.shinshu-u.ac.j [Department of Electric and Electronic Engineering, Faculty of Engineering, Shinshu University, 4-17-1 Wakasato, Nagano 380-8553 (Japan); Endo, Morinobu [Institute of Carbon Science and Technology, Shinshu University, 4-17-1 Wakasato, Nagano 380-8553 (Japan)] [Department of Electric and Electronic Engineering, Faculty of Engineering, Shinshu University, 4-17-1 Wakasato, Nagano 380-8553 (Japan)

2010-08-01

We fabricated nitrogen-decorated porous carbon exhibiting high capacitance per unit volume and unit weight via chemical activation of novolac resin containing peptide linkage. The porosity and the amount of nitrogen atoms were controlled by changing the molecular weight of novolac resin, the added amount of potassium hydroxide, or both. After chemical activation, positively charged nitrogen atoms (i.e., pyridine/pyrrole) at 400.3 eV in photoemission spectra contributed to both a shift in the point of zero charge toward negative potential and the generation of pseudocapacitance. Suitably developed pores and the positively charged nitrogen atoms make nitrogen-decorated novolac resin-derived porous carbon a promising material for electrodes in high-performance supercapacitors.

Improvement in char formability of phenolic resin for development of Carbon/Carbon composites

International Nuclear Information System (INIS)

Hajhosseini, M.; Payami, A.; Ghaffarian, S. R.; Rezadoust, A. M.

2008-01-01

In the processing of carbon/carbon composites using polymer resin as the matrix precursor, it is inevitable that a porous structure was formed after carbonization. As a result, densification by liquid phase impregnation followed by recarbonization is required to obtain a densified composite. Consequently, the char formability of resin is an important factor in reducing the number of densification cycles and hence the processing cost. In this study, a novel approach is adopted to improve the densification of carbon/carbon composites by using a new phenolic resin modified by pitch. For this purpose, soluble part of pitch was extracted and dispersed in resol type phenolic resin. The polymerization reaction was performed in presence of para-formaldehyde and a resol-pitch compound was obtained. The second compound was prepared by mixing novolac-furfural in 55:45 weight ratio containing 9% by weight hexamethylene tetramine. This compound was added to resol-pitch compound in 10,20,50 and 80 w %. The microstructure of carbonized resin was investigated by X-ray diffraction and char yield, and the linear and volumetric shrinkage were obtained. Results show that in 80:20 ratio of resol-pitch to novolac-furfural , the char yield would be maximized by 71% and volumetric shrinkage would be minimized at 16.4%. At the same time, XRD results indicate that the resin has a strong ability to graphitize carbon/carbon composites matrix as a necessary step for its processing

Functionalization of Nanodiamond with Four Kinds of Expoxies.

Science.gov (United States)

Ma, Weijia; Liu, Ruojin; Yu, Xiaoyan; Naito, Kimiyoshi; Qu, Xiongwei; Zhang, Qingxin

2017-01-01

In this work, a simple and effective method for the covalent functionalization of nanodiamond (ND) with four epoxies has been developed. After homogenization by mixed acids and thionyl chlorides, the surface of ND was modified with triethylenetetramine (TETA) to possess amine groups, which were used as active points to react with epoxy by ring opening reaction. Four different epoxies used are bifunctional diglycidyl ether of bisphenol-A (DGEBA), trifunctional triglycidyl p-amino phenol (TGAP), tetrafunctional tetraglycidyldiamino diphenylmethane (TGDDM) and bisphenol-A novolac epoxy resin (BAEPN). FT-IR spectra revealed that the epoxy was covalently attached to the ND (ND-g-epoxy). In addition, functionalized ND particles were characterized with WAXD and UV-Vis spectra to confirm the result. The weight gains as a result of the epoxy-functionalized ND were determined by TGA analysis. The ND-g-epoxy particles were better dispersed in common organic solvents and the average diameters were characterized. The better dispersion and of the modified ND were identified from the SEM images.

High-capacitance supercapacitors using nitrogen-decorated porous carbon derived from novolac resin containing peptide linkage

OpenAIRE

Kim, Yong Jung; Jang, In Young; Park, Ki Chul; Jung, Yong Chae; Oka, Takuyuki; Iinou, Satoshi; Komori, Yasuhiro; Kozutsumi, Toshihiko; Hashiba, Takashi; Kim, Yoong Ahm; Endo, Morinobu

2010-01-01

We fabricated nitrogen-decorated porous carbon exhibiting high capacitance per unit volume and unit weight via chemical activation of novolac resin containing peptide linkage. The porosity and the amount of nitrogen atoms were controlled by changing the molecular weight of novolac resin, the added amount of potassium hydroxide, or both. After chemical activation, positively charged nitrogen atoms (i.e., pyridine/pyrrole) at 400.3 eV in photoemission spectra contributed to both a shift in the ...

Utilização de ligninas em resinas fenólicas: 1. Preparação de novolacas a partir de lignossulfonatos Use of lignins in phenolic resins: 1. Preparation of novolacs from lignosulfonates 49

Directory of Open Access Journals (Sweden)

Fernando dos Santos

1999-01-01

Full Text Available Este trabalho descreve uma utilização mais nobre para a lignina obtida de processos industriais de polpação. Foram preparadas resinas fenólicas tipo novolaca, utilizando-se lignossulfonato de amônio e lignossulfonato de sódio (com diferentes teores de açúcares residuais como correagentes, em substituição parcial ao fenol. As resinas foram preparadas mantendo-se o processo utilizado industrialmente. As resinas foram caracterizadas por análises químicas, quanto à distribuição de massa molar e análises térmicas. As resinas preparadas com lignossulfonatos apresentaram maior reatividade com hexametilenotetramina (agente de reticulação. Isto é uma vantagem, pois pode-se ter ciclos de moldagem de peças mais curtos, o que economicamente é favorável.This work describes the production of high value products using lignins obtained from industrial pulping processes. Novolac phenolic resins were prepared employing ammonium lignosulfonates and sodium lignosulfonates (with different residual sugar contents in a partial replacement of phenol. The resins were prepared using the same conditions employed in the industrial phenolic resins production. The lignin based resins were characterized by chemical analysis, molecular weight distribution and thermal analysis. The resins prepared using lignosulfonates showed higher reactivity with hexamethylenetetramine (crosslink agent. This behavior lead to another economic advantage as consequence of the reduction in the expended time for molding cycles.

Corrosion Protection of Phenolic-Epoxy/Tetraglycidyl Metaxylediamine Composite Coatings in a Temperature-Controlled Borax Environment

Science.gov (United States)

Xu, Wenhua; Wang, Zhenyu; Han, En-Hou; Liu, Chunbo

2017-12-01

The failure behavior for two kinds of phenolic-epoxy/tetraglycidyl metaxylediamine composite coatings in 60 °C borax aqueous solution was evaluated using electrochemical methods (EIS) combined with scanning electron microscopy, confocal laser scanning microscope, water immersion test, and Raman spectrum. The main focus was on the effect of curing agent on the corrosion protection of coatings. Results revealed that the coating cured by phenolic modified aromatic amine possessed more compact cross-linked structure, better wet adhesion, lower water absorption (0.064 mg h-1 cm-2) and its impedance values was closed to 108 Ω cm2 after immersion for 576 h, while the coating cured by modified aromatic ring aliphatic amine was lower than 105 Ω cm2. The corrosion mechanism of the two coatings is discussed.

α-aminoacetophenones as photobase generators

International Nuclear Information System (INIS)

Hisatoshi Kura; Hidetaka Oka

1999-01-01

It was demonstrated that α-aminoacetophenones such as Irgacure 907 and Irgacure 369 work effectively as photobase generators in epoxy-based compositions. Upon irradiation they accelerate the thermal reaction of phenol novolac epoxy resins with polyacrylates having carboxylic acid groups despite of their high latency before irradiation. Irgacure 369 is much more active than Irgacure 907 due to the more reactive amine generated. We believe that conformational and steric effects contribute to the latency of the amine moiety. The bulky benzoyl group of the aminoacetophenone moiety shields the amino nitrogen from acidic species present in the composition. Upon irradiation, the benzoyl part is cleaved and the active tertiary amine base is liberated

Low temperature measurement of thermal and mechanical properties of phenolic laminate, the pultruded polyester fiberglass and A and B epoxy putty

International Nuclear Information System (INIS)

Wang, S.T.; Kim, S.H.; Kim, N.S.; Cheng, R.S.; Hoffman, J.; Gonczy, J.

1979-01-01

Low temperature measurements were made and are reported of thermal and mechanical properties of phenolic laminate, pultruded polyester fiberglass, and A and B epoxy putty. To determine the modulus, compressive and tensile stress and strain, an Instron machine, a Tinus-Olsen testing machine, a Wheatstone bridge and strain gages were used

Surface characterization and stability of an epoxy resin surface modified with polyamines grafted on polydopamine

Energy Technology Data Exchange (ETDEWEB)

Schaubroeck, David, E-mail: David.Schaubroeck@elis.ugent.be [Center for Microsystems Technology (CMST), imec and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium); Vercammen, Yannick; Van Vaeck, Luc [Biomolecular and Analytical Mass Spectrometry, University of Antwerp, Universiteitsplein 1, B-2610 Wilrijk (Belgium); Vanderleyden, Els; Dubruel, Peter [Polymer Chemistry and Biomaterials Research Group, Ghent University, Krijgslaan 281 S4 bis, B-9000 Ghent (Belgium); Vanfleteren, Jan [Center for Microsystems Technology (CMST), imec and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium)

2014-06-01

This paper reports on polydopamine and polyamine surface modifications of an etched epoxy cresol novolac (ECN) resin using the ‘grafting to’ method. Three different polyamines are used for the grafting reactions: branched polyethyleneimine (B-PEI), linear polyethyleneimine (L-PEI) and diethylenetriamine (DETA). These modifications are compared to control materials prepared via direct deposition of polyamines. The stability of the modifications toward a concentrated hydrochloric acid (HCl) environment is evaluated. The modified surfaces are characterized with scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and time-of-flight static secondary ion mass spectroscopy (TOF-S-SIMS).

Physico-Chemical Studies Involving Incorporation of Radioactive and Industrial Waste In Cement-Epoxy Resin Matrix

International Nuclear Information System (INIS)

Sayed, M.S.; Hafez, N.

1999-01-01

Cement and epoxy resin as chemical additives are proposed to incorporate different types of wastes. The study was extended to prepare different mixtures of cement and epoxy resin in presence of some toxic ions. The studied ions were Cd II, Ni II, Cu II, Fe III, Ce IV, 154+152 Eu, phenol and toluene. The physical, mechanical and leaching properties of the mixtures were studied. The thermal analysis and infrared spectra were also investigated. It was observed that all the studied properties of the epoxy modified cement as a disposal matrix was improved

On The Molecular Mechanism Of Positive Novolac Resists

Science.gov (United States)

Huang, Jian-Ping; Kwei, T. K.; Reiser, Arnost

1989-08-01

A molecular mechanism for the dissolution of novolac is proposed, based on the idea of a critical degree of deprotonation as being the condition for the transfer of polymer into solution. The rate at which the critical deprotonation condition is achieved is controlled by the supply of developer into a thin penetration zone, and depends in particular on the rate of diffusion of the base cations which are the developer component with the lowest mobility. The penetration zone contains phenolate ions and ion-bound water, but it retains the structure of a rigid polymer membrane, as evidenced by the diffusion coefficient of cations in the pene;tration zone which is several orders of magnitude slower than in an open gel of the same material. When the critical degree of deprotonation is reached, the membrane structure unravels and all subsequent events, chain rearrangement and transfer into solution, occur rapidly. The supralinear dependence of dissolution rate on base concentration and the effect of the size of the base cation are plausibly interpreted by the model. The diffusion of developer components is assumed to occur preferentially via hydrophilic sites in the polymer matrix. These sites define a diffusion path which acts like a hydrophilic diffusion channel. Suitably designed hydrophobic molecules can block some of the channels and in this way alter the dissolution rate. They reduce in effect the diffusion crossect ion of the material. Hydrophilic additives, on the other hand, introduce additional channels into the system and promote dissolution. The concept of diffusion channels appears to provide a unified interpretation for a number of common observations.

Photobleachable Diazonium Salt-Phenolic Resin Two-Layer Resist System

Science.gov (United States)

Uchino, Shou-ichi; Iwayanagi, Takao; Hashimoto, Michiaki

1988-01-01

This article describes a new negative two-layer photoresist system formed by a simple, successive spin-coating method. An aqueous acetic acid solution of diazonium salt and poly(N-vinylpyrrolidone) is deposited so as to contact a phenolic resin film spin-coated on a silicon wafer. The diazonium salt diffuses into the phenolic resin layer after standing for several minutes. The residual solution on the phenolic resin film doped with diazonium salt is spun to form the diazonium salt-poly(N-vinylpyrrolidone) top layer. This forms a uniform two-layer resist without phase separation or striation. Upon UV exposure, the diazonium salt in the top layer bleaches to act as a CEL dye, while the diazonium salt in the bottom layer decomposes to cause insolubilization. Half μm line-and-space patterns are obtained with an i-line stepper using 4-diazo-N,N-dimethylaniline chloride zinc chloride double salt as the diazonium salt and a cresol novolac resin for the bottom polymer layer. The resist formation processes, insolubilization mechanism, and the resolution capability of the new two-layer resist are discussed.

Biobased Epoxy Nanocomposites Derived from Lignin-Based Monomers.

Science.gov (United States)

Zhao, Shou; Abu-Omar, Mahdi M

2015-07-13

Biobased epoxy nanocomposites were synthesized based on 2-methoxy-4-propylphenol (dihydroeugenol, DHE), a molecule that has been obtained from the lignin component of biomass. To increase the content of hydroxyl groups, DHE was o-demethylated using aqueous HBr to yield propylcatechol (DHEO), which was subsequently glycidylated to epoxy monomer. Optimal conditions in terms of yield and epoxy equivalent weight were found to be 60 °C with equal NaOH/phenolic hydroxyl molar ratio. The structural evolution from DHE to cured epoxy was followed by (1)H NMR and Fourier transform infrared spectroscopy. The nano-montmorillonite modified DHEO epoxy exhibited improved storage modulus and thermal stability as determined from dynamic mechanical analysis and thermogravimetric analysis. This study widens the synthesis routes of biobased epoxy thermosets from lignin-based molecules.

Organic materials for semiconductor. Epoxy molding compound for IC encapsulation; Handotai kanren no yuki zairyo. Handotai fushiyo epoxy seikei zairyo ni tsuite

Energy Technology Data Exchange (ETDEWEB)

Kusuhara, A. [Sumitomo Bakelite Co. Ltd., Tokyo (Japan)

1998-11-05

This paper describes organic materials for semiconductor. Based on the composition and raw material, typical materials are epoxy resins, curing agents including phenol-novolak resins, fillers including silica and alumina, flame retardants including brominated epoxy resin and antimony oxide, hardening accelerators including amine compounds and phosphorus compounds, coupling agents including silane compounds and titanate compounds, and the others including colorants and mold lubricants. Raw materials are heated and kneaded after mixing, and produced as tablets after cooling and crushing. Recently, the packages have changed from insertion type to surface mounting type for the small thin IC package and for improving the efficiency of soldering during the incorporation of IC package on the print circuit substrate. High temperature of 260degC has been employed from the conventional limit of 100degC. Reduction of water absorption, improvement of adhesion, reduction of thermal expansion coefficient, and reduction of elastic modulus during heating are promoted for avoiding the peeling and cracking due to the sudden evaporation of adsorbed moisture. This paper also describes the organic materials for BGA. 10 figs., 4 tabs.

Effects of cryogenic reactor irradiation on organic insulators

International Nuclear Information System (INIS)

Kato, Teruo

1995-01-01

Insulators for the superconducting magnets of fusion reactor are classified as electrical and thermal insulators for which tough organic materials will be used. When the magnet is exposed by fast neutrons and gamma-rays from plasma in a fusion reactor, the fusion reactor systems will cause fatal damage by the degradation of insulators. Therefore, it is necessary to select materials resistant irradiation damage for use as insulators. Electrical and mechanical tests were carried out at 4.2 K without warmup after the reactor irradiation at 5 K. The effects of reactor irradiation at the dose of 10 7 Gy on epoxy resins (bisphenol-A), G-10 CR, VL-E 200 and G-11 CR caused large decreases in mechanical strength. Polyetheretherketone (PEEK), polyimide and phenol novolac resins, which were used to laminate reinforced plastics with glass-cloth against irradiation, showed good resistance. Effects of cryogenic reactor irradiation on several organic materials and epoxy laminate-reinforced plastics with glass-cloth and Kevlar-cloth were also discussed. (author)

Chromatographic assessment of two hybrid monoliths prepared via epoxy-amine ring-opening polymerization and methacrylate-based free radical polymerization using methacrylate epoxy cyclosiloxane as functional monomer.

Science.gov (United States)

Wang, Hongwei; Ou, Junjie; Lin, Hui; Liu, Zhongshan; Huang, Guang; Dong, Jing; Zou, Hanfa

2014-11-07

Two kinds of hybrid monolithic columns were prepared by using methacrylate epoxy cyclosiloxane (epoxy-MA) as functional monomer, containing three epoxy moieties and one methacrylate group. One column was in situ fabricated by ring-opening polymerization of epoxy-MA and 1,10-diaminodecane (DAD) using a porogenic system consisting of isopropanol (IPA), H2O and ethanol at 65°C for 12h. The other was prepared by free radical polymerization of epoxy-MA and ethylene dimethacrylate (EDMA) using 1-propanol and 1,4-butanediol as the porogenic solvents at 60°C for 12h. Two hybrid monoliths were investigated on the morphology and chromatographic assessment. Although two kinds of monolithic columns were prepared with epoxy-MA, their morphologies looked rather different. It could be found that the epoxy-MA-DAD monolith possessed higher column efficiencies (25,000-34,000plates/m) for the separation of alkylbenzenes than the epoxy-MA-EDMA monolith (12,000-13,000plates/m) in reversed-phase nano-liquid chromatography (nano-LC). Depending on the remaining epoxy or methacrylate groups on the surface of two pristine monoliths, the epoxy-MA-EDMA monolith could be easily modified with 1-octadecylamine (ODA) via ring-opening reaction, while the epoxy-MA-DAD monolith could be modified with stearyl methacrylate (SMA) via free radical reaction. The chromatographic performance for the separation of alkylbenzenes on SMA-modified epoxy-MA-DAD monolith was remarkably improved (42,000-54,000 plates/m) when compared with that on pristine epoxy-MA-DAD monolith, while it was not obviously enhanced on ODA-modified epoxy-MA-EDMA monolith when compared with that on pristine epoxy-MA-EDMA monolith. The enhancement of the column efficiency of epoxy-MA-DAD monolith after modification might be ascribed to the decreased mass-transfer resistence. The two kinds of hybrid monoliths were also applied for separations of six phenols and seven basic compounds in nano-LC. Copyright © 2014 Elsevier B.V. All

Gamma ray induced electrical conductivity in bisphenol-A type epoxy resin and polyethylene terephthalate

International Nuclear Information System (INIS)

Maeda, Hideaki; Nakakita, Tsuneo

1978-01-01

The insulation materials to support magnets for nuclear fusion reactors are exposed to high energy neutron beam and the gamma ray due to the accompanying induced radio activity through blankets or radiation shields. In such materials, radiation-induced conduction (RIC) is a problem, which occurs due to the charged particles generated in the insulation materials during irradiation. As one of such materials, use of epoxy composite material is expected, but its RIC has been scarcely measured. An approach to measure the wave form of transient current (or electric charge) caused by irradiating the radiation pulses of nano-second order to the materials has been developed. This paper reports the results of having measured RIC in bisphenol-A type epoxy resin at the electric field from 1 x 10 4 to 3 x 10 5 V/cm and γ dose rate from 9 x 10 3 to 9 x 10 5 R/h over the temperature range of -170 deg. C to +110 deg. C. The RIC of polyethylene terephthalate (PET) was also measured in the same regions, whose molecular structure is comparatively similar to the bisphenol-A type epoxy resin, and of which the fundamental processes for RIC have been clarified pretty well. The radiation sources of 4.3 kCi 60 Co of NAIG and 45 kCi 60 Co of JAERI were used. The experimental circuits and the cryostat are described, then as for the results, explanation and discussion are given to the characteristics of induced current, dependence on dose rate and dependence on temperature of RIC conductivity. The process of capturing carrier in deep traps seems to be dominant in the bisphenol-A type epoxy resin, similarly to that of PET. (Wakatsuki, Y.)

Experimental investigation of coating degradation during simultaneous acid and erosive particle exposure

DEFF Research Database (Denmark)

Møller, Victor Buhl; Dam-Johansen, Kim; Frankær, Sarah Maria

When used in industrial processes, such as stirred acid leaching in the mineral industry, thermoset coatings are exposed to a combination of aggressive chemicals and erosive particlewear. While each exposure condition has been studied separately, no research has been presented on the effects...... of a simultaneous exposure. To investigate this, a pilot-scale stirred acid leaching tank, containing erosive particles and acidic solutions, has been designed and constructed. Resin types considered are amine-cured novolac epoxy and vinyl ester. Transient coating degradation is mapped through visual inspection...

A novel method based on selective laser sintering for preparing high-performance carbon fibres/polyamide12/epoxy ternary composites

Science.gov (United States)

Zhu, Wei; Yan, Chunze; Shi, Yunsong; Wen, Shifeng; Liu, Jie; Wei, Qingsong; Shi, Yusheng

2016-09-01

A novel method based on selective laser sintering (SLS) process is proposed for the first time to prepare complex and high-performance carbon fibres/polyamide12/epoxy (CF/PA12/EP) ternary composites. The procedures are briefly described as follows: prepare polyamide12 (PA12) coated carbon fibre (CF) composite powder; build porous green parts by SLS; infiltrate the green parts with high-performance thermosetting epoxy (EP) resin; and finally cure the resin at high temperature. The obtained composites are a ternary composite system consisting of the matrix of novolac EP resin, the reinforcement of CFs and the transition thin layer of PA12 with a thickness of 595 nm. The SEM images and micro-CT analysis prove that the ternary system is a three-dimensional co-continuous structure and the reinforcement of CFs are well dispersed in the matrix of EP with the volume fraction of 31%. Mechanical tests show that the composites fabricated by this method yield an ultimate tensile strength of 101.03 MPa and a flexural strength of 153.43 MPa, which are higher than those of most of the previously reported SLS materials. Therefore, the process proposed in this paper shows great potential for manufacturing complex, lightweight and high-performance CF reinforced composite components in aerospace, automotive industries and other areas.

Graphene and Carbon Nanotubes Synergistically Improved the Thermal Conductivity of Phenolic Resin

OpenAIRE

Wang Han

2017-01-01

People discover the synergistic effect of graphene and carbon nanotubes on heat conduction in graphene carbon nanotubes / epoxy resin hybrid composites. In this article we added them into the phenolic resin and test the thermal conductivity. We found the thermal conductivity was increased by 6.5% in the phenolic resin by adding 0.45wt% graphene and 0.15wt% single wall carbon nanotubes (maintain the mass ratio 3:1). So if graphene and carbon nanotubes are added in proportion, thermal conductiv...

PREPARATION OF NOVOLACS USING PHENOLIC RICH ...

African Journals Online (AJOL)

Preferred Customer

Institute of Chemical Industry of Forest Products, CAF; National Engineering Laboratory for. Biomass Chemical Utilization; Key and Open Laboratory on Forest Chemical Engineering,. SFA, Nanjing 210042 ... INTRODUCTION ..... chemical composition of the bio-oil tends to change toward thermodynamic equilibrium and.

Comparison of structural health assessment capabilities in epoxy – carbon black and epoxy – carbon nanotube nanocomposites

OpenAIRE

F. Inam; B. R. Bhat; N. Luhyna; T. Vo

2014-01-01

A novel method for comparing structural health of different types of brittle epoxy nanocomposites filled with carbon nanostructured fillers is presented. Epoxy – 0.2 vol% carbon black (CB) and epoxy – 0.2 vol% carbon nanotube (CNT) nanocomposite bars were prepared by calendering and thermal curing. Nanocomposite bars were subjected to Vickers diamond indentation to produce sub-surface damage. Electrical conductivities were analysed by 4-point method to estimate the structural damage caused by...

Photo-assisted Fenton type processes for the degradation of phenol: A kinetic study

International Nuclear Information System (INIS)

Kusic, Hrvoje; Koprivanac, Natalija; Bozic, Ana Loncaric; Selanec, Iva

2006-01-01

In this study the application of advanced oxidation processes (AOPs), dark Fenton and photo-assisted Fenton type processes; Fe 2+ /H 2 O 2 , Fe 3+ /H 2 O 2 , Fe 0 /H 2 O 2 , UV/Fe 2+ /H 2 O 2 , UV/Fe 3+ /H 2 O 2 and UV/Fe 0 /H 2 O 2 , for degradation of phenol as a model organic pollutant in the wastewater was investigated. A detail kinetic modeling which describes the degradation of phenol was performed. Mathematical models which predict phenol decomposition and formation of primary oxidation by-products: catechol, hydroquinone and benzoquinone, by applied processes were developed. The study also consist the modeling of mineralization kinetic of the phenol solution by applied AOPs. This part, besides well known reactions of Fenton and photo-Fenton chemistry, involves additional reactions which describe removal of iron from catalytic cycle through formation of ferric complexes and its regeneration induced by UV radiation. Phenol decomposition kinetic was monitored by HPLC analysis and total organic carbon content measurements (TOC). Complete phenol removal was obtained by all applied processes. Residual TOC by applied Fenton type processes ranged between 60.2 and 44.7%, while the efficiency of those processes was significantly enhanced in the presence of UV light, where residual TOC ranged between 15.2 and 2.4%

Wettability of nano-epoxies to UHMWPE fibers.

Science.gov (United States)

Neema, S; Salehi-Khojin, A; Zhamu, A; Zhong, W H; Jana, S; Gan, Y X

2006-07-01

Ultra high molecular weight polyethylene (UHMWPE) fibers have a unique combination of outstanding mechanical, physical, and chemical properties. However, as reinforcements for manufacturing high performance composite materials, UHMWPE fibers have poor wettability with most polymers. As a result, the interfacial bonding strength between the fibers and polymer matrices is very low. Recently, developing so-called nano-matrices containing reactive graphitic nanofibers (r-GNFs) has been proposed to promote the wetting of such matrices to certain types of fiber reinforcements. In this work, the wettability of UHMWPE fibers with different epoxy matrices including a nano-epoxy, and a pure epoxy was investigated. Systematic experimental work was conducted to determine the viscosity of the epoxies, the contact angle between the epoxies and the fibers. Also obtained are the surface energy of the fibers and the epoxies. The experimental results show that the wettability of the UHMWPE fibers with the nano-epoxy is much better than that of the UHMWPE fibers with the pure epoxy.

Effect of epoxy resin on bending momentum in L type corner joins

Directory of Open Access Journals (Sweden)

Mehmet Nuri Yıldırım

2017-11-01

Full Text Available In the furniture industry, the joining points of frame and box construction furniture according to the loads to be affected by the use place is important for the security of the user and service life of the furniture element. In this direction, it is aimed to determine the diagonal compression and diagonal tensile moment values of "L" type corner joints of box framed construction furniture prepared from solid wood materials. The Pinus Nigra, Fagus Orientalis L and Populus Nigra were used as solid wood materials. Wood-based biscuit joining elements were used in corner joints of the test construction and epoxy resin was used as glue for materials. The static loads were applied to construction according to ASTM-D1037. The results show that, the highest tensile and compression values were obtained from Fagus Orientalis L and the lowest values were obtained from Populus Nigra specimens. In the statistical study, the difference between the tensile and compressive bending moment values of the biscuit connection element was found to be statistically significant. This study indicates that, it is suggested to use of L type joints prepared from Fagus Orientalis L by using epoxy resin and wood based biscuit joining element in frame constructions.

Role of surface thermal properties of HfB2 nanoparticles on heat ...

Indian Academy of Sciences (India)

2018-02-02

Feb 2, 2018 ... flow in MWCNT/novolac composites ... C to investigate the thermal behaviour and the mechanism of mass loss of the samples. Two phenolic matrix ..... endothermic gases undergo heat exchange with the incoming heat flux ...

Curing behaviors and properties of an extrinsic toughened epoxy/anhydride system and an intrinsic toughened epoxy/anhydride system

International Nuclear Information System (INIS)

Fan, Mengjin; Liu, Jialin; Li, Xiangyuan; Cheng, Jue; Zhang, Junying

2013-01-01

Highlights: ► Two curing systems (ETRS and ITRS) with similar chemical composite were prepared. ► The curing kinetics of the ETRS and the novel ITRS were comparatively studied. ► Crosslinking density can affect the kinetic schemes of the two curing systems. ► Their mechanical properties and thermal stabilities were also comparatively studied. ► Crosslinking density may play an influential role in mechanical properties. - Abstract: The curing kinetics of an extrinsic toughened epoxy (mixture of diglycidyl ether of bisphenol-A and 1,4-butanediol epoxy resin, DGEBA/DGEBD) and an intrinsic toughened epoxy (ethoxylated bisphenol-A epoxy resin with two oxyethylene units, DGEBAEO-2) using hexahydrophthalic anhydride (HHPA) as curing agent and tris-(dimethylaminomethyl) phenol (DMP-30) as accelerator were comparatively studied by non-isothermal DSC with a model-fitting Málek approach and a model-free advanced isoconversional method of Vyazovkin. The dynamic mechanical properties and thermal stabilities of the cured materials were investigated by DMTA and TGA, respectively. The results showed that Šesták–Berggren model can generally simulate well the reaction rates of these two systems. The activation energy of DGEBA/DGEBD/HHPA/DMP-30 at high fractional conversion changed much higher than that of DGEBAEO-2/HHPA/DMP-30, indicating the increased steric hindrance mainly affected the reaction kinetic scheme of DGEBA/DGEBD/HHPA/DMP-30. The T g and storage moduli of cured DGEBAEO-2/HHPA/DMP-30 were lower than those of cured DGEBA/DGEBD/HHPA/DMP-30 according to DMTA while TGA showed that the thermal stabilities of these two cured systems were similar

Curing behaviors and properties of an extrinsic toughened epoxy/anhydride system and an intrinsic toughened epoxy/anhydride system

Energy Technology Data Exchange (ETDEWEB)

Fan, Mengjin; Liu, Jialin; Li, Xiangyuan [Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing 100029 (China); Cheng, Jue, E-mail: chengjue@mail.buct.edu.cn [Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing 100029 (China); Zhang, Junying, E-mail: zjybuct@gmail.com [Key Laboratory of Carbon Fiber and Functional Polymers, Ministry of Education, Beijing University of Chemical Technology, Beijing 100029 (China)

2013-02-20

Highlights: ► Two curing systems (ETRS and ITRS) with similar chemical composite were prepared. ► The curing kinetics of the ETRS and the novel ITRS were comparatively studied. ► Crosslinking density can affect the kinetic schemes of the two curing systems. ► Their mechanical properties and thermal stabilities were also comparatively studied. ► Crosslinking density may play an influential role in mechanical properties. - Abstract: The curing kinetics of an extrinsic toughened epoxy (mixture of diglycidyl ether of bisphenol-A and 1,4-butanediol epoxy resin, DGEBA/DGEBD) and an intrinsic toughened epoxy (ethoxylated bisphenol-A epoxy resin with two oxyethylene units, DGEBAEO-2) using hexahydrophthalic anhydride (HHPA) as curing agent and tris-(dimethylaminomethyl) phenol (DMP-30) as accelerator were comparatively studied by non-isothermal DSC with a model-fitting Málek approach and a model-free advanced isoconversional method of Vyazovkin. The dynamic mechanical properties and thermal stabilities of the cured materials were investigated by DMTA and TGA, respectively. The results showed that Šesták–Berggren model can generally simulate well the reaction rates of these two systems. The activation energy of DGEBA/DGEBD/HHPA/DMP-30 at high fractional conversion changed much higher than that of DGEBAEO-2/HHPA/DMP-30, indicating the increased steric hindrance mainly affected the reaction kinetic scheme of DGEBA/DGEBD/HHPA/DMP-30. The T{sub g} and storage moduli of cured DGEBAEO-2/HHPA/DMP-30 were lower than those of cured DGEBA/DGEBD/HHPA/DMP-30 according to DMTA while TGA showed that the thermal stabilities of these two cured systems were similar.

High Temperature Epoxy Foam: Optimization of Process Parameters

Directory of Open Access Journals (Sweden)

Samira El Gazzani

2016-06-01

Full Text Available For many years, reduction of fuel consumption has been a major aim in terms of both costs and environmental concerns. One option is to reduce the weight of fuel consumers. For this purpose, the use of a lightweight material based on rigid foams is a relevant choice. This paper deals with a new high temperature epoxy expanded material as substitution of phenolic resin, classified as potentially mutagenic by European directive Reach. The optimization of thermoset foam depends on two major parameters, the reticulation process and the expansion of the foaming agent. Controlling these two phenomena can lead to a fully expanded and cured material. The rheological behavior of epoxy resin is studied and gel time is determined at various temperatures. The expansion of foaming agent is investigated by thermomechanical analysis. Results are correlated and compared with samples foamed in the same temperature conditions. The ideal foaming/gelation temperature is then determined. The second part of this research concerns the optimization of curing cycle of a high temperature trifunctional epoxy resin. A two-step curing cycle was defined by considering the influence of different curing schedules on the glass transition temperature of the material. The final foamed material has a glass transition temperature of 270 °C.

Coarse-grained molecular dynamics simulations of the tensile behavior of a thermosetting polymer.

Science.gov (United States)

Yang, Shaorui; Qu, Jianmin

2014-07-01

Using a previously developed coarse-grained model, we conducted large-scale (∼ 85 × 85 × 85 nm(3)) molecular dynamics simulations of uniaxial-strain deformation to study the tensile behavior of an epoxy molding compound, epoxy phenol novolacs (EPN) bisphenol A (BPA). Under the uniaxial-strain deformation, the material is found to exhibit cavity nucleation and growth, followed by stretching of the ligaments separated by the cavities, until the ultimate failure through ligament scissions. The nucleation sites of cavities are rather random and the subsequent cavity growth accounts for much (87%) of the volumetric change during the uniaxial-strain deformation. Ultimate failure of the materials occurs when the cavity volume fraction reaches ∼ 60%. During the entire deformation process, polymer strands in the network are continuously extended to their linear states and broken in the postyielding strain hardening stage. When most of the strands are stretched to their taut configurations, rapid scission of a large number of strands occurs within a small strain increment, which eventually leads to fracture. Finally, through extensive numerical simulations of various loading conditions in addition to uniaxial strain, we find that yielding of the EPN-BPA can be described by the pressure-modified von Mises yield criterion.

Coarse-grained molecular dynamics simulations of the tensile behavior of a thermosetting polymer

Science.gov (United States)

Yang, Shaorui; Qu, Jianmin

2014-07-01

Using a previously developed coarse-grained model, we conducted large-scale (˜85×85×85nm3) molecular dynamics simulations of uniaxial-strain deformation to study the tensile behavior of an epoxy molding compound, epoxy phenol novolacs (EPN) bisphenol A (BPA). Under the uniaxial-strain deformation, the material is found to exhibit cavity nucleation and growth, followed by stretching of the ligaments separated by the cavities, until the ultimate failure through ligament scissions. The nucleation sites of cavities are rather random and the subsequent cavity growth accounts for much (87%) of the volumetric change during the uniaxial-strain deformation. Ultimate failure of the materials occurs when the cavity volume fraction reaches ˜60%. During the entire deformation process, polymer strands in the network are continuously extended to their linear states and broken in the postyielding strain hardening stage. When most of the strands are stretched to their taut configurations, rapid scission of a large number of strands occurs within a small strain increment, which eventually leads to fracture. Finally, through extensive numerical simulations of various loading conditions in addition to uniaxial strain, we find that yielding of the EPN-BPA can be described by the pressure-modified von Mises yield criterion.

Modification of a Phenolic Resin with Epoxy- and Methacrylate-Functionalized Silica Sols to Improve the Ablation Resistance of Their Glass Fiber-Reinforced Composites

Directory of Open Access Journals (Sweden)

Yu Hu

2014-01-01

Full Text Available Functionalized silica sols were obtained by the hydrolytic condensation of (γ-methacryloxypropyltrimethoxysilane (MPMS, (γ-glycidyloxypropyltrimethoxysilane (GPMS and tetraethoxysilane (TEOS. Three different sols were obtained: MPS (derived from MPMS and TEOS, GPS-MPS (derived from GPMS, MPMS and TEOS, and GPSD (derived from GPMS, TEOS and diglycidyl ether of bisphenol A, DGEBA. These silica sols were mixed with a phenolic resin (PR. Ethylenediamine was used as a hardener for epoxy-functionalized sols and benzoyl peroxide was used as an initiator of the free-radical polymerization of methacrylate-functionalized silica sols. Glass fiber-reinforced composites were obtained from the neat PR and MPS-PR, GPS-MPS-PR and GPSD-PR. The resulting composites were evaluated as ablation resistant materials in an acetylene-oxygen flame. A large increase in the ablation resistance was observed when the PR was modified by the functionalized silica sols. The ablation resistance of the composites decreased as follows: GPSD-PR > MPS-PR > GPS-MPS-PR > PR.

Features of nanomodifiers synthesis based on trifunctional oxyphenyls for mineral suspensions

Directory of Open Access Journals (Sweden)

Shapovalov Nikolay Afanasyevich

2016-10-01

Full Text Available The focused influence on the rheological characteristics of highly-concentrated mineral suspensions used in the building industry is possible due to the directed synthesis of nano-sized macromolecules that have the certain structure and high adsorbing capacity on the surface of mineral particles and that are able to modify the boundary layer composition. The adsorbing capacity of organic compounds depends mostly on the hydrocarbon chain length and the molecular weight of the compound. The result of the condensate interaction of phenol and its derivatives with aldehydes is oligomers and polymers whose structure depends on the phenol functionality, the kind of aldehyde, molecular ration of reagents, the Ph medium of the reaction. So, changing the type or the functionality of initial monomers or the synthesis conditions one can produce linear thermoplastic oligomers (novolacs or highly branched thermosetting oligomers (resols. It has been found that the resole production takes place under softer conditions, and there is no necessity to neutralize reaction products as with novolac production that usually requires acid environment. A number of thermosetting oligomers based on trifunctional polyatomic phenols have been synthesized. The theoretical and practical characteristics of resole oligomer synthesis have been studied, synthesis optimal conditions have been determined, the composition and structure of macromolecules were revealed by the methods of infrared spectroscopy, proton magnetic resonance spectroscopy, liquid chromatography and conductivity measurement, the length of the enlarged oligomer molecule was calculated. Obtained compounds can be qualified as nanoscaled modifiers of mineral dispersions.

OPTIMASI PROSES POLIMERISASI MINYAK KULIT JAMBU METE (CNSL, CASHEW NUT SHELL LIQUID DENGAN FORMALDEHID

Directory of Open Access Journals (Sweden)

Luqman Buchori

2012-02-01

Full Text Available Jambu mete represents the crop which is a lot of its benefit. From various benefit of jambu mete, there is onepart of which not yet been exploited in an optimal that is husk. Whereas in its husk is contain oil so-calledCashew Nut Shell Liquid (CNSL about 32-36%. This oil can be used as natural source phenol and alternativelysubstitution phenol from petroleum. This phenol is reacted by formaldehyde will form the phenol formaldehyderesin. Besides containing natural phenol, CNSL also contain the other bunch like karboksilat bunch, alkylbunch and alkenes bunch. This bunch will influence process of forming of phenol formaldehyde resin as aconsequence have an effect on characteristic and quality of resin so that require to be searched the optimumcondition in making of phenol formaldehyde resin. Objective of this research is to look for the optimumcondition in making of phenol formaldehyde resin of novolac type and also know the influence of comparison ofreactant and operating temperature for to resin yielded. Dependent variables in this research are reactorvolume (500 ml with the volume bases 250 ml, catalyst acid HCl, mixing speed (200 rpm, operating time (90minute, pH (2 and operating pressure (1 atm. Independent variables are CNSL/formaldehyde ratio andoperating temperature. Perceived parameter is free rate formaldehyde. Method is used to design and processdata is RSM (Response Surface Methodology method constructively the Static program. Result of this researchindicates that the most effect on variable is ratio CNSL/formaldehyde. Optimum condition are obtained at F/Cratio of 0.65-0.85 and temperature of 75-850C with the conversion of 0.55. The biggest rate resin obtained atF/C ratio 0.75/1 and temperature 80oC. This resin is very jell and have best sticky and also drug after runningdry. This novolac resin is applicated as furniture coating. Coating yielded have well sticky with the auburncolor.

Emissions of fine particulate nitrated phenols from the burning of five common types of biomass.

Science.gov (United States)

Wang, Xinfeng; Gu, Rongrong; Wang, Liwei; Xu, Wenxue; Zhang, Yating; Chen, Bing; Li, Weijun; Xue, Likun; Chen, Jianmin; Wang, Wenxing

2017-11-01

Nitrated phenols are among the major constituents of brown carbon and affect both climates and ecosystems. However, emissions from biomass burning, which comprise one of the most important primary sources of atmospheric nitrated phenols, are not well understood. In this study, the concentrations and proportions of 10 nitrated phenols, including nitrophenols, nitrocatechols, nitrosalicylic acids, and dinitrophenol, in fine particles from biomass smoke were determined under three different burning conditions (flaming, weakly flaming, and smoldering) with five common types of biomass (leaves, branches, corncob, corn stalk, and wheat straw). The total abundances of fine nitrated phenols produced by biomass burning ranged from 2.0 to 99.5 μg m -3 . The compositions of nitrated phenols varied with biomass types and burning conditions. 4-nitrocatechol and methyl nitrocatechols were generally most abundant, accounting for up to 88-95% of total nitrated phenols in flaming burning condition. The emission ratios of nitrated phenols to PM 2.5 increased with the completeness of combustion and ranged from 7 to 45 ppmm and from 239 to 1081 ppmm for smoldering and flaming burning, respectively. The ratios of fine nitrated phenols to organic matter in biomass burning aerosols were comparable to or lower than those in ambient aerosols affected by biomass burning, indicating that secondary formation contributed to ambient levels of fine nitrated phenols. The emission factors of fine nitrated phenols from flaming biomass burning were estimated based on the measured mass fractions and the PM 2.5 emission factors from literature and were approximately 0.75-11.1 mg kg -1 . According to calculations based on corn and wheat production in 31 Chinese provinces in 2013, the total estimated emission of fine nitrated phenols from the burning of corncobs, corn stalks, and wheat straw was 670 t. This work highlights the apparent emission of methyl nitrocatechols from biomass burning and

Comparison of structural health assessment capabilities in epoxy – carbon black and epoxy – carbon nanotube nanocomposites

Directory of Open Access Journals (Sweden)

F. Inam

2014-01-01

Full Text Available A novel method for comparing structural health of different types of brittle epoxy nanocomposites filled with carbon nanostructured fillers is presented. Epoxy – 0.2 vol% carbon black (CB and epoxy – 0.2 vol% carbon nanotube (CNT nanocomposite bars were prepared by calendering and thermal curing. Nanocomposite bars were subjected to Vickers diamond indentation to produce sub-surface damage. Electrical conductivities were analysed by 4-point method to estimate the structural damage caused by indentation. For comprehensive comparison, fracture toughness and percolation threshold were analysed as well. Because of the systematically induced indentation damage, a sharp decrease of 89% was observed in the electrical conductivity of epoxy – CNT nanocomposite as compared to 25% in the electrical conductivity of epoxy – CB nanocomposite. CNTs impart superior damage sensing capability in brittle nanocomposite structures, in comparison to CB, due to their high aspect ratio (fibrous nature and high electrical conductivity.

Emissions of fine particulate nitrated phenols from the burning of five common types of biomass

International Nuclear Information System (INIS)

Wang, Xinfeng; Gu, Rongrong; Wang, Liwei; Xu, Wenxue; Zhang, Yating; Chen, Bing; Li, Weijun; Xue, Likun; Chen, Jianmin; Wang, Wenxing

2017-01-01

Nitrated phenols are among the major constituents of brown carbon and affect both climates and ecosystems. However, emissions from biomass burning, which comprise one of the most important primary sources of atmospheric nitrated phenols, are not well understood. In this study, the concentrations and proportions of 10 nitrated phenols, including nitrophenols, nitrocatechols, nitrosalicylic acids, and dinitrophenol, in fine particles from biomass smoke were determined under three different burning conditions (flaming, weakly flaming, and smoldering) with five common types of biomass (leaves, branches, corncob, corn stalk, and wheat straw). The total abundances of fine nitrated phenols produced by biomass burning ranged from 2.0 to 99.5 μg m −3 . The compositions of nitrated phenols varied with biomass types and burning conditions. 4-nitrocatechol and methyl nitrocatechols were generally most abundant, accounting for up to 88–95% of total nitrated phenols in flaming burning condition. The emission ratios of nitrated phenols to PM 2.5 increased with the completeness of combustion and ranged from 7 to 45 ppmm and from 239 to 1081 ppmm for smoldering and flaming burning, respectively. The ratios of fine nitrated phenols to organic matter in biomass burning aerosols were comparable to or lower than those in ambient aerosols affected by biomass burning, indicating that secondary formation contributed to ambient levels of fine nitrated phenols. The emission factors of fine nitrated phenols from flaming biomass burning were estimated based on the measured mass fractions and the PM 2.5 emission factors from literature and were approximately 0.75–11.1 mg kg −1 . According to calculations based on corn and wheat production in 31 Chinese provinces in 2013, the total estimated emission of fine nitrated phenols from the burning of corncobs, corn stalks, and wheat straw was 670 t. This work highlights the apparent emission of methyl nitrocatechols from biomass burning

Prediction of brittle fracture of epoxy-aluminum flanging

Directory of Open Access Journals (Sweden)

Korbel J.

2010-07-01

Full Text Available This paper presents a fracture mechanical approach for estimation of critical bending load of different types of aluminum-epoxy flanging and comparison with experimental measurements. For this purpose, several designs of the flanges were investigated. The flanges were glued to the epoxy bars and adhesive-epoxy interface was considered as a bi-material notch. Prediction of the failure is based on generalized stress intensity factor and generalized fracture toughness.

Epoxy cracking in the epoxy-impregnated superconducting winding: nonuniform dissipation of stress energy in a wire-epoxy matrix model

International Nuclear Information System (INIS)

Tsukamoto, O.; Iwasa, Y.

1985-01-01

The authors present the epoxy-crack-induced temperature data of copper wires imbedded in wire-epoxy resin composite model at 4.2 K. The experimental results show that the epoxy-crackinduced temperature rise is higher in the copper wires than in the epoxy matrix, indicating that in stress-induced wire-epoxy failure, stress energy stored in the wire-epoxy matrix is preferrentially dissipated in the wire. A plausible mechanism of the nonuniform dissipation is presented

Positron lifetime study of electron-irradiated epoxy resins

International Nuclear Information System (INIS)

Suevegh, K.; Vertes, A.; Wojnarovits, L.; Foeldiak, G.; Liszkai, L.; Kajcsos, Zs.

1990-01-01

Two bisphenol-A type epoxy resins were irradiated by electron beam and studied afterwards by positron lifetime spectroscopy. An interesting result is that despite of the considerable amount of free-radicals, no inhibition of positronium formation was observed in the two epoxies. Nevertheless, several serious differences were detected between the studied polymers. The results suggest that the radiation-resistant properties of epoxies depend strongly on the amount of the curing agent. (author) 8 refs.; 2 figs

Simultaneous acid exposure and erosive particle wear of thermoset coatings

DEFF Research Database (Denmark)

Møller, Victor Buhl; Dam-Johansen, Kim; Frankær, Sarah Maria

2018-01-01

, similar to the erosion/corrosion-type phenomena found in metals. A vinyl ester-based coating was the most resistant to the simultaneous erosive/acidic exposure, with a maximum polishing rate of 3.24±0.61 μm/week, while novolac epoxy and polyurethane coatings showed high polishing rates of 11.7±1.50 and 13.4±0......Handling acidic chemicals is a challenge in the chemical industry, requiring a careful choice of contact material. Certain thermoset organic coatings are applicable in low pH environments, but when particulate erosion is also present the performance demand is increased. This is the case in, e...

Cure monitoring of epoxy resin by using fiber bragg grating sensor

Energy Technology Data Exchange (ETDEWEB)

Lee, Jin Hyuk [KEPCO, Naju (Korea, Republic of); Kim, Dae Hyun [Dept. of Mechanical and Automotive Engineering, Seoul National University of Science and Technology, Seoul (Korea, Republic of)

2016-06-15

In several industrial fields, epoxy resin is widely used as an adhesive for co-curing and manufacturing various structures. Controlling the manufacturing process is required for ensuring robust bonding performance and the stability of the structures. A fiber optic sensor is suitable for the cure monitoring of epoxy resin owing to the thready shape of the sensor. In this paper, a fiber Bragg grating (FBG) sensor was applied for the cure monitoring of epoxy resin. Based on the experimental results, it was demonstrated that the FBG sensor can monitor the status of epoxy resin curing by measuring the strain caused by volume shrinkage and considering the compensation of temperature. In addition, two types of epoxy resin were used for the cure-monitoring; moreover, when compared to each other, it was found that the two types of epoxy had different cure-processes in terms of the change of strain during the curing. Therefore, the study proved that the FBG sensor is very profitable for the cure-monitoring of epoxy resin.

Catalytic removal of phenol from gas streams by perovskite-type catalysts.

Science.gov (United States)

Chen, Dai Ling; Pan, Kuan Lun; Chang, Moo Been

2017-06-01

Three perovskite-type catalysts prepared by citric acid method are applied to remove phenol from gas streams with the total flow rate of 300mL/min, corresponding to a GHSV of 10,000/hr. LaMnO 3 catalyst is first prepared and further partially substituted with Sr and Cu to prepare La 0.8 Sr 0.2 MnO 3 and La 0.8 Sr 0.2 Mn 0.8 Cu 0.2 O 3 , and catalytic activities and fundamental characteristics of these three catalysts are compared. The results show that phenol removal efficiency achieved with La 0.8 Sr 0.2 Mn 0.8 Cu 0.2 O 3 reaches 100% with the operating temperature of 200°C and the rate of mineralization at 300°C is up to 100%, while the phenol removal efficiencies achieved with La 0.8 Sr 0.2 MnO 3 and LaMnO 3 are up to 100% with the operating temperature of 300°C and 400°C, respectively. X-ray photoelectron spectroscopy (XPS) analysis shows that the addition of Sr and Cu increases the lattice oxygen of La 0.8 Sr 0.2 Mn 0.8 Cu 0.2 O 3 , and further increases mobility or availability of lattice oxygen. The results indicate that La 0.8 Sr 0.2 Mn 0.8 Cu 0.2 O 3 has the best activity for phenol removal among three catalysts prepared and the catalytic activity of phenol oxidation is enhanced by the introduction of Sr and Cu into LaMnO 3 . Apparent activation energy of 48kJ/mol is calculated by Mars-Van Krevelen Model for phenol oxidation with La 0.8 Sr 0.2 Mn 0.8 Cu 0.2 O 3 as catalyst. Copyright © 2016. Published by Elsevier B.V.

Toughening Mechanisms in Silica-Filled Epoxy Nanocomposites

Science.gov (United States)

Patel, Binay S.

Epoxies are widely used as underfill resins throughout the microelectronics industry to mechanically couple and protect various components of flip-chip assemblies. Generally rigid materials largely surround underfill resins. Improving the mechanical and thermal properties of epoxy resins to better match those of their rigid counterparts can help extend the service lifetime of flip-chip assemblies. Recently, researchers have demonstrated that silica nanoparticles are effective toughening agents for lightly-crosslinked epoxies. Improvements in the fracture toughness of silica-filled epoxy nanocomposites have primarily been attributed to two toughening mechanisms: particle debonding with subsequent void growth and matrix shear banding. Various attempts have been made to model the contribution of these toughening mechanisms to the overall fracture energy observed in silica-filled epoxy nanocomposites. However, disparities still exist between experimental and modeled fracture energy results. In this dissertation, the thermal, rheological and mechanical behavior of eight different types of silica-filled epoxy nanocomposites was investigated. Each nanocomposite consisted of up to 10 vol% of silica nanoparticles with particle sizes ranging from 20 nm to 200 nm, with a variety of surface treatments and particle structures. Fractographical analysis was conducted with new experimental approaches in order to accurately identify morphological evidence for each proposed toughening mechanism. Overall, three major insights into the fracture behavior of real world silica-filled epoxy nanocomposites were established. First, microcracking was observed as an essential toughening mechanism in silica-filled epoxy nanocomposites. Microcracking was observed on the surface and subsurface of fractured samples in each type of silica-filled epoxy nanocomposite. The additional toughening contribution of microcracking to overall fracture energy yielded excellent agreement between experimental

Enhancement of mechanical properties of epoxy/graphene nanocomposite

Science.gov (United States)

Berhanuddin, N. I. C.; Zaman, I.; Rozlan, S. A. M.; Karim, M. A. A.; Manshoor, B.; Khalid, A.; Chan, S. W.; Meng, Q.

2017-10-01

Graphene is a novel class of nanofillers possessing outstanding characteristics including most compatible with most polymers, high absolute strength, high aspect ratio and cost effectiveness. In this study, graphene was used to reinforce epoxy as a matrix, to enhance its mechanical properties. Two types of epoxy composite were developed which are epoxy/graphene nanocomposite and epoxy/modified graphene nanocomposite. The fabrication of graphene was going through thermal expansion and sonication process. Chemical modification was only done for modified graphene where 4,4’-Methylene diphenyl diisocyanate (MDI) is used. The mechanical properties of both nanocomposite, such as Young’s modulus and maximum stress were investigated. Three weight percentage were used for this study which are 0.5 wt%, 1.0 wt% and 1.5 wt%. At 0.5 wt%, modified and unmodified shows the highest value compared to neat epoxy, where the value were 8 GPa, 6 GPa and 0.675 GPa, respectively. For maximum stress, neat epoxy showed the best result compared to both nanocomposite due to the changes of material properties when adding the filler into the matrix. Therefore, both nanocomposite increase the mechanical properties of the epoxy, however modification surface of graphene gives better improvement.

Modification of (DGEBA epoxy resin with maleated depolymerised natural rubber

Directory of Open Access Journals (Sweden)

2008-04-01

Full Text Available In this work, diglycidyl ether of bisphenol A (DEGBA type epoxy resin has been modified with maleated depolymerised natural rubber (MDPR. MDPR was prepared by grafting maleic anhydride onto depolymerised natural rubber. MDPR has been characterized by Fourier transform infrared (FT-IR spectroscopy and nuclear magnetic resonance spectroscopy. MDPR was blended with epoxy resin at three different ratios (97/3, 98/2 and 99/1, by keeping the epoxy resin component as the major phase and maleated depolymerised natural rubber component as the minor phase. The reaction between the two blend components took place between the acid/anhydride group in the MDPR and the epoxide group of the epoxy resin. The proposed reaction schemes were supported by the FT-IR spectrum of the uncured Epoxy/MDPR blends. The neat epoxy resin and Epoxy/MDPR blends were cured by methylene dianiline (DDM at 100°C for three hours. Thermal, morphological and mechanical properties of the neat epoxy and the blends were investigated. Free volume studies of the cured, neat epoxy and Epoxy/MDPR blends were correlated with the morphological and mechanical properties of the same systems using Positron Annihilation Lifetime Studies.

Realtime 3D stress measurement in curing epoxy packaging

DEFF Research Database (Denmark)

Richter, Jacob; Hyldgård, A.; Birkelund, Karen

2007-01-01

This paper presents a novel method to characterize stress in microsystem packaging. A circular p-type piezoresistor is implemented on a (001) silicon chip. We use the circular stress sensor to determine the packaging induced stress in a polystyrene tube filled with epoxy. The epoxy curing process...

Epoxy composites based on inexpensive tire waste filler

Science.gov (United States)

Ahmetli, Gulnare; Gungor, Ahmet; Kocaman, Suheyla

2014-05-01

Tire waste (TW) was recycled as raw material for the preparation of DGEBA-type epoxy composite materials. The effects of filler amount and epoxy type on the mechanical properties of the composites were investigated. Tensile strength and Young's modulus of the composites with NPEL were generally higher than composites with NPEF. The appropriate mass level for TW in both type composites was found to be 20 wt%. The equilibrium water sorption of NPEL/TW and NPEF/TW composites for 14-day immersion was determined as 0.10 % and 0.21 %, respectively. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used for characterization of the composites.

Epoxy composites based on inexpensive tire waste filler

International Nuclear Information System (INIS)

Ahmetli, Gulnare; Gungor, Ahmet; Kocaman, Suheyla

2014-01-01

Tire waste (TW) was recycled as raw material for the preparation of DGEBA-type epoxy composite materials. The effects of filler amount and epoxy type on the mechanical properties of the composites were investigated. Tensile strength and Young’s modulus of the composites with NPEL were generally higher than composites with NPEF. The appropriate mass level for TW in both type composites was found to be 20 wt%. The equilibrium water sorption of NPEL/TW and NPEF/TW composites for 14-day immersion was determined as 0.10 % and 0.21 %, respectively. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used for characterization of the composites

Electrically Conductive Epoxy Adhesives

Directory of Open Access Journals (Sweden)

Lan Bai

2011-02-01

Full Text Available Conductive adhesives are widely used in electronic packaging applications such as die attachment and solderless interconnections, component repair, display interconnections, and heat dissipation. The effects of film thickness as functions of filler volume fraction, conductive filler size, shape, as well as uncured adhesive matrix viscosity on the electrical conduction behavior of epoxy-based adhesives are presented in this work. For this purpose, epoxy-based adhesives were prepared using conductive fillers of different size, shape, and types, including Ni powder, flakes, and filaments, Ag powder, and Cu powder. The filaments were 20 μm in diameter, and 160 or 260 μm in length. HCl and H3PO4 acid solutions were used to etch and remove the surface oxide layers from the fillers. The plane resistance of filled adhesive films was measured using the four-point method. In all cases of conductive filler addition, the planar resistivity levels for the composite adhesive films increased when the film thickness was reduced. The shape of resistivity-thickness curves was negative exponential decaying type and was modeled using a mathematical relation. The relationships between the conductive film resistivities and the filler volume fractions were also derived mathematically based on the experimental data. Thus, the effects of surface treatment of filler particles, the type, size, shape of fillers, and the uncured epoxy viscosity could be included empirically by using these mathematical relations based on the experimental data. By utilizing the relations we proposed to model thickness-dependent and volume fraction-dependent conduction behaviors separately, we were able to describe the combined and coupled volume fraction-film thickness relationship mathematically based on our experimental data.

Study on an amine-containing benzoxazine: Homo- and copolymerization with epoxy resin

Directory of Open Access Journals (Sweden)

L. Zhang

2016-07-01

Full Text Available An amine-containing benzoxazine (P-deta based homopolymer and its epoxy (Ep copolymers are investigated in this study. The structure of benzoxazine, prepared from phenol, diethylenetriamine and formalin, is confirmed by Fourier transform infrared spectroscopy (FT-IR and nuclear magnetic resonance spectroscopy (NMR. The viscosity of P-deta is much lower than that of commercialized benzoxazine monomers. The curing profiles of P-deta with various Ep ratios are studied by deconvolution and the related mechanism is clarified. Epoxy will not increase the curing temperature of P-deta, instead, it helps P-deta overcome the conversion limitation and promotes the curing rate. The thermal and viscoelastic properties were determined and compared. The copolymer of P-deta/Ep = 50/50 (wt/wt shows the highest glass transition temperature, higher than both individual homopolymers and other copolymers. Increasing benzoxazine fraction enhances modulus at room temperature but deteriorates the crosslink density. It can also enhances the char yield, but deteriorates the thermal stability of the copolymers.

An examination of impact damage in glass-phenolic and aluminum honeycomb core composite panels

Science.gov (United States)

Nettles, A. T.; Lance, D. G.; Hodge, A. J.

1990-01-01

An examination of low velocity impact damage to glass-phenolic and aluminum core honeycomb sandwich panels with carbon-epoxy facesheets is presented. An instrumented drop weight impact test apparatus was utilized to inflict damage at energy ranges between 0.7 and 4.2 joules. Specimens were checked for extent of damage by cross sectional examination. The effect of core damage was assessed by subjecting impact-damaged beams to four-point bend tests. Skin-only specimens (facings not bonded to honeycomb) were also tested for comparison purposes. Results show that core buckling is the first damage mode, followed by delaminations in the facings, matrix cracking, and finally fiber breakage. The aluminum honeycomb panels exhibited a larger core damage zone and more facing delaminations than the glass-phenolic core, but could withstand more shear stress when damaged than the glass-phenolic core specimens.

Chemopreventive effects of free and bound phenolics associated to steep waters (nejayote) obtained after nixtamalization of different maize types.

Science.gov (United States)

Rojas-García, Carlos; García-Lara, Silverio; Serna-Saldivar, Sergio O; Gutiérrez-Uribe, Janet A

2012-03-01

Free and bound phenolics extracts from nejayote solids were obtained after optimally lime-cooking blue, normal white, red, normal yellow, high-carotenoid and quality protein maize types. The extraction yield ranged from 4.47 to 10.05%. Bound phenolics extracts had higher content of total phenolics, antioxidant activity and ferulic acid compared to the free phenolics extracts. In general, free phenolics extracts were less cytotoxic than the bound phenolics counterparts. Bound phenolics extracts had higher induction of quinone reductase (QR) and particularly the normal yellow nejayote exerted the highest chemopreventive index tested in Hepa1c1c7 cells. When tested for monofunctional phase 2 induction capacity in BPrc1 cells, the bound phenolics extracts of blue, normal white and quality protein nejayotes were better inducers than the normal yellow counterpart. Particularly, the free phenolics extract of the white maize nejayote induced BPrc1 cells QR and exerted a higher chemopreventive index compared to the bound phenolics extract. Therefore, the nejayote of the normal white maize was the best source of monofunctional phase 2 enzyme inducers.

Sorption of phenol and phenol derivatives in hydrotalcite

International Nuclear Information System (INIS)

Avina G, E.I.

2002-01-01

One of the main problems in Mexico and in the World is the waste water pollution of a great variety of industrial processes by organic compounds. Among those ones the phenol compounds which are highly toxic, refractories (to the chemical degradation) and poorly biodegradable. This is due in a large extent to the problem created by the accelerated increase in the environmental pollution in the cities and industrial centers. The phenol compounds are used in a great variety of industries such as the production of resins, plasticizers, antioxidants, pesticides, colourings, disinfectants, etc. These phenol compounds are specially harmful, since they have repercussions on the flora of plants of biological treatment of water affecting its operation. The main objective of this work is to evaluate the capacities of phenol detention and its derivatives in an hydrotalcite type compound and diminishing with it the presence in water, in this case, of solutions prepared in the laboratory. In order to analyse this elimination process was used a methodology based in the carrying out in batch experiments and in the elaboration of a sorption isotherm. It is worth pointing out that this work was realized at laboratory scale, at relatively high phenol concentration ratio. With the obtained results when the sorption properties are evaluated the calcined hydrotalcite (HTC) for detaining phenol and p-chloro phenol it was observed that it is detained greater quantity of p-chloro phenol than phenol in the HTC. The detention of these phenol compounds in the HTC is due to the memory effect by the hydrotalcite regeneration starting from the oxides which are formed by the burning material. (Author)

Green Preparation of Epoxy/Graphene Oxide Nanocomposites Using a Glycidylamine Epoxy Resin as the Surface Modifier and Phase Transfer Agent of Graphene Oxide.

Science.gov (United States)

Tang, Xinlei; Zhou, Yang; Peng, Mao

2016-01-27

In studies of epoxy/graphene oxide (GO) nanocomposites, organic solvents are commonly used to disperse GO, and vigorous mechanical processes and complicated modification of GO are usually required, increasing the cost and hindering the development and application of epoxy nanocomposites. Here, we report a green, facile, and efficient method of preparing epoxy/GO nanocomposites. When triglycidyl para-aminophenol (TGPAP), a commercially available glycidyl amine epoxy resin with one tertiary amine group per molecule, is used as both the surface modifier and phase transfer agent of GO, GO can be directly and rapidly transferred from water to diglycidyl ether of bisphenol A and other types of epoxy resins by manual stirring under ambient conditions, whereas GO cannot be transferred to these epoxy resins in the absence of TGPAP. The interaction between TGPAP and GO and the effect of the TGPAP content on the dispersion of GO in the epoxy matrix were investigated systematically. Superior dispersion and exfoliation of GO nanosheets and remarkably improved mechanical properties, including tensile and flexural properties, toughness, storage modulus, and microhardness, of the epoxy/GO nanocomposites with a suitable amount of TGPAP were demonstrated. This method is organic-solvent-free and technically feasible for large-scale preparation of high-performance nanocomposites; it opens up new opportunities for exploiting the unique properties of graphene or even other nanofillers for a wide range of applications.

Electrodeposition properties of modified cational epoxy resin-type photoresist

International Nuclear Information System (INIS)

Yong He; Yunlong Zhang; Feipeng Wu; Miaozhen Li; Erjian Wang

1999-01-01

Multi-component cationic epoxy and acrylic resin system for ED photoresist was used in this work, since they can provide better storage stability for ED emulsion and better physical and chemical properties of deposited film than one-component system. The cationic main resin (AE) was prepared from amine modified epoxy resins and then treated with acetic acid. The amination degree was controlled as required. The synthetic procedure of cationic main resins is described in scheme I. The ED photoresist (AME) is composed of cationic main resin (AE) and nonionic multifunctional acrylic crosslinkers (PETA), in combination with suitable photo-initiator. They can easily be dispersed in deionized water to form a stable ED emulsion. The exposed part of deposited film upon UV irradiation occurs crosslinking to produce an insoluble semi-penetrating network and the unexposed part remains good solubility in the acidic water solution. It is readily utilized for fabrication of fine micropattern. The electrodeposition are carried out on Cu plate at room temperature. To evaluate the electrodeposition properties of ED photoresist (AME), the different influences are examined

A Study of Clay-Epoxy Nanocomposites Consisting of Unmodified Clay and Organo Clay

Directory of Open Access Journals (Sweden)

Graham Edward

2006-04-01

Full Text Available Clay-epoxy nanocomposites were synthesized from DGEBA resin and montmorillonite clay with an in-situ polymerization. One type of untreated clay and two types of organo clay were used to produce the nanocompsoites. The aims of this study were to examine the nanocomposite structure using different tools and to compare the results between the unmodified clay and modified clays as nanofillers. Although diffractogram in reflection mode did not show any apparent peak of both types of materials, the transmitted XRD (X-Ray Difraction graphs, DSC (Differential Scanning Calorimeter analysis and TEM (Transmission Electron Microscope images revealed that the modified clay-epoxy and unmodified clay-epoxy provides different results. Interestingly, the micrographs showed that some of the modified clay layers possessed non-exfoliated layers in the modified clay-epoxy nanocomposites. Clay aggregates and a hackle pattern were found from E-SEM images for both types of nanocomposite materials. It is shown that different tools should be used to determine the nanocomposite structure.

Isothermal and non-isothermal cure of a tri-functional epoxy resin (TGAP): a stochastic TMDSC study

OpenAIRE

Hutchinson, John M.; Shiravand, Fatemeh; Calventus Solé, Yolanda; Fraga Rivas, Iria

2012-01-01

The isothermal cure of a highly reactive tri-functional epoxy resin, tri-glycidyl para-amino phenol (TGAP), with diamino diphenyl sulphone (DDS), at two different cure temperatures Tc has been studied by both conventional differential scanning calorimetry (DSC) and by a stochastic temperature modulated DSC technique, TOPEM. From a series of isothermal cure experiments for increasing cure times, the glass transition temperature Tg as a function of isothermal cure time is determined by co...

Dermatosis profesional por resina epoxi: Presentación de un caso clínico Professional dermatosis for epoxy resin: A clinical case report

Directory of Open Access Journals (Sweden)

S Gaviola

2008-06-01

Full Text Available Mostramos un caso de dermatosis profesional originado por plásticos (resinas epoxi y la importancia de la detección precoz. Las resinas epoxi son de gran utilización en todo tipo de industrias (artes graficas, construcción, electrónica, componentes de prótesis traumatológicas, prótesis odontológicas, etc. y sus componentes pueden ser causa de dermatitis de contacto irritativa y por sensibilización.We describe a case of professional dermatosis caused by exposition to plastic products (epoxy resin and importance of early detection. The epoxy resins are widely used in all types of industries (graphics arts, construction, electronics, traumathological and odontological prothesis, etc. and their components may be the cause of contact dermatitis and sensitivity. Risk factors at work with epoxy resins are present during the production base resins, hardening agents, plasticizers and dilutants increase the risk of exposition at work. This requires preventive measures and early diagnosis.

Thermal conductivity and Kapitza resistance of cyanate ester epoxy mix and tri-functional epoxy electrical insulations at superfluid helium temperature

CERN Document Server

Pietrowicz, S; Jones, S; Canfer, S; Baudouy, B

2012-01-01

In the framework of the European Union FP7 project EuCARD, two composite insulation systems made of cyanate ester epoxy mix and tri-functional epoxy (TGPAP-DETDA) with S-glass fiber have been thermally tested as possible candidates to be the electrical insulation of 13 T Nb$_{3}$Sn high field magnets under development for this program. Since it is expected to be operated in pressurized superfluid helium at 1.9 K and 1 atm, the thermal conductivity and the Kapitza resistance are the most important input parameters for the thermal design of this type of magnet and have been determined in this study. For determining these thermal properties, three sheets of each material with different thicknesses varying from 245 μm to 598 μm have been tested in steady-state condition in the temperature range of 1.6 K - 2.0 K. The thermal conductivity for the tri-functional epoxy (TGPAP-DETDA) epoxy resin insulation is found to be k=[(34.2±5.5).T-(16.4±8.2)]×10-3 Wm-1K-1 and for the cyanate ester epoxy k=[(26.8±4.8).T- (9...

Solving the problem of building models of crosslinked polymers: an example focussing on validation of the properties of crosslinked epoxy resins.

Science.gov (United States)

Hall, Stephen A; Howlin, Brendan J; Hamerton, Ian; Baidak, Alex; Billaud, Claude; Ward, Steven

2012-01-01

The construction of molecular models of crosslinked polymers is an area of some difficulty and considerable interest. We report here a new method of constructing these models and validate the method by modelling three epoxy systems based on the epoxy monomers bisphenol F diglycidyl ether (BFDGE) and triglycidyl-p-amino phenol (TGAP) with the curing agent diamino diphenyl sulphone (DDS). The main emphasis of the work concerns the improvement of the techniques for the molecular simulation of these epoxies and specific attention is paid towards model construction techniques, including automated model building and prediction of glass transition temperatures (T(g)). Typical models comprise some 4200-4600 atoms (ca. 120-130 monomers). In a parallel empirical study, these systems have been cast, cured and analysed by dynamic mechanical thermal analysis (DMTA) to measure T(g). Results for the three epoxy systems yield good agreement with experimental T(g) ranges of 200-220°C, 270-285°C and 285-290°C with corresponding simulated ranges of 210-230°C, 250-300°C, and 250-300°C respectively.

21 CFR 177.2280 - 4,4′-Isopropyl-idenedi-phenol-epichloro-hydrin thermo-setting epoxy resins.

Science.gov (United States)

2010-04-01

... with mixed dimers and trimers of unsaturated C18 monobasic fatty acids derived from animal and... basic thermosetting epoxy resin is made by reacting 4,4′-isopropylidenediphenol with epi-chloro-hydrin...′-isopropylidenediphenol-epichlorohydrin basic resin and limited to use in contact with alcoholic beverages containing not...

Effect of the addition of different types of oenological commercial tannins on phenolic and sensorial red wine characteristics evolution

OpenAIRE

Jordão, António; Muxagata, Sara; Fontes, Luísa; Correia, Ana Cristina; Nunes, Fernando; Cosme, Fernanda

2016-01-01

The main objective of this work was to understand the effect of the addition of different commercial types of oenological tannins on red wine phenolic compounds and sensorial characteristics evolution. So, six different commercial oenological tannins obtained from different sources at an average dosage recommended by the manufactures were added to a red wine. During 120 wine aging days several phenolic parameters were analyzed (including several individual phenolic compounds by HPLC) and also...

Birches against mineral oils. Lignin - a renewable resource for the alternative production of phenols; Birke contra Erdoel. Lignin - ein nachwachsender Rohstoff zur alternativen Gewinnung von Phenolen

Energy Technology Data Exchange (ETDEWEB)

Zehnpfund, C.; Bormann, J.; Wehrkamp zu Hoene, F. [Gymnasium Bersenbrueck (Germany)

1998-02-01

We wanted to offer an alternative for the `After-mineral oil time` with our work when we attempted to isolate phenols, which are won up to now from mineral oil, of a growing raw material. Phenols are economic important substances for production of epoxies, herbicides, artificial resins, dyes and drugs (e.g. aspirin or Paracetamol). We managed to isolate phenols with normal conditions of lignin, a component of wood. (orig.) [Deutsch] Wir wollten mit unserer Arbeit eine Alternative fuer die `Nach-Erdoel-Zeit` bieten, indem wir versuchten, Phenole, die bisher aus Erdoel gewonnen werden, aus einem nachwachsenden Rohstoff zu isolieren. Phenole sind volkswirtschaftlich bedeutsame Substanzen zur Herstellung von Kunststoffen, Herbiziden, Kunstharzen, Farbstoffen und Arzneimitteln (z.B. Aspirin oder Paracetamol). Es gelang uns, Phenole unter Normalbedingungen aus Lignin, einem Bestandteil des Holzes, zu isolieren. (orig.)

Oxidation of lignin in hemp fibres by laccase: effects on mechanical properties of hemp fibres and unidirectional fibre/epoxy composites

DEFF Research Database (Denmark)

Liu, Ming; Baum, Andreas; Odermatt, Jürgen

2017-01-01

Laccase activity catalyzes oxidation and polymerization of phenols. The effect of laccase treatment on the mechanical properties of hemp fibres and hemp fibre/epoxy composites was examined. Laccase treatment on top of 0.5% EDTA + 0.2% endo-polygalacturonase (EPG) treatments increased the mechanical...... properties of hemp fibres and fibre/epoxy composites. Comparing all fibre treatments, composites with 0.5% EDTA + 0.2% EPG + 0.5% laccase treated fibres had highest stiffness of 42 GPa and highest ultimate tensile strength (UTS) of 326 MPa at a fibre volume content of 50%. The thermal resistance of hemp...... hemp fibres and their composites were due to laccase catalyzed polymerization of lignin moieties in hemp fibres....

A critical evaluation of the enhancement of mechanical properties of epoxy modified using CNTs

Science.gov (United States)

Bedsole, Robert W.; Park, Cheol; Bogert, Philip B.; Tippur, Hareesh V.

2015-09-01

Carbon nanotubes (CNTs) have been widely shown in the literature to improve mechanical properties of epoxy, such as tensile strength, elastic modulus, strain to failure, and fracture toughness. These improvements in nanocomposite properties have been attributed to the extraordinary properties of the nanotubes, as well as the quality of their dispersion within and adhesion to the epoxy matrix. However, many authors have also struggled to show significant mechanical improvements using similar methodologies and despite, in some cases, showing qualitative improvements in dispersion with optical microscopy. These authors have frequently resorted to other methods for improving the mechanical properties of CNT/epoxy, such as electrically aligning CNTs, using different types of CNTs, or modifying the stoichiometry. The current work examines many different dispersion techniques, types of CNTs, types of epoxies, curing cycles, and other variables in an attempt to improve the mechanical properties of neat epoxy with CNTs. Despite seeing significant changes in the microscopy, no significant improvements in tensile or fracture properties have been attributed to CNTs in this work.

Structural study of synthetic polymers by MALDI-TOFMS; MALDI-TOFMS ni yoru gosei kobunshi no kozo kaiseki

Energy Technology Data Exchange (ETDEWEB)

Noguchi, K.; Hirayama, K. [Ajinomoto Co. Inc., Tokyo (Japan)

1998-08-01

As observation results on the time-dependent change in the ring-opening reaction of novolac epoxy resin with acetic acid by MALDI-TOFMS, the epoxy ring was opened with reaction time, the hydroxy group formed by the ring-opening reaction was acetylated, those components were measured. In the case of the FABMS/MS observation of materials and the reaction products, the estimation structure could be confirmed from the measured results of MALDI-TOFMS. In the polymerization of bisphenol A epoxy resin with N, N`-dimethylethylenediamine, it was observed by MALDI-TOFMS that many kinds of polymers with high molecular weight were formed with an increase of reaction time. In this case, the LSIMS/MS observation of materials and the reaction products was carried out, the estimation structure could be confirmed from the measured results of MALDI-TOFMS. 19 refs., 8 figs.

Electroactive polymer gels based on epoxy resin

Science.gov (United States)

Samui, A. B.; Jayakumar, S.; Jayalakshmi, C. G.; Pandey, K.; Sivaraman, P.

2007-04-01

Five types of epoxy gels have been synthesized from common epoxy resins and hardeners. Fumed silica and nanoclay, respectively, were used as fillers and butyl methacrylate/acrylamide were used as monomer(s) for making interpenetrating polymer networks (IPNs) in three compositions. Swelling study, tensile property evaluation, dynamic mechanical thermal analysis, thermo-gravimetric analysis, scanning electron microscopy and electroactive property evaluation were done. The gels have sufficient mechanical strength and the time taken for bending to 20° was found to be 22 min for forward bias whereas it was just 12 min for reverse bias.

Chetoui olive leaf extracts: influence of the solvent type on the phenolics and antioxidant activities

Energy Technology Data Exchange (ETDEWEB)

Abaza, L.; Ben Youssef, N.; Manai, H.; Haddada, F.M.; Methenni, K.; Zarrouk, M.

2011-07-01

The aim of this study was to investigate the influence of the solvent type on the extraction of phenolics and the antioxidant properties of the extracts obtained from Chetoui olive leaves. Extraction was conducted at room temperature using four solvents: deionized water (ddH2O), 80% methanol (80% MeOH), 70% ethanol (70% EtOH), and 80% acetone. Total phenols and total flavonoids were measured using the Folin-Ciocalteau and aluminum chloride colorimetric methods, respectively. The antioxidant properties have been determined by two scavenging activity methods, DPPH and ABTS. (Author).

Comparison of total phenolic content and composition of individual ...

African Journals Online (AJOL)

A successful peanut breeding to obtain genotypes with greater phenolic content requires information on type and content of phenolic compounds in parental peanut genotypes. The aim of this study was to investigate the total phenolic contents and phenolic acid profiles of 15 Valencia-type peanut genotypes both in peanut ...

Behaviour of Epoxy Silica Nanocomposites Under Static and Creep Loading

Science.gov (United States)

Constantinescu, Dan Mihai; Picu, Radu Catalin; Sandu, Marin; Apostol, Dragos Alexandru; Sandu, Adriana; Baciu, Florin

2017-12-01

Specific manufacturing technologies were applied for the fabrication of epoxy-based nanocomposites with silica nanoparticles. For dispersing the fillers in the epoxy resin special equipment such as a shear mixer and a high energy sonicator with temperature control were used. Both functionalized and unfunctionalized silica nanoparticles were added in three epoxy resins. The considered filling fraction was in most cases 0.1, 0.3 and 0.5 wt%.. The obtained nanocomposites were subjected to monotonic uniaxial and creep loading at room temperature. The static mechanical properties were not significantly improved regardless the filler percentage and type of epoxy resin. Under creep loading, by increasing the stress level, the nanocomposite with 0.1 wt% silica creeps less than all other materials. Also the creep rate is reduced by adding silica nanofillers.

Synthesis and characterization of rubbery epoxy/organoclay hectorite nanocomposites

Directory of Open Access Journals (Sweden)

2007-12-01

Full Text Available The present research investigates the morphology, the mechanical, and the viscoelastic properties of rubbery epoxy/clay nanocomposites synthesized by in situ polymerisation of a prepolymer diglycidyl ether of bisphenol-A crosslinked with an aliphatic diamine based on a polyoxypropylene backbone. The inorganic phase was hectorite, exchanged with octadecylammonium ions in order to give organophilic properties to the phyllosilicate. An ultrasonicator was used to disperse the silicate clay layer into epoxy-amine matrix. The morphology of epoxy-hectorite nanocomposites examined by transmission electron microscopy (TEM showed that mixed delamination or intercalation or microdispersion could occur depending on type of organoclay. Moreover, the mechanical and viscoelastic properties were found to be improved with only the treated hectorite.

Solving the problem of building models of crosslinked polymers: an example focussing on validation of the properties of crosslinked epoxy resins.

Directory of Open Access Journals (Sweden)

Stephen A Hall

Full Text Available The construction of molecular models of crosslinked polymers is an area of some difficulty and considerable interest. We report here a new method of constructing these models and validate the method by modelling three epoxy systems based on the epoxy monomers bisphenol F diglycidyl ether (BFDGE and triglycidyl-p-amino phenol (TGAP with the curing agent diamino diphenyl sulphone (DDS. The main emphasis of the work concerns the improvement of the techniques for the molecular simulation of these epoxies and specific attention is paid towards model construction techniques, including automated model building and prediction of glass transition temperatures (T(g. Typical models comprise some 4200-4600 atoms (ca. 120-130 monomers. In a parallel empirical study, these systems have been cast, cured and analysed by dynamic mechanical thermal analysis (DMTA to measure T(g. Results for the three epoxy systems yield good agreement with experimental T(g ranges of 200-220°C, 270-285°C and 285-290°C with corresponding simulated ranges of 210-230°C, 250-300°C, and 250-300°C respectively.

Synthesis of polyoxometalate-loaded epoxy composites

Science.gov (United States)

Anderson, Benjamin J

2014-10-07

The synthesis of a polyoxometalate-loaded epoxy uses a one-step cure by applying an external stimulus to release the acid from the polyoxometalate and thereby catalyze the cure reaction of the epoxy resin. Such polyoxometalate-loaded epoxy composites afford the cured epoxy unique properties imparted by the intrinsic properties of the polyoxometalate. For example, polyoxometalate-loaded epoxy composites can be used as corrosion resistant epoxy coatings, for encapsulation of electronics with improved dielectric properties, and for structural applications with improved mechanical properties.

‘Containers’ for self-healing epoxy composites and coating: Trends and advances

Directory of Open Access Journals (Sweden)

P. Vijayan

2016-06-01

Full Text Available The introduction of self-healing functionality into epoxy matrix is an important and challenging topic. Various micro/nano containers loaded self-healing agents are developed and incorporated into epoxy matrix to impart self-healing ability. The current report reviews the major findings in the area of self-healing epoxy composites and coatings with special emphasis on these containers. The preparation and use of polymer micro/nano capsules, polymer fibers, hollow glass fibers/bubbles, inorganic nanotubes, inorganic meso- and nano-porous materials, carbon nanotubes etc. as self-healing containers are outlined. The nature of the container and its response to the external stimulations greatly influence the self-healing performance. The self-healing mechanism associated with each type of container and the role of container parameters on self-healing performance of self-healing epoxy systems are reviewed. Comparison of the efficiency offered by different types of containers is introduced. Finally, the selection of containers to develop cost effective and green self-healing systems are mentioned.

Optical emission behavior and radiation resistance of epoxy resins

International Nuclear Information System (INIS)

Kawanishi, Shunichi; Udagawa, Akira; Hagiwara, Miyuki

1987-11-01

To make clear a mechanism of radiation resistance of epoxy resin systems, a role of energy trapping site induced in bisphenol A type epoxy resins cured with 4 kinds of aromatic amines (Φ N ) was studied in comparison with the case of aliphatic amine curing system through a measurement of optical emission. In the system of the epoxy resin cured with DETA, the optical emission from an excited state of bisphenol A unit of epoxy resin and a charge transfer complex was observed. On the other hand, the optical emission from Φ N was observed in the aromatic amine curing system. Their excitation spectrum consists of peaks of absorption spectrum of BA and those of Φ N , showing that the excited state of Φ N is formed through the excitation of both BA and Φ N . Therefore, the excited energy of BA transfers to the excited state of Φ N . Emission intensity of Φ N band was 20 ∼ 100 times as large as that of BA. These results indicate that the radiation energy is effectively released as an optical emission from excited state of Φ N in the epoxy resin when cured with aromatic amine. It can be concluded from the above results that aromatic amine hardeners contribute to enhancement of the radiation resistance of epoxy resin by acting as an energy transfer agent. (author)

Radiation tests on selected electrical insulating materials for high-power and high voltage application

International Nuclear Information System (INIS)

Liptak, G.; Schuler, R.; Haberthuer, B.; Mueller, H.; Zeier, W.; Maier, P.; Schoenbacher, H.

1985-01-01

This report presents a comprehensive set of test results on the irradiation of insulating materials and systems used for the windings of rotating machines, dry-type transformers, and magnet coils. The materials were: Novolac, bisphenol-A, and cycloaliphatic types of epoxy; saturated and unsaturated polyesterimide; silicone, phenolic, and acrylic resins. The reinforcement consisted of glass mat, glass roving, glass cloth, mica paper, polyester mat, polyester roving, polyester cloth, aromatic polyamide paper, or combinations thereof. The materials were irradiated in an 8 MW pool reactor up to integrated doses of 10 8 Gy. On most samples, flexural properties were examined as recommended by IEC Standard 544. For tapes and varnishes, the breakdown voltage was measured. The adhesion of copper bars glued together with an epoxy resin was examined by means of a lap-shear test. A cupping test by means of the Erichsen apparatus was used to measure the flexibility of varnishes. The results are presented in tables and graphs for each of the materials tested. Those from mechanical tests show that the radiation resistance of composite resin-rich insulations depends not only on the base resin combination and the reinforcement material but, to a large degree, also on the adhesion between the two. It appears that better adhesion, and consequently higher radiation resistance, is obtained by special surface treatments of glass fibres. For laminates, higher radiation resistance is obtained with glass mat and resin combinations than with glass cloth as reinforcing materials. The breakdown voltage tests show that the application of mechanical stress to most irradiated samples causes the insulation layer to crack, resulting in lower dielectric strength. For a number of materials, the critical properties of flexural strength and breakdown voltage are above 50% of the initial value at doses between 10 7 and 10 8 Gy, i.e. a radiation index of 7 to 8 at 10 5 Gy/h. (orig.)

Determinants of epoxy allergy in the construction industry: a case-control study.

Science.gov (United States)

Spee, Ton; Timmerman, Johan G; Rühl, Reinhold; Kersting, Klaus; Heederik, Dick J J; Smit, Lidwien A M

2016-05-01

Workers exposed to epoxy products are at risk of developing allergic contact dermatitis. To compare workers throughout the German construction industry with and without skin allergy to epoxy resins, hardeners, and/or reactive diluents, and to investigate which determinants are related to the development of epoxy allergy. A questionnaire was completed by 179 epoxy allergy cases, and 151 epoxy workers as controls. Crude and adjusted odds ratios (ORs) and 95% confidence intervals (CIs) were estimated by the use of backwards stepwise logistic regression analysis. A multiple imputation approach was used to deal with missing data. Epoxy allergy was associated with an unusually high level of exposure to epoxy products [OR 2.13 (95%CI: 1.01-4.51)], wearing short sleeves or short trousers [OR 2.38 (95%CI: 1.03-5.52)], and not always using the correct type of gloves [OR 2.12 (95%CI: 1.12-4.01)]. A monotonic increasing risk was found with increasing exposure hours per week [OR 1.72 (95%CI: 1.39-2.14)]. Not using skin cream was inversely associated with epoxy allergy [OR 0.22 (95%CI: 0.08-0.59)]. Years working with epoxy products were inversely associated with epoxy allergy [OR 0.41 (95%CI: 0.27-0.61) per 10-year increase], suggesting a healthy worker survivor effect. Occupational epoxy allergy may be prevented by improving occupational hygiene behaviour and personal protection. © 2016 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Epoxy-based broadband antireflection coating for millimeter-wave optics.

Science.gov (United States)

Rosen, Darin; Suzuki, Aritoki; Keating, Brian; Krantz, William; Lee, Adrian T; Quealy, Erin; Richards, Paul L; Siritanasak, Praween; Walker, William

2013-11-20

We have developed epoxy-based, broadband antireflection coatings for millimeter-wave astrophysics experiments with cryogenic optics. By using multiple-layer coatings where each layer steps in dielectric constant, we achieved low reflection over a wide bandwidth. We suppressed the reflection from an alumina disk to 10% over fractional bandwidths of 92% and 104% using two-layer and three-layer coatings, respectively. The dielectric constants of epoxies were tuned between 2.06 and 7.44 by mixing three types of epoxy and doping with strontium titanate powder required for the high dielectric mixtures. At 140 K, the band-integrated absorption loss in the coatings was suppressed to less than 1% for the two-layer coating, and below 10% for the three-layer coating.

Adhesive properties and adhesive joints strength of graphite/epoxy composites

Science.gov (United States)

Rudawska, Anna; Stančeková, Dana; Cubonova, Nadezda; Vitenko, Tetiana; Müller, Miroslav; Valášek, Petr

2017-05-01

The article presents the results of experimental research of the adhesive joints strength of graphite/epoxy composites and the results of the surface free energy of the composite surfaces. Two types of graphite/epoxy composites with different thickness were tested which are used to aircraft structure. The single-lap adhesive joints of epoxy composites were considered. Adhesive properties were described by surface free energy. Owens-Wendt method was used to determine surface free energy. The epoxy two-component adhesive was used to preparing the adhesive joints. Zwick/Roell 100 strength device were used to determination the shear strength of adhesive joints of epoxy composites. The strength test results showed that the highest value was obtained for adhesive joints of graphite-epoxy composite of smaller material thickness (0.48 mm). Statistical analysis of the results obtained, the study showed statistically significant differences between the values of the strength of the confidence level of 0.95. The statistical analysis of the results also showed that there are no statistical significant differences in average values of surface free energy (0.95 confidence level). It was noted that in each of the results the dispersion component of surface free energy was much greater than polar component of surface free energy.

Comparative Study of the Use of Trichloroacetic Acid and Phenolic Acid in the Treatment of Atrophic-Type Acne Scars.

Science.gov (United States)

Dalpizzol, Mariana; Weber, Magda B; Mattiazzi, Anna Paula F; Manzoni, Ana Paula D

2016-03-01

Many therapies involving varying degrees of complexity have been used to treat acne scars, but none is considered the gold standard treatment. A comparative evaluation of 88% phenol and 90% trichloroacetic acid (TCA) applied using the chemical reconstruction of skin scars (CROSS) technique. A nonrandomized, single-blinded self-controlled clinical trial was conducted among patients with ice pick-type and boxcar-type atrophic acne scars. Using 88% phenol on the left hemiface and 90% TCA on the right hemiface was adopted as the standard practice of the CROSS technique. The dermatological quality of life index (DLQI) questionnaire, acne scar grading scale Échelle d´Evaluation Clinique des Cicatrices d'Acne (ECCA), and evaluation of improvement were performed pretreatment and post-treatment. Regarding ECCA, significant differences were found in pretreatment and post-treatment (p < .001). Regarding tolerance to pain, it was found that the discomfort felt with 90% TCA was significantly less than that felt with 88% phenol (p = .020). Regarding the quality of life measured with the DLQI, the results showed that the mean score in post-treatment assessment was significantly lower than that in the pretreatment assessment (p < .05). Hypochromia and enlargement scar were only seen after the use of 90% TCA. This study confirmed the efficacy of both TCA and phenol for treating such scars, with less severe complications from the use of phenol.

Photochemical studies on aromatic γ,δ-epoxy ketones: efficient synthesis of benzocyclobutanones and indanones.

Science.gov (United States)

Shao, Yutian; Yang, Chao; Gui, Weijun; Liu, Yang; Xia, Wujiong

2012-04-11

Irradiation of terminal aromatic γ,δ-epoxy ketones with a 450 W UV lamp led to Norrish type II cyclization/semi-pinacol rearrangement cascade reaction which formed the benzocyclobutanones containing a full-carbon quaternary center, whereas irradiation of substituted aromatic γ,δ-epoxy ketones led to the indanones through a photochemical epoxy rearrangement and 1,5-biradicals cyclization tandem reaction. This journal is © The Royal Society of Chemistry 2012

Epoxy-based carbon nanotubes reinforced composites

CSIR Research Space (South Africa)

Kesavan Pillai, Sreejarani

2011-04-01

Full Text Available of the three major epoxy resin producers worldwide [May, 1987]. Epoxy resin is most commonly used as a matrix for advanced composites due to their superior thermal, mechanical and electrical properties; dimensional stability and chemical resistance. Epoxy... and modifiers to create products with an almost unlimited range and variety of performance properties [The epoxy book, 2000]. Epoxy resins are widely used as high-grade synthetic resins, for example, in the electronics, aeronautics and astronautic industries...

Interaction of water with epoxy.

Energy Technology Data Exchange (ETDEWEB)

Powers, Dana Auburn

2009-07-01

The chemistries of reactants, plasticizers, solvents and additives in an epoxy paint are discussed. Polyamide additives may play an important role in the absorption of molecular iodine by epoxy paints. It is recommended that the unsaturation of the polyamide additive in the epoxy cure be determined. Experimental studies of water absorption by epoxy resins are discussed. These studies show that absorption can disrupt hydrogen bonds among segments of the polymers and cause swelling of the polymer. The water absorption increases the diffusion coefficient of water within the polymer. Permanent damage to the polymer can result if water causes hydrolysis of ether linkages. Water desorption studies are recommended to ascertain how water absorption affects epoxy paint.

Revestimentos de alta camada obtidos com a modificação de resinas epóxi novolaca pela reação com organo-siloxano e catálise ácida

Directory of Open Access Journals (Sweden)

Roberta Jachura Rocha

Full Text Available Epoxy resins are an important class of thermostable polymers, widely used in structural applications or as adhesives. However, the low fracture resistance is their main weakness in many applications. Due to this fact, this study aims to modify a polymer matrix based on a novolac epoxy resin with an organo siloxane (AMS. The final properties of cured epoxys resins are affected by the curing process and the coatings modified in this study with AMS and cured with acid catalyst presented greater resistance to thermal decomposition compared to that cured with Aradur, demonstrating a higher content of crosslinking in the siloxane polyether and the novolak epoxy resin chains. This epoxy matrix modified was used to prepare coatings whose films applied to 1020 steel surfaces presented a resistance of 1010 Ohm-cm-2. This resistance value is one order of magnitude greater than that of epoxy resins films modified by siloxanes in published studies, which demonstrates a potential economy in terms of maintenance costs of metal structures and machines used in power plants (UTE. To obtain the developed inks in pilot plant scale, it was used an aromatic polyamine as curing agent, characterizing the product obtained as an epoxy bi-component paint for commercial use.

Enhanced Flexural Strength of Tellurium Nanowires/epoxy Composites with the Reinforcement Effect of Nanowires

Science.gov (United States)

Balguri, Praveen Kumar; Harris Samuel, D. G.; Aditya, D. B.; Vijaya Bhaskar, S.; Thumu, Udayabhaskararao

2018-02-01

Investigating the mechanical properties of polymer nanocomposite materials has been greatly increased in the last decade. In particular, flexural strength plays a major role in resisting bending and shear loads of a composite material. Here, one dimensional (1D) tellurium nanowires (TeNWs) reinforced epoxy composites have been prepared and the flexural properties of resulted TeNWs/epoxy nanocomposites are studied. The diameter and length of the TeNWs used to make TeNWs/epoxy nanocomposites are 21±2.5 nm and 697±87 nm, respectively. Plain and TeNWs/epoxy nanocomposites are characterized by X-ray diffraction (XRD), thermogravimetric analysis (TGA), and differential thermal analysis (DTA). Furthermore, significant enhancement in the flexural strength of TeNWs/epoxy nanocomposite is observed in comparison to plain epoxy composite, i.e. flexural strength is increased by 65% with the addition of very little amount of TeNWs content (0.05 wt.%) to epoxy polymer. Structural details of plain and TeNWs/epoxy at micrometer scale were examined by scanning electron microscopy (SEM). We believe that our results provide a new type of semiconductor nanowires based high strength epoxy polymer nanocomposites.

Effect of the addition of different types of oenological commercial tannins on phenolic and sensorial red wine characteristics evolution

Directory of Open Access Journals (Sweden)

Jordão António M.

2016-01-01

Full Text Available The main objective of this work was to understand the effect of the addition of different commercial types of oenological tannins on red wine phenolic compounds and sensorial characteristics evolution. So, six different commercial oenological tannins obtained from different sources at an average dosage recommended by the manufactures were added to a red wine. During 120 wine aging days several phenolic parameters were analyzed (including several individual phenolic compounds by HPLC and also the sensorial characteristics of the wines. Wines treated with oenological tannins showed higher total phenols and flavonoid phenols and lesser color degradation during the aging time considered. After 120 aging days, wines aged with oenological tannins showed more total and individual anthocyanins and significantly more red color that induced significantly color differences in relation to the untreated wine (especially for the wines treated with condensed tannins. From a sensorial point of view it was also possible to detect a clear differentiation between the wines.

Fabrication of High Gas Barrier Epoxy Nanocomposites: An Approach Based on Layered Silicate Functionalized by a Compatible and Reactive Modifier of Epoxy-Diamine Adduct

Directory of Open Access Journals (Sweden)

Ran Wei

2018-05-01

Full Text Available To solve the drawbacks of poor dispersion and weak interface in gas barrier nanocomposites, a novel epoxy-diamine adduct (DDA was synthesized by reacting epoxy monomer DGEBA with curing agent D400 to functionalize montmorillonite (MMT, which could provide complete compatibility and reactivity with a DGEBA/D400 epoxy matrix. Thereafter, sodium type montmorillonite (Na-MMT and organic-MMTs functionalized by DDA and polyether amines were incorporated with epoxy to manufacture nanocomposites. The effects of MMT functionalization on the morphology and gas barrier property of nanocomposites were evaluated. The results showed that DDA was successfully synthesized, terminating with epoxy and amine groups. By simulating the small-angle neutron scattering data with a sandwich structure model, the optimal dispersion/exfoliation of MMT was observed in a DDA-MMT/DGEBA nanocomposite with a mean radius of 751 Å, a layer thickness of 30.8 Å, and only two layers in each tactoid. Moreover, the DDA-MMT/DGEBA nanocomposite exhibited the best N2 barrier properties, which were about five times those of neat epoxy. Based on a modified Nielsen model, it was clarified that this excellent gas barrier property was due to the homogeneously dispersed lamellas with almost exfoliated structures. The improved morphology and barrier property confirmed the superiority of the adduct, which provides a general method for developing gas barrier nanocomposites.

Void-free epoxy castings for cryogenic insulators and seals

International Nuclear Information System (INIS)

Quirk, J.F.

1983-01-01

The design of the Westinghouse Magnet for the Oak Ridge National Laboratory's Large Coil Program (LCP) incorporates a main lead bushing which transmits heat-leak loads by conduction to the supercritical helium stream. The bushing, which consists of epoxy resin cast about a copper conductor, must be electrically insulated, vacuum tight and be capable of withstanding the stresses encountered in cryognic service. The seal design of the bushing is especially important; leakage from either the helium system or the external environment into the vacuum will cause the magnet to quench. Additionally, the epoxy-resin casting must resist mechanical loads caused by the weight of leads attached to the bushing and thermal stresses transmitted to the epoxy via the conductor. The epoxy resin is cast about the conductor in such a way as to provide the required vacuum tight seal. The technique by which this is accomplished is reviewed. Equally important is the elimination of voids in the epoxy which will act as stress-concentrating discontinuities during cooling to or warming from 4K. The types of voids that could be expected and their causes are described. The paper reviews techniques employed to eliminate voids within the cast-resin portion of the bushing

Flexural properties of treated and untreated kenaf/epoxy composites

International Nuclear Information System (INIS)

Yousif, B.F.; Shalwan, A.; Chin, C.W.; Ming, K.C.

2012-01-01

Graphical abstract: Untreated kenaf fibre/epoxy composites. Treated kenaf fibre/epoxy composites. Highlights: ► Treatment of kenaf fibres with 6% NaOH has improved the flexural properties of epoxy composites. ► Interfacial adhesion of the natural fibres is controlled by the microstructure of the fibres. ► Kenaf fibres have a potential to replace glass fibres for flexural applications. -- Abstract: In the current work, flexural properties of unidirectional long kenaf fibre reinforced epoxy (KFRE) composites are studied. The kenaf fibres were prepared into two types as untreated and treated (with 6% NaOH). The failure mechanism and damage features of the materials were categorized with the surface observation by scanning electron microscope (SEM). The results revealed that reinforcement of epoxy with treated kenaf fibres increased the flexural strength of the composite by about 36%, while, untreated fibres introduced 20% improvement. This was mainly due to the high improvement of the chemical treatment (NaOH) on the interfacial adhesion of the fibres and the porosity of the composites which prevented the debonding, detachments or pull out of fibres. For untreated KFRE, the fracture mechanisms were debonding, tearing, detachments and pull out of fibres. The developed composite exhibited superior properties compared to the previous composites based on natural and synthetic fibres.

Phenolic content, physical and sensory properties of breads made with different types of barley wort.

Science.gov (United States)

Baiano, Antonietta; Viggiani, Ilaria; Terracone, Carmela; Romaniello, Roberto; Del Nobile, Matteo Alessandro

2015-10-01

Barley wort, an intermediate product of beer brewing, is rich in phenolic compounds. The aim of this work was to evaluate the possibility of increasing the antioxidant content of bread by replacing water with three types of wort: two of them withdrawn at the end of the mashing operation during the production of a Pilsner and a Double Malt Pilsner beer respectively; the other collected at an intermediate stage of mashing of the Pilsner beer. The chemical, physical and sensory properties of the wort-added breads were compared with those of a control bread. All three worts led to increased phenolic content, volume and specific volume of the breads and induced significant changes in 11 of 23 sensory descriptors. The highest phenolic contents were detected in breads made either with the Pilsner wort withdrawn at an intermediate stage of mashing or with the Double Malt Pilsner wort. The former also gave the highest increase in volume and specific volume but significantly reduced the scores for crunchiness, firmness and cohesiveness. The latter led to lower increases in volume and specific volume, but less significant changes in the sensory properties were associated with its use. Worts can be conveniently used to increase the antioxidant content of bread. However, different types of wort can modify to different extents the physical and sensory properties of the product. © 2014 Society of Chemical Industry.

Epoxy resin/phosphonium ionic liquid/carbon nanofiller systems: Chemorheology and properties

Directory of Open Access Journals (Sweden)

H. Maka

2014-10-01

Full Text Available Epoxy nanocomposites with commercial carbon nanotubes (CNT or graphene (GN have been prepared using phosphonium ionic liquid [trihexyltetradecylphosphonium bis(2,4,4-trimethylpentyl phosphinate, IL-f]. IL-f served simultaneously as nanofiller dispersing medium and epoxy resin catalytic curing agent. An influence of IL-f/epoxy weight ratio (3, 6 and 9/100, phr, carbon nanofiller type and content on viscosity of epoxy compositions during storage at ambient temperature was evaluated. Curing process was controlled for neat and CNT or GN modified epoxy compositions (0.25-1.0 wt.% load using differential scanning calorimetry and rheometry. Epoxy nanocomposites exhibited slightly increased glass transition temperature values (146 to 149°C whereas tan δ and storage modulus decreased (0.30 to 0.27 and 2087 to 1070 MPa, respectively as compared to reference material. Crosslink density regularly decreased for composites with increasing CNT content (11 094 to 7 020 mol/m3. Electrical volume resistivity of the nanocomposites was improved in case of CNT to 4•101 Ω•m and GN to 2•105 Ω•m (nanofiller content 1 wt.%. Flame retardancy was found for modified epoxy materials with as low GN and phosphorus content as 0.25 and 0.7 wt.%, respectively (increase of limiting oxygen index to 26.5%.

SYNERGISTIC EFFECTS OF NOVOLAC-BASED CHAR FORMER WITH A PHOSPHORUS/NITROGEN-CONTAINING FLAME RETARDANT IN POLYAMIDE 6

Institute of Scientific and Technical Information of China (English)

Wei-cheng Xiong; Li Chen; De-yi Wang; Fei Song; Yu-zhong Wang

2012-01-01

The synergistic effect of phosphorus oxynitride (PON) with a novolac-based char former modified by salification (NA-metal salt) on the flame retardance of polyamide 6 (PA6) was investigated.For this purpose,various flame-retardant PA6 systems were melt-compounded with PON,PON/NA,PON/NA-V2O5 and PON/NA-Fe2O3,and their flame retardance was evaluated by measuring the limiting oxygen index (LOI) values and UL-94 vertical burning ratings.The results showed that,compared with the PA6/PON/NA system,the combination of two char formers (NA-V2O5,NA-Fe2O3) with PON could obviously improve the char formation and flame retardance of PA6.The flame retardance and cone calorimetric analyses showed the stronger synergism as well as the better flame retardant performance of PON/NA-Fe2O3 flame retardant system.The effects of different char formers on the flame retardance and thermal stability of this system were also discussed.

Preparation and characterization of hybrid materials of epoxy resin type bisphenol a with silicon and titanium oxides by sol-gel process

International Nuclear Information System (INIS)

Carrillo C, A.; Osuna A, J. G.

2011-01-01

Hybrid materials were synthesized from epoxy resins as a result bisphenol type A-silicon oxide and epoxy resin bisphenol type A-titanium oxide were obtained. The synthesis was done by sol-gel process using tetraethyl orthosilicate (Teos) and titanium isopropoxide (I Ti) as inorganic precursors. The molar ratio of bisphenol A to the inorganic precursors was the studied variable. The materials were characterized by thermal analysis, infrared spectroscopy, scanning electron microscopy and energy dispersive X-ray spectroscopy. The hybrid nature of the materials was demonstrated through thermal analysis and infrared spectroscopy. In both systems, as the amount of alkoxide increased, the bands described above were more defined. This behavior indicates the interactions between the resin and the alkoxides. Hybrids with Teos showed a smoother and homogeneous surface in its entirety, without irregularities. Hybrids with titanium isopropoxide had low roughness. Both Teos and I Ti hybrids showed a decrease on the atomic weight percentage of carbon due to a slight reduction of the organic part on the surface. (Author)

Preparation and characterization of hybrid materials of epoxy resin type bisphenol a with silicon and titanium oxides by sol-gel process

Energy Technology Data Exchange (ETDEWEB)

Carrillo C, A.; Osuna A, J. G., E-mail: acc.carrillo@gmail.com [Universidad Autonoma de Coahuila, Facultad de Ciencias Quimicas, Blvd. Venustiano Carranza y Jose Cardenas Valdes, 25000 Saltillo, Coahuila (Mexico)

2011-07-01

Hybrid materials were synthesized from epoxy resins as a result bisphenol type A-silicon oxide and epoxy resin bisphenol type A-titanium oxide were obtained. The synthesis was done by sol-gel process using tetraethyl orthosilicate (Teos) and titanium isopropoxide (I Ti) as inorganic precursors. The molar ratio of bisphenol A to the inorganic precursors was the studied variable. The materials were characterized by thermal analysis, infrared spectroscopy, scanning electron microscopy and energy dispersive X-ray spectroscopy. The hybrid nature of the materials was demonstrated through thermal analysis and infrared spectroscopy. In both systems, as the amount of alkoxide increased, the bands described above were more defined. This behavior indicates the interactions between the resin and the alkoxides. Hybrids with Teos showed a smoother and homogeneous surface in its entirety, without irregularities. Hybrids with titanium isopropoxide had low roughness. Both Teos and I Ti hybrids showed a decrease on the atomic weight percentage of carbon due to a slight reduction of the organic part on the surface. (Author)

Contact allergy to epoxy resin

DEFF Research Database (Denmark)

Bangsgaard, Nannie; Thyssen, Jacob Pontoppidan; Menné, Torkil

2012-01-01

Background. Epoxy resin monomers are strong skin sensitizers that are widely used in industrial sectors. In Denmark, the law stipulates that workers must undergo a course on safe handling of epoxy resins prior to occupational exposure, but the effectiveness of this initiative is largely unknown...... in an educational programme. Conclusion. The 1% prevalence of epoxy resin contact allergy is equivalent to reports from other countries. The high occurrence of epoxy resin exposure at work, and the limited use of protective measures, indicate that reinforcement of the law is required....

Mechanical Properties of Epoxy and Its Carbon Fiber Composites Modified by Nanoparticles

Directory of Open Access Journals (Sweden)

Fang Liu

2017-01-01

Full Text Available Compressive properties are commonly weak parts in structural application of fiber composites. Matrix modification may provide an effective way to improve compressive performance of the composites. In this work, the compressive property of epoxies (usually as matrices of fiber composites modified by different types of nanoparticles was firstly investigated for the following study on the compressive property of carbon fiber reinforced epoxy composites. Carbon fiber/epoxy composites were fabricated by vacuum assisted resin infusion molding (VARIM technique using stitched unidirectional carbon fabrics, with the matrices modified with nanosilica, halloysite, and liquid rubber. Testing results showed that the effect of different particle contents on the compressive property of fiber/epoxy composites was more obvious than that in epoxies. Both the compressive and flexural results showed that rigid nanoparticles (nanosilica and halloysite have evident strengthening effects on the compression and flexural responses of the carbon fiber composite laminates fabricated from fabrics.

Modified silyl-terminated polyether polymer blends with bisphenol A diglycidyl ether epoxy for adhesive applications

International Nuclear Information System (INIS)

Bitenieks, J; Meri, R Merijs; Zicans, J; Berzins, R; Umbraško, J; Rekners, U

2016-01-01

Modified silyl-terminated polyether polymer (MS Polymer) was blended with bisphenol A diglycidyl ether (DGEBPA) epoxy at MS Polymer/epoxy ratio from 30/70 to 70/30. MS Polymer/epoxy systems were examined for two-component adhesive formulation with additional fillers. Applicability of the MS Polymer/epoxy system at the ratio of the components 60/40 is demonstrated for the development of adhesive formulation. Rheological analysis of the components A and B shows suitable viscosity values for development of two- component adhesives formulation. Curing dynamics as well as tensile stress-strain properties and Shore A hardness of the chosen adhesive formulation are reasonable for the development of MS Polymer/epoxy type adhesive. (paper)

Development of epoxy resin-type neutron shielding materials (I)

Energy Technology Data Exchange (ETDEWEB)

Cho, Soo Haeng; Kim, Ik Soo; Shin, Young Joon; Do, Jae Bum; Ro, Seung Gy

1997-12-01

Because the exposure to radiation in the nuclear facilities can be fatal to human, it is important to reduce the radiation dose level to a tolerable level. The purpose of this study is to develop highly effective neutron shielding materials for the shipping and storage cask of radioactive materials or in the nuclear /radiation facilities. On this study, we developed epoxy resin based neutron shielding materials and their various materials properties, including neutron shielding ability, fire resistance, combustion characteristics, radiation resistance, thermal and mechanical properties were evaluated experimentally. (author). 31 refs., 22 tabs., 17 figs.

Zirconium tungstate/epoxy nanocomposites: effect of nanoparticle morphology and negative thermal expansivity.

Science.gov (United States)

Wu, Hongchao; Rogalski, Mark; Kessler, Michael R

2013-10-09

The ability to tailor the coefficient of thermal expansion (CTE) of a polymer is essential for mitigating thermal residual stress and reducing microcracks caused by CTE mismatch of different components in electronic applications. This work studies the effect of morphology and thermal expansivity of zirconium tungstate nanoparticles on the rheological, thermo-mechanical, dynamic-mechanical, and dielectric properties of ZrW2O8/epoxy nanocomposites. Three types of ZrW2O8 nanoparticles were synthesized under different hydrothermal conditions and their distinct properties were characterized, including morphology, particle size, aspect ratio, surface area, and CTE. Nanoparticles with a smaller particle size and larger surface area led to a more significant reduction in gel-time and glass transition temperature of the epoxy nanocomposites, while a higher initial viscosity and significant shear thinning behavior was found in prepolymer suspensions containing ZrW2O8 with larger particle sizes and aspect ratios. The thermo- and dynamic-mechanical properties of epoxy-based nanocomposites improved with increasing loadings of the three types of ZrW2O8 nanoparticles. In addition, the introduced ZrW2O8 nanoparticles did not negatively affect the dielectric constant or the breakdown strength of the epoxy resin, suggesting potential applications of ZrW2O8/epoxy nanocomposites in the microelectronic insulation industry.

Effective functionalization of carbon nanotubes for bisphenol F epoxy matrix composites

Directory of Open Access Journals (Sweden)

Zhe Wang

2012-08-01

Full Text Available A brand-new type of multifunctional nanocomposites with high DC conductivity and enhanced mechanical strength was fabricated. Ionic liquid functionalized Carbon Nanotubes (CNTs-IL were embedded into epoxy matrix with covalent bonding by the attached epoxy groups. The highest DC conductivity was 8.38 x 10-3 S.m-1 with 1.0 wt. (% loading of CNTs-IL and the tensile strength was increased by 36.4% only at a 0.5 wt. (% concentration. A mixing solvent was used to disperse CNTs-IL in the epoxy monomer. The dispersion and distribution of CNTs-IL in the polymer matrix were measured by utilizing both optical microscopy and scanning electron microscopy, respectively.

Molecular Modeling of Aerospace Polymer Matrices Including Carbon Nanotube-Enhanced Epoxy

Science.gov (United States)

Radue, Matthew S.

-functionalresins) are simulated with embedded CNT to understand how the affinity to nanoparticles affects the mechanical response. Multiscale modeling techniques are then employed to translate the molecular phenomena observed to predict the behavior of realistic composites. The effective stiffness of hybrid composites are predicted for CNT/epoxy composites with randomly oriented CNTs, for CF/CNT/epoxy systems with aligned CFs and randomly oriented CNTs, and for woven CF/CNT/epoxy fabric with randomly oriented CNTs. The results indicate that in the CNT/epoxy systems the epoxy type has a significant influence on the elastic properties. For the CF/CNT/epoxy hybrid composites, the axial modulus is highly influenced by CF concentration, while the transverse modulus is primarily affected by the CNT weight fraction.

Tailored SWCNT functionalization optimized for compatibility with epoxy matrices

International Nuclear Information System (INIS)

Martinez-Rubi, Y; Kingston, C T; Daroszewska, M; Barnes, M; Simard, B; Gonzalez-Dominguez, J M; Ansón-Casaos, A; Martinez, M T; Hubert, P; Cattin, C

2012-01-01

We have modified single walled carbon nanotubes (SWCNTs) with well defined matrix-based architectures to improve interface interaction in SWCNT/epoxy composites. The hardener and two pre-synthesized oligomers containing epoxy and hardener moieties were covalently attached to the SWCNT walls by in situ diazonium or carboxylic coupling reactions. In this way, SWCNTs bearing amine or epoxide-terminated fragments of different molecular weights, which resemble the chemical structure of the cured resin, were synthesized. A combination of characterization techniques such as Raman and infrared absorption (FTIR) spectroscopy, elemental analysis and coupled thermogravimetry-FTIR spectroscopy were used to identify both the functional groups and degree of functionalization of SWCNTs synthesized by the laser ablation and arc-discharge methods. Depending on the type of reaction employed for the chemical functionalization and the molecular weight of the attached fragment, it was possible to control the degree of functionalization and the electronic properties of the functionalized SWCNTs. Improved dispersion of SWCNTs in the epoxy matrix was achieved by direct integration without using solvents, as observed from optical microscopy and rheology measurements of the SWCNT/epoxy mixtures. Composite materials using these fillers are expected to exhibit improved properties while preserving the thermosetting architecture. (paper)

Epoxy-based carbon nanotubes reinforced composites

CSIR Research Space (South Africa)

Kesavan Pillai, Sreejarani

2011-04-01

Full Text Available of the three major epoxy resin producers worldwide [May, 1987]. Epoxy resin is most commonly used as a matrix for advanced composites due to their superior thermal, mechanical and electrical properties; dimensional stability and chemical resistance. Epoxy... are electrical insulators, and the widespread use of the epoxy resins for many high-performance applications is constrained because of their inherent brittleness, delamination and fracture toughness limitations. There were quite a few approaches to enhance...

Evaluation and Control of Thiol-ene/Thiol-epoxy Hybrid Networks.

Science.gov (United States)

Carioscia, Jacquelyn A; Stansbury, Jeffrey W; Bowman, Christopher N

2007-03-08

The development of thiol-ene/thiol-epoxy hybrid networks offers the advantage of tailorable polymerization kinetics while producing a highly crosslinked, high T(g) polymer that has significantly reduced shrinkage stress. Stoichiometric mixtures of pentaerythritol tetra(3-mercaptopropionate) (PETMP)/triallyl-1,3,5-triazine-2,4,6-trione (TATATO) (thiol-ene, mixture 1) and PETMP/bisphenol a diglycidyl ether (BADGE) (thiol-epoxy, mixture 2) were prepared and hybrid mixtures of 75/25, 50/50, 25/75, and 10/90 w/w of mixtures 1 and 2 were polymerized using a combination of both radical and anionic initiation. The light exposure timing and the relative initiation conditions of the two types were used to control the order and relative rates of the radical and anionic polymerizations. The 50/50 w/w thiol-ene/thiol-epoxy hybrid material exhibited a final stress of only 0.2 MPa, which is 90 % lower than the stress developed in a control dimethacrylate resin. Kinetic analysis indicates composition affects network development in thiol-ene/thiol-epoxy hybrid networks and produces materials with robust mechanical properties.

Thermal expansion of epoxy-fiberglass composite specimens

International Nuclear Information System (INIS)

McElroy, D.L.; Weaver, F.J.; Bridgman, C.

1986-01-01

The thermal expansion behavior of three epoxy-fiberglass composite specimens was measured from 20 to 120 0 C (70 to 250 0 F) using a fused quartz push-rod dilatometer. Billets produced by vacuum impregnating layers of two types of fiberglass cloth with an epoxy resin were core-drilled to produce cylindrical specimens. These were used to study expansion perpendicular and parallel to the fiberglass layers. The dilatometer is held at a preselected temperature until steady-state is indicated by stable length and temperature data. Before testing the composite specimens, a reliability check of the dilatometer was performed using a copper secondary standard. This indicated thermal expansion coefficient (α) values within +-2% of expected values from 20 to 200 0 C

Thermally activated, single component epoxy systems

KAUST Repository

Unruh, David A.; Pastine, Stefan J.; Moreton, Jessica C.; Frechet, Jean

2011-01-01

A single component epoxy system in which the resin and hardener components found in many two-component epoxies are combined onto the same molecule is described. The single molecule precursor to the epoxy resin contains both multiple epoxide moieties and a diamine held latent by thermally degradable carbamate linkages. These bis-carbamate "single molecule epoxies" have an essentially infinite shelf life and access a significant range in curing temperatures related to the structure of the carbamate linkages used. © 2011 American Chemical Society.

Thermally activated, single component epoxy systems

KAUST Repository

Unruh, David A.

2011-08-23

A single component epoxy system in which the resin and hardener components found in many two-component epoxies are combined onto the same molecule is described. The single molecule precursor to the epoxy resin contains both multiple epoxide moieties and a diamine held latent by thermally degradable carbamate linkages. These bis-carbamate "single molecule epoxies" have an essentially infinite shelf life and access a significant range in curing temperatures related to the structure of the carbamate linkages used. © 2011 American Chemical Society.

Low-Dissipation Thermosets Derived from Oligo(2,6-Dimethyl Phenylene Oxide-Containing Benzoxazines

Directory of Open Access Journals (Sweden)

Chien-Han Chen

2018-04-01

Full Text Available Poly(2,6-dimethyl phenyl oxide (PPO is known for its low dissipation factor. To achieve insulating materials with low dissipation factors for high-frequency communication applications, a telechelic oligomer-type benzoxazine (P-APPO and a main-chain type benzoxazine polymer (BPA-APPO were prepared from an amine end-capped oligo (2,6-dimethyl phenylene oxide (APPO. The APPO was prepared from a nucleophilic substitution of a phenol-end capped oligo (2,6-dimethyl phenylene oxide (a commercial product, SA 90 with fluoronitrobenzene, and followed by catalytic hydrogenation. After self-curing or curing with a dicyclopentadiene-phenol epoxy (HP 7200, thermosets with high-Tg and low-dissipation factor can be achieved. Furthermore, the resulting epoxy thermosets show better thermal and dielectric properties than those of epoxy thermoset cured from its precursor SA90, demonstrating it is a successful modification in simultaneously enhancing the thermal and dielectric properties.

Synthesis of alkyl phenols by means of radiofrequency plasmas

International Nuclear Information System (INIS)

Ropero, M.; Armas, F.; Iacocca, D.; Patino, P.

1992-01-01

New and promising possibilities in chemical synthesis have been opened through the interactions of oxygen plasmas with liquid alkyl benzene compounds. The alkyl phenols are the main products of the reaction mixtures (> 80%) oxygen, excited by radio-frequency (R.F.) is allowed to reach the surface of the liquid organic compound. The R.F. power supply is a Branson/IPC-PM 118. The substrate we have chosen are: methyl, ethyl, propyl, n-butyl, t-butyl, dimethyl and trimethyl benzenes. Under the same O 2 pressure and a power of 60 W, m-xylene and mesethylene behaved similarly. For all these substrates, values for the temperature of the liquid surface seem to indicate that oxidation tends to an optimum when P O 2 /vapor pressure (substrate) is higher than 20. In our experiments oxygen pressure in the reactor was about 0.2 Torr. Oxidation is basically attributed to O 3 P and the addition to alkyl benzenes selectively takes place on the aromatic rings, at low reactor pressure. The oxygen atom impinges on the liquid surface and epoxy intermediates could be formed. These intermediates then progress to the corresponding phenols. (author)

Physiological and functional diversity of phenol degraders isolated from phenol-grown aerobic granules: Phenol degradation kinetics and trichloroethylene co-metabolic activities.

Science.gov (United States)

Zhang, Yi; Tay, Joo Hwa

2016-03-15

Aerobic granule is a novel form of microbial aggregate capable of degrading toxic and recalcitrant substances. Aerobic granules have been formed on phenol as the growth substrate, and used to co-metabolically degrade trichloroethylene (TCE), a synthetic solvent not supporting aerobic microbial growth. Granule formation process, rate limiting factors and the comprehensive toxic effects of phenol and TCE had been systematically studied. To further explore their potential at the level of microbial population and functions, phenol degraders were isolated and purified from mature granules in this study. Phenol and TCE degradation kinetics of 15 strains were determined, together with their TCE transformation capacities and other physiological characteristics. Isolation in the presence of phenol and TCE exerted stress on microbial populations, but the procedure was able to preserve their diversity. Wide variation was found with the isolates' kinetic behaviors, with the parameters often spanning 3 orders of magnitude. Haldane kinetics described phenol degradation well, and the isolates exhibited actual maximum phenol-dependent oxygen utilization rates of 9-449 mg DO g DW(-1) h(-1), in phenol concentration range of 4.8-406 mg L(-1). Both Michaelis-Menten and Haldane types were observed for TCE transformation, with the actual maximum rate of 1.04-21.1 mg TCE g DW(-1) h(-1) occurring between TCE concentrations of 0.42-4.90 mg L(-1). The TCE transformation capacities and growth yields on phenol ranged from 20-115 mg TCE g DW(-1) and 0.46-1.22 g DW g phenol(-1), respectively, resulting in TCE transformation yields of 10-70 mg TCE g phenol(-1). Contact angles of the isolates were between 34° and 82°, suggesting both hydrophobic and hydrophilic cell surface. The diversity in the isolates is a great advantage, as it enables granules to be versatile and adaptive under different operational conditions. Copyright © 2015 Elsevier Ltd. All rights reserved.

Influence of the silica fillers on the ageing of epoxy resins under irradiations

International Nuclear Information System (INIS)

Benard, F.

2004-01-01

Various studies were carried out on the ageing of epoxy resins under irradiations. In all cases, pure polymers were studied. The aim of our work managed by the CEA and the CNRS consists on studying the part of fillers and particularly the part of silica on ageing process under electron beam irradiations. Because of their wide use in industrial applications and especially in nuclear environment, the DGEBA-TETA resins (Diglycidylether of Bisphenol A - Triethylenetetramine) were chosen. Those epoxy resins are difficult to analyse because of their insolubility. Some pure and nano-metric silica filled chemical models which chemical structure very close to the one the DGEBA/TETA resin were synthesized and analysed with classical methods in organic chemistry. A major phenomenon of rupture of the C-O and C-N chemical bonds with creation of phenolic extremities, methylketone extremities, of primary and tertiary amines and notably enamine functions were revealed by the analyses. The quantitative 1 H and 13 C NMR analyses revealed the screen effect due to the silica and the reactions between the chemical species created by the irradiations and the silica surface. Thermic and thermodynamic analyses of the different epoxy resins in function of the irradiation dose and of the kind of silica showed the decrease of the glass transition temperature, of the relaxation temperature and of the crosslink density confirming the major phenomenon of bond ruptures during irradiations. With silica, the decrease of the crosslink density is slowed. This phenomenon can be explained with interactions between the nano-metric silica surface and the epoxy resin offsetting the effect of the chain rupture on the resin mechanical properties. The 13 C solid state NMR analyses confirmed the choice of the chemical models and permitted to detect the chemical species created by the irradiations. The analyse of the polarization transfers with 13 C CP-MAS NMR spectroscopy revealed the stiffening of the nano

Characterization of Epoxy Functionalized Graphite Nanoparticles and the Physical Properties of Epoxy Matrix Nanocomposites

Science.gov (United States)

Miller, Sandi G.; Bauer, Jonathan L.; Maryanski, Michael J.; Heimann, Paula J.; Barlow, Jeremy P.; Gosau, Jan-Michael; Allred, Ronald E.

2010-01-01

This work presents a novel approach to the functionalization of graphite nanoparticles. The technique provides a mechanism for covalent bonding between the filler and matrix, with minimal disruption to the sp2 hybridization of the pristine graphene sheet. Functionalization proceeded by covalently bonding an epoxy monomer to the surface of expanded graphite, via a coupling agent, such that the epoxy concentration was measured as approximately 4 wt.%. The impact of dispersing this material into an epoxy resin was evaluated with respect to the mechanical properties and electrical conductivity of the graphite-epoxy nanocomposite. At a loading as low as 0.5 wt.%, the electrical conductivity was increased by five orders of magnitude relative to the base resin. The material yield strength was increased by 30% and Young s modulus by 50%. These results were realized without compromise to the resin toughness.

Effect of Montmorillonite Nanogel Composite Fillers on the Protection Performance of Epoxy Coatings on Steel Pipelines.

Science.gov (United States)

Atta, Ayman M; El-Saeed, Ashraf M; Al-Lohedan, Hamad A; Wahby, Mohamed

2017-06-02

Montmorillonite (MMT) clay mineral is widely used as filler for several organic coatings. Its activity is increased by exfoliation via chemical modification to produce nanomaterials. In the present work, the modification of MMT to form nanogel composites is proposed to increase the dispersion of MMT into epoxy matrices used to fill cracks and holes produced by the curing exotherms of epoxy resins. The dispersion of MMT in epoxy improved both the mechanical and anti-corrosion performance of epoxy coatings in aggressive marine environments. In this respect, the MMT surfaces were chemically modified with different types of 2-acrylamido-2-methyl propane sulfonic acid (AMPS) nanogels using a surfactant-free dispersion polymerization technique. The effect of the chemical structure, nanogel content and the interaction with MMT surfaces on the surface morphology, surface charges and dispersion in the epoxy matrix were investigated for use as nano-filler for epoxy coatings. The modified MMT nanogel epoxy composites showed excellent resistance to mechanical damage and salt spray resistance up to 1000 h. The interaction of MMT nanogel composites with the epoxy matrix and good response of AMPS nanogel to sea water improve their ability to act as self-healing materials for epoxy coatings for steel.

An Overview of Plant Phenolic Compounds and Their Importance in Human Nutrition and Management of Type 2 Diabetes

Directory of Open Access Journals (Sweden)

Derong Lin

2016-10-01

Full Text Available In this paper, the biosynthesis process of phenolic compounds in plants is summarized, which includes the shikimate, pentose phosphate and phenylpropanoid pathways. Plant phenolic compounds can act as antioxidants, structural polymers (lignin, attractants (flavonoids and carotenoids, UV screens (flavonoids, signal compounds (salicylic acid and flavonoids and defense response chemicals (tannins and phytoalexins. From a human physiological standpoint, phenolic compounds are vital in defense responses, such as anti-aging, anti-inflammatory, antioxidant and anti-proliferative activities. Therefore, it is beneficial to eat such plant foods that have a high antioxidant compound content, which will cut down the incidence of certain chronic diseases, for instance diabetes, cancers and cardiovascular diseases, through the management of oxidative stress. Furthermore, berries and other fruits with low-amylase and high-glucosidase inhibitory activities could be regarded as candidate food items in the control of the early stages of hyperglycemia associated with type 2 diabetes.

Surface treated fly ash filled modified epoxy composites

Directory of Open Access Journals (Sweden)

Uma Dharmalingam

2015-01-01

Full Text Available Abstract Fly ash, an inorganic alumino silicate has been used as filler in epoxy matrix, but it reduces the mechanical properties due to its poor dispersion and interfacial bonding with the epoxy matrix. To improve its interfacial bonding with epoxy matrix, surface treatment of fly ash was done using surfactant sodium lauryl sulfate and silane coupling agent glycidoxy propyl trimethoxy silane. An attempt is also made to reduce the particle size of fly ash using high pressure pulverizer. To improve fly ash dispersion in epoxy matrix, the epoxy was modified by mixing with amine containing liquid silicone rubber (ACS. The effect of surface treated fly ash with varying filler loadings from 10 to 40% weight on the mechanical, morphological and thermal properties of modified epoxy composites was investigated. The surface treated fly ash was characterized by particle size analyzer and FTIR spectra. Morphological studies of surface treated fly ash filled modified epoxy composites indicate good dispersion of fillers in the modified epoxy matrix and improves its mechanical properties. Impact strength of the surface treated fly ash filled modified epoxy composites show more improvement than unmodified composites.

Effect of the hardener to epoxy monomer ratio on the water absorption behavior of the DGEBA/TETA epoxy system

Directory of Open Access Journals (Sweden)

Ayrton Alef Castanheira Pereira

2016-02-01

Full Text Available Abstract The water absorption behavior of the DGEBA/TETA epoxy system was evaluated as a function of the epoxy monomer to amine hardener ratio. Weight gain versus immersion time curves were obtained and the experimental points were fitted using Fickian and Non-Fickian diffusion models. The results obtained showed that for all epoxy monomer to hardener ratios analyzed water diffusion followed non-Fickian behavior. It was possible to correlate the water absorption behavior to the macromolecular structure developed when the epoxy/ hardener ratio was varied. All epoxy/hardener ratios present a two-phase macromolecular structure, composed of regions with high crosslink density and regions with lower crosslinking. Epoxy rich systems have a more open macromolecular structure with a lower fraction of the dense phase than the amine rich systems, which present a more compact two-phase structure.

A review of phenolic compounds in oil-bearing plants: Distribution, identification and occurrence of phenolic compounds.

Science.gov (United States)

Alu'datt, Muhammad H; Rababah, Taha; Alhamad, Mohammad N; Al-Mahasneh, Majdi A; Almajwal, Ali; Gammoh, Sana; Ereifej, Khalil; Johargy, Ayman; Alli, Inteaz

2017-03-01

Over the last two decades, separation, identification and measurement of the total and individual content of phenolic compounds has been widely investigated. Recently, the presence of a wide range of phenolic compounds in oil-bearing plants has been shown to contribute to their therapeutic properties, including anti-cancer, anti-viral, anti-oxidant, hypoglycemic, hypo-lipidemic, and anti-inflammatory activities. Phenolics in oil-bearing plants are now recognized as important minor food components due to several organoleptic and health properties, and they are used as food or sources of food ingredients. Variations in the content of phenolics in oil-bearing plants have largely been attributed to several factors, including the cultivation, time of harvest and soil types. A number of authors have suggested that the presence phenolics in extracted proteins, carbohydrates and oils may contribute to objectionable off flavors The objective of this study was to review the distribution, identification and occurrence of free and bound phenolic compounds in oil-bearing plants. Copyright © 2016 Elsevier Ltd. All rights reserved.

The application of epoxy resin coating in grounding grid

Science.gov (United States)

Hu, Q.; Chen, Z. R.; Xi, L. J.; Wang, X. Y.; Wang, H. F.

2018-01-01

Epoxy resin anticorrosion coating is widely used in grounding grid corrosion protection because of its wide range of materials, good antiseptic effect and convenient processing. Based on the latest research progress, four kinds of epoxy anticorrosive coatings are introduced, which are structural modified epoxy coating, inorganic modified epoxy coating, organic modified epoxy coating and polyaniline / epoxy resin composite coating. In this paper, the current research progress of epoxy base coating is analyzed, and prospected the possible development direction of the anti-corrosion coating in the grounding grid, which provides a reference for coating corrosion prevention of grounding materials.

Comparison of tensile strength of different carbon fabric reinforced epoxy composites

Directory of Open Access Journals (Sweden)

Jane Maria Faulstich de Paiva

2006-03-01

Full Text Available Carbon fabric/epoxy composites are materials used in aeronautical industry to manufacture several components as flaps, aileron, landing-gear doors and others. To evaluate these materials become important to know their mechanical properties, for example, the tensile strength. Tensile tests are usually performed in aeronautical industry to determinate tensile property data for material specifications, quality assurance and structural analysis. For this work, it was manufactured four different laminate families (F155/PW, F155/HS, F584/PW and F584/HS using pre-impregnated materials (prepregs based on F155TM and F584TM epoxy resins reinforced with carbon fiber fabric styles Plain Weave (PW and Eight Harness Satin (8HS. The matrix F155TM code is an epoxy resin type DGEBA (diglycidil ether of bisphenol A that contains a curing agent and the F584TM code is a modified epoxy resin type. The laminates were obtained by handing lay-up process following an appropriate curing cycle in autoclave. The samples were evaluated by tensile tests according to the ASTM D3039. The F584/PW laminates presented the highest values of tensile strength. However, the highest modulus results were determined for the 8HS composite laminates. The correlation of these results emphasizes the importance of the adequate combination of the polymeric matrix and the reinforcement arrangement in the structural composite manufacture. The microscopic analyses of the tested specimens show valid failure modes for composites used in aeronautical industry.

Contact allergy to epoxy (meth)acrylates.

Science.gov (United States)

Aalto-Korte, Kristiina; Jungewelter, Soile; Henriks-Eckerman, Maj-Len; Kuuliala, Outi; Jolanki, Riitta

2009-07-01

Contact allergy to epoxy (meth)acrylates, 2,2-bis[4-(2-hydroxy-3-methacryloxypropoxy) phenyl]propane (bis-GMA), 2,2-bis[4-(2-hydroxy-3-acryloxypropoxy)phenyl]-propane (bis-GA), 2,2-bis[4-(methacryl-oxyethoxy)phenyl] propane (bis-EMA), 2,2-bis[4-(methacryloxy)phenyl]-propane (bis-MA), and glycidyl methacrylate (GMA) is often manifested together with contact allergy to diglycidyl ether of bisphenol A (DGEBA) epoxy resin. To analyse patterns of concomitant allergic reactions to the five epoxy (meth)acrylates in relation to exposure. We reviewed the 1994-2008 patch test files at the Finnish Institute of Occupational Health (FIOH) for reactions to the five epoxy (meth)acrylates, and examined the patients' medical records for exposure. Twenty-four patients had an allergic reaction to at least one of the studied epoxy (meth)acrylates, but specific exposure was found only in five patients: two bis-GMA allergies from dental products, two bis-GA allergies from UV-curable printing inks, and one bis-GA allergy from an anaerobic glue. Only 25% of the patients were negative to DGEBA epoxy resin. The great majority of allergic patch test reactions to bis-GMA, bis-GA, GMA and bis-EMA were not associated with specific exposure, and cross-allergy to DGEBA epoxy resin remained a probable explanation. However, independent reactions to bis-GA indicated specific exposure. Anaerobic sealants may induce sensitization not only to aliphatic (meth)acrylates but also to aromatic bis-GA.

Design of carbon nanofiber embedded conducting epoxy resin

International Nuclear Information System (INIS)

Gantayat, Subhra; Sarkar, Niladri; Rout, Dibyaranjan; Swain, Sarat K.

2017-01-01

Acid treated carbon nanofiber (t-CNF) reinforced epoxy nanocomposites were fabricated by hand lay-up method with various wt % of t-CNF loadings. Pristine or unmodified carbon nano fibers (u-CNFs) were made compatible with epoxy matrix by means of mixed acid treatment. Fabricated nanocomposites were characterized with Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) study, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atomic force microscopy (AFM). Mechanical and thermal properties of the nanocomposites were measured as a function of t-CNF content. Effect of acid treated CNFs on to the mechanical properties of epoxy nanocomposites was justified by comparing the mechanical properties of epoxy/t-CNF and epoxy/u-CNF nanocomposites with same loading level. The electrical conductivity was achieved by epoxy resin with a threshold at 1 wt % of t-CNF. Substantial improvement in thermal, mechanical and electrical properties of the synthesized epoxy/t-CNF nanocomposites may be suitable for fabricating electronic devices. - Highlights: • Epoxy/t-CNF nanocomposites are characterized by XRD, FTIR, SEM, AFM and TEM. • Electrical conductivity was achieved by epoxy with a threshold at 1 wt% of t-CNF. • Tensile strength is enhanced by 40% due to dispersion of t-CNF. • Synthesized nanocomposites are suitable for fabricating electronic devises.

Design of carbon nanofiber embedded conducting epoxy resin

Energy Technology Data Exchange (ETDEWEB)

Gantayat, Subhra [Department of Chemistry, Veer Surendra Sai University of Technology, Burla, Sambalpur 768018, Odisha (India); School of Applied Sciences, KIIT University, Bhubaneswar 751024, Odisha (India); Sarkar, Niladri [Department of Chemistry, Veer Surendra Sai University of Technology, Burla, Sambalpur 768018, Odisha (India); Rout, Dibyaranjan [School of Applied Sciences, KIIT University, Bhubaneswar 751024, Odisha (India); Swain, Sarat K., E-mail: swainsk2@yahoo.co.in [Department of Chemistry, Veer Surendra Sai University of Technology, Burla, Sambalpur 768018, Odisha (India)

2017-01-15

Acid treated carbon nanofiber (t-CNF) reinforced epoxy nanocomposites were fabricated by hand lay-up method with various wt % of t-CNF loadings. Pristine or unmodified carbon nano fibers (u-CNFs) were made compatible with epoxy matrix by means of mixed acid treatment. Fabricated nanocomposites were characterized with Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) study, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atomic force microscopy (AFM). Mechanical and thermal properties of the nanocomposites were measured as a function of t-CNF content. Effect of acid treated CNFs on to the mechanical properties of epoxy nanocomposites was justified by comparing the mechanical properties of epoxy/t-CNF and epoxy/u-CNF nanocomposites with same loading level. The electrical conductivity was achieved by epoxy resin with a threshold at 1 wt % of t-CNF. Substantial improvement in thermal, mechanical and electrical properties of the synthesized epoxy/t-CNF nanocomposites may be suitable for fabricating electronic devices. - Highlights: • Epoxy/t-CNF nanocomposites are characterized by XRD, FTIR, SEM, AFM and TEM. • Electrical conductivity was achieved by epoxy with a threshold at 1 wt% of t-CNF. • Tensile strength is enhanced by 40% due to dispersion of t-CNF. • Synthesized nanocomposites are suitable for fabricating electronic devises.

Thermo-curable epoxy systems for nanoimprint lithography

International Nuclear Information System (INIS)

Wu, Chun-Chang; Hsu, Steve Lien-Chung

2010-01-01

In this work, we have used solvent-free thermo-curable epoxy systems for low-pressure and moderate-temperature nanoimprint lithography (NIL). The curing kinetic parameters and conversion of diglycidyl ether of bisphenol A (DGEBA) resin with different ambient-cure 930 and 954 hardeners were studied by the isothermal DSC technique. They are useful for the study of epoxy resins in the imprinting application. The DGEBA/930 and DGEBA/954 epoxy resists can be imprinted to obtain high-density nano- and micro-scale patterns on a flexible indium tin oxide/poly(ethylene terephthalate) (ITO/PET) substrate. The DGEBA/930 epoxy resin is not only suitable for resist material, but also for plastic mold material. Highly dense nanometer patterns can be successfully imprinted using a UV-curable resist from the DGEBA/930 epoxy mold. Using the replicated DGEBA/930 epoxy mold instead of the expensive master can prevent brittle failure of the silicon molds in the NIL

Fatigue life extension of epoxy materials using ultrafast epoxy-SbF5 healing system introduced by manual infiltration

Directory of Open Access Journals (Sweden)

X. J. Ye

2015-03-01

Full Text Available The present paper is devoted to the verification of the capability of epoxy-SbF5 system as a healing chemistry for rapidly retarding and/or arresting fatigue cracks in epoxy materials at room temperature. Owing to the very fast curing speed of epoxy catalyzed by SbF5, epoxy monomer and the hardener (ethanol solution of SbF5–ethanol complex are successively infiltrated into the fracture plane under cyclic loading during the tension-tension fatigue test. As a result, the mechanisms including hydrodynamic pressure crack tip shielding, polymeric wedge and adhesive bonding of the healing agent are revealed. It is found that the healing agent forms solidified wedge at the crack tip within 20 s after start of polymerization of the epoxy monomer, so that the highest healing effect is offered at the moment. The epoxy-SbF5 system proves to be effective in rapidly obstructing fatigue crack propagation (despite that its cured version has lower fracture toughness than the matrix, and satisfies the requirement of constructing fast self-healing polymeric materials.

The aba mutant of Arabidopsis thaliana is impaired in epoxy-carotenoid biosynthesis

Energy Technology Data Exchange (ETDEWEB)

Rock, C.D.; Zeevaart, J.A.D. (Michigan State Univ., East Lansing (United States))

1991-09-01

The three mutant alleles of the ABA locus of Arabidopsis thaliana result in plants that are deficient in the plant growth regulator abscisic acid (ABA). The authors have used {sup 18}O{sub 2} to label ABA in water-stressed leaves of mutant and wild-type Arabidopsis. Analysis by selected ion monitoring and tandem mass spectrometry of ({sup 18}O)ABA and its catabolites, phaseic acid and ABA-glucose ester ({beta}-D-glucopyranosyl abscisate), indicates that the aba genotypes are impaired in ABA biosynthesis and have a small ABA precursor pool of compounds that contain oxygens on the rings, presumably oxygenated carotenoids (xanthophylls). Quantitation of the carotenoids form mutant and wild-type leaves establishes that the aba alleles cause a deficiency of the epoxy-carotenoids violaxanthin and neoxanthin and an accumulation of their biosynthetic precursor, zeaxanthin. These results provide evidence that ABA is synthesized by oxidative cleavage of epoxy-carotenoids (the indirect pathway). Furthermore the carotenoid mutant they describe undergoes normal greening. Thus the aba alleles provide an opportunity to study the physiological roles of epoxy-carotenoids in photosynthesis in a higher plants.

Design and Analysis of Drive Shaft using Kevlar/Epoxy and Glass/Epoxy as a Composite Material

Science.gov (United States)

Karthikeyan, P.; Gobinath, R.; Kumar, L. Ajith; Jenish, D. Xavier

2017-05-01

In automobile industry drive shaft is one of the most important components to transmit power form the engine to rear wheel through the differential gear. Generally steel drive shaft is used in automobile industry, nowadays they are more interested to replace steel drive shaft with that of composite drive shaft. The overall objective of this paper is to analyze the composite drive shaft using to find out the best replacement for conventional steel drive shaft. The uses of advanced composite materials such as Kevlar, Graphite, Carbon and Glass with proper resins ware resulted in remarkable achievements in automobile industry because of its greater specific strength and specific modulus, improved fatigue and corrosion resistances and reduction in energy requirements due to reduction in weight as compared to steel shaft. This paper is to presents, the modeling and analysis of drive shaft using Kevlar/Epoxy and Glass/Epoxy as a composite material and to find best replacement for conventional steel drive shafts with an Kevlar/epoxy or Glass/Epoxy resin composite drive shaft. Modeling is done using CATIA software and Analysis is carried out by using ANSYS 10.0 software for easy understanding. The composite drive shaft reduces the weight by 81.67 % for Kevlar/Epoxy and 72.66% for Glass/Epoxy when compared with conventional steel drive shaft.

Fabrication of a Multi-Walled Nanotube (MWNT Ionic Liquid Electrode and Its Application for Sensing Phenolics in Red Wines

Directory of Open Access Journals (Sweden)

Kyo-Il Kim

2009-08-01

Full Text Available A multi-walled nanotube (MWNT ionic liquid was prepared by the immobilization of 1-butylimidazole bromide onto an epoxy group on a poly(glycidyl methacrylate-grafted MWNT, which was synthesized by radiation-induced graft polymerization of glycidyl methacrylate onto MWNT in an aqueous solution. Subsequently, a MWNT ionic liquid electrode was fabricated by hand-casting MWNT ionic liquid, tyrosinase, and chitosan solution as a binder on indium tin oxide (ITO glass. The sensing ranges of the MWNT ionic liquid electrode with immobilized tyrosinase was in the range of 0.01-0.08 mM in a phosphate buffer solution. The optimal conditions such as pH, temperature, and effects of different phenolic compounds were determined. The total phenolic compounds of three commercial red wines were also determined on the tyrosinase-immobilized biosensor.

Fracture behavior of α-zirconium phosphate-based epoxy nanocomposites

International Nuclear Information System (INIS)

Sue, H.-J.; Gam, K.T.; Bestaoui, N.; Clearfield, A.; Miyamoto, M.; Miyatake, N.

2004-01-01

The fracture behaviors of α-zirconium phosphate (α-ZrP) based epoxy nanocomposites, with and without core-shell rubber (CSR) toughening, were investigated. The state of exfoliation and dispersion of α-ZrP nanofiller in epoxy were characterized using X-ray scattering and various microscopy tools. The level of enhancement in storage moduli of epoxy nanocomposite against neat epoxy is found to depend on the state of exfoliation of α-ZrP as well as the damping characteristics of the epoxy matrix. The fracture process in epoxy nanocomposite is dominated by preferred crack propagation along the weak intercalated α-ZrP interfaces, and the presence of α-ZrP does not alter the fracture toughness of the epoxy matrix. However, the toughening using CSR can significantly improve the fracture toughness of the nanocomposite. The fracture mechanisms responsible for such a toughening effect in CSR-toughened epoxy nanocomposite are rubber particle cavitation, followed by shear banding of epoxy matrix. The ductility and toughenability of epoxy do not appear to be affected by the incorporation of α-ZrP. Approaches for producing toughened high performance polymer nanocomposites are discussed

Evaluation of mechanical properties of four different carbon/epoxy composites used in aeronautical field

Directory of Open Access Journals (Sweden)

Jane Maria Faulstich de Paiva

2005-03-01

Full Text Available Four families of carbon fiber reinforced composites (CFRC used in aeronautical industry were evaluated by flexural and interlaminar shear tests. It is also characterized three families of non-conditioned and conditioned CFRC by compression test. The composites were obtained by hand lay-up process in autoclave by using prepregs based on epoxy matrices (F155 and F584 and carbon fiber fabric reinforcements (PW-"Plain Weave" and 8HS-"Eight Harness Satin". The F155-epoxy matrix was cured at 121 °C and the F584-epoxy type at 177 °C. After molding, the laminates were cut in specimens attending the ASTM D790 for the flexural test, the ASTM D2344 for the interlaminar shear test (ILSS and the ASTM D3410 for the compressive test. The compressive tests were performed for testing the specimens before and after hygrothermal conditioning. The results show that the F584-epoxy matrix laminates present higher mechanical properties when compared to the F155-epoxy ones. The shear-tested samples observed by scanning electron microscopy and that ones tested in flexural, analyzed by stereoscopy, revealed that the fractured surfaces present typical aspects. The compressive results show that the hygrothermal conditioning caused the decrease of the compressive strength in, approximately, 8-20% depending on the laminate type. The failure modes of the tested specimens were evaluated showing good agreement with the literature.

Environmental Degradation and Durability of Epoxy-Clay Nanocomposites

Directory of Open Access Journals (Sweden)

Raman P. Singh

2010-01-01

Full Text Available This experimental investigation reports on the durability of epoxy-clay nanocomposites upon exposure to multiple environments. Nanocomposites are fabricated by mixing the clay particles using various combinations of mechanical mixing, high-shear dispersion, and ultrasonication. Clay morphology is characterized using X-ray diffraction and transmission electron microscopy. Specimens of both neat epoxy and the epoxy-clay nanocomposite are subjected to two environmental conditions: combined UV radiation and condensation on 3-hour repeat cycle and constant temperature-humidity, for a total exposure duration of 4770 hours. The presence of nanoscale clay inhibits moisture uptake, as demonstrated by exposure to constant temperature-humidity. Nonetheless, both materials lose mass under exposure to combined UV radiation and condensation due to the erosion of epoxy by a synergistic process. Surprisingly, the epoxy-clay specimens exhibit greater mass loss, as compared to neat epoxy. Mechanical testing shows that either environment does not significant affect the flexure modulus of either material. On the other hand, both materials undergo degradation in flexural strength when exposed to either environment. However, the epoxy-clay nanocomposite retains 37% more flexure strength than the neat epoxy after 4072 hours of exposure.

Environmental Degradation and Durability of Epoxy-Clay Nanocomposites

International Nuclear Information System (INIS)

Singh, R.P.; Zunjarrao, S.C.; Pandey, G.; Khait, M.; Korach, C.S.

2010-01-01

This experimental investigation reports on the durability of epoxy-clay nanocomposites upon exposure to multiple environments. Nanocomposites are fabricated by mixing the clay particles using various combinations of mechanical mixing, high-shear dispersion, and ultrasonication. Clay morphology is characterized using X-ray diffraction and transmission electron microscopy. Specimens of both neat epoxy and the epoxy-clay nanocomposite are subjected to two environmental conditions: combined UV radiation and condensation on 3-hour repeat cycle and constant temperature-humidity, for a total exposure duration of 4770 hours. The presence of nanoscale clay inhibits moisture uptake, as demonstrated by exposure to constant temperature-humidity. Nonetheless, both materials lose mass under exposure to combined UV radiation and condensation due to the erosion of epoxy by a synergistic process. Surprisingly, the epoxy-clay specimens exhibit greater mass loss, as compared to neat epoxy. Mechanical testing shows that either environment does not significant affect the flexure modulus of either material. On the other hand, both materials undergo degradation in flexural strength when exposed to either environment. However, the epoxy-clay nanocomposite retains 37% more flexure strength than the neat epoxy after 4072 hours of exposure.

Occupational exposure to epoxy resins

NARCIS (Netherlands)

Terwoert, J.; Kersting, K.

2014-01-01

Products based on epoxy resins as a binder have become popular in various settings, among which the construction industry and in windmill blade production, as a result of their excellent technical properties. However, due to the same properties epoxy products are a notorious cause of allergic skin

Atomistic modeling of thermomechanical properties of SWNT/Epoxy nanocomposites

Science.gov (United States)

Fasanella, Nicholas; Sundararaghavan, Veera

2015-09-01

Molecular dynamics simulations are performed to compute thermomechanical properties of cured epoxy resins reinforced with pristine and covalently functionalized carbon nanotubes. A DGEBA-DDS epoxy network was built using the ‘dendrimer’ growth approach where 75% of available epoxy sites were cross-linked. The epoxy model is verified through comparisons to experiments, and simulations are performed on nanotube reinforced cross-linked epoxy matrix using the CVFF force field in LAMMPS. Full stiffness matrices and linear coefficient of thermal expansion vectors are obtained for the nanocomposite. Large increases in stiffness and large decreases in thermal expansion were seen along the direction of the nanotube for both nanocomposite systems when compared to neat epoxy. The direction transverse to nanotube saw a 40% increase in stiffness due to covalent functionalization over neat epoxy at 1 K whereas the pristine nanotube system only saw a 7% increase due to van der Waals effects. The functionalized SWNT/epoxy nanocomposite showed an additional 42% decrease in thermal expansion along the nanotube direction when compared to the pristine SWNT/epoxy nanocomposite. The stiffness matrices are rotated over every possible orientation to simulate the effects of an isotropic system of randomly oriented nanotubes in the epoxy. The randomly oriented covalently functionalized SWNT/Epoxy nanocomposites showed substantial improvements over the plain epoxy in terms of higher stiffness (200% increase) and lower thermal expansion (32% reduction). Through MD simulations, we develop means to build simulation cells, perform annealing to reach correct densities, compute thermomechanical properties and compare with experiments.

Atomistic modeling of thermomechanical properties of SWNT/Epoxy nanocomposites

International Nuclear Information System (INIS)

Fasanella, Nicholas; Sundararaghavan, Veera

2015-01-01

Molecular dynamics simulations are performed to compute thermomechanical properties of cured epoxy resins reinforced with pristine and covalently functionalized carbon nanotubes. A DGEBA-DDS epoxy network was built using the ‘dendrimer’ growth approach where 75% of available epoxy sites were cross-linked. The epoxy model is verified through comparisons to experiments, and simulations are performed on nanotube reinforced cross-linked epoxy matrix using the CVFF force field in LAMMPS. Full stiffness matrices and linear coefficient of thermal expansion vectors are obtained for the nanocomposite. Large increases in stiffness and large decreases in thermal expansion were seen along the direction of the nanotube for both nanocomposite systems when compared to neat epoxy. The direction transverse to nanotube saw a 40% increase in stiffness due to covalent functionalization over neat epoxy at 1 K whereas the pristine nanotube system only saw a 7% increase due to van der Waals effects. The functionalized SWNT/epoxy nanocomposite showed an additional 42% decrease in thermal expansion along the nanotube direction when compared to the pristine SWNT/epoxy nanocomposite. The stiffness matrices are rotated over every possible orientation to simulate the effects of an isotropic system of randomly oriented nanotubes in the epoxy. The randomly oriented covalently functionalized SWNT/Epoxy nanocomposites showed substantial improvements over the plain epoxy in terms of higher stiffness (200% increase) and lower thermal expansion (32% reduction). Through MD simulations, we develop means to build simulation cells, perform annealing to reach correct densities, compute thermomechanical properties and compare with experiments. (paper)

Multi scale analysis by acoustic emission of damage mechanisms in natural fibre woven fabrics/epoxy composites.

Directory of Open Access Journals (Sweden)

Touchard F.

2010-06-01

Full Text Available This paper proposes to develop an experimental program to characterize the type and the development of damage in composite with complex microstructure. A multi-scale analysis by acoustic emission has been developed and applied to hemp fibre woven fabrics/epoxy composite. The experimental program consists of tensile tests performed on single yarn, neat epoxy resin and composite materials to identify their AE amplitude signatures. A statistical analysis of AE amplitude signals has been realised and correlated with microscopic observations. Results have enabled to identify three types of damage in composites and their associated AE amplitudes: matrix cracking, interfacial debonding and reinforcement damage and fracture. Tracking of these damage mechanisms in hemp/epoxy composites has been performed to show the process of damage development in natural fibre reinforced composites.

Chemistry and health of olive oil phenolics.

Science.gov (United States)

Cicerale, Sara; Conlan, Xavier A; Sinclair, Andrew J; Keast, Russell S J

2009-03-01

The Mediterranean diet is associated with a lower incidence of atherosclerosis, cardiovascular disease, and certain types of cancer. The apparent health benefits have been partially attributed to the dietary consumption of virgin olive oil by Mediterranean populations. Most recent interest has focused on the biologically active phenolic compounds naturally present in virgin olive oils. Studies (human, animal, in vivo and in vitro) have shown that olive oil phenolics have positive effects on certain physiological parameters, such as plasma lipoproteins, oxidative damage, inflammatory markers, platelet and cellular function, and antimicrobial activity. Presumably, regular dietary consumption of virgin olive oil containing phenolic compounds manifests in health benefits associated with a Mediterranean diet. This paper summarizes current knowledge on the physiological effects of olive oil phenolics. Moreover, a number of factors have the ability to affect phenolic concentrations in virgin olive oil, so it is of great importance to understand these factors in order to preserve the essential health promoting benefits of olive oil phenolic compounds.

Mechanical properties of graphene oxide (GO/epoxy composites

Directory of Open Access Journals (Sweden)

Shivan Ismael Abdullah

2015-08-01

Full Text Available In this study, the effects of graphene oxide (GO on composites based on epoxy resin were analyzed. Different contents of GO (1.5–6 vol.% were added to epoxy resin. The GO/epoxy composite was prepared using the casting method and was prepared under room temperature. Mechanical tests’ results such as tensile test, impact test and hardness test show enhancements of the mechanical properties of the GO/epoxy composite. The experimental results clearly show an improvement in the Young’s modulus, tensile strength and hardness. The impact strength was seen to decrease, pointing to brittleness increase of the GO/epoxy composite. A microstructure analysis using Scanning Electron Microscopy (SEM and X-ray diffraction (XRD analysis was also performed, which showed how GO impeded the propagation of cracks in the composite. From the SEM images we observed the interface between the GO and the epoxy composite. As can be seen from this research, the GO/epoxy composites can be used for a large number of applications. The results of this research are a strong evidence for GO/epoxy composites being a potential candidate for use in a variety of industrial applications, especially for automobile parts, aircraft components, and electronic parts such as supercapacitors, transistors, etc.

Epoxy resin casting of trim coils for superconducting cyclotron

International Nuclear Information System (INIS)

Hajra, D.P.; Sarkar, S.C.; Saha, Subimal; Chaudhuri, J.; Bhandari, R.K.

2006-01-01

The life of any magnet depends on the soundness of the coil insulation, its aging properties and initial and final endurance limitations. The insulation of water-cooled trim coils for superconducting cyclotron is made of glass fibre tape with heat cured unfilled epoxy resin combination. This type of insulation has been selected to achieve excellent stability against thermal and electromagnetic stresses, tight dimensional control, good dielectric strength, non-hygroscopic and considerably low vapour-pressure as it will be inside rough vacuum. The process development and the difficulties encountered for appropriate selection of epoxy resin combination, potting, vacuum process, curing cycle, control of coil dimension to achieve a sound coil absolutely free from cracks, trapped air and voids has been discussed. (author)

Epoxy resin systems for FGD units

International Nuclear Information System (INIS)

Brytus, V.; Puglisi, J.S.

1984-01-01

This paper discusses ongoing research work which is directed towards epoxy resins and curing agents which are designed to withstand aggressive environments. This work includes not only a chemical description of the materials involved, but the application testing necessary to verify the usefulness of these systems. It demonstrates that new high performance epoxy systems are superior to those which traditionally come to mind when one thinks epoxy. Finally, it discusses the results of testing designed specifically to screen candidates for use in FGD units

Sorption of phenol and phenol derivatives in hydrotalcite; Sorcion de fenol y derivados de fenol en hidrotalcita

Energy Technology Data Exchange (ETDEWEB)

Avina G, E I

2002-07-01

One of the main problems in Mexico and in the World is the waste water pollution of a great variety of industrial processes by organic compounds. Among those ones the phenol compounds which are highly toxic, refractories (to the chemical degradation) and poorly biodegradable. This is due in a large extent to the problem created by the accelerated increase in the environmental pollution in the cities and industrial centers. The phenol compounds are used in a great variety of industries such as the production of resins, plasticizers, antioxidants, pesticides, colourings, disinfectants, etc. These phenol compounds are specially harmful, since they have repercussions on the flora of plants of biological treatment of water affecting its operation. The main objective of this work is to evaluate the capacities of phenol detention and its derivatives in an hydrotalcite type compound and diminishing with it the presence in water, in this case, of solutions prepared in the laboratory. In order to analyse this elimination process was used a methodology based in the carrying out in batch experiments and in the elaboration of a sorption isotherm. It is worth pointing out that this work was realized at laboratory scale, at relatively high phenol concentration ratio. With the obtained results when the sorption properties are evaluated the calcined hydrotalcite (HTC) for detaining phenol and p-chloro phenol it was observed that it is detained greater quantity of p-chloro phenol than phenol in the HTC. The detention of these phenol compounds in the HTC is due to the memory effect by the hydrotalcite regeneration starting from the oxides which are formed by the burning material. (Author)

Erosion wear response of epoxy composites filled with steel industry slag and sludge particles: A comparative study

Science.gov (United States)

Purohit, Abhilash; Satapathy, Alok

2018-03-01

In the field of composite research, use of industrial wastes such as slag and sludge particles as filler in wear resistant polymer composites has not been very common. Owing to the very high cost of conventional filler materials in polymer composites, exploring the possibility of using low cost minerals and industrial wastes for this purpose has become the need of the hour. In this context this work explores the possibility of such polymer composites filled with low cost industrial wastes and presents a comparison of mechanical characteristics among three types of epoxy based composites filled with Linz - Donawitz sludge (LD sludge), blast furnace slag (BF slag) and Linz - Donawitz slag (LD slag) respectively. A comparative study in regard to their solid particle erosion wear characteristics under similar test conditions is also included. Composites with different weight proportions (0, 5, 10, 15 and 20 wt. %) of LD sludge are fabricated by solution casting technique. Mechanical properties such as micro- hardness, tensile strength and flexural strength of three types of composites have been evaluated as per ASTM test standards and solid particle erosion wear test is performed following a design of experiment approach based on Taguchi’s orthogonal array. Five control factors (impact velocity, erodent size, filler content, impingement angle and erodent temperature) each at five levels are considered to conduct erosion wear tests. The test results for epoxy-LD sludge composites are compared with those of epoxy-BF slag and epoxy-LD slag composites reported by previous investigators. The comparison reveals that epoxy filled with LD sludge exhibits superior mechanical and erosion wear characteristics among the three types of composites considered in this study. This work also opens up a new avenue for value added utilization of an abundant industrial waste in the making of epoxy based functional composites.

[Branch-specific detection of phenols and assessment of ground water solubility].

Science.gov (United States)

Fischer, F; Kerndorff, H; Kühn, S

2000-01-01

There are about 500 technically relevant phenolic compounds such as cresols, chlorophenols or nitrophenols. It is most preferable to determine phenols as single compounds via gas chromatography. Further, phenols can also be assayed as photometrically as an overall parameter (Phenolindex): however, no conclusions about specific compounds can be drawn from this type of test. Also this method is not as reliable for an hazard assessment as gas chromatography. First, not all phenols, for instance resorcinol or 1-naphthol can be determined with this method. Second, phenolic groups in humic substances, which do not constitute a threat for groundwater, are determined alongside environmentally relevant phenols using this method. In most cases, it is possible to deduce which phenols can be expected in the groundwater of contaminated sites from the type of industrial usage, such as chlorophenols and pulp bleaching or nitrophenols and the production of explosives. Phenols are formed during coal combustion for instance at cokemanufactures or gasworks. They are important raw materials for the chemical industry from which resins, surfactants, pharmaceuticals, pigments, explosives, and stabilizers are produced. During the 80's phenol, cresols, nonylphenols, anisidines, aminophenols, dihydroxybenzenes, and naphthols were manufactured in amounts exceeding 10,000 t/a. Also, phenolic compounds are used as additives in many areas for example as solvents in the electric industry, in sawmills, papermanufacture, electroplating of metal sheets, as photographic developers, as textile dyes, or for the tanning of hydes. Due to the formation and use of phenols at industrial sites, groundwater contaminations are possible via infiltration through the unsaturated zone. Especially at gasworks and ammunition factories, groundwater contaminations with phenols have become known. In the vicinity of railway tracks and associated facillities contaminations due to the use of pesticides or mineral oils

Adhesion between coating layers based on epoxy and silicone

DEFF Research Database (Denmark)

Svendsen, Jacob R.; Kontogeorgis, Georgios; Kiil, Søren

2007-01-01

The adhesion between a silicon tie-coat and epoxy primers, used in marine coating systems, has been studied in this work. Six epoxy coatings (with varying chain lengths of the epoxy resins), some of which have shown problems with adhesion to the tie-coat during service life, have been considered....... The experimental investigation includes measurements of the surface tension of the tie-coat and the critical surface tensions of the epoxies, topographic investigation of the surfaces of cured epoxy coatings via atomic force microscopy (AFM), and pull-off tests for investigating the strength of adhesion...... to the silicon/epoxy systems. Calculations for determining the roughness factor of the six epoxy coatings (based on the AFM topographies) and the theoretical work of adhesion have been carried out. The coating surfaces are also characterized based on the van Oss-Good theory. Previous studies on the modulus...

Design and characterization of cellulose nanocrystal-enhanced epoxy hardeners

Science.gov (United States)

Shane X. Peng; Robert J. Moon; Jeffrey P. Youngblood

2014-01-01

Cellulose nanocrystals (CNCs) are renewable, sustainable, and abundant nanomaterial widely used as reinforcing fillers in the field of polymer nanocomposites. In this study, two-part epoxy systems with CNC-enhanced hardeners were fabricated. Three types of hardeners, Jeffamine D400 (JD400), diethylenetriamine (DETA), and (±)-trans-1,2- diaminocyclohexane (DACH), were...

Fabrication process and electromagnetic wave absorption characterization of a CNT/Ni/epoxy nanocomposite.

Science.gov (United States)

Ryu, Seongwoo; Mo, Chan Bin; Lee, Haeshin; Hong, Soon Hyung

2013-11-01

Since carbon nanotube (CNT) was first discovered in 1991, it has been considered as a viable type of conductive filler for electromagnetic wave absorption materials in the GHz range. In this paper, pearl-necklace-structure CNT/Ni nano-powders were fabricated by a polyol process as conductive fillers. Compared to synthesized CNT, pearl-necklace Ni-decorated CNT increased the electrical conductivity by an order of 1 due to the enhancement of the Ni-conductive network. Moreover, the decorated Ni particles prevented the agglomeration of CNTs by counterbalancing the Van der Walls interaction between the CNTs. A CNT/Ni nanocomposite showed a homogeneous dispersion in an epoxy-based matrix. This enhanced physical morphology and electrical properties lead to an increase in the loss tangent and reflection loss in the CNT/Ni/Epoxy nanocomposite compared to these characteristics of a CNT/Epoxy nanocomposite in range of 8-12 GHz. The electromagnetic wave absorption properties of CNT/Ni/epoxy nanocomposites will provide enormous opportunities for electronic applications where lightweight EMI shielding or electro-magnetic wave absorption properties are necessary.

Cure Kinetics of Epoxy Nanocomposites Affected by MWCNTs Functionalization: A Review

Science.gov (United States)

Saeb, Mohammad Reza; Bakhshandeh, Ehsan; Khonakdar, Hossein Ali; Mäder, Edith; Scheffler, Christina; Heinrich, Gert

2013-01-01

The current paper provides an overview to emphasize the role of functionalization of multiwalled carbon nanotubes (MWCNTs) in manipulating cure kinetics of epoxy nanocomposites, which itself determines ultimate properties of the resulting compound. In this regard, the most commonly used functionalization schemes, that is, carboxylation and amidation, are thoroughly surveyed to highlight the role of functionalized nanotubes in controlling the rate of autocatalytic and vitrification kinetics. The current literature elucidates that the mechanism of curing in epoxy/MWCNTs nanocomposites remains almost unaffected by the functionalization of carbon nanotubes. On the other hand, early stage facilitation of autocatalytic reactions in the presence of MWCNTs bearing amine groups has been addressed by several researchers. When carboxylated nanotubes were used to modify MWCNTs, the rate of such reactions diminished as a consequence of heterogeneous dispersion within the epoxy matrix. At later stages of curing, however, the prolonged vitrification was seen to be dominant. Thus, the type of functional groups covalently located on the surface of MWCNTs directly affects the degree of polymer-nanotube interaction followed by enhancement of curing reaction. Our survey demonstrated that most widespread efforts ever made to represent multifarious surface-treated MWCNTs have not been directed towards preparation of epoxy nanocomposites, but they could result in property synergism. PMID:24348181

Allergic Reaction to Polyether Ether Ketone Following Cross-Reactivity to Epoxy Resin.

Science.gov (United States)

Kofler, Lukas; Wambacher, Markus; Schweinzer, Katrin; Scherl, Maritta; Kofler, Heinz

Polyether ether ketone (PEEK) is a thermoplastic polymer frequently used in engineering but also in medical devices. Only 1 case of allergic reaction to PEEK used as an implanted medical device has been reported so far; however, the route of sensitization remained unclear. Here we report on a 62-year-old male patient with a preknown, severe type IV allergy to epoxy resin. He reported strong pain in his shoulder after implantation of a PEEK-containing device after a rotator cuff injury. For testing, the device was implanted in a small pouch subcutaneously on the abdomen. The patient reported massive pain starting 8 hours after the implantation, strictly limited to the procedural area and showing perifocal erythema. A possible explanation of the sensitization mode is the source material for PEEK and epoxy resin, as both are mainly based on bisphenols. An allergic reaction to PEEK with preknown epoxy resin sensitization has not been reported so far. As epoxy resins are a frequent cause of occupational contact dermatitis and PEEK is widely used for medical and nonmedical devices, we believe that this is of great clinical relevance.

Morphology and properties of silica/novolac hybrid xerogels synthesized using sol–gel polymerization at solvent vapor-saturated atmosphere

International Nuclear Information System (INIS)

Seraji, Mohamad Mehdi; Seifi, Azadeh; Bahramian, Ahmad Reza

2015-01-01

Highlights: • Sol–gel polymerization in vapor of solvent saturated atmosphere is developed. • Highly porous novolac–silica hybrid xerogels are successfully synthesized. • Novolac–silica hybrid gel was dried in ambient condition with low shrinkage. • Required time for preparation of gel reduced from 5 days to about 5 h. • By incorporation of silica into the novolac xerogel structure, the pore size decreases. - Abstract: Highly porous novolac–silica hybrid xerogels were successfully synthesized via the novel method of sol–gel polymerization in solvent vapor-saturated atmosphere. This method removes the need for supercritical drying and yields the hybrid xerogels with reduced shrinkage in comparison with conventional sol–gel process. Tetraethoxysilane (TEOS) was used as the precursor of silica-based inorganic phase. The chemical and structural characterization of the prepared hybrid xerogels were performed by Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM) analysis, respectively. Thermal and mechanical properties of the hybrid samples were investigated by differential scanning calorimetry (DSC), and compressive strength analysis. The resultant hybrid xerogels show a nanostructured colloidal hybrid network with high porosity (above 80%) and low density (below 0.25 g cm −3 ). Si mapping images shows the good distribution of silica phase throughout the hybrid structure

Action of ionizing radiation on epoxy resins

Energy Technology Data Exchange (ETDEWEB)

Van de Voorde, M. E.

1970-12-01

The resistance of classical and experimental epoxy resins to irradiation was studied. The resistance to irradiation of epoxy resins of diverse compositions as well as the development of resins having a radioresistance that approaches that of certain ceramics are discussed. Sources of irradiation and the techniques of dosimetry used are described. The structures of certain epoxy resins and of hardeners are given. The preparation of these resins and their physical properties is described. The effects of radiation on epoxy resins, as well as conditions of irradiation, and suggested mechanisms for degradation of the irradiated resins are discussed. The relationship between chemical structure of the resins and their physical properties is evaluated. (115 references) (JCB)

Experimental and Numerical Simulation Analysis of Typical Carbon Woven Fabric/Epoxy Laminates Subjected to Lightning Strike

Science.gov (United States)

Yin, J. J.; Chang, F.; Li, S. L.; Yao, X. L.; Sun, J. R.; Xiao, Y.

2017-12-01

To clarify the evolution of damage for typical carbon woven fabric/epoxy laminates exposed to lightning strike, artificial lightning testing on carbon woven fabric/epoxy laminates were conducted, damage was assessed using visual inspection and damage peeling approaches. Relationships between damage size and action integral were also elucidated. Results showed that damage appearance of carbon woven fabric/epoxy laminate presents circular distribution, and center of the circle located at the lightning attachment point approximately, there exist no damage projected area dislocations for different layers, visual damage territory represents maximum damage scope; visible damage can be categorized into five modes: resin ablation, fiber fracture and sublimation, delamination, ablation scallops and block-shaped ply-lift; delamination damage due to resin pyrolysis and internal pressure exist obvious distinguish; project area of total damage is linear with action integral for the same type specimens, that of resin ablation damage is linear with action integral, but no correlation with specimen type, for all specimens, damage depth is linear with logarithm of action integral. The coupled thermal-electrical model constructed is capable to simulate the ablation damage for carbon woven fabric/epoxy laminates exposed to simulated lightning current through experimental verification.

Wine phenolics.

Science.gov (United States)

Waterhouse, Andrew L

2002-05-01

Wine contains many phenolic substances, most of which originate in the grape berry. The phenolics have a number of important functions in wine, affecting the tastes of bitterness and astringency, especially in red wine. Second, the color of red wine is caused by phenolics. Third, the phenolics are the key wine preservative and the basis of long aging. Lastly, since phenolics oxidize readily, they are the component that suffers owing to oxidation and the substance that turns brown in wine (and other foods) when exposed to air. Wine phenolics include the non-flavonoids: hydroxycinnamates, hydroxybenzoates and the stilbenes; plus the flavonoids: flavan-3-ols, the flavonols, and the anthocyanins. While polymeric condensed tannins and pigmented tannins constitute the majority of wine phenolics, their large size precludes absorption and thus they are not likely to have many health effects (except, perhaps, in the gut). The total amount of phenols found in a glass of red wine is on the order of 200 mg versus about 40 mg in a glass of white wine.

Flexural Properties of Activated Carbon Filled Epoxy Nano composites

International Nuclear Information System (INIS)

Khalil, H.P.S.A.; Khalil, H.P.S.A.; Alothman, O.Y.; Paridah, M.T.; Zainudin, E.S.

2014-01-01

Activated carbon (AC) filled epoxy nano composites obtained by mixing the desired amount of nano AC viz., bamboo stem, oil palm empty fruit bunch, and coconut shell from agricultural biomass with the epoxy resin. Flexural properties of activated carbons filled epoxy nano composites with 1 %, and 5 % filler loading were measured. In terms of flexural strength and modulus, a significant increment was observed with addition of 1 % vol and 5 % vol nano-activated carbon as compared to neat epoxy. The effect of activated carbon treated by two chemical agents (potassium hydroxide and phosphoric acid) on the flexural properties of epoxy nano composites were also investigated. Flexural strength of activated carbon-bamboo stem, activated carbon-oil palm, and activated carbon-coconut shell reinforced epoxy nano composites showed almost same value in case of 5 % potassium hydroxide activated carbon. Flexural strength of potassium hydroxide activated carbon-based epoxy nano composites was higher than phosphoric acid activated carbon. The flexural toughness of both the potassium hydroxide and phosphoric acid activated carbon reinforced composites range between 0.79 - 0.92 J. It attributed that developed activated carbon filled epoxy nano composites can be used in different applications. (author)

Solidification and performance of cement doped with phenol

International Nuclear Information System (INIS)

Vipulanandan, C.; Krishnan, S.

1991-01-01

Treating mixed hazardous wastes using the solidification/stabilization technology is becoming a critical element in waste management planning. The effect of phenol, a primary constituent in many hazardous wastes, on the setting and solidification process of Type I Portland cement was evaluated. The leachability of phenol from solidified cement matrix (TCLP test) and changes in mechanical properties were studied after curing times up to 28 days. The changes in cement hydration products due to phenol were studied using the X-ray diffraction (XRD) powder technique. Results show that phenol interferes with initial cement hydration by reducing the formation of calcium hydroxide and also reduces the compressive strength of cement. A simple model has been proposed to quantify the phenol leached from the cement matrix during the leachate test

Atomistic Modeling of Thermal Conductivity of Epoxy Nanotube Composites

Science.gov (United States)

Fasanella, Nicholas A.; Sundararaghavan, Veera

2016-05-01

The Green-Kubo method was used to investigate the thermal conductivity as a function of temperature for epoxy/single wall carbon nanotube (SWNT) nanocomposites. An epoxy network of DGEBA-DDS was built using the `dendrimer' growth approach, and conductivity was computed by taking into account long-range Coulombic forces via a k-space approach. Thermal conductivity was calculated in the direction perpendicular to, and along the SWNT axis for functionalized and pristine SWNT/epoxy nanocomposites. Inefficient phonon transport at the ends of nanotubes is an important factor in the thermal conductivity of the nanocomposites, and for this reason discontinuous nanotubes were modeled in addition to long nanotubes. The thermal conductivity of the long, pristine SWNT/epoxy system is equivalent to that of an isolated SWNT along its axis, but there was a 27% reduction perpendicular to the nanotube axis. The functionalized, long SWNT/epoxy system had a very large increase in thermal conductivity along the nanotube axis (~700%), as well as the directions perpendicular to the nanotube (64%). The discontinuous nanotubes displayed an increased thermal conductivity along the SWNT axis compared to neat epoxy (103-115% for the pristine SWNT/epoxy, and 91-103% for functionalized SWNT/epoxy system). The functionalized system also showed a 42% improvement perpendicular to the nanotube, while the pristine SWNT/epoxy system had no improvement over epoxy. The thermal conductivity tensor is averaged over all possible orientations to see the effects of randomly orientated nanotubes, and allow for experimental comparison. Excellent agreement is seen for the discontinuous, pristine SWNT/epoxy nanocomposite. These simulations demonstrate there exists a threshold of the SWNT length where the best improvement for a composite system with randomly oriented nanotubes would transition from pristine SWNTs to functionalized SWNTs.

Halloysite reinforced epoxy composites with improved mechanical properties

Directory of Open Access Journals (Sweden)

Saif Muhammad Jawwad

2016-03-01

Full Text Available Halloysite nanotubes (HNTs reinforced epoxy composites with improved mechanical properties were prepared. The prepared HNTs reinforced epoxy composites demonstrated improved mechanical properties especially the fracture toughness and flexural strength. The flexural modulus of nanocomposite with 6% mHNTs loading was 11.8% higher than that of neat epoxy resin. In addition, the nanocomposites showed improved dimensional stability. The prepared halloysite reinforced epoxy composites were characterized by thermal gravimetric analysis (TGA. The improved properties are attributed to the unique characteristics of HNTs, uniform dispersion of reinforcement and interfacial coupling.

Shape memory polymers from benzoxazine-modified epoxy

International Nuclear Information System (INIS)

Rimdusit, Sarawut; Lohwerathama, Montha; Dueramae, Isala; Hemvichian, Kasinee; Kasemsiri, Pornnapa

2013-01-01

Novel shape memory polymers (SMPs) were prepared from benzoxazine-modified epoxy resin. Specimens consisting of aromatic epoxy (E), aliphatic epoxy (N), Jeffamine D230 (D) and BA-a benzoxazine monomer (B) were evaluated. The mole ratio of D/B was used as a mixed curing agent for an epoxy system with a fixed E/N. The effects of BA-a content on the thermal, mechanical and shape memory properties of epoxy-based shape memory polymers (SMPs) were investigated by differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), flexural test and shape recovery test. The results revealed that the obtained SMPs exhibited a higher flexural strength and flexural modulus than those of the unmodified epoxy-based SMP at room temperature and at 20 ° C above glass transition temperature (T g ). The presence of 1 mol BA-a as a curing agent provided the specimen with the highest T g , i.e. about 72 ° C higher than that of epoxy-based SMP cured by Jeffamine D230. All SMP samples needed only a few minutes to fully recover to their original shape. The samples exhibited high shape fixity (98–99%) and shape recovery ratio (90–100%). In addition, the recovery stress values increased with increasing BA-a mole ratio from 20 to 38 kPa, when BA-a up to 1 mol ratio was added. All of the SMP samples exhibited only minimum change in their flexural strength at the end of a 100 recovery cycles test. (paper)

Effect of Sonification Time on Synthesisi and Corrosion Resistance of Epoxy-Clay Nanocomposite

Directory of Open Access Journals (Sweden)

Niloufar Bahrami Panah

2016-09-01

Full Text Available In recent years many research works have been carried out on anti-corrosive nanocomposites coatings containing mineral reinforcements. The most important criteria in these attempts are polymerization method and the type of matrix and reinforcement of nanocomposites. In this regard, the physical and mechanical properties of the polymers in which a small amount of filler is used can be improved. In this research, an epoxy-clay nanocomposite was synthesized by in-situ polymerization method using a resin matrix based on bisphenol-A type epoxy and montmorillonite clay (Closite 15A. The treatment was used at different ultrasonic stirring times to disperse 1-4 weight percentages of clay particles into the matrix. The structure of synthesized epoxy-clay nanocomposite was studied by scanning electron microscopy and X-ray diffraction techniques. The average size of clay particles was determined by X-ray diffraction measurement. Then, anti-corrosion properties of epoxy-clay coatings, prepared under different ultrasonic durations and applied on carbon steel panels, were investigated by Tafel and electrochemical impedance spectroscopy techniques. For this purpose, the carbon steel panels coated with these coatings were immersed in 3.5% sodium chloride solution and tested at different immersion times. The results indicated that a nanocomposite containing 1% clay, synthesized, stirred 60 min ultrasonically, produced smaller particle size, lower corrosion current density and higher coating corrosion resistance than the other composite formulations. This nanocomposite provided superior protection against corrosion in sodium chloride solution.

Characterization and Curing Kinetics of Epoxy/Silica Nano-Hybrids

Science.gov (United States)

Yang, Cheng-Fu; Wang, Li-Fen; Wu, Song-Mao; Su, Chean-Cheng

2015-01-01

The sol-gel technique was used to prepare epoxy/silica nano-hybrids. The thermal characteristics, curing kinetics and structure of epoxy/silica nano-hybrids were studied using differential scanning calorimetry (DSC), 29Si nuclear magnetic resonance (NMR) and transmission electron microscopy (TEM). To improve the compatibility between the organic and inorganic phases, a coupling agent was used to modify the diglycidyl ether of bisphenol A (DGEBA) epoxy. The sol-gel technique enables the silica to be successfully incorporated into the network of the hybrids, increasing the thermal stability and improving the mechanical properties of the prepared epoxy/silica nano-hybrids. An autocatalytic mechanism of the epoxy/SiO2 nanocomposites was observed. The low reaction rate of epoxy in the nanocomposites is caused by the steric hindrance in the network of hybrids that arises from the consuming of epoxide group in the network of hybrids by the silica. In the nanocomposites, the nano-scale silica particles had an average size of approximately 35 nm, and the particles were well dispersed in the epoxy matrix, according to the TEM images. PMID:28793616

High-performance fiber/epoxy composite pressure vessels

Science.gov (United States)

Chiao, T. T.; Hamstad, M. A.; Jessop, E. S.; Toland, R. H.

1978-01-01

Activities described include: (1) determining the applicability of an ultrahigh-strength graphite fiber to composite pressure vessels; (2) defining the fatigue performance of thin-titanium-lined, high-strength graphite/epoxy pressure vessel; (3) selecting epoxy resin systems suitable for filament winding; (4) studying the fatigue life potential of Kevlar 49/epoxy pressure vessels; and (5) developing polymer liners for composite pressure vessels. Kevlar 49/epoxy and graphite fiber/epoxy pressure vessels, 10.2 cm in diameter, some with aluminum liners and some with alternation layers of rubber and polymer were fabricated. To determine liner performance, vessels were subjected to gas permeation tests, fatigue cycling, and burst tests, measuring composite performance, fatigue life, and leak rates. Both the metal and the rubber/polymer liner performed well. Proportionately larger pressure vessels (20.3 and 38 cm in diameter) were made and subjected to the same tests. In these larger vessels, line leakage problems with both liners developed the causes of the leaks were identified and some solutions to such liner problems are recommended.

Pollen types and levels of total phenolic compounds in propolis produced by Apis mellifera L. (Apidae in an area of the Semiarid Region of Bahia, Brazil

Directory of Open Access Journals (Sweden)

VANESSA R. MATOS

2014-03-01

Full Text Available Twenty-two propolis samples produced by Apis mellifera L. in an area of the Semiarid region the the State of Bahia (Agreste of Alagoinhas, Brazil, were palynologically analyzed and quantified regarding their levels of total phenolic compounds. These samples were processed using the acetolysis technique with the changes suggested for use with propolis. We found 59 pollen types belonging to 19 families and 36 genera. The family Fabaceae was the most representative in this study with nine pollen types, followed by the family Asteraceae with seven types. The types Mikania and Mimosa pudica occurred in all samples analyzed. The types Mimosa pudica and Eucalyptus had frequency of occurrence above 50% in at least one sample. The highest similarity index (c. 72% occurred between the samples ER1 and ER2, belonging to the municipality of Entre Rios. Samples from the municipality of Inhambupe displayed the highest (36.78±1.52 mg/g EqAG and lowest (7.68 ± 2.58 mg/g EqAG levels of total phenolic compounds. Through the Spearman Correlation Coefficient we noticed that there was a negative linear correlation between the types Mimosa pudica (rs = -0.0419 and Eucalyptus (rs = -0.7090 with the profile of the levels of total phenolic compounds of the samples.

Viscoelastic properties of graphene-based epoxy resins

Science.gov (United States)

Nobile, Maria Rossella; Fierro, Annalisa; Rosolia, Salvatore; Raimondo, Marialuigia; Lafdi, Khalid; Guadagno, Liberata

2015-12-01

In this paper the viscoelastic properties of an epoxy resin filled with graphene-based nanoparticles have been investigated in the liquid state, before curing, by means of a rotational rheometer equipped with a parallel plate geometry. Exfoliated graphite was prepared using traditional acid intercalation followed by a sudden treatment at high temperature (900°C). The percentage of exfoliated graphite was found to be 56%. The epoxy matrix was prepared by mixing a tetrafunctional precursor with a reactive diluent which produces a significant decrease in the viscosity of the epoxy precursor so that the dispersion step of nanofillers in the matrix can easily occur. The hardener agent, the 4,4-diaminodiphenyl sulfone (DDS), was added at a stoichiometric concentration with respect to all the epoxy rings. The inclusion of the partially exfoliated graphite (pEG) in the formulated epoxy mixture significantly modifies the rheological behaviour of the mixture itself. The epoxy mixture, indeed, shows a Newtonian behaviour while, at 3 wt % pEG content, the complex viscosity of the nanocomposite clearly shows a shear thinning behaviour with η* values much higher at the lower frequencies. The increase in complex viscosity with the increasing of the partially exfoliated graphite content was mostly caused by a dramatic increase in the storage modulus. All the graphene-based epoxy mixtures were cured by a two-stage curing cycles: a first isothermal stage was carried out at the lower temperature of 125°C for 1 hour while the second isothermal stage was performed at the higher temperature of 200°C for 3 hours. The mechanical properties of the cured nanocomposites show high values in the storage modulus and glass transition temperature.

Epoxy Nanocomposites Containing Zeolitic Imidazolate Framework-8.

Science.gov (United States)

Liu, Cong; Mullins, Michael; Hawkins, Spencer; Kotaki, Masaya; Sue, Hung-Jue

2018-01-10

Zeolitic imidazole framework-8 (ZIF-8) is utilized as a functional filler and a curing agent in the preparation of epoxy nanocomposites. The imidazole group on the surface of the ZIF-8 initiates epoxy curing, resulting in covalent bonding between the ZIF-8 crystals and epoxy matrix. A substantial reduction in dielectric constant and increase in tensile modulus were observed. The implication of the present study for utilization of metal-organic framework to improve physical and mechanical properties of polymeric matrixes is discussed.

Plasma Treated Multi-Walled Carbon Nanotubes (MWCNTs for Epoxy Nanocomposites

Directory of Open Access Journals (Sweden)

Jie Lian

2011-12-01

Full Text Available Plasma nanocoating of allylamine were deposited on the surfaces of multi-walled carbon nanotubes (MWCNTs to provide desirable functionalities and thus to tailor the surface characteristics of MWCNTs for improved dispersion and interfacial adhesion in epoxy matrices. Plasma nanocoated MWCNTs were characterized using scanning electron microscopy (SEM, high-resolution transmission electron microscopy (HR-TEM, surface contact angle, and pH change measurements. Mechanical testing results showed that epoxy reinforced with 1.0 wt % plasma coated MWCNTs increased the tensile strength by 54% as compared with the pure epoxy control, while epoxy reinforced with untreated MWCNTs have lower tensile strength than the pure epoxy control. Optical and electron microscopic images show enhanced dispersion of plasma coated MWCNTs in epoxy compared to untreated MWCNTs. Plasma nanocoatings from allylamine on MWCNTs could significantly enhance their dispersion and interfacial adhesion in epoxy matrices. Simulation results based on the shear-lag model derived from micromechanics also confirmed that plasma nanocoating on MWCNTs significantly improved the epoxy/fillers interface bonding and as a result the increased composite strength.

Evaluation of Moisture Damage and Stripping of Asphalt Concrete Prepared With New Additives of Polymer Modified Bitumen

Directory of Open Access Journals (Sweden)

Basim H. Al-Humeidawi

2016-03-01

Full Text Available The moisture induced damage and stripping are two of common reasons of premature failure of flexible pavement. The current research involved an extensive experimental investigation on two types of polymers (Novolac and PVA as modifiers in order to produce Polymer Modified Bitumen (PMB. Different ratios of both additives were investigated for rheological properties of binder and mechanical properties of Hot Mix Asphalt (HMA. The rheological properties of PMB were evaluated by penetration, softening point, ductility and thin film oven tests. The mechanical properties of HMA were assessed by Marshall Stability test, Retained Marshall Stability test, indirect tensile strength test, Tensile Strength Ratio (TSR, and striping test. The results of tests showed that the Novolac modifier improves the cohesion properties of binder and the adhesion of binder to aggregate. The PVA modifier mainly improves the adhesion of binder to aggregate with less degree of that of using Novolac. Both modifiers significantly improve moisture sensitivity and decrease the stripping of HMA. Also, the results showed that the addition of 2% of Novolac to binder to produce PMB represents the optimum option. The HMA with PMB Novolac 2% improves the Marshall Stability, Retained Marshall Stability, and TSR by 45%, 14% and 44% respectively. The very small amount of these additives compared with mix components and their reasonable price make them a superior and practical solution for premature failure of flexible pavement.

Conduction noise absorption by fiber-reinforced epoxy composites with carbon nanotubes

International Nuclear Information System (INIS)

Lee, Ok Hyoung; Kim, Sung-Soo; Lim, Yun-Soo

2011-01-01

Nearly all electronic equipment is susceptible to malfunction as a result of electromagnetic interference. In this study, glass fiber, and carbon fiber as a type reinforcement and epoxy as a matrix material were used to fabricate composite materials. In an attempt to increase the conduction noise absorption, carbon nanotubes were grown on the surface of glass fibers and carbon fibers. A microstrip line with characteristic impedance of 50 Ω in connection with network analyzer was used to measure the conduction noise absorption. In comparing a glass fiber/epoxy composite with a GF-CNT/Ep composite, it was demonstrated that the CNTs significantly influence the noise absorption property mainly due to increase in electric conductivity. In the carbon fiber composites, however, the effectiveness of CNTs on the degree of electric conductivity is negligible, resulting in a small change in reflection and transmission of an electromagnetic wave. - Research Highlights: → In this study, glass fiber and carbon fiber as a type reinforcement and epoxy as a matrix material were used to fabricate composite materials. In an attempt to increase the conduction noise absorption, carbon nanotubes (CNTs) were grown on the surface of glass fibers and carbon fibers. A microstrip line with characteristic impedance of 50 Ω in connection with network analyzer was used to measure the conduction noise absorption. → In comparing a glass fiber/epoxy composite with a GF-CNT/Ep composite, it was demonstrated that the CNTs significantly influence the noise absorption property mainly due to increase in electric conductivity. In the carbon fiber composites, however, the effectiveness of CNTs on the degree of electric conductivity is negligible, resulting in a small change in reflection and transmission of an electromagnetic wave.

Development of AlN/Epoxy Composites with Enhanced Thermal Conductivity

Science.gov (United States)

Xu, Yonggang; Yang, Chi; Li, Jun; Zhang, Hailong; Hu, Song; Wang, Shiwei

2017-01-01

AlN/epoxy composites with high thermal conductivity were successfully prepared by infiltrating epoxy into AlN porous ceramics which were fabricated by gelcasting of foaming method. The microstructure, mechanical, and thermal properties of the resulting composites were investigated. The compressive strengths of the AlN/epoxy composites were enhanced compared with the pure epoxy. The AlN/epoxy composites demonstrate much higher thermal conductivity, up to 19.0 W/(m·K), compared with those by the traditional particles filling method, because of continuous thermal channels formed by the walls and struts of AlN porous ceramics. This study demonstrates a potential route to manufacture epoxy-based composites with extremely high thermal conductivity. PMID:29258277

Development of AlN/Epoxy Composites with Enhanced Thermal Conductivity.

Science.gov (United States)

Xu, Yonggang; Yang, Chi; Li, Jun; Mao, Xiaojian; Zhang, Hailong; Hu, Song; Wang, Shiwei

2017-12-18

AlN/epoxy composites with high thermal conductivity were successfully prepared by infiltrating epoxy into AlN porous ceramics which were fabricated by gelcasting of foaming method. The microstructure, mechanical, and thermal properties of the resulting composites were investigated. The compressive strengths of the AlN/epoxy composites were enhanced compared with the pure epoxy. The AlN/epoxy composites demonstrate much higher thermal conductivity, up to 19.0 W/(m·K), compared with those by the traditional particles filling method, because of continuous thermal channels formed by the walls and struts of AlN porous ceramics. This study demonstrates a potential route to manufacture epoxy-based composites with extremely high thermal conductivity.

Phenolics composition and antidiabetic property of Brachystegia eurycoma seed flur in high-fat diet, low-dose streptozotocin-induced type 2 diabetes in rats

Directory of Open Access Journals (Sweden)

Emmanuel Anyachukwu Irondi

2015-06-01

Full Text Available Objective: To quantify some major pharmacologically important flavonoids and phenolic acids in Brachystegia eurycoma seed flour (BESF and evaluate its antidiabetic activity in type 2 diabetic rats. Method: Flavonoids and phenolic acids were quantified using a reverse-phase high pressure liquid chromatrography coupled with diode array detection. Type 2 diabetes was induced in rats using high-fat diet, low-dose streptozotocin (HFD/STZ model, by feeding the rats with HFD for 2 weeks followed by single dose administration of STZ (40 mg/kg body weight, intraperitoneally. The diabetic rats were later fed BESF-supplemented (10% and 20% diets, or administered with metformin (25 mg/kg b.w. for 21 days; the control rats were fed basal diet during this period. After the dietary regimen, the rats were sacrificed, and their blood, liver and pancreas samples were collected for biochemical assays. Results: The flavonoids (catechin, rutin, quercitrin, quercetin and kaempferol and phenolic acids (gallic acid, caffeic, chlorogenic and ellagic acid were abundant in BESF. BESFsupplemented diets (BESF-SD significantly (P 0.05 with metformin administration in some of the biomarkers. Conclusion: The flavonoids and phenolic acids in BESF may have acted synergistically to produce the observed antidiabetic effects. BESF could therefore be an effective and affordable dietary therapy for the management of T2DM; and an excellent source for drug discovery.

Corrosion performance of epoxy-coated reinforcement in aggressive environments

Science.gov (United States)

Vaca Cortes, Enrique

The objective of this research was to investigate the integrity and corrosion performance of epoxy-coated reinforcement in aggressive environments. A series of experimental studies were conducted: (a) hot water immersion and knife adhesion testing for assessment of coating adhesion; (b) materials and procedures for repairing coating damage; (c) degree of mechanical damage caused during concrete placement when using metal head and rubber head vibrators; (d) accelerated corrosion of coated bars embedded in macrocell and beam specimens placed in a corrosive environment for more than four years. The effects of coating condition and amount of damage, repaired vs. unrepaired damage, bar fabrication, and concrete cracking were studied. Regardless of coating condition, the performance of epoxy-coated bars was better than that of uncoated bars. Unlike black bars, coated bars did not exhibit deep pitting or substantial loss of cross section at crack locations. Damage to epoxy coating was the most significant factor affecting corrosion performance. Bars with coating in good condition, without any visible damage, performed best. The greater the size and frequency of damage, the more severe and extensive the amount of corrosion. The performance of bars that were fabricated or bent after coating was worse than that of coated straight bars. Mixing coated and uncoated bars in the same concrete member led to undesirable performance. Patching damaged coating reduced but did not prevent corrosion, particularly at bar ends. The most important factor in coating repair was the type and properties of the patching material. Surface preparation prior to coating had little effect. The absence of cracks in the concrete delayed, but did not prevent the onset of corrosion of coated bars. During consolidation of concrete, rubber head vibrators caused less damage to epoxy-coated reinforcement than did comparable metal heads. Hot water and adhesion tests were useful and practical for evaluating

Radiation processing of carbon fiber-acrylated epoxy composites

International Nuclear Information System (INIS)

Singh, A.; Saunders, C.B.

1992-01-01

Advanced composites, specifically carbon fiber reinforced epoxies, are being used for a variety of demanding structural applications, primarily because of their high strength-to-weight and stiffness-to-weight ratios, corrosion resistance, and damage tolerance characteristics. For these composites the key advantages of using electron beam (EB), rather than thermal curing, are curing at ambient temperature, reduced curing times for individual components, improved resin stability, fewer volatiles, and better control of the profile of energy absorption. Epoxy compounds do, however, have to be modified to make them EB curable. The electron beam penetration limit, a function of beam energy, product density, and the thickness of any container required, must also be examined when considering EB processing. Research is being conducted to develop EB-curable carbon fiber-acrylated epoxy composites. The tensile properties of these laminates are comparable to those of thermally cured epoxy laminates. Research is continuing to develop suitable resin formulations and coupling agents to optimize the mechanical properties of EB-cured carbon fiber laminates. In this chapter the EB curing of epoxies, processing considerations, and typical properties of EB-cured carbon fiber-acrylated epoxy laminates are discussed. (orig.)

Thermal-mechanical properties of a graphitic-nanofibers reinforced epoxy.

Science.gov (United States)

Salehi-Khojin, Amin; Jana, Soumen; Zhong, Wei-Hong

2007-03-01

We previously developed a series of reactive graphitic nanofibers (r-GNFs) reinforced epoxy (nano-epoxy) as composite matrices, which have shown good wetting and adhesion properties with continuous fiber. In this work, the thermal-mechanical properties of the nano-epoxy system containing EponTM Resin 828 and Epi-cure Curing Agent W were characterized. Results from three-point bending tests showed that the flexural strength and flexural modulus of this system with 0.30 wt% of reactive nanofibers were increased by 16%, and 21% respectively, over pure epoxy. Fracture toughness increased by ca. 40% for specimens with 0.50 wt% of r-GNFs. By dynamic mechanical analysis (DMA) test, specimens with 0.30 wt% of r-GNFs showed a significant increase in storage modulus E' (by ca. 122%) and loss modulus E" (by ca. 111%) with respect to that of pure epoxy. Also thermo-dilatometry analysis (TDA) was used to measure dimensional change of specimens as a function of temperature, and then, coefficients of thermal expansion (CTE) before and after glass transition temperature (Tg) were obtained. Results implied that nano-epoxy materials had good dimensional stability and reduced CTE values when compared to those of pure epoxy.

Mechanical properties of functionalised CNT filled kenaf reinforced epoxy composites

Science.gov (United States)

Sapiai, Napisah; Jumahat, Aidah; Mahmud, Jamaluddin

2018-04-01

This paper aims to study the effect of functionalised carbon nanotubes (CNT) on mechanical properties of kenaf fibre reinforced polymer composites. The CNT was functionalised using acid mixtures of H2SO4:HNO3 and 3-Aminopropyl Triethoxysilane before it was incorporated into epoxy resin. Three different types of CNT were used, i.e. pristine (PCNT), acid-treated (ACNT) and acid-silane treated (SCNT), to fabricate kenaf composite. Three different filler contents were mixed in each composite system, i.e. 0.5, 0.75 and 1.0 wt%. The functionalised CNT was characterized using x-ray Diffraction (XRD), Fourier Transform Infrared (FTIR) and Transmission Electron Microscopy (TEM). Tensile, flexural and Izod impact tests were conducted in order to evaluate the effect of CNT contents and surface treatment of mechanical properties of kenaf composites. It was observed that the inclusion of 1 wt% acid-silane treated CNT improved the tensile, flexural and impact strengths of kenaf/epoxy composite by 43.30%, 21.10%, and 130%, respectively. Silane modification had been proven to be beneficial in enhancing the dispersibility and reducing agglomeration of CNT in the epoxy matrix.

Performance of epoxy-nanocomposite under corrosive environment

Directory of Open Access Journals (Sweden)

2007-06-01

Full Text Available Nanocomposite materials consisting of polymeric matrix materials and natural or synthetic layered minerals like clay are currently an expanding field of study because these new materials often exhibit a wide range of improved properties over their unmodified starting polymers. Epoxy/organoclay nanocomposites have been prepared by intercalating epoxy into the organoclay via direct mixing process. The clay exfoliation was monitored by X-ray diffraction (XRD and transmission electron microscopy (TEM. Water diffusion and sulfuric acid corrosion resistance of epoxy-based nanocomposites were evaluated. Diffusion was studied through epoxy samples containing up to 6 phr (parts per hundred resin of an organically treated montmorillonite. The diffusion of the environmental solution was measured by noting the increase in weight of the samples as a function of immersion time in these solutions at 80°C. The effect of the degree of exfoliation of the organoclay on water barrier and corrosion resistance was specifically studied. The data have been compared to those obtained from the neat epoxy resin to evaluate the diffusion properties of the nanocomposites. The flexural strength of the epoxy/organoclay nanocomposites samples made was examined to compare their mechanical performance under corrosive conditions as a function of immersion time and temperature. It was found, that the organoclay was mainly intercalated with some exfoliation and that addition of the organoclay yields better flexural strength retention under immersion into sulfuric acid.

Effect of functionalization of graphene nanoplatelets on the mechanical response of graphene/epoxy composites

International Nuclear Information System (INIS)

Ahmadi-Moghadam, B.; Sharafimasooleh, M.; Shadlou, S.; Taheri, F.

2015-01-01

Highlights: • A new functionalization strategy for GNPs, using trimethoxysilane is introduced. • Bond quality between GNP and silane agent is verified by the Raman spect. and TGA. • The functionaliz’n effects on mechanical properties of GNP/epoxy were investigated. • The functionaliz’n effects on the fracture mechanisms of GNP/epoxy investigated. • GNP dispersion quality is also evaluated using SEM micrographs and XRD. - Abstract: This study introduces a new strategy for functionalizing graphene nanoplatelets (GNPs) by bonding a silane agent to its structure. In order to evaluate the efficacy of the proposed method, epoxy resin specimens reinforced with silane modified GNPs (G-Si) are prepared at different weight contents of nanoparticles along with three other types of GNPs (unmodified GNP, graphene oxide GNP [GO], and amino functionalized GNP [G-NH 2 ]). The nanocomposites’ mechanical properties, such as the elastic modulus, ultimate strength, modulus of toughness and fracture toughness are evaluated and compared for different types of functionalization. Raman spectroscopy, thermo-gravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FTIR) are employed to characterize the chemical and structural changes of the functionalized GNPs. The results show that nanocomposites containing G-Si and G-NH 2 provide the best results for most of the mentioned properties. The functionalization of GNPs gives the most promising results for fracture toughness of epoxy, showing an 82% increase, and scanning electron microscopy (SEM) micrographs and XRD analysis reveal that an improved dispersion status is obtained by GNP functionalization

In-situ Elevated Temperature Mechanical Performance of MWCNT/epoxy Nanocomposite

Directory of Open Access Journals (Sweden)

Bhanu Pratap Singh

2017-03-01

Full Text Available The present investigation has been focused on the effects of multi-walled carbon nanotube (MWCNT addition on the mechanical performance of epoxy under different in-service elevated temperature environments. Room temperature flexural test results revealed that addition of 0.1 wt. % MWCNT into epoxy resin resulted in modulus and strength enhancement of 21 % and 9 % respectively. With increase in service temperature, significant decrement in both modulus and strength was noticed for both materials (neat epoxy and MWCNT/epoxy nanocomposite, but the rate of degradation was found to be quite drastic for the nanocomposite. At 90 °C temperature, the CNT/epoxy nanocomposite exhibited inferior modulus and strength, which are 41 % and 59 % lower than neat epoxy respectively. The variation trend in elastic modulus with temperature obtained from both flexural testing and DMA for both these materials was also analyzed. It was found that addition of 0.1 % CNT in the epoxy reduced the glass transition temperature by about 16°C.

Effect of aluminium particles on mechanical and morphological properties of epoxy nanocomposites

Directory of Open Access Journals (Sweden)

Bello Sefiu A.

2017-01-01

Full Text Available Bumper is a front or rear part of automobiles. It is designed and shaped to be impact absorbing and protecting automobiles from damage in low impact collisions. Initially, they were made from heavy steels, increasing the weight of automobiles and fuel consumption. Also, high impacts of steel bumpers on pedestrians during accidental collision cause fatalities and or disabilities. An effort to enhance fuel efficiency, safety, freedom of design and shape detailing, heavy alloys for automobile applications are now being replaced with polymeric composites. Aluminium micro particles and nanoparticles were prepared from aluminium cans through sand casting, lathe machine spinning, and ball milling techniques. Both types of aluminium particles were incorporated into a mixture of diglycidyl ether of bisphenol A (DGEBA, epoxy resin cured with amine base hardener (ABH. Phases of the epoxy polymer and composites were identified using Xray Diffraction (XRD. Spatial arrangement of the phases within the matrix and their elemental composition were examined using Scanning Electron Microscope with attached energy dispersive X-ray spectroscopy (SEM/EDX. Tensile, impact and micro hardness tests were conducted on the prepared epoxy/aluminium composites. Results of the XRD showed the presence of aluminium compounds/phases due to chemical reactions between aluminium particles and DGEBA/ABH system. SEM confirmed a homogeneous distribution of the phases within the epoxy matrix, and that there is a strong adhesion between the epoxy matrix and aluminium particles. Correlation between the mechanical properties of the prepared nanocomposite and the procured bumper materials exhibited a fair suitability of the prepared nanocomposites for automobile applications.

METHODS OF REDUCTION OF FREE PHENOL CONTENT IN PHENOLIC FOAM

Directory of Open Access Journals (Sweden)

Bruyako Mikhail Gerasimovich

2012-12-01

method aimed at reduction of toxicity of phenolic foams consists in the introduction of a composite mixture of chelate compounds. Raw materials applied in the production of phenolic foams include polymers FRB-1A and VAG-3. The aforementioned materials are used to produce foams FRP-1. Introduction of 1% aluminum fluoride leads to the 40% reduction of the free phenol content in the foam. Introduction of crystalline zinc chloride accelerates the foaming and curing of phenolic foams. The technology that contemplates the introduction of zeolites into the mixture includes pre-mixing with FRB -1A and subsequent mixing with VAG-3; thereafter, the composition is poured into the form, in which the process of foaming is initiated. The content of free phenol was identified using the method of UV spectroscopy. The objective of the research was to develop methods of reduction of the free phenol content in the phenolic foam.

Accelerated thermal aging of rubber modified epoxy encapsulants

International Nuclear Information System (INIS)

Sayre, J.A.

1979-01-01

A program is outlined to enable prediction of physical properties of rubber modified epoxy encapsulants over the life time of the extended life neutron generators. Preliminary results show that the chief aging phenomenon occurring is increased crosslink density of the epoxy matrix. No changes in the rubber phase have been detected. The effect of increased epoxy crosslink density has been higher volume resistivity at 66 0 C, increased tensile strength, and decreased ultimate elongation

Phenolic Compounds Analysis of Root, Stalk, and Leaves of Nettle

OpenAIRE

Otles, Semih; Yalcin, Buket

2012-01-01

Types of nettles (Urtica dioica) were collected from different regions to analyze phenolic compounds in this research. Nettles are specially grown in the coastal part. According to this kind of properties, nettle samples were collected from coastal part of (Mediterranean, Aegean, Black sea, and Marmara) Turkey. Phenolic profile, total phenol compounds, and antioxidant activities of nettle samples were analyzed. Nettles were separated to the part of root, stalk, and leaves. Then, these parts ...

Growth and phenolic compounds of Lactuca sativa L. grown in a closed-type plant production system with UV-A, -B, or -C lamp.

Science.gov (United States)

Lee, Min-Jeong; Son, Jung Eek; Oh, Myung-Min

2014-01-30

The production of high-quality crops based on phytochemicals is a strategy for accelerating the practical use of plant factories. Previous studies have demonstrated that ultraviolet (UV) light is effective in improving phytochemical production. This study aimed to determine the effect of various UV wavelengths on growth and phenolic compound accumulation in lettuce (Lactuca sativa L.) grown in a closed-type plant production system. Seven days, 1 day and 0.25 day were determined as the upper limit of the irradiation periods for UV-A, -B, and -C, respectively, in the lettuce based on physiological disorders and the fluorescence parameter F(v)/F(m). Continuous UV-A treatment significantly induced the accumulation of phenolic compounds and antioxidants until 4 days of treatment without growth inhibition, consistent with an increase in phenylalanine ammonia lyase (PAL) gene expression and PAL activity. Repeated or gradual UV-B exposure yielded approximately 1.4-3.6 times more total phenolics and antioxidants, respectively, than the controls did 2 days after the treatments, although both treatments inhibited lettuce growth. Repeated UV-C exposure increased phenolics but severely inhibited the growth of lettuce plants. Our data suggest that UV irradiation can improve the accumulation of phenolic compounds with antioxidant properties in lettuce cultivated in plant factories. © 2013 Society of Chemical Industry.

Thermoset epoxy polymers from renewable resources

Science.gov (United States)

East, Anthony [Madison, NJ; Jaffe, Michael [Maplewood, NJ; Zhang, Yi [Harrison, NJ; Catalani, Luiz H [Carapicuiba, BR

2009-11-17

Novel thermoset epoxy polymers using the bisglycidyl ethers of anhydrosugars, such as isosorbide, isomannide, and isoidide, are disclosed. The bisglycidyl ethers are useful as substitutes for bisphenol A in the manufacture of thermoset epoxy ethers. The anhydrosugars are derived from renewable sources and the bisglycidyl ethers are not xenoestrogenic and the thermoset curing agents are likewise derived form renewable resources.

Understanding the thermal, mechanical and electrical properties of epoxy nanocomposites

International Nuclear Information System (INIS)

Sarathi, R.; Sahu, R.K.; Rajeshkumar, P.

2007-01-01

In the present work, the electrical, mechanical and thermal properties of epoxy nanocomposite materials were studied. The electrical insulation characteristics were analyzed through short time breakdown voltage test, accelerated electrical ageing test, and by tracking test. The breakdown voltage increases with increase in nano-clay content up to 5 wt%, under AC and DC voltages. The volume resistivity, permittivity and tan(δ) of the epoxy nanocomposites were measured. The Weibull studies indicate that addition of nanoclay upto 5 wt% enhances the characteristic life of epoxy nanocomposite insulation material. The tracking test results indicate that the tracking time is high with epoxy nanocomposites as compared to pure epoxy. Ageing studies were carried out to understand the surface characteristic variation through contact angle measurement. The hydrophobicity of the insulating material was analysed through contact angle measurement. The diffusion coefficients of the material with different percentage of clay in epoxy nanocomposites were calculated. The exfoliation characteristics in epoxy nanocomposites were analyzed through wide angle X-ray diffraction (WAXD) studies. The thermal behaviour of the epoxy nanocomposites was analyzed by carrying out thermo gravimetric-differential thermal analysis (TG-DTA) studies. Heat deflection temperature of the material was measured to understand the stability of the material for intermittent temperature variation. The dynamic mechanical analysis (DMA) results indicated that storage modulus of the material increases with small amount of clay in epoxy resin. The activation energy of the material was calculated from the DMA results

Modeling and mechanical performance of carbon nanotube/epoxy resin composites

International Nuclear Information System (INIS)

Srivastava, Vijay Kumar

2012-01-01

Highlights: ► The MWCNT fillers are uniformly dispersed in the epoxy resin, which improved the mechanical properties of epoxy resin. ► Modified Halpin–Tsai model is useful to calculate the Young’s modulus of MWCNT/epoxy resin composite. ► The experimental moduli are within the variation of 27% with the theoretical values. -- Abstract: The effect of multi-walled carbon nanotube (MWCNT) addition on mechanical properties of epoxy resin was investigated to obtain the tensile strength, compressive strength and Young’s modulus from load versus displacement graphs. The result shows that the tensile strength, compressive strength and Young’s modulus of epoxy resin were increased with the addition of MWCNT fillers. The significant improvements in tensile strength, compressive strength and Young’s modulus were obtained due to the excellent dispersion of MWCNT fillers in the epoxy resin. The dispersion of MWCNT fillers in epoxy resin was observed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analysis. Also, Halpin–Tsai model was modified by considering the average diameter of internal/external of multi-walled nanotube and orientation factor (α) to calculate the Young’s modulus of multi-walled carbon nanotubes (MWCNTs)/epoxy resin composite. There was a good correlation between the experimentally obtained Young’s modulus and modified Halpin–Tsai model.

The failure mode of natural silk epoxy triggered composite tubes

International Nuclear Information System (INIS)

Eshkour, R A; Ariffin, A K; Zulkifli, R; Sulong, A B; Azhari, C H

2012-01-01

In this study the quasi static compression test over natural silk epoxy triggered composite tubes has been carried out, the natural silk epoxy composite tubes consist of 24 layer of woven natural silk as reinforcement and thermoset epoxy resin as matrix which both of them i e natural silk and epoxy have excellent mechanical properties More over the natural silk have better moisture resistance in comparison with other natural reinforcements, the length of tubes are 50, 80 and 120 mm The natural silk epoxy composite tubes are associated with an external trigger which includes 4 steel pieces welded on downside flat plate fixture The hand lay up fabrication method has been used to make the natural silk epoxy composite tubes Instron universal testing machine with 250 KN load capacity has been employed to accomplish this investigation The failure modes of natural silk epoxy triggered composite tubes has been investigated by representative photographs which has been taken by a high resolution camera(12 2 Mp) during the quasi static compression test, from the photographs is observed the failure modes is progressive local buckling

Fracture behaviour of a self-healing microcapsule-loaded epoxy system

Directory of Open Access Journals (Sweden)

2011-03-01

Full Text Available The effect of temperature on the fracture behaviour of a microcapsule-loaded epoxy matrix was investigated. Microencapsulated epoxy and mercaptan-derivative healing agents were incorporated into an epoxy matrix to produce a polymer composite capable of self-healing. Maximum fracture loads were measured using the double-torsion method. Thermal aging at 55 and 110°C for 17 hours [hrs] was applied to heal the pre-cracked samples. The addition of microcapsules appeared to increase significantly the load carrying capacity of the epoxy after healing. Once healed, the composites achieved as much as 93–171% of its virgin maximum fracture load at 18, 55 and 110°C. The fracture behavior of the microcapsule- loaded epoxy matrix was influenced by the healing temperature. The high self-healing efficiency may be attributed to the result of the subsurface micro-crack pinning or deviation, and to a stronger microencapsulated epoxy and mercaptanderivative binder than that of the bulk epoxy. The results show that the healing temperature has a significant effect on recovery of load transferring capability after fracture.

Epoxy/α-alumina nanocomposite with high electrical insulation performance

Directory of Open Access Journals (Sweden)

Yun Chen

2017-10-01

Full Text Available An experimental study was conducted to improve the electrical insulation of epoxy resin. The effects of boehmite, γ-alumina and α-alumina nanoparticles on the volume resistivity, dielectric strength and glass transition temperature of epoxy nanocomposites were investigated. The results showed that α-alumina nanoparticles displayed obvious advantages in enhancing electrical insulation performance of epoxy nanocomposites, compared to boehmite and γ-alumina nanoparticles. The direct current volume resistivity and breakdown strength of epoxy nanocomposite with 2.0 wt% α-alumina nanoparticles was improved to 2.2 × 1018 Ω cm and 76.1 kV mm−1 respectively. And these improved values of electrical insulation properties are much higher than these of epoxy nanocomposites reported in previous studies. The main reason of these improvements may be that the epoxy/α-alumina interaction zone was enhanced by crosslink. Keywords: Nanocomposite, Epoxy resin, Insulation, α-alumina

Selective Clay Placement Within a Silicate-Clay Epoxy Blend Nanocomposite

Science.gov (United States)

Miller, Sandi G (Inventor)

2013-01-01

A clay-epoxy nanocomposite may be prepared by dispersing a layered clay in an alkoxy epoxy, such as a polypropylene oxide based epoxide before combining the mixture with an aromatic epoxy to improve the nanocomposite's thermal and mechanical properties.

Experimental design applied optimization of a state in epoxy clay dispersion; Planejamento de experimentos aplicado a otimizacao do estado de dispersao de argilas em epoxi

Energy Technology Data Exchange (ETDEWEB)

Paz, Juliana D' Avila; Bertholdi, Jonas; Folgueras, Marilena Valadares; Pezin, Sergio Henrique; Coelho, Luiz Antonio Ferreira, E-mail: julianadpaz@yahoo.com.b [Universidade do Estado de Santa Catarina (UDESC), Joinville, SC (Brazil). Centro de Ciencias Tecnologicas

2010-07-01

This paper presents some analysis showed that the exfoliation / intercalation of a montmorillonite clay in epoxy resin such as viscosity, X-ray diffraction (XRD), scanning electron microscopy (SEM) and thermogravimetry (TG). Increasing the viscosity of epoxy resin diglycidyl ether bisphenol A with the addition of clay associated with the sonification system at the time of dispersion is a good indication of exfoliation. The X-ray diffraction already cured composite shows a decrease of crystallinity of clay and EDS microanalysis of SEM, non-uniform dispersion of clay in epoxy resin. Thermal analysis TG composite clay / epoxy shows an increase in thermal stability relative to pure epoxy. (author)

Bio-Based Aromatic Epoxy Monomers for Thermoset Materials

Directory of Open Access Journals (Sweden)

Feifei Ng

2017-01-01

Full Text Available The synthesis of polymers from renewable resources is a burning issue that is actively investigated. Polyepoxide networks constitute a major class of thermosetting polymers and are extensively used as coatings, electronic materials, adhesives. Owing to their outstanding mechanical and electrical properties, chemical resistance, adhesion, and minimal shrinkage after curing, they are used in structural applications as well. Most of these thermosets are industrially manufactured from bisphenol A (BPA, a substance that was initially synthesized as a chemical estrogen. The awareness on BPA toxicity combined with the limited availability and volatile cost of fossil resources and the non-recyclability of thermosets implies necessary changes in the field of epoxy networks. Thus, substitution of BPA has witnessed an increasing number of studies both from the academic and industrial sides. This review proposes to give an overview of the reported aromatic multifunctional epoxide building blocks synthesized from biomass or from molecules that could be obtained from transformed biomass. After a reminder of the main glycidylation routes and mechanisms and the recent knowledge on BPA toxicity and legal issues, this review will provide a brief description of the main natural sources of aromatic molecules. The different epoxy prepolymers will then be organized from simple, mono-aromatic di-epoxy, to mono-aromatic poly-epoxy, to di-aromatic di-epoxy compounds, and finally to derivatives possessing numerous aromatic rings and epoxy groups.

Epoxy composite dusts with and without carbon nanotubes cause similar pulmonary responses, but differences in liver histology in mice following pulmonary deposition

DEFF Research Database (Denmark)

Saber, Anne Thoustrup; Mortensen, Alicja; Szarek, Jozef

2016-01-01

Background: The toxicity of dusts from mechanical abrasion of multi-walled carbon nanotube (CNT) epoxy nanocomposites is unknown. We compared the toxic effects of dusts generated by sanding of epoxy composites with and without CNT. The used CNT type was included for comparison.Methods: Mice recei...

Magnetism in graphene oxide induced by epoxy groups

Energy Technology Data Exchange (ETDEWEB)

Lee, Dongwook, E-mail: dongwookleedl324@gmail.com [Cavendish Laboratory, University of Cambridge, Cambridge CB3 0HE (United Kingdom); Division of Physics and Applied Physics, Nanyang Technological University, Singapore 637371 (Singapore); Seo, Jiwon, E-mail: jiwonseo@yonsei.ac.kr [Department of Physics and IPAP, Yonsei University, Seoul 120-749 (Korea, Republic of); School of Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon 440-746 (Korea, Republic of); Zhu, Xi; Su, Haibin [Division of Materials Science, School of Materials Science and Engineering, Nanyang Technological University, Singapore 639798 (Singapore); Cole, Jacqueline M. [Cavendish Laboratory, University of Cambridge, Cambridge CB3 0HE (United Kingdom); Argonne National Laboratory, 9700S Cass Avenue, Argonne, Illinois 60439 (United States)

2015-04-27

We have engineered magnetism in graphene oxide. Our approach transforms graphene into a magnetic insulator while maintaining graphene's structure. Fourier transform infrared spectroscopy spectra reveal that graphene oxide has various chemical groups (including epoxy, ketone, hydroxyl, and C-O groups) on its surface. Destroying the epoxy group with heat treatment or chemical treatment diminishes magnetism in the material. Local density approximation calculation results well reproduce the magnetic moments obtained from experiments, and these results indicate that the unpaired spin induced by the presence of epoxy groups is the origin of the magnetism. The calculation results also explain the magnetic properties, which are generated by the interaction between separated magnetic regions and domains. Our results demonstrate tunable magnetism in graphene oxide based on controlling the epoxy group with heat or chemical treatment.

The characteristics of epoxy resin cured by {gamma}-ray and E-beam

Energy Technology Data Exchange (ETDEWEB)

Nho, Y.C. E-mail: ycnho@kaeri.re.kr; Kang, Phil Hyun; Park, Jong Seok

2004-10-01

Epoxy resins are widely used as high-performance thermosetting resins for many industrial applications. In this study, the effect of an electron beam (E-beam) and {gamma}-ray irradiation on the curing of epoxy resins was investigated. Diglycidyl ether of bisphenol-A(DGEBA), diglycidyl ether of bisphenol-F(DGEBF) as epoxy resins, triarylsulfonium hexafluoroantimonate(TASHFA), and triarylsulfonium hexafluorophosphate(TASHFP) as initiators were used in this study. The chemical and mechanical characteristics of irradiated epoxy resins were compared after curing of E-beam and {gamma}-ray irradiation up to 50 kGy in N{sub 2} and air atmosphere. We ascertained the effect of oxygen on the radiation curing of epoxy resin. The thermal properties of cured epoxy were investigated using DMA and TGA. Mechanical properties such as flexural strength were measured. The chemical structures of cured epoxy were characterized by FT-NIR. The gel fraction and the stress at yield of epoxy resins irradiated by E-beam and {gamma}-ray in N{sub 2} atmosphere were also compared with those of epoxy resins irradiated by E-beam and {gamma}-ray in air.

Corrosion Protection of Steel by Epoxy-Organoclay Nanocomposite Coatings

OpenAIRE

Domna Merachtsaki; Panagiotis Xidas; Panagiotis Giannakoudakis; Konstantinos Triantafyllidis; Panagiotis Spathis

2017-01-01

The purpose of the present work was to study the corrosion behavior of steel coated with epoxy-(organo) clay nanocomposite films. The investigation was carried out using salt spray exposures, optical and scanning electron microscopy examination, open circuit potential, and electrochemical impedance measurements. The mechanical, thermomechanical, and barrier properties of pristine glassy epoxy polymer and epoxy-clay nanocomposites were examined. The degree of intercalation/exfoliation of clay ...

Effects of Nanofillers on the Thermo-Mechanical Properties and Chemical Resistivity of Epoxy Nanocomposites.

Science.gov (United States)

Atchudan, Raji; Pandurangan, Arumugam; Joo, Jin

2015-06-01

MWCNTs was synthesized using Ni-Cr/MgO by CVD method and were purified. The purified MWCNT was used as a filler material for the fabrication of epoxy nanocomposites. The epoxy nanocomposites with different amount (wt% = 0.5, 1.0, 2.0, 3.0, 4.0 and 5.0) of nanofillers (CB, SiO2 and MWCNTs) were prepared by casting method. The effects of nanofillers on the properties of neat epoxy matrix were well studied. The thermal properties of nanocomposites were studied using DSC, TGA and flame retardant, and also the mechanical properties such as tensile strength, flexural strength, compressive strength, impact strength, determination of hardness and chemical resistance were studied extensively. Based on the experiment's results, 2 wt% MWCNTs loading in epoxy resin showed the highest improvement in tensile strength, as compared to neat epoxy and to other epoxy systems (CB/epoxy, SiO2/epoxy). Improvements in tensile strength, glass transition temperature and decomposition temperature were observed by the addition of MWCNTs. The mechanical properties of the epoxy nanocomposites were improved due to the interfacial bonding between the MWCNTs and epoxy resin. Strain hardening behavior was higher for MWCNT/epoxy nanocomposites compared with CB/epoxy and SiO2/epoxy nanocomposites. The investigation of thermal and mechanical properties reveals that the incorporation of MWCNTs into the epoxy nanocomposites increases its thermal stability to a great extent. Discrete increase of glass transition temperature of nanocomposites is linearly dependent on MWCNTs content. Due to strong interfacial bonding between MWCNTs and epoxy resin, the chemical resistivity of MWCNT/epoxy nanocomposites is superior to neat epoxy and other epoxy systems.

Silane coupling agent for attaching fusion-bonded epoxy to steel.

Science.gov (United States)

Tchoquessi Diodjo, Madeleine R; Belec, Lénaïk; Aragon, Emmanuel; Joliff, Yoann; Lanarde, Lise; Perrin, François-Xavier

2013-07-24

We describe the possibility of using γ-aminopropyltriethoxysilane (γ-APS) to increase the durability of epoxy powder coating/steel joints. The curing temperature of epoxy powder coatings is frequently above 200 °C, which is seen so far as a major limitation for the use of the heat-sensitive aminosilane coupling agent. Despite this limitation, we demonstrate that aminosilane is a competitive alternative to traditional chromate conversion to enhance the durability of epoxy powder coatings/steel joints. Fourier-transform reflection-absorption infrared spectroscopy (FT-RAIRS), X-ray photoelectron spectroscopy (XPS), and atomic force microscopy (AFM) were used to identify the silane deposition conditions that influence the adhesion of epoxy powder coatings on steel. We show that AFM analysis provides highly sensitive measurements of mechanical property development and, as such, the degree of condensation of the silane. The joint durability in water at 60 °C was lower when the pH of the γ-APS solution was controlled at 4.6 using formic acid, rather than that at natural pH (10.6). At the curing temperature of 220 °C, oxidation of the carbon adjacent to the amine headgroup of γ-APS gives amide species by a pseudofirst-order kinetics. However, a few amino functionalities remain to react with oxirane groups of epoxy resin and, thus, strengthen the epoxy/silane interphase. The formation of ammonium formate in the acidic silane inhibits the reaction between silane and epoxy, which consequently decreases the epoxy/silane interphase cohesion. We find that the nanoroughness of silane deposits increases with the cure temperature which is beneficial to the wet stability of the epoxy/steel joints, due to increased mechanical interlocking.

Dienone-phenol Rearrangement of C-9 Oxygenated Decalinic Dienone and Analogs through B-Ring Cleavage

Institute of Scientific and Technical Information of China (English)

无

2003-01-01

Dehydrogenation of 9-hydroxy decalinic enones and analogs with DDQ resulted in a formal dienone-phenol type rearrangement via B-ring cleavage, while the corresponding dienone acetates underwent base-catalyzed formal dienone-phenol type rearrangement analogously.

Hydrophobic Modification of Layered Clays and Compatibility for Epoxy Nanocomposites

Directory of Open Access Journals (Sweden)

Jiang-Jen Lin

2010-04-01

Full Text Available Recent studies on the intercalation and exfoliation of layered clays with polymeric intercalating agents involving poly(oxypropylene-amines and the particular uses for epoxy nanocomposites are reviewed. For intercalation, counter-ionic exchange reactions of clays including cationic layered silicates and anionic Al-Mg layered double hydroxide (LDH with polymeric organic ions afforded organoclays led to spatial interlayer expansion from 12 to 92 Å (X-ray diffraction as well as hydrophobic property. The inorganic clays of layered structure could be modified by the poly(oxypropyleneamine-salts as the intercalating agents with molecular weights ranging from 230 to 5,000 g/mol. Furthermore, natural montmorillonite (MMT clay could be exfoliated into thin layer silicate platelets (ca. 1 nm thickness in one step by using polymeric types of exfoliating agents. Different lateral dimensions of MMT, synthetic fluorinated Mica and LDH clays had been cured into epoxy nanocomposites. The hydrophobic amine-salt modification resulting in high spacing of layered or exfoliation of individual clay platelets is the most important factor for gaining significant improvements of properties. In particular, these modified clays were reported to gain significant improvements such as reduced coefficient of thermal expansion (CTE, enhanced thermal stability, and hardness. The utilization of these layered clays for initiating the epoxy self-polymerization was also reported to have a unique compatibility between clay and organic resin matrix. However, the matrix domain lacks of covalently bonded crosslink and leads to the isolation of powder material. It is generally concluded that the hydrophobic expansion of the clay inter-gallery spacing is the crucial step for enhancing the compatibility and the ultimate preparation of the advanced epoxy materials.

Hydrophobic Modification of Layered Clays and Compatibility for Epoxy Nanocomposites

Science.gov (United States)

Lin, Jiang-Jen; Chan, Ying-Nan; Lan, Yi-Fen

2010-01-01

Recent studies on the intercalation and exfoliation of layered clays with polymeric intercalating agents involving poly(oxypropylene)-amines and the particular uses for epoxy nanocomposites are reviewed. For intercalation, counter-ionic exchange reactions of clays including cationic layered silicates and anionic Al-Mg layered double hydroxide (LDH) with polymeric organic ions afforded organoclays led to spatial interlayer expansion from 12 to 92 Å (X-ray diffraction) as well as hydrophobic property. The inorganic clays of layered structure could be modified by the poly(oxypropylene)amine-salts as the intercalating agents with molecular weights ranging from 230 to 5,000 g/mol. Furthermore, natural montmorillonite (MMT) clay could be exfoliated into thin layer silicate platelets (ca. 1 nm thickness) in one step by using polymeric types of exfoliating agents. Different lateral dimensions of MMT, synthetic fluorinated Mica and LDH clays had been cured into epoxy nanocomposites. The hydrophobic amine-salt modification resulting in high spacing of layered or exfoliation of individual clay platelets is the most important factor for gaining significant improvements of properties. In particular, these modified clays were reported to gain significant improvements such as reduced coefficient of thermal expansion (CTE), enhanced thermal stability, and hardness. The utilization of these layered clays for initiating the epoxy self-polymerization was also reported to have a unique compatibility between clay and organic resin matrix. However, the matrix domain lacks of covalently bonded crosslink and leads to the isolation of powder material. It is generally concluded that the hydrophobic expansion of the clay inter-gallery spacing is the crucial step for enhancing the compatibility and the ultimate preparation of the advanced epoxy materials.

Phenolic Compounds Analysis of Root, Stalk, and Leaves of Nettle

Directory of Open Access Journals (Sweden)

Semih Otles

2012-01-01

Full Text Available Types of nettles (Urtica dioica were collected from different regions to analyze phenolic compounds in this research. Nettles are specially grown in the coastal part. According to this kind of properties, nettle samples were collected from coastal part of (Mediterranean, Aegean, Black sea, and Marmara Turkey. Phenolic profile, total phenol compounds, and antioxidant activities of nettle samples were analyzed. Nettles were separated to the part of root, stalk, and leaves. Then, these parts of nettle were analyzed to understand the difference of phenolic compounds and amount of them. Nettle (root, stalk and leaves samples were analyzed by using High-Performance Liquid Chromatography with Diode-Array Detection (HPLC-DAD to qualitative and quantitative determination of the phenolic compounds. Total phenolic components were measured by using Folin-Ciocalteu method. The antioxidant activity was measured by using DPPH (2,2-diphenyl-1-picrylhydrazyl which is generally used for herbal samples and based on single electron transfer (SET.

Phenolic compounds analysis of root, stalk, and leaves of nettle.

Science.gov (United States)

Otles, Semih; Yalcin, Buket

2012-01-01

Types of nettles (Urtica dioica) were collected from different regions to analyze phenolic compounds in this research. Nettles are specially grown in the coastal part. According to this kind of properties, nettle samples were collected from coastal part of (Mediterranean, Aegean, Black sea, and Marmara) Turkey. Phenolic profile, total phenol compounds, and antioxidant activities of nettle samples were analyzed. Nettles were separated to the part of root, stalk, and leaves. Then, these parts of nettle were analyzed to understand the difference of phenolic compounds and amount of them. Nettle (root, stalk and leaves) samples were analyzed by using High-Performance Liquid Chromatography with Diode-Array Detection (HPLC-DAD) to qualitative and quantitative determination of the phenolic compounds. Total phenolic components were measured by using Folin-Ciocalteu method. The antioxidant activity was measured by using DPPH (2,2-diphenyl-1-picrylhydrazyl) which is generally used for herbal samples and based on single electron transfer (SET).

Phenolic Compounds Analysis of Root, Stalk, and Leaves of Nettle

Science.gov (United States)

Otles, Semih; Yalcin, Buket

2012-01-01

Types of nettles (Urtica dioica) were collected from different regions to analyze phenolic compounds in this research. Nettles are specially grown in the coastal part. According to this kind of properties, nettle samples were collected from coastal part of (Mediterranean, Aegean, Black sea, and Marmara) Turkey. Phenolic profile, total phenol compounds, and antioxidant activities of nettle samples were analyzed. Nettles were separated to the part of root, stalk, and leaves. Then, these parts of nettle were analyzed to understand the difference of phenolic compounds and amount of them. Nettle (root, stalk and leaves) samples were analyzed by using High-Performance Liquid Chromatography with Diode-Array Detection (HPLC-DAD) to qualitative and quantitative determination of the phenolic compounds. Total phenolic components were measured by using Folin-Ciocalteu method. The antioxidant activity was measured by using DPPH (2,2-diphenyl-1-picrylhydrazyl) which is generally used for herbal samples and based on single electron transfer (SET). PMID:22593694

Epoxy Nanocomposites filled with Carbon Nanoparticles.

Science.gov (United States)

Martin-Gallego, M; Yuste-Sanchez, V; Sanchez-Hidalgo, R; Verdejo, R; Lopez-Manchado, M A

2018-01-10

Over the past decades, the development of high performance lightweight polymer nanocomposites and, in particular, of epoxy nanocomposites has become one the greatest challenges in material science. The ultimate goal of epoxy nanocomposites is to extrapolate the exceptional intrinsic properties of the nanoparticles to the bulk matrix. However, in spite of the efforts, this objective is still to be attained at commercially attractive scales. Key aspects to achieve this are ultimately the full understanding of network structure, the dispersion degree of the nanoparticles, the interfacial adhesion at the phase boundaries and the control of the localization and orientation of the nanoparticles in the epoxy system. In this Personal Account, we critically discuss the state of the art and evaluate the strategies to overcome these barriers. © 2018 The Chemical Society of Japan & Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Toxicity of Phenol and Salt on the Phenol-Degrading Pseudomonas aeruginosa Bacterium

Directory of Open Access Journals (Sweden)

Samaei

2016-08-01

Full Text Available Background Phenolic compounds, phenol and phenol derivatives are environmental contaminants in some industrial effluents. Entrance of such substances into the environment causes severe environmental pollution, especially pollution of water resources. Biological treatment is a method that uses the potential of microorganisms to clean up contaminated environments. Among microorganisms, bacteria play an important role in treating wastewater contaminated with phenol. Objectives This study aimed to examine the effects of Pseudomonas aeruginosa on degradation of phenol in wastewater contaminated with this pollutant. Methods In this method, the growth rate of P. aeruginosa bacteria was investigated using different concentrations of salt and phenol. This is an experimental study conducted as a pilot in a batch reactor with different concentrations of phenol (25, 50, 100, 150, 300 and 600 mg L-1 and salt (0%, 0.5%, 1%, 2.5% and 5% during 9, 12 and 15 hours. During three days, from 5 experimental and 3 control samples, 18 samples were taken a day forming a sample size of 54 samples for each phenol concentration. Given the number of phenol concentrations (n = 6, a total of 324 samples were analyzed using a spectrophotometer at a wavelength of 600 nm. Results The phenol concentration of 600 mg L-1 was toxic for P. aeruginosa. However, at a certain concentration, it acts as a carbon source for P. aeruginosa. During investigations, it was found that increasing the concentration of phenol increases the rate of bacteria growth. The highest bacteria growth rate occurred was at the salt concentration of zero and phenol concentration of 600 mg L-1. Conclusions The findings of the current study indicate that at high concentrations of salt, the growth of bacteria reduces so that it stops at a concentration of 50 mg L-1 (5%. Thus, the bacterium is halotolerant or halophilic. With an increase in phenol concentration, the growth rate increased. Phenol toxicity appears

Mechanical Reinforcement of Epoxy Composites with Carbon Fibers and HDPE

Science.gov (United States)

He, R.; Chang, Q.; Huang, X.; Li, J.

2018-01-01

Silanized carbon fibers (CFs) and a high-density polyethylene with amino terminal groups (HDPE) were introduced into epoxy resins to fabricate high-performance composites. A. mechanical characterization of the composites was performed to investigate the effect of CFs in cured epoxy/HDPE systems. The composites revealed a noticeable improvement in the tensile strength, elongation at break, flexural strength, and impact strength in comparison with those of neat epoxy and cured epoxy/HDPE systems. SEM micrographs showed that the toughening effect could be explained by yield deformations, phase separation, and microcracking.

Functionalizing CNTs for Making Epoxy/CNT Composites

Science.gov (United States)

Chen, Jian; Rajagopal, Ramasubramaniam

2009-01-01

Functionalization of carbon nanotubes (CNTs) with linear molecular side chains of polyphenylene ether (PPE) has been shown to be effective in solubilizing the CNTs in the solvent components of solutions that are cast to make epoxy/CNT composite films. (In the absence of solubilization, the CNTs tend to clump together instead of becoming dispersed in solution as needed to impart, to the films, the desired CNT properties of electrical conductivity and mechanical strength.) Because the PPE functionalizes the CNTs in a noncovalent manner, the functionalization does not damage the CNTs. The functionalization can also be exploited to improve the interactions between CNTs and epoxy matrices to enhance the properties of the resulting composite films. In addition to the CNTs, solvent, epoxy resin, epoxy hardener, and PPE, a properly formulated solution also includes a small amount of polycarbonate, which serves to fill voids that, if allowed to remain, would degrade the performance of the film. To form the film, the solution is drop-cast or spin-cast, then the solvent is allowed to evaporate.

Preparation and Performance of Amphiphilic Random Copolymer Noncovalently Modified MWCNTs/Epoxy Composite

Directory of Open Access Journals (Sweden)

MA Qiang

2016-09-01

Full Text Available An amphiphilic random copolymer of polyglycidyl methacrylate-co-N-vinyl carbazole P(GMA-co-NVC was synthesized by free radical polymerization and was used to noncovalently modify multi-walled carbon nanotubes (MWCNTs. The obtained P(GMA-co-NVC/MWCNTs was mixed with epoxy resin and used to reinforce epoxy resin. Polymer modified carbon nanotubes/epoxy resin composites were prepared by a casting molding method. Tensile test, electrical resistivity test and differential scanning calorimeter(DSC analysis were used to study the effect of polymer modified carbon nanotubes on the mechanical, electrical, and thermal properties of epoxy resin. The results show that the epoxy composite reinforced with P(GMA-co-NVC/MWCNTs shows a remarkable enhancement in both tensile strength and elongation at break compared to either the pure epoxy or the pristine MWCNTs/epoxy composites. In addition, the electrical conductivity of epoxy is significantly improved and the volume resistivity decreases from 1014Ω·m to 106Ω·m with 0.25% mass fraction loading of P(GMA-co-NVC/MWCNTs. Moreover, glass transition temperature of the epoxy composite also increases from 144℃ to 149℃.

Phenolic compounds in Ross Sea water

Science.gov (United States)

Zangrando, Roberta; Barbaro, Elena; Gambaro, Andrea; Barbante, Carlo; Corami, Fabiana; Kehrwald, Natalie; Capodaglio, Gabriele

2016-04-01

Phenolic compounds are semi-volatile organic compounds produced during biomass burning and lignin degradation in water. In atmospheric and paleoclimatic ice cores studies, these compounds are used as biomarkers of wood combustion and supply information on the type of combusted biomass. Phenolic compounds are therefore indicators of paleoclimatic interest. Recent studies of Antarctic aerosols highlighted that phenolic compounds in Antarctica are not exclusively attributable to biomass burning but also derive from marine sources. In order to study the marine contribution to aerosols we developed an analytical method to determine the concentration of vanillic acid, vanillin, p-coumaric acid, syringic acid, isovanillic acid, homovanillic acid, syringaldehyde, acetosyringone and acetovanillone present in dissolved and particle phases in Sea Ross waters using HPLC-MS/MS. The analytical method was validated and used to quantify phenolic compounds in 28 sea water samples collected during a 2012 Ross Sea R/V cruise. The observed compounds were vanillic acid, vanillin, acetovanillone and p-coumaric acid with concentrations in the ng/L range. Higher concentrations of analytes were present in the dissolved phase than in the particle phase. Sample concentrations were greatest in the coastal, surficial and less saline Ross Sea waters near Victoria Land.

Thermosetting polymer for dynamic nuclear polarization: Solidification of an epoxy resin mixture including TEMPO

Energy Technology Data Exchange (ETDEWEB)

Noda, Yohei, E-mail: noda.yohei@jaea.go.jp [Quantum Beam Science Centre, Sector of Nuclear Science Research, Japan Atomic Energy Agency, Shirakata-Shirane, Tokai, Ibaraki 319-1195 (Japan); Kumada, Takayuki [Quantum Beam Science Centre, Sector of Nuclear Science Research, Kansai Photon Science Institute, Japan Atomic Energy Agency, Kizugawa, Kyoto 619-0215 (Japan); Yamaguchi, Daisuke; Shamoto, Shin-ichi [Quantum Beam Science Centre, Sector of Nuclear Science Research, Japan Atomic Energy Agency, Shirakata-Shirane, Tokai, Ibaraki 319-1195 (Japan)

2015-03-11

We investigated the dynamic nuclear polarization (DNP) of typical thermosetting polymers (two-component type epoxy resins; Araldite{sup ®} Standard or Araldite{sup ®} Rapid) doped with a (2,2,6,6-tetramethylpiperidine-1-yl)oxy (TEMPO) radical. The doping process was developed by carefully considering the decomposition of TEMPO during the solidification of the epoxy resin. The TEMPO electron spin in each two-component paste decayed slowly, which was favorable for our study. Furthermore, despite the dissolved TEMPO, the mixture of the two-component paste successfully solidified. With the resulting TEMPO-doped epoxy-resin samples, DNP experiments at 1.2 K and 3.35 T indicated a magnitude of a proton-spin polarization up to 39%. This polarization is similar to that (35%) obtained for TEMPO-doped polystyrene (PS), which is often used as a standard sample for DNP. To combine this solidification of TEMPO-including mixture with a resin-casting technique enables a creation of polymeric target materials with a precise and complex structure.

Multiscale Modeling of Carbon Nanotube-Epoxy Nanocomposites

Science.gov (United States)

Fasanella, Nicholas A.

Epoxy-composites are widely used in the aerospace industry. In order to improve upon stiffness and thermal conductivity; carbon nanotube additives to epoxies are being explored. This dissertation presents multiscale modeling techniques to study the engineering properties of single walled carbon nanotube (SWNT)-epoxy nanocomposites, consisting of pristine and covalently functionalized systems. Using Molecular Dynamics (MD), thermomechanical properties were calculated for a representative polymer unit cell. Finite Element (FE) and orientation distribution function (ODF) based methods were used in a multiscale framework to obtain macroscale properties. An epoxy network was built using the dendrimer growth approach. The epoxy model was verified by matching the experimental glass transition temperature, density, and dilatation. MD, via the constant valence force field (CVFF), was used to explore the mechanical and dilatometric effects of adding pristine and functionalized SWNTs to epoxy. Full stiffness matrices and linear coefficient of thermal expansion vectors were obtained. The Green-Kubo method was used to investigate the thermal conductivity as a function of temperature for the various nanocomposites. Inefficient phonon transport at the ends of nanotubes is an important factor in the thermal conductivity of the nanocomposites, and for this reason discontinuous nanotubes were modeled in addition to long nanotubes. To obtain continuum-scale elastic properties from the MD data, multiscale modeling was considered to give better control over the volume fraction of nanotubes, and investigate the effects of nanotube alignment. Two methods were considered; an FE based method, and an ODF based method. The FE method probabilistically assigned elastic properties of elements from the MD lattice results based on the desired volume fraction and alignment of the nanotubes. For the ODF method, a distribution function was generated based on the desired amount of nanotube alignment

Rapid microwave processing of epoxy nanocomposites using carbon nanotubes

OpenAIRE

Luhyna, Nataliia; Inam, Fawad; Winnington, Ian

2013-01-01

Microwave processing is one of the rapid processing techniques for manufacturing nanocomposites. There is very little work focussing on the addition of CNTs for shortening the curing time of epoxy nanocomposites. Using microwave energy, the effect of CNT addition on the curing of epoxy nanocomposites was researched in this work. Differential scanning calorimetry (DSC) was used to determine the degree of cure for epoxy and nanocomposite samples. CNT addition significantly reduced the duration ...

Structural and electrical properties of functionalized multiwalled carbon nanotube/epoxy composite

International Nuclear Information System (INIS)

Gantayat, S.; Rout, D.; Swain, S. K.

2016-01-01

The effect of the functionalization of multiwalled carbon nanotube on the structure and electrical properties of composites was investigated. Samples based on epoxy resin with different weight percentage of MWCNTs were prepared and characterized. The interaction between MWCNT & epoxy resin was noticed by Fourier transform infrared spectroscopy (FTIR). The structure of functionalized multiwalled carbon nanotube (f-MWCNT) reinforced epoxy composite was studied by field emission scanning electron microscope (FESEM). The dispersion of f-MWCNT in epoxy resin was evidenced by high resolution transmission electron microscope (HRTEM). Electrical properties of epoxy/f-MWCNT nanocomposites were measured & the result indicated that the conductivity increased with increasing concentration of f-MWCNTs.

Experimental design applied optimization of a state in epoxy clay dispersion

International Nuclear Information System (INIS)

Paz, Juliana D'Avila; Bertholdi, Jonas; Folgueras, Marilena Valadares; Pezin, Sergio Henrique; Coelho, Luiz Antonio Ferreira

2010-01-01

This paper presents some analysis showed that the exfoliation / intercalation of a montmorillonite clay in epoxy resin such as viscosity, X-ray diffraction (XRD), scanning electron microscopy (SEM) and thermogravimetry (TG). Increasing the viscosity of epoxy resin diglycidyl ether bisphenol A with the addition of clay associated with the sonification system at the time of dispersion is a good indication of exfoliation. The X-ray diffraction already cured composite shows a decrease of crystallinity of clay and EDS microanalysis of SEM, non-uniform dispersion of clay in epoxy resin. Thermal analysis TG composite clay / epoxy shows an increase in thermal stability relative to pure epoxy. (author)

Phenolic Molding Compounds

Science.gov (United States)

Koizumi, Koji; Charles, Ted; de Keyser, Hendrik

Phenolic Molding Compounds continue to exhibit well balanced properties such as heat resistance, chemical resistance, dimensional stability, and creep resistance. They are widely applied in electrical, appliance, small engine, commutator, and automotive applications. As the focus of the automotive industry is weight reduction for greater fuel efficiency, phenolic molding compounds become appealing alternatives to metals. Current market volumes and trends, formulation components and its impact on properties, and a review of common manufacturing methods are presented. Molding processes as well as unique advanced techniques such as high temperature molding, live sprue, and injection/compression technique provide additional benefits in improving the performance characterisitics of phenolic molding compounds. Of special interest are descriptions of some of the latest innovations in automotive components, such as the phenolic intake manifold and valve block for dual clutch transmissions. The chapter also characterizes the most recent developments in new materials, including long glass phenolic molding compounds and carbon fiber reinforced phenolic molding compounds exhibiting a 10-20-fold increase in Charpy impact strength when compared to short fiber filled materials. The role of fatigue testing and fatigue fracture behavior presents some insight into long-term reliability and durability of glass-filled phenolic molding compounds. A section on new technology outlines the important factors to consider in modeling phenolic parts by finite element analysis and flow simulation.

Epoxy modified bitumen : Chemical hardening and its interpretation

NARCIS (Netherlands)

Apostolidis, P.; Pipintakos, G.; van de Ven, M.F.C.; Liu, X.; Erkens, Sandra; Scarpas, Athanasios

2018-01-01

Epoxy modified bitumen (EMB) is a promising technology for long lasting paving materials ensuring higher resistance to rutting, oxygen- and moisture-induced damage. In this paper, an analysis of the chemical reactions that take place during the chemical hardening process (curing) of epoxy modified

Thermomechanical Behavior of High Performance Epoxy/Organoclay Nanocomposites

Directory of Open Access Journals (Sweden)

Artur Soares Cavalcanti Leal

2014-01-01

Full Text Available Nanocomposites of epoxy resin containing bentonite clay were fabricated to evaluate the thermomechanical behavior during heating. The epoxy resin system studied was prepared using bifunctional diglycidyl ether of bisphenol A (DGEBA, crosslinking agent diaminodiphenylsulfone (DDS, and diethylenetriamine (DETA. The purified bentonite organoclay (APOC was used in all experiments. The formation of nanocomposite was confirmed by X-ray diffraction analysis. Specimens of the fabricated nanocomposites were characterized by dynamic mechanical analysis (DMA. According to the DMA results a significant increase in glass transition temperature and storage modulus was evidenced when 1 phr of clay is added to epoxy resin.

Generalized morphea/eosinophilic fasciitis overlap after epoxy exposure

Directory of Open Access Journals (Sweden)

Warren H. Chan, MS

2018-03-01

Full Text Available Generalized morphea is associated with epoxy resin vapors and is characterized by the development of lesions shortly after exposure. Morphea presenting along with eosinophilic fasciitis (EF, or morphea/EF overlap, is rare and an indicator of poor prognosis and resistance to treatment. Here we present a case of generalized morphea/EF overlap linked to epoxy exposure. Our patient received multiple therapies—ultraviolet A1 phototherapy, prednisone, methotrexate, azathioprine, mycophenolate mofetil, cyclophosphamide, cyclosporine, and rituximab—none of which led to a significant response. The refractory nature of this disease warrants vigilance in its association with epoxy exposure.

Fabrication and characterization of TiO2-epoxy nanocomposite

International Nuclear Information System (INIS)

Chatterjee, Amit; Islam, Muhammad S.

2008-01-01

A systematic study has been conducted to investigate the matrix properties by introducing nanosize TiO 2 (5-40 nm, 0.5-2% by weight) fillers into an epoxy resin. Ultrasonic mixing process, via sonic cavitations, was employed to disperse the particles into the resin system. The thermal, mechanical, morphology and the viscoelastic properties of the nanocomposite and the neat resin were measured with TGA, DMA, TEM and Instron. The nano-particles are dispersed evenly throughout the entire volume of the resin. The nanofiller infusion improves the thermal, mechanical and viscoelastic properties of the epoxy resin. The nanocomposite shows increase in storage modulus, glass transition temperature, tensile modulus, flexural modulus and short beam shear strength from neat epoxy resin. The mechanical performance and thermal stability of the epoxy nanocomposites are depending on with the dispersion state of the TiO 2 in the epoxy matrix and are correlated with loading (0.0015-0.006% by volume). In addition, the nanocomposite shows enhanced flexural strength. Several reasons to explain these effects in terms of reinforcing mechanisms were discussed

Physical, structural and thermomechanical properties of oil palm nano filler/kenaf/epoxy hybrid nanocomposites

Energy Technology Data Exchange (ETDEWEB)

Saba, N., E-mail: naheedchem@gmail.com [Laboratory of Biocomposite Technology, Institute of Tropical Forestry and Forest Products(INTROP), Universiti Putra Malaysia, 43400 UPM Serdang, Selangor (Malaysia); Paridah, M.T. [Laboratory of Biocomposite Technology, Institute of Tropical Forestry and Forest Products(INTROP), Universiti Putra Malaysia, 43400 UPM Serdang, Selangor (Malaysia); Abdan, K. [Department of Biological and Agricultural Engineering, Faculty of Engineering, Universiti Putra Malaysia, 43400 UPM Serdang Selangor (Malaysia); Ibrahim, N.A. [Department of Chemistry, Faculty of Science, Universiti Putra Malaysia, 43400 UPM Serdang, Selangor (Malaysia)

2016-12-01

The present research study deals with the fabrication of kenaf/epoxy hybrid nanocomposites by the incorporation of oil palm nano filler, montmorillonite (MMT) and organically modified montmorillonite (OMMT) at 3% loading, through hand lay-up technique. Effect of adding different nano fillers on the physical (density), structural [X-ray diffraction (XRD)] and thermomechanical analysis (TMA) of kenaf/epoxy composites were carried out. Density results revealed that the incorporation of nano filler in the kenaf/epoxy composites increases the density which in turn increases the hardness of the hybrid nanocomposites. XRD analysis confirmed the presence of nano fillers in the structure of their respective fabricated hybrid nanocomposites. All hybrid nanocomposites displayed lower coefficient of thermal expansion (CTE) with respect to kenaf/epoxy composites. Overall results predicted that the properties improvement in nano OPEFB/kenaf/epoxy was quite comparable to MMT/kenaf/epoxy but relatively lesser to OMMT/kenaf/epoxy hybrid nanocomposites and higher with respect to kenaf/epoxy composites. The improvement ascribed due to improved interfacial bonding or cross linking between kenaf fibers and epoxy matrix by addition of nano filler. - Highlights: • Nano OPEFB/kenaf/epoxy hybrid nanocomposites were fabricated by hand lay-up. • Effect of nano OPEFB on density & structure of kenaf/epoxy were investigated. • Thermal expansion coefficients of kenaf/epoxy and hybrid nanocomposites evaluated. • Comparative studies were made with MMT and OMMT kenaf/epoxy hybrid nanocomposites.

Physical, structural and thermomechanical properties of oil palm nano filler/kenaf/epoxy hybrid nanocomposites

International Nuclear Information System (INIS)

Saba, N.; Paridah, M.T.; Abdan, K.; Ibrahim, N.A.

2016-01-01

The present research study deals with the fabrication of kenaf/epoxy hybrid nanocomposites by the incorporation of oil palm nano filler, montmorillonite (MMT) and organically modified montmorillonite (OMMT) at 3% loading, through hand lay-up technique. Effect of adding different nano fillers on the physical (density), structural [X-ray diffraction (XRD)] and thermomechanical analysis (TMA) of kenaf/epoxy composites were carried out. Density results revealed that the incorporation of nano filler in the kenaf/epoxy composites increases the density which in turn increases the hardness of the hybrid nanocomposites. XRD analysis confirmed the presence of nano fillers in the structure of their respective fabricated hybrid nanocomposites. All hybrid nanocomposites displayed lower coefficient of thermal expansion (CTE) with respect to kenaf/epoxy composites. Overall results predicted that the properties improvement in nano OPEFB/kenaf/epoxy was quite comparable to MMT/kenaf/epoxy but relatively lesser to OMMT/kenaf/epoxy hybrid nanocomposites and higher with respect to kenaf/epoxy composites. The improvement ascribed due to improved interfacial bonding or cross linking between kenaf fibers and epoxy matrix by addition of nano filler. - Highlights: • Nano OPEFB/kenaf/epoxy hybrid nanocomposites were fabricated by hand lay-up. • Effect of nano OPEFB on density & structure of kenaf/epoxy were investigated. • Thermal expansion coefficients of kenaf/epoxy and hybrid nanocomposites evaluated. • Comparative studies were made with MMT and OMMT kenaf/epoxy hybrid nanocomposites.

Enhanced thermal and mechanical properties of epoxy composites by mixing thermotropic liquid crystalline epoxy grafted graphene oxide

Directory of Open Access Journals (Sweden)

B. Qi

2014-07-01

Full Text Available Graphene oxide (GO sheets were chemically grafted with thermotropic liquid crystalline epoxy (TLCP. Then we fabricated composites using TLCP-g-GO as reinforcing filler. The mechanical properties and thermal properties of composites were systematically investigated. It is found that the thermal and mechanical properties of the composites are enhanced effectively by the addition of fillers. For instance, the composites containing 1.0 wt% of TLCP-g-GO present impact strength of 51.43 kJ/m2, the tensile strength of composites increase from 55.43 to 80.85 MPa, the flexural modulus of the composites increase by more than 48%. Furthermore, the incorporation of fillers is effective to improve the glass transition temperature and thermal stability of the composites. Therefore, the presence of the TLCP-g-GO in the epoxy matrix could make epoxy not only stronger but also tougher.

Predicting the mechanical behaviour of Kevlar/epoxy and carbon/epoxy filament-wound tubes

Science.gov (United States)

Cazeneuve, C.; Joguet, P.; Maile, J. C.; Oytana, C.

1992-11-01

The axial, hoop and shear moduli and failure conditions of carbon/epoxy and Kevlar/epoxy filament-wound tubes have been determined through respective applications of internal pressure, tension and torsion. The introduction in the laminated plate theory of a gradual reduction in individual moduli makes it possible to overcome the limitations of the theory and enables accurate predictions to be made of the linear and non-linear stress/strain curves of 90 deg +/- 0/90 deg tubes. The existence of a dominant layer in the failure of the multilayered tubes has been shown experimentally. When associated with a failure criterion applied to the dominant layer, the new model permits the prediction of tube failure. Agreement between calculated and experimental data is better than 5 percent.

Epoxy encapsulant as serendipitous dosimeters during radiological/nuclear events

Energy Technology Data Exchange (ETDEWEB)

Barkyoumb, J.H. [Carderock Division, Naval Surface Warfare Center, 9500 MacArthur Blvd., West Bethesda, MD 20817-5700 (United States)], E-mail: jhbarky@earthlink.net; Mathur, V.K. [Carderock Division, Naval Surface Warfare Center, 9500 MacArthur Blvd., West Bethesda, MD 20817-5700 (United States)

2008-02-15

The radiation response of a smart chip (embedded integrated circuit) module has been reported earlier using the technique of optically stimulated luminescence (OSL). It was found that a smart chip module could be used to evaluate the personnel exposure in the accident dosimetry range. Through subsequent experiments, the radiation sensitivity of the chip module was traced to the epoxy encapsulant provided to protect the chip from the environment and physical damage and that the radiation sensitivity of the epoxy is due to the silica used as the 'filler' for controlling the thixotropic properties of the epoxy used for 'glob top' or 'dam-and-fill' encapsulation. It is desirable to retain the ability to use the smart chip as an accident dosimeter without requiring a modification of standard manufacturing process for which an infrastructure already exists to avoid additional costs. For this reason, we have investigated commercially available filled and unfilled epoxies both as received from the manufacturer and compared their response with epoxies to which commercial fillers are added. In this work we investigate the OSL response of various epoxies commonly used for potting of electronic circuits with and without various filler materials for their potential to be used as a casualty dosimeter in the exposure range of 0.5-10 Gy.

Processing and properties of carbon nanofibers reinforced epoxy powder composites

International Nuclear Information System (INIS)

Palencia, C.; Mazo, M. A.; Nistal, A.; Rubio, F.; Rubio, J.; Oteo, J. L.

2011-01-01

Commercially available CNFs (diameter 30–300 nm) have been used to develop both bulk and coating epoxy nanocomposites by using a solvent-free epoxy matrix powder. Processing of both types of materials has been carried out by a double-step process consisting in an initial physical premix of all components followed by three consecutive extrusions. The extruded pellets were grinded into powder and sieved. Carbon nanofibers powder coatings were obtained by electrostatic painting of the extruded powder followed by a curing process based in a thermal treatment at 200 °C for 25 min. On the other hand, for obtaining bulk carbon nanofibers epoxy composites, a thermal curing process involving several steps was needed. Gloss and mechanical properties of both nanocomposite coatings and bulk nanocomposites were improved as a result of the processing process. FE-SEM fracture surface microphotographs corroborate these results. It has been assessed the key role played by the dispersion of CNFs in the matrix, and the highly important step that is the processing and curing of the nanocomposites. A processing stage consisted in three consecutive extrusions has reached to nanocomposites free of entanglements neither agglomerates. This process leads to nanocomposite coatings of enhanced properties, as it has been evidenced through gloss and mechanical properties. A dispersion limit of 1% has been determined for the studied system in which a given dispersion has been achieved, as the bending mechanical properties have been increased around 25% compared with the pristine epoxy resin. It has been also demonstrated the importance of the thickness in the nanocomposite, as it involves the curing stage. The complex curing treatment carried out in the case of bulk nanocomposites has reached to reagglomeration of CNFs.

Processing and properties of carbon nanofibers reinforced epoxy powder composites

Science.gov (United States)

Palencia, C.; Mazo, M. A.; Nistal, A.; Rubio, F.; Rubio, J.; Oteo, J. L.

2011-11-01

Commercially available CNFs (diameter 30-300 nm) have been used to develop both bulk and coating epoxy nanocomposites by using a solvent-free epoxy matrix powder. Processing of both types of materials has been carried out by a double-step process consisting in an initial physical premix of all components followed by three consecutive extrusions. The extruded pellets were grinded into powder and sieved. Carbon nanofibers powder coatings were obtained by electrostatic painting of the extruded powder followed by a curing process based in a thermal treatment at 200 °C for 25 min. On the other hand, for obtaining bulk carbon nanofibers epoxy composites, a thermal curing process involving several steps was needed. Gloss and mechanical properties of both nanocomposite coatings and bulk nanocomposites were improved as a result of the processing process. FE-SEM fracture surface microphotographs corroborate these results. It has been assessed the key role played by the dispersion of CNFs in the matrix, and the highly important step that is the processing and curing of the nanocomposites. A processing stage consisted in three consecutive extrusions has reached to nanocomposites free of entanglements neither agglomerates. This process leads to nanocomposite coatings of enhanced properties, as it has been evidenced through gloss and mechanical properties. A dispersion limit of 1% has been determined for the studied system in which a given dispersion has been achieved, as the bending mechanical properties have been increased around 25% compared with the pristine epoxy resin. It has been also demonstrated the importance of the thickness in the nanocomposite, as it involves the curing stage. The complex curing treatment carried out in the case of bulk nanocomposites has reached to reagglomeration of CNFs.

Morphology and contact angle studies of poly(styrene-co-acrylonitrile modified epoxy resin blends and their glass fibre reinforced composites

Directory of Open Access Journals (Sweden)

2007-06-01

Full Text Available In this study, the surface characteristics of blends and composites of epoxy resin were investigated. Poly(styrene-co-acylonitrile (SAN was used to modify diglycedyl ether of bisphenol-A (DGEBA type epoxy resin cured with diamino diphenyl sulfone (DDS and the modified epoxy resin was used as the matrix for fibre reinforced composites (FRP’s. E-glass fibre was used as the fibre reinforcement. The scanning electron micrographs of the fractured surfaces of the blends and composites were analyzed. Morphological analysis revealed different morphologies such as dispersed, cocontinuous and phase-inverted structures for the blends. Contact angle studies were carried out using water and methylene iodide at room temperature. The solid surface energy was calculated using harmonic mean equations. Blending of epoxy resin increases its contact angle. The surface free energy, work of adhesion, interfacial free energy, spreading coefficient and Girifalco-Good’s interaction parameter were changed significantly in the case of blends and composites. The incorporation of thermoplastic and glass fibre reduces the wetting and hydrophilicity of epoxy resin.

Evaluation of epoxy resin for cryogenic use by positron annihilation method. Change of characteristics of epoxy resin with cross-linking density and positron lifetime

International Nuclear Information System (INIS)

Nishijima, Shigehiro; Honda, Yoshihide; Okada, Toichi; Kobayashi, Yoshinori; Namba, Shingo.

1994-01-01

The positron annihilation method has been applied to evaluate unoccupied space in epoxy aiming at the design of the molecular structure for cryogenic use. To confirm the model in which molecular free space is needed in the epoxy for cryogenic use, the molecular weight between cross-linkings in epoxy was changed. The increase of molecular weight between cross-linkings brought an increase of fracture toughness even at liquid helium temperature and the model was found to be confirmed. The increase of molecular weight between cross-linkings was also found to decrease the 3rd lifetime of positrons. It suggested that the epoxy main chains were folded and this was confirmed by the molecular mechanical calculation. (author)

Thermal conductivity of pillared graphene-epoxy nanocomposites using molecular dynamics

Science.gov (United States)

Lakshmanan, A.; Srivastava, S.; Ramazani, A.; Sundararaghavan, V.

2018-04-01

Thermal conductivity in a pillared graphene-epoxy nanocomposite (PGEN) is studied using equilibrium molecular dynamics simulations. PGEN is a proposed material for advanced thermal management applications because it combines high in-plane conductivity of graphene with high axial conductivity of a nanotube to significantly enhance the overall conductivity of the epoxy matrix material. Anisotropic conductivity of PGEN has been compared with that of pristine and functionalized carbon nanotube-epoxy nanocomposites, showcasing the advantages of the unique hierarchical structure of PGEN. Compared to pure carbon allotropes, embedding the epoxy matrix also promotes a weaker dependence of conductivity on thermal variations. These features make this an attractive material for thermal management applications.

(nanoclay and CaSiO3)-reinforced E-glass-reinforced epoxy

Indian Academy of Sciences (India)

For instance, Zhang et al. [6] have prepared 30 types of epoxy matrix reinforced with ... the resin in a high-speed metal blade rotation medium. The .... Tests were run for .... Figure 2. Mean effect plots showing the influence of load, nanoclay content and speed on ..... [8] Wang K, Chen L, Wu J, Toh M L, He C and Yee A F 2005.

Thermoset Blends of an Epoxy Resin and Polydicyclopentadiene

Energy Technology Data Exchange (ETDEWEB)

Rohde, Brian J.; Le, Kim Mai; Krishnamoorti, Ramanan; Robertson, Megan L.

2016-12-13

The mechanical properties of two chemically distinct and complementary thermoset polymers were manipulated through development of thermoset blends. The thermoset blend system was composed of an anhydride-cured diglycidyl ether of bisphenol A (DGEBA)-based epoxy resin, contributing high tensile strength and modulus, and polydicyclopentadiene (PDCPD), which has a higher toughness and impact strength as compared to other thermoset polymers. Ultra-small-angle and small-angle X-ray scattering analysis explored the morphology of concurrently cured thermoset blends, revealing a macroscopically phase separated system with a surface fractal structure across blended systems of varying composition. The epoxy resin rich and PDCPD rich phases exhibited distinct glass transitions (Tg’s): the Tg observed at higher temperature was associated with the epoxy resin rich phase and was largely unaffected by the presence of PDCPD, whereas the PDCPD rich phase Tg systematically decreased with increasing epoxy resin content due to inhibition of dicyclopentadiene ring-opening metathesis polymerization. The mechanical properties of these phase-separated blends were in reasonable agreement with predictions by the rule of mixtures for the blend tensile strength, modulus, and fracture toughness. Scanning electron microscopy analysis of the tensile and fracture specimen fracture surfaces showed an increase in energy dissipation mechanisms, such as crazing, shear banding, and surface roughness, as the fraction of the more ductile component, PDPCD, increased. These results present a facile method to tune the mechanical properties of a toughened thermoset network, in which the high modulus and tensile strength of the epoxy resin can be largely retained at high epoxy resin content in the blend, while increasing the fracture toughness.

Self-healing woven glass fabric/epoxy composites with the healant consisting of micro-encapsulated epoxy and latent curing agent

International Nuclear Information System (INIS)

Yin Tao; Zhou Lin; Rong Minzhi; Zhang Mingqiu

2008-01-01

This paper reports a study of self-healing woven glass fabric reinforced epoxy composites. The healing agent was a two-component one synthesized in the authors' laboratory, which consisted of epoxy-loaded urea-formaldehyde microcapsules as the polymerizable binder and CuBr 2 (2-methylimidazole) 4 (CuBr 2 (2-MeIm) 4 ) as the latent hardener. Both the microcapsules and the matching catalyst were pre-embedded and pre-dissolved in the composites' matrix, respectively. When the microcapsules are split by propagating cracks, the uncured epoxy can be released into the damaged areas and then consolidated under the catalysis of CuBr 2 (2-MeIm) 4 that was homogeneously distributed in the composites' matrix on a molecular scale. As a result, the cracked faces can be bonded together. The influence of the content of the self-healing agent on the composites' tensile properties, interlaminar fracture toughness and healing efficiency was evaluated. It was found that a healing efficiency over 70% relative to the fracture toughness of virgin composites was obtained in the case of 30 wt% epoxy-loaded microcapsules and 2 wt% latent hardener

Fabrication and mechanical properties of multi-walled carbon nanotubes/epoxy nanocomposites

International Nuclear Information System (INIS)

Yeh, M.-K.; Hsieh, T.-H.; Tai, N.-H.

2008-01-01

Carbon nanotubes have better physical and mechanical behavior than the traditional materials. In this study, the multi-walled carbon nanotubes (MWNTs) were added to the epoxy resin as a reinforcement to fabricate MWNTs/epoxy nanocomposites. The pressure and temperature were applied to cure the MWNTs/epoxy compound by hot press method. Mechanical properties such as tensile strength, Young's modulus, and Poisson's ratio were measured. The effect of weight percentages of the MWNTs was investigated. Morphologies of the fracture surface of MWNTs/epoxy nanocomposites were observed by scanning electron microscope

Stronger Fire-Resistant Epoxies

Science.gov (United States)

Fohlen, George M.; Parker, John A.; Kumar, Devendra

1988-01-01

New curing agent improves mechanical properties and works at lower temperature. Use of aminophenoxycyclotriphosphazene curing agents yields stronger, more heat- and fire-resistant epoxy resins. Used with solvent if necessary for coating fabrics or casting films.

Fullerene–epoxy nanocomposites-enhanced mechanical properties at low nanofiller loading

International Nuclear Information System (INIS)

Rafiee, Mohammad A.; Yavari, Fazel; Rafiee, Javad; Koratkar, Nikhil

2011-01-01

In this study, we characterized the mechanical properties of fullerence (C 60 ) epoxy nanocomposites at various weight fractions of fullerene additives in the epoxy matrix. The mechanical properties measured were the Young’s modulus, ultimate tensile strength, fracture toughness, fracture energy, and the material’s resistance to fatigue crack propagation. All of the above properties of the epoxy polymer were significantly enhanced by the fullerene additives at relatively low nanofiller loading fractions (∼0.1 to 1% of the epoxy matrix weight). By contrast, other forms of nanoparticle fillers such as silica, alumina, and titania nanoparticles require up to an order of magnitude higher weight fraction to achieve comparable enhancement in properties.

Thermal properties of oil palm nano filler/kenaf reinforced epoxy hybrid nanocomposites

Science.gov (United States)

Saba, N.; Paridah, M. T.; Abdan, K.; Ibrahim, N. A.

2016-11-01

The aim of this research study was to fabricate nano oil palm empty fruit bunch (OPEFB)/kenaf/epoxy hybrid nanocomposites and to make comparative study on the thermal properties of nano OPEFB/kenaf/epoxy hybrid nanocomposites with the montmorillonite (MMT)/kenaf/epoxy hybrid nanocomposites and organically modified MMT (OMMT)/kenaf/epoxy hybrid nanocomposites. Epoxy based kenaf hybrid nanocomposites was prepared by dispersing the nano filler (nano OPEFB filler, MMT, OMMT) at 3% loading through high speed mechanical stirrer followed by hand lay-up technique. Thermal properties of hybrid nanocomposites were analyzed through thermogravimetry analyzer (TGA), and differential scanning calorimetry (DSC). Obtained results specified that addition of nano OPEFB filler improves the thermal stability and char yield of kenaf/epoxy composites. Furthermore, the increase in decomposition temperature by the nano OPEFB filler was quite comparable to the MMT/kenaf/epoxy but relatively less than OMMT/kenaf/epoxy hybrid nanocomposites. We concluded from overall consequences that the nano OPEFB filler can be used as the promising and innovative alternative of existing expensive nano filler, with relatively lesser impact on the environment having marked pronounced impact on the construction, automotive, aerospace, electronics and semiconducting sectors as future industries based on bio-wastes with satisfactory light weight and thermal stability on other side.

Rheological and electrical properties of hybrid nanocomposites of epoxy resins filled with graphite nanoplatelets and carbon black.

Science.gov (United States)

Truong, Quang-Trung; Lee, Seon-Suk; Lee, Dai-Soo

2011-02-01

Graphite nanoplatelets (GNP) were prepared by microwave irradiation of natural graphites intercalated with ferric chloride in nitromethane (GIC). Intercalated structure of GIC was confirmed by X-ray diffraction patterns. SEM images of GIC after microwave irradiation showed the exfoliation of GIC, the formation of GNPs. Hybrid nanocomposites of bisphenol-A type epoxy resins filled with GNP and a conductive carbon black (CB) were prepared and rheological and electrical properties of the nanocomposites were investigated. Viscosity and electrical surface resistivity of the nanocomposites showed minima at certain mixtures of GNP and CB in the epoxy resins.

Stochastic estimation of acoustic impedance of glass-reinforced epoxy coating 128-134

Energy Technology Data Exchange (ETDEWEB)

Kim, No Hyu [School of MechatronicEngineering, Korea University of Technology and Education, Chunan (Korea, Republic of); Nah, Hwan Seon [Structural Engineering Lab., Korea Electric Power Research Institute, Daejeon (Korea, Republic of)

2014-04-15

An epoxy coating applied to the concrete surface of a containment building deteriorates in hazardous environments such as those containing radiation, heat, and moisture. Unlike metals, the epoxy coating on a concrete liner absorbs and discharges moisture during the degradations process, so it has a different density and volume during service. In this study, acoustic impedance was adopted for characterizing the degradation of a glass-reinforced epoxy coating using the acoustic reflection coefficient (reflectance) on a rough epoxy coating. For estimating the acoustic reflectance on a wavy epoxy coating surface, a probabilistic model was developed to represent the multiple irregular reflections of the acoustic wave from the wavy surface on the basis of the simulated annealing technique. A number of epoxy-coated concrete specimens were prepared and exposed to accelerated aging conditions to induce an artificial aging degradation in them. The acoustic impedance of the degraded epoxy coating was estimated successfully by minimizing the error between a waveform calculated from the mathematical model and a waveform measured from the surface of the rough coating.

Stochastic estimation of acoustic impedance of glass-reinforced epoxy coating 128-134

International Nuclear Information System (INIS)

Kim, No Hyu; Nah, Hwan Seon

2014-01-01

An epoxy coating applied to the concrete surface of a containment building deteriorates in hazardous environments such as those containing radiation, heat, and moisture. Unlike metals, the epoxy coating on a concrete liner absorbs and discharges moisture during the degradations process, so it has a different density and volume during service. In this study, acoustic impedance was adopted for characterizing the degradation of a glass-reinforced epoxy coating using the acoustic reflection coefficient (reflectance) on a rough epoxy coating. For estimating the acoustic reflectance on a wavy epoxy coating surface, a probabilistic model was developed to represent the multiple irregular reflections of the acoustic wave from the wavy surface on the basis of the simulated annealing technique. A number of epoxy-coated concrete specimens were prepared and exposed to accelerated aging conditions to induce an artificial aging degradation in them. The acoustic impedance of the degraded epoxy coating was estimated successfully by minimizing the error between a waveform calculated from the mathematical model and a waveform measured from the surface of the rough coating.

Hansen solubility parameters for a carbon fiber/epoxy composite

DEFF Research Database (Denmark)

Launay, Helene; Hansen, Charles M.; Almdal, Kristoffer

2007-01-01

In this study, the physical affinity between an epoxy matrix and oxidized, unsized carbon fibers has been evaluated using Hansen solubility (cohesion) parameters (HSP). A strong physical compatibility has been shown, since their respective HSP are close. The use of a glassy carbon substrate...... as a model for unsized carbon fiber has been demonstrated as appropriate for the study of interactions between the materials in composite carbon fiber-epoxy systems. The HSP of glassy carbon are similar to those of carbon fibers and epoxy matrix. (C) 2007 Elsevier Ltd. All rights reserved....

Electrical and Mechanical Properties of 3D-Printed Graphene-Reinforced Epoxy

Science.gov (United States)

Compton, Brett G.; Hmeidat, Nadim S.; Pack, Robert C.; Heres, Maximilian F.; Sangoro, Joshua R.

2018-03-01

Recent developments in additive manufacturing have demonstrated the potential for thermoset polymer feedstock materials to achieve high strength, stiffness, and functionality through incorporation of structural and functional filler materials. In this work, graphene was investigated as a potential filler material to provide rheological properties necessary for direct-write three-dimensional (3D) printing and electrostatic discharge properties to the printed component. The rheological properties of epoxy/graphene mixtures were characterized, and printable epoxy/graphene inks formulated. Sheet resistance values for printed epoxy/graphene composites ranged from 0.67 × 102 Ω/sq to 8.2 × 103 Ω/sq. The flexural strength of printed epoxy/graphene composites was comparable to that of cast neat epoxy ( 80 MPa), suggesting great potential for these new materials in multifunctional 3D-printed devices.

Degradation of modified carbon black/epoxy nanocomposite coatings under ultraviolet exposure

International Nuclear Information System (INIS)

Ghasemi-Kahrizsangi, Ahmad; Shariatpanahi, Homeira; Neshati, Jaber; Akbarinezhad, Esmaeil

2015-01-01

Graphical abstract: - Highlights: • Degradation behavior of modified Carbon Black (CB) epoxy coating was studied under UV irradiation using based on EIS technique. • By using SDS as a surfactant, nano particles of CB were uniformly dispersed in an epoxy matrix. • ATR-FTIR analysis showed that the CB coatings were degraded less than epoxy coating. • EIS results showed the coating with 2.5 wt% CB nanoparticles had higher corrosion resistance than neat epoxy. - Abstract: Degradation of epoxy coatings with and without Carbon Black (CB) nanoparticles under ultraviolet (UV) radiation were investigated using electrochemical impedance spectroscopy (EIS). Sodium dodecyl sulfate (SDS) was used to obtain a good dispersion of CB nanoparticles in a polymer matrix. TEM analysis proved a uniform dispersion of modified CB nanoparticles in epoxy coating. The coatings were subjected to UV radiation to study the degradation behavior and then immersed in 3.5 wt% NaCl. The results showed that the electrochemical behavior of neat epoxy coating was related to the formation and development of microcracks on the surface. The occurrence of microcracks on the surface of the coatings and consequently the penetration of ionic species reduced by adding CB nanoparticles into the formulation of the coatings. CB nanoparticles decreased degradation of CB coatings by absorbing UV irradiation. The ATR-FTIR results showed that decrease in the intensity of methyl group as main peak in presence of 2.5 wt% CB was lower than neat epoxy. In addition, the reduction in impedance of neat epoxy coating under corrosive environment was larger than CB coatings. The CB coating with 2.5 wt% nanoparticles had the highest impedance to corrosive media after 2000 h UV irradiation and 24 h immersion in 3.5 wt% NaCl.

Degradation of modified carbon black/epoxy nanocomposite coatings under ultraviolet exposure

Energy Technology Data Exchange (ETDEWEB)

Ghasemi-Kahrizsangi, Ahmad, E-mail: ahmad_usk@yahoo.com [Corrosion Department, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163, Tehran (Iran, Islamic Republic of); Shariatpanahi, Homeira, E-mail: shariatpanahih@ripi.ir [Coating Research Center, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163, Tehran (Iran, Islamic Republic of); Neshati, Jaber [Corrosion Department, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163, Tehran (Iran, Islamic Republic of); Akbarinezhad, Esmaeil [Coating Research Center, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163, Tehran (Iran, Islamic Republic of)

2015-10-30

Graphical abstract: - Highlights: • Degradation behavior of modified Carbon Black (CB) epoxy coating was studied under UV irradiation using based on EIS technique. • By using SDS as a surfactant, nano particles of CB were uniformly dispersed in an epoxy matrix. • ATR-FTIR analysis showed that the CB coatings were degraded less than epoxy coating. • EIS results showed the coating with 2.5 wt% CB nanoparticles had higher corrosion resistance than neat epoxy. - Abstract: Degradation of epoxy coatings with and without Carbon Black (CB) nanoparticles under ultraviolet (UV) radiation were investigated using electrochemical impedance spectroscopy (EIS). Sodium dodecyl sulfate (SDS) was used to obtain a good dispersion of CB nanoparticles in a polymer matrix. TEM analysis proved a uniform dispersion of modified CB nanoparticles in epoxy coating. The coatings were subjected to UV radiation to study the degradation behavior and then immersed in 3.5 wt% NaCl. The results showed that the electrochemical behavior of neat epoxy coating was related to the formation and development of microcracks on the surface. The occurrence of microcracks on the surface of the coatings and consequently the penetration of ionic species reduced by adding CB nanoparticles into the formulation of the coatings. CB nanoparticles decreased degradation of CB coatings by absorbing UV irradiation. The ATR-FTIR results showed that decrease in the intensity of methyl group as main peak in presence of 2.5 wt% CB was lower than neat epoxy. In addition, the reduction in impedance of neat epoxy coating under corrosive environment was larger than CB coatings. The CB coating with 2.5 wt% nanoparticles had the highest impedance to corrosive media after 2000 h UV irradiation and 24 h immersion in 3.5 wt% NaCl.

Mechanical properties of multi-walled carbon nanotube/epoxy polysulfide nanocomposite

International Nuclear Information System (INIS)

Shirkavand Hadavand, Behzad; Mahdavi Javid, Kimya; Gharagozlou, Mehrnaz

2013-01-01

Highlights: ► Preparation of epoxy polysulfide nanocomposite. ► Multi-walled carbon nanotubes have been modified and dispersed in epoxy polysulfide matrix. ► Mechanical properties of MWNT/epoxy polysulfide have been studied. - Abstract: In this research, multi-walled carbon nanotubes (MWCNTs) were modified by acid functionalization (H 2 SO 4 :HNO 3 = 1:3 by volume) and then mechanical properties of reinforced epoxy polysulfide resin by the both pure and treated MWNTs have been evaluated. For achieving this goal, different weight percentages of pure and treated MWCNT (0.1–0.3 wt%) were dispersed in the epoxy polysulfide resin separately and then mixed with curing agent. Experimental results have shown significant difference between acid treated and untreated MWCNTs in mechanical properties of epoxy polysulfide nanocomposites. In nanocomposite with 0.1–0.3% acid treated MWCNTs we observed increase of Young’s modulus from 458 to 723 MPa, tensile strength from 5.29 to 8.83 MPa and fracture strain from 0.16% to 0.25%. For understanding the structure and morphology of nanocomposite, the dispersion states were studied using scanning electron microscopy (SEM) and field emission electron microscopy (FESEM). The results showed better dispersion of modified carbon nanotube than unmodified in polymeric matrix

Study by dynamic light scattering of an o/w emulsion of an epoxi resin dispersed in water by means of a triblock copolymer of type PEO-PPO-PEO

International Nuclear Information System (INIS)

Uscanga, E. H.; Rio, J. M. del; Avendano-Gomez, J. R.

2009-01-01

The curing epoxy resins are widely used in various fields of chemical industry, such as adhesives, automotive, coatings, etc. The process operation consisting of flow and mixing of epoxy resins become difficult due to their high viscosity. One solution is to dissolve the epoxy resin in volatile organic solvents (VOS) such as toluene, xylene or benzene. However, the use of VOS is not only expensive but harmful to the environment. (Author)

Thermal and mechanical interfacial properties of epoxy composites based on functionalized carbon nanotubes

International Nuclear Information System (INIS)

Jin Fanlong; Ma Changjie; Park, Soo-Jin

2011-01-01

Highlights: → CNTs were functionalized by acid and amine treatments. → Epoxy resin/CNT composites were prepared. → T g of the composites increased by about 10 deg. C compared to neat epoxy resins. → Toughness of the composites was significantly improved by the addition of functionalized CNTs. - Abstract: Carbon nanotubes (CNTs) were treated by a mixture of acid and functionalized subsequently by amine treatment to improve interfacial interactions and dispersion of CNTs in epoxy matrix. The thermal stabilities and mechanical interfacial properties of epoxy/CNT composites were investigated using several techniques. The dispersion state of CNTs in the epoxy matrix was observed by scanning electron microscope (SEM) and transmission electron microscopy (TEM). As a result, the glass transition temperature of epoxy/CNT composites increased by about 11 deg. C compared to neat epoxy resins. The mechanical interfacial property of the composites was significantly increased by the addition of amine treated CNTs. The SEM and TEM results showed that the separation and uniform dispersion of CNTs in the epoxy matrix.

Kevlar 49/Epoxy COPV Aging Evaluation

Science.gov (United States)

Sutter, James K.; Salem, Jonathan L.; Thesken, John C.; Russell, Richard W.; Littell, Justin; Ruggeri, Charles; Leifeste, Mark R.

2008-01-01

NASA initiated an effort to determine if the aging of Kevlar 49/Epoxy composite overwrapped pressure vessels (COPV) affected their performance. This study briefly reviews the history and certification of composite pressure vessels employed on NASA Orbiters. Tests to evaluate overwrap tensile strength changes compared 30 year old samples from Orbiter vessels to new Kevlar/Epoxy pressure vessel materials. Other tests include transverse compression and thermal analyses (glass transition and moduli). Results from these tests do not indicate a noticeable effect due to aging of the overwrap materials.

The microwave absorbing properties of SmCo attached single wall carbon nanotube/epoxy composites

International Nuclear Information System (INIS)

Yu, Liming; Li, Bo; Sheng, Leimei; An, Kang; Zhao, Xinluo

2013-01-01

Highlights: •The SmCo nanoparticles attached SWCNTs were prepared by dc arc discharge method. •The nano-composite prepared by a rare earth permanent magnet Sm 2 Co 17 as catalyst. •The SmCo attached SWCNT/epoxy composites have an excellent electromagnetic matching characteristics. •The reflection loss and bandwidth below −20 dB of the composite can reach −23.7 dB, 6.2 GHz, respectively. -- Abstract: The SmCo nanoparticles attached single wall carbon nanotubes (SmCo attached SWCNTs) were prepared by hydrogen dc arc discharge method using 2:17 type SmCo permanent powder as catalyst. The SmCo attached SWCNT/epoxy composites with different doping ratios were investigated in the frequency region of 2–18 GHz. The complex permittivity and permeability of the SmCo attached SWCNT/epoxy composites were calculated. The reflection loss properties were simulated by transmission line theory and the microwave absorptive mechanisms were discussed. The results indicate that, due to the better interfacial polarization absorption mechanism of SmCo attached SWCNTs and the electromagnetic (EM) matching of magnetic loss and dielectric loss, the microwave absorption properties of SmCo attached SWCNT/epoxy are evidently improved. When the SmCo attached SWCNTs is doped by 1 wt%, the composite display a larger and wider absorption peak, and the bandwidth of the reflection loss below −20 dB is larger than 6 GHz with the thickness of 3.3 mm. It is expected that the new SmCo attached SWCNT/epoxy composites will be a good microwave absorbing material for the applications in X band, Ku band, or even K band

Phenolation of vegetable oils

Directory of Open Access Journals (Sweden)

ZORAN S. PETROVIĆ

2011-04-01

Full Text Available Novel bio-based compounds containing phenols suitable for the syn­thesis of polyurethanes were prepared. The direct alkylation of phenols with different vegetable oils in the presence of superacids (HBF4, triflic acid as ca­talysts was studied. The reaction kinetics was followed by monitoring the de­crease of the double bond content (iodine value with time. In order to under­stand the mechanism of the reaction, phenol was alkylated with model com­pounds. The model compounds containing one internal double bond were 9-oc­tadecene and methyl oleate and those with three double bonds were triolein and high oleic safflower oil (82 % oleic acid. It was shown that the best structures for phenol alkylation are fatty acids with only one double bond (oleic acid. Fatty acids with two double bonds (linoleic acid and three double bonds (lino­lenic acid lead to polymerized oils by a Diels–Alder reaction, and to a lesser extent to phenol alkylated products. The reaction product of direct alkylation of phenol with vegetable oils is a complex mixture of phenol alkylated with poly­merized oil (30–60 %, phenyl esters formed by transesterification of phenol with triglyceride ester bonds (<10 % and unreacted oil (30 %. The phenolated vegetable oils are new aromatic–aliphatic bio-based raw materials suitable for the preparation of polyols (by propoxylation, ethoxylation, Mannich reactions for the preparation of polyurethanes, as intermediates for phenolic resins or as bio-based antioxidants.

Surface modification of titanium hydride with epoxy resin via microwave-assisted ball milling

International Nuclear Information System (INIS)

Ning, Rong; Chen, Ding; Zhang, Qianxia; Bian, Zhibing; Dai, Haixiong; Zhang, Chi

2014-01-01

Highlights: • TiH 2 was modified with epoxy resin by microwave-assisted ball milling. • The epoxy ring was opened under the coupling effect of microwave and ball milling. • Microwave-assisted ball milling improved the compatibility of TiH 2 with epoxy. - Abstract: Surface modification of titanium hydride with epoxy resin was carried out via microwave-assisted ball milling and the products were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), thermo-gravimetry (TG) and Fourier transform infrared spectroscopy (FT-IR). A sedimentation test was performed to investigate the compatibility of the modified nano titanium hydride with the epoxy resin. The results show that the epoxy resin molecules were grafted on the surface of nano titanium hydride particles during the microwave-assisted ball milling process, which led to the improvement of compatibility between the nanoparticles and epoxy resin. According to the FT-IR, the grafting site was likely to be located around the epoxy group due to the fact that the epoxy ring was opened. However, compared with microwave-assisted ball milling, the conventional ball milling could not realize the surface modification, indicating that the coupling effect of mechanical force and microwave played a key role during the process

Toughening Effect of Microscale Particles on the Tensile and Vibration Properties of S-Glass-Fiber-Reinforced Epoxy Composites

Science.gov (United States)

Erkliğ, A.; Bulut, M.; Fayzulla, B.

2018-03-01

The effect of borax, sewage sludge ash, silicon carbide, and perlite microparticles on the tensile, damping, and vibration characteristics of S-glass/epoxy composite laminates was examined Their damping and vibration properties were evaluated experimentally by using the dynamic modal analysis, identifying the response of the fundamental natural frequency to the type and weight content of the particulates. The results obtained showed that the introduction of specific amounts of such particulates into the matrix of S-glass/epoxy composite noticeably improved its mechanical properties.

Epoxy based nanocomposites with fully exfoliated unmodified clay: mechanical and thermal properties.

Science.gov (United States)

Li, Binghai; Zhang, Xiaohong; Gao, Jianming; Song, Zhihai; Qi, Guicun; Liu, Yiqun; Qiao, Jinliang

2010-09-01

The unmodified clay has been fully exfoliated in epoxy resin with the aid of a novel ultrafine full-vulcanized powdered rubber. Epoxy/rubber/clay nanocomposites with exfoliated morphology have been successfully prepared. The microstructures of the nanocomposites were characterized by means of X-ray diffraction and transmission electron microscopy. It was found that the unmodified clay was fully exfoliated and uniformly dispersed in the resulting nanocomposite. Characterizations of mechanical properties revealed that the impact strength of this special epoxy/rubber/clay nanocomposite increased up 107% over the neat epoxy resin. Thermal analyses showed that thermal stability of the nanocomposite was much better than that of epoxy nanocomposite based on organically modified clay.

Los cambios de temperatura en los revestimientos epoxi II

Directory of Open Access Journals (Sweden)

Fernández Cánovas, M.

1970-04-01

Full Text Available This article is the second part of a previous paper published by the author in no. 189 of this magazine. It describes the tests carried out to check the theoretical results published in the earlier article. The tests have consisted in submitting concrete slabs covered with a layer of epoxi mortar to certain thermal conditions, to check the behaviour of the covering in the face of thermal changes. In all the tests, described in detail in the article, the epoxi layer has behaved extremely well, and no bonding failure has been observed, nor failures in the concrete base or in the epoxi layer.Este artículo es la segunda parte de un trabajo publicado por el autor en el número 189 de esta revista, y en él se realiza una descripción de los ensayos prácticos llevados a cabo para complementar el estudio teórico publicado en aquella primera parte. Los ensayos han consistido en someter a placas de hormigón revestidas de una Kipa de mor tero epoxi a determinadas condiciones térmicas, con el fin de poder comprobar el comportamiento del revestimiento frente a los cambios de temperatura. En todos los ensayos realizados y que, con detalle, están descritos en este artículo, el comportamiento de los revestimientos de mortero epoxi ha sido excelente, no habiéndose notado ningún fallo de adherencia, ni roturas en la base de hormigón, ni en la capa de mortero epoxi.

Energy absorption and failure response of silk/epoxy composite square tubes: Experimental

DEFF Research Database (Denmark)

Oshkovr, Simin Ataollahi; Taher, Siavash Talebi; A. Eshkoor, Rahim

2012-01-01

This paper focuses on natural silk/epoxy composite square tubes energy absorption and failure response. The tested specimens were featured by a material combination of different lengths and same numbers of natural silk/epoxy composite layers in form of reinforced woven fabric in thermosetting epoxy...

Measurements of print-through in graphite fiber epoxy composites

Science.gov (United States)

Jaworske, Donald A.; Jeunnette, Timothy T.; Anzic, Judith M.

1989-01-01

High-reflectance accurate-contour mirrors are needed for solar dynamic space power systems. Graphite fiber epoxy composites are attractive candidates for such applications owing to their high modulus, near-zero coefficient of thermal expansion, and low mass. However, mirrors prepared from graphite fiber epoxy composite substrates often exhibit print-through, a distortion of the surface, which causes a loss in solar specular reflectance. Efforts to develop mirror substrates without print-through distortion require a means of quantifying print-through. Methods have been developed to quantify the degree of print-through in graphite fiber epoxy composite specimens using surface profilometry.

Characterization of epoxy hybrid composites filled with cellulose fibers and nano-SiC

KAUST Repository

Alamri, H.

2012-04-06

Three different approaches have been applied and investigated to enhance the thermal and mechanical properties of epoxy resin. Epoxy system reinforced with either recycled cellulose fibers (RCF) or nanosilicon carbide (n-SiC) particles as well as with both RCF and n-SiC has been fabricated and investigated. The effect of RCF/n-SiC dispersion on the mechanical and thermal properties of these composites has been characterized. The fracture surface morphology and toughness mechanisms were investigated by scanning electron microscopy. The dispersion of n-SiC particles into epoxy nanocomposites was studied by synchrotron radiation diffraction and transmission electron microscopy. Results indicated that mechanical properties increased as a result of the addition of n-SiC. The presence of RCF layers significantly increased the mechanical properties of RCF/epoxy composites when compared with neat epoxy and its nanocomposites. The influence of the addition of n-SiC to RCF/epoxy composites in mechanical properties was found to be positive in toughness properties. At high temperatures, thermal stability of neat epoxy increased due to the presence of either n-SiC particles or RCF layers. However, the presence of RCF accelerated the thermal degradation of neat epoxy as well as the addition of n-SiC to RCF/epoxy samples increased the rate of the major thermal degradation. © 2012 Wiley Periodicals, Inc.

ORGANIC/INORGANIC HYBRID EPOXY NANOCOMPOSITES BASED ON OCTA(AMINOPHENYL)SILSESQUIOXANE

Institute of Scientific and Technical Information of China (English)

Hai-bo Fan; Rong-jie Yang; Xiang-mei Li

2013-01-01

Octa(aminophenyl)silsesquioxane (OAPS) was used as the curing agent of diglycidyl ether of bisphenol-A (DGEBA) epoxy resin.A study on comparison of DGEBA/OAPS with DGEBA/4,4'-diaminodiphenyl sulfone (DDS) epoxy resins was achieved.Differential scanning calorimetry was used to investigate the curing reaction and its kinetics,and the glass transition of DGEBA/OAPS.Thermogravimetric analysis was used to investigate thermal decomposition of the two kinds of epoxy resins.The reactions between amino groups and epoxy groups were investigated using Fourier transform infrared spectroscopy.Scanning electron microscopy was used to observe morphology of the two epoxy resins.The results indicated that OAPS had very good compatibility with DGEBA in molecular level,and could form a transparent DGEBA/OAPS resin.The curing reaction of the DGEBA/OAPS prepolymer could occur under low temperatures compared with DGEBA/DDS.The DGEBA/OAPS resin didn't exhibit glass transition,but the DGEBA/DDS did,which meant that the large cage structure of OAPS limited the motion of chains between the cross-linking points.Measurements of the contact angle indicated that the DGEBA/OAPS showed larger angles with water than the DGEBA/DDS resin.Thermogravimetric analysis indicated that the incorporation of OAPS into epoxy system resulted in low mass loss rate and high char yield,but its initial decomposition temperature seemed to be lowered.

Exit Presentation: Infrared Thermography on Graphite/Epoxy

Science.gov (United States)

Comeaux, Kayla

2010-01-01

This slide presentation reports on the internship project that was accomplished during the summer of 2010. The objectives of the project were to: (1) Simulate Flash Thermography on Graphite/Epoxy Flat Bottom hole Specimen and thin void specimens, (2) Obtain Flash Thermography data on Graphite/Epoxy flat bottom hole specimens, (3) Compare experimental results with simulation results, Compare Flat Bottom Hole Simulation with Thin Void Simulation to create a graph to determine size of IR Thermography detected defects

CNTs, Al2O3 and SiO2 Reinforced Epoxy: Tribological Properties of Polymer Nanocomposites

Directory of Open Access Journals (Sweden)

M.A. Ramadan,

2017-09-01

Full Text Available The present work studied the effect of filling epoxy matrix by different types and concentrations of nanoparticles on the friction and wear behaviors. Various concentrations (0.2 %, 0.4 %, 0.6 %, 0.8 % and 1 wt.% of multi walled carbon nano tubes (MWCNTs, aluminum oxide (Al2O3, and silica (SiO2 nanoparticles were used to reinforce epoxy matrix. These epoxy nanocomposites are widely used as indoor flooring tiles in schools, boutiques, hospitals, offices, conference rooms, homes, trade fair stands and homes for the aged. Experiments involved sliding of the epoxy nanocomposite specimens against rotating steel disc at dry sliding condition. Experiments were carried out using a test rig of pin-on-disc, designed and manufactured for the test. The friction force was measured using load cell which connected with a digital screen to detect the friction force. All experiments were done at room temperature and carried out at constant normal load (7 N, constant speed (0.93 m/sec and constant running time (300 seconds. The worn surfaces were investigated with back scattered scanning electron microscopy (SEM. Based on the observations in the present work, it was found that addition of the tested filling nanoparticles have greatly affected the friction and highly improves wear resistance.

Bio-phenolic resin from oil palm empty fruit bunches

Science.gov (United States)

Zakaria, Zuhaili; Zakaria, Sarani; Roslan, Rasidi; Chia, Chin Hua; Jaafar, Sharifah Nabihah Syed; Amran, Umar Adli

2018-04-01

Utilization of oil palm empty fruit bunches (EFB) in the production of bio-phenolic resin is an alternative way to reduce the dependency of petroleum-based phenol. In this study, resol type bio-phenolic resin (BPR) was synthesized from EFB fibers using sulfuric acid as the catalyst to produce liquefied empty fruit bunches (LEFB) followed by resinification reaction with formaldehyde in alkaline condition. The SEM image of LEFB residue showed separation of fiber bundles into individual fibers. This indicate that lignin was destroyed during the liquefaction process. The increased of formaldehyde/LEFB molar ratio has resulted an increase of viscosity, solid content and pH of the resin. The obtained FTIR spectra confirmed that functional groups of BPR resins was almost similar with commercial resin.

Synthesis and characterization of polyimide-epoxy hybrid films

International Nuclear Information System (INIS)

Butt, M.S.; Akhter, Z.; Siddiqi, H.M.

2011-01-01

Composites from polyimide and epoxy-amine were prepared aiming for enhancing its thermal and mechanical properties. Polyimide-epoxy-amine hybrid films were prepared by blending of polyimide and epoxy-amine in different ratios whereas, polyimide was prepared by reacting 1,2-di(p-aminophenyloxy)ethylene with 3,3/sub '/4,4/sub '/-benzophenone tetracarboxylic acid dianhydride. The blend systems with Araldite LY564 (1,4-butanediolediglycidyl ether) (BDDE) and Hardener HY2954 (3,3/sub '/-dimethyl-4,4/sub '/-diamino dicyclohexyl)methane (MACM) were investigated in term of thermal, mechanical and viscoelastic measurements. Thermal stability was determined using thermogravimetric analysis. The effect of the polyimide content on the glass transition temperature (Tg) and thermal stability was observed. Viscoelastic measurements showed that the glass transition temperature shifted with the increase of polyimide content. The composites showed higher thermal stability in comparison with neat epoxy-amine matrix for higher polyimide concentration. The effect of polyimide content on the mechanical properties was also investigated. The tensile measurements of the films showed that with the increase of polyimide content the tensile modulus of the films was increased. (author)

Intrinsic Flame-Retardant and Thermally Stable Epoxy Endowed by a Highly Efficient, Multifunctional Curing Agent

Directory of Open Access Journals (Sweden)

Chunlei Dong

2016-12-01

Full Text Available It is difficult to realize flame retardancy of epoxy without suffering much detriment in thermal stability. To solve the problem, a super-efficient phosphorus-nitrogen-containing reactive-type flame retardant, 10-(hydroxy(4-hydroxyphenylmethyl-5,10-dihydrophenophosphazinine-10-oxide (HB-DPPA is synthesized and characterized. When it is used as a co-curing agent of 4,4′-methylenedianiline (DDM for curing diglycidyl ether of bisphenol A (DGEBA, the cured epoxy achieves UL-94 V-0 rating with the limiting oxygen index of 29.3%. In this case, the phosphorus content in the system is exceptionally low (0.18 wt %. To the best of our knowledge, it currently has the highest efficiency among similar epoxy systems. Such excellent flame retardancy originates from the exclusive chemical structure of the phenophosphazine moiety, in which the phosphorus element is stabilized by the two adjacent aromatic rings. The action in the condensed phase is enhanced and followed by pressurization of the pyrolytic gases that induces the blowing-out effect during combustion. The cone calorimeter result reveals the formation of a unique intumescent char structure with five discernible layers. Owing to the super-efficient flame retardancy and the rigid molecular structure of HB-DPPA, the flame-retardant epoxy acquires high thermal stability and its initial decomposition temperature only decreases by 4.6 °C as compared with the unmodified one.

Influence of the particle size of activated mineral carbon on the phenol and chlorophenol adsorption

International Nuclear Information System (INIS)

Garcia M, A.

2001-01-01

Water pollution by phenolic compounds is a problem that requires a solution since these phenolic compounds are not completely biodegradable, they accumulate through the food chains and they are quite toxic when enter in contact with living organisms. In human beings, ingestion or contact of the skin with this type of compounds produces irritation and damages mainly to the liver and kidneys. In fact, the Environmental Protection Agency of the United States (EPA assigned nine phenolic compounds among the 275 most toxic substances in 1991. Phenols are found in wastewater from agriculture and industry, because phenolic compounds are used as pesticides and in diverse industrial activities. The treatment of this type of water is not simple because they are generally composed of a mixture of residuals with different chemical nature A useful method for the removal of phenols is the adsorption by activated carbon, since this material has a great surface area and it can be regenerated. The adsorption process depends, among other factors, on the activated carbon characteristics. When they are modified, their capacity to remove pollutants from the water changes. The effect of activated carbon particle size on the removal of phenolic compounds has not been completely studied. Therefore, the aim of this work was to determine the influence of the mineral activated carbon particle size on the phenol and 4-chloro phenol adsorption in aqueous solution, on adsorption column system. The results of the present work indicate that the mineral activated carbon particle size has a very important influence on the adsorption of phenol and 4-chloro phenol. When the particles were smaller, the retention quantities of phenol and 4-chloro phenol increased. This behavior was related to the particle characteristics of the mineral activated carbon such as surface area and pore volume, while other factors such as elementary composition of the activated carbon did not influence the adsorption process

Characterization of Hybrid Epoxy Nanocomposites

Science.gov (United States)

Simcha, Shelly; Dotan, Ana; Kenig, Samuel; Dodiuk, Hanna

2012-01-01

This study focused on the effect of Multi Wall Carbon Nanotubes (MWCNT) content and its surface treatment on thermo-mechanical properties of epoxy nanocomposites. MWCNTs were surface treated and incorporated into two epoxy systems. MWCNT's surface treatments were based on: (a) Titania coating obtained by sol-gel process and (b) a nonionic surfactant. Thermo-mechanical properties improvement was obtained following incorporation of treated MWCNT. It was noticed that small amounts of titania coated MWCNT (0.05 wt %) led to an increase in the glass transition temperature and stiffness. The best performance was achieved adding 0.3 wt % titania coated MWCNT where an increase of 10 °C in the glass transition temperature and 30% in storage modulus were obtained. PMID:28348313

Thermal properties and corrosion resistance of organoclay/epoxy resin film

Science.gov (United States)

Baiquni, M.; Soegijono, B.

2018-03-01

Hybrid materials organoclay/epoxy resin films were prepared by varying organoclay content in epoxy resin as a matrix. The film were investigated by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and thermal conductivity. TGA and FT-IR results confirmed that the melting temperature shifted to a lower point. The thermal conductivity and corrosion resistant generally increase with increasing organoclay content. The changes on these properties may due to cross link between organoclay and epoxy.

Preparation and Various Characteristics of Epoxy/Alumina Nanocomposites

Science.gov (United States)

Kozako, Masahiro; Ohki, Yoshimichi; Kohtoh, Masanori; Okabe, Shigemitsu; Tanaka, Toshikatsu

Epoxy/ alumina nanocomposites were newly prepared by dispersing 3, 5, 7, and 10 weight (wt) % boehmite alumina nanofillers in a bisphenol-A epoxy resin using a special two-stage direct mixing method. It was confirmed by scanning electron microscopy imaging that the nanofillers were homogeneously dispersed in the epoxy matrix. Dielectric, mechanical, and thermal properties were investigated. It was elucidated that nanofillers affects various characteristics of epoxy resins, when they are nanostructrued. Such nano-effects we obtained are summarized as follows. Partial discharge resistance increases as the filler content increases; e.g. 7 wt% nanofiller content creates a 60 % decrease in depth of PD-caused erosion. Weibull analysis shows that short-time electrical treeing breakdown time is prolonged to 265 % by 5 wt% addition of nanofillers. But there was more data scatter in nanocomposites than in pure epoxy. Permittivity tends to increase from 3.7 to 4.0 by 5 wt% nanofiller addition as opposed to what was newly found in the recent past. Glass transition temperature remains unchanged as 109 °C. Mechanical properties such as flexural strength and flexural modulus increase; e.g. flexural strength and flexural modulus are improved by 5 % and 8 % with 5 wt% content, respectively. Excess addition causes a reverse effect. It is concluded from permittivity and glass transition temperature characteristics that interfacial bonding seems to be more or less weak in the nanocomposite specimens prepared this time, even though mechanical strengths increase. There is a possibility that the nanocomposites specimens will be improved in interfacial quality.

Liquid crystalline epoxy nanocomposite material for dental application.

Science.gov (United States)

Tai, Yun-Yuan; Hsu, Sheng-Hao; Chen, Rung-Shu; Su, Wei-Fang; Chen, Min-Huey

2015-01-01

Novel liquid crystalline epoxy nanocomposites, which exhibit reduced polymerization shrinkage and effectively bond to tooth structures, can be applied in esthetic dentistry, including core and post systems, direct and indirect restorations, and dental brackets. The purposes of this study were to investigate the properties of liquid crystalline epoxy nanocomposites including biocompatibility, microhardness, and frictional forces of bracket-like blocks with different filler contents for further clinical applications. In this study, we evaluated liquid crystalline epoxy nanocomposite materials that exhibited various filler contents, by assessing their cell activity performance using a 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide assay and their microhardness with or without thermocycling. We also evaluated the frictional force between bracket-like duplicates and commercially available esthetic bracket systems using Instron 5566. The liquid crystalline epoxy nanocomposite materials showed good biocompatibility. The materials having high filler content demonstrated greater microhardness compared with commercially available bracket materials, before and after the thermocycling treatment. Thus, manufacturing processes are important to reduce frictional force experienced by orthodontic brackets. The microhardness of the bracket-like blocks made by our new material is superior to the commercially available brackets, even after thermocycling. Our results indicate that the evaluated liquid crystalline epoxy nanocomposite materials are of an appropriate quality for application in dental core and post systems and in various restorations. By applying technology to refine manufacturing processes, these new materials could also be used to fabricate esthetic brackets for orthodontic treatment. Copyright © 2014. Published by Elsevier B.V.

The effects of MWNT on thermal conductivity and thermal mechanical properties of epoxy

Science.gov (United States)

Ismadi, A. I.; Othman, R. N.

2017-12-01

Multiwall nanotube (MWNT) was used as filler in various studies to improve thermal conductivity and mechanical properties of epoxy. Present study varied different weight loading (0, 0.1 %, 0.5 %, 1 %, 1.5 %, 3 % and 5 %) of MWNT in order to observe the effects on the epoxy. Nanocomposite was analyzed by dynamic-mechanical thermal analyser (DMTA) and KD2 pro analyzer. DMTA measured storage modulus (E') and glass transition temperature (Tg) of the nanocomposite. Result showed that Tg value of neat epoxy is higher than all MWNT epoxy nanocomposite. Tg values drop from 81.55 °C (neat epoxy) to 65.03 °C (at 0.1 wt%). This may happen due to the agglomeration of MWNT in the epoxy. However, Tg values increases with the increase of MWNT wt%. Tg values increased from 65.03 °C to 78.53 °C at 1 wt%. Increment of storage modulus (E') at 3 °C (glassy region) was observed as the MWNT loading increases. Maximum value of E' during glassy region was observed to be at 5 wt% with (7.26±0.7) E+08 Pa compared to neat epoxy. On the contrary, there is slight increased and slight decreased with E' values at 100 °C (rubbery region) for all nanocomposite. Since epoxy exhibits low thermal conductivity properties, addition of MWNT has enhanced the properties. Optimum value of thermal conductivity was observed at 3 wt%. The values increased up to 9.03 % compared to neat epoxy. As expected, the result showed decrease value in thermal conductivity at 5 wt% as a result of agglomeration of MWNT in the epoxy.

High Tg and fast curing epoxy-based anisotropic conductive paste for electronic packaging

Science.gov (United States)

Keeratitham, Waralee; Somwangthanaroj, Anongnat

2016-03-01

Herein, our main objective is to prepare the fast curing epoxy system with high glass transition temperature (Tg) by incorporating the multifunctional epoxy resin into the mixture of diglycidyl ether of bisphenol A (DGEBA) as a major epoxy component and aromatic diamine as a hardener. Furthermore, the curing behavior as well as thermal and thermomechanical properties were investigated by differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA) and thermomechanical analysis (TMA). It was found that Tg obtained from tan δ of DGEBA/aromatic diamine system increased from 100 °C to 205 °C with the presence of 30 percentage by weight of multifunctional epoxy resin. Additionally, the isothermal DSC results showed that the multifunctional epoxy resin can accelerate the curing reaction of DGEBA/aromatic diamine system. Namely, a high degree of curing (˜90%) was achieved after a few minutes of curing at low temperature of 130 °C, owing to a large number of epoxy ring of multifunctional epoxy resin towards the active hydrogen atoms of aromatic diamine.

Comparative evaluation of in vitro mechanical properties of different designs of epoxy-pin external skeletal fixation systems.

Science.gov (United States)

Tyagi, Surbhi Kuldeep; Aithal, Hari Prasad; Kinjavdekar, Prakash; Amarpal; Pawde, Abhijit Motiram; Srivastava, Tuhin; Tyagi, Kanti Prakash; Monsang, Shongsir Warson

2014-03-01

To compare in vitro biomechanical properties of different designs of epoxy-pin external skeletal fixator (ESF) constructs. Mechanical testing study. Four epoxy-pin ESF design constructs (uniplanar [EU], multiplanar-I [EM-I], multiplanar-II [EM-II], and circular [EC]) were mechanically tested in compression, bending, and torsion. Four different designs of free-form epoxy-pin external fixator constructs were developed using 1.5 mm K-wires and epoxy resin mounted in an ultra-high density polyethylene rod (20 mm diameter). Three-point fixation was done in each fragment, and the distance between fixation wires, and between the rod and the side bars was kept constant in all the designs. A 5 mm gap was maintained at the center of the fixation rod to simulate an unstable fracture condition. The fixator constructs (n = 12 of each design) were subjected to mechanical testing in axial compression, bending, or torsion. Load-deformation curves were generated and mechanical properties were compared between construct types. EU was the weakest design. Under compression, constructs EM-I, EM-II, and EC were similar. Under bending, EM-I and EM-II had similar strength, whereas EC was strongest. Under torsion, EC was strongest, followed by EM-II, EM-I, and EU; EM-II provided double the rotational stability of EM-I. Overall, EC followed by EM-II epoxy-pin fixator designs had better mechanical strength. © Copyright 2014 by The American College of Veterinary Surgeons.

Non-isothermal cure and exfoliation of tri-functional epoxy-clay nanocomposites

Directory of Open Access Journals (Sweden)

F. Shiravand

2015-08-01

Full Text Available The non-isothermal cure kinetics of polymer silicate layered nanocomposites based on a tri-functional epoxy resin has been investigated by differential scanning calorimetry. From an analysis of the kinetics as a function of the clay content, it can be concluded that the non-isothermal cure reaction can be considered to consist of four different processes: the reaction of epoxy groups with the diamine curing agent; an intra-gallery homopolymerisation reaction which occurs concurrently with the epoxy-amine reaction; and two extra-gallery homopolymerisation reactions, catalysed by the onium ion of the organically modified clay and by the tertiary amines resulting from the epoxy-amine reaction. The final nanostructure displays a similar quality of exfoliation as that observed for the isothermal cure of the same nanocomposite system. This implies that the intra-gallery reaction, which is responsible for the exfoliation, is not significantly inhibited by the extra-gallery epoxy-amine cross-linking reaction.

Tensile properties of compressed moulded Napier/glass fibre reinforced epoxy composites

Science.gov (United States)

Fatinah, T. S.; Majid, M. S. Abdul; Ridzuan, M. J. M.; Hong, T. W.; Amin, N. A. M.; Afendi, M.

2017-10-01

This paper describes the experimental investigation of the tensile properties of compressed moulded Napier grass fibres reinforced epoxy composites. The effect of treatment 5% sodium hydroxide (NaOH) concentrated solution and hybridization of Napier with CSM E-glass fibres on tensile properties was also studied. The untreated and treated Napier fibres with 25% fibre loading were fabricated with epoxy resin by a cold press process. 7% fibre loading of CSM glass fibre was hybrid as the skin layer for 18% fibre loading of untreated Napier grass fibre. The tensile tests were conducted using Universal Testing Machine in accordance with ASTM D638. The tensile properties of the untreated Napier/epoxy composites were compared with treated Napier/epoxy and untreated Napier/CSM/epoxy composites. The results demonstrated that the tensile performance of untreated Napier fibre composites was significantly improved by both of the modification; alkali treatment and glass fibre hybridization. Napier grass fibres showed promising potentials to be used as reinforcement in the polymer based composites.

Plant Oil-Derived Epoxy Polymers toward Sustainable Biobased Thermosets.

Science.gov (United States)

Wang, Zhongkai; Yuan, Liang; Ganewatta, Mitra S; Lamm, Meghan E; Rahman, Md Anisur; Wang, Jifu; Liu, Shengquan; Tang, Chuanbing

2017-06-01

Epoxy polymers (EPs) derived from soybean oil with varied chemical structures are synthesized. These polymers are then cured with anhydrides to yield soybean-oil-derived epoxy thermosets. The curing kinetic, thermal, and mechanical properties are well characterized. Due to the high epoxide functionality per epoxy polymer chain, these thermosets exhibit tensile strength over an order of magnitude higher than a control formulation with epoxidized soybean oil. More importantly, thermosetting materials ranging from soft elastomers to tough thermosets can be obtained simply by using different EPs and/or by controlling feed ratios of EPs to anhydrides. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Chemical changes and tensile and electrical properties of epoxy ...

African Journals Online (AJOL)

The properties of epoxy rsesin can be improved by the use of nanofiller such as carbon black (CB), The nanocomposite was synthesized by dispersion via sonication and shear mixing. The morphology, surface chemistry and the structure of CB and the epoxy/CB nanocomposites were investigated using XPS, FTIR, FESEM, ...

Education and Public Outreach for NASA's EPOXI Mission.

Science.gov (United States)

McFadden, Lucy-Ann A.; Crow, C. A.; Behne, J.; Brown, R. N.; Counley, J.; Livengood, T. A.; Ristvey, J. D.; Warner, E. M.

2009-09-01

NASA's EPOXI mission is reusing the Deep Impact (DI) flyby spacecraft to study comets and extra-solar planets around other stars. During the Extrasolar Planetary Observations and Characterization (EPOCh) phase of the mission extrasolar planets transiting their parent stars were observed to gain further knowledge and understanding of planetary systems. Observations of Earth also allowed for characterization of Earth as an extrasolar planet. A movie of a lunar transit of the Earth created from EPOCh images and links to existing planet finding activities from other NASA missions are available on the EPOXI website. The Deep Impact Extended Investigation (DIXI) continues the Deep Impact theme of investigating comet properties and formation by observing comet Hartley 2 in November 2010. The EPOXI Education and Public Outreach (E/PO) program is both creating new materials and updating and modifying existing Deep Impact materials based on DI mission results. Comparing Comets is a new educational activity under development that will guide students in conducting analyses of comet surface features similar to those the DIXI scientists will perform after observing comet Hartley 2. A new story designed to stimulate student creativity was developed in alignment with national educational standards. EPOXI E/PO also funded Family Science Night (FSN), a program bringing together students, families, and educators for an evening at the National Air and Space Museum in Washington, DC. FSN events include time for families to explore the museum, a presentation by a space scientist, and an astronomy themed IMAX film. Nine events were held during the 2008-2009 school year with a total attendance of 3,145 (attendance since inception reached 44,732). Half of attendance is reserved for schools with high percentages of underrepresented minorities. EPOXI additionally offers a bi-monthly newsletter to keep the public, teachers, and space enthusiasts updated on current mission activities. For more

The regulation by phenolic compounds of soil organic matter dynamics under a changing environment.

Science.gov (United States)

Min, Kyungjin; Freeman, Chris; Kang, Hojeong; Choi, Sung-Uk

2015-01-01

Phenolics are the most abundant plant metabolites and are believed to decompose slowly in soils compared to other soil organic matter (SOM). Thus, they have often been considered as a slow carbon (C) pool in soil dynamics models. Here, however, we review changes in our concept about the turnover rate of phenolics and quantification of different types of phenolics in soils. Also, we synthesize current research on the degradation of phenolics and their regulatory effects on decomposition. Environmental changes, such as elevated CO2, warming, nitrogen (N) deposition, and drought, could influence the production and form of phenolics, leading to a change in SOM dynamics, and thus we also review the fate of phenolics under environmental disturbances. Finally, we propose the use of phenolics as a tool to control rates of SOM decomposition to stabilize organic carbon in ecosystems. Further studies to clarify the role of phenolics in SOM dynamics should include improving quantification methods, elucidating the relationship between phenolics and soil microorganisms, and determining the interactive effects of combinations of environmental changes on the phenolics production and degradation and subsequent impact on SOM processing.

Aging in CTBN modified epoxy resin stocks

International Nuclear Information System (INIS)

Creed, K.E. Jr.

1979-01-01

The cause of degradation in the glass transition temperature (T/sub G/) of a partially crystallized polymer was investigated. Sample epoxy resin filled capacitors were cured at 90 0 C for 24 hours, then stored at room atmospheric conditions. These showed typical degradation in T/sub G/ after storage for one month. One set of epoxy resin castings was stored at room atmosphere and another set was stored in a dry box at 0% relative humidity and 27 0 C. The samples at room atmospheric conditions showed typical degradation in T/sub G/, while the T/sub G/ for those stored in the dry box increased. Further tests were then made on epoxy resin castings at various curing temperatures and times at both room atmosphere and 0% humidity. Resulting data indicated that absorption of moisture during storage was the predominant cause of T/sub G/ degradation, with stress relaxation another, though smaller, contributing factor

Spall Strength Measurements in Transparent Epoxy Polymers

Science.gov (United States)

Pepper, Jonathan; Rahmat, Meysam; Petel, Oren

2017-06-01

Polymer nanocomposites are seeing more frequent use in transparent armour applications. The role of the microstructure on the performance of these materials under dynamic tensile loading conditions is of particular interest. In the present study, a series of plate impact experiments was conducted in order to evaluate the dynamic response of an epoxy (EPON 828) cured with two differed hardeners. The purpose was to compare the role of these hardeners on the dynamic performance of the resulting transparent epoxy. The material response was resolved with a multi-channel photonic Doppler velocimeter. This system was used to determine the shock Hugoniot and dynamic tensile (spall) strength of the materials. The experimental results are presented in reference to spall theory and are evaluated against results predicted by an analytical model of the impacts. While varying the hardener did not change the shock Hugoniot of the epoxy, it did have an effect on the measured spall strengths.

Epoxy-silicate nanocomposites: Cure monitoring and characterization

International Nuclear Information System (INIS)

Hussain, Farzana; Chen, Jihua; Hojjati, Mehdi

2007-01-01

Epoxy-clay nanocomposites were prepared with organically modified layered clay with varying clay contents (1-8 wt.%). Neat resin and nanocomposite were characterized using different techniques. At first, the effect of nanoclay concentration on the cure behaviour was investigated using an on-line dielectric cure monitoring technique. Differential scanning calorimetry (DSC) was used to verify the dielectric measurement results. Furthermore, mechanical and thermal properties were studied using tensile test and Dynamic Mechanical Analysis (DMA), respectively. Experimental results showed that properties of the epoxy were changed evidently because of the nanoclay loading. The tensile modulus of the nanocomposites increased by 47%, however, no improvement in tensile strength and glass transition temperature (T g ) was observed. Fracture surface of the tensile samples were analyzed by Scanning Electron Microscope (SEM). The nanocomposites structures were characterized with Wide Angle X-Ray Diffraction (WAXD) and Transmission Electron Microscopy (TEM), which revealed the intercalated morphology of clay layers in the epoxy resin systems

(Liquid + liquid) equilibrium of {water + phenol + (1-butanol, or 2-butanol, or tert-butanol)} systems

International Nuclear Information System (INIS)

Hadlich de Oliveira, Leonardo; Aznar, Martin

2010-01-01

(Liquid + liquid) equilibrium (LLE) and binodal curve data were determined for the systems (water + phenol + tert-butanol) at T = 298.15 K, (water + phenol + 2-butanol) and (water + phenol + 1-butanol) at T = 298.15 K and T = 313.15 K by the combined techniques of densimetry and refractometry. Type I curve (for tert-butanol) and Type II curves (for 1- and 2-butanol) were found. The data were correlated with the NRTL model and the parameters estimated present root mean square deviations below 2% for the system with tert-butanol and lower than 0.8% for the other systems.

Advances in extraction and analysis of phenolic compounds from plant materials

Institute of Scientific and Technical Information of China (English)

XU Cong-Cong; WANG Bing; PU Yi-Qiong; TAO Jian-Sheng; ZHANG Tong

2017-01-01

Phenolic compounds,the most abundant secondary metabolites in plants,have received more and more attention in recent years because of their distinct bioactivities.This review summarizes different types of phenolic compounds and their extraction and analytical methods used in the recent reports,involving 59 phenolic compounds from 52 kinds of plants.The extraction methods include solid-liquid extraction,ultrasound-assisted extractions,microwave-assisted extractions,supercritical fluid extraction,and other methods.The analysis methods include spectrophotometry,gas chromatography,liquid chromatography,thin-layer chromatography,capillary electrophoresis,and near-infrared spectroscopy.After illustrating the specific conditions of the analytical methods,the advantages and disadvantages of each method are also summarized,pointing out their respective suitability.This review provides valuable reference for identification and/or quantification of phenolic compounds from natural products.

Identification and characterization of phenol hydroxylase from phenol-degrading Candida tropicalis strain JH8.

Science.gov (United States)

Long, Yan; Yang, Sheng; Xie, Zhixiong; Cheng, Li

2014-09-01

The gene phhY encoding phenol hydroxylase from Candida tropicalis JH8 was cloned, sequenced, and expressed in Escherichia coli. The gene phhY contained an open reading frame of 2130 bp encoding a polypeptide of 709 amino acid residues. From its sequence analysis, it is a member of a family of flavin-containing aromatic hydroxylases and shares 41% amino acid identity with phenol hydroxylase from Trichosporon cutaneum. The recombinant phenol hydroxylase exists as a homotetramer structure with a native molecular mass of 320 kDa. Recombinant phenol hydroxylase was insensitive to pH treatment; its optimum pH was at 7.6. The optimum temperature for the enzyme was 30 °C, and its activity was rapidly lost at temperatures above 60 °C. Under the optimal conditions with phenol as substrate, the K(m) and V(max) of recombinant phenol hydroxylase were 0.21 mmol·L(-1) and 0.077 μmol·L(-1)·min(-1), respectively. This is the first paper presenting the cloning and expression in E. coli of the phenol hydroxylase gene from C. tropicalis and the characterization of the recombinant phenol hydroxylase.

Radiation curing of γ-Al2O3 filled epoxy resin

International Nuclear Information System (INIS)

Kang, Phil Hyun; Kim, Dong Jin; Nho, Young Chang

2003-01-01

Epoxy resins are widely utilized as high performance thermosetting resins for many industrial applications but characterized by a relatively low toughness. Recently, the incorporation with rigid inorganic was suggested to improve the mechanical properties of epoxy resins. In the present work, an attempt has been taken to disperse nano-sized γ- Al 2 O 3 particles into diglycidyl ether of bisphenol-A (DGEBA) epoxy resins for improvement of the mechanical properties. These hybrid epoxy-alumina composites were prepared using by the γ-ray curing technique that was conducted with 100kGy under nitrogen at room temperature. The composites were characterized by determining gel content, UTM (Instron model 4443), SEM, FT-IR studies

Preparations and applications in UV curing coatings of epoxy acrylates containing carboxyl

International Nuclear Information System (INIS)

Wu Yu Min

1999-01-01

This paper introduces preparations of epoxy acrylates containing carboxyl through the reactions of epoxy acrylates with butanedioic anhydride, pentanedioic anhydride, cis-butenedioic anhydride, phthalic anhydride, tetrabromophthalic anhydride and -tetrahydrophthalic anhydride. These epoxy acrylates containing carboxyl have been applied to UV-curing coatings and their effects on properties of UV-curing coatings have been studied

ANALISIS ARAH DAN PERLAKUAN SERAT TAPIS SERTA RASIO EPOXY HARDENER TERHADAP SIFAT FISIS DAN MEKANIS KOMPOSIT TAPIS/EPOXY

Directory of Open Access Journals (Sweden)

Putu Lokantara

2012-11-01

Full Text Available Tapis kelapa (Coconut filter as natural fiber, in this time its resources very copius but no longer be exploited and thrown off hand as waste though in fact its used for other material dissimilar inovatif and high economic valuable that is as one of natural fiber alternative to be composite. The objective of this research is to investigate the behavior changing of physical and mechanical properties of composite tapis kelapa as reinforcement and epoxy 7120 with hardener Versamid 140 as matrix. The fiber is treated with the chemical NaOH and KMnO4 with percentage 0.5%, 1%, and 2% in weight, respectively. The ratio of epoxy and hardener is 7:3 and 6:4, and fiber orientation 0o, 45o, dan 90o. For testing of the speciment in tensile test with ASTM standard D3039 and three point bending test with ASTM standard D790. The result of this research obtained that fiber treatment with KMnO4 give the better effect to machine properties compared to NaOH. Variation of percentage 0.5%, 1%, and 2% NaOH and KMnO4 give the effect in fiber surface which higher percentage make the cleaner of surface, decrease of wax contain, and roughness of fiber surface so that stronger of linkage of fiber and matrix and increase of tensile strength, bending strength, and bending modulus of the composite. The highest tensile strength, modulus of elasticity and bending strength are 70.23 MPa, 446.24 GPa and 97.81 MPa respectively reached at composite with ratio epoxy/hardener 7:3; by 2% KMnO4 and fiber orientation 45o. While the highest modulus of elasticity is 385.48 GPa reached at composite with the ratio epoxy/hardener 6:4; 2% KMnO4 and fiber orientation 90o. Keywords: Tensile Strength, bending strength, ratio of epoxy/hardener, NaOH, KMnO4

Multiligand Metal-Phenolic Assembly from Green Tea Infusions.

Science.gov (United States)

Rahim, Md Arifur; Björnmalm, Mattias; Bertleff-Zieschang, Nadja; Ju, Yi; Mettu, Srinivas; Leeming, Michael G; Caruso, Frank

2018-03-07

The synthesis of hybrid functional materials using the coordination-driven assembly of metal-phenolic networks (MPNs) is of interest in diverse areas of materials science. To date, MPN assembly has been explored as monoligand systems (i.e., containing a single type of phenolic ligand) where the phenolic components are primarily obtained from natural sources via extraction, isolation, and purification processes. Herein, we demonstrate the fabrication of MPNs from a readily available, crude phenolic source-green tea (GT) infusions. We employ our recently introduced rust-mediated continuous assembly strategy to prepare these GT MPN systems. The resulting hollow MPN capsules contain multiple phenolic ligands and have a shell thickness that can be controlled through the reaction time. These multiligand MPN systems have different properties compared to the analogous MPN systems reported previously. For example, the Young's modulus (as determined using colloidal-probe atomic force microscopy) of the GT MPN system presented herein is less than half that of MPN systems prepared using tannic acid and iron salt solutions, and the disassembly kinetics are faster (∼50%) than other, comparable MPN systems under identical disassembly conditions. Additionally, the use of rust-mediated assembly enables the formation of stable capsules under conditions where the conventional approach (i.e., using iron salt solutions) results in colloidally unstable dispersions. These differences highlight how the choice of phenolic ligand and its source, as well as the assembly protocol (e.g., using solution-based or solid-state iron sources), can be used to tune the properties of MPNs. The strategy presented herein expands the toolbox of MPN assembly while also providing new insights into the nature and robustness of metal-phenolic interfacial assembly when using solution-based or solid-state metal sources.

Epoxy-resin adhesive and method for bonding using such an epoxy resin adhesive

NARCIS (Netherlands)

Bhowmik, S.; Poulis, J.A.; Benedictus, R.

2008-01-01

The invention relates to an epoxy resin adhesive comprising a dotation of nano-substances, wherein the nano- substances are selected from the group comprising carbon-fibre nanotubes, carbon nano-fibres, silicate nano powders, and wherein the nano-substances are dispersed in the adhesive with a

Fracture toughness behaviour of carbon fibre epoxy composite with Kevlar reinforced interleave

International Nuclear Information System (INIS)

Yadav, S.N.; Kumar, Vijai; Verma, Sushil K.

2006-01-01

This work was to evaluate as to how mode II fracture toughness G II is affected by interleave having Kevlar fibre reinforcement in the fracture plane. Thermoset interleave and chopped Kevlar fibres were applied between the carbon/epoxy composite layers. An artificial crack starter was implanted in the mid-plane to initiate the fracture process. The following five different types of carbon fibre/epoxy composites were prepared and tested. (a) Base laminate without interleave (b) unreinforced interleave and (c) 0.5, 1.0 and 1.5 mg/cm 2 chopped Kevlar fibre reinforced interleave. Results obtained show that fracture toughness G IIC enhanced up to about two times in all the laminates. However, enhancement in fracture toughness G IIC was more effective in interleaved laminate than Kevlar reinforced interleaved because of large energy absorbing capabilities of interleaf. Mechanism of fracture and toughening were examined by using scanning electron microscope

Preparation and Properties of Epoxy Resin-Coated Micro-Sized Ferrosilicon Powder

OpenAIRE

Ku,Jiangang; Chen,Huihuang; He,Kui; Yan,Quanxiang

2016-01-01

Ferrosilicon powder surface coated with a dense epoxy resin membrane was prepared via coating precipitation methods using silane coupling agents as the modifier and epoxy resin as the coating agent. FTIR, FESEM, MPMS-XL, and TG-DSC were used to analyze the morphology, surface composition, magnetic property and thermostability of ferrosilicon powder before and after the modification and coating. The experimental results indicate that epoxy resin membranes of a certain thickness were successful...

Impact Damage In Carbon/Epoxy And Carbon/PEEK Composites

Science.gov (United States)

Nettles, A. T.; Magold, N. J.

1991-01-01

Report describes results of drop-weight impact testing of specimens of carbon-fiber/epoxy and carbon-fiber/polyetheretherketone (PEEK) composite materials. Panels made of these materials assembled into lightweight, strong, stiff structures useful in automobiles, aircraft, sporting goods, and many other products. PEEK specimens showed less delamination than epoxy specimens at given impact energy.

Phenolic Compounds in Brassica Vegetables

Directory of Open Access Journals (Sweden)

Pablo Velasco

2010-12-01

Full Text Available Phenolic compounds are a large group of phytochemicals widespread in the plant kingdom. Depending on their structure they can be classified into simple phenols, phenolic acids, hydroxycinnamic acid derivatives and flavonoids. Phenolic compounds have received considerable attention for being potentially protective factors against cancer and heart diseases, in part because of their potent antioxidative properties and their ubiquity in a wide range of commonly consumed foods of plant origin. The Brassicaceae family includes a wide range of horticultural crops, some of them with economic significance and extensively used in the diet throughout the world. The phenolic composition of Brassica vegetables has been recently investigated and, nowadays, the profile of different Brassica species is well established. Here, we review the significance of phenolic compounds as a source of beneficial compounds for human health and the influence of environmental conditions and processing mechanisms on the phenolic composition of Brassica vegetables.

Effect of epoxy resin and hardener containing microcapsules on healing efficiency of epoxy adhesive based metal joints

International Nuclear Information System (INIS)

Khan, Nazrul Islam; Halder, Sudipta; Goyat, M.S.

2016-01-01

Dual component microcapsules of epoxy resin and polyamine hardener with polymethyl methacrylate (PMMA) shell were synthesized using a water-oil-water emulsion solvent evaporation method. The high concentration of sodium dodecyl sulfate (SDS) was used to reduce the thickness of shell wall of dual component microcapsules. The dual microcapsules of 1:1 weight ratio were introduced in the epoxy adhesive to study the healing effect. The morphology, chemical structure and thermal characteristics of the microcapsules were characterized by scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA), respectively. The insertion of dual component microcapsules in epoxy matrix reduced the lap shear strength of adhesive joints, which may be attributed to the generation of stress concentration cites because of micron sized capsules. However, the extension and absorbed failure energy of adhesive joints under uniaxial loading increased with the increase of concentration of dual microcapsules. The viscoelastic nature of the dual microcapsules may be responsible for this enhancement. Significant enhancement in the healing efficiency (90.93%) of the joints was achieved for 10 wt% of dual microcapsules. The crack pinning and crack blunting mechanisms at the vicinity of the crack path adjacent to the microcapsules were found responsible for significant enhancement in the healing efficiency of the adhesive joints. - Highlights: • High SDS concentration was used to control the dual component microcapsules shell wall thickness. • Self-healing performance of dual component microcapsules reinforced epoxy adhesive based single lap joints was studied. • 90.93% of the damage healing was achieved for self-healing adhesive based single lap joints. • Increase in concentration of microcapsules reduces the lap shear properties of the self-healing joints.

Effect of epoxy resin and hardener containing microcapsules on healing efficiency of epoxy adhesive based metal joints

Energy Technology Data Exchange (ETDEWEB)

Khan, Nazrul Islam [Department of Mechanical Engineering, National Institute of Technology Silchar, Silchar 788010, Assam (India); Halder, Sudipta, E-mail: shalder@nits.ac.in [Department of Mechanical Engineering, National Institute of Technology Silchar, Silchar 788010, Assam (India); Goyat, M.S. [Department of Physics, University of Petroleum & Energy Studies, Dehradun, Uttarakhand 248007 (India)

2016-03-01

Dual component microcapsules of epoxy resin and polyamine hardener with polymethyl methacrylate (PMMA) shell were synthesized using a water-oil-water emulsion solvent evaporation method. The high concentration of sodium dodecyl sulfate (SDS) was used to reduce the thickness of shell wall of dual component microcapsules. The dual microcapsules of 1:1 weight ratio were introduced in the epoxy adhesive to study the healing effect. The morphology, chemical structure and thermal characteristics of the microcapsules were characterized by scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA), respectively. The insertion of dual component microcapsules in epoxy matrix reduced the lap shear strength of adhesive joints, which may be attributed to the generation of stress concentration cites because of micron sized capsules. However, the extension and absorbed failure energy of adhesive joints under uniaxial loading increased with the increase of concentration of dual microcapsules. The viscoelastic nature of the dual microcapsules may be responsible for this enhancement. Significant enhancement in the healing efficiency (90.93%) of the joints was achieved for 10 wt% of dual microcapsules. The crack pinning and crack blunting mechanisms at the vicinity of the crack path adjacent to the microcapsules were found responsible for significant enhancement in the healing efficiency of the adhesive joints. - Highlights: • High SDS concentration was used to control the dual component microcapsules shell wall thickness. • Self-healing performance of dual component microcapsules reinforced epoxy adhesive based single lap joints was studied. • 90.93% of the damage healing was achieved for self-healing adhesive based single lap joints. • Increase in concentration of microcapsules reduces the lap shear properties of the self-healing joints.

Improvement in electrical, thermal and mechanical properties of epoxy by filling carbon nanotube

Directory of Open Access Journals (Sweden)

2008-01-01

Full Text Available In this study, electrical, thermal and mechanical properties of multi-walled carbon nanotubes (CNTs reinforced Epon 862 epoxy have been evaluated. Firstly, 0.1, 0.2, 0.3, and 0.4 wt% CNT were infused into epoxy through a high intensity ultrasonic liquid processor and then mixed with EpiCure curing agent W using a high speed mechanical agitator. Electric conductivity, dynamic mechanical analysis (DMA, three point bending tests and fracture tests were then performed on unfilled, CNT-filled epoxy to identify the loading effect on the properties of materials. Experimental results show significant improvement in electric conductivity. The resistivity of epoxy decreased from 1014 Ω•m of neat epoxy to 10 Ω•m with 0.4% CNT. The experimental results also indicate that the frequency dependent behavior of CNT/epoxy nanocomposite can be modeled by R-C circuit, permittivity of material increase with increasing of CNT content. DMA studies revealed that filling the carbon nanotube into epoxy can produce a 90% enhancement in storage modulus and a 17°C increase in Tg. Mechanical test results showed that modulus increased with higher CNT loading percentages, but the 0.3 wt% CNT-infusion system showed the maximum strength and fracture toughness enhancement. The decrease in strength and fracture toughness in 0.4% CNT/epoxy was attributed to poor dispersions of nanotubes in the composite.

A study of thermal diffusivity of carbon-epoxy and glass-epoxy composites using the modified pulse method

Directory of Open Access Journals (Sweden)

Terpiłowski Janusz

2014-09-01

Full Text Available Transient heat transfer is studied and compared in two planeparallel composite walls and one EPIDIAN 53 epoxy resin wall acting as a matrix for both composites. The first of the two walls is made of carbonepoxy composite; the other wall is made of glass-epoxy composite, both with comparable thickness of about 1 mm and the same number of carbon and glass fabric layers (four layers. The study was conducted for temperatures in the range of 20-120 °C. The results of the study of thermal diffusivity which characterizes the material as a heat conductor under transient conditions have a preliminary character. Three series of tests were conducted for each wall. Each series took about 24 h. The results from the three series were approximated using linear functions and were found between (0.7-1.35×10−7m2/s. In the whole range of temperature variation, the thermal diffusivity values for carbon-epoxy composite are from 1.2 to 1.5 times higher than those for the other two materials with nearly the same thermal diffusivity characteristics.

Amino phenolics from the fruit of the argan tree Argania spinosa (Skeels L.).

Science.gov (United States)

Klika, D; Khallouki, Farid; Owen, Robert W

2014-01-01

A new phenolic-type compound containing a nitrogenous, heterocyclic-fused ring from the fruit of the argan tree, Argania spinosa (Skeels L.), is described. This and another already known compound also isolated in the course of the work belong to an obscure and rare class of natural products, the amino phenolics.

Antiplasmodial activity of some phenolic compounds from ...

African Journals Online (AJOL)

Background: Plasmodium falciparum, one of the causative agents of malaria, has high adaptability through mutation and is resistant to many types of anti-malarial drugs. This study presents an in vitro assessment of the antiplasmodial activity of some phenolic compounds isolated from plants of the genus Allanblackia.

The influence of stiffeners on axial crushing of glass-fabric-reinforced epoxy composite shells

Directory of Open Access Journals (Sweden)

A. Vasanthanathan

2017-01-01

Full Text Available A generic static and impact experimental procedure has been developed in this work aimed at improving the stability of glass fabric reinforced epoxy shell structures by bonding with axial stiffeners. Crashworthy structures fabricated from composite laminate with stiffeners would offer energy absorption superior to metallic structures under compressive loading situations. An experimental material characterisation of the glass fabric reinforced epoxy composite under uni-axial tension has been carried out in this study. This work provides a numerical simulation procedure to describe the static and dynamic response of unstiffened glass fabric reinforced epoxy composite shell (without stiffeners and stiffened glass fabric reinforced epoxy composite shell (with axial stiffeners under static and impact loading using the Finite Element Method. The finite element calculation for the present study was made with ANSYS®-LS-DYNA® software. Based upon the experimental and numerical investigations, it has been asserted that glass fabric reinforced epoxy shells stiffened with GFRP stiffeners are better than unstiffened glass fabric reinforced epoxy shell and glass fabric reinforced epoxy shell stiffened with aluminium stiffeners. The failure surfaces of the glass fabric reinforced epoxy composite shell structures tested under impact were examined by SEM.

Epoxy coatings for anticorrosion challenges: a link between chemistry and performance?

Energy Technology Data Exchange (ETDEWEB)

Sauvant-Moynot, Valerie; Schweitzer, Sylvie; Grenier, Jacky; Duval, Sebastien [Institut Francais du Petrole, 1 et 4 avenue Bois Preau, 92450 Rueil-Malmaison (France)

2004-07-01

Epoxy coatings have been used extensively for pipeline protection in the oil and gas industries over the past decades. Thank to their outstanding adhesive properties, epoxy resins are classically used for external coating of offshore pipelines although cathodic protection is applied. They provide corrosion protection while being used as neat coating or as primer layer in a three-layer coating. Protection of internal pipelines devoted to gas transport is another application of epoxy coatings. Whatever the case, the choice of the right epoxy formulation should be adapted to the service conditions, namely exposition medium and temperature, in order to provide efficient and sustainable corrosion protection. Epoxy resins constitute a wide family and classical formulations may not fulfill the requirements of today's challenges: as pipelines are require d to operate in more and more difficult conditions, coatings are expected to function in higher temperature conditions; additionally, practical conditions such as temporary injection of methanol make the environmental exposure of the epoxy coating harsher. Therefore, there is a need of a better knowledge of technical performance and limitations of high temperature epoxy resins. This paper examined the influence of the epoxy network architecture on their protection properties and durability while exposed to distilled / sea water at 110 deg. C and to methanol at room temperature. The objective was to investigate the link between resin chemistry and final performance with respect to anticorrosion applications. Five epoxy resin formulations mixed in stoichiometric proportions were cured and post-cured to infinite extent in order to achieve densely cross-linked networks exhibiting controlled and reproducible architectures. Gravimetric and pressurised differential scanning calorimetry (DSC) measurements were performed to evaluate the plasticization effect of both water and methanol on formulations under study. The related

Flame resistant hybrid epoxy composites

Czech Academy of Sciences Publication Activity Database

Śliwa, R.; Oleksy, M.; Heneczkowski, M.; Oliwa, R.; Budzik, G.; Kozik, B.; Markowska, O.; Strachota, Adam

2015-01-01

Roč. 60, č. 10 (2015), s. 667-670 ISSN 0032-2725 Institutional support: RVO:61389013 Keywords : epoxy resin * quaternary phosphonium salts * modified bentonite Subject RIV: CD - Macromolecular Chemistry Impact factor: 0.718, year: 2015

Characterization and analysis of epoxy/clay nanotubes composites; Cacaterizacao e analise de compositos de epoxi, argila e nanotubos de carbono

Energy Technology Data Exchange (ETDEWEB)

NONE

2011-07-01

An DGEBA epoxy matrix was used aiming to achieve a nanocomposite material, through the dispersion of (CNT) via mechanical stirring followed by sonication. In this work the following characterization were performed: mechanical characterization, differential scanning calorimetry (DSC), wide angle X-ray diffraction (WXRD) and scanning electron microscopy (SEM). The addition of CNT and modified clays promoted the increase of modulus of the epoxy matrix, and a synergistic effect between CNT and both clays could be presumed. SEM images of the fracture surface show the difference between the fracture surface area and the presence of clusters among the samples, allowing a correlation with the modulus of elasticity. X-ray diffractograms from 2{Theta} = 5 deg showed no peaks for modified clay samples, however it is possible to affirm that modified clay platelets are forming a less organized structure compared to the structure of the clay as natural in epoxy. (author)

Novel epoxy activated hydrogels for solving lactose intolerance.

Science.gov (United States)

Elnashar, Magdy M M; Hassan, Mohamed E

2014-01-01

"Lactose intolerance" is a medical problem for almost 70% of the world population. Milk and dairy products contain 5-10% w/v lactose. Hydrolysis of lactose by immobilized lactase is an industrial solution. In this work, we succeeded to increase the lactase loading capacity to more than 3-fold to 36.3 U/g gel using epoxy activated hydrogels compared to 11 U/g gel using aldehyde activated carrageenan. The hydrogel's mode of interaction was proven by FTIR, DSC, and TGA. The high activity of the epoxy group was regarded to its ability to attach to the enzyme's -SH, -NH, and -OH groups, whereas the aldehyde group could only bind to the enzyme's -NH2 group. The optimum conditions for immobilization such as epoxy chain length and enzyme concentration have been studied. Furthermore, the optimum enzyme conditions were also deliberated and showed better stability for the immobilized enzyme and the Michaelis constants, K m and V max, were doubled. Results revealed also that both free and immobilized enzymes reached their maximum rate of lactose conversion after 2 h, albeit, the aldehyde activated hydrogel could only reach 63% of the free enzyme. In brief, the epoxy activated hydrogels are more efficient in immobilizing more enzymes than the aldehyde activated hydrogel.

Kinetics of Phenol Degradation in Aqueous Solution Oxidized under Low Frequency Ultrasonic Irradiation

Directory of Open Access Journals (Sweden)

Marwan Marwan

2014-06-01

Full Text Available Phenol is categorized as a refractory pollutant and its presence in water stream is strictly limited according to the government regulation. The present study investigated the degra-dation of phenol in aqueous solution by the effect of ultrasound. The process took place in a 500 ml glass reactor equipped with magnetic stirring and irradiated by low frequency (28 kHz ultrasound from a horn type probe. Ultrasonic irradiation was found to enhance oxidation rates at ambient conditions, compared to other approaches. Optimum conditions were observed at a stirring speed of 400 rpm and temperature of 30 C in acidic solution. It was revealed that the phenol degradation was the first order kinetics with respect to phenol. A low value of the activation energy 6.04 kcal/mol suggested that diffusional steps were rate determining during the phenol decomposition. It also confirmed that phenol was mostly degraded in the film region and less occurred in the bulk solution.

Phenols removal by immobilized tyrosinase reactor in on-line high performance liquid chromatography

International Nuclear Information System (INIS)

Girelli, Anna Maria; Mattei, Enrico; Messina, Antonella

2006-01-01

The development of an immobilized enzyme reactor (IMER) based on tyrosinase immobilized on aminopropyl-controlled pore glass (AP-CPG) for the removal of phenols from model aqueous solutions was reported. To elucidate the influence of the substrate nature, the apparent (V ' max , K ' m ) and the inherent (V max , K m ) Michaelis-Menten constants were determined by Lineweaver-Burk method and the external diffusional contributions on measured enzyme activities were removed by a graphical method. The dephenolization process was realized by recycling the phenol solutions through the bioreactor connected to a chitosan trap in order to remove the colored quinone-type products of the tyrosinase reactions. The results indicated that a complete removal of phenol derivatives in the range of 150-300min, with the exception of 60% removal for phenol reached in 400min, was obtained. The observed sequence: cresol>4-methylcathecol>catechol>4-Cl-phenol-bar phenol was in accordance to the V ' max /K ' m values

Quantitative Study of Interface/Interphase in Epoxy/Graphene-Based Nanocomposites by Combining STEM and EELS.

Science.gov (United States)

Liu, Yu; Hamon, Ann-Lenaig; Haghi-Ashtiani, Paul; Reiss, Thomas; Fan, Benhui; He, Delong; Bai, Jinbo

2016-12-14

A quantitative study of the interphase and interface of graphene nanoplatelets (GNPs)/epoxy and graphene oxide (GO)/epoxy was carried out by combining scanning transmission electron microscopy (STEM) and electron energy-loss spectroscopy (EELS). The interphase regions between GNPs and epoxy matrix were clearly identified by the discrepancy of the plasmon peak positions in the low energy-loss spectra due to different valence electron densities. The spectrum acquisitions were carried out along lines across the interface. An interphase thickness of 13 and 12.5 nm was measured for GNPs/epoxy and GO/epoxy, respectively. The density of the GNPs/epoxy interphase was 2.89% higher than that of the epoxy matrix. However, the density of the GO/epoxy interphase was 1.37% lower than that of the epoxy matrix. The interphase layer thickness measured in this work is in good agreement with the transition layer theory, which proposed an area with modulus linearly varying across a finite width. The results provide an insight into the interphase for carbon-based polymer composites that can help to design the functionalization of nanofillers to improve the composite properties.

Photocured epoxy/graphene nanocomposites with enhanced water vapor barrier properties

Science.gov (United States)

Periolatto, M.; Sangermano, M.; Spena, P. Russo

2016-05-01

A transparent, water vapor barrier film made of an epoxy resin and graphene oxide (GO) was synthesized by photopolymerization process. The epoxy/GO film with just 0.05 wt% GO gives a 93% WVTR reduction with respect to the pristine polymer, reaching barrier properties better than other polymer composites containing higher amounts of graphene. The excellent water vapor barrier is attributed to the good dispersion of GO in the polymer matrix. Moreover, GO significantly enhances the toughness and the damping capacity of the epoxy resins. The hybrid film can have potential applications in anticorrosive coatings, electronic devices, pharmaceuticals and food packaging.

Photocured epoxy/graphene nanocomposites with enhanced water vapor barrier properties

Energy Technology Data Exchange (ETDEWEB)

Periolatto, M.; Spena, P. Russo [Faculty of Science and Technology, Free University of Bozen-Bolzano, Piazza Università 5, Bolzano (Italy); Sangermano, M. [Dipartimento di Scienza Applicata e Tecnologia, Politecnico di Torino, C.so Duca degli Abruzzi 24, Torino (Italy)

2016-05-18

A transparent, water vapor barrier film made of an epoxy resin and graphene oxide (GO) was synthesized by photopolymerization process. The epoxy/GO film with just 0.05 wt% GO gives a 93% WVTR reduction with respect to the pristine polymer, reaching barrier properties better than other polymer composites containing higher amounts of graphene. The excellent water vapor barrier is attributed to the good dispersion of GO in the polymer matrix. Moreover, GO significantly enhances the toughness and the damping capacity of the epoxy resins. The hybrid film can have potential applications in anticorrosive coatings, electronic devices, pharmaceuticals and food packaging.

Photocured epoxy/graphene nanocomposites with enhanced water vapor barrier properties

International Nuclear Information System (INIS)

Periolatto, M.; Spena, P. Russo; Sangermano, M.

2016-01-01

A transparent, water vapor barrier film made of an epoxy resin and graphene oxide (GO) was synthesized by photopolymerization process. The epoxy/GO film with just 0.05 wt% GO gives a 93% WVTR reduction with respect to the pristine polymer, reaching barrier properties better than other polymer composites containing higher amounts of graphene. The excellent water vapor barrier is attributed to the good dispersion of GO in the polymer matrix. Moreover, GO significantly enhances the toughness and the damping capacity of the epoxy resins. The hybrid film can have potential applications in anticorrosive coatings, electronic devices, pharmaceuticals and food packaging.

Synthesis of cuprous oxide epoxy nanocomposite as an environmentally antimicrobial coating.

Science.gov (United States)

M El Saeed, Ashraf; Abd El-Fattah, M; Azzam, Ahmed M; Dardir, M M; Bader, Magd M

2016-08-01

Cuprous oxide is commonly used as a pigment; paint manufacturers begin to employ cuprous oxide as booster biocides in their formulations, to replace the banned organotins as the principal antifouling compounds. Epoxy coating was reinforced with cuprous oxide nanoparticles (Cu2O NPs). The antibacterial as well as antifungal activity of Cu2O epoxy nanocomposite (Cu2O EN) coating films was investigated. Cu2O NPs were also experimented for antibiofilm and time-kill assay. The thermal stability and the mechanical properties of Cu2O EN coating films were also investigated. The antimicrobial activity results showed slowdown, the growth of organisms on the Cu2O EN coating surface. TGA results showed that incorporating Cu2O NPs into epoxy coating considerably enhanced the thermal stability and increased the char residue. The addition of Cu2O NPs at lower concentration into epoxy coating also led to an improvement in the mechanical resistance such as scratch and abrasion. Cu2O NPs purity was confirmed by XRD. The TEM photograph demonstrated that the synthesized Cu2O NPs were of cubic shape and the average diameter of the crystals was around 25nm. The resulting perfect dispersion of Cu2O NPs in epoxy coating revealed by SEM ensured white particles embedded in the epoxy matrix. Copyright © 2016 Elsevier B.V. All rights reserved.

The non-isothermal DSC kinetics of polyethylene tereftalate–epoxy compatible blends

International Nuclear Information System (INIS)

Zvetkov, V.L.; Djoumaliisky, S.; Simeonova-Ivanova, E.

2013-01-01

Highlights: ► The non-isothermal DSC kinetics of the reaction of DGEBA with DDS, in particular in the presence of phase separating PET, has been studied. ► The specific features in the kinetics of PET formulations in comparison to the pure system have been discussed. ► The fast pre-curing of the epoxy phase allows supposing sub-micro phase separation of PET and efficient toughening of the epoxy matrix. - Abstract: Polyethylene tereftalate has been dissolved in an epoxy resin based on diglycidyl ether of bisphenol-A, DGEBA, and the epoxy component has been cross-linked with the aid of two diamine hardeners. Two series of samples have been tested at the epoxy-amine stoichiometry applying the differential scanning calorimetry, DSC, in scanning mode. One of the series of samples was pre-cured at low temperatures with the aid of an aliphatic diamine hardener near the gel point and post-cured with diaminodiphenyl sulfone, DDS. The other series of samples contained the higher temperature hardener only. Consequently, the experimental data obtained in this study on both systems relate to the non-isothermal curing of DGEBA with DDS. The kinetics has been estimated applying preferably isoconversional (model free) methods. It has been established that the fast pre-curing allows performing a sub-micro phase separation and efficient toughening of the epoxy matrix

The non-isothermal DSC kinetics of polyethylene tereftalate–epoxy compatible blends

Energy Technology Data Exchange (ETDEWEB)

Zvetkov, V.L., E-mail: zvetval@yahoo.com [Institute of Mechanics, Bulgarian Academy of Sciences, bl. I, Sofia 1113 (Bulgaria); Djoumaliisky, S.; Simeonova-Ivanova, E. [Institute of Mechanics, Bulgarian Academy of Sciences, bl. I, Sofia 1113 (Bulgaria)

2013-02-10

Highlights: ► The non-isothermal DSC kinetics of the reaction of DGEBA with DDS, in particular in the presence of phase separating PET, has been studied. ► The specific features in the kinetics of PET formulations in comparison to the pure system have been discussed. ► The fast pre-curing of the epoxy phase allows supposing sub-micro phase separation of PET and efficient toughening of the epoxy matrix. - Abstract: Polyethylene tereftalate has been dissolved in an epoxy resin based on diglycidyl ether of bisphenol-A, DGEBA, and the epoxy component has been cross-linked with the aid of two diamine hardeners. Two series of samples have been tested at the epoxy-amine stoichiometry applying the differential scanning calorimetry, DSC, in scanning mode. One of the series of samples was pre-cured at low temperatures with the aid of an aliphatic diamine hardener near the gel point and post-cured with diaminodiphenyl sulfone, DDS. The other series of samples contained the higher temperature hardener only. Consequently, the experimental data obtained in this study on both systems relate to the non-isothermal curing of DGEBA with DDS. The kinetics has been estimated applying preferably isoconversional (model free) methods. It has been established that the fast pre-curing allows performing a sub-micro phase separation and efficient toughening of the epoxy matrix.

Colorless triphenylamine-based aliphatic thermoset epoxy for multicolored and near-infrared electrochromic applications.

Science.gov (United States)

Chuang, Ya-Wen; Yen, Hung-Ju; Wu, Jia-Hao; Liou, Guey-Sheng

2014-03-12

In this study, two novel colorless thermoset epoxy resins with anodically electrochromism were prepared from the thermal curing of two triphenylamine-based diamine monomers, 4,4'-diamino-4″-methoxytriphenylamine (1) and N,N'-bis(4-aminophenyl)-N,N'-di(4-methoxylphenyl)-1,4-phenylenediamine (2) with aliphatic epoxy triglycidyl isocyanurate, respectively. The resulting thermoset epoxy resins showed excellent softening temperature (Ts, 270 and 280 °C) due to the rigid structure and highly crosslinking density. In addition, novel colorless epoxy resin films revealed good reversible electrochemical oxidation and interesting multi-electrochromic behavior with high contrast ratio both in visible and near-infrared regions. The aliphatic thermoset epoxy resins also exhibited high transparency in visible region as colorless and great potential for practical electrochromic applications.

Damage detection and conductivity evolution in carbon nanofiber epoxy via electrical impedance tomography

International Nuclear Information System (INIS)

Tallman, T N; Wang, K W; Gungor, S; Bakis, C E

2014-01-01

Utilizing electrically conductive nanocomposites for integrated self-sensing and health monitoring is a promising area of structural health monitoring (SHM) research wherein local changes in conductivity coincide with damage. In this research we conduct proof of concept investigations using electrical impedance tomography (EIT) for damage detection by identifying conductivity changes and by imaging conductivity evolution in a carbon nanofiber (CNF) filled epoxy composite. CNF/epoxy is examined because fibrous composites can be manufactured with a CNF/epoxy matrix thereby enabling the entire matrix to become self-sensing. We also study the mechanisms of conductivity evolution in CNF/epoxy through electrical impedance spectroscopy (EIS) testing. The results of these tests indicate that thermal expansion is responsible for conductivity evolution in a CNF/epoxy composite. (paper)

Nanoindentation study of interphases in epoxy/amine thermosetting systems modified with thermoplastics.

Science.gov (United States)

Ramos, Jose Angel; Blanco, Miren; Zalakain, Iñaki; Mondragon, Iñaki

2009-08-15

The characterization of a mixture of epoxy/amine with different stoichiometric ratios was carried out by means of nanoindentation. The epoxy system was composed by diglycidyl ether of bisphenol-A and 4,4'-methylene bis-(3-chloro 2,6-diethylaniline). Diffusion through interface formed by epoxy/amine system in stoichiometric ratio and several thermoplastic polymers was also analyzed by means of stiffness analysis, as studied by atomic force microscopy (AFM) and coupled nanoindentation tests. Used thermoplastics were an amorphous, atactic polystyrene, and two semicrystalline, syndiotactic polystyrene and poly(phenylene sulfide). Larger range diffusion was obtained in epoxy/amine systems modified with atactic polystyrene while the study of the influence of stoichiometric ratio suggests that the excess of epoxy generated stiffer material. In addition, larger indentation loads resulted in higher apparent stiffness because of the more number of polymer chains that had to re-accommodate owing to the increase in contact area.

E-Beam-Cured Layered-Silicate and Spherical Silica Epoxy Nanocomposites (Preprint)

National Research Council Canada - National Science Library

Chen, Chenggang; Anderson, David P

2007-01-01

.... The nanofillers can be two dimensional (layered-silicate) and zero dimensional (spherical silica). Both the spherical silica epoxy nanocomposite and the layered-silicate epoxy nanocomposite can be cured to a high degree of curing...

UV absorption by cerium oxide nanoparticles/epoxy composite thin films

International Nuclear Information System (INIS)

Dao, Ngoc Nhiem; Luu, Minh Dai; Nguyen, Quang Khuyen; Kim, Byung Sun

2011-01-01

Cerium oxide (CeO 2 ) nanoparticles have been used to modify properties of an epoxy matrix in order to improve the ultra-violet (UV) absorption property of epoxy thin films. The interdependence of mechanical properties, UV absorption property and the dispersed concentration of CeO 2 nanoparticles was investigated. Results showed that, by increasing the dispersed concentration of CeO 2 nanoparticles up to 3 wt%, tensile modulus increases while two other mechanical properties, namely tensile strength and elongation, decrease. The UV absorption peak and the absorption edges of the studied thin films were observed in the UV-Vis absorption spectra. By incorporating CeO 2 nanoparticles into the epoxy matrix, an absorption peak appears at around 318 nm in UV-Vis spectra with increasing CeO 2 concentration from 0.1 to 1.0 wt%. Scanning electron microscopy (SEM) images revealed that a good dispersion of nanoparticles in the epoxy matrix by an ultrasonic method was achieved

Improvement of Mechanical and Dielectric Properties of Epoxy Resin Using CNTs/ZnO Nanocomposite.

Science.gov (United States)

Vu, Pham Gia; Truc, Trinh Anh; Chinh, Nguyen Thuy; Tham, Do Quang; Trung, Tran Huu; Oanh, Vu Ke; Hang, To Thi Xuan; Olivier, Marjorie; Hoang, Thai

2018-04-01

In this study, carbon nanotubes (CNTs)/ZnO composites had been prepared using the sol-gel method and then incorporated into an epoxy resin for reinforcement of mechanical and electrical properties. Fourier Transform Infrared (FTIR), X-ray diffraction (XRD) Field Emission Scanning Electron Microscope (FE-SEM) analyses show that the ZnO nanoparticles deposited on CNTs were crystallized in a hexagonal wurtzite structure. Average particle size of ZnO deposited on the CNT was about 8 nm. The mechanical and dielectric properties of epoxy containing CNTs/ZnO were investigated in comparison to epoxy resin and epoxy resin containing only CNT or ZnO nanoparticles. The results indicated that tensile strength and elongation at break of the nanocomposite were substantially improved with the presence of CNTs/ZnO at the equal volume. The DSC analysis associate with the dielectric results shows that the behavior of epoxy/CNTs/ZnO is identical to epoxy/ZnO composite, and the CNTs is essential to the distributed arrangement of ZnO in the epoxy resin.

Inhibitory effects of phenolic compounds of rice straw formed by saccharification during ethanol fermentation by Pichia stipitis.

Science.gov (United States)

Wang, Xiahui; Tsang, Yiu Fai; Li, Yuhao; Ma, Xiubing; Cui, Shouqing; Zhang, Tian-Ao; Hu, Jiajun; Gao, Min-Tian

2017-11-01

In this study, it was found that the type of phenolic acids derived from rice straw was the major factor affecting ethanol fermentation by Pichia stipitis. The aim of this study was to investigate the inhibitory effect of phenolic acids on ethanol fermentation with rice straw. Different cellulases produced different ratios of free phenolic acids to soluble conjugated phenolic acids, resulting in different fermentation efficiencies. Free phenolic acids exhibited much higher inhibitory effect than conjugated phenolic acids. The flow cytometry results indicated that the damage to cell membranes was the primary mechanism of inhibition of ethanol fermentation by phenolic acids. The removal of free phenolic acids from the hydrolysates increased ethanol productivity by 2.0-fold, indicating that the free phenolic acids would be the major inhibitors formed during saccharification. The integrated process for ethanol and phenolic acids may constitute a new strategy for the production of low-cost ethanol. Copyright © 2017 Elsevier Ltd. All rights reserved.

DEGRADATION OF MAGNET EPOXY AT NSLS X-RAY RING.

Energy Technology Data Exchange (ETDEWEB)

HU,J.P.; ZHONG,Z.; HAAS,E.; HULBERT,S.; HUBBARD,R.

2004-05-24

Epoxy resin degradation was analyzed for NSLS X-ring magnets after two decades of 2.58-2.8 GeV continuous electron-beam operation, based on results obtained from thermoluminescent dosimeters irradiated along the NSLS ring and epoxy samples irradiated at the beamline target location. A Monte Carlo-based particle transport code, MCNP, was utilized to verify the dose from synchrotron radiation distributed along the axial- and transverse-direction in a ring model, which simulates the geometry of a ring quadrupole magnet and its central vacuum chamber downstream of the bending-magnet photon ports. The actual life expectancy of thoroughly vacuum baked-and-cured epoxy resin was estimated from radiation tests on similar polymeric materials using a radiation source developed for electrical insulation and mechanical structure studies.

Protection of Steel Rebar in Salt-Contaminated Cement Mortar Using Epoxy Nanocomposite Coatings

Directory of Open Access Journals (Sweden)

The Huu Nguyen

2018-01-01

Full Text Available Epoxy reinforced with two kinds of nanoparticles dealing with nano-SiO2 and nano-Fe2O3 was coated on steel rebar embedded in a chloride contaminated cement mortar. NaCl was added to the fresh Portland cement paste (at 0.3% and 0.5% by weight of cement to simulate the chloride contamination at the critical level. The effect of incorporating nanoparticles on the corrosion resistance of epoxy-coated steel rebar was investigated by linear potentiodynamic polarization and electrochemical impedance spectroscopy. For the 0.3 wt.% chloride mortars, the electrochemical monitoring of the coated steel rebars during immersion for 56 days in 0.1 M NaOH solutions suggested the beneficial role of nano-Fe2O3 particles in significantly improving the corrosion resistance of the epoxy-coated rebar. After 56 days of immersion, the nano-Fe2O3 reduced the corrosion current of epoxy-coated rebar by a factor of 7.9. When the chloride concentration in the cement mortar was 0.5 wt.%, the incorporation of nanoparticles into the epoxy matrix did not enhance the corrosion resistance of epoxy coating for the rebar. At this critical level, chloride ions initiated rebar corrosion through nanoparticles at the epoxy/rebar interface.

Effect of Thermally Reduced Graphene Oxide on Mechanical Properties of Woven Carbon Fiber/Epoxy Composite

Directory of Open Access Journals (Sweden)

Nitai Chandra Adak

2018-02-01

Full Text Available Thermally reduced graphene oxide (TRGO was incorporated as a reinforcing filler in the epoxy resin to investigate the effect on the mechanical properties of carbon fiber (CF/epoxy composites. At first, the epoxy matrix was modified by adding different wt % of TRGO from 0.05 to 0.4 wt % followed by the preparation of TRGO/CF/epoxy composites througha vacuum-assisted resin transfer molding process. The prepared TRGO was characterized by using Fourier transform infrared spectroscopy, Raman Spectroscopy and field emission scanning electron microscopy (FE-SEM techniques. It was observed that the wrinkled structure of synthesized TRGO may be helpful to interlock with the epoxy resin and CF.The inter-laminar shear strength, in-plane fracture toughness and impact strength increased by ~67%, 62% and 93% at 0.2 wt % of TRGO loading in the CF/epoxy composites as compared to the CF reinforced epoxy. The mechanical properties of the hybrid composites decreased beyond the 0.2 wt % of TRGO incorporation in the epoxy resin. The fracture surfaces of the hybrid composites were studied by FE-SEM image analysis to investigate the synergistic effect of TRGO in the CF/epoxy composite. This study suggested that TRGO could be used asgood nanofiller to resist the matrix and fiber fracture.

Efficient Enzymatic Synthesis of Phenolic Ester by Increasing Solubility of Phenolic Acids in Ionic Liquids

DEFF Research Database (Denmark)

Yang, Zhiyong; Guo, Zheng; Xu, Xuebing

Compounds from phenolic acid family are well known natural antioxidants, but the application of phenolic acids as antioxidants in industry is limited due to the relatively low solubility in oil-based media. The properties of phenolic acids can be modified through enzymatic lipophilization...... and modified phenolic acids will have amphiphilic property, therefore they can be localized at oil-water or water-oil phase where oxidation is considered to occur frequently. It had been reported that immobilized Candida Antarctica lipase B was the most effective biocatalyst for the various esterification...... reactions, and it had been widely used for esterification of various phenolic acids with fatty alcohol or triglycerides. However, the conversion of phenolic acids is low due to low solubility in hydrophobic solvents and hindrance effect of unsaturated side chain towards the enzyme. Our studies show...

Characterization and analysis of epoxy/clay nanotubes composites

International Nuclear Information System (INIS)

Sene, Tarcisio S.; Kock, Thyago; Coelho, Luiz A.F.; Becker, Daniela

2011-01-01

An DGEBA epoxy matrix was used aiming to achieve a nanocomposite material, through the dispersion of (CNT) via mechanical stirring followed by sonication. In this work the following characterization were performed: mechanical characterization, differential scanning calorimetry (DSC), wide angle X-ray diffraction (WXRD) and scanning electron microscopy (SEM). The addition of CNT and modified clays promoted the increase of modulus of the epoxy matrix, and a synergistic effect between CNT and both clays could be presumed. SEM images of the fracture surface show the difference between the fracture surface area and the presence of clusters among the samples, allowing a correlation with the modulus of elasticity. X-ray diffractograms from 2Θ = 5 deg showed no peaks for modified clay samples, however it is possible to affirm that modified clay platelets are forming a less organized structure compared to the structure of the clay as natural in epoxy. (author)

Hydrothermal ageing of glass/epoxy composites for wind turbine blades

NARCIS (Netherlands)

Rocha, I.B.C.M.; Raijmaekers, S.; Nijssen, R.P.L.; Van der Meer, F.P.

2015-01-01

In this work, a glass/epoxy material system commonly applied in wind turbine design was used to evaluate damage processes brought by water ingression during service life. Composite short-beams and neat epoxy beams and dog-bones were conditioned by water immersion at 50º until saturation and tested

Consolidation of the formation sand by chemical methods

Directory of Open Access Journals (Sweden)

Mariana Mihočová

2006-10-01

Full Text Available The sand control by consolidation involves the process of injecting chemicals into the naturally unconsolidated formation to provide an in situ grain-to-grain cementation. The sand consolidation chemicals are available for some 30 years. Several types of consolidating material were tried. Presently available systems utilize solidified plastics to provide the cementation. These systems include phenol resin, phenol-formaldehyde, epoxy, furan and phenolic-furfuryl.The sand consolidation with the steam injection is a novel technique. This process provides a highly alkaline liquid phase and temperatures to 300 °C to geochemically create cements by interacting with the dirty sand.While the formation consolidation has widely applied, our experience has proved a high level of success.

Nickel-catalyzed regio- and enantioselective aminolysis of 3,4-epoxy alcohols.

Science.gov (United States)

Wang, Chuan; Yamamoto, Hisashi

2015-04-08

The first catalytic regio- and enantioselective aminolysis of 3,4-epoxy alcohols has been accomplished. Under the catalysis of Ni(ClO4)2·6H2O, the C4 selective ring opening of various 3,4-epoxy alcohols proceeded in a stereospecific manner with high regioselectivities. Furthermore, with the Ni-BINAM catalytic system the enantioselective ring opening of 3,4-epoxy alcohols furnished various γ-hydroxy-δ-amino alcohols as products with complete regiocontrol and high enantioselectivities (up to 94% ee).

Novel Formulations of Phase Change Materials—Epoxy Composites for Thermal Energy Storage

OpenAIRE

Maria Elena Arce; Miguel Angel Alvarez Feijoo; Andres Suarez Garcia; Claudia C. Luhrs

2018-01-01

This research aimed to evaluate the thermal properties of new formulations of phase change materials (PCMs)-epoxy composites, containing a thickening agent and a thermally conductive phase. The composite specimens produced consisted of composites fabricated using (a) inorganic PCMs (hydrated salts), epoxy resins and aluminum particulates or (b) organic PCM (paraffin), epoxy resins, and copper particles. Differential Scanning Calorimetry (DSC) was used to analyze the thermal behavior of the sa...

Creep behavior of an epoxy resin and an epoxy-based FRP in condition of simultaneous supply of radiation and stress at cryogenic temperatures

International Nuclear Information System (INIS)

Nishiura, Tetsuya; Nishijima, Shigehiro; Okada, Toichi

1995-01-01

Creep tests of an epoxy resin and an epoxy-based FRP in bending under irradiation condition have been carried out, to investigate the synergistic effects of radiation and stress on mechanical properties of FRP. Simultaneous supply of stress and irradiation on the epoxy resin and the FRP enhanced creep rates in comparison with that supply of the stress on a post-irradiated one did. ESR spectra measurement was also carried out to study the change of molecule of the resin irradiated. Increase of molecular weight between crosslinks was found out to be enhanced by the synergistic effect of radiation and stress. The mechanism of increased damage of FRP induced by the effects of simultaneous stress and irradiation is discussed. (author)

Determination of Young's modulus of epoxy coated polyethylene micro-cantilever using phase-shift shadow moiré method

Science.gov (United States)

Lim, J. H.; Ratnam, M. M.; Azid, I. A.; Mutharasu, D.

2011-11-01

Young's moduli of various epoxy coated polyethylene terephthalate (PET) micro-cantilevers were determined from the deflection results obtained using the phase-shift shadow moiré (PSSM) method. The filler materials for epoxy coatings were aluminum and graphite powders that were mixed with epoxy at various percentages. Young's moduli were calculated from theory based on the deflection results. The PET micro-cantilever coated with aluminum-epoxy coating showed increasing value of Young's modulus when the ratios of the aluminum-epoxy were increased. The graphite-epoxy coating on the PET micro-cantilever also showed the same trend. The experimental results also show that Young's modulus of the graphite-epoxy coating is higher than aluminum-epoxy coating in comparison at the same mixing ratio.

Preparation, Characterization, and Modeling of Carbon Nanofiber/Epoxy Nanocomposites

Directory of Open Access Journals (Sweden)

Lan-Hui Sun

2011-01-01

Full Text Available There is a lack of systematic investigations on both mechanical and electrical properties of carbon nanofiber (CNF-reinforced epoxy matrix nanocomposites. In this paper, an in-depth study of both static and dynamic mechanical behaviors and electrical properties of CNF/epoxy nanocomposites with various contents of CNFs is provided. A modified Halpin-Tsai equation is used to evaluate the Young's modulus and storage modulus of the nanocomposites. The values of Young's modulus predicted using this method account for the effect of the CNF agglomeration and fit well with those obtained experimentally. The results show that the highest tensile strength is found in the epoxy nanocomposite with a 1.0 wt% CNFs. The alternate-current (AC electrical properties of the CNF/epoxy nanocomposites exhibit a typical insulator-conductor transition. The conductivity increases by four orders of magnitude with the addition of 0.1 wt% (0.058 vol% CNFs and by ten orders of magnitude for nanocomposites with CNF volume fractions higher than 1.0 wt% (0.578 vol%. The percolation threshold (i.e., the critical CNF volume fraction is found to be at 0.057 vol%.

AC electrical breakdown phenomena of epoxy/layered silicate nanocomposite in needle-plate electrodes.

Science.gov (United States)

Park, Jae-Jun; Lee, Jae-Young

2013-05-01

Epoxy/layered silicate nanocomposite for the insulation of heavy electric equipments were prepared by dispersing 1 wt% of a layered silicate into an epoxy matrix with a homogenizing mixer and then AC electrical treeing and breakdown tests were carried out. Wide-angle X-ray diffraction (WAXD) analysis and transmission electron microscopy (TEM) observation showed that nano-sized monolayers were exfoliated from a multilayered silicate in the epoxy matrix. When the nano-sized silicate layers were incorporated into the epoxy matrix, the breakdown rate in needle-plate electrode geometry was 10.6 times lowered than that of the neat epoxy resin under the applied electrical field of 520.9 kV/mm at 30 degrees C, and electrical tree propagated with much more branches in the epoxy/layered silicate nanocomposite. These results showed that well-dispersed nano-sized silicate layers retarded the electrical tree growth rate. The effects of applied voltage and ambient temperature on the tree initiation, growth, and breakdown rate were also studied, and it was found that the breakdown rate was largely increased, as the applied voltage and ambient temperature increased.

The Effect of Nanoparticles Percentage on Mechanical Behavior of Silica-Epoxy Nanocomposites

International Nuclear Information System (INIS)

Islam, M.S.; Masoodi, R.; Rostami, H.

2013-01-01

Silica-epoxy nanocomposites are very common among nanocomposites, which makes them very important. Several researchers have studied the effect of nanoparticle’s size, shape, and loading on mechanical behavior of silica-epoxy nanocomposites. This paper reviews the most important research done on the effect of nanoparticle loading on mechanical properties of silica-epoxy nanocomposites. While the main focus is the tensile behavior of nanocomposite, the compressive behavior and flexural behavior were also reviewed. Finally, some of the published experimental data were combined in the graphs, using dimensionless parameters. Later, the best fitted curves were used to derive some empirical formulas for mechanical properties of silica-epoxy nanocomposites as functions of weight or volume fraction of nanoparticles.

Novel Epoxy Activated Hydrogels for Solving Lactose Intolerance

Directory of Open Access Journals (Sweden)

Magdy M. M. Elnashar

2014-01-01

Full Text Available “Lactose intolerance” is a medical problem for almost 70% of the world population. Milk and dairy products contain 5–10% w/v lactose. Hydrolysis of lactose by immobilized lactase is an industrial solution. In this work, we succeeded to increase the lactase loading capacity to more than 3-fold to 36.3 U/g gel using epoxy activated hydrogels compared to 11 U/g gel using aldehyde activated carrageenan. The hydrogel’s mode of interaction was proven by FTIR, DSC, and TGA. The high activity of the epoxy group was regarded to its ability to attach to the enzyme’s –SH, –NH, and –OH groups, whereas the aldehyde group could only bind to the enzyme’s –NH2 group. The optimum conditions for immobilization such as epoxy chain length and enzyme concentration have been studied. Furthermore, the optimum enzyme conditions were also deliberated and showed better stability for the immobilized enzyme and the Michaelis constants, Km and Vmax, were doubled. Results revealed also that both free and immobilized enzymes reached their maximum rate of lactose conversion after 2 h, albeit, the aldehyde activated hydrogel could only reach 63% of the free enzyme. In brief, the epoxy activated hydrogels are more efficient in immobilizing more enzymes than the aldehyde activated hydrogel.

Phenolics and Lipophilized Phenolics as Antioxidants in Fish Oil Enriched Emulsions,

DEFF Research Database (Denmark)

Sørensen, Ann-Dorit Moltke; Nielsen, Nina Skall; Jacobsen, Charlotte

work better as antioxidants in bulk oil, whereas lipophilic compounds are better antioxidants in emulsions. This presentation is an overview of our previous work in the area of fish oil enriched emulsions with antioxidants. Our studies have shown that the lipophilicity of the compounds is not the only...... with increased lipophilicity. Instead a cut-off effect was observed in relation to the alkyl chain length lipophilized to the phenolic compound. Furthermore, the efficacy of lipophilic antioxidants is influenced by the type of food system. Thus, our results show that the antioxidant behavior may not be as simple...

Interlaminar fracture in woven carbon/epoxy laminates

Directory of Open Access Journals (Sweden)

Paulo N.B. Reis

2014-10-01

Full Text Available This paper describes an experimental study developed to characterize the mode I and mode II fracture toughness of carbon/epoxy woven composites, using DCB and ENF tests, respectively. The laminates were manufactured using an epoxy resin and twelve woven balanced bi-directional layers of carbon fibres, all of them with the same orientation (0/90º. Significant instantaneous delaminations were observed particularly for the DCB specimen, which were responsible for an oscillatory behaviour of GI versus crack length. The maximum values obtained for GIC and GIIC were 281 and 1800 J/m2, respectively.

Control of pore size in epoxy systems.

Energy Technology Data Exchange (ETDEWEB)

Sawyer, Patricia Sue; Lenhart, Joseph Ludlow (North Dakota State University, Fargo, ND); Lee, Elizabeth (North Dakota State University, Fargo, ND); Kallam, Alekhya (North Dakota State University, Fargo, ND); Majumdar, Partha (North Dakota State University, Fargo, ND); Dirk, Shawn M.; Gubbins, Nathan; Chisholm, Bret J. (North Dakota State University, Fargo, ND); Celina, Mathias C.; Bahr, James (North Dakota State University, Fargo, ND); Klein, Robert J.

2009-01-01

Both conventional and combinatorial approaches were used to study the pore formation process in epoxy based polymer systems. Sandia National Laboratories conducted the initial work and collaborated with North Dakota State University (NDSU) using a combinatorial research approach to produce a library of novel monomers and crosslinkers capable of forming porous polymers. The library was screened to determine the physical factors that control porosity, such as porogen loading, polymer-porogen interactions, and polymer crosslink density. We have identified the physical and chemical factors that control the average porosity, pore size, and pore size distribution within epoxy based systems.

Preparation of a bio-based epoxy with comparable properties to those of petroleum-based counterparts

Directory of Open Access Journals (Sweden)

X. Q. Liu

2012-04-01

Full Text Available In this paper a bio-based epoxy with outstanding thermal and mechanical properties was synthesized using a rosin-based epoxy monomer and a rosin-based curing agent. The chemical structures of rosin based epoxy monomer and curing agent were confirmed by Nuclear Magnetic Resonance (NMR and Fourier Transform Infrared (FT-IR spectra. The flexural mechanical and dynamic mechanical properties as well as thermal stability of the cured epoxy were investigated. The results showed that the cured epoxy exhibited a glass transition temperature (Tg of 164°C and its flexural strength and modulus were as high as 70 and 2200 MPa, respectively. This indicated that a wholly bio-based epoxy resin possessing high performance was successfully obtained.

Wear Behavior of Woven Roving Aramid / Epoxy Composite under Different Conditions

Directory of Open Access Journals (Sweden)

Asad A. Khalid

2012-09-01

Full Text Available Wear behavior studies of aramid woven roving /epoxy composite has been conducted. Sliding the material against smooth steel counter face under dry and  lubricated with oil conditions has been investigated. Powder of Silicon carbide has been mixed with the epoxy resin and tested also. The powder was mixed in a volumetric fraction of 10% with the epoxy resin. Four Laminates of six layers were fabricated by hand lay up  method. A pin on disc apparatus has been fabricated to conduct the sliding wear tests on specimens of (4 mm   4 mm   12 mm in size have been cut from the four laminates. The effect of sliding condition including dry, lubricated, dry with additives and lubricated with additives have been studied. Wear rate tests have been conducted at different sliding speeds and loads. Results show that the wear characteristics are influenced by the operating conditions and the construction of the composite material used. It was also found that the wear of aramid /epoxy composite onto the steel counter face were significantly reduced by using lubricant and additives but still took place.Keywords: Wear, Composite materials, Woven roving aramid, Epoxy, Additives, Lubricant.

Metabolism of benzene and phenol by a reconstituted purified phenobarbital induced rat liver mixed function oxidase system

International Nuclear Information System (INIS)

Griffiths, J.C.

1986-01-01

Cytochrome P-450 and the electron-donor, NADPH-cytochrome c reductase were isolated from phenobarbital induced rat liver microsomes. Both benzene and its primary metabolite phenol, were substrates for the reconstituted purified phenobarbital induced rat liver mixed function oxidase system. Benzene was metabolized to phenol and the polyhydroxylated metabolites; catechol, hydroquinone and 1,2,4 benzenetriol. Benzene elicited a Type I spectral change upon its interaction with the cytochrome P-450 while phenol's interaction with the cytochrome P-450 produced a reverse Type I spectra. The formation of phenol showed a pH optimum of 7.0 compared with 6.6-6.8 for the production of the polyhyrdoxylated metabolites. Cytochrome P-450 inhibitors, such as metyrapone and SKF 525A, diminished the production of phenol from benzene but not the production of the polyhydroxylated metabolites from phenol. The radical trapping agents, DMSO, KTBA and mannitol, decreased the recovery of polyhydroxylated metabolites, from 14 C-labeled benzene and/or phenol. As KTBA and DMSO interacted with OH. There was a concomitant release of ethylene and methane, which was measured. Desferrioxamine, an iron-chelator and catalase also depressed the recovery of polyhydroxylated metabolites. In summary, benzene and phenol were both substrates for this reconstituted purified enzyme system, but they differed in binding to cytochrome P-450, pH optima and mode of hydroxylation

The thermal properties of a carbon nanotube-enriched epoxy: Thermal conductivity, curing, and degradation kinetics

KAUST Repository

Ventura, Isaac Aguilar

2013-05-31

Multiwalled carbon nanotube-enriched epoxy polymers were prepared by solvent evaporation based on a commercially available epoxy system and functionalized multiwalled carbon nanotubes (COOH-MWCNTs). Three weight ratio configurations (0.05, 0.5, and 1.0 wt %) of COOH-MWCNTs were considered and compared with neat epoxy and ethanol-treated epoxy to investigate the effects of nano enrichment and processing. Here, the thermal properties of the epoxy polymers, including curing kinetics, thermal conductivity, and degradation kinetics were studied. Introducing the MWCNTs increased the curing activation energy as revealed by differential scanning calorimetry. The final thermal conductivity of the 0.5 and 1.0 wt % MWCNT-enriched epoxy samples measured by laser flash technique increased by up to 15% compared with the neat material. The activation energy of the degradation process, investigated by thermogravimetric analysis, was found to increase with increasing CNT content, suggesting that the addition of MWCNTs improved the thermal stability of the epoxy polymers. © 2013 Wiley Periodicals, Inc.

Effect of electron beam irradiation on thermal and mechanical properties of aluminum based epoxy composites

Science.gov (United States)

Visakh, P. M.; Nazarenko, O. B.; Sarath Chandran, C.; Melnikova, T. V.; Nazarenko, S. Yu.; Kim, J.-C.

2017-07-01

The epoxy resins are widely used in nuclear and aerospace industries. The certain properties of epoxy resins as well as the resistance to radiation can be improved by the incorporation of different fillers. This study examines the effect of electron beam irradiation on the thermal and mechanical properties of the epoxy composites filled with aluminum nanoparticles at percentage of 0.35 wt%. The epoxy composites were exposed to the irradiation doses of 30, 100 and 300 kGy using electron beam generated by the linear electron accelerator ELU-4. The effects of the doses on thermal and mechanical properties of the aluminum based epoxy composites were investigated by the methods of thermal gravimetric analysis, tensile test, and dynamic mechanical analysis. The results revealed that the studied epoxy composites showed good radiation resistance. The thermal and mechanical properties of the aluminum based epoxy composites increased with increasing the irradiation dose up to 100 kGy and decreased with further increasing the dose.

Phenol oxidation with hydrogen peroxide

Energy Technology Data Exchange (ETDEWEB)

Ramiez Cortina, R.C.; Hernadez Perez, I. [Univ. Autonoma Metropolitana - Azcapotzalco, Div. de CBI, Dept. de Energia, Azcapotzalco (Mexico); Ortiz Lozoya, C.E. [Univ. Autonoma Metropolitana - Azcapotzalco, Div. de CBI, Dept. de Energia, Azcapotzalco (Mexico)]|[Inst. Mexicano del Petroleo (Mexico); Alonso Gutierrez, M.S. [Inst. National Polytechnique, ENSCT, Lab. of Chimie Agro-Industrielle, Toulouse (France)

2003-07-01

In this work the process application of advanced oxidation is investigated with hydrogen peroxide, for the phenol destruction. The experiments were carried out in a glass reactor of 750 mL. Three phenol concentrations were studied (2000, 1000 and 500 ppm) being oxidized with H{sub 2}O{sub 2} (1, 2 and 3 M). The tests of oxidation had a reaction time of 48 h at ambient temperature and pressure. The phenol degradation was determined as COD at different reaction times and intermediate oxidation products were analyzed by chromatography. The results of this study show that it is possible to degrade phenol (1000 ppm) until 90% with H{sub 2}O{sub 2} 2M. Being achieved the best efficiency with a good molar relationship of H{sub 2}O{sub 2}/phenol. Intends a reaction outline in the degradation of the phenol. (orig.)

Phenolic Composition, Antioxidant Capacity and in vitro Cytotoxicity Assessment of Fruit Wines

Directory of Open Access Journals (Sweden)

Ana Ljevar

2016-01-01

Full Text Available Fruit wines contain a wide range of phenolic compounds with biological effects, but their composition and potential benefits to human health have been studied to the much lesser extent compared to grape wines. The aim of this research is to study the phenolic profile of different types of fruit wines and to evaluate their antioxidant and biological potential. Commercially available fruit wines from blackberry, cherry, raspberry, blackcurrant, strawberry and apple produced in Croatia were analyzed. To the best of our knowledge, this study represents the first comprehensive screening of Croatian fruit wines. The phenolic characterization was performed by spectrophotometry and HPLC-PDA/MS analysis. The antioxidant capacity was determined using ABTS and FRAP assays, while in vitro biological activity was analyzed by the cytotoxicity assay on human breast (MCF-7, colon (CaCo-2 and cervical (HeLa cancer cell lines. Among the studied fruit wines, blackberry, cherry and blackcurrant wines contained the highest amount of total phenolics, while the last two also contained the highest amount of total anthocyanins. The analysis of individual phenolic compounds showed distinctive phenolic composition of each type of fruit wine, notably as regards anthocyanins. Blackberry, followed by cherry, raspberry and blackcurrant wines also had a significantly higher antioxidant capacity than strawberry and apple wines. Fruit wines inhibited the growth of human cancer cells in vitro in a dose-dependent manner with differing susceptibility among tested cancer cells. Blackberry, cherry, raspberry and blackcurrant wines in the volume ratio of 10 and 20 % showed to be the most effective anti-proliferative agents, with higher susceptibility in HeLa and MCF-7 cells than CaCo-2 cells.

Design and analysis of MEMS MWCNT / epoxy strain sensor using ...

Indian Academy of Sciences (India)

Gaurav Sapra

2017-06-20

Jun 20, 2017 ... In this paper, highly sensitive MEMS-based multi- walled (MWCNT)/epoxy strain sensor has been designed using ... This paper also discusses the process flow for fabricating MWCNT/epoxy thin film ... stone bridge, i.e., connected to the gold metal pad of the sensor. The change in resistance with respect to.

Phenols removal by immobilized tyrosinase reactor in on-line high performance liquid chromatography

Energy Technology Data Exchange (ETDEWEB)

Girelli, Anna Maria [Dipartimento di Chimica, Universita degli Studi di Roma ' La Sapienza' , P.le Aldo Moro 5, 00185 Rome (Italy)]. E-mail: annamaria.girelli@uniroma1.it; Mattei, Enrico [Dipartimento di Chimica, Universita degli Studi di Roma ' La Sapienza' , P.le Aldo Moro 5, 00185 Rome (Italy); Messina, Antonella [Dipartimento di Chimica, Universita degli Studi di Roma ' La Sapienza' , P.le Aldo Moro 5, 00185 Rome (Italy)

2006-11-24

The development of an immobilized enzyme reactor (IMER) based on tyrosinase immobilized on aminopropyl-controlled pore glass (AP-CPG) for the removal of phenols from model aqueous solutions was reported. To elucidate the influence of the substrate nature, the apparent (V{sup '}{sub max}, K{sup '}{sub m}) and the inherent (V{sub max}, K{sub m}) Michaelis-Menten constants were determined by Lineweaver-Burk method and the external diffusional contributions on measured enzyme activities were removed by a graphical method. The dephenolization process was realized by recycling the phenol solutions through the bioreactor connected to a chitosan trap in order to remove the colored quinone-type products of the tyrosinase reactions. The results indicated that a complete removal of phenol derivatives in the range of 150-300min, with the exception of 60% removal for phenol reached in 400min, was obtained. The observed sequence: cresol>4-methylcathecol>catechol>4-Cl-phenol-bar phenol was in accordance to the V{sup '}{sub max}/K{sup '}{sub m} values.

Morphological Study on Room-Temperature-Cured PMMA-Grafted Natural Rubber-Toughened Epoxy/Layered Silicate Nanocomposite

OpenAIRE

Yuhana, N. Y.; Ahmad, S.; Kamal, M. R.; Jana, S. C.; Bahri, A. R. Shamsul

2012-01-01

A morphological study was conducted on ternary systems containing epoxy, PMMA-grafted natural rubber, and organic chemically modified montmorillonite (Cloisite 30B). Optical microscopy, transmission electron microscopy (TEM), scanning electron microscopy (SEM), energy dispersive X-ray (EDX), and wide-angle X-ray diffraction (WAXD) analysis were used. The following four materials were prepared at room temperature: cured unmodified epoxy, cured toughened epoxy, cured unmodified epoxy/Cloisite 3...

Relationship between red wine grades and phenolics. 1. Tannin and total phenolics concentrations.

Science.gov (United States)

Mercurio, Meagan D; Dambergs, Robert G; Cozzolino, Daniel; Herderich, Markus J; Smith, Paul A

2010-12-08

Measuring chemical composition is a common approach to support decisions about allocating foods and beverages to grades related to market value. Red wine is a particularly complex beverage, and multiple compositional attributes are needed to account for its sensory properties, including measurement of key phenolic components such as anthocyanins, total phenolics, and tannin, which are related to color and astringency. Color has been shown to relate positively to red wine grade; however, little research has been presented that explores the relationship between astringency-related components such as total phenolic or tannin concentration and wine grade. The aim of this research has been to investigate the relationship between the wine grade allocations of commercial wineries and total phenolic and tannin concentrations, respectively, in Australian Shiraz and Cabernet Sauvignon wines. Total phenolic and tannin concentrations were determined using the methyl cellulose precipitable (MCP) tannin assay and then compared to wine grade allocations made by winemaker panels during the companies' postvintage allocation process. Data were collected from wines produced by one Australian wine company over the 2005, 2006, and 2007 vintages and by a further two companies in 2007 (total wines = 1643). Statistical analysis revealed a positive trend toward higher wine grade allocation and wines that had higher concentrations of both total phenolics and tannin, respectively. This research demonstrates that for these companies, in general, Cabernet Sauvignon and Shiraz wines allocated to higher market value grades have higher total phenolics and higher tannin concentrations and suggests that these compositional parameters should be considered in the development of future multiparameter decision support systems for relevant commercial red wine grading processes. In addition, both tannin and total phenolics would ideally be included because although, in general, a positive relationship

Improvement of the piezoelectric properties of glass fiber-reinforced epoxy composites by poling treatment

International Nuclear Information System (INIS)

Oh, S M; Hwang, H Y

2013-01-01

Recently, a new non-destructive method has been proposed for damage monitoring of glass fiber-reinforced polymer composite materials using the piezoelectric characteristics of a polymeric matrix. Several studies of the piezoelectric properties of unidirectional glass fiber epoxy composites and damage monitoring of double-cantilever beams have supported the claim that the piezoelectric method is feasible and powerful enough to monitor the damage of glass fiber epoxy composites. Generally, conventional piezoelectric materials have higher piezoelectric characteristics through poling treatment. In this work, we investigated the change of the piezoelectric properties of glass fiber-reinforced epoxy composites before and after poling treatment. The piezoelectric constants (d 33 ) of glass fiber-reinforced epoxy composites increased by more than 400%. Also, x-ray diffraction tests revealed that poling treatment changed the degree of crystallinity of the epoxy matrix, and this led to the improvement of the piezoelectric characteristics of glass fiber-reinforced epoxy composites. (paper)

UV curing silicon-containing epoxy resin and its glass cloth reinforced composites

International Nuclear Information System (INIS)

Yang Guang; Tang Zhuo; Huang Pengcheng

2007-01-01

A UV-curable cationic silicon-containing epoxy resin formulation was developed. The gel conversion of the cured resin after 10-min UV irradiation reached 80% in the presence of 5% diaryliodonium salt photoinitiator and 5.5% polyol chain transfer agent by cationic ring-opening polymerization. The glass cloth-reinforced composites were fabricated with the silicon-containing epoxy resin using the wet lay-up technique and UV irradiation. The mechanical properties of the composites were evaluated. Compared with glass cloth reinforced bisphenol A epoxy resin matrix composites, the silicon-containing epoxy resin matrix composites possessed higher tensile strength and interlayer shear strength which was 158.5MPa and 9.9MPa respectively while other mechanical properties such as flexural property and tensile modulus were similar. (authors)

The reactivity of natural phenols

Energy Technology Data Exchange (ETDEWEB)

Denisov, Evgenii T; Denisova, Taisa G [Institute of Problems of Chemical Physics, Russian Academy of Sciences, Chernogolovka, Moscow Region (Russian Federation)

2009-11-30

This review surveys physicochemical data of natural phenols published in recent years. The structures of some compounds of this class are given. A complete set of the dissociation energies of the O-H bonds for 71 natural phenols is presented. Kinetic characteristics of the reactions of peroxyl, alkyl and thiyl radicals with natural phenols, exchange reactions of phenoxyl radicals with phenols and reactions of phenoxyl radicals with lipids, hydroperoxides, cysteine and ascorbic acid are compiled and described systematically. The reactivity of phenols in radical reactions and the factors that determine the reactivity (the enthalpy of reaction, triplet repulsion, the electronegativities of atoms at the reaction centre, the presence of pi-electrons adjacent to the reaction centre, the radii of atoms at the reaction centre, steric hindrance, the force constants of the reacting bonds) are discussed. An important role of hydrogen bonding between surrounding molecules and the OH groups of natural phenols in decreasing their reactivities is noted.

Bromination of Phenol

Science.gov (United States)

Talbot, Christopher

2013-01-01

This "Science note" examines the bromination of phenol, a reaction that is commonly taught at A-level and IB (International Baccalaureate) as an example of electrophilic substitution. Phenol undergoes bromination with bromine or bromine water at room temperature. A white precipitate of 2,4,6-tribromophenol is rapidly formed. This…

Velocity Measurement of ultrasonic for evaluation of aging epoxy coating in containment structure of nuclear power plant

International Nuclear Information System (INIS)

Eun, Gil Soo; Kim, Noh Yu; Nah, Hwan Seon; Song, Young Chol

2001-01-01

Relative variation of ultrasonic velocity in aging epoxy coating in nuclear plant is measured for evaluation of the degradation of the epoxy coating. Time delay for ultrasound to travel through the epoxy film due to change of ultrasonic velocity is measured indirectly using ultrasonic interferometry which compares two reflection waves from the same point of coating surface at two different distances. Magnitude of the difference of two waves increases or decreases depending on change of the time of flight of ultrasound in the epoxy film caused by heat damage in the epoxy coating. Based on the transfer functions of the wedge and the epoxy coating in frequency domain, the reflection wave is analyzed and related to the velocity of ultrasound in the epoxy coating. A specially designed conical wedge is adopted to minimize the waviness effect of the surface of the epoxy coating. Epoxy films are fabricated, degraded under the accelerated aging conditions and tested to evaluate the change of ultrasonic velocity in the films. The experimental results show that the method can be applied to evaluate quantitatively the sealing quality of the epoxy coating.

Organocatalyzed Domino [3+2] Cycloaddition/Payne-Type Rearrangement using Carbon Dioxide and Epoxy Alcohols.

Science.gov (United States)

Kleij, Arjan Willem; Sopeña, Sergio; Cozzolino, Mariachiara; Escudero-Adán, Eduardo C; Martínez Belmonte, Marta; Maquilón, Cristina

2018-05-09

An unprecedented organocatalytic approach towards highly substituted cyclic carbonates from tri- and tetra-substituted oxiranes and carbon dioxide has been developed. The protocol involves the use of a simple and cheap superbase under mild, additive- and metal-free conditions towards the initial formation of a less substituted carbonate product that equilibrates to a tri- or even tetra-substituted cyclic carbonate under thermodynamic control. The latter are conveniently trapped in situ providing overall a new domino process for synthetically elusive heterocyclic scaffolds. Control experiments provide a rationale for the observed cascade reactions, which demonstrate high similarity with the well-known Payne rearrangement of epoxy alcohols. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Syntheses and characterization of novel P/Si polysilsesquioxanes/epoxy nanocomposites

International Nuclear Information System (INIS)

Chiu Yiechan; Liu Fangyi; Ma, C.-C.M.; Chou, I.-C.; Riang Linawati; Chiang, C.-L.; Yang, J.-C.

2008-01-01

Phosphorus-containing polysilsesquioxane (PSSQ) was introduced into diglycidyl ether of bisphenol A epoxy (DGEBA) to generate a novel P/Si PSSQ nanocomposite. A series of nanocomposites was fabricated by changing the content of the 2-(diphenylphosphino)ethyltriethoxysilane (DPPETES) monomer or P/Si PSSQ cured with DGEBA epoxy and modified epoxy. The structure, thermal properties and flame-retardancy of the P/Si PSSQ nanocomposites were characterized by FT-IR, solid-state 29 Si NMR, thermogravimetric analysis (TGA) and limited oxygen index (LOI) instruments. The nano-sizes of the particles in P/Si PSSQ were approximately 30-50 nm, and the polarity of nanocomposites might generate the nanophase-separated structure from transmission electron microscopy (TEM). The urethane-like side group of the modified epoxy and the fabrication of oligomers in the curing reaction affected the T d5 values of nanocomposites. TGA and LOI results indicated that the char yield (29 wt%) increased and the nanocomposites were not very flammable (LOI = 30). The hybrid materials also exhibited high thermal stability, good flame-retardance and a lack of phase separation

How to Plant Apple Trees to Reduce Replant Disease in Apple Orchard: A Study on the Phenolic Acid of the Replanted Apple Orchard.

Directory of Open Access Journals (Sweden)

Chengmiao Yin

Full Text Available Apple replant disease (ARD is an important problem in the production of apple. The phenolic acid is one of the causes of ARD. How phenolic acid affects the ARD was not well known. In this study, we analyzed the type, concentration and annual dynamic variation of phenolic acid in soil from three replanted apple orchards using an accelerated solvent extraction system with high performance liquid chromatography (ASE-HPLC. We found that the type and concentration of phenolic acid were significantly differed among different seasons, different sampling positions and different soil layers. Major types of phenolic acid in three replanted apple orchards were phlorizin, benzoic acid and vanillic aldehyde. The concentration of phenolic acid was highest in the soil of the previous tree holes and it was increased from the spring to autumn. Moreover, phenolic acid was primarily distributed in 30-60 cm soil layer in the autumn, while it was most abundant in 0-30 cm soil layer in the spring. Our results suggest that phlorizin, benzoic acid and vanillic aldehyde may be the key phenolic acid that brought about ARD in the replanted apple orchard.

Mechanical, Thermal, and Electrical Properties of Graphene-Epoxy Nanocomposites—A Review

Directory of Open Access Journals (Sweden)

Rasheed Atif

2016-08-01

Full Text Available Monolithic epoxy, because of its brittleness, cannot prevent crack propagation and is vulnerable to fracture. However, it is well established that when reinforced—especially by nano-fillers, such as metallic oxides, clays, carbon nanotubes, and other carbonaceous materials—its ability to withstand crack propagation is propitiously improved. Among various nano-fillers, graphene has recently been employed as reinforcement in epoxy to enhance the fracture related properties of the produced epoxy–graphene nanocomposites. In this review, mechanical, thermal, and electrical properties of graphene reinforced epoxy nanocomposites will be correlated with the topographical features, morphology, weight fraction, dispersion state, and surface functionalization of graphene. The factors in which contrasting results were reported in the literature are highlighted, such as the influence of graphene on the mechanical properties of epoxy nanocomposites. Furthermore, the challenges to achieving the desired performance of polymer nanocomposites are also suggested throughout the article.

Seawater infiltration effect on thermal degradation of fiber reinforced epoxy composites

Science.gov (United States)

Ibrahim, Mohd Haziq Izzuddin bin; Hassan, Mohamad Zaki bin; Ibrahim, Ikhwan; Rashidi, Ahmad Hadi Mohamed; Nor, Siti Fadzilah M.; Daud, Mohd Yusof Md

2018-05-01

Seawater salinity has been associated with the reduction of polymer structure durability. The aim of this study is to investigate the change in thermal degradation of fiber reinforced epoxy composite due to the presence of seawater. Carbon fiber, carbon/kevlar, fiberglass, and jute that reinforced with epoxy resin was laminated through hand-layup technique. Initially, these specimen was sectioned to 5×5 mm dimension, then immersed in seawater and distilled water at room temperature until it has thoroughly saturated. Following, the thermal degradation analysis using Differential Scanning Calorimetry (DSC), the thermic changes due to seawater infiltration was defined. The finding shows that moisture absorption reduces the glass transition temperature (Tg) of fiber reinforced epoxy composite. However, the glass transition temperature (Tg) of seawater infiltrated laminate composite is compareable with distilled water infiltrated laminate composite. The carbon fiber reinfored epoxy has the highest glass transition temperature out of all specimen.

Techniques for Analysis of Plant Phenolic Compounds

Directory of Open Access Journals (Sweden)

Thomas H. Roberts

2013-02-01

Full Text Available Phenolic compounds are well-known phytochemicals found in all plants. They consist of simple phenols, benzoic and cinnamic acid, coumarins, tannins, lignins, lignans and flavonoids. Substantial developments in research focused on the extraction, identification and quantification of phenolic compounds as medicinal and/or dietary molecules have occurred over the last 25 years. Organic solvent extraction is the main method used to extract phenolics. Chemical procedures are used to detect the presence of total phenolics, while spectrophotometric and chromatographic techniques are utilized to identify and quantify individual phenolic compounds. This review addresses the application of different methodologies utilized in the analysis of phenolic compounds in plant-based products, including recent technical developments in the quantification of phenolics.

Interfacial Strength and Physical Properties of Functionalized Graphene - Epoxy Nanocomposites

Science.gov (United States)

Miller, Sandi G.; Heimann, Paula; Scheiman, Daniel; Adamson, Douglas H.; Aksay, Iihan A.; Prud'homme, Robert K.

2006-01-01

The toughness and coefficient of thermal expansion of a series of functionalized graphene sheet - epoxy nanocomposites are investigated. Functionalized graphene sheets are produced by splitting graphite oxide into single graphene sheets through a rapid thermal expansion process. These graphene sheets contain approx. 10% oxygen due to the presence of hydroxide, epoxide, and carboxyl functional groups which assist in chemical bond formation with the epoxy matrix. Intrinsic surface functionality is used to graft alkyl amine chains on the graphene sheets, and the addition of excess hardener insures covalent bonding between the epoxide matrix and graphene sheets. Considerable improvement in the epoxy dimensional stability is obtained. An increase in nanocomposite toughness is observed in some cases.

Influence of Water Absorption on Volume Resistivity and the Dielectric Properties of Neat Epoxy Material

KAUST Repository

Sulaimani, Anwar Ali

2014-07-15

Influence of Water Absorption on the Dielectric Properties and Volume Resistivity of Neat Epoxy Material Anwar Ali Sulaimani Epoxy resins are widely used materials in the industry as electrical insulators, adhesives and in aircrafts structural components because of their high mechanical sti ness, strength and high temperature and chemical resistance properties. But still, the in uence of water uptake due to moisture adsorption is not fully understood as it detrimentally modi es the electrical and chemical properties of the material. Here, we investigate the in uence of water moisture uptake on the neat epoxy material by monitoring the change in the volume resistivity and dielectric properties of epoxy material at three di erent thickness con gurations: 0.250 mm, 0.50 mm and 1 mm thicknesses. Gravimetric analysis was done to monitor the mass uptake behaviour, Volume Resistivity was measured to monitor the change in conductivity of the material, and the dielectric properties were mapped to characterise the type of water mechanism available within the material during two ageing processes of sorption and desorption. Two-stage behaviours of di usion and reaction have been identi ed by the mass uptake analysis. Moreover, the plot of volume resistivity versus mass uptake has indi- cated a non-uniform relationship between the two quantities. However, the analysis of the dielectric spectrum at medium range of frequency and time has showed a change 5 in the dipolar activities and also showed the extent to which the water molecules can be segregated between bounding to the resin or existing as free water.

Isothermal and non-isothermal cure of a tri-functional epoxy resin (TGAP): A stochastic TMDSC study

International Nuclear Information System (INIS)

Hutchinson, John M.; Shiravand, Fatemeh; Calventus, Yolanda; Fraga, Iria

2012-01-01

Highlights: ► First evaluation of T g of tri-functional epoxy resin TGAP by DSC. ► Clearly shows advantages of TOPEM for isothermal and non-isothermal cure analysis. ► Evidence of highly non-linear enthalpy relaxation in partially cured TGAP system. - Abstract: The isothermal cure of a highly reactive tri-functional epoxy resin, tri-glycidyl para-amino phenol (TGAP), with diamino diphenyl sulphone (DDS), at two different cure temperatures T c has been studied by both conventional differential scanning calorimetry (DSC) and by a stochastic temperature modulated DSC technique, TOPEM. From a series of isothermal cure experiments for increasing cure times, the glass transition temperature T g as a function of isothermal cure time is determined by conventional DSC from a second (non-isothermal) scan, and the vitrification time t v is obtained as the time at which T g = T c . In parallel, TOPEM experiments at the same T c lead directly to the determination of t v from the sigmoidal change in the quasi-static heat capacity. It is not possible to identify the glass transition temperature of the fully cured system, T g∞ , in a third scan by conventional DSC. In contrast, with TOPEM a second (non-isothermal) scan at 2 K/min after the isothermal cure gives rise to three separate transitions: devitrification of the partially cured and vitrified material; almost immediate vitrification as the T g of the system again rises; finally another devitrification, at a temperature approximating closely to T g∞ . Thus with TOPEM it is possible to obtain a calorimetric measure of the glass transition temperature of this fully cured system.

Mechanical properties of ramie fiber reinforced epoxy lamina composite for socket prosthesis

Directory of Open Access Journals (Sweden)

Tresna Soemardi

2010-10-01

Full Text Available This paper presents an investigation into the application of natural fiber composite especially ramie fiber reinforced epoxy lamina composite for socket prosthesis. The research focuses on the tensile and shear strength from ramie fiber reinforced epoxy lamina composite which will be applied as alternative material for socket prosthesis. The research based on American Society for Testing Material (ASTM standard D 3039/D 3039M for tensile strength and ASTM D 4255/D 4255M-83 for shear strength. The ramie fiber applied is a fiber continue 100 % Ne14'S with Epoxy Resin Bakelite EPR 174 as matrix and Epoxy Hardener V-140 as hardener. The sample composite test made by hand lay up method. Multiaxial characteristic from ramie fiber reinforced epoxy composite will be compared with ISO standard for plastic/polymer for health application and refers strength of material application at Prosthetics and Orthotics. The analysis was completed with the mode of the failure and the failure criterion observation by using Scanning Electron Microscope (SEM. Based on results of the research could be concluded that ramie fiber reinforced epoxy composite could be developed further as the alternative material for socket prosthesis on Vf 40-50%. Results of the research will be discussed in more detail in this paper.

Occupational contact dermatitis caused by aniline epoxy resins in the aircraft industry.

Science.gov (United States)

Pesonen, Maria; Suuronen, Katri; Jolanki, Riitta; Aalto-Korte, Kristiina; Kuuliala, Outi; Henriks-Eckerman, Maj-Len; Valtanen, Ilona; Alanko, Kristiina

2015-08-01

Tetraglycidyl-4,4'-methylenedianiline (TGMDA) is an aniline epoxy resin used in, for example, resin systems of pre-impregnated composite materials (prepregs) of the aircraft industry. Allergic contact dermatitis caused by TGMDA in prepregs has been described previously. To report on 9 patients with occupational allergic contact dermatitis caused by TGMDA in epoxy glues used in helicopter assembly. The patients were examined with patch testing at the Finnish Institute of Occupational Health in 2004-2009. The first patient was diagnosed by testing both components of two epoxy glues from the workplace, and was also tested with glue ingredients, including TGMDA. The following patients were tested with the glues and TGMDA. The resin parts of the glues were analysed for their epoxy compounds, including TGMDA. All of the patients had a patch test reaction to one or both of the resin parts of the TGMDA-containing glues. Eight of them had a strong allergic reaction to TGMDA, and one had a doubtful reaction to TGMDA. Two of the patients also had an allergic reaction to triglycidyl-p-aminophenol (TGPAP), another aniline epoxy resin, which was not present in the TGMDA-containing glues. In aircraft industry workers with suspected occupational dermatitis, aniline epoxy resins should be considered and patch tested as possible contact allergens. © 2015 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

Novel Formulations of Phase Change Materials—Epoxy Composites for Thermal Energy Storage

Science.gov (United States)

Alvarez Feijoo, Miguel Angel

2018-01-01

This research aimed to evaluate the thermal properties of new formulations of phase change materials (PCMs)-epoxy composites, containing a thickening agent and a thermally conductive phase. The composite specimens produced consisted of composites fabricated using (a) inorganic PCMs (hydrated salts), epoxy resins and aluminum particulates or (b) organic PCM (paraffin), epoxy resins, and copper particles. Differential Scanning Calorimetry (DSC) was used to analyze the thermal behavior of the samples, while hardness measurements were used to determine changes in mechanical properties at diverse PCM and conductive phase loading values. The results indicate that the epoxy matrix can act as a container for the PCM phase without hindering the heat-absorbing behavior of the PCMs employed. Organic PCMs presented reversible phase transformations over multiple cycles, an advantage that was lacking in their inorganic counterparts. The enthalpy of the organic PCM-epoxy specimens increased linearly with the PCM content in the matrix. The use of thickening agents prevented phase segregation issues and allowed the fabrication of specimens containing up to 40% PCM, a loading significantly higher than others reported. The conductive phase seemed to improve the heat transfer and the mechanical properties of the composites when present in low percentages (phase combination (PCM + epoxy resin + hardener + thickening agent) presents great potential as a heat-absorbing material at the temperatures employed. PMID:29373538

Synthesis and characterisation of epoxy resins reinforced with carbon nanotubes and nanofibers.

Science.gov (United States)

Prolongo, S G; Gude, M R; Ureña, A

2009-10-01

Epoxy nanocomposites were fabricated using two kinds of nanofiller, amino-functionalized multi-walled carbon nanotubes (CNTs) and non-treated long carbon nanofibers (CNFs). The non-cured mixtures were analysed through viscosity measurements. The effect of the nanoreinforcement on the curing process was determined by differential scanning calorimetry. Finally, the characterisation of cured nanocomposites was carried out studying their thermo-mechanical and electrical behaviour. At room temperature, the addition of CNTs causes a viscosity increase of epoxy monomer much more marked than the introduction of CNFs due to their higher specific area. It was probed that in that case exists chemical reaction between amino-functionalized CNTs and the oxirane rings of epoxy monomer. The presence of nanoreinforcement induces a decrease of curing reaction rate and modifies the epoxy conversion reached. The glass transition temperature of the nanocomposites decreases with the contents of CNTs and CNFs added, which could be related to plasticization phenomena of the nanoreinforcements. The storage modulus of epoxy resin significantly increases with the addition of CNTs and CNFs. This augment is higher with amino-functionalized CNTs due, between other reasons, to the stronger interaction with the epoxy matrix. The electrical conductivity is greatly increased with the addition of CNTs and CNFs. In fact, the percolation threshold is lower than 0.25 wt% due to the high aspect ratio of the used nanoreinforcements.

Adhesion of epoxy primer to hydrotalcite conversion coated AA2024

Science.gov (United States)

Leggat, Robert Benton, III

Hydrotalcite-based (HT) conversion coatings are being developed as an environmentally benign alternative to chromate conversion coatings (CCC). Accelerated exposure tests were conducted on epoxy primed, HT-modified AA2024 to gauge service performance. HT-based conversion coatings did not perform as well as the CCC when used with an epoxy primer. The current HT chemistries are optimized for stand-alone corrosion protection, however additional research into the primer/HT interactions is necessary before they can be implemented within a coating scheme. The relative contribution of mechanical and physico-chemical interactions in controlling adhesion has been investigated in this study. Practical adhesion tests were used to assess the dry and wet bond strength of epoxy primer on HT coatings using the pull-off tensile strength (POTS) as the figure of merit. The practical adhesion of HT coated samples generally fell between that observed for the CCC and bare AA2024. Laboratory testing was done to assess the physical and chemical properties of HT coatings. Contact angle measurements were performed using powders representative of different HT chemistries to evaluate the dispersive and acid-base character of the surface. The wet POTS correlated with the electrodynamic (dipole + dispersive) parameter of the surface tension. The HT surfaces were found to be predominantly basic. Given the basicity of epoxy, these results indicate that increasing the acidic character of HT coatings may increase the adhesion performance. This was supported by electrokinetic measurements in which the dry POTS was found to increase with decreasing conversion coating iso-electric point. The correlations with the dry and wet state adhesion are interpreted as indicating that dry state adhesion is optimized by minimizing unfavorable polar interactions between the basic epoxy and HT interfaces. Wet state adhesion, where polar interactions are disrupted, is dictated by non-polar bonding. FTIR

Fabrication of tough epoxy with shape memory effects by UV-assisted direct-ink write printing.

Science.gov (United States)

Chen, Kaijuan; Kuang, Xiao; Li, Vincent; Kang, Guozheng; Qi, H Jerry

2018-03-07

3D printing of epoxy-based shape memory polymers with high mechanical strength, excellent thermal stability and chemical resistance is highly desirable for practical applications. However, thermally cured epoxy in general is difficult to print directly. There have been limited numbers of successes in printing epoxy but they suffer from relatively poor mechanical properties. Here, we present an ultraviolet (UV)-assisted 3D printing of thermally cured epoxy composites with high tensile toughness via a two-stage curing approach. The ink containing UV curable resin and epoxy oligomer is used for UV-assisted direct-ink write (DIW)-based 3D printing followed by thermal curing of the part containing the epoxy oligomer. The UV curable resin forms a network by photo polymerization after the 1st stage of UV curing, which can maintain the printed architecture at an elevated temperature. The 2nd stage thermal curing of the epoxy oligomer yields an interpenetrating polymer network (IPN) composite with highly enhanced mechanical properties. It is found that the printed IPN epoxy composites enabled by the two-stage curing show isotropic mechanical properties and high tensile toughness. We demonstrated that the 3D-printed high-toughness epoxy composites show good shape memory properties. This UV-assisted DIW 3D printing via a two-stage curing method can broaden the application of 3D printing to fabricate thermoset materials with enhanced tensile toughness and tunable properties for high-performance and functional applications.

Phenolics and Plant Allelopathy

Directory of Open Access Journals (Sweden)

De-An Jiang

2010-12-01

Full Text Available Phenolic compounds arise from the shikimic and acetic acid (polyketide metabolic pathways in plants. They are but one category of the many secondary metabolites implicated in plant allelopathy. Phenolic allelochemicals have been observed in both natural and managed ecosystems, where they cause a number of ecological and economic problems, such as declines in crop yield due to soil sickness, regeneration failure of natural forests, and replanting problems in orchards. Phenolic allelochemical structures and modes of action are diverse and may offer potential lead compounds for the development of future herbicides or pesticides. This article reviews allelopathic effects, analysis methods, and allelopathic mechanisms underlying the activity of plant phenolic compounds. Additionally, the currently debated topic in plant allelopathy of whether catechin and 8-hydroxyquinoline play an important role in Centaurea maculata and Centaurea diffusa invasion success is discussed. Overall, the main purpose of this review is to highlight the allelopacthic potential of phenolic compounds to provide us with methods to solve various ecology problems, especially in regard to the sustainable development of agriculture, forestry, nature resources and environment conservation.

Improving Fracture Toughness of Epoxy Nanocomposites by Silica Nanoparticles

Directory of Open Access Journals (Sweden)

Seyed Reza Akherati Sany

2017-04-01

Full Text Available An epoxy resin was modified by silica nanoparticles and cured with an anhydride. The particles with different batches of 12, 20, and 40 nm sizes were each distributed into the epoxy resin ultrasonically. Electron microscopy images showed that the silica particles were well dispersed throughout the resin. Tensile test results showed that Young’s modulus and tensile strength increased with the volume fraction and surface area of the silica particles. The simultaneous use of two average sizes of 20 and 40 nm diameter silica particles still increased these mechanical properties but other combinations of silica particles were unsuccessful. A three-point bending test on each pre-cracked specimen was performed to measure the mode I fracture toughness energy. The fracture energy increased from 283 J/m2 for the unmodified epoxy to about 740 J/m2 for the epoxy with 4.5 wt% of 12 nm diameter silica nanoparticles. The fracture energy of smaller particles was greater because of their higher surface to volume ratio. The fracture energy results showed also that the combined nanoparticles has a synergic effect on the fracture toughness of nanocomposites. Simultaneous use of 10 and 20 nm particles increased the fracture energy to about 770 J/m2. Finally, crack-opening displacement was calculated and found to be in the range of several micrometers which was much larger than the sizes of particles studied. Thus, the toughening mechanisms of crack pinning and crack deflection have a negligible effect on improvement of toughness, nevertheless, the plastic deformation and plastic void growth are dominant mechanisms in epoxy toughening by nanoparticles.

Preparation and optical properties of indium tin oxide/epoxy nanocomposites with polyglycidyl methacrylate grafted nanoparticles.

Science.gov (United States)

Tao, Peng; Viswanath, Anand; Schadler, Linda S; Benicewicz, Brian C; Siegel, Richard W

2011-09-01

Visibly highly transparent indium tin oxide (ITO)/epoxy nanocomposites were prepared by dispersing polyglycidyl methacrylate (PGMA) grafted ITO nanoparticles into a commercial epoxy resin. The oleic acid stabilized, highly crystalline, and near monodisperse ITO nanoparticles were synthesized via a nonaqueous synthetic route with multigram batch quantities. An azido-phosphate ligand was synthesized and used to exchange with oleic acid on the ITO surface. The azide terminal group allows for the grafting of epoxy resin compatible PGMA polymer chains via Cu(I) catalyzed alkyne-azide "click" chemistry. Transmission electron microscopy (TEM) observation shows that PGMA grafted ITO particles were homogeneously dispersed within the epoxy matrix. Optical properties of ITO/epoxy nanocomposites with different ITO concentrations were studied with an ultraviolet-visible-near-infrared (UV-vis-NIR) spectrometer. All the ITO/epoxy nanocomposites show more than 90% optical transparency in the visible light range and absorption of UV light from 300 to 400 nm. In the near-infrared region, ITO/epoxy nanocomposites demonstrate low transmittance and the infrared (IR) transmission cutoff wavelength of the composites shifts toward the lower wavelength with increased ITO concentration. The ITO/epoxy nanocomposites were applied onto both glass and plastic substrates as visibly transparent and UV/IR opaque optical coatings.

Immobilization of spent resin with epoxy resin

International Nuclear Information System (INIS)

Gultom, O.; Suryanto; Sayogo; Ramdan

1997-01-01

immobilization of spent resin using epoxy resin has been conducted. The spent resin was mixtured with epoxy resin in variation of concentration, i.e., 30, 40, 50, 60, 70 weight percent of spent resin. The mixture were pour into the plastic tube, with a diameter of 40 mm and height of 40 mm. The density, compressive strength and leaching rate were respectively measured by quanta chrome, paul weber apparatus and gamma spectrometer. The results showed that the increasing of waste concentration would be decreased the compressive strength, and increased density by immobilized waste. The leaching rate of 137 Cs from waste product was not detected in experiment (author)

High T{sub g} and fast curing epoxy-based anisotropic conductive paste for electronic packaging

Energy Technology Data Exchange (ETDEWEB)

Keeratitham, Waralee, E-mail: waralee.ke@student.chula.ac.th; Somwangthanaroj, Anongnat, E-mail: anongnat.s@chula.ac.th [Department of Chemical Engineering, Faculty of Engineering, Chulalongkorn University, Bangkok, 10330 (Thailand)

2016-03-09

Herein, our main objective is to prepare the fast curing epoxy system with high glass transition temperature (T{sub g}) by incorporating the multifunctional epoxy resin into the mixture of diglycidyl ether of bisphenol A (DGEBA) as a major epoxy component and aromatic diamine as a hardener. Furthermore, the curing behavior as well as thermal and thermomechanical properties were investigated by differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA) and thermomechanical analysis (TMA). It was found that T{sub g} obtained from tan δ of DGEBA/aromatic diamine system increased from 100 °C to 205 °C with the presence of 30 percentage by weight of multifunctional epoxy resin. Additionally, the isothermal DSC results showed that the multifunctional epoxy resin can accelerate the curing reaction of DGEBA/aromatic diamine system. Namely, a high degree of curing (∼90%) was achieved after a few minutes of curing at low temperature of 130 °C, owing to a large number of epoxy ring of multifunctional epoxy resin towards the active hydrogen atoms of aromatic diamine.

Nanocellulose composites with enhanced interfacial compatibility and mechanical properties using a hybrid-toughened epoxy matrix.

Science.gov (United States)

Kuo, Pei-Yu; Barros, Luizmar de Assis; Yan, Ning; Sain, Mohini; Qing, Yan; Wu, Yiqiang

2017-12-01

Although there is a growing interest in utilizing nanocellulose fibres (NCFs) based composites for achieving a higher sustainability, mechanical performance of these composites is limited due to the poor compatibility between fibre reinforcement and polymer matrices. Here we developed a bio-nanocomposite with an enhanced fibre/resin interface using a hybrid-toughened epoxy. A strong reinforcing effect of NCFs was achieved, demonstrating an increase up to 88% in tensile strength and 298% in tensile modulus as compared to neat petro-based P-epoxy. The toughness of neat P-epoxy was improved by 84% with the addition of 10wt% bio-based E-epoxy monomers, which also mitigated the amount of usage of bisphenol A (BPA). The morphological analyses showed that the hybrid epoxy improved the resin penetration and fibre distribution significantly in the resulting composites. Thus, our findings demonstrated the promise of developing sustainable and high performance epoxy composites combing NCFs with a hybrid petro-based and bio-based epoxy resin system. Copyright © 2017 Elsevier Ltd. All rights reserved.

Evaluation of Carbon Composite Overwrap Pressure Vessels Fabricated Using Ionic Liquid Epoxies

Data.gov (United States)

National Aeronautics and Space Administration — In terms of "Innovation" this is a unique epoxy with unique properties, and NASA co-holds the patent. This epoxy is being exclusively formulated for cryogenic use....

How to Plant Apple Trees to Reduce Replant Disease in Apple Orchard: A Study on the Phenolic Acid of the Replanted Apple Orchard

OpenAIRE

Yin, Chengmiao; Xiang, Li; Wang, Gongshuai; Wang, Yanfang; Shen, Xiang; Chen, Xuesen; Mao, Zhiquan

2016-01-01

Apple replant disease (ARD) is an important problem in the production of apple. The phenolic acid is one of the causes of ARD. How phenolic acid affects the ARD was not well known. In this study, we analyzed the type, concentration and annual dynamic variation of phenolic acid in soil from three replanted apple orchards using an accelerated solvent extraction system with high performance liquid chromatography (ASE-HPLC). We found that the type and concentration of phenolic acid were significa...

Degradation of modified carbon black/epoxy nanocomposite coatings under ultraviolet exposure

Science.gov (United States)

Ghasemi-Kahrizsangi, Ahmad; Shariatpanahi, Homeira; Neshati, Jaber; Akbarinezhad, Esmaeil

2015-10-01

Degradation of epoxy coatings with and without Carbon Black (CB) nanoparticles under ultraviolet (UV) radiation were investigated using electrochemical impedance spectroscopy (EIS). Sodium dodecyl sulfate (SDS) was used to obtain a good dispersion of CB nanoparticles in a polymer matrix. TEM analysis proved a uniform dispersion of modified CB nanoparticles in epoxy coating. The coatings were subjected to UV radiation to study the degradation behavior and then immersed in 3.5 wt% NaCl. The results showed that the electrochemical behavior of neat epoxy coating was related to the formation and development of microcracks on the surface. The occurrence of microcracks on the surface of the coatings and consequently the penetration of ionic species reduced by adding CB nanoparticles into the formulation of the coatings. CB nanoparticles decreased degradation of CB coatings by absorbing UV irradiation. The ATR-FTIR results showed that decrease in the intensity of methyl group as main peak in presence of 2.5 wt% CB was lower than neat epoxy. In addition, the reduction in impedance of neat epoxy coating under corrosive environment was larger than CB coatings. The CB coating with 2.5 wt% nanoparticles had the highest impedance to corrosive media after 2000 h UV irradiation and 24 h immersion in 3.5 wt% NaCl.

Physical and chemical durability of cement impregnated epoxy resin

International Nuclear Information System (INIS)

Suryantoro

1997-01-01

Immobilization of simulation radioactive waste contains Cs and Sr with cement impregnated epoxy resin has been done. Low level liquid waste in 30% weight mixed cement homogeneously and then set in its curing time about 28 days. Waste from was impregnated with epoxy resin (Bisphenol-A-diglycidylether) and use Triethylenteramin as catalyst. the sample of cement impregnated epoxy resin 2.5 cm x 2.5 cm in diameter and length was tested by Paul Weber. The compressive strength was obtained of 4.08 kN.cm - 2. The sochxlet apparatus was run on flow rate of 300 ml/hour at 100 o C and during 24 hours. The leaching rate of Cs was round on 5.5 x 10 - 4 g.cm - 2.d - 1 and Sr was 6.1 x 10 - 4 g.cm - 2.d - 1 (author)

Synthesis and Antimicrobial Activity of Long-Chain 3,4-Epoxy-2-alkanones

OpenAIRE

Wood, William F.

2010-01-01

3,4-Epoxy-2-dodecanone, a major component in the preorbital gland of the African grey duiker (Sylvicapra grimmia), showed antimicrobial activity in preliminary tests. The C11 to C17 homologues of this compound were prepared and their activity against several pathogenic dermal bacteria and fungi was tested. 3,4-Epoxy-2-dodecanone and 3,4-epoxy-2-tridecanone inhibited the growth of Trichophyton mentagrophytes at 25 μg/mL. Moderate inhibition of the growth of the bacteria Propionibacterium acnes...

Elaboration, structural and optical investigations of ZnO/epoxy nanocomposites

Science.gov (United States)

Moussa, S.; Namouchi, F.; Guermazi, H.

2015-07-01

Hybrid nanocomposites were elaborated by incorporating ZnO nanoparticles into a transparent epoxy polymer matrix, using the direct dispersion method. The effect of the nanoparticles on the structural and optical properties of the polymer matrix was investigated using Fourier transform infrared (FTIR), Raman and UV-Visible spectroscopies. Nanocomposites FTIR spectra showed a variation of band intensities attributed to nanoparticles agglomeration within the polymer. The UV-Visible measurements showed a redshift on the band gap energy of the nanocomposites differently from neat epoxy resin, caused by interactions between ZnO NPs and polymer chains. Raman spectra confirm these interactions and the formation of hydrogen bonds in the nanocomposites. The UV-Visible transmittance spectra revealed that addition of a very low concentration (0.2wt%) of ZnO nanoparticles to a transparent epoxy matrix would maintain high visible-light transparency. The decrease of transmittance with increasing ZnO percentage is due to light scattering which originates from the agglomeration of nanoparticles in the matrix, the mismatch between the refractive index of ZnO and that of the epoxy matrix, and the increase of the surface roughness of the nanocomposite with increasing ZnO addition. Moreover, the UV-vis absorption spectra revealed that adding more than 1wt% ZnO leads to the improvement of the UV shielding properties of the nanocomposites. These results prove that the elaborated ZnO/epoxy nanocomposites can be used as UV shielding materials.

Bioavailability of dietary phenolic compounds: Review

Directory of Open Access Journals (Sweden)

Erick Gutiérrez-Grijalva Paul Gutiérrez-Grijalva

2015-12-01

Full Text Available Phenolic compounds are ubiquitous in plant-based foods. High dietary intake of fruits, vegetables and cereals is related to a decreased rate in chronic diseases. Phenolic compounds are thought to be responsible, at least in part, for those health effects. Nonetheless, phenolic compounds bioaccessibility and biotransformation is often not considered in these studies; thus, a precise mechanism of action of phenolic compounds is not known. In this review we aim to present a comprehensive knowledge of the metabolic processes through which phenolic compounds go after intake.

Current-Voltage Characteristics of the Composites Based on Epoxy Resin and Carbon Nanotubes

Directory of Open Access Journals (Sweden)

Iwona Pełech

2015-01-01

Full Text Available Polymer composites based on epoxy resin were prepared. Multiwalled carbon nanotubes synthesized on iron-cobalt catalyst were applied as a filler in a polymer matrix. Chlorine or hydroxyl groups were incorporated on the carbon nanotubes surface via chlorination or chlorination followed by hydroxylation. The effect of functionalized carbon nanotubes on the epoxy resin matrix is discussed in terms of the state of CNTs dispersion in composites as well as electrical properties. For the obtained materials current-voltage characteristics were determined. They had a nonlinear character and were well described by an exponential-type equation. For all the obtained materials the percolation threshold occurred at a concentration of about 1 wt%. At a higher filler concentration >2 wt%, better conductivity was demonstrated by polymer composites with raw carbon nanotubes. At a lower filler concentration <2 wt%, higher values of electrical conductivity were obtained for polymer composites with modified carbon nanotubes.

Radiochemical ageing of epoxy coating for nuclear plants

International Nuclear Information System (INIS)

Queiroz, D.P.R.; Fraisse, F.; Fayolle, B.; Kuntz, M.; Verdu, J.

2010-01-01

The degradation of an epoxy-amine network exposed to gamma irradiation in oxygen atmosphere has been studied by using a variety of analytical methods, including infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), and sol-gel analysis. Results show that the oxidation of epoxy systems grows with the irradiation dose. Hydroperoxides, which are species resulting from oxidation, were identified and quantified by DSC. As indicated by the sol-gel analysis, the mechanism of degradation of chain scission seems to be predominant over crosslinking. The modifications induced by irradiation reflect in a greater capacity of water absorption.

Comparison of the Nanostructure and Mechanical Performance of Highly Exfoliated Epoxy-Clay Nanocomposites Prepared by Three Different Protocols

Directory of Open Access Journals (Sweden)

Fatemeh Shiravand

2014-05-01

Full Text Available Three different protocols for the preparation of polymer layered silicate nanocomposites based upon a tri-functional epoxy resin, triglycidyl para-amino phenol (TGAP, have been compared in respect of the cure kinetics, the nanostructure and their mechanical properties. The three preparation procedures involve 2 wt% and 5 wt% of organically modified montmorillonite (MMT, and are: isothermal cure at selected temperatures; pre-conditioning of the resin-clay mixture before isothermal cure; incorporation of an initiator of cationic homopolymerisation, a boron tri-fluoride methyl amine complex, BF3·MEA, within the clay galleries. It was found that features of the cure kinetics and of the nanostructure correlate with the measured impact strength of the cured nanocomposites, which increases as the degree of exfoliation of the MMT is improved. The best protocol for toughening the TGAP/MMT nanocomposites is by the incorporation of 1 wt% BF3·MEA into the clay galleries of nanocomposites containing 2 wt% MMT.

Comparison of the Nanostructure and Mechanical Performance of Highly Exfoliated Epoxy-Clay Nanocomposites Prepared by Three Different Protocols.

Science.gov (United States)

Shiravand, Fatemeh; Hutchinson, John M; Calventus, Yolanda; Ferrando, Francesc

2014-05-30

Three different protocols for the preparation of polymer layered silicate nanocomposites based upon a tri-functional epoxy resin, triglycidyl para -amino phenol (TGAP), have been compared in respect of the cure kinetics, the nanostructure and their mechanical properties. The three preparation procedures involve 2 wt% and 5 wt% of organically modified montmorillonite (MMT), and are: isothermal cure at selected temperatures; pre-conditioning of the resin-clay mixture before isothermal cure; incorporation of an initiator of cationic homopolymerisation, a boron tri-fluoride methyl amine complex, BF₃·MEA, within the clay galleries. It was found that features of the cure kinetics and of the nanostructure correlate with the measured impact strength of the cured nanocomposites, which increases as the degree of exfoliation of the MMT is improved. The best protocol for toughening the TGAP/MMT nanocomposites is by the incorporation of 1 wt% BF₃·MEA into the clay galleries of nanocomposites containing 2 wt% MMT.

Utilization of ilmenite/epoxy composite for neutrons and gamma rays attenuation

Energy Technology Data Exchange (ETDEWEB)

El-Sayed Abdo, A. E-mail: attiaabdo11@hotmail.com; El-Sarraf, M.A.; Gaber, F.A

2003-01-01

This work deals with the study of ilmenite/epoxy composite as an injecting mortar for cracks developed in biological concrete shields, as well as, neutrons and gamma rays attenuation. Effects of the particle size on the mechanical strengths have been studied for epoxy resin filled with crushed ilmenite with different maximum particle sizes ranging from 32 to 500 {mu}m. Thermal neutrons and gamma rays attenuation in ilmenite/epoxy composites with 75 and 80 wt.% of ilmenite concentration have been investigated. The total mass attenuation coefficients {mu}/{rho} (cm{sup 2} g{sup -1}) of gamma ray for five ilmenite/epoxy composites have been calculated using the XCOM program (version 3.1) at energies from 10 keV to 100 MeV. Also, the total mass attenuation coefficients ({mu}/{rho}) have estimated based on the measured total linear attenuation coefficients ({mu}) and compared with the calculated results where, a reasonable agreement was found.

Sensibilización a bisfenol A y bisfenol F en trabajadores expuestos a resinas epoxi

Directory of Open Access Journals (Sweden)

L. Jiménez Bajo

2008-06-01

Full Text Available Las aplicaciones de las diferentes resinas epoxi basadas en bisfenol A y F son extensas. Las resinas epoxi basadas en bisfenol F son más nuevas y resistentes que las de bisfenol A, y ambas son causa conocida de dermatitis de contacto alérgica. Se estudian 39 casos de sensibilización a resinas epoxi en los últimos 5 años. Los resultados obtenidos son: prevalencia de sensibilización a resinas epoxi entre los pacientes estudiados del 2%, 27 varones y 8 mujeres, con una edad media de 42.77, un período de medio sensibilización de 23,8 meses. La sensibilización a bisfenol F desde que se incluye para las pruebas del parche en la batería de resinas epoxi es del 100% para los casos sensibilizados a la resina. La localización mayoritaria se dio en las manos, con una relevancia actual del 84%. Se recomendó un cambio de puesto en el trabajo al 46% de estos pacientes. El aumento de la sensibilización encontrada a bisfenol F puede explicarse por una sensibilización concomitante con bisfenol A, una declaración incorrecta de la composición de la resina o una reactividad cruzada de ambos.The applications of epoxy resins based on bisphenol A and F are extensive. Epoxy resins based on bisphenol F are new and more resistant than epoxy resins based on bisphenol A. Both of them cause allergic contact dermatitis. In the last 5 years, we have studied 39 cases of sensitization to epoxy resin. The results of our study were these: the global prevalence of epoxy resin sensitization was 2%, 27 men and 8 women. The mean age was 42.77 years and the sensitization period was 23.8 months. The most frequent localization of the lesions were hands (84% of the patients. Since bisphenol F was included in epoxy resin battery for patch testing, a 100% of positives responses in patients sensitized to epoxy resin have been found. Sensitization to epoxy resins was a cause of change in workplace in 46% of cases in our series. There has been an increase in sensitization of

Hearing loss in workers exposed to epoxy adhesives and noise: a cross-sectional study.

Science.gov (United States)

Yang, Hsiao-Yu; Shie, Ruei-Hao; Chen, Pau-Chung

2016-02-18

Epoxy adhesives contain organic solvents and are widely used in industry. The hazardous effects of epoxy adhesives remain unclear. The objective of this study was to investigate the risk of hearing loss among workers exposed to epoxy adhesives and noise. Cross-sectional study. For this cross-sectional study, we recruited 182 stone workers who were exposed to both epoxy adhesives and noise, 89 stone workers who were exposed to noise only, and 43 workers from the administrative staff who had not been exposed to adhesives or noise. We obtained demographic data, occupational history and medical history through face-to-face interviews and arranged physical examinations and pure-tone audiometric tests. We also conducted walk-through surveys in the stone industry. A total of 40 representative noise assessments were conducted in 15 workplaces. Air sampling was conducted at 40 workplaces, and volatile organic compounds were analysed using the Environmental Protection Agency (EPA) TO-15 method. The mean sound pressure level was 87.7 dBA (SD 9.9). The prevalence of noise-induced hearing loss was considerably increased in the stone workers exposed to epoxy adhesives (42%) compared with the stone workers who were not exposed to epoxy adhesives (21%) and the administrative staff group (9.3%). A multivariate logistic regression analysis revealed that exposure to epoxy adhesives significantly increased the risk of hearing loss between 2 and 6 kHz after adjusting for age. Significant interactions between epoxy adhesives and noise and hearing impairment were observed at 3, 4 and 6 kHz. Epoxy adhesives exacerbate hearing impairment in noisy environments, with the main impacts occurring in the middle and high frequencies. Published by the BMJ Publishing Group Limited. For permission to use (where not already granted under a licence) please go to http://www.bmj.com/company/products-services/rights-and-licensing/

Modification of the Interfacial Interaction between Carbon Fiber and Epoxy with Carbon Hybrid Materials

Directory of Open Access Journals (Sweden)

Kejing Yu

2016-05-01

Full Text Available The mechanical properties of the hybrid materials and epoxy and carbon fiber (CF composites were improved significantly as compared to the CF composites made from unmodified epoxy. The reasons could be attributed to the strong interfacial interaction between the CF and the epoxy composites for the existence of carbon nanomaterials. The microstructure and dispersion of carbon nanomaterials were characterized by transmission electron microscopy (TEM and optical microscopy (OM. The results showed that the dispersion of the hybrid materials in the polymer was superior to other carbon nanomaterials. The high viscosity and shear stress characterized by a rheometer and the high interfacial friction and damping behavior characterized by dynamic mechanical analysis (DMA indicated that the strong interfacial interaction was greatly improved between fibers and epoxy composites. Remarkably, the tensile tests presented that the CF composites with hybrid materials and epoxy composites have a better reinforcing and toughening effect on CF, which further verified the strong interfacial interaction between epoxy and CF for special structural hybrid materials.

Epoxy – the hub for the most versatile polymer with exceptional combination of superlative features

OpenAIRE

Inam, Fawad

2014-01-01

Epoxy resins and epoxy based materials have experienced significant advancement since their beginning in 1936, when Dr. Castan of Switzerland and Dr. Greenlee of USA succeeded in synthesizing the very first bisphenol-A-based epoxy resins. Whether it is the new carbon fiber composite of Boeing’s Dreamliner or the thin set terrazzo flooring, epoxy has always been the ideal choice because of its superlative properties and unique chemical composition. Belonging to thermoset family, it is certainl...

Effect of Thermally Reduced Graphene Oxide on Mechanical Properties of Woven Carbon Fiber/Epoxy Composite

OpenAIRE

Nitai Chandra Adak; Suman Chhetri; Naresh Chandra Murmu; Pranab Samanta; Tapas Kuila

2018-01-01

Thermally reduced graphene oxide (TRGO) was incorporated as a reinforcing filler in the epoxy resin to investigate the effect on the mechanical properties of carbon fiber (CF)/epoxy composites. At first, the epoxy matrix was modified by adding different wt % of TRGO from 0.05 to 0.4 wt % followed by the preparation of TRGO/CF/epoxy composites througha vacuum-assisted resin transfer molding process. The prepared TRGO was characterized by using Fourier transform infrared spectroscopy, Raman Spe...

Enhancing Mechanical and Thermal Properties of Epoxy Nanocomposites via Alignment of Magnetized SiC Whiskers.

Science.gov (United States)

Townsend, James; Burtovyy, Ruslan; Aprelev, Pavel; Kornev, Konstantin G; Luzinov, Igor

2017-07-12

This research is focused on the fabrication and properties of epoxy nanocomposites containing magnetized SiC whiskers (MSiCWs). To this end, we report an original strategy for fabrication of magnetically active SiCWs by decorating the whiskers with magnetic (iron oxide) nanoparticles via polymer-polymer (poly(acrylic acid)/poly(2-vinyl pyridine)) complexation. The obtained whiskers demonstrated a substantial magnetic response in the polymerizing epoxy resin, with application of only a 20 mT (200 G) magnetic field. We also found that the whiskers chemically reacted with the epoxy resin, causing formation of an extended interphase near the boundary of the whiskers. The SiC whiskers oriented with the magnetic field demonstrated positive effects on the behavior of epoxy-based nanocomposites. Namely, the aligned MSiCWs enhanced the thermomechanical properties of the materials significantly above that of the neat epoxy and epoxy nanocomposite, with randomly oriented whiskers.

Enhancing the Heat Transfer Efficiency in Graphene-Epoxy Nanocomposites Using a Magnesium Oxide-Graphene Hybrid Structure.

Science.gov (United States)

Du, Fei-Peng; Yang, Wen; Zhang, Fang; Tang, Chak-Yin; Liu, Sheng-Peng; Yin, Le; Law, Wing-Cheung

2015-07-08

Composite materials, such as organic matrices doped with inorganic fillers, can generate new properties that exhibit multiple functionalities. In this paper, an epoxy-based nanocomposite that has a high thermal conductivity and a low electrical conductivity, which are required for the use of a material as electronic packaging and insulation, was prepared. The performance of the epoxy was improved by incorporating a magnesium oxide-coated graphene (MgO@GR) nanomaterial into the epoxy matrix. We found that the addition of a MgO coating not only improved the dispersion of the graphene in the matrix and the interfacial bonding between the graphene and epoxy but also enhanced the thermal conductivity of the epoxy while preserving the electrical insulation. By adding 7 wt % MgO@GR, the thermal conductivity of the epoxy nanocomposites was enhanced by 76% compared with that of the neat epoxy, and the electrical resistivity was maintained at 8.66 × 10(14) Ω m.

Synthesis and Characterization of Modified Epoxy Resins by Silicic Acid Tetraethyl Ester and Nano-SiO2

Institute of Scientific and Technical Information of China (English)

李海燕; 张之圣

2004-01-01

A kind of modified epoxy resins was obtained by condensation of epoxy resin with silicic acid tetraethyl ester(TEOS) and nano-SiO2. The reactions were performed with hydrochloric acid as a catalyst at 63 °C.The structure, thermal stability and morphological characteristics of the modified epoxy resins were studied through infrared spectra(FT-IR) analysis, thermogravimetric (TG) analysis and scanning electron microscopy respectively. It has been found from the IR and TG study that modified epoxy resins have greater thermal stability than epoxy resins, and its thermal stability has been improved by the formation of inter-crosslinked network structure. The modified epoxy resins exhibit heterogeneous morphology and heterogeneity increases with more TEOS feeding, which in turn confirms the formation of inter-crosslinked network structure in modified epoxy resins.

Radiation curing of {gamma}-Al{sub 2}O{sub 3} filled epoxy resin

Energy Technology Data Exchange (ETDEWEB)

Kang, Phil Hyun; Kim, Dong Jin; Nho, Young Chang [KAERI, Taejon (Korea, Republic of)

2003-10-01

Epoxy resins are widely utilized as high performance thermosetting resins for many industrial applications but characterized by a relatively low toughness. Recently, the incorporation with rigid inorganic was suggested to improve the mechanical properties of epoxy resins. In the present work, an attempt has been taken to disperse nano-sized {gamma}- Al{sub 2}O{sub 3} particles into diglycidyl ether of bisphenol-A (DGEBA) epoxy resins for improvement of the mechanical properties. These hybrid epoxy-alumina composites were prepared using by the {gamma}-ray curing technique that was conducted with 100kGy under nitrogen at room temperature. The composites were characterized by determining gel content, UTM (Instron model 4443), SEM, FT-IR studies.

Tensile Mechanical Property of Oil Palm Empty Fruit Bunch Fiber Reinforced Epoxy Composites

Science.gov (United States)

Ghazilan, A. L. Ahmad; Mokhtar, H.; Shaik Dawood, M. S. I.; Aminanda, Y.; Ali, J. S. Mohamed

2017-03-01

Natural, short, untreated and randomly oriented oil palm empty fruit bunch fiber reinforced epoxy composites were manufactured using vacuum bagging technique with 20% fiber volume composition. The performance of the composite was evaluated as an alternative to synthetic or conventional reinforced composites. Tensile properties such as tensile strength, modulus of elasticity and Poisson’s ratio were compared to the tensile properties of pure epoxy obtained via tensile tests as per ASTM D 638 specifications using Universal Testing Machine INSTRON 5582. The tensile properties of oil palm empty fruit bunch fiber reinforced epoxy composites were lower compared to plain epoxy structure with the decrement in performances of 38% for modulus of elasticity and 61% for tensile strength.

Effect of micro-oxygenation and wood type on the phenolic composition and color of an aged red wine.

Science.gov (United States)

Sánchez-Iglesias, Montserrat; González-Sanjosé, Ma Luisa; Pérez-Magariño, Silvia; Ortega-Heras, Miriam; González-Huerta, Carlos

2009-12-23

Many studies have recently been published focused on the effects of micro-oxygenation on the quality of wines, its application modes, and doses, etc. However, there are still few scientific papers on how previously micro-oxygenated wines perform during storage or barrel aging. This study focused on the evolution of the phenolic composition, especially of anthocyanins, and color, together with astringency and tannins, during micro-oxygenation before barrel aging. In addition, to evaluate whether wine evolution during aging depends on barrel type, wines were aged in four different oak barrel types. Tempranillo wines, some micro-oxygenated before malolactic fermentation and others not, were aged for 12 months in American, French, Central European, and Spanish oak, following wine evolution during that period. The study was carried out for two consecutive vintages. Results showed that all wines evolved similarly; therefore, the micro-oxygenation treatment neither accelerated nor delayed the typical changes of aging. Slightly different evolutions were detected according to the barrel wood type, whether or not the wine was micro-oxygenated. The varied evolutions must therefore be associated with the differences from each oak type (structure, grain and density, composition, etc.).

Thermally induced self-healing epoxy/glass laminates with porous layers containing crystallized healing agent

Directory of Open Access Journals (Sweden)

T. Szmechtyk

2018-07-01

Full Text Available Porous glass fiber and paper layers were tested for application in thermally induced self healing epoxy laminates as healing porous layers. Both types of layers were impregnated using high purity bisphenol A diglycidyl ether (BADGE epoxy with ability to crystallize during storage under 25 °C. Absorption capacity of porous layers was evaluated. Differential scanning calorimetry was used to investigate BADGE healing agent recrystallization process. Healing porous glass layers (HPGL were selected for further tests. Liquid chromatography and Fourier transform infrared (FT IR spectroscopy provided information about average molecular mass of embedded healing agent and functional groups in HPGL layers. Self-healing efficiency of three different laminates with HPGL layers was calculated based on the results of three-point bending test and Charpy impact test. Also, flexural properties and impact strength of laminates were evaluated. The obtained results confirm competitive self healing ability of composites with HPGL.

Mechanical and Thermal Properties of Epoxy Composites Containing Zirconia-Impregnated Halloysite Nanotubes with Different Loadings.

Science.gov (United States)

Kim, Suhyun; Kim, Moon Il; Shon, Minyoung; Seo, Bongkuk; Lim, Choongsun

2018-09-01

Epoxy resins are widely used in various industrial fields due to their low cost, good workability, heat resistance, and good mechanical strength. However, they suffer from brittleness, an issue that must be addressed for further applications. To solve this problem, additional fillers are needed to improve the mechanical and thermal properties of the resins; zirconia is one such filler. However, it has been reported that aggregation may occur in the epoxy composites as the amount of zirconia increases, preventing enhancement of the mechanical strength of the epoxy composites. Herein, to reduce the aggregation, zirconia was well dispersed on halloysite nanotubes (HNTs), which have high thermal and mechanical strength, by a conventional wet impregnation method. The HNTs were impregnated with zirconia at different loadings using zirconyl chloride octahydrate as a precursor. The mechanical and thermal strengths of the epoxy composites with these fillers were investigated. The zirconia-impregnated HNTs (Zr/HNT) were characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and tunneling electron microscopy (TEM). The hardening conditions of the epoxy composites were analyzed by differential scanning calorimetry (DSC). The thermal strength of the epoxy composites was studied by thermomechanical analysis (TMA) and micro-calorimetry and the mechanical strength of the epoxy composites (flexural strength and tensile strength) was studied by using a universal testing machine (UTM). The mechanical and thermal strengths of the epoxy composites with Zr/HNT were improved compared to those of the epoxy composite with HNT, and also increased as the zirconia loading on HNT increased.

Noncovalently Functionalized Tungsten Disulfide Nanosheets for Enhanced Mechanical and Thermal Properties of Epoxy Nanocomposites.

Science.gov (United States)

Sahu, Megha; Narashimhan, Lakshmi; Prakash, Om; Raichur, Ashok M

2017-04-26

In the present study, noncovalently functionalized tungsten disulfide (WS 2 ) nanosheets were used as a toughening agent for epoxy nanocomposites. WS 2 was modified with branched polyethyleneimine (PEI) to increase the degree of interaction of nanosheets with the epoxy matrix and prevent restacking and agglomeration of the sheets in the epoxy matrix. The functionalization of WS 2 sheets was confirmed through Fourier transform infrared spectroscopy and thermogravimetric analysis. The exfoliation of the bulk WS 2 was confirmed through X-ray diffraction and various microscopic techniques. Epoxy nanocomposites containing up to 1 wt % of WS 2 -PEI nanosheets were fabricated. They showed a remarkable improvement in fracture toughness (K IC ). K IC increased from 0.94 to 1.72 MPa m -1/2 for WS 2 -PEI nanosheet loadings as low as 0.25 wt %. Compressive and flexural properties also showed a significant improvement as incorporation of 0.25 wt % of WS 2 -PEI nanosheets resulted in 43 and 65% increase in the compressive and flexural strengths of epoxy nanocomposites, respectively, compared with neat epoxy. Thermal stability and thermomechanical properties of the WS 2 -PEI-modified epoxy also showed a significant improvement. The simultaneous improvement in the mechanical and thermal properties could be attributed to the good dispersion of WS 2 -PEI nanosheets in the matrix, intrinsic high strength and thermal properties of the nanosheets, and improved interaction of the WS 2 nanosheets with the epoxy matrix owing to the presence of PEI molecules on the surface of the WS 2 nanosheets.

Control of Maillard-type off-flavor development in ultrahigh-temperature-processed bovine milk by phenolic chemistry.

Science.gov (United States)

Kokkinidou, Smaro; Peterson, Devin G

2014-08-13

The application of phenolic compounds to suppress Maillard chemistry and off-flavor development in ultrahigh-termperature (UHT)-processed milk during processing and storage was investigated. Five phenolic compounds were examined for structure-reactivity relationships (catechin, genistein, daidzein, 1,2,3-trihydroxybenzene, and 1,3,5-trihydroxybenzene). The levels of key transient Maillard reaction (MR) intermediates (reactive carbonyl species) and select off-flavor markers (methional, 2-acetyl-2-thiazoline, 2-acetyl-1-pyrroline) were quantified by LC-MS/MS and GC-MS/ToF, respectively. The addition of phenolic compounds prior to UHT processing significantly reduced the concentration of MR intermediates and related off-flavor compounds compared to a control sample (p markers and reactive carbonyl species. Sensory studies were in agreement with the analytical data. The cooked flavor intensity was rated lower for the recombination model samples of the catechin-treated UHT milk compared to the control UHT milk. Additionally, consumer acceptability studies showed catechin-treated UHT milk to have significantly higher liking scores when compared the control sample (Fisher's LSD = 0.728).

Effect of Hygrothermal Aging on the Mechanical Properties of Fluorinated and Nonfluorinated Clay-Epoxy Nanocomposites.

Science.gov (United States)

Hamim, Salah U; Singh, Raman P

2014-01-01

Hydrophilic nature of epoxy polymers can lead to both reversible and irreversible/permanent changes in epoxy upon moisture absorption. The permanent changes leading to the degradation of mechanical properties due to combined effect of moisture and elevated temperature on EPON 862, Nanomer I.28E, and Somasif MAE clay-epoxy nanocomposites are investigated in this study. The extent of permanent degradation on fracture and flexural properties due to the hygrothermal aging is determined by drying the epoxy and their clay-epoxy nanocomposites after moisture absorption. Significant permanent damage is observed for fracture toughness and flexural modulus, while the extent of permanent damage is less significant for flexural strength. It is also observed that permanent degradation in Somasif MAE clay-epoxy nanocomposites is higher compared to Nanomer I.28E clay-epoxy nanocomposites. Fourier transform infrared (FTIR) spectroscopy revealed that both clays retained their original chemical structure after the absorption-desorption cycle without undergoing significant changes. Scanning electron microscopy (SEM) images of the fracture surfaces provide evidence that Somasif MAE clay particles offered very little resistance to crack propagation in case of redried specimens when compared to Nanomer I.28E counterpart. The reason for the observed higher extent of permanent degradation in Somasif MAE clay-epoxy system has been attributed to the weakening of the filler-matrix interface.

Potential application of hemoglobin as an alternative to peroxidase in a phenol biosensor

International Nuclear Information System (INIS)

Kafi, A.K.M.; Lee, Dong-Yun; Park, Sang-Hyun; Kwon, Young-Soo

2008-01-01

This work describes a new amperometric biosensor for detecting phenolic compounds. The sensor was designed by immobilizing Hemoglobin (Hb) in a sol-gel matrix onto a carbon electrode. Using the peroxidase activity of Hb, the phenolic compound can be reduced in the presence of H 2 O 2 . The biosensor's performance in phenolic compound detection was based on mediated electron transfer by Hb. The direct electron transfer of Hb can be avoided by use of the sol-gel matrix. The proposed biosensor presents a very sensitive response for phenolic compounds at an applied potential of 0.0 mV vs. Ag/AgCl. The parameters of the fabrication process for the electrode were optimized. Experimental conditions influencing the biosensor performance, such as pH and potential, were investigated and assessed. Various types of phenolic compounds were detected. Among them, using the optimized conditions, a linearity for the detection of the phenol was observed from 5 μM to 50 μM. Biosensor response levels after 30 days were at more than 80% of their initial response readings level. The response time of the biosensor was about 10 s

Epoxy Nanocomposites - Curing Rheokinetics, Wetting and Adhesion to Fibers

International Nuclear Information System (INIS)

Ilyin, S. O.; Kotomin, S. V.; Kulichikhin, V. G.

2010-01-01

Epoxy nanocomposites considered as challenging polymeric matrix for advanced reinforced plastics. Nanofillers change rheokinetics of epoxy resin curing, affect wetting and adhesion to aramid and carbon fibers. In all cases extreme dependence of adhesive strength vs filler content in the binder was observed. New experimental techniques were developed to study wettability and fiber-matrix adhesion interaction, using yarn penetration path length, aramid fiber knot pull-up test and electrical admittance of the fracture surface of CFRP.

Novel Formulations of Phase Change Materials—Epoxy Composites for Thermal Energy Storage

Directory of Open Access Journals (Sweden)

Maria Elena Arce

2018-01-01

Full Text Available This research aimed to evaluate the thermal properties of new formulations of phase change materials (PCMs-epoxy composites, containing a thickening agent and a thermally conductive phase. The composite specimens produced consisted of composites fabricated using (a inorganic PCMs (hydrated salts, epoxy resins and aluminum particulates or (b organic PCM (paraffin, epoxy resins, and copper particles. Differential Scanning Calorimetry (DSC was used to analyze the thermal behavior of the samples, while hardness measurements were used to determine changes in mechanical properties at diverse PCM and conductive phase loading values. The results indicate that the epoxy matrix can act as a container for the PCM phase without hindering the heat-absorbing behavior of the PCMs employed. Organic PCMs presented reversible phase transformations over multiple cycles, an advantage that was lacking in their inorganic counterparts. The enthalpy of the organic PCM-epoxy specimens increased linearly with the PCM content in the matrix. The use of thickening agents prevented phase segregation issues and allowed the fabrication of specimens containing up to 40% PCM, a loading significantly higher than others reported. The conductive phase seemed to improve the heat transfer and the mechanical properties of the composites when present in low percentages (<10 wt %; however, given its mass, the enthalpy detected in the composites was reduced as their loading further increased. The conductive phase combination (PCM + epoxy resin + hardener + thickening agent presents great potential as a heat-absorbing material at the temperatures employed.

Fabrication of carbon nanotube/epoxy nanocomposite and characterization of its mechanical properties

Energy Technology Data Exchange (ETDEWEB)

Mubin, Muhammad Shamsul Huda

2007-02-15

In this study, carbon nanotube polymer nanocomposites have been fabricated incorporating single walled carbon nantubes (SWNTs) or multiwalled carbon nanotubes (MWNTs) in a thermosetting polymer matrix, epoxy resin. Nanoindentation measurements showed that elastic modulus of epoxy polymer matrix has changed from 3.5 GPa to 4.0 GPa (∼ 15 % increase) only for 0.005 wt% single walled carbon nanotubes loading. The hardness of the single walled carbon nanotube incorporated epoxy nanocomposites remained nearly unchanged for 0.005 wt % nanotube loading. Multiwalled carbon nanotube incorporated epoxy nanocomposites showed deterioration of both the hardness, from 0.2 GPa to 0.08 GPa (∼factor 2.5), and elastic modulus, from 3.5 GPa to 2.1 GPa (∼ factor 1.6), for 0.02 wt % nanotube loading. Homogeneity study using continuous stiffness measurement (CSM) mode of indentation techniques revealed the lack in homogeneity of the fabricated nancomposite may be responsible for deteriorating mechanical properties. High resolution scanning electronic microscopic (SEM) images taken from cross section of carbon nanotubes incorporated epoxy nanocomposites showed several poorly attached thin layers of nanocomposites staked on each other which may be another cause of property deterioration.

Fabrication of carbon nanotube/epoxy nanocomposite and characterization of its mechanical properties

International Nuclear Information System (INIS)

Mubin, Muhammad Shamsul Huda

2007-02-01

In this study, carbon nanotube polymer nanocomposites have been fabricated incorporating single walled carbon nantubes (SWNTs) or multiwalled carbon nanotubes (MWNTs) in a thermosetting polymer matrix, epoxy resin. Nanoindentation measurements showed that elastic modulus of epoxy polymer matrix has changed from 3.5 GPa to 4.0 GPa (∼ 15 % increase) only for 0.005 wt% single walled carbon nanotubes loading. The hardness of the single walled carbon nanotube incorporated epoxy nanocomposites remained nearly unchanged for 0.005 wt % nanotube loading. Multiwalled carbon nanotube incorporated epoxy nanocomposites showed deterioration of both the hardness, from 0.2 GPa to 0.08 GPa (∼factor 2.5), and elastic modulus, from 3.5 GPa to 2.1 GPa (∼ factor 1.6), for 0.02 wt % nanotube loading. Homogeneity study using continuous stiffness measurement (CSM) mode of indentation techniques revealed the lack in homogeneity of the fabricated nancomposite may be responsible for deteriorating mechanical properties. High resolution scanning electronic microscopic (SEM) images taken from cross section of carbon nanotubes incorporated epoxy nanocomposites showed several poorly attached thin layers of nanocomposites staked on each other which may be another cause of property deterioration

Purification of bioactive phenolics from Phanerochaete chysosporium biomass extract on selected macroporous resins

Science.gov (United States)

Idris, Z. M.; Dzahir, M. I. H. M.; Jamal, P.; Barkat, A. A.; Xian, R. L. W.

2017-06-01

In this study, two different types of macroporous resins known as XAD-7HP and HP-20 were evaluated for the adsorption and desorption properties against bioactive phenolics extracted from Phanerochaete chrysosporium. From the previous static sorption studies, it was found that the adsorption capacity for both resins had has no significant difference. Then, the kinetic adsorption data were analyzed with both pseudo-first-order and pseudo-second-order equations and the later performed better. The adsorption isotherm data were fitted well by both Langmuir and Freundlich models. Meanwhile in desorption study, HP-20 and XAD-7HP gave 90.52% and 88.28% recoveries, respectively. Considering the desorption results of the macroporous resins, HP-20 and XAD-7HP were packed in chromatography column to further purify the phenolics. For dynamic adsorption, breakthrough capacity of HP-20 (0.522) was found to be higher than XAD-7HP (0.131). Different ethanol concentrations (30% to 50% (v/v)) were investigated at fixed flowrate (1 ml/min) on phenolics recovery from both types of resins. The highest recovery of bioactive phenolics was 94.3% using XAD-7HP resins at 50% (v/v) of ethanol. Only 77.1% of bioactive phenolics were recovered using HP-20 resin at the same experimental conditions. The purified extract subsequently was analyzed using HPLC. The results showed that three phenolics (gallic acid 3,4-dihydroxybenzoic acid and 4-hydroxybenzoic acid) were identified with higher concentrations as compared to non-purified extract. Finally, the purified extract was tested for scavenging activity against DPPH, and it showed that the activity increased significantly to 90.80% from 59.94% in non-purified extract.

IMPACT OF THERMAL FATIGUE ON YOUNG’S MODULUS OF EPOXY ADHESIVES

Directory of Open Access Journals (Sweden)

Mariusz Kłonica

2015-11-01

Full Text Available The following paper presents a comparative analysis of two epoxy-based adhesives: Hysol 9466 and Hysol 3421, prior to and after thermal shock testing. The tests focused on determining Young’s modulus. Epoxy-based materials are among the most widespread adhesive materials used as universal structural adhesives. The prepared epoxy samples (Hysol 9466 and Hysol 3421 were subjected to thermal shock cycling tests, according to a specified programme, in a thermal shock testing chamber, at a temperature range –40 °C to +60 °C and in the number of 200 cycles. Conclusions from the tests are presented at the final stage of the paper.

Wine phenolic compounds influence the production of volatile phenols by wine-related lactic acid bacteria.

Science.gov (United States)

Silva, I; Campos, F M; Hogg, T; Couto, J A

2011-08-01

To evaluate the effect of wine phenolic compounds on the production of volatile phenols (4-vinylphenol [4VP] and 4-ethylphenol [4EP]) from the metabolism of p-coumaric acid by lactic acid bacteria (LAB). Lactobacillus plantarum, Lactobacillus collinoides and Pediococcus pentosaceus were grown in MRS medium supplemented with p-coumaric acid, in the presence of different phenolic compounds: nonflavonoids (hydroxycinnamic and benzoic acids) and flavonoids (flavonols and flavanols). The inducibility of the enzymes involved in the p-coumaric acid metabolism was studied in resting cells. The hydroxycinnamic acids tested stimulated the capacity of LAB to synthesize volatile phenols. Growth in the presence of hydroxycinnamic acids, especially caffeic acid, induced the production of 4VP by resting cells. The hydroxybenzoic acids did not significantly affect the behaviour of the studied strains. Some of the flavonoids showed an effect on the production of volatile phenols, although strongly dependent on the bacterial species. Relatively high concentrations (1 g l(-1) ) of tannins inhibited the synthesis of 4VP by Lact. plantarum. Hydroxycinnamic acids were the main compounds stimulating the production of volatile phenols by LAB. The results suggest that caffeic and ferulic acids induce the synthesis of the cinnamate decarboxylase involved in the metabolism of p-coumaric acid. On the other hand, tannins exert an inhibitory effect. This study highlights the capacity of LAB to produce volatile phenols and that this activity is markedly influenced by the phenolic composition of the medium. © 2011 The Authors. Journal of Applied Microbiology © 2011 The Society for Applied Microbiology.

Mechanical, thermal and microstructural characteristics of cellulose fibre reinforced epoxy/organoclay nanocomposites

KAUST Repository

Alamri, H.

2012-10-01

Epoxy nanocomposites reinforced with recycled cellulose fibres (RCFs) and organoclay platelets (30B) have been fabricated and investigated in terms of WAXS, TEM, mechanical properties and TGA. Results indicated that mechanical properties generally increased as a result of the addition of nanoclay into the epoxy matrix. The presence of RCF significantly enhanced flexural strength, fracture toughness, impact strength and impact toughness of the composites. However, the inclusion of 1 wt.% clay into RCF/epoxy composites considerably increased the impact strength and toughness. The presence of either nanoclay or RCF accelerated the thermal degradation of neat epoxy, but at high temperature, thermal stability was enhanced with increased char residue over neat resin. The failure micromechanisms and energy dissipative processes in these nanocomposites were discussed in terms of microstructural observations. © 2012 Published by Elsevier Ltd. All rights reserved.

Thermomechanical response and toughening mechanisms of a carbon nano bead reinforced epoxy composite

Energy Technology Data Exchange (ETDEWEB)

Goyat, M.S., E-mail: goyatmanjeetsingh@gmail.com [Department of Metallurgical and Materials Engineering, Indian Institute of Technology Roorkee, Roorkee, 247667 (India); Suresh, Sumit; Bahl, Sumit [Department of Metallurgical and Materials Engineering, Indian Institute of Technology Roorkee, Roorkee, 247667 (India); Halder, Sudipta [Department of Mechanical Engineering, National Institute of Technology, Silchar, 788010, Assam (India); Ghosh, P.K. [Department of Metallurgical and Materials Engineering, Indian Institute of Technology Roorkee, Roorkee, 247667 (India)

2015-09-15

The current research on carbon nano beads (CNB) is focused on various applications such as high strength nanocomposites, electronic devices, lubricants, semiconductors, and high-performance batteries, etc. The commercial uses of CNB are yet juvenile for the market. Only limited results have been published so far on CNB reinforced polymers [1]. This study highlights the synthesis of uniform size, spherical CNB using chemical vapour deposition (CVD) method. The synthesized CNB are introduced into epoxy matrix by ultrasonic dual mode mixing route to produce CNB/epoxy nanocomposite. The CNB are characterized by X-ray diffraction, Energy dispersive X-ray analysis and field emission scanning electron microscope (FESEM). Morphology, thermal and mechanical properties of the CNB/epoxy nanocomposites is characterized by FESEM, Thermo-gravimetric analyzer and tensile and bending tests respectively. A noticeable improvement in thermal and mechanical properties of CNB reinforced epoxy matrix with low nanofiller content is observed. Several toughening mechanisms such as particle pull out, crack deflection, particle bridging, crack pinning, shear yielding or plastic deformation, and microcracking are identified. But, only the crack deflection, particle bridging and shear yielding or plastic deformations are recognized as the leading toughening mechanisms for CNB/epoxy nanocomposite. These results can be considered as symptomatic of a potential CNB espousal in new composites. - Highlights: • Synthesis of uniform size, spherical CNB using chemical vapour deposition method. • Fabrication of CNB/epoxy nanocomposites by ultrasonic dual mode mixing route. • Significant enhancement in thermomechanical properties of CNB/epoxy nanocomposite. • Main toughening mechanisms: Crack deflection, particle bridging and shear yielding.

Thermomechanical response and toughening mechanisms of a carbon nano bead reinforced epoxy composite

International Nuclear Information System (INIS)

Goyat, M.S.; Suresh, Sumit; Bahl, Sumit; Halder, Sudipta; Ghosh, P.K.

2015-01-01

The current research on carbon nano beads (CNB) is focused on various applications such as high strength nanocomposites, electronic devices, lubricants, semiconductors, and high-performance batteries, etc. The commercial uses of CNB are yet juvenile for the market. Only limited results have been published so far on CNB reinforced polymers [1]. This study highlights the synthesis of uniform size, spherical CNB using chemical vapour deposition (CVD) method. The synthesized CNB are introduced into epoxy matrix by ultrasonic dual mode mixing route to produce CNB/epoxy nanocomposite. The CNB are characterized by X-ray diffraction, Energy dispersive X-ray analysis and field emission scanning electron microscope (FESEM). Morphology, thermal and mechanical properties of the CNB/epoxy nanocomposites is characterized by FESEM, Thermo-gravimetric analyzer and tensile and bending tests respectively. A noticeable improvement in thermal and mechanical properties of CNB reinforced epoxy matrix with low nanofiller content is observed. Several toughening mechanisms such as particle pull out, crack deflection, particle bridging, crack pinning, shear yielding or plastic deformation, and microcracking are identified. But, only the crack deflection, particle bridging and shear yielding or plastic deformations are recognized as the leading toughening mechanisms for CNB/epoxy nanocomposite. These results can be considered as symptomatic of a potential CNB espousal in new composites. - Highlights: • Synthesis of uniform size, spherical CNB using chemical vapour deposition method. • Fabrication of CNB/epoxy nanocomposites by ultrasonic dual mode mixing route. • Significant enhancement in thermomechanical properties of CNB/epoxy nanocomposite. • Main toughening mechanisms: Crack deflection, particle bridging and shear yielding.

Octyl Phenol Synthesis Using Natural Clays

Directory of Open Access Journals (Sweden)

S. Casuscelli

2000-03-01

Full Text Available A series of clay minerals, HB, NB and Al-PILC have been studied in the alkylation reactions of 2-octanol with phenol at 180°C, under conditions of alcohol/phenol = 1 (mole ratio and W/FAo °= 64,27 ghmol-1. The selectivity of Al-PILC was 77,12% for octyl phenol and 16,5% for dioctyl phenol.

Synthesis and antimicrobial activity of long-chain 3,4-Epoxy-2-alkanones.

Science.gov (United States)

Wood, William F

2010-01-01

3,4-Epoxy-2-dodecanone, a major component in the preorbital gland of the African grey duiker (Sylvicapra grimmia), showed antimicrobial activity in preliminary tests. The C(11) to C(17) homologues of this compound were prepared and their activity against several pathogenic dermal bacteria and fungi was tested. 3,4-Epoxy-2-dodecanone and 3,4-epoxy-2-tridecanone inhibited the growth of Trichophyton mentagrophytes at 25 Îg/mL. Moderate inhibition of the growth of the bacteria Propionibacterium acnes and the lipophilic yeast, Pityrosporum ovale, was seen for several of the homologues.

Evaluation of the use of inorganic pigments and fillers in cure of epoxy resins by microwave irradiation

International Nuclear Information System (INIS)

Kersting, Daniel; Wiebeck, Helio

2013-01-01

The use of microwave in chemical processes began soon after the WW II. The mechanism of curing via microwave heating is independent of the thermal conductivity of the irradiated material and offers a good solution to operate with materials that do not have a good thermal conductivity, such as polymers. Despite these advantages, the use of multimode microwave ovens, the main source used today, indicates some challenges to overcome. Associated with the use of epoxy resins in various applications, the use of pigments and inorganic fillers has added more variables to be studied. Much of the inorganic fillers used commercially are good absorbers of microwave providing changes in the amount of radiation absorbed, and thus the amount of heat transferred to the epoxy resin curing process. After selecting the key fillers and pigments traditionally used in the production of parts with epoxy resins they were subjected to the same microwave irradiation for evaluation of their behavior alone. In order to observe the effect of mixtures 1, 2, and 5% by weight of filler were added to epoxy resin, and it was verified these effects in the curing process. The preliminary results are promising, because for the same cure cycle for different types of fillers added separately, gains in curing time were obtained, making the process of cure via microwave quick and efficient without substantial losses in thermal properties of the final products obtained. (author)

Silica Treatments: A Fire Retardant Strategy for Hemp Fabric/Epoxy Composites

Directory of Open Access Journals (Sweden)

Francesco Branda

2016-08-01

Full Text Available In this paper, for the first time, inexpensive waterglass solutions are exploited as a new, simple and ecofriendly chemical approach for promoting the formation of a silica-based coating on hemp fabrics, able to act as a thermal shield and to protect the latter from heat sources. Fourier Transform Infrared (FTIR and solid-state Nuclear Magnetic Resonance (NMR analysis confirm the formation of –C–O–Si– covalent bonds between the coating and the cellulosic substrate. The proposed waterglass treatment, which is resistant to washing, seems to be very effective for improving the fire behavior of hemp fabric/epoxy composites, also in combination with ammonium polyphosphate. In particular, the exploitation of hemp surface treatment and Ammonium Polyphosphate (APP addition to epoxy favors a remarkable decrease of the Heat Release Rate (HRR, Total Heat Release (THR, Total Smoke Release (TSR and Specific Extinction Area (SEA (respectively by 83%, 35%, 45% and 44% as compared to untreated hemp/epoxy composites, favoring the formation of a very stable char, as also assessed by Thermogravimetric Analysis (TGA. Because of the low interfacial adhesion between the fabrics and the epoxy matrix, the obtained composites show low strength and stiffness; however, the energy absorbed by the material is higher when using treated hemp. The presence of APP in the epoxy matrix does not affect the mechanical behavior of the composites.

Phenolics from Ageratina adenophora roots and their phytotoxic effects on Arabidopsis thaliana seed germination and seedling growth.

Science.gov (United States)

Zhou, Zhong-Yu; Liu, Wan-Xue; Pei, Gang; Ren, Hui; Wang, Jing; Xu, Qiao-Lin; Xie, Hai-Hui; Wan, Fang-Hao; Tan, Jian-Wen

2013-12-04

A bioassay-directed phytochemical study was conducted to investigate potential allelochemicals in the roots of the invasive plant Ageratina adenophora. Eleven phenolic compounds, including seven new ones, 7-hydroxy-8,9-dehydrothymol 9-O-trans-ferulate (1), 7-hydroxythymol 9-O-trans-ferulate (2), 7,8-dihydroxythymol 9-O-trans-ferulate (3), 7,8-dihydroxythymol 9-O-cis-ferulate (4), methyl (7R)-3-deoxy-4,5-epoxy-D-manno-2-octulosonate 8-O-trans-p-coumarate (5), methyl (7R)-3-deoxy-4,5-epoxy-D-manno-2-octulosonate 8-O-cis-p-coumarate (6), and 3-(2-hydroxyphenyl)propyl methyl malonate (7), were isolated from a bioactive subfraction of the ethanol extract of the roots of A. adenophora. The new structures were established on the basis of detailed spectroscopic analysis. The potential phytotoxic effects of these compounds on the germination of Arabidopsis thaliana seeds were tested by a filter paper assay. Compound 7 and known compounds 3-(2-hydroxyphenyl)-1-propanol (8) and o-coumaric acid (9) remarkably showed inhibition activity against Arabidopsis seed germination at a concentration of 1.0 mM. Compounds 1, 2, 5, 6, and 10 showed slight inhibitory activity at the test concentration after treatment for 3 days, while the other compounds showed no obvious inhibitory effects. Moreover, 7-9 were further found to show obvious inhibitory activity on retarding the seedling growth of Ar. thaliana cultured in soil medium.

Characterization of Low Density Glass Filled Epoxies

National Research Council Canada - National Science Library

Quesenberry, Matthew

2003-01-01

This report discusses the experimental determination and modeling of several thermophysical and mechanical properties of glass filled epoxy composite systems for potential use as electronic potting compounds...

Determinants of epoxy allergy in the construction industry : a case-control study

NARCIS (Netherlands)

Spee, Ton; Timmerman, Johan G; Rühl, Reinhold; Kersting, Klaus; Heederik, Dick J J; Smit, Lidwien A M

2016-01-01

BACKGROUND: Workers exposed to epoxy products are at risk of developing allergic contact dermatitis. OBJECTIVES: To compare workers throughout the German construction industry with and without skin allergy to epoxy resins, hardeners, and/or reactive diluents, and to investigate which determinants

Phytochemical phenolics in organically grown vegetables.

Science.gov (United States)

Young, Janice E; Zhao, Xin; Carey, Edward E; Welti, Ruth; Yang, Shie-Shien; Wang, Weiqun

2005-12-01

Fruit and vegetable intake is inversely correlated with risks for several chronic diseases in humans. Phytochemicals, and in particular, phenolic compounds, present in plant foods may be partly responsible for these health benefits through a variety of mechanisms. Since environmental factors play a role in a plant's production of secondary metabolites, it was hypothesized that an organic agricultural production system would increase phenolic levels. Cultivars of leaf lettuce, collards, and pac choi were grown either on organically certified plots or on adjacent conventional plots. Nine prominent phenolic agents were quantified by HPLC, including phenolic acids (e. g. caffeic acid and gallic acid) and aglycone or glycoside flavonoids (e. g. apigenin, kaempferol, luteolin, and quercetin). Statistically, we did not find significant higher levels of phenolic agents in lettuce and collard samples grown organically. The total phenolic content of organic pac choi samples as measured by the Folin-Ciocalteu assay, however, was significantly higher than conventional samples (p lettuce and collards, the organic system provided an increased opportunity for insect attack, resulting in a higher level of total phenolic agents in pac choi.

Preparation and characterization of carbon nanotube-hybridized carbon fiber to reinforce epoxy composite

International Nuclear Information System (INIS)

An, Feng; Lu, Chunxiang; Li, Yonghong; Guo, Jinhai; Lu, Xiaoxuan; Lu, Huibin; He, Shuqing; Yang, Yu

2012-01-01

Highlights: → CNTs were uniformly grown onto the carbon fibers. → No obvious mechanical properties of carbon fiber were observed after CNT growth. → The IFSS of multiscale epoxy composite was measured by single fiber pull-out tests. → Observing fractography of composite, the fracture modes of CNTs were discussed. -- Abstract: The multiscale carbon nanotube-hybridized carbon fiber was prepared by a newly developed aerosol-assisted chemical vapour deposition. Scanning electron microscopy and transmission electron microscope were carried out to characterize this multiscale material. Compared with the original carbon fibers, the fabrication of this hybrid fiber resulted in an almost threefold increase of BET surface area to reach 2.22 m 2 /g. Meanwhile, there was a slight degradation of fiber tensile strength within 10%, while the fiber modulus was not significantly affected. The interfacial shearing strength of a carbon fiber-reinforced polymer composite with carbon nanotube-hybridized carbon fiber and an epoxy matrix was determined from the single fiber pull-out tests of microdroplet composite. Due to an efficient increase of load transfer at the fiber/matrix interfaces, the interracial shear strength of composite reinforced by carbon nanotube-hybridized carbon fiber is almost 94% higher than that of one reinforced by the original carbon fiber. Based on the fractured morphologies of the composites, the interfacial reinforcing mechanisms were discussed through proposing different types of carbon nanotube fracture modes along with fiber pulling out from epoxy composites.

Improvement of fatigue resistance of epoxy composite with microencapsulated epoxy-SbF5 self-healing system

Directory of Open Access Journals (Sweden)

X. J. Ye

2017-11-01

Full Text Available Rapid retardation and arresting of fatigue crack are successfully realized in the epoxy composite containing microencapsulated epoxy and ethanol solution of antimony pentafluoride-ethanol complex (SbF5·HOC2H5/HOC2H5. The effects of (i microcapsules induced-toughening, (ii hydrodynamic pressure crack tip shielding offered by the released healing agent, and (iii polymeric wedge and adhesive bonding of cured healing agent account for extension of fatigue life of the material. The two components of the healing agent can quickly react with each other soon after rupture of the microcapsules, and reconnect the crack only 20 seconds as of the test. The applied stress intensity range not only affects the healing efficiency, but also can be used to evaluate the healing speed. The present work offers a very fast healing system, and sets up a framework for characterizing speed of self-healing.

Space charge dynamic of irradiated cyanate ester/epoxy at cryogenic temperatures

Science.gov (United States)

Wang, Shaohe; Tu, Youping; Fan, Linzhen; Yi, Chengqian; Wu, Zhixiong; Li, Laifeng

2018-03-01

Glass fibre reinforced polymers (GFRPs) have been widely used as one of the main electrical insulating structures for superconducting magnets. A new type of GFRP insulation material using cyanate ester/epoxy resin as a matrix was developed in this study, and the samples were irradiated by Co-60 for 1 MGy and 5 MGy dose. Space charge distributed within the sample were tested using the pulsed electroacoustic method, and charge concentration was found at the interfaces between glass fibre and epoxy resin. Thermally stimulated current (TSC) and dc conduction current were also tested to evaluate the irradiation effect. It was supposed that charge mobility and density were suppressed at the beginning due to the crosslinking reaction, and for a higher irradiation dose, molecular chain degradation dominated and led to more sever space charge accumulation at interfaces which enhance the internal electric field higher than the external field, and transition field for conduction current was also decreased by irradiation. Space charge dynamic at cryogenic temperature was revealed by conduction current and TSC, and space charge injection was observed for the irradiated samples at 225 K, which was more obvious for the irradiated samples.

High performance, rapid thermal/UV curing epoxy resin for additive manufacturing of short and continuous carbon fiber epoxy composites

Science.gov (United States)

Lewicki, James

2018-04-17

An additive manufacturing resin system including an additive manufacturing print head; a continuous carbon fiber or short carbon fibers operatively connected to the additive manufacturing print head; and a tailored resin operatively connected to the print head, wherein the tailored resin has a resin mass and wherein the tailored resin includes an epoxy component, a filler component, a catalyst component, and a chain extender component; wherein the epoxy component is 70-95% of the resin mass, wherein the filler component is 1-20% of the resin mass, wherein the catalyst component is 0.1-10% of the resin mass, and wherein the chain extender component is 0-50% of the resin mass.

Pristine and γ-irradiated halloysite reinforced epoxy nanocomposites - Insight study

Science.gov (United States)

Saif, Muhammad Jawwad; Naveed, Muhammad; Zia, Khalid Mahmood; Asif, Muhammad

2016-10-01

The present study focuses on development of epoxy system reinforced with naturally occurring halloysite nanotubes (HNTs). A comparative study is presented describing the performance of pristine and γ-irradiated HNTs in an epoxy matrix. The γ-irradiation treatment was used for structural modification of natural pristine HNTs under air sealed environment at different absorbed doses and subsequently these irradiated HNTs were incorporated in epoxy resin with various wt% loadings. The consequences of γ-irradiation on HNTs were studied by FTIR and X-ray diffraction analysis (XRD) in terms of changes in functional groups and crystalline characteristics. An improvement is observed in mechanical properties and crack resistance of composites reinforced with γ-irradiated HNTs. The irradiated HNTs imparted an improved flexural and tensile strength/modulus along with better thermal performance.

Interactions between iron, phenolic compounds, emulsifiers, and pH in omega-3-enriched oil-in-water emulsions

DEFF Research Database (Denmark)

Sørensen, Ann-Dorit Moltke; Haahr, Anne-Mette; Becker, E.M.

2008-01-01

The behavior of antioxidants in emulsions is influenced by several factors such as pH and emulsifier type. This study aimed to evaluate the interaction between selected food emulsifiers, phenolic compounds, iron, and pH and their effect on the oxidative stability of n-3 polyunsaturated lipids...... products. When iron was present, the pH was crucial for the formation of lipid oxidation products. At pH 3 some phenolic compounds, especially caffeic acid, reduced Fe3+ to Fe2+, and Fe2+ increased lipid oxidation at this pH compared to pH 6. Among the evaluated phenols, caffeic acid had the most...... significant effects, as caffeic acid was found to be prooxidative irrespective of pH, emulsifier type, and presence of iron, although the degrees of lipid oxidation were different at the different experimental conditions. The other evaluated phenols were prooxidative at pH 3 in Citrem-stabilized emulsions...

Exploring biomass based carbon black as filler in epoxy composites: Flexural and thermal properties

International Nuclear Information System (INIS)

Abdul Khalil, H.P.S.; Firoozian, P.; Bakare, I.O.; Akil, Hazizan Md.; Noor, Ahmad Md.

2010-01-01

Carbon blacks (CB), derived from bamboo stem (BS-CB), coconut shells (CNS-CB) and oil palm empty fiber bunch (EFB-CB), were obtained by pyrolysis of fibers at 700 o C, characterized and used as filler in epoxy composites. The results obtained showed that the prepared carbon black possessed well-developed porosities and are predominantly made up of micropores. The BS-CB, CNS-CB and EFB-CB filled composites were prepared and characterized using scanning electron microscope (SEM) and thermogravimetric analyzer (TGA). The SEM showed that the fractured surface of the composite indicates its high resistance to fracture. The CBs-epoxy composites exhibited better flexural properties than the neat epoxy, which was attributed to better adhesion between the CBs and the epoxy resin. TGA showed that there was improvement in thermal stability of the carbon black filled composites compared to the neat epoxy resin.

Static and Dynamic Mechanical Properties of Graphene Oxide-Incorporated Woven Carbon Fiber/Epoxy Composite

Science.gov (United States)

Adak, Nitai Chandra; Chhetri, Suman; Kim, Nam Hoon; Murmu, Naresh Chandra; Samanta, Pranab; Kuila, Tapas

2018-03-01

This study investigates the synergistic effects of graphene oxide (GO) on the woven carbon fiber (CF)-reinforced epoxy composites. The GO nanofiller was incorporated into the epoxy resin with variations in the content, and the CF/epoxy composites were manufactured using a vacuum-assisted resin transfer molding process and then cured at 70 and 120 °C. An analysis of the mechanical properties of the GO (0.2 wt.%)/CF/epoxy composites showed an improvement in the tensile strength, Young's modulus, toughness, flexural strength and flexural modulus by 34, 20, 83, 55 and 31%, respectively, when compared to the CF/epoxy composite. The dynamic mechanical analysis of the composites exhibited an enhancement of 56, 114 and 22% in the storage modulus, loss modulus and damping capacity (tan δ), respectively, at its glass transition temperature. The fiber-matrix interaction was studied using a Cole-Cole plot analysis.

Experimental and theoretical binding affinity between polyvinylpolypyrrolidone and selected phenolic compounds from food matrices.

Science.gov (United States)

Durán-Lara, Esteban F; López-Cortés, Xaviera A; Castro, Ricardo I; Avila-Salas, Fabián; González-Nilo, Fernando D; Laurie, V Felipe; Santos, Leonardo S

2015-02-01

Polyvinylpolypyrrolidone (PVPP) is a fining agent, widely used in winemaking and brewing, whose mode of action in removing phenolic compounds has not been fully characterised. The aim of this study was to evaluate the experimental and theoretical binding affinity of PVPP towards six phenolic compounds representing different types of phenolic species. The interaction between PVPP and phenolics was evaluated in model solutions, where hydroxyl groups, hydrophobic bonding and steric hindrance were characterised. The results of the study indicated that PVPP exhibits high affinity for quercetin and catechin, moderate affinity for epicatechin, gallic acid and lower affinity for 4-methylcatechol and caffeic acid. The affinity has a direct correlation with the hydroxylation degree of each compound. The results show that the affinity of PVPP towards phenols is related with frontier orbitals. This work demonstrates a direct correlation between the experimental affinity and the interaction energy calculations obtained through computational chemistry methods. Copyright © 2014 Elsevier Ltd. All rights reserved.

Grafting of polyethylenimine onto cellulose nanofibers for interfacial enhancement in their epoxy nanocomposites.

Science.gov (United States)

Zhao, Jiangqi; Li, Qingye; Zhang, Xiaofang; Xiao, Meijie; Zhang, Wei; Lu, Canhui

2017-02-10

Cellulose nanofibers (CNFs) were surface-modified with polyethyleneimine (PEI), which brought plentiful amine groups on the surface of CNFs, leading to a reduced hydrogen bond density between CNFs and consequently less CNFs agglomerates. The amine groups could also react with the epoxy as an effective curing agent that could increase the interfacial crosslinking density and strengthen interfacial adhesion. The tensile strength and Young's modulus of CNFs-PEI/Epoxy nanocomposites were 88.1% and 237.6% higher than those of neat epoxy, respectively. The tensile storage modulus of the nanocomposites also increased significantly at the temperature either below or above the Tg. The coefficient of thermal expansion for the CNFs-PEI/Epoxy nanocomposites was 22.2ppmK -1 , much lower than that of the neat epoxy (88.6ppmK -1 ). In addition, the thermal conductivity of the nanocomposites was observed to increase as well. The exceptional and balanced properties may provide the nanocomposites promising applications in automotive, construction and electronic devices. Copyright © 2016 Elsevier Ltd. All rights reserved.

Enhanced mechanical properties of epoxy nanocomposites by mixing noncovalently functionalized boron nitride nanoflakes.

Science.gov (United States)

Lee, Dongju; Song, Sung Ho; Hwang, Jaewon; Jin, Sung Hwan; Park, Kwang Hyun; Kim, Bo Hyun; Hong, Soon Hyung; Jeon, Seokwoo

2013-08-12

The influence of surface modifications on the mechanical properties of epoxy-hexagonal boron nitride nanoflake (BNNF) nanocomposites is investigated. Homogeneous distributions of boron nitride nanoflakes in a polymer matrix, preserving intrinsic material properties of boron nitride nanoflakes, is the key to successful composite applications. Here, a method is suggested to obtain noncovalently functionalized BNNFs with 1-pyrenebutyric acid (PBA) molecules and to synthesize epoxy-BNNF nanocomposites with enhanced mechanical properties. The incorporation of noncovalently functionalized BNNFs into epoxy resin yields an elastic modulus of 3.34 GPa, and 71.9 MPa ultimate tensile strength at 0.3 wt%. The toughening enhancement is as high as 107% compared to the value of neat epoxy. The creep strain and the creep compliance of the noncovalently functionalized BNNF nanocomposite is significantly less than the neat epoxy and the nonfunctionalized BNNF nanocomposite. Noncovalent functionalization of BNNFs is effective to increase mechanical properties by strong affinity between the fillers and the matrix. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Isolation and characterization of phenol degrading yeast.

Science.gov (United States)

Patel, Riddhi; Rajkumar, Shalini

2009-04-01

A phenol degrading yeast isolate was identified and characterized from the soil sample collected from a landfill site, in Ahmedabad, India, by plating the soil dilutions on Sabouraud's Dextrose Agar. The microscopic studies and biochemical tests indicated the isolate to be Saccharomyces cerevisiae. The phenol degrading potential of the isolate was measured by inoculation of pure culture in the mineral medium containing various phenol concentrations ranging from 100 to 800 mg l(-1 )and monitoring phenol disappearance rate at regular intervals of time. Growth of the isolate in mineral medium with various phenol concentrations was monitored by measuring the turbidity (OD(600) nm). The results showed that the isolated yeast was tolerant to phenol up to 800 mg(-1). The phenol degradation ranged from 8.57 to 100% for the concentration of phenol from 800 mg l(-1 )to 200 mg l(-1), respectively. ((c) 2009 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim).

Dynamic Changes in Phenolics and Antioxidant Capacity during Pecan (Carya illinoinensis Kernel Ripening and Its Phenolics Profiles

Directory of Open Access Journals (Sweden)

Xiaodong Jia

2018-02-01

Full Text Available Pecan (Carya illinoinensis kernels have a high phenolics content and a high antioxidant capacity compared to other nuts—traits that have attracted great interest of late. Changes in the total phenolic content (TPC, condensed tannins (CT, total flavonoid content (TFC, five individual phenolics, and antioxidant capacity of five pecan cultivars were investigated during the process of kernel ripening. Ultra-performance liquid chromatography coupled with quadruple time-of-flight mass (UPLC-Q/TOF-MS was also used to analyze the phenolics profiles in mixed pecan kernels. TPC, CT, TFC, individual phenolics, and antioxidant capacity were changed in similar patterns, with values highest at the water or milk stages, lowest at milk or dough stages, and slightly varied at kernel stages. Forty phenolics were tentatively identified in pecan kernels, of which two were first reported in the genus Carya, six were first reported in Carya illinoinensis, and one was first reported in its kernel. The findings on these new phenolic compounds provide proof of the high antioxidant capacity of pecan kernels.

Dynamic Changes in Phenolics and Antioxidant Capacity during Pecan (Carya illinoinensis) Kernel Ripening and Its Phenolics Profiles.