  1. ATOMIC LAYER DEPOSITION OF TITANIUM OXIDE THIN FILMS ONNANOPOROUS ALUMINA TEMPLATES FOR MEDICAL APPLICATIONS

    Energy Technology Data Exchange (ETDEWEB)

    Brigmon, R.

    2009-05-05

    Nanostructured materials may play a significant role in controlled release of pharmacologic agents for treatment of cancer. Many nanoporous polymer materials are inadequate for use in drug delivery. Nanoporous alumina provides several advantages over other materials for use in controlled drug delivery and other medical applications. Atomic layer deposition was used to coat all the surfaces of the nanoporous alumina membrane in order to reduce the pore size in a controlled manner. Both the 20 nm and 100 nm titanium oxide-coated nanoporous alumina membranes did not exhibit statistically lower viability compared to the uncoated nanoporous alumina membrane control materials. In addition, 20 nm pore size titanium oxide-coated nanoporous alumina membranes exposed to ultraviolet light demonstrated activity against Escherichia coli and Staphylococcus aureus bacteria. Nanostructured materials prepared using atomic layer deposition may be useful for delivering a pharmacologic agent at a precise rate to a specific location in the body. These materials may serve as the basis for 'smart' drug delivery devices, orthopedic implants, or self-sterilizing medical devices.

  2. Alumina Template-Dependant Growth of Cobalt Nanowire Arrays

    Directory of Open Access Journals (Sweden)

    L. Malferrari

    2009-01-01

    Full Text Available Different electrochemical regimes and porous alumina were applied for template synthesis of cobalt nanowire (nw arrays, revealing several peculiar cases. In contrast to quite uniform filling of sulfuric acid alumina templates by alternating current deposition, nonuniform growth of the Co nw tufts and mushrooms was obtained for the case of oxalic acid templates. We showed herein for the first time that such configurations arise from the spontaneous growth of cobalt nw groups evolving from the cobalt balls at the Al/alumina interface. Nevertheless, the uniform growth of densely packed cobalt nw arrays, up to tens of micrometers in length, was obtained via long-term direct current galvanostatic deposition at low current density using oxalic acid templates one-side coated by conducting layer. The unique point of this regime is the formation of hexagonal lattice Co nws with a preferred (100 growth direction.

  3. Ordered Nanomaterials Thin Films via Supported Anodized Alumina Templates

    Directory of Open Access Journals (Sweden)

    Mohammed eES-SOUNI

    2014-10-01

    Full Text Available Supported anodized alumina template films with highly ordered porosity are best suited for fabricating large area ordered nanostructures with tunable dimensions and aspect ratios. In this paper we first discuss important issues for the generation of such templates, including required properties of the Al/Ti/Au/Ti thin film heterostructure on a substrate for high quality templates. We then show examples of anisotropic nanostructure films consisting of noble metals using these templates, discuss briefly their optical properties and their applications to molecular detection using surface enhanced Raman spectroscopy. Finally we briefly address the possibility to make nanocomposite films, exemplary shown on a plasmonic-thermochromic nanocomposite of VO2-capped Au-nanorods.

  4. Electroless Fabrication of Cobalt Alloys Nanowires within Alumina Template

    Directory of Open Access Journals (Sweden)

    Nazila Dadvand

    2007-01-01

    Full Text Available A new method of nanowire fabrication based on electroless deposition process is described. The method is novel compared to the current electroless procedure used in making nanowires as it involves growing nanowires from the bottom up. The length of the nanowires was controlled at will simply by adjusting the deposition time. The nanowires were fabricated within the nanopores of an alumina template. It was accomplished by coating one side of the template by a thin layer of palladium in order to activate the electroless deposition within the nanopores from bottom up. However, prior to electroless deposition process, the template was pretreated with a suitable wetting agent in order to facilitate the penetration of the plating solution through the pores. As well, the electroless deposition process combined with oblique metal evaporation process within a prestructured silicon wafer was used in order to fabricate long nanowires along one side of the grooves within the wafer.

  5. High field matching effects in superconducting Nb porous arrays catalyzed from anodic alumina templates

    DEFF Research Database (Denmark)

    Vinckx, W.; Vanacken, J.; Moshchalkov, V.V.;

    2007-01-01

    Vortex pinning in a superconducting Nb thin film deposited on an anodically grown alumina template is investigated. Anodic oxidation of aluminium layers permits under specific conditions the formation of highly ordered porous alumina, a membrane-like structure consisting of triangular arrays...... of parallel pores. Its pore diameter and interpore distance are set by careful tuning of the anodization parameters. A superconducting Nb thin film is deposited directly onto the alumina film. The porous alumina acts as a template and it allows Nb to form a periodic pinning array during its growth. Pinning...

  6. Vertically aligned nanowires on flexible silicone using a supported alumina template prepared by pulsed anodization

    DEFF Research Database (Denmark)

    Mátéfi-Tempfli, Stefan; Mátéfi-Tempfli, M.

    2009-01-01

    Carpets of vertically aligned nanowires on flexible substrates are successfully realized by a template method. Applying special pulsed anodization conditions, defect-free nanoporous alumina structures supported on polydimethylsiloxane (PDMS), a flexible silicone elastomer, are created. By using...

  7. Porous Aluminas: The bio template method for the synthesis of stable high surface area aluminas; Aluminas porosas: El metodo de bio-replica para la sintesis de aluminas estables de alta superficie especifica

    Energy Technology Data Exchange (ETDEWEB)

    Benitez Guerrero, M.; Perez Maqueda, L.; Pena Castro, P.; Pascual Cosp, J.

    2013-07-01

    Development of porous alumina has been the objective of numerous studies in recent decades, due to the intrinsic properties of aluminium oxide, such as high melting point, low thermal conductivity, chemical inertness and corrosion resistance which, in addition to a high surface area and permeability, make aluminas being used for many different industrial and technical applications. The crystallographic and textural stability of alumina acquires significant importance in those processes involving high temperatures; however, most of the synthesis methods yield metastable oxides of little interest in high-temperature processes due to the transformation to alpha phase, with the consequent reduction in surface area. The present article reviews diverse procedures for obtaining porous alumina with high specific surface area, including methods and strategies for preparing high surface alpha-alumina. Within this framework, the paper analyzes the results obtained through bio replica of lignocellulose materials. This technology allows preparing aluminas with the complex structural hierarchy of the lignocellulose templates. (Author)

  8. NOTE: Fabrication of a gecko-like hierarchical fibril array using a bonded porous alumina template

    Science.gov (United States)

    Suryadi Kustandi, Tanu; Samper, Victor Donald; Ng, Wan Sing; Chong, Ai Shing; Gao, Han

    2007-10-01

    We report a new method to fabricate a hierarchical microfibril array by using bonded porous alumina templates. The fabrication approach extends a powerful and well-established technique of creating porous alumina to create a polymer multilevel structure, mimicking the hierarchical structure of gecko adhesive foot hairs. The nanoporous alumina (pore diameter ≈60 nm; interpore distance ≈100 nm) was generated by the anodization of an aluminum film in an oxalic acid solution. The microporous alumina was produced by exploiting the parallel wafer-scale processing of conventional lithography and anisotropic chemical etching of the thick film of anodic alumina pores. The micro- and nanoporous alumina membranes were subsequently brought into intimate contact and their bonding was accomplished by means of capillary forces and then van der Waals bonding. Hierarchical polymeric microfibrils (fibril diameter ≈10 µm fibril length ≈70 µm) with nanofibril arrays at their tips were obtained after depositing a desired material into the pores and selective etching of the template membranes. The nanofibril has a lateral dimension of approximately 60 nm with length-to-diameter aspect ratios as high as 100:1.

  9. Synthesis of mesoporous alumina using polyvinyl alcohol template as porosity control additive

    Directory of Open Access Journals (Sweden)

    Zoltán Ecsedi

    2007-12-01

    Full Text Available The effects of polyvinyl alcohol (PVA template and calcinations temperatures on the characteristics of the alumina films were investigated. The samples were prepared by sol-gel method using aluminium triisopropylate precursor. The variation of microstructure, pore size and pore volume, were determined by nitrogen adsorption/desorption analysis and the macropore size distribution was determined using mercury porosimetry. TEM and SEM were used to observe the texture of these samples and the particle morphology. Experimental observation after drying and annealing shows that it is possible to produce crack free nanoporous alumina films using polyvinyl alcohol template. The obtained alumina samples have macroporous microstructure (with the average pore diameter dav = 34.9 μm, for sample prepared with 42.5 wt% of PVA addition and annealed at 1000°C with high portion of mesopores (with the average pore diameter Dav = 14.0 nm for the same sample.

  10. Unifying the templating effects of porous anodic alumina on metallic nanoparticles for carbon nanotube synthesis

    Energy Technology Data Exchange (ETDEWEB)

    Haase, Mark R., E-mail: Mark.R.Haase@gmail.com, E-mail: haasemr@mail.uc.edu; Alvarez, Noe T.; Malik, Rachit; Schulz, Mark; Shanov, Vesselin [580 Engineering Research Center, Department of Biomedical, Chemical and Environmental Engineering (United States)

    2015-09-15

    Carbon nanotubes (CNTs) are a promising material for many applications, due to their extraordinary properties. Some of these properties vary in relation to the diameter of the nanotubes; thus, precise control of CNT diameter can be critical. Porous anodic alumina (PAA) membranes have been successfully used to template electrodeposited catalyst. However, the catalysts used in CNT synthesis are frequently deposited with more precise techniques, such as electron beam deposition. We test the efficacy of PAA as a template for electron beam-deposited catalyst by studying the diameter distribution of CNTs grown catalyst of various thicknesses supported by PAA. These are then compared by ANOVA to the diameter distributions of CNTs grown on metal catalyst supported by a conventional alumina film. These results also allow a unified description of two templating effects, the more common particles-in-pores model, and the recently described particles-between-pores.

  11. Properties of Ni and Ni–Fe nanowires electrochemically deposited into a porous alumina template

    Directory of Open Access Journals (Sweden)

    Alla I. Vorobjova

    2016-11-01

    Full Text Available The comparative analysis of the electrochemical deposition of Ni and Ni–Fe nanowires (NWs into ordered porous alumina templates is presented. The method developed allows for obtaining NWs of 50 ± 5 nm in diameter and 25 μm in length, i.e., with an aspect ratio of 500. XRD data demonstrate the polycrystalline nature of Ni and Ni–Fe in a face-centered cubic close-packed lattice. Both fabricated materials, Ni and Ni–Fe, have shown ferromagnetic properties. The specific magnetization value of Ni–Fe NWs in the alumina template is higher than that of the Ni sample and bulk Ni, also the Curie temperature of the Ni–Fe sample (790 K is higher than that of the Ni sample one or bulk Ni.

  12. Hemispherical Shell Nanostructures from Metal-Stripped Embossed Alumina on Aluminum Templates

    DEFF Research Database (Denmark)

    Nielsen, Peter; Albrektsen, Ole; Simonsen, Adam Cohen

    2011-01-01

    aluminum/ alumina (Al/Al2O3) templates as a novel and versatile nanofabrication procedure, and we demonstrate explicitly how to exploit the technique for developing large-area hexagonally close-packed hemispherical shell nanostructures by stripping noble metal layers from embossed templates fabricated from...... anodized Al. Utilizing for this process the linear relationship between anodization voltage and the resulting interpore distance in the formed oxide, it is possible to tune the radius of curvature of the resulting hemispherical shells continuously, which in turn results in tunable optical properties...

  13. Commercial alumina templates as base to fabricate 123-type high-T{sub c} superconductor nanowires

    Energy Technology Data Exchange (ETDEWEB)

    Koblischka, M.R.; Zeng, X.L.; Hartmann, U. [Institute of Experimental Physics, Saarland University, P. O. Box 151150, 66041 Saarbruecken (Germany)

    2016-04-15

    Nanowires of high-T{sub c} superconductors of the RE-123 type (RE = rare earths) were grown by the anodized alumina template method, employing commercially available alumina templates with nominal pore diameters of 20 and 100 nm. Pre-reacted YBa{sub 2}Cu{sub 3}O{sub x} (YBCO) and NdBa{sub 2}Cu{sub 3}O{sub x} (NdBCO) powder was molten on top of the templates in order to fill the pores with the 123-type material. The resulting samples were oxygen-annealed at 450 C. Superconductivity with a transition temperature of 88 K (YBCO) and 96 K (NdBCO) was confirmed by means of magnetic susceptibility measurements (SQUID) using pieces of the filled template. The electric (resistance) and magnetic measurements revealed further relatively sharp superconducting transitions. To understand the dimensions of the resulting nanowires (length up to 10 μm, diameter between 100 and 250 nm), which do not correspond to the nominal pore diameters, the empty and filled commercial templates were analyzed in detail by scanning electron microscopy. We discuss the feasibility of this approach to produce larger amounts of nanowires. (copyright 2015 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  14. Preparation of High Surface Area, Large Pore Volume Alumina by Using β-Cyclodextrin as a Non-surfactant Template

    Institute of Scientific and Technical Information of China (English)

    Lai Jun WANG; Ming Fen WEN; Yu Shan LI; Dong YANG; Jing CHEN; Chong Li SONG

    2006-01-01

    A series of alumina samples were prepared using β-cyclodextrin as the non-surfactant template. These samples were characterized by XRD, BET and TEM. The results showed that the alumina samples prepared using β-cyclodextrin template had the higher surface areas (124-484 m2/g), larger pore volumes (0.7-1.27 mL/g) and more thermal stability than samples prepared without using β-cyclodextrin.

  15. Structure of the carbon nanofilaments formed by liquid phase carbonization in porous anodic alumina template

    OpenAIRE

    Habazaki, H.; Kiriu, M.; M. Hayashi; Konno, H.

    2007-01-01

    Platelet structure carbon nanofilaments of ~30 nm in diameter have been prepared by heating a mixture of porous anodic alumina template and poly(vinyl)chloride (PVC) powders in an argon atmosphere, and the change in their structure and morphology with heat treatment temperature, ranging from 600 to 2800 °C, has been examined using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and nitrogen gas adsorption measurements. The diameter of the ca...

  16. Frequency Shifts of Luminescence for ZnO Nanoparticles in Porous Alumina Template

    Institute of Scientific and Technical Information of China (English)

    2006-01-01

    ZnO nanoparticles in porous anodized alumina were fabricated by sol-gel method. The PL spectra of pure ZnO nanoparticles, porous alumina template and the ZnO/PAA composite system were investigated after annealed at different temperatures. The annealing of ZnO/PAA composite system displays very complicated behavior, where changing of luminescence intensity and a "red shift" of emission frequency were observed at less or higher than 500 ℃ of the annealing temperature, respectively. To explain the phenomenon, it is considered that the emission origin of the green luminescence of ZnO nanoparticles came from OZn. It is suggested that the ZnO/PAA composite system should be annealed at the temperature above 500 ℃ in order to get intense luminescence of ZnO nanoparticle.

  17. A Reliable Method for the Preparation of Multiporous Alumina Monoliths by Ice-Templating

    Directory of Open Access Journals (Sweden)

    Jérémy Dhainaut

    2016-03-01

    Full Text Available Alumina supports presenting a bimodal porosity are generally advantageous for the conversion of bulky molecules such as found in biomass, refining, and petrochemistry. However, shaping of such materials, while controlling pores size and orientation, proves to be hard. This problem can be tackled by using a simple method involving sol-gel chemistry, surfactant self-assembly, and ice-templating. Herein, a systematic study of the formulation and process parameters’ influence on the final material properties is presented. This protocol results in the repeatable preparation of centimeter-sized alumina monoliths presenting a uni-directional macroporosity and structured mesopores. These monoliths should be of particular interest in high flow rate catalytic applications.

  18. Fabrication of TiO2 Nanotanks Embedded in a Nanoporous Alumina Template

    Directory of Open Access Journals (Sweden)

    C. Massard

    2015-01-01

    Full Text Available The feasibility of surface nanopatterning with TiO2 nanotanks embedded in a nanoporous alumina template was investigated. Self-assembled anodized aluminium oxide (AAO template, in conjunction with sol gel process, was used to fabricate this nanocomposite object. Through hydrolysis and condensation of the titanium alkoxide, an inorganic TiO2 gel was moulded within the nanopore cavities of the alumina template. The nanocomposite object underwent two thermal treatments to stabilize and crystallize the TiO2. The morphology of the nanocomposite object was characterized by Field Emission Scanning Electron Microscopy (FESEM. The TiO2 nanotanks obtained have cylindrical shapes and are approximately 69 nm in diameter with a tank-to-tank distance of 26 nm. X-ray diffraction analyses performed by Transmission Electron Microscopy (TEM with selected area electron diffraction (SAED were used to investigate the TiO2 structure. The optical properties were studied using UV-Vis spectroscopy.

  19. Self-organized magnetic nanowire arrays based on alumina and titania templates.

    Science.gov (United States)

    Prida, V M; Pirota, K R; Navas, D; Asenjo, A; Hernández-Vélez, M; Vázquez, M

    2007-01-01

    Densely packed arrays of magnetic nanowires have been synthesized by electrodeposition filling of nanopores in alumina and titania membranes formed by self-assembling during anodization process. Emphasis is made on the control of the production parameters leading to ordering degree and lattice parameter of the array as well as nanowires diameter and length. Structural, morphological and magnetic properties exhibited by nanowire arrays have been studied for several nanowire compositions, different ordering degree and for different nanowire aspect ratios. The magnetic behaviour of nanowires array is governed by the balance between different energy contributions: shape anisotropy of individual nanowires, the magnetostatic interaction of dipolar origin among nanowires, and magnetocrystalline and magnetoelastic anisotropies induced by the pattern templates. These novel nanocomposites, based on ferromagnetic nanowires embedded in anodic nanoporous templates, are becoming promising candidates for technological applications such as functionalised arrays for magnetic sensing, ultrahigh density magnetic storage media or spin-based electronic devices.

  20. Porous anodic alumina on galvanically grown PtSi layer for application in template-assisted Si nanowire growth

    Directory of Open Access Journals (Sweden)

    Stavrinidou Eleni

    2011-01-01

    Full Text Available Abstract We report on the fabrication and morphology/structural characterization of a porous anodic alumina (PAA/PtSi nano-template for use as matrix in template-assisted Si nanowire growth on a Si substrate. The PtSi layer was formed by electroless deposition from an aqueous solution containing the metal salt and HF, while the PAA membrane by anodizing an Al film deposited on the PtSi layer. The morphology and structure of the PtSi layer and of the alumina membrane on top were studied by Scanning and High Resolution Transmission Electron Microscopies (SEM, HRTEM. Cross sectional HRTEM images combined with electron diffraction (ED were used to characterize the different interfaces between Si, PtSi and porous anodic alumina.

  1. Substrate integrated waveguide isolator based on ferromagnetic nanowires in porous alumina template

    Science.gov (United States)

    Van Kerckhoven, Vivien; Piraux, Luc; Huynen, Isabelle

    2014-11-01

    We demonstrate the operation of a fully integrated and miniaturized waveguide based on ferromagnetic nanowires as a promising alternative to macroscopic ferrite slab-loaded metallic rectangular waveguides used as microwave isolators. Nanowires of various heights are selectively grown at dedicated areas into a low-loss nanoporous alumina template in order to create the shielding walls of a Substrate Integrated Waveguide (SIW) topology and the ferromagnetic slab supporting a circularly polarized nonreciprocal propagation. A model is proposed for the microwave response of the SIW and its non-reciprocity, which takes into account the substrate permittivity and the tensorial permeability of the ferromagnetic nanowires, and its predictions are validated by measurements. A significant isolation of 7 dB/cm is obtained experimentally at 13.5 GHz, without the need of a DC bias magnetic field.

  2. Structure of the carbon nanofilaments formed by liquid phase carbonization in porous anodic alumina template

    Energy Technology Data Exchange (ETDEWEB)

    Habazaki, H. [Graduate School of Engineering, Hokkaido University, N13-W8, Sapporo 060-8628 (Japan)], E-mail: habazaki@eng.hokudai.ac.jp; Kiriu, M.; Hayashi, M.; Konno, H. [Graduate School of Engineering, Hokkaido University, N13-W8, Sapporo 060-8628 (Japan)

    2007-10-15

    Platelet structure carbon nanofilaments of {approx}30 nm in diameter have been prepared by heating a mixture of porous anodic alumina template and poly(vinyl)chloride (PVC) powders in an argon atmosphere, and the change in their structure and morphology with heat treatment temperature, ranging from 600 to 2800 deg. C, has been examined using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and nitrogen gas adsorption measurements. The diameter of the carbon nanofilaments formed does not change with heat treatment temperature, being in agreement with the pore diameter of the template, while their length is reduced with the temperature. The platelet-type orientation of graphene layers is evident even at 600 deg. C with the layer structure further developing with increasing heat treatment temperature. The carbon nanofilaments formed at lower temperatures have micropores, while those formed at higher temperatures do not have porosity. Highly graphitized carbon nanofilaments have been obtained after heat treatment at 2800 deg. C, with another characteristic structural feature being presence of loops at the edge of graphene layers formed at 2800 deg. C.

  3. Self-Ordered Nanoporous Alumina Templates Formed by Anodization of Aluminum in Oxalic Acid

    Science.gov (United States)

    Vida-Simiti, Ioan; Nemes, Dorel; Jumate, Nicolaie; Thalmaier, Gyorgy; Sechel, Niculina

    2012-10-01

    Anodic aluminum oxide (AAO) membranes with highly ordered nanopores serve as ideal templates for the formation of various nanostructured materials. The procedure of the template preparation is based on a two-step self-organized anodization of aluminum. In the current study, AAO templates were fabricated in 0.3 M oxalic acid under the anodizing potential range of 30-60 V at an electrolyte temperature of ~5°C. The AAO templates were analyzed using scanning electron microscopy, x-ray diffraction, Fourier-transform infrared spectroscopy, and differential thermal analysis. The as obtained layers are amorphous; the mean pore size is between 40 nm and 75 nm and increases with the increase of the anodization potential. Well-defined pores across the whole aluminum template, a pore density of ~1010 pores/cm2, and a tendency to form a porous structure with hexagonal symmetry were observed.

  4. Electrochemical growth of ZnO nanowires inside nanoporous alumina templates. A comparison with metallic Zn nanowires growth

    Energy Technology Data Exchange (ETDEWEB)

    Ramirez, Daniel [Instituto de Quimica, Pontificia Universidad Catolica de Valparaiso, Valparaiso (Chile); Laboratoire d' Electrochimie et Chimie Analytique (UMR CNRS 7575), Ecole Nationale Superieure de Chimie de Paris (ENSCP) (France); Pauporte, Thierry; Lincot, Daniel [Laboratoire d' Electrochimie et Chimie Analytique (UMR CNRS 7575), Ecole Nationale Superieure de Chimie de Paris (ENSCP) (France); Gomez, Humberto [Instituto de Quimica, Pontificia Universidad Catolica de Valparaiso, Valparaiso (Chile)

    2008-10-15

    Molecular oxygen reduction in presence of Zn(II) allowed to get arrays of zinc oxide (ZnO) nanowires (NWs) inside thick anodic alumina membranes (AAM), previously made by anodization in oxalic acid. A Zinc (Zn) NWs array made by electrochemical deposition (ED) was employed as a metal reference in order to compare its growth behavior with respect to that of ZnO, a semiconducting material. Chronoamperometric measurements for Zn NWs showed a typical response for metallic growth inside porous templates while ZnO NWs did not show this behavior. We observed that Zn NWs grew faster than ZnO NWs as checked by the electrical charge. SEM images showed the presence of ZnO NWs only after long deposition time. X-ray diffraction data confirmed the ZnO structure. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  5. Fabrication of Acrylonitrile-Butadiene-Styrene Nanostructures with Anodic Alumina Oxide Templates, Characterization and Biofilm Development Test for Staphylococcus epidermidis.

    Directory of Open Access Journals (Sweden)

    Camille Desrousseaux

    Full Text Available Medical devices can be contaminated by microbial biofilm which causes nosocomial infections. One of the strategies for the prevention of such microbial adhesion is to modify the biomaterials by creating micro or nanofeatures on their surface. This study aimed (1 to nanostructure acrylonitrile-butadiene-styrene (ABS, a polymer composing connectors in perfusion devices, using Anodic Alumina Oxide templates, and to control the reproducibility of this process; (2 to characterize the physico-chemical properties of the nanostructured surfaces such as wettability using captive-bubble contact angle measurement technique; (3 to test the impact of nanostructures on Staphylococcus epidermidis biofilm development. Fabrication of Anodic Alumina Oxide molds was realized by double anodization in oxalic acid. This process was reproducible. The obtained molds present hexagonally arranged 50 nm diameter pores, with a 100 nm interpore distance and a length of 100 nm. Acrylonitrile-butadiene-styrene nanostructures were successfully prepared using a polymer solution and two melt wetting methods. For all methods, the nanopicots were obtained but inside each sample their length was different. One method was selected essentially for industrial purposes and for better reproducibility results. The flat ABS surface presents a slightly hydrophilic character, which remains roughly unchanged after nanostructuration, the increasing apparent wettability observed in that case being explained by roughness effects. Also, the nanostructuration of the polymer surface does not induce any significant effect on Staphylococcus epidermidis adhesion.

  6. Synthesis of Nanorods Titanium Dioxide via Anodic Alumina Membrane Template and their Applications in Dye-Sensitized Solar Cells

    Science.gov (United States)

    Suryana, R.; Sehati; Kusumandari

    2016-08-01

    Titanium dioxide (TiO2) nanorods have been successfully synthesized through sol- gel method via Anodic Alumina Membrane (AAM) as template. AAM template was removed using 6 M NaOH solution to obtain TiO2 nanorods only. Then TiO2 nanorods were annealed at 400°C for 2 h. Phase TiO2 nanorods were characterized using X-Ray Diffraction (XRD) and morphology of TiO2 nanorods were observed using Atomic Force Microscopy (AFM). In addition, the I-V meter was used to determine the DSSC efficiency. The XRD patterns showed that all peaks of synthesized-TiO2 indicated anatase phase. AFM images confirmed that TiO2 nanorods have diameters in range 18-30 nm. TiO2 nanorods were mixed with TiO2 nanoparticles having 21 nm in size then it was applied in the DSSC with p-carotene from carrot as dye. The efficiency of DSSC using TiO2 mixed-nanorods and nanoparticles increase about 154.20% compare to using TiO2 nanoparticles only. It is considered that TiO2 nanorod structures can be effective in photon trapping thus many photon interact to dyes to produce many excited-electrons.

  7. Vortex pinning in superconducting Nb thin films deposited on nanoporous alumina templates

    DEFF Research Database (Denmark)

    Vinckx, W.; Vanacken, J.; Moshchalkov, V.V.

    2006-01-01

    We present a study of magnetization and transport properties of superconducting Nb thin films deposited on nanoporous aluminium oxide templates. Periodic oscillations in the critical temperature vs. field, matching effects in fields up to 700 mT and strongly enhanced critical currents were observ...... centers, which enhances vortex pinning in broad field and temperature ranges. © EDP Sciences/Società Italiana di Fisica/Springer-Verlag 2006....

  8. Fabrication of cobalt-nickel binary nanowires in a highly ordered alumina template via AC electrodeposition.

    Science.gov (United States)

    Ali, Ghafar; Maqbool, Muhammad

    2013-08-14

    Cobalt-nickel (Co-Ni) binary alloy nanowires of different compositions were co-deposited in the nanopores of highly ordered anodic aluminum oxide (AAO) templates from a single sulfate bath using alternating current (AC) electrodeposition. AC electrodeposition was accomplished without modifying or removing the barrier layer. Field emission scanning electron microscope was used to study the morphology of templates and alloy nanowires. Energy-dispersive X-ray analysis confirmed the deposition of Co-Ni alloy nanowires in the AAO templates. Average diameter of the alloy nanowires was approximately 40 nm which is equal to the diameter of nanopore. X-ray diffraction analysis showed that the alloy nanowires consisted of both hexagonal close-packed and face-centered cubic phases. Magnetic measurements showed that the easy x-axis of magnetization is parallel to the nanowires with coercivity of approximately 706 Oe. AC electrodeposition is very simple, fast, and is useful for the homogenous deposition of various secondary nanostuctured materials into the nanopores of AAO.

  9. Effect of process parameters on growth rate and diameter of nano-porous alumina templates

    Indian Academy of Sciences (India)

    P Chowdhury; K Raghuvaran; M Krishnan; Harish C Barshilia; K S Rajam

    2011-06-01

    Anodic aluminium oxide (AAO) template with hexagonal shaped nano-pores with high aspect ratio was fabricated by two-step anodization processes from high purity aluminium foil. It was observed that pore dimensions were affected by anodizing voltage, electrolyte temperature and the duration of anodization time. The vertical growth rate of the pores (10–250 nm/min) was found to vary exponentially with anodizing voltage; however, it exhibits linear increment with the electrolyte temperature. The measured pore diameter (50–130 nm) shows a linear variation with anodizing voltage. The bottom barrier oxide layer was etched out by pore widening treatment to obtain through holes.

  10. Electrochemical synthesis of CdS nanowires by underpotential deposition in anodic alumina membrane templates

    Energy Technology Data Exchange (ETDEWEB)

    Bicer, Mustafa; Aydin, Ali Osman [Department of Chemistry, Arts and Sciences Faculty, Sakarya University, 54187 Sakarya (Turkey); Sisman, Ilkay, E-mail: isisman@sakarya.edu.t [Department of Chemistry, Arts and Sciences Faculty, Sakarya University, 54187 Sakarya (Turkey)

    2010-04-15

    Cadmium sulfide (CdS) nanowires were electrosynthesized within the pores of the anodic alumina membranes (AAM) using underpotential deposition (UPD) through an electrochemical co-deposition at room temperature (25 deg. C). The nanowire arrays were grown from an aqueous solution of CdSO{sub 4}, ethylenediaminetetraacetic acid (EDTA), and Na{sub 2}S at pH 4.0. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), UV-vis absorption spectroscopy, and energy dispersive spectroscopy (EDS) were employed to characterize the nanowires. These nanowires have uniform diameters of approximately 90 nm, and their lengths are up to 7 mum. XRD analysis reveals that the electrosynthesized nanowires deposited at -500 mV (vs. Ag/AgCl) have a preferential orientation along (1 1 0) direction for hexagonal crystal. Electrochemical and EDS results of the deposits confirm that the atomic ratio of Cd to S is very close to 1:1 stoichiometry. UV-vis absorption measurement shows a blue-shifted absorption at 488 nm because of the quantum confinement at low dimensions.

  11. Direct electrical transport measurement on a single thermoelectric nanowire embedded in an alumina template.

    Science.gov (United States)

    Ben Khedim, Meriam; Cagnon, Laurent; Garagnon, Christophe; Serradeil, Valerie; Bourgault, Daniel

    2016-04-28

    Electrical conductivity is a key parameter to increase the performance of thermoelectric materials. However, the measurement of such performance remains complex for 1D structures, involving tedious processing. In this study, we present a non-destructive, rapid and easy approach for the characterization of electrical conductivity of Bi2Te3 based single nanowires. By controlling the nanowire overgrowth, each nanowire emerges in the form of a micrometric hemisphere constituting a unique contact zone for direct nanoprobing. As nanowires need no preliminary preparation and remain in their template during measurement, we avoid oxidation effects and time-consuming processing. Electrical transport results show a low nanowire resistivity for compact nanowires obtained at low overpotential. Such values are comparable to bulk materials and thin films. This method not only confirmed its reliability, but it could also be adopted for other semiconducting or metallic electrodeposited nanowires.

  12. Electrochemical Fabrication of Pd-Ag Alloy Nanowire Arrays in Anodic Alumina Oxide Template

    Institute of Scientific and Technical Information of China (English)

    Erhong YUE; Gang YU; Yuejun OUYANG; Baicheng WENG; Weiwei SI; Liyuan YE

    2008-01-01

    The synthesis of Pd-Ag alloy nanowires in nanopores of porous anodic aluminum oxide (AAO) template by electrochemical deposition technique was reported.Pd-Ag alloy nanowires with 16%-25% Ag content are expected to serve as candidates of useful nanomaterials for the hydrogen sensors.Scanning electron microscopy (SEM) and energy dispersed X-ray spectroscopy (EDX) were employed to characterize the morphologies and compositions of the Pd-Ag nanowires.X-ray diffraction (XRD) was used to characterize the phase properties of the Pd-Ag nanowires.Pd-Ag alloy nanowire arrays with 17.28%-23.76% Ag content have been successfully fabricated by applying potentials ranging from -0.8 to -1.0 V (vs SCE).The sizes of the alloy nanowires are in agreement with the diameter of AAO nanopores.The underpotential deposition of Ag+ on Pd and Au plays an important role in producing an exceptionally high Ag content in the alloy.Alloy compositions can still be controlled by adjusting the ion concentration ratio of Pd2+ and Ag+ and the electrodeposition processes.XRD shows that nanowires obtained are in the form of alloy of Pd and Ag.

  13. Investigation of CuInSe2 nanowire arrays with core-shell structure electrodeposited at various duty cycles into anodic alumina templates

    Science.gov (United States)

    Cheng, Yu-Song; Wang, Na-Fu; Tsai, Yu-Zen; Lin, Jia-Jun; Houng, Mau-Phon

    2017-02-01

    Copper indium selenide (CuInSe2) nanowire (NW) arrays were prepared at various electrolyte duty cycles by filling anodic alumina templates through the pulsed electrodeposition technique. X-ray diffraction and scanning electron microscopy (SEM) images showed that the nucleation mechanism of CuInSe2 NW arrays was affected by the electrodeposition duty cycle. Moreover, SEM images showed that the diameter and length of the NWs were 80 nm and 2 μm, respectively. Furthermore, PEDOT/CuInSe2 NW core-shell arrays were fabricated using surfactant-modified CuInSe2 NW surfaces showing the lotus effect. Transmission electron microscopy images confirmed that a core-shell structure was achieved. Current-voltage plots revealed that the CuInSe2 NW arrays were p-type semiconductors; moreover, the core-shell structure improved the diode ideality factor from 3.91 to 2.63.

  14. Magnetic and structural properties of electrodeposited CoPt and FePt nanowires in nanoporous alumina templates

    Energy Technology Data Exchange (ETDEWEB)

    Dahmane, Y [Laboratoire Louis Neel, CNRS, BP 166, 38042 Grenoble cedex 9 (France); Cagnon, L [Laboratoire de Cristallographie, CNRS, BP 166, 38042 Grenoble cedex 9 (France); Voiron, J [Laboratoire Louis Neel, CNRS, BP 166, 38042 Grenoble cedex 9 (France); Pairis, S [Laboratoire de Cristallographie, CNRS, BP 166, 38042 Grenoble cedex 9 (France); Bacia, M [Laboratoire de Cristallographie, CNRS, BP 166, 38042 Grenoble cedex 9 (France); Ortega, L [Laboratoire de Cristallographie, CNRS, BP 166, 38042 Grenoble cedex 9 (France); Benbrahim, N [Laboratoire de Materiaux, Electrochimie et Corrosion, BP 17, 15000 Tizi-Ouzou (Algeria); Kadri, A [Laboratoire de Materiaux, Electrochimie et Corrosion, BP 17, 15000 Tizi-Ouzou (Algeria)

    2006-11-07

    CoPt and FePt nanowire arrays were successfully prepared by electrodeposition into nanochannels of porous alumina membranes. The as-deposited CoPt alloy has a face centred cubic structure and displays soft magnetic properties. Heat treatment at 700 {sup 0}C for different durations, under vacuum condition was carried out in order to obtain the ordered face centred tetragonal phase L1{sub 0}, exhibiting hard magnetic properties. After annealing, arrays of nanowires actually show hard magnetic properties with coercive fields up to 1.1 T at room temperature. Phase transformation, structural and magnetic properties were analysed and necessary conditions to obtain optimum magnetic properties are concluded. The first results obtained with FePt nanowires denote a more complicated system since the as-deposited material shows no magnetization. Magnetism appears only after annealing at 700 {sup 0}C minimum. Coercivity up to 1.1 T has been obtained at room temperature but with inhomogeneous phase composition.

  15. Giant increase in the metal-enhanced fluorescence of organic molecules in nanoporous alumina templates and large molecule-specific red/blue-shift of the fluorescence peak.

    Science.gov (United States)

    Sarkar, S; Kanchibotla, B; Nelson, J D; Edwards, J D; Anderson, J; Tepper, G C; Bandyopadhyay, S

    2014-10-08

    The fluorescence of organic fluorophore molecules is enhanced when they are placed in contact with certain metals (Al, Ag, Cu, Au, etc.) whose surface plasmon waves couple into the radiative modes of the molecules and increase the radiative efficiency. Here, we report a hitherto unknown size dependence of this metal-enhanced fluorescence (MEF) effect in the nanoscale. When the molecules are deposited in nanoporous anodic alumina films with exposed aluminum at the bottom of the pores, they form organic nanowires standing on aluminum nanoparticles whose plasmon waves have much larger amplitudes. This increases the MEF strongly, resulting in several orders of magnitude increase in the fluorescence intensity of the organic fluorophores. The increase in intensity shows an inverse superlinear dependence on nanowire diameter because the nanowires also act as plasmonic "waveguides" that concentrate the plasmons and increase the coupling of the plasmons with the radiative modes of the molecules. Furthermore, if the nanoporous template housing the nanowires has built-in electric fields due to space charges, a strong molecule-specific red- or blue-shift is induced in the fluorescence peak owing to a renormalization of the dipole moment of the molecule. This can be exploited to detect minute amounts of target molecules in a mixture using their optical signature (fluorescence) despite the presence of confounding background signals. It can result in a unique new technology for biosensing and chemical sensing.

  16. Compositionally graded Fe(1-x)-Pt(x) nanowires produced by alternating current electrodeposition into alumina templates

    Science.gov (United States)

    Fardi-Ilkhchy, Ali; Nasirpouri, Farzad; Bran, Cristina; Vázquez, Manuel

    2016-12-01

    Fe(1-x)-Pt(x) (0length) were fabricated by alternating current (AC) electrodeposition into nanoporous aluminum oxide templates through a systematic approach. The effect of AC electrodeposition parameters such as frequency, voltage and electrolyte concentration on morphology and chemical composition of Fe-Pt alloy nanowires was studied. Based on experimental data, AC sine wave deposition at an intermediate voltage of 12 Vrms and a frequency of 50 Hz, produces nanowires with nearly stoichiometric composition (Fe42Pt58) and a reasonably good uniformity of pore filling. However, there is a gradual change of composition in Fe-Pt alloy nanowires along the length under certain AC parameters. The observed dependency of alloy composition on the deposition voltage and frequency of AC electrodeposition is explained by an interplay between reduction potentials and diffusion coefficients of Fe and Pt ions which makes FePt system able to access compositionally graded nanowires. Magnetic measurements of nanowires of as-deposited nanowires confirm that maximum coercivity of 1.55 kOe is observed for nearly stoichiometric composition which increases up to 1.81 kOe after thermal annealing at 550 °C.

  17. Hydrogen Production by Steam Reforming of Liquefied Natural Gas (LNG) Over Nickel-Phosphorus-Alumina Xerogel Catalyst Prepared by a Carbon-Templating Epoxide-Driven Sol-Gel Method.

    Science.gov (United States)

    Bang, Yongju; Park, Seungwon; Han, Seung Ju; Yoo, Jaekyeong; Choi, Jung Ho; Kang, Tae Hun; Lee, Jinwon; Song, In Kyu

    2016-05-01

    A nickel-phosphorus-alumina xerogel catalyst was prepared by a carbon-templating epoxide-driven sol-gel method (denoted as CNPA catalyst), and it was applied to the hydrogen production by steam reforming of liquefied natural gas (LNG). For comparison, a nickel-phosphorus-alumina xerogel catalyst was also prepared by a similar method in the absence of carbon template (denoted as NPA catalyst). The effect of carbon template addition on the physicochemical properties and catalytic activities of the catalysts in the steam reforming of LNG was investigated. Both CNPA and NPA catalysts showed excellent textural properties with well-developed mesoporous structure. However, CNPA catalyst retained a more reducible nickel aluminate phase than NPA catalyst. XRD analysis of the reduced CNPA and NPA catalysts revealed that nickel sintering on the CNPA catalyst was suppressed compared to that on the NPA catalyst. From H2-TPD and CH4-TPD measurements of the reduced CNPA and NPA catalysts, it was also revealed that CNPA catalyst with large amount of hydrogen uptake and strong hydrogen-binding sites showed larger amount of methane adsorption than NPA catalyst. In the hydrogen production by steam reforming of LNG, CNPA catalyst with large methane adsorption capacity showed a better catalytic activity than NPA catalyst.

  18. Fabrication of porous alumina templates with a large-scale tunable interpore distance in a H2C2O4-C2H5OH-H2O solution

    Institute of Scientific and Technical Information of China (English)

    LI Yi; LING ZhiYuan; WANG JinChi; GHEN ShuoShuo; HU Xing; HE XinHua

    2008-01-01

    Highly ordered porous alumina templates with a large-scale tunable interpore distance (100-445 nm) have been successfully fabricated under an electric field of 40-180 V by modifying oxalic acid solution with adequate alcohol. The results under our experimental conditions show that the phenomena of burning and breakdown during the high-field anodization process can be avoided by adding a proper amount of alcohol to the oxalic acid solution, An excellent linear relationship between interpore dis-tance and anodization voltage is obtained under 40-170 V, and the maximum anodization voltage that could be used to avoid burning and breakdown is 180 V.

  19. Poly(ethylene oxide)-poly(butylene oxide)-poly(ethylene oxide)-templated synthesis of mesoporous alumina: effect of triblock copolymer and acid concentration.

    Science.gov (United States)

    Materna, Kelly L; Grant, Stacy M; Jaroniec, Mietek

    2012-07-25

    Mesoporous alumina was synthesized via a one-pot self-assembly of aluminum isopropoxide and poly(ethylene oxide)-poly(butylene oxide)-poly(ethylene oxide) triblock copolymer in an acidic ethanol solution. The effects of the polymer concentration and nitric acid concentration, independently, on the adsorption properties (such as surface area, pore volume, microporosity, mesoporosity, and pore width) were studied. An increase in the specific surface area and the pore volume was seen for the samples containing a polymer/aluminum isopropoxide wt. ratio up to 0.71 and a polymer/acid wt ratio of 0.88. Titania isopropoxide was also added to the synthesis to illustrate the extension of this approach to alumina-based mixed metal oxides.

  20. 特殊型纳米多孔阳极氧化铝模板的制备%Fabrication of Special-Type Nanoporous Anodic Alumina Templates

    Institute of Scientific and Technical Information of China (English)

    叶秋梅; 宋晔; 刘鹏; 胡隽隽

    2011-01-01

    Porous anodic alumina(PAA) templates have been used widely and studied extensively due to their excellent mechanical and thermal stabilities,highly-ordered hexagonal nanochannel-array architecture and controllable pore structures.In recent years,significant progress has been made in the field of PAA synthesis and a variety of special type PAA templates have been prepared by precisely adjusting the anodizing conditions.By means of the special templates,many novel functional nanomaterials have been synthesized successfully via physical or chemical processing routes.After a brief introduction to the fabrication methods of conventional PAA templates,this paper presents a comprehensive review on the fabrication approaches of PAA templates with special nanopore arrays(e.g.,branched,serrated,bone-shaped or inverted cone nanopores);diamond,triangle or square pore patterns;modulated pore structures with different diameters,lengths,geometries,and periodicity.Several critical factors including the applied electric field,temperature,type and concentration of the electrolyte which determine the pore modulation of PAA are emphasized.Finally,the development trend and future prospects of the special templates are given.%多孔阳极氧化铝(PAA)模板具有六角有序排列的柱形孔,且孔径均匀可调,加之其良好的机械和热稳定性,在纳米材料领域得到了广泛研究和应用。近年来,人们通过改变铝阳极氧化条件制备出了多种特殊型纳米PAA模板,并利用这些模板结合物理或化学方法成功地合成了多种新型纳米功能材料。本文在简要介绍常规纳米PAA模板制备的基础上,较全面地综述了诸如孔道呈分叉形、锯齿形、骨形、倒圆锥形,孔洞呈菱形、三角形、正方形,孔道或孔壁结构呈周期性变化等特殊型纳米PAA模板的制备,揭示了电场强度和电解液种类、温度在PAA孔洞形貌尺寸调控方面的重要性,并展望了这类模板的发展方向及应用前景。

  1. Improvement of Method to Prepare Porous Anodic Alumina Template%多孔阳极氧化铝(PAA)模板制备方法的改进

    Institute of Scientific and Technical Information of China (English)

    高明

    2016-01-01

    通过改进制备方法成功制备出高度有序的多孔阳极氧化铝(porous anodic alumina,P从)模板.对称结构的电解池两侧容室使用等量的、相同浓度的稀硫酸电解液,能够同时对两片铝片接触电解液的面进行阳极氧化,更好的平衡了铝片两侧的压力,有利于提高所制备模板的有序度,同时提高了制备效率.

  2. Vertical Carbon Nanotube Device in Nanoporous Templates

    Science.gov (United States)

    Maschmann, Matthew Ralph (Inventor); Fisher, Timothy Scott (Inventor); Sands, Timothy (Inventor); Bashir, Rashid (Inventor)

    2014-01-01

    A modified porous anodic alumina template (PAA) containing a thin CNT catalyst layer directly embedded into the pore walls. CNT synthesis using the template selectively catalyzes SWNTs and DWNTs from the embedded catalyst layer to the top PAA surface, creating a vertical CNT channel within the pores. Subsequent processing allows for easy contact metallization and adaptable functionalization of the CNTs and template for a myriad of applications.

  3. Synthesis and characterization of single-crystalline alumina nanowires

    Institute of Scientific and Technical Information of China (English)

    ZHAO Qing; XU Xiang-yu; ZHANG Hong-zhou; CHEN Yao-feng; XU Jun; YU Da-peng

    2005-01-01

    Alumina nanowires were synthesized on large-area silicon substrate via simple thermal evaporation method of heating a mixture of aluminum and alumina powders without using any catalyst or template. The phase structure and the surface morphology of the as-grown sample were analyzed by X-ray diffractometry(XRD) and scanning electron microscopy (SEM), respectively. The chemical composition and the microstructure of the as-grown alumina nanowires were characterized using transmission electron microscope(TEM). The nanowires are usually straight and the single crystalline has average diameter of 40 nm and length of 3 - 5 μm. The growth direction is along the [002] direction. Well aligned alumina nanowire arrays were observed on the surface of many large particles. The catalyst-free growth of the alumina nanowires was explained under the framework of a vapor-solid(VS)growth mechanism. This as-synthesized alumina nanowires could find potential applications in the fabrication of nanodevices.

  4. Challenges and Strategies in the Synthesis of Mesoporous Alumina Powders and Hierarchical Alumina Monoliths

    Directory of Open Access Journals (Sweden)

    Anne Galarneau

    2012-02-01

    Full Text Available A new rapid, very simple and one-step sol-gel strategy for the large-scale preparation of highly porous γ-Al2O3 is presented. The resulting mesoporous alumina materials feature high surface areas (400 m2 g−1, large pore volumes (0.8 mL g−1 and the ��-Al2O3 phase is obtained at low temperature (500 °C. The main advantages and drawbacks of different preparations of mesoporous alumina materials exhibiting high specific surface areas and large pore volumes such as surfactant-nanostructured alumina, sol-gel methods and hierarchically macro-/mesoporous alumina monoliths have been analyzed and compared. The most reproducible synthesis of mesoporous alumina are given. Evaporation-Induced Self-Assembly (EISA is the sole method to lead to nanostructured mesoporous alumina by direct templating, but it is a difficult method to scale-up. Alumina featuring macro- and mesoporosity in monolithic shape is a very promising material for in flow applications; an optimized synthesis is described.

  5. Template-assisted synthesis and characterisation of quasi-one-dimensional ceramic nanomaterials

    OpenAIRE

    2010-01-01

    The major results of the present work are the template-assisted (porous alumina or polycarbonate) manufacturing of nanowires, nanorods or nanotubes with tailored dimensions, composition, and physical-chemical properties, as well as optimisation of routine producing of alumina templates with the nanochannels open through from both ends. A successful attempt to alter the geometry of silicon-based ceramic nanowires by means of anodic alumina pore size tailoring has been made. However, diverse op...

  6. POROUS MEMBRANE TEMPLATED SYNTHESIS OF POLYMER PILLARED LAYER

    Institute of Scientific and Technical Information of China (English)

    Zhong-wei Niu; Dan Li; Zhen-zhong Yang

    2003-01-01

    The anodic porous alumina membranes with a definite pore diameter and aspect ratio were used as templates to synthesize polymer pillared layer structures. The pillared polymer was produced in the template membrane pores, and the layer on the template surfaces. Rigid cured epoxy resin, polystyrene and soft hydrogel were chosen to confirm the methodology. The pillars were in the form of either tubes or fibers, which were controlled by the alumina membrane pore surface wettability. The structural features were confirmed by scanning electron microscopy results.

  7. Porous Alumina Films with Width-Controllable Alumina Stripes

    Directory of Open Access Journals (Sweden)

    Huang Shi-Ming

    2010-01-01

    Full Text Available Abstract Porous alumina films had been fabricated by anodizing from aluminum films after an electropolishing procedure. Alumina stripes without pores can be distinguished on the surface of the porous alumina films. The width of the alumina stripes increases proportionally with the anodizing voltage. And the pores tend to be initiated close to the alumina stripes. These phenomena can be ascribed to the electric field distribution in the alumina barrier layer caused by the geometric structure of the aluminum surface.

  8. Porous Alumina Films with Width-Controllable Alumina Stripes.

    Science.gov (United States)

    Huang, Kai; Huang, Shi-Ming; Pu, Lin; Shi, Yi; Wu, Zhi-Ming; Ji, Li; Kang, Jun-Yong

    2010-08-21

    Porous alumina films had been fabricated by anodizing from aluminum films after an electropolishing procedure. Alumina stripes without pores can be distinguished on the surface of the porous alumina films. The width of the alumina stripes increases proportionally with the anodizing voltage. And the pores tend to be initiated close to the alumina stripes. These phenomena can be ascribed to the electric field distribution in the alumina barrier layer caused by the geometric structure of the aluminum surface.

  9. Reuse of activated alumina

    Energy Technology Data Exchange (ETDEWEB)

    Hobensack, J.E. [Martin Marietta Energy Systems, Inc., Piketon, OH (United States)

    1991-12-31

    Activated alumina is used as a trapping media to remove trace quantities of UF{sub 6} from process vent streams. The current uranium recovery method employs concentrated nitric acid which destroys the alumina pellets and forms a sludge which is a storage and disposal problem. A recently developed technique using a distilled water rinse followed by three dilute acid rinses removes on average 97% of the uranium, and leaves the pellets intact with crush strength and surface area values comparable with new material. Trapping tests confirm the effectiveness of the recycled alumina as UF{sub 6} trapping media.

  10. Behavior of alumina barrier layer in the supporting electrolytes for deposition of nanowired materials

    Energy Technology Data Exchange (ETDEWEB)

    Jagminas, Arunas, E-mail: jagmin@ktl.mii.l [Institute of Chemistry, A. Gostauto 9, 01108 Vilnius (Lithuania); Cesuniene, Asta [Institute of Chemistry, A. Gostauto 9, 01108 Vilnius (Lithuania); Vrublevsky, Igor [Department of Microelectronics, Belarusian State University of Informatics and Radioelectronics, 6 Brovka str, Minsk 220013 (Belarus); Jasulaitiene, Vitalija; Ragalevicius, Rimas [Institute of Chemistry, A. Gostauto 9, 01108 Vilnius (Lithuania)

    2010-03-30

    In this study, we report the results obtained investigating the behavior of sulfuric and chromic acid alumina templates in typical supporting electrolytes frequently used for alternating current (ac) deposition of various nm-scaled materials. Qualitative analysis of voltammetric profiles taken for as-grown, ac-treated and annealed alumina films in a conventional tetraborate re-anodizing solution revealed dramatical changes in the properties of alumina barrier layer during ac treatment in these supporting electrolytes even at low current density. These changes were related here with the transport of protons through the barrier layer during ac treatment, discharge at the metal/oxide interface and hydrogenation of alumina material by hydrogen atoms in an upward way. This conclusion comes from the behavior of Pt/Hg|alumina|Me{sup z+} electrode and the valence band X-ray photoelectron spectra taken from the inner part of alumina barrier layer material before and after the ac treatment.

  11. Study of preparation and surface morphology of self-ordered nanoporous alumina; Estudo da preparacao e da morfologia de superficie de alumina nanoporosa auto-organizada

    Energy Technology Data Exchange (ETDEWEB)

    Rodrigues, Elisa Marchezini; Martins, Maximiliano Delany, E-mail: elisamarch@gmail.com, E-mail: MG.mdm@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG. (Brazil); Silva, Ronald Arreguy, E-mail: arregsilva@yahoo.com.br [Centro Universitario de Belo Horizonte (UniBH), Belo Horizonte, MG (Brazil)

    2013-07-01

    Nanoporous alumina is a typical material that exhibits self-ordered nanochannels spontaneously organized in hexagonal shape. Produced by anodizing of metallic aluminum, it has been used as a template for production of materials at the nanoscale. This work aimed to study the preparation of nanoporous alumina by anodic anodizing of metallic aluminum substrates. The nanoporous alumina was prepared following the methodology proposed by Masuda and Fukuda (1995), a two-step method consisting of anodizing the aluminum sample in the potentiostatic mode, removing the layer of aluminum oxide (alumina) formed and then repeat the anodization process under the same conditions as the first anodization. This method produces nanoporous alumina with narrow pore diameter distribution and well-ordered structure. (author)

  12. Chemical Strategies for Template Syntheses of Composite Micro and Nanostructures.

    Science.gov (United States)

    2007-11-02

    syntheses can be accomplished within the pores of the alumina templates to make semiconductor tubules (27). Figure 5 shows that Ti02 tubules prepared...surface area forms have higher photo efficiencies (28). Ti02 /conductor nanocomposites may prove to be useful photocatalysts because the template...synthesized Ti02 nanostructures have very high surface areas (27). Furthermore, as discussed previously, each outer tubular Ti02 catalyst particle has

  13. Energy transfer in porous anodic alumina/rhodamine 110 nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Elhouichet, H., E-mail: habib.elhouichet@fst.rnu.tn [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95, Hammam-Lif 2050 (Tunisia); Departement de Physique, Faculte des Sciences de Tunis, University of Tunis Elmanar 2092 Tunis (Tunisia); Harima, N.; Koyama, H. [Hyogo University of Teacher Education, Kato, Hyogo 673-1494 (Japan); Gaponenko, N.V. [Belarusian State University of Informatics and Radioelectronics, P. Browki St. 6, 220013 Minsk (Belarus)

    2012-09-15

    We have used porous anodic alumina (PAA) films as templates for embedding rhodamine 110 (Rh110) molecules and examined their photoluminescence (PL) properties in detail. The analysis of the polarization memory (PM) of PL strongly suggests that there is a significant energy transfer from PAA to Rh110 molecules. The effect of annealing the PAA layer on the PL properties of the nanocomposite has been studied. The results show that the energy transfer becomes more efficient in annealed PAA. - Highlights: Black-Right-Pointing-Pointer Porous anodic alumina-rhodamine 110 nanocomposites are elaborated. Black-Right-Pointing-Pointer Efficient energy transfer from the host to Rh110 molecules is evidenced from measurements of photoluminescence and degree of polarization memory spectra. Black-Right-Pointing-Pointer Thermal annealing of porous anodic alumina can improve the process of excitation transfer.

  14. N-doped mesoporous alumina for adsorption of carbon dioxide

    Institute of Scientific and Technical Information of China (English)

    Jayshri A.Thote; Ravikrishna V.Chatti; Kartik S.Iyer; Vivek Kumar; Arti N.Valechha; Nitin K.Labhsetwar; Rajesh B.Biniwale; M.K.N.Yenkie; Sadhana S.Rayalu

    2012-01-01

    N-doped mesoporous alumina has been synthesized using chitosan as the biopolymer template.The adsorbent has been thoroughly investigated for the adsorption of CO2 from a simulated flue gas stream (15% CO2 balanced with N2) and compared with commercially available mesoporous alumina procured from SASOL,Germany.CO2 adsorption was studied under different conditions of pretreatment and adsorption temperature,inlet CO2 concentration and in the presence of oxygen and moisture.The adsorption capacity was determined to be 29.4 mg CO2/g of adsorbent at 55℃.This value was observed to be 4 times higher in comparison to that of commercial mesoporous alumina at a temperature of 55℃.Basicity of alumina surface coupled with the presence of nitrogen in template in synthesized sample is responsible for this enhanced CO2 adsorption.Adsorption capacity for CO2 was retained in the presence of oxygen; however moisture had a deteriorating effect on the adsorption capacity reducing it to nearly half the value.

  15. Bauxite and alumina

    Science.gov (United States)

    Bray, E.L.

    2010-01-01

    The article reports on the global market performance of bauxite and alumina in 2009 and presents an outlook for their 2010 performance. There were only several U.S. states that could produce bauxite and bauxitic clays including Georgia, Arkansas, and Alabama. The prices for imported refractory-grade calcined bauxite ranged between 426 U.S. dollars and 554 dollars per ton.

  16. Prediction of alumina penetration

    Energy Technology Data Exchange (ETDEWEB)

    Mandell, D A

    1993-02-01

    The MESA hydrocode was used to predict two-dimensional tests of L/D 10 and L/D 15 tungsten rods impacting AD 90 alumina with a steel backing. The residual penetration into the steel is the measured quantity in these experiments conducted at the Southwest Research Institute (SWR). The interface velocity as a function of time between an alumina target and a lithium fluoride window, impacted by an alumina disk at velocities between 544 m/s and 2329 m/s, was also predicted. These one-dimensional flyer plate experiments were conducted at Sandia National Laboratories using Coors AD 995 alumina. The material strength and fracture models are important in the prediction of ceramic experiments. The models used in these predictions are discussed. The penetrations in the two-dimensional tests were predicted to 11.4 percent or better. In five of the six experiments, the predicted penetration depth was deeper than the measured value. This trend is expected since the calculation is based on ideal conditions. The results show that good agreement between the 1-D flyer plate data and the MESA predictions exists at the lower impact velocities, but the maximum velocity is overpredicted as the flyer plate velocity increases. At a flyer plate velocity of 2329 m/s the code overpredicted the data by 12.3 percent.

  17. Alumina Technology Roadmap

    Energy Technology Data Exchange (ETDEWEB)

    none,

    2002-02-01

    The Alumina Technology Roadmap outlines a comprehensive long-term research and development plan that defines the industry's collective future and establishes a clear pathway forward. It emphasizes twelve high-priority R&D areas deemed most significant in addressing the strategic goals.

  18. Nanolithography based contacting method for electrical measurements on single template synthesized nanowires

    DEFF Research Database (Denmark)

    Fusil, S.; Piraux, L.; Mátéfi-Tempfli, Stefan

    2005-01-01

    A reliable method enabling electrical measurements on single nanowires prepared by electrodeposition in an alumina template is described. This technique is based on electrically controlled nanoindentation of a thin insulating resist deposited on the top face of the template filled by the nanowire...

  19. Rapid fabrication of self-ordered porous alumina with 10-/sub-10-nm-scale nanostructures by selenic acid anodizing.

    Science.gov (United States)

    Nishinaga, Osamu; Kikuchi, Tatsuya; Natsui, Shungo; Suzuki, Ryosuke O

    2013-09-25

    Anodic porous alumina has been widely investigated and used as a nanostructure template in various nanoapplications. The porous structure consists of numerous hexagonal cells perpendicular to the aluminum substrate and each cell has several tens or hundreds of nanoscale pores at its center. Because the nanomorphology of anodic porous alumina is limited by the electrolyte during anodizing, the discovery of additional electrolytes would expand the applicability of porous alumina. In this study, we report a new self-ordered nanoporous alumina formed by selenic acid (H2SeO4) anodizing. By optimizing the anodizing conditions, anodic alumina possessing 10-nm-scale pores was rapidly assembled (within 1 h) during selenic acid anodizing without any special electrochemical equipment. Novel sub-10-nm-scale spacing can also be achieved by selenic acid anodizing and metal sputter deposition. Our new nanoporous alumina can be used as a nanotemplate for various nanostructures in 10-/sub-10-nm-scale manufacturing.

  20. A hybrid approach to the surface biofunctionalization of nanostructured porous alumina

    Energy Technology Data Exchange (ETDEWEB)

    Silvan, Miguel Manso; Ruiz, Josefa Predestinacion Garcia [Departamento de Fisica Aplicada y Departamento de Biologia Molecular, Facultad de Ciencias, Universidad Autonoma de Madrid, Unidad Asociada GMNF (ICMM-CSIC), 28049 Madrid (Spain); Centro de Investigaciones Biomedicas en Red, Bioingenieria Biomateriales y Nanomedicina (CIBERbbn) (Spain); Gonzalez, Ruy Sanz [Instituto de Ciencia de Materiales de Madrid, Consejo Superior de Investigaciones Cientificas, 28049 Madrid (Spain); Velez, Manuel Hernandez [Departamento de Fisica Aplicada y Departamento de Biologia Molecular, Facultad de Ciencias, Universidad Autonoma de Madrid, Unidad Asociada GMNF (ICMM-CSIC), 28049 Madrid (Spain)

    2010-02-15

    The application of nanostructured porous alumina templates as a solid support in biomedical assays requires a surface biofunctionalization process that has been addressed in this work by an hybrid aminopropyl-triethoxysilane/tetraisopropyl-orthotitanate (APTS/ TIPT) self assembled film. The nanostructured porous alumina templates are activated in a peroxide solution before immersion in the biofunctionalizing APTS/TIPT solution. The biofunctionalization process was followed up by UV-vis spectroscopy, which confirmed the modification of the dielectric structure of the alumina surface. The influence of the biofunctionalization step in an immunological assay was carried out by fluorescence microscopy. Results confirm the gain in activity after the immobilization of an FITC labelled mouse Igg. Specific biological recognition in a bovine serum albumin (BSA)-antiBSA assay is proved afterwards by shifts observed in the reflectance interferograms thus providing a fast biosensing transducer platform. (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  1. Calcium aluminate in alumina

    Science.gov (United States)

    Altay, Arzu

    The properties of ceramic materials are determined not only by the composition and structure of the phases present, but also by the distribution of impurities, intergranular films and second phases. The phase distribution and microstructure both depend on the fabrication techniques, the raw materials used, the phase-equilibrium relations, grain growth and sintering processes. In this dissertation research, various approaches have been employed to understand fundamental phenomena such as grain growth, impurity segregation, second-phase formation and crystallization. The materials system chosen was alumina intentionally doped with calcium. Atomic-scale structural analyses of grain boundaries in alumina were carried on the processed samples. It was found that above certain calcium concentrations, CA6 precipitated as a second phase at all sintering temperatures. The results also showed that abnormal grain growth can occur after precipitation and it is not only related to the calcium level, but it is also temperature dependent. In order to understand the formation mechanism of CA6 precipitates in calcium doped alumina samples, several studies have been carried out using either bulk materials or thin films The crystallization of CA2 and CA6 powders has been studied. Chemical processing techniques were used to synthesize the powders. It was observed that CA2 powders crystallized directly, however CA6 powders crystallized through gamma-Al 2O3 solid solution. The results of energy-loss near-edge spectrometry confirmed that gamma-Al2O3 can dissolve calcium. Calcium aluminate/alumina reaction couples have also been investigated. All reaction couples were heat treated following deposition. It was found that gamma-Al2O3 was formed at the interface as a result of the interfacial reaction between the film and the substrate. gamma-Al 2O3 at the interface was stable at much higher temperatures compared to the bulk gamma-Al2O3 formed prior to the CA6 crystallization. In order to

  2. Bauxite Mining and Alumina Refining

    Science.gov (United States)

    Frisch, Neale; Olney, David

    2014-01-01

    Objective: To describe bauxite mining and alumina refining processes and to outline the relevant physical, chemical, biological, ergonomic, and psychosocial health risks. Methods: Review article. Results: The most important risks relate to noise, ergonomics, trauma, and caustic soda splashes of the skin/eyes. Other risks of note relate to fatigue, heat, and solar ultraviolet and for some operations tropical diseases, venomous/dangerous animals, and remote locations. Exposures to bauxite dust, alumina dust, and caustic mist in contemporary best-practice bauxite mining and alumina refining operations have not been demonstrated to be associated with clinically significant decrements in lung function. Exposures to bauxite dust and alumina dust at such operations are also not associated with the incidence of cancer. Conclusions: A range of occupational health risks in bauxite mining and alumina refining require the maintenance of effective control measures. PMID:24806720

  3. Code Generation with Templates

    CERN Document Server

    Arnoldus, Jeroen; Serebrenik, A

    2012-01-01

    Templates are used to generate all kinds of text, including computer code. The last decade, the use of templates gained a lot of popularity due to the increase of dynamic web applications. Templates are a tool for programmers, and implementations of template engines are most times based on practical experience rather than based on a theoretical background. This book reveals the mathematical background of templates and shows interesting findings for improving the practical use of templates. First, a framework to determine the necessary computational power for the template metalanguage is presen

  4. Synthesis and Photoluminescence Enhancement of Silver Nanoparticles Decorated Porous Anodic Alumina

    Institute of Scientific and Technical Information of China (English)

    Song Ye; Yidong Hou; Renyi Zhu; Shulong Gu; Jingquan Wang; Zhiyou Zhang; Sha Shi; Jinglei Du

    2011-01-01

    Silver nanoparticles (Ag NPs) were successfully assembled in porous anodic alumina (AAO) templates via a green silver mirror reaction. The Ag NPs/AAO composite templates then were characterized by field emission scanning electron microscopy (FESEM), energy-dispersive X-ray microanalysis (EDX), and X-ray diffraction (XRD). Furthermore, the photoluminescence (PL) properties were also investigated. Compared with the blank AAO, the PL intensity of Ag NPs/AAO templates are enhanced and the maximum enhancement is 2.58 times. Based on the local electric field enhancement effect, the theoretical values were also deduced, which are basically coincident with the experimental.

  5. Gelcasting Polycrystalline Alumina

    Energy Technology Data Exchange (ETDEWEB)

    Janney, M.A.; Zuk, K.J.; Wei, G.C.

    2000-01-01

    OSRAM SYLVANIA INC. is a major U.S. manufacturer of high-intensity lighting. Among its products is the Lumalux TM line of high-pressure sodium vapor arc lamps, which are used for industrial, highway, and street lighting. The key to the performance of these lamps is the polycrystalline alumina (PCA) tube that is used to contain the plasma that is formed in the electric arc. That plasma consists of ionized sodium, mercury, and xenon vapors. The key attributes of the PCA tubes are their transparency ({approximately}97% total transmittance in the visible), their refractoriness (inner wall temperature can reach l2OOC), and their chemical resistance (sodium and mercury vapor are extremely corrosive). The current efficiency of the lamps is very high, up to 100 initial lumens per watt. (Compare incandescent lamps 10-20 lumens per watt, fluorescent lamps 25-90 lumens per watt.)

  6. Alumina-magnesia Refractory Castables

    Institute of Scientific and Technical Information of China (English)

    Wang Jing

    2010-01-01

    @@ 1 Scope This standard specifies the classification,technical requirements,test methods,quality appraisal procedures,packing,marking,transportation,storage,and quality certificate of alumina-magnesia refractory castables.

  7. Macroporous silica–alumina composites with mesoporous walls

    Indian Academy of Sciences (India)

    Gautam Gundiah

    2001-04-01

    Macroporous silica–alumina composites with mesopores have been prepared by employing polymethylmethacrylate beads as templates in the presence of the cationic surfactant, N-cetyl-N,N,N-trimethylammonium bromide. The Si/Al ratio in the composites has been varied between 4.5 and 48 and the occurrence of mesopores has been verified by X-ray diffraction. The surface areas of the samples vary between 676 and 1038 m2g–1, with the highest value in the sample with Si/Al = 48.

  8. Sol-Gel Template Synthesis and Photocatalytic Activity of TiO2 Nanofibrils Loaded on Al2O3 Template

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    TiO2 nanofibrils were prepared within the pores of alumina template membrane by use of sol-gel chemistry. The TiO2 nanofibrils have good crystallinity and size. There is agglomeration free among the particulates of TiO2 and the fibrils show high catalytic activity.

  9. Gelcasting polycrystalline alumina

    Energy Technology Data Exchange (ETDEWEB)

    Janney, M.A. [Oak Ridge National Lab., TN (United States)

    1997-04-01

    This work is being done as part of a CRADA with Osram-Sylvania, Inc. (OSI) OSI is a major U.S. manufacturer of high-intensity lighting. Among its products is the Lumalux{reg_sign} line of high-pressure sodium vapor arc lamps, which are used for industrial, highway, and street lighting. The key to the performance of these lamps is the polycrystalline alumina (PCA) tube that is used to contain the plasma that is formed in the electric arc. That plasma consists of ionized sodium, mercury, and xenon vapors. The key attributes of the PCA tubes are their transparency (95% total transmittance in the visible region), their refractoriness (inner wall temperature can reach 1400{degrees}C), and their chemical resistance (sodium and mercury vapor are extremely corrosive). The current efficiency of the lamps is very high, on the order of several hundred lumens / watt. (Compare - incandescent lamps -13 lumens/watt fluorescent lamps -30 lumens/watt.) Osram-Sylvania would like to explore using gelcasting to form PCA tubes for Lumalux{reg_sign} lamps, and eventually for metal halide lamps (known as quartz-halogen lamps). Osram-Sylvania, Inc. currently manufactures PCA tubes by isostatic pressing. This process works well for the shapes that they presently use. However, there are several types of tubes that are either difficult or impossible to make by isostatic pressing. It is the desire to make these new shapes and sizes of tubes that has prompted Osram-Sylvania`s interest in gelcasting. The purpose of the CRADA is to determine the feasibility of making PCA items having sufficient optical quality that they are useful in lighting applications using gelcasting.

  10. Modelling the growth of porous alumina matrix for creating hyperbolic media

    Science.gov (United States)

    Aryslanova, E. M.; Alfimov, A. V.; Chivilikhin, S. A.

    2016-08-01

    Porous aluminum oxide is a regular self-assembled structure. During anodization it is possible to control nano-parameters of the structure using macroscopic parameters of anodization. Porous alumina films can be used as a template for the creation of hyperbolic media. In this work we consider the anodization process, our model takes into account the influence of layers of aluminum and electrolyte on the rate of growth of aluminum oxide, as well as the effect of surface diffusion. As a result of our model we obtain the minimum distance between centers of alumina pores in the beginning of anodizing process. We also present the results obtained by numerical modelling of hyperbolic media based on porous alumina film.

  11. Transport properties of alumina nanofluids

    Energy Technology Data Exchange (ETDEWEB)

    Wong, Kau-Fui Vincent; Kurma, Tarun [Department of Mechanical and Aerospace Engineering, University of Miami, Coral Gables, FL 33124 (United States)], E-mail: kwong@miami.edu

    2008-08-27

    Recent studies have showed that nanofluids have significantly greater thermal conductivity compared to their base fluids. Large surface area to volume ratio and certain effects of Brownian motion of nanoparticles are believed to be the main factors for the significant increase in the thermal conductivity of nanofluids. In this paper all three transport properties, namely thermal conductivity, electrical conductivity and viscosity, were studied for alumina nanofluid (aluminum oxide nanoparticles in water). Experiments were performed both as a function of volumetric concentration (3-8%) and temperature (2-50 deg. C). Alumina nanoparticles with a mean diameter of 36 nm were dispersed in water. The effect of particle size was not studied. The transient hot wire method as described by Nagaska and Nagashima for electrically conducting fluids was used to test the thermal conductivity. In this work, an insulated platinum wire of 0.003 inch diameter was used. Initial calibration was performed using de-ionized water and the resulting data was within 2.5% of standard thermal conductivity values for water. The thermal conductivity of alumina nanofluid increased with both increase in temperature and concentration. A maximum thermal conductivity of 0.7351 W m{sup -1} K{sup -1} was recorded for an 8.47% volume concentration of alumina nanoparticles at 46.6 deg. C. The effective thermal conductivity at this concentration and temperature was observed to be 1.1501, which translates to an increase in thermal conductivity by 22% when compared to water at room temperature. Alumina being a good conductor of electricity, alumina nanofluid displays an increasing trend in electrical conductivity as volumetric concentration increases. A microprocessor-based conductivity/TDS meter was used to perform the electrical conductivity experiments. After carefully calibrating the conductivity meter's glass probe with platinum tip, using a standard potassium chloride solution, readings were

  12. Transport properties of alumina nanofluids.

    Science.gov (United States)

    Wong, Kau-Fui Vincent; Kurma, Tarun

    2008-08-27

    Recent studies have showed that nanofluids have significantly greater thermal conductivity compared to their base fluids. Large surface area to volume ratio and certain effects of Brownian motion of nanoparticles are believed to be the main factors for the significant increase in the thermal conductivity of nanofluids. In this paper all three transport properties, namely thermal conductivity, electrical conductivity and viscosity, were studied for alumina nanofluid (aluminum oxide nanoparticles in water). Experiments were performed both as a function of volumetric concentration (3-8%) and temperature (2-50 °C). Alumina nanoparticles with a mean diameter of 36 nm were dispersed in water. The effect of particle size was not studied. The transient hot wire method as described by Nagaska and Nagashima for electrically conducting fluids was used to test the thermal conductivity. In this work, an insulated platinum wire of 0.003 inch diameter was used. Initial calibration was performed using de-ionized water and the resulting data was within 2.5% of standard thermal conductivity values for water. The thermal conductivity of alumina nanofluid increased with both increase in temperature and concentration. A maximum thermal conductivity of 0.7351 W m(-1) K(-1) was recorded for an 8.47% volume concentration of alumina nanoparticles at 46.6 °C. The effective thermal conductivity at this concentration and temperature was observed to be 1.1501, which translates to an increase in thermal conductivity by 22% when compared to water at room temperature. Alumina being a good conductor of electricity, alumina nanofluid displays an increasing trend in electrical conductivity as volumetric concentration increases. A microprocessor-based conductivity/TDS meter was used to perform the electrical conductivity experiments. After carefully calibrating the conductivity meter's glass probe with platinum tip, using a standard potassium chloride solution, readings were taken at

  13. SINTESIS DAN KARAKTERISASI GAMMA ALUMINA (γ-Al2O3 DARI KAOLIN ASAL TATAKAN, SELATAN BERDASARKAN VARIASI TEMPERATUR KALSINASI

    Directory of Open Access Journals (Sweden)

    Utami Irawati

    2013-05-01

    Full Text Available Sintesis dan karakterisasi gamma alumina (γ-Al2O3 dari kaolin asal Tatakan, Kalimantan Selatan berdasarkan variasi temperatur kalsinasi telah dilakukan. Gamma alumina (γ-Al2O3 diperoleh dengan metode sol-gel. Polyethylene glycol 6000 digunakan sebagai template pembentuk pori, presipitasi dilakukan dengan penambahan NH4OH 2,6 M hingga pH larutan 8-9 untuk memperoleh Al(OH3. Kalsinasi dilakukan pada temperatur 500, 600, 700 dan 800 0C. Gamma alumina (γ-Al2O3 hasil kalsinasi kemudian di analisis menggunakan Fourier Transform Infrared (FTIR dan X-Ray Diftraction (XRD. Hasil analisis karakterisasi FTIR menunjukkan pada masing-masing variasi temperatur terbentuknya kerangka gamma alumina (γ-Al2O3 dan hasil XRD menunjukkan fasa alumina yang terbentuk adalah gamma alumina (γ-Al2O3. Struktur terbaik dari gamma alumina (γ-Al2O3 berdasarkan kekristalannya yaitu pada temperatur kalsinasi 700 0C dengan nilai 2θ = 46,06; 60,07 dan 66,93.

  14. Template synthesis, characterization and transformations of iron nanowires while aging

    Energy Technology Data Exchange (ETDEWEB)

    Jagminas, Arunas [Institute of Chemistry, A. Gostauto 9, LT-01108 Vilnius (Lithuania)], E-mail: jagmin@ktl.mii.lt; Mazeika, Kestutis; Reklaitis, Jonas [Institute of Physics, Savanoriu 231, LT-02300 Vilnius (Lithuania); Kurtinaitiene, Marija [Institute of Chemistry, A. Gostauto 9, LT-01108 Vilnius (Lithuania); Baltrunas, Dalis [Institute of Physics, Savanoriu 231, LT-02300 Vilnius (Lithuania)

    2008-05-15

    Densely packed arrays of various materials demonstrating enhanced magnetic properties remain of great interest nowadays. In this study, transmission electron microscopy (TEM), Moessbauer spectroscopy (MS) and powder X-ray diffraction (XRD) were used to characterize the morphology, composition and phase of iron nanowires (nws) deposited from the developed solution within alumina template pores of the average diameter of ca.15 nm by the alternating current (ac) electrolysis protocol. The same investigations were performed after Fe nws storage in the air for several months. Characterization of the as-grown product shows the formation of the crystalline {alpha}-Fe nws array with a preferred [1 1 0] nw growth direction. The aging of samples leads to the corrosion of Fe nws mainly from the template top side while aging of Fe nws liberated from the template and kept for several months under ambient conditions results in the corrosion of nws along their full length producing catkin-twig shapes.

  15. Highly Ordered Carbon Nanotube Arrays with Open Ends Grown in Anodic Alumina Nanoholes

    Institute of Scientific and Technical Information of China (English)

    2003-01-01

    Highly ordered multiwalled carbon nanotube arrays were fabricated by pyrolysis of acetylene within anodic alumina templates.Nanotubes are very uniform in diameter and open at both ends. High resolution transmission electron microscopy and electron diffraction analysis show that the carbon nanotubes are well graphitized. These standing and open carbon nanotubes are possible to offer a potential elegant technique for electron emitting devices,chemical functionalization and nanotube composites.

  16. Ion guiding in alumina capillaries

    DEFF Research Database (Denmark)

    Juhász, Z.; Sulik, B.; Biri, S.

    2009-01-01

    Transmission of a few keV impact energy Ne ions through capillaries in anodic alumina membranes has been studied with different ion counting methods using an energy dispersive electrostatic spectrometer, a multichannel plate (MCP) array and sensitive current-measurement. In the present work, we...

  17. Alumina Coating on Carbon Fibers by Sol-Gel Method

    OpenAIRE

    2006-01-01

    Alumina precursor film was coated on carbon fibers by a sol-gel method using aluminum alkoxide solution. The optimum coating condition for the concentration of alumina alkoxide and silane coupling agent was determined to uniformly coat alumina precursor on carbon fibers. Alumina precursor converted to alumina ceramics by heating at 750℃. SEM and EPMA showed that alumina ceramics was uniformly coated on carbon fibers. The thickness of alumina layer increased with increasing coating times. The ...

  18. Templating mesoporous zeolites

    DEFF Research Database (Denmark)

    Egeblad, Kresten; Christensen, Christina Hviid; Kustova, Marina

    2008-01-01

    The application of templating methods to produce zeolite materials with hierarchical bi- or trimodal pore size distributions is reviewed with emphasis on mesoporous materials. Hierarchical zeolite materials are categorized into three distinctly different types of materials: hierarchical zeolite...... crystals, nanosized zeolite crystals, and supported zeolite crystals. For the pure zeolite materials in the first two categories, the additional meso- or macroporosity can be classified as being either intracrystalline or intercrystalline, whereas for supported zeolite materials, the additional porosity...... originates almost exclusively from the support material. The methods for introducing mesopores into zeolite materials are discussed and categorized. In general, mesopores can be templated in zeolite materials by use of solid templating, supramolecular templating, or indirect templating...

  19. Processing and Performance of Alumina Fiber Reinforced Alumina Composites

    Institute of Scientific and Technical Information of China (English)

    P.Y.Lee; T.Uchijima; T.Yano

    2003-01-01

    Processing of alumina fiber-reinforced alumina matrix composites by hot-pressing was described. The mechanical properties of the composites fabricated by different sintering conditions including temperature and pressure have been investigated. The results indicated that the higher sintering temperature and pressure corresponded to the higher bulk density and higher maximum strength of the composite, whereas the pseudo-ductility of the composite was lower. The preliminary results of the composite with monazite-coated fibers showed that maximum strength could be improved up to 35% compared with the noncoated fiber composite in the same sintering condition. Moreover, the fracture behavior of the composite changed from completely brittle fracture to non-brittle fracture under the suitable sintering conditions. SEM observation of the fracture surface indicated that the coating worked as a protective barrier and avoided sintering of the fibers together even at high temperature and pressure during densification process.

  20. Tailoring thermal conductivity via three-dimensional porous alumina

    Science.gov (United States)

    Abad, Begoña; Maiz, Jon; Ruiz-Clavijo, Alejandra; Caballero-Calero, Olga; Martin-Gonzalez, Marisol

    2016-12-01

    Three-dimensional anodic alumina templates (3D-AAO) are an astonishing framework with open highly ordered three-dimensional skeleton structures. Since these templates are architecturally different from conventional solids or porous templates, they teem with opportunities for engineering thermal properties. By establishing the mechanisms of heat transfer in these frameworks, we aim to create materials with tailored thermal properties. The effective thermal conductivity of an empty 3D-AAO membrane was measured. As the effective medium theory was not valid to extract the skeletal thermal conductivity of 3D-AAO, a simple 3D thermal conduction model was developed, based on a mixed series and parallel thermal resistor circuit, giving a skeletal thermal conductivity value of approximately 1.25 W·m-1·K-1, which matches the value of the ordinary AAO membranes prepared from the same acid solution. The effect of different filler materials as well as the variation of the number of transversal nanochannels and the length of the 3D-AAO membrane in the effective thermal conductivity of the composite was studied. Finally, the thermal conductivity of two 3D-AAO membranes filled with cobalt and bismuth telluride was also measured, which was in good agreement with the thermal model predictions. Therefore, this work proved this structure as a powerful approach to tailor thermal properties.

  1. Tailoring thermal conductivity via three-dimensional porous alumina.

    Science.gov (United States)

    Abad, Begoña; Maiz, Jon; Ruiz-Clavijo, Alejandra; Caballero-Calero, Olga; Martin-Gonzalez, Marisol

    2016-12-09

    Three-dimensional anodic alumina templates (3D-AAO) are an astonishing framework with open highly ordered three-dimensional skeleton structures. Since these templates are architecturally different from conventional solids or porous templates, they teem with opportunities for engineering thermal properties. By establishing the mechanisms of heat transfer in these frameworks, we aim to create materials with tailored thermal properties. The effective thermal conductivity of an empty 3D-AAO membrane was measured. As the effective medium theory was not valid to extract the skeletal thermal conductivity of 3D-AAO, a simple 3D thermal conduction model was developed, based on a mixed series and parallel thermal resistor circuit, giving a skeletal thermal conductivity value of approximately 1.25 W·m(-1)·K(-1), which matches the value of the ordinary AAO membranes prepared from the same acid solution. The effect of different filler materials as well as the variation of the number of transversal nanochannels and the length of the 3D-AAO membrane in the effective thermal conductivity of the composite was studied. Finally, the thermal conductivity of two 3D-AAO membranes filled with cobalt and bismuth telluride was also measured, which was in good agreement with the thermal model predictions. Therefore, this work proved this structure as a powerful approach to tailor thermal properties.

  2. Sintering behaviour of spinel–alumina composites

    Indian Academy of Sciences (India)

    Soumen Pal; A K Bandyopadhyay; P G Pal; S Mukherjee; B N Samaddar

    2009-04-01

    Study of alumina–magnesia binary phase diagram reveals that around 40–50 wt% alumina dissolves in spinel (MgAl2O4) at 1600°C. Solid solubility of alumina in spinel decreases rapidly with decreasing temperature, which causes exsolution of alumina from spinel phase. Previous work of one of the authors revealed that the exsolution of alumina makes some interlocking structures in between alumina and spinel phases. In the present investigation, refractory grade calcined alumina and spinel powder were used to make different batch compositions. Green pellets, formed at a pressure of 1550 kg cm-2 were fired at different temperatures of 1500°, 1550° and 1600°C for 2 h soaking time. Bulk density, percent apparent porosity, firing shrinkage etc were measured at each temperature. Sintering results were analysed to understand the mechanism of spinel–alumina interactions. SEM study of present samples does not reveal the distinct precipitation of needle shaped -alumina from spinel, but has some effect on densification process of spinel–alumina composites. Microstructural differences between present and previous work suggest an ample scope of further work in spinel–alumina composites.

  3. Rf glow discharge optical emission spectrometry for the analysis of arrays of Ni nanowires in nanoporous alumina and titania membranes

    Energy Technology Data Exchange (ETDEWEB)

    Prida, V.M.; Bordel, N.; Hernando, B. [Depto. Fisica, Universidad Oviedo, Calvo Sotelo s/n, 33007 Oviedo (Spain); Navas, D.; Pirota, K.R.; Vazquez, M. [Instituto de Ciencia de Materiales de Madrid (CSIC), Cantoblanco, 28049 Madrid (Spain); Hernandez-Velez, M. [Instituto de Ciencia de Materiales de Madrid (CSIC), Cantoblanco, 28049 Madrid (Spain); Depto. Fisica Aplicada, C-XII, Universidad Autonoma Madrid, Cantoblanco, 28049 Madrid (Spain); Menendez, A.; Pereiro, R.; Sanz-Medel, A. [Depto. Quimica Fisica y Analitica, Facultad de Quimica, Julian Claveria 8, 33006 Oviedo (Spain)

    2006-05-15

    Anodic alumina (Al{sub 2}O{sub 3}) and titania (TiO{sub 2}) nanoporous oxide membranes are among the most widely studied self-organized nanopore templates, formed by uniform and well aligned arrays of synthetized nanometric pores or tubes. Here, we perform a comparative study of the depth profiling analysis in self-ordered alumina and titania nanoporous membrane templates by means of the radiofrequency glow discharge coupled to optical emission spectrometry (rf-GD-OES) technique. The densely packed columnar arrays of hexagonally self-ordered nanoporous alumina membranes investigated, with an average inner pore diameter of 35 nm and 105 nm interspacing, give an uniform thickness pore length about more than 5 {mu}m, depending on the anodization time. Meanwhile, the analysis of the anodized titania nanotubes, with an average inner pore diameter of 100 nm and 40 nm wall thickness, shown to be about 300 nm in length. Each type of membranes were also studied in both cases, when the nanopores were empty and after filling with electrodeposited Ni. The direct analysis by rf-GD-OES reveals the ability of this technique to control the quality of these so synthesized nanocomposites formed by electrodeposited Ni nanowires into the alumina and titania nanoporous templates. (copyright 2006 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  4. Rf glow discharge optical emission spectrometry for the analysis of arrays of Ni nanowires in nanoporous alumina and titania membranes

    Science.gov (United States)

    Prida, V. M.; Navas, D.; Pirota, K. R.; Hernandez-Velez, M.; Menéndez, A.; Bordel, N.; Pereiro, R.; Sanz-Medel, A.; Hernando, B.; Vazquez, M.

    2006-05-01

    Anodic alumina (Al2O3) and titania (TiO2) nanoporous oxide membranes are among the most widely studied self-organized nanopore templates, formed by uniform and well aligned arrays of synthetized nanometric pores or tubes. Here, we perform a comparative study of the depth profiling analysis in self-ordered alumina and titania nanoporous membrane templates by means of the radiofrequency glow discharge coupled to optical emission spectrometry (rf-GD-OES) technique. The densely packed columnar arrays of hexagonally self-ordered nanoporous alumina membranes investigated, with an average inner pore diameter of 35 nm and 105 nm interspacing, give an uniform thickness pore length about more than 5 μm, depending on the anodization time. Meanwhile, the analysis of the anodized titania nanotubes, with an average inner pore diameter of 100 nm and 40 nm wall thickness, shown to be about 300 nm in length. Each type of membranes were also studied in both cases, when the nanopores were empty and after filling with electrodeposited Ni. The direct analysis by rf-GD-OES reveals the ability of this technique to control the quality of these so synthesized nanocomposites formed by electrodeposited Ni nanowires into the alumina and titania nanoporous templates.

  5. Nanoporous Thin Film Templates for the Fabrication of Nanowires and Nanotubes

    DEFF Research Database (Denmark)

    Bordo, Kirill

    2011-01-01

    of nanowires or nanotubes are obtained. Such arrays can be subsequently integrated into e.g. solar cells and other electronic devices. This thesis is focused on the fabrication of thin-film porous anodic alumina (PAA) templates on different substrates. The fabrication of organic nanowires and nanotubes via....... The prepared thin-film PAA templates were directly used for the fabrication of poly(3-hexylthiophene) (P3HT) nanotubes by means of melt-assisted wetting. Different architectures of solar cells based on P3HT nanotube arrays and thin films of PCBM were considered. Additionally, 1D nanostructures from P3HT, poly......The method of template wetting allows one to fabricate highly ordered arrays of upright standing nanowires or nanotubes from different materials in a controllable manner. In this method, a porous template is filled by an appropriate solution or melt. After selective removal of the template, arrays...

  6. Wettability of Aluminum on Alumina

    Science.gov (United States)

    Bao, Sarina; Tang, Kai; Kvithyld, Anne; Tangstad, Merete; Engh, Thorvald Abel

    2011-12-01

    The wettability of molten aluminum on solid alumina substrate has been investigated by the sessile drop technique in a 10-8 bar vacuum or under argon atmosphere in the temperature range from 1273 K to 1673 K (1000 °C to 1400 °C). It is shown that the reduction of oxide skin on molten aluminum is slow under normal pressures even with ultralow oxygen potential, but it is enhanced in high vacuum. To describe the wetting behavior of the Al-Al2O3 system at lower temperatures, a semiempirical calculation was employed. The calculated contact angle at 973 K (700 °C) is approximately 97 deg, which indicates that aluminum does not wet alumina at aluminum casting temperatures. Thus, a priming height is required for aluminum to infiltrate a filter. Wetting in the Al-Al2O3 system increases with temperature.

  7. Bone regeneration of hydroxyapatite/alumina bilayered scaffold with 3 mm passage-like medullary canal in canine tibia model.

    Science.gov (United States)

    Kim, Jong Min; Son, Jun Sik; Kang, Seong Soo; Kim, Gonhyung; Choi, Seok Hwa

    2015-01-01

    The aim of this study was to evaluate the bone regeneration of hydroxyapatite (HA)/alumina bilayered scaffold with a 3 mm passage-like medullary canal in a beagle tibia model. A porous HA/alumina scaffold was fabricated using a polymeric template-coating technique. HA/alumina scaffold dimensions were 10 mm in outer diameter, 20 mm in length, and with either a 3 mm passage or no passage. A 20 mm segmental defect was induced using an oscillating saw through the diaphysis of the beagle tibia. The defects of six beagles were filled with HA/alumina bilayered scaffolds with a 3 mm passage or without. The segmental defect was fixated using one bone plate and six screws. Bone regeneration within the HA/alumina scaffolds was observed at eight weeks after implantation. The evaluation of bone regeneration within the scaffolds after implantation in a beagle tibia was performed using radiography, computerized tomography (CT), micro-CT, and fluorescence microscopy. New bone successfully formed in the tibia defects treated with 3 mm passage HA/alumina scaffolds compared to without-passage HA/alumina scaffolds. It was concluded that the HA/alumina bilayered scaffold with 3 mm passage-like medullary canal was instrumental in inducing host-scaffold engraftment of the defect as well as distributing the newly formed bone throughout the scaffold at 8 weeks after implantation.

  8. Bone Regeneration of Hydroxyapatite/Alumina Bilayered Scaffold with 3 mm Passage-Like Medullary Canal in Canine Tibia Model

    Directory of Open Access Journals (Sweden)

    Jong Min Kim

    2015-01-01

    Full Text Available The aim of this study was to evaluate the bone regeneration of hydroxyapatite (HA/alumina bilayered scaffold with a 3 mm passage-like medullary canal in a beagle tibia model. A porous HA/alumina scaffold was fabricated using a polymeric template-coating technique. HA/alumina scaffold dimensions were 10 mm in outer diameter, 20 mm in length, and with either a 3 mm passage or no passage. A 20 mm segmental defect was induced using an oscillating saw through the diaphysis of the beagle tibia. The defects of six beagles were filled with HA/alumina bilayered scaffolds with a 3 mm passage or without. The segmental defect was fixated using one bone plate and six screws. Bone regeneration within the HA/alumina scaffolds was observed at eight weeks after implantation. The evaluation of bone regeneration within the scaffolds after implantation in a beagle tibia was performed using radiography, computerized tomography (CT, micro-CT, and fluorescence microscopy. New bone successfully formed in the tibia defects treated with 3 mm passage HA/alumina scaffolds compared to without-passage HA/alumina scaffolds. It was concluded that the HA/alumina bilayered scaffold with 3 mm passage-like medullary canal was instrumental in inducing host-scaffold engraftment of the defect as well as distributing the newly formed bone throughout the scaffold at 8 weeks after implantation.

  9. The Trouble With Templates

    CERN Document Server

    Sampson, Laura; Yunes, Nicolas

    2013-01-01

    Waveform templates are a powerful tool for extracting and characterizing gravitational wave signals, acting as highly restrictive priors on the signal morphologies that allow us to extract weak events buried deep in the instrumental noise. The templates map the waveform shapes to physical parameters, thus allowing us to produce posterior probability distributions for these parameters. However, there are attendant dangers in using highly restrictive signal priors. If strong field gravity is not accurately described by General Relativity (GR), then using GR templates may result in fundamental bias in the recovered parameters, or even worse, a complete failure to detect signals. Here we study such dangers, concentrating on three distinct possibilities. First, we show that there exist modified theories compatible with all existing tests that would fail to be detected by the LIGO/Virgo network using searches based on GR templates, but which would be detected using a one parameter post-Einsteinian extension. Second...

  10. E3 Charter Template

    Science.gov (United States)

    This is a charter template which includes decisions made during the project planning phase, as well as local project goals, a communication strategy, an outreach strategy, distribution of responsibilities and a schedule.

  11. images_template

    Data.gov (United States)

    National Aeronautics and Space Administration — Images for the website template go here. It will not change their names or locations, but will hopefully help to organize them. Oh, but for a directory structure...

  12. Acetic acid mediated interactions between alumina surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Sato, Kimiyasu, E-mail: sato.kimiyasu@aist.go.jp [National Institute of Advanced Industrial Science and Technology (AIST), Anagahora 2266-98, Shimoshidami, Moriyama-ku, Nagoya 463-8560 (Japan); Y Latin-Small-Letter-Dotless-I lmaz, Hueseyin [National Institute of Advanced Industrial Science and Technology (AIST), Anagahora 2266-98, Shimoshidami, Moriyama-ku, Nagoya 463-8560 (Japan); Gebze Institute of Technology, Materials Science and Engineering Department, 41400, Gebze-Kocaeli (Turkey); Ijuin, Atsuko; Hotta, Yuji; Watari, Koji [National Institute of Advanced Industrial Science and Technology (AIST), Anagahora 2266-98, Shimoshidami, Moriyama-ku, Nagoya 463-8560 (Japan)

    2012-02-01

    Low-molecular-weight organic acids have been known to modify colloidal stability of alumina-based suspensions. We investigated interaction forces between alumina surfaces mediated by acetic acid which is one of the simplest organic acids. Forces between alumina surfaces were measured using the colloid-probe method of atomic force microscope (AFM). Repulsive forces attributed to steric repulsion due to adsorbed molecules and electrostatic repulsion dominated the interaction. Results of rheological characterization of the alumina slurry containing acetic acid supported the finding.

  13. Structural Effects of Lanthanide Dopants on Alumina

    Science.gov (United States)

    Patel, Ketan; Blair, Victoria; Douglas, Justin; Dai, Qilin; Liu, Yaohua; Ren, Shenqiang; Brennan, Raymond

    2017-01-01

    Lanthanide (Ln3+) doping in alumina has shown great promise for stabilizing and promoting desirable phase formation to achieve optimized physical and chemical properties. However, doping alumina with Ln elements is generally accompanied by formation of new phases (i.e. LnAlO3, Ln2O3), and therefore inclusion of Ln-doping mechanisms for phase stabilization of the alumina lattice is indispensable. In this study, Ln-doping (400 ppm) of the alumina lattice crucially delays the onset of phase transformation and enables phase population control, which is achieved without the formation of new phases. The delay in phase transition (θ → α), and alteration of powder morphology, particle dimensions, and composition ratios between α- and θ-alumina phases are studied using a combination of solid state nuclear magnetic resonance, electron microscopy, digital scanning calorimetry, and high resolution X-ray diffraction with refinement fitting. Loading alumina with a sparse concentration of Ln-dopants suggests that the dopants reside in the vacant octahedral locations within the alumina lattice, where complete conversion into the thermodynamically stable α-domain is shown in dysprosium (Dy)- and lutetium (Lu)-doped alumina. This study opens up the potential to control the structure and phase composition of Ln-doped alumina for emerging applications.

  14. Structural Effects of Lanthanide Dopants on Alumina

    Energy Technology Data Exchange (ETDEWEB)

    Patel, Ketan; Blair, Victoria; Douglas, Justin; Dai, Qilin; Liu, Yaohua; Ren, Shenqiang; Brennan, Raymond

    2017-01-06

    Lanthanide (Ln3+) doping in alumina has shown great promise for stabilizing and promoting desirable phase formation to achieve optimized physical and chemical properties. However, doping alumina with Ln elements is generally accompanied by formation of new phases (i.e. LnAlO3, Ln2O3), and therefore inclusion of Ln-doping mechanisms for phase stabilization of the alumina lattice is indispensable. In this study, Ln-doping (400 ppm) of the alumina lattice crucially delays the onset of phase transformation and enables phase population control, which is achieved without the formation of new phases. The delay in phase transition (θ → α), and alteration of powder morphology, particle dimensions, and composition ratios between α- and θ-alumina phases are studied using a combination of solid state nuclear magnetic resonance, electron microscopy, digital scanning calorimetry, and high resolution X-ray diffraction with refinement fitting. Loading alumina with a sparse concentration of Ln-dopants suggests that the dopants reside in the vacant octahedral locations within the alumina lattice, where complete conversion into the thermodynamically stable α-domain is shown in dysprosium (Dy)- and lutetium (Lu)-doped alumina. This study opens up the potential to control the structure and phase composition of Ln-doped alumina for emerging applications.

  15. Influence of Alumina Addition on the Optical Property of Zirconia/Alumina Composite Dental Ceramics

    Institute of Scientific and Technical Information of China (English)

    JIANG Li; LIAO Yunmao; LI Wei; WAN Qianbing; ZHAO Yongqi

    2011-01-01

    The influence of various alumina additions on the optical property of zirconia/alumina composite ceramics was investigated.The relative sintered densities,transmittances,color and the microstructure of the composite ceramics were studied.The experimental results showed that the relative sintered densities and transmittances decreased with alumina addition.The lightness increased obviously but the chroma change was small.Pure zirconia nanopowders sintered densely could obtain the relatively high transmittance,while the transmittance and the lightness of slight addition changed significantly.The zirconia/alumina composite ceramics with alumina addition less than 7.5wt% could achieve the relatively stable and reliable optical properties.

  16. MECHANICAL STRENGTH ENHANCEMENT OF OPEN-CELL ALUMINA FOAMS USING OPTIMUM CONCENTRATION OF DEFLOCCULANT

    Directory of Open Access Journals (Sweden)

    A. Hadi

    2015-06-01

    Full Text Available Open-cell alumina foams were prepared using the appropriate alumina slurry and polyurethane sponge with linear pore density of approximately 14 pores per inch (ppi as a template by the replica method. The rheological studies showed that the optimum solid content for the slurries without deflocculants was 60 wt. %. In order to increase the slurry solid content, Tiron (1,2-dihydroxy-3,5-benzene disulfonic acid disodium salt was used as dispersant. To determine the optimum concentration of dispersant, the viscosity curves of alumina slurries containing different values of Tiron from 0 to 1.2 wt. % (based on dry material weight were studied. The optimum concentration of Tiron obtained for lowest viscosity was 0.8 wt. %. Thus, the solid content in the slurry could be increased from 60 to 66 wt. %. The effect of increase in the slurry solid content and the way it affects the foam structure and the mechanical strength were investigated. Microstructural observations of the foams show a significant reduction in macroscopic and microscopic defects in the foam struts when the slurry solid content is increased. Total porosity of the produced alumina foams prepared using slurries containing 60 and 66 wt. % solid are 83.3 and 80.4 %, respectively, while the compressive strength of the foams has increased from 1.33 to 3.24 MPa.

  17. Joomla! 3 template essentials

    CERN Document Server

    Frankowski, Pawel

    2013-01-01

    Using this hands-on, step-by step tutorial filled with practical examples, the readers will be able to create beautiful templates and themes for your websites that will make them stand out from others.This book is written for all of you who wish to create your own unique templates for Joomla! 3.x. This book can be used by Joomla! administrators or visual designers (with no programming experience) or those of you who are used to working with common web developer tools like HTML/CSS editors for coding purposes. You would need basic knowledge of Joomla! and some knowledge of CSS and HTML.

  18. Computing layouts with deformable templates

    KAUST Repository

    Peng, Chihan

    2014-07-27

    In this paper, we tackle the problem of tiling a domain with a set of deformable templates. A valid solution to this problem completely covers the domain with templates such that the templates do not overlap. We generalize existing specialized solutions and formulate a general layout problem by modeling important constraints and admissible template deformations. Our main idea is to break the layout algorithm into two steps: a discrete step to lay out the approximate template positions and a continuous step to refine the template shapes. Our approach is suitable for a large class of applications, including floorplans, urban layouts, and arts and design. Copyright © ACM.

  19. β-Phase Morphology in Ordered Poly(9,9-dioctylfluorene Nanopillars by Template Wetting Method

    Directory of Open Access Journals (Sweden)

    Martinez-Ferrero E

    2011-01-01

    Full Text Available Abstract An efficient method based in template wetting is applied for fabrication of ordered Poly(9,9-dioctylfluorene (PFO nanopillars with β-phase morphology. In this process, nanoporous alumina obtained by anodization process is used as template. PFO nanostructures are prepared under ambient conditions via infiltration of the polymeric solution into the pores of the alumina with an average pore diameter of 225 nm and a pore depth of 500 nm. The geometric features of the resulting structures are characterized with environmental scanning electron microscopy (ESEM, luminescence fluorimeter (PL and micro μ-X-ray diffractometer (μ-XRD. The characterization demonstrates the β-phase of the PFO in the nanopillars fabricated. Furthermore, the PFO nanopillars are characterized by Raman spectroscopy to study the polymer conformation. These ordered nanostructures can be used in optoelectronic applications such as polymer light-emitting diodes, sensors and organic solar cells.

  20. Template Composite Dark Matter

    DEFF Research Database (Denmark)

    Drach, Vincent; Hietanen, Ari; Pica, Claudio

    2015-01-01

    We present a non perturbative study of SU(2) gauge theory with two fundamental Dirac flavours. We discuss how the model can be used as a template for composite Dark Matter (DM). We estimate one particular interaction of the DM candidate with the Standard Model : the interaction through photon...

  1. Template Composite Dark Matter

    DEFF Research Database (Denmark)

    Drach, Vincent; Hietanen, Ari; Pica, Claudio

    2015-01-01

    We present a non perturbative study of SU(2) gauge theory with two fundamental Dirac flavours. We discuss how the model can be used as a template for composite Dark Matter (DM). We estimate one particular interaction of the DM candidate with the Standard Model : the interaction through photon...

  2. Biometric template revocation

    Science.gov (United States)

    Arndt, Craig M.

    2004-08-01

    Biometric are a powerful technology for identifying humans both locally and at a distance. In order to perform identification or verification biometric systems capture an image of some biometric of a user or subject. The image is then converted mathematical to representation of the person call a template. Since we know that every human in the world is different each human will have different biometric images (different fingerprints, or faces, etc.). This is what makes biometrics useful for identification. However unlike a credit card number or a password to can be given to a person and later revoked if it is compromised and biometric is with the person for life. The problem then is to develop biometric templates witch can be easily revoked and reissued which are also unique to the user and can be easily used for identification and verification. In this paper we develop and present a method to generate a set of templates which are fully unique to the individual and also revocable. By using bases set compression algorithms in an n-dimensional orthogonal space we can represent a give biometric image in an infinite number of equally valued and unique ways. The verification and biometric matching system would be presented with a given template and revocation code. The code will then representing where in the sequence of n-dimensional vectors to start the recognition.

  3. Electrochemical synthesis of highly ordered Ni nanowire arrays through AAO templates

    Institute of Scientific and Technical Information of China (English)

    LI Mei-jing; LI Xiao-ru; SONG Guo-jun; ZHAO Qing-pei

    2015-01-01

    One-dimensional Ni nanowires arrays were fabricated successfully by the electrochemical deposit in porous anodic alumina oxide (AAO) templates. The microstructure of nanoarrays was respectively observed by scanning electron microscope s (SEM) and transmission electron microscopes (TEM). The results show that the obtained Ni nanowires are arranged orderly and the diameter is about 200nm. Crystallization way was observed by X-ray diffraction (XRD). The results show that Ni nanowire is face-centered cubic structure.

  4. Functional Fe-Pd nanomaterials synthesized by template-assisted methods

    Energy Technology Data Exchange (ETDEWEB)

    Prida, V.M., E-mail: vmpp@uniovi.es [Depto. de Fisica, Universidad de Oviedo, Calvo Sotelo s/n, 33007 Oviedo, Asturias (Spain); Vega, V.; Garcia, J.; Gonzalez, L.; Rosa, W.O.; Fernandez, A.; Hernando, B. [Depto. de Fisica, Universidad de Oviedo, Calvo Sotelo s/n, 33007 Oviedo, Asturias (Spain)

    2012-10-15

    In this work, we highlight our recent progress in the synthesis and characterization of functional nanomaterials based on Fe-Pd ferromagnetic alloys by means of template-assisted deposition techniques employing highly ordered nanoporous alumina membranes, such as ordered arrays of nanowires and antidots thin films. Special attention is paid on their basic magnetic properties, such as coercivity, remanence and magnetic anisotropy, and their dependence on the microstructure and morphological parameters of the ordered arrays.

  5. Alumina forming iron base superalloy

    Energy Technology Data Exchange (ETDEWEB)

    Yamamoto, Yukinori; Muralidharan, Govindarajan; Brady, Michael P.

    2014-08-26

    An austenitic stainless steel alloy, consists essentially of, in weight percent 2.5 to 4 Al; 25 to 35 Ni; 12 to 19 Cr; at least 1, up to 4 total of at least one element selected from the group consisting of Nb and Ta; 0.5 to 3 Ti; less than 0.5 V; 0.1 to 1 of at least on element selected from the group consisting of Zr and Hf; 0.03 to 0.2 C; 0.005 to 0.1 B; and base Fe. The weight percent Fe is greater than the weight percent Ni. The alloy forms an external continuous scale including alumina, and contains coherent precipitates of .gamma.'-Ni.sub.3Al, and a stable essentially single phase FCC austenitic matrix microstructure. The austenitic matrix is essentially delta-ferrite-free and essentially BCC-phase-free.

  6. Dissolution Kinetics of Alumina Calcine

    Energy Technology Data Exchange (ETDEWEB)

    Batcheller, Thomas Aquinas

    2001-09-01

    Dissolution kinetics of alumina type non-radioactive calcine was investigated as part of ongoing research that addresses permanent disposal of Idaho High Level Waste (HLW). Calcine waste was produced from the processing of nuclear fuel at the Idaho Nuclear Technology and Engineering Center (INTEC). Acidic radioactive raffinates were solidified at ~500°C in a fluidized bed reactor to form the dry granular calcine material. Several Waste Management alternatives for the calcine are presented in the Idaho High Level Waste Draft EIS. The Separations Alternative addresses the processing of the calcine so that the HLW is ready for removal to a national geological repository by the year 2035. Calcine dissolution is the key front-end unit operation for the separations alternative.

  7. Recent Development of High Alumina Refractories in China

    Institute of Scientific and Technical Information of China (English)

    WANGJin-xiang; LIUJie-hua

    1994-01-01

    The paper reviews the achievements which have been attained recently in China in high alumina refractories raw materials and their products,including 1) homogenization ,urification and electric fusion of high alumina raw materials and synthesizing of spinel from natural raw materials;2) processing principle and characteristics and microstructural features of creep-resistance high alu-mina brick ,alumina-magnesia-carbon brick and thermal shock resistanced high alumina brikc and their application in practice.

  8. Fracture toughness of advanced alumina ceramics and alumina matrix composites used for cutting tool edges

    Directory of Open Access Journals (Sweden)

    M. Szutkowska

    2012-10-01

    Full Text Available Purpose: Specific characteristics in fracture toughness measurements of advanced alumina ceramics and alumina matrix composites with particular reference to α-Al2O3, Al2O3-ZrO2, Al2O3-ZrO2-TiC and Al2O3-Ti(C,N has been presented.Design/methodology/approach: The present study reports fracture toughness obtained by means of the conventional method and direct measurements of the Vickers crack length (DCM method of selected tool ceramics based on alumina: pure alumina, alumina-zirconia composite with unstabilized and stabilized zirconia, alumina–zirconia composite with addition of TiC and alumina–nitride-carbide titanium composite with 2wt% of zirconia. Specimens were prepared from submicro-scale trade powders. Vicker’s hardness (HV1, fracture toughness (KIC at room temperature, the indentation fracture toughness, Young’s modulus and apparent density were also evaluated. The microstructure was observed by means of scanning electron microscopy (SEM.Findings: The lowest value of KIC is revealed by pure alumina ceramics. The addition of (10 wt% unstabilized zirconia to alumina or a small amount (5 wt% of TiC to alumina–zirconia composite improve fracture toughness of these ceramics in comparison to alumina ceramics. Alumina ceramics and alumina-zirconia ceramics reveal the pronounced character of R-curve because of an increasing dependence on crack growth resistance with crack extension as opposed to the titanium carbide-nitride reinforced composite based on alumina. R-curve has not been observed for this composite.Practical implications: The results show the method of fracture toughness improvement of alumina tool ceramics.Originality/value: Taking into account the values of fracture toughness a rational use of existing ceramic tools should be expected.

  9. Semiconductor nanowires and templates for electronic applications

    Energy Technology Data Exchange (ETDEWEB)

    Ying, Xiang

    2009-07-15

    This thesis starts by developing a platform for the organized growth of nanowires directly on a planar substrate. For this, a method to fabricate horizontal porous alumina membranes is studied. The second part of the thesis focuses on the study of nanowires. It starts by the understanding of the growth mechanisms of germanium nanowires and follows by the structural and electrical properties at the single nanowire level. Horizontally aligned porous anodic alumina (PAA) was used as a template for the nanowire synthesis. Three PAA arrangements were studied: - high density membranes - micron-sized fingers - multi-contacts Membranes formed by a high density of nanopores were obtained by anodizing aluminum thin films. Metallic and semiconducting nanowires were synthesized into the PAA structures via DC deposition, pulsed electro-depostion and CVD growth. The presence of gold, copper, indium, nickel, tellurium, and silicon nanowires inside PAA templates was verified by SEM and EDX analysis. Further, room-temperature transport measurements showed that the pores are completely filled till the bottom of the pores. In this dissertation, single crystalline and core-shell germanium nanowires are synthesized using indium and bismuth as catalyst in a chemical vapor deposition procedure with germane (GeH{sub 4}) as growth precursor. A systematic growth study has been performed to obtain high aspect-ratio germanium nanowires. The influence of the growth conditions on the final morphology and the crystalline structure has been determined via scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM). In the case of indium catalyzed germanium nanowires, two different structures were identified: single crystalline and crystalline core-amorphous shell. The preferential growth axis of both kinds of nanowires is along the [110] direction. The occurrence of the two morphologies was found to only depend on the nanowire dimension. In the case of bismuth

  10. Regularity control of porous anodic alumina and photodegradation activity of highly ordered titania nanostructures

    Institute of Scientific and Technical Information of China (English)

    LIU Xiang-zhi; XU Ming-xia; TIAN Yu-ming; SHANG Meng; ZHANG Ping

    2006-01-01

    A two-step anodizing process was used to prepare wide-range highly ordered porous anodic alumina membrane (PAA) in the electrolyte of oxalic acid. The effects of anodic voltage,anodizing time,size of aluminium foil and additives on the regularity of PAA membrane were also studied in the process of two-step anodization. The template method was combined with the sol-electrophoresis deposition and sol-gel method respectively to prepare highly ordered titania nanostructures. The diameter and length of the obtained nanostructures were determined by the pore size and depth of the PAA template. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used to characterize the morphology and phase structure of the PAA template and the titania nanostructures. The results show that the anodizing time and the additive of ethanol have a great effect on the regularity of PAA template. This can be explained from the self-organized process and the current density theory. A theoretical model based on the self-organized process was established to discuss the formation mechanism of PAA template from the chemical perspective. The titania nanostructures prepared with this method has a high specific surface area. Furthermore,the photocatalytic activity of titania nanostructures on methyl orange were studied. Compared with ordinary titania membranes,the titania nanostructures synthesized with this method have higher photodegradation activity.

  11. Burned Microporous Alumina-Graphite Brick

    Institute of Scientific and Technical Information of China (English)

    2008-01-01

    @@ 1 Scope This standard specifies the definition,classifica-tion,technical requirements,test methods,inspection rules,marking,packing,transportation and quality certificate of burned microporous alumina-graphite brick.

  12. Loss tangent measurements on unirradiated alumina

    Energy Technology Data Exchange (ETDEWEB)

    Zinkle, S.J.; Goulding, R.H. [Oak Ridge National Lab., TN (United States)

    1996-04-01

    Unirradiated room temperature loss tangent for sapphire and several commercial grades of polycrystalline alumina are complied for frequencies between 10{sup 5} and 4x10{sup 11} Hz. Sapphire exhibits significantly lower values for the loss tangent at frequencies up to 10{sup 11} Hz. The loss tangents of 3 different grades of Wesgo alumina (AL300, AL995, AL998) and 2 different grades of Coors alumina (AD94, AD995) have typical values near {approx}10{sup -4} at a frequency of 10{sup 8} Hz. On the other hand, the loss tangent of Vitox alumina exhibits a large loss peak tan d{approx} 5x10{sup -3} at this frequency.

  13. Alumina Carbon Refractory Products for Continuous Casting

    Institute of Scientific and Technical Information of China (English)

    2008-01-01

    @@ 1 Scope This standard specifies the classification.techni-cal requirements,test methods,inspection rules,packing,marking,transportation,storage and quality certificate of alumina carbon refractory products for continuous casting.

  14. Fabrication and characterization of mesoporous silica nanochannels inside the channels of anodic alumina membrane

    Directory of Open Access Journals (Sweden)

    Moataz M. Mekawy

    2016-03-01

    Full Text Available Brij type surfactants (CnEOx that have different chemical structures were used to fabricate 3D Mesoporous Silica Nanochannels (MSN inside the channels of Anodic Alumina Membrane (AAM under acidic conditions. The fabricated 3D MSN were characterized using TEM-ED, SEM, Small angle XRD, and N2 isotherm. Results revealed that the synthesis of ordered 3D cubic Im3m mesostructures can be formed with tunable pore diameters varied from 4.0 to 4.9 nm that are partially affected with the length of ethylene oxide (EO group in the template surfactant.

  15. Manufacturing ontology through templates

    Directory of Open Access Journals (Sweden)

    Diciuc Vlad

    2017-01-01

    Full Text Available The manufacturing industry contains a high volume of knowhow and of high value, much of it being held by key persons in the company. The passing of this know-how is the basis of manufacturing ontology. Among other methods like advanced filtering and algorithm based decision making, one way of handling the manufacturing ontology is via templates. The current paper tackles this approach and highlights the advantages concluding with some recommendations.

  16. The Watermark Template Attack

    OpenAIRE

    Herrigel, Alexander; Voloshynovskyy, Svyatoslav; Rytsar, Yuriy

    2001-01-01

    This paper presents a new attack, called the watermark template attach, for watermarked images. In contrast to the Stirmark benchmark, this attack does not severely reduce the quality of the image. This attack maintains, therefore, the commercial value of the watermarked image. In contrast to previous approaches, it is not the aim of the attack to change the statistics of embedded watermarks fooling the detection process but to utilize specific concepts that have been recently developed for m...

  17. Ion channel mimetic membranes and silica nanotubes prepared from porous aluminum oxide templates

    Science.gov (United States)

    Mitchell, David Tanner

    Chapter 1 provides background information on the template synthesis of nanomaterials. The template synthesis method is examined with special attention to the use of membranes containing monodisperse cylindrical pores as templates. Several examples of the utility of template-synthesized nanomaterials are given. The production of one type of template membrane, nanopore alumina, is reviewed. Reviews of sol-gel and silane chemistry are also provided. In Chapter 2, a sol-gel template synthesis process is used to produce silica nanotubes within the pores of alumina templates. The nanotubes can be modified using a variety of chemistries, typically via a silanization process. Because the nanotubes are formed in a template, the interior and exterior surface can be modified independently. Modified nanotubes can be used for drug detoxification or as extractants for the removal of metal ions. The nanotube surface can also be biotinylated, which causes binding to avidinated surfaces. Composite microtubes of silica and various polymers are also prepared. Additionally, Au nanowires are shown to assemble with colloidal Au particles using dithiols as linkers. Chapter 3 describes the attachment of proteins onto template-synthesized silica nanotubes. The proteins are covalently linked via an aldehyde silane bridge that binds to pendant primary amino moieties on the protein. Protein-modified nanotubes function as highly specific extractants. Avidin-modified nanotubes extract biotin-coated Au nanoparticles from solution with high extraction efficiency. Immunoprotein-modified nanotubes extract the corresponding antibody from solution with high specificity. Antibody-modified nanotubes extract one enantiomer from a racemic mix. Enzymes, including drug detoxification enzymes, were also attached to the nanotubes and were shown to retain their catalytic activity. Immunoproteins on the outside of nanotubes can be used to direct nanotube binding, creating specific labeling agents. Chapter 4

  18. Effect of Anodic Alumina Oxide Pore Diameter on the Crystallization of Poly(butylene adipate).

    Science.gov (United States)

    Sun, Xiaoli; Fang, Qunqun; Li, Huihui; Ren, Zhongjie; Yan, Shouke

    2016-04-05

    Poly(butylene adipate) (PBA) was infiltrated into the anodic alumina oxide (AAO) templates with the pore diameter of around 30, 70, and 100 nm and PBA nanotubes with different diameters were prepared. The crystallization and phase transition behavior of the obtained PBA nanotubes capped in the nanopores have been explored by using X-ray diffraction and differential scanning calorimetry. Only α-PBA crystals form in the bulk sample during nonisothermal crystallization. By contrast, predominant β-PBA crystals form in the AAO templates. The β-PBA crystals formed in the nanopores with pore diameter less than 70 nm prefer to adopt an orientation with their b-axis parallel to the long axis of the pore. During the melt recrystallization, it was found that the critical temperature (Tβ), below which pure β-crystals form, is 20 °C for bulk PBA. It drops down significantly with the pore diameter for the PBA in the AAO template. Moreover, the β-crystals in the porous template exhibit larger lattice parameters compared with the bulk crystals. By monitoring the change of β-crystals in the heating process, it was found that β-crystals in the AAO template with the pore diameter of 30 nm (D30) melt directly while the β-crystals transform to α-crystals in the template with the pore diameter of 100 nm (D100). The intensity of (020) Bragg peak of β-crystals decreases at a similar rate in both D30 and D100 but disappears at a relatively lower temperature in D30. On the other hand, the β(110) peak intensity of β-PBA crystals formed in the D100 template decreases first at slower rate before α crystals appear, and then at a faster rate once the β to α phase transition takes place.

  19. Magnetic properties of Ni-Fe nanowire arrays: effect of template material and deposition conditions

    Energy Technology Data Exchange (ETDEWEB)

    Singleton, John [Los Alamos National Laboratory; Aravamudhan, Shyan [U OF SOUTH FL; Goddard, Paul A [U OF OXFORD; Bhansali, Shekhar [U OF SOUTH FL

    2008-01-01

    The objective of this work is to study the magnetic properties of arrays of Ni-Fe nanowires electrodeposited in different template materials such as porous silicon, polycarbonate and alumina. Magnetic properties were studied as a function of template material, applied magnetic field (parallel and perpendicular) during deposition, wire length, as well as magnetic field orientation during measurement. The results show that application of magnetic field during deposition strongly influences the c-axis preferred orientation growth of Ni-Fe nanowires. The samples with magnetic field perpendicular to template plane during deposition exhibits strong perpendicular anisotropy with greatly enhanced coercivity and squareness ratio, particularly in Ni-Fe nanowires deposited in polycarbonate templates. In case of polycarbonate template, as magnetic field during deposition increases, both coercivity and squareness ratio also increase. The wire length dependence was also measured for polycarbonate templates. As wire length increases, coercivity and squarness ratio decrease, but saturation field increases. Such magnetic behavior (dependence on template material, magnetic field, wire length) can be qualitatively explained by preferential growth phenomena, dipolar interactions among nanowires, and perpendicular shape anisotropy in individual nanowires.

  20. Polarization properties of porous anodic alumina with Y-branched Cu nanowires

    Institute of Scientific and Technical Information of China (English)

    Xuejun Su; Lichun Zhang; Qingshan Li; Dechun Liang

    2008-01-01

    @@ Porous anodic alumina (PAA) templates with branch structure are fabricated by the two-step anodic oxidation processes, and then the Y-branched Cu nanowires are synthesized in the templates using an alternating current (AC) deposition method. We observe the morphology image of the samples by scanning electron microscopy (SEM), and measure the transmission spectrum and the polarization spectrum of the samples by the spectrophotometer. The results show that PAA films with Y-branched Cu nanowires have better transmittance in the near infrared region. An extinction ratio of 15-18 dB and an insertion loss of 0.1-0.4 dB are obtained in this region. Therefore PAA with Y-branched Cu nanowires can be used as a near-infrared micropolarizer, and this kind of micropolarizer would have a promising future in the field of photoelectricity integration.

  1. Direct foaming porous alumina ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Salvini, V.R.; Sandurkov, B.A.; Klein-Gunnewiek, R.F.; Pandolfelli, V.C. [Federal Univ. of Sao Carlos, Materials Engineering Dept., FIRE Associate Lab., Sao Carlos, SP (Brazil)

    2007-07-01

    This paper presents the work carried out in order to improve the properties of these porous alumina ceramics, concerning their application as thermal insulating. Changes in solid content of ceramic suspension, variations of pore forming agents and other additives were carried out and their effects on the green and the sintered mechanical strength are also shown. According to the literature, several starch types seem to be attractive pore forming agents as well as binders for porous ceramics. Most of them consist of a mixture of two polysaccharide types, amylose (linear) and amylopectin (highly branched). Corn, potato and rice starches were used in the present study because of their difference in size and shape. In order to increase the mechanical strength of the sintered porous ceramics a part of the Al{sub 2}O{sub 3} in the composition was replaced by Al(OH){sub 3}. Due to the changes of the composition and additives, porosities up to 81% and a mechanical strength of 15 MPa were obtained. (orig.)

  2. The Cadastral Template Project

    DEFF Research Database (Denmark)

    Enemark, Stig; Steudler, Daniel; Williamson, Ian P.

    2004-01-01

      While many country reports have been compiled in the area of land administration over the last decade, there has not much attention been given to the basic cadastral issues. As a result, one of the objectives of Working Group 3 ?Cadastre? of the PCGIAP is the establishment of a cadastral template....... The work of the PCGIAP-Working Group 3 ?Cadastre? is being done in collaboration with Comission 7 ?Cadastre and Land Management? of the International Federation of Surveyors (FIG), which has extensive experience in comparative cadastral studies. This article describes the creation and the content...

  3. Bioactive glass-ceramics coatings on alumina

    Energy Technology Data Exchange (ETDEWEB)

    Vitale Brovarone, C.; Verne, E.; Lupo, F. [Politecnico di Torino (Italy). Materials Science and Chemical Eng. Dept.; Moisescu, C. [Jena Univ. (Germany). Otto-Schott-Inst. fuer Glaschemie; Zanardi, L.; Bosetti, M.; Cannas, M. [Eastern Piemont Univ., Novara (Italy). Medical Science Dept.

    2001-07-01

    In this work, aiming to combine the mechanical performances of alumina with the surface properties of a bioactive material, we coated full density alumina substrates by a bioactive glass-ceramic GC. This latter was specially tailored, in term of costituents and specific quantity to have a thermal expansion coefficient close to that of alumina (8.5-9{sup *}10{sup -6}/ C) which is lower than most of the bioactive glasses and glass-ceramics already in use. In this way, we sought to avoid, as much as possible, the crack formation and propagation due to residual stresses generated by the thermal expansion coefficients mismatch. Furthermore, the high reactivity of alumina toward the glass-ceramic was carefully controlled to avoid deep compositional modification of the GC that will negatively affect its bioactivity. At this purpose, an intermediate layer of an appropriate glass G was coated prior to coat the bioactive glass-ceramic. On the materials obtained, preliminary biological tests have been done to evaluate glass-ceramic biocompatibility respect to alumina. (orig.)

  4. Monitoring Transport Across Modified Nanoporous Alumina Membranes

    Directory of Open Access Journals (Sweden)

    Erich D. Steinle

    2007-11-01

    Full Text Available This paper describes the use of several characterization methods to examinealumina nanotubule membranes that have been modified with specific silanes. The functionof these silanes is to alter the transport properties through the membrane by changing thelocal environment inside the alumina nanotube. The presence of alkyl groups, either long(C18 or short and branched (isopropyl hydrocarbon chains, on these silanes significantlydecreases the rate of transport of permeant molecules through membranes containingalumina nanotubes as monitored via absorbance spectroscopy. The presence of an ionicsurfactant can alter the polarity of these modified nanotubes, which correlates to anincreased transport of ions. Fluorescent spectroscopy is also utilized to enhance thesensitivity of detecting these permeant molecules. Confirmation of the alkylsilaneattachment to the alumina membrane is achieved with traditional infrared spectroscopy,which can also examine the lifetime of the modified membrane. The physical parameters ofthese silane-modified porous alumina membranes are studied via scanning electronmicroscopy. The alumina nanotubes are not physically closed off or capped by the silanesthat are attached to the alumina surfaces.

  5. High contrast laser marking of alumina

    Energy Technology Data Exchange (ETDEWEB)

    Penide, J. [Applied Physics Department, University of Vigo, EEI, Lagoas-Marcosende, 9, Vigo 36310 (Spain); Quintero, F., E-mail: fquintero@uvigo.es [Applied Physics Department, University of Vigo, EEI, Lagoas-Marcosende, 9, Vigo 36310 (Spain); Riveiro, A. [Applied Physics Department, University of Vigo, EEI, Lagoas-Marcosende, 9, Vigo 36310 (Spain); Fernández, A. [Department of Engineering Design, University of Vigo, Escuela de Ingeniería Industrial, Campus Universitario, Vigo E-36310 (Spain); Val, J. del [Applied Physics Department, University of Vigo, EEI, Lagoas-Marcosende, 9, Vigo 36310 (Spain); Comesaña, R. [Materials Engineering, Applied Mechanics and Construction Department, University of Vigo, EEI, Lagoas-Marcosende, Vigo E-36310 (Spain); Lusquiños, F.; Pou, J. [Applied Physics Department, University of Vigo, EEI, Lagoas-Marcosende, 9, Vigo 36310 (Spain)

    2015-05-01

    Highlights: • Laser marking of alumina using near infrared (NIR) lasers was experimentally analyzed. • Color change produced by NIR lasers is due to thermally induced oxygen vacancies. • Laser marking results obtained using NIR lasers and green laser are compared. • High contrast marks on alumina were achieved. - Abstract: Alumina serves as raw material for a broad range of advanced ceramic products. These elements should usually be identified by some characters or symbols printed directly on them. In this sense, laser marking is an efficient, reliable and widely implemented process in industry. However, laser marking of alumina still leads to poor results since the process is not able to produce a dark mark, yielding bad contrast. In this paper, we present an experimental study on the process of marking alumina by three different lasers working in two wavelengths: 1064 nm (Near-infrared) and 532 nm (visible, green radiation). A colorimetric analysis has been carried out in order to compare the resulting marks and its contrast. The most suitable laser operating conditions were also defined and are reported here. Moreover, the physical process of marking by NIR lasers is discussed in detail. Field Emission Scanning Electron Microscopy, High Resolution Transmission Electron Microscopy and X-ray Photoelectron Spectroscopy were also employed to analyze the results. Finally, we propose an explanation for the differences of the coloration induced under different atmospheres and laser parameters. We concluded that the atmosphere is the key parameter, being the inert one the best choice to produce the darkest marks.

  6. Synthesis of aluminum oxy-hydroxide nanofibers from porous anodic alumina.

    Science.gov (United States)

    Jha, Himendra; Kikuchi, Tatsuya; Sakairi, Masatoshi; Takahashi, Hideaki

    2008-10-01

    A novel method for the synthesis of aluminum oxy-hydroxide nanofibers from a porous anodic oxide film of aluminum is demonstrated. In the present method, the porous anodic alumina not only acts as a template, but also serves as the starting material for the synthesis. The porous anodic alumina film is hydrothermally treated for pore-sealing, which forms aluminum oxy-hydroxide inside the pores of the oxide film as well as on the surface of the film. The hydrothermally sealed porous oxide film is immersed in the sodium citrate solution, which selectively etches the porous aluminum oxide from the film, leaving the oxy-hydroxide intact. The method is simple and gives highly uniform aluminum oxy-hydroxide nanofibers. Moreover, the diameter of the nanofibers can be controlled by controlling the pore size of the porous anodic alumina film, which depends on the anodizing conditions. Nanofibers with diameters of about 38-85 nm, having uniform shape and size, were successfully synthesized using the present method.

  7. Dielectric Performance of a High Purity HTCC Alumina at High Temperatures - a Comparison Study with Other Polycrystalline Alumina

    Science.gov (United States)

    Chen, Liangyu

    2014-01-01

    A very high purity (99.99+%) high temperature co-fired ceramic (HTCC) alumina has recently become commercially available. The raw material of this HTCC alumina is very different from conventional HTCC alumina, and more importantly there is no glass additive in this alumina material for co-firing processing. Previously, selected HTCC and LTCC (low temperature co-fired ceramic) alumina materials were evaluated at high temperatures as dielectric and compared to a regularly sintered 96% polycrystalline alumina (96% Al2O3), where 96% alumina was used as the benchmark. A prototype packaging system based on regular 96% alumina with Au thickfilm metallization successfully facilitated long term testing of high temperature silicon carbide (SiC) electronic devices for over 10,000 hours at 500 C. In order to evaluate this new high purity HTCC alumina for possible high temperature packaging applications, the dielectric properties of this HTCC alumina substrate were measured and compared with those of 96% alumina and a previously tested LTCC alumina from room temperature to 550 C at frequencies of 120 Hz, 1 KHz, 10 KHz, 100 KHz, and 1 MHz. A parallel-plate capacitive device with dielectric of the HTCC alumina and precious metal electrodes were used for measurements of the dielectric constant and dielectric loss of the co-fired alumina material in the temperature and frequency ranges. The capacitance and AC parallel conductance of the capacitive device were directly measured by an AC impedance meter, and the dielectric constant and parallel AC conductivity of the dielectric were calculated from the capacitance and conductance measurement results. The temperature and frequency dependent dielectric constant, AC conductivity, and dissipation factor of the HTCC alumina substrate are presented and compared to those of 96% alumina and a selected LTCC alumina. Other technical advantages of this new co-fired material for possible high packaging applications are also discussed.

  8. Size-selective recognition of catecholamines by molecular imprinting on silica-alumina gel.

    Science.gov (United States)

    Ling, Tzong-Rong; Syu, Yau Zen; Tasi, Yau-Ching; Chou, Tse-Chuan; Liu, Chung-Chiun

    2005-12-15

    The preparation of a catecholamine receptor was carried out using a molecular imprinting method with silica-alumina gel to form complementary structures for template recognition. The molecularly imprinted polymer (MIP) was synthesized by the condensation of silicate from tetraethyl orthosilictate (TEOS) under hydrothermal conditions at 60 degrees C. Aluminum chloride was added as a functional monomer to increase the material's rebinding ability. The selectivity of the MIP receptor prepared with different ratios of template to Si and Al, was examined with seven analytes including: dopamine, epinephrine, norepinephrine, ascorbic acid, homovanillic acid, uric acid, and l-tyrosine. The results showed a size selective effect for the receptors with respect to the recognition of the catecholamines. Some factors affecting the recognition ability were investigated including: the solution pH of analytes, surface capping on the MIP, and the imprinting pH of the silica-alumina solution. Also, the catecholamine MIP films on quartz crystal microbalance (QCM) electrodes were fabricated as sensors for in situ monitoring of the analytes in a 2-propanol solution.

  9. A Deformable Template Model, with Special Reference to Elliptical Templates

    DEFF Research Database (Denmark)

    Hobolth, Asger; Pedersen, Jan; Jensen, Eva Bjørn Vedel

    2002-01-01

    This paper suggests a high-level continuous image model for planar star-shaped objects. Under this model, a planar object is a stochastic deformation of a star-shaped template. The residual process, describing the difference between the radius-vector function of the template and the object...

  10. Synthesis and characterization of alumina precursor and alumina to be used as nano composite; Sintese e caracterizacao de precursores de alumina e alumina para uso em nanocompositos

    Energy Technology Data Exchange (ETDEWEB)

    Antunes, M.L.P., E-mail: malu@sorocaba.unesp.b [Universidade Estadual Paulista Julio de Mesquita Filho (UNESP), Sorocaba, SP (Brazil); Santos, H. Souza [Universidade de Sao Paulo (IF/USP), SP (Brazil). Inst. de Fisica; Santos, P. Souza [Universidade de Sao Paulo (EP/USP), SP (Brazil). Escola Politecnica

    2009-07-01

    With the evolution of nanomaterials technology, mainly in the 90s, it was possible to observe produced composites with alumina matrix and nanomaterial as reinforcing materials. It results in a significant improvement of mechanical proprieties of these composites. Thenceforth the study of synthesis and characterization of nanostructured materials has attracted great scientific interest. In this perspective, the aim of this work is to present an experimental procedure to obtain nordstrandite (aluminum hydroxide) with nanometric dimensions. Nordstrandite synthesis, obtained by the reaction of slightly amalgamated aluminum foil with aqueous ethylene glycol, which allows the control of the size of crystal produced. This control could be confirmed by X-Ray Diffraction and Electron Microscopy. Thermal transformation study is also presented. This study allowed the identification of transition aluminas that have potential to produce nanometric aluminas. (author)

  11. Iron films deposited on porous alumina substrates

    Science.gov (United States)

    Yamada, Yasuhiro; Tanabe, Kenichi; Nishida, Naoki; Kobayashi, Yoshio

    2016-12-01

    Iron films were deposited on porous alumina substrates using an arc plasma gun. The pore sizes (120 - 250 nm) of the substrates were controlled by changing the temperature during the anodic oxidation of aluminum plates. Iron atoms penetrated into pores with diameters of less than 160 nm, and were stabilized by forming γ-Fe, whereas α-Fe was produced as a flat plane covering the pores. For porous alumina substrates with pore sizes larger than 200 nm, the deposited iron films contained many defects and the resulting α-Fe had smaller hyperfine magnetic fields. In addition, only a very small amount of γ-Fe was obtained. It was demonstrated that the composition and structure of an iron film can be affected by the surface morphology of the porous alumina substrate on which the film is grown.

  12. Dynamical Mechanical Properties for AD90 Alumina

    Institute of Scientific and Technical Information of China (English)

    REN Hui-lan; NING Jian-guo; LI Ping

    2007-01-01

    The dynamic response of polycrystalline alumina was investigated in the pressure range of 0 -13 GPa by planar impact experiments.Velocity interferometer system for any reflector(VISAR) was used to obtain free surface velocity profile and determine the Hugoniot elastic limit,and manganin gauges were employed to obtain the stress-time histories and determine Hugoniot curve.Both the free surface particle velocity profiles and Hugoniot curves indicate the dispersion of the "plastic" wave for alumina.With the measured stress histories,the complete histories of strain,particle velocity,specific volume and specific internal energy are gained by using path line principle of Lagrange analysis.The dynamic mechanical behaviors for alumina under impact loading are analyzed,such as nonlinear characteristic,strain rate dependence,dispersion and declination of shock wave in the material.

  13. A Novel Processing Route for Ni-doped Alumina Composites

    Institute of Scientific and Technical Information of China (English)

    JING Mao-xiang; SHEN Xiang-qian; ZHOU Jian-xin; LI Dong-hong; LI Wang-xing

    2006-01-01

    Alumina-based composites containing 0-15wt% Ni metallic phase were produced by hot press-sintering Ni-coated alumina powders. The Ni-coated alumina powders were prepared by the aqueous heterogeneous precipitation of alumina micro-powders and nickel sulfate salt followed by reduction process. The microstructural features and dispersion of Ni phase in Ni-coated alumina powders and the subsequent alumina-Ni cermets were investigated using scanning electron microscope (SEM), X-ray diffractometer (XRD), and transmission electron microscope (TEM). The relative density of the hot press-sintered composites was measured with the Archimedes' method while the fracture strength and the fracture toughness were defined with the three-point bending method and the micro-indentation fracture method. In the formation of alumina-Ni cermets from sintered Ni-coated alumina powders, Ni phase to some extent limits the densification rate and stifles the coarsening and growing process of alumina grains. The Ni phase is found to be located at the interfaces and the triple-joint junctions of alumina grains which results into alteration of the fracture mode of alumina and its increased fracture strength and fracture toughness if compared with monolithic alumina.

  14. Tribological properties of nanoscale alumina-zirconia composites

    NARCIS (Netherlands)

    Kerkwijk, B.; Winnubst, A.J.A.; Verweij, H.; Mulder, E.J.; Metselaar, H.S.C.; Schipper, D.J.

    1999-01-01

    The tribological properties of zirconia (Y-TZP), alumina and their composites, alumina dispersed in zirconia (ADZ) and zirconia-toughened alumina (ZTA), were investigated. These ceramics are made by colloidal processing methods such that well-defined, homogeneous microstructures with submicron grain

  15. Nanomechanical humidity detection through porous alumina cantilevers

    Directory of Open Access Journals (Sweden)

    Olga Boytsova

    2015-06-01

    Full Text Available We present here the behavior of the resonance frequency of porous anodic alumina cantilever arrays during water vapor adsorption and emphasize their possible use in the micromechanical sensing of humidity levels at least in the range of 10–22%. The sensitivity of porous anodic aluminium oxide cantilevers (Δf/Δm and the humidity sensitivity equal about 56 Hz/pg and about 100 Hz/%, respectively. The approach presented here for the design of anodic alumina cantilever arrays by the combination of anodic oxidation and photolithography enables easy control over porosity, surface area, geometric and mechanical characteristics of the cantilever arrays for micromechanical sensing.

  16. Microwave fast sintering of submicrometer alumina

    Directory of Open Access Journals (Sweden)

    Romualdo Rodrigues Menezes

    2010-09-01

    Full Text Available Commercially available alumina powder with high-purity submicrometer particle size and narrow particle size distribution was fully densified by a microwave hybrid fast firing technique. The alumina compacts were surrounded by susceptor material, which helped the heating of the samples, and sintered in a microwave oven at a frequency of 2.45 GHz and a power level of 1.8 kW. The sintered samples reached densities of 99% in sintering cycles of 30 to 40 minutes, a much shorter time than conventional sintering processes. The sintered samples showed uniform microstructures with powder particle size/average grain size rations higher than 1:2.

  17. DNA-templated nanofabrication.

    Science.gov (United States)

    Becerril, Héctor A; Woolley, Adam T

    2009-02-01

    Nanofabrication, or the organizational control over matter at the nanometre scale, is an intriguing scientific challenge requiring multidisciplinary tools for its solution. DNA is a biomolecule that can be combined with other nanometre-scale entities through chemical self-assembly to form a broad variety of nanomaterials. In this tutorial review we present the principles that allow DNA to interact with other chemical species, and describe the challenges and potential applications of DNA as a template for making both biological and inorganic features with nanometre resolution. As such, this report should be of interest to chemists, surface and materials scientists, biologists, and nanotechnologists, as well as others who seek to use DNA in nanofabrication.

  18. Templated quasicrystalline molecular layers

    Science.gov (United States)

    Smerdon, Joe; Young, Kirsty; Lowe, Michael; Hars, Sanger; Yadav, Thakur; Hesp, David; Dhanak, Vinod; Tsai, An-Pang; Sharma, Hem Raj; McGrath, Ronan

    2014-03-01

    Quasicrystals are materials with long range ordering but no periodicity. We report scanning tunneling microscopy (STM) observations of quasicrystalline molecular layers on five-fold quasicrystal surfaces. The molecules adopt positions and orientations on the surface consistent with the quasicrystalline ordering of the substrate. Carbon-60 adsorbs atop sufficiently-separated Fe atoms on icosahedral Al-Cu-Fe to form a unique quasicrystalline lattice whereas further C60 molecules decorate remaining surface Fe atoms in a quasi-degenerate fashion. Pentacene (Pn) adsorbs at tenfold-symmetric points around surface-bisected rhombic triacontahedral clusters in icosahedral Ag-In-Yb. These systems constitute the first demonstrations of quasicrystalline molecular ordering on a template. EPSRC EP/D05253X/1, EP/D071828/1, UK BIS.

  19. Template-synthesized opal hydrogels

    Institute of Scientific and Technical Information of China (English)

    LI Jun; JI Lijun; RONG Jianhua; YANG Zhenzhong

    2003-01-01

    Opal hydrogels could be synthesized with polymer inverse opal template. A pH responsive opal N-iso- propylacrylamide/acrylic acid copolymerized hydrogel was prepared as an example. The ordered structure and response to pH were investigated. Through the sol-gel process of tetrabutyl titanate, opal titania was obtained with the opal hydrogel template.

  20. The fabrication of high sensitivity gold nanorod H2S gas sensors utilizing the highly uniform anodic aluminum oxide template

    Directory of Open Access Journals (Sweden)

    Chien-Yu Li

    2016-12-01

    Full Text Available Gold nanorod were fabricated using anodic alumina oxide template for H2S gas detection. The nanorod gas sensor exhibits high surface density and contact area, which can increase detection sensitivity. The anodic alumina oxide template contains an array of pores, with a width of 70 nm and a length of 27μm. Au nanorod were obtained through electro-deposition under a pulse bias of −1 V. The resistance of the Au nanorod was recorded upon exposure to various concentrations of H2S. The resistance could be attributed to the high electron affinity between sulfide and Au nanorod. Au–sulfide bonds provide strong bonding, which could alter the conductivity of the sensor. The gas sensor exhibits high sensitivity and short response time for H2S detection at room temperature.

  1. The fabrication of high sensitivity gold nanorod H2S gas sensors utilizing the highly uniform anodic aluminum oxide template

    Science.gov (United States)

    Li, Chien-Yu; Li, Ciao-Yu; Wu, You-Lin; Hsu, Chung-Ping; Lee, Ming-Ching; Houng, Mau-Phon

    2016-12-01

    Gold nanorod were fabricated using anodic alumina oxide template for H2S gas detection. The nanorod gas sensor exhibits high surface density and contact area, which can increase detection sensitivity. The anodic alumina oxide template contains an array of pores, with a width of 70 nm and a length of 27 μ m . Au nanorod were obtained through electro-deposition under a pulse bias of -1 V. The resistance of the Au nanorod was recorded upon exposure to various concentrations of H2S. The resistance could be attributed to the high electron affinity between sulfide and Au nanorod. Au-sulfide bonds provide strong bonding, which could alter the conductivity of the sensor. The gas sensor exhibits high sensitivity and short response time for H2S detection at room temperature.

  2. Fabrication and characterization of uniform TiO2 nanotube arrays by sol–gel template method

    Indian Academy of Sciences (India)

    T Maiyalagan; B Viswanathan; U V Varadaraju

    2006-12-01

    TiO2 nanotubes have been synthesized by sol–gel template method using alumina membrane. Scanning electron microscopy (SEM), transmission electron microscopy (TEM), Raman spectroscopy, UV absorption spectrum and X-ray diffraction techniques have been used to investigate the structure, morphology and optical properties of TiO2 nanotubes. SEM image showed that TiO2 nanotubes obtained were ordered and uniform. The diameter and length of the nanotubes were decided by the pore size and thickness of alumina template. Raman and XRD measurements confirmed the crystallinity and anatase phase of the TiO2 nanotubes. The optical absorption measurement of TiO2 nanotubes exhibits a blue shift with respect to that of the bulk TiO2 owing to the quantum size effect.

  3. Making Deformable Template Models Operational

    DEFF Research Database (Denmark)

    Fisker, Rune

    2000-01-01

    Deformable template models are a very popular and powerful tool within the field of image processing and computer vision. This thesis treats this type of models extensively with special focus on handling their common difficulties, i.e. model parameter selection, initialization and optimization...... published during the Ph.D. project. To put these articles into the general context of deformable template models and to pass on an overview of the deformable template model literature, the thesis starts with a compact survey of the deformable template model literature with special focus on representation....... A proper handling of the common difficulties is essential for making the models operational by a non-expert user, which is a requirement for intensifying and commercializing the use of deformable template models. The thesis is organized as a collection of the most important articles, which has been...

  4. Drug-delivery strategies by using template-synthesized nanotubes.

    Science.gov (United States)

    Perry, Jillian L; Martin, Charles R; Stewart, Jon D

    2011-05-27

    Encapsulating drugs within hollow nanotubes offers several advantages, including protection from degradation, the possibility of targeting desired locations, and drug release only under specific conditions. Template synthesis utilizes porous membranes prepared from alumina, polycarbonate, or other materials that can be dissolved under specific conditions. The method allows for great control over the lengths and diameters of nanotubes; moreover, tubes can be constructed from a wide variety of tube materials including proteins, DNA, silica, carbon, and chitosan. A number of capping strategies have been developed to seal payloads within nanotubes. Combining these advances with the ability to target and internalize nanotubes into living cells will allow these assemblies to move into the next phase of development, in vivo experiments.

  5. Study of the molybdenum retention in alumina; Estudio de la retencion de molibdeno en alumina

    Energy Technology Data Exchange (ETDEWEB)

    Wilkinson, Maria V.; Mondino, Angel V.; Manzini, Alberto [Comision Nacional de Energia Atomica, Buenos Aires (Argentina). Centro Atomico Ezeiza. Radioquimica y Quimica de las Radiaciones

    2002-07-01

    The Argentine National Atomic Energy Commission routinely produces {sup 99} Mo by fission of highly enriched uranium contained in targets irradiated in RA-3 reactor. The current process begins with the dissolution of the irradiated target in a basic media, considering the possibility of changing the targets, it could be convenient to dissolve them in acid media. The use of alumina as a first separation step in acid dissolution processes is already known although it is necessary to determine both the type of alumina to be used and the separation conditions. The study of molybdenum retention in alumina was performed at laboratory scale, using Mo-99 as radiotracer. Different kinds of alumina were tried, varying charge solution acidity. Influence of uranium concentration in the loading solution on molybdenum retention was also studied. (author)

  6. Third-generation alumina-on-alumina ceramic bearings in cementless total hip arthroplasty.

    Science.gov (United States)

    Lusty, P J; Tai, C C; Sew-Hoy, R P; Walter, W L; Walter, W K; Zicat, B A

    2007-12-01

    Wear debris has been implicated in the pathogenesis of osteolysis. Alumina-on-alumina ceramic bearings have a low wear rate, which may reduce the prevalence of osteolysis. The purpose of this study was to determine the rates of wear and osteolysis associated with modern cementless hip arthroplasty with alumina-on-alumina bearings at five years. We analyzed a series of 301 third-generation alumina-on-alumina cementless primary total hip replacements in 283 patients. The average age of the patients at the time of the arthroplasty was fifty-eight years. All procedures were performed with use of the same surgical technique and the same implant at a single center. At a minimum of five years postoperatively, ten patients had died and twenty-two patients were lost to follow-up. We assessed patients clinically and radiographically, and all retrieved bearings were analyzed for wear. At the time of the latest follow-up, the mean Harris hip score was 95 points. All surviving implants had radiographic evidence of stable bone ingrowth. There were nine revisions of one or both components. Four stems were revised following periprosthetic fracture, one stem was revised because of aseptic loosening at two months, and one stem was revised to facilitate a femoral shortening osteotomy. Two cups were revised because of psoas tendinitis, and both components of one arthroplasty were revised because of impingement and osteolysis. The rate of survival of both components, with revision because of aseptic loosening or osteolysis as the end point, was 99% at seven years. The retrieved femoral heads showed an early median wear rate of 0.2 mm(3) per year. Cementless primary total hip prostheses with a third-generation alumina-on-alumina bearing showed very low wear and were associated with minimal osteolysis at the time of follow-up, at a minimum of five years.

  7. LOW TEMPERATURE SINTERING OF ALUMINA BIOCERAMIC UNDER NORMAL PRESSURE

    Institute of Scientific and Technical Information of China (English)

    2000-01-01

    Superfine alumina powder with high purity (mean particle size is less than 0. 35μm) were used as main starting material for sintering alumina ceramic. A multiple additive MgO-ZrO2 (Y2O3) was homogeneously added into the batch by the chemical coprecipitation method. Sintering of alumina bioceramic at low tempera ture (<1600C) was achieved resulting in a dense and high strength alumina ceramic with the bending strength up to 382 MPa and an improved fracture toughness. Mechanism that the multiple additives promote the sintering of alumina ceramic is discussed on the base of XRD and SEM analysis.

  8. Thermal Conductivity of Alumina-Toughened Zirconia Composites

    Science.gov (United States)

    Bansal, Narottam P.; Zhu, Dong-Ming

    2003-01-01

    10-mol% yttria-stabilized zirconia (10YSZ)-alumina composites containing 0 to 30 mol% alumina were fabricated by hot pressing at 1500 C in vacuum. Thermal conductivity of the composites, determined at various temperatures using a steady-state laser heat flux technique, increased with increase in alumina content. Composites containing 0, 5, and 10-mol% alumina did not show any change in thermal conductivity with temperature. However, those containing 20 and 30-mol% alumina showed a decrease in thermal conductivity with increase in temperature. The measured values of thermal conductivity were in good agreement with those calculated from simple rule of mixtures.

  9. Stabilization of Self-Assembled Alumina Mesophases

    NARCIS (Netherlands)

    Perez, Lidia Lopez; Perdriau, Sebastien; ten Brink, Gert; Kooi, Bart J.; Heeres, Hero Jan; Melian-Cabrera, Ignacio

    2013-01-01

    An efficient route to stabilize alumina mesophases derived from evaporation-induced self-assembly is reported after investigating various aspects in-depth: influence of the solvent (EtOH, s-BuOH, and t-BuOH) on the textural and structural properties of the mesophases based on aluminum

  10. Selective metallization of alumina by laser

    NARCIS (Netherlands)

    Shrivastva, P.B.; Boose, C.A.; Kolster, B.H.; Harteveld, C.; Meinders, B.

    1991-01-01

    Nickel has been selectively deposited on an alumina substrate without any pretreatment from a flow of a nickel acetate solution using the focused beam of an excimer laser. Nickel spots as well as nickel lines were drawn and subsequently plated with an electroless Ni-B coating. Excellent adhesion of

  11. Stabilization of Self-Assembled Alumina Mesophases

    NARCIS (Netherlands)

    Perez, Lidia Lopez; Perdriau, Sebastien; ten Brink, Gert; Kooi, Bart J.; Heeres, Hero Jan; Melian-Cabrera, Ignacio

    2013-01-01

    An efficient route to stabilize alumina mesophases derived from evaporation-induced self-assembly is reported after investigating various aspects in-depth: influence of the solvent (EtOH, s-BuOH, and t-BuOH) on the textural and structural properties of the mesophases based on aluminum tri-sec-butoxi

  12. alumina phase transformation from thermal decomposition of ...

    African Journals Online (AJOL)

    HOD

    INTRODUCTION. Alumina is one of the major components used as catalyst support ... used for processing petroleum, gas, petrochemicals and for other ... The extent and total conversion to the corundum ... purification, vegetable glues, porcelain cements, natural deodorant ..... Catalyst in Steam Reforming of Dimethyl ether:.

  13. Dielectric Performance of High Purity HTCC Alumina at High Temperatures - A Comparison Study with Other Polycrystalline Alumina

    Science.gov (United States)

    Chen, Liang-Yu

    2012-01-01

    A very high purity (99.99+) high temperature co-fired ceramic (HTCC) alumina has recently become commercially available. The raw material of this HTCC alumina is very different from conventional HTCC alumina, and more importantly there is no glass additive in this co-fired material. Previously, selected HTCC and LTCC (low temperature co-fired ceramic) alumina materials were evaluated at high temperatures as dielectric and compared to a regularly sintered 96 polycrystalline alumina (96 Al2O3), where 96 alumina was used as the benchmark. A prototype packaging system based on regular 96 alumina with Au thick-film metallization successfully facilitated long term testing of high temperature silicon carbide (SiC) electronic devices for over 10,000 hours at 500C. In order to evaluate this new HTCC alumina for possible high temperature packaging applications, the dielectric properties of this HTCC alumina substrate were measured and compared with those of 96 alumina and a LTCC alumina from room temperature to 550C at frequencies of 120 Hz, 1 KHz, 10 KHz, 100 KHz, and 1 MHz. A parallel-plate capacitive device with dielectric of the HTCC alumina and precious metal electrodes were used for measurements of the dielectric constant and dielectric loss of the co-fired alumina material in the temperature and frequency ranges. The capacitance and AC parallel conductance of the capacitive device were directly measured by an AC impedance meter, and the dielectric constant and parallel AC conductivity of the dielectric were calculated from the capacitance and conductance measurement results. The temperature and frequency dependent dielectric constant, AC conductivity, and dissipation factor of the HTCC alumina substrate are presented and compared to those of 96 alumina. Other technical advantages of this new co-fired material for possible high packaging applications are also discussed.

  14. MECHANICAL BEHAVIOUR OF ALUMINA-ZIRCONIA COMPOSITE BY SLURRY METHOD

    Directory of Open Access Journals (Sweden)

    JYOTI PRAKASH

    2011-02-01

    Full Text Available Alumina has got some excellent properties like chemical inertness, thermal and mechanical strength against hazardous environment. Alumina is a good ceramic material which is being used for structuralapplications. To enhance the toughness and strength of the body some Zirconia is also used with it. The use of Zirconia in alumina is known as toughening of alumina. One difficulty arises, when alumina and alumina toughened composite are sintered , because the low sinterability of Alumina-Zirconia forced the compact to give very low density body. To overcome this problem alumina and alumina composites are made from slurry method which gives nearly theoretical density. The combined effect of alumina and Zirconia on the phase transformation and microstructure development of heat-treated Alumina-Zirconia composites has been studied. Slurry is prepared by adding water, dispersant, binder and anti-foaming agent. In the present study, Sintering schedule is optimized and kept constant for all samples. After sintering, mechanical behaviour of the composite has been studied.

  15. Surface modification of alumina nanoparticles with silane coupling agents

    Energy Technology Data Exchange (ETDEWEB)

    Prado, Luis A.S.A.; Sriyai, Montira; Ghislandi, Marcos; Schulte, Karl [Technische Universitaet Hamburg-Harburg, Hamburg (Germany). Inst. fuer Kunststoffe und Verbundwerkstoffe (M-11); Barros-Timmons, Ana [University of Aveiro (Portugal). Dept. of Chemistry. Centro de Investigacao em Materiais Ceramicos e Compositos (CICECO)

    2010-07-01

    In the present paper we describe the surface modification of alumina nanoparticles using epoxy-containing alkoxysilanes (silane coupling agents, SCA). The materials were characterized using infrared spectroscopy and solid-state nuclear magnetic resonance. Whereas, neat alumina nanoparticles could be expectedly modified with the afore mentioned SCA, as evidenced by {sup 13}C CPMAS NMR, the presence of arylsulphonates at the surface of alumina caused the ringopening polymerization of the epoxide. This polymerization reaction facilitated the surface modification of alumina by the SCA. X-ray powder diffraction and {sup 27}Al MAS NMR clearly demonstrated that in spite of the SCA polymerization, there were neither structural changes nor phase transitions in the alumina after the surface modification. The surface modification decreased the thermal stability of alumina, in comparison to pristine alumina nanoparticles. (author)

  16. Cloning nanocrystal morphology with soft templates

    Science.gov (United States)

    Thapa, Dev Kumar; Pandey, Anshu

    2016-08-01

    In most template directed preparative methods, while the template decides the nanostructure morphology, the structure of the template itself is a non-general outcome of its peculiar chemistry. Here we demonstrate a template mediated synthesis that overcomes this deficiency. This synthesis involves overgrowth of silica template onto a sacrificial nanocrystal. Such templates are used to copy the morphologies of gold nanorods. After template overgrowth, gold is removed and silver is regrown in the template cavity to produce a single crystal silver nanorod. This technique allows for duplicating existing nanocrystals, while also providing a quantifiable breakdown of the structure - shape interdependence.

  17. Synthesis of alumina-α using aluminium acetate; Sintese de alumina-α utilizando acetato de aluminio

    Energy Technology Data Exchange (ETDEWEB)

    Cartaxo, J.M.; Galdino, M.N.; Neves, G.A., E-mail: lulianamelo25@gmail.com [Universidade Federal de Campina Grande (UFCG), PB (Brazil). Unidade Academica de Engenharia de Materiais; Menezes, R.R.; Ferreira, H.S. [Universidade Federal da Paraiba (UFPB), Joao Pessoa, PB (Brazil). Departamento de Engenharia de Materiais

    2011-07-01

    In the face of great technological importance of alumina, this paper aims to synthesize the α-alumina using chemical activation from aluminum acetate. The synthesized powders were characterized by X-ray diffraction and thermal analysis. The results obtained proved the thermal decomposition of the precursor, as well as possible metastable phases of alumina before the phase transformation in α. There was also difficult to obtain α-alumina from aluminum acetate, on the other hand there was, comparatively, that the chemical activation accelerated the synthesis of α-alumina. (author)

  18. Degradation of alumina and zirconia toughened alumina (ZTA) hip prostheses tested under microseparation conditions in a shock device

    CERN Document Server

    Uribe, Juliana; Gremillard, Laurent; Reynard, Bruno

    2013-01-01

    This paper considers the degradation of alumina and zirconia toughened alumina vs. alumina for hip implants. The materials are as assumed to be load bearing surfaces subjected to shocks in wet conditions. The load is a peak of force; 9 kN was applied over 15 ms at 2 Hz for 800,000 cycles. The volumetric wear and roughness are lower for ZTA than for alumina. The long ZTA ageing did not seem to have a direct influence on the roughness. The ageing increased the wear volumes of ZTA and it was found to have a higher wear resistance compared to alumina.

  19. Artificial pinning centers using the barrier layer of ordered nanoporous alumina templates

    DEFF Research Database (Denmark)

    Hallet, X.; Mátéfi-Tempfli, Stefan; Mátéfi-Tempfli, M.

    2009-01-01

    The barrier layer of self-ordered anodized aluminium oxide, which is grown from an aluminium foil, has been revealed by a selective chemical etching of the remaining aluminium. The surface obtained in this way consists of a triangular lattice of bumps with 100nm spacing, and heights of approximat...

  20. Hemispherical Shell Nanostructures from Metal-Stripped Embossed Alumina on Aluminum Templates

    DEFF Research Database (Denmark)

    Nielsen, Peter; Albrektsen, Ole; Simonsen, Adam Cohen

    2011-01-01

    anodized Al. Utilizing for this process the linear relationship between anodization voltage and the resulting interpore distance in the formed oxide, it is possible to tune the radius of curvature of the resulting hemispherical shells continuously, which in turn results in tunable optical properties...

  1. Graphene coated with alumina and its utilization as a thermal conductivity enhancer for alumina sphere/thermoplastic polyurethane composite

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Ki Tae; Dao, Trung Dung [Department of Chemistry, Energy Harvest-Storage Research Center, University of Ulsan, Ulsan 680-749 (Korea, Republic of); Jeong, Han Mo, E-mail: hmjeong@mail.ulsan.ac.kr [Department of Chemistry, Energy Harvest-Storage Research Center, University of Ulsan, Ulsan 680-749 (Korea, Republic of); Anjanapura, Raghu V. [Center for Emerging Technologies, Jain Global Campus, Jain University, Jakkasandra, Ramanagara 562-112 (India); Aminabhavi, Tejraj M. [Soniya College of Pharmacy, S. R. Nagar, Dharwad 580-002 (India)

    2015-03-01

    Graphene was oxidized with H{sub 2}O{sub 2} to introduce additional anchoring sites for effective alumina coating on graphene by the sol–gel method. The X-ray photoelectron spectroscopy studies showed that the oxygen-containing groups such as hydroxyl group useful for coating were introduced by the oxidation. The transmission electron microscopy images and thermogravimetric analysis data demonstrated that the additional anchoring sites enhanced the efficiency of the alumina coating. A small amount of alumina-coated graphene synergistically improved the thermal conductivity of the alumina sphere/thermoplastic polyurethane (TPU) composite without any increase in the electrical conductivity, because the electrical conductivity of graphene effectively decreased by the alumina coating. Moreover, the synergistic effect of a small amount of graphene was enhanced by the alumina coating, and the stiffening of the alumina sphere/TPU composite due to the added graphene was alleviated by the alumina coating. - Highlights: • Oxidation of graphene with H{sub 2}O{sub 2} introduced anchoring sites for alumina coating. • The anchoring sites improved the efficiency of alumina coating on graphene. • The alumina-coated graphene synergistically enhanced the thermal conductivity.

  2. Template synthesized chitosan nano test tubes for drug delivery applications

    Science.gov (United States)

    Perry, Jillian L. Moulton

    There is tremendous current interest in developing nanoscale drug delivery vehicles. Though intensive efforts have focused on developing spherical drug delivery vehicles, cylindrically shaped vehicles such as nanotubes offer many advantages. Typically, nanotubes can carry a larger inner payload than nanoparticles of the same diameter. Also, we can prepare nanotubes in templates whose geometries can be controlled, in turn allowing precise control over the length and diameter of the tubes. In addition, template synthesized nanotubes can be differentially functionalized on the inner and outer surfaces. Furthermore, templates that are closed on one end can be used to fabricate nano test tubes (closed on one end). The geometry of these nano test tubes allows them to be easily filled with a payload, the open end sealed with a nanoparticle to protect the payload from leaking out, and then the exterior of the tube can be functionalized with a targeting moiety. In an effort to develop such a system, we explored the fabrication of chitosan nano test tubes. Defect-free, chitosan nano test tubes of uniform size were synthesized within the pores of a nanoporous alumina template membrane. While the nano test tubes remained within the template membrane, their inner cavities were filled with a model payload. The payload was then trapped inside the nano test tubes by sealing the open ends of the tubes with latex nanoparticle caps. For proof-of-principle studies, imine linkages were used to attach the caps to the nano test tubes. To create a self-disassembling system, disulfide chemistry was used to covalently cap the nano test tubes. Once removed from the template, the exterior of the nano test tubes were modified with a targeting moiety, allowing them to be targeted to pathological sites. We have also shown that the chitosan nano test tubes are biodegradable by two systems: enzymatic cleavage by lysozymes and disulfide cleavage of the crosslinker by reducing environments

  3. Rheological Properties of Aqueous Nanometric Alumina Suspensions

    Energy Technology Data Exchange (ETDEWEB)

    Li, Chuanping [Iowa State Univ., Ames, IA (United States)

    2004-01-01

    Colloidal processing is an effective and reliable approach in the fabrication of the advanced ceramic products. Successful colloidal processing of fine ceramic powders requires accurate control of the rheological properties. The accurate control relies on the understanding the influences of various colloidal parameters on the rheological properties. Almost all research done on the rheology paid less attention to the interactions of particle and solvent. However, the interactions of the particles are usually built up through the media in which the particles are suspended. Therefore, interactions of the particle with the media, the adsorbed layers on the particle surface, and chemical and physical properties of media themselves must influence the rheology of the suspension, especially for the dense suspensions containing nanosized particles. Relatively little research work has been reported in this area. This thesis addresses the rheological properties of nanometric alumina aqueous suspensions, and paying more attention to the interactions between particle and solvent, which in turn influence the particle-particle interactions. Dense nanometric alumina aqueous suspensions with low viscosity were achieved by environmentally-benign fructose additives. The rheology of nanometric alumina aqueous suspensions and its variation with the particle volume fraction and concentration of fructose were explored by rheometry. The adsorptions of solute (fructose) and solvent (water) on the nanometric alumina particle surfaces were measured and analyzed by TG/DSC, TOC, and NMR techniques. The mobility of water molecules in the suspensions and its variation with particle volume fractions and fructose additive were determined by the 17O NMR relaxation method. The interactions between the nanometric alumina particles in water and fructose solutions were investigated by AFM. The results indicated that a large number of water layers were physically bound on the particles

  4. Rheological Properties of Aqueous Nanometric Alumina Suspensions

    Energy Technology Data Exchange (ETDEWEB)

    Chuanping Li

    2004-12-19

    Colloidal processing is an effective and reliable approach in the fabrication of the advanced ceramic products. Successful colloidal processing of fine ceramic powders requires accurate control of the rheological properties. The accurate control relies on the understanding the influences of various colloidal parameters on the rheological properties. Almost all research done on the rheology paid less attention to the interactions of particle and solvent. However, the interactions of the particles are usually built up through the media in which the particles are suspended. Therefore, interactions of the particle with the media, the adsorbed layers on the particle surface, and chemical and physical properties of media themselves must influence the rheology of the suspension, especially for the dense suspensions containing nanosized particles. Relatively little research work has been reported in this area. This thesis addresses the rheological properties of nanometric alumina aqueous suspensions, and paying more attention to the interactions between particle and solvent, which in turn influence the particle-particle interactions. Dense nanometric alumina aqueous suspensions with low viscosity were achieved by environmentally-benign fructose additives. The rheology of nanometric alumina aqueous suspensions and its variation with the particle volume fraction and concentration of fructose were explored by rheometry. The adsorptions of solute (fructose) and solvent (water) on the nanometric alumina particle surfaces were measured and analyzed by TG/DSC, TOC, and NMR techniques. The mobility of water molecules in the suspensions and its variation with particle volume fractions and fructose additive were determined by the {sup 17}O NMR relaxation method. The interactions between the nanometric alumina particles in water and fructose solutions were investigated by AFM. The results indicated that a large number of water layers were physically bound on the particles

  5. Templated Growth of Carbon Nanotubes

    Science.gov (United States)

    Siochik Emilie J. (Inventor)

    2007-01-01

    A method of growing carbon nanotubes uses a synthesized mesoporous si lica template with approximately cylindrical pores being formed there in. The surfaces of the pores are coated with a carbon nanotube precu rsor, and the template with the surfaces of the pores so-coated is th en heated until the carbon nanotube precursor in each pore is convert ed to a carbon nanotube.

  6. A study of color modulation of porous alumina processed by physical vapor deposition

    Energy Technology Data Exchange (ETDEWEB)

    Wang Xulongqi; Zhang Haijun; Zhang Dongxian, E-mail: zhangdx@zju.edu.cn [State Key Laboratory of Modern Optical Instrumentation, Zhejiang University, Hangzhou, 310027 (China)

    2011-02-01

    With the development of the porous alumina (PA) fabrication technology, more and more scholars plough into the research of its properties, especially optical properties. Recently, we observed an interesting phenomenon that the PA templates processed by Physical Vapor Deposition (PVD) show color differences related to light path difference. Our work attempts to make the principle clear and to find an effective method to modulate the color of PA samples. This article describes the details of our experimental and theoretical results. We successfully prepared some PA templates with different pore-depth by controlling the time of anodization in oxalic acid solution. In order to enhance the reflectivity of air-PA interface, a layer of TiO{sub 2} film of 18 nm is coated with PVD technique, which makes PA templates display quite distinct colors with different hole-depth. By modelling and analyzing PA samples, we make the interpretation of this optical property by taking the PA sample with 150 nm pore-depth as an example, and then put forward a way to simulate sample's color within its hole-depth and material refraction-index. The results are in good agreement with our theoretical analysis, which proves the feasibility of our simulation mode.

  7. Control of the γ-alumina to α-alumina phase transformation for an optimized alumina densification

    Energy Technology Data Exchange (ETDEWEB)

    Lamouri, S.; Hamidouche, M.; Bouaouadja, N.; Belhouchet, H.; Garnier, V.; Fantozzi, G.; Trelkat, J.F.

    2017-07-01

    In this work, we studied the aptitude to sintering green bodies using γ-Al2O3 transition alumina as raw powder. We focused on the influence of the heating rate on densification and microstructural evolution. Phase transformations from transition alumina γ→δ→θ→α-Al2O3 were studied by in situ X-rays diffraction from the ambient to 1200°C. XRD patterns revealed coexistence of various phase transformations during the heating cycle. DTA and dilatometry results showed that low heating rate leads to a significant reduction of the temperature of the α-Al2O3 alumina formation. Around 1190, 1217 and 1240°C were found when using 5, 10 and 20°C/min of heating rate, respectively. The activation energy for θ-Al2O3→α-Al2O3 transformation calculated by Kissinger and JMA equations using dilatometry method were 464.29 and 488.79kJ/mol, respectively and by DTA method were 450.72 and 475.49kJ/mol, respectively. In addition, the sintering of the green bodies with low heating rate promotes the rearrangement of the grains during θ-Al2O3→α-Al2O3 transformation, enhancing the relative density to 95% and preventing the development of a vermicular structure. (Author)

  8. Control of the γ-alumina to α-alumina phase transformation for an optimized alumina densification

    Directory of Open Access Journals (Sweden)

    Samir Lamouri

    2017-03-01

    Full Text Available In this work, we studied the aptitude to sintering green bodies using γ-Al2O3 transition alumina as raw powder. We focused on the influence of the heating rate on densification and microstructural evolution. Phase transformations from transition alumina γ → δ → θ → α-Al2O3 were studied by in situ X-rays diffraction from the ambient to 1200 °C. XRD patterns revealed coexistence of various phase transformations during the heating cycle. DTA and dilatometry results showed that low heating rate leads to a significant reduction of the temperature of the α-Al2O3 alumina formation. Around 1190, 1217 and 1240 °C were found when using 5, 10 and 20 °C/min of heating rate, respectively. The activation energy for θ-Al2O3 → α-Al2O3 transformation calculated by Kissinger and JMA equations using dilatometry method were 464.29 and 488.79 kJ/mol, respectively and by DTA method were 450.72 and 475.49 kJ/mol, respectively. In addition, the sintering of the green bodies with low heating rate promotes the rearrangement of the grains during θ-Al2O3 → α-Al2O3 transformation, enhancing the relative density to 95% and preventing the development of a vermicular structure.

  9. Redox responsive nanotubes from organometallic polymers by template assisted layer by layer fabrication

    Science.gov (United States)

    Song, Jing; Jańczewski, Dominik; Guo, Yuanyuan; Xu, Jianwei; Vancso, G. Julius

    2013-11-01

    Redox responsive nanotubes were fabricated by the template assisted layer-by-layer (LbL) assembly method and employed as platforms for molecular payload release. Positively and negatively charged organometallic poly(ferrocenylsilane)s (PFS) were used to construct the nanotubes, in combination with other polyions. During fabrication, multilayers of these polyions were deposited onto the inner pores of template porous membranes, followed by subsequent removal of the template. Anodized porous alumina and track-etched polycarbonate membranes were used as templates. The morphology, electrochemistry, composition and other properties of the obtained tubular structure were characterized by fluorescence microscopy, scanning (SEM) and transmission electron microscopy (TEM) and energy-dispersive X-ray (EDX) spectroscopy. Composite nanotubes, consisting of poly(acrylic acid) anions with PFS+ and nanoparticles including fluorophore labelled dextran and decorated quantum dots, with PFS polyelectrolytes were also fabricated, broadening the scope of the structures. Cyclic voltammograms of PFS containing nanotubes showed similar redox responsive behaviour to thin LbL assembled films. Redox triggered release of labelled macromolecules from these tubular structures demonstrated application potential in controlled molecular delivery.Redox responsive nanotubes were fabricated by the template assisted layer-by-layer (LbL) assembly method and employed as platforms for molecular payload release. Positively and negatively charged organometallic poly(ferrocenylsilane)s (PFS) were used to construct the nanotubes, in combination with other polyions. During fabrication, multilayers of these polyions were deposited onto the inner pores of template porous membranes, followed by subsequent removal of the template. Anodized porous alumina and track-etched polycarbonate membranes were used as templates. The morphology, electrochemistry, composition and other properties of the obtained tubular

  10. Influence of alumina characteristics on glaze properties

    Directory of Open Access Journals (Sweden)

    Arrufat, S.

    2010-10-01

    Full Text Available Aluminium oxide is a synthetic raw material manufactured from bauxite by the Bayer process, whose Al2O3 content typically exceeds 99%. Four main types of alumina can be defined, depending on the processing used: hydrargillite Al(OH3, boehmite AlOOH, transition aluminas (calcined at low temperatures, 1000 °C, with an intermediary crystallographic structure between hydrates and alpha alumina, and α-Al2O3 (calcined at high temperatures, >1100 °C. In glaze manufacturing, α-Al2O3 is the main type of alumina used. This raw material acts as a matting agent: the matt effect depends on alumina particle size and content in the glaze. This study examines the effect of the degree of alumina calcination on glaze technical and aesthetic properties. For this purpose, aluminas with different degrees of calcination were added to a glaze formulated with a transparent frit and kaolin, in order to simplify the system to be studied. The results show that, depending on the degree of calcination, alumina particles can react with the glaze components (SiO2, CaO, and ZnO to form new crystalline phases (anorthite and gahnite. Both crystallisations extract CaO and ZnO from the glassy phase, increasing glassy phase viscosity. The variation in crystalline phases and glassy phase viscosity yields glazes with different technical and aesthetic properties.

    El óxido de aluminio es una materia prima sintética fabricada a partir de la bauxita por medio del proceso Bayer, cuyo contenido de Al2O3 supera, por regla general, el 99%. Se pueden definir cuatro tipos de alúmina, en función del tipo de proceso usado: hidrargilita Al(OH3, boehmita AlOOH, alúminas de transición (calcinadas a bajas temperaturas, 1000 °C, con una estructura cristalográfica intermedia entre los hidratos y la alfa alúmina, y la α-Al2O3 (calcinada a

  11. Impact of AD995 alumina rods

    Energy Technology Data Exchange (ETDEWEB)

    Chhabildas, L.C.; Furnish, M.D.; Reinhart, W.D. [Sandia National Labs., Albuquerque, NM (United States); Grady, D.E. [Applied Research Associates, Inc., Albuquerque, NM (United States)

    1997-10-01

    Gas guns and velocity interferometric techniques have been used to determine the loading behavior of an AD995 alumina rod 19 mm in diameter by 75 mm and 150 mm long, respectively. Graded-density materials were used to impact both bare and sleeved alumina rods while the velocity interferometer was used to monitor the axial-velocity of the free end of the rods. Results of these experiments demonstrate that (1) a time-dependent stress pulse generated during impact allows an efficient transition from the initial uniaxial strain loading to a uniaxial stress state as the stress pulse propagates through the rod, and (2) the intermediate loading rates obtained in this configuration lie between split Hopkinson bar and shock-loading techniques.

  12. Nanoparticles in alumina: Microscopy and Theory

    Science.gov (United States)

    Idrobo, Juan C.; Halabica, Andrej; Rashkeev, Sergey; Glazoff, Michael V.; Boatner, Lynn A.; Haglund, Richard F.; Pennycook, Stephen. J.; Pantelides, Sokrates T.

    2007-03-01

    Transition-metal nanoparticles formed by ion implantation in alumina can be used to modify the optical properties of naturally oxidized and anodized aluminum. Here, we report atomic-resolution Z-contrast images using a scanning transmission electron microscope (STEM) of CoFe and other metal nanoparticles in alumina. We also report electron energy loss spectra (EELS) and relate them to visual appearance and optical properties. Finally, we report first-principles density- functional calculations of nucleation mechanisms for these nanoparticles. This research was sponsored by the Office of Basic Energy Sciences, Division of Materials Sciences and Engineering, U.S. Department of Energy, under contract DE-AC05- 00OR22725 with Oak Ridge National Laboratory, managed and operated by UT-Battelle, by NSF grant No. DMR-0513048, and by Alcoa Inc.

  13. Silica containing highly porous alumina ceramic

    Science.gov (United States)

    Svinka, R.; Svinka, V.; Zake, I.

    2011-04-01

    Porous alumina ceramic were produced by slip casting of aqueous alumina slurry with added small amount of metallic aluminium powder. Pores form in result of chemical reaction of aluminum with water by hydrogen gas evolution reaction and solidification of suspension. Porosity of such materials sintered at a temperature of 1600 - 1750°C varies from 60 to 90%. Pore size distribution and mechanical strength of these materials depend largely on the grain size of used raw materials. The major part of pores in the materials produced without additive of silica are larger than 10 ±m, but with 5 - 10 wt.% additive of silica in the raw mix pore size decreases considerably. The sintering shrinkage decreases to 2.5%. Coefficient of thermal expansion equally decreases from 8.9-10-6 K-1 to 7.1 10-6 K-1 and classification temperature increases to 1600°C, while deformation at high temperature decreases considerably.

  14. Improvement in nanoscale contact resistance of alumina

    Energy Technology Data Exchange (ETDEWEB)

    Bhattacharya, Manjima; Chakraborty, Riya; Mandal, Ashok Kumar [CSIR - Central Glass and Ceramic Research Institute, Kolkata (India); Dey, Arjun [CSIR - Central Glass and Ceramic Research Institute, Kolkata (India); ISRO Satellite Centre, Thermal Systems Group, Bangalore (India); Mukhopadhyay, Anoop Kumar [CSIR - Central Glass and Ceramic Research Institute, Kolkata (India); Central Glass and Ceramic Research Institute, Kolkata 32 (India)

    2012-06-15

    In all contact-related applications such as the wear-resistant inserts, biomedical implants, high strain rate impact-resistant plates, etc., nanohardness, i.e. the intrinsic contact resistance at the nano scale, plays a major role. In spite of the wealth of literature, the studies on nanohardness of dense, coarse-grain alumina ceramics which represent many commercial varieties; have reasonably good hardness at the macro scale and characteristically exhibit R-curve behaviour, are far from significant. Here, to the best of our knowledge, we report for the first time the experimental observations of the increase in intrinsic contact resistance at the nano scale with the loading rate applied to a high-density ({proportional_to}95 % of theoretical) coarse-grain ({proportional_to}20 {mu}m) alumina ceramics. These observations were explained in terms of the initiation of nanoscale plasticity and maximum shear stress generated just underneath the nanoindenter. (orig.)

  15. Polyfluorene nanowires with pronounced axial texturing prepared by melt-assisted template wetting

    Energy Technology Data Exchange (ETDEWEB)

    O' Carroll, Deirdre; Irwin, Jennifer [Nanotechnology Group, Tyndall National Institute, Lee Maltings, Prospect Row, Cork (Ireland); Tanner, David A. [Department of Manufacturing and Operations Engineering, Materials and Surface Science Institute, University of Limerick, Limerick (Ireland); Redmond, Gareth [Nanotechnology Group, Tyndall National Institute, Lee Maltings, Prospect Row, Cork (Ireland)], E-mail: gareth.redmond@tyndall.ie

    2008-02-15

    Poly(9,9-dioctylfluorene) conjugated polymer nanowires were fabricated by melt-assisted wetting of porous anodic alumina templates. Analysis by high-resolution transmission electron microscopy and X-ray diffraction suggested that the polymer molecules were axially textured within the nanowires. Polarized optical microscopy images of single nanowires exhibited a pronounced optical birefringence consistent with internal axial alignment of the polymer molecules. Polarization-resolved photoluminescence images and spectra were acquired following near-field optical addressing of single nanowires. This data revealed that nanowire luminescence was markedly anisotropic with a preferred axial polarization of wire emission.

  16. Tribology of alumina-graphite composites

    Science.gov (United States)

    Yu, Chih-Yuan

    Alumina-graphite composites, which combine high wear resistance and self-lubricity, are a potential and promising candidate for advanced tribological applications. The processing, mechanical properties and tribology of alumina-graphite composites are discussed. Full density is difficult to achieve by a pressureless sintering route. Porosity of the composites increases with graphite content which causes the strength, modulus of elasticity, and hardness of the composites to decrease. The increased porosity does cause the fracture toughness to slightly increases. Tribology of alumina-graphite composites was studied with a pin-on-disk tribometer with emphasis on the following aspects: the graphite content in both pin and disk, the graphite flake size and the orientation of the graphite flakes. Scan electronic microscopy (SEM) and X-ray diffraction are utilized to examine and characterize the wear debris and the worn surface. Results confirmed that it is necessary to optimize the structure and the supply of lubricant to improve the tribological behavior and that the arrangements of sliding couples also affect the tribology of self-lubricated ceramic composites. Continuous measurements of the friction coefficients were collected at high frequency in an attempt to correlate the tribology of alumina-graphite composites to vibrations introduced by friction. While these measurements indicate that the time frequency behavior of tribology is an important area of study, conclusions regarding the frequency response of different sliding couples could not be definitively stated. Finally, a new concept connecting instantaneous wear coefficient and instantaneous contact stress is proposed for prediction of wear behavior of brittle materials.

  17. Ultraviolet photoluminescence of porous anodic alumina films

    Institute of Scientific and Technical Information of China (English)

    2003-01-01

    Photoluminescence (PL) properties of porous anodic alumina (PAA) films prepared by using electrochemical anodization technique in a mixed solution of oxalic and sulfuric acid have been investigated. The PAA films have an intensive ultraviolet PL emission around 350 nm, of which a possible PL mechanism has been proposed. It was found that the incorporated oxalic ions, which could transform into PL centers and exist in the PAA films, are responsible for this ultraviolet PL emission.

  18. The LOLITA User-Definable Template Interface

    OpenAIRE

    Košmelj, Katarina

    2001-01-01

    The development of user-definable templates interfaces which allow the user to design new templates definitions in a user-friendly way is a new issue in the field of information extraction. The LOLITA user-definable templates interface allows the user to define new templates using sentences in natural language text with a few restrictions and formal elements. This approach is rather different from previous approaches to information extraction which require developers to code the template defi...

  19. Free-standing alumina nanobottles and nanotubes pre-integrated into nanoporous alumina membranes

    Science.gov (United States)

    Fang, Jinghua; Levchenko, Igor; (Ken Ostrikov, Kostya

    2014-08-01

    A novel interfacial structure consisting of long (up to 5 μm), thin (about 300 nm), highly-ordered, free-standing, highly-reproducible aluminum oxide nanobottles and long tubular nanocapsules attached to a rigid, thin (less than 1 μm) nanoporous anodic alumina membrane is fabricated by simple, fast, catalyst-free, environmentally friendly voltage-pulse anodization. A growth mechanism is proposed based on the formation of straight channels in alumina membrane by anodization, followed by neck formation due to a sophisticated voltage control during the process. This process can be used for the fabrication of alumina nanocontainers with highly controllable geometrical size and volume, vitally important for various applications such as material and energy storage, targeted drug and diagnostic agent delivery, controlled drug and active agent release, gene and biomolecule reservoirs, micro-biologically protected platforms, nano-bioreactors, tissue engineering and hydrogen storage.

  20. Influence of TAC on Dispersion of Aqueous Nano Alumina Suspension

    Institute of Scientific and Technical Information of China (English)

    ZHAO Wei; YANG De-an; SONG Jian-jing; YANG Zi; LIANG Chong; XU Ming-xia; XU Ting-xian

    2004-01-01

    The stability of aqueous nano alumina powder suspensions with and without dispersant tri-ammonium citrate (TAC) was investigated by measuring zeta potential at different pH values. The isoelectric point (IEP) of alumina powder shifts towards more acidic pH range by adding TAC dispersant. The results illustrate that adsorption of TAC on alumina powder surface existed in the aqueous suspension, which leads to a high stability of the suspension.

  1. Novel self assembly behavior for γ-alumina nanoparticles

    Institute of Scientific and Technical Information of China (English)

    Osama Saber

    2012-01-01

    In this study,self assembly behavior was induced for γ-alumina nanoparticles by adsorption of dimethyl disulfide.Following this trend,we have developed a chemical process to obtain γ-alumina in the nano scale.Scanning electron microscopy images of the prepared γ-alumina showed big and strong agglomeration of the nanoparticles indicating that these nanoparticles have strong surface forces.Transmission electron microscopy images confirmed that the γ-alumina nanoparticles 3-7 nm in size were converted to uniform spherical shape in the size range of 1-2 mm after shaking with dimethyl disulfide in the presence of n-hexane at room temperature.This phenomenon did not appear in the case of alumina in the micro scale.The surface properties of the prepared γ-alumina in the nano scale were characterized and compared with the γ-alumina in the micro scale by using low temperature nitrogen adsorption-desorption system,indicating that the specific surface area of the prepared γ-alumina nanoparticles is larger than that of the γ-alumina in the micro scale.Furthermore,micro-and meso-pores were observed for the γ-alumina nanoparticles while only mesoporous structure was detected for the γ-alumina in the micro scale.These experimental results suggested that the self assembly behavior of the γ-alumina nanoparticles may be due to the selective adsorption of dimethyl disulfide in the micropores of these nanoparticles to act as bridge linking the nanoparticles.

  2. Corrosion of Refractory Alumina-Graphite and Alumina-Graphite-Zirconia in Slag Containing Titania

    Institute of Scientific and Technical Information of China (English)

    XU Yuan; LIU Qing-cai; BAI Chen-guang; CHEN Deng-fu; Joseph W Newkirk

    2004-01-01

    The corrosion of refractory alumina-graphite and alumina-graphite-zirconia in the slag containing titania was studied by immersion tests (quasi-static and dynamic tests). Combining direct observation with microscopic investigations, a mechanism for corrosion was proposed based on the oxidation of graphite and the dissolution of refractory components. During the corrosion process, there are some special phenomena and laws that can be explained by the relation between the corrosion rate and the TiO2 mass percent, the rotational refractory velocity and the morphology of the deteriorated layer.

  3. Modelling the initial stage of porous alumina growth during anodization

    Science.gov (United States)

    Aryslanova, E. M.; Alfimov, A. V.; Chivilikhin, S. A.

    2013-05-01

    Artificially on the surface of aluminum there may be build a thick layer of Al2O3, which has a porous structure. In this paper we present a model of growth of porous alumina in the initial stage of anodizing, identifying dependencies anodizing parameters on the rate of growth of the film and the distance between the pores and as a result of the created model equations were found for changes in the disturbance of alumina for the initial stage of anodizing aluminum oxide porous border aluminum-alumina and alumina-electrolyte, with the influence of surface diffusion of aluminum oxide.

  4. Aqueous combustion synthesis and characterization of zirconia-alumina nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Kishan, J.; Mangam, Venu; Reddy, B.S.B.; Das, Siddhartha [Department of Metallurgical and Materials Engineering, Indian Institute of Technology, Kharagpur, West Bengal 721302 (India); Das, Karabi, E-mail: karabi@metal.iitkgp.ernet.i [Department of Metallurgical and Materials Engineering, Indian Institute of Technology, Kharagpur, West Bengal 721302 (India)

    2010-02-04

    The zirconia-alumina nanocomposite powders with 3-48 mol% of alumina are prepared by aqueous combustion synthesis technique using stoichiometric amounts of aluminium nitrate, zirconyl nitrate and glycine. The nanopowders are compacted uniaxially and sintered at 1000 {sup o}C temperature in a muffle furnace. Thermodynamic modeling of the combustion reaction shows that, as the alumina content increases, the amount of gases produced increases with a decrease in the adiabatic flame temperature. The green and sintered densities of cold press composite powders decrease with an increase in the mol% of alumina.

  5. Rheology of Alumina-Based Graphite-Containing Castables

    Institute of Scientific and Technical Information of China (English)

    YE Fangbao; M. Rigaud; LIU Xinhong; ZHONG Xiangchong

    2005-01-01

    In this work, the rheological behavior of ultra-low cement alumina-based castables with addition of flake graphite and extruded graphite pellets has been investigated by using IBB rheometer. Emphasis has been laid on the influence of the type and amount of carbon addition on rheological properties of the alumina-based castables and the results are compared with corresponding alumina castable samples without any carbon addition. It is found that alumina-based castables with extruded graphite pellets have good rheological behavior and flowability with lower water demand ( < 6. 3% )and no segregation during the shearing of castable.

  6. Template synthesis of test tube nanoparticles using non-destructive replication.

    Science.gov (United States)

    Wagner, Jonathan; Yao, Jingyuan; Rodgers, David; Hinds, Bruce

    2013-03-01

    Nano test tubes are a promising delivery vehicle for a range of therapeutics, including small molecule drugs and biologics. However, current template synthesis methods of producing nano test tubes are prohibitively expensive and time consuming. Here, non-destructive template replication was used to increase nano test tube yield from porous alumina by more than a hundredfold. We demonstrate how to produce nano test tubes of several sizes and compositions, including hybrid tubes with different inner and outer surfaces for targeted surface chemistry. Nano test tubes were readily suspended and stored in aqueous solutions without the need for chemical treatment. These nano test tubes should find application as delivery vehicles for therapeutics, particularly for processive 'bionanoreactors' loaded with enzymes.

  7. Restrictions of Si-based Ge nanodots from porous alumina membranes

    Science.gov (United States)

    Zhan, Wenbo; Huangfu, Yourui; Ding, Guqiao; Ye, Hui

    2013-08-01

    This paper reports growth of ordered Ge nanodots (NDs) with uniform sizes on silicon substrates using porous alumina membranes (PAMs) as templates. The relationships between substrate temperatures (400-600 °C) and site distribution of Ge NDs are studied. Ordered arrangements of Ge NDs are realized at 400 °C and 500 °C, respectively. Due to joint effect of substrate temperature and restrictions from PAM, an uncommon size change trend is found. At 400 °C, triangular pyramid-like and short cylindrical Ge NDs are obtained with different nanopore aspect ratios of PAMs. A geometrical optic method is used to analyze the mechanism of Ge NDs with such shapes. Raman characterization is utilized to study the strain in Ge NDs. As a result, almost pure Ge content and 1.5% tensile strain are revealed, which are attributed respectively to the low substrate temperature and thermal mismatch among Si substrate, Ge ND and PAM.

  8. Plasmonic properties of gold-coated nanoporous anodic alumina with linearly organized pores

    Indian Academy of Sciences (India)

    Dheeraj Pratap; P Mandal; S Anantha Ramakrishna

    2014-12-01

    Anodization of aluminium surfaces containing linearly oriented scratches leads to the formation of nanoporous anodic alumina (NAA) with the nanopores arranged preferentially along the scratch marks. NAA, when coated with a thin gold film, support plasmonic resonances. Dark-field spectroscopy revealed that gold-coated NAA with such linearly arranged pores shows a polarization-dependent scattering, that is larger when the incident light is polarized parallel to the scratch direction than when polarized perpendicular to the scratch direction. Fluorescence studies from rhodamine-6G (R6G) molecules dissolved in polymethylmethacrylate (PMMA) and deposited on these NAA templates showed that fluorescence can be strongly enhanced with the bare NAA due to multiple light scattering in the NAA, while fluorescence from the molecules deposited on gold-coated NAA is strongly quenched due to the strong plasmonic coupling.

  9. Enhancing the platinum atomic layer deposition infiltration depth inside anodic alumina nanoporous membrane

    Energy Technology Data Exchange (ETDEWEB)

    Vaish, Amit, E-mail: anv@udel.edu; Krueger, Susan; Dimitriou, Michael; Majkrzak, Charles [National Institute of Standards and Technology (NIST) Center for Neutron Research, Gaithersburg, MD 20899-8313 (United States); Vanderah, David J. [Institute for Bioscience and Biotechnology Research, NIST, Rockville, Maryland 20850 (United States); Chen, Lei, E-mail: lei.chen@nist.gov [NIST Center for Nanoscale Science and Technology, Gaithersburg, Maryland 20899-8313 (United States); Gawrisch, Klaus [Laboratory of Membrane Biochemistry and Biophysics, National Institute on Alcohol Abuse and Alcoholism, National Institutes of Health, Bethesda, Maryland 20892 (United States)

    2015-01-15

    Nanoporous platinum membranes can be straightforwardly fabricated by forming a Pt coating inside the nanopores of anodic alumina membranes (AAO) using atomic layer deposition (ALD). However, the high-aspect-ratio of AAO makes Pt ALD very challenging. By tuning the process deposition temperature and precursor exposure time, enhanced infiltration depth along with conformal coating was achieved for Pt ALD inside the AAO templates. Cross-sectional scanning electron microscopy/energy dispersive x-ray spectroscopy and small angle neutron scattering were employed to analyze the Pt coverage and thickness inside the AAO nanopores. Additionally, one application of platinum-coated membrane was demonstrated by creating a high-density protein-functionalized interface.

  10. Optical and magnetic properties of porous anodic alumina films embedded with Co nanowires

    Institute of Scientific and Technical Information of China (English)

    Zhang Jing-Jing; Li Zi-Yue; Zhang Hui-Min; Hou Xue; Sun Hui-Yuan

    2013-01-01

    A simple method to tune the optical properties of porous anodic alumina (PAA) films embedded with Co nanowires (PAA@Co nanocomposite films) is reported in this paper.The films exhibit vivid structural colors and magnetic properties.The optical properties of the films can be effectively tuned by adjusting the thickness of the PAA template.The deposition of Co nanowires greatly increases the color saturation of the PAA films.The theoretical results of the changes in structural color according to the Bragg-Snell formula are consistent with the experimental results.PAA@Co films can be used in many areas,including decoration,display,and multifunctional anti-counterfeiting applications.

  11. Biometric template transformation: a security analysis

    Science.gov (United States)

    Nagar, Abhishek; Nandakumar, Karthik; Jain, Anil K.

    2010-01-01

    One of the critical steps in designing a secure biometric system is protecting the templates of the users that are stored either in a central database or on smart cards. If a biometric template is compromised, it leads to serious security and privacy threats because unlike passwords, it is not possible for a legitimate user to revoke his biometric identifiers and switch to another set of uncompromised identifiers. One methodology for biometric template protection is the template transformation approach, where the template, consisting of the features extracted from the biometric trait, is transformed using parameters derived from a user specific password or key. Only the transformed template is stored and matching is performed directly in the transformed domain. In this paper, we formally investigate the security strength of template transformation techniques and define six metrics that facilitate a holistic security evaluation. Furthermore, we analyze the security of two wellknown template transformation techniques, namely, Biohashing and cancelable fingerprint templates based on the proposed metrics. Our analysis indicates that both these schemes are vulnerable to intrusion and linkage attacks because it is relatively easy to obtain either a close approximation of the original template (Biohashing) or a pre-image of the transformed template (cancelable fingerprints). We argue that the security strength of template transformation techniques must consider also consider the computational complexity of obtaining a complete pre-image of the transformed template in addition to the complexity of recovering the original biometric template.

  12. Excitation and emission processes of Tb{sup 3+} in porous anodic alumina

    Energy Technology Data Exchange (ETDEWEB)

    Dabboussi, S. [Unite de recherche de Spectroscopie Raman, Departement de Physique, Faculte des Sciences de Tunis, Elmanr 2092, Tunis (Tunisia); Elhouichet, H. [Unite de recherche de Spectroscopie Raman, Departement de Physique, Faculte des Sciences de Tunis, Elmanr 2092, Tunis (Tunisia)], E-mail: habib.elhouichet@fst.rnu.tn; Bouzidi, C. [Unite de recherche de Spectroscopie Raman, Departement de Physique, Faculte des Sciences de Tunis, Elmanr 2092, Tunis (Tunisia); Maliarevich, G.K.; Gaponenko, N.V. [Belarusian State University of Informatics and Radioelectronics, P. Browki St. 6, 220013 Minsk (Belarus); Oueslati, M. [Unite de recherche de Spectroscopie Raman, Departement de Physique, Faculte des Sciences de Tunis, Elmanr 2092, Tunis (Tunisia)

    2009-01-15

    The strong photoluminescence (PL) of porous anodic alumina (PAA) with terbium deposition is reported. PAA, which has a regular pore morphology, is considered an effective template for fabricating luminescent composites. Tb was deposited onto PAA films by immersion in alcoholic solution with terbium chloride followed by heat treatment. The PL spectra demonstrate typical bands of Tb{sup 3+} corresponding to {sup 5}D{sub 4} {yields} {sup 7}F{sub j} (j = 3, 4, 5, 6,) electron transition, with the maximum at 18,360 cm{sup -1} ({sup 5}D{sub 4} {yields} {sup 7}F{sub 5}). The PL mechanism of Tb{sup 3+} was systematically studied with annealing temperature. The non-radiative relaxation channel is provided by OH hydroxyls at the surface of porous anodic alumina and, after annealing at 900 deg. C, the PL yield is highly improved. The PL intensity of Tb{sup 3+} increases with laser power and a saturation phenomenon, associated with the ratio of Tb{sup 3+} to Tb{sup 4+} ions, is observed at approximately 90 W/cm{sup 2}. Based on a theoretical model, the optical cross-section {sigma} of terbium in PAA is estimated, with a value close to that of other porous materials doped with the rare-earth elements.

  13. Quantificational Etching of AAO Template

    Institute of Scientific and Technical Information of China (English)

    Guojun SONG; Dong CHEN; Zhi PENG; Xilin SHE; Jianjiang LI; Ping HAN

    2007-01-01

    Ni nanowires were prepared by electrodeposition in porous anodized aluminum oxide (AAO) template from a composite electrolyte solution. Well-ordered Ni nanowire arrays with controllable length were then made by the partial removal of AAO using a mixture of phosphoric acid and chromic acid (6 wt pct H3PO4:1.8 wt pct H3CrO4). The images of Ni nanowire arrays were studied by scanning electron microscopy (SEM) to determine the relationship between etching time and the length of Ni nanowire arrays. The results indicate that the length of nanowires exposed from the template can be accurately controlled by controlling etching time.

  14. Synthesis of Rh/Macro-Porous Alumina Over Micro-Channel Plate and Its Catalytic Activity Tests for Diesel Reforming.

    Science.gov (United States)

    Seong, Yeon Baek; Kim, Yong Sul; Park, No-Kuk; Lee, Tae Jin

    2015-11-01

    Macro-porous Al2O3 as the catalytic support material was synthesized using colloidal polystyrene spheres over a micro-channel plate. The colloidal polystyrene spheres were used as a template for the production of an ordered macro porous material using an alumina nitrate solution as the precursor for Al2O3. The close-packed colloidal crystal array template method was applied to the formulation of ordered macro-porous Al2O3 used as a catalytic support material over a micro-channel plate. The solvent in the mixture solution, which also contained the colloidal polystyrene solution, aluminum nitrate solution and the precursor of the catalytic active materials (Rh), was evaporated in a vacuum oven at 50 degrees C. The ordered polystyrene spheres and aluminum salt of the solid state were deposited over a micro channel plate, and macro-porous Al2O3 was formed after calcination at 600 degrees C to remove the polystyrene spheres. The catalytic activity of the Rh/macro-porous alumina supported over the micro-channel plate was tested for diesel reforming.

  15. NMR Revealed Activated Alumina-Water Interaction

    Institute of Scientific and Technical Information of China (English)

    ZHOU Rui; ZHOU Yan; HU Kai; JI Zhen-ping; CHENG Gong-zhen

    2005-01-01

    Three different spin-lattice relaxation times (T1) of water were obtained in activated alumina-water slurry system, which indicate that there exist three states of water: bound water, pore water and bulk water. The chemical shift (δH) decreases as the amount of water added to the system increases due to the differences in contribution of these three states of water in the samples. The δH value for adsorbed water decreases nearly linearly and T1 increases with elevating temperature, which result from the decrease in the content of bound water by the increase in thermal motion.

  16. Anisotropic shrinkage characteristics of tape cast alumina

    Science.gov (United States)

    Patwardhan, Jaideep Suresh

    Dimensional control during sintering is a major issue in ceramics processing to avoid high post-sintering costs associated with machining of the fired ceramic part to desired tolerances and dimensions. Ceramic forming processes such as tape casting, injection molding, and extrusion involve shear of anisotropic particles resulting in preferential alignment of the particles in the green body. This preferential alignment causes directionality in mechanical, electrical, optical, and magnetic properties and most importantly warpage or distortion during sintering. A large effort has been devoted to synthesizing ceramic green bodies with minimal density gradients and uniform packing and modeling the sintering behavior evolution but little effort has been devoted to characterizing orientation of particles and the effect of preferential alignment on sintering shrinkage anisotropy. A systematic study was initiated to study the effect of processing variables such as shear rate, solids loading, temperature, and binder content on aqueous tape cast alumina. Three different alumina systems: A16-SG, Baikowski RC-UFX DBM and RC-LS DBM were investigated. Aqueous tapes of high solids loading alumina (56 vol. %) were tape cast at various speeds and thicknesses and assuming plane Couette flow a shear rate regime of 21--270 s-1 was investigated. Higher shear rates and high solids loading resulted in higher in-plane anisotropy whereas the anisotropy in the thickness direction was higher for low solids loading systems. The anisotropy was found to be fairly constant above a certain critical shear rate (˜100 s-1) irrespective of the temperature and the solids loading and this correlated with the viscosity-shear rate relationship of the cast slips. The higher shrinkage anisotropy in the thickness direction for the low solids loading systems (35 and 45 vol. %) was attributed to the higher amount of organics in the slip required to sustain the suitable viscosity for tape casting and

  17. Nanotube Arrays in Porous Anodic Alumina Membranes

    Institute of Scientific and Technical Information of China (English)

    Liang LI; Naoto KOSHIZAKI; Guanghai LI

    2008-01-01

    This review summarizes the various techniques developed for fabricating nanotube arrays in porous anodic alumina membranes (AAMs). After a brief introduction to the fabrication process of AAMs, taking carbons, metals, semiconductors, organics, biomoleculars, and heterojunctions as typical examples, attention will be focused on the recently established methods to fabricate nanotubes in AAM, including electrochemical deposition, surface sol-gel, modified chemical vapor deposition, atomic layer deposition, and layer-by-layer growth. Every method is demonstrated by one or two reported results. Finally, this review is concluded with some perspectives on the research directions and focuses on the AAM-based nanotubes fields.

  18. Intercalation of water into lithium. beta. -alumina

    Energy Technology Data Exchange (ETDEWEB)

    Dudney, N J; Bates, J B; Wang, J C; Brown, G M; Larson, B C; Engstrom, H

    1981-01-01

    Infrared absorption, neutron diffraction and weight loss techniques have been used to investigate the hydration of single crystals of Li ..beta..-alumina. The hydration is a reversible intercalation reaction. Up to approximately two water molecules per formula unit can penetrate the conduction plane. Other protonated species are formed from the dissociation of the molecular water. The rate of hydration is controlled by the diffusion of water in the conduction plane. A likely diffusion mechanism requires dissociation of the water and an interstitialcy motion of the oxygen.

  19. Progress of NIL template making

    Science.gov (United States)

    Yusa, Satoshi; Hiraka, Takaaki; Kobiki, Ayumi; Sasaki, Shiho; Itoh, Kimio; Toyama, Nobuhito; Kurihara, Masaaki; Mohri, Hiroshi; Hayashi, Naoya

    2007-05-01

    Nano-imprint lithography (NIL) has been counted as one of the lithography solutions for hp32nm node and beyond. Recently, the small line edge roughness (LER) as well as the potentially high resolution that will ensure no-OPC mask feature is attracting many researchers. The template making is one of the most critical issues for the realization of NIL. Especially when we think of a practical template fabrication process on a 65mm square format that is going to be the industry standard, the resolution of the template making process showed a limitation. We have achieved for the first time an hp22nm resolution on the 65nm template format. Both line and space patterns and hole patterns were well resolved. Regarding dot patterns, we still need improvement, but we have achieved resolution down to hp28nm. Although so far we cannot achieve these resolution limits of various pattern category at the same time on one substrate, an intermediate process condition showed sufficient uniformity both in lateral CD and in vertical depth. Global pattern image placement also showed sufficient numbers at this stage of lithography development. A 20nm feature (with a pitch of 80nm) showed sufficient imprint result.

  20. Supply-Chain Optimization Template

    Science.gov (United States)

    Quiett, William F.; Sealing, Scott L.

    2009-01-01

    The Supply-Chain Optimization Template (SCOT) is an instructional guide for identifying, evaluating, and optimizing (including re-engineering) aerospace- oriented supply chains. The SCOT was derived from the Supply Chain Council s Supply-Chain Operations Reference (SCC SCOR) Model, which is more generic and more oriented toward achieving a competitive advantage in business.

  1. 21 CFR 73.1010 - Alumina (dried aluminum hydroxide).

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 1 2010-04-01 2010-04-01 false Alumina (dried aluminum hydroxide). 73.1010 Section 73.1010 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES GENERAL LISTING OF COLOR ADDITIVES EXEMPT FROM CERTIFICATION Drugs § 73.1010 Alumina (dried...

  2. Textural stability of titania–alumina composite membranes

    NARCIS (Netherlands)

    Kumar, Krishnankutty-Nair P.; Keizer, Klaas; Burggraaf, Anthonie J.

    1993-01-01

    Textural evolution (porosity reduction, pore and crystallite growth) in titania–alumina composite membranes has been studied using thermal analysis, X-ray diffraction, field emission scanning electron microscopy and N2 physisorption techniques. The presence of alumina in the membranes improved the t

  3. Chemical modification/grafting of mesoporous alumina with polydimethylsiloxane (PDMS)

    NARCIS (Netherlands)

    Pinheiro de Melo, A.F.; Nijmeijer, A.; Sripathi, V.G.P.; Winnubst, A.J.A.

    2015-01-01

    A method for polydimethylsiloxane grafting of alumina powders is described which involves chemical modification of the surface of mesoporous (5 nm) γ-alumina flakes with a linker (3-aminopropyltriethoxysilane: APTES), either by a solution phase (SPD) or a vapour phase (VPD) reaction, followed by PDM

  4. Chemical modification/grafting of mesoporous alumina with polydimethylsiloxane (PDMS)

    NARCIS (Netherlands)

    Pinheiro de Melo, A.F.; Nijmeijer, Arian; Sripathi, V.G.P.; Winnubst, Aloysius J.A.

    2015-01-01

    A method for polydimethylsiloxane grafting of alumina powders is described which involves chemical modification of the surface of mesoporous (5 nm) γ-alumina flakes with a linker (3-aminopropyltriethoxysilane: APTES), either by a solution phase (SPD) or a vapour phase (VPD) reaction, followed by

  5. Development of Reproducing Alumina-Magnesia-Carbon Bricks

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    The reproducing alumina-magnesia-carbon bricks were prepared with the dumped bricks as starting materials. The bulk density, apparent porosity, crushing strength, modolus of rupture and slag resistance of the specimen were analyzed. The results show that the used refractories can be reused and recycled by the right method. The reproducing alumina-magnesia-carbon bricks with better abilities were prepared.

  6. 40 CFR 721.10120 - Siloxane modified alumina nanoparticles (generic).

    Science.gov (United States)

    2010-07-01

    ... nanoparticles (generic). 721.10120 Section 721.10120 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY... Specific Chemical Substances § 721.10120 Siloxane modified alumina nanoparticles (generic). (a) Chemical... as siloxane modified alumina nanoparticles (PMN P-05-687) is subject to reporting under this...

  7. Dynamic compressive and tensile strengths of spark plasma sintered alumina

    Science.gov (United States)

    Girlitsky, I.; Zaretsky, E.; Kalabukhov, S.; Dariel, M. P.; Frage, N.

    2014-06-01

    Fully dense submicron grain size alumina samples were manufactured from alumina nano-powder using Spark Plasma Sintering and tested in two kinds of VISAR-instrumented planar impact tests. In the first kind, samples were loaded by 1-mm tungsten impactors, accelerated to a velocity of about 1 km/s. These tests were aimed at studying the Hugoniot elastic limit (HEL) of Spark Plasma Sintering (SPS)-processed alumina and the decay, with propagation distance, of the elastic precursor wave. In the tests of the second kind, alumina samples of 3-mm thickness were loaded by 1-mm copper impactors accelerated to 100-1000 m/s. These tests were aimed at studying the dynamic tensile (spall) strength of the alumina specimens. The tensile fracture of the un-alloyed alumina shows a monotonic decline of the spall strength with the amplitude of the loading stress pulse. Analysis of the decay of the elastic precursor wave allowed determining the rate of the irreversible (inelastic) strains in the SPS-processed alumina at the initial stages of the shock-induced inelastic deformation and to clarify the mechanisms responsible for the deformation. The 1-% addition of Cr2O3 decreases the HEL of the SPS-processed alumina by 5-% and its spall strength by 50% but barely affects its static properties.

  8. Viral-templated Palladium Nanocatalysts

    Science.gov (United States)

    Yang, Cuixian

    Despite recent progress on nanocatalysis, there exist several critical challenges in simple and readily controllable nanocatalyst synthesis including the unpredictable particle growth, deactivation of catalytic activity, cumbersome catalyst recovery and lack of in-situ reaction monitoring. In this dissertation, two novel approaches are presented for the fabrication of viral-templated palladium (Pd) nanocatalysts, and their catalytic activities for dichromate reduction reaction and Suzuki Coupling reaction were thoroughly studied. In the first approach, viral template based bottom-up assembly is employed for the Pd nanocatalyst synthesis in a chip-based format. Specifically, genetically displayed cysteine residues on each coat protein of Tobacco Mosaic Virus (TMV) templates provide precisely spaced thiol functionalities for readily controllable surface assembly and enhanced formation of catalytically active Pd nanoparticles. Catalysts with the chip-based format allow for simple separation and in-situ monitoring of the reaction extent. Thorough examination of synthesis-structure-activity relationship of Pd nanoparticles formed on surface-assembled viral templates shows that Pd nanoparticle size, catalyst loading density and catalytic activity of viral-templated Pd nanocatalysts can be readily controlled simply by tuning the synthesis conditions. The viral-templated Pd nanocatalysts with optimized synthesis conditions are shown to have higher catalytic activity per unit Pd mass than the commercial Pd/C catalysts. Furthermore, tunable and selective surface assembly of TMV biotemplates is exploited to control the loading density and location of Pd nanocatalysts on solid substrates via preferential electroless deposition. In addition, the catalytic activities of surface-assembled TMV-templated Pd nanocatalysts were also investigated for the ligand-free Suzuki Coupling reaction under mild reaction conditions. The chip-based format enables simple catalyst separation and

  9. Nanowires and nanotubes from π-conjugated organic materials fabricated by template wetting

    DEFF Research Database (Denmark)

    Bordo, Kirill; Schiek, Manuela; Rubahn, Horst-Günter

    2014-01-01

    wetting of porous anodic alumina membranes by solutions and/or melts of the respective materials. Arrays of 1D nanostructures from the polymers PF8 and P3HT can be obtained by both solution- and melt-assisted template wetting. In the case of PF8, the morphology of the obtained nanostructures depends...... on the wetting conditions: for diluted PF8 solutions mostly nanotubes are obtained; while for concentrated PF8 solutions and PF8 melts, the formation of nanowires is dominating. Wetting of the template pores by P3HT solutions and melts leads to the formation of nanotubes. For the small-molecule material PTCDI-C8......, arrays of nanowires can only be obtained by melt-assisted wetting. Wetting of the template pores with PTCDI-C8 solutions does not allow the formation of pronounced 1D nanostructures. For all three materials, the diameters of the formed nanowires and nanotubes correspond to those of the template pores...

  10. DC electrodeposition of NiGa alloy nanowires in AAO template

    Energy Technology Data Exchange (ETDEWEB)

    Maleki, K. [Nanomaterials Group, Department of Materials Engineering, Tarbiat Modares University, Iran, P.O. Box: 14115-143, Tehran (Iran, Islamic Republic of); Sanjabi, S., E-mail: sanjabi@modares.ac.ir [Nanomaterials Group, Department of Materials Engineering, Tarbiat Modares University, Iran, P.O. Box: 14115-143, Tehran (Iran, Islamic Republic of); Alemipour, Z. [Department of Physics, University of Kurdistan, Sanandaj (Iran, Islamic Republic of)

    2015-12-01

    NiGa alloy nanowires were electrodeposited from an acidic sulfate bath into nanoporous anodized alumina oxide (AAO). This template was fabricated by two-step anodizing. The effects of bath composition and current density were explored on the Ga content of electrodeposited nanowires. The Ga content in the deposits was increased by increasing both Ga in the bath composition and electrodepositing current density. The NiGa alloy nanowires were synthesized for Ga content up to 2–4% without significant improving the magnetic properties. Above this threshold Ga clusters were formed and decreased the magnetic properties of the nanowires. For Ga content of the alloy above 30%, the wires were too short and incomplete. X-ray diffraction patterns reveal that the significant increase of Ga content in the nanowires, changes the FCC crystal structure of Ni to an amorphous phase. It also causes a sizeable increase in the Ga cluster size; these both lead to a significant reduction in the coercivity and the magnetization respectively. - Highlights: • NiGa alloy nanowires were electrodeposited from acidic sulphate baths into nanoporous anodized alumina oxide (AAO) template. • The Ga content was increased by increasing the Ga in the bath composition and electrodeposition current density. • The magnetic parameters such as coercivity and magnetization were not changed for the alloy nanowire with Ga content less than 4%.

  11. Sub-5 nm nanostructures fabricated by atomic layer deposition using a carbon nanotube template

    Science.gov (United States)

    Woo, Ju Yeon; Han, Hyo; Kim, Ji Weon; Lee, Seung-Mo; Ha, Jeong Sook; Shim, Joon Hyung; Han, Chang-Soo

    2016-07-01

    The fabrication of nanostructures having diameters of sub-5 nm is very a important issue for bottom-up nanofabrication of nanoscale devices. In this work, we report a highly controllable method to create sub-5 nm nano-trenches and nanowires by combining area-selective atomic layer deposition (ALD) with single-walled carbon nanotubes (SWNTs) as templates. Alumina nano-trenches having a depth of 2.6 ∼ 3.0 nm and SiO2 nano-trenches having a depth of 1.9 ∼ 2.2 nm fully guided by the SWNTs have been formed on SiO2/Si substrate. Through infilling ZnO material by ALD in alumina nano-trenches, well-defined ZnO nanowires having a thickness of 3.1 ∼ 3.3 nm have been fabricated. In order to improve the electrical properties of ZnO nanowires, as-fabricated ZnO nanowires by ALD were annealed at 350 °C in air for 60 min. As a result, we successfully demonstrated that as-synthesized ZnO nanowire using a specific template can be made for various high-density resistive components in the nanoelectronics industry.

  12. Thermal Conductivity of Alumina-reinforced Zirconia Composites

    Science.gov (United States)

    Bansal, Narottam P.

    2005-01-01

    10-mol% yttria-stabilized zirconia (10SZ) - alumina composites containing 0-30 mol% alumina were fabricated by hot pressing at 1500 C in vacuum. Thermal conductivity was determined at various temperatures using a steady-state laser heat flux technique. Thermal conductivity of the composites increased with increase in alumina content. Composites containing 0, 5, and 10-mol% alumina did not show any change in thermal conductivity with temperature. However, those containing 20 and 30-mol% alumina showed a decrease in thermal conductivity with increase in temperature. The measured values of thermal conductivity were in good agreement with those calculated from the Maxwell-Eucken model where one phase is uniformly dispersed within a second major continuous phase.

  13. Thermal shock behavior of rare earth modified alumina ceramic composites

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Junlong; Liu, Changxia [Ludong Univ., Yantai (China). School of Transportation

    2017-05-15

    Alumina matrix ceramic composites toughened by AlTiC master alloys, diopside and rare earths were fabricated by hot-pressing and their thermal shock behavior was investigated and compared with that of monolithic alumina. Results showed that the critical thermal shock temperature (ΔT) of monolithic alumina was 400 C. However, it decreased to 300 C for alumina incorporating only AlTiC master alloys, and increased with further addition of diopside and rare earths. Improvement of thermal shock resistance was obtained for alumina ceramic composites containing 9.5 wt.% AlTiC master alloys and 0.5 wt.% rare earth additions, which was mainly attributed to the formation of elongated grains in the composites.

  14. Comparison of deep desulfurization methods in alumina production process

    Institute of Scientific and Technical Information of China (English)

    刘战伟; 李旺兴; 马文会; 尹中林; 武国宝

    2015-01-01

    Several methods of deep desulfurization in alumina production process were studied, and the costs of these methods were compared. It is found that most of the S2− in sodium aluminate solution can be removed by adding sodium nitrate or hydrogen peroxide in digestion process, and in this way the effect of S2− on alumina product quality is eliminated. However, the removal efficiency of2-23SOin sodium aluminate solution is very low by this method. Both S2− and2-23SO in sodium aluminate solution can be removed completely by wet oxidation method in digestion process. The cost of desulfurization by wet oxidation is lower than by adding sodium nitrate or hydrogen peroxide. The results of this research reveal that wet oxidation is an economical and feasible method for the removal of sulfur in alumina production process to improve alumina quality, and provide valuable guidelines for alumina production by high-sulfur bauxite.

  15. Morphology and transmittance of porous alumina on glass substrate

    Energy Technology Data Exchange (ETDEWEB)

    Guo Peitao, E-mail: guopeitao@hotmail.com [Wuhan University of Technology. Wuhan (China); Xia Zhilin [Wuhan University of Technology. Wuhan (China); Key Laboratory of Low Dimensional Materials and Application Technology, Xiangtan University, Ministry of Education, Xiangtan (China); Xue Yiyu [Wuhan University of Technology. Wuhan (China); Huang Caihua [China Three Gorges University, Yichang (China); Zhao Lixin [Wuhan University of Technology. Wuhan (China)

    2011-02-01

    The porous optical film has higher threshold of laser-induced damage than densified films, for the study of mechanism of laser-induced damage of porous optical film with ordered pore structure. Porous anodic alumina (PAA) film with high transmittance on glass substrate has been prepared. Aluminum film was deposited on glass substrate by means of resistance and electron beam heat (EBH) evaporation. Porous alumina was prepared in oxalic acid solution under different anodizing conditions. At normal incidence, the optical transmittance spectrum over 300-1000 nm spectra region was obtained by spectrophotometer. SEM was introduced to analysis the morphology of the porous alumina film. The pore aperture increased with the increase of anodizing voltage, which resulted in a rapid decrease of the pore concentration and the optical thickness of porous alumina film. Damage morphology of porous alumina film is found to be typically defects initiated, and the defect is the pore presented on the film.

  16. Thermal Shock Behaviour of Alumina-Iron Composites

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    Thermal shock behaviour was investigated for two morphologically different composites comprising an alumina matrix and 20 vol. pct Fe particles for a wide range of quenching temperature differences (△T=100~800°C) and compared to a monolithic alumina. The retained strength and critical quenching temperature difference, △Tc, of the two composites were a significant improvement over the values for the respective monolithic alumina. Crack lengths and densities were shown to be greater for the alumina than for the two composites at all quenching temperature differences. The thermal shock resistance parameters for monolithic alumina and the two composites were calculated according to their mechanical and physical properties. The calculated results agree well with the experimental one and indicate possible explanations for the differences in thermal shock behaviour.

  17. National Wildlife Refuge System Survey Protocol Template

    Data.gov (United States)

    US Fish and Wildlife Service, Department of the Interior — This template was developed for drafting National Wildlife Refuge System (NWRS) Survey Protocols. The template is arranged in the same order as the eight basic...

  18. Web Template Extraction Based on Hyperlink Analysis

    Directory of Open Access Journals (Sweden)

    Julián Alarte

    2015-01-01

    Full Text Available Web templates are one of the main development resources for website engineers. Templates allow them to increase productivity by plugin content into already formatted and prepared pagelets. For the final user templates are also useful, because they provide uniformity and a common look and feel for all webpages. However, from the point of view of crawlers and indexers, templates are an important problem, because templates usually contain irrelevant information such as advertisements, menus, and banners. Processing and storing this information is likely to lead to a waste of resources (storage space, bandwidth, etc.. It has been measured that templates represent between 40% and 50% of data on the Web. Therefore, identifying templates is essential for indexing tasks. In this work we propose a novel method for automatic template extraction that is based on similarity analysis between the DOM trees of a collection of webpages that are detected using menus information. Our implementation and experiments demonstrate the usefulness of the technique.

  19. The synthesis of amino acids and sugars on an inorganic template from constituents of the prebiotic atmosphere

    Science.gov (United States)

    Field, B. O.; Spencer, J. E. D.

    1990-05-01

    Inelastic Electron Tunnelling Spectroscopy (IETS) has been used to identify the reaction products present on an alumina surface when it is exposed to likely components of the earth's prebiotic atmosphere. The alumina barrier of Al-AlO x -Pb tunnelling junctions have been exposed to water; aqueous ammonia; wet carbon monoxide gas and to aqueous formaldehyde vapour under normal atmospheric conditions at room temperature. The water spectrum shows strong coincidence with that of a genuine sample of formic acid. It is proposed that atmospheric CO2 is involved in this surface catalyzed reaction. The aqueous ammonia spectrum is assigned as an amino acid species produced from ammonia, water and atmospheric carbon dioxide. This spectrum compares very closely with the tunnelling spectrum of a genuine sample of glycine. The wet carbon monoxide spectrum and the aqueous formaldehyde spectrum have been produced by an infusion doping process. These spectra of CO and aqueous formaldehyde are assigned as a sugar like polymer or a sugar formed on the alumina surface. A tunnelling spectrum of D(-) fructose has been produced to aid this assignment. The role of an inorganic template such as alumina in the original prebiotic synthesis of amino acids and sugars is considered.

  20. Catalytic cleavage of lignin β-O-4 link mimics using copper on alumina and magnesia-alumina

    NARCIS (Netherlands)

    Strassberger, Z.; Alberts, A.H.; Louwerse, M.J.; Tanase, S.; Rothenberg, G.

    2013-01-01

    Copper on γ-alumina and on mixed magnesia-alumina, Cu/MgO-Al2O3, catalyse the hydrodeoxygenation (HDO) of β-O-4 lignin-type dimers, giving valuable aromatics. The typical selectivity to phenol is as high as 20%. By changing the support's acidity we can modify the dispersion of copper. Interestingly,

  1. Properties of Transition Metal Doped Alumina

    Science.gov (United States)

    Nykwest, Erik; Limmer, Krista; Brennan, Ray; Blair, Victoria; Ramprasad, Rampi

    Crystallographic texture can have profound effects on the properties of a material. One method of texturing is through the application of an external magnetic field during processing. While this method works with highly magnetic systems, doping is required to couple non-magnetic systems with the external field. Experiments have shown that low concentrations of rare earth (RE) dopants in alumina powders have enabled this kind of texturing. The magnetic properties of RE elements are directly related to their f orbital, which can have as many as 7 unpaired electrons. Since d-block elements can have as many as 5 unpaired electrons the effects of substitutional doping of 3d transition metals (TM) for Al in alpha (stable) and theta (metastable) alumina on the local structure and magnetic properties, in addition to the energetic cost, have been calculated by performing first-principles calculations based on density functional theory. This study has led to the development of general guidelines for the magnetic moment distribution at and around the dopant atom, and the dependence of this distribution on the dopant atom type and its coordination environment. It is anticipated that these findings can aid in the selection of suitable dopants help to guide parallel experimental efforts. This project was supported in part by an internship at the Army Research Laboratory, administered by the Oak Ridge Institute for Science and Education, along with a grant of computer time from the DoD High Performance Computing Modernization Program.

  2. Modified-starch Consolidation of Alumina Ceramics

    Institute of Scientific and Technical Information of China (English)

    JU Chenhui; WANG Yanmin; YE Jiandong; HUANG Yun

    2008-01-01

    The alumina ceramics with the homogeneous microstructure and the higher density were fabricated via the modified-starch consolidation process by 1.0 wt%of a modified starch as a consolidator/binder.The swelling behavior of the modified oxidized tapioca starch was analyzed by optical microscope,and two other corn starches(common corn starch and high amylose COrn starch)were also analyzed for comparison.The modified starch used as a binder for the consolidation swelled at about 55℃.began to gelatinize at 65℃ and then was completely gelatinized at 75℃.But the corn starches could not be completely gelatinized even at 80℃for 1 h.The high-strength green bodies(10.6 MPa)with the complex shapes were produced.The green bodies were sintered without any binder burnout procedure at 1700℃and a relative density of 95.3% was obtained for the sintered bodies,which is similar to that of the sintered sample formed by conventional slip casting.In addition,the effect of temperature on the apparent viscosity of the starch/alumina slurry in the process was investigated,and the corresponding mechanism for the starch consolidation was discussed.

  3. Parsing abnormal grain growth in specialty aluminas

    Science.gov (United States)

    Lawrence, Abigail Kremer

    Grain growth in alumina is strongly affected by the impurities present in the material. Certain impurity elements are known to have characteristic effects on abnormal grain growth in alumina. Specialty alumina powders contain multiple impurity species including MgO, CaO, SiO2, and Na 2O. In this work, sintered samples made from alumina powders containing various amounts of the impurities in question were characterized by their grain size and aspect ratio distributions. Multiple quantitative methods were used to characterize and classify samples with varying microstructures. The grain size distributions were used to partition the grain size population into subpopulations depending on the observed deviation from normal behavior. Using both grain size and aspect ratio a new visual representation for a microstructure was introduced called a morphology frequency map that gives a fingerprint for the material. The number of subpopulations within a sample and the shape of the distribution on the morphology map provided the basis for a classification scheme for different types of microstructures. Also using the two parameters a series of five metrics were calculated that describe the character of the abnormal grains in the sample, these were called abnormal character values. The abnormal character values describe the fraction of grains that are considered abnormal, the average magnitude of abnormality (including both grain size and aspect ratio), the average size, and variance in size. The final metric is the correlation between grain size and aspect ratio for the entire population of grains. The abnormal character values give a sense of how different from "normal" the sample is, given the assumption that a normal sample has a lognormal distribution of grain size and a Gaussian distribution of aspect ratios. In the second part of the work the quantified measures of abnormality were correlated with processing parameters such as composition and heat treatment conditions. A

  4. Template electrodeposition of catalytic nanomotors.

    Science.gov (United States)

    Wang, Joseph

    2013-01-01

    The combination of nanomaterials with electrode materials has opened new horizons in electroanalytical chemistry, and in electrochemistry in general. Over the past two decades we have witnessed an enormous activity aimed at designing new electrochemical devices based on nanoparticles, nanotubes or nanowires, and towards the use of electrochemical routes--particularly template-assisted electrodeposition--for preparing nanostructured materials. The power of template-assisted electrochemical synthesis is demonstrated in this article towards the preparation and the realization of self-propelled catalytic nanomotors, ranging from Pt-Au nanowire motors to polymer/Pt microtube engines. Design considerations affecting the propulsion behavior of such catalytic nanomotors are discussed along with recent bioanalytical and environmental applications. Despite recent major advances, artificial nanomotors have a low efficiency compared to their natural counterparts. Hopefully, the present Faraday Discussion will stimulate other electrochemistry teams to contribute to the fascinating area of artificial nanomachines.

  5. Growth Mechanism of γ-MnS Nanorod-Arrays by Hydrothermal Method on Anodic Aluminum Oxide Template

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Jianming; Liu, Weifeng; Lv, Yong; Yao, Lianzeng [Chinese Academy of Science, Hefei, Anhui (China)

    2010-09-15

    Hydrothermal method is a general, low-cost and convenience method which was utilized for synthesis of nanomaterials. Our research group has reported that oriented MnS nanorods on anodic aluminum oxide template were synthesized under a hydrothermal condition and demonstrated the effect of precursor content on the morphology evolution of as-samples. In order to research the growth mechanism of the arrays, herein we synthesized MnS nanorod arrays by combination of anodic aluminum oxide template and hydrothermal method on different substrates. Through-hole anodic aluminum oxide templates were prepared using Al foil (99.999%) via a two-step anodization process as described in literature. To investigate the effect of different substrates on the morphology of the-products, different substrates including anodic aluminum oxide template (sample A), one-step anodization Al foil (sample B, which was prepared by first anodizing Al foil for 10h and then removing the alumina layer with the mixed acid (0.6 M H{sub 3}PO{sub 4} and 0.15 M H{sub 2}CrO{sub 4}), where the foil still kept the close-packed concave nano-pits consistently with the nanopole of anodic aluminum oxide template), Al foil (sample C, dipped in HNO{sub 3} solution and covered by a compact alumina layer), Si wafer (sample D) respectively were put into Teflon-lined stainless steel autoclaves of 20 mL capacity filled with 16 mL mixed solution consisting of 2 mol/L MnCl{sub 4} and 2 mol/L thiourea. We kept the reaction at 150 .deg. C for 20 h. When reactions completed the products were washed three times with distilled water and absolute ethanol, respectively. Then the products were dried in an oven at 60 .deg. C.

  6. Fabrication of Alumina Nanowires from Porous Alumina Membranes by Etching in Phosphoric Acid Solution

    Science.gov (United States)

    Wang, Xuehua; Li, Chengyong; Ma, Lianjiao; Cao, Hong; Zhang, Baohua

    Alumina nanowires (ANWs) with high aspect ratios were synthesized by the chemical etching of porous alumina membranes (PAMs) in phosphoric acid solution. The morphology and structure of ANWs were analyzed by SEM and XRD, respectively. The results showed that the typical features of ANWs are around 35 nm in diameter and around 20 μm in length, the crystalline structure of the ANWs was amorphous, which was in accordance with that of the PAMs. Furthermore, the morphology of the PAMs was characterized by AFM and SEM in detail. On the basis of AFM and SEM observations, a possible formation mechanism of ANWs was discussed, and the inhomogeneous of the dissolution between the triple points and the side walls was considered to be the essential factor deciding the formation of ANWs.

  7. Terbium luminescence in alumina xerogel fabricated in porous anodic alumina matrix under various excitation conditions

    Energy Technology Data Exchange (ETDEWEB)

    Gaponenko, N. V., E-mail: nik@nano.bsuir.edu.by [Belarusian State University of Informatics and Radioelectronics (Belarus); Kortov, V. S. [Yeltsin Ural Federal University (Russian Federation); Orekhovskaya, T. I.; Nikolaenko, I. A. [Belarusian State University of Informatics and Radioelectronics (Belarus); Pustovarov, V. A.; Zvonarev, S. V.; Slesarev, A. I. [Yeltsin Ural Federal University (Russian Federation); Prislopski, S. Ya. [National Academy of Sciences of Belarus, Stepanov Institute of Physics (Belarus)

    2011-07-15

    Terbium-doped alumina xerogel layers are synthesized by the sol-gel method in pores of a porous anodic alumina film 1 {mu}m thick with a pore diameter of 150-180 nm; the film is grown on a silicon substrate. The fabricated structures exhibit terbium photoluminescence with bands typical of trivalent terbium terms. Terbium X-ray luminescence with the most intense band at 542 nm is observed for the first time for such a structure. Morphological analysis of the structure by scanning electron microscopy shows the presence of xerogel clusters in pore channels, while the main pore volume remains unfilled and pore mouths remain open. The data obtained confirm the promising applications of fabricated structures for developing matrix converters of X-rays and other ionizing radiations into visible light. The possibilities of increasing luminescence intensity in the matrix converter are discussed.

  8. Microstructural evolution of alumina-zirconia nanocomposites; Evolucao microestrutural de nanocompositos alumina-zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Ojaimi, C.L.; Chinelatto, A.S.A.; Chinelatto, A.L. [Universidade Estadual de Ponta Grossa (UEPG), PR (Brazil); Pallone, E.M.J.A., E-mail: christianelago@yahoo.com.br [Universidade de Sao Paulo (USP), Pirassununga, Sao Paulo, SP (Brazil). Faculdade de Zootecnia e Engenharia de Alimentos

    2012-07-01

    Ceramic materials have limited use due to their brittleness. The inclusion of nanosized particles in a ceramic matrix, which are called nanocomposites, and ceramic processing control by controlling the grain size and densification can aid in obtaining ceramic products of greater strength and toughness. Studies showed that the zirconia nano inclusions in the matrix of alumina favors an increase in mechanical properties by inhibiting the grain growth of the matrix and not by the mechanism of the transformation toughening phase of zirconia. In this work, the microstructural evolution of alumina nanocomposites containing 15% by volume of nanometric zirconia was studied. From the results it was possible to understand the sintering process of these nanocomposites. (author)

  9. LTL - The Little Template Library

    Science.gov (United States)

    Gössl, C. A.; Drory, N.; Snigula, J.

    2004-07-01

    The Little Template Library is an expression templates based C++ library for array processing, image processing, FITS and ASCII I/O, and linear algebra. It is released under the GNU Public License (GPL). Although the library is developed with application to astronomical image and data processing in mind, it is by no means restricted to these fields of application. In fact, it qualifies as a fully general array processing package. Focus is laid on a high abstraction level regarding the handling of expressions involving arrays or parts thereof and linear algebra related operations without the usually involved negative impact on performance. The price to pay is dependence on a compiler implementing enough of the current ANSI C++ specification, as well as significantly higher demand on resources at compile time. The LTL provides dynamic arrays of up to 5 dimensions, sub-arrays and slicing, support for fixed size vectors and matrices including basic linear algebra operations, expression templates based evaluation, and I/O facilities for columnar ASCII and FITS format files. In addition it supplies utility classes for statistics, linear and non-linear least squares fitting, and command line and configuration file parsing. YODA (Drory 2002) and all elements of the WeCAPP reduction pipeline (Riffeser et al. 2001, Gössl & Riffeser 2002, 2003) were implemented using the LTL.

  10. Deformation Behaviour of Coarse Grain Alumina under Shock Loading

    Science.gov (United States)

    Gupta, Satish

    2013-06-01

    To develop better understanding of the shock wave induced deformation behavior of coarse grain alumina ceramics, and for measurement of its Hugoniot Elastic Limit (HEL), in-situ and recovery gas gun experiments have been carried out on coarse grain alumina (grain size ~ 10 μm), prepared in the form of discs (>99.9% TMD) by pressure-less sintering of alpha alumina powder at 1583 K. The HEL value of 1.9 GPa has been determined from the kink in the pressure history recorded using piezoresistance gauge and also from the free surface velocity history of the sample shocked to 9 GPa. The nano-indentation measurements on the alumina samples shocked to 6.5 GPa showed hardness value 15% lower than 21.3 GPa for unshocked alumina, and strong Indentation Size Effect (ISE); the hardness value was still lower and the ISE was stronger for the sample shocked to 12 GPa. The XRD measurements showed reduced particle size and increased microstrains in the shocked alumina fragments. SEM, FESEM and TEM measurements on shock treated samples showed presence of grain localized micro- and nano-scale deformations, micro-cleavages, grain-boundary microcracks, extensive shear induced deformations, and localized micro-fractures, etc. These observations led to the development of a qualitative model for the damage initiation and its subsequent growth mechanisms in shocked alumina. The work performed in collaboration with K.D. Joshi of BARC and A.K. Mukhopadhyay of CGCRI.

  11. Dissolution kinetics for alumina in cryolite melts. Distribution of alumina in the electrolyte of industrial aluminium cells

    Energy Technology Data Exchange (ETDEWEB)

    Kobbeltvedt, Ove

    1997-12-31

    This thesis contributes to the understanding of which factors determine the rate of dissolution of alumina added to the bath in alumina reduction cells. Knowing this may help reduce the occurrences of operation interruptions and thus make it possible to produce aluminium using less energy. When alumina powder was added to a stirred cryolite melt, the alumina dissolved in two distinct main stages. In the first stage, the dissolution rate was very high, which reflects dissolution of single alumina grains that are being dispersed in the bath upon addition. In the second stage, lumps of alumina infiltrated with bath dissolved at a rate considerably slower than that of the first stage. The formation of these alumina agglomerates is the most important contributor to slow dissolution. The parameters varied in the experiments were convection, batch size, and temperature of the bath and of the added alumina. Increased gas stirring of the bath speeded up dissolution in both stages but the size of the batch was of little significance. Increasing the bath temperature had no effect in the first stage but speeded up dissolution considerably in the second stage. Compared to adding alumina at room temperature, preheating it to a high temperature (600 {sup o}C) increased the dissolution rate in the first stage while preheating to lower temperatures (100-300 {sup o}C) decreased the dissolution rate. In the second stage, preheating slowed the dissolution. The two latter phenomena of reduced dissolution rates are ascribed to the removal of moisture from the alumina upon preheating. The bath flow and the distribution of alumina in the bath were measured in four different types of cells. It was found that if a certain asymmetry of the magnetic field traverse to the cell was present, due to the presence of risers, then loops of high velocity bath flow occurred near the short ends of the cell. Thus, alumina added near the short ends is effectively transferred away from the feeding

  12. Testing sensory evidence against mnemonic templates.

    Science.gov (United States)

    Myers, Nicholas E; Rohenkohl, Gustavo; Wyart, Valentin; Woolrich, Mark W; Nobre, Anna C; Stokes, Mark G

    2015-01-01

    Most perceptual decisions require comparisons between current input and an internal template. Classic studies propose that templates are encoded in sustained activity of sensory neurons. However, stimulus encoding is itself dynamic, tracing a complex trajectory through activity space. Which part of this trajectory is pre-activated to reflect the template? Here we recorded magneto- and electroencephalography during a visual target-detection task, and used pattern analyses to decode template, stimulus, and decision-variable representation. Our findings ran counter to the dominant model of sustained pre-activation. Instead, template information emerged transiently around stimulus onset and quickly subsided. Cross-generalization between stimulus and template coding, indicating a shared neural representation, occurred only briefly. Our results are compatible with the proposal that template representation relies on a matched filter, transforming input into task-appropriate output. This proposal was consistent with a signed difference response at the perceptual decision stage, which can be explained by a simple neural model.

  13. Ballistic Performance of Alumina and Zirconia-toughened Alumina Against 7.62 Armour Piercing Projectile

    Directory of Open Access Journals (Sweden)

    S G. Savio

    2014-09-01

    Full Text Available A study was carried out to compare the ballistic performance of high purity alumina and zirconia-toughened alumina (ZTA using depth of penetration (DoP test configuration against 7.62 mm armour piercing (AP ammunition. The effect of tile thickness on the differential efficiency factor (DEF was studied for tile thickness in the range of 3 mm to 6 mm for alumina tiles and 3 mm to 5 mm for ZTA tiles. The DEF is found to increase as tile thickness increases. An analysis on the failed shots showed that the residual shot weight does not follow a single linear relationship with ceramic tile thickness unlike the residual DoP for all thicknesses of tiles. Post-ballistic analysis on ceramic powder for particle size distribution was carried out and the results are presented.Defence Science Journal, Vol. 64, No. 5, September 2014, pp.477-483, DOI:http://dx.doi.org/10.14429/dsj.64.6745

  14. Design and fabrication of alumina micro reciprocating engine

    Institute of Scientific and Technical Information of China (English)

    JIN Peng; GAO Yu-long; LIU Nan; JIANG Kylie

    2008-01-01

    Microengines are regarded as the potential replacements for batteries. Aimed at the unsatisfactory thermal property of silicon used in the combustion chambers, ceramics are chosen as the construction material in this paper. The fabrication process where alumina has been chosen as the microengine material is discussed. Vigorous FEA has been carried out, and it is found that the material satisfies the stress and deformation require-ments of the design. Then the alumina fabrication process is described. Soft reusable polydimethylsiloxane (PDMS) moulds are produced from SU-8 resist masters, and alumina microengine parts are produced using the PDMS moulds. Images of the ceramic components show that the fabrication satisfies the design requirements.

  15. Processing of silicon nitride and alumina nanosize powders

    Energy Technology Data Exchange (ETDEWEB)

    Gonzalez, E.J.; Piermarini, G.; Hockey, B.; Malghan, S.G. [National Inst. of Standard and Technology, Gaithersburg, MD (United States)

    1995-08-01

    The effects of pressure on the compaction and subsequent processing of nanosize {gamma} alumina powders were studied. A 3 mm diameter piston/cylinder die was used to compact the nanosize powders to pressures of 1 and 2.5 GPa. The green bodies were sintered at temperatures up to 1600{degrees}C. Results show that green body density can be increased by higher compaction pressures. It appears that as a result of the {gamma}-to-{alpha} transformation in alumina, higher green density does not necessarily produce a higher density sintered alumina body. The microstructures of the sintered bodies are described in terms of porosity and phase content.

  16. Alumina Paste Sublimation Suppression Barrier for Thermoelectric Device

    Science.gov (United States)

    Paik, Jong-Ah (Inventor); Caillat, Thierry (Inventor)

    2014-01-01

    Alumina as a sublimation suppression barrier for a Zintl thermoelectric material in a thermoelectric power generation device operating at high temperature, e.g. at or above 1000K, is disclosed. The Zintl thermoelectric material may comprise Yb.sub.14MnSb.sub.11. The alumina may be applied as an adhesive paste dried and cured on a substantially oxide free surface of the Zintl thermoelectric material and polished to a final thickness. The sublimation suppression barrier may be finalized by baking out the alumina layer on the Zintl thermoelectric material until it becomes substantially clogged with ytterbia.

  17. Special requirements for alumina ceramic of ESG electrode bowl

    Institute of Scientific and Technical Information of China (English)

    ZHANG Jun-an; XUE Kai; ZHANG Jia-tai; ZHANG Qiang

    2004-01-01

    At present ESG (Electrostatic Suspended Gyro) is the most precise inertia element in the world. The electrode bowl, which has direct effect on the precision of ESG, is a key part to ESG. Through the analysis of the function and characteristic of the electrode bowl in hollow rotor ESG and the present situation of new material development in the world, the alumina ceramic is regarded as the best material for the electrode bowl of hollow rotor ESG. By analyzing the present situation of alumina ceramic in the world, main technique requirements have been put forward for the alumina ceramic of ESG electrode bowl which is also fit for solid rotor ESG.

  18. Wenshan’s 800,000-ton Alumina Project Completed

    Institute of Scientific and Technical Information of China (English)

    2012-01-01

    <正>On September 26,2012,the completion ceremony of the 800,000-ton alumina project was held at the alumina factory in Matang Industrial Park, Wenshan city,Yunnan.Wenshan’s 800,000-ton alumina project and its supporting mining construction projects have been listed as one of 20 major industrial construction projects of Yunnan. The project covers an area of approximately 5,500 mu,with an estimated total investment of RMB 4,987 million. It is invested and built

  19. Porous Alumina Based Capacitive MEMS RH Sensor

    CERN Document Server

    Juhasz, L; Timar-Horvath, Veronika; Desmulliez, Marc; Dhariwal, Resh

    2008-01-01

    The aim of a joint research and development project at the BME and HWU is to produce a cheap, reliable, low-power and CMOS-MEMS process compatible capacitive type relative humidity (RH) sensor that can be incorporated into a state-of-the-art, wireless sensor network. In this paper we discuss the preparation of our new capacitive structure based on post-CMOS MEMS processes and the methods which were used to characterize the thin film porous alumina sensing layer. The average sensitivity is approx. 15 pF/RH% which is more than a magnitude higher than the values found in the literature. The sensor is equipped with integrated resistive heating, which can be used for maintenance to reduce drift, or for keeping the sensing layer at elevated temperature, as an alternative method for temperature-dependence cancellation.

  20. Aluminum matrix composites reinforced with alumina nanoparticles

    CERN Document Server

    Casati, Riccardo

    2016-01-01

    This book describes the latest efforts to develop aluminum nanocomposites with enhanced damping and mechanical properties and good workability. The nanocomposites exhibited high strength, improved damping behavior and good ductility, making them suitable for use as wires. Since the production of metal matrix nanocomposites by conventional melting processes is considered extremely problematic (because of the poor wettability of the nanoparticles), different powder metallurgy routes were investigated, including high-energy ball milling and unconventional compaction methods. Special attention was paid to the structural characterization at the micro- and nanoscale, as uniform nanoparticle dispersion in metal matrix is of prime importance. The aluminum nanocomposites displayed an ultrafine microstructure reinforced with alumina nanoparticles produced in situ or added ex situ. The physical, mechanical and functional characteristics of the materials produced were evaluated using different mechanical tests and micros...

  1. Electrochemical modification process of anodic alumina membrane

    Institute of Scientific and Technical Information of China (English)

    YU Mei; LIU Jian-hua; LI Song-mei

    2006-01-01

    The modification procedure of anodic alumina membrane(AAM) was studied. The AAM structure after modification was characterized by nickel nanowires prepared in AAM. Scanning electron microscopy was used to characterize the topography and structure properties of the AAM and nickel nanowires. The transformation of the current during the voltage reduction was studied. The mechanism of current and structure change during modification was discussed. The results show that a root structure produces after the AAM modification. The length of the root structure depends on the velocity of the voltage reduction. Slow voltage reduction leads to a large length of the root structure,otherwise,a short length of the root structure. At the end of the modification,the barrier layer is thin enough to be passed by electrons. Hence,the direct electrodeposition of one-dimensional nanowires can be carried out on the AAM with barrier layer and aluminum matrix successfully without any other treatments.

  2. Crystallography of Alumina-YAG-Eutectic

    Science.gov (United States)

    Farmer, Serene C.; Sayir, Ali; Dickerson, Robert M.; Matson, Lawrence E.

    2000-01-01

    Multiple descriptions of the alumina-YAG eutectic crystallography appear in the ceramic literature. The orientation between two phases in a eutectic system has direct impact on residual stress, morphology, microstructural stability, and high temperature mechanical properties. A study to demonstrate that the different crystallographic relationships can be correlated with different growth constraints was undertaken. Fibers produced by Laser-Heated Float Zone (LHFZ) and Edge-defined Film-fed Growth (EFG) were examined. A map of the orientation relationship between Al2O3 and Y3Al5O12 and their relationship to the fiber growth axis as a function of pull rate are presented. Regions in which a single orientation predominates are identified.

  3. Fracture simulation for zirconia toughened alumina microstructure

    CERN Document Server

    Kim, Kyungmok; Forest, Bernard

    2013-01-01

    Purpose - The purpose of this paper is to describe finite element modelling for fracture and fatigue behaviour of zirconia toughened alumina microstructures. Design/methodology/approach - A two-dimensional finite element model is developed with an actual $Al{_2}O{_3}$ - 10 vol% $ZrO{_2}$ microstructure. A bilinear, time-independent cohesive zone law is implemented for describing fracture behaviour of grain boundaries. Simulation conditions are similar to those found at contact between a head and a cup of hip prosthesis. Residual stresses arisen from the mismatch of thermal coefficient between grains are determined. Then, effects of a micro-void and contact stress magnitude are investigated with models containing residual stresses. For the purpose of simulating fatigue behaviour, cyclic loadings are applied to the models. Findings - Results show that crack density is gradually increased with increasing magnitude of contact stress or number of fatigue cycles. It is also identified that a micro-void brings about...

  4. Characterization of Glasses in One Type of Alumina Rich Fly Ash by Chemical Digestion Methods: Implications for Alumina Extraction

    Directory of Open Access Journals (Sweden)

    Lijun Zhao

    2016-01-01

    Full Text Available In recent years, one type of alumina rich fly ash (ARFA with about 50 wt% of alumina has been extensively investigated for alumina extraction in China. Due to the silica in ARFA, alumina extraction would have to generate a huge amount of solid waste. There is a growing interest in the glasses in ARFA, because they are composed mainly of silica and could be removed prior to alumina extraction. In this work, the glasses in ARFA have been investigated by chemical methods, that is, acid and base digestions. The chemical compositions have been measured by XRF for ARFA from the digestion processes. The K2O standard, XRD, and FTIR spectroscopies were successfully used to define the digestions processes, and size analysis and SEM-EDX provided rich information on particle transformations. As a result, acid and base digestion methods were found to produce very similar results for the glasses in ARFA. The K2O standard was attributed to the formation of glasses by illites, and TiO2 and Fe2O3 were proposed to originate from ilmenite in alumina rich coals (ARC. Some implications of the results were also discussed for the alumina extraction from ARFA.

  5. Fabrication of a Ni nano-imprint stamp for an anti-reflective layer using an anodic aluminum oxide template.

    Science.gov (United States)

    Park, Eun-Mi; Lim, Seung-Kyu; Ra, Senug-Hyun; Suh, Su-Jung

    2013-11-01

    Aluminum anodizing can alter pore diameter, density distribution, periodicity and layer thickness in a controlled way. Because of this property, porous type anodic aluminum oxide (AAO) was used as a template for nano-structure fabrication. The alumina layer generated at a constant voltage increased the pore size from 120 nm to 205 nm according to an increasing process time from 60 min to 150 min. The resulting fabricated AAO templates had pore diameters at or less than 200 nm. Ni was sputtered as a conductive layer onto this AAO template and electroplated using DC and pulse power. Comparing these Ni stamps, those generated from electroplating using on/reverse/off pulsing had an ordered pillar array and maintained the AAO template morphology. This stamp was used for nano-imprinting on UV curable resin coated glass wafer. Surface observations via electron microscopy showed that the nano-imprinted patterned had the same shape as the AAO template. A soft mold was subsequently fabricated and nano-imprinted to form a moth-eye structure on the glass wafer. An analysis of the substrate transmittance using UV-VIS/NIR spectroscopy showed that the transmittance of the substrate with the moth-eye structure was 5% greater that the non-patterned substrate.

  6. Template fabrication of highly ordered arrays of organic semiconductor nanowires

    Energy Technology Data Exchange (ETDEWEB)

    Heckel, Christian; Ostendorp, Stefan; Lei, Yong; Wilde, Gerhard [Institut fuer Materialphysik, Muenster (Germany)

    2011-07-01

    Porous alumina membrane (PAM) is a widely used template for the fabrication of highly ordered arrays of one-dimensional (1D) nanostructures. The structural parameters of the PAMs are adjustable, including the pore diameter and spacing, and the thickness of the membranes. And thus the structures of the 1D nanomaterials prepared using PAMs can be controlled. On the other hand, the investigation of organic semiconductors opens a new field of applications in computer technology like twistable displays or printing integrated circuits. In the current work, these two technologies are combined by depositing organic n-type semiconductors into the pores of PAMs using different synthesizing processes such as molecular evaporation and solution-phase self-assembly. As a result, highly ordered arrays of organic semiconducting wires are obtained within the pores with a diameter of about 50 nm, which indicates that it is possible to fill the pores with organic materials.The properties of these ''filled'' membranes are characterized by measuring the electrical properties of several nanowires pooled together and also of single nanowires by AFM-based methods.

  7. High Alumina Refractory Mortars GB/T 2994-2008

    Institute of Scientific and Technical Information of China (English)

    Wang Jing; Chai Junlan

    2009-01-01

    @@ 1 Scope This standard specifies the classification, techni-cal requirements, test methods, quality appraisal pro-cedure, packing, marking, transportation, storage and quality certificate of high alumina refractory mortars.

  8. Direct spray pyrolysis of aluminum chloride solution for alumina preparation

    Institute of Scientific and Technical Information of China (English)

    吕国志; 张廷安; 王龙; 马思达; 豆志河; 刘燕

    2014-01-01

    The effects of pyrolysis mode and pyrolysis parameters on Cl content in alumina were investigated, and the alumina products were characterized by XRD, SEM and ASAP. The experimental results indicate that the spray pyrolysis efficiency is higher than that of static pyrolysis process, and the reaction and evaporation process lead to a multi-plot state of the alumina products by spray pyrolysis. Aluminum phase starts to transform intoγ-Al2O3 at spray pyrolysis temperature of 600 °C, which is about 200 °C lower than that of static pyrolysis process. The primary particle size of γ-Al2O3 product is 27.62 nm, and Cl content in alumina products is 0.38%at 800 °C for 20 min.

  9. Fused Cast Alumina Refractory Products for Glass Tank Furnace

    Institute of Scientific and Technical Information of China (English)

    SHEN Keyin

    2006-01-01

    @@ 1 Subject and Scope The standard specifies the requirement, testing method, inspection rule and requirements for the labeling, packing, shipping and storing of the fused cast alumina refractory products for glass tanks.

  10. Aluminum microstructures on anodic alumina for aluminum wiring boards.

    Science.gov (United States)

    Jha, Himendra; Kikuchi, Tatsuya; Sakairi, Masatoshi; Takahashi, Hideaki

    2010-03-01

    The paper demonstrates simple methods for the fabrication of aluminum microstructures on the anodic oxide film of aluminum. The aluminum sheets were first engraved (patterned) either by laser beam or by embossing to form deep grooves on the surface. One side of the sheet was then anodized, blocking the other side by using polymer mask to form the anodic alumina. Because of the lower thickness at the bottom part of the grooves, the part was completely anodized before the complete oxidation of the other parts. Such selectively complete anodizing resulted in the patterns of metallic aluminum on anodic alumina. Using the technique, we fabricated microstructures such as line patterns and a simple wiring circuit-board-like structure on the anodic alumina. The aluminum microstructures fabricated by the techniques were embedded in anodic alumina/aluminum sheet, and this technique is promising for applications in electronic packaging and devices.

  11. High Alumina Refractory Bricks for Electric Arc Furnace Roofs

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    @@ 1 Scope This standard specifies the sort, technical requirement, test method, inspection rules, marking, packing, transportation, storage and quality certification of high alumina refractory bricks for electric arc furnace roofs.

  12. Superhydrophobic alumina surface based on stearic acid modification

    Energy Technology Data Exchange (ETDEWEB)

    Feng Libang, E-mail: lepond@hotmail.com [School of Mechatronic Engineering, Lanzhou Jiaotong University, Lanzhou 730070 (China); Zhang Hongxia; Mao Pengzhi; Wang Yanping; Ge Yang [School of Mechatronic Engineering, Lanzhou Jiaotong University, Lanzhou 730070 (China)

    2011-02-15

    A novel superhydrophobic alumina surface is fabricated by grafting stearic acid layer onto the porous and roughened aluminum film. The chemical and phase structure, morphology, and the chemical state of the atoms at the superhydrophobic surface were investigated by techniques as FTIR, XRD, FE-SEM, and XPS, respectively. Results show that a super water-repellent surface with a contact angle of 154.2{sup o} is generated. The superhydrophobic alumina surface takes on an uneven flowerlike structure with many nanometer-scale hollows distribute in the nipple-shaped protrusions, and which is composed of boehmite crystal and {gamma}-Al{sub 2}O{sub 3}. Furthermore, the roughened and porous alumina surface is coated with a layer of hydrophobic alkyl chains which come from stearic acid molecules. Therefore, both the roughened structure and the hydrophobic layer endue the alumina surface with the superhydrophobic behavior.

  13. Synthesis of beta alumina from aluminum hydroxide and oxyhydroxide precursors

    CSIR Research Space (South Africa)

    Van Zyl, A

    1993-02-01

    Full Text Available Two aluminium oxyhydroxides, boehmite and pseudoboehmite, and two aluminium hydroxides, bayerite and gibbsite, have been investigated as precursors for the synthesis of the solid electrolyte, beta alumina. Reaction pathways and products have been...

  14. I - Template Metaprogramming for Massively Parallel Scientific Computing - Expression Templates

    CERN Document Server

    CERN. Geneva

    2016-01-01

    Large scale scientific computing raises questions on different levels ranging from the fomulation of the problems to the choice of the best algorithms and their implementation for a specific platform. There are similarities in these different topics that can be exploited by modern-style C++ template metaprogramming techniques to produce readable, maintainable and generic code. Traditional low-level code tend to be fast but platform-dependent, and it obfuscates the meaning of the algorithm. On the other hand, object-oriented approach is nice to read, but may come with an inherent performance penalty. These lectures aim to present he basics of the Expression Template (ET) idiom which allows us to keep the object-oriented approach without sacrificing performance. We will in particular show to to enhance ET to include SIMD vectorization. We will then introduce techniques for abstracting iteration, and introduce thread-level parallelism for use in heavy data-centric loads. We will show to to apply these methods i...

  15. A template for design personas

    DEFF Research Database (Denmark)

    Nielsen, Lene; Storgaard Nielsen, Kira; Stage, Jan

    2015-01-01

    The persona method is gaining widespread use and support. Many researchers have reported from single cases and from novel domains on how they have used the method. However, the way companies and design groups describe personas has not been the focus of attention. This paper analyses 47 descriptions...... from 13 companies and compares these to an analysis of recommendations from 11 templates from literature. Furthermore, 28 interviews with Danish practitioners with experience in using personas are analyzed for content on persona descriptions. The study finds that a Danish persona style has developed...

  16. Templated growth of graphenic materials

    Energy Technology Data Exchange (ETDEWEB)

    Nicholas, Nolan W; Connors, L Matthew [Department of Physics, Rice University, 6100 Main, Houston, TX (United States); Ding, Feng [Institute of Textile and Clothing, Hong Kong Polytechnic University, Kowloon (Hong Kong); Yakobson, Boris I [Department of Mechanical Engineering and Materials Science, Rice University, 6100 Main, Houston, TX (United States); Schmidt, Howard K; Hauge, Robert H [Richard E Smalley Institute for Nanoscale Science and Technology, Rice University, 6100 Main, Houston, TX (United States)], E-mail: nolan.nicholas@matricresearch.com

    2009-06-17

    A novel strategy is proposed for the topologically controlled synthesis of extended graphenic sheets by additively reacting carbon into a pre-existing graphene sheet which is on top of a templating substrate. This concept is implemented and demonstrated using chemical vapor deposition (CVD). Novel morphological features observed in this study suggest unusual aspects of the CVD growth process. CVD results demonstrate the basic soundness of the synthesis strategy but highlight the sensitivity of the process to certain types of disruption and the need for alternative forms of embodiment.

  17. Recent advances in silica-alumina refractory: A review

    Directory of Open Access Journals (Sweden)

    Chaouki Sadik

    2014-06-01

    Full Text Available In this article, the elaboration and the characterization of silica-alumina refractory have been reviewed. Refractory oxides encompass a broad range of unary, binary, and ternary ceramic compounds that can be used in structural, insulating, and other applications. This paper provides a historical perspective on the elaboration and the use of silica-alumina refractory, reviews applications for refractory oxides, describes typical processing routes, overviews fundamental structure–property relations, and summarizes the properties of these materials.

  18. Electronic Structure of High-Pressure Alumina Polymorphs

    Institute of Scientific and Technical Information of China (English)

    LIU Xiao-Lei; DUAN Wen-Hui; GU Bing-Lin

    2000-01-01

    Electronic properties are investigated for three alumina polymorphs (corundum, Rb2 O3 (Ⅱ) and Pbnm perovskite),which are predicted as the stable structures under different pressure range, by means of the first-principles molecular dynamics method within local density functional framework. The similarity in electronic properties of the polymorphs of alumina is observed. The effect of possible phase transitions on ruby (Cr+3-doped Al2 O3)fluorescences is discussed.

  19. CSL grain boundary distribution in alumina and zirconia ceramics

    OpenAIRE

    Vonlanthen, Pierre; Grobéty, Bernard

    2008-01-01

    The distributions of general and coincidence site lattice (CSL) grain boundaries (GBs) in texture-free alumina and zirconia ceramics sintered at two different temperatures were investigated based on electron backscatter diffraction (EBSD) measurements. Results were compared with the distributions obtained from random 2D spatial models and with calculated random distributions reported in the literature. All alumina samples independent on sintering temperature show the same characteristic devia...

  20. Hard template synthesis of metal nanowires

    Directory of Open Access Journals (Sweden)

    Go eKawamura

    2014-11-01

    Full Text Available Metal nanowires (NWs have attracted much attention because of their high electron conductivity, optical transmittance and tunable magnetic properties. Metal NWs have been synthesized using soft templates such as surface stabilizing molecules and polymers, and hard templates such as anodic aluminum oxide, mesoporous oxide, carbon nanotubes. NWs prepared from hard templates are composites of metals and the oxide/carbon matrix. Thus, selecting appropriate elements can simplify the production of composite devices. The resulting NWs are immobilized and spatially arranged, as dictated by the ordered porous structure of the template. This avoids the NWs from aggregating, which is common for NWs prepared with soft templates in solution. Herein, the hard template synthesis of metal NWs is reviewed, and the resulting structures, properties and potential applications are discussed.

  1. Preparation of spherical hollow alumina particles by thermal plasma

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Wonkyung [Department of Chemical Engineering, INHA University, 253 Yonghyun-dong, Nam-gu, Incheon 402‐751 (Korea, Republic of); Regional Innovation Center for Environmental Technology of Thermal Plasma (RIC-ETTP), INHA University, 253 Yonghyun-dong, Nam-gu, Incheon 402‐751 (Korea, Republic of); Choi, Sooseok [Center for Advance Research in Fusion Reactor Engineering, Seoul National University, 599 Gwanak-ro, Gwanak-gu, Seoul 151‐742 (Korea, Republic of); Oh, Seung-Min [Daejoo Electronic Materials Co., 1236‐10 Jeongwang-dong, Siheung-si, Kyunggi-do 429‐848 (Korea, Republic of); Park, Dong-Wha, E-mail: dwpark@inha.ac.kr [Department of Chemical Engineering, INHA University, 253 Yonghyun-dong, Nam-gu, Incheon 402‐751 (Korea, Republic of); Regional Innovation Center for Environmental Technology of Thermal Plasma (RIC-ETTP), INHA University, 253 Yonghyun-dong, Nam-gu, Incheon 402‐751 (Korea, Republic of)

    2013-02-01

    Spherical hollow particles were prepared from solid alumina powders using DC arc thermal plasma, and then spray coating was performed with the as-prepared particles. Operating variables for the hollow particle preparation process were additional plasma gas, input power, and carrier gas flow rate. The spherical hollow alumina particles were produced in the case of using additive gas of H{sub 2} or N{sub 2}, while alumina surface was hardly molten in the pure argon thermal plasma. In addition, the hollow particles were well produced in high power and low carrier gas conditions due to high melting point of alumina. Hollow structure was confirmed by focused ion beam-scanning electron microscopy analysis. Morphology and size distribution of the prepared particles that were examined by field emission-scanning electron microscopy and phase composition of the particles was characterized by X-ray diffraction. In the spray coating process, the as-prepared hollow particles showed higher deposition rate. - Highlights: ► Spherical hollow alumina powder was prepared by non-transferred DC arc plasma. ► Diatomic gasses were added in Ar plasma for high power. ► Prepared hollow alumina powder was efficient for the plasma spray coating.

  2. Antibacterial activity of zinc oxide-coated nanoporous alumina

    Energy Technology Data Exchange (ETDEWEB)

    Skoog, S.A. [Joint Department of Biomedical Engineering, University of North Carolina and North Carolina State University, Box 7115, Raleigh, NC 27695-7115 (United States); Bayati, M.R. [Department of Materials Science and Engineering, North Carolina State University, Box 7907, Raleigh, NC 27695-7907 (United States); Petrochenko, P.E. [Joint Department of Biomedical Engineering, University of North Carolina and North Carolina State University, Box 7115, Raleigh, NC 27695-7115 (United States); Division of Biology, Office of Science and Engineering Laboratories, Center for Devices and Radiological Health, U.S. Food and Drug Administration, Silver Spring, MD 20993 (United States); Stafslien, S.; Daniels, J.; Cilz, N. [Center for Nanoscale Science and Engineering, North Dakota State University, 1805 Research Park Drive, Fargo, ND 58102 (United States); Comstock, D.J.; Elam, J.W. [Energy Systems Division, Argonne National Laboratory, Argonne, IL 60439 (United States); Narayan, R.J., E-mail: roger_narayan@msn.com [Joint Department of Biomedical Engineering, University of North Carolina and North Carolina State University, Box 7115, Raleigh, NC 27695-7115 (United States); Department of Materials Science and Engineering, North Carolina State University, Box 7907, Raleigh, NC 27695-7907 (United States)

    2012-07-25

    Highlights: Black-Right-Pointing-Pointer Atomic layer deposition was used to deposit ZnO on nanoporous alumina membranes. Black-Right-Pointing-Pointer Scanning electron microscopy showed continuous coatings of zinc oxide nanocrystals. Black-Right-Pointing-Pointer Activity against B. subtilis, E. coli, S. aureus, and S. epidermidis was shown. - Abstract: Nanoporous alumina membranes, also known as anodized aluminum oxide membranes, are being investigated for use in treatment of burn injuries and other skin wounds. In this study, atomic layer deposition was used for coating the surfaces of nanoporous alumina membranes with zinc oxide. Agar diffusion assays were used to show activity of zinc oxide-coated nanoporous alumina membranes against several bacteria found on the skin surface, including Bacillus subtilis, Escherichia coli, Staphylococcus aureus, and Staphylococcus epidermidis. On the other hand, zinc oxide-coated nanoporous alumina membranes did not show activity against Pseudomonas aeruginosa, Enterococcus faecalis, and Candida albicans. These results suggest that zinc oxide-coated nanoporous alumina membranes have activity against some Gram-positive and Gram-negative bacteria that are associated with skin colonization and skin infection.

  3. Adsorption of itaconic acid from aqueous solutions onto alumina

    Directory of Open Access Journals (Sweden)

    JELENA J. GULICOVSKI

    2008-08-01

    Full Text Available Itaconic acid, IA (C5H6O4, was investigated as a potential flocculant for the aqueous processing of alumina powders. The adsorption of IA, as a function of its concentration and pH value of the solution, onto the alumina surface was studied by the solution depletion method. The stability of the suspensions in the presence of itaconic acid was evaluated in light of the surface charge of the alumina powder used, the degree of dissociation of IA, as well as the sedimentation behavior and rheology of the suspensions. It was found that the adsorption process is extremely pH dependent; the maximum adsorption of IA onto alumina surface occurring at a pH close to the value of the first IA dissociation constant, pKa1. Also, IA does not influence the value of the point of zero charge of alumina. It was shown that IA represents an efficient flocculant for concentrated acidic alumina suspensions.

  4. Procoagulant behavior and platelet microparticle generation on nanoporous alumina.

    Science.gov (United States)

    Ferraz, Natalia; Hong, Jaan; Karlsson Ott, Marjam

    2010-05-01

    In the present work, we have investigated platelet microparticle (PMP) generation in whole blood after contact with nanoporous alumina. Alumina membranes with pore sizes of 20 and 200 nm in diameter were incubated with whole blood and the number of PMP in the fluid phase was determined by flow cytometry. The role of the complement system in PMP generation was investigated using an analog of the potent complement inhibitor compstatin. Moreover, the procoagulant activity of the two pore size membranes were compared by measuring thrombin formation. Results indicated that PMP were not present in the fluid phase after whole blood contact with either of the alumina membranes. However, scanning electron microscope micrographs clearly showed the presence of PMP clusters on the 200 nm pore size alumina, while PMP were practically absent on the 20 nm membrane. We probed no influence of complement activation in PMP generation and adhesion and we hypothesize that other specific material-related protein-platelet interactions are taking place. A clear difference in procoagulant activity between the membranes could also be seen, 20 nm alumina showed 100% higher procoagulant activity than 200 nm membrane. By combining surface evaluation and flow cytometry analyses of the fluid phase, we are able to conclude that 200 nm pore size alumina promotes PMP generation and adhesion while the 20 nm membrane does not appreciably cause any release or adhesion of PMP, thus indicating a direct connection between PMP generation and nanoporosity.

  5. Alumina Concentration Detection Based on the Kernel Extreme Learning Machine.

    Science.gov (United States)

    Zhang, Sen; Zhang, Tao; Yin, Yixin; Xiao, Wendong

    2017-09-01

    The concentration of alumina in the electrolyte is of great significance during the production of aluminum. The amount of the alumina concentration may lead to unbalanced material distribution and low production efficiency and affect the stability of the aluminum reduction cell and current efficiency. The existing methods cannot meet the needs for online measurement because industrial aluminum electrolysis has the characteristics of high temperature, strong magnetic field, coupled parameters, and high nonlinearity. Currently, there are no sensors or equipment that can detect the alumina concentration on line. Most companies acquire the alumina concentration from the electrolyte samples which are analyzed through an X-ray fluorescence spectrometer. To solve the problem, the paper proposes a soft sensing model based on a kernel extreme learning machine algorithm that takes the kernel function into the extreme learning machine. K-fold cross validation is used to estimate the generalization error. The proposed soft sensing algorithm can detect alumina concentration by the electrical signals such as voltages and currents of the anode rods. The predicted results show that the proposed approach can give more accurate estimations of alumina concentration with faster learning speed compared with the other methods such as the basic ELM, BP, and SVM.

  6. Porous alumina and zirconia ceramics with tailored thermal conductivity

    Science.gov (United States)

    Gregorová, E.; Pabst, W.; Sofer, Z.; Jankovský, O.; Matějíček, J.

    2012-11-01

    The thermal conductivity of porous ceramics can be tailored by slip casting and uniaxial dry pressing, using either fugitive pore formers (saccharides) or partial sintering. Porous alumina and zirconia ceramics have been prepared using appropriate powder types (ungranulated for casting, granulated for pressing) and identical firing regimes (but different maximum temperatures in the case of partial sintering). Thermal diffusivities have been measured by the laser- and xenon-flash method and transformed into relative thermal conductivities, which enable a temperature-independent comparison between different materials. While the porosity can be controlled in a similar way for both materials when using pore formers, partial sintering exhibits characteristic differences between alumina and zirconia (for alumina porosities below 45 %, full density above 1600 °C, for zirconia porosities below 60 %, full density above 1300 °C). The different compaction behavior of alumina and zirconia (porosity after pressing 0.465 and 0.597, respectively) is reflected in the fact that for alumina the relative conductivity data of partially sintered materials are below the exponential prediction, while for zirconia they coincide with the latter. Notwithstanding these characteristic differences, for both alumina and zirconia it is possible to tailor the thermal conductivity from 100 % down to approx. 15 % of the solid phase value.

  7. Dynamic yield and tensile strengths of spark plasma sintered alumina

    Science.gov (United States)

    Girlitsky, I.; Zaretsky, E.; Kalabukhov, S.; Dariel, M.; Frage, N.

    2014-05-01

    Fully dense alumina samples with 0.6 μm grain size were produced from alumina powder using Spark Plasma Sintering and tested in two types of VISAR-instrumented planar impact tests. In the tests of the first type the samples of 0.28 to 6-mm thickness were loaded by 1-mm tungsten impactors accelerated up to a velocity of about 1 km/s. These tests were aimed to study the Hugoniot elastic limit (HEL) of the SPS-processed alumina and the decay of the elastic precursor wave with propagation distance. In the second type of test the samples of ~3-mm thickness were loaded by 1-mm copper impactors accelerated up to velocities 100-1000 m/s. These tests were aimed to study the dynamic tensile (spall) strength of the alumina. The data on tensile fracture of the alumina demonstrate a monotonic decline of the spall strength with the amplitude of the loading stress pulse. The data on the decay of the elastic precursor wave allows for determining the rates of the irreversible (inelastic) strains in the SPS-processed alumina at the initial stages of shock-induced inelastic deformation and, thus, to derive some conclusions concerning the mechanisms responsible of the deformation.

  8. Influence of additives on the stability of the phases of alumina; Influencia de aditivos na estabilidade das fases da alumina

    Energy Technology Data Exchange (ETDEWEB)

    Rosario, D.C.C.; Gouvea, D., E-mail: deisedorosario@usp.br [Universidade de Sao Paulo (USP), SP (Brazil). Departamento de Engenharia Metalurgica e de Materiais. Laboratorio de Processos Ceramicos

    2011-07-01

    Problems with the stability of gamma alumina in catalytic reactions have been solved with the inclusion of additives during the synthesis of alumina. These additives stabilize the temperature of phase transition allowing the use of metastable alumina at high temperatures, but the mechanisms of action of additives are not well defined. It is known that each family of additive or additives behaves in different ways for this stabilization. This work aimed to study the performance of MgO and ZrO{sub 2}, respectively at different concentrations in alumina synthesized via Pechini. The samples were analyzed by DSC, X-ray diffraction, measurement of specific surface area by BET analysis, and infrared analysis. The results showed an increase in transition temperature for both additives, and a different changes for specific surface area, showing that MgO and ZrO{sub 2} work on improving the stability but with distinct mechanisms. (author)

  9. High-throughput templated multisegment synthesis of gold nanowires and nanorods.

    Science.gov (United States)

    Burdick, Jared; Alonas, Eric; Huang, Huang-Chiao; Rege, Kaushal; Wang, Joseph

    2009-02-11

    A cost-effective, high-throughput method for generating gold nanowires and/or nanorods based on a multisegment template electrodeposition approach is described. Using this method, multiple nanowires/nanorods can be generated from a single pore of alumina template membranes by alternately depositing segments of desirable (e.g., gold) and non-desirable metals (e.g., silver), followed by dissolution of the template and the non-desirable metal. Critical cost analysis indicates substantial savings in material requirements, processing times, and processing costs compared to the commonly used single-segment method. In addition to solid gold nanowires/nanorods, high yields of porous gold nanowires/nanorods are obtained by depositing alternate segments of gold-silver alloy and silver from the same gold-silver plating solution followed by selective dissolution of the silver from both segments. It is anticipated that this high-throughput method for synthesizing solid and porous gold nanowires and nanorods will accelerate their use in sensing, electronic, and biomedical applications.

  10. Influence of template fill in graphoepitaxy DSA

    Science.gov (United States)

    Doise, Jan; Bekaert, Joost; Chan, Boon Teik; Hong, SungEun; Lin, Guanyang; Gronheid, Roel

    2016-03-01

    Directed self-assembly (DSA) of block copolymers (BCP) is considered a promising patterning approach for the 7 nm node and beyond. Specifically, a grapho-epitaxy process using a cylindrical phase BCP may offer an efficient solution for patterning randomly distributed contact holes with sub-resolution pitches, such as found in via and cut mask levels. In any grapho-epitaxy process, the pattern density impacts the template fill (local BCP thickness inside the template) and may cause defects due to respectively over- or underfilling of the template. In order to tackle this issue thoroughly, the parameters that determine template fill and the influence of template fill on the resulting pattern should be investigated. In this work, using three process flow variations (with different template surface energy), template fill is experimentally characterized as a function of pattern density and film thickness. The impact of these parameters on template fill is highly dependent on the process flow, and thus pre-pattern surface energy. Template fill has a considerable effect on the pattern transfer of the DSA contact holes into the underlying layer. Higher fill levels give rise to smaller contact holes and worse critical dimension uniformity. These results are important towards DSA-aware design and show that fill is a crucial parameter in grapho-epitaxy DSA.

  11. Effect of alumina composition and surface integrity in alumina/epoxy composites on the ultrasonic attenuation properties.

    Science.gov (United States)

    Cho, Eikhyun; Park, Gwanwoo; Lee, Jae-Wan; Cho, Sung-Min; Kim, Taekyung; Kim, Joongeok; Choi, Wonjoon; Ohm, Won-Suk; Kang, Shinill

    2016-03-01

    We report a method of fabricating backing blocks for ultrasonic imaging transducers, using alumina/epoxy composites. Backing blocks contain scatterers such as alumina particles interspersed in the epoxy matrix for the effective scattering and attenuation of ultrasound. Here, the surface integrity can be an issue, where the composite material may be damaged during machining because of differences in strength, hardness and brittleness of the hard alumina particles and the soft epoxy matrix. Poor surface integrity results in the formation of air cavities between the backing block and the piezoelectric element upon assembly, hence the increased reflection off the backing block and the eventual degradation in image quality. Furthermore, with an issue of poor surface integrity due to machining, it is difficult to increase alumina as scatterers more than a specific mass fraction ratio. In this study, we increased the portion of alumina within epoxy matrix by obtaining an enhanced surface integrity using a net shape fabrication method, and verified that this method could allow us to achieve higher ultrasonic attenuation. Backing blocks were net-shaped with various mass fractions of alumina to characterize the formability and the mechanical properties, including hardness, surface roughness and the internal micro-structure, which were compared with those of machined backing blocks. The ultrasonic attenuation property of the backing blocks was also measured.

  12. Comparison between the standard SPM2 template and Korean-standard template in FDG-PET

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jung Hee; Lee, Byeong Il; Song, Ho Chun; Min, Jung Joon; Bom, Hee Seung [Chonnam National University Hospital, Gwangju (Korea, Republic of); Lee, Jae Sung [Seoul National University Hospital, Seoul (Korea, Republic of)

    2005-07-01

    The preprocessing step of statistical parametric mapping (SPM) requires the procedure of spatial normalization that consists of applying the nonlinear deformations needed to force every particular PET scan to match a reference template. The purpose of this study is to asses the statistic influence of using 2 different templates (the standard SPM2-PET template and Korean-standard PET template) in the normalization. We compared the regional metabolic patterns on 18F-FDG (fluorodeoxyglucose) images obtained from 4 patients with Alzheimers disease (AD) and 16 normal subjects. The statistical outcome of between- group comparison was analyzed with SPM2 and was applied into two levels of thresholds (an uncorrected P value of P <0.001, a corrected P value of P < 0.05). As a result, the most significant hypometabolic region was commonly found in the left temporal gyrus regardless of template type or thresholds. However, inconsistent results including different extent and the t-score statistics representing metabolic changes could be also observed between two templates. While the standard SPM2 template showed hypometabolic regions corresponding to Brodman area (BA) 7 and 9, Korean-standard template was not observed these regions. In addition, hypometabolic regions corresponding to BA 38 and 46 indicated not the standard SPM2 template but Korean-standard template. Statistic result showed that the standard SPM2 template effectively reflects the dorsal region of the brain while Korean-standard template is more sensitive to the medial region of the brain.

  13. Cast alumina forming austenitic stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Muralidharan, Govindarajan; Yamamoto, Yukinori; Brady, Michael P

    2013-04-30

    An austenitic stainless steel alloy consisting essentially of, in terms of weight percent ranges 0.15-0.5C; 8-37Ni; 10-25Cr; 2.5-5Al; greater than 0.6, up to 2.5 total of at least one element selected from the group consisting of Nb and Ta; up to 3Mo; up to 3Co; up to 1W; up to 3Cu; up to 15Mn; up to 2Si; up to 0.15B; up to 0.05P; up to 1 total of at least one element selected from the group consisting of Y, La, Ce, Hf, and Zr; <0.3Ti+V; <0.03N; and, balance Fe, where the weight percent Fe is greater than the weight percent Ni, and wherein the alloy forms an external continuous scale comprising alumina, and a stable essentially single phase FCC austenitic matrix microstructure, the austenitic matrix being essentially delta-ferrite free and essentially BCC-phase-free. A method of making austenitic stainless steel alloys is also disclosed.

  14. Nanoparticle assisted coagulation of aqueous alumina suspensions

    Directory of Open Access Journals (Sweden)

    Abdullah Fatih Çetinel

    2012-02-01

    Full Text Available Colloidal processing of ceramics offers a high potential to achieve homogeneous microstructures with improved material properties. In this study, a novel forming method is investigated, which was already applied successfully for the fabrication of ceramic matrix composites (CMC, but is also considered to be a suitable direct casting technique for the fabrication of advanced ceramics with tailored microstructure and properties. The so-called nanoparticle assisted coagulation method (NPAC represents a modification of the hydrolysis-assisted solidification (HAS technique. It promises green components with high green strength, uniform density as well as homogeneous and tailored microstructure. Electrostatically stabilized colloidal suspensions with high solid loadings were produced by dispersing various fractions of submicron alumina powder and aluminium hydroxide nano-powder in water without use of any organic binder. Rheology and coagulation kinetics of suspensions and green part properties were studied regarding to modifications of pH value, setting temperature, amount of setting agent, amount of nano-powder, solids loading and process parameters like ultrasound treatment. It could be revealed that the homogeneous core-shell arrangement of submicron and nanoparticles in the colloidal state can be transmitted to the green state, which improves the microstructure and green density of the green parts. For this, the NPAC method is seen as a promising technique for the fabrication of advanced ceramics with tailored microstructure and properties.

  15. Mechanical properties of alumina porcelain during heating

    Science.gov (United States)

    Šín, Peter; Podoba, Rudolf; ŠtubÅa, Igor; Trník, Anton

    2014-11-01

    The mechanical strength and Young's modulus of green alumina porcelain (50 wt. % of kaolin, 25 wt. % of Al2O3, and 25 wt. % of feldspar) were measured during heating up to 900 °C and 1100 °C, respectively. To this end, we used the three point-bending method and modulated force thermomechanical analysis (mf-TMA). The loss liberation - of the physically bound water (20 - 250 °C) strengthens the sample and Young's modulus increases its values significantly. The dehydroxylation that takes place in the range of 400 - 650 °C causes a slight decrease in Young's modulus. On the other hand, the mechanical strength slightly increases in this temperature range, although it has a sudden drop at 420 °C. Beyond the dehydroxylation range, above 650 °C, both Young's modulus and mechanical strength increase. Above 950 °C, a sharp increase of Young's modulus is caused by the solid-state sintering and the new structure created by the high-temperature reactions in metakaolinite.

  16. Preparation of thin hexagonal highly-ordered anodic aluminum oxide (AAO) template onto silicon substrate and growth ZnO nanorod arrays by electrodeposition

    Science.gov (United States)

    Chahrour, Khaled M.; Ahmed, Naser M.; Hashim, M. R.; Elfadill, Nezar G.; Qaeed, M. A.; Bououdina, M.

    2014-12-01

    In this study, anodic aluminum oxide (AAO) templates of Aluminum thin films onto Ti-coated silicon substrates were prepared for growth of nanostructure materials. Hexagonally highly ordered thin AAO templates were fabricated under controllable conditions by using a two-step anodization. The obtained thin AAO templates were approximately 70 nm in pore diameter and 250 nm in length with 110 nm interpore distances within an area of 3 cm2. The difference between first and second anodization was investigated in details by in situ monitoring of current-time curve. A bottom barrier layer of the AAO templates was removed during dropping the voltage in the last period of the anodization process followed by a wet etching using phosphoric acid (5 wt%) for several minutes at ambient temperature. As an application, Zn nanorod arrays embedded in anodic alumina (AAO) template were fabricated by electrodeposition. Oxygen was used to oxidize the electrodeposited Zn nanorods in the AAO template at 700 °C. The morphology, structure and photoluminescence properties of ZnO/AAO assembly were analyzed using Field-emission scanning electron microscope (FESEM), Energy dispersive X-ray spectroscopy (EDX), Atomic force microscope (AFM), X-ray diffraction (XRD) and photoluminescence (PL).

  17. Templates for integrated nanofiber growth

    DEFF Research Database (Denmark)

    Oliveira Hansen, Roana Melina de

    Para-hexaphenylene (p6P) molecules have the ability to self-assemble into organic nanofibers. These nanofibers hold unique optoelectronic properties, which make them interesting candidates as elements in electronic and optoelectronic devices. Typically these nanofibers are grown on specific single......, high-volume integration. Besides such single-crystalline templates, the nanofibers can also be grown on non-crystalline gold surfaces, on which the orientation of the nanofibers can be manipulated by structuring the gold surface prior to p6P deposition. In this work, a novel method for in-situ growth...... of p6P nanofibers on nano-structured gold surfaces is presented. The substrates are prepared by conventional nanofabrication techniques such as e-beam lithography and metal deposition, which increase their potential as device platforms. Some of the results presented here demonstrate, that both...

  18. Testing by C++ template metaprograms

    CERN Document Server

    Pataki, Norbert

    2010-01-01

    Testing is one of the most indispensable tasks in software engineering. The role of testing in software development has grown significantly because testing is able to reveal defects in the code in an early stage of development. Many unit test frameworks compatible with C/C++ code exist, but a standard one is missing. Unfortunately, many unsolved problems can be mentioned with the existing methods, for example usually external tools are necessary for testing C++ programs. In this paper we present a new approach for testing C++ programs. Our solution is based on C++ template metaprogramming facilities, so it can work with the standard-compliant compilers. The metaprogramming approach ensures that the overhead of testing is minimal at runtime. This approach also supports that the specification language can be customized among other advantages. Nevertheless, the only necessary tool is the compiler itself.

  19. A Template for Design Personas:

    DEFF Research Database (Denmark)

    Nielsen, Lene; Hansen, Kira Storgaard; Stage, Jan;

    2015-01-01

    The persona method is gaining widespread use and support. Many researchers have reported from single cases and from novel domains on how they have used the method. However, the way companies and design groups describe personas has not been the focus of attention. This paper analyses 47 descriptions...... from 13 companies and compares these to an analysis of recommendations from 11 templates from literature. Furthermore, 28 interviews with Danish practitioners with experience in using personas are analyzed for content on persona descriptions. The study finds that a Danish persona style has developed...... that is different from the recommendations in the lack of marketing and business related information and the absence of goals as differentiator for personas. Furthermore, the inspiration and knowledge on personas originates from co-workers and seminars and not much from literature. This indicates that the community...

  20. Alumina-on-alumina total hip replacement for femoral neck fracture in healthy patients

    Directory of Open Access Journals (Sweden)

    Moretti Lorenzo

    2011-02-01

    Full Text Available Abstract Background Total hip replacement is considered the best option for treatment of displaced intracapsular fractures of the femoral neck (FFN. The size of the femoral head is an important factor that influences the outcome of a total hip arthroplasty (THA: implants with a 28 mm femoral head are more prone to dislocate than implants with a 32 mm head. Obviously, a large head coupled to a polyethylene inlay can lead to more wear, osteolysis and failure of the implant. Ceramic induces less friction and minimal wear even with larger heads. Methods A total of 35 THAs were performed for displaced intracapsular FFN, using a 32 mm alumina-alumina coupling. Results At a mean follow-up of 80 months, 33 have been clinically and radiologically reviewed. None of the implants needed revision for any reason, none of the cups were considered to have failed, no dislocations nor breakage of the ceramic components were recorded. One anatomic cementless stem was radiologically loose. Conclusions On the basis of our experience, we suggest that ceramic-on-ceramic coupling offers minimal friction and wear even with large heads.

  1. Template synthesis of ordered macroporous hydroxyapatite bioceramics.

    Science.gov (United States)

    Ji, Lijun; Jell, Gavin; Dong, Yixiang; Jones, Julian R; Stevens, Molly M

    2011-08-28

    Hydroxyapatite has found wide application in bone tissue engineering. Here we use a macroporous carbon template to generate highly ordered macroporous hydroxyapatite bioceramics composed of close-packed hollow spherical pores with interconnected channels. The template has advantages for the preparation of ordered materials.

  2. Screening for templates that promote crystallization

    NARCIS (Netherlands)

    Urbanus, J.; Roelands, C.P.M.; Horst, J.H. ter; Verdoes, D.; Jansens, P.J.

    2008-01-01

    In Situ Product Recovery (ISPR) applied in fermentation processes leads to improved yield and productivity of these processes. In principle, ISPR can be achieved using Template Induced Crystallization (TIC), which is one possible ISPR technique. With TIC, templates are added to the solution as a spe

  3. Indexing Images: Testing an Image Description Template.

    Science.gov (United States)

    Jorgensen, Corinne

    1996-01-01

    A template for pictorial image description to be used by novice image searchers in recording their descriptions of images was tested; image attribute classes derived in previous research were used to model the template. Results indicated that users may need training and/or more guidance to correctly assign descriptors to higher-level classes.…

  4. Template Assembly for Detailed Urban Reconstruction

    KAUST Repository

    Nan, Liangliang

    2015-05-04

    We propose a new framework to reconstruct building details by automatically assembling 3D templates on coarse textured building models. In a preprocessing step, we generate an initial coarse model to approximate a point cloud computed using Structure from Motion and Multi View Stereo, and we model a set of 3D templates of facade details. Next, we optimize the initial coarse model to enforce consistency between geometry and appearance (texture images). Then, building details are reconstructed by assembling templates on the textured faces of the coarse model. The 3D templates are automatically chosen and located by our optimization-based template assembly algorithm that balances image matching and structural regularity. In the results, we demonstrate how our framework can enrich the details of coarse models using various data sets.

  5. Solvable model for template coexistence in protocells

    CERN Document Server

    Fontanari, J F

    2012-01-01

    Compartmentalization of self-replicating molecules (templates) in protocells is a necessary step towards the evolution of modern cells. However, coexistence between distinct template types inside a protocell can be achieved only if there is a selective pressure favoring protocells with a mixed template composition. Here we study analytically a group selection model for the coexistence between two template types using the diffusion approximation of population genetics. The model combines competition at the template and protocell levels as well as genetic drift inside protocells. At the steady state, we find a continuous phase transition separating the coexistence and segregation regimes, with the order parameter vanishing linearly with the distance to the critical point. In addition, we derive explicit analytical expressions for the critical steady-state probability density of protocell compositions.

  6. Solvable model for template coexistence in protocells

    Science.gov (United States)

    Fontanari, J. F.; Serva, M.

    2013-02-01

    Compartmentalization of self-replicating molecules (templates) in protocells is a necessary step towards the evolution of modern cells. However, coexistence between distinct template types inside a protocell can be achieved only if there is a selective pressure favoring protocells with a mixed template composition. Here we study analytically a group selection model for the coexistence between two template types using the diffusion approximation of population genetics. The model combines competition at the template and protocell levels as well as genetic drift inside protocells. At the steady state, we find a continuous phase transition separating the coexistence and segregation regimes, with the order parameter vanishing linearly with the distance to the critical point. In addition, we derive explicit analytical expressions for the critical steady-state probability density of protocell compositions.

  7. The mechanical reliability of alumina scales and coatings

    Energy Technology Data Exchange (ETDEWEB)

    Alexander, K.B.; Pruebner, K.; Tortorelli, P.F. [Oak Ridge National Lab., TN (United States)

    1996-08-01

    The mechanical integrity of oxide scales ultimately determines their ability to protect materials from corrosion and other environmental effects arising from deleterious reactions with gases and condensable products. The microstructure and mechanical behavior of alumina products thermally grown or deposited on Fe-28 at.% Al intermetallic alloys are being characterized in order to develop the knowledge and means to control the mechanical reliability of alumina scales by microstructural manipulation through design and processing. Mechanical characterization involved gravimetric data from cyclic oxidation experiments, in-situ observation of oxidized specimens undergoing flexural loading in a scanning electron microscope, and measurements of hardness, elastic modulus and cracking resistance by nanoindentation. Values of cracking thresholds for Al{sub 2}O{sub 3} scales were consistent with other measurements for surface and bulk alumina. The oxidation behavior of Fe{sub 3}Al alloys coated with a thin (0.5 - 1 {mu}m) alumina film deposited by plasma synthesis has been studied. During exposure in the oxidizing environment, new oxide was formed between the coating and the substrate. The presence of the deposited amorphous oxide inhibited the subsequent thermal oxidation of the metal. Because the thermally grown alumina forms under the deposit, the adherence of the coating is controlled by the strength of the metal/oxide interface that develops during oxidation.

  8. Plasma Processes : Plasma sprayed alumina coatings for radiation detector development

    Indian Academy of Sciences (India)

    Mary Alex; V Balagi; K R Prasad; K P Sreekumar; P V Ananthapadmanabhan

    2000-11-01

    Conventional design of radiation detectors uses sintered ceramic insulating modules. The major drawback of these ceramic components is their inherent brittleness. Ion chambers, in which these ceramic spacers are replaced by metallic components with plasma spray coated alumina, have been developed in our Research Centre. These components act as thin spacers that have good mechanical strength as well as high electrical insulation and replace alumina insulators with the same dimensions. As a result, the design of the beam loss monitor ion chamber for CAT could be simplified by coating the outer surface of the HT electrode with alumina. One of the chambers developed for isotope calibrator for brachytherapy gamma sources has its outer aluminium electrode (60 mm dia × 220 mm long) coated with 250 thick alumina (97%) + titania (3%). In view of potential applications in neutron-sensitive ion chambers used in reactor control instrumentation, studies were carried out on alumina 100 to 500 thick coatings on copper, aluminium and SS components. The electrical insulation varied from 108 ohms to 1012 ohms for coating thicknesses above 200 . The porosity in the coating resulted in some fall in electrical insulation due to moisture absorption. An improvement could be achieved by providing the ceramic surface with moisture-repellent silicone oil coating. Irradiation at Apsara reactor core location showed that the coating on aluminium was found to be unaffected after exposure to 1017 nvt fluence.

  9. Template Assisted Growth of Zinc Oxide-Based Nanowires by Electrochemical Deposition

    Directory of Open Access Journals (Sweden)

    T. Singh

    2011-01-01

    Full Text Available Ordered ZnO and Zn1 – xCdxO nanowire/nanorod arrays were fabricated by cathodic electrodeposition based on anodic alumina (AAO membrane and polycarbonate membrane (PCM from an aqueous solution containing zinc nitrate precursor at different bath temperatures. The electrodeposition process involves the electroreduction of nitrate ions to alter the local pH within the pores and precipitation of the metal oxide within the pores. X-Ray diffraction measurements showed that the nanowires/nanorods were of wurtzite crystallographic structures and the average length and diameter of nanorods were measured by SEM and TEM. HRTEM measurements confirm the crystallinity and elemental composition of grown nanowires on PCM/AAO templates.

  10. Si nanopillar arrays with nanocrystals produced by template-induced growth at room temperature

    Science.gov (United States)

    Bai, An-Qi; Zheng, Jun; Tao, Ye-Liao; Zuo, Yu-Hua; Xue, Chun-Lai; Cheng, Bu-Wen; Wang, Qi-Ming

    2011-11-01

    Well-aligned and closely-packed silicon nanopillar (SNP) arrays are fabricated by using a simple method with magnetron sputtering of Si on a porous anodic alumina (PAA) template at room temperature. The SNPs are formed by selective growth on the top of the PAA pore walls. The growth mechanism analysis indicates that the structure of the SNPs can be modulated by the pore spacing of the PAA and the sputtering process and is independent of the wall width of the PAA. Moreover, nanocrystals are identified by using transmission electron microscopy in the as-deposited SNP samples, which are related to the heat isolation structure of the SNPs. The Raman focus depth profile reveals a high crystallization ratio on the surface.

  11. Peltier heats in cryolite melts with alumina

    Energy Technology Data Exchange (ETDEWEB)

    Flem, B.E.; Ratkje, S.K.; Sterten, A. [Univ. of Trondheim (Norway)

    1996-10-01

    The Seebeck coefficient was measured for cells with electrolytes of molten mixtures of sodium fluoride and aluminum fluoride saturated with alumina. The electrodes were either a pair of oxygen electrodes or a pair of aluminum electrodes. For the molar ratio NaF/AlF{sub 3} equal to 1.8, 1.2 and 1.0, the authors obtained the Seebeck coefficients {minus}1.80 mV K{sup {minus}1} at 971 C, {minus}1.63 mV K{sup {minus}1} at 813.6 C and {minus}0.583 mV K{sup {minus}1} at 758 C, respectively, for the oxygen electrodes. For the aluminum electrodes, the authors obtained the Seebeck coefficient {minus}1.23 mV K{sup {minus}1} at 962 C, for the molar ratio NaF/AlF{sub 3} equal to 1.8. The results suggest that there is a substantial reversible heat consumption at the anode during aluminum electrolysis and a large reversible heat production at the cathode. The highest temperature in the Hall-Heroult cell is then closer to the cathode than the anode. The transported entropies of Al{sup 3+} and O{sup 2{minus}} were calculated to be 77 J mol{sup {minus}1} K{sup {minus}1} and 10 J mol{sup {minus}1} K{sup {minus}1}, respectively, when the molar ratio NaF/AlF{sub 3} was equal to 1.0.

  12. Challenges in Additive Manufacturing of Alumina

    Science.gov (United States)

    Gonzalez, Hugo

    Additive manufacturing is seen by many as the holy grail of manufacturing, the ability to produce parts nearly autonomously. Adding material rather than removing it would eliminate the need for expensive resources and machining. The recent expiration of key 3D printing patents has led to many advances in the field and has dramatically lowered the prices of 3D printers, making them accessible to the average individual. The one area where additive manufacturing is still in its infancy is in ceramics. Ceramic materials have advantages over polymers and metals such as corrosion resistance, insulating behavior, high stiffness and high temperature stability that make them attractive in industries such as aerospace, medical, and electronics. Processing and machining ceramics however is difficult and expensive as it requires high temperature furnaces and diamond tooling. There are currently two companies that produce printers capable of printing technical ceramics, Lithoz in Germany and 3D Ceram in France. The issue is that both of these printers retail for over $100,000. The work in this thesis intends to show the challenges associated with setting up a ceramic 3D printer at a fraction of that cost for 3D printing of alumina. The first such challenge was creating a photopolymer resin that could be loaded with a large volume percent of aluminum oxide powder while maintain its curability and low viscosity. Several combinations of monomers and dispersants were evaluated before coming to the conclusion that the use of a hexanediol diacrylate monomer and quarternary ammonia acetate were the most effective in suspending volume sold loadings of over 40% while maintaining a low viscosity. The next challenge was adapting an inexpensive polymer printer to use the powder loaded resin. Various printer parameters were modified and different window coatings were implemented to create a print. The issue of the layers curing on the build area window however, proved to be difficult to

  13. Fabrication and optical properties of platinum nanowire arrays on anodic aluminium oxide templates

    Institute of Scientific and Technical Information of China (English)

    高铁仁; 陈子瑜; 彭勇; 李发伸

    2002-01-01

    Arrays of Pt nanowires, fabricated by electrodepositing Pt metal into nanoporous anodic aluminium oxide (AAO)templates, exhibit a preferable optical absorption band in the ultraviolet-visible (UV-VIS) spectra and present a blueshift as the wire aspect ratio increases or its radius decreases. This type of optical property of Pt nanowire/porous alumina composites has been theoretically explored using Maxwell-Garnett (MG) effective medium theory. The MG theory,however, is only applicable to nanowires with an infinitesimally small radius relative to the wavelength of an incident light. The nanowire radius is controlled by the pore radius of the host alumina, which depends on anodizing conditions such as the selected electrolyte, anodizing time, temperature and voltage. The nanowire aspect ratios depend on the amount of Pt deposited into the nanopores of AAO films. The optical absorption properties of the arrays of Pt nanowires with diameters of 24, 55 and 90nm have been investigated by the UV-VIS spectra, which show that the extinction maximum (λmax) shifts to shorter wavelength side as the wire aspect ratio increases or its radius decreases.The results are qualitatively consistent with those calculated based on the MG theory.

  14. Template-mediated synthesis and bio-functionalization of flexible lignin-based nanotubes and nanowires

    Science.gov (United States)

    Caicedo, Hector M.; Dempere, Luisa A.; Vermerris, Wilfred

    2012-03-01

    Limitations of cylindrical carbon nanotubes based on the buckminsterfullerene structure as delivery vehicles for therapeutic agents include their chemical inertness, sharp edges and toxicological concerns. As an alternative, we have developed lignin-based nanotubes synthesized in a sacrificial template of commercially available alumina membranes. Lignin is a complex phenolic plant cell wall polymer that is generated as a waste product from paper mills and biorefineries that process lignocellulosic biomass into fuels and chemicals. We covalently linked isolated lignin to the inner walls of activated alumina membranes and then added layers of dehydrogenation polymer onto this base layer via a peroxidase-catalyzed reaction. By using phenolic monomers displaying different reactivities, we were able to change the thickness of the polymer layer deposited within the pores, resulting in the synthesis of nanotubes with a wall thickness of approximately 15 nm or nanowires with a nominal diameter of 200 nm. These novel nanotubes are flexible and can be bio-functionalized easily and specifically, as shown by in vitro assays with biotin and Concanavalin A. Together with their intrinsic optical properties, which can also be varied as a function of their chemical composition, these lignin-based nanotubes are expected to enable a variety of new applications including as delivery systems that can be easily localized and imaged after uptake by living cells.

  15. Fabrication of alumina films with laminated structures by ac anodization

    Directory of Open Access Journals (Sweden)

    Hiroyo Segawa

    2014-01-01

    Full Text Available Anodization techniques by alternating current (ac are introduced in this review. By using ac anodization, laminated alumina films are fabricated. Different types of alumina films consisting of 50–200 nm layers were obtained by varying both the ac power supply and the electrolyte. The total film thickness increased with an increase in the total charge transferred. The thickness of the individual layers increased with the ac voltage; however, the anodization time had little effect on the film thickness. The laminated alumina films resembled the nacre structure of shells, and the different morphologies exhibited by bivalves and spiral shells could be replicated by controlling the rate of increase of the applied potentials.

  16. Origin of High-Alumina Basalt, Andesite, and Dacite Magmas.

    Science.gov (United States)

    Hamilton, W

    1964-10-30

    The typical volcanic rocks of most island arcs and eugeosynclines, and of some continental environments, are basalt, andesite, and dacite, of high alumina content. The high-alumina basalt differs from tholeiitic basalt primarily in having a greater content of the components of calcic plagioclase. Laboratory data indicate that in the upper mantle, below the level at which the basaltic component of mantle rock is transformed by pressure to eclogite or pyroxenite, the entire basaltic portion probably is melted within a narrow temperature range, but that above the level of that transformation plagioclase is melted selectively before pyroxene over a wide temperature range. The broad spectrum of high-alumina magmas may represent widely varying degrees of partial melting above the transformation level, whereas narrow-spectrum tholeiite magma may represent more complete melting beneath it.

  17. Pressureless sintering behavior of injection molded alumina ceramics

    Directory of Open Access Journals (Sweden)

    Liu W.

    2014-01-01

    Full Text Available The pressureless sintering behaviors of two widely used submicron alumina (MgOdoped and undoped with different solid loadings produced by injection molding have been studied systematically. Regardless of the sinterability of different powders depending on their inherent properties, solid loading plays a critical role on the sintering behavior of injection molded alumina, which greatly determines the densification and grain size, and leads to its full densification at low temperatures. As compared to the MgO-doped alumina powder, the undoped specimens exhibit a higher sinterability for its smaller particle size and larger surface area. While full densification could be achieved for MgO-doped powders with only a lower solid loading, due to the fact that MgO addition can reduce the detrimental effect of the large pore space on the pore-boundary separation.

  18. Thermal and Electrical Characterization of Alumina Substrate for Microelectronic Applications

    Science.gov (United States)

    Ahmad, S.; Ibrahim, A.; Alias, R.; Shapee, S. M.; Ambak, Z.; Zakaria, S. Z.; Yahya, M. R.; Mat, A. F. A.

    2010-03-01

    This paper reports the effect of sintering temperature on thermal and electrical properties of alumina material as substrate for microelectronic devices. Alumina materials in the form of green sheet with 1 mm thickness were sintered at 1100° C, 1300° C and 1500° C for about 20 hours using heating and cooling rates of 2° C/min. The densities were measured using densitometer and the microstructures of the samples were analyzed using SEM micrographs. Meanwhile thermal and electrical properties of the samples were measured using flash method and impedance analyzer respectively. It was found that thermal conductivity and thermal diffusivity of the substrate increases as sintering temperature increases. It was found also that the dielectric constant of alumina substrate increases as the sintering temperature increases.

  19. Porous Alumina as a Promising Biomaterial for Public Health.

    Science.gov (United States)

    Bragazzi, Nicola Luigi; Gasparini, Roberto; Amicizia, Daniela; Panatto, Donatella; Larosa, Claudio

    2015-01-01

    Porous aluminum is a nanostructured material characterized by unique properties, such as chemical stability, regular uniformity, dense hexagonal porous lattice with high aspect ratio nanopores, excellent mechanical strength, and biocompatibility. This overview examines how the structure and properties of porous alumina can be exploited in the field of public health. Porous alumina can be employed for fabricating membranes and filters for bioremediation, water ultrafiltration, and microfiltration/nanofiltration, being a promising technique for having clean and fresh water, which is essential for human health. Porous alumina-based nanobiosensor coated with specific antibodies or peptides seem to be a useful tool to detect and remove pathogens both in food and in water, as well as for environmental monitoring. Further, these applications, being low-energy demanding and cost-effective, are particularly valuable in resource-limited settings and contexts, and can be employed as point of use devices in developing countries, where there is an urgent need of hygiene and safety assurance.

  20. Modifying alumina red mud to support a revegetation cover

    Science.gov (United States)

    Xenidis, A.; Harokopou, A. D.; Mylona, E.; Brofas, G.

    2005-02-01

    Alumina red mud, a fine-textured, iron-rich, alkaline residue, is the major waste product of bauxite digestion with caustic soda to remove alumina. The high alkalinity and salinity as well as the poor nutrient status are considered to be the major constraints of red mud revegetation. This research was conducted to evaluate the ameliorating effect of gypsum, sewage sludge, ferrous sulfate, ammonium sulfate, ammonium nitrate, and calcium phosphate on alumina red mud. The effectiveness of the mixtures was evaluated by applying extraction tests and performing experiments using six plant species. Gypsum amendment significantly reduced the pH, electrical conductivity, and sodium and aluminum content of red mud. Sewage sludge application had an extended effect in improving both the soil structure and the nutrient status of the gypsum-amended red mud. Together with the gypsum and sewage sludge, calcium phosphate application into red mud enhanced plant growth and gave the most promising results.

  1. Effect of different sources of alumina on the microstructure and mechanical properties of the triaxial porcelain

    OpenAIRE

    Gralik,G.; Chinelattot,A. L.; A. S. A. Chinelatto

    2014-01-01

    Porcelains composed of kaolin-quartz-feldspar are called triaxial porcelains. The use of alumina as a substitute for quartz in porcelains has been developed for some time. The results show a significant improvement in their mechanical properties, but alumina has a high cost. The possibility of using alternative materials as a source of alumina with lower cost was investigated. In this work, alternative raw materials were used as a source of alumina: refractory bauxite, primary aluminum hydrox...

  2. A Bayesian method for pulsar template generation

    CERN Document Server

    Imgrund, M; Kramer, M; Lesch, H

    2015-01-01

    Extracting Times of Arrival from pulsar radio signals depends on the knowledge of the pulsars pulse profile and how this template is generated. We examine pulsar template generation with Bayesian methods. We will contrast the classical generation mechanism of averaging intensity profiles with a new approach based on Bayesian inference. We introduce the Bayesian measurement model imposed and derive the algorithm to reconstruct a "statistical template" out of noisy data. The properties of these "statistical templates" are analysed with simulated and real measurement data from PSR B1133+16. We explain how to put this new form of template to use in analysing secondary parameters of interest and give various examples: We implement a nonlinear filter for determining ToAs of pulsars. Applying this method to data from PSR J1713+0747 we derive ToAs self consistently, meaning all epochs were timed and we used the same epochs for template generation. While the average template contains fluctuations and noise as unavoida...

  3. Factors contributing to the breakdown of sodium beta-alumina

    Energy Technology Data Exchange (ETDEWEB)

    Buechele, A.C.

    1982-05-01

    Clarification of the breakdown process occurring during charge transfer in sodium beta alumina solid electrolytes was derived from: (1) studying the effects of molten sodium contact at 350/sup 0/C on single crystal sodium beta alumina and polycrystalline sodium beta alumina; (2) determination of critical current density by monitoring acoustic emissions accompanying crack growth in sodium/sodium beta alumina/sodium cells subjected to linear current ramping at 1 mA cm/sup -2/ sec/sup -1/; (3) failure analysis conducted on cycled electrolytes, some from commercial sodium/sulfur cells, which had been subjected to up to 703 Ahr cm/sup -2/ of charge transfer. Gray coloration developing in beta aluminas in contact with molten sodium was found to be a consequence of formation, through reduction by sodium, of oxygen vacancies charge compensated by electrons. Electronic conductivity of the electrolyte increases as a result. No second phase formation was detected. Colored electrolytes from sodium/sulfur cells show evidence of a newly recognized degradation mechanism in which fracture occurs when sodium is reduced and deposited internally under pressure as metal in regions where an electronic conductivity gradient exists. Heating colored beta aluminas in air produces reoxidation and bleaching. Kinetics and other properties of the coloration and bleaching processes were determined. Critical current density was found to bear an inverse relation to average electrolyte grain size. Evidence was found in the cycled electrolytes for a slow crack growth mechanism and a progressive mode of degradation advancing from the sulfur electrode interface. Implications of the findings for the construction and operation of sodium/sulfur battery systems are discussed.

  4. Templated Growth of Magnetic Recording Media

    Science.gov (United States)

    Sundar, Vignesh

    Current and potential next-generation magnetic recording technologies are based on the writing and reading of bits on a magnetic thin film with a granular microstructure, with grains of the magnetic material surrounded by an amorphous segregant. In order to realize the highest achievable data storage capabilities, there is a need for better control of the magnetic media microstructure, particularly in terms of minimizing grain size and grain boundary thickness distributions. In this work, a guided magnetic media growth is attempted by creating a pre-fabricated template with a specific material and morphology. The template is designed in such a way that, when magnetic media consisting of the magnetic alloy and segregant are sputtered, the sites on the template result in a controlled two-phase growth of magnetic media. The template is fabricated using self-assembling block copolymers, which can be used to fabricate nanostructures with a regular hexagonal lattice of spheres of one block in the other's matrix. These are then used as etch-masks to fabricate the template. In this thesis, we describe the approach used to fabricate these templates and demonstrate the two-phase growth of magnetic recording media. In such an approach, the magnetic grain size is defined by the uniform pitch of the block copolymer pattern, resulting in a uniform microstructure with much better grain size distribution than can be obtained with conventional un-templated media growth. The templated growth technique is also a suitable additive technique for the fabrication of Bit Patterned Media, another potential next-generation technology wherein the magnetic bits are isolated patterned islands. Combining nanoimprint lithography with templated growth, we can generate a long range spatially ordered array of magnetic islands with no etching of the magnetic material.

  5. Effect of Filler Composition on the Brazing of Alumina to Copper Using Ultrasonic Wave

    Institute of Scientific and Technical Information of China (English)

    Khalid M. HAFEZ; Masaaki NAKA

    2003-01-01

    An ultrasonic wave was applied during brazing of alumina to Cu. First alumina was metallized by applying ultrasonicwave in braze bath. Then the metallized alumina was brazed with Cu using the same filler alloy. The filler used wereZn-Al alloys and Zn-Sn A

  6. Cylindrical Three-Dimensional Porous Anodic Alumina Networks

    Directory of Open Access Journals (Sweden)

    Pedro M. Resende

    2016-11-01

    Full Text Available The synthesis of a conformal three-dimensional nanostructure based on porous anodic alumina with transversal nanopores on wires is herein presented. The resulting three-dimensional network exhibits the same nanostructure as that obtained on planar geometries, but with a macroscopic cylindrical geometry. The morphological analysis of the nanostructure revealed the effects of the initial defects on the aluminum surface and the mechanical strains on the integrity of the three-dimensional network. The results evidence the feasibility of obtaining 3D porous anodic alumina on non-planar aluminum substrates.

  7. Atomistic force field for alumina fit to density functional theory.

    Science.gov (United States)

    Sarsam, Joanne; Finnis, Michael W; Tangney, Paul

    2013-11-28

    We present a force field for bulk alumina (Al2O3), which has been parametrized by fitting the energies, forces, and stresses of a large database of reference configurations to those calculated with density functional theory (DFT). We use a functional form that is simpler and computationally more efficient than some existing models of alumina parametrized by a similar technique. Nevertheless, we demonstrate an accuracy of our potential that is comparable to those existing models and to DFT. We present calculations of crystal structures and energies, elastic constants, phonon spectra, thermal expansion, and point defect formation energies.

  8. Controllable synthesis and characterization of alumina/MWNT nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Nemeth, Zoltan; Hernadi, Klara [Department of Applied and Environmental Chemistry, University of Szeged, Rerrich Bela ter 1, 6720 Szeged (Hungary); Marko, Kata; Erdohelyi, Andras [Department of Physical Chemistry and Material Science, University of Szeged, Aradi ter 2, 6720 Szeged (Hungary); Forro, Laszlo [Laboratory of Physics of Complex Matter, IPMC, EPFL, 1026 Ecublens (Switzerland)

    2011-11-15

    The aim of this work is to develop a controllable synthesis pathway which produces a stable alumina layer on the surface of carbon nanotubes by impregnation method. Precursor compounds such as aluminium isopropoxide and aluminium-acetyl-acetonate were used to cover the surface of multiwalled carbon nanotubes (MWNTs) under different solvent conditions. As-prepared alumina coverages were characterized by TEM, SEM, SEM-EDX, TG and X-ray diffraction techniques. Results revealed that homogeneous coverage can be achieved in a controllable way. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  9. Mechanical properties of tricalcium phosphate-alumina composites

    Science.gov (United States)

    Sakka, S.; Ben Ayed, F.; Bouaziz, J.

    2012-02-01

    Tricalcium phosphate and alumina powder were mixed in order to elaborate biphasic ceramics composites. This study deals to produce bioceramics composites sintered at various temperatures for differents times. The characterization of samples, before and after the sintering process was investigated, using X-Ray diffraction, scanning electronic microscopy, 31P and 27Al nuclear magnetic resonance and differential thermal analysis. Mechanical properties of biphasic composites were studied using Brazilian test. The tricalcium phosphate - 75 wt% alumina composites mechanical resistance increased with sintered temperature. The mechanical resistance reach it's optimum value (8.6 MPa) at 1550°C for two hours.

  10. CRACK PROPAGATION BEHAVIOR AND LIFETIME PREDICTION IN ALUMINA AND ZIRCONIA

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    The lifetime prediction of ceramics is discussed on the basis of the relationship between stress intensity factor KI and crack velocity v. The effects of water environment, the cyclic loading and microstructure of material on KI-v characteristics are studied by carrying out the crack growth tests by the double torsion (DT) method under the static and cyclic loading in both environments of air and water for alumina and zirconia. KI-v characteristics determined by the double torsion method are used to predict time-to-failure under the cyclic loading of alumina and zirconia ceramics. The predictions agree qualitatively with the experimental results.

  11. Templating irreversible covalent macrocyclization by using anions.

    Science.gov (United States)

    Kataev, Evgeny A; Kolesnikov, Grigory V; Arnold, Rene; Lavrov, Herman V; Khrustalev, Victor N

    2013-03-11

    Inorganic anions were used as templates in the reaction between a diamine and an activated diacid to form macrocyclic amides. The reaction conditions were found to perform the macrocyclization sufficiently slow to observe a template effect. A number of analytical methods were used to clarify the reaction mechanisms and to show that the structure of the intermediate plays a decisive role in determining the product distribution. For the macrocyclization under kinetic control, it was shown that the amount of a template, the conformational rigidity of building blocks, and the anion affinities of reaction components and intermediates are important parameters that one should take into consideration to achieve high yields.

  12. Fabrication of Gold-Coated Ultra-Thin Anodic Porous Alumina Substrates for Augmented SERS

    Directory of Open Access Journals (Sweden)

    Chiara Toccafondi

    2016-05-01

    Full Text Available Anodic porous alumina (APA is a nanostructured material used as a template in several nanotechnological applications. We propose the use of APA in ultra-thin form (<100 nm for augmented surface-enhanced Raman scattering (SERS. Here, the effect of in-depth thinning of the APA nanostructures for possible maximization of SERS was addressed. Anodization was carried out on ultra-thin films of aluminum on glass and/or silicon, followed by pore-opening. Gold (Au was overcoated and micro‑Raman/SERS measurements were carried out on test target analytes. Finite integration technique simulations of the APA-Au substrate were used both for the experimental design and simulations. It was observed that, under optimized conditions of APA and Au thickness, the SERS enhancement is higher than on standard APA-Au substrates based on thin (~100 nm APA by up to a factor of ~20 for test molecules of mercaptobenzoic acid. The agreement between model and experimental results confirms the current understanding of SERS as being mainly due to the physical origin of plasmon resonances. The reported results represent one step towards micro-technological, integrated, disposable, high-sensitivity SERS chemical sensors and biosensors based on similar substrates.

  13. Templated and template-free fabrication strategies for zero-dimensional hollow MOF superstructures.

    Science.gov (United States)

    Kim, Hyehyun; Lah, Myoung Soo

    2017-03-23

    Various fabrication strategies for hollow metal-organic framework (MOF) superstructures are reviewed and classified using various types of external templates and their properties. Hollow MOF superstructures have also been prepared without external templates, wherein unstable intermediates obtained during reactions convert to the final hollow MOF superstructures. Many hollow MOF superstructures have been fabricated using hard templates. After the core-shell core@MOF structure was prepared using a hard template, the core was selectively etched to generate a hollow MOF superstructure. Another approach for generating hollow superstructures is to use a solid reactant as a sacrificial template; this method requires no additional etching process. Soft templates such as discontinuous liquid/emulsion droplets and gas bubbles in a continuous soft phase have also been employed to prepare hollow MOF superstructures.

  14. Template for safety reports with descriptive example

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1995-12-01

    This report provides a template for future safety reports on long-term safety in support of important decisions and permit applications in connection with the construction of a deep repository system. The template aims at providing a uniform structure for describing long-term safety, after the repository has been closed and sealed. The availability of such a structure will simplify both preparation and review of the safety reports, and make it possible to follow how safety assessments are influenced by the progressively more detailed body of data that emerges. A separate section containing `descriptive examples` has been appended to the template. This section illustrates what the different chapters of the template should contain. 279 refs.

  15. Surgical Templates for Dental Implant Positioning; Current ...

    African Journals Online (AJOL)

    applied scientifically based research techniques to develop an endosseous implant that forms ... KEYWORDS: Dental implants, surgical templates, surgical procedure, stent .... during the surgical stage for single implant therapy.[24] Afterward,.

  16. Nanowires and nanostructures fabrication using template methods

    DEFF Research Database (Denmark)

    Mátéfi-Tempfli, Stefan; Mátéfi-Tempfli, M.; Vlad, A.;

    2009-01-01

    One of the great challenges of today is to find reliable techniques for the fabrication of nanomaterials and nanostructures. Methods based on template synthesis and on self organization are the most promising due to their easiness and low cost. This paper focuses on the electrochemical synthesis ...... of nanowires and nanostructures using nanoporous host materials such as supported anodic aluminum considering it as a key template for nanowires based devices. New ways are opened for applications by combining such template synthesis methods with nanolithographic techniques.......One of the great challenges of today is to find reliable techniques for the fabrication of nanomaterials and nanostructures. Methods based on template synthesis and on self organization are the most promising due to their easiness and low cost. This paper focuses on the electrochemical synthesis...

  17. Template Approach for Adaptive Learning Strategies

    NARCIS (Netherlands)

    Abbing, Jana; Koidl, Kevin

    2006-01-01

    Please, cite this publication as: Abbing, J. & Koidl, K. (2006). Template Approach for Adaptive Learning Strategies. Proceedings of Adaptive Hypermedia. June, Dublin, Ireland. Retrieved June 30th, 2006, from http://dspace.learningnetworks.org

  18. Performance Evaluation of Biometric Template Update

    CERN Document Server

    Giot, Romain; Dorizzi, Bernadette

    2012-01-01

    Template update allows to modify the biometric reference of a user while he uses the biometric system. With such kind of mechanism we expect the biometric system uses always an up to date representation of the user, by capturing his intra-class (temporary or permanent) variability. Although several studies exist in the literature, there is no commonly adopted evaluation scheme. This does not ease the comparison of the different systems of the literature. In this paper, we show that using different evaluation procedures can lead in different, and contradictory, interpretations of the results. We use a keystroke dynamics (which is a modality suffering of template ageing quickly) template update system on a dataset consisting of height different sessions to illustrate this point. Even if we do not answer to this problematic, it shows that it is necessary to normalize the template update evaluation procedures.

  19. Fast Legendre moment computation for template matching

    Science.gov (United States)

    Li, Bing C.

    2017-05-01

    Normalized cross correlation (NCC) based template matching is insensitive to intensity changes and it has many applications in image processing, object detection, video tracking and pattern recognition. However, normalized cross correlation implementation is computationally expensive since it involves both correlation computation and normalization implementation. In this paper, we propose Legendre moment approach for fast normalized cross correlation implementation and show that the computational cost of this proposed approach is independent of template mask sizes which is significantly faster than traditional mask size dependent approaches, especially for large mask templates. Legendre polynomials have been widely used in solving Laplace equation in electrodynamics in spherical coordinate systems, and solving Schrodinger equation in quantum mechanics. In this paper, we extend Legendre polynomials from physics to computer vision and pattern recognition fields, and demonstrate that Legendre polynomials can help to reduce the computational cost of NCC based template matching significantly.

  20. Macroporous polymer foams by hydrocarbon templating

    OpenAIRE

    Shastri, Venkatram Prasad; Martin, Ivan; Langer, Robert

    2000-01-01

    Porous polymeric media (polymer foams) are utilized in a wide range of applications, such as thermal and mechanical insulators, solid supports for catalysis, and medical devices. A process for the production of polymer foams has been developed. This process, which is applicable to a wide range of polymers, uses a hydrocarbon particulate phase as a template for the precipitation of the polymer phase and subsequent pore formation. The use of a hydrocarbon template allows for enhanced control ov...

  1. Scalable, Fast Cloud Computing with Execution Templates

    OpenAIRE

    Mashayekhi, Omid; Qu, Hang; Shah, Chinmayee; Levis, Philip

    2016-01-01

    Large scale cloud data analytics applications are often CPU bound. Most of these cycles are wasted: benchmarks written in C++ run 10-51 times faster than frameworks such as Naiad and Spark. However, calling faster implementations from those frameworks only sees moderate (3-5x) speedups because their control planes cannot schedule work fast enough. This paper presents execution templates, a control plane abstraction for CPU-bound cloud applications, such as machine learning. Execution template...

  2. Template synthesis of monodisperse carbon nanodots

    Science.gov (United States)

    Kurdyukov, D. A.; Eurov, D. A.; Stovpiaga, E. Yu.; Kirilenko, D. A.; Konyakhin, S. V.; Shvidchenko, A. V.; Golubev, V. G.

    2016-12-01

    Monodisperse carbon nanodots in pores of mesoporous silica particles are obtained by template synthesis. This method is based on introducing a precursor (organosilane) into pores, its thermal decomposition with formation of carbon nanodots, and the template removal. Structural analysis of the nanomaterial has been performed, which showed that carbon nanodots have an approximately spherical form and a graphite-like structure. According to dynamic light scattering data, the size of carbon nanodots is 3.3 ± 0.9 nm.

  3. Lipid bilayers on nano-templates

    Science.gov (United States)

    Noy, Aleksandr; Artyukhin, Alexander B.; Bakajin, Olgica; Stoeve, Pieter

    2009-08-04

    A lipid bilayer on a nano-template comprising a nanotube or nanowire and a lipid bilayer around the nanotube or nanowire. One embodiment provides a method of fabricating a lipid bilayer on a nano-template comprising the steps of providing a nanotube or nanowire and forming a lipid bilayer around the polymer cushion. One embodiment provides a protein pore in the lipid bilayer. In one embodiment the protein pore is sensitive to specific agents

  4. Substrate-induced coagulation (SIC) of nano-disperse alumina in non-aqueous media: The dispersibility and stability of alumina in N-methyl-2-pyrrolidinone

    OpenAIRE

    Basch, Angelika; Strnad, Simona

    2011-01-01

    This work investigated colloidal properties such as the zeta-potential, the electrophoretic mobilities and the wetting behaviour of alumina dispersed in non-aqueous media. Non-aqueous dispersions of alumina were prepared in the solvent N-methyl-2-pyrrolidinone (NMP). The wetting behaviour of alumina in NMP was characterized by the powder contact angle method and the Wilhemy plate method. The behaviour of the dispersion should provide information for the development of a substrate-induced coag...

  5. Effect of La2O3 on Microstructure and Transmittance of Transparent Alumina Ceramics

    Institute of Scientific and Technical Information of China (English)

    2006-01-01

    Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H2 atmosphere. The results indicate that relative densities of alumina specimens increase to theoretical densities (T.D.) with increasing content of La2O3. With increasing holding time during sintering, much less pores and larger grains were found in the sintered alumina samples. Higher transmittance was achieved in alumina codoped with MgO and La2O3 as compared with that doped with MgO only. The total-transmittance of alumina sample is up to 86% at a wavelength range of 300~800 nm.

  6. A General Procedure for Surface Modification of Nano-alumina and Its Application to Dendrimers

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    A general procedure for surface modification of nano-alumina using N, N'-dicyclohexyl-carbodiimide (DCC) mediated amidation is reported. Aliphatic and aromatic carboxylic acids reacted smoothly with nano-alumina pretreated with 3-aminopropyltriethoxysilane in the presence of DCC, giving modified aluminas having organic surfaces. The grafted aluminas have been characterized qualitatively by FT-IR or 13C CPMAS NMR spectroscopy, and quantitatively by thermogravimetric analysis and elemental analysis. The procedure was applied to polyether dendrons bearing carboxyl groups at the focal points, giving successful grafting of dendrimers onto nano-alumina.

  7. Multi-template polymerase chain reaction

    Directory of Open Access Journals (Sweden)

    Elena Kalle

    2014-12-01

    Full Text Available PCR is a formidable and potent technology that serves as an indispensable tool in a wide range of biological disciplines. However, due to the ease of use and often lack of rigorous standards many PCR applications can lead to highly variable, inaccurate, and ultimately meaningless results. Thus, rigorous method validation must precede its broad adoption to any new application. Multi-template samples possess particular features, which make their PCR analysis prone to artifacts and biases: multiple homologous templates present in copy numbers that vary within several orders of magnitude. Such conditions are a breeding ground for chimeras and heteroduplexes. Differences in template amplification efficiencies and template competition for reaction compounds undermine correct preservation of the original template ratio. In addition, the presence of inhibitors aggravates all of the above-mentioned problems. Inhibitors might also have ambivalent effects on the different templates within the same sample. Yet, no standard approaches exist for monitoring inhibitory effects in multitemplate PCR, which is crucial for establishing compatibility between samples.

  8. Joining between alumina and metal by use of plasma sprayed Ni-Al coating on alumina. Alumina ni plasma yoshashita Ni-Al kinzoku himaku wo kaishite no alumina kinzoku tono setsugo

    Energy Technology Data Exchange (ETDEWEB)

    Murakami, N.; Kishitake, K.; Hasebe, M.; Kobayashi, T.; Murashige, K. (Kyushu Institute of Technology, Kitakyushu (Japan). Faculty of Engineering)

    1993-06-30

    A ceramic material is joined and compounded with a metal by spraying another metal on the ceramic material, and then joined with the intended metal because of small adhesion strength in both materials. Adhesion strength of the spraying metal is important even in this case. The present experiment performed plasma spraying of Ni-Al mixed powder on alumina to investigate effects of the heating on the adhesion strength. Solder joining of Ni-Al sprayed alumina with soft steel rod and copper rod was also tested. As a result, the adhesion strength of as-sprayed Ni-Al film on the alumina was about 5 MPa and maximum of 10 MPa. Heating the materials to 1173 K for 10 hours or longer provided an average strength of 20 MPa and a maximum strength of 35 MPa. Improving the adhesion strength requires spinel to be produced through reactions on the interface. It was found that alumina can be joined with metal easily by going through this film. 12 refs., 6 figs.

  9. Development of Cast Alumina-Forming Austenitic Stainless Steels

    Science.gov (United States)

    Muralidharan, G.; Yamamoto, Y.; Brady, M. P.; Walker, L. R.; Meyer, H. M., III; Leonard, D. N.

    2016-11-01

    Cast Fe-Ni-Cr chromia-forming austenitic stainless steels with Ni levels up to 45 wt.% are used at high temperatures in a wide range of industrial applications that demand microstructural stability, corrosion resistance, and creep strength. Although alumina scales offer better corrosion protection at these temperatures, designing cast austenitic alloys that form a stable alumina scale and achieve creep strength comparable to existing cast chromia-forming alloys is challenging. This work outlines the development of cast Fe-Ni-Cr-Al austenitic stainless steels containing about 25 wt.% Ni with good creep strength and the ability to form a protective alumina scale for use at temperatures up to 800-850°C in H2O-, S-, and C-containing environments. Creep properties of the best alloy were comparable to that of HK-type cast chromia-forming alloys along with improved oxidation resistance typical of alumina-forming alloys. Challenges in the design of cast alloys and a potential path to increasing the temperature capability are discussed.

  10. Laser-induced prenucleation of alumina for electroless plating

    NARCIS (Netherlands)

    Shrivastva, P.B.; Harteveld, C.; Boose, C.A.; Kolster, B.H.

    1991-01-01

    This paper deals with the deposition of palladium from decomposition of a thin palladium acetate layer on rough and porous alumina ceramic surfaces by irradiating it with a UV excimer laser. The palladium acetate layer was formed from a combination of propyl glycol methyl ether acetate solvent and p

  11. Development of Cast Alumina-Forming Austenitic Stainless Steels

    Science.gov (United States)

    Muralidharan, G.; Yamamoto, Y.; Brady, M. P.; Walker, L. R.; Meyer, H. M., III; Leonard, D. N.

    2016-09-01

    Cast Fe-Ni-Cr chromia-forming austenitic stainless steels with Ni levels up to 45 wt.% are used at high temperatures in a wide range of industrial applications that demand microstructural stability, corrosion resistance, and creep strength. Although alumina scales offer better corrosion protection at these temperatures, designing cast austenitic alloys that form a stable alumina scale and achieve creep strength comparable to existing cast chromia-forming alloys is challenging. This work outlines the development of cast Fe-Ni-Cr-Al austenitic stainless steels containing about 25 wt.% Ni with good creep strength and the ability to form a protective alumina scale for use at temperatures up to 800-850°C in H2O-, S-, and C-containing environments. Creep properties of the best alloy were comparable to that of HK-type cast chromia-forming alloys along with improved oxidation resistance typical of alumina-forming alloys. Challenges in the design of cast alloys and a potential path to increasing the temperature capability are discussed.

  12. Experiments on individual alumina-supported adatoms and clusters

    Science.gov (United States)

    Nilius, N.; Cörper, A.; Bozdech, G.; Ernst, N.; Freund, H.-J.

    2001-08-01

    To contribute to an understanding of growth conditions and electronic properties of metal clusters on technologically relevant oxides we have examined the mobility of individual, alumina-supported Pt-adatoms and the optical properties of single supported Ag-clusters. Using field-ion microscopy (FIM) we have prepared and imaged an individual Pt-adatom at approximately 40 K, both on the apex plane of a [1 1 0]-oriented NiAl tip and on a thin alumina film, grown on the same NiAl specimen by oxidation. On the alumina film, the onset temperature for Pt surface diffusion approaches 100 K being distinctively lower than the value 165 K measured on NiAl(1 1 0). Employing the tip of a scanning tunneling microscope (STM) as a local electron source, photon emission from individual, alumina-supported Ag-clusters was spectroscopically analyzed. The occurrence of a distinct emission line is explained by the decay of a collective electron oscillation (Mie-plasmon resonance). For decreasing Ag-cluster diameter, the emission lines (i) shift to higher energies and (ii) their widths increase. To explain these observations, we discuss (i) the reduced screening of the plasmon oscillation due to the Ag 4d electrons and (ii) an enhanced electron surface scattering rate in small clusters.

  13. Dynamical stability of the alpha and theta phases of alumina

    DEFF Research Database (Denmark)

    Lodziana, Zbigniew; Parlinski, K.

    2003-01-01

    Using density functional calculations the phonon dispersion relations, phonon density of states, and free energy of theta and alpha phases of alumina are investigated. The temperature dependence of the free energy indicates that entropy contributes to the destabilization of the alpha phase...

  14. Gas and surface diffusion in modified γ-alumina systems

    NARCIS (Netherlands)

    Uhlhorn, R.J.R.; Keizer, K.; Burggraaf, A.J.

    1989-01-01

    The transport of pure gases through a microporous membrane is described. The alumina-based membrane (pores 2.5-4 nm) is suitable for Knudsen diffusion separation. To improve the separation factor, interaction with and mobility on the pore wall of one of the gases of a mixture is necessary. To introd

  15. Capillary condensation in porous alumina observed by positronium lifetime spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Ivanov, Eugeniu [National Institute for Nuclear Physics and Engineering-Horia Hulubei, Atomistilor Street 407, CP MG 06, Magurele, Bucharest (Romania); Center for Advanced Studies in Physics of the Roumanian Academy, Casa Academiei Romane, Calea 13 Septembrie No. 13, Bucharest (Romania); Vata, Ion [National Institute for Nuclear Physics and Engineering-Horia Hulubei, Atomistilor Street 407, CP MG 06, Magurele, Bucharest (Romania)], E-mail: vata@ifin.nipne.ro; Toderian, Stefan; Dudu, Dorin; Rusen, Ion; Stefan, Nitisor [National Institute for Nuclear Physics and Engineering-Horia Hulubei, Atomistilor Street 407, CP MG 06, Magurele, Bucharest (Romania)

    2008-10-31

    The PALS method based on time distribution measurements has been used to study capillary condensation of different gases adsorbed in microporous alumina powder. The isotherms exhibit features which are associated with a shifted gas-liquid transition. The sorption and desorption processes are irreversible presenting a hysteresis effect. Suggestions on some new aspects of the capillary condensation dynamics are made.

  16. Structure and surface properties of praseodymium modified alumina

    Energy Technology Data Exchange (ETDEWEB)

    Tankov, I. [Institute of Catalysis, Bulgarian Academy of Sciences, 1113 Sofia (Bulgaria); Pawelec, B. [Instituto de Catalisis y Petroleoquimica, CSIC, Cantoblanco, 28049 Madrid (Spain); Arishtirova, K. [Institute of Catalysis, Bulgarian Academy of Sciences, 1113 Sofia (Bulgaria); Damyanova, S., E-mail: soniad@ic.bas.bg [Institute of Catalysis, Bulgarian Academy of Sciences, 1113 Sofia (Bulgaria)

    2011-10-15

    Mixed PrO{sub 2}-Al{sub 2}O{sub 3} oxides with different PrO{sub 2} content (1-20 wt.%) were prepared by wetness impregnation of {gamma}-alumina with aqueous solution of praseodymium nitrate. The samples were characterized by different techniques, using surface adsorption-desorption of N{sub 2} (S{sub BET}), thermogravimetric analysis (TGA), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), UV-vis diffuse reflectance spectroscopy (DRS), temperature-programmed reduction (TPR) and temperature-programmed desorption of CO{sub 2} (TPD-CO{sub 2}). TGA and XRD showed the presence of small praseodymium oxide species on the alumina surface. XPS and DRS detected electron deficient interaction between deposited praseodymium oxide and alumina. It was observed a lower reduction temperature for supported Pr oxide species compared to that of the bulk Pr{sub 6}O{sub 11}. TPD-CO{sub 2} studies suggested that the deposition of Pr oxide on alumina leaded to increase of the basicity of mixed oxides.

  17. Ionic Segregation on Grain Boundaries in Thermally Grown Alumina Scales

    Energy Technology Data Exchange (ETDEWEB)

    Pint, Bruce A [ORNL; Unocic, Kinga A [ORNL

    2012-01-01

    This study first examined segregation behaviour in the alumina scale formed after 100 h at 1100 C on bare and MCrAlYHfSi-coated single-crystal superalloys with {approx}10 ppma La and Y. For the bare superalloy, Hf and Ti were detected on the grain boundaries of the inner columnar alumina layer. Increasing the oxidation temperature to 1200 C for 2 h did not change the segregation behavior. With the bond coating, both Y and Hf were segregated to the grain boundaries as expected. However, there was evidence of Ti-rich oxide particles near the gas interface suggesting that Ti diffused from the superalloy through the coating. To further understand these segregation observations with multiple dopants, other alumina-forming systems were examined. Alumina scale grain boundary co-segregation of Ti with Y is common for FeCrAl alloys. Co-segregation of Hf and Ti was observed in the scale formed on co-doped NiAl. No La segregation was detected in the scale formed on NiCrAl with only a 19 ppma La addition, however, the scale was adherent.

  18. Osseointegration of alumina bioceramic granules: A comparative experimental study

    Science.gov (United States)

    Rerikh, V. V.; Avetisyan, A. R.; Zaydman, A. M.; Anikin, K. A.; Bataev, V. A.; Nikulina, A. A.; Sadovoy, M. A.; Aronov, A. M.; Semantsova, E. S.

    2016-08-01

    To perform a comparative analysis of osseointegration of bioceramic alumina-based granules, hydroxyapatite-based granules, and deproteinized bone granules. The experiment was conducted on 52 adult male Kyoto-Wistar rats weighing 350 to 520 g. The animals were divided into five matched groups that differed only in the type of an implanted material. The granules were implanted in the lumbar vertebral bodies and in the distal right femur of each laboratory animal. Two months after surgery, the animals were euthanized, followed by tissue sampling for morphological studies. An examination of specimens from the groups with implanted alumina granules revealed the newly formed trabecular bone with remodeling signs. The bone tissue filled the intragranular space, tightly adhering to the granule surface. There was no connective tissue capsule on the border between bone tissue and alumina granules. Cylindrical bioceramic alumina-based granules with an open internal channel have a higher strength surpassing than that of analogs and the osseointegration ability close to that of hydroxyapatite and deproteinized bone granules.

  19. Sol-gel based alumina powders with catalytic applications

    Science.gov (United States)

    Crişan, Maria; Zaharescu, Maria; Kumari, Valluri Durga; Subrahmanyam, Machiraju; Crişan, Dorel; Drăgan, Nicolae; Răileanu, Mălina; Jitianu, Mihaela; Rusu, Adriana; Sadanandam, Gullapelli; Krishna Reddy, Jakkidi

    2011-10-01

    The sol-gel process provides a new approach to the preparation of oxide materials and offers many advantages for making catalysts. Since homogeneous mixing can be achieved at the molecular scale, the chemical reactivity of the oxide surface can be greatly enhanced; thus powders with high surface area and optimized pore size distribution can be obtained at low temperatures. In the present work NiO/Al 2O 3 sol-gel catalysts were obtained by simultaneous gelation of aluminium isopropoxide and nickel nitrate. A comparative study with pure sol-gel alumina was also realized. By physical-structural studies the changes induced by the introduction of the Ni precursor, before and after aluminium alkoxide hydrolysis were highlighted. The introduction of Ni at the beginning of the reaction favors γ-Al 2O 3 crystallization. When Ni is added at the end of reaction, it delays the alumina crystallization and induces the disorder of the lattice. The obtained Ni doped sol-gel derived alumina has been used as catalyst in the finished form for glycerol reforming to generate H 2 for fuel cell applications. Some evaluation results of Ni-doped alumina combined with TiO 2 in photocatalytic glycerol reforming reaction have been included.

  20. State of the art: alumina ceramics for energy applications

    Energy Technology Data Exchange (ETDEWEB)

    Hauth, W.E.; Stoddard, S.D.

    1978-01-01

    Prominent ceramic raw materials and products manufacturers were surveyed to determine the state of the art for alumina ceramic fabrication. This survey emphasized current capabilities and limitations for fabrication of large, high-density, high-purity, complex shapes. Some directions are suggested for future needs and development.

  1. Thin alumina and silica films by chemical vapor deposition (CVD)

    NARCIS (Netherlands)

    Hofman, R.; Morssinkhof, R.W.J.; Fransen, T.; Westheim, J.G.F.; Gellings, P.J.

    1993-01-01

    Alumina and silica coatings have been deposited by MOCVD (Metal Organic Chemical Vapor Deposition) on alloys to protect them against high temperature corrosion. Aluminium Tri-lsopropoxide (ATI) and DiAcetoxyDitertiaryButoxySilane (DAOBS) have been used as metal organic precursors to prepare these ce

  2. Multifunctional substrates of thin porous alumina for cell biosensors

    KAUST Repository

    Toccafondi, Chiara

    2014-02-27

    We have fabricated anodic porous alumina from thin films (100/500 nm) of aluminium deposited on technological substrates of silicon/glass, and investigated the feasibility of this material as a surface for the development of analytical biosensors aiming to assess the status of living cells. To this goal, porous alumina surfaces with fixed pitch and variable pore size were analyzed for various functionalities. Gold coated (about 25 nm) alumina revealed surface enhanced Raman scattering increasing with the decrease in wall thickness, with factor up to values of approximately 104 with respect to the flat gold surface. Bare porous alumina was employed for micro-patterning and observation via fluorescence images of dye molecules, which demonstrated the surface capability for a drug-loading device. NIH-3T3 fibroblast cells were cultured in vitro and examined after 2 days since seeding, and no significant (P > 0.05) differences in their proliferation were observed on porous and non-porous materials. The effect on cell cultures of pore size in the range of 50–130 nm—with pore pitch of about 250 nm—showed no significant differences in cell viability and similar levels in all cases as on a control substrate. Future work will address combination of all above capabilities into a single device.

  3. Fabrication and investigation of regular arrays of Fe, Ni and Co nanowires using template synthesizing technique

    Energy Technology Data Exchange (ETDEWEB)

    Winkler, Nina; Lei, Yong; Wilde, Gerhard [Institute of Materials Physics and Center for Nanotechnology, University of Muenster, 48149 Muenster (Germany)

    2011-07-01

    Regular arrays of magnetic nanowires with a high aspect ratio have possible applications in high density magnetic recording media. Basic knowledge about magnetism may be obtained from these nanowire arrays as transition of multi-domain to single-domain wires occurs at the nanoscale. Modified Porous Alumina Membranes (PAMs) with pore diameters from 20 to 80 nm are well suited as templates for electrodeposition due to their high pore regularity. The pores of the PAM were filled with nickel, iron, cobalt, and multilayer structures of these metals, resulting in different metallic nanowire arrays. The deposition conditions for growing metallic nanowires are investigated in detail. The homogeneous structure and morphology of the template-prepared nanowire arrays is observed by SEM and TEM. The TEM and X-ray measurements indicate that the crystalline structure is either polycrystalline or amorphous depending on the deposition conditions. The magnetic properties of the nanowire arrays are investigated with vibrating sample magnetometry, which shows a preferential direction of magnetization along the wire axis due to the high aspect ratio of the nanowires. The wire interaction in the array is observed qualitatively with magnetic force microscopy.

  4. Template-assisted self-assembly of individual and clusters of magnetic nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Badini Confalonieri, G A; Ebbing, A; Mishra, D; Szary, P; Petracic, O; Zabel, H [Ruhr-Universitaet Bochum, Institut fuer Experimentalphysik/Festkoerperphysik, Bochum 44780 (Germany); Vega, V; Prida, V M, E-mail: giovanni.badini@rub.de [Departamento de Fisica, Universidad de Oviedo, Calvo Sotelo s/n, E-33007 Oviedo (Spain)

    2011-07-15

    The deliberate control over the spatial arrangement of nanostructures is the desired goal for many applications such as, for example, in data storage, plasmonics or sensor arrays. Here we present a novel method to assist the self-assembly process of magnetic nanoparticles. The method makes use of nanostructured aluminum templates obtained after anodization of aluminum discs and the subsequent growth and removal of the newly formed alumina layer, resulting in a regular honeycomb-type array of hexagonally shaped valleys. The iron oxide nanoparticles, 20 nm in diameter, are spin-coated onto the surface of honeycomb nanostructured Al templates. Depending on the size, each hexagon site can host up to 30 nanoparticles. These nanoparticles form clusters of different arrangements within the valleys, such as collars, chains and hexagonally closed islands. Ultimately, it is possible to isolate individual nanoparticles. The strengths of the magnetic interaction between particles in a cluster are probed using the memory effect known from the coupled state in superspin glass systems.

  5. High Thermal and Electrical Conductivity of Template Fabricated P3HT/MWCNT Composite Nanofibers.

    Science.gov (United States)

    Smith, Matthew K; Singh, Virendra; Kalaitzidou, Kyriaki; Cola, Baratunde A

    2016-06-15

    Nanoporous alumina membranes are filled with multiwalled carbon nanotubes (MWCNTs) and then poly(3-hexylthiophene-2,5-diyl) (P3HT) melt, resulting in nanofibers with nanoconfinement induced coalignment of both MWCNT and polymer chains. The simple sonication process proposed here can achieve vertically aligned arrays of P3HT/MWCNT composite nanofibers with 3 wt % to 55 wt % MWCNT content, measured using thermogravimetric methods. Electrical and thermal transport in the composite nanofibers improves drastically with increasing carbon nanotube content where nanofiber thermal conductivity peaks at 4.7 ± 1.1 Wm(-1)K(-1) for 24 wt % MWCNT and electrical percolation occurs once 20 wt % MWCNT content is surpassed. This is the first report of the thermal conductivity of template fabricated composite nanofibers and the first proposed processing technique to enable template fabrication of composite nanofibers with high filler content and long aspect ratio fillers, where enhanced properties can also be realized on the macroscale due to vertical alignment of the nanofibers. These materials are interesting for thermal management applications due to their high thermal conductivity and temperature stability.

  6. Fabrication of diameter-modulated and ultrathin porous nanowires in anodic aluminum oxide templates

    Energy Technology Data Exchange (ETDEWEB)

    Sulka, Grzegorz D., E-mail: Sulka@chemia.uj.edu.pl [Max Planck Institute of Microstructure Physics, Weinberg 2, 06120 Halle (Germany); Department of Physical Chemistry and Electrochemistry, Jagiellonian University, Ingardena 3, 30060 Krakow (Poland); Brzozka, Agnieszka [AGH University of Science and Technology, Faculty of Non-Ferrous Metals, Al. Mickiewicza 30, Krakow 30-059 (Poland); Liu, Lifeng [Max Planck Institute of Microstructure Physics, Weinberg 2, 06120 Halle (Germany)

    2011-05-30

    Graphical abstract: Display Omitted Highlights: > AAO templates with modulated pore diameter were fabricated by pulse anodization. > HA pulse duration tunes the shape of pores and the structure of AAO channels. > Au, Ag, Ni and Ag-Au diameter-modulated nanowires were synthetized. > Porous ultrathin Au nanowires were obtained by dealloying Ag-Au nanowires. - Abstract: Anodic aluminum oxide (AAO) membranes with modulated pore diameter were synthesized by pulse anodization in 0.3 M sulfuric acid at 1 deg. C. For AAO growth, a typical combination of alternating mild anodizing (MA) and hard anodizing (HA) pulses with applied potential pulses of 25 V and 35 V was applied. The control of the duration of HA pulses will provide an interesting way to tune the shape of pores and the structure of AAO channels. It was found that a non-uniform length of HA segments in cross section of AAO is usually observed when the HA pulse duration is shorter than 1.2 s. The pulse anodization performed with longer HA pulses leads to the formation of AAO templates with periodically modulated pore diameter and nearly uniform length of segments. Various diameter-modulated metallic nanowires (Au, Ag, Ni and Ag-Au) were fabricated by electrodeposition in the pores of anodic alumina membranes. A typical average nanowire diameter was about 30 nm and 48 nm for MA and HA nanowire segments, respectively. After a successful dealloying silver from Ag-Au nanowires, porous ultrathin Au nanowires were obtained.

  7. Synthesis and structural evaluation of freeze-cast porous alumina

    Energy Technology Data Exchange (ETDEWEB)

    Souza, Douglas F., E-mail: souzadf@outlook.com [Department of Metallurgical and Materials Engineering, Federal University of Minas Gerais — UFMG, Avenida Presidente Antônio Carlos, 6627, Campus UFMG, Belo Horizonte, MG CEP: 31270-901, Escola de Engenharia, bloco 2, sala 2230 (Brazil); Nunes, Eduardo H.M., E-mail: eduardohmn@gmail.com [Department of Metallurgical and Materials Engineering, Federal University of Minas Gerais — UFMG, Avenida Presidente Antônio Carlos, 6627, Campus UFMG, Belo Horizonte, MG CEP: 31270-901, Escola de Engenharia, bloco 2, sala 2230 (Brazil); Pimenta, Daiana S.; Vasconcelos, Daniela C.L. [Department of Metallurgical and Materials Engineering, Federal University of Minas Gerais — UFMG, Avenida Presidente Antônio Carlos, 6627, Campus UFMG, Belo Horizonte, MG CEP: 31270-901, Escola de Engenharia, bloco 2, sala 2230 (Brazil); Nascimento, Jailton F.; Grava, Wilson [Petrobras/CENPES, Avenida Horácio Macedo 950, Cidade Universitária, Ilha do Fundão, Rio de Janeiro, RJ CEP:21941-915 (Brazil); Houmard, Manuel [Department of Materials Engineering and Civil Construction, Federal University of Minas Gerais — UFMG, Avenida Presidente Antônio Carlos, 6627, Campus UFMG, Belo Horizonte, MG CEP: 31270-901, Escola de Engenharia, bloco 1, sala 3304 (Brazil); Vasconcelos, Wander L., E-mail: wlv@demet.ufmg.br [Department of Metallurgical and Materials Engineering, Federal University of Minas Gerais — UFMG, Avenida Presidente Antônio Carlos, 6627, Campus UFMG, Belo Horizonte, MG CEP: 31270-901, Escola de Engenharia, bloco 2, sala 2230 (Brazil)

    2014-10-15

    In this work we fabricated alumina samples by the freeze-casting technique using tert-butanol as the solvent. The prepared materials were examined by scanning electron microscopy and X-ray microtomography. Next, they were coated with sol–gel silica films by dip-coating. Permeability tests were carried out in order to assess the permeation behavior of the materials processed in this study. We observed that the sintering time and alumina loading showed a remarkable effect on both the structural properties and flexural strength of the freeze-cast samples. Nitrogen adsorption tests revealed that the silica prepared in this study exhibited a microporous structure. It was observed that the presence of silica coatings on the alumina surface decreased the CO{sub 2} permeance by about one order of magnitude. Because of the similar kinetic diameters of nitrogen and carbon dioxide, the CO{sub 2}/N{sub 2} system showed a separation efficiency that was lower than that observed for the He/CO{sub 2} and He/N{sub 2} systems. We noticed that increasing the feed pressure improved the separation capacity of the obtained materials. - Highlights: • Porous alumina samples obtained by the freeze-casting technique • Microporous silica coating prepared by a simple sol–gel dip-coating methodology • Samples examined by SEM, μ-CT, and nitrogen sorption tests • Mechanical tests were carried out in the freeze-cast samples. • The presence of silica coatings on the alumina surface decreased the CO{sub 2} permeance.

  8. Advanced morphological analysis of patterns of thin anodic porous alumina

    Energy Technology Data Exchange (ETDEWEB)

    Toccafondi, C. [Istituto Italiano di Tecnologia, Department of Nanophysics, Via Morego 30, Genova I 16163 (Italy); Istituto Italiano di Tecnologia, Department of Nanostructures, Via Morego 30, Genova I 16163 (Italy); Stępniowski, W.J. [Department of Advanced Materials and Technologies, Faculty of Advanced Technologies and Chemistry, Military University of Technology, 2 Kaliskiego Str., 00-908 Warszawa (Poland); Leoncini, M. [Istituto Italiano di Tecnologia, Department of Nanostructures, Via Morego 30, Genova I 16163 (Italy); Salerno, M., E-mail: marco.salerno@iit.it [Istituto Italiano di Tecnologia, Department of Nanophysics, Via Morego 30, Genova I 16163 (Italy)

    2014-08-15

    Different conditions of fabrication of thin anodic porous alumina on glass substrates have been explored, obtaining two sets of samples with varying pore density and porosity, respectively. The patterns of pores have been imaged by high resolution scanning electron microscopy and analyzed by innovative methods. The regularity ratio has been extracted from radial profiles of the fast Fourier transforms of the images. Additionally, the Minkowski measures have been calculated. It was first observed that the regularity ratio averaged across all directions is properly corrected by the coefficient previously determined in the literature. Furthermore, the angularly averaged regularity ratio for the thin porous alumina made during short single-step anodizations is lower than that of hexagonal patterns of pores as for thick porous alumina from aluminum electropolishing and two-step anodization. Therefore, the regularity ratio represents a reliable measure of pattern order. At the same time, the lower angular spread of the regularity ratio shows that disordered porous alumina is more isotropic. Within each set, when changing either pore density or porosity, both regularity and isotropy remain rather constant, showing consistent fabrication quality of the experimental patterns. Minor deviations are tentatively discussed with the aid of the Minkowski measures, and the slight decrease in both regularity and isotropy for the final data-points of the porosity set is ascribed to excess pore opening and consequent pore merging. - Highlights: • Thin porous alumina is partly self-ordered and pattern analysis is required. • Regularity ratio is often misused: we fix the averaging and consider its spread. • We also apply the mathematical tool of Minkowski measures, new in this field. • Regularity ratio shows pattern isotropy and Minkowski helps in assessment. • General agreement with perfect artificial patterns confirms the good manufacturing.

  9. EFFECTIVE ELASTIC PROPERTIES OF ALUMINA-ZIRCONIA COMPOSITE CERAMICS - PART 4. TENSILE MODULUS OF POROUS ALUMINA AND ZIRCONIA

    Directory of Open Access Journals (Sweden)

    W. Pabst

    2004-12-01

    Full Text Available In this fourth paper of a series on the effective elastic properties of alumina-zirconia composite ceramics the influence of porosity on the effective tensile modulus of alumina and zirconia ceramics is discussed. The examples investigated are alumina and zirconia ceramics prepared from submicron powders by starch consolidation casting using two different types of starch, potato starch (median size D50 =47.2 µm and corn starch (median size D50 =13.7 µm. The dependence of effective tensile moduli E, on the porosity f, measured for porosities in the ranges of approx. 19-55 vol.% and 10-42 vol.% for alumina and zirconia, respectively, using a resonant frequency technique, was evaluated by fitting with various model relations, including newly developed ones. A detailed comparison of the fitting results suggests the superiority of the new relation E/E0 = (1 - f·(1 - f/fC, developed by the authors (with the tensile modulus of the dense ceramic material E0 and the critical porosity fC, over most other existing fit models. Only for special purposes and well-behaved data sets the recently proposed exponential relation E/E0 = exp [-Bf/(1 - f] and the well-known Phani-Niyogi relation E/E0 = (1 - f/fCN might be preferable.

  10. Porous alumina, zirconia and alumina/zirconia for bone repair: fabrication, mechanical and in vitro biological response.

    Science.gov (United States)

    Hadjicharalambous, Chrystalleni; Buyakov, Ales; Buyakova, Svetlana; Kulkov, Sergey; Chatzinikolaidou, Maria

    2015-04-23

    Zirconia (ZrO2) and alumina (Al2O3) based ceramics are widely used for load-bearing applications in bone repair due to their excellent mechanical properties and biocompatibility. They are often regarded as bioinert since no direct bone-material interface is created unless a porous structure intercedes, leading to better bone bonding. In this regard, investigating interactions between cells and porous ceramics is of great interest. In the present study, we report on the successful fabrication of sintered alumina A-61, zirconia Z-50 and zirconia/alumina composite ZA-60 ceramics with medium porosities of 61, 50 and 60%, respectively, indicating a bimodal pore size distribution and good interconnectivity. They exhibit elastic moduli of 3-10 GPa and compressive strength values of 60-240 MPa, similar to those of human cortical bone.We performed in vitro cell-material investigations comparing the adhesion, proliferation and differentiation of mouse pre-osteoblasts MC3T3-E1 on the three porous materials. While all three ceramics demonstrate a strong cell attachment, better cell spreading is observed on zirconia-containing substrates. Significantly higher cell growth was quantified on the latter ceramics, revealing an increased alkaline phosphatase activity, higher collagen production and increased calcium biomineralization compared to A-61. Hence, these porous zirconia-containing ceramics elicit superior biological responses over porous alumina of similar porosity, promoting enhanced biological interaction, with potential use as non-degradable bone grafts or as implant coatings.

  11. Simplification of Template-free Method to Prepare Polyaniline Nanotubes

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    1 Introduction Conducting polymer nanostructures (e.g.nanotubes or nanofibers) have received considerable attention owing their unique properties and promising applications in technology and nano-devices[1]. Conducting polymer nanostructures can be generally synthesized through "hard" and "soft" template method.Usually an external hard template in a "hard-template" method is required and the post-treatment of removing template is rather tedious."Soft-template" method is advantageous of omitting external...

  12. Conversion of Radiology Reporting Templates to the MRRT Standard.

    Science.gov (United States)

    Kahn, Charles E; Genereaux, Brad; Langlotz, Curtis P

    2015-10-01

    In 2013, the Integrating the Healthcare Enterprise (IHE) Radiology workgroup developed the Management of Radiology Report Templates (MRRT) profile, which defines both the format of radiology reporting templates using an extension of Hypertext Markup Language version 5 (HTML5), and the transportation mechanism to query, retrieve, and store these templates. Of 200 English-language report templates published by the Radiological Society of North America (RSNA), initially encoded as text and in an XML schema language, 168 have been converted successfully into MRRT using a combination of automated processes and manual editing; conversion of the remaining 32 templates is in progress. The automated conversion process applied Extensible Stylesheet Language Transformation (XSLT) scripts, an XML parsing engine, and a Java servlet. The templates were validated for proper HTML5 and MRRT syntax using web-based services. The MRRT templates allow radiologists to share best-practice templates across organizations and have been uploaded to the template library to supersede the prior XML-format templates. By using MRRT transactions and MRRT-format templates, radiologists will be able to directly import and apply templates from the RSNA Report Template Library in their own MRRT-compatible vendor systems. The availability of MRRT-format reporting templates will stimulate adoption of the MRRT standard and is expected to advance the sharing and use of templates to improve the quality of radiology reports.

  13. Synthesis of RNA oligomers on heterogeneous templates

    Science.gov (United States)

    Ertem, G.; Ferris, J. P.

    1996-01-01

    The concept of an RNA world in the chemical origin of life is appealing, as nucleic acids are capable of both information storage and acting as templates that catalyse the synthesis of complementary molecules. Template-directed synthesis has been demonstrated for homogeneous oligonucleotides that, like natural nucleic acids, have 3',5' linkages between the nucleotide monomers. But it seems likely that prebiotic routes to RNA-like molecules would have produced heterogeneous molecules with various kinds of phosphodiester linkages and both linear and cyclic nucleotide chains. Here we show that such heterogeneity need be no obstacle to the templating of complementary molecules. Specifically, we show that heterogeneous oligocytidylates, formed by the montmorillonite clay-catalysed condensation of actuated monomers, can serve as templates for the synthesis of oligoguanylates. Furthermore, we show that oligocytidylates that are exclusively 2',5'-linked can also direct synthesis of oligoguanylates. Such heterogeneous templating reactions could have increased the diversity of the pool of protonucleic acids from which life ultimately emerged.

  14. Automated Template Quantification for DNA Sequencing Facilities

    Science.gov (United States)

    Ivanetich, Kathryn M.; Yan, Wilson; Wunderlich, Kathleen M.; Weston, Jennifer; Walkup, Ward G.; Simeon, Christian

    2005-01-01

    The quantification of plasmid DNA by the PicoGreen dye binding assay has been automated, and the effect of quantification of user-submitted templates on DNA sequence quality in a core laboratory has been assessed. The protocol pipets, mixes and reads standards, blanks and up to 88 unknowns, generates a standard curve, and calculates template concentrations. For pUC19 replicates at five concentrations, coefficients of variance were 0.1, and percent errors were from 1% to 7% (n = 198). Standard curves with pUC19 DNA were nonlinear over the 1 to 1733 ng/μL concentration range required to assay the majority (98.7%) of user-submitted templates. Over 35,000 templates have been quantified using the protocol. For 1350 user-submitted plasmids, 87% deviated by ≥ 20% from the requested concentration (500 ng/μL). Based on data from 418 sequencing reactions, quantification of user-submitted templates was shown to significantly improve DNA sequence quality. The protocol is applicable to all types of double-stranded DNA, is unaffected by primer (1 pmol/μL), and is user modifiable. The protocol takes 30 min, saves 1 h of technical time, and costs approximately $0.20 per unknown. PMID:16461949

  15. A comparison of the magnetic properties of Ni and Co nanowires deposited in different templates and on different substrates

    Energy Technology Data Exchange (ETDEWEB)

    Yalçın, O., E-mail: o.yalcin@nigde.edu.tr [Department of Physics, Niğde University, 51240 Niğde (Turkey); Kartopu, G. [Centre for Solar Energy Research (CSER), Glyndŵr University, OpTIC, St. Asaph Business Park, St. Asaph, LL17 0JD (United Kingdom); Çetin, H. [Department of Physics, Bozok University, 6600 Yozgat (Turkey); Demiray, A.S.; Kazan, S. [Department of Physics, Gebze Institute of Technology, 41400 Gebze, Kocaeli (Turkey)

    2015-01-01

    Nickel (Ni) and cobalt (Co) nanowire arrays (NWs) grown by electrodeposition in porous nano-templates are studied by the ferromagnetic resonance (FMR) technique at room temperature (RT) by comparing the effects of template type (alumina and polycarbonate) and the deposition substrate (i.e., metallic back contact). The line-width and resonance field of the FMR spectra strongly depends on the orientation of the applied field direction. A model is developed to analyze the spectra in order to extract the magnetic parameters such as g-values, spin–spin relaxation times (T{sub 2}) and uniaxial anisotropy parameters. The experimental FMR spectra and their resonance field values were fitted using the imaginary part of magnetic susceptibility and a dispersion relation of magnetization, including the Bloch–Bloembergen type damping term. The easy axes of magnetization for all Ni and Co NWs were found to be perpendicular to the wire-axis. Surface spin modes have been observed only when pure Au was used as substrate. A discussion will be provided to explain the observed differences in terms of the anisotropic behavior and magnetic parameters of the NWs for different substrates and growth templates.

  16. Effect of ac electrodeposition conditions on the growth of high aspect ratio copper nanowires in porous aluminum oxide templates.

    Science.gov (United States)

    Gerein, Nathan J; Haber, Joel A

    2005-09-22

    The effect of several deposition parameters on the uniformity of copper electrodeposition through the alumina barrier layer into porous aluminum oxide templates grown in sulfuric or oxalic acid was systematically investigated. A fractional factorial design of experiment was conducted to find suitable deposition conditions among the variables: frequency, voltage, pulsed or continuous deposition, electrolyte concentration, and barrier layer thinning voltage. Continuous ac sine wave deposition conditions yielded excellent uniformity of pore-filling but damaged the porous aluminum oxide templates when deposition was continued to grow bulk copper on the surface. Pulsed electrodeposition yielded comparable uniformity of pore-filling and no damage to the porous aluminum oxide templates, even when bulk copper was deposited on them. Further optimization of pulsed deposition conditions was accomplished by comparing square and sine waveforms and pulse polarity. Pulsed square waveforms produced better pore-filling than pulsed sine waveforms. For sine wave depositions, the oxidative/reductive pulse polarity was more efficient than the commonly used reductive/oxidative pulse polarity. For square wave depositions into sulfuric acid grown pores, the reductive/oxidative pulse polarity produces more uniform pore-filling, likely as a result of enhanced resonant tunneling through the barrier layer and reoxidation of copper in faster filling pores.

  17. Polymer templated nickel cobaltate for energy storage★

    Directory of Open Access Journals (Sweden)

    Albohani Shaymaa

    2017-01-01

    Full Text Available In order to take advantage of the increasing sophistication of technology for harnessing renewable energy resources, serious attention must be paid to how to store and re-access this energy. Electrochemical storage, in the guise of batteries, supercapacitors and pseudocapacitors, has attracted much attention as a viable option for enhanced energy storage applications. But in order for these technologies to be implemented successfully we need to find materials that perform better and are relatively easy to synthesise. Bimetallic transition metal oxides are materials that are readily synthesised and may be multifunctional, i.e. have a role at the electrochemical atomic level as well as the device level. In order for these materials to work efficiently in new generation systems based on sodium and lithium they also need to be mesoporous. This can be achieved by trying to find synthetic techniques that produce specific, highly regulated nanostructures or by adding a ‘templating’ agent during the bulk synthesis step. We have investigated the simple hydrothermal preparation of a number of nickel cobaltate (NiCo2O4 materials using polymer templates, eggshell membrane (ESM and poly methyl methacrylate (PMMA, as potential electrode materials for supercapacitors. The ESM was expected to act as a fibrous, random polymeric template while the PMMA should produce a much more ordered material. Electrochemical testing showed that the different templates have led to changes in material morphology and these have resulted in a difference in electrochemical properties. Templated materials increased specific capacitance compared to non-templated and the choice of template could influence the capacitance by as much as 30%.

  18. Substrate-induced coagulation (SIC) of nano-disperse alumina in non-aqueous media: The dispersibility and stability of alumina in N-methyl-2-pyrrolidinone.

    Science.gov (United States)

    Basch, Angelika; Strnad, Simona

    2011-01-20

    This work investigated colloidal properties such as the zeta-potential, the electrophoretic mobilities and the wetting behaviour of alumina dispersed in non-aqueous media. Non-aqueous dispersions of alumina were prepared in the solvent N-methyl-2-pyrrolidinone (NMP). The wetting behaviour of alumina in NMP was characterized by the powder contact angle method and the Wilhemy plate method. The behaviour of the dispersion should provide information for the development of a substrate-induced coagulation (SIC) coating process of nano-sized alumina in non-aqeous media. SIC is a dip-coating process that coats pretreated but chemically different surfaces with nano-sized particles. It was found that the anionic surfactant dioctyl sulfosuccinate (AOT) had no stabilizing effect on alumina dispersed in NMP.

  19. Microwave assisted template synthesis of silver nanoparticles

    Indian Academy of Sciences (India)

    K J Sreeram; M Nidhin; B U Nair

    2008-12-01

    Easier, less time consuming, green processes, which yield silver nanoparticles of uniform size, shape and morphology are of interest. Various methods for synthesis, such as conventional temperature assisted process, controlled reaction at elevated temperatures, and microwave assisted process have been evaluated for the kind of silver nanoparticles synthesized. Starch has been employed as a template and reducing agent. Electron microscopy, photon correlation spectroscopy and surface plasmon resonance have been employed to characterize the silver nanoparticles synthesized. Compared to conventional methods, microwave assisted synthesis was faster and provided particles with an average particle size of 12 nm. Further, the starch functions as template, preventing the aggregation of silver nanoparticles.

  20. Templates for Deposition of Microscopic Pointed Structures

    Science.gov (United States)

    Pugel, Diane E.

    2008-01-01

    Templates for fabricating sharply pointed microscopic peaks arranged in nearly regular planar arrays can be fabricated by a relatively inexpensive technique that has recently been demonstrated. Depending on the intended application, a semiconducting, insulating, or metallic film could be deposited on such a template by sputtering, thermal evaporation, pulsed laser deposition, or any other suitable conventional deposition technique. Pointed structures fabricated by use of these techniques may prove useful as photocathodes or field emitters in plasma television screens. Selected peaks could be removed from such structures and used individually as scanning tips in atomic force microscopy or mechanical surface profiling.

  1. Preparation of porous lanthanum phosphate with templates

    Energy Technology Data Exchange (ETDEWEB)

    Onoda, Hiroaki, E-mail: onoda@kpu.ac.jp [Department of Informatics and Environmental Sciences, Faculty of Life and Environmental Sciences, Kyoto Prefectural University, 1-5, Shimogamo Nakaragi-cyo, Sakyo-ku, Kyoto 606-8522 (Japan); Ishima, Yuya [Department of Applied Chemistry, Faculty of Life Sciences, Ritsumeikan University, 1-1-1, Nojihigashi, Kusatsu, Shiga 525-8577 (Japan); Takenaka, Atsushi [Department of Materials Science, Yonago National College of Technology, 4448, Hikona-cho, Yonago, Tottori 683-8502 (Japan); Tanaka, Isao [Department of Materials Science and Engineering, Faculty of Engineering, Kyoto University, Yoshida-Honmachi, Sakyo-ku, Kyoto 606-8501 (Japan)

    2009-08-05

    Malonic acid, propionic acid, glycine, n-butylamine, and urea were added to the preparation of lanthanum phosphate from lanthanum nitrate and phosphoric acid solutions. All additives were taken into lanthanum phosphate particles. The additives that have a basic site were easy to contain in precipitates. The addition of templates improved the specific surface area of lanthanum phosphate. The amount of pore, with radius smaller than 4 nm, increased with the addition of templates. The remained additives had influence on the acidic properties of lanthanum phosphate.

  2. Vertex finding with deformable templates at LHC

    Energy Technology Data Exchange (ETDEWEB)

    Stepanov, N. [European Organization for Nuclear Research, Geneva (Switzerland); Khanov, A. [European Organization for Nuclear Research, Geneva (Switzerland)

    1997-04-11

    We present a novel vertex finding technique. The task is formulated as a discrete-continuous optimisation problem in a way similar to the deformable templates approach for the track finding. Unlike the track finding problem, ``elastic hedgehogs`` rather than elastic arms are used as deformable templates. They are initialised by a set of procedures which provide zero level approximation for vertex positions and track parameters at the vertex point. The algorithm was evaluated using the simulated events for the LHC CMS detector and demonstrated good performance. (orig.).

  3. Protective coating for alumina-silicon carbide whisker composites

    Science.gov (United States)

    Tiegs, Terry N.

    1989-01-01

    Ceramic composites formed of an alumina matrix reinforced with silicon carbide whiskers homogenously dispersed therein are provided with a protective coating for preventing fracture strength degradation of the composite by oxidation during exposure to high temperatures in oxygen-containing atmospheres. The coating prevents oxidation of the silicon carbide whiskers within the matrix by sealing off the exterior of the matrix so as to prevent oxygen transport into the interior of the matrix. The coating is formed of mullite or mullite plus silicon oxide and alumina and is formed in place by heating the composite in air to a temperature greater than 1200.degree. C. This coating is less than about 100 microns thick and adequately protects the underlying composite from fracture strength degradation due to oxidation.

  4. Alumina lightweight ceramics modified with plasma synthesized nanopowders

    Science.gov (United States)

    Zake, I.; Svinka, R.; Svinka, V.; Palcevskis, E.

    2011-12-01

    The aim of this study is to clarify possibilities of using plasma synthesized Al2O3 and SiC nanopowders as additives in alumina lightweight ceramics prepared by slip casting. Each plasma synthesized nanopowder (PSNP) was incorporated in the material by a different method, because of their diverse influence on the properties of slip. Al2O3 PSNP was introduced in the matrix in form of aqueous suspension. SiC nanopowder was added directly to raw materials. Bending strength, bulk density, apparent porosity and thermal shock resistance were determined to evaluate the influence of these additives. The effect of Al2O3 PSNP addition on the properties of material depends on the initial sintering temperature. SiC particles during sintering oxidize into SiO2 and then in the reaction with alumina form mullite. Addition of SiC considerably improves bending strength and thermal shock resistance.

  5. Epitaxial growth of tungsten nanoparticles on alumina and spinel surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Rodriguez-Suarez, T; Lopez-Esteban, S; Pecharroman, C; Esteban-Cubillo, A; Moya, J S [Instituto de Ciencia de Materiales de Madrid (ICMM), Consejo Superior de Investigaciones Cientificas (CSIC), C/ Sor Juana Ines de la Cruz 3, 28049, Cantoblanco, Madrid (Spain); Diaz, L A; Torrecillas, R [Nanomaterials and Nanotechnology Research Center (CINN), Consejo Superior de Investigaciones CientIficas (CSIC), C/ Francisco Pintado Fe 26, 33011, Oviedo, Asturias (Spain); Gremillard, L [Universite de Lyon, INSA-Lyon, MATEIS, UMR CNRS 5510, 20 avenue Albert Einstein, Villeurbanne F-69621 (France)], E-mail: jsmoya@icmm.csic.es

    2008-05-28

    Isolated tungsten nanoparticles ({alpha}-W and {beta}-W phase) were synthesized and epitaxially grown on alumina and spinel particle surfaces with an average tungsten size of {<=}20 nm for a low tungsten content (of {<=}1.5 vol%). Using tungsten (VI) ethoxide alcoholic solutions, tungsten trioxide hydrated precursors were attached to a ceramic grains surface as a nanoparticle coating. High-resolution transmission electron microscopy (HRTEM) micrographs showed epitaxial interfaces between alumina, spinel and metallic tungsten. This epitaxial growth is assumed to be due to the effect of water vapour on the sublimation of ortho-tungstic acid during the reduction process in a hydrogen atmosphere. The planes involved in the epitaxy were found to be (22-bar 0){sub Al2O3} parallel (121){sub W} and (311){sub MgAl2O4} parallel (110){sub W}.

  6. Measurements of prompt radiation induced conductivity of alumina and sapphire

    Energy Technology Data Exchange (ETDEWEB)

    Hartman, E. Frederick [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Zarick, Thomas Andrew [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Sheridan, Timothy J. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Preston, Eric F. [ITT Coporation, Colorado Springs, CO (United States)

    2011-04-01

    We performed measurements of the prompt radiation induced conductivity in thin samples of Alumina and Sapphire at the Little Mountain Medusa LINAC facility in Ogden, UT. Five mil thick samples were irradiated with pulses of 20 MeV electrons, yielding dose rates of 1E7 to 1E9 rad/s. We applied variable potentials up to 1 kV across the samples and measured the prompt conduction current. Analysis rendered prompt conductivity coefficients between 1E10 and 1E9 mho/m/(rad/s), depending on the dose rate and the pulse width for Alumina and 1E7 to 6E7 mho/m/(rad/s) for Sapphire.

  7. Preparation of zirconia-alumina powder by co-precipitation

    Institute of Scientific and Technical Information of China (English)

    2000-01-01

    A zirconia-alumina powder with a near spherical shape and an average size of 0.1 ~ 0.2μm was prepared byco-precipitation. XRD analysis shows that α-Al2O3 phase may be directly transformed from amorphous in calcining the hydroxide composite. The ZrO2-Al2O3 composite ceramics manufactured from this powder has the maximum fracture toughness of 9 M Pa·m- 1/2 at 15 % ZrO2 and 740 MPa fracture strength at 5 % ZrO2. Zirconia grains about 1 μm in diameter aredispersed uniformly in the alumina ceramic matrix

  8. Melt processing of Bi--2212 superconductors using alumina

    Science.gov (United States)

    Holesinger, Terry G.

    1999-01-01

    Superconducting articles and a method of forming them, where the superconducting phase of an article is Bi.sub.2 Sr.sub.2 CaCu.sub.2 O.sub.y (Bi-2212). Alumina is combined with Bi-2212 powder or Bi-2212 precursor powder and, in order to form an intimate mixture, the mixture is melted and rapidly cooled to form a glassy solid. The glassy solid is comminuted and the resulting powder is combined with a carrier. An alternative to melting is to form the mixture of nanophase alumina and material having a particle size of less than about 10 microns. The powder, with the carrier, is melt processed to form a superconducting article.

  9. Optical characterization of gold coated over nanostructured alumina films

    Science.gov (United States)

    Aslan, Mustafa M.

    2014-02-01

    The gold coated over nanostructured alumina (GCON-A) films were investigated for layers' thicknesses and optical properties between 400 and 800 nm wavelength. First GCON-A films were fabricated in three steps: atomic layer deposition of alumina, hot water treatment, and gold deposition. Then, polarization maintained angular reflectance measurements were taken with a spectroscopic ellipsometry. Layer thicknesses, effective refractive indices, and absorption coefficients of films were determined through regression analysis on the ellipsometry data. To investigate the optical properties of the GCON-A films further, reflection measurements were taken by the visible spectroscopy. All these results verify that it is feasible to tune optical properties of the GCON-A films.

  10. Catalyst materials based on plasma-processed alumina nanopowder

    Directory of Open Access Journals (Sweden)

    Dubencovs Konstantins

    2012-01-01

    Full Text Available A platinum catalyst for glycerol oxidation by molecular oxygen has been developed applying the extractive-pyrolytic method and using, as a support, a fine alumina powder with an average particle size of 30-60 nm processed by plasma technology. The extractive-pyrolytic method (EPM allows affixing small amounts of catalytic metals (1-5% with the particle size ranging from several nanometers to several tens of nanometers onto the surface of the support. The prepared material - 4.8 wt. % platinum on nano-sized alumina - can be used as a catalyst for glycerol oxidation by oxygen with conversion up to 84%, in order to produce some organic acids (glyceric and lactic acid with a selectivity of about 60%.

  11. Synthesis of catalysts supported in {gamma}-alumina; Sintese de catalisadores suportados na {gamma}-alumina

    Energy Technology Data Exchange (ETDEWEB)

    Pereira, Luiza Gabriel; Silva, A.J.N.; Santos, I.M.G.; Souza, A.G. [Paraiba Univ, Joao Pessoa, PB (Brazil). Dept. de Quimica. Lab. de Termoquimica e Materiais]. E-mail: luizagaby@yahoo.com.br; Fernandes Junior, V.J.; Araujo, A.S. [Rio Grande do Norte Univ., Natal, RN (Brazil). Dept. de Quimica. Lab. de Combustiveis

    2003-07-01

    Fuels contain a great amount of undesirable pollutants as asphaltenes, metals, sulfides and nitrogen compounds. The content of sulfur in petroleum is around 1%,. When burned, fuels liberate SO{sub x}, the greatest air pollutant . The maximum sulfur quantity in diesel is {approx}350 wppm, but in agreement to European specifications, this content will fall to 50 wppm up to 2005. To remove this sulfur a deep hydrodesulfurization is necessary, requiring high performance catalysts. This way, in this work, the following catalysts were synthesized, using Pechini method: MoO{sub 3} containing Ni and/or Co supported on {gamma}-alumina, with the formulas Co{sub x}Mo{sub 1-x}O{sub 3}/Al{sub 2}O{sub 3}, Ni{sub x}Mo{sub 1-x}O{sub 3}/Al{sub 2}O{sub 3} and Ni{sub x/2}Co{sub x/2}Mo{sub 1-x}O{sub 3}/Al{sub 2}O{sub 3} where x 0,01, 0,02 and 0,03 in mol percentage. This method was proposed, due to its high stoichiometry control, purity, reproducibility and homogeneity. All catalysts were submitted to thermal treatment at 500 deg C to 700 deg C and characterized by thermogravimetry, infrared spectroscopy, X-ray diffraction. Results indicate the stabilization of the requested composition at around 622 deg C. The X-ray diffraction results indicate that secondary phase increases with dopant amount. (author)

  12. MICROWAVE JOINING OF ALUMINA CERAMIC AND HYDROXYLAPATITE BIOCERAMIC

    Institute of Scientific and Technical Information of China (English)

    1999-01-01

    Microwave joining is a rapid developmental new techniqu e in recent years.This paper introduces a new microwave joining equipment which was made by our lab,succeeds in alumina ceramic-hydroxylapatite bioceramic j o in in the equipment, and analyzes the join situation of join boundary by using s canni ng electron microscope(SEM),this paper analyzes the mechanism of microwave joini ng also.

  13. Single Crystal Structure Determination of Alumina to 1 Mbar

    Science.gov (United States)

    Dong, H.; Zhang, L.; Prakapenka, V.; Mao, H.

    2014-12-01

    Aluminum oxide (Al2O3) is an important ceramic material and a major oxide in the earth. Additionally, alumina is a widely used pressure standard in static high-pressure experiments (Cr3+-bearing corundum, ruby). The changes of its crystal structure with pressure (P) and temperature (T) are important for its applications and understanding its physical properties in the deep Earth. There have been numerous reports on the high P-T polymorphs of alumina. Previous theoretical calculations and experiments suggest that the crystal structure of Al2O3 evolves greatly at high P-T. In this study, we used the newly developed multigrain crystallography method combined with single-crystal x-ray diffraction analysis technique for the structure determination of alumina at high P-T to provide single-crystal structure refinement for high-pressure phases of Al2O3. Alumina powder was mixed with ~10% Pt and Ne was used as both pressure transmitting media and thermal insulating layers during laser-heating. Coarse-grained aggregates of Al2O3 were synthesized in a laser-heated diamond anvil cell. The structure change of Al2O3 was monitored by in situ x-ray diffraction at ~1 Mbar and 2700 K. The results allow us to distinguish the structural differences between the Rh2O3 (II) structure (space group Pbcn) and perovskite structure (space group Pbnm) for the first high-pressure phase of Al2O3. More detailed results will be discussed in the later work.

  14. Ion irradiation effect of alumina and its luminescence

    Energy Technology Data Exchange (ETDEWEB)

    Aoki, Yasushi; Yamamoto, Shunya; Naramoto, Hiroshi [Japan Atomic Energy Research Inst., Takasaki, Gunma (Japan). Takasaki Radiation Chemistry Research Establishment; My, N.T.

    1997-03-01

    The luminescence spectra of single crystalline alpha-alumina and ruby which has 0.02% of Cr{sub 2}O{sub 3} as a impurity, induced by 200 keV He{sup +} and Ar{sup +} irradiation were measured at room temperature as a function of irradiation dose. The analysis of the measured spectra showed the existence of three main luminescence features in the wavelength region of 250 to 350 nm, namely anionic color centers, F-center at 411 nm and F{sup +}-center at 330 nm and a band observed around 315 nm. As alpha-alumina was irradiated with He{sup +}, F-center and F{sup +}-center luminescence grew and decayed, but the behaviors of those were different from each other. It seems that a concentration quenching occurred on the F-center luminescence in the dose range above 1x10{sup 14} He/cm{sup 2}. Furthermore, F-center luminescence was strongly suppressed in ruby, compared with that in alumina. On the other hand, the luminescence band around 315 nm appeared only in the early stage of irradiation and did not show its growth part. The dose dependent behavior was similar to that of Cr{sup 3+} emission at 695 nm (R-line) in ruby in both cases of He{sup +} and Ar{sup +} irradiation. Based on the experimental results mentioned above, the processes of defect formation and excitation in alumina in the early stage of ion irradiation will be discussed. (author)

  15. Friction and Wear of Sintered Alumina at High Temperature

    OpenAIRE

    Senda, Tetsuya; TAKAHASHl, Chiori; UEMATSU, Susumu; Amada, Shigeyasu

    1991-01-01

    The frictional behavior of alumina ceramics was investigated at various temperatures up to 1200℃. The coefficient of friction decreased with increasing temperature and this temperature dependency became more pronounced as higher contact pressures were applied. Wear loss at room temperature could be interpreted as being caused by one of either two different behavior modes. These have a rate difference of a factor of ten. At temperatures higher than 800℃, the wear loss was far less than that at...

  16. Thin alumina and silica films by chemical vapor deposition (CVD)

    OpenAIRE

    Hofman, R.; Morssinkhof, R.W.J.; Fransen, T.; Westheim, J.G.F.; Gellings, P.J.

    1993-01-01

    Alumina and silica coatings have been deposited by MOCVD (Metal Organic Chemical Vapor Deposition) on alloys to protect them against high temperature corrosion. Aluminium Tri-lsopropoxide (ATI) and DiAcetoxyDitertiaryButoxySilane (DAOBS) have been used as metal organic precursors to prepare these ceramic coatings. The influence of several process steps on the deposition rate and surface morphology is discussed. The deposition of SiO2 at atmospheric pressure is kinetically limited below 833 K ...

  17. Results of recent KROTOS FCI tests. Alumina vs. corium melts

    Energy Technology Data Exchange (ETDEWEB)

    Huhtiniemi, I.; Magallon, D.; Hohmann, H. [Commission of the European Communities, Ispra (Italy). Joint Research Center

    1998-01-01

    Recent results from KROTOS fuel-coolant interaction experiments are discussed. Five tests with alumina were performed under highly subcooled conditions, all of these tests resulted in spontaneous steam explosions. Additionally, four tests were performed at low subcooling to confirm, on one hand, the suppression of spontaneous steam explosions under such conditions and, on the other hand, that such a system is still triggerable using an external initiator. The other test parameters in these alumina tests included the melt superheat and the initial pressure. All the tests in the investigated superheat range (150 K - 750 K) produced a steam explosion and no evidence of the explosion suppression by the elevated initial pressure (in the limited range of 0.1 - 0.375 MPa) was observed in the alumina tests. The corium test series include a test with 3 kg of melt under both subcooled and near saturated conditions at ambient pressure. Two additional tests were performed with subcooled water; one test was performed at an elevated pressure of 0.2 MPa with 2.4 kg of melt and another test with 5.1 kg of melt at ambient pressure. None of these tests with corium produced a propagating energetic steam explosion. However, propagating low energy (about twice the energy of the trigger pulse) events were observed. All corium tests produced significantly higher water level swells during the mixing phase than the corresponding alumina tests. Present experimental evidence suggests that the water depletion in the mixing zone suppresses energetic steam explosions with corium melts at ambient pressure and in the present pour geometry. Processes that could produce such a difference in void generation are discussed. (author)

  18. Proton adsorption onto alumina: extension of multisite complexation (MUSIC) theory

    Energy Technology Data Exchange (ETDEWEB)

    Nagashima, K.; Blum, F.D.

    1999-09-01

    The adsorption isotherm of protons onto a commercial {gamma}-alumina sample was determined in aqueous nitric acid with sodium nitrate as a background electrolyte. Three discrete regions could be discerned in the log-log plots of the proton isotherm determined at the solution pH 5 to 2. The multisite complexation (MUSIC) model was modified to analyze the simultaneous adsorption of protons onto various kinds of surface species.

  19. Mullite/SiAlON/alumina composites by infiltration processing

    Energy Technology Data Exchange (ETDEWEB)

    Albano, M.P.; Scian, A.N. [Centro de Tecnologia de Recursos Minerales y Ceramica, Buenos Aires (Argentina)

    1997-01-01

    The formation of mullite/SiAlON/alumina composites was studied by infiltrating a SiAlON/alumina-base composite with two different solutions, followed by thermal treatment. The base composite was prepared from a mixture of tabular Al{sub 2}O{sub 3} grains, fume SiO{sub 2}, and aluminum powders. The mixture was pressed into test bars and nitrided in a nitrogen-gas (N{sub 2}) atmosphere at 1,480 C. The infiltrants were prehydrolyzed ethyl polysilicate solution and ethyl polysilicate-aluminum nitrate solution. The composites were infiltrated under vacuum, cured at 100 C, and precalcined in air at 700 C. This infiltration process was repeated several times to produce bars that had been subjected to multiple infiltrations, then the bars were calcined in a N{sub 2} atmosphere at 1,480 C to obtain mullite/SiAlON/alumina composites. The infiltration process increased the percentage of nitrogenous crystalline and mullite phases in the matrix; therefore, a decrease of the composite microporosity was observed. The infiltration increased the mechanical strength of the composites. Of the two composites, the one produced using prehydrolyzed ethyl polysilicate as the infiltrant had a higher mechanical strength, before and after being subjected to a severe thermal shock.

  20. Intensifying digestion of diaspore and separation of alumina and silica

    Institute of Scientific and Technical Information of China (English)

    李小斌; 彭志宏; 刘桂华; 周秋生

    2003-01-01

    It was found that there lies a linear relationship among the thermodynamic data of complicate inorganic compounds with similar components. A method for estimating the thermodynamic data of complicate compound and a thermodynamic database involving alumina production were developed. It was found that the alumina digestion rate of activated diasporic bauxite by means of heat field increased much due to the structure aberration, i.e, from perfect structure to unstable corundum. The results from thermodynamic calculation and experiments showed that it was feasible for desilication at atmospheric pressure, and the effects on equilibrium concentration of SiO2 included temperature, mole ratio of Na2O/Al2O3 (αk), caustic and Na+ concentration. The technology of desilication of green liquor at atmosphere and separation of alumina and silica in aluminate solution with high concentration were established. The reaction activity of compounds containing silica and the converting law among compounds were studied, and the prototype technology of desilication products by hydrotreatment was also developed.

  1. Zirconia-alumina-nanodiamond composites with gemological properties

    Science.gov (United States)

    Díaz, Luis A.; Montes-Morán, Miguel A.; Peretyagin, Pavel Y.; Vladimirov, Yuriy G.; Okunkova, Anna; Moya, José S.; Torrecillas, Ramón

    2014-02-01

    Nanodiamonds have excellent mechanical and optical properties with a wide range of potential applications as a filler material for nanocomposites. Here, we present a new family of zirconia-alumina-nanodiamond composites using two main processing routes: (1) a colloidal method, and (2) power mixing homogenization. Composites with detonation nanodiamonds quantities ranging within 0.3-5 vol.% followed by a pulsed electrical current sintering at a temperature range from 1,200 to 1,500 °C have been analyzed, and a significant enhancement in mechanical properties, i.e., indentation hardness (16.17 GPa), fracture toughness (15.5 MPa m1/2), and bending strength (1,600 MPa), could be observed. To support these excellent properties, TEM, color, reflectivity, and Raman spectroscopy measurements were also carried out. The microstructure of the composites is very homogeneous with average grain sizes between 200 and 500 nm depending on the processing temperature. Two morphologies are present: (a) intergranular dispersion of alumina grains and nanodiamonds distributed along the grain boundaries of the ZrO2 matrix, and (b) intragranular nano-dispersion of ZrO2 particles with sizes 20-80 nm located inside the alumina grains. In the present article, we show, for the first time in the scientific literature, a continuous palette of gray color gradation of new ceramic materials of metalized colors (white index L* 98-40) for gemological applications.

  2. Environmental Sustainability of the Alumina Industry in Western Europe

    Directory of Open Access Journals (Sweden)

    Valentina Dentoni

    2014-12-01

    Full Text Available The implementation of European policies on environmental protection is enforcing some substantial modifications in the processing methods and technologies traditionally adopted in the alumina industry and, in particular, in the management of the alumina residue produced. The article analyses the evolution of the alumina production and the residue disposal practices in Western Europe. Some critical aspects regarding the legal implementation of the EU Directive on the landfill of waste are highlighted and discussed. With reference to the requirements established for the landfill of non-hazardous waste, a key point is represented by the possibility of reducing the deposit protection measures if the collection and treatment of leachate is not necessary. The flexibility introduced by the Directive is not incorporated into the Italian law; this fact may represent a major issue in the prospect of disposal conversion from wet to dry methods for companies operating in Italy, as it may endanger the economic sustainability of the plants’ upgrade, as well as the opportunity to attract outside investments.

  3. High strength alumina produced by direct coagulation casting

    Energy Technology Data Exchange (ETDEWEB)

    Baader, F.H.; Will, J.; Tieche, D. [Swiss Federal Institute of Technology, Zuerich (Switzerland)

    1995-09-01

    Direct Coagulation Casting is a new colloidal forming technique. Double layer stabilized, concentrated alumina suspensions are solidified by shifting the suspensions pH from 4 towards the isoelectric point at 9 using the in situ enzyme-catalyzed decomposition of urea. This reaction minimizes the repulsive forces between the suspended particles. The remaining, attractive Van der Waals forces form a stiff particle network. Suspensions with low viscosities (0.3 Pa*s, 59 vol%) were prepared at pH 4. Deagglomeration of the suspensions by ball milling reduced the agglomerate size below 5 pm. The coagulation kinetics could be influenced either by the urease concentration or by the suspension temperature. Process variables were established, providing long idle times, which allowed additional filtration and degassing steps. Coagulation was followed by drying and sintering, whereby densities of more than 3.97 g/cm{sup 3}, a 4-point bending strength of 685 MPa (HIPed) and a high reliablility (m = 40) for high purity alumina were achieved. DCC has the potential to improve the reliability of alumina components of complex shape, as well as to avoid expensive molding.

  4. Alumina Based 500 C Electronic Packaging Systems and Future Development

    Science.gov (United States)

    Chen, Liang-Yu

    2012-01-01

    NASA space and aeronautical missions for probing the inner solar planets as well as for in situ monitoring and control of next-generation aeronautical engines require high-temperature environment operable sensors and electronics. A 96% aluminum oxide and Au thick-film metallization based packaging system including chip-level packages, printed circuit board, and edge-connector is in development for high temperature SiC electronics. An electronic packaging system based on this material system was successfully tested and demonstrated with SiC electronics at 500 C for over 10,000 hours in laboratory conditions previously. In addition to the tests in laboratory environments, this packaging system has more recently been tested with a SiC junction field effect transistor (JFET) on low earth orbit through the NASA Materials on the International Space Station Experiment 7 (MISSE7). A SiC JFET with a packaging system composed of a 96% alumina chip-level package and an alumina printed circuit board mounted on a data acquisition circuit board was launched as a part of the MISSE7 suite to International Space Station via a Shuttle mission and tested on the orbit for eighteen months. A summary of results of tests in both laboratory and space environments will be presented. The future development of alumina based high temperature packaging using co-fired material systems for improved performance at high temperature and more feasible mass production will also be discussed.

  5. Nanocarbon-Coated Porous Anodic Alumina for Bionic Devices

    Directory of Open Access Journals (Sweden)

    Morteza Aramesh

    2015-08-01

    Full Text Available A highly-stable and biocompatible nanoporous electrode is demonstrated herein. The electrode is based on a porous anodic alumina which is conformally coated with an ultra-thin layer of diamond-like carbon. The nanocarbon coating plays an essential role for the chemical stability and biocompatibility of the electrodes; thus, the coated electrodes are ideally suited for biomedical applications. The corrosion resistance of the proposed electrodes was tested under extreme chemical conditions, such as in boiling acidic/alkali environments. The nanostructured morphology and the surface chemistry of the electrodes were maintained after wet/dry chemical corrosion tests. The non-cytotoxicity of the electrodes was tested by standard toxicity tests using mouse fibroblasts and cortical neurons. Furthermore, the cell–electrode interaction of cortical neurons with nanocarbon coated nanoporous anodic alumina was studied in vitro. Cortical neurons were found to attach and spread to the nanocarbon coated electrodes without using additional biomolecules, whilst no cell attachment was observed on the surface of the bare anodic alumina. Neurite growth appeared to be sensitive to nanotopographical features of the electrodes. The proposed electrodes show a great promise for practical applications such as retinal prostheses and bionic implants in general.

  6. Superhydrophobicity of Bionic Alumina Surfaces Fabricated by Hard Anodizing

    Institute of Scientific and Technical Information of China (English)

    Jing Li; Feng Du; Xianli Liu; Zhonghao Jiang; Luquan Ren

    2011-01-01

    Bionic alumina samples were fabricated on convex dome type aluminum alloy substrate using hard anodizing technique.The convex domes on the bionic sample were fabricated by compression molding under a compressive stress of 92.5 MPa.The water contact angles of the as-anodized bionic samples were measured using a contact angle meter (JC2000A) with the 3 μL water drop at room temperature.The measurement of the wetting property showed that the water contact angle of the unmodified as-anodized bionic alumina samples increases from 90° to 137° with the anodizing time.The increase in water contract angle with anodizing time arises from the gradual formation of hierarchical structure or composite structure.The structure is composed of the micro-scaled alumina columns and pores.The height of columns and the depth of pores depend on the anodizing time.The water contact angle increases significantly from 96° to 152° when the samples were modified with self-assembled monolayer of octadecanethiol (ODT),showing a change in the wettability from hydrophobicity to super-hydrophobicity.This improvement in the wetting property is attributed to the decrease in the surface energy caused by the chemical modification.

  7. Removing Bacillus subtilis from fermentation broth using alumina nanoparticles.

    Science.gov (United States)

    Mu, Dashuai; Mu, Xin; Xu, Zhenxing; Du, Zongjun; Chen, Guanjun

    2015-12-01

    In this study, an efficient separation technology using Al2O3 nanoparticles (NPs) was developed for removing Bacillus subtilis from fermentation broth. The dosage of alumina nanoparticles used for separating B. subtilis increased during the culture process and remained stable in the stationary phase of the culture process. The pH of the culture-broth was also investigated for its effects on flocculation efficiency, and showed an acidic pH could enhance the flocculation efficiency. The attachment mechanisms of Al2O3 NPs to the B. subtilis surface were investigated, and the zeta potential analysis showed that Al2O3 NPs could attach to B. subtilis via electrostatic attachment. Finally, the metabolite content and the antibacterial effect of the fermentation supernatants were detected and did not significantly differ between alumina nanoparticle separation and centrifugation separation. Together, these results indicate a great potential for a highly efficient and economical method for removing B. subtilis from fermentation broth using alumina nanoparticles. Copyright © 2015 Elsevier Ltd. All rights reserved.

  8. Physical Properties of Copper Based MMC Strengthened with Alumina

    Directory of Open Access Journals (Sweden)

    Kaczmar J. W.

    2014-06-01

    Full Text Available The aim of this work is the development of Cu-Al2O3 composites of copper Cu-ETP matrix composite materials reinforced by 20 and 30 vol.% Al2O3 particles and study of some chosen physical properties. Squeeze casting technique of porous compacts with liquid copper was applied at the pressure of 110 MPa. Introduction of alumina particles into copper matrix affected on the significant increase of hardness and in the case of Cu-30 vol. % of alumina particles to 128 HBW. Electrical resistivity was strongly affected by the ceramic alumina particles and addition of 20 vol. % of particles caused diminishing of electrical conductivity to 20 S/m (34.5% IACS. Thermal conductivity tests were performed applying two methods and it was ascertained that this parameter strongly depends on the ceramic particles content, diminishing it to 100 Wm-1K-1 for the composite material containing 30 vol.% of ceramic particles comparing to 400 Wm-1K-1 for the unreinforced copper. Microstructural analysis was carried out using SEM microscopy and indicates that Al2O3 particles are homogeneously distributed in the copper matrix. EDS analysis shows remains of silicon on the surface of ceramic particles after binding agent used during preparation of ceramic preforms.

  9. Thermodynamics of selenium sorption on alumina and montmorillonite

    Directory of Open Access Journals (Sweden)

    Jean-Pierre Morel

    2015-12-01

    Full Text Available The effect of pH and temperature on the thermodynamics of selenium sorption on alumina and montmorillonite was investigated. The equilibrium constants were obtained from batch experiments carried out at 25 and 40°C, under acidic and near to neutral conditions. Microcalorimetry was used to measure directly the enthalpy change upon sorption. These data were analysed by taking into account the different reactions that occur during the sorption process (the acid–base equilibria in the bulk solution on the one hand and the complexation equilibria between surface sites of the solid and solution species on the other hand. This was done using a simple surface model which assumes that the thermodynamic properties of the aluminol surface sites of both alumina and montmorillonite are identical. Two of the considered reactions were found to predominate, one under acidic conditions and one at near neutral pH. The microcalorimetric data allowed to check that the temperature effect on selenium sorption on alumina and montmorillonite can be correctly predicted simply using the above assumption concerning the sorption sites and by applying van’t Hoff relation both to the homogeneous and heterogeneous reactions.

  10. Wear and flexural strength comparisons of alumina/feldspar resin infiltrated dental composites.

    Science.gov (United States)

    Le Roux, A R; Lachman, N; Walker, M; Botha, T

    2008-11-01

    Incorporating a feldspar chemical bond between alumina filler particles is expected to increase the wear-resistant and flexural strength properties. An investigation was carried out to evaluate the influence of the feldspar chemical bonding between alumina filler particles on wear and flexural strength of experimental alumina/feldspar dental composites. It was hypothesized that wear resistance and flexural strength would be significantly increased with increased feldspar mass. Alumina was chemically sintered and bonded with 30% and 60% feldspar mass, silanized and infiltrated with UDMA resin to prepare the dental restorative composite material. Higher wear-resistant characteristics resulted with increased feldspar mass of up to 60% (p 0.05). Feldspar chemical bonding between the alumina particles may improve on the wear-resistance and flexural strength of alumina/feldspar composites.

  11. Formation process of a strong water-repellent alumina surface by the sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Feng Libang, E-mail: lepond@hotmail.com [School of Mechatronic Engineering, Lanzhou Jiaotong University, 88 West Anning Road, Lanzhou 730070 (China); Li Hui; Song Yongfeng; Wang Yulong [School of Mechatronic Engineering, Lanzhou Jiaotong University, 88 West Anning Road, Lanzhou 730070 (China)

    2010-03-01

    A novel strong water-repellent alumina thin film is fabricated by chemically adsorbing stearic acid (STA) layer onto the porous and roughened aluminum film coated with polyethyleneimine (PEI). The formation process and the structure of the strong water-repellent alumina film are investigated by means of contact angle measurement and atomic force microscope (AFM). Results show that the water contact angles for the alumina films increase with the increase of the immersion time in the boiling water, and meanwhile, the roughness of the alumina films increases with the dissolution of the boehmite in the boiling water. Finally, the strong water-repellent film with a high water contact angle of 139.1 deg. is obtained when the alumina films have distinct roughened morphology with some papillary peaks and porous structure. Moreover, both the roughened structure and the hydrophobic materials of the STA endow the alumina films with the strong water-repellence.

  12. Formation process of a strong water-repellent alumina surface by the sol-gel method

    Science.gov (United States)

    Feng, Libang; Li, Hui; Song, Yongfeng; Wang, Yulong

    2010-03-01

    A novel strong water-repellent alumina thin film is fabricated by chemically adsorbing stearic acid (STA) layer onto the porous and roughened aluminum film coated with polyethyleneimine (PEI). The formation process and the structure of the strong water-repellent alumina film are investigated by means of contact angle measurement and atomic force microscope (AFM). Results show that the water contact angles for the alumina films increase with the increase of the immersion time in the boiling water, and meanwhile, the roughness of the alumina films increases with the dissolution of the boehmite in the boiling water. Finally, the strong water-repellent film with a high water contact angle of 139.1° is obtained when the alumina films have distinct roughened morphology with some papillary peaks and porous structure. Moreover, both the roughened structure and the hydrophobic materials of the STA endow the alumina films with the strong water-repellence.

  13. A Study on the Effect of Nano Alumina Particles on Fracture Behavior of PMMA

    Directory of Open Access Journals (Sweden)

    Arezou Sezavar

    2015-04-01

    Full Text Available In the current research, the role of nano-sized alumina on deformation and fracture mechanism of Poly Methyl Methacrylate (PMMA was investigated. For this purpose, PMMA matrix nanocomposite reinforced with different wt% of alumina (i.e., 5, 10 and 15 were fabricated using the compression molding technique. Tensile properties of produced nanocomposites were studied using Zwick Z250 apparatus at cross head speed of about 5 mm/min. In order to specify the role of alumina nanoparticles on deformation and fracture mechanism of PMMA, microscopic evaluation was performed using scanning electron microscope (SEM. The achieved results prove that tensile properties of PMMA depend on alumina wt%. For example, addition of 15 wt% alumina to PMMA causes an increase of about 25% modulus of elasticity. Micrographs taken from the fracture surface of PMMA and its nanocomposites show deformation and fracture mechanism of PMMA changes as alumina is added to it.

  14. The biogeochemical cycle of the adsorbed template. II - Selective adsorption of mononucleotides on adsorbed polynucleotide templates

    Science.gov (United States)

    Lazard, Daniel; Lahav, Noam; Orenberg, James B.

    1988-01-01

    Experimental results are presented for the verification of the specific interaction step of the 'adsorbed template' biogeochemical cycle, a simple model for a primitive prebiotic replication system. The experimental system consisted of gypsum as the mineral to which an oligonucleotide template attaches (Poly-C or Poly-U) and (5-prime)-AMP, (5-prime)-GMP, (5-prime)-CMP and (5-prime)-UMP as the interacting biomonomers. When Poly-C or Poly-U were used as adsorbed templates, (5-prime)-GMP and (5-prime)-AMP, respectively, were observed to be the most strongly adsorbed species.

  15. The biogeochemical cycle of the adsorbed template. II - Selective adsorption of mononucleotides on adsorbed polynucleotide templates

    Science.gov (United States)

    Lazard, Daniel; Lahav, Noam; Orenberg, James B.

    1988-01-01

    Experimental results are presented for the verification of the specific interaction step of the 'adsorbed template' biogeochemical cycle, a simple model for a primitive prebiotic replication system. The experimental system consisted of gypsum as the mineral to which an oligonucleotide template attaches (Poly-C or Poly-U) and (5-prime)-AMP, (5-prime)-GMP, (5-prime)-CMP and (5-prime)-UMP as the interacting biomonomers. When Poly-C or Poly-U were used as adsorbed templates, (5-prime)-GMP and (5-prime)-AMP, respectively, were observed to be the most strongly adsorbed species.

  16. Selective, ultrathin membrane skins prepared by deposition of novel polymer films on porous alumina supports

    Science.gov (United States)

    Balachandra, Anagi Manjula

    Membrane-based separations are attractive in industrial processes because of their low energy costs and simple operation. However, low permeabilities often make membrane processes uneconomical. Since flux is inversely proportional to membrane thickness, composite membranes consisting of ultrathin, selective skins on highly permeable supports are required to simultaneously achieve high throughput and high selectivity. However, the synthesis of defect-free skins with thicknesses less than 50 nm is difficult, and thus flux is often limited. Layer-by-layer deposition of oppositely charged polyelectrolytes on porous supports is an attractive method to synthesize ultrathin ion-separation membranes with high flux and high selectivity. The ion-transport selectivity of multilayer polyelectrolyte membranes (MPMs) is primarily due to Donnan exclusion; therefore increase in fixed charge density should yield high selectivity. However, control over charge density in MPMs is difficult because charges on polycations are electrostatically compensated by charges on polyanions, and the net charge in the bulk of these films is small. To overcome this problem, we introduced a templating method to create ion-exchange sites in the bulk of the membrane. This strategy involves alternating deposition of a Cu2+-poly(acrylic acid) complex and poly(allylamine hydrochloride) on a porous alumina support followed by removal of Cu2+ and deprotonation to yield free -COO- ion-exchange sites. Diffusion dialysis studies showed that the Cl-/SO42-. Selectivity of Cu2+-templated membranes is 4-fold higher than that of membranes prepared in the absence of Cu2+. Post-deposition cross-linking of these membranes by heat-induced amide bond formation further increased Cl-/SO42- selectivity to values as high as 600. Room-temperature, surface-initiated atom transfer radical polymerization (ATRP) provides another convenient method for formation of ultrathin polymer skins. This process involves attachment of

  17. Comparative study on sintered alumina for ballistic shielding application; Estudo comparativo entre aluminas sinterizadas visando aplicacao em blindagem balistica

    Energy Technology Data Exchange (ETDEWEB)

    Melo, Francisco Cristovao Lourenco de; Goncalves, Diniz Pereira [Centro Tecnico Aeroespacial (CTA), Sao Jose dos Campos, SP (Brazil). Inst. de Aeronautica e Espaco

    1997-12-31

    This work presents a development of the armor made from special ceramic materials and kevlar. An experimental investigation was conducted to study the ballistic penetration resistance on three samples taken from sintered alumina: a commercial one and two formulations A and B made in IAE/CTA. The main differences between the two formulations was the grain size and bend resistance. The knowledge of the mechanisms during the penetration and perforation process allowed to apply a ductile composite laminate made form kevlar under the alumina to delay its rupture. The last ballistic test showed how a Weibull`s modulii and other mechanical properties are able to improve ballistic penetration resistance. (author) 3 refs.

  18. Effect of Heat Treatment of the Alumina Powder on the Microstructure and Properties of Coatings

    Directory of Open Access Journals (Sweden)

    Prozorova Mayya

    2015-01-01

    Full Text Available The alumina powder was treated at a high temperature (1000°C. Dense (porosity of less than 2%, solid (1280 ± 30 HV0.3 and wear-resistant coatings based on heat-treated alumina powder were obtained by a multi-chamber detonation sprayer on the steel substrate. The microstructure, microhardness and the wear resistance of the alumina coatings were investigated.

  19. The Effect of Alumina Dispersant Powder on the Workability of Chromia Based Refractory for IGCC Application

    Science.gov (United States)

    Ming, Zhao Jing; Xun, Yang Zheng; Hong, Hwang Kyu; Hwan, Park Sang

    2011-10-01

    The quality of refractory applied on IGCC is a key factor that affects the cost of production. The workability and microstructure of chromia based castable are varied by introducing different type of alumina dispersant powder, such as active alumina powder. In this study, three types of active alumina powder are added to improve the workability. It's proved that the specific surface area and particle size distribution of fine powders in matrix part greatly affect the flow values and microstructures.

  20. Controlling monomer-sequence using supramolecular templates

    OpenAIRE

    ten Brummelhuis, Niels

    2014-01-01

    The transcription and translation of information contained in nucleic acids that has been perfected by nature serves as inspiration for chemists to devise strategies for the creation of polymers with welldefined monomer sequences. In this review the various approaches in which templates (either biopolymers or synthetic ones) are used to influence the monomer-sequence are discussed.

  1. A lightweight approach for biometric template protection

    Science.gov (United States)

    Al-Assam, Hisham; Sellahewa, Harin; Jassim, Sabah

    2009-05-01

    Privacy and security are vital concerns for practical biometric systems. The concept of cancelable or revocable biometrics has been proposed as a solution for biometric template security. Revocable biometric means that biometric templates are no longer fixed over time and could be revoked in the same way as lost or stolen credit cards are. In this paper, we describe a novel and an efficient approach to biometric template protection that meets the revocability property. This scheme can be incorporated into any biometric verification scheme while maintaining, if not improving, the accuracy of the original biometric system. However, we shall demonstrate the result of applying such transforms on face biometric templates and compare the efficiency of our approach with that of the well-known random projection techniques. We shall also present the results of experimental work on recognition accuracy before and after applying the proposed transform on feature vectors that are generated by wavelet transforms. These results are based on experiments conducted on a number of well-known face image databases, e.g. Yale and ORL databases.

  2. Porous and mesh alumina formed by anodization of high purity aluminum films at low anodizing voltage

    Energy Technology Data Exchange (ETDEWEB)

    Abd-Elnaiem, Alaa M., E-mail: alaa.abd-elnaiem@science.au.edu.eg [KACST-Intel Consortium Center of Excellence in Nano-manufacturing Applications (CENA), Riyadh (Saudi Arabia); Physics Department, Faculty of Science, Assiut University, Assiut 71516 (Egypt); Mebed, A.M. [Physics Department, Faculty of Science, Assiut University, Assiut 71516 (Egypt); Department of Physics, Faculty of Science, Al-Jouf University, Sakaka 2014 (Saudi Arabia); El-Said, Waleed Ahmed [Department of Chemistry, Faculty of Science, Assiut University, Assiut 71516 (Egypt); Abdel-Rahim, M.A. [Physics Department, Faculty of Science, Assiut University, Assiut 71516 (Egypt)

    2014-11-03

    Electrochemical oxidation of high-purity aluminum (Al) films under low anodizing voltages (1–10) V has been conducted to obtain anodic aluminum oxide (AAO) with ultra-small pore size and inter-pore distance. Different structures of AAO have been obtained e.g. nanoporous and mesh structures. Highly regular pore arrays with small pore size and inter-pore distance have been formed in oxalic or sulfuric acids at different temperatures (22–50 °C). It is found that the pore diameter, inter-pore distance and the barrier layer thickness are independent of the anodizing parameters, which is very different from the rules of general AAO fabrication. The brand formation mechanism has been revealed by the scanning electron microscope study. Regular nanopores are formed under 10 V at the beginning of the anodization and then serve as a template layer dominating the formation of ultra-small nanopores. Anodization that is performed at voltages less than 5 V leads to mesh structured alumina. In addition, we have introduced a simple one-pot synthesis method to develop thin walls of oxide containing lithium (Li) ions that could be used for battery application based on anodization of Al films in a supersaturated mixture of lithium phosphate and phosphoric acid as matrix for Li-composite electrolyte. - Highlights: • We develop anodic aluminum oxide (AAO) with small pore size and inter-pore distance. • Applying low anodizing voltages onto aluminum film leads to form mesh structures. • The value of anodizing voltage (1–10 V) has no effect on pore size or inter-pore distance. • Applying anodizing voltage less than 5 V leads to mesh structured AAO. • AAO can be used as a matrix for Li-composite electrolytes.

  3. Electromotive force measurements on cells involving beta-alumina solid electrolyte

    Science.gov (United States)

    Choudhury, N. S.

    1973-01-01

    Open-circuit emf measurements have been made to demonstrate that a two-phase, polycrystalline mixture of beta-alumina and alpha-alumina could be used as a solid electrolyte in galvanic cells with reversible electrodes fixing oxygen or aluminum chemical potentials. These measurements indicate that such a two-phase solid electrolyte may be used to monitor oxygen chemical potentials as low as that corresponding to Al and Al2O3 coexistence (potentials of about 10 to the minus 47th power atm at 1000 K). The activity of Na2O in beta-alumina in coexistence with alpha-alumina was also determined by emf measurements.

  4. The effect of alumina nanofillers size and shape on mechanical behavior of PMMA matrix composite

    Directory of Open Access Journals (Sweden)

    Ben Hasan Somaya Ahmed

    2014-01-01

    Full Text Available Composites with the addition of alumina nanofillers show improvement in mechanical properties. The PMMA polymer was used as a matrix and two different types of nanofillers, having extremely different shapes were added in the matrix to form the composite. Reinforcements were based on alumina nanoparticles having either spherical shape or whiskers having the length to diameter ratio of 100. The influence of alumina fillers size, shape and fillers loading on mechanical properties of prepared composite were studied using the nanoindentation measurements and dynamic mechanical analysis. It was observed that both alumina whiskers and alumina spherical nanoparticles added in the PMMA matrix improved the mechanical properties of the composite but the improvement was significantly higher with alumina whisker reinforcement. The concentration of the reinforcing alumina spherical nanoparticles and alumina whiskers in PMMA matrix varied up to 5 wt. %. The best performance was obtained by the addition of 3 wt. % of alumina whiskers in the PMMA matrix with regard to mechanical properties of the obtained composite.

  5. On the possibility of producing alumina ceramic with a slight electrical conductivity

    CERN Document Server

    Caspers, Fritz

    1989-01-01

    Antistatic alumina ceramic is desirable for certain particle accelerator applications. In general, highly insulating surface close to a charged particle beam must be avoided in order to prevent the formation of ion pockets and other unwanted electrical effects. For the AA vacuum chamber (UHV), an antistatic ferrite has been produced and successfully installed. The fabrication of antistatic alumina might be possible in a similar way. By using certain metal oxides in the cement, which holds the alumina particles together, a slight conductivity could be obtained after the firing and sintering process, without deteriorating the mechanical and outgassing properties of the alumina compound.

  6. Surface insulating properties of titanium implanted alumina ceramics by plasma immersion ion implantation

    Science.gov (United States)

    Zhu, Mingdong; Song, Falun; Li, Fei; Jin, Xiao; Wang, Xiaofeng; Wang, Langping

    2017-09-01

    The insulating property of the alumina ceramic in vacuum under high voltage is mainly limited by its surface properties. Plasma immersion ion implantation (PIII) is an effective method to modify the surface chemical and physical properties of the alumina ceramic. In order to improve the surface flashover voltage of the alumina ceramic in vacuum, titanium ions with an energy of about 20 keV were implanted into the surface of the alumina ceramic using the PIII method. The surface properties of the as-implanted samples, such as the chemical states of the titanium, morphology and surface resistivity, were characterized by X-ray photoelectron spectroscopy, scanning electron microscope and electrometer, respectively. The surface flashover voltages of the as-implanted alumina samples were measured by a vacuum surface flashover experimental system. The XPS spectra revealed that a compound of Ti, TiO2 and Al2O3 was formed in the inner surface of the alumina sample. The electrometer results showed that the surface resistivity of the implanted alumina decreased with increased implantation time. In addition, after the titanium ion implantation, the maximum hold-off voltage of alumina was increased to 38.4 kV, which was 21.5% higher than that of the unimplanted alumina ceramic.

  7. Templated Self Assemble of Nano-Structures

    Energy Technology Data Exchange (ETDEWEB)

    Suo, Zhigang [Harvard University

    2013-04-29

    This project will identify and model mechanisms that template the self-assembly of nanostructures. We focus on a class of systems involving a two-phase monolayer of molecules adsorbed on a solid surface. At a suitably elevated temperature, the molecules diffuse on the surface to reduce the combined free energy of mixing, phase boundary, elastic field, and electrostatic field. With no template, the phases may form a pattern of stripes or disks. The feature size is on the order of 1-100 nm, selected to compromise the phase boundary energy and the long-range elastic or electrostatic interaction. Both experimental observations and our theoretical simulations have shown that the pattern resembles a periodic lattice, but has abundant imperfections. To form a perfect periodic pattern, or a designed aperiodic pattern, one must introduce a template to guide the assembly. For example, a coarse-scale pattern, lithographically defined on the substrate, will guide the assembly of the nanoscale pattern. As another example, if the molecules on the substrate surface carry strong electric dipoles, a charged object, placed in the space above the monolayer, will guide the assembly of the molecular dipoles. In particular, the charged object can be a mask with a designed nanoscale topographic pattern. A serial process (e.g., e-beam lithography) is necessary to make the mask, but the pattern transfer to the molecules on the substrate is a parallel process. The technique is potentially a high throughput, low cost process to pattern a monolayer. The monolayer pattern itself may serve as a template to fabricate a functional structure. This project will model fundamental aspects of these processes, including thermodynamics and kinetics of self-assembly, templated self-assembly, and self-assembly on unconventional substrates. It is envisioned that the theory will not only explain the available experimental observations, but also motivate new experiments.

  8. Enhanced removal of Cd(II) and Pb(II) by composites of mesoporous carbon stabilized alumina

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Weichun [Department of Environmental Engineering, School of Metallurgy and Environment, Central South University, Lushan South Road 932, Changsha 410017 (China); Chinese National Engineering Research Center for Control & Treatment of Heavy Metal Pollution, Lushan South Road 932, Changsha 410017 (China); Tang, Qiongzhi; Wei, Jingmiao; Ran, Yajun [Department of Environmental Engineering, School of Metallurgy and Environment, Central South University, Lushan South Road 932, Changsha 410017 (China); Chai, Liyuan [Department of Environmental Engineering, School of Metallurgy and Environment, Central South University, Lushan South Road 932, Changsha 410017 (China); Chinese National Engineering Research Center for Control & Treatment of Heavy Metal Pollution, Lushan South Road 932, Changsha 410017 (China); Wang, Haiying, E-mail: haiyw25@163.com [Department of Environmental Engineering, School of Metallurgy and Environment, Central South University, Lushan South Road 932, Changsha 410017 (China); Chinese National Engineering Research Center for Control & Treatment of Heavy Metal Pollution, Lushan South Road 932, Changsha 410017 (China)

    2016-04-30

    Graphical abstract: - Highlights: • Mesoporous carbon stabilized alumina was prepared by one-pot hard-templating method. • MC/Al{sub 2}O{sub 3} showed excellent performance for Cd(II) and Pb(II) adsorption. • Enhanced adsorption was due to the high surface area and special functional groups. - Abstract: A novel adsorbent of mesoporous carbon stabilized alumina (MC/Al{sub 2}O{sub 3}) was synthesized through one-pot hard-templating method. The adsorption potential of MC/Al{sub 2}O{sub 3} for Cd(II) and Pb(II) from aqueous solution was investigated compared with the mesoporous carbon. The results indicated the MC/Al{sub 2}O{sub 3} showed excellent performance for Cd(II) and Pb(II) removal, the adsorption capacity reached 49.98 mg g{sup −1} for Cd(II) with initial concentration of 50 mg L{sup −1} and reached 235.57 mg g{sup −1} for Pb(II) with initial concentration of 250 mg L{sup −1}, respectively. The kinetics data of Cd(II) adsorption demonstrated that the Cd(II) adsorption rate was fast, and the removal efficiencies with initial concentration of 10 and 50 mg L{sup −1} can reach up 99% within 5 and 20 min, respectively. The pseudo-second-order kinetic model could describe the kinetics of Cd(II) adsorption well, indicating the chemical reaction was the rate-controlling step. The mechanism for Cd(II) and Pb(II) adsorption by MC/Al{sub 2}O{sub 3} was investigated by X-ray photoelectron spectroscopy (XPS) and Fourier transformed infrared spectroscopy (FTIR), and the results indicated that the excellent performance for Cd(II) and Pb(II) adsorption of MC/Al{sub 2}O{sub 3} was mainly attributed to its high surface area and the special functional groups of hydroxy-aluminum, hydroxyl, carboxylic through the formation of strong surface complexation or ion-exchange. It was concluded that MC/Al{sub 2}O{sub 3} can be recognized as an effective adsorbent for removal of Cd(II) and Pb(II) in aqueous solution.

  9. Review of Research on Template Methods in Preparation of Nanomaterials

    Directory of Open Access Journals (Sweden)

    Yadian Xie

    2016-01-01

    Full Text Available The nanomaterials have been widely used in various fields, such as photonics, catalysis, and adsorption, because of their unique physical and chemical properties. Therefore, their production methods are of utmost importance. Compared with traditional synthetic methods, the template method can effectively control the morphology, particle size, and structure during the preparation of nanomaterials, which is an effective method for their synthesis. The key for the template method is to choose different templates, which are divided into hard template and soft template according to their different structures. In this paper, the effects of different types of templates on the morphology of nanomaterials during their preparation are investigated from two aspects: hard template and soft template, combined with the mechanism of action.

  10. Emergency department documentation templates: variability in template selection and association with physical examination and test ordering in dizziness presentations

    Directory of Open Access Journals (Sweden)

    Meurer William J

    2011-03-01

    Full Text Available Abstract Background Clinical documentation systems, such as templates, have been associated with process utilization. The T-System emergency department (ED templates are widely used but lacking are analyses of the templates association with processes. This system is also unique because of the many different template options available, and thus the selection of the template may also be important. We aimed to describe the selection of templates in ED dizziness presentations and to investigate the association between items on templates and process utilization. Methods Dizziness visits were captured from a population-based study of EDs that use documentation templates. Two relevant process outcomes were assessed: head computerized tomography (CT scan and nystagmus examination. Multivariable logistic regression was used to estimate the probability of each outcome for patients who did or did not receive a relevant-item template. Propensity scores were also used to adjust for selection effects. Results The final cohort was 1,485 visits. Thirty-one different templates were used. Use of a template with a head CT item was associated with an increase in the adjusted probability of head CT utilization from 12.2% (95% CI, 8.9%-16.6% to 29.3% (95% CI, 26.0%-32.9%. The adjusted probability of documentation of a nystagmus assessment increased from 12.0% (95%CI, 8.8%-16.2% when a nystagmus-item template was not used to 95.0% (95% CI, 92.8%-96.6% when a nystagmus-item template was used. The associations remained significant after propensity score adjustments. Conclusions Providers use many different templates in dizziness presentations. Important differences exist in the various templates and the template that is used likely impacts process utilization, even though selection may be arbitrary. The optimal design and selection of templates may offer a feasible and effective opportunity to improve care delivery.

  11. PENGARUH PERBEDAAN SIFAT PENYANGGA ALUMINA TERHADAP SIFAT KATALIS HYDROTREATING BERBASIS NIKEL-MOLIBDENUM

    Directory of Open Access Journals (Sweden)

    Maria Ulfah

    2012-11-01

    Full Text Available EFFECT OF ALUMINA SUPPORT PROPERTIES ON THE NICKEL-MOLIBDENUM BASE HYDROTREATING CATALYST. Effect of surface characteristics of three species of synthesized γ-alumina (alumina-1, alumina-2 and alumina-3 on characteristics NiMo catalysts has been studied. Those aluminas are derived from boehmite Catapal B by varying rasio mol nitric acid to boehmite. A sol-gel method is used to synthesize γ-Al2O3 support. The Nitrogen adsorption, X-ray diffraction (XRD, Temperature Programmed Reduction (TPR of H2, Temperature Programmed Desorption (TPD of NH3, and mechanical strength are used to characterize the supports and catalysts. The results showed that the surface area alumina affects the formation of crystalline MoO3 in the NiMo catalyst, while γ-Al2O3-3 support which has the highest surface area (about 195 m2/g compared to the other two types of alumina (>195 m2/g does not have a crystalline MoO3. The formation of crystalline MoO3 is not influenced by the acidity alumina. Based on the results of XRD, it is  indicated that the supported alumina-3 NiMo catalyst (having the highest acid strength shows that there is no presence of crystalline MoO3. Pore size distribution of support did not change significantly after the deposition of Ni and Mo oxides. Mechanical strength of support also affects the strength NiMo catalyst. Support alumina-3 which has the highest mechanical strength gives the mechanical strength of the highest NiMo catalyst. Pengaruh sifat penyangga γ-alumina hasil pengembangan (alumina-1, alumina-2 dan alumina-3 pada karakter katalis hydrotreating nikel-molibdenum (NiMo telah dipelajari. Ketiga jenis γ-alumina diturunkan dari boehmite “Catapal B” dengan menvariasikan nisbah mol asam nitrat terhadap boehmite. Pembuatan γ-alumina menggunakan metoda sol-gel. Adsorpsi Nitrogen, X-ray difraksi (XRD, Temperature Programmed Reduction (TPR H2, Temperature Programmed Desorption (TPD NH3, dan kekuatan mekanik digunakan untuk

  12. Business Process Variability : A Tool for Declarative Template Design

    NARCIS (Netherlands)

    Bulanov, P.; Groefsema, H.; Aiello, M.

    2012-01-01

    To lower both implementation time and cost, many Business Process Management tools use process templates to implement highly recurring processes. However, in order for such templates to be used, a process has to adhere substantially to the template. Therefore, current practice for processes which de

  13. Templated electrodeposition of functional nanostructures: nanowires, nanotubes and nanocubes

    NARCIS (Netherlands)

    Maijenburg, Albert Wouter

    2014-01-01

    This thesis is entitled “Templated electrodeposition of functional nanostructures: nanowires, nanotubes and nanocubes”. Templated electrodeposition is the synthesis technique that was used throughout this thesis, and it comprises the use of a template with specific shape and dimensions for the forma

  14. Viscosity of aqueous and cyanate ester suspensions containing alumina nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Lawler, Katherine [Iowa State Univ., Ames, IA (United States)

    2009-01-01

    The viscosities of both aqueous and cyanate ester monomer (BECy) based suspensions of alumina nanoparticle were studied. The applications for these suspensions are different: aqueous suspensions of alumina nanoparticles are used in the production of technical ceramics made by slip casting or tape casting, and the BECy based suspensions are being developed for use in an injection-type composite repair resin. In the case of aqueous suspensions, it is advantageous to achieve a high solids content with low viscosity in order to produce a high quality product. The addition of a dispersant is useful so that higher solids content suspensions can be used with lower viscosities. For BECy suspensions, the addition of nanoparticles to the BECy resin is expected to enhance the mechanical properties of the cured composite. The addition of saccharides to aqueous suspensions leads to viscosity reduction. Through DSC measurements it was found that the saccharide molecules formed a solution with water and this resulted in lowering the melting temperature of the free water according to classic freezing point depression. Saccharides also lowered the melting temperature of the bound water, but this followed a different rule. The shear thinning and melting behaviors of the suspensions were used to develop a model based on fractal-type agglomeration. It is believed that the structure of the particle flocs in these suspensions changes with the addition of saccharides which leads to the resultant viscosity decrease. The viscosity of the BECy suspensions increased with solids content, and the viscosity increase was greater than predicted by the classical Einstein equation for dilute suspensions. Instead, the Mooney equation fits the viscosity behavior well from 0-20 vol% solids. The viscosity reduction achieved at high particle loadings by the addition of benzoic acid was also investigated by NMR. It appears that the benzoic acid interacts with the surface of the alumina particle which may

  15. Viscosity of aqueous and cyanate ester suspensions containing alumina nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Lawler, Katherine [Iowa State Univ., Ames, IA (United States)

    2009-01-01

    The viscosities of both aqueous and cyanate ester monomer (BECy) based suspensions of alumina nanoparticle were studied. The applications for these suspensions are different: aqueous suspensions of alumina nanoparticles are used in the production of technical ceramics made by slip casting or tape casting, and the BECy based suspensions are being developed for use in an injection-type composite repair resin. In the case of aqueous suspensions, it is advantageous to achieve a high solids content with low viscosity in order to produce a high quality product. The addition of a dispersant is useful so that higher solids content suspensions can be used with lower viscosities. For BECy suspensions, the addition of nanoparticles to the BECy resin is expected to enhance the mechanical properties of the cured composite. The addition of saccharides to aqueous suspensions leads to viscosity reduction. Through DSC measurements it was found that the saccharide molecules formed a solution with water and this resulted in lowering the melting temperature of the free water according to classic freezing point depression. Saccharides also lowered the melting temperature of the bound water, but this followed a different rule. The shear thinning and melting behaviors of the suspensions were used to develop a model based on fractal-type agglomeration. It is believed that the structure of the particle flocs in these suspensions changes with the addition of saccharides which leads to the resultant viscosity decrease. The viscosity of the BECy suspensions increased with solids content, and the viscosity increase was greater than predicted by the classical Einstein equation for dilute suspensions. Instead, the Mooney equation fits the viscosity behavior well from 0-20 vol% solids. The viscosity reduction achieved at high particle loadings by the addition of benzoic acid was also investigated by NMR. It appears that the benzoic acid interacts with the surface of the alumina particle which may

  16. Intermetallic strengthened alumina-forming austenitic steels for energy applications

    Science.gov (United States)

    Hu, Bin

    In order to achieve energy conversion efficiencies of >50 % for steam turbines/boilers in power generation systems, materials required are strong, corrosion-resistant at high temperatures (>700°C), and economically viable. Austenitic steels strengthened with Laves phase and Ni3Al precipitates, and alloyed with aluminum to improve oxidation resistance, are potential candidate materials for these applications. The creep resistance of these alloys is significantly improved through intermetallic strengthening (Laves-Fe 2Nb + L12-Ni3Al precipitates) without harmful effects on oxidation resistance. This research starts with microstructural and microchemical analyses of these intermetallic strengthened alumina-forming austenitic steels in a scanning electron microscope. The microchemistry of precipitates, as determined by energy-dispersive x-ray spectroscopy and transmission electron microscope, is also studied. Different thermo-mechanical treatments were carried out to these stainless steels in an attempt to further improve their mechanical properties. The microstructural and microchemical analyses were again performed after the thermo-mechanical processing. Synchrotron X-ray diffraction was used to measure the lattice parameters of these steels after different thermo-mechanical treatments. Tensile tests at both room and elevated temperatures were performed to study mechanical behaviors of this novel alloy system; the deformation mechanisms were studied by strain rate jump tests at elevated temperatures. Failure analysis and post-mortem TEM analysis were performed to study the creep failure mechanisms of these alumina-forming austenitic steels after creep tests. Experiments were carried out to study the effects of boron and carbon additions in the aged alumina-forming austenitic steels.

  17. Kinetic studies of the sucrose adsorption onto an alumina interface

    Science.gov (United States)

    Singh, Kaman; Mohan, Sudhanshu

    2004-01-01

    An account is given of an experimental kinetic study of adsorption of analar reagent sucrose (ARS) onto an alumina interface spectrometrically ( λmax=570 nm) at pH 8.0 and at room temperature. The adsorption isotherm is a typical Langmuirian isotherm (S-type) and adsorption parameters have been deduced according to the Langmuir's model. The adsorption coefficient evaluated from the Langmuir's equation was found to be 2.52×10 2 l mol -1. Adsorption mechanism has been interpreted on the basis of metal-saccharide interaction as found in organometallic compounds and interaction due to negatively charged ends on the disaccharide molecules and positively charge groups on the surface on alumina which depends on the pH value. The effects of variation in experimental conditions of the adsorption system have also been investigated. The adsorption exhibited a typical response to the pH effect and on going towards the PZC the net charge decreases and any reaction making dependence on charge and maximum adsorption (amount) was found near the isoelectric point of alumina (pH 9.0). The presence of ions like Cl -, SO 42- and PO 43- affect the adsorbed amount quantitatively and it seems that these anions compete with sucrose for the positively charged surface sites. The addition of similar concentration of cations was found to reduce the adsorbed amount. The temperature was found to have an inverse effect on adsorption. The additions of catonic and anionic detergents influence both the adsorbed amount and the adsorption rate. The thermodynamics of the titled adsorption model indicates the spontaneous and exothermic nature. The negative value of entropy is an indication of probability of favorable and complex nature of the adsorption.

  18. Carbon Nanotube Templated Asembly of Protein

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Guodong; Lin, Yuehe

    2006-04-01

    This paper describes a novel general strategy for fabricating protein-polyion multilayers by electrostatic layer-by-layer (LBL) self-assembly on a carbon nanotube (CNT) template. Such a noncovalent functionalization method is important for preserving the activity of biomolecules and the mechanical and electrical properties of CNTs. Glucose oxidase and poly (diallydimethylammonium) chloride polymer were used as a model to investigate the LBL process on a CNT template. High-resolution transmission electron microscopy and electrochemical characterization confirm the formation of LBL nanostructures on carboxyl functionalized CNTs. We have also demonstrated the applications of these nanoshell bioreactors to the direct electrochemistry of proteins and biosensing. This strategy can be applied to assemble other biological molecules, such as antibodies, antigens, and DNA, for wide bioassay applications.

  19. Physical synthesis of quantum circuits using templates

    Science.gov (United States)

    Mirkhani, Zahra; Mohammadzadeh, Naser

    2016-10-01

    Similar to traditional CMOS circuits, quantum circuit design flow is divided into two main processes: logic synthesis and physical design. Addressing the limitations imposed on optimization of the quantum circuit metrics because of no information sharing between logic synthesis and physical design processes, the concept of " physical synthesis" was introduced for quantum circuit flow, and a few techniques were proposed for it. Following that concept, in this paper a new approach for physical synthesis inspired by template matching idea in quantum logic synthesis is proposed to improve the latency of quantum circuits. Experiments show that by using template matching as a physical synthesis approach, the latency of quantum circuits can be improved by more than 23.55 % on average.

  20. Metathesis depolymerization for removable surfactant templates.

    Energy Technology Data Exchange (ETDEWEB)

    Zifer, Thomas (Sandia National Laboratories, Livermore, CA); Wheeler, David Roger; Rahimian, Kamayar; McElhanon, James Ross (Sandia National Laboratories, Livermore, CA); Long, Timothy Michael; Jamison, Gregory Marks; Loy, Douglas Anson (Los Alamos National Laboratories, Los Alamos, NM); Kline, Steven R. (National Institute of Standards and Technology, Gaithersburg, MD); Simmons, Blake Alexander (Sandia National Laboratories, Livermore, CA)

    2005-03-01

    Current methodologies for the production of meso- and nanoporous materials include the use of a surfactant to produce a self-assembled template around which the material is formed. However, post-production surfactant removal often requires centrifugation, calcination, and/or solvent washing which can damage the initially formed material architecture(s). Surfactants that can be disassembled into easily removable fragments following material preparation would minimize processing damage to the material structure, facilitating formation of templated hybrid architectures. Herein, we describe the design and synthesis of novel cationic and anionic surfactants with regularly spaced unsaturation in their hydrophobic hydrocarbon tails and the first application of ring closing metathesis depolymerization to surfactant degradation resulting in the mild, facile decomposition of these new compounds to produce relatively volatile nonsurface active remnants.

  1. Deep Human Parsing with Active Template Regression.

    Science.gov (United States)

    Liang, Xiaodan; Liu, Si; Shen, Xiaohui; Yang, Jianchao; Liu, Luoqi; Dong, Jian; Lin, Liang; Yan, Shuicheng

    2015-12-01

    In this work, the human parsing task, namely decomposing a human image into semantic fashion/body regions, is formulated as an active template regression (ATR) problem, where the normalized mask of each fashion/body item is expressed as the linear combination of the learned mask templates, and then morphed to a more precise mask with the active shape parameters, including position, scale and visibility of each semantic region. The mask template coefficients and the active shape parameters together can generate the human parsing results, and are thus called the structure outputs for human parsing. The deep Convolutional Neural Network (CNN) is utilized to build the end-to-end relation between the input human image and the structure outputs for human parsing. More specifically, the structure outputs are predicted by two separate networks. The first CNN network is with max-pooling, and designed to predict the template coefficients for each label mask, while the second CNN network is without max-pooling to preserve sensitivity to label mask position and accurately predict the active shape parameters. For a new image, the structure outputs of the two networks are fused to generate the probability of each label for each pixel, and super-pixel smoothing is finally used to refine the human parsing result. Comprehensive evaluations on a large dataset well demonstrate the significant superiority of the ATR framework over other state-of-the-arts for human parsing. In particular, the F1-score reaches 64.38 percent by our ATR framework, significantly higher than 44.76 percent based on the state-of-the-art algorithm [28].

  2. Multibiometric Systems: Fusion Strategies and Template Security

    Science.gov (United States)

    2008-01-01

    gratitude to Linda Moore, Debbie Kruch, Cathy Davison, Starr Portice, Norma Teague, Kim Thompson, Cathy Sparks, Sue Watson and Adam Pitcher for their...Weighted sum rule Red, Green , Blue channels for face [109] Match score Sum and min rules [166] Feature; match score Feature selection and concatenation...FVC2002-DB2 database, mosaiced template leads to a GAR of 94% and 3The core point was detected using the commercial Neurotechnologija Verifinger software

  3. CPU and GPU (Cuda Template Matching Comparison

    Directory of Open Access Journals (Sweden)

    Evaldas Borcovas

    2014-05-01

    Full Text Available Image processing, computer vision or other complicated opticalinformation processing algorithms require large resources. It isoften desired to execute algorithms in real time. It is hard tofulfill such requirements with single CPU processor. NVidiaproposed CUDA technology enables programmer to use theGPU resources in the computer. Current research was madewith Intel Pentium Dual-Core T4500 2.3 GHz processor with4 GB RAM DDR3 (CPU I, NVidia GeForce GT320M CUDAcompliable graphics card (GPU I and Intel Core I5-2500K3.3 GHz processor with 4 GB RAM DDR3 (CPU II, NVidiaGeForce GTX 560 CUDA compatible graphic card (GPU II.Additional libraries as OpenCV 2.1 and OpenCV 2.4.0 CUDAcompliable were used for the testing. Main test were made withstandard function MatchTemplate from the OpenCV libraries.The algorithm uses a main image and a template. An influenceof these factors was tested. Main image and template have beenresized and the algorithm computing time and performancein Gtpix/s have been measured. According to the informationobtained from the research GPU computing using the hardwarementioned earlier is till 24 times faster when it is processing abig amount of information. When the images are small the performanceof CPU and GPU are not significantly different. Thechoice of the template size makes influence on calculating withCPU. Difference in the computing time between the GPUs canbe explained by the number of cores which they have.

  4. Silicon carbide whisker-zirconia reinforced mullite and alumina ceramics

    Science.gov (United States)

    Becher, Paul F.; Tiegs, Terry N.

    1987-01-01

    The flexural strength and/or fracture toughness of SiC whisker-reinforced composites utilizing mullite or alumina as the matrix material for the composite are increased by the addition of zirconia in a monoclinic or tetragonal phase to the matrix. The zirconia addition also provides for a lower hot-pressing temperature and increases the flexural strength and/or fracture toughness of the SiC whisker-reinforced composites over SiC whisker-reinforced composites of the similar matrix materials reinforced with similar concentrations of SiC whiskers.

  5. Toughening and strengthening mechanism of zirconia-alumina multiphase ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Yu, M.Q.; Fan, S.G. [Research Inst. of Synthetic Crystals, Beijing, BJ (China); Shen, Q.; Zhang, L.M. [Wuhan Univ. of Technology (China)

    2003-07-01

    In the present study, the effect of compositions on the mechanical properties of zirconia-alumina multiphase ceramics was studied. The results showed that with the variety of ZrO{sub 2} content, the change of bending strength and fracture toughness of the multiphase ceramics exhibited a saddle shape which could be divided into three zones: ZTA, ADZ, and Transition zone. The mechanism of toughening and strengthening in each zone was mainly analyzed, and it was found that stress-induced transformation toughening of ZrO{sub 2} and dispersion strengthening of Al{sub 2}O{sub 3} were the two main factors. (orig.)

  6. Optical properties of porous anodic alumina embedded Cu nanocomposite films

    Science.gov (United States)

    Liu, Huiyuan; Sun, Huiyuan; Liu, Lihu; Hou, Xue; Jia, Xiaoxuan

    2015-06-01

    Porous anodic alumina embedded Cu with iridescent colors were fabricated in copper sulfate electrolyte. The films display highly saturated colors after being synthesized by an ac electrodeposition method. Tunable color in the films is obtained by adjusting anodization time, and can be adjusted across the entire visible range. Theoretical results of the changes in the structural color according to the Bragg-Snell formula are consistent with the experimental results. The films could be used in many areas including decoration, display and multifunctional anti-counterfeiting applications.

  7. Development of technology and applications based on porous alumina nanostructures

    OpenAIRE

    Vojkuvka, Lukas

    2009-01-01

    La disertación ha sido organizada de la siguiente manera. En el primer capítulo se presenta el estado del arte, donde se exponen algunos conceptos básicos de las propiedades electroquimicaselectroquímicas del alumino, las fases del crecimiento de los poros y el proceso de auto-ordenación de los mismos. El segundo capítulo de la tesis esta relacionado con la preparación y caracterización morfológica de las muestras de alumina porosa. >En el capítulo 4 se desglosan los resultados obtenidos de l...

  8. Recovery of alumina and some heavy metals from sulfate liquor

    Directory of Open Access Journals (Sweden)

    M.N. El Hazek

    2016-05-01

    Full Text Available The gibbsite bearing shale occurrence in the Paleozoic sedimentary sequence of SW Sinai, Egypt, was found to be associated with several metal values. From sulfate liquor prepared by proper leaching, the recovery of these metal values has been studied. Alumina was first separated in the form of potash alum followed by Cu-selective extraction by hydroxyoxime LIX-973N solvent. Then U recovery using an anionic exchange resin Amberlite IRA-400 was achieved. For the associated heavy metal Zn, it was subsequently extracted using di-2-ethylhexyl phosphoric acid. The relevant factors affecting the extraction process were adequately studied.

  9. Alcohol dehydration: Mechanism of ether formation using an alumina catalyst

    Energy Technology Data Exchange (ETDEWEB)

    Shi, B.; Davis, B.H. [Univ. of Kentucky, Lexington, KY (United States)

    1995-12-01

    Ether formation during the dehydration of secondary alcohols, namely, 2-butanol, 3-pentanol, and 1-cyclopentylethanol, was investigated. Using the proper reaction conditions, the yield of di-2-butyl ether during the dehydration of 2-butanol on alumina can be as high as 40%. That ether is formed by adding an alcohol to the alkene is ruled out by the results from deuterium tracer studies. Results from experiments using S(+)- 2-butanol suggest that the formation of di-2-butyl ether occurs by a S{sub N}2-type mechanism. 33 refs., 5 figs., 3 tabs.

  10. UV NIL template making and imprint evaluation

    Science.gov (United States)

    Sasaki, Shiho; Hiraka, Takaaki; Mizuochi, Jun; Sakai, Yuko; Yusa, Satoshi; Morikawa, Yasutaka; Mohri, Hiroshi; Hayashi, Naoya

    2009-01-01

    UV NIL shows excellent resolution capability with remarkable low line edge roughness, and has been attracting pioneers in the industry who were searching for the finest patterns. We have been focused on the resolution improvement in NIL template making with a 100keV acceleration voltage spot beam EB writer process, and have established a template making process to meet the requirements of the pioneers. Usually such templates needed just a small field (several hundred microns square or so) Now, for several semiconductor devices, the UV NIL is considered not only as a patterning solution for R&D purpose but eventually as a potential candidate for production, and instead of a small field, a full chip field mask is required. Although the 100kV EB writers have excellent resolution capability, they are adopting spot beams (SB) to generate the pattern and have a fatally low throughput if we need full chip writing. In this paper, we are focusing on the 50keV variable shaped beam (VSB) EB writers, which are used in current 4X photomask manufacturing. The 50keV VSB writers can generate full chip pattern in a reasonable time, and by choosing the right patterning material and process, we achieved resolution down to hp28nm, and initial promising results of hp22nm (partial resolution) for line and spaces, and hp26nm for dense holes were observed..

  11. Template learning in morphological neural nets

    Science.gov (United States)

    Davidson, Jennifer L.; Sun, K.

    1991-07-01

    This paper presents an application of morphology neural networks to a template learning problem. Morphology neural networks are a nonlinear version of the familiar artificial neural networks. Typically, an artificial neural net is used to solve pattern classification problems One useful characterization of many neural network algorithms is the ability to 'learn' to respond correctly to new data based only on a selection of known data responses. For example, in the multilayer perceptron model, the 'learning' is a procedure whereby parameters are fed back from output to input neurons and the weights changed to give a better response. The morphological neural net in this paper solves a different type of image processing problem. Specifically, given an input image and an output image which corresponds to a dilated version of the input, one would like to determine what template produced the output. The problem corresponds to teaching the network to solve for the weights in a morphological net, as the weights are the template's values. A reasonable method has been investigated for the boolean case; in this paper results are presented for gray scale images. Image algebra has been shown to provide a succinct expression of neural networks algorithms and also to allow a generalization of neural networks, and thus the authors describe the algorithm in image algebra. The remainder of the paper gives a brief discussion of image algebra, the relationship of image algebra and neural networks, a recap of the dilation morphology neural network boolean for boolean images, and the generalization to grayscale data.

  12. Modification of alumina matrices through chemical etching and electroless deposition of nano-Au array for amperometric sensing

    Directory of Open Access Journals (Sweden)

    Valinčius Gintaras

    2007-01-01

    Full Text Available AbstractSimple nanoporous alumina matrix modification procedure, in which the electrically highly insulating alumina barrier layer at the bottom of the pores is replaced with the conductive layer of the gold beds, was described. This modification makes possible the direct electron exchange between the underlying aluminum support and the redox species encapsulated in the alumina pores, thus, providing the generic platform for the nanoporous alumina sensors (biosensors with the direct amperometric signal readout fabrication.

  13. Development of a PDMS-grafted alumina membrane and its evaluation as solvent resistant nanofiltration membrane

    NARCIS (Netherlands)

    Pinheiro de Melo, A.F.; Hoogendoorn, D.; Nijmeijer, A.; Winnubst, A.J.A.

    2014-01-01

    A new solvent resistant nanofiltration (SRNF) membrane is developed by grafting a PDMS polymer into the pores of a 5 nm γ-alumina ceramic membrane. These PDMS-grafted γ-alumina membranes were attained through a two-step synthesis. The linking agent, 3-aminopropyltriethoxysilane (APTES), was first ap

  14. STUDY OF CATALYTIC CYCLISATION OF (+-CITRONELLAL WITH Zn/γ-ALUMINA AS CATALYST

    Directory of Open Access Journals (Sweden)

    Elvina Dhiaul Iftitah

    2010-06-01

    Full Text Available The reaction of catalytic cyclisation of (+-citronellal has been done using g-alumina and Zn/γ-alumina as catalysts. Zn/γ-alumina catalyst was prepared by impregnation of ZnBr2 into solid of γ-alumina in methanol as a solvent. The calcination process is performed on Muchalal reactor at 400 oC. The reactions were carried out under nitrogen gas atmosphere by mixing 5 mL sample and 1.0 g catalyst at 90-95 oC for 3 hours. The product of reaction was analyzed using GC, FT-IR and GC-MS. The reaction of cyclization of (+-citronellal with γ-alumina catalyst did not give targeted product as well as reaction with Zn/g-alumina catalyst. Whereas, the reactions with Zn/γ-alumina catalyst gave four compounds of isopulegol stereoisomer. Conversion of (--Isopulegol, (+-Neoisopulegol, (+-Isoisopulegol and (+-Neoisoisopulegol  were 64,29%, 18,80%, 9,20% and 3,32% respectively. For that reason, the transformation of (+-sitronelal using Zn/γ-alumina was considered to be the best catalyst. A reaction mechanism is proposed where the (+-citronellal molecule binds to a catalyst Lewis acid site via the aldehyde oxygen and the π-electrons of the double bond. Subsequent protonation of the aldehyde via a neighbouring Bronsted acid site initiates the cyclisation to isopulegol.   Keywords: catalytic cyclisation, impregnation, (+-isopulegol

  15. A Review of Alumina Feeding and Dissolution Factors in Aluminum Reduction Cells

    Science.gov (United States)

    Lavoie, Pascal; Taylor, Mark P.; Metson, James B.

    2016-08-01

    Modern aluminum reduction cells use point feeding technology to replenish alumina as it is consumed by the electrolytic process. The dissolution of alumina has become increasingly difficult to control as the cell sizes and electrolysis intensity have increased. The mass of alumina added per unit time is now much higher than a decade ago, and must take place within a smaller electrolyte mixing volume. In order to replenish the alumina concentration evenly, the alumina needs to be delivered, dispersed, dissolved, and distributed throughout the reduction cell. The dissolution itself follows a 4-step process that can be limited by a multitude of factors. The status of the research on each of these factors is reviewed in the present paper. Although research in laboratory cells has been conducted many times, and the impact of many factors on dissolution has been measured, published observations of alumina feeding on industrial cells are very sparse, especially regarding the dissolution dynamics in the space-time domain and the impact of the feeder hole condition. The present paper therefore presents a qualitative model of the factors governing alumina dissolution in industrial cells and offers the hypothesis that maintenance of the feeder hole condition is central to ensuring alumina dissolution and prevention of sludging.

  16. Morphology and thermal properties of compatibilized PA12/PP blends with boehmite alumina nanofiller inclusions

    CSIR Research Space (South Africa)

    Ogunniran, ES

    2011-12-01

    Full Text Available -1 Morphology and Thermal Properties of Compatibilized PA12/PP Blends with Boehmite Alumina Nanofiller Inclusions 1. Elijah Soba Ogunniran1, 2. Rotimi Sadiku1, 3. Suprakas Sinha Ray2,*, 4. Nyambeni Luruli3 Keywords: ? boehmite alumina; ? morphology...

  17. Polyethyleneglycol grafting of γ-alumina membranes for solvent resistant nanofiltration

    NARCIS (Netherlands)

    Tanardi, C.R.; Catana, Romina; Barboiu, Mihai; Ayral, André; Vankelecom, I.F.J.; Nijmeijer, A.; Winnubst, A.J.A.

    2016-01-01

    A method is presented for grafting mesoporous g-alumina (pore size 5 nm), supported on an a-alumina ceramic membrane, with polyethylene glycols (PEG). The grafting performance of g-Al2O3 powders with various PEG grafting agents, having different molecular weights, alkoxy groups, and ureido functiona

  18. Ge Honglin: Expand and Consolidate Chemical Alumina to Create World Top-class Brand

    Institute of Scientific and Technical Information of China (English)

    2015-01-01

    On June 9,Chinalco convened discussion meeting on integrated utilization of chemical alumina and red mud.Ge Honglin,Chairman and Secretary of the Party Leadership Group of Chinalco,emphasized:"It is imperative to unswervingly expand and consolidate chemical alumina,create world top-class brand,continually propel red mud integrated utilization,and improve integrated utilization rate of resources."

  19. Effect of Calcination on the Sintering of Gel-Derived, Zirconia-Toughened Alumina

    NARCIS (Netherlands)

    Exter, den Peter; Winnubst, Louis; Leuwerink, Theo H.P.; Burggraaf, Anthonie J.

    1994-01-01

    The densification behavior of ZrO2 (+ 3 mol% Y2O3)/85 wt% Al2O3 powder compacts, prepared by the hydrolysis of metal chlorides, can be characterized by a transition- and an α-alumina densification stage. The sintering behavior is strongly determined by the densification of the transition alumina agg

  20. Effect of Microstructure of Composite Powders on Microstructure and Properties of Microwave Sintered Alumina Matrix Ceramics

    Institute of Scientific and Technical Information of China (English)

    Hanmin Bian; Yong Yang; You Wang; Wei Tian; Haifu Jiang; Zhijuan Hu; Weimin Yu

    2013-01-01

    Two kinds of different structured alumina-titania composite powders were used to prepare alumina matrix ceramics by microwave sintering.One was powder mixture of alumina and titania at a micron-submicron level,in which fused-and-crushed alumina particles (micrometers) was clad with submicron-sized titania.The other was powder mixture of alumina and titania at nanometer-nanometer level,in which nano-sized alumina and nano-sized titania particles were homogeneously mixed by ball-milling and spray dried to prepare spherical alumina-titania composite powders.The effect of the microstructure of composite powders on microstructure and properties of microwave sintered alumina matrix ceramics were investigated.Nano-sized composite (NC) powder showed enhanced sintering behavior compared with micro-sized composite (MC) powders.The asprepared NC ceramic had much denser,finer and more homogenous microstructure than MC ceramic.The mechanical properties of NC ceramic were significantly higher than that of MC ceramic,e.g.the flexural strength,Vickers hardness and fracture toughness of NC ceramic were 85.3%,130.3% and 25.7% higher than that of MC ceramic,respectively.The improved mechanical properties of NC ceramic compared with that of MC ceramic were attributed to the enhanced densification and the finer and more homogeneous microstruc.ture through the use of the nanostructured composite powders.

  1. Nanostructural characterization of large-scale porous alumina fabricated via anodizing in arsenic acid solution

    Science.gov (United States)

    Akiya, Shunta; Kikuchi, Tatsuya; Natsui, Shungo; Suzuki, Ryosuke O.

    2017-05-01

    Anodizing of aluminum in an arsenic acid solution is reported for the fabrication of anodic porous alumina. The highest potential difference (voltage) without oxide burning increased as the temperature and the concentration of the arsenic acid solution decreased, and a high anodizing potential difference of 340 V was achieved. An ordered porous alumina with several tens of cells was formed in 0.1-0.5 M arsenic acid solutions at 310-340 V for 20 h. However, the regularity of the porous alumina was not improved via anodizing for 72 h. No pore sealing behavior of the porous alumina was observed upon immersion in boiling distilled water, and it may be due to the formation of an insoluble complex on the oxide surface. The porous alumina consisted of two different layers: a hexagonal alumina layer that contained arsenic from the electrolyte and a pure alumina honeycomb skeleton. The porous alumina exhibited a white photoluminescence emission at approximately 515 nm under UV irradiation at 254 nm.

  2. Crystallography-Induced Correlations in Pore Ordering of Anodic Alumina Films

    NARCIS (Netherlands)

    Roslyakov, Ilya V.; Koshkodaev, Dmitry S.; Eliseev, Andrei A.; Hermida-Merino, Daniel; Petukhov, Andrei V.; Napolskii, Kirill S.

    2016-01-01

    A crystallographic approach to tailoring the morphology and ordering degree of the porous structure of alumina films obtained by anodization of single-crystalline aluminum is discussed. The examination of porous structure of anodic alumina films formed on low-index and vicinal planes of Al single cr

  3. Synthesis and characterization of alumina application in support of zeolite membrane; Sintese e caracterizacao de alumina para aplicacao com o suporte de membrana zeolitica

    Energy Technology Data Exchange (ETDEWEB)

    Barbosa, A.S.; Rodrigues, M.G.F., E-mail: antoniellybarbosa@yahoo.com.br [Universidade Federal de Campina Grande (UFCG), PB (Brazil). Unidade Academica de Engenharia Quimica

    2012-07-01

    Much interest has been aroused in process applications using zeolite membrane. The physicochemical properties of the support have a strong effect on the quality of zeolite membrane. This work is to synthesize and characterize alumina for use as a support for zeolite membrane. In this work was synthesized α-alumina: 40% alumina, 0.2% for PABA, 0.5% oleic acid and 59.3% ethyl alcohol. The mixture was ground in ball mill and placed in an oven for 24 hours at 60 °C, allowed to stand for 24h. The pressing was performed with 4 tons. The pressed material was subjected to sintering at 1400 °C/hour. The samples were characterized by EDX, XRD and SEM. The results for the media by XRD showed that they are crystalline and pure. By EDX was observed that the supports consist essentially of alumina. (author)

  4. Synthesis of alumina-α using chemical and activation energy por microwave; Sintese de alumina-α utilizando ativacao quimica e energia por microondas

    Energy Technology Data Exchange (ETDEWEB)

    Cartaxo, J.M.; Galdino, M.N.; Neves, G.A., E-mail: juliana@dema.ufcg.edu.br [Universidade Federal de Campina Grande (DEMA/UFCG), PB (Brazil). Unidade Academica de Engenharia de Materiais; Campos, L.F.A.; Menezes, R.R. [Universidade Federal da Paraiba (UFPB), PB (Brazil). Dept. de Engenharia de Materiais; Kiminami, R.H.G.A. [Universidade Federal de Sao Carlos (UFSC), SP (Brazil)

    2012-07-01

    With the great technological advances of alumina, this study aimed to synthesize the α-alumina and chemical activation using microwave energy from aluminum nitrate precursor. The synthesized powders were characterized by X-ray diffraction, thermal analysis (DTA and TGA) and surface area by BET. The chemical activation process was conducted by varying the concentration of the acid solution and exposure time of the material solution. The results proved the effectiveness of chemical activation by accelerating the synthesis process. The results of thermal analysis can observe the thermal decomposition temperature and the possible nucleation of new phases of alumina. The results of X-ray diffraction showed that the powders have the structure of α-alumina with specific areas ranging from 3 to 15m{sup 2}/g pore diameters between 190 to 485nm. (author)

  5. Microstructure-mechanical behaviour relationship in alumina-calcium exaluminate composites; Relaciones microestructura-comportamiento mecanico en materiales de alumina-hexaluminato calcico

    Energy Technology Data Exchange (ETDEWEB)

    Sanchez-Herencia, A. J.; Moreno, R.; Baudin, C.

    2001-07-01

    The grain growth behaviour of dense alumina materials has been modified by the addition of calcium hexaluminate particles. Maximum dispersion has been obtained by colloidal processing routes. The influence of sintering temperature (1500-1600 degree centigree) on the size and shape of the alumina grains has been established. The mechanical behaviour of three composite materials with the same composition ({approx}10 vol% CA{sub 6}) and large microstructural differences has been studied in comparison with that of monophasic alumina of the same grain size. The influence of grain size and shape on toughness has been established. R-curve behaviour has been detected during fracture of the material with the alumina grains presenting the largest shape factor. (Author) 18 refs.

  6. Converting Basic D3 Charts into Reusable Style Templates.

    Science.gov (United States)

    Harper, Jonathan; Agrawala, Maneesh

    2017-02-07

    We present a technique for converting a basic D3 chart into a reusable style template. Then, given a new data source we can apply the style template to generate a chart that depicts the new data, but in the style of the template. To construct the style template we first deconstruct the input D3 chart to recover its underlying structure: the data, the marks and the mappings that describe how the marks encode the data. We then rank the perceptual effectiveness of the deconstructed mappings. To apply the resulting style template to a new data source we first obtain importance ranks for each new data field. We then adjust the template mappings to depict the source data by matching the most important data fields to the most perceptually effective mappings. We show how the style templates can be applied to source data in the form of either a data table or another D3 chart. While our implementation focuses on generating templates for basic chart types (e.g. variants of bar charts, line charts, dot plots, scatterplots, etc.), these are the most commonly used chart types today. Users can easily find such basic D3 charts on the Web, turn them into templates, and immediately see how their own data would look in the visual style (e.g. colors, shapes, fonts, etc.) of the templates. We demonstrate the effectiveness of our approach by applying a diverse set of style templates to a variety of source datasets.

  7. Interactions of L-alanine with alumina as studied by vibrational spectroscopy.

    Science.gov (United States)

    Garcia, Ana R; de Barros, Ricardo Brito; Fidalgo, Alexandra; Ilharco, Laura M

    2007-09-25

    The interactions of L-alanine with gamma- and alpha-alumina have been investigated by diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS). L-alanine/alumina samples were dried from aqueous suspensions, at 36.5 degrees C, with two amino acid concentrations (0.4 and 0.8 mmol g-1) and at different pH values (1, 6, and 13). The vibrational spectra proved that the nature of L-alanine interactions with both aluminas is the same (hydrogen bonding), although the groups involved depend on the L-alanine form and on alumina surface groups, both controlled by the pH. For samples prepared at pH 1, cationic L-alanine [CH3CH(NH3+)COOH] displaces physisorbed water from alumina, and strong hydrogen bonds are established between the carbonyl groups of alanine, as electron donors, and the surface Al-OH2+ groups of alumina. This occurs at the expense of alanine dimer dissociation and breaking of intramolecular bonds. When samples are prepared at pH 6, the interacting groups are Al-OH2+ and the carboxylate groups of zwitterionic L-alanine [CH3CH(NH3+)COO-]. The affinity of L-alanine toward alumina decreases, as the strong NH3+...-OOC intermolecular hydrogen bonds prevail over the interactions with alumina. Thus, for a load of 0.8 mmol g-1, phase segregation is observed. On alpha-alumina, crystal deposition is even observed for a load of 0.4 mmol g-1. At pH 13, the carboxylate groups of anionic L-alanine [CH3CH(NH2)COO-] are not affected by alumina. Instead, hydrogen bond interactions occur between NH2 and the Al-OH surface groups of the substrate. Complementary N2 adsorption-desorption isotherms showed that adsorption of L-alanine occurs onto the alumina pore network for samples prepared at pH 1 and 13, whereas at pH 6 the amino acid/alumina interactions are not strong enough to promote adsorption. The mesoporous structure and the high specific surface area of gamma-alumina make it a more efficient substrate for adsorption of L-alanine. For each alumina, however, it is

  8. Cellulose extraction from Zoysia japonica pretreated by alumina-doped MgO in AMIMCl.

    Science.gov (United States)

    Liu, Le; Ju, Meiting; Li, Weizun; Jiang, Yang

    2014-11-26

    In this study, alumina-doped MgO was produced as a solid alkali for lignocellulose pretreatment. Pretreatment with alumina-doped MgO disrupted the lignocellulose structure and significantly reduced the lignin content of the Z. japonica. After pretreatment, Z. japonica showed significant solubility in 1-allyl-3-methylimidazolium chloride (AMIMCl). The similar high solubility of pretreated Z. japonica samples by original alumina-doped MgO and used alumina-doped MgO also proved that alumina-doped MgO had strong stability, which can be recycled and used repeatedly. The regenerated cellulose was similar to microcrystalline cellulose according to FTIR and NMR analyses. Compared to microcrystalline cellulose, only the crystallinity of the regenerated cellulose decreased.

  9. Investigation of Mechanical Behavior of Alfa and Gamma Nano- Alumina/ Epoxy Composite Made By Vartm

    Directory of Open Access Journals (Sweden)

    P. Ghabezi

    2016-06-01

    Full Text Available In this paper, the mechanical properties (flexural and tensional modulus and strength are investigated by manufacturing Epoxy/Glass Nano-composite samples with different Nano-particle wt% (Nano-Alumina to find optimum conditions. The alpha and Gamma grade of Nano alumina were added to the epoxy system with the weight percentage of 1, 2, 3, 4, 5 and 6. The experimental results show that the maximum flexural stiffness in Alfa and Gamma Nano-alumina composite is related to 6 wt% and 4 wt% samples, respectively. And the highest tensional stiffness in Alfa and Gamma Nano-alumina composite is related to 4 wt% and 5 wt% samples, respectively. Also the highest toughness for Alfa and Gamma Nano-composites is observed for 4 wt% and 3 wt% samples and in the same way Nano-alumina in grade Alfa with 1 wt% and Gamma with 3 wt% have highest failure strain.

  10. Processing, nano indentation and scratch testing of alumina-coated YTZP

    Energy Technology Data Exchange (ETDEWEB)

    Valle, J.; Anglada, M.; Ferrari, B.; Baudin, C.

    2015-10-01

    In this work, alumina-coated YTZP materials are proposed as means to combine the mechanical reliability of YTZP with the stiffness and hardness of alumina. Additionally, compressive stresses are developed in the alumina coating when cooling from the sintering temperature due to the thermal expansion mismatch between alumina and YTZP. The proposed processing method involves dipping of pre-sintered YTZP specimens in stable alumina suspensions and co-sintering of the dipped specimens. The influence of the processing parameters on the macro and microstructure of the materials has been established. Berkovich indentation has been performed to determine the Young's modulus of the substrates and coatings. The structural integrity of the coatings has been analysed using scratch tests. The Young's modulus. The optimised specimens present high resistance to scratch up to loads of 150 N. (Author)

  11. Robust Mechanical Properties of Electrically Insulative Alumina Films by Supersonic Aerosol Deposition

    Science.gov (United States)

    Lee, Jong-Gun; Cha, You-Hong; Kim, Do-Yeon; Lee, Jong-Hyuk; Lee, Tae-Kyu; Kim, Woo-Young; Park, Jieun; Lee, Dongyun; James, Scott C.; Al-Deyab, Salem S.; Yoon, Sam S.

    2015-08-01

    Electrically insulating alumina films were fabricated on steel substrates using supersonic aerosol deposition and their hardness and scratchability were measured. Alumina particles (0.4-μm diameter) were supersonically sprayed inside a low-pressure chamber using between 1 and 20 nozzle passes. These alumina particles were annealed between 300 and 800 K to determine the temperature's effect on film crystal size (37-41 nm). Smoother surface morphology and increased electrical resistance of the thin films were observed as their thicknesses grew by increasing the number of passes. Resistances of up to 10,000 MΩ demonstrate robust electrical insulation. Significant hardness was measured (1232 hv or 13.33 GPa), but the alumina films could be peeled off with normal loads of 36 and 47 N for films deposited on stainless steel and SKD11 substrates, respectively. High insulation and hardness confirm that these alumina films would make excellent electrical insulators.

  12. Mechanical performance of alumina reinforced with NbC, TiC and WC

    Directory of Open Access Journals (Sweden)

    Wilson Acchar

    2012-12-01

    Full Text Available The incorporation of refractory hard particles in Al2O3-based composites may inhibit grain growth of the matrix, which could significantly contribute to mechanical performance of the composite. The present study aimed to investigate the potential use of NbC as alumina reinforcing material, as an alternative to other carbides such as TiC and WC. Alumina was mixed with a fixed carbide concentration of 30 wt.(% in a ball mill and uniaxially hot-pressed at 1650 ºC under a load of 30 MPa in an inert atmosphere. X-ray diffraction revealed no oxidation products were present after the sintering process. Microstructure analyses indicate a homogeneous carbide distribution in the alumina matrix. Results obtained in this study show that alumina reinforced with NbC is a composite material with properties comparable to those of alumina reinforced with WC and TiC, thereby making it good reinforcing material.

  13. Micromechanics of deformation in porous liquid phase sintered alumina under hertzian contact

    Energy Technology Data Exchange (ETDEWEB)

    DIGIOVANNI,ANTHONY A.; CHAN,HELEN M.; HARMER,MARTIN P.; NIED,HERMAN F.

    2000-05-15

    A series of fine-grained porous alumina samples, with and without a liquid phase, were fabricated in compositions matched closely to commercially available alumina used as a microelectronic substrates. Hertzian indentation on monolithic specimens of the glass-containing samples produced a greater quasi-ductile stress-strain response compared to that observed in the pure alumina. Maximum residual indentation depths, determined from surface profilometry, correlated with the stress-strain results. Moreover, microstructural observations from bonded interface specimens revealed significantly more damage in the form of microcracking and under extreme loading, pore collapse, in the glass-containing specimens. The absence of the typical twin faulting mechanism observed for larger-grained alumina suggests that the damage mechanism for quasi-ductility in these fine-grained porous alumina derived from the pores acting as a stress concentrator and the grain boundary glass phase providing a weak path for short crack propagation.

  14. Bond strength of a resin cement to high-alumina and zirconia-reinforced ceramics : The effect of surface conditioning

    NARCIS (Netherlands)

    Felipe Valandro, Luiz; Ozcan, Mutlu; Bottino, Marco Cicero; Bottino, Marco Antonio; Scotti, Roberto; Della Bona, Alvaro

    2006-01-01

    Purpose: The aim of this study was to evaluate the effect of two surface conditioning methods on the microtensile bond strength of a resin cement to three high-strength core ceramics: high alumina-based (In-Ceram Alumina, Procera AllCeram) and zirconia-reinforced alumina-based (in-Ceram Zirconia) ce

  15. Bond strength of a resin cement to high-alumina and zirconia-reinforced ceramics: The effect of surface conditioning

    NARCIS (Netherlands)

    Valandro, L.F.; Ozcan, M.; Bottino, M.C.; Bottino, M.A.; Scotti, R.; Della Bona, A.

    2006-01-01

    Purpose: The aim of this study was to evaluate the effect of two surface conditioning methods on the microtensile bond strength of a resin cement to three high-strength core ceramics: high alumina-based (In-Ceram Alumina, Procera AllCeram) and zirconia-reinforced alumina-based (in-Ceram Zirconia) ce

  16. Bond strength of a resin cement to high-alumina and zirconia-reinforced ceramics: The effect of surface conditioning

    NARCIS (Netherlands)

    Valandro, L.F.; Ozcan, M.; Bottino, M.C.; Bottino, M.A.; Scotti, R.; Della Bona, A.

    2006-01-01

    Purpose: The aim of this study was to evaluate the effect of two surface conditioning methods on the microtensile bond strength of a resin cement to three high-strength core ceramics: high alumina-based (In-Ceram Alumina, Procera AllCeram) and zirconia-reinforced alumina-based (in-Ceram Zirconia)

  17. A Neonatal Bimodal MR-CT Head Template

    Science.gov (United States)

    Mohtasebi, Mehrana; Abrishami Moghaddam, Hamid; Grebe, Reinhard; Gity, Masoumeh; Wallois, Fabrice

    2017-01-01

    Neonatal MR templates are appropriate for brain structural analysis and spatial normalization. However, they do not provide the essential accurate details of cranial bones and fontanels-sutures. Distinctly, CT images provide the best contrast for bone definition and fontanels-sutures. In this paper, we present, for the first time, an approach to create a fully registered bimodal MR-CT head template for neonates with a gestational age of 39 to 42 weeks. Such a template is essential for structural and functional brain studies, which require precise geometry of the head including cranial bones and fontanels-sutures. Due to the special characteristics of the problem (which requires inter-subject inter-modality registration), a two-step intensity-based registration method is proposed to globally and locally align CT images with an available MR template. By applying groupwise registration, the new neonatal CT template is then created in full alignment with the MR template to build a bimodal MR-CT template. The mutual information value between the CT and the MR template is 1.17 which shows their perfect correspondence in the bimodal template. Moreover, the average mutual information value between normalized images and the CT template proposed in this study is 1.24±0.07. Comparing this value with the one reported in a previously published approach (0.63±0.07) demonstrates the better generalization properties of the new created template and the superiority of the proposed method for the creation of CT template in the standard space provided by MR neonatal head template. The neonatal bimodal MR-CT head template is freely downloadable from https://www.u-picardie.fr/labo/GRAMFC. PMID:28129340

  18. Ordered three-dimensional interconnected nanoarchitectures in anodic porous alumina

    Science.gov (United States)

    Martín, Jaime; Martín-González, Marisol; Fernández, Jose Francisco; Caballero-Calero, Olga

    2014-01-01

    Three-dimensional nanostructures combine properties of nanoscale materials with the advantages of being macro-sized pieces when the time comes to manipulate, measure their properties, or make a device. However, the amount of compounds with the ability to self-organize in ordered three-dimensional nanostructures is limited. Therefore, template-based fabrication strategies become the key approach towards three-dimensional nanostructures. Here we report the simple fabrication of a template based on anodic aluminum oxide, having a well-defined, ordered, tunable, homogeneous 3D nanotubular network in the sub 100 nm range. The three-dimensional templates are then employed to achieve three-dimensional, ordered nanowire-networks in Bi2Te3 and polystyrene. Lastly, we demonstrate the photonic crystal behavior of both the template and the polystyrene three-dimensional nanostructure. Our approach may establish the foundations for future high-throughput, cheap, photonic materials and devices made of simple commodity plastics, metals, and semiconductors. PMID:25342247

  19. Unconventional nanotubes self-assembled in alumina channels: morphology and surface potential of isolated nanostructures at surfaces.

    Science.gov (United States)

    Palermo, Vincenzo; Liscio, Andrea; Talarico, Anna Maria; Zhi, Linjie; Müllen, Klaus; Samorì, Paolo

    2007-06-15

    Synthetic nanographenes have been self-assembled from solution on the surface of nanometric channels of an alumina membrane template. By controlling the interplay between intermolecular and interfacial interactions, the molecules have been adsorbed either 'face-on' or 'edge-on' on the pore's surfaces, leading to the formation of columnar stacks in the latter case. Upon thermal treatment at high temperature, the molecular cross-linking of the columns has been triggered, transforming the delicate supramolecular arrangement into robust carbon nanotubes, with the graphitic planes at predetermined orientations with respect to the tube axis. Scanning force microscopy characterization of single nanotubes deposited from suspensions on mica showed that the nanotubes can self-assemble on flat surfaces adopting preferential alignments which reflect the threefold symmetry of the mica substrate. Kelvin probe force microscopy studies revealed that the nanotubes possess a surface potential much smaller than the work function of both graphite and conventional vacuum-processed nanotubes, providing evidence for their more confined electronic structure.

  20. A Novel Method for Fabricating Double Layers Porous Anodic Alumina in Phosphoric/Oxalic Acid Solution and Oxalic Acid Solution

    Directory of Open Access Journals (Sweden)

    Yanfang Xu

    2016-01-01

    Full Text Available A novel method for fabricating ordered double layers porous anodic alumina (DL-PAA with controllable nanopore size was presented. Highly ordered large pore layer with interpore distance of 480 nm was fabricated in phosphoric acid solution with oxalic acid addition at the potential of 195 V and the small pore layer was fabricated in oxalic acid solution at the potential from 60 to 100 V. Experimental results show that the thickness of large pore layer is linearly correlative with anodizing time, and pore diameter is linearly correlative with pore widening time. When the anodizing potential in oxalic acid solution was adjusted from 60 to 100 V, the small pore layers with continuously tunable interpore distance from 142 to 241 nm and pore density from 1.94×109 to 4.89×109 cm−2 were obtained. And the interpore distance and the pore density of small pore layers are closely correlative with the anodizing potential. The fabricated DL-PAA templates can be widely utilized for fabrication of ordered nanomaterials, such as superhydrophobic or gecko-inspired adhesive materials and metal or semiconductor nanowires.

  1. Interfaces fracas em compósitos de matriz cerâmica de alumina/alumina

    OpenAIRE

    Hablitzel,M.P.; Garcia,D.E.; Hotza,D.

    2011-01-01

    O uso de cerâmicas estruturais é limitado por sua fratura frágil. Compósitos de matriz cerâmica (CMCs) são materiais que possuem reforços estruturais que atuam aumentando a energia necessária para que o material se frature. O presente artigo apresenta uma alternativa para a produção de CMCs em que matriz e fibras são constituídas de alumina. Os mecanismos responsáveis pelo aumento da tenacidade ocorrem devido a uma interfase porosa entre matriz e fibras.

  2. Morphology-controlled electrochemical sensing amaranth at nanomolar levels using alumina

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Yuanyuan [School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074 (China); Gan, Tian [College of Chemistry and Chemical Engineering, Xinyang Normal University, Xinyang 464000 (China); Wan, Chidan [School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074 (China); Wu, Kangbing, E-mail: kbwu@hust.edu.cn [School of Chemistry and Chemical Engineering, Huazhong University of Science and Technology, Wuhan 430074 (China)

    2013-02-18

    Highlights: ► A facile way to tune morphology and sensing properties of alumina was developed. ► Oxidation activities of amaranth on alumina surface were morphology-dependent. ► Alumina microfibers were more active and greatly increased the signal of amaranth. ► Sensitive, rapid, selective and accurate method was developed for amaranth detection. -- Abstract: Different-shaped aluminas were readily prepared via hydrothermal reaction. It was found that the morphology and the electrochemical sensing properties of alumina were heavily dependent on the reaction time. When extending the reaction time from 6 h to 24 h, the obtained alumina samples changed from amorphous bumps to regular microfibers in diameter of 200 nm, as confirmed by scanning electron microscopy. Transmission electron microscopy observation revealed that longer reaction time was beneficial for the formation of porous and uniform fiber-like structures. Electrochemical tests proved that alumina microfibers were more active for the oxidation of amaranth and exhibited much higher enhancement effect, compared with alumina bumps. On the surface of alumina microfibers, the oxidation peak currents of amaranth increased remarkably. The influences of pH value, amount of alumina microfibers, and accumulation time on the signal enhancement of amaranth were discussed. As a result, a novel electrochemical method was developed for the detection of amaranth. The linear range was from 1 to 150 nM, and the detection limit was 0.75 nM after 1-min accumulation. The analytical application in drink samples was investigated, and the results consisted with the values that obtained by high-performance liquid chromatography.

  3. Extraction and characterization of alumina nanopowders from aluminum dross by acid dissolution process

    Science.gov (United States)

    Sarker, Md. Saifur Rahman; Alam, Md. Zahangir; Qadir, Md. Rakibul; Gafur, M. A.; Moniruzzaman, Mohammad

    2015-04-01

    A significant amount of aluminum dross is available as a waste in foundry industries in Bangladesh. In this study, alumina was extracted from aluminum dross collected from two foundry industries situated in Dhamrai and Manikgang, near the capital city, Dhaka. Aluminum dross samples were found to approximately contain 75wt% Al2O3 and 12wt% SiO2. An acid dissolution process was used to recover the alumina value from the dross. The effects of various parameters, e.g., temperature, acid concentration, and leaching time, on the extraction of alumina were studied to optimize the dissolution process. First, Al(OH)3 was produced in the form of a gel. Calcination of the Al(OH)3 gel at 1000°C, 1200°C, and 1400°C for 2 h produced γ-Al2O3, (α+γ)-Al2O3, and α-alumina powder, respectively. Thermal characterization of the Al(OH)3 gel was performed by thermogravimetric/differential thermal analysis (TG/DTA) and differential scanning calorimetry (DSC). The phases and crystallite size of the alumina were determined by X-ray diffraction analysis. The dimensions of the alumina were found to be on the nano level. The chemical compositions of the aluminum dross and alumina were determined by X-ray fluorescence (XRF) spectroscopy. The microstructure and morphology of the alumina were studied with scanning electron microscopy. The purity of the alumina extracted in this study was found to be 99.0%. Thus, it is expected that the obtained alumina powders can be potentially utilized as biomaterials.

  4. Synthesis of magnesium aluminate spinel by periclase and alumina chlorination

    Energy Technology Data Exchange (ETDEWEB)

    Orosco, Pablo, E-mail: porosco@unsl.edu.ar [Instituto de Investigaciones en Tecnología Química (INTEQUI), Chacabuco y Pedernera, San Luis (Argentina); Facultad de Química, Bioquímica y Farmacia, Universidad Nacional de San Luis Chacabuco y Pedernera, San Luis (Argentina); Barbosa, Lucía [Instituto de Investigaciones en Tecnología Química (INTEQUI), Chacabuco y Pedernera, San Luis (Argentina); Instituto de Ciencias Básicas (ICB), Universidad Nacional de Cuyo Parque General San Martín, Mendoza (Argentina); Ruiz, María del Carmen [Instituto de Investigaciones en Tecnología Química (INTEQUI), Chacabuco y Pedernera, San Luis (Argentina); Facultad de Química, Bioquímica y Farmacia, Universidad Nacional de San Luis Chacabuco y Pedernera, San Luis (Argentina)

    2014-11-15

    Highlights: • Use of chlorination for the synthesis of magnesium aluminate spinel. • The reagents used were alumina, periclase and chlorine. • Isothermal and non-isothermal assays were performed in air and Cl{sub 2}–N{sub 2} flows. • The chlorination produced magnesium aluminate spinel at 700 °C. • Selectivity of the chlorination reaction to obtain spinel is very high. - Abstract: A pyrometallurgical route for the synthesis of magnesium aluminate spinel by thermal treatment of a mechanical mixture containing 29 wt% MgO (periclase) and 71 wt% Al{sub 2}O{sub 3} (alumina) in chlorine atmosphere was developed and the results were compared with those obtained by calcining the same mixture of oxides in air atmosphere. Isothermal and non-isothermal assays were performed in an experimental piece of equipment adapted to work in corrosive atmospheres. Both reagents and products were analyzed by differential thermal analysis (DTA), X-ray diffraction (XRD) and X-ray fluorescence (XRF). Thermal treatment in Cl{sub 2} atmosphere of the MgO–Al{sub 2}O{sub 3} mixture produces magnesium aluminate spinel at 700 °C, while in air, magnesium spinel is generated at 930 °C. The synthesis reaction of magnesium aluminate spinel was complete at 800 °C.

  5. Thermochemical Analysis of Molybdenum Thin Films on Porous Alumina.

    Science.gov (United States)

    Lee, Kyoungjin; de Lannoy, Charles-François; Liguori, Simona; Wilcox, Jennifer

    2017-01-12

    Molybdenum (Mo) thin films (thickness thin-film composites were stable below 300 °C but had no reactivity toward gases. Mo thin films showed nitrogen incorporation on the surface as well as in the subsurface at 450 °C, as confirmed by X-ray photoelectron spectroscopy. The reactivity toward nitrogen was diminished in the presence of CO2, although no carbon species were detected either on the surface or in the subsurface. The Mo thin films have a very stable native oxide layer, which may further oxidize to higher oxidation states above 500 °C due to the reaction with the porous anodized alumina substrate. The oxidation of Mo thin films was accelerated in the presence of oxidizing gases. At 600 °C in N2, the Mo thin film on anodized alumina was completely oxidized and may also have been volatilized. The results imply that choosing thermally stable and inactive porous supports and operating in nonoxidizing conditions below 500 °C will likely maintain the stability of the Mo composite. This study provides key information about the chemical and structural stability of a Mo thin film on a porous substrate for future membrane applications and offers further insights into the integrity of thin-film composites when exposed to harsh conditions.

  6. Synthesis of Alumina Thin Films Using Reactive Magnetron Sputtering Method

    Science.gov (United States)

    Angarita, G.; Palacio, C.; Trujillo, M.; Arroyave, M.

    2017-06-01

    Alumina (Al2O3) thin films were deposited on Si (100) by Magnetron Sputtering in reactive conditions between an aluminium target and oxygen 99.99% pure. The plasma was formed employing Argon with an R.F power of 100 W, the dwelling time was 3 hours. 4 samples were produced with temperatures between 350 and 400 ºC in the substrate by using an oxygen flow of 2 and 8 sccm, the remaining parameters of the process were fixed. The coatings and substrates were characterized using Atomic Force Microscopy (AFM), Scanning Electron Microscopy (SEM), X-ray diffraction (XRD) and Energy Dispersive Spectroscopy (EDS) in order to compare their properties before and after deposition. The films thicknesses were between 47 and 70 nm. The results show that at high oxygen flow the alumina structure prevails in the coatings while at lower oxygen flow only aluminum is deposited in the coatings. It was shown that the temperature increases grain size and roughness while decreasing the thicknesses of the coatings.

  7. Oxidation of Alumina-Forming MAX Phases in Turbine Environments

    Science.gov (United States)

    Smialek, James; Garg, Anita; Harder, Bryan; Nesbitt, James; Gabb, Timothy; Gray, SImon

    2017-01-01

    Protective coatings for high temperature turbine components are based on YSZ thermal barriers and oxidation resistant, alumina-forming NiAl or NiCoCrAlY bond coats. Ti2AlC and Cr2AlC MAX phases are thus of special interest because of good oxidation resistance and CTE that can match Al2O3 and YSZ. Their alumina scales grow according to cubic kinetics due to grain growth in the scale, with initial heating dominated by fast TiO2 growth. Protective cubic kinetics are also found in high pressure burner rig tests of MAXthal 211 Ti2AlC, but with reduced rates due to volatile TiO(OH)2 formation in water vapor. YSZ-coatings on bulk Ti2AlC exhibit remarkable durability up to 1300C in furnace tests and at least a 25x life advantage compared to superalloys. At another extreme, Cr2AlC is resistant to low temperature Na2SO4 hot corrosion and exhibits thermal cycling stability bonded to a superalloy disk material. Accordingly, sputtered Cr2AlC coatings on disk specimens prevented hot corrosion detriments on LCF. Breakaway oxidation (Ti2AlC), scale spallation (Cr2AlC), interdiffusion, and processing as coatings still present serious challenges. However the basic properties of MAX phases provide some unusual opportunities for use in high temperature turbines.

  8. Alumina ceramics prepared with new pore-forming agents

    Directory of Open Access Journals (Sweden)

    Zuzana Živcová

    2008-06-01

    Full Text Available Porous ceramics have a wide range of applications at all length scales, ranging from fi ltration membranes and catalyst supports to biomaterials (scaffolds for bone ingrowths and thermally or acoustically insulating bulk materials or coating layers. Organic pore-forming agents (PFAs of biological origin can be used to control porosity, pore size and pore shape. This work concerns the characterization and testing of several less common pore-forming agents (lycopodium, coffee, fl our and semolina, poppy seed, which are of potential interest from the viewpoint of size, shape or availability. The performance of these new PFAs is compared to that of starch, which has become a rather popular PFA for ceramics during the last decade. The PFAs investigated in this work are in the size range from 5 μm (rice starch to approximately 1 mm (poppy seed, all with more or less isometric shape. The burnout behavior of PFAs is studied by thermal analysis, i.e. thermogravimetry and differential thermal analysis. For the preparation of porous alumina ceramics from alumina suspensions containing PFAs traditional slip casting (into plaster molds and starch consolidation casting (using metal molds are used in this work. The resulting microstructures are investigated using optical microscopy, combined with image analysis, as well as other methods (Archimedes method of double-weighing in water, mercury intrusion porosimetry.

  9. DNA repair by RNA: Templated, or not templated, that is the question.

    Science.gov (United States)

    Meers, Chance; Keskin, Havva; Storici, Francesca

    2016-08-01

    Cells are continuously exposed to both endogenous and exogenous sources of genomic stress. To maintain chromosome stability, a variety of mechanisms have evolved to cope with the multitude of genetic abnormalities that can arise over the life of a cell. Still, failures to repair these lesions are the driving force of cancers and other degenerative disorders. DNA double-strand breaks (DSBs) are among the most toxic genetic lesions, inhibiting cell ability to replicate, and are sites of mutations and chromosomal rearrangements. DSB repair is known to proceed via two major mechanisms: homologous recombination (HR) and non-homologous end joining (NHEJ). HR reliance on the exchange of genetic information between two identical or nearly identical DNA molecules offers increased accuracy. While the preferred substrate for HR in mitotic cells is the sister chromatid, this is limited to the S and G2 phases of the cell cycle. However, abundant amounts of homologous genetic substrate may exist throughout the cell cycle in the form of RNA. Considered an uncommon occurrence, the direct transfer of information from RNA to DNA is thought to be limited to special circumstances. Studies have shown that RNA molecules reverse transcribed into cDNA can be incorporated into DNA at DSB sites via a non-templated mechanism by NHEJ or a templated mechanism by HR. In addition, synthetic RNA molecules can directly template the repair of DSBs in yeast and human cells via an HR mechanism. New work suggests that even endogenous transcript RNA can serve as a homologous template to repair a DSB in chromosomal DNA. In this perspective, we will review and discuss the recent advancements in DSB repair by RNA via non-templated and templated mechanisms. We will provide current findings, models and future challenges investigating RNA and its role in DSB repair.

  10. Studies of oxidation of iron nanowires encased in porous aluminium oxide template

    Energy Technology Data Exchange (ETDEWEB)

    Mazeika, Kestutis, E-mail: kestas@ar.fi.lt; Reklaitis, Jonas [Institute of Physics (Lithuania); Jagminas, Arunas [Institute of Chemistry (Lithuania); Baltrunas, Dalis [Institute of Physics (Lithuania)

    2009-02-15

    The transformations of phase composition of iron nanowires deposited into porous alumina template when annealing in the air were studied. The samples of iron nanowires of different diameter (8, 13, 15, 30 nm) were annealed for 1.5 h at temperature up to 600{sup o}C. In addition, for nanowires of 15 nm diameter the dependence of phase composition on annealing time was investigated. The phases were determined by applying Moessbauer spectroscopy. New Fe(II) and Fe(III) contributions to Moessbauer spectra were found and those were indentified as caused by the formation of hercynite FeAl{sub 2}O{sub 4} and (Fe{sub x}Al{sub 1-x}){sub 2}O{sub 3} with small x values (x {<=} 0.15). It has been found that though initially the Fe(II) compound forms rapidly, afterwards its formation rate becomes lower than that of Fe(III) and after longer annealing time the Fe(III) content exceeds Fe(II) one.

  11. Ear Authentication and Template Protection using Bio-key

    Directory of Open Access Journals (Sweden)

    K. Annapurani

    2014-09-01

    Full Text Available Biometric authentication is gaining popularity in the current scenario. Biometric based authentication is the science of using physical or behavioral characteristic for ensuring that the person is the claimed identity. Biometric authentication system is also vulnerable to attacks in various phases. The biometric data stored in the template has to be protected, since variety of attacks like circumvent, covert acquisition affects the normal functioning of the system. An attacker may create new biometric data or steal the template or modify the template. Once the biometric template is compromised then the entire system is lost. So securing biometric template is an important aspect in biometric authentication system. In this study ear biometric template is secured by a new method of generating bio key from the ear fused template. Here the transformed template is stored in the database. During verification phase, for the new biometric sample a bio key is generated. Using this bio key the person is authenticated if the transformed feature generated is matched with the stored one. Hence the template is protected with the bio key. The authenticated person alone can access the system, since the key to decrypt the encrypted template is obtained from the ear trait of the authenticated person. FAR and FRR are used to evaluate the system performance.

  12. Wet chemical synthesis of nickel supported on alumina catalysts; Sintese de catalisadores de niquel suportado em alumina por via umida

    Energy Technology Data Exchange (ETDEWEB)

    Freire, Ranny Rodrigues; Costa, Talita Kenya Oliveira; Morais, Ana Carla da Fonseca Ferreira; Costa, Ana Cristina Figueiredo de Melo; Freitas, Normanda Lino de, E-mail: normanda@ufcg.edu.br [Universidade Federal de Campina Grande (UFCG), PB (Brazil)

    2016-07-01

    Heterogenic catalysts are those found to be in a different phase on the reaction when compared to the reactants and products. Preferred when compared to homogeneous catalysts due to the easiness on which the separation is processed. The objective of this study is to obtain and characterize Alumina based catalysts impregnated with Nickel (Al{sub 2}O{sub 3}), by wet impregnation. The alumina was synthesized by combustion reaction. Before and after the impregnation the catalysts were characterized by X-ray diffraction (XRD), granulometric analysis, the textural analysis will be held by nitrogen adsorption (BET), energy-dispersive X-ray spectroscopy (EDX) and scanning electron microscopy (SEM). The results show a presence of a stable crystalline phase of Al2O3 in all the studied samples and after the impregnation the second phase formed was of NiO and NiAl{sub 2}O{sub 4}. The Al{sub 2}O{sub 3} e Ni/Al{sub 2}O{sub 3} catalysts resulted in clusters with a medium diameter of 18.9 and 14.2 μm, respectively. The catalysts show a medium-pore characteristic (medium pore diameter between 2 and 50 nm), the superficial area to Al{sub 2}O{sub 3} and Ni/Al{sub 2}O{sub 3} catalysts were 8.69 m{sup 2}/g and 5.56 m{sup 2}/g, respectively. (author)

  13. X-ray residual stress measurement of alumina detonation coating. Bakuhatsu yosha alumina himaku no X sen zanryu oryoku sokutei

    Energy Technology Data Exchange (ETDEWEB)

    Tanaka, K.; Mine, N. (Kyoto University, Kyoto (Japan). Faculty of Engineering); Suzuki, K. (Niigata University, Niigata (Japan). Faculty of Engineering); Kawase, R. (Ariake Institute of Technology, Fukuoka (Japan))

    1991-01-15

    Alumina ceramics were coated on mild steel by a detonation gun with different amounts of detonation gas, and residual stresses in coated films were measured by X-ray diffraction from the (844) plane of {gamma}-alumina by Cu-K {alpha} radiation. Cracks and pores were observed on the film surface and cross section. The pore increased and the film bulk density decreased with a decrease in amount of detonation gas, and the mechanical Young {prime} s modulus decreased with an increase in pore. Since strains measured mechanically were those in the film bulk with pores while strains measured by X-ray were average values in only crystalline phases, the X-ray Young {prime} s modulus was larger than the mechanical one. The residual stress in films was a large tensile stress and distributed uniformly in films. The residual tensile stress decreased with an increase in amount of detonation gas, however, it was rather insensitive to the film thickness and surface grinding after coating. 10 refs., 8 figs., 2 tabs.

  14. Rank-based decompositions of morphological templates.

    Science.gov (United States)

    Sussner, P; Ritter, G X

    2000-01-01

    Methods for matrix decomposition have found numerous applications in image processing, in particular for the problem of template decomposition. Since existing matrix decomposition techniques are mainly concerned with the linear domain, we consider it timely to investigate matrix decomposition techniques in the nonlinear domain with applications in image processing. The mathematical basis for these investigations is the new theory of rank within minimax algebra. Thus far, only minimax decompositions of rank 1 and rank 2 matrices into outer product expansions are known to the image processing community. We derive a heuristic algorithm for the decomposition of matrices having arbitrary rank.

  15. The Contextualization of Archetypes: Clinical Template Governance.

    Science.gov (United States)

    Pedersen, Rune; Ulriksen, Gro-Hilde; Ellingsen, Gunnar

    2015-01-01

    This paper is a status report from a large-scale openEHR-based EPR project from the North Norway Regional Health Authority. It concerns the standardization of a regional ICT portfolio and the ongoing development of a new process oriented EPR systems encouraged by the unfolding of a national repository for openEHR archetypes. Subject of interest; the contextualization of clinical templates is governed over multiple national boundaries which is complex due to the dependency of clinical resources. From the outset of this, we are interested in how local, regional, and national organizers maneuver to standardize while applying OpenEHR technology.

  16. Progress of UV-NIL template making

    Science.gov (United States)

    Hiraka, Takaaki; Mizuochi, Jun; Nakanishi, Yuko; Yusa, Satoshi; Sasaki, Shiho; Morikawa, Yasutaka; Mohri, Hiroshi; Hayashi, Naoya

    2009-04-01

    Nano-imprint lithography (NIL) has been counted as one of the lithography candidates for hp32nm node and beyond and has showed excellent resolution capability with remarkable low line edge roughness that is attracting many researchers in the industry who were searching for the finest patterning technology. Therefore, recently we have been focusing on the resolution improvement on the NIL templates with the 100keV acceleration voltage spot beam (SB) EB writer and the 50keV acceleration voltage variable shaped beam (VSB) EB writer. The 100keV SB writers have high resolution capability, but they show fatally low throughput if we need full chip writing. Usually templates for resolution pioneers needed just a small field (several hundred microns square or so), but recently requirements for full chip templates are increasing. For full chip writing, we have also started the resolution improvement with the 50keV VSB writers used in current 4X photomask manufacturing. The 50keV VSB writers could generate full chip pattern in a reasonable time though resolution limits are inferior to that with the 100keV SB writers. In this paper, we will show latest results with both the 100keV SB and the 50keV VSB EB writers. With the 100keV SB EB writer, we have achieved down to hp15nm resolution for line and space pattern, but found that to achieve further improvement, an innovation in pattern generation method or material would be inevitable. With the 50keV VSB EB writer, we have achieved down to hp22nm resolution for line and space pattern. Though NIL has excellent resolution capability, solutions for defect inspection and repair are not clearly shown yet. In this paper, we will show preliminary inspection results with an EB inspection tool. We tested an EB inspection tool by Hermes Microvision, Inc. (HMI), which was originally developed for and are currently used as a wafer inspection tool, and now have been started to seek the application for mask use, using a programmed defect

  17. Template-directed porous electrodes in electroanalysis.

    Science.gov (United States)

    Walcarius, Alain

    2010-01-01

    Nano- and/or macrostructuring of electrode surfaces has recently emerged as a powerful method of improving the performances of electrochemical devices by enhancing both molecular accessibility and rapid mass transport via diffusion, by increasing the electroactive surface area in comparison to the geometric one, and/or by providing confinement platforms for hosting suitable reagents. This brief overview highlights how template technology offers advantages in terms of designing new types of porous electrodes-mostly based on thin films, and functionalized or not-and discusses their use in analytical chemistry via some recent examples from the literature on electrochemical sensors and biosensors.

  18. Infrared radiative properties of alumina up to the melting point: A first-principles study

    Science.gov (United States)

    Yang, J. Y.; Xu, M.; Liu, L. H.

    2016-11-01

    The high thermal emission of alumina dominates the radiative heat transfer of rocket exhaust plume. Yet numerous experimental measurements on radiative properties of alumina at high temperatures vary considerably from each other and cannot provide physical insight into the underlying mechanism. In this work, the ab initio molecular dynamics (AIMD) method and ab initio parameterized Drude model are combined to predict the radiative properties of alumina for temperatures up to 2327 K (the melting point) in the spectral range 1-12 μm. Contributed by different microscopic processes, the optical absorption of alumina in the spectral range 1-4 and 4-12 μm is described by two distinct methods. In the spectral range 4-12 μm, the multi-phonon process mainly contributes to optical absorption and can be simulated by the AIMD method based on the linear response theory. While in the spectral range 1-4 μm, the optical absorption is mainly caused by intrinsic carriers and can be effectively described by the ab initio parameterized Drude model. The first-principles calculations can successfully predict the infrared radiative properties of alumina at high temperatures and well reproduce the literature experiments. Moreover, the theoretical simulations verify that alumina can retain its semiconducting character even in the liquid phase and there emerges sharp increase in the near-infrared optical absorption of alumina upon melting.

  19. Properties of micro-nano particle size admixtures of alumina at different sintering condition

    Science.gov (United States)

    Sifat, Rahin; Akter, Manira; Rashid, A. K. M. Bazlur

    2016-07-01

    Among various ceramic materials, alumina is mostly used material for its hardness and strength. There is a difference between the properties of alumina due to their different particle size. Also different holding time in the sintering temperature has effect on the sintering of alumina of different particle size. In this study, micro alumina and nano alumina were mixed in different ratios and sintered at different sintering condition to compare their mechanical properties that varied due to their different particle size distribution. In this work, conventional solid state sintering route was followed to prepare final samples. Six different particle size ratio of alumina (micro:nano= 100:0, 95:5, 90:10, 10:90, 5:95, 0:100) with a doping of 0.1% MgO were used. The sintering temperature was 1500° C but sintering condition was different. After comparing the mechanical properties, it has been observed that relatively improved properties can be obtained by increasing nano particle percentages in the micro alumina than the reverse mixture.

  20. [Characterization of alumina adobe and sintered body of GI-infiltrated ceramic].

    Science.gov (United States)

    Wang, H; Chao, Y; Liao, Y; Liang, X; Zhu, Z; Gao, W

    2001-06-01

    This study was conducted to elucidate the mechanism of formation of porous structure by investigating the porosity of the alumina adobe and sintered body of GI-II Infiltrate Ceramic, and its role in strengthening and toughening this kind of ceramic composite. The alumina powder size-mass distribution was obtained by BI-XDC powder size analysis device; the open pore parameters of alumina adobe and sintered body were analyzed using the mercury pressure method. Their fracture surfaces were observed under scanning electronic microscope. Fine powder had two main size groups of 0.09-0.1 micron and 0.2-0.5 micron, respectively, and coarse powder, with size between 1.5 to 4.5 microns, occupied the majority of powder mass. Alumina adobe's pores became larger after sintering. The median pore radii of adobe and sintered body were 0.2531 micron and 0.3081 micron, respectively; the average pore radii changed from 0.0956 micron to 0.1102 micron. Under scanning electronic microscope, fine alumina powders were fused partially together and their surfaces were blunted, but coarse powders did not show such phenomena. The alumina size distribution contributes to the formation of porous structure of alumina sintered body. This porous structure is not only the shape skeleton but also the mechanical skeleton of GI-II Infiltrated Ceramic. It plays an important role in raising the mechanical properties of this kind of ceramic composite.

  1. Preparation and electrochemical performance of sulfur-alumina cathode material for lithium-sulfur batteries

    Energy Technology Data Exchange (ETDEWEB)

    Dong, Kang [Faculty of Material Science and Chemistry, China University of Geosciences, 388 Lumo Road, 430074 Wuhan (China); Wang, Shengping, E-mail: spwang@cug.edu.cn [Faculty of Material Science and Chemistry, China University of Geosciences, 388 Lumo Road, 430074 Wuhan (China); Zhang, Hanyu; Wu, Jinping [Faculty of Material Science and Chemistry, China University of Geosciences, 388 Lumo Road, 430074 Wuhan (China)

    2013-06-01

    Highlights: ► Micron-sized alumina was synthesized as adsorbent for lithium-sulfur batteries. ► Sulfur-alumina material was synthesized via crystallizing nucleation. ► The Al{sub 2}O{sub 3} can provide surface area for the deposition of Li{sub 2}S and Li{sub 2}S{sub 2}. ► The discharge capacity of the battery is improved during the first several cycles. - Abstract: Nano-sized sulfur particles exhibiting good adhesion with conducting acetylene black and alumina composite materials were synthesized by means of an evaporated solvent and a concentrated crystallization method for use as the cathodes of lithium-sulfur batteries. The composites were characterized and examined by X-ray diffraction, environmental scanning electron microscopy and electrochemical methods, such as cyclic voltammetry, electrical impedance spectroscopy and charge–discharge tests. Micron-sized flaky alumina was employed as an adsorbent for the cathode material. The initial discharge capacity of the cathode with the added alumina was 1171 mAh g{sup −1}, and the remaining capacity was 585 mAh g{sup −1} after 50 cycles at 0.25 mA cm{sup −2}. Compared with bare sulfur electrodes, the electrodes containing alumina showed an obviously superior cycle performance, confirming that alumina can contribute to reducing the dissolution of polysulfides into electrolytes during the sulfur charge–discharge process.

  2. Morphology-controlled electrochemical sensing amaranth at nanomolar levels using alumina.

    Science.gov (United States)

    Zhang, Yuanyuan; Gan, Tian; Wan, Chidan; Wu, Kangbing

    2013-02-18

    Different-shaped aluminas were readily prepared via hydrothermal reaction. It was found that the morphology and the electrochemical sensing properties of alumina were heavily dependent on the reaction time. When extending the reaction time from 6 h to 24 h, the obtained alumina samples changed from amorphous bumps to regular microfibers in diameter of 200 nm, as confirmed by scanning electron microscopy. Transmission electron microscopy observation revealed that longer reaction time was beneficial for the formation of porous and uniform fiber-like structures. Electrochemical tests proved that alumina microfibers were more active for the oxidation of amaranth and exhibited much higher enhancement effect, compared with alumina bumps. On the surface of alumina microfibers, the oxidation peak currents of amaranth increased remarkably. The influences of pH value, amount of alumina microfibers, and accumulation time on the signal enhancement of amaranth were discussed. As a result, a novel electrochemical method was developed for the detection of amaranth. The linear range was from 1 to 150 nM, and the detection limit was 0.75 nM after 1-min accumulation. The analytical application in drink samples was investigated, and the results consisted with the values that obtained by high-performance liquid chromatography.

  3. Effect of different sources of alumina on the microstructure and mechanical properties of the triaxial porcelain

    Directory of Open Access Journals (Sweden)

    G. Gralik

    2014-12-01

    Full Text Available Porcelains composed of kaolin-quartz-feldspar are called triaxial porcelains. The use of alumina as a substitute for quartz in porcelains has been developed for some time. The results show a significant improvement in their mechanical properties, but alumina has a high cost. The possibility of using alternative materials as a source of alumina with lower cost was investigated. In this work, alternative raw materials were used as a source of alumina: refractory bauxite, primary aluminum hydroxide, reprecipitated aluminum hydroxide. Compositions with commercial alumina and quartz were also formulated to better understand the effects of adding these alternative materials. The raw materials were milled, dried, and characterized by analysis of the particle size distribution, X-ray diffraction, and X-ray fluorescence. The compositions were formulated by replacing the different sources of alumina in the formulation of porcelain. The compositions studied were shaped by pressing and sintered at different temperatures (1150-1400 ºC. The results showed that the use of bauxite and aluminum hydroxide as an alternative source of Al2O3 is viable. The impurities contained in refractory bauxite contributed to the lower values of flexural strength found in compositions having refractory bauxite as a source of alumina. The compositions with reprecipitated aluminum hydroxide showed a high mechanical resistance at low sintering temperatures, while compositions with aluminum hydroxide obtained by the Bayer process achieved good results of mechanical strength in a wide temperature range.

  4. Preparation of Micro-Porous Alumina Sheet Support for Ceramic Membrane by Extrusion

    Science.gov (United States)

    Hemra, Khanthima; Atong, Duangduen; Aungkavattana, Pavadee

    Among several types of ceramic membrane developed for a half of century, alumina is the most extensive advantage. In this study, many types of alumina with different particle size distributions were used as a starting material for fabrication of support sheet ceramic membrane using extrusion process. The investigation focused on the alumina dough components composed of some organic binders and water. The organic binder of about 12 wt. % was required in order for dough to be easily extruded, while the amount of water added to the dough depended on the particle size of alumina powder. The particle size and size distribution of starting powder showed strong effects on pore size of sintered alumina support. The pore size decreased when smaller particle size of starting powder was used. In addition, the pore volume of the sintered alumina decreased with increasing the sintering temperature due to improvement in densification, while pore size remained the same. The mechanical strength of alumina supports was also influenced by the particle size of starting powder; the finer particle size resulted in the higher mechanical strength. However, in order to obtain a good flux for the membrane, a high mechanical strength of the support along with its effective porosity is critical concerns. In this work, the support sintered at 1450°C provided a proper porosity of approximately 40% with an acceptable mechanical strength of 30-45MPa.

  5. Evaluation of hemocompatibility and in vitro immersion on microwave-assisted hydroxyapatite–alumina nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Radha, G. [National Centre for Nanoscience and Nanotechnology, University of Madras, Guindy campus, Chennai - 600025 (India); Balakumar, S., E-mail: balasuga@yahoo.com [National Centre for Nanoscience and Nanotechnology, University of Madras, Guindy campus, Chennai - 600025 (India); Venkatesan, Balaji; Vellaichamy, Elangovan [Department of Biochemistry, University of Madras, Guindy campus, Chennai - 600025 (India)

    2015-05-01

    This study reports the microwave-assisted synthesis and characterization of nHAp (nano-hydroxyapatite)–alumina composites. The crystalline phase and interaction of alumina with nHAp was analyzed using X-ray diffraction (XRD) and Raman microscopy analysis, respectively. High resolution transmission electron microscopy (HRTEM) micrographs exhibit morphological changes of nHAp composites with increasing alumina concentrations. Microhardness studies reveal the enhanced mechanical strength of nHAp10 and nHAp20 nanocomposites than pure nHAp. In vitro bioactivity of the nanocomposites was studied by immersing samples in simulated body fluid (Hank's solution) for 21 days. The surface of biomineralized samples were analyzed using field emission scanning electron microscopy (FESEM) and energy dispersive X-ray spectroscopy (EDX). Hemolytic assay revealed acceptable compatibility for varying concentrations of all the samples. Cell proliferation assay was systematically investigated for 1 day and 3 days on Saos-2 osteoblast-like cell lines and it was found that nHAp nanocomposites improved the proliferation. - Highlights: • The microwave-assisted hydroxyapatite (nHAp)–alumina nanocomposites were prepared. • Structural and interaction between nHAp and alumina have been explored. • Increased alumina concentration enhanced mechanical strength of the nHAp. • Trace elements from SBF, incorporated on nHAp–alumina nanocomposite surface, were characterized by FESEM and EDX techniques. • Hemocompatibility of the samples were evaluated and the results are in accordance with ASTM standards.

  6. Photoluminescence properties of heat-treated porous alumina films formed in oxalic acid

    Energy Technology Data Exchange (ETDEWEB)

    Vrublevsky, I., E-mail: vrublevsky@bsuir.edu.b [Belarusian State University of Informatics and Radioelectronics Minsk, Department of Micro and Nanoelectronics, 220013 Minsk (Belarus); Chernyakova, K. [Belarusian State University of Informatics and Radioelectronics Minsk, Department of Micro and Nanoelectronics, 220013 Minsk (Belarus); Ispas, A.; Bund, A.; Gaponik, N.; Dubavik, A. [Technische Universitaet Dresden, Physikalische Chemie und Elektrochemie, 01062 Dresden (Germany)

    2011-05-15

    Photoluminescence and optical properties of as-anodized and heat-treated at 500 {sup o}C porous alumina films formed in a 0.3 M oxalic acid at 40 V have been studied. The FTIR indicates that the oxalate ions are embedded in the anodic alumina as chelating bidentate structures and further heating up to 500 {sup o}C does not cause any change in ion coordination. The results of time-resolved spectroscopy show the presence of two luminescence centers both in the as-anodized and heat-treated anodic alumina films with lifetimes of about 0.25 and 4.0 ns. The F{sup +}-centers in anodic alumina are responsible for the luminescence peak at about 420 nm, with a lifetime of about 4.0 ns. The luminescence peak at about 480 nm, with lifetime of about 0.25 ns, can be attributed to the luminescence of carboxylate ions existing in bulk of anodic alumina. - Research highlights: {yields} Photoluminescence and optical properties of porous alumina films have been studied. {yields} In anodic alumina the oxalate ions are embedded as chelating bidentate structures. {yields} The results show the presence of two luminescence centers. {yields} The F{sup +}-centers are responsible for the peak at 420 nm with a lifetime of 4.0 ns. {yields} The peak at 480 nm with a lifetime of 0.25 ns can be attributed to carboxylate ions.

  7. Metastable zirconia-yttria-alumina ceramics: Structure, processing and properties

    Science.gov (United States)

    Zhou, Xinzhang

    2002-09-01

    Metastable phases of zirconia-yttria-alumina produced by atmospheric plasma spray and subsequent quenching were studied. Two kinds of quenching methods were used: water quenching and splat quenching. Quenching rates were estimated to be 104°C/s for water quenching and between 105--107°C/s for splat quenching. Five compositions of sprayed dried powders (pure alumina, TZ3Y20A, TZ3Y57A, TZ3Y80A and pure zirconia) were plasma sprayed and quenched. The phases and microstructures of the plasma sprayed powders and thin films were investigated by XRD and FESEM. It was found that at different compositions and quenching rates, different high temperature phases formed. These phases are metastable at room temperature and can be in the form of an extended solid solution phase, an intermediate phase, or an amorphous structure. The grain sizes of the metastable phases are below 50 nm, as determined by XRD peak broadening. At the eutectic composition, zirconia-rich fibers (50 nm in diameter) uniformly distributed in an alumina-rich matrix were observed. 2-D and 3-D metastable phase diagrams were constructed to explain the metastable phase formation. Plasma spraying can be used to fabricate ceramic nanocomposites either by pressure-assisted sintering or spray forming of the metastable powders. Mechanical properties of TZ3Y20A specimens produced by plasma spray forming on steel substrates were studied. The dependence of the 4-point bend strength on plasma spray parameters was studied by a 26-2 statistical experimental design. It was found that the bend strength was sensitive to both standoff distance and scanning speed. The results of study show much promise in applications of the metastable ceramics. Firstly, homogeneous nucleation and growth of stable phases during sintering and high creep rate at elevated temperatures will result in uniformly dense nanoceramic composites. Secondly, extended solid solutions of rare earth elements in glass will greatly enhance the optical

  8. Contact fatigue response of porcelain-veneered alumina model systems.

    Science.gov (United States)

    Stappert, Christian F J; Baldassarri, Marta; Zhang, Yu; Stappert, Dina; Thompson, Van P

    2012-02-01

    Fatigue damage modes and reliability of hand-veneered (HV) and over-pressed (OP) aluminum-oxide layer structures were compared. Influence of luting cement thickness on mechanical performance was investigated. Sixty-four aluminum-oxide plates (10 × 10 × 0.5 mm) were veneered with hand built-up or pressed porcelain (0.7 mm) and adhesively luted (50- or 150-μm cement thickness) to water-aged composite resin blocks (12 × 12 × 4 mm). Single-load-to-failure and fatigue tests were performed with a spherical tungsten carbide indenter (d = 6.25 mm) applied in the center of the veneer layer. Specimens were inspected with polarized-reflected-light and scanning electron microscopy. Use-level probability Weibull curves were plotted with two-sided 90% confidence bounds, and reliability at 75,000 cycles and 250 N load was calculated. For all specimens but two OP with 50-μm cement thickness, failure was characterized by flexural radial cracks initiating at the bottom surface of the alumina core and propagating into the veneering porcelain before cone cracks could extend to the porcelain/alumina interface. HV specimens showed higher reliability compared to OP. Those with 50-μm cement thickness were more reliable relative to their 150-μm counterparts (HV_50 μm: 95% (0.99/0.67); HV_150 μm: 55% (0.92/0.01); OP_50 μm: 69% (0.84/0.48); OP_150 μm: 15% (0.53/0.004)). Similar failure modes were observed in HV and OP specimens. Radial cracks developing in the core and spreading into the veneer are suggested to cause bulk fracture, which is the characteristic failure mode for alumina core crowns. However, the highest resistance to fatigue loading was found for the HV specimens with thin cement thickness, while the lowest occurred for the OP with thick cement layer.

  9. Removal of hazardous anions from aqueous solutions by La(III)- and Y(III)-impregnated alumina

    Energy Technology Data Exchange (ETDEWEB)

    Wasay, Syed Abdul; Tokunaga, Shuzo [National Inst. of Materials and Chemical Research, Ibaraka (Japan); Park, S.W. [Keimyung Univ., Daegu City (Korea, Democratic People`s Republic of)

    1996-06-01

    New adsorbents, La(III)- and Y(III)-impregnated alumina, were prepared for the removal of hazardous anions from aqueous solutions. A commercially available alumina was impregnated with La(III) or Y(III) ions by the adsorption process. The change in the surface charge due to the impregnation was measured by acid/base titration. The adsorption rate and the capacity of the alumina for La(III) and Y(III) ions were determined. The adsorption characteristics of the La(III)- and Y(III)-impregnated alumina and the original alumina for fluoride, phosphate, arsenate and selenite ions were analyzed under various conditions. The pH effect, dose effect, and kinetics were studied. The removal selectivity by the impregnated alumina was in the order fluoride > phosphate > arsenate > selenite. The impregnated alumina has been successfully applied for the removal of hazardous anions from synthetic and high-tech industrial wastewaters.

  10. Observers change their target template based on expected context.

    Science.gov (United States)

    Bravo, Mary J; Farid, Hany

    2016-04-01

    Previous studies have shown that when observers search repeatedly for a target in a particular context, they may develop a target template that is biased for that context. Because the same target may appear in multiple contexts, we wondered whether observers are able to develop multiple templates for the same target, with each template biased for a particular context. In a series of behavioral experiments, we show that observers can learn multiple target templates for a single target and that they can voluntarily switch among these templates depending on the context they expect to see. Our results suggest that these biased templates may coexist with an unbiased representation of the target, provided they are learned first.

  11. A New Vectorization Technique for Expression Templates in C++

    CERN Document Server

    Progsch, J; Adelmann, A

    2011-01-01

    Vector operations play an important role in high performance computing and are typically provided by highly optimized libraries that implement the BLAS (Basic Linear Algebra Subprograms) interface. In C++ templates and operator overloading allow the implementation of these vector operations as expression templates which construct custom loops at compile time and providing a more abstract interface. Unfortunately existing expression template libraries lack the performance of fast BLAS(Basic Linear Algebra Subprograms) implementations. This paper presents a new approach - Statically Accelerated Loop Templates (SALT) - to close this performance gap by combining expression templates with an aggressive loop unrolling technique. Benchmarks were conducted using the Intel C++ compiler and GNU Compiler Collection to assess the performance of our library relative to Intel's Math Kernel Library as well as the Eigen template library. The results show that the approach is able to provide optimization comparable to the fas...

  12. A nanocluster beacon based on the template transformation of DNA-templated silver nanoclusters.

    Science.gov (United States)

    Teng, Ye; Jia, Xiaofang; Zhang, Shan; Zhu, Jinbo; Wang, Erkang

    2016-01-28

    In this work, we developed a novel light-up nanocluster beacon (NCB) based on shuttling dark silver nanoclusters (NCs) to a bright scaffold through hybridization. The fluorescence enhancement was as high as 70-fold when the two templates were on the opposite sides of the duplexes, enabling sensitive and selective detection of DNA.

  13. Silicon template preparation for the fabrication of thin patterned gold films via template stripping

    Science.gov (United States)

    Schmidl, G.; Dellith, J.; Dellith, A.; Teller, N.; Zopf, D.; Li, G.; Dathe, A.; Mayer, G.; Hübner, U.; Zeisberger, M.; Stranik, O.; Fritzsche, W.

    2015-12-01

    Metallic nanostructures play an important role in the vast field of modern nanophotonics, which ranges from the life sciences to biomedicine and beyond. Gold is a commonly-used and attractive material for plasmonics in the visible wavelength range, most importantly due to its chemical stability. In the present work, we focused on the different methods of plasmonic nanostructure fabrication that possess the greatest potential for cost-efficient fabrication. Initially, reusable (1 0 0) silicon templates were prepared. For this purpose, three different lithography methods (i.e. e-beam, optical, and nanoparticle lithography) were used that correspond to the desired structural scales. The application of a subsequent anisotropic crystal orientation-dependent wet etching process produced well-defined pyramidal structures in a wide variety of sizes, ranging from several microns to less than 100 nm. Finally, a 200 nm-thick gold layer was deposited by means of confocal sputtering on the silicon templates and stripped in order to obtain gold films that feature a surface replica of the initial template structure. The surface roughness that was achieved on the stripped films corresponds well with the roughness of the template used. This makes it possible to prepare cost-efficient high-quality structured films in large quantities with little effort. The gold films produced were thoroughly characterized, particularly with respect to their plasmonic response.

  14. Novel encoding methods for DNA-templated chemical libraries.

    Science.gov (United States)

    Li, Gang; Zheng, Wenlu; Liu, Ying; Li, Xiaoyu

    2015-06-01

    Among various types of DNA-encoded chemical libraries, DNA-templated library takes advantage of the sequence-specificity of DNA hybridization, enabling not only highly effective DNA-templated chemical reactions, but also high fidelity in library encoding. This brief review summarizes recent advances that have been made on the encoding strategies for DNA-templated libraries, and it also highlights their respective advantages and limitations for the preparation of DNA-encoded libraries.

  15. Template Synthesis and Characterization of TiO2 Nanotubules%Tio2纳米管的模板法制备及表征

    Institute of Scientific and Technical Information of China (English)

    李晓红; 张校刚; 力虎林

    2001-01-01

    The template method for preparing nanostructures entails the synthesis of the desired material within the pores of a nanoporous membrane.In this work,TiO2 nanotubules of the anatase form have been synthesized by sol-gel chemical method using porous anodic alumina as the template.Transmission electron microscopy (TEM),scanning electron microscopy (SEM),infrared spectroscopy (IR) and X-ray diffraction were used to investigate the structure and morphology of the TiO2 nanotubules.The results showed that the diameter and length of the obtained nanotubules were determined by the pore size and length of the PAA template.It was founded that through control of immersion time,both tubules and fibrils can be prepared; in addition,the wall thickness of the nanotubules can be varied at will.The result indicated that the sol particles absorbed preferably to the pore walls of the PAA membrane due to the fact that the pore walls were negatively charged and the TiO2 particles were positively charged.

  16. Biocompatibility of Soft-Templated Mesoporous Carbons

    Energy Technology Data Exchange (ETDEWEB)

    Gencoglu, Maria F. [Michigan Technological Univ., Houghton, MI (United States). Dept. of Chemical Engineering; Spurri, Amanda [Widener Univ., Chester, PA (United States). Dept. of Chemical Engineering; Franko, Mitchell [Widener Univ., Chester, PA (United States). Dept. of Chemical Engineering; Chen, Jihua [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Science (CNMS); Hensley, Dale K. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Science (CNMS); Heldt, Caryn L. [Michigan Technological Univ., Houghton, MI (United States). Dept. of Chemical Engineering; Saha, Dipendu [Widener Univ., Chester, PA (United States). Dept. of Chemical Engineering

    2014-08-21

    We report that soft-templated mesoporous carbon is morphologically a non-nano type of carbon. It is a relatively newer variety of biomaterial, which has already demonstrated its successful role in drug delivery applications. To investigate the toxicity and biocompatibility, we introduced three types of mesoporous carbons with varying synthesis conditions and pore textural properties. We compared the Brunauer–Emmett–Teller (BET) surface area and pore width and performed cytotoxicity experiments with HeLa cells, cell viability studies with fibroblast cells and hemocomapatibility studies. Cytotoxicity tests reveal that two of the carbons are not cytotoxic, with cell survival over 90%. The mesoporous carbon with the highest surface area showed slight toxicity (~70% cell survival) at the highest carbon concentration of 500 μg/mL. Fibroblast cell viability assays suggested high and constant viability of over 98% after 3 days with no apparent relation with materials property and good visible cell-carbon compatibility. No hemolysis (<1%) was confirmed for all the carbon materials. Protein adsorption experiments with bovine serum albumin (BSA) and fibrinogen revealed a lower protein binding capacity of 0.2–0.6 mg/m2 and 2–4 mg/m2 for BSA and fibrinogen, respectively, with lower binding associated with an increase in surface area. The results of this study confirm the biocompatibility of soft-templated mesoporous carbons.

  17. Pd-Pt Catalysts on Fluorinated Alumina Support Studied by X-Ray Absorption Fine Structure

    Science.gov (United States)

    Yan, Wensheng; Li, Zhongrui; Wei, Zheng; Wei, Shiqiang

    2007-02-01

    A series of bi-metallic Pd-Pt catalysts supported on both pristine and fluorinated alumina supports were investigated with x-ray absorption spectroscopy. It was found that Pd and Pt form small alloy particles on the pristine alumina support; the composition and the cluster size of the PdPt bimetallic alloys, and the electronic properties of the metals were significantly altered on the fluorinated support. The remarkable increase in sulfur tolerance of the PdPt metallic clusters supported on the fluorine pretreated alumina can be attributed to an electronic depletion of the metals, large particle size and direct participation of the acid sites in the reaction.

  18. EFFECT OF NANOPOWDER ADDITION ON THE FLEXURAL STRENGTH OF ALUMINA CERAMIC - A WEIBULL MODEL ANALYSIS

    Directory of Open Access Journals (Sweden)

    Daidong Guo

    2016-05-01

    Full Text Available Alumina ceramics were prepared either with micrometer-sized alumina powder (MAP or with the addition of nanometer-sized alumina powder (NAP. The density, crystalline phase, flexural strength and the fracture surface of the two ceramics were measured and compared. Emphasis has been put on the influence of nanopowder addition on the flexural strength of Al₂O₃ ceramic. The analysis based on the Weibull distribution model suggests the distribution of the flexural strength of the NAP ceramic is more concentrated than that of the MAP ceramic. Therefore, the NAP ceramics will be more stable and reliable in real applications.

  19. Rare earth-doped alumina thin films deposited by liquid source CVD processes

    Energy Technology Data Exchange (ETDEWEB)

    Deschanvres, J.L.; Meffre, W.; Joubert, J.C.; Senateur, J.P. [Ecole Nat. Superieure de Phys. de Grenoble, St. Martin d`Heres (France). Lab. des Materiaux et du Genie Phys.; Robaut, F. [Consortium des Moyens Technologiques Communs, Institut National Polytechnique de Grenoble, BP 75, 38402 St Martin d`Heres (France); Broquin, J.E.; Rimet, R. [Laboratoire d`Electromagnetisme, Microondes et Optoelectronique, CNRS-Ecole Nationale Superieure d`Electronique et Radioelectricite de Grenoble, BP 257, 38016 Grenoble, Cedex (France)

    1998-07-24

    Two types of liquid-source CVD processes are proposed for the growth of rare earth-doped alumina thin films suitable as amplifying media for integrated optic applications. Amorphous, transparent, pure and erbium- or neodymium-doped alumina films were deposited between 573 and 833 K by atmospheric pressure aerosol CVD. The rare earth doping concentration increases by decreasing the deposition temperature. The refractive index of the alumina films increases as a function of the deposition temperature from 1.53 at 573 K to 1.61 at 813 K. Neodymium-doped films were also obtained at low pressure by liquid source injection CVD. (orig.) 7 refs.

  20. Transport properties of anodic porous alumina for ReRAM

    Energy Technology Data Exchange (ETDEWEB)

    Kato, S; Nigo, S; Lee, J W; Mihalik, M; Kitazawa, H; Kido, G [National Institute for Materials Science, 1-2-1 Sengen, Tsukuba, Ibaraki, 305-0047 (Japan)], E-mail: KATO.Seiichi@nims.go.jp

    2008-03-15

    A voltage-induced bistable switching effect has been studied for M/AlO{sub x}/Al devices made of the anodic porous alumina with a top electrode of aluminium (or silver) to develop a next generation memory (AlO{sub x}-ReRAM). The resistance state of memory is switched between OFF-state (high resistance) and ON-state (low resistance), where the resistance ratio is higher than 10{sup 4}. In the thermally stimulated current (TSC) measurement, a narrow band was observed around 290 K, indicating the conduction mechanism comes from a kind of impurity band in the energy gap. An anomaly was also observed around 290 K in the temperature dependence of resistance at the ON-state.