WorldWideScience

Sample records for oil-based polyurethane adhesive

  1. Alternative castor oil-based polyurethane adhesive used in the production of plywood

    Directory of Open Access Journals (Sweden)

    Fabricio Moura Dias

    2004-09-01

    Full Text Available Plywood is normally produced with urea-formaldehyde and/or phenol-formaldehyde adhesives. However, the former is considerably toxic and environmentally damaging, while the latter is expensive, thus motivating the search for alternative raw materials in plywood production. The castor oil-based polyurethane adhesive developed at the São Carlos Institute of Chemistry, University of São Paulo, is an environmentally friendly vegetal oil-based polymer that is harmless to humans. The wood species Eucalyptus grandis offers favorable properties for plywood the manufacture. The study reported on here involved the use of castor oil-based polyurethane adhesive to produce plywood with Eucalyptus grandis layers. The plywood's performance was evaluated based on the results of physical and mechanical tests recommended by the Brazilian code, ABNT. Tests results showed higher values than those reported in the literature and recommended by the ABNT, indicating that the castor oil-based polyurethane adhesive is a promising glue for the manufacture of plywood.

  2. Palm oil based polyols for acrylated polyurethane production

    International Nuclear Information System (INIS)

    Rida Tajau; Mohd Hilmi Mahmood; Mek Zah Salleh; Khairul Zaman Mohd Dahlan; Rosley Che Ismail

    2006-01-01

    Palm oil becomes important renewable resources for the production of polyols for the polyurethane manufacturing industry. The main raw materials used for the production of acrylated polyurethane are polyols, isocyanates and hydroxyl terminated acrylate compounds. In these studies, polyurethane based natural polymer (palm oil), i.e., POBUA (Palm Oil Based Urethane Acrylate) were prepared from three different types of palm oil based polyols i.e., epoxidised palm oil (EPOP), palm oil oleic acid and refined, bleached and deodorized (RBD) palm olein based polyols. The performances of these three acrylated polyurethanes when used for coatings and adhesives were determined and compared with each other. (Author)

  3. Vegetable Oil-Based Hyperbranched Thermosetting Polyurethane/Clay Nanocomposites

    Directory of Open Access Journals (Sweden)

    Deka Harekrishna

    2009-01-01

    Full Text Available Abstract The highly branched polyurethanes and vegetable oil-based polymer nanocomposites have been showing fruitful advantages across a spectrum of potential field of applications.Mesua ferreaL. seed oil-based hyperbranched polyurethane (HBPU/clay nanocomposites were prepared at different dose levels by in situ polymerization technique. The performances of epoxy-cured thermosetting nanocomposites are reported for the first time. The partially exfoliated structure of clay layers was confirmed by XRD and TEM. FTIR spectra indicate the presence of H bonding between nanoclay and the polymer matrix. The present investigation outlines the significant improvement of tensile strength, scratch hardness, thermostability, water vapor permeability, and adhesive strength without much influencing impact resistance, bending, and elongation at break of the nanocomposites compared to pristine HBPU thermoset. An increment of two times the tensile strength, 6 °C of melting point, and 111 °C of thermo-stability were achieved by the formation of nanocomposites. An excellent shape recovery of about 96–99% was observed for the nanocomposites. Thus, the formation of partially exfoliated clay/vegetable oil-based hyperbranched polyurethane nanocomposites significantly improved the performance.

  4. Vegetable Oil-Based Hyperbranched Thermosetting Polyurethane/Clay Nanocomposites.

    Science.gov (United States)

    Deka, Harekrishna; Karak, Niranjan

    2009-04-25

    The highly branched polyurethanes and vegetable oil-based polymer nanocomposites have been showing fruitful advantages across a spectrum of potential field of applications. Mesua ferrea L. seed oil-based hyperbranched polyurethane (HBPU)/clay nanocomposites were prepared at different dose levels by in situ polymerization technique. The performances of epoxy-cured thermosetting nanocomposites are reported for the first time. The partially exfoliated structure of clay layers was confirmed by XRD and TEM. FTIR spectra indicate the presence of H bonding between nanoclay and the polymer matrix. The present investigation outlines the significant improvement of tensile strength, scratch hardness, thermostability, water vapor permeability, and adhesive strength without much influencing impact resistance, bending, and elongation at break of the nanocomposites compared to pristine HBPU thermoset. An increment of two times the tensile strength, 6 degrees C of melting point, and 111 degrees C of thermo-stability were achieved by the formation of nanocomposites. An excellent shape recovery of about 96-99% was observed for the nanocomposites. Thus, the formation of partially exfoliated clay/vegetable oil-based hyperbranched polyurethane nanocomposites significantly improved the performance.

  5. Mixed Field Modification of Thermally Cured Castor Oil Based Polyurethanes

    International Nuclear Information System (INIS)

    Mortley, A.

    2006-01-01

    Thermally cured polyurethanes were prepared from castor oil and hexamethylene diisocyanatee (HMDI). Due to the long aliphatic chain of the castor oil component of polyurethane, thermal curing of castor oil based polyurethane (COPU) is limited by increasing polymer viscosity. To enhance further crosslinking, COPUs were subjected to a range of accumulated doses (0.0-3.0 MGy) produced by the mixed ionizing field of the SLOWPOKE-2 research reactor. The physico-mechanical properties of COPU, unirradiated and irradiated, were characterized by mechanical tests. Increased bond formation resulting from radiation-induced crosslinking was confirmed by favorable increases in mechanical properties and by solid-state 13 C -NMR and FTIR spectra

  6. Synthesis and characterization of castor oil based polyurethane ...

    Indian Academy of Sciences (India)

    Unknown

    Abstract. A series of interpenetrating polymer networks (IPNs) of castor oil based polyurethane/polyacrylo- nitrile (PU/PAN: 80/20, 60/40, 50/50, 40/60 and 20/80) were synthesized by condensation reaction of castor oil with methylene diisocyanate and acrylonitrile, employing benzoyl peroxide (BPO) and ethylene glycol ...

  7. Castor Oil Based Polyurethanes: Synthesis and Characterization

    Science.gov (United States)

    Macalino, AD; Salen, VA; Reyes, LQ

    2017-09-01

    In this study, polyurethanes based on castor oil and 1,6-hexamethylene diisocyanate (HMDI) were synthesized with varying weight ratio of the castor oil and HMDI. The formation of urethane linkages was verified through the use of a fourier transform infrared spectroscopy (FTIR). The hydrophilicity of the films was evaluated through the use of a contact angle meter and it was found that the contact angle of all the films were below 90 degrees which confirms their hydrophilicity. The thermal stability of the PU films were studies through the use of a thermal gravimetric analyzer and found that all of the polyurethane films exhibited two weight loss events at elevated temperatures wherein the first weight loss event was observed to occur at 285°C to 384°C while the second weight loss event was observed at around 521°C to 551°C. The hardness, elastic modulus, and tensile elongation of the PU films were determined by using a universal testing machine (UTM) where it was found out that the hardness and the elastic modulus of the film is directly proportional with HMDI loading while the tensile elongation is inversely proportional to it. Lastly, it was known through the swelling studies of the PU films that it does not swell, this is due to the presence of unreacted triglycerides in the material, which prevents water from permeating to the films.

  8. Polyurethane adhesives in flat roofs

    Directory of Open Access Journals (Sweden)

    Bogárová Markéta

    2017-01-01

    Full Text Available It is necessary to stabilize individual layers of flat roofs, mainly because of wind suction. Apart from anchoring and surcharge, these layers can be secured by bonding. At present gluing is an indispensable and widely used stabilization method. On our market we can found many types of adhesives, most widely used are based on polyurethane. This paper focuses on problematic about stabilization thermal insulation from expanded polystyrene to vapor barrier from bitumen. One of the main issues is to calculate the exact amount of adhesive, which is required to guarantee the resistance against wind suction. In this problematic we can not find help neither in technical data sheets provided by the manufactures. Some of these data sheets contain at least information about amount of adhesive depending on location in roof plane and building height, but they do not specify the strength of such connection. It was therefore resorted to select several representatives polyurethane adhesives and their subsequent testing on specimens simulating the flat roof segment. The paper described the test methodology and results for two types of polyurethane adhesives.

  9. Characterization of Novel Castor Oil-Based Polyurethane Polymer Electrolytes

    Directory of Open Access Journals (Sweden)

    Salmiah Ibrahim

    2015-04-01

    Full Text Available Castor oil-based polyurethane as a renewable resource polymer has been synthesized for application as a host in polymer electrolyte for electrochemical devices. The polyurethane was added with LiI and NaI in different wt% to form a film of polymer electrolytes. The films were characterized by using attenuated total reflectance-Fourier transform infrared spectroscopy, dynamic mechanical analysis, electrochemical impedance spectroscopy, linear sweep voltammetry and transference number measurement. The highest conductivity of 1.42 × 10−6 S cm−1 was achieved with the addition of 30 wt% LiI and 4.28 × 10−7 S·cm−1 upon addition of 30 wt% NaI at room temperature. The temperature dependence conductivity plot indicated that both systems obeyed Arrhenius law. The activation energy for the PU-LiI and PU-NaI systems were 0.13 and 0.22 eV. Glass transition temperature of the synthesized polyurethane decreased from −15.8 °C to ~ −26 to −28 °C upon salts addition. These characterizations exhibited the castor oil-based polyurethane polymer electrolytes have potential to be used as alternative membrane for electrochemical devices.

  10. Polyurethane adhesives in flat roofs

    OpenAIRE

    Bogárová Markéta; Stodůlka Jindřich; Šuhajda Karel

    2017-01-01

    It is necessary to stabilize individual layers of flat roofs, mainly because of wind suction. Apart from anchoring and surcharge, these layers can be secured by bonding. At present gluing is an indispensable and widely used stabilization method. On our market we can found many types of adhesives, most widely used are based on polyurethane. This paper focuses on problematic about stabilization thermal insulation from expanded polystyrene to vapor barrier from bitumen. One of the main issues is...

  11. The Effect of Reactives Diluents to the Physical Properties of Acrylated Palm Oil Based Polyurethane Coatings

    Directory of Open Access Journals (Sweden)

    Onn Munirah

    2016-01-01

    Full Text Available The development of polyurethane with hydroxyl access in a molecule leads to a new alternative of low toxicity green product. Palm oil is one of the major commodities in Malaysia. The potential of palm oil to be used as coatings raw material such as alkyd is limited due to low unsaturated side on fatty acid chains. To overcome this limitation, palm oil was modified through transesterification process to produce polyol. Acrylated isocyanate (urethane oligomer was then grafted onto polyol to produce polyurethane with vinylic ends. The polyurethane was formulated with different cross-linkers (reactive diluents and cured under UV radiation. The effect of three different diluents; monoacrylate, diacrylate and triacrylate on the properties of cured polymer were studied in this research. Fourier Transform Infrared (FTIR, Hydroxyl Value Titration, Gel Content, and Volatile Organic Compound (VOC were used for characterization. Physical testing performed were Pencil Hardness and Pull-Off Adhesion test. Novel palm oil-based polyurethane coatings have been found to have good properties with mono acrylate functionality.

  12. Adhesion aspects of polyurethane foam sandwich panels.

    OpenAIRE

    Ng, Simon L.

    2016-01-01

    Sandwich panels, polyurethane foam sandwiched between two sheets of steel, form the walls and roofs in the construction of buildings. ArcelorMittal is a manufacturer of the steel as well as these finished panels. For this project they combined with a supplier of the polyurethane foams, Huntsman Polyurethanes, to joint-fund a research project investigating the fundamental mechanisms of adhesion, as well as the causes of failures in the product which manifests primarily in two different ways...

  13. Biomaterial based novel polyurethane adhesives for wood to wood and metal to metal bonding

    Directory of Open Access Journals (Sweden)

    Mitesh Ramanlal Patel

    2009-01-01

    Full Text Available Polyurethane adhesives made from synthetic chemicals are non-biodegradable, costly and difficult to find raw materials from local market. To avoid solid pollution problem, cost effectiveness and easy availability of raw materials, biomaterials based polyurethane adhesives are used in current industrial interest. Direct use of castor oil in polyurethane adhesive gives limited hardness. Modification on active sites of castor oil to utilize double bond of unsaturated fatty acid and carboxyl group yields new modified or activated polyols, which can be utilized for polyurethane adhesive formulation. In view of this, we have synthesized polyurethane adhesives from polyester polyols, castor oil based polyols and epoxy based polyols with Isocyanate adducts based on castor oil and trimethylolpropane. To study the effects of polyurethane adhesive strength (i.e. lap shear strength on wood-to-wood and metal-to-metal bonding through various types of polyols, cross-linking density, isocyanate adducts and also to compare adhesive strength between wood to wood and metal to metal surface. These polyols and polyurethanes were characterized through GPC, NMR and IR-spectroscopy, gel and surface drying time. Thermal stability of PU adhesives was determined under the effect of cross-linking density (NCO/OH ratio. The NCO/OH ratio (1.5 was optimized for adhesives as the higher NCO/OH ratio (2.0 increasing cross-linking density and decreases adhesion. Lower NCO/OH ratio (1.0 provideslow cross-linking density and low strength of adhesives.

  14. Production of Particleboards from Hevea brasiliensis Clones and Castor Oil-based Polyurethane Resin

    Directory of Open Access Journals (Sweden)

    Maristela Gava

    2015-08-01

    Full Text Available The economic exploitation of rubber tree (Hevea brasiliensis usage is primarily directed toward latex extraction. After the productive life of the rubber tree forest, the managed area is harvested for planting reformulation. The harvested wood is most often used for energy generation purposes. The aim of this work was to study the feasibility of using rubberwood waste and castor oil-based polyurethane resin in the production of particleboards. Homogeneous and heterogeneous panels were made with nominal dimensions of 500 x 500 mm and thicknesses of 10 mm using particles from GT1 and RRIM600 clones of the rubber tree and 12% castor oil-based polyurethane adhesive. The panels were pressed at 140 °C for 12 min with 40 kgf/cm2 specific pressure. Density, moisture content, thickness swelling, water absorption for 2 and 24 h, static bending, and internal bonding determinations were performed according to the Brazilian Standard (NBR 14810-3 (2006 for the physical-mechanical panel characterization. The results show that using Hevea brasiliensis in particleboard production is viable. However, multilayer boards exhibited better results.

  15. Mechanical and thermal properties of sisal fiber-reinforced rubber seed oil-based polyurethane composites

    International Nuclear Information System (INIS)

    Bakare, I.O.; Okieimen, F.E.; Pavithran, C.; Abdul Khalil, H.P.S.; Brahmakumar, M.

    2010-01-01

    The development of high-performance composite materials from locally sourced and renewable materials was investigated. Rubber seed oil polyurethane resin synthesized using rubber seed monoglyceride derived from glycerolysis of the oil was used as matrix in the composite samples. Rubber seed oil-based polyurethane composite reinforced with unidirectional sisal fibers were prepared and characterized. Results showed that the properties of unidirectional fiber-reinforced rubber seed oil-based polyurethane composites gave good thermal and mechanical properties. Also, the values of tensile strengths and flexural moduli of the polyurethane composites were more than tenfold and about twofold higher than un-reinforced rubber seed oil-based polyurethane. The improved thermal stability and the scanning electron micrographs of the fracture surface of the composites were attributed to good fiber-matrix interaction. These results indicate that high-performance 'all natural products' composite materials can be developed from resources that are readily available locally.

  16. Synthesis and characterization of castor oil-based polyurethane

    Indian Academy of Sciences (India)

    Polyurethane (PU) based on polyol, derived from castor oil has been synthesized and characterized for potential use as a base material for electrolytes. Transesterification process of castor oil formed a polyol with hydroxyl value of 190 mg KOH g–1 and molecular weight of 2786 g mol–1. The polyols together with 4 ...

  17. Preparation and Characterization of Controlled-Release Avermectin/Castor Oil-Based Polyurethane Nanoemulsions.

    Science.gov (United States)

    Zhang, Hong; Qin, He; Li, Lingxiao; Zhou, Xiaoteng; Wang, Wei; Kan, Chengyou

    2017-06-12

    Avermectin (AVM) is a low-toxic and high-active biopesticide, but it can be easily degraded by UV light. In this paper, biodegradable castor oil-based polyurethanes (CO-PU) are synthesized and used as carriers to fabricate a new kind of AVM/CO-PU nanoemulsion through an emulsion solvent evaporation method, and the chemical structure, colloidal property, AVM loading capacity, controlled-release behavior, foliar adhesion, and photostability of the AVM/CO-PU drug delivery systems are investigated. Results show that AVM is physically encapsulated in the CO-PU carrier nanospheres, the diameter of the AVM/CO-PU nanoparticles is 85%. The release profiles indicate that the release rate is relatively high at the early stage and then slows, which can be adjusted by loaded AVM content, temperature, and pH of the release medium. The foliar pesticide retention of the AVM/CO-PU nanoemulsions is improved, and the photolysis rate of AVM in the AVM/CO-PU nanoparticles is significantly slower than that of the free AVM. A release mechanism of the AVM/CO-PU nanoemulsions is proposed, which is controlled by both diffusion and matrix erosion.

  18. Green waste cooking oil-based rigid polyurethane foam

    Science.gov (United States)

    Enderus, N. F.; Tahir, S. M.

    2017-11-01

    Polyurethane is a versatile polymer traditionally prepared using petroleum-based raw material. Petroleum, however, is a non-renewable material and polyurethane produced was found to be non-biodegradable. In quest for a more environmentally friendly alternative, wastecooking oil, a highly abundant domestic waste with easily derivatized structure, is a viable candidate to replace petroleum. In this study,an investigation to determine physical and chemical properties of rigid polyurethane (PU) foam from waste cooking oil (WCO) was carried out. WCO was first adsorbed by using coconut husk activated carbon adsorbent prior to be used for polyol synthesis. The purified WCO was then used to synthesize polyol via transesterification reaction to yield alcohol groups in the WCO chains structure. Finally, the WCO-based polyol was used to prepare rigid PU foam. The optimum formulation for PU formation was found to be 90 polyol: 60 glycerol: 54 water: 40 diethanolamine: 23 diisocyanate. The rigid PU foam has density of 208.4 kg/m3 with maximum compressive strength and capability to receive load at 0.03 MPa and 0.09 kN, respectively. WCO-based PU can potentially be used to replace petroleum-based PU as house construction materials such as insulation panels.

  19. Production and characterization of MDF using eucalyptus fibers and castor oil-based polyurethane resin

    Directory of Open Access Journals (Sweden)

    Campos Cristiane Inácio de

    2004-01-01

    Full Text Available The growing popularity of wooden panels renders this market segment increasingly competitive. MDF (Medium Density Fiberboard, in particular, is widely employed for a variety of applications, including civil construction, furniture, and packaging. This paper discusses a study of MDF produced from alternative raw materials, i.e., Eucalyptus fibers and castor-oil-based polyurethane resin. Physical and mechanical tests were performed to determine the MDF's modulus of elasticity and modulus of rupture in static bending tests, its swelling, water absorption, moisture and density. The results of the physical and mechanical characterization of this laboratory-produced MDF are discussed and compared with the Euro MDF Board standard. MDF produced with eucalyptus fiber and castor-oil-based polyurethane resin presents results very satisfactory.

  20. Synthesis and properties of radiation modified thermally cured castor oil based polyurethanes

    Energy Technology Data Exchange (ETDEWEB)

    Mortley, Aba [Department of Chemistry and Chemical Engineering, Royal Military College of Canada, Kingston, P.O. Box 17000, Stn Forces, Kingston, ON, K7K 7B4 (Canada)], E-mail: aba.mortley@rmc.ca; Bonin, H.W.; Bui, V.T. [Department of Chemistry and Chemical Engineering, Royal Military College of Canada, Kingston, P.O. Box 17000, Stn Forces, Kingston, ON, K7K 7B4 (Canada)

    2007-12-15

    Thermally cured polyurethanes were prepared from castor oil and hexamethylene diisocyanate (HMDI). Due to the long aliphatic chain of the castor oil component of polyurethane, thermal curing of castor oil based polyurethane (COPU) is limited by increasing polymer viscosity. To enhance further crosslinking, COPUs were exposed to doses up to 3.0 MGy produced by the mixed ionizing radiation field of a SLOWPOKE-2 research nuclear reactor. The physico-mechanical properties of castor oil based polyurethanes (COPU), unirradiated and irradiated, were characterized by mechanical tensile tests. A four-fold increase in modulus and tensile strength values from 0.930 to 4.365 MPa and 0.149 to 0.747 MPa, respectively, suggests improved physico-mechanical properties resulting from radiation. The changing areas of the carbonyl and the NH absorbance peaks and the disappearance of the isocyanate peak in the FTIR spectra as radiation progressed, indicates increased hydrogen bonding and intermolecular crosslinking, which is in agreement with the mechanical tests. Unchanging {sup 13}C solid state NMR spectra imply limited sample degradation with increasing radiation.

  1. Synthesis and properties of radiation modified thermally cured castor oil based polyurethanes

    International Nuclear Information System (INIS)

    Mortley, Aba; Bonin, H.W.; Bui, V.T.

    2007-01-01

    Thermally cured polyurethanes were prepared from castor oil and hexamethylene diisocyanate (HMDI). Due to the long aliphatic chain of the castor oil component of polyurethane, thermal curing of castor oil based polyurethane (COPU) is limited by increasing polymer viscosity. To enhance further crosslinking, COPUs were exposed to doses up to 3.0 MGy produced by the mixed ionizing radiation field of a SLOWPOKE-2 research nuclear reactor. The physico-mechanical properties of castor oil based polyurethanes (COPU), unirradiated and irradiated, were characterized by mechanical tensile tests. A four-fold increase in modulus and tensile strength values from 0.930 to 4.365 MPa and 0.149 to 0.747 MPa, respectively, suggests improved physico-mechanical properties resulting from radiation. The changing areas of the carbonyl and the NH absorbance peaks and the disappearance of the isocyanate peak in the FTIR spectra as radiation progressed, indicates increased hydrogen bonding and intermolecular crosslinking, which is in agreement with the mechanical tests. Unchanging 13 C solid state NMR spectra imply limited sample degradation with increasing radiation

  2. Synthesis and Application of Jatropha Oil based Polyurethane as Paint Coating Material

    Directory of Open Access Journals (Sweden)

    Zainal Alim Mas’ud

    2012-08-01

    Full Text Available Recently, the use of renewable sources in the preparation of various industrial materials has been revitalized in response to environmental concerns. Natural oils are considered to be the most important genre of renewable sources. Jatropha curcas oil (JPO based polyol is an alternative material that may possibly replace petrochemical-based polyol for polyurethane coating material. Polyurethane was synthesized by reacting JPO-based polyol with isocyanate. To produce JPO-based polyol, JPO was first epoxidized to form epoxidized J. curcas oil (EJP, subsequently it was converted to polyol by the opening ring reaction with acrylic acid (AA using triethylamine (TEA as a catalyst. The JPO-based polyurethane film resulting from this study is compared with polyurethane film from commercial polyol for gloss, hardness, and adhesion quality. The result showed that the source of polyol has an influence on gloss, hardness, and adhesion of polyurethane film, but the differences with using isocyanate has less influence. Using visual observation, polyurethane film produced from L.OHV polyol, H.OHV polyol and commercial polyol have similar quality.

  3. Mechanical Behavior of Castor-Oil-Based Advanced Polyurethane Functionalized with Glycidol and Siloxanes

    Science.gov (United States)

    Mathew, Aiswarea; Kurmvanshi, Surendra; Mohanty, Smita; Nayak, Sanjay K.

    2017-12-01

    Castor-oil-based polyurethane (PU), epoxy (glycidol) terminated polyurethane (EPU), and hydroxy terminated poly (dimethyl siloxane) (HTPDMS) modified EPU (EPDMS) were synthesized. The PU and EPU were synthesized with polyol:diisocyanate and polyol:diisocyanate:glycidol ratio of 1:1.2 and 1:3:3, respectively, whereas EPDMS was prepared by the incorporation of 5 wt.%, 10 wt.%, 20 wt.%, and 30 wt.% of HTPDMS into the EPU. The structural modification of EPDMS was confirmed by solid-state CP/MAS 13C and 29Si NMR spectroscopy. The results of a tensile test revealed that the EPDMS with 10 wt.% loading of HTPDMS (EPDMS10) exhibited considerable enhancement in the tensile strength and modulus. The scanning electron microscope analysis was performed to understand the increased phase heterogeneity of the samples.

  4. Preparation and characterization of Jatropha oil-based Polyurethane as non-aqueous solid polymer electrolyte for electrochemical devices

    International Nuclear Information System (INIS)

    Mustapa, Siti Rosnah; Aung, Min Min; Ahmad, Azizan; Mansor, Ahmad; TianKhoon, Lee

    2016-01-01

    Jatropha-oil based polyurethane is one of the initiative for replacing conventional petroleum based polyurethane. The vegetable oil-based polyurethane is more cost-effective and synthesize from renewable resources. Polyurethane was synthesized through prepolymerization method between jatropha oil-based polyol and diphenylmethane 4, 4’diisocyanate, (MDI) in inert condition. Then, lithium perchloride ion (LiClO 4 ) was added to the polyurethane system to form electrolyte film via solution casting technique. The polymer electrolytes were prepared by varying the amount of LiClO 4 ion 10 wt.% to 30 wt. %. The highest conductivity is achieved at 25 wt.% of LiClO 4 salt content, which is 1.29 × 10 −4 S/cm at room temperature 30 °C. The FTIR results showed the shifting of carbonyl group (C=O) (1750 cm −1 – 1730 cm −1 ), ether and ester group (C-O-C) (1300 cm −1 –1000 cm −1 ) and amine functional groups (N-H) (1650 cm −1 –1500 cm −1 ) in polyurethane electrolytes from the blank polyurethane shows that oxygen and nitrogen atom acts as electron donor in the electrolytes system. It also confirmed that the intermolecular reaction had occurred in the electrolytes system. While, the XRD analysis showed the semi-crystalline properties of polyurethane have been reduced to amorphous phase upon the increasing addition of lithium ion. SEM results revealed the morphology analysis of the polyurethane electrolytes. There is homogenous and smooth surface in polyurethane and the dissociation of salt was observed after the addition of salt indicates there was interaction between salt and the polymer host.

  5. Evaluation of castor oil-based polyurethane membranes in rat bone-marrow cell culture.

    Science.gov (United States)

    Cerejo, Sofia de Amorim; Rahal, Sheila Canevese; Lima Neto, João Ferreira de; Voorwald, Fabiana Azevedo; Alvarenga, Fernanda da Cruz Landim e

    2011-10-01

    To evaluate three methods to isolate rats MSCs and to analyze the potential of a castor oil polyurethane base membrane as a scaffold for MSCs. Four male Wistar rats, aged 20-30 days were used. Bone marrow aspirates from femur and tibia were harvested using DMEM high glucose and heparin. The cell culture was performed in three different ways: direct culture and two types of density gradients. After 15 days, was made the 1st passage and analyzed cell viability with markers Hoerscht 33342 and propidium iodide. The MSCs were characterized by surface markers with the aid of flow cytometry. After this, three types of castor oil polyurethane membranes associated with the MSCs were kept on the 6-well plate for 5 days and were analyzed by optical microscopy to confirm cell aggregation and growth. Separation procedures 1 and 2 allowed adequate isolation of MSCs and favored cell growth with the passage being carried out at 70% confluence after 15 days in culture. The cells could not be isolated using procedure 3. When the 3 castor oil polyurethane membrane types were compared it was possible to observe that the growth of MSCs was around 80% in membrane type 3, 20% in type 2, and 10% in type 1. Both Ficoll-Hypaque densities allow isolation of rat MSCs, and especially castor oil-based membrane type 3 may be used as a scaffold for MSCs.

  6. Thermal stability of novel polyurethane adhesives investigated by TGA

    Directory of Open Access Journals (Sweden)

    Mariusz Mamiński

    2014-05-01

    Full Text Available The objective of the work was an assessment of thermal stability of novel polyurethane wood adhesives by means of TGA. Hyperbranched polyglycerols of various structures were used as polyol components cured with polymeric methylenediphenyldiisocyanate (PMDI or polymeric hexamethylenediisocyanate (PHDI. Resultant adhesives were thermally degraded in temperature range 20 - 500ºC. Performance of polyurethane based on fully aliphatic polyglycerol was inferior to those based on polyglycerols bearing aromatic moieties. The differences in 50%-weight loss temperature achieving 27 - 39°C as well as residual weights at 480 ºC indicate the contribution of aromatic units presence within the macromonomer structure to increased thermal stability of polyurethane upon thermal degradation. Furthermore, temperature of 50% weight loss revealed that thermal stability of the developed hyperbranched polyglycerol-based adhesives was comparable to that of the commercial PUR adhesive.

  7. PLATELET ADHESION TO POLYURETHANE UREA UNDER PULSATILE FLOW CONDITIONS

    Science.gov (United States)

    Navitsky, Michael A.; Taylor, Joshua O.; Smith, Alexander B.; Slattery, Margaret J.; Deutsch, Steven; Siedlecki, Christopher A.; Manning, Keefe B.

    2014-01-01

    Platelet adhesion to a polyurethane urea surface is a precursor to thrombus formation within blood-contacting cardiovascular devices, and platelets have been found to adhere strongly to polyurethane surfaces below a shear rate of approximately 500 s−1. The aim of the current work is to determine platelet adhesion properties to the polyurethane urea surface as a function of time varying shear exposure. A rotating disk system is used to study the influence of steady and pulsatile flow conditions (e.g. cardiac inflow and sawtooth waveforms) for platelet adhesion to the biomaterial surface. All experiments retain the same root mean square angular rotation velocity (29.63 rad/s) and waveform period. The disk is rotated in platelet rich bovine plasma for two hours with adhesion quantified by confocal microscopy measurements of immunofluorescently labeled bovine platelets. Platelet adhesion under pulsating flow is found to exponentially decay with increasing shear rate. Adhesion levels are found to depend upon peak platelet flux and shear rate regardless of rotational waveform. In combination with flow measurements, these results may be useful for predicting regions susceptible to thrombus formation within ventricular assist devices. PMID:24721222

  8. Electrical, thermal and structural properties of plasticized waste cooking oil-based polyurethane solid polymer electrolyte

    Science.gov (United States)

    Huzaizi, Rahmatina Mohd; Tahir, Syuhada Mohd; Mahbor, Kamisah Mohamad

    2017-12-01

    Waste cooking oil-based polyol was synthesized using epoxidation and hydroxylation methods. The polyol was combined with 4,4-diphenylmethane diisocyanate to produce polyurethane (PU) to be used as polymer host in solid polymer electrolyte. 30 wt% LiClO4 was added as doping salt and two types of plasticizers were used; ethylene carbonate (PU-EC) and polyethylene glycol (PU-PEG). The SPE films were characterized using Fourier transform infrared spectroscopy, electrochemical impedance spectroscopy, differential scanning calorimetry (DSC) and X-ray diffraction (XRD). The highest conductivity achieved was 8.4 x 10-8 S cm-1 upon addition of 10 wt% EC. The XRD results showed a decrease of crystalline peaks in PU-EC and the increase in PU-PEG. DSC results revealed that the films; PU, PU-EC and PU-PEG had glass transition temperatures of 159.7, 106.0 and 179.7 °C, respectively. The results showed that the addition of EC increased the amorphous region and the free volume in the SPE structure, thus resulted in higher ionic conductivity.

  9. Structure-property studies of thermoplastic and thermosetting polyurethanes using palm and soya oils-based polyols.

    Science.gov (United States)

    Mohammed, Issam Ahmed; Al-Mulla, Emad Abbas Jaffar; Kadar, Nurul Khizien Abdul; Ibrahim, Mazlan

    2013-01-01

    Palm and soya oils were converted to monoglycerides via transesterification of triglycerides with glycerol by one step process to produce renewable polyols. Thermoplastic polyurethanes (TPPUs) were prepared from the reaction of the monoglycerides which act as polyol with 4,4'-methylenediphenyldiisocyanate (MDI) whereas, thermosetting polyurethanes (TSPUs) were prepared from the reaction of glycerol, MDI and monoglycerides in one pot. Characterization of the polyurethanes was carried out by FT-IR, (1)H NMR, and iodine value and sol-gel fraction. The TSPUs showed good thermal properties compared to TPPUs as well as TSPUs exhibits good properties in pencil hardness and adhesion, however poorer in flexural and impact strength compared to TPPUs. The higher percentage of cross linked fraction, the higher degree of cross linking occurred, which is due to the higher number of double bond presents in the TSPUs. These were reflected in iodine value test as the highest iodine value of the soya-based thermosetting polyurethanes confirmed the highest degree of cross linking. Polyurethanes based on soya oil showed better properties compared to palm oil. This study is a breakthrough development of polyurethane resins using palm and soya oils as one of the raw materials.

  10. Studies on polyurethane adhesives and surface modification of hydrophobic substrates

    Science.gov (United States)

    Krishnamoorthy, Jayaraman

    This thesis work deals with (a) Curing of reactive, hot-melt polyurethane adhesives and (b) Adsorption studies using different interactions. Research on polyurethanes involves characterization of polyurethane prepolymers and a novel mechanism to cure isocyanate-terminated polyurethane prepolymer by a "trigger" mechanism. Curing of isocyanate-terminated polyurethane prepolymers has been shown to be influenced by morphology and environmental conditions such as temperature and relative humidity. Although the initial composition, final morphology and curing kinetics are known, information regarding the intermediate prepolymer mixture is yet to be established. Polyurethane prepolymers prepared by the reaction of diisocyanates with the primary hydroxyls of polyester diol (PHMA) and secondary hydroxyls of polyether diol (PPG) were characterized. The morphology and crystallization kinetics of a polyurethane prepolymer was compared with a blend of PPG prepolymer (the product obtained by the reaction of PPG with diisocyanate) and a PHMA prepolymer (the product obtained by the reaction of PHMA with diisocyanate) to study the effect of copolymer formed in the polyurethane prepolymer on the above-mentioned properties. Although the morphology of the polyurethane prepolymer is determined in the first few minutes of application, the chemical curing of isocyanate-terminated prepolymer occurs over hours to days. In the literature, different techniques are described to follow the curing kinetics. But there is no established technique to control the curing of polyurethane prepolymer. To make the curing process independent of environmental factors, a novel approach using a trigger mechanism was designed and implemented by using ammonium salts as curing agents. Ammonium salts that are stable at room temperature but decompose on heating to yield active hydrogen-containing compounds, NH3 and H2O, were used as 'Trojan horses' to cure the prepolymer chemically. Research on adsorption

  11. Aluminum and steel adhesion with polyurethanes from castor oil adhesives submitted to gamma irradiation

    International Nuclear Information System (INIS)

    Azevedo, Elaine C.; Assumpcao, Roberto L.; Nascimento, Eduardo M. do; Claro Neto, Salvador; Soboll, Daniel S.

    2009-01-01

    Polyurethanes adhesive from castor oil is used to join aluminum and steel pieces. The effect of gamma radiation on the resistance to tension tests is investigated. The aluminum and steel pieces after being glued with the adhesive were submitted to gamma irradiation in doses of 1 kGy, 25 kGy and 100 kGy. The rupture strength of the joints after irradiation have a slightly increase or remains practically unchanged indicating that the adhesive properties is not affected by the gamma radiation. (author)

  12. Soybean-oil-based waterborne polyurethane dispersions: effects of polyol functionality and hard segment content on properties.

    Science.gov (United States)

    Lu, Yongshang; Larock, Richard C

    2008-11-01

    The environmentally friendly vegetable-oil-based waterborne polyurethane dispersions with very promising properties have been successfully synthesized without difficulty from a series of methoxylated soybean oil polyols (MSOLs) with different hydroxyl functionalities ranging from 2.4 to as high as 4.0. The resulting soybean-oil-based waterborne polyurethane (SPU) dispersions exhibit a uniform particle size, which increases from about 12 to 130 nm diameter with an increase in the OH functionality of the MSOL from 2.4 to 4.0 and decreases with increasing content of the hard segments. The structure and thermophysical and mechanical properties of the resulting SPU films, which contain 50-60 wt % MSOL as renewable resources, have been studied by Fourier transform infrared spectroscopy, differential scanning calorimetry, dynamic mechanical analysis, thermogravimetric analysis, transmission electron microscopy, and mechanical testing. The experimental results reveal that the functionality of the MSOLs and the hard segment content play a key role in controlling the structure and the thermophysical and mechanical properties of the SPU films. These novel films exhibit tensile stress-strain behavior ranging from elastomeric polymers to rigid plastics and possess Young's moduli ranging from 8 to 720 MPa, ultimate tensile strengths ranging from 4.2 to 21.5 MPa, and percent elongation at break values ranging from 16 to 280%. This work has addressed concerns regarding gelation and higher cross-linking caused by the high functionality of vegetable-oil-based polyols. This article reports novel environmentally friendly biobased SPU materials with promising applications as decorative and protective coatings.

  13. Platelet adhesion studies on dipyridamole coated polyurethane surfaces

    Directory of Open Access Journals (Sweden)

    Aldenhoff Y. B.J.

    2003-06-01

    Full Text Available Surface modification of polyurethanes (PUs by covalent attachment of dipyridamole (Persantinregistered is known to reduce adherence of blood platelets upon exposure to human platelet rich plasma (PRP. This effect was investigated in further detail. First platelet adhesion under static conditions was studied with four different biomaterial surfaces: untreated PU, PU immobilised with conjugate molecule 1, PU immobilised with conjugate molecule 2, and PU immobilised with conjugate molecule 3. In PU immobilised with 1 dipyridamole is directly linked to the surface, in PU immobilised with 2 there is a short hydrophilic spacer chain in between the surface and the dipyridamole, while conjugate molecule 3 is merely the spacer chain. Scanning electron microscopy (SEM was used to characterise platelet adhesion from human PRP under static conditions, and fluorescence imaging microscopy was used to study platelet adhesion from whole blood under flow. SEM experiments encompassed both density measurements and analysis of the morphology of adherent platelets. In the static experiments the surface immobilised with 2 showed the lowest platelet adherence. No difference between the three modified surfaces emerged from the flow experiments. The surfaces were also incubated with washed blood platelets and labeled with Oregon-Green Annexin V. No capture of Oregon-Green Annexin V was seen, implying that the adhered platelets did not expose any phosphatidyl serine at their exteriour surface.

  14. Preparation and characterization of novel antibacterial castor oil-based polyurethane membranes for wound dressing application.

    Science.gov (United States)

    Yari, Abbas; Yeganeh, Hamid; Bakhshi, Hadi; Gharibi, Reza

    2014-01-01

    Preparation of novel antibacterial and cytocompatible polyurethane membranes as occlusive dressing, which can provide moist and sterile environment over mild exudative wounds is considered in this work. In this regard, an epoxy-terminated polyurethane (EPU) prepolymer based on castor oil and glycidyltriethylammonium chloride (GTEAC) as a reactive bactericidal agent were synthesized. Polyurethane membranes were prepared through cocuring of EPU and different content of GTEAC with 1,4-butane diamine. The physical and mechanical properties, as well as cytocompatibility and antibacterial performance of prepared membranes were studied. Depending on their chemical formulations, the equilibrium water absorption and water vapor transmission rate values of the membranes were in ranges of 3-85% and 53-154g m(-2) day(-1), respectively. Therefore, these transparent membranes can maintain for a long period the moist environment over the wounds with low exudates. Detailed cytotoxicity analysis of samples against mouse L929 fibroblast and MCA-3D keratinocyte cells showed good level of cytocompatibility of membranes after purification via extraction of residual unreacted GTEAC moieties. The antibacterial activity of the membranes against Escherichia coli and Staphylococcus aureus bacteria was also studied. The membrane containing 50% GTEAC exhibited an effective antibacterial activity, while showed acceptable cytocompatibility and therefore, can be applied as an antibacterial occlusive wound dressing. Copyright © 2013 Wiley Periodicals, Inc., a Wiley Company.

  15. Transport behavior of n-alkane penetrants into castor oil based polyurethane-polyester nonwoven fabric composites

    International Nuclear Information System (INIS)

    Satheesh Kumar, M.N.; Manjula, K.S.; Siddaramaiah

    2007-01-01

    Castor oil based polyurethane (PU)-polyester nonwoven fabric composites were fabricated by impregnating the polyester nonwoven fabric in a composition containing castor oil and diisocyanate. Composites were fabricated with two different isocyanates such as toluene-2,4-diisocyanate (TDI) and hexamethylene diisocyanate (HMDI). Transport behavior of n-alkane penetrants (pentane, hexane and heptane) into both PUs and PU-polyester nonwoven fabric composites were studied. Sorption studies were carried out at different temperatures. From the sorption results, the diffusion (D) and permeation (P) coefficients of penetrants have been calculated. Significant increase in the diffusion and permeation coefficients was observed with increase in the temperature of sorption experiments. Drastical reduction in diffusion and permeation coefficients was noticed in the composites compared to neat PUs. Attempts were made to estimate the empirical parameters like n, which suggests the mode of transport and K is a constant depends on the structural characteristics of the composite in addition to its interaction with penetrants. The temperature dependence of the transport coefficients has been used to estimate the activation energy parameter for diffusion (E D ) and permeation (E P ) processes from Arrhenius plots. Furthermore, the sorption results have been interpreted in terms of the thermodynamic parameters such as enthalpy (ΔH) and entropy (ΔS)

  16. Characterization of adhesive of polyurethane from castor oil by FTIR, TGA and XRD

    International Nuclear Information System (INIS)

    Azevedo, Elaine C.; Santana, Simone S. de M.; Nascimento, Eduardo M. do; Claro Neto, Salvador; Lepienski, Carlos M.

    2009-01-01

    Castor oil polyurethanes are an alternative to adhesives that emanate volatile compounds. This adhesive come from a renewable source and has very low toxicity. In this work the microstructural and thermal characterization is presented. This material is partially crystalline. The mass loss start at 240 deg C and the glass transition temperature is 60 deg C. Then the adhesive is adequate to be employed at temperatures lower than 60 deg C. (author)

  17. Double-chain phospholipid end-capped polyurethanes: Synthesis, characterization and platelet adhesion study

    International Nuclear Information System (INIS)

    Tan Dongsheng; Zhang Xiaoqing; Li Jiehua; Tan Hong; Fu Qiang

    2012-01-01

    A novel phospholipid containing double chains and phosphotidylcholine polar head groups, 2-(10-(2-aminoethylamino)-10-oxodecanamido)-3-(decyloxy)-3-oxopropyl phosphorylcholine (ADDPC), was synthesized and characterized. Two kinds of double-chain phospholipid end-capped polyurethanes with different soft segments were prepared. The structure of prepared polyurethanes was characterized by X-ray photoelectron spectroscopic (XPS), attenuated total reflection Fourier transform infrared (ATR-FTIR) spectrometry and atomic force microscope (AFM), which indicated that the double-chain phospholipids enriched onto the top surface of the prepared polyurethane films. The preliminary evaluation of blood compatibility showed that these novel phospholipid end-capped polyurethanes could suppress platelet adhesion and activation effectively. This property did not depend on the chemical structure of polyurethanes. In addition, according to tensile test results, the phospholipid polyurethanes kept good mechanical properties in comparison with original polyurethanes. It is suggested that double-chain phospholipid end-caption has good potential for achieving both hemocompatibility and good mechanical properties simultaneously for polyurethanes.

  18. Effect of tackifier and crosslinkers on electron beam curable polyurethane pressure sensitive adhesive

    International Nuclear Information System (INIS)

    Kumar Singh, Anil; Singh Mehra, Dayal; Kumar Niyogi, Utpal; Sabharwal, Sunil; Kumar Khandal, Rakesh

    2012-01-01

    Polyurethane based pressure sensitive adhesive using monofunctional urethane acrylate and difunctional urethane acrylate has been made using electron beam irradiation. The effect of varying electron beam doses on the adhesion properties viz., peel adhesion, shear adhesion and initial tack has been studied. Effect of tackifier and crosslinkers viz., polymeric methylene diphenyl diisocynate, carbodiimide modified methylene diphenyl diisocynate and triallyl cynurate on adhesion properties as well as on moisture vapor transmission rate and gel content of the polyurethane based pressure sensitive adhesive has also been studied. It was found that with increasing dose, tackifier and crosslinkers concentration, all the adhesion properties viz., peel adhesion, shear adhesion strength and initial tack were increased upto a certain dose, concentration of tackifier and crosslinkers, reached a plateau and then levelled off with further increasing the dose, tackifier and crosslinkers concentration. Similarly, moisture vapor transmission rate was decreased and the gel content increased with increasing dose of electron beam. - Highlights: ► The optimized e-beam dose was 20 kGy. ► Optimized concentration of tackifier was 15% while PMDI, CMDI 6% and TAC 4%. ► CMDI has highest while TAC has lowest adhesion properties. ► Tackifier has highest while TAC has lowest MVTR. ► TAC has highest while tackifier has lowest gel content.

  19. Strength and durability of one-part polyurethane adhesive bonds to wood

    Science.gov (United States)

    C. B. Vick; E. A. Okkonen

    1998-01-01

    One-part polyurethane wood adhesives comprise a new class of general purpose consumer products. Manufacturersa claims of waterproof bonds brought many inquiries to the Forest Products Laboratory (FPL) from users constructing aircraft, boats, lawn furniture, and other laminated materials for outdoor use. Although FPL has technical information on several types of...

  20. Design of Xylose-Based Semisynthetic Polyurethane Tissue Adhesives with Enhanced Bioactivity Properties.

    Science.gov (United States)

    Balcioglu, Sevgi; Parlakpinar, Hakan; Vardi, Nigar; Denkbas, Emir Baki; Karaaslan, Merve Goksin; Gulgen, Selam; Taslidere, Elif; Koytepe, Suleyman; Ates, Burhan

    2016-02-01

    Developing biocompatible tissue adhesives with high adhesion properties is a highly desired goal of the tissue engineering due to adverse effects of the sutures. Therefore, our work involves synthesis, characterization, adhesion properties, protein adsorption, in vitro biodegradation, in vitro and in vivo biocompatibility properties of xylose-based semisynthetic polyurethane (NPU-PEG-X) bioadhesives. Xylose-based semisynthetic polyurethanes were developed by the reaction among 4,4'-methylenebis(cyclohexyl isocyanate) (MCI), xylose and polyethylene glycol 200 (PEG). Synthesized polyurethanes (PUs) showed good thermal stability and high adhesion strength. The highest values in adhesion strength were measured as 415.0 ± 48.8 and 94.0 ± 2.8 kPa for aluminum substrate and muscle tissue in 15% xylose containing PUs (NPU-PEG-X-15%), respectively. The biodegradation of NPU-PEG-X-15% was also determined as 19.96 ± 1.04% after 8 weeks of incubation. Relative cell viability of xylose containing PU was above 86%. Moreover, 10% xylose containing NPU-PEG-X (NPU-PEG-X-10%) sample has favorable tissue response, and inflammatory reaction between 1 and 6 weeks implantation period. With high adhesiveness and biocompatibility properties, NPU-PEG-X can be used in the medical field as supporting materials for preventing the fluid leakage after abdominal surgery or wound closure.

  1. Polyurethane structural adhesives applied in automotive composite joints

    Directory of Open Access Journals (Sweden)

    Josue Garcia Quini

    2012-06-01

    Full Text Available In recent years structural adhesives technology has demonstrated great potential for application due to its capacity to transform complex structures into solid unitary and monolithic assemblies using different materials. Thus, seams or joints integrate these structures providing, besides a reduction in weight, a considerable increase in the mechanical resistance and stiffness. The increase in the industrial use of structural adhesives is mainly due to their ability to efficiently bond different materials in an irreversible manner, even replacing systems involving mechanical joints. In the automobile industry structural adhesives have been widely used for the bonding of metal substrates, thermoplastics and composites, frequently employing these in combination, particularly glass fiber and polyester resin composites molded using RTM and SMC processes. However, the use of urethane structural adhesives in applications involving composites and thermoplastics has been the subject of few investigations. In this study the effects of temperature and time on the shear strength of RTM, SMC and ABS joints, applying temperatures of -40, 25, 80, 120 and 177 °C and times of 20 minutes and 500 hours, were determined. The objective was to evaluate the performance under extreme conditions of use in order to assess whether these joints could be used in passenger or off-road vehicles. The results showed that the urethane structural adhesive promoted the efficient bonding of these materials, considering that due to the high adhesive strength the failures occurred in the substrates without adversely affecting the bonded area. For each test condition the joint failure modes were also determined.

  2. Study of the aging processes in polyurethane adhesives using thermal treatment and differential calorimetric, dielectric, and mechanical techniques ; 1, identifying the aging processes ; 2, quantifying the aging effect

    CERN Document Server

    Althouse, L P

    1979-01-01

    Study of the aging processes in polyurethane adhesives using thermal treatment and differential calorimetric, dielectric, and mechanical techniques ; 1, identifying the aging processes ; 2, quantifying the aging effect

  3. Waterborne polyurethane-acrylic hybrid nanoparticles by miniemulsion polymerization: applications in pressure-sensitive adhesives.

    Science.gov (United States)

    Lopez, Aitziber; Degrandi-Contraires, Elise; Canetta, Elisabetta; Creton, Costantino; Keddie, Joseph L; Asua, José M

    2011-04-05

    Waterborne polyurethane-acrylic hybrid nanoparticles for application as pressure-sensitive adhesives (PSAs) were prepared by one-step miniemulsion polymerization. The addition of polyurethane to a standard waterborne acrylic formulation results in a large increase in the cohesive strength and hence a much higher shear holding time (greater than seven weeks at room temperature), which is a very desirable characteristic for PSAs. However, with the increase in cohesion, there is a decrease in the relative viscous component, and hence there is a decrease in the tack energy. The presence of a small concentration of methyl methacrylate (MMA) in the acrylic copolymer led to phase separation within the particles and created a hemispherical morphology. The tack energy was particularly low in the hybrid containing MMA because of the effects of lower energy dissipation and greater cross-linking. These results highlight the great sensitivity of the viscoelastic and adhesive properties to the details of the polymer network architecture and hence to the precise composition and synthesis conditions.

  4. Breathability studies of electron beam curable polyurethane pressure sensitive adhesive for bio-medical application

    International Nuclear Information System (INIS)

    Singh, Anil Kumar; Mehra, Dayal Singh; Niyogi, Utpal Kumar; Sabharwal, Sunil; Singh, Gurdeep

    2014-01-01

    Polyurethane (PU) based pressure sensitive adhesive (PSA) commonly used in surgical dressing has been made by electron beam (e-beam) irradiation. In contact with biological substrate like skin, PSAs generally lose their adhesive strength due to very low moisture vapor transmission rate (MVTR). In the present study, effects of varying e-beam dose and different crosslinkers on the MVTR of the PU-PSA have been investigated. A comparative study of effects of different crosslinkers showed that PU-PSA with IPDI has the least while that with TAC has the highest gel content and crystallinity and a reverse trend was observed for the MVTR. - Highlights: • On increasing e-beam dose from 5 kGy to 60 kGy the MVTR decreased continuously. • Increasing crosslinker concentration from 2% to10% resulted in decrease of MVTR. • IPDI has the highest and TAC has the least MVTR in PU-PSA system among the crosslinkers. • MVTR/peel adhesion/shear adhesion/initial tack: IPDI>MDI>CMDI>PMDI>TAIC>TAC. • Gel content/T g /crystallinity: TAC>TAIC>PMDI>CMDI>MDI>IPDI

  5. Thermal and mechanical properties of palm oil-based polyurethane acrylate/clay nanocomposites prepared by in-situ intercalative method and electron beam radiation

    International Nuclear Information System (INIS)

    Salih, A. M.; Ahmad, Mansor Bin; Ibrahim, Nor Azowa; Dahlan, Khairul Zaman Hj Mohd; Tajau, Rida; Mahmood, Mohd Hilmi; Yunus, Wan Md. Zin Wan

    2014-01-01

    Palm oil based-polyurethane acrylate (POBUA)/clay nanocomposites were prepared via in-situ intercalative polymerization using epoxidized palm oil acrylate (EPOLA) and 4,4' methylene diphenyl diisocyante (MDI). Organically modified Montmorillonite (ODA-MMT) was incorporated in EPOLA (1, 3 and 5%wt), and then subjected to polycondensation reaction with MDI. Nanocomposites solid films were obtained successfully by electron beam radiation induced free radical polymerization (curing). FTIR results reveal that the prepolymer was obtained successfully, with nanoclay dispersed in the matrix. The intercalation of the clay in the polymer matrix was investigated by XRD and the interlayer spacing of clay was found to be increased up to 37 Å, while the structure morphology of the nanocomposites was investigated by TEM and SEM. The nanocomposites were found to be a mixture of exfoliated and intercalated morphologies. The thermal stability of the nanocomposites was significantly increased by incorporation of nanoclay into the polymer matrix. DSC results reveal that the Tg was shifted to higher values, gradually with increasing the amount of filler in the nanocomposites. Tensile strength and Young's modulus of the nanocomposites showed remarkable improvement compared to the neat POBUA

  6. Thermal and mechanical properties of palm oil-based polyurethane acrylate/clay nanocomposites prepared by in-situ intercalative method and electron beam radiation

    Energy Technology Data Exchange (ETDEWEB)

    Salih, A. M. [Department of Chemistry, Faculty of Science, University Putra Malaysia 43400, UPM, Serdang, Selangor, Malaysia and Department of Radiation Processing, Sudan Atomic Energy Commission, Khartoum 1111 (Sudan); Ahmad, Mansor Bin; Ibrahim, Nor Azowa [Department of Chemistry, Faculty of Science, University Putra Malaysia 43400, UPM, Serdang, Selangor (Malaysia); Dahlan, Khairul Zaman Hj Mohd [Polycomposite Sdn Bhd, No.75-2, Jalan TKS 1, Taman Kajang Sentral, 43000 Kajang, Selangor (Malaysia); Tajau, Rida [Radiation Processing Technology Division, Nuclear Malaysia, Bangi, 43000 Kajang, Selangor (Malaysia); Mahmood, Mohd Hilmi [No. 107, Jalan 2, Taman Kajang Baru, Sg Jelok, 43000 Kajang, Selangor (Malaysia); Yunus, Wan Md. Zin Wan [Department of Chemistry, Centre for Defence Foundation Studies, National Defence University of Malaysia, 57000, Sungai Besi Camp, Kuala Lumpur (Malaysia)

    2014-02-12

    Palm oil based-polyurethane acrylate (POBUA)/clay nanocomposites were prepared via in-situ intercalative polymerization using epoxidized palm oil acrylate (EPOLA) and 4,4' methylene diphenyl diisocyante (MDI). Organically modified Montmorillonite (ODA-MMT) was incorporated in EPOLA (1, 3 and 5%wt), and then subjected to polycondensation reaction with MDI. Nanocomposites solid films were obtained successfully by electron beam radiation induced free radical polymerization (curing). FTIR results reveal that the prepolymer was obtained successfully, with nanoclay dispersed in the matrix. The intercalation of the clay in the polymer matrix was investigated by XRD and the interlayer spacing of clay was found to be increased up to 37 Å, while the structure morphology of the nanocomposites was investigated by TEM and SEM. The nanocomposites were found to be a mixture of exfoliated and intercalated morphologies. The thermal stability of the nanocomposites was significantly increased by incorporation of nanoclay into the polymer matrix. DSC results reveal that the Tg was shifted to higher values, gradually with increasing the amount of filler in the nanocomposites. Tensile strength and Young's modulus of the nanocomposites showed remarkable improvement compared to the neat POBUA.

  7. Thermal and mechanical properties of palm oil-based polyurethane acrylate/ clay nano composites prepared by in-situ intercalative method and electron beam radiation

    International Nuclear Information System (INIS)

    Salih, A.M.; Mansor Ahmad; Nor Azowa Ibrahim; Rida Tajau; Wan Mohd Zin Wan Yunus

    2013-01-01

    Full-text: Palm oil based-polyurethane acrylate (POBUA)/ clay nano composites were prepared via in-situ intercalative polymerization using epoxidized palm oil acrylate (EPOLA) and 4,4 ' methylene diphenyl diisocyante (MDI). Organically modified Montmorillonite (ODA-MMT) was incorporated in EPOLA (1, 3 and 5 % wt), and then subjected to polycondensation reaction with MDI. Nano composites solid films were obtained successfully by electron beam radiation induced free radical polymerization (curing). FTIR results reveal that the prepolymer was obtained successfully, with nano clay dispersed in the matrix. The intercalation of the clay in the polymer matrix was investigated by XRD and the interlayer spacing of clay was found to be increased up to 37 Angstrom, while the structure morphology of the nano composites was investigated by TEM and SEM. The nano composites were found to be a mixture of exfoliated and intercalated morphologies. The thermal stability of the nano composites was significantly increased by incorporation of nano clay into the polymer matrix. DSC results reveal that the T g was shifted to higher values, gradually with increasing the amount of filler in the nano composites. Tensile strength and Young's modulus of the nano composites showed remarkable improvement compared to the neat POBUA. (author)

  8. Radiation curable pressure sensitive adhesives (PSA) formulations from palm oil based resin

    International Nuclear Information System (INIS)

    Mohd Hilmi Mahmood; Rosley Che Ismail; Khairul Zaman Mohd Dahlan

    2000-01-01

    Various low glass transition temperature (T g ) acrylate and methacrylate monomers were mixed with epoxidised palm oil acrylate (EPOLA) with the ratio of 50/50 prior to curing with electron beam (EB) irradiation. Methacrylate monomers such as dicyclopentenyloxyethyl methacrylate (DCPOEMA) and isobornyl methacrylate (ISBMA), although displaying relatively higher adhesive properties compared to others were finally excluded from being further utilised as monomers for PSA because of a very slow curing speed. Literally, it is suggested that poorer adhesive performances of the cured films made from 50/50:EPOLA/monomer mixture as compared to that of 100% monomer was attributed to the lack of compatibility between EPOLA and the particular monomers. Further compatibility investigations were continued using formulations prepared via prepolymer route cured by ultraviolet (UV) irradiation and the results showed that several monoacrylate monomers with polar and non-polar groups exhibited high curing speed as well as good compatibility with EPOLA as shown by their cured film properties such as surface tackiness, peel adhesion and creep resistance. It is also suggested that these monomers were acting as surfactants for EPOLA which consequently enhance their compatibility upon mixing. Earlier results of the studies on the use of several tackifiers such as poly(vinylmethylether) (PVME), liquid epoxidised natural rubber (LENR) and acrylic oligomer based active tackifier (IRR-153) in the PSA formulations showed that the addition of tackifiers, particularly 3 to 50% IRR-153 into the PSA formulations (while maintaining palm oil contents at 50% ) significantly improved the adhesive properties of cured films. The use qf tackifiers also reducing or eliminating the needs to employ prepolymer method in preparing PSA formulations since most of their viscosities are already above the optimum level (>500 Cps at 25 degree C)

  9. Production on pressure sensitive adhesives (PSA) from palm oil based resin - a prepolymer method

    International Nuclear Information System (INIS)

    Mohd Hilmi Mahmood; Zahid Abdullah; Khairul Zaman Mohd Dahlan; Yasuo Sakurai

    1999-01-01

    Various low T sub g acrylate and methacrylate monomers were mixed with epoxidized palm oil acrylate (EPOLA) with the ratio of 50/50 prior to curing with an electron beam (EB) irradiation. Methacrylate monomers such as dicyclopentenyloxyethyl methacrylate (DCPOEMA) and isobornyl methacrylate (ISBMA), although displayed relatively high adhesive properties but were finally excluded from being further utilised as monomers for PSA because of a very slow curing speed. Literally, it is suggested that poorer adhesive performances of the cured films made from 50/50:EPOLA/monomer mixture as compared to that of 100% monomer was attributed to the lack of compatibility between EPOLA and that particular monomers. Further compatibility investigations were continued using formulations prepared via prepolymer route cured by an ultraviolet (UV) irradiation and the results showed that several monoacrylate monomers with polar and non-polar groups exhibited high curing speed as well as good compatibility with EPOLA as shown by their cured film properties such as; surface tackiness, peel adhesion and creep resistance. It is also suggested that these monomers were acting as surfactants for EPOLA which consequently enhance their compatibility upon mixing

  10. Decreased astroglial cell adhesion and proliferation on zinc oxide nanoparticle polyurethane composites

    Directory of Open Access Journals (Sweden)

    Justin T Seil

    2008-11-01

    Full Text Available Justin T Seil, Thomas J WebsterLaboratory for Nanomedicine Research, Division of Engineering, Brown University, Providence, RI, USAAbstract: Nanomaterials offer a number of properties that are of interest to the field of neural tissue engineering. Specifically, materials that exhibit nanoscale surface dimensions have been shown to promote neuron function while simultaneously minimizing the activity of cells such as astrocytes that inhibit central nervous system regeneration. Studies demonstrating enhanced neural tissue regeneration in electrical fields through the use of conductive materials have led to interest in piezoelectric materials (or those materials which generate a transient electrical potential when mechanically deformed such as zinc oxide (ZnO. It has been speculated that ZnO nanoparticles possess increased piezoelectric properties over ZnO micron particles. Due to this promise in neural applications, the objective of the present in vitro study was, for the first time, to assess the activity of astroglial cells on ZnO nanoparticle polymer composites. ZnO nanoparticles embedded in polyurethane were analyzed via scanning electron microscopy to evaluate nanoscale surface features of the composites. The surface chemistry was characterized via X-ray photoelectron spectroscopy. Astroglial cell response was evaluated based on cell adhesion and proliferation. Astrocyte adhesion was significantly reduced on ZnO nanoparticle/polyurethane (PU composites with a weight ratio of 50:50 (PU:ZnO wt.%, 75:25 (PU:ZnO wt.%, and 90:10 (PU:ZnO wt.% in comparison to pure PU. The successful production of ZnO nanoparticle composite scaffolds suitable for decreasing astroglial cell density demonstrates their potential as a nerve guidance channel material with greater efficiency than what may be available today.Keywords: zinc oxide, nanoparticles, astrocytes, neural tissue, nervous system, biomaterials

  11. Decreased astroglial cell adhesion and proliferation on zinc oxide nanoparticle polyurethane composites

    Science.gov (United States)

    Seil, Justin T; Webster, Thomas J

    2008-01-01

    Nanomaterials offer a number of properties that are of interest to the field of neural tissue engineering. Specifically, materials that exhibit nanoscale surface dimensions have been shown to promote neuron function while simultaneously minimizing the activity of cells such as astrocytes that inhibit central nervous system regeneration. Studies demonstrating enhanced neural tissue regeneration in electrical fields through the use of conductive materials have led to interest in piezoelectric materials (or those materials which generate a transient electrical potential when mechanically deformed) such as zinc oxide (ZnO). It has been speculated that ZnO nanoparticles possess increased piezoelectric properties over ZnO micron particles. Due to this promise in neural applications, the objective of the present in vitro study was, for the first time, to assess the activity of astroglial cells on ZnO nanoparticle polymer composites. ZnO nanoparticles embedded in polyurethane were analyzed via scanning electron microscopy to evaluate nanoscale surface features of the composites. The surface chemistry was characterized via X-ray photoelectron spectroscopy. Astroglial cell response was evaluated based on cell adhesion and proliferation. Astrocyte adhesion was significantly reduced on ZnO nanoparticle/polyurethane (PU) composites with a weight ratio of 50:50 (PU:ZnO) wt.%, 75:25 (PU:ZnO) wt.%, and 90:10 (PU:ZnO) wt.% in comparison to pure PU. The successful production of ZnO nanoparticle composite scaffolds suitable for decreasing astroglial cell density demonstrates their potential as a nerve guidance channel material with greater efficiency than what may be available today. PMID:19337420

  12. Surface grafting of carboxylic groups onto thermoplastic polyurethanes to reduce cell adhesion

    Energy Technology Data Exchange (ETDEWEB)

    Alves, P., E-mail: palves@eq.uc.pt [CIEPQPF, Departamento de Engenharia Química, Universidade de Coimbra, Polo II, Pinhal de Marrocos, 3030-790 Coimbra (Portugal); Ferreira, P. [CIEPQPF, Departamento de Engenharia Química, Universidade de Coimbra, Polo II, Pinhal de Marrocos, 3030-790 Coimbra (Portugal); Kaiser, Jean-Pierre [EMPA, St. Gallen, Lerchenfeldstrasse 5, CH-9014 St. Gallen (Switzerland); Salk, Natalie [Mikrofertigung – Micro Engineering, Fraunhofer IFAM, Wiener Strasse 12, D-288359 Bremen (Germany); Bruinink, Arie [EMPA, St. Gallen, Lerchenfeldstrasse 5, CH-9014 St. Gallen (Switzerland); Sousa, Hermínio C. de; Gil, M.H. [CIEPQPF, Departamento de Engenharia Química, Universidade de Coimbra, Polo II, Pinhal de Marrocos, 3030-790 Coimbra (Portugal)

    2013-10-15

    The interaction of polymers with other materials is an important issue, being their surface properties clearly crucial. For some important polymer applications, their surfaces have to be modified. Surface modification aims to tailor the surface characteristics of a material for a specific application without affecting its bulk properties. Materials can be surface modified by using biological, chemical or physical methods. The aim of this work was to improve the reactivity of the thermoplastic polyurethane (TPU) material (Elastollan{sup ®}) surface and to make its surface cell repellent by grafting carboxylic groups onto its surface. Two TPU materials were studied: a polyether-based TPU and a polyester-based TPU. The grafting efficiency was evaluated by contact angle measurements and by analytical determination of the COOH groups. Scanning electron microscopy (SEM) of the membranes surface was performed as well as cell adhesion tests. It was proved that the surfaces of the TPUs membranes were successfully modified and that cell adhesion was remarkably reduced.

  13. A novel silanized CoFe{sub 2}O{sub 4}/fluorinated waterborne polyurethane pressure sensitive adhesive

    Energy Technology Data Exchange (ETDEWEB)

    Fu, Heqing, E-mail: fuhq@scut.edu.cn; Wang, Yin; Chen, Weifeng; Zhou, Wei; Xiao, Jing

    2015-10-01

    Highlights: • The hydrophobicity, thermal stability, dynamic mechanical properties, as well as adhesive properties of silanized. • CoFe{sub 2}O{sub 4}/fluorinated waterborne polyurethane (SC/FWPU) were improved with the incorporation of silanized CoFe{sub 2}O{sub 4} into FWPU. • The higher the spreading-penetration parameter is, the faster the contact angle reaches equilibrium, and the faster the SC/FWPU pressure sensitive adhesive penetrates and spreads. - Abstract: A novel silanized CoFe{sub 2}O{sub 4}/fluorinated waterborne polyurethane (SC/FWPU) pressure sensitive adhesive was synthesized and characterized by atomic force microscopy (AFM), thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA) and contact angle tester. The adhesive properties were measured in a test machine. Experimental results showed that the hydrophobicity, thermal stability, dynamic mechanical properties, as well as adhesive properties of SC/FWPU were improved with the incorporation of SC into FWPU. The dynamic hydrophobicity can be well described by the wetting kinetic model. The spreading-penetration parameter increased with an increase in SC content. The higher the spreading-penetration parameter is, the faster the contact angle reaches equilibrium, and the faster the SC/FWPU pressure sensitive adhesive penetrates and spreads.

  14. The relationship between cellular adhesion and surface roughness for polyurethane modified by microwave plasma radiation

    Directory of Open Access Journals (Sweden)

    Heidari S

    2011-04-01

    Full Text Available Saeed Heidari Keshel1, S Neda Kh Azhdadi2, Azadeh Asefnezhad2, Mohammad Sadraeian3, Mohamad Montazeri4, Esmaeil Biazar51Stem Cell Preparation Unit, Eye Research Center, Farabi Eye Hospital, Tehran University of Medical Sciences; 2Department of Biomaterial Engineering, Faculty of Biomedical Engineering, Science and Research Branch - Islamic Azad University; 3Young Researchers Club, Islamic Azad University, North Tehran Branch, Tehran; 4Faculty of Medical Sciences, Babol University of Medical Sciences, Babol; 5Department of Chemistry, Islamic Azad University, Tonekabon, IranAbstract: Surface modification of medical polymers is carried out to improve biocompatibility. In this study, conventional polyurethane was exposed to microwave plasma treatment with oxygen and argon gases for 30 seconds and 60 seconds. Attenuated total reflection Fourier transform infrared spectra investigations of irradiated samples indicated the presence of functional groups. Atomic force microscope images of samples irradiated with inert and active gases indicated the nanometric topography of the sample surfaces. Samples irradiated by oxygen plasma indicated high roughness compared with those irradiated by inert plasma for the different lengths of time. In addition, surface roughness increased with time, which can be due to a reduction of contact angle of samples irradiated by oxygen plasma. Contact angle analysis indicated a reduction in samples irradiated with both types of plasma. However, samples irradiated with oxygen plasma indicated lower contact angle compared with those irradiated by argon plasma. Cellular investigations with unrestricted somatic stem cells showed better adhesion, cell growth, and proliferation among samples radiated by oxygen plasma for longer than for normal samples.Keywords: surface topography, polyurethane, plasma treatment, cellular investigation

  15. Investigation of a Biocompatible Polyurethane-Based Isotropically Conductive Adhesive for UHF RFID Tag Antennas

    Science.gov (United States)

    Yang, Cheng; Yuen, Matthew M. F.; Gao, Bo; Ma, Yuhui; Wong, C. P.

    2011-01-01

    As a candidate dispersant for silver-based isotropically conductive adhesives (ICAs), polyurethane (PU) is an environmentally benign material that can withstand a high deformation rate and that exhibits excellent reliability. In this work we investigated methyl ethyl ketoxime (MEKO) blocked isophorone diisocyanate (IPDI) and MEKO blocked hexamethylene diisocyanate (HDI) as dispersant materials, and we characterize the electrical conductivity, mechanical properties, and reliability of these PU-based ICAs with silver-flake filler content ranging from 30 wt.% to 75 wt.%. Results of temperature-humidity testing (THT) at 85°C and 85% relative humidity (RH) and thermal cycling testing (TCT) at -40°C to 125°C show that these ICAs have excellent reliability. Our experimental results suggest that the MEKO blocked PU dispersants are suitable for preparing ultralow-cost, flexible, high-performance ICAs for printing antennas for ultrahigh-frequency radiofrequency identification (RFID) tags. These tags can potentially be used for identifying washable items and food packaging.

  16. Propriedades mecânicas do cimento ósseo e da poliuretana de mamona com e sem catalisador Mechanical properties of bone cement and castor oil-based polyurethane with and without a catalyst

    Directory of Open Access Journals (Sweden)

    A.F.M. Lima

    2008-10-01

    Full Text Available Avaliou-se o comportamento mecânico do polímero de mamona, tendo por variáveis o tempo de produção e a presença de catalisador, e utilizando como padrão comparativo o cimento ósseo (polimetilmetacrilato. Foram estabelecidos três grupos experimentais, de acordo com o tipo de corpo de prova (cilindro ou barra e polímero utilizado, que foram posteriormente subdivididos em subgrupos conforme o tempo após produção, ou seja, 24, 48 e 72 horas. O ensaio de compressão analisou a carga máxima e a tensão e o ensaio de dobramento estudou o módulo de dobramento e a resistência. Estatisticamente não houve diferenças nos valores de resistência à compressão ou ao dobramento às 24, 48 e 72 horas após a produção do polimetilmetacrilato e da poliuretana, com ou sem catalisador. A poliuretana com catalisador foi a mais resistente nos ensaios de compressão, apresentando módulo de dobramento semelhante ao do polimetilmetacrilato e resistência ao dobramento superior à da poliuretana sem catalisador. Conclui-se que: o tempo não alterou as propriedades mecânicas dos compósitos avaliados; o catalisador melhorou o desempenho mecânico da poliuretana de mamona; na resistência mecânica à compressão, a poliuretana com catalisador suportou mais carga que o polimetilmetacrilato.The mechanical properties of castor oil-based polyurethane was evaluated considering post-production time and the presence of a catalyst as variables and using bone cement (polymethylmetacrylate as a comparative pattern. According to proof body type (cylinders or bars and the used polymer, three experimental groups were established. Such groups were later subdivided according to post-production time, namely, 24, 48, and 72 hours. A compression assay analyzed maximum load and tension, and a folding assay evaluated the folding module and resistance. There were no statistical differences in the values for resistance to compression or folding at 24, 48, and 72 hours

  17. Novel amphiphilic poly(dimethylsiloxane) based polyurethane networks tethered with carboxybetaine and their combined antibacterial and anti-adhesive property

    Energy Technology Data Exchange (ETDEWEB)

    Jiang, Jingxian; Fu, Yuchen; Zhang, Qinghua, E-mail: qhzhang@zju.edu.cn; Zhan, Xiaoli; Chen, Fengqiu

    2017-08-01

    Highlights: • An amphiphilic poly(dimethylsiloxane) (PDMS) based polyurethane (PU) network tethered with carboxybetaine is prepared. • The surface distribution of PDMS and zwitterionic segments produces an obvious amphiphilic heterogeneous surface. • This designed PDMS-based amphiphilic PU network exhibits combined antibacterial and anti-adhesive properties. - Abstract: The traditional nonfouling materials are powerless against bacterial cells attachment, while the hydrophobic bactericidal surfaces always suffer from nonspecific protein adsorption and dead bacterial cells accumulation. Here, amphiphilic polyurethane (PU) networks modified with poly(dimethylsiloxane) (PDMS) and cationic carboxybetaine diol through simple crosslinking reaction were developed, which had an antibacterial efficiency of 97.7%. Thereafter, the hydrolysis of carboxybetaine ester into zwitterionic groups brought about anti-adhesive properties against bacteria and proteins. The surface chemical composition and wettability performance of the PU network surfaces were investigated by attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), X-ray photoelectron spectroscopy (XPS) and contact angle analysis. The surface distribution of PDMS and zwitterionic segments produced an obvious amphiphilic heterogeneous surface, which was demonstrated by atomic force microscopy (AFM). Enzyme-linked immunosorbent assays (ELISA) were used to test the nonspecific protein adsorption behaviors. With the advantages of the transition from excellent bactericidal performance to anti-adhesion and the combination of fouling resistance and fouling release property, the designed PDMS-based amphiphilic PU network shows great application potential in biomedical devices and marine facilities.

  18. Effect of structure and molecular weight on properties of pressure sensitive adhesives (PSA) formulated from palm oil based urethane acrylate (POBUA)

    International Nuclear Information System (INIS)

    Mohd Hilmi Mahmood; Shahrol Najmin Baharom; Rida Tajau; Mek Zah Salleh; Khairul Zaman Mohd Dahlan; Rosley Che Ismail

    2004-01-01

    Various palm oil (RBD Palm Olein) based urethane acrylate prepolymers (UPs) having different structures and molecular weight were synthesized from palm oil based polyols, diisocyanate compounds and hydroxyl terminated acrylate monomers by following established synthesis procedures described elsewhere. The products (UPs) were compared with each other in term of their molecular weight (MW), viscosities and UV curing performances of pressure sensitive adhesives (PSA) UP based formulations. The molecular structure of diisocyanate compounds and hydroxyl acrylate monomers tend to determine the molecular weight and hence viscosities of the final products of urethane acrylate prepolymers (UP), whereas, the MW of the UP has no direct effects on the coatings and adhesive properties of UV curable UP based PSA. (Author)

  19. Effect on Shear Strength of Machining Methods in Pinus nigra Arnold Bonded with Polyurethane and Polyvinyl Acetate Adhesives

    Directory of Open Access Journals (Sweden)

    Murat Kılıç

    2016-06-01

    Full Text Available Specimens taken from Pinus nigra Arnold were subject to surfacing techniques by being cut with a circular saw, planed with a thickness machine, and sanded with a calibrating sanding machine (with P80 grit sandpaper. First, their surface roughness values were measured; then, the specimens were processed in the machines in a radial and tangential process. Afterwards, the change in shear strength (adhesiveness resistance was analyzed as a result of bonding with various adhesive types (PVAc, PU and pressure applications (0.45 N/mm² or 0.9 N/mm². Approximately 600 specimens were prepared with the purpose of identifying the effect of variables on the bonding performance, and they were subjected to shear testing. The greatest shear strength achieved for both the tangential and radial surfaces in terms of cutting was observed in specimens processed in the thickness machine, on which polyvinyl acetate adhesive and 0.9 N/mm². pressure were applied. Specimens bonded with polyvinyl acetate adhesive displayed higher shear strength in general in comparison to those bonded with polyurethane for both tangential and radial surfaces.

  20. Mechanical Performance of Polyurethane and Epoxy Adhesives in Connections with Glued-in Rods at Elevated Temperatures

    Directory of Open Access Journals (Sweden)

    Mathieu Verdet

    2016-08-01

    Full Text Available Glued-in rods have successfully been used for connections or reinforcement of timber structures due to their high strength and stiffness. However, their performance is potentially sensitive to temperature. This paper deals with an experimental investigation of the connections and adhesives in elevated temperatures. First, dynamic mechanical analysis (DMA tests were performed to characterize an epoxy (EPX and a polyurethane (PUR adhesive. The evolution of the stiffness and the glass transition temperature, Tg, were measured in the range of 30 °C to 120 °C. Then, a total of 66 specimens with glued-in rods and the same adhesives were tested under a static tensile load at 20 °C, 40 °C, 50 °C, 60 °C, and 70 °C. In both types of tests, the EPX outperformed PUR due to its higher stiffness at temperatures of up to 40 °C; however, it showed a more rapid degradation of the stiffness and strength than the PUR at higher temperatures. No direct correlation was established between the Tg and the performance of the connections. The test results suggest that timber structures with glued-in rods may be vulnerable in service at temperatures above 40 °C.

  1. Study on the Heating Behavior of Fe_3O_4-Embedded Thermoplastic Polyurethane Adhesive Film via Induction heating

    International Nuclear Information System (INIS)

    Bae, Duck Hwan; Shon, Min Young; Oh, Sang Taek; Kim, Gu Ni

    2016-01-01

    The heating behavior of thermoplastic polyurethane adhesive (TPU) embedded by nanometer or micrometer Fe_3O_4 particle is examined by induction heating. The effects of the size and the amount of Fe_3O_4 particle, TPU film thickness, and input power of the induction heater were examined on heating behaviors of TPU. The quantity of heat generated in the TPU films increased with the amount of Fe_3O_4 particles, film thickness, or input power. On the other hand, the quantity of heat generation of TPU is decreased with increasing Fe_3O_4 size. We confirmed that the mechanism of hysteresis led to heat loss in the nanometer and micrometer-sized Fe_3O_4 particles, and it was the key controller of the quantity of heat generated in the Fe_3O_4 particle-embedded TPU films by induction heating.

  2. Physical properties of a high molecular weight hydroxyl-terminated polydimethylsiloxane modified castor oil based polyurethane/epoxy interpenetrating polymer network composites

    Science.gov (United States)

    Chen, Shoubing; Wang, Qihua; Wang, Tingmei

    2011-06-01

    A series of polyurethane (PU)/epoxy resin (EP) graft interpenetrating polymer network (IPN) composites modified by a high molecular weight hydroxyl-terminated polydimethylsiloxane (HTPDMS) were prepared. The effects of HTPDMS content on the phase structure, damping properties and the glass transition temperature ( Tg) of the HTPDMS-modified PU/EP IPN composites were studied by scanning electron microscopy (SEM) and dynamic mechanical analysis (DMA). Thermogravimetric analysis (TGA) showed that the thermal decomposition temperature of the composites increased with the increase of HTPDMS content. The tensile strength and impact strength of the IPN composites were also significantly improved, especially when the HTPDMS content was 10%. The modified IPN composites were expected to be used as structural damping materials in the future.

  3. Novel amphiphilic poly(dimethylsiloxane) based polyurethane networks tethered with carboxybetaine and their combined antibacterial and anti-adhesive property

    Science.gov (United States)

    Jiang, Jingxian; Fu, Yuchen; Zhang, Qinghua; Zhan, Xiaoli; Chen, Fengqiu

    2017-08-01

    The traditional nonfouling materials are powerless against bacterial cells attachment, while the hydrophobic bactericidal surfaces always suffer from nonspecific protein adsorption and dead bacterial cells accumulation. Here, amphiphilic polyurethane (PU) networks modified with poly(dimethylsiloxane) (PDMS) and cationic carboxybetaine diol through simple crosslinking reaction were developed, which had an antibacterial efficiency of 97.7%. Thereafter, the hydrolysis of carboxybetaine ester into zwitterionic groups brought about anti-adhesive properties against bacteria and proteins. The surface chemical composition and wettability performance of the PU network surfaces were investigated by attenuated total reflectance Fourier transform infrared spectroscopy (ATR-FTIR), X-ray photoelectron spectroscopy (XPS) and contact angle analysis. The surface distribution of PDMS and zwitterionic segments produced an obvious amphiphilic heterogeneous surface, which was demonstrated by atomic force microscopy (AFM). Enzyme-linked immunosorbent assays (ELISA) were used to test the nonspecific protein adsorption behaviors. With the advantages of the transition from excellent bactericidal performance to anti-adhesion and the combination of fouling resistance and fouling release property, the designed PDMS-based amphiphilic PU network shows great application potential in biomedical devices and marine facilities.

  4. Preparation and Characterization of Graphene Oxide-Modified Sapium sebiferum Oil-Based Polyurethane Composites with Improved Thermal and Mechanical Properties

    Directory of Open Access Journals (Sweden)

    Guiying Wu

    2018-01-01

    Full Text Available Bio-based polyurethane (PU composites with superior thermal and mechanical properties have received wide attention. This is due to the recent rapid developments in the PU industry. In the work reported here, novel nano-composites with graphene oxide (GO-modified Sapium sebiferum oil (SSO-based PU has been synthesized via in situ polymerization. GO, prepared using the improved Hummers method from natural graphene (NG, and SSO-based polyol with a hydroxyl value of 211 mg KOH/g, prepared by lipase hydrolysis, were used as raw materials. The microstructures and properties of GO and the nano-composites were both characterized using Fourier transform infrared spectroscopy (FTIR, Raman spectroscopy, X-ray diffraction (XRD, transmission electron microscopy (TEM, scanning electron microscopy (SEM, thermogravimetric analysis (TGA, differential scanning calorimetry (DSC, and tensile tests. The results showed that GO with its nano-sheet structure possessed a significant number of oxygen-containing functional groups at the surface. The nano-composites containing 1 wt % GO in the PU matrix (PU1 exhibited excellent comprehensive properties. Compared with those for pure PU, the glass transition temperature (Tg and initial decomposition temperature (IDT of the PU1 were enhanced by 14.1 and 31.8 °C, respectively. In addition, the tensile strength and Young’s modulus of the PU1 were also improved by 126% and 102%, respectively, compared to the pure PU. The significant improvement in both the thermal stability and mechanical properties for PU/GO composites was attributed to the homogeneous dispersion and good compatibility of GO with the PU matrix. The improvement in the properties upon the addition of GO may be attributable to the strong interfacial interaction between the reinforcing agent and the PU matrix.

  5. QUALITY OF Pinus elliottii PARTICLE BOARDS BONDED WITH POLYURETHANE ADHESIVE UNDER VARIOUS COMBINATIONS OF TEMPERATURE AND PRESSURE

    Directory of Open Access Journals (Sweden)

    Juarez Benigno Paes

    2011-09-01

    Full Text Available This work aimed to produce homogeneous layer particle boards with residues of Pinus elliottii wood adhered with polyurethane adhesive to castor oil plant base and to evaluate the effect of the combination of pressure and temperature in the quality of the particle boards produced. To do so, 12 particle boards were manufactured, subdivided into four treatments in function of the pressure (2.0; 3.0; 3.5; and 3.5 MPa and temperature (90; 90; 50; and 60 ºC. The particleboards were sectioned in test samples, and accomplished by physical-mechanical tests for the determination of density, swelling and absorption of water (0-2h; 2-24h; e 0-24h; rupture module and elasticity module in static bending, internal ligation and screw withdrawal. The particle boards pressed with pressure of 3.0 MPa and temperature of 90 ºC and that with pressure of 3.5 MPa and temperature of 60 ºC presented the best  results. The higher temperature of pressing was the predominant variable in the quality of those particle boards manufactured.

  6. Adhesive compositions and methods

    Science.gov (United States)

    Allen, Scott D.; Sendijarevic, Vahid; O'Connor, James

    2017-12-05

    The present invention encompasses polyurethane adhesive compositions comprising aliphatic polycarbonate chains. In one aspect, the present invention encompasses polyurethane adhesives derived from aliphatic polycarbonate polyols and polyisocyanates wherein the polyol chains contain a primary repeating unit having a structure:. In another aspect, the invention provides articles comprising the inventive polyurethane compositions as well as methods of making such compositions.

  7. The effects of the structure and molecular weight of the macrodiol on the properties polyurethane anionic adhesives

    Czech Academy of Sciences Publication Activity Database

    Cakić, S. M.; Ristić, I. S.; Marinović-Cincović, M.; Špírková, Milena

    2013-01-01

    Roč. 41, March (2013), s. 132-139 ISSN 0143-7496 R&D Projects: GA ČR GAP108/10/0195 Institutional support: RVO:61389013 Keywords : polyurethane * thermal analysis * phase separation Subject RIV: CD - Macromolecular Chemistry Impact factor: 2.216, year: 2013

  8. Adhesion strength between thermoplastics and its polyurethane coating made by using the technology combination of injection molding and reaction injection molding

    Science.gov (United States)

    Bloß, P.; Böhme, A.; Müller, J.; Krajewsky, P.; Michaelis, J.

    2014-05-01

    A complete equipment for injection molding (IM) of a thermoplastic (TP) carrier and reaction injection molding (RIM) of polyurethane (PUR) coatings including IM and RIM machines, a color module for PUR, and a robot was built up. A modularly composed sliding split mold was constructed and manufactured allowing different parts including thicker (2 mm thickness) soft touch and thin (0.4 mm) lacquer PUR coatings. As TP PC/ABS and PA6 GF15 compounds were used, and aromatic and aliphatic PUR systems as well. From the parts made by IM+RIM, test specimens for peel force measurements were cut. These investigations were performed prior and after ageing under climatic conditions @ 50 % RH and temperature changes between -30 °C and 90 °C. By varying IM processing parameters, we have found that mold and TP temperatures are particularly important for the adhesion strength between TP and PUR. The waiting time between the end of TP cooling and PUR injection has a minor influence on its mean value. However, to short waiting times may result in inhomogeneous adhesion. It was surprising that surface defects of the TP carrier leads also to inhomogeneous adhesion. We have observed that ageing may cause an increase and decrease of adhesions strength depending on the TP+PUR system used. We have found that the results are valid only for the actual TP and PUR combination. A generalization seems to be inappropriate, hence, the actual combination should be investigated to prevent unwanted surprises when the coated TP part is in its application.

  9. The Load-Bearing Capacity of Timber-Glass Composite I-Beams Made with Polyurethane Adhesives

    Science.gov (United States)

    Rodacki, Konrad

    2017-12-01

    This article discusses the issue of composite timber-glass I-beams, which are an interesting alternative for load-bearing beams of ceilings and roofs. The reasoning behind the use of timber-glass I-beams is the combination of the best features of both materials - this enables the creation of particularly safe beams with regard to structural stability and post-breakage load capacity. Due to the significant differences between the bonding surfaces of timber and glass, a study on the adhesion of various adhesives to both surfaces is presented at the beginning of the paper. After examination, two adhesives were selected for offering the best performance when used with composite beams. The beams were investigated using a four-point bending test under quasi-static loading.

  10. Adhesion

    Science.gov (United States)

    ... Supplements Videos & Tools Español You Are Here: Home → Medical Encyclopedia → Adhesion URL of this page: //medlineplus.gov/ency/article/001493.htm Adhesion To use the sharing features on this page, please enable JavaScript. Adhesions are bands of scar-like tissue that form between two ...

  11. Study on the Heating Behavior of Fe{sub 3}O{sub 4}-Embedded Thermoplastic Polyurethane Adhesive Film via Induction heating

    Energy Technology Data Exchange (ETDEWEB)

    Bae, Duck Hwan; Shon, Min Young [Pukyong National University, Busan (Korea, Republic of); Oh, Sang Taek; Kim, Gu Ni [Korea Institute of Footwear and Leather Technology, Busan (Korea, Republic of)

    2016-08-15

    The heating behavior of thermoplastic polyurethane adhesive (TPU) embedded by nanometer or micrometer Fe{sub 3}O{sub 4} particle is examined by induction heating. The effects of the size and the amount of Fe{sub 3}O{sub 4} particle, TPU film thickness, and input power of the induction heater were examined on heating behaviors of TPU. The quantity of heat generated in the TPU films increased with the amount of Fe{sub 3}O{sub 4} particles, film thickness, or input power. On the other hand, the quantity of heat generation of TPU is decreased with increasing Fe{sub 3}O{sub 4} size. We confirmed that the mechanism of hysteresis led to heat loss in the nanometer and micrometer-sized Fe{sub 3}O{sub 4} particles, and it was the key controller of the quantity of heat generated in the Fe{sub 3}O{sub 4} particle-embedded TPU films by induction heating.

  12. Cardiomyocyte behavior on biodegradable polyurethane/gold nanocomposite scaffolds under electrical stimulation

    Energy Technology Data Exchange (ETDEWEB)

    Ganji, Yasaman [Faculty of Biomedical Engineering, Amirkabir University of Technology, 424 Hafez Ave, Tehran (Iran, Islamic Republic of); Institute for Materials Science, Dept. Biocompatible Nanomaterials, University of Kiel, Kaiserstr. 2, D-24143 Kiel (Germany); Li, Qian [Institute for Materials Science, Dept. Biocompatible Nanomaterials, University of Kiel, Kaiserstr. 2, D-24143 Kiel (Germany); Quabius, Elgar Susanne [Dept. of Otorhinolaryngology, Head and Neck Surgery, University of Kiel, Arnold-Heller-Str. 3, Building 27, D-24105 Kiel (Germany); Institute of Immunology, University of Kiel, Arnold-Heller-Str. 3, Building 17, D-24105 Kiel (Germany); Böttner, Martina [Department of Anatomy, University of Kiel, Otto-Hahn-Platz 8, 24118 Kiel (Germany); Selhuber-Unkel, Christine, E-mail: cse@tf.uni-kiel.de [Institute for Materials Science, Dept. Biocompatible Nanomaterials, University of Kiel, Kaiserstr. 2, D-24143 Kiel (Germany); Kasra, Mehran [Faculty of Biomedical Engineering, Amirkabir University of Technology, 424 Hafez Ave, Tehran (Iran, Islamic Republic of)

    2016-02-01

    Following a myocardial infarction (MI), cardiomyocytes are replaced by scar tissue, which decreases ventricular contractile function. Tissue engineering is a promising approach to regenerate such damaged cardiomyocyte tissue. Engineered cardiac patches can be fabricated by seeding a high density of cardiac cells onto a synthetic or natural porous polymer. In this study, nanocomposite scaffolds made of gold nanotubes/nanowires incorporated into biodegradable castor oil-based polyurethane were employed to make micro-porous scaffolds. H9C2 cardiomyocyte cells were cultured on the scaffolds for one day, and electrical stimulation was applied to improve cell communication and interaction in neighboring pores. Cells on scaffolds were examined by fluorescence microscopy and scanning electron microscopy, revealing that the combination of scaffold design and electrical stimulation significantly increased cell confluency of H9C2 cells on the scaffolds. Furthermore, we showed that the gene expression levels of Nkx2.5, atrial natriuretic peptide (ANF) and natriuretic peptide precursor B (NPPB), which are functional genes of the myocardium, were up-regulated by the incorporation of gold nanotubes/nanowires into the polyurethane scaffolds, in particular after electrical stimulation. - Highlights: • Biodegradable polyurethane/gold nanocomposites for cardiomyocyte adhesion are proposed. • The nanocomposite scaffolds are porous and electrical stimulation enhances cell adhesion. • Expression levels of functional myocardium genes were upregulated after electrical stimulation.

  13. Evaluation of castor oil-based polyurethane membranes in rat bone-marrow cell culture Avaliação de membranas à base de óleo de polímero de mamona em culturas de células de medula óssea de ratos

    Directory of Open Access Journals (Sweden)

    Sofia de Amorim Cerejo

    2011-10-01

    Full Text Available PURPOSE: To evaluate three methods to isolate rats MSCs and to analyze the potential of a castor oil polyurethane base membrane as a scaffold for MSCs. METHODS: Four male Wistar rats, aged 20-30 days were used. Bone marrow aspirates from femur and tibia were harvested using DMEM high glucose and heparin. The cell culture was performed in three different ways: direct culture and two types of density gradients. After 15 days, was made the 1st passage and analyzed cell viability with markers Hoerscht 33342 and propidium iodide. The MSCs were characterized by surface markers with the aid of flow cytometry. After this, three types of castor oil polyurethane membranes associated with the MSCs were kept on the 6-well plate for 5 days and were analyzed by optical microscopy to confirm cell aggregation and growth. RESULTS: Separation procedures 1 and 2 allowed adequate isolation of MSCs and favored cell growth with the passage being carried out at 70% confluence after 15 days in culture. The cells could not be isolated using procedure 3. When the 3 castor oil polyurethane membrane types were compared it was possible to observe that the growth of MSCs was around 80% in membrane type 3, 20% in type 2, and 10% in type 1. CONCLUSION: Both Ficoll-Hypaque densities allow isolation of rat MSCs, and especially castor oil-based membrane type 3 may be used as a scaffold for MSCs.OBJETIVO: Avaliar três formas de cultivo de células-tronco mesenquimais de ratos; e analisar o potencial do polímero de mamona na forma de membrana como arcabouço para CTMs. MÉTODOS: Foram utilizados quatro ratos machos Wistar, de 20 a 30 dias de idade. Aspirados da medula óssea do fêmur e da tíbia foram colhidos com DMEM alta glicose e heparina. As células foram isoladas de três formas diferentes: cultivo direto e com dois tipos de gradientes de densidade. Após 15 dias, foi feita a 1ª passagem e analisada a viabilidade celular com os marcadores Hoerscht 33342 e Iodeto de Prop

  14. Mixed field radiation modification of polyurethanes based on castor oil

    International Nuclear Information System (INIS)

    Mortley, A.; Bonin, H.W.; Bui, V.T.

    2006-01-01

    Polyurethane is among the polymers and polymer-based composite materials being investigated at the Royal Military College of Canada for the fabrication of leak-tight containers for the long-term disposal of radioactive waste. Due to the long aliphatic chain of the castor oil component of polyurethane, thermal curing of castor oil based polyurethane (COPU) is limited by increasing polymer viscosity. To enhance further crosslinking, COPUs were subjected to a range of doses (0.0 - 3.0 MGy) produced by the mixed ionizing radiation field of a SLOWPOKE-2 research nuclear reactor. The tensile mechanical properties of castor oil based polyurethanes (COPU), unirradiated and irradiated, were characterized by mechanical tensile tests. Increases in mechanical strength due to radiation-induced crosslinking and limitations of thermal curing were confirmed by tensile tests and changing 13 C-NMR and FTIR spectra. (author)

  15. Mixed field radiation modification of polyurethanes based on castor oil

    Energy Technology Data Exchange (ETDEWEB)

    Mortley, A.; Bonin, H.W.; Bui, V.T. [Royal Military College of Canada, Dept. of Chemistry and Chemical Engineering, Kingston, Ontario (Canada)]. E-mail: aba.mortley@rmc.ca

    2006-07-01

    Polyurethane is among the polymers and polymer-based composite materials being investigated at the Royal Military College of Canada for the fabrication of leak-tight containers for the long-term disposal of radioactive waste. Due to the long aliphatic chain of the castor oil component of polyurethane, thermal curing of castor oil based polyurethane (COPU) is limited by increasing polymer viscosity. To enhance further crosslinking, COPUs were subjected to a range of doses (0.0 - 3.0 MGy) produced by the mixed ionizing radiation field of a SLOWPOKE-2 research nuclear reactor. The tensile mechanical properties of castor oil based polyurethanes (COPU), unirradiated and irradiated, were characterized by mechanical tensile tests. Increases in mechanical strength due to radiation-induced crosslinking and limitations of thermal curing were confirmed by tensile tests and changing {sup 13}C-NMR and FTIR spectra. (author)

  16. Effect of γ-radiation sterilization on the stability of polyurethane potting compounds based on castor oil/SMDI and caprolactone polyol/SMDI, used for hollow fibre haemodialyzer

    International Nuclear Information System (INIS)

    Jayabalan, M.; Lizymol, P.P.

    1997-01-01

    Stability of polyurethane potting compounds based on castor oil/SMDI and caprolactone polyol/SMDI in repeated gamma radiation sterilization was studied. Radiation-induced degradation and leaching of low molecular weight fragments are higher in castor oil based polyurethane than in caprolactone polyol based polyurethane. For castor oil and caprolactone polyol based polyurethanes degradation increases up to 5 Mrad dose of sterilization. Further increase of dose of sterilization decreases leaching in caprolactone polyol based polyurethane which has resulted from secondary reactions leading to crosslinking. In the case of castor oil based polyurethane such crosslinks undergo cleavage at 10 Mrad dose of sterilization. (author)

  17. THz Properties of Adhesives

    Science.gov (United States)

    Stübling, E.; Gomell, L.; Sommer, S.; Winkel, A.; Kahlmeyer, M.; Böhm, S.; Koch, M.

    2018-06-01

    We determined the THz properties of 12 different adhesives which are mainly used for industrial purposes. The adhesives applied can be classified according to their chemical structure: epoxy resins, acrylic resins, and polyurethane based materials. This work represents a basis for future studies, which will concentrate on aging effects, including the absorption of water of adhesive joints. Thus, the dielectric properties of the unaged adhesives are investigated and the results of these measurements are described herein.

  18. Síntesis y caracterización de adhesivos reposicionables de poliuretano dispersos en agua, obtenidos a partir de aceite de castor maleinizado Synthesis and characterization of pressure-sensitive adhesives of waterborne polyurethane from maleinizated castor oil

    Directory of Open Access Journals (Sweden)

    Paula Mazo

    2010-06-01

    evaluated for their mechanical and adhesive properties (tack, loop tack, hold, peel. These measurements allowed classifying the polyurethanes synthesized as repositionable adhesives, for use in labels.

  19. Synthesis and characterization of castor oil-based polyurethane for ...

    Indian Academy of Sciences (India)

    Administrator

    2School of Chemical Sciences and Food Technology, Faculty of Science and Technology,. Universiti Kebangsaan .... (THF) were supplied by R&M Marketing, Essex, UK, while 4 ... thoroughly with MDI using a digital magnetic stirrer at.

  20. Structures and Properties of Polyurethanes. Part II,

    Science.gov (United States)

    1979-03-23

    effect was observed for polymethyl methacrylate (222, 2721. The polyol, which contain fluorine , decrease adhesion, in spite DOC = 79011112 PAGE S4% of...small differences in the hardness of films on the basis of the fluorine -bearing polyol and generally accepted polyol. Is investigated the etfect ot...polyurethane, to rigid surface. DOC 79011112 P A * S The effect of the solvent, utilized for obtaining the varnish , on adhesion is investigated in

  1. Eficacia de un apósito autoadhesivo de poliuretano para prevenir la formación de cicatrices hipertróficas Efficacy of a polyurethane self-adhesive dressing in preventing hypertrophic scars

    Directory of Open Access Journals (Sweden)

    J. Bisbal

    2011-12-01

    Full Text Available Valoramos la eficacia de un apósito autoadhesivo para prevenir las cicatrices hipertróficas sobre un grupo de pacientes sometidas a cirugía de reducción mamaria. Tras la curación de las heridas, aplicamos en todas las pacientes un protocolo preventivo mediante compresión y apósito adhesivo: 66 pacientes (35,6±10,8 años de edad utilizaron Trofolastin® reductor de cicatrices como adhesivo (sujetos y 47 pacientes (38,7±12 años de edad fueron tratadas con otros adhesivos (controles. En el grupo control, el 23,4 % de los casos presentó cicatrices hipertróficas, mientras que en el grupo de sujetos el porcentaje fue sólo del 9,1 % (p Our goal is to evaluate the efficacy of a polyurethane self-adhesive dressing in preventing hypertrophic scars in a group of patients undergoing breast reduction surgery. After the initial wound healing period, all patients were submitted to the preventive procedure with compression and adhesive dressing: 66 patients (35.6±10.8 years old used Trofolastin® reduction scar as adhesive (subjects and 47 patients (38.7±12 years old were treated with other adhesives (controls. In the control group, 23.4 % of patients presented hypertrophic scars, whereas this percentage was only 9.1 % in subjects (p < 0.05. Moreover, 27 patients of the control group (56.5 % presented scars with a Vancouver score equal or higher than 4 in contrast with only 6 cases (9.1 % in the group of subjects (p < 0.0001. In conclusion, the prophylactic use of Trofolastin® reduction scar, once the initial wound healing period is complete, significantly reduces the risk of hypertrophic scars (relative risk 6.32 [95 % CI 2.83-14.09], according the Fisher's exact test.

  2. Bio-functionalized MWCNT/hyperbranched polyurethane bionanocomposite for bone regeneration

    International Nuclear Information System (INIS)

    Das, Beauty; Karak, Niranjan; Chattopadhyay, Pronobesh; Upadhyay, Aadesh; Maji, Somnath; Maity, Tapas Kumar; Purkayastha, Manashi Das; Mohanta, Charu lata

    2015-01-01

    The proper fabrication of biomaterials, particularly for purposes like bone regeneration, is of the utmost importance for the clinical success of materials that fulfill the design criteria at bio-interfacial milieu. Building on this aspect, a polyurethane nanocomposite (PNC) was fabricated by the combination of rapeseed protein functionalized multi-walled carbon nanotubes (MWCNTs) and vegetable-oil-based hyperbranched polyurethane. Biofunctionalized MWCNTs showed incredible biocompatibility compared to pristine MWCNTs as ascertained via in vitro and in vivo studies. PNC showed enhanced MG63 cell differentiation ability compared to the control and carboxyl functionalized MWCNT-based nanocomposite, as postulated by alkaline phosphatase activity together with better cellular adhesion, spreading and proliferation. Consequently, a critical-sized fracture gap (6 mm) bridged by the sticky PNC scaffold illustrated rapid bone neoformation within 30–45 d, with 90–93% of the defect area filling up. Histopathological studies demonstrated the reorganization of the normal tibial architecture and biodegradation of the implant. The subsequent toxicological study through cytokine expression, biochemical analysis and hematological studies suggested non-immunogenic and non-toxic effects of PNCs and their degraded/leached products. Their excellent bio-physiological features with high load-bearing ability (49–55.5 Mpa), ductility (675–790%) and biodegradability promote them as the best alternative biomaterials for bone regeneration in a comprehensive manner. (paper)

  3. Oil-based paint poisoning

    Science.gov (United States)

    Paint - oil-based - poisoning ... Hydrocarbons are the primary poisonous ingredient in oil paints. Some oil paints have heavy metals such as lead, mercury, cobalt, and barium added as pigment. These heavy metals can cause additional ...

  4. UV curable palm oil based inks

    International Nuclear Information System (INIS)

    Mek Zah Salleh; Hilmi Mahmood

    2002-01-01

    UV curable inks are useful for their instant drying, energy saving and high productivity properties. The basic materials for formulating UV curable inks consist of prepolymer, monomers, photoinitiators, pigments and other additives. The percentage composition and ingredients depend very much on the types of inks to be produced. Palm oil is one of the main raw materials available in the country. Hence, the diversification of palm oil derivatives into new products has been given priority. The current focus of the present work is to evaluate the use of palm oil based urethane acrylate (POBUA) as a prepolymer in the UV inks system. A study was conducted on the use of POBUA with other materials in ink formulation. These include the types and concentration of photoinitiators, monomers and commercial urethane acrylates. The evaluation of the ink properties such as curing, adhesion, color density have been carried out. It was found that POBUA could be introduced in the UV ink system. (Author)

  5. Influence of carbon source and inoculum type on anaerobic biomass adhesion on polyurethane foam in reactors fed with acid mine drainage.

    Science.gov (United States)

    Rodriguez, Renata P; Zaiat, Marcelo

    2011-04-01

    This paper analyzes the influence of carbon source and inoculum origin on the dynamics of biomass adhesion to an inert support in anaerobic reactors fed with acid mine drainage. Formic acid, lactic acid and ethanol were used as carbon sources. Two different inocula were evaluated: one taken from an UASB reactor and other from the sediment of a uranium mine. The values of average colonization rates and the maximum biomass concentration (C(max)) were inversely proportional to the number of carbon atoms in each substrate. The highest C(max) value (0.35 g TVS g(-1) foam) was observed with formic acid and anaerobic sludge as inoculum. Maximum colonization rates (v(max)) were strongly influenced by the type of inoculum when ethanol and lactic acid were used. For both carbon sources, the use of mine sediment as inoculum resulted in a v(max) of 0.013 g TVS g(-1) foam day(-1), whereas 0.024 g TVS g(-1) foam day(-1) was achieved with anaerobic sludge. Copyright © 2011 Elsevier Ltd. All rights reserved.

  6. Comparison of anti-corrosion properties of polyurethane based composite coatings with low infrared emissivity

    International Nuclear Information System (INIS)

    Wang Yajun; Xu Guoyue; Yu Huijuan; Hu Chen; Yan Xiaoxing; Guo Tengchao; Li Jiufen

    2011-01-01

    Four polyurethane resins, pure polyurethane (PU), epoxy modified polyurethane (EPU), fluorinated polyurethane (FPU) and epoxy modified fluorinated polyurethane (EFPU), with similar polyurethane backbone structure but different grafting group were used as organic adhesive for preparing low infrared emissivity coatings with an extremely low emissivity near 0.10 at 8-14 μm, respectively. By using these four resins, the effect of different resin matrics on the corrosion protection of the low infrared emissivity coatings was investigated in detail by using neutral salt spray test, SEM and FTIR. It was found that the emissivity of the coatings with different resin matrics changes significantly in corrosion media. And the results indicated that the coating using EFPU as organic adhesive exhibited excellent corrosion resistance property which was mainly attributed to the presence of epoxy group and atomic fluorine in binder simultaneously.

  7. Biobased composites from cross-linked soybean oil and thermoplastic polyurethane

    Science.gov (United States)

    Soybean oil is an important sustainable material. Crosslinked acrylated epoxidized soybean oil (AESO) is brittle and the incorporation of thermoplastic polyurethane improves its toughness. The hydrophilic functional groups from both oil and polyurethane contribute to the adhesion of the blend compon...

  8. Szycher's handbook of polyurethanes

    National Research Council Canada - National Science Library

    Szycher, M

    2013-01-01

    .... Filled with tables, charts, and photographs, it includes new data on green polyurethanes, automotive applications, new coatings, new manufacturing equipment, new health-care uses, and other topics...

  9. Polyurethane Filler for Electroplating

    Science.gov (United States)

    Beasley, J. L.

    1984-01-01

    Polyurethane foam proves suitable as filler for slots in parts electroplated with copper or nickel. Polyurethane causes less contamination of plating bath and of cleaning and filtering tanks than wax fillers used previously. Direct cost of maintenance and indirect cost of reduced operating time during tank cleaning also reduced.

  10. Nanoclay Dispersion and its Effect on Properties of Waterborne Polyurethanes

    Directory of Open Access Journals (Sweden)

    H. Honarkar

    2014-01-01

    Full Text Available In recent years, waterborne polyurethanes as in coatings and adhesives formulations have attracted considerable attention because they are non-toxic, non-flammable and friendly to environment. Besides environmental management, the flexibility, low temperature property, high tensile strength, good adhesion and improved rheological property are specific properties of waterborne polyurethanes. Also low production cost of water borne polyurethanes over solvent-borne polyurethanes is also a reason for their applications. However, these materials have some defects such as weak water resistance and low adhesion in the moisture environment due to sensitivity of their hydrophilic ionic bonds, ether groups, urethane and ester groups to hydrolysis which need to be improved. Also, low heat resistance of these materials is due to a relatively low crystalline melting point or glass transition temperature of hard segments. One of the ways to solve this problem and improve its properties for different applications is the addition of inorganic fillers especially nano-sized layered silicates within polyurethane matrix. In this way water resistance, heat resistance, mechanical properties and modulus increase simultaneously. In this research, waterborne polyurethane nanocomposites with PTMG polyol, IPDI, DMPA (internal emulsifier, TEA (neutralizer and 1, 3 and 5weight % of Cloisite 30B as reinforcement were synthesized and characterized. Polarity of the samples was investigated by contact angle test and dispersion of nano particles in the samples was characterized by X-Ray and TEM, Thermal properties and dynamic mechanical properties were measured by TGA and DMTA, respectively. The results showed that incorporation of clay into polyurethanes did reduce water absorption and increased heat resistance, modulus, particle size and contact angle.In recent years, waterborne polyurethanes including coatings and adhesives have attracted considerable attention because they

  11. Characterization studies of lower and non-TDI polyurethane encapsulants

    International Nuclear Information System (INIS)

    Wilson, M.H.

    1993-09-01

    Polyurethane prepolymers containing toluene diisocyanate (TDI) are used within the Nuclear Weapons complex for many adhesive and encapsulation applications. As part of a program for minimizing hazards to workers and the environment, TDI will be eliminated. This report presents evaluation of alternative encapsulants

  12. Polyurethane-Foam Maskant

    Science.gov (United States)

    Bodemeijer, R.

    1985-01-01

    Brown wax previously used to mask hardware replaced with polyurethane foam in electroplating and electroforming operations. Foam easier to apply and remove than wax and does not contaminate electrolytes.

  13. Szycher's handbook of polyurethanes

    National Research Council Canada - National Science Library

    Szycher, M

    2013-01-01

    "Written as a reference for polyurethane technologists and end users, raw materials suppliers, and students in the field, this second edition covers the technical advances in the field over the past 10 years...

  14. Hydrophilic polyurethane matrix promotes chondrogenesis of mesenchymal stem cells☆

    Science.gov (United States)

    Nalluri, Sandeep M.; Krishnan, G. Rajesh; Cheah, Calvin; Arzumand, Ayesha; Yuan, Yuan; Richardson, Caley A.; Yang, Shuying; Sarkar, Debanjan

    2016-01-01

    Segmental polyurethanes exhibit biphasic morphology and can control cell fate by providing distinct matrix guided signals to increase the chondrogenic potential of mesenchymal stem cells (MSCs). Polyethylene glycol (PEG) based hydrophilic polyurethanes can deliver differential signals to MSCs through their matrix phases where hard segments are cell-interactive domains and PEG based soft segments are minimally interactive with cells. These coordinated communications can modulate cell–matrix interactions to control cell shape and size for chondrogenesis. Biphasic character and hydrophilicity of polyurethanes with gel like architecture provide a synthetic matrix conducive for chondrogenesis of MSCs, as evidenced by deposition of cartilage-associated extracellular matrix. Compared to monophasic hydrogels, presence of cell interactive domains in hydrophilic polyurethanes gels can balance cell–cell and cell–matrix interactions. These results demonstrate the correlation between lineage commitment and the changes in cell shape, cell–matrix interaction, and cell–cell adhesion during chondrogenic differentiation which is regulated by polyurethane phase morphology, and thus, represent hydrophilic polyurethanes as promising synthetic matrices for cartilage regeneration. PMID:26046282

  15. Hydrophilic polyurethane matrix promotes chondrogenesis of mesenchymal stem cells.

    Science.gov (United States)

    Nalluri, Sandeep M; Krishnan, G Rajesh; Cheah, Calvin; Arzumand, Ayesha; Yuan, Yuan; Richardson, Caley A; Yang, Shuying; Sarkar, Debanjan

    2015-09-01

    Segmental polyurethanes exhibit biphasic morphology and can control cell fate by providing distinct matrix guided signals to increase the chondrogenic potential of mesenchymal stem cells (MSCs). Polyethylene glycol (PEG) based hydrophilic polyurethanes can deliver differential signals to MSCs through their matrix phases where hard segments are cell-interactive domains and PEG based soft segments are minimally interactive with cells. These coordinated communications can modulate cell-matrix interactions to control cell shape and size for chondrogenesis. Biphasic character and hydrophilicity of polyurethanes with gel like architecture provide a synthetic matrix conducive for chondrogenesis of MSCs, as evidenced by deposition of cartilage-associated extracellular matrix. Compared to monophasic hydrogels, presence of cell interactive domains in hydrophilic polyurethanes gels can balance cell-cell and cell-matrix interactions. These results demonstrate the correlation between lineage commitment and the changes in cell shape, cell-matrix interaction, and cell-cell adhesion during chondrogenic differentiation which is regulated by polyurethane phase morphology, and thus, represent hydrophilic polyurethanes as promising synthetic matrices for cartilage regeneration. Copyright © 2015 Elsevier B.V. All rights reserved.

  16. Polyurethane compounds having carbon nanotubes

    NARCIS (Netherlands)

    2010-01-01

    The invention relates to semi-crystalline polyurethane (PUR) compositions filled with carbon nanotubes (CNT) and having improved electrical properties, which can be obtained on the basis of water-based polyurethane/CNT mixtures. The invention further relates to a method for producing polyurethane

  17. Preparation and characterization of polyurethane plasticizer for flexible packaging applications: Natural oils affirmed access

    Directory of Open Access Journals (Sweden)

    Mohammed A. Mekewi

    2017-03-01

    Full Text Available Developing bio-renewable feedstock for polyurethane (PU manufacturing and polymer industry as a whole has become highly desirable for both economic and environmental reasons. In this work castor oil (CO and palm olein (PO polyols were synthesized and partially used as renewable feedstock for the manufacturing of polyurethane plasticizing resin for printing ink applications. The chemical structure of the prepared polyols and polyurethanes were characterized using IR spectra and GPC and their solubility in common solvents was tested. As well, properties such as flexibility, mechanical properties, optical properties, heat seal and freeze resistance of these prepared printing inks were determined. The results indicated that the prepared printing inks from 50% synthesized polyurethane have high thermal stability, adhesion and excellent freeze resistance. The net technical properties of the new ink formulations are relatively comparable to the printing ink prepared from standard polyurethane plasticizer.

  18. [In Situ Polymerization and Characterization of Hydroxyapatite/polyurethane Implanted Material].

    Science.gov (United States)

    Gu, Muqing; Xiao, Fengjuan; Liang, Ye; Yue, Lin; Li, Song; Li, Lanlan; Feng, Feifei

    2015-08-01

    In order to improve the interfacial bonding strength of hydroxyapatite/polyurethane implanted material and dispersion of hydroxyapatite in the polyurethane matrix, we in the present study synthesized nano-hydroxyapatite/polyurethane composites by in situ polymerization. We then characterized and analyzed the fracture morphology, thermal stability, glass transition temperature and mechanical properties. We seeded MG63 cells on composites to evaluate the cytocompatibility of the composites. In situ polymerization could improve the interfacial bonding strength, ameliorate dispersion of hydroxyapatite in the properties of the composites. After adding 20 wt% hydroxyapatite into the polyurethane, the thermal stability was improved and the glass transition temperatures were increased. The tensile strength and maximum elongation were 6.83 MPa and 861.17%, respectively. Compared with those of pure polyurethane the tensile strength and maximum elongation increased by 236.45% and 143.30%, respectively. The composites were helpful for cell adhesion and proliferation in cultivation.

  19. Biodegradation of polyurethanes; Polyurethane no biseibutsu bunkai

    Energy Technology Data Exchange (ETDEWEB)

    Kinpara, N; Ando, M; Ohira, Z [Suzuki Motor Corp., Shizuoka (Japan); Nakajima, T; Nakahara, T [University of Tsukuba, Tsukuba (Japan)

    1997-10-01

    Different types of Polyurethane (PUR) are used for various industrial products and are used in increasing quantities every year. We experimented with biodegradation of PURs to dispose of industrial wastes. 2 strains of fungi and 1 strain of bacteria which were seemed to have the ability to degrade PURs well were isolated from various soils and waste water. These strains could degrade ester-type PUR and PUR made from a mixture of ester and ether. However, these strains could not degrade ether-type PUR. From Scanning Electron Microscopy observation, it is suggested that the microbial degradation proceeded in at least 2 patterns. 4 refs., 8 figs., 2 tabs.

  20. Synthesis of waterborne, branched, functional poly(urethane)s and theire applications

    OpenAIRE

    Ongun, Nihan

    2014-01-01

    Polyurethanes are an important class of polymers that have wide application in a number of different industrial sectors. Their versatile chemistry enables researchers to design novel materials ranging from liquid, soft and rubbery solids to rigid thermoplastic and thermoset polymer for elastomeric materials, coating and adhesive. The present study focuses on synthesizing waterborne, branched and chemically functional polyurethanes with unique architectures via novel methodologies for coating ...

  1. Flexible polyurethane foams

    NARCIS (Netherlands)

    2012-01-01

    Embodiments of the invention provide for a method of preparing a polyurethane foam, including reacting least one initiator comprising at least two hydroxyl groups with at least one 12-hydroxystearic acid to form at least one polyester polyol, reacting the at least one polyester polyol with at least

  2. Wood : adhesives

    Science.gov (United States)

    A.H. Conner

    2001-01-01

    This chapter on wood adhesives includes: 1) Classification of wood adhesives 2) Thermosetting wood adhesives 3) Thermoplastic adhesives, 4) Wood adhesives based on natural sources 5) Nonconventional bonding of wood 6) Wood bonding.

  3. Microbial degradation of polyurethane, polyester polyurethanes and polyether polyurethanes.

    Science.gov (United States)

    Nakajima-Kambe, T; Shigeno-Akutsu, Y; Nomura, N; Onuma, F; Nakahara, T

    1999-02-01

    Polyurethane (PUR) is a polymer derived from the condensation of polyisocyanate and polyol and it is widely used as a base material in various industries. PUR, in particular, polyester PUR, is known to be vulnerable to microbial attack. Recently, environmental pollution by plastic wastes has become a serious issue and polyester PUR had attracted attention because of its biodegradability. There are many reports on the degradation of polyester PUR by microorganisms, especially by fungi. Microbial degradation of polyester PUR is thought to be mainly due to the hydrolysis of ester bonds by esterases. Recently, polyester-PUR-degrading enzymes have been purified and their characteristics reported. Among them, a solid-polyester-PUR-degrading enzyme (PUR esterase) derived from Comamonas acidovorans TB-35 had unique characteristics. This enzyme has a hydrophobic PUR-surface-binding domain and a catalytic domain, and the surface-binding domain was considered as being essential for PUR degradation. This hydrophobic surface-binding domain is also observed in other solid-polyester-degrading enzymes such as poly(hydroxyalkanoate) (PHA) depolymerases. There was no significant homology between the amino acid sequence of PUR esterase and that of PHA depolymerases, except in the hydrophobic surface-binding region. Thus, PUR esterase and PHA depolymerase are probably different in terms of their evolutionary origin and it is possible that PUR esterases come to be classified as a new solid-polyester-degrading enzyme family.

  4. Synthesis and Thermomechanical Properties of Polyurethanes and Biocomposites Derived from Macauba Oil and Coconut Husk Fibers

    OpenAIRE

    Quirino, Rafael; Silva, Taynara da; Payne, Amanda; Lopes, Roseany de V. V.; Paterno, Leonardo; Sales, Maria

    2015-01-01

    This work reports on a very effective route to produce bio-based polyurethanes (PUs) and composites with high content of renewable carbon sources. The PUs are prepared with polyols synthesized from macauba oil (Acrocomia aculeata) and methylene diphenyl diisocyanate, at different [NCO]/[OH] molar ratios. Later, biocomposites are prepared with the as-obtained PUs reinforced with coconut husk fibers. The successful synthesis of natural oil-based polyols is ascribed to the hydroxylation and cons...

  5. 21 CFR 177.1680 - Polyurethane resins.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 3 2010-04-01 2009-04-01 true Polyurethane resins. 177.1680 Section 177.1680 Food... of Single and Repeated Use Food Contact Surfaces § 177.1680 Polyurethane resins. The polyurethane...) For the purpose of this section, polyurethane resins are those produced when one or more of the...

  6. Synthesis and Physicochemical Behaviour of Polyurethane-Multiwalled Carbon Nanotubes Nanocomposites Based on Renewable Castor Oil Polyols

    Directory of Open Access Journals (Sweden)

    Alaa Ali

    2014-01-01

    Full Text Available Polyurethanes (PUs are high performance materials, with vast industrial and engineering applications. In this research, effects of Multiwalled Carbon Nanotubes (MWCNTs on physicochemical properties of Castor Oil based Polyurethanes (COPUs were studied. MWCNTs were added in different weight percentages (0% to 1% wt in a castor oil based polyurethane (COPUs-MWCNTs nanocomposites. The composition, structure, and morphology of polyurethanes were characterized by Fourier transform infrared spectroscopy (FTIR, X-ray diffraction (XRD, scanning electron microscopy (SEM, field emission scanning electron microscopy (FESEM, and element detection by energy dispersive spectroscopy (EDX analysis, respectively. Thermal stability was studied by thermogravimetric analysis (TGA. Barrier properties and surface area studies were investigated by nitrogen permeability machine and BET technique. Mechanical properties were calculated by tensile universal testing machine. Results showed well dispersed MWCNTs in polyurethane matrix at different weight percentages. The best results were obtained with 0.3 wt% of MWCNTs in the composite. Surface area studies revealed presence of very few pores which is in a good agreement with barrier permeability, reduced up to ~68% in 1 wt% and ~70% in 0.5 wt% of MWCNTs in polymer matrix, with respect to pure COPUs samples.

  7. Cell–material interactions on biphasic polyurethane matrix

    Science.gov (United States)

    Dicesare, Patrick; Fox, Wade M.; Hill, Michael J.; Krishnan, G. Rajesh; Yang, Shuying; Sarkar, Debanjan

    2013-01-01

    Cell–matrix interaction is a key regulator for controlling stem cell fate in regenerative tissue engineering. These interactions are induced and controlled by the nanoscale features of extracellular matrix and are mimicked on synthetic matrices to control cell structure and functions. Recent studies have shown that nanostructured matrices can modulate stem cell behavior and exert specific role in tissue regeneration. In this study, we have demonstrated that nanostructured phase morphology of synthetic matrix can control adhesion, proliferation, organization and migration of human mesenchymal stem cells (MSCs). Nanostructured biodegradable polyurethanes (PU) with segmental composition exhibit biphasic morphology at nanoscale dimensions and can control cellular features of MSCs. Biodegradable PU with polyester soft segment and hard segment composed of aliphatic diisocyanates and dipeptide chain extender were designed to examine the effect polyurethane phase morphology. By altering the polyurethane composition, morphological architecture of PU was modulated and its effect was examined on MSC. Results show that MSCs can sense the nanoscale morphology of biphasic polyurethane matrix to exhibit distinct cellular features and, thus, signifies the relevance of matrix phase morphology. The role of nanostructured phases of a synthetic matrix in controlling cell–matrix interaction provides important insights for regulation of cell behavior on synthetic matrix and, therefore, is an important tool for engineering tissue regeneration. PMID:23255285

  8. Hyaluronan Immobilized Polyurethane as a Blood Contacting Material

    Directory of Open Access Journals (Sweden)

    Feirong Gong

    2010-01-01

    Full Text Available Hyaluronan (hyaluronic acid, HA was immobilized onto the surface of amino-functionalized polyurethane films with the goal of obtaining a novel kind of biomaterial which had the potential in blood-contacting applications. The amino-functionalized polyurethane was prepared by synthesized acidic polyurethane whose pendant carboxyl groups were treated with an excess amount of 1,3-diaminopropane in the presence of N,N-carbonyldiimidazole (CDI. Attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR, Raman spectroscopy (RS, scanning electron microscopy (SEM, and water contact angle measurement were used to confirm the surface changes at each step of treatment, both in morphologies and chemical compositions. APTT and PT results showed that HA immobilization could prolong the blood coagulation time, thus HA-immobilized polyurethane (PU-HA exhibited improved blood compatibility. Cytotoxicity analysis showed that the PU-HA films synthesized in this study were cytocompatible and could support human vein endothelial cells (HUVECs adhesion and proliferation.

  9. TANNIN ADHESIVES AS AN ALTENATIVE TO THE SYNTHETIC PHENOLIC ADHESIVES

    Directory of Open Access Journals (Sweden)

    Semra Çolak

    2003-04-01

    Full Text Available Recently, increasing attention has been paid industrially to the use of tannin formaldehyde adhesives in production of wood based panel products such as particleboard, fiber board and plywood. The researches on the use of tannin extracts as a wood adhesive started in 1950, however, they proceeded very slowly since the problems associated with the application of them. The idea which tannin extract can be used replace the oil-based phenolic adhesive was the base of several studies after the oil crisis of the 1970s. In the past, the economical aspects were important in the researches on the tannin-based adhesives. Nowadays, however, both economical and ecological factors should have taken into consideration in wood bonding.

  10. Developement of Spherical Polyurethane Beads

    Institute of Scientific and Technical Information of China (English)

    K. Maeda; H. Ohmori; H. Gyotoku

    2005-01-01

    @@ 1Results and Discussion We established a new method to produce the spherical polyurethane beads which have narrower distribution of particle size. This narrower distribution was achieved by the polyurethane prepolymer which contains ketimine as a blocked chain-extending agent. Firstly, the prepolymer is dispersed into the aqueous solution containing surfactant. Secondaly, water comes into the inside of prepolymer as oil phase. Thirdly, ketimine is hydrolyzed to amine, and amine reacts with prepolymer immediately to be polyurethane.Our spherical polyurethane beads are very suitable for automotive interior parts especially for instrument panel cover sheet producing under the slush molding method, because of good process ability, excellent durability to the sunlight and mechanical properties at low temperature. See Fig. 1 ,Fig. 2 and Fig. 3 (Page 820).

  11. Elimination of the reactivation process in the adhesion of chlorinated SBS rubber with polychloroprene adhesives

    Directory of Open Access Journals (Sweden)

    2007-04-01

    Full Text Available Chlorination treatment of a thermoplastic styrene-butadiene-styrene rubber (SBS with a 3 wt% solution of trichloroisocyanuric acid (TCI in methyl ethyl ketone (MEK introduces chlorinated and oxidized moieties on the rubber surface which increase its surface energy and produces surface microroughness. Consequently adhesion properties, evaluated by T-peel strength measurements in chlorinated SBS/solvent based-polyurethane adhesive/leather joints, are enhanced. In this study, two solvent-based polychloroprene adhesives (PCP0 and PCP30R have been considered as an alternative to the commonly used solvent-based polyurethane adhesive (PU. A thermoreactive phenolic resin was added to one of the polychloroprene adhesive formulations (PCP30R. This tackifier resin favors chlorination of the adhesive and reinforces the interface between the chlorinated adhesive and the chlorinated rubber surface. Besides, PCP30R adhesive does not need adhesive reactivation and considerable high T-peel strength value (5.7±0.3 kN/m was obtained. Elimination of the reactivation process implies a considerable improvement of the manufacturing process in the footwear industry.

  12. Soil burial biodegradation studies of palm oil-based UV-curable films

    International Nuclear Information System (INIS)

    Tajau, Rida; Salleh, Mek Zah; Salleh, Nik Ghazali Nik; Abdurahman, Mohamad Norahiman; Salih, Ashraf Mohammed; Fathy, Siti Farhana; Azman, Anis Asmi; Hamidi, Nur Amira

    2016-01-01

    The palm oil-based ultraviolet (uv)-curable films were subjected to an outdoor soil burial test to investigate the biodegradation under natural environment. The films were burial in the soil experiment plot at the Nuclear Malaysia’s Dengkil complex. The uv-curable films were synthesized from the epoxidized palm oil acrylated (EPOLA) resin and the polyurethane palm oil (POBUA) resin, respectively. Biodegradation tests are more specific to burial film in soil experiments for 12 months under natural conditions. The biodegradability of palm oil resin based uv-curable films were investigated and compared with the petrochemical resin based film. The films properties were compared with respect to properties of the thermal characteristic, the crystallinity, the morphology and the weight loss which are analyzed using the thermogravimetric analysis (TGA), the differential scanning calorimetry (DSC), the scanning electron microscope (SEM), an optical microscope and the weight loss of film calculation. These findings suggested that the palm oil-based uv-curable films show quite satisfactory biodegradation levels

  13. Soil burial biodegradation studies of palm oil-based UV-curable films

    Science.gov (United States)

    Tajau, Rida; Salleh, Mek Zah; Salleh, Nik Ghazali Nik; Abdurahman, Mohamad Norahiman; Salih, Ashraf Mohammed; Fathy, Siti Farhana; Azman, Anis Asmi; Hamidi, Nur Amira

    2016-01-01

    The palm oil-based ultraviolet (uv)-curable films were subjected to an outdoor soil burial test to investigate the biodegradation under natural environment. The films were burial in the soil experiment plot at the Nuclear Malaysia's Dengkil complex. The uv-curable films were synthesized from the epoxidized palm oil acrylated (EPOLA) resin and the polyurethane palm oil (POBUA) resin, respectively. Biodegradation tests are more specific to burial film in soil experiments for 12 months under natural conditions. The biodegradability of palm oil resin based uv-curable films were investigated and compared with the petrochemical resin based film. The films properties were compared with respect to properties of the thermal characteristic, the crystallinity, the morphology and the weight loss which are analyzed using the thermogravimetric analysis (TGA), the differential scanning calorimetry (DSC), the scanning electron microscope (SEM), an optical microscope and the weight loss of film calculation. These findings suggested that the palm oil-based uv-curable films show quite satisfactory biodegradation levels.

  14. Soil burial biodegradation studies of palm oil-based UV-curable films

    Energy Technology Data Exchange (ETDEWEB)

    Tajau, Rida, E-mail: rida@nuclearmalaysia.gov.my; Salleh, Mek Zah, E-mail: mekzah@nuclearmalaysia.gov.my; Salleh, Nik Ghazali Nik, E-mail: nik-ghazali@nuclearmalaysia.gov.my; Abdurahman, Mohamad Norahiman, E-mail: iman5031@yahoo.com [Division of Radiation Processing Technology, Malaysia Nuclear Agency, Bangi, 43000 Kajang, Selangor (Malaysia); Salih, Ashraf Mohammed, E-mail: ashraf.msalih@gmail.com [Department of Radiation Processing, Sudan Atomic Energy Commission, Khartoum, 1111 Sudan (Sudan); Fathy, Siti Farhana, E-mail: farhana811@hotmail.com [Laboratory of Molecular Biomedicine, Institute of Bioscience (IBS), Universiti Putra Malaysia (UPM), 43400 UPM, Serdang, Selangor (Malaysia); Azman, Anis Asmi, E-mail: anisasmi18@gmail.com; Hamidi, Nur Amira, E-mail: amirahamidi93@yahoo.com [School of Chemical Sciences, Universiti Sains Malaysia (USM), 11800 USM, Pulau Pinang (Malaysia)

    2016-01-22

    The palm oil-based ultraviolet (uv)-curable films were subjected to an outdoor soil burial test to investigate the biodegradation under natural environment. The films were burial in the soil experiment plot at the Nuclear Malaysia’s Dengkil complex. The uv-curable films were synthesized from the epoxidized palm oil acrylated (EPOLA) resin and the polyurethane palm oil (POBUA) resin, respectively. Biodegradation tests are more specific to burial film in soil experiments for 12 months under natural conditions. The biodegradability of palm oil resin based uv-curable films were investigated and compared with the petrochemical resin based film. The films properties were compared with respect to properties of the thermal characteristic, the crystallinity, the morphology and the weight loss which are analyzed using the thermogravimetric analysis (TGA), the differential scanning calorimetry (DSC), the scanning electron microscope (SEM), an optical microscope and the weight loss of film calculation. These findings suggested that the palm oil-based uv-curable films show quite satisfactory biodegradation levels.

  15. Denture Adhesives

    Science.gov (United States)

    ... Devices Products and Medical Procedures Dental Devices Denture Adhesives Share Tweet Linkedin Pin it More sharing options ... Wearers Reporting Problems to the FDA Background Denture adhesives are pastes, powders or adhesive pads that may ...

  16. Physicochemical and Biological Investigation of Different Structures of Carbon Coatings Deposited onto Polyurethane

    Directory of Open Access Journals (Sweden)

    Witold Kaczorowski

    2016-01-01

    Full Text Available The aim of this study was to examine the thrombogenic properties of polyurethane that was surface modified with carbon coatings. Physicochemical properties of manufactured coatings were investigated using transmission electron microscopy (TEM, atomic force microscopy (AFM, X-ray Photoelectron Spectroscopy (XPS, Raman spectroscopy and contact angle measurement methods. Samples were examined by the Impact-R method evaluating the level of platelets activation and adhesion of particular blood cell elements. The analysis of antimicrobial resistance against E. coli colonization and viability of endothelial cells showed that polyurethane modified with use of carbon layers constituted an interesting solution for biomedical application.

  17. Unidirectional fibers and polyurethane elastomer matrix based composites synthesis and properties. Ph.D. Thesis

    Science.gov (United States)

    Chakar, A.

    1984-01-01

    A study of the properties and manufacturing techniques for long-fiber reinforced elastomeric composites for flexible and damping structural materials is presented. Attention is given to the usage of polyurethane in the matrix to obtain plastic elastomeric matrices and vitreous transition temperatures which vary from -80 C to 10 C, as well as assure good fiber adhesion. Various polyurethane formulations synthesized from diisocyanate prepolymers are examined in terms of mechanical and thermal properties. The principal reinforcing fiber selected is a unidirectional glass cloth.

  18. Evaluation gamma radiation in composite sisal fiber- polyurethane derived of castor oil by bending test

    International Nuclear Information System (INIS)

    Souza, Felipe H. de; Geraldo, Ricardo R.; Vasco, Marina C.; Azevedo, Elaine; Claro Neto, Salvador

    2015-01-01

    Materials used for making furniture and accessories or positioning in X -ray examination rooms should not exhale volatile organic compounds and are resistant to ionizing radiation. One solution is the use of vegetable fiber and polyurethane composites of vegetable origin, since they are biodegradable, derived from renewable raw materials and have no volatile organic compounds. The main difficulty in developing this material is fiber adhesion with the polymer. The objective of this study is to evaluate the mechanical properties of composite sisal fiber composite, without further treatment, and polyurethane derived from castor oil, with a dose of 25 kGy gamma radiation, subjected to 3 points bending tests. (author)

  19. 40 CFR 721.8095 - Silylated polyurethane.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Silylated polyurethane. 721.8095... Substances § 721.8095 Silylated polyurethane. (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as a silylated polyurethane (PMN P-95-1356) is...

  20. 40 CFR 721.8090 - Polyurethane polymer.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Polyurethane polymer. 721.8090 Section... Substances § 721.8090 Polyurethane polymer. (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as a polyurethane polymer (P-94-47) is subject...

  1. Polyurethane Foams with Pyrimidine Rings

    Directory of Open Access Journals (Sweden)

    Kania Ewelina

    2014-09-01

    Full Text Available Oligoetherols based on pyrimidine ring were obtained upon reaction of barbituric acid with glycidol and alkylene carbonates. These oligoetherols were then used to obtain polyurethane foams in the reaction of oligoetherols with isocyanates and water. The protocol of foam synthesis was optimized by the choice of proper kind of oligoetherol and synthetic composition. The thermal resistance was studied by dynamic and static methods with concomitant monitoring of compressive strength. The polyurethane foams have similar physical properties as the classic ones except their enhanced thermal resistance. They stand long-time heating even at 200°C. Moreover thermal exposition of foams results generally in increase of their compressive strength.

  2. Polyurethane - positioning aids in radiotherapy

    International Nuclear Information System (INIS)

    Alzen, G.; Boeck, E.G.; Thelen, M.; Kutzner, J.

    1985-01-01

    A simple and cheap method is described for the manufacturing of individual positioning aids made of foamed polyurethane. Some examples are given to demonstrate the applicability of these positioning aids for the irradiation of different body regions. The reproducibility of the radiation field in the head and neck area was investigated with and without positioning aid. It was proved that the field is adjusted more exactly when positioning aids are applied. The dosimetric investigations performed showed a negligible influence of foamed polyurethane on the radiation quality. So the positioning aids could be left within the radiation field when drawing the field borders. (orig.) [de

  3. Bioactive polyurethane implants with hydroxyapatite

    Energy Technology Data Exchange (ETDEWEB)

    Rozhnova, R.; Kebuladze, I.; Galatenko, N. [NAS Ukraine, Kiev (Ukraine). Dept. of Polymers of Medical Appointment

    2001-07-01

    Biologically active polyurethane compositions for plastic of bone defects that contain bioceramic - hydroxyapatite (HAP) and immunomodulator - levamisole (LEV) were designed. The influence of the biologically active fillers in structure polyurethane compositions on their physical and chemical properties in condition in vivo by method of Equilibrium Swelling, method of IR-spectroscopy, roentgen-structural analysis was studied. The introduce in structure of the biodegraded polymeric matrix of HAP is established to promote accumulation of the inorganic component of bone tissue in vivo which is being by basis of the bone formation in regenerating tissue. (orig.)

  4. Additive Manufacturing of Polyurethane Materials

    Energy Technology Data Exchange (ETDEWEB)

    Kunc, Vlastimil [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Lindahl, John M. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Minneci, Robert P. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Pyzik, Alek [Dow Chemical Company, Saginaw, MI (United States); Gorin, Craig [Dow Chemical Company, Midland, MI (United States); Allen, Sharon [Dow Chemical Company, Midland, MI (United States); Wilson, Keith [Dow Chemical Company, Midland, MI (United States); Howard, Kevin [Dow Chemical Company, Midland, MI (United States)

    2017-08-10

    ORNL worked with The DOW Chemical Company to validate the feasibility of 3D printing DOW’s polyurethane (PU) materials using ORNL’s equipment and know-how. This led to the development of the first directly-3D-printable PU material.

  5. UV-curable polyurethane coatings derived from cellulose

    International Nuclear Information System (INIS)

    Patel, M. M.; Patel, K. I.; Patel, H. B.; Parmar, J. S.

    2009-01-01

    At the present time coating industry is devoting much research in the direction of low volatile organic compounds to make eco-friendly coating material. In this study, such materials are developed from cellulose derived from bagasse, a sugar industry waste. Cellulose is converted to cellulose glyco glycoside by acid hydrolysis of cellulose under heterogeneous condition. Cellulose glyco glycoside is treated with polyethylene glycol having different molecular weights to give glyco glycosides which in turn are reacted with various diisocyanates to obtain polyurethane having free NCO groups. These materials are then reacted with hydroxyethylmethacrylate to give polyurethane acrylates. The acrylates are characterized for specific gravity, viscosity, colour and molecular weight as well as by fourier transform infrared spectroscopy. The UV-curable coating composition was prepared by blending PU-acrylate, reactive diluents and photoinitiator. Coating compositions were cured under UV-light and characterized for adhesion, flexibility, impact resistance, solvent resistance and for dynamic mechanical analysis as well as by thermal gravimetric analysis for thermal stability. The cured films give thickness of 23-24 microns and cure time required is less than 1.5-2.0 min. There is no liberation of any volatiles during curing and films have good adhesion to mild steel substrate. The cured coatings give excellent dynamic, mechanical and chemical properties. The scratch resistance was found to be satisfactory. The application was made in unpigmented form but it is found that various pigments can be used to give coloured UV-curable coatings.

  6. Microphase separated structure and surface properties of fluorinated polyurethane resin

    International Nuclear Information System (INIS)

    Sudaryanto; Nishino, T.; Hori, Y.; Nakamae, K.

    2000-01-01

    The effect of fluorination on microphase separation and surface properties of segmented polyurethane (PU) resin were investigated. A series of fluorinated polyurethane resin (FPU) was synthesized by reacting a fluorinated diol with aromatic diisocyanate. The microphase separated structure of FPU was studied by thermal analysis, and small angle X-ray scattering (SAXS) as well as wide angle X-ray diffraction (WAXD). The surface structure and properties were characterized by X-ray photoelectron spectroscopy (XPS) and dynamic contact angle measurement. The incorporation of fluorine into hard segment brings the FPU to have a higher hard domain cohesion and increase the phase separation, however localization of fluorine on the surface could not be observed. On the other hands, localization of fluorine on the surface could be achieved for soft segment fluorinated PU without any significant change in microphase separated structure. The result from this study give an important basic information for designing PU coating material with a low surface energy and strong adhesion as well as for development of release film on pressure sensitive adhesive tape. (author)

  7. Fabrication of superhydrophobic polyurethane/organoclay nano-structured composites from cyclomethicone-in-water emulsions

    International Nuclear Information System (INIS)

    Bayer, I.S.; Steele, A.; Martorana, P.J.; Loth, E.

    2010-01-01

    Nano-structured polyurethane/organoclay composite films were fabricated by dispersing moisture-curable polyurethanes and fatty amine/amino-silane surface modified montmorillonite clay (organoclay) in cyclomethicone-in-water emulsions. Cyclomethicone Pickering emulsions were made by emulsifying decamethylcyclopentasiloxane (D 5 ), dodecamethylcyclohexasiloxane (D 6 ) and aminofunctional siloxane polymers with water using montmorillonite particles as emulsion stabilizers. Polyurethane and organoclay dispersed emulsions were spray coated on aluminum surfaces. Upon thermosetting, water repellent self-cleaning coatings were obtained with measured static water contact angles exceeding 155 o and low contact angle hysteresis ( o ). Electron microscopy images of the coating surfaces revealed formation of self-similar hierarchical micro- and nano-scale surface structures. The surface morphology and the coating adhesion strength to aluminum substrates were found to be sensitive to the relative amounts of dispersed polyurethane and organoclay in the emulsions. The degree of superhydrophobicity was analyzed using static water contact angles as well as contact angle hysteresis measurements. Due to biocompatibility of cyclomethicones and polyurethane, developed coatings can be considered for specific bio-medical applications.

  8. Fabrication of superhydrophobic polyurethane/organoclay nano-structured composites from cyclomethicone-in-water emulsions

    Energy Technology Data Exchange (ETDEWEB)

    Bayer, I.S., E-mail: ibayer1@illinois.edu [Department of Aerospace Engineering, University of Illinois at Urbana-Champaign, IL 61801 (United States); Steele, A.; Martorana, P.J. [Department of Aerospace Engineering, University of Illinois at Urbana-Champaign, IL 61801 (United States); Loth, E. [Department of Aerospace Engineering, University of Illinois at Urbana-Champaign, IL 61801 (United States); Department of Mechanical and Aerospace Engineering, University of Virginia, VA 22904 (United States)

    2010-11-15

    Nano-structured polyurethane/organoclay composite films were fabricated by dispersing moisture-curable polyurethanes and fatty amine/amino-silane surface modified montmorillonite clay (organoclay) in cyclomethicone-in-water emulsions. Cyclomethicone Pickering emulsions were made by emulsifying decamethylcyclopentasiloxane (D{sub 5}), dodecamethylcyclohexasiloxane (D{sub 6}) and aminofunctional siloxane polymers with water using montmorillonite particles as emulsion stabilizers. Polyurethane and organoclay dispersed emulsions were spray coated on aluminum surfaces. Upon thermosetting, water repellent self-cleaning coatings were obtained with measured static water contact angles exceeding 155{sup o} and low contact angle hysteresis (<8{sup o}). Electron microscopy images of the coating surfaces revealed formation of self-similar hierarchical micro- and nano-scale surface structures. The surface morphology and the coating adhesion strength to aluminum substrates were found to be sensitive to the relative amounts of dispersed polyurethane and organoclay in the emulsions. The degree of superhydrophobicity was analyzed using static water contact angles as well as contact angle hysteresis measurements. Due to biocompatibility of cyclomethicones and polyurethane, developed coatings can be considered for specific bio-medical applications.

  9. Protein adhesives

    Science.gov (United States)

    Charles R. Frihart; Linda F. Lorenz

    2018-01-01

    Nature uses a wide variety of chemicals for providing adhesion internally (e.g., cell to cell) and externally (e.g., mussels to ships and piers). This adhesive bonding is chemically and mechanically complex, involving a variety of proteins, carbohydrates, and other compounds.Consequently,the effect of protein structures on adhesive properties is only partially...

  10. Sustained Release Drug Delivery Applications of Polyurethanes

    Directory of Open Access Journals (Sweden)

    Michael B. Lowinger

    2018-05-01

    Full Text Available Since their introduction over 50 years ago, polyurethanes have been applied to nearly every industry. This review describes applications of polyurethanes to the development of modified release drug delivery. Although drug delivery research leveraging polyurethanes has been ongoing for decades, there has been renewed and substantial interest in the field in recent years. The chemistry of polyurethanes and the mechanisms of drug release from sustained release dosage forms are briefly reviewed. Studies to assess the impact of intrinsic drug properties on release from polyurethane-based formulations are considered. The impact of hydrophilic water swelling polyurethanes on drug diffusivity and release rate is discussed. The role of pore formers in modulating drug release rate is examined. Finally, the value of assessing mechanical properties of the dosage form and approaches taken in the literature are described.

  11. High molecular weight polyurethanes and a polyurethane urea based on 1,4-butanediisocyanate

    NARCIS (Netherlands)

    Spaans, CJ; de Groot, JH; Dekens, FG; Pennings, AJ

    New biomedical polyurethanes and a polyurethane urea based on epsilon-caprolactone and 1,4-butanediisocyanate have been developed. On degradation, only non-toxic products are produced. The polyurethane urea with poly(epsilon-caprolactone) soft segments and butanediisocyanate/butanediamine hard

  12. Sorption of heteropoly acids by polyurethane foam

    International Nuclear Information System (INIS)

    Dmitreinko, S.G.; Goncharova, L.V.; Runov, V.K.; Zakharov, V.N.; Aslanova, L.A.

    1997-01-01

    Sorption of oxidized and reduced forms of molybdosilicic, molybdophosphoric and molybdovanadophosphoric acids by polyurethane foam based on ethers and esters is studied. On the basis of sorption dependence on solution pH, polyurethane foam type and spectral characteristics of sorbates the suggestion has been made that in the polyurethane foam phase there are two main types of sorbent-sorbate interaction: electrostatic (ion-ion) and with hydrogen bond formation: and it is impossible to determine the contribution of every interaction

  13. Structure and Properties of Polyurethanes. Part 1,

    Science.gov (United States)

    1979-03-23

    since the solidification of varnish coatings on basis it is polyurethane usually it occurs under conditions for contact wita moisture of air. Page...containing fluorine is polyurethane. In works (44, 84-86] is given the information about synthesis 11 DOC = 79011105 PAGE and special feature/peculiarities...of the phase transformations of the series/number of the fluorine -bedrlng aliphatic ones it is polyurethane. Page 87. In particular, were investigated

  14. Polyurethane Functional Coatings for Protection of Different Surfaces from Aggressive Environmental Factors

    Directory of Open Access Journals (Sweden)

    Savelyev, U.V., Markovska, L.A., Robota, L.P., Parkhomenko, N.I., and Savelyeva, O.O.

    2014-05-01

    Full Text Available New polyurethane compositions (PC as multifunctional protective materials that can serve as coatings or binders or impregnating materials have been created. PC have high adhesion values and the PC-based materials are waterproof and resistant to aggressive biotic (abiotic and technogenic factors (biocorrosion, UV radiation, chemical agents. Putting active compounds into the polymer macrochain prolongs the protection functions of the materials. This is their advantage to existing materials.

  15. Attachment of inorganic moieties onto aliphatic polyurethanes

    Directory of Open Access Journals (Sweden)

    Eliane Ayres

    2007-06-01

    Full Text Available Polyurethanes have been used in a series of applications due basically to their versatility in terms of controlling the behavior by altering basically the type of reagents used. However, for more specific and advanced applications, such as in membranes, biomaterials and sensors, well-organized and defined chemical functionalities are necessary. In this work, inorganic functionalities were incorporated into aliphatic polyurethanes (PU having different macromolecular architectures. Polyurethanes were synthesized using a polyether diol and dicyclohexylmethane 4,4' diisocyanate (H12-MDI. Polyurethanes having carboxylic acid groups were also produced by introducing 2,2- bis (hydroxymethyl propionic acid in the polymerization process. Inorganic functionalities were inserted into polyurethanes by reacting isocyanate end capped chains with aminopropyltriethoxysilane followed by tetraethoxysilane. PU having carboxylic acid groups yielded transparent samples after the incorporation of inorganic entities, as an evidence of smaller and better dispersed inorganic entities in the polymer network. FTIR and swelling measurements showed that polyurethanes having carboxylic acid groups had inorganic domains less packed, condensed and cross-linked when compared to polyurethanes with no carboxylic acid groups. Results also suggested that the progressive incorporation of inorganic moieties in both types of polyurethanes occurred in regions previously activated with inorganic functionalities, instead of by the creation of new domains. The temperatures of thermal decomposition and glass transition were also shifted to higher temperatures when inorganic functionalities were incorporated into polyurethanes.

  16. UV curable palm oil based ink

    International Nuclear Information System (INIS)

    Mek Zah Salleh; Mohd Hilmi Mahmood; Khairul Zaman Mohd Dahlan; Rosley Che Ismail

    2002-01-01

    UV curable inks are useful for their instant drying, energy saving and high productivity properties. The basic materials for formulating UV curable inks consist of prepolymer, monomers, photoinitiators, pigments and other additives. The percentage composition and ingredients depend very much on the types of inks to be produced. Palm oil is one of the main raw materials available in the country. Hence, the diversification of palm oil derivatives into new products has been given priority. The current focus of the present work is to evaluate the use of palm oil urethane acrylate (POBUA) as a prepolymer in the UV ink system. A study was conducted on the use of POBUA with other materials in ink formulation. These include the types and concentration of photoinitiators, monomers and commercial urethane acrylates. The evaluation of the ink properties such as curing, adhesion, color density have been carried out. It was found that POBUA could be introduced in the UV ink system. (Author)

  17. Preparation and characterization of plasticized palm-based polyurethane solid polymer electrolyte

    International Nuclear Information System (INIS)

    Daud, Farah Nadia; Ahmad, Azizan; Badri, Khairiah Haji

    2013-01-01

    Palm-based polyurethane solid polymer electrolyte was prepared via prepolymerization method between palm kernel oil based polyols (PKO-p) and 2,4’-diphenylmethane diisocyanate (2,4’-MDI) in acetone at room temperature with the vary amount of lithium trifuoromethanesulfonate (LiCF 3 SO 3 ) salt and polyethylene glycol (PEG). The film was analyzed using attenuated total reflection infrared (ATR-IR) spectroscopy, electrochemical impedance spectroscopy (EIS) and X-ray diffractometry (XRD). EIS result indicated ionic conductivity obtained with 30 wt% LiCF3SO3 increased to 6.55 × 10 −6 S cm −1 when 10 wt.% of plasticizer was added into the system. FTIR analysis showed the interaction between lithium ions and amine (-N-H) at 3600–3100 cm −1 , carbonyl (-C=O) at 1750–1650 cm −1 and ether (-C-O-C-) at 1150–1000 cm −1 of the polyurethane forming polymer-salt complexes. The XRD result confirmed that LiCF 3 SO 3 salt completely dissociated within the polyurethane film with the absence of crystalline peaks of LiCF 3 SO 3

  18. Preparation and characterization of plasticized palm-based polyurethane solid polymer electrolyte

    Energy Technology Data Exchange (ETDEWEB)

    Daud, Farah Nadia; Ahmad, Azizan; Badri, Khairiah Haji [School of Chemical Science and Food Technology, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, 43600 UKM Bangi, Selangor Darul Ehsan (Malaysia)

    2013-11-27

    Palm-based polyurethane solid polymer electrolyte was prepared via prepolymerization method between palm kernel oil based polyols (PKO-p) and 2,4’-diphenylmethane diisocyanate (2,4’-MDI) in acetone at room temperature with the vary amount of lithium trifuoromethanesulfonate (LiCF{sub 3}SO{sub 3}) salt and polyethylene glycol (PEG). The film was analyzed using attenuated total reflection infrared (ATR-IR) spectroscopy, electrochemical impedance spectroscopy (EIS) and X-ray diffractometry (XRD). EIS result indicated ionic conductivity obtained with 30 wt% LiCF3SO3 increased to 6.55 × 10{sup −6} S cm{sup −1} when 10 wt.% of plasticizer was added into the system. FTIR analysis showed the interaction between lithium ions and amine (-N-H) at 3600–3100 cm{sup −1}, carbonyl (-C=O) at 1750–1650 cm{sup −1} and ether (-C-O-C-) at 1150–1000 cm{sup −1} of the polyurethane forming polymer-salt complexes. The XRD result confirmed that LiCF{sub 3}SO{sub 3} salt completely dissociated within the polyurethane film with the absence of crystalline peaks of LiCF{sub 3}SO{sub 3}.

  19. Formulation, Preparation, and Characterization of Polyurethane Foams

    Science.gov (United States)

    Pinto, Moises L.

    2010-01-01

    Preparation of laboratory-scale polyurethane foams is described with formulations that are easy to implement in experiments for undergraduate students. Particular attention is given to formulation aspects that are based on the main chemical reactions occurring in polyurethane production. This allows students to develop alternative formulations to…

  20. Polyurethane doped with low-concentration erbium

    NARCIS (Netherlands)

    Ciobanu, C.; Stoica, E.; Cascaval, C.N.; Rosu, D.; Rosu, L.; State, M.; Emandi, A.; Nemes, I.; Petrescu, F.

    2007-01-01

    ABSTRACT: Polyurethane (PU) with lactate structures inits conformation can be used as a biological and biodegradablepolymer. Polyurethane lactate (PUL) was dopedwith small quantities of an erbium (Er3þ) complex, whichhindered the N¼N group. 2,20-Dihydroxyazobenzene wasused as a ligand for the Er3þ

  1. Preparation and characterization of new biologically active polyurethane foams.

    Science.gov (United States)

    Savelyev, Yuri; Veselov, Vitali; Markovskaya, Ludmila; Savelyeva, Olga; Akhranovich, Elena; Galatenko, Natalya; Robota, Ludmila; Travinskaya, Tamara

    2014-12-01

    Biologically active polyurethane foams are the fast-developed alternative to many applications of biomedical materials. Due to the polyurethane structure features and foam technology it is possible to incorporate into their structure the biologically active compounds of target purpose via structural-chemical modification of macromolecule. A series of new biologically active polyurethane foams (PUFs) was synthesized with polyethers (MM 2500-5000), polyesters MM (500-2200), 2,4(2,6) toluene diisocyanate, water as a foaming agent, catalysts, foam stabilizers and functional compounds. Different functional compounds: 1,4-di-N-oxy-2,3-bis-(oxymethyl)-quinoxaline (DOMQ), partial sodium salt of poly(acrylic acid) and 2,6-dimethyl-N,N-diethyl aminoacetatanilide hydrochloride were incorporated into the polymer structure/composition due to the chemical and/or physical bonding. Structural peculiarities of PUFs were studied by FTIR spectroscopy and X-ray scattering. Self-adhesion properties of PUFs were estimated by measuring of tensile strength at break of adhesive junction. The optical microscopy method was performed for the PUF morphology studies. Toxicological estimation of the PUFs was carried out in vitro and in vivo. The antibacterial action towards the Gram-positive and Gram-negative bacteria (Escherichia coli ATC 25922, E. coli ATC 2150, Klebsiella pneumoniae 6447, Staphylococcus aureus 180, Pseudomonas aeruginosa 8180, Proteus mirabilis F 403, P. mirabilis 6054, and Proteus vulgaris 8718) was studied by the disc method on the solid nutrient. Physic-chemical properties of the PUFs (density, tensile strength and elongation at break, water absorption and vapor permeability) showed that all studied PUFs are within the operational requirements for such materials and represent fine-cellular foams. Spectral studies confirmed the incorporation of DOMQ into the PUF's macrochain. PUFs are characterized by microheterogeneous structure. They are antibacterially active, non

  2. Cellular Adhesion and Adhesion Molecules

    OpenAIRE

    SELLER, Zerrin

    2014-01-01

    In recent years, cell adhesion and cell adhesion molecules have been shown to be important for many normal biological processes, including embryonic cell migration, immune system functions and wound healing. It has also been shown that they contribute to the pathogenesis of a large number of common human disorders, such as rheumatoid arthritis and tumor cell metastasis in cancer. In this review, the basic mechanisms of cellular adhesion and the structural and functional features of adhes...

  3. Enhancement of antibacterial properties of polyurethanes by chitosan and heparin immobilization

    International Nuclear Information System (INIS)

    Kara, Filiz; Aksoy, E. Ayse; Yuksekdag, Zehranur; Aksoy, Serpil; Hasirci, Nesrin

    2015-01-01

    Graphical abstract: - Highlights: • Polyurethane elastomer was synthesized in medical purity. • Chitosan (CH) and heparin (Hep) were immobilized on polyurethane films. • Modification with CH and Hep increased hydrophilicity and surface free energy. • Immobilized films had high antibacterial activity against four bacteria. • Bacterial adhesion significantly decreased on the modified surfaces. - Abstract: Being antibacterial is a required property for the materials used in medical devices and instruments. Polyurethanes (PUs) are one class of polymers widely used in the production of devices that especially come in contact with blood (e.g. heart valves, blood vessels, vascular grafts and catheters). In this study, hexamethylene diisocyanate based polyurethanes (PUh) were synthesized and antibacterial and anti-adhesive properties were added by immobilizing chitosan (CH) and heparin (Hep) on the samples of PUh via a stepwise process. Chemistry and topography of the modified film samples (PUh-CH and PUh-CH-Hep) were examined by Fourier Transform Infrared Spectrophotometry-Attenuated Total Reflectance (FTIR-ATR), Electron Spectroscopy for Chemical Analysis (ESCA) and Atomic Force Microscopy (AFM), and surface free energy (SFE) values after each step were determined by goniometer. PUh-CH and PUh-CH-Hep samples were found to be antibacterial against Staphylococcus aureus (S. aureus) and Staphylococcus epidermidis (S. epidermidis) (both Gram positive) and Escherichia coli (E. coli) and Pseudomonas aeruginosa (P. aeruginosa) (both Gram negative) bacteria, and bacterial adhesion results showed a significant decrease in the number of viable bacteria on both modified samples where PUh-CH-Hep was the most effective. The findings of this study show that polymeric surfaces can be effectively modified and converted to be antibacterial by chitosan and heparin immobilization, and presence of both chemicals enhance efficacy against bacteria.

  4. Enhancement of antibacterial properties of polyurethanes by chitosan and heparin immobilization

    Energy Technology Data Exchange (ETDEWEB)

    Kara, Filiz [Department of Chemistry, Faculty of Science, Gazi University, 06500 Ankara (Turkey); Aksoy, E. Ayse [Department of Basic Pharmaceutical Sciences, Faculty of Pharmacy, Hacettepe University, 06100 Ankara (Turkey); Yuksekdag, Zehranur [Biotechnology Laboratory, Department of Biology, Faculty of Science, Gazi University, 06500 Ankara (Turkey); Aksoy, Serpil [Department of Chemistry, Faculty of Science, Gazi University, 06500 Ankara (Turkey); Hasirci, Nesrin, E-mail: nhasirci@metu.edu.tr [BIOMATEN, Center of Excellence in Biomaterials and Tissue Engineering, Middle East Technical University, 06800 Ankara (Turkey); Department of Chemistry, Faculty of Arts and Sciences, Middle East Technical University, 06800 Ankara (Turkey)

    2015-12-01

    Graphical abstract: - Highlights: • Polyurethane elastomer was synthesized in medical purity. • Chitosan (CH) and heparin (Hep) were immobilized on polyurethane films. • Modification with CH and Hep increased hydrophilicity and surface free energy. • Immobilized films had high antibacterial activity against four bacteria. • Bacterial adhesion significantly decreased on the modified surfaces. - Abstract: Being antibacterial is a required property for the materials used in medical devices and instruments. Polyurethanes (PUs) are one class of polymers widely used in the production of devices that especially come in contact with blood (e.g. heart valves, blood vessels, vascular grafts and catheters). In this study, hexamethylene diisocyanate based polyurethanes (PUh) were synthesized and antibacterial and anti-adhesive properties were added by immobilizing chitosan (CH) and heparin (Hep) on the samples of PUh via a stepwise process. Chemistry and topography of the modified film samples (PUh-CH and PUh-CH-Hep) were examined by Fourier Transform Infrared Spectrophotometry-Attenuated Total Reflectance (FTIR-ATR), Electron Spectroscopy for Chemical Analysis (ESCA) and Atomic Force Microscopy (AFM), and surface free energy (SFE) values after each step were determined by goniometer. PUh-CH and PUh-CH-Hep samples were found to be antibacterial against Staphylococcus aureus (S. aureus) and Staphylococcus epidermidis (S. epidermidis) (both Gram positive) and Escherichia coli (E. coli) and Pseudomonas aeruginosa (P. aeruginosa) (both Gram negative) bacteria, and bacterial adhesion results showed a significant decrease in the number of viable bacteria on both modified samples where PUh-CH-Hep was the most effective. The findings of this study show that polymeric surfaces can be effectively modified and converted to be antibacterial by chitosan and heparin immobilization, and presence of both chemicals enhance efficacy against bacteria.

  5. Polyurethane membranes for surgical gown applications

    Science.gov (United States)

    Ukpabi, Pauline Ozoemena

    The Occupational Safety and Health Administration (OSHA) recently issued a directive requiring all employers to supply personnel protective equipment to employees who are at risk of exposure to blood or other potentially infectious body fluids. For the healthcare worker, a wide variety of surgical gowns is available commercially but there are concerns over their barrier effectiveness and/or wearer comfort. To successfully create a barrier fabric which combines resistance to fluid penetration with comfort, a complete understanding of the relationship between membrane structure and functional properties is required. In this study, we investigated the surface properties of hydrophilicity and hydrophobicity in polyurethane membranes intended for use in surgical gowns. The polyurethane membranes were grafted with side chains of varying lengths, polyethylene glycol (PEG) being used for the hydrophilic modifications and perfluoroalkyl compounds (a monofunctional acid and a difunctional amino alcohol) for the hydrophobic modifications. The hydrophilic treatment was intended to improve the comfort properties of monolithic membranes without adversely affecting their barrier properties. The hydrophobic treatment, on the other hand, was intended to improve the fluid repellency and hence barrier properties of microporous membranes without adversely affecting their comfort properties. Reflection infrared spectroscopy showed that fluorine was successfully grafted onto the polyurethane backbone during the hydrophobic modification, but was not sensitive enough to detect PEG grafting in leached polyethylene glycol-treated polyurethanes. X-ray photoelectron spectroscopy showed that the perfluoroalkylated polyurethanes contained up to 40% fluorine on their surfaces and the PEG-treated polyurethanes showed an increase in their C-O content over the unmodified polyurethane. Scanning electron microscopy not only showed that perfluoroalkylation yielded polyurethane membranes with very

  6. Adhesion science

    CERN Document Server

    Comyn, John

    1997-01-01

    The use of adhesives is widespread and growing, and there are few modern artefacts, from the simple cereal packet, to the jumbo jet, that are without this means of joining. Adhesion Science provides an illuminating account of the science underlying the use of adhesives, a branch of chemical technology which is fundamental to the science of coatings and composite materials and to the performance of all types of bonded structures. This book guides the reader through the essential basic polymer science, and the chemistry of adhesives in use at present. It discusses surface preparation for adhesive bonding, and the use of primers and coupling agents. There is a detailed chapter on contact angles and what can be predicted from them. A simple guide on stress distribution joints and how this relates to testing is included. It also examines the interaction of adhesives and the environment, including an analysis of the resistance of joints to water, oxygen and ultra-violet light. Adhesion Science provides a comprehens...

  7. Electromechanical study of polyurethane films with carbon black nanoparticles for MEMS actuators

    International Nuclear Information System (INIS)

    Roussel, M; Deman, A-L; Chateaux, J-F; Malhaire, C; Petit, L; Seveyrat, L; Galineau, J; Guiffard, B; Seguineau, C; Desmarres, J-M; Martegoutte, J

    2014-01-01

    Pure polyurethane and nanocomposite carbon black (CB) polyurethane solutions were deposited by spin-coating on a silicon substrate using gold as the adhesion layer and electrode. Different test structures were achieved for electrical and mechanical characterizations. The incorporation of CB nanoparticles in the polyurethane matrix has a significant influence on the dielectric permittivity of the material with an increase of about one third of its value. The Young's modulus of PU and nanocomposite PU films was determined by different characterization methods. Nanoindentation experiments have pointed out a Young's modulus gradient through the film thickness. By performing mechanical tests (tensile, bulge, point deflection) on freestanding films, an average Young's modulus value of about 30 MPa was found as well as a residual stress value of about 0.4 MPa. However, no influence of the presence of the nanoparticles was found. Finally, several MEMS actuators were realized and characterized. At their fundamental resonance frequency, the actuation of the nanocomposite membranes is more efficient than that of pure polyurethane. However, the time constant of the material seems to provide a major barrier for the development of high-frequency PU-based micro-actuators. (paper)

  8. Creep of thermoplastic polyurethane reinforced with ozone functionalized carbon nanotubes

    Directory of Open Access Journals (Sweden)

    Z. Zhang

    2012-09-01

    Full Text Available This work focused on the mechanical behavior, especially creep resistance, of thermoplastic polyurethane (TPU filled with ozone-treated multi-walled carbon nanotubes (MWCNTs. It was found that the ozone functionalization of MWCNTs could improve their dispersion and interfacial adhesion to the TPU matrix as proved by scanning electron microscope and Raman spectrometer. It finally contributed to the enhancement of Young’s modulus and yield strength of TPU/MWCNT composites. Moreover, the creep resistance and recovery of MWCNT/TPU composites revealed a significant improvement by incorporating ozone functionalized MWCNTs. The strong interaction between the modified MWCNTs and TPU matrix would enhance the interfacial bonding and facilitate the load transfer, resulting in low creep strain and unrecovered strain.

  9. Neutron gauging to detect voids in polyurethane

    International Nuclear Information System (INIS)

    Tsang, F.Y.; Alger, D.M.; Brugger, R.M.

    1978-01-01

    Thermal-neutron radiography and fast-neutron gauging measurements were made to evaluate the feasibility of detecting voids in a polyurethane block placed between steel plates. This sandwich of polyurethane and steel simulates the walls of a canister being designed to hold explosive devices. The polyurethane would act as a shock absorber in the canister. A large fabrication cost saving would result by casting the polyurethane, but a nondestructive testing (NDT) method is needed to determine the uniformity of the polyurethane fill. The radiography measurements used a beam of thermal neutrons, while the gauging used filtered beams of 24 keV and fission spectrum neutrons. For the 83-mm-thick polyurethane and 130-mm-thick steel matrix, the thermal-neutron radiography was able to detect only those voids equal to about one-half the polyurethane thickness. The gauging detected voids in the path of the neutron beam of a few millimetres thickness in seconds to minutes. The gauging is feasible as an NDT method for the canister application

  10. Gamma radiation effects on mechanical properties and morphology of a polyurethane derivate from castor oil

    Science.gov (United States)

    Azevedo, Elaine Cristina; Orivaldo Chierice, Gilberto; Claro Neto, Salvador; Scheidegger Soboll, Daniel; Mauro Nascimento, Eduardo; Lepienski, Carlos Mauricio

    2011-03-01

    In this study, an adhesive of a polyurethane derivate from castor oil was irradiated with gamma radiation from a 60Co source, at doses from 0.2 to 25 kGy. This adhesive polyurethane is considered for use in hospital furniture because it does not liberate dangerous solvents. Hardness and elastic modulus were measured by instrumented indentation with a pyramidal Berkovich indenter, using loads from 0.08-40 mN with a nanoindenter XP. The instrumented indentation hardness was 110 MPa for an untreated sample, increasing to 124 MPa after irradiation with 25 kGy, at penetration depths of about 5 μm. The increases in elastic modulus induced by radiation were less pronounced. This polyurethane is naturally cross-linked and the relative modifications in the hardness are attributed to an additional cross-linking process induced by radiation. X-ray diffraction indicates a slight increase in crystallinity. The roughness measured by atomic force microscopy increases after gamma irradiation.

  11. Effect of Reinforced Hybrid Palm Shells on Mechanical Properties of Polyurethane-Jute Woven/ Vinyl Ester Sandwich Board

    International Nuclear Information System (INIS)

    Cheng, T.S.; Nurul Ain Nanyan; Lan, D.N.U.; Leng, T.P.

    2014-01-01

    A natural fiber sandwich was constructed from palm shells/polyurethane core and jute woven/vinyl ester face sheets by the in-situ sandwich process (core and panel prepared simultaneously). The polyurethane sandwich core was reinforced by hybrid shell systems of dried palm shell (DPS) and palm kernel shell (PKS) (50P-50D, 25P-75D), and single shell system of PKS (100P) as well as 20 phr empty fruit bunch (EFB) based on hundred part of polyurethane. The sandwich face sheets are prepared by using two jute woven layers and impregnated by vinyl ester. Interlocking between DPS and polyurethane matrix was formed, which hence enhanced the mechanical properties. The interfacial adhesion between DPS, PKS, and EFB with the polyurethane binder played the important role to achieve high mechanical properties. It was found that hybrid shells exhibited high reinforcement for sandwich's performance resulting better compression (50P-50D) and flexural (25P-75D) properties. The single shell 100P showed only improvement on flexural modulus.The fracture surface morphology of sandwich under mechanical test was performed by using optical microscopy. (author)

  12. From oil-based mud to water-based mud

    International Nuclear Information System (INIS)

    Christiansen, C.

    1991-01-01

    Maersk Olie og Gas AS has used low toxic oil-based muds extensively since 1982 for drilling development wells and later in the development of horizontal well drilling techniques. However, in view of the strong drive towards a reduction in the amount of oil discharged to the North Sea from the oil industry, Maersk Olie og Gas AS initiated trials with new or improved types of water-based mud, first in deviated wells (1989) and then in horizontal wells (1990). The paper reviews Maersk Olie og Gas As experience with oil-based mud since the drilling of the first horizontal well in 1987, specifically with respect to cuttings washing equipment, oil retention on cuttings, and the procedure for monitoring of this parameter. It describes the circumstances leading to the decision to revert to water-based mud systems. Finally, it reviews the experience gained so far with the new improved types of water-based mud systems, mainly glycol and KCl/polymer mud systems. Comparison of operational data, such as rate of penetration, torque and drag, etc., is made between wells drilled with oil-based mud and water-based mud. The trials with the new improved types of water-based mud systems have been positive, i.e. horizontal wells can be drilled successfully with water-based mud. As a result, Maersk Olie og and Gas AS has decided to discontinue the use of low toxic oil-based muds in the Danish sector of the North Sea

  13. Flame Retardants Used in Flexible Polyurethane Foam

    Science.gov (United States)

    The partnership project on flame retardants in furniture seeks to update the health and environmental profiles of flame-retardant chemicals that meet fire safety standards for upholstered consumer products with polyurethane foam

  14. Thermoplastic polyurethane and multi-walled carbon nanotubes nanocomposites for electrostatic dissipation

    International Nuclear Information System (INIS)

    Lavall, Rodrigo L.; Sales, Juliana A. de; Borges, Raquel S.; Calado, Hallen D. R.; Machado, Jose C.; Windmoeller, Dario; Silva, Glaura G.; Lacerda, Rodrigo G.; Ladeira, Luiz O.

    2010-01-01

    Polyurethane/multi-walled carbon nanotube (MWCNT) nanocomposites have been prepared with nanotube concentrations between 0.01 wt% and 1 wt%. MWCNT as-synthesized samples with ∼74 nm diameter and ∼7 mm length were introduced by solution processing in the polyurethane matrix. Scanning electron microscopy (SEM) images demonstrated good dispersion and adhesion of the CNTs to the polymeric matrix. The C=O stretching band showed evidence of perturbation of the hydrogen interaction between urethanic moieties in the nanocomposites as compared to pure TPU. Differential scanning calorimetry and positron annihilation lifetime spectroscopy measurements allowed the detection of glass transition displacement with carbon nanotube addition. Furthermore, the electrical conductivity of the nanocomposites was significantly increased with the addition of CNT. (author)

  15. POLYURETHANE COMPOSITES AS DRUG CARRIERS:: RELEASE PATTERNS

    Directory of Open Access Journals (Sweden)

    M. V. Grigoreva

    2013-10-01

    Full Text Available Biodegradable polyurethanes attract interest of those developing composite materials for biomedical applications. One of their features is their ability to serve as carriers, or matrixes, for medicines and other bioactive compounds to produce a therapeutic effect in body through targeted and/or prolonged delivery of these compounds in the process of their controlled release from matrix. The review presents polyurethane composites as matrices for a number of drugs. The relation between structure of the composites and their degradability both in vitro and in vivo and the dependence of drug release kinetics on physicochemical properties of polyurethane matrix are highlighted. The release of drugs (cefazolin, naltrexone and piroxicam from the composites based on cross-linked polyurethanes (synthesized from laprols, Mw between 1,500 and 2,000 Da and toluylene diisocyanate demonstrated more or less the same pattern (about 10 days in vitro and three to five days in vivo. In contrast, the composites with dioxydine based on a linear polyurethanes (synthesized from oligotetramethilene glycol, Mw 1,000 Da, diphenylmethane-4,4’-diisocyanate and 1,4-butanediol retained their antimicrobial activity at least 30 days. They also showed a significantly higher breaking strength as compared to that of the composites based on cross-linked polyurethanes.

  16. Development of palm oil-based UV-curable epoxy acrylate and urethane acrylate resins for wood coating application

    International Nuclear Information System (INIS)

    Tajau, Rida; Mahmood, Mohd Hilmi; Salleh, Mek Zah; Salleh, Nik Ghazali Nik; Ibrahim, Mohammad Izzat; Yunus, Nurulhuda Mohd

    2014-01-01

    The trend of using renewable sources such as palm oil as raw material in radiation curing is growing due to the demand from the market to produce a more environmental friendly product. In this study, the radiation curable process was done using epoxy acrylate and urethane acrylate resins which are known as epoxidised palm olein acrylate (EPOLA) and palm oil based urethane acrylate (POBUA), respectively. The purpose of the study was to investigate curing properties and the application of this UV-curable palm oil resins for wood coating. Furthermore, the properties of palm oil based coatings are compared with the petrochemical-based compound such as ebecryl (EB) i.e. EB264 and EB830. From the experiment done, the resins from petrochemical-based compounds resulted higher degree of crosslinking (up to 80%) than the palm oil based compounds (up to 70%), where the different is around 10-15%. The hardness property from this two type coatings can reached until 50% at the lower percentage of the oligomer. However, the coatings from petrochemical-based have a high scratch resistance as it can withstand at least up to 3.0 Newtons (N) compared to the palm oil-based compounds which are difficult to withstand the load up to 1.0 N. Finally, the test on the rubber wood substrate showed that the coatings containing benzophenone photoinitiator give higher adhesion property and their also showed a higher glosiness property on the glass substrate compared to the coatings containing irgacure-819 photoinitiator. This study showed that the palm oil coatings can be a suitable for the replacement of petrochemicals compound for wood coating. The palm oil coatings can be more competitive in the market if the problems of using high percentage palm oil oligomer can be overcome as the palm oil price is cheap enough

  17. Development of palm oil-based UV-curable epoxy acrylate and urethane acrylate resins for wood coating application

    International Nuclear Information System (INIS)

    Rida Tajau; Nurulhuda Mohd Yunus; Mohd Hilmi Mahmood; Mek Zah Salleh; Nik Ghazali Nik Salleh

    2013-01-01

    Full-text: The trend of using renewable sources such as palm oil as raw material in radiation curing is growing due to the demand from the market to produce a more environmental friendly product. In this study, the radiation curable process was done using epoxy acrylate and urethane acrylate resins which are known as epoxidized palm olein acrylate (EPOLA) and palm oil based urethane acrylate (POBUA), respectively. The purpose of the study was to investigate curing properties and the application of this UV-curable palm oil resins for wood coating. Furthermore, the properties of palm oil based coatings are compared with the petrochemical-based compound such as ebecryl (EB) for example EB264 and EB830. From the experiment done, the resins from petrochemical-based compounds resulted higher degree of crosslinking (up to 80 %) than the palm oil based compounds (up to 70 %), where the different is around 10-15 %. The hardness property from this two type coatings can reached until 50 % at the lower percentage of the oligomer. However, the coatings from petrochemical-based have a high scratch resistance as it can withstand at least up to 3.0 Newton's (N) compared to the palm oil-based compounds which are difficult to withstand the load up to 1.0 N. Finally, the test on the rubber wood substrate showed that the coatings containing benzophenone photo initiator give higher adhesion property and their also showed a higher glossiness property on the glass substrate compared to the coatings containing irgacure-819 photo initiator. This study showed that the palm oil coatings can be a suitable for the replacement of petrochemicals compound for wood coating. The palm oil coatings can be more competitive in the market if the problems of using high percentage palm oil oligomer can be overcome as the palm oil price is cheap enough. (author)

  18. Development of palm oil-based UV-curable epoxy acrylate and urethane acrylate resins for wood coating application

    Energy Technology Data Exchange (ETDEWEB)

    Tajau, Rida; Mahmood, Mohd Hilmi; Salleh, Mek Zah; Salleh, Nik Ghazali Nik [Radiation Processing Technology Division, Malaysian Nuclear Agency (Nuclear Malaysia), Bangi, 43000 Kajang, Selangor (Malaysia); Ibrahim, Mohammad Izzat [Faculty of Science, University of Malaya (UM), 50603 Kuala Lumpur (Malaysia); Yunus, Nurulhuda Mohd [Faculty of Science and Technology, National University Malaysia (UKM), 43600 Bangi, Selangor (Malaysia)

    2014-02-12

    The trend of using renewable sources such as palm oil as raw material in radiation curing is growing due to the demand from the market to produce a more environmental friendly product. In this study, the radiation curable process was done using epoxy acrylate and urethane acrylate resins which are known as epoxidised palm olein acrylate (EPOLA) and palm oil based urethane acrylate (POBUA), respectively. The purpose of the study was to investigate curing properties and the application of this UV-curable palm oil resins for wood coating. Furthermore, the properties of palm oil based coatings are compared with the petrochemical-based compound such as ebecryl (EB) i.e. EB264 and EB830. From the experiment done, the resins from petrochemical-based compounds resulted higher degree of crosslinking (up to 80%) than the palm oil based compounds (up to 70%), where the different is around 10-15%. The hardness property from this two type coatings can reached until 50% at the lower percentage of the oligomer. However, the coatings from petrochemical-based have a high scratch resistance as it can withstand at least up to 3.0 Newtons (N) compared to the palm oil-based compounds which are difficult to withstand the load up to 1.0 N. Finally, the test on the rubber wood substrate showed that the coatings containing benzophenone photoinitiator give higher adhesion property and their also showed a higher glosiness property on the glass substrate compared to the coatings containing irgacure-819 photoinitiator. This study showed that the palm oil coatings can be a suitable for the replacement of petrochemicals compound for wood coating. The palm oil coatings can be more competitive in the market if the problems of using high percentage palm oil oligomer can be overcome as the palm oil price is cheap enough.

  19. Adhesion molecules

    CERN Document Server

    Preedy, Victor R

    2016-01-01

    This book covers the structure and classification of adhesion molecules in relation to signaling pathways and gene expression. It discusses immunohistochemical localization, neutrophil migration, and junctional, functional, and inflammatory adhesion molecules in pathologies such as leukocyte decompression sickness and ischemia reperfusion injury. Highlighting the medical applications of current research, chapters cover diabetes, obesity, and metabolic syndrome; hypoxia; kidney disease; smoking, atrial fibrillation, and heart disease, the brain and dementia; and tumor proliferation. Finally, it looks at molecular imaging and bioinformatics, high-throughput technologies, and chemotherapy.

  20. Bacterial Adhesion & Blocking Bacterial Adhesion

    DEFF Research Database (Denmark)

    Vejborg, Rebecca Munk

    2008-01-01

    , which influence the transition from a planktonic lifestyle to a sessile lifestyle, have been studied. Protein conditioning film formation was found to influence bacterial adhesion and subsequent biofilm formation considerable, and an aqueous extract of fish muscle tissue was shown to significantly...... tract to the microbial flocs in waste water treatment facilities. Microbial biofilms may however also cause a wide range of industrial and medical problems, and have been implicated in a wide range of persistent infectious diseases, including implantassociated microbial infections. Bacterial adhesion...... is the first committing step in biofilm formation, and has therefore been intensely scrutinized. Much however, still remains elusive. Bacterial adhesion is a highly complex process, which is influenced by a variety of factors. In this thesis, a range of physico-chemical, molecular and environmental parameters...

  1. Wood cross-arms coated with polyurethane resin - tests and numerical simulations

    Directory of Open Access Journals (Sweden)

    Ruy Alberto Correa Altafim

    2006-03-01

    Full Text Available Brazil's electric power utilities have commonly employed native timbers as the main material for manufacturing cross-arms for distribution lines. However, the increasingly high costs of these timbers and Brazil's new environmental laws have contributed to change this situation, spurring research on new materials for application in transmission and distribution systems. This paper discusses two reforested wood species, Pinus elliottii and Eucalyptus citriodora, coated with castor oil-based polyurethane resins, as an alternative material for distribution line cross-arms, from the standpoint of their mechanical and electrical properties and their low cost. Numerical simulations and a complete description of the entire coating process are also part of this work.

  2. Endothelial cell adhesion to ion implanted polymers

    Energy Technology Data Exchange (ETDEWEB)

    Suzuki, Y; Kusakabe, M [SONY Corp., Tokyo (Japan); Lee, J S; Kaibara, M; Iwaki, M; Sasabe, H [RIKEN (Inst. of Physical and Chemical Research), Saitama (Japan)

    1992-03-01

    The biocompatibility of ion implanted polymers has been studied by means of adhesion measurements of bovine aorta endothelial cells in vitro. The specimens used were polystyrene (PS) and segmented polyurethane (SPU). Na{sup +}, N{sub 2}{sup +}, O{sub 2}{sup +} and Kr{sup +} ion implantations were performed at an energy of 150 keV with fluences ranging from 1x10{sup 15} to 3x10{sup 17} ions/cm{sup 2} at room temperature. The chemical and physical structures of ion-implanted polymers have been investigated in order to analyze their tissue compatibility such as improvement of endothelial cell adhesion. The ion implanted SPU have been found to exhibit remarkably higher adhesion and spreading of endothelial cells than unimplanted specimens. By contrast, ion implanted PS demonstrated a little improvement of adhesion of cells in this assay. Results of FT-IR-ATR showed that ion implantation broke the original chemical bond to form new radicals such as OH, ....C=O, SiH and condensed rings. The results of Raman spectroscopy showed that ion implantation always produced a peak near 1500 cm{sup -1}, which indicated that these ion implanted PS and SPU had the same carbon structure. This structure is considered to bring the dramatic increase in the extent of cell adhesion and spreading to these ion implanted PS and SPU. (orig.).

  3. 40 CFR 721.8082 - Polyester polyurethane acrylate.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Polyester polyurethane acrylate. 721... Substances § 721.8082 Polyester polyurethane acrylate. (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as polyester polyurethane acrylate...

  4. 40 CFR 721.9959 - Polyurethane polymer (generic).

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Polyurethane polymer (generic). 721... Substances § 721.9959 Polyurethane polymer (generic). (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as a polyurethane polymer (PMN P-01...

  5. Polyurethane Production from Waste Bale Fibers

    Directory of Open Access Journals (Sweden)

    İbrahim BİLİCİ

    2017-12-01

    Full Text Available Nowadays, the methods of eliminating the pollution from wastes of the materials produced as much as the production methods are important. This requires efficiently use of sources economical and ecologically. Polyester based polymers, which is one of the most important consumed plastic materials in the world, have lots of number of recycling methods. Basically it is called chemical and physical recycling. Chemical recycle methods include glycolysis, aminolysis, methanolysis, hydrolysis and etc.. In this study aromatic polyester polyols produced from bale fiber wastes via glycolysis method. Zinc Acetate used as a catalysts and diethylene glycol used for the glycolysis reaction and moiety of glycol investigated as an experimental parameter. Polyurethane material produced via obtained polyol and TDI (Toluene di Isocyanate reaction. Obtained polyurethane material investigated via FTIR and TGA and compared with the commercial polyurethane. As a result, it has been decided that glycolysis is usable and applicable method for the waste bale fibers.

  6. Study of polyurethanes ageing offshore

    Energy Technology Data Exchange (ETDEWEB)

    Aquino, Fabio G.; Sheldrake, Terry; Clevelario, Judimar; Pires, Fabio [Wellstream International, Panama City, FL (United States); Coutinho, Fernanda M.B. [Universidade do Estado do Rio de Janeiro (UERJ), RJ (Brazil)

    2008-07-01

    The oil industry is one of the sectors with the highest number of production systems employing high technology. Brazil is worldwide renowned as a leader in oil and gas extraction in deep and ultra deep water. Inside the production chain, a great part the oil and gas produced is conveyed through flexible pipelines that connect the production wells to the platforms. There are two segments of these lines that receive different names according to their application characteristics. When the pipes are laid on the seabed in a static service condition, are called Flow lines and when they raise from the seabed to the platform in a dynamic service condition, are called Risers. The pipes designed for dynamic applications are equipped with Bend Stiffeners, components with conical form and in general with urethane basis, which has the function of providing a smooth stiffness transition between the flexible structure of the pipes and an extremely rigid structure, the platform, not allowing that this component infringes their minimum operation Bend Radius. According to Caire, the proper compression of curvature stiffeners and the material used in its manufacture is becoming increasingly important in industry due to its growing use and the occurrence of failures that have been recorded in recent years. This paper discusses the changes in the mechanical properties of polyurethanes by the hydrolysis during accelerated ageing, reaction of water with functional groups of the polymer chain, as well as mass variation, considering that these materials are designed for a service life exceeding twenty years for operation in water. (author)

  7. Development of a gelatin-based polyurethane vascular graft by spray, phase-inversion technology

    International Nuclear Information System (INIS)

    Losi, Paola; Al Kayal, Tamer; Briganti, Enrica; Volpi, Silvia; Soldani, Giorgio; Mancuso, Luisa; Cao, Giacomo; Celi, Simona; Gualerzi, Alice

    2015-01-01

    The capacity of a composite vascular graft constituting polyurethane (PU) and gelatin to support cell growth was investigated using human mesenchymal stem cells (hMSCs). Gelatin-based polyurethane grafts were fabricated by co-spraying polyurethane and gelatin using a spray, phase-inversion technique. Graft microstructure was investigated by light and scanning electron microscopy. Uniaxial tensile tests were performed to assess the grafts’ mechanical properties in longitudinal and circumferential directions. hMSCs obtained from bone marrow aspirate were seeded onto flat graft samples. After 24, 48, and 72 h of incubation, cell morphology was evaluated by Giemsa staining and cell viability was calculated by XTT assay. SEM analysis evidenced that PU samples display a microporous structure, whereas the gelatin-based PU samples show a fibrillar appearance. The presence of cross-linked gelatin produced a significant increase of ultimate tensile strength and ultimate elongation in circumferential directions compared to PU material. Qualitative analysis of hMSC adhesion onto the grafts revealed remarkable differences between gelatin-based PU and control graft. hMSCs grown onto gelatin-based PU graft form a monolayer that reached confluence at 72 h, whereas cells seeded onto the control graft were not able to undergo appropriate spreading. hMSCs grown onto gelatin-based PU graft showed significantly higher viability than cells seeded onto bare PU at all time points. In conclusion, a composite vascular graft was successfully manufactured by simultaneous co-spraying of a synthetic polymer and a protein to obtain a scaffold that combines the mechanical characteristics of polyurethanes with the favorable cell interaction features of gelatin. (paper)

  8. Effect of repeated contact on adhesion measurements involving polydimethylsiloxane structural material

    International Nuclear Information System (INIS)

    Kroner, E; Arzt, E; Maboudian, R

    2009-01-01

    During the last few years several research groups have focused on the fabrication of artificial gecko inspired adhesives. For mimicking these structures, different polymers are used as structure material, such as polydimethylsiloxanes (PDMS), polyurethanes (PU), and polypropylene (PP). While these polymers can be structured easily and used for artificial adhesion systems, the effects of repeated adhesion testing have never been investigated closely. In this paper we report on the effect of repeated adhesion measurements on the commercially available poly(dimethylsiloxane) polymer kit Sylgard 184 (Dow Corning). We show that the adhesion force decreases as a function of contact cycles. The rate of change and the final value of adhesion are found to depend on the details of the PDMS synthesis and structuring.

  9. Comparison of environmentally friendly, selective polyurethane catalysts

    Czech Academy of Sciences Publication Activity Database

    Strachota, Adam; Strachotová, Beata; Špírková, Milena

    2008-01-01

    Roč. 23, č. 6 (2008), s. 566-570 ISSN 1042-6914 R&D Projects: GA MPO FT-TA3/034 Institutional research plan: CEZ:AV0Z40500505 Keywords : amine catalyst * foam * gelation * kinetics * polyurethane Subject RIV: CD - Macromolecular Chemistry Impact factor: 0.706, year: 2008

  10. Flexible optical fiber sensor based on polyurethane

    DEFF Research Database (Denmark)

    Kaysir, Md Rejvi; Stefani, Alessio; Lwin, Richard

    Polyurethane (PU) based hollow core fibers are investigated as optical sensors. The flexibility of PU fibers makes it suitable for sensing mechanical perturbations. We fabricated a PU fiber using the fiber drawing method, characterized the fiber and experimentally demonstrated a simple way...... to measure deformation, in the form of applied pressure....

  11. The reactive extrusion of thermoplastic polyurethane

    NARCIS (Netherlands)

    Verhoeven, Vincent Wilhelmus Andreas

    2006-01-01

    The objective of this thesis was to increase the understanding of the reactive extrusion of thermoplastic polyurethane. Overall, several issues were identified: • Using a relative simple extrusion model, the reactive extrusion process can be described. This model can be used to further investigate

  12. Inkjet printing of polyurethane colloidal suspensions

    NARCIS (Netherlands)

    Berg, van den A.M.J.; Smith, P.J.; Perelaer, J.; Schrof, W.; Koltzenburg, S.; Schubert, U.S.

    2007-01-01

    An aqueous 40 wt% dispersion of polyurethane has been successfully printed at room temperature using a piezoelectric inkjet printer. Simple layered structures, as well as dots, were made and subsequently analyzed using white-light interferometry. A single layer was found to have a structure height

  13. Preparation of eugenol-based polyurethane

    Science.gov (United States)

    Li, Yupeng; Luo, Fang; Cheng, Chuanjie

    2018-03-01

    The regenerative eugenol was used as the starting material to prepare diol species by two steps, with a total yield of 28%. Furthermore, the prepared diol reacts with 1,6-hexadiisocyanate(HDI) to afford the corresponding polyurethane (PU). The structure of intermediates and PU are characterized by 1H-NMR or IR.

  14. Self-stratifying antimicrobial polyurethane coatings

    NARCIS (Netherlands)

    Yagci, M.B.; Bolca, S.; Heuts, J.P.A.; Ming, W.; With, de G.

    2011-01-01

    In this work antimicrobial polyurethane coatings were prepared aiming at self-stratification. A hydroxyl end-capped liquid oligoester consisting of three equimolar diacids and an excess of 1,4-butanediol has been synthesized by a condensation reaction. A set of quaternary ammonium compounds (QACs)

  15. Rigid polyurethane and kenaf core composite foams

    Science.gov (United States)

    Rigid polyurethane foams are valuable in many construction applications. Kenaf is a bast fiber plant where the surface stem skin provides bast fibers whose strength-to-weight ratio competes with glass fiber. The higher volume product of the kenaf core is an under-investigated area in composite appli...

  16. Time-dependent crashworthiness of polyurethane foam

    Science.gov (United States)

    Basit, Munshi Mahbubul; Cheon, Seong Sik

    2018-05-01

    Time-dependent stress-strain relationship as well as crashworthiness of polyurethane foam was investigated under constant impact energy with different velocities, considering inertia and strain-rate effects simultaneously during the impact testing. Even though the impact energies were same, the percentage in increase in densification strain due to higher impact velocities was found, which yielded the wider plateau region, i.e. growth in crashworthiness. This phenomenon is analyzed by the microstructure of polyurethane foam obtained from scanning electron microscopy. The equations, coupled with the Sherwood-Frost model and the impulse-momentum theory, were employed to build the constitutive equation of the polyurethane foam and calculate energy absorption capacity of the foam. The nominal stress-strain curves obtained from the constitutive equation were compared with results from impact tests and were found to be in good agreement. This study is dedicated to guiding designer use polyurethane foam in crashworthiness structures such as an automotive bumper system by providing crashworthiness data, determining the crush mode, and addressing a mathematical model of the crashworthiness.

  17. Effect of leaning angle of gecko-inspired slanted polymer nanohairs on dry adhesion

    KAUST Repository

    Jeong, Hoon Eui; Lee, Jin-Kwan; Kwak, Moon Kyu; Moon, Sang Heup; Suh, Kahp Yang

    2010-01-01

    We present analysis of adhesion properties of angled polymer nanohairs with a wide range of leaning angles from 0° to 45° and ultraviolet (UV)-curable polyurethane acrylate (PUA) materials of two different elastic moduli (19.8 and 320 MPa). It is demonstrated that shear adhesion and adhesion hysteresis can be greatly enhanced by increasing the leaning angle of nanohairs both for soft and hard materials due to increased contact area and reduced structural stiffness. © 2010 American Institute of Physics.

  18. Offshore disposal of oil-based drilling fluid waste

    International Nuclear Information System (INIS)

    Malachosky, E.; Shannon, B.E.; Jackson, J.E.

    1991-01-01

    Offshore drilling operations in the Gulf of Mexico may use oil-based drilling fluids to mitigate drilling problems. The result is the generation of a significant quantity of oily cuttings and mud. The transportation of this waste for onshore disposal is a concern from a standpoint of both personnel safety and potential environmental impact. A process for preparing a slurry of this waste and the subsequent disposal of the slurry through annular pumping has been put into use by ARCO Oil and Gas Company. The disposal technique has been approved by the Minerals Management Service (MMS). The slurried waste is displaced down a casing annulus into a permeable zone at a depth below the surface casing setting depth. The annular disposal includes all cuttings and waste oil mud generated during drilling with oil-based fluids. This disposal technique negates the need for cuttings storage on the platform, transportation to shore, and the environmental effects of onshore surface disposal. The paper describes the environmental and safety concerns with onshore disposal, the benefits of annular disposal, and the equipment and process used for the preparation and pumping of the slurry

  19. Graded porous polyurethane foam: A potential scaffold for oro-maxillary bone regeneration

    Energy Technology Data Exchange (ETDEWEB)

    Giannitelli, S.M. [Department of Engineering, Tissue Engineering Unit, Università Campus Bio-Medico di Roma, Rome (Italy); Basoli, F. [Department of Chemical Science and Technology, University of Rome “Tor Vergata”, Rome (Italy); Mozetic, P. [Department of Engineering, Tissue Engineering Unit, Università Campus Bio-Medico di Roma, Rome (Italy); Piva, P.; Bartuli, F.N.; Luciani, F. [University of Rome “Tor Vergata”, Rome (Italy); Arcuri, C. [Department of Periodontics, University of Rome “Tor Vergata”, Rome (Italy); U.O.C.C. Odontostomatology, “S. Giovanni Calibita, Fatebenefratelli” Hospital, Rome (Italy); Trombetta, M. [Department of Engineering, Tissue Engineering Unit, Università Campus Bio-Medico di Roma, Rome (Italy); Rainer, A., E-mail: a.rainer@unicampus.it [Department of Engineering, Tissue Engineering Unit, Università Campus Bio-Medico di Roma, Rome (Italy); Licoccia, S. [Department of Chemical Science and Technology, University of Rome “Tor Vergata”, Rome (Italy)

    2015-06-01

    Bone tissue engineering applications demand for biomaterials offering a substrate for cell adhesion, migration, and proliferation, while inferring suitable mechanical properties to the construct. In the present study, polyurethane (PU) foams were synthesized to develop a graded porous material—characterized by a dense shell and a porous core—for the treatment of oro-maxillary bone defects. Foam was synthesized via a one-pot reaction starting from a polyisocyanate and a biocompatible polyester diol, using water as a foaming agent. Different foaming conditions were examined, with the aim of creating a dense/porous functional graded material that would perform at the same time as an osteoconductive scaffold for bone defect regeneration and as a membrane-barrier to gingival tissue ingrowth. The obtained PU was characterized in terms of morphological and mechanical properties. Biocompatibility assessment was performed in combination with bone-marrow-derived human mesenchymal stromal cells (hBMSCs). Our findings confirm that the material is potentially suitable for guided bone regeneration applications. - Highlights: • Graded porous polyurethane foams were synthesized via a one-pot foaming reaction. • The inner porous core might act as a scaffold for guided bone regeneration. • A dense outer shell was introduced to act as a barrier to gingival tissue ingrowth. • The synthesized foams were non-toxic and supportive of hBMSC adhesion.

  20. Graded porous polyurethane foam: A potential scaffold for oro-maxillary bone regeneration

    International Nuclear Information System (INIS)

    Giannitelli, S.M.; Basoli, F.; Mozetic, P.; Piva, P.; Bartuli, F.N.; Luciani, F.; Arcuri, C.; Trombetta, M.; Rainer, A.; Licoccia, S.

    2015-01-01

    Bone tissue engineering applications demand for biomaterials offering a substrate for cell adhesion, migration, and proliferation, while inferring suitable mechanical properties to the construct. In the present study, polyurethane (PU) foams were synthesized to develop a graded porous material—characterized by a dense shell and a porous core—for the treatment of oro-maxillary bone defects. Foam was synthesized via a one-pot reaction starting from a polyisocyanate and a biocompatible polyester diol, using water as a foaming agent. Different foaming conditions were examined, with the aim of creating a dense/porous functional graded material that would perform at the same time as an osteoconductive scaffold for bone defect regeneration and as a membrane-barrier to gingival tissue ingrowth. The obtained PU was characterized in terms of morphological and mechanical properties. Biocompatibility assessment was performed in combination with bone-marrow-derived human mesenchymal stromal cells (hBMSCs). Our findings confirm that the material is potentially suitable for guided bone regeneration applications. - Highlights: • Graded porous polyurethane foams were synthesized via a one-pot foaming reaction. • The inner porous core might act as a scaffold for guided bone regeneration. • A dense outer shell was introduced to act as a barrier to gingival tissue ingrowth. • The synthesized foams were non-toxic and supportive of hBMSC adhesion

  1. Effects of a fish oil-based emulsion on rat hepatoma cell invasion in culture.

    Science.gov (United States)

    Hagi, Akifumi; Nakayama, Mitsuo; Miura, Yutaka; Yagasaki, Kazumi

    2007-01-01

    Total parenteral nutrition containing a lipid emulsion is often employed after surgical tumor resection. This study investigated the effects of a fish oil-based infusion on rat hepatoma cell invasion. Rat ascites hepatoma cell line AH109A was precultured with a fish oil-based or safflower oil-based emulsion for 48 h. Changes in membranous fatty acid composition were evaluated by gas chromatography. The invasiveness of hepatoma cells was assessed by coculturing with mesentery-derived mesothelial cells. To examine ex vivo effects of the fish oil-based infusion on hepatoma invasion, sera were prepared from rats infused with fish oil- or safflower oil-based emulsion and the effects of these sera were assessed. To clarify the mechanism of inhibition of invasion by the fish oil-based emulsion, the effects of prostaglandin (PG) E(2) and PGE(3) on invasion were examined. Pretreatment with the fish oil-based emulsion reduced invasiveness without affecting growth compared with the safflower oil-based emulsion. Pretreatment with the sera from rats infused with the fish oil-based emulsion also reduced invasiveness compared with the sera from rats infused with the safflower oil-based emulsion. The addition of PGE(2) eliminated the inhibitory effect of the fish oil-based emulsion, and the addition of PGE(3) reduced the invasiveness of hepatoma cells pretreated with the safflower oil-based emulsion. These results suggest that the fish oil-based emulsion may have anti-invasive effects. Changes in the membranous fatty acid composition and consequent changes in the prostaglandins produced may be involved in this inhibitory effect.

  2. Biodegradable polyurethane nanocomposites containing dexamethasone for ocular route

    International Nuclear Information System (INIS)

    Rodrigues da Silva, Gisele; Silva-Cunha, Armando da; Behar-Cohen, Francine; Ayres, Eliane; Orefice, Rodrigo L.

    2011-01-01

    The treatment of posterior segment ocular diseases, such as uveitis, by using eye drops and oral drugs is usually not effective due to the body's natural barriers to drug penetration. In this study, ocular implants to treat uveitis were synthesized by incorporating dexamethasone acetate, an important type of corticoid used in the treatment of some uveitis, into a biodegradable polyurethane containi clay nanoparticles. Biodegradable polyurethane nanocomposites having poly(caprolactone) oligomers as soft segments were obtained by delaminating clay particles within a polyurethane aqueous dispersion. The drug was incorporated into the polymer by dispersing it in the waterborne polyurethane followed by a drying step. Nanoparticles derived from clay were demonstrated to be able to tailor the mechanical properties of polyurethanes to achieve values that can match the properties of ocular soft tissues. Infrared spectra (FTIR) showed that the presence of clay particles was able to change the microphase separation process typical of polyurethanes. X-ray diffraction and small angle x-ray scattering (SAXS) results were explored to show that the incorporation of both dexamethasone acetate and nanocomponents derived from clay led to a less defined two-phase polyurethane. The presence of clay nanoparticles increased the rate of drug release measured in vitro. Human retinal pigment epithelial cells (ARPE-19) were cultured in contact with polyurethanes and polyurethane nanocomposites, and the viability of them (evaluated by using MTT assay after 7 days) showed that no toxic components were released from polyurethanes containing no drugs during the test.

  3. Biodegradable polyurethane nanocomposites containing dexamethasone for ocular route

    Energy Technology Data Exchange (ETDEWEB)

    Rodrigues da Silva, Gisele [Federal University of Sao Joao Del Rei, School of Pharmacy, Divinopolis, Minas Gerais (Brazil); Silva-Cunha, Armando da [Federal University of Minas Gerais, School of Pharmacy, Belo Horizonte, Minas Gerais (Brazil); Behar-Cohen, Francine [INSERM, Physiopathology of ocular diseases: Therapeutic innovations, Institut des Cordeliers, Paris (France); Laboratoire d' Innovations Therapeutiques, Fondation Rothschild, Paris (France); Universite Rene Descartes, Hotel Dieu University Hospital, Paris (France); Ayres, Eliane [Federal University of Minas Gerais, Department of Metallurgical and Materials Engineering, Belo Horizonte, Minas Gerais (Brazil); Orefice, Rodrigo L., E-mail: rorefice@demet.ufmg.br [Federal University of Minas Gerais, Department of Metallurgical and Materials Engineering, Belo Horizonte, Minas Gerais (Brazil)

    2011-03-12

    The treatment of posterior segment ocular diseases, such as uveitis, by using eye drops and oral drugs is usually not effective due to the body's natural barriers to drug penetration. In this study, ocular implants to treat uveitis were synthesized by incorporating dexamethasone acetate, an important type of corticoid used in the treatment of some uveitis, into a biodegradable polyurethane containi clay nanoparticles. Biodegradable polyurethane nanocomposites having poly(caprolactone) oligomers as soft segments were obtained by delaminating clay particles within a polyurethane aqueous dispersion. The drug was incorporated into the polymer by dispersing it in the waterborne polyurethane followed by a drying step. Nanoparticles derived from clay were demonstrated to be able to tailor the mechanical properties of polyurethanes to achieve values that can match the properties of ocular soft tissues. Infrared spectra (FTIR) showed that the presence of clay particles was able to change the microphase separation process typical of polyurethanes. X-ray diffraction and small angle x-ray scattering (SAXS) results were explored to show that the incorporation of both dexamethasone acetate and nanocomponents derived from clay led to a less defined two-phase polyurethane. The presence of clay nanoparticles increased the rate of drug release measured in vitro. Human retinal pigment epithelial cells (ARPE-19) were cultured in contact with polyurethanes and polyurethane nanocomposites, and the viability of them (evaluated by using MTT assay after 7 days) showed that no toxic components were released from polyurethanes containing no drugs during the test.

  4. Friction welding of wood – A fast, adhesive-free bonding technology for prefabricated elements in timber construction

    OpenAIRE

    Hahn, Benjamin; Hatt, Fred

    2013-01-01

    Up to now chemical adhesives based on polyurethane are used for the assembling of timber planks to large-scale structural elements, in particular cross-laminated timber panels (CLT), which opened new possibilities for architects and engineers in timber construction. The use of these adhesives still implicates, beside others, concerns about their impact on health and environment during application as well for later disposal. In order to overcome the geometrical limitations of timber by maintai...

  5. Polyurethane/polylactide-based biomaterials combined with rat olfactory bulb-derived glial cells and adipose-derived mesenchymal stromal cells for neural regenerative medicine applications.

    Science.gov (United States)

    Grzesiak, Jakub; Marycz, Krzysztof; Szarek, Dariusz; Bednarz, Paulina; Laska, Jadwiga

    2015-01-01

    Research concerning the elaboration and application of biomaterial which may support the nerve tissue regeneration is currently one of the most promising directions. Biocompatible polymer devices are noteworthy group among the numerous types of potentially attractive biomaterials for regenerative medicine application. Polylactides and polyurethanes may be utilized for developing devices for supporting the nerve regeneration, like nerve guide conduits or bridges connecting the endings of broken nerve tracts. Moreover, the combination of these biomaterial devices with regenerative cell populations, like stem or precursor cells should significantly improve the final therapeutic effect. Therefore, the composition and structure of final device should support the proper adhesion and growth of cells destined for clinical application. In current research, the three polymer mats elaborated for connecting the broken nerve tracts, made from polylactide, polyurethane and their blend were evaluated both for physical properties and in vitro, using the olfactory-bulb glial cells and mesenchymal stem cells. The evaluation of Young's modulus, wettability and roughness of obtained materials showed the differences between analyzed samples. The analysis of cell adhesion, proliferation and morphology showed that the polyurethane-polylactide blend was the most neutral for cells in culture, while in the pure polymer samples there were significant alterations observed. Our results indicated that polyurethane-polylactide blend is an optimal composition for culturing and delivery of glial and mesenchymal stem cells. Copyright © 2015. Published by Elsevier B.V.

  6. The use of abrasive polishing and laser processing for developing polyurethane surfaces for controlling fibroblast cell behaviour

    International Nuclear Information System (INIS)

    Irving, Michael; Murphy, Mark F; Lilley, Francis; French, Paul W; Burton, David R; Dixon, Simon; Sharp, Martin C

    2017-01-01

    Studies have shown that surfaces having micro and nano-scale features can be used to control cell behaviours including; cell proliferation, migration and adhesion. The aim of this work was to compare the use of laser processing and abrasive polishing to develop micro/nano-patterned polyurethane substrates for controlling fibroblast cell adhesion, migration and proliferation. Laser processing in a directional manner resulted in polyurethane surfaces having a ploughed field effect with micron-scale features. In contrast, abrasive polishing in a directional and random manner resulted in polyurethane surfaces having sub-micron scale features orientated in a linear or random manner. Results show that when compared with flat (non-patterned) polymer, both the laser processed and abrasive polished surface having randomly organised features, promoted significantly greater cell adhesion, while also enhancing cell proliferation after 72 h. In contrast, the abrasive polished surface having linear features did not enhance cell adhesion or proliferation when compared to the flat surface. For cell migration, the cells growing on the laser processed and abrasively polished random surface showed decreased levels of migration when compared to the flat surface. This study shows that both abrasive polishing and laser processing can be used to produce surfaces having features on the nano-scale and micron-scale, respectively. Surfaces produced using both techniques can be used to promote fibroblast cell adhesion and proliferation. Thus both methods offer a viable alternative to using lithographic techniques for developing patterned surfaces. In particular, abrasive polishing is an attractive method due to it being a simple, rapid and inexpensive method that can be used to produce surfaces having features on a comparable scale to more expensive, multi-step methods. - Highlights: • Abrasive polishing can generate nano-scratches on stainless steel to cast polymer films for cell

  7. The use of abrasive polishing and laser processing for developing polyurethane surfaces for controlling fibroblast cell behaviour

    Energy Technology Data Exchange (ETDEWEB)

    Irving, Michael; Murphy, Mark F; Lilley, Francis; French, Paul W; Burton, David R [General Engineering Research Institute, Liverpool John Moores University, Liverpool, L3 3AF (United Kingdom); Dixon, Simon [Biomer Technology LTD, 10 Seymour Court, Tudor Road, Manor Park, Runcorn, Cheshire, WA7 1SY (United Kingdom); Sharp, Martin C [General Engineering Research Institute, Liverpool John Moores University, Liverpool, L3 3AF (United Kingdom)

    2017-02-01

    Studies have shown that surfaces having micro and nano-scale features can be used to control cell behaviours including; cell proliferation, migration and adhesion. The aim of this work was to compare the use of laser processing and abrasive polishing to develop micro/nano-patterned polyurethane substrates for controlling fibroblast cell adhesion, migration and proliferation. Laser processing in a directional manner resulted in polyurethane surfaces having a ploughed field effect with micron-scale features. In contrast, abrasive polishing in a directional and random manner resulted in polyurethane surfaces having sub-micron scale features orientated in a linear or random manner. Results show that when compared with flat (non-patterned) polymer, both the laser processed and abrasive polished surface having randomly organised features, promoted significantly greater cell adhesion, while also enhancing cell proliferation after 72 h. In contrast, the abrasive polished surface having linear features did not enhance cell adhesion or proliferation when compared to the flat surface. For cell migration, the cells growing on the laser processed and abrasively polished random surface showed decreased levels of migration when compared to the flat surface. This study shows that both abrasive polishing and laser processing can be used to produce surfaces having features on the nano-scale and micron-scale, respectively. Surfaces produced using both techniques can be used to promote fibroblast cell adhesion and proliferation. Thus both methods offer a viable alternative to using lithographic techniques for developing patterned surfaces. In particular, abrasive polishing is an attractive method due to it being a simple, rapid and inexpensive method that can be used to produce surfaces having features on a comparable scale to more expensive, multi-step methods. - Highlights: • Abrasive polishing can generate nano-scratches on stainless steel to cast polymer films for cell

  8. Electrospun propolis/polyurethane composite nanofibers for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jeong In [Department of Bio-nano System Engineering, Chonbuk National University, Jeonju 561–756 (Korea, Republic of); Pant, Hem Raj, E-mail: hempant@jbnu.ac.kr [Department of Bio-nano System Engineering, Chonbuk National University, Jeonju 561–756 (Korea, Republic of); Department of Engineering Science and Humanities, Pulchowk Campus, Tribhuvan University, Kathmandu (Nepal); Research Institute for Next Generation, Kalanki, Kathmandu (Nepal); Sim, Hyun-Jaung [Department of Bioactive Material Science, Research Center of Bioactive Material, Chonbuk National University, Jeonju, Chonbuk (Korea, Republic of); Lee, Kang Min [Department of Molecular Biology, College of Natural Science, Chonbuk National University, Jeonju, 561–756 (Korea, Republic of); Kim, Cheol Sang, E-mail: chskim@jbnu.ac.kr [Department of Bio-nano System Engineering, Chonbuk National University, Jeonju 561–756 (Korea, Republic of)

    2014-11-01

    Tissue engineering requires functional polymeric membrane for adequate space for cell migration and attachment within the nanostructure. Therefore, biocompatible propolis loaded polyurethane (propolis/PU) nanofibers were successfully prepared using electrospinning of propolis/PU blend solution. Here, composite nanofibers were subjected to detailed analysis using electron microscopy, FT-IR spectroscopy, thermal gravimetric analysis (TGA), and mechanical properties and water contact angle measurement. FE-SEM images revealed that the composite nanofibers became point-bonded with increasing amounts of propolis in the blend due to its adhesive properties. Incorporation of small amount of propolis through PU matrix could improve the hydrophilicity and mechanical strength of the fibrous membrane. In order to assay the cytocompatibility and cell behavior on the composite scaffolds, fibroblast cells were seeded on the matrix. Results suggest that the incorporation of propolis into PU fibers could increase its cell compatibility. Moreover, composite nanofibers have effective antibacterial activity. Therefore, as-synthesized nanocomposite fibrous mat has great potentiality in wound dressing and skin tissue engineering. - Highlights: • Sufficient amount of propolis is simply loaded through PU fibers. • Propolis increases the hydrophilicity and mechanical properties of PU fibers. • Composite mat shows excellent antibacterial activity. • Small amount of propolis can enhance the cell compatibility of PU fibers.

  9. Electrospun propolis/polyurethane composite nanofibers for biomedical applications

    International Nuclear Information System (INIS)

    Kim, Jeong In; Pant, Hem Raj; Sim, Hyun-Jaung; Lee, Kang Min; Kim, Cheol Sang

    2014-01-01

    Tissue engineering requires functional polymeric membrane for adequate space for cell migration and attachment within the nanostructure. Therefore, biocompatible propolis loaded polyurethane (propolis/PU) nanofibers were successfully prepared using electrospinning of propolis/PU blend solution. Here, composite nanofibers were subjected to detailed analysis using electron microscopy, FT-IR spectroscopy, thermal gravimetric analysis (TGA), and mechanical properties and water contact angle measurement. FE-SEM images revealed that the composite nanofibers became point-bonded with increasing amounts of propolis in the blend due to its adhesive properties. Incorporation of small amount of propolis through PU matrix could improve the hydrophilicity and mechanical strength of the fibrous membrane. In order to assay the cytocompatibility and cell behavior on the composite scaffolds, fibroblast cells were seeded on the matrix. Results suggest that the incorporation of propolis into PU fibers could increase its cell compatibility. Moreover, composite nanofibers have effective antibacterial activity. Therefore, as-synthesized nanocomposite fibrous mat has great potentiality in wound dressing and skin tissue engineering. - Highlights: • Sufficient amount of propolis is simply loaded through PU fibers. • Propolis increases the hydrophilicity and mechanical properties of PU fibers. • Composite mat shows excellent antibacterial activity. • Small amount of propolis can enhance the cell compatibility of PU fibers

  10. Bio-based hyperbranched thermosetting polyurethane/triethanolamine functionalized multi-walled carbon nanotube nanocomposites as shape memory materials.

    Science.gov (United States)

    Kalita, Hemjyoti; Karak, Niranjan

    2014-07-01

    Here, bio-based shape memory polymers have generated immense interest in recent times. Here, Bio-based hyperbranched polyurethane/triethanolamine functionalized multi-walled carbon nanotube (TEA-f-MWCNT) nanocomposites were prepared by in-situ pre-polymerization technique. The Fourier transform infrared spectroscopy and the transmission electron microscopic studies showed the strong interfacial adhesion and the homogeneous distribution of TEA-f-MWCNT in the polyurethane matrix. The prepared epoxy cured thermosetting nanocomposites exhibited enhanced tensile strength (6.5-34.5 MPa), scratch hardness (3.0-7.5 kg) and thermal stability (241-288 degrees C). The nanocomposites showed excellent shape fixity and shape recovery. The shape recovery time decreases (24-10 s) with the increase of TEA-f-MWCNT content in the nanocomposites. Thus the studied nanocomposites have potential to be used as advanced shape memory materials.

  11. Comparison of Selected Properties of Shellac Varnish for Restoration and Polyurethane Varnish for Reconstruction of Historical Artefacts

    Directory of Open Access Journals (Sweden)

    Kristýna Šimůnková

    2018-03-01

    Full Text Available At present, many historical artefacts and furniture are only reconstructed and not restored. They are preserved in terms of material reparation, but their historical value decreases significantly. This work is focused on the comparison of the resistance of high-gloss polyurethane varnish with traditional shellac varnish. The varnishes were applied to oak wood and exposed to interior artificial accelerated ageing in Xenotest. Before and after ageing, cold liquid-resistance tests were performed on the tested specimens and gloss, colour, and adhesion were also evaluated. The structures of the surfaces were also analysed using a confocal laser scanning microscope. As expected, polyurethane varnish was much more durable than shellac varnish. Interestingly, shellac varnish was fairly resistant to water at the beginning, but this resistance was greatly reduced after artificial accelerated ageing. This illustrates the importance of sheltering the shellac treated artefacts in stable temperature-humidity conditions with the least possible effect of solar radiation.

  12. Synthesis and characterization of nanocomposites based on polyurethane in aqueous dispersions with non-modified hydrophilic clays

    International Nuclear Information System (INIS)

    Miranda, G.S.; Delpechi, M.C.; Santo, W.L.E.

    2010-01-01

    Several studies involving the formation of polyurethane nanocomposites employing clays of montmorillonite modified. This involves the presence of quaternary ammonium salts, the cation exchange needed to increase the interlayer space of clays that incorporate more than one step to the process, generates a higher cost. In this paper the synthesis of nanocomposite polyurethanes dispersed in water allowed not only the production of materials less harmful to the environment, but also the incorporation of hydrophilic clays, calcium and sodium in nature, without any modifications. Dispersions produced from 0.5, 1.0 and 2.5% clay (on the mass of prepolymer) were characterized in terms of total solids content, the films obtained by casting were evaluated for adhesiveness, diffraction X-rays, scanning electron microscopy. Most systems showed intercalated and partially exfoliated structures. (author)

  13. Development of halthane adhesives for phase 3 weapons: status report

    International Nuclear Information System (INIS)

    Hammon, H.G.; Althouse, L.P.

    1975-01-01

    Three new adhesives of the polyurethane type have been developed to meet the requirements for the current phase 3 nuclear weapons. They are designated Halthanes to avoid confusion with Adiprenes. Two of these adhesives are made from LLL-developed MDI-terminated prepolymers cured with a blend of polyols. The third is made from an LLL-developed prepolymer terminated with Hylene W and cured with aromatic diamines. All of the adhesives have low moduli over a wide temperature range, bond rapidly and well to most substrates, and are compatible with weapons components. This report updates information reported in Chemistry Department Technical Notes Nos. 75-23 and 75-24. Characterization and compatibility studied are continuing

  14. Marine biofouling resistance of polyurethane with biodegradation and hydrolyzation.

    Science.gov (United States)

    Xu, Wentao; Ma, Chunfeng; Ma, Jielin; Gan, Tiansheng; Zhang, Guangzhao

    2014-03-26

    We have prepared polyurethane with poly(ε-caprolactone) (PCL) as the segments of the main chain and poly(triisopropylsilyl acrylate) (PTIPSA) as the side chains by a combination of radical polymerization and a condensation reaction. Quartz crystal microbalance with dissipation studies show that polyurethane can degrade in the presence of enzyme and the degradation rate decreases with the PTIPSA content. Our studies also demonstrate that polyurethane is able to hydrolyze in artificial seawater and the hydrolysis rate increases as the PTIPSA content increases. Moreover, hydrolysis leads to a hydrophilic surface that is favorable to reduction of the frictional drag under dynamic conditions. Marine field tests reveal that polyurethane has good antifouling ability because polyurethane with a biodegradable PCL main chain and hydrolyzable PTIPSA side chains can form a self-renewal surface. Polyurethane was also used to carry and release a relatively environmentally friendly antifoulant, and the combined system exhibits a much higher antifouling performance even in a static marine environment.

  15. Plant oil-based shape memory polymer using acrylic monolith

    Directory of Open Access Journals (Sweden)

    T. Tsujimoto

    2015-09-01

    Full Text Available This article deals with the synthesis of a plant oil-based material using acrylic monolith. An acrylic monolith bearing oxirane groups was prepared via simple technique that involved the dissolution of poly(glycidyl methacrylate-comethyl methacrylate (PGMA in ethanolic – aqueous solution by heating and subsequent cooling. The PGMA monolith had topologically porous structure, which was attributed to the phase separation of the polymer solution. The PGMA monolith was impregnated by epoxidized soybean oil (ESO containing thermally-latent catalyst, and the subsequent curing produced a crosslinked material with relatively good transparency. The Young’s modulus and the tensile strength of polyESO/PGMA increased compared with the ESO homopolymer. The strain at break of polyESO/PGMA was larger than that of the ESO homopolymer and crosslinked PGMA. Furthermore, polyESO/PGMA exhibited good shape memory-recovery behavior.

  16. Designing a suitable alternative to oil-based mud

    International Nuclear Information System (INIS)

    Holgate, M.; Irwin, G.; Cousins, L.

    1991-01-01

    This paper reports on wireline logging problems which have plagued the reservoir section of development wells in Welton oil field in the East Midlands area of England. And resulting incomplete or poor-quality logging data spurred a look at ways of improving hole conditions. Oil-based muds often are seen as the ideal solution, but they are expensive. Their use also commits the operator to additional costs from safeguarding personnel and limiting environmental impact. Such expense was initiated to develop a cheaper, more environmentally friendly, water-based alternative. A wide-ranging review was carried out to determine the most cost-effective options to obtain reservoir information. This included an examination of lithology, casing design, bit selection, hydraulics, logging requirements and techniques, and development of a suitable water-based mud. This holistic approach was seen as the most effective method of avoiding use of oil-based mud. After successful experimentation, a water-based mud was used in subsequent wells at Welton. A high-salt mud system and the drilling principles discussed here produced significant improvement in hole conditions. Application of a holistic approach led to many operational improvements. For instance, the casing shoe was deepened to case off the most troublesome zone in the local Edlington formation. There also was a better awareness of alternative logging techniques, the commercial factors that influenced their use and their operational and technical limitations. Logging problems were reduced but not eliminated. Where there were problems, application of improved techniques minimized their impact. Last, but not least, there was an unexpected spin-off in that the bit chosen to reduce hole erosion also reduced the time taken to drill the section

  17. Urinary catheter with polyurethane coating modified by ion implantation

    International Nuclear Information System (INIS)

    Kondyurina, I.; Nechitailo, G.S.; Svistkov, A.L.; Kondyurin, A.; Bilek, M.

    2015-01-01

    A low friction urinary catheter that could be used without a lubricant is proposed in this work. A polyurethane coating was synthesised on the surface of a metal guide wire catheter. Ion implantation was applied to surface modify the polyurethane coating. FTIR ATR, wetting angle, AFM and friction tests were used for analysis. Low friction was found to be provided by the formation of a hard carbonised layer on the polyurethane surface

  18. Degradation mechanism of polyurethane foam induced by electron beam irradiation

    International Nuclear Information System (INIS)

    Huang Wei; Fu Yibei; Bian Zhishang; He Meiying

    2002-01-01

    The degradation mechanism of irradiated polyurethane foam has been studied in detail. The changes of chemical structure and micro-phase separation have been determined by DTG. The gas products from irradiated samples are analyzed quantitatively and qualitatively by GC. The degradation mechanism of irradiated polyurethane foam has been deduced according to the experimental results. It provides some basis of the application on the polyurethane in the radiation field

  19. Rigid Polyurethane Foam Reinforced Coconut Coir Fiber Properties

    OpenAIRE

    Mohd Azham Azmi

    2012-01-01

    This research work studied the properties of composite foam panels. Coconut coir fibers were used as reinforcement in polyurethane (PU) foam in order to increase the properties of foam. This composite foam panels were fabricated by using polyurethane molded method. The polyurethane foam panels reinforced from 5 to 20wt% coconut coir were produced to investigate the physical and mechanical test via density test and three point bending test respectively. It was found that the density test resul...

  20. Bio-based polyurethane for tissue engineering applications: How hydroxyapatite nanoparticles influence the structure, thermal and biological behavior of polyurethane composites.

    Science.gov (United States)

    Gabriel, Laís P; Santos, Maria Elizabeth M Dos; Jardini, André L; Bastos, Gilmara N T; Dias, Carmen G B T; Webster, Thomas J; Maciel Filho, Rubens

    2017-01-01

    In this work, thermoset polyurethane composites were prepared by the addition of hydroxyapatite nanoparticles using the reactants polyol polyether and an aliphatic diisocyanate. The polyol employed in this study was extracted from the Euterpe oleracea Mart. seeds from the Amazon Region of Brazil. The influence of hydroxyapatite nanoparticles on the structure and morphology of the composites was studied using scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS), the structure was evaluated by Fourier transform infrared spectroscopy (FT-IR), thermal properties were analyzed by thermogravimetry analysis (TGA), and biological properties were studied by in vitro and in vivo studies. It was found that the addition of HA nanoparticles promoted fibroblast adhesion while in vivo investigations with histology confirmed that the composites promoted connective tissue adherence and did not induce inflammation. In this manner, this study supports the further investigation of bio-based, polyurethane/hydroxyapatite composites as biocompatible scaffolds for numerous tissue engineering applications. Copyright © 2016 Elsevier Inc. All rights reserved.

  1. Characterization and properties of sepiolite/polyurethane nanocomposites

    International Nuclear Information System (INIS)

    Chen Hongxiang; Zheng Maosheng; Sun Hongying; Jia Qingming

    2007-01-01

    In situ polymerization method is employed to prepare sepiolite/polyurethane nanocomposite. The morphology and the dispersion of sepiolite in polyurethane have been characterized by X-ray diffraction, scanning electron microscope, transmission electron microscope and Fourier transform infrared spectroscopy. The results show the sepiolite is dispersed homogeneously in the polyurethane matrix at a nanometer scale. The tensile test shows that the tensile strength and elongation at break for the nanocomposites increase with the addition of sepiolite as compared to those of the pure polyurethane. The TGA analysis reveals that the addition of nanofillers results in the higher thermal stability

  2. Crosslinked polyurethanes based on hyperbranched polymers

    Directory of Open Access Journals (Sweden)

    Vuković Jasna

    2008-01-01

    Full Text Available In this paper, two samples of polyurethane (PU crosslinked with hydroxy -functonal hyperbranched aliphatic polyester of the second pseudo generation were investigated. For the synthesis of these crosslinked PUs two different macrodiols were used: poly(tetramethyleneoxide (PTMO for PUPTMO and ethylene oxide-poly(dimethylsiloxane-ethylene oxide (PDMS-EO for PUPDMS-EO sample. Synthesized samples behave as elastomers and have yellow color. Obtained results show that swelling degree of the sample PUPDMS-EO in N-methyl-2-pyrrolidinon (NMP determined at room temperature is higher than for the sample PUPTMO. It has been also observed that thermal properties of these polyurethane networks can be changed by incorporation of siloxane sequences in their structure.

  3. Novel metallomesogenic polyurethanes: Synthesis, characterization and properties

    International Nuclear Information System (INIS)

    Senthilkumar, Natarajan; Narasimhaswamy, Tanneru; Kim, Il-Jin

    2012-01-01

    A series of tetradentate Schiff base metallomesogenic diols were synthesized from two simple dihydroxy benzenes. The metallomesogenic diol was constructed from three ring containing mesogen linked through ester and azomethine with terminal hydroxy group. This upon complexation with copper(II) formed metallomesogenic diol with varying terminal chain length. A series of metallomesogenic polyurethanes were synthesized using these metallomesogenic diols as chain extenders for the prepolymers based on polytetramethylene glycol (PTMG) of varying molecular weight (M n = 650, 2000) and 2,4-toluene diisocyanate (TDI), or 4,4′-methylene bis(phenyl isocyanate) (MDI). The molar ratio of metallomesogenic diol and PTMG were varied in the polyurethane to find their role in liquid crystalline and mechanical properties. Extensive characterization of all metallomesogenic compounds and intermediates were carried out by FT-IR, 1 H and 13 C NMR, EPR, VSM, Mass (EI and FAB) and UV–visible spectroscopy. Hot stage polarizing microscope and differential scanning calorimetry were used to ensure the phase characteristics such as nature of phase, melting and clearing temperatures and phase range. The appearance of enantiotropic smectic A phases indicated high molecular polarizability of the core due to the metal ion. - Highlights: ► Design and synthesis of metallomesogenic diols. ► Metallomesogenic polyurethanes were prepared using these diols as chain extenders. ► Liquid crystalline and mechanical properties were studied. ► A square pyramidal structure for the copper(II) complexes have been proposed. ► Polyurethanes exhibited enantiotropic smectic A phases.

  4. Biodegradability of polyurethane/polysaccharide blends

    International Nuclear Information System (INIS)

    Mothe, Cheila G.; Leite, Selma G.

    2001-01-01

    Biodegradable polymers for use in environmental waste-management has been the subject of much discussion over the last few years. Polyurethane mixtures with polysaccharide (80/20 and 90/10 w/w ) have been prepared and films obtained. These films were inoculated, according to ASTM G22-76 rule and analysed by thermogravimetry and scanning electronic microscopy (SEM). The results are discussed in terms of thermal degradation and biodegradability. (author)

  5. Epoxy polyurethane nanocomposites filled with fullerite

    International Nuclear Information System (INIS)

    Rozhnova, R.A.; Galatenko, N.A.; Lukashevich, S.A.; Shirokov, O.D.; Levenets', Je.G.

    2015-01-01

    New nanocomposite materials based on epoxy polyurethane (EPU) containing nanoscale fullerite in its composition are produced. The influence of small impurities of fullerite on physical and mechanical properties of the nanocomposites is established. The effect of a nanofiller and its concentration on the structure and properties of the composite and the ability to biodegradation in vitro is studied. The developed nanocomposites exhibit the biodegradability, and the presence of nanofillers in the EPU facilitates the course of the process

  6. Adhesion in microelectronics

    CERN Document Server

    Mittal, K L

    2014-01-01

    This comprehensive book will provide both fundamental and applied aspects of adhesion pertaining to microelectronics in a single and easily accessible source. Among the topics to be covered include; Various theories or mechanisms of adhesionSurface (physical or chemical) characterization of materials as it pertains to adhesionSurface cleaning as it pertains to adhesionWays to improve adhesionUnraveling of interfacial interactions using an array of pertinent techniquesCharacterization of interfaces / interphasesPolymer-polymer adhesionMetal-polymer adhesion  (metallized polymers)Polymer adhesi

  7. Reflections about Adhesive Systems

    OpenAIRE

    de Freitas Borges, Marciano; Diesel, Pâmela Gutheil; Corrêa, Fernanda Gomez; Bernardi, Eledana; Fernandes Montagner, Anelise; Skupien, Jovito Adiel; Susin, Alexandre Henrique

    2010-01-01

    The adhesive systems are responsible for an efficient union between teeth and resin, resulting in a longevity restoration. They are organic molecules di or multifunctional that contain reactive groups that interact with dentin and with the resin monomer of composite resin. The adhesive systems are characterized by wet adhesion, which is a result of presence of hidrophylics radicals in their compositions, to promote a better bond and the best properties of the adhesion. Adhesive systems may us...

  8. 40 CFR 446.10 - Applicability; description of the oil-base solvent wash paint subcategory.

    Science.gov (United States)

    2010-07-01

    ...-base solvent wash paint subcategory. 446.10 Section 446.10 Protection of Environment ENVIRONMENTAL...-Base Solvent Wash Paint Subcategory § 446.10 Applicability; description of the oil-base solvent wash... production of oil-base paint where the tank cleaning is performed using solvents. When a plant is subject to...

  9. Evaluation gamma radiation in composite sisal fiber- polyurethane derived of castor oil by bending test; Avaliacao da influencia da radiacao gama em compositos de fibra de sisal - poliuretano derivado de oleo de mamona atraves de ensaios de flexao

    Energy Technology Data Exchange (ETDEWEB)

    Souza, Felipe H. de; Geraldo, Ricardo R.; Vasco, Marina C.; Azevedo, Elaine, E-mail: helunica@yahoo.com.br [Universidade Tecnologica Federal do Parana (UTFPR), Curitiba, PR (Brazil); Claro Neto, Salvador [Universidade de Sao Paulo (USP), Sao Carlos, SP (Brazil). Instituto de Quimica

    2015-07-01

    Materials used for making furniture and accessories or positioning in X -ray examination rooms should not exhale volatile organic compounds and are resistant to ionizing radiation. One solution is the use of vegetable fiber and polyurethane composites of vegetable origin, since they are biodegradable, derived from renewable raw materials and have no volatile organic compounds. The main difficulty in developing this material is fiber adhesion with the polymer. The objective of this study is to evaluate the mechanical properties of composite sisal fiber composite, without further treatment, and polyurethane derived from castor oil, with a dose of 25 kGy gamma radiation, subjected to 3 points bending tests. (author)

  10. Strenght of the glue line of edge glued panels of Pinus taeda made with different adhesives

    Directory of Open Access Journals (Sweden)

    Merielen de Carvalho Lopes

    2013-12-01

    Full Text Available The study compares the strength of the glue line of edge glued panels of Pinus taeda made with different industrial adhesives. Three types of adhesives (poly(vinyl acetate (PVAc, emulsion polymer isocyanate (EPI and polyurethane (PU glued in two side gluing orientation (radial and tangential and analyzed after the conditioning tests (dry and wet were analyzed. The 360 specimens were prepared for determining the shear strength of edge glued panels of Pinus taeda, and these were tested in a universal testing machine called EMIC. The shear strength of the glue line at dry condition was lower in the tangential side for the three types of adhesives analyzed. The PU adhesive showed the highest values of shear strength in the applied conditions, differing from PVAc and EPI adhesive when tested on dry condition and did not differ from the others adhesives when tested on wet condition. The highest percentage of wood failure was observed after the shear strength test at dry condition to EPI adhesive glued in the radial side. And in the wet condition, the EPI adhesive and PU adhesive glued in tangential side showed higher mean values of wood failure. Thus, it was possible to conclude that the strength of the glue line of Pinus taeda wood was influenced by the type of adhesive and side gluing orientation, and showed differently behavior according to the condition of use (wet or dry.

  11. Fluorinated Polyurethane Scaffolds for 19F Magnetic Resonance Imaging

    NARCIS (Netherlands)

    Lammers, Twan; Mertens, Marianne E.; Schuster, Philipp; Rahimi, Khosrow; Shi, Yang; Schulz, Volkmar; Kuehne, Alexander J.C.; Jockenhoevel, Stefan; Kiessling, Fabian

    2017-01-01

    Researchers used fluorinated polyurethane scaffolds for 19F magnetic resonance imaging. They generated a novel fluorinated polymer based on thermoplastic polyurethane (19F -TPU) which possesses distinct properties rendering it suitable for fluorine-based MRI. The 19F -TPU is synthesized from a

  12. Molecular simulation of fibronectin adsorption onto polyurethane surfaces

    Science.gov (United States)

    Polyethylene glycol-based polyurethanes have been widely used in biomedical applications, however are prone to swelling. A natural polyol, castor oil can be incorporated into these polyurethanes to control the degree of the swelling, which alters mechanical properties and protein adsorption characte...

  13. Optimization of polyurethane foam cube in enhancing the ...

    African Journals Online (AJOL)

    Attachment of microalgae biomass to polyurethane foam material is believed could reduce the cost and time needed for harvesting process in making it reliable to be used in industry for biodiesel production. This paper aim to optimize the usage of polyurethane for higher attachment of microalgae biomass yield in term of it ...

  14. Systematic approach for synthesis of palm oil-based biorefinery

    Energy Technology Data Exchange (ETDEWEB)

    NG, Rex T. L.; NG, Denny K. S.; LAM, Hon Loong [Dept. of Chemical and Environmental Engineering, Centre of Excellence for Green Technologies, Univ. of Nottingham, Selangor, (Malaysia); TAY, Douglas H. S.; LIM, Joseph H. E. [2GGS Eco Solutions Sdn Bhd, Kuala Lumpur (Malaysia)

    2012-11-01

    Various types of palm oil biomasses are generated from palm oil mill when crude palm oil (CPO) is produced from fresh fruit bunch (FFB). In the current practice, palm oil biomasses are used as the main source of energy input in the palm oil mill to produce steam and electricity. Moreover, those biomasses are regarded as by-products and can be reclaimed easily. Therefore, there is a continuous increasing interest concerning biomasses generated from the palm oil mill as a source of renewable energy. Although various technologies have been exploited to produce bio-fuel (i.e., briquette, pellet, etc.) as well as heat and power generation, however, no systematic approach which can analyse and optimise the synthesise biorefinery is presented. In this work, a systematic approach for synthesis and optimisation of palm oil-based biorefinery which including palm oil mill and refinery with maximum economic performance is developed. The optimised network configuration with achieves the maximum economic performance can also be determined. To illustrate the proposed approach, a case study is solved in this work.

  15. Design and development of low cost polyurethane biopolymer based on castor oil and glycerol for biomedical applications.

    Science.gov (United States)

    Tan, A C W; Polo-Cambronell, B J; Provaggi, E; Ardila-Suárez, C; Ramirez-Caballero, G E; Baldovino-Medrano, V G; Kalaskar, D M

    2018-02-01

    In the current study, we present the synthesis of novel low cost bio-polyurethane compositions with variable mechanical properties based on castor oil and glycerol for biomedical applications. A detailed investigation of the physicochemical properties of the polymer was carried out by using mechanical testing, ATR-FTIR, and X-ray photoelectron spectroscopy (XPS). Polymers were also tested in short term in-vitro cell culture with human mesenchymal stem cells to evaluate their biocompatibility for potential applications as biomaterial. FTIR analysis confirmed the synthesis of castor oil and glycerol based PU polymers. FTIR also showed that the addition of glycerol as co-polyol increases crosslinking within the polymer backbone hence enhancing the bulk mechanical properties of the polymer. XPS data showed that glycerol incorporation leads to an enrichment of oxidized organic species on the surface of the polymers. Preliminary investigation into in vitro biocompatibility showed that serum protein adsorption can be controlled by varying the glycerol content with polymer backbone. An alamar blue assay looking at the metabolic activity of the cells indicated that castor oil based PU and its variants containing glycerol are non-toxic to the cells. This study opens an avenue for using low cost bio-polyurethane based on castor oil and glycerol for biomedical applications. © 2017 The Authors Biopolymers Published by Wiley Periodicals, Inc.

  16. Biodegradative Activities of Selected Environmental Fungi on a Polyester Polyurethane Varnish and Polyether Polyurethane Foams.

    Science.gov (United States)

    Álvarez-Barragán, Joyce; Domínguez-Malfavón, Lilianha; Vargas-Suárez, Martín; González-Hernández, Ricardo; Aguilar-Osorio, Guillermo; Loza-Tavera, Herminia

    2016-09-01

    Polyurethane (PU) is widely used in many aspects of modern life because of its versatility and resistance. However, PU waste disposal generates large problems, since it is slowly degraded, there are limited recycling processes, and its destruction may generate toxic compounds. In this work, we isolated fungal strains able to grow in mineral medium with a polyester PU (PS-PU; Impranil DLN) or a polyether PU (PE-PU; Poly Lack) varnish as the only carbon source. Of the eight best Impranil-degrading strains, the six best degraders belonged to the Cladosporium cladosporioides complex, including the species C. pseudocladosporioides, C. tenuissimum, C. asperulatum, and C. montecillanum, and the two others were identified as Aspergillus fumigatus and Penicillium chrysogenum The best Impranil degrader, C. pseudocladosporioides strain T1.PL.1, degraded up to 87% after 14 days of incubation. Fourier transform infrared (FTIR) spectroscopy analysis of Impranil degradation by this strain showed a loss of carbonyl groups (1,729 cm(-1)) and N-H bonds (1,540 and 1,261 cm(-1)), and gas chromatography-mass spectrometry (GC-MS) analysis showed a decrease in ester compounds and increase in alcohols and hexane diisocyanate, indicating the hydrolysis of ester and urethane bonds. Extracellular esterase and low urease, but not protease activities were detected at 7 and 14 days of culture in Impranil. The best eight Impranil-degrading fungi were also able to degrade solid foams of the highly recalcitrant PE-PU type to different extents, with the highest levels generating up to 65% of dry-weight losses not previously reported. Scanning electron microscopy (SEM) analysis of fungus-treated foams showed melted and thinner cell wall structures than the non-fungus-treated ones, demonstrating fungal biodegradative action on PE-PU. Polyurethane waste disposal has become a serious problem. In this work, fungal strains able to efficiently degrade different types of polyurethanes are reported, and

  17. Indoor air pollution evaluation with emphasize on HDI and biological assessment of HDA in the polyurethane factories.

    Science.gov (United States)

    Mirmohammadi, Mirtaghi; Hakimi Ibrahim, M; Ahmad, Anees; Kadir, Mohd Omar Abdul; Mohammadyan, M; Mirashrafi, S B

    2010-06-01

    Today, many raw materials used in factories may have a dangerous effect on the physiological system of workers. One of them which is widely used in the polyurethane factories is diisocyanates. These compounds are widely used in surface coatings, polyurethane foams, adhesives, resins, elastomers, binders, and sealants. Exposure to diisocyanates causes irritation to the skin, mucous membranes, eyes, and respiratory tract. Hexamethylene diamine (HDA) is metabolite of hexamethylene diisocyanate (HDI). It is an excretory material by worker's urine who is exposed to HDI. Around 100 air samples were collected from five defined factories by midget impinger which contained dimethyl sulfoxide absorbent as a solvent and tryptamine as reagent. Samples were analyzed by high-performance liquid chromatography with EC\\UV detector using NIOSH 5522 method of sampling. Also, 50 urine samples collected from workers were also analyzed using William's biological analysis method. The concentration of HDI into all air samples were more than 88 microg/m(3), and they have shown high concentration of pollutant in the workplaces in comparison with NIOSH standard, and all of the workers' urine were contaminated by HDA. The correlation and regression test were used to obtain statistical model for HDI and HDA, which is useful for the prediction of diisocyanates pollution situation in the polyurethane factories.

  18. Development of segmented polyurethane elastomers with low iodine content exhibiting radiopacity and blood compatibility.

    Science.gov (United States)

    Dawlee, S; Jayabalan, Muthu

    2011-10-01

    Biofunctionally active and inherently radiopaque polymers are the emerging need for biomedical applications. Novel segmented polyurethane elastomer with inherent radiopacity was prepared using aliphatic chain extender 2,3-diiodo-2-butene-1,4-diol, polyol polytetramethylene glycol and 4,4'-methylenebis(phenyl isocyanate) (MDI) for blood compatible applications. Aliphatic polyurethane was also prepared using hexamethylene diisocyanate for comparison. X-ray analysis of the polyurethanes revealed good radiopacity even at a relatively low concentration of 3% iodine in aromatic polyurethane and 10% in aliphatic polyurethane. The polyurethanes also possessed excellent thermal stability. MDI-based polyurethane showed considerably higher tensile strength than the analogous HDI-based polyurethane. MDI-based aromatic polyurethane exhibited a dynamic surface morphology in aqueous medium, resulting in the segregation of hydrophilic domains which was more conducive to anti-thrombogenic properties. The polyurethane was cytocompatible with L929 fibroblast cells, non-hemolytic, and possessed good blood compatibility.

  19. Development of segmented polyurethane elastomers with low iodine content exhibiting radiopacity and blood compatibility

    International Nuclear Information System (INIS)

    Dawlee, S; Jayabalan, Muthu

    2011-01-01

    Biofunctionally active and inherently radiopaque polymers are the emerging need for biomedical applications. Novel segmented polyurethane elastomer with inherent radiopacity was prepared using aliphatic chain extender 2,3-diiodo-2-butene-1,4-diol, polyol polytetramethylene glycol and 4,4'-methylenebis(phenyl isocyanate) (MDI) for blood compatible applications. Aliphatic polyurethane was also prepared using hexamethylene diisocyanate for comparison. X-ray analysis of the polyurethanes revealed good radiopacity even at a relatively low concentration of 3% iodine in aromatic polyurethane and 10% in aliphatic polyurethane. The polyurethanes also possessed excellent thermal stability. MDI-based polyurethane showed considerably higher tensile strength than the analogous HDI-based polyurethane. MDI-based aromatic polyurethane exhibited a dynamic surface morphology in aqueous medium, resulting in the segregation of hydrophilic domains which was more conducive to anti-thrombogenic properties. The polyurethane was cytocompatible with L929 fibroblast cells, non-hemolytic, and possessed good blood compatibility.

  20. Development of segmented polyurethane elastomers with low iodine content exhibiting radiopacity and blood compatibility

    Energy Technology Data Exchange (ETDEWEB)

    Dawlee, S; Jayabalan, Muthu, E-mail: muthujayabalan@rediffmail.com [Polymer Science Division, Biomedical Technology Wing, Sree Chitra Tirunal Institute for Medical Sciences and Technology, Thiruvananthapuram, Kerala 695 012 (India)

    2011-10-15

    Biofunctionally active and inherently radiopaque polymers are the emerging need for biomedical applications. Novel segmented polyurethane elastomer with inherent radiopacity was prepared using aliphatic chain extender 2,3-diiodo-2-butene-1,4-diol, polyol polytetramethylene glycol and 4,4'-methylenebis(phenyl isocyanate) (MDI) for blood compatible applications. Aliphatic polyurethane was also prepared using hexamethylene diisocyanate for comparison. X-ray analysis of the polyurethanes revealed good radiopacity even at a relatively low concentration of 3% iodine in aromatic polyurethane and 10% in aliphatic polyurethane. The polyurethanes also possessed excellent thermal stability. MDI-based polyurethane showed considerably higher tensile strength than the analogous HDI-based polyurethane. MDI-based aromatic polyurethane exhibited a dynamic surface morphology in aqueous medium, resulting in the segregation of hydrophilic domains which was more conducive to anti-thrombogenic properties. The polyurethane was cytocompatible with L929 fibroblast cells, non-hemolytic, and possessed good blood compatibility.

  1. Strategies to improve the adhesion of rubbers to adhesives by means of plasma surface modification

    Science.gov (United States)

    Martín-Martínez, J. M.; Romero-Sánchez, M. D.

    2006-05-01

    The surface modifications produced by treatment of a synthetic sulfur vulcanized styrene-butadiene rubber with oxidizing (oxygen, air, carbon dioxide) and non oxidizing (nitrogen, argon) RF low pressure plasmas, and by treatment with atmospheric plasma torch have been assessed by ATR-IR and XPS spectroscopy, SEM, and contact angle measurements. The effectiveness of the low pressure plasma treatment depended on the gas atmosphere used to generate the plasma. A lack of relationship between surface polarity and wettability, and peel strength values was obtained, likely due to the cohesive failure in the rubber obtained in the adhesive joints. In general, acceptable adhesion values of plasma treated rubber were obtained for all plasmas, except for nitrogen plasma treatment during 15 minutes due to the creation of low molecular weight moieties on the outermost rubber layer. A toluene wiping of the N{2 } plasma treated rubber surface for 15 min removed those moieties and increased adhesion was obtained. On the other hand, the treatment of the rubber with atmospheric pressure by means of a plasma torch was proposed. The wettability of the rubber was improved by decreasing the rubber-plasma torch distance and by increasing the duration because a partial removal of paraffin wax from the rubber surface was produced. The rubber surface was oxidized by the plasma torch treatment, and the longer the duration of the plasma torch treatment, the higher the degree of surface oxidation (mainly creation of C O moieties). However, although the rubber surface was effectively modified by the plasma torch treatment, the adhesion was not greatly improved, due to the migration of paraffin wax to the treated rubber-polyurethane adhesive interface once the adhesive joint was produced. On the other hand, the extended treatment with plasma torch facilitated the migration of zinc stearate to the rubber-adhesive interface, also contributing to deteriorate the adhesion in greater extent. Finally

  2. Nasolacrimal Polyurethane Stent: Complications with CT Correlation

    International Nuclear Information System (INIS)

    Pinto, Isabel T.; Paul, Laura; Grande, Carlos

    1998-01-01

    Purpose: To evaluate initial results in patients with epiphora secondary to obstruction of the nasolacrimal duct treated by placement of a polyurethane stent, and to discuss the technical problems and complications arising during the procedure, with visualization of the anatomy of the drainage apparatus using computed tomography (CT). Methods: We inserted 20 polyurethane Song stents under fluoroscopic guidance after dacryocystography in 19 patients with grade 3-4 epiphora caused by idiopathic obstruction of the nasolacrimal duct. CT scans were obtained following stent placement in all patients. Results: We focus on the technical problems and complications that arose during these procedures. During negotiation of the guidewire past the obstruction at the level of the junction of the duct with the lacrimal sac, the guidewire created a false passage in a posterior suborbital direction in two cases and towards the posterior midline in another. In all cases the guidewire was withdrawn and reinserted through the proper anatomic route without further difficulty or complications. In two cases the stent was improperly positioned wholly or partially outside the nasolacrimal system (one medially, one posteriorly). In one case the stent was removed and reinserted; in the other it remains in place and functional. CT was performed in all these cases to ensure proper anatomic alignment and determine what had gone wrong. The epiphora was completely resolved in 13 cases and partially relieved in four; there were three cases of stent obstruction. Epistaxis of short duration (1 hr) occurred in seven patients and headache in one. Conclusions: Treatment of epiphora with polyurethane stents is a technique that is well tolerated by patients and achieves a high success rate, yet problems in placement may be encountered. Though no major consequences for patients are involved, cognizance of such difficulties is important to avoid incorrect positioning of stents

  3. Polyurethane/nano-hydroxyapatite composite films as osteogenic platforms.

    Science.gov (United States)

    Jackson, Bailey K; Bow, Austin J; Kannarpady, Ganesh; Biris, Alexandru S; Anderson, David E; Dhar, Madhu; Bourdo, Shawn E

    2018-05-02

    A wide variety of biomaterials are utilized in tissue engineering to promote cell proliferations in vitro or tissue growth in vivo. The combination of cells, extracellular matrices, and biocompatible materials may make it possible to grow functional living tissues ranging from bone to nerve cells. In bone regeneration, polymeric scaffolds can be enhanced by the addition of bioactive materials. To this end, this study designed several ratios of polyurethane (PU) and nano-hydroxyapatite (nHA) composites (PU-nHA ratios: 100/0, 90/10, 80/20, 70/30, 60/40 w/w). The physical and mechanical properties of these composites and their relative cellular compatibility in vitro were determined. The chemical composition and crystallinity of the composites were confirmed using X-ray diffraction, X-ray photoelectron spectroscopy, and thermogravimetric analyses. Atomic force microscopy, nano-indentation, and contact angle measurements were used to evaluate surface properties. The results showed a significant increase in surface roughness and a decrease in contact angle when the nHA concentration increased above 20%, resulting in a significant increase in hydrophilicity. These surface property changes influenced cellular behavior when MC 3T3-E1 cells were seeded on the composites. All composites were cytocompatible. There was a linear increase in cell proliferation on the 80/20 and 70/30 composites only, whereas subjective evaluation demonstrated noticeable clusters or nodules of cells (considered hallmarks of osteogenic differentiation) in the absence of any osteogenic inducers only on the 90/10 and 80/20 composites. Cellular data suggests that the 80/20 composite was an optimal environment for cell adhesion, proliferation, and, potentially, osteogenic differentiation in vitro.

  4. Preparation of smooth, flexible and stable silver nanowires- polyurethane composite transparent conductive films by transfer method

    Science.gov (United States)

    Bai, Shengchi; Wang, Haifeng; Yang, Hui; Zhang, He; Guo, Xingzhong

    2018-02-01

    Silver nanowires (AgNWs)-polyurethane (PU) composite transparent conductive films were fabricated via transfer method using AgNWs conductive inks and polyurethane as starting materials, and the effects of post-treatments including heat treatment, NaCl solution bath and HCl solution bath for AgNWs film on the sheet resistance and transmittance of the composite films were respectively investigated in detail. AgNWs networks are uniformly embedded in the PU layer to improve the adhesion and reduce the surface roughness of AgNWs-PU composite films. Heat treatment can melt and weld the nanowires, and NaCl and HCl solution baths promote the dissolution and re-deposition of silver and the dissolving of the polymer, both which form conduction pathways and improve contact of AgNWs for reducing the sheet resistance. Smooth and flexible AgNWs-PU composite film with a transmittance of 85% and a sheet resistance of 15 Ω · sq‑1 is obtained after treated in 0.5 wt% HCl solution bath for 60 s, and the optoelectronic properties of the resultant composite film can maintain after 1000 cycles of bending and 100 days.

  5. Synthesis and properties of aqueous polyurethane dispersions: Influence of molecular weight of polyethylene glycol

    Energy Technology Data Exchange (ETDEWEB)

    Mumtaz, Fatima; Zuber, Mohammad; Zia, Khalid Mahmood [Government College University, Faisalabad (Pakistan); Jamil, Tahir [University of the Punjab, Lahore (Pakistan); Hussain, Rizwan [National Engineering and Scientific Commission (NESCOM), Islamabad (Pakistan)

    2013-12-15

    Aqueous polyurethane dispersions (PUDs) have recently emerged as important alternatives to their solvent-based counterparts for various applications due to increasing health and environmental awareness. A series of aqueous polyurethane dispersions containing carboxylate anion as hydrophilic pendant groups were synthesized through step growth polymerization reaction using hexamethylene diisocyanate (HDI), 1,4-butanediol (1,4-BDO), dimethylol propionic acid (DMPA) and polyethylene glycol (PEG) of different molecular weight. Effect of PEG molecular weight was investigated on molecular structure, contact angle measurement, and physical and adhesive properties of PU emulsions. Fourier transform infrared spectroscopy (FT-IR) was used to check the completion of polymerization reaction. Contact angle measurement indicated that the hydrophilicity of polymer increases by increasing molecular weight of PEG with a corresponding decrease in contact angle. Results of T-peel test showed a decrease in peel strength by increasing molecular weight of PEG. Moreover, solid contents%, drying time and storage stability suggested fast drying properties and greater stability of aqueous PU dispersions.

  6. Polyurethane elastomer as a matrix material for short carbon fiber reinforced thermoplastic composites

    Directory of Open Access Journals (Sweden)

    Ümit Tayfun

    2017-09-01

    Full Text Available Short carbon fibers (CF with different surface sized (epoxy (EP and polyurethane (PU were used as reinforcing agent in thermoplastic polyurethane (TPU based composites. Composites containing 5, 10, 15, and 20 weight % sized and desized CFs were prepared by using melt-mixing method. The surface characteristics of CFs were examined by energy dispersive X-ray spectroscopy (EDX and Fourier transform infrared spectroscopy (FTIR. Tensile testing, shore hardness test, dynamic mechanical analysis (DMA and melt flow index (MFI test were performed for determining final composite properties. The dispersion of CFs in TPU matrix was examined by scanning electron microscopy (SEM. Tensile strength, Youngs’ modulus and Shore hardness of TPU were enhanced by the addition of sized CFs. About two-fold improvement for tensile strength and ten-fold improvement for Youngs’ modulus were observed with the incorporation of 20 wt% EP-CF and PU-CF in TPU. The storage modulus of PU-CF containing composites was higher than those of TPU and other composites. No remarkable change was observed in MFI value of TPU after CF loadings. Processing conditions in this work was suitable for composite production. Sized CFs exhibited better dispersion with regard to desized CF due to the stronger adhesion of TPU matrix to fiber surface.

  7. Chapter 9:Wood Adhesion and Adhesives

    Science.gov (United States)

    Charles R. Frihart

    2013-01-01

    The recorded history of bonding wood dates back at least 3000 years to the Egyptians (Skeist and Miron 1990, River 1994a), and adhesive bonding goes back to early mankind (Keimel 2003). Although wood and paper bonding are the largest applications for adhesives, some of the fundamental aspects leading to good bonds are not fully understood. Better understanding of these...

  8. Mechanical Characterization of Rigid Polyurethane Foams

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Wei-Yang [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States). Mechanics of Materials

    2014-12-01

    Foam materials are used to protect sensitive components from impact loading. In order to predict and simulate the foam performance under various loading conditions, a validated foam model is needed and the mechanical properties of foams need to be characterized. Uniaxial compression and tension tests were conducted for different densities of foams under various temperatures and loading rates. Crush stress, tensile strength, and elastic modulus were obtained. A newly developed confined compression experiment provided data for investigating the foam flow direction. A biaxial tension experiment was also developed to explore the damage surface of a rigid polyurethane foam.

  9. Study of fuel properties of rubber seed oil based biodiesel

    International Nuclear Information System (INIS)

    Ahmad, Junaid; Yusup, Suzana; Bokhari, Awais; Kamil, Ruzaimah Nik Mohammad

    2014-01-01

    Graphical abstract: - Highlights: • This article presents the comparative studies of the fuel properties of rubber seed oil based biodiesel. • The design expert has been adopted for the optimization of the process variables. • The FTIR, cold flow properties and oxidation stability are the findings of present study. • All the fuel properties met the standards such as ASTM D6751 and EN 14214. • Present study reveals that rubber seed oil as a non-edible source potentially contributes for esters production. - Abstract: The scarcity of the fossil fuel, environmental pollution and food crisis are the world’s major issues in current era. Biodiesel is an alternative to diesel fuel, environment friendly and biodegradable and is produced from either edible or non-edible oils. In this study, a non-edible rubber seed oil (RSO) with high free fatty acid (FFA) content of 45% were used for the production of biodiesel. The process comprises of two steps. The first step is the acid esterification to reduce the FFA value and the second step is the base transesterification. The response surface methodology (RSM) was used for parametric optimization of the two stage processes i.e. acid esterification and base transesterification. The yield of biodiesel was analyzed using gas chromatography. The FTIR (Fourier Transform Infra-Red) spectrum was also determined to confirm the conversion of fatty acid to methyl esters. The fuel properties were analyzed according to the ASTM D6751 and EN14214 and were compared with the previous finding of researchers. All analyzed properties fulfilled the biodiesel standard criteria

  10. Laminated composite based on polyester geotextile fibers and polyurethane resin for coating wood structures

    Directory of Open Access Journals (Sweden)

    Yuri Andrey Olivato Assagra

    2013-01-01

    Full Text Available New environmental laws have restricted the use of hardwood trees in overhead power lines structures, such as, poles and cross-arms, leading companies to seek alternative materials. Reforested wood coated with polymeric resin has been proposed as an environmental friendly solution, with improved electrical properties and protection against external agents, e.g. moisture, ultraviolet radiation and fungi. However, the single thin layer of resin, normally applied on such structures reveal to be inefficient, due to be easily damage during handling. In this paper, we present a composite coating, based on geotextile fibers and polyurethane resin that is suitable for wooden structures. Results obtained from two different tree species (from managed and reforested areas coated with the composite reveal that the additional layer not only provided a stronger adhesion between wood and ccoating layer but also a further improvement in the electrical properties and better protection against abrasion and moisture.

  11. Specie – treatment – adhesive combinations for glulam purpose

    Directory of Open Access Journals (Sweden)

    Carlito Calil Neto

    2016-12-01

    Full Text Available Glued laminated timber is an engineered product that requires precision manufacturing in all its stages. The finished product can only be tested in laboratory conditions. However, it is necessary to have quality control in the production to ensure that the properties of the glulam are appropriate to the product specified requirements in accordance with the standards. In Brazil is still no specific standard of qualification for the manufactures of Glulam. In this context, different kinds of wood, adhesives and preservative treatments in the composition of Glulam can be used. This paper aims to evaluate the proposed trials conducted with combinations of four Brazilian reforestation species, three adhesives and three types of preservative treatment. As a result was observed that combinations, which showed the best performance, were pine and parica wood, with any type of adhesive or treatment investigated, which can be used in exterior applications. Lyptus® wood for any combination of treatments falls into the internal use class. Teak wood can be used indoors (adhesive polyurethane and all kinds of treatment or external (phenol resorcinol formaldehyde adhesive and all kinds of treatment.

  12. PH dependent adhesive peptides

    Science.gov (United States)

    Tomich, John; Iwamoto, Takeo; Shen, Xinchun; Sun, Xiuzhi Susan

    2010-06-29

    A novel peptide adhesive motif is described that requires no receptor or cross-links to achieve maximal adhesive strength. Several peptides with different degrees of adhesive strength have been designed and synthesized using solid phase chemistries. All peptides contain a common hydrophobic core sequence flanked by positively or negatively charged amino acids sequences.

  13. Prevention of bacterial adhesion

    DEFF Research Database (Denmark)

    Klemm, Per; Vejborg, Rebecca Munk; Hancock, Viktoria

    2010-01-01

    . As such, adhesion represents the Achilles heel of crucial pathogenic functions. It follows that interference with adhesion can reduce bacterial virulence. Here, we illustrate this important topic with examples of techniques being developed that can inhibit bacterial adhesion. Some of these will become...

  14. Synthetic Adhesive Attachment Discs based on Spider Pyriform Silk Architecture

    Science.gov (United States)

    Jain, Dharamdeep; Sahni, Vasav; Dhinojwala, Ali

    2014-03-01

    Among the variety of silks produced by spiders, pyriform silk is used in conjunction with the dragline silk to attach webs to different surfaces. Cob weaver spiders employ different architectural patterns to utilize the pyriform silk and form attachment joints with each pattern having a characteristic adhesive performance. The staple pin architecture is a one of the strongest attachment designs employed by spiders to attach their webs. Here we use a synthetic approach to create the a similar patterned architecture attachment discs on aluminum substrate using thermoplastic polyurethane. Measurable pull off forces are generated when the synthetic discs are peeled off a surface. This innovative adhesive strategy can be a source of design in various biomedical applications. Financial Support from National Science Foundation.

  15. A review: fabrication of porous polyurethane scaffolds.

    Science.gov (United States)

    Janik, H; Marzec, M

    2015-03-01

    The aim of tissue engineering is the fabrication of three-dimensional scaffolds that can be used for the reconstruction and regeneration of damaged or deformed tissues and organs. A wide variety of techniques have been developed to create either fibrous or porous scaffolds from polymers, metals, composite materials and ceramics. However, the most promising materials are biodegradable polymers due to their comprehensive mechanical properties, ability to control the rate of degradation and similarities to natural tissue structures. Polyurethanes (PUs) are attractive candidates for scaffold fabrication, since they are biocompatible, and have excellent mechanical properties and mechanical flexibility. PU can be applied to various methods of porous scaffold fabrication, among which are solvent casting/particulate leaching, thermally induced phase separation, gas foaming, emulsion freeze-drying and melt moulding. Scaffold properties obtained by these techniques, including pore size, interconnectivity and total porosity, all depend on the thermal processing parameters, and the porogen agent and solvents used. In this review, various polyurethane systems for scaffolds are discussed, as well as methods of fabrication, including the latest developments, and their advantages and disadvantages. Copyright © 2014. Published by Elsevier B.V.

  16. Electrospun polyurethane membranes for Tissue Engineering applications

    Energy Technology Data Exchange (ETDEWEB)

    Gabriel, Laís P., E-mail: lagabriel@gmail.com [National Institute of Biofabrication, Campinas (Brazil); Department of Chemical Engineering, University of Campinas, Campinas (Brazil); Rodrigues, Ana Amélia [National Institute of Biofabrication, Campinas (Brazil); Department of Medical Sciences, University of Campinas, Campinas (Brazil); Macedo, Milton; Jardini, André L.; Maciel Filho, Rubens [National Institute of Biofabrication, Campinas (Brazil); Department of Chemical Engineering, University of Campinas, Campinas (Brazil)

    2017-03-01

    Tissue Engineering proposes, among other things, tissue regeneration using scaffolds integrated with biological molecules, growth factors or cells for such regeneration. In this research, polyurethane membranes were prepared using the electrospinning technique in order to obtain membranes to be applied in Tissue Engineering, such as epithelial, drug delivery or cardiac applications. The influence of fibers on the structure and morphology of the membranes was studied using scanning electron microscopy (SEM), the structure was evaluated by Fourier transform infrared spectroscopy (FT-IR), and the thermal stability was analyzed by thermogravimetry analysis (TGA). In vitro cells attachment and proliferation was investigated by SEM, and in vitro cell viability was studied by 3-(4,5-dimethyl-2-thiazolyl)-2,5-diphenyl-2H-tetrazolium bromide (MTT) assays and Live/Dead® assays. It was found that the membranes present an homogeneous morphology, high porosity, high surface area/volume ratio, it was also observed a random fiber network. The thermal analysis showed that the membrane degradation started at 254 °C. In vitro evaluation of fibroblasts cells showed that fibroblasts spread over the membrane surface after 24, 48 and 72 h of culture. This study supports the investigation of electrospun polyurethane membranes as biocompatible scaffolds for Tissue Engineering applications and provides some guidelines for improved biomaterials with desired properties.

  17. Preparation, Physicochemical Properties and Hemocompatibility of Biodegradable Chitooligosaccharide-Based Polyurethane

    Directory of Open Access Journals (Sweden)

    Weiwei Xu

    2018-05-01

    Full Text Available The purpose of this study was to develop a process to achieve biodegradable chitooligosaccharide-based polyurethane (CPU with improved hemocompatibility and mechanical properties. A series of CPUs with varying chitooligosaccharide (COS content were prepared according to the conventional two-step method. First, the prepolymer was synthesized from poly(ε-caprolactone (PCL and uniform-size diurethane diisocyanates (HBH. Then, the prepolymer was chain-extended by COS in N,N-dimethylformamide (DMF to obtain the weak-crosslinked CPU, and the corresponding films were obtained from the DMF solution by the solvent evaporation method. The uniform-size hard segments and slight crosslinking of CPU were beneficial for enhancing the mechanical properties, which were one of the essential requirements for long-term implant biomaterials. The chemical structure was characterized by FT-IR, and the influence of COS content in CPU on the physicochemical properties and hemocompatibility was extensively researched. The thermal stability studies indicated that the CPU films had lower initial decomposition temperature and higher maximum decomposition temperature than pure polyurethane (CPU-1.0 film. The ultimate stress, initial modulus, and surface hydrophilicity increased with the increment of COS content, while the strain at break and water absorption decreased, which was due to the increment of crosslinking density. The results of in vitro degradation signified that the degradation rate increased with the increasing content of COS in CPU, demonstrating that the degradation rate could be controlled by adjusting COS content. The surface hemocompatibility was examined by protein adsorption and platelet adhesion tests. It was found that the CPU films had improved resistance to protein adsorption and possessed good resistance to platelet adhesion. The slow degradation rate and good hemocompatibility of the CPUs showed great potential in blood-contacting devices. In

  18. Rapid hemostatic and mild polyurethane-urea foam wound dressing for promoting wound healing

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Xiangyu; Niu, Yuqing [College of Materials Science and Engineering, Shenzhen University, Shenzhen 518060 (China); Nanshan District Key lab for Biopolymers and Safety Evaluation, Shenzhen 518060 (China); Shenzhen Key Laboratory of Polymer Science and Technology, Shenzhen 518060 (China); Guangdong Research Center for Interfacial Engineering of Functional Materials, Shenzhen 518060 (China); Chen, Kevin C. [Multidisciplinary Research Center, Shantou University, Shantou, Guangdong 515063 (China); Chen, Shiguo, E-mail: csg@szu.edu.cn [College of Materials Science and Engineering, Shenzhen University, Shenzhen 518060 (China); Nanshan District Key lab for Biopolymers and Safety Evaluation, Shenzhen 518060 (China); Shenzhen Key Laboratory of Polymer Science and Technology, Shenzhen 518060 (China); Guangdong Research Center for Interfacial Engineering of Functional Materials, Shenzhen 518060 (China)

    2017-02-01

    A novel rapid hemostatic and mild polyurethane-urea foam (PUUF) wound dressing was prepared by the particle leaching method and vacuum freeze-drying method using 4, 4-Methylenebis(cyclohexyl isocyanate), 4,4-diaminodicyclohexylmethane and poly (ethylene glycol) as raw materials. And X-ray diffraction (XRD), tensile test, differential scanning calorimetry (DSC) and thermogravimetry (TG) were used to its crystallinity, stress and strain behavior, and thermal properties, respectively. Platelet adhesion, fibrinogen adhesion and blood clotting were performed to evaluate its hemostatic effect. And H&E staining and Masson Trichrome staining were used to its wound healing efficacy. The results revealed the pore size of PUUF is 50–130 μm, and its porosity is 71.01%. Porous PUUF exhibited good water uptake that was benefit to adsorb abundant wound exudates to build a regional moist environment beneficial for wound healing. The PUUF wound dressing exhibit better blood coagulation effect than commercial polyurethane dressing (CaduMedi). Though both PUUF and CaduMedi facilitated wound healing generating full re-epithelialization within 13 days, PUUF was milder and lead to more slight inflammatory response than CaduMedi. In addition, PUUF wound dressing exhibited lower cytotoxicity than CaduMedi against NIH3T3 cells. Overall, porous PUUF represents a novel mild wound dressing with excellent water uptake, hemostatic effect and low toxicity, and it can promote wound healing and enhance re-epithelialization. - Highlights: • Rapid hemostatic and mild PUUF wound dressing was fabricated. • Low-toxic PUUF exhibited good water uptake that could build a regional moist environment beneficial for wound healing. • PUUF could promote wound healing and enhance re-epithelialization.

  19. Hydroxyapatite-silver nanoparticles coatings on porous polyurethane scaffold

    International Nuclear Information System (INIS)

    Ciobanu, Gabriela; Ilisei, Simona; Luca, Constantin

    2014-01-01

    The present paper is focused on a study regarding the possibility of obtaining hydroxyapatite-silver nanoparticle coatings on porous polyurethane scaffold. The method applied is based on a combined strategy involving hydroxyapatite biomimetic deposition on polyurethane surface using a Supersaturated Calcification Solution (SCS), combined with silver ions reduction and in-situ crystallization processes on hydroxyapatite-polyurethane surface by sample immersing in AgNO 3 solution. The morphology, composition and phase structure of the prepared samples were characterized by scanning electron microscopy coupled with energy dispersive X-ray spectroscopy (SEM-EDX), X-ray diffraction (XRD), UV-Vis spectroscopy and X-ray photoelectron spectroscopy (XPS) measurements. The data obtained show that a layer of hydroxyapatite was deposited on porous polyurethane support and the silver nanoparticles (average size 34.71 nm) were dispersed among and even on the hydroxyapatite crystals. Hydroxyapatite/polyurethane surface acts as a reducer and a stabilizing agent for silver ions. The surface plasmon resonance peak in UV-Vis absorption spectra showed an absorption maximum at 415 nm, indicating formation of silver nanoparticles. The hydroxyapatite-silver polyurethane scaffolds were tested against Staphylococcus aureus and Escherichia coli and the obtained data were indicative of good antibacterial properties of the materials. - Highlights: • The hydroxyapatite and silver nanoparticles were grown on the polyurethane scaffold • The hydroxyapatite/polyurethane acts as reducing agent, stabilizer and matrix for Ag • The samples were well characterized by SEM-EDX, XRD, XPS, UV-visible spectroscopy • The hydroxyapatite/silver polyurethane scaffold shows antibacterial property

  20. Applicability of liquid radiopaque polyurethane for transcatheter embolization

    International Nuclear Information System (INIS)

    Novak, D.; Wieners, H.; Rueckner, R.

    1983-01-01

    Polyurethane Bayer was tested as an occlusive agent for experimental embolization in postmortem and postnephrectomy kidneys which served as a tumor model. Coaxial and balloon catheters were used for the embolization. To make polyurethane radiopaque, the material was labeled with different water-soluble, oily and solid contrast agents. Best results were achieved with oily contrast materials, e.g., Pantopaque. We found that polyurethane can easily be injected during a predetermined working time of 8-10 min. The embolization results in a complete, permanent, and homogeneous occlusion of the proximal arterial branches and small peripheral vessels. (orig.)

  1. Study of the morphology exhibited by linear segmented polyurethanes

    International Nuclear Information System (INIS)

    Pereira, I.M.; Orefice, R.L.

    2009-01-01

    Five series of segmented polyurethanes with different hard segment content were prepared by the prepolymer mixing method. The nano-morphology of the obtained polyurethanes and their microphase separation were investigated by infrared spectroscopy, modulated differential scanning calorimetry and small-angle X-ray scattering. Although highly hydrogen bonded hard segments were formed, high hard segment contents promoted phase mixture and decreased the chain mobility, decreasing the hard segment domain precipitation and the soft segments crystallization. The applied techniques were able to show that the hard-segment content and the hard-segment interactions were the two controlling factors for determining the structure of segmented polyurethanes. (author)

  2. Particle adhesion and removal

    CERN Document Server

    Mittal, K L

    2015-01-01

    The book provides a comprehensive and easily accessible reference source covering all important aspects of particle adhesion and removal.  The core objective is to cover both fundamental and applied aspects of particle adhesion and removal with emphasis on recent developments.  Among the topics to be covered include: 1. Fundamentals of surface forces in particle adhesion and removal.2. Mechanisms of particle adhesion and removal.3. Experimental methods (e.g. AFM, SFA,SFM,IFM, etc.) to understand  particle-particle and particle-substrate interactions.4. Mechanics of adhesion of micro- and  n

  3. Synthesis and Thermomechanical Properties of Polyurethanes and Biocomposites Derived from Macauba Oil and Coconut Husk Fibers

    Directory of Open Access Journals (Sweden)

    Rafael L. Quirino

    2015-08-01

    Full Text Available This work reports on a very effective route to produce bio-based polyurethanes (PUs and composites with high content of renewable carbon sources. The PUs are prepared with polyols synthesized from macauba oil (Acrocomia aculeata and methylene diphenyl diisocyanate, at different [NCO]/[OH] molar ratios. Later, biocomposites are prepared with the as-obtained PUs reinforced with coconut husk fibers. The successful synthesis of natural oil-based polyols is ascribed to the hydroxylation and consumption of carbon-carbon double bonds in the fatty acid chains of the original starting oil as attested by FTIR spectroscopy. According to different thermal analysis techniques (TG, DTG, and DTA, the increase in the [NCO]/[OH] molar ratio improves the thermal stability of PUs, likely due to an increase of crosslinks. Dynamic mechanical analysis evidences the reinforcement effect of coconut husk fibers in bio-based PUs. The present PUs and composites are of low-cost and environmentally friendly materials for structural applications.

  4. Bio-Based Polyols from Seed Oils for Water-Blown Rigid Polyurethane Foam Preparation

    Directory of Open Access Journals (Sweden)

    Paweena Ekkaphan

    2016-01-01

    Full Text Available The preparation of water-blown rigid polyurethane (RPUR foams using bio-based polyols from sesame seed oil and pumpkin seed oil has been reported. Polyols synthesis involved two steps, namely, hydroxylation and alcoholysis reaction. FTIR, NMR, and ESI-MS were used to monitor the process of the synthesized polyols and their physicochemical properties were determined. The resulting polyols have OH number in the range of 340–351 mg KOH/g. RPUR foams blown with water were produced from the reaction of biopolyols with commercial polymeric methylene diphenyl diisocyanate (PMDI. The proper PUR formulations can be manipulated to produce the desired material applications. These seed oil-based RPUR foams exhibited relatively high compressive strength (237.7–240.2 kPa with the density in the range of 40–45 kg/m3. Additionally, the cell foam morphology investigated by scanning electron microscope indicated that their cellular structure presented mostly polygonal closed cells. The experimental results demonstrate that these bio-based polyols can be used as an alternative starting material for RPUR production.

  5. Study of physical and tribology properties of soybean oil-based grease formulated with polysoap

    Science.gov (United States)

    Soybean oil-based grease formulated with polysoaps, which was synthesized from polymeric epoxdized soybean oil, was investigated. Greases were prepared using a mixture of lithium soap and triethanolammonium polysoap. Grease properties investigated were: hardness, using cone penetration procedure (AS...

  6. Gamma-ray irradiation, autoclave and ethylene oxide sterilization to thermosetting polyurethane: sterilization to polyurethane

    International Nuclear Information System (INIS)

    Hirata, Noriko; Matsumoto, Ken-Ichi; Inishita, Takashi; Takenaka, Yoshinori; Suma, Yasunori; Shintani, Hideharu; National Inst. of Health Sciences, Tokyo

    1995-01-01

    Thermosetting polyurethane (PU) is widely used in a large variety of medical devices. 4,4'-methylenedianiline (MDA) was produced from PU by sterilization and it was studied for the relationship between urethane components or polymer characteristics and formation of MDA upon sterilization, using the commercially available dialyzers fabricated with different combination of isocyanate and polyol. We confirmed that the molecular-weight of polyol influenced the production of MDA upon sterilization. (author)

  7. Biological and Clinical Aspects of an Olive Oil-Based Lipid Emulsion—A Review

    Directory of Open Access Journals (Sweden)

    Wei Cai

    2018-06-01

    Full Text Available Intravenous lipid emulsions (ILEs have been an integral component of parenteral nutrition for more than 50 years. Numerous formulations are available and are based on vegetable (soybean, olive, coconut and animal (fish oils. Therefore, each of these formulations has a unique fatty acid composition that offers both benefits and limitations. As clinical experience and our understanding of the effects of fatty acids on various physiological processes has grown, there is evidence to suggest that some ILEs may have benefits compared with others. Current evidence suggests that olive oil-based ILE may preserve immune, hepatobiliary, and endothelial cell function, and may reduce lipid peroxidation and plasma lipid levels. There is good evidence from a large randomized controlled study to support a benefit of olive oil-based ILE over soybean oil-based ILE on reducing infections in critically ill patients. At present there is limited evidence to demonstrate a benefit of olive oil-based ILE over other ILEs on glucose metabolism, and few data exist to demonstrate a benefit on clinical outcomes such as hospital or intensive care unit stay, duration of mechanical ventilation, or mortality. We review the current research and clinical evidence supporting the potential positive biological and clinical aspects of olive oil-based ILE and conclude that olive oil-based ILE is well tolerated and provides effective nutritional support to various PN-requiring patient populations. Olive oil-based ILE appears to support the innate immune system, is associated with fewer infections, induces less lipid peroxidation, and is not associated with increased hepatobiliary or lipid disturbances. These data would suggest that olive oil-based ILE is a valuable option in various PN-requiring patient populations.

  8. Thermal insulating materials consisting of polyurethane rigid foam. Production - application - properties. 2. ed.; Waermedaemmstoffe aus Polyurethan-Hartschaum. Herstellung - Anwendung - Eigenschaften

    Energy Technology Data Exchange (ETDEWEB)

    Endres, Edmund; Kleser, Joachim

    2008-02-15

    Using rigid polyurethane (PU) / polyisocyanurate (PIR) foam as a thermal insulation material enables a conservation of resources and energy conservation. Environmentally harmful emissions significantly are reduced. Under this aspect, the authors of the contribution report on the production, application, technical and physical properties of rigid polyurethane foams. Sustainable construction with rigid polyurethane foam, quality assurance and product certification are further topics of this paper.

  9. The effect of radiosterilization on surface properties of polyurethane film

    International Nuclear Information System (INIS)

    Sheikh, N.

    2003-01-01

    In this paper the effect of sterilization method by gamma-ray on structure and cytotoxicity of polyurethane film surface has been investigated. For this purpose reactive urethan prepolymer was synthesized by the reaction between Tdi with a mixture of Peg and castro oil (50/50, w/w). The cured prepolymer films were prepared due to the reaction of reactive prepolymer with air moister under ambient conditions. The polyurethane films were sterilized by gamma-ray (25 kGy). The surface of sterilized polyurethane film was observed by Sem and compared to that of the unsterilized film. Also, the in vitro interaction of fibroblast L 929 cells and sterilized polyurethane film was evaluated. Results showed no signs of cell toxicity

  10. The effect of radiosterilization on cytotoxicity of polyurethane film

    International Nuclear Information System (INIS)

    Sheikh, N.

    2003-01-01

    Nowadays a sequence of tests for evaluation of sterilized biomaterial includes an initial set of tests in vitro, both biological (cell culture) and non-biological (mechanical tests). In this paper the cytotoxicity of a sterilized polyurethane film, in order to use as biomaterial, has been investigated. For this purpose NCO-terminated urethane prepolymer in medical quality was synthesized without ingredients beside monomers (polyethylene glycol/castor oil and toluene diisocyanate). The cured prepolymer films were prepared under ambient conditions due to the reaction of free NCO-groups of prepolymer with air moisture. The polyurethane films were sterilized by gamma-ray (25 kGy). The surface structure of sterilized polyurethane film was observed by SEM and compared to that of the unsterilized film. Also, the in vitro interaction of fibroblast cells and sterilized polyurethane film in culture medium containing serum was evaluated in comparison with control samples. Results showed no signs of cell toxicity

  11. Characterization of synthesized polyurethane/montmorillonite nanocomposites foams

    International Nuclear Information System (INIS)

    Ansari, Farahnaz; Njuguna, James; Sachse, Sophia; Kavosh, Masoud; Michalowski, S; Pielichowski, Krzysztof

    2014-01-01

    Nanophased hybrid composites based on polyurethane/montmorillonite (PU/MMT) have been fabricated. The nanocomposite which was formed by the addition of a polyol premix with 4,4'-diphenylmethane diisocyanate to obtain nanophased polyurethane foams which were then used for fabrication of nanocomposite panels has been shown to have raised strength, stiffness and thermal insulation properties. The nanophased polyurethane foam was characterized by means of scanning electron microscope (SEM), transmission electron microscope (TEM) measurements and X-ray diffraction (XRD). TEM and SEM analysis indicated that nanophased particles are dispersed homogeneously in the polyurethane matrix on the nanometer scale indicating that PU/MMT is an intercalated nanocomposite with a 2-3 nm nanolayer thickness

  12. Polyurethane foam for roadway stabilization NH route 129, Loudon, NH.

    Science.gov (United States)

    2016-12-12

    This report summarizes the evaluation of the performance of polyurethane foam as a method of roadway : stabilization for a rural roadway experiencing substantial frost heaving. : NHDOT is responsible for many roads which have evolved from gravel road...

  13. Surface coated polyurethane with improved bioactivity and cytocompatability

    CSIR Research Space (South Africa)

    Chetty, AS

    2006-02-01

    Full Text Available Polyurethane (PU) may be suitable for various implant applications; however, it lacks bioactivity. Bioactivity allows for direct tissue attachment at the bio- interface, enabling implant fixation while preventing fibrous encapsulation. To impart...

  14. Nano-engineered polyurethane resin-modified concrete.

    Science.gov (United States)

    2014-04-01

    The goal of the proposed work is to investigate the application of nano-engineered polyurethane (NEPU) emulsions for latex modified : concrete (LMC). NEPU emulsions are non-toxic, environment friendly, durable over a wide temperature range, provide b...

  15. Soy-based UV resistant polyurethane pultruded composites.

    Science.gov (United States)

    2012-02-01

    Aliphatic polyurethane (PU) nanocomposites were synthesized using organically modified nanoclays. X-Ray diffraction results : confirmed good exfoliation of nanoclay particles in the PU resin system. With the addition of just 1% of nanoclay in the bas...

  16. Influence of polyols on properties of bio-based polyurethanes

    Indian Academy of Sciences (India)

    resources for the preparation of polyols required for the polyurethane industry. Among the vegetable oils, cardanol a meta-substituted phenol obtained (Kumar et al 2002) from ... High ortho-multinuclear cardanol–formaldehyde resin was.

  17. Experimental Investigation of Polyurethane Camouflage Coating Using Dynamic Mechanical Analysis

    National Research Council Canada - National Science Library

    Crawford, Dawn

    1999-01-01

    .... The current polyurethane solvent-based (SOL) formulation, used as a chemical-agent-resistant camouflage top coat on all military tactical vehicles, was investigated, along with newly developed water-reducible (WR...

  18. Fast-Responding Bio-Based Shape Memory Thermoplastic Polyurethanes.

    Science.gov (United States)

    Petrović, Zoran S; Milić, Jelena; Zhang, Fan; Ilavsky, Jan

    2017-07-14

    Novel fast response shape-memory polyurethanes were prepared from bio-based polyols, diphenyl methane diisocyanate and butane diol for the first time. The bio-based polyester polyols were synthesized from 9-hydroxynonanoic acid, a product obtained by ozonolysis of fatty acids extracted from soy oil and castor oil. The morphology of polyurethanes was investigated by synchrotron ultra-small angle X-ray scattering, which revealed the inter-domain spacing between the hard and soft phases, the degree of phase separation, and the level of intermixing between the hard and soft phases. We also conducted thorough investigations of the thermal, mechanical, and dielectric properties of the polyurethanes, and found that high crystallization rate of the soft segment gives these polyurethanes unique properties suitable for shape-memory applications, such as adjustable transition temperatures, high degree of elastic elongations, and good mechanical strength. These materials are also potentially biodegradable and biocompatible, therefore suitable for biomedical and environmental applications.

  19. Thermoplastic polyurethane and multi-walled carbon nanotubes nanocomposites for electrostatic dissipation; Nanocompositos de poliuretana termoplastica e nanotubos de carbono de paredes multiplas para dissipacao eletrostatica

    Energy Technology Data Exchange (ETDEWEB)

    Lavall, Rodrigo L; Sales, Juliana A. de; Borges, Raquel S; Calado, Hallen D. R.; Machado, Jose C; Windmoeller, Dario; Silva, Glaura G [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte, MG (Brazil). Inst. de Ciencias Exatas. Dept. de Quimica; Lacerda, Rodrigo G; Ladeira, Luiz O [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte, MG (Brazil). Inst. de Ciencias Exatas. Dept. de Fisica

    2010-07-01

    Polyurethane/multi-walled carbon nanotube (MWCNT) nanocomposites have been prepared with nanotube concentrations between 0.01 wt% and 1 wt%. MWCNT as-synthesized samples with {approx}74 nm diameter and {approx}7 mm length were introduced by solution processing in the polyurethane matrix. Scanning electron microscopy (SEM) images demonstrated good dispersion and adhesion of the CNTs to the polymeric matrix. The C=O stretching band showed evidence of perturbation of the hydrogen interaction between urethanic moieties in the nanocomposites as compared to pure TPU. Differential scanning calorimetry and positron annihilation lifetime spectroscopy measurements allowed the detection of glass transition displacement with carbon nanotube addition. Furthermore, the electrical conductivity of the nanocomposites was significantly increased with the addition of CNT. (author)

  20. STUDY ON MOISTURE-CUR ED POLYURETHANE AS UNDERCOATING LAYER FOR METALLIZATION

    Directory of Open Access Journals (Sweden)

    M.N. Mohamad Ibrahim

    2017-11-01

    Full Text Available In this work a technique of metallizing substrate via electroless plating using moisture-cured polyurethane (MCPU system as the undercoat is presented. MCPU prepolymer was prepared by mixing polyethylene glycol divinyl ether and diphenylmethane-4, 4’-diisocyanate in 1:1 ratio. The effects of etching time as well as curing period on the surface characteristic of MCPU undercoating were investigated. Contact angle measurements, FTIR and SEM were employed to study the changes on the surface of the treated MCPU undercoatsprior to electroless nickel plating. Electroless plating was performed using nickel bath and visual inspection was performed after completing the electroless plating cycles. Relative increase in wettability of the treated MCPU was observed. The surface became hydrophilic after subjecting to mild etching for 1 minute. SEM analysis revealed different pitted structures on the treated MCPU that were cured at different periods. FTIR analysis of the treated MCPU showed some chemical changes marked by the presence of free hydroxyl group and decrease of CH (methylene, urethane C=O, urethane amide and ether peaks. FTIR also showed the sign of further NCO reaction, which indicates by the decrease of NCO peak and increase of NH and urea C=O peaks. The standard pull-off testing method (ASTM D 4541 was employed to evaluate the adhesion strength of nickel deposits coated on MCPU undercoating layer.The test results revealed that curing period and etching time influence the adhesion performance.The results also show that at a selected curing period, prolong etching time will decrease the adhesion strength. Meanwhile prolong curing period will improve the adhesion strength.

  1. Multifunctional composite material based on carbon-filled polyurethane

    International Nuclear Information System (INIS)

    Malinovskaya, T; Melentyev, S; Pavlov, S

    2015-01-01

    The research paper deals with the performance of composite resistive material heating coatings based on the polyurethane binder, filled with colloidal-graphite preparation C- 1, which can be used in structures of electric heaters. Frequency dependences of transmission and reflection coefficients, dielectric permeability of composite materials with the various content of carbon fillers (technical carbon, graphite) in polyurethane varnish in ranges of frequencies 26-40 GHz and 110-260 GHz are experimentally investigated. (paper)

  2. Antimicrobial polyurethane thermosets based on undecylenic acid: synthesis and evaluation

    OpenAIRE

    Cádiz, V.; Galià, M.; Ronda, J.C.; Lligadas, G.; Bordons, A.; Esteve-Zarzoso, B.; Lluch, C.

    2014-01-01

    10.1002/mabi.201400017 In the present study, plant oil-derived surface-modifiable polyurethane thermosets are presented. Polyol synthesis is carried out taking advantage of thiol-yne photopolymerization of undecylenic acid derivatives containing methyl ester or hydroxyl moieties. The prepared methyl ester-containing polyurethanes allow surface modification treatment to enhance their hydrophilicity and impart antimicrobial activity through the following two steps: i) grafting poly(propylen...

  3. Polyurethane Coatings Reinforced by Halloysite Nanotubes

    Directory of Open Access Journals (Sweden)

    Diethelm Johannsmann

    2013-01-01

    Full Text Available The pencil hardness of a two-component polyurethane coating was improved by adding halloysite nanotubes to the recipe at a weight fraction of less than 10%. The pencil hardness was around F for the unfilled coating and increased to around 2H upon filling. It was important to silanize the surface of the filler in order to achieve good coupling to the matrix. Sonicating the sample during drying also improved the hardness. Scanning electron micrographs suggest that the nanotubes are always well immersed into the bulk of the film. With a thickness between 10 and 20 µm, the optical clarity was good enough to clearly read letters through the film. The films can be used in applications where transparency is required.

  4. Degradation characteristics of waste polyurethane by radiation

    Energy Technology Data Exchange (ETDEWEB)

    Park, Jong Seok; Ahn, Sung Jun; Gwon Hui Jeong; Jeong, Sung In; Nho, Young Chang; Lim, Youn Mook [Research Division for Industry and Environment, Korea Atomic Energy Research Institute, Jeongeup (Korea, Republic of)

    2017-06-15

    Polyurethane (PU) is a very popular polymer that is used in a variety of applications due to its good mechanical, thermal, and chemical properties. However, waste PU recycling has received significant attention due to environmental issues. The aim of this work was to investigate the degradation characteristics of waste PU to recycle. Degradation of waste PU was carried out using a radiation techniques. Waste PUs were exposed to a gamma {sup 60}Co sources. To verify degradation, the irradiated PUs were characterized using FT-IR, gel permeation chromatography (GPC), and their thermal/mechanical properties are reported. When the radiation dose was 500 kGy, the molecular weight of the waste PU drastically decreased. Also, the mechanical properties of waste PU were approximately 4 times lower than those of non-irradiated PU. This study has confirmed the possibility of making fine particle of waste PU for recycling through radiation degradation techniques.

  5. Polyurethane elastomers from morphology to mechanical aspects

    CERN Document Server

    Prisacariu, Cristina

    2011-01-01

    A comprehensive account of the physical / mechanical behaviour of polyurethanes (PU´s) elastomers, films and blends of variable crystallinity. Aspects covered include the elasticity and inelasticity of amorphous to crystalline PUs, in relation to their sensitivity to chemical and physical structure. A study is made of how aspects of the constitutive responses of PUs vary with composition: the polyaddition procedure, the hard segment, soft segment and chain extender (diols and diamines) are varied systematically in a large number of systems of model and novel crosslinked andthermoplastic PUs. Results will be related to: microstructural changes, on the basis of evidence from x-ray scattering (SAXS and WAXS), and also dynamic mechanical analyses (DMA), differential scanning calorimetry (DSC) and IR dichroism. Inelastic effects will be investigated also by including quantitative correlations between the magnitude of the Mullins effect and the fractional energy dissipation by hysteresis under cyclic straining, g...

  6. Biodegradation of polyurethane derived from castor oil

    Directory of Open Access Journals (Sweden)

    José M. Cangemi

    2008-09-01

    Full Text Available The aim of this research was to study the biodegradation of a polymer derived from castor oil, which is a renewable, natural material that is a practical alternative for the replacement of traditional polyurethane foams. Due to its molecular structure, which contains polyester segments derived from vegetable oil, the polymeric surface is susceptible to microorganism attack. This study tested the biological degrading agent that was in contact with the microorganisms resulting from microbiological grease degrading agents, when foam was inoculated. Solid-media agar-plate tests were conducted for their potential to evaluate the biodegradation of polymeric particles by specific strains of microorganisms during 216 hours. The growth rate was defined. This technique provides a way of distinguishing the degradation abilities of microorganisms from the degradability of materials.

  7. Engineering Performance of Polyurethane Bonded Aggregates

    Directory of Open Access Journals (Sweden)

    Haimin WU

    2017-08-01

    Full Text Available In this paper the engineering performance of polyurethane (PUR bonded aggregate were studied. The engineering performance, including compressive and flexural mechanical properties, void ratio, and coefficient of permeability were determined through laboratory tests. Moreover, the effects of two different curing conditions on the compressive strength properties of a PUR bonded aggregate were also evaluated. The compressive strengths of PUR bonded aggregates were found to be lower than that of conventional porous concrete, which is a commonly used cushion material. However, experimental results indicated a higher void ratio and coefficient of permeability, lower elasticity modulus, better toughness, and stronger adaptability to flexural deformation compared to porous concrete. Consequently, PUR bonded aggregate is a better solution than porous concrete when used as the cushion material of a geomembrane surface barrier for a high rock-fill dam.DOI: http://dx.doi.org/10.5755/j01.ms.23.2.15798

  8. The effects of nitric oxide in settlement and adhesion of zoospores of the green alga Ulva.

    Science.gov (United States)

    Thompson, Stephanie E M; Callow, Maureen E; Callow, James A

    2010-01-01

    Previous studies have shown that elevated nitric oxide (NO) reduces adhesion in diatom, bacterial and animal cells. This article reports experiments designed to investigate whether elevated NO reduces the adhesion of zoospores of the green alga Ulva, an important fouling species. Surface-normalised values of NO were measured using the fluorescent indicator DAF-FM DA and parallel hydrodynamic measurements of adhesion strength were made. Elevated levels of NO caused by the addition of the exogenous NO donor SNAP reduced spore settlement by 20% and resulted in lower adhesion strength. Addition of the NO scavenger cPTIO abolished the effects of SNAP on adhesion. The strength of attachment and NO production by spores in response to four coatings (Silastic T2; Intersleek 700; Intersleek 900 and polyurethane) shows that reduced adhesion is correlated with an increase in NO production. It is proposed that in spores of Ulva, NO is used as an intracellular signalling molecule to detect how conducive a surface is for settlement and adhesion. The effect of NO on the adhesion of a range of organisms suggests that NO-releasing coatings could have the potential to control fouling.

  9. Preparation and Characterization of Fluorinated Hydrophobic UV-Crosslinkable Thiol-Ene Polyurethane Coatings

    Directory of Open Access Journals (Sweden)

    Wenjing Xia

    2017-08-01

    Full Text Available The polyurethane prepolymer terminated with a double bond was synthesized using isophorone diisocyanate (IPDI, hydroxyl terminated polybutadiene (HTPB, 1,4-butanediol (BDO, and 2-hydroxyethyl acrylate (HEA. Then, a series of innovative UV-curable polyurethane coatings were prepared by blending ene-terminated polyurethane, fluoroacrylate monomer, and multifunctional thiol crosslinker upon UV exposure. The incorporation of fluoroacrylate monomer and multifunctional thiols into polyurethane coatings significantly enhanced the hydrophobic property, mechanical property, pencil hardness, and glossiness of the polyurethane coatings. This method of preparing UV crosslinkable, hydrophobic polyurethane coatings based on thiol-ene chemistry exhibited numerous advantages over other UV photocuring systems.

  10. Hydroxyapatite-silver nanoparticles coatings on porous polyurethane scaffold.

    Science.gov (United States)

    Ciobanu, Gabriela; Ilisei, Simona; Luca, Constantin

    2014-02-01

    The present paper is focused on a study regarding the possibility of obtaining hydroxyapatite-silver nanoparticle coatings on porous polyurethane scaffold. The method applied is based on a combined strategy involving hydroxyapatite biomimetic deposition on polyurethane surface using a Supersaturated Calcification Solution (SCS), combined with silver ions reduction and in-situ crystallization processes on hydroxyapatite-polyurethane surface by sample immersing in AgNO3 solution. The morphology, composition and phase structure of the prepared samples were characterized by scanning electron microscopy coupled with energy dispersive X-ray spectroscopy (SEM-EDX), X-ray diffraction (XRD), UV-Vis spectroscopy and X-ray photoelectron spectroscopy (XPS) measurements. The data obtained show that a layer of hydroxyapatite was deposited on porous polyurethane support and the silver nanoparticles (average size 34.71 nm) were dispersed among and even on the hydroxyapatite crystals. Hydroxyapatite/polyurethane surface acts as a reducer and a stabilizing agent for silver ions. The surface plasmon resonance peak in UV-Vis absorption spectra showed an absorption maximum at 415 nm, indicating formation of silver nanoparticles. The hydroxyapatite-silver polyurethane scaffolds were tested against Staphylococcus aureus and Escherichia coli and the obtained data were indicative of good antibacterial properties of the materials. © 2013.

  11. Energetics of bacterial adhesion

    International Nuclear Information System (INIS)

    Loosdrecht, M.C.M. van; Zehnder, A.J.B.

    1990-01-01

    For the description of bacterial adhesion phenomena two different physico-chemical approaches are available. The first one, based on a surface Gibbs energy balance, assumes intimate contact between the interacting surfaces. The second approach, based on colloid chemical theories (DLVO theory), allows for two types of adhesion: 1) secondary minimum adhesion, which is often weak and reversible, and 2) irreversible primary minimum adhesion. In the secondary minimum adhesion a thin water film remains present between the interacting surface. The merits of both approaches are discussed in this paper. In addition, the methods available to measure the physico-chemical surface characteristics of bacteria and the influence of adsorbing (in)organic compounds, extracellular polymers and cell surface appendages on adhesion are summarized. (author) 2 figs., 1 tab., 50 refs

  12. Radiation-curable adhesives

    International Nuclear Information System (INIS)

    Woods, J.G.

    1992-01-01

    Radiation-curable adhesives may be classified into two broad categories. In the first category, adhesive bonding occurs as a direct result of irradiation. The second category includes pressure-sensitive and hot-melt adhesives, which are composed of linear or lightly cross-linked polymers prepared by a radiation-induced polymerization reaction. This chapter is mainly concerned with radiation-curable adhesives of the first category. The various adhesive types are discussed and adhesive performance is examined, particularly in relation to the chemistry and chemical technology which underlies the individual materials. A description of a limited number of representative applications is included as is an outline of recent developments of curing and dispensing equipment. 268 refs., 14 figs., 13 tabs

  13. The adhesive strength and initial viscosity of denture adhesives.

    Science.gov (United States)

    Han, Jian-Min; Hong, Guang; Dilinuer, Maimaitishawuti; Lin, Hong; Zheng, Gang; Wang, Xin-Zhi; Sasaki, Keiichi

    2014-11-01

    To examine the initial viscosity and adhesive strength of modern denture adhesives in vitro. Three cream-type denture adhesives (Poligrip S, Corect Cream, Liodent Cream; PGS, CRC, LDC) and three powder-type denture adhesives (Poligrip Powder, New Faston, Zanfton; PGP, FSN, ZFN) were used in this study. The initial viscosity was measured using a controlled-stress rheometer. The adhesive strength was measured according to ISO-10873 recommended procedures. All data were analyzed independently by one-way analysis of variance combined with a Student-Newman-Keuls multiple comparison test at a 5% level of significance. The initial viscosity of all the cream-type denture adhesives was lower than the powder-type adhesives. Before immersion in water, all the powder-type adhesives exhibited higher adhesive strength than the cream-type adhesives. However, the adhesive strength of cream-type denture adhesives increased significantly and exceeded the powder-type denture adhesives after immersion in water. For powder-type adhesives, the adhesive strength significantly decreased after immersion in water for 60 min, while the adhesive strength of the cream-type adhesives significantly decreased after immersion in water for 180 min. Cream-type denture adhesives have lower initial viscosity and higher adhesive strength than powder type adhesives, which may offer better manipulation properties and greater efficacy during application.

  14. Synaptic Cell Adhesion

    OpenAIRE

    Missler, Markus; Südhof, Thomas C.; Biederer, Thomas

    2012-01-01

    Chemical synapses are asymmetric intercellular junctions that mediate synaptic transmission. Synaptic junctions are organized by trans-synaptic cell adhesion molecules bridging the synaptic cleft. Synaptic cell adhesion molecules not only connect pre- and postsynaptic compartments, but also mediate trans-synaptic recognition and signaling processes that are essential for the establishment, specification, and plasticity of synapses. A growing number of synaptic cell adhesion molecules that inc...

  15. Reversible Thermoset Adhesives

    Science.gov (United States)

    Mac Murray, Benjamin C. (Inventor); Tong, Tat H. (Inventor); Hreha, Richard D. (Inventor)

    2016-01-01

    Embodiments of a reversible thermoset adhesive formed by incorporating thermally-reversible cross-linking units and a method for making the reversible thermoset adhesive are provided. One approach to formulating reversible thermoset adhesives includes incorporating dienes, such as furans, and dienophiles, such as maleimides, into a polymer network as reversible covalent cross-links using Diels Alder cross-link formation between the diene and dienophile. The chemical components may be selected based on their compatibility with adhesive chemistry as well as their ability to undergo controlled, reversible cross-linking chemistry.

  16. Effect of Hyaluronic Acid Incorporation Method on the Stability and Biological Properties of Polyurethane-Hyaluronic Acid Biomaterials

    Science.gov (United States)

    Ruiz, Amaliris; Rathnam, Kashmila R.; Masters, Kristyn S.

    2014-01-01

    The high failure rate of small diameter vascular grafts continues to drive the development of new materials and modification strategies that address this clinical problem, with biomolecule incorporation typically achieved via surface-based modification of various biomaterials. In this work, we examined whether the method of biomolecule incorporation (i.e., bulk vs. surface modification) into a polyurethane (PU) polymer impacted biomaterial performance in the context of vascular applications. Specifically, hyaluronic acid (HA) was incorporated into a poly(ether urethane) via bulk copolymerization or covalent surface tethering, and the resulting PU-HA materials characterized with respect to both physical and biological properties. Modification of PU with HA by either surface or bulk methods yielded materials that, when tested under static conditions, possessed no significant differences in their ability to resist protein adsorption, platelet adhesion, and bacterial adhesion, while supporting endothelial cell culture. However, only bulk-modified PU-HA materials were able to fully retain these characteristics following material exposure to flow, demonstrating a superior ability to retain the incorporated HA and minimize enzymatic degradation, protein adsorption, platelet adhesion, and bacterial adhesion. Thus, despite bulk methods rarely being implemented in the context of biomolecule attachment, these results demonstrate improved performance of PU-HA upon bulk, rather than surface, incorporation of HA. Although explored only in the context of PU-HA, the findings revealed by these experiments have broader implications for the design and evaluation of vascular graft modification strategies. PMID:24276670

  17. Polyethyleneimine brushes effectively inhibit encrustation on polyurethane ureteral stents both in dynamic bioreactor and in vivo

    Energy Technology Data Exchange (ETDEWEB)

    Gultekinoglu, Merve [Department of Basic Pharmaceutical Sciences, Faculty of Pharmacy, Hacettepe University, Ankara 06100 (Turkey); Bioengineering Division, Institute for Graduate Studies in Science and Engineering, Hacettepe University, Ankara 06532 (Turkey); Kurum, Barış [Department of Surgery, Faculty of Veterinary Medicine, Kırıkkale University, Kırıkkale 71450 (Turkey); Karahan, Siyami [Department of Histology and Embryology, Faculty of Veterinary Medicine, Kırıkkale University, Kırıkkale 71450 (Turkey); Kart, Didem; Sagiroglu, Meral [Department of Pharmaceutical Microbiology, Faculty of Pharmacy, Hacettepe University, Ankara 06100 (Turkey); Ertaş, Nusret [Department of Analytical Chemistry, Faculty of Pharmacy, Gazi University, Ankara 06330 (Turkey); Haluk Ozen, A. [Department of Urology, Faculty of Medicine, Hacettepe University, Ankara 06100 (Turkey); Ulubayram, Kezban, E-mail: ukezban@hacettepe.edu.tr [Department of Basic Pharmaceutical Sciences, Faculty of Pharmacy, Hacettepe University, Ankara 06100 (Turkey); Bioengineering Division, Institute for Graduate Studies in Science and Engineering, Hacettepe University, Ankara 06532 (Turkey)

    2017-02-01

    Polyurethane (PU) ureteral stents have been widely used as biomedical devices to aid the flow of the urine. Due to the biofilm formation and encrustation complications it has been hindered their long term clinical usage. To overcome these complications, in this study, cationic polyethyleneimine (PEI) brushes grafted on PU stents and their performances were tested both in a dynamic biofilm reactor system (in vitro) and in a rat model (in vivo). Thus, we hypothesized that PEI brushes inhibit bacterial adhesion owing to the dynamic motion of brushes in liquid environment. In addition, cationic structure of PEI disrupts the membrane and so kills the bacteria on time of contact. Cationic PEI brushes decreased the biofilm formation up to 2 orders of magnitude and approximately 50% of encrustation amount in respect to unmodified PU, in vitro. In addition, according to Atomic Absorption Spectroscopy (AAS) results, approximately 90% of encrustation was inhibited on in vivo animal models. Decrease in encrustation was clearly observed on the stents obtained from rat model, by Scanning Electron Microscopy (SEM). Also, histological evaluations showed that; PEI brush grafting decreased host tissue inflammation in close relation to decrease in biofilm formation and encrustation. As a results; dual effect of anti-adhesive and contact-killing antibacterial strategy showed high efficiency on PEI brushes grafted PU stents both in vitro and in vivo.

  18. Polyethyleneimine brushes effectively inhibit encrustation on polyurethane ureteral stents both in dynamic bioreactor and in vivo

    International Nuclear Information System (INIS)

    Gultekinoglu, Merve; Kurum, Barış; Karahan, Siyami; Kart, Didem; Sagiroglu, Meral; Ertaş, Nusret; Haluk Ozen, A.; Ulubayram, Kezban

    2017-01-01

    Polyurethane (PU) ureteral stents have been widely used as biomedical devices to aid the flow of the urine. Due to the biofilm formation and encrustation complications it has been hindered their long term clinical usage. To overcome these complications, in this study, cationic polyethyleneimine (PEI) brushes grafted on PU stents and their performances were tested both in a dynamic biofilm reactor system (in vitro) and in a rat model (in vivo). Thus, we hypothesized that PEI brushes inhibit bacterial adhesion owing to the dynamic motion of brushes in liquid environment. In addition, cationic structure of PEI disrupts the membrane and so kills the bacteria on time of contact. Cationic PEI brushes decreased the biofilm formation up to 2 orders of magnitude and approximately 50% of encrustation amount in respect to unmodified PU, in vitro. In addition, according to Atomic Absorption Spectroscopy (AAS) results, approximately 90% of encrustation was inhibited on in vivo animal models. Decrease in encrustation was clearly observed on the stents obtained from rat model, by Scanning Electron Microscopy (SEM). Also, histological evaluations showed that; PEI brush grafting decreased host tissue inflammation in close relation to decrease in biofilm formation and encrustation. As a results; dual effect of anti-adhesive and contact-killing antibacterial strategy showed high efficiency on PEI brushes grafted PU stents both in vitro and in vivo.

  19. Preparation and antifouling property of polyurethane film modified by chondroitin sulfate

    Science.gov (United States)

    Yuan, Huihui; Xue, Jing; Qian, Bin; Chen, Huaying; Zhu, Yonggang; Lan, Minbo

    2017-02-01

    An antifouling polyurethane film modified by chondroitin sulfate (PU-CS) was prepared by chemical grafting with N-Boc-1,3-propanediamine as a spacer. The different mass fraction of N-Boc-1,3-propanediamine was investigated to obtain PU-CS films with different CS grafting density. The surface properties of PU-CS films were comprehensively characterized. Proteins adsorption and glycosaminoglycans adhesion on films were evaluated. Moreover, inorganic salt deposition on film with highest CS grafting density (3.70 μg/cm2) was briefly investigated. The results showed that the increase of CS grafting density improved not only the hydrophilicity but the antifouling performance of films. The best antifouling film reduced the adsorption of fibrinogen (BFG), human serum albumin (HSA) and lysozyme (LYS) by 81.4%, 95.0% and 76.5%, respectively, and the adhesion of chondroitin (CS), heparin (HP) and hyaluronic acid (HA) by 70.6%, 87.4% and 81.3%, respectively. In addition, the co-adsorption of proteins and glycosaminoglycans reduced up to 86.9% and 75.5%, respectively. Changes in inorganic salt deposition after co-adsorption of proteins and glycosaminoglycans on PU-CS(3) suggested that the proteins promoted the inorganic salt deposition, while glycosaminoglycans inhibited the crystal growth. The negatively charged polysaccharides might promote the generation of smaller crystals which could be conducive to provide theoretical and practical guide to develop novel urinary stents with significant anti-encrustation properties.

  20. Radiation-resistance of polyurethane pipes for cooling liquid in BES III

    International Nuclear Information System (INIS)

    Li Xunfeng; Zheng Lifang; Ji Quan; Wu Ping; Wang Li

    2009-01-01

    Gamma ray radiation and neutron radiation are predominant in the working conditions of BES III, and the radiation-resistance aging of polyurethane pipes is very important in this condition, as the pipes of cooling liquid for beam pipe and SCQ (superconducting quadrupole) vacuum pipe in BESIII. Polyester polyurethane pipes and polyether polyurethane pipes were irradiated by gamma ray and neutron. The radiation doses were as much as ten years' doses in BES. Pressure test, FTIR and thermal analysis were used to study the radiation-resistance of these two kinds of polyurethane pipes. The results show that the radiation-resistance and thermal stability of polyester polyurethane pipes are prior to those of polyether polyurethane pipes, and the pressure resistance of polyester polyurethane pipes is almost maintained after the irradiation by gamma ray and neutron, but the polyether polyurethane pipes can be aged and ruptured after the irradiation by neutron. (authors)

  1. IDENTIFICATION OF CFC AND HCFC SUBSTITUTES FOR BLOWING POLYURETHANE FOAM INSULATION PRODUCTS

    Science.gov (United States)

    The report gives results of a cooperative effort to identiry chlorofluorocarbons and hydrochlorofluorocarbon substitutes for blowing polyurethane foam insulation products. The substantial ongoing effort is identifying third-generation blowing agets for polyurethane foams to repla...

  2. Biobased composites from thermoplastic polyurethane elastomer and cross-linked acrylated-epoxidized soybean oil

    Science.gov (United States)

    Soybean oil is an important sustainable material. Crosslinked acrylated epoxidized soybean oil (AESO) is brittle without flexibility and the incorporation of thermoplastic polyurethane improves its toughness for industrial applications. The hydrophilic functional groups from both oil and polyurethan...

  3. Adhesive interactions with wood

    Science.gov (United States)

    Charles R. Frihart

    2004-01-01

    While the chemistry for the polymerization of wood adhesives has been studied systematically and extensively, the critical aspects of the interaction of adhesives with wood are less clearly understood. General theories of bond formation need to be modified to take into account the porosity of wood and the ability of chemicals to be absorbed into the cell wall....

  4. Soy protein adhesives

    Science.gov (United States)

    Charles R. Frihart

    2010-01-01

    In the quest to manufacture and use building materials that are more environmentally friendly, soy adhesives can be an important component. Trees fix and store carbon dioxide in the atmosphere. After the trees are harvested, machinery converts the wood into strands, which are then bonded together with adhesives to form strandboard, used in constructing long-lasting...

  5. SPECIFIC FEATURES OF OLIGOMERIC PRODUCT SOLIDIFICATION FROM POLYURETHANE WASTES AND THEIR PRACTICAL APPLICATION

    OpenAIRE

    V. Belyatsky; Yu. Kryvogus

    2012-01-01

    The paper considers a possibility to use secondary polyurethane obtained by  thermal depolymerization of wastes on the basis of cross-linked polyurethane (polyurethane adduct) and isocyanate. An effect of density dependence of the obtained polyurethane samples on nature and quantity of solvent has been revealed and it is significantly observed while using low-boiling solvents. The influence of adduct/solidification agent ratio on mechanical hardness of the obtained samples has been studied in...

  6. Preparation and Characterization of Fluorinated Hydrophobic UV-Crosslinkable Thiol-Ene Polyurethane Coatings

    OpenAIRE

    Wenjing Xia; Nianqing Zhu; Rongjie Hou; Wengui Zhong; Mingqing Chen

    2017-01-01

    The polyurethane prepolymer terminated with a double bond was synthesized using isophorone diisocyanate (IPDI), hydroxyl terminated polybutadiene (HTPB), 1,4-butanediol (BDO), and 2-hydroxyethyl acrylate (HEA). Then, a series of innovative UV-curable polyurethane coatings were prepared by blending ene-terminated polyurethane, fluoroacrylate monomer, and multifunctional thiol crosslinker upon UV exposure. The incorporation of fluoroacrylate monomer and multifunctional thiols into polyurethane ...

  7. Polyurethane Organosilicate Nanocomposites as Blood Compatible Coatings

    Directory of Open Access Journals (Sweden)

    Johnson H. Y. Chung

    2012-02-01

    Full Text Available Polymer clay nanocomposites (NCs show remarkable potential in the field of drug delivery due to their enhanced barrier properties. It is hypothesised that well dispersed clay particles within the polymer matrix create a tortuous pathway for diffusing therapeutic molecules, thereby resulting in more sustained release of the drug. As coatings for medical devices, these materials can simultaneously modulate drug release and improve the mechanical performance of an existing polymer system without introducing additional materials with new chemistries that can lead to regulatory concerns. In this study, polyurethane organosilicate nanocomposites (PUNCs coated onto stainless steel wires were evaluated for their feasibility as blood compatible coatings and as drug delivery systems. Heparin was selected as the model drug to examine the impact of silicate loading and modifier chain length in modulating release. Findings revealed that better dispersion was achieved from samples with lower clay loadings and longer alkyl chains. The blood compatibility of PUNCs as assessed by thrombin generation assays showed that the addition of silicate particles did not significantly decrease the thrombin generation lag time (TGT, p = 0.659 or the peak thrombin (p = 0.999 of polyurethane (PU. PUNC coatings fabricated in this research were not cytotoxic as examined by the cell growth inhibition assay and were uniformly intact, but had slightly higher growth inhibition compared to PU possibly due to the presence of organic modifiers (OM. The addition of heparin into PUNCs prolonged the TGT, indicating that heparin was still active after the coating process. Cumulative heparin release profiles showed that the majority of heparin released was from loosely attached residues on the surface of coils. The addition of heparin further prolonged the TGT as compared to coatings without added heparin, but a slight decrease in heparin activity was observed in the NCs

  8. Determination of Indonesian palm-oil-based bioenergy sustainability indicators using fuzzy inference system

    Science.gov (United States)

    Arkeman, Y.; Rizkyanti, R. A.; Hambali, E.

    2017-05-01

    Development of Indonesian palm-oil-based bioenergy faces an international challenge regarding to sustainability issue, indicated by the establishment of standards on sustainable bioenergy. Currently, Indonesia has sustainability standards limited to palm-oil cultivation, while other standards are lacking appropriateness for Indonesian palm-oil-based bioenergy sustainability regarding to real condition in Indonesia. Thus, Indonesia requires sustainability indicators for Indonesian palm-oil-based bioenergy to gain recognition and easiness in marketing it. Determination of sustainability indicators was accomplished through three stages, which were preliminary analysis, indicator assessment (using fuzzy inference system), and system validation. Global Bioenergy partnership (GBEP) was used as the standard for the assessment because of its general for use, internationally accepted, and it contained balanced proportion between environment, economic, and social aspects. Result showed that the number of sustainability indicators using FIS method are 21 indicators. The system developed has an accuracy of 85%.

  9. Interaction between vegetable oil based plasticizer molecules and polyvinyl chloride, and their plasticization effect

    Science.gov (United States)

    Haryono, Agus; Triwulandari, Evi; Jiang, Pingping

    2017-01-01

    Plasticizer molecules are low molecular weight compounds that are widely used in polymer industries especially in polyvinyl chloride (PVC) resin. As an additive in PVC resin, the important role of plasticizer molecules is to improve the flexibility and processability of PVC by lowering the glass transition temperature (Tg). However, the commercial plasticizer like di(2-ethylhexyl)phthalate (DEHP) is known to cause liver cancer, at least in laboratory rats. DEHP can leach out from PVC into blood, certain drug solutions and fatty foods, which has been detected in the bloodstream of patients undergoing transfusion. Vegetable oil based plasticizers have some attractive properties such as non-toxic, bio-degradable, good heat and light stability, renewable resources, and environmentally friendly. Here we discussed the main results and development of vegetable oil based plasticizer, and especially palm oil based plasticizer. The interaction between plasticizer and polymer was discussed from the properties of the plasticized polymeric material.

  10. Ecological effects of low toxicity oil-based mud drilling in the Beatrice oilfield

    Energy Technology Data Exchange (ETDEWEB)

    Addy, J M; Hartley, J P; Tibbetts, P J.C.

    1984-12-01

    To investigate the effects of drilling discharges on the seabed fauna, surveys were carried out in the Beatrice oilfield after drilling 13 wells with water-based muds, and then after one and five further wells had been drilled using low toxicity oil-based muds. Localized benthic effects were found after the water-based mud drilling. After the use of oil-based muds, the nature of the effects was different, although there was little increase in the area involved. Possible reasons for this are discussed and burial and organic enrichment are suggested as the major influences. It is concluded that the use of low toxicity oil-based mud at Beatrice has resulted in only limited benthic effects, suggesting that the use of these muds is environmentally acceptable.

  11. Polyurethanes for potential use in transparent armour investigated using DSC and DMA

    NARCIS (Netherlands)

    Ekeren, P.J. van; Carton, E.P.

    2011-01-01

    A material combination that may be applied as transparent armour is glass-clad polyurethane. These are comprised of a relatively thin glass strike face and a relatively thick (transparent) polyurethane backing layer. Three transparent polyurethane samples were investigated using differential

  12. 40 CFR 721.8079 - Isophorone diisocyanate neopentyl glycol adipate polyurethane prepolymer.

    Science.gov (United States)

    2010-07-01

    ... glycol adipate polyurethane prepolymer. 721.8079 Section 721.8079 Protection of Environment ENVIRONMENTAL... adipate polyurethane prepolymer. (a) Chemical substance and significant new uses subject to reporting. (1... polyurethane prepolymer (PMN P-94-1743) is subject to reporting under this section for the significant new uses...

  13. Rheokinetics and effect of shear rate on the kinetics of linear polyurethane formation

    NARCIS (Netherlands)

    Navarchian, AH; Picchioni, F; Janssen, LPBM

    In this article, the rheokinetics of polyurethane formation and the influence of shear rate on its kinetics have been studied. Two different linear polyurethane systems with 0% and 100% hard segments are examined in a cone and plate rheometer. The isothermal increase of viscosity during polyurethane

  14. 40 CFR 63.1293 - Standards for slabstock flexible polyurethane foam production.

    Science.gov (United States)

    2010-07-01

    ... polyurethane foam production. 63.1293 Section 63.1293 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY... CATEGORIES National Emission Standards for Hazardous Air Pollutants for Flexible Polyurethane Foam Production § 63.1293 Standards for slabstock flexible polyurethane foam production. Each owner or operator of a...

  15. 40 CFR 63.1300 - Standards for molded flexible polyurethane foam production.

    Science.gov (United States)

    2010-07-01

    ... polyurethane foam production. 63.1300 Section 63.1300 Protection of Environment ENVIRONMENTAL PROTECTION AGENCY... CATEGORIES National Emission Standards for Hazardous Air Pollutants for Flexible Polyurethane Foam Production § 63.1300 Standards for molded flexible polyurethane foam production. Each owner or operator of a new...

  16. TOPEM DSC study of glass transition region of polyurethane cationomers

    International Nuclear Information System (INIS)

    Pielichowska, Kinga; Król, Piotr; Król, Bożena; Pagacz, Joanna

    2012-01-01

    Highlights: ► TOPEM DSC method was employed to investigate the glass transition (T g ) region of fluorinated polyurethane cationomers. ► Introduction of fluorine compounds significantly changes thermal behaviour of cationomers in the T g region of hard segments. ► Introduction of fluorine compound leads to changes of the slope in activation diagram of glass transition. - Abstract: In this paper TOPEM DSC method was employed to investigate the glass transition region of fluorinated polyurethane cationomers. Fluorinated polyurethane cationomers have been synthesised in the reaction of MDI with poly(ethylene glycol) (600) and butane1,4-diol or N-methyl- or N-butyldiethanolamine and 2,2,3,3-tetrafluoro-1,4-butanediol. Better rigidity was found for generally amorphous cationomer coats. It was found that introduction of fluorine compound changes thermal behaviour of polyurethane cationomers as well as leads to changes in the slope in activation diagram profiles of glass transition in comparison to polyuretahene cationomer without fluorine compound. Application of TOPEM DSC allows to obtain more information concerning frequency dependence of glass transition region and thermodynamical stability of polyurethane structures.

  17. Unified Creep Plasticity Damage (UCPD) Model for Rigid Polyurethane Foams.

    Energy Technology Data Exchange (ETDEWEB)

    Neilsen, Michael K. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Lu, Wei-Yang [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Scherzinger, William M. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Hinnerichs, Terry D. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Lo, Chi S. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2015-06-01

    Numerous experiments were performed to characterize the mechanical response of several different rigid polyurethane foams (FR3712, PMDI10, PMDI20, and TufFoam35) to large deformation. In these experiments, the effects of load path, loading rate, and temperature were investigated. Results from these experiments indicated that rigid polyurethane foams exhibit significant volumetric and deviatoric plasticity when they are compressed. Rigid polyurethane foams were also found to be very strain-rate and temperature dependent. These foams are also rather brittle and crack when loaded to small strains in tension or to larger strains in compression. Thus, a new Unified Creep Plasticity Damage (UCPD) model was developed and implemented into SIERRA with the name Foam Damage to describe the mechanical response of these foams to large deformation at a variety of temperatures and strain rates. This report includes a description of recent experiments and experimental findings. Next, development of a UCPD model for rigid, polyurethane foams is described. Selection of material parameters for a variety of rigid polyurethane foams is then discussed and finite element simulations with the new UCPD model are compared with experimental results to show behavior that can be captured with this model.

  18. Stooped Nanohairs: Geometry-Controllable, Unidirectional, Reversible, and Robust Gecko-like Dry Adhesive

    KAUST Repository

    Kim, Tae-il

    2009-06-12

    A study was conducted to demonstrate a simple method for fabricating stopped high-aspect-ratio (AR) nanohairs of polyurethane acrylate (PUA) material that utilized replica molding and post-electron-beam irradiation. The method offered a facile route to prepare angled polymer nanohairs without multistep processes or surface treatment. It was demonstrated that the PUA material was molded into a geometry controlled and high-density nanochair surface with an AR of up to 10 without facing self-matting problem, due to its favorable mechanical properties. The as-formed hairy structures also allowed for structural transformation into directional and angled nanohairs, while maintaining better adhesion capability. The nanohair surface also showed significant unidirectional adhesion properties and a higher shear adhesion due to its structural similarity to natural gecko foot hairs.

  19. Process, Design and Materials for Unidirectionally Tilted Polymeric Micro/Nanohairs and Their Adhesion Characteristics

    Directory of Open Access Journals (Sweden)

    Hyeon Seong Im

    2016-09-01

    Full Text Available Recent research in the field of gecko-inspired dry adhesive has focused on modifying the material and structural properties of polymer-based nanohairs. Polymers such as polystyrene (PS, high-density polyethylene (HDPE, ultraviolet curable epoxy (SU-8, polyurethane acrylate (PUA, polycarbonate (PC, and polydimethyl siloxane (PDMS can fulfill many mechanical property requirements, are easily tunable, and can be produced via large-scale fabrication. However, the fabrication process for tilted structure remains challenging. The tilted structure is a crucial factor in high-degree conformal contact, which facilitates high adhesion, low effective modulus, and directional adhesion properties. Recent studies have attempted to create a tilted structure by applying beam irradiation, mechanical and thermal stress, and magnetic fields. This review provides a comprehensive investigation into advanced strategies for producing tilted polymeric nanostructures and their potential applications in the near future.

  20. Biodegradation of Polyester Polyurethane by Endophytic Fungi▿

    Science.gov (United States)

    Russell, Jonathan R.; Huang, Jeffrey; Anand, Pria; Kucera, Kaury; Sandoval, Amanda G.; Dantzler, Kathleen W.; Hickman, DaShawn; Jee, Justin; Kimovec, Farrah M.; Koppstein, David; Marks, Daniel H.; Mittermiller, Paul A.; Núñez, Salvador Joel; Santiago, Marina; Townes, Maria A.; Vishnevetsky, Michael; Williams, Neely E.; Vargas, Mario Percy Núñez; Boulanger, Lori-Ann; Bascom-Slack, Carol; Strobel, Scott A.

    2011-01-01

    Bioremediation is an important approach to waste reduction that relies on biological processes to break down a variety of pollutants. This is made possible by the vast metabolic diversity of the microbial world. To explore this diversity for the breakdown of plastic, we screened several dozen endophytic fungi for their ability to degrade the synthetic polymer polyester polyurethane (PUR). Several organisms demonstrated the ability to efficiently degrade PUR in both solid and liquid suspensions. Particularly robust activity was observed among several isolates in the genus Pestalotiopsis, although it was not a universal feature of this genus. Two Pestalotiopsis microspora isolates were uniquely able to grow on PUR as the sole carbon source under both aerobic and anaerobic conditions. Molecular characterization of this activity suggests that a serine hydrolase is responsible for degradation of PUR. The broad distribution of activity observed and the unprecedented case of anaerobic growth using PUR as the sole carbon source suggest that endophytes are a promising source of biodiversity from which to screen for metabolic properties useful for bioremediation. PMID:21764951

  1. Melt electrospinning of biodegradable polyurethane scaffolds

    Science.gov (United States)

    Karchin, Ari; Simonovsky, Felix I.; Ratner, Buddy D.; Sanders, Joan E.

    2014-01-01

    Electrospinning from the melt, in contrast to from solution, is an attractive tissue engineering scaffold manufacturing process as it allows for the formation of small diameter fibers while eliminating potentially cytotoxic solvents. Despite this, there is a dearth of literature on scaffold formation via melt electrospinning. This is likely due to the technical challenges related to the need for a well-controlled high temperature setup and the difficulty in developing an appropriate polymer. In this paper, a biodegradable and thermally stable polyurethane (PU) is described specifically for use in melt electrospinning. Polymer formulations of aliphatic PUs based on (CH2)4-content diisocyanates, polycaprolactone (PCL), 1,4-butanediamine and 1,4-butanediol (BD) were evaluated for utility in the melt electrospinning process. The final polymer formulation, a catalyst-purified PU based on 1,4-butane diisocyanate, PCL and BD in a 4/1/3 molar ratio with a weight-average molecular weight of about 40 kDa, yielded a nontoxic polymer that could be readily electrospun from the melt. Scaffolds electrospun from this polymer contained point bonds between fibers and mechanical properties analogous to many in vivo soft tissues. PMID:21640853

  2. Isothermal recovery rates in shape memory polyurethanes

    International Nuclear Information System (INIS)

    Azra, Charly; Plummer, Christopher J G; Månson, Jan-Anders E

    2011-01-01

    This work compares the time dependence of isothermal shape recovery in thermoset and thermoplastic shape memory polyurethanes (SMPUs) with comparable glass transition temperatures. In each case, tensile tests have been used to quantify the influence of various thermo-mechanical programming parameters (deformation temperature, recovery temperature, and stress and storage times following the deformation step) on strain recovery under zero load (free recovery) and stress recovery under fixed strain (constrained recovery). It is shown that the duration of the recovery event may be tuned over several decades of time with an appropriate choice of programming parameters, but that there is a trade-off between the rate of shape recovery and the recoverable stress level. The results are discussed in terms of the thermal characteristics of the SMPUs in the corresponding temperature range as characterized by modulated differential scanning calorimetry and dynamic mechanical analysis, with the emphasis on the role of the effective width of the glass transition temperature and the stability of the network that gives rise to the shape memory effect. (fast track communication)

  3. Carboxylated Polyurethanes Containing Hyperbranched Polyester Soft Segments

    Directory of Open Access Journals (Sweden)

    Žigon, M.

    2006-09-01

    Full Text Available hyperbranched polyester soft segments (HB PU with functional carboxylic groups in order to enable the preparation of stable HB PU dispersions. Carboxylated hyperbranched polyurethanes were synthesized using a hyperbranched polyester based on 2,2-bis(methylolpropionic acid of the fourth pseudo-generation (Boltorn H40 and hexamethylene (HDI or isophorone diisocyanate (IPDI. The reactivity of hyperbranched polyester with HDI was lower than expected, possibly due to the presence of less reactive hydroxyl groups in the linear repeat units. A gel was formed at mole ratios rNCO/OH = 1:2 or 1:4. The synthesis of HB PU was performed with partly esterified hyperbranched polyester with lowered hydroxyl functionality. The carboxyl groups were incorporated in the HB PU backbone by reaction of residual hydroxyl groups with cis-1,2-cyclohexanedicarboxylic anhydride. HB PU aqueous dispersions were stable at least for two months, although their films were brittle. The tensile strength and Young's modulus of blends of linear and HB PU decreased with increasing content of HB PU whereas elongation at break remained nearly constant, which was explained in terms of looser chain packing due to more open tree-like hyperbranched structures.

  4. Shape memory of polyurethanes with silver nanoparticles

    International Nuclear Information System (INIS)

    Monteiro, Fernanda M.A.; Souza, Patterson P. de; Pereira, Iaci M.; Silva, Livio B.J. da; Orefice, Rodrigo L.

    2011-01-01

    Biodegradable polyurethane nano composites were synthesized in an aqueous environment and have their shape memory properties investigated. The matrix based in isopharane diisocyanate and poly(caprolactone diol) (Mn=1250, 2000 g.mol -1 ) was prepared by the prepolymer mixing process. The silver nanoparticles were produced by mixing AgNO 3 and tannic acid. The shape memory properties were measured using universal testing machine (DL3000, EMIC). The shape memory cycle consisted of the following steps: samples were deformed at room temperature; the mechanical constraints on the polymers were removed; samples were cooled down to 0 deg C and to retain the deformed shape; three processes were tested to recover the shape: (a) samples were heated up to 80 deg C in an oven, (b) immersed in pH 4.0 and (c) immersed in pH 7.0. To study the shape memory effect on the nanostructure, small angle X-ray scattering, wide angle X-ray scattering, infrared spectroscopy experiments were carried on. (author)

  5. Nano-Aramid Fiber Reinforced Polyurethane Foam

    Science.gov (United States)

    Semmes, Edmund B.; Frances, Arnold

    2008-01-01

    Closed cell polyurethane and, particularly, polyisocyanurate foams are a large family of flexible and rigid products the result of a reactive two part process wherein a urethane based polyol is combined with a foaming or "blowing" agent to create a cellular solid at room temperature. The ratio of reactive components, the constituency of the base materials, temperature, humidity, molding, pouring, spraying and many other processing techniques vary greatly. However, there is no known process for incorporating reinforcing fibers small enough to be integrally dispersed within the cell walls resulting in superior final products. The key differentiating aspect from the current state of art resides in the many processing technologies to be fully developed from the novel concept of milled nano pulp aramid fibers and their enabling entanglement capability fully enclosed within the cell walls of these closed cell urethane foams. The authors present the results of research and development of reinforced foam processing, equipment development, strength characteristics and the evolution of its many applications.

  6. Hemocompatibility studies on a degradable polar hydrophobic ionic polyurethane (D-PHI).

    Science.gov (United States)

    Brockman, Kathryne S; Kizhakkedathu, Jayachandran N; Santerre, J Paul

    2017-01-15

    Biomaterial blood compatibility is a complex process that involves four key pathways, including the coagulation cascade, the complement system, platelets, and leukocytes. While many studies have addressed the initial contact of blood with homopolymeric (e.g. Teflon) or simple copolymeric (e.g. Dacron) biomaterials, relatively less attention has been given to investigating blood coagulation with respect to complex copolymeric systems containing well defined and diverse function. The current study sought to assess the hemocompatibility of a complex polyurethane (PU) containing a unique combination of polar, hydrophobic, and ionic domains (D-PHI). This included a whole blood (WB) study, followed by tests on the intrinsic and extrinsic coagulation pathways, complement activation, platelet activation, and an assessment of the effect of leukocytes on platelet-biomaterial interactions. A small increase in blood clot formation was observed on D-PHI in WB; however, there was no significant increase in clotting via the intrinsic coagulation cascade. No significant increase in platelet adhesion and only a very slight increase in platelet activation were observed in comparison to albumin-coated substrates (negative control). D-PHI showed mild complement activation and increased initiation of the extrinsic pathway of coagulation, along with the observation that leukocytes were important in mediating platelet-biomaterial interactions. It is proposed that complement is responsible for activating coagulation by inciting leukocytes to generate tissue factor (TF), which causes extrinsic pathway activation. This low level of blood clotting on D-PHI's surface may be necessary for the beneficial wound healing of vascular constructs that has been previously reported for this material. Understanding the hemocompatibility of devices intended for blood-contacting applications is important for predicting device failure. Hemocompatibility is a complex parameter (affected by at least four

  7. Physics of adhesion

    International Nuclear Information System (INIS)

    Gerberich, W W; Cordill, M J

    2006-01-01

    Adhesion physics was relegated to the lowest echelons of academic pursuit until the advent of three seemingly disconnected events. The first, atomic force microscopy (AFM), eventually allowed fine-scale measurement of adhesive point contacts. The second, large-scale computational materials science, now permits both hierarchical studies of a few thousand atoms from first principles or of billions of atoms with less precise interatomic potentials. The third is a microelectronics industry push towards the nanoscale which has provided the driving force for requiring a better understanding of adhesion physics. In the present contribution, an attempt is made at conjoining these separate events into an updating of how theoretical and experimental approaches are providing new understanding of adhesion physics. While all material couples are briefly considered, the emphasis is on metal/semiconductor and metal/ceramic interfaces. Here, adhesion energies typically range from 1 to 100 J m -2 where the larger value is considered a practical work of adhesion. Experimental emphasis is on thin-film de-adhesion for 10 to 1000 nm thick films. For comparison, theoretical approaches from first principles quantum mechanics to embedded atom methods used in multi-scale modelling are utilized

  8. EB curable laminating adhesives

    International Nuclear Information System (INIS)

    Matsuyama, Asao; Kobayashi, Masahide; Gotoh, Sakiko

    1992-01-01

    New developed solvent free EB curable laminating adhesives have two liquid components, A with hydroxy and acryloyl group, B with isocyanate and acryloyl group in a molecule. These EB laminating adhesives do not need any aging process, which is a big advantage, and are very suitable for environment, safety, and health because of no heating process and solvent free formulas. And we have made basic research about the relation of peel strength or heat seal strength versus Tg of cured film, elongation at break, elastic modulus, and so on. Basic specifications of the new developed adhesives are shown. (author)

  9. Synthesis and characterization of waterborne polyurethane acrylate copolymers

    International Nuclear Information System (INIS)

    Sultan, Misbah; Bhatti, Haq Nawaz; Zuber, Mohammad; Barikani, Mehdi

    2013-01-01

    Polyurethane acrylate copolymers were synthesized by emulsion polymerization process. To reduce the environmental hazards, organic solvents were replaced by eco-friendly aqueous system. Concentration of polyurethane and acrylate monomer was varied to investigate the effect of chemical composition on performance properties of copolymers. FTIR spectroscopy was used as a key tool to record the chemical synthesis route. The synthesized copolymer emulsions were characterized by evaluating their particle size, viscosity, dry weight content, chemical and water resistance. Thermal decomposition was studied by thermogravimetric analysis. Scanning electron microscope was used to visualize the morphological structure of copolymers. The experimental results indicate better polyurethane acrylate compatibility till the ratio of 30/70. However, these copolymers exhibited synergistic effects between the two polymers and revealed a remarkable improvement in numerous coating properties

  10. Extraction behavior of uranium(VI) with polyurethane foam

    International Nuclear Information System (INIS)

    Tingchia Huang; Donghwang Chen; Muchang Shieh; Chingtsven Huang

    1992-01-01

    The extraction of uranium(VI) from aqueous solution with polyether-based polyurethane (PU) foam was studied. The effects of the kinds and concentrations of nitrate salts, uranium(VI) concentration, temperature, nitric acid concentration, pH, the content of poly(ethylene oxide) in the polyurethane foam, and the ratio of PU foam weight and solution volume on the extraction of uranium(VI) were investigated. The interferences of fluoride and carbonate ions on the extraction of uranium(VI) were also examined, and methods to overcome both interferences were suggested. It was found that no uranium was extracted in the absence of a nitrate salting-out agent, and the extraction behaviors of uranium(IV) with polyurethane foam could be explained in terms of an etherlike solvent extraction mechanism. In addition, the percentage extraction of a multiple stage was also estimated theoretically

  11. Thermal Properties of Anionic Polyurethane Composition for Leather Finishing

    Directory of Open Access Journals (Sweden)

    Olga KOVTUNENKO

    2016-09-01

    Full Text Available Thermal properties of anionic polyurethane composition mixed with collagen product and hydrophilic sodium form of montmorillonite for use in the finishing of leather were studied by thermogravimetric method. The thermal indices of processes of thermal and thermo-oxidative destruction depending on the polyurethane composition were determined. The influence of anionic polyurethane composition on thermal behavior of chromium tanned gelatin films that imitate the leather were studied. APU composition with natural compounds increases their thermal stability both in air and in nitrogen atmosphere due to the formation of additional bonds between active groups of APU, protein and chrome tanning agent as the result of chemical reactions between organic and inorganic parts with the new structure formation.DOI: http://dx.doi.org/10.5755/j01.ms.22.3.10043

  12. Antimicrobial polyurethane thermosets based on undecylenic acid: synthesis and evaluation.

    Science.gov (United States)

    Lluch, Cristina; Esteve-Zarzoso, Braulio; Bordons, Albert; Lligadas, Gerard; Ronda, Juan C; Galià, Marina; Cádiz, Virginia

    2014-08-01

    In the present study, plant oil-derived surface-modifiable polyurethane thermosets are presented. Polyol synthesis is carried out taking advantage of thiol-yne photopolymerization of undecylenic acid derivatives containing methyl ester or hydroxyl moieties. The prepared methyl ester-containing polyurethanes allow surface modification treatment to enhance their hydrophilicity and impart antimicrobial activity through the following two steps: i) grafting poly(propylene glycol) monoamine (Jeffamine M-600) via aminolysis and ii) Jeffamine M-600 layer complexation with iodine. The antimicrobial activity of the iodine-containing polyurethanes is demonstrated by its capacity to inhibit the growth of Staphylococcus aureus, and Candida albicans in agar media. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  13. Direct transfer of graphene films for polyurethane substrate

    Energy Technology Data Exchange (ETDEWEB)

    Vilani, C.; Romani, E.C.; Larrudé, D.G. [Departamento de Física, Pontifícia Universidade Católica do Rio de Janeiro, 22451-900 Rio de Janeiro, RJ (Brazil); Barbosa, Gelza M. [Diretoria de Sistemas de Armas da Marinha, Marinha do Brasil, 20010-00 Rio de Janeiro, RJ (Brazil); Freire, F.L., E-mail: lazaro@vdg.fis.puc-rio.br [Departamento de Física, Pontifícia Universidade Católica do Rio de Janeiro, 22451-900 Rio de Janeiro, RJ (Brazil); Centro Brasileiro de Pesquisas Físicas, 22290-180 Rio de Janeiro, RJ (Brazil)

    2015-11-30

    Highlights: • Graphene was prepared by CVD using copper foils as substrates. • Monolayer, bilayer and multilayer graphene were transferred to PU. • Samples were characterized by Raman and optical spectroscopies. • PU/monolayer graphene has transmittance around 80% in visible range. - Abstract: We have proposed the direct transfer of large-area graphene films grown by chemical vapor deposition to polymeric substrate by evaporating of solvents of polyurethane/tetrahydrofurane solution. The graphene films on polyurethane substrates were characterized by Raman spectroscopy, optical and atomic force microscopies and UV–vis spectroscopy measurements. The Raman spectra revealed that it is possible to transfer in a controlled manner monolayer, bilayer and multilayer graphene films over polyurethane substrate.

  14. Direct transfer of graphene films for polyurethane substrate

    International Nuclear Information System (INIS)

    Vilani, C.; Romani, E.C.; Larrudé, D.G.; Barbosa, Gelza M.; Freire, F.L.

    2015-01-01

    Highlights: • Graphene was prepared by CVD using copper foils as substrates. • Monolayer, bilayer and multilayer graphene were transferred to PU. • Samples were characterized by Raman and optical spectroscopies. • PU/monolayer graphene has transmittance around 80% in visible range. - Abstract: We have proposed the direct transfer of large-area graphene films grown by chemical vapor deposition to polymeric substrate by evaporating of solvents of polyurethane/tetrahydrofurane solution. The graphene films on polyurethane substrates were characterized by Raman spectroscopy, optical and atomic force microscopies and UV–vis spectroscopy measurements. The Raman spectra revealed that it is possible to transfer in a controlled manner monolayer, bilayer and multilayer graphene films over polyurethane substrate.

  15. Optical adhesive property study

    Energy Technology Data Exchange (ETDEWEB)

    Sundvold, P.D.

    1996-01-01

    Tests were performed to characterize the mechanical and thermal properties of selected optical adhesives to identify the most likely candidate which could survive the operating environment of the Direct Optical Initiation (DOI) program. The DOI system consists of a high power laser and an optical module used to split the beam into a number of channels to initiate the system. The DOI requirements are for a high shock environment which current military optical systems do not operate. Five candidate adhesives were selected and evaluated using standardized test methods to determine the adhesives` physical properties. EC2216, manufactured by 3M, was selected as the baseline candidate adhesive based on the test results of the physical properties.

  16. Fabrication and characterization of cellulose nanocrystal based transparent electroactive polyurethane

    Science.gov (United States)

    Ko, Hyun-U.; Kim, Hyun Chan; Kim, Jung Woong; Zhai, Lindong; Jayaramudu, Tippabattini; Kim, Jaehwan

    2017-08-01

    This paper reports cellulose nanocrystal (CNC) based transparent and electroactive polyurethane (CPPU), suitable for actively tunable optical lens. CNC is used for high dielectric filler to improve electromechanical behavior of CPPU. For high transparency and homogeneous distribution of CNC in polyurethane, CNC-poly[di(ethylene glycol) adipate] is used to play a role of polyol and isocyanate salt. The fabricated CPPU exhibits high transparency (>90%) and 10% of electromechanical strain under 3 V μm-1 electric field. Mechanical, dielectric properties as well as physical and chemical characteristics are investigated to prove the electromechanical behavior of CPPU.

  17. Changes in the Characteristics of Water-in-Oil-based High Internal ...

    African Journals Online (AJOL)

    Changes in the Characteristics of Water-in-Oil-based High Internal Phase Emulsion Containing Moringa Leaves Extract at Various Storage Conditions. ... Conclusion: Moringa HIPE showed stability and can be guided exclusively to protect skin against ultraviolet radiation-mediated oxidative damage. Keywords: Moringa ...

  18. Effect of polysoap on physical and tribology properties of soybean oil-based grease

    Science.gov (United States)

    The overall objective of this work was to evaluate the evolution of soybean oil based grease containing polysoaps made from polymeric epoxdized soybean oil. With this aim, lubricating greases were prepared from a mixed soap comprising lithium soap and triethanol ammonium polysoap synthesized from so...

  19. Sublethal Toxic effects of spent Oil Based Drilling Mud and Cuttings ...

    African Journals Online (AJOL)

    Sublethal toxic effects of spent oil based drilling mud collected from an abandoned oil drilling site in Mpanak, Akwa Ibom State, Nigeria were assessed in the earthworm Aporrectodea longa. The test annelid was exposed to sub-lethal Concentration of 0ppm SPP; 62,500ppm SPP; 125, 000ppm SPP; 250,000ppm SPP and ...

  20. LABORATORY SCALE EVALUATION OF HYDRA-TONE GRAFF-OFF™ COCONUT OIL BASED DEGREASER

    Science.gov (United States)

    This technical and economic assessment evaluated the effectiveness of a biodegradable, coconut oil-based degreaser called Graff-Off™. In immersion (cold) cleaning and rinse tests, Graff-Off™ was compared to a conventional chlorinated solvent 1,1,1 trichloroethane (TCA) and to an ...

  1. 40 CFR 447.10 - Applicability; description of the oil-base solvent wash ink subcategory.

    Science.gov (United States)

    2010-07-01

    ...-base solvent wash ink subcategory. 447.10 Section 447.10 Protection of Environment ENVIRONMENTAL...-Base Solvent Wash Ink Subcategory § 447.10 Applicability; description of the oil-base solvent wash ink...-base ink where the tank washing system uses solvents. When a plant is subject to effluent limitations...

  2. Lipid for biodiesel production from attached growth Chlorella vulgaris biomass cultivating in fluidized bed bioreactor packed with polyurethane foam material.

    Science.gov (United States)

    Mohd-Sahib, Ainur-Assyakirin; Lim, Jun-Wei; Lam, Man-Kee; Uemura, Yoshimitsu; Isa, Mohamed Hasnain; Ho, Chii-Dong; Kutty, Shamsul Rahman Mohamed; Wong, Chung-Yiin; Rosli, Siti-Suhailah

    2017-09-01

    The potential to grow attached microalgae Chlorella vulgaris in fluidized bed bioreactor was materialized in this study, targeting to ease the harvesting process prior to biodiesel production. The proposed thermodynamic mechanism and physical property assessment of various support materials verified polyurethane to be suitable material favouring the spontaneous adhesion by microalgae cells. The 1-L bioreactor packed with only 2.4% (v/v) of 1.00-mL polyurethane foam cubes could achieve the highest attached growth microalgae biomass and lipid weights of 812±122 and 376±37mg, respectively, in comparison with other cube sizes. The maturity of attached growth microalgae biomass for harvesting could also be determined from the growth trend of suspended microalgae biomass. Analysis of FAME composition revealed that the harvested microalgae biomass was dominated by C16-C18 (>60%) and mixture of saturated and mono-unsaturated fatty acids (>65%), satiating the biodiesel standard with adequate cold flow property and oxidative stability. Copyright © 2017 Elsevier Ltd. All rights reserved.

  3. Bioinspired pressure actuated adhesive system

    NARCIS (Netherlands)

    Paretkar, D.R.; Kamperman, M.M.G.; Schneider, A.S.; Martina, D.; Creton, C.; Arzt, E.

    2011-01-01

    We developed a dry synthetic adhesive system inspired by gecko feet adhesion that can switch reversibly from adhesion to non-adhesion with applied pressure as external stimulus. Micropatterned polydimethylsiloxane (PDMS) surfaces with pillars of 30 µm length and 10 µm diameter were fabricated using

  4. Many Roles of Wood Adhesives

    Science.gov (United States)

    Charles R. Frihart

    2014-01-01

    Although wood bonding is one of the oldest applications of adhesives, going back to early recorded history (1), some aspects of wood bonds are still not fully understood. Most books in the general area of adhesives and adhesion do not cover wood bonding. However, a clearer understanding of wood bonding and wood adhesives can lead to improved products. This is important...

  5. Cohesion and Adhesion with Proteins

    Science.gov (United States)

    Charles R. Frihart

    2016-01-01

    With increasing interest in bio-based adhesives, research on proteins has expanded because historically they have been used by both nature and humans as adhesives. A wide variety of proteins have been used as wood adhesives. Ancient Egyptians most likely used collagens tobond veneer to wood furniture, then came casein (milk), blood, fish scales, and soy adhesives, with...

  6. Auxetic Polyurethane Foam (Fabrication, Properties and Applications)

    International Nuclear Information System (INIS)

    Yousif, H.I.Y.

    2012-01-01

    Modern technology requires new materials of special properties. For the last two decades there has been a great interest in a class of materials known as auxetic materials. An auxetic material is a material that has a negative Poisson's ratio which means that this material expands laterally when they subjected to a tensile force unlike most of the other traditional materials. This material has superior properties over the traditional material such as high shear modulus and high impact resistance, which makes this material a good candidate for many engineering applications. In the present research work, auxetic flexible polyurethane polymeric foams having different densities were fabricated from conventional flexible polyurethane polymeric foam at different compression ratios. The microstructure of conventional and processed foams was examined by optical microscope to compare between the two structures. The microstructure of processed foam was compared with the one presented in the literature and it has shown the auxetic structure configuration. This is the first time to produce auxetic foam in Egypt. Conventional and auxetic foam samples having cylindrical and square cross-sections were produced from foams having different densities (25 kg/m 3 and 30 kg/m 3 ). The compression ratios used to produce the auxetic samples are (5.56, 6.94 and 9.26). Four mechanical tests were carried out to get the mechanical properties for both conventional and auxetic foams. Two quasi-static mechanical tests t ension and compression a nd two dynamic mechanical tests H ysteresis and resilience w ere carried out to compare between the conventional and auxetic foams. The quasi-static tensile test was carried out at speed was adjusted to be position control rate of 0.2 mm/s. The compression and hysteresis tests were carried out at strain control rate of 0.3 S -1 . The data recorded from the machine were stress and strain. The modulus of elasticity and Poisson's ratio of the test

  7. In vivo modulation of foreign body response on polyurethane by surface entrapment technique.

    Science.gov (United States)

    Khandwekar, Anand P; Patil, Deepak P; Hardikar, Anand A; Shouche, Yogesh S; Doble, Mukesh

    2010-11-01

    Implanted polymeric materials, such as medical devices, provoke the body to initiate an inflammatory reaction, known as the foreign body response (FBR), which causes several complications. In this study, polyurethane (Tecoflex®, PU) surface modified with the nonionic surfactant Tween80® (PU/T80) and the cell adhesive PLL-RGD peptide (PU/PLL-RGD) by a previously described entrapment technique were implanted in the peritoneal cavity of Wistar rats for 30 days. Implants were retrieved and examined for tissue reactivity and cellular adherence by various microscopic and analytical techniques. Surface-induced inflammatory response was assessed by real-time PCR based quantification of proinflammatory cytokine transcripts, namely, TNF-α and IL-1β, normalized to housekeeping gene GAPDH. Cellular adherence and their distribution profile were assessed by microscopic examination of H&E stained implant sections. It was observed that PU/PLL-RGD followed by the bare PU surface exhibited severe inflammatory and fibrotic response with an average mean thickness of 19 and 12 μm, respectively, in 30 days. In contrast, PU/T80 surface showed only a cellular monolayer of 2-3 μm in thickness, with a mild inflammatory response and no fibrotic encapsulation. The PU/PLL-RGD peptide-modified substrate promoted an enhanced rate of macrophage cell fusion to form foreign body giant cell (FBGCs), whereas FBGCs were rarely observed on Tween80®-modified substrate. The expression levels of proinflammatory cytokines (TNF-α and IL-1β) were upregulated on PU/PLL-RGD surface followed by bare PU, whereas the cytokine expressions were significantly suppressed on PU/T80 surface. Thus, our study highlights modulation of foreign body response on polyurethane surfaces through surface entrapment technique in the form of differential responses observed on PLL-RGD and Tween80® modified surfaces with the former effective in triggering tissue cell adhesion thereby fibrous encapsulation, while the later

  8. Radiation-Induced Grafting with One-Step Process of Waste Polyurethane onto High-Density Polyethylene

    Directory of Open Access Journals (Sweden)

    Jong-Seok Park

    2015-12-01

    Full Text Available The recycling of waste polyurethane (PU using radiation-induced grafting was investigated. The grafting of waste PU onto a high-density polyethylene (HDPE matrix was carried out using a radiation technique with maleic anhydride (MAH. HDPE pellets and PU powders were immersed in a MAH-acetone solution. Finally, the prepared mixtures were irradiated with an electron beam accelerator. The grafted composites were characterized by Fourier transformed infrared spectroscopy (FT-IR, surface morphology, and mechanical properties. To make a good composite, the improvement in compatibility between HDPE and PU is an important factor. Radiation-induced grafting increased interfacial adhesion between the PU domain and the HDPE matrix. When the absorbed dose was 75 kGy, the surface morphology of the irradiated PU/HDPE composite was nearly a smooth and single phase, and the elongation at break increased by approximately three times compared with that of non-irradiated PU/HDPE composite.

  9. A critical review of the measurement of ice adhesion to solid substrates

    Science.gov (United States)

    Work, Andrew; Lian, Yongsheng

    2018-04-01

    Ice adhesion is an issue spanning a wide range of technical fields. In the aerospace industry, ice accretion has led to a large number of casualties and costs the industry billions of dollars every year. To design effective anti-/de-icing systems, the adhesion of ice to surfaces must be understood. In this review paper, the authors surveyed for papers providing methods for the measurement of ice adhesion. 113 papers were identified for comparison, with data being extracted from 58 papers with common test surfaces (aluminum, steel, Teflon® (Chemours), and polyurethane). The methods used were categorized and data were compared based on their precision and the trends they demonstrated. Conceptual problems were identified with the tests used in the literature and discussed, and open questions relevant to testing the adhesion of ice were identified. Several key parameters affecting ice adhesion identified from the literature were temperature, surface roughness, strain rate, and impact velocity. Their effects on adhesion strength were discussed. While researching this topic, it was discovered that many papers did not report the strain rate in their tests, and the vast majority of papers did not correct their data for stress concentrations on the surface, either of which has been shown to cause variation in the data by one order of magnitude. Data compared from the literature typically spanned one to three orders of magnitude. The causes of these variations were discussed.

  10. Dry adhesives with sensing features

    International Nuclear Information System (INIS)

    Krahn, J; Menon, C

    2013-01-01

    Geckos are capable of detecting detachment of their feet. Inspired by this basic observation, a novel functional dry adhesive is proposed, which can be used to measure the instantaneous forces and torques acting on an adhesive pad. Such a novel sensing dry adhesive could potentially be used by climbing robots to quickly realize and respond appropriately to catastrophic detachment conditions. The proposed torque and force sensing dry adhesive was fabricated by mixing Carbon Black (CB) and Polydimethylsiloxane (PDMS) to form a functionalized adhesive with mushroom caps. The addition of CB to PDMS resulted in conductive PDMS which, when under compression, tension or torque, resulted in a change in the resistance across the adhesive patch terminals. The proposed design of the functionalized dry adhesive enables distinguishing an applied torque from a compressive force in a single adhesive pad. A model based on beam theory was used to predict the change in resistance across the terminals as either a torque or compressive force was applied to the adhesive patch. Under a compressive force, the sensing dry adhesive was capable of measuring compression stresses from 0.11 Pa to 20.9 kPa. The torque measured by the adhesive patch ranged from 2.6 to 10 mN m, at which point the dry adhesives became detached. The adhesive strength was 1.75 kPa under an applied preload of 1.65 kPa for an adhesive patch with an adhesive contact area of 7.07 cm 2 . (paper)

  11. Dry adhesives with sensing features

    Science.gov (United States)

    Krahn, J.; Menon, C.

    2013-08-01

    Geckos are capable of detecting detachment of their feet. Inspired by this basic observation, a novel functional dry adhesive is proposed, which can be used to measure the instantaneous forces and torques acting on an adhesive pad. Such a novel sensing dry adhesive could potentially be used by climbing robots to quickly realize and respond appropriately to catastrophic detachment conditions. The proposed torque and force sensing dry adhesive was fabricated by mixing Carbon Black (CB) and Polydimethylsiloxane (PDMS) to form a functionalized adhesive with mushroom caps. The addition of CB to PDMS resulted in conductive PDMS which, when under compression, tension or torque, resulted in a change in the resistance across the adhesive patch terminals. The proposed design of the functionalized dry adhesive enables distinguishing an applied torque from a compressive force in a single adhesive pad. A model based on beam theory was used to predict the change in resistance across the terminals as either a torque or compressive force was applied to the adhesive patch. Under a compressive force, the sensing dry adhesive was capable of measuring compression stresses from 0.11 Pa to 20.9 kPa. The torque measured by the adhesive patch ranged from 2.6 to 10 mN m, at which point the dry adhesives became detached. The adhesive strength was 1.75 kPa under an applied preload of 1.65 kPa for an adhesive patch with an adhesive contact area of 7.07 cm2.

  12. Synthesis and characterization of bio-based polyurethane from ...

    Indian Academy of Sciences (India)

    Benzoylated tannin prepared by benzoylation of cashewnut husk tannin, was treated with hexame-thylenediisocyanate in the presence of 1,4-butanediol as an extender to prepare thermosetting polyurethane. The sample was characterized using FT–IR and 13C NMR spectra. Thermal, morphological, physico-chemical and ...

  13. WEATHERING DEGRADATION OF A POLYURETHANE COATING. (R828081E01)

    Science.gov (United States)

    The degradation of polyurethane topcoat over a chromate pigmented epoxy primer was examined by atomic force microscopy (AFM), scanning electronic microscopy (SEM), X-ray photo-electron spectroscopy (XPS) and Fourier transform infra-red spectroscopy (FTIR) after the coated pane...

  14. Thermoplastic shape-memory polyurethanes based on natural oils

    International Nuclear Information System (INIS)

    Saralegi, Ainara; Eceiza, Arantxa; Corcuera, Maria Angeles; Johan Foster, E; Weder, Christoph

    2014-01-01

    A new family of segmented thermoplastic polyurethanes with thermally activated shape-memory properties was synthesized and characterized. Polyols derived from castor oil with different molecular weights but similar chemical structures and a corn-sugar-based chain extender (propanediol) were used as starting materials in order to maximize the content of carbon from renewable resources in the new materials. The composition was systematically varied to establish a structure–property map and identify compositions with desirable shape-memory properties. The thermal characterization of the new polyurethanes revealed a microphase separated structure, where both the soft (by convention the high molecular weight diol) and the hard phases were highly crystalline. Cyclic thermo-mechanical tensile tests showed that these polymers are excellent candidates for use as thermally activated shape-memory polymers, in which the crystalline soft segments promote high shape fixity values (close to 100%) and the hard segment crystallites ensure high shape recovery values (80–100%, depending on the hard segment content). The high proportion of components from renewable resources used in the polyurethane formulation leads to the synthesis of bio-based polyurethanes with shape-memory properties. (paper)

  15. Development of a phenomenological constitutive model for polyurethane foams

    International Nuclear Information System (INIS)

    Neilsen, M.K.; Morgan, H.S.; Krieg, R.D.; Yoshimura, H.R.

    1989-01-01

    Rigid, closed-cell, polyurethane foam is used in impact limiters in nuclear waste transport containers. During a hypothetical nuclear waste transport accident, the foam is expected to absorb a significant amount of impact energy by undergoing large inelastic volume reductions. Consequently, the crushing of polyurethane foams must be well characterized and accurately modeled to properly analyze a transport container accident. At the request of Sandia National Laboratories, a series of uniaxial, hydrostatic and triaxial compression tests on polyurethane foams were performed by the New Mexico Engineering Research Institute (NMERI). The combination of hydrostatic and triaxial tests was chosen to provide sufficient data to characterize both the volumetric and deviatoric behaviors of the foams and the coupling between the two responses. Typical results from the NMERI tests are included in this paper. A complete description of these tests can be found in Neilsen et al., 1987. Constitutive models that have been used in the past to model foam did not capture some important foam behaviors observed in the NMERI tests. Therefore, a new constitutive model for rigid, closed-cell, polyurethane foams was developed and implemented in two finite element codes. Development of the new model is discussed in this paper. Also, results from analyses with the new model and other constitutive models are presented to demonstrate differences between the various models. 4 refs., 6 figs., 1 tab

  16. Sorption of Triangular Silver Nanoplates on Polyurethane Foam

    Science.gov (United States)

    Furletov, A. A.; Apyari, V. V.; Garshev, A. V.; Volkov, P. A.; Tolmacheva, V. V.; Dmitrienko, S. G.

    2018-02-01

    The sorption of triangular silver nanoplates on polyurethane foam is investigated as a procedure for creating a nanocomposite sensing material for subsequent use in optical means of chemical analysis. Triangular silver nanoplates are synthesized and characterized, and a simple sorption technique for the formation of a composite material based on these nanoplates is proposed.

  17. Antimicrobial polyurethane coatings based on ionic liquid quaternary ammonium compounds

    NARCIS (Netherlands)

    Yagci, M.B.; Bolca, S.; Heuts, J.P.A.; Ming, W.; With, de G.

    2011-01-01

    The antimicrobial effect of ionic liquids (ILs) as comonomers in polyurethane surface coatings was investigated. Ionic liquid-containing coatings were prepared from a hydroxyl end-capped liquid oligoester and a triisocyanate crosslinker. Three different commercially available hydroxyl end-capped

  18. Polyurethanes with bio-based and recycled components

    Czech Academy of Sciences Publication Activity Database

    Beneš, Hynek; Vlček, T.; Černá, R.; Hromádková, Jiřina; Walterová, Zuzana; Svitáková, Romana

    2012-01-01

    Roč. 114, č. 1 (2012), s. 71-83 ISSN 1438-7697 R&D Projects: GA MPO 2A-2TP1/135 Institutional research plan: CEZ:AV0Z40500505 Keywords : natural oil * polyol * polyurethane Subject RIV: CD - Macromolecular Chemistry Impact factor: 2.266, year: 2012

  19. Polyurethanes elastomers with amide chain extenders of uniform length

    NARCIS (Netherlands)

    van der Schuur, J.M.; Noordover, B.A.J.; Noordover, Bart; Gaymans, R.J.

    2006-01-01

    Toluene diisocyanate based polyurethanes with amide extenders were synthesized poly(propylene oxide) with a number average molecular weight of 2000 and endcapped with toluene diisocyanate was used as the polyether segment. The chain extenders were based on poly(hexamethylene terephthalamide):

  20. Novel polycarbonate-based polyurethane elastomers: composition–property relationship

    Czech Academy of Sciences Publication Activity Database

    Špírková, Milena; Pavličevic, J.; Strachota, Adam; Poreba, Rafal; Bera, O.; Kaprálková, Ludmila; Baldrian, Josef; Šlouf, Miroslav; Lazić, N.; Budinski-Simendic, J.

    2011-01-01

    Roč. 47, č. 5 (2011), s. 959-972 ISSN 0014-3057 R&D Projects: GA ČR GAP108/10/0195 Institutional research plan: CEZ:AV0Z40500505 Keywords : polyurethane elastomer * polycarbonate diol * montmorillonite Subject RIV: CD - Macromolecular Chemistry Impact factor: 2.739, year: 2011

  1. Use of porous polyurethanes for meniscal reconstruction and meniscal prostheses

    NARCIS (Netherlands)

    deGroot, JH; deVrijer, R; Pennings, AJ; Veth, RPH; Jansen, HWB

    In the past, porous materials made of an aromatic polyurethane (PU) were successfully used for meniscal reconstruction in dogs. Since aromatic PUs yield very toxic fragments upon degradation, a linear PU was synthesized by curing a poly(epsilon-caprolactone) and 1,4-trans-cyclohexane diisocyanate I

  2. 78 FR 55641 - Polyurethane-Type Polymers; Tolerance Exemption

    Science.gov (United States)

    2013-09-11

    ...-Type Polymers; Tolerance Exemption AGENCY: Environmental Protection Agency (EPA). ACTION: Final rule... polymers produced by the reaction of either 1,6-hexanediisocyanate; 2,4,4-trimethyl-1,6-hexanediisocyanate... (also known as polyurethane-type polymers), when used as an inert ingredient in a pesticide chemical...

  3. Utilization of natural oils for decomposition of polyurethanes

    Czech Academy of Sciences Publication Activity Database

    Beneš, Hynek; Černá, R.; Ďuračková, Andrea; Látalová, Petra

    2012-01-01

    Roč. 20, č. 1 (2012), s. 175-185 ISSN 1566-2543 R&D Projects: GA MPO 2A-2TP1/135 Institutional research plan: CEZ:AV0Z40500505 Keywords : polyurethane * oleochemical polyol * chemical recycling Subject RIV: CD - Macromolecular Chemistry Impact factor: 1.495, year: 2012

  4. Sanitary and hygienic assessment of polyurethane foam compositions

    Energy Technology Data Exchange (ETDEWEB)

    Sukhanov, V V; Putilina, O.N. (Donetskii NII Gigieny Truda i Professional' nykh Zabolevanii (USSR))

    1990-07-01

    Describes and presents the results of a long-term study performed by the Skochinski Institute and DonUGI into the suitability of various Soviet and foreign polyurethane foams as rock strengtheners in coal mines. Concludes that although further research is needed to clarify the effect of polyurethane absorbed by coal particles and on pneumoconioses, the industrial use of injectable polyisocyanite-based polyurethanes in amounts of up to 1 t/shift and with a minimum air exchange rate of 300 m{sup 3}/min is feasible as long as the safety laws are strictly observed. Those working with this material should be given a medical examination at least once a year. If the substance comes into contact with the skin or eyes, they should be washed with a 1-3% solution of sodium bicarbonate and then pure water; if it contaminates protective clothing this should be degassed in a 5-10% solution of ammonia for 24 hours and then washed. Due to the risk of toxic substances being released from the components of the polyurethane in the event of an endogenic fire, all workers should be equipped with their own personal breathing apparatus.

  5. Recycling Waste Polyurethane as a Carbon Resource in Ironmaking ...

    African Journals Online (AJOL)

    Globally, major avenues available for dealing with waste Poly-Urethane (PU) are disposal at landfill sites and incineration. However, PU contains high levels of carbon and hydrogen that can be recovered for use as reductant in metal extraction processes. In this work the use of post-consumer PU as reductant for the ...

  6. Novel route of synthesis for cellulose fiber-based hybrid polyurethane

    Science.gov (United States)

    Ikhwan, F. H.; Ilmiati, S.; Kurnia Adi, H.; Arumsari, R.; Chalid, M.

    2017-07-01

    Polyurethanes, obtained by the reaction of a diisocyanate compound with bifunctional or multifunctional reagent such as diols or polyols, have been studied intensively and well developed. The wide range modifier such as chemical structures and molecular weight to build polyurethanes led to designs of materials that may easily meet the functional product demand and to the extraordinary spreading of these materials in market. Properties of the obtained polymer are related to the chemical structure of polyurethane backbone. A number polyurethanes prepared from biomass-based monomers have been reported. Cellulose fiber, as a biomass material is containing abundant hydroxyl, promising material as chain extender for building hybrid polyurethanes. In previous researches, cellulose fiber was used as filler in synthesis of polyurethane composites. This paper reported a novel route of hybrid polyurethane synthesis, which a cellulose fiber was used as chain extender. The experiment performed by reacting 4,4’-Methylenebis (cyclohexyl isocyanate) (HMDI) and polyethylene glycol with variation of molecular weight to obtained pre-polyurethane, continued by adding micro fiber cellulose (MFC) with variation of type and composition in the mixture. The experiment was evaluated by NMR, FTIR, SEM and STA measurement. NMR and FTIR confirmed the reaction of the hybrid polyurethane. STA showed hybrid polyurethane has good thermal stability. SEM showed good distribution and dispersion of sorghum-based MFC.

  7. Performance of adhesives base on PU, Epoxy and silane in the Kevlar/alumina interface; Desempenho de adesivos a base de PU, epoxi e silano na interface Kevlar/alumina

    Energy Technology Data Exchange (ETDEWEB)

    Noronha, K.F.; Melo, F.C.L.; Lopes, C.M.A. [Divisao de Materiais, Instituto de Aeronautica e Espaco (IAE), Sao Jose dos Campos, SP (Brazil); Divisao de Engenharia Mecanica-Aeronautica, Instituto Tecnologico de Aeronautica (ITA), Sao Jose dos Campos, SP (Brazil)], e-mail: cmoniz@iae.cta.br

    2010-07-01

    Hybrid ceramic/polymer composites are used for ballistic protection due to the good high-velocity impact absorption properties. The choice of the proper adhesive used to bond ceramic and polymer layers is one of the major issues for hybrid armor development due to its influence in the ballistic resistance behaviour. This work presents an adhesion study in composites of aramid textile (Kevlar) and alumina. Adhesives of different chemical nature, based on polyurethane, epoxy and silane were evaluated. T-Peel test was performed for the interface characterization and the post- failure surfaces were examined by optical microscopy. In all samples the failure occurred at the interface. The silane-based adhesive showed no interaction with the polymer, while the PU hot melt adhesive presented the highest adhesion strengths. (author)

  8. The Modification of Polyurethane Foams Using New Boroorganic Polyols (II) Polyurethane Foams from Boron-Modified Hydroxypropyl Urea Derivatives

    Science.gov (United States)

    2014-01-01

    The work focuses on research related to determination of application possibility of new, ecofriendly boroorganic polyols in rigid polyurethane foams production. Polyols were obtained from hydroxypropyl urea derivatives esterified with boric acid and propylene carbonate. The influence of esterification type on properties of polyols and next on polyurethane foams properties was determined. Nitrogen and boron impacts on the foams' properties were discussed, for instance, on their physical, mechanical, and electric properties. Boron presence causes improvement of dimensional stability and thermal stability of polyurethane foams. They can be applied even at temperature 150°C. Unfortunately, introducing boron in polyurethanes foams affects deterioration of their water absorption, which increases as compared to the foams that do not contain boron. However, presence of both boron and nitrogen determines the decrease of the foams combustibility. Main impact on the decrease combustibility of the obtained foams has nitrogen presence, but in case of proper boron and nitrogen ratio their synergic activity on the combustibility decrease can be easily seen. PMID:24587721

  9. Electrically Conductive Epoxy Adhesives

    Directory of Open Access Journals (Sweden)

    Lan Bai

    2011-02-01

    Full Text Available Conductive adhesives are widely used in electronic packaging applications such as die attachment and solderless interconnections, component repair, display interconnections, and heat dissipation. The effects of film thickness as functions of filler volume fraction, conductive filler size, shape, as well as uncured adhesive matrix viscosity on the electrical conduction behavior of epoxy-based adhesives are presented in this work. For this purpose, epoxy-based adhesives were prepared using conductive fillers of different size, shape, and types, including Ni powder, flakes, and filaments, Ag powder, and Cu powder. The filaments were 20 μm in diameter, and 160 or 260 μm in length. HCl and H3PO4 acid solutions were used to etch and remove the surface oxide layers from the fillers. The plane resistance of filled adhesive films was measured using the four-point method. In all cases of conductive filler addition, the planar resistivity levels for the composite adhesive films increased when the film thickness was reduced. The shape of resistivity-thickness curves was negative exponential decaying type and was modeled using a mathematical relation. The relationships between the conductive film resistivities and the filler volume fractions were also derived mathematically based on the experimental data. Thus, the effects of surface treatment of filler particles, the type, size, shape of fillers, and the uncured epoxy viscosity could be included empirically by using these mathematical relations based on the experimental data. By utilizing the relations we proposed to model thickness-dependent and volume fraction-dependent conduction behaviors separately, we were able to describe the combined and coupled volume fraction-film thickness relationship mathematically based on our experimental data.

  10. Research into Oil-based Colloidal-Graphite Lubricants for Forging of Al-based Alloys

    International Nuclear Information System (INIS)

    Petrov, A.; Petrov, P.; Petrov, M.

    2011-01-01

    The presented paper describes the topical problem in metal forging production. It deals with the choice of an optimal lubricant for forging of Al-based alloys. Within the scope of the paper, the properties of several oil-based colloidal-graphite lubricants were investigated. The physicochemical and technological properties of these lubricants are presented. It was found that physicochemical properties of lubricant compositions have an influence on friction coefficient value and quality of forgings.The ring compression method was used to estimate the friction coefficient value. Hydraulic press was used for the test. The comparative analysis of the investigated lubricants was carried out. The forging quality was estimated on the basis of production test. The practical recommendations were given to choose an optimal oil-based colloidal-graphite lubricant for isothermal forging of Al-based alloy.

  11. Study on Biodegradation of Palm Oil-based UV-Curable Films in Soil

    International Nuclear Information System (INIS)

    Rida Tajau; Siti Farhana Fathy; Mohamad Norahiman Abdurahman; Anis Asmi Azman; Nur Amira Hamidi; Mek Zah Salleh; Nik Ghazali Nik Salleh

    2014-01-01

    The palm oil-based ultraviolet (UV)-curable films were subjected to an outdoor soil burial test to investigate the biodegradation under natural environment. The films were burial in the soil experiment plot at the Nuclear Malaysia's Dengkil complex which is near the BTS building at block 42. Biodegradation tests are more specific to burial film in soil experiments for 12 months under natural conditions. The biodegradability of palm oil resin based UV-curable films were investigated and compared with the petrochemical resin based film. The films properties were compared with respect to properties of the film morphology and the film weight loss which are analyzed using the scanning electron microscope (SEM), an optical microscope and the weight loss of film calculation. These findings suggested that the palm oil-based UV-curable films show quite satisfactory biodegradation levels. (author)

  12. Mechanically robust silver coatings prepared by electroless plating on thermoplastic polyurethane

    Science.gov (United States)

    Vasconcelos, B.; Vediappan, K.; Oliveira, J. C.; Fonseca, C.

    2018-06-01

    A simple and low-cost surface functionalization method is proposed to activate a thermoplastic polyurethane (TPU) for the electroless deposition of a silver coating with excellent adhesion and low resistivity. The TPU surface functionalization was performed in solution and consisted in forming a physical interpenetrating network at the TPU surface, involving TPU and polyvinylpyrrolidone (PVP), a polymer displaying a strong affinity for metals. The presence of PVP on the TPU surface and its stability in aqueous solution were assessed by ATR-FTIR and contact angle measurements as a function of the PVP concentration and treatment time. A modified Tollens solution was used to grow a silver film on the TPU substrate, by using the electroless plating method. Compact silver films with an average thickness of 12.5 μm and a resistivity of 8.57 mΩ·cm were obtained for a 24 h plating time. The adhesion strength of the silver film proved to be higher than 8.5 N/cm. The resistance to fatigue of the silver films was studied by performing series of compression/stretching tests (150 cycles). It was concluded that the films kept low resistance values, although displaying a higher sensitivity to compression than to stretching. Furthermore, the films keep a good conductivity for strains up to 400%. The excellent electrical and mechanical properties of the films make them suitable candidates for the coating of multipin dry bioelectrodes. Owing to the high affinity of many metals for PVP, this activation technique has the potential to be extended to the deposition of other metals and other polymers as well, provided a suitable solvent is used.

  13. Electrospinning thermoplastic polyurethane/graphene oxide scaffolds for small diameter vascular graft applications

    Energy Technology Data Exchange (ETDEWEB)

    Jing, Xin [National Engineering Research Center of Novel Equipment for Polymer Processing, The Key Laboratory of Polymer Processing Engineering of Ministry of Education, South China University of Technology, Guangzhou (China); Department of Mechanical Engineering, University of Wisconsin–Madison, WI (United States); Wisconsin Institute for Discovery, University of Wisconsin–Madison, WI (United States); Mi, Hao-Yang [National Engineering Research Center of Novel Equipment for Polymer Processing, The Key Laboratory of Polymer Processing Engineering of Ministry of Education, South China University of Technology, Guangzhou (China); Salick, Max R. [Wisconsin Institute for Discovery, University of Wisconsin–Madison, WI (United States); Department of Engineering Physics, University of Wisconsin–Madison, WI (United States); Cordie, Travis M. [Wisconsin Institute for Discovery, University of Wisconsin–Madison, WI (United States); Department of Biomedical Engineering, University of Wisconsin–Madison, WI (United States); Peng, Xiang-Fang, E-mail: pmxfpeng@scut.edu.cn [National Engineering Research Center of Novel Equipment for Polymer Processing, The Key Laboratory of Polymer Processing Engineering of Ministry of Education, South China University of Technology, Guangzhou (China); Turng, Lih-Sheng, E-mail: turng@engr.wisc.edu [Department of Mechanical Engineering, University of Wisconsin–Madison, WI (United States); Wisconsin Institute for Discovery, University of Wisconsin–Madison, WI (United States)

    2015-04-01

    Fabrication of small diameter vascular grafts plays an important role in vascular tissue engineering. In this study, thermoplastic polyurethane (TPU)/graphene oxide (GO) scaffolds were fabricated via electrospinning at different GO contents as potential candidates for small diameter vascular grafts. In terms of mechanical and surface properties, the tensile strength, Young's modulus, and hydrophilicity of the scaffolds increased with an increase of GO content while plasma treatment dramatically improved the scaffold hydrophilicity. Mouse fibroblast (3T3) and human umbilical vein endothelial cells (HUVECs) were cultured on the scaffolds separately to study their biocompatibility and potential to be used as vascular grafts. It was found that cell viability for both types of cells, fibroblast proliferation, and HUVEC attachment were the highest at a 0.5 wt.% GO loading whereas oxygen plasma treatment also enhanced HUVEC viability and attachment significantly. In addition, the suture retention strength and burst pressure of tubular TPU/GO scaffolds containing 0.5 wt.% GO were found to meet the requirements of human blood vessels, and endothelial cells were able to attach to the inner surface of the tubular scaffolds. Platelet adhesion tests using mice blood indicated that vascular scaffolds containing 0.5% GO had low platelet adhesion and activation. Therefore, the electrospun TPU/GO tubular scaffolds have the potential to be used in vascular tissue engineering. - Highlights: • TPU/GO vascular scaffolds were prepared via electrospinning. • The addition of GO improved the modulus and hydrophilicity of the scaffolds. • Fibroblast cell culture verified the scaffolds' biocompatibility. • Endothelial cell culture verified the scaffolds' vascular graft affinity. • The mechanical properties fulfilled the requirements of vascular grafts.

  14. Hard and transparent hybrid polyurethane coatings using in situ incorporation of calcium carbonate nanoparticles

    International Nuclear Information System (INIS)

    Yao Lu; Yang Jie; Sun Jing; Cai Lifang; He Linghao; Huang Hui; Song Rui; Hao Yongmei

    2011-01-01

    Highlights: → In situ mineralization via gas diffusion was adopted for a good dispersion of calcium carbonate nanoparticles in the polymeric PU matrix. → Hybrid films with high dispersion, transparency, robust and thermal stability can be obtained by controlling the CaCO 3 loading. → The hybrid films display a significant improvement in its water resistance, surface hardness, scratch resistance and flexibility, with the introduction of CaCO 3 , and all coatings exhibited excellent chemical resistance and adhesion. - Abstract: The combination of hardness, scratch resistance, and flexibility is a highly desired feature in many coating applications. The aim of this study is to achieve this goal through the in situ introduction of an unmodified calcium carbonate (CaCO 3 ) into a water-soluble polyurethane (PU) matrix. Smooth and (semi-) transparent films were prepared from both the neat PU and the CaCO 3 -filled composites. As evidenced by the measurements from scanning electron microscopy (SEM), optical microscopy, dynamic mechanical analysis (DMA) and thermogravimetric analysis (TGA), hybrid films with high dispersion, transparency, robustness and thermal stability could be obtained by controlling the CaCO 3 loading. The storage modulus could increase from 441 MPa of neat PU matrix to 1034 MPa of hybrid film containing 2% (w/w) CaCO 3 . In addition, the same hybrid films displayed a significant improvement in its water resistance. In this case, the water-uptake ratio decreased from 41.54% of PU to 2.21% of hybrid film containing 2% (w/w) CaCO 3 . Moreover, with the introduction of CaCO 3 , conventional coating characterization methods demonstrated an increase in the surface hardness, scratch resistance and flexibility, and all coatings exhibited excellent chemical resistance and adhesion.

  15. Reversible adhesion switching of porous fibrillar adhesive pads by humidity.

    Science.gov (United States)

    Xue, Longjian; Kovalev, Alexander; Dening, Kirstin; Eichler-Volf, Anna; Eickmeier, Henning; Haase, Markus; Enke, Dirk; Steinhart, Martin; Gorb, Stanislav N

    2013-01-01

    We report reversible adhesion switching on porous fibrillar polystyrene-block-poly(2-vinyl pyridine) (PS-b-P2VP) adhesive pads by humidity changes. Adhesion at a relative humidity of 90% was more than nine times higher than at a relative humidity of 2%. On nonporous fibrillar adhesive pads of the same material, adhesion increased only by a factor of ~3.3. The switching performance remained unchanged in at least 10 successive high/low humidity cycles. Main origin of enhanced adhesion at high humidity is the humidity-induced decrease in the elastic modulus of the polar component P2VP rather than capillary force. The presence of spongelike continuous internal pore systems with walls consisting of P2VP significantly leveraged this effect. Fibrillar adhesive pads on which adhesion is switchable by humidity changes may be used for preconcentration of airborne particulates, pollutants, and germs combined with triggered surface cleaning.

  16. Application of game theory in decision making strategy: Does gas fuel industry need to kill oil based fuel industry?

    Science.gov (United States)

    Azmi, Abdul Luky Shofi'ul; Prabandari, Dyah Lusiana; Hakim, Muhammad Lintang Islami

    2017-03-01

    Even though conversion of oil based fuel (Bahan Bakar Minyak) into gas fuel (Bahan Bakar Gas) for transportation (both land and sea) is one of the priority programs of the government of Indonesia, rules that have been established merely basic rules of gas fuel usage license for transportation, without discussing position of gas fuel related to oil based fuel in detail. This paper focus on possible strategic behavior of the key players in the oil-gas fuel conversion game, who will be impacted by the position of gas fuel as complement or substitution of oil based fuel. These players include industry of oil based fuel, industry of gas fuel, and the government. Modeling is made based on two different conditions: government plays a passive role and government plays an active role in legislating additional rules that may benefit industry of gas fuel. Results obtained under a passive government is that industry of oil based fuel need to accommodate the presence of industry of gas fuel, and industry of gas fuel does not kill/ eliminate the oil based fuel, or gas fuel serves as a complement. While in an active government, the industry of oil based fuel need to increase its negotiation spending in the first phase so that the additional rule that benefitting industry of gas fuel would not be legislated, while industry of gas fuel chooses to indifferent; however, in the last stage, gas fuel turned to be competitive or choose its role to be substitution.

  17. Use of Oil-Based Mud Cutting Waste in Cement Clinker Manufacturing

    OpenAIRE

    Saif Al-Dhamri, H; Black, L

    2014-01-01

    Oil-based Mud (OBM) cutting waste is generated during the process of oil well drilling. The drilled rocks are removed from deep within the drilled well and pumped to the surface. The portion removed , known at "cutting", is a mixture of rocks, mud, water and oil. Most drilling companies store this waste in open yards with no specific treatment solution. The environmental regulations in Oman specify that storage should involve isolation, to prevent penetration of the contamination to the surfa...

  18. Microcapsules Filled with a Palm Oil-Based Alkyd as Healing Agent for Epoxy Matrix

    OpenAIRE

    Nurshafiza Shahabudin; Rosiyah Yahya; Seng Neon Gan

    2016-01-01

    One of the approaches to prolong the service lifespan of polymeric material is the development of self-healing ability by means of embedded microcapsules containing a healing agent. In this work, poly(melamine-urea-formaldehyde) (PMUF) microcapsules containing a palm oil-based alkyd were produced by polymerization of melamine resin, urea and formaldehyde that encapsulated droplets of the suspended alkyd particles. A series of spherical and free-flowing microcapsules were obtained. The chemica...

  19. Comparison of theories of anisotropy in transformer oil-based magnetic fluids

    OpenAIRE

    Kúdelčík, Jozef; Bury, Peter; Drga, Jozef; Kopčanský, Peter; Závišová, Vlasta; Timko, Milan

    2013-01-01

    The external magnetic field in transformer oil-based magnetic fluids leads to the aggregation of magnetic nanoparticles and formation of clusters. These aggregations are the result of the interaction between the external magnetic field and the magnetic moments of the nanoparticles occurs. However, the temperature of magnetic fluids has also very important influence on the structural changes because the mechanism of thermal motion acts against the cluster creation. The acoustic spectroscopy ...

  20. Cell-seeded polyurethane-fibrin structures – A possible system for intervertebral disc regeneration

    Directory of Open Access Journals (Sweden)

    C Mauth

    2009-10-01

    Full Text Available Nowadays, intervertebral disc (IVD degeneration is one of the principal causes of low back pain involving high expense within the health care system. The long-term goal is the development of a medical treatment modality focused on a more biological regeneration of the inner nucleus pulposus (NP. Hence, interest in the endoscopic implantation of an injectable material took center stage in the recent past. We report on the development of a novel polyurethane (PU scaffold as a mechanically stable carrier system for the reimplantation of expanded autologous IVD-derived cells (disc cells to stimulate regenerative processes and restore the chondrocyte-like tissue within the NP. Primary human disc cells were seeded into newly developed PU spheroids which were subsequently encapsulated in fibrin hydrogel. The study aims to analyze adhesion properties, proliferation capacity and phenotypic characterization of these cells. Polymerase chain reaction was carried out to detect the expression of genes specifically expressed by native IVD cells. Biochemical analyses showed an increased DNA content, and a progressive enhancement of total collagen and glycosaminoglycans (GAG was observed during cell culture. The results suggest the synthesis of an appropriate extracellular matrix as well as a stable mRNA expression of chondrogenic and/or NP specific markers. In conclusion, the data presented indicate an alternative medical approach to current treatment options of degenerated IVD tissue.

  1. New Polyurethane Nail Lacquers for the Delivery of Terbinafine: Formulation and Antifungal Activity Evaluation.

    Science.gov (United States)

    Gregorí Valdes, Barbara S; Serro, Ana Paula; Gordo, Paulo M; Silva, Alexandra; Gonçalves, Lídia; Salgado, Ana; Marto, Joana; Baltazar, Diogo; Dos Santos, Rui Galhano; Bordado, João Moura; Ribeiro, Helena Margarida

    2017-06-01

    Onychomycosis is a fungal nail infection. The development of new topical antifungal agents for the treatment of onychomycosis has focused on formulation enhancements that optimize the pharmacological characteristics required for its effective treatment. Polyurethanes (PUs) have never been used in therapeutic nail lacquers. The aim of this work has been the development of new PU-based nail lacquers with antifungal activity containing 1.0% (wt/wt) of terbinafine hydrochloride. The biocompatibility, wettability, and the prediction of the free volume in the polymeric matrix were assessed using a human keratinocytes cell line, contact angle, and Positron Annihilation Lifetime Spectroscopy determinations, respectively. The morphology of the films obtained was confirmed by scanning electron microscopy, while the nail lacquers' bioadhesion to nails was determined by mechanical tests. Viscosity, in vitro release profiles, and antifungal activity were also assessed. This study demonstrated that PU-terbinafine-based nail lacquers have good keratinocyte compatibility, good wettability properties, and adequate free volume. They formed a homogenous film after application, with suitable adhesion to the nail plate. Furthermore, the antifungal test results demonstrated that the terbinafine released from the nail lacquer Formulation A PU 19 showed activity against dermatophytes, namely Trichophyton rubrum. Copyright © 2017 American Pharmacists Association®. Published by Elsevier Inc. All rights reserved.

  2. Influence of chemical treatment on the tensile properties of kenaf fiber reinforced thermoplastic polyurethane composite

    Directory of Open Access Journals (Sweden)

    Y. A. El-Shekeil

    2012-12-01

    Full Text Available In this study, the effect of polymeric Methylene Diphenyl Diisocyanate (pMDI chemical treatment on kenaf (Hibiscus cannabinus reinforced thermoplastic polyurethane (TPU/KF was examined using two different procedures. The first consisted of treating the fibers with 4% pMDI, and the second involved 2% NaOH + 4% pMDI. The composites were characterized according to their tensile properties, Fourier Transform Infrared Spectroscopy (FTIR and Scanning Electron Microscopy (SEM. The treatment of the composite with 4% pMDI did not significantly affect its tensile properties, but the treatment with 2% NaOH + 4% pMDI significantly increased the tensile properties of the composite (i.e., 30 and 42% increases in the tensile strength and modulus, respectively. FTIR also showed that treatment with 2% NaOH + 4% pMDI led to the strongest H-bonding. Additionally, the surface morphology of specimens after tensile fracture confirmed that the composite treated with 2% NaOH + 4% pMDI had the best adhesion and wettability.

  3. Microstructure, optimum pigment content and low infrared emissivity of polyurethane/Ag composite coatings

    International Nuclear Information System (INIS)

    Zhang, Weigang; Xu, Guoyue; Ding, Ruya; Qiao, Jialiang; Duan, Kaige

    2013-01-01

    Polyurethane (PU)/Ag composite coatings with low infrared emissivity were successfully prepared by using PU and flaky Ag powders as adhesives and pigments, respectively. The infrared emissivity and microstructure of as-prepared products were systematically investigated by infrared emissometer and scanning electron microscopy, respectively. Infrared emissivity measurement shows that the emissivity of the coatings approaches the lowest value of 0.082 at the wavelength of 8–14 µm when the Ag content is about 20 wt%. Microstructure observation shows that the coatings have similar one-dimensional photonic structural characteristics. According to the structural characteristics, a simulation method for optimum pigment content and the cause of low infrared emissivity of the coatings were successfully obtained and discussed by using the theories of one-dimensional photonic structure, respectively. The results indicate that the low infrared emissivity of PU/Ag composite coatings is derived from the similar one-dimensional photonic structure in the coatings, and the calculated optimum Ag content is in good agreement with the experimental value, which reveals that it is a practical simulation method for optimum pigment content of low infrared emissivity composite coatings

  4. Effect of temperature and strain rate on the compressive behaviour of supramolecular polyurethane

    Directory of Open Access Journals (Sweden)

    Tang Xuegang

    2015-01-01

    Full Text Available Supramolecular polyurethanes (SPUs possess thermoresponsive and thermoreversible properties, and those characteristics are highly desirable in both bulk commodity and value-added applications such as adhesives, shape-memory materials, healable coatings and lightweight, impact-resistant structures (e.g. protection for mobile electronics. A better understanding of the mechanical properties, especially the rate and temperature sensitivity, of these materials are required to assess their suitability for different applications. In this paper, a newly developed SPU with tuneable thermal properties was studied, and the response of this SPU to compressive loading over strain rates from 10−3 to 104 s−1 was presented. Furthermore, the effect of temperature on the mechanical response was also demonstrated. The sample was tested using an Instron mechanical testing machine for quasi-static loading, a home-made hydraulic system for moderate rates and a traditional split Hopkinson pressure bars (SHPBs for high strain rates. Results showed that the compression stress-strain behaviour was affected significantly by the thermoresponsive nature of SPU, but that, as expected for polymeric materials, the general trends of the temperature and the rate dependence mirror each other. However, this behaviour is more complicated than observed for many other polymeric materials, as a result of the richer range of transitions that influence the behaviour over the range of temperatures and strain rates tested.

  5. Robust hydrophobic polyurethane fibrous membranes with tunable porous structure for waterproof and breathable application

    Science.gov (United States)

    Gu, Jiatai; Gu, Haihong; Cao, Jin; Chen, Shaojie; Li, Ni; Xiong, Jie

    2018-05-01

    In this work, novel nanofibrous membranes with waterproof and breathable (W&B) performance were successfully fabricated by the combination of electrospinning and surface modification technology. This fibrous membranes consisted of polyurethane (PU), NaCl, and fluoroalkylsilane (FAS). Firstly, The fibrous construction and porous structure of fibrous membranes were regulated by tuning the NaCl concentrations in PU solutions. Then, the obtained PU/NaCl fibrous membranes were further modified with fluoroalkylsilane (FAS) to improve hydrophobic property. The synergistic effect of porous structure and hydrophobicity on waterproof and breathable performance was investigated. Furthermore, the mechanical property of fibrous membranes was deeply analysed on the basis of macromolecule orientation and adhesive structure. Benefiting from the optimized porous structure and hydrophobic modification, the resultant fibrous membranes exhibited excellent waterproof (hydrostatic pressure of 1261 Mbar), breathable (water vapor transmission (WVT) rate of 9.06 kg m-2 d-1 and air permeability of 4.8 mm s-1) performance, as well as high tensile strength (breakage stress of 10.4 MPa), suggesting a promising candidate for various applications, especially in protective clothing.

  6. New biobased high functionality polyols and their use in polyurethane coatings.

    Science.gov (United States)

    Pan, Xiao; Webster, Dean C

    2012-02-13

    High-functionality polyols for application in polyurethanes (PUs) were prepared by epoxide ring-opening reactions from epoxidized sucrose esters of soybean oil-epoxidized sucrose soyates-in which secondary hydroxyl groups were generated from epoxides on fatty acid chains. Ester polyols were prepared by using a base-catalyzed acid-epoxy reaction with carboxylic acids (e.g., acetic acid); ether polyols were prepared by using an acid-catalyzed alcohol-epoxy reaction with monoalcohols (e.g., methanol). The polyols were characterized by using gel permeation chromatography, FTIR spectroscopy, (1)H NMR spectroscopy, differential scanning calorimetry (DSC), and viscosity measurements. PU thermosets were prepared by using aliphatic polyisocyanates based on isophorone diisocyanate and hexamethylene diisocyanate. The properties of the PUs were studied by performing tensile testing, dynamic mechanical analysis, DSC, and thermogravimetric analysis. The properties of PU coatings on steel substrates were evaluated by using ASTM methods to determine coating hardness, adhesion, solvent resistance, and ductility. Compared to a soy triglyceride polyol, sucrose soyate polyols provide greater hardness and range of cross-link density to PU thermosets because of the unique structure of these macromolecules: well-defined compact structures with a rigid sucrose core coupled with high hydroxyl group functionality. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  7. Flexible thermoplastic composite of Polyvinyl Butyral (PVB and waste of rigid Polyurethane foam

    Directory of Open Access Journals (Sweden)

    Marilia Sônego

    2015-04-01

    Full Text Available This study reports the preparation and characterization of composites with recycled poly(vinyl butyral (PVB and residue of rigid polyurethane foam (PUr, with PUr contents of 20, 35 and 50 wt %, using an extruder equipped with a Maillefer single screw and injection molding. The components of the composites were thermally characterized using differential scanning calorimetry (DSC and thermogravimetry. The composites were evaluated by melt flow index (MFI, tensile and hardness mechanical tests and scanning electron microscopy (SEM. Tg determined by DSC of PVB sample (53 °C indicated the presence of plasticizer (Tg of pure PVB is 70 °C. MFI of the composites indicated a viscosity increase with the PUr content and, as the shear rate was held constant during injection molding, higher viscosities promoted higher shear stresses in the composites, thereby causing breaking or tearing of the PUr particles. The SEM micrographs showed low adhesion between PVB and PUr and the presence of voids, both inherent in the rigid foam and in the interphase PVB-PUr. The SEM micrographs also showed that PVB/PUr (50/50 composite exhibited the smallest particle size and a more homogeneous and compact structure with fewer voids in the interface. The stiffness of the composites increases with addition of the PUr particles, as evidenced in the mechanical tests.

  8. Magnetically-tunable rebound property for variable elastic devices made of magnetic elastomer and polyurethane foam

    Science.gov (United States)

    Oguro, Tsubasa; Endo, Hiroyuki; Kawai, Mika; Mitsumata, Tetsu

    2017-12-01

    A device consisting of a phase of magnetic elastomer, a phase of polyurethane foam (PUF), and permanent magnet was fabricated and the stress-strain curves for the two-phase magnetic elastomer were measured by a uniaxial compression measurement. A disk of magnetic elastomer was adhered on a disk of PUF by an adhesive agent. The PUF thickness was varied from 1 mm to 5 mm while the thickness of magnetic elastomers was constant at 5 mm. The stress at a strain of 0.15 for the two-phase magnetic elastomers was evaluated in the absence and in the presence of a magnetic field of 410 mT. The stress at 0 mT decreased remarkably with the PUF thickness due to the deformation of the PUF phase. On the other hand, the stress at 410 mT slightly decreased with the thickness; however, it kept high values even at high thickness. When the PUF thickness was 5 mm, the maximum stress increment with 45 times to the off-field stress was observed. An experiment using ping-pong balls demonstrated that the coefficient of restitution for the two-phase magnetic elastomers can be dramatically altered by the magnetic field.

  9. Switchable bio-inspired adhesives

    Science.gov (United States)

    Kroner, Elmar

    2015-03-01

    Geckos have astonishing climbing abilities. They can adhere to almost any surface and can run on walls and even stick to ceilings. The extraordinary adhesion performance is caused by a combination of a complex surface pattern on their toes and the biomechanics of its movement. These biological dry adhesives have been intensely investigated during recent years because of the unique combination of adhesive properties. They provide high adhesion, allow for easy detachment, can be removed residue-free, and have self-cleaning properties. Many aspects have been successfully mimicked, leading to artificial, bio-inspired, patterned dry adhesives, and were addressed and in some aspects they even outperform the adhesion capabilities of geckos. However, designing artificial patterned adhesion systems with switchable adhesion remains a big challenge; the gecko's adhesion system is based on a complex hierarchical surface structure and on advanced biomechanics, which are both difficult to mimic. In this paper, two approaches are presented to achieve switchable adhesion. The first approach is based on a patterned polydimethylsiloxane (PDMS) polymer, where adhesion can be switched on and off by applying a low and a high compressive preload. The switch in adhesion is caused by a reversible mechanical instability of the adhesive silicone structures. The second approach is based on a composite material consisting of a Nickel- Titanium (NiTi) shape memory alloy and a patterned adhesive PDMS layer. The NiTi alloy is trained to change its surface topography as a function of temperature, which results in a change of the contact area and of alignment of the adhesive pattern towards a substrate, leading to switchable adhesion. These examples show that the unique properties of bio-inspired adhesives can be greatly improved by new concepts such as mechanical instability or by the use of active materials which react to external stimuli.

  10. Synthesis and characterization of nanocomposites based on polyurethane in aqueous dispersions with non-modified hydrophilic clays; Sintese e caracterizacao de nanocompositos a base de poliuretanos em dispersoes aquosas com argilas hidrofilicas nao-modificadas

    Energy Technology Data Exchange (ETDEWEB)

    Miranda, G.S.; Delpechi, M.C.; Santo, W.L.E., E-mail: mcd@uerj.b [Universidade do Estado do Rio de Janeiro (UERJ), RJ (Brazil)

    2010-07-01

    Several studies involving the formation of polyurethane nanocomposites employing clays of montmorillonite modified. This involves the presence of quaternary ammonium salts, the cation exchange needed to increase the interlayer space of clays that incorporate more than one step to the process, generates a higher cost. In this paper the synthesis of nanocomposite polyurethanes dispersed in water allowed not only the production of materials less harmful to the environment, but also the incorporation of hydrophilic clays, calcium and sodium in nature, without any modifications. Dispersions produced from 0.5, 1.0 and 2.5% clay (on the mass of prepolymer) were characterized in terms of total solids content, the films obtained by casting were evaluated for adhesiveness, diffraction X-rays, scanning electron microscopy. Most systems showed intercalated and partially exfoliated structures. (author)

  11. Comparison between computed tomography with oral oil-based contrast and laparotomy for gastric cancer staging

    International Nuclear Information System (INIS)

    Marco, S. F.; Garcia-Vila, J. H.; Cervera, J.; Gomez, R.; Piqueras, R. M.; Perona, I.; Escrig, J.; Salvador, J. L.

    2000-01-01

    To compare the utility of conventional computed tomography (CT) with oral oil-based contrast with that of laparotomy in the preoperative staging of gastric cancer. We prospectively studied 41 patients diagnosed as having gastric adenocarcinoma according to the results of endoscopy and biopsy. Applying the TNM classification for gastric cancer staging, we compared the findings in CT associated with oral oil-based contrast and intraoperative staging with definitive postoperative pathological staging. Definitive pathological studies demonstrated that there were 7 stage T1-T2 lesions, 26 stage T3 and 8 stage T4. The assessment of lymph node involvement showed that 10 patients presented stage N0 and 31 stage N1-N3. Ten patients had metastases. The diagnostic reliability for tumor staging according to CT was 56% versus 80% for laparotomy. In the determination of nodal involvement CT had a diagnostic yield of 71% versus 6% for laparotomy. Metastatic disease was correctly diagnosed by CT in 83% of cases versus 88% by laparotomy. There were no statistically significant differences between CT with oral oil-based contrast and laparotomy for the staging of nodal involvement and metastases. However, the CT diagnosis was significantly more reliable than laparotomy for the determination of tumor infiltration. (Author) 21 refs

  12. Structure of nanoparticles in transformer oil-based magnetic fluids, anisotropy of acoustic attenuation

    International Nuclear Information System (INIS)

    Kúdelčík, Jozef; Bury, Peter; Kopčanský, Peter; Timko, Milan

    2015-01-01

    The anisotropy of acoustic attenuation in transformer oil-based magnetic fluids upon the external magnetic field was studied to discover the structure of nanoparticles. When a magnetic field is increased, the interaction between the external magnetic field and the magnetic moments of the nanoparticles leads to the aggregation of magnetic nanoparticles and following clusters formation. However, the temperature of magnetic fluids and the concentration of nanoparticles also have very important influence on the structural changes. The measurement of the dependence of the acoustic attenuation on the angle between the magnetic field direction and acoustic wave vector (anisotropy) can give the useful information about the structure of magnetic nanoparticles formations. In the present, the results of anisotropy measurements of the transformer oil-based magnetic fluids are described and using appropriate theory the basic parameters of clusters are calculated. On the basis of the performed calculations, the proportion of the acoustic wave energy used for excitation of the translational and rotational degrees of freedom was also established. - Highlights: • Nanoparticles formation in transformer oil-based magnetic fluids was investigated. • The anisotropy acoustic spectroscopy as the method of investigation was used. • The external conditions on the structure of magnetic fluids were studied. • The structure parameters using suitable theoretical model were determined

  13. The effect of nanoparticle surfactant polarization on trapping depth of vegetable insulating oil-based nanofluids

    Energy Technology Data Exchange (ETDEWEB)

    Li, Jian, E-mail: lijian@cqu.edu.cn; Du, Bin; Wang, Feipeng; Yao, Wei; Yao, Shuhan

    2016-02-05

    Nanoparticles can generate charge carrier trapping and reduce the velocity of streamer development in insulating oils ultimately leading to an enhancement of the breakdown voltage of insulating oils. Vegetable insulating oil-based nanofluids with three sizes of monodispersed Fe{sub 3}O{sub 4} nanoparticles were prepared and their trapping depths were measured by thermally stimulated method (TSC). It is found that the nanoparticle surfactant polarization can significantly influence the trapping depth of vegetable insulating oil-based nanofluids. A nanoparticle polarization model considering surfactant polarization was proposed to calculate the trapping depth of the nanofluids at different nanoparticle sizes and surfactant thicknesses. The results show the calculated values of the model are in a fairly good agreement with the experimental values. - Highlights: • Three different sized Fe{sub 3}O{sub 4} vegetable-oil based nanofluids was successfully prepared. • The trapping depth of the Fe{sub 3}O{sub 4} nanofluids was investigated. • A new model considering surfactant polarization was proposed to calculate the trapping depth of the nanofluids.

  14. Ivermectin disposition kinetics after subcutaneous and intramuscular administration of an oil-based formulation to cattle.

    Science.gov (United States)

    Lifschitz, A; Virkel, G; Pis, A; Imperiale, F; Sanchez, S; Alvarez, L; Kujanek, R; Lanusse, C

    1999-10-01

    Slight differences in formulation may change the plasma kinetics and ecto-endoparasiticide activity of endectocide compounds. This work reports on the disposition kinetics and plasma availability of ivermectin (IVM) after subcutaneous (SC) and intramuscular (IM) administration as an oil-based formulation to cattle. Parasite-free Aberdeen Angus calves (n = 24; 240-280 kg) were divided into three groups (n = 8) and treated (200 microg/kg) with either an IVM oil-based pharmaceutical preparation (IVM-TEST formulation) (Bayer Argentina S.A.) given by subcutaneous (Group A) and intramuscular (Group B) injections or the IVM-CONTROL (non-aqueous formulation) (Ivomec, MSD Agvet) subcutaneously administered (Group C). Blood samples were taken over 35 days post-treatment and the recovered plasma was extracted and analyzed by HPLC using fluorescence detection. IVM was detected in plasma between 12 h and 35 days post-administration of IVM-TEST (SC and IM injections) and IVM-CONTROL formulations. Prolonged IVM absorption half-life (p oil-based formulation examined in this trial, compared to the standard preparation, may positively impact on its strategic use in cattle.

  15. Structure of nanoparticles in transformer oil-based magnetic fluids, anisotropy of acoustic attenuation

    Energy Technology Data Exchange (ETDEWEB)

    Kúdelčík, Jozef, E-mail: kudelcik@fyzika.uniza.sk [Department of Physics, University of Žilina, Univerzitná 1, 010 01 Žilina (Slovakia); Bury, Peter [Department of Physics, University of Žilina, Univerzitná 1, 010 01 Žilina (Slovakia); Kopčanský, Peter; Timko, Milan [Department of Magnetism, IEP SAS, Watsonova 47, 040 01 Košice (Slovakia)

    2015-08-15

    The anisotropy of acoustic attenuation in transformer oil-based magnetic fluids upon the external magnetic field was studied to discover the structure of nanoparticles. When a magnetic field is increased, the interaction between the external magnetic field and the magnetic moments of the nanoparticles leads to the aggregation of magnetic nanoparticles and following clusters formation. However, the temperature of magnetic fluids and the concentration of nanoparticles also have very important influence on the structural changes. The measurement of the dependence of the acoustic attenuation on the angle between the magnetic field direction and acoustic wave vector (anisotropy) can give the useful information about the structure of magnetic nanoparticles formations. In the present, the results of anisotropy measurements of the transformer oil-based magnetic fluids are described and using appropriate theory the basic parameters of clusters are calculated. On the basis of the performed calculations, the proportion of the acoustic wave energy used for excitation of the translational and rotational degrees of freedom was also established. - Highlights: • Nanoparticles formation in transformer oil-based magnetic fluids was investigated. • The anisotropy acoustic spectroscopy as the method of investigation was used. • The external conditions on the structure of magnetic fluids were studied. • The structure parameters using suitable theoretical model were determined.

  16. Switchable Adhesion in Vacuum Using Bio-Inspired Dry Adhesives.

    Science.gov (United States)

    Purtov, Julia; Frensemeier, Mareike; Kroner, Elmar

    2015-11-04

    Suction based attachment systems for pick and place handling of fragile objects like glass plates or optical lenses are energy-consuming and noisy and fail at reduced air pressure, which is essential, e.g., in chemical and physical vapor deposition processes. Recently, an alternative approach toward reversible adhesion of sensitive objects based on bioinspired dry adhesive structures has emerged. There, the switching in adhesion is achieved by a reversible buckling of adhesive pillar structures. In this study, we demonstrate that these adhesives are capable of switching adhesion not only in ambient air conditions but also in vacuum. Our bioinspired patterned adhesive with an area of 1 cm(2) provided an adhesion force of 2.6 N ± 0.2 N in air, which was reduced to 1.9 N ± 0.2 N if measured in vacuum. Detachment was induced by buckling of the structures due to a high compressive preload and occurred, independent of air pressure, at approximately 0.9 N ± 0.1 N. The switch in adhesion was observed at a compressive preload between 5.6 and 6.0 N and was independent of air pressure. The difference between maximum adhesion force and adhesion force after buckling gives a reasonable window of operation for pick and place processes. High reversibility of the switching behavior is shown over 50 cycles in air and in vacuum, making the bioinspired switchable adhesive applicable for handling operations of fragile objects.

  17. Isolation and characterization of a bacterium which utilizes polyester polyurethane as a sole carbon and nitrogen source.

    Science.gov (United States)

    Nakajima-Kambe, T; Onuma, F; Kimpara, N; Nakahara, T

    1995-06-01

    Various soil samples were screened for the presence of microorganisms which have the ability to degrade polyurethane compounds. Two strains with good polyurethane degrading activity were isolated. The more active strain was tentatively identified as Comamonas acidovorans. This strain could utilize polyester-type polyurethanes but not the polyether-type polyurethanes as sole carbon and nitrogen sources. Adipic acid and diethylene glycol were probably the main degradation products when polyurethane was supplied as a sole carbon and nitrogen source. When ammonium nitrate was used as nitrogen source, only diethylene glycol was detected after growth on polyurethane.

  18. an Adhesive Patch

    Directory of Open Access Journals (Sweden)

    S. Mojtaba Taghizadeh

    2013-01-01

    Full Text Available Drug-in-adhesive transdermal drug delivery systems  TDDSs containing stimulants, termed as energetic substances, such as caffeine and pantothenic acid, were studied. Caffeine is a white crystalline substance and a stimulant to central nervous system. In humans, caffeine acts as a central nervous system stimulant, temporarily warding off drowsiness and restoring alertness. Pantothenic acid, also recognized as vitamin B5, is a water-soluble vitamin. For many animals, pantothenic acid is an essential nutrient. Animals require pantothenic acid to synthesize and metabolize proteins, carbohydrates and fats. For this purpose caffeine and pantothenic acid were  used  as  drug  components with  6.32%  and  1.12%  loadings,  in  different functional and non-functional acrylic pressure sensitive adhesives (PSAs of 52.89%, respectively. Ethylene glycol as a chemical enhancer was used in all TDDSs with 39.67%. The effect of PSAs  type on  in vitro  release and adhesion properties  (peel strength and tack values from drug delivery devices were evaluated. It was found that TDDS containing -COOH functional PSA showed  the  lowest steady state fux. The adhesion properties of the samples were improved by addition of functional acrylic PSA in formulations.

  19. Leukocyte adhesion deficiencies

    NARCIS (Netherlands)

    van de Vijver, Edith; van den Berg, Timo K.; Kuijpers, Taco W.

    2013-01-01

    During inflammation, leukocytes play a key role in maintaining tissue homeostasis through elimination of pathogens and removal of damaged tissue. Leukocytes migrate to the site of inflammation by crawling over and through the blood vessel wall, into the tissue. Leukocyte adhesion deficiencies (ie,

  20. Adhesive tape exfoliation

    DEFF Research Database (Denmark)

    Bohr, Jakob

    2015-01-01

    Single-crystal graphite can be cleaved by the use of an adhesive tape. This was also the initial route for obtaining graphene, a one-layer thick graphite slab. In this letter a few simple and fun considerations are presented in an attempt to shed some light on why this procedure is successful...

  1. Wood Composite Adhesives

    Science.gov (United States)

    Gomez-Bueso, Jose; Haupt, Robert

    The global environment, in which phenolic resins are being used for wood composite manufacture, has changed significantly during the last decade. This chapter reviews trends that are driving the use and consumption of phenolic resins around the world. The review begins with recent data on volume usage and regional trends, followed by an analysis of factors affecting global markets. In a section on environmental factors, the impact of recent formaldehyde emission regulations is discussed. The section on economics introduces wood composite production as it relates to the available adhesive systems, with special emphasis on the technical requirement to improve phenolic reactivity. Advances in composite process technology are introduced, especially in regard to the increased demands the improvements place upon adhesive system performance. The specific requirements for the various wood composite families are considered in the context of adhesive performance needs. The results of research into current chemistries are discussed, with a review of recent findings regarding the mechanisms of phenolic condensation and acceleration. Also, the work regarding alternate natural materials, such as carbohydrates, lignins, tannins, and proteinaceous materials, is presented. Finally, new developments in alternative adhesive technologies are reported.

  2. Nerve regeneration using tubular scaffolds from biodegradable polyurethane.

    Science.gov (United States)

    Hausner, T; Schmidhammer, R; Zandieh, S; Hopf, R; Schultz, A; Gogolewski, S; Hertz, H; Redl, H

    2007-01-01

    In severe nerve lesion, nerve defects and in brachial plexus reconstruction, autologous nerve grafting is the golden standard. Although, nerve grafting technique is the best available approach a major disadvantages exists: there is a limited source of autologous nerve grafts. This study presents data on the use of tubular scaffolds with uniaxial pore orientation from experimental biodegradable polyurethanes coated with fibrin sealant to regenerate a 8 mm resected segment of rat sciatic nerve. Tubular scaffolds: prepared by extrusion of the polymer solution in DMF into water coagulation bath. The polymer used for the preparation of tubular scaffolds was a biodegradable polyurethane based on hexamethylene diisocyanate, poly(epsilon-caprolactone) and dianhydro-D-sorbitol. EXPERIMENTAL MODEL: Eighteen Sprague Dawley rats underwent mid-thigh sciatic nerve transection and were randomly assigned to two experimental groups with immediate repair: (1) tubular scaffold, (2) 180 degrees rotated sciatic nerve segment (control). Serial functional measurements (toe spread test, placing tests) were performed weekly from 3rd to 12th week after nerve repair. On week 12, electrophysiological assessment was performed. Sciatic nerve and scaffold/nerve grafts were harvested for histomorphometric analysis. Collagenic connective tissue, Schwann cells and axons were evaluated in the proximal nerve stump, the scaffold/nerve graft and the distal nerve stump. The implants have uniaxially-oriented pore structure with a pore size in the range of 2 micorm (the pore wall) and 75 x 700 microm (elongated pores in the implant lumen). The skin of the tubular implants was nonporous. Animals which underwent repair with tubular scaffolds of biodegradable polyurethanes coated with diluted fibrin sealant had no significant functional differences compared with the nerve graft group. Control group resulted in a trend-wise better electrophysiological recovery but did not show statistically significant

  3. Development and characterization of amorphous acrylate networks for use as switchable adhesives inspired from shapememory behavior

    Science.gov (United States)

    Lakhera, Nishant

    Several types of insects and animals such as spiders and geckos are inherently able to climb along vertical walls and ceilings. This remarkable switchable adhesive behavior has been attributed to the fibrillar structures on their feet, with size ranging from few nanometers to a few micrometers depending on the species. Several studies have attempted to create synthetic micro-patterned surfaces trying to imitate this adhesive behavior seen in nature. The experimental procedures are scattered, with sole purpose of trying to increase adhesion, thereby making direct comparison between studies very difficult. There is a lack of fundamental understanding on adhesion of patterned surfaces. The influence of critical parameters like material modulus, glass transition temperature, viscoelastic effects, temperature and water absorption on adhesion is not fully explored and characterized. These parameters are expected to have a decisive influence on adhesion behavior of the polymer. Previous studies have utilized conventional "off-the-shelf" materials like epoxy, polyurethanes etc. It is however, impossible to change the material modulus, glass transition temperature etc. of these polymer systems without changing the base constituents itself, thereby explaining the gaps in the current research landscape. The purpose of this study was to use acrylate shape-memory polymers (SMPs) for their ability to be tailored to specific mechanical properties by control of polymer chemistry, without changing the base constituents. Polymer networks with tailorable glass transition, material modulus, water absorption etc. were developed and adhesion studies were performed to investigate the influence of temperature, viscoelastic effects, material modulus on the adhesion behavior of flat acrylate polymer surfaces. The knowledge base gained from these studies was utilized to better understand the fundamental mechanisms associated with adhesion behavior of patterned acrylate surfaces. Thermally

  4. Extraction of uranium from aqueous solution by phosphonic acid-imbedded polyurethane foam

    International Nuclear Information System (INIS)

    Katragadda, S.; Gesser, H.D.; Chow, A.

    1997-01-01

    Phenylphosphonic acid was imbedded into the matrix of the polyurethane foam during the fabrication process of the polymer. The extraction of uranium by phosphonic acid-imbedded polyurethane foam and blank polyurethane (i.e., foam without phosphonic acid functional groups) was investigated. Phosphonic acid-imbedded foam showed superior extractability of uranium from solutions with pH = 7.0 ± 1.5 over a wide range of temperatures. (author)

  5. Bio-Based Polyurethane Containing Isosorbide for Use in Composites and Coatings

    Science.gov (United States)

    2015-04-01

    ARL-TR-7259 ● APR 2015 US Army Research Laboratory Bio-Based Polyurethane Containing Isosorbide for Use in Composites and...copyright notation hereon. ARL-TR-7259 ● APR 2015 US Army Research Laboratory Bio-Based Polyurethane Containing Isosorbide for Use...4. TITLE AND SUBTITLE Bio-Based Polyurethane Containing Isosorbide for Use in Composites and Coatings 5a. CONTRACT NUMBER 5b. GRANT NUMBER 5c

  6. Use of Polyurethane Coating to Prevent Corrosion in Oil and Gas Pipelines Transfer

    OpenAIRE

    Amir Samimi

    2012-01-01

    Corrosion is one of the major problems in the oil and gas industry is one that automatically allocates huge sums annually. Polyurethane is a thermoses polymer with various applications. Using form this polymer has spread for military applications by Otto Bayer in 1930. In one general look polyurethane is product of Iso Syanate and ploy with each other, So that: Iso + ploy = polyurethane. Spend large cost for application and launching oil and gas transitions, has cleared the necessity protecti...

  7. Contact compliance effects in the frictional response of bioinspired fibrillar adhesives

    Science.gov (United States)

    Piccardo, Marco; Chateauminois, Antoine; Fretigny, Christian; Pugno, Nicola M.; Sitti, Metin

    2013-01-01

    The shear failure and friction mechanisms of bioinspired adhesives consisting of elastomer arrays of microfibres terminated by mushroom-shaped tips are investigated in contact with a rigid lens. In order to reveal the interplay between the vertical and lateral loading directions, experiments are carried out using a custom friction set-up in which normal stiffness can be made either high or low when compared with the stiffness of the contact between the fibrillar adhesive and the lens. Using in situ contact imaging, the shear failure of the adhesive is found to involve two successive mechanisms: (i) cavitation and peeling at the contact interface between the mushroom-shaped fibre tip endings and the lens; and (ii) side re-adhesion of the fibre's stem to the lens. The extent of these mechanisms and their implications regarding static friction forces is found to depend on the crosstalk between the normal and lateral loading directions that can result in contact instabilities associated with fibre buckling. In addition, the effects of the viscoelastic behaviour of the polyurethane material on the rate dependence of the shear response of the adhesive are accounted for. PMID:23554349

  8. Deep UV patterning of acrylic masters for molding biomimetic dry adhesives

    International Nuclear Information System (INIS)

    Sameoto, D; Menon, C

    2010-01-01

    We present a novel fabrication method for the production of biomimetic dry adhesives that allows enormous variation in fiber shapes and sizes. The technology is based on deep-UV patterning of commercial acrylic with semi-collimated light available from germicidal lamps, and combined careful processing conditions, material selection and novel developer choices to produce relatively high-aspect-ratio fibers with overhanging caps on large areas. These acrylic fibers are used as a master mold for subsequent silicone rubber negative mold casting. Because the bulk acrylic demonstrates little inherent adhesion to silicone rubbers, the master molds created in this process do not require any surface treatments to achieve high-yield demolding of interlocked structures. Multiple polymers can be cast from silicone rubber negative molds and this process could be used to structure smart materials on areas over multiple square feet. Using direct photopatterning of acrylic allows many of the desired structures for biomimetic dry adhesives to be produced with relative ease compared to silicon-based molding processes, including angled fibers and hierarchical structures. Optimized fiber shapes for a variety of polymers can be produced using this process, and adhesion measurements on a well-characterized polyurethane, ST-1060, are used to determine the effect of fiber geometry on adhesion performance

  9. Adhesive bonding of wood materials

    Science.gov (United States)

    Charles B. Vick

    1999-01-01

    Adhesive bonding of wood components has played an essential role in the development and growth of the forest products industry and has been a key factor in the efficient utilization of our timber resource. The largest use of adhesives is in the construction industry. By far, the largest amounts of adhesives are used to manufacture building materials, such as plywood,...

  10. Influence of Surface Properties and Impact Conditions on Adhesion of Insect Residues

    Science.gov (United States)

    Wohl, Christopher J.; Smith, Joseph G.; Connell, John W.; Siochi, Emilie J.; Doss, Jereme R.; Shanahan, Michelle H.; Penner, Ronald K.

    2015-01-01

    Insect residues can cause premature transition to turbulent flow on laminar flow airfoils. Engineered surfaces that mitigate the adhesion of insect residues provide, therefore, a route to more efficient aerodynamics and reduced fuel burn rates. Areal coverage and heights of residues depend not only on surface properties, but also on impact conditions. We report high speed photography of fruit fly impacts at different angles of inclination on a rigid aluminum surface, optical microscopy and profilometry, and contact angle goniometry to support the design of engineered surfaces. For the polyurethane and epoxy coatings studied, some of which exhibited superhydrophobicity, it was determined that impact angle and surface compositions play critical roles in the efficacy of these surfaces to reduce insect residue adhesion.

  11. Effects of surface modification with hydroxyl terminated polydimethylsiloxane on the corrosion protection of polyurethane coating

    International Nuclear Information System (INIS)

    Jeon, Jae Hong; Shon, Min Young

    2014-01-01

    Polyurethane coating was designed to give a hydrophobic property on its surface by modifying it with hydroxyl terminated polydimethylsiloxane and then effects of surface hydrophobic tendency, water transport behavior and hence corrosion protectiveness of the modified polyurethane coating were examined using FT-IR/ATR spectroscopy, contact angle measurement and electrochemical impedance test. As results, the surface of polyurethane coating was changed from hydrophilic to hydrophobic property due primarily to a phase separation tendency between polyurethane and modifier by the modification. The phase separation tendency is more appreciable when modified by polydimethylsiloxane with higher content. Water transport behavior of the modified polyurethane coating decreased more in that with higher hydrophobic surface property. The decrease in the impedance modulus ⅠZⅠ at low frequency region in immersion test for polyurethane coatings was associated with the water transport behavior and surface hydrophobic properties of modified polyurethane coatings. The corrosion protectiveness of the modified polyurethane coated carbon steel generally increased with an increase in the modifier content, confirming that corrosion protectiveness of the modified polyurethane coating is well agreed with its water transport behavior

  12. Study on thermal properties of synthetic and bio-based polyurethane

    Directory of Open Access Journals (Sweden)

    Šercer Mladen

    2015-01-01

    Full Text Available Polymers that are created by the chemical polymerization of naturally occurring monomers are attracting considerable commercial interest in the last few years because of their non-toxicity, biodegradability and biocompatibility and use of feedstock that is renewable. The development of specialized lignin compounds, such as electrically conducting polymers, engineering plastics and polyurethane, is an area of highest interest and growth. The paper will present the comparison of the mechanical and thermal properties of conventional polyurethane and bio-based polyurethane, i.e. polyurethane based on polyols produced by liquefaction of waste wood biomass.

  13. Development of bacterially resistant polyurethane for coating medical devices

    International Nuclear Information System (INIS)

    Roohpour, Nima; Moshaverinia, Alireza; Wasikiewicz, Jaroslaw M; Paul, Deepen; Vadgama, Pankaj; Wilks, Mark; Millar, Michael

    2012-01-01

    Polyurethanes have been widely used in medicine for coating and packaging implantable and other medical devices. Polyether-urethanes, in particular, have superior mechanical properties and are biocompatible, but in common with other medical materials they are susceptible to microbial film formation. In this study, polyether-urethane was end-capped with silver lactate and silver sulfadiazine functional groups to produce a bacterially resistant polymer without sacrificing the useful mechanical properties of the polyether-polyurethane. The silver ions were covalently incorporated into the polymer during chain extension of the prepolymer. The functionalized polymers were structurally characterized by light scattering, electron microscopy, NMR, FTIR and Raman spectroscopy. Mechanical properties, hydrophilicity, in vitro stability and antibacterial action of polymers were also investigated. Results indicate that both silver salts were successfully incorporated into the polymer structure without significant effect on mechanical properties, whilst conferring acceptable bacterial resistance.

  14. Gamma radiation effect on sisal / polyurethane composites without coupling agents

    Directory of Open Access Journals (Sweden)

    Marina Cardoso Vasco

    Full Text Available Abstract Natural fibers and polyurethane based composites may present chemical bonding between the components of the polymer and the lignin of the fiber. The incidence of radiation can cause degradation of the polymeric material and alter its mechanical properties. The objective of this study was to obtain and characterize cold pressed composites from polyurethane derived from castor oil and sisal fibers, without coupling agents, through thermogravimetric and mechanical tests, before and after the incidence of 25 kGy dose of gamma radiation. Woven composites that were not irradiated had maximum values of 4.40 GPa for flexural elastic modulus on three point flexural test and dispersed fiber composite that were not irradiated had maximum values of 2.25 GPa. These materials are adequate for use in non-structural applications in radiotherapy and radiodiagnostic rooms.

  15. Gamma radiation effect on sisal / polyurethane composites without coupling agents

    Energy Technology Data Exchange (ETDEWEB)

    Vasco, Marina Cardoso; Claro Neto, Salvador; Nascimento, Eduardo Mauro; Azevedo, Elaine, E-mail: marina.mcv@gmail.com [University of Patras (Greece); Universidade de Sao Paulo (USP) Sao Carlos, SP (Brazil); Universidade Tecnologica Federal do Parana (UTFPR), Curitiba, PR (Brazil)

    2017-04-15

    Natural fibers and polyurethane based composites may present chemical bonding between the components of the polymer and the lignin of the fiber. The incidence of radiation can cause degradation of the polymeric material and alter its mechanical properties. The objective of this study was to obtain and characterize cold pressed composites from polyurethane derived from castor oil and sisal fibers, without coupling agents, through thermogravimetric and mechanical tests, before and after the incidence of 25 kGy dose of gamma radiation. Woven composites that were not irradiated had maximum values of 4.40 GPa for flexural elastic modulus on three point flexural test and dispersed fiber composite that were not irradiated had maximum values of 2.25 GPa. These materials are adequate for use in non-structural applications in radiotherapy and radiodiagnostic rooms. (author)

  16. Extraction kinetics of uranium (VI) with polyurethane foam

    International Nuclear Information System (INIS)

    Huang, Ting-Chia; Chen, Dong-Hwang; Huang, Shius-Dong; Huang, Ching-Tsven; Shieh, Mu-Chang.

    1993-01-01

    The extraction kinetics of uranium(VI) from aqueous nitrate solution with polyether-based polyurethane foam was investigated in a batch reactor with automatic squeezing. The extraction curves of uranium(VI) concentration in solution vs. extraction time exhibited a rather rapid exponential decay within the first few minutes, followed by a slower exponential decay during the remaining period. This phenomenon can be attributed to the presence of two-phase structure, hard segment domains and soft segment matrix in the polyurethane foam. A two-stage rate model expressed by a superposition of two exponential curves was proposed, according to which the experimental data were fitted by an optimization method. The extraction rate of uranium (VI) was also found to increase with increasing temperature, nitrate concentration, and hydration of the cation of nitrate salt. (author)

  17. The small angle neutron scattering study on the segmented polyurethane

    International Nuclear Information System (INIS)

    Sudirman; Gunawan; Prasetyo, S.M.; Karo Karo, A.; Lahagu, I.M.; Darwinto, Tri

    1999-01-01

    The distance between hard segment (HS) and soft segment (SS) of segmented polyurethane have been determined using the Small Angle Neutron Scattering (SANS) technique. The segmented Polyurethanes (SPU) are linear multiblock copolymers, which include elastomer thermoplastic. SPU consist of hard segment and soft segment, each has tendency to make a group with similar type to form a domain. The soft segments used were polypropylene glycol (PPG) and 4,4 diphenylmethane diisocyanate (MDI), while l,4 butanediol (BD) was used as hard segment. The characteristic of SPU depends on its phase structure which is affected by several factors, such as type of chemical formula and the composition of the HS and SS, solvent as well as the synthesizing process. The samples used in this study were SPU56 and SPU68. Based on the appearance of SANS profile, it was obtained that domain distances are 12.32 nm for the SPU56 and 19 nm for the SPU68. (author)

  18. Glycolysis of flexible polyurethane foam in recycling of car seats

    Czech Academy of Sciences Publication Activity Database

    Beneš, Hynek; Rösner, J.; Holler, Petr; Synková, Hana; Kotek, Jiří; Horák, Zdeněk

    2007-01-01

    Roč. 18, č. 2 (2007), s. 149-156 ISSN 1042-7147. [International Conference on Polymeric Materials in Automotive , Slovak Rubber Conference /17./. Bratislava, 10.5.2005-12.5.2005] R&D Projects: GA MŽP SL/7/26/05 Institutional research plan: CEZ:AV0Z40500505 Keywords : polyurethanes * foams * recycling Subject RIV: CD - Macromolecular Chemistry Impact factor: 1.504, year: 2007

  19. Improved Lignin Polyurethane Properties with Lewis Acid Treatment

    OpenAIRE

    Chung, Hoyong; Washburn, Newell R.

    2012-01-01

    Chemical modification strategies to improve the mechanical properties of lignin-based polyurethanes are presented. We hypothesized that treatment of lignin with Lewis acids would increase the concentration of hydroxyl groups available to react with diisocyanate monomers. Under the conditions used, hydrogen bromide-catalyzed modification resulted in a 28% increase in hydroxyl group content. Associated increases in hydrophilicity of solvent-cast thin films were also recorded as evidenced by ...

  20. Preparation and characterization of polyurethane - Fe powder composites

    Czech Academy of Sciences Publication Activity Database

    Špírková, Milena; Bureš, R.; Fáberová, M.; Trchová, Miroslava; Strachota, Adam; Kaprálková, Ludmila

    2011-01-01

    Roč. 11, 3/4 (2011), s. 290-299 ISSN 1335-8987 R&D Projects: GA ČR GAP108/10/0195 Institutional research plan: CEZ:AV0Z40500505 Keywords : polyurethanes * polybutadiene diol * Fe powder Subject RIV: CD - Macromolecular Chemistry http://www.imr.saske.sk/pmp/issue/3-4-2011/PMP_Vol11_No3-4_p_290-299.pdf

  1. The effects of using immobilizer made of the polyurethane foam

    International Nuclear Information System (INIS)

    Kim, Yong Hwan; Chung, Sang Hwa; Kim, Hwa Young; Lim, Shin Taek; Oh, Sae Dong

    1992-01-01

    The immogilzer for control the patient movement during the radiation beam on was made of the polyurethane foam. The time consumption is abut 8 minutes for completely making the immobilizer. In this experimental study, the effects of using the individual immobilizer have shown that the patients have had always a same position with comfortable and high reproducibilities. Furthermore, it has shown the time for patient setup was decreased by using the individual patient immobilizer.

  2. Polyurethane Nanofiber Membranes for Waste Water Treatment by Membrane Distillation

    OpenAIRE

    Jiříček, T.; Komárek, M.; Lederer, T.

    2017-01-01

    Self-sustained electrospun polyurethane nanofiber membranes were manufactured and tested on a direct-contact membrane distillation unit in an effort to find the optimum membrane thickness to maximize flux rate and minimize heat losses across the membrane. Also salt retention and flux at high salinities up to 100 g kg−1 were evaluated. Even though the complex structure of nanofiber layers has extreme specific surface and porosity, membrane performance was surprisingly predictable; the highest ...

  3. Polyester Polyols from Waste PET Bottles for Polyurethane Rigid Foams

    OpenAIRE

    Evtimova, Rozeta; Lozeva, Yordanka; Schmidt, Karl-Heinz; Wotzka, Michael; Wagner, Peter; Behrendt, Gerhard

    2003-01-01

    This paper describes a modified process to produce polyester polyols from PET wastes derived from the “bottle fraction residue” of the German Dual System (DSD) [11] employing a waste oligoester condensate of the polyesterification process with the addition of some glycols of longer chain and occasional modification with further dicarboxylic acids to produce polyester polyols of a broad range of properties which are further reacted to form polyurethane or polyisocyanurate rigid foams for insul...

  4. Modyfication of the Rigid Polyurethane-Polyisocyanurate Foams

    OpenAIRE

    Bogusław Czupryński; Joanna Liszkowska; Joanna Paciorek-Sadowska

    2014-01-01

    The effect of polyethylene glycol 1500 on physicomechanical properties of rigid polyurethane-polyisocyanurate (PUR-PIR) foams has been studied. It was found that application of polyethylene glycol 1500 for synthesis of foams in amount from 0% to 20% w/w had an effect on reduction of brittleness and softening point, while the greater the increase in compressive strength the higher its content in foam composition was. Wastes from production of these foams were ground and subjected to glycolysis...

  5. Effect of fiber loading on mechanical and morphological properties of cocoa pod husk fibers reinforced thermoplastic polyurethane composites

    International Nuclear Information System (INIS)

    El-Shekeil, Y.A.; Sapuan, S.M.; Algrafi, M.W.

    2014-01-01

    Highlights: • Increase in fiber loading increased tensile strength and modulus of the composites. • Tensile strain was decreasing with increase in fiber loading. • Flexural strength and modulus increased with increase in fiber content. • Impact strength was deteriorated with increasing fiber loading. • Morphology observations shown a good adhesion between fibers and matrix. - Abstract: In this study, cocoa (Theobroma cacao) pod husk (CPH) fiber reinforced thermoplastic polyurethane (TPU) was prepared by melt compounding method using Haake Polydrive R600 internal mixer. The composites were prepared with different fiber loading: 20%, 30% and 40% (by weight), with the optimum processing parameters: 190 °C, 11 min, and 40 rpm for temperature, time and speed, respectively. Five samples were cut from the composite sheet. Mean value was taken for each composite according to ASTM standards. Effect of fiber loading on mechanical (i.e. tensile, flexural properties and impact strength) and morphological properties was studied. TPU/CPH composites showed increase in tensile strength and modulus with increase in fiber loading, while tensile strain was decreasing with increase in fiber loading. The composite also showed increase in flexural strength and modulus with increase in fiber content. Impact strength was deteriorated with increase in fiber loading. Morphology observations using Scanning Electron Microscope (SEM) showed fiber/matrix good adhesion

  6. The important parameters of polyurethane's properties and preparation

    International Nuclear Information System (INIS)

    Rad, A.S.

    2009-01-01

    Polyurethane (PU) is a type of plastic rind is formed by reacting a polyol (a polymeric alcohol with more than. two reactive hydroxyl groups per molecule) with diisocyanates or polymeric isocyanate in the presence of suitable catalysts and additives. Variations in the number of substitutions and the spacing between and within branch chains produce PUs ranging from linear to branched and flexible to rigid. Linear PUs are used for the manufacture of fibers and molding. The structure of polyurethane can be medley containing 'hard' and 'soft' sect, which contribute to the harmony between rigid and elastomeric properties. The chemical composition and molecular weight distribution (MWD)- of the incorporated soft block influence the macroscopic properties of the resulting coating. In modifying the backbone structure of PU coatings it is necessary to consider the end use for the coating and the cost of modification: The properties of the modified PU coating, The resistance of the coating towards mechanical and The compatibility of the coating and the substrate over the temperature range of expected application and The between the benefits to be gained and the additional cost are the parameters that must be A surface functionalization of a synthetic polyurethane was carried out by using biofunctional moieties to obtain a material with the appropriate mechanical properties and processing conditions. (author)

  7. Study on polyurethane foamed concrete for use in structural applications

    Directory of Open Access Journals (Sweden)

    Iman Kattoof Harith

    2018-06-01

    Full Text Available Recently, foamed concrete is being widely used in civil construction and building, because of its high fluidity and settlement, low self-weight and low thermal conductivity. However, it has some major setbacks such as low strength and increased shrinkage at later ages. The strength gain of concrete depends upon several variables; one of these is the curing conditions. This work aims to study the potential production of foamed concrete as a sustainable structural material by varying the curing methods. For this purpose, sample cubes, cylinders and prisms were prepared to find the compressive strength, modulus of elasticity and drying shrinkage at different ages. Samples of the polyurethane foamed concrete cured under four different curing regimes (water, moisture, sealing by membrane-forming curing compound and air curing. At the end of the study, polyurethane foamed concrete used for this study has shown the potential for use in structural applications. Also, the results show that the samples cured by moisture have the highest compressive strength at all ages. Keywords: Polyurethane foamed concrete, Curing conditions, Fly ash, Compressive strength, Static modulus of elasticity drying shrinkage

  8. Chemical and Enzymatic Hydrolysis of Polyurethane/Polylactide Blends

    Directory of Open Access Journals (Sweden)

    Joanna Brzeska

    2015-01-01

    Full Text Available Polyether-esterurethanes containing synthetic poly[(R,S-3-hydroxybutyrate] (R,S-PHB and polyoxytetramethylenediol in soft segments and polyesterurethanes with poly(ε-caprolactone and poly[(R,S-3-hydroxybutyrate] were blended with poly([D,L]-lactide (PLA. The products were tested in terms of their oil and water absorption. Oil sorption tests of polyether-esterurethane revealed their higher response in comparison to polyesterurethanes. Blending of polyether-esterurethanes with PLA caused the increase of oil sorption. The highest water sorption was observed for blends of polyether-esterurethane, obtained with 10% of R,S-PHB in soft segments. The samples mass of polyurethanes and their blends were almost not changed after incubation in phosphate buffer and trypsin and lipase solutions. Nevertheless the molecular weight of polymers was significantly reduced after degradation. It was especially visible in case of incubation of samples in phosphate buffer what suggested the chemical hydrolysis of polymer chains. The changes of surface of polyurethanes and their blends, after incubation in both enzymatic solutions, indicated on enzymatic degradation, which had been started despite the lack of mass lost. Polyurethanes and their blends, contained more R,S-PHB in soft segments, were degraded faster.

  9. A multilayered polyurethane foam technique for skin graft immobilization.

    Science.gov (United States)

    Nakamura, Motoki; Ito, Erika; Kato, Hiroshi; Watanabe, Shoichi; Morita, Akimichi

    2012-02-01

    Several techniques are applicable for skin graft immobilization. Although the sponge dressing is a popular technique, pressure failure near the center of the graft is a weakness of the technique that can result in engraftment failure. To evaluate the efficacy of a new skin graft immobilization technique using multilayered polyurethane foam in vivo and in vitro. Twenty-six patients underwent a full-thickness skin graft. Multiple layers of a hydrocellular polyurethane foam dressing were used for skin graft immobilization. In addition, we created an in vitro skin graft model that allowed us to estimate immobilization pressure at the center and edges of skin grafts of various sizes. Overall mean graft survival was 88.9%. In the head and neck region (19 patients), mean graft survival was 93.6%. Based on the in vitro outcomes, this technique supplies effective pressure (skin graft. This multilayered polyurethane foam dressing is simple, safe, and effective for skin graft immobilization. © 2011 by the American Society for Dermatologic Surgery, Inc. Published by Wiley Periodicals, Inc.

  10. (Biodegradable Ionomeric Polyurethanes Based on Xanthan: Synthesis, Properties, and Structure

    Directory of Open Access Journals (Sweden)

    T. V. Travinskaya

    2017-01-01

    Full Text Available New (biodegradable environmentally friendly film-forming ionomeric polyurethanes (IPU based on renewable biotechnological polysaccharide xanthan (Xa have been obtained. The influence of the component composition on the colloidal-chemical and physic-mechanical properties of IPU/Xa and based films, as well as the change of their properties under the influence of environmental factors, have been studied. The results of IR-, PMS-, DMA-, and X-ray scattering study indicate that incorporation of Xa into the polyurethane chain initiates the formation of a new polymer structure different from the structure of the pure IPU (matrix: an amorphous polymer-polymer microdomain has occurred as a result of the chemical interaction of Xa and IPU. It predetermines the degradation of the IPU/Xa films as a whole, unlike the mixed polymer systems, and plays a key role in the improvement of material performance. The results of acid, alkaline hydrolysis, and incubation into the soil indicate the increase of the intensity of degradation processes occurring in the IPU/Xa in comparison with the pure IPU. It has been shown that the introduction of Xa not only imparts the biodegradability property to polyurethane, but also improves the mechanical properties.

  11. Microencapsulation of 2-octylcyanoacrylate tissue adhesive for self-healing acrylic bone cement.

    Science.gov (United States)

    Brochu, Alice B W; Chyan, William J; Reichert, William M

    2012-10-01

    Here, we report the first phase of developing self-healing acrylic bone cement: the preparation and characterization of polyurethane (PUR) microcapsules containing a medical cyanoacrylate tissue adhesive. Capsules were prepared by interfacial polymerization of a toluene-2,4-diisocyanate-based polyurethane prepolymer with 1,4-butanediol to encapsulate 2-octylcyanoacrylate (OCA). Various capsule characteristics, including: resultant morphology, average size and size distribution, shell thickness, content and reactivity of encapsulated agent, and shelf life are investigated and their reliance on solvent type and amount, surfactant type and amount, temperature, pH, agitation rate, reaction time, and mode of addition of the oil phase to the aqueous phase are presented. Capsules had average diameters ranging from 74 to 222 μm and average shell thicknesses ranging from 1.5 to 6 μm. The capsule content was determined via thermogravimetric analysis and subsequent analysis of the capsules following up to 8 weeks storage revealed minimal loss of core contents. Mechanical testing of OCA-containing capsules showed individual capsules withstood compressive forces up to a few tenths of Newtons, and the contents released from crushed capsules generated tensile adhesive forces of a few Newtons. Capsules were successfully mixed into the poly(methyl methacrylate) bone cement, surviving the mixing process, exposure to methyl methacrylate monomer, and the resulting exothermic matrix curing. Copyright © 2012 Wiley Periodicals, Inc.

  12. Syndecans and cell adhesion

    DEFF Research Database (Denmark)

    Couchman, J R; Chen, L; Woods, A

    2001-01-01

    Now that transmembrane signaling through primary cell-matrix receptors, integrins, is being elucidated, attention is turning to how integrin-ligand interactions can be modulated. Syndecans are transmembrane proteoglycans implicated as coreceptors in a variety of physiological processes, including...... cell adhesion, migration, response to growth factors, development, and tumorigenesis. This review will describe this family of proteoglycans in terms of their structures and functions and their signaling in conjunction with integrins, and indicate areas for future research....

  13. Using the transformer oil-based nanofluid for cooling of power distribution transformer

    OpenAIRE

    Mushtaq Ismael Hasan

    2017-01-01

    Thermal behavior of electrical distribution transformer has been numerically studied with the effect of surrounding air temperature. 250 KVA distribution transformer is chosen as a study model and studied in temperature range cover the weather conditions of hot places. Transformer oil-based nanofluids were used as a cooling medium instead of pure transformer oil. Four types of solid particles (Cu, Al2O3, TiO2 and SiC) were used to compose nanofluids with volume fractions (1%, 3%, 5%, 7%, and ...

  14. Microwave Synthesis and Characterization of Waste Soybean Oil-Based Gemini Imidazolinium Surfactants with Carbonate Linkage

    Science.gov (United States)

    Tripathy, Divya Bajpai; Mishra, Anuradha

    Gemini surfactants are presently gaining attention due to their unusual self-assembling characteristics and incomparable interfacial activity. Current research work involves the cost-effective microwave (MW) synthesis of waste soybean oil-based gemini imidazolinium surfactants (GIS) having a carbonate linkage in its spacer moiety. Structural characterizations of the materials have been done using FT-IR, 1H-NMR and 13C-NMR. Using indigenous and natural material as base and MW as energy source for synthesizing the GIS with easily degradable chemical moiety make them to be labeled as green surfactants.

  15. The study of the curing of the polyurethane coating by method of IR spectroscopy

    Directory of Open Access Journals (Sweden)

    N. A. Korshunova

    2016-12-01

    Full Text Available The results of the study of the curing process of polyurethane compositions with participation of two different catalysts by the method of IR spectroscopy are given. The time dependences of curing of polyurethane coatings from concentrations of catalysts were determined, on the basis of which the most effective catalyst was selected.

  16. MORPHOLOGICAL CHANGES IN POLYURETHANE COATINGS ON EXPOSURE TO WATER. (R828081E01)

    Science.gov (United States)

    When a polyurethane self-priming coating on a sol-gel treated aluminum panel was immersed in dilute Harrison's solution, subsequent change of the polyurethane coating surface was inspected with atomic force microscopy (AFM) and scanning electron microscopy (SEM). After immersi...

  17. Electrospun Polyurethane Fibers for Absorption of Volatile Organic Compounds from Air

    NARCIS (Netherlands)

    Scholten, E.; Bromberg, L.; Rutledge, G.C.; Hatton, T.A.

    2011-01-01

    Electrospun polyurethane fibers for removal of volatile organic compounds (VOC) from air with rapid VOC absorption and desorption have been developed. Polyurethanes based on 4,4-methylenebis(phenylisocyanate) (MDI) and aliphatic isophorone diisocyanate as the hard segments and butanediol and

  18. Light Scattering of TiO2 Nanoparticles Embedded in Polyurethane

    DEFF Research Database (Denmark)

    Gudla, Visweswara Chakravarthy; Canulescu, Stela; Johansen, Villads Egede

    A new approach of enhancing light scattering in polyurethane polymer through the effect of TiO2 nanoparticles (NP) is explored. The TiO2 NP with sizes of 360 nm, 410 nm and 500 nm were dispersed in polyurethane polymer in concentrations ranging from 0.25 wt% up to 2 wt%. Reflectivity and UV-visible...

  19. The use of polyurethane foam as an antimicrobial dressing material in hand surgery

    Directory of Open Access Journals (Sweden)

    Nebil Yesiloglu

    2015-12-01

    Full Text Available Polyurethane foam is generally used in negative pressure-assisted wound closure therapy. It provides an antimicrobial environment around the wound, while reducing the rate of skin maceration. The authors used polyurethane foam in routine hand dressings after hand surgery operations that were performed for both congenital and acquired purposes. [Hand Microsurg 2015; 4(3.000: 91-92

  20. Polyurethanes irradiation by accelerated electrons: molecular and supramolecular evolution, incidence on the extractable and biomedical implications

    International Nuclear Information System (INIS)

    Guignot, C.

    2002-11-01

    Face to the development of radiosterilization and polymers medical devices it was wished to study the behavior of polyurethanes under accelerated electrons in oxidizing atmosphere. This study has been made to reveal the physico chemical and organisational modifications of polyurethanes for a medical use. (N.C.)

  1. Study of methane solubility in oil base used in oil base drilling fluid; Estudo da solubilidade de metano em base oleo utilizada em fluido de perfuracao base oleo

    Energy Technology Data Exchange (ETDEWEB)

    Silva, Carolina Teixeira da; Mariolani, Jose Ricardo Lenzi [Universidade Estadual de Campinas, SP (Brazil); Ribeiro, Paulo Roberto; Lomba, Rosana Fatima Teixeira; Bonet, Euclides Jose

    2004-07-01

    During drilling a well, it is necessary to prevent and control high pressurized zones because while drilling on those zones, could occur a kick if the formation pressure were higher then downhole pressure, allowing the entering of undesirables fluids from the formation to the wellbore. If the well is not controlled this kick could became a blowout, generating damages to the environment, to the equipment and the human life. When drilling using oil-based mud, the concern related to the well control would be higher due the gas solubility in the mud, which could make it hard to detect the kick, especially in deep and ultra deep waters. In this work we have studied the interaction between methane and organic liquids used in drilling fluids, and the measurement and analysis of the thermodynamic properties of those gas liquid mixtures. There have been measured parameters like the oil formation volume factor (FVF{sub o}), bubble pressure, solubility (Rs) and the density of the saturated liquid in function of methane mole fraction and temperature. The results have shown that the gas solubility, at downhole conditions and during kick circulation, is a factor very important to the safety during well drilling in deep and ultra deep waters. (author)

  2. Environmental implications of release of oil-based drilling fluids and oily cuttings into waters of the Canadian northwest Atlantic

    Energy Technology Data Exchange (ETDEWEB)

    Barchard, W.W.; Doe, K.G.; Mahon, S.D.; Moores, R.B.; Osborne, J.M.; Parker, W.R.

    1986-01-01

    In 1982, the Environmental Protection Service became aware that companies conducting petroleum exploration in the waters of eastern Canada would request permission to use and discharge oil-based drilling fluids and/or drill cuttings contaminated with oil-based drilling fluids. It was determined from an evaluation of North Sea data that aspects of the toxicity of oil-based drilling fluids should be evaluated using techniques applicable to Canadian marine conditions. Although it is unlikely that permission will be granted to dispose of whole oil-based muds into the ocean, whole mud formulations were tested as a close approximation to the mixture which would adhere to discharged drilling cuttings. Test organisms were exposed to whole muds as an approximation of the worst possible exposure regime. Static bioassays (96-hour) were conducted using threespine stickleback (Gasterosteus aculeatus). In general, high pH and the inclusion of certain emulsifiers seemed to contribute greatly to the lethality of the whole muds. Diesel oil-based muds were more acutely toxic than those formulated with alternate base oils which were virtually non-acutely toxic. Acute, sublethal and long-term studies were also conducted only on drill cuttings contaminated with alternate base oil muds. These more closely reflect proposed discharge strategies. Although 96-hour exposures resulted in no mortality, longer-term exposures (four to thirty-two days) resulted in significant behavioural changes and/or mortality to Macoma balthica, Strongylocentrotus droebachiensis, larval Homarus americanus and Nephthys caeca. The results suggest that use of alternate oil-based drilling fluids will have an effect on the marine environment intermediate between water-based muds and diesel oil-based muds. 73 refs., 6 figs., 18 tabs.

  3. Waste to Want: Polymer nanocomposites using nanoclays extracted from Oil based drilling mud waste

    International Nuclear Information System (INIS)

    Adegbotolu, Urenna V; Njuguna, James; Pollard, Pat; Yates, Kyari

    2014-01-01

    Due to the European Union (EU) waste frame work directive (WFD), legislations have been endorsed in EU member states such as UK for the Recycling of wastes with a vision to prevent and reduce landfilling of waste. Spent oil based drilling mud (drilling fluid) is a waste from the Oil and Gas industry with great potentials for recycling after appropriate clean-up and treatment processes. This research is the novel application of nanoclays extracted from spent oil based drilling mud (drilling fluid) clean-up as nanofiller in the manufacture of nanocomposite materials. Research and initial experiments have been undertaken which investigate the suitability of Polyamide 6 (PA6) as potential polymer of interest. SEM and EDAX were used to ascertain morphological and elemental characteristics of the nanofiller. ICPOES has been used to ascertain the metal concentration of the untreated nanofiller to be treated (by oil and heavy metal extraction) before the production of nanocomposite materials. The challenges faced and future works are also discussed

  4. Gas inflow in oil base fluids; Influxo de gas em fluidos a base de oleo

    Energy Technology Data Exchange (ETDEWEB)

    Lazaro, Welmar [PETROBRAS, Rio de Janeiro (Brazil). Dept. de Perfuracao. Div. de Fluidos de Perfuracao; Boas, Mario Barbosa V [PETROBRAS, Rio de Janeiro (Brazil). Centro de Pesquisas. Div. de Explotacao

    1990-12-31

    One of the major problems related to the use of oil base fluids is the dissolution of the natural gas in the fluid. This paper attempts initially at making a bibliographical review of all that was written on the subject of drilling fluids up to now. It also mentions some theoretical aspects regarding the process of gas dissolution in diesel oils, in order to produce an understanding of how the dissolution mechanism is processed. For a same increase in measured volume on the surface, the amount of gas incorporated into the fluid is significantly larger if the gas is dissolved in the oil phase than if it is emulsified in the fluid, as occurs when the fluid is water base. A rig team used to working with water-base fluids may be surprised with the fact that an increase of 20 bbl of fluid on the surface of a 5000 m well can mean the incorporation of about 1800 m{sup 3} of gas, if the fluid is oil-base and all the gas is in solution instead of the incorporation of 900 m{sup 3} if the fluid is water base. This paper has the goal of warning drilling engineers and technicians about this problem, as well as presenting charts and equations that allow for a more realistic evaluation of the amount of gas incorporated into oil fluids. (author) 16 refs., 7 figs., 2 tabs.

  5. Structure of transformer oil-based magnetic fluids studied using acoustic spectroscopy

    International Nuclear Information System (INIS)

    Kúdelčík, Jozef; Bury, Peter; Drga, Jozef; Kopčanský, Peter; Závišová, Vlasta; Timko, Milan

    2013-01-01

    The structural changes in transformer oil-based magnetic fluids upon the effect of an external magnetic field and temperature were studied by acoustic spectroscopy. The attenuation of acoustic wave was measured as a function of the magnetic field in the range of 0–300 mT and in the temperature range of 15–35 °C for various magnetic nanoparticles concentrations. The effect of anisotropy of the acoustic attenuation was determined, too. The both strong influence of the magnetic field on the acoustic attenuation and its hysteresis were observed. When a magnetic field is increased, the interaction between the external magnetic field and the magnetic moments of the nanoparticles occurs, leading to the aggregation of magnetic nanoparticles and following clusters formation. However, the temperature of magnetic fluids also has very important influence on the structural changes because of the mechanism of thermal motion that acts against the cluster creation. The observed influences of both magnetic field and temperature on the investigated magnetic fluid structure are discussed. - Highlights: ► Structural changes in transformer oil-based magnetic fluids were investigated. ► The acoustic spectroscopy as the method of investigation was used. ► The influence of magnetic field on the structural was studied. ► The influence of temperatures on the structures was investigated, too. ► The influence of external conditions on the structure of MF is interpreted.

  6. Performance of the mineral blended ester oil-based drilling fluid systems

    Energy Technology Data Exchange (ETDEWEB)

    Ismail, A.R.; Kamis, A.; Foo, K.S. [University Teknologi (Malaysia)

    2001-06-01

    A study was conducted in which the properties of ester oil-based drilling fluid systems were examined using a blended mixture of ester and synthetic mineral oil. Biodegradable invert emulsion ester-based fluids are preferred over mineral oil-based drilling fluids for environmental reasons, but they tend to cause alkaline hydrolysis resulting in solidification of the drilling fluid systems. The drilling fluid examined here consisted of Malaysian palm oil ester derivatives (methyl laureate ester or isopropyl laureate ester) blended with commercially available synthetic mineral oil. This mineral oil was added to reduce the problem of alkaline hydrolysis. This mixture, however, was found to be unstable and could not solve the problem at high temperature. The isopropyl laureate and mineral oil blended system was more stable towards the hydrolysis process up to 250 degrees F. In order to enhance the performance of an invert emulsion drilling fluid system, it was recommended that brine water content of the fluid system be lowered. 3 refs., 2 figs.

  7. III: Use of biomarkers as Risk Indicators in Environmental Risk Assessment of oil based discharges offshore.

    Science.gov (United States)

    Sanni, Steinar; Lyng, Emily; Pampanin, Daniela M

    2017-06-01

    Offshore oil and gas activities are required not to cause adverse environmental effects, and risk based management has been established to meet environmental standards. In some risk assessment schemes, Risk Indicators (RIs) are parameters to monitor the development of risk affecting factors. RIs have not yet been established in the Environmental Risk Assessment procedures for management of oil based discharges offshore. This paper evaluates the usefulness of biomarkers as RIs, based on their properties, existing laboratory biomarker data and assessment methods. Data shows several correlations between oil concentrations and biomarker responses, and assessment principles exist that qualify biomarkers for integration into risk procedures. Different ways that these existing biomarkers and methods can be applied as RIs in a probabilistic risk assessment system when linked with whole organism responses are discussed. This can be a useful approach to integrate biomarkers into probabilistic risk assessment related to oil based discharges, representing a potential supplement to information that biomarkers already provide about environmental impact and risk related to these kind of discharges. Copyright © 2016 Elsevier Ltd. All rights reserved.

  8. Comparison of Theories of Anisotropy in Transformer Oil-Based Magnetic Fluids

    Directory of Open Access Journals (Sweden)

    Jozef Kudelcik

    2013-01-01

    Full Text Available The external magnetic field in transformer oil-based magnetic fluids leads to the aggregation of magnetic nanoparticles and formation of clusters. These aggregations are the result of the interaction between the external magnetic field and the magnetic moments of the nanoparticles occurs. However, the temperature of magnetic fluids has also very important influence on the structural changes because the mechanism of thermal motion acts against the cluster creation. The acoustic spectroscopy was used to study the anisotropy of transformer oil-based magnetic fluids upon the effect of an external magnetic field and temperature. In present the anisotropy of the magnetic fluids can be described by two theories. Taketomi theory assumes the existence of spherical clusters. These clusters form long chains, aligned in a magnetic field direction. Shliomis in his theory supposed that only nanoparticles formed chains. A comparison of the experimental results with the predictions of the Taketomi theory allowed a determination of the cluster radius and the number density of the colloidal particles. The proportions of the acoustic wave energy used for excitation of the translational and rotational motion were determined.

  9. Structure of transformer oil-based magnetic fluids studied using acoustic spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Kudelcik, Jozef, E-mail: kudelcik@fyzika.uniza.sk [Department of Physics, University of Zilina, Univerzitna 1, 010 01 Zilina (Slovakia); Bury, Peter; Drga, Jozef [Department of Physics, University of Zilina, Univerzitna 1, 010 01 Zilina (Slovakia); Kopcansky, Peter; Zavisova, Vlasta; Timko, Milan [Department of Magnetism, IEP SAS, Watsonova 47, 040 01 Kosice (Slovakia)

    2013-01-15

    The structural changes in transformer oil-based magnetic fluids upon the effect of an external magnetic field and temperature were studied by acoustic spectroscopy. The attenuation of acoustic wave was measured as a function of the magnetic field in the range of 0-300 mT and in the temperature range of 15-35 Degree-Sign C for various magnetic nanoparticles concentrations. The effect of anisotropy of the acoustic attenuation was determined, too. The both strong influence of the magnetic field on the acoustic attenuation and its hysteresis were observed. When a magnetic field is increased, the interaction between the external magnetic field and the magnetic moments of the nanoparticles occurs, leading to the aggregation of magnetic nanoparticles and following clusters formation. However, the temperature of magnetic fluids also has very important influence on the structural changes because of the mechanism of thermal motion that acts against the cluster creation. The observed influences of both magnetic field and temperature on the investigated magnetic fluid structure are discussed. - Highlights: Black-Right-Pointing-Pointer Structural changes in transformer oil-based magnetic fluids were investigated. Black-Right-Pointing-Pointer The acoustic spectroscopy as the method of investigation was used. Black-Right-Pointing-Pointer The influence of magnetic field on the structural was studied. Black-Right-Pointing-Pointer The influence of temperatures on the structures was investigated, too. Black-Right-Pointing-Pointer The influence of external conditions on the structure of MF is interpreted.

  10. A Review on Properties, Opportunities, and Challenges of Transformer Oil-Based Nanofluids

    Directory of Open Access Journals (Sweden)

    Muhammad Rafiq

    2016-01-01

    Full Text Available The mineral oil or synthetic oil in conjunction with paper is mainly being applied as dielectric medium in many of the high voltage apparatus. However, the advent of high voltage levels such high voltage alternating current (HVAC and high voltage direct current (HVDC has prompted researchers to direct their focus onto an insulation system which can bear the rising high voltage levels. The modern insulating liquid material development is guided by various factors such as high electrical insulation requirements and other safety and economic considerations. Therefore transformer manufacturer companies have to design transformers with these new specific requirements. The transformer oil-based nanofluids with improved dielectric and thermal properties have the potential to replace mineral oil base products in the market place. They are favorable because they function more superior than mineral oil and they contribute definite insulating and thermal gains. This paper reviews recent status of nanofluids use as transformer oils. The nanofluids used as transformer oils are presented and their advantages are described in comparison with mineral oil. The multiple experimental works carried out by different researchers are described, providing an overview of the current research conducted on nanofluids. In addition scope and challenges being confronted in this area of research are clearly presented.

  11. Insight into the dielectric response of transformer oil-based nanofluids

    Directory of Open Access Journals (Sweden)

    Ming Dong

    2017-02-01

    Full Text Available The oil-based nanofluids with greater dielectric strength have attracted much attention as a crucial insulating materials in high-voltage oil-immersed power equipment. In fact, the different microstructures of the transformer oil-based nanofluids (TNFs would result in different dielectric properties. In this work, the broadband dielectric spectroscopy measurement was used to establish the linkage between the electric double layer (EDL and dielectric response properties of TNFs which was performed at 298K temperature and with frequency range from 10-2Hz∼106Hz. The modified Havriliak-Negami (HN model function was used to analyze the measured results. The results demonstrate that both the real and imaginary parts of dielectric spectra of two kinds of oil are composed of the conductivity and polarization process. Compared with pure oil, two polarization process could be observed for the TNFs, explained by the EDL structure reasonably. The introduction of the EDL structure provides an idea to account for the insulating strength improvement of TNFs for the first time.

  12. SPECIFIC FEATURES OF OLIGOMERIC PRODUCT SOLIDIFICATION FROM POLYURETHANE WASTES AND THEIR PRACTICAL APPLICATION

    Directory of Open Access Journals (Sweden)

    V. Belyatsky

    2012-01-01

    Full Text Available The paper considers a possibility to use secondary polyurethane obtained by  thermal depolymerization of wastes on the basis of cross-linked polyurethane (polyurethane adduct and isocyanate. An effect of density dependence of the obtained polyurethane samples on nature and quantity of solvent has been revealed and it is significantly observed while using low-boiling solvents. The influence of adduct/solidification agent ratio on mechanical hardness of the obtained samples has been studied in the paper. The paper shows that the most optimal ratio is within the following limits – from 7/1 to 10/1. Plasticizing effect of polyurethane adduct on bitumen materials has been also found in the paper.A conclusion has been made that there is a possibility of practical usage of composites in building and road-building materials. 

  13. Synthesis and optical properties of polyurethane foam modified with silver nanoparticles

    International Nuclear Information System (INIS)

    Apyari, V V; Volkov, P A; Dmitrienko, S G

    2012-01-01

    This paper for the first time describes peculiarities of synthesis of polyurethane foam modified with silver nanoparticles as a potential material for optical sensors in analytical chemistry. We found that the unique sorptional properties of polyurethane foam gave an opportunity to perform such a synthesis by two different approaches. The first one was based on sorption of previously synthesized in-solution nanoparticles by polyurethane foam, the second one consisted in preparation of nanoparticles directly in polyurethane foam matrix. This possibility is novel and interesting for practical use because the nanoparticles in polyurethane foam are capable of surface plasmon resonance. The influence of different factors during the synthesis was investigated and the optimal conditions were found. The samples prepared were characterized by diffuse reflectance spectroscopy and scanning electron microscopy. On the basis of the results obtained we first suggested that this material is attractive from the viewpoint of analytical chemistry as a convenient analytical form for determination of oxidants and reductants

  14. Reflectance spectroscopy from TiO2 particles embedded in polyurethane

    DEFF Research Database (Denmark)

    Gudla, Visweswara Chakravarthy; Canulescu, Stela; Johansen, Villads Egede

    2013-01-01

    This paper presents the results of a physical simulation carried out using TiO2-Polyurethane composite coating on bright aluminium surface to understand the light scattering effect for designing white surfaces. Polyurethane matrix is selected due to the matching refractive index (1.7) with Al2O3...... layer on anodized aluminium surfaces. Three different TiO2 particle distributions were dispersed in polyurethane and spin coated onto high gloss and caustic etched aluminium substrates. Reflectance spectra of TiO2-polyurethane films of various concentrations were analysed using an integrating sphere....... The results show that the TiO2-polyurethane coatings have a high diffuse reflectance as a result of multiple scattering from TiO2 particles. Diffuse reflectance spectra of TiO2 containing films vary weakly with particle concentration and reach a steady state value at a concentration of 0.75 wt.%. Using...

  15. Cylindrical multiwire two-coordinate chamber with foam-polyurethane supporting element

    International Nuclear Information System (INIS)

    Vakhtin, V.G.; Travkin, V.I.

    1988-01-01

    Construction and technology of producing the two-coordinate cylindrical chamber with foam-polyurethane supporting element are described. Use of foam-polyurethane permits to reduce the substance quantity at particle path up to 0.2 g/cm 2 . The supporting element represents a foam-polyurethane tube the outside diameter being 126 mm, the thickness - 6.5 mm and the length 600 mm. Special attention was paid to study of elastic properties of foam-polyurethane tubes and to the effect of the chamber working fluid vapors on the tube sizes. It is stated that after a sustained load (3750 N for 6 days) the tube shrinks by 1.25 %. The foam-polyurethane supporting element arranged in 50% argon + 33% methane + 17% methylane mixture didn't change its sizes in the limit of 0.05% for three weeks. The chamber operates under self-qquenching streamer conditions

  16. Studies on incorporation of exfoliated bentonitic clays in polyurethane foams for increasing flame retardancy

    International Nuclear Information System (INIS)

    Quagliano, J; García, Irma Gavilán

    2012-01-01

    In this contribution we report the results of studying the incorporation of exfoliated bentonitic clays into polyurethane foams. A suspension in water of a sodium bentonite from Argentine Patagonia was interchanged with cetyl trimethyl ammonium bromide (CTAB) for 4 h at 80°C, rendering an exfoliated clay, which is nanometric in only one dimension. This nanoclay, when dispersed in the polyurethane, resulted in the same fire retardancy rating (UL-94) than when polyurethane was treated with a commercial nanoclay. Scanning electron microscopy (SEM) at low augmentations of polyurethane samples treated with the synthethized nanoclay (2,5% w/w) showed no differences respect to untreated polyurethane, except for the irregularity of void edges.

  17. Experimental study of polyurethane foam reinforced soil used as a rock-like material

    Directory of Open Access Journals (Sweden)

    Eren Komurlu

    2015-10-01

    Full Text Available In this study, polyurethane foam type thermoset polymerizing, due to chemical reaction between its liquid ingredients, was tested as binder after solidifying and then a rock-like material mixing with a sandy silt type soil was prepared. The uniaxial compressive strengths (UCSs of polyurethane foam reinforced soil specimens were determined for different polyurethane ratios in the mixture. Additionally, a series of tests on slake durability, impact value, freezing–thawing resistance, and abrasion resistance of polyurethane reinforced soil (PRS mixture was conducted. The UCS values over 3 MPa were measured from the PRS specimens. The testing results showed that treated soil can economically become a desirable rock-like material in terms of slake durability and resistances against freezing–thawing, impact effect and abrasion. As another characteristic of the rock-like material made with polyurethane foam, unit volume weight was found to be quite lower than those of natural rock materials.

  18. Syndecan proteoglycans and cell adhesion

    DEFF Research Database (Denmark)

    Woods, A; Oh, E S; Couchman, J R

    1998-01-01

    It is now becoming clear that a family of transmembrane proteoglycans, the syndecans, have important roles in cell adhesion. They participate through binding of matrix ligand to their glycosaminoglycan chains, clustering, and the induction of signaling cascades to modify the internal microfilament...... organization. Syndecans can modulate the type of adhesive responses induced by other matrix ligand-receptor interactions, such as those involving the integrins, and so contribute to the control of cell morphology, adhesion and migration....

  19. Polyurethane-Coated Breast Implants Revisited: A 30-Year Follow-Up

    Directory of Open Access Journals (Sweden)

    Nikki Castel

    2015-03-01

    Full Text Available BackgroundPolyurethane coating of breast implants has been shown to reduce capsular contracture in short-term follow-up studies. This 30-year study is the longest examination of the use of polyurethane-coated implants and their correlation with capsular contracture.MethodsThis study evaluates the senior surgeon's (F.D.P. experience with the use of polyurethane-coated implants in aesthetic breast augmentation in 382 patients over 30 years. Follow-up evaluations were conducted for six months after surgery. After the six-month follow-up period, 76 patients returned for reoperation. The gross findings, histology, and associated capsular contracture were noted at the time of explantation.ResultsNo patient during the six-month follow-up period demonstrated capsular contracture. For those who underwent reoperation for capsular contracture, Baker II/III contractures were noted nine to 10 years after surgery and Baker IV contractures were noted 12 to 21 years after surgery. None of the explanted implants had macroscopic evidence of polyurethane, which was only found during the first five years after surgery. The microscopic presence of polyurethane was noted in all capsules up to 30 years after the original operation.ConclusionsAn inverse correlation was found between the amount of polyurethane coating on the implant and the occurrence of capsular contracture. Increasingly severe capsular contracture was associated with a decreased amount of polyurethane coating on the surface of the implants. No contracture occurred in patients whose implants showed incomplete biodegradation of polyurethane, as indicated by the visible presence of polyurethane coating. We recommend research to find a non-toxic, non-biodegradable synthetic material as an alternative to polyurethane.

  20. The neural cell adhesion molecule

    DEFF Research Database (Denmark)

    Berezin, V; Bock, E; Poulsen, F M

    2000-01-01

    During the past year, the understanding of the structure and function of neural cell adhesion has advanced considerably. The three-dimensional structures of several of the individual modules of the neural cell adhesion molecule (NCAM) have been determined, as well as the structure of the complex...... between two identical fragments of the NCAM. Also during the past year, a link between homophilic cell adhesion and several signal transduction pathways has been proposed, connecting the event of cell surface adhesion to cellular responses such as neurite outgrowth. Finally, the stimulation of neurite...

  1. Improved lignin polyurethane properties with Lewis acid treatment.

    Science.gov (United States)

    Chung, Hoyong; Washburn, Newell R

    2012-06-27

    Chemical modification strategies to improve the mechanical properties of lignin-based polyurethanes are presented. We hypothesized that treatment of lignin with Lewis acids would increase the concentration of hydroxyl groups available to react with diisocyanate monomers. Under the conditions used, hydrogen bromide-catalyzed modification resulted in a 28% increase in hydroxyl group content. Associated increases in hydrophilicity of solvent-cast thin films were also recorded as evidenced by decreases in water contact angle. Polyurethanes were then prepared by first preparing a prepolymer based on mixtures of toluene-2,4-diisocyanate (TDI) and unmodified or modified lignin, then polymerization was completed through addition of polyethylene glycol (PEG), resulting in mass ratios of TDI:lignin:PEG of 43:17:40 in the compositions investigated here. The mixture of TDI and unmodified lignin resulted in a lignin powder at the bottom of the liquid, suggesting it did not react directly with TDI. However, a homogeneous solution resulted when TDI and the hydrogen bromide-treated lignin were mixed, suggesting demethylation indeed increased reactivity and resulted in better integration of lignin into the urethane network. Significant improvements in mechanical properties of modified lignin polyurethanes were observed, with a 6.5-fold increase in modulus, which were attributed to better integration of the modified lignin into the covalent polymer network due to the higher concentration of hydroxyl groups. This research indicates that chemical modification strategies can lead to significant improvements in the properties of lignin-based polymeric materials using a higher fraction of an inexpensive lignin monomer from renewable resources and a lower fraction an expensive, petroleum-derived isocyanate monomer to achieve the required material properties.

  2. Hemocompatible polyethersulfone/polyurethane composite membrane for high-performance antifouling and antithrombotic dialyzer.

    Science.gov (United States)

    Yin, Zehua; Cheng, Chong; Qin, Hui; Nie, Chuanxiong; He, Chao; Zhao, Changsheng

    2015-01-01

    Researches on blood purification membranes are fuelled by diverse clinical needs, such as hemodialysis, hemodiafiltration, hemofiltration, plasmapheresis, and plasma collection. To approach high-performance dialyzer, the integrated antifouling and antithrombotic properties are highly necessary for the design/modification of advanced artificial membranes. In this study, we propose and demonstrate that the physical blend of triblock polyurethane (PU) and polyethersulfone (PES) may advance the performance of hemodialysis membranes with greatly enhanced blood compatibility. It was found that the triblock PU could be blended with PES at high ratio owing to their excellent miscibility. The surfaces of the PES/PU composite membranes were characterized using attenuated total reflectance-Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, water contact angle measurement, and surface ζ-potentials. The results indicated that the membrane surfaces were assembled with hydrophilic segregation layer owing to the migration of amphiphilic PU segments during membrane preparation, which might confer the composite membranes with superior hemocompatibility. The cross-section scanning electron microscopy images of the composite membranes exhibited structure transformation from finger-like structure to sponge-like structure, which indicated that the composite membrane had tunable porosity and permeability. The further ultrafiltration experiments indicated that the composite membranes showed increased permeability and excellent antifouling ability. The blood compatibility observation indicated that PES/PU composite membranes owned decreased protein adsorption, suppressed platelet adhesion, and prolonged plasma recalcification time. These results indicated that the PES/PU composite membranes exhibited enhanced antifouling and antithrombotic properties than the pristine PES membrane. The strategy may forward the fabrication of blood compatible composite membranes for

  3. Structural–mechanical and antibacterial properties of a soft elastic polyurethane surface after plasma immersion N{sub 2}{sup +} implantation

    Energy Technology Data Exchange (ETDEWEB)

    Morozov, Ilya A., E-mail: ilya.morozov@gmail.com [Institute of Continuous Media Mechanics UB RAS, Academika Koroleva st. 1, 614013 Perm (Russian Federation); Perm State University, Bukireva st. 15, 614990 Perm (Russian Federation); Mamaev, Alexander S. [Institute of Electrophysics UD RAS, Amundsen st. 106, 620016 Ekaterinburg (Russian Federation); Osorgina, Irina V. [Perm State University, Bukireva st. 15, 614990 Perm (Russian Federation); Lemkina, Larisa M. [Institute of Ecology and Genetics of Microorganisms UB RAS, Golev st. 13, 614081 Perm (Russian Federation); Korobov, Vladimir P. [Institute of Ecology and Genetics of Microorganisms UB RAS, Golev st. 13, 614081 Perm (Russian Federation); Perm National Research Polytechnic University, Komsomolsky av. 29, 614990 Perm (Russian Federation); Belyaev, Anton Yu [Institute of Continuous Media Mechanics UB RAS, Academika Koroleva st. 1, 614013 Perm (Russian Federation); Porozova, Svetlana E. [Perm National Research Polytechnic University, Komsomolsky av. 29, 614990 Perm (Russian Federation); Sherban, Marina G. [Perm State University, Bukireva st. 15, 614990 Perm (Russian Federation)

    2016-05-01

    The surface of elastic polyurethane treated by plasma immersion N{sub 2}{sup +} ion implantation at different fluences has been investigated. A folded surface structure is observed in all cases. Analysis has been performed to study the structural (roughness, steepness and fraction of folds, fractal characteristics), mechanical (stiffness, adhesion force between the AFM probe and the material) and wetting properties of surfaces. Under uniaxial stretching the cracks orthogonal to the axis of deformation and longitudinal folds are formed on the examined surfaces. After unloading the initial structure of the surface of deformed materials exposed to low fluences becomes smoother and does not recover, i.e. it has plastic properties. By contrast, the structure of the surfaces of materials subjected to high-fluence treatment recovers without visible changes and the cracks are fully closed. The study of Staphylococcus colonies grown on these materials has demonstrated significant reduction (from 3 to 5 times) in the vitality of bacteria on treated surfaces. This result was repeated on samples after 11 months of storage. Such antibacterial properties are primarily related to the structural changes of the surfaces accompanied by the increased hydrophilicity. - Highlights: • Surface of soft polyurethane after plasma immersion ion implantation was studied. • Treated surfaces have fluence dependent plicated fractal structure. • Surface properties were investigated both in undeformed and stretched states. • Vitality of bacteria on treated surfaces demonstrated significant reduction.

  4. Quasi-Static Behavior of Palm-Based Elastomeric Polyurethane: For Strengthening Application of Structures under Impulsive Loadings

    Directory of Open Access Journals (Sweden)

    H. M. Chandima Chathuranga Somarathna

    2016-05-01

    Full Text Available In recent years, attention has been focused on elastomeric polymers as a potential retrofitting material considering their capability in contributing towards the impact resistance of various structural elements. A comprehensive understanding of the behavior and the morphology of this material are essential to propose an effective and feasible alternative to existing structural strengthening and retrofitting materials. This article presents the findings obtained from a series of experimental investigations to characterize the physical, mechanical, chemical and thermal behavior of eight types of palm-based polyurethane (PU elastomers, which were synthesized from the reaction between palm kernel oil-based monoester polyol (PKO-p and 4,4-diphenylmethane diisocyanate (MDI with polyethylene glycol (PEG as the plasticizer via pre-polymerization. Fourier transform infrared (FT-IR spectroscopy analysis was conducted to examine the functional groups in PU systems. Mechanical and physical behavior was studied with focus on elongation, stresses, modulus, energy absorption and dissipation, and load dispersion capacities by conducting hardness, tensile, flexural, Izod impact, and differential scanning calorimetry tests. Experimental results suggest that the palm-based PU has positive effects as a strengthening and retrofitting material against dynamic impulsive loadings both in terms of energy absorption and dissipation, and load dispersion. In addition, among all PUs with different plasticizer contents, PU2 to PU8 (which contain 2% to 8% (w/w PEG with respect to PKO-p content show the best correlation with mechanical response under quasi-static conditions focusing on energy absorption and dissipation and load dispersion characteristics.

  5. Polyurethane nanofibers containing copper nanoparticles as future materials

    DEFF Research Database (Denmark)

    Sheikh, Faheem A.; Kanjwal, Muzafar Ahmed; Saran, Saurabh

    2011-01-01

    nanofibers. Typically, a colloidal gel consisting of copper NPs and polyurethane has been electrospun. SEM-EDX and TEM results confirmed well oriented nanofibers and good dispersion of pure copper NPs. Copper NPs have diameter in the range of 5–10nm. The thermal stability of the synthesized nanofibers...... the antimicrobial efficacy of these nanofiber mats. Subsequently, antimicrobial tests have indicated that the prepared nanofibers do posses good bactericidal effect. Accordingly, it is noted that the obtained nanofiber mats can be used as future filter membranes with good antimicrobial activities....

  6. Dielectric and conductivity properties of composite polyaniline/polyurethane network

    Science.gov (United States)

    Liang, C.; Gest, J.; Leroy, G.; Carru, J.-C.

    2013-09-01

    In this work, we present the dielectric characterization of polyaniline/polyurethane composite. The samples consisting of 0.5%, 1%, and 5% of polyaniline were deposited on glass fiber, and the measurements were performed in a frequency range of 20 Hz to 20 GHz. The results showed a dielectric relaxation strongly dependent on the concentration of polyaniline. This phenomenon is explained by a theoretical model. In this model, we assume that the alternative conductivity of the polymer network systems is due to conducting clusters whose lengths followed a Gaussian distribution. Depending on their size and the frequency of the excitation signal, the clusters showed a resistive or capacitive effect.

  7. Investigation of Industrial Polyurethane Foams Modified with Antimicrobial Copper Nanoparticles

    Directory of Open Access Journals (Sweden)

    Maria Chiara Sportelli

    2016-07-01

    Full Text Available Antimicrobial copper nanoparticles (CuNPs were electrosynthetized and applied to the controlled impregnation of industrial polyurethane foams used as padding in the textile production or as filters for air conditioning systems. CuNP-modified materials were investigated and characterized morphologically and spectroscopically, by means of Transmission Electron Microscopy (TEM, and X-ray Photoelectron Spectroscopy (XPS. The release of copper ions in solution was studied by Electro-Thermal Atomic Absorption Spectroscopy (ETAAS. Finally, the antimicrobial activity of freshly prepared, as well as aged samples—stored for two months—was demonstrated towards different target microorganisms.

  8. Stretchable polyurethane sponge reinforced magnetorheological material with enhanced mechanical properties

    International Nuclear Information System (INIS)

    Ge, Lin; Xuan, Shouhu; Liao, Guojiang; Yin, Tiantian; Gong, Xinglong

    2015-01-01

    A stretchable magnetorheological material (SMRM) consisting of micro-meter carbonyl iron (CI) particles, low cross-linking polyurethane (PU) polymer and porous PU sponge has been developed. Due to the presence of the PU sponge, the high-performance MR material can be reversibly stretched or bent, just as MR elastomers. When the CI content increases to 80 wt%, the magnetic induced modulus of the MR material can reach as high as 7.34 MPa and the corresponding relative MR effect increases to 820%. A possible strengthening mechanism of the SMRM was proposed. The attractive mechanical properties make the SMRM a promising candidate for future high-performance devices. (technical note)

  9. Method for providing a low density high strength polyurethane foam

    Science.gov (United States)

    Whinnery, Jr., Leroy L.; Goods, Steven H.; Skala, Dawn M.; Henderson, Craig C.; Keifer, Patrick N.

    2013-06-18

    Disclosed is a method for making a polyurethane closed-cell foam material exhibiting a bulk density below 4 lbs/ft.sup.3 and high strength. The present embodiment uses the reaction product of a modified MDI and a sucrose/glycerine based polyether polyol resin wherein a small measured quantity of the polyol resin is "pre-reacted" with a larger quantity of the isocyanate in a defined ratio such that when the necessary remaining quantity of the polyol resin is added to the "pre-reacted" resin together with a tertiary amine catalyst and water as a blowing agent, the polymerization proceeds slowly enough to provide a stable foam body.

  10. Electron beam curing polyurethane acrylate oligomer in air

    International Nuclear Information System (INIS)

    Zhu, Zhenkang; Chen, Xing; Zhou, Jichun; Ma, Zue-Teh

    1988-01-01

    It has been found according to our synthesis that a novel kind of polyurethane acrylate oligomer can be cured by electron beam in the presence of oxygen, even at normal atomospheric levels, without any additives. Irradiation of the oligomer with substantially complete cure to a solid non-tacky state is quite remarkable. It has the same gel content (90 %) in air as in nitrogen at dose of 33 kGy. Double bond conversion of the oligomer is about 50 % by I.R. (author)

  11. Radiation-induced changes affecting polyester based polyurethane binder

    Science.gov (United States)

    Pierpoint, Sujita Basi

    The application of thermoplastic polyurethane elastomers as binders in the high energy explosives particularly when used in weapons presents a significantly complex and challenging problem due to the impact of the aging of this polymer on the useful service life of the explosive. In this work, the effects of radiation on the aging of the polyester based polyurethane were investigated using both electron beam and gamma irradiation at various dose rates in the presence and absence of oxygen. It was found by means of GPC that, in the presence and absence of oxygen, the poly (ester urethane) primarily undergoes cross-linking, by means of a carbon-centered secondary alkyl radical. It was also concluded that the polymer partially undergoes scission of the backbone of the main chain at C-O, N-C, and C-C bonds. Substantial changes in the conditions of irradiation and in dose levels did not affect the cross-linking and scission yields. Experiments were also performed with EPR spectroscopy for the purpose of identifying the initial carbon-centered free radicals and for studying the decay mechanisms of these radicals. It was found that the carbon-centered radical which is produced via C-C scission (primary alkyl radical) is rapidly converted to a long-lived allylic species at higher temperatures; more than 80% radicals are converted to allyl species in 2.5 hours. In the presence of oxygen, the allyl radical undergoes a fast reaction to produce a peroxyl radical; this radical decays with a 1.7 hour half-life by pseudo first-order kinetics to negligible levels in 13 hours. FTIR measurements were conducted to identify the radiation-induced changes to the functional groups in the polyester polyurethane. These measurements show an increase in carbonyl, amine and carboxylic groups as a result of reaction of H atoms with R-C-O·, ·NH-R and R-COO·. The FTIR results also demonstrate the production of the unsaturation resulting from hydrogen atom transfer during intrachain conversion

  12. Improved Adhesion and Compliancy of Hierarchical Fibrillar Adhesives.

    Science.gov (United States)

    Li, Yasong; Gates, Byron D; Menon, Carlo

    2015-08-05

    The gecko relies on van der Waals forces to cling onto surfaces with a variety of topography and composition. The hierarchical fibrillar structures on their climbing feet, ranging from mesoscale to nanoscale, are hypothesized to be key elements for the animal to conquer both smooth and rough surfaces. An epoxy-based artificial hierarchical fibrillar adhesive was prepared to study the influence of the hierarchical structures on the properties of a dry adhesive. The presented experiments highlight the advantages of a hierarchical structure despite a reduction of overall density and aspect ratio of nanofibrils. In contrast to an adhesive containing only nanometer-size fibrils, the hierarchical fibrillar adhesives exhibited a higher adhesion force and better compliancy when tested on an identical substrate.

  13. Stretchable, Adhesion-Tunable Dry Adhesive by Surface Wrinkling

    KAUST Repository

    Jeong, Hoon Eui

    2010-02-16

    We introduce a simple yet robust method of fabricating a stretchable, adhesion-tunable dry adhesive by combining replica molding and surface wrinkling. By utilizing a thin, wrinkled polydimethyl siloxane (PDMS) sheet with a thickness of 1 mm with built-in micropillars, active, dynamic control of normal and shear adhesion was achieved. Relatively strong normal (∼10.8 N/cm2) and shear adhesion (∼14.7 N/cm2) forces could be obtained for a fully extended (strained) PDMS sheet (prestrain of∼3%), whereas the forces could be rapidly reduced to nearly zero once the prestrain was released (prestrain of ∼0.5%). Moreover, durability tests demonstrated that the adhesion strength in both the normal and shear directions was maintained over more than 100 cycles of attachment and detachment. © 2010 American Chemical Society.

  14. Effect of adhesive thickness on adhesively bonded T-joint

    International Nuclear Information System (INIS)

    Abdullah, A R; Afendi, Mohd; Majid, M S Abdul

    2013-01-01

    The aim of this work is to analyze the effect of adhesive thickness on tensile strength of adhesively bonded stainless steel T-joint. Specimens were made from SUS 304 Stainless Steel plate and SUS 304 Stainless Steel perforated plate. Four T-joint specimens with different adhesive thicknesses (0.5, 1.0, 1.5 and 2.0 mm) were made. Experiment result shows T-joint specimen with adhesive thickness of 1.0 mm yield highest maximum load. Identical T-joint specimen jointed by spot welding was also tested. Tensile test shows welded T-Joint had eight times higher tensile load than adhesively bonded T-joint. However, in low pressure application such as urea granulator chamber, high tensile strength is not mandatory. This work is useful for designer in fertilizer industry and others who are searching for alternative to spot welding

  15. Stretchable, Adhesion-Tunable Dry Adhesive by Surface Wrinkling

    KAUST Repository

    Jeong, Hoon Eui; Kwak, Moon Kyu; Suh, Kahp Y.

    2010-01-01

    We introduce a simple yet robust method of fabricating a stretchable, adhesion-tunable dry adhesive by combining replica molding and surface wrinkling. By utilizing a thin, wrinkled polydimethyl siloxane (PDMS) sheet with a thickness of 1 mm with built-in micropillars, active, dynamic control of normal and shear adhesion was achieved. Relatively strong normal (∼10.8 N/cm2) and shear adhesion (∼14.7 N/cm2) forces could be obtained for a fully extended (strained) PDMS sheet (prestrain of∼3%), whereas the forces could be rapidly reduced to nearly zero once the prestrain was released (prestrain of ∼0.5%). Moreover, durability tests demonstrated that the adhesion strength in both the normal and shear directions was maintained over more than 100 cycles of attachment and detachment. © 2010 American Chemical Society.

  16. New insights into polyurethane biodegradation and realistic prospects for the development of a sustainable waste recycling process.

    Science.gov (United States)

    Cregut, Mickael; Bedas, M; Durand, M-J; Thouand, G

    2013-12-01

    Polyurethanes are polymeric plastics that were first used as substitutes for traditional polymers suspected to release volatile organic hazardous substances. The limitless conformations and formulations of polyurethanes enabled their use in a wide variety of applications. Because approximately 10 Mt of polyurethanes is produced each year, environmental concern over their considerable contribution to landfill waste accumulation appeared in the 1990s. To date, no recycling processes allow for the efficient reuse of polyurethane waste due to their high resistance to (a)biotic disturbances. To find alternatives to systematic accumulation or incineration of polyurethanes, a bibliographic analysis was performed on major scientific advances in the polyurethane (bio)degradation field to identify opportunities for the development of new technologies to recondition this material. Until polymers exhibiting oxo- or hydro-biodegradative traits are generated, conventional polyurethanes that are known to be only slightly biodegradable are of great concern. The research focused on polyurethane biodegradation highlights recent attempts to reprocess conventional industrial polyurethanes via microbial or enzymatic degradation. This review describes several wonderful opportunities for the establishment of new processes for polyurethane recycling. Meeting these new challenges could lead to the development of sustainable management processes involving polymer recycling or reuse as environmentally safe options for industries. The ability to upgrade polyurethane wastes to chemical compounds with a higher added value would be especially attractive. © 2013.

  17. Combinatorial and high-throughput screening of the effect of siloxane composition on the surface properties of crosslinked siloxane-polyurethane coatings.

    Science.gov (United States)

    Ekin, Abdullah; Webster, Dean C

    2007-01-01

    Libraries of siloxane-polyurethane coatings were designed, formulated, and screened using high-throughput experimentation. Four independent variables that were analyzed were the molecular weight of poly(dimethylsiloxane) (PDMS), presence or absence of poly(epsilon-caprolactone) (PCL) blocks attached to the PDMS backbone, the length of the PCL blocks, and the siloxane polymer level in the coating formulations. In addition to the siloxane libraries (3-aminopropyl-terminated PDMS and poly(epsilon-caprolactone)-poly(dimethylsiloxane)-poly(epsilon-caprolactone) (PCL-PDMS-PCL) triblock copolymers), the coating formulation included a trifunctional isocyanate crosslinker, trifunctional poly(epsilon-caprolactone) polyol, 2,4-pentanedione (pot-life extender), dibutyltin diacetate (catalyst), and a blend of solvents. The resulting coatings were analyzed for their surface energy and pseudobarnacle adhesion both before and after aging the coatings for 30 days in water. The water and methylene iodide contact angle averages increase with increasing molecular weight of PDMS. Coatings prepared from PCL-PDMS-PCL triblock copolymers have lower surface energies than coatings prepared from 3-aminopropyl-terminated PDMS; however, lower pseudobarnacle adhesion results were obtained for the coatings prepared from 3-aminopropyl-terminated PDMS than coatings prepared from PCL-PDMS-PCL triblock copolymers. The siloxane polymer level in the coating formulations does not have a significant effect on the surface energy of the coatings, but it resulted in higher pseudobarnacle adhesion.

  18. Syndecans, signaling, and cell adhesion

    DEFF Research Database (Denmark)

    Couchman, J R; Woods, A

    1996-01-01

    structures within the heparan sulfate chains, leaving the roles of chondroitin sulfate chains and extracellular portion of the core proteins to be elucidated. Evidence that syndecans are a class of receptor involved in cell adhesion is mounting, and their small cytoplasmic domains may link...... transmembrane signaling from matrix to cytoskeleton, as proposed for other classes of adhesion receptors....

  19. Controlling adhesive behavior during recycling

    Science.gov (United States)

    Carl Houtman; Karen Scallon; Jihui Guo; XinPing Wang; Steve Severtson; Mark Kroll; Mike Nowak

    2004-01-01

    Adhesives can be formulated to facilitate their removal by typical paper recycling unit operations. The investigations described in this paper are focused on determining fundamental properties that control particle size during pulping. While pressure-sensitive adhesives (PSAs) with high elastic moduli tend to survive pulping with larger particles, facestock and...

  20. The Fossil Fueled Metropolis: Los Angeles and the Emergence of Oil-Based Energy in North America, 1865--1930

    Science.gov (United States)

    Cooke, Jason Arthur

    Beginning with coal in the nineteenth century, the mass production and intensive consumption of fossil fuel energy fundamentally changed patterns of urban and industrial development in North America. Focusing on the metropolitan development of Los Angeles, this dissertation examines how the emergence of oil-based capitalism in the first three decades of the twentieth century was sustained and made increasingly resilient through the production of urban and industrial space. In a region where coal was scarce, the development of oil-based energy was predicated on long-term investments into conversion technologies, storage systems and distribution networks that facilitated the efficient and economical flow of liquefied fossil fuel. In this dissertation, I argue that the historical and geographical significance of the Southern California petroleum industry is derived from how its distinctive market expansion in the first three decades of the twentieth century helped establish the dominance of oil-based energy as the primary fuel for transportation in capitalist society. In North America, the origins of oil-based capitalism can be traced to the turn of the twentieth century when California was the largest oil-producing economy in the United States and Los Angeles was the fastest growing metropolitan region. This dissertation traces how Los Angeles became the first city in North America where oil became a formative element of urban and industrial development: not only as fuel for transportation, but also in the infrastructures, landscapes and networks that sustain a critical dependence on oil-based energy. With a distinctive metropolitan geography, decentralized and automobile-dependent, Los Angeles became the first oil-based city in North America and thus provides an ideal case study for examining the regional dynamics of energy transition, establishment and dependence. Interwoven with the production of urban and industrial space, oil remains the primary fuel that

  1. Identification of carbonate reservoirs based on well logging data for boreholes drilled using oil base muds

    International Nuclear Information System (INIS)

    Abdukhalikov, Ya.N; Serebrennikov, V.S.

    1979-01-01

    Experiment on carbonate reservoir identification according to well logging data for boreholes drilled using oil base muds is described. Pulse neutron-neutron logging (PNNL) was widely used at the territory of Pripyat' hole to solve the task. To evaluate volumetric clayiness of carbonate rocks the dependence of gamma-logging, that is data of gamma-logging against clayey rocks built for every hollow, is used. Quantitative estimation of clayiness of dense and clayey carbonate rocks-non-reservoirs is carried out on the basis of the data of neutron-gamma and acoustic logging. Porosity coefficient and lithological characteristic of rocks are also determined according to the data of acoustic and neutron gamma-logging

  2. Dielectric oil-based polymer actuator for improved thickness strain and breakdown voltage

    Energy Technology Data Exchange (ETDEWEB)

    Cho, Min Sung; Yamamoto, Akio [Dept. of Precision Engineering, School of Engineering, The University of Tokyo, Tokyo (Japan)

    2016-09-15

    Dielectric elastomer actuators (DEAs) have been increasingly investigated as alternative actuators to conventional ones. However, DEAs suffer from high rates of premature failure. Therefore, this study proposes a dielectric oil-based polymer actuator, also called a Dielectric liquid actuator (DLA), to compensate for the drawbacks of DEAs. DLA was experimentally compared with conventional DEAs. Results showed that DLA successfully prevented thermal runaway at defects in the electrode and excessive thinning of the film, resulting in increased breakdown voltage. Consequently, premature failure was inhibited, and the performance was improved. The breakdown voltages of DLA and DEA were 6000 and 2000 V, respectively, and their maximum thickness strains were 49.5% and 37.5%, respectively.

  3. Soya oil-based shampoo superior to 0.5% permethrin lotion for head louse infestation.

    Science.gov (United States)

    Burgess, Ian F; Kay, Katrina; Burgess, Nazma A; Brunton, Elizabeth R

    2011-01-01

    This was a randomized, assessor-blind, controlled comparison of a soya oil- based medical device shampoo with a medicinal permethrin lotion in an alcohol vehicle for treatment of head louse infestation to generate data suitable for a regulatory submission to achieve reimbursable status for the shampoo product. We treated 91 children and adults, divided between two sites, on two occasions 9 days apart. Participants washed their hair and towel-dried it before treatment. The shampoo was used twice for 30 minutes each time. The lotion was used for 30 minutes followed by rinsing. Assessments were made by dry detection combing on days 2, 9, 11, and 14 after the first treatment. According to present knowledge, this combing technique does not influence the overall head louse populations or outcome of treatment. The soya oil shampoo was significantly (P shampoo was more effective than the permethrin lotion, more cosmetically acceptable, and less irritant.

  4. Dielectric oil-based polymer actuator for improved thickness strain and breakdown voltage

    International Nuclear Information System (INIS)

    Cho, Min Sung; Yamamoto, Akio

    2016-01-01

    Dielectric elastomer actuators (DEAs) have been increasingly investigated as alternative actuators to conventional ones. However, DEAs suffer from high rates of premature failure. Therefore, this study proposes a dielectric oil-based polymer actuator, also called a Dielectric liquid actuator (DLA), to compensate for the drawbacks of DEAs. DLA was experimentally compared with conventional DEAs. Results showed that DLA successfully prevented thermal runaway at defects in the electrode and excessive thinning of the film, resulting in increased breakdown voltage. Consequently, premature failure was inhibited, and the performance was improved. The breakdown voltages of DLA and DEA were 6000 and 2000 V, respectively, and their maximum thickness strains were 49.5% and 37.5%, respectively

  5. Preparation and Characterization of Liquid Crystalline Polyurethane/Al2O3/Epoxy Resin Composites for Electronic Packaging

    Directory of Open Access Journals (Sweden)

    Shaorong Lu

    2012-01-01

    Full Text Available Liquid crystalline polyurethane (LCPU/Al2O3/epoxy resin composites were prepared by using LCPU as modifier. The mechanical properties, thermal stability, and electrical properties of the LCPU/Al2O3/epoxy resin composites were investigated systematically. The thermal oxidation analysis indicated that LCPU/Al2O3/epoxy resin composites can sustain higher thermal decomposition temperature. Meanwhile, coefficient of thermal expansion (CTE was also found to decrease with addition of LCPU and nano-Al2O3.

  6. Regulative mechanisms of chondrocyte adhesion

    DEFF Research Database (Denmark)

    Schmal, Hagen; Mehlhorn, Alexander T; Fehrenbach, Miriam

    2006-01-01

    Interaction between chondrocytes and extracellular matrix is considered a key factor in the generation of grafts for matrix-associated chondrocyte transplantation. Therefore, our objective was to study the influence of differentiation status on cellular attachment. Adhesion of chondrocytes...... to collagen type II increased after removal from native cartilage up to the third day in monolayer in a dose-dependent manner. Following dedifferentiation after the second passage, adhesion to collagen types I (-84%) and II (-46%) decreased, whereas adhesion to fibrinogen (+59%) and fibronectin (+43......%) increased. A cartilage construct was developed based on a clinically established collagen type I scaffold. In this matrix, more than 80% of the cells could be immobilized by mechanisms of adhesion, filtration, and cell entrapment. Confocal laser microscopy revealed focal adhesion sites as points of cell...

  7. Soya oil-based shampoo superior to 0.5% permethrin lotion for head louse infestation

    Directory of Open Access Journals (Sweden)

    Nazma A Burgess

    2011-03-01

    Full Text Available Ian F Burgess1, Katrina Kay1,2, Nazma A Burgess1, Elizabeth R Brunton11Medical Entomology Centre, Insect Research and Development Limited, Cambridge, 2Leeds Primary Care Trust, Leeds, UKBackground: This was a randomized, assessor-blind, controlled comparison of a soya oil-based medical device shampoo with a medicinal permethrin lotion in an alcohol vehicle for treatment of head louse infestation to generate data suitable for a regulatory submission to achieve reimbursable status for the shampoo product.Methods: We treated 91 children and adults, divided between two sites, on two occasions 9 days apart. Participants washed their hair and towel-dried it before treatment. The shampoo was used twice for 30 minutes each time. The lotion was used for 30 minutes followed by rinsing. Assessments were made by dry detection combing on days 2, 9, 11, and 14 after the first treatment. According to present knowledge, this combing technique does not influence the overall head louse populations or outcome of treatment.Results: The soya oil shampoo was significantly (P < 0.01 more effective than the lotion for both intention to treat (62.2% versus 34.8% successful treatment and per-protocol (74.3% versus 36.8% success groups. Post-treatment assessments showed the necessity for repeat treatment, but that a 9-day interval was too long because if eggs hatched after the first treatment, the lice could grow old enough to lay eggs before the second treatment.Conclusion: The soya oil-based shampoo was more effective than the permethrin lotion, more cosmetically acceptable, and less irritant.Keywords: pediculosis, medical device, medicinal product, insecticide, vegetable oil

  8. Study of Dielectric Breakdown Performance of Transformer Oil Based Magnetic Nanofluids

    Directory of Open Access Journals (Sweden)

    Yuzhen Lv

    2017-07-01

    Full Text Available Research on the transformer oil-based nanofluids (NFs has been raised expeditiously over the past decade. Although, there is discrepancy in the stated results and inadequate understanding of the mechanisms of improvement of dielectric nanofluids, these nanofluids have emerged as a potential substitute of mineral oils as insulating and heat removal fluids for high voltage equipment. The transformer oil (TO based magnetic fluids (ferrofluids may be regarded as the posterity insulation fluids as they propose inspiring unique prospectus to improve dielectric breakdown strength, as well as heat transfer efficiency, as compared to pure transformer oils. In this work, transformer oil-based magnetic nanofluids (MNFs are prepared by dispersal of Fe3O4 nanoparticles (MNPs into mineral oil as base oil, with various NPs loading from 5 to 80% w/v. The lightning impulse breakdown voltages (BDV measurement was conducted in accordance with IEC 60897 by using needle to sphere electrodes geometry. The test results showed that dispersion of magnetic NPs may improve the insulation strength of MO. With the increment of NPs concentrations, the positive lightning impulse (LI breakdown strength of TO is first raised, up to the highest value at 40% loading, and then tends to decrease at higher concentrations. The outcomes of negative LI breakdown showed that BDV of MNFs, with numerous loadings, were inferior to the breakdown strength of pure MO. The 40% concentration of nanoparticles (optimum concentration was selected, and positive and negative LI breakdown strength was also further studied at different sizes (10 nm, 20 nm, 30 nm and 40 nm of NPs and different electrode gap distances. Augmentation in the BDV of the ferrofluids (FFs is primarily because of dielectric and magnetic features of Fe3O4 nanoaprticles, which act as electron scavengers and decrease the rate of free electrons produced in the ionization process. Research challenges and technical difficulties

  9. Oil base fluids without tensoactive additives; Fluidos a base de oleo sem tensoativos

    Energy Technology Data Exchange (ETDEWEB)

    Machado, Jose Carlos V; Aragao, Atila Fernando L [PETROBRAS, XX (Brazil). Centro de Desenvolvimento de Recursos Humanos Norte e Nordeste

    1990-12-31

    The goal of this paper is to define an ideal oil base fluid composition without tensoactive additives, since these may cause damage to producing formation during drilling or well completion. We investigated the rheological, filtrating and phase separation properties of the systems composed of diesel oil, organophilic clay and a polar agent (water or ethyl alcohol). In order to to that, we used the 286 Baroid digital rotating viscometer, filtrating cells standardized according to the American Petroleum Institute (AP) for temperatures of 25 deg C to 149 deg C and pressures of 6,89 x 10{sup 5} Pa (100 psig) to 3,44 x 10{sup 6} (500 psig), and the setting method, according to the determinations of respectively rheological, filtrating and phase separation parameters. Results proved that the composition: diesel oil-94% v/v, Na Cl saturated solution - 6% v/v and bentone - 17,1 to 22,8 kg/m{sup 3} (6 to 8 lb/bbl), is ideal to meet the properties required for drilling and well completion operations for low densities, that is 0,84% to 1,02 (6,9 to 8,5 ib/gal). In order to obtain densities in the interval of 1,02 to 1,14 (8,5 to 9,5 ib/gal) the system should be condensed with calcite (Ca CO{sub 3}) and the base fluid composition should be : diesel oil-94 to 98% v/v, Na Cl saturated solution - 2 to 6% v/v and bentone 17,1 to 22,8 kg/m{sup 3} (6 to 8 ib/bbl). The average cost per barrel for the systems studied here is of the same order of conventional oil base fluids (with tensoactive additives). (author) 13 refs., 7 figs., 3 tabs.

  10. Oil base fluids without tensoactive additives; Fluidos a base de oleo sem tensoativos

    Energy Technology Data Exchange (ETDEWEB)

    Machado, Jose Carlos V.; Aragao, Atila Fernando L. [PETROBRAS, XX (Brazil). Centro de Desenvolvimento de Recursos Humanos Norte e Nordeste

    1989-12-31

    The goal of this paper is to define an ideal oil base fluid composition without tensoactive additives, since these may cause damage to producing formation during drilling or well completion. We investigated the rheological, filtrating and phase separation properties of the systems composed of diesel oil, organophilic clay and a polar agent (water or ethyl alcohol). In order to to that, we used the 286 Baroid digital rotating viscometer, filtrating cells standardized according to the American Petroleum Institute (AP) for temperatures of 25 deg C to 149 deg C and pressures of 6,89 x 10{sup 5} Pa (100 psig) to 3,44 x 10{sup 6} (500 psig), and the setting method, according to the determinations of respectively rheological, filtrating and phase separation parameters. Results proved that the composition: diesel oil-94% v/v, Na Cl saturated solution - 6% v/v and bentone - 17,1 to 22,8 kg/m{sup 3} (6 to 8 lb/bbl), is ideal to meet the properties required for drilling and well completion operations for low densities, that is 0,84% to 1,02 (6,9 to 8,5 ib/gal). In order to obtain densities in the interval of 1,02 to 1,14 (8,5 to 9,5 ib/gal) the system should be condensed with calcite (Ca CO{sub 3}) and the base fluid composition should be : diesel oil-94 to 98% v/v, Na Cl saturated solution - 2 to 6% v/v and bentone 17,1 to 22,8 kg/m{sup 3} (6 to 8 ib/bbl). The average cost per barrel for the systems studied here is of the same order of conventional oil base fluids (with tensoactive additives). (author) 13 refs., 7 figs., 3 tabs.

  11. Local sustained delivery of bupivacaine HCl from a new castor oil-based nanoemulsion system.

    Science.gov (United States)

    Rachmawati, Heni; Arvin, Yang Aryani; Asyarie, Sukmadjaja; Anggadiredja, Kusnandar; Tjandrawinata, Raymond Rubianto; Storm, Gert

    2018-06-01

    Bupivacaine HCl (1-butyl-2',6'-pipecoloxylidide hydrochloride), an amide local anesthetic compound, is a local anesthetic drug utilized for intraoperative local anesthesia, post-operative analgesia and in the treatment of chronic pain. However, its utility is limited by the relative short duration of analgesia after local administration (approximately 9 h after direct injection) and risk for side effects. This work is aimed to develop a nanoemulsion of bupivacaine HCl with sustained local anesthetics release kinetics for improved pain management, by exhibiting extended analgesic action and providing reduced peak levels in the circulation to minimize side effects. Herein, biodegradable oils were evaluated for use in nanoemulsions to enable sustained release kinetics of bupivacaine HCl. Only with castor oil, a clear and stable nanoemulsion was obtained without the occurrence of phase separation over a period of 3 months. High loading of bupivacaine HCl into the castor oil-based nanoemulsion system was achieved with about 98% entrapment efficiency and the resulting formulation showed high stability under stress conditions (accelerated stability test) regarding changes in visual appearance, drug content, and droplet size. We show herein that the in vitro release and in vivo pharmacokinetic profiles as well as pharmacodynamic outcome (pain relief test) after subcutaneous administration in rats correlate well and clearly demonstrate the prolonged release and extended duration of activity of our novel nanoformulation. In addition, the lower C max value achieved in the blood compartment suggests the possibility that the risk for systemic side effects is reduced. We conclude that castor oil-based nanomulsion represents an attractive pain treatment possibility to achieve prolonged local action of bupivacaine HCl.

  12. A Novel Biodegradable Polyurethane Matrix for Auricular Cartilage Repair: An In Vitro and In Vivo Study.

    Science.gov (United States)

    Iyer, Kartik; Dearman, Bronwyn L; Wagstaff, Marcus J D; Greenwood, John E

    2016-01-01

    Auricular reconstruction poses a challenge for reconstructive and burns surgeons. Techniques involving cartilage tissue engineering have shown potential in recent years. A biodegradable polyurethane matrix developed for dermal reconstruction offers an alternative to autologous, allogeneic, or xenogeneic biologicals for cartilage reconstruction. This study assesses such a polyurethane matrix for this indication in vivo and in vitro. To evaluate intrinsic cartilage repair, three pigs underwent auricular surgery to create excisional cartilage ± perichondrial defects, measuring 2 × 3 cm in each ear, into which acellular polyurethane matrices were implanted. Biopsies were taken at day 28 for histological assessment. Porcine chondrocytes ± perichondrocytes were cultured and seeded in vitro onto 1 × 1 cm polyurethane scaffolds. The total culture period was 42 days; confocal, histological, and immunohistochemical analyses of scaffold cultures were performed on days 14, 28, and 42. In vivo, the polyurethane matrices integrated with granulation tissue filling all biopsy samples. Minimal neocartilage invasion was observed marginally on some samples. Tissue composition was identical between ears whether perichondrium was left intact, or not. In vitro, the polyurethane matrix was biocompatible with chondrocytes ± perichondrocytes and supported production of extracellular matrix and Type II collagen. No difference was observed between chondrocyte culture alone and chondrocyte/perichondrocyte scaffold coculture. The polyurethane matrix successfully integrated into the auricular defect and was a suitable scaffold in vitro for cartilage tissue engineering, demonstrating its potential application in auricular reconstruction.

  13. Nano-TiO2/polyurethane composites for antibacterial and self-cleaning coatings

    International Nuclear Information System (INIS)

    Charpentier, P A; Burgess, K; Wang, L; Chowdhury, R R; Lotus, A F; Moula, G

    2012-01-01

    Grafting from polymerization was used to synthesize nano-titania/polyurethane (nTiO 2 /polyurethane) composite coatings, where nTiO 2 was chemically attached to the backbone of the polyurethane polymer matrix with a bifunctional monomer, 2,2-bis(hydroxymethyl) propionic acid (DMPA). This bifunctional monomer can coordinate to nTiO 2 through an available –COOH group, with two available hydroxyl groups that can react with diisocyanate terminated pre-polyurethane through step-growth polymerization. The coordination reaction was monitored by FTIR and TGA, with the coordination reaction found to follow first order kinetics. After step-growth polymerization, the polyurethane nanocomposites were found to be stable on standing with excellent distribution of Ti in the polymer matrix without any significant agglomeration compared to simple physical mixtures of nTiO 2 in the polyurethane coatings. The functionalized nTiO 2 –polyurethane composite coatings showed excellent antibacterial activity against gram-negative bacteria Escherichia coli; 99% of E. coli were killed within less than one hour under solar irradiation. Self-cleaning was also demonstrated using stearic acid as a model for ‘dirt’. (paper)

  14. Thermal assault and polyurethane foam-evaluating protective mechanisms

    International Nuclear Information System (INIS)

    Williamson, C.L.; Iams, Z.L.

    2004-01-01

    Rigid polyurethane foam utilizes a variety of mechanisms to mitigate the thermal assault of a ''regulatory burn''. Polymer specific heat and foam k-factor are of limited usefulness in predicting payload protection. Properly formulated rigid polyurethane foam provides additional safeguards by employing ablative mechanisms which are effective even when the foam has been crushed or fractured as a result of trauma. The dissociative transitions from polymer to gas and char, and the gas transport of heat from inside the package out into the environment are also thermal mitigators. Additionally, the in-situ production of an intumescent, insulative, carbonaceous char, confers thermal protection even when a package's outer steel skin has been breached. In this test program, 19 liter, ''Five gallon'' steel pails are exposed on one end to the flame of an ''Oil Burner'' as described in the US Federal Aviation Administration (FAA) ''Aircraft Materials Fire Test Handbook''. When burning 2 diesel at a nominal rate of 8.39 kg (18.5 pounds)/hr, the burner generates a high emissivity flame that impinges on the pail face with the thermal intensity of a full scale pool-fire environment. Results of these tests, TGA and MDSC analysis on the subject foams are reported, and their relevance to full size packages and pool fires are discussed

  15. Stem cell responses to plasma surface modified electrospun polyurethane scaffolds.

    Science.gov (United States)

    Zandén, Carl; Hellström Erkenstam, Nina; Padel, Thomas; Wittgenstein, Julia; Liu, Johan; Kuhn, H Georg

    2014-07-01

    The topographical effects from functional materials on stem cell behavior are currently of interest in tissue engineering and regenerative medicine. Here we investigate the influence of argon, oxygen, and hydrogen plasma surface modification of electrospun polyurethane fibers on human embryonic stem cell (hESC) and rat postnatal neural stem cell (NSC) responses. The plasma gases were found to induce three combinations of fiber surface functionalities and roughness textures. On randomly oriented fibers, plasma treatments lead to substantially increased hESC attachment and proliferation as compared to native fibers. Argon plasma was found to induce the most optimal combination of surface functionality and roughness for cell expansion. Contact guided migration of cells and alignment of cell processes were observed on aligned fibers. Neuronal differentiation around 5% was found for all samples and was not significantly affected by the induced variations of surface functional group distribution or individual fiber topography. In this study the influence of argon, oxygen, and hydrogen plasma surface modification of electrospun polyurethane fibers on human embryonic stem cell and rat postnatal neural stem cell (NSC) responses is studied with the goal of clarifying the potential effects of functional materials on stem cell behavior, a topic of substantial interest in tissue engineering and regenerative medicine. Copyright © 2014 Elsevier Inc. All rights reserved.

  16. Preparation and characterization of polyurethane microcapsules containing functional oil

    Energy Technology Data Exchange (ETDEWEB)

    Kim, I.H.; Seo, J.B.; Kim, Y.J. [Sungkyunkwan University, Suwon (Korea)

    2002-05-01

    Polyurethane microcapsules containing functional oil (citronella oil) were successfully prepared by conventional interfacial polymerization of tolulene 2,4-diisocyanate (TDI) and ethylene glycol (EG) and characterized by Fourier transform (FT-IR) spectroscopy, Ultraviolet spectroscopy, particle size analysis, thermogravimetric analysis (TGA), and scanning electron microscopy (SEM). The effects of polymerization variables such as surfactant concentration and agitation speed, on the particle size and particle size distribution were investigated. FT-IR spectroscopic data showed that citronella oil was successfully encapsulated in the microcapsule. Thermogravimetric analysis data showed that the microcapsule was thermally stable up to 220 deg. C. The controlled release of the citronella oil present in the microcapsule core in a methanol medium was demonstrated by ultraviolet spectroscopy, showing that the amount of released citronella oil was increased with increasing time. It was observed that the amount of released citronella oil was increased with increasing stirring speed and emulsifier concentration in the microcapsule preparation step. Polyurethane microcapsules containing citronella oil showed excellent anti-moth property. (author). 28 refs., 1 tab., 12 figs.

  17. Corrosion Prevention of Aluminum Nanoparticles by a Polyurethane Coating.

    Science.gov (United States)

    Nishimura, Toshiyasu; Raman, Vedarajan

    2014-06-19

    In order to prevent corrosion, aluminum nanoparticles were coated with a polyurethane polymer. The coverage of the polyurethane polymer was controlled from 0 to 100%, which changed the corrosion rate of the nanoparticles quantitatively. The surface of the polymer coating was investigated by Transmission Electron Microscopy (TEM) and Atomic Force Microscopy (AFM), and the corrosion resistance of the nanoparticles was estimated by a wet/dry corrosion test on a Pt plate with a NaCl solution. From a TEM with EDAX analysis, the 10 mass% polymer coated Al particles in the synthesis were almost 100% covered on the surface by a polymer film of 10 nm thick. On the other hand, the 3 mass% polymer coated Al was almost 40% covered by a film. In the AFM, the potential around the Al particles had a relatively low value with the polymer coating, which indicated that the conductivity of the Al was isolated from the Pt plate by the polymer. Both the corrosion and H₂ evolution reaction rates were quantitatively reduced by the mass% of polymer coating. In the case of the 10 mass% coated sample, there was no corrosion of Al nanoparticles. This fact suggested that the electrochemical reaction was suppressed by the polymer coating. Moreover, the reaction rate of Al nanoparticles was suppressed in proportion to the coverage percentage of the coating. Thus, to conclude, it was found that the corrosion rate of Al nanoparticles could be quantitatively suppressed by the coverage percentage of the polymer coating.

  18. Effect of the ionizing radiation in polyurethane of medical grade

    International Nuclear Information System (INIS)

    Ceron, P.; Rivera, T.; Calderon, J. A.; Paredes, L.

    2011-10-01

    The polyurethane is a material broadly used in implant medical devices, such as the connection blocks of the pacemakers and the insulator of the electrodes. Some patients that are users of these devices possibly have the necessity to receive external radiotherapy. For that reason is necessary to know the effects induced by the ionizing radiation in this polymer. In this study samples of Pellethane 2363 80a (thermoplastic polyurethane of medical grade) were irradiated. It was used the same energy and absorbed dose of a treatment of external radiotherapy in pelvis, by means of a linear accelerator of X-rays of 6 MeV and absorbed dose of 60 Gy to isocenter. The irradiation corresponding to the gamma sterilization of the material was reproduced (1, 5, 7.5, 10 and 25 kGy for the Co 60) the effects induced by the radiotherapy and for the sterilization in the material were studied by means of an analysis of the chemical connection, the molecular structure and identification of the functional groups of the polymer, by means of the infrared spectroscopy by Fourier transform in the infrared half region. (Author)

  19. Polyurethane/polylactide-based biomaterials combined with rat olfactory bulb-derived glial cells and adipose-derived mesenchymal stromal cells for neural regenerative medicine applications

    Energy Technology Data Exchange (ETDEWEB)

    Grzesiak, Jakub, E-mail: grzesiak.kuba@gmail.com [Electron Microscopy Laboratory, University of Environmental and Life Sciences, Kozuchowska 5b, 51-631 Wroclaw (Poland); Marycz, Krzysztof [Electron Microscopy Laboratory, University of Environmental and Life Sciences, Kozuchowska 5b, 51-631 Wroclaw (Poland); Szarek, Dariusz [Department of Neurosurgery, Lower Silesia Specialist Hospital of T. Marciniak, Emergency Medicine Center, Traugutta 116, 50-420 Wroclaw (Poland); Bednarz, Paulina [State Higher Vocational School in Tarnów, Mickiewicza 8, 33-100 Tarnów (Poland); Laska, Jadwiga [AGH University of Science and Technology, Faculty of Materials Science and Ceramics, Mickiewicza 30, 30-059 Kraków (Poland)

    2015-07-01

    Research concerning the elaboration and application of biomaterial which may support the nerve tissue regeneration is currently one of the most promising directions. Biocompatible polymer devices are noteworthy group among the numerous types of potentially attractive biomaterials for regenerative medicine application. Polylactides and polyurethanes may be utilized for developing devices for supporting the nerve regeneration, like nerve guide conduits or bridges connecting the endings of broken nerve tracts. Moreover, the combination of these biomaterial devices with regenerative cell populations, like stem or precursor cells should significantly improve the final therapeutic effect. Therefore, the composition and structure of final device should support the proper adhesion and growth of cells destined for clinical application. In current research, the three polymer mats elaborated for connecting the broken nerve tracts, made from polylactide, polyurethane and their blend were evaluated both for physical properties and in vitro, using the olfactory-bulb glial cells and mesenchymal stem cells. The evaluation of Young's modulus, wettability and roughness of obtained materials showed the differences between analyzed samples. The analysis of cell adhesion, proliferation and morphology showed that the polyurethane–polylactide blend was the most neutral for cells in culture, while in the pure polymer samples there were significant alterations observed. Our results indicated that polyurethane–polylactide blend is an optimal composition for culturing and delivery of glial and mesenchymal stem cells. - Highlights: • Polyurethane–polylactide blends exhibit different characteristics from pure polymers. • Pure PU and PLA negatively influence on morphology of glial and mesenchymal cells. • PU/PLA blend was neutral for glial and mesenchymal cell proliferation and morphology.

  20. Polyurethane/polylactide-based biomaterials combined with rat olfactory bulb-derived glial cells and adipose-derived mesenchymal stromal cells for neural regenerative medicine applications

    International Nuclear Information System (INIS)

    Grzesiak, Jakub; Marycz, Krzysztof; Szarek, Dariusz; Bednarz, Paulina; Laska, Jadwiga

    2015-01-01

    Research concerning the elaboration and application of biomaterial which may support the nerve tissue regeneration is currently one of the most promising directions. Biocompatible polymer devices are noteworthy group among the numerous types of potentially attractive biomaterials for regenerative medicine application. Polylactides and polyurethanes may be utilized for developing devices for supporting the nerve regeneration, like nerve guide conduits or bridges connecting the endings of broken nerve tracts. Moreover, the combination of these biomaterial devices with regenerative cell populations, like stem or precursor cells should significantly improve the final therapeutic effect. Therefore, the composition and structure of final device should support the proper adhesion and growth of cells destined for clinical application. In current research, the three polymer mats elaborated for connecting the broken nerve tracts, made from polylactide, polyurethane and their blend were evaluated both for physical properties and in vitro, using the olfactory-bulb glial cells and mesenchymal stem cells. The evaluation of Young's modulus, wettability and roughness of obtained materials showed the differences between analyzed samples. The analysis of cell adhesion, proliferation and morphology showed that the polyurethane–polylactide blend was the most neutral for cells in culture, while in the pure polymer samples there were significant alterations observed. Our results indicated that polyurethane–polylactide blend is an optimal composition for culturing and delivery of glial and mesenchymal stem cells. - Highlights: • Polyurethane–polylactide blends exhibit different characteristics from pure polymers. • Pure PU and PLA negatively influence on morphology of glial and mesenchymal cells. • PU/PLA blend was neutral for glial and mesenchymal cell proliferation and morphology

  1. Universal adhesives: the next evolution in adhesive dentistry?

    Science.gov (United States)

    Alex, Gary

    2015-01-01

    Every so often a new material, technique, or technological breakthrough spurs a paradigm shift in the way dentistry is practiced. The development and evolution of reliable enamel and dentin bonding agents is one such example. Indeed, the so-called "cosmetic revolution" in dentistry blossomed in large part due to dramatic advances in adhesive technology. It is the ability to bond various materials in a reasonably predictable fashion to both enamel and dentin substrates that enables dentists to routinely place porcelain veneers, direct and indirect composites, and a plethora of other restorative and esthetic materials. In fact, the longevity and predictability of many (if not most) current restorative procedures is wholly predicated on the dentist's ability to bond various materials to tooth tissues. Adhesive systems have progressed from the largely ineffective systems of the 1970s and early 1980s to the relatively successful total- and self-etching systems of today. The latest players in the adhesive marketplace are the so-called "universal adhesives." In theory, these systems have the potential to significantly simplify and expedite adhesive protocols and may indeed represent the next evolution in adhesive dentistry. But what defines a universal system, and are all these new systems truly "universal" and everything they are claimed to be? This article will examine the origin, chemistry, strengths, weaknesses, and clinical relevance of this new genre of dental adhesives.

  2. Comparison of polyurethane with cyanoacrylate in hemostasis of vascular injury in guinea pigs.

    Science.gov (United States)

    Kubrusly, Luiz Fernando; Formighieri, Marina Simões; Lago, José Vitor Martins; Graça, Yorgos Luiz Santos de Salles; Sobral, Ana Cristina Lira; Lago, Marianna Martins

    2015-01-01

    To evaluate the behavior of castor oil-derived polyurethane as a hemostatic agent and tissue response after abdominal aortic injury and to compare it with 2-octyl-cyanoacrylate. Twenty-four Guinea Pigs were randomly divided into three groups of eight animals (I, II, and III). The infrarenal abdominal aorta was dissected, clamped proximally and distally to the vascular puncture site. In group I (control), hemostasis was achieved with digital pressure; in group II (polyurethane) castor oil-derived polyurethane was applied, and in group III (cyanoacrylate), 2-octyl-cyanoacrylate was used. Group II was subdivided into IIA and IIB according to the time of preparation of the hemostatic agent. Mean blood loss in groups IIA, IIB and III was 0.002 grams (g), 0.008 g, and 0.170 g, with standard deviation of 0.005 g, 0.005 g, and 0.424 g, respectively (P=0.069). The drying time for cyanoacrylate averaged 81.5 seconds (s) (standard deviation: 51.5 seconds) and 126.1 s (standard deviation: 23.0 s) for polyurethane B (P=0.046). However, there was a trend (P=0.069) for cyanoacrylate to dry more slowly than polyurethane A (mean: 40.5 s; SD: 8.6 s). Furthermore, polyurethane A had a shorter drying time than polyurethane B (P=0.003), mean IIA of 40.5 s (standard deviation: 8.6 s). In group III, 100% of the animals had mild/severe fibrosis, while in group II only 12.5% showed this degree of fibrosis (P=0.001). Polyurethane derived from castor oil showed similar hemostatic behavior to octyl-2-cyanoacrylate. There was less perivascular tissue response with polyurethane when compared with cyanoacrylate.

  3. Guiding the orientation of smooth muscle cells on random and aligned polyurethane/collagen nanofibers.

    Science.gov (United States)

    Jia, Lin; Prabhakaran, Molamma P; Qin, Xiaohong; Ramakrishna, Seeram

    2014-09-01

    Fabricating scaffolds that can simulate the architecture and functionality of native extracellular matrix is a huge challenge in vascular tissue engineering. Various kinds of materials are engineered via nano-technological approaches to meet the current challenges in vascular tissue regeneration. During this study, nanofibers from pure polyurethane and hybrid polyurethane/collagen in two different morphologies (random and aligned) and in three different ratios of polyurethane:collagen (75:25; 50:50; 25:75) are fabricated by electrospinning. The fiber diameters of the nanofibrous scaffolds are in the range of 174-453 nm and 145-419 for random and aligned fibers, respectively, where they closely mimic the nanoscale dimensions of native extracellular matrix. The aligned polyurethane/collagen nanofibers expressed anisotropic wettability with mechanical properties which is suitable for regeneration of the artery. After 12 days of human aortic smooth muscle cells culture on different scaffolds, the proliferation of smooth muscle cells on hybrid polyurethane/collagen (3:1) nanofibers was 173% and 212% higher than on pure polyurethane scaffolds for random and aligned scaffolds, respectively. The results of cell morphology and protein staining showed that the aligned polyurethane/collagen (3:1) scaffold promote smooth muscle cells alignment through contact guidance, while the random polyurethane/collagen (3:1) also guided cell orientation most probably due to the inherent biochemical composition. Our studies demonstrate the potential of aligned and random polyurethane/collagen (3:1) as promising substrates for vascular tissue regeneration. © The Author(s) 2014 Reprints and permissions: sagepub.co.uk/journalsPermissions.nav.

  4. Comparison of polyurethane with cyanoacrylate in hemostasis of vascular injury in guinea pigs

    Directory of Open Access Journals (Sweden)

    Luiz Fernando Kubrusly

    2015-02-01

    Full Text Available Objective: To evaluate the behavior of castor oil-derived polyurethane as a hemostatic agent and tissue response after abdominal aortic injury and to compare it with 2-octyl-cyanoacrylate. Methods: Twenty-four Guinea Pigs were randomly divided into three groups of eight animals (I, II, and III. The infrarenal abdominal aorta was dissected, clamped proximally and distally to the vascular puncture site. In group I (control, hemostasis was achieved with digital pressure; in group II (polyurethane castor oil-derived polyurethane was applied, and in group III (cyanoacrylate, 2-octyl-cyanoacrylate was used. Group II was subdivided into IIA and IIB according to the time of preparation of the hemostatic agent. Results: Mean blood loss in groups IIA, IIB and III was 0.002 grams (g, 0.008 g, and 0.170 g, with standard deviation of 0.005 g, 0.005 g, and 0.424 g, respectively (P=0.069. The drying time for cyanoacrylate averaged 81.5 seconds (s (standard deviation: 51.5 seconds and 126.1 s (standard deviation: 23.0 s for polyurethane B (P=0.046. However, there was a trend (P=0.069 for cyanoacrylate to dry more slowly than polyurethane A (mean: 40.5 s; SD: 8.6 s. Furthermore, polyurethane A had a shorter drying time than polyurethane B (P=0.003, mean IIA of 40.5 s (standard deviation: 8.6 s. In group III, 100% of the animals had mild/severe fibrosis, while in group II only 12.5% showed this degree of fibrosis (P=0.001. Conclusion: Polyurethane derived from castor oil showed similar hemostatic behavior to octyl-2-cyanoacrylate. There was less perivascular tissue response with polyurethane when compared with cyanoacrylate.

  5. Influences of the Ratio of Polyol and MDI on the Acoustic Parameters of Polyurethane

    Science.gov (United States)

    Wang, Yonghua; Liu, Zheming; Wu, Haiquan; Zhang, Chengchun; Yu, Huadong; Ren, Luquan; Ichchou, Mohamed

    2018-05-01

    In this paper, the influence of different ratio of polyol and MDI on the absorption coefficient and acoustic parameters of polyurethane was studied. Ratio of 100:40 and 100:45 show the best sound absorption performance, and the change trend of transmission loss and sound absorption coefficient are opposite. The flow resistance increased with the increasing of the ratio of polyol and MDI, the greater the flow resistance, the worse the high frequency sound absorption property of the polyurethane. When the ratio of polyol and MDI keep 100:45, the minimum porosity of sample, the polyurethane porosity increase with the ratio of polyol and MDI increase.

  6. Thermal behaviour properties and corrosion resistance of organoclay/polyurethane film

    Science.gov (United States)

    Kurniawan, O.; Soegijono, B.

    2018-03-01

    Organoclay/polyurethane film composite was prepared by adding organoclay with different content (1, 3, and 5 wt.%) in polyurethane as a matrix. TGA and DSC showed decomposition temperature shifted to a lower point as organoclay content change. FT-IR spectra showed chemical bonding of organoclay and polyurethane as a matrix, which means that the bonding between filler and matrix occured and the composite was stronger but less bonding occur in composite with 5 wt.% organoclay. The corrosion resistance overall increased with the increasing organoclay content. Composite with 5 wt.% organoclay had more thermal stability and corrosion resistance may probably due to exfoliation of organoclay.

  7. Electron beam curable branched chain polyurethane acrylates for magnetic media coatings

    International Nuclear Information System (INIS)

    Ukachi, Takashi; Haga, Kei-ichi; Matsumura, Yoshio

    1989-01-01

    Electron beam curable binder resins have been studied to realize the high quality magnetic coatings. It was supposed that resins with a higher crosslink density could lead to magnetic coatings with higher abrasion resistance. Branched chain polyurethane acrylates show a higher degree of cure by irradiation with an electron beam in comparison with linear polyurethane acrylates. This paper describes the potential wear resistance between properties of magnetic coatings and the physical properties of the cured unpigmented branched chain polyurethane acrylates that were used as the binder resins. (author)

  8. Comparison between properties of polyurethane nano composites prepared by two different methods

    International Nuclear Information System (INIS)

    Barmar, M.; Barikani, M.; Fereidoonnia, M.

    2009-01-01

    In this work, a thermoplastic polyurethane elastomer model based on polytetramethylene glycol. toluene diisocyanate and 1,4-butanediol was selected and synthesized. According to this model two types of polyurethane nano composites were prepared by in situ polymerization and melt intercalation procedures. The organo-modified nano clay was used in nano composites samples in 0.4 weight percent level. The prepared nano composites were studied by WAXD, tensile and thermal analysis. Thermal properties of the nano composites were higher than those of pure polyurethane elastomers. Nano composites prepared via melt intercalation method showed a lower tensile strength and hardness than those prepared through in situ polymerization method

  9. Adhesion and multi-materials

    International Nuclear Information System (INIS)

    Schultz, J.

    1997-01-01

    Adhesion is a multidisciplinary science relevant to many practical fields. The main application of adhesion is bonding by adhesives. This technique is widely used in the industrial world and more specifically in the advanced technical domains. Adhesion is also involved in multi-component materials such as coatings, multilayer materials, polymer blends, composite materials... The multidisciplinary aspect of adhesion is well demonstrated by considering the wide variety of concepts, models and theories proposed for its description. An example of the adhesion between a fiber and a matrix in a composite material will lead to a general model relating the molecular properties of the interface to its capacity of stress transfer and hence to the macroscopic mechanical properties of the composite. This relationship is valid whatever the fiber (glass, carbon, polymeric) or the polymer matrix (thermoplastics, thermosetting). Any deviation from this model can be attributed to the existence of an interfacial zone or interphase exhibiting properties, mainly mechanical properties, different from the bulk matrix. Two examples are examined: the first one deals with the creation of a trans crystalline interphase in a semi-crystalline thermoplastic matrix and the second one is concerned with the formation of a pseudo glassy interphase in an elastomer matrix. These examples stress the need for complementary approaches in the understanding of adhesion phenomena at different levels of knowledge, from molecular to macroscopic. They also show how important it is to understand the mechanisms of formation of inter phases in order to be able to master the performance of multicomponent materials. (Author)

  10. Photovoltaic module with adhesion promoter

    Science.gov (United States)

    Xavier, Grace

    2013-10-08

    Photovoltaic modules with adhesion promoters and methods for fabricating photovoltaic modules with adhesion promoters are described. A photovoltaic module includes a solar cell including a first surface and a second surface, the second surface including a plurality of interspaced back-side contacts. A first glass layer is coupled to the first surface by a first encapsulating layer. A second glass layer is coupled to the second surface by a second encapsulating layer. At least a portion of the second encapsulating layer is bonded directly to the plurality of interspaced back-side contacts by an adhesion promoter.

  11. Adhesives from modified soy protein

    Science.gov (United States)

    Sun, Susan [Manhattan, KS; Wang, Donghai [Manhattan, KS; Zhong, Zhikai [Manhattan, KS; Yang, Guang [Shanghai, CN

    2008-08-26

    The present invention provides useful adhesive compositions having similar adhesive properties to conventional UF and PPF resins. The compositions generally include a protein portion and modifying ingredient portion selected from the group consisting of carboxyl-containing compounds, aldehyde-containing compounds, epoxy group-containing compounds, and mixtures thereof. The composition is preferably prepared at a pH level at or near the isoelectric point of the protein. In other preferred forms, the adhesive composition includes a protein portion and a carboxyl-containing group portion.

  12. Structural adhesives directory and databook

    CERN Document Server

    Wilson, Jo

    1996-01-01

    A worldwide directory of commercially available adhesive products for use in a wide range of engineering disciplines. Along with product names and suppliers, basic property data are tabulated and cross-referenced. The book is subdivided according to class of adhesive, with introductions to each class followed by comparison tables and datasheets for each adhesive. The datasheets contain detailed information, from product codes to environmental properties and are therefore of interest across a broad readership. Standardized data will aid the user in cross-comparison between different manufacturers and in easily identifying the required information.

  13. Comparing Soy Flour Wood Adhesives to Purified Soy Protein Adhesives

    Science.gov (United States)

    Charles R. Frihart; Linda F. Lorenz

    2013-01-01

    While economics dictate that soy-based wood adhesives be made with soy flour, much of the recent literature on soy-based wood adhesives has involved using soy protein isolate. The obvious assumption is that the additional carbohydrates in the flour but not in the isolate only serve as inert diluents. Our studies have shown that the isolate can provide 10 times the wet...

  14. Bacterial endotoxin adhesion to different types of orthodontic adhesives

    Directory of Open Access Journals (Sweden)

    Priscilla Coutinho ROMUALDO

    Full Text Available Abstract Bacterial endotoxin (LPS adhesion to orthodontic brackets is a known contributing factor to inflammation of the adjacent gingival tissues. Objective The aim of this study was to assess whether LPS adheres to orthodontic adhesive systems, comparing two commercial brands. Material and Methods Forty specimens were fabricated from Transbond XT and Light Bond composite and bonding agent components (n=10/component, then contaminated by immersion in a bacterial endotoxin solution. Contaminated and non-contaminated acrylic resin samples were used as positive and negative control groups, respectively. LPS quantification was performed by the Limulus Amebocyte Lysate QCL-1000™ test. Data obtained were scored and subjected to the Chi-square test using a significance level of 5%. Results There was endotoxin adhesion to all materials (p0.05. There was no significant difference (p>0.05 among commercial brands. Affinity of endotoxin was significantly greater for the bonding agents (p=0.0025. Conclusions LPS adhered to both orthodontic adhesive systems. Regardless of the brand, the endotoxin had higher affinity for the bonding agents than for the composites. There is no previous study assessing the affinity of LPS for orthodontic adhesive systems. This study revealed that LPS adheres to orthodontic adhesive systems. Therefore, additional care is recommended to orthodontic applications of these materials.

  15. Influence of therapeutic radiation on polycaprolactone and polyurethane biomaterials

    Energy Technology Data Exchange (ETDEWEB)

    Cooke, Shelley L. [Department of Materials Science and Engineering, Virginia Polytechnic Institute and State University, Blacksburg, VA 24061 (United States); Whittington, Abby R., E-mail: awhit@mse.vt.edu [Department of Materials Science and Engineering, Virginia Polytechnic Institute and State University, Blacksburg, VA 24061 (United States); Department of Chemical Engineering, Virginia Polytechnic Institute and State University, Blacksburg, VA 24061 (United States)

    2016-03-01

    ABSTRACT: Biomedical polymers are exposed in vivo to ionizing radiation as implants, coatings and bystander materials. High levels of ionizing radiation (e.g. X-ray and gamma) have been reported to cause degradation and/or cross-linking in many polymers. This pilot study sought to determine causes of failure, by investigating how therapeutic radiation affects two different porous polymeric scaffolds: polycaprolactone (PCL) and polyurethane (PU). PCL is a bioresorbable material used in biomedical devices (e.g., dentistry, internal fixation devices and targeted drug delivery capsules). PU is commonly used in medical applications (e.g., coatings for pacemakers, tissue expanders, catheter tubing and wound dressings). PU was specifically fabricated to be a non-degradable polymer in this study. Porous scaffolds, fabricated using solvent casting and/or salt leeching techniques, were placed in phosphate buffered saline (PBS, pH = 7.4) and exposed to typical cancer radiotherapy. A total dose of 50 Gy was broken into 25 doses over an eleven-week period. Collected PBS was tested for polymer leachants and degradation products using Gas Chromatography Mass Spectroscopy (GC–MS), results revealed no analyzable leachants from either polymer. Scaffolds were characterized using Environmental Scanning Electron Microscopy, Size-exclusion chromatography (SEC), Differential Scanning Calorimetry (DSC) and Fourier Transform Infrared Spectroscopy (FTIR). No gross visual changes were observed in either polymer, however PU exhibited microstructure changes after irradiation. Increased number average molecular weight and weight average molecular weight in PCL and PU were observed after irradiation, indicating crosslinking. PU displayed an increase in intrinsic viscosity that further confirms increased crosslinking. PCL and PU showed decreases in crystallinity after irradiation, and PU crystallinity shifted from long-range-order hard segments to short-range-order hard segments after

  16. Influence of therapeutic radiation on polycaprolactone and polyurethane biomaterials

    International Nuclear Information System (INIS)

    Cooke, Shelley L.; Whittington, Abby R.

    2016-01-01

    ABSTRACT: Biomedical polymers are exposed in vivo to ionizing radiation as implants, coatings and bystander materials. High levels of ionizing radiation (e.g. X-ray and gamma) have been reported to cause degradation and/or cross-linking in many polymers. This pilot study sought to determine causes of failure, by investigating how therapeutic radiation affects two different porous polymeric scaffolds: polycaprolactone (PCL) and polyurethane (PU). PCL is a bioresorbable material used in biomedical devices (e.g., dentistry, internal fixation devices and targeted drug delivery capsules). PU is commonly used in medical applications (e.g., coatings for pacemakers, tissue expanders, catheter tubing and wound dressings). PU was specifically fabricated to be a non-degradable polymer in this study. Porous scaffolds, fabricated using solvent casting and/or salt leeching techniques, were placed in phosphate buffered saline (PBS, pH = 7.4) and exposed to typical cancer radiotherapy. A total dose of 50 Gy was broken into 25 doses over an eleven-week period. Collected PBS was tested for polymer leachants and degradation products using Gas Chromatography Mass Spectroscopy (GC–MS), results revealed no analyzable leachants from either polymer. Scaffolds were characterized using Environmental Scanning Electron Microscopy, Size-exclusion chromatography (SEC), Differential Scanning Calorimetry (DSC) and Fourier Transform Infrared Spectroscopy (FTIR). No gross visual changes were observed in either polymer, however PU exhibited microstructure changes after irradiation. Increased number average molecular weight and weight average molecular weight in PCL and PU were observed after irradiation, indicating crosslinking. PU displayed an increase in intrinsic viscosity that further confirms increased crosslinking. PCL and PU showed decreases in crystallinity after irradiation, and PU crystallinity shifted from long-range-order hard segments to short-range-order hard segments after

  17. The influence of conditioning film on antifouling properties of the polyurethane film modified by chondroitin sulfate in urine

    Science.gov (United States)

    Yuan, Huihui; Qian, Bin; Chen, Huaying; Lan, Minbo

    2017-12-01

    The encrustation and induced infection severely impact on the therapeutic effectiveness and service life of urinary stents due to the fast formation of conditioning film on urinary stents after implantation. The composition and properties of conditioning film have great influence on antifouling properties of stent materials. In our previous work, we modified polyurethane films by chondroitin sulfate (PU-CS) with different CS grafting densities to verify its anti-fouling properties. To obtain the in-depth understanding of encrustation on urinary stents, we investigated the impact of the composition and properties of conditioning film on the following inorganic salt deposition and bacteria adhesion in urine. The results showed that quantity of proteins and polysaccharides in conditioning films, and the roughness, water contact angle and zeta potential of PU-CSs covered with corresponding conditioning film decreased with the increase of CS grafting density on PU films.PU-CS(3) with highest CS grafting density (3.70 g/cm2) had the highest bacteria inhibition rate and least inorganic salt deposition among the PU-CSs in artificial urine. Moreover, inorganic salts depositing on the PU-CS(3) were less and smaller than those on other films. Bacteria were not detectable until day 21 in real urine. Meanwhile, the pH value was elevated. The results suggested that the component of conditioning films was more important than other surface properties such as hydrophilicity, zeta potential and roughness for inorganic salt deposition and bacteria adhesion. Moreover, the anti-encrustation properties of the surface was promoted by proteins and inhibited by polysaccharides.

  18. Preparation and properties of high storage stability polyester polyol dispersion for two-component waterborne polyurethane coating

    Science.gov (United States)

    Hao, H.; Hu, J. Q.; Wang, F.; Tu, W. P.

    2017-01-01

    A new type of polyester polyol dispersion with good storage stability was prepared based on a hydrophilic monomer 5-sodium sulfodimethyl isophthalate (5-SIPM), and frequently-used monomers such as neopentyl glycol (NPG), dimethyl terephthalate (DMT), dimethyl phthalate (DMP) and trimethylolpropane (TMP) by the transpolycondensation and polycondensation method. The polyester polyol dispersion was characterized by FTIR and GPC. The proper content of these monomers were determined by the performance of polyester dispersion: the content of TMP was 15wt%, the content of NPG was 7.5wt% and the hydrophilic monomer 5-SIPM content was 5wt%. Two-component waterborne polyurethane (2K-WPU) coatings were prepared by Bayhydur® XP2487/1 and polyester polyol dispersions, which were stored before and after at 40 ° for 6 weeks, the prepared films have no differences in drying time, adhesion, pencil hardness, gloss and chemical resistance, the result also reveals that the polyester polyol dispersion have excellent storage stability resistance.

  19. Enhancement of the thermal and mechanical properties of polyurethane/polyvinyl chloride blend by loading single walled carbon nanotubes

    Directory of Open Access Journals (Sweden)

    A.M. Hezma

    2017-06-01

    Full Text Available Structural, thermal, and mechanical properties of pure blend and nanocomposites based on polyurethane (PU and polyvinyl chloride (PVC doped with low different content of single walled-carbon nanotubes (SWCNTs were studied. The nanocomposites at different concentration were prepared via casting technique. The interaction between PU/PVC and CNTs were examined via FT-IR studies. The changes in the structures of the nanocomposites were examined using X- Ray Diffraction (XRD, and the results indicated that the amorphous domains of nanocomposites increased with increasing SWCNTs content. Transmission electron microscope (TEM observation indicated that SWCNTs surface was wrapped with the polymer with the thermal properties of nanocomposites improved. The mechanical behavior of the nanocomposites was evaluated as a function of SWCNTs content. The main enhancement in tensile properties was observed, e.g., the tensile strength and elastic modulus increased compared with the pure blend, which may be attributed to the interaction and adhesion between CNTs and the polymer matrices due to the hydrogen bonding between carbonyl groups (C=O of polymer blend chains and carboxylic acid (COOH groups of CNTs.

  20. Thermoresponsive polyurethane/siloxane membrane for wound dressing and cell sheet transplantation: In-vitro and in-vivo studies

    Energy Technology Data Exchange (ETDEWEB)

    Rezapour-Lactoee, Alireza [Department of Tissue Engineering, School of Advanced Medical Technologies, Tehran University of Medical Sciences, 14177-55469 Tehran (Iran, Islamic Republic of); Yeganeh, Hamid, E-mail: h.yeganeh@ippi.ac.ir [Iran Polymer and Petrochemical Institute, P.O. Box: 14965/115, Tehran (Iran, Islamic Republic of); Ostad, Seyed Nasser, E-mail: ostadnas@sina.tums.ac.ir [Department of Tissue Engineering, School of Advanced Medical Technologies, Tehran University of Medical Sciences, 14177-55469 Tehran (Iran, Islamic Republic of); Department of Pharmacology and Toxicology, Faculty of Pharmacy, Tehran University of Medical Sciences, 16 Azar St, Enqelab Sq, Tehran 1417614411 (Iran, Islamic Republic of); Gharibi, Reza [Department of Tissue Engineering, School of Advanced Medical Technologies, Tehran University of Medical Sciences, 14177-55469 Tehran (Iran, Islamic Republic of); Mazaheri, Zohreh [Department of Anatomical Sciences, Faculty of Medical Sciences, Tarbiat Modares University, Tehran (Iran, Islamic Republic of); Ai, Jafar [Department of Tissue Engineering, School of Advanced Medical Technologies, Tehran University of Medical Sciences, 14177-55469 Tehran (Iran, Islamic Republic of)

    2016-12-01

    Polyurethane/siloxane based wound dressing for transferring fibroblast cell sheet to wounded skin and ability to provide an optimum condition for cellular activity at damaged tissue was prepared in this research. The dressing was made thermoresponsive, via the introduction of a poly(N-isopropyl acrylamide) copolymer into the backbone of dressing. The ability of membrane for adhesion, growth, and proliferation of fibroblast cells was improved via surface modification with gelatin. The optimized dressing exhibited appropriate tensile strength (4.5 MPa) and elongation at break (80%) to protect wound against physical forces. Due to controlled equilibrium water absorption of about 89% and water vapor transmission rate of 2040 g/m{sup 2} day, the dressing could maintain the favorable moist environment over moderate to high exuding wounds. The grown cell sheet on dressing membrane could easily roll up from the surface just with lowering the temperature. The in vivo study of the wound dressed with cell loaded membrane confirmed the accelerated healing and production of tissue with complete re-epithelization, enhanced vascularization, and increased collagen deposition on the damaged area. - Highlights: • Versatile polymerization procedure to prepare wound dressing membranes • Improved cytocompatibility to support growth and proliferation of seeded fibroblasts • Utilizing thermoresponsive characteristic to transfer cell sheet to damaged tissue • Excellent physicomechanical properties of dressings to protect wound bed • Excellent fluid handling to provide moist environment over wounded tissue.