Sample records for oxyselenides
-
Zhao, Xu-Wen; Gao, Guan-Yin; Yan, Jian-Min; Chen, Lei; Xu, Meng; Zhao, Wei-Yao; Xu, Zhi-Xue; Guo, Lei; Liu, Yu-Kuai; Li, Xiao-Guang; Wang, Yu; Zheng, Ren-Kui
2018-05-01
Copper-based ZrCuSiAs-type compounds of LnCuChO (Ln =Bi and lanthanides, Ch =S , Se, Te) with a layered crystal structure continuously attract worldwide attention in recent years. Although their high-temperature (T ≥ 300 K) electrical properties have been intensively studied, their low-temperature electronic transport properties are little known. In this paper, we report the integration of ZrCuSiAs-type copper oxyselenide thin films of B i0.94P b0.06CuSeO (BPCSO) with perovskite-type ferroelectric Pb (M g1 /3N b2 /3 ) O3-PbTi O3 (PMN-PT) single crystals in the form of ferroelectric field effect devices that allow us to control the electronic properties (e.g., carrier density, magnetoconductance, dephasing length, etc.) of BPCSO films in a reversible and nonvolatile manner by polarization switching at room temperature. Combining ferroelectric gating and magnetotransport measurements with the Hikami-Larkin-Nagaoka theory, we demonstrate two-dimensional (2D) electronic transport characteristics and weak antilocalization effect as well as strong carrier-density-mediated competition between weak antilocalization and weak localization in BPCSO films. Our results show that ferroelectric gating using PMN-PT provides an effective and convenient approach to probe the carrier-density-related 2D electronic transport properties of ZrCuSiAs-type copper oxyselenide thin films.
-
Electrical resistivity, optical and magnetic properties of the layered oxyselenide SmCuOSe
International Nuclear Information System (INIS)
Llanos, Jaime; Pena, Octavio
2005-01-01
The electrical and magnetic properties of the tetragonal phase SmCuOSe are reported as a function of the temperature. The optical properties were studied by means of diffuse reflectance spectrum in the UV-Vis range. The electrical resistivity measurements as well as diffuse reflectance spectrum show that SmCuOSe is a semiconductor with an optical band gap (E g ) of 2.6eV. In this phase, Cu is at its monovalent oxidation state and, as such, it does not contribute to the total magnetic moment, whereas Sm is in its 3+ oxidation state, with a large VanVleck contribution due to the admixture of the fundamental state with higher energy levels
-
Synthesis and characterization of rare-earth oxide transition-metal arsenides and selenides
Energy Technology Data Exchange (ETDEWEB)
Peschke, Simon Friedrich
2017-04-06
The present thesis includes two different quaternary systems that have been studied extensively. On the one hand, several samples of the REFeAsO{sub 1-x}F{sub x} family of iron-based superconductors were prepared using a novel solid state metathesis reaction, which also provided a possibility to prepare late rare-earth compounds of this family at ambient pressure. Comparison of structural and physical properties of those samples with samples from conventional solid state and high pressure syntheses revealed both, commonalities as well as striking differences. The observations gave reason to the conclusion that superconducting properties strongly depend, beside electronic infl uence, on the structural parameters. On the other hand, the quaternary system RE-T-Se-O with T = Ti-Mn was investigated using a NaI/KI flux mediated synthesis route. It has been shown that oC -La{sub 2}O{sub 2}MnSe{sub 2} is exclusively accessible in su fficient purity by the use of a fl ux material. Therefore, further syntheses in this quaternary system were performed by a flux mediated synthesis route leading to a large amount of new materials. Among them, a new polymorph mC-La{sub 2}O{sub 2}MnSe{sub 2} which forms, together with La{sub 4}MnSe{sub 3}O{sub 4} and La{sub 6}MnSe{sub 4}O{sub 6}, the series La{sub 2n+2}MnSe{sub n+2}O{sub 2n+2}. In addition, the alternative preparation method also enabled a large scale synthesis of the first examples of rare-earth chromium oxyselenides with chromium in the oxidation state +II, namely RE{sub 2}CrSe{sub 2}O{sub 2} (RE = La-Nd), which opened the door to study their magnetism in detail by powder neutron diffraction and muon spin rotation techniques. Research into the La-V-Se-O system revealed the first fi ve quaternary compounds of this family with interesting magnetic properties including ferromagnetism, antiferromagnetism, metamagnetism and more complex behaviour. In addition, the crystal structure of two new quaternary titanium containing
-
Synthesis and characterization of rare-earth oxide transition-metal arsenides and selenides
International Nuclear Information System (INIS)
Peschke, Simon Friedrich
2017-01-01
The present thesis includes two different quaternary systems that have been studied extensively. On the one hand, several samples of the REFeAsO_1_-_xF_x family of iron-based superconductors were prepared using a novel solid state metathesis reaction, which also provided a possibility to prepare late rare-earth compounds of this family at ambient pressure. Comparison of structural and physical properties of those samples with samples from conventional solid state and high pressure syntheses revealed both, commonalities as well as striking differences. The observations gave reason to the conclusion that superconducting properties strongly depend, beside electronic infl uence, on the structural parameters. On the other hand, the quaternary system RE-T-Se-O with T = Ti-Mn was investigated using a NaI/KI flux mediated synthesis route. It has been shown that oC -La_2O_2MnSe_2 is exclusively accessible in su fficient purity by the use of a fl ux material. Therefore, further syntheses in this quaternary system were performed by a flux mediated synthesis route leading to a large amount of new materials. Among them, a new polymorph mC-La_2O_2MnSe_2 which forms, together with La_4MnSe_3O_4 and La_6MnSe_4O_6, the series La_2_n_+_2MnSe_n_+_2O_2_n_+_2. In addition, the alternative preparation method also enabled a large scale synthesis of the first examples of rare-earth chromium oxyselenides with chromium in the oxidation state +II, namely RE_2CrSe_2O_2 (RE = La-Nd), which opened the door to study their magnetism in detail by powder neutron diffraction and muon spin rotation techniques. Research into the La-V-Se-O system revealed the first fi ve quaternary compounds of this family with interesting magnetic properties including ferromagnetism, antiferromagnetism, metamagnetism and more complex behaviour. In addition, the crystal structure of two new quaternary titanium containing oxyselenides were identifi ed and revealed unique structural building blocks that have not been
-
Energy Technology Data Exchange (ETDEWEB)
Lü, Minfeng; Mentré, Olivier; Gordon, Elijah E.; Whangbo, Myung-Hwan; Wattiaux, Alain; Duttine, Mathieu; Tiercelin, Nicolas; Kabbour, Houria
2017-12-01
The layered oxysulfide Sr3Fe2O5Cu2S2 was prepared, and its crystal structure and magnetic properties were characterized by synchrotron X-ray diffraction (XRD), powder neutron diffraction (PND), Mössbauer spectroscopy measurements and by density functional theory (DFT) calculations. In addition, the spin exchange interactions leading to the ordered magnetic structure of Sr3Fe2O5Cu2S2 were compared with those of its selenium analogue Sr3Fe2O5Cu2Se2. The oxysulfide Sr3Fe2O5Cu2S2 adopts a G-type antiferromagnetic (AFM) structure at a temperature in the range 485–512 K, which is comparable with the three-dimensional (3D) AFM ordering temperature, TN ≈ 490 K, found for Sr3Fe2O5Cu2Se2. Consistent with this observation, the spin exchange interactions of the magnetic (Sr3Fe2O5)2+ layers are slightly greater (but comparable) for oxysulfide than for the oxyselenide. Attempts to reduce or oxidize Sr3Fe2O5Cu2S2 using topochemical routes yield metallic Fe.
-
The BiCu{sub 1−x}OS oxysulfide: Copper deficiency and electronic properties
Energy Technology Data Exchange (ETDEWEB)
Berthebaud, D.; Guilmeau, E.; Lebedev, O.I. [Laboratoire CRISMAT, UMR 6508 CNRS/ENSICAEN/UCBN, 6 bd du Maréchal Juin, F-14050 CAEN Cedex 4 (France); Maignan, A., E-mail: antoine.maignan@ensicaen.fr [Laboratoire CRISMAT, UMR 6508 CNRS/ENSICAEN/UCBN, 6 bd du Maréchal Juin, F-14050 CAEN Cedex 4 (France); Gamon, J.; Barboux, P. [Institut de Recherche de Chimie de Paris, Ecole Nationale Supérieure de Chimie de Paris, 11 rue Pierre et Marie Curie, 75231 Paris Cedex 09 France (France)
2016-05-15
An oxysulfide series of nominal compositions BiCu{sub 1−x}OS with x<0.20 has been prepared and its structural properties characterized by combining powder X-ray diffraction and transmission electron microscopy techniques. It is found that this oxysulfide, crystallizing in the P4/nmm space group, tends to adopt a constant amount of copper vacancy corresponding to x=0.05 in the BiCu{sub 1−x}OS formula. The presence of Cu vacancies is confirmed by HAADF-STEM analysis showing, in the Cu atomic columns, alternating peaks of different intensities in some very localized regions. For larger Cu deficiencies (x>0.05 in the nominal composition), other types of structural nanodefects are evidenced such as bismuth oxysulfides of the “BiOS” ternary system which might explain the report of superconductivity for the BiCu{sub 1−x}OS oxysulfide. Local epitaxial growth of the BiCuOS oxysulfide on top of CuO is also observed. In marked contrast to the BiCu{sub 1−x}OSe oxyselenide, these results give an explanation to the limited impact of Cu deficiency on the Seebeck coefficient in BiCu{sub 1−x}OS compounds. - Graphical abstract: High resolution TEM image showing a Bi(Cu)OS/Bi{sub 2}O{sub 2}S interface and corresponding dislocation region. The Bi(Cu)OS structure adopts a rather constant Cu content (near 0.95); starting from BiCuOS leads to the formation of defects such as the Bi{sub 2}O{sub 2}S oxysulfide.