  1. Microstructural variation in titanium oxide thin films deposited by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Pandian, Ramanathaswamy; Natarajan, Gomathi; Kamruddin, M.; Tyagi, A.K.

    2013-01-01

    We report on the microstructural evolution of titanium oxide thin films deposited by reactive DC magnetron sputtering using titanium metal target. By varying the ratio of sputter-gas mixture containing argon, oxygen and nitrogen various phases of titanium oxide, almost pure rutile, rutile-rich and anatase-rich nano-crystalline, were deposited on Si substrates at room temperature. Using high-resolution scanning electron microscopy, X-ray diffraction and micro-Raman techniques the microstructure of the films were revealed. The relationship between the microstructure of the films and the oxygen partial pressure during sputtering is discussed

  2. Effect of thermally grown oxide (TGO) microstructure on the durability of TBCs with PtNiAl diffusion bond coats

    Energy Technology Data Exchange (ETDEWEB)

    Spitsberg, Irene [Materials and Process Engineering Department, GE Aircraft Engines, Evendale, OH (United States)]. E-mail: irene.spitsberg@kennametal.com; More, Karren [Metals and Ceramics Division, Oak Ridge National Laboratory, Oak Ridge, TN (United States)

    2006-02-15

    The role of pre-oxidation surface treatments on the oxide microstructure and the failure mechanism of multi-layer thermal barrier systems based on Pt-modified NiAl bond coats and electron beam deposited thermal barrier coatings (TBCs) have been studied. The primary pre-oxidation experimental variable was the partial pressure of oxygen in the pre-oxidizing atmosphere at constant temperature and bond coat composition. The durability of TBCs deposited on surfaces following different pre-oxidation treatments were measured and compared using furnace cycling tests. The oxide layers corresponding to different levels of TBC performance were characterized microstructurally, chemically, and compositionally using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS) techniques. TBC performance was enhanced by the formation of a surface oxide having a coarse-grained columnar structure during the pre-oxidation process. Increased TBC durability was consistent with a slower oxide growth rate during exposure of the TBC to high-temperature, cyclic conditions, as was observed for this particular pre-oxidation condition. An oxide microstructure having fewer through-thickness transport pathways (grain boundaries) should also result in slower lateral oxide growth rates, consistent with a slowed rate of ratcheting as was observed in the pre-oxidized samples that had the best TBC performance. The desired surface oxide grain structure was achieved by pre-oxidizing the bond coat prior to TBC deposition at an intermediate partial pressure of oxygen.

  3. A microstructure-composition map of a ternary liquid/liquid/particle system with partially-wetting particles.

    Science.gov (United States)

    Yang, Junyi; Roell, David; Echavarria, Martin; Velankar, Sachin S

    2017-11-22

    We examine the effect of composition on the morphology of a ternary mixture comprising two molten polymeric liquid phases (polyisobutylene and polyethylene oxide) and micron-scale spherical silica particles. The silica particles were treated with silanes to make them partially wetted by both polymers. Particle loadings up to 30 vol% are examined while varying the fluid phase ratios across a wide range. Numerous effects of particle addition are catalogued, stabilization of Pickering emulsions and of interfacially-jammed co-continuous microstructures, meniscus-bridging of particles, particle-induced coalescence of the dispersed phase, and significant shifts in the phase inversion composition. Many of the effects are asymmetric, for example particle-induced coalescence is more severe and drop sizes are larger when polyisobutylene is the continuous phase, and particles promote phase continuity of the polyethylene oxide. These asymmetries are likely attributable to a slight preferential wettability of the particles towards the polyethylene oxide. A state map is constructed which classifies the various microstructures within a triangular composition diagram. Comparisons are made between this diagram vs. a previous one constructed for the case when particles are fully-wetted by polyethylene oxide.

  4. On evolving deformation microstructures in non-convex partially damaged solids

    KAUST Repository

    Gurses, Ercan

    2011-06-01

    The paper outlines a relaxation method based on a particular isotropic microstructure evolution and applies it to the model problem of rate independent, partially damaged solids. The method uses an incremental variational formulation for standard dissipative materials. In an incremental setting at finite time steps, the formulation defines a quasi-hyperelastic stress potential. The existence of this potential allows a typical incremental boundary value problem of damage mechanics to be expressed in terms of a principle of minimum incremental work. Mathematical existence theorems of minimizers then induce a definition of the material stability in terms of the sequential weak lower semicontinuity of the incremental functional. As a consequence, the incremental material stability of standard dissipative solids may be defined in terms of weak convexity notions of the stress potential. Furthermore, the variational setting opens up the possibility to analyze the development of deformation microstructures in the post-critical range of unstable inelastic materials based on energy relaxation methods. In partially damaged solids, accumulated damage may yield non-convex stress potentials which indicate instability and formation of fine-scale microstructures. These microstructures can be resolved by use of relaxation techniques associated with the construction of convex hulls. We propose a particular relaxation method for partially damaged solids and investigate it in one- and multi-dimensional settings. To this end, we introduce a new isotropic microstructure which provides a simple approximation of the multi-dimensional rank-one convex hull. The development of those isotropic microstructures is investigated for homogeneous and inhomogeneous numerical simulations. © 2011 Elsevier Ltd. All rights reserved.

  5. Chemical polishing of partially oxidized T-111 alloy

    International Nuclear Information System (INIS)

    Teaney, P.E.

    1974-01-01

    The specimens were pressure-mounted in Bakelite and ground through 600 grit on silicon carbide papers. The specimens were rough-polished on a vibratory polisher for 4 to 6 h, using a water slurry of one micron alumina on Texmet, followed by 0.3-μ alumina on Texmet overnight. Final polishing was accomplished by continuous swabbing with a chemical polish. A chemical polish consisting of ten parts lactic acid, four parts nitric acid, and four parts hydrofluoric acid worked well for the T-111 parent material specimens; however, in the partially oxidized specimens, considerable pitting and staining occurred in the oxygen-affected zone and in the transition zone between the oxygen-affected zone and the parent material. A chemical polish was developed for the partially oxidized specimens by adjusting the ratio of the acids to ten parts lactic acid, two parts nitric acid, and two parts hydrofluoric acid. This slowed the chemical attack on the oxygen-affected zone considerably and, with continuous swabbing, the pitting and stain could be avoided. The specimens were rinsed and checked occasionally on the metallograph to determine when the proper polish had been obtained. Some specimens required intermittent polishing times up to 1 / 2 hour. No relationship could be established between the oxygen content of the specimen and the time required for chemical polishing in the partially oxidized specimens. However, the microstructure of the transition zone was the most difficult to obtain, and specimens with uniform reaction zones across the width of the specimen polished quicker than those with the transition zone

  6. Influence of Nitrogen Partial Pressure on Microstructure and Tribological Properties of Mo-Cu-V-N Composite Coatings with High Cu Content

    Directory of Open Access Journals (Sweden)

    Haijuan Mei

    2018-01-01

    Full Text Available In this study, Mo-Cu-V-N composite coatings with high Cu content of ~18 at.% were deposited on 316L stainless steel and YT14 cemented carbide substrates by high power impulse magnetron sputtering in Ar–N2 gas mixtures. The influence of N2 partial pressure was investigated with respect to the microstructure and tribological properties of the coatings. The results indicated that the Mo-Cu-V-N composite coatings exhibited FCC B1-MoN phase with a strong (200 preferred orientation, and Cu phase was found to exist as metallic species. As the N2 partial pressure increased from 0.11 to 0.35 Pa, the peak intensity of (200 plane decreased gradually and simultaneous peak broadening was observed, which was typical for grain refinement. With increasing the N2 partial pressure, the columnar microstructure became much coarser, which led to the decrease of residual stress and hardness. The Mo-Cu-V-N composite coatings with high Cu content exhibited a relatively low wear rate of 10−8 mm3/N·m at 25 °C, which was believed to be attributed to the mixed lubricious oxides of MoO2, CuO and V2O5 formed during tribo-oxidation, which cannot be formed in the coatings with low Cu content. When the wear temperature was increased up to 400 °C, the wear rate increased sharply up to 10−6 mm3/N·m despite the formation of lubricious oxides of MoO3/CuMoO4 and V2O5. This could be due to the loss of nitrogen and pronounced oxidation at high temperatures, which led the wear mechanism to be transformed from mild oxidation wear to severe oxidation wear.

  7. The effect of substrate microstructure on high temperature oxidation of Zr alloy

    International Nuclear Information System (INIS)

    Li, H.; Lin, J.; Szpunar, J.

    2005-01-01

    'Full text:' Specimens with various substrate microstructures of Zr-2.5Nb, Zircaloy 4 and pure Zr have been oxidized at 500C in air. Oxidation kinetics is measured and the microstructures of both oxide and substrate are analyzed. The difference in oxidation kinetics among various specimens is significant. This difference is explained by the distribution of oxide grain size, grain shape and grain boundary, which are controlled by substrate grain size and β phase distribution. The previously proposed model of Zr oxidation is used to predict oxidation kinetics and oxide microstructure from substrate microstructure. Computer simulation based on the model is performed and simulation results are compared with the experimental results. (author)

  8. New theory for competing interactions and microstructures in partially-ordered (liquid-crystalline) phases

    International Nuclear Information System (INIS)

    Dowell, F.

    1987-01-01

    A summary of results from a unique statistical-physics theory to predict and explain competing interactions and resulting microstructures in some partially-ordered [in this case, liquid-crystalline (LC)] phases is presented. The static aspects of both partial orientational and partial positional ordering of the molecules into various microstructures in these phases (including the incommensurate smectic-Ad phase) can be understood in terms of various competing interactions (both entropic and energetic) involved in the packing together of the different molecular sub-units at given pressures and temperatures. These microstructures are predicted and explained (using no ad hoc or arbitrarily adjustable parameter) as a function of molecule chemical structure [including lengths and shapes (from bond lengths and angles), intramolecular rotations, site-site polarizabilities and pair potentials, dipole moments, etc]. Theoretical results are presented for the nematic, re-entrant nematic, smectic-Ad, and smectic-Al LC phases and the isotropic phase

  9. Microstructural aspects of the oxidation of zirconium alloys

    International Nuclear Information System (INIS)

    Proff, Ch.

    2011-01-01

    This thesis is focused on the microstructural characterisation of precipitates in the oxide of binary zirconium alloys (1 wt.% Fe, Cr or Ni or 0.6 wt.% Nb) under different oxidation conditions at 415 C. The samples were oxidised in autoclave in air and steam and in an environmental scanning electron microscope in water vapour. The microstructural evolution of the precipitates during oxidation was characterised using electron microscopy. The findings from the analysis are the following: -Two types of oxidation behaviour are observed for precipitates. -Pilling Bedworth ratio of precipitates is higher than that of the zirconium matrix. -Formation of pure iron oxide crystals on the surface for iron bearing precipitates close to or at the surface. From these observations it is concluded that the precipitate oxidation behaviour can be correlated to precipitate composition and oxidation tendency of the elements in the precipitates. Iron exhibits clearly different behaviour. (author)

  10. On evolving deformation microstructures in non-convex partially damaged solids

    KAUST Repository

    Gurses, Ercan; Miehe, Christian

    2011-01-01

    . These microstructures can be resolved by use of relaxation techniques associated with the construction of convex hulls. We propose a particular relaxation method for partially damaged solids and investigate it in one- and multi-dimensional settings. To this end, we

  11. Microstructural development in physical vapour-deposited partially stabilized zirconia thermal barrier coatings

    Energy Technology Data Exchange (ETDEWEB)

    Sohn, Y. H. (Center for Intelligent Processing of Materials, Worcester Polytechnic Institute, 100 Institute Road, Worcester, MA 01609-2280 (United States)); Biederman, R.R. (Center for Intelligent Processing of Materials, Worcester Polytechnic Institute, 100 Institute Road, Worcester, MA 01609-2280 (United States)); Sisson, R.D. Jr. (Center for Intelligent Processing of Materials, Worcester Polytechnic Institute, 100 Institute Road, Worcester, MA 01609-2280 (United States))

    1994-10-01

    The effects of processing parameters of physical vapour deposition on the microstructure of partially stabilized zirconia (PSZ) thermal barrier coatings have been experimentally investigated. Emphasis has been placed on the crystallographic texture of the PSZ coatings and the microstructure of the top surface of the PSZ coatings as well as the metal-ceramic interface. The variations in the deposition chamber temperature, substrate thickness, substrate rotation and vapour incidence angle resulted in the observation of significant differences in the crystallographic texture and microstructure of the PSZ coatings. ((orig.))

  12. Oxidation behaviour of Zr-Ce alloys. Kinetic and microstructure aspects

    International Nuclear Information System (INIS)

    Rouillon, Ludovic

    1996-01-01

    As Zircaloy alloys are used for fuel rods in pressurized water nuclear reactors, this research thesis aims at studying and improving corrosion resistance of zirconium alloys while maintaining their mechanical properties. It more precisely deals with the kinetic and microstructure aspects of the external corrosion of the cladding by the coolant. In the case of Zircaloys, this corrosion is characterized by a kinetic transition from an initially parabolic to a linear regime. This research aims at intervening on this transition by elaborating zirconium alloys containing an element which stabilizes zirconia, in this case cerium. After having reported a bibliographical study on sheath oxidation, on parameters which influence sheath oxidation kinetics, on zirconia stabilization by doping elements, on the interest of lanthanide oxides, the author reports a feasibility study on the use of cerium (choice and preparation, sintered ceramic characterization, annealing of stabilized zirconia), reports a metallurgical study of Zr-Ce alloys, reports the study of the oxidation behaviour of these alloys (in autoclave, in presence of oxygen, under oxygen and then water) and the characterization of the microstructures of the oxide layers. He finally discusses the relationship between microstructure and oxidation kinetics, the role of cerium in the oxidation process, and the role of water in the oxidation process [fr

  13. Microstructure and oxidation performance of a γ–γ′ Pt-aluminide ...

    Indian Academy of Sciences (India)

    Microstructure and oxidation performance of a –' Pt-aluminide bond coat on directionally solidified superalloy CM-247LC ... Keywords. Platinum aluminide bond coat; coating; cyclic oxidation; superalloy; microstructure. ... Defence Metallurgical Research Laboratory, Kanchanbagh, Hyderabad 500 058, India ...

  14. Impact of Microstructure on MoS2 Oxidation and Friction.

    Science.gov (United States)

    Curry, John F; Wilson, Mark A; Luftman, Henry S; Strandwitz, Nicholas C; Argibay, Nicolas; Chandross, Michael; Sidebottom, Mark A; Krick, Brandon A

    2017-08-23

    This work demonstrates the role of microstructure in the friction and oxidation behavior of the lamellar solid lubricant molybdenum disulfide (MoS 2 ). We report on systematic investigations of oxidation and friction for two MoS 2 films with distinctively different microstructures-amorphous and planar/highly-ordered-before and after exposure to atomic oxygen (AO) and high-temperature (250 °C) molecular oxygen. A combination of experimental tribology, molecular dynamics simulations, X-ray photoelectron spectroscopy (XPS), and high-sensitivity low-energy ion scattering (HS-LEIS) was used to reveal new insights about the links between structure and properties of these widely utilized low-friction materials. Initially, ordered MoS 2 films showed a surprising resistance to both atomic and molecular oxygens (even at elevated temperature), retaining characteristic low friction after exposure to extreme oxidative environments. XPS shows comparable oxidation of both coatings via AO; however, monolayer resolved compositional depth profiles from HS-LEIS reveal that the microstructure of the ordered coatings limits oxidation to the first atomic layer.

  15. Microstructure characterizaton of advanced oxide fuel

    International Nuclear Information System (INIS)

    Rasmussen, D.E.; Gerber, E.W.; McCord, R.B.

    1977-01-01

    Preirradiation porosity, grain size, and microcomposition characteristics are presented for selected advanced oxide (PuO 2 -UO 2 ) LMFBR developmental fuels fabricated for irradiation testing in EBR-II. Quantitative microscopy, electron microprobe analysis, and a recently developed quantitative autoradiographic technique are utilized to relate microstructure characteristics to fabrication parameters

  16. Microstructure, characterizations, functionality and compressive strength of cement-based materials using zinc oxide nanoparticles as an additive

    Energy Technology Data Exchange (ETDEWEB)

    Nochaiya, Thanongsak [Department of Physics, Faculty of Science, Naresuan University, Phitsanulok 65000 (Thailand); Sekine, Yoshika [Department of Chemistry, School of Science, Tokai University, 4-1-1 Kitakaname, Hiratsuka, Kanagawa 259-1292 (Japan); Choopun, Supab [Applied Physics Research Laboratory, Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Chaipanich, Arnon, E-mail: arnon.chaipanich@cmu.ac.th [Advanced Cement-Based Materials Research Unit, Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand)

    2015-05-05

    Highlights: • Nano zinc oxide was used as an additive material. • Microstructure and phase characterization of pastes were characterized using SEM and XRD. • TGA and FTIR were also used to determine the hydration reaction. • Compressive strength of ZnO mixes was found to increase at 28 days. - Abstract: Zinc oxide nanoparticles as a nanophotocatalyst has great potential for self-cleaning applications in concrete structures, its effects on the cement hydration, setting time and compressive strength are also important when using it in practice. This paper reports the effects of zinc oxide nanoparticles, as an additive material, on properties of cement-based materials. Setting time, compressive strength and porosity of mortars were investigated. Microstructure and morphology of pastes were characterized using scanning electron microscope and X-ray diffraction (XRD), respectively. Moreover, thermal gravimetric analysis (TGA) and Fourier-transform infrared spectrometer (FTIR) were also used to determine the hydration reaction. The results show that Portland cement paste with additional ZnO was found to slightly increase the water requirement while the setting time presented prolongation period than the control mix. However, compressive strength of ZnO mixes was found to be higher than that of PC mix up to 15% (at 28 days) via filler effect. Microstructure, XRD and TGA results of ZnO pastes show less hydration products before 28 days but similar at 28 days. In addition, FTIR results confirmed the retardation when ZnO was partially added in Portland cement pastes.

  17. Microstructure, characterizations, functionality and compressive strength of cement-based materials using zinc oxide nanoparticles as an additive

    International Nuclear Information System (INIS)

    Nochaiya, Thanongsak; Sekine, Yoshika; Choopun, Supab; Chaipanich, Arnon

    2015-01-01

    Highlights: • Nano zinc oxide was used as an additive material. • Microstructure and phase characterization of pastes were characterized using SEM and XRD. • TGA and FTIR were also used to determine the hydration reaction. • Compressive strength of ZnO mixes was found to increase at 28 days. - Abstract: Zinc oxide nanoparticles as a nanophotocatalyst has great potential for self-cleaning applications in concrete structures, its effects on the cement hydration, setting time and compressive strength are also important when using it in practice. This paper reports the effects of zinc oxide nanoparticles, as an additive material, on properties of cement-based materials. Setting time, compressive strength and porosity of mortars were investigated. Microstructure and morphology of pastes were characterized using scanning electron microscope and X-ray diffraction (XRD), respectively. Moreover, thermal gravimetric analysis (TGA) and Fourier-transform infrared spectrometer (FTIR) were also used to determine the hydration reaction. The results show that Portland cement paste with additional ZnO was found to slightly increase the water requirement while the setting time presented prolongation period than the control mix. However, compressive strength of ZnO mixes was found to be higher than that of PC mix up to 15% (at 28 days) via filler effect. Microstructure, XRD and TGA results of ZnO pastes show less hydration products before 28 days but similar at 28 days. In addition, FTIR results confirmed the retardation when ZnO was partially added in Portland cement pastes

  18. Microstructure and oxidation behaviour of aluminized coating of inconel 625

    International Nuclear Information System (INIS)

    Khalid, F.A.; Hussain, N.; Shahid, K.A.; Rehman, S.; Qureshi, A.H.; Khan, I.H.

    1999-01-01

    Microstructural and oxidation characteristics of aluminized coated Inconel 625 have been examined using scanning electron microscopy (SEM) and fine-probe spot and linescan EDS microanalysis techniques. The formation of slowly growing adherent metallic coatings is essential for protection against the severe environments. Aluminising of the superalloy samples was carried out by pack cementation process at 900 deg. C. in an argon atmosphere. The samples were subsequently oxidized in air at various temperatures to examine performance of the pack aluminized coated alloy. The microstructural changes that occurred in the aluminized layer at various exposure temperature and time were examined to study the oxidation behavior and formation of different phases in the aluminized coating deposited on Inconel 625. (author)

  19. Partial oxidation of 2-propanol on perovskites

    Energy Technology Data Exchange (ETDEWEB)

    Sumathi, R.; Viswanathan, B.; Varadarajan, T.K. [Indian Inst. of Tech., Madras (India). Dept. of Chemistry

    1998-12-31

    Partial oxidation of 2-propanol was carried out on AB{sub 1-x}B`{sub x}O{sub 3} (A=Ba, B=Pb, Ce, Ti; B`=Bi, Sb and Cu) type perovskite oxides. Acetone was the major product observed on all the catalysts. All the catalysts underwent partial reduction during the reaction depending on the composition of the reactant, nature of the B site cation and the extent of substitution at B site. The catalytic activity has been correlated with the reducibility of the perovskite oxides determined from Temperature Programmed Reduction (TPR) studies. (orig.)

  20. Tracking Solid Oxide Cell Microstructure Evolution by High Resolution 3D Nano-Tomography

    DEFF Research Database (Denmark)

    De Angelis, Salvatore

    . The degradation processes are mainly attributed to morphological changes occurring within the electrodes microstructure. Therefore, precise tracking of 3D microstructural evolution during operation is considered crucial to understanding the complex relationship between microstructure and performance. In this work......, X-ray ptychographic tomography is applied to SOC materials, demonstrating unprecedented spatial resolution and data quality. The eect of a complete redox cycle on the same Ni-YSZ microstructure is visualized ex-situ in 3D, showing major rearrangement of the nickel network after reduction......, the formation of cracks in the YSZ, and void formation in nickel oxide after oxidation. Capitalizing on the high resolution of ptychography, the eect of nickel coarsening on the Ni-YSZ microstructure evolution is studied ex-situ in three dimensions, while the sample is repeatedly scanned and treated at high...

  1. Design and In-Situ Processing of Metal-Ceramic and Ceramic-Ceramic Microstructures

    National Research Council Canada - National Science Library

    Sass, Stephen

    1997-01-01

    .... Metal-ceramic microstructures have been synthesized in situ by a variety of novel processing techniques, including the partial reduction of oxide compounds and displacement reactions and sol-gel...

  2. Reactor modeling and process analysis for partial oxidation of natural gas

    NARCIS (Netherlands)

    Albrecht, B.A.

    2004-01-01

    This thesis analyses a novel process of partial oxidation of natural gas and develops a numerical tool for the partial oxidation reactor modeling. The proposed process generates syngas in an integrated plant of a partial oxidation reactor, a syngas turbine and an air separation unit. This is called

  3. Electrochemical and partial oxidation of methane

    Science.gov (United States)

    Singh, Rahul

    2008-10-01

    Hydrogen has been the most common fuel used for the fuel cell research but there remains challenging technological hurdles and storage issues with hydrogen fuel. The direct electrochemical oxidation of CH4 (a major component of natural gas) in a solid oxide fuel cell (SOFC) to generate electricity has a potential of commercialization in the area of auxiliary and portable power units and battery chargers. They offer significant advantages over an external reformer based SOFC, namely, (i) simplicity in the overall system architecture and balance of plant, (ii) more efficient and (iii) availability of constant concentration of fuel in the anode compartment of SOFC providing stability factor. The extreme operational temperature of a SOFC at 700-1000°C provides a thermodynamically favorable pathway to deposit carbon on the most commonly used Ni anode from CH4 according to the following reaction (CH4 = C + 2H2), thus deteriorating the cell performance, stability and durability. The coking problem on the anode has been a serious and challenging issue faced by the catalyst research community worldwide. This dissertation presents (i) a novel fabricated bi-metallic Cu-Ni anode by electroless plating of Cu on Ni anode demonstrating significantly reduced or negligible coke deposition on the anode for CH4 and natural gas fuel after long term exposure, (ii) a thorough microstructural examination of Ni and Cu-Ni anode exposed to H2, CH4 and natural gas after long term exposure at 750°C by scanning electron microscopy, energy dispersive X-ray spectroscopy and X-ray diffraction and (iii) in situ electrochemical analysis of Ni and Cu-Ni for H2, CH4 and natural gas during long term exposure at 750°C by impedance spectroscopy. A careful investigation of variation in the microstructure and performance characteristics (voltage-current curve and impedance) of Ni and Cu-Ni anode before and after a long term exposure of CH4 and natural gas would allow us to test the validation of a

  4. Comparative analysis of graphite oxidation behaviour based on microstructure

    Energy Technology Data Exchange (ETDEWEB)

    Badenhorst, Heinrich, E-mail: heinrich.badenhorst@up.ac.za; Focke, Walter

    2013-11-15

    Two unidentified powdered graphite samples, from a natural and a synthetic origin respectively, were examined. These materials are intended for use in nuclear applications, but have an unknown treatment history since they are considered proprietary. In order to establish a baseline for comparison, the samples were compared to two commercial flake natural graphite samples with varying impurity levels. The samples were characterized by conventional techniques such as powder X-ray diffraction, Raman spectroscopy and X-ray fluorescence. The results indicated that all four samples were very similar, with low impurity levels and good crystallinity, yet they exhibit remarkably different oxidation behaviours. The oxidized microstructures of the materials were examined using high-resolution scanning electron microscopy at low acceleration voltages. The relative influence of each factor affecting the oxidation was established, enabling a structured comparison of the different oxidative behaviours. Based on this analysis, it was possible to account for the measured differences in oxidative reactivity. The material with the lowest reactivity was a flake natural graphite which was characterized as having highly visible crystalline perfection, large particles with a high aspect ratio and no traces of catalytic activity. The second sample, which had an identical inherent microstructure, was found to have an increased reactivity due to the presence of small catalytic impurities. This material also exhibited a more gradual reduction in the oxidation rate at higher conversion, caused by the accumulation of particles which impede the oxidation. The sample with the highest reactivity was found to be a milled, natural graphite material, despite its evident crystallinity. The increased reactivity was attributable to a smaller particle size, the presence of catalytic impurities and extensive damage to the particle structure caused by jet milling. Despite displaying the lowest levels of

  5. Analysis of the Microstructure and Oxidation Behavior of Some Commercial Carbon Fibers

    International Nuclear Information System (INIS)

    Kim, Dae Ho; Kim, Bohye; Yang, Kap Seung; Im, Hun Kook; Bang, Yun Hyuk; Kim, Sung Ryong

    2011-01-01

    The relationship between the microstructure, mechanical properties, and oxidation behavior of pitch-, polyacrylonitrile (PAN)-, and Rayon-based carbon fibers (CFs) has been studied in detail. Three types of carbon fiber were exposed to isothermal oxidation in air and the weight change was measured by thermogravimetric analyzer (TGA) apparatus. After activation energy was gained according to the conversion at reacting temperature, the value of specific surface area and the surface morphology was compared, and the reaction mechanism of oxidation affecting development of pores of carbon fibers was examined. This study will lead to a new insight into the relationship between the microstructure and mechanical properties of carbon fibers

  6. Partial oxidation process

    International Nuclear Information System (INIS)

    Najjar, M.S.

    1987-01-01

    A process is described for the production of gaseous mixtures comprising H/sub 2/+CO by the partial oxidation of a fuel feedstock comprising a heavy liquid hydrocarbonaceous fuel having a nickel, iron, and vanadium-containing ash or petroleum coke having a nickel, iron, and vanadium-containing ash, or mixtures thereof. The feedstock includes a minimum of 0.5 wt. % of sulfur and the ash includes a minimum of 5.0 wt. % vanadium, a minimum of 0.5 ppm nickel, and a minimum of 0.5 ppm iron. The process comprises: (1) mixing together a copper-containing additive with the fuel feedstock; wherein the weight ratio of copper-containing additive to ash in the fuel feedstock is in the range of about 1.0-10.0, and there is at least 10 parts by weight of copper for each part by weight of vanadium; (2) reacting the mixture from (1) at a temperature in the range of 2200 0 F to 2900 0 F and a pressure in the range of about 5 to 250 atmospheres in a free-flow refactory lined partial oxidation reaction zone with a free-oxygen containing gas in the presence of a temperature moderator and in a reducing atmosphere to produce a hot raw effluent gas stream comprising H/sub 2/+CO and entrained molten slag; and where in the reaction zone and the copper-containing additive combines with at least a portion of the nickel and iron constituents and sulfur found in the feedstock to produce a liquid phase washing agent that collects and transports at least a portion of the vanadium-containing oxide laths and spinels and other ash components and refractory out of the reaction zone; and (3) separating nongaseous materials from the hot raw effluent gas stream

  7. Hydrogen Production by Catalytic Partial Oxidation of Coke Oven Gas in BaCo0.7Fe0.3-xZrxO3-δ Ceramic Membrane Reactors

    Directory of Open Access Journals (Sweden)

    Yao Weilin

    2016-01-01

    Full Text Available The BaCo0.7Fe0.3-xZrxO3-δ (BCFZ, x = 0.04–0.12 mixed ionic–electronic conducting (MIEC membranes were synthesized with a sol–gel method and evaluated as potential membrane reactor materials for the partial oxidation of coke oven gas (COG. The effect of zirconium content on the phase structure, microstructure and performance of the BCFZ membrane under He or COG atmosphere were systemically investigated. The BaCo0.7Fe0.24Zr0.06O3-δ membrane exhibited the best oxygen permeability and good operation stability, which could be a potential candidate of the membrane materials for hydrogen production through the partial oxidation of COG.

  8. Microstructures and oxidation behavior of some Molybdenum based alloys

    Energy Technology Data Exchange (ETDEWEB)

    Ray, Pratik Kumar [Iowa State Univ., Ames, IA (United States)

    2011-01-01

    The advent of Ni based superalloys revolutionized the high temperature alloy industry. These materials are capable of operating in extremely harsh environments, comprising of temperatures around 1050 C, under oxidative conditions. Demands for increased fuel efficiency, however, has highlighted the need for materials that can be used under oxidative conditions at temperatures in excess of 1200 C. The Ni based superalloys are restricted to lower temperatures due to the presence of a number of low melting phases that melt in the 1250 - 1450 C, resulting in softening of the alloys above 1000 C. Therefore, recent research directions have been skewed towards exploring and developing newer alloy systems. This thesis comprises a part of such an effort. Techniques for rapid thermodynamic assessments were developed and applied to two different systems - Mo-Si alloys with transition metal substitutions (and this forms the first part of the thesis) and Ni-Al alloys with added components for providing high temperature strength and ductility. A hierarchical approach towards alloy design indicated the Mo-Ni-Al system as a prospective candidate for high temperature applications. Investigations on microstructures and oxidation behavior, under both isothermal and cyclic conditions, of these alloys constitute the second part of this thesis. It was seen that refractory metal systems show a marked microstructure dependence of oxidation.

  9. Microstructure And Mechanical Properties Of Lead Oxide- Thermoplastic Elas Tomer Composite

    International Nuclear Information System (INIS)

    Sudirman; Handayani, Ari; Darwinto, Tri; Teguh, Yulius S.P.P.; Sunarni, Anik; Marlijanti, Isni

    2000-01-01

    Research on microstructure and mechanical properties of lead oxide-thermoplastic elastomer composite with Pb 3 O 4 as lead oxide. Thermoplastic elastomer synthesized from natural rubber as the elastomer and methyl metacrilate as the thermoplastic and irradiated simultaneously with optimum gamma ray. Thermoplastic elastomer (NR-PMMA) grind in a laboplastomill and Pb 3 O 4 was added in varied amount of 10%. 30%. 40% and 50%wt.The results showed that mechanical properties (tensile strength and elongation break) decreased as the Pb 3 O 4 composition increased. Microstructure from SEM observation showed that Pb 3 O 4 distributed evenly and having function as filler in composite

  10. Enhanced performance of solid oxide electrolysis cells by integration with a partial oxidation reactor: Energy and exergy analyses

    International Nuclear Information System (INIS)

    Visitdumrongkul, Nuttawut; Tippawan, Phanicha; Authayanun, Suthida; Assabumrungrat, Suttichai; Arpornwichanop, Amornchai

    2016-01-01

    Highlights: • Process design of solid oxide electrolyzer integrated with a partial oxidation reactor is studied. • Effect of key operating parameters of partial oxidation reactor on the electrolyzer performance is presented. • Exergy analysis of the electrolyzer process is performed. • Partial oxidation reactor can enhance the solid oxide electrolyzer performance. • Partial oxidation reactor in the process is the highest exergy destruction unit. - Abstract: Hydrogen production without carbon dioxide emission has received a large amount of attention recently. A solid oxide electrolysis cell (SOEC) can produce pure hydrogen and oxygen via a steam electrolysis reaction that does not emit greenhouse gases. Due to the high operating temperature of SOEC, an external heat source is required for operation, which also helps to improve SOEC performance and reduce operating electricity. The non-catalytic partial oxidation reaction (POX), which is a highly exothermic reaction, can be used as an external heat source and can be integrated with SOEC. Therefore, the aim of this work is to study the effect of operating parameters of non-catalytic POX (i.e., the oxygen to carbon ratio, operating temperature and pressure) on SOEC performance, including exergy analysis of the process. The study indicates that non-catalytic partial oxidation can enhance the hydrogen production rate and efficiency of the system. In terms of exergy analysis, the non-catalytic partial oxidation reactor is demonstrated to be the highest exergy destruction unit due to irreversible chemical reactions taking place, whereas SOEC is a low exergy destruction unit. This result indicates that the partial oxidation reactor should be improved and optimally designed to obtain a high energy and exergy system efficiency.

  11. Microstructure Evolution of Mg-Gd-Y-Zn-Zr Magnesium Alloy During Partial Remelting

    Directory of Open Access Journals (Sweden)

    Jianquan TAO

    2014-12-01

    Full Text Available The article deals with the research on the microstructure evolution of Mg-Gd-Y-Zn-Zr magnesium alloy through partial remelting process. It aims at finding out what effects the microstructure of semi-solid Mg-Gd-Y-Zn-Zr alloy will result in under different remelting temperatures and holding times. Based on the results, if to raise the remelting temperature and to prolong the holding time, the size of solid grain will tend to expand and its spheroidization degree also begins to show improvement. In addition, the grain shows tendency of coarsening when the holding time increases. DOI: http://dx.doi.org/10.5755/j01.ms.20.4.6483

  12. Role of oxygen partial pressure in microstructural development and properties of YBCO superconductors

    International Nuclear Information System (INIS)

    Singh, J.P.; Guttschow, R.; Dusek, J.T.; Poeppel, R.B.

    1991-01-01

    Results are presented for the effect of oxygen partial pressure (pO 2 ) on the sintered density and microstructure of YBCO superconductors. Extruded YBCO wires were sintered at 910C at different values of pO 2 . Generally, the density increased with decreasing pO 2 , and a density of 91% was achieved at pO 2 = 0.01 atm. Wires sintered at pO 2 = 0.01 atm had a fine microstructure with an average grain size of ∼3 μm and an average strength of 191 MPa. The high strength is due to the small grain size, which causes a decrease in residual tensile stress because of grain anisotropy

  13. Effects of oxide distributed in grain boundaries on microstructure stability of nanocrystalline metals

    Science.gov (United States)

    Zhou, Kai; Li, Hui; Biao Pang, Jin; Wang, Zhu

    2013-06-01

    Nanocrystalline copper and zinc prepared by high-pressure compaction method have been studied by positron lifetime spectroscopy associated with X-ray diffraction. For nanocrystalline Cu, mean grain sizes of the samples decrease after being annealed at 900 °C and increase during aging at 180 °C, revealing that the atoms exchange between the two regions. The positron lifetime results indicate that the vacancy clusters formed in the annealing process are unstable and decomposed at the aging time below 6 hours. In addition, the partially oxidized surfaces of the nanoparticles hinder the grain growth during the ageing at 180 °C, and the vacancy clusters inside the disorder regions which are related to Cu2O need longer aging time to decompose. In the case of nanocrystalline Zn, the open volume defect (not larger than divacancy) is dominant according to the high relative intensity for the short positron lifetime (τ1). The oxide (ZnO) inside the grain boundaries has been found having an effect to hinder the decrease of average positron lifetime (τav) during the annealing, which probably indicates that the oxide stabilizes the microstructure of the grain boundaries. For both nanocrystalline copper and zinc, the oxides in grain boundaries enhance the thermal stability of the microstucture, in spite of their different crystal structures. This effect is very important for the nanocrystalline materials using as radiation resistant materials.

  14. Effects of oxide distributed in grain boundaries on microstructure stability of nanocrystalline metals

    International Nuclear Information System (INIS)

    Zhou Kai; Li Hui; Pang Jinbiao; Wang Zhu

    2013-01-01

    Nanocrystalline copper and zinc prepared by high-pressure compaction method have been studied by positron lifetime spectroscopy associated with X-ray diffraction. For nanocrystalline Cu, mean grain sizes of the samples decrease after being annealed at 900 °C and increase during aging at 180 °C, revealing that the atoms exchange between the two regions. The positron lifetime results indicate that the vacancy clusters formed in the annealing process are unstable and decomposed at the aging time below 6 hours. In addition, the partially oxidized surfaces of the nanoparticles hinder the grain growth during the ageing at 180 °C, and the vacancy clusters inside the disorder regions which are related to Cu 2 O need longer aging time to decompose. In the case of nanocrystalline Zn, the open volume defect (not larger than divacancy) is dominant according to the high relative intensity for the short positron lifetime (τ 1 ). The oxide (ZnO) inside the grain boundaries has been found having an effect to hinder the decrease of average positron lifetime (τ av ) during the annealing, which probably indicates that the oxide stabilizes the microstructure of the grain boundaries. For both nanocrystalline copper and zinc, the oxides in grain boundaries enhance the thermal stability of the microstucture, in spite of their different crystal structures. This effect is very important for the nanocrystalline materials using as radiation resistant materials.

  15. Microstructure and Oxidation Behavior of CrAl Laser-Coated Zircaloy-4 Alloy

    Directory of Open Access Journals (Sweden)

    Jeong-Min Kim

    2017-02-01

    Full Text Available Laser coating of a CrAl layer on Zircaloy-4 alloy was carried out for the surface protection of the Zr substrate at high temperatures, and its microstructural and thermal stability were investigated. Significant mixing of CrAl coating metal with the Zr substrate occurred during the laser surface treatment, and a rapidly solidified microstructure was obtained. A considerable degree of diffusion of solute atoms and some intermetallic compounds were observed to occur when the coated specimen was heated at a high temperature. Oxidation appears to proceed more preferentially at Zr-rich region than Cr-rich region, and the incorporation of Zr into the CrAl coating layer deteriorates the oxidation resistance because of the formation of thermally unstable Zr oxides.

  16. Evaluation of microstructural parameters of oxide dispersion strengthened steels from X-ray diffraction profiles

    International Nuclear Information System (INIS)

    Vlasenko, Svetlana; Benediktovitch, Andrei; Ulyanenkova, Tatjana; Uglov, Vladimir; Skuratov, Vladimir; O'Connell, Jacques; Neethling, Johannes

    2016-01-01

    The microstructural parameters of oxide dispersion strengthened (ODS) steels from measured diffraction profiles were evaluated using an approach where the complex oxide nanoparticles (Y 2 Ti 2 O 7 and Y 4 Al 2 O 9 ) are modeled as spherical inclusions in the steel matrix with coherent or incoherent boundaries. The proposed method enables processing of diffraction data from materials containing spherical inclusions in addition to straight dislocations, and taking into account broadening due to crystallite size and instrumental effects. The parameters of crystallite size distribution modeled by a lognormal distribution function (the parameters m and σ), the strain anisotropy parameter q, the dislocation density ρ, the dislocation arrangement parameter M, the density of oxide nanoparticles ρ np and the nanoparticle radius r 0 were determined for the ODS steel samples. The results obtained are in good agreement with the results of transmission electron microscopy (TEM). - Highlights: • The microstructural parameters of oxide dispersion strengthened steels were obtained. • The microstructure of irradiated and unirradiated samples was investigated. • Oxide nanoparticles are modeled as spherical inclusions. • We considered the influence of dislocations, inclusions and size effects.

  17. Evaluation of microstructural parameters of oxide dispersion strengthened steels from X-ray diffraction profiles

    Energy Technology Data Exchange (ETDEWEB)

    Vlasenko, Svetlana, E-mail: svetlana.vlasenko.bsu@gmail.com [Belarusian State University, Nezavisimosti Avenue 4, Minsk (Belarus); Benediktovitch, Andrei [Belarusian State University, Nezavisimosti Avenue 4, Minsk (Belarus); Ulyanenkova, Tatjana [Rigaku Europe SE, Am Hardtwald 11, Ettlingen (Germany); Uglov, Vladimir [Belarusian State University, Nezavisimosti Avenue 4, Minsk (Belarus); Tomsk Polytechnic University, Lenina Avenue 2a, Tomsk (Russian Federation); Skuratov, Vladimir [Flerov Laboratory of Nuclear Reactions, Joint Institute for Nuclear Research, Dubna (Russian Federation); O' Connell, Jacques; Neethling, Johannes [Centre for High Resolution Transmission Electron Microscopy, Nelson Mandela Metropolitan University, Port Elizabeth (South Africa)

    2016-03-15

    The microstructural parameters of oxide dispersion strengthened (ODS) steels from measured diffraction profiles were evaluated using an approach where the complex oxide nanoparticles (Y{sub 2}Ti{sub 2}O{sub 7} and Y{sub 4}Al{sub 2}O{sub 9}) are modeled as spherical inclusions in the steel matrix with coherent or incoherent boundaries. The proposed method enables processing of diffraction data from materials containing spherical inclusions in addition to straight dislocations, and taking into account broadening due to crystallite size and instrumental effects. The parameters of crystallite size distribution modeled by a lognormal distribution function (the parameters m and σ), the strain anisotropy parameter q, the dislocation density ρ, the dislocation arrangement parameter M, the density of oxide nanoparticles ρ{sub np} and the nanoparticle radius r{sub 0} were determined for the ODS steel samples. The results obtained are in good agreement with the results of transmission electron microscopy (TEM). - Highlights: • The microstructural parameters of oxide dispersion strengthened steels were obtained. • The microstructure of irradiated and unirradiated samples was investigated. • Oxide nanoparticles are modeled as spherical inclusions. • We considered the influence of dislocations, inclusions and size effects.

  18. Microstructured fibers with high lanthanum oxide glass core for nonlinear applications

    Science.gov (United States)

    Kobelke, J.; Schuster, K.; Litzkendorf, D.; Schwuchow, A.; Kirchhof, J.; Bartelt, H.; Tombelaine, V.; Leproux, P.; Couderc, V.; Labruyere, A.

    2009-05-01

    We demonstrate a low loss microstructured fiber (MOF) with a high nonlinear glass core and silica holey cladding. The substitution of mostly used silica as core material of microstructured fibers by lanthanum oxide glass promises a high nonlinear conversion efficiency for supercontinuum (SC) generation. The glass composition is optimized in terms of thermochemical and optical requirements. The glass for the MOF core has a high lanthanum oxide concentration (10 mol% La2O3) and a good compatibility with the silica cladding. This is performed by adding a suitable alumina concentration up to 20 mol%. The lanthanum oxide glass preform rods were manufactured by melting technique. Besides purity issues the material homogeneity plays an important role to achieve low optical loss. The addition of fluorides allows the better homogenization of the glass composition in the preform volume by refining. The minimum attenuation of an unstructured fiber drawn from this glass is about 0.6 dB/m. It is mostly caused by decreasing of scattering effects. The microstructured silica cladding allows the considerable shifting of dispersive behavior of the MOF for an optimal pump light conversion. The MOF shows zero dispersion wavelengths (ZDW) of 1140 nm (LP01 mode) and 970 nm (LP11 mode). The supercontinuum generation was investigated with a 1064 nm pump laser (650 ps). It shows a broad band emission between 500 nm and 2200 nm.

  19. Heterogeneous Partial (ammOxidation and Oxidative Dehydrogenation Catalysis on Mixed Metal Oxides

    Directory of Open Access Journals (Sweden)

    Jacques C. Védrine

    2016-01-01

    Full Text Available This paper presents an overview of heterogeneous partial (ammoxidation and oxidative dehydrogenation (ODH of hydrocarbons. The review has been voluntarily restricted to metal oxide-type catalysts, as the partial oxidation field is very broad and the number of catalysts is quite high. The main factors of solid catalysts for such reactions, designated by Grasselli as the “seven pillars”, and playing a determining role in catalytic properties, are considered to be, namely: isolation of active sites (known to be composed of ensembles of atoms, Me–O bond strength, crystalline structure, redox features, phase cooperation, multi-functionality and the nature of the surface oxygen species. Other important features and physical and chemical properties of solid catalysts, more or less related to the seven pillars, are also emphasized, including reaction sensitivity to metal oxide structure, epitaxial contact between an active phase and a second phase or its support, synergy effect between several phases, acid-base aspects, electron transfer ability, catalyst preparation and activation and reaction atmospheres, etc. Some examples are presented to illustrate the importance of these key factors. They include light alkanes (C1–C4 oxidation, ethane oxidation to ethylene and acetic acid on MoVTe(SbNb-O and Nb doped NiO, propene oxidation to acrolein on BiMoCoFe-O systems, propane (ammoxidation to (acrylonitrile acrylic acid on MoVTe(SbNb-O mixed oxides, butane oxidation to maleic anhydride on VPO: (VO2P2O7-based catalyst, and isobutyric acid ODH to methacrylic acid on Fe hydroxyl phosphates. It is shown that active sites are composed of ensembles of atoms whose size and chemical composition depend on the reactants to be transformed (their chemical and size features and the reaction mechanism, often of Mars and van Krevelen type. An important aspect is the fact that surface composition and surface crystalline structure vary with reaction on stream until

  20. Bactericidal activity of partially oxidized nanodiamonds.

    Science.gov (United States)

    Wehling, Julia; Dringen, Ralf; Zare, Richard N; Maas, Michael; Rezwan, Kurosch

    2014-06-24

    Nanodiamonds are a class of carbon-based nanoparticles that are rapidly gaining attention, particularly for biomedical applications, i.e., as drug carriers, for bioimaging, or as implant coatings. Nanodiamonds have generally been considered biocompatible with a broad variety of eukaryotic cells. We show that, depending on their surface composition, nanodiamonds kill Gram-positive and -negative bacteria rapidly and efficiently. We investigated six different types of nanodiamonds exhibiting diverse oxygen-containing surface groups that were created using standard pretreatment methods for forming nanodiamond dispersions. Our experiments suggest that the antibacterial activity of nanodiamond is linked to the presence of partially oxidized and negatively charged surfaces, specifically those containing acid anhydride groups. Furthermore, proteins were found to control the bactericidal properties of nanodiamonds by covering these surface groups, which explains the previously reported biocompatibility of nanodiamonds. Our findings describe the discovery of an exciting property of partially oxidized nanodiamonds as a potent antibacterial agent.

  1. Investigation of influence of radioactive irradiation on the microstructure of oxide dispersion strengthened steels

    International Nuclear Information System (INIS)

    Vlasenko, S.V.; Benediktovich, A.I.; Ul'yanenkova, T.A.; O’Konnell, Zh.; Nitling, I.

    2015-01-01

    The microstructure of unirradiated and irradiated samples of oxide dispersion strengthened (ODS) steels was investigated by X-ray diffraction in order to determine the influence of radiation on mechanical properties of steels. The microstructural parameters of ODS steels from measured diffraction profiles were evaluated using an approach where the complex oxide nanoparticles (Y 2 Ti 2 O 7 and Y 4 Al 2 O 9 ) are modeled as spherical inclusions in the steel matrix with coherent boundaries. The proposed method enables processing of diffraction data from materials containing spherical inclusions by treating them as one more source of peak broadening in addition to straight dislocations, and taking into account broadening due to crystallite size and instrumental effects. The microstructural parameters were obtained on the basis of fitting of experimental data by theoretical curve. The parameters of crystallite size distribution modeled by a lognormal distribution function (the median m and the variance σ), the strain anisotropy parameter q, the dislocation density, the dislocation arrangement parameter M, the density of oxide nanoparticles and the nanoparticle radius r 0 were determined for the ODS steel samples. It was established that irradiation has no significant influence on microstructure. The results obtained for physical parameters are in good agreement with the results of high-resolution transmission electron microscopy (HRTEM). (authors)

  2. Microstructure Evolution and Mechanical Behavior of a CMnSiAl TRIP Steel Subjected to Partial Austenitization Along with Quenching and Partitioning Treatment

    Science.gov (United States)

    Kong, H.; Chao, Q.; Cai, M. H.; Pavlina, E. J.; Rolfe, B.; Hodgson, P. D.; Beladi, H.

    2018-02-01

    The present study investigated the microstructure evolution and mechanical behavior in a low carbon CMnSiAl transformation-induced plasticity (TRIP) steel, which was subjected to a partial austenitization at 1183 K (910 °C) followed by one-step quenching and partitioning (Q&P) treatment at different isothermal holding temperatures of [533 K to 593 K (260 °C to 320 °C)]. This thermal treatment led to the formation of a multi-phase microstructure consisting of ferrite, tempered martensite, bainitic ferrite, fresh martensite, and retained austenite, offering a superior work-hardening behavior compared with the dual-phase microstructure (i.e., ferrite and martensite) formed after partial austenitization followed by water quenching. The carbon enrichment in retained austenite was related to not only the carbon partitioning during the isothermal holding process, but also the carbon enrichment during the partial austenitization and rapid cooling processes, which has broadened our knowledge of carbon partitioning mechanism in conventional Q&P process.

  3. Comparison Study on the Microstructure of Nanocrystalline TiO2 in Different Ti-Si Binary Oxides

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    Three different Ti-Si oxide structuares, silica supported titania, silica coated titania and intimately mixed silicatitania, containing 10%-40% SiO2, were made by sol-gel process. The variations of microstructure parameters of nanocrystalline (nc) TiO2-anatase in the three kirds of binary oxides, including in-plane spacing d, cell constants (a0, CQ), cell volume V, cell axial ratio c0/a0 and crystal grain size, were comparatively investigated by high resolution transmission electron microscopy (HRTEM) and X-ray diffraction (XRD). It is found that the microstructure parameters vary remarkably with increasing SiO2 content and annealing temperature. Different structured Ti-Si binary oxides lead to different variation tendencies of microstructure parameters. The more SiO2 the binary oxide contains, the more lattice defects of nc TiO2-anatase appear; diffusion or migration of Si cations could be an important influential factor in the variations of microstructure. The grain size of nc TiO2 in the three kinds of binary oxides not only depends on SiO2 content and annealing temperature but also on the degree of lattice microstrain and distortion of nc TiO2-anatase. Both grain size and phase transformation of nc TiO2-anatase are effectively inhibited with increasing SiOa content.

  4. The study and microstructure analysis of zinc and zinc oxide

    Czech Academy of Sciences Publication Activity Database

    Luptáková, Natália; Pešlová, F.; Kliber, J.

    2015-01-01

    Roč. 54, č. 1 (2015), s. 43-46 ISSN 0543-5846 Grant - others:KEGA(SK) KEGA 007 TnUAD-4/2013 Institutional support: RVO:68081723 Keywords : zinc * production of zinc oxide * microstructure * chemical composition * zinc slag Subject RIV: JG - Metal lurgy Impact factor: 0.959, year: 2014

  5. Rheology and microstructure of dilute graphene oxide suspension

    International Nuclear Information System (INIS)

    Tesfai, Waka; Singh, Pawan; Shatilla, Youssef; Iqbal, Muhammad Z.; Abdala, Ahmed A.

    2013-01-01

    Graphene and graphene oxide are potential candidates as nanofluids for thermal management applications. Here, we investigate the rheological properties and intrinsic viscosity of aqueous suspension of graphene and use the measured intrinsic viscosity to determine the aspect ratio of graphene oxide. Dilute suspension of graphene oxide (0.05 to 0.5 mg/mL) exhibits a shear thinning behavior at low shear rates followed by a shear-independent region that starts at shear rate between 5 and 100/s depending on the concentration. This shear thinning behavior becomes more pronounced with the increase of particle loading. Moreover, AFM imaging of the dried graphene oxide indicates the evolution of irregular and thin low fractal aggregates of 0.3–1.8 nm thickness at lower concentrations to oblate compact structures of 1–18 nm thickness of nanosheets at higher concentration. These observations elucidate the microstructure growth mechanisms of graphene oxide in multiphase systems, which are important for nanofluids applications and for dispersing graphene and graphene oxide in composite materials. The suspension has a very high intrinsic viscosity of 1661 due to the high graphene oxide aspect ratio. Based on this intrinsic viscosity, we predict graphene oxide aspect ratio of 2445. While the classical Einstein and Batchelor models underestimate the relative viscosity of graphene oxide suspension, Krieger–Dougherty prediction is in a good agreement with the experimental measurement

  6. Microstructure and Mechanical Properties of Graphene Oxide/Copper Composites

    Directory of Open Access Journals (Sweden)

    HONG Qi-hu

    2016-09-01

    Full Text Available Graphene oxide/copper (GO/Cu composites were successfully synthesized through the ball milling and vacuum hot press sintering process. The morphologies of the mixture powders, and the microstructure and mechanical properties of GO/Cu composites were investigated by OM, SEM, XRD, hardness tester and electronic universal testing machine, respectively. The results show that the GO/Cu composites are compact. Graphene oxide with flake morphology is uniformly dispersed and well consolidated with copper matrix. When the mass fraction of graphene oxide is 0.5%, the microhardness and compress strength at RT reach up to 63HV and 276MPa, increased by 8.6% and 28%, respectively. The strengthening mechanism is load transfer effect, dislocation strengthening and fine crystal reinforcing.

  7. Processing/microstructure/mechanical-property relationships in FeAlZrB with and without an oxide dispersion

    International Nuclear Information System (INIS)

    Strothers, S.D.H.

    1991-01-01

    The effect of powder and processing variables on the microstructure of an extruded FeAlZrB alloy was investigated. Results shows that key parameters in microstructural development are extrusion temperature and powder particle size. In addition to powder and processing variables, the effect of a 1 vol% Y 2 O 3 dispersion was investigated. The microstructure of this material was very fine-grained. By manipulating powder and processing parameters and heat treatments, a very large range of microstructures were obtained. This enabled an evaluation of the role of microstructure and grain size on the room-temperature and elevated-temperature mechanical behavior of this alloy. At 1,100K the coarse-grained materials exhibited larger yield strengths in tension with the exception of the very-fine-grained oxide-dispersion-strengthened extrusions. These had the highest yields strengths despite their fine grain sizes. The oxide-dispersion-strengthened alloys also showed the greatest compression creep resistance at 1,100K even when heat treated to large grain sizes

  8. Partially oxidized atomic cobalt layers for carbon dioxide electroreduction to liquid fuel

    Science.gov (United States)

    Gao, Shan; Lin, Yue; Jiao, Xingchen; Sun, Yongfu; Luo, Qiquan; Zhang, Wenhua; Li, Dianqi; Yang, Jinlong; Xie, Yi

    2016-01-01

    Electroreduction of CO2 into useful fuels, especially if driven by renewable energy, represents a potentially ‘clean’ strategy for replacing fossil feedstocks and dealing with increasing CO2 emissions and their adverse effects on climate. The critical bottleneck lies in activating CO2 into the CO2•- radical anion or other intermediates that can be converted further, as the activation usually requires impractically high overpotentials. Recently, electrocatalysts based on oxide-derived metal nanostructures have been shown to enable CO2 reduction at low overpotentials. However, it remains unclear how the electrocatalytic activity of these metals is influenced by their native oxides, mainly because microstructural features such as interfaces and defects influence CO2 reduction activity yet are difficult to control. To evaluate the role of the two different catalytic sites, here we fabricate two kinds of four-atom-thick layers: pure cobalt metal, and co-existing domains of cobalt metal and cobalt oxide. Cobalt mainly produces formate (HCOO-) during CO2 electroreduction; we find that surface cobalt atoms of the atomically thin layers have higher intrinsic activity and selectivity towards formate production, at lower overpotentials, than do surface cobalt atoms on bulk samples. Partial oxidation of the atomic layers further increases their intrinsic activity, allowing us to realize stable current densities of about 10 milliamperes per square centimetre over 40 hours, with approximately 90 per cent formate selectivity at an overpotential of only 0.24 volts, which outperforms previously reported metal or metal oxide electrodes evaluated under comparable conditions. The correct morphology and oxidation state can thus transform a material from one considered nearly non-catalytic for the CO2 electroreduction reaction into an active catalyst. These findings point to new opportunities for manipulating and improving the CO2 electroreduction properties of metal systems

  9. Magnetic properties of partially oxidized Fe films

    Science.gov (United States)

    Garcia, Miguel Angel; Lopez-Dominguez, Victor; Hernando, Antonio

    Hybrid magnetic nanostructures exhibit appealing properties due to interface and proximity effects. A simple and interesting system of hybrid magnetic nanomaterials are partially oxidized ferromagnetic films. We have fabricated Fe films by thermal evaporation and performed a partial oxidation to magnetite (Fe3O4) by annealing in air at different times and temperatures. The magnetic properties of the films evolve from those of pure metallic iron to pure magnetite, showing intermediate states where the proximity effects control the magnetic behavior. At some stages, the magnetization curves obtained by SQUID and MOKE magnetometry exhibit important differences due to the dissimilar contribution of both phases to the magneto-optical response of the system This work has been supported by the Ministerio Español de Economia y Competitividad (MINECO) MAT2013-48009-C4-1. V.L.D and M.A.G. acknowledges financial support from BBVA foundation.

  10. The Effects of Oxidation Temperature on the Microstructure and Photocatalytic Activity of the TiO2 Coating

    Directory of Open Access Journals (Sweden)

    Xinxin TANG

    2017-08-01

    Full Text Available Titanium coatings were prepared on the surface of 1mm ZrO2 balls by mechanical ball mill, then the coatings were oxidized to photocatalytic TiO2 films at 400 ~ 600 °C. X-Ray Diffraction, Scanning Electron Microscope, Energy Dispersive Spectroscopy and Optical Microscope were used to analyze the microstructure and crystal form of the films. The photocatalytic activity of the samples was also evaluated. After that, the effects of oxidation temperature on the microstructure and photocatalytic activity of the films were discussed. The results show that the fabricated coatings are uneven, with average thickness of 60 μm. In the process of oxidation, oxygen is imported into the inner coatings by the gaps existed in the Ti coatings, which makes the Ti particles oxidize from surface to core, finally the films with TiO2 + Ti composite microstructure are obtained. The films oxidized at 500 °C have the best photocatalytic performance with the degradation rate of methyl orange solution 79.08 %, this owing to the existence of anatase and the TiO2+Ti composite microstructure. The result will provide theoretical basis for the fabrication of efficient photocatalytic film.DOI: http://dx.doi.org/10.5755/j01.ms.23.2.15590

  11. Microstructure, elastic and inelastic properties of partially graphitized biomorphic carbons

    Science.gov (United States)

    Orlova, T. S.; Kardashev, B. K.; Smirnov, B. I.; Gutierrez-Pardo, A.; Ramirez-Rico, J.; Martinez-Fernandez, J.

    2015-03-01

    The microstructural characteristics and amplitude dependences of the Young's modulus E and internal friction (logarithmic decrement δ) of biocarbon matrices prepared by beech wood carbonization at temperatures T carb = 850-1600°C in the presence of a nickel-containing catalyst have been studied. Using X-ray diffraction and electron microscopy, it has been shown that the use of a nickel catalyst during carbonization results in a partial graphitization of biocarbons at T carb ≥ 1000°C: the graphite phase is formed as 50- to 100-nm globules at T carb = 1000°C and as 0.5- to 3.0-μm globules at T carb = 1600°C. It has been found that the measured dependences E( T carb) and δ( T carb) contain three characteristic ranges of variations in the Young's modulus and logarithmic decrement with a change in the carbonization temperature: E increases and δ decreases in the ranges T carb 1300°C; in the range 1000 biocarbons carbonized in the presence of nickel correlates with the evolution of their microstructure. The largest values of E are obtained for samples with T carb = 1000 and 1600°C. However, the samples with T carb = 1600°C exhibit a higher susceptibility to microplasticity due to the presence of a globular graphite phase that is significantly larger in size and total volume.

  12. Addition of Fish Oil to Cream Cheese Affects Lipid Oxidation, Sensory Stability and Microstructure

    Directory of Open Access Journals (Sweden)

    Andy Horsewell

    2012-11-01

    Full Text Available The objective of this study was to investigate the differences in the oxidative stability during storage of fish oil enriched cream cheeses when fish oil was added either as neat oil or pre-emulsified oil with sodium caseinate, whey protein isolate, or a combination of milk proteins and phospholipids as emulsifier. Results showed that the addition of fish oil decreased the oxidative stability of cream cheeses regardless of the addition method, especially when the cheese was stored longer than five weeks. The oxidative stability of fish oil enriched cream cheeses was highest when fish oil was added as neat oil or in a delivery emulsion prepared with a combination of milk proteins and phospholipids. Adding the fish oil in a delivery emulsion prepared with whey protein or caseinate resulted in a less oxidative stable product. It was furthermore shown that the microstructure of the cream cheeses was affected by fish oil addition, and it was suggested that the change in microstructure was partly responsible for the oxidative stability of the cream cheeses.

  13. Three dimensional electrochemical simulation of solid oxide fuel cell cathode based on microstructure reconstructed by marching cubes method

    Science.gov (United States)

    He, An; Gong, Jiaming; Shikazono, Naoki

    2018-05-01

    In the present study, a model is introduced to correlate the electrochemical performance of solid oxide fuel cell (SOFC) with the 3D microstructure reconstructed by focused ion beam scanning electron microscopy (FIB-SEM) in which the solid surface is modeled by the marching cubes (MC) method. Lattice Boltzmann method (LBM) is used to solve the governing equations. In order to maintain the geometries reconstructed by the MC method, local effective diffusivities and conductivities computed based on the MC geometries are applied in each grid, and partial bounce-back scheme is applied according to the boundary predicted by the MC method. From the tortuosity factor and overpotential calculation results, it is concluded that the MC geometry drastically improves the computational accuracy by giving more precise topology information.

  14. Oxidation of C/SiC Composites at Reduced Oxygen Partial Pressures

    Science.gov (United States)

    Opila, Elizabeth J.; Serra, Jessica

    2009-01-01

    Carbon-fiber reinforced SiC (C/SiC) composites are proposed for leading edge applications of hypersonic vehicles due to the superior strength of carbon fibers at high temperatures (greater than 1500 C). However, the vulnerability of the carbon fibers in C/SiC to oxidation over a wide range of temperatures remains a problem. Previous oxidation studies of C/SiC have mainly been conducted in air or oxygen, so that the oxidation behavior of C/SiC at reduced oxygen partial pressures of the hypersonic flight regime are less well understood. In this study, both carbon fibers and C/SiC composites were oxidized over a wide range of temperatures and oxygen partial pressures to facilitate the understanding and modeling of C/SiC oxidation kinetics for hypersonic flight conditions.

  15. Hydrogen generator, via catalytic partial oxidation of methane for fuel cells

    Science.gov (United States)

    Recupero, Vincenzo; Pino, Lidia; Di Leonardo, Raffaele; Lagana', Massimo; Maggio, Gaetano

    It is well known that the most acknowledged process for generation of hydrogen for fuel cells is based upon the steam reforming of methane or natural gas. A valid alternative could be a process based on partial oxidation of methane, since the process is mildly exothermic and therefore not energy intensive. Consequently, great interest is expected from conversion of methane into syngas, if an autothermal, low energy intensive, compact and reliable process could be developed. This paper covers the activities, performed by the CNR Institute of Transformation and Storage of Energy (CNR-TAE), on theoretical and experimental studies for a compact hydrogen generator, via catalytic selective partial oxidation of methane, integrated with second generation fuel cells (EC-JOU2 contract). In particular, the project focuses the attention on methane partial oxidation via heterogeneous selective catalysts, in order to: demonstrate the basic catalytic selective partial oxidation of methane (CSPOM) technology in a subscale prototype, equivalent to a nominal output of 5 kWe; develop the CSPOM technology for its application in electric energy production by means of fuel cells; assess, by a balance of plant analysis, and a techno-economic evaluation, the potential benefits of the CSPOM for different categories of fuel cells.

  16. Transmission electron microscopy of oxide dispersion strengthened (ODS) molybdenum: effects of irradiation on material microstructure

    International Nuclear Information System (INIS)

    Baranwal, R.; Burke, M.G.

    2003-01-01

    Oxide dispersion strengthened (ODS) molybdenum has been characterized using transmission electron microscopy (TEM) to determine the effects of irradiation on material microstructure. This work describes the results-to-date from TEM characterization of unirradiated and irradiated ODS molybdenum. The general microstructure of the unirradiated material consists of fine molybdenum grains (< 5 (micro)m average grain size) with numerous low angle boundaries and isolated dislocation networks. 'Ribbon'-like lanthanum oxides are aligned along the working direction of the product form and are frequently associated with grain boundaries, serving to inhibit grain boundary and dislocation movement. In addition to the 'ribbons', discrete lanthanum oxide particles have also been detected. After irradiation, the material is characterized by the presence of nonuniformly distributed large (∼ 20 to 100 nm in diameter), multi-faceted voids, while the molybdenum grain size and oxide morphology appear to be unaffected by irradiation

  17. Some microstructural characterisations in a friction stir welded oxide dispersion strengthened ferritic steel alloy

    International Nuclear Information System (INIS)

    Legendre, F.; Poissonnet, S.; Bonnaillie, P.; Boulanger, L.; Forest, L.

    2009-01-01

    The goal of this study is to characterize microstructure of a friction stir welded oxide dispersion strengthened alloy. The welded material is constituted by two sheets of an yttria-dispersion-strengthened PM 2000 ferritic steel. Different areas of the friction stir welded product were analyzed using field emission gun secondary electron microscopy (FEG-SEM) and electron microprobe whereas nanoindentation was used to evaluate mechanical properties. The observed microstructural evolution, including distribution of the yttria dispersoids, after friction stir welding process is discussed and a correlation between the microstructure and the results of nanoindentation tests is established.

  18. Microstructure/Oxidation/Microhardness Correlations in Gamma-Based and Tau-Based Al-Ti-Cr Alloys

    Science.gov (United States)

    Brady, Michael P.; Smialek, J. L.; Humphrey, D. L.

    1994-01-01

    The relationships between alloy microstructure and air oxidation kinetics and alloy microstructure and microhardness in the Al-Ti-Cr system for exposures at 800 C and 1000 C were investigated. The relevant phases were identified as tau (Ll2), gamma (LIO), r-Al2Ti, TiCrAl (laves), and Cr2AI. Protective alumina formation was associated with tau, Al-rich TiCrAl, and gamma/TiCrAl mixtures. Brittleness was associated with the TiCrAl phase and tau decomposition to A12Ti + Cr2AI. It was concluded that two-phase gamma + TiCrAl alloys offer the greatest potential for oxidation resistance and room temperature ductility in the Al-Ti-Cr system.

  19. Experimental and simulation analysis of hydrogen production by partial oxidation of methanol

    Energy Technology Data Exchange (ETDEWEB)

    Sikander, U. [National Univ. of Science and Technology, Islamabad (Pakistan)

    2014-10-15

    Partial oxidation of methanol is the only self-sustaining process for onboard production of hydrogen. For this a fixed bed catalytic reactor is designed, based on heterogeneous catalytic reaction. To develop an optimized process, simulation is carried out using ASPEN HYSYS v 7.1. Reaction kinetics is developed on the basis of Langmuir Hinshel wood model. 45:55:5 of CuO: ZnO: Al/sub 2/O/sub 3/ is used as a catalyst. Simulation results are studied in detail to understand the phenomenon of partial oxidation of methanol inside the reactor. An experimental rig is developed for hydrogen production through partial oxidation of methanol. Results obtained from process simulation and experimental work; are compared with each other. (author)

  20. Effect of oxygen partial pressure on oxidation of Mo-metal

    Science.gov (United States)

    Sharma, Rabindar Kumar; Kumar, Prabhat; Singh, Megha; Gopal, Pawar; Reddy, G. B.

    2018-05-01

    This report explains the effect of oxygen partial pressure (PO2 ) on oxidation of Mo-metal in oxygen plasma. XRD results indulge that oxide layers formed on Mo-surfaces at different oxygen partial pressures have two different oxide phases (i.e. orthorhombic MoO3 and monoclinic Mo8O23). Intense XRD peaks at high pressure (i.e. 2.0×10-1 Torr) points out the formation of thick oxide layer on Mo-surface due to presence of large oxygen species in chamber and less oxide volatilization. Whereas, at low PO2 (6.5×10-2 and 7.5×10-2 Torr.) the reduced peak strength is owing to high oxide volatilization rate. SEM micrographs and thickness measurements also support XRD results and confirm that the optimum -2value of PO2 to deposited thicker and uniform oxide film on glass substrate is 7.5×10-2 Torr through plasma assistedoxidation process. Further to study the compositional properties, EDX of the sample M2 (the best sample) is carried out, which confirms that the stoichiometric ratio is less than 3 (i.e. 2.88). Less stoichiometric ratio again confirms the presence of sub oxides in oxide layers on Mo metal as evidenced by XRD results. All the observed results are well in consonance with each other.

  1. EXAFS and XRD studies of nanocrystalline cerium oxide: the effect of preparation method on the microstructure

    International Nuclear Information System (INIS)

    Savin, S.L.P.; Chadwick, A.V.; Smith, M.E.; O'Dell, L.A.

    2007-01-01

    There is considerable interest in nanocrystalline materials due to their unusual properties, such as enhanced ionic conductivity in the case of nanocrystalline ionic solids. This has potential commercial applications, particularly for oxide ion conductors. However, a detailed knowledge of the microstructure is important in fully understanding the novel properties exhibited by nanocrystalline materials. The final microstructure of a material is dependent on the preparation method used, for example, sol-gel and ball-milling methods are commonly used in the preparation of nanocrystalline oxides. Additionally, there is a problem in maintaining the materials in nanocrystalline form when they are subjected to elevated temperatures. We have been exploring strategies to restrict the growth of nanocrystalline oxides and have found that adding a small amount of an inert material, e.g. SiO 2 or Al 2 O 3 , is particularly effective. We will report XRD and EXAFS studies of nanocrystalline ceria prepared by sol-gel, sol-gel pinned and ball-milling methods and the effect of preparation method on the final microstructure. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  2. Catalytic Partial Oxidation of Biomass/Oil Mixture

    Czech Academy of Sciences Publication Activity Database

    Veselý, Václav; Hanika, Jiří; Tukač, V.; Lederer, J.; Kovač, D.

    2013-01-01

    Roč. 7, č. 10 (2013), s. 1940-1945 ISSN 1934-8983 R&D Projects: GA TA ČR TE01020080; GA MPO 2A-2TP1/024 Institutional support: RVO:67985858 Keywords : hydrocarbon oil * biomass * catalytic partial oxidation Subject RIV: CI - Industrial Chemistry, Chemical Engineering http://www.davidpublishing.com/journals_info.asp?jId=1718#

  3. Corrosion characteristics and oxide microstructures of Zircaloy-4 in aqueous alkali hydroxide solutions

    International Nuclear Information System (INIS)

    Jeong, Y.H.; Baek, J.H.; Kim, S.J.; Kim, H.G.

    1999-01-01

    The corrosion characteristics of Zircaloy-4 have been investigated in various aqueous solutions of LiOH, NaOH, KOH, RbOH and CsOH with equimolar M + and OH - at 350 C. The characterization of the oxides was performed using transmission electron microscope (TEM) and scanning electron microscope (SEM) on the samples which were prepared to have an equal oxide thickness in pre-transition and post-transition regimes. At a low concentration (4.3 mmol) of aqueous alkali hydroxide solutions, the corrosion rates decrease gradually as the ionic radius of cation increases. At a high concentration (32.5 mmol), the corrosion rate increases significantly in LiOH solution and slightly in NaOH solution, but in the other hydroxide solutions such as KOH, RbOH and CsOH, the corrosion rate is not accelerated. Even if the specimens have an equal oxide thickness in LiOH, NaOH and KOH solutions, the oxide microstructure formed in the LiOH solution is quite different from those formed in the NaOH or the KOH solutions. In the LiOH solution, the oxides grown in the pre-transition regime as well as in the post-transition regime have an equiaxed structure including many pores and open grain boundaries. The oxides grown in the NaOH solution have a protective columnar structure in the pre-transition regime but an equiaxed structure in the post-transition regime. On the other hand, in the KOH solution, the columnar structure is maintained from its pre-transition regime to the post-transition regime. On the basis of the above results, it can be suggested that the cation incorporation into zirconium oxide would control the oxide microstructure, the oxide growth mechanism at the metal-oxide interface and the corrosion rate in alkali hydroxide solutions. (orig.)

  4. Microstructure and optical appearance of anodized friction stir processed Al - Metal oxide surface composites

    DEFF Research Database (Denmark)

    Gudla, Visweswara Chakravarthy; Jensen, Flemming; Bordo, Kirill

    2014-01-01

    Multiple-pass friction stir processing (FSP) was employed to impregnate Ti, Y and Ce oxide powders into the surface of an Aluminium alloy. The FSP processed surface composite was subsequently anodized with an aim to develop optical effects in the anodized layer owing to the presence of incorporated...... oxide particles which will influence the scattering of light. This paper presents the investigations on relation between microstructure of the FSP zone and optical appearance of the anodized layer due to incorporation of metal oxide particles and modification of the oxide particles due to the anodizing...

  5. Gas phase deposition of oxide and metal-oxide coatings on fuel particles

    International Nuclear Information System (INIS)

    Patokin, A.P.; Khrebtov, V.L.; Shirokov, B.M.

    2008-01-01

    Production processes and properties of oxide (Al 2 O 3 , ZrO 2 ) and metal-oxide (Mo-Al 2 O 3 , Mo-ZrO 2 , W-Al 2 O 3 , W-ZrO 2 ) coatings on molybdenum substrates and uranium dioxide fuel particles were investigated. It is shown that the main factors that have an effect on the deposition rate, density, microstructure and other properties of coatings are the deposition temperature, the ratio of H 2 and CO 2 flow rates, the total reactor pressure and the ratio of partial pressures of corresponding metal chlorides during formation of metal-oxide coatings

  6. Advances in the Partial Oxidation of Methane to Synthesis Gas

    Institute of Scientific and Technical Information of China (English)

    Quanli Zhu; Xutao Zhao; Youquan Deng

    2004-01-01

    The conversion and utilization of natural gas is of significant meaning to the national economy,even to the everyday life of people. However, it has not become a popular industrial process as expected due to the technical obstacles. In the past decades, much investigation into the conversion of methane,predominant component of natural gas, has been carried out. Among the possible routes of methane conversion, the partial oxidation of methane to synthesis gas is considered as an effective and economically feasible one. In this article, a brief review of recent studies on the mechanism of the partial oxidation of methane to synthesis gas together with catalyst development is wherein presented.

  7. Partial oxidation of methane in a temperature-controlled dielectric barrier discharge reactor

    KAUST Repository

    Zhang, Xuming

    2015-01-01

    We studied the relative importance of the reduced field intensity and the background reaction temperature in the partial oxidation of methane in a temperature-controlled dielectric barrier discharge reactor. We obtained important mechanistic insight from studying high-temperature and low-pressure conditions with similar reduced field intensities. In the tested range of background temperatures (297 < T < 773 K), we found that the conversion of methane and oxygen depended on both the electron-induced chemistry and the thermo-chemistry, whereas the chemical pathways to the products were overall controlled by the thermo-chemistry at a given temperature. We also found that the thermo-chemistry enhanced the plasma-assisted partial oxidation process. Our findings expand our understanding of the plasma-assisted partial oxidation process and may be helpful in the design of cost-effective plasma reformers. © 2014 The Combustion Institute.

  8. Generation of synthesis gas by partial oxidation of natural gas in a gas turbine

    NARCIS (Netherlands)

    Cornelissen, R.; Tober, E.; Kok, Jacobus B.W.; van der Meer, Theodorus H.

    2006-01-01

    The application of partial oxidation in a gas turbine (PO-GT) in the production of synthesis gas for methanol production is explored. In PO-GT, methane is compressed, preheated, partial oxidized and expanded. For the methanol synthesis a 12% gain in thermal efficiency has been calculated for the

  9. Effect of LiOH, NaOH and KOH on corrosion and oxide microstructure of Zr-based alloys

    International Nuclear Information System (INIS)

    Jeong, Y.H.; Kim, H.G.; Jung, Y.H.; Ruhmann, H.

    1999-01-01

    Long-term corrosion test, SIMS analysis, and TEM microstructural study were carried out to investigate the corrosion characteristics and mechanism of Zr alloys in alkali hydroxides. The corrosion tests were performed in solutions of LiOH, NaOH, KOH, RbOH, and CsOH at 350 deg. C for 500 days. SIMS analysis was performed for the specimens prepared to have an equal oxide thickness. TEM studies on the specimens with an equal oxide thickness in various solutions in both pre- and post-transition regimes were also conducted. The corrosion rate in alkali hydroxide solutions was observed to decrease as the ionic radius of alkali cation was increased. The penetration depth of cation into the oxide decreases with increasing the ionic radius of cation. Even though the oxide thickness was equal, the different oxide morphologies were observed in specimens. Namely, in LiOH solution the oxide morphology was transformed early from columnar to equiaxed structure. However, in KOH solution the columnar structure was maintained up to post-transition regime. Based on the corrosion test, SIMS analysis, and microstructural study, the cation is considered to control the corrosion in a alkali hydroxide solution and its effect is dependent on the concentration of alkali and the oxide thickness. The slight acceleration of the corrosion rate at a low concentration is thought to be caused by cation incorporation into oxide while the significant acceleration at a high concentration is due to the transformation of oxide microstructure that would be induced by cation incorporation. KOH was shown not to affect significantly the corrosion and the hydrogen pickup of Zircaloy. Therefore, it has a potential for PWR application only from the point of view of Zircaloy corrosion. (author)

  10. The influence of the oxygen partial pressure on the quasi-ternary system Cr-Mn-Ti-oxide

    International Nuclear Information System (INIS)

    Garcia-Rosales, C.; Schulze, H.A.; Naoumidis, A.; Nickel, H.

    1991-05-01

    The passivation layers formed by the oxidizing corrosion of high temperature alloys consist primarily of oxides and mixed oxides of the elements chromium, manganese and titanium. For a reproducible formation and characterization of such oxide layers it is necessary to know the phase equilibria of these oxide systems at temperature and oxygen partial pressure conditions which will be relevant during their application. For the investigation of the quasi-ternary system Cr-Mn-Ti-oxide, oxide powders were prepared and annealed at 1000deg C under different oxygen partial pressures ranging from 0.21 bar to 10 -21 bar. Phase identification and determination of lattice parameter using X-ray diffraction analysis as well as the direct measurement of phase boundaries as a function of oxygen partial pressure using the emf-methode were carried out for these investigations. In the quasi-ternary system Cr-Mn-Ti-oxide the spinels play a decisive role in the oxigen partial pressure range examined. The spinel MnCr 2 O 4 may be regarded as the most significant compound. Part of the chronium can be replaced by trivalent manganese at high oxygen partial pressures and by trivalent titanium at low pressures, and the formation of a solid solution with the spinel Mn 2 TiO 4 is possible in all cases. In this way a coherent single-phase spinel region is observed which extends over the entire oxygen partial pressure range form 0.21 bar to 10 -21 bar examined at 1000deg C. (orig.) [de

  11. Microstructure, mechanical properties and oxidation behaviors of magnetron sputtered NbN_x coatings

    International Nuclear Information System (INIS)

    Qi, Zhengbing; Wu, Zhengtao; Zhang, Dongfang; Zuo, Juan; Wang, Zhoucheng

    2016-01-01

    Mechanical properties and oxidation resistance are of importance for the NbN_x coatings as used in cutting and forming tools. In this study, the NbN_x coatings were deposited by magnetron sputtering at nitrogen partial pressure ranging from 0 to 40%. The chemical and phase compositions, morphologies, mechanical properties and oxidation behaviors of the NbN_x coatings were investigated by electron probe microanalysis, X-ray photoelectron spectroscopy, grazing incidence X-ray diffraction, scanning and transmission electron microscopy, and nanoindentation measurements. The results reveal the composition evolution of the NbN_x coatings as α-Nb (0%), β-Nb_2N (5%), a mixture of β-Nb_2N and δ-NbN (10%), and δ-NbN (20–40%). The single phase coatings exhibit columnar structure while the mixed phases coating shows nano-composite structure. Compared with the single phase δ-NbN coatings (21.6 ± 0.8–28.0 ± 1.2 GPa), higher hardness of the single phase β-Nb_2N coating (30.9 ± 1.0 GPa) is due to the higher covalent character and much finer grains. The maximum hardness reaches 33.3 ± 1.5 GPa for the nano-composite coating with mixed phases of β-Nb_2N and δ-NbN. The oxidation results demonstrate that the activation energies are 219.3 and 192.3 kJ/mol for the Nb_2N and NbN coatings respectively. Non-protective Nb_2O_5 scales with cracks and pores result in poorer oxidation resistance of the NbN coating in comparison to the Nb_2N coating. - Highlights: • Chemical and phase compositions and microstructure of NbN_x coatings were investigated. • Maximum hardness is obtained for nano-composite coating with mixed Nb_2N and NbN phases. • Activation energies are 219.3 and 192.3 kJ/mol for oxidation of Nb_2N and NbN coatings. • Non-protective Nb_2O_5 scales with cracks and pores lower oxidation resistance of NbN coating.

  12. One-Pot Synthesis of Cu(II Complex with Partially Oxidized TTF Moieties

    Directory of Open Access Journals (Sweden)

    Hiroki Oshio

    2012-07-01

    Full Text Available The one-pot synthesis of a Cu(II complex with partially oxidized tetrathiafulvalene (TTF moieties in its capping MT-Hsae-TTF ligands, [CuII(MT-sae-TTF2] [CuICl2] was realized by the simultaneous occurrence of Cu(II complexation and CuIICl2 mediated oxidation of TTF moieties. The crystal structure was composed of one-dimensional columns formed by partially oxidized TTF moieties and thus the cation radical salt showed relatively high electrical conductivity. Tight binding band structure calculations indicated the existence of a Peierls gap due to the tetramerization of the TTF moieties in the one-dimensional stacking column at room temperature, which is consistent with the semiconducting behavior of this salt.

  13. Kinetic studies of isooctane partial oxidation over a nickel-based catalyst

    International Nuclear Information System (INIS)

    Ibrahim, Hussameldin; Idem, Raphael; Aboudheir, Ahmed

    2006-01-01

    The production of hydrogen (H 2 ) for fuel cell applications in mobile vehicles by reforming technologies such as partial oxidation of various fossil fuels has gained much attention recently. In this study, the production of H 2 by the catalytic partial oxidation of isooctane ((C 8 H 18 ) used here as a surrogate for gasoline) was investigated over alumina (AI 2 O 3 )supported nickel (Ni) catalyst. The work investigated the kinetics of the partial oxidation of isooctane over a stable Ni/□-AI 2 O 3 catalyst in the range of 863 to 913 K, at atmospheric pressure, W/F i c8 in the range of 1.97 to 8.58 g h mol - 1, and molar feed ratio in the range of 2.0 to 8.0 experiments to obtain kinetic data were performed in a 12.7 mm diameter Inconel micro-reactor housed in an electrically controlled furnace. The chemical reaction was then modeled using rate models developed from the Langmuir-Hinshelwood-hougen-Watson (LHHW) and Eley-Rideal (ER) formulations. The model parameters were estimated using an adaptive Gauss-Newton and Marquardi-Levenberg minimization algorithm. Rival models were screened for their thermodynamic consistency and physicochemical significance of estimated parameters. Langmuir-Hinshelwood-hougen-Watson mechanism requiring the dissociative adsorption of isooctane and oxygen on two different sites appeared to be the most likely pathway for the partial oxidation reaction of isooctane. Reaction order with respect to isooctane indicates the strong coverage of nickel by isooctane. The activation energy of 73±3.1 kJ mol - 1 estimated from the LHHW model is consistent with the trend observed with lower hydrocarbons.(Author)

  14. Partial-Isothermally-Treated Low Alloy Ultrahigh Strength Steel with Martensitic/Bainitic Microstructure

    Science.gov (United States)

    Luo, Quanshun; Kitchen, Matthew; Patel, Vinay; Filleul, Martin; Owens, Dave

    We introduce a new strengthening heat treatment of a Ni-Cr-Mo-V alloyed spring steel by partial isothermal salt-bath and subsequent air-cooling and tempering. Detailed isothermal treatments were made at temperatures below or above the Ms point (230°C). The salt bath time was controlled between 10 and 80 minutes. Through the new treatment, the candidate steel developed ultrahigh tensile strength 2,100 MPa, yield strength 1,800 MPa, elongation 8-10 %, hardness 580-710 HV, and V-notch Charpy toughness 10-12 J. Optical and electron microscopic observations and X-ray diffraction revealed multi-phase microstructures of bainitic/martensitic ferrites, fine carbide precipitates and retained austenite. Carbon partitioning during the bainitic/martensitic transformation was investigated for its remarkable influence on the strengthening mechanism.

  15. Dynamic mechanical properties of hydroxyapatite/polyethylene oxide nanocomposites: characterizing isotropic and post-processing microstructures

    Science.gov (United States)

    Shofner, Meisha; Lee, Ji Hoon

    2012-02-01

    Compatible component interfaces in polymer nanocomposites can be used to facilitate a dispersed morphology and improved physical properties as has been shown extensively in experimental results concerning amorphous matrix nanocomposites. In this research, a block copolymer compatibilized interface is employed in a semi-crystalline matrix to prevent large scale nanoparticle clustering and enable microstructure construction with post-processing drawing. The specific materials used are hydroxyapatite nanoparticles coated with a polyethylene oxide-b-polymethacrylic acid block copolymer and a polyethylene oxide matrix. Two particle shapes are used: spherical and needle-shaped. Characterization of the dynamic mechanical properties indicated that the two nanoparticle systems provided similar levels of reinforcement to the matrix. For the needle-shaped nanoparticles, the post-processing step increased matrix crystallinity and changed the thermomechanical reinforcement trends. These results will be used to further refine the post-processing parameters to achieve a nanocomposite microstructure with triangulated arrays of nanoparticles.

  16. Effect of Calcium Oxide Microstructure on the Diffusion of Isotopes

    CERN Document Server

    Fernandes Ramos, João Pedro; Stora, T

    2012-01-01

    Calcium oxide (CaO) powder targets have been successfully used at CERN-ISOLDE to produce neutron deficient exotic argon and carbon isotopes under proton irradiation at high temperatures (>1000°C). These targets outperform the other related targets for the production of the same beams. However, they presented either slow release rates (yields) from the beginning or a rapid decrease over time. This problem was believed to come from the target microstructure degradation, justifying the material investigation. In order to do so, the synthesis, reactivity in ambient air and sintering kinetics of CaO were studied, through surface area determination by N2 adsorption, X-ray diffraction for crystalline phase identification and crystallite size determination, and scanning and transmission electron microscopy to investigate the microstructure. The synthesis studies revealed that a nanometric material is obtained from the decarbonation of CaCO3 in vacuum at temperatures higher than 550°C, which is very reactive in air....

  17. Microstructure evolution of the oxide dispersion strengthened CLAM steel during mechanical alloying process

    Energy Technology Data Exchange (ETDEWEB)

    Song, Liangliang [Key Laboratory of Neutronics and Radiation Safety, Institute of Nuclear Energy Safety Technology, Chinese Academy of Science, Hefei, Anhui, 230031 (China); University of Science and Technology of China, Hefei, Anhui, 230031 (China); Liu, Shaojun, E-mail: shaojun.liu@fds.org.cn [Key Laboratory of Neutronics and Radiation Safety, Institute of Nuclear Energy Safety Technology, Chinese Academy of Science, Hefei, Anhui, 230031 (China); Mao, Xiaodong [Key Laboratory of Neutronics and Radiation Safety, Institute of Nuclear Energy Safety Technology, Chinese Academy of Science, Hefei, Anhui, 230031 (China)

    2016-11-15

    Highlights: • A nano-sized oxides dispersed ODS-CLAM steel was obtained by MA and HIP. • A minimum saturated grain size of down to 30 nm was achieved by varying the milling time from 0 to 100 h. • Solution of W in the MA powder could be significantly improved by increasing MA rotation speed. - Abstracts: Oxide dispersion strengthened Ferritic/Martensitic steel is considered as one of the most potential structural material for future fusion reactor, owing to its high mechanical properties and good irradiation resistance. The oxide dispersion strengthened China Low Activation Martensitic (ODS-CLAM) steel was fabricated by mechanical alloying (MA) and hot isostatic pressing (HIP). The microstructural evolutions during the process of ball milling and subsequent consolidation were investigated by SEM, XRD and TEM. The results showed that increasing the milling time during the first 36 h milling could effectively decrease the grain size to a value of around 30 nm, over which grain sized remained nearly constant. Increasing the rotation speed promoted the solution of tungsten (W) element obviously and decreased the grain size to a certain degree. Observation on the consolidated and further heat-treated ODS-CLAM steel samples indicated that a martensite microstructure with a high density of nano-particles was achieved.

  18. Oxidative stress and partial migration in brown trout (Salmo trutta)

    DEFF Research Database (Denmark)

    Birnie-Gauvin, Kim; Peiman, K. S.; Larsen, Martin Hage

    2017-01-01

    of oxidative status in migration biology, particularly in fish. Semi-anadromous brown trout (Salmo trutta, Linnaeus 1758) exhibit partial migration, where some individuals smoltify and migrate to sea, and others become stream residents, providing us with an excellent model to investigate the link between...... oxidative stress and migration. Using the brown trout, we obtained blood samples from juveniles from a coastal stream in Denmark in the fall prior to peak seaward migration which occurs in the spring, and assayed for antioxidant capacity (oxygen radical absorbance capacity) and oxidative stress levels...

  19. Microstructural evolution and growth kinetics of thermally grown oxides in plasma sprayed thermal barrier coatings

    Directory of Open Access Journals (Sweden)

    Xiaoju Liu

    2016-02-01

    Full Text Available The formation of thermally grown oxide (TGO during high temperature is a key factor to the degradation of thermal barrier coatings (TBCs applied on hot section components. In the present study both the CoNiCrAlY bond coat and ZrO2-8 wt.% Y2O3 (8YSZ ceramic coat of TBCs were prepared by air plasma spraying (APS. The composition and microstructure of TGO in TBCs were investigated using scanning electron microscopy (SEM, energy dispersive spectroscopy (EDS and X-ray diffraction (XRD analysis. The growth rate of TGO for TBC and pure BC were gained after isothermal oxidation at 1100 °C for various times. The results showed that as-sprayed bond coat consisted of β and γ/γ′phases, β phase reducesd as the oxidation time increased. The TGO comprised α-Al2O3 formed in the first 2 h. CoO, NiO, Cr2O3 and spinel oxides appeared after 20 h of oxidation. Contents of CoO and NiO reduced while that of Cr2O3 and spinel oxides increased in the later oxidation stage. The TGO eventually consisted of a sub-Al2O3 layer with columnar microstructure and the upper porous CS clusters. The TGO growth kinetics for two kinds of samples followed parabolic laws, with oxidation rate constant of 0.344 μm/h0.5 for TBCs and 0.354 μm/h0.5 for pure BCs.

  20. Hydrogen or Soot?: Partial Oxidation of High-boiling Hydrocarbon Wastes

    Czech Academy of Sciences Publication Activity Database

    Lederer, J.; Hanika, Jiří; Nečesaný, F.; Poslední, W.; Tukač, V.; Veselý, Václav

    2015-01-01

    Roč. 29, č. 1 (2015), s. 5-11 ISSN 0352-9568 Institutional support: RVO:67985858 Keywords : partial oxidation * waste * hydrocarbon Subject RIV: CI - Industrial Chemistry, Chemical Engineering Impact factor: 0.675, year: 2015

  1. A microstructural study of the degradation and calcium release from hydroxyapatite-calcium oxide ceramics made by infiltration.

    Science.gov (United States)

    Zhang, Qinghao; Schmelzer, Eva; Gerlach, Jörg C; Nettleship, Ian

    2017-04-01

    Hydroxyapatite pellets, partially densified in a low-temperature heat treatment, were infiltrated with calcium nitrate solution followed by in-situ precipitation of Ca(OH) 2 and CaCO 3 . The infiltrated bodies were then densified to high relative density and the calcium carbonate transformed to calcium oxide during sintering and resulted in biphasic hydroxyapatite-CaO ceramics. This work investigated the influence of the infiltration on surface morphology, weight change, and microstructural-level degradation caused by exposure to saline at pH=7.4 and a temperature of 20°C. The CaO rendered the materials more susceptible to degradation, and released calcium into the saline faster than single phase, calcium deficient hydroxyapatite (HA) that were used as a control. In consequence, these ceramics could be used to release calcium into the culture microenvironments of bone tissue or bone marrow cells next to a scaffold surface. Copyright © 2016 Elsevier B.V. All rights reserved.

  2. Effect of oxygen partial pressure on the microstructural, optical and gas sensing characterization of nanostructured Gd doped ceria thin films deposited by pulsed laser deposition

    Directory of Open Access Journals (Sweden)

    Nagaraju P.

    2017-12-01

    Full Text Available Microstructural properties of 10 mol% gadolinium doped ceria (CeO2 thin films that were deposited on quartz substrate at substrate temperature of 1023 K by using pulsed laser deposition with different oxygen partial pressures in the range of 50–200 mTorr. The influence of oxygen partial pressure on microstructural, morphological, optical and gas sensing characterization of the thin films was systematically studied. The microstructure of the thin films was investigated using X-ray diffraction, atomic force microscopy and Raman spectroscopy. Morphological studies have been carried out using scanning electron microscope. The experimental results confirmed that the films were polycrystalline in nature with cubic fluorite structure. Optical properties of the thin films were examined using UV–vis spectrophotometer. The optical band gap calculated from Tauc’s relation. Gas sensing characterization has been carried at different operating temperatures (room temperature to 523 K for acetone gas. Response and recovery times of the sensor were calculated using transient response plot.

  3. Microstructure and elevated-temperature erosion-oxidation behaviour of aluminized 9Cr-1Mo Steel

    OpenAIRE

    Huttunen, E.; Honkanen, M.; Tsipas, Sophia Alexandra; Omar, H.; Tsipas, D.

    2012-01-01

    Degradation of materials by a combination of erosive wear and atmospheric oxidation at elevated temperatures constitutes a problem in some power generation processes, such as fluidized-bed combustion. In this work, 9Cr-1Mo steel, a common tube material in combustion chambers, is coated by a pack cementation method from an Al-containing pack in order to improve the resistance to erosion-oxidation at elevated temperatures. The resulting coating is studied in terms of microstructure and microhar...

  4. Effect of substrate temperature and oxygen partial pressure on RF sputtered NiO thin films

    Science.gov (United States)

    Cheemadan, Saheer; Santhosh Kumar, M. C.

    2018-04-01

    Nickel oxide (NiO) thin films were deposited by RF sputtering process and the physical properties were investigated for varying substrate temperatures and oxygen partial pressure. The variation of the crystallographic orientation and microstructure of the NiO thin films with an increase in substrate temperature were studied. It was observed that NiO thin films deposited at 350 °C shows relatively good crystalline characteristics with a preferential orientation along (111) plane. With the optimum substrate temperature of 350 °C, the NiO thin films were deposited under various oxygen partial pressures at the same experimental conditions. The structural, optical and electrical properties of NiO thin films under varying oxygen partial pressure of 10%–50% were investigated. From XRD it is clear that the films prepared in the pure argon atmosphere were amorphous while the films in oxygen partial pressure exhibited polycrystalline NiO phase. SEM and AFM investigations unveil that the higher substrate temperature improves the microstructure of the thin films. It is revealed that the NiO thin films deposited at oxygen partial pressure of 40% and a substrate temperature of 350 °C, showed higher electrical conductivity with p-type characteristics.

  5. Microstructural evolution of nanograin nickel-zirconia cermet anode materials for solid oxide fuel cell applications

    International Nuclear Information System (INIS)

    Nayak, Bibhuti Bhusan

    2012-01-01

    The aim of the study is to study the structure, microstructure, porosity, thermal expansion, electrical conductivity and electrochemical behavior of the anode material thus synthesized in order to find its suitability for solid oxide fuel cell (SOFC) anode application

  6. Study of film graphene/graphene oxide obtained by partial reduction chemical of oxide graphite

    International Nuclear Information System (INIS)

    Gascho, J.L.S.; Costa, S.F.; Hoepfner, J.C.; Pezzin, S.H.

    2014-01-01

    This study investigated the morphology of graphene/graphene oxide film obtained by partial chemical reduction of graphite oxide (OG) as well as its resistance to solvents. Films of graphene/graphene oxide are great candidates for replacement of indium oxide doped with tin (ITO) in photoelectric devices. The OG was obtained from natural graphite, by Hummer's method modified, and its reduction is made by using sodium borohydride. Infrared spectroscopy analysis of Fourier transform (FTIR), Xray diffraction (XRD) and scanning electron microscopy, high-resolution (SEM/FEG) for the characterization of graphene/graphene oxide film obtained were performed. This film proved to be resilient, not dispersing in any of the various tested solvents (such as ethanol, acetone and THF), even under tip sonication, this resistance being an important property for the applications. Furthermore, the film had a morphology similar to that obtained by other preparation methods.(author)

  7. Palm H-FAME Production through Partially Hydrogenation using Nickel/Carbon Catalyst to Increase Oxidation Stability

    Directory of Open Access Journals (Sweden)

    Ramayeni Elsa

    2018-01-01

    Full Text Available One of the methods to improve the oxidation stability of palm biodiesel is through partially hydrogenation. The production using Nickel/Carbon catalyst to speed up the reaction rate. Product is called Palm H-FAME (Hydrogenated FAME. Partial hydrogenation breaks the unsaturated bond on FAME (Fatty Acid Methyl Ester, which is a key component of the determination of oxidative properties. Changes in FAME composition by partial hydrogenation are predicted to change the oxidation stability so it does not cause deposits that can damage the injection system of diesel engine, pump system, and storage tank. Partial hydrogenation is carried out under operating conditions of 120 °C and 6 bar with 100:1, 100:3, 100:5, 100:10 % wt catalyst in the stirred batch autoclave reactor. H-FAME synthesis with 100:5 % wt Ni/C catalyst can decrease the iodine number which is the empirical measure of the number of unsaturated bonds from 91.78 to 82.38 (g-I2/100 g with an increase of oxidation stability from 585 to 602 minutes.

  8. Microstructure, mechanical properties and oxidation behaviors of magnetron sputtered NbN{sub x} coatings

    Energy Technology Data Exchange (ETDEWEB)

    Qi, Zhengbing, E-mail: zbqi@xmut.edu.cn [College of Materials Science and Engineering, Xiamen University of Technology, Xiamen (China); Department of Chemical and Biochemical Engineering, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen (China); Wu, Zhengtao; Zhang, Dongfang [Department of Chemical and Biochemical Engineering, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen (China); Zuo, Juan [College of Materials Science and Engineering, Xiamen University of Technology, Xiamen (China); Wang, Zhoucheng, E-mail: zcwang@xmu.edu.cn [Department of Chemical and Biochemical Engineering, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen (China)

    2016-08-05

    Mechanical properties and oxidation resistance are of importance for the NbN{sub x} coatings as used in cutting and forming tools. In this study, the NbN{sub x} coatings were deposited by magnetron sputtering at nitrogen partial pressure ranging from 0 to 40%. The chemical and phase compositions, morphologies, mechanical properties and oxidation behaviors of the NbN{sub x} coatings were investigated by electron probe microanalysis, X-ray photoelectron spectroscopy, grazing incidence X-ray diffraction, scanning and transmission electron microscopy, and nanoindentation measurements. The results reveal the composition evolution of the NbN{sub x} coatings as α-Nb (0%), β-Nb{sub 2}N (5%), a mixture of β-Nb{sub 2}N and δ-NbN (10%), and δ-NbN (20–40%). The single phase coatings exhibit columnar structure while the mixed phases coating shows nano-composite structure. Compared with the single phase δ-NbN coatings (21.6 ± 0.8–28.0 ± 1.2 GPa), higher hardness of the single phase β-Nb{sub 2}N coating (30.9 ± 1.0 GPa) is due to the higher covalent character and much finer grains. The maximum hardness reaches 33.3 ± 1.5 GPa for the nano-composite coating with mixed phases of β-Nb{sub 2}N and δ-NbN. The oxidation results demonstrate that the activation energies are 219.3 and 192.3 kJ/mol for the Nb{sub 2}N and NbN coatings respectively. Non-protective Nb{sub 2}O{sub 5} scales with cracks and pores result in poorer oxidation resistance of the NbN coating in comparison to the Nb{sub 2}N coating. - Highlights: • Chemical and phase compositions and microstructure of NbN{sub x} coatings were investigated. • Maximum hardness is obtained for nano-composite coating with mixed Nb{sub 2}N and NbN phases. • Activation energies are 219.3 and 192.3 kJ/mol for oxidation of Nb{sub 2}N and NbN coatings. • Non-protective Nb{sub 2}O{sub 5} scales with cracks and pores lower oxidation resistance of NbN coating.

  9. Catalytic partial oxidation of pyrolysis oils

    Science.gov (United States)

    Rennard, David Carl

    2009-12-01

    This thesis explores the catalytic partial oxidation (CPO) of pyrolysis oils to syngas and chemicals. First, an exploration of model compounds and their chemistries under CPO conditions is considered. Then CPO experiments of raw pyrolysis oils are detailed. Finally, plans for future development in this field are discussed. In Chapter 2, organic acids such as propionic acid and lactic acid are oxidized to syngas over Pt catalysts. Equilibrium production of syngas can be achieved over Rh-Ce catalysts; alternatively mechanistic evidence is derived using Pt catalysts in a fuel rich mixture. These experiments show that organic acids, present in pyrolysis oils up to 25%, can undergo CPO to syngas or for the production of chemicals. As the fossil fuels industry also provides organic chemicals such as monomers for plastics, the possibility of deriving such species from pyrolysis oils allows for a greater application of the CPO of biomass. However, chemical production is highly dependent on the originating molecular species. As bio oil comprises up to 400 chemicals, it is essential to understand how difficult it would be to develop a pure product stream. Chapter 3 continues the experimentation from Chapter 2, exploring the CPO of another organic functionality: the ester group. These experiments demonstrate that equilibrium syngas production is possible for esters as well as acids in autothermal operation with contact times as low as tau = 10 ms over Rh-based catalysts. Conversion for these experiments and those with organic acids is >98%, demonstrating the high reactivity of oxygenated compounds on noble metal catalysts. Under CPO conditions, esters decompose in a predictable manner: over Pt and with high fuel to oxygen, non-equilibrium products show a similarity to those from related acids. A mechanism is proposed in which ethyl esters thermally decompose to ethylene and an acid, which decarbonylates homogeneously, driven by heat produced at the catalyst surface. Chapter 4

  10. Microstructure of oxides in thermal barrier coatings grown under dry/humid atmosphere

    International Nuclear Information System (INIS)

    Zhou Zhaohui; Guo Hongbo; Wang Juan; Abbas, Musharaf; Gong Shengkai

    2011-01-01

    Graphical abstract: The presence of water vapor promoted the formation of spinels in the TBC. Highlights: → Thermal barrier coatings are produced by electron beam physical vapour deposition. → Oxidation behaviour of the coatings at 1100 deg. C has been investigated in dry/humid O 2 . → Thermally grown oxides formed in the coatings are characterized. → The presence of water vapour promotes the formation of spinel in the TBCs. - Abstract: The microstructure of thermally grown oxide (TGO) in thermal barrier coatings (TBCs) oxidized under dry/humid atmosphere at 1100 deg. C has been characterized by transmission electron microscopy. A thin and continuous oxide layer is formed in the as-deposited TBCs produced by electron beam physical vapor deposition. The TGO formed in dry atmosphere consists of an outer layer of fine α-alumina, zirconia grains and an inner layer of columnar α-alumina grains. However, a small amount of spinel is observed in the TGO under humid atmosphere. The presence of water vapour promotes the formation of spinel.

  11. The chemical energy unit partial oxidation reactor operation simulation modeling

    Science.gov (United States)

    Mrakin, A. N.; Selivanov, A. A.; Batrakov, P. A.; Sotnikov, D. G.

    2018-01-01

    The chemical energy unit scheme for synthesis gas, electric and heat energy production which is possible to be used both for the chemical industry on-site facilities and under field conditions is represented in the paper. The partial oxidation reactor gasification process mathematical model is described and reaction products composition and temperature determining algorithm flow diagram is shown. The developed software product verification showed good convergence of the experimental values and calculations according to the other programmes: the temperature determining relative discrepancy amounted from 4 to 5 %, while the absolute composition discrepancy ranged from 1 to 3%. The synthesis gas composition was found out practically not to depend on the supplied into the partial oxidation reactor (POR) water vapour enthalpy and compressor air pressure increase ratio. Moreover, air consumption coefficient α increase from 0.7 to 0.9 was found out to decrease synthesis gas target components (carbon and hydrogen oxides) specific yield by nearly 2 times and synthesis gas target components required ratio was revealed to be seen in the water vapour specific consumption area (from 5 to 6 kg/kg of fuel).

  12. Effects of isothermal treatment on microstructure and scratch test behavior of plasma sprayed zirconia coatings

    Directory of Open Access Journals (Sweden)

    Veloso Guilherme

    2004-01-01

    Full Text Available The increase of the petroleum cost in the last decades revitalized the interest for lighter and more economic vehicles. Simultaneously, the demand for safe and unpolluted transports grows. The application of thermal barriers coatings (TBC on combustion chamber and on flat surface of pistons reduces the thermal losses of the engines, resulting in higher temperatures in the combustion chamber. This fact contributes to the improvement of the thermal efficiency (performance and for the reduction of incomplete combustion. Supported on these initial ideas, thermal barriers coatings constituted by CaO partially stabilized zirconia were produced and their microstructure examined. This coating still presents some drawbacks associated with thermal stresses and permeability to oxidizing gases, which will, eventually, lead to failure of the TBC by spallation. The failure may, in general, be associated to one of three factors: oxide growth at the ceramic-metal interface, formed during thermal cycling; stress build-up due to thermal cycling; and metal-oxide interface segregation, mainly of S. However, it is also relevant to understand the behavior of TBC's under isothermal oxidation. Therefore, this paper investigates the effect of oxidation on the adherence of thermal sprayed coatings. The adherence was measured by linear scratching tests, widely used for thin coatings. Plasma sprayed calcia partially stabilized zirconia was used as TBC and Ni-5%Al as bond coat, with Al substrates. Coated samples were submitted to heat treatments at 500 °C, for 50 h. The microstructures were examined by optical light microscopy, X-ray diffraction, profilometry and SEM.

  13. Microstructure and mechanical properties of multi-components rare earth oxide-doped molybdenum alloys

    International Nuclear Information System (INIS)

    Zhang Guojun; Sun Yuanjun; Zuo Chao; Wei Jianfeng; Sun Jun

    2008-01-01

    Pure molybdenum and molybdenum alloys doped with two- or three-components rare earth oxide particles were prepared by powder metallurgy. Both the tensile property and fracture toughness of the pure molybdenum and multi-components rare earth oxide-doped molybdenum alloys were determined at room temperature. The multi-components rare earth oxide-doped molybdenum alloys are fine grained and contain a homogeneous distribution of fine particles in the submicron and nanometer size ranges, which is why the molybdenum alloys have higher strength and fracture toughness than pure molybdenum. Quantitative analysis is used to explain the increase in yield strength with respect to grain size and second phase strengthening. Furthermore, the relationship between the tensile properties and microstructural parameters is quantitatively established

  14. Microstructure characterisation of solid oxide electrolysis cells operated at high current density

    DEFF Research Database (Denmark)

    Bowen, Jacob R.; Bentzen, Janet Jonna; Chen, Ming

    degradation of cell components in relation to the loss of electrochemical performance specific to the mode of operation. Thus descriptive microstructure characterization methods are required in combination with electrochemical characterization methods to decipher degradation mechanisms. In the present work......High temperature solid oxide cells can be operated either as fuel cells or electrolysis cells for efficient power generation or production of hydrogen from steam or synthesis gas (H2 + CO) from steam and CO2 respectively. When operated under harsh conditions, they often exhibit microstructural...... quantified using the mean linear intercept method as a function of current density and correlated to increases in serial resistance. The above structural changes are then compared in terms of electrode degradation observed during the co-electrolysis of steam and CO2 at current densities up to -1.5 A cm-2...

  15. Microstructural study and wear behavior of ductile iron surface alloyed by Inconel 617

    International Nuclear Information System (INIS)

    Arabi Jeshvaghani, R.; Jaberzadeh, M.; Zohdi, H.; Shamanian, M.

    2014-01-01

    Highlights: • The Ni-base alloy was deposited on the surface of ductile iron by TIG welding process. • Microstructure of alloyed layer consisted of carbides embedded in Ni-rich dendrite. • Hardness and wear resistance of coated sample greatly improved. • The formation of oxide layer and delamination were dominant mechanisms of wear. - Abstract: In this research, microstructure and wear behavior of Ni-based alloy is discussed in detail. Using tungsten inert gas welding process, coating of nearly 1–2 mm thickness was deposited on ductile iron. Optical and scanning electron microscopy, as well as X-ray diffraction analysis and electron probe microanalysis were used to characterize the microstructure of the surface alloyed layer. Micro-hardness and wear resistance of the alloyed layer was also studied. Results showed that the microstructure of the alloyed layer consisted of M 23 C 6 carbides embedded in Ni-rich solid solution dendrites. The partial melted zone (PMZ) had eutectic ledeburit plus martensite microstructure, while the heat affected zone (HAZ) had only a martensite structure. It was also noticed that hardness and wear resistance of the alloyed layer was considerably higher than that of the substrate. Improvement of wear resistance is attributed to the solution strengthening effect of alloying elements and also the presence of hard carbides such as M 23 C 6 . Based on worn surface analysis, the dominant wear mechanisms of alloyed layer were found to be oxidation and delamination

  16. Ce-Fe-O mixed oxide as oxygen carrier for the direct partial oxidation of methane to syngas

    Institute of Scientific and Technical Information of China (English)

    魏永刚; 王华; 李孔斋

    2010-01-01

    The Ce-Fe-O mixed oxide with a ratio of Ce/Fe=7:3, which was prepared by coprecipitation method and employed as oxygen carrier, for direct partial oxidation of methane to syngas in the absence of gaseous oxygen was explored. The mixed oxide was characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM), and the catalytic performances were studied in a fixed-bed quartz reactor and a thermogravimetric reactor, respectively. Approximately 99.4% H2 se...

  17. Analysis of electrical and microstructural characteristics of a ZnO-based varistor doped with rare earth oxide

    International Nuclear Information System (INIS)

    Andrade, J.M. de; Dias, R.; Furtado, J.G. de M.; Assuncao, F.C.R.

    2010-01-01

    Varistor is a semiconductor device, used in the protection of electrical systems, characterized to have a high no-linear electric resistance. Its properties are directly dependents of its chemical composition and microstructural characteristics. In this work were analyzed microstructural and electrical characteristics of a ZnO-based varistor doped with rare earth oxide, with chemical composition (mol%) 98,5.ZnO - 0,3.Pr 6 O 11 - 0,2.Dy 2 O 3 - 0,9.Co 2 O 3 - 0,1.Cr 2 O 3 . X-ray diffraction for phase characterization, scanning electron microscopy and energy dispersive X-ray spectroscopy were used for microstructural analysis. Measurement of average grain size and electrical and dielectric characteristics complete the characterization. The results show the formation of biphasic microstructure and with high densification, presenting relevant varistors characteristics but that would need improvements.(author)

  18. Modelling of the partial oxidation of {alpha}, {beta}-unsaturated aldehydes on Mo-V-oxides based catalysts

    Energy Technology Data Exchange (ETDEWEB)

    Boehnke, H.; Petzoldt, J.C.; Stein, B.; Weimer, C.; Gaube, J.W. [Technische Univ. Darmstadt (Germany). Inst. fuer Chemische Technologie

    1998-12-31

    A kinetic model based on the Mars-van Krevelen mechanism that allows to describe the microkinetics of the heterogeneously catalysed partial oxidation of {alpha}, {beta}-unsaturated aldehydes is presented. This conversion is represented by a network, composed of the oxidation of the {alpha}, {beta}-unsaturated aldehyde towards the {alpha}, {beta}-unsaturated carboxylic acid and the consecutive oxidation of the acid as well as the parallel reaction of the aldehyde to products of deeper oxidation. The reaction steps of aldehyde respectively acid oxidation and catalyst reoxidation have been investigated separately in transient experiments. The combination of steady state and transient experiments has led to an improved understanding of the interaction of the catalyst with the aldehyde and the carboxylic acids as well as to a support of the kinetic model assumptions. (orig.)

  19. Evaluation of the structure and microstructure of NixMg1-xO oxides obtained by co-precipitation

    International Nuclear Information System (INIS)

    Martinez L, G.; Kryshtab, T.; Hesiquio G, M.; Kryvko, A.

    2013-01-01

    Ni x Mg 1-x O oxides were prepared by thermal treatment at temperatures of 400, 600 and 800 C from a hydrotalcite-like precursor obtained by co-precipitation at constant ph. The oxides obtained were characterized by X-ray diffraction methods. From the obtained results we concluded that the oxides calcined at temperatures of 400, and 600 C are unstable that means that there exists the effect of memory and with a time they return to the precursor. Presence of Ni in Mg oxide provides stability of the compounds thermally treated at 800 C. In order to analyze the structure and microstructure, the reflections 111, 200 and 220 were used. The positions of the maxima of the diffraction peaks are shifted with respect to the simulated ones for Mg O and Ni O. This result reveals that in solid solutions studied compressive strains or vacation are present. The parameters of the microstructure (coherent domain size and micro deformations) were evaluated. The coherent domain size was found to be in the range of 8 - 10 nm and the presence of residual strains of micro deformation can be associated with the existence of extended defects. (Author)

  20. Complete and Partial Photo-oxidation of Dissolved Organic Matter Draining Permafrost Soils.

    Science.gov (United States)

    Ward, Collin P; Cory, Rose M

    2016-04-05

    Photochemical degradation of dissolved organic matter (DOM) to carbon dioxide (CO2) and partially oxidized compounds is an important component of the carbon cycle in the Arctic. Thawing permafrost soils will change the chemical composition of DOM exported to arctic surface waters, but the molecular controls on DOM photodegradation remain poorly understood, making it difficult to predict how inputs of thawing permafrost DOM may alter its photodegradation. To address this knowledge gap, we quantified the susceptibility of DOM draining the shallow organic mat and the deeper permafrost layer of arctic soils to complete and partial photo-oxidation and investigated changes in the chemical composition of each DOM source following sunlight exposure. Permafrost and organic mat DOM had similar lability to photomineralization despite substantial differences in initial chemical composition. Concurrent losses of carboxyl moieties and shifts in chemical composition during photodegradation indicated that photodecarboxylation could account for 40-90% of DOM photomineralized to CO2. Permafrost DOM had a higher susceptibility to partial photo-oxidation compared to organic mat DOM, potentially due to a lower abundance of phenolic moieties with antioxidant properties. These results suggest that photodegradation will likely continue to be an important control on DOM fate in arctic freshwaters as the climate warms and permafrost soils thaw.

  1. Partial Oxidation of High-Boiling Hydrocarbon Mixtures in the Pilot Unit

    Czech Academy of Sciences Publication Activity Database

    Hanika, Jiří; Lederer, J.; Nečesaný, F.; Poslední, W.; Tukač, V.; Veselý, Václav

    2014-01-01

    Roč. 68, č. 12 (2014), s. 1701-1706 ISSN 0366-6352 Institutional support: RVO:67985858 Keywords : partial oxidation * high-boiling hydrocarbons * pilot plant Subject RIV: CI - Industrial Chemistry , Chemical Engineering Impact factor: 1.468, year: 2014

  2. Development of oxide dispersion strengthened 2205 duplex stainless steel composite

    Directory of Open Access Journals (Sweden)

    Oladayo OLANIRAN

    2015-05-01

    Full Text Available Composites of duplex stainless steel were produced by oxide dispersion strengthening with comparatively improved mechanical properties by hot press sintering of partially stabilized Zirconia (PSZ, 3% yttria, mole fraction dispersion in 2205 duplex stainless steels. Ceramic oxide was added as reinforcement, while chromium (Cr and Nickel (Ni were incorporated to maintain the austenitic/ferritic phase balance of the duplex stainless steel. The powders and sintered were characterized in detail using scanning electron microscopy (SEM and X-ray diffraction (XRD. The microstructural evolution and phase formation during oxide dispersion strengthening of duplex stainless steel composites were investigated. The influence of composition variation of the reinforcements on the microstructural and corrosion behaviour in simulated mine water of the composites were investigated. In this manuscript, it was established that composition has great influence on the structure/properties relationship of the composites developed.

  3. Biological degradation of partially oxidated constituents of stabilized sapropel; Biologischer Abbau teiloxidierter Inhaltsstoffe stabilisierter Faulschlaemme

    Energy Technology Data Exchange (ETDEWEB)

    Scheminski, A.; Krull, R.; Hempel, D.C. [Technische Univ. Braunschweig (Germany). Inst. fuer Bioverfahrenstechnik

    1999-07-01

    Partial oxidation of sapropel with ozone destroys the cell walls of microorganisms in sludge and releases the cell constituents. Substances that are not biologically degraded because of the size or structure of their molecules are transformed into smaller, water-soluble and biologically degradable fractions by the reaction with ozone. The experiments aim to render the partially oxidated sewage sludge constituents highly biologically degradable using a minimum of oxidation agents. For the experiments described, stabilized sapropels with low biological activity are used. Hence the ozone is mainly used for the partial oxidation of recalcitrant constituents. (orig.) [German] Durch partielle Oxidation von Faulschlaemmen mit Ozon werden die Zellwaende der Mikroorganismen im Schlamm zerstoert und die Zellinhaltsstoffe freigesetzt. Dabei werden Substanzen, die aufgrund ihrer Molekuelgroesse oder -struktur biologisch nicht abgebaut werden, durch die Reaktion mit Ozon in kleinere, wasserloesliche und biologisch abbaubare Bruchstuecke ueberfuehrt. Ziel der Versuche ist es, durch den Einsatz moeglichst geringer Mengen an Oxidationsmitteln eine hohe biologische Abbaubarkeit der teiloxidierten Klaerschlamminhaltsstoffe zu erreichen. Fuer die hier vorgestellten Experimente wurden stabilisierte Faulschlaemme mit geringer biologischer Aktivitaet eingesetzt. Dadurch wird das Ozon vorwiegend zur Teiloxidation recalcitranter Inhaltsstoffe genutzt. (orig.)

  4. Microstructure formation in partially melted zone during gas tungsten arc welding of AZ91 Mg cast alloy

    International Nuclear Information System (INIS)

    Zhu Tianping; Chen, Zhan W.; Gao Wei

    2008-01-01

    During gas tungsten arc (GTA) welding of AZ91 Mg cast alloy, constitutional liquid forms locally in the original interdendritic regions in the partially melted zone (PMZ). The PMZ re-solidification behaviour has not been well understood. In this study, the gradual change of the re-solidification microstructure within PMZ from base metal side to weld metal side was characterised. High cooling rate experiments using Gleeble thermal simulator were also conducted to understand the morphological change of the α-Mg/β-Mg 17 Al 12 phase interface formed during re-solidification after partial melting. It was found that the original partially divorced eutectic structure has become a more regular eutectic phase in most of the PMZ, although close to the fusion boundary the re-solidified eutectic is again a divorced one. Proceeding the eutectic re-solidification, if the degree of partial melting is sufficiently high, α-Mg re-solidified with a cellular growth, resulting in a serrated interface between α-Mg and α-Mg/β-Mg 17 Al 12 in the weld sample and between α-Mg and β-Mg 17 Al 12 (fully divorced eutectic) in Gleeble samples. The morphological changes affected by the peak temperature and cooling rate are also explained

  5. Correlation of waterside corrosion and cladding microstructure in high-burnup fuel and gadolinia rods

    International Nuclear Information System (INIS)

    Chung, H.M.

    1989-09-01

    Waterside corrosion of the Zircaloy cladding has been examined in high-burnup fuel rods from several BWRs and PWRs, as well as in 3 wt % gadolinia burnable poison rods obtained from a BWR. The corrosion behavior of the high-burnup rods was then correlated with results from a microstructural characterization of the cladding by optical, scanning-electron, and transmission-electron microscopy (OM, SEM, and TEM). OM and SEM examination of the BWR fuel cladding showed both uniform and nodular oxide layers 2 to 45 μm in thickness after burnups of 11 to 30 MWd/kgU. For one of the BWRs, which was operated at 307 degree C rather than the normal 288 degree C, a relatively thick (50 to 70 μm) uniform oxide, rather than nodular oxides, was observed after a burnup of 27 to 30 MWd/kgU. TEM characterization revealed a number of microstructural features that occurred in association with the intermetallic precipitates in the cladding metal, apparently as a result of irradiation-induced or -enhanced processes. The BWR rods that exhibited white nodular oxides contained large precipitates (300 to 700 nm in size) that were partially amorphized during service, indicating that a distribution of the large intermetallic precipitates is conductive to nodular oxidation. 23 refs., 9 figs

  6. Effect of coating parameters on the microstructure of cerium oxide conversion coatings

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, Benedict Y.; Edington, Joe; O' Keefe, Matthew J

    2003-11-25

    The microstructure and morphology of cerium oxide conversion coatings prepared under different deposition conditions were characterized by transmission electron microscopy (TEM). The coatings were formed by a spontaneous reaction between a water-based solution containing CeCl{sub 3} and aluminum alloy 7075-T6 substrates. Microstructural characterization was performed to determine the crystallinity of the coatings and to obtain a better understanding of the deposition parameters on coating microstructure. The results of TEM imaging and electron diffraction analysis indicated that the as-deposited coating was composed of nanocrystalline particles of a previously unreported cerium compound. The particles of the coatings produced using glycerol as an additive were found to be much finer than those of the coatings prepared in the absence of glycerol. This indicates that glycerol may act as a grain refiner and/or growth inhibitor during coating deposition. After deposition, the coated panels were treated for 5 min in a phosphate sealing solution. The sealing treatment converted the as-deposited coating into hydrated cerium phosphate. Panels coated from solutions containing no glycerol followed by phosphate sealing performed poorly in salt fog tests. With glycerol addition, the corrosion resistance of the coatings that were phosphate sealed improved considerably, achieving an average passing rate of 85%.

  7. Growth and surface characterization of sputter-deposited molybdenum oxide thin films

    Energy Technology Data Exchange (ETDEWEB)

    Ramana, Chintalapalle V.; Atuchin, Victor V.; Kesler, V. G.; Kochubey, V. A.; Pokrovsky, L. D.; Shutthanandan, V.; Becker, U.; Ewing, Rodney C.

    2007-04-15

    Molybdenum oxide thin films were produced by magnetron sputtering using a molybdenum (Mo) target. The sputtering was performed in a reactive atmosphere of argon-oxygen gas mixture under varying conditions of substrate temperature (Ts) and oxygen partial pressure (pO2). The effect of Ts and pO2 on the growth and microstructure of molybdenum oxide films was examined in detail using reflection high-energy electron diffraction (RHEED), Rutherford backscattering spectrometry (RBS), energy dispersive X-ray spectrometry (EDS), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM) measurements. The analyses indicate that the effect of Ts and pO2 on the microstructure and phase of the grown molybdenum oxide thin films is remarkable. RHEED and RBS results indicate that the films grown at 445 *C under 62.3% O2 pressure were stoichiometric and polycrystalline MoO3. Films grown at lower pO2 were nonstoichiometric MoOx films with the presence of secondary phase. The microstructure of the grown Mo oxide films is discussed and conditions were optimized to produce phase pure, stoichiometric, and highly textured polycrystalline MoO3 films.

  8. Microstructure and microtexture evolutions of deformed oxide layers on a hot-rolled microalloyed steel

    International Nuclear Information System (INIS)

    Yu, Xianglong; Jiang, Zhengyi; Zhao, Jingwei; Wei, Dongbin; Zhou, Cunlong; Huang, Qingxue

    2015-01-01

    Highlights: • Microtexture development of deformed oxide layers is investigated. • Magnetite shares the {0 0 1} fibre texture with wustite. • Hematite develops the {0 0 0 1} basal fibre parallel to the oxide growth. • Stress relief and ion vacancy diffusion mechanism for magnetite seam. - Abstract: Electron backscatter diffraction (EBSD) analysis has been presented to investigate the microstructure and microtexture evolutions of deformed oxide scale formed on a microalloyed steel during hot rolling and accelerated cooling. Magnetite and wustite in oxide layers share a strong {0 0 1} and a weak {1 1 0} fibres texture parallel to the oxide growth. Trigonal hematite develops the {0 0 0 1} basal fibre parallel to the crystallographic plane {1 1 1} in magnetite. Taylor factor estimates have been conducted to elucidate the microtexture evolution. The fine-grained magnetite seam adjacent to the substrate is governed by stress relief and ions vacancy diffusion mechanism

  9. Laser-induced partial oxidation of cyclohexane in liquid phase

    International Nuclear Information System (INIS)

    Oshima, Y.; Wu, X.W.; Koda, S.

    1995-01-01

    A laser-induced partial oxidation of cyclohexane was studied in the liquid phase. With KrF excimer laser (248 nm) irradiation to neat liquid cyclohexane in which O 2 was dissolved, cyclohexanol and cyclohexanone were obtained with very high selectivities, together with cyclohexane as a minor product. Radical recombination reactions to produce dicyclohexyl ether and bicyclohexyl also took place, while these products were not observed in the gas phase reaction. These experimental results were considered to be due not only to higher concentration of cyclohexane but to the cage effect in the liquid phase oxidation. To clarify the reaction progress including the photoabsorption process, the effects of laser intensity and O 2 pressure on product distribution were studied. (author)

  10. Investigation of microstructure thermal evolution in nanocrystalline Cu

    International Nuclear Information System (INIS)

    Zhou Kai; Li Hui; Pang Jinbiao; Wang Zhu

    2011-01-01

    The microstructure of nanocrystalline Cu prepared by compacting nanoparticles (50-60 nm in diameter) under high pressures has been studied by means of positron lifetime spectroscopy and X-ray diffraction. These nanoparticles were produced by two different methods. We found that there are order regions interior to the grains and disorder regions at the grain boundaries with a wide distribution of interatomic distances. The mean grain sizes of the nanocrystalline Cu samples decrease after being annealed at 900 o C and increase during aging at 180 o C, which are observed by X-ray diffraction, revealing that the atoms exchange between the two regions. The positron lifetime results clearly indicate that the vacancy clusters formed in the annealing process are unstable and decomposed at the aging time below 6 hours. In addition, the partially oxidized surfaces of the nanoparticles hinder grain growth when the samples age at 180 o C, and the vacancy clusters inside the disorder regions, which are related to Cu 2 O, need longer aging time to decompose. The disorder regions remain after the heat treatment in this work, in spite of the grain growth, which will be good for the samples keeping the properties of nanocrystalline material. -- Research highlights: → We use a digital positron lifetime spectrometer correlated with XRD to study the microstructure evolution of nanocrystalline Cu during thermal treatment. → An atomic scale microstructure of grain boundary is characterized. Further, the surface oxidation of the nanoparticles is considered. → The disorder regions remain after the heat treatment in this work, in spite of grain growth.

  11. Microstructure and mechanical properties of metal/oxide and metal/silicide interfaces

    International Nuclear Information System (INIS)

    Shaw, L.; Miracle, D.; Abbaschian, R.

    1995-01-01

    Fracture energies of Al 2 O 3 /Nb interfaces and MoSi 2 /Nb interfaces with and without Al 2 O 3 coating were measured using sandwich-type chevron-notched specimens. The relations between the mechanical properties, microstructures, types of bonds at the interface and processing routes were explored. The fracture energy of the Al 2 O 3 /Nb interface was determined to be 9 J/m 2 and changed to 16 J/m 2 when Nb was pre-oxidized before the formation of the Al 2 O 3 /Nb interface. The fracture energy of the MoSi 2 /Nb interface could not be determined directly because of the formation of the interfacial compounds. However, the fracture energy at the MoSi 2 /Nb interfacial region was found to depend on the interfacial bond strength, roughness of interfaces and microstructure of interfacial compounds. The interfacial fracture energies of Al 2 O 3 with silicides, MoSi 2 , Nb 5 Si 3 , or (Nb, Mo)Si 2 were estimated to be about 16 J/m 2 , while the interfacial fracture energies between two silicides or between Nb and a silicide were larger than 34 J/m 2 . The measured fracture energies between two silicides or between Nb and a silicide were larger than 34 J/m 2 . The measured fracture energies of the various interfaces are discussed in terms of the interfacial microstructures and types of bonds at the interfaces

  12. Partial oxidation of methane in a temperature-controlled dielectric barrier discharge reactor

    KAUST Repository

    Zhang, Xuming; Cha, Min

    2015-01-01

    We studied the relative importance of the reduced field intensity and the background reaction temperature in the partial oxidation of methane in a temperature-controlled dielectric barrier discharge reactor. We obtained important mechanistic insight

  13. A spectroscopic and microstructural study of oxide coatings produced on a Ti–6Al–4V alloy by plasma electrolytic oxidation

    International Nuclear Information System (INIS)

    Hussein, R.O.; Nie, X.; Northwood, D.O.

    2012-01-01

    Highlights: ► PEO (plasma electrolytic oxidation) for production of oxide coatings on a Ti–6Al–4V alloy. ► Two different current modes namely pulsed unipolar and bipolar was used. ► Optical emission spectroscopy (OES) was used to characterize the PEO plasma. ► This is the first attempt to characterize spectroscopically the PEO plasma of Ti and its alloys. ► The discharge behavior effect on the formation and structure of the coating was determined. - Abstract: In this study, we have used PEO (plasma electrolytic oxidation) for the production of oxide coatings on a Ti–6Al–4V alloy at two different current modes, namely pulsed unipolar and bipolar. Optical emission spectroscopy (OES) in the visible and near UV band (280–800 nm) was used to characterize the PEO plasma. The emission spectra were recorded and the plasma temperature profile versus processing time was constructed using a line intensity ratios method. The aim of this work was to study the effect of the process parameters, including current mode and pulse duration time, on the plasma characteristics, surface morphology and microstructure and corrosion resistance of oxides grown on Ti–6Al–4V by PEO process. Scanning electron microscopy (SEM) with energy dispersive X-ray analysis (EDS) and X-ray diffraction (XRD) were used to study the coating microstructure, morphology and phase composition. The corrosion resistance of the coated and uncoated samples was examined by potentiodynamic polarization in a 3.5% NaCl solution. It was found that the plasma temperature profiles are significantly influenced by changing the current mode from unipolar to bipolar. The strongest discharges that are initiated at the interface between the substrate and the coating can be reduced or eliminated by using a bipolar current mode. This produces a thinner, denser and more corrosion-resistant coating.

  14. Plasma-assisted partial oxidation of methane at low temperatures: numerical analysis of gas-phase chemical mechanism

    Energy Technology Data Exchange (ETDEWEB)

    Goujard, Valentin; Nozaki, Tomohiro; Yuzawa, Shuhei; Okazaki, Ken [Department of Mechanical and Control Engineering, Tokyo Institute of Technology, 2-12-1 O-okayama, Meguro, 1528552, Tokyo (Japan); Agiral, Anil, E-mail: tnozaki@mech.titech.ac.jp [Mesoscale Chemical Systems, MESA Institute for Nanotechnology, Faculty of Science and Technology, University of Twente, PO Box 217, 7500 AE, Enschede (Netherlands)

    2011-07-13

    Methane partial oxidation was investigated using a plasma microreactor. The experiments were performed at 5 and 300 deg. C. Microreactor configuration allows an efficient evacuation of the heat generated by methane partial oxidation and dielectric barrier discharges, allowing at the same time a better temperature control. At 5 deg. C, liquid condensation of low vapour pressure compounds, such as formaldehyde and methanol, occurs. {sup 1}H-NMR analysis allowed us to demonstrate significant CH{sub 3}OOH formation during plasma-assisted partial oxidation of methane. Conversion and product selectivity were discussed for both temperatures. In the second part of this work, a numerical simulation was performed and a gas-phase chemical mechanism was proposed and discussed. From the comparison between the experimental results and the simulation it was found that CH{sub 3}OO{center_dot} formation has a determinant role in oxygenated compound production, since its fast formation disfavoured radical recombination. At 5 deg. C the oxidation leads mainly towards oxygenated compound formation, and plasma dissociation was the major phenomenon responsible for CH{sub 4} conversion. At 300 deg. C, higher CH{sub 4} conversion resulted from oxidative reactions induced by {center_dot}OH radicals with a chemistry predominantly oxidative, producing CO, H{sub 2}, CO{sub 2} and H{sub 2}O.

  15. Microstructure of Semi-Solid 6063 Alloy Fabricated by Radial Forging Combined with Unidirectional Compression Recrystallization and Partial Melting Process

    Directory of Open Access Journals (Sweden)

    Wang Yongfei

    2017-01-01

    Full Text Available Radial forging combined with unidirectional compression (RFCUM is introduced in recrystallization and partial melting (RAP to fabricate semi-solid 6063 aluminum alloy, which can be defined as a process of RFCUM-RAP. In this study, the microstructures of semi-solid 6063 alloy prepared by semi-solid isothermal treatment (SSIT and RFCUM-RAP processes are investigated. The results show that, the solid grains of semi-solid alloy prepared by SSIT are large and irregular. However, solid grains of semi-solid billet prepared by RFCUC-RAP are fine and spherical. Additionally, during RFCUC-RAP process, with the increase of isothermal holding time, the shape of solid grain is more and more spherical, but the size of solid grain is gradually increased. To obtain ideal semi-solid microstructure, the optimal isothermal holding temperature and time are 630 °C and 5~10 min, respectively.

  16. Oxidation of Fe–22Cr Coated with Co3O4: Microstructure Evolution and the Effect of Growth Stresses

    DEFF Research Database (Denmark)

    Hansson, Anette Nørgaard; Burriel, Monica; Garcia, Gemma

    2007-01-01

    The oxidation behavior of a commercially available Fe–22Cr alloy coated with a Co3O4 layer by metal organic—chemical vapor deposition was investigated in air with 1% H2O at 1,173 K and compared to the oxidation behavior of the non-coated alloy. The oxide morphology was examined with X......-ray diffraction, electron microscopy, and energy dispersive X-ray spectroscopy. Cr2O3 developed in between the Co3O4 coating and the alloy, while alloying elements of the substrate were incorporated into the coating. Particular attention was devoted to possible sources of growth stresses and the effect...... of the growth stresses on microstructure evolution in the scales that developed on the non-coated and the coated Fe–22Cr alloy. Microstructural features suggested that scale spallation on coated Fe–22Cr occurred as a result of superimposing thermal stresses during cooling onto the growth stresses, that had...

  17. Microstructure-property relationships of rare-earth--zinc-oxide varistors

    International Nuclear Information System (INIS)

    Williams, P.; Krivanek, O.L.; Thomas, G.; Yodogawa, M.

    1980-01-01

    The microstructure and properties of ZnO varistors containing Ba, Co, and rare-earth--metal oxides, which give values of α [α=d(log I)/d(log V)] as high as 29, are examined. Mean ZnO grain size is 11 μm, and the grains are uniformly doped with Co. The barium and rare earth metals concentrate into 1.5-μm-wide particles embedded in a matrix of ZnO grains. Within the grains and at grain boundaries, the barium and rare-earth--metal concentration is below the detection limit of the energy-dispersive spectrometer technique (about 0.5%). No intergranular films, amorphous or crystalline, are detected, to within 10 A resolution. These results are shown to be consistent with the grain boundary charge depletion model for the voltage barrier formation and breakdown

  18. Evolution of Microstructure and Mechanical Properties of Oxide Dispersion Strengthened Steels Made from Water-Atomized Ferritic Powder

    Science.gov (United States)

    Arkhurst, Barton Mensah; Kim, Jeoung Han

    2018-05-01

    Nano-structured oxide dispersion strengthened (ODS) steels produced from a 410L stainless steel powder prepared by water-atomization was studied. The influences of Ti content and milling time on the microstructure and the mechanical properties were analysed. It was found that the ODS steels made from the Si bearing 410L powder contained Y-Ti-O, Y-Ti-Si-O, Y-Si-O, and TiO2 oxides. Most nanoparticles produced after 80 h of milling were aggregated nanoparticles; however, after 160 h of milling, most aggregated nanoparticles dissociated into smaller individual nanoparticles. Perfect mixing of Y and Ti was not achieved even after the longer milling time of 160 h; instead, the longer hours of milling rather resulted in Si incorporation into the Y-Ti-O rich nanoparticles and a change in the matrix morphology from an equiaxed microstructure to a tempered martensite-like microstructure. The overall micro-hardness of the ODS steel increased with the increase of milling time. After 80 and 160 h, the microhardnesses were over 400 HV, which primarily resulted from the finer dispersed nanoparticles and in part to the formation of martensitic phases. Tensile strength of the 410L ODS steels was comparable with that of ODS steel produced from gas-atomized powder.

  19. Microstructure and Mechanical Property of 12Cr Oxide Dispersion Strengthened Steel

    Science.gov (United States)

    Xu, Haijian; Lu, Zheng; Jia, Chunyan; Gao, Hao; Liu, Chunming

    2016-03-01

    Nanostructured oxide dispersion strengthened (ODS) steels with nominal compositions (wt%): Fe-12Cr-2W-0.3Ti-0.3Y2O3 were produced by mechanical alloying and hot isostatic pressing. The microstructure was characterized by means of electron microscopy (EBSD, TEM and HRTEM) and the hardness and the tensile properties at different temperatures were measured. The results showed that the ultimate tensile strength of the fabricated 12Cr-ODS steel reached nearly 1,100 MPa at room temperature and maintained around 340 MPa at 700°C. Nano-oxide particles with size ranging from several nm to 30 nm and the number density was 3.6 × 1020/m3 were observed by TEM. Following heat treatment, including normalizing at 1,100°C for 1 h and tempering at 750°C for 2 h, the average grain size was a little decreased. The number of nano-oxide particles increased and the number density was 8.9 × 1020/m3. Specimens showed much higher ductility and there was a slight increase of ultimate tensile strength and Vickers hardness at the same time.

  20. Effect of nano-ZrO2 addition on microstructure, mechanical property and thermal shock behaviour of dense chromic oxide refractory material

    International Nuclear Information System (INIS)

    Lu, Lixia; Ding, Chunhui; Zhanga, Chi; Yanga, De'an; Di, Lizhi

    2015-01-01

    To obtain a good performance hot-face lining material in gasifier, nano-ZrO 2 , up to 5 wt %, was added into chromic oxide powder with 3 wt % TiO 2 followed by sintering at 1500°C for 2.5 h. The effect of nano-ZrO 2 addition on microstructure, mechanical property and thermal shock behaviour was studied. ZrO 2 promoted densification at contents higher than 1 wt %. Microcracks and phase transformation toughened the dense chromic oxide refractory material. The main reason for decrease of strength was the existence microcracks in specimens and weakening of intergranular fracture. Dense chromic oxide refractory material with 2∼3 wt % nano-ZrO 2 possessed good densification, uniform microstructure, normal mechanical property and proper thermal shock resistance. The rupture strength retention ratio was nearly twice than that of chromic oxide material without ZrO 2 after three cycles of quenching test from 950°C to cold water. (author)

  1. Hydrogen Production via Synthetic Gas by Biomass/Oil Partial Oxidation

    Czech Academy of Sciences Publication Activity Database

    Hanika, Jiří; Lederer, J.; Tukač, V.; Veselý, Václav; Kováč, D.

    176-177, - (2011), s. 286-290 ISSN 1385-8947. [International Conference on Chemical Reactors CHEMREACTOR-19 /19./. Vienna, 05.09.2010-09.09.2010] R&D Projects: GA MPO 2A-2TP1/024 Institutional research plan: CEZ:AV0Z40720504 Keywords : hydrogen * biomass * partial oxidation Subject RIV: CI - Industrial Chemistry, Chemical Engineering Impact factor: 3.461, year: 2011

  2. Partial oxidation of TiN coating by hydrothermal treatment and ozone treatment to improve its osteoconductivity

    International Nuclear Information System (INIS)

    Shi, Xingling; Xu, Lingli; Le, Thi Bang; Zhou, Guanghong; Zheng, Chuanbo; Tsuru, Kanji; Ishikawa, Kunio

    2016-01-01

    Dental implants made of pure titanium suffer from abrasion and scratch during routine oral hygiene procedures. This results in an irreversible surface damage, facilitates bacteria adhesion and increases risk of peri-implantitis. To overcome these problems, titanium nitride (TiN) coating was introduced to increase surface hardness of pure titanium. However, the osteoconductivity of TiN is considered to be similar or superior to that of titanium and its alloys and therefore surface modification is necessary. In this study, TiN coating prepared through gas nitriding was partially oxidized by hydrothermal (HT) treatment and ozone (O 3 ) treatment in pure water to improve its osteoconductivity. The effects of HT treatment and O 3 treatment on surface properties of TiN were investigated and the osteoconductivity after undergoing treatment was assessed in vitro using osteoblast evaluation. The results showed that the critical temperature for HT treatment was 100 °C since higher temperatures would impair the hardness of TiN coating. By contrast, O 3 treatment was more effective in oxidizing TiN surfaces, improving its wettability while preserving its morphology and hardness. Osteoblast attachment, proliferation, alkaline phosphatase (ALP) expression and mineralization were improved on oxidized specimens, especially on O 3 treated specimens, compared with untreated ones. These effects seemed to be consequences of partial oxidation, as well as improved hydrophilicity and surface decontamination. Finally, it was concluded that, partially oxidized TiN is a promising coating to be used for dental implant. - Highlights: • TiN coating surface was oxidized by hydrothermal or ozone treatment while preserving its hardness. • Improved wettability, decontamination and interstitial N promoted osteoblast responses. • Partial oxidation makes TiN a promising coating for dental implant with good osteoconductivity.

  3. Partial oxidation of TiN coating by hydrothermal treatment and ozone treatment to improve its osteoconductivity

    Energy Technology Data Exchange (ETDEWEB)

    Shi, Xingling [School of Material Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang 212003 (China); Department of Biomaterials, Faculty of Dental Science, Kyushu University, Fukuoka 812-8582 (Japan); Jiangsu Provincial Key Laboratory for Interventional Medical Devices, Huaiyin Institute of Technology, Huaian 223003 (China); Xu, Lingli, E-mail: linly311@163.com [School of Material Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang 212003 (China); Le, Thi Bang [Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur (Malaysia); Zhou, Guanghong [Jiangsu Provincial Key Laboratory for Interventional Medical Devices, Huaiyin Institute of Technology, Huaian 223003 (China); Zheng, Chuanbo, E-mail: zjust316@163.com [School of Material Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang 212003 (China); Tsuru, Kanji; Ishikawa, Kunio [Department of Biomaterials, Faculty of Dental Science, Kyushu University, Fukuoka 812-8582 (Japan)

    2016-02-01

    Dental implants made of pure titanium suffer from abrasion and scratch during routine oral hygiene procedures. This results in an irreversible surface damage, facilitates bacteria adhesion and increases risk of peri-implantitis. To overcome these problems, titanium nitride (TiN) coating was introduced to increase surface hardness of pure titanium. However, the osteoconductivity of TiN is considered to be similar or superior to that of titanium and its alloys and therefore surface modification is necessary. In this study, TiN coating prepared through gas nitriding was partially oxidized by hydrothermal (HT) treatment and ozone (O{sub 3}) treatment in pure water to improve its osteoconductivity. The effects of HT treatment and O{sub 3} treatment on surface properties of TiN were investigated and the osteoconductivity after undergoing treatment was assessed in vitro using osteoblast evaluation. The results showed that the critical temperature for HT treatment was 100 °C since higher temperatures would impair the hardness of TiN coating. By contrast, O{sub 3} treatment was more effective in oxidizing TiN surfaces, improving its wettability while preserving its morphology and hardness. Osteoblast attachment, proliferation, alkaline phosphatase (ALP) expression and mineralization were improved on oxidized specimens, especially on O{sub 3} treated specimens, compared with untreated ones. These effects seemed to be consequences of partial oxidation, as well as improved hydrophilicity and surface decontamination. Finally, it was concluded that, partially oxidized TiN is a promising coating to be used for dental implant. - Highlights: • TiN coating surface was oxidized by hydrothermal or ozone treatment while preserving its hardness. • Improved wettability, decontamination and interstitial N promoted osteoblast responses. • Partial oxidation makes TiN a promising coating for dental implant with good osteoconductivity.

  4. Interaction of dimethylamine with clean and partially oxidized copper surfaces

    Science.gov (United States)

    Kelber, J. A.; Rogers, J. W.; Banse, B. A.; Koel, B. E.

    1990-05-01

    The interaction of dimethylamine (DMA) with partially oxidized polycrystalline copper [Cu(poly)] and clean and partially oxidized Cu(110) between 110 and 500 K has been examined using electron stimulated desorption (ESD), high resolution electron energy loss spectroscopy (HREELS) and temperature programmed desorption (TPD). ESD mass spectra of the DMA adsorbed on O/Cu(poly) between 112 and 230 K consistently display peaks at 44 amu [(CH 3) 2N] + and 46 amu [(CH 3) 2NH-H] +, but no significant parent peak at 45 amu [(CH 3) 2NH] +, even though this last feature is prominent in the gas-phase mass spectrum. OH - is not observed at temperatures below 184 K and the yield at higher temperatures is much less than that of O +. HREELS of DMA on clean and oxygen covered Cu(110) obtained at temperatures between 100 and 320 K show characteristic vibrational spectra for molecular DMA and no OH(a) vibrational modes. TPD results show that the desorption profiles of all the major peaks in the DMA mass spectrum follow that of the parent peak with no evidence for production of H 2O. The ESD, HREELS and TPD results all indicate that DMA is molecularly and reversibly adsorbed, with no significant formation of surface hydroxyl species. The results indicate that preferential adsorption of amines from amine/epoxy mixtures onto metal oxide surfaces could passivate the surface and prevent subsequent bonding to the epoxy resin.

  5. Oxidation of boron carbide at high temperatures

    International Nuclear Information System (INIS)

    Steinbrueck, Martin

    2005-01-01

    The oxidation kinetics of various types of boron carbides (pellets, powder) were investigated in the temperature range between 1073 and 1873 K. Oxidation rates were measured in transient and isothermal tests by means of mass spectrometric gas analysis. Oxidation of boron carbide is controlled by the formation of superficial liquid boron oxide and its loss due to the reaction with surplus steam to volatile boric acids and/or direct evaporation at temperatures above 1770 K. The overall reaction kinetics is paralinear. Linear oxidation kinetics established soon after the initiation of oxidation under the test conditions described in this report. Oxidation is strongly influenced by the thermohydraulic boundary conditions and in particular by the steam partial pressure and flow rate. On the other hand, the microstructure of the B 4 C samples has a limited influence on oxidation. Very low amounts of methane were produced in these tests

  6. Microstructure and High Temperature Oxidation Property of Fe-Cr-B Based Metal/Ceramic Composite Manufactured by Powder Injection Molding Process

    Science.gov (United States)

    Joo, Yeun-Ah; Kim, Young-Kyun; Yoon, Tae-Sik; Lee, Kee-Ahn

    2018-03-01

    This study investigated the microstructure and high temperature oxidation property of Fe-Cr-B metal/ceramic composite manufactured using powder injection molding process. Observations of initial microstructure showed a unique structure where α-Fe and (Cr, Fe)2B form a continuous three-dimensional network. High temperature oxidation tests were performed at 900, 1000 and 1100 °C, for 24 h, and the oxidation weight gain according to each temperature condition was 0.13, 0.84 and 6.4 mg/cm2, respectively. The oxidation results according to time at 900 and 1000 °C conditions represented parabolic curves, and at 1100 °C condition formed a rectilinear curve. Observation and phase analysis results of the oxides identified Cr2O3 and SiO2 at 900 and 1000 °C. In addition to Cr2O3 and SiO2, CrBO3 and FeCr2O4 formed due to phase decomposition of boride were identified at 1100 °C. Based on the findings above, this study suggested the high temperature oxidation mechanism of Fe-Cr-B metal/ceramic composite manufactured using powder injection molding, and the possibility of its application as a high temperature component material was also discussed.

  7. Growth and surface characterization of sputter-deposited molybdenum oxide thin films

    Energy Technology Data Exchange (ETDEWEB)

    Ramana, C.V. [Nanoscience and Surface Chemistry Laboratory, Department of Geological Sciences, University of Michigan, Ann Arbor, MI 48109 (United States)]. E-mail: ramanacv@umich.edu; Atuchin, V.V. [Laboratory of Optical Materials and Structures, Institute of Semiconductor Physics, SB RAS, Novosibirsk 630090 (Russian Federation); Kesler, V.G. [Technical Centre, Institute of Semiconductor Physics, SB RAS, Novosibirsk 630090 (Russian Federation); Kochubey, V.A. [Laboratory of Optical Materials and Structures, Institute of Semiconductor Physics, SB RAS, Novosibirsk 630090 (Russian Federation); Pokrovsky, L.D. [Laboratory of Optical Materials and Structures, Institute of Semiconductor Physics, SB RAS, Novosibirsk 630090 (Russian Federation); Shutthanandan, V. [Environmental Molecular Sciences Laboratory, Pacific Northwest National Laboratory, Richland, WA 99352 (United States); Becker, U. [Nanoscience and Surface Chemistry Laboratory, Department of Geological Sciences, University of Michigan, Ann Arbor, MI 48109 (United States); Ewing, R.C. [Nanoscience and Surface Chemistry Laboratory, Department of Geological Sciences, University of Michigan, Ann Arbor, MI 48109 (United States)

    2007-04-15

    Molybdenum oxide thin films were produced by magnetron sputtering using a molybdenum (Mo) target. The sputtering was performed in a reactive atmosphere of an argon-oxygen gas mixture under varying conditions of substrate temperature (T {sub s}) and oxygen partial pressure (pO{sub 2}). The effect of T {sub s} and pO{sub 2} on the growth and microstructure of molybdenum oxide films was examined in detail using reflection high-energy electron diffraction (RHEED), Rutherford backscattering spectrometry (RBS), energy-dispersive X-ray spectrometry (EDS), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM) measurements. The analyses indicate that the effect of T {sub s} and pO{sub 2} on the microstructure and phase of the grown molybdenum oxide thin films is remarkable. RHEED and RBS results indicate that the films grown at 445 deg. C under 62.3% O{sub 2} pressure were stoichiometric and polycrystalline MoO{sub 3}. Films grown at lower pO{sub 2} were non-stoichiometric MoO {sub x} films with the presence of secondary phase. The microstructure of the grown Mo oxide films is discussed and conditions were optimized to produce phase pure, stoichiometric, and highly textured polycrystalline MoO{sub 3} films.

  8. The influence of the texture and microstructure of a Zr-2.5Nb substrate upon the oxidation kinetics

    International Nuclear Information System (INIS)

    Lin, J.; Cao Xiaohui; Szpunar, J.A.

    2002-01-01

    The thin oxide layer growing on the zirconium alloy is dense and adherent and therefore is protective against further oxidation and hydrogen ingress, which is deleterious to zirconium pressure tube used in nuclear power stations because it facilitates formation of zirconium hydrides. Heat treatment and other surface modification methods were applied to zirconium alloys and the texture was investigated. Thermogravimetric analytic (TGA) was used for oxidation kinetics studies. The oxidation kinetics data show the variation of the oxidation rate due to the difference of texture and microstructure and the oxidation resistance is improved after the substrate is cold worked and heat treated. After cold work and heat treatment, the texture of substrate changes from (11-20)[1-100] to (11-23)[1-100]. (orig.)

  9. Microstructure evolution during pressureless sintering of bulk oxide ceramics

    Directory of Open Access Journals (Sweden)

    Karel Maca

    2009-06-01

    Full Text Available The author’s experience concerning the infl uence of the choice of different pressureless heating schedules on the fi nal microstructure of oxide ceramic materials is summarized in the paper. Alumina, ceria, strontium titanate, as well as tetragonal (3 mol% Y2O3 and cubic (8 mol% Y2O3 zirconia were cold isostatically pressed or injection moulded and pressureless sintered with different heating schedules – namely with Constant-Rate of Heating with different dwell temperatures (CRH, with Rate-Controlled Sintering (RCS and with Two-Step Sintering (TSS. It was examined whether some of these three sintering schedules, with the same fi nal density achieved, can lead to a decrease of the grain size of sintered ceramics. The results showed that only TSS (and only for selected materials brought significant decrease of the grain size.

  10. Microstructural evolution and deformation features in gas turbine blades operated in-service

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Fei [Key Laboratory of Liquid Structure and Heredity of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); Tong, Jinyan [National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083 (China); Feng, Qiang [National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083 (China); State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083 (China); Zhang, Jianxin [Key Laboratory of Liquid Structure and Heredity of Materials, Ministry of Education, Shandong University, Jinan 250061 (China)

    2015-01-05

    Highlights: • Gas turbine blades operated in-service have been investigated. • Two primary MC decomposition reactions take place during servicing. • Deformation features during servicing have been analyzed. - Abstract: The nickel based superalloy GH4037 is employed in gas turbine blades because of its high temperature strength and oxidation resistance. Microstructural evolution and deformation features in gas turbine blades after 1600 h service have been investigated by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM). The microstructure of blade changes according to complex and comprehensive temperature and stress fields applied on it. Microstructural observations show that minor carbide precipitates dispersedly precipitate in the matrix. Two MC decomposition reactions occur: MC + γ → M{sub 23}C{sub 6} + γ′ and MC + γ → M{sub 23}C{sub 6} + η. Blocky, closely spaced M{sub 23}C{sub 6} particles continuously distribute along grain boundaries. The main deformation features, such as slip bands, APB-coupled dislocation pairs, stacking faults bound by partial dislocations and deformation twinning, have also been analyzed in terms of fundamental deformation mechanisms and environmental effects.

  11. Selective Internal Oxidation and Severe Plastic Deformation of Multiphase Fe-Y Alloys

    Science.gov (United States)

    Kachur, Stephen J.

    hours, using a Rhines pack to maintain low oxygen partial pressures so that in situ oxidation could occur. Oxidation rates were accelerated when compared to traditional theory, and were not well described by a single parabolic rate constant throughout the duration of the experiment. While results agreed with Wagner theory that increased Y content should lead to decreased oxidation rates, this was attributed to a depletion of oxygen supply from the Rhines pack over time. Samples were also subjected to plastic deformation to observe how changes in microstructure influenced kinetics. Connectivity of the oxidizable phase was found to be critical to promoting the fastest rates of oxidation. Oxidation studies where then carried out using thermogravimetric analysis. A gaseous mixture of Ar-H2 was passed through a dew point control unit to vary oxidant partial pressure between 10-25 and 10-20 atm. Flow rate of the gas parallel to the sample surface was also altered. Canonical correlation analysis was then used to analyze and simplify the relationships between input and output variables. This analysis pointed to the importance of quantifying the relationship between the size of formed oxides and changes in oxidation kinetics over time. Where sustained parabolic kinetics were observed, oxides were small throughout the depth of internal oxidation. The effects of oxide size on penetration depth were then numerically modeled and incorporated into existing oxidation theory to show that the observed kinetics could be qualitatively described. After oxidation experiments, severe plastic deformation was applied to both oxidized and unoxidized microstructures using equal channel angular pressing. By manipulating pressing temperature and the number of passes, microstructures were altered to varying degrees of success. No oxide refinement was observed, but increasing temperatures and number of passes allowed for even dispersion of both oxides and Fe17Y2 intermetallic.

  12. Facile one-step template-free synthesis of uniform hollow microstructures of cryptomelane-type manganese oxide K-OMS-2.

    Science.gov (United States)

    Galindo, Hugo M; Carvajal, Yadira; Njagi, Eric; Ristau, Roger A; Suib, Steven L

    2010-08-17

    Hollow microstructures of cryptomelane-type manganese oxide were produced in a template-free one-step process based on the fine-tuning of the oxidation rate of manganese species during the synthesis. The tuning of the reaction rate brought about by a mixture of the oxidants oxone and potassium nitrate becomes apparent from the gradual physical changes taking place in the reaction medium at early times of the synthesis. The successful synthesis of the hollow uniform structures could be performed in the ranges 120-160 degrees C and 8.2-10.7 for temperature and mass ratio oxone/potassium nitrate, respectively. Independent of the conditions of the synthesis, all of the complex microstructures showed the same pattern for the array of very long nanofibers in which some of these elongated around the surface confining the cavity and the other fibers grew normal to the surface created by the previous arrangement. A mechanism based on the heterogeneous nucleation of the cryptomelane phase on the surface of an amorphous precursor and the growth of the nanoscale fibers by processes such as dissolution-crystallization and lateral attachment of primary nanocrystalline fibers is proposed to explain the formation of the hollow structures.

  13. EBSD Analysis of Deformed and Partially Recrystallized Microstructures in ECAE-Processed Copper

    DEFF Research Database (Denmark)

    Mishin, Oleg; Bowen, Jacob R.; Godfrey, A.

    2012-01-01

    The deformed microstructure and recrystallization behavior of copper samples processed using equal channel angular extrusion (ECAE) have been investigated. The heavily deformed microstructure was found to be non-uniform through the sample thickness and to vary in a manner consistent with the non...

  14. Kinetics of the partial oxidation of methanol over a Fe-Mo catalyst

    NARCIS (Netherlands)

    Deshmukh, S.A.R.K.; Sint Annaland, van M.; Kuipers, J.A.M.

    2005-01-01

    The intrinsic steady-state kinetics of the partial oxidation of methanol to formaldehyde over a commercial Fe-Mo catalyst has been studied experimentally in a differentially operated reactor at temperatures of 230–260 °C, over a wide range of methanol and oxygen concentrations. The principal

  15. Kinetics of the partial oxidation of methanol over a Fe-Mo catalyst

    NARCIS (Netherlands)

    Deshmukh, S.A.R.K.; van Sint Annaland, M.; Kuipers, J.A.M.

    2005-01-01

    The intrinsic steady-state kinetics of the partial oxidation of methanol to formaldehyde over a commercial Fe-Mo catalyst has been studied experimentally in a differentially operated reactor at temperatures of 230¿260 °C, over a wide range of methanol and oxygen concentrations. The principal

  16. Partial oxidation of methane over Ni/Mg/Al/La mixed oxides prepared from layered double hydrotalcites

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Jun [Low Carbon Energy Conversion Center, Shanghai Advanced Research Institute, Chinese Academy of Sciences, Shanghai 201203 (China); State Key Laboratory of Coal Conversion, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001, Shanxi (China); Graduate University of Chinese Academy of Sciences, Beijing 100049 (China); Zhao, Ning; Wei, Wei [State Key Laboratory of Coal Conversion, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001, Shanxi (China); Sun, Yuhan [Low Carbon Energy Conversion Center, Shanghai Advanced Research Institute, Chinese Academy of Sciences, Shanghai 201203 (China); State Key Laboratory of Coal Conversion, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001, Shanxi (China)

    2010-11-15

    A series of Ni/Mg/Al/La mixed oxides prepared by thermal decomposition of layered double hydrotalcites (HT) were characterized by XRD, ICP, EXAFS, TGA, TPR-H{sub 2}, SEM, and N{sub 2} adsorption/desorption technique. The results revealed the formation of periclase-type catalysts with mesoporous structure, and the addition of La{sup 3+} lowered the phase crystallization with the formation of small oxide particles. Such catalysts had both high activities and stabilities toward partial oxidation of methane (POM). The catalyst containing 6.5 mol.% La{sup 3+} showed the highest performance at 1053 K with CH{sub 4} conversion of 99%, CO selectivity of 93% and H{sub 2} selectivity of 96%, which could be attributed to the presence of highly dispersed nickel and then the resistance to coke formation due to the promotion effect of lanthanum. (author)

  17. Comparison of partial and full nitrification processes applied for treating high-strength nitrogen wastewaters: microbial ecology through nitrous oxide production.

    Science.gov (United States)

    Ahn, Joon Ho; Kwan, Tiffany; Chandran, Kartik

    2011-04-01

    The goal of this study was to compare the microbial ecology, gene expression, biokinetics, and N2O emissions from a lab-scale bioreactor operated sequentially in full-nitrification and partial-nitrification modes. Based on sequencing of 16S rRNA and ammonia monooxygenase subunit A (amoA) genes, ammonia oxidizing bacteria (AOB) populations during full- and partial-nitrification modes were distinct from one another. The concentrations of AOB (XAOB) and their respiration rates during full- and partial-nitrification modes were statistically similar, whereas the concentrations of nitrite oxidizing bacteria (XNOB) and their respiration rates declined significantly after the switch from full- to partial-nitrification. The transition from full-nitrification to partial nitrification resulted in a protracted transient spike of nitrous oxide (N2O) and nitric oxide (NO) emissions, which later stabilized. The trends in N2O and NO emissions correlated well with trends in the expression of nirK and norB genes that code for the production of these gases in AOB. Both the transient and stabilized N2O and NO emissions during partial nitrification were statistically higher than those during steady-state full-nitrification. Based on these results, partial nitrification strategies for biological nitrogen removal, although attractive for their reduced operating costs and energy demand, may need to be optimized against the higher carbon foot-print attributed to their N2O emissions.

  18. Microstructure and local texture of partially recrystallized titanium sheet

    International Nuclear Information System (INIS)

    Zaefferer, S.; Schwarzer, R.A.

    1993-01-01

    The microstructure of TiAl6V4 sheet was investigated by transmission electron microscopy. Two types of microstructure were found: regions with a recrystallized and regions with a deformed structure. They could be distinguished from each other by grain size and shape, by the dislocation density and local texture. The orientations of individual grains were measured by on-line interpretation of Kikuchi patterns with a TEM. The results were represented on inverse pole figures. The deformed structure showed a strong preferred orientation (11 anti 20)[10 anti 10], while the texture of the recrystallized areas was substantially weaker containing other preferred orientations. The global texture of the sample was investigated by measuring pole figures with an x-ray texture goniometer. The ODF as well as inverse pole figures were calculated and compared to the TEM pole figures. (orig.)

  19. Partial oxidation of n-hexadecane through decomposition of hydrogen peroxide in supercritical water

    KAUST Repository

    Alshammari, Y.M.

    2015-01-01

    © 2014 The Institution of Chemical Engineers. This work reports the experimental analysis of partial oxidation of n-hexadecane under supercritical water conditions. A novel reactor flow system was developed which allows for total decomposition of hydrogen peroxide in a separate reactor followed partial oxidation of n-hexadecane in a gasification reactor instead of having both reactions in one reactor. The kinetics of hydrothermal decomposition of hydrogen peroxide was studied in order to confirm its full conversion into water and oxygen under the desired partial oxidation conditions, and the kinetic data were found in a good agreement with previously reported literature. The gas yield and gasification efficiency were investigated under different operating parameters. Furthermore, the profile of C-C/C=C ratio was studied which showed the favourable conditions for maximising yields of n-alkanes via hydrogenation of their corresponding 1-alkenes. Enhanced hydrogenation of 1-alkenes was observed at higher O/C ratios and higher residence times, shown by the increase in the C-C/C=C ratio to more than unity, while increasing the temperature has shown much less effect on the C-C/C=C ratio at the current experimental conditions. In addition, GC-MS analysis of liquid samples revealed the formation of heavy oxygenated compounds which may suggest a new addition reaction to account for their formation under the current experimental conditions. Results show new promising routes for hydrogen production with in situ hydrogenation of heavy hydrocarbons in a supercritical water reactor.

  20. Prospective use of the 3D printing technology for the microstructural engineering of Solid Oxide Fuel Cell components

    Energy Technology Data Exchange (ETDEWEB)

    Hernandez-Rodriguez, E. M.; Acosta-Mora, P.; Mendez-Ramos, J.; Borges Chinea, E.; Esparza Ferrera, P.; Canales-Vazquez, J.; Nunez, P.; Ruiz-Morales, J.

    2014-07-01

    A cost-effective micro-manufacturing process to accurately build 3D microstructures for their prospective use in the fabrication of Solid Oxide Fuel Cells components has been tested. The 3D printing method, based on the stereo lithography, allows solidifying layer by layer a dispersion of ceramic material in a liquid photosensitive organic monomer. A simple projector, a computer-controlled z-stage and a few PowerPoint slides may be used for the fabrication of a wide range of complex 3D microstructures in few minutes. In this work, 3D ceramic microstructures based on the yttria-stabilized zirconia (YSZ) were successfully fabricated. The micro structured ceramic components produced were stable after sintering at 1400 degree centigrade for 4 h. Impedance measurements show that the fabrication process does not have any detrimental effect on the electrical properties of the structured material. (Author)

  1. Prospective use of the 3D printing technology for the microstructural engineering of Solid Oxide Fuel Cell components

    International Nuclear Information System (INIS)

    Hernandez-Rodriguez, E. M.; Acosta-Mora, P.; Mendez-Ramos, J.; Borges Chinea, E.; Esparza Ferrera, P.; Canales-Vazquez, J.; Nunez, P.; Ruiz-Morales, J.

    2014-01-01

    A cost-effective micro-manufacturing process to accurately build 3D microstructures for their prospective use in the fabrication of Solid Oxide Fuel Cells components has been tested. The 3D printing method, based on the stereo lithography, allows solidifying layer by layer a dispersion of ceramic material in a liquid photosensitive organic monomer. A simple projector, a computer-controlled z-stage and a few PowerPoint slides may be used for the fabrication of a wide range of complex 3D microstructures in few minutes. In this work, 3D ceramic microstructures based on the yttria-stabilized zirconia (YSZ) were successfully fabricated. The micro structured ceramic components produced were stable after sintering at 1400 degree centigrade for 4 h. Impedance measurements show that the fabrication process does not have any detrimental effect on the electrical properties of the structured material. (Author)

  2. Microstructure and emission ability of rare earth oxides doped molybdenum cathodes

    International Nuclear Information System (INIS)

    Yang Jiancan; Nie Zuoren; Wang Yiman

    2003-01-01

    We adopted high-resolution transmission electron microscopy (TEM) and scanning electron microscopy (SAM) to observe and analyze the microstructure of rare earth oxide (La 2 O 3 , Sc 2 O 3 ) doped molybdenum cathodes. The results show that there are many nanometer particles in the molybdenum matrix besides some sub-micrometer particles in the crystal interfaces. All these particles are rare earth oxides as determined through calculating the electron diffraction pattern. Then we determined the electron work function and the zero-field emission current of molybdenum cathodes by the electron emission measurement. To correlate the emission data with surface composition, we use Auger electron spectroscopy (AES) to analyze the elements on the activated cathode surface and their depth profiles. We found that there were about 20 nm thick layers on an activated cathode surface, which have a high content of rare earth elements. We also use AES to analyze the elements diffusion to the cathode surface from cathode body during heating up to its operating temperature to find out which element positively affects the electron emission

  3. Microstructure of titanium oxide films synthesized by ion beam dynamic mixing

    International Nuclear Information System (INIS)

    Makino, Y.; Setsuhara, Y.; Miyake, S.

    1994-01-01

    The microstructure of titanium oxide films synthesized by the ion beam dynamic mixing (IBDM) method is investigated by glancing angle X-ray diffraction and multi-reflectance FT-IR methods. Titanium oxide films are identified as rutile phases having different degrees of (110) orientation. The IBDM rutile phase with a standard crystalline state is produced by controlling the ratio of the intensities between the (110) and (101) peaks of the rutile, I(110)/I(101), so as to approach the ratio to the value (=2.0) of ASTM standard rutile. The crystallite size of the rutile phase increases with increasing ratio of intensities of the two XRD peaks, I(110)/I(101). The increase of the crystallite size is suggested to be attributed to the increase of oxygen ion energy per Ti atom. From the dependence of the IR absorption near 500 cm -1 upon I(110)/I(101), it is indicated that the Ti-O bond strength is delicately affected by the degree of (110) orientation of the IBDM rultile phase. ((orig.))

  4. Oxidation behavior of V-Cr-Ti alloys in low-partial-pressure oxygen environments

    International Nuclear Information System (INIS)

    Natesan, K.; Uz, M.

    1998-01-01

    A test program is in progress at Argonne National Laboratory to evaluate the effect of pO 2 in the exposure environment on oxygen uptake, scaling kinetics, and scale microstructure in V-Cr-Ti alloys. The data indicate that the oxidation process follows parabolic kinetics in all of the environments used in the present study. From the weight change data, parabolic rate constants were evaluated as a function of temperature and exposure environment. The temperature dependence of the parabolic rate constants was described by an Arrhenius relationship. Activation energy for the oxidation process was fairly constant in the oxygen pressure range of 1 x 10 -6 to 1 x 10 -1 torr for both the alloys. The activation energy for oxidation in air was significantly lower than in low-pO 2 environments, and for oxidation in pure O 2 at 760 torr was much lower than in low-pO 2 environments. X-ray diffraction analysis of the specimens showed that VO 2 was the dominant phase in low-pO 2 environments, while V 2 O 5 was dominant in air and in pure oxygen at 76f0 torr

  5. Microgravity Processing of Oxide Superconductors

    Science.gov (United States)

    Hofmeister, William H.; Bayuzick, Robert J.; Vlasse, Marcus; McCallum, William; Peters, Palmer (Technical Monitor)

    2000-01-01

    The primary goal is to understand the microstructures which develop under the nonequilibrium solidification conditions achieved by melt processing in copper oxide superconductor systems. More specifically, to define the liquidus at the Y- 1:2:3 composition, the Nd-1:2:3 composition, and several intermediate partial substitution points between pure Y-1:2:3 and Nd-1:2:3. A secondary goal has been to understand resultant solidification morphologies and pathways under a variety of experimental conditions and to use this knowledge to better characterize solidification phenomena in these systems.

  6. Partial oxidation of landfill leachate in supercritical water: Optimization by response surface methodology

    International Nuclear Information System (INIS)

    Gong, Yanmeng; Wang, Shuzhong; Xu, Haidong; Guo, Yang; Tang, Xingying

    2015-01-01

    Highlights: • Partial oxidation of landfill leachate in supercritical water was investigated. • The process was optimized by Box–Behnken design and response surface methodology. • GY H2 , TRE and CR could exhibit up to 14.32 mmol·gTOC −1 , 82.54% and 94.56%. • Small amounts of oxidant can decrease the generation of tar and char. - Abstract: To achieve the maximum H 2 yield (GY H2 ), TOC removal rate (TRE) and carbon recovery rate (CR), response surface methodology was applied to optimize the process parameters for supercritical water partial oxidation (SWPO) of landfill leachate in a batch reactor. Quadratic polynomial models for GY H2 , CR and TRE were established with Box–Behnken design. GY H2 , CR and TRE reached up to 14.32 mmol·gTOC −1 , 82.54% and 94.56% under optimum conditions, respectively. TRE was invariably above 91.87%. In contrast, TC removal rate (TR) only changed from 8.76% to 32.98%. Furthermore, carbonate and bicarbonate were the most abundant carbonaceous substances in product, whereas CO 2 and H 2 were the most abundant gaseous products. As a product of nitrogen-containing organics, NH 3 has an important effect on gas composition. The carbon balance cannot be reached duo to the formation of tar and char. CR increased with the increase of temperature and oxidation coefficient

  7. Microstructural characterization of thermal barrier coating on Inconel 617 after high temperature oxidation

    Directory of Open Access Journals (Sweden)

    Mohammadreza Daroonparvar

    2013-06-01

    Full Text Available A turbine blade was protected against high temperature corrosion and oxidation by thermal barrier coatings (TBCsusing atmospheric plasma spraying technique (APS on a Ni-based superalloy (Inconel 617. The coatings (NiCr6AlY/ YSZ and NiCr10AlY/YSZ consist of laminar structure with substantial interconnected porosity transferred oxygen from Yittria stabilized Zirconia (YSZ layer toward the bond coat (NiCrAlY. Hence, a thermally grown oxide layer (TGO was formed on the metallic bond coat and internal oxidation of the bond coat occurred during oxidation. The TBC systems were oxidized in a normal electrically heated furnace at 1150 °C for 18, 22, 26, 32 and 40h.Microstructural characterization of coatings demonstrated that the growth of the TGO layer on the nickel alloy with 6wt. % Al is more rapid than TGO with 10wt. % Al. In addition, many micro-cracks were observed at the interface of NiCr6AlY/YSZ. X-ray diffraction analysis (XRD showed the existence of detrimental oxides such as NiCr2O4, NiCrO3 and NiCrO4 in the bond coat containing 6wt. % Al, accompanied by rapid volume expansion causing the destruction of TBC. In contrast, in the bond coat with 10wt. % Al, NiO, Al2O3and Cr2O3 oxides were formed while very low volume expansion occurred. The oxygen could not penetrate into the TGO layer of bond coat with 10 wt. % Al during high temperature oxidation and the detrimental oxides were not extensively formed within the bond coat as more oxygen was needed. The YSZ with higher Al content showed higher oxidation resistance.

  8. Effect of calcium on the microstructure and corrosion behavior of microarc oxidized Mg-xCa alloys.

    Science.gov (United States)

    Pan, Yaokun; Chen, Chuanzhong; Feng, Rui; Cui, Hongwei; Gong, Benkui; Zheng, Tingting; Ji, Yarou

    2018-01-16

    Magnesium alloys are potential biodegradable implants for biomedical applications, and calcium (Ca) is one kind of ideal element being examined for magnesium alloys and biodegradable ceramic coatings owing to its biocompatibility and mechanical suitability. In this study, microarc oxidation (MAO) coatings were prepared on Mg-xCa alloys to study the effect of Ca on the microstructure and corrosion resistance of Mg-xCa alloys and their surface MAO coatings. The electrochemical corrosion behavior was investigated using an electrochemical workstation, and the degradability and bioactivity were evaluated by soaking tests in simulated body fluid (SBF) solutions. The corrosion products were characterized by scanning electron microscopy, x-ray diffractometry, and Fourier transform infrared spectrometry. The effects of Ca on the alloy phase composition, microstructure, MAO coating formation mechanism, and corrosion behavior were investigated. Results showed that the Mg-0.82Ca alloy and MAO-coated Mg-0.82Ca exhibited the highest corrosion resistance. The number and distribution of Mg 2 Ca phases can be controlled by adjusting the Ca content in the Mg-xCa alloys. The proper amount of Ca in magnesium alloy was about 0.5-0.8 wt. %. The pore size, surface roughness, and corrosion behavior of microarc oxidized Mg-xCa samples can be controlled by the number and distribution of the Mg 2 Ca phase. The corrosion behaviors of microarc oxidized Mg-Ca in SBF solutions were discussed.

  9. Influence of Al-Si alloy microstructure on the corrosion resistance of coatings formed by the microarc oxidation method

    Directory of Open Access Journals (Sweden)

    Dudareva Natalia.Y.

    2017-01-01

    Full Text Available The impact of the high-silicon aluminum alloy initial microstructure on the quality of the coating formed by microarc oxidation (MAO has been studied. The MAO treatment is applied to AK12D samples in the initial coarse-grained state and after high pressure torsion. The following coating properties are studied: thickness, microhardness, porosity and corrosion resistance. It is established that the MAO layers properties depend on the base microstructure much. High pressure torsion applied to AK12D samples before MAO results in increase of the coating thickness by ∼ 2 times. The microhardness of coatings reduces and their corrosion resistance degrades by ∼ 10 times.

  10. Microstructured extremely thin absorber solar cells

    DEFF Research Database (Denmark)

    Biancardo, Matteo; Krebs, Frederik C

    2007-01-01

    In this paper we present the realization of extremely thin absorber (ETA) solar cells employing conductive glass substrates functionalized with TiO2 microstructures produced by embossing. Nanocrystalline or compact TiO2 films on Indium doped tin oxide (ITO) glass substrates were embossed by press......In this paper we present the realization of extremely thin absorber (ETA) solar cells employing conductive glass substrates functionalized with TiO2 microstructures produced by embossing. Nanocrystalline or compact TiO2 films on Indium doped tin oxide (ITO) glass substrates were embossed...

  11. Texture and microstructure analysis of epitaxial oxide layers prepared on textured Ni-12wt%Cr tapes

    Energy Technology Data Exchange (ETDEWEB)

    Huehne, R; Kursumovic, A; Tomov, R I; Glowacki, B A [Department of Materials Science and IRC in Superconductivity, University of Cambridge, Pembroke Street, Cambridge, CB2 3QZ (United Kingdom); Holzapfel, B [Institut fuer Festkoerper- und Werkstoffforschung, Helmholtzstrasse 20, 01069 Dresden (Germany); Evetts, J E [Department of Materials Science and IRC in Superconductivity, University of Cambridge, Pembroke Street, Cambridge, CB2 3QZ (United Kingdom)

    2003-05-07

    Oxide layers for the preparation of YBa{sub 2}Cu{sub 3}O{sub 7-x} coated conductors were grown on highly textured Ni-12wt%Cr tapes in pure oxygen using surface oxidation epitaxy at temperatures between 1000 deg. C and 1300 deg. C. Microstructural investigations revealed a layered oxide structure. The upper layer consists mainly of dense cube textured NiO. This is followed by a porous layer containing NiO and NiCr{sub 2}O{sub 4} particles. A detailed texture analysis showed a cube-on-cube relationship of the NiCr{sub 2}O{sub 4} spinel to the metal substrate. Untextured Cr{sub 2}O{sub 3} particles in a nickel matrix were found in a third layer arising from internal oxidation of the alloy. A high surface roughness and mechanical instability of the oxide were observed, depending on oxidation temperature and film thickness. However, mechanically stable oxide layers have been prepared using an additional annealing step in a protective atmosphere. Additionally, mechanical polishing or a second buffer layer, which grows with a higher smoothness, may be applied to reduce the surface roughness for coated conductor applications.

  12. Modeling of termokinetic oscillations at partial oxidation of methane

    Science.gov (United States)

    Arutyunov, A. V.; Belyaev, A. A.; Inovenkov, I. N.; Nefedov, V. V.

    2017-12-01

    Partial oxidation of natural gas at moderate temperatures below 1500 K has significant interest for a number of industrial applications. But such processes can proceed at different unstable regimes including oscillating modes. Nonlinear phenomena at partial oxidation of methane were observed at different conditions. The investigation of the complex nonlinear system of equations that describes this process is a real method to insure its stability at industrial conditions and, at the same time, is an effective tool for its further enhancement. Numerical analysis of methane oxidation kinetics in the continuous stirred-tank reactor, with the use of detailed kinetic model has shown the possibility of the appearance of oscillating modes in the appropriate range of reaction parameters that characterize the composition, pressure, reagents flow, thermophysical features of the system, and geometry of the reactor. The appearance of oscillating modes is connected both with the reaction kinetics, heat release and sink and reagents introduction and removing. At that, oscillations appear only at a limited range of parameters, but can be accompanied by significant change in the yield of products. We have determined the range of initial temperature and pressure at which oscillations can be observed, if all other parameters remained fixed. The boundaries of existence of oscillations on the phase plane were calculated. It was shown that depending on the position inside the oscillation region the oscillations have different frequency and amplitude. It was reviled the role of heat exchange with the environment: at the absence of heat exchange the oscillating modes are impossible. In the vicinity of the boundary of phase range, where oscillations exist, significant change of concentration of some products were observed, for example, that of CO2, which in this case one of the principal products is. At that, insignificant increase in pressure not only change the character of CO2 behaving

  13. Role of Microstructure on the Performance of UHTCs

    Science.gov (United States)

    Johnson, Sylvia M.; Gasch, Matthew J.; Lawson, John W.; Gusman, Michael I.; Stackpoole, Mairead

    2010-01-01

    We have investigated a number of methods to control microstructure. We have routes to form: a) in situ "composites" b) Very fine microstructures. Arcjet testing and other characterization of monolithic materials. Control oxidation through microstructure and composition. Beginning to incorporate these materials as matrices for composites. Modeling effort to facilitate material design and characterization.

  14. Rhodium and Hafnium Influence on the Microstructure, Phase Composition, and Oxidation Resistance of Aluminide Coatings

    OpenAIRE

    Maryana Zagula-Yavorska; Małgorzata Wierzbińska; Jan Sieniawski

    2017-01-01

    A 0.5 μm thick layer of rhodium was deposited on the CMSX 4 superalloy by the electroplating method. The rhodium-coated superalloy was hafnized and aluminized or only aluminized using the Chemical vapour deposition method. A comparison was made of the microstructure, phase composition, and oxidation resistance of three aluminide coatings: nonmodified (a), rhodium-modified (b), and rhodium- and hafnium-modified (c). All three coatings consisted of two layers: the additive layer and the interdi...

  15. Microstructural characterization of Y2O3 ODS-Fe-Cr model alloys

    International Nuclear Information System (INIS)

    Castro, V. de; Leguey, T.; Munoz, A.; Monge, M.A.; Pareja, R.; Marquis, E.A.; Lozano-Perez, S.; Jenkins, M.L.

    2009-01-01

    Two Fe-12 wt% Cr alloys, one containing 0.4 wt% Y 2 O 3 and the other Y 2 O 3 -free, have been produced by mechanical alloying followed by hot isostatic pressing. These oxide dispersion strengthened and reference alloys were characterized both in the as-HIPed state and after tempering by transmission electron microscopy and atom-probe tomography. The as-HIPed alloys exhibited the characteristic microstructure of lath martensite and contained a high density of dislocations. Small voids with sizes 3 C and M 23 C 6 carbides (M = Cr, Fe) probably as a result of C ingress during milling. After tempering at 1023 K for 4 h the microstructures had partially recovered. In the recovered regions, martensite laths were replaced by equiaxed grains in which M 23 C 6 carbides decorated the grain boundaries. In the ODS alloy nanoparticles containing Y were commonly observed within grains, although they were also present at grain boundaries and adjacent to large carbides.

  16. High temperature oxidation in the context of life assessment and microstructural degradation of weldments of 2.25Cr-1Mo steel

    International Nuclear Information System (INIS)

    Singh Raman, R.K.; Muddle, B.C.

    2002-01-01

    The prevalence of in-service failures in the welds of chromium-molybdenum ferritic steels causes great concern in steam generating/handling systems of power plants, and components of petroleum/petrochemical industries. This paper is a review of the non-uniform scaling behaviour across microstructural gradients in weldments of pressure vessel steels in order to develop a global model for life-assessment by relating oxide scale thickness with time-temperature history of in-service components. The paper also investigates gaseous corrosion-assisted deterioration of the weldment microstructure

  17. Thermocyclic behaviour of microstructurally modified EB-PVD thermal barrier coatings

    International Nuclear Information System (INIS)

    Schulz, U.; Fritscher, K.; Raetzer-Scheibe, H.-J.; Kaysser, W.A.; Peters, M.

    1997-01-01

    This paper focuses on the combined effects of substrate temperature and rotation during electron-beam physical vapor deposition (EB-PVD) on the columnar microstructure of yttria partially stabilized zirconia (YPSZ) thermal barrier coatings. Diameter and degree of ordering of the columns and the density of the coatings are sensitive to the processing parameters. Results are discussed in the frame of common structural zone models for PVD processes. The models are extended to consider the rotational effect. EB-PVD YPSZ TBCs of different column diameters were deposited on top of an EB-PVD NiCoCrAlY bondcoat on IN 100 superalloy test bars. The performance of the TBCs was investigated in a cyclic oxidation furnace test rig between 1100 C and 130 C and in a burner rig under hot gas corrosion conditions at a maximum temperature of 900 C. Results showed a correlation between cyclic lifetime and the various microstructures of the TBCs. Samples having a non-regular arrangement of columns performed best in both tests. (orig.)

  18. Partial oxidation of landfill leachate in supercritical water: Optimization by response surface methodology

    Energy Technology Data Exchange (ETDEWEB)

    Gong, Yanmeng; Wang, Shuzhong; Xu, Haidong; Guo, Yang; Tang, Xingying

    2015-09-15

    Highlights: • Partial oxidation of landfill leachate in supercritical water was investigated. • The process was optimized by Box–Behnken design and response surface methodology. • GY{sub H2}, TRE and CR could exhibit up to 14.32 mmol·gTOC{sup −1}, 82.54% and 94.56%. • Small amounts of oxidant can decrease the generation of tar and char. - Abstract: To achieve the maximum H{sub 2} yield (GY{sub H2}), TOC removal rate (TRE) and carbon recovery rate (CR), response surface methodology was applied to optimize the process parameters for supercritical water partial oxidation (SWPO) of landfill leachate in a batch reactor. Quadratic polynomial models for GY{sub H2}, CR and TRE were established with Box–Behnken design. GY{sub H2}, CR and TRE reached up to 14.32 mmol·gTOC{sup −1}, 82.54% and 94.56% under optimum conditions, respectively. TRE was invariably above 91.87%. In contrast, TC removal rate (TR) only changed from 8.76% to 32.98%. Furthermore, carbonate and bicarbonate were the most abundant carbonaceous substances in product, whereas CO{sub 2} and H{sub 2} were the most abundant gaseous products. As a product of nitrogen-containing organics, NH{sub 3} has an important effect on gas composition. The carbon balance cannot be reached duo to the formation of tar and char. CR increased with the increase of temperature and oxidation coefficient.

  19. Partial oxidation of municipal sludge with activited carbon catalyst in supercritical water

    International Nuclear Information System (INIS)

    Guo Yang; Wang Shuzhong; Gong Yanmeng; Xu Donghai; Tang Xingying; Ma Honghe

    2010-01-01

    The partial oxidation (POX) characteristics of municipal sludge in supercritical water (SCW) were investigated by using batch reactor. Effects of reaction parameters such as oxidant equivalent ratio (OER), reaction time and temperature were investigated. Activated carbon (AC) could effectively improve the mole fraction of H 2 in gas product at low OER. However, high OER (greater than 0.3) not only led to the combustion reaction of CO and H 2 , but also caused corrosion of reactor inner wall. Hydrogenation and polymerization of the intermediate products are possible reasons for the relative low COD removal rate in our tests. Metal oxide leached from the reactor inner wall and the main components of the granular sludge were deposited in the AC catalyst. Reaction time had more significant effect on BET surface area of AC than OER had. Long reaction time led to the methanation reaction following hydrolysis and oxidation reaction of AC in SCW in the presence of oxygen. Correspondingly, the possible reaction mechanisms were proposed.

  20. Synthesis and Charaterization of Magensium Oxide Mesoporous Microstructures Using Pluronic F127

    Directory of Open Access Journals (Sweden)

    A. Tadjarodi

    2012-09-01

    Full Text Available Mesoporous  MgO  microstructures  were  synthesized  using magnesium  acetate  tetrahydrate,  ammonium  oxalate  monohydrate and  Pluronic  F127  via  heating  at  40  °C  for  24  h  and  subsequent calcination. The mesoporous structure of magnesium oxide with the specific  surface  area  of  47m2 /g,  pore  volume  0.30  cm3 /g  and  the average pore size 24 nm is produced. According to XRD studies, the diffraction peaks of  the product pattern can be  indexed  to  the cubic structure magnesium oxide with  the  lattice parameter of a = 4.22 Å and  showing  no  impurities.  The  product  was  characterized  by Fourier  transform  infrared  spectroscopy,  X-ray  powder  diffraction analysis,  N2  adsorption-desorption  and  Scanning  electron microscopy.

  1. The influence of partial oxidation mechanisms on tar destruction in TwoStage biomass gasification

    DEFF Research Database (Denmark)

    Ahrenfeldt, Jesper; Egsgaard, Helge; Stelte, Wolfgang

    2013-01-01

    adsorption and determined by stable isotope dilution analysis. The results have shown that partial oxidation reduces and converts primary tars into low molecular weight, polycyclic aromatic hydrocarbons (PAHs), primarily naphthalene. At temperatures above 950°C practically all phenol is converted...

  2. Oxygen partial pressure: a key to alloying and discovery in metal oxide--metal eutectic systems

    International Nuclear Information System (INIS)

    Holder, J.D.; Clark, G.W.; Oliver, B.F.

    1978-01-01

    Control of oxygen partial pressure is essential in the directional solidification of oxide--metal eutectic composites by techniques involving gas-solid and gas-liquid interactions. The existence of end components in the eutectic composite is Po 2 sensitive as are melt stoichiometry, solid phase compositions, and vapor losses due to oxidation-volatilization. Simple criteria are postulated which can aid the experimentalist in selecting the proper gas mixture for oxide--metal eutectic composite growth. The Cr 2 O 3 --Mo--Cr systems was used to verify certain aspects of the proposed criteria

  3. Effet des additions sur la microstructure et le comportement ...

    African Journals Online (AJOL)

    the microstructure, thermal fatigue and tribological tests of the NiAl coating, obtained by atmospheric plasma ...... Mechanisms of oxidation and its role in microstructural evolution of ... protective coatings, Surface and Coatings Technology, Vol.

  4. Partial oxidation process for producing a stream of hot purified gas

    Science.gov (United States)

    Leininger, T.F.; Robin, A.M.; Wolfenbarger, J.K.; Suggitt, R.M.

    1995-03-28

    A partial oxidation process is described for the production of a stream of hot clean gas substantially free from particulate matter, ammonia, alkali metal compounds, halides and sulfur-containing gas for use as synthesis gas, reducing gas, or fuel gas. A hydrocarbonaceous fuel comprising a solid carbonaceous fuel with or without liquid hydrocarbonaceous fuel or gaseous hydrocarbon fuel, wherein said hydrocarbonaceous fuel contains halides, alkali metal compounds, sulfur, nitrogen and inorganic ash containing components, is reacted in a gasifier by partial oxidation to produce a hot raw gas stream comprising H{sub 2}, CO, CO{sub 2}, H{sub 2}O, CH{sub 4}, NH{sub 3}, HCl, HF, H{sub 2}S, COS, N{sub 2}, Ar, particulate matter, vapor phase alkali metal compounds, and molten slag. The hot raw gas stream from the gasifier is split into two streams which are separately deslagged, cleaned and recombined. Ammonia in the gas mixture is catalytically disproportionated into N{sub 2} and H{sub 2}. The ammonia-free gas stream is then cooled and halides in the gas stream are reacted with a supplementary alkali metal compound to remove HCl and HF. Alkali metal halides, vaporized alkali metal compounds and residual fine particulate matter are removed from the gas stream by further cooling and filtering. The sulfur-containing gases in the process gas stream are then reacted at high temperature with a regenerable sulfur-reactive mixed metal oxide sulfur sorbent material to produce a sulfided sorbent material which is then separated from the hot clean purified gas stream having a temperature of at least 1000 F. 1 figure.

  5. Thermodynamic Study on the Catalytic Partial Oxidation of Methane to Syngas

    Institute of Scientific and Technical Information of China (English)

    XUJian; WEIWeisheng; 等

    2002-01-01

    The catalytic partial oxidation of methane to syngas (CO+H2) has been simulated thermodynamically with the advanced process simulator PRO/Ⅱ. The influences of temperature,pressure,CH4/O2 ratio and steam addition in feed gas on the conversion of CH4 selectively to syngas and heat duty required were investigated, and their effects on carbon formation were also discussed. The simulation results were in good agreement with the literature data taken from a spouted bed reactor.

  6. Microstructural evolution of ferritic steel powder during mechanical alloying with iron oxide

    Energy Technology Data Exchange (ETDEWEB)

    Wen, Yuren; Liu, Yong; Liu, Donghua; Tang, Bei [Central South Univ., State Key Lab. of Powder Metallurgy, Changsha (China); Liu, C.T. [The Hong Kong Polytechnic Univ., Dept. of Mechanical Engineering, Hong Kong (China)

    2011-02-15

    Mechanical alloying of mixed powders is of great importance for preparing oxide dispersion strengthened ferritic steels. In this study, the microstructural evolution of ferritic steel powder mixed with TiH{sub x}, YH{sub 2} and Fe{sub 2}O{sub 3} in the process of mechanical alloying is systematically investigated by using X-ray diffraction analysis, scanning electron microscopy, transmission electron microscopy and microhardness tests. It is found that titanium, yttrium hydrides and iron oxide are completely dissolved during milling, and homogeneous element distribution can be achieved after milling for 12 h. The disintegration of the composite powder particles occurs at 24 h and reaches the balance of welding and fracturing after 36 h. The oxygen content increases sharply with the disintegration of powder particles due to the absorption of oxygen at the solid/gas interface from the milling atmosphere, which is the main source of extra oxygen in the milled powder. Grain refinement down to nanometer level occurs due to the severe plastic deformation of particles; however, the grain size does not change much with further disintegration of particles. The hardness increases with milling time and then becomes stable during further milling. The study indicates that the addition of iron oxide and hydrides may be more beneficial for the dispersion and homogenization of chemical compositions in the powder mixture, thus shortening the mechanical alloying process. (orig.)

  7. The role of microstructure and phase distribution in the failure mechanisms and life prediction model for PSZ coatings

    Science.gov (United States)

    Sisson, R. D., Jr.; Sone, Ichiro; Biederman, R. R.

    1985-01-01

    Partially Stabilized Zirconia (PSZ) may become widely used for Thermal Barrier Coatings (TBC). Failure of these coatings can occur due to thermal fatigue in oxidizing atmospheres. The failure is due to the strains that develop due to thermal gradients, differences in thermal expansion coefficients, and oxidation of the bond coating. The role of microstructure and the cubic, tetragonal, and monoclinic phase distribution in the strain development and subsequent failure will be discussed. An X-ray diffraction technique for accurate determination of the fraction of each phase in PSZ will be applied to understanding the phase transformations and strain development. These results will be discussed in terms of developing a model for life prediction in PSZ coatings during thermal cycling.

  8. Influence of the heat treatment condition of alloy AlCu4Mg1 on the microstructure and properties of anodic oxide layers

    Science.gov (United States)

    Morgenstern, R.; Dietrich, D.; Sieber, M.; Lampke, T.

    2017-03-01

    Due to their outstanding specific mechanical properties, high-strength, age-hardenable aluminum alloys offer a high potential for lightweight security-related applications. However, the use of copper-alloyed aluminum is limited because of their susceptibility to selective corrosion and their low wear resistance. These restrictions can be overcome and new applications can be opened up by the generation of protective anodic aluminum oxide layers. In contrast to the anodic oxidation of unalloyed aluminum, oxide layers produced on copper-rich alloys exhibit a significantly more complex pore structure. It is the aim of the investigation to identify the influence of microstructural parameters such as size and distribution of the strengthening precipitations on the coating microstructure. The aluminum alloy EN AW-2024 (AlCu4Mg1) in different heat treatment conditions serves as substrate material. The influence of the strengthening precipitations’ size and distribution on the development of the pore structure is investigated by the use of high-resolution scanning electron microscopy. Integral coating properties are characterized by non-destructive and light-microscopic thickness measurements and instrumented indentation tests.

  9. Hydrogen production by ethanol partial oxidation over nano-iron oxide catalysts produced by chemical vapour synthesis

    Energy Technology Data Exchange (ETDEWEB)

    Ahmed, Wael Ahmed Abou Taleb Sayed

    2011-01-13

    This work presents the experimental results of the synthesis of unsupported and supported SiC iron oxide nanoparticles and their catalytic activity towards ethanol partial oxidation. For comparison, further unsupported iron oxide phases were investigated towards the ethanol partial oxidation. These {gamma}-Fe{sub 2}O{sub 3} and {alpha}/{gamma}-Fe{sub 2}O{sub 3} phase catalysts were prepared by the CVS method using Fe(CO){sub 5} as precursor, supplied by another author. The {alpha}-Fe{sub 2}O{sub 3} and SiC nanoparticles were prepared by the CVS method using a home made hot wall reactor technique at atmospheric pressure. Ferrocene and tetramethylsilane were used as precursor for the production process. Process parameters of precursor evaporation temperature, precursor concentration, gas mixture velocity and gas mixture dilution were investigated and optimised to produce particle sizes in a range of 10 nm. For Fe{sub 2}O{sub 3}/SiC catalyst series production, a new hot wall reactor setup was used. The particles were produced by simultaneous thermal decomposition of ferrocene and tetramethylsilane in one reactor from both sides. The production parameters of inlet tube distance inside the reactor, precursor evaporation temperature and carrier gas flow were investigated to produce a series of samples with different iron oxide content. The prepared catalysts composition, physical and chemical properties were characterized by XRD, EDX, SEM, BET surface area, FTIR, XPS and dynamic light scattering (DLS) techniques. The catalytic activity for the ethanol gas-phase oxidation was investigated in a temperature range from 260 C to 290 C. The product distributions obtained over all catalysts were analysed with mass spectrometry analysis tool. The activity of bulk Fe{sub 2}O{sub 3} and SiC nanoparticles was compared with prepared nano-iron oxide phase catalysts. The reaction parameters, such as reaction temperature and O{sub 2}/ethanol ratio were investigated. The catalysts

  10. Oxidation of SiC/BN/SiC Composites in Reduced Oxygen Partial Pressures

    Science.gov (United States)

    Opila, Elizabeth J.; Boyd, Meredith

    2010-01-01

    SiC fiber-reinforced SiC composites with a BN interphase are proposed for use as leading edge structures of hypersonic vehicles. The durability of these materials under hypersonic flight conditions is therefore of interest. Thermogravimetric analysis was used to characterize the oxidation kinetics of both the constituent fibers and composite coupons at four temperatures: 816, 1149, 1343, and 1538 C (1500, 2100, 2450, and 2800 F) and in oxygen partial pressures between 5% and 0.1% (balance argon) at 1 atm total pressure. One edge of the coupons was ground off so the effects of oxygen ingress into the composite could be monitored by post-test SEM and EDS. Additional characterization of the oxidation products was conducted by XPS and TOF-SIMS. Under most conditions, the BN oxidized rapidly, leading to the formation of borosilicate glass. Rapid initial oxidation followed by volatilization of boria lead to protective oxide formation and further oxidation was slow. At 1538C in 5% oxygen, both the fibers and coupons exhibited borosilicate glass formation and bubbling. At 1538C in 0.1% oxygen, active oxidation of both the fibers and the composites was observed leading to rapid SiC degradation. BN oxidation at 1538C in 0.1% oxygen was not significant.

  11. Development of a novel reactor concept for the partial oxidation of methane to syngas

    NARCIS (Netherlands)

    Smit, J.; van Sint Annaland, M.; Kuipers, J.A.M.

    2004-01-01

    The gas-to-liquid process, consisting of the partial oxidation of methane (POM) followed by the Fischer-Tropsch reaction, is a promising alternative to conventional oil processing for the production of liquid fuels. The cost of a conventional POM process is mainly determined by cryogenic air

  12. Modelling of a reverse flow catalytic membrane reactor for the partial oxidation of methane

    NARCIS (Netherlands)

    Smit, J.; van Sint Annaland, M.; Kuipers, J.A.M.

    2003-01-01

    Gas-To-Liquid (GTL) processes have great potential as alternative to conventional oil and coal processing for the production of liquid fuels. In GTL-processes the partial oxidation of methane (POM) is combined with the Fischer-Tropsch reaction. An important part of the investment costs of a

  13. Microstructure and electrical-optical properties of cesium tungsten oxides synthesized by solvothermal reaction followed by ammonia annealing

    International Nuclear Information System (INIS)

    Liu Jingxiao; Ando, Yoshihiko; Dong Xiaoli; Shi Fei; Yin Shu; Adachi, Kenji; Chonan, Takeshi; Tanaka, Akikazu; Sato, Tsugio

    2010-01-01

    Cesium tungsten oxides (Cs x WO 3 ) were synthesized by solvothermal reactions using ethanol and 57.1 vol% ethanol aqueous solution at 200 o C for 12 h, and the effects of post annealing in ammonia atmosphere on the microstructure and electrical-optical properties were investigated. Agglomerated particles consisting of disk-like nanoparticles and nanorods of Cs x WO 3 were formed in the pure ethanol and ethanol aqueous solutions, respectively. The samples retained the original morphology and crystallinity after annealing in ammonia atmosphere up to 500 o C, while a small amount of nitrogen ion were incorporated in the lattice. The as-prepared Cs x WO 3 sample showed excellent near infrared (NIR) light shielding ability as well as high transparency in the visible light region. The electrical resistivity of the pressed pellets of the powders prepared in pure ethanol and 57.1 vol% ethanol aqueous solution greatly decreased after ammonia annealing at 500 o C, i.e., from 734 to 31.5 and 231 to 3.58 Ω cm, respectively. - Graphical abstract: Cesium tungsten oxides (Cs x WO 3 ) with different morphology were synthesized by solvothermal reaction, and the effects of post-ammonia annealing on the microstructure and electrical-optical properties were investigated.

  14. Study of PM2000 microstructure evolution following FSW process

    International Nuclear Information System (INIS)

    Mathon, M.H.; Klosek, V.; Carlan, Y. de; Forest, L.

    2009-01-01

    The materials reinforced by oxides dispersion, usually called ODS (Oxide Strengthened Dispersion), have a vast applicability because of their excellent mechanical resistance at medium and high temperatures. Their weldability is one of the technological issue which remain today. The Friction Stir Welding process is a means of welding which would make it possible to preserve the oxides dispersion in the metal matrix. As a solid-state joint process, Friction Stir Welding (FSW) joins metals by locally introducing frictional heat and plastic flow by rotation of the welding tool with resulting local microstructure changes. The local microstructure determines the weld mechanical properties. Therefore, it is important to investigate the relationship between the microstructure and the mechanical properties. In this work, the PM2000 steel microstructure in friction stir (FS) weld was studied by neutron scattering. The oxides size distribution evolution between the bulk and the weld was analyzed by SANS. Crystallographic texture variations during friction stir processing were investigated by neutron diffraction. Indeed, heating and severe plastic deformation can significantly alter the original texture and then affect the physical and mechanical properties. The texture was studied in different zones: in the bulk, in the thermo-mechanically affected zone (TMAZ) and is the heat-affected zone (HAZ) of the PM2000 alloy. Lastly, the stresses distribution after welding is a crucial parameter for the mechanical properties. Their variation prediction under FSW, taking into account of the microstructure evolution which occur during the process, is very delicate. The neutron diffraction allowed characterizing the distribution of the stresses in the different zones.

  15. Small angle neutron scattering study of nano sized microstructure in Fe-Cr ODS steels for gen IV in-core applications.

    Science.gov (United States)

    Han, Young-Soo; Mao, Xiadong; Jang, Jinsung

    2013-11-01

    The nano-sized microstructures in Fe-Cr oxide dispersion strengthened steel for Gen IV in-core applications were studied using small angle neutron scattering. The oxide dispersion strengthened steel was manufactured through hot isostatic pressing with various chemical compositions and fabrication conditions. Small angle neutron scattering experiments were performed using a 40 m small angle neutron scattering instrument at HANARO. Nano sized microstructures, namely, yttrium oxides and Cr-oxides were quantitatively analyzed by small angle neutron scattering. The yttrium oxides and Cr-oxides were also observed by transmission electron microscopy. The microstructural analysis results from small angle neutron scattering were compared with those obtained by transmission electron microscopy. The effects of the chemical compositions and fabrication conditions on the microstructure were investigated in relation to the quantitative microstructural analysis results obtained by small angle neutron scattering. The volume fraction of Y-oxide increases after fabrication, and this result is considered to be due to the formation of non-stochiometric Y-Ti-oxides.

  16. 3D Microstructural Characterization of Uranium Oxide as a Surrogate Nuclear Fuel: Effect of Oxygen Stoichiometry on Grain Boundary Distributions

    Energy Technology Data Exchange (ETDEWEB)

    Rudman, K. [Arizona State Univ., Tempe, AZ (United States); Dickerson, P. [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Byler, Darrin David [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Peralta, P. [Arizona State Univ., Tempe, AZ (United States); Lim, H. [Arizona State Univ., Tempe, AZ (United States); McDonald, R. [Arizona State Univ., Tempe, AZ (United States); Dickerson, R. [Los Alamos National Lab. (LANL), Los Alamos, NM (United States); Mcclellan, Kenneth James [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

    2017-09-06

    The initial microstructure of an oxide fuel can play a key role in its performance. At low burn-ups, the diffusion of fission products can depend strongly on grain size and grain boundary (GB) characteristics, which in turn depend on processing conditions and oxygen stoichiometry. Serial sectioning techniques using Focused Ion Beam were developed to obtain Electron Backscatter Diffraction (EBSD) data for depleted UO2 pellets that were processed to obtain 3 different oxygen stoichiometries. The EBSD data were used to create 3D microstructure reconstructions and to gather statistical information on the grain and GB crystallography, with emphasis on identifying the character (twist, tilt, mixed) for GBs that meet the Coincident Site Lattice (CSL) criterion as well as GBs with the most common misorientation angles. Data on dihedral angles at triple points were also collected. The results were compared across different samples to understand effects of oxygen content on microstructure evolution.

  17. Oxidation and microstrucure of V-Cr-Ti alloys exposed to oxygen-containing environments

    Energy Technology Data Exchange (ETDEWEB)

    Natesan, K. [Argonne National Lab., IL (United States); Uz, M. [Lafayette College, Easton, PA (United States); Ulie, T.

    1997-08-01

    The objectives of this task are to (a) evaluate the oxygen uptake of several V-Cr-Ti alloys as a function of temperature and oxygen partial pressure in the exposure environment, (b) examine the microstructural characteristics of oxide scales and oxygen trapped at the grain boundaries in the substrate alloys, and (c) evaluate the influence of alloy composition on oxygen uptake and develop correlation(s) between alloy composition, exposure environment, and temperature.

  18. Oxidation and microstrucure of V-Cr-Ti alloys exposed to oxygen-containing environments

    International Nuclear Information System (INIS)

    Natesan, K.; Uz, M.; Ulie, T.

    1997-01-01

    The objectives of this task are to (a) evaluate the oxygen uptake of several V-Cr-Ti alloys as a function of temperature and oxygen partial pressure in the exposure environment, (b) examine the microstructural characteristics of oxide scales and oxygen trapped at the grain boundaries in the substrate alloys, and (c) evaluate the influence of alloy composition on oxygen uptake and develop correlation(s) between alloy composition, exposure environment, and temperature

  19. Reaction scheme of partial oxidation of methane to synthesis gas over yttrium-stabilized zirconia

    NARCIS (Netherlands)

    Zhu, J.J.; van Ommen, J.G.; Lefferts, Leonardus

    2004-01-01

    The partial oxidation of methane to synthesis gas over yttrium-stabilized zirconia (YSZ) was studied with in situ FTIR and both steady-state and transient experiments. The four major products, CO, H2, CO2, and H2O, are primary products of CPOM over YSZ. Besides these major products and traces of

  20. In situ observations of microstructural changes in SOFC anodes during redox cycling

    DEFF Research Database (Denmark)

    Klemensø, Trine; Appel, C. C.; Mogensen, Mogens Bjerg

    2006-01-01

    The anode-supported solid oxide fuel cell (SOFC) degrades when the anode is subjected to redox cycling. The degradation has qualitatively been related to microstructural changes in the nickel-yttria stabilized zirconia anode of the tested cells. In this work, the microstructural changes were...... observed in situ using environmental scanning electron microscopy. In the reduced state, a dynamic rounding of the nickel particles occurred. The oxide growth upon re-oxidation depended on the oxidation kinetics. During rapid oxidation, the NiO particles divided into 2-4 particles, which grew...... into the surrounding voids. For slower oxidation, an external oxide layer was seen to develop around the individual particles. (c) 2006 The Electrochemical Society....

  1. Study on Thixojoining Process Using Partial Remelting Method

    Directory of Open Access Journals (Sweden)

    M. N. Mohammed

    2013-01-01

    Full Text Available Cold-work tool steel is considered to be a nonweldable metal due to its high percentage content of carbon and alloy elements. The application of a new process of the semisolid joining of two dissimilar metals is proposed. AISI D2 cold-work tool steel was thixojoined to 304 stainless steel by using a partial remelting method. After thixojoining, microstructural examination including metallographic analysis, energy dispersive spectroscopy (EDS, and Vickers hardness tests was performed. From the results, metallographic analyses along the joint interface between semisolid AISI D2 and stainless steel showed a smooth transition from one to another and neither oxides nor microcracking was observed. Hardness values obtained from the points in the diffusion zone were much higher than those in the 304 stainless steel but lower than those in the AISI D2 tool steel. The study revealed that a new type of nonequilibrium diffusion interfacial structure was constructed at the interface of the two different types of steel. The current work successfully confirmed that avoidance of a dendritic microstructure in the semisolid joined zone and high bonding quality components can be achieved without the need for force or complex equipment when compared to conventional welding processes.

  2. Oscillatory behaviour of catalytic properties, structure and temperature during the catalytic partial oxidation of methane on Pd/Al2O3

    DEFF Research Database (Denmark)

    Kimmerle, B.; Baiker, A.; Grunwaldt, Jan-Dierk

    2010-01-01

    Pd/Al2O3 catalysts showed an oscillatory behaviour during the catalytic partial oxidation (CPO) of methane, which was investigated simultaneously by IR-thermography, X-ray absorption spectroscopy, and online mass-spectrometry to correlate the temperature, state of the catalyst and catalytic...... to self-reduction leading to extinction of the process. The latter was the key driver for the oscillations and thus gave additional insight into the mechanism of partial methane oxidation....

  3. Mechanism and Microstructure of Oxide Fluxes for Gas Tungsten Arc Welding of Magnesium Alloy

    Science.gov (United States)

    Liu, L. M.; Zhang, Z. D.; Song, G.; Wang, L.

    2007-03-01

    Five single oxide fluxes—MgO, CaO, TiO2, MnO2, and Cr2O3—were used to investigate the effect of active flux on the depth/width ratio in AZ31B magnesium alloy. The microstructure and mechanical property of the tungsten inert gas (TIG) welding seam were studied. The oxygen content in the weld seam and the arc images during the TIG welding process were analyzed. A series of emission spectroscopy of weld arc for TIG welding for magnesium with and without flux were developed. The results showed that for the five single oxide fluxes, all can increase the weld penetration effectively and grain size in the weld seam of alternating current tungsten inert gas (ACTIG) welding of the Mg alloy. The oxygen content of the welds made without flux is not very different from those produced with oxide fluxes not considering trapped oxide. However, welds that have the best penetration have a relatively higher oxygen content among those produced with flux. It was found that the arc images with the oxide fluxes were only the enlarged form of the arc images without flux; the arc constriction was not observed. The detection of arc spectroscopy showed that the metal elements in the oxides exist as the neutral atom or the first cation in the weld arc. This finding would influence the arc properties. When TIG simulation was carried out on a plate with flux applied only on one side, the arc image video showed an asymmetric arc, which deviated toward the flux free side. The thermal stability, the dissociation energy, and the electrical conductivity of oxide should be considered when studying the mechanism for increased TIG flux weld penetration.

  4. A novel technique for hydrogen production from hog-manure in supercritical partial oxidation (SCWPO)

    Energy Technology Data Exchange (ETDEWEB)

    Youssef, Emhemmed A.; Charpentier, Paul [Western Ontario Univ., London, ON (Canada). Dept. of Chemical and Biochemical Engineering; Nakhla, George [Western Ontario Univ., London, ON (Canada). Dept. of Chemical and Biochemical Engineering; Western Ontario Univ., London, ON (Canada). Dept. of Civil and Environmental Engineering; Elbeshbishy, Elsayed; Hafez, Hisham [Western Ontario Univ., London, ON (Canada). Dept. of Civil and Environmental Engineering

    2010-07-01

    In this study, the catalytic hydrogen production from hog manure using supercritical water partial oxidation was investigated in a batch reactor at a temperature of 500 C, and pressure of 28 MPa using several metallic catalysts. Hog manure was characterized by a total and soluble chemical oxygen demand (TCOD, SCOD) of 57000 and 28000 mg/L, total and volatile suspended solids (TSS, VSS) of 25000, 19000, and ammonia of 2400 mg/L, respectively. The order of H{sub 2} production was the following: Pd/AC > Ru/Al{sub 2}O{sub 3} > Ru/AC > AC > NaOH. The order of COD reduction efficiency was as follows: NaOH > Ru/AC > AC > Ru/Al{sub 2}O{sub 3} > Pd/AC. The behaviour of the volatile fatty acids (VFA's), ethanol, methanol, ammonia, H{sub 2}S, and Sulfate was investigated experimentally and discussed. A 35 % reduction in the H{sub 2} and CH{sub 4} yields was observed in the sequential gasification partial oxidation (oxidant at an 80 % of theoretical requirement) experiments compared to the gasification experiments (catalyst only). Moreover, this reduction in gas yields was coincided with a 45 % reduction in the liquid effluent chemical oxygen demand (COD), 60 % reduction of the ammonia concentration in the liquid effluent, and 20 % reduction in the H{sub 2}S concentration in the effluent gas. (orig.)

  5. Oxidative Stress in Patients with Drug Resistant Partial Complex Seizure

    Directory of Open Access Journals (Sweden)

    Lourdes Lorigados Pedre

    2018-06-01

    Full Text Available Oxidative stress (OS has been implicated as a pathophysiological mechanism of drug-resistant epilepsy, but little is known about the relationship between OS markers and clinical parameters, such as the number of drugs, age onset of seizure and frequency of seizures per month. The current study’s aim was to evaluate several oxidative stress markers and antioxidants in 18 drug-resistant partial complex seizure (DRPCS patients compared to a control group (age and sex matched, and the results were related to clinical variables. We examined malondialdehyde (MDA, advanced oxidation protein products (AOPP, advanced glycation end products (AGEs, nitric oxide (NO, uric acid, superoxide dismutase (SOD, glutathione, vitamin C, 4-hydroxy-2-nonenal (4-HNE and nitrotyrosine (3-NT. All markers except 4-HNE and 3-NT were studied by spectrophotometry. The expressions of 4-HNE and 3-NT were evaluated by Western blot analysis. MDA levels in patients were significantly increased (p ≤ 0.0001 while AOPP levels were similar to the control group. AGEs, NO and uric acid concentrations were significantly decreased (p ≤ 0.004, p ≤ 0.005, p ≤ 0.0001, respectively. Expressions of 3-NT and 4-HNE were increased (p ≤ 0.005 similarly to SOD activity (p = 0.0001, whereas vitamin C was considerably diminished (p = 0.0001. Glutathione levels were similar to the control group. There was a positive correlation between NO and MDA with the number of drugs. The expression of 3-NT was positively related with the frequency of seizures per month. There was a negative relationship between MDA and age at onset of seizures, as well as vitamin C with seizure frequency/month. We detected an imbalance in the redox state in patients with DRCPS, supporting oxidative stress as a relevant mechanism in this pathology. Thus, it is apparent that some oxidant and antioxidant parameters are closely linked with clinical variables.

  6. Partial oxidation of dimethyl ether using the structured catalyst Rh/Al2O3/Al prepared through the anodic oxidation of aluminum.

    Science.gov (United States)

    Yu, B Y; Lee, K H; Kim, K; Byun, D J; Ha, H P; Byun, J Y

    2011-07-01

    The partial oxidation of dimethyl ether (DME) was investigated using the structured catalyst Rh/Al2O3/Al. The porous Al2O3 layer was synthesized on the aluminum plate through anodic oxidation in an oxalic-acid solution. It was observed that about 20 nm nanopores were well developed in the Al2O3 layer. The thickness of Al2O3 layer can be adjusted by controlling the anodizing time and current density. After pore-widening and hot-water treatment, the Al2O3/Al plate was calcined at 500 degrees C for 3 h. The obtained delta-Al2O3 had a specific surface area of 160 m2/g, making it fit to be used as a catalyst support. A microchannel reactor was designed and fabricated to evaluate the catalytic activity of Rh/Al2O3/Al in the partial oxidation of DME. The structured catalyst showed an 86% maximum hydrogen yield at 450 degrees C. On the other hand, the maximum syngas yield by a pack-bed-type catalyst could be attained by using a more than fivefold Rh amount compared to that used in the structured Rh/Al2O3/Al catalyst.

  7. Intrinsic Resistance Switching in Amorphous Silicon Suboxides: The Role of Columnar Microstructure.

    Science.gov (United States)

    Munde, M S; Mehonic, A; Ng, W H; Buckwell, M; Montesi, L; Bosman, M; Shluger, A L; Kenyon, A J

    2017-08-24

    We studied intrinsic resistance switching behaviour in sputter-deposited amorphous silicon suboxide (a-SiO x ) films with varying degrees of roughness at the oxide-electrode interface. By combining electrical probing measurements, atomic force microscopy (AFM), and scanning transmission electron microscopy (STEM), we observe that devices with rougher oxide-electrode interfaces exhibit lower electroforming voltages and more reliable switching behaviour. We show that rougher interfaces are consistent with enhanced columnar microstructure in the oxide layer. Our results suggest that columnar microstructure in the oxide will be a key factor to consider for the optimization of future SiOx-based resistance random access memory.

  8. A study of emission property and microstructure of rare earth oxide-molybdenum cermet cathode materials made by spark plasma sintering

    International Nuclear Information System (INIS)

    Wang Jinshu; Li Hongyi; Yang Sa; Cui Ying; Zhou Meiling

    2004-01-01

    A fast sintering method, spark plasma sintering (SPS) was used for the synthesis of rare earth oxide-molybdenum cathode material. The secondary emission property, microstructure, and phase constitution of materials have been studied in this paper. The experimental results show that the maximum secondary emission coefficient of this material can be high to 3.84, much higher than that of rare earth oxide-molybdenum cathode made by traditional sintering method. The grain size is less than 1 μm and rare earth distributed evenly in the material. After the material was activated at 1600 deg. C, a 4 μm layer of rare earth oxide which leads to the high secondary emission coefficient of the material, is formed on the surface of the cathode

  9. Production of reduction gases: partial oxidation of hydrocarbons and coal

    Energy Technology Data Exchange (ETDEWEB)

    Tippmer, K

    1976-04-01

    After some general remarks on reduction gas and quality demands, the Texaco process of partial oxidation with scrubbing is dealt with. A comparison of current iron-sponge techniques shows that a heat demand below 3 M kcal/t Fe should be envisaged, which means that heavy fuel oil or coal should be used. The special features of oxygen generation, coal processing, demands made on fuel oil, gasoline, and natural gas, gas generation, soot recovery, hydrogen sulphide-carbon dioxide scrubbing, system Benfield HP process, recycle-carbon dioxide scrubbing, auxiliary steam system, gas preheating, recycle gas cooling and compression, process data and heat balances for natural gas (one-heat system) and heating fuel oil or naphtha (two-heat system) are given.

  10. Quantitative data analysis methods for 3D microstructure characterization of Solid Oxide Cells

    DEFF Research Database (Denmark)

    Jørgensen, Peter Stanley

    through percolating networks and reaction rates at the triple phase boundaries. Quantitative analysis of microstructure is thus important both in research and development of optimal microstructure design and fabrication. Three dimensional microstructure characterization in particular holds great promise...... for gaining further fundamental understanding of how microstructure affects performance. In this work, methods for automatic 3D characterization of microstructure are studied: from the acquisition of 3D image data by focused ion beam tomography to the extraction of quantitative measures that characterize...... the microstructure. The methods are exemplied by the analysis of Ni-YSZ and LSC-CGO electrode samples. Automatic methods for preprocessing the raw 3D image data are developed. The preprocessing steps correct for errors introduced by the image acquisition by the focused ion beam serial sectioning. Alignment...

  11. Microstructure refinement and strengthening mechanisms of a 9Cr oxide dispersion strengthened steel by zirconium addition

    International Nuclear Information System (INIS)

    Xu, Hai Jian; Lu, Zheng; Wang, Dong Mei; Liu, Chunming

    2017-01-01

    To study the effects of zirconium (Zr) addition on the microstructure, hardness and the tensile properties of oxide dispersion strengthened (ODS) ferritic-martensitic steels, two kinds of 9Cr-ODS ferritic-martensitic steels with nominal compositions (wt.%) of Fe-9Cr-2W-0.3Y_2O-3 and Fe-9Cr-2W-0.3Zr-0.3Y_2O_3 were fabricated by the mechanical alloying (MA) of premixed powders and then consolidated by hot isostatic pressing (HIP) techniques. The experimental results showed that the average grain size decreases with Zr addition. The trigonal δ-phase Y_4Zr_3O_1_2 oxides and body-centered cubic Y_2O_3 oxides are formed in the 9Cr-Zr-ODS steel and 9Cr non-Zr ODS steel, respectively, and the average size of Y_4Zr_3O_1_2 particles is much smaller than that of Y_2O_3. The dispersion morphology of the oxide particles in 9Cr-Zr-ODS steel is significantly improved and the number density is 1.1 x 10"2"3/m"3 with Zr addition. The 9Cr-Zr-ODS steel shows much higher tensile ductility, ultimate tensile strength and Vickers hardness at the same time

  12. Adiabatic Gasification and Pyrolysis of Coffee Husk Using Air-Steam for Partial Oxidation

    OpenAIRE

    Catalina Rodriguez; Gerardo Gordillo

    2011-01-01

    Colombian coffee industry produces about 0.6 million tons of husk (CH) per year which could serve as feedstock for thermal gasification to produce gaseous and liquid fuels. The current paper deals with: (i) CH adiabatic gasification modeling using air-steam blends for partial oxidation and (ii) experimental thermogravimetric analysis to determine the CH activation energy (E). The Chemical Equilibrium with Applications Program (CEA), developed by NASA, was used to estimate the effect of equiva...

  13. Synthesis, microstructures and properties of {gamma}-aluminum oxynitride

    Energy Technology Data Exchange (ETDEWEB)

    Wang Xidong; Wang Fuming; Li Wenchao

    2003-02-15

    This paper deals with the synthesis, microstructures and properties of {gamma}-aluminum oxynitride (AlON). The thermodynamic properties of AlON were analyzed and the Gibbs energy of AlON with different compositions and temperatures were evaluated. Based on thermodynamic studies, AlON has been synthesized. The microstructures, mechanical properties and oxidation resistance of the synthetic AlON have been examined and discussed.

  14. Effect of surface composition of yttrium-stabilized zirconia on partial oxidation of methane to synthesis gas.

    NARCIS (Netherlands)

    Zhu, J.J.; van Ommen, J.G.; Knoester, A.; Lefferts, Leonardus

    2005-01-01

    Catalytic partial oxidation of methane to synthesis gas (CPOM) over yttrium-stabilized zirconia (YSZ) was studied within a wide temperature window (500¿1100 °C). The catalysts were characterized by X-ray fluorescence (XRF) and low-energy ion scattering (LEIS). The influence of calcination

  15. Microstructure of ultra high performance concrete containing lithium slag.

    Science.gov (United States)

    He, Zhi-Hai; Du, Shi-Gui; Chen, Deng

    2018-04-03

    Lithium slag (LS) is discharged as a byproduct in the process of the lithium carbonate, and it is very urgent to explore an efficient way to recycle LS in order to protect the environments and save resources. Many available supplementary cementitious materials for partial replacement of cement and/or silica fume (SF) can be used to prepare ultra high performance concrete (UHPC). The effect of LS to replace SF partially by weight used as a supplementary cementitious material (0%, 5%, 10% and 15% of binder) on the compressive strengths and microstructure evolution of UHPC has experimentally been studied by multi-techniques including mercury intrusion porosimetry, scanning electron microscope and nanoindentation technique. The results show that the use of LS degrades the microstructure of UHPC at early ages, and however, the use of LS with the appropriate content improves microstructure of UHPC at later ages. The hydration products of UHPC are mainly dominated by ultra-high density calcium-silicate-hydrate (UHD C-S-H) and interfacial transition zone (ITZ) in UHPC has similar compact microstructure with the matrix. The use of LS improves the hydration degree of UHPC and increases the elastic modulus of ITZ in UHPC. LS is a promising substitute for SF for preparation UHPC. Copyright © 2018 Elsevier B.V. All rights reserved.

  16. Fabrication of three-dimensional platinum microstructures with laser irradiation and electrochemical technique

    International Nuclear Information System (INIS)

    Kikuchi, T.; Takahashi, H.; Maruko, T.

    2007-01-01

    Three-dimensional (3D) platinum microstructures were fabricated by successive procedures: aluminum anodizing, laser irradiation, nickel/platinum electroplating, and removal of the aluminum substrate, the oxide films, and the nickel metal layer. Aluminum plates and rods were anodized in an oxalic acid solution to form porous type oxide films. The anodized specimens were immersed in a nickel electroplating solution, and then irradiated with a pulsed Nd-yttrium aluminum garnet (YAG) laser beam to remove the anodic oxide film with a three-dimensional XYZθ stage. The specimens were cathodically polarized in the nickel and a platinum electroplating solution to form the metal micropattern at the laser-irradiated area. The electroplated specimens were immersed in NaOH solution to dissolve the aluminum substrate and the oxide films, and then immersed in HCl solution to dissolve the nickel deposits. A platinum grid-shaped microstructure, a microspring, and a cylindrical network microstructure with 50-100 μm line width were obtained successfully

  17. Fabrication of three-dimensional platinum microstructures with laser irradiation and electrochemical technique

    Energy Technology Data Exchange (ETDEWEB)

    Kikuchi, T. [Graduate School of Engineering, Hokkaido University, N13, W8, Kita-Ku, Sapporo (Japan)]. E-mail: kiku@elechem1-mc.eng.hokudai.ac.jp; Takahashi, H. [Graduate School of Engineering, Hokkaido University, N13, W8, Kita-Ku, Sapporo (Japan); Maruko, T. [Furuya Metal Co. Ltd., R and D Group, Shimodate Daiichi Kogyodanchi 1915, Morisoejima, Chikusei, Ibaraki (Japan)

    2007-02-01

    Three-dimensional (3D) platinum microstructures were fabricated by successive procedures: aluminum anodizing, laser irradiation, nickel/platinum electroplating, and removal of the aluminum substrate, the oxide films, and the nickel metal layer. Aluminum plates and rods were anodized in an oxalic acid solution to form porous type oxide films. The anodized specimens were immersed in a nickel electroplating solution, and then irradiated with a pulsed Nd-yttrium aluminum garnet (YAG) laser beam to remove the anodic oxide film with a three-dimensional XYZ{theta} stage. The specimens were cathodically polarized in the nickel and a platinum electroplating solution to form the metal micropattern at the laser-irradiated area. The electroplated specimens were immersed in NaOH solution to dissolve the aluminum substrate and the oxide films, and then immersed in HCl solution to dissolve the nickel deposits. A platinum grid-shaped microstructure, a microspring, and a cylindrical network microstructure with 50-100 {mu}m line width were obtained successfully.

  18. Microstructural characterization of the cycling behavior of electrodeposited manganese oxide supercapacitors using 3D electron tomography

    Science.gov (United States)

    Dalili, N.; Clark, M. P.; Davari, E.; Ivey, D. G.

    2016-10-01

    Manganese oxide has been investigated extensively as an electrochemical capacitor or supercapacitor electrode material. Manganese oxide is inexpensive to fabricate and exhibits relatively high capacitance values, i.e., in excess of 200 F g-1 in many cases; the actual value depends very much on the fabrication method and test conditions. The cycling behavior of Mn oxide, fabricated using anodic electrodeposition, is investigated using slice and view techniques, via a dual scanning electron microscope (SEM) and focused ion beam (FIB) instrument to generate three-dimensional (3D) images, coupled with electrochemical characterization. The initial as-fabricated electrode has a rod-like appearance, with a fine-scale, sheet-like morphology within the rods. The rod-like structure remains after cycling, but there are significant morphological changes. These include partial dissolution of Mn oxide followed by redeposition of Mn oxide in regions close to the substrate. The redeposited material has a finer morphology than the original as-fabricated Mn oxide. The Mn oxide coverage is also better near the substrate. These effects result in an increase in the specific capacitance.

  19. Microstructural characterization of Y{sub 2}O{sub 3} ODS-Fe-Cr model alloys

    Energy Technology Data Exchange (ETDEWEB)

    Castro, V. de [Department of Materials, University of Oxford, Oxford OX1 3PH (United Kingdom)], E-mail: vanessa.decastro@materials.ox.ac.uk; Leguey, T.; Munoz, A.; Monge, M.A.; Pareja, R. [Departamento de Fisica, Universidad Carlos III de Madrid, 28911 Leganes (Spain); Marquis, E.A.; Lozano-Perez, S.; Jenkins, M.L. [Department of Materials, University of Oxford, Oxford OX1 3PH (United Kingdom)

    2009-04-30

    Two Fe-12 wt% Cr alloys, one containing 0.4 wt% Y{sub 2}O{sub 3} and the other Y{sub 2}O{sub 3}-free, have been produced by mechanical alloying followed by hot isostatic pressing. These oxide dispersion strengthened and reference alloys were characterized both in the as-HIPed state and after tempering by transmission electron microscopy and atom-probe tomography. The as-HIPed alloys exhibited the characteristic microstructure of lath martensite and contained a high density of dislocations. Small voids with sizes <10 nm were also observed. Both alloys also contained M{sub 3}C and M{sub 23}C{sub 6} carbides (M = Cr, Fe) probably as a result of C ingress during milling. After tempering at 1023 K for 4 h the microstructures had partially recovered. In the recovered regions, martensite laths were replaced by equiaxed grains in which M{sub 23}C{sub 6} carbides decorated the grain boundaries. In the ODS alloy nanoparticles containing Y were commonly observed within grains, although they were also present at grain boundaries and adjacent to large carbides.

  20. Development of a simultaneous partial nitrification and anaerobic ammonia oxidation process in a single reactor.

    Science.gov (United States)

    Cho, Sunja; Fujii, Naoki; Lee, Taeho; Okabe, Satoshi

    2011-01-01

    Up-flow oxygen-controlled biofilm reactors equipped with a non-woven fabric support were used as a single reactor system for autotrophic nitrogen removal based on a combined partial nitrification and anaerobic ammonium oxidation (anammox) reaction. The up-flow biofilm reactors were initiated as either a partial nitrifying reactor or an anammox reactor, respectively, and simultaneous partial nitrification and anammox was established by careful control of the aeration rate. The combined partial nitrification and anammox reaction was successfully developed in both biofilm reactors without additional biomass inoculation. The reactor initiated as the anammox reactor gave a slightly higher and more stable mean nitrogen removal rate of 0.35 (±0.19) kg-N m(-3) d(-1) than the reactor initiated as the partial nitrifying reactor (0.23 (±0.16) kg-N m(-3) d(-1)). FISH analysis revealed that the biofilm in the reactor started as the anammox reactor were composed of anammox bacteria located in inner anoxic layers that were surrounded by surface aerobic AOB layers, whereas AOB and anammox bacteria were mixed without a distinguishable niche in the biofilm in the reactor started as the partial nitrifying reactor. However, it was difficult to efficiently maintain the stable partial nitrification owing to inefficient aeration in the reactor, which is a key to development of the combined partial nitrification and anammox reaction in a single biofilm reactor. Copyright © 2010 Elsevier Ltd. All rights reserved.

  1. Effect of Target Density on Microstructural, Electrical, and Optical Properties of Indium Tin Oxide Thin Films

    Science.gov (United States)

    Zhu, Guisheng; Zhi, Li; Yang, Huijuan; Xu, Huarui; Yu, Aibing

    2012-09-01

    In this paper, indium tin oxide (ITO) targets with different densities were used to deposit ITO thin films. The thin films were deposited from these targets at room temperature and annealed at 750°C. Microstructural, electrical, and optical properties of the as-prepared films were studied. It was found that the target density had no effect on the properties or deposition rate of radiofrequency (RF)-sputtered ITO thin films, different from the findings for direct current (DC)-sputtered films. Therefore, when using RF sputtering, the target does not require a high density and may be reused.

  2. Near-liquidus forging, partial remelting and thixoforging of an AZ91D + Y magnesium alloy

    International Nuclear Information System (INIS)

    Zhao Zude; Chen Qiang; Hu Chuankai; Huang Shuhai; Wang Yuanqing

    2009-01-01

    A new route, near-liquidus forging plus partial remelting, has been developed for obtaining globular microstructures. Firstly, a material is formed by near-liquidus forging for obtaining a fine dendritic microstructure. Globular microstructure can be produced by reheating the material into the semi-solid temperature range for a period of time. In this paper, an AZ91D alloy with the addition of yttrium was prepared by near-liquidus forging. Microstructure evolution during partial remelting was studied at temperatures and for times. Tensile mechanical properties of thixoforged components were also determined. It is shown that the fine dendritic structure firstly evolves into a blocky structure during partial remelting. With prolonged holding time, the blocky structure disintegrates into polygonal solid particles. Prolonging time and increasing temperature promote a faster spheroidization. Good mechanical properties are obtained for the thixoforged AZ91D alloy with the addition of yttrium prepared by near-liquidus forging, with a yield strength of 160.9 MPa and a ultimate tensile strength of 301.7 MPa and a elongation to fracture of 9.734%.

  3. Effects of Oxygen Partial Pressure on Oxidation Behavior of CMnSi TRIP Steel in an Oxidation-Reduction Scheme

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Seong-Hwan; Huh, Joo-Youl [Korea University, Seoul (Korea, Republic of); Kim, Myung-Soo; Kim, Jong-Sang [POSCO Technical Research Laboratories, Gwangyang (Korea, Republic of)

    2017-02-15

    An oxidation-reduction scheme is an alternative approach for improving the galvanizability of advanced high-strength steel in the continuous hot-dip galvanizing process. Here, we investigated the effect of oxygen partial pressure (Po{sub 2}) on the oxidation behavior of a transformation-induced plasticity steel containing 1.5 wt% Si and 1.6 wt% Mn during heating to and holding for 60 s at 700 ℃ under atmospheres with various Po{sub 2} values. Irrespective of Po{sub 2}, a thin amorphous Si-rich layer of Si-Mn-O was formed underneath the Fe oxide scale (a Fe{sub 2}O{sub 3}/Fe{sub 3}O{sub 4} bilayer) in the heating stage. In contrast to Si, Mn tended to segregate at the scale surface as (Fe,Mn){sub 2}O{sub 3}. The multilayered structure of (Fe,Mn){sub 2}O{sub 3}/Fe{sub 2}O{sub 3}/Fe{sub 3}O{sub 4}/amorphous Si-Mn-O remained even after extended oxidizing at 700 ℃ for 60 s. Fe{sub 2}O{sub 3} was the dominantly growing oxide phase in the scale. The enhanced growth rate of Fe{sub 2}O{sub 3} with increasing Po{sub 2} resulted in the formation of more Kirkendall voids in the amorphous Si-rich layer and a less Mn segregation at the scale surface. The mechanisms underlying the absence of FeO and the formation of Kirkendall voids are discussed.

  4. Formation and microstructure of nickel oxide films

    Energy Technology Data Exchange (ETDEWEB)

    Marcius, Marijan [Ruder Boskovic Institute, P.O. Box 180, HR-10002 Zagreb (Croatia); Ristic, Mira, E-mail: ristic@irb.hr [Ruder Boskovic Institute, P.O. Box 180, HR-10002 Zagreb (Croatia); Ivanda, Mile; Music, Svetozar [Ruder Boskovic Institute, P.O. Box 180, HR-10002 Zagreb (Croatia)

    2012-11-15

    Highlights: Black-Right-Pointing-Pointer Difference in NiO films formed on Ni plate or glass substrate were found. Black-Right-Pointing-Pointer NiO particle sizes on Ni plate changed from nano to micron dimensions. Black-Right-Pointing-Pointer NiO particle sizes on glass substrate changed from {approx}16 to {approx}27 nm. Black-Right-Pointing-Pointer Raman and UV/Vis/NIR spectra are related to the microstructure of NiO films. - Abstract: The formation and microstructure of NiO films on different substrates were monitored using XRD, Raman, UV/Vis/NIR and FE-SEM/EDS techniques. The formation of NiO films on Ni plates in air atmosphere between 400 and 800 Degree-Sign C was confirmed by XRD and Raman spectroscopy. The origin of Raman bands and corresponding Raman shifts in the samples are discussed. An increase in the size of NiO particles in the films from nano to micro dimensions was demonstrated. A change in the atomic ratio Ni:O with an increase in heating temperature was observed. Polished Ni plates coated with a thin Ni-acetate layer upon heating at high temperatures gave similar NiO microstructures on the surface like in the case of non-treated Ni plates. Glass substrates coated with thin Ni-acetate films upon heating between 400 and 800 Degree-Sign C yielded pseudospherical NiO nanoparticles. The dominant Raman band as an indicator of NiO formation on a glass substrate was shown. The formation of NiO nanoparticles on glass substrates with maximum size distribution from 16 to 27 nm in a broad temperature range from 400 to 800 Degree-Sign C can be explained by the absence of a constant source of metallic nickel which was present in the case of Ni plates.

  5. The influence of surface microstructure and chemical composition on corrosion behaviour in fuel-grade bio-ethanol of low-alloy steel modified by plasma nitro-carburizing and post-oxidizing

    Science.gov (United States)

    Boniatti, Rosiana; Bandeira, Aline L.; Crespi, Ângela E.; Aguzzoli, Cesar; Baumvol, Israel J. R.; Figueroa, Carlos A.

    2013-09-01

    The interaction of bio-ethanol on steel surfaces modified by plasma-assisted diffusion technologies is studied for the first time. The influence of surface microstructure and chemical composition on corrosion behaviour of AISI 4140 low-alloy steel in fuel-grade bio-ethanol was investigated. The steel surfaces were modified by plasma nitro-carburizing followed plasma oxidizing. X-ray diffraction, scanning electron microscopy, optical microscopy, X-ray dispersive spectroscopy, and glow-discharge optical emission spectroscopy were used to characterize the modified surface before and after immersion tests in bio-ethanol up to 77 days. The main corrosion mechanism is pit formation. The pit density and pit size were measured in order to quantify the corrosion resistance which was found to depend more strongly on microstructure and morphology of the oxide layer than on its thickness. The best corrosion protection was observed for samples post-oxidized at 480 °C and 90 min.

  6. The influence of surface microstructure and chemical composition on corrosion behaviour in fuel-grade bio-ethanol of low-alloy steel modified by plasma nitro-carburizing and post-oxidizing

    International Nuclear Information System (INIS)

    Boniatti, Rosiana; Bandeira, Aline L.; Crespi, Ângela E.; Aguzzoli, Cesar; Baumvol, Israel J.R.; Figueroa, Carlos A.

    2013-01-01

    The interaction of bio-ethanol on steel surfaces modified by plasma-assisted diffusion technologies is studied for the first time. The influence of surface microstructure and chemical composition on corrosion behaviour of AISI 4140 low-alloy steel in fuel-grade bio-ethanol was investigated. The steel surfaces were modified by plasma nitro-carburizing followed plasma oxidizing. X-ray diffraction, scanning electron microscopy, optical microscopy, X-ray dispersive spectroscopy, and glow-discharge optical emission spectroscopy were used to characterize the modified surface before and after immersion tests in bio-ethanol up to 77 days. The main corrosion mechanism is pit formation. The pit density and pit size were measured in order to quantify the corrosion resistance which was found to depend more strongly on microstructure and morphology of the oxide layer than on its thickness. The best corrosion protection was observed for samples post-oxidized at 480 °C and 90 min.

  7. Microstructure and properties of aluminium-aluminium oxide graded composite materials

    Science.gov (United States)

    Kamaruzaman, F. F.; Nuruzzaman, D. M.; Ismail, N. M.; Hamedon, Z.; Iqbal, A. K. M. A.; Azhari, A.

    2018-03-01

    In this research works, four-layered aluminium-aluminium oxide (Al-Al2O3) graded composite materials were fabricated using powder metallurgy (PM) method. In processing, metal-ceramic graded composite materials of 0%, 10%, 20% and 30% weight percentage of ceramic concentration were prepared under 30 ton compaction load using a cylindrical die-punch set made of steel. After that, two-step pressureless sintering was carried out at sintering temperature and time 600°C and 3 hours respectively. It was observed that the sintered cylindrical specimens of 30 mm diameter were prepared successfully. The graded composite specimens were analysed and the properties such as density, microstructure and hardness were measured. It was found that after sintering process, the diameter of the graded cylindrical structure was decreased. Using both Archimedes method and rule of mixture (ROM), he density of structure was measured. The obtained results revealed that the microvickers hardness was increased as the ceramic component increases in the graded layer. Moreover, it was observed that the interface of the graded structure is clearly distinguished within the multilayer stack and the ceramic particles are almost uniformly distributed in the Al matrix.

  8. Partial oxidation of methane to syngas on Rh/Al{sub 2}O{sub 3} and Rh/Ce-ZrO{sub 2} catalysts

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, Raquel L.; Bitencourt, Isabela G.; Passos, Fabio B., E-mail: fbpassos@vm.uff.br [Universidade Federal Fluminense (UFF), Niteroi, RJ (Brazil). Dept. de Engenharia Quimica e Petroleo

    2013-01-15

    The partial oxidation of methane with {gamma}-Al{sub 2}O{sub 3}-, CeO{sub 2}-, ZrO{sub 2}- and Ce-ZrO{sub 2}-supported rhodium catalysts was investigated. DRIFTS (diffuse reflectance infrared spectroscopy) measurements of adsorbed CO showed the formation of different rhodium species on different supports, which influenced the dispersion of the metal. The effects of the metal dispersion, oxygen storage capacity on the activity of these catalysts for the partial oxidation of methane are discussed. (author)

  9. Dynamic Mechanical Properties and Microstructure of Graphene Oxide Nanosheets Reinforced Cement Composites

    Directory of Open Access Journals (Sweden)

    Wu-Jian Long

    2017-11-01

    Full Text Available This paper presents an experimental investigation on the effect of uniformly dispersed graphene oxide (GO nanosheets on dynamic mechanical properties of cement based composites prepared with recycled fine aggregate (RFA. Three different amounts of GO, 0.05%, 0.10%, and 0.20% in mass of cement, were used in the experiments. The visual inspections of GO nanosheets were also carried out after ultrasonication by transmission electron microscope (TEM atomic force microscope (AFM, and Raman to characterize the dispersion effect of graphite oxide. Dynamic mechanical analyzer test showed that the maximum increased amount of loss factor and storage modulus, energy absorption was 125%, 53%, and 200% when compared to the control sample, respectively. The flexural and compressive strengths of GO-mortar increased up to 22% to 41.3% and 16.2% to 16.4% with 0.20 wt % GO at 14 and 28 days, respectively. However the workability decreased by 7.5% to 18.8% with 0.05% and 0.2% GO addition. Microstructural analysis with environmental scanning electron microscopy (ESEM/backscattered mode (BSEM showed that the GO-cement composites had a much denser structure and better crystallized hydration products, meanwhile mercury intrusion porosimetry (MIP testing and image analysis demonstrated that the incorporation of GO in the composites can help in refining capillary pore structure and reducing the air voids content.

  10. Identification of key nitrous oxide production pathways in aerobic partial nitrifying granules.

    Science.gov (United States)

    Ishii, Satoshi; Song, Yanjun; Rathnayake, Lashitha; Tumendelger, Azzaya; Satoh, Hisashi; Toyoda, Sakae; Yoshida, Naohiro; Okabe, Satoshi

    2014-10-01

    The identification of the key nitrous oxide (N2O) production pathways is important to establish a strategy to mitigate N2O emission. In this study, we combined real-time gas-monitoring analysis, (15)N stable isotope analysis, denitrification functional gene transcriptome analysis and microscale N2O concentration measurements to identify the main N2O producers in a partial nitrification (PN) aerobic granule reactor, which was fed with ammonium and acetate. Our results suggest that heterotrophic denitrification was the main contributor to N2O production in our PN aerobic granule reactor. The heterotrophic denitrifiers were probably related to Rhodocyclales bacteria, although different types of bacteria were active in the initial and latter stages of the PN reaction cycles, most likely in response to the presence of acetate. Hydroxylamine oxidation and nitrifier denitrification occurred, but their contribution to N2O emission was relatively small (20-30%) compared with heterotrophic denitrification. Our approach can be useful to quantitatively examine the relative contributions of the three pathways (hydroxylamine oxidation, nitrifier denitrification and heterotrophic denitrification) to N2O emission in mixed microbial populations. © 2014 Society for Applied Microbiology and John Wiley & Sons Ltd.

  11. Direct Synthesis of Methanol by Partial Oxidation of Methane with Oxygen over Cobalt Modified Mesoporous H-ZSM-5 Catalyst

    Directory of Open Access Journals (Sweden)

    Yuni Krisyuningsih Krisnandi

    2015-11-01

    Full Text Available Partial oxidation of methane over mesoporous catalyst cobalt modified H-ZSM-5 has been carried out. Mesoporous Na-ZSM-5 (Si/Al = 35.4 was successfully synthesized using double template method which has high surface area (450 m2/g and average pore diameter distribution of 1.9 nm. The as-synthesized Na-ZSM-5 was converted to H-ZSM-5 through multi-exchange treatment with ammonium ion solution, causing decreased crystallinity and surface area, but increased porous diameter, due to dealumination during treatment process. Moreover, H-ZSM-5 was loaded with cobalt (Co = 2.5% w by the incipient impregnation method and calcined at 550 °C. Partial oxidation of methane was performed in the batch reactor with 0.75 bar methane and 2 bar of nitrogen (with impurities of 0.5% oxygen as the input at various reaction time (30, 60 and 120 min. The reaction results show that cobalt species in catalyst has an important role, because H-ZSM-5 cannot produce methanol in partial oxidation of methane. The presence of molecular oxygen increased the percentage of methanol yield. The reaction is time-dependent with the highest methanol yield (79% was acquired using Co/H-ZSM-5 catalyst for 60 min.

  12. In situ photoemission spectroscopy using synchrotron radiation for O2 translational kinetic energy induced oxidation processes of partially-oxidized Si(001) surfaces

    International Nuclear Information System (INIS)

    Teraoka, Yuden; Yoshigoe, Akitaka

    2001-01-01

    The influence of translational kinetic energy of incident O 2 molecules for the passive oxidation process of partially-oxidized Si(001) surfaces has been studied by photoemission spectroscopy. The translational kinetic energy of O 2 molecules was controlled up to 3 eV by a supersonic seed beam technique using a high temperature nozzle. Two translational kinetic energy thresholds (1.0 eV and 2.6 eV) were found out in accordance with the first-principles calculation for the oxidation of clean surfaces. Si-2p photoemission spectra measured in representative translational kinetic energies revealed that the translational kinetic energy dependent oxidation of dimers and the second layer (subsurface) backbonds were caused by the direct dissociative chemisorption of O 2 molecules. Moreover, the difference in chemical bonds for oxygen atoms was found out to be as low and high binding energy components in O-1s photoemission spectra. Especially, the low binding energy component increased with increasing the translational kinetic energy that indicates the translational kinetic energy induced oxidation in backbonds. (author)

  13. Preparation and Characterization of Plasma-Sprayed Ultrafine Chromium Oxide Coatings

    International Nuclear Information System (INIS)

    Lin Feng; Jiang Xianliang; Yu Yueguang; Zeng Keli; Ren Xianjing; Li Zhenduo

    2007-01-01

    Ultrafine chromium oxide coatings were prepared by plasma spraying with ultrafine feedstock. Processing parameters of plasma spraying were optimized. Optical microscope (OM) was used to observe the microstructure of the ultrafine chromium oxide coatings. Scanning electron microscopy (SEM) was used to observe the morphology and particle size of ultrafine powder feedstock as well as to examine the microstructure of the chromium oxide coating. In addition, hardness and bonding strength of the ultrafine chromium oxide coatings were measured. The results showed that the optimized plasma spraying parameters were suitable for ultrafine chromium oxide coating and the properties and microstructure of the optimized ultrafine chromium oxide coating were superior compared to conventional chromium oxide wear resistant coatings

  14. Microstructure and magnetic properties of yttrium alumina silicate glass microspheres containing iron oxide

    International Nuclear Information System (INIS)

    Sharma, K.; Basak, C.B.; Prajapat, C.L.; Singh, M.R.

    2015-01-01

    Yttrium alumino-silicate glass microspheres have been used for localized delivery of high radiation dose to tissues in the treatment of hepatocellular carcinoma (BCC) and synovitis. 90 Y is a pure beta emitter with beta emission energy of 0.9367 MeV, average penetration range in tissue 2.5 mm, physical half-life of 64.2 h, thus an effective radioisotope for delivering high radiation dose to the tumor. The efficacy of radiotherapy can further be improved if the glass microspheres are doped with magnetic particles for targeted delivery of high radiation dose. Magnetic glass microspheres can also be utilized for cancer treatment using the magnetic heating of tumor cell. The magnetic glass microspheres are obtained from the glasses with nominal composition (64-x) SiO 2 -17Y 2 O 3 -19 Al 2 O 3 -xFe 2 O 3 (x=4-16 mol %). Density of glasses increases from 3.5g/cc to 3.8g/cc as iron oxide content is increased from 4 to 16 mol %. The glass transition temperature and peak crystallization temperature decreases as the iron oxide content increases. T g values of glass samples decreases with increase of Fe 2 O 3 , while SiO 2 content is decreased. SiO 2 is a network forming oxide and a decrease in the network former in glass lead to decrease in thermo-physical properties like T g . The development of ferrimagnetic crystallites in glasses arise from the conversion of iron oxide into magnetite, magnemite and hematite, which is influenced by the structural and ordering of magnetic particles. The microstructure of glass-ceramic exhibited the formation of 50-100 nm size particles. The magnetite and hematite are formed as major crystalline phases. The magnetization values increased with an increase of iron oxide content and attributed to formation of magnetite phase. Results have shown that the glass microspheres with magnetic properties can be used as potential materials for cancer treatment. (author)

  15. Synthesis and Microstructural Characterization of Manganese Oxide Electrodes for Application as Electrochemical Supercapacitors

    Science.gov (United States)

    Babakhani, Banafsheh

    by the composition and pH of the electrolyte, temperature, current density and polymer deposition time. Mn oxide/PEDOT coaxial core/shell rods consisted of MnO2 with an antifluorite-type structure coated with amorphous PEDOT. The Mn oxide/PEDOT coaxial core/shell electrodes prepared by the sequential method showed significantly better specific capacity and redox performance properties relative to both uncoated Mn oxide rods and co- electrodeposited Mn oxide/PEDOT electrodes. The best specific capacitance for Mn oxide/PEDOT rods produced sequentially was ˜295 F g-1 with ˜92% retention after 250 cycles in 0.5 M Na2SO4 at 100 mV s-1. To further improve the electrochemical capacitive behavior of Mn oxide electrodes, Co-doped and Fe-doped Mn oxide electrodes with a rod-like morphology and antifluorite-type crystal structure were synthesized by anodic electrodeposition, on Au coated Si substrates, from dilute solutions of Mn acetate and Co sulphate and Mn acetate and Fe chloride. Also, Mn-Co oxide/PEDOT coaxial core/shell rods were synthesized by applying a shell of PEDOT on Mn-Co oxide electrodes. Mn-Co oxide/PEDOT electrodes consisted of MnO2, with partial Co 2+ and Co3+ ion substitution for Mn4+, and amorphous PEDOT. Mn-Fe oxide electrodes consisted of MnO2, with partial Fe2+ and Fe3+ ion substitution for Mn4+. Electrochemical analysis showed that the capacitance values for all deposits increased with increasing scan rate to 100 mVs -1, and then decreased after 100 mVs-1. The Mn-Co oxide/PEDOT electrodes showed improved specific capacity and electrochemical cyclability relative to uncoated Mn-Co oxides and Mn-Fe oxides. Mn-Co oxide/PEDOT electrodes with rod-like structures had high capacitances (up to 310 Fg -1) at a scan rate of 100 mVs-1 and maintained their capacitance after 500 cycles in 0.5 M Na2SO4 (91% retention). Capacitance reduction for the deposits was mainly due to the loss of Mn ions by dissolution in the electrolyte solution. To better understand the

  16. Catalytic partial oxidation of methane over porous silica supported VO{sub x} catalysts

    Energy Technology Data Exchange (ETDEWEB)

    Pirovano, C.; Schoenborn, E.; Kalevaru, V.N.; Wohlrab, S.; Luecke, B.; Martin, A. [University Rostock e.V., Rostock (Germany). Leibniz Inst. for Catalysis

    2011-07-01

    High surface area mesoporous siliceous MCM-41 and SBA-15 materials have been used as supports to disperse vanadium oxide species using wet impregnation and incipient wetness impregnation methods. These materials were used as catalysts for the partial oxidation of methane (POM) to formaldehyde. The physico-chemical properties of the solids were studied by means of BET, DR-UV/Vis spectroscopy, Py-FTIR and TEM. The influence of support and the preparation method on the dispersion of VOx is also investigated. The catalytic properties of the catalysts were examined in a fixed bed stainless steel reactor at 923 K. So far a maximum production of formaldehyde can be detected on SBA-15 supported VOx-catalysts prepared by incipient wetness impregnation. On this V/SBA-15 material a covalent attachment of catalytic active molecular vanadium species dominates, which in turn leads to a lower activation temperature and thereby reduced over-oxidation. From the best case, the space time yield of HCHO could be reached close to 775 g{sub HCHO} Kg{sub cat}{sup -1} h{sup -1}. (orig.)

  17. Microstructural evolution and some mechanical properties of nanosized yttrium oxide dispersion strengthened 13Cr steel

    International Nuclear Information System (INIS)

    Nguyen, Van Tich; Doan, Dinh Phuong; Tran, Tran BaoTrung; Luong, Van Duong; Nguyen, Van An; Phan, Anh Tu

    2010-01-01

    Oxide dispersion strengthened (ODS) steels, manufactured by a mechanical alloying method, during the past few years, appear to be promising candidates for structural applications in nuclear power plants. The purpose of this work is to elaborate the manufacturing processes of ODS 13Cr steel with the addition of 1.0 wt% yttrium oxide through the powder metallurgy route using the high energy ball mill. Microstructural analysis by scanning electron microscopy (SEM), x-ray diffraction (XRD) and hardness testing have been used to optimize the technological parameters of milling, hot isostatic pressing and heat-treatment processes. The steel hardness increases with decreasing particle size of 13Cr ODS steel. The best hardness was obtained from more than 70 h of milling in the two tanks planetary ball mill or 30 h of milling in the one tank planetary ball mill and hot isostatic pressing at 1150 °C . The particle size of the steel is less than 100 nm, and the density and hardness are about 7.3 g cm −3 and 490 HB, respectively

  18. Microstructure refinement and strengthening mechanisms of a 9Cr oxide dispersion strengthened steel by zirconium addition

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Hai Jian; Lu, Zheng; Wang, Dong Mei; Liu, Chunming [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), School of Materials Science and Engineering, Northeastern University, Shenyang (China)

    2017-02-15

    To study the effects of zirconium (Zr) addition on the microstructure, hardness and the tensile properties of oxide dispersion strengthened (ODS) ferritic-martensitic steels, two kinds of 9Cr-ODS ferritic-martensitic steels with nominal compositions (wt.%) of Fe-9Cr-2W-0.3Y{sub 2}O-3 and Fe-9Cr-2W-0.3Zr-0.3Y{sub 2}O{sub 3} were fabricated by the mechanical alloying (MA) of premixed powders and then consolidated by hot isostatic pressing (HIP) techniques. The experimental results showed that the average grain size decreases with Zr addition. The trigonal δ-phase Y{sub 4}Zr{sub 3}O{sub 12} oxides and body-centered cubic Y{sub 2}O{sub 3} oxides are formed in the 9Cr-Zr-ODS steel and 9Cr non-Zr ODS steel, respectively, and the average size of Y{sub 4}Zr{sub 3}O{sub 12} particles is much smaller than that of Y{sub 2}O{sub 3}. The dispersion morphology of the oxide particles in 9Cr-Zr-ODS steel is significantly improved and the number density is 1.1 x 10{sup 23}/m{sup 3} with Zr addition. The 9Cr-Zr-ODS steel shows much higher tensile ductility, ultimate tensile strength and Vickers hardness at the same time.

  19. Effects of Chilling and Partial Freezing on Rigor Mortis Changes of Bighead Carp (Aristichthys nobilis) Fillets: Cathepsin Activity, Protein Degradation and Microstructure of Myofibrils.

    Science.gov (United States)

    Lu, Han; Liu, Xiaochang; Zhang, Yuemei; Wang, Hang; Luo, Yongkang

    2015-12-01

    To investigate the effects of chilling and partial freezing on rigor mortis changes in bighead carp (Aristichthys nobilis), pH, cathepsin B, cathepsin B+L activities, SDS-PAGE of sarcoplasmic and myofibrillar proteins, texture, and changes in microstructure of fillets at 4 °C and -3 °C were determined at 0, 2, 4, 8, 12, 24, 48, and 72 h after slaughter. The results indicated that pH of fillets (6.50 to 6.80) was appropriate for cathepsin function during the rigor mortis. For fillets that were chilled and partially frozen, the cathepsin activity in lysosome increased consistently during the first 12 h, followed by a decrease from the 12 to 24 h, which paralleled an increase in activity in heavy mitochondria, myofibrils and sarcoplasm. There was no significant difference in cathepsin activity in lysosomes between fillets at 4 °C and -3 °C (P > 0.05). Partially frozen fillets had greater cathepsin activity in heavy mitochondria than chilled samples from the 48 to 72 h. In addition, partially frozen fillets showed higher cathepsin activity in sarcoplasm and lower cathepsin activity in myofibrils compared with chilled fillets. Correspondingly, we observed degradation of α-actinin (105 kDa) by cathepsin L in chilled fillets and degradation of creatine kinase (41 kDa) by cathepsin B in partially frozen fillets during the rigor mortis. The decline of hardness for both fillets might be attributed to the accumulation of cathepsin in myofibrils from the 8 to 24 h. The lower cathepsin activity in myofibrils for fillets that were partially frozen might induce a more intact cytoskeletal structure than fillets that were chilled. © 2015 Institute of Food Technologists®

  20. Interfacial microstructure of partial transient liquid phase bonded Si3N4-to-Inconel 718 joints

    International Nuclear Information System (INIS)

    Kim, Jae Joong; Park, Jin-Woo; Eagar, Thomas W.

    2003-01-01

    This work presents transmission electron microscopy (TEM) analysis of the interfacial microstructure in Si 3 N 4 -to-Inconel 718 joints with Ni interlayers produced by partial transient liquid phase bonding (PTLPB). Ti and Cu microfoils have been inserted between Si 3 N 4 and the Ni interlayer and joining has been performed at lower temperatures than previous PTLPBs of Si 3 N 4 with the same insert metals. The TEM work is focused on phase identification of the reaction layers between the Si 3 N 4 and the Ni interlayer. According to the TEM analysis, most of the Cu precipitates without reacting with Ti and Ni. Si diffused in the filler metal and thin reaction layer formed at the interface between Si 3 N 4 and the filler metal producing good bond-formation and hence, high interfacial strength. No interfacial fractures occurred after cooling from the bonding temperature of 900 deg. C, which supports the results observed in the TEM analysis. This work confirms that this joining process can produce a more heat resistant Si 3 N 4 -to-Inconel 718 joint than active brazing using Ag-Cu-Ti alloys

  1. Multi-length scale tomography for the determination and optimization of the effective microstructural properties in novel hierarchical solid oxide fuel cell anodes

    Science.gov (United States)

    Lu, Xuekun; Taiwo, Oluwadamilola O.; Bertei, Antonio; Li, Tao; Li, Kang; Brett, Dan J. L.; Shearing, Paul R.

    2017-11-01

    Effective microstructural properties are critical in determining the electrochemical performance of solid oxide fuel cells (SOFCs), particularly when operating at high current densities. A novel tubular SOFC anode with a hierarchical microstructure, composed of self-organized micro-channels and sponge-like regions, has been fabricated by a phase inversion technique to mitigate concentration losses. However, since pore sizes span over two orders of magnitude, the determination of the effective transport parameters using image-based techniques remains challenging. Pioneering steps are made in this study to characterize and optimize the microstructure by coupling multi-length scale 3D tomography and modeling. The results conclusively show that embedding finger-like micro-channels into the tubular anode can improve the mass transport by 250% and the permeability by 2-3 orders of magnitude. Our parametric study shows that increasing the porosity in the spongy layer beyond 10% enhances the effective transport parameters of the spongy layer at an exponential rate, but linearly for the full anode. For the first time, local and global mass transport properties are correlated to the microstructure, which is of wide interest for rationalizing the design optimization of SOFC electrodes and more generally for hierarchical materials in batteries and membranes.

  2. Evolution of microstructure, strain and physical properties in oxide nanocomposite films.

    Science.gov (United States)

    Chen, Aiping; Weigand, Marcus; Bi, Zhenxing; Zhang, Wenrui; Lü, Xuejie; Dowden, Paul; MacManus-Driscoll, Judith L; Wang, Haiyan; Jia, Quanxi

    2014-06-24

    We, using LSMO:ZnO nanocomposite films as a model system, have studied the effect of film thickness on the physical properties of nanocomposites. It shows that strain, microstructure, as well as magnetoresistance strongly rely on film thickness. The magnetotransport properties have been fitted by a modified parallel connection channel model, which is in agreement with the microstructure evolution as a function of film thickness in nanocomposite films on sapphire substrates. The strain analysis indicates that the variation of physical properties in nanocomposite films on LAO is dominated by strain effect. These results confirm the critical role of film thickness on microstructures, strain states, and functionalities. It further shows that one can use film thickness as a key parameter to design nanocomposites with optimum functionalities.

  3. Effects of dissolved oxygen and pH on nitrous oxide production rates in autotrophic partial nitrification granules.

    Science.gov (United States)

    Rathnayake, Rathnayake M L D; Oshiki, Mamoru; Ishii, Satoshi; Segawa, Takahiro; Satoh, Hisashi; Okabe, Satoshi

    2015-12-01

    The effects of dissolved oxygen (DO) and pH on nitrous oxide (N2O) production rates and pathways in autotrophic partial nitrification (PN) granules were investigated at the granular level. N2O was primarily produced by betaproteobacterial ammonia-oxidizing bacteria, mainly Nitrosomonas europaea, in the oxic surface layer (production increased with increasing bulk DO concentration owing to activation of the ammonia (i.e., hydroxylamine) oxidation in this layer. The highest N2O emissions were observed at pH 7.5, although the ammonia oxidation rate was unchanged between pH 6.5 and 8.5. Overall, the results of this study suggest that in situ analyses of PN granules are essential to gaining insight into N2O emission mechanisms in a granule. Copyright © 2015 Elsevier Ltd. All rights reserved.

  4. Multiscale Transient and Steady-State Study of the Influence of Microstructure Degradation and Chromium Oxide Poisoning on Solid Oxide Fuel Cell Cathode Performance

    Science.gov (United States)

    Li, Guanchen; von Spakovsky, Michael R.; Shen, Fengyu; Lu, Kathy

    2018-01-01

    Oxygen reduction in a solid oxide fuel cell cathode involves a nonequilibrium process of coupled mass and heat diffusion and electrochemical and chemical reactions. These phenomena occur at multiple temporal and spatial scales, making the modeling, especially in the transient regime, very difficult. Nonetheless, multiscale models are needed to improve the understanding of oxygen reduction and guide cathode design. Of particular importance for long-term operation are microstructure degradation and chromium oxide poisoning both of which degrade cathode performance. Existing methods are phenomenological or empirical in nature and their application limited to the continuum realm with quantum effects not captured. In contrast, steepest-entropy-ascent quantum thermodynamics can be used to model nonequilibrium processes (even those far-from equilibrium) at all scales. The nonequilibrium relaxation is characterized by entropy generation, which can unify coupled phenomena into one framework to model transient and steady behavior. The results reveal the effects on performance of the different timescales of the varied phenomena involved and their coupling. Results are included here for the effects of chromium oxide concentrations on cathode output as is a parametric study of the effects of interconnect-three-phase-boundary length, oxygen mean free path, and adsorption site effectiveness. A qualitative comparison with experimental results is made.

  5. Steam and partial oxidation reforming options for hydrogen production from fossil fuels for PEM fuel cells

    Directory of Open Access Journals (Sweden)

    Yousri M.A. Welaya

    2012-06-01

    Full Text Available Proton exchange membrane fuel cell (PEM generates electrical power from air and from hydrogen or hydrogen rich gas mixtures. Therefore, there is an increasing interest in converting current hydrocarbon based marine fuels such as natural gas, gasoline, and diesel into hydrogen rich gases acceptable to the PEM fuel cells on board ships. Using chemical flow sheeting software, the total system efficiency has been calculated. Natural gas appears to be the best fuel for hydrogen rich gas production due to its favorable composition of lower molecular weight compounds. This paper presents a study for a 250 kW net electrical power PEM fuel cell system utilizing a partial oxidation in one case study and steam reformers in the second. This study has shown that steam-reforming process is the most competitive fuel processing option in terms of fuel processing efficiency. Partial oxidation process has proved to posses the lowest fuel processing efficiency. Among the options studied, the highest fuel processing efficiency is achieved with natural gas steam reforming system.

  6. Effect of ZnO on phase emergence, microstructure and surface modifications of calcium phosphosilicate glass/glass-ceramics having iron oxide

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, K.; Dixit, A.; Bhattacharya, S.; Jagannath [Technical Physics and Prototype Engineering Division, Bhabha Atomic Research Centre, Mumbai 400 085 (India); Deo, M.N. [High Pressure Physics Division, Bhabha Atomic Research Centre, Mumbai 400 085 (India); Kothiyal, G.P., E-mail: gpkoth@barc.gov.in [Technical Physics and Prototype Engineering Division, Bhabha Atomic Research Centre, Mumbai 400 085 (India)

    2010-03-01

    The effect of ZnO on phase emergence and microstructure properties of glass and glass-ceramics with composition 25SiO{sub 2}-50CaO-15P{sub 2}O{sub 5}-(10 - x)Fe{sub 2}O{sub 3}-xZnO (where x = 0, 2, 5, 7 mol%) has been studied. They have been characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). Surface modifications of these glass-ceramics in simulated body fluid have been studied using Fourier transform infrared reflection spectroscopy (FTIR), XPS and SEM. Results have shown a decrease in the fraction of non-bridging oxygen with increase in zinc oxide content. Emergence of crystalline phases in glass-ceramics at different heat treatment temperatures was studied using XRD. When glass is heat treated at 800 deg. C calcium phosphate, hematite and magnetite are developed as major phases in the glass-ceramics samples with ZnO up to 5 mol%. In addition to these, calcium silicate (Ca{sub 3}Si{sub 2}O{sub 7}) phase is also observed when glass is heat treated at 1000 deg. C. The microstructure of the glass-ceramics heat treated at 800 deg. C exhibits the formation of nano-size (40-50 nm) grains. On heat treatment at 1000 deg. C crystallites grow to above 50 nm size and more than one phase are observed in the microstructure. The formation of thin flake-like structure with coarse particles is observed at high zinc oxide concentration (x = 7 mol%). In vitro studies have shown the surface modifications and formation of Ca-P-rich layer on the glass-ceramics when immersed in simulated body fluids (SBF) for different durations. The bioactive response was found to depend on ZnO content.

  7. Effect of ZnO on phase emergence, microstructure and surface modifications of calcium phosphosilicate glass/glass-ceramics having iron oxide

    International Nuclear Information System (INIS)

    Sharma, K.; Dixit, A.; Bhattacharya, S.; Jagannath; Deo, M.N.; Kothiyal, G.P.

    2010-01-01

    The effect of ZnO on phase emergence and microstructure properties of glass and glass-ceramics with composition 25SiO 2 -50CaO-15P 2 O 5 -(10 - x)Fe 2 O 3 -xZnO (where x = 0, 2, 5, 7 mol%) has been studied. They have been characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). Surface modifications of these glass-ceramics in simulated body fluid have been studied using Fourier transform infrared reflection spectroscopy (FTIR), XPS and SEM. Results have shown a decrease in the fraction of non-bridging oxygen with increase in zinc oxide content. Emergence of crystalline phases in glass-ceramics at different heat treatment temperatures was studied using XRD. When glass is heat treated at 800 deg. C calcium phosphate, hematite and magnetite are developed as major phases in the glass-ceramics samples with ZnO up to 5 mol%. In addition to these, calcium silicate (Ca 3 Si 2 O 7 ) phase is also observed when glass is heat treated at 1000 deg. C. The microstructure of the glass-ceramics heat treated at 800 deg. C exhibits the formation of nano-size (40-50 nm) grains. On heat treatment at 1000 deg. C crystallites grow to above 50 nm size and more than one phase are observed in the microstructure. The formation of thin flake-like structure with coarse particles is observed at high zinc oxide concentration (x = 7 mol%). In vitro studies have shown the surface modifications and formation of Ca-P-rich layer on the glass-ceramics when immersed in simulated body fluids (SBF) for different durations. The bioactive response was found to depend on ZnO content.

  8. Analytical Tem Comparisons of Stress-Corrosion-Crack Microstructures in Alloy 600 under Steam-Generator Service and Laboratory Test Conditions

    International Nuclear Information System (INIS)

    Thomas, L.E.; Bruemmer, S.M.; Scott, P.M.

    2002-01-01

    High-resolution analytical transmission electron microscopy (ATEM) has been used to characterize stress-corrosion cracks (SCC) in Alloy 600 steam-generator (SG) tubing from tests with caustic and acid-sulfate solutions. The aim of this work was to identify the microstructural and microchemical signatures of intergranular attack and cracking produced under well-controlled test conditions in order to determine the local environments promoting degradation in service. Cross-sectioned cracks and crack tips were examined in samples of mill-annealed alloy 600 tested in concentrated caustic and acid-sulfate solutions at 320 C. Characteristic microstructures observed in the caustic (10% NaOH) test sample included deeply penetrative attack along crack-intersected grain boundaries, with Cr-rich spinel and NiO structure oxides ranging from random nanocrystalline to oriented epitaxial films filling cracks up to the tips. Sodium was readily detectable in the oxides (up to 5 wt.% in the spinel corrosion product) along with S and Cu enrichment at crack-wall metal/oxide interfaces and local attack of the metal matrix around IG carbide particles. In the sulfate (Na 2 SO 4 + FeSO 4 ) test sample, the grain boundaries were also deeply attacked/cracked. Epitaxial NiO-structure oxide formed on the crack walls and S, sometimes with Cu, was concentrated between the oriented oxide layers rather than along the metal/oxide interfaces. Carbides were attacked and partially converted to fine-grained oxide containing up to several percent S. Observations of crack tips in the acid sulfate sample also revealed nm-wide cracks preceding the oxide along grain boundaries. The SCC structures produced in the laboratory tests differed in most details from the secondary-side SCC structures observed in pulled SG tubes. Important differences included the oxide morphologies, the presence of easily detectable Na and absence of sulfides in the test samples, different types of attack on IG carbide particles

  9. Investigation of partial oxidation of hydrogen sulfide for dry desulfurisation of fuel gases; Untersuchung der Partialoxidation von Schwefelwasserstoff zur Trockenentschwefelung von Brenngasen

    Energy Technology Data Exchange (ETDEWEB)

    Kliemczak, U.

    2002-07-01

    Three process variants for direct desulfurisation in the dry state of coal gasification gases by partial oxidation of H{sub 2}S were investigated in Prenflo conditions: 1. Heterogeneously catalyzed partial oxidation of H{sub 2}S on fly dust followed by sulfur deposition on the dust; 2. Non-catalyzed partial oxidation of H{sub 2}S in a homogeneous gaseous phase followed by sulfur deposition in a spray separator; 3. Heterogeneously catalyzed partial oxidation of H{sub 2}S in a fixed bed. The experiments were carried out in conditions similar to the crude gas conditions of slag bath gasification at SVZ Schwarze Pumpe. The fixed bed materials investigated were hearth furnace coke, Berl saddles, and an activated carbon developed specially for the investigations, Oxorbon CJ. The focus of the investigations was on the envisaged continuous operation of the process. [German] Im Rahmen der vorliegenden Arbeit wurde an einer zu diesem Zweck modifizierten Technikumsanlage die trockene Direktentschwefelung von Brenngasen aus der Kohlevergasung durch partielle Oxidation von H{sub 2}S untersucht. Im Vordergrund standen zwei Verfahrensvarianten, deren Eignung fuer die Bedingungen der Prenflo-Vergasung ueberprueft werden sollte: Variante 1: die heterogen katalysierte Partialoxidation von H{sub 2}S an Flugstaub mit anschliessender Schwefelabscheidung auf dem Staub und, Variante 2: die nichtkatalysierte Partialoxidation von H{sub 2}S in homogener Gasphase mit anschliessender Schwefelabscheidung in einem Spruehabscheider. Ausgehend von den Versuchsergebnissen der Verfahrensvarianten 1 und 2 wurde zusaetzlich als Verfahrensvariante 3 die heterogen katalysierte Partialoxidation von H{sub 2}S am Festbett untersucht. Diese Versuche orientierten sich an den Rohgasbedingungen der Schlackebadvergasung des SVZ Schwarze Pumpe. Als Festbettmaterialien kamen Herdofenkoks, Berlsaettel und eine, speziell fuer diese Verfahrensvariante entwickelte Aktivkohle Oxorbon CJ, zum Einsatz. Die Eignung des

  10. Oxidation and creep failure of alloy 617 foils at high temperature

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, S.K.; Ko, G.D.; Li, F.X. [Department of Mechanical Engineering, Chonnam National University, Gwangju 500 757 (Korea, Republic of); Kang, K.J. [Department of Mechanical Engineering, Chonnam National University, Gwangju 500 757 (Korea, Republic of)], E-mail: kjkang@chonnam.ac.kr

    2008-08-31

    The microstructure of thermally grown oxides (TGO) and the creep properties of alloy 617 were investigated. Oxidation and creep tests were performed on 100 {mu}m thick foils at 800-1000 deg. C in air environment, while the thickness of TGO was monitored in situ. According to energy dispersive X-ray (EDX) mapping micrographs observation, superficial dense oxides, chromia (Cr{sub 2}O{sub 3}), which was thermodynamically unstable at 1000 deg. C, and discrete internal oxides, alumina ({alpha}-Al{sub 2}O{sub 3}), were found. Consequently, the weight of the foil specimen decreased due to the spalling and volatilization of the Cr{sub 2}O{sub 3} oxide layer after an initial weight-gaining. Secondary and tertiary creeps were observed at 800 deg. C, while the primary, secondary and tertiary creeps were observed at 1000 deg. C. Dynamic recrystallization occurred at 800 deg. C and 900 deg. C, while partial dynamic recrystallization at 1000 deg. C. The apparent activation energy, Q{sub app}, for the creep deformation was 271 kJ/mol, which was independent of the applied stress.

  11. Effect of initial as-cast microstructure on semisolid microstructure of AZ91D alloy during the strain-induced melt activation process

    International Nuclear Information System (INIS)

    Wang, J.G.; Lin, H.Q.; Li, Y.Q.; Jiang, Q.C.

    2008-01-01

    The effects of different as-cast microstructures which were initially cast in graphite, metal, sand and firebrick moulds, respectively on the semisolid microstructure of AZ91D alloy, have been investigated during the strain-induced melt activation (SIMA) process. The experimental results showed that the moulds with high cooling capacity could produce the fine-grained as-cast microstructure in which the fine α-Mg dendrites were surrounded by a narrow layer of eutectic mixtures. After compressive deformation, in the fine-grained as-cast microstructure, the more systemic strain energy would be gradually accumulated and abundantly stored due to uniform inner crystal lattice distortion, so the recrystallization was easily induced by the stored strain energy at the elevated temperature. As a channel for the diffusion of atoms, the subgrain boundary along which Al element was enriched, foremost melted above the eutectic temperature and resulted in the separation of neighboring subgrains from primary dendrites. Therefore, the refining role of recrystallization on the microstructural evolution from dendrite to globular particles in morphology was easier to play in the fine-grained as-cast microstructure, which was advantageous for the production of fine-grained semisolid microstructure. Additionally, in the fine-grained as-cast microstructure, the melting fracture of narrow secondary dendritic arms was easy to occur in their roots, which also attributed to the production of fine globular grains in semisolid microstructure from primary dendrites. The finer dendrites in the initial as-cast alloy could evolve into the finer globular grains with relatively small grain size distribution range in the semisolid microstructure during partial remelting; therefore, the finer the dendrites in the initial as-cast microstructure, the better were the tensile properties of the evolved semisolid microstructure

  12. Influences of Cr content and PWHT on microstructure and oxidation behavior of stainless steel weld overlay cladding materials in high temperature water

    Energy Technology Data Exchange (ETDEWEB)

    Cao, X.Y.; Ding, X.F. [National Center for Materials Service Safety, University of Science and Technology Beijing, 30 Xueyuan Road, 100083 Beijing (China); Lu, Y.H., E-mail: lu_yonghao@mater.ustb.edu.cn [National Center for Materials Service Safety, University of Science and Technology Beijing, 30 Xueyuan Road, 100083 Beijing (China); Zhu, P. [Suzhou Nuclear Power Research Institute Co. Ltd., 1788 Xihuan Road, 215004 Suzhou (China); Shoji, T. [National Center for Materials Service Safety, University of Science and Technology Beijing, 30 Xueyuan Road, 100083 Beijing (China); Fracture and Reliability Research Institute, Tohoku University, 6-6-01 Aramaki Aoba, Aoba-ku, Sendai City 980-8579 (Japan)

    2015-12-15

    Influences of Cr content and post weld heat treatment (PWHT) on microstructure and oxidation behavior of stainless steel cladding materials in high temperature water were investigated. The amounts of metal oxidized and dissolved were estimated to compare the oxidation behaviors of cladding materials with different Cr contents and PWHT. The results indicated that higher Cr content led to formation of more ferrite content, and carbides were found along δ/γ phase interface after PWHT. Higher Cr content enhanced the pitting resistance and compactness of the oxide film to reduce metal amount oxidized and dissolved, which mitigated the weight changes and the formation of Fe-rich oxides. PWHT promoted more and deeper pitting holes along the δ/γ phase interface due to formation of carbides, which resulted in an increase in metal amount oxidized and dissolved, and were also responsible for more Fe-rich oxides and higher weight changes. - Highlights: • The amounts of metal oxidized and metal dissolved were estimated. • Higher Cr content increased ferrite content and PWHT led to formation of carbides. • PWHT promoted more and deeper pitting holes along the δ/γ phase interface. • Lower Cr content and PWHT promoted the metal amounts oxidized and dissolved. • Lower Cr content and PWHT increased weight changes and Fe-rich film formation.

  13. Influence of Ti Content on the Partial Oxidation of TixFeCoNi Thin Films in Vacuum Annealing

    Directory of Open Access Journals (Sweden)

    Ya-Chu Yang

    2017-09-01

    Full Text Available This study investigated the effects of Ti content and vacuum annealing on the microstructure evolution of TixFeCoNi (x = 0, 0.5, and 1 thin films and the underlying mechanisms. The as-deposited thin film transformed from an FCC (face center cubic structure at x = 0 into an amorphous structure at x = 1, which can be explained by determining topological instability and a hard ball model. After annealing was performed at 1000 °C for 30 min, the films presented a layered structure comprising metal solid solutions and oxygen-deficient oxides, which can be major attributed to oxygen traces in the vacuum furnace. Different Ti contents provided various phase separation and layered structures. The underlying mechanism is mainly related to the competition among possible oxides in terms of free energy production at 1000 °C.

  14. A novel partial SOI LDMOSFET with periodic buried oxide for breakdown voltage and self heating effect enhancement

    Science.gov (United States)

    Jamali Mahabadi, S. E.; Rajabi, Saba; Loiacono, Julian

    2015-09-01

    In this paper a partial silicon on insulator (PSOI) lateral double diffused metal oxide semiconductor field effect transistor (LDMOSFET) with periodic buried oxide layer (PBO) for enhancing breakdown voltage (BV) and self-heating effects (SHEs) is proposed for the first time. This new structure is called periodic buried oxide partial silicon on insulator (PBO-PSOI). In this structure, periodic small pieces of SiO2 were used as the buried oxide (BOX) layer in PSOI to modulate the electric field in the structure. It was demonstrated that the electric field is distributed more evenly by producing additional electric field peaks, which decrease the common peaks near the drain and gate junctions in the PBO-PSOI structure. Hence, the area underneath the electric field curve increases which leads to higher breakdown voltage. Also a p-type Si window was introduced in the source side to force the substrate to share the vertical voltage drop, leading to a higher vertical BV. Furthermore, the Si window under the source and those between periodic pieces of SiO2 create parallel conduction paths between the active layer and substrate thereby alleviating the SHEs. Simulations with the two dimensional ATLAS device simulator from the Silvaco suite of simulation tools show that the BV of PBO-PSOI is 100% higher than that of the conventional partial SOI (C-PSOI) structure. Furthermore the PBO-PSOI structure alleviates SHEs to a greater extent than its C-PSOI counterpart. The achieved drain current for the PBO-PSOI structure (100 μA), at drain-source voltage of VDS = 100 V and gate-source voltage of VGS = 25 V, is shown to be significantly larger than that in C-PSOI and fully depleted SOI (FD-SOI) structures (87 μA and 51 μA respectively). Drain current can be further improved at the expense of BV by increasing the doping of the drift region.

  15. Microstructural characterization of catalysis product of nanocement based materials: A review

    Science.gov (United States)

    Sutan, Norsuzailina Mohamed; Izaitul Akma Ideris, Nur; Taib, Siti Noor Linda; Lee, Delsye Teo Ching; Hassan, Alsidqi; Kudnie Sahari, Siti; Mohamad Said, Khairul Anwar; Rahman Sobuz, Habibur

    2018-03-01

    Cement as an essential element for cement-based products contributed to negative environmental issues due to its high energy consumption and carbon dioxide emission during its production. These issues create the need to find alternative materials as partial cement replacement where studies on the potential of utilizing silica based materials as partial cement replacement come into picture. This review highlights the effectiveness of microstructural characterization techniques that have been used in the studies that focus on characterization of calcium hydroxide (CH) and calcium silicate hydrate (C-S-H) formation during hydration process of cement-based product incorporating nano reactive silica based materials as partial cement replacement. Understanding the effect of these materials as cement replacement in cement based product focusing on the microstructural development will lead to a higher confidence in the use of industrial waste as a new non-conventional material in construction industry that can catalyse rapid and innovative advances in green technology.

  16. Microstructural characterization of catalysis product of nanocement based materials: A review

    Directory of Open Access Journals (Sweden)

    Mohamed Sutan Norsuzailina

    2018-01-01

    Full Text Available Cement as an essential element for cement-based products contributed to negative environmental issues due to its high energy consumption and carbon dioxide emission during its production. These issues create the need to find alternative materials as partial cement replacement where studies on the potential of utilizing silica based materials as partial cement replacement come into picture. This review highlights the effectiveness of microstructural characterization techniques that have been used in the studies that focus on characterization of calcium hydroxide (CH and calcium silicate hydrate (C-S-H formation during hydration process of cement-based product incorporating nano reactive silica based materials as partial cement replacement. Understanding the effect of these materials as cement replacement in cement based product focusing on the microstructural development will lead to a higher confidence in the use of industrial waste as a new non-conventional material in construction industry that can catalyse rapid and innovative advances in green technology.

  17. Microstructure and Mechanical Properties of TIG Weld Joint of ZM5 Magnesium Alloy

    Directory of Open Access Journals (Sweden)

    QIN Ren-yao

    2016-06-01

    Full Text Available The ZM5 magnesium alloy plates were welded by TIG welding method. The microstructural characteristics and mechanical properties of ZM5 magnesium alloy joint were studied by optical microscopy, microhardness and tensile testers. The results show that the TIG weld joint of ZM5 magnesium alloy is composed of heat affected zone, partially melted zone and weld metal. The heat affected zone is consisted of primary α-Mg phase and eutectic phase that is composed of eutectic α-Mg and eutectic β-Mg17Al12 phase and mainly precipitated at grain boundaries. In the partially melted zone, the eutectic phase is not only increasingly precipitated at grain boundaries, but also dispersed in grains, and the growth of the β-Mg17Al12 phase is obviously observed. The microstructure in the weld is the typical dendritic morphology. The dendrites are considered as primary α-Mg phase, and the interdendritic regions are α+β eutectic phase. The difference in the microstructure of the heat affected zone, partially melted zone and weld results in their various microhardness values, and leads to the smaller tensile strength and ductility in the ZM5 alloy weld joint than parent metal.

  18. Oxidation of trichloroethylene, toluene, and ethanol vapors by a partially saturated permeable reactive barrier

    Science.gov (United States)

    Mahmoodlu, Mojtaba G.; Hassanizadeh, S. Majid; Hartog, Niels; Raoof, Amir

    2014-08-01

    The mitigation of volatile organic compound (VOC) vapors in the unsaturated zone largely relies on the active removal of vapor by ventilation. In this study we considered an alternative method involving the use of solid potassium permanganate to create a horizontal permeable reactive barrier for oxidizing VOC vapors. Column experiments were carried out to investigate the oxidation of trichloroethylene (TCE), toluene, and ethanol vapors using a partially saturated mixture of potassium permanganate and sand grains. Results showed a significant removal of VOC vapors due to the oxidation. We found that water saturation has a major effect on the removal capacity of the permeable reactive layer. We observed a high removal efficiency and reactivity of potassium permanganate for all target compounds at the highest water saturation (Sw = 0.6). A change in pH within the reactive layer reduced oxidation rate of VOCs. The use of carbonate minerals increased the reactivity of potassium permanganate during the oxidation of TCE vapor by buffering the pH. Reactive transport of VOC vapors diffusing through the permeable reactive layer was modeled, including the pH effect on the oxidation rates. The model accurately described the observed breakthrough curve of TCE and toluene vapors in the headspace of the column. However, miscibility of ethanol in water in combination with produced water during oxidation made the modeling results less accurate for ethanol. A linear relationship was found between total oxidized mass of VOC vapors per unit volume of permeable reactive layer and initial water saturation. This behavior indicates that pH changes control the overall reactivity and longevity of the permeable reactive layer during oxidation of VOCs. The results suggest that field application of a horizontal permeable reactive barrier can be a viable technology against upward migration of VOC vapors through the unsaturated zone.

  19. A DRIFTS study of the partial oxidation of ethanol on Rh catalysts; Estudo da oxidacao parcial do etanol em catalisadores de Rh por DRIFTS

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, Raquel Lima; Passos, Fabio Barboza, E-mail: fbpassos@vm.uff.br [Universidade Federal Fluminense (UFF), Niteroi, RJ (Brazil). Departamento de Engenharia Quimica e de Petroleo

    2013-09-01

    The partial oxidation of ethanol on {gamma}-Al{sub 2}O{sub 3}, CeO{sub 2}, ZrO{sub 2} and Ce{sub x}Zr{sub 1-x}O{sub 2} supported rhodium catalysts was investigated by Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS). The catalysts were characterized by temperature-programmed reduction (TPR) and cyclohexane dehydrogenation. DRIFTS studies on the partial oxidation of ethanol showed that ethanol is adsorbed dissociatively, through O-H bond breaking, with the formation of ethoxy species, followed by successive dehydrogenation to acetaldehyde and acetyl species. Further oxidation to acetate and carbonate species lead to the formation of CO, CH{sub 4} and H{sub 2} by decomposition. The presence of CeO{sub 2} in the catalysts favored the oxidation steps due to its oxygen storage capacity. (author)

  20. Microstructured optical fibers for gas sensing systems

    Science.gov (United States)

    Challener, William Albert; Choudhury, Niloy; Palit, Sabarni

    2017-10-17

    Microstructured optical fiber (MOF) includes a cladding extending a length between first and second ends. The cladding includes an inner porous microstructure that at least partially surrounds a hollow core. A perimeter contour of the hollow core has a non-uniform radial distance from a center axis of the cladding such that first segments of the cladding along the perimeter contour have a shorter radial distance from the center axis relative to second segments of the cladding along the perimeter contour. The cladding receives and propagates light energy through the hollow core, and the inner porous microstructure substantially confines the light energy within the hollow core. The cladding defines at least one port hole that extends radially from an exterior surface of the cladding to the hollow core. Each port hole penetrates the perimeter contour of the hollow core through one of the second segments of the cladding.

  1. Influence of thermal treatment in N{sub 2} atmosphere on chemical, microstructural and optical properties of indium tin oxide and nitrogen doped indium tin oxide rf-sputtered thin films

    Energy Technology Data Exchange (ETDEWEB)

    Stroescu, H.; Anastasescu, M.; Preda, S.; Nicolescu, M.; Stoica, M. [Institute of Physical Chemistry “Ilie Murgulescu” of the Romanian Academy, Spl. Independentei 202, 060021 Bucharest (Romania); Stefan, N. [National Institute for Lasers, Plasma and Radiation Physics, Atomistilor 409, RO-77125, Bucharest-Magurele (Romania); Kampylafka, V.; Aperathitis, E. [FORTH-IESL, Crete (Greece); Modreanu, M. [Tyndall National Institute, University College Cork, Cork (Ireland); Zaharescu, M. [Institute of Physical Chemistry “Ilie Murgulescu” of the Romanian Academy, Spl. Independentei 202, 060021 Bucharest (Romania); Gartner, M., E-mail: mgartner@icf.ro [Institute of Physical Chemistry “Ilie Murgulescu” of the Romanian Academy, Spl. Independentei 202, 060021 Bucharest (Romania)

    2013-08-31

    We report the influence of the normal thermal treatment (TT) and of rapid thermal annealing (RTA) on the microstructural, optical and electrical properties of indium tin oxide (ITO) and nitrogen doped indium tin oxide (ITO:N) thin films. The TT was carried out for 1 h at 400 °C and the RTA for 1 min up to 400 °C, both in N{sub 2} atmosphere. The ITO and ITO:N films were deposited by reactive sputtering in Argon, and respectively Nitrogen plasma, on Si with (100) and (111) orientation. The present study brings data about the microstructural and optical properties of ITO thin films with thicknesses around 300–400 nm. Atomic Force Microscopy analysis showed the formation of continuous and homogeneous films, fully covered by quasi-spherical shaped particles, with higher roughness values on Si(100) as compared to Si(111). Spectroscopic ellipsometry allowed the determination of film thickness, optical band gap as well as of the dispersion curves of n and k optical constants. X-ray diffraction analysis revealed the presence of diffraction peaks corresponding to the same nominal bulk composition of ITO, but with different intensities and preferential orientation depending on the substrate, atmosphere of deposition and type of thermal treatment. - Highlights: ► Stability of the films can be monitored by experimental ellipsometric spectra. ► The refractive index of indium tin oxide film on 0.3–30 μm range is reported. ► Si(100) substrate induces rougher film surfaces than Si(111). ► Rapid thermal annealing and normal thermal treatment lead to stable conductive film. ► The samples have a higher preferential orientation after rapid thermal annealing.

  2. Microstructure and elevated-temperature erosion-oxidation behaviour of aluminized 9Cr-1Mo Steel

    Science.gov (United States)

    Huttunen-Saarivirta, E.; Honkanen, M.; Tsipas, S. A.; Omar, H.; Tsipas, D.

    2012-10-01

    Degradation of materials by a combination of erosive wear and atmospheric oxidation at elevated temperatures constitutes a problem in some power generation processes, such as fluidized-bed combustion. In this work, 9Cr-1Mo steel, a common tube material in combustion chambers, is coated by a pack cementation method from an Al-containing pack in order to improve the resistance to erosion-oxidation at elevated temperatures. The resulting coating is studied in terms of microstructure and microhardness and tested for its resistance against impacts by sand particles in air at temperatures of 550-700 °C under several conditions, with thickness changes and appearance of the exposed surfaces being studied. The coating was found to contain several phases and layers, the outermost of which was essentially Al-rich and contained e.g., small AlN precipitates. The microhardness values for such coating ranged from 950 to 1100 HV20g. The coating provided the substrate with increased protection particularly against normal particle impacts, as manifested by smaller thickness losses for coated specimens as compared to uncoated counterparts. However, much of the coating was lost under all test conditions, despite the fact that particle debris formed a homogeneous layer on the surface. These results are described and discussed in this paper.

  3. Direct Simulation of Transport Properties from Three-Dimensional (3D) Reconstructed Solid-Oxide Fuel-Cell (SOFC) Electrode Microstructures

    International Nuclear Information System (INIS)

    Gunda, Naga Siva Kumar; Mitra, Sushanta K

    2012-01-01

    A well-known approach to develop a high efficiency solid-oxide fuel-cell (SOFC) consists of extracting the microstructure and transport properties such as volume fractions, internal surface area, geometric connectivity, effective gas diffusivity, effective electronic conductivity and geometric tortuosities from three-dimensional (3D) microstructure of the SOFC electrodes; thereafter, performing the SOFC efficiency calculations using previously mentioned quantities. In the present work, dual-beam focused ion beam - scanning electron microscopy (FIB-SEM) is applied on one of the SOFC cathodes, a lanthanum strontium manganite (LSM) electrode, to estimate the aforementioned properties. A framework for calculating transport properties is presented in this work. 3D microstructures of LSM electrode are reconstructed from a series of two-dimensional (2D) cross-sectional FIB-SEM images. Volume percentages of connected, isolated and dead-ends networks of pore and LSM phases are estimated. Different networks of pore and LSM phases are discretized with tetrahedral elements. Finally, the finite element method (FEM) is applied to calculate effective gas diffusivity and electronic conductivity of pore and LSM phases, respectively. Geometric tortuosities are estimated from the porosity and effective transport properties. The results obtained using FEM are compared with the finite volume method (FVM) results obtained by Gunda et al. [J. Power Sources, 196(7), 35929(2011)] and other numerical results obtained on randomly generated porous medium. Effect of consideration of dead-ends and isolated-ends networks on calculation of effective transport properties is studied.

  4. Microstructural Stability and Oxidation Resistance of 9-12 Chromium Steels at Elevated Temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Dogan, O.N.; Alman, D.E.; Jablonski, P.D.; Hawk, J.A.

    2006-05-01

    Various martensitic 9-12 Cr steels are utilized currently in fossil fuel powered energy plants for their good elevated temperature properties such as creep strength, steam side oxidation resistance, fire side corrosion resistance, and thermal fatigue resistance. Need for further improvements on the properties of 9-12 Cr steels for higher temperature (>600oC) use is driven by the environmental concerns (i.e., improve efficiency to reduce emissions and fossil fuel consumption). In this paper, we will discuss the results of the research done to explore new subsitutional solute solution and precipitate hardening mechanisms for improved strength of 9-12 Cr martensitic steels. Stability of the phases present in the steels will be evaluated for various temperature and time exposures. A comparison of microstructural properties of the experimental steels and commercial steels will also be presented.

    The influence of a Ce surface treatment on oxidation behavior of a commercial (P91) and several experimental steels containing 9 to 12 weight percent Cr was examined at 650ºC in flowing dry and moist air. The oxidation behavior of all the alloys without the Ce modification was significantly degraded by the presence of moisture in the air during testing. For instance the weight gain for P91 was two orders of magnitude greater in moist air than in dry air. This was accompanied by a change in oxide scale from the formation of Cr-based scales in dry air to the formation of Fe-based scales in moist air. The Ce surface treatment was very effective in improving the oxidation resistance of the experimental steels in both moist and dry air. For instance, after exposure to moist air at 650ºC for 2000 hours, an experimental alloy with the cerium surface modification had a weight gain three orders of magnitude lower than the alloy without the Ce modification and two orders of magnitude lower than P91. The Ce surface treatment suppressed the formation of Fe-based scales and

  5. Microstructural and chemical characterization of cladding material zirconia scales

    International Nuclear Information System (INIS)

    Cadalbert, R.; Boulanger, L.; Lansiart, S.; Silvestre, G.; Juliet, P.

    1991-01-01

    Uniform corrosion of Zircaloy-4 in PWR conditions depends both on the microstructure of the material and on its precise chemical composition. For a good understanding of the influence of the different parameters which are involved in the oxidation mechanisms, a detailed characterization of the oxide scale and the underlying metal is needed. The results on the alloying elements distribution in the oxide and the metal obtained by electron probe Microanalysis and Secondary Ion Mass Spectrometry as well as the TEM observations on the oxide crystal structure and the metal oxide interface are reported

  6. Synthesis of poly(ethylene oxide)-silica hybrids

    International Nuclear Information System (INIS)

    Ishak Manaf

    2002-01-01

    A hybrid material incorporating silica networks in poly (ethylene oxide) was produced using the sol-gel process from solution mixtures of poly (ethylene oxide) dissolved in water and partially polymerized tetraethylorthosilicate (TEOS) with and without compatibilisation agent. These mixtures were converted into films by solvent evaporation and drying them in an air-circulating oven at 60 degree C. Depending on the alkoxysilane solution composition and several mixing parameters, different morphologies were obtained, varying from semi-interpenetrating networks of PEO within highly cross linked silica chains, to finely dispersed heterogeneous system exhibiting either co-continuous or particulate microstructure. The influence of pH, type of solvents, mixing temperatures and time, as well as the nature of compatibiliser was found to be extremely important in controlling the morphology and properties of the fine hybrid films. It was found that compatibilisation of PEO-SiO 2 hybrid system is achieved exclusively with the use of γ-glycidyloxypropyltrimethoxysilane (GOTMS) coupling agent. (Author)

  7. Oscillatory Behavior during the Catalytic Partial Oxidation of Methane: Following Dynamic Structural Changes of Palladium Using the QEXAFS Technique

    DEFF Research Database (Denmark)

    Stoetzel, Jan; Frahm, Ronald; Kimmerle, Bertram

    2012-01-01

    oxidation of methane, the catalyst reduced from the end to the beginning of the catalyst bed and oxidized again toward the end as soon as the entire catalyst bed was reduced. On an entirely oxidized catalyst bed, only total oxidation of methane was observed and consumed the oxygen until the conditions...... of the Pd particles at increasing age of the catalyst was observed, which leads to a lower oscillation frequency. Effects of particle size, oven temperature, and oxygen/methane ratio on the oscillation behavior were studied in detail. The deactivation period (reoxidation of Pd) was much less influenced...... by the oven temperature than the ignition behavior of the catalytic partial oxidation of methane. This indicates that deactivation is caused by an autoreduction of the palladium at the beginning of the catalyst bed due to the high temperature achieved by total oxidation of methane....

  8. Microstructure and high temperature oxidation resistance of Ti-Ni gradient coating on TA2 titanium alloy fabricated by laser cladding

    Science.gov (United States)

    Liu, Fencheng; Mao, Yuqing; Lin, Xin; Zhou, Baosheng; Qian, Tao

    2016-09-01

    To improve the high temperature oxidation resistance of TA2 titanium alloy, a gradient Ni-Ti coating was laser cladded on the surface of the TA2 titanium alloy substrate, and the microstructure and oxidation behavior of the laser cladded coating were investigated experimentally. The gradient coating with a thickness of about 420-490 μm contains two different layers, e.g. a bright layer with coarse equiaxed grain and a dark layer with fine and columnar dendrites, and a transition layer with a thickness of about 10 μm exists between the substrate and the cladded coating. NiTi, NiTi2 and Ni3Ti intermetallic compounds are the main constructive phases of the laser cladded coating. The appearance of these phases enhances the microhardness, and the dense structure of the coating improves its oxidation resistance. The solidification procedure of the gradient coating is analyzed and different kinds of solidification processes occur due to the heat dissipation during the laser cladding process.

  9. Importance of controlling the Tl-oxide partial pressure throughout the processing of TlBa2CaCu2O7 thin films

    International Nuclear Information System (INIS)

    Siegal, M.P.; Venturini, E.L.; Newcomer, P.P.; Overmyer, D.L.; Dominguez, F.; Dunn, R.

    1995-01-01

    TlBa 2 CaCu 2 O 7 (Tl-1212) superconducting films 5000--6000 A thick have been grown on LaAlO 3 (100) substrates using oxide precursors in a closed two-zone thallination furnace. Tl-1212 films can be grown with transition temperatures ∼100 K, and critical current densities measured by magnetization of J cm (5 K)>10 7 A/cm 2 and J cm (77 K)>10 5 A/cm 2 . Processing conditions, substrate temperatures and Tl-oxide source temperatures are found which result in smooth, nearly phase-pure Tl-1212 films. Variations in the respective temperature ramps of the Tl-oxide zone and the substrate zone can greatly influence resulting film properties such as microstructure, morphology, superconducting transition temperature, and critical current density. copyright 1995 American Institute of Physics

  10. Development of a membrane-assisted fluidized bed reactor - 2 - Experimental demonstration and modeling for the partial oxidation of methanol

    NARCIS (Netherlands)

    Deshmukh, S.A.R.K.; Laverman, J.A.; van Sint Annaland, M.; Kuipers, J.A.M.

    2005-01-01

    A small laboratory-scale membrane-assisted fluidized bed reactor (MAFBR) was constructed in order to experimentally demonstrate the reactor concept for the partial oxidation of methanol to formaldehyde. Methanol conversion and product selectivities were measured at various overall fluidization

  11. Investigating microstructural evolution during the electroreduction of UO{sub 2} to U in LiCl-KCl eutectic using focused ion beam tomography

    Energy Technology Data Exchange (ETDEWEB)

    Brown, L.D.; Abdulaziz, R.; Tjaden, B.; Inman, D.; Brett, D.J.L.; Shearing, P.R., E-mail: p.shearing@ucl.ac.uk

    2016-11-15

    Reprocessing of spent nuclear fuels using molten salt media is an attractive alternative to liquid-liquid extraction techniques. Pyroelectrochemical processing utilizes direct, selective, electrochemical reduction of uranium dioxide, followed by selective electroplating of a uranium metal. Thermodynamic prediction of the electrochemical reduction of UO{sub 2} to U in LiCl-KCl eutectic has shown to be a function of the oxide ion activity. The pO{sup 2−} of the salt may be affected by the microstructure of the UO{sub 2} electrode. A uranium dioxide filled “micro-bucket” electrode has been partially electroreduced to uranium metal in molten lithium chloride-potassium chloride eutectic. This partial electroreduction resulted in two distinct microstructures: a dense UO{sub 2} and a porous U metal structure were characterised by energy dispersive X-ray spectroscopy. Focused ion beam tomography was performed on five regions of this electrode which revealed an overall porosity ranging from 17.36% at the outer edge to 3.91% towards the centre, commensurate with the expected extent of reaction in each location. The pore connectivity was also seen to reduce from 88.32% to 17.86% in the same regions and the tortuosity through the sample was modelled along the axis of propagation of the electroreduction, which was seen to increase from a value of 4.42 to a value of infinity (disconnected pores). These microstructural characteristics could impede the transport of O{sup 2−} ions resulting in a change in the local pO{sup 2−} which could result in the inability to perform the electroreduction. - Highlights: • The microstructural evolution of the reduction from UO{sub 2} to U has been investigated. • The porosity and tortuosity is seen to change significantly during electroreduction. • Low porosity and high tortuosity associated with the UO{sub 2} phase may impede O{sup 2−} transport.

  12. Characteristics of hydrogen produced by partial oxidation and auto-thermal reforming in a small methanol reformer

    Science.gov (United States)

    Horng, Rong-Fang; Chou, Huann-Ming; Lee, Chiou-Hwang; Tsai, Hsien-Te

    This paper investigates experimentally, the transient characteristics of a small methanol reformer using partial oxidation (POX) and auto-thermal reforming (ATR) for fuel cell applications. The parameters varied were heating temperature, methanol supply rate, steady mode shifting temperature, O 2/C (O 2/CH 3OH) and S/C (H 2O/CH 3OH) molar ratios with the main aim of promoting a rapid response and a high flow rate of hydrogen. The experiments showed that a high steady mode shifting temperature resulted in a faster temperature rise at the catalyst outlet and vice versa and that a low steady mode shifting temperature resulted in a lower final hydrogen concentration. However, when the mode shifting temperature was too high, the hydrogen production response was not necessarily improved. It was subsequently shown that the optimum steady mode shifting temperature for this experimental set-up was approximately 75 °C. Further, the hydrogen concentration produced by the auto-thermal process was as high as 49.12% and the volume flow rate up to 23.0 L min -1 compared to 40.0% and 20.5 L min -1 produced by partial oxidation.

  13. Microstructure, Wear Resistance and Oxidation Behavior of Ni-Ti-Si Coatings Fabricated on Ti6Al4V by Laser Cladding.

    Science.gov (United States)

    Zhuang, Qiaoqiao; Zhang, Peilei; Li, Mingchuan; Yan, Hua; Yu, Zhishui; Lu, Qinghua

    2017-10-30

    The Ni-Ti-Si composite coatings were successfully fabricated on Ti6Al4V by laser cladding. The microstructure were studied by SEM (scanning electron microscopy) and EDS (energy dispersive spectrometer). It has been found that Ti₂Ni and Ti₅Si₃ phases exist in all coatings, and some samples have TiSi₂ phases. Moreover, due to the existence of these phases, coatings presented relatively higher microhardness than that of the substrate (826 HV (Vickers hardness)) and the microhardness value of coating 3 is about twice larger than that of the substrate. During the dry sliding friction and wear test, due to the distribution of the relatively ductile phase of Ti₂Ni and reinforcement phases of Ti₅Si₃ and TiSi₂, the coatings performed good wear resistance. The oxidation process contains two stages: the rapid oxidation and slow oxidation by high temperature oxidation test at 800 °C for 50 h. Meanwhile, the value of the oxidation weight gain of the substrate is approximately three times larger than that of the coating 4. During the oxidation process, the oxidation film formed on the coating is mainly consisted of TiO₂, Al₂O₃ and SiO₂. Phases Ti₂Ni, Ti₅Si₃, TiSi₂ and TiSi were still found and it could be responsible for the improvement in oxidation resistance of the coatings by laser cladding.

  14. The influence of annealing on yttrium oxide thin film deposited by reactive magnetron sputtering: Process and microstructure

    Directory of Open Access Journals (Sweden)

    Y. Mao

    2017-01-01

    Full Text Available Yttrium oxide thin films were prepared by reactive magnetron sputtering in different deposition condition with various oxygen flow rates. The annealing influence on the yttrium oxide film microstructure is investigated. The oxygen flow shows a hysteresis behavior on the deposition rate. With a low oxygen flow rate, the so called metallic mode process with a high deposition rate (up to 1.4µm/h was achieved, while with a high oxygen flow rate, the process was considered to be in the poisoned mode with an extremely low deposition rate (around 20nm/h. X-ray diffraction (XRD results show that the yttrium oxide films that were produced in the metallic mode represent a mixture of different crystal structures including the metastable monoclinic phase and the stable cubic phase, while the poisoned mode products show a dominating monoclinic phase. The thin films prepared in metallic mode have relatively dense structures with less porosity. Annealing at 600 °C for 15h, as a structure stabilizing process, caused a phase transformation that changes the metastable monoclinic phase to stable cubic phase for both poisoned mode and metallic mode. The composition of yttrium oxide thin films changed from nonstoichiometric to stoichiometric together with a lattice parameter variation during annealing process. For the metallic mode deposition however, cracks were formed due to the thermal expansion coefficient difference between thin film and the substrate material which was not seen in poisoned mode deposition. The yttrium oxide thin films that deposited in different modes give various application options as a nuclear material.

  15. Microstructural examination of commercial ferritic alloys at 299 DPA

    International Nuclear Information System (INIS)

    Gelles, D.S.

    1995-11-01

    Microstructures and density change measurements are reported for Martensitic commercial steels HT-9 and Modified 9Cr-lMo (T9) and oxide dispersion strengthened ferritic alloys MA956 and NU957 following irradiation in the FFTF/MOTA at 420 degrees C to 200 DPA. Swelling as determined by density change remains below 2% for all conditions. Microstructures are found to be stable except in recrystallized grains of MA957, which are fabrication artifacts, with only minor swelling in the Martensitic steels and α' precipitation in alloys with 12% or more chromium. These results further demonstrate the high swelling resistance and microstructural stability of the ferritic alloy class

  16. Microstructure and high-temperature oxidation resistance of TiN/Ti3Al intermetallic matrix composite coatings on Ti6Al4V alloy surface by laser cladding

    Science.gov (United States)

    Zhang, Xiaowei; Liu, Hongxi; Wang, Chuanqi; Zeng, Weihua; Jiang, Yehua

    2010-11-01

    A high-temperature oxidation resistant TiN embedded in Ti3Al intermetallic matrix composite coating was fabricated on titanium alloy Ti6Al4V surface by 6kW transverse-flow CO2 laser apparatus. The composition, morphology and microstructure of the laser clad TiN/Ti3Al intermetallic matrix composite coating were characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectrometer (EDS). In order to evaluate the high-temperature oxidation resistance of the composite coatings and the titanium alloy substrate, isothermal oxidation test was performed in a conventional high-temperature resistance furnace at 600°C and 800°C respectively. The result shows that the laser clad intermetallic composite coating has a rapidly solidified fine microstructure consisting of TiN primary phase (granular-like, flake-like, and dendrites), and uniformly distributed in the Ti3Al matrix. It indicates that a physical and chemical reaction between the Ti powder and AlN powder occurred completely under the laser irradiation. In addition, the microhardness of the TiN/Ti3Al intermetallic matrix composite coating is 844HV0.2, 3.4 times higher than that of the titanium alloy substrate. The high-temperature oxidation resistance test reveals that TiN/Ti3Al intermetallic matrix composite coating results in the better modification of high-temperature oxidation behavior than the titanium substrate. The excellent high-temperature oxidation resistance of the laser cladding layer is attributed to the formation of the reinforced phase TiN and Al2O3, TiO2 hybrid oxide. Therefore, the laser cladding TiN/Ti3Al intermetallic matrix composite coating is anticipated to be a promising oxidation resistance surface modification technique for Ti6Al4V alloy.

  17. Fast high-temperature consolidation of Oxide-Dispersion Strengthened (ODS) steels: process, microstructure, precipitation, properties

    International Nuclear Information System (INIS)

    Boulnat, Xavier

    2014-01-01

    This work aims to lighten the understanding of the behavior of a class of metallic materials called Oxide-Dispersion Strengthened (ODS) ferritic steels. ODS steels are produced by powder metallurgy with various steps including atomization, mechanical alloying and high-temperature consolidation. The consolidation involves the formation of nanoparticles in the steel and various evolutions of the microstructure of the material that are not fully understood. In this thesis, a novel consolidation technique assisted by electric field called 'Spark Plasma Sintering' (SPS) or 'Field-Assisted Sintering Technique' (FAST) was assessed. Excellent mechanical properties were obtained by SPS, comparable to those of conventional hot isostatic pressed (HIP) materials but with much shorter processing time. Also, a broad range of microstructures and thus of tensile strength and ductility were obtained by performing SPS on either milled or atomized powder at different temperatures. However, SPS consolidation failed to avoid heterogeneous microstructure composed of ultrafine-grained regions surrounded by micron grains despite of the rapid consolidation kinetics. A multi-scale characterization allowed to understand and model the evolution of this complex microstructure. An analytical evaluation of the contributing mechanisms can explain the appearance of the complex grain structure and its thermal stability during further heat treatments. Inhomogeneous distribution of plastic deformation in the powder is argued to be the major cause of heterogeneous recrystallization and further grain growth during hot consolidation. Even if increasing the solute content of yttrium, titanium and oxygen does not impede abnormal growth, it permits to control the fraction and the size of the retained ultrafine grains, which is a key-factor to tailor the mechanical properties. Since precipitation through grain boundary pinning plays a significant role on grain growth, a careful

  18. Preparation of Cement Composites with Ordered Microstructures via Doping with Graphene Oxide Nanosheets and an Investigation of Their Strength and Durability

    Directory of Open Access Journals (Sweden)

    Shenghua Lv

    2016-11-01

    Full Text Available The main problem with cement composites is that they have structural defects, including cracks, holes, and a disordered morphology, which significantly affects their strength and durability. Therefore, the construction of cement composites with defect-free structures and high strength and long durability is an important research topic. Here, by controlling the size and chemical groups of graphene oxide nanosheets (GONs used for doping, we were able to control the entire cement matrix to form an ordered microstructure consisting of polyhedron-like crystals and exhibit flower-like patterns. The cracks and holes in the cement matrix just about vanished. The compressive and flexural strengths as well as the parameters for the durability assessment of the corresponding cement composites obviously improved compared with the control samples. Thus, the formation mechanism of the cement matrix with the ordered microstructure is proposed, and a proper explanation is given to regulation action.

  19. Preparation of thin layer materials with macroporous microstructure for SOFC applications

    International Nuclear Information System (INIS)

    Marrero-Lopez, D.; Ruiz-Morales, J.C.; Pena-Martinez, J.; Canales-Vazquez, J.; Nunez, P.

    2008-01-01

    A facile and versatile method using polymethyl methacrylate (PMMA) microspheres as pore formers has been developed to prepare thin layer oxide materials with controlled macroporous microstructure. Several mixed oxides with fluorite and perovskite-type structures, i.e. doped zirconia, ceria, ferrites, manganites, and NiO-YSZ composites have been prepared and characterised by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), nitrogen adsorption and mercury porosimetry. The synthesised materials are nanocrystalline and present a homogeneous pore distribution and relatively high specific surface area, which makes them interesting for SOFC and catalysis applications in the intermediate temperature range. - Graphical abstract: Thin films materials of mixed oxides with potential application in SOFC devices have been prepared with macroporous microstructure using PMMA microspheres as pore formers. Display Omitted

  20. Effect of PEEP and inhaled nitric oxide on pulmonary gas exchange during gaseous and partial liquid ventilation with small volumes of perfluorocarbon.

    Science.gov (United States)

    Max, M; Kuhlen, R; Falter, F; Reyle-Hahn, M; Dembinski, R; Rossaint, R

    2000-04-01

    Partial liquid ventilation, positive end-expiratory pressure (PEEP) and inhaled nitric oxide (NO) can improve ventilation/perfusion mismatch in acute lung injury (ALI). The aim of the present study was to compare gas exchange and hemodynamics in experimental ALI during gaseous and partial liquid ventilation at two different levels of PEEP, with and without the inhalation of nitric oxide. Seven pigs (24+/-2 kg BW) were surfactant-depleted by repeated lung lavage with saline. Gas exchange and hemodynamic parameters were assessed in all animals during gaseous and subsequent partial liquid ventilation at two levels of PEEP (5 and 15 cmH2O) and intermittent inhalation of 10 ppm NO. Arterial oxygenation increased significantly with a simultaneous decrease in cardiac output when PEEP 15 cmH2O was applied during gaseous and partial liquid ventilation. All other hemodynamic parameters revealed no relevant changes. Inhalation of NO and instillation of perfluorocarbon had no additive effects on pulmonary gas exchange when compared to PEEP 15 cmH2O alone. In experimental lung injury, improvements in gas exchange are most distinct during mechanical ventilation with PEEP 15 cmH2O without significantly impairing hemodynamics. Partial liquid ventilation and inhaled NO did not cause an additive increase of PaO2.

  1. Partial catalytic oxidation of CH{sub 4} to synthesis gas for power generation - Final report

    Energy Technology Data Exchange (ETDEWEB)

    Mantzaras, I.; Schneider, A.

    2006-03-15

    The partial oxidation of methane to synthesis gas over rhodium catalysts has been investigated experimentally and numerically in the pressure range of 4 to 10 bar. The methane/oxidizer feed has been diluted with large amounts of H{sub 2}O and CO{sub 2} (up to 70% vol.) in order to simulate new power generation cycles with large exhaust gas recycle. Experiments were carried out in an optically accessible channel-flow reactor that facilitated laser-based in situ measurements, and also in a subscale gas-turbine catalytic reactor. Full-elliptic steady and transient two-dimensional numerical codes were used, which included elementary hetero-/homogeneous chemical reaction schemes. The following are the key conclusions: a) Heterogeneous (catalytic) and homogeneous (gas-phase) schemes have been validated for the partial catalytic oxidation of methane with large exhaust gas recycle. b) The impact of added H{sub 2}O and CO{sub 2} has been elucidated. The added H{sub 2}O increased the methane conversion and hydrogen selectivity, while it decreased the CO selectivity. The chemical impact of CO{sub 2} (dry reforming) was minimal. c) The numerical model reproduced the measured catalytic ignition times. It was further shown that the chemical impact of H{sub 2}O and CO{sub 2} on the catalytic ignition delay times was minimal. d) The noble metal dispersion increased with different support materials, in the order Rh/{alpha}-Al{sub 2}O{sub 3}, Rh/ZrO{sub 2}, and Rh/Ce-ZrO{sub 2}. An evident relationship was established between the noble metal dispersion and the catalytic behavior. (authors)

  2. Influence of deposition temperature and amorphous carbon on microstructure and oxidation resistance of magnetron sputtered nanocomposite Crsbnd C films

    Science.gov (United States)

    Nygren, Kristian; Andersson, Matilda; Högström, Jonas; Fredriksson, Wendy; Edström, Kristina; Nyholm, Leif; Jansson, Ulf

    2014-06-01

    It is known that mechanical and tribological properties of transition metal carbide films can be tailored by adding an amorphous carbon (a-C) phase, thus making them nanocomposites. This paper addresses deposition, microstructure, and for the first time oxidation resistance of magnetron sputtered nanocomposite Crsbnd C/a-C films with emphasis on studies of both phases. By varying the deposition temperature between 20 and 700 °C and alternating the film composition, it was possible to deposit amorphous, nanocomposite, and crystalline Crsbnd C films containing about 70% C and 30% Cr, or 40% C and 60% Cr. The films deposited at temperatures below 300 °C were X-ray amorphous and 500 °C was required to grow crystalline phases. Chronoamperometric polarization at +0.6 V vs. Ag/AgCl (sat. KCl) in hot 1 mM H2SO4 resulted in oxidation of Crsbnd C, yielding Cr2O3 and C, as well as oxidation of C. The oxidation resistance is shown to depend on the deposition temperature and the presence of the a-C phase. Physical characterization of film surfaces show that very thin C/Cr2O3/Crsbnd C layers develop on the present material, which can be used to improve the oxidation resistance of, e.g. stainless steel electrodes.

  3. Image analysis: a tool characterising and modelling the microstructure of the MOX fuel

    International Nuclear Information System (INIS)

    Charollais, F.

    1997-01-01

    The MOX nuclear fuel, made up of about 3 to 10 % of plutonium oxide mixed with uranium oxide, is elaborated by an original manufacturing method (MIMAS process). The MOX pellets feature a singular and complex microstructure, including enriched plutonium zones dispersed in a low plutonium content matrix. Their properties as well as their performances levels are strongly linked with this microstructure. Tools, found in the literature, allowing to quantify with relevant parameters the microstructural images from different analytical equipment (optical microscopy, electron probe micro-analyser and autoradiography) have been adapted and used in order to characterize these nuclear fuels. Taking into account the heterogeneity of the MOX microstructure, we turn our's attention, at the beginning of this study, to the analysis conditions: choice of the magnification, sampling and statistical analysis of the measurements. An improvement of the ceramographic preparation of the samples, required for an automatic image analysis (of the granular structure), has been realised by thermal etching under oxidizing gas. This method enables the strong content plutonium zones to be revealed distinctly. The first part of the study concerns the characterization of the three-dimensional structure of uranium oxide and MOX fuels by average variables using the principles of mathematical morphology and stereology. The second part introduces probabilistic models, in particular the Boolean scheme, in order to improve and complete the three-dimensional characterization of the MOX fuel and more specifically the enriched plutonium islands dispersion in the pellet. [fr

  4. Characteristic of nitrous oxide production in partial denitrification process with high nitrite accumulation.

    Science.gov (United States)

    Du, Rui; Peng, Yongzhen; Cao, Shenbin; Wang, Shuying; Niu, Meng

    2016-03-01

    Nitrous oxide (N2O) production during the partial denitrification process with nitrate (NO3(-)-N) to nitrite (NO2(-)-N) transformation ratio of 80% was investigated in this study. Results showed that N2O was seldom observed before complete depletion of NO3(-)-N, but it was closely related to the reduction of NO2(-)-N rather than NO3(-)-N. High COD/NO3(-)-N was in favor of N2O production in partial denitrification with high NO2(-)-N accumulation. It was seriously enhanced at constant acidic pH due to the free nitrous acid (FNA) inhibition. However, the N2O production was much lower at initial pH of 5.5 and 6.5 due to the pH increase during denitrification process. Significantly, the pH turning point could be chosen as a controlled parameter to denote the end of NO3(-)-N reduction, which could not only achieve high NO2(-)-N accumulation but also decrease the N2O production significantly for practical application. Copyright © 2015 Elsevier Ltd. All rights reserved.

  5. Visualizing a Catalyst at Work during the Ignition of the Catalytic Partial Oxidation of Methane

    DEFF Research Database (Denmark)

    Kimmerle, Bertram; Grunwaldt, Jan-Dierk; Baiker, Alfons

    2009-01-01

    We present a spatiotemporal operando X-ray absorption study of a highly dynamic process, the ignition of the noble metal catalyzed partial oxidation of methane. Evolvement and propagation of the platinum component's structural changes are investigated with a high-speed X-ray camera, which...... in combination with temperature profiling by IR-thermography and catalytic activity measurements by online mass spectrometry gives insight into the first stages of the ignition of the reaction toward hydrogen and carbon monoxide....

  6. Direct comparison between X-ray nanotomography and scanning electron microscopy for the microstructure characterization of a solid oxide fuel cell anode

    International Nuclear Information System (INIS)

    Quey, R.; Suhonen, H.; Laurencin, J.; Cloetens, P.; Bleuet, P.

    2013-01-01

    X-ray computed nanotomography (nano-CT) and scanning electron microscopy (SEM) have been applied to characterize the microstructure of a Solid Oxide Fuel Cell (SOFC) anode. A direct comparison between the results of both methods is conducted on the same region of the microstructure to assess the spatial resolution of the nano-CT microstructure, SEM being taken as a reference. A registration procedure is proposed to find out the position of the SEM image within the nano-CT volume. It involves a second SEM observation, which is taken along an orthogonal direction and gives an estimate reference SEM image position, which is then refined by an automated optimization procedure. This enables an unbiased comparison between the cell porosity morphologies provided by both methods. In the present experiment, nano-CT is shown to underestimate the number of pores smaller than 1 μm and overestimate the size of the pores larger than 1.5 μm. - Highlights: ► X-ray computed nanotomography (nano-CT) and SEM are used to characterize an SOFC anode. ► A methodology is proposed to compare the nano-CT and SEM data on the same region. ► The spatial resolution of the nano-CT data is assessed from that comparison

  7. Microstructural characterization of silicon added titanium aluminide

    International Nuclear Information System (INIS)

    Khan, A.N.

    2009-01-01

    Titanium aluminides intermetallic compounds have received great attention during the past decade, since they have the potential, in aircraft and automotive engines, to replace the high density Ni-base superalloys However, these intermetallics possess poor oxidation properties at high temperatures. Previous studies showed that protective alumina scale formation on gamma-TiAl can be obtained by small additions (around 2 at.%) of Ag. In the present study, a number of cast Ti-Al-Si alloys were investigated in relation to transient oxide formation in air at 1300 deg. C. After various oxidation times the oxide composition, microstructure and morphology were studied by combining a number of analysis techniques. The TiAl-Si alloys appear to form Al Ti and Si oxides. However, the formation of silicon oxide at the interface of base metal and scale slows down the oxidation rate significantly. (author)

  8. Effects of substrate microstructure on the formation of oriented oxide nanotube arrays on Ti and Ti alloys

    Energy Technology Data Exchange (ETDEWEB)

    Ferreira, C.P. [State University of Campinas (Unicamp), Department of Materials Engineering (Dema/FEM), CP 6122, Campinas 13083-970, SP (Brazil); Gonçalves, M.C. [State University of Campinas (Unicamp), Instituto de Química, CP 6154, Cidade Universitária Zeferino Vaz, Campinas 13083-970, SP (Brazil); Caram, R. [State University of Campinas (Unicamp), Department of Materials Engineering (Dema/FEM), CP 6122, Campinas 13083-970, SP (Brazil); Bertazzoli, R., E-mail: rbertazzoli@fem.unicamp.br [State University of Campinas (Unicamp), Department of Materials Engineering (Dema/FEM), CP 6122, Campinas 13083-970, SP (Brazil); Rodrigues, C.A. [Federal University of São Paulo – Campus Diadema (UNIFESP – Campus Diadema), Departamento de Ciências Exatas e da Terra, Rua São Nicolau n° 210, 09913-030 Diadema, SP (Brazil)

    2013-11-15

    The formation of nanotubular oxide layers on Ti and Ti alloys has been widely investigated for the photocatalytic degradation of organic compounds due to their excellent catalytic efficiency, chemical stability, and low cost and toxicity. Aiming to improve the photocatalytic efficiency of this nanostructured oxide, this work investigated the influence of substrate grain size on the growth of nanotubular oxide layers. Ti and Ti alloys (Ti–6Al, Ti–6Al–7Nb) were produced by arc melting with non-consumable tungsten electrode and water-cooled copper hearth under argon atmosphere. Some of the ingots were heat-treated at 1000 °C for 12 and 24 h in argon atmosphere, followed by slow cooling rates to reduce crystalline defects and increase the grain size of their microstructures. Three types of samples were anodized: commercial substrate, as-prepared and heat-treated samples. The anodization was performed using fluoride solution and a cell potential of 20 V. The samples were characterized by optical microscopy, field-emission scanning electron microscopy and X-ray diffraction. The heat treatment preceding the anodization process increased the grain size of pure Ti and Ti alloys and promoted the formation of Widmanstätten structures in Ti{sub 6}Al{sub 7}Nb. The nanotubes layers grown on smaller grain and thermally untreated samples were more regular and homogeneous. In the case of Ti–6Al–7Nb alloy, which presents a α + β phase microstructure, the morphology of nanotubes nucleated on α matrix was more regular than those of nanotubes nucleated on β phase. After the annealing process, the Ti–6Al–7Nb alloy presented full diffusion process and the growth of equilibrium phases resulting in the appearance of regions containing higher concentrations of Nb, i.e. beta phase. In those regions the dissolution rate of Nb{sub 2}O{sub 5} is lower than that of TiO{sub 2}, resulting in a nanoporous layer. In general, heat treating reduces crystalline defects and promotes

  9. Thin film oxygen partial pressure sensor

    Science.gov (United States)

    Wortman, J. J.; Harrison, J. W.; Honbarrier, H. L.; Yen, J.

    1972-01-01

    The development is described of a laboratory model oxygen partial pressure sensor using a sputtered zinc oxide thin film. The film is operated at about 400 C through the use of a miniature silicon bar. Because of the unique resistance versus temperature relation of the silicon bar, control of the operational temperature is achieved by controlling the resistance. A circuit for accomplishing this is described. The response of sputtered zinc oxide films of various thicknesses to oxygen, nitrogen, argon, carbon dioxide, and water vapor caused a change in the film resistance. Over a large range, film conductance varied approximately as the square root of the oxygen partial pressure. The presence of water vapor in the gas stream caused a shift in the film conductance at a given oxygen partial pressure. A theoretical model is presented to explain the characteristic features of the zinc oxide response to oxygen.

  10. Nitrous Oxide Production in a Granule-based Partial Nitritation Reactor: A Model-based Evaluation.

    Science.gov (United States)

    Peng, Lai; Sun, Jing; Liu, Yiwen; Dai, Xiaohu; Ni, Bing-Jie

    2017-04-03

    Sustainable wastewater treatment has been attracting increasing attentions over the past decades. However, the production of nitrous oxide (N 2 O), a potent GHG, from the energy-efficient granule-based autotrophic nitrogen removal is largely unknown. This study applied a previously established N 2 O model, which incorporated two N 2 O production pathways by ammonia-oxidizing bacteria (AOB) (AOB denitrification and the hydroxylamine (NH 2 OH) oxidation). The two-pathway model was used to describe N 2 O production from a granule-based partial nitritation (PN) reactor and provide insights into the N 2 O distribution inside granules. The model was evaluated by comparing simulation results with N 2 O monitoring profiles as well as isotopic measurement data from the PN reactor. The model demonstrated its good predictive ability against N 2 O dynamics and provided useful information about the shift of N 2 O production pathways inside granules for the first time. The simulation results indicated that the increase of oxygen concentration and granule size would significantly enhance N 2 O production. The results further revealed a linear relationship between N 2 O production and ammonia oxidation rate (AOR) (R 2  = 0.99) under the conditions of varying oxygen levels and granule diameters, suggesting that bulk oxygen and granule size may exert an indirect effect on N 2 O production by causing a change in AOR.

  11. Microstructural evolution and stability of tetragonal precipitates in Y2O3 partially-stabilized ZrO2 single crystals

    International Nuclear Information System (INIS)

    Martinez-Fernandez, J.; Jimenez-Melendo, M.; Dominguez-Rodriguez, A.

    1995-01-01

    The microstructure and morphology of tetragonal precipitates (t-ZrO 2 ) in yttria partially-stabilized zirconia single crystals containing various amounts of Y 2 O 3 (3, 4, 4.7 and 5.8 mol%) have been studied as a function of aging time at 1,600 C in air. The precipitate size and volume fraction of t-ZrO 2 phase were determined using transmission electron microscopy. The evolution of the precipitate volume fraction with aging time indicated that the precipitation reaction was completed after 24 h of annealing, in agreement with the values of the Y 2 O 3 composition in the matrix measured by analytical electron microscopy. Further aging coarsened the precipitates which joined together forming fiber-like particles of several micrometers in length and remaining untransformed despite their large size. The stability of the t-ZrO 2 precipitates against the tetragonal to monoclinic transformation in the ZrO 2 -Y 2 O 3 system seems to be related to interactions between precipitates due to coherency stresses rather than with their morphological characteristics

  12. Prospective use of the 3D printing technology for the microstructural engineering of Solid Oxide Fuel Cell components

    Directory of Open Access Journals (Sweden)

    Hernández-Rodríguez, E. M.

    2014-10-01

    Full Text Available A cost-effective micro-manufacturing process to accurately build 3D microstructures for their prospective use in the fabrication of Solid Oxide Fuel Cells components has been tested. The 3D printing method, based on the stereolithography, allows solidifying layer by layer a dispersion of ceramic material in a liquid photosensitive organic monomer. A simple projector, a computer-controlled z-stage and a few PowerPoint slides may be used for the fabrication of a wide range of complex 3D microstructures in few minutes. In this work, 3D ceramic microstructures based on the yttria-stabilized zirconia (YSZ were successfully fabricated. The microstructured ceramic components produced were stable after sintering at 1400 ºC for 4 h. Impedance measurements show that the fabrication process does not have any detrimental effect on the electrical properties of the structured material.Se ha probado un método económico de microfabricación que permite construir con precisión microestructuras 3D para su potencial uso en la producción de componentes de pilas de combustible de óxidos sólidos. El método de impresión 3D basado en la estereolitografía, permite solidificar, capa por capa, una dispersión de material cerámico en un líquido que contiene un monómero orgánico fotosensible. Un simple proyector, una plataforma vertical automatizada y unas pocas imágenes de PowerPoint pueden ser utilizados para la fabricación de un amplio rango de estructuras complejas 3D en unos pocos minutos. En este trabajo se han fabricado con éxito microestructuras 3D basadas en la zirconia dopada con itria (YSZ. El material cerámico microestructurado producido se mantuvo estable después de sinterizarse a 1400 ºC durante 4 h. Las medidas de impedancia demostraron que el proceso de fabricación no tenía ningún efecto perjudicial en las propiedades eléctricas del material estructurado.

  13. Microstructural characterization of ODS ferritic steels at different processing stages

    Energy Technology Data Exchange (ETDEWEB)

    Gil, E., E-mail: egil@ceit.es; Ordás, N.; García-Rosales, C.; Iturriza, I., E-mail: iiturriza@ceit.es

    2015-10-15

    Highlights: • ODS ferritic stainless steel produced by new route without mechanical alloying. • Fully dense ferritic stainless steels containing Y and Ti were obtained by HIPping. • Y and Ti-rich precipitates prevent grain growth during heat treatment up to 1320 °C. • HIPping at 1220 °C dissolves the metastable oxides on PPBs. - Abstract: Nanostructured Oxide Dispersion Strengthened Reduced Activation Ferritic Stainless Steels (ODS RAF) are promising structural materials for fusion reactors, due to their ultrafine microstructure and the presence of a dispersion of Y–Ti–O nanoclusters that provide excellent creep strength at high temperatures (up to 750 °C). The traditional powder metallurgical route to produce these steels is based on Gas Atomization (GA) + Mechanical Alloying (MA) + HIP + ThermoMechanical Treatments (TMTs). Recently, alternative methods have arisen to avoid the MA step. In line with this new approach, ferritic stainless steel powders were produced by gas atomization and HIPped, after adjusting their oxygen, Y and Ti contents to form Y–Ti–O nanoclusters during subsequent heat treatments. The microstructure of as-HIPped steels mainly consists of ferrite grains, Y–Ti precipitates, carbides and oxides on Prior Particle Boundaries (PPBs). Post-HIP heat treatments performed at high temperatures (1270 and 1300 °C) evaluated the feasibility of achieving a complete dissolution of the oxides on PPBs and a precipitation of ultrafine Ti- and Y-rich oxides in the Fe14Cr2W matrix. FEG-SEM with extensive EDS analysis was used to characterize the microstructure of the atomized powders and the ODS-RAF specimens after HIP consolidation and post-HIP heat treatments. A deeper characterization of atomized powder was carried out by TEM.

  14. Microstructure, Wear Resistance and Oxidation Behavior of Ni-Ti-Si Coatings Fabricated on Ti6Al4V by Laser Cladding

    Directory of Open Access Journals (Sweden)

    Qiaoqiao Zhuang

    2017-10-01

    Full Text Available The Ni-Ti-Si composite coatings were successfully fabricated on Ti6Al4V by laser cladding. The microstructure were studied by SEM (scanning electron microscopy and EDS (energy dispersive spectrometer. It has been found that Ti2Ni and Ti5Si3 phases exist in all coatings, and some samples have TiSi2 phases. Moreover, due to the existence of these phases, coatings presented relatively higher microhardness than that of the substrate (826 HV (Vickers hardness and the microhardness value of coating 3 is about twice larger than that of the substrate. During the dry sliding friction and wear test, due to the distribution of the relatively ductile phase of Ti2Ni and reinforcement phases of Ti5Si3 and TiSi2, the coatings performed good wear resistance. The oxidation process contains two stages: the rapid oxidation and slow oxidation by high temperature oxidation test at 800 °C for 50 h. Meanwhile, the value of the oxidation weight gain of the substrate is approximately three times larger than that of the coating 4. During the oxidation process, the oxidation film formed on the coating is mainly consisted of TiO2, Al2O3 and SiO2. Phases Ti2Ni, Ti5Si3, TiSi2 and TiSi were still found and it could be responsible for the improvement in oxidation resistance of the coatings by laser cladding.

  15. Models for the Configuration and Integrity of Partially Oxidized Fuel Rod Cladding at High Temperatures

    International Nuclear Information System (INIS)

    Siefken, L.J.

    1999-01-01

    Models were designed to resolve deficiencies in the SCDAP/RELAP5/MOD3.2 calculations of the configuration and integrity of hot, partially oxidized cladding. These models are expected to improve the calculations of several important aspects of fuel rod behavior. First, an improved mapping was established from a compilation of PIE results from severe fuel damage tests of the configuration of melted metallic cladding that is retained by an oxide layer. The improved mapping accounts for the relocation of melted cladding in the circumferential direction. Then, rules based on PIE results were established for calculating the effect of cladding that has relocated from above on the oxidation and integrity of the lower intact cladding upon which it solidifies. Next, three different methods were identified for calculating the extent of dissolution of the oxidic part of the cladding due to its contact with the metallic part. The extent of dissolution effects the stress and thus the integrity of the oxidic part of the cladding. Then, an empirical equation was presented for calculating the stress in the oxidic part of the cladding and evaluating its integrity based on this calculated stress. This empirical equation replaces the current criterion for loss of integrity which is based on temperature and extent of oxidation. Finally, a new rule based on theoretical and experimental results was established for identifying the regions of a fuel rod with oxidation of both the inside and outside surfaces of the cladding. The implementation of these models is expected to eliminate the tendency of the SCDAP/RELAP5 code to overpredict the extent of oxidation of the upper part of fuel rods and to underpredict the extent of oxidation of the lower part of fuel rods and the part with a high concentration of relocated material. This report is a revision and reissue of the report entitled, Improvements in Modeling of Cladding Oxidation and Meltdown

  16. Oxidative stability and microstructure of 5% fish-oil-enriched granola bars added natural antioxidants derived from brown algaFucus vesiculosus

    DEFF Research Database (Denmark)

    Karadağ, Ayşe; Hermund, Ditte Baun; Jensen, Louise Helene Søgaard

    2017-01-01

    The aims of this study were to; 1) investigate the ability of Icelandic brown algae Fucus vesiculosus extracts to inhibit lipid oxidation in granola bars fortified with fish oil-in-water emulsion; 2) investigate whether addition of the seaweed extracts affected the physical microstructure...... efficacy of these two extracts was among other related to an improved incorporation of the fish oil-in-water emulsions in the bars, high total phenolic content, high radical scavenging activity together with high interfacial affinity of phenolic compounds and probably regeneration of tocopherol. Practical...... applications: The work showed the application potential of Fucus vesiculosus extracts as a natural antioxidant in low-moisture foods such as granola bars. These findings implied that the multi-functional nature of these extracts provides not only oxidative stability of the food but also a physical stability....

  17. Microstructure and high temperature oxidation resistance of in-situ synthesized TiN/Ti_3Al intermetallic composite coatings on Ti6Al4V alloy by laser cladding process

    International Nuclear Information System (INIS)

    Liu, Hongxi; Zhang, Xiaowei; Jiang, Yehua; Zhou, Rong

    2016-01-01

    High temperature anti-oxidation TiN/Ti_3Al intermetallic composite coatings were fabricated with the powder and AlN powder on Ti6Al4V titanium alloy surface by 6 kW transverse-flow CO_2 laser apparatus. The chemical composition, morphology and microstructure of the TiN/Ti_3Al composite coatings were characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectrometer (EDS). In order to evaluate the high temperature oxidation resistance of TiN/Ti_3Al coating, the isothermal oxidation test was performed in a high temperature resistance furnace at 600 °C and 800 °C, respectively. The result shows that the composite coating has a rapidly solidified fine microstructure consisting of TiN primary phase (granular-like, flake-like or dendrites), with an even distribution in Ti_3Al matrix. It indicates that a physical and chemical reaction between Ti powder and AlN powder has completely occurred under the laser irradiation condition. In addition, the microhardness of the TiN/Ti3Al intermetallic composite coating is 3.4 times higher than that of the Ti6Al4V alloy substrate and reaches 844 HV_0_._2. The high temperature oxidation behavior test reveals that the high temperature oxidation resistance of TiN/Ti_3Al composite coating is much better than that of titanium alloy substrate. The excellent high temperature oxidation resistance of TiN/Ti_3Al intermetallic composite coating is attributed to the formation of reinforced phases TiN, Al_2O_3 and TiO_2. The laser cladding TiN/Ti_3Al intermetallic composite coating is anticipated to be a promising high temperature oxidation resistance coating for Ti6Al4V alloy. - Highlights: • In-situ TiN/Ti_3Al composite coating was synthesized on Ti6Al4V alloy by laser cladding. • The influence of Ti and AlN molar ratio on the microstructure of the coating was studied. • The TiN/Ti_3Al intermetallic coating is mainly composed of α-Ti, TiN and Ti_3Al phases. • The

  18. Fuel processor integrated H{sub 2}S catalytic partial oxidation technology for sulfur removal in fuel cell power plants

    Energy Technology Data Exchange (ETDEWEB)

    Gardner, T.H.; Berry, D.A.; Lyons, K.D.; Beer, S.K.; Freed, A.D. [U.S. Department of Energy, Morgantown, WV (USA). National Energy Technology Laboratory

    2002-12-01

    H{sub 2}S catalytic partial oxidation technology with an activated carbon catalyst was found to be a promising method for the removal of hydrogen sulfide from fuel cell hydrocarbon feedstocks. Three different fuel cell feedstocks were considered for analysis: sour natural gas, sour effluent from a liquid middle distillate fuel processor and a Texaco O{sub 2}-blown coal-derived synthesis gas. The H{sub 2}S catalytic partial oxidation reaction, its integratability into fuel cell power plants with different hydrocarbon feedstocks and its salient features are discussed. Experimental results indicate that H{sub 2}S concentration can be removed down to the part-per-million level in these plants. Additionally, a power law rate expression was developed and reaction kinetics compared to prior literature. The activation energy for this reaction was determined to be 34.4 kJ/g mol with the reaction being first order in H{sub 2}S and 0.3 order in O{sub 2}. 18 refs., 14 figs., 3 tabs.

  19. Microstructure and corrosion behavior of coated AZ91 alloy by microarc oxidation for biomedical application

    Science.gov (United States)

    Wang, Y. M.; Wang, F. H.; Xu, M. J.; Zhao, B.; Guo, L. X.; Ouyang, J. H.

    2009-08-01

    Magnesium and its alloy currently are considered as the potential biodegradable implant materials, while the accelerated corrosion rate in intro environment leads to implant failure by losing the mechanical integrity before complete restoration. Dense oxide coatings formed in alkaline silicate electrolyte with and without titania sol addition were fabricated on magnesium alloy using microarc oxidation process. The microstructure, composition and degradation behavior in simulated body fluid (SBF) of the coated specimens were evaluated. It reveals that a small amount of TiO 2 is introduced into the as-deposited coating mainly composed of MgO and Mg 2SiO 4 by the addition of titania sol into based alkaline silicate electrolytic bath. With increasing concentration of titania sol from 0 to 10 vol.%, the coating thickness decreases from 22 to 18 μm. Electrochemical tests show that the Ecorr of Mg substrate positively shifted about 300˜500 mV and icorr lowers more than 100 times after microarc oxidation. However, the TiO 2 modified coatings formed in electrolyte containing 5 and 10 vol.% titania sol indicate an increasing worse corrosion resistance compared with that of the unmodified coating, which is possibly attributed to the increasing amorphous components caused by TiO 2 involvement. The long term immersing test in SBF is consistent with the electrochemical test, with the coated Mg alloy obviously slowing down the biodegradation rate, meanwhile accompanied by the increasing damage trends in the coatings modified by 5 and 10 vol.% titania sol.

  20. Nitrous oxide production in intermittently aerated Partial Nitritation-Anammox reactor: oxic N2O production dominates and relates with ammonia removal rate

    DEFF Research Database (Denmark)

    Blum, Jan-Michael; Jensen, Marlene Mark; Smets, Barth F.

    2018-01-01

    Emissions of the greenhouse gas nitrous oxide from the Partial Nitritation-Anammox process are of concern and can determine the carbon footprint of the process. In order to reduce nitrous oxide emissions intermittent aeration regimes have been shown to be a promising mode of operation, possibly due...

  1. Effect of Graphene Oxide (GO on the Morphology and Microstructure of Cement Hydration Products

    Directory of Open Access Journals (Sweden)

    Liguo Wang

    2017-12-01

    Full Text Available In this study, the effects of graphene oxide (GO on the microstructure of cement mortars were studied using scanning electron microscopy (SEM, thermogravimetric (TG, and X-ray diffraction (XRD techniques. Cement mortar samples with different proportions of GO (0.02, 0.04, 0.06, and 0.08 wt % based on the weight of cement were prepared. The test results showed that GO affected the crystallization of cement hydration products, C–S–H (calcium silicate hydrate is the main hydrate product and CH (calcium hydroxide. The morphology of hydration products changed with the increase of GO content. Furthermore, the results of XRD analyses showed that the diffraction peak intensity and the crystal grain size of CH (001, (100, (101, and (102 for GO samples increased considerably compared with the control sample. Based on the results, it can be understood that GO can modify the crystal surface of CH, leading to the formation of larger crystals.

  2. Microstructural evaluation of ceria-samaria-gadolinia-nickel oxide composite after reduction in hydrogen atmosphere

    International Nuclear Information System (INIS)

    Arakaki, A. R.; Yoshito, W.K.; Ussui, V.; Lazar, D.R.R.

    2012-01-01

    The ceria-samaria-gadolinia-nickel composite (Ni-SGDC), used as Solid Oxide Fuel Cell (SOFC) anode, was obtained by 'in situ' reduction of NiO-SGDC, with composition Ce 0,8 (SmGd) 0,2 O 1,9 /NiO and mass proportion 40:60%. The composite was produced by hydroxides coprecipitation using CTAB surfactant, followed by solvothermal treatment in butanol, calcination at 600 deg C, pressing and sintering at 1350 deg C for 1 h. The composite reduction kinetic was evaluated in a tubular furnace under dynamic atmosphere of 4% H2 /Air, fixing the temperature at 900 deg C and time between 10 and 120 minutes. The microstructural characterization was performed by optical and scanning electron microscopy. The samples were characterized either by X-ray diffraction and density measurements by immersion technique in water. It was verified that the NiO reduced fraction reached values between 80 and 90% and the achieved porosity (about 30%) is acceptable to a good anode performance (author)

  3. Microstructure and phase composition of sputter-deposited zirconia-yttria films

    International Nuclear Information System (INIS)

    Knoll, R.W.; Bradley, E.R.

    1983-11-01

    Thin ZrO 2 -Y 2 O 3 coatings ranging in composition from 3 to 15 mole % Y 2 O 3 were produced by rf sputter deposition. This composition range spanned the region on the equilibrium ZrO 2 -Y 2 O 3 phase diagram corresponding to partially stabilized zirconia (a mixture of tetragonal ZrO 2 and cubic solid solution). Microstructural characteristics and crystalline phase composition of as-deposited and heat treated films (1100 0 C and 1500 0 C) were determined by transmission electron microscopy (TEM) and by x-ray diffraction (XRD). Effects of substrate bias (0 approx. 250 volts), which induced ion bombardment of the film during growth, were also studied. The as-deposited ZrO 2 -Y 2 O 3 films were single phase over the composition range studied, and XRD data indicated considerable local atomic disorder in the lattice. Films produced at low bias contained intergranular voids, pronounced columnar growth, and porosity between columns. At high bias, the microstructure was denser, and films contained high compressive stress. After heat treatment, all deposits remained single phase, therefore a microstructure and precipitate distribution characteristic of toughened, partially stabilized zirconia appear to be difficult to achieve in vapor deposited zirconia coatings

  4. High temperature mechanisms and kinetics of SiC oxidation under low partial pressures of oxygen: application to the fuel cladding of gas fast reactors

    International Nuclear Information System (INIS)

    Hun, N.

    2011-01-01

    Gas Fast Reactor (GFR) is one of the different Generation IV concepts under investigation for energy production. SiC/SiC composites are candidates of primary interest for a GFR fuel cladding use, thanks to good corrosion resistance among other properties. The mechanisms and kinetics of SiC oxidation under operating conditions have to be identified and quantified as the corrosion can decrease the mechanical properties of the composite. An experimental device has been developed to study the oxidation of silicon carbide under high temperature and low oxygen partial pressure. The results pointed out that not only parabolic oxidation, but also interfacial reactions and volatilization occur under such conditions. After determining the kinetics of each mechanism, as functions of oxygen partial pressure and temperature, the data are used for the modeling of the composites oxidation. The model will be used to predict the lifetime of the composite in operating conditions. (author) [fr

  5. Microstructure and mechanical properties of SiC materials

    International Nuclear Information System (INIS)

    Yarahmadi, M.

    1985-01-01

    The effect of the microstructure on the mechanical properties of SiC materials of different chemical composition (SSiC, SiSiC, and RSiC) was investigated. Furthermore, the creep strength was determined on oxidized samples and on non-pretreated samples. (HSCH)

  6. Numerical evaluation of micro-structural parameters of porous supports in metal-supported solid oxide fuel cells

    DEFF Research Database (Denmark)

    Reiss, Georg; Frandsen, Henrik Lund; Brandstätter, Wilhelm

    2014-01-01

    Metallic supported Solid Oxide Fuel Cells (SOFCs) are considered as a durable and cost effective alternative to the state-of-the-art ceramic supported cell designs. In order to understand the mass and charge transport in the metal-support of this new type of cell a novel technique involving X......-ray tomography and micro-structural modelling is presented in this work. The simulation technique comprises a novel treatment of the boundary conditions, which leads to more accurate effective transport parameters compared to those, which can be achieved with the conventional homogenisation procedures....... Furthermore, the porosity distribution in the metal-support was determined, which provided information about the inhomogeneous nature of the material. In addition to that, transport parameters for two identified, different dense layers of the metal-support are evaluated separately. The results...

  7. Initial microstructural study of a Ce-La alloy using electron backscattered diffraction

    International Nuclear Information System (INIS)

    Scott, Thomas B.; Younes, Charles M.; Ling, Michael; Jones, Christopher P.; Nicholson, John A.; Heard, Peter J.; Jenkins, Roderick

    2011-01-01

    Research highlights: → First ever successful EBSD microstructural analysis of Ce-La alloy. → Successful preparation using electro-polishing in the open laboratory. → Equiaxed grains 20-40 μm in size dominate the microstructure, with random orientations, relatively straight grain boundary contacts and no evidence for crystal twinning. → All grains matched to a fcc γ-phase. → Problematic presence of entrapped oxide particles. - Abstract: To better understand and exploit the unique electronic and structural properties of f-block metals and their alloys it is perceived that an improved knowledge of the microstructural characteristics and phase changes as a function of temperature and pressure, is necessary. For other different types of metallic systems, the use of electron back-scattered diffraction (EBSD) is becoming a common practice in order to obtain detailed microstructural information, but this has, as yet, been very limited in case of f-block metals. Because of their extreme affinity to oxygen and rapid surface reaction, EBSD studies of this metal-category are very sparse with only one work published on cerium metal providing an example of technical hurdles for a prerequisite oxide-free metal surface. Specifically the need to remove the oxide by ion etching was considered essential to enable a successful EBSD analysis. The current work presents the results of a first attempt to characterise the microstructure of a Ce-La alloy using EBSD. It demonstrates that high quality diffraction patterns and crystal orientation maps can be successfully obtained following a carefully controlled preparation of the alloy surface in the open laboratory by applying a simple and reproducible electro-polishing procedure without a further need for ion etching in vaccuo.

  8. Microstructures in the 6060 aluminium alloy after various severe plastic deformation treatments

    International Nuclear Information System (INIS)

    Adamczyk-Cieslak, Boguslawa; Mizera, Jaroslaw; Kurzydlowski, Krzysztof Jan

    2011-01-01

    This paper presents the results concerning the microstructural refinement of the industrial 6060 aluminium alloy processed by severe plastic deformation (SPD). The high level of plastic deformation was achieved using the three methods: hydrostatic extrusion (HE), equal channel angular extrusion (ECAE) and extrusion torsion (ET), which differed in the dynamics of the loading, intensity and homogeneity of the plastic strain field. Microstructure analyses were performed before and after SPD deformation using a transmission (TEM) and a scanning electron microscope (SEM). The refined microstructures were examined qualitatively and quantitatively by the stereological methods and computer image analyses. The microstructure of the industrial 6060 aluminium alloy after deformation was characterized by an average grain size of about 0.4 μm. The results show that the precipitates strongly affect the degree of refinement and the mechanism of microstructural transformations. During the SPD, the second phase particles break apart and homogenize. The HE method generates the largest increase of the volume fraction of the small primary particles. Moreover, the HE process is most effective in reducing the primary particle size. During HE and ECAE processes the second phase precipitates dissolve partially and change their shape. - Research Highlights: → SPD results in a significant increase in the density of the small primary particles. → SPD homogenizes the particle size distribution. → HE and ECAE processes bring nano-grains in the vicinity of the primary particles. → HE and ECAE processing results in the β' precipitates partial dissolutions. → During HE and ECAE processes the β' particles change their shape.

  9. Microstructural and mechanical characterization of the parabolic spring steel 51CrV4

    Energy Technology Data Exchange (ETDEWEB)

    Koemec, Aydin [TT Celikyay Co., Duezce (Turkey); Dikci, Kazim [TT Celikyay Co., Duezce (Turkey). Quality Dept.; Atapek, S. Hakan; Polat, Seyda; Aktas Celik, Guelsah [Kocaeli Univ. (Turkey). Dept. of Metallurgical and Materials Engineering

    2017-07-01

    Findings about the microstructural features of, spring steels are necessary for the producers to enhance their mechanical properties. There are several reports revealing the basic relation between microstructure and fatigue performance. However, the results are commonly obtained from universal test procedures and have limited use due to the lack of real service conditions. In this study, the microstructural features of 51CrV4 alloy, used as spring steel component, were investigated by metallographic examinations starting from raw material to the final product. Its fatigue behavior was investigated using a self-designed test machine and a test procedure approved by the automotive industry to simulate the service conditions. Fractographic examination of fatigue failed surface was carried out to specify the effect of microstructural features on the fracture. It was concluded that (i) both oxide and decarburization layers were minimized by shot peening and (ii) although tested samples had superior fatigue resistance and failed above 10{sup 5} cycles limit, oxide layer played a major role for crack initiation.

  10. Low temperature oxidation of hydrocarbons using an electrochemical reactor

    DEFF Research Database (Denmark)

    Ippolito, Davide

    conversion was a complex function of multiple variables: the microstructure of the backbone, the polarization resistance of the electrodes, both at OCV and under polarization, the electrical and morphological properties of the infiltrated material and the specific reaction conditions like the propene......This study investigated the use of a ceramic porous electrochemical reactor for the deep oxidation of propene. Two electrode composites, La0.85Sr0.15MnO3±d/Ce0.9Gd0.1O1.95 (LSM/CGO) and La0.85Sr0.15FeMnO3/Ce0.9Gd0.1O1.95 (LSF/CGO), were produced in a 5 single cells stacked configuration and used...... prolonged polarization was able to partially counteract the instability of the infiltrated Ce0.9Gd0.1O1.95. This project demonstrated the possibility to enhance the oxidation of propene by polarization in a porous ceramic reactor. The infiltration of different active materials helped to increase...

  11. Microstructures of poly(N-methylpyrrole) and their interaction with morphine

    Energy Technology Data Exchange (ETDEWEB)

    Teixeira-Dias, Bruno [Departament d' Enginyeria Quimica, ETSEIB, Universitat Politecnica de Catalunya, Av. Diagonal 647, 08028, Barcelona (Spain); Center for Research in Nanoengineering, Universitat Politecnica de Catalunya, Campus Sud, Edifici C' , C/Pasqual i Vila s/n, 08028, Barcelona (Spain); Aleman, Carlos, E-mail: carlos.aleman@upc.edu [Departament d' Enginyeria Quimica, ETSEIB, Universitat Politecnica de Catalunya, Av. Diagonal 647, 08028, Barcelona (Spain); Center for Research in Nanoengineering, Universitat Politecnica de Catalunya, Campus Sud, Edifici C' , C/Pasqual i Vila s/n, 08028, Barcelona (Spain); Estrany, Francesc [Center for Research in Nanoengineering, Universitat Politecnica de Catalunya, Campus Sud, Edifici C' , C/Pasqual i Vila s/n, 08028, Barcelona (Spain); Unitat de Quimica Industrial, EUETIB, Universitat Politecnica de Catalunya, Comte d' Urgell 187, 08036, Barcelona (Spain); Azambuja, Denise S. [Institute of Chemistry, Universidade Federal do Rio Grande do Sul, Av. Bento Goncalves 9500 - CEP 91501-970, Porto Alegre, RS (Brazil); Armelin, Elaine, E-mail: elaine.armelin@upc.edu [Departament d' Enginyeria Quimica, ETSEIB, Universitat Politecnica de Catalunya, Av. Diagonal 647, 08028, Barcelona (Spain); Center for Research in Nanoengineering, Universitat Politecnica de Catalunya, Campus Sud, Edifici C' , C/Pasqual i Vila s/n, 08028, Barcelona (Spain)

    2011-06-30

    Graphical abstract: . Display Omitted Highlights: > Poly(N-methylpyrrole)/poly(styrenesulfonic acid) hollow microstructures has been prepared using gas templates. > The dimensions, abundance and texture of the microstructures have been electrochemically controlled. > Poly(N-methylpyrrole)/poly(styrenesulfonic acid) microstructures act as efficient morphine sensors. - Abstract: Microstructures of poly(N-methylpyrrole) have been generated by direct electrochemical oxidation of N-methylpyrrole with poly(styrenesulfonic acid) in aqueous solution, using a micelle formation mechanism with gas bubble templates. These microstructures present a 'doughnut'-like morphology with diameters ranging from 20 to 100 {mu}m. Other anionic surfactants, such as camphorsulfonic acid and {beta}-naphthalenesulfonic acid, have been also employed, results evidencing that the morphology of the microstructures depends on the nature of the surfactant electrolytes. The dimensions, abundance and texture of the microstructures have been modulated by varying the surfactant molecules, the electrochemical technique, and the distance between the working and counter-electrode. The generated microstructures have been characterized using electrochemical techniques, Raman and infrared spectroscopies, scanning electron microscopy and atomic force microscopy. Hollow microstructures-containing films made of poly(N-methylpyrrole)/poly(styrenesulfonic acid), which present remarkable electroactivity and electrostability, has been proved to interact with morphine molecules. Thus, systems based on this prominent material show a high ability to capture the drug molecules and to retain them for a long period of time.

  12. High-temperature Thermoelectric and Microstructural Characteristics of Ga Substituted on the Co-site in Cobalt-based Oxides

    DEFF Research Database (Denmark)

    Van Nong, Ngo; Yanagiya, S.; Sonne, Monica

    2011-01-01

    The effects of Ga substitution on the Co-site on the high-temperature thermoelectric properties and microstructure are investigated for the misfitlayered Ca3Co4O9 and the complex perovskite-related Sr3RECo4O10.5 (RE = rare earth) cobalt-based oxides. For both systems, substitution of Ga for Co...... results in a simultaneous increase in the Seebeck coefficient (S) and the electrical conductivity (σ), and the influence is more significant in the high temperature region. The power factor (S 2 σ) is thereby remarkably improved by Ga substitution, particularly at high temperatures. Texture factor......0.05O9 shows the best ZT value of 0.45 at 1200 K, which is about 87.5% higher than the nondoped one, a considerable improvement....

  13. Triple phase boundary specific pathway analysis for quantitative characterization of solid oxide cell electrode microstructure

    DEFF Research Database (Denmark)

    Jørgensen, Peter Stanley; Ebbehøj, Søren Lyng; Hauch, Anne

    2015-01-01

    of the pathways through which they can be reached. New methods for performing TPB specific pathway analysis on 3D image data are introduced, analyzing the pathway properties of each TPB site in the electrode structure. The methods seek to provide additional information beyond whether the TPB sites are percolating......The density and percolation of Triple phase boundary sites are important quantities in analyzing microstructures of solid oxide fuel cell electrodes from tomography data. However, these measures do not provide descriptions of the quality of the TPB sites in terms of the length and radius...... or not by also analyzing the pathway length to the TPB sites and the bottleneck radius of the pathway. We show how these methods can be utilized in quantifying and relating the TPB specific results to cell test data of an electrode reduction protocol study for Ni/Scandia-and-Yttria-doped-Zirconia (Ni...

  14. Alumina composites for oxide/oxide fibrous monoliths

    International Nuclear Information System (INIS)

    Cruse, T. A.; Polzin, B. J.; Picciolo, J. J.; Singh, D.; Tsaliagos, R. N.; Goretta, K. C.

    2000-01-01

    Most work on ceramic fibrous monoliths (FMs) has focused on the Si 3 N 4 /BN system. In an effort to develop oxidation-resistant FMs, several oxide systems have recently been examined. Zirconia-toughened alumina and alumina/mullite appear to be good candidates for the cell phase of FMs. These composites offer higher strength and toughness than pure alumina and good high-temperature stability. By combining these oxides, possibly with a weaker high-temperature oxide as the cell-boundary phase, it should be possible to product a strong, resilient FM that exhibits graceful failure. Several material combinations have been examined. Results on FM fabrication and microstructural development are presented

  15. A study on the polymer precursor formation and microstructure evolution of square-shaped (La{sub 0.5}Ba{sub 0.5})(Mn{sub 0.5}Fe{sub 0.5})O{sub 3} ceramic nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Romero, M.; Pardo, H.; Faccio, R.; Suescun, L.; Fernandez-Werner, L.; Mombru, A.W. [Univ. de la Republica, Montevideo (Uruguay). Cryssmat-Lab/Centro NanoMat; Univ. de la Republica, Montevideo (Uruguay). Centro Interdisciplinario de Nanotecnologia, Quimica y Fisica de Materiales; Vazquez, S.; Laborda, I. [Univ. de la Republica, Montevideo (Uruguay). Cryssmat-Lab/Centro NanoMat; Acosta, A. [Univ. de la Republica, Montevideo (Uruguay). Catedra de Quimica Inorganica; Castiglioni, J. [Univ. de la Republica, Montevideo (Uruguay). Catedra de Fisicoquimica

    2015-07-01

    The polymer precursor formation and the growth mechanism of (La{sub 0.5}Ba{sub 0.5})(Mn{sub 0.5}Fe{sub 0.5})O{sub 3} ceramic nanoparticles have been studied. First, we focused on the influence of isolated metals (La, Ba, Mn, Fe) on the polymer precursor formation by means of Raman, FT-IR, scanning electron microscopy and differential scanning calorimetry, showing that the presence of metal ions, especially iron, increases the oxidation rate of the polymer precursor, while the presence of barium leads to a higher degree of polymerization, preventing partial oxidation of the polymer at low temperatures and allowing the presence of nitrates at the combustion stage. Nevertheless, when all metals are present, the polymer precursor showed a largely homogeneous microstructure with a global average influence from all cations. Finally,we studied the microstructure evolution of nanoparticles obtained after calcination above 700 C. SAXS and TEM analysis suggests that the formation of square-shaped nanoparticles below 900 C and coalescence leads to the formation of larger-sized and round-shaped nanoparticles at 900 C.

  16. Microstructure of rapidly solidified Nb-based pre-alloyed powders for additive manufacturing

    Energy Technology Data Exchange (ETDEWEB)

    Guo, Yueling; Jia, Lina, E-mail: jialina@buaa.edu.cn; Kong, Bin; Zhang, Shengnan; Zhang, Fengxiang; Zhang, Hu

    2017-07-01

    Highlights: • Sphere shaped Nb-37Ti-13Cr-2Al-1Si pre-alloyed powders were prepared by PREP. • An oxide layer with a thickness of 9.39 nm was generated on the powder surface. • The main phases of the pre-alloyed powders were Nbss and Cr{sub 2}Nb. • SDAS increased and microhardness decreased with the increase of powder size. • Microstructure of powders evolved into large grains from dendrite structures after HT. - Abstract: For powder-based additive manufacturing, sphere-shaped Nb-37Ti-13Cr-2Al-1Si pre-alloyed powders were prepared by plasma rotating electrode processing (PREP). The microstructure, surface oxidation and microhardness of the pre-alloyed powders were systematically investigated. Results showed that the main phases were Nb solid solution (Nbss) and Cr{sub 2}Nb. The Cr{sub 2}Nb phases were further determined using transmission electron microscopy (TEM). Fine dendrite structures were observed in the as-fabricated pre-alloyed powders, which transformed to large grains after heat treatment (HT) at 1450 °C for 3 h. With the increase of powder size, the secondary dendrite arm spacing (SDAS) increased and the microhardness (HV) decreased. A clean powder surface free of oxide particles was obtained by PREP and an oxide layer with 9.39 nm in thickness was generated on the powder surface. Compared with Cr- and Nb-oxides, more Ti-oxides were formed on outmost powder surface with a higher content of Ti (up to 47.86 at.%). The differences upon the microstructure and microhardness of the pre-alloyed powders with different sizes were discussed.

  17. Microstructural characterization of Ni/YSZ based SOFC anodes after cyclic reduction and oxidation using electron microscopy

    International Nuclear Information System (INIS)

    Waldbillig, D.; He, A.; Ivey, D.

    2003-01-01

    The effect of redox cycling on the microstructure, of an SOFC anode, was studied using two approaches. Bulk samples were redox cycled and then examined in the SEM. In addition, electron transparent samples were prepared, redox cycled, and then examined in the TEM. Significant microstructural changes were observed. The anode in the as received condition consists of NiO particles several microns in size, YSZ grains about one micron in size and intergranular porosity. After the first reduction, the overall Ni grain size remains the same as the consumed NiO and epitaxial growth of Ni crystals on NiO grains is observed. The amount of intergranular porosity increases and very fine (50 nm) intragranular pores are formed throughout the Ni grains. This increase in the amount of porosity is expected due to the large volume change that occurs upon reduction. When samples are reoxidized the NiO particles in the SEM images appear spongy with much smaller pores than the as received, oxidized samples. The reoxidized anode consists of fine (<100 nm), randomly oriented grains of NiO. The grain refinement that occurs upon reoxidation is likely due to the large number of intragranular pores that occur upon reduction, which serve as nucleation sites. Rereduced samples were also very fine grained (<200 nm) and contained significant amounts of small intergranular porosity. The YSZ grains were unaffected by the redox cycles. (author)

  18. Characterization of microstructure of A508III/309L/308L weld and oxide films formed in deaerated high-temperature water

    Science.gov (United States)

    Xiong, Qi; Li, Hongjuan; Lu, Zhanpeng; Chen, Junjie; Xiao, Qian; Ma, Jiarong; Ru, Xiangkun

    2018-01-01

    The microstructure of A508III/309L/308L weld clad and the properties of the oxide films formed in simulated pressurized water reactor primary water at 290 °C were characterized. The A508III heat-affected zone (HAZ) consisted primarily of a decarburization zone with ferrite near the fusion line and a following pearlite structure with fine grains. A high hardness region in the HAZ could be the result of C-enrichment. M23C6 and M7C3 precipitates were observed in element transition zone. 308L stainless steel (SS) containing ∼ 12% ferrites exhibited both ferritic-austenitic solidification mode (FA mode, δ→γ) and austenitic-ferritic solidification mode (AF mode, γ→δ), whereas 309L SS containing ∼ 9% ferrites exhibited only FA mode. The A508III surface oxide film was mainly Fe3O4 in deaerated high-temperature water. The coarse grain zone covered with few oxide particles was different from other types of film on the other region of HAZ and the bulk zone. More pitting appears on 309L SS after immersion in deaerated high-temperature water due to the dissolution of inclusions. SS surface oxide films consisted primarily of spinels. The oxide film on SS was divided into two layers. Ni was concentrated mainly at the oxide/substrate interface. The oxide film formed on 309L was thicker than that on the 308L. The ferrite in the stainless steel could improve the oxidation resistance.

  19. Temperature oscillations in methanol partial oxidation reactor for the production of hydrogen

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jinsu; Byeon, Jeonguk; Seo, Il Gyu; Lee, Hyun Chan; Kim, Dong Hyun; Lee, Jietae [Kyungpook National University, Daegu (Korea, Republic of)

    2013-04-15

    Methanol partial oxidation (POX) is a well-known reforming reaction for the production of hydrogen from methanol. Since POX is relatively fast and highly exothermic, this reforming method will be efficient for the fast start-up and load-following operation. However, POX generates hot spots around catalyst and even oscillations in the reactor temperature. These should be relieved for longer operations of the reactor without catalyst degradations. For this, temperature oscillations in a POX reactor are investigated experimentally. Various patterns of temperature oscillations according to feed flow rates of reactants and reactor temperatures are obtained. The bifurcation phenomena from regular oscillations to chaotic oscillations are found as the methanol flow rate increases. These experimental results can be used for theoretical analyses of oscillations and for designing safe reforming reactors.

  20. Temperature oscillations in methanol partial oxidation reactor for the production of hydrogen

    International Nuclear Information System (INIS)

    Kim, Jinsu; Byeon, Jeonguk; Seo, Il Gyu; Lee, Hyun Chan; Kim, Dong Hyun; Lee, Jietae

    2013-01-01

    Methanol partial oxidation (POX) is a well-known reforming reaction for the production of hydrogen from methanol. Since POX is relatively fast and highly exothermic, this reforming method will be efficient for the fast start-up and load-following operation. However, POX generates hot spots around catalyst and even oscillations in the reactor temperature. These should be relieved for longer operations of the reactor without catalyst degradations. For this, temperature oscillations in a POX reactor are investigated experimentally. Various patterns of temperature oscillations according to feed flow rates of reactants and reactor temperatures are obtained. The bifurcation phenomena from regular oscillations to chaotic oscillations are found as the methanol flow rate increases. These experimental results can be used for theoretical analyses of oscillations and for designing safe reforming reactors

  1. Microstructural studies on steam oxidised Zr-2.5%Nb pressure tube under simulated LOCA condition

    International Nuclear Information System (INIS)

    Banerjee, Suparna; Sawarn, Tapan K.; Pandit, K.M.; Anantharaman, S.; Srivastava, D.; Sah, D.N.

    2013-03-01

    Study of the microstructural evolution of Zr-2.5%Nb pressure tube material of Indian Pressurized Heavy Water Reactors (PHWRs) due to steam oxidation at high temperature (in the range 500-1050°C) was carried out on pressure tube coupons. Hydrogen pick up was less than 55 ppm in the samples oxidized at temperatures up to 850°C but high (250-400 ppm) in the samples oxidized in the β phase region (900°C and above). The microstructure of the samples oxidized above the α-Zr/β-Zr transition temperature showed from the surface inwards sequentially the presence of an oxide layer, an underlying oxygen stabilized α-Zr layer and a prior β-Zr phase containing hydride precipitates. An increase in the hardness was observed near the oxide-metal interface in the coupons oxidized above 900°C, due to formation of oxygen stabilized α-Zr layer. Higher hardness was also observed in the base metal in the samples oxidized at 1000 and 1050°C (author)

  2. Microstructure formation and corrosion behaviour in HVOF-sprayed Inconel 625 coatings

    International Nuclear Information System (INIS)

    Zhang, D.; Harris, S.J.; McCartney, D.G.

    2003-01-01

    The nickel-based alloy Inconel 625 was thermally sprayed by two different variants of the high velocity oxy-fuel process. In this study, coatings deposited by a liquid-fuelled gun were compared with those produced by a gas-fuelled system; in general, the former generates higher particle velocities but lower particle temperatures. Investigations into the microstructural evolution of the coatings, using scanning electron microscopy and X-ray diffraction, are presented along with results on their aqueous corrosion behaviour, obtained from salt spray and potentiodynamic tests. It is inferred from coating microstructures that, during spraying, powder particles generally comprised three separate zones as follows: fully melted regions; partially melted zones; and an unmelted core. However, the relative proportions formed in an individual powder particle depended on its size, trajectory through the gun, the gas dynamics (velocity/temperature) of the thermal spray gun and the type of gun employed. Cr 2 O 3 was the principal oxide phase formed during spraying and the quantity appeared to be directly related to the degree to which particles were melted. The salt spray test provides a sensitive means of determining the presence of interconnected porosity in coatings and those produced with the liquid-fuelled gun exhibited reduced interconnected porosity and increased corrosion resistance compared with deposits obtained from the gas-fuelled system. In addition, potentiodynamic tests revealed that passive current densities are 10-20 times lower in liquid-fuel coatings than in those sprayed with the gas-fuelled gun

  3. A finite element framework for multiscale/multiphysics analysis of structures with complex microstructures

    Science.gov (United States)

    Varghese, Julian

    This research work has contributed in various ways to help develop a better understanding of textile composites and materials with complex microstructures in general. An instrumental part of this work was the development of an object-oriented framework that made it convenient to perform multiscale/multiphysics analyses of advanced materials with complex microstructures such as textile composites. In addition to the studies conducted in this work, this framework lays the groundwork for continued research of these materials. This framework enabled a detailed multiscale stress analysis of a woven DCB specimen that revealed the effect of the complex microstructure on the stress and strain energy release rate distribution along the crack front. In addition to implementing an oxidation model, the framework was also used to implement strategies that expedited the simulation of oxidation in textile composites so that it would take only a few hours. The simulation showed that the tow architecture played a significant role in the oxidation behavior in textile composites. Finally, a coupled diffusion/oxidation and damage progression analysis was implemented that was used to study the mechanical behavior of textile composites under mechanical loading as well as oxidation. A parametric study was performed to determine the effect of material properties and the number of plies in the laminate on its mechanical behavior. The analyses indicated a significant effect of the tow architecture and other parameters on the damage progression in the laminates.

  4. Cryo-SEM studies of latex/ceramic nanoparticle coating microstructure development.

    Science.gov (United States)

    Luo, Hui; Scriven, L E; Francis, Lorraine F

    2007-12-15

    Cryogenic scanning electron microscopy (cryo-SEM) was used to investigate microstructure development of composite coatings prepared from dispersions of antimony-doped tin oxide (ATO) nanoparticles (approximately 30 nm) or indium tin oxide (ITO) nanoparticles (approximately 40 nm) and latex particles (polydisperse, D(v): approximately 300 nm). Cryo-SEM images of ATO/latex dispersions as-frozen show small clusters of ATO and individual latex particles homogeneously distribute in a frozen water matrix. In contrast, cryo-SEM images of ITO/latex dispersions as-frozen show ITO particles adsorb onto latex particle surfaces. Electrostatic repulsion between negatively charged ATO and negatively charged latex particles stabilizes the ATO/latex dispersion, whereas in ITO/latex dispersion, positively charged ITO particles are attracted onto surfaces of negatively charged latex particles. These results are consistent with calculations of interaction potentials from past research. Cryo-SEM images of frozen and fractured coatings reveal that both ceramic nanoparticles and latex become more concentrated as drying proceeds; larger latex particles consolidate with ceramic nanoparticles in the interstitial spaces. With more drying, compaction flattens the latex-latex particle contacts and shrinks the voids between them. Thus, ceramic nanoparticles are forced to pack closely in the interstitial spaces, forming an interconnected network. Finally, latex particles partially coalesce at their flattened contacts, thereby yielding a coherent coating. The research reveals how nanoparticles segregate and interconnect among latex particles during drying.

  5. Advanced STEM/EDX investigation on an oxide scale thermally grown on a high-chromium iron–nickel alloy under very low oxygen partial pressure

    International Nuclear Information System (INIS)

    Latu-Romain, L.; Madi, Y.; Mathieu, S.; Robaut, F.; Petit, J.-P.; Wouters, Y.

    2015-01-01

    Highlights: • A scale grown on a high-chromium iron–nickel alloy under low oxygen partial pressure was studied. • STEM-EDX maps at high resolution on a transversal thin lamella have been conducted. • The real complexity of the oxide layer has been highlighted. • These results explain the elevated number of semiconducting contributions. - Abstract: A thermal oxide scale has been grown on a high-chromium iron-nickel alloy under very low oxygen partial pressure (1050 °C, 10"−"1"0 Pa). In this paper, a special attention has been paid to morphological and chemical characterizations of the scale by scanning transmission electron microscopy and energy dispersive X-ray analysis at high resolution on a cross-section thin lamella beforehand prepared by using a combined focused ion beam/scanning electron microscope instrument. The complexity of the oxide layer is highlighted, and the correlation between the present results and the ones of a photoelectrochemical study is discussed.

  6. A framework for automatic segmentation in three dimensions of microstructural tomography data

    DEFF Research Database (Denmark)

    Jørgensen, Peter Stanley; Hansen, Karin Vels; Larsen, Rasmus

    2010-01-01

    Routine use of quantitative three dimensional analysis of material microstructure by in particular, focused ion beam (FIB) serial sectioning is generally restricted by the time consuming task of manually delineating structures within each image slice or the quality of manual and automatic...... segmentation schemes. We present here a framework for performing automatic segmentation of complex microstructures using a level set method. The technique is based on numerical approximations to partial differential equations to evolve a 3D surface to capture the phase boundaries. Vector fields derived from...

  7. Microstructure characteristic of ceramic coatings fabricated on magnesium alloys by micro-arc oxidation in alkaline silicate solutions

    Energy Technology Data Exchange (ETDEWEB)

    Guo, H.F. [Department of Applied Chemistry, Harbin Institute of Technology, Harbin 150001 (China)]. E-mail: Guohf@hit.edu.cn; An, M.Z. [Department of Applied Chemistry, Harbin Institute of Technology, Harbin 150001 (China)]. E-mail: mzan@hit.edu.cn; Huo, H.B. [Department of Applied Chemistry, Harbin Institute of Technology, Harbin 150001 (China); Xu, S. [Department of Applied Chemistry, Harbin Institute of Technology, Harbin 150001 (China); Wu, L.J. [Department of Applied Chemistry, Harbin Institute of Technology, Harbin 150001 (China)

    2006-09-15

    Micro-arc oxidation (MAO) of AZ31B magnesium alloys was studied in alkaline silicate solutions at constant applied current densities. The microstructure, phase composition and elemental distribution of ceramic coatings were investigated using scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy-dispersive spectroscopy (EDX). There are two inflections in the voltage-time response, three regions were identifiable and each of the regions was almost linear. The pores with different shapes distributed all over the coating surface, the number of the pores was decreasing, while the diameter was apparently increasing with prolonged MAO treatment time. There were also cracks on the coating surface, resulting from the rapid solidification of the molten oxide. The ceramic coating was comprised of two layers, an outer loose layer and an inner dense layer. The ceramic coating was mainly composed of forsterite phase Mg{sub 2}SiO{sub 4} and MgO; the formation of MgO was similar to conversional anodizing technology, while formation of Mg{sub 2}SiO{sub 4} was attributed to a high temperature phase transformation reaction. Presence of Si and O indicated that the electrolyte components had intensively incorporated into coatings.

  8. Microstructure and mechanical properties of an oxide dispersion strengthened ferritic steel by a new fabrication route

    International Nuclear Information System (INIS)

    Guo Lina; Jia Chengchang; Hu Benfu; Li Huiying

    2010-01-01

    A reduced activation oxide dispersion strengthened (ODS) ferritic steel with nominal composition of Fe-12Cr-2.5W-0.25Ti-0.2V-0.4Y 2 O 3 (designated 12Cr-ODS) was produced by using EDTA-citrate complex method to synthesize and add Y 2 O 3 particles to an argon atomized steel powder, followed by hot isostatic pressing at 1160 deg. C for 3 h under the pressure of 130 MPa, forging at 1150 deg. C, and heat treatment at 1050 deg. C for 2 h. The microstructure, tensile, and Charpy impact properties of the 12Cr-ODS steel were investigated. Transmission electron microscopy studies indicate that the 12Cr-ODS steel exhibits the characteristic ferritic structure containing few dislocations. Tensile characterization has shown that the 12Cr-ODS steel has superior tensile strength accompanied by good elongation at room temperature and 550 deg. C. The material exhibits very attractive Charpy impact properties with upper shelf energy of 22 J and a ductile-to-brittle transition temperature (DBTT) of about -15 deg. C. The formation of small, equiaxed grains and fine dispersion of oxide particles are the main reasons for the good compromise between tensile strength and impact properties.

  9. Microstructure and mechanical properties of an oxide dispersion strengthened ferritic steel by a new fabrication route

    Energy Technology Data Exchange (ETDEWEB)

    Guo Lina, E-mail: guoln702@yahoo.com.cn [School of Material Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Jia Chengchang; Hu Benfu; Li Huiying [School of Material Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China)

    2010-07-25

    A reduced activation oxide dispersion strengthened (ODS) ferritic steel with nominal composition of Fe-12Cr-2.5W-0.25Ti-0.2V-0.4Y{sub 2}O{sub 3} (designated 12Cr-ODS) was produced by using EDTA-citrate complex method to synthesize and add Y{sub 2}O{sub 3} particles to an argon atomized steel powder, followed by hot isostatic pressing at 1160 deg. C for 3 h under the pressure of 130 MPa, forging at 1150 deg. C, and heat treatment at 1050 deg. C for 2 h. The microstructure, tensile, and Charpy impact properties of the 12Cr-ODS steel were investigated. Transmission electron microscopy studies indicate that the 12Cr-ODS steel exhibits the characteristic ferritic structure containing few dislocations. Tensile characterization has shown that the 12Cr-ODS steel has superior tensile strength accompanied by good elongation at room temperature and 550 deg. C. The material exhibits very attractive Charpy impact properties with upper shelf energy of 22 J and a ductile-to-brittle transition temperature (DBTT) of about -15 deg. C. The formation of small, equiaxed grains and fine dispersion of oxide particles are the main reasons for the good compromise between tensile strength and impact properties.

  10. Isothermal oxidation behavior of ternary Zr-Nb-Y alloys at high temperature

    Energy Technology Data Exchange (ETDEWEB)

    Prajitno, Djoko Hadi, E-mail: djokohp@batan.go.id [Research Center for Nuclear Materials and Radiometry, Jl. Tamansari 71, Bandung 40132 (Indonesia); Soepriyanto, Syoni; Basuki, Eddy Agus [Metallurgy Engineering, Institute Technology Bandung, Jl. Ganesha 10, Bandung 40132 (Indonesia); Wiryolukito, Slameto [Materials Engineering, Institute Technology Bandung, Jl. Ganesha 10, Bandung 40132 (Indonesia)

    2014-03-24

    The effect of yttrium content on isothermal oxidation behavior of Zr-2,5%Nb-0,5%Y, Zr-2,5%Nb-1%Y Zr-2,5%Nb-1,5%Y alloy at high temperature has been studied. High temperature oxidation carried out at tube furnace in air at 600,700 and 800°C for 1 hour. Optical microscope is used for microstructure characterization of the alloy. Oxidized and un oxidized specimen was characterized by x-ray diffraction. In this study, kinetic oxidation of Zr-2,5%Nb with different Y content at high temperature has also been studied. Characterization by optical microscope showed that microstructure of Zr-Nb-Y alloys relatively unchanged and showed equiaxed microstructure. X-ray diffraction of the alloys depicted that the oxide scale formed during oxidation of zirconium alloys is monoclinic ZrO2 while unoxidised alloy showed two phase α and β phase. SEM-EDS examination shows that depletion of Zr composition took place under the oxide layer. Kinetic rate of oxidation of zirconium alloy showed that increasing oxidation temperature will increase oxidation rate but increasing yttrium content in the alloys will decrease oxidation rate.

  11. PuMA: the Porous Microstructure Analysis software

    Science.gov (United States)

    Ferguson, Joseph C.; Panerai, Francesco; Borner, Arnaud; Mansour, Nagi N.

    2018-01-01

    The Porous Microstructure Analysis (PuMA) software has been developed in order to compute effective material properties and perform material response simulations on digitized microstructures of porous media. PuMA is able to import digital three-dimensional images obtained from X-ray microtomography or to generate artificial microstructures. PuMA also provides a module for interactive 3D visualizations. Version 2.1 includes modules to compute porosity, volume fractions, and surface area. Two finite difference Laplace solvers have been implemented to compute the continuum tortuosity factor, effective thermal conductivity, and effective electrical conductivity. A random method has been developed to compute tortuosity factors from the continuum to rarefied regimes. Representative elementary volume analysis can be performed on each property. The software also includes a time-dependent, particle-based model for the oxidation of fibrous materials. PuMA was developed for Linux operating systems and is available as a NASA software under a US & Foreign release.

  12. SUPERCRITICAL WATER PARTIAL OXIDATION PHASE I - PILOT-SCALE TESTING / FEASIBILITY STUDIES FINAL REPORT

    Energy Technology Data Exchange (ETDEWEB)

    SPRITZER,M; HONG,G

    2005-01-01

    Under Cooperative Agreement No. DE-FC36-00GO10529 for the Department of Energy, General Atomics (GA) is developing Supercritical Water Partial Oxidation (SWPO) as a means of producing hydrogen from low-grade biomass and other waste feeds. The Phase I Pilot-scale Testing/Feasibility Studies have been successfully completed and the results of that effort are described in this report. The Key potential advantages of the SWPO process is the use of partial oxidation in-situ to rapidly heat the gasification medium, resulting in less char formation and improved hydrogen yield. Another major advantage is that the high-pressure, high-density aqueous environment is ideal for reaching and gasifying organics of all types. The high water content of the medium encourages formation of hydrogen and hydrogen-rich products and is especially compatible with high water content feeds such as biomass materials. The high water content of the medium is also effective for gasification of hydrogen-poor materials such as coal. A versatile pilot plant for exploring gasification in supercritical water has been established at GA's facilities in San Diego. The Phase I testing of the SWPO process with wood and ethanol mixtures demonstrated gasification efficiencies of about 90%, comparable to those found in prior laboratory-scale SCW gasification work carreid out at the University of Hawaii at Manoa (UHM) as well as other biomass gasification experience with conventional gasifiers. As in the prior work at UHM, a significant amount of the hydrogen found in the gas phase products is derived from the water/steam matrix. The studies at UHM utilized an indirectly heated gasifier with an acitvated carbon catalyst. In contrast, the GA studies utilized a directly heated gasifier without catalyst, plus a surrogate waste fuel. Attainment of comparable gasification efficiencies without catalysis is an important advancement for the GA process, and opens the way for efficient hydrogen production from low

  13. Effect of chip size on mechanical property and microstructure of AZ91D magnesium alloy prepared by solid state recycling

    International Nuclear Information System (INIS)

    Hu Maoliang; Ji Zesheng; Chen Xiaoyu; Zhang Zhenkao

    2008-01-01

    In this study, different kinds of AZ91D magnesium alloy chips were prepared by solid state recycling. Mechanical properties and microstructures of the recycled specimens were investigated. Various microstructural analyses were performed using the techniques of optical microscopy, scanning electron microscopy and oxygen-nitrogen analysis. Microstructural observations revealed that all the recycled specimens consisted of fine grains due to dynamic recrystallization. The oxide precipitate content is closely related to the recycled chip size. Accumulated oxygen concentration linearly increases with the total surface area of the machined chips in the recycled specimens. Ambient oxide in the recycled specimen contributes to a higher ultimate tensile strength and a higher elongation to failure; however, excessive oxide in the recycled specimen may adversely affect the elongation to failure

  14. The partial pressure of oxygen affects biomarkers of oxidative stress in cultured rainbow trout (Oncorhynchus mykiss) hepatocytes.

    Science.gov (United States)

    Finne, E F; Olsvik, P A; Berntssen, M H G; Hylland, K; Tollefsen, K E

    2008-09-01

    Oxidative stress, the imbalance between production of reactive oxygen species and the cellular detoxification of these reactive compounds, is believed to be involved in the pathology of various diseases. Several biomarkers for oxidative stress have been proposed to serve as tools in toxicological and ecotoxicological research. Not only may exposure to various pro-oxidants create conditions of cellular oxidative stress, but hyperoxic conditions may also increase the production of reactive oxygen species. The objective of the current study was to determine the extent to which differences in oxygen partial pressure would affect biomarkers of oxidative stress in a primary culture of hepatocytes from rainbow trout (Oncorhynchus mykiss). Membrane integrity, metabolic activity, levels of total and oxidized glutathione (tGSH/GSSG) was determined, as well as mRNA expression levels of the antioxidant enzymes superoxide dismutase (SOD), catalase (CAT), glutathione peroxidase (GSH-Px), glutathione reductase (GSSG-R), gamma-glutamyl-cystein synthetase (GCS) and thioredoxin (TRX). The results show that different biomarkers of oxidative stress are affected when the cell culture is exposed to atmospheric oxygen, and that changes such as increased GSSG content and induction of GSSG-R and GSH-Px can be reduced by culturing the cells under lower oxygen tension. Oxygen tension may thus influence results of in vitro based cell research and is particularly important when assessing parameters in the antioxidant defence system. Further research is needed to establish the magnitude of this effect in different cellular systems.

  15. Effect of mass-transport limitations on the performance of a packed bed membrane reactor for partial oxidations. Intraparticle mass transport

    NARCIS (Netherlands)

    Sint Annaland, van M.; Kurten, U.; Kuipers, J.A.M.

    2007-01-01

    For partial oxidation systems, where the reaction order in oxygen of the formation rate of the target product is smaller than the reaction order in oxygen of the consecutive reaction rate toward the waste product, a packed bed membrane reactor can be applied to distributively dose oxygen along the

  16. Effect of Mass-Transport Limitations on the Performance of a Packed Bed Membrane Reactor for Partial Oxidations. Intraparticle Mass Transport

    NARCIS (Netherlands)

    van Sint Annaland, M.; Kurten, U.; Kuipers, J.A.M.

    2007-01-01

    For partial oxidation systems, where the reaction order in oxygen of the formation rate of the target product is smaller than the reaction order in oxygen of the consecutive reaction rate toward the waste product, a packed bed membrane reactor can be applied to distributively dose oxygen along the

  17. Influence of additives on the structure and microstructure of lanthanides and actinides oxalates

    International Nuclear Information System (INIS)

    Haidon, Blaise; Vitart, Anne-Lise; Rivenet, Murielle; Arab-Chapelet, Benedicte; Roussel, Pascal; Delahaye, Thibaud; Grandjean, Stephane; Abraham, Francis

    2015-07-01

    Oxalic conversion is a well-known process in the nuclear industry where it is used for precipitating plutonium as an oxalate thereafter calcinated into an oxide. As there is a strong relationship between the morphology of the oxalate precursor and that of the resulting oxide, it is of interest to control the oxalate structure and microstructure during the precipitation step. The influence of additives on the precipitation of neodymium (III) oxalates, non-radioactive analogs of actinides (III) oxalates, was explored. With the use of nitrilotri-methylphosphonic acid (NTMP), the structure and microstructure of the neodymium oxalates are different from that obtained without additive. (authors)

  18. Corrosion and characterisation of dual phase Mg–Li–Ca alloy in Hank’s solution: The influence of microstructural features

    International Nuclear Information System (INIS)

    Zeng, Rong-Chang; Sun, Lu; Zheng, Yu-Feng; Cui, Hong-Zhi; Han, En-Hou

    2014-01-01

    Highlights: •A schematic four-layered structural model of the natural oxide film has been constructed. •A novel concept for the Pilling–Bedworth ratios of chemical compounds is proposed. •Grain refinement in the microstructure leads to a shift from pitting corrosion to overall corrosion. •A method to characterise the corrosion rate of dual phase Mg–Li–Ca alloys is proposed. -- Abstract: The influence of the microstructure and the oxide film of the Mg–9.29Li–0.88Ca alloy on its corrosion behaviour was investigated using SEM, EPMA, XPS and corrosion measurements. The results demonstrated that the fine-grained microstructure improved the mechanical and corrosion resistance of the alloy and shifted pitting corrosion to overall corrosion. The oxide film contained a multi-layered structure, with the outer layer being enriched in lithium-bearing compounds; the interior layer predominantly consisting of oxides, hydroxides and carbonates of lithium and magnesium; and the bottom layer containing oxides. The Pilling–Bedworth ratio for chemical compounds was proposed, and the corrosion rates were characterised

  19. Modulating laser intensity profile ellipticity for microstructural control during metal additive manufacturing

    International Nuclear Information System (INIS)

    Roehling, Tien T.; Wu, Sheldon S.Q.; Khairallah, Saad A.; Roehling, John D.; Soezeri, S. Stefan; Crumb, Michael F.; Matthews, Manyalibo J.

    2017-01-01

    Additively manufactured (AM) metals are often highly textured, containing large columnar grains that initiate epitaxially under steep temperature gradients and rapid solidification conditions. These unique microstructures partially account for the massive property disparity existing between AM and conventionally processed alloys. Although equiaxed grains are desirable for isotropic mechanical behavior, the columnar-to-equiaxed transition remains difficult to predict for conventional solidification processes, and much more so for AM. In this study, the effects of laser intensity profile ellipticity on melt track macrostructures and microstructures were studied in 316L stainless steel. Experimental results were supported by temperature gradients and melt velocities simulated using the ALE3D multi-physics code. As a general trend, columnar grains preferentially formed with increasing laser power and scan speed for all beam profiles. However, when conduction mode laser heating occurs, scan parameters that result in coarse columnar microstructures using Gaussian profiles produce equiaxed or mixed equiaxed-columnar microstructures using elliptical profiles. By modulating spatial laser intensity profiles on the fly, site-specific microstructures and properties can be directly engineered into additively manufactured parts.

  20. Microstructure and mechanical properties of friction stir welded 9Cr ODS steel

    International Nuclear Information System (INIS)

    Min, Hyoung Kee; Kang, Suk Hoon; Noh, Sanghoon; Lee, Jung Gu; Jang, Jinsung; Kim, Tae Kyu

    2013-01-01

    It is well known that the welding of ODS steel with a conventional melting.solidification process is not adequate to reserve nano-oxide particles in the matrix homogeneously. To reserve nano-oxide particles in the matrix homogeneously, friction stir welding (FSW) is the most promising technique to join ODS alloys. In this study, the effects of FSW on the microstructure and mechanical properties of a ODS steel were studied to apply the FSW process to 9Cr ODS steels. Microstructures were observed by means of optical microscopy, electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). A tensile test and hardness test were carried out to the investigate mechanical properties. FSW could successfully produce defect-free welds on ODS plates. FSW produced a fine grain structure consisting of ferrite and martensite. Tensile strengths and elongations of the SZs were excellent at 298 K, compared to those of the BM. This study suggests that FSW might be an appropriate welding method of ODS steels. Oxide dispersion strengthened (ODS) ferritic-martensitic (FM) steel containing 9 wt%Cr is a promising candidate material for high temperature components operating in aggressive environments such as nuclear fusion and fission systems because of the excellent elevated temperature strength, corrosion and radiation resistance. These characteristics come from microstructures consisting of fine grains and nano-oxide particles dispersed in high number density. However, for more applications of ODS steel in nuclear systems, its weldability is the one of the barrier to be solved

  1. Low-fat frankfurters formulated with a healthier lipid combination as functional ingredient: microstructure, lipid oxidation, nitrite content, microbiological changes and biogenic amine formation.

    Science.gov (United States)

    Delgado-Pando, Gonzalo; Cofrades, Susana; Ruiz-Capillas, Claudia; Solas, Maria Teresa; Triki, Mehdi; Jiménez-Colmenero, Francisco

    2011-09-01

    Oil (healthier lipid combination of olive, linseed and fish oils)-in-water emulsions stabilized with different protein systems (prepared with sodium caseinate (SC), soy protein isolate (SPI), and microbial transglutaminase (MTG)) were used as pork backfat replacers in low-fat frankfurters. Microstructure, lipid oxidation, nitrite content, microbiological changes and biogenic amine formation of frankfurters were analyzed and found to be affected by the type of oil-in-water emulsion and by chilling storage (2° C, 41 days). Although the lipid oxidation levels attained were low, replacement of animal fat by healthier oil combinations in frankfurter formulation did promote a slight increase in lipid oxidation. Residual nitrite was affected (P nitrite was detectable in the product after processing and 17-46% at the end of storage. The microbial population was low in all formulations during chilling storage. Spermine was the most abundant amine (19-20 mg/kg), but similar in level to all samples. Copyright © 2011 Elsevier Ltd. All rights reserved.

  2. Microstructure and electrical properties of bismuth and bismuth oxide deposited by magnetron sputtering UBM

    International Nuclear Information System (INIS)

    Otalora B, D. M.; Dussan, A.; Olaya F, J. J.

    2015-01-01

    In this work, bismuth (Bi) and bismuth oxide (Bi 2 O 3 ) thin films were prepared, at room temperature, by Sputtering Unbalanced Magnetron (UBM - Unbalance Magnetron) technique under glass substrates. Microstructural and electrical properties of the samples were studied by X-ray diffraction (XRD) and System for Measuring Physical Properties - PPMS (Physical Property Measurement System). Dark resistivity of the material was measured for a temperature range between 100 and 400 K. From the XRD measurements it was observed a polycrystalline character of the Bi associated to the presence of phases above the main peak, 2θ = 26.42 grades and a growth governed by a rhombohedral structure. Crystal parameters were obtained for both compounds, Bi and Bi 2 O 3 . From the analysis of the spectra of the conductivity as a function of temperature, it was established that the transport mechanism that governs the region of high temperature (T>300 K) is thermally activated carriers. From conductivity measurements the activation energies were obtained of 0.0094 eV and 0.015 eV for Bi 2 O 3 and Bi, respectively. (Author)

  3. Electron microscopy study of microstructure of the oxide-dispersion-strengthed steel

    International Nuclear Information System (INIS)

    Xing, H.; Sun, J.; Zhou, Z.J.

    2010-01-01

    The microstructure of the ODS ferritic-martensitic steel with chemical composition of Fe-12Cr-2W-0.5Ti-0.2V-0.2Si-0.13C-0.35Y 2 O 3 wt% fabricated by MA and HIP has been investigated by TEM. The emphasis is focused on the structure and chemical composition of the fine ODS particles and inclusions. The results showed that two types of complex ODS particles such as Y-Ti-O and Y-Si-O with nanometer size distribute homogeneously and incoherently in the matrix of the steel. Additionally, large (Ti,V)N inclusions were observed in the steel. The results of microstructural characterization are discussed to correlate with the processing and mechanical properties of the ODS steel. (author)

  4. Adiabatic Fixed-Bed Gasification of Colombian Coffee Husk Using Air-Steam Blends for Partial Oxidation

    Directory of Open Access Journals (Sweden)

    Javier Bonilla

    2017-01-01

    Full Text Available The increasing energy consumption, mostly supplied by fossil fuels, has motivated the research and development of alternative fuel technologies to decrease the humanity’s dependence on fossil fuels, which leads to pollution of natural sources. Small-scale biomass gasification, using air-steam blends for partial oxidation, is a good alternative since biomass is a neutral carbon feedstock for sustainable energy generation. This research presents results obtained from an experimental study on coffee husk (CH gasification, using air-steam blends for partial oxidation in a 10 kW fixed-bed gasifier. Parametric studies on equivalence ratio (ER (1.53 < ER < 6.11 and steam-fuel (SF ratio (0.23 < SF < 0.89 were carried out. The results show that increasing both SF and ER results in a syngas rich in CH4 and H2 but poor in CO. Also, decreased SF and ER decrease the peak temperature (Tpeak at the gasifier combustion zone. The syngas high heating value (HHV ranged from 3112 kJ/SATPm3 to 5085 kJ/SATPm3 and its maximum value was obtained at SF = 0.87 and ER = 4.09. The dry basis molar concentrations of the species, produced under those operating conditions (1.53 < ER < 6.11 and 0.23 < SF < 0.89, were between 1.12 and 4.1% for CH4, between 7.77 and 13.49% for CO, and between 7.54 and 19.07% for H2. Other species were in trace amount.

  5. Microstructural evolution and rheological properties of AA6063 alloy produced by semisolid processing (SIMA and MHD)

    International Nuclear Information System (INIS)

    Bustos, O.; Leiva, R.; Sanchez, C.; Ordonez, S.; Carvajal, L.; Mannheim, R.

    2007-01-01

    In this work the rheological behaviour and the microstructural evolution of alloy AA6063 submitted to two different processing routes were studied: cold deformation and partial fusion (SIMA process) and magneto hydrodynamic stirring during its solidification (MHD process). The microstructural evolution during the isothermal holding was studied to verify if the Ost wald ripening mechanisms, classic growth and coalescence, are applicable to alloys made by these processing routes. The rheological properties were evaluated using a compression rheometer with parallel plates and digital capture of position and time data. Compression tests were made in short cylinders extracted from ingots that showed: a dendritic microstructure typical of as cast material, a typical microstructure of cold deformed material and a microstructure of materials obtained by MHD process. It was found that a globular microstructure has a typical behaviour of a fluid when being formed in semisolid state, contrary to the behaviour of the as cast dendritic microstructure. In addition, the mechanisms that operate in the microstructural evolution during the isothermal holdings were verified, through metallographic analysis. (Author) 29 refs

  6. Characterization of the oxide grown on Zr-20 Nb with different heat treatments in water at high temperature

    International Nuclear Information System (INIS)

    Olmedo, Ana M.; Bordoni, Roberto; Koenig, Patricia

    2003-01-01

    This work presents the corrosion behaviour of Zr-20 Nb alloy with different heat treatments. All the samples were annealed at 850 C degrees for one hour and cooled in air. After this heat treatment the sample coupons were aged at different temperatures and times. The corrosion kinetic of the different coupon samples were determined in water at 315 C degrees. The microstructure of the oxides were analysed using X-ray diffraction. The oxides grown in water steam at 400 C degrees, in coupons with a β Zr microstructure and in coupons aged in order to obtain a α Zr· + β Nb microstructure were also analysed. The oxides grown at the different temperatures and for all the microstructures were very adherent and black for all the times studied. The corrosion kinetics showed that the aging treatments decrease the corrosion rate of this material in degassed water at 315 C degrees and also in water steam at 400 C degrees. The greatest corrosion resistance is achieved for the equilibrium or near equilibrium microstructure of the samples and the presence of the · phase does not decrease the corrosion resistance of the material. The microstructure analysis of the oxides indicated that oxides grown on samples with β Zr microstructure are composed mainly by a Zr-Nb oxide of the type Nb 2 O 5· 6ZrO 2 , together with a small fraction of monoclinic ZrO 2 . Aging treatments produce an increase of the monoclinic phase and diminish the proportion of the mixed oxide. When the aging treatment gives the equilibrium or near equilibrium microstructure of α Zr· + β Nb , the oxide is composed mainly of monoclinic ZrO 2 , a small proportion of tetragonal component and also Nb 2 O 5 . (author)

  7. Effect of rare earth oxide addition on microstructures of ultra-fine WC-Co particulate reinforced Cu matrix composites prepared by direct laser sintering

    International Nuclear Information System (INIS)

    Gu Dongdong; Shen Yifu; Zhao Long; Xiao Jun; Wu Peng; Zhu Yongbing

    2007-01-01

    This paper presents a detailed investigation into the influence of the rare earth (RE) oxide (La 2 O 3 ) addition upon the densification and the resultant microstructural characteristics of the submicron WC-Co particulate reinforced Cu matrix composites prepared by direct laser sintering. It is found that the relative density of the laser sintered sample with 1 wt.% La 2 O 3 addition increased by 11.5% as compared with the sample without RE addition. The addition of RE element favored the microstructural refinement and improved the particulate dispersion homogeneity and the particulate/matrix interfacial coherence. The metallurgical functions of the RE element in improving the sinterability were also addressed. It shows that due to the unique properties of RE element such as high surface activity and large atomic radius, the addition of trace RE element can decrease the surface tension of the melt, resist the grain growth coarsening and increase the heterogeneous nucleation rate during laser sintering

  8. Electrochemical migration of tin in electronics and microstructure of the dendrites

    Energy Technology Data Exchange (ETDEWEB)

    Minzari, Daniel, E-mail: dmin@mek.dtu.d [Section for Materials and Surface Technology, Department for Mechanical Engineering, Technical University of Denmark (Denmark); Grumsen, Flemming Bjerg; Jellesen, Morten S.; Moller, Per; Ambat, Rajan [Section for Materials and Surface Technology, Department for Mechanical Engineering, Technical University of Denmark (Denmark)

    2011-05-15

    Graphical abstract: The electrochemical migration of tin in electronics forms dendritic structures, consisting of a metallic tin core, which is surrounded by oxide layers having various thickness. Display Omitted Research highlights: Electrochemical migration occurs if two conductors are connected by condensed moisture. Metallic ions are dissolved and grow in a dendritic structure that short circuit the electrodes. The dendrite consists of a metallic tin core with oxide layers of various thickness surrounding. Detailed microstructure of dendrites is investigated using electron microscopy. The dendrite microstructure is heterogeneous along the growth direction. - Abstract: The macro-, micro-, and nano-scale morphology and structure of tin dendrites, formed by electrochemical migration on a surface mount ceramic chip resistor having electrodes consisting of tin with small amounts of Pb ({approx}2 wt.%) was investigated by scanning electron microscopy and transmission electron microscopy including Energy dispersive X-ray spectroscopy and electron diffraction. The tin dendrites were formed under 5 or 12 V potential bias in 10 ppm by weight NaCl electrolyte as a micro-droplet on the resistor during electrochemical migration experiments. The dendrites formed were found to have heterogeneous microstructure along the growth direction, which is attributed to unstable growth conditions inside the micro-volume of electrolyte. Selected area electron diffraction showed that the dendrites are metallic tin having sections of single crystal orientation and lead containing intermetallic particles embedded in the structure. At certain areas, the dendrite structure was found to be surrounded by an oxide crust, which is believed to be due to unstable growth conditions during the dendrite formation. The oxide layer was found to be of nanocrystalline structure, which is expected to be formed by the dehydration of the hydrated oxide originally formed in solution ex-situ in ambient air.

  9. Comparative examination of the microstructure and high temperature oxidation performance of NiCrBSi flame sprayed and pack cementation coatings

    Science.gov (United States)

    Chaliampalias, D.; Vourlias, G.; Pavlidou, E.; Skolianos, S.; Chrissafis, K.; Stergioudis, G.

    2009-01-01

    Coatings formed from NiCrBSi powder were deposited by thermal spray and pack cementation processes on low carbon steel. The microstructure and morphology of the coatings were studied by scanning electron microscopy (SEM) and X-ray diffraction analysis (XRD). Flame sprayed coatings exhibited high porosity and were mechanically bonded to the substrate while pack cementation coatings were more compact and chemically bonded to the substrate. The microhardness and the high temperature oxidation resistance of the coated samples were evaluated by a Vickers microhardness tester and by thermogravimetric measurements (TG), respectively. Pack cementation coatings showed higher hardness and were more protective to high temperature environments than the flame sprayed coatings.

  10. Microstructure and high temperature oxidation resistance of in-situ synthesized TiN/Ti{sub 3}Al intermetallic composite coatings on Ti6Al4V alloy by laser cladding process

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Hongxi, E-mail: piiiliuhx@sina.com; Zhang, Xiaowei; Jiang, Yehua; Zhou, Rong

    2016-06-15

    High temperature anti-oxidation TiN/Ti{sub 3}Al intermetallic composite coatings were fabricated with the powder and AlN powder on Ti6Al4V titanium alloy surface by 6 kW transverse-flow CO{sub 2} laser apparatus. The chemical composition, morphology and microstructure of the TiN/Ti{sub 3}Al composite coatings were characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive spectrometer (EDS). In order to evaluate the high temperature oxidation resistance of TiN/Ti{sub 3}Al coating, the isothermal oxidation test was performed in a high temperature resistance furnace at 600 °C and 800 °C, respectively. The result shows that the composite coating has a rapidly solidified fine microstructure consisting of TiN primary phase (granular-like, flake-like or dendrites), with an even distribution in Ti{sub 3}Al matrix. It indicates that a physical and chemical reaction between Ti powder and AlN powder has completely occurred under the laser irradiation condition. In addition, the microhardness of the TiN/Ti3Al intermetallic composite coating is 3.4 times higher than that of the Ti6Al4V alloy substrate and reaches 844 HV{sub 0.2}. The high temperature oxidation behavior test reveals that the high temperature oxidation resistance of TiN/Ti{sub 3}Al composite coating is much better than that of titanium alloy substrate. The excellent high temperature oxidation resistance of TiN/Ti{sub 3}Al intermetallic composite coating is attributed to the formation of reinforced phases TiN, Al{sub 2}O{sub 3} and TiO{sub 2}. The laser cladding TiN/Ti{sub 3}Al intermetallic composite coating is anticipated to be a promising high temperature oxidation resistance coating for Ti6Al4V alloy. - Highlights: • In-situ TiN/Ti{sub 3}Al composite coating was synthesized on Ti6Al4V alloy by laser cladding. • The influence of Ti and AlN molar ratio on the microstructure of the coating was studied. • The TiN/Ti{sub 3}Al intermetallic

  11. Contribution to the study of the microstructure of uranium dioxide (1962)

    International Nuclear Information System (INIS)

    Porneuf, A.

    1960-05-01

    The microstructure of sintered uranium dioxide is studied in relation with several parameters, specially the sintering temperatures and atmospheres. The external surface and the internal microstructure of the sintered are examined, using fractography and ceramography. Various techniques for preparing surfaces (mechanical and electrolytic polishing) and for revealing the structure (chemical and anodic attack, ionic bombardment oxidation) have been experienced and compared. Patterns similar to those revealed in metals and probably related with interactions between dislocations and vacancies have been observed. (author) [fr

  12. Microstructural Study on Oxygen Permeated Arc Beads

    Directory of Open Access Journals (Sweden)

    Kuan-Heng Liu

    2015-01-01

    Full Text Available We simulated short circuit of loaded copper wire at ambient atmosphere and successfully identified various phases of the arc bead. A cuprous oxide flake was formed on the surface of the arc bead in the rapid solidification process, and there were two microstructural constituents, namely, Cu-κ eutectic structure and solutal dendrites. Due to the arc bead formed at atmosphere during the local equilibrium solidification process, the phase of arc bead has segregated to the cuprous oxide flake, Cu-κ eutectic, and Cu phase solutal dendrites, which are the fingerprints of the arc bead permeated by oxygen.

  13. Structural changes of noble metal catalysts during ignition and extinction of the partial oxidation of methane studied by advanced QEXAFS techniques

    DEFF Research Database (Denmark)

    Grunwaldt, Jan-Dierk; Beier, M.; Kimmerle, B.

    2009-01-01

    The dynamics of the ignition and extinction of the catalytic partial oxidation (CPO) of methane to hydrogen and carbon monoxide over Pt-Rh/Al2O3 and Pt/Al2O3 were studied in the subsecond timescale using quick-EXAFS with a novel cam-driven X-ray monochromator employing Si(111) and Si(311) crystals...... to discuss the potential and limitation of this technique in catalysis and related areas. With respect to the noble metal catalysed partial oxidation of methane, several interesting observations were made: structural changes during ignition were-independent of the chosen reaction conditions......-significantly faster than during the extinction of the reaction. The dynamic behavior of the catalysts was dependent on the flow conditions and the respective noble metal component(s). Higher reaction gas flow led to a faster ignition process. While the ignition over Pt-Rh/Al2O3 occurred at lower temperature than over...

  14. Partially and fully de-alloyed glassy ribbons based on Au: Application in methanol electro-oxidation studies

    Energy Technology Data Exchange (ETDEWEB)

    Paschalidou, Eirini Maria, E-mail: epaschal@unito.it [Dipartimento di Chimica e Centro Interdipartimentale NIS (Nanostructured Surfaces and Interfaces), Università di Torino, Via Pietro Giuria 7, 10125, Torino (Italy); Scaglione, Federico [Dipartimento di Chimica e Centro Interdipartimentale NIS (Nanostructured Surfaces and Interfaces), Università di Torino, Via Pietro Giuria 7, 10125, Torino (Italy); Gebert, Annett; Oswald, Steffen [Leibniz Institut für Festkörper- und Werkstoffforschung IFW, Helmholtzstraße 20, 01069, Dresden (Germany); Rizzi, Paola; Battezzati, Livio [Dipartimento di Chimica e Centro Interdipartimentale NIS (Nanostructured Surfaces and Interfaces), Università di Torino, Via Pietro Giuria 7, 10125, Torino (Italy)

    2016-05-15

    In this work, electrochemical de-alloying of an amorphous alloy, Au{sub 40}Cu{sub 28}Ag{sub 7}Pd{sub 5}Si{sub 20}, cast in ribbon form by melt spinning, has been performed, obtaining self standing nanoporous materials suitable for use as electrodes for electrocatalytic applications. The de-alloying encompasses removal of less noble elements and the crystallization of Au, resulting in interconnected ligaments whose size and morphology are described as a function of time. Depending on de-alloying time, the crystals may contain residual amounts of Cu, Ag and Pd, as shown by Auger Electron Spectroscopy (AES), Energy Dispersive Spectroscopy (EDS) and Cyclic Voltammetry (CV) in a basic solution. Current density peaks in the 0.16–0.28 V range (vs Ag/AgCl) indicate that the porous ribbons are active for the electro-oxidation of methanol. The partially de-alloyed samples, which still partially contain the amorphous phase because of the shorter etching times, have finer ligaments and display peaks at lower potential. However, the current density decreases rapidly during repeated potential scans. This is attributed to the obstruction of Au sites, mainly by the Cu oxides formed during the scans. The fully de-alloyed ribbons display current peaks at about 0.20 V and remain active for hundreds of scans at more than 60% of the initial current density. They can be fully re-activated to achieve the same performance levels after a brief immersion in nitric acid. The good activity is due to trapped Ag and Pd atoms in combination with ligament morphology. - Graphical abstract: Fine ligaments and pores made by de-alloying a glassy ribbon of a Au-based alloy, homogeneously produced across the thickness (25 μm) for studying methanol's electro-oxidation behavior. - Highlights: • Size and composition of nanoporous layers tailored in de-alloying Au-based glassy ribbons. • From amorphous precursor fine crystals occur in ligaments with residual Pd and Ag. • Fully de

  15. Thin film devices used as oxygen partial pressure sensors

    Science.gov (United States)

    Canady, K. S.; Wortman, J. J.

    1970-01-01

    Electrical conductivity of zinc oxide films to be used in an oxygen partial pressure sensor is measured as a function of temperature, oxygen partial pressure, and other atmospheric constituents. Time response following partial pressure changes is studied as a function of temperature and environmental changes.

  16. Partial oxidation of methane to methanol over catalyst ZSM-5 from coal fly ash and rice husk ash

    Directory of Open Access Journals (Sweden)

    Mirda Yanti Fusia

    2017-01-01

    Full Text Available Methane is one of the greenhouse gases that can be converted into liquid fuels such as methanol to retain most of the energy of methane and produce a cleaner environment. The conversion of methane to methanol using ZMS-5 represents a breakthrough in the utilization of methane. However, material sources for zeolite synthesis as catalyst usually are pro-analysis grade materials, which are expensive. Therefore, in this research, coal fly ash and rice husk ash were used as raw materials for mesoporous ZSM-5 zeolite synthesis. First, coal fly ash and rice husk were subjected to pre-treatment to extract silicate (SiO44− and aluminate (AlO45− and impurities separation. The ZSM-5 zeolite was synthesized through hydrothermal treatment using two types of templates. After ZSM-5 was synthesized, it was modified with Cobalt through impregnation method. The catalytic activity of both ZSM-5 and Co/ZSM-5 zeolites as heterogeneous catalysts in partial oxidation of methane were preliminary tested and compared with that commercial one. The result showed that the zeolite catalyst ZSM-5 from fly ash coal and rice husk ash has the potential to be used as catalysts in the partial oxidation of methane to methanol.

  17. Contribution to the study of the microstructure of uranium dioxide (1962); Contribution a l'etude de la microstructure du dioxyde d'uranium (1962)

    Energy Technology Data Exchange (ETDEWEB)

    Porneuf, A [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1960-05-15

    The microstructure of sintered uranium dioxide is studied in relation with several parameters, specially the sintering temperatures and atmospheres. The external surface and the internal microstructure of the sintered are examined, using fractography and ceramography. Various techniques for preparing surfaces (mechanical and electrolytic polishing) and for revealing the structure (chemical and anodic attack, ionic bombardment oxidation) have been experienced and compared. Patterns similar to those revealed in metals and probably related with interactions between dislocations and vacancies have been observed. (author) [French] La microstructure de frittes d'oxyde d'uranium est etudiee en fonction de divers parametres, en particulier de la temperature et de l'atmosphere de frittage, par examen de la surface externe des frittes, puis de leur microstructure interne (fractographie, ceramographie). Differentes techniques de preparation des surfaces (polissage mecanique ou electrolytique) et de revelation de la structure (attaque chimique ou anodique, bombardement ionique, oxydation preferentielle) ont ete experimentees et comparees. Des figures comparables a celles revelees dans les metaux et liees probablement a des interactions entre dislocations et lacunes ont ete observees. (auteur)

  18. Growth and characterization of oxide layers on zirconium alloys

    International Nuclear Information System (INIS)

    Maroto, A.J.G.; Bordoni, R.; Villegas, M.; Blesa, M.A.; Olmedo, A.M.; Iglesias, A.; Rigotti, G.

    1997-01-01

    Corrosion behaviour in aqueous media at high temperature of zirconium alloys has been extensively studied in order to elucidate the corrosion mechanism and kinetics. The characterization of the morphology and microstructure of these oxides through the different stages of oxide growth may contribute to understand their corrosion mechanism. Argentina has initiated a research program to correlate long term in and out-reactor corrosion of these alloys. This paper reports a comparative study of out of pile oxidation of Zr-2.5Nb and Zry-4, which are structural materials of in-core components of nuclear power plants. Kinetic data at different temperatures and microstructural characterization of the oxide films are presented. (author). 25 refs, 18 figs, 1 tab

  19. Growth and characterization of oxide layers on zirconium alloys

    Energy Technology Data Exchange (ETDEWEB)

    Maroto, A J.G.; Bordoni, R; Villegas, M; Blesa, M A; Olmedo, A M; Iglesias, A; Rigotti, G [Comision Nacional de Energia Atomica, Buenos Aires (Argentina)

    1997-02-01

    Corrosion behaviour in aqueous media at high temperature of zirconium alloys has been extensively studied in order to elucidate the corrosion mechanism and kinetics. The characterization of the morphology and microstructure of these oxides through the different stages of oxide growth may contribute to understand their corrosion mechanism. Argentina has initiated a research program to correlate long term in and out-reactor corrosion of these alloys. This paper reports a comparative study of out of pile oxidation of Zr-2.5Nb and Zry-4, which are structural materials of in-core components of nuclear power plants. Kinetic data at different temperatures and microstructural characterization of the oxide films are presented. (author). 25 refs, 18 figs, 1 tab.

  20. A study on crystalline phases present in the as-solidified and crystallized microstructures in Zr53Cu21Al10Ni8Ti8 alloy

    International Nuclear Information System (INIS)

    Neogy, S.; Tewari, R.; Srivastava, D.; Dey, G.K.

    2011-01-01

    In the present study the as-solidified and crystallized microstructures of Zr 53 Cu 21 Al 10 Ni 8 Ti 8 alloy have been examined in detail. Solidification was carried out by melt spinning, suction casting and copper mould casting techniques. The last technique yielded a partially crystalline microstructure, whereas, the other two techniques resulted in amorphous microstructures. (author)

  1. Study of film graphene/graphene oxide obtained by partial reduction chemical of oxide graphite; Estudo de filme de grafeno/oxido de grafeno obtido por reducao quimica parcial do oxido de grafite

    Energy Technology Data Exchange (ETDEWEB)

    Gascho, J.L.S.; Costa, S.F.; Hoepfner, J.C.; Pezzin, S.H., E-mail: juliagascho@hotmail.com [Universidade do Estado de Santa Catarina (UDESC), Joinville, SC (Brazil). Programa de Pos-Graduacao em Ciencia e Engenharia de Materiais

    2014-07-01

    This study investigated the morphology of graphene/graphene oxide film obtained by partial chemical reduction of graphite oxide (OG) as well as its resistance to solvents. Films of graphene/graphene oxide are great candidates for replacement of indium oxide doped with tin (ITO) in photoelectric devices. The OG was obtained from natural graphite, by Hummer's method modified, and its reduction is made by using sodium borohydride. Infrared spectroscopy analysis of Fourier transform (FTIR), Xray diffraction (XRD) and scanning electron microscopy, high-resolution (SEM/FEG) for the characterization of graphene/graphene oxide film obtained were performed. This film proved to be resilient, not dispersing in any of the various tested solvents (such as ethanol, acetone and THF), even under tip sonication, this resistance being an important property for the applications. Furthermore, the film had a morphology similar to that obtained by other preparation methods.(author)

  2. Composite Materials for Thermal Energy Storage: Enhancing Performance through Microstructures

    Science.gov (United States)

    Ge, Zhiwei; Ye, Feng; Ding, Yulong

    2014-01-01

    Chemical incompatibility and low thermal conductivity issues of molten-salt-based thermal energy storage materials can be addressed by using microstructured composites. Using a eutectic mixture of lithium and sodium carbonates as molten salt, magnesium oxide as supporting material, and graphite as thermal conductivity enhancer, the microstructural development, chemical compatibility, thermal stability, thermal conductivity, and thermal energy storage performance of composite materials are investigated. The ceramic supporting material is essential for preventing salt leakage and hence provides a solution to the chemical incompatibility issue. The use of graphite gives a significant enhancement on the thermal conductivity of the composite. Analyses suggest that the experimentally observed microstructural development of the composite is associated with the wettability of the salt on the ceramic substrate and that on the thermal conduction enhancer. PMID:24591286

  3. Microstructural degradation of Ni-YSZ anodes for solid oxide fuel cells

    DEFF Research Database (Denmark)

    Thydén, Karl Tor Sune

    2008-01-01

    -reforming catalysis. In the context of electrochemically tested and technologically relevant cells, the majority of the microstructural work is performed on a cell tested at 850°C under relatively severe conditions for 17,500 hours. It is demonstrated that the major Ni rearrangements take place at the interface...... are of technological relevance, it is difficult to identify the effect from isolated parameters such as temperature, fuel gas composition and polarization. Model studies of high temperature aged Ni-YSZ cermets are generally performed in atmospheres containing relatively low concentrations of H2O. In this work......, the microstructural degradation in both electrochemically longterm tested cells and high-temperature aged model materials are studied. Since Ni particle sintering / coarsening is attributed to be the major cause of anode degradation, this subject attains the primary focus. A large part of the work is focused...

  4. Methane partial oxidation over a LaCr0.85Ru0.15O3 catalyst : Characterization, activity tests and kinetic modeling

    NARCIS (Netherlands)

    Melchiori, T.; Di Felice, L.; Mota, N.; Navarro, R.M.; Fierro, J.L.G.; Sint Annaland, van M.; Gallucci, F.

    2014-01-01

    A new LaCr0.85Ru0.15O3 perovskite-type catalyst for CH4 partial oxidation with a high activity and selectivity for syngas with good thermal stability and resistance against coking has been developed. In this paper, the catalyst preparation method, catalyst characterization, results of catalytic

  5. Microstructural evolution during DPRM process of semisolid ledeburitic D2 tool steel.

    Science.gov (United States)

    Mohammed, M N; Omar, M Z; Syarif, J; Sajuri, Z; Salleh, M S; Alhawari, K S

    2013-01-01

    Semisolid metal processing is a relatively new technology that offers several advantages over liquid processing and solid processing because of the unique behaviour and characteristic microstructure of metals in this state. With the aim of finding a minimum process chain for the manufacture of high-quality production at minimal cost for forming, the microstructural evolution of the ledeburitic AISI D2 tool steel in the semisolid state was studied experimentally. The potential of the direct partial remelting (DPRM) process for the production of AISI D2 with a uniform globular microstructure was revealed. The liquid fraction was determined using differential scanning calorimetry. The microstructures of the samples were investigated using an optical microscope and a scanning electron microscope equipped with an energy dispersive spectroscopy analyser, while X-ray phase analysis was performed to identify the phase evolution and the type of carbides. Mechanical characterisation was completed by hardness measurements. The typical microstructure after DPRM consists of metastable austenite which was located particularly in the globular grains (average grain size about 50 μ m), while the remaining interspaces were filled by precipitated eutectic carbides on the grain boundaries and lamellar network.

  6. Microstructural Evolution during DPRM Process of Semisolid Ledeburitic D2 Tool Steel

    Directory of Open Access Journals (Sweden)

    M. N. Mohammed

    2013-01-01

    Full Text Available Semisolid metal processing is a relatively new technology that offers several advantages over liquid processing and solid processing because of the unique behaviour and characteristic microstructure of metals in this state. With the aim of finding a minimum process chain for the manufacture of high-quality production at minimal cost for forming, the microstructural evolution of the ledeburitic AISI D2 tool steel in the semisolid state was studied experimentally. The potential of the direct partial remelting (DPRM process for the production of AISI D2 with a uniform globular microstructure was revealed. The liquid fraction was determined using differential scanning calorimetry. The microstructures of the samples were investigated using an optical microscope and a scanning electron microscope equipped with an energy dispersive spectroscopy analyser, while X-ray phase analysis was performed to identify the phase evolution and the type of carbides. Mechanical characterisation was completed by hardness measurements. The typical microstructure after DPRM consists of metastable austenite which was located particularly in the globular grains (average grain size about 50 μm, while the remaining interspaces were filled by precipitated eutectic carbides on the grain boundaries and lamellar network.

  7. Microstructural Evolution during DPRM Process of Semisolid Ledeburitic D2 Tool Steel

    Science.gov (United States)

    Mohammed, M. N.; Omar, M. Z.; Syarif, J.; Sajuri, Z.; Salleh, M. S.; Alhawari, K. S.

    2013-01-01

    Semisolid metal processing is a relatively new technology that offers several advantages over liquid processing and solid processing because of the unique behaviour and characteristic microstructure of metals in this state. With the aim of finding a minimum process chain for the manufacture of high-quality production at minimal cost for forming, the microstructural evolution of the ledeburitic AISI D2 tool steel in the semisolid state was studied experimentally. The potential of the direct partial remelting (DPRM) process for the production of AISI D2 with a uniform globular microstructure was revealed. The liquid fraction was determined using differential scanning calorimetry. The microstructures of the samples were investigated using an optical microscope and a scanning electron microscope equipped with an energy dispersive spectroscopy analyser, while X-ray phase analysis was performed to identify the phase evolution and the type of carbides. Mechanical characterisation was completed by hardness measurements. The typical microstructure after DPRM consists of metastable austenite which was located particularly in the globular grains (average grain size about 50 μm), while the remaining interspaces were filled by precipitated eutectic carbides on the grain boundaries and lamellar network. PMID:24223510

  8. Phase transformations and resulting microstructures in Ti - 47 Al -2 Cr alloy

    International Nuclear Information System (INIS)

    Ghasemi-Armaki, H.; Heshmati-Manesh, S.; Jafarian, H. R.; Nili-Ahmadabadi, M.

    2008-01-01

    During the last three decades, intermetallic alloys have focused attention because of their high strength to weight ratio and good creep resistance. Titanium aluminide alloys based on γ-Ti Al are potential candidates to replace Ni-based super alloys currently used in jet engine components at high temperatures because of their low density, high melting temperature, good elevated-temperature strength and modulus retention, high resistance to oxidation and hydrogen absorption, and excellent creep properties. One of the major concerns in these alloys is their poor ductility at room and intermediate temperatures which has been improved slightly by microstructure modifications through heat treatment. Thus, modification of microstructure during cooling and CCT diagram in these alloys is of vital importance. In this study, Ti - 47 Al - 2 Cr intermetallic alloy has been prepared by remelting 4 times with a vacuum arc remelting furnace. Homogenizing treatment was done at 1125 d eg C for 72 h in a sealed vacuum quartz tube. All heat treatments on the samples were carried out in a vacuum heat treatment furnace under a pressure of 10 -1 bar. The atmosphere inside the furnace was changed to that of high purity argon for each heat treatment as an added precaution against oxidation. In this paper, phase transformations in a γ-Ti Al based intermetallic alloy containing chromium were investigated. Heat treatments on samples of this alloy at temperatures above Tα and subsequent cooling with various cooling rates resulted in variety of microstructures. The schematic CCT diagram for this alloy was drawn from microstructural studies using microscopy routs and X-ray diffraction. Then, cyclic heat treatment with grain refining purpose was conducted on a sample of this alloy having massive gamma microstructure. During cyclic heat treatment, gradual dissociation of the gamma phase resulted in the formation of a Widmanstaetten type structure. Trend of microstructure evolution and

  9. The variation of cationic microstructure in Mn-doped spinel ferrite during calcination and its effect on formaldehyde catalytic oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Liang, Xiaoliang [CAS Key Laboratory of Mineralogy and Metallogeny, Guangzhou Institute of Geochemistry, Chinese Academy of Sciences, Guangzhou 510640 (China); Guangdong Provincial Key Laboratory of Mineral Physics and Materials, Guangzhou 510640 (China); Liu, Peng [CAS Key Laboratory of Mineralogy and Metallogeny, Guangzhou Institute of Geochemistry, Chinese Academy of Sciences, Guangzhou 510640 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Guangdong Provincial Key Laboratory of Mineral Physics and Materials, Guangzhou 510640 (China); He, Hongping, E-mail: hehp@gig.ac.cn [CAS Key Laboratory of Mineralogy and Metallogeny, Guangzhou Institute of Geochemistry, Chinese Academy of Sciences, Guangzhou 510640 (China); Guangdong Provincial Key Laboratory of Mineral Physics and Materials, Guangzhou 510640 (China); Wei, Gaoling [Guangdong Institute of Eco-Environmental and Soil Sciences, Guangzhou 510650 (China); Chen, Tianhu [School of Resources and Environmental Engineering, Hefei University of Technology, Hefei 230009 (China); Tan, Wei; Tan, Fuding [CAS Key Laboratory of Mineralogy and Metallogeny, Guangzhou Institute of Geochemistry, Chinese Academy of Sciences, Guangzhou 510640 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Guangdong Provincial Key Laboratory of Mineral Physics and Materials, Guangzhou 510640 (China); Zhu, Jianxi; Zhu, Runliang [CAS Key Laboratory of Mineralogy and Metallogeny, Guangzhou Institute of Geochemistry, Chinese Academy of Sciences, Guangzhou 510640 (China); Guangdong Provincial Key Laboratory of Mineral Physics and Materials, Guangzhou 510640 (China)

    2016-04-05

    Highlights: • Calcination causes the activity variation of Mn-doped ferrites for HCHO oxidation. • The variation of catalytic activity of ferrites by calcination is non-linear. • Mn enriches on the calcinated ferrite surface in the valence of +3 and +4. • The reduction temperature of surface Mn{sup 4+} species is well correlated to T50. - Abstract: In this study, a series of Mn substituted spinel ferrites calcinated at different temperatures were used as catalysts for the oxidation of formaldehyde (HCHO). X-ray diffraction, Raman spectroscopy, X-ray photoelectron spectroscopy and H{sub 2} temperature-programmed reduction were conducted to characterize the structure and physico-chemical properties of catalysts, which were affected by calcination in the range of 200–600 °C. Results show that all the ferrites were with spinel structure, and those calcinated in the range of 300–600 °C were in the phase of maghemite. The calcination changed the valence and distribution of Mn and Fe on the ferrite surface, and accordingly the reducibility of ferrites. The HCHO catalytic oxidation test showed that with the increase of calcination temperature, the activity was initially improved until 400 °C, but then decreased. The variation of HCHO conversion performance was well positively correlated to the variation of reduction temperature of surface Mn{sup 4+} species. The remarkable effect of calcination on the catalytic activity of Mn-doped spinel ferrites for HCHO oxidation was discussed in view of reaction mechanism and variations in cationic microstructure of Mn-doped ferrites.

  10. The variation of cationic microstructure in Mn-doped spinel ferrite during calcination and its effect on formaldehyde catalytic oxidation

    International Nuclear Information System (INIS)

    Liang, Xiaoliang; Liu, Peng; He, Hongping; Wei, Gaoling; Chen, Tianhu; Tan, Wei; Tan, Fuding; Zhu, Jianxi; Zhu, Runliang

    2016-01-01

    Highlights: • Calcination causes the activity variation of Mn-doped ferrites for HCHO oxidation. • The variation of catalytic activity of ferrites by calcination is non-linear. • Mn enriches on the calcinated ferrite surface in the valence of +3 and +4. • The reduction temperature of surface Mn"4"+ species is well correlated to T50. - Abstract: In this study, a series of Mn substituted spinel ferrites calcinated at different temperatures were used as catalysts for the oxidation of formaldehyde (HCHO). X-ray diffraction, Raman spectroscopy, X-ray photoelectron spectroscopy and H_2 temperature-programmed reduction were conducted to characterize the structure and physico-chemical properties of catalysts, which were affected by calcination in the range of 200–600 °C. Results show that all the ferrites were with spinel structure, and those calcinated in the range of 300–600 °C were in the phase of maghemite. The calcination changed the valence and distribution of Mn and Fe on the ferrite surface, and accordingly the reducibility of ferrites. The HCHO catalytic oxidation test showed that with the increase of calcination temperature, the activity was initially improved until 400 °C, but then decreased. The variation of HCHO conversion performance was well positively correlated to the variation of reduction temperature of surface Mn"4"+ species. The remarkable effect of calcination on the catalytic activity of Mn-doped spinel ferrites for HCHO oxidation was discussed in view of reaction mechanism and variations in cationic microstructure of Mn-doped ferrites.

  11. Microstructural and electrical characteristics of rare earth oxides doped ZnO varistor films

    Science.gov (United States)

    Jiao, Lei; Mei, Yunzhu; Xu, Dong; Zhong, Sujuan; Ma, Jia; Zhang, Lei; Bao, Li

    2018-02-01

    ZnO-Bi2O3 varistor films doped with two kinds of rare earth element oxides (Lu2O3 and Yb2O3) were prepared by the sol-gel method. The effects of Lu2O3/Yb2O3 doping on the microstructure and electrical characteristics of ZnO-Bi2O3 varistor films were investigated. All samples show a homogenized morphology and an improved nonlinear relationship between the electric field (E) and current density (I). Both Yb2O3 and Lu2O3 doping can decrease the grain size of ZnO-Bi2O3 varistor films and improve the electrical properties, which have a positive effect on the development of ZnO varistor ceramics. Yb2O3 doping significantly increases the dielectric constant at low frequency. 0.2 mol. % Yb2O3 doped ZnO-Bi2O3 varistor films exhibit the highest nonlinear coefficient (2.5) and the lowest leakage current (328 μA) among Lu2O3/Yb2O3 doped ZnO-Bi2O3 varistor films. Similarly, 0.1 mol. % Lu2O3 doping increases the nonlinear coefficient to 1.9 and decrease the leakage current to 462 μA.

  12. Microstructural modelling of nuclear graphite using multi-phase models

    International Nuclear Information System (INIS)

    Berre, C.; Fok, S.L.; Marsden, B.J.; Mummery, P.M.; Marrow, T.J.; Neighbour, G.B.

    2008-01-01

    This paper presents a new modelling technique using three-dimensional multi-phase finite element models in which meshes representing the microstructure of thermally oxidised nuclear graphite were generated from X-ray micro-tomography images. The density of the material was related to the image greyscale using Beer-Lambert's law, and multiple phases could thus be defined. The local elastic and non-linear properties of each phase were defined as a function of density and changes in Young's modulus, tensile and compressive strength with thermal oxidation were calculated. Numerical predictions compared well with experimental data and with other numerical results obtained using two-phase models. These models were found to be more representative of the actual microstructure of the scanned material than two-phase models and, possibly because of pore closure occurring during compression, compressive tests were also predicted to be less sensitive to the microstructure geometry than tensile tests

  13. Oxygen binding to partially nitrosylated hemoglobin.

    Science.gov (United States)

    Fago, Angela; Crumbliss, Alvin L; Hendrich, Michael P; Pearce, Linda L; Peterson, Jim; Henkens, Robert; Bonaventura, Celia

    2013-09-01

    Reactions of nitric oxide (NO) with hemoglobin (Hb) are important elements in protection against nitrosative damage. NO in the vasculature is depleted by the oxidative reaction with oxy Hb or by binding to deoxy Hb to generate partially nitrosylated Hb (Hb-NO). Many aspects of the formation and persistence of Hb-NO are yet to be clarified. In this study, we used a combination of EPR and visible absorption spectroscopy to investigate the interactions of partially nitrosylated Hb with O2. Partially nitrosylated Hb samples had predominantly hexacoordinate NO-heme geometry and resisted oxidation when exposed to O2 in the absence of anionic allosteric effectors. Faster oxidation occurred in the presence of 2,3-diphosphoglycerate (DPG) or inositol hexaphosphate (IHP), where the NO-heme derivatives had higher levels of pentacoordinate heme geometry. The anion-dependence of the NO-heme geometry also affected O2 binding equilibria. O2-binding curves of partially nitrosylated Hb in the absence of anions were left-shifted at low saturations, indicating destabilization of the low O2 affinity T-state of the Hb by increasing percentages of NO-heme, much as occurs with increasing levels of CO-heme. Samples containing IHP showed small decreases in O2 affinity, indicating shifts toward the low-affinity T-state and formation of inert α-NO/β-met tetramers. Most remarkably, O2-equilibria in the presence of the physiological effector DPG were essentially unchanged by up to 30% NO-heme in the samples. As will be discussed, under physiological conditions the interactions of Hb with NO provide protection against nitrosative damage without impairing O2 transport by Hb's unoccupied heme sites. This article is part of a Special Issue entitled: Oxygen Binding and Sensing Proteins. Copyright © 2013 Elsevier B.V. All rights reserved.

  14. Influence of microstructural change of the interface between Nd2Fe14B and Nd-O phases on coercivity of Nd-Fe-B films by oxidation and subsequent low-temperature annealing

    International Nuclear Information System (INIS)

    Matsuura, Masashi; Tezuka, Nobuki; Sugimoto, Satoshi; Goto, Ryota

    2011-01-01

    This study provides the influence of microstructural change of the interface between Nd 2 Fe 14 B and Nd-O phases on coercivity of Nd-Fe-B thin films during annealing at low temperature (∼350 deg. C). All films were prepared by using ultra high vacuum (UHV) magnetron sputtering, and the Nd-Fe-B layer was oxidized under Ar gas atmosphere (O 2 content; ∼2 Vol.ppm). Then, the films were annealed at 250-350 deg. C under UHV condition. After oxidation, the coercivity of Nd-Fe-B film decreased to around 40% of the coercivity of as-deposited Nd-Fe-B film. The Nd-rich phase changed from α-Nd to amorphous Nd(-O), and the interface of Nd 2 Fe 14 B/Nd(-O) became rough. In the Nd-Fe-B films oxidized and subsequent annealed at 350 deg. C, the coercivity decreased to around 20%. In the films, poly crystalline hcp Nd 2 O 3 phase crystallized in Nd-rich phase, and there were some steps at the surface of Nd 2 Fe 14 B phase contacting with hcp Nd 2 O 3 phase. Regardless of crystal orientation of Nd 2 Fe 14 B, the microstructural changes of the interface described above were observed.

  15. Hybrid Nitrous Oxide Production from a Partial Nitrifying Bioreactor: Hydroxylamine Interactions with Nitrite.

    Science.gov (United States)

    Terada, Akihiko; Sugawara, Sho; Hojo, Keisuke; Takeuchi, Yuki; Riya, Shohei; Harper, Willie F; Yamamoto, Tomoko; Kuroiwa, Megumi; Isobe, Kazuo; Katsuyama, Chie; Suwa, Yuichi; Koba, Keisuke; Hosomi, Masaaki

    2017-03-07

    The goal of this study was to elucidate the mechanisms of nitrous oxide (N 2 O) production from a bioreactor for partial nitrification (PN). Ammonia-oxidizing bacteria (AOB) enriched from a sequencing batch reactor (SBR) were subjected to N 2 O production pathway tests. The N 2 O pathway test was initiated by supplying an inorganic medium to ensure an initial NH 4 + -N concentration of 160 mg-N/L, followed by 15 NO 2 - (20 mg-N/L) and dual 15 NH 2 OH (each 17 mg-N/L) spikings to quantify isotopologs of gaseous N 2 O ( 44 N 2 O, 45 N 2 O, and 46 N 2 O). N 2 O production was boosted by 15 NH 2 OH spiking, causing exponential increases in mRNA transcription levels of AOB functional genes encoding hydroxylamine oxidoreductase (haoA), nitrite reductase (nirK), and nitric oxide reductase (norB) genes. Predominant production of 45 N 2 O among N 2 O isotopologs (46% of total produced N 2 O) indicated that coupling of 15 NH 2 OH with 14 NO 2 - produced N 2 O via N-nitrosation hybrid reaction as a predominant pathway. Abiotic hybrid N 2 O production was also observed in the absence of the AOB-enriched biomass, indicating multiple pathways for N 2 O production in a PN bioreactor. The additional N 2 O pathway test, where 15 NH 4 + was spiked into 400 mg-N/L of NO 2 - concentration, confirmed that the hybrid N 2 O production was a dominant pathway, accounting for approximately 51% of the total N 2 O production.

  16. Effects of impurity elements on mechanical properties and microstructures of reduced-activation ferritic/martensitic steels

    Energy Technology Data Exchange (ETDEWEB)

    Sawahata, A. [Ibaraki Univ., Graduate School of Science and Engineering, Hitachi (Japan); Tanigawa, H.; Shiba, K. [Japan Atomic Energy Agency, Naga-gun, Ibaraki-ken (Japan); Enomoto, M. [Ibaraki Univ., Dept. of Materials Science, Faculty of Engineering, Hitachi (Japan)

    2007-07-01

    Full text of publication follows: Reduced activation ferritic/martensitic steels (RAFs), such as F82H (Fe-8Cr-2W-0.2V- 0.04Ta-0.1C, in wt%), are one of the leading candidates for structural materials of fusion reactors. Impact property of F82H can be improved by adjusting the amount of tantalum or titanium concentration. On the other hand, it was reported by microstructure analyses of IEA steel that tantalum has a tendency to form oxides and causes a large dispersion of fracture toughness. In this study, the correlation between titanium or tantalum concentration and the impact property were reported focusing on difference in microstructure. Charpy impact test and microstructure analyses were carried out against modified F82H series of which titanium, nitrogen and tantalum composition were controlled. Charpy impact test results showed that the ductile-brittle transition temperature (DBTT) of T05A (0.05Ta- 0.0014N-oxides at the fracture initiation point, although simple TaO oxides and composite Al{sub 2}O{sub 3}-Ta(V,Ti)O oxides were observed in both steels. The size distribution analyses of oxides indicate that the number density of composite oxides in T05B was higher than in T05A. In addition, EDX analyses showed that composite oxides in T05B had a strong peak of titanium, but the peak were not detected in the oxides in T05A. These results suggest that titanium has a significant influence on the formation of oxides, and affects the impact property. The influence of tantalum concentration on the formation of these oxides and mechanical properties will be reported. (authors)

  17. Phase transformations in nickel sulphide: Microstructures and mechanisms

    International Nuclear Information System (INIS)

    Yousfi, Oussama; Donnadieu, Patricia; Brechet, Yves; Robaut, Florence; Charlot, Frederic; Kasper, Andreas; Serruys, Francis

    2010-01-01

    Nickel sulphide inclusions are known to be responsible for delayed fracture in tempered glasses due to phase transformation within the inclusion. Microstructural identification of the phase transformation mechanisms in the Ni-S system close to the NiS composition were carried out on a series of partially transformed states. Observations allow to investigate the morphological evolution during transformation, the phase orientation relationships and the first stages of the transformation were investigated by optical microscopy, electron backscatter diffraction, and scanning and transmission electron microscopy. The transformation mechanisms change significantly with the change in sulphur content of the α-NiS phase. Massive transformation is observed for near-stoichiometric composition. For overstoichiometric composition, the transformation is controlled by a long-range diffusion mechanism. The influence of stoichiometry and impurities (Fe) on the microstructural evolution and transformation mechanisms has also been studied.

  18. Axial Changes of Catalyst Structure and Temperature in a Fixed-Bed Microreactor During Noble Metal Catalysed Partial Oxidation of Methane

    DEFF Research Database (Denmark)

    Hannemann, S.; Grunwaldt, Jan-Dierk; Kimmerle, B.

    2009-01-01

    The catalytic partial oxidation of methane (CPO) over flame-made 2.5%Rh-2.5%Pt/Al2O3 and 2.5%Rh/Al2O3 in 6%CH4/3%O-2/He shows the potential of in situ studies using miniaturized fixed-bed reactors, the importance of spatially resolved studies and its combination with infrared thermography and on-...

  19. Microstructural evolution and thixoformability of semi-solid aluminum 319s alloy during re-melting

    International Nuclear Information System (INIS)

    Hu, X.G.; Zhu, Q.; Lu, H.X.; Zhang, F.; Li, D.Q.; Midson, S.P.

    2015-01-01

    The aim of this paper is to characterize both microstructural evolution and thixoformability during partial melting of semi-solid 319s alloy. The thixoformability criteria of 319s was initially investigated by thermodynamic analysis. In-situ observation of partial re-melting was performed by a Confocal Laser Scanning Microscope to determine the effect of heating rate on melting characteristics. Meanwhile, the microstructural evolution of 319s alloy at extremely low heating rate was also investigated in order to understand the mechanism of re-melting process. The studies demonstrated that 319s alloy is suitable for thixocasting because of the controllable liquid fraction in the operating window of 15 °C. The process window was effected by both temperature and heating time. The primary particles evolution in 319s alloy can be divided into four stages, and the coarsening rate during isothermal test is 227 μm 3 /s. The effective method to obtain desirable microstructure is to manage the time in the semi-solid state by controlling heating rate and soaking time. - Highlights: • The thixoformability of 319s is discussed by using SPSC and thermodynamic analysis. • The re-melting processes at different heating rate are in-situ observed. • We identified the four stages of microstructural evolution during re-melting. • The coarsening rate K for 319s during isothermal test is identified. • The variation tendency of Si particle size with increasing time is reported

  20. Mixed conducting materials for partial oxidation of hydrocarbons

    Directory of Open Access Journals (Sweden)

    Frade, J. R.

    2004-06-01

    Full Text Available Thermodynamic calculations with additional conditions for the conservation of carbon and hydrogen were used to predict the gas composition obtained by partial oxidation of methane as a function of oxygen partial pressure and temperature; this was used to assess the stability and oxygen permeability requirements of mixed conducting membrane materials proposed for this purpose. A re-examination of known mixed conductors shows that most materials with highest permeability still fail to fulfil the requirements of stability under reducing conditions. Other materials possess sufficient stability but their oxygen permeability is insufficient. Different approaches were thus used to attempt to overcome those limitations, including changes in composition in the A and B site positions of ABO3 perovskites, and tests of materials with different structure types. Promising results were obtained mainly for some materials with perovskite or related K2NiF4-type structures. Limited stability of the most promising materials shows that one should rely mainly on kinetic limitations in the permeate side to protect the mixed conductor from severe reducing conditions.

    Se han usado cálculos termodinámicos con condiciones adicionales para la conservación del carbono e hidrógeno para predecir la composición del gas obtenido mediante la oxidación parcial del metano en función de la presión parcial de oxígeno y de la temperatura; esto se ha usado para asegurar los requerimientos de estabilidad y permeabilidad al oxígeno de los materiales conductores mixtos empleados como membrana para este propósito. Un nuevo exámen de los conductores mixtos conocidos muestra que la mayoría de los materiales con la mayor permeabilidad todavía fallan en el cumplimiento de los requerimientos de estabilidad bajo condiciones reductoras. Otros materiales poseen suficiente estabilidad, pero su permeabilidad al oxígeno es insuficiente. Por ello se han empleado diferentes

  1. Investigation of microstructure changes in ODS-EUROFER after hydrogen loading

    International Nuclear Information System (INIS)

    Emelyanova, O.V.; Ganchenkova, M.G.; Malitskii, E.; Yagodzinskyy, Y.N.; Klimenkov, M.; Borodin, V.A.; Vladimirov, P.V.; Lindau, R.; Möslang, A.; Hänninen, H.

    2016-01-01

    The effect of hydrogen on the microstructure of mechanically tested ODS-EUROFER steel was investigated by means of transmission electron microscopy, thermal desorption spectroscopy, and atomistic simulations. The presence of yttrium oxide particles notably increases hydrogen uptake in ODS-EUROFER steel as compared to ODS-free EUROFER 97. Under tensile loading, hydrogen accumulation promotes the loss of cohesion at the oxide particle interfaces. First-principles molecular dynamics simulations indicate that hydrogen can be trapped at nanoparticle/matrix interface, creating OH-groups. The accumulation of hydrogen atoms at the oxide particle surface can be the reason for the observed hydrogen-induced oxide/matrix interface weakening and de-cohesion under the action of external tensile stress.

  2. Sintering, microstructure and properties of WC-AISI304 powder composites

    International Nuclear Information System (INIS)

    Marques, B.J.; Fernandes, C.M.; Senos, A.M.R.

    2013-01-01

    Highlights: ► Total replacement of Co binder by stainless steel AISI 304 in WC based composites. ► Processing conditions for WC–stainless steel composites. ► Mechanical behavior and oxidation resistance of WC–stainless steel composites. -- Abstract: Tungsten carbide–stainless steel (AISI 304) based composites were successfully prepared by powder metallurgy routes using vacuum sintering at a maximum temperature of 1500 °C. The effects of the binder amount (between 6 and 15 wt.%) on the phase composition, microstructure and mechanical properties, namely hardness and fracture toughness, were investigated. Appreciable amount of (M,W) 6 C up to 12 wt.% was detected, especially for the higher SS contents. However, a good compromise between toughness and hardness was observed. Besides that, improved oxidation resistance was noticed in WC–SS based composites compared with WC–Co composites. The results are discussed having in mind the correlation between chemical composition, phase composition, microstructure and mechanical behavior

  3. Processing, microstructure, and electric properties of buried resistors in low-temperature co-fired ceramics

    International Nuclear Information System (INIS)

    Yang, Pin; Rodriguez, Mark A.; Kotula, Paul; Miera, Brandon K.; Dimos, Duane

    2001-01-01

    The electrical properties of ruthenium oxide based devitrifiable resistors embedded within low-temperature co-fired ceramics were investigated from -100 o C to 100 o C. Special attention was given to the processing conditions and their effects on resistance and temperature coefficient of resistance (TCR). Results indicate that within this temperature range the conductance for these buried resistors is limited by tunneling of charge carriers through the thin glass layer between ruthenium oxide particles. A modified version of the tunneling barrier model is proposed to account for the microstructure ripening observed during thermal processing. The model parameters determined from curve fitting show that charging energy (i.e., the energy required for a charge carrier to tunnel through the glass barrier) is strongly dependent on particle size and particle--particle separation between ruthenium oxide grains. Initial coarsening of ruthenium oxide grains was found to reduce the charging energy and lower the resistance. However, when extended ripening occurs, the increase in particle--particle separation increases the charging energy, reduces the tunneling probability and gives rise to a higher resistance. The tradeoff between these two effects results in an optimum microstructure with a minimum resistance and TCR. Furthermore, the TCR of these buried resistors has been shown to be governed by the magnitude of the charging energy. Model parameters determined by our analysis appear to provide quantitative physical interpretations to the microstructural changes in the resistor, which in turn, are controlled by the processing conditions

  4. Composite materials for thermal energy storage: enhancing performance through microstructures.

    Science.gov (United States)

    Ge, Zhiwei; Ye, Feng; Ding, Yulong

    2014-05-01

    Chemical incompatibility and low thermal conductivity issues of molten-salt-based thermal energy storage materials can be addressed by using microstructured composites. Using a eutectic mixture of lithium and sodium carbonates as molten salt, magnesium oxide as supporting material, and graphite as thermal conductivity enhancer, the microstructural development, chemical compatibility, thermal stability, thermal conductivity, and thermal energy storage performance of composite materials are investigated. The ceramic supporting material is essential for preventing salt leakage and hence provides a solution to the chemical incompatibility issue. The use of graphite gives a significant enhancement on the thermal conductivity of the composite. Analyses suggest that the experimentally observed microstructural development of the composite is associated with the wettability of the salt on the ceramic substrate and that on the thermal conduction enhancer. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  5. Oxidation of PCEA nuclear graphite by low water concentrations in helium

    Energy Technology Data Exchange (ETDEWEB)

    Contescu, Cristian I., E-mail: ContescuCI@ornl.gov [Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831-6087 (United States); Mee, Robert W. [Department of Business Analytics and Statistics, University of Tennessee, Knoxville, TN 37996-0525 (United States); Wang, Peng [Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831-6087 (United States); Romanova, Anna V.; Burchell, Timothy D. [Department of Business Analytics and Statistics, University of Tennessee, Knoxville, TN 37996-0525 (United States)

    2014-10-15

    Accelerated oxidation tests were performed to determine kinetic parameters of the chronic oxidation reaction (i.e. slow, continuous, and persistent) of PCEA graphite in contact with helium coolant containing low moisture concentrations in high temperature gas-cooled reactors. To the authors’ knowledge such a study has not been done since the detailed analysis of reaction of H-451 graphite with steam (Velasquez, Hightower, Burnette, 1978). Since that H-451 graphite is now unavailable, it is urgently needed to characterize chronic oxidation behavior of new graphite grades that are being considered for use in gas-cooled reactors. The Langmuir–Hinshelwood mechanism of carbon oxidation by water results in a non-linear reaction rate expression, with at least six different parameters. They were determined in accelerated oxidation experiments that covered a large range of temperatures (800–1100 °C), and partial pressures of water (15–850 Pa) and hydrogen (30–150 Pa) and used graphite specimens thin enough (4 mm) in order to avoid diffusion effects. Data analysis employed a statistical method based on multiple likelihood estimation of parameters and simultaneous fitting of non-linear equations. The results show significant material-specific differences between graphite grades PCEA and H-451 which were attributed to microstructural dissimilarity between the two materials. It is concluded that kinetic data cannot be transferred from one graphite grade to another.

  6. The Relationship Between Structural and Catalytic Activity of α and γ-Bismuth-Molybdate Catalysts for Partial Oxidation of Propylene to Acrolein

    Science.gov (United States)

    Fansuri, H.; Pham, G. H.; Wibawanta, S.; Zhang, D. K.; French, David

    Bismuth-molybdate catalysts are known to be effective for catalytic partial oxidation of propylene to acrolein. Their properties and the kinetics and reaction mechanisms for acrolein production have been extensively studied, especially in their basic forms, such as α, β, and γ-bismuth-molybdate. Although the reaction mechanisms have been reported widely in the literature, a general agreement has not been reached, especially from a catalyst-structure point of view. The present contribution reports an effort to understand the structural changes of α and γ-bismuth-molybdate catalysts at varying temperatures as examined using high temperature XRD and to relate the catalyst performance (activity and selectivity) for propylene partial oxidation to acrolein. The XRD analysis was performed at temperature between 250 and 450°C in ambient atmosphere and the Rietveld refinement method was used to extract unit cell parameters. The results showed a distinct similarity between the shapes of the thermal expansion of the catalysts and their activity and selectivity curves, indicating a significant role that the catalyst interatomic structure plays in the overall reaction mechanism.

  7. Microstructure and tensile properties of oxide dispersion strengthened Fe–14Cr–0.3Y2O3 and Fe–14Cr–2W–0.3Ti–0.3Y2O3

    International Nuclear Information System (INIS)

    Auger, M.A.; Castro, V. de; Leguey, T.; Monge, M.A.; Muñoz, A.; Pareja, R.

    2013-01-01

    Two ODS ferritic steels with nominal compositions (wt.%): Fe–14Cr–0.3Y 2 O 3 and Fe–14Cr–2W–0.3Ti–0.3Y 2 O 3 have been produced by mechanical alloying and consolidation by hot isostatic pressing. The microstructure and tensile properties of these materials after being forged and heat-treated at 1123 K have been investigated to clarify the interrelation between composition, microstructure and mechanical properties. The second-phase precipitates in these alloys have been analyzed by high-angle annular dark-field imaging in scanning TEM mode and electron diffraction. Fe–14Cr–2W–0.3Ti–0.3Y 2 O 3 exhibits a duplex microstructure consisting of large recrystallized grains, as large as 1.5 μm, and unrecovered regions containing submicron equiaxed grains. In addition, three types of secondary phase particles have been found: large M 23 C 6 particles containing W and Cr, (Cr + Ti) rich spherical particles with diameters between 50 and 500 nm, and fine (Y + Ti) oxide particles with sizes below 30 nm. In contrast, Fe14CrY shows a uniform structure of equiaxed grains, with sizes in the range 0.5–3 μm, containing a fine dispersion of Y oxide particles ( 2 O 3 at temperatures up to 773 K, but the opposite appears to occur beyond this temperature

  8. Prediction of Thermal Transport Properties of Materials with Microstructural Complexity

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Youping

    2017-10-10

    This project aims at overcoming the major obstacle standing in the way of progress in dynamic multiscale simulation, which is the lack of a concurrent atomistic-continuum method that allows phonons, heat and defects to pass through the atomistic-continuum interface. The research has led to the development of a concurrent atomistic-continuum (CAC) methodology for multiscale simulations of materials microstructural, mechanical and thermal transport behavior. Its efficacy has been tested and demonstrated through simulations of dislocation dynamics and phonon transport coupled with microstructural evolution in a variety of materials and through providing visual evidences of the nature of phonon transport, such as showing the propagation of heat pulses in single and polycrystalline solids is partially ballistic and partially diffusive. In addition to providing understanding on phonon scattering with phase interface and with grain boundaries, the research has contributed a multiscale simulation tool for understanding of the behavior of complex materials and has demonstrated the capability of the tool in simulating the dynamic, in situ experimental studies of nonequilibrium transient transport processes in material samples that are at length scales typically inaccessible by atomistically resolved methods.

  9. Experimental test of the viscous anisotropy hypothesis for partially molten rocks.

    Science.gov (United States)

    Qi, Chao; Kohlstedt, David L; Katz, Richard F; Takei, Yasuko

    2015-10-13

    Chemical differentiation of rocky planets occurs by melt segregation away from the region of melting. The mechanics of this process, however, are complex and incompletely understood. In partially molten rocks undergoing shear deformation, melt pockets between grains align coherently in the stress field; it has been hypothesized that this anisotropy in microstructure creates an anisotropy in the viscosity of the aggregate. With the inclusion of anisotropic viscosity, continuum, two-phase-flow models reproduce the emergence and angle of melt-enriched bands that form in laboratory experiments. In the same theoretical context, these models also predict sample-scale melt migration due to a gradient in shear stress. Under torsional deformation, melt is expected to segregate radially inward. Here we present torsional deformation experiments on partially molten rocks that test this prediction. Microstructural analyses of the distribution of melt and solid reveal a radial gradient in melt fraction, with more melt toward the center of the cylinder. The extent of this radial melt segregation grows with progressive strain, consistent with theory. The agreement between theoretical prediction and experimental observation provides a validation of this theory.

  10. The influence of surface morphology and oxide microstructure on the nucleation and growth of uranium hydride on alpha uranium

    International Nuclear Information System (INIS)

    Hanrahan, R.J. Jr.; Hawley, M.E.; Brown, G.W.

    1998-01-01

    While the bulk kinetics of the uranium-hydrogen reaction are well understood, the mechanisms underlying the initial nucleation of uranium hydride on uranium remain controversial. In this study, the authors have employed environmental cell optical microscopy, Scanning Electron Microscopy (SEM) and Atomic Force Microscopy, (AFM) in an attempt to relate the structure of the surface and the microstructure of the substrate with the susceptibility and site of hydride nucleation. Samples have been investigated with varying grain size, inclusion (carbide) concentration, and thermal history. There is a clear correlation to heat treatment immediately prior to hydrogen exposure. Susceptibility to hydride formation also appears to be related to impurities in the uranium. The oxidized surface is very complex, exhibiting wide variations in thickness and topography between samples, between grains in the same sample, and within individual grains. It is, however, very difficult to relate this fine scale variability to the relatively sparse hydride initiation sites. Therefore, the surface oxide layer itself does not appear to control the sites where hydride attack is initiated, although it must play a role in the induction period prior to hydride initiation

  11. The influence of surface morphology and oxide microstructure on the nucleation and growth of uranium hydride on alpha uranium

    Energy Technology Data Exchange (ETDEWEB)

    Hanrahan, R.J. Jr.; Hawley, M.E.; Brown, G.W. [Los Alamos National Lab., NM (United States). Materials Science and Technology Div.

    1998-12-31

    While the bulk kinetics of the uranium-hydrogen reaction are well understood, the mechanisms underlying the initial nucleation of uranium hydride on uranium remain controversial. In this study the authors have employed environmental cell optical microscopy, Scanning Electron Microscopy (SEM) and Atomic Force Microscopy, (AFM) in an attempt to relate the structure of the surface and the microstructure of the substrate with the susceptibility and site of hydride nucleation. Samples have been investigated with varying grain size, inclusion (carbide) concentration, and thermal history. There is a clear correlation to heat treatment immediately prior to hydrogen exposure. Susceptibility to hydride formation also appears to be related to impurities in the uranium. The oxidized surface is very complex, exhibiting wide variations in thickness and topography between samples, between grains in the same sample, and within individual grains. It is, however, very difficult to relate this fine scale variability to the relatively sparse hydride initiation sites. Therefore, the surface oxide layer itself does not appear to control the sites where hydride attack is initiated, although it must play a role in the induction period prior to hydride initiation.

  12. The influence of surface morphology and oxide microstructure on the nucleation and growth of uranium hydride on alpha uranium

    Energy Technology Data Exchange (ETDEWEB)

    Hanrahan, R.J. Jr.; Hawley, M.E.; Brown, G.W.

    1998-12-31

    While the bulk kinetics of the uranium-hydrogen reaction are well understood, the mechanisms underlying the initial nucleation of uranium hydride on uranium remain controversial. In this study, the authors have employed environmental cell optical microscopy, Scanning Electron Microscopy (SEM) and Atomic Force Microscopy, (AFM) in an attempt to relate the structure of the surface and the microstructure of the substrate with the susceptibility and site of hydride nucleation. Samples have been investigated with varying grain size, inclusion (carbide) concentration, and thermal history. There is a clear correlation to heat treatment immediately prior to hydrogen exposure. Susceptibility to hydride formation also appears to be related to impurities in the uranium. The oxidized surface is very complex, exhibiting wide variations in thickness and topography between samples, between grains in the same sample, and within individual grains. It is, however, very difficult to relate this fine scale variability to the relatively sparse hydride initiation sites. Therefore, the surface oxide layer itself does not appear to control the sites where hydride attack is initiated, although it must play a role in the induction period prior to hydride initiation.

  13. Effect of beta phase composition and surface machining on the oxidation behavior of Zr-2.5Nb pressure tube material

    International Nuclear Information System (INIS)

    Nouduru, S.K.; Kiran Kumar, M.; Kain, V.; Khanna, A.S.

    2015-01-01

    Zr-2.5Nb is commonly used as the pressure tube material in pressurized heavy water reactors. it is also the pressure tube material for Advanced Heavy Water Reactor (AHWR) being developed indigenously in India with light water as coolant and water chemistry similar to Boiling Water Reactors (BWR). Oxidation of the pressure tube depends on various factors like material composition, microstructure, fabrication route, and water chemistry. In the present research, the role of the composition and morphology of second phase β on the high temperature and pressure oxidation behavior of Zr-2.5Nb pressure tube material in steam was systematically studied. The as-received pressure tube material (fabricated through cold worked and stress relieved, CWSR route) was subjected to selective heat treatments to generate microstructures containing predominantly β(Zr) (∼ 20% Nb) and β(Nb) (∼ 80% Nb) phases. The presence of such phases was characterized by X-ray diffraction and transmission electron microscopy-energy dispersive spectroscopy. Subsequently both the heat treated materials were subjected to surface machining. The Zr-2.5Nb material in different microstructural conditions was subjected to accelerated oxidation exposures in steam at 400 C. degrees, and 10 MPa pressure up to 30 days. Raman spectroscopy was carried out on the oxide surfaces to observe the variation in tetragonal versus monoclinic phase fractions with oxidation duration. The microstructure consisting of predominantly β(Nb) showed a relatively improved oxidation resistance as compared to the one with predominantly β(Zr). The tetragonal phase fraction in the oxide film decreased with oxidation time in all microstructural conditions and was found to be the least in the microstructure containing β(Zr) after 10 days of exposures. The explanation for the observed higher oxidation resistance of β(Nb) microstructure lies in the context of depleted matrix Nb content in the case of β(Nb). Surface machining

  14. Microstructure of absorber layers in CdTe/CdS solar cells

    International Nuclear Information System (INIS)

    Cousins, M.A.

    2001-04-01

    This work concerns the microstructure of CSS-grown CdTe layers used for CdTe/CdS solar cells. Particular attention is given to how the development of microstructure on annealing with CdCl 2 may correlate with increases in efficiency. By annealing pressed pellets of bulk CdTe powder, it is shown that microstructural change does occur on heating the material, enhanced by the inclusion of CdCl 2 flux. However, the temperature required to cause significant effects is demonstrated to be higher than that at which heavy oxidation takes place. The dynamics of this oxidation are also examined. To investigate microstructural evolution in thin-films of CdTe, bi-layers of CdTe and CdS are examined by bevelling, thus revealing the microstructure to within ∼1 μm of the interface. This allows optical microscopy and subsequent image analysis of grain structure. The work shows that the grain-size, which is well described by the Rayleigh distribution, varies linearly throughout the layer, but is invariant under CdCl 2 treatment. Electrical measurements on these bi-layers, however, showed increased efficiency, as is widely reported. This demonstrates that the efficiency of these devices is not dictated by the bulk microstructure. Further, the region within 1 μm of the interface, of similar bi-layers to above, is examined by plan-view TEM. This reveals five-fold grain-growth on CdCl 2 treatment. Moreover, these grains show a considerably smaller grain size than expected from extrapolating the linear trend in the bulk. These observations are explained in terms of the pinning of the CdTe grain size to the underlying CdS, and the small grain size this causes. A simple model was proposed for a link between the grain-growth to the efficiency improvement. The study also examines the behaviour of defects within grains upon CdCl 2 treatment provided the first direct evidence of recovery on CdCl 2 treatment in this system. Finally, a computer model is presented to describe the evolution of

  15. Numerical evaluation of oxide growth in metallic support microstructures of Solid Oxide Fuel Cells and its influence on mass transport

    DEFF Research Database (Denmark)

    Reiss, Georg; Frandsen, Henrik Lund; Persson, Åsa Helen

    2015-01-01

    is evaluated by determining an effective diffusion coefficient and the equivalent electrical area specific resistance (ASR) due to diffusion over time. It is thus possible to assess the applicability (in terms of corrosion behaviour) of potential metallic supports without costly long-term experiments......-temperature corrosion theory, and the required model parameters can be retrieved by standard corrosion weight gain measurements. The microstructure is reconstructed from X-ray computed tomography, and converted into a computational grid. The influence of the changing microstructure on the fuel cell performance...

  16. Contribution to the study of the microstructure of uranium dioxide (1962); Contribution a l'etude de la microstructure du dioxyde d'uranium (1962)

    Energy Technology Data Exchange (ETDEWEB)

    Porneuf, A. [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1960-05-15

    The microstructure of sintered uranium dioxide is studied in relation with several parameters, specially the sintering temperatures and atmospheres. The external surface and the internal microstructure of the sintered are examined, using fractography and ceramography. Various techniques for preparing surfaces (mechanical and electrolytic polishing) and for revealing the structure (chemical and anodic attack, ionic bombardment oxidation) have been experienced and compared. Patterns similar to those revealed in metals and probably related with interactions between dislocations and vacancies have been observed. (author) [French] La microstructure de frittes d'oxyde d'uranium est etudiee en fonction de divers parametres, en particulier de la temperature et de l'atmosphere de frittage, par examen de la surface externe des frittes, puis de leur microstructure interne (fractographie, ceramographie). Differentes techniques de preparation des surfaces (polissage mecanique ou electrolytique) et de revelation de la structure (attaque chimique ou anodique, bombardement ionique, oxydation preferentielle) ont ete experimentees et comparees. Des figures comparables a celles revelees dans les metaux et liees probablement a des interactions entre dislocations et lacunes ont ete observees. (auteur)

  17. Simulation study of a PEM fuel cell system fed by hydrogen produced by partial oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Ozdogan, S [Marmara University, Faculty of Engineering, Istanbul (Turkey); Ersoz, A; Olgun, H [TUBITAK Marmara Research Center, Energy Systems and Environmental Research Institute, Kocaeli (Turkey)

    2003-09-01

    Within the frame of sustainable development, efficient and clean, if possible zero emission energy production technologies are of utmost importance in various sectors such as utilities, industry, households and transportation. Low-temperature fuel cell systems are suitable for powering transportation systems such as automobiles and trucks in an efficient and low-emitting manner. Proton exchange membrane (PEM) fuel cell systems constitute the most promising low temperature fuel cell option being developed globally. PEM fuel cells generate electric power from air and hydrogen or from a hydrogen rich gas via electrochemical reactions. Water and waste heat are the only by-products of PEM fuel cells. There is great interest in converting current hydrocarbon based common transportation fuels such as gasoline and diesel into hydrogen rich gases acceptable by PEM fuel cells. Hydrogen rich gases can be produced from conventional transportation fuels via various reforming technologies. Steam reforming, partial oxidation and auto-thermal reforming are the three major reforming technologies. In this paper, we discuss the results of a simulation study for a PEM fuel cell with partial oxidation. The Aspen HYSYS 3.1 code has been used for simulation purposes. Two liquid hydrocarbon fuels have been selected to investigate the effect of average molecular weights of hydrocarbons, on the fuel processing efficiency. The overall system efficiency depends on the fuel preparation and fuel cell efficiencies as well as on the heat integration within the system. It is desired to investigate the overall system efficiencies for net electrical power production at 100 kW considering bigger scale transport applications. Results indicate that fuel properties, fuel preparation system operating parameters and PEM fuel cell polarization curve characteristics all affect the overall system efficiency. (authors)

  18. High-Temperature Oxidation and Smelt Deposit Corrosion of Ni-Cr-Ti Arc-Sprayed Coatings

    Science.gov (United States)

    Matthews, S.; Schweizer, M.

    2013-08-01

    High Cr content Ni-Cr-Ti arc-sprayed coatings have been extensively applied to mitigate corrosion in black liquor recovery boilers in the pulp and paper industry. In a previous article, the effects of key spray parameters on the coating's microstructure and its composition were investigated. Three coating microstructures were selected from that previous study to produce a dense, oxidized coating (coating A), a porous, low oxide content coating (coating B), and an optimized coating (coating C) for corrosion testing. Isothermal oxidation trials were performed in air at 550 and 900 °C for 30 days. Additional trials were performed under industrial smelt deposits at 400 and 800 °C for 30 days. The effect of the variation in coating microstructure on the oxidation and smelt's corrosion response was investigated through the characterization of the surface corrosion products, and the internal coating microstructural developments with time at high temperature. The effect of long-term, high-temperature exposure on the interaction between the coating and substrate was characterized, and the mechanism of interdiffusion was discussed.

  19. Microstructural characteristics of high-temperature oxidation in nickel-base superalloy

    International Nuclear Information System (INIS)

    Khalid, F.A.

    1997-01-01

    Superalloys are used for aerospace and nuclear applications where they can withstand high-temperature and severe oxidizing conditions. High-temperature oxidation behavior of a nickel-base superalloy is examined using optical and scanning electron microscopical techniques. The morphology of the oxide layers developed is examined, and EDX microanalysis reveals diffusion of the elements across the oxide-metal interface. Evidence of internal oxidation is presented, and the role of structural defects is considered. The morphology of the oxide-metal interface formed in the specimens exposed in steam and air is examined to elucidate the mechanism of high-temperature oxidation

  20. Effect of microstructure on low cycle fatigue properties of ODS steels

    Energy Technology Data Exchange (ETDEWEB)

    Kubena, Ivo, E-mail: kubena@ipm.cz [IPM, Institute of Physics of Materials, Academy of Sciences of the Czech Republic, Zizkova 22, Brno (Czech Republic); Fournier, Benjamin [CEA/DEN/DANS/DMN/SRMA, Bat. 453, 91191 Gif-sur-Yvette Cedex (France); Kruml, Tomas [CEITEC IPM, Institute of Physics of Materials, Academy of Sciences of the Czech Republic, Zizkova 22, Brno (Czech Republic)

    2012-05-15

    Highlights: Black-Right-Pointing-Pointer Three various ODS steels are studied and compared. Black-Right-Pointing-Pointer Low cycle fatigue data at RT, 650 Degree-Sign C and 750 Degree-Sign C are given. Black-Right-Pointing-Pointer Microstructural characterization. Black-Right-Pointing-Pointer Detailed discussion of strengthening mechanisms. - Abstract: Low cycle fatigue properties at room temperature, 650 Degree-Sign C and 750 Degree-Sign C of three high chromium steels (9%Cr ferritic-martensitic and two 14%Cr ferritic steels) strengthened by oxide dispersion were studied and compared. Cyclic softening/hardening curves, cyclic deformation curves, S-N curves and Coffin-Manson curves are presented together with microstructural observations. Differences in cyclic response, stress level and fatigue life are attributed to differences in the matrix microstructure. The oxide particles stabilize the cyclic response, even if cyclic softening is detected for some experimental conditions. The strength of these steels is discussed in terms of strengthening mechanisms such as grain size effect, particle-dislocations interaction and dislocation density. Comparing three different ODS steels offers an opportunity to tests the contribution of individual mechanisms to the cyclic strength. The reduction of fatigue life in one of the ferritic steels is explained by the presence of large grains, facilitating the fatigue crack nucleation and the early growth.

  1. Partial oxidation of n- and i-pentane over promoted vanadium-phosphorus oxide catalysts

    Energy Technology Data Exchange (ETDEWEB)

    Zazhigalov, V.A.; Mikhajluk, B.D.; Komashko, G.A. [AN Ukrainskoj SSR, Kiev (Ukraine). Inst. Fizicheskoj Khimii

    1998-12-31

    It is known, that the cost of raw materials for catalytic oxidation processes is about 60% of the product price. Cheap initial compounds to produce variety of products and to replace olefins and aromatic hydrocarbons are paraffins. That is why catalytic systems which could be possibly rather efficient in selective oxidation of paraffin hydrocarbons are under very close investigation now. One of such processes in n-pentane oxidation. The obtained results on n-pentane oxidation over VPO catalysts were quite encouraging in respect of possible reach high selectivity and yield of phthalic anhydride. However, in our work it was shown that the main product of n-pentane oxidation in the presence of VPO catalytic system as well as VPMeO was maleic anhydride. Some later our results were confirmed in, where to grow the selectivity towards phthalic anhydride the Co-additive was introduced. On the basis of the proposal made before on the mechanism of paraffins conversion over the vanadyl pyrophosphate surface with their activation at the first and fourth carbon atoms, we assumed possible methylmaleic (citraconic) anhydride forming at n- and i-pentane oxidation. This assumption has been recently supported by both our and other researchers` experimental results. In it was also hypothized possible mechanistic features for phthalic anhydride forming from n-pentane. The present work deals with the results of n- and i-pentane oxidation over VPO catalysts promoted with Bi, Cs, Te, Zr. (orig.)

  2. Supplementary Microstructural Features Induced During Laser Surface Melting of Thermally Sprayed Inconel 625 Coatings

    Science.gov (United States)

    Ahmed, Nauman; Voisey, K. T.; McCartney, D. G.

    2014-02-01

    Laser surface melting of thermally sprayed coatings has the potential to enhance their corrosion properties by incorporating favorable microstructural changes. Besides homogenizing the as-sprayed structure, laser melting may induce certain microstructural modifications (i.e., supplementary features) in addition to those that directly improve the corrosion performance. Such features, being a direct result of the laser treatment process, are described in this paper which is part of a broader study in which high velocity oxy-fuel sprayed Inconel 625 coatings on mild-steel substrates were treated with a diode laser and the modified microstructure characterized using optical and scanning electron microscopy and x-ray diffraction. The laser treated coating features several different zones, including a region with a microstructure in which there is a continuous columnar dendritic structure through a network of retained oxide stringers.

  3. Analysis of electrical and microstructural characteristics of a ZnO-based varistor doped with rare earth oxide; Analise das caracteristicas microestruturais e eletricas de um varistor a base de ZnO dopado com oxidos de terras raras

    Energy Technology Data Exchange (ETDEWEB)

    Andrade, J.M. de; Dias, R.; Furtado, J.G. de M. [Centro de Pesquisas de Energia Eletrica (CEPEL), Rio de Janeiro, RJ (Brazil); Assuncao, F.C.R. [Pontificia Univ. Catolica do Rio de Janeiro (PUC/Rio), RJ (Brazil)

    2010-07-01

    Varistor is a semiconductor device, used in the protection of electrical systems, characterized to have a high no-linear electric resistance. Its properties are directly dependents of its chemical composition and microstructural characteristics. In this work were analyzed microstructural and electrical characteristics of a ZnO-based varistor doped with rare earth oxide, with chemical composition (mol%) 98,5.ZnO - 0,3.Pr{sub 6}O{sub 11} - 0,2.Dy{sub 2}O{sub 3} - 0,9.Co{sub 2}O{sub 3} - 0,1.Cr{sub 2}O{sub 3}. X-ray diffraction for phase characterization, scanning electron microscopy and energy dispersive X-ray spectroscopy were used for microstructural analysis. Measurement of average grain size and electrical and dielectric characteristics complete the characterization. The results show the formation of biphasic microstructure and with high densification, presenting relevant varistors characteristics but that would need improvements.(author)

  4. Enzymatic Upgrading of Heavy Crudes via Partial Oxidation or Conversion of PAHs

    Energy Technology Data Exchange (ETDEWEB)

    Borole, A P; Davison, B H; Kuritz, T

    2002-07-01

    The objective of this program was to investigate new enzyme-based technologies for upgrading of heavy oils. Enzymes were selected for screening from those capable of conversion of polyaromatic hydrocarbons (PAHs) reported in the literature. Oxidative reactions of PAHs using hydrogen peroxide as an oxidant with conversion to partially oxidized products were used. The enzymes (lignin peroxidase, cytochrome c) were tested in various organic solvents and found to loose activity in pure organic solvents. A thermodynamic analysis revealed lack of effective interaction between the substrate and enzyme as the cause for low activity. The protein cytochrome c was modified to work in organic media by chemical hydrophobic group attachment. Two different modifications were made: attachment of polyethylene glycol (PEG) and alkyl groups. Alkyl groups, being small could be attached at interior locations within the core of the enzyme and possibly near the active site. Increase in the threshold solvent concentration where maximum enzyme activity occurred indicated potential of this strategy for effective enzyme-substrate interaction. Further improvements in enzyme activity called for other diverse methods due to the unavailability of sufficient chemical modification sites. Genetic techniques were therefore explored for further improvements. These experiments focused on cloning of a gene for the fungal enzyme lignin peroxidase (lip) into yeast Pichia pastoris, which would allow easy manipulation of the gene. However, differences in the fungal and yeast cellular machinery impeded significant expression of the fungal enzyme. Several strategies were explored to allow higher-level expression of the enzyme, which was required for enzyme improvement. The strategies used in this investigation are described in the report. Industrial in-kind support was available throughout the project period. review of the research results was carried out on a regular basis (bimonthly reports and annual

  5. Effect of zirconium addition on the microstructure and mechanical properties of 15Cr-ODS ferritic Steels consolidated by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Haijian, E-mail: haijianxu@eis.hokudai.ac.jp [Key Laboratory for Anisotropy and Texture of Materials, Ministry of Education, Northeastern University, Shenyang 110819 (China); Material Science and Engineering, Faculty of Engineering, Hokkaido University, Sapporo 060-8628 (Japan); Lu, Zheng; Wang, Dongmei; Liu, Chunming [Key Laboratory for Anisotropy and Texture of Materials, Ministry of Education, Northeastern University, Shenyang 110819 (China)

    2017-01-15

    The influence of Zr addition on the microstructure and mechanical properties of mechanically alloyed (MA) ODS ferritic steels were studied in this work. The microstructure characteristics included the grain size, oxide particles number densities, size distributions, crystal structures and compositions. TEM foils measurements were complemented by studies of alloys on carbon extraction replica and focus ion beam (FIB) foils. The tensile properties were carried out at different temperatures. The microstructure and mechanical properties were analyzed and compared with nominal compositions (wt.%): Fe-15Cr-2W-0.3Y{sub 2}O{sub 3} and Fe-15Cr −2W-0.3Zr-0.3Y{sub 2}O{sub 3}. The experimental revealed that the addition of Zr increased the volume fraction of the smallest and equiaxed ferritic grains, number density of nano-oxide particles and decreased the average size of oxide particles within the ferritic matrix, promoting the formation of fine trigonal δ-phase Y{sub 4}Zr{sub 3}O{sub 12} nano-oxides and leading to the enhancement of the mechanical properties of the ODS steels.

  6. Microstructure of HIPed and SPSed 9Cr-ODS steel and its effect on helium bubble formation

    International Nuclear Information System (INIS)

    Lu, Chenyang; Lu, Zheng; Xie, Rui; Liu, Chunming; Wang, Lumin

    2016-01-01

    Two 9Cr-ODS steels with the same nominal composition were consolidated by hot isostatic pressing (HIP, named COS-1) and spark plasma sintering (SPS, named COS-2). Helium ions were implanted into COS-1, COS-2 and non-ODS Eurofer 97 steels up at 673 K. Microstructures before and after helium ion implantations were carefully characterized. The results show a bimodal grain size distribution in COS-2 and a more uniform grain size distribution in COS-1. Nanoscale clusters of GP-zone type Y–Ti–O and Y_2Ti_2O_7 pyrochlore as well as large spinel Mn(Ti)Cr_2O_4 particles are all observed in the two ODS steels. The Y–Ti-enriched nano-oxides in COS-1 exhibit higher number density and smaller size than in COS-2. The Y–Ti-enriched nano-oxides in fine grains of COS-2 show higher number density and smaller size than that in coarse grains of COS-2. Nano-oxides effectively trap helium atoms and lead to the formation of high density and ultra-fine helium bubbles. - Highlights: • The microstructure changes of two ODS steels before and after helium ion implantation have been elucidated. • The mechanism of the microstructures of ODS steels under varied thermal mechanical processing paths have been explored. • The dependence of the size, density and distribution of helium bubbles on the specific microstructure features are explored.

  7. Microstructure of HIPed and SPSed 9Cr-ODS steel and its effect on helium bubble formation

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Chenyang [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), School of Material Science and Engineering, Northeastern University, Shenyang 110819, Liaoning (China); Department of Nuclear Engineering and Radiological Science, University of Michigan, Ann Arbor, MI, 48109 (United States); Lu, Zheng, E-mail: luz@atm.neu.edu.cn [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), School of Material Science and Engineering, Northeastern University, Shenyang 110819, Liaoning (China); Xie, Rui; Liu, Chunming [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), School of Material Science and Engineering, Northeastern University, Shenyang 110819, Liaoning (China); Wang, Lumin, E-mail: lmwang@umich.edu [Department of Nuclear Engineering and Radiological Science, University of Michigan, Ann Arbor, MI, 48109 (United States)

    2016-06-15

    Two 9Cr-ODS steels with the same nominal composition were consolidated by hot isostatic pressing (HIP, named COS-1) and spark plasma sintering (SPS, named COS-2). Helium ions were implanted into COS-1, COS-2 and non-ODS Eurofer 97 steels up at 673 K. Microstructures before and after helium ion implantations were carefully characterized. The results show a bimodal grain size distribution in COS-2 and a more uniform grain size distribution in COS-1. Nanoscale clusters of GP-zone type Y–Ti–O and Y{sub 2}Ti{sub 2}O{sub 7} pyrochlore as well as large spinel Mn(Ti)Cr{sub 2}O{sub 4} particles are all observed in the two ODS steels. The Y–Ti-enriched nano-oxides in COS-1 exhibit higher number density and smaller size than in COS-2. The Y–Ti-enriched nano-oxides in fine grains of COS-2 show higher number density and smaller size than that in coarse grains of COS-2. Nano-oxides effectively trap helium atoms and lead to the formation of high density and ultra-fine helium bubbles. - Highlights: • The microstructure changes of two ODS steels before and after helium ion implantation have been elucidated. • The mechanism of the microstructures of ODS steels under varied thermal mechanical processing paths have been explored. • The dependence of the size, density and distribution of helium bubbles on the specific microstructure features are explored.

  8. Effect of phosphate additives on the microstructure, bioactivity, and degradability of microarc oxidation coatings on Mg-Zn-Ca-Mn alloy.

    Science.gov (United States)

    Dou, Jinhe; You, Qiongya; Gu, Guochao; Chen, Chuanzhong; Zhang, Xihua

    2016-09-20

    Calcium phosphate coatings were prepared on the surface of self-designed Mg-Zn-Ca-Mn alloy using microarc oxidization technology. To characterize the microstructures, cross-section morphologies, and compositions of the coatings, the authors used scanning electron microscopy equipped with an energy-disperse spectrometer, x-ray diffraction, and Fourier transform infrared spectroscopy. Potentiodynamic polarization in the simulated body fluid (SBF) was used to evaluate the corrosion behaviors of the samples. An SBF immersion test was used to evaluate the coating bioactivity and degradability. After the immersion tests, some bonelike apatite formed on the coating surfaces indicate that bioactivity of the coatings is excellent. The coating prepared in electrolyte containing (NaPO3)6 had slower degradation rate after immersion test for 21 days.

  9. Adiabatic Gasification and Pyrolysis of Coffee Husk Using Air-Steam for Partial Oxidation

    Directory of Open Access Journals (Sweden)

    Catalina Rodriguez

    2011-01-01

    Full Text Available Colombian coffee industry produces about 0.6 million tons of husk (CH per year which could serve as feedstock for thermal gasification to produce gaseous and liquid fuels. The current paper deals with: (i CH adiabatic gasification modeling using air-steam blends for partial oxidation and (ii experimental thermogravimetric analysis to determine the CH activation energy (E. The Chemical Equilibrium with Applications Program (CEA, developed by NASA, was used to estimate the effect of equivalence ratio (ER and steam to fuel ratio (S : F on equilibrium temperature and gas composition of ~150 species. Also, an atom balance model was developed for comparison purposes. The results showed that increased ER and (S : F ratios produce mixtures that are rich in H2 and CO2 but poor in CO. The value for the activation energy was estimated to be 221 kJ/kmol.

  10. Experimental investigation and thermodynamic simulation of the uranium oxide-zirconium oxide-iron oxide system in air

    Czech Academy of Sciences Publication Activity Database

    Petrov, Y. B.; Udalov, Y. P.; Šubrt, Jan; Bakardjieva, Snejana; Sázavský, P.; Kiselová, M.; Selucký, P.; Bezdička, Petr; Joumeau, C.; Piluso, P.

    2011-01-01

    Roč. 37, č. 2 (2011), s. 212-229 ISSN 1087-6596 Institutional research plan: CEZ:AV0Z40320502 Keywords : uranium oxide * zirconium oxide * iron oxide * fusibility curve * oxygen partial pressure * crystallization * phase composition Subject RIV: CA - Inorganic Chemistry Impact factor: 0.492, year: 2011

  11. Microstructure and Properties of High-Temperature Superconductors

    CERN Document Server

    Parinov, Ivan A

    2007-01-01

    The main features of high-temperature superconductors (HTSC) that define their properties are intrinsic brittleness of oxide cuprates, the layered anisotropic structure and the supershort coherence length. Taking into account these features, this treatise presents research into HTSC microstructure and properties, and also explores the possibilities of optimization of the preparation techniques and superconducting compositions. The "composition-technique-experiment-theory-model," employed here, assumes considerable HTSC defectiveness and structure heterogeneity and helps to draw a comprehensive picture of modern representations of the microstructure, strength and the related structure-sensitive properties of the materials considered. Special attention is devoted to the Bi-Sr-Ca-Cu-O and Y-Ba-Cu-O families, which currently offer the most promising applications. Including a great number of illustrations and references, this monograph addresses students, post-graduate students and specialists, taking part in the ...

  12. Microstructure and Properties of High-Temperature Superconductors

    CERN Document Server

    Parinov, I A

    2012-01-01

    The main features of high-temperature superconductors (HTSC) that define their properties are intrinsic brittleness of oxide cuprates, the layered anisotropic structure and the supershort coherence length. Taking into account these features, this treatise presents research into HTSC microstructure and properties, and also explores the possibilities of optimization of the preparation techniques and superconducting compositions. The "composition-technique-experiment-theory-model," employed here, assumes considerable HTSC defectiveness and structure heterogeneity and helps to draw a comprehensive picture of modern representations of the microstructure, strength and the related structure-sensitive properties of the materials considered. Special attention is devoted to the Bi-Sr-Ca-Cu-O and Y-Ba-Cu-O families, which currently offer the most promising applications. Including a great number of illustrations and references, this monograph addresses students, post-graduate students and specialists, taking part in the ...

  13. Characterization of SCC crack tips and surface oxide layers in alloy 600

    Energy Technology Data Exchange (ETDEWEB)

    Fujii, Katsuhiko; Fukuya, Koji [Inst. of Nuclear Safety System Inc., Mihama, Fukui (Japan)

    2002-09-01

    In order to investigate the mechanism of primary water stress corrosion cracking (SCC), direct observation of microstructures of SCC crack tips and surface oxide layers in alloy 600 were carried out. A focused-ion beam (FIB) micro-processing technique was applied to prepare electron transparent foils including the crack tip and the surface oxide layer without any damage to those microstructures. Transmission electron microscopy and analysis were used to characterize the crack tips and surface oxide layers. Cr-rich oxides and a metal-Ni phase were identified in the crack tips and grain boundaries ahead of the crack tips independent of dissolved hydrogen concentrations. >From the fact that the Cr-rich oxides and metal-Ni phase were observed in the inner surface oxide layer, the same oxidation mechanism as the surface is proposed for the crack tip region and internal oxidation accompanying selective Cr oxidation is suggested as the mechanism. (author)

  14. Inkjet Impregnation for Tailoring Air Electrode Microstructure to Improve Solid Oxide Cells Performance

    KAUST Repository

    Da’as, Eman H.

    2015-09-30

    The urge to lower the operating temperature of solid oxide cells (SOCs) to the intermediate ranges between 500-700°C motivated the research into impregnation processes, which offer highly efficient SOC air electrodes at low operating temperatures. Lack of controllability and reproducibility of this technique in the conventional way is still considered as an inadequacy for industrialization since it is performed manually. Therefore, inkjet-printing technology was proposed as an adequate approach to perform scalable and controllable impregnation for SOC air electrodes, which in turn leads to low operating temperatures. Composite LSM-ionic conductive air electrodes of weight ratio 1:2 were fabricated by inkjet impregnation of lanthanum strontium manganite (La0.8Sr0.2MnO3) precursor nitrates onto a porous ionic conductive backbone structure. First, porous yttria stabilized zirconia (8YSZ) substrates prepared by tape casting were used to study the influence of the printing parameters on the lateral dispersion and penetration of LSM ink inside the pores. XRD analysis confirmed the formation of LSM phase after calcination at 800°C for 2 h, while SEM revealed the formation of LSM nanostructures. It has been found by optical microscope observations that the spacing between the drops and the substrate temperature have a significant role in controlling the printing process. Next, the optimized printing parameters were applied in the inkjet impregnation of the LSM ink into porous YSZ electrodes that were spin coated on both sides of dense YSZ layers. LSM-YSZ composite air electrodes achieved an area specific resistance (ASR) of around 0.29 Ω.cm2 at 700°C. The performance of LSM-YSZ composite electrodes was influenced by the microstructure and the thickness, and by the electrode/electrolyte interface characteristics. As a result, the enhancement in LSM-YSZ composite electrode performance was observed due to the better percolation in LSM, YSZ and oxygen diffusion. Finally

  15. The surface microstructure of cusps and leaflets in rabbit and mouse heart valves

    Directory of Open Access Journals (Sweden)

    Xia Ye

    2014-05-01

    Full Text Available In this investigation, scanning electron microscopy was used to characterize the microstructure on the surfaces of animal heart valve cusps/leaflets. The results showed that though these surfaces appear smooth to the naked eye, they are actually comprised of a double hierarchical structure consisting of a cobblestone-like microstructure and nano-cilia along with mastoids with a directional arrangement. Such nanostructures could play a very important role in the hemocompatibility characteristics of heart valves. On this basis, the model of the microstructure was constructed and theoretical analysis was used to obtain optimal geometric parameters for the rough surface of artificial valve cusps/leaflets. This model may help improve reconstructive techniques and it may be beneficial in the design and fabrication of valve substitutes or partial substitutes. Namely, the model may help ameliorate heart valve replacement surgery.

  16. Microstructure and thermoelectric properties of screen-printed thick-films of misfit-layered cobalt oxides with Ag addition

    DEFF Research Database (Denmark)

    Van Nong, Ngo; Samson, Alfred Junio; Pryds, Nini

    2012-01-01

    Thermoelectric properties of thick (~60 μm) films prepared by a screen-printing technique using p-type misfit-layered cobalt oxide Ca3Co4O9+δ with Ag addition have been studied. The screen-printed films were sintered in air at various temperatures ranging from 973 K to 1223 K. After each sintering...... process, crystal and microstructure analyses were carried out to determine the optimal sintering condition. The results show that the thermoelectric properties of pure Ca3Co4O9+δ thick film are comparable to those of cold isostatic pressing (CIP) samples. We found that the maximum power factor...... was improved by about 67% (to 0.3 mW/m K2) for film with proper silver (Ag) metallic inclusions as compared with 0.18 mW/m K2 for pure Ca3Co4O9+δ film under the same sintering condition of 1223 K for 2 h in air....

  17. Influence of Normalizing Temperature on the Microstructure and Hardness of 9Cr-1Mo ODS Steel

    Energy Technology Data Exchange (ETDEWEB)

    Jang, Ki Nam; Kim, Tae Kyu [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Kim, Kyu Tae [Dongguk University, Gyeongju (Korea, Republic of)

    2016-10-15

    Oxide dispersion strengthened(ODS) steel has superior high-temperature strength and creep properties because fine oxide particles having an excellent stability at high temperatures are uniformly distributed in the matrix. ODS steel has being developed for structure materials of sodium fast cooled reactor(SFR) because of its excellent irradiation resistance and mechanical properties. 9Cr-1Mo ODS steel has better high temperature strength and irradiation resistance than common 9Cr-1Mo steel because Y{sub 2}O{sub 3} nano-sized particles which interrupt dislocation movement and grain boundary slip are uniformly dispersed in the martensite matrix. The mechanical properties of the ODS steels are mainly determined by their microstructures, and the microstructure is considerably decided by the heat-treatment conditions. This study focused on the effect of normalizing temperature on microstructure and hardness of 9Cr-1Mo martensitic ODS steel so as to optimize the heat-treatment condition. In this study, the effect of normalizing temperature on mechanical property and microstructures of 9Cr-1Mo martensitic ODS steel was investigated. It was shown that the microhardness was steadily increased with increasing of the normalizing temperature. According to TEM observation, mechanical property of 9Cr-1Mo ODS steel was significantly affected by lath width. These observations, could be useful to understand the relationship between normalizing temperature and microstructure.

  18. Effect of processing conditions on microstructural features in Mn–Si sintered steels

    Energy Technology Data Exchange (ETDEWEB)

    Oro, Raquel, E-mail: raqueld@chalmers.se [Department of Materials and Manufacturing Technology, Chalmers University of Technology, Rännvägen 2A, SE-41296 Gothenburg (Sweden); Hryha, Eduard, E-mail: hryha@chalmers.se [Department of Materials and Manufacturing Technology, Chalmers University of Technology, Rännvägen 2A, SE-41296 Gothenburg (Sweden); Campos, Mónica, E-mail: campos@ing.uc3m.es [Department of Materials Science and Engineering, IAAB, Universidad Carlos III de Madrid, Av. Universidad 30, 28911 Leganés, Madrid (Spain); Torralba, José M., E-mail: torralba@ing.uc3m.es [Department of Materials Science and Engineering, IAAB, Universidad Carlos III de Madrid, Av. Universidad 30, 28911 Leganés, Madrid (Spain); IMDEA Materials Institute, c/Eric Kandel, 2, 28906 Getafe, Madrid (Spain)

    2014-09-15

    Sintering of steels containing oxidation sensitive elements is possible if such elements are alloyed with others which present lower affinity for oxygen. In this work, a master alloy powder containing Fe–Mn–Si–C, specifically designed to create a liquid phase during sintering, has been used for such purpose. The effect of processing conditions such as sintering temperature and atmosphere was studied with the aim of describing the microstructural evolution as well as the morphology and distribution of oxides in the sintered material, evaluating the potential detrimental effect of such oxides on mechanical properties. Chemical analyses, metallography and fractography studies combined with X-ray photoelectron spectroscopy analyses on the fracture surfaces were used to reveal the main mechanism of fracture and their correlation with the chemical composition of the different fracture surfaces. The results indicate that the main mechanism of failure in these steels is brittle fracture in the surrounding of the original master alloy particles due to degradation of grain boundaries by the presence of oxide inclusions. Mn–Si oxide inclusions were observed on intergranular decohesive facets. The use of reducing atmospheres and high sintering temperatures reduces the amount and size of such oxide inclusions. Besides, high heating and cooling rates reduce significantly the final oxygen content in the sintered material. A model for microstructure development and oxide evolution during different stages of sintering is proposed, considering the fact that when the master alloy melts, the liquid formed can dissolve some of the oxides as well as the surface of the surrounding iron base particles. - Highlights: • Oxide distribution in steels containing oxidation-sensitive elements • Mn, Si introduced in a master alloy powder, mixed with a base iron powder • Selective oxidation of Mn and Si on iron grain boundaries • Decohesive fracture caused by degradation of grain

  19. Effect of processing conditions on microstructural features in Mn–Si sintered steels

    International Nuclear Information System (INIS)

    Oro, Raquel; Hryha, Eduard; Campos, Mónica; Torralba, José M.

    2014-01-01

    Sintering of steels containing oxidation sensitive elements is possible if such elements are alloyed with others which present lower affinity for oxygen. In this work, a master alloy powder containing Fe–Mn–Si–C, specifically designed to create a liquid phase during sintering, has been used for such purpose. The effect of processing conditions such as sintering temperature and atmosphere was studied with the aim of describing the microstructural evolution as well as the morphology and distribution of oxides in the sintered material, evaluating the potential detrimental effect of such oxides on mechanical properties. Chemical analyses, metallography and fractography studies combined with X-ray photoelectron spectroscopy analyses on the fracture surfaces were used to reveal the main mechanism of fracture and their correlation with the chemical composition of the different fracture surfaces. The results indicate that the main mechanism of failure in these steels is brittle fracture in the surrounding of the original master alloy particles due to degradation of grain boundaries by the presence of oxide inclusions. Mn–Si oxide inclusions were observed on intergranular decohesive facets. The use of reducing atmospheres and high sintering temperatures reduces the amount and size of such oxide inclusions. Besides, high heating and cooling rates reduce significantly the final oxygen content in the sintered material. A model for microstructure development and oxide evolution during different stages of sintering is proposed, considering the fact that when the master alloy melts, the liquid formed can dissolve some of the oxides as well as the surface of the surrounding iron base particles. - Highlights: • Oxide distribution in steels containing oxidation-sensitive elements • Mn, Si introduced in a master alloy powder, mixed with a base iron powder • Selective oxidation of Mn and Si on iron grain boundaries • Decohesive fracture caused by degradation of grain

  20. Bias-induced migration of ionized donors in amorphous oxide semiconductor thin-film transistors with full bottom-gate and partial top-gate structures

    Directory of Open Access Journals (Sweden)

    Mallory Mativenga

    2012-09-01

    Full Text Available Bias-induced charge migration in amorphous oxide semiconductor thin-film transistors (TFTs confirmed by overshoots of mobility after bias stressing dual gated TFTs is presented. The overshoots in mobility are reversible and only occur in TFTs with a full bottom-gate (covers the whole channel and partial top-gate (covers only a portion of the channel, indicating a bias-induced uneven distribution of ionized donors: Ionized donors migrate towards the region of the channel that is located underneath the partial top-gate and the decrease in the density of ionized donors in the uncovered portion results in the reversible increase in mobility.

  1. Microstructure and Mechanical Property of ODS Ferritic Steels Using Commercial Alloy Powders for High Temperature Service Applications

    Energy Technology Data Exchange (ETDEWEB)

    Noh, Sanghoon; Choi, Byoung-Kwon; Kang, Suk Hoon; Kim, Tae Kyu [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2016-10-15

    Oxide dispersion strengthening (ODS) is one of the promising ways to improve the mechanical property at high temperatures. This is mainly attributed to uniformly distributed nano-oxide particle with a high density, which is extremely stable at the high temperature and acts as effective obstacles when the dislocations are moving. In this study, as a preliminary examination to develop the advanced structural materials for high temperature service applications, ODS ferritic steels were fabricated using commercial alloy powders and their microstructural and mechanical properties were investigated. In this study, ODS ferritic steels were fabricated using commercial stainless steel 430L powder and their microstructures and mechanical properties were investigated. Morphology of micro-grains and oxide particles were significantly changed by the addition of minor alloying elements such as Ti, Zr, and Hf. The ODS ferritic steel with Zr and Hf additions showed ultra-fine grains with fine complex oxide particles. The oxide particles were uniformly located in grains and on the grain boundaries. This led to higher hardness than ODS ferritic steel with Ti addition.

  2. The reaction mechanism of the partial oxidation of methane to synthesis gas: a transient kinetic study over rhodium and a comparison with platinum

    NARCIS (Netherlands)

    Mallens, E.P.J.; Hoebink, J.H.B.J.; Marin, G.B.M.M.

    1997-01-01

    The partial oxidation of methane to synthesis gas over rhodium sponge has been investigated by admitting pulses of pure methane and pure oxygen as well as mixtures of methane and oxygen to rhodium sponge at temperatures from 873 to 1023 K. Moreover, pulses of oxygen followed by methane and vice

  3. Processing, microstructure evolution and properties of nanoscale aluminum alloys

    Science.gov (United States)

    Han, Jixiong

    In this project, phase transformations and precipitation behavior in age-hardenable nanoscale materials systems, using Al-Cu alloys as model materials, were first studied. The Al-Cu nanoparticles were synthesized by a Plasma Ablation process and found to contain a 2˜5 nm thick adherent aluminum oxide scale, which prevented further oxidation. On aging of the particles, a precipitation sequence consisting of, nearly pure Cu precipitates to the metastable theta' to equilibrium theta was observed, with all three forming along the oxide-particle interface. The structure of theta' and its interface with the Al matrix has been characterized in detail. Ultrafine Al-Cu nanoparticles (5˜25 nm) were also synthesized by inert gas condensation (IGC) and their aging behavior was studied. These particles were found to be quite stable against precipitation. Secondly, pure Al nanoparticles were prepared by the Exploding Wire process and their sintering and consolidation behavior were studied. It was found that nanopowders of Al could be processed to bulk structures with high hardness and density. Sintering temperature was found to have a dominant effect on density, hardness and microstructure. Sintering at temperatures >600°C led to breakup of the oxide scale, leading to an interesting nanocomposite composed of 100˜200 nm Al oxide dispersed in a bimodal nanometer-micrometer size Al matrix grains. Although there was some grain growth, the randomly dispersed oxide fragments were quite effective in pinning the Al grain boundaries, preventing excessive grain growth and retaining high hardness. Cold rolling and hot rolling were effective methods for attaining full densification and high hardness. Thirdly, the microstructure evolution and mechanical behavior of Al-Al 2O3 nanocomposites were studied. The composites can retain high strength at elevated temperature and thermal soaking has practically no detrimental effect on strength. Although the ductility of the composite remains

  4. Mechanisms of microstructural changes of fuel under irradiation

    International Nuclear Information System (INIS)

    Garcia, P.; Carlot, G.; Dorado, B.; Maillard, S.; Sabathier, C.; Martin, G.; Oh, J.Y.; Welland, M.J.

    2015-01-01

    Nuclear fuels are subjected to high levels of radiation damage mainly due to the slowing of fission fragments, which results in substantial modifications of the initial fuel microstructure. Microstructure changes alter practically all engineering fuel properties such as atomic transport or thermomechanical properties so understanding these changes is essential to predicting the performance of fuel elements. Also, with increasing burn-up, the fuel drifts away from its initial composition as the fission process produces new chemical elements. Because nuclear fuels operate at high temperature and usually under high-temperature gradients, damage annealing, foreign atom or defect clustering and migration occur on multiple time and length scales, which make long-term predictions difficult. The end result is a fuel microstructure which may show extensive differences on the scale of a single fuel pellet. The main challenge we are faced with is, therefore, to identify the phenomena occurring on the atom scale that are liable to have macroscopic effects that will determine the microstructure changes and ultimately the life-span of a fuel element. One step towards meeting this challenge is to develop and apply experimental or modelling methods capable of connecting events that occur over very short length and timescales to changes in the fuel microstructure over engineering length and timescales. In the first part of this chapter, we provide an overview of some of the more important microstructure modifications observed in nuclear fuels. The emphasis is placed on oxide fuels because of the extensive amount of data available in relation to these materials under neutron or ion irradiation. When possible and relevant, the specifics of other types of fuels such as metallic or carbide fuels are alluded to. Throughout this chapter but more specifically in the latter part, we attempt to give examples of how modelling and experimentation at various scales can provide us with

  5. One-step fabrication of nanostructure-covered microstructures using selective aluminum anodization based on non-uniform electric field

    Science.gov (United States)

    Park, Yong Min; Kim, Byeong Hee; Seo, Young Ho

    2016-06-01

    This paper presents a selective aluminum anodization technique for the fabrication of microstructures covered by nanoscale dome structures. It is possible to fabricate bulging microstructures, utilizing the different growth rates of anodic aluminum oxide in non-uniform electric fields, because the growth rate of anodic aluminum oxide depends on the intensity of electric field, or current density. After anodizing under a non-uniform electric field, bulging microstructures covered by nanostructures were fabricated by removing the residual aluminum layer. The non-uniform electric field induced by insulative micropatterns was estimated by computational simulations and verified experimentally. Utilizing computational simulations, the intensity profile of the electric field was calculated according to the ratio of height and width of the insulative micropatterns. To compare computational simulation results and experimental results, insulative micropatterns were fabricated using SU-8 photoresist. The results verified that the shape of the bottom topology of anodic alumina was strongly dependent on the intensity profile of the applied electric field, or current density. The one-step fabrication of nanostructure-covered microstructures can be applied to various fields, such as nano-biochip and nano-optics, owing to its simplicity and cost effectiveness.

  6. Thermoelectric Properties and Microstructure of Modified Novel Complex Cobalt Oxides Sr3RECo4O10.5 (RE = Y, Gd)

    DEFF Research Database (Denmark)

    Van Nong, Ngo; Pryds, Nini

    2012-01-01

    We report on the high-temperature thermoelectric properties and microstructure of modified novel complex cobalt oxides Sr3RECo4O10.5 (RE = Y, Gd), in which the Sr- and Co-sites are partly substituted by Ca and Ga, respectively. We have found that the sample with RE = Gd shows a significant higher......-sample resulting in a substantial decrease in porosity, its thermal diffusivity exhibits a lower value then the non-doped one, particularly in high temperature region. © 2012 American Institute of Physics...

  7. Partial thermodynamic functions of hydrogen in complex hydrated vanadium(5) and tungsten(6) oxides

    International Nuclear Information System (INIS)

    Volkov, V.L.; Zakharova, G.S.

    2003-01-01

    The partial thermodynamic characteristics of hydrogen in the complex hydrated vanadium(5) and tungsten(6) oxides, obtained through the sol-gel method, of the general formula H 2 V 12-y W y O 31+δ ·nH 2 O (0 ≤ x ≤ 0.33) are determined through the emf method. The changes in these values (ΔG-bar(H 2 ), ΔH-bar(H 2 ) and ΔS-bar(H 2 )) in dependence on the compound composition are discussed. It is established that ΔG-bar(H 2 ) phases, amorphous to X-rays are determined by the ΔS-bar(H 2 ) value and crystalline ones by ΔH-bar(H 2 ). The scheme of the phase relationships of the H 2 O-H-WO 3 -V 2 O 5 system, whereto the given phases are related are presented [ru

  8. ODS steel fabrication: relationships between process, microstructure and mechanical properties

    International Nuclear Information System (INIS)

    Couvrat, M.

    2011-01-01

    Oxide Dispersion Strengthened (ODS) steels are promising candidate materials for generation IV and fusion nuclear energy systems thanks to their excellent thermal stability, high-temperature creep strength and good irradiation resistance. Their superior properties are attributed both to their nano-structured matrix and to a high density of Y-Ti-O nano-scale clusters (NCs). ODS steels are generally prepared by Mechanical Alloying of a pre-alloyed Fe-Cr-W-Ti powder with Y 2 O 3 powder. A fully dense bar or tube is then produced from this nano-structured powder by the mean of hot extrusion. The aim of this work was to determine the main parameters of the process of hot extrusion and to understand the link between the fabrication process, the microstructure and the mechanical properties. The material microstructure was characterized at each step of the process and bars were extruded with varying hot extrusion parameters so as to identify the impact of these parameters. Temperature then appeared to be the main parameter having a great impact on microstructure and mechanical properties of the extruded material. We then proposed a cartography giving the microstructure versus the process parameters. Based on these results, it is possible to control very accurately the obtained material microstructure and mechanical properties setting the extrusion parameters. (author) [fr

  9. Oxidative Stability of Nano-Microstructures containing fish oil

    DEFF Research Database (Denmark)

    García Moreno, Pedro Jesús; Özdemir, N.; Boutrup Stephansen, Karen

    investigated. For that purpose, three different biopolymers namely pullulan, dextran and whey protein concentrate (WPC) were evaluated as encapsulating materials. First, the influence of biopolymer concentration on the physical properties (e.g. viscosity, conductivity and surface tension) of the biopolymer...... solutions and on the morphology of NMS was assayed. Secondly, the oxidative stability of the biopolymer solutions containing emulsified fish oil during storage (14 days at 40 °C) and of NMS loaded with fish oil (e.g. pullulan fibers and dextran and WPC capsules) was determined. Finally, to improve...... the oxidative status of the NMS, pullulan fibers, dextran capsules and WPC capsules were produced by adding neat fish oil instead of emulsified fish oil to the biopolymer solutions. These latter NMS presented a higher oxidative stability, which may be due to a better entrapment of the fish oil into biopolymer...

  10. A new partial SOI-LDMOSFET with a modified buried oxide layer for improving self-heating and breakdown voltage

    International Nuclear Information System (INIS)

    Jamali Mahabadi, S E; Orouji, Ali A; Keshavarzi, P; Moghadam, Hamid Amini

    2011-01-01

    In this paper, for the first time, we propose a partial silicon-on-insulator (P-SOI) lateral double-diffused metal-oxide-semiconductor-field-effect-transistor (LDMOSFET) with a modified buried layer in order to improve breakdown voltage (BV) and self-heating effects (SHEs). The main idea of this work is to control the electric field by shaping the buried layer. With two steps introduced in the buried layer, the electric field distribution is modified. Also a P-type window introduced makes the substrate share the vertical voltage drop, leading to a high vertical BV. Moreover, four interface electric field peaks are introduced by the buried P-layer, the Si window and two steps, which modulate the electric field in the SOI layer and the substrate. Hence, a more uniform electric field is obtained; consequently, a high BV is achieved. Furthermore, the Si window creates a conduction path between the active layer and substrate and alleviates the SHE. Two-dimensional simulations show that the BV of double step partial silicon on insulator is nearly 69% higher and alleviates SHEs 17% in comparison with its single step partial SOI counterpart and nearly 265% higher and alleviate SHEs 18% in comparison with its conventional SOI counterpart

  11. Hydrogen or synthesis gas production via the partial oxidation of methane over supported nickel-cobalt catalysts

    Energy Technology Data Exchange (ETDEWEB)

    Koh, Alaric C.W. [Department of Chemistry, National University of Singapore, 3 Science Drive 3, Singapore 117543 (Singapore); Institute of Chemical and Engineering Sciences, 1 Pesek Road, Jurong Island, Singapore 627833 (Singapore); Chen, Luwei; Lin, Jianyi [Institute of Chemical and Engineering Sciences, 1 Pesek Road, Jurong Island, Singapore 627833 (Singapore); Kee Leong, Weng [Department of Chemistry, National University of Singapore, 3 Science Drive 3, Singapore 117543 (Singapore); Johnson, Brian F.G.; Khimyak, Tetyana [University Chemical Laboratory, University of Cambridge, Lensfield Road, Cambridge, UK CB2 1EW (United Kingdom)

    2007-05-15

    Activity, selectivity, and coking-resistance of a series of Ni{sub x}Co{sub y} (where x,y are the respective metal loadings of 0, 1, 2 or 3 wt.%; x+y=3) bimetallic catalysts supported on CaAl{sub 2}O{sub 4}/Al{sub 2}O{sub 3} have been studied for hydrogen/synthesis gas production via the catalytic partial oxidation (CPO) of methane. Catalysts were characterized by temperature programmed reduction (TPR), transmission electron microscopy (TEM) and X-ray fluorescence multi-element analysis (XRF). Their activity for the partial oxidation of methane to hydrogen and carbon monoxide (at 1 bar, gas hourly space velocity (GHSV) of 144,000cm{sup 3}g{sup -1}h{sup -1} and CH{sub 4}/O{sub 2} molar ratio of 2) was investigated, and coke deposited on the spent catalysts was studied by scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and thermogravimetric analysis (TGA). The activity was found to decrease in the order of Ni{sub 2}Co>Ni{sub 3}>NiCo{sub 2}>>Co{sub 3}, while CO and H{sub 2} selectivities were found to be in the order ofNi{sub 2}Co>Ni{sub 3}{approx}NiCo{sub 2}>Co{sub 3}. Ni{sub 2}Co is also shown to be more resistant to coking as compared to Ni{sub 3}, which is a current catalyst of choice. Results show that not only does Ni{sub 2}Co have the highest activity and selectivity among all the catalysts tested, it is also relatively resistant to coking. This finding would be helpful for catalyst design to achieve high coking resistivity catalysts for hydrogen production from CPO of methane. (author)

  12. The Effect of adding pore formers on the microstructure of NiO-YSZ ceramic composite

    International Nuclear Information System (INIS)

    Silva, F.S.; Santos, F.S.; Medeiros, L.M.; Yoshito, W.K.; Lazar, D.R.R.; Ussui, V.

    2011-01-01

    The ceramic composite of nickel oxide (NiO) with zirconium stabilized with 8 mol% yttria (8-YSZ) is the most employed material for use as anode for solid oxide fuel cells (SOFC). The nickel oxide in the composite is reduced to metallic nickel and this result in a 15% of porosity although the porosity needed to a proper function of an anode is about 30%, demanding the use of a pore former. In this work, NiO-YSZ composite powders were synthesized by a combustion process with urea as fuel, and the effect of the addition of carbon black and corn and rice starch as pore former were investigated. Powders were pressed as cylindrical pellets, sintered at 1350 °C for 60 minutes and density were measured by an immersion method and microstructure were observed by scanning electron microscopy. Results showed that ceramic composite has homogeneous microstructure and pores have different morphology and size depending on the kind of the pore former employed. (author)

  13. Calculation of solidification microstructure maps for the system Al-Fe-Si

    International Nuclear Information System (INIS)

    Gilgien, P.

    1996-01-01

    Computer programs have been developed in order to calculate solidification microstructure maps for binary and ternary alloys. These programs are based on recent analytical models for the constrained growth of dendrites and eutectics. Due to the importance of phase diagrams data, programs for the calculation of growth kinetics are coupled with ThermoCalc, a commercial software for phase diagram calculations. These programs have been used to calculate a solidification microstructure map for the Al-Fe system from 0 to 4 at%Fe. Comparison of the calculated results with an experimental solidification microstructure map from the literature shows that all microstructure transitions were predicted. Nevertheless there remain significant discrepancies between some calculated and experimental transition velocities. The programs were also used to calculate solidification microstructure maps in the Al-rich corner of the Al-Fe-Si system (0 to 8 at% Fe and 0 to 8 at% Si). In this case also, calculated results were in satisfactory agreement with experimental solidification microstructure maps, although the comparison was only partial since experimental ternary microstructure maps are less complete than for the binary system, and because the available thermodynamic database does not, as yet, include metastable phases. Laser surface remelting experiments were carried out on an Al-4 at% Fe alloy in order to link results from the literature, obtained at high solidification rates by laser surface remelting and at low solidification rates by Bridman experiments. Finally, Bridman experiments were carried out with an Al-2.63 wt% Fe alloy in order to determine the critical velocity at which a planar Al-Al 13 Fe 4 eutectic front is destabilised in a cellular eutectic by a small amount of Si. The critical solidification velocity thus obtained was in agreement with a criterion of constitutional undercooling. (author) figs., tabs., refs

  14. Evaluation of the structure and microstructure of Ni{sub x}Mg{sub 1-x}O oxides obtained by co-precipitation; Evaluacion de la estructura y microestructura de oxidos de Ni{sub x}Mg{sub 1-x}O obtenidos por co-precipitacion

    Energy Technology Data Exchange (ETDEWEB)

    Martinez L, G.; Kryshtab, T. [IPN, Escuela Superior de Fisica y Matematicas, Departamento de Fisica, Av. Instituto Politecnico Nacional s/n, Edif. 9, 07738 Mexico D. F. (Mexico); Hesiquio G, M. [IPN, Escuela Superior de Ingenieria Quimica e Industrias Extractivas, Av. Instituto Politecnico Nacional s/n, Edif. 6, 07738 Mexico D. F. (Mexico); Kryvko, A., E-mail: marloz7@yahoo.com.mx [IPN, Escuela Superior de Ingenieria Mecanica y Electrica, Departamento de Sistemas, Av. Instituto Politecnico Nacional s/n, Edif. Z-4, 07738 Mexico D. F. (Mexico)

    2013-06-01

    Ni{sub x}Mg{sub 1-x}O oxides were prepared by thermal treatment at temperatures of 400, 600 and 800 C from a hydrotalcite-like precursor obtained by co-precipitation at constant ph. The oxides obtained were characterized by X-ray diffraction methods. From the obtained results we concluded that the oxides calcined at temperatures of 400, and 600 C are unstable that means that there exists the effect of memory and with a time they return to the precursor. Presence of Ni in Mg oxide provides stability of the compounds thermally treated at 800 C. In order to analyze the structure and microstructure, the reflections 111, 200 and 220 were used. The positions of the maxima of the diffraction peaks are shifted with respect to the simulated ones for Mg O and Ni O. This result reveals that in solid solutions studied compressive strains or vacation are present. The parameters of the microstructure (coherent domain size and micro deformations) were evaluated. The coherent domain size was found to be in the range of 8 - 10 nm and the presence of residual strains of micro deformation can be associated with the existence of extended defects. (Author)

  15. Microstructure and annealing behavior of a modified 9Cr−1Mo steel after dynamic plastic deformation to different strains

    International Nuclear Information System (INIS)

    Zhang, Z.B.; Mishin, O.V.; Tao, N.R.; Pantleon, W.

    2015-01-01

    The microstructure, hardness and tensile properties of a modified 9Cr−1Mo steel processed by dynamic plastic deformation (DPD) to different strains (0.5 and 2.3) have been investigated in the as-deformed and annealed conditions. It is found that significant structural refinement and a high level of strength can be achieved by DPD to a strain of 2.3, and that the microstructure at this strain contains a large fraction of high angle boundaries. The ductility of the DPD processed steel is however low. Considerable structural coarsening of the deformed microstructure without pronounced recrystallization takes place during annealing of the low-strain and high-strain samples for 1 h at 650 °C and 600 °C, respectively. Both coarsening and partial recrystallization occur in the high-strain sample during annealing at 650 °C for 1 h. For this sample, it is found that whereas coarsening alone results in a loss of strength with only a small gain in ductility, coarsening combined with pronounced partial recrystallization enables a combination of appreciably increased ductility and comparatively high strength

  16. Diesel soot oxidation under controlled conditions

    OpenAIRE

    Song, Haiwen

    2003-01-01

    This thesis was submitted for the degree of Doctor of Philosophy and awarded by Brunel University, 11/12/2003. In order to improve understanding of diesel soot oxidation, an experimental rig was designed and set up, in which the soot oxidation conditions, such as temperature, oxygen partial pressure, and CO2 partial pressure, could be varied independently of each other. The oxidizing gas flow in the oxidizer was under laminar condition. This test rig comprised a naturally-aspirated single ...

  17. Microstructural degradation of Ni-YSZ anodes for solid oxide fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Thyden, K.

    2008-03-15

    Ni-YSZ cermets have been used as anode materials in SOFCs for more than 20 years. Despite this fact, the major cause of degradation within the Ni-YSZ anode, namely Ni sintering / coarsening, is still not fully understood. Even if microstructural studies of anodes in tested cells are of technological relevance, it is difficult to identify the effect from isolated parameters such as temperature, fuel gas composition and polarization. Model studies of high temperature aged Ni-YSZ cermets are generally performed in atmospheres containing relatively low concentrations of H2O. In this work, the microstructural degradation in both electrochemically longterm tested cells and high-temperature aged model materials are studied. Since Ni particle sintering / coarsening is attributed to be the major cause of anode degradation, this subject attains the primary focus. A large part of the work is focused on improving microstructural techniques and shows that the application of low acceleration voltages (<= 1 kV) in a FE-SEM makes it possible to obtain two useful types of contrast between the phases in Ni-YSZ composites. By changing between the ordinary lateral SE detector and the inlens detector, using similar microscope settings, two very different sample characteristics are probed: 1) The difference in secondary emission coefficient, delta, between the percolating and non-percolating Ni is maximized in the low-voltage range due to a high delta for the former and the suppression of delta by a positive charge for the latter. This difference yields a contrast between the two phases which is picked up by an inlens secondary electron detector. 2) The difference in backscatter coefficient, eta, between Ni and YSZ is shown to increase with decreasing voltage. The contrast is illustrated in images collected by the normal secondary detector since parts of the secondary signals are generated by backscattered electrons. High temperature aging experiments of model Ni-YSZ anode cermets show

  18. Microstructure and superconducting properties of YBCO bulk superconductors with RE substitutions

    Czech Academy of Sciences Publication Activity Database

    Volochová, D.; Antal, V.; Piovarči, S.; Kováč, J.; Jirsa, Miloš; Noudem, J.; Diko, P.

    2016-01-01

    Roč. 26, č. 3 (2016), s. 1-4, č. článku 7200604. ISSN 1051-8223 Institutional support: RVO:68378271 Keywords : yttrium barium copper oxide * critical current density (superconductivity) * powders * magnetic fields * microstructure * temperature measurement Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.092, year: 2015

  19. Microstructure and wear-resistance of laser clad TiC particle-reinforced coating

    NARCIS (Netherlands)

    Lei, T.C.; Ouyang, J.H.; Pei, Y.T.; Zhou, Y.

    A TiC-Ni alloy composite coating was clad to 1045 steel substrate using a 2kW CO2 laser. The microstructural constituents of the clad layer are found to be gamma-Ni and TiCp in the dendrites, and a fine eutectic of gamma-Ni plus (Fe, Cr)(23)C-6 in the interdendritic areas. Partial dissolution and

  20. Review of theoretical conceptions on regimes of oxidation and hydrogen pickup in Zr-alloys

    International Nuclear Information System (INIS)

    Likhanskii, V.; Evdokimov, I.

    2008-01-01

    In this paper the following issues are presented: 1) Experimental observations published in the journals on corrosion regimes of zirconium alloys of various compositions both for ex-pile oxidation experiments and for in-pile operating conditions of the materials. Factors experimentally stated on the effect of alloying composition, microstructure and texture on the rate of uniform corrosion and susceptibility of alloys to nodular corrosion. 2) Phenomenological models existing in publications, which describe conditions of uniform and nodular corrosion for Zr-alloys of various composition and microstructures, effect of irradiation and oxidizing medium; 3) Experimental data and phenomenological models describing regimes of hydrogen absorption in zirconium alloys; 4) Examples of application of physical models in explaining regimes, peculiarities of oxidation and hydrogen pickup for zirconium claddings of various alloying composition and microstructure

  1. Absorption of calcium ions on oxidized graphene sheets and study its dynamic behavior by kinetic and isothermal models

    Directory of Open Access Journals (Sweden)

    Mahmoud Fathy

    2016-07-01

    Full Text Available Abstract Sorption of calcium ion from the hard underground water using novel oxidized graphene (GO sheets was studied in this paper. Physicochemical properties and microstructure of graphene sheets were investigated using Raman spectrometer, thermogravimetry analyzer, transmission electron microscope, scanning electron microscope. The kinetics adsorption of calcium on graphene oxide sheets was examined using Lagergren first and second orders. The results show that the Lagergren second-order was the best-fit model that suggests the conception process of calcium ion adsorption on the Go sheets. For isothermal studies, the Langmuir and Freundlich isotherm models were used at temperatures ranging between 283 and 313 K. Thermodynamic parameters resolved at 283, 298 and 313 K indicating that the GO adsorption was exothermic spontaneous process. Finally, the graphene sheets show high partiality toward calcium particles and it will be useful in softening and treatment of hard water.

  2. Plasma arc cutting: Microstructural modifications of hafnium cathodes during first cycles

    Energy Technology Data Exchange (ETDEWEB)

    Rotundo, F., E-mail: fabio.rotundo@unibo.it [Dept. of Mechanical Engineering (DIEM), Alma Mater Studiorum, Universita di Bologna, Via Saragozza 8, 40123 Bologna (Italy); Martini, C.; Chiavari, C.; Ceschini, L. [Dept. of Metals Science, Electrochemistry and Chemical Techniques (SMETEC), Alma Mater Studiorum, Universita di Bologna, Viale Risorgimento 4, 40136 Bologna (Italy); Concetti, A.; Ghedini, E.; Colombo, V. [Dept. of Mechanical Engineering (DIEM), Alma Mater Studiorum, Universita di Bologna, Via Saragozza 8, 40123 Bologna (Italy); Dallavalle, S. [Cebora S.p.A., Via Andrea Costa 24, 40057 Cadriano di Granarolo (Italy)

    2012-06-15

    In the present work, the microstructural modifications of the Hf insert in plasma arc cutting (PAC) electrodes operating at 250 A were experimentally investigated during first cycles, in order to understand those phenomena occurring on and under the Hf emissive surface and involved in the electrode erosion process. Standard electrodes were subjected to an increasing number of cutting cycles (CCs) on mild steel plates in realistic operative conditions, with oxygen/air as plasma/shield gas. Microstructural analysis was performed for each electrode at different erosion stages by means of scanning electron microscopy (SEM) equipped with energy dispersive spectroscopy (EDS) and Raman spectroscopy. Electrodes cross sections were also observed by means of optical microscopy (both in bright field and in reflected polarised light) after chemical etching. In the insert, three typical zones were found after cutting: monoclinic HfO{sub 2} layer; thermally-modified transition zone with O{sub 2}-Hf solid solution; unmodified Hf. The erosion cavity and the oxide layer thickness increase with the number of cutting cycles. Macrocracking was observed in the oxide layer, while microcracking and grain growth were detected in the remelted Hf. Moreover, detachment was found at the Hf/Cu interface. Based on thermodynamics and kinetics of the Hf high temperature oxidation, conclusions can be drawn on the erosion mechanism involved. - Highlights: Black-Right-Pointing-Pointer Hf microstructural modifications in cathodes after plasma arc cutting cycles investigated. Black-Right-Pointing-Pointer 3 zones identified after cutting: HfO{sub 2} layer; remelted zone with O{sub 2}-Hf solid solution; unmodified Hf. Black-Right-Pointing-Pointer Hf-based ejections both in arc-on and arc-off phases; erosion cavity deepens with cutting cycles. Black-Right-Pointing-Pointer Detachment at the Hf/Cu interfaces, worsening heat dissipation and oxidation/erosion phenomena. Black-Right-Pointing-Pointer The use

  3. Surface chemistry and microstructure of metallic biomaterials for hip and knee endoprostheses

    Science.gov (United States)

    Jenko, Monika; Gorenšek, Matevž; Godec, Matjaž; Hodnik, Maxinne; Batič, Barbara Šetina; Donik, Črtomir; Grant, John T.; Dolinar, Drago

    2018-01-01

    The surface chemistry and microstructures of titanium alloys (both new and used) and CoCrMo alloys used for hip and knee endoprostheses were determined using SEM (morphology), EBSD (phase analysis), AES and XPS (surface chemistry). Two new and two used endoprostheses were studied. The SEM SE and BE images showed their microstructures, while the EBSD provided the phases of the materials. During the production of the hip and knee endoprostheses, these materials are subject to severe thermomechanical treatments and physicochemical processes that are decisive for CoCrMo alloys. The AES and XPS results showed that thin oxide films on (a) Ti6Al4V are primarily a mixture of TiO2 with a small amount of Al2O3, while the V is depleted, (b) Ti6Al7Nb is primarily a mixture of TiO2 with a small amount of Al2O3 and Nb2O5, and (c) the CoCrMo alloy is primarily a mixture of Cr2O3 with small amounts of Co and Mo oxides. The thin oxide film on the CoCrMo alloy should prevent intergranular corrosion and improve the biocompatibility. The thin oxide films on the Ti alloys prevent further corrosion, improve the biocompatibility, and affect the osseointegration.

  4. Microstructure taxonomy based on spatial correlations: Application to microstructure coarsening

    International Nuclear Information System (INIS)

    Fast, Tony; Wodo, Olga; Ganapathysubramanian, Baskar; Kalidindi, Surya R.

    2016-01-01

    To build materials knowledge, rigorous description of the material structure and associated tools to explore and exploit information encoded in the structure are needed. These enable recognition, categorization and identification of different classes of microstructure and ultimately enable to link structure with properties of materials. Particular interest lies in the protocols capable of mining the essential information in large microstructure datasets and building robust knowledge systems that can be easily accessed, searched, and shared by the broader materials community. In this paper, we develop a protocol based on automated tools to classify microstructure taxonomies in the context of coarsening behavior which is important for long term stability of materials. Our new concepts for enhanced description of the local microstructure state provide flexibility of description. The mathematical description of microstructure that capture crucial attributes of the material, although central to building materials knowledge, is still elusive. The new description captures important higher order spatial information, but at the same time, allows down sampling if less information is needed. We showcase the classification protocol by studying coarsening of binary polymer blends and classifying steady state structures. We study several microstructure descriptions by changing the microstructure local state order and discretization and critically evaluate their efficacy. Our analysis revealed the superior properties of microstructure representation is based on the first order-gradient of the atomic fraction.

  5. Measurement of the oxidation of spent fuel between 140/degree/ and 225/degree/C by thermogravimetric analysis

    International Nuclear Information System (INIS)

    Woodley, R.E.; Einziger, R.E.; Buchanan, H.C.

    1988-09-01

    A series of PWR spent fuel samples from Turkey Point Unit 3 have been oxidized at temperatures between 140/degree/ and 225/degree/C in air atmospheres with dew points between 14.5/degree/ and /minus/70/degree/C, using a thermogravimetric analysis system (TGA). Tests lasted between 400 and 2100 hours. At the conclusion of a test, the atmosphere was sampled to determine the release of fission gas during testing, and the fuel samples were analyzed for microstructural changes. It appears that the mechanism for oxidation of spent fuel to U/sub 3/O/sub 7/ takes place in two steps that occur somewhat simultaneously. Oxygen migrates along the grain boundaries, which are oxidized and enlarged. The grains oxidize by the inward progression of a layer of U/sub 4/O/sub 9/ saturated with oxygen. A simplified model of the mechanism, which considers oxygen diffusion through the product layer as the rate-controlling step, yields an activation energy of 27 /plus minus/ 4 kcal/mol. Moisture, between dew points of /minus/70/degree/ to +14.5/degree/C, i.e., water vapor partial pressures varying over four orders of magnitude, had no significant effect on the oxidation rate. 34 refs., 12 figs., 6 tabs

  6. Effect of systemic nitric oxide synthase inhibition on optic disc oxygen partial pressure in normoxia and in hypercapnia.

    Science.gov (United States)

    Petropoulos, Ioannis K; Pournaras, Jean-Antoine C; Stangos, Alexandros N; Pournaras, Constantin J

    2009-01-01

    To investigate the effect of systemic nitric oxide synthase (NOS) inhibition on optic disc oxygen partial pressure (PO(2)) in normoxia and hypercapnia. Intervascular optic disc PO(2) was measured in 12 anesthetized minipigs by using oxygen-sensitive microelectrodes placed 0.1), despite a 21% increase of mean arterial pressure. Optic disc PO(2) increase under hypercapnia was blunted after L-NAME injection (DeltaPO(2) = 0.6 +/- 1.1 mm Hg; 3%; P > 0.1), and this effect was reversible by L-arginine. Moreover, L-NAME reduced the response to carbogen by 29% (DeltaPO(2) = 9.1 +/- 4.4 mm Hg; 49%; P = 0.01 versus before L-NAME). The response to hyperoxia was not affected. Whereas systemic NOS inhibition did not affect optic disc PO(2) in normoxia, a blunting effect was noted on the CO(2)-induced optic disc PO(2) increase. Nitric oxide appears to mediate the hypercapnic optic disc PO(2) increase.

  7. Oxidation and creep behaviour of dense silicon nitride materials with different compositions

    International Nuclear Information System (INIS)

    Ernstberger, U.

    1985-09-01

    The study was intended to yield information on the oxidation and creep behaviour of Si 3 N 4 materials of different composition and microstructure, and produced by different processes. The experiments carried out in a vast temperature and load range showed that the chemical grain boundary composition is the key parameter affecting the materials' high-temperature properties. Significant correlations could be established between oxidation and creep behaviour on the one hand, and between microstructure and the behaviour on the other. (orig./IHOE) [de

  8. Catalyst development and systems analysis of methanol partial oxidation for the fuel processor - fuel cell integration

    Energy Technology Data Exchange (ETDEWEB)

    Newson, E; Mizsey, P; Hottinger, P; Truong, T B; Roth, F von; Schucan, Th H [Paul Scherrer Inst. (PSI), Villigen (Switzerland)

    1999-08-01

    Methanol partial oxidation (pox) to produce hydrogen for mobile fuel cell applications has proved initially more successful than hydrocarbon pox. Recent results of catalyst screening and kinetic studies with methanol show that hydrogen production rates have reached 7000 litres/hour/(litre reactor volume) for the dry pox route and 12,000 litres/hour/(litre reactor volume) for wet pox. These rates are equivalent to 21 and 35 kW{sub th}/(litre reactor volume) respectively. The reaction engineering problems remain to be solved for dry pox due to the significant exotherm of the reaction (hot spots of 100-200{sup o}C), but wet pox is essentially isothermal in operation. Analyses of the integrated fuel processor - fuel cell systems show that two routes are available to satisfy the sensitivity of the fuel cell catalysts to carbon monoxide, i.e. a preferential oxidation reactor or a membrane separator. Targets for individual system components are evaluated for the base and best case systems for both routes to reach the combined 40% efficiency required for the integrated fuel processor - fuel cell system. (author) 2 figs., 1 tab., 3 refs.

  9. Thermally stimulated iron oxide transformations and magnetic behaviour of cerium dioxide/iron oxide reactive sorbents

    Energy Technology Data Exchange (ETDEWEB)

    Luňáček, J., E-mail: jiri.lunacek@vsb.cz [Department of Physics, VŠB – Technical University of Ostrava, 17, listopadu 15/2172, 708 33 Ostrava-Poruba (Czech Republic); Department 606, VŠB – Technical University of Ostrava, 17, listopadu 15/2172, 708 33 Ostrava-Poruba (Czech Republic); Životský, O. [Department of Physics, VŠB – Technical University of Ostrava, 17, listopadu 15/2172, 708 33 Ostrava-Poruba (Czech Republic); Department 606, VŠB – Technical University of Ostrava, 17, listopadu 15/2172, 708 33 Ostrava-Poruba (Czech Republic); Jirásková, Y. [CEITEC IPM, Institute of Physics of Materials, Academy of Sciences of the Czech Republic, Žižkova 22, 616 62 Brno (Czech Republic); Institute of Physics of Materials, Academy of Sciences of the Czech Republic, Žižkova 22, 616 62 Brno (Czech Republic); Buršík, J. [Institute of Physics of Materials, Academy of Sciences of the Czech Republic, Žižkova 22, 616 62 Brno (Czech Republic); Janoš, P. [Faculty of the Environment, University of Jan Evangelista Purkyně, Králova Výšina 7, 400 96 Ústí nad Labem (Czech Republic)

    2016-10-15

    The present paper is devoted to detailed study of the magnetically separable sorbents based on a cerium dioxide/iron oxide composite annealed at temperatures T{sub a} = 773 K, 873 K, and 973 K. The X-ray diffraction and high resolution transmission electron microscopy are used to determine the phase composition and microstructure morphology. Mössbauer spectroscopy at room (300 K) and low (5 K) temperatures has contributed to more exact identification of iron oxides and their transformations Fe{sub 3}O{sub 4} → γ-Fe{sub 2}O{sub 3} (ε-Fe{sub 2}O{sub 3}) → α-Fe{sub 2}O{sub 3} in dependence on calcination temperature. Different iron oxide phase compositions and grain size distributions influence the magnetic characteristics determined from the room- and low-temperature hysteresis loop measurements. The results are supported by zero-field-cooled and field-cooled magnetization measurements allowing a quantitative estimation of the grain size distribution and its effect on the iron oxide transformations. - Highlights: •Magnetically separable sorbents based on a CeO{sub 2}/Fe{sub 2}O{sub 3} composite were investigated. •Microstructure of sorbents was determined by XRD, TEM and Mössbauer spectroscopy. •Magnetic properties were studied by hysteresis loops at room- and low-temperatures. •Phase transitions of iron oxides with increasing annealing temperature are observed.

  10. Microstructural Investigations of Al2O3 Scale Formed on FeCrAl Steel during High Temperature Oxidation in SO2

    International Nuclear Information System (INIS)

    Homa, M.; Zurek, Z.; Morgiel, B.; Zieba, P.; Wojewoda, J.

    2008-01-01

    The results of microstructure observations of the Al 2 O 3 scale formed on a Fe-Cr-Al steel during high temperature oxidation in the SO 2 atmosphere are presented. Morphology of the scale has been studied by SEM and TEM techniques. Phase and chemical compositions have been studied by EDX and XRD techniques. The alumina oxide is a primary component of the scale. TEM observations showed that the scale was multilayer. The entire surface of the scale is covered with 'whiskers, which look like very thin platelets and have random orientation. The cross section of a sample shows, that the 'whiskers' are approximately 2 μm high, however the compact scale layer on which they reside is 0.2 μm thick. The scale layer was composed mainly of small equiaxial grains and a residual amount of small columnar grains. EDX analysis of the scale surface showed that the any sulfides were found in the formed outer and thin inner scale layer. A phase analysis of the scale formed revealed that it is composed mainly of the θ-Al 2 O 3 phase and a residual amount of α-Al 2 O 3

  11. Characterization of Nano Sized Microstructures in Fe and Ni Base ODS Alloys Using Small Angle Neutron Scattering

    International Nuclear Information System (INIS)

    Han, Young-Soo; Jang, Jin-Sung; Mao, Xiaodong

    2015-01-01

    Ferritic ODS(Oxide-dispersion-strengthened) alloy is known as a primary candidate material of the cladding tubes of a sodium fast reactor (SFR) in the Generation IV research program. In ODS alloy, the major contribution to the enhanced high-temperature mechanical property comes from the existence of nano-sized oxide precipitates, which act as obstacles to the movement of dislocations. In addition for the extremely high temperature application(>950 .deg. C) of future nuclear system, Ni base ODS alloys are considered as candidate materials. Therefore the characterization of nano-sized microstructures is important for determining the mechanical properties of the material. Small angle neutron scattering (SANS) technique non-destructively probes structures in materials at the nano-meter length of scale (1 - 1000 nm) and has been a very powerful tool in a variety of scientific/engineering research areas. In this study, nano-sized microstructures were quantitatively analyzed by small angle neutron scattering. Quantitative microstructural information on nanosized oxide in ODS alloys was obtained from SANS data. The effects of the thermo mechanical treatment on the size and volume fraction of nano-sized oxides were analyzed. For 12Cr ODS alloy, the experimental A-ratio is two-times larger than the theoretical A-ratio., and this result is considered to be due to the imperfections included in YTaO 4 . For Ni base ODS alloy, the volume fraction of the mid-sized particles (- 30 nm) increases rapidly as hot extrusion temperature decreases

  12. Origin of the visible emission of black silicon microstructures

    International Nuclear Information System (INIS)

    Fabbri, Filippo; Lin, Yu-Ting; Bertoni, Giovanni; Rossi, Francesca; Salviati, Giancarlo; Smith, Matthew J.; Gradečak, Silvija; Mazur, Eric

    2015-01-01

    Silicon, the mainstay semiconductor in microelectronics, is considered unsuitable for optoelectronic applications due to its indirect electronic band gap that limits its efficiency as light emitter. Here, we univocally determine at the nanoscale the origin of visible emission in microstructured black silicon by cathodoluminescence spectroscopy and imaging. We demonstrate the formation of amorphous silicon oxide microstructures with a white emission. The white emission is composed by four features peaking at 1.98 eV, 2.24 eV, 2.77 eV, and 3.05 eV. The origin of such emissions is related to SiO x intrinsic point defects and to the sulfur doping due to the laser processing. Similar results go in the direction of developing optoelectronic devices suitable for silicon-based circuitry

  13. Softlithographic partial integration of surface-active nanoparticles in a PDMS matrix for microfluidic biodevices

    Energy Technology Data Exchange (ETDEWEB)

    Demming, Stefanie; Buettgenbach, Stephanus [Institute for Microtechnology (IMT), Technische Universitaet Braunschweig, Alte Salzdahlumer Strasse 203, 38124 Braunschweig (Germany); Hahn, Anne; Barcikowski, Stephan [Nanotechnology Department, Laser Zentrum Hannover e.V. (LZH), Hollerithallee 8, 30419 Hannover (Germany); Edlich, Astrid; Franco-Lara, Ezequiel; Krull, Rainer [Institute of Biochemical Engineering (IBVT), Technische Universitaet Braunschweig, Gaussstrasse 17, 38106 Braunschweig (Germany)

    2010-04-15

    The mergence of microfluidics and nanocomposite materials and their in situ structuring leads to a higher integration level within microsystems technology. Nanoparticles (Cu and Ag) produced via laser radiation were suspended in Poly(dimethylsiloxane) to permanently modify surface material. A microstructuring process was implemented which allows the incorporation of these nanomaterials globally or partially at defined locations within a microbioreactor (MBR) for the determination of their antiseptic and toxic effects on the growth of biomass. Partially structured PDMS with nanoparticle-PDMS composite. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

  14. Effect of current density on the microstructure and corrosion resistance of microarc oxidized ZK60 magnesium alloy.

    Science.gov (United States)

    You, Qiongya; Yu, Huijun; Wang, Hui; Pan, Yaokun; Chen, Chuanzhong

    2014-09-01

    The application of magnesium alloys as biomaterials is limited by their poor corrosion behavior. Microarc oxidation (MAO) treatment was used to prepare ceramic coatings on ZK60 magnesium alloys in order to overcome the poor corrosion resistance. The process was conducted at different current densities (3.5 and 9.0 A/dm(2)), and the effect of current density on the process was studied. The microstructure, elemental distribution, and phase composition of the MAO coatings were characterized by scanning electron microscopy, energy-dispersive x-ray spectrometry, and x-ray diffraction, respectively. The increment of current density contributes to the increase of thickness. A new phase Mg2SiO4 was detected as the current density increased to 9.0 A/dm(2). A homogeneous distribution of micropores could be observed in the coating produced at 3.5 A/dm(2), while the surface morphology of the coating formed at 9.0 A/dm(2) was more rough and apparent microcracks could be observed. The coating obtained at 3.5 A/dm(2) possessed a better anticorrosion behavior.

  15. Effect of Mass-Transport Limitations on the Performance of a Packed Bed Membrane Reactor for Partial Oxidations. Transport from the Membrane to the Packed Bed

    NARCIS (Netherlands)

    van Sint Annaland, M.; Kurten, U.; Kuipers, J.A.M.

    2007-01-01

    With a packed bed membrane reactor, the product yield can be significantly enhanced for partial oxidation systems, via distributive addition of oxygen to the reaction mixture along the axial coordinate of the reactor, provided that the reaction order in oxygen of the formation rate of the target

  16. Effect of mass-transport limitations on the performance of a packed bed membrane reactor for partial oxidations. Transport from the membrane to the packed bed

    NARCIS (Netherlands)

    Sint Annaland, van M.; Kurten, U.; Kuipers, J.A.M.

    2007-01-01

    With a packed bed membrane reactor, the product yield can be significantly enhanced for partial oxidation systems, via distributive addition of oxygen to the reaction mixture along the axial coordinate of the reactor, provided that the reaction order in oxygen of the formation rate of the target

  17. Poly(propylene carbonate): Insight into the Microstructure and Enantioselective Ring-Opening Mechanism

    KAUST Repository

    Salmeia, Khalifah A.

    2012-11-13

    Different poly(propylene carbonate) (PPC) microstructures have been synthesized from the alternating copolymerization of CO 2 with both racemic propylene oxide (PO) and various mixtures of PO enantiomers using chiral salen catalysts. The microstructures of the obtained copolymers as a function of polymerization time have been analyzed by a combination of chiral GC and high-resolution NMR spectroscopy. The 13C NMR spectra of selected poly(propylene carbonate) samples were recorded using a 900 MHz ( 1H) spectrometer, showing a previously unreported fine splitting of the carbonate resonances. This allowed a detailed assignment of signals for various copolymer microstructures taking into account the specifics in their stereo- and regioirregularities. For example, the enantioselectivity preference of the (R,R-salen)Co catalyst for (S)-PO at the beginning of the copolymerization leads predominantly to (S)-PO insertion, with any (R)-PO misinsertion being followed by incorporation of (S)-PO, so that the microstructure features isolated stereoerrors. K rel calculations for the copolymerization showed around 5-fold enantioselectivity for (S)-PO over (R)-PO at short reaction time. Analysis of the copolymer microstructures obtained under various reaction conditions appears to be an additional approach to differentiate the occurrence of bimetallic and bifunctional copolymerization mechanisms that are widely discussed in the literature. © 2012 American Chemical Society.

  18. Poly(propylene carbonate): Insight into the Microstructure and Enantioselective Ring-Opening Mechanism

    KAUST Repository

    Salmeia, Khalifah A.; Vagin, Sergei; Anderson, Carly E.; Rieger, Bernhard

    2012-01-01

    Different poly(propylene carbonate) (PPC) microstructures have been synthesized from the alternating copolymerization of CO 2 with both racemic propylene oxide (PO) and various mixtures of PO enantiomers using chiral salen catalysts. The microstructures of the obtained copolymers as a function of polymerization time have been analyzed by a combination of chiral GC and high-resolution NMR spectroscopy. The 13C NMR spectra of selected poly(propylene carbonate) samples were recorded using a 900 MHz ( 1H) spectrometer, showing a previously unreported fine splitting of the carbonate resonances. This allowed a detailed assignment of signals for various copolymer microstructures taking into account the specifics in their stereo- and regioirregularities. For example, the enantioselectivity preference of the (R,R-salen)Co catalyst for (S)-PO at the beginning of the copolymerization leads predominantly to (S)-PO insertion, with any (R)-PO misinsertion being followed by incorporation of (S)-PO, so that the microstructure features isolated stereoerrors. K rel calculations for the copolymerization showed around 5-fold enantioselectivity for (S)-PO over (R)-PO at short reaction time. Analysis of the copolymer microstructures obtained under various reaction conditions appears to be an additional approach to differentiate the occurrence of bimetallic and bifunctional copolymerization mechanisms that are widely discussed in the literature. © 2012 American Chemical Society.

  19. Mechanical and microstructural behavior of oxide dispersion strengthened 8Cr-2W and 8Cr-1W steels during creep deformation

    Energy Technology Data Exchange (ETDEWEB)

    Shinozuka, K.; Tamura, M.; Esaka, H. [National Defense Academy, Dept. MS and E, Kanagawa (Japan); Shiba, K.; Nakamura, K. [Japan Atomic Energy Agency, Tokai-mura, Naga-gun, Ibaraki-ken (Japan)

    2007-07-01

    Full text of publication follows: Oxide dispersion strengthened (ODS) steel is a promising candidate for fusion reactor material because of excellent mechanical properties. However, the ODS steel exhibits some defects, such as mechanical anisotropy and little elongation . To reveal details of these defects, we investigated correlations between mechanical and microstructural behavior of ODS ferritic steels during creep deformation at high temperature. The materials used in this study are two kinds of hot rolled ODS steels: Fe-8Cr-2W-0.2V-0.1Ta-0.2Ti-0.4Y{sub 2}O{sub 3} (J1) and Fe-8Cr-1W-0.2Ti-0.4Y{sub 2}O{sub 3} (J2). Creep tests was carried out on specimens sampling along both the rolling direction and the cross direction at 670, 700 and 730 deg. C. Microstructural analyses were made on the normalized and tempered condition by using OM, SEM, TEM and XRD. Creep ruptured and interrupted specimens were also investigated. Both J1 and J2 existed two phases, namely martensite and {delta}-ferrite which was elongated in the rolling direction. Y-Ti complex oxide particles were finely dispersed in martensite and {delta}- ferrite phases. Results of creep tests indicated that the time-to-rupture of specimens of J1 were much longer than J2, and the time-to-rupture of specimens sampling along the rolling direction were longer than cross direction. Accordingly, J1 sampling along hot rolling direction was the strongest, for instance, the time-to-rupture was 11400 h at 700 deg. C and 162 MPa. All specimens indicated that elongation was less than 1.3 % and the rupture occurred at steady state creep region from creep curves. Internal cracks were propagated in martensite phase along elongated {delta}-ferrite phase in the direction of hot rolling. On the other hand, {delta}-ferrite phases seemed to prevent combining cracks. These results suggest that elongated {delta}-ferrite and internal clacks in martensite strongly affect on the anisotropy and little elongation of creep. (authors)

  20. Aligned poly(ε-caprolactone)/graphene oxide and reduced graphene oxide nanocomposite nanofibers: Morphological, mechanical and structural properties.

    Science.gov (United States)

    Ramazani, Soghra; Karimi, Mohammad

    2015-11-01

    A number of studies have demonstrated that the mechanical properties of electrospun polymeric nanofibrous scaffolds are enhanced with the incorporation of graphene and its derivatives, thus developing their applications in hard tissue engineering. However, our understanding of the relationship between the microstructure and properties of these fibrous scaffolds and how they are influenced by graphene oxide (GO) and reduced graphene oxide (RGO) loading is much more limited. Thus, in this paper, poly(ε-caprolactone) (PCL)/GO and RGO nanocomposite nanofibers containing 0, 0.1, 0.5 and 1wt.% GO and RGO were prepared using an electrospinning technique. With the addition of 0.1wt.% of GO and RGO nanosheets in PCL, the tensile strength of PCL scaffolds increased over ~160 and 304% respectively and elastic modulus increased over 103 and 163% due to the good dispersion of the nanosheets and their interaction with the molecular chains of PCL. These were supported by the parallel increase in relaxation time and molecular orientation of PCL chains at the presence of nanosheets with a loading of 0.1wt.%. The enhancement effect of the nanosheets was weakened with an increase in GO and RGO loading up to 1wt.% in which it is connected to a partial exfoliation of the nanosheets. Copyright © 2015 Elsevier B.V. All rights reserved.

  1. 3D Microstructural Architectures for Metal and Alloy Components Fabricated by 3D Printing/Additive Manufacturing Technologies

    Science.gov (United States)

    Martinez, E.; Murr, L. E.; Amato, K. N.; Hernandez, J.; Shindo, P. W.; Gaytan, S. M.; Ramirez, D. A.; Medina, F.; Wicker, R. B.

    The layer-by-layer building of monolithic, 3D metal components from selectively melted powder layers using laser or electron beams is a novel form of 3D printing or additive manufacturing. Microstructures created in these 3D products can involve novel, directional solidification structures which can include crystallographically oriented grains containing columnar arrays of precipitates characteristic of a microstructural architecture. These microstructural architectures are advantageously rendered in 3D image constructions involving light optical microscopy and scanning and transmission electron microscopy observations. Microstructural evolution can also be effectively examined through 3D image sequences which, along with x-ray diffraction (XRD) analysis in the x-y and x-z planes, can effectively characterize related crystallographic/texture variances. This paper compares 3D microstructural architectures in Co-base and Ni-base superalloys, columnar martensitic grain structures in 17-4 PH alloy, and columnar copper oxides and dislocation arrays in copper.

  2. Thermal stability of the microstructure of an aged Nb-Zr-C alloy

    Science.gov (United States)

    Uz, Mehmet; Titran, Robert H.

    1991-01-01

    The effects of thermal aging with and without an applied stress on the microstructure of a Nb-Zr-C alloy containing 0.9 wt percent Zr and 0.06 percent C were studied. Chemical analysis, metallographic examination, energy dispersive X-ray spectra of the bulk material, and chemical and X-ray analyses of the phase-extracted residue were used to characterize the microstructure. The samples examined were from a creep strength study involving hot and cold working, and various combinations of exposure to temperatures ranging from 1350 to 1755 K with and without applied load times as long as 34,000 plus hours. The results showed that the initial microstructure consisted primarily of orthorombic precipitates of Nb sub C which were partially or completely transformed to face-centered cubic carbides of Nb and Zr, (Zr, Nb)C, upon prolonged exposure to elevated temperatures. Furthermore, it was found that the microstructure of the alloy is extremely stable owing to the very finely distributed precipitates throughout its matrix and along the grain boundaries. The lattice parameters of the cubic carbides were determined to vary from 0.458 to 0.465 nm as the Zr/Nb ratio varied from 38/62 to 75/25.

  3. Thermal stability of the microstructure of an aged Nb-Zr-C alloy

    International Nuclear Information System (INIS)

    Uz, M.; Titran, R.H.

    1991-01-01

    The effects of thermally aging with and without an applied stress on the microstructure of a Nb-Zr-C alloy containing 0.9 wt % Zr and 0.06 wt % C were studied. Chemical analysis, metallographic examination, energy dispersive x-ray spectra of the bulk material, and chemical and x-ray analyses of the phase-extracted residue were used to characterize the microstructure. The samples examined were from a creep strength study involving hot and cold working, and various combinations of exposure to temperatures ranging from 1350 to 1755 K with and without applied load for times as long as 34,000 plus hours. The results showed that the initial microstructure consisted primarily of orthorhombic precipitates of Nb 2 C which were partially or completely transformed to face-centered cubic carbides of Nb and Zr, (Zr,Nb)C, upon prolonged exposure to elevated temperatures. Furthermore, it was found that the microstructure of the alloy is extremely stable owing to the very finely distributed precipitates throughout its matrix and along the grain boundaries. The lattice parameters of the cubic carbides were determined to vary from 0.458 to 0.465 nm as the Zr/Nb ratio varied from 38/62 to 75/25. 25 refs., 5 figs., 4 tabs

  4. CO2 separation by calcium looping from full and partial fuel oxidation processes

    International Nuclear Information System (INIS)

    Sivalingam, Senthoorselvan

    2013-01-01

    This thesis work deals with the research and development of calcium looping process for CO 2 separation from full and partial fuel oxidation based power generation systems. CO 2 is the main greenhouse gas and undoubtedly a major contributor to the global warming. It is estimated that more than one third of the total anthropogenic CO 2 emissions come from fossil fuel based heat and power generation. Moreover, fossil fuels are unlikely to be phased out rapidly, since developing alternative energy sources not only take time but also require huge investments and infrastructure. An alternative way to reduce emissions in a medium term is to capture the CO 2 from fossil fueled power plants and store it away from the atmosphere. This process system combining a bunch of technologies is called carbon capture and storage (CCS). CO 2 capture is an important and costly part of CCS and an array of technologies is considered for this. Calcium looping (CaL) is one of such and seems to offer effective and efficient CO 2 separation from fuel oxidation processes. CaL process involves separation of CO 2 at high temperatures (600-700 C) by calcium sorbents (CaO). CO 2 reacts with CaO in a carbonation process and produces CaCO 3 . In a subsequent thermal regeneration (>850 C) called calcination, the CO 2 is released from CaCO 3 . By alternating carbonations and calcinations over multiple cycles, CO 2 is separated from a gas stream. Moreover, the CaL is realised in industrial scale with dual fluidised bed reactors for CO 2 capture (the carbonator) and sorbent regeneration (the calciner). As a process in the development, research is still required in many aspects from thermodynamic modeling to experimental studies. Research works have been carried out in process simulations, sorbent reactivity and optimisation studies in a controlled reactor environment and process parametric studies in a semi-pilot scale CaL test facility. ASPEN Plus power plant simulations integrating the CaL based CO 2

  5. Microstructural Changes during High Temperature Service of a Cobalt-Based Superalloy First Stage Nozzle

    Directory of Open Access Journals (Sweden)

    A. Luna Ramírez

    2016-01-01

    Full Text Available Superalloys are a group of alloys based on nickel, iron, or cobalt, which are used to operate at high temperatures (T > 540°C and in situations involving very high stresses like in gas turbines, particularly in the manufacture of blades, nozzles, combustors, and discs. Besides keeping its high resistance to temperatures which may approach 85% of their melting temperature, these materials have excellent corrosion resistance and oxidation. However, after long service, these components undergo mechanical and microstructural degradation; the latter is considered a major cause for replacement of the main components of gas turbines. After certain operating time, these components are very expensive to replace, so the microstructural analysis is an important tool to determine the mode of microstructure degradation, residual lifetime estimation, and operating temperature and most important to determine the method of rehabilitation for extending its life. Microstructural analysis can avoid catastrophic failures and optimize the operating mode of the turbine. A case study is presented in this paper.

  6. Mathematical Modelling of Intraretinal Oxygen Partial Pressure

    African Journals Online (AJOL)

    Erah

    oxygen availability) is required for retinal oxidative metabolism. .... retina was described using Hill's equation and Fick's law. ... ganglion cell / nerve fiber layer and the superficial ..... parameter values producing the best. Figure 2: Partial ...

  7. Oxygen potentials of transuranium oxides

    International Nuclear Information System (INIS)

    Haruyoshi Otobe; Mituso Akabori; Arai Yasuo; Kazuo Minato

    2008-01-01

    The oxygen potentials of pyrochlore-type Pu 2 Zr 2 O 7+y , fluorite-type (Pu 0.5 Zr 0.5 )O 2-x and AmO 2-x have been measured by the electromotive force (EMF) method with a zirconia solid-electrolyte. The oxygen potentials of these oxides were reviewed. The phase relations, microstructure, equilibrium state of these oxides were discussed, referring to the isothermal curve of the oxygen potentials. (authors)

  8. Composite modulation of Fano resonance in plasmonic microstructures by electric-field and microcavity

    International Nuclear Information System (INIS)

    Zhang, Fan; Wu, Chenyun; Yang, Hong; Hu, Xiaoyong; Gong, Qihuang

    2014-01-01

    Composite modulation of Fano resonance by using electric-field and microcavity simultaneously is realized in a plasmonic microstructure, which consists of a gold nanowire grating inserted into a Fabry-Perot microcavity composited of a liquid crystal layer sandwiched between two indium tin oxide layers. The Fano resonance wavelength varies with the applied voltage and the microcavity resonance. A large shift of 48 nm in the Fano resonance wavelength is achieved when the applied voltage is 20 V. This may provide a new way for the study of multi-functional integrated photonic circuits and chips based on plasmonic microstructures

  9. Composite modulation of Fano resonance in plasmonic microstructures by electric-field and microcavity

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Fan; Wu, Chenyun; Yang, Hong [State Key Laboratory for Mesoscopic Physics and Department of Physics, Peking University, Beijing 100871 (China); Hu, Xiaoyong, E-mail: xiaoyonghu@pku.edu.cn; Gong, Qihuang [State Key Laboratory for Mesoscopic Physics and Department of Physics, Peking University, Beijing 100871 (China); Collaborative Innovation Center of Quantum Matter, Beijing 100871 (China)

    2014-11-03

    Composite modulation of Fano resonance by using electric-field and microcavity simultaneously is realized in a plasmonic microstructure, which consists of a gold nanowire grating inserted into a Fabry-Perot microcavity composited of a liquid crystal layer sandwiched between two indium tin oxide layers. The Fano resonance wavelength varies with the applied voltage and the microcavity resonance. A large shift of 48 nm in the Fano resonance wavelength is achieved when the applied voltage is 20 V. This may provide a new way for the study of multi-functional integrated photonic circuits and chips based on plasmonic microstructures.

  10. Microstructural examination of irradiated zircaloy-2 pressure tube material

    International Nuclear Information System (INIS)

    Srivastava, D.; Tewari, R.; Dey, G.K.; Sah, D.N.; Banerjee, S.

    2005-01-01

    Irradiation induced microstructural changes in Zr alloys strongly influence the creep, growth and mechanical properties of pressure tube material. Since dimensional changes and mechanical property degradation can limit the life of pressure tube, it is essential to study and develop an understanding of the microstructure produced by neutron irradiation, by examining samples taken from the irradiated components. In the present work, an effort has been made to examine, microstructure of the Zircaloy-2 pressure tube material irradiated in the Indian Pressurized Heavy Water Reactor (PHWR). The present work is a first step towards a comprehensive program of characterization of microstructure of reactor materials after irradiation to different fluence levels in power reactors. In this study, samples from a Zircaloy-2 pressure tube, which had been in operation in the high flux region of Rajasthan Atomic Power Station Unit 1, for a period for 6.77 effective full power years (EFPYs), have been prepared and examined. The samples selected from the tube are expected to have a cumulative radiation damage of about 3 dpa. Samples prepared from the off cuts of RAPS-1 pressure tubes were also studied for examining the unirradiated microstructure of the material. The samples were examined in a 200kV JEOL 2000 FX microscope. This paper presents the distinct features observed in irradiated sample and a comprehensive comparison of the microstructures of the unirradiated and irradiated material. The effect of annealing on the annihilation of the defects generated during irradiation has been also studied. The bright field micrographs revealed that microstructure of the irradiated samples was different in many respects from the microstructure of the unirradiated samples. The presence of defect structure in the form of loops etc could be seen in the irradiated sample. These loops were mostly c-type loops lying in the basal plane. The dissolution and redistribution of the precipitates were

  11. OXIDATIVE-REFORMING OF METHANE AND PARTIAL OXIDATION OF METHANE REACTIONS OVER NiO/PrO2/ZrO2 CATALYSTS: EFFECT OF NICKEL CONTENT

    Directory of Open Access Journals (Sweden)

    Y. J. O. Asencios

    Full Text Available Abstract In this work the behavior of NiO-PrO2-ZrO2 catalysts containing various nickel loadings was evaluated in the partial oxidation of methane and oxidative-reforming reactions of methane. The catalysts were characterized by X-Ray Diffraction Analysis (in situ-XRD, Temperature Programmed Reduction (H2-TPR, Scanning Electron Microscopy (SEM/EDX and Adsorption-Desorption of nitrogen (BET area. The reactions were carried out at 750 °C and 1 atm for 5 hours. The catalysts were studied with different nickel content: 0, 5, 10 and 15% (related to total weight of catalyst, wt%. In both reactions, the catalyst containing the mixture of the three oxides (NiO/PrO2/ZrO2 with 15% nickel (15NiPrZr catalyst showed the best activity for the conversion of the reactants into Syngas and showed high selectivity for H2 and CO. The results suggest that the promoter PrO2 and the Niº centers are in a good proportion in the catalyst with 15% Ni. Our results showed that low nickel concentrations in the catalyst led to high metallic dispersion; however, very low nickel concentrations did not favor the methane transformation into Syngas. The catalyst containing only NiO/ZrO2 in the mixture was not sufficient for the catalysis. The presence of the promoter PrO2 was very important for the catalysis of the POM.

  12. Microstructural evolution of cold-sprayed Inconel 625 superalloy coatings on low alloy steel substrate

    International Nuclear Information System (INIS)

    Chaudhuri, Atanu; Raghupathy, Y.; Srinivasan, Dheepa; Suwas, Satyam; Srivastava, Chandan

    2017-01-01

    This study illustrates microstructural evolution of INCONEL 625 superalloy coatings cold-sprayed on a 4130 chrome alloy steel with medium carbon content. INCONEL 625 powder (5–25 μm) were successfully cold sprayed without any oxidation. The comprehensive microstructure analysis of the as-sprayed coatings and of the substrate-coating interface was carried out using EBSD, TEM, and XRD. The coating microstructure at the substrate-coating interface was markedly different from the microstructure away from the interface. The coating microstructure at steel-coating interface consisted of a fine layer of small grains. The microstructure beyond this fine layer can be divided into splats, inter splat and intra splat boundaries. Both splat and splat boundaries exhibited deformation induced dislocations. Dynamic recovery of dislocations-ridden regions inside the splat was responsible for the development of sub grain structure inside a splat with both low and high angle grain boundaries. Splat-splat (inter splat) boundary consisted of a relatively high density of dislocations and shear bands as a result of adiabatic shear flow localisation. This flow instability is believed to enhance the microstructural integrity by eliminating porosity at splat-splat boundaries. Based on the microstructural analysis using electron microscopy, a plausible mechanism for the development of microstructure has been proposed in this work. Cold spray technique can thus be deployed to develop high quality coatings of commercial importance. - Graphical abstract: Schematics of the evolution of microstructure at the 4130 steel substrate close to interface. i) initial deformation close to interface. ii) Accumulation of dislocation in the substrate. iii) Formation of cell structure due to dislocation tangling and arrangement. iv) Dislocation rearrangement and subgrain formation. v.a) Formation HAGB from dislocation accumulation into LAGB. v.b) HAGB formation through DRX by progressive lattice rotation

  13. The syngas production by partial oxidation using a homogeneous charge compression ignition engine

    International Nuclear Information System (INIS)

    Yang, Yoon Cheol; Lim, Mun Sup; Chun, Young Nam

    2009-01-01

    It is essential to develop the environment-friendly alternative energies urgently considering the limited fossil fuel and the global warming caused by environmental destruction. In this research, the new technology was studied to produce syngas from methane or simulated biogas with a HCCI reforming engine. The purpose is to provide the basics for the research on biogas treatment mainly comprising of methane and carbon dioxide, the cause of global warming. This experiment was conducted on the changes in syngas concentration according to the variations of oxygen/methane ratio, total flow rate, intake heating temperature, CO 2 in mixture and oxygen enrichment with partial oxidation. Through the parametric screening studies, optimum conditions and their results in this study was taken as follows; The maximum content of syngas was; 27.4% at 0.3 of oxygen/methane ratio, 32.38% at 117.3 L/min of total flow rate, and 35.83% at 355 C of intake heating temperature. 41.06% of syngas was produced at 50.33% of oxygen enrichment ratio. (author)

  14. Oxidation of methyl heterocyclic compounds on vanadium oxide catalysts

    International Nuclear Information System (INIS)

    Shimanskaya, M.V.; Lejtis, L.A.; Iovel', I.G.; Gol'dberg, Yu.Sh.; Skolmejstere, R.A.; Golender, L.O.

    1985-01-01

    Data on vapor-phase oxidation of methyl derivatives of thiophene, Δ 2 - thiazo line, pyridine, pyrazine and pyramidine on oxide vanadium-molybdenum catalysts to corresponding heterylaldehydes are generalized. The dependence of catalytic properties of oxide vanadium-molybdenum systems in oxidation reactions of methylheterocyclic compounds on V:Mo ratio in the catalyst is revealed. It is shown that heterocyclic compounds are coordinated by a heteroatom on Lewis centres of V-Mo-O-catalyst primarily with partially reduced vanadium ions

  15. Selective three-dimensional hydrophilization of microstructured polymer surfaces through confined photocatalytic oxidation

    International Nuclear Information System (INIS)

    Ammosova, Lena; Jiang, Yu; Suvanto, Mika; Pakkanen, Tapani A.

    2015-01-01

    Graphical abstract: - Highlights: • Microstructured polymer surfaces with selective 3-D anisotropy were created. • Selective UV treatment was performed to alter surface wettability. • Removable meshes resembling a photomask were applied during UV treatment. • Micropatterning by viscous polymer on solid surface was performed. - Abstract: While the conventional photomask technique gives only two-dimensional anisotropies, in this study we fabricated microstructured polymer surfaces with a selective three-dimensional anisotropy. With the applied removable mesh, we were able to confine the contacting area between the surface and photoinitiator and provide three-dimensional wettability anisotropies. Different types of meshes were used depending on the desired micropatterns shape, size and substrate material. The results revealed the three-dimensional anisotropic micropits pattern with depth profiles, which would be applicable for the confinement and patterning of cells and biomolecules. In addition, the proposed method is applicable for creating selectively activated polymer surface as a substrate for further atomic layer deposition. Moreover, we demonstrate a low cost and fast mass productive method for patterning a viscous polymer liquid in a micro-sized scale

  16. Gravity Effects Observed In Partially Premixed Flames

    Science.gov (United States)

    Puri, Ishwar K.; Aggarwal, Suresh K.; Lock, Andrew J.; Gauguly, Ranjan; Hegde, Uday

    2003-01-01

    Partially premixed flames (PPFs) contain a rich premixed fuel air mixture in a pocket or stream, and, for complete combustion to occur, they require the transport of oxidizer from an appropriately oxidizer-rich (or fuel-lean) mixture that is present in another pocket or stream. Partial oxidation reactions occur in fuel-rich portions of the mixture and any remaining unburned fuel and/or intermediate species are consumed in the oxidizer-rich portions. Partial premixing, therefore, represents that condition when the equivalence ratio (phi) in one portion of the flowfield is greater than unity, and in another section its value is less than unity. In general, for combustion to occur efficiently, the global equivalence ratio is in the range fuel-lean to stoichiometric. These flames can be established by design by placing a fuel-rich mixture in contact with a fuel-lean mixture, but they also occur otherwise in many practical systems, which include nonpremixed lifted flames, turbulent nonpremixed combustion, spray flames, and unwanted fires. Other practical applications of PPFs are reported elsewhere. Although extensive experimental studies have been conducted on premixed and nonpremixed flames under microgravity, there is a absence of previous experimental work on burner stabilized PPFs in this regard. Previous numerical studies by our group employing a detailed numerical model showed gravity effects to be significant on the PPF structure. We report on the results of microgravity experiments conducted on two-dimensional (established on a Wolfhard-Parker slot burner) and axisymmetric flames (on a coannular burner) that were investigated in a self-contained multipurpose rig. Thermocouple and radiometer data were also used to characterize the thermal transport in the flame.

  17. Instability of supercritical porosity in highly doped ceria under reduced oxygen partial pressure

    DEFF Research Database (Denmark)

    Teocoli, Francesca; Ni, De Wei; Esposito, Vincenzo

    2015-01-01

    The thermomechanical behavior and microstructural evolution of low relative density (∼0.40) gadolinium-doped ceria are characterized under oxidative and reducing conditions at high temperatures. The electronic defects generated in the structure by Ce4+ to Ce3+ reduction play an important role on ...

  18. Microstructural investigation of the oxide formed on TP 347H FG during long-term steam oxidation

    DEFF Research Database (Denmark)

    Hansson, Anette Nørgaard; Danielsen, Hilmar Kjartansson; Grumsen, Flemming Bjerg

    2010-01-01

    The long-term oxidation behaviour of TP347H FG in ultra supercritical steam conditions was assessed by exposing the steel in test superheater loops in a Danish coal-fired power plant and characterising the oxide layer with reflective light and electron microscopy. Double layered oxide scales formed...... during steam oxidation. TEM investigations reveal that the inner oxide layer consists of particles of metallic Ni/Fe and Fe-Cr spinel in the interior of the former alloy grains and a compact layer of Fe-Cr spinel and Cr2O3 along the former alloy grain boundaries. The morphology suggests that the inner...

  19. Characterization of microstructural fluctuations in Waspaloy exposed to 760 deg. C for times up to 2500 h

    International Nuclear Information System (INIS)

    Kelekanjeri, V. Siva Kumar G.; Gerhardt, Rosario A.

    2006-01-01

    The microstructure of Waspaloy, a nickel-base superalloy, was investigated as a function of thermal exposure to 760 deg. C for times up to 2502 h. The primary strengthening phase in this material is the γ' precipitate phase-Ni 3 (Al, Ti). The microstructure of the specimens was monitored using impedance spectroscopy (IS), X-ray diffraction (XRD), optical and scanning electron microscopy (SEM). The average grain size varied significantly during thermal exposure. SEM analysis indicated that the precipitates had a bimodal size distribution, with morphologies ranging from spherical to cubic. High-resolution XRD experiments indicated that the γ' lattice parameter is a non-linear function of the exposure time. Energy dispersive (EDS) analysis of Al and Ti composition in the matrix surrounding the primary γ' precipitates also varied. The normalized admittance maximum displayed a partial inverse correlation with the volume fraction of the primary γ' precipitates, and a partial direct correlation with the matrix grain size as a function of thermal exposure time. It is hypothesized that the fluctuations detected by the above techniques are indicative of repetitive nucleation, coarsening and dissolution events occurring during the course of the extended thermal exposure. These results suggest that IS may be useful for monitoring the microstructure of these alloys non-destructively

  20. Control of the kerf size and microstructure in Inconel 738 superalloy by femtosecond laser beam cutting

    Energy Technology Data Exchange (ETDEWEB)

    Wei, J.; Ye, Y.; Sun, Z. [Department of Mechanical Engineering, Tsinghua University, Beijing (China); Liu, L., E-mail: liulei@tsinghua.edu.cn [The State Key Laboratory of Tribology, Tsinghua University, Beijing (China); Zou, G., E-mail: sunzhg@tsinghua.edu.cn [Department of Mechanical Engineering, Tsinghua University, Beijing (China)

    2016-05-01

    Highlights: • Effects of processing parameters on the kerf size in Inconel 738 are investigated. • Defocus is a key parameter affecting the kerf width due to the intensity clamping. • The internal surface microstructures with different scanning speed are presented. • The material removal mechanism contains normal vaporization and phase explosion. • Oxidation mechanism is attributed to the trapping effect of the dangling bonds. - Abstract: Femtosecond laser beam cutting is becoming widely used to meet demands for increasing accuracy in micro-machining. In this paper, the effects of processing parameters in femtosecond laser beam cutting on the kerf size and microstructure in Inconel 738 have been investigated. The defocus, pulse width and scanning speed were selected to study the controllability of the cutting process. Adjusting and matching the processing parameters was a basic enhancement method to acquire well defined kerf size and the high-quality ablation of microstructures, which has contributed to the intensity clamping effect. The morphology and chemical compositions of these microstructures on the cut surface have been characterized by a scanning electron microscopy equipped with an energy dispersive X-ray spectroscopy, X-ray diffraction and X-ray photoelectron spectroscopy. Additionally, the material removal mechanism and oxidation mechanism on the Inconel 738 cut surface have also been discussed on the basis of the femtosecond laser induced normal vaporization or phase explosion, and trapping effect of the dangling bonds.

  1. Ion irradiation studies of oxide ceramics

    International Nuclear Information System (INIS)

    Zinkle, S.J.

    1988-01-01

    This paper presents the initial results of an investigation of the depth-dependent microstructures of three oxide ceramics following ion implantation to moderate doses. The implantations were performed using ion species that occur as cations in the target material; for example, Mg + ions were used for MgO and MgAl 2 O 4 (spinel) irradiations. This minimized chemical effects associated with the implantation and allowed a more direct evaluation to be made of the effects of implanted ions on the microstructure. 11 refs., 14 figs

  2. Microstructure characterization and cation distribution of nanocrystalline cobalt ferrite

    Energy Technology Data Exchange (ETDEWEB)

    Abbas, Y.M., E-mail: ymabbas@live.com [Suez Canal University, Faculty of Science, Physics Department, Ismailia (Egypt); Mansour, S.A.; Ibrahim, M.H. [Suez Canal University, Faculty of Science, Physics Department, Ismailia (Egypt); Ali, Shehab E., E-mail: shehab_physics@yahoo.com [Suez Canal University, Faculty of Science, Physics Department, Ismailia (Egypt)

    2011-11-15

    Nanocrystalline cobalt ferrite has been synthesized using two different methods: ceramic and co-precipitation techniques. The nanocrystalline ferrite phase has been formed after 3 h of sintering at 1000 deg. C. The structural and microstructural evolutions of the nanophase have been studied using X-ray powder diffraction and the Rietveld method. The refinement result showed that the type of the cationic distribution over the tetrahedral and octahedral sites in the nanocrystalline lattice is partially an inverse spinel. The transmission electronic microscope analysis confirmed the X-ray results. The magnetic properties of the samples were characterized using a vibrating sample magnetometer. - Highlights: > The refinement result showed that the cationic distribution over the sites in the lattice is partially an inverse spinel. > The transmission electronic microscope analysis confirmed the X-ray results. > The magnetic properties of the samples were characterized using a vibrating sample magnetometer.

  3. Thermal oxidation of medical Ti6Al4V blasted with ceramic particles: Effects on the microstructure, residual stresses and mechanical properties.

    Science.gov (United States)

    Lieblich, M; Barriuso, S; Multigner, M; González-Doncel, G; González-Carrasco, J L

    2016-02-01

    Roughening of Ti6Al4V by blasting with alumina or zirconia particles improves the mechanical fixation of implants by increasing the surface area available for bone/implant apposition. Additional thermal oxidation treatments of the blasted alloy have already shown to be a complementary low-cost solution to enhancing the in vitro biocompatibility and corrosion resistance of the alloy. In this work, the effects of oxidation treatment on a grit blasted Ti6Al4V biomedical alloy have been analysed in order to understand the net effect of the combined treatments on the alloy fatigue properties. Synchrotron radiation diffraction experiments have been performed to measure residual stresses before and after the treatments and microstructural and hardness changes have been determined. Although blasting of Ti6Al4V with small spherical zirconia particles increases the alloy fatigue resistance with respect to unblasted specimens, fatigue strength after oxidation decreases below the unblasted value, irrespective of the type of particle used for blasting. Moreover, at 700°C the as-blasted compressive residual stresses (700MPa) are not only fully relaxed but even moderate tensile residual stresses, of about 120MPa, are found beneath the blasted surfaces. Contrary to expectations, a moderate increase in hardness occurs towards the blasted surface after oxidation treatments. This can be attributed to the fact that grit blasting modifies the crystallographic texture of the Ti6Al4V shifting it to a random texture, which affects the hardness values as shown by additional experiments on cold rolled samples. The results indicate that the oxidation treatment performed to improve biocompatibility and corrosion resistance of grit blasted Ti6Al4V should be carried out with caution since the alloy fatigue strength can be critically diminished below the value required for high load-bearing components. Copyright © 2015 Elsevier Ltd. All rights reserved.

  4. Relation between microstructure and thermal conductivity in aluminium nitride substrates; Relations entre la microstructure et la conductivite thermique dans les substrats de nitrure d`aluminium

    Energy Technology Data Exchange (ETDEWEB)

    Jarrige, J.; Lecompte, J.P.; Seck, O. [Faculte des Sciences (CNRS), 87 - Limoges (France). Laboratoire de Materiaux Ceramiques et Traitements de Surface

    1996-12-31

    Sintered aluminium nitride is a promising ceramic substrate for future power electronics applications. This ceramic is characterized by a high thermal conductivity (100 to 200 W/m.K) which depends on two main factors: the oxygen content of the AlN powder used for the sintering process and the microstructure of the sintered material. The oxygen content changes with sintering additions. For instance, boron nitride allows the diffusion of oxygen from the nitride grains to the grain joints. With a complement of yttrium oxide in the liquid phase, the BN/Y{sub 2}O{sub 3} couple allows to increase the conductivity to 190 W/m.K with a reduction of the oxygen content. The second part of the study concerns the microstructure of sintered materials. A control of conductivity can be obtained using an adjustment of the sintering cycles. Only two types of microstructure, the secondary phase dispersed in the AlN matrix and the secondary phase that concentrates around triple junctions, allow a better contact between nitride grains and thus higher conductivities of 210 W/m.K. (J.S.) 6 refs.

  5. In Situ Atom Probe Deintercalation of Lithium-Manganese-Oxide.

    Science.gov (United States)

    Pfeiffer, Björn; Maier, Johannes; Arlt, Jonas; Nowak, Carsten

    2017-04-01

    Atom probe tomography is routinely used for the characterization of materials microstructures, usually assuming that the microstructure is unaltered by the analysis. When analyzing ionic conductors, however, gradients in the chemical potential and the electric field penetrating dielectric atom probe specimens can cause significant ionic mobility. Although ionic mobility is undesirable when aiming for materials characterization, it offers a strategy to manipulate materials directly in situ in the atom probe. Here, we present experimental results on the analysis of the ionic conductor lithium-manganese-oxide with different atom probe techniques. We demonstrate that, at a temperature of 30 K, characterization of the materials microstructure is possible without measurable Li mobility. Also, we show that at 298 K the material can be deintercalated, in situ in the atom probe, without changing the manganese-oxide host structure. Combining in situ atom probe deintercalation and subsequent conventional characterization, we demonstrate a new methodological approach to study ionic conductors even in early stages of deintercalation.

  6. Microstructural Characterization of the Heat-Affected Zones in Grade 92 Steel Welds: Double-Pass and Multipass Welds

    Science.gov (United States)

    Xu, X.; West, G. D.; Siefert, J. A.; Parker, J. D.; Thomson, R. C.

    2018-04-01

    The microstructure in the heat-affected zone (HAZ) of multipass welds typical of those used in power plants and made from 9 wt pct chromium martensitic Grade 92 steel is complex. Therefore, there is a need for systematic microstructural investigations to define the different regions of the microstructure across the HAZ of Grade 92 steel welds manufactured using the traditional arc welding processes in order to understand possible failure mechanisms after long-term service. In this study, the microstructure in the HAZ of an as-fabricated two-pass bead-on-plate weld on a parent metal of Grade 92 steel has been systematically investigated and compared to a complex, multipass thick section weldment using an extensive range of electron and ion-microscopy-based techniques. A dilatometer has been used to apply controlled thermal cycles to simulate the microstructures in distinctly different regions in a multipass HAZ using sequential thermal cycles. A wide range of microstructural properties in the simulated materials were characterized and compared with the experimental observations from the weld HAZ. It has been found that the microstructure in the HAZ can be categorized by a combination of sequential thermal cycles experienced by the different zones within the complex weld metal, using the terminology developed for these regions based on a simpler, single-pass bead-on-plate weld, categorized as complete transformation, partial transformation, and overtempered.

  7. Microstructural analysis of the potential of sugarcane bagasse ash as a pozzolan material in cement composites

    International Nuclear Information System (INIS)

    Pereira, A.M.; Assuncao, C.C.; Guimaraes, L. de M.; Malmonge, J.A.; Tashima, M.M; Akasaki, J.L.

    2016-01-01

    For civil construction, the ash obtained by burning sugarcane bagasse (SCBA) in sugar-cane industry is being treated as a pozzolan material because, in addition to containing high amounts of silicon and aluminium oxides, can promote reduction of the environmental impact caused by cement production, since this alternative material may partially replace the Portland cement.The present study evaluated the pozzolanic potential of the SCBA, from different states of Brazil (Sao Paulo (SP), Goias (GO) and Mato Grosso (MT)). The reactivity of the material was analyzed by microstructural characterization, besides the pastes production (lime / SCBA and cement / SCBA) for the analysis of the hydration products formed, which are evaluated by TG and SEM. There was a decrease in the formation of ettringite in the matrixes, inversely proportional to the amount of ash, which favored the reduction of the cracking in cementitious matrices. It has also observed that the pastes produced with the ashes from State of SP showed greater fixation of lime and, consequently, a high reactivity. (author)

  8. Microstructure and tensile properties of oxide dispersion strengthened Fe–14Cr–0.3Y{sub 2}O{sub 3} and Fe–14Cr–2W–0.3Ti–0.3Y{sub 2}O{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Auger, M.A., E-mail: mauger@fis.uc3m.es [Departamento de Física, Universidad Carlos III de Madrid, 28911 Leganés (Spain); Castro, V. de; Leguey, T.; Monge, M.A.; Muñoz, A.; Pareja, R. [Departamento de Física, Universidad Carlos III de Madrid, 28911 Leganés (Spain)

    2013-11-15

    Two ODS ferritic steels with nominal compositions (wt.%): Fe–14Cr–0.3Y{sub 2}O{sub 3} and Fe–14Cr–2W–0.3Ti–0.3Y{sub 2}O{sub 3} have been produced by mechanical alloying and consolidation by hot isostatic pressing. The microstructure and tensile properties of these materials after being forged and heat-treated at 1123 K have been investigated to clarify the interrelation between composition, microstructure and mechanical properties. The second-phase precipitates in these alloys have been analyzed by high-angle annular dark-field imaging in scanning TEM mode and electron diffraction. Fe–14Cr–2W–0.3Ti–0.3Y{sub 2}O{sub 3} exhibits a duplex microstructure consisting of large recrystallized grains, as large as 1.5 μm, and unrecovered regions containing submicron equiaxed grains. In addition, three types of secondary phase particles have been found: large M{sub 23}C{sub 6} particles containing W and Cr, (Cr + Ti) rich spherical particles with diameters between 50 and 500 nm, and fine (Y + Ti) oxide particles with sizes below 30 nm. In contrast, Fe14CrY shows a uniform structure of equiaxed grains, with sizes in the range 0.5–3 μm, containing a fine dispersion of Y oxide particles (<30 nm) homogeneously distributed inside the grains, as well as large carbide and oxide particles. Tensile tests performed over the temperature range 273–973 K have revealed that the alloy containing W and Ti has lower yield and tensile strengths than Fe–14Cr–0.3Y{sub 2}O{sub 3} at temperatures up to 773 K, but the opposite appears to occur beyond this temperature.

  9. Microstructure and Properties of Composite Coatings Obtained on Aluminium Alloys

    Directory of Open Access Journals (Sweden)

    Bara M.

    2016-09-01

    Full Text Available This paper presents methods of modifying the anode surface layers of Al2O3 by introducing carbon to their microstructure. Composite coatings were prepared using two different methods. In the first, coatings were formed by means of oxidation under constant current conditions. Anodic oxidation of aluminium was conducted in a multicomponent electrolyte with the addition of organic acids and graphite. The second method was based on the formation of oxide coatings in an electrolyte without the addition of graphite or heat treatment of the layers of succinic acid. The obtained coatings were tested using SEM, TEM, and GDOES (glow discharge optical emission spectrometry and their tribological and stereometric properties were measured. The study demonstrated the beneficial effects of the methods when used to improve the tribological properties of sliding couples.

  10. Steam assisted oxide growth on aluminium alloys using oxidative chemistries: Part I Microstructural investigation

    DEFF Research Database (Denmark)

    Din, Rameez Ud; Piotrowska, Kamila; Gudla, Visweswara Chakravarthy

    2015-01-01

    The surface treatment of aluminium alloys under steam containing KMnO4 and HNO3resulted in the formation of an oxide layer having a thickness of up to 825 nm. The use of KMnO4 and HNO3 in the steam resulted in incorporation of the respective chemical species into the oxide layer. Steam treatment ...

  11. Effects of Temperature, Oxygen Partial Pressure, and Materials Selection on Slag Infiltration into Porous Refractories for Entrained-Flow Gasifiers

    Science.gov (United States)

    Kaneko, Tetsuya Kenneth

    The penetration rate of molten mineral contents (slag) from spent carbonaceous feedstock into porous ceramic-oxide refractory linings is a critical parameter in determining the lifecycle of integrated gasification combined cycle energy production plants. Refractory linings that withstand longer operation without interruption are desirable because they can mitigate consumable and maintenance costs. Although refractory degradation has been extensively studied for many other high-temperature industrial processes, this work focuses on the mechanisms that are unique to entrained-flow gasification systems. The use of unique feedstock mixtures, temperatures from 1450 °C to 1600 °C, and oxygen partial pressures from 10-7 atm to 10-9 atm pose engineering challenges in designing an optimal refractory material. Experimentation, characterization, and modeling show that gasifier slag infiltration into porous refractory is determined by interactions between the slag and the refractory that either form a physical barrier that impedes fluid flow or induce an increased fluid viscosity that decelerates the velocity of the fluid body. The viscosity of the slag is modified by the thermal profile of the refractory along the penetration direction as well as reactions between the slag and refractory that alter the chemistry, and thereby the thermo-physical properties of the fluid. Infiltration experiments reveal that the temperature gradient inherently present along the refractory lining limits penetration. A refractory in near-isothermal conditions demonstrates deeper slag penetration as compared to one that experiences a steeper thermal profile. The decrease in the local temperatures of the slag as it travels deeper into the refractory increases the viscosity of the fluid, which in turn slows the infiltration velocity of fluid body into the pores of the refractory microstructure. With feedstock mixtures that exhibit high iron-oxide concentrations, a transition-metal-oxide, the oxygen

  12. Zinc oxide tetrapod: a morphology with multifunctional applications

    International Nuclear Information System (INIS)

    Modi, Gaurav

    2015-01-01

    Zinc oxide has emerged as a material of great interest due to its unique optical, electrical and magnetic properties. This review comprehensively covers the various aspects of zinc oxide tetrapods. Tetrapod is a one dimensional zinc oxide nano-microstructure and has been found to have very promising applications in diverse fields. The growth model, properties, synthesis methods and variations in the tetrapod morphology by varying the synthesis conditions have been discussed. The promising applications of zinc oxide tetrapod morphology have been also discussed in detail. (review)

  13. Microstructure of ZnO thin films deposited by high power impulse magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Reed, A.N., E-mail: amber.reed.5@us.af.mil [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States); Department of Chemical and Materials Engineering, University of Dayton, Dayton, OH 45469 (United States); Shamberger, P.J. [Department of Materials Science and Engineering, Texas A& M University, College Station, TX 77843 (United States); Hu, J.J. [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States); University of Dayton Research Institute, University of Dayton, Dayton, OH 45469 (United States); Muratore, C. [Department of Chemical and Materials Engineering, University of Dayton, Dayton, OH 45469 (United States); Bultman, J.E. [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States); University of Dayton Research Institute, University of Dayton, Dayton, OH 45469 (United States); Voevodin, A.A., E-mail: andrey.voevodin@us.af.mil [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States)

    2015-03-31

    High power impulse magnetron sputtering was used to deposit thin (~ 100 nm) zinc oxide (ZnO) films from a ceramic ZnO target onto substrates heated to 150 °C. The resulting films had strong crystallinity, highly aligned (002) texture and low surface roughness (root mean square roughness less than 10 nm), as determined by X-ray diffraction, transmission electron microscopy, scanning electron microscopy and atomic force spectroscopy measurements. Deposition pressure and target–substrate distance had the greatest effect on film microstructure. The degree of alignment in the films was strongly dependent on the gas pressure. Deposition at pressures less than 0.93 Pa resulted in a bimodal distribution of grain sizes. An initial growth layer with preferred orientations (101) and (002) parallel to the interface was observed at the film–substrate interface under all conditions examined here; the extent of that competitive region was dependent on growth conditions. Time-resolved current measurements of the target and ion energy distributions, determined using energy resolved mass spectrometry, were correlated to film microstructure in order to investigate the effect of plasma conditions on film nucleation and growth. - Highlights: • Low temperature growth of nanocrystalline zinc oxide (ZnO) films. • ZnO films had a highly (002) textured, smooth, dense microstructure. • Dominant (002) orientation of films was pressure dependent. • Interfacial (101)/(002) mixed orientation layer controlled by substrate location.

  14. Powder processing of high Tc oxide superconductors and their properties

    International Nuclear Information System (INIS)

    Vajpei, A.C.; Upadhyaya, G.S.

    1992-01-01

    Powder processing of ceramics is an established technology and in the area of high T c superconductors, its importance is felt even more significantly. The present monograph is an attempt in this direction to explore the perspectives and practice of powder processing routes towards control and optimization of the microstructure and pertinent properties of high T c oxide superconductors. The monograph consists of 6 chapters. After a very brief introduction (Chapter 1), Chapter 2 describes various classes of high T c oxide superconductors and their phase equilibria. Chapter 3 highlights the preparation of oxide superconductor powders through various routes and details their subtle distinctions. Chapter 4 briefly covers characterisation of the oxide superconductors, laying emphasis on the process-analysis and microstructure. Chapter 5 describes in detail various fabrication techniques for bulk superconductors through the powder routes. The last Chapter (Chapter 6) describing properties of bulk oxide superconductors, discusses the role of subtituents, compositional variations and processing methods on such properties. References are given at the end of each chapter. (orig.)

  15. Excellent performance of Pt-C/TiO2 for methanol oxidation: Contribution of mesopores and partially coated carbon

    Science.gov (United States)

    Wu, Xinbing; Zhuang, Wei; Lu, Linghong; Li, Licheng; Zhu, Jiahua; Mu, Liwen; Li, Wei; Zhu, Yudan; Lu, Xiaohua

    2017-12-01

    Partial deposition of carbon onto mesoporous TiO2 (C/TiO2) were prepared as supporting substrate for Pt catalyst development. Carbon deposition is achieved by in-situ carbonization of furfuryl alcohol. The hybrid catalysts were characterized by XRD, Raman, SEM and TEM and exhibited outstanding catalytic activity and stability in methanol oxidation reaction. The heterogeneous carbon coated on mesoporous TiO2 fibers provided excellent electrical conductivity and strong interfacial interaction between TiO2 support and Pt metal nanoparticles. Methanol oxidation reaction results showed that the activity of Pt-C/TiO2 is 3.0 and 1.5 times higher than that of Pt-TiO2 and Pt-C, respectively. In addition, the Pt-C/TiO2 exhibited a 6.7 times enhanced stability compared with Pt-C after 2000 cycles. The synergistic effect of C/TiO2 is responsible for the enhanced activity of Pt-C/TiO2, and its excellent durability could be ascribed to the strong interfacial interaction between Pt nanoparticles and C/TiO2 support.

  16. Influence of Thermal Annealing on the Microstructural Properties of Indium Tin Oxide Nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Sung Nam; Kim, Seung Bin [Pohang University of Science and Technology, Pohang (Korea, Republic of); Choi, Hyun Chul [Chonnam National University, Gwangju (Korea, Republic of)

    2012-01-15

    In this work, we studied the microstructural changes of ITO during the annealing process. ITO nanoparticles were prepared by the sol-gel method using indium tin hydroxide as the precursor. The prepared sample was investigated using TEM, powder XRD, XPS, DRIFT, and 2D correlation analysis. The O 1s XPS spectra suggested that the microstructural changes during the annealing process are closely correlated with the oxygen sites of the ITO nanoparticles. The temperature-dependent in situ DRIFT spectra suggested that In-OH in the terminal sites is firstly decomposed and, then, Sn-O-Sn is produced in the ITO nanoparticles during the thermal annealing process. Based on the 2D correlation analysis, we deduced the following sequence of events: 1483 (due to In-OH bending mode) → 2268, 2164 (due to In-OH stretching mode) → 1546 (due to overtones of Sn- O-Sn modes) → 1412 (due to overtones of Sn-O-Sn modes) cm{sup -1}.

  17. Synthesis and microstructure of La_1_−_xCa_xCoO_3 nanoparticles and their catalytic activity for CO oxidation

    International Nuclear Information System (INIS)

    Luu, Tien Hung; Nguyen, Xuan Dung; Phan, Thi Minh Huyen; Schulze, Steffen; Hietschold, Michael

    2015-01-01

    Perovskite nanoparticles of La_1_−_xCa_xCoO_3 (x = 0, 0.2, 0.3, 0.5) were synthesized by the combustion method using polyvinyl alcohol (PVA) and corresponding metal nitrates. Microstructure of samples was characterized by high resolution transmission electron microscopy (HRTEM) and selected area electron diffraction (SAED) combined with x-ray diffraction (XRD). The nanoparticles were characterized by thermogravimetric and differential thermal analysis (TG-DTA) and BET (Brunauer–Emmet–Teller). A high surface area (15–21 m"2 g"−"1) at low temperature (600 °C) of samples was obtained. The optimal preparative conditions were PVA/metals 2:1 by mole, pH = 3 and 80 °C for gel formation. Perovskites exhibit a good catalytic activity in total oxidation of CO at the low temperature (<250 °C) of reaction. (paper)

  18. Oxide characterization and hydrogen behaviors of Zr-based alloys

    International Nuclear Information System (INIS)

    Kim, Y. S.; Kim, D. J.; Kwon, S. H.; Lee, H. S.; Oh, S. J.; Yim, B. J.; Son, S. B.; Yun, S. P.

    2006-03-01

    The work scope and contents of the research are as follows : basic properties of zirconium alloys, hydrogen pick-up mechanism of zirconium alloy, effects of hydride on the corrosion behaviors of zirconium alloys, estimation on stress of oxide layer in the zirconium alloy, microstructure and characteristic of oxide in pre-hydrided zirconium alloys

  19. Microstructure evolution of superalloy for large exhaust valve during hot forging

    International Nuclear Information System (INIS)

    Jeong, H.S.; Cho, J.R.; Park, H.C.

    2004-01-01

    The nickel-based alloy Nimonic 80A possesses strength, and corrosion, creep and oxidation resistance at high temperature. These products are used for aerospace, marine engineering and power generation, etc. The control of forging parameters such as strain, strain rate, temperature and holding time is important because the microstructure change in hot working affects the mechanical properties. It is necessary to understand the microstructure variation evolution. The microstructure change evolution occurs by recovery, recrystallization and grain growth phenomena. The dynamic recrystallization evolution has been studied in the temperature range 950-1250 deg. C and strain rate range 0.05-5s-1 using hot compression tests. The metadynamic recrystallization and grain growth evolution has been studied in the temperature range 950-1250 deg. C and strain rate range 0.05, 5s-1, holding time range 5, 10, 100, 600 sec using hot compression tests. Modeling equations are developed to represent the flow curve, recrystallized grain size, recrystallized fraction and grain growth phenomena by various tests. Parameters of modeling equation are expressed as a function of the Zener-Hollomon parameter. The modeling equation for grain growth is expressed as a function of initial grain size and holding time. The developed modeling equation was combined with thermo-viscoplastic finite element modeling to predict various microstructure change evolution during thermo mechanical processing. The predicted grain size in developed FE simulation results is compared with results obtained in various tests. In order to obtain a final microstructure and good mechanical properties in forging, the FEM would become a useful tool in the simulation of the microstructure development

  20. Gas atomized precursor alloy powder for oxide dispersion strengthened ferritic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Rieken, Joel [Iowa State Univ., Ames, IA (United States)

    2011-12-13

    Gas atomization reaction synthesis (GARS) was employed as a simplified method for producing precursor powders for oxide dispersion strengthened (ODS) ferritic stainless steels (e.g., Fe-Cr-Y-(Ti,Hf)-O), departing from the conventional mechanical alloying (MA) process. During GARS processing a reactive atomization gas (i.e., Ar-O2) was used to oxidize the powder surfaces during primary break-up and rapid solidification of the molten alloy. This resulted in envelopment of the powders by an ultra-thin (t < 150 nm) metastable Cr-enriched oxide layer that was used as a vehicle for solid-state transport of O into the consolidated microstructure. In an attempt to better understand the kinetics of this GARS reaction, theoretical cooling curves for the atomized droplets were calculated and used to establish an oxidation model for this process. Subsequent elevated temperature heat treatments, which were derived from Rhines pack measurements using an internal oxidation model, were used to promote thermodynamically driven O exchange reactions between trapped films of the initial Cr-enriched surface oxide and internal Y-enriched intermetallic precipitates. This novel microstructural evolution process resulted in the successful formation of nano-metric Y-enriched dispersoids, as confirmed using high energy X-ray diffraction and transmission electron microscopy (TEM), equivalent to conventional ODS alloys from MA powders. The thermal stability of these Y-enriched dispersoids was evaluated using high temperature (1200°C) annealing treatments ranging from 2.5 to 1,000 hrs of exposure. In a further departure from current ODS practice, replacing Ti with additions of Hf appeared to improve the Y-enriched dispersoid thermal stability by means of crystal structure modification. Additionally, the spatial distribution of the dispersoids was found to depend strongly on the original rapidly solidified microstructure. To exploit this, ODS microstructures were engineered from

  1. Microstructure evolution and microstructure/mechanical properties relationships in alpha+beta titanium alloys

    Science.gov (United States)

    Lee, Eunha

    In this study, the microstructural evolution of Timetal 550 was investigated. Timetal 550 showed two types of phase transformations (martensitic and nucleation and growth) depending on the cooling rate from the beta region. The alpha phase initially precipitated at the prior beta grain boundaries, and it had a Burgers OR with one of the adjacent grains. It was found that colonies could grow, even in the fast-cooled Timetal 550 sample, from the grain boundary alpha into the prior beta grain with which it exhibited the Burgers OR. Three orientation relationships were also found between alpha laths in the basketweave microstructure. Microhardness testing demonstrated that fast-cooled Timetal 550 samples with basketweave microstructure were harder than slowly-cooled samples with colony microstructure. Orientation-dependent deformation was found in the colony microstructure. Specifically, when the surface normal is perpendicular to the [0001] of alpha, the material deforms easily in the direction perpendicular to the [0001] of alpha. Fuzzy logic and Bayesian neural network models were developed to predict the room temperature tensile properties of Timetal 550. This involved the development of a database relating microstructural features to mechanical properties. A Gleeble 3800 thermal-mechanical simulator was used to develop various microstructures. Microstructural features of tensile-tested samples were quantified using stereological procedures. The quantified microstructural features and the tensile properties were used as inputs and outputs, respectively, for modeling the relationships between them. The individual influence of five microstructural features on tensile properties was determined using the established models. The microstructural features having the greatest impact on UTS and YS were the thickness of alpha laths and the width of grain boundary alpha layer, and the microstructural features having the greatest impact on elongation were the thickness of

  2. The effect of substrate orientation on the kinetics and thermodynamics of initial oxide-film growth on metals

    Energy Technology Data Exchange (ETDEWEB)

    Reichel, Friederike

    2007-11-19

    This thesis addresses the effect of the parent metal-substrate orientation on the thermodynamics and kinetics of ultra-thin oxide-film growth on bare metals upon their exposure to oxygen gas at low temperatures (up to 650 K). A model description has been developed to predict the thermodynamically stable microstructure of a thin oxide film grown on its bare metal substrate as function of the oxidation conditions and the substrate orientation. For Mg and Ni, the critical oxide-film thickness is less than 1 oxide monolayer and therefore the initial development of an amorphous oxide phase on these metal substrates is unlikely. Finally, for Cu and densely packed Cr and Fe metal surfaces, oxide overgrowth is predicted to proceed by the direct formation and growth of a crystalline oxide phase. Further, polished Al single-crystals with {l_brace}111{r_brace}, {l_brace}100{r_brace} and {l_brace}110{r_brace} surface orientations were introduced in an ultra-high vacuum system for specimen processing and analysis. After surface cleaning and annealing, the bare Al substrates have been oxidized by exposure to pure oxygen gas. During the oxidation, the oxide-film growth kinetics has been established by real-time in-situ spectroscopic ellipsometry. After the oxidation, the oxide-film microstructures were investigated by angle-resolved X-ray photoelectron spectroscopy and low energy electron diffraction. Finally, high-resolution transmission electron microscopic analysis was applied to study the microstructure and morphology of the grown oxide films on an atomic scale. (orig.)

  3. Microstructural characterization of the geopolymer obtained from iron-rich metakaolin

    International Nuclear Information System (INIS)

    Vassalo, Erica Antunes de S.; Aguilar, Maria Teresa P.; Gumieri, Adriana Guerra

    2014-01-01

    Geopolymer is a material derived from precursors rich in SiO_2 and Al_2O_3, activated in an alkaline solution by means of a polymerization process. In this process, units of tetrahedral aluminosilicate structures are organized in repetitions that share oxygen. One of the precursors most commonly used to obtain geopolymer is metakaolin. Recent studies have reported iron enhancement in a partial replacement of the aluminium present in metakaolin. This paper presents the microstructural characterization and analysis of a geopolymer obtained by means of the activation of iron-rich metakaolin with sodium hydroxide at 12, 15 and 18 mol, both at room temperature and in an oven at 85±3°C. The geopolymers obtained were classified and analysed using X-ray fluorescence testing (EDX-720), a scanning electron microscope (SEM) and a Fourier transform infrared spectroscopy (FTIR). The results enabled an assessment of their physical-chemical and microstructural characteristics, as well as their reactive potential. (author)

  4. Ytterbium-Phosphate Glass for Microstructured Fiber Laser

    Directory of Open Access Journals (Sweden)

    Ryszard Stępień

    2014-06-01

    Full Text Available In the paper, we report on the development of a synthesis and melting method of phosphate glasses designed for active microstructured fiber manufacturing. Non-doped glass synthesized in a P2O5-Al2O3-BaO-ZnO-MgO-Na2O oxide system served as the matrix material; meanwhile, the glass was doped with 6 mol% (18 wt% of Yb2O3, as fiber core. The glasses were well-fitted in relation to optical (refractive index and thermal proprieties (thermal expansion coefficient, rheology. The fiber with the Yb3+-doped core, with a wide internal photonic microstructure for a laser pump, as well as with a high relative hole size in the photonic outer air-cladding, was produced. The laser built on the basis of this fiber enabled achieving 8.07 W of output power with 20.5% slope efficiency against the launched pump power, in single-mode operation M2 = 1.59, from a 53 cm-long cavity.

  5. Microstructure characterization and cation distribution of nanocrystalline cobalt ferrite

    International Nuclear Information System (INIS)

    Abbas, Y.M.; Mansour, S.A.; Ibrahim, M.H.; Ali, Shehab E.

    2011-01-01

    Nanocrystalline cobalt ferrite has been synthesized using two different methods: ceramic and co-precipitation techniques. The nanocrystalline ferrite phase has been formed after 3 h of sintering at 1000 deg. C. The structural and microstructural evolutions of the nanophase have been studied using X-ray powder diffraction and the Rietveld method. The refinement result showed that the type of the cationic distribution over the tetrahedral and octahedral sites in the nanocrystalline lattice is partially an inverse spinel. The transmission electronic microscope analysis confirmed the X-ray results. The magnetic properties of the samples were characterized using a vibrating sample magnetometer. - Highlights: → The refinement result showed that the cationic distribution over the sites in the lattice is partially an inverse spinel. → The transmission electronic microscope analysis confirmed the X-ray results. → The magnetic properties of the samples were characterized using a vibrating sample magnetometer.

  6. Artificial Microstructures to Investigate Microstructure-Property Relationships in Metallic Glasses

    Science.gov (United States)

    Sarac, Baran

    Technology has evolved rapidly within the last decade, and the demand for higher performance materials has risen exponentially. To meet this demand, novel materials with advanced microstructures have been developed and are currently in use. However, the already complex microstructure of technological relevant materials imposes a limit for currently used development strategies for materials with optimized properties. For this reason, a strategy to correlate microstructure features with properties is still lacking. Computer simulations are challenged due to the computing size required to analyze multi-scale characteristics of complex materials, which is orders of magnitude higher than today's state of the art. To address these challenges, we introduced a novel strategy to investigate microstructure-property relationships. We call this strategy "artificial microstructure approach", which allows us to individually and independently control microstructural features. By this approach, we defined a new way of analyzing complex microstructures, where microstructural second phase features were precisely varied over a wide range. The artificial microstructures were fabricated by the combination of lithography and thermoplastic forming (TPF), and subsequently characterized under different loading conditions. Because of the suitability and interesting properties of metallic glasses, we proposed to use this toolbox to investigate the different deformation modes in cellular structures and toughening mechanism in metallic glass (MG) composites. This study helped us understand how to combine the unique properties of metallic glasses such as high strength, elasticity, and thermoplastic processing ability with plasticity generated from heterostructures of metallic glasses. It has been widely accepted that metallic glass composites are very complex, and a broad range of contributions have been suggested to explain the toughening mechanism. This includes the shear modulus, morphology

  7. Formation of polar surfaces in microstructured ZnO by doping with Cu and applications in photocatalysis using visible light

    International Nuclear Information System (INIS)

    Pawar, Rajendra C.; Choi, Da-Hyun; Lee, Jai-Sung; Lee, Caroline S.

    2015-01-01

    We report the synthesis of copper-doped zinc oxide microstructures with a large amount of polar surfaces using a single-step facile chemical method by collecting powders of zinc oxide (ZnO) microstructures. It was found that rod-like morphology of ZnO transformed into disk and sphere-like structure with nanosheets. Hollow disk-like structures were formed due to the surface etching properties of Cl − ions in the copper chloride precursor. The photocatalytic degradation of methylene blue (MB) and rhodamine B (RhB) dyes was measured under irradiation with visible light using the structures as catalysts. The Cu-doped ZnO exhibited better photodegradation properties than did undoped ZnO. The enhanced performance is attributed to the existence of (001) polar surfaces, oxygen vacancies, and increased optical absorbance at visible wavelengths, which is consistent with the field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), room temperature photoluminescence (PL), and optical absorbance measurements. These favorable photocatalytic properties of the doped microstructures demonstrate their potential for use in wastewater treatment. - Graphical abstract: Graphical abstract shows the electron transfer mechanism under visible light for Cu-doped ZnO microstructures and the photocatalytic degradation of dye. - Highlights: • Cu induced microstructures of ZnO with polar surfaces. • Methylene blue degradation under visible light irradiation. • Room temperature ferromagnetism due to oxygen vacancies in ZnO. • 7% Cu–ZnO has highest photocatalytic activity

  8. Selective oxidation

    International Nuclear Information System (INIS)

    Cortes Henao, Luis F.; Castro F, Carlos A.

    2000-01-01

    It is presented a revision and discussion about the characteristics and factors that relate activity and selectivity in the catalytic and not catalytic partial oxidation of methane and the effect of variables as the temperature, pressure and others in the methane conversion to methanol. It thinks about the zeolites use modified for the catalytic oxidation of natural gas

  9. Microstructural and paleomagnetic insight into the cooling history of the IAB parent body

    Science.gov (United States)

    Nichols, Claire I. O.; Krakow, Robert; Herrero-Albillos, Julia; Kronast, Florian; Northwood-Smith, Geraint; Harrison, Richard J.

    2018-05-01

    The IABs represent one of only two groups of iron meteorites that did not form by fractional crystallization of liquid Fe-Ni in the core of a differentiated planetesimal. Instead, they are believed to originate from a partially differentiated body that was severely disrupted by one or more impacts during its early history. We present a detailed microstructural and paleomagnetic study of the Odessa and Toluca IAB meteorites, with a view to further constraining the complex history of the IAB parent body. X-ray photoemission electron microscopy and energy dispersive spectroscopy were used to generate high-resolution Ni/Fe maps. The crystallographic architecture of Odessa was analysed using electron backscatter diffraction. Paleomagnetic signals and the magnetic properties of several microstructures were also assessed using X-ray magnetic circular dichroism. Odessa exhibits a complex series of microstructures, requiring an unusual evolution during slow cooling. A conventional Widmanstätten microstructure, consisting of multiple generations of kamacite lamellae surrounded by M-shaped diffusion profiles, developed via continuous precipitation to temperatures below ∼400 °C. Multiple generations of pearlitic plessite nucleated from kamacite/taenite (T > 400 °C) and tetrataenite rim/taenite interfaces (T theories, these rafts cannot have formed by coarsening of pre-existing pearlitic plessite. A new bowing mechanism is proposed, whereby rafts of Ni-enriched taenite form between advancing lobes of an irregular reaction front during discontinuous precipitation. Subsequent coarsening leads to the growth of the taenite rafts, and the partial or complete removal of pearlite lamellae, resulting in spheroidised plessite with a crystallographic architecture matching the experimental observations. We find no evidence for a strong magnetic field on the IAB parent body, suggesting it did not have an active core dynamo at the time of cloudy zone formation. This supports the

  10. Corrosion behaviour of nanometre sized cerium oxide and titanium oxide incorporated aluminium in NaCl solution

    International Nuclear Information System (INIS)

    Ashraf, P. Muhamed; Edwin, Leela

    2013-01-01

    Highlights: ► Corrosion resistant aluminium incorporated with nano oxides of cerium and titanium. ► 0.2% nano CeO 2 and 0.05% nano TiO 2 showed increased corrosion resistance. ► Nano TiO 2 concentration influenced the optimum performance of the material. ► Comparison of Micro and nano CeO 2 and TiO 2 aluminium showed the latter is best. - Abstract: The study highlights the development of an aluminium matrix composite by incorporating mixture of nanometre sized cerium oxide and titanium oxide in pure aluminium and its corrosion resistance in marine environment. The mixed nanometre sized oxides incorporated aluminium exhibited improved microstructure and excellent corrosion resistance. Corrosion resistance depends on the concentration of nanometre sized titanium oxide. Electrochemical characteristics improved several folds in nanometre sized mixed oxides incorporated aluminium than micrometre sized oxides incorporated aluminium.

  11. Study of the dynamics of the MoO2-Mo2C system for catalytic partial oxidation reactions

    Science.gov (United States)

    Cuba Torres, Christian Martin

    On a global scale, the energy demand is largely supplied by the combustion of non-renewable fossil fuels. However, their rapid depletion coupled with environmental and sustainability concerns are the main drivers to seek for alternative energetic strategies. To this end, the sustainable generation of hydrogen from renewable resources such as biodiesel would represent an attractive alternative solution to fossil fuels. Furthermore, hydrogen's lower environmental impact and greater independence from foreign control make it a strong contender for solving this global problem. Among a wide variety of methods for hydrogen production, the catalytic partial oxidation offers numerous advantages for compact and mobile fuel processing systems. For this reaction, the present work explores the versatility of the Mo--O--C catalytic system under different synthesis methods and reforming conditions using methyl oleate as a surrogate biodiesel. MoO2 exhibits good catalytic activity and exhibits high coke-resistance even under reforming conditions where long-chain oxygenated compounds are prone to form coke. Moreover, the lattice oxygen present in MoO2 promotes the Mars-Van Krevelen mechanism. Also, it is introduced a novel beta-Mo2C synthesis by the in-situ formation method that does not utilize external H2 inputs. Herein, the MoO 2/Mo2C system maintains high catalytic activity for partial oxidation while the lattice oxygen serves as a carbon buffer for preventing coke formation. This unique feature allows for longer operation reforming times despite slightly lower catalytic activity compared to the catalysts prepared by the traditional temperature-programmed reaction method. Moreover, it is demonstrated by a pulse reaction technique that during the phase transformation of MoO2 to beta-Mo2C, the formation of Mo metal as an intermediate is not responsible for the sintering of the material wrongly assumed by the temperature-programmed method.

  12. Reaction phenomena of catalytic partial oxidation of methane under the impact of carbon dioxide addition and heat recirculation

    International Nuclear Information System (INIS)

    Chen, Wei-Hsin; Lin, Shih-Cheng

    2015-01-01

    The reaction phenomena of CPOM (catalytic partial oxidation of methane) in a Swiss-roll reactor are studied numerically where a rhodium-based catalyst bed is embedded at the center of the reactor. CO 2 is added into the feed gas and excess enthalpy recovery is performed to evaluate their influences on CPOM performance. In the study, the mole ratio of O 2 to CH 4 (O 2 /CH 4 ratio) is fixed at 0.5 and the mole ratio of CO 2 to O 2 (CO 2 /O 2 ratio) is in the range of 0–2. The results reveal that CO 2 addition into the influent has a slight effect on methane combustion, but significantly enhances dry reforming and suppresses steam reforming. The reaction extents of steam reforming and dry reforming in CPOM without heat recovery and CO 2 addition are in a comparable state. Once CO 2 is added into the feed gas, the dry reforming is enhanced, thereby dominating CH 4 consumption. Compared to the reactor without excess enthalpy recovery, heat recirculation drastically increases the maximum reaction temperature and CH 4 conversion in the catalyst bed; it also intensifies the H 2 selectivity, H 2 yield, CO 2 conversion, and syngas production rate. The predictions indicate that the heat recirculation is able to improve the syngas formation up to 45%. - Highlights: • Catalytic partial oxidation of methane with CO 2 addition and heat recovery is studied. • CO 2 addition has a slight effect on methane combustion. • CO 2 addition significantly enhances dry reforming and suppresses steam reforming. • Dry reforming dominates CH 4 consumption when CO 2 addition is large. • Heat recirculation can improve the syngas formation up to 45%

  13. Partial Oxidation of n-Butane over a Sol-Gel Prepared Vanadium Phosphorous Oxide

    Directory of Open Access Journals (Sweden)

    Juan M. Salazar

    2013-01-01

    Full Text Available Vanadium phosphorous oxide (VPO is traditionally manufactured from solid vanadium oxides by synthesizing VOHPO4∙0.5H2O (the precursor followed by in situ activation to produce (VO2P2O7 (the active phase. This paper discusses an alternative synthesis method based on sol-gel techniques. Vanadium (V triisopropoxide oxide was reacted with ortho-phosphoric acid in an aprotic solvent. The products were dried at high pressure in an autoclave with a controlled excess of solvent. This procedure produced a gel of VOPO4 with interlayer entrapped molecules. The surface area of the obtained materials was between 50 and 120 m2/g. Alcohol produced by the alkoxide hydrolysis reduced the vanadium during the drying step, thus VOPO4 was converted to the precursor. This procedure yielded non-agglomerated platelets, which were dehydrated and evaluated in a butane-air mixture. Catalysts were significantly more selective than the traditionally prepared materials with similar intrinsic activity. It is suggested that the small crystallite size obtained increased their selectivity towards maleic anhydride.

  14. Microstructural record vs chemical and geochronological preservation in muscovite: implications for P-T-t estimates in deformed metapelites

    Science.gov (United States)

    Airaghi, Laura; Lanari, Pierre; Warren, Clare J.; de Sigoyer, Julia; Guillot, Stéphane

    2017-04-01

    Pressure-temperature-deformation (P-T-ɛ) paths for metamorphic rocks commonly relies on the link between successive metamorphic assemblages and the microstructures. However, with increasing P-T conditions, metamorphic minerals in an early microstructure can re-equilibrate by changing their chemical composition. The direct link between deformation phases and mineral compositions for thermobarometry purposes can therefore be distorted. This study focuses on a series of garnet-biotite metapelites from the Longmen Shan (Sichuan, China) that preserve muscovite of different chemistry in distinct microstructures. To quantify the degree of re-equilibration of muscovite, a microstructural study was coupled with high-resolution chemical mapping. Then, the chemical evolution of muscovite (Si4+ and XMg) was modeled using Gibbs free energy minimization along a P-T loop previously constrained by phase equilibria calculations, semi-empirical and empirical thermobarometry. Our results show that the studied metapelites experienced a "typical" three stages metamorphic history: (1) heating and burial up to 11 kbar, 530˚ C, (2) minor decompression and heating up to 6 kbar, 580˚ C and (3) decompression and cooling down to 4-5 kbar, 380-450˚ C. However, muscovite has been partially or completely re-equilibrated during the three stages by idiomorphic replacement, although it is mainly observed in prograde microstructures preceding the pressure peak. The main factors controlling the degree of re-equilibration are the intensity of the deformation and the fluid availability during metamorphism. The P-T conditions of metamorphic assemblages thus reflect pulses of fluids release that enhanced mineral resorption and local replacement. The metamorphic peak (2) was dated by in situ 40Ar/39Ar on biotite porphyroblasts and by in situ (U-Pb)/Th laser ablation on allanite (REE-rich epidote) at 185±15 Ma. Muscovite grains preserved in prograde microstructures and partially re-equilibrated during

  15. The effect of minor alloying elements on oxidation and hydrogen pickup in Zr-2.5Nb

    International Nuclear Information System (INIS)

    Ploc, R.A.

    2002-01-01

    In CANDU reactors, fuel and coolant are contained in horizontal pressure tubes made of Zr-2.5 wt% Nb alloy. In the past decade, the effect of more than 20 impurity elements, in various concentrations, on oxidation and deuterium pickup (at 300 o C, pD = 10.5, Li 2 O) have been investigated in over 70 Zr-2.5Nb alloys. The studies were performed using non-consumable arc-melted alloy logs that were rolled and made into corrosion coupons and corroded in autoclaves. This study represents one of the largest collections of previously unpublished data on the effect of impurity elements on oxide film growth and deuterium pickup in a zirconium alloy. Elements such as Al, Ti, Mn, and Pt, to name but a few, were found to significantly accelerate the corrosion process. Some elements, such as tin, had a positive effect on oxidation (lowers the rate of oxide film development) and a negative effect on hydrogen pickup (increases pickup). Three parameters were important to the corrosion process, namely, microstructure, surface finish, and synergistic interactions between the impurity elements. The above studies culminated in two response surface analyses (RSA). The first was conducted on the effect of C and Fe on oxygen and deuterium pickup in Zr-2.5Nb drop castings corroded at 325 o C in CANDU conditions. The second study was performed in autoclaves at 300 o C on the affect of four impurity elements, C, Fe, Cr, and Si, in Zr-2.5Nb micro-tubes, which possess the same microstructure as full-size pressure tubes. The first RSA revealed a quadratic dependence of corrosion on C and Fe concentrations, with an optimum resistance at about 30 ppm (wt) C and 1100 ppm (wt) Fe. This has been partially confirmed by out-reactor corrosion of Zr-2.5Nb-Fe micro-pressure tubes. Trends in- and out-reactor were similar for oxidation but different in magnitude for deuterium pickup. There is no linear dependence on the Fe concentration in-reactor, implying that Fe and C form a complex. The second RSA

  16. The effect of minor alloying elements on oxidation and hydrogen pickup in Zr-2.5Nb

    International Nuclear Information System (INIS)

    Ploc, R.A.

    2002-01-01

    In CANDU reactors, fuel and coolant are contained in horizontal pressure tubes made of Zr-2.5 wt% Nb alloy. In the past decade, the effect of more than 20 impurity elements, in various concentrations, on oxidation and deuterium pickup (at 300 deg C, pD = 10.5, Li 2 O) have been investigated in over 70 Zr-2.5Nb alloys. The studies were performed using non-consumable arc-melted alloy logs that were rolled and made into corrosion coupons and corroded in autoclaves. This study represents one of the largest collections of previously unpublished data on the effect of impurity elements on oxide film growth and deuterium pickup in a zirconium alloy. Elements such as Al, Ti, Mn, and Pt, to name but a few, were found to significantly accelerate the corrosion process. Some elements, such as tin, had a positive effect on oxidation (lowers the rate of oxide film development) and a negative effect on hydrogen pickup (increases pickup). Three parameters were important to the corrosion process, namely, microstructure, surface finish, and synergistic interactions between the impurity elements. The above studies culminated in two response surface analyses (RSA). The first was conducted on the effect of C and Fe on oxygen and deuterium pickup in Zr-2.5Nb drop castings corroded at 325 deg C in CANDU conditions. The second study was performed in autoclaves at 300 deg C on the affect of four impurity elements, C, Fe, Cr, and Si, in Zr-2.5Nb micro-tubes, which possess the same microstructure as full-size pressure tubes. The first RSA revealed a quadratic dependence of corrosion on C and Fe concentrations, with an optimum resistance at about 30 ppm (wt) C and 1100 ppm (wt) Fe. This has been partially confirmed by out-reactor corrosion of Zr-2.5Nb-Fe micro-pressure tubes. Trends in- and out-reactor were similar for oxidation but different in magnitude for deuterium pickup. There is no linear dependence on the Fe concentration in-reactor, implying that Fe and C form a complex. The second

  17. The production of reduced graphene oxide by a low-cost vacuum system for supercapacitors applications

    International Nuclear Information System (INIS)

    Cardoso, Q.A.; Sakata, S.K.; Faria, R.N.; Silva, F.M.; Vieira, L.S.; Casini, J.C.S.

    2016-01-01

    Graphene (G) has attracted great interest for its excellent electrical properties. However, the large-scale production of graphene is still currently under investigations. Graphene oxide (GO) can be partially reduced to graphene-like sheets by removing the oxygen-containing groups with the recovery of a conjugated structure. It can be produced using inexpensive graphite as raw material by cost-effective chemical methods. High vacuum and temperature (10 -7 mbar/1100 deg C) is well established as an effective route for reduced powder preparation on a laboratory scale. However, a high vacuum reduction system, which can be routinely operated at 10 -7 mbar, has a considerable capital, operational and maintenance cost to be used in a large scale. In the present work, a low-cost route aiming large scale reduction of graphene oxide has been investigated. A stainless steel vessel has been evacuated to backing-pump pressure (10 -2 mbar) to process graphene oxide at low and high temperatures. Attempts of reducing GO powder using low vacuum pressures have been carried out and investigated by X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). The experimental results of processing graphene oxide powder at various temperatures (200-1000°C) at relatively low pressures have been reported. The microstructures of the processed material have been investigated using scanning electron microscopy (SEM) and chemical microanalyses employing energy dispersive X-ray analysis (EDX). (author)

  18. Ni/YSZ microstructure optimization for long-term stability of solid oxide electrolysis cells

    DEFF Research Database (Denmark)

    Hauch, Anne; Brodersen, Karen; Karas, Filip

    2014-01-01

    of keeping the Ni particles in their required positions in the porous Ni/YSZ cermet close to the electrolyte. In this work we report cell tests and microstructures from reference and long-term tested SOEC with varied initial Ni/YSZ ratio with the aim of investigating the effect of changed Ni/YSZ ratio...

  19. Evolution of Near-Surface Internal and External Oxide Morphology During High-Temperature Selective Oxidation of Steels

    Science.gov (United States)

    Story, Mary E.; Webler, Bryan A.

    2018-05-01

    In this work we examine some observations made using high-temperature confocal scanning laser microscopy (HT-CSLM) during selective oxidation experiments. A plain carbon steel and advanced high-strength steel (AHSS) were selectively oxidized at high temperature (850-900°C) in either low oxygen or water vapor atmospheres. Surface evolution, including thermal grooving along grain boundaries and oxide growth, was viewed in situ during heating. Experiments investigated the influence of the microstructure and oxidizing atmosphere on selective oxidation behavior. Sequences of CSLM still frames collected during the experiment were processed with ImageJ to obtain histograms that showed a general darkening trend indicative of oxidation over time with all samples. Additional ex situ scanning electron microscopy and energy dispersive spectroscopy analysis supported in situ observations. Distinct oxidation behavior was observed for each case. Segregation, grain orientation, and extent of internal oxidation were all found to strongly influence surface evolution.

  20. Study on the influences of reduction temperature on nickel-yttria-stabilized zirconia solid oxide fuel cell anode using nickel oxide-film electrode

    Science.gov (United States)

    Jiao, Zhenjun; Ueno, Ai; Suzuki, Yuji; Shikazono, Naoki

    2016-10-01

    In this study, the reduction processes of nickel oxide at different temperatures were investigated using nickel-film anode to study the influences of reduction temperature on the initial performances and stability of nickel-yttria-stabilized zirconia anode. Compared to conventional nickel-yttria-stabilized zirconia composite cermet anode, nickel-film anode has the advantage of direct observation at nickel-yttria-stabilized zirconia interface. The microstructural changes were characterized by scanning electron microscopy. The reduction process of nickel oxide is considered to be determined by the competition between the mechanisms of volume reduction in nickel oxide-nickel reaction and nickel sintering. Electrochemical impedance spectroscopy was applied to analyze the time variation of the nickel-film anode electrochemical characteristics. The anode performances and microstructural changes before and after 100 hours discharging and open circuit operations were analyzed. The degradation of nickel-film anode is considered to be determined by the co-effect between the nickel sintering and the change of nickel-yttria-stabilized zirconia interface bonding condition.