  1. Formability of Annealed Ni-Ti Shape Memory Alloy Sheet

    Science.gov (United States)

    Fann, K. J.; Su, J. Y.; Chang, C. H.

    2018-03-01

    Ni-Ti shape memory alloy has two specific properties, superelasiticity and shape memory effect, and thus is widely applied in diverse industries. To extend its application, this study attempts to investigate the strength and cold formability of its sheet blank, which is annealed at various temperatures, by hardness test and by Erichsen-like cupping test. As a result, the higher the annealing temperature, the lower the hardness, the lower the maximum punch load as the sheet blank fractured, and the lower the Erichsen-like index or the lower the formability. In general, the Ni-Ti sheet after annealing has an Erichsen-like index between 8 mm and 9 mm. This study has also confirmed via DSC that the Ni-Ti shape memory alloy possesses the austenitic phase and shows the superelasticity at room temperature.

  2. NiTiCu/AlN/NiTiCu shape memory thin film heterostructures for vibration damping in MEMS

    Energy Technology Data Exchange (ETDEWEB)

    Kaur, Navjot; Kaur, Davinder, E-mail: dkaurfph@iitr.ernet.in

    2014-03-25

    Highlights: • Fabrication of NiTiCu/AlN/NiTiCu heterostructure using dc/rf magnetron sputtering. • Exhibits highest hardness (38 GPa) and elastic modulus (187 GPa). • Enhanced dissipation of mechanical energy (E{sub d} = 5.7 N J). • High damping capacity (0.052) and figure of merit (∼0.62). • Can be applied for vibration damping in MEMS. -- Abstract: Shape memory alloy (NiTiCu) thin films coupled with piezoelectric AlN layer produce an intelligent material for vibration damping. In the present study pure NiTiCu, NiTiCu/AlN and NiTiCu/AlN/NiTiCu heterostructures have been deposited on Si substrate using magnetron sputtering technique. By the use of the interfaces and shape memory effect provided by NiTiCu layers, the damping capacity can be increased along with increase in stiffness and mechanical hardness. The heterostructures were characterized in terms of structural, electrical, morphological and mechanical properties by X-ray diffraction (XRD), four probe resistivity method, atomic force microscopy, field emission scanning electron microscopy, and nanoindentation. The NiTiCu/AlN/NiTiCu heterostructure exhibit enhanced mechanical and damping properties as compared to NiTiCu/AlN and pure NiTiCu. This enhancement in hardness and damping of the heterostructure could be attributed to the shape memory effect of NiTiCu, intrinsic piezoelectricity of AlN and increased number of interfaces in heterostructure that help in dissipation of mechanical vibrations. The findings of this work provide additional impetus for the application of these heterostructures in emerging fields of nanotechnology and microelectro mechanical (MEMS) devices.

  3. NiTiCu/AlN/NiTiCu shape memory thin film heterostructures for vibration damping in MEMS

    International Nuclear Information System (INIS)

    Kaur, Navjot; Kaur, Davinder

    2014-01-01

    Highlights: • Fabrication of NiTiCu/AlN/NiTiCu heterostructure using dc/rf magnetron sputtering. • Exhibits highest hardness (38 GPa) and elastic modulus (187 GPa). • Enhanced dissipation of mechanical energy (E d = 5.7 N J). • High damping capacity (0.052) and figure of merit (∼0.62). • Can be applied for vibration damping in MEMS. -- Abstract: Shape memory alloy (NiTiCu) thin films coupled with piezoelectric AlN layer produce an intelligent material for vibration damping. In the present study pure NiTiCu, NiTiCu/AlN and NiTiCu/AlN/NiTiCu heterostructures have been deposited on Si substrate using magnetron sputtering technique. By the use of the interfaces and shape memory effect provided by NiTiCu layers, the damping capacity can be increased along with increase in stiffness and mechanical hardness. The heterostructures were characterized in terms of structural, electrical, morphological and mechanical properties by X-ray diffraction (XRD), four probe resistivity method, atomic force microscopy, field emission scanning electron microscopy, and nanoindentation. The NiTiCu/AlN/NiTiCu heterostructure exhibit enhanced mechanical and damping properties as compared to NiTiCu/AlN and pure NiTiCu. This enhancement in hardness and damping of the heterostructure could be attributed to the shape memory effect of NiTiCu, intrinsic piezoelectricity of AlN and increased number of interfaces in heterostructure that help in dissipation of mechanical vibrations. The findings of this work provide additional impetus for the application of these heterostructures in emerging fields of nanotechnology and microelectro mechanical (MEMS) devices

  4. Cold Forming of Ni-Ti Shape Memory Alloy Sheet

    Science.gov (United States)

    Fann, Kaung-Jau; Su, Jhe-Yung

    2018-03-01

    Ni-Ti shape memory alloy has two specific properties, superelasiticity and shape memory effect, and thus is widely applied in diverse industries. To extend its further application, this study attempts to investigate the feasibility of cold forming its sheet blank especially under a bi-axial tensile stress state. Not only experiments but also a Finite Element Analysis (FEA) with DEFORM 2D was conducted in this study. The material data for FEA was accomplished by the tensile test. An Erichsen-like cupping test was performed as well to determine the process parameter for experiment setup. As a result of the study, the Ni-Ti shape memory alloy sheet has a low formability for cold forming and shows a relative large springback after releasing the forming load.

  5. Thermomechanical model for NiTi shape memory wires

    International Nuclear Information System (INIS)

    Frost, M; Sedlák, P; Sippola, M; Šittner, P

    2010-01-01

    A simple one-dimensional rate-independent model is proposed. It is able to capture responses of a NiTi shape memory alloy wire element to mechanical and thermal loadings. Since the model takes into account martensitic phase transformation as well as deformation processes in the martensite, both shape memory effects and pseudoelasticity can be simulated. The model introduces non-hysteretic transformation strain. Particular attention was paid to description of partial loading cycles. By changing the input parameters the model can be adapted to various types of NiTi-based materials. The model was implemented in the finite element code Abaqus as a User routine and several simulations were performed to validate the implementation

  6. Confining jackets for concrete cylinders using NiTiNb and NiTi shape memory alloy wires

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Eunsoo; Yoon, Soon-Jong [Department of Civil Engineering, Hongik University, Seoul 121-791 (Korea, Republic of); Nam, Tae-Hyun [School of Materials Science and Engineering and ERI, Gyeongsang National University, Jinju, Gyeongnam 600-701 (Korea, Republic of); Cho, Sun-Kyu [School of Civil Engineering, Seoul National University of Technology, Seoul 139-743 (Korea, Republic of); Park, Joonam, E-mail: eunsoochoi@hongik.ac.k [Department of Railroad Structure Research, Korea Railroad Research Institute, Uiwang 437-050, Korea (Korea, Republic of)

    2010-05-01

    This study used prestrained NiTiNb and NiTi shape memory alloy (SMA) wires to confine concrete cylinders. The recovery stress of the wires was measured with respect to the maximal prestrain of the wires. SMA wires were preelongated during the manufacturing process and then wrapped around concrete cylinders of 150 mmx300 mm ({phi}xL). Unconfined concrete cylinders were tested for compressive strength and the results were compared to those of cylinders confined by SMA wires. NiTiNb SMA wires increased the compressive strength and ductility of the cylinders due to the confining effect. NiTiNb wires were found to be more effective in increasing the peak strength of the cylinders and dissipating energy than NiTi wires. This study showed the potential of the proposed method to retrofit reinforced concrete columns using SMA wires to protect them from earthquakes.

  7. Shape memory properties in NiTi alloys

    International Nuclear Information System (INIS)

    Airoldi, G.; Vicentini, B.; Ranucci, T.; Rivolta, B.

    1991-01-01

    Mechanical properties of shape memory NiTi alloys are here examined in the frame of literature's results. The operating temperature respect to the intrinsic transformation temperatures explains thoroughly the different stress-strain behaviour, ascribed to different deformation mechanisms acting and to their interplay. Attention is moreover paid to the stress-strain behaviour consequent to a different physical state (martensite phase or parent phase), obtained within the hysteresis cycle, at the same temperature. Evidence of oriented variants, selected by the applied stress, is also given

  8. Thermal processing of polycrystalline NiTi shape memory alloys

    International Nuclear Information System (INIS)

    Frick, Carl P.; Ortega, Alicia M.; Tyber, Jeffrey; Maksound, A.El.M.; Maier, Hans J.; Liu Yinong; Gall, Ken

    2005-01-01

    The objective of this study is to examine the effect of heat treatment on polycrystalline Ti-50.9 at.% Ni in hot-rolled and cold-drawn states. In particular, we examine microstructure, transformation temperatures as well as mechanical behavior in terms of both uniaxial monotonic testing and instrumented Vickers micro-indentation. The results constitute a fundamental understanding of the effect of heat treatment on thermal/stress-induced martensite and resistance to plastic flow in NiTi, all of which are critical for optimizing the mechanical properties. The high temperature of the hot-rolling process caused recrystallization, recovery, and hindered precipitate formation, essentially solutionizing the NiTi. The subsequent cold-drawing-induced a high density of dislocations and martensite. Heat treatments were carried out on hot-rolled, as well as, hot-rolled then cold-drawn materials at various temperatures for 1.5 h. Transmission Electron Microscopy observations revealed that Ti 3 Ni 4 precipitates progressively increased in size and changed their interface with the matrix from being coherent to incoherent with increasing heat treatment temperature. Accompanying the changes in precipitate size and interface coherency, transformation temperatures were observed to systematically shift, leading to the occurrence of the R-phase and multiple-stage transformations. Room temperature stress-strain tests illustrated a variety of mechanical responses for the various heat treatments, from pseudoelasticity to shape memory. The changes in stress-strain behavior are interpreted in terms of shifts in the primary martensite transformation temperatures, rather then the occurrence of the R-phase transformation. The results confirm that Ti 3 Ni 4 precipitates can be used to elicit a desired isothermal stress-strain behavior in polycrystalline NiTi. Instrumented micro-indention tests revealed that Martens (Universal) Hardness values are more dependent on the resistance to dislocation

  9. Nitride coating enhances endothelialization on biomedical NiTi shape memory alloy

    Energy Technology Data Exchange (ETDEWEB)

    Ion, Raluca [University of Bucharest, Department of Biochemistry and Molecular Biology, 91-95 Spl. Independentei, 050095 Bucharest (Romania); Luculescu, Catalin [National Institute for Laser, Plasma and Radiation Physics, 409 Atomistilor, P.O. Box MG-36, 077125 Magurele-Bucharest (Romania); Cimpean, Anisoara, E-mail: anisoara.cimpean@bio.unibuc.ro [University of Bucharest, Department of Biochemistry and Molecular Biology, 91-95 Spl. Independentei, 050095 Bucharest (Romania); Marx, Philippe [AMF Company, Route de Quincy, 18120 Lury-sur-Arnon (France); Gordin, Doina-Margareta; Gloriant, Thierry [INSA Rennes, UMR CNRS 6226 ISCR, 20 Avenue des Buttes de Coësmes, 35708 Rennes Cedex 7 (France)

    2016-05-01

    Surface nitriding was demonstrated to be an effective process for improving the biocompatibility of implantable devices. In this study, we investigated the benefits of nitriding the NiTi shape memory alloy for vascular stent applications. Results from cell experiments indicated that, compared to untreated NiTi, a superficial gas nitriding treatment enhanced the adhesion of human umbilical vein endothelial cells (HUVECs), cell spreading and proliferation. This investigation provides data to demonstrate the possibility of improving the rate of endothelialization on NiTi by means of nitride coating. - Highlights: • Gas nitriding process of NiTi is competent to promote cell spreading. • Surface nitriding of NiTi is able to stimulate focal adhesion formation and cell proliferation. • Similar expression pattern of vWf and eNOS was exhibited by bare and nitrided NiTi. • Gas nitriding treatment of NiTi shows promise for better in vivo endothelialization.

  10. Cyclic deformation of NiTi shape memory alloys

    International Nuclear Information System (INIS)

    Liu Yong; Van Humbeeck, J.; Xie Zeliang

    1999-01-01

    Recently, there is an increasing interest in applying the high damping capacity of shape memory alloys (SMAs). The purpose is to explore the feasibility of those materials for the protection of buildings and other civil constructions as a result of earthquake damages. So far, few experimental results have been reported concerning the mechanical cyclic behaviour of SMAs in their martensitic state (ferroelastic). In the present work, the experimental results on the mechanical behaviour of martensitic NiTi SMAs under tension-compression cyclic deformation up to strains of ±4% are summarized with major attention to the damping capacity, characteristic stresses and strains as a function of deformation cycles. Effect of strain rate, strain amplitude and annealing condition on the martensite damping is summarized. Explanation of the cyclic hardening and cyclic softening phenomenon is proposed based on TEM observations. (orig.)

  11. A Review of Selective Laser Melted NiTi Shape Memory Alloy

    Science.gov (United States)

    Khoo, Zhong Xun; Shen, Yu Fang

    2018-01-01

    NiTi shape memory alloys (SMAs) have the best combination of properties among the different SMAs. However, the limitations of conventional manufacturing processes and the poor manufacturability of NiTi have critically limited its full potential applicability. Thus, additive manufacturing, commonly known as 3D printing, has the potential to be a solution in fabricating complex NiTi smart structures. Recently, a number of studies on Selective Laser Melting (SLM) of NiTi were conducted to explore the various aspects of SLM-produced NiTi. Compared to producing conventional metals through the SLM process, the fabrication of NiTi SMA is much more challenging. Not only do the produced parts require a high density that leads to good mechanical properties, strict composition control is needed as well for the SLM NiTi to possess suitable phase transformation characteristics. Additionally, obtaining a good shape memory effect from the SLM NiTi samples is another challenging task that requires further understanding. This paper presents the results of the effects of energy density and SLM process parameters on the properties of SLM NiTi. Its shape memory properties and potential applications were then reviewed and discussed. PMID:29596320

  12. Surface microstructures and corrosion resistance of Ni-Ti-Nb shape memory thin films

    Science.gov (United States)

    Li, Kun; Li, Yan; Huang, Xu; Gibson, Des; Zheng, Yang; Liu, Jiao; Sun, Lu; Fu, Yong Qing

    2017-08-01

    Ni-Ti-Nb and Ni-Ti shape memory thin films were sputter-deposited onto silicon substrates and annealed at 600 °C for crystallization. X-ray diffraction (XRD) measurements indicated that all of the annealed Ni-Ti-Nb films were composed of crystalline Ni-Ti (Nb) and Nb-rich grains. X-ray photoelectron spectroscopy (XPS) tests showed that the surfaces of Ni-Ti-Nb films were covered with Ti oxides, NiO and Nb2O5. The corrosion resistance of the Ni-Ti-Nb films in 3.5 wt.% NaCl solution was investigated using electrochemical tests such as open-circuit potential (OCP) and potentio-dynamic polarization tests. Ni-Ti-Nb films showed higher OCPs, higher corrosion potentials (Ecorr) and lower corrosion current densities (icorr) than the binary Ni-Ti film, which indicated a better corrosion resistance. The reason may be that Nb additions modified the passive layer on the film surface. The OCPs of Ni-Ti-Nb films increased with further Nb additions, whereas no apparent difference of Ecorr and icorr was found among the Ni-Ti-Nb films.

  13. Surface microstructures and corrosion resistance of Ni-Ti-Nb shape memory thin films

    Energy Technology Data Exchange (ETDEWEB)

    Li, Kun [School of Materials Science and Engineering, Beihang University, Beijing 100191 (China); Beijing Key Laboratory for Advanced Functional Materials and Thin Film Technology, Beihang University, Beijing 100191 (China); Faculty of Engineering and Environment, Northumbria University, Newcastle Upon Tyne NE1 8ST (United Kingdom); Li, Yan, E-mail: liyan@buaa.edu.cn [School of Materials Science and Engineering, Beihang University, Beijing 100191 (China); Beijing Key Laboratory for Advanced Functional Materials and Thin Film Technology, Beihang University, Beijing 100191 (China); Huang, Xu [Memry Corporation, Bethel, CT 06801 (United States); Gibson, Des [Institute of Thin Films, Sensors & Imaging, Scottish Universities Physics Alliance, University of the West of Scotland, Paisley PA1 2BE (United Kingdom); Zheng, Yang; Liu, Jiao; Sun, Lu [School of Materials Science and Engineering, Beihang University, Beijing 100191 (China); Beijing Key Laboratory for Advanced Functional Materials and Thin Film Technology, Beihang University, Beijing 100191 (China); Fu, Yong Qing, E-mail: richard.fu@northumbria.ac.uk [Faculty of Engineering and Environment, Northumbria University, Newcastle Upon Tyne NE1 8ST (United Kingdom)

    2017-08-31

    Highlights: • The corrosion resistance of Ni-Ti-Nb shape memory thin films is investigated. • Modified surface oxide layers improve the corrosion resistance of Ni-Ti-Nb films. • Further Nb additions reduce the potential corrosion tendency of the films. - Abstract: Ni-Ti-Nb and Ni-Ti shape memory thin films were sputter-deposited onto silicon substrates and annealed at 600 °C for crystallization. X-ray diffraction (XRD) measurements indicated that all of the annealed Ni-Ti-Nb films were composed of crystalline Ni-Ti (Nb) and Nb-rich grains. X-ray photoelectron spectroscopy (XPS) tests showed that the surfaces of Ni-Ti-Nb films were covered with Ti oxides, NiO and Nb{sub 2}O{sub 5}. The corrosion resistance of the Ni-Ti-Nb films in 3.5 wt.% NaCl solution was investigated using electrochemical tests such as open-circuit potential (OCP) and potentio-dynamic polarization tests. Ni-Ti-Nb films showed higher OCPs, higher corrosion potentials (E{sub corr}) and lower corrosion current densities (i{sub corr}) than the binary Ni-Ti film, which indicated a better corrosion resistance. The reason may be that Nb additions modified the passive layer on the film surface. The OCPs of Ni-Ti-Nb films increased with further Nb additions, whereas no apparent difference of E{sub corr} and i{sub corr} was found among the Ni-Ti-Nb films.

  14. Fabrication of SLM NiTi Shape Memory Alloy via Repetitive Laser Scanning

    Science.gov (United States)

    Khoo, Zhong Xun; Liu, Yong; Low, Zhi Hong; An, Jia; Chua, Chee Kai; Leong, Kah Fai

    2018-01-01

    Additive manufacturing has the potential to overcome the poor machinability of NiTi shape-memory alloy in fabricating smart structures of complex geometry. In recent years, a number of research activities on selective laser melting (SLM) of NiTi have been carried out to explore the optimal parameters for producing SLM NiTi with the desired phase transformation characteristics and shape-memory properties. Different effects of energy density and processing parameters on the properties of SLM NiTi were reported. In this research, a new approach—repetitive laser scanning—is introduced to meet these objectives as well. The results suggested that the laser absorptivity and heat conductivity of materials before and after the first scan significantly influence the final properties of SLM NiTi. With carefully controlled repetitive scanning process, the fabricated samples have demonstrated shape-memory effect of as high as 5.11% (with an average value of 4.61%) and exhibited comparable transformation characteristics as the NiTi powder used. These results suggest the potential for fabricating complex NiTi structures with similar properties to that of the conventionally produced NiTi parts.

  15. Fabrication of SLM NiTi Shape Memory Alloy via Repetitive Laser Scanning

    Science.gov (United States)

    Khoo, Zhong Xun; Liu, Yong; Low, Zhi Hong; An, Jia; Chua, Chee Kai; Leong, Kah Fai

    2018-03-01

    Additive manufacturing has the potential to overcome the poor machinability of NiTi shape-memory alloy in fabricating smart structures of complex geometry. In recent years, a number of research activities on selective laser melting (SLM) of NiTi have been carried out to explore the optimal parameters for producing SLM NiTi with the desired phase transformation characteristics and shape-memory properties. Different effects of energy density and processing parameters on the properties of SLM NiTi were reported. In this research, a new approach—repetitive laser scanning—is introduced to meet these objectives as well. The results suggested that the laser absorptivity and heat conductivity of materials before and after the first scan significantly influence the final properties of SLM NiTi. With carefully controlled repetitive scanning process, the fabricated samples have demonstrated shape-memory effect of as high as 5.11% (with an average value of 4.61%) and exhibited comparable transformation characteristics as the NiTi powder used. These results suggest the potential for fabricating complex NiTi structures with similar properties to that of the conventionally produced NiTi parts.

  16. High Work Output Ni-Ti-Pt High Temperature Shape Memory Alloys and Associated Processing Methods

    Science.gov (United States)

    Noebe, Ronald D. (Inventor); Draper, Susan L. (Inventor); Nathal, Michael V. (Inventor); Garg, Anita (Inventor)

    2009-01-01

    According to the invention, compositions of Ni-Ti-Pt high temperature, high force, shape memory alloys are disclosed that have transition temperatures above 100 C.; have narrow hysteresis; and produce a high specific work output.

  17. Processing and Characterization of NiTi Shape Memory Alloy Particle Reinforced Sn-In Solders

    National Research Council Canada - National Science Library

    Chung, Kohn C

    2006-01-01

    .... In previous work, it was proposed that reinforcement of solder by NiTi shape memory alloy particles to form smart composite solder reduces the inelastic strain of the solder and hence, may enhance...

  18. Microstructure, mechanical and functional properties of NiTi-based shape memory ribbons

    International Nuclear Information System (INIS)

    Mehrabi, K.; Bruncko, M.; Kneissl, A.C.

    2012-01-01

    Highlights: ► Melt-spun samples exhibited martensite structure and shape memory effects immediately after processing at room temperature. ► Using a new etchant and interference contrast, it is possible to reveal the fine microstructures and grain boundaries. ► The martensite structure in NiTi is very fine, and nano-sized twin boundaries could be revealed using TEM only. ► Two-way effects have been successfully introduced by different thermomechanical training methods in NiTi, NiTiCu and NiTiW alloys, which can be used for several applications, e.g. microsensors and microactuators. - Abstract: The present work has been aimed to study the microstructures, functional properties and the influence of different thermomechanical training methods on the two-way shape memory effect in NiTi-based melt-spun ribbons. In order to get small-dimensioned shape memory alloys (SMAs) with good functional and mechanical properties, a rapid solidification technique was employed. Their fracture and elasticity characteristics have been determined, as well as shape memory properties by thermomechanical cycling. The ribbons were trained under tensile and bending deformation by thermal cycling through the phase transformation temperature range. The results displayed that all different training methods were effective in developing a two-way shape memory effect (TWSME). The influence of copper (5–25 at.% Cu) and tungsten (2 at.% W) on the microstructure, and the functional and mechanical behavior of NiTi thin ribbons was also investigated. All samples show a shape memory effect immediately after processing without further heat treatment. The melt-spun ribbons were trained under constant strain (bending and tensile deformation) by thermal cycling through the phase transformation temperature range. The addition of copper was effective to narrow the transformation hysteresis. The W addition has improved the TWSME stability of the NiTi alloys and mechanical properties. Results about

  19. Powder metallurgy of NiTi-alloys with defined shape memory properties

    International Nuclear Information System (INIS)

    Bram, M.; Ahmad-Khanlou, A.; Buchkremer, H.P.; Stoever, D.

    2001-01-01

    The aim of the present work is the development of fabrication processes for NiTi shape memory alloys by powder metallurgical means. The starting materials used were prealloyed powders as well as elemental powder mixtures. Three techniques seem to be very promising for shaping of NiTi compacts. Hot Isostatic Pressing (HIP) has been examined for the production of dense semi-finished components. A promising technique for the production of dense and porous coatings with an increased wear resistance is Vacuum Plasma Spraying (VPS). Metal Injection Moulding (MIM) is especially suitable for near-net shape fabrication of small components with a complex geometry considering that large numbers of units have to be produced for compensating high tool and process costs. Subsequently, thermal treatments are required to establish defined shape memory properties. The reproducibility and stability of the shape memory effect are main aspects thinking about a production of NiTi components in an industrial scale. (author)

  20. Study on properties of stress relaxation for NiTiNb shape memory alloy

    International Nuclear Information System (INIS)

    Zhou Xuchang; Mo Huaqiang; Zeng Guangting; Shen Baoluo; Huo Yongzhong

    2002-01-01

    Stress relaxation tests at high temperature are performed for NiTiNb shape memory alloy to obtain the properties of stress relaxation. The relaxation curve fitted with the expression, which is deduced based on the relation between the relaxation and the creep. With the aid of experimental data, relaxation characteristic coefficient and remaining stress ratio are obtained, which characterize the relaxation behavior. The results of the study show that stress relaxation would be more evident with the higher temperature and/or greater initial stress. NiTiNb alloy has good relaxation resistance in the temperature range 300-400 degree C and the initial stress range 260-360 MPa. NiTiNb has better properties to resist relaxation than NiTiFe, therefore it is more applicable to work at high temperature

  1. Modelling and experimental investigation of geometrically graded NiTi shape memory alloys

    International Nuclear Information System (INIS)

    Shariat, Bashir S; Liu, Yinong; Rio, Gerard

    2013-01-01

    To improve actuation controllability of a NiTi shape memory alloy component in applications, it is desirable to create a wide stress window for the stress-induced martensitic transformation in the alloy. One approach is to create functionally graded NiTi with a geometric gradient in the actuation direction. This geometric gradient leads to transformation load and displacement gradients in the structure. This paper reports a study of the pseudoelastic behaviour of geometrically graded NiTi by means of mechanical model analysis and experimentation using three types of sample geometry. Closed-form solutions are obtained for nominal stress–strain variation of such components under cyclic tensile loading and the predictions are validated with experimental data. The geometrically graded NiTi samples exhibit a distinctive positive stress gradient for the stress-induced martensitic transformation and the slope of the stress gradient can be adjusted by sample geometry design. (paper)

  2. On the development of high quality NiTi shape memory and pseudoelastic parts by additive manufacturing

    International Nuclear Information System (INIS)

    Haberland, Christoph; Elahinia, Mohammad; Walker, Jason M; Meier, Horst; Frenzel, Jan

    2014-01-01

    Additive manufacturing provides an attractive processing method for nickel–titanium (NiTi) shape memory and pseudoelastic parts. In this paper, we show how the additive manufacturing process affects structural and functional properties of additively manufactured NiTi and how the process parameter set-up can be optimized to produce high quality NiTi parts and components. Comparisons of shape recovery due to shape memory and pseudoelasticity in additively manufactured and commercial NiTi exhibit promising potential for this innovative processing method. (paper)

  3. Effect of surface oxidation on thermomechanical behavior of NiTi shape memory alloy wire

    Science.gov (United States)

    Ng, Ching Wei; Mahmud, Abdus Samad

    2017-12-01

    Nickel titanium (NiTi) alloy is a unique alloy that exhibits special behavior that recovers fully its shape after being deformed to beyond elastic region. However, this alloy is sensitive to any changes of its composition and introduction of inclusion in its matrix. Heat treatment of NiTi shape memory alloy to above 600 °C leads to the formation of the titanium oxide (TiO2) layer. Titanium oxide is a ceramic material that does not exhibit shape memory behaviors and possess different mechanical properties than that of NiTi alloy, thus disturbs the shape memory behavior of the alloy. In this work, the effect of formation of TiO2 surface oxide layer towards the thermal phase transformation and stress-induced deformation behaviors of the NiTi alloy were studied. The NiTi wire with composition of Ti-50.6 at% Ni was subjected to thermal oxidation at 600 °C to 900 °C for 30 and 60 minutes. The formation of the surface oxide layers was characterized by using the Scanning Electron Microscope (SEM). The effect of surface oxide layers with different thickness towards the thermal phase transformation behavior was studied by using the Differential Scanning Calorimeter (DSC). The effect of surface oxidation towards the stress-induced deformation behavior was studied through the tensile deformation test. The stress-induced deformation behavior and the shape memory recovery of the NiTi wire under tensile deformation were found to be affected marginally by the formation of thick TiO2 layer.

  4. Recovery stress and shape memory stability in Ni-Ti-Cu thin wires at high temperatures

    Czech Academy of Sciences Publication Activity Database

    Molnár, Peter; Van Humbeeck, J.

    2011-01-01

    Roč. 102, č. 11 (2011), s. 1362-1368 ISSN 1862-5282 Institutional research plan: CEZ:AV0Z10100520 Keywords : shape memory alloys * recovery stress * Ni-Ti-Cu * stress relaxation Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.830, year: 2011 http://www.ijmr.de/directlink.asp?MK110596

  5. Tribological characteristics of ceramic conversion treated NiTi shape memory alloy

    International Nuclear Information System (INIS)

    Ju, X; Dong, H

    2007-01-01

    NiTi shape memory alloys are very attractive for medical implants and devices (such as orthopaedic and orthodontic implants) and various actuators. However, wear is a major concern for such applications and a novel surface engineering process, ceramic conversion treatment, has recently been developed to address this problem. In this study, the tribological characteristics of ceramic conversion treated NiTi alloy have been systematically investigated under dry unidirectional wear, reciprocating-corrosion wear and fretting-corrosion wear condition. Based on the experimental results, the wear behaviour under different conditions is compared and wear mechanisms involved are discussed

  6. Tribological characteristics of ceramic conversion treated NiTi shape memory alloy

    Energy Technology Data Exchange (ETDEWEB)

    Ju, X; Dong, H [Department of Metallurgy and Materials, School of Engineering, University of Birmingham, Edgbaston, Birmingham B15 2TT (United Kingdom)

    2007-09-21

    NiTi shape memory alloys are very attractive for medical implants and devices (such as orthopaedic and orthodontic implants) and various actuators. However, wear is a major concern for such applications and a novel surface engineering process, ceramic conversion treatment, has recently been developed to address this problem. In this study, the tribological characteristics of ceramic conversion treated NiTi alloy have been systematically investigated under dry unidirectional wear, reciprocating-corrosion wear and fretting-corrosion wear condition. Based on the experimental results, the wear behaviour under different conditions is compared and wear mechanisms involved are discussed.

  7. Texture memory and strain-texture mapping in a NiTi shape memory alloy

    International Nuclear Information System (INIS)

    Ye, B.; Majumdar, B. S.; Dutta, I.

    2007-01-01

    The authors report on the near-reversible strain hysteresis during thermal cycling of a polycrystalline NiTi shape memory alloy at a constant stress that is below the yield strength of the martensite. In situ neutron diffraction experiments are used to demonstrate that the strain hysteresis occurs due to a texture memory effect, where the martensite develops a texture when it is cooled under load from the austenite phase and is thereafter ''remembered.'' Further, the authors quantitatively relate the texture to the strain by developing a calculated strain-texture map or pole figure for the martensite phase, and indicate its applicability in other martensitic transformations

  8. Deposition of Chitosan Layers on NiTi Shape Memory Alloy

    Directory of Open Access Journals (Sweden)

    Kowalski P.

    2015-04-01

    Full Text Available The NiTi shape memory alloys have been known from their application in medicine for implants as well as parts of medical devices. However, nickel belongs to the family of elements, which are toxic. Apart from the fact that nickel ions are bonded with titanium into intermetallic phase, their presence may cause allergy. In order to protect human body against release of nickel ions a surface of NiTi alloy can be modified with use of titanium nitrides, oxides or diamond-like layers. On the one hand the layers can play protective role but on the other hand they may influence shape memory behavior. Too stiff or too brittle layer can lead to limiting or completely blocking of the shape recovery. It was the reason to find more elastic covers for NiTi surface protection. This feature is characteristic for polymers, especially, biocompatible ones, which originate in nature. In the reported paper, the chitosan was applied as a deposited layer on surface of the NiTi shape memory alloy. Due to the fact that nature of shape memory effect is sensitive to thermo and/or mechanical treatments, the chitosan layer was deposited with use of electrophoresis carried out at room temperature. Various deposition parameters were checked and optimized. In result of that thin chitosan layer (0.45µm was received on the NiTi alloy surface. The obtained layers were characterized by means of chemical and phase composition, as well as surface quality. It was found that smooth, elastic surface without cracks and/or inclusions can be produced applying 10V and relatively short deposition time - 30 seconds.

  9. Experimental investigation on local mechanical response of superelastic NiTi shape memory alloy

    International Nuclear Information System (INIS)

    Xiao, Yao; Zeng, Pan; Lei, Liping

    2016-01-01

    In this paper, primary attention is paid to the local mechanical response of NiTi shape memory alloy (SMA) under uniaxial tension. With the help of in situ digital image correlation, sets of experiments are conducted to measure the local strain field at various thermomechanical conditions. Two types of mechanical responses of NiTi SMA are identified. The residual strain localization phenomena are observed, which can be attributed to the localized phase transformation (PT) and we affirm that most of the irreversibility is accumulated simultaneously during PT. It is found that temperature and PT play important roles in inducing delocalization of the reverse transformation. We conclude that forward transformation has more influence on the transition of mechanical response in NiTi SMA than reverse transformation in terms of the critical transition temperature for inducing delocalized reverse transformation. (technical note)

  10. Characterization of the laser gas nitrided surface of NiTi shape memory alloy

    International Nuclear Information System (INIS)

    Cui, Z.D.; Man, H.C.; Yang, X.J.

    2003-01-01

    Owing to its unique properties such as shape memory effects, superelasticity and radiopacity, NiTi alloy is a valuable biomaterial for fabricating implants. The major concern of this alloy for biological applications is the high atomic percentage of nickel in the alloy and the deleterious effects to the body by the corrosion and/or wears products. In this study, a continuous wave Nd-YAG laser was used to conduct laser gas nitriding on the substrate of NiTi alloy. The results show that a continuous and crack-free thin TiN layer was produced in situ on the NiTi substrate. The characteristics of the nitrided surface layer were investigated using SEM, XRD, XPS and AAS. No nickel signal was detected on the top surface of the laser gas nitrided layer. As compared with the mechanical polished NiTi alloy, the nickel ion release rate out of the nitrided NiTi alloy decreased significantly in Hanks' solution at 37 deg. C, especially the initial release rate

  11. Surface treatment of NiTi shape memory alloy by modified advanced oxidation process

    Institute of Scientific and Technical Information of China (English)

    CHU Cheng-lin; WANG Ru-meng; YIN Li-hong; PU Yue-pu; DONG Yin-sheng; GUO Chao; SHENG Xiao-bo; LIN Ping-hua; CHU Paul-K

    2009-01-01

    A modified advanced oxidation process(AOP) utilizing a UV/electrochemically-generated peroxide system was used to fabricate titania films on chemically polished NiTi shape memory alloy(SMA). The microstructure and biomedical properties of the film were characterized by scanning electron microscopy(SEM), X-ray photoelectron spectroscopy(XPS), inductively-coupled plasma mass spectrometry(ICPMS), hemolysis analysis, and blood platelet adhesion test. It is found that the modified AOP has a high processing effectiveness and can result in the formation of a dense titania film with a Ni-free zone near its top surface. In comparison, Ni can still be detected on the outer NiTi surface by the conventional AOP using the UV/H2O2 system. The depth profiles of O, Ni, Ti show that the film possesses a smooth graded interface structure next to the NiTi substrate and this structure enhances the mechanical stability of titania film. The titania film can dramatically reduce toxic Ni ion release and also improve the hemolysis resistance and thromboresistance of biomedical NiTi SMA.

  12. Powder Metallurgy Fabrication of Porous 51(at.%)Ni-Ti Shape Memory Alloys for Biomedical Applications

    Science.gov (United States)

    Ibrahim, Mustafa K.; Hamzah, E.; Saud, Safaa N.; Nazim, E. M.

    2018-05-01

    The effect of time and temperature on the microwave sintering of 51(at.%)Ni-Ti shape memory alloys (SMAs) was investigated in the current research. Furthermore, the microstructure, mechanical properties, and bio-corrosion properties were analyzed based on the sintering conditions. The results revealed that the sintering condition of 700 °C for 15 min produced a part with coherent surface survey that does not exhibit gross defects. Increasing the sintering time and temperature created defects on the outer surface, while reducing the temperature to 550 °C severely affected the mechanical properties. The microstructure of these samples showed two regions of Ni-rich region and Ti-rich region between them Ti2Ni, NiTi, and Ni3Ti phases. The differential scanning calorimeter (DSC) curves of Ni-Ti samples exhibited a multi-step phase transformation B19'-R-B2 during heating and cooling. An increase in the sintering temperature from 550 to 700 °C was found to increase the fracture strength significantly and decreased the fracture strain slightly. Reducing the sintering temperature from 700 to 550 °C severely affected the corrosion behaviors of 51%Ni-Ti SMAs. This research aims to select the optimum parameters to produce Ni-Ti alloys with desired microstructure, mechanical properties, and corrosion behaviors for biomedical applications.

  13. Effects of Stoichiometry on Transformation Temperatures and Actuator-Type Performance of NiTiPd and NiTiPdX High-Temperature Shape Memory Alloys

    Science.gov (United States)

    Bigelow, Glen S.; Gaydosh, Darrell; Garg, Anita; Padula, Santo A., II; Noebe, Ronald D.

    2007-01-01

    High-temperature shape memory NiTiPd and NiTiPdX (X=Au, Pt, Hf) alloys were produced with titanium equivalent (Ti+Hf) compositions of 50.5, 50.0, 49.5, and 49.0 at.%. Thermo-mechanical testing in compression was used to evaluate the transformation temperatures, transformation strain, work output, and permanent deformation behavior of each alloy to study the effects of quaternary alloying and stoichiometry on high-temperature shape memory alloy behavior. Microstructural evaluation showed the presence of second phases for all alloy compositions. No load transformation temperatures in the stoichiometric alloys were relatively unchanged by Au and Pt substitutions, while the substitution of Hf for Ti causes a drop in transformation temperatures. The NiTiPd, NiTiPdAu and NiTiPdHf alloys exhibited transformation temperatures that were highest in the Ti-rich compositions, slightly lower at stoichiometry, and significantly reduced when the Ti equivalent composition was less than 50 at.%. For the NiTiPdPt alloy, transformation temperatures were highest for the Ti-rich compositions, lowest at stoichiometry, and slightly higher in the Ni-rich composition. When thermally cycled under constant stresses of up to 300 MPa, all of the alloys had transformation strains, and therefore work outputs, which increased with increasing stress. In each series of alloys, the transformation strain and thus work output was highest for stoichiometric or Ti-rich compositions while permanent strain associated with the constant-load thermal cycling was lowest for alloys with Ni-equivalent-rich compositions. Based on these results, basic rules for optimizing the composition of NiTiPd alloys for actuator performance will be discussed.

  14. Void formation in NiTi shape memory alloys by medium-voltage electron irradiation

    International Nuclear Information System (INIS)

    Schlossmacher, P.; Stober, T.

    1995-01-01

    In-situ electron irradiation experiments of NiTi shape memory alloys, using high-voltage transmission electron microscopes, result in amorphization of the intermetallic compound. In all of these experiments high-voltages more than 1.0 MeV had to be applied in order to induce the crystalline-to-amorphous transformation. To their knowledge no irradiation effects of medium-voltage electrons of e.g. 0.5 MeV have been reported in the literature. In this contribution, the authors describe void formation in two different NiTi shape memory alloys, resulting from in-situ electron irradiation, using a 300 kV electron beam in a transmission electron microscope. First evidence is presented that void formation is correlated with the total oxygen content of the alloys

  15. Additive Manufacturing of NiTiHf High Temperature Shape Memory Alloy

    Science.gov (United States)

    Benafan, Othmane; Bigelow, Glen S.; Elahinia, Mohammad; Moghaddam, Narges Shayesteh; Amerinatanzi, Amirhesam; Saedi, Soheil; Toker, Guher Pelin; Karaca, Haluk

    2017-01-01

    Additive manufacturing of a NiTi-20Hf high temperature shape memory alloy (HTSMA) was investigated. A selective laser melting (SLM) process by Phenix3D Systems was used to develop components from NiTiHf powder (of approximately 25-75 m particle fractions), and the thermomechanical response was compared to the conventionally vacuum induction skull melted counterpart. Transformation temperatures of the SLM material were found to be slightly lower due to the additional oxygen pick up from the gas atomization and melting process. The shape memory response in compression was measured for stresses up to 500 MPa, and transformation strains were found to be very comparable (Up to 1.26 for the as-extruded; up to 1.52 for SLM).

  16. Ni4Ti3 precipitate structures in Ni-rich NiTi shape memory alloys

    Czech Academy of Sciences Publication Activity Database

    Holec, David; Bojda, Ondřej; Dlouhý, Antonín

    2008-01-01

    Roč. 481, Sp. Iss. (2008), s. 462-465 ISSN 0921-5093. [ESOMAT 2006. Bochum, 10.09.2006-15.09.2006] R&D Projects: GA ČR(CZ) GA106/05/0918 Institutional research plan: CEZ:AV0Z20410507 Keywords : NiTi shape memory alloys * Ni4Ti3 precipitates * Multi-step martensitic transformations Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.806, year: 2008

  17. Precipitation Strengthenable NiTiPd High Temperature Shape Memory Alloys

    Science.gov (United States)

    Bigelow, Glen; Garg, Anita; Benafan, Othmane; Noebe, Ronald; Gaydosh, Darrell; Padula, Santo, II

    2017-01-01

    In binary NiTi alloys, it has long been known that Ni-rich alloys can be heat treated to produce precipitates which both strengthen the matrix against dislocations and improve the behavior of the material under thermal and mechanical cycling. Within recent years, the same effect has been observed in Ni-rich NiTiHf high temperature shape memory alloys and heat treatment regimens have been defined which will reliably produce improved properties. In NiTiPd alloys, precipitation has also been observed, but studies are still underway to define reliable heat treatments and compositions which will provide a balance of strengthening and good thermomechanical properties. For this study, a series of NiTi-32 at.Pd alloys was produced to determine the effect of changing nickeltitanium content on the transformation behavior and heat treatability of the material. Samples were aged at temperatures between 350C and 450C for times up to 100 hours. Actuation type behavior was evaluated using uniaxial constant force thermal cycling (UCFTC) to determine the effect of composition and aging on the material behavior. TEMSEM was used to evaluate the microstructure and determine the types of precipitates formed. The correlation between composition, heat treat, microstructure, and thermomechanical behavior will be addressed and discussed.

  18. Nanoscale compositional analysis of NiTi shape memory alloy films deposited by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, S. K.; Mohan, S. [Centre for Nano Science and Engineering, Indian Institute of Science, Bangalore-560012 (India); Bysakh, S. [Central Glass and Ceramics Research Institute, Kolkata-700032 (India); Kumar, A.; Kamat, S. V. [Defence Metallurgical Research Laboratory, Hyderabad-500058 (India)

    2013-11-15

    The formation of surface oxide layer as well as compositional changes along the thickness for NiTi shape memory alloy thin films deposited by direct current magnetron sputtering at substrate temperature of 300 °C in the as-deposited condition as well as in the postannealed (at 600 °C) condition have been thoroughly studied by using secondary ion mass spectroscopy, x-ray photoelectron spectroscopy, and scanning transmission electron microscopy-energy dispersive x-ray spectroscopy techniques. Formation of titanium oxide (predominantly titanium dioxide) layer was observed in both as-deposited and postannealed NiTi films, although the oxide layer was much thinner (8 nm) in as-deposited condition. The depletion of Ti and enrichment of Ni below the oxide layer in postannealed films also resulted in the formation of a graded microstructure consisting of titanium oxide, Ni{sub 3}Ti, and B2 NiTi. A uniform composition of B2 NiTi was obtained in the postannealed film only below a depth of 200–250 nm from the surface. Postannealed film also exhibited formation of a ternary silicide (Ni{sub x}Ti{sub y}Si) at the film–substrate interface, whereas no silicide was seen in the as-deposited film. The formation of silicide also caused a depletion of Ni in the film in a region ∼250–300 nm just above the film substrate interface.

  19. Thermomechanical model for NiTi shape memory wires

    Czech Academy of Sciences Publication Activity Database

    Frost, Miroslav; Sedlák, Petr; Sippola, M.; Šittner, Petr

    2010-01-01

    Roč. 19, č. 9 (2010), s. 1-10 ISSN 0964-1726 R&D Projects: GA MŠk(CZ) 1M06031; GA ČR(CZ) GA106/09/1573; GA ČR(CZ) GP106/09/P302; GA ČR GAP108/10/1296 Institutional research plan: CEZ:AV0Z20760514; CEZ:AV0Z10100520 Keywords : shape memory alloys * modeling * proportional loading Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.094, year: 2010 http://apps.isiknowledge.com/full_record.do?product=WOS&search_mode=GeneralSearch&qid=3&SID=U2fe5mHN9p3gHClCdF1&page=1&doc=1

  20. On the shock response of the shape memory alloy, NiTi

    International Nuclear Information System (INIS)

    Millett, J.C.F.; Bourne, N.K.; Stevens, G.S.; Gray, G.T. III

    2002-01-01

    There has been recent interest in the behaviour of the shape-memory alloy NiTi since it undergoes a stress-induced phase change at a low stress value. It has been additionally noted that the NiTi does not appear to exhibit a Hugoniot elastic limit (HEL) in the way normally associated with other metals. In order to investigate the possible mechanisms operating to give rise to these effects, a series of plate impact experiments have been conducted in order to probe the material's response to shock. In particular attention has been paid to determination of the material Hugoniot in order to ascertain whether the observed features of the response may be explained. A series of other shots where shaped waves are applied are described in order to probe the lower rate response

  1. NiTi shape memory via solid-state nudge-elastic band

    Science.gov (United States)

    Zarkevich, Nikolai A.; Johnson, Duane D.

    2014-03-01

    We determine atomic mechanisms of the shape memory effect in NiTi from a generalized solid-state nudge elastic band (SSNEB) method. We consider transformation between the austenite B2 and the ground-state base-centered orthorhombic (BCO) structures. In these pathways we obtain the R-phase and discuss its structure. We confirm that BCO is the ground state, and determine the pathways to BCO martensite, which dictate transition barriers. While ideal B2 is unstable, we find a B2-like NiTi high-temperature solid phase with significant local displacement disorder, which is B2 on average. This B2-like phase appears to be entropically stabilized. This work is supported by the U.S. Department of Energy, Office of Basic Energy Science, Division of Materials Science and Engineering. Ames Laboratory is operated for the U.S. DOE by Iowa State University under contract DE-AC02-07CH11358.

  2. Surface mechanical attrition treatment induced phase transformation behavior in NiTi shape memory alloy

    International Nuclear Information System (INIS)

    Hu, T.; Wen, C.S.; Lu, J.; Wu, S.L.; Xin, Y.C.; Zhang, W.J.; Chu, C.L.; Chung, J.C.Y.; Yeung, K.W.K.; Kwok, D.T.K.; Chu, Paul K.

    2009-01-01

    The phase constituents and transformation behavior of the martensite B19' NiTi shape memory alloy after undergoing surface mechanical attrition treatment (SMAT) are investigated. SMAT is found to induce the formation of a parent B2 phase from the martensite B19' in the top surface layer. By removing the surface layer-by-layer, X-ray diffraction reveals that the amount of the B2 phase decreases with depth. Differential scanning calorimetry (DSC) further indicates that the deformed martensite in the sub-surface layer up to 300 μm deep exhibits the martensite stabilization effect. The graded phase structure and transformation behavior in the SMATed NiTi specimen can be attributed to the gradient change in strain with depth.

  3. Tensile and superelastic fatigue characterization of NiTi shape memory cables

    Science.gov (United States)

    Sherif, Muhammad M.; Ozbulut, Osman E.

    2018-01-01

    This paper discusses the tensile response and functional fatigue characteristics of a NiTi shape memory alloy (SMA) cable with an outer diameter of 5.5 mm. The cable composed of multiple strands arranged as one inner core and two outer layers. The results of the tensile tests revealed that the SMA cable exhibits good superelastic behavior up to 10% strain. Fatigue characteristics were investigated under strain amplitudes ranging from 3% to 7% and a minimum of 2500 loading cycles. The evolutions of maximum tensile stress, residual strains, energy dissipation, and equivalent viscous damping under a number of loading cycles were analyzed. The fracture surface of a specimen subjected to 5000 loading cycles and 7% strain was discussed. Functional fatigue test results indicated a very high superelastic fatigue life cycle for the tested NiTi SMA cable.

  4. Structure and properties of nitrided surface layer produced on NiTi shape memory alloy by low temperature plasma nitriding

    International Nuclear Information System (INIS)

    Czarnowska, Elżbieta; Borowski, Tomasz; Sowińska, Agnieszka; Lelątko, Józef; Oleksiak, Justyna; Kamiński, Janusz; Tarnowski, Michał; Wierzchoń, Tadeusz

    2015-01-01

    Highlights: • Low temperature plasma nitriding process of NiTi shape memory alloy is presented. • The possibility of treatment details of sophisticated shape. • TiN surface layer has diffusive character. • TiN surface layer increases corrosion resistance of NiTi alloy. • Produced TiN layer modify the biological properties of NiTi alloy. - Abstract: NiTi shape memory alloys are used for bone and cardiological implants. However, on account of the metallosis effect, i.e. the release of the alloy elements into surrounding tissues, they are subjected to various surface treatment processes in order to improve their corrosion resistance and biocompatibility without influencing the required shape memory properties. In this paper, the microstructure, topography and morphology of TiN surface layer on NiTi alloy, and corrosion resistance, both before and after nitriding in low-temperature plasma at 290 °C, are presented. Examinations with the use of the potentiodynamic and electrochemical impedance spectroscopy methods were carried out and show an increase of corrosion resistance in Ringer's solution after glow-discharge nitriding. This surface titanium nitride layer also improved the adhesion of platelets and the proliferation of osteoblasts, which was investigated in in vitro experiments with human cells. Experimental data revealed that nitriding NiTi shape memory alloy under low-temperature plasma improves its properties for bone implant applications

  5. Structure and properties of nitrided surface layer produced on NiTi shape memory alloy by low temperature plasma nitriding

    Energy Technology Data Exchange (ETDEWEB)

    Czarnowska, Elżbieta [Children' s Memorial Health Institute, Pathology Department, Al. Dzieci Polskich 20, 04-730 Warsaw (Poland); Borowski, Tomasz [Warsaw University of Technology, Faculty of Materials Science and Engineering, Wołoska 141, 02-507 Warsaw (Poland); Sowińska, Agnieszka [Children' s Memorial Health Institute, Pathology Department, Al. Dzieci Polskich 20, 04-730 Warsaw (Poland); Lelątko, Józef [Silesia University, Faculty of Computer Science and Materials Science, 75 Pułku Piechoty 1A, 41-500 Chorzów (Poland); Oleksiak, Justyna; Kamiński, Janusz; Tarnowski, Michał [Warsaw University of Technology, Faculty of Materials Science and Engineering, Wołoska 141, 02-507 Warsaw (Poland); Wierzchoń, Tadeusz, E-mail: twierz@inmat.pw.edu.pl [Warsaw University of Technology, Faculty of Materials Science and Engineering, Wołoska 141, 02-507 Warsaw (Poland)

    2015-04-15

    Highlights: • Low temperature plasma nitriding process of NiTi shape memory alloy is presented. • The possibility of treatment details of sophisticated shape. • TiN surface layer has diffusive character. • TiN surface layer increases corrosion resistance of NiTi alloy. • Produced TiN layer modify the biological properties of NiTi alloy. - Abstract: NiTi shape memory alloys are used for bone and cardiological implants. However, on account of the metallosis effect, i.e. the release of the alloy elements into surrounding tissues, they are subjected to various surface treatment processes in order to improve their corrosion resistance and biocompatibility without influencing the required shape memory properties. In this paper, the microstructure, topography and morphology of TiN surface layer on NiTi alloy, and corrosion resistance, both before and after nitriding in low-temperature plasma at 290 °C, are presented. Examinations with the use of the potentiodynamic and electrochemical impedance spectroscopy methods were carried out and show an increase of corrosion resistance in Ringer's solution after glow-discharge nitriding. This surface titanium nitride layer also improved the adhesion of platelets and the proliferation of osteoblasts, which was investigated in in vitro experiments with human cells. Experimental data revealed that nitriding NiTi shape memory alloy under low-temperature plasma improves its properties for bone implant applications.

  6. Magnetron sputtered Cu{sub 3}N/NiTiCu shape memory thin film heterostructures for MEMS applications

    Energy Technology Data Exchange (ETDEWEB)

    Kaur, Navjot; Choudhary, Nitin [Indian Institute of Technology Roorkee, Roorkee, Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology (India); Goyal, Rajendra N. [Indian Institute of Technology, Roorkee, Department of Chemistry (India); Viladkar, S. [Indian Institute of Technology Roorkee, Roorkee, Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology (India); Matai, I.; Gopinath, P. [Indian Institute of Technology, Roorkee, Centre for Nanotechnology (India); Chockalingam, S. [Indian Institute of Technology, Guwahati, Department of Biotechnology (India); Kaur, Davinder, E-mail: dkaurfph@iitr.ernet.in [Indian Institute of Technology Roorkee, Roorkee, Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology (India)

    2013-03-15

    In the present study, for the first time, Cu{sub 3}N/NiTiCu/Si heterostructures were successfully grown using magnetron sputtering technique. Nanocrystalline copper nitride (Cu{sub 3}N with thickness {approx}200 nm) thin films and copper nanodots were subsequently deposited on the surface of 2-{mu}m-thick NiTiCu shape memory thin films in order to improve the surface corrosion and nickel release properties of NiTiCu thin films. Interestingly, the phase transformation from martensite phase to austenite phase has been observed in Cu{sub 3}N/NiTiCu heterostructures with corresponding change in texture and surface morphology of top Cu{sub 3}N films. Field emission scanning electron microscopy and atomic force microscope images of the heterostructures reveals the formation of 20-nm-sized copper nanodots on NiTiCu surface at higher deposition temperature (450 Degree-Sign C) of Cu{sub 3}N. Cu{sub 3}N passivated NiTiCu films possess low corrosion current density with higher corrosion potential and, therefore, better corrosion resistance as compared to pure NiTiCu films. The concentration of Ni released from the Cu{sub 3}N/NiTiCu samples was observed to be much less than that of pure NiTiCu film. It can be reduced to the factor of about one-ninth after the surface passivation resulting in smooth, homogeneous and highly corrosion resistant surface. The antibacterial and cytotoxicity of pure and Cu{sub 3}N coated NiTiCu thin films were investigated through green fluorescent protein expressing E. coli bacteria and human embryonic kidney cells. The results show the strong antibacterial property and non cytotoxicity of Cu{sub 3}N/NiTiCu heterostructure. This work is of immense technological importance due to variety of BioMEMS applications.

  7. Atomistic characterization of pseudoelasticity and shape memory in NiTi nanopillars

    International Nuclear Information System (INIS)

    Zhong Yuan; Gall, Ken; Zhu Ting

    2012-01-01

    Molecular dynamics simulations are performed to study the atomistic mechanisms governing the pseudoelasticity and shape memory in nickel–titanium (NiTi) nanostructures. For a 〈1 1 0〉 – oriented nanopillar subjected to compressive loading–unloading, we observe either a pseudoelastic or shape memory response, depending on the applied strain and temperature that control the reversibility of phase transformation and deformation twinning. We show that irreversible twinning arises owing to the dislocation pinning of twin boundaries, while hierarchically twinned microstructures facilitate the reversible twinning. The nanoscale size effects are manifested as the load serration, stress plateau and large hysteresis loop in stress–strain curves that result from the high stresses required to drive the nucleation-controlled phase transformation and deformation twinning in nanosized volumes. Our results underscore the importance of atomistically resolved modeling for understanding the phase and deformation reversibilities that dictate the pseudoelasticity and shape memory behavior in nanostructured shape memory alloys.

  8. Electron energy-loss spectroscopy study of NiTi shape memory alloys

    International Nuclear Information System (INIS)

    Yang, Z.Q.; Schryvers, D.

    2008-01-01

    Electron energy loss spectroscopy (EELS) investigations were carried out on NiTi shape memory alloys. The composition of lens-shaped precipitates is determined to be Ni 4 Ti 3 by model-based EELS quantification, and the Ni-depleted zone in the B2 matrix surrounding the Ni 4 Ti 3 precipitates was quantified. The Young's modulus Y m of the B2 matrix with 51 at.% Ni and the Ni 4 Ti 3 precipitates was evaluated to be about 124 and 175 GPa, respectively. The intensity of the Ni L 3 edge for the precipitate is slightly higher than that for the B2 phase

  9. X-ray diffraction studies of NiTi shape memory alloys

    OpenAIRE

    E. Łągiewka; Z. Lekston

    2007-01-01

    Purpose: The purpose of this paper is to present the results of the investigations of phase transitions of TiNiCo and Ni-rich NiTi shape memory alloys designed for medical applications.Design/methodology/approach: Temperature X-ray diffraction (TXRD), differential scanning calorimetry (DSC), electrical resistivity (ER) and the temperature shape recovery measurements in three-point bending ASTM 2082-01 tests were used.Findings: It has been found in this work that ageing after solution treatme...

  10. Characterization of NiTi Shape Memory Damping Elements designed for Automotive Safety Systems

    Science.gov (United States)

    Strittmatter, Joachim; Clipa, Victor; Gheorghita, Viorel; Gümpel, Paul

    2014-07-01

    Actuator elements made of NiTi shape memory material are more and more known in industry because of their unique properties. Due to the martensitic phase change, they can revert to their original shape by heating when subjected to an appropriate treatment. This thermal shape memory effect (SME) can show a significant shape change combined with a considerable force. Therefore such elements can be used to solve many technical tasks in the field of actuating elements and mechatronics and will play an increasing role in the next years, especially within the automotive technology, energy management, power, and mechanical engineering as well as medical technology. Beside this thermal SME, these materials also show a mechanical SME, characterized by a superelastic plateau with reversible elongations in the range of 8%. This behavior is based on the building of stress-induced martensite of loaded austenite material at constant temperature and facilitates a lot of applications especially in the medical field. Both SMEs are attended by energy dissipation during the martensitic phase change. This paper describes the first results obtained on different actuator and superelastic NiTi wires concerning their use as damping elements in automotive safety systems. In a first step, the damping behavior of small NiTi wires up to 0.5 mm diameter was examined at testing speeds varying between 0.1 and 50 mm/s upon an adapted tensile testing machine. In order to realize higher testing speeds, a drop impact testing machine was designed, which allows testing speeds up to 4000 mm/s. After introducing this new type of testing machine, the first results of vertical-shock tests of superelastic and electrically activated actuator wires are presented. The characterization of these high dynamic phase change parameters represents the basis for new applications for shape memory damping elements, especially in automotive safety systems.

  11. Exploiting NiTi shape memory alloy films in design of tunable high frequency microcantilever resonators

    Science.gov (United States)

    Stachiv, I.; Sittner, P.; Olejnicek, J.; Landa, M.; Heller, L.

    2017-11-01

    Shape memory alloy (SMA) films are very attractive materials for microactuators because of their high energy density. However, all currently developed SMA actuators utilize martensitic transformation activated by periodically generated heating and cooling; therefore, they have a slow actuation speed, just a few Hz, which restricts their use in most of the nanotechnology applications such as high frequency microcantilever based physical and chemical sensors, atomic force microscopes, or RF filters. Here, we design tunable high frequency SMA microcantilevers for nanotechnology applications. They consist of a phase transforming NiTi SMA film sputtered on the common elastic substrate material; in our case, it is a single-crystal silicon. The reversible tuning of microcantilever resonant frequencies is then realized by intentionally changing the Young's modulus and the interlayer stress of the NiTi film by temperature, while the elastic substrate guarantees the high frequency actuation (up to hundreds of kHz) of the microcantilever. The experimental results qualitatively agree with predictions obtained from the dedicated model based on the continuum mechanics theory and a phase characteristic of NiTi. The present design of SMA microcantilevers expands the capability of current micro-/nanomechanical resonators by enabling tunability of several consecutive resonant frequencies.

  12. Shape memory behavior of high strength NiTiHfPd polycrystalline alloys

    International Nuclear Information System (INIS)

    Karaca, H.E.; Acar, E.; Ded, G.S.; Basaran, B.; Tobe, H.; Noebe, R.D.; Bigelow, G.; Chumlyakov, Y.I.

    2013-01-01

    Systematic characterization of the shape memory properties of a quaternary Ni 45.3 –Ti 29.7 –Hf 20 –Pd 5 (at.%) polycrystalline alloy was performed in compression after selected aging treatments. Precipitation characteristics were revealed by transmission electron microscopy. The effects of aging temperature and time on transformation temperatures, recoverable and residual strains, and temperature and stress hystereses were determined by differential scanning calorimetry, constant-load thermal cycling experiments and isothermal strain cycling (superelasticity) tests. The crystal structure and lattice parameters of the transforming phases were determined from X-ray diffraction analysis. It was revealed that precipitation hardening significantly improved the shape memory properties of the NiTiHfPd alloy. Under optimum aging conditions, shape memory strains of up to 4% under 1 GPa were possible, and superelasticity experiments resulted in full strain recovery without any plastic deformation, even at stress levels as high as 2 GPa. The NiTiHfPd polycrystalline alloy exhibited very high damping capacity/absorbed energy (30–34 J cm −3 ) and work output (30–35 J cm −3 ), which were attributed to the ability to operate at high stress levels without significant plastic deformation and to a high mechanical hysteresis (>900 MPa) at temperatures ranging from 20 °C to 80 °C

  13. Narrow thermal hysteresis of NiTi shape memory alloy thin films with submicrometer thickness

    Energy Technology Data Exchange (ETDEWEB)

    Hou, Huilong; Hamilton, Reginald F., E-mail: rfhamilton@psu.edu; Horn, Mark W. [Department of Engineering Science and Mechanics, The Pennsylvania State University, University Park, Pennsylvania 16802 (United States)

    2016-09-15

    NiTi shape memory alloy (SMA) thin films were fabricated using biased target ion beam deposition (BTIBD), which is a new technique for fabricating submicrometer-thick SMA thin films, and the capacity to exhibit shape memory behavior was investigated. The thermally induced shape memory effect (SME) was studied using the wafer curvature method to report the stress-temperature response. The films exhibited the SME in a temperature range above room temperature and a narrow thermal hysteresis with respect to previous reports. To confirm the underlying phase transformation, in situ x-ray diffraction was carried out in the corresponding phase transformation temperature range. The B2 to R-phase martensitic transformation occurs, and the R-phase transformation is stable with respect to the expected conversion to the B19′ martensite phase. The narrow hysteresis and stable R-phase are rationalized in terms of the unique properties of the BTIBD technique.

  14. Atomistic to Continuum Multiscale and Multiphysics Simulation of NiTi Shape Memory Alloy

    Science.gov (United States)

    Gur, Sourav

    Shape memory alloys (SMAs) are materials that show reversible, thermo-elastic, diffusionless, displacive (solid to solid) phase transformation, due to the application of temperature and/ or stress (/strain). Among different SMAs, NiTi is a popular one. NiTi shows reversible phase transformation, the shape memory effect (SME), where irreversible deformations are recovered upon heating, and superelasticity (SE), where large strains imposed at high enough temperatures are fully recovered. Phase transformation process in NiTi SMA is a very complex process that involves the competition between developed internal strain and phonon dispersion instability. In NiTi SMA, phase transformation occurs over a wide range of temperature and/ or stress (strain) which involves, evolution of different crystalline phases (cubic austenite i.e. B2, different monoclinic variant of martensite i.e. B19', and orthorhombic B19 or BCO structures). Further, it is observed from experimental and computational studies that the evolution kinetics and growth rate of different phases in NiTi SMA vary significantly over a wide spectrum of spatio-temporal scales, especially with length scales. At nano-meter length scale, phase transformation temperatures, critical transformation stress (or strain) and phase fraction evolution change significantly with sample or simulation cell size and grain size. Even, below a critical length scale, the phase transformation process stops. All these aspects make NiTi SMA very interesting to the science and engineering research community and in this context, the present focuses on the following aspects. At first this study address the stability, evolution and growth kinetics of different phases (B2 and variants of B19'), at different length scales, starting from the atomic level and ending at the continuum macroscopic level. The effects of simulation cell size, grain size, and presence of free surface and grain boundary on the phase transformation process

  15. Enhanced photomechanical response of a Ni-Ti shape memory alloy coated with polymer-based photothermal composites

    Science.gov (United States)

    Perez-Zúñiga, M. G.; Sánchez-Arévalo, F. M.; Hernández-Cordero, J.

    2017-10-01

    A simple way to enhance the activation of shape memory effects with light in a Ni-Ti alloy is demonstrated. Using polydimethylsiloxane-carbon nanopowder (PDMS+CNP) composites as coatings, the one-way shape memory effect (OWSME) of the alloy can be triggered using low power IR light from a laser diode. The PDMS+CNP coatings serve as photothermal materials capable to absorb light, and subsequently generate and dissipate heat in a highly efficient manner, thereby reducing the optical powers required for triggering the OWSME in the Ni-Ti alloy. Experimental results with a cantilever flexural test using both, bare Ni-Ti and coated samples, show that the PDMS+CNP coatings perform as thermal boosters, and therefore the temperatures required for phase transformation in the alloy can be readily obtained with low laser powers. It is also shown that the two-way shape memory effect (TWSME) can be set in the Ni-Ti alloy through cycling the TWSME by simply modulating the laser diode signal. This provides a simple means for training the material, yielding a light driven actuator capable to provide forces in the mN range. Hence, the use of photothermal coatings on Ni-Ti shape memory alloys may offer new possibilities for developing light-controlled smart actuators.

  16. Impurity levels and fatigue lives of pseudoelastic NiTi shape memory alloys

    International Nuclear Information System (INIS)

    Rahim, M.; Frenzel, J.; Frotscher, M.; Pfetzing-Micklich, J.; Steegmüller, R.; Wohlschlögel, M.; Mughrabi, H.; Eggeler, G.

    2013-01-01

    In the present work we show how different oxygen (O) and carbon (C) levels affect fatigue lives of pseudoelastic NiTi shape memory alloys. We compare three alloys, one with an ultrahigh purity and two which contain the maximum accepted levels of C and O. We use bending rotation fatigue (up to cycle numbers >10 8 ) and scanning electron microscopy (for investigating microstructural details of crack initiation and growth) to study fatigue behavior. High cycle fatigue (HCF) life is governed by the number of cycles required for crack initiation. In the low cycle fatigue (LCF) regime, the high-purity alloy outperforms the materials with higher number densities of carbides and oxides. In the HCF regime, on the other hand, the high-purity and C-containing alloys show higher fatigue lives than the alloy with oxide particles. There is high experimental scatter in the HCF regime where fatigue cracks preferentially nucleate at particle/void assemblies (PVAs) which form during processing. Cyclic crack growth follows the Paris law and does not depend on impurity levels. The results presented in the present work contribute to a better understanding of structural fatigue of pseudoelastic NiTi shape memory alloys

  17. Thermomechanical behavior of Ti-rich NiTi shape memory alloys

    International Nuclear Information System (INIS)

    Paula, A.S.; Mahesh, K.K.; Santos, C.M.L. dos; Braz Fernandes, F.M.; Costa Viana, C.S. da

    2008-01-01

    Phase transformations associated with shape memory effect in nickel-titanium (NiTi) alloys can be one-stage, B19' (martensite) ↔ B2 (austenite), two-stage including an intermediate R-phase stage, or multiple-stage depending on the thermal and/or mechanical history of the alloy. In the present paper, we highlight the effect of (i) deformation by cold-rolling (from 10% to 40% thickness reduction) and (ii) final annealing on the transformation characteristics of a Ti-rich NiTi shape memory alloy. For this purpose, one set of samples initially heat treated at 773 K followed by cold-rolling (10-40% thickness reduction), has been further heat treated at various temperatures between 673 and 1073 K. Another sample was subjected to heat treatment at 1040 K for 300 s followed by hot rolling (50%) after cooling in air to 773 K and water quenching to room temperature (T room ). Phase transformations were studied using differential scanning calorimetry, electrical resistivity measurements and in situ X-ray diffraction. A specific pattern of transformation sequences is found as a result of combination of the competing effects due to mechanical-working and annealing

  18. Characterisation of melt spun Ni-Ti shape memory Ribbons' microstructure

    Science.gov (United States)

    Mehrabi, Kambiz; Brunčko, Mihael; Kneissl, Albert C.; Čolič, Miodrag; Stamenković, Dragoslav; Ferčec, Janko; Anžel, Ivan; Rudolf, Rebeka

    2012-06-01

    NiTi alloys are the most technologically important medical Shape Memory Alloys in a wide range of applications used in Orthopaedics, Neurology, Cardiology and interventional Radiology as guide-wires, self-expandable stents, stent grafts, inferior vena cava filters and clinical instruments. This paper discusses the use of rapid solidification by the melt spinning method for the preparation of thin NiTi ribbons for medical uses. Generally, the application of rapid solidification via melt-spinning can change the microstructure drastically, which improves ductility and shape memory characteristics and leads to samples with small dimensions. As the increase in the wheel speed led to a reduced ribbon thickness, the cooling rate increased and, therefore, the martensitic substructure became finer. Furthermore, no transition from the crystalline phase to the amorphous phase was obtained by increasing the cooling rate, even at a wheel speed of 30 m/s. Specimens for our metallographic investigation were cut from the longitudinal cross sections of melt-spun ribbons. Conventional TEM studies were carried out with an acceleration voltage of 120 kV. Additionally, the chemical composition of the samples was examined with a TEM equipped with an EDX analyser. The crystallographic structure was determined using Bragg-Brentano x-ray diffraction with Cu-Kα radiation at room temperature.

  19. Mechanical response of nitrogen ion implanted NiTi shape memory alloy

    International Nuclear Information System (INIS)

    Kucharski, S.; Levintant-Zayonts, N.; Luckner, J.

    2014-01-01

    Highlights: • The effect of ion implantation process on shape memory alloy was investigated. • In the implantation process both surface layer and bulk material are modified. • The microstructure is modified and superelastic effect is destroyed in surface layer. • The parameters of superelastic phenomena are changed in bulk material. - Abstract: In the paper a change of material (mechanical) parameters of NiTi shape memory alloy subjected to ion implantation treatment is investigated. The spherical indentation tests in micro- and nano-scale and tension test have been performed to study an evolution of local superelastic effect in different volumes of nonimplanted and nitrogen ion implanted NiTi alloy. The differential scanning calorimetry has been applied to measure the change of characteristic temperatures due to ion implantation treatment. The structure of implanted material has been investigated using electron microscopy technique. It has been found that the ion implantation process changes the properties not only in a thin surface layer but also in bulk material. In the layer the pseudoelastic effect is destroyed, and in the substrate is preserved, however its parameters are changed. The characteristic phase transformation temperatures in substrate are also modified

  20. Precipitation-induced of partial annealing of Ni-rich NiTi shape memory alloy

    Science.gov (United States)

    Nashrudin, Muhammad Naqib; Mahmud, Abdus Samad; Mohamad, Hishamiakim

    2018-05-01

    NiTi shape memory alloy behavior is very sensitive to alloy composition and heat treatment processes. Thermomechanical behavior of near-equiatomic alloy is normally enhanced by partial anneal of a cold-worked specimen. The shape memory behavior of Ni-rich alloy can be enhanced by ageing precipitation. This work studied the effect of simultaneous partial annealing and ageing precipitation of a Ni-rich cold drawn Ti-50.9at%Ni wire towards martensite phase transformation behavior. Ageing treatment of a non-cold worked specimen was also done for comparison. It was found that the increase of heat treatment temperature caused the forward transformation stress to decrease for the cold worked and non-cold worked specimens. Strain recovery on the reverse transformation of the cold worked wire improved compared to the non-cold worked wire as the temperature increased.

  1. Powder-metallurgy preparation of NiTi shape-memory alloy using mechanical alloying and spark-plasma sintering.

    Czech Academy of Sciences Publication Activity Database

    Novák, P.; Moravec, H.; Vojtěch, V.; Knaislová, A.; Školáková, A.; Kubatík, Tomáš František; Kopeček, Jaromír

    2017-01-01

    Roč. 51, č. 1 (2017), s. 141-144 ISSN 1580-2949 R&D Projects: GA ČR(CZ) GA14-03044S Institutional support: RVO:61389021 ; RVO:68378271 Keywords : mechanical alloying * spark plasma sintering * NiTi * shape memory alloy Subject RIV: JG - Metallurgy; JG - Metallurgy (FZU-D) OBOR OECD: Materials engineering ; Materials engineering (FZU-D) Impact factor: 0.436, year: 2016 https://www.researchgate.net/publication/313900224_Powder-metallurgy_preparation_of_NiTi_shape-memory_alloy_using_mechanical_alloying_and_spark-plasma_sintering

  2. Sn buffered by shape memory effect of NiTi alloys as high-performance anodes for lithium ion batteries

    International Nuclear Information System (INIS)

    Hu Renzong; Zhu Min; Wang Hui; Liu Jiangwen; Liuzhang Ouyang; Zou Jin

    2012-01-01

    By applying the shape memory effect of the NiTi alloys to buffer the Sn anodes, we demonstrate a simple approach to overcome a long-standing challenge of Sn anode in the applications of Li-ion batteries – the capacity decay. By supporting the Sn anodes with NiTi shape memory alloys, the large volume change of Sn anodes due to lithiation and delithiation can be effectively accommodated, based on the stress-induced martensitic transformation and superelastic recovery of the NiTi matrix respectively, which leads to a decrease in the internal stress and closing of cracks in Sn anodes. Accordingly, stable cycleability (630 mA h g −1 after 100 cycles at 0.7C) and excellent high-rate capabilities (478 mA h g −1 at 6.7C) were attained with the NiTi/Sn/NiTi film electrode. These shape memory alloys can also combine with other high-capacity metallic anodes, such as Si, Sb, Al, and improve their cycle performance.

  3. Scale up of NiTi shape memory alloy production by EBM

    Science.gov (United States)

    Otubo, J.; Rigo, O. D.; Moura Neto, C.; Kaufman, M. J.; Mei, P. R.

    2003-10-01

    The usual process to produce NiTi shape memory alloy is by vacuum induction melting (VIM) using a graphite crucible, which causes contamination of the melt with carbon. Contamination with oxygen originates from the residual oxygen inside the melting chamber. An alternative process to produce NiTi alloys is by electron beam melting (EBM) using a water-cooled copper crucible that eliminates carbon contamination, and the oxygen contamination would be minimal due to operation in a vacuum of better than 10^{-2} Pa. In a previous work, it was demonstrated that the technique is feasible for button shaped samples weighing around 30g. The present work presents the results on the scale up program that enables the production of larger samples/ingots. The results are very promising in terms of chemical composition homogeneity as well as in terms of carbon contamination, the latter being four to ten times lower than the commercially-produced VIM products, and in terms of final oxygen content which is shown to depend primarily on the starting raw materials.

  4. Improvement of Ti-plasma coating on Ni-Ti shape memory alloy applying to implant materials and its evaluation

    International Nuclear Information System (INIS)

    Okuyama, Masaru; Endo, Jun; Take, Seisho; Itoi, Yasuhiko; Kambe, Satoshi

    2002-01-01

    Utilizing of Ni-Ti shape memory alloy for implant materials has been world-widely studied. it is, however, known that Ni-Ti alloy is easily attacked by chloride ion contained in body liquid. To prevent Ni dissolution, the authors tried to coat the alloy surface with titanium metal by means of plasma-spray coating method. The plasma coating films resulted in rather accelerating pitting corrosion because of their high porosity. Therefore, sealing of the porous films was required. In order to solve this problem and satisfy prolonged lifetime in the body, the authors tried to use the vacuum evaporation technique of titanium metal. Two types of Ti vacuum evaporation procedures were employed. The one was to cover a thin film on Ni-Ti alloy surface prior to massive Ti plasma spray coating. The other was to first coat plasma spray films on Ni-Ti alloy and then to cover them with vacuum evaporation films of Ti. Protective ability against pitting corrosion was examined by electrochemical polarization measurement in physiological solution and the coating films were characterized by microscopic and SEM observation and EPMA analysis. Vacuum evaporation thin films could not protect Ni-Ti alloy from pitting corrosion. In the case of plasma spray coating over the Ti vacuum evaporation thin film, the substrate Ni-Ti alloy could not be better protected. On the contrary, vacuum evaporation of Ti over the porous plasma spray coating layer remarkably improved corrosion protective performance

  5. Loading Path and Control Mode Effects During Thermomechanical Cycling of Polycrystalline Shape Memory NiTi

    Science.gov (United States)

    Nicholson, D. E.; Benafan, O.; Padula, S. A.; Clausen, B.; Vaidyanathan, R.

    2018-01-01

    Loading path dependencies and control mode effects in polycrystalline shape memory NiTi were investigated using in situ neutron and synchrotron X-ray diffraction performed during mechanical cycling and thermal cycling at constant strain. Strain-controlled, isothermal, reverse loading (to ± 4%) and stress-controlled, isothermal, cyclic loading (to ± 400 MPa for up to ten cycles) at room temperature demonstrated that the preferred martensite variants selected correlated directly with the macroscopic uniaxial strain and did not correlate with the compressive or tensile state of stress. During cyclic loading (up to ten cycles), no significant cycle-to-cycle evolution of the variant microstructure corresponding to a given strain was observed, despite changes in the slope of the stress-strain response with each cycle. Additionally, thermal cycling (to above and below the phase transformation) under constant strain (up to 2% tensile strain) showed that the martensite variant microstructure correlated directly with strain and did not evolve following thermal cycling, despite relaxation of stress in both martensite and austenite phases. Results are presented in the context of variant reorientation and detwinning processes in martensitic NiTi, the fundamental thermoelastic nature of such processes and the ability of the variant microstructure to accommodate irreversible deformation processes.

  6. Laser shock wave assisted patterning on NiTi shape memory alloy surfaces

    Science.gov (United States)

    Seyitliyev, Dovletgeldi; Li, Peizhen; Kholikov, Khomidkhodza; Grant, Byron; Karaca, Haluk E.; Er, Ali O.

    2017-02-01

    An advanced direct imprinting method with low cost, quick, and less environmental impact to create thermally controllable surface pattern using the laser pulses is reported. Patterned micro indents were generated on Ni50Ti50 shape memory alloys (SMA) using an Nd:YAG laser operating at 1064 nm combined with suitable transparent overlay, a sacrificial layer of graphite, and copper grid. Laser pulses at different energy densities which generates pressure pulses up to 10 GPa on the surface was focused through the confinement medium, ablating the copper grid to create plasma and transferring the grid pattern onto the NiTi surface. Scanning electron microscope (SEM) and optical microscope images of square pattern with different sizes were studied. One dimensional profile analysis shows that the depth of the patterned sample initially increase linearly with the laser energy until 125 mJ/pulse where the plasma further absorbs and reflects the laser beam. In addition, light the microscope image show that the surface of NiTi alloy was damaged due to the high power laser energy which removes the graphite layer.

  7. Finding the energy source for self-propagating high-temperature synthesis production of NiTi shape memory alloy

    Czech Academy of Sciences Publication Activity Database

    Novák, P.; Školáková, A.; Pignol, D.; Průša, F.; Salvetr, P.; Kubatík, Tomáš František; Perriere, L.; Karlík, M.

    2016-01-01

    Roč. 181, September (2016), s. 295-300 ISSN 0254-0584 Institutional support: RVO:61389021 Keywords : NiTi * Shape memory alloys * Powder metallurgy * Microstructure Subject RIV: JG - Metallurgy Impact factor: 2.084, year: 2016 http://www.sciencedirect.com/science/article/pii/S025405841630476X

  8. Atomistic study on shock behaviour of NiTi shape memory alloy

    Science.gov (United States)

    Yin, Qiuyun; Wu, Xianqian; Huang, Chenguang

    2017-06-01

    The shock behaviour of NiTi shape memory alloy is investigated by using molecular dynamics simulation. The nano-pillar samples of the alloy are subjected to the impact of a piston with a velocity of 350 m/s at initial environment temperatures of 325 and 500 K. At 325 K, we observe two different pathways of the formation of BCO phase, the gradient twins, and the detwinning phenomena, strongly depending on the local stress and the deformation state. As the initial temperature increases to 500 K, the plasticity is dominated by the dislocation movements rather than the twinning at 325 K. The phase transformation and plasticity result in stress attenuation when the stress wave propagates through the nano-pillar. Furthermore, it is interesting to note that multiple stress peaks occur due to the formation of local complex atomic structures with various wave speeds, leading to the catch up and overlap of the stress waves.

  9. Ni4Ti3 precipitate structures in Ni-rich NiTi shape memory alloys

    International Nuclear Information System (INIS)

    Holec, D.; Bojda, O.; Dlouhy, A.

    2008-01-01

    Non-uniform distributions of Ni 4 Ti 3 precipitate crystallographic variants are investigated in a Ni-rich NiTi shape memory alloy after aging, assisted by external stress. A finite-element method model is presented that considers the elastic anisotropy of the B2 parent phase and also mutual misorientations of grains in a polycrystalline sample. On loading by the external stress, the stress is redistributed in the microstructure and the precipitation of some Ni 4 Ti 3 crystallographic variants becomes distinctly favorable in grain boundary regions since these variant configurations minimize the elastic interaction energy. The volume fraction of the affected grain boundary regions is calculated and the numerical results are compared with the data obtained by differential scanning calorimetry and transmission electron microscopy

  10. Formation of titanium oxide coatings on NiTi shape memory alloys by selective oxidation

    International Nuclear Information System (INIS)

    Pohl, M.; Glogowski, T.; Kuehn, S.; Hessing, C.; Unterumsberger, F.

    2008-01-01

    Materials used for medical devices that are in contact with human tissue must have good corrosion resistance and biocompatibility. NiTi shape memory alloys (SMAs) are often used in medical applications due to their special functional and mechanical properties (shape memory effect, pseudo elasticity). Because of the high Ni content in nearly stoichiometric NiTi SMAs, the possibility of Ni being released needs to be considered as Ni may cause problems in the human body. SMAs exhibit a high intrinsic corrosion resistance because of the thermodynamic stability of Ni (thermodynamic reason) and the low degree of disorder in a thin protective TiO 2 -layer (kinetic reason). While therefore there is no need to be concerned too much about a normal corrosive attack in the human body, it has to be kept in mind that in medical applications, these materials represent one part of a tribological system where wear processes need to be considered. The formation of a uniform TiO 2 -layer can be beneficial in this respect. The selective oxidation of Ti to TiO 2 on the surface is a promising method to decrease the Ni release significantly. This can be achieved by controlling the partial pressure of oxygen during a controlled oxidation process. The atmosphere must be adjusted so that TiO 2 is stable while NiO cannot yet form. The result of a selective oxidation is a TiO 2 -layer that has an excellent degree of purity and represents a safe barrier against Ni emission

  11. The effect of addition of various elements on properties of NiTi-based shape memory alloys for biomedical application

    Science.gov (United States)

    Kök, Mediha; Ateş, Gonca

    2017-04-01

    In biomedical applications, NiTi and NiTi-based alloys that show their shape memory effects at body temperature are preferred. In this study, the purpose is to produce NiTi and NiTi-based alloys with various chemical rates and electron concentrations and to examine their various physical properties. N45Ti55, Ni45Ti50Cr2.5Cu2.5, Ni48Ti51X (X=Mn, Sn, Co) alloys were produced in an arc melter furnace in this study. After the homogenization of these alloys, the martensitic phase transformation temperatures were determined with differential-scanner calorimeter. The transformation temperature was found to be below the 37 ° C (body temperature) in Ni45Ti50Cr2.5Cu2.5, Ni48Ti51X (X=Mn, Co) alloys; and the transformation temperature of the N45Ti55, Ni48Ti51Sn alloys was found to be over 37 ° C . Then, the micro and crystal structure analyses of the alloys were made, and it was determined that Ni45Ti50Cr2.5Cu2.5, Ni48Ti51X (X=Mn, Co) alloys, which were in austenite phase at room temperature, included B2 (NiTi) phase and Ti2Ni precipitation phase, and the alloys that were in the martensite phase at room temperature included B19ı (NiTi) phase and Ti2Ni phase. The common phase in both alloy groups is the Ti2Ni phase, and this type of phase is generally seen in NiTi alloys that are rich in titanium (Ti-rich).

  12. Review on structural fatigue of NiTi shape memory alloys: Pure mechanical and thermo-mechanical ones

    Directory of Open Access Journals (Sweden)

    Guozheng Kang

    2015-11-01

    Full Text Available Structural fatigue of NiTi shape memory alloys is a key issue that should be solved in order to promote their engineering applications and utilize their unique shape memory effect and super-elasticity more sufficiently. In this paper, the latest progresses made in experimental and theoretical analyses for the structural fatigue features of NiTi shape memory alloys are reviewed. First, macroscopic experimental observations to the pure mechanical and thermo-mechanical fatigue features of the alloys are summarized; then the state-of-arts in the mechanism analysis of fatigue rupture are addressed; further, advances in the construction of fatigue failure models are provided; finally, summary and future topics are outlined.

  13. Training and two-way shape memory in NiTi alloys: influence on thermal parameters

    International Nuclear Information System (INIS)

    Lahoz, R.; Puertolas, J.A.

    2004-01-01

    The two-way shape memory effect (TWSME) was studied in a near equiatomic commercial alloy. A training procedure based on a constant load applied in the temperature range of the parent → martensite transformation was carried out on NiTi wires. The efficiency of the method was determined from deformation-temperature measurements by MTA at different training stress and number of cycles. A maximum of two shape memory strain was obtained for a stress training of 115 MPa, independently of number of training cycles. A correlation was established between the TWSME arisen and the permanent strain generated during the training. The A s and A f transitions present a positive shift and the M s and M f a negative one with increasing training stress. All the transitions temperatures decrease with the training cycling. In the trained material, the P→M and M→P temperatures and the latent heat of these conversions undergoes a strong decrease with increasing training stress, with a strong asymmetry between the forward and the reversed transitions. The changes of these thermal parameters as a function of the training parameters were studied on a thermodynamic frame

  14. Laser Shock Wave-Assisted Patterning on NiTi Shape Memory Alloy Surfaces

    Science.gov (United States)

    Ilhom, Saidjafarzoda; Seyitliyev, Dovletgeldi; Kholikov, Khomidkohodza; Thomas, Zachary; Er, Ali O.; Li, Peizhen; Karaca, Haluk E.; San, Omer

    2018-01-01

    Shape memory alloys (SMAs) are a unique class of smart materials and they were employed in various applications in engineering, biomedical, and aerospace technologies. Here, we report an advanced, efficient, and low-cost direct imprinting method with low environmental impact to create thermally controllable surface patterns. Patterned microindents were generated on Ni50Ti50 (at. %) SMAs using an Nd:YAG laser with 1064 nm wavelength at 10 Hz. Laser pulses at selected fluences were focused on the NiTi surface and generated pressure pulses of up to a few GPa. Optical microscope images showed that surface patterns with tailorable sizes can be obtained. The depth of the patterns increases with laser power and irradiation time. Upon heating, the depth profile of SMA surfaces changed where the maximum depth recovery ratio of 30% was observed. Recovery ratio decreased and stabilized when the number of pulses and thus the well depth were further increased. A numerical simulation of pressure evolution in shape memory alloys showed a good agreement with the experimental results. The stress wave closely followed the rise time of the laser pulse to its peak value and initial decay. Rapid attenuation and dispersion of the stress wave were found in our simulation.

  15. Thermomechanical behavior of NiTiPdPt high temperature shape memory alloy springs

    International Nuclear Information System (INIS)

    Nicholson, D E; Vaidyanathan, R; Padula II, S A; Noebe, R D; Benafan, O

    2014-01-01

    Transformation strains in high temperature shape memory alloys (HTSMAs) are generally smaller than for conventional NiTi alloys and can be purposefully limited in cases where stability and repeatability at elevated temperatures are desired. Yet such alloys can still be used in actuator applications that require large strokes when used in the form of springs. Thus there is a need to understand the thermomechanical behavior of shape memory alloy spring actuators, particularly those consisting of alternative alloys. In this work, a modular test setup was assembled with the objective of acquiring stroke, stress, temperature, and moment data in real time during joule heating and forced convective cooling of Ni 19.5 Ti 50.5 Pd 25 Pt 5 HTSMA springs. The spring actuators were subjected to both monotonic axial loading and thermomechanical cycling. The role of rotational constraints (i.e., by restricting rotation or allowing for free rotation at the ends of the springs) on stroke performance was also assessed. Finally, recognizing that evolution in the material microstructure can result in changes in HTSMA spring geometry, the effect of material microstructural evolution on spring performance was examined. This was done by taking into consideration the changes in geometry that occurred during thermomechanical cycling. This work thus provides insight into designing with HTSMA springs and predicting their thermomechanical performance. (paper)

  16. Laser Shock Wave-Assisted Patterning on NiTi Shape Memory Alloy Surfaces

    Science.gov (United States)

    Ilhom, Saidjafarzoda; Seyitliyev, Dovletgeldi; Kholikov, Khomidkohodza; Thomas, Zachary; Er, Ali O.; Li, Peizhen; Karaca, Haluk E.; San, Omer

    2018-03-01

    Shape memory alloys (SMAs) are a unique class of smart materials and they were employed in various applications in engineering, biomedical, and aerospace technologies. Here, we report an advanced, efficient, and low-cost direct imprinting method with low environmental impact to create thermally controllable surface patterns. Patterned microindents were generated on Ni50Ti50 (at. %) SMAs using an Nd:YAG laser with 1064 nm wavelength at 10 Hz. Laser pulses at selected fluences were focused on the NiTi surface and generated pressure pulses of up to a few GPa. Optical microscope images showed that surface patterns with tailorable sizes can be obtained. The depth of the patterns increases with laser power and irradiation time. Upon heating, the depth profile of SMA surfaces changed where the maximum depth recovery ratio of 30% was observed. Recovery ratio decreased and stabilized when the number of pulses and thus the well depth were further increased. A numerical simulation of pressure evolution in shape memory alloys showed a good agreement with the experimental results. The stress wave closely followed the rise time of the laser pulse to its peak value and initial decay. Rapid attenuation and dispersion of the stress wave were found in our simulation.

  17. A micromechanical constitutive model for anisotropic cyclic deformation of super-elastic NiTi shape memory alloy single crystals

    Science.gov (United States)

    Yu, Chao; Kang, Guozheng; Kan, Qianhua

    2015-09-01

    Based on the experimental observations on the anisotropic cyclic deformation of super-elastic NiTi shape memory alloy single crystals done by Gall and Maier (2002), a crystal plasticity based micromechanical constitutive model is constructed to describe such anisotropic cyclic deformation. To model the internal stress caused by the unmatched inelastic deformation between the austenite and martensite phases on the plastic deformation of austenite phase, 24 induced martensite variants are assumed to be ellipsoidal inclusions with anisotropic elasticity and embedded in the austenite matrix. The homogeneous stress fields in the austenite matrix and each induced martensite variant are obtained by using the Mori-Tanaka homogenization method. Two different inelastic mechanisms, i.e., martensite transformation and transformation-induced plasticity, and their interactions are considered in the proposed model. Following the assumption of instantaneous domain growth (Cherkaoui et al., 1998), the Helmholtz free energy of a representative volume element of a NiTi shape memory single crystal is established and the thermodynamic driving forces of the internal variables are obtained from the dissipative inequalities. The capability of the proposed model to describe the anisotropic cyclic deformation of super-elastic NiTi single crystals is first verified by comparing the predicted results with the experimental ones. It is concluded that the proposed model can capture the main quantitative features observed in the experiments. And then, the proposed model is further used to predict the uniaxial and multiaxial transformation ratchetting of a NiTi single crystal.

  18. Laser beam welding of NiTi-shape memory alloys; Laserstrahl-Schweissen von NiTi-Formgedaechtnislegierungen

    Energy Technology Data Exchange (ETDEWEB)

    Haas, T.

    1996-04-01

    Using a Nd:YAG laser, the weldability of binary nickel-titanium shape memory alloys containing 50.0 and 48.5 at.-% Ti respectively was investigated. By tensile tests within a temperature range of -80 C to +200 C the mechanical properties of the laser welded joints were examined. Changes in the transformation behaviour were detected by calorimetric measurements (DSC method). The stress-strain behaviour was attributed to the microstructure of the welds, revealed by optical microscopy and transmission electron microscopy (TEM). Using a scanning electron microscope (SEM), the mechanisms of failure were examined. Joints of the martensitic Ti-rich alloy were brittle, showing an ultimate tensile strength of 600 MPa, corresponding to half of the value of the base material. The reduction in strength was explained by the formation of Ti{sub 2}Ni precipitations along grain boundaries in the weld. Since the welds still exhibited twin deformation, pseudoplastic strains of 7% were achieved. Ultimate strength data showed a very low scatter. Therefore it was possible to use the shape memory effect up to a strain of 6% without failure. After a total elongation to 6% strain, the laser welded joints showed a free recovery with an amnesia of 0.3%. The shape memory effect was shown to be retained in the laser welded joints. 154 refs.

  19. Application of Taguchi method to optimization of surface roughness during precise turning of NiTi shape memory alloy

    Science.gov (United States)

    Kowalczyk, M.

    2017-08-01

    This paper describes the research results of surface quality research after the NiTi shape memory alloy (Nitinol) precise turning by the tools with edges made of polycrystalline diamonds (PCD). Nitinol, a nearly equiatomic nickel-titanium shape memory alloy, has wide applications in the arms industry, military, medicine and aerospace industry, and industrial robots. Due to their specific properties NiTi alloys are known to be difficult-to-machine materials particularly by using conventional techniques. The research trials were conducted for three independent parameters (vc, f, ap) affecting the surface roughness were analyzed. The choice of parameter configurations were performed by factorial design methods using orthogonal plan type L9, with three control factors, changing on three levels, developed by G. Taguchi. S/N ratio and ANOVA analyses were performed to identify the best of cutting parameters influencing surface roughness.

  20. Precipitation of Ni4Ti3-variants in a polycrystalline Ni-rich NiTi shape memory alloy

    Czech Academy of Sciences Publication Activity Database

    Bojda, Ondřej; Eggeler, G.; Dlouhý, Antonín

    2005-01-01

    Roč. 53, č. 1 (2005), s. 99-104 ISSN 1359-6462 R&D Projects: GA ČR(CZ) GA106/05/0918 Institutional research plan: CEZ:AV0Z20410507 Keywords : NiTi shape memory alloys * Ni4Ti3 precipitation * Transmission electron microscopy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.228, year: 2005

  1. Deformation and Phase Transformation Processes in Polycrystalline NiTi and NiTiHf High Temperature Shape Memory Alloys

    Science.gov (United States)

    Benafan, Othmane

    2012-01-01

    The deformation and transformation mechanisms of polycrystalline Ni49.9Ti50.1 and Ni50.3Ti29.7Hf20 (in at.%) shape memory alloys were investigated by combined experimental and modeling efforts aided by an in situ neutron diffraction technique at stress and temperature. The thermomechanical response of the low temperature martensite, the high temperature austenite phases, and changes between these two states during thermomechanical cycling were probed and reported. In the cubic austenite phase, stress-induced martensite, deformation twinning and slip processes were observed which helped in constructing a deformation map that contained the limits over which each of the identified mechanisms was dominant. Deformation of the monoclinic martensitic phase was also investigated where the microstructural changes (texture, lattice strains, and phase fractions) during room-temperature deformation and subsequent thermal cycling were compared to the bulk macroscopic response. When cycling between these two phases, the evolution of inelastic strains, along with the shape setting procedures were examined and used for the optimization of the transformation properties as a function of deformation levels and temperatures. Finally, this work was extended to the development of multiaxial capabilities at elevated temperatures for the in situ neutron diffraction measurements of shape memory alloys on the VULCAN Diffractometer at Oak Ridge National Laboratory.

  2. Effect of ageing temperatures on pseudoelasticity of Ni-rich NiTi shape memory alloy

    Science.gov (United States)

    Mohamad, Hishamiakim; Mahmud, Abdus Samad; Nashrudin, Muhammad Naqib; Razali, Muhammad Fauzinizam

    2018-05-01

    The shape memory behavior of NiTi alloy is very sensitive to alloy composition and heat treatments, particularly annealing and ageing. This paper analysed the effect of ageing towards the thermomechanical behaviour of Ti-51at%Ni wire. The analysis focused on the effect of ageing at the different temperature on thermal transformation sequence and tensile deformation behaviour with respect to the recoverability of the alloy. It was found that B2-R transformation peak appeared in the differential scanning calorimetry (DSC) measurement when the alloys were aged at the temperature between 400°C to 475°C for 30 minutes. Further ageing at 500°C to 550°C yielded two stage transformation, B2-R-B19' in cooling. All aged wires exhibited good pseudoelastic behaviour when deformed at room temperature and yielded below 1% residual strain upon unloading. Ageing at 450°C resulted the smallest unrecovered strain of about 0.4%.

  3. Correlation between Mechanical Behavior and Actuator-type Performance of Ni-Ti-Pd High-temperature Shape Memory Alloys

    Science.gov (United States)

    Bigelow, Glen S.; Padula, Santo A., II; Garg, Anita; Noebe, Ronald D.

    2007-01-01

    High-temperature shape memory alloys in the NiTiPd system are being investigated as lower cost alternatives to NiTiPt alloys for use in compact solid-state actuators for the aerospace, automotive, and power generation industries. A range of ternary NiTiPd alloys containing 15 to 46 at.% Pd has been processed and actuator mimicking tests (thermal cycling under load) were used to measure transformation temperatures, work behavior, and dimensional stability. With increasing Pd content, the work output of the material decreased, while the amount of permanent strain resulting from each load-biased thermal cycle increased. Monotonic isothermal tension testing of the high-temperature austenite and low temperature martensite phases was used to partially explain these behaviors, where a mismatch in yield strength between the austenite and martensite phases was observed at high Pd levels. Moreover, to further understand the source of the permanent strain at lower Pd levels, strain recovery tests were conducted to determine the onset of plastic deformation in the martensite phase. Consequently, the work behavior and dimensional stability during thermal cycling under load of the various NiTiPd alloys is discussed in relation to the deformation behavior of the materials as revealed by the strain recovery and monotonic tension tests.

  4. High quality vacuum induction melting of small quantities of NiTi shape memory alloys in graphite crucibles

    International Nuclear Information System (INIS)

    Frenzel, J.; Zhang, Z.; Neuking, K.; Eggeler, G.

    2004-01-01

    Binary NiTi based shape memory alloys can be produced starting from the pure elements (Ni-pellets, Ti-rods) by using vacuum induction melting (VIM). VIM ingot metallurgy is known to produce materials with a good chemical homogeneity; it, moreover, is cheaper than vacuum arc melting (VAM) when small quantities of laboratory materials are needed. In a VIM procedure, graphite crucibles are attractive because they have appropriate electrical properties. For NiTi melting, graphite crucibles are interesting because they are reasonably priced and they show a good resistance against thermal cracking. On the other hand, it is well known that melting of Ti alloys in graphite crucibles is associated with a vigorous interface reaction. And the carbon concentration of NiTi alloys needs to be kept below a certain minimum in order to assure that the functional properties of the alloys meet the required targets. Therefore, it is important to minimize the carbon pick up of the melt. The present work presents experimental results and discusses thermodynamic and kinetic aspects of the reaction of NiTi melts with graphite crucibles; a method is suggested to keep the carbon dissolution into the melt at a minimum

  5. Forming and control of pores by capsule-free hot isostatic pressing in NiTi shape memory alloys

    International Nuclear Information System (INIS)

    Yuan, B; Zhu, M; Gao, Y; Li, X; Chung, C Y

    2008-01-01

    In this study, the pore evolution process of porous NiTi shape memory alloys (SMAs) fabricated by capsule-free hot isostatic pressing (CF-HIP) was investigated by adopting different fabricating parameters. It is shown that porous NiTi SMAs with homogeneous pore distribution and nearly spherical pore shape can be prepared by CF-HIP under suitable conditions. In addition, two novel pore structures were produced, one with a sandwich-like structure, and another with controlled gradient of porosity along the radial direction, with pore size increasing from the outside towards the center of the specimen. The former was obtained by balancing the pressure in the HIP chamber and the gas pressure resulting from the gas expansion in the green sample. The latter resulted from the formation of air bubbles in the liquid phase during the sintering

  6. Influence of Structure and Microstructure on Deformation Localization and Crack Growth in NiTi Shape Memory Alloys

    Science.gov (United States)

    Paul, Partha P.; Fortman, Margaret; Paranjape, Harshad M.; Anderson, Peter M.; Stebner, Aaron P.; Brinson, L. Catherine

    2018-04-01

    Porous NiTi shape memory alloys have applications in the biomedical and aerospace fields. Recent developments in metal additive manufacturing have made fabrication of near-net-shape porous products with complicated geometries feasible. There have also been developments in tailoring site-specific microstructures in metals using additive manufacturing. Inspired by these developments, we explore two related mechanistic phenomena in a simplified representation of porous shape memory alloys. First, we computationally elucidate the connection between pore geometry, stress concentration around pores, grain orientation, and strain-band formation during tensile loading of NiTi. Using this, we present a method to engineer local crystal orientations to mitigate the stress concentrations around the pores. Second, we experimentally document the growth of cracks around pores in a cyclically loaded superelastic NiTi specimen. In the areas of stress concentration around holes, cracks are seen to grow in large grains with [1 1 0] oriented along the tensile axis. This combined work shows the potential of local microstructural engineering in reducing stress concentration and increasing resistance to propagation of cracks in porous SMAs, potentially increasing the fatigue life of porous SMA components.

  7. Tribological performance of near equiatomic and Ti-rich NiTi shape memory alloy thin films

    International Nuclear Information System (INIS)

    Tillmann, Wolfgang; Momeni, Soroush

    2015-01-01

    Near equiatomic and Ti-rich NiTi shape memory alloy thin films were magnetron sputtered with the same processing parameters and thickness of 3 μm. The microstructure, composition, shape memory behavior, mechanical and tribological properties of the deposited thin films were analyzed by using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), differential scanning calorimetry (DSC), nanoindentation, ball-on-disc, scratch test, and three dimensional (3D) optical microscopy. The obtained results clearly show how the crystallization evolution and precipitation formation of these two sets of thin films can drastically influence their mechanical and tribological performances

  8. Martensitic transformation and shape memory effect in NiTi alloy covered by chitosan/silver layer

    Directory of Open Access Journals (Sweden)

    Goryczka Tomasz

    2015-01-01

    Full Text Available The NiTi shape memory alloy was covered with chitosan/silver layer. Coatings were deposited at room temperature using combination of processing parameters such as deposition voltage and amount of silver in colloidal suspension. Structure of layers was studied by means of X-ray diffraction. Quality of the coatings was evaluated basing on observations done in scanning electron microscopy. Transformation behaviour of coated samples was studied with use of differential scanning calorimeter. The covered sample revealed presence of the reversible martensitic transformation and ability to deformation (in bending mode up to 8%. Forward martensitic transformation, in as-received NiTi alloy and in alloy after layer deposition occurred in two steps B2-R-B19’. After deformation quality of the chitosan/silver layer remained unchanged.

  9. Microstructure and mechanical behavior of a shape memory Ni-Ti bi-layer thin film

    Energy Technology Data Exchange (ETDEWEB)

    Mohri, Maryam [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran (Iran, Islamic Republic of); Karlsruhe Institute of Technology, Institute of Nanotechnology, 76021 Karlsruhe (Germany); Nili-Ahmadabadi, Mahmoud, E-mail: nili@ut.ac.ir [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran (Iran, Islamic Republic of); Center of Excellence for High Performance Materials, University of Tehran, Tehran (Iran, Islamic Republic of); Ivanisenko, Julia [Karlsruhe Institute of Technology, Institute of Nanotechnology, 76021 Karlsruhe (Germany); Schwaiger, Ruth [Karlsruhe Institute of Technology, Institute for Applied Materials, 76021 Karlsruhe (Germany); Hahn, Horst; Chakravadhanula, Venkata Sai Kiran [Karlsruhe Institute of Technology, Institute of Nanotechnology, 76021 Karlsruhe (Germany)

    2015-05-29

    Two different single-layers and a bi-layer Ni-Ti thin films with chemical compositions of Ni{sub 45}Ti{sub 50}Cu{sub 5}, Ni{sub 50.8}Ti{sub 49.2} and Ni{sub 50.8}Ti{sub 49.2}/Ni{sub 45}Ti{sub 50}Cu{sub 5} (numbers indicate at.%) determined by energy dispersive X-ray spectroscopy were deposited on Si (111) substrates using DC magnetron sputtering. The structures, surface morphology and transformation temperatures of annealed thin films at 500 °C for 15 min and 1 h were studied using grazing incidence X-ray diffraction, transmission electron microscopy (TEM), atomic force microscopy and differential scanning calorimetry (DSC), respectively. Nanoindentation was used to characterize the mechanical properties. The DSC and X-ray diffraction results indicated the austenitic structure of the Ni{sub 50.8}Ti{sub 49.2} and martensitic structure of the Ni{sub 45}Ti{sub 50}Cu{sub 5} thin films while the bi-layer was composed of austenitic and martensitic thin films. TEM study revealed that copper encourages crystallization in the bi-layer such that crystal structure containing nano-precipitates in the Ni{sub 45}Ti{sub 50}Cu{sub 5} layer was detected after 15 min annealing while the Ni{sub 50.8}Ti{sub 49.2} layer crystallized after 60 min at 500 °C. Furthermore, after annealing at 500 °C for 15 min, a precipitate free zone and thin layer amorphous were observed closely to the interface in the top layer. The bi-layer was completely crystallized at 500 °C for 1 h and the orientation of the Ni-rich precipitates indicated a stress gradient in the bi-layer. The bi-layer thin film showed different transformation temperatures and mechanical behavior from the single-layers. The developed bi-layer has different phase transformation temperatures, the higher temperatures of shape memory effect and lower temperature of pseudo-elastic behavior compared to the single-layers. Also, the bi-layer thin film exhibited a combined pseudo-elastic behavior and shape memory effect with a reduced

  10. On the widths of the hysteresis of mechanically and thermally induced martensitic transformations in Ni-Ti-based shape memory alloys

    Energy Technology Data Exchange (ETDEWEB)

    Jaeger, Stefanie; Maass, Burkhard; Frenzel, Jan; Schmidt, Marvin; Ullrich, Johannes; Seelecke, Stefan; Schuetze, Andreas; Kastner, Oliver; Eggeler, Gunther [Bochum Univ. (Germany). Inst. fuer Werkstoffe

    2015-10-15

    It is well known that a good crystallographic compatibility between austenite and martensite in Ni-Ti-based shape memory alloys results in narrow thermal hystereses (e.g. Ball and James, Arch. Ration. Mech. Anal., 1987). The present work suggests that a good crystallographic fit is moreover associated with a small mechanical hysteresis width, observed during a forward and reverse stress-induced transformation. Furthermore, shape memory alloys with a good crystallographic fit show smaller transformation strains. The results obtained in the present study suggest that these correlations are generic and apply to binary Ni-Ti (with varying Ni contents) and quaternary Ni-Ti-Cu-X (X = Cr, Fe, V) alloys. For binary Ni-Ti, it was observed that Ni-rich compositions (good lattice fit) show a lower accumulation of irreversible strains during pseudoelastic cycling.

  11. An in situ neutron diffraction study of shape setting shape memory NiTi

    International Nuclear Information System (INIS)

    Benafan, O.; Padula, S.A.; Noebe, R.D.; Brown, D.W.; Clausen, B.; Vaidyanathan, R.

    2013-01-01

    A bulk polycrystalline Ni 49.9 Ti 50.1 (at.%) shape memory alloy specimen was shape set while neutron diffraction spectra were simultaneously acquired. The objective was to correlate internal stress, phase volume fraction, and texture measurements (from neutron diffraction spectra) with the macroscopic stress and shape changes (from load cell and extensometry measurements) during the shape setting procedure and subsequent shape recovery. Experimental results showed the evolution of the martensitic transformation (lattice strains, phase fractions and texture) against external constraints during both heating and cooling. Constrained heating resulted in a build-up of stresses during the martensite to austenite transformation, followed by stress relaxation due to thermal expansion, final conversion of retained martensite, and recovery processes. Constrained cooling also resulted in stress build-up arising from thermal contraction and early formation of martensite, followed by relaxation as the austenite fully transformed to martensite. Comparisons were also made between specimens pre-shape set and post-shape set with and without external constraints. The specimens displayed similar shape memory behavior consistent with the microstructure of the shape set sample, which was mostly unchanged by the shape setting process and similar to that of the as-received material

  12. Effects of Hydrogen Charging on the Phase Transformation of Martensitic NiTi Shape Memory Alloy Wires

    Science.gov (United States)

    Snir, Yoav; Carl, Matthew; Ley, Nathan A.; Young, Marcus L.

    2017-12-01

    Ti-rich martensitic NiTi shape memory alloy (SMA) wires of 0.5 mm diameter were tested under hydrogen-charging conditions to reveal the effects on phase transformation. Hydrogen charging was performed by immersion testing for several durations. The SMA wires were characterized by differential scanning calorimetry (DSC), scanning electron microscopy with energy dispersive spectroscopy, and synchrotron radiation X-ray diffraction (SR-XRD) for the the as-received, polished, and hydrogen-charged conditions. The DSC revealed the phase-transformation behavior of the NiTi SMA wires. Single and triple heating/cooling cycles in the DSC show the relationship between hydrogen and temperature on the material. Five distinct peaks (peaks I-V) are observed during heating/cooling in the DSC. Peak I corresponds to the martensite-to-austenite (M → A) transformation. Peaks II, III, and IV are related to hydrogen charging. Peak II appears at about 210-230 °C, while peaks III and IV appear at about 350 and 440 °C, respectively. These higher temperature peaks, peaks II-IV, were observed for the first time for a martensitic NiTi SMA due to the large temperature range covered using the DSC. Only one peak (peak V) appears during cooling and corresponds to the austenite-to-martensite transformation peak. Ex situ and in situ SR-XRD revealed the phases and the crystallographic relationship to peaks I-V in the DSC.

  13. Rapid Obtaining of Nano-Hydroxyapatite Bioactive Films on NiTi Shape Memory Alloy by Electrodeposition Process

    Science.gov (United States)

    Lobo, A. O.; Otubo, J.; Matsushima, J. T.; Corat, E. J.

    2011-07-01

    Nano-hydroxyapatite (n-HA) crystalline films have been developed in this study by electrodeposition method on NiTi shape memory alloy (SMA). The electrodeposition of the n-HA films was carried out using 0.042 mol/L Ca(NO3)2 · 4H2O + 0.025 mol/L (NH4) · 2HPO4 electrolytes by applying a constant potential of -2.0 V for 120 min and keeping the solution temperature at 70 °C. The characterization of n-HA films is of special importance since bioactive properties related to n-HA have been directly identified with its specific composition and crystalline structure. AFM, XRD, EDX, FEG-SEM and Raman spectroscopy shows a homogeneous film, with high crystallinity, special composition, and bioactivity properties (Ca/P = 1.93) of n-HA on NiTi SMA surfaces. The n-HA coating with special structure would benefit the use of NiTi alloy in orthopedic applications.

  14. Effect of different stages of deformation on the microstructure evolution of Ti-rich NiTi shape memory alloy

    Energy Technology Data Exchange (ETDEWEB)

    Tadayyon, Ghazal, E-mail: Ghazal.tadayyon@gmail.com [Department of Metallurgical and Materials Engineering, Faculty of Engineering, Ferdowsi University of Mashhad (Iran, Islamic Republic of); Centre for Research in Medical Devices (CURAM), National University of Ireland, Galway (Ireland); Guo, Yina, E-mail: Yina.Guo@ul.ie [Materials and Surface Science Institute, University of Limerick, Limerick (Ireland); Mazinani, Mohammad, E-mail: mazinani@um.ac.ir [Department of Metallurgical and Materials Engineering, Faculty of Engineering, Ferdowsi University of Mashhad (Iran, Islamic Republic of); Zebarjad, Seyed Mojtaba, E-mail: mojtabazebarjad@shirazu.ac.ir [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz (Iran, Islamic Republic of); Tiernan, Peter, E-mail: Peter.Tiernan@ul.ie [Materials and Surface Science Institute, University of Limerick, Limerick (Ireland); Tofail, Syed A.M., E-mail: Tofail.Syed@ul.ie [Materials and Surface Science Institute, University of Limerick, Limerick (Ireland); Biggs, Manus J.P., E-mail: manus.biggs@nuigalway.ie [Centre for Research in Medical Devices (CURAM), National University of Ireland, Galway (Ireland)

    2017-03-15

    The main objective of this work was to investigate the thermomechanical behavior and microstructural changes of a Ti-rich NiTi shape memory alloy (SMA). The microstructural and texture evolution of aged NiTi alloy at different degrees of deformation were elicited by transmission electron microscopy (TEM). An effort was made to correlate results obtained from the tensile test with results from microstructure studies. The undeformed sample reveals a self-accommodated morphology with straight and well defined twin boundaries. At different stages of deformation, diverse mechanisms were involved. These mechanisms include marstraining, detwinning accompanied by dislocation movement, and finally, severe plastic deformation, subdivision and amorphization of the matrix. Under increasing strains, high density lattice defects were generated and the morphology of B19’ became disordered. - Graphical abstract: The summary of microstructure changes of the martensite twins during tensile deformation in polycrystalline NiTi SMAs. - Highlights: • Initial elastic response, dislocation avalanche and deformation bands were studied. • < 011 > Type II twin accompanied by detwinned area after 2% cold work was observed. • Visible parallel fine stacking faults showed plastic flow of the material. • At higher strains, subgrains changed to recrystallized, finely amorphous structure.

  15. Experimental study on Response Parameters of Ni-rich NiTi Shape Memory Alloy during Wire Electric Discharge Machining

    Science.gov (United States)

    Bisaria, Himanshu; Shandilya, Pragya

    2018-03-01

    Nowadays NiTi SMAs are gaining more prominence due to their unique properties such as superelasticity, shape memory effect, high fatigue strength and many other enriched physical and mechanical properties. The current studies explore the effect of machining parameters namely, peak current (Ip), pulse off time (TOFF), and pulse on time (TON) on wire wear ratio (WWR), and dimensional deviation (DD) in WEDM. It was found that high discharge energy was mainly ascribed to high WWR and DD. The WWR and DD increased with the increase in pulse on time and peak current whereas high pulse off time was favourable for low WWR and DD.

  16. Characterization of Sputtered Nickel-Titanium (NiTi) Stress and Thermally Actuated Cantilever Bimorphs Based on NiTi Shape Memory Alloy (SMA)

    Science.gov (United States)

    2015-11-01

    necessary anneal . Following this, a thin film of NiTi was blanket sputtered at 600 °C. This NiTi blanket layer was then wet -etch patterned using a...varying the sputter parameters during NiTi deposition, such as thickness, substrate temperature during deposition and anneal , and argon pressure during...6 Fig. 4 Surface texture comparison between NiTi sputtered at RT, then annealed at 600 °C, and NiTi

  17. Evaluation of the interfacial shear strength between pseudoplastic NiTi shape memory alloy wires and epoxy by the pull-out method

    International Nuclear Information System (INIS)

    Spārniņš, E; Michaud, V; Leterrier, Y; Andersons, J

    2015-01-01

    The interfacial shear strength (IFSS) between nickel–titanium (NiTi) shape memory alloy wires, characterized by a nonlinear stress–strain behavior, and epoxy matrix was determined by pull-out tests. Tests were carried out at several temperatures and levels of pre-strain in the wires, to evaluate the effects of embedded wire length and of crystalline state of the alloy. The IFSS between the twinned NiTi and epoxy was estimated at 24 MPa, and found to increase to 47 MPa for completely detwinned and preloaded martensitic NiTi. This increase in IFSS values was attributed to microcracking of the superficial TiO 2 layer and the resulting roughening of the NiTi wire surface. (paper)

  18. Development of a self-stressing NiTiNb shape memory alloy (SMA)/fiber reinforced polymer (FRP) patch

    International Nuclear Information System (INIS)

    El-Tahan, M; Dawood, M; Song, G

    2015-01-01

    The objective of this research is to develop a self-stressing patch using a combination of shape memory alloys (SMAs) and fiber reinforced polymer (FRP) composites. Prestressed carbon FRP patches are emerging as a promising alternative to traditional methods to repair cracked steel structures and civil infrastructure. However, prestressing these patches typically requires heavy and complex fixtures, which is impractical in many applications. This paper presents a new approach in which the prestressing force is applied by restraining the shape memory effect of NiTiNb SMA wires. The wires are subsequently embedded in an FRP overlay patch. This method overcomes the practical challenges associated with conventional prestressing. This paper presents the conceptual development of the self-stressing patch with the support of experimental observations. The bond between the SMA wires and the FRP is evaluated using pull-out tests. The paper concludes with an experimental study that evaluates the patch response during activation subsequent monotonic tensile loading. The results demonstrate that the self-stressing patch with NiTiNb SMA is capable of generating a significant prestressing force with minimal tool and labor requirements. (paper)

  19. The effect of martensite plasticity on the cyclic deformation of super-elastic NiTi shape memory alloy

    International Nuclear Information System (INIS)

    Song, Di; Kang, Guozheng; Kan, Qianhua; Yu, Chao; Zhang, Chuanzeng

    2014-01-01

    Based on stress-controlled cyclic tension–unloading experiments with different peak stresses, the effect of martensite plasticity on the cyclic deformation of super-elastic NiTi shape memory alloy micro-tubes is investigated and discussed. The experimental results show that the reverse transformation from the induced martensite phase to the austenite phase is gradually restricted by the plastic deformation of the induced martensite phase caused by an applied peak stress that is sufficiently high (higher than 900 MPa), and the extent of such restriction increases with further increasing the peak stress. The residual and peak strains of super-elastic NiTi shape memory alloy accumulate progressively, i.e., transformation ratchetting occurs during the cyclic tension–unloading with peak stresses from 600 to 900 MPa, and the transformation ratchetting strain increases with the increase of the peak stress. When the peak stress is higher than 900 MPa, the peak strain becomes almost unchanged, but the residual strain accumulates and the dissipation energy per cycle decreases very quickly with the increasing number of cycles due to the restricted reverse transformation by the martensite plasticity. Furthermore, a quantitative relationship between the applied stress and the stabilized residual strain is obtained to reasonably predict the evolution of the peak strain and the residual strain. (paper)

  20. Laser welding of NiTi shape memory alloy: Comparison of the similar and dissimilar joints to AISI 304 stainless steel

    Science.gov (United States)

    Mirshekari, G. R.; Saatchi, A.; Kermanpur, A.; Sadrnezhaad, S. K.

    2013-12-01

    The unique properties of NiTi alloy, such as its shape memory effect, super-elasticity and biocompatibility, make it ideal material for various applications such as aerospace, micro-electronics and medical device. In order to meet the requirement of increasing applications, great attention has been given to joining of this material to itself and to other materials during past few years. Laser welding has been known as a suitable joining technique for NiTi shape memory alloy. Hence, in this work, a comparative study on laser welding of NiTi wire to itself and to AISI 304 austenitic stainless steel wire has been made. Microstructures, mechanical properties and fracture morphologies of the laser joints were investigated using optical microscopy, scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X-ray diffraction analysis (XRD), Vickers microhardness (HV0.2) and tensile testing techniques. The results showed that the NiTi-NiTi laser joint reached about 63% of the ultimate tensile strength of the as-received NiTi wire (i.e. 835 MPa) with rupture strain of about 16%. This joint also enabled the possibility to benefit from the pseudo-elastic properties of the NiTi component. However, tensile strength and ductility decreased significantly after dissimilar laser welding of NiTi to stainless steel due to the formation of brittle intermetallic compounds in the weld zone during laser welding. Therefore, a suitable modification process is required for improvement of the joint properties of the dissimilar welded wires.

  1. Preparation of Ni-Ti shape memory alloy by spark plasma sintering method

    Czech Academy of Sciences Publication Activity Database

    Salvetr, P.; Kubatík, Tomáš František; Novák, P.

    2016-01-01

    Roč. 16, č. 4 (2016), s. 804-808 ISSN 1213-2489 Institutional support: RVO:61389021 Keywords : Ni-Ti alloy * Powder metallurgy * Reactive sintering * Spark plasma sintering Subject RIV: JK - Corrosion ; Surface Treatment of Materials

  2. Effects of water plasma immersion ion implantation on surface electrochemical behavior of NiTi shape memory alloys in simulated body fluids

    International Nuclear Information System (INIS)

    Liu, X.M.; Wu, S.L.; Chu, Paul K.; Chung, C.Y.; Chu, C.L.; Yeung, K.W.K.; Lu, W.W.; Cheung, K.M.C.; Luk, K.D.K.

    2007-01-01

    Water plasma immersion ion implantation (PIII) was conducted on orthopedic NiTi shape memory alloy to enhance the surface electrochemical characteristics. The surface composition of the NiTi alloy before and after H 2 O-PIII was determined by X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM) was utilized to determine the roughness and morphology of the NiTi samples. Potentiodynamic polarization tests and electrochemical impedance spectroscopy (EIS) were carried out to investigate the surface electrochemical behavior of the control and H 2 O-PIII NiTi samples in simulated body fluids (SBF) at 37 deg. C as well as the mechanism. The H 2 O-PIII NiTi sample showed a higher breakdown potential (E b ) than the control sample. Based on the AFM results, two different physical models with related equivalent electrical circuits were obtained to fit the EIS data and explain the surface electrochemical behavior of NiTi in SBF. The simulation results demonstrate that the higher resistance of the oxide layer produced by H 2 O-PIII is primarily responsible for the improvement in the surface corrosion resistance

  3. PIIID-formed (Ti, O)/Ti, (Ti, N)/Ti and (Ti, O, N)/Ti coatings on NiTi shape memory alloy for medical applications

    Energy Technology Data Exchange (ETDEWEB)

    Sun Tao, E-mail: taosun@hotmail.com.hk [Department of Mechanical Engineering, University of Hong Kong, Pokfulam Road (Hong Kong); Institute of Microelectronics, Agency for Science, Technology and Research (A-STAR) (Singapore); Wang Langping, E-mail: aplpwang@hit.edu.cn [State Key Lab of Advanced Welding and Joining, Harbin Institute of Technology (China); Wang Min; Tong Howang [Department of Mechanical Engineering, University of Hong Kong, Pokfulam Road (Hong Kong); Lu, William W. [Department of Orthopedics and Traumatology, University of Hong Kong, Sassoon Road (Hong Kong)

    2012-08-01

    (Ti, O)/Ti, (Ti, N)/Ti and (Ti, O, N)/Ti composite coatings were fabricated on NiTi shape memory alloy via plasma immersion ion implantation and deposition (PIIID). Surface morphology of samples was investigated using atomic force microscopy (AFM) and scanning electron microscopy (SEM). Cross-sectional morphology indicated that the PIIID-formed coatings were dense and uniform. X-ray diffraction (XRD) was used to characterize the phase composition of samples. X-ray photoelectron spectroscopy (XPS) results showed that the surface of coated NiTi SMA samples was Ni-free. Nanoindentation measurements and pin-on-disc tests were carried out to evaluate mechanical properties and wear resistance of coated NiTi SMA, respectively. For the in vitro biological assessment of the composite coatings in terms of cell morphology and cell viability, osteoblast-like SaOS-2 cells and breast cancer MCF-7 cells were cultured on NiTi SMA samples, respectively. SaOS-2 cells attached and spread better on coated NiTi SMA. Viability of MCF-7 cells showed that the PIIID-formed composite coatings were noncytotoxic and coated samples were more biocompatible than uncoated samples. - Highlights: Black-Right-Pointing-Pointer PIIID-formed coatings were fabricated on NiTi SMA to improve its biocompatibility. Black-Right-Pointing-Pointer Microstructure, mechanical properties and biocompatibility of coatings were investigated. Black-Right-Pointing-Pointer All PIIID-formed composite coatings were noncytotoxic and cytocompatible.

  4. Influence of Test Procedures on the Thermomechanical Properties of a 55NiTi Shape Memory Alloy

    Science.gov (United States)

    Padula, Santo A., II; Gaydosh, Darrell J.; Noebe, Ronald D.; Bigelow, Glen S.; Garg, Anita; Lagoudas, Dimitris; Karaman, Ibrahim; Atli, Kadri C.

    2008-01-01

    Over the past few decades, binary NiTi shape memory alloys have received attention due to their unique mechanical characteristics, leading to their potential use in low-temperature, solid-state actuator applications. However, prior to using these materials for such applications, the physical response of these systems to mechanical and thermal stimuli must be thoroughly understood and modeled to aid designers in developing SMA-enabled systems. Even though shape memory alloys have been around for almost five decades, very little effort has been made to standardize testing procedures. Although some standards for measuring the transformation temperatures of SMA s are available, no real standards exist for determining the various mechanical and thermomechanical properties that govern the usefulness of these unique materials. Consequently, this study involved testing a 55NiTi alloy using a variety of different test methodologies. All samples tested were taken from the same heat and batch to remove the influence of sample pedigree on the observed results. When the material was tested under constant-stress, thermal-cycle conditions, variations in the characteristic material responses were observed, depending on test methodology. The transformation strain and irreversible strain were impacted more than the transformation temperatures, which only showed an affect with regard to applied external stress. In some cases, test methodology altered the transformation strain by 0.005-0.01mm/mm, which translates into a difference in work output capability of approximately 2 J/cu cm (290 in!lbf/cu in). These results indicate the need for the development of testing standards so that meaningful data can be generated and successfully incorporated into viable models and hardware. The use of consistent testing procedures is also important when comparing results from one research organization to another. To this end, differences in the observed responses will be presented, contrasted and

  5. Wafer-level integration of NiTi shape memory alloy on silicon using Au–Si eutectic bonding

    International Nuclear Information System (INIS)

    Gradin, Henrik; Bushra, Sobia; Braun, Stefan; Stemme, Göran; Van der Wijngaart, Wouter

    2013-01-01

    This paper reports on the wafer level integration of NiTi shape memory alloy (SMA) sheets with silicon substrates through Au–Si eutectic bonding. Different bond parameters, such as Au layer thicknesses and substrate surface treatments were evaluated. The amount of gold in the bond interface is the most important parameter to achieve a high bond yield; the amount can be determined by the barrier layers between the Au and Si or by the amount of Au deposition. Deposition of a gold layer of more than 1 μm thickness before bonding gives the most promising results. Through patterning of the SMA sheet and by limiting bonding to small areas, stresses created by the thermal mismatch between Si and NiTi are reduced. With a gold layer of 1 μm thickness and bond areas between 200 × 200 and 800 × 800 μm 2 a high bond strength and a yield above 90% is demonstrated. (paper)

  6. Grain size effects on stability of nonlinear vibration with nanocrystalline NiTi shape memory alloy

    Science.gov (United States)

    Xia, Minglu; Sun, Qingping

    2017-10-01

    Grain size effects on stability of thermomechanical responses for a nonlinear torsional vibration system with nanocrystalline superelastic NiTi bar are investigated in the frequency and amplitude domains. NiTi bars with average grain size from 10 nm to 100 nm are fabricated through cold-rolling and subsequent annealing. Thermomechanical responses of the NiTi bar as a softening nonlinear damping spring in the torsional vibration system are obtained by synchronised acquisition of rotational angle and temperature under external sinusoidal excitation. It is shown that nonlinearity and damping capacity of the NiTi bar decrease as average grain size of the material is reduced below 100 nm. Therefore jump phenomena of thermomechanical responses become less significant or even vanish and the vibration system becomes more stable. The work in this paper provides a solid experimental base for manipulating the undesired jump phenomena of thermomechanical responses and stabilising the mechanical vibration system through grain refinement of NiTi SMA.

  7. Three-dimensional modeling for deformation of austenitic NiTi shape memory alloys under high strain rate

    Science.gov (United States)

    Yu, Hao; Young, Marcus L.

    2018-01-01

    A three-dimensional model for phase transformation of shape memory alloys (SMAs) during high strain rate deformation is developed and is then calibrated based on experimental results from an austenitic NiTi SMA. Stress, strain, and martensitic volume fraction distribution during high strain rate deformation are simulated using finite element analysis software ABAQUS/standard. For the first time, this paper presents a theoretical study of the microscopic band structure during high strain rate compressive deformation. The microscopic transformation band is generated by the phase front and leads to minor fluctuations in sample deformation. The strain rate effect on phase transformation is studied using the model. Both the starting stress for transformation and the slope of the stress-strain curve during phase transformation increase with increasing strain rate.

  8. Orientation dependence of stress-induced martensite formation during nanoindentation in NiTi shape memory alloys

    International Nuclear Information System (INIS)

    Laplanche, G.; Pfetzing-Micklich, J.; Eggeler, G.

    2014-01-01

    In the present work we used nanoindentation with a spherical indenter tip to study the formation of stress-induced martensite in NiTi shape memory alloys. Prior to nanoindentation, orientation imaging was performed to select austenite grains with specific crystallographic orientations, including the principal crystallographic directions [0 0 1], [1 0 1] and [1 1 1]. We studied a material where stress-induced martensite is stable at room temperature and found surface patterns with four-, two- and threefold symmetries for the [0 0 1], [1 0 1] and [1 1 1] crystallographic indentation directions, respectively. Atomic force microscopy investigations of the topography showed that the surface patterns were associated with sink-ins. The crystallographic sink-in patterns disappeared during heating, which proved their martensitic origin. Our results provide clear experimental evidence which shows that the crystallographic anisotropy of nanoindentation is governed by the crystallographic anisotropy of the stress-induced formation of martensite

  9. Texture development and strain hysteresis in a NiTi shape-memory alloy during thermal cycling under load

    International Nuclear Information System (INIS)

    Ye, B.; Majumdar, B.S.; Dutta, I.

    2009-01-01

    Thermal cycling experiments were conducted on a NiTi shape-memory alloy at different constant applied stresses below the yield strength of the martensite. The mechanical strain response manifested as strain hysteresis loops, whose range was proportional to the applied stress. In situ neutron diffraction experiments show that the strain hysteresis occurs as a result of the establishment of a stress-dependent crystallographic texture of the martensite during the first cool-down from austenite, and thereafter repeated during thermal cycling under the same load. This texture is found to depend on the stress during the thermal cycling experiments. A strain-pole map is derived and shown to explain the observed texture during thermal cycling. The strain-pole methodology is shown to work with similar martensitic transformations in other material systems.

  10. Energy landscape for martensitic phase transformation in shape memory NiTi

    International Nuclear Information System (INIS)

    Kibey, S.; Sehitoglu, H.; Johnson, D.D.

    2009-01-01

    First-principles calculations are presented for parent B2 phase and martensitic B19 and B19' phases in NiTi. The results indicate that both B19 and B19' are energetically more stable than the parent B2 phase. By means of ab initio density functional theory, the complete distortion-shuffle energy landscape associated with B2 → B19 transformation in NiTi is then determined. In addition to accounting for the Bain-type deformation through the Cauchy-Born rule, the study explicitly accounts for the shuffle displacements experienced by the internal ions in NiTi. The energy landscape allows the energy barrier associated with the B2 → B19 transformation pathway to be identified. The results indicate that a barrier of 0.48 mRyd atom -1 (relative to the B2 phase) must be overcome to transform the parent B2 NiTi to orthorhombic B19 martensite

  11. On the multiplication of dislocations during martensitic transformations in NiTi shape memory alloys

    Czech Academy of Sciences Publication Activity Database

    Simon, T.; Kröger, A.; Somsen, Ch.; Dlouhý, Antonín; Eggeler, G.

    2010-01-01

    Roč. 58, č. 5 (2010), s. 1850-1860 ISSN 1359-6454 R&D Projects: GA ČR GA106/09/1913 Institutional research plan: CEZ:AV0Z20410507 Keywords : NiTi * Martensitic transformations * Dislocation multiplication mechanism * Martensite variants * Dislocations Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.781, year: 2010

  12. Biocompatibility and corrosion behavior of the shape memory NiTi alloy in the physiological environments simulated with body fluids for medical applications

    International Nuclear Information System (INIS)

    Khalil-Allafi, Jafar; Amin-Ahmadi, Behnam; Zare, Mehrnoush

    2010-01-01

    Due to unique properties of NiTi shape memory alloys such as high corrosion resistance, biocompatibility, super elasticity and shape memory behavior, NiTi shape memory alloys are suitable materials for medical applications. Although TiO 2 passive layer in these alloys can prevent releasing of nickel to the environment, high nickel content and stability of passive layer in these alloys are very debatable subjects. In this study a NiTi shape memory alloy with nominal composition of 50.7 atom% Ni was investigated by corrosion tests. Electrochemical tests were performed in two physiological environments of Ringer solution and NaCl 0.9% solution. Results indicate that the breakdown potential of the NiTi alloy in NaCl 0.9% solution is higher than that in Ringer solution. The results of Scanning Electron Microscope (SEM) reveal that low pitting corrosion occurred in Ringer solution compared with NaCl solution at potentiostatic tests. The pH value of the solutions increases after the electrochemical tests. The existence of hydride products in the X-ray diffraction analysis confirms the decrease of the concentration of hydrogen ion in solutions. Topographical evaluations show that corrosion products are nearly same in all samples. The biocompatibility tests were performed by reaction of mouse fibroblast cells (L929). The growth and development of cells for different times were measured by numbering the cells or statistics investigations. The figures of cells for different times showed natural growth of cells. The different of the cell numbers between the test specimen and control specimen was negligible; therefore it may be concluded that the NiTi shape memory alloy is not toxic in the physiological environments simulated with body fluids.

  13. Damage-based life prediction model for uniaxial low-cycle stress fatigue of super-elastic NiTi shape memory alloy microtubes

    Science.gov (United States)

    Song, Di; Kang, Guozheng; Kan, Qianhua; Yu, Chao; Zhang, Chuanzeng

    2015-08-01

    Based on the experimental observations for the uniaxial low-cycle stress fatigue failure of super-elastic NiTi shape memory alloy microtubes (Song et al 2015 Smart Mater. Struct. 24 075004) and a new definition of damage variable corresponding to the variation of accumulated dissipation energy, a phenomenological damage model is proposed to describe the damage evolution of the NiTi microtubes during cyclic loading. Then, with a failure criterion of Dc = 1, the fatigue lives of the NiTi microtubes are predicted by the damage-based model, the predicted lives are in good agreement with the experimental ones, and all of the points are located within an error band of 1.5 times.

  14. Damage-based life prediction model for uniaxial low-cycle stress fatigue of super-elastic NiTi shape memory alloy microtubes

    International Nuclear Information System (INIS)

    Song, Di; Kang, Guozheng; Kan, Qianhua; Yu, Chao; Zhang, Chuanzeng

    2015-01-01

    Based on the experimental observations for the uniaxial low-cycle stress fatigue failure of super-elastic NiTi shape memory alloy microtubes (Song et al 2015 Smart Mater. Struct. 24 075004) and a new definition of damage variable corresponding to the variation of accumulated dissipation energy, a phenomenological damage model is proposed to describe the damage evolution of the NiTi microtubes during cyclic loading. Then, with a failure criterion of D c = 1, the fatigue lives of the NiTi microtubes are predicted by the damage-based model, the predicted lives are in good agreement with the experimental ones, and all of the points are located within an error band of 1.5 times. (paper)

  15. Negative and Zero Thermal Expansion NiTi Superelastic Shape Memory Alloy by Microstructure Engineering

    Science.gov (United States)

    Sun, Qingping; Yu, Chao; Kang, Guozheng

    2018-03-01

    We report recent progress in tailoring the thermal expansion (TE) of nanocrystalline (NC) NiTi by microstructure hierarchical design and control without composition change. Fabrication and characterization methods are outlined and preliminary results of both experiment and mechanism-based modeling are presented to understand and get insight into the unusual TE phenomena. The important roles of the intrinsic thermal expansion anisotropy of B19' lattice and the suppression of phase transition by the extrinsic fabricated microstructure (cold rolling and annealing, grain size, defects, textures and volume fractions of nanoscaled B2 and B19' lattices) in the overall macroscopic TE behaviors of the superelastic NC NiTi polycrystal SMAs are emphasized.

  16. Negative and Zero Thermal Expansion NiTi Superelastic Shape Memory Alloy by Microstructure Engineering

    Science.gov (United States)

    Sun, Qingping; Yu, Chao; Kang, Guozheng

    2018-02-01

    We report recent progress in tailoring the thermal expansion (TE) of nanocrystalline (NC) NiTi by microstructure hierarchical design and control without composition change. Fabrication and characterization methods are outlined and preliminary results of both experiment and mechanism-based modeling are presented to understand and get insight into the unusual TE phenomena. The important roles of the intrinsic thermal expansion anisotropy of B19' lattice and the suppression of phase transition by the extrinsic fabricated microstructure (cold rolling and annealing, grain size, defects, textures and volume fractions of nanoscaled B2 and B19' lattices) in the overall macroscopic TE behaviors of the superelastic NC NiTi polycrystal SMAs are emphasized.

  17. Work production using the two-way shape memory effect in NiTi and a Ni-rich NiTiHf high-temperature shape memory alloy

    International Nuclear Information System (INIS)

    Atli, K C; Karaman, I; Noebe, R D; Bigelow, G; Gaydosh, D

    2015-01-01

    The work output capacity of the two-way shape memory effect (TWSME) in a Ni 50.3 Ti 29.7 Hf 20 (at%) high-temperature shape memory alloy (HTSMA) was investigated and compared to that of binary Ni 49.9 Ti 50.1 (at%). TWSME was induced through a training procedure of 100 thermomechanical cycles under different tensile stresses. It was observed that TWSME in as-extruded and trained Ni 50.3 Ti 29.7 Hf 20 could produce 0.7% strain against a compressive stress of 100 MPa, corresponding to a maximum work output of 0.08 J g −1 , compared to a maximum value of 0.06 J g −1 for binary NiTi. A peak aging heat treatment of 3 h at 550 °C, which previously has been shown to result in near-perfect functional stability in Ni 50.3 Ti 29.7 Hf 20 during isobaric thermal cycling, did not improve the TWSME and actually resulted in a decrease in the magnitude and stability of the TWSME and its work output capacity. Nevertheless, the magnitude of TWSM behavior of Ni 50.3 Ti 29.7 Hf 20 , in the absence of an aging heat treatment, renders it an attractive candidate for high-temperature TWSM actuation. (paper)

  18. Effect of thermal cycling on the transformation temperature ranges of a Ni-Ti shape memory alloy

    International Nuclear Information System (INIS)

    Paula, A.S.; Canejo, J.P.H.G.; Martins, R.M.S.; Braz Fernandes, F.M.

    2003-01-01

    Shape memory alloys (SMA) represents a class of metallic materials that has the capability of recovering a previously defined initial shape when subject to an adequate thermomechanical treatment. The present work aims to study the influence of thermal cycles on the transition temperatures of a Ni-Ti alloy. In this system, small variations around the equiatomic composition give rise to significant transformation temperature variations ranging from 173 to 373 K. SMA usually presents the shape memory effect after an annealing treatment at ca. 973 K. The optimisation of the thermomechanical treatment will allow to 'tune' the material to different transformation temperature ranges from the same starting material, just by changing the processing conditions. Differential scanning calorimeter (DSC) and in situ high-temperature X-ray diffraction (XRD) have been used to identify the transformation temperatures and the phases that are present after different thermal cycles. The results concerning a series of thermal cycles with different heating and cooling rates (from 1.67x10 -2 to 1.25x10 -1 K/s) and different holding temperatures (from 473 to 1033 K) are presented

  19. Characterization of NiTi shape memory alloys using dual kriging interpolation

    International Nuclear Information System (INIS)

    Trochu, F.; Sacepe, N.; Volkov, O.; Turenne, S.

    1999-01-01

    A large number of industrial applications could benefit from the remarkable properties of shape memory alloys (SMA). The development of a general material law is the first important step before reliable design calculations of shape memory devices can be carried out. This paper presents a new phenomenological constitutive law based on dual kriging, which is a powerful mathematical tool used here as interpolation method to simulate the macroscopic mechanical behavior of shape memory alloys. From a set of experimental strain-temperature curves at constant loads, two deformation surfaces are constructed in the stress, strain and temperature space which describe the cooling and heating behaviors of the material for any stress. The response of a specimen subjected to complex thermomechanical loading can be calculated by dual kriging form a general 3-dimensional parametric solid constructed inside the hysteretic domain delimited by the main cooling and heating deformation surfaces. This approach presents the advantage of yielding immediately the explicit equation of any partial cycle inside the main hysteretic domain, thus yielding a general material law for shape memory alloys. Preliminary validation for a set of simple examples demonstrates the potential of this new model that includes in a single formulation superelasticity, rubber-like behavior and shape memory effect. (orig.)

  20. Improving the Performance of Electrically Activated NiTi Shape Memory Actuators by Pre-Aging

    Science.gov (United States)

    Rathmann1, Christian; Fleczok1, Benjamin; Otibar1, Dennis; Kuhlenkötter, Bernd

    2017-06-01

    Shape memory alloys possess an array of unique functional properties which are influenced by a complex interaction of different factors. Due to thermal sensitivity, slight changes in temperature may cause the properties to change significantly. This poses a huge challenge especially for the use of shape memory alloys as actuators. The displacement is the key performance indicator, which has to be of equal or better quality compared to conventional actuators. One problem of shape memory alloys is the change in functional fatigue in the first cycles, which makes it rather difficult to design the actuator. Therefore, the reduction of this shakedown effect is crucial. For this reason, this paper investigates the effect of electrical heat treatment as a method for pre-aging. This topic has so far been little investigated so that the investigations focus on identifying important factors and effects by using the design of experiments.

  1. Characterization of Ternary NiTiPd High-Temperature Shape-Memory Alloys under Load-Biased Thermal Cycling

    Science.gov (United States)

    Bigelow, Glen S.; Padula, Santo A.; Noebe, Ronald D.; Garg, Anita; Gaydosh, Darrell

    2010-01-01

    While NiTiPd alloys have been extensively studied for proposed use in high-temperature shape-memory applications, little is known about the shape-memory response of these materials under stress. Consequently, the isobaric thermal cyclic responses of five (Ni,Pd)49.5Ti50.5 alloys with constant stoichiometry and Pd contents ranging from 15 to 46 at. pct were investigated. From these tests, transformation temperatures, transformation strain (which is proportional to work output), and unrecovered strain per cycle (a measure of dimensional instability) were determined as a function of stress for each alloy. It was found that increasing the Pd content over this range resulted in a linear increase in transformation temperature, as expected. At a given stress level, work output decreased while the amount of unrecovered strain produced during each load-biased thermal cycle increased with increasing Pd content, during the initial thermal cycles. However, continued thermal cycling at constant stress resulted in a saturation of the work output and nearly eliminated further unrecovered strain under certain conditions, resulting in stable behavior amenable to many actuator applications.

  2. Characterization of a hot-rolled Cu--Al--Ni--Ti shape memory alloy

    International Nuclear Information System (INIS)

    Segui, C.; Pons, J.; Cesari, E.

    1999-01-01

    The changes in the martensitic transformation of a Cu-Al-Ni-Ti alloy hot-rolled at different temperatures have been studied in detail, covering different aspects such as ageing in the parent phase at temperatures ranging between 250 and 350 o C, stabilisation of the martensite and betatization of the previously hot-rolled specimens. Besides the evolution of transformation temperatures upon different thermal treatments, special attention has been paid to the changes in mechanical properties of the alloy, such as elastic modulus and internal friction. These results are analysed in relation to the microstructural changes as observed by transmission electron microscopy. (orig.)

  3. Vacuum Arc Melting Processes for Biomedical Ni-Ti Shape Memory Alloy

    OpenAIRE

    Tsai De-Chang; Chiang Chen-Hsueh

    2015-01-01

    This study primarily involved using a vacuum arc remelting (VAR) process to prepare a nitinol shape-memory alloy with distinct ratios of alloy components (nitinol: 54.5 wt% to 57 wt%). An advantage of using the VAR process is the adoption of a water-cooled copper crucible, which effectively prevents crucible pollution and impurity infiltration. Optimising the melting production process enables control of the alloy component and facilitates a uniformly mixed compound during subsequent processi...

  4. Phase transformation kinetics and microstructure of NiTi shape

    Indian Academy of Sciences (India)

    Phase transformation kinetics and microstructure of NiTi shape memory alloy: ... by 1.4687 J. In addition, entropy of the alloys decreases by 0.2335 J (g ∘ C) − 1 ... is an obvious difference in the grain sizes of the unpressured sample and the ...

  5. Influence of compressive load conditions and thickness on the two-way shape memory behavior in tube-shaped NiTi alloy

    International Nuclear Information System (INIS)

    Yoo, Young Ik; Shin, Dong Kil; Lee, Jung Ju; Lee, Chang Ho

    2012-01-01

    The two-way shape memory behavior of Ni 55 Ti 45 was investigated to develop a tube-shaped NiTi actuator which could generate a large amount of force. The two-way shape memory effect (TWSME) was induced by thermal cycling under various amounts of constant compressive stress. Six specimens with the same outer diameter and different thickness were used to apply the TWSME to an actuator. A fast saturation tendency of the recovery strain was shown through training at each level of constant stress, after which the two-way shape memory strain was quantitatively measured during thermal cycling for each level of applied stress. From the results, the maximum two-way strain value was obtained after training at a constant level of stress and then decreased thereafter. In addition, the two-way strain was found to depend on the thickness of the tube-shaped specimen. All specimens could be divided into two groups depending on the rate of increase in the two-way strain. After two-way strain was obtained, the two-way recovery stress was measured to verify the performance of the sample as an actuator. The results showed that the two-way recovery stress behavior was similar to the two-way strain; if the optimal thickness of the specimen and the stress applied for training are used for the development of the TWSME, tube-shaped NiTi using the TWSME can replace one-way shape memory alloys. (paper)

  6. Experimental Studies on Dynamic Vibration Absorber using Shape Memory Alloy (NiTi) Springs

    International Nuclear Information System (INIS)

    Kumar, V. Raj; Kumar, M. B. Bharathi Raj; Kumar, M. Senthil

    2011-01-01

    Shape memory alloy (SMA) springs have been used as actuators in many applications although their use in the vibration control area is very recent. Since shape memory alloys differ from conventional alloy materials in many ways, the traditional design approach for springs is not completely suitable for designing SMA springs. Some vibration control concepts utilizing unique characteristics of SMA's will be presented in this paper.A dynamic vibration absorber (DVA) using shape memory alloy (SMA) actuator is developed for attenuation of vibration in a cantilever beam. The design procedure of the DVA is presented. The system consists of a cantilever beam which is considered to generate the real-time vibration using shaker. A SMA spring is used with a mass attached to its end. The stiffness of the SMA spring is dynamically varied in such a way to attenuate the vibration. Both simulation and experimentation are carried out using PID controller. The experiments were carried out by interfacing the experimental setup with a computer using LabVIEW software, Data acquisition and control are implemented using a PCI data acquisition card. Standard PID controllers have been used to control the vibration of the beam. Experimental results are used to demonstrate the effectiveness of the controllers designed and the usefulness of the proposed test platform by exciting the structure at resonance. In experimental setup, an accelerometer is used to measure the vibration which is fed to computer and correspondingly the SMA spring is actuated to change its stiffness to control the vibration. The results obtained illustrate that the developed DVA using SMA actuator is very effective in reducing structural response and have great potential to be an active vibration control medium.

  7. Vacuum Arc Melting Processes for Biomedical Ni-Ti Shape Memory Alloy

    Directory of Open Access Journals (Sweden)

    Tsai De-Chang

    2015-01-01

    Full Text Available This study primarily involved using a vacuum arc remelting (VAR process to prepare a nitinol shape-memory alloy with distinct ratios of alloy components (nitinol: 54.5 wt% to 57 wt%. An advantage of using the VAR process is the adoption of a water-cooled copper crucible, which effectively prevents crucible pollution and impurity infiltration. Optimising the melting production process enables control of the alloy component and facilitates a uniformly mixed compound during subsequent processing. This study involved purifying nickel and titanium and examining the characteristics of nitinol alloy after alloy melt, including its microstructure, mechanical properties, phase transition temperature, and chemical components.

  8. Characteristics and in vitro biological assessment of (Ti, O, N)/Ti composite coating formed on NiTi shape memory alloy

    International Nuclear Information System (INIS)

    Sun Tao; Wang Langping; Wang Min; Tong, Ho-Wang; Lu, William W.

    2011-01-01

    In this investigation, plasma immersion ion implantation and deposition (PIIID) was used to fabricate a (Ti, O, N)/Ti coating on NiTi shape memory alloy (SMA) to improve its long-term biocompatibility and wear resistance. The surface morphology, composition and roughness of uncoated and coated NiTi SMA samples were examined. Energy dispersive X-ray elemental mapping of cross-sections of (Ti, O, N)/Ti coated NiTi SMA revealed that Ni was depleted from the surface of coated samples. No Ni was detected by X-ray photoelectron spectroscopy on the surface of coated samples. Furthermore, three-point bending tests showed that the composite coating could undergo large deformation without cracking or delamination. After 1 day cell culture, SaOS-2 cells on coated samples spread better than those on uncoated NiTi SMA samples. The proliferation of SaOS-2 cells on coated samples was significantly higher at day 3 and day 7 of cell culture.

  9. Multiscale Modeling of Polycrystalline NiTi Shape Memory Alloy under Various Plastic Deformation Conditions by Coupling Microstructure Evolution and Macroscopic Mechanical Response.

    Science.gov (United States)

    Hu, Li; Jiang, Shuyong; Zhou, Tao; Tu, Jian; Shi, Laixin; Chen, Qiang; Yang, Mingbo

    2017-10-13

    Numerical modeling of microstructure evolution in various regions during uniaxial compression and canning compression of NiTi shape memory alloy (SMA) are studied through combined macroscopic and microscopic finite element simulation in order to investigate plastic deformation of NiTi SMA at 400 °C. In this approach, the macroscale material behavior is modeled with a relatively coarse finite element mesh, and then the corresponding deformation history in some selected regions in this mesh is extracted by the sub-model technique of finite element code ABAQUS and subsequently used as boundary conditions for the microscale simulation by means of crystal plasticity finite element method (CPFEM). Simulation results show that NiTi SMA exhibits an inhomogeneous plastic deformation at the microscale. Moreover, regions that suffered canning compression sustain more homogeneous plastic deformation by comparison with the corresponding regions subjected to uniaxial compression. The mitigation of inhomogeneous plastic deformation contributes to reducing the statistically stored dislocation (SSD) density in polycrystalline aggregation and also to reducing the difference of stress level in various regions of deformed NiTi SMA sample, and therefore sustaining large plastic deformation in the canning compression process.

  10. Effect of surface modification by nitrogen ion implantation on the electrochemical and cellular behaviors of super-elastic NiTi shape memory alloy.

    Science.gov (United States)

    Maleki-Ghaleh, H; Khalil-Allafi, J; Sadeghpour-Motlagh, M; Shakeri, M S; Masoudfar, S; Farrokhi, A; Beygi Khosrowshahi, Y; Nadernezhad, A; Siadati, M H; Javidi, M; Shakiba, M; Aghaie, E

    2014-12-01

    The aim of this investigation was to enhance the biological behavior of NiTi shape memory alloy while preserving its super-elastic behavior in order to facilitate its compatibility for application in human body. The surfaces of NiTi samples were bombarded by three different nitrogen doses. Small-angle X-ray diffraction was employed for evaluating the generated phases on the bombarded surfaces. The electrochemical behaviors of the bare and surface-modified NiTi samples were studied in simulated body fluid (SBF) using electrochemical impedance and potentio-dynamic polarization tests. Ni ion release during a 2-month period of service in the SBF environment was evaluated using atomic absorption spectrometry. The cellular behavior of nitrogen-modified samples was studied using fibroblast cells. Furthermore, the effect of surface modification on super-elasticity was investigated by tensile test. The results showed the improvement of both corrosion and biological behaviors of the modified NiTi samples. However, no significant change in the super-elasticity was observed. Samples modified at 1.4E18 ion cm(-2) showed the highest corrosion resistance and the lowest Ni ion release.

  11. Multiscale Modeling of Polycrystalline NiTi Shape Memory Alloy under Various Plastic Deformation Conditions by Coupling Microstructure Evolution and Macroscopic Mechanical Response

    Directory of Open Access Journals (Sweden)

    Li Hu

    2017-10-01

    Full Text Available Numerical modeling of microstructure evolution in various regions during uniaxial compression and canning compression of NiTi shape memory alloy (SMA are studied through combined macroscopic and microscopic finite element simulation in order to investigate plastic deformation of NiTi SMA at 400 °C. In this approach, the macroscale material behavior is modeled with a relatively coarse finite element mesh, and then the corresponding deformation history in some selected regions in this mesh is extracted by the sub-model technique of finite element code ABAQUS and subsequently used as boundary conditions for the microscale simulation by means of crystal plasticity finite element method (CPFEM. Simulation results show that NiTi SMA exhibits an inhomogeneous plastic deformation at the microscale. Moreover, regions that suffered canning compression sustain more homogeneous plastic deformation by comparison with the corresponding regions subjected to uniaxial compression. The mitigation of inhomogeneous plastic deformation contributes to reducing the statistically stored dislocation (SSD density in polycrystalline aggregation and also to reducing the difference of stress level in various regions of deformed NiTi SMA sample, and therefore sustaining large plastic deformation in the canning compression process.

  12. An informatics approach to transformation temperatures of NiTi-based shape memory alloys

    International Nuclear Information System (INIS)

    Xue, Dezhen; Xue, Deqing; Yuan, Ruihao; Zhou, Yumei; Balachandran, Prasanna V.; Ding, Xiangdong; Sun, Jun; Lookman, Turab

    2017-01-01

    The martensitic transformation serves as the basis for applications of shape memory alloys (SMAs). The ability to make rapid and accurate predictions of the transformation temperature of SMAs is therefore of much practical importance. In this study, we demonstrate that a statistical learning approach using three features or material descriptors related to the chemical bonding and atomic radii of the elements in the alloys, provides a means to predict transformation temperatures. Together with an adaptive design framework, we show that iteratively learning and improving the statistical model can accelerate the search for SMAs with targeted transformation temperatures. The possible mechanisms underlying the dependence of the transformation temperature on these features is discussed based on a Landau-type phenomenological model.

  13. A new mechanical characterization method for thin film microactuators and its application to NiTiCi shape memory alloy

    International Nuclear Information System (INIS)

    Seward, K P

    1999-01-01

    In an effort to develop a more full characterization tool of shape memory alloys, a new technique is presented for the mechanical characterization of microactuators and applied to SMA thin films. A test instrument was designed to utilize a spring-loaded transducer in measuring displacements with resolution of 1.5 pm and forces with resolution of 0.2 mN. Employing an out-of-plane loading method for freestanding SMA thin films, strain resolution of 30(mu)(epsilon) and stress resolution of 2.5 MPa were achieved. This new testing method is presented against previous SMA characterization methods for purposes of comparison. Four mm long, 2(micro)m thick NiTiCu ligaments suspended across open windows were bulk micromachined for use in the out-of-plane stress and strain measurements. The fabrication process used to micromachine the ligaments is presented step-by-step, alongside methods of fabrication that failed to produce testable ligaments. Static analysis showed that 63% of the applied strain was recovered while ligaments were subjected to tensile stresses of 870 MPa. In terms of recoverable stress and recoverable strain, the ligaments achieved maximum recovery of 700 MPa and 3.0% strain. No permanent deformations were seen in any ligament during deflection measurements. Maximum actuation forces and displacements produced by the 4 mm ligaments situated on 1 cm square test chips were 56 mN and 300(micro)m, respectively. Fatigue analysis of the ligaments showed degradation in recoverable strain from 0.33% to 0.24% with 200,000 cycles, corresponding to deflections of 90(micro)m and forces of 25 mN. Cycling also produced a wavering shape memory effect late in ligament life, leading to broad inconsistencies of as much as 35% deviation from average. Unexpected phenomena like stress-induced martensitic twinning that leads to less recoverable stress and the shape memory behavior of long life devices are addressed. Finally, a model for design of microactuators using shape memory

  14. NiTi shape-memory alloy oxidized in low-temperature plasma with carbon coating: Characteristic and a potential for cardiovascular applications

    Science.gov (United States)

    Witkowska, Justyna; Sowińska, Agnieszka; Czarnowska, Elżbieta; Płociński, Tomasz; Borowski, Tomasz; Wierzchoń, Tadeusz

    2017-11-01

    Surface layers currently produced on NiTi alloys do not meet all the requirements for materials intended for use in cardiology. Plasma surface treatments of titanium and its alloys under glow discharge conditions make it possible to produce surface layers, such as TiN or TiO2, which increases corrosion resistance and biocompatibility. The production of layers on NiTi alloys with the same properties, and maintaining their shape memory and superelasticity features, requires the use of low-temperature processes. At the same time, since it is known that the carbon-based layers could prevent excessive adhesion and aggregation of platelets, we examined the composite a-CNH + TiO2 type surface layer produced by means of a hybrid method combining oxidation in low-temperature plasma and Radio Frequency Chemical Vapor Deposition (RFCVD) processes. Investigations have shown that this composite layer increases the corrosion resistance of the material, and both the low degree of roughness and the chemical composition of the surface produced lead to decreased platelet adhesion and aggregation and proper endothelialization, which could extend the range of applications of NiTi shape memory alloys.

  15. Challenges and Progress in the Development of High-Temperature Shape Memory Alloys Based on NiTiX Compositions for High-Force Actuator Applications

    Science.gov (United States)

    Padula, Santo, II; Bigelow, Glen; Noebe, Ronald; Gaydosh, Darrell; Garg, Anita

    2006-01-01

    Interest in high-temperature shape memory alloys (HTSMA) has been growing in the aerospace, automotive, process control, and energy industries. However, actual materials development has seriously lagged component design, with current commercial NiTi alloys severely limited in their temperature capability. Additions of Pd, Pt, Au, Hf, and Zr at levels greater than 10 at.% have been shown to increase the transformation temperature of NiTi alloys, but with few exceptions, the shape memory behavior (strain recovery) of these NiTiX systems has been determined only under stress free conditions. Given the limited amount of basic mechanical test data and general lack of information regarding the work attributes of these materials, a program to investigate the mechanical behavior of potential HTSMAs, with transformation temperatures between 100 and 500 C, was initiated. This paper summarizes the results of studies, focusing on both the practical temperature limitations for ternary TiNiPd and TiNiPt systems based on the work output of these alloys and the ability of these alloys to undergo repeated thermal cycling under load without significant permanent deformation or "walking". These issues are ultimately controlled by the detwinning stress of the martensite and resistance to dislocation slip of the individual martensite and austenite phases. Finally, general rules that govern the development of useful, high work output, next-generation HTSMA materials, based on the lessons learned in this work, will be provided

  16. The effects of vacuum induction melting and electron beam melting techniques on the purity of NiTi shape memory alloys

    Energy Technology Data Exchange (ETDEWEB)

    Otubo, J. [Instituto Tecnologico de Aeronautica (ITA), 12228-900 S.J. Campos, SP (Brazil) and DEMA-FEM-UNICAMP, 13083-000 Campinas, SP (Brazil)]. E-mail: jotubo@ita.br; Rigo, O.D. [DEMA-FEM-UNICAMP, 13083-000 Campinas, SP (Brazil); Neto, C. Moura [Instituto Tecnologico de Aeronautica (ITA), 12228-900 S.J. Campos, SP (Brazil); Mei, P.R. [DEMA-FEM-UNICAMP, 13083-000 Campinas, SP (Brazil)

    2006-11-25

    The usual process to produce NiTi shape memory alloys is by vacuum induction melting (VIM) using graphite crucible that contaminates the bath with carbon. The contamination by oxygen comes from residual oxygen inside the melting chamber. A new alternative process to produce NiTi alloys is by electron beam melting (EBM) using water-cooled copper crucible that eliminates the carbon contamination and the oxygen contamination would be minimized due to operation in high vacuum. This work compares the two processes and shows that the carbon contamination is four to ten times lower for EBM compared to VIM products and that the final oxygen content is much more dependent on the starting raw materials. The purity of the final product should be very important mainly in terms of biomedical applications and the contaminations by carbon and oxygen affect the direct and reverse martensitic transformation temperatures.

  17. Experimental observations on uniaxial whole-life transformation ratchetting and low-cycle stress fatigue of super-elastic NiTi shape memory alloy micro-tubes

    Science.gov (United States)

    Song, Di; Kang, Guozheng; Kan, Qianhua; Yu, Chao; Zhang, Chuanzeng

    2015-07-01

    In this work, the low-cycle fatigue failure of super-elastic NiTi shape memory alloy micro-tubes with a wall thickness of 150 μm is investigated by uniaxial stress-controlled cyclic tests at human body temperature 310 K. The effects of mean stress, peak stress, and stress amplitude on the uniaxial whole-life transformation ratchetting and fatigue failure of the NiTi alloy are observed. It is concluded that the fatigue life depends significantly on the stress levels, and the extent of martensite transformation and its reverse play an important role in determining the fatigue life. High peak stress or complete martensite transformation shortens the fatigue life.

  18. Experimental observations on uniaxial whole-life transformation ratchetting and low-cycle stress fatigue of super-elastic NiTi shape memory alloy micro-tubes

    International Nuclear Information System (INIS)

    Song, Di; Kang, Guozheng; Kan, Qianhua; Yu, Chao; Zhang, Chuanzeng

    2015-01-01

    In this work, the low-cycle fatigue failure of super-elastic NiTi shape memory alloy micro-tubes with a wall thickness of 150 μm is investigated by uniaxial stress-controlled cyclic tests at human body temperature 310 K. The effects of mean stress, peak stress, and stress amplitude on the uniaxial whole-life transformation ratchetting and fatigue failure of the NiTi alloy are observed. It is concluded that the fatigue life depends significantly on the stress levels, and the extent of martensite transformation and its reverse play an important role in determining the fatigue life. High peak stress or complete martensite transformation shortens the fatigue life. (paper)

  19. Annealing behavior and shape memory effect in NiTi alloy processed by equal-channel angular pressing at room temperature

    International Nuclear Information System (INIS)

    Shahmir, Hamed; Nili-Ahmadabadi, Mahmoud; Wang, Chuan Ting; Jung, Jai Myun; Kim, Hyoung Seop; Langdon, Terence G.

    2015-01-01

    A martensitic NiTi shape memory alloy was processed successfully by equal-channel angular pressing (ECAP) for one pass at room temperature using a core–sheath billet design. The annealing behavior and shape memory effect of the ECAP specimens were studied followed by post-deformation annealing (PDA) at 673 K for various times. The recrystallization and structural evolution during annealing were investigated by differential scanning calorimetry, dilatometry, X-ray diffraction, transmission electron microscopy and microhardness measurements. The results indicate that the shape memory effect improves by PDA after ECAP processing. Annealing for 10 min gives a good shape memory effect which leads to a maximum in recoverable strain of 6.9 pct upon heating where this is more than a 25 pct improvement compared with the initial state

  20. H-Phase Precipitation and Martensitic Transformation in Ni-rich Ni-Ti-Hf and Ni-Ti-Zr High-Temperature Shape Memory Alloys

    Science.gov (United States)

    Evirgen, A.; Pons, J.; Karaman, I.; Santamarta, R.; Noebe, R. D.

    2018-03-01

    The distributions of H-phase precipitates in Ni50.3Ti29.7Hf20 and Ni50.3Ti29.7Zr20 alloys formed by aging treatments at 500 and 550 °C or slow furnace cooling and their effects on the thermal martensitic transformation have been investigated by TEM and calorimetry. The comparative study clearly reveals faster precipitate-coarsening kinetics in the NiTiZr alloy than in NiTiHf. For precipitates of a similar size of 10-20 nm in both alloys, the martensite plates in Ni50.3Ti29.7Zr20 have larger widths and span a higher number of precipitates compared with the Ni50.3Ti29.7Hf20 alloy. However, for large H-phase particles with hundreds of nm in length, no significant differences in the martensitic microstructures of both alloy systems have been observed. The martensitic transformation temperatures of Ni50.3Ti29.7Hf20 are 80-90 °C higher than those of Ni50.3Ti29.7Zr20 in the precipitate-free state and in the presence of large particles of hundreds on nm in length, but this difference is reduced to only 10-20 °C in samples with small H-phase precipitates. The changes in the transformation temperatures are consistent with the differences in the precipitate distributions between the two alloy systems observed by TEM.

  1. The effect of annealing on the mechanical properties and microstructural evolution of Ti-rich NiTi shape memory alloy

    Energy Technology Data Exchange (ETDEWEB)

    Tadayyon, Ghazal [Department of Metallurgical and Materials Engineering Faculty of Engineering, Ferdowsi University of Mashhad (Iran, Islamic Republic of); Centre for Research in Medical Devices (CURAM), National University of Ireland, Galway (Ireland); Mazinani, Mohammad, E-mail: mazinani@um.ac.ir [Department of Metallurgical and Materials Engineering Faculty of Engineering, Ferdowsi University of Mashhad (Iran, Islamic Republic of); Guo, Yina [Materials and Surface Science Institute, University of Limerick, Limerick (Ireland); Zebarjad, Seyed Mojtaba [Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz (Iran, Islamic Republic of); Tofail, Syed A.M. [Materials and Surface Science Institute, University of Limerick, Limerick (Ireland); Biggs, Manus J. [Centre for Research in Medical Devices (CURAM), National University of Ireland, Galway (Ireland)

    2016-04-26

    An investigation was carried out into the influence of the annealing temperatures on the thermo-mechanical behavior of Ti-rich NiTi alloy with regard to transformation temperatures, mechanical properties at room temperature and microstructure evolution under deformation. It was found that annealing above the recrystallization temperature (600 °C) modulated the mechanical behavior of the alloy significantly. Based on tensile and DSC analysis, it was observed that by increasing the annealing temperature, the shape memory behavior of the alloys improved. Scanning and transmission electron microscopy were used to investigate the fracture surfaces and microstructural evolution of the NiTi samples after failure. Fractography revealed the brittle fracture area produced through the propagation of cleavage cracks; however, ductile fracture via nucleation growth and coalescence of micro-dimples in the martensitic phase at room temperature were also observed. During plastic deformation, the NiTi alloy was also observed to undergo a detwinning process, dislocation slip and the formation of submicrocrystalline grains, nanocrystallization and amorphous bands.

  2. Characteristics of the stress-induced formation of R-phase in ultrafine-grained NiTi shape memory wire

    International Nuclear Information System (INIS)

    Olbricht, J.; Yawny, A.; Pelegrina, J.L.; Eggeler, G.; Yardley, V.A.

    2013-01-01

    Highlights: •We investigated the stress-induced formation of R-phase in NiTi shape memory wires. •The R-phase related strains were isolated from the overall stress-strain-behavior. •The stress–strain characteristics of R-phase suggest a homogeneous transformation. •Thermography confirms the homogeneous R-phase formation in ultrafine-grained NiTi. -- Abstract: The transformation between the cubic B2 and monoclinic B19′ phases in ultrafine-grained pseudoelastic NiTi can occur as a two-step process involving the intermediate rhombohedral R-phase. Experimental work using differential scanning calorimetry, electrical resistance measurements and transmission electron microscopy has demonstrated the formation of this intermediate phase during thermal cycling and during mechanical loading. In the present paper, complementary mechanical and thermographic results are presented which allow to further assess the character of the stress-induced R-phase formation. The transformation from B2 to R-phase is demonstrated to occur homogeneously within the gauge length rather than via advancing Lüders-type transition regions as it is the case in the localized transformation from B2 or R-phase to B19′

  3. Evolution of macroscopic elastic moduli of martensitic polycrystalline NiTi and NiTiCu shape memory alloys with pseudoplastic straining

    Czech Academy of Sciences Publication Activity Database

    Thomasová, M.; Seiner, Hanuš; Sedlák, Petr; Frost, Miroslav; Ševčík, Martin; Szurman, I.; Kocich, R.; Drahokoupil, Jan; Šittner, Petr; Landa, Michal

    2017-01-01

    Roč. 123, January (2017), s. 146-156 ISSN 1359-6454 R&D Projects: GA ČR(CZ) GP14-28306P; GA ČR GA14-15264S Institutional support: RVO:61388998 ; RVO:68378271 Keywords : shape memory alloys * polycrystals * elastic behavior Subject RIV: BM - Solid Matter Physics ; Magnetism; BM - Solid Matter Physics ; Magnetism (FZU-D) OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.); Condensed matter physics (including formerly solid state physics, supercond.) (FZU-D) Impact factor: 5.301, year: 2016

  4. Assessing the morphology of selective laser melted NiTi-scaffolds for a three-dimensional quantification of the one-way shape memory effect

    Science.gov (United States)

    Bormann, Therese; de Wild, Michael; Beckmann, Felix; Müller, Bert

    2013-04-01

    NiTi is promising for the use as bone scaffold, because the pseudoelasticity or the one- and two-way shape memory effect in the physiological window can mechanically stimulate the adherent cells. Such stimuli can enhance osseointegration and might reduce stress shielding associated with load bearing implants. The present study is based on the additive manufacturing technique of selective laser melting (SLM) to fabricate three-dimensional NiTi scaffolds. We demonstrate that the morphology of the scaffolds can be quantified using synchrotron radiation-based micro computed tomography (SRμCT) and sophisticated registration software. Comparing the CAD file with the SLM scaffolds, quality factors are derived. With respect to the CAD file, the overlap corresponds to (92.5 +/- 0.6) %. (7.4 +/- 0.42) % of material was missing and (48.9 +/- 2.3) % of excess material found. This means that the actual scaffold is less porous than expected, a fact that has to be considered for the scaffold design. In order to quantify the shape memory effect during the shape recovery process, we acquired radiographs rotating an initially deformed scaffold in angular steps of 0.2 degree during controlled heating. The continuously acquired radiographs were combined to tomography data, showing that the quality factors evolved with temperature as the scaffold height, measured by conventional thermo-mechanical analysis. Furthermore, the data comprise the presence of compressive and tensile local strains in the three-dimensional scaffolds to be compared with the physiological situation.

  5. Phase volume fractions and strain measurements in an ultrafine-grained NiTi shape-memory alloy during tensile loading

    International Nuclear Information System (INIS)

    Young, M.L.; Wagner, M.F.-X.; Frenzel, J.; Schmahl, W.W.; Eggeler, G.

    2010-01-01

    An ultrafine-grained pseudoelastic NiTi shape-memory alloy wire with 50.9 at.% Ni was examined using synchrotron X-ray diffraction during in situ uniaxial tensile loading (up to 1 GPa) and unloading. Both macroscopic stress-strain measurements and volume-averaged lattice strains are reported and discussed. The loading behavior is described in terms of elasto-plastic deformation of austenite, emergence of R phase, stress-induced martensitic transformation, and elasto-plastic deformation, grain reorientation and detwinning of martensite. The unloading behavior is described in terms of stress relaxation and reverse plasticity of martensite, reverse transformation of martensite to austenite due to stress relaxation, and stress relaxation of austenite. Microscopically, lattice strains in various crystallographic directions in the austenitic B2, martensitic R, and martensitic B19' phases are examined during loading and unloading. It is shown that the phase transformation occurs in a localized manner along the gage length at the plateau stress. Phase volume fractions and lattice strains in various crystallographic reflections in the austenite and martensite phases are examined over two transition regions between austenite and martensite, which have a width on the order of the wire diameter. Anisotropic effects observed in various crystallographic reflections of the austenitic phase are also discussed. The results contribute to a better understanding of the tensile loading behavior, both macroscopically and microscopically, of NiTi shape-memory alloys.

  6. An overview of NiTi shape memory alloy: Corrosion resistance and antibacterial inhibition for dental application

    Energy Technology Data Exchange (ETDEWEB)

    Fadlallah, Sahar A., E-mail: sahar.fadlallah@yahoo.com [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia); Chemistry Department, Faculty of Science, Cairo University, Cairo (Egypt); El-Bagoury, Nader [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia); Casting Technology Lab., Manufacturing Technology Dept., CMRDI, P.O. Box 87, Helwan, Cairo (Egypt); Gad El-Rab, Sanaa M.F. [Biotechnology Department, Faculty of Science, Taif University, Taif (Saudi Arabia); Botany Department, Faculty of Science, Asuit University, Asuit (Egypt); Ahmed, Rasha A. [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia); Forensic Chemistry Laboratories, Medico Legal Department, Ministry of Justice, Cairo (Egypt); El-Ousamii, Ghaida [Materials and Corrosion Lab. (MCL), Faculty of Science, Taif University, Taif (Saudi Arabia)

    2014-01-15

    Highlights: • Evaluate the corrosion resistance of NiTi alloy by using electrochemical techniques. • Estimate the Antibacterial inhibition rate of NiTi alloy. • Assessment the mechanical properties of NiTi from the hardness measurements. • Comparsion the microstructures of cast NiTi with Ti, this indicate the role of Ni to change the behavior of alloy in oral environment. • Advise drinking green tea in small quantities in small quantities in the event of present NiTi alloy in the oral cavity. • Recommendation to use NiTi for dental application. -- Abstract: Nowadays, Nickel–titanium nearly equiatomic is considered as one of the best biomaterials. The aim of the present work deals with the evolution of the electrochemical behavior of NiTi in simulated oral environment. The hardness, microstructures corrosion resistance and antibacterial performance of NiTi alloy were compared with pure titanium. The hardness of NiTi is twice the hardness of pure titanium. Electrochemical techniques were used to detect the corrosion resistance of both biomaterials in Hank’s solution containing (−)-epigallocatechin gallate (EGCG) which used to simulate the oral environment. In the physiological solution selected for the present study, the impedance spectroscopy (EIS) results showed that EGCG sharply increase the corrosion resistance of NiTi from 129 kΩ cm{sup 2} to 1.10 T Ω cm{sup 2} while slowly increase the corrosion resistance of pure titanium from 9.4 kΩ cm{sup 2} to 11.3 kΩ cm{sup 2} during the duration time of immersion at 37 °C. The plate-counting method was used to evaluate the antibacterial performance against Staphylococcus aureus (ATCC 6538). Among the two specimens of biomaterials studied, the antibacterial performance results revealed that the NiTi alloy is better than the pure titanium. The morphology and chemical structure of NiTi and Ti samples were systematically investigated by scanning electron microscope (SEM) and energy dispersive X

  7. An overview of NiTi shape memory alloy: Corrosion resistance and antibacterial inhibition for dental application

    International Nuclear Information System (INIS)

    Fadlallah, Sahar A.; El-Bagoury, Nader; Gad El-Rab, Sanaa M.F.; Ahmed, Rasha A.; El-Ousamii, Ghaida

    2014-01-01

    Highlights: • Evaluate the corrosion resistance of NiTi alloy by using electrochemical techniques. • Estimate the Antibacterial inhibition rate of NiTi alloy. • Assessment the mechanical properties of NiTi from the hardness measurements. • Comparsion the microstructures of cast NiTi with Ti, this indicate the role of Ni to change the behavior of alloy in oral environment. • Advise drinking green tea in small quantities in small quantities in the event of present NiTi alloy in the oral cavity. • Recommendation to use NiTi for dental application. -- Abstract: Nowadays, Nickel–titanium nearly equiatomic is considered as one of the best biomaterials. The aim of the present work deals with the evolution of the electrochemical behavior of NiTi in simulated oral environment. The hardness, microstructures corrosion resistance and antibacterial performance of NiTi alloy were compared with pure titanium. The hardness of NiTi is twice the hardness of pure titanium. Electrochemical techniques were used to detect the corrosion resistance of both biomaterials in Hank’s solution containing (−)-epigallocatechin gallate (EGCG) which used to simulate the oral environment. In the physiological solution selected for the present study, the impedance spectroscopy (EIS) results showed that EGCG sharply increase the corrosion resistance of NiTi from 129 kΩ cm 2 to 1.10 T Ω cm 2 while slowly increase the corrosion resistance of pure titanium from 9.4 kΩ cm 2 to 11.3 kΩ cm 2 during the duration time of immersion at 37 °C. The plate-counting method was used to evaluate the antibacterial performance against Staphylococcus aureus (ATCC 6538). Among the two specimens of biomaterials studied, the antibacterial performance results revealed that the NiTi alloy is better than the pure titanium. The morphology and chemical structure of NiTi and Ti samples were systematically investigated by scanning electron microscope (SEM) and energy dispersive X-ray analysis (EDX). The

  8. Comparative studies on ultrasonic, friction, laser and resistance pressure welding of NiTi shape memory alloys with high-alloy steels. Final report; Vergleichende Untersuchungen zum Ultraschall-, Reib-, Laserstrahl- und Widerstandspressschweissen von NiTi-Shape-Memory-Metall mit hochlegierten Staehlen. Abschlussbericht

    Energy Technology Data Exchange (ETDEWEB)

    Zuckschwerdt, K.

    2000-04-01

    The suitability of different welding techniques for welding of NiTi shape memory alloys with high-alloy steel (C12CrNi17-7, X5CrNiNb19-9, X20Cr13) was investigated. The quality of the welds was analyzed using mechanical-technological, fractographic, metallographic and electron microscopy analysis. [German] Ziel dieses Forschungsvorhabens ist es, die Eignung der einzelnen Schweissverfahren fuer das Fuegen von NiTi-Formgedaechtnislegierungen mit hochlegiertem Stahl (X12CrNi17-7, X5CrNiNb19-9, X20Cr13) darzustellen und zu beurteilen. Die Qualitaet der Fuegeverbindungen wird mit Hilfe mechanisch-technologischer, fraktographischer, metallographischer und elektronenmikroskopischer Untersuchungen bewertet.

  9. Observation on the transformation domains of super-elastic NiTi shape memory alloy and their evolutions during cyclic loading

    International Nuclear Information System (INIS)

    Xie, Xi; Kan, Qianhua; Kang, Guozheng; Li, Jian; Qiu, Bo; Yu, Chao

    2016-01-01

    The strain field of a super-elastic NiTi shape memory alloy (SMA) and its variation during uniaxial cyclic tension-unloading were observed by a non-contact digital image correlation method, and then the transformation domains and their evolutions were indirectly investigated and discussed. It is seen that the super-elastic NiTi (SMA) exhibits a remarkable localized deformation and the transformation domains evolve periodically with the repeated cyclic tension-unloading within the first several cycles. However, the evolutions of transformation domains at the stage of stable cyclic transformation depend on applied peak stress: when the peak stress is low, no obvious transformation band is observed and the strain field is nearly uniform; when the peak stress is large enough, obvious transformation bands occur due to the residual martensite caused by the prevention of enriched dislocations to the reverse transformation from induced martensite to austenite. Temperature variations measured by an infrared thermal imaging method further verifies the formation and evolution of transformation domains. (paper)

  10. Observation on the transformation domains of super-elastic NiTi shape memory alloy and their evolutions during cyclic loading

    Science.gov (United States)

    Xie, Xi; Kan, Qianhua; Kang, Guozheng; Li, Jian; Qiu, Bo; Yu, Chao

    2016-04-01

    The strain field of a super-elastic NiTi shape memory alloy (SMA) and its variation during uniaxial cyclic tension-unloading were observed by a non-contact digital image correlation method, and then the transformation domains and their evolutions were indirectly investigated and discussed. It is seen that the super-elastic NiTi (SMA) exhibits a remarkable localized deformation and the transformation domains evolve periodically with the repeated cyclic tension-unloading within the first several cycles. However, the evolutions of transformation domains at the stage of stable cyclic transformation depend on applied peak stress: when the peak stress is low, no obvious transformation band is observed and the strain field is nearly uniform; when the peak stress is large enough, obvious transformation bands occur due to the residual martensite caused by the prevention of enriched dislocations to the reverse transformation from induced martensite to austenite. Temperature variations measured by an infrared thermal imaging method further verifies the formation and evolution of transformation domains.

  11. Feasibility of Shape-Memory Ni/Ti Alloy Wire Containing Tube Elevators for Transcrestal Detaching Maxillary Sinus Mucosa: Ex Vivo Study

    Directory of Open Access Journals (Sweden)

    Yanfeng Li

    2016-12-01

    Full Text Available Background: Osteotome sinus floor elevation is a less invasive approach to augment an insufficient alveolar bone at the posterior maxilla for dental implantation. However, this approach has some limitations due to the lack of sinus lift tools available for clinical use and the small transcrestal access to the maxillary sinus floor. We recently invented shape-memory Ni/Ti alloy wire containing tube elevators for transcrestal detaching maxillary sinus mucosa, and developed goat ex vivo models for direct visualizing the effectiveness of detaching sinus mucosa in real time during transcrestal maxillary sinus floor elevation. Methods: We evaluated our invented elevators, namely elevator 012 and elevator 014, for their effectiveness for transcrestal detaching maxillary sinus mucosa using the goat ex vivo models. We measured the length of sinus mucosa detached in mesial and distal directions or buccal and palatal directions, and the space volume created by detaching maxillary sinus mucosa in mesial, distal, buccal and palatal directions using the invented elevators. Results: Elevator 012 had a shape-memory Ni/Ti alloy wire with a diameter of 0.012 inch, while elevator 014 had its shape-memory Ni/Ti alloy wire with a diameter of 0.014 inch. Elevator 012 could detach the goat maxillary sinus mucosa in the mesial or distal direction for 12.1±4.3 mm, while in the buccal or palatal direction for 12.5±6.7 mm. The elevator 014 could detach the goat maxillary sinus mucosa for 23.0±4.9 mm in the mesial or distal direction, and for 19.0±8.1 mm in the buccal or palatal direction. An average space volume of 1.7936±0.2079 ml was created after detaching the goat maxillay sinus mucosa in both mesial/distal direction and buccal/palatal direction using elevator 012; while the average space volume created using elevator 014 was 1.8764±0.2366 ml. Conclusion: Both two newly invented tube elevators could effectively detach the maxillary sinus mucosa on the goat ex

  12. Feasibility of Shape-Memory Ni/Ti Alloy Wire Containing Tube Elevators for Transcrestal Detaching Maxillary Sinus Mucosa: Ex Vivo Study.

    Science.gov (United States)

    Li, Yanfeng; Wang, Fuli; Hu, Pin; Fan, Jiadong; Han, Yishi; Liu, Bin; Liu, Tao; Yang, Chunhao; Gu, Xiangmin

    2016-01-01

    Osteotome sinus floor elevation is a less invasive approach to augment an insufficient alveolar bone at the posterior maxilla for dental implantation. However, this approach has some limitations due to the lack of sinus lift tools available for clinical use and the small transcrestal access to the maxillary sinus floor. We recently invented shape-memory Ni/Ti alloy wire containing tube elevators for transcrestal detaching maxillary sinus mucosa, and developed goat ex vivo models for direct visualizing the effectiveness of detaching sinus mucosa in real time during transcrestal maxillary sinus floor elevation. We evaluated our invented elevators, namely elevator 012 and elevator 014, for their effectiveness for transcrestal detaching maxillary sinus mucosa using the goat ex vivo models. We measured the length of sinus mucosa detached in mesial and distal directions or buccal and palatal directions, and the space volume created by detaching maxillary sinus mucosa in mesial, distal, buccal and palatal directions using the invented elevators. Elevator 012 had a shape-memory Ni/Ti alloy wire with a diameter of 0.012 inch, while elevator 014 had its shape-memory Ni/Ti alloy wire with a diameter of 0.014 inch. Elevator 012 could detach the goat maxillary sinus mucosa in the mesial or distal direction for 12.1±4.3 mm, while in the buccal or palatal direction for 12.5±6.7 mm. The elevator 014 could detach the goat maxillary sinus mucosa for 23.0±4.9 mm in the mesial or distal direction, and for 19.0±8.1 mm in the buccal or palatal direction. An average space volume of 1.7936±0.2079 ml was created after detaching the goat maxillay sinus mucosa in both mesial/distal direction and buccal/palatal direction using elevator 012; while the average space volume created using elevator 014 was 1.8764±0.2366 ml. Both two newly invented tube elevators could effectively detach the maxillary sinus mucosa on the goat ex vivo sinus models. Moreover, elevator 014 has advantages over

  13. On the Ni-Ion release rate from surfaces of binary NiTi shape memory alloys

    Science.gov (United States)

    Ševčíková, Jana; Bártková, Denisa; Goldbergová, Monika; Kuběnová, Monika; Čermák, Jiří; Frenzel, Jan; Weiser, Adam; Dlouhý, Antonín

    2018-01-01

    The study is focused on Ni-ion release rates from NiTi surfaces exposed in the cell culture media and human vascular endothelial cell (HUVEC) culture environments. The NiTi surface layers situated in the depth of 70 μm below a NiTi oxide scale are affected by interactions between the NiTi alloys and the bio-environments. The finding was proved with use of inductively coupled plasma mass spectrometry and electron microscopy experiments. As the exclusive factor controlling the Ni-ion release rates was not only thicknesses of the oxide scale, but also the passivation depth, which was two-fold larger. Our experimental data strongly suggested that some other factors, in addition to the Ni concentration in the oxide scale, admittedly hydrogen soaking deep below the oxide scale, must be taken into account in order to rationalize the concentrations of Ni-ions released into the bio-environments. The suggested role of hydrogen as the surface passivation agent is also in line with the fact that the Ni-ion release rates considerably decrease in NiTi samples that were annealed in controlled hydrogen atmospheres prior to bio-environmental exposures.

  14. Surface Characteristics of Machined NiTi Shape Memory Alloy: The Effects of Cryogenic Cooling and Preheating Conditions

    Science.gov (United States)

    Kaynak, Y.; Huang, B.; Karaca, H. E.; Jawahir, I. S.

    2017-07-01

    This experimental study focuses on the phase state and phase transformation response of the surface and subsurface of machined NiTi alloys. X-ray diffraction (XRD) analysis and differential scanning calorimeter techniques were utilized to measure the phase state and the transformation response of machined specimens, respectively. Specimens were machined under dry machining at ambient temperature, preheated conditions, and cryogenic cooling conditions at various cutting speeds. The findings from this research demonstrate that cryogenic machining substantially alters austenite finish temperature of martensitic NiTi alloy. Austenite finish ( A f) temperature shows more than 25 percent increase resulting from cryogenic machining compared with austenite finish temperature of as-received NiTi. Dry and preheated conditions do not substantially alter austenite finish temperature. XRD analysis shows that distinctive transformation from martensite to austenite occurs during machining process in all three conditions. Complete transformation from martensite to austenite is observed in dry cutting at all selected cutting speeds.

  15. Effect of cooling rate on the phase transformation behavior and mechanical properties of Ni-rich NiTi shape memory alloy

    Energy Technology Data Exchange (ETDEWEB)

    Motemani, Y. [School of Mechanical and Aerospace Engineering, Nanyang Technological University, Singapore 639798 (Singapore); Nili-Ahmadabadi, M. [School of Metallurgy and Materials Engineering, Faculty of Engineering, University of Tehran, 14395-731 Tehran (Iran, Islamic Republic of); Tan, M.J. [School of Mechanical and Aerospace Engineering, Nanyang Technological University, Singapore 639798 (Singapore)], E-mail: mmjtan@ntu.edu.sg; Bornapour, M.; Rayagan, Sh. [School of Metallurgy and Materials Engineering, Faculty of Engineering, University of Tehran, 14395-731 Tehran (Iran, Islamic Republic of)

    2009-02-05

    TiNi alloy is a well-known shape memory alloy and has been widely used for bio-medical, mechanical and electrical applications. In this study, a Ni-rich NiTi alloy was prepared by vacuum arc melting in a water-cooled copper crucible. Three samples of this alloy were heated to 1000 deg. C and cooled in three media: furnace, water, and dry-ice bath. Differential scanning calorimetry (DSC), X-ray diffraction (XRD), hardness measurement and tensile test were carried out to investigate the effect of cooling rate on transformation temperature and mechanical properties. The results show that Ni{sub 3}Ti intermetallic compounds have a great influence on martensitic phase transformation temperature. These tests clearly showed the correlation between cooling rate and properties of the alloy.

  16. Effect of milling duration on the evolution of shape memory properties in a powder processed Cu-Al-Ni-Ti alloy

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, Mohit; Gupta, Gaurav K.; Shafeeq, Muhamed M.; Modi, Om P.; Prasad, Braj K. [CSIR - Advanced Materials and Processes Research Institute, Bhopal (India)

    2013-09-15

    The present work describes the effect of milling duration on the properties of a powder metallurgy processed Cu-Al-Ni-Ti shape memory alloy employing mechanical alloying. Powder mixtures milled for different durations were sintered in order to investigate the formation of solid solution and evolution of martensitic structure. The idea was to optimize the duration of milling (mechanical alloying) to obtain chemical homogeneity as well as shape memory properties in the processed material without undergoing extensive post homogenization treatment. The martensitic structure was noted to evolve in the powder mix milled for at least 16 hrs, whereas complete transformation to martensite occurred after milling for 40 hrs. Interestingly, the dissolution of alloying elements (to form the {beta} phase prior to the formation of martensite) was noted to complete partially only during mechanical alloying for 40 hrs and remaining during subsequent sintering for 1 hr. The hot pressed compacts of the powders milled for 40 hrs were chemically homogeneous and consisted of fully martensite phase, which is essential for the realization of shape memory properties. They also revealed almost 100% shape recovery at the applied pre-strain levels of 1 and 2%. (orig.)

  17. Behavior and effect of Ti2Ni phase during processing of NiTi shape memory alloy wire from cast ingot

    International Nuclear Information System (INIS)

    Bhagyaraj, J.; Ramaiah, K.V.; Saikrishna, C.N.; Bhaumik, S.K.; Gouthama

    2013-01-01

    Highlights: •Ti 2 Ni second phase particles forms in different sizes and shapes in cast ingot. •TEM evidences showed shearing/fragmentation of Ti 2 Ni during processing. •Matrix close to Ti 2 Ni experienced severe plastic deformation lead to amorphisation. •Ti 2 Ni interfaces were mostly faceted and assist in nucleation of martensite. •Heterogeneity of microstructure observed near to and away from Ti 2 Ni. -- Abstract: Binary NiTi alloy is one of the commercially successful shape memory alloys (SMAs). Generally, the NiTi alloy composition used for thermal actuator application is slightly Ti-rich. In the present study, vacuum arc melted alloy of 50.2Ti–Ni (at.%) composition was prepared and characterized using optical, scanning and transmission electron microcopy. Formation of second phase particles (SPPs) in the cast alloy and their influence on development of microstructure during processing of the alloy into wire form has been investigated. Results showed that the present alloy contained Ti 2 Ni type SPPs in the matrix. In the cast alloy, the Ti 2 Ni particles form in varying sizes (1–10 μm) and shapes. During subsequent thermo-mechanical processing, these SPPs get sheared/fragmented into smaller particles with low aspect ratio. The presence of SPPs plays a significant role in refinement of the microstructure during processing of the alloy. During deformation of the alloy, the matrix phase around the SPPs experiences conditions similar to that observed in severe plastic deformation of metallic materials, leading to localized amorphisation of the matrix phase

  18. On the effect of TiC particles on the tensile properties and on the intrinsic two way effect of NiTi shape memory alloys produced by powder metallurgy

    International Nuclear Information System (INIS)

    Johansen, K.; Voggenreiter, H.; Eggeler, G.

    1999-01-01

    The present study investigates the tensile properties of a nickel titanium (NiTi) shape memory alloy (SMA) produced by powder metallurgy (PM) with and without TiC-particles. It discusses the effect of the addition of particles on the mechanical behavior in tension and studies the intrinsic two way effect (ε 2W ) after thermomechanical training. Special emphasis is placed on the stability of ε 2W after subsequent thermal cycling. The results are discussed on the basis of an analysis of the thermomechanical data and microstructural results. The present study shows that the PM route can produce NiTi SMAs with tensile properties which match those of materials produced by classical ingot metallurgy. Adding TiC particles to NiTi SMAs alters the phase transition temperatures (PTTs) and affects the SMA performance. Adding more than ten volume percent TiC particles results in early and brittle rupture during tensile loading. (orig.)

  19. Grain Nucleation and Growth in Deformed NiTi Shape Memory Alloys: An In Situ TEM Study

    Science.gov (United States)

    Burow, J.; Frenzel, J.; Somsen, C.; Prokofiev, E.; Valiev, R.; Eggeler, G.

    2017-12-01

    The present study investigates the evolution of nanocrystalline (NC) and ultrafine-grained (UFG) microstructures in plastically deformed NiTi. Two deformed NiTi alloys were subjected to in situ annealing in a transmission electron microscope (TEM) at 400 and 550 °C: an amorphous material state produced by high-pressure torsion (HPT) and a mostly martensitic partly amorphous alloy produced by wire drawing. In situ annealing experiments were performed to characterize the microstructural evolution from the initial nonequilibrium states toward energetically more favorable microstructures. In general, the formation and evolution of nanocrystalline microstructures are governed by the nucleation of new grains and their subsequent growth. Austenite nuclei which form in HPT and wire-drawn microstructures have sizes close to 10 nm. Grain coarsening occurs in a sporadic, nonuniform manner and depends on the physical and chemical features of the local environment. The mobility of grain boundaries in NiTi is governed by the local interaction of each grain with its microstructural environment. Nanograin growth in thin TEM foils seems to follow similar kinetic laws to those in bulk microstructures. The present study demonstrates the strength of in situ TEM analysis and also highlights aspects which need to be considered when interpreting the results.

  20. Investigation of the Self-Healing Behavior of Sn-Bi Metal Matrix Composite Reinforced with NiTi Shape Memory Alloy Strips Under Flexural Loading

    Science.gov (United States)

    Poormir, Mohammad Amin; Khalili, Seyed Mohammad Reza; Eslami-Farsani, Reza

    2018-06-01

    Utilizing intelligent materials such as shape memory alloys as reinforcement in metal matrix composites is a novel method to mimic self-healing behavior. In this study, the bending behavior of a self-healing metal matrix composite made from Sn-13 wt.% Bi alloy as matrix and NiTi shape memory alloy (SMA) strips as reinforcement is investigated. Specimens were fabricated in different reinforcement vol.% (0.78, 1.55, 2.33) and in various pre-strains (0, 2, 6%) and were healed at three healing temperatures (170°C, 180°C, 190°C). Results showed that shape recovery was accomplished in all the specimens, but not all of them were able to withstand second loading after healing. Only specimens with 2.33 vol.% of SMA strips, 1.55 vol.% of SMA, and 6% pre-strain could endure bending force after healing, and they gained 35.31-51.83% of bending force self-healing efficiency.

  1. A Two-Way Shape Memory Study on Ni-Rich NiTi Shape Memory Alloy by Combination of the All-Round Treatment and the R-Phase Transformation

    Science.gov (United States)

    Wu, Z. H.; Vokoun, D.; Leu, C. C.; Hu, C. T.

    2017-12-01

    Ni4Ti3 precipitates are formed in Ni-rich NiTi shape memory alloys (SMAs) after a certain heat treatment. Such a treatment then results in the changed phase transformation behavior of the alloy switching from the one-step reversible phase change B2 ↔ B19' to the two-step, B2 ↔ R ↔ B19', phase change. The present study reports a two-way shape memory (TWSM) due to an all-round treatment followed by an R-phase constraint aging at room temperature. The enhanced TWSM behavior was observed upon temperature cycling between 273 K (R-phase) and 77 K (B19' phase). The effect of various constraint strains in R-phase aging by employing different diameters of the constraint ring was studied. However, the TWSM effect due to constraining the R-phase will be eliminated after a temperature rise of specimen to the fully parent phase (373 K).

  2. The High Performance Shape Memory Effect (HP-SME in Ni Rich NiTi Wires: In Situ X-Ray Diffraction on Thermal Cycling

    Directory of Open Access Journals (Sweden)

    Coduri Mauro

    2015-01-01

    Full Text Available A novel approach for using Shape Memory Alloys (SMA was recently proposed and named highperformance shape memory effect (HP-SME. The HP-SME exploits the thermal cycling of stress-induced martensite for producing extremely high mechanical work with a very stable functional fatigue behaviour in Ni rich NiTi alloy. The latter was found to differ significantly from the functional fatigue behaviour observed for conventional SMA. This study was undertaken in order to elucidate the microstructural modifications at the basis of this particular feature. To this purpose, the functional fatigue was coupled to in situ Synchrotron Radiation X-Ray Diffraction, by recording patterns on wires thermally cycled by Joule effect under a constant applied stress (800 MPa. The accurate analysis the line profile XRD data suggests the accumulation of defects upon functional cycling, while the fibre texture was not observed to change. The functional fatigue exhibits a very similar behaviour as the line broadening of XRD peaks, thus suggesting the accumulation of dislocations as the origin of the mechanism of the permanent deformation.

  3. In Situ Synchrotron Radiation X-ray Diffraction Study on Phase and Oxide Growth during a High Temperature Cycle of a NiTi-20 at.% Zr High Temperature Shape Memory Alloy

    Science.gov (United States)

    Carl, Matthew; Van Doren, Brian; Young, Marcus L.

    2018-02-01

    Ternary additions to binary NiTi shape memory alloys are known to significantly affect the characteristic martensite-to-austenite phase transformation, i.e., decrease or increase transformation temperatures. High temperature shape memory alloys can be created by adding Au, Pt, Pd, Hf, or Zr to binary NiTi in appropriate amounts; however, the majority of these ternary additions are exceedingly expensive, unfortunately making them impractical for most commercial applications. Zr is the exception of the group, but it is often disregarded because of its poor workability and thermal stability. In an effort to find a temperature range that allows for the potential workability of NiTiZr alloys in normal atmosphere environments and to gain understanding as to the cause of failure during processing, a NiTi-20 at.% Zr was subjected to a thermal cycle ranging from RT to 1000 °C with short 15 min holds at select temperatures during both heating and cooling while simultaneously collecting high-energy synchrotron radiation X-ray diffraction measurements. This study provides valuable insight into the kinetics of precipitation and oxide formation and its relationship to processing. In addition, scanning electron microscopy was performed on five samples, each isothermally held to examine precipitation and oxide structure and growth.

  4. Plugging of feed inlet tube upstands with Ni/Ti shape memory alloy plugs - Heysham 1 power station

    International Nuclear Information System (INIS)

    Mathews, A.J.

    1988-01-01

    The paper contains a description of a new approach for Plugging feed inlet tubes of Gas-Cooled Reactors. Instead of utilizing the original explosive method plugging by fitting a shape memory alloy plug into the upstand is being described. (author)

  5. The influence of imposed strain on the development of microstructure and transformation characteristics of Ni-Ti shape memory alloys

    Czech Academy of Sciences Publication Activity Database

    Kocich, R.; Krusa, M.; Szurman, I.; Dlouhý, Antonín

    2011-01-01

    Roč. 509, č. 6 (2011), s. 2716-2722 ISSN 0925-8388 Institutional research plan: CEZ:AV0Z20410507 Keywords : intermetallics * metals and alloys * shape memory Subject RIV: JG - Metallurgy Impact factor: 2.289, year: 2011

  6. Low Temperature Creep of Hot-Extruded Near-Stoichiometric NiTi Shape Memory Alloy. Part I; Isothermal Creep

    Science.gov (United States)

    Raj, S. V.; Noebe, R. D.

    2013-01-01

    This two-part paper is the first published report on the long term, low temperature creep of hot-extruded near-stoichiometric NiTi. Constant load tensile creep tests were conducted on hot-extruded near-stoichiometric NiTi at 300, 373 and 473 K under initial applied stresses varying between 200 and 350 MPa as long as 15 months. These temperatures corresponded to the martensitic, two-phase and austenitic phase regions, respectively. Normal primary creep lasting several months was observed under all conditions indicating dislocation activity. Although steady-state creep was not observed under these conditions, the estimated creep rates varied between 10(exp -10) and 10(exp -9)/s. The creep behavior of the two phases showed significant differences. The martensitic phase exhibited a large strain on loading followed by a primary creep region accumulating a small amount of strain over a period of several months. The loading strain was attributed to the detwinning of the martensitic phase whereas the subsequent strain accumulation was attributed to dislocation glide-controlled creep. An "incubation period" was observed before the occurrence of detwinning. In contrast, the austenitic phase exhibited a relatively smaller loading strain followed by a primary creep region, where the creep strain continued to increase over several months. It is concluded that the creep of the austenitic phase occurs by a dislocation glide-controlled creep mechanism as well as by the nucleation and growth of deformation twins.

  7. GRAIN-REFINEMENT AND THE RELATED PHENOMENA IN QUATERNARY Cu-Al-Ni-Ti SHAPE MEMORY ALLOYS

    OpenAIRE

    Sugimoto , K.; Kamei , K.; Matsumoto , H.; Komatsu , S.; Akamatsu , K.; Sugimoto , T.

    1982-01-01

    It was reported that the addition of a small amount of titanium (0.5 - 3.99%) to a Cu-13.93%Al-3.36%Ni ternary alloy resulted in a remarkable grain-refining. The original grain-size of about 750 microns under hot-rolled and quenched conditions of the ternary alloy was reduced to that of the order of about 100 microns by addition of tiatanium. It was suggested that several technical improvements of the mechanical properties of Cu-Al-Ni shape memory alloys, such as better formability, less crac...

  8. Fatigue behaviour of NiTi shape memory alloy scaffolds produced by SLM, a unit cell design comparison.

    Science.gov (United States)

    Speirs, M; Van Hooreweder, B; Van Humbeeck, J; Kruth, J-P

    2017-06-01

    Selective laser melting (SLM) is an additive manufacturing technique able to produce complex functional parts via successively melting layers of metal powder. This process grants the freedom to design highly complex scaffold components to allow bone ingrowth and aid mechanical anchorage. This paper investigates the compression fatigue behaviour of three different unit cells (octahedron, cellular gyroid and sheet gyroid) of SLM nitinol scaffolds. It was found that triply periodic minimal surfaces display superior static mechanical properties in comparison to conventional octahedron beam lattice structures at identical volume fractions. Fatigue resistance was also found to be highly geometry dependent due to the effects of AM processing techniques on the surface topography and notch sensitivity. Geometries minimising nodal points and the staircase effect displayed the greatest fatigue resistance when normalized to yield strength. Furthermore oxygen analysis showed a large oxygen uptake during SLM processing which must be altered to meet ASTM medical grade standards and may significantly reduce fatigue life. These achieved fatigue properties indicate that NiTi scaffolds produced via SLM can provide sufficient mechanical support over an implants lifetime within stress range values experienced in real life. Copyright © 2017 Elsevier Ltd. All rights reserved.

  9. Macroscopic and Microstructural Aspects of the Transformation Behavior in a Polycrystalline NiTi Shape Memory Alloy

    Science.gov (United States)

    Benafan, Othmane; Noebe, Ronald D.; Padula, Santo A., II; Lerch, Bradley A.; Bigelow, Glen S.; Gaydosh, Darrell J.; Garg, Anita; An, Ke; Vaidyanathan, Raj

    2013-01-01

    The mechanical and microstructural behavior of a polycrystalline Ni(49.9)Ti(50.1) (at.%) shape memory alloy was investigated as a function of temperature around the transformation regime. The bulk macroscopic responses, measured using ex situ tensile deformation and impulse excitation tests, were compared to the microstructural evolution captured using in situ neutron diffraction. The onset stress for inelastic deformation and dynamic Young's modulus were found to decrease with temperature, in the martensite regime, reaching a significant minimum at approximately 80 C followed by an increase in both properties, attributed to the martensite to austenite transformation. The initial decrease in material compliance during heating affected the ease with which martensite reorientation and detwinning could occur, ultimately impacting the stress for inelastic deformation prior to the start of the reverse transformation.

  10. Biocorrosion investigation of two shape memory nickel based alloys: Ni-Mn-Ga and thin film NiTi.

    Science.gov (United States)

    Stepan, L L; Levi, D S; Gans, E; Mohanchandra, K P; Ujihara, M; Carman, G P

    2007-09-01

    Thin film nitinol and single crystal Ni-Mn-Ga represent two new shape memory materials with potential to be used as percutaneously placed implant devices. However, the biocompatibility of these materials has not been adequately assessed. Immersion tests were conducted on both thin film nitinol and single crystal Ni-Mn-Ga in Hank's balanced salt solution at 37 degrees C and pH 7.4. After 12 h, large pits were found on the Ni-Mn-Ga samples while thin film nitinol displayed no signs of corrosion. Further electrochemical tests on thin film nitinol samples revealed breakdown potentials superior to a mechanically polished nitinol disc. These results suggest that passivation or electropolishing of thin film nitinol maybe unnecessary to promote corrosion resistance.

  11. Comportamento termomecânico de compósitos ativos preparados com nanocompósitos epóxi/argila organofílica e fios de liga Ni-Ti com memória de forma Thermomechanical behavior of active composites prepared with epoxy/organoclay nanocomposites and Ni-Ti shape memory alloy wires

    Directory of Open Access Journals (Sweden)

    Artur S. C. Leal

    2012-01-01

    Full Text Available Neste trabalho, nanocompósitos epóxi/argila organofílica foram selecionados como matriz por apresentarem valores de temperatura de transição vítrea (Tg e estabilidade térmica suficientemente alta para que fios de uma liga com memória de forma (LMF possam ser incorporados. Para tanto, quatro frações volumétricas de fios LMF de Ni-Ti (1,55, 2,56, 3,57 e 4,54% foram embebidas na matriz epoxídica diglicidil éter do bisfenol-A (DGEBA, reticulada com a amina aromática 4,4’-diamino difenil sulfona (DDS contendo 1 pcr da argila bentonita purificada organofiliada (APOC. A formação do nanocompósito foi confirmada por análise de difração de raio X, enquanto a transformação de fase dos fios de Ni-Ti foi determinada por análise dinâmico-mecânica (DMA. As amostras dos compósitos ativos preparados a partir da matriz de nanocompósito e fios de Ni-Ti foram caracterizadas principalmente por DMA. De acordo com os resultados obtidos foi constatada uma recuperação do módulo de armazenamento do compósito ativo durante o aquecimento na faixa de transformação de fase dos fios de Ni-Ti quando a fração volumétrica foi mantida em torno de 3,5%.In this work, epoxy/organoclay nanocomposites were selected as matrix for presenting high enough glass transition temperature (Tg and thermal stability values in order to be incorporated in shape memory alloys (SMA. Four volume fractions of SMA wires containing Ni-Ti (1.55, 2.56, 3.57 and 4.54% were embedded in diglycidyl ether of bisphenol A (DGEBA, cured with the aromatic amine 4,4’-diamino diphenyl sulfone (DDS and containing 1 phr of purified organobentonite (APOC. The formation of nanocomposite was confirmed by X ray diffraction analysis, while the phase transformation of Ni-Ti wires was determined by dynamic mechanical analysis (DMA. Samples of the active composites prepared from nanocomposite matrix and Ni-Ti wires were mainly characterized by DMA. A recovery of the storage modulus of

  12. The Corrosion Resistance of Composite Arch Wire Laser-Welded By NiTi Shape Memory Alloy and Stainless Steel Wires with Cu Interlayer in Artificial Saliva with Protein

    Science.gov (United States)

    Zhang, Chao; Sun, Xinhua; Hou, Xu; Li, Hongmei; Sun, Daqian

    2013-01-01

    In this paper, the corrosion resistance of laser-welded composite arch wire (CoAW) with Cu interlayer between NiTi shape memory alloy and stainless steel wire in artificial saliva with different concentrations of protein was studied. It was found that protein addition had a significant influence on the corrosion behavior of CoAW. Low concentration of protein caused the corrosion resistance of CoAW decrease in electrochemical corrosion and immersion corrosion tests. High concentration of protein could reduce this effect. PMID:23801895

  13. Effect of chemical treatment on surface characteristics of sputter deposited Ti-rich NiTi shape memory alloy thin-films

    International Nuclear Information System (INIS)

    Sharma, S.K.; Mohan, S.

    2014-01-01

    Graphical abstract: FTIR spectra recorded for sputter deposited (a) untreated and (b) chemically treated NiTi SMA thin-films. - Highlights: • The effect of chemical treatment on surface properties of NiTi films demonstrated. • Chemically treated films offer strong ability to form protective TiO 2 layer. • TiO 2 layer formation offer great application prospects in biomedical fields. - Abstract: NiTi thin-films were deposited by DC magnetron sputtering from single alloy target (Ni/Ti:45/55 at.%). The rate of deposition and thickness of sputter deposited films were maintained to ∼35 nm min −1 and 4 μm respectively. A set of sputter deposited NiTi films were selected for specific chemical treatment with the solution comprising of de-ionized water, HF and HNO 3 respectively. The influence of chemical treatment on surface characteristics of NiTi films before and after chemical treatment was investigated for their structure, micro-structure and composition using different analytical techniques. Prior to chemical treatment, the composition of NiTi films using energy dispersive X-ray dispersive spectroscopy (EDS), were found to be 51.8 atomic percent of Ti and 48.2 atomic percent of Ni. The structure and morphology of these films were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). XRD investigations, demonstrated the presence of dominant Austenite (1 1 0) phase along with Martensite phase, for untreated NiTi films whereas some additional diffraction peaks viz. (1 0 0), (1 0 1), and (2 0 0) corresponding to Rutile and Anatase phase of Titanium dioxide (TiO 2 ) along with parent Austenite (1 1 0) phase were observed for chemically treated NiTi films. FTIR studies, it can be concluded that chemically treated films have higher tendency to form metal oxide/hydroxide than the untreated NiTi films. XPS investigations, demonstrated the presence of Ni-free surface and formation of a protective metal oxide (TiO 2 ) layer on the surface of

  14. Mechanical Properties of TiTaHfNbZr High-Entropy Alloy Coatings Deposited on NiTi Shape Memory Alloy Substrates

    Science.gov (United States)

    Motallebzadeh, A.; Yagci, M. B.; Bedir, E.; Aksoy, C. B.; Canadinc, D.

    2018-04-01

    TiTaHfNbZr high-entropy alloy (HEA) thin films with thicknesses of about 750 and 1500 nm were deposited on NiTi substrates by RF magnetron sputtering using TiTaHfNbZr equimolar targets. The thorough experimental analysis on microstructure and mechanical properties of deposited films revealed that the TiTaHfNbZr films exhibited amorphous and cauliflower-like structure, where grain size and surface roughness increased concomitant with film thickness. More importantly, the current findings demonstrate that the TiTaHfNbZr HEA films with mechanical properties of the same order as those of the NiTi substrate constitute promising biomedical coatings effective in preventing Ni release.

  15. Mechanical Properties of TiTaHfNbZr High-Entropy Alloy Coatings Deposited on NiTi Shape Memory Alloy Substrates

    Science.gov (United States)

    Motallebzadeh, A.; Yagci, M. B.; Bedir, E.; Aksoy, C. B.; Canadinc, D.

    2018-06-01

    TiTaHfNbZr high-entropy alloy (HEA) thin films with thicknesses of about 750 and 1500 nm were deposited on NiTi substrates by RF magnetron sputtering using TiTaHfNbZr equimolar targets. The thorough experimental analysis on microstructure and mechanical properties of deposited films revealed that the TiTaHfNbZr films exhibited amorphous and cauliflower-like structure, where grain size and surface roughness increased concomitant with film thickness. More importantly, the current findings demonstrate that the TiTaHfNbZr HEA films with mechanical properties of the same order as those of the NiTi substrate constitute promising biomedical coatings effective in preventing Ni release.

  16. Safety and efficacy of the NiTi Shape Memory Compression Anastomosis Ring (CAR/ColonRing) for end-to-end compression anastomosis in anterior resection or low anterior resection.

    Science.gov (United States)

    Kang, Jeonghyun; Park, Min Geun; Hur, Hyuk; Min, Byung Soh; Lee, Kang Young; Kim, Nam Kyu

    2013-04-01

    Compression anastomoses may represent an improvement over traditional hand-sewn or stapled techniques. This prospective exploratory study aimed to assess the efficacy and complication rates in patients undergoing anterior resection (AR) or low anterior resection (LAR) anastomosed with a novel end-to-end compression anastomosis ring, the ColonRing. In all, 20 patients (13 male) undergoing AR or LAR were enrolled to be anastomosed using the NiTi Shape Memory End-to-End Compression Anastomosis Ring (NiTi Medical Technologies Ltd, Netanya, Israel). Demographic, intraoperative, and postoperative data were collected. Patients underwent AR (11/20) or LAR using laparoscopy (75%), robotic (10%) surgery, or an open laparotomy (15%) approach, with a median anastomotic level of 14.5 cm (range, 4-25 cm). Defunctioning loop ileostomies were formed in 6 patients for low anastomoses. Surgeons rated the ColonRing device as either easy or very easy to use. One patient developed an anastomotic leakage in the early postoperative period; there were no late postoperative complications. Mean time to passage of first flatus and commencement of oral fluids was 2.5 days and 3.2 days, respectively. Average hospital stay was 12.6 days (range, 8-23 days). Finally, the device was expelled on average 15.3 days postoperatively without difficulty. This is the first study reporting results in a significant number of LAR patients and the first reported experience from South Korea; it shows that the compression technique is surgically feasible, easy to use, and without significant complication rates. A large randomized controlled trial is warranted to investigate the benefits of the ColonRing over traditional stapling techniques.

  17. Xenon focused ion beam in the shape memory alloys investigation – the case of NiTi and CoNiAl

    Czech Academy of Sciences Publication Activity Database

    Kopeček, Jaromír; Jurek, Karel; Kopecký, Vít; Klimša, Ladislav; Seiner, Hanuš; Sedlák, Petr; Landa, Michal; Dluhoš, J.; Petrenec, M.; Hladík, L.; Doupal, A.; Heczko, Oleg

    2014-01-01

    Roč. 20, Aug (2014), s. 335-336 ISSN 1431-9276 R&D Projects: GA ČR(CZ) GA14-03044S Institutional support: RVO:68378271 ; RVO:61388998 Keywords : scanning electron microscope * SEM * focused ion beam * FIB * xenon plasma focused ion beam * dual beam * shape memory alloy * SMA Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 1.877, year: 2014

  18. The effect of cold work, heat treatment, and composition on the austenite to R-phase transformation temperature of Ni-Ti shape memory alloys

    International Nuclear Information System (INIS)

    Thoma, P.E.; Angst, D.R.; Schachner, K.D.

    1995-01-01

    The influence of cold work (CW) and heat treatment (HT) on the austenite to R-Phase (A→R) transformation temperature (TT) of a near equiatomic and three other Ti rich NiTi SMA is examined. For the SMA having a near equiatomic composition, the A→R TT increases with increasing CW at low HT temperatures. For the SMA having the maximum possible Ti content, the A→R TT decreases with increasing CW at low HT temperatures. For all compositions, the A→R TT is not sensitive to CW at high HT temperatures. At a Ti content slightly below the maximum possible, the A→R TT is relatively insensitive to CW and HT temperature. For all of the SMA investigated, the A→R TT increases with increasing Ti content for a specific CW and HT temperature, and this effect is greatest at low CW and at high HT temperatures. (orig.)

  19. Thermomechanical model for NiTi-based shape memory alloys including R-phase and material anisotropy under multi-axial loadings

    Czech Academy of Sciences Publication Activity Database

    Sedlák, Petr; Frost, Miroslav; Benešová, Barbora; Zineb, T.B.; Šittner, Petr

    2012-01-01

    Roč. 39, DEC 2012 (2012), s. 132-151 ISSN 0749-6419 R&D Projects: GA ČR GAP108/10/1296; GA ČR GA106/09/1573; GA ČR(CZ) GA101/09/0702; GA ČR GAP107/12/0800 Institutional research plan: CEZ:AV0Z20760514; CEZ:AV0Z10100521 Keywords : shape memory alloys * constitutive modeling * R-phase * non-proportional loading * dissipation function Subject RIV: BJ - Thermodynamics; JJ - Other Materials (FZU-D) Impact factor: 4.356, year: 2012 http://www.sciencedirect.com/science/article/pii/S0749641912001027

  20. Modeling of mechanical response of NiTi shape memory alloy subjected to combined thermal and non-proportional mechanical loading: A case study on helical spring actuator

    Czech Academy of Sciences Publication Activity Database

    Frost, Miroslav; Sedlák, Petr; Kadeřávek, Lukáš; Heller, Luděk; Šittner, Petr

    2016-01-01

    Roč. 27, č. 14 (2016), s. 1927-1938 ISSN 1045-389X R&D Projects: GA ČR(CZ) GP14-28306P; GA ČR GA14-15264S; GA ČR GAP107/12/0800 Institutional support: RVO:61388998 ; RVO:68378271 Keywords : shape memory alloys * R-phase * modeling * elastic anisotropy * helical spring Subject RIV: BM - Solid Matter Physics ; Magnetism; BM - Solid Matter Physics ; Magnetism (FZU-D) Impact factor: 2.255, year: 2016 http://jim.sagepub.com/content/27/14/1927.full.pdf

  1. Determining Recoverable and Irrecoverable Contributions to Accumulated Strain in a NiTiPd High-Temperature Shape Memory Alloy During Thermomechanical Cycling

    Science.gov (United States)

    Monroe, J. A.; Karaman, I.; Lagoudas, D. C.; Bigelow, G.; Noebe, R. D.; Padula, S., II

    2011-01-01

    When Ni(29.5)Ti(50.5)Pd30 shape memory alloy is thermally cycled under stress, significant strain can accumulate due to elasticity, remnant oriented martensite and plasticity. The strain due to remnant martensite can be recovered by further thermal cycling under 0 MPa until the original transformation-induced volume change and martensite coefficient of thermal expansion are obtained. Using this technique, it was determined that the 8.15% total accumulated strain after cycling under 200 MPa consisted of 0.38%, 3.97% and 3.87% for elasticity, remnant oriented martensite and creep/plasticity, respectively.

  2. Low Temperature Creep of Hot-Extruded Near-Stoichiometric NiTi Shape Memory Alloy. Part 2; Effect of Thermal Cycling

    Science.gov (United States)

    Raj, S. V.; Noebe, R. D.

    2013-01-01

    This paper is the first report on the effect prior low temperature creep on the thermal cycling behavior of NiTi. The isothermal low temperature creep behavior of near-stoichiometric NiTi between 300 and 473 K was discussed in Part I. The effect of temperature cycling on its creep behavior is reported in the present paper (Part II). Temperature cycling tests were conducted between either 300 or 373 K and 473 K under a constant applied stress of either 250 or 350 MPa with hold times lasting at each temperature varying between 300 and 700 h. Each specimen was pre-crept either at 300 or at 473 K for several months under an identical applied stress as that used in the subsequent thermal cycling tests. Irrespective of the initial pre-crept microstructures, the specimens exhibited a considerable increase in strain with each thermal cycle so that the total strain continued to build-up to 15 to 20 percent after only 5 cycles. Creep strains were immeasurably small during the hold periods. It is demonstrated that the strains in the austenite and martensite are linearly correlated. Interestingly, the differential irrecoverable strain, in the material measured in either phase decreases with increasing number of cycles, similar to the well-known Manson-Coffin relation in low cycle fatigue. Both phases are shown to undergo strain hardening due to the development of residual stresses. Plots of true creep rate against absolute temperature showed distinct peaks and valleys during the cool-down and heat-up portions of the thermal cycles, respectively. Transformation temperatures determined from the creep data revealed that the austenitic start and finish temperatures were more sensitive to the pre-crept martensitic phase than to the pre-crept austenitic phase. The results are discussed in terms of a phenomenological model, where it is suggested that thermal cycling between the austenitic and martensitic phase temperatures or vice versa results in the deformation of the austenite and

  3. Simulations of Self-Expanding Braided Stent Using Macroscopic Model of NiTi Shape Memory Alloys Covering R-Phase

    Czech Academy of Sciences Publication Activity Database

    Frost, Miroslav; Sedlák, Petr; Kruisová, Alena; Landa, Michal

    2014-01-01

    Roč. 23, č. 7 (2014), s. 2584-2590 ISSN 1059-9495 R&D Projects: GA ČR GA14-15264S; GA ČR(CZ) GP14-28306P; GA ČR GA13-13616S Grant - others:Rada Programu interní podpory projektů mezinárodní spolupráce AV ČR(CZ) M100761203 Program:M Institutional support: RVO:61388998 Keywords : braided stent * numerical simulation * R-phase * shape memory alloys Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.998, year: 2014 http://link.springer.com/article/10.1007/s11665-014-0966-z

  4. Three-dimensional deformation response of a NiTi shape memory helical-coil actuator during thermomechanical cycling: experimentally validated numerical model

    Science.gov (United States)

    Dhakal, B.; Nicholson, D. E.; Saleeb, A. F.; Padula, S. A., II; Vaidyanathan, R.

    2016-09-01

    Shape memory alloy (SMA) actuators often operate under a complex state of stress for an extended number of thermomechanical cycles in many aerospace and engineering applications. Hence, it becomes important to account for multi-axial stress states and deformation characteristics (which evolve with thermomechanical cycling) when calibrating any SMA model for implementation in large-scale simulation of actuators. To this end, the present work is focused on the experimental validation of an SMA model calibrated for the transient and cyclic evolutionary behavior of shape memory Ni49.9Ti50.1, for the actuation of axially loaded helical-coil springs. The approach requires both experimental and computational aspects to appropriately assess the thermomechanical response of these multi-dimensional structures. As such, an instrumented and controlled experimental setup was assembled to obtain temperature, torque, degree of twist and extension, while controlling end constraints during heating and cooling of an SMA spring under a constant externally applied axial load. The computational component assesses the capabilities of a general, multi-axial, SMA material-modeling framework, calibrated for Ni49.9Ti50.1 with regard to its usefulness in the simulation of SMA helical-coil spring actuators. Axial extension, being the primary response, was examined on an axially-loaded spring with multiple active coils. Two different conditions of end boundary constraint were investigated in both the numerical simulations as well as the validation experiments: Case (1) where the loading end is restrained against twist (and the resulting torque measured as the secondary response) and Case (2) where the loading end is free to twist (and the degree of twist measured as the secondary response). The present study focuses on the transient and evolutionary response associated with the initial isothermal loading and the subsequent thermal cycles under applied constant axial load. The experimental

  5. Development and Characterization of Improved NiTiPd High-Temperature Shape-Memory Alloys by Solid-Solution Strengthening and Thermomechanical Processing

    Science.gov (United States)

    Bigelow, Glen; Noebe, Ronald; Padula, Santo, II; Garg, Anita; Olson, David

    2006-01-01

    The need for compact, solid-state actuation systems for use in the aerospace, automotive, and other transportation industries is currently motivating research in high-temperature shape-memory alloys (HTSMA) with transformation temperatures greater than 100 C. One of the basic high-temperature alloys investigated to fill this need is Ni(19.5)Ti(50.5)Pd30. Initial testing has indicated that this alloy, while having acceptable work characteristics, suffers from significant permanent deformation (or ratcheting) during thermal cycling under load. In an effort to overcome this deficiency, various solid-solution alloying and thermomechanical processing schemes were investigated. Solid-solution strengthening was achieved by substituting 5at% gold or platinum for palladium in Ni(19.5)Ti(50.5)Pd30, the so-called baseline alloy, to strengthen the martensite and austenite phases against slip processes and improve thermomechanical behavior. Tensile properties, work behavior, and dimensional stability during repeated thermal cycling under load for the ternary and quaternary alloys were compared. The relative difference in yield strength between the martensite and austenite phases and the dimensional stability of the alloy were improved by the quaternary additions, while work output was only minimally impacted. The three alloys were also thermomechanically processed by cycling repeatedly through the transformation range under a constant stress. This so-called training process dramatically improved the dimensional stability in these samples and also recovered the slight decrease in work output caused by quaternary alloying. An added benefit of the solid-solution strengthening was maintenance of enhanced dimensional stability of the trained material to higher temperatures compared to the baseline alloy, providing a greater measure of over-temperature capability.

  6. Phase transformation kinetics and microstructure of NiTi shape ...

    Indian Academy of Sciences (India)

    2017-07-28

    Jul 28, 2017 ... exhibiting thermoelastic martensitic transition is deformed or bent at a temperature ... Memory-Metalle Gmbh, Germany. The nominal composi- ... ture Ap, martensite peak temperature Mp and absorbed energy values during ...

  7. Influence of NiTi alloy on the root canal shaping capabilities of the ProTaper Universal and ProTaper Gold rotary instrument systems

    Directory of Open Access Journals (Sweden)

    Jussaro Alves DUQUE

    Full Text Available Abstract Objective This study aimed to evaluate the influence of the NiTi wire in Conventional NiTi (ProTaper Universal PTU and Controlled Memory NiTi (ProTaper Gold PTG instrument systems on the quality of root canal preparation. Material and Methods Twelve mandibular molars with separate mesial canals were scanned using a high-definition microcomputed tomography system. The PTU and PTG instruments were used to shape twelve mesial canals each. The canals were scanned after preparation with F2 and F3 instruments of the PTU and PTG systems. The analyzed parameters included the remaining dentin thickness at the apical and cervical levels, root canal volume and untouched canal walls. Data was analyzed for statistical significance by the Friedman and Dunn’s tests. For the comparison of data between groups, the Mann-Whitney test was used. Results In the pre-operative analysis, there were no statistically significant differences between the groups in terms of the area and volume of root canals (P>.05. There was also no statistically significant difference between the systems with respect to root canal volume after use of the F2 and F3 instruments. There was no statistical difference in the dentin thickness at the first apical level between, before and after instrumentation for both systems. At the 3 cervical levels, the PTG maintained centralization of the preparation on the transition between the F2 and F3 instruments, which did not occur with the PTU. Conclusion The Conventional NiTi (PTU and Controlled Memory NiTi (PTG instruments displayed comparable capabilities for shaping the straight mesial root canals of mandibular molars, although the PTG was better than the PTU at maintaining the centralization of the shape in the cervical portion.

  8. Influence of NiTi alloy on the root canal shaping capabilities of the ProTaper Universal and ProTaper Gold rotary instrument systems

    Science.gov (United States)

    DUQUE, Jussaro Alves; VIVAN, Rodrigo Ricci; CAVENAGO, Bruno Cavalini; AMOROSO-SILVA, Pablo Andrés; BERNARDES, Ricardo Affonso; de VASCONCELOS, Bruno Carvalho; DUARTE, Marco Antonio Hungaro

    2017-01-01

    Abstract Objective This study aimed to evaluate the influence of the NiTi wire in Conventional NiTi (ProTaper Universal PTU) and Controlled Memory NiTi (ProTaper Gold PTG) instrument systems on the quality of root canal preparation. Material and Methods Twelve mandibular molars with separate mesial canals were scanned using a high-definition microcomputed tomography system. The PTU and PTG instruments were used to shape twelve mesial canals each. The canals were scanned after preparation with F2 and F3 instruments of the PTU and PTG systems. The analyzed parameters included the remaining dentin thickness at the apical and cervical levels, root canal volume and untouched canal walls. Data was analyzed for statistical significance by the Friedman and Dunn’s tests. For the comparison of data between groups, the Mann-Whitney test was used. Results In the pre-operative analysis, there were no statistically significant differences between the groups in terms of the area and volume of root canals (P>.05). There was also no statistically significant difference between the systems with respect to root canal volume after use of the F2 and F3 instruments. There was no statistical difference in the dentin thickness at the first apical level between, before and after instrumentation for both systems. At the 3 cervical levels, the PTG maintained centralization of the preparation on the transition between the F2 and F3 instruments, which did not occur with the PTU. Conclusion The Conventional NiTi (PTU) and Controlled Memory NiTi (PTG) instruments displayed comparable capabilities for shaping the straight mesial root canals of mandibular molars, although the PTG was better than the PTU at maintaining the centralization of the shape in the cervical portion. PMID:28198973

  9. Superelastic NiTi memory alloy micro-tube under tension - nucleation and propagation of martensite band

    International Nuclear Information System (INIS)

    Li, Z.Q.; Sun, Q.P.

    2000-01-01

    The superelastic behavior of polycrystalline NiTi shape memory alloy micro-tube under tension is studied experimentally. The nominal stress-strain curve of the micro-tube is recorded. By using a special surface coating it is found that the deformation of the tube is via the nucleation and propagation of stress-induced martensite band. The experiments show that the martensite nucleates in the form of a spiral lens-shaped narrow band that is inclined at 61 to the axis of loading when the stress reaches the peak of stress-strain curve. The width and the length of the band grew gradually with increase of loading and finally joined and merged into a single band. The subsequent deformation of the tube is realized by the propagation of this cylindrical martensite band. (orig.)

  10. Microstructure and kinetics of a functionally graded NiTi-TiC x composite produced by combustion synthesis

    International Nuclear Information System (INIS)

    Burkes, Douglas E.; Moore, John J.

    2007-01-01

    Production of a NiTi-TiC x functionally graded material (FGM) composite is possible through use of a combustion synthesis (CS) reaction employing the propagating mode (SHS). The NiTi-TiC x FGM combines the well-known and understood superelastic and shape memory capabilities of NiTi with the high hardness, wear and corrosion resistance of TiC x . The material layers were observed as functionally graded both in composition and porosity with distinct interfaces, while still maintaining good material interaction and bonding. XRD of the FGM composite revealed the presence of TiC x with equi-atomic NiTi and minor NiTi 2 and NiTi 3 phases. The TiC x particle size decreased with increasing NiTi content. Microindentation performed across the length of the FGM revealed a decrease in hardness as the NiTi content increased

  11. Geometric analysis of root canals prepared by four rotary NiTi shaping systems.

    Science.gov (United States)

    Hashem, Ahmed Abdel Rahman; Ghoneim, Angie Galal; Lutfy, Reem Ahmed; Foda, Manar Yehia; Omar, Gihan Abdel Fatah

    2012-07-01

    A great number of nickel-titanium (NiTi) rotary systems with noncutting tips, different cross-sections, superior resistance to torsional fracture, varying tapers, and manufacturing method have been introduced to the market. The purpose of this study was to evaluate and compare the effect of 4 rotary NiTi preparation systems, Revo-S (RS; Micro-Mega, Besancon Cedex, France), Twisted file (TF; SybronEndo, Amersfoort, The Netherlands), ProFile GT Series X (GTX; Dentsply, Tulsa Dental Specialties, Tulsa, OK), and ProTaper (PT; Dentsply Maillefer, Ballaigues, Switzerland), on volumetric changes and transportation of curved root canals. Forty mesiobuccal canals of mandibular molars with an angle of curvature ranging from 25° to 40° were divided according to the instrument used in canal preparation into 4 groups of 10 samples each: group RS, group TF, group GTX, and group PT. Canals were scanned using an i-CAT CBCT scanner (Imaging Science International, Hatfield, PA) before and after preparation to evaluate the volumetric changes. Root canal transportation and centering ratio were evaluated at 1.3, 2.6, 5.2, and 7.8 mm from the apex. The significance level was set at P ≤ .05. The PT system removed a significantly higher amount of dentin than the other systems (P = .025). At the 1.3-mm level, there was no significant difference in canal transportation and centering ratio among the groups. However, at the other levels, TF maintained the original canal curvature recording significantly the least degree of canal transportation as well as the highest mean centering ratio. The TF system showed superior shaping ability in curved canals. Revo-S and GTX were better than ProTaper regarding both canal transportation and centering ability. Copyright © 2012 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

  12. Shape memory alloys

    International Nuclear Information System (INIS)

    Kaszuwara, W.

    2004-01-01

    Shape memory alloys (SMA), when deformed, have the ability of returning, in certain circumstances, to their initial shape. Deformations related to this phenomenon are for polycrystals 1-8% and up to 15% for monocrystals. The deformation energy is in the range of 10 6 - 10 7 J/m 3 . The deformation is caused by martensitic transformation in the material. Shape memory alloys exhibit one directional or two directional shape memory effect as well as pseudoelastic effect. Shape change is activated by temperature change, which limits working frequency of SMA to 10 2 Hz. Other group of alloys exhibit magnetic shape memory effect. In these alloys martensitic transformation is triggered by magnetic field, thus their working frequency can be higher. Composites containing shape memory alloys can also be used as shape memory materials (applied in vibration damping devices). Another group of composite materials is called heterostructures, in which SMA alloys are incorporated in a form of thin layers The heterostructures can be used as microactuators in microelectromechanical systems (MEMS). Basic SMA comprise: Ni-Ti, Cu (Cu-Zn,Cu-Al, Cu-Sn) and Fe (Fe-Mn, Fe-Cr-Ni) alloys. Shape memory alloys find applications in such areas: automatics, safety and medical devices and many domestic appliances. Currently the most important appears to be research on magnetic shape memory materials and high temperature SMA. Vital from application point of view are composite materials especially those containing several intelligent materials. (author)

  13. A comparison of the shaping ability of reciprocating NiTi instruments in simulated curved canals

    Directory of Open Access Journals (Sweden)

    Young-Sil Yoo

    2011-11-01

    Full Text Available Objectives The study was to compare the shaping ability of Reciproc (VDW and WaveOne (Dentsply Maillefer instruments compared with ProTaper, Profile and hand instrument during the preparation of simulated root canals. Materials and Methods Five groups (n = 5 were established. Reciproc, WaveOne, ProTaper, Profile and K file (K-flexo file were used to prepare the resin simulated canals. A series of preoperative and postoperative images were taken by a microscope and superimposed in 2 different layers. The amount of resin removed from both the inner and the outer sides of the canal was measured to the level of 10 mm from the apical tip, with a 1 mm increment. Results The mean of resin removal from the inner canal wall was not different from the outer canal wall for Reciproc and WaveOne groups at apical third (1 - 3 mm level. There was no difference in the change of working length and maintenance of canal curvature. NiTi instruments are superior to stainless-steel K file in their shaping ability. Conclusions Within the limitation of this present study, Reciproc and WaveOne instruments maintained the original canal curvature in curved canals better than ProTaper and Profile, which tend to transport towards the outer canal wall of the curve in the apical part of the canal.

  14. Processing and Characterization of Liquid-Phase Sintered NiTi Woven Structures

    Science.gov (United States)

    Erdeniz, Dinc; Weidinger, Ryan P.; Sharp, Keith W.; Dunand, David C.

    2018-03-01

    Porous NiTi is of interest for bone implants because of its unique combination of biocompatibility (encouraging osseointegration), high strength (to prevent fracture), low stiffness (to reduce stress shielding), and shape memory or superelasticity (to deploy an implant). A promising method for creating NiTi structures with regular open channels is via 3D weaving of NiTi wires. This paper presents a processing method to bond woven NiTi wire structures at contact points between wires to achieve structural integrity: (i) a slurry consisting of a blend of NiTi and Nb powders is deposited on the surface of the NiTi wires after the weaving operation; (ii) the powders are melted to create a eutectic liquid phase which collects at contact points; and (iii) the liquid is solidified and binds the NiTi woven structures. The bonded NiTi wire structures exhibited lower transformation temperatures compared to the as-woven NiTi wires because of Nb diffusion into the NiTi wires. A bonded woven sample was deformed in bending and showed near-complete recovery up to 6% strain and recovered nearly half of the deformation up to 19% strain.

  15. Shape memory materials

    Institute of Scientific and Technical Information of China (English)

    2001-01-01

    Compared with piezoelectric ceramics and magnetostrictive materials, the shape memory materials possess larger recoverable strain and recovery stress but slower response to external field. It is expected that the magneto-shape memory materials may develop considerable strain as well as rapid and precise shape control. Pseudoelasticity and shape memory effect (SME) resulted from martensitic transformation and its reverse transformation in shape memory materials were generally described. The requirements of appearing the shape memory effect in materials and the criteria for thermoelastic martensitic transformation were given. Some aspects concerning characteristics of martensitic transformation, and factors affecting SME in Ni-Ti, Cu-Zn-Al and Fe-Mn-Si based alloys as well as ZrO2 containing ceramics were briefly reviewed. Thermodynamic calculation of Ms temperature as function of grain size and parent ordering in Cu-Zn-Al was presented. The works on prediction of Ms in Fe-Mn-Si based alloys and in ZrO2-CeO2 were mentioned. Magnetic shape memory materials were briefly introduced.

  16. Development of a Nano-Satellite Micro-Coupling Mechanism with Characterization of a Shape Memory Alloy Interference Joint

    Science.gov (United States)

    2010-12-01

    for the softer martensitic phase was greater than that of the harder austenite phase [8]. When comparing NiTi to stainless steel 304 for resistance...interference joint, consisting of a detwinned martensitic NiTi SMA ring and stainless steel hub, could obtain sufficient axial coupling strength to...titanium (NiTi), shape memory alloy (SMA) cylindrical ring that is press-fit, in its detwinned martensitic phase, into a steel bushing, creating an

  17. Understanding the shape-memory alloys used in orthodontics.

    Science.gov (United States)

    Fernandes, Daniel J; Peres, Rafael V; Mendes, Alvaro M; Elias, Carlos N

    2011-01-01

    Nickel-titanium (NiTi) shape-memory alloys (SMAs) have been used in the manufacture of orthodontic wires due to their shape memory properties, super-elasticity, high ductility, and resistance to corrosion. SMAs have greater strength and lower modulus of elasticity when compared with stainless steel alloys. The pseudoelastic behavior of NiTi wires means that on unloading they return to their original shape by delivering light continuous forces over a wider range of deformation which is claimed to allow dental displacements. The aim of this paper is to discuss the physical, metallurgical, and mechanical properties of NiTi used in Orthodontics in order to analyze the shape memory properties, super-elasticity, and thermomechanical characteristics of SMA.

  18. Influence of compaction pressure on the morphology and phase evolution of porous NiTi alloy prepared by SHS technique

    Directory of Open Access Journals (Sweden)

    Sirikul Wisutmethangoon

    2008-08-01

    Full Text Available The influence of compaction pressure on the pore morphology of porous NiTi shape memory alloys (SMAs fabricated by self-propagating high-temperature synthesis (SHS was investigated. The compaction pressure has a significant effect on the combustion temperature and pore morphology. The porous NiTi (SMAs thus obtained have the porosity of product in the range of 37.4-57.9 vol.%. The open porosity ratios were observed to be greater than 88%, which indicatesthat porous NiTi (SMAs are suitable for biomedical applications. In addition, the predominant phases in the porous product are B2(NiTi and B19’(NiTi with small amounts of secondary phases, NiTi2 and Ni4Ti3.

  19. The Effect of Particles Shape and Size on Feedstock Flowibility and Chemical content of As-sintered NiTi Alloys

    Science.gov (United States)

    Kadir, R. A. Abdul; Razali, R.; Mohamad Nor, N. H.; Subuki, I.; Ismail, M. H.

    2018-05-01

    This paper presents a comparative study of two different titanium powders in fabrication of NiTi alloys by metal injection moulding (MIM) route. Two batches of powder mixture consisted of Ni-Ti and Ni-TiH2 with atomic ratio (at%) of 50-50 were prepared. TiH2 powder was used as a substitution for pure Ti powder owing to its relatively cheaper cost and has been claimed favourable in producing less impurity uptake in sintering process. The binder system used for both mixtures comprised of composite binder of palm stearin (PS) and polyethylene (PE) at weigth ratio (wt%) of 60-40. The flow behaviour of the mixtures was analysed using a capillary rheometer at different shear rates and temperatures. The results showed that owing to irregular shape of TiH2 compared to Ti powder, the viscosity of the feedstock was significantly higher, thus required greater temperature in order to improve the mouldability of the feedstock. Nevertheless, both feedstocks exhibited pseudoplastic, a shear thinning behavior with shear rate and temperature, desirable properties for injection moulding process. Samples prepared with Ni-Ti feedstock were sintered in a high vacuum furnace, while Ni-TiH2 feedstock was sintered in a tube furnace under a flowing of Argon gas. The results showed that the impurity contents (Carbon and Oxygen) for both feedstocks were almost comparable, suggesting NiTi alloy samples prepared with TiH2 powder is an attractive route for manufacturing of NiTi alloys.

  20. Microstructure, mechanical properties and superelasticity of biomedical porous NiTi alloy prepared by microwave sintering.

    Science.gov (United States)

    Xu, J L; Bao, L Z; Liu, A H; Jin, X J; Tong, Y X; Luo, J M; Zhong, Z C; Zheng, Y F

    2015-01-01

    Porous NiTi alloys were prepared by microwave sintering using ammonium hydrogen carbonate (NH4HCO3) as the space holder agent to adjust the porosity in the range of 22-62%. The effects of porosities on the microstructure, hardness, compressive strength, bending strength, elastic modulus, phase transformation temperature and superelasticity of the porous NiTi alloys were investigated. The results showed that the porosities and average pore sizes of the porous NiTi alloys increased with increasing the contents of NH4HCO3. The porous NiTi alloys consisted of nearly single NiTi phase, with a very small amount of two secondary phases (Ni3Ti, NiTi2) when the porosities are lower than 50%. The amount of Ni3Ti and NiTi2 phases increased with further increasing of the porosity proportion. The porosities had few effects on the phase transformation temperatures of the porous NiTi alloys. By increasing the porosities, all of the hardness, compressive strength, elastic modulus, bending strength and superelasticity of the porous NiTi alloys decreased. However, the compressive strength and bending strength were higher or close to those of natural bone and the elastic modulus was close to the natural bone. The superelastic recovery strain of the trained porous NiTi alloys could reach between 3.1 and 4.7% at the pre-strain of 5%, even if the porosity was up to 62%. Moreover, partial shape memory effect was observed for all porosity levels under the experiment conditions. Therefore, the microwave sintered porous NiTi alloys could be a promising candidate for bone implant. Copyright © 2014 Elsevier B.V. All rights reserved.

  1. Mechanical and shape memory properties of porous Ni50.1Ti49.9 alloys manufactured by selective laser melting.

    Science.gov (United States)

    Taheri Andani, Mohsen; Saedi, Soheil; Turabi, Ali Sadi; Karamooz, M R; Haberland, Christoph; Karaca, Haluk Ersin; Elahinia, Mohammad

    2017-04-01

    Near equiatomic NiTi shape memory alloys were fabricated in dense and designed porous forms by Selective Laser Melting (SLM) and their mechanical and shape memory properties were systematically characterized. Particularly, the effects of pore morphology on their mechanical responses were investigated. Dense and porous NiTi alloys exhibited good shape memory effect with a recoverable strain of about 5% and functional stability after eight cycles of compression. The stiffness and residual plastic strain of porous NiTi were found to depend highly on the pore shape and the level of porosity. Since porous NiTi structures have lower elastic modulus and density than dense NiTi with still good shape memory properties, they are promising materials for lightweight structures, energy absorbers, and biomedical implants. Copyright © 2017 Elsevier Ltd. All rights reserved.

  2. Comparative study of root-canal shaping with stainless steel and rotary NiTi files performed by preclinical dental students.

    Science.gov (United States)

    Alrahabi, Mothanna

    2015-01-01

    We evaluated the use of NiTi rotary and stainless steel endodontic instruments for canal shaping by undergraduate students. We also assessed the quality of root canal preparation as well as the occurrence of iatrogenic events during instrumentation. In total, 30 third-year dental students attending Taibah University Dental College prepared 180 simulated canals in resin blocks with NiTi rotary instruments and stainless steel hand files. Superimposed images were prepared to measure the removal of material at different levels from apical termination using the GSA image analysis software. Preparation time, procedural accidents, and canal shape after preparation were analyzed using χ 2 and t-tests. The statistical significance level was set at P instruments and stainless steel files; the former was associated with shorter preparation time, less ledge formation (1.1% vs. 14.4%), and greater instrument fracture (5.56% vs. 1.1%). These results indicate that NiTi rotary instruments result in better canal geometry and cause less canal transportation. Manual instrumentation using stainless steel files is safer than rotary instrumentation for inexperienced students. Intensive preclinical training is a prerequisite for using NiTi rotary instruments. These results prompted us to reconsider theoretical and practical coursework when teaching endodontics.

  3. In Vitro Corrosion Assessment of Additively Manufactured Porous NiTi Structures for Bone Fixation Applications

    Directory of Open Access Journals (Sweden)

    Hamdy Ibrahim

    2018-03-01

    Full Text Available NiTi alloys possess distinct functional properties (i.e., shape memory effect and superelasticity and biocompatibility, making them appealing for bone fixation applications. Additive manufacturing offers an alternative method for fabricating NiTi parts, which are known to be very difficult to machine using conventional manufacturing methods. However, poor surface quality, and the presence of impurities and defects, are some of the major concerns associated with NiTi structures manufactured using additive manufacturing. The aim of this study is to assess the in vitro corrosion properties of additively manufactured NiTi structures. NiTi samples (bulk and porous were produced using selective laser melting (SLM, and their electrochemical corrosion characteristics and Ni ion release levels were measured and compared with conventionally fabricated NiTi parts. The additively manufactured NiTi structures were found to have electrochemical corrosion characteristics similar to those found for the conventionally fabricated NiTi alloy samples. The highest Ni ion release level was found in the case of 50% porous structures, which can be attributed to their significantly higher exposed surface area. However, the Ni ion release levels reported in this work for all the fabricated structures remain within the range of most of values for conventionally fabricated NiTi alloys reported in the literature. The results of this study suggest that the proposed SLM fabrication process does not result in a significant deterioration in the corrosion resistance of NiTi parts, making them suitable for bone fixation applications.

  4. Laser Annealing on the Surface Treatment of Thin Super Elastic NiTi Wire

    Science.gov (United States)

    Samal, S.; Heller, L.; Brajer, J.; Tyc, O.; Kadrevek, L.; Sittner, P.

    2018-05-01

    Here the aim of this research is annealing the surface of NiTi wire for shape memory alloy, super-elastic wire by solid state laser beam. The laser surface treatment was carried out on the NiTi wire locally with fast, selective, surface heat treatment that enables precisely tune the localized material properties without any precipitation. Both as drawn (hard) and straight annealing NiTi wire were considered for laser annealing with input power 3 W, with precisely focusing the laser beam height 14.3 % of the Z-axis with a spot size of 1 mm. However, straight annealing wire is more interest due to its low temperature shape setting behavior and used by companies for stent materials. The variable parameter such as speed of the laser scanning and tensile stress on the NiTi wire were optimized to observe the effect of laser response on the sample. Superelastic, straight annealed NiTi wires (d: 0.10 mm) were held prestrained at the end of the superelastic plateau (ε: 5 ∼6.5 %) above the superelastic region by a tensile machine ( Mitter: miniature testing rig) at room temperature (RT). Simultaneously, the hardness of the wires along the cross-section was performed by nano-indentation (NI) method. The hardness of the NiTi wire corresponds to phase changes were correlated with NI test. The laser induced NiTi wire shows better fatigue performance with improved 6500 cycles.

  5. Laser Welding of Shape Memory Alloys

    Science.gov (United States)

    Oliveira, Joao Pedro de Sousa

    Joining of shape memory alloys is of great importance for both functional and structural applications as it can provide an increased design flexibility. In this work similar NiTi/NiTi, CuAlMn/CuAlMn and dissimilar NiTi/Ti6Al4V joints were produced by Nd:YAG laser. For the NiTi/NiTi joints the effect of process parameters (namely the heat input) on the superelastic and shape memory effects of the joints was assessed and correlated to its microstructure. Microstructural analysis was performed by means of X-ray diffraction using synchrotron radiation, which allowed for fine probing of the welded material. It was noticed the presence of martensite in the thermally affected regions, while the base material remained fully austenitic. The mechanisms for the formation of martensite, at room temperature, due to the welding procedure are presented and the influence of this phase on the functional properties of the joints is discussed. Additionally, the residual stresses were determined using synchrotron X-ray diffraction. For the dissimilar NiTi/Ti6Al4V joints, a Niobium interlayer was used to prevent the formation undesired brittle intermetallic compounds. Additionally, it was observed that positioning of the laser beam was of significant importance to obtain a sound joint. The mechanisms responsible for the joint formation are discussed based on observations with advanced characterization techniques, such as transmission electron microscopy. At the NiTi/Nb interface, an eutectic reaction promotes joining of the two materials, while at the Ti6Al4V/Nb interface fusion and, subsequent solidification of the Ti6Al4V was responsible for joining. Short distance diffusion of Nb to the fusion zone of Ti6Al4V was observed. Although fracture of the dissimilar welded joints occurred at a stress lower than the minimum required for the stress induced transformation, an improvement on the microstructure and mechanical properties, relatively to existing literature, was obtained. Finally

  6. Characterization of constrained aged Ni Ti strips for using in artificial muscle actuators

    International Nuclear Information System (INIS)

    Hassanzadeh Nemati, N.; Sadrnezhaad, S. K.

    2011-01-01

    Marvelous bending/straightening effects of two-way shape memory alloy help their employment in design and manufacturing of new medical appliances. Constrained ageing with bending load scheme can induce two-way shape memory effect. Scanning electron microscopic analysis, electrical resistivity measurement and differential scanning calorimetry are employed to determine the property change due to flat strip constrained aging. Results show that flat-annealing prior to the aging shifts Ni Ti transformations temperatures to higher values. Super elastic behavior of the as-received/flat-annealed/aged samples with more adequate transition temperatures due to biological tissue replacement is studied by three-point flexural tests. Results show that curing changes the transition points of the Ni Ti strips. These changes affect the shape memory behavior of the Ni Ti strips embedded within the biocompatible flexible composite segments.

  7. Cyclic fatigue resistances of Hyflex EDM, WaveOne gold, Reciproc blue and 2shape NiTi rotary files in different artificial canals.

    Science.gov (United States)

    Özyürek, Taha; Gündoğar, Mustafa; Uslu, Gülşah; Yılmaz, Koray; Staffoli, Simone; Nm, Grande; Plotino, Gianluca; Polimeni, Antonella

    2018-01-30

    The aim of the present study was to compare the cyclic fatigue resistances of HyFlex EDM (HEDM), WaveOne Gold (WOG), Reciproc Blue (RB), and 2Shape (TS) NiTi systems having different metallurgic properties. HEDM, WOG, RB, and TS instruments were rotated in artificial canals which were made of stainless steel with an inner diameter of 1.5 mm, 45°, and 90° angles of curvatures and a radius of curvature of 5 mm until fracture occurred, and the time to fracture (TTF) was recorded in seconds. Also, number of cycles to fracture was calculated (NCF). Data were statistically analyzed using Kruskal-Wallis and t test. The statistical significance level was set at P  0.05). When the NCF values were taken into consideration, HEDM reported a significantly higher cyclic fatigue resistance than TS in both canal curvatures analyzed (P < 0.05). Within the limitations of the present study, RB NiTi files showed statistically higher cyclic fatigue resistance in artificial canals with 45° and 90° than the other NiTi files tested.

  8. Shape memory thermal conduction switch

    Science.gov (United States)

    Vaidyanathan, Rajan (Inventor); Krishnan, Vinu (Inventor); Notardonato, William U. (Inventor)

    2010-01-01

    A thermal conduction switch includes a thermally-conductive first member having a first thermal contacting structure for securing the first member as a stationary member to a thermally regulated body or a body requiring thermal regulation. A movable thermally-conductive second member has a second thermal contacting surface. A thermally conductive coupler is interposed between the first member and the second member for thermally coupling the first member to the second member. At least one control spring is coupled between the first member and the second member. The control spring includes a NiTiFe comprising shape memory (SM) material that provides a phase change temperature <273 K, a transformation range <40 K, and a hysteresis of <10 K. A bias spring is between the first member and the second member. At the phase change the switch provides a distance change (displacement) between first and second member by at least 1 mm, such as 2 to 4 mm.

  9. Corrosion of NiTi wires with cracked oxide layer

    Czech Academy of Sciences Publication Activity Database

    Racek, Jan; Šittner, Petr; Heller, Luděk; Pilch, Jan; Petrenec, M.; Sedlák, Petr

    2014-01-01

    Roč. 23, č. 7 (2014), s. 2659-2668 ISSN 1059-9495. [International Conference on Shape Memory and Superelastic Technologies (SMST 2013). Praha, 21.05.2013-24.05.2013] R&D Projects: GA ČR GPP108/12/P111; GA ČR GAP107/12/0800; GA MŠk(CZ) 7E11058 EU Projects: European Commission(XE) 262806 - SmartNets Institutional support: RVO:68378271 ; RVO:61388998 Keywords : bending * electrochemical corrosion tests * martensitic transformation * shape memory alloy * superelastic NiTi wires Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.998, year: 2014

  10. Modeling of NiTiHf using finite difference method

    Science.gov (United States)

    Farjam, Nazanin; Mehrabi, Reza; Karaca, Haluk; Mirzaeifar, Reza; Elahinia, Mohammad

    2018-03-01

    NiTiHf is a high temperature and high strength shape memory alloy with transformation temperatures above 100oC. A constitutive model based on Gibbs free energy is developed to predict the behavior of this material. Two different irrecoverable strains including transformation induced plastic strain (TRIP) and viscoplastic strain (VP) are considered when using high temperature shape memory alloys (HTSMAs). The first one happens during transformation at high levels of stress and the second one is related to the creep which is rate-dependent. The developed model is implemented for NiTiHf under uniaxial loading. Finite difference method is utilized to solve the proposed equations. The material parameters in the equations are calibrated from experimental data. Simulation results are captured to investigate the superelastic behavior of NiTiHf. The extracted results are compared with experimental tests of isobaric heating and cooling at different levels of stress and also superelastic tests at different levels of temperature. More results are generated to investigate the capability of the proposed model in the prediction of the irrecoverable strain after full transformation in HTSMAs.

  11. NiTi bonded space regainer/maintainer

    Directory of Open Access Journals (Sweden)

    Negi K

    2010-06-01

    Full Text Available Early orthodontic interventions are often initiated in the developing dentition to promote favorable developmental changes. Interceptive orthodontic can eliminate or reduce the severity of a developing malocclusion, the complexity of orthodontic treatment, overall treatment time and cost. Premature loss of deciduous tooth or teeth can often destroy the integrity of normal occlusion. There are many space regaining and maintaining devices mentioned in literature. In this article, I present a simple space regaining method by a piece of nickel titanium (NiTi wire bonded between the teeth in active loop form, and the unique shape memory property of NiTi wire will upright or move the teeth and the lost space can be regained easily.

  12. Pseudo-creep in Shape Memory Alloy Wires and Sheets

    Science.gov (United States)

    Russalian, V. R.; Bhattacharyya, A.

    2017-10-01

    Interruption of loading during reorientation and isothermal pseudoelasticity in shape memory alloys with a strain arrest ( i.e., holding strain constant) results in a time-dependent evolution in stress or with a stress arrest ( i.e., holding stress constant) results in a time-dependent evolution in strain. This phenomenon, which we term as pseudo-creep, is similar to what was reported in the literature three decades ago for some traditional metallic materials undergoing plastic deformation. In a previous communication, we reported strain arrest of isothermal pseudoelastic loading, isothermal pseudoelastic unloading, and reorientation in NiTi wires as well as a rate-independent phase diagram. In this paper, we provide experimental results of the pseudo-creep phenomenon during stress arrest of isothermal pseudoelasticity and reorientation in NiTi wires as well as strain arrest of isothermal pseudoelasticity and reorientation in NiTi sheets. Stress arrest in NiTi wires accompanied by strain accumulation or recovery is studied using the technique of multi-video extensometry. The experimental results were used to estimate the amount of mechanical energy needed to evolve the wire from one microstructural state to another during isothermal pseudoelastic deformation and the difference in energies between the initial and the final rest state between which the aforementioned evolution has occurred.

  13. Cutting NiTi with Femtosecond Laser

    Directory of Open Access Journals (Sweden)

    L. Quintino

    2013-01-01

    Full Text Available Superelastic shape memory alloys are difficult to machine by thermal processes due to the facility for Ti oxidation and by mechanical processes due to their superelastic behavior. In this study, femtosecond lasers were tested to analyze the potential for machining NiTi since femtosecond lasers allow nonthermal processing of materials by ablation. The effect of processing parameters on machining depth was studied, and material removal rates were computed. Surfaces produced were analyzed under SEM which shows a resolidified thin layer with minimal heat affected zones. However, for high cutting speeds, that is, for short interaction times, this layer was not observed. A depletion of Ni was seen which may be beneficial in biomedical applications since Ni is known to produce human tissue reactions in biophysical environments.

  14. Effect of pre-strain on microstructure of Ni-Ti orthodontic archwires

    Energy Technology Data Exchange (ETDEWEB)

    Jafari, J. [Department of Materials Science and Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Azadi Square, P.O. Box 91775-1111, Mashhad (Iran, Islamic Republic of); Zebarjad, S.M. [Department of Materials Science and Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Azadi Square, P.O. Box 91775-1111, Mashhad (Iran, Islamic Republic of)], E-mail: Zebarjad@um.ac.ir; Sajjadi, S.A. [Department of Materials Science and Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Azadi Square, P.O. Box 91775-1111, Mashhad (Iran, Islamic Republic of)

    2008-01-25

    One of the most important applications of shape memory alloy is in medicine, especially orthodontic archwires. In this category Ni-Ti orthodontic archwires is one of the oldest used materials. Biocompatibility, corrosion resistance, super elasticity, etc. are its outstanding properties. In spite of the importance of dependency of pre-strain on microstructure of Ni-Ti there are limited sources concentrated on the subject. For this reason the main purpose of the current study is determination of the effect of pre-strain on microstructure of Ni-Ti orthodontic archwires. In this regard, three-point bending was performed on the orthodontic archwire specimens to apply different amount of strain. The microstructures were compared with the un-strained wire using optical and scanning electron microscopes. The results showed that the stable phase depends strongly on the value of pre-strain. Increasing pre-strain causes to decrease martensite laths and leads the microstructure toward austenite phase.

  15. Effect of pre-strain on microstructure of Ni-Ti orthodontic archwires

    International Nuclear Information System (INIS)

    Jafari, J.; Zebarjad, S.M.; Sajjadi, S.A.

    2008-01-01

    One of the most important applications of shape memory alloy is in medicine, especially orthodontic archwires. In this category Ni-Ti orthodontic archwires is one of the oldest used materials. Biocompatibility, corrosion resistance, super elasticity, etc. are its outstanding properties. In spite of the importance of dependency of pre-strain on microstructure of Ni-Ti there are limited sources concentrated on the subject. For this reason the main purpose of the current study is determination of the effect of pre-strain on microstructure of Ni-Ti orthodontic archwires. In this regard, three-point bending was performed on the orthodontic archwire specimens to apply different amount of strain. The microstructures were compared with the un-strained wire using optical and scanning electron microscopes. The results showed that the stable phase depends strongly on the value of pre-strain. Increasing pre-strain causes to decrease martensite laths and leads the microstructure toward austenite phase

  16. Tungsten inert gas (TIG) welding of Ni-rich NiTi plates: functional behavior

    Science.gov (United States)

    Oliveira, J. P.; Barbosa, D.; Braz Fernandes, F. M.; Miranda, R. M.

    2016-03-01

    It is often reported that, to successfully join NiTi shape memory alloys, fusion-based processes with reduced thermal affected regions (as in laser welding) are required. This paper describes an experimental study performed on the tungsten inert gas (TIG) welding of 1.5 mm thick plates of Ni-rich NiTi. The functional behavior of the joints was assessed. The superelasticity was analyzed by cycling tests at maximum imposed strains of 4, 8 and 12% and for a total of 600 cycles, without rupture. The superelastic plateau was observed, in the stress-strain curves, 30 MPa below that of the base material. Shape-memory effect was evidenced by bending tests with full recovery of the initial shape of the welded joints. In parallel, uniaxial tensile tests of the joints showed a tensile strength of 700 MPa and an elongation to rupture of 20%. The elongation is the highest reported for fusion-welding of NiTi, including laser welding. These results can be of great interest for the wide-spread inclusion of NiTi in complex shaped components requiring welding, since TIG is not an expensive process and is simple to operate and implement in industrial environments.

  17. Behaviour of smart reinforced concrete beam with super elastic shape memory alloy subjected to monotonic loading

    Science.gov (United States)

    Hamid, Nubailah Abd; Ibrahim, Azmi; Adnan, Azlan; Ismail, Muhammad Hussain

    2018-05-01

    This paper discusses the superelastic behavior of shape memory alloy, NiTi when used as reinforcement in concrete beams. The ability of NiTi to recover and reduce permanent deformations of concrete beams was investigated. Small-scale concrete beams, with NiTi reinforcement were experimentally investigated under monotonic loads. The behaviour of simply supported reinforced concrete (RC) beams hybrid with NiTi rebars and the control beam subject to monotonic loads were experimentally investigated. This paper is to highlight the ability of the SMA bars to recover and reduce permanent deformations of concrete flexural members. The size of the control beam is 125 mm × 270 mm × 1000 mm with 3 numbers of 12 mm diameter bars as main reinforcement for compression and 3 numbers of 12 mm bars as tension or hanger bars while 6 mm diameter at 100 mm c/c used as shear reinforcement bars for control beam respectively. While, the minimal provision of 200mm using the 12.7mm of superelastic Shape Memory Alloys were employed to replace the steel rebar at the critical region of the beam. In conclusion, the contribution of the SMA bar in combination with high-strength steel to the conventional reinforcement showed that the SMA beam has exhibited an improve performance in term of better crack recovery and deformation. Therefore the usage of hybrid NiTi with the steel can substantially diminish the risk of the earthquake and also can reduce the associated cost aftermath.

  18. Comparing the cyclic behavior of concrete cylinders confined by shape memory alloy wire or steel jackets

    International Nuclear Information System (INIS)

    Park, Joonam; Choi, Eunsoo; Kim, Hong-Taek; Park, Kyoungsoo

    2011-01-01

    Shape memory alloy (SMA) wire jackets for concrete are distinct from conventional jackets of steel or fiber reinforced polymer (FRP) since they provide active confinement which can be easily achieved due to the shape memory effect of SMAs. This study uses NiTiNb SMA wires of 1.0 mm diameter to confine concrete cylinders with the dimensions of 300 mm × 150 mm (L × D). The NiTiNb SMAs have a relatively wider temperature hysteresis than NiTi SMAs; thus, they are more suitable for the severe temperature-variation environments to which civil structures are exposed. Steel jackets of passive confinement are also prepared in order to compare the cyclic behavior of actively and passively confined concrete cylinders. For this purpose, monotonic and cyclic compressive loading tests are conducted to obtain axial and circumferential strain. Both strains are used to estimate the volumetric strains of concrete cylinders. Plastic strains from cyclic behavior are also estimated. For the cylinders jacketed by NiTiNb SMA wires, the monotonic axial behavior differs from the envelope of cyclic behavior. The plastic strains of the actively confined concrete show a similar trend to those of passive confinement. This study proposed plastic strain models for concrete confined by SMA wire or steel jackets. For the volumetric strain, the active jackets of NiTiNb SMA wires provide more energy dissipation than the passive jacket of steel

  19. A comparative study of the cytotoxicity and corrosion resistance of nickel-titanium and titanium-niobium shape memory alloys.

    Science.gov (United States)

    McMahon, Rebecca E; Ma, Ji; Verkhoturov, Stanislav V; Munoz-Pinto, Dany; Karaman, Ibrahim; Rubitschek, Felix; Maier, Hans J; Hahn, Mariah S

    2012-07-01

    Nickel-titanium (NiTi) shape memory alloys (SMAs) are commonly used in a range of biomedical applications. However, concerns exist regarding their use in certain biomedical scenarios due to the known toxicity of Ni and conflicting reports of NiTi corrosion resistance, particularly under dynamic loading. Titanium-niobium (TiNb) SMAs have recently been proposed as an alternative to NiTi SMAs due to the biocompatibility of both constituents, the ability of both Ti and Nb to form protective surface oxides, and their superior workability. However, several properties critical to the use of TiNb SMAs in biomedical applications have not been systematically explored in comparison with NiTi SMAs. These properties include cytocompatibility, corrosion resistance, and alterations in alloy surface composition in response to prolonged exposure to physiological solutions. Therefore, the goal of the present work was to comparatively investigate these aspects of NiTi (49.2 at.% Ti) and TiNb (26 at.% Nb) SMAs. The results from the current studies indicate that TiNb SMAs are less cytotoxic than NiTi SMAs, at least under static culture conditions. This increased TiNb cytocompatibility was correlated with reduced ion release as well as with increased corrosion resistance according to potentio-dynamic tests. Measurements of the surface composition of samples exposed to cell culture medium further supported the reduced ion release observed from TiNb relative to NiTi SMAs. Alloy composition depth profiles also suggested the formation of calcium phosphate deposits within the surface oxide layers of medium-exposed NiTi but not of TiNb. Collectively, the present results indicate that TiNb SMAs may be promising alternatives to NiTi for certain biomedical applications. Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  20. A study on poly (N-vinyl-2-pyrrolidone covalently bonded NiTi surface for inhibiting protein adsorption

    Directory of Open Access Journals (Sweden)

    Hongyan Yu

    2016-12-01

    Full Text Available Near equiatomic NiTi alloys have been extensively applied as biomaterials owing to its unique shape memory effect, superelasticity and biocompatibility. It has been demonstrated that surfaces capable of preventing plasma protein adsorption could reduce the reactivity of biomaterials with human blood. This motivated a lot of researches on the surface modification of NiTi alloy. In the present work, following heat and alkaline treatment and silanization by trichlorovinylsilane (TCVS, coating of poly (N-vinyl-2-pyrrolidone (PVP was produced on the NiTi alloy by gamma ray induced chemical bonding. The structures and properties of modified NiTi were characterized and in vitro biocompatibility of plasma protein adsorption was investigated. The results indicated that heat treatment at 823 K for 1 h could result in the formation of a protective TiO2 layer with “Ni-free” zone on NiTi surface. It was found that PVP was covalently bonded on NiTi surface to create a hydrophilic layer for inhibiting protein adsorption on the surface. The present work offers a green approach to introduce a bioorganic surface on metal and other polymeric or inorganic substrates by gamma irradiation.

  1. Finite element simulations of internal stresses generated during the ferroelastic deformation of NiTi bodies

    International Nuclear Information System (INIS)

    Manach, P.Y.; Favier, D.; Rio, G.

    1996-01-01

    The aim of this paper is to analyse the generation of internal stresses during the predeformation of NiTi shape memory alloys in the martensitic state. This allows to determine the initial stress state in which the material will transform during the shape memory effect due to heating consecutively to this prestrain. In that way a three-dimensional finite element model of the deformation of shape memory alloys has been developed, the constitutive law being defined using an elastohysteresis tensor model. The influence of behavioural and geometrical factors are illustrated considering the numerical simulation of different cases of practical importance for industrial applications : the study of the bending behaviour of a NiTi cantilever beam as well as the study of the swelling of a pipe connection under both uniform and non uniform internal displacement fields. (orig.)

  2. Neutron irradiation effect on thermomechanical properties of shape memory alloys

    International Nuclear Information System (INIS)

    Abramov, V.Ya.; Ionajtis, R.R.; Kotov, V.V.; Loguntsev, E.N.; Ushakov, V.P.

    1996-01-01

    Alloys of Ti-Ni, Ti-Ni-Pd, Fe-Mn-Si, Mn-Cu-Cr, Mn-Cu, Cu-Al-Mn, Cu-Al-Ni systems are investigated after irradiation in IVV-2M reactor at various temperatures with neutron fluence of 10 19 - 10 20 cm -2 . The degradation of shape memory effect in titanium nickelide base alloys is revealed after irradiation. Mn-Cu and Mn-Cu-Cr alloys show the best results. Trends in shape memory alloy behaviour depending on irradiation temperature are found. A consideration is given to the possibility of using these alloys for components of power reactor control and protection systems [ru

  3. Martensitic phase transformations in Ni–Ti-based shape memory alloys: The Landau theory

    International Nuclear Information System (INIS)

    Shchyglo, Oleg; Salman, Umut; Finel, Alphonse

    2012-01-01

    We present a simple Landau free energy functional for cubic-to-orthorhombic and cubic-to-monoclinic martensitic phase transformations. The functional is derived following group–subgroup relations between different martensitic phases – tetragonal, trigonal, orthorhombic and monoclinic – in order to fully capture the symmetry properties of the free energy of the austenite and martensite phases. The derived free energy functional is fitted to the elastic and thermodynamic properties of NiTi and NiTiCu shape memory alloys which exhibit cubic-to-monoclinic and cubic-to-orthorhombic martensitic phase transformations, respectively.

  4. Stress Relaxation Of Superelastic Shape Memory Alloy Under Bending And Torsional Load

    Directory of Open Access Journals (Sweden)

    Sakib Tanvir

    2017-04-01

    Full Text Available Stress Relaxation of Superelastic Shape memory NiTi Alloy under bending and torsion is uncommon in literature. Therefore experimental set up has been devised and test results are obtained for superelastic SMA.Unlike the other common engineering materials superelastic SMA it gives dramatic reduction in stress. In this paper therefore results of stress relaxation of superelastic shape memory alloy under bending and torsion are presented graphically and interpreted in terms of stress induced martensitic transformation.

  5. Shape Memory Alloys (Part II: Classification, Production and Application

    Directory of Open Access Journals (Sweden)

    I. Ivanic

    2014-09-01

    Full Text Available Shape memory alloys (SMAs have been extensively investigated because of their unique shape memory behaviour, i.e. their ability to recover their original shape they had before deformation. Shape memory effect is related to the thermoelastic martensitic transformation. Austenite to martensite phase transformation can be obtained by mechanical (loading and thermal methods (heating and cooling. Depending on thermomechanical conditions, SMAs demonstrate several thermomechanical phenomena, such as pseudoelasticity, superelasticity, shape memory effect (one-way and two-way and rubber-like behaviour. Numerous alloys show shape memory effect (NiTi-based alloys, Cu-based alloys, Fe-based alloys etc.. Nitinol (NiTi is the most popular and the most commonly used SMA due to its superior thermomechanical and thermoelectrical properties. NiTi alloys have greater shape memory strain and excellent corrosion resistance compared to Cu – based alloys. However, they are very costly. On the other hand, copper-based alloys (CuZn and CuAl based alloys are much less expensive, easier to manufacture and have a wider range of potential transformation temperatures. The characteristic transformation temperatures of martensitic transformation of CuAlNi alloys can lie between −200 and 200 °C, and these temperatures depend on Al and Ni content. Among the Cu – based SMAs, the most frequently applied are CuZnAl and CuAlNi alloys. Although CuZnAl alloys with better mechanical properties are the most popular among the Cu-based SMAs, they lack sufficient thermal stability, while CuAlNi shape memory alloys, in spite of their better thermal stability, have found only limited applications due to insufficient formability owing to the brittle γ2 precipitates. The most important disadvantage of polycrystalline CuAlNi alloys is a small reversible deformation (one-way shape memory effect: up to 4 %; two-way shape memory effect: only approximately 1.5 % due to intergranular

  6. Electromagnetic heating of a shape memory alloy translator

    Science.gov (United States)

    Giroux, E.-A.; Maglione, M.; Gueldry, A.; Mantoux, J.-L.

    1996-03-01

    The active part of a linear translator is a shape memory alloy (SMA) made of nickel and titanium (NiTi) wire which is to be thermally cycled. We have achieved heating using electromagnetic radiation with a magnetic sheath and low-frequency waves at 8 kHz and without magnetic sheath and radio frequency waves at 28 MHz. The heating is equivalent for these two arrangements. In vitro experiments have been confirmed by computer simulations of the radiation distribution within the implant. We thus show that electromagnetic radiation could specifically heat a NiTi wire inside a stainless steel tube without heating the tube. An application could be a femoral prosthesis for the lengthening of the bone.

  7. Effect of particle size of titanium and nickel on the synthesis of NiTi by TE-SHS

    Czech Academy of Sciences Publication Activity Database

    Novák, P.; Veselý, T.; Marek, I.; Dvořák, P.; Vojtěch, V.; Salvetr, P.; Karlík, M.; Haušild, P.; Kopeček, Jaromír

    2016-01-01

    Roč. 47, č. 2 (2016), s. 932-938 ISSN 1073-5615 R&D Projects: GA ČR(CZ) GA14-03044S Institutional support: RVO:68378271 Keywords : shape memory alloys * behavior * NiTi Subject RIV: JG - Metallurgy Impact factor: 1.642, year: 2016

  8. In situ neutron diffraction studies of martensitic transformations in NiTi polycrystals under tension and compression stress

    Czech Academy of Sciences Publication Activity Database

    Šittner, Petr; Lukáš, Petr; Novák, Václav; Daymond, M. R.; Swallowe, G. M.

    2004-01-01

    Roč. 378, - (2004), s. 97-104 ISSN 0921-5093 Institutional research plan: CEZ:AV0Z1010914 Keywords : martensitic transformation * shape memory alloy * neutron diffraction * NiTi Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.445, year: 2004

  9. Effect of titanium content and cooling rate on the microstructure and martensitic transformation of rapidly solidified Ti-Ni shape memory alloys; Influencia do Ti e da taxa de resfriamento na microestrutura e na temperatura M{sub S} em ligas Ni-Ti com EMF solidificadas rapidamente

    Energy Technology Data Exchange (ETDEWEB)

    Anselmo, George Carlos dos Santos; Castro, Walman Benicio de, E-mail: georgeanselmo@yahoo.com.br, E-mail: walman.castro@ufcg.edu.br [Universidade Federal de Campina Grande (UFCG), PB (Brazil)

    2017-01-15

    One important challenge of microsystems design is the implementation of efficient principles of miniaturized actuation at the micro-scale. Shape memory alloys (SMAs) have early been considered as a potential solution to this problem as these materials offer attractive properties like a high-power to weight ratio, large deformation and the capability to be micro-scale processed. Alloys of composition Ni-44,8wt%Ti and Ni- 45,3wt%Ti were produced using the melt spinning method in air atmosphere. Ribbons obtained in this process showed martensitic grain size between 5 and 30 μm, depending on the alloy composition and the linear velocity of the wheel. (author)

  10. Dynamic actuation of a novel laser-processed NiTi linear actuator

    International Nuclear Information System (INIS)

    Pequegnat, A; Daly, M; Wang, J; Zhou, Y; Khan, M I

    2012-01-01

    A novel laser processing technique, capable of locally modifying the shape memory effect, was applied to enhance the functionality of a NiTi linear actuator. By altering local transformation temperatures, an additional memory was imparted into a monolithic NiTi wire to enable dynamic actuation via controlled resistive heating. Characterizations of the actuator load, displacement and cyclic properties were conducted using a custom-built spring-biased test set-up. Monotonic tensile testing was also implemented to characterize the deformation behaviour of the martensite phase. Observed differences in the deformation behaviour of laser-processed material were found to affect the magnitude of the active strain. Furthermore, residual strain during cyclic actuation testing was found to stabilize after 150 cycles while the recoverable strain remained constant. This laser-processed actuator will allow for the realization of new applications and improved control methods for shape memory alloys. (paper)

  11. Additive Manufacturing of Shape Memory Alloys

    Science.gov (United States)

    Van Humbeeck, Jan

    2018-04-01

    Selective Laser Melting (SLM) is an additive manufacturing production process, also called 3D printing, in which functional, complex parts are produced by selectively melting patterns in consecutive layers of powder with a laser beam. The pattern the laser beam is following is controlled by software that calculates the pattern by slicing a 3D CAD model of the part to be constructed. Apart from SLM, also other additive manufacturing techniques such as EBM (Electron Beam Melting), FDM (Fused Deposition Modelling), WAAM (Wire Arc Additive Manufacturing), LENS (Laser Engineered Net Shaping such as Laser Cladding) and binder jetting allow to construct complete parts layer upon layer. But since more experience of AM of shape memory alloys is collected by SLM, this paper will overview the potentials, limits and problems of producing NiTi parts by SLM.

  12. Modeling, Simulation, Additive Manufacturing, and Experimental Evaluation of Solid and Porous NiTi

    Science.gov (United States)

    Taheri Andani, Mohsen

    In recent years, shape memory alloys (SMAs) have entered a wide range of engineering applications in fields such as aerospace and medical applications. Nickel-titanium (NiTi) is the most commonly used SMAs due to its excellent functional characteristics (shape memory effect and superelasticity behavior). These properties are based on a solid-solid phase transformation between martensite and austenite. Beside these two characteristics, low stiffness, biocompatibility and corrosion properties of NiTi make it an attractive candidate for biomedical applications (e.g., bone plates, bone screws, and vascular stents). It is well know that manufacturing and processing of NiTi is very challenging. The functional properties of NiTi are significantly affected by the impurity level and due to the high titanium content, NiTi are highly reactive. Therefore, high temperature processed parts through methods such as melting and casting which result in increased impurity levels have inadequate structural and functional properties. Furthermore, high ductility and elasticity of NiTi, adhesion, work hardening and spring back effects make machining quite challenging. These unfavorable effects for machining cause significant tool wear along with decreasing the quality of work piece. Recently, additive manufacturing (AM) has gained significant attention for manufacturing NiTi. Since AM can create a part directly from CAD data, it is predicted that AM can overcome most of the manufacturing difficulties. This technique provides the possibility of fabricating highly complex parts, which cannot be processed by any other methods. Curved holes, designed porosity, and lattice like structures are some examples of mentioned complex parts. This work investigates manufacturing superelastic NiTi by selective laser melting (SLM) technique (using PXM by Phenix/3D Systems). An extended experimental study is conducted on the effect of subsequent heat treatments with different aging conditions on phase

  13. Influence of SLM on compressive response of NiTi scaffolds

    Science.gov (United States)

    Shayesteh Moghaddam, Narges; Saedi, Soheil; Amerinatanzi, Amirhesam; Jahadakbar, Ahmadreza; Saghaian, Ehsan; Karaca, Haluk; Elahinia, Mohammad

    2018-03-01

    Porous Nickel-Titanium shape memory alloys (NiTi-SMAs) have attracted much attention in biomedical applications due to their high range of pure elastic deformability (i.e., superelasticity) as well as their bone-level modulus of elasticity (E≈12-20 GPa). In recent years, Selective Laser Melting (SLM) has been used to produce complex NiTi components. The focus of this study is to investigate the superelasticity and compressive properties of SLM NiTi-SMAs. To this aim, several NiTi components with different level of porosities (32- 58%) were fabricated from Ni50.8Ti (at. %) powder via SLM PXM by Phenix/3D Systems, using optimum processing parameter (Laser power-P=250 W, scanning speed-v=1250mm/s, hatch spacing-h=120μm, layer thickness-t=30μm). To tailor the superelasticity behavior at body temperature, the samples were solution annealed and aged for 15 min at 350°C. Then, transformation temperatures (TTs), superelastic response, and cyclic behavior of NiTi samples were studied. As the porosity was increased, the irrecoverable strain was observed to be higher in the samples. At the first superelastic cycle, 3.5%, 3.5%, and 2.7% strain recovery were observed for the porosity levels of 32%, 45%, and 58%, respectively. However, after 10 cycles, the superelastic response of the samples was stabilized and full strain recovery was observed. Finally, the modulus of elasticity of dense SLM NiTi was decreased from 47 GPa to 9 GPa in the first cycle by adding 58% porosity.

  14. Shape memory effect and superelasticity of titanium nickelide alloys implanted with high ion doses

    International Nuclear Information System (INIS)

    Pogrebnjak, A D; Bratushka, S N; Beresnev, V M; Levintant-Zayonts, N

    2013-01-01

    The state of the art in ion implantation of superelastic NiTi shape memory alloys is analyzed. Various technological applications of the shape memory effect are outlined. The principles and techiques of ion implantation are described. Specific features of its application for modification of surface layers in surface engineering are considered. Key properties of shape memory alloys and problems in utilization of ion implantation to improve the surface properties of shape memory alloys, such as corrosion resistance, friction coefficient, wear resistance, etc. are discussed. The bibliography includes 162 references

  15. The Characterization of Thin Film Nickel Titanium Shape Memory Alloys

    Science.gov (United States)

    Harris Odum, Nicole Latrice

    Shape memory alloys (SMA) are able to recover their original shape through the appropriate heat or stress exposure after enduring mechanical deformation at a low temperature. Numerous alloy systems have been discovered which produce this unique feature like TiNb, AgCd, NiAl, NiTi, and CuZnAl. Since their discovery, bulk scale SMAs have undergone extensive material property investigations and are employed in real world applications. However, its thin film counterparts have been modestly investigated and applied. Researchers have introduced numerous theoretical microelectromechanical system (MEMS) devices; yet, the research community's overall unfamiliarity with the thin film properties has delayed growth in this area. In addition, it has been difficult to outline efficient thin film processing techniques. In this dissertation, NiTi thin film processing and characterization techniques will be outlined and discussed. NiTi thin films---1 mum thick---were produced using sputter deposition techniques. Substrate bound thin films were deposited to analysis the surface using Scanning Electron Microscopy; the film composition was obtained using Energy Dispersive Spectroscopy; the phases were identified using X-ray diffraction; and the transformation temperatures acquired using resistivity testing. Microfabrication processing and sputter deposition were employed to develop tensile membranes for membrane deflection experimentation to gain insight on the mechanical properties of the thin films. The incorporation of these findings will aid in the movement of SMA microactuation devices from theory to fruition and greatly benefit industries such as medicinal and aeronautical.

  16. Influence of temperature of the short-period heat treatment on mechanical properties of the NiTi alloy

    Directory of Open Access Journals (Sweden)

    Jaroslav Čapek

    2014-01-01

    Full Text Available The equiatomic alloy of nickel and titanium, known as nitinol, possesses unique properties such as superelasticity, pseudoplasticity, shape memory, while maintaining good corrosion resistance and sufficient biocompatibility. Therefore it is used for production of various devices including surgery implants. Heat treatment of nickel-rich NiTi alloys can result in precipitation of nickel-rich phases, which strongly influence tensile and fatigue behaviour of the material.In this work we have studied influence of short-period heat treatment on tensile behaviour and fatigue life of the NiTi (50.9 at. % Ni wire intended for fabrication of surgery stents.

  17. Shape memory polymers

    Energy Technology Data Exchange (ETDEWEB)

    Wilson, Thomas S.; Bearinger, Jane P.

    2017-08-29

    New shape memory polymer compositions, methods for synthesizing new shape memory polymers, and apparatus comprising an actuator and a shape memory polymer wherein the shape memory polymer comprises at least a portion of the actuator. A shape memory polymer comprising a polymer composition which physically forms a network structure wherein the polymer composition has shape-memory behavior and can be formed into a permanent primary shape, re-formed into a stable secondary shape, and controllably actuated to recover the permanent primary shape. Polymers have optimal aliphatic network structures due to minimization of dangling chains by using monomers that are symmetrical and that have matching amine and hydroxl groups providing polymers and polymer foams with clarity, tight (narrow temperature range) single transitions, and high shape recovery and recovery force that are especially useful for implanting in the human body.

  18. Shape memory polymers

    Science.gov (United States)

    Wilson, Thomas S.; Bearinger, Jane P.

    2015-06-09

    New shape memory polymer compositions, methods for synthesizing new shape memory polymers, and apparatus comprising an actuator and a shape memory polymer wherein the shape memory polymer comprises at least a portion of the actuator. A shape memory polymer comprising a polymer composition which physically forms a network structure wherein the polymer composition has shape-memory behavior and can be formed into a permanent primary shape, re-formed into a stable secondary shape, and controllably actuated to recover the permanent primary shape. Polymers have optimal aliphatic network structures due to minimization of dangling chains by using monomers that are symmetrical and that have matching amine and hydroxyl groups providing polymers and polymer foams with clarity, tight (narrow temperature range) single transitions, and high shape recovery and recovery force that are especially useful for implanting in the human body.

  19. Experimental characterization of shape memory alloy actuator cables

    Science.gov (United States)

    Biggs, Daniel B.; Shaw, John A.

    2016-04-01

    Wire rope (or cables) are a fundamental structural element in many engineering applications. Recently, there has been growing interest in stranding NiTi wires into cables to scale up the adaptive properties of NiTi tension elements and to make use of the desirable properties of wire rope. Exploratory experiments were performed to study the actuation behavior of two NiTi shape memory alloy cables and straight monofilament wire of the same material. The specimens were held under various dead loads ranging from 50 MPa to 400 MPa and thermally cycled 25 times from 140°C to 5°C at a rate of 12°C/min. Performance metrics of actuation stroke, residual strain, and work output were measured and compared between specimen types. The 7x7 cable exhibited similar actuation to the single straight wire, but with slightly longer stroke and marginally more shakedown, while maintaining equivalent specific work output. This leads to the conclusion that the 7x7 cable effectively scaled up the adaptive properties the straight wire. Under loads below 150 MPa, the 1x27 cable had up to double the actuation stroke and work output, but exhibited larger shakedown and poorer performance when loaded higher.

  20. Atomic Layer-Deposited TiO2 Coatings on NiTi Surface

    Science.gov (United States)

    Vokoun, D.; Racek, J.; Kadeřávek, L.; Kei, C. C.; Yu, Y. S.; Klimša, L.; Šittner, P.

    2018-02-01

    NiTi shape-memory alloys may release poisonous Ni ions at the alloys' surface. In an attempt to prepare a well-performing surface layer on an NiTi sample, the thermally grown TiO2 layer, which formed during the heat treatment of NiTi, was removed and replaced with a new TiO2 layer prepared using the atomic layer deposition (ALD) method. Using x-ray photoelectron spectroscopy, it was found that the ALD layer prepared at as low a temperature as 100 °C contained Ti in oxidation states + 4 and + 3. As for static corrosion properties of the ALD-coated NiTi samples, they further improved compared to those covered by thermally grown oxide. The corrosion rate of samples with thermally grown oxide was 1.05 × 10-5 mm/year, whereas the corrosion rate of the ALD-coated samples turned out to be about five times lower. However, cracking of the ALD coating occurred at about 1.5% strain during the superelastic mechanical loading in tension taking place via the propagation of a localized martensite band.

  1. Design and experimental characterization of a NiTi-based, high-frequency, centripetal peristaltic actuator

    International Nuclear Information System (INIS)

    Borlandelli, E; Scarselli, D; Bettini, P; Morandini, M; Sala, G; Quadrio, M; Nespoli, A; Rigamonti, D; Villa, E

    2015-01-01

    Development and experimental testing of a peristaltic device actuated by a single shape-memory NiTi wire are described. The actuator is designed to radially shrink a compliant silicone pipe, and must work on a sustained basis at an actuation frequency that is higher than those typical of NiTi actuators. Four rigid, aluminum-made circular sectors are sitting along the pipe circumference and provide the required NiTi wire housing. The aluminum assembly acts as geometrical amplifier of the wire contraction and as heat sink required to dissipate the thermal energy of the wire during the cooling phase. We present and discuss the full experimental investigation of the actuator performance, measured in terms of its ability to reduce the pipe diameter, at a sustained frequency of 1.5 Hz. Moreover, we investigate how the diameter contraction is affected by various design parameters as well as actuation frequencies up to 4 Hz. We manage to make the NiTi wire work at 3% in strain, cyclically providing the designed pipe wall displacement. The actuator performance is found to decay approximately linearly with actuation frequencies up to 4 Hz. Also, the interface between the wire and the aluminum parts is found to be essential in defining the functional performance of the actuator. (paper)

  2. Two-way shape memory effect induced by repetitive compressive loading cycles

    International Nuclear Information System (INIS)

    Kim, Hyun-Chul; Yoo, Young-Ik; Lee, Jung-Ju

    2009-01-01

    The NiTi alloy can be trained by repetitive loading or heating cycles. As a result of the training, a two-way shape memory effect (TWSME) can be induced. Considerable research has been reported regarding the TWSME trained by tensile loading. However, the TWSME trained by compressive loading has not been investigated nearly as much. In this paper, the TWSME is induced by compressive loading cycles and the two-way shape memory strain is evaluated by using two types of specimen: a solid cylinder type and a tube type. The TWSME trained by compressive loading is different from that trained by tensile loading owing to the severe tension/compression asymmetry as described in previous research. After repetitive compressive loading cycles, strain variation upon cooling is observed, and this result proves that the TWSME is induced by compressive loading cycles. By performing compressive loading cycles, plastic deformation in NiTi alloy occurs more than for tensile loading cycles, which brings about the appearance of TWSME. It can be said that the TWSME is induced by compressive loading cycles more easily. The two-way shape memory strain increases linearly as the maximum strain of compressive loading cycles increases, regardless of the shape and the size of the NiTi alloy; this two-way shape memory strain then shows a tendency towards saturation after some repeated cycles

  3. Improved Functional Properties and Efficiencies of Nitinol Wires Under High-Performance Shape Memory Effect (HP-SME)

    Science.gov (United States)

    Casati, R.; Saghafi, F.; Biffi, C. A.; Vedani, M.; Tuissi, A.

    2017-10-01

    Martensitic Ti-rich NiTi intermetallics are broadly used in various cyclic applications as actuators, which exploit the shape memory effect (SME). Recently, a new approach for exploiting austenitic Ni-rich NiTi shape memory alloys as actuators was proposed and named high-performance shape memory effect (HP-SME). HP-SME is based on thermal recovery of de-twinned martensite produced by mechanical loading of the parent phase. The aim of the manuscript consists in evaluating and comparing the fatigue and actuation properties of austenitic HP-SME wires and conventional martensitic SME wires. The effect of the thermomechanical cycling on the actuation response and the changes in the electrical resistivity of both shape memory materials were studied by performing the actuation tests at different stages of the fatigue life. Finally, the changes in the transition temperatures before and after cycling were also investigated by differential calorimetric tests.

  4. Cyclic degradation of antagonistic shape memory actuated structures

    International Nuclear Information System (INIS)

    Sofla, A Y N; Elzey, D M; Wadley, H N G

    2008-01-01

    Antagonistic shape memory actuated structures exploit opposing pairs of one-way shape memory alloy (SMA) linear actuators to create devices capable of a fully reversible response. Unlike many conventional reversible SMA devices they do not require bias force components (springs) to return them to their pre-actuated configuration. However, the repeated use of SMA antagonistic devices results in the accumulation of plastic strain in the actuators which can diminish their actuation stroke. We have investigated this phenomenon and the effect of shape memory alloy pre-strain upon it for near equi-atomic NiTi actuators. We find that the degradation eventually stabilizes during cycling. A thermomechanical treatment has been found to significantly reduce degradation in cyclic response of the actuators

  5. Reactive Ni/Ti nanolaminates

    International Nuclear Information System (INIS)

    Adams, D. P.; Bai, M. M.; Rodriguez, M. A.; McDonald, J. P.; Jones, E. Jr.; Brewer, L.; Moore, J. J.

    2009-01-01

    Nickel/titanium nanolaminates fabricated by sputter deposition exhibited rapid, high-temperature synthesis. When heated locally, self-sustained reactions were produced in freestanding Ni/Ti multilayer foils characterized by average propagation speeds between ∼0.1 and 1.4 m/s. The speed of a propagating reaction front was affected by total foil thickness and bilayer thickness (layer periodicity). In contrast to previous work with compacted Ni-Ti powders, no preheating of Ni/Ti foils was required to maintain self-propagating reactions. High-temperature synthesis was also stimulated by rapid global heating demonstrating low ignition temperatures (T ig )∼300-400 deg. C for nanolaminates. Ignition temperature was influenced by bilayer thickness with more coarse laminate designs exhibiting increased T ig . Foils reacted in a vacuum apparatus developed either as single-phase B2 cubic NiTi (austenite) or as a mixed-phase structure that was composed of monoclinic B19 ' NiTi (martensite), hexagonal NiTi 2 , and B2 NiTi. Single-phase, cubic B2 NiTi generally formed when the initial bilayer thickness was made small.

  6. Behaviour of human endothelial cells on surface modified NiTi alloy.

    Science.gov (United States)

    Plant, Stuart D; Grant, David M; Leach, Lopa

    2005-09-01

    Intravascular stents are being designed which utilise the shape memory properties of NiTi alloy. Despite the clinical advantages afforded by these stents their application has been limited by concerns about the large nickel ion content of the alloy. In this study, the surface chemistry of NiTi alloy was modified by mechanical polishing and oxidising heat treatments and subsequently characterised using X-ray photon spectroscopy (XPS). The effect of these surfaces on monolayer formation and barrier integrity of human umbilical vein endothelial cells (HUVEC) was then assessed by confocal imaging of the adherens junctional molecule VE-cadherin, perijunctional actin and permeability to 42kDa dextrans. Dichlorofluoroscein assays were used to measure oxidative stress in the cells. XPS analysis of NiTi revealed its surface to be dominated by TiO(2). However, where oxidation had occurred after mechanical polishing or post polishing heat treatments at 300 and 400 degrees C in air, a significant amount of metallic nickel or nickel oxide species (10.5 and 18.5 at%) remained on the surface. Exposure of HUVECs to these surfaces resulted in increased oxidative stress within the cells, loss of VE-cadherin and F-actin and significantly increased paracellular permeability. These pathological phenomena were not found in cells grown on NiTi which had undergone heat treatment at 600 degrees C. At this temperature thickening of the TiO(2) layer had occurred due to diffusion of titanium ions from the bulk of the alloy, displacing nickel ions to sub-surface areas. This resulted in a significant reduction in nickel ions detectable on the sample surface (4.8 at%). This study proposes that the integrity of human endothelial monolayers on NiTi is dependent upon the surface chemistry of the alloy and that this can be manipulated, using simple oxidising heat treatments.

  7. Surface chemistry and cytotoxicity of reactively sputtered tantalum oxide films on NiTi plates

    Energy Technology Data Exchange (ETDEWEB)

    McNamara, K. [Materials and Surface Science Institute, University of Limerick, Limerick (Ireland); Department of Physics & Energy, University of Limerick, Limerick (Ireland); Kolaj-Robin, O.; Belochapkine, S.; Laffir, F. [Materials and Surface Science Institute, University of Limerick, Limerick (Ireland); Gandhi, A.A. [Materials and Surface Science Institute, University of Limerick, Limerick (Ireland); Department of Physics & Energy, University of Limerick, Limerick (Ireland); Tofail, S.A.M., E-mail: tofail.syed@ul.ie [Materials and Surface Science Institute, University of Limerick, Limerick (Ireland); Department of Physics & Energy, University of Limerick, Limerick (Ireland)

    2015-08-31

    NiTi, an equiatomic alloy containing nickel and titanium, exhibits unique properties such as shape memory effect and superelasticity. NiTi also forms a spontaneous protective titanium dioxide (TiO{sub 2}) layer that allows its use in biomedical applications. Despite the widely perceived biocompatibility there remain some concerns about the sustainability of the alloy's biocompatibility due to the defects in the TiO{sub 2} protective layer and the presence of high amount of sub-surface Ni, which can give allergic reactions. Many surface treatments have been investigated to try to improve both the corrosion resistance and biocompatibility of this layer. For such purposes, we have sputter deposited tantalum (Ta) oxide thin films onto the surface of the NiTi alloy. Despite being one of the promising metals for biomedical applications, Ta, and its various oxides and their interactions with cells have received relatively less attention. The oxidation chemistry, crystal structure, morphology and biocompatibility of these films have been investigated. In general, reactive sputtering especially in the presence of a low oxygen mixture yields a thicker film with better control of the film quality. The sputtering power influenced the surface oxidation states of Ta. Both microscopic and quantitative cytotoxicity measurements show that Ta films on NiTi are biocompatible with little to no variation in cytotoxic response when the surface oxidation state of Ta changes. - Highlights: • Reactive sputtering in low oxygen mixture yields thicker better quality films. • Sputtering power influenced surface oxidation states of Ta. • Cytotoxicity measurements show Ta films on NiTi are biocompatible. • Little to no variation in cytotoxic response when oxidation state changes.

  8. NiTi Alloys for Tribological Applications: The Role of In-Situ Nanotechnology

    Science.gov (United States)

    Dellacorte, Christopher

    2016-01-01

    Beginning in 2004, NASA initiated the investigation and development of, Nitinol 60, a nickel-rich and dimensionally stable version of shape memory alloy Nitinol 55, as an alternative to bearing steel. Early investigations showed it to be hard and impervious to aqueous corrosion but the fundamental reasons for these properties were unknown. Shape memory alloys made from equiatomic Ni-Ti are widely known for their unique dimensional instability behavior that can be triggered by thermal and mechanical stress. The nickel-rich alloys exhibit no such dimension change property and have high hardness but have largely been overlooked by industry and the engineering community. Though steel is the dominant material of choice for mechanical components (bearings and gears) it has intrinsic limitations related to corrosion and plastic deformation. In contrast, Ni-Ti alloys are intrinsically rustproof and can withstand high contact loads without damage (denting). Over the last decade, focused RD to exploit these alloys for new applications has revealed that in-situ nano-scale phases that form during processing are largely responsible for NiTis remarkable properties. In this presentation, the state-of-art of nickel-rich NiTi alloys will be introduced and the nanotechnology behind their intriguing behavior will be addressed. The presentation will include discussion of how NASA is adopting this new technology inside the space station water recycling system as a pathfinder for more down-to-earth tribological challenges.

  9. Recent activities of association of shape memory alloys (ASMA) in Japan

    Energy Technology Data Exchange (ETDEWEB)

    Kobayashi, J [ASMA, Yokohama (Japan); Yamauchi, K [TOKIN Corp., Sendai (Japan); Miyashita, T [Nishimatsu Construction Co., Ltd., Yamato (Japan); Ohkata, I [Kato Hatsujo Kaisha, Ltd., Yokohama (Japan); Narumi, S [Sogo Hatsujo Co., Ltd. (Japan); Suzuki, Y [Furukawa Electric Co. Ltd., Tokyo (Japan)

    1995-12-01

    The Association of Shape Memory Alloys(ASMA) was established in 1983 and systematic surveys on the Ni-Ti and Cu based SMAs were carried out until 1986. The ASMA is now reorganized as a private association. In this paper, we briefly introduce several SMA products of the member companies and present a couple of products, a static rock breaking system and a thermostatic mixing valve in detail. (orig.).

  10. Thermo-mechanical response and fatigue behavior of shape memory alloy

    International Nuclear Information System (INIS)

    Kusagawa, Masaki; Asada, Yasuhide; Nakamura, Toshiya

    1998-01-01

    Mechanical, thermo-mechanical and fatigue behaviors of Ni-Ti-Nb shape memory alloy (SMA) have been studied to prepare material data for a design purpose. Presented are testing devices, testing procedure and test results of monotonic tensile, recovery of inelastic deformation due to post heating (thermo-mechanical recovery) and fatigue for future use of the SMA as a structural material of nuclear incore structures. (orig.)

  11. Recent activities of association of shape memory alloys (ASMA) in Japan

    International Nuclear Information System (INIS)

    Kobayashi, J.; Yamauchi, K.; Miyashita, T.; Ohkata, I.; Narumi, S.; Suzuki, Y.

    1995-01-01

    The Association of Shape Memory Alloys(ASMA) was established in 1983 and systematic surveys on the Ni-Ti and Cu based SMAs were carried out until 1986. The ASMA is now reorganized as a private association. In this paper, we briefly introduce several SMA products of the member companies and present a couple of products, a static rock breaking system and a thermostatic mixing valve in detail. (orig.)

  12. Thermo-mechanical response and fatigue behavior of shape memory alloy

    Energy Technology Data Exchange (ETDEWEB)

    Kusagawa, Masaki; Asada, Yasuhide; Nakamura, Toshiya [Tokyo Univ. (Japan). Dept. of Mechanical Engineering

    1998-11-01

    Mechanical, thermo-mechanical and fatigue behaviors of Ni-Ti-Nb shape memory alloy (SMA) have been studied to prepare material data for a design purpose. Presented are testing devices, testing procedure and test results of monotonic tensile, recovery of inelastic deformation due to post heating (thermo-mechanical recovery) and fatigue for future use of the SMA as a structural material of nuclear incore structures. (orig.)

  13. Study of the Behavior of a Bell-Shaped Colonic Self-Expandable NiTi Stent under Peristaltic Movements

    Directory of Open Access Journals (Sweden)

    Sergio Puértolas

    2013-01-01

    Full Text Available Managing bowel obstruction produced by colon cancer requires an emergency intervention to patients usually in poor conditions, and it requires creating an intestinal stoma in most cases. Regardless of that the tumor may be resectable, a two-stage surgery is mandatory. To avoid these disadvantages, endoscopic placement of self-expanding stents has been introduced more than 10 years ago, as an alternative to relieve colonic obstruction. It can be used as a bridge to elective single-stage surgery avoiding a stoma or as a definitive palliative solution in patients with irresectable tumor or poor estimated survival. Stents must be capable of exerting an adequate radial pressure on the stenosed wall, keeping in mind that stent must not move or be crushed, guaranteeing an adequate lumen when affected by peristaltic waves. A finite element simulation of bell-shaped nitinol stent functionality has been done. Catheter introduction, releasing at position, and the effect of peristaltic wave were simulated. To check the reliability of the simulation, a clinical experimentation with porcine specimens was carried out. The stent presented a good deployment and flexibility. Stent behavior was excellent, expanding from the very narrow lumen corresponding to the maximum peristaltic pressure to the complete recovery of operative lumen when the pressure disappears.

  14. Fatigue behavior of lubricated Ni-Ti endodontic rotary instruments

    Directory of Open Access Journals (Sweden)

    A. Brotzu

    2014-04-01

    Full Text Available The use of Ni-Ti alloys in the practice of endodontic comes from their important properties such as shape memory and superelasticity phenomena, good corrosion resistance and high compatibility with biological tissues. In the last twenty years a great variety of nickel-titanium rotary instruments, with various sections and taper, have been developed and marketed. Although they have many advantages and despite their increasing popularity, a major concern with the use of Ni-Ti rotary instruments is the possibility of unexpected failure in use due to several reasons: novice operator handling, presence manufacturing defects, fatigue etc. Recently, the use of an aqueous gel during experimental tests showed a longer duration of the instruments. The aim of the present work is to contribute to the study of the fracture behavior of these endodontic rotary instruments particularly assessing whether the use of the aqueous lubricant gel can extend their operative life stating its reasons. A finite element model (FEM has been developed to support the experimental results. The results were rather contradictory, also because the Perspex (Poly-methyl methacrylate, PMMA cannot simulate completely the dentin mechanical behavior; however the results highlight some interesting points which are discussed in the paper.

  15. Exploiting NiTi shape memory alloy films in design of tunable high frequency microcantilever resonators

    Czech Academy of Sciences Publication Activity Database

    Stachiv, Ivo; Šittner, Petr; Olejníček, Jiří; Landa, M.; Heller, Luděk

    2017-01-01

    Roč. 111, č. 21 (2017), s. 1-5, č. článku 213105. ISSN 0003-6951 R&D Projects: GA ČR GC15-13174J Institutional support: RVO:68378271 Keywords : equipment and apparatus * microactuators * smart materials * continuum mechanics * sensors Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 3.411, year: 2016

  16. Thermokinetic Simulation of Precipitation in NiTi Shape Memory Alloys

    Science.gov (United States)

    Cirstea, C. D.; Karadeniz-Povoden, E.; Kozeschnik, E.; Lungu, M.; Lang, P.; Balagurov, A.; Cirstea, V.

    2017-06-01

    Considering classical nucleation theory and evolution equations for the growth and composition change of precipitates, we simulate the evolution of the precipitates structure in the classical stages of nucleation, growth and coarsening using the solid-state transformation Matcalc software. The formation of Ni3Ti, Ni4Ti3 or Ni3Ti2 precipitate is the key to hardening phenomenon of the alloys, which depends on the nickel solubility in the bulk alloys. The microstructural evolution of metastable Ni4Ti3 and Ni3Ti2 precipitates in Ni-rich TiNi alloys is simulated by computational thermokinetics, based on thermodynamic and diffusion databases. The simulated precipitate phase fractions are compared with experimental data.

  17. Effect of SHS conditions on microstructure of NiTi shape memory alloy

    Czech Academy of Sciences Publication Activity Database

    Novák, P.; Mejzliková, L.; Michalcová, A.; Čapek, J.; Beran, Přemysl; Vojtěch, D.

    2013-01-01

    Roč. 42, NOV 2013 (2013), s. 85-91 ISSN 0966-9795 R&D Projects: GA ČR GBP108/12/G043; GA MŠk(XE) LM2011019 Institutional support: RVO:61389005 Keywords : intermetallics * miscellaneous * phase identification * reaction synthesis * electron microscopy * scanning Subject RIV: JG - Metallurgy Impact factor: 2.119, year: 2013

  18. Cellular Shape Memory Alloy Structures: Experiments & Modeling (Part 1)

    Science.gov (United States)

    2012-08-01

    High -­‐ temperature  SMAs 24 Braze  Joint  between  two  wrought  pieces  of  a  Ni24.5Pd25Ti50.5  HTSMA   (HTSMA  from...process  can  be  used   to  join  other  metal  alloys  and   high -­‐ temperature   SMAs 25 Cellular  Shape  Memory...20 30 40 50 60 910 3 4 8 5 2 T (°C) Shape memory & superelasticity 1 0 e (%) (GPa) 6 7 A NiTi wire

  19. Three-Dimensional Cellular Structures Enhanced By Shape Memory Alloys

    Science.gov (United States)

    Nathal, Michael V.; Krause, David L.; Wilmoth, Nathan G.; Bednarcyk, Brett A.; Baker, Eric H.

    2014-01-01

    This research effort explored lightweight structural concepts married with advanced smart materials to achieve a wide variety of benefits in airframe and engine components. Lattice block structures were cast from an aerospace structural titanium alloy Ti-6Al-4V and a NiTi shape memory alloy (SMA), and preliminary properties have been measured. A finite element-based modeling approach that can rapidly and accurately capture the deformation response of lattice architectures was developed. The Ti-6-4 and SMA material behavior was calibrated via experimental tests of ligaments machined from the lattice. Benchmark testing of complete lattice structures verified the main aspects of the model as well as demonstrated the advantages of the lattice structure. Shape memory behavior of a sample machined from a lattice block was also demonstrated.

  20. Cavitation resistance of surface composition "Steel-Ni-TiNi-TiNiZr-cBNCo", formed by High-Velocity Oxygen-Fuel spraying

    Science.gov (United States)

    Blednova, Zh. M.; Dmitrenko, D. V.; Balaev, E. U. O.

    2018-01-01

    The object of the study is a multilayered surface composition "Steel - a Multicomponent material with Shape Memory Effect - a wear-resistant layer" under conditions of cavitation effects in sea water. Multicomponent TiNi-based coatings with addition of alloying elements such as Zr in an amount up to 10% mass, allow to create a composite material with a gradient of properties at the interface of layers, which gives new properties to coatings and improves their performance significantly. The use of materials with shape memory effect (SME) as surface layers or in the composition of surface layered compositions allows to provide an effective reaction of materials to the influence of external factors and adaptation to external influences. The surface composite layer cBN-10%Co has high hardness and strength, which ensures its resistance to shock cyclic influences of collapsing caverns. The increased roughness of the surface of a solid surface composite in the form of strong columnar structures ensures the crushing of vacuum voids, redistributing their effect on the entire surface, and not concentrating them in certain zones. In addition, the gradient structure of the multilayer composite coating TiNi-Ti33Ni49Zr18-cBN-10%Co Co makes it possible to create conditions for the relaxation of stresses created by the variable impact load of cavitation caverns and the manifestation of compensating internal forces due to thermo-elastic martensitic transformations of SME materials. The cavitation resistance of the coating TiNi-Ti33Ni49Zr18-cBN-10%Co according to the criterion of mass wear is 15-20 times higher than that of the base material without coating and 10-12 times higher than that of the TiNi-TiNiZr coating. The proposed architecture of the multifunctional gradient composition, "steel-Ni-TiNi- Ti33Ni49Zr18-cBN-10%Co", each layer of which has its functional purpose, allows to increase the service life of parts operating under conditions of cavitation-fatigue loading in

  1. Torsion and bending properties of shape memory and superelastic nickel-titanium rotary instruments.

    Science.gov (United States)

    Ninan, Elizabeth; Berzins, David W

    2013-01-01

    Recently introduced into the market are shape memory nickel-titanium (NiTi) rotary files. The objective of this study was to investigate the torsion and bending properties of shape memory files (CM Wire, HyFlex CM, and Phoenix Flex) and compare them with conventional (ProFile ISO and K3) and M-Wire (GT Series X and ProFile Vortex) NiTi files. Sizes 20, 30, and 40 (n = 12/size/taper) of 0.02 taper CM Wire, Phoenix Flex, K3, and ProFile ISO and 0.04 taper HyFlex CM, ProFile ISO, GT Series X, and Vortex were tested in torsion and bending per ISO 3630-1 guidelines by using a torsiometer. All data were statistically analyzed by analysis of variance and the Tukey-Kramer test (P = .05) to determine any significant differences between the files. Significant interactions were present among factors of size and file. Variability in maximum torque values was noted among the shape memory files brands, sometimes exhibiting the greatest or least torque depending on brand, size, and taper. In general, the shape memory files showed a high angle of rotation before fracture but were not statistically different from some of the other files. However, the shape memory files were more flexible, as evidenced by significantly lower bending moments (P < .008). Shape memory files show greater flexibility compared with several other NiTi rotary file brands. Copyright © 2013 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

  2. The use of shape memory compression anastomosis clips in cholecystojejunostomy in pigs – a preliminary study

    Directory of Open Access Journals (Sweden)

    Piotr Holak

    2015-01-01

    Full Text Available This paper reports on the use of compression anastomosis clips (CAC in cholecystoenterostomy in an animal model. Cholecystojejunostomy was performed in 6 pigs using implants made of nickel-titanium alloy in the form of elliptical springs with two-way shape memory. The applied procedure led to the achievement of tight anastomosis with a minimal number of complications and positive results of histopathological evaluations of the anastomotic site. The results of the study indicate that shape memory NiTi clips are a promising surgical tool for cholecystoenterostomy in cats and dogs.

  3. Finite Element Simulation and Additive Manufacturing of Stiffness-Matched NiTi Fixation Hardware for Mandibular Reconstruction Surgery

    Directory of Open Access Journals (Sweden)

    Ahmadreza Jahadakbar

    2016-12-01

    Full Text Available Process parameters and post-processing heat treatment techniques have been developed to produce both shape memory and superelastic NiTi using Additive Manufacturing. By introducing engineered porosity, the stiffness of NiTi can be tuned to the level closely matching cortical bone. Using additively manufactured porous superelastic NiTi, we have proposed the use of patient-specific, stiffness-matched fixation hardware, for mandible skeletal reconstructive surgery. Currently, Ti-6Al-4V is the most commonly used material for skeletal fixation devices. Although this material offers more than sufficient strength for immobilization during the bone healing process, the high stiffness of Ti-6Al-4V implants can cause stress shielding. In this paper, we present a study of mandibular reconstruction that uses a dry cadaver mandible to validate our geometric and biomechanical design and fabrication (i.e., 3D printing of NiTi skeletal fixation hardware. Based on the reference-dried mandible, we have developed a Finite Element model to evaluate the performance of the proposed fixation. Our results show a closer-to-normal stress distribution and an enhanced contact pressure at the bone graft interface than would be in the case with Ti-6Al-4V off-the-shelf fixation hardware. The porous fixation plates used in this study were fabricated by selective laser melting.

  4. Evaluation of selected mechanical properties of NiTi rotary glide path files manufactured from controlled memory wires.

    Science.gov (United States)

    Nishijo, Miki; Ebihara, Arata; Tokita, Daisuke; Doi, Hisashi; Hanawa, Takao; Okiji, Takashi

    2018-03-28

    This study aimed to investigate mechanical properties related to flexibility and fracture resistance of controlled memory wiremanufactured nickel-titanium rotary glide path files [HyFlex EDM Glide Path File (EDM) and HyFlex GPF (GPF)]. Scout RaCe (RaCe) served as control. Bending loads, torsional/cyclic fatigue resistance, and screw-in forces were measured. EDM showed a significantly larger torque at fracture, a longer time to cyclic fracture in reciprocation and a larger screw-in force compared with GPF and RaCe. GPF showed significantly lower bending loads and higher angular deflection values than EDM and RaCe, and a significantly longer time to cyclic fracture than RaCe. The time to cyclic fracture was significantly longer in reciprocation compared with continuous rotation in EDM and GPF. It can be concluded that EDM and/or GPF showed higher flexibility and cyclic/torsional fatigue resistance compared with RaCe; and that reciprocation conferred better cyclic fatigue resistance to EDM and GPF.

  5. [Utility of nickel-titanium shape memory alloys of vertebral body reduction fixator with assisted distraction bar].

    Science.gov (United States)

    Man, Yi; Zheng, Yue-huan; Cao, Peng; Chen, Bo; Zheng, Tao; Sun, Chang-hui; Lu, Jiong

    2011-06-07

    To test the nickel-titanium (Ni-Ti) shape memory alloys of vertebral body reduction fixator with assisted distraction bar for the treatment of traumatic and osteoporotic vertebral body fracture. A Ni-Ti shape memory alloys of vertebral body reduction fixator with assisted distraction bar was implanted into the compressed fracture specimens through vertebral pedicle with the radiographic monitoring to reduce the collapsed endplate as well as distract the compressed vertebral fracture. Radiographic film and computed tomographic reconstruction technique were employed to evaluate the effects of reduction and distraction. A biomechanic test machine was used to measure the fatigue and the stability of deformation of fixation segments. Relying on the effect of temperature shape memory, such an assembly could basically reduce the collapsed endplate as well as distract the compressed vertebral fracture. And when unsatisfied results of reduction and distraction occurred, its super flexibility could provide additional distraction strength. A Ni-Ti shape memory alloys of vertebral body reduction fixator with assisted distraction bar may provide effective endplate reduction, restore the vertebral height and the immediate biomechanic spinal stability. So the above assembly is indicated for the treatment of traumatic and osteoporotic vertebral body fracture.

  6. Orthodontic buccal tooth movement by nickel-free titanium-based shape memory and superelastic alloy wire.

    Science.gov (United States)

    Suzuki, Akihiro; Kanetaka, Hiroyasu; Shimizu, Yoshinaka; Tomizuka, Ryo; Hosoda, Hideki; Miyazaki, Shuichi; Okuno, Osamu; Igarashi, Kaoru; Mitani, Hideo

    2006-11-01

    To examine the mechanical properties and the usefulness of titanium-niobium-aluminum (Ti-Nb-Al) wire in orthodontic tooth movement as compared with nickel-titanium (Ni-Ti) wire. The load deflection of expansion springs was gauged with an original jig. The gradient of the superelastic region was measured during the unloading process. Expansion springs comprising the two types of alloy wires were applied to upper first molars of rats. The distance between the first molars was measured with micrometer calipers. The force magnitude of the Ti-Nb-Al expansion spring was lower than that of the Ni-Ti expansion spring over the entire deflection range. The initial force magnitude and the gradient in the superelastic region of the Ti-Nb-Al expansion springs were half those of the Ni-Ti expansion springs. Thus, Ti-Nb-Al expansion springs generated lighter and more continuous force. Tooth movement in the Ni-Ti group proceeded in a stepwise fashion. On the other hand, tooth movement in the Ti-Nb-Al group showed relatively smooth and continuous progression. At 17 days after insertion of expansion springs, there were no significant differences between the Ti-Nb-Al and Ni-Ti groups in the amount of tooth movement. These results indicate that Ti-Nb-Al wire has excellent mechanical properties for smooth, continuous tooth movement and suggest that Ti-Nb-Al wire may be used as a practical nickel-free shape memory and superelastic alloy wire for orthodontic treatment as a substitute for Ni-Ti wire.

  7. Biased Target Ion Beam Deposition and Nanoskiving for Fabricating NiTi Alloy Nanowires

    Science.gov (United States)

    Hou, Huilong; Horn, Mark W.; Hamilton, Reginald F.

    2016-12-01

    Nanoskiving is a novel nanofabrication technique to produce shape memory alloy nanowires. Our previous work was the first to successfully fabricate NiTi alloy nanowires using the top-down approach, which leverages thin film technology and ultramicrotomy for ultra-thin sectioning. For this work, we utilized biased target ion beam deposition technology to fabricate nanoscale (i.e., sub-micrometer) NiTi alloy thin films. In contrast to our previous work, rapid thermal annealing was employed for heat treatment, and the B2 austenite to R-phase martensitic transformation was confirmed using stress-temperature and diffraction measurements. The ultramicrotome was programmable and facilitated sectioning the films to produce nanowires with thickness-to-width ratios ranging from 4:1 to 16:1. Energy dispersive X-ray spectroscopy analysis confirmed the elemental Ni and Ti make-up of the wires. The findings exposed the nanowires exhibited a natural ribbon-like curvature, which depended on the thickness-to-width ratio. The results demonstrate nanoskiving is a potential nanofabrication technique for producing NiTi alloy nanowires that are continuous with an unprecedented length on the order of hundreds of micrometers.

  8. Effect of laser welding parameters on the austenite and martensite phase fractions of NiTi

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, J.P., E-mail: jp.oliveira@campus.fct.unl.pt [CENIMAT/i3N, Faculdade de Ciências e Tecnologia, Universidade Nova de Lisboa (Portugal); Braz Fernandes, F.M. [CENIMAT/i3N, Faculdade de Ciências e Tecnologia, Universidade Nova de Lisboa (Portugal); Miranda, R.M. [UNIDEMI, Faculdade de Ciências e Tecnologia, Universidade Nova de Lisboa (Portugal); Schell, N. [Institute of Materials Research, Helmholtz-Zentrum Geesthacht, Max-Planck-Str. 1, D-21502 Geesthacht (Germany); Ocaña, J.L. [Centro Láser UPM, Universidad Politécnica de Madrid, Edificio “La Arboleda”, Ctra. Valencia, km 7,300, Campus Sur UPM, 28031 Madrid (Spain)

    2016-09-15

    Although laser welding is probably the most used joining technique for NiTi shape memory alloys there is still a lack of understanding about the effects of laser welding parameters on the microstructural induced changes: in both the heat affected and fusion zones martensite may be present, while the base material is fully austenitic. Synchrotron X-ray diffraction was used for fine probing laser welded NiTi joints. Through Rietveld refinement the martensite and austenite phase fractions were determined and it was observed that the martensite content increases towards the weld centreline. This is related to a change of the local transformation temperatures on these regions, which occurs due to compositional variation in those regions. The martensite phase fraction in the thermally affected regions may have significant implications on functional properties on these joints. - Highlights: •Synchrotron X-ray diffraction was used for fine probing of the microstructure in laser welded NiTi joints. •Rietveld refinement allowed to determine the content of martensite along the heat affected and fusion zones. •The martensite content increases from the base material towards the weld centreline.

  9. Shape memory polymer medical device

    Science.gov (United States)

    Maitland, Duncan [Pleasant Hill, CA; Benett, William J [Livermore, CA; Bearinger, Jane P [Livermore, CA; Wilson, Thomas S [San Leandro, CA; Small, IV, Ward; Schumann, Daniel L [Concord, CA; Jensen, Wayne A [Livermore, CA; Ortega, Jason M [Pacifica, CA; Marion, III, John E.; Loge, Jeffrey M [Stockton, CA

    2010-06-29

    A system for removing matter from a conduit. The system includes the steps of passing a transport vehicle and a shape memory polymer material through the conduit, transmitting energy to the shape memory polymer material for moving the shape memory polymer material from a first shape to a second and different shape, and withdrawing the transport vehicle and the shape memory polymer material through the conduit carrying the matter.

  10. Shape memory effect alloys

    International Nuclear Information System (INIS)

    Koshimizu, S.

    1992-01-01

    Although the pseudo- or super-elasticity phenomena and the shape memory effect were known since the 1940's, the enormous curiosity and the great interest to their practical applications emerged with the development of the NITINOL alloy (Nickel-Titanium Naval Ordance Laboratory) by the NASA during the 1960's. This fact marked the appearance of a new class of materials, popularly known as shape memory effect alloys (SMEA). The objective of this work is to present a state-of-the-art of the development and applications for the SMEA. (E.O.)

  11. Magnetic shape memory behaviour

    International Nuclear Information System (INIS)

    Brown, P.J.; Gandy, A.P.; Ishida, K.; Kainuma, R.; Kanomata, T.; Matsumoto, M.; Morito, H.; Neumann, K.-U.; Oikawa, K.; Ouladdiaf, B.; Ziebeck, K.R.A.

    2007-01-01

    Materials that can be transformed at one temperature T F , then cooled to a lower temperature T M and plastically deformed and on heating to T F regain their original shape are currently receiving considerable attention. In recovering their shape the alloys can produce a displacement or a force, or a combination of the two. Such behaviour is known as the shape memory effect and usually takes place by change of temperature or applied stress. For many applications the transformation is not sufficiently rapid or a change in temperature/pressure not appropriate. As a result, considerable effort is being made to find a ferromagnetic system in which the effect can be controlled by an applied magnetic field. The results of recent experiments on ferromagnetic shape memory compounds aimed at understanding the underlying mechanism will be reviewed

  12. Fracture analysis of Ag nanobrazing of NiTi to Ti alloy

    Directory of Open Access Journals (Sweden)

    L. Quintino

    2013-09-01

    Full Text Available Dissimilar joining of shape memory alloys to Ti alloys has long been attempted by several research groups due to the foreseen potential industrial applications. However, the very dissimilar thermo-physical properties of both materials place several difficulties. Brazing can be a solution since the base materials are subjected to a less sharp thermal cycle. In the present study brazed overlap joints of 1 mm thick plates of equiatomic NiTi and Ti6Al4V were produced using nano silver based filler materials. Surfaces were analyzed to assess the type of fracture and the capability of achieving bonding and involved mechanisms are discussed.

  13. Instability of cyclic superelastic deformation of NiTi investigated by synchrotron X-ray diffraction

    Czech Academy of Sciences Publication Activity Database

    Sedmák, P.; Šittner, Petr; Pilch, Jan; Curfs, C.

    2015-01-01

    Roč. 94, Aug (2015), s. 257-270 ISSN 1359-6454 R&D Projects: GA ČR GB14-36566G; GA ČR GPP108/12/P111; GA ČR GA14-15264S; GA ČR GAP107/12/0800 Institutional support: RVO:68378271 Keywords : shape memory alloy * NiTi * superelasticity * cyclic deformation * in situ X-ray diffraction Subject RIV: JG - Metallurgy Impact factor: 5.058, year: 2015

  14. Fracture analysis of Ag nanobrazing of NiTi to Ti alloy

    Energy Technology Data Exchange (ETDEWEB)

    Quintino, L., E-mail: lquirino@ist.utl.pt [Universidade Tecnica de Lisboa (IST/UTL) (Portugal). Instituto Superior Tecnico. Dept. de Engenharia Mecanica; Liu, L., E-mail: ray.plasma@gmail.com [Tsinghua Univ., Beijing (China). Dept. of Mechanical Engineering; Hu, A.; Zhou, Y., E-mail: anming.hu@uwaterloo.ca, E-mail: nzhou@uwaterloo.ca [University of Waterloo, Ontario (Canada). Dept. of Mechanical Engineering; Miranda, R.M., E-mail: rmiranda@fct.unl.pt [Universidade Nova de Lisboa (UNIDEMI), Caparica (Portugal). Dept. de Engenharia Mecanica e Industrial

    2013-07-15

    Dissimilar joining of shape memory alloys to Ti alloys has long been attempted by several research groups due to the foreseen potential industrial applications. However, the very dissimilar thermo-physical properties of both materials place several difficulties. Brazing can be a solution since the base materials are subjected to a less sharp thermal cycle. In the present study brazed overlap joints of 1 mm thick plates of equiatomic Ni Ti and Ti6Al4V were produced using nano silver based filler materials. Surfaces were analyzed to asses the type of fracture and the capability of achieving bonding and involved mechanisms are discussed. (author)

  15. The Effect of Pre-Stressing on the Static Indentation Load Capacity of the Superelastic 60NiTi

    Science.gov (United States)

    DellaCorte, Christopher; Moore, Lewis E., III; Clifton, Joshua S.

    2013-01-01

    Superelastic nickel-titanium alloys, such as 60NiTi (60Ni-40Ti by wt.%), are under development for use in mechanical components like rolling element bearings and gears. Compared to traditional bearing steels, these intermetallic alloys, when properly heat-treated, are hard but exhibit much lower elastic modulus (approx.100 GPa) and a much broader elastic deformation range (approx.3 percent or more). These material characteristics lead to high indentation static load capacity, which is important for certain applications especially space mechanisms. To ensure the maximum degree of elastic behavior, superelastic materials must be pre-stressed, a process referred to as "training" in shape memory effect (SME) terminology, at loads and stresses beyond expected use conditions. In this paper, static indentation load capacity tests are employed to assess the effects of pre-stressing on elastic response behavior of 60NiTi. The static load capacity is measured by pressing 12.7 mm diameter ceramic Si3N4 balls into highly polished, hardened 60NiTi flat plates that have previously been exposed to varying levels of pre-stress (up to 2.7 GPa) to determine the load that results in shallow but measurable (0.6 m, 25 in. deep) permanent dents. Hertz stress calculations are used to estimate contact stress. Without exposure to pre-stress, the 60NiTi surface can withstand an approximately 3400 kN load before significant denting (>0.4 m deep) occurs. When pre-stressed to 2.7 GPa, a static load of 4900 kN is required to achieve a comparable dent, a 30 percent increase. These results suggest that stressing contact surfaces prior to use enhances the static indentation load capacity of the superelastic 60NiTi. This approach may be adaptable to the engineering and manufacture of highly resilient mechanical components such as rolling element bearings.

  16. Reactive Stresses in Ni49Fe18Ga27Co6 Shape-Memory-Alloy Single Crystals

    Science.gov (United States)

    Averkin, A. I.; Krymov, V. M.; Guzilova, L. I.; Timashov, R. B.; Soldatov, A. V.; Nikolaev, V. I.

    2018-03-01

    The reactive stresses induced in Ni49Fe18Ga27Co6-alloy single crystals during martensitic transformations with a limited possibility of shape-memory-strain recovery have been experimentally studied. The data on these crystals are compared with the results obtained previously for Cu-Al-Ni, Ni-Ti, and Ni‒Fe-Ga crystals. The potential of application of the Ni49Fe18Ga27Co6 single crystals in designing drives and power motors is demonstrated.

  17. Shape memory behavior of single and polycrystalline nickel rich nickel titanium alloys

    Science.gov (United States)

    Kaya, Irfan

    NiTi is the most commonly used shape memory alloy (SMA) and has been widely used for bio-medical, electrical and mechanical applications. Nickel rich NiTi shape memory alloys are coming into prominence due to their distinct superelasticity and shape memory properties as compared to near equi-atomic NiTi shape memory alloys. Besides, their lower density and higher work output than steels makes these alloys an excellent candidate for aerospace and automotive industry. Shape memory properties and phase transformation behavior of high Ni-rich Ni54Ti46 (at.%) polycrystals and Ni-rich Ni 51Ti49 (at.%) single-crystals are determined. Their properties are sensitive to heat treatments that affect the phase transformation behavior of these alloys. Phase transformation properties and microstructure were investigated in aged Ni54Ti46 alloys with differential scanning calorimetry (DSC) and transmission electron microscopy (TEM) to reveal the precipitation characteristics and R-phase formation. It was found that Ni54Ti46 has the ability to exhibit perfect superelasticity under high stress levels (~2 GPa) with 4% total strain after 550°C-3h aging. Stress independent R-phase transformation was found to be responsible for the change in shape memory behavior with stress. The shape memory responses of [001], [011] and [111] oriented Ni 51Ti49 single-crystals alloy were reported under compression to reveal the orientation dependence of their shape memory behavior. It has been found that transformation strain, temperatures and hysteresis, Classius-Clapeyron slopes, critical stress for plastic deformation are highly orientation dependent. The effects of precipitation formation and compressive loading at selected temperatures on the two-way shape memory effect (TWSME) properties of a [111]- oriented Ni51Ti49 shape memory alloy were revealed. Additionally, aligned Ni4Ti3 precipitates were formed in a single crystal of Ni51Ti49 alloy by aging under applied compression stress along the

  18. Performance characteristics of shape memory alloy and its applications for fusion technology

    International Nuclear Information System (INIS)

    Nishikawa, Masahiro; Watanabe, Kenji

    1987-01-01

    As a shape memory alloy, Au-Cd alloy was found in 1951. Thereafter, also in In-Tl alloy, shape memory effect was found. The U.S. Naval Ordinance Laboratory developed Ni-Ti alloy, and published in 1965 as NITINOL. As Cu group shape memory alloys, there are Cu-Zn-Al alloy, Cu-Al-Be alloy and Cu-Al-Ni alloy. Recently, iron group shape memory alloy was published. In 1975, 'Shape memory effect and its application' symposium, in 1978, 'NITINOL heat engine international conference', and in 1982 and 1986, 'Martensite transformation international conference' were held, and the method of the proper use of shape memory alloys and the problems of the alloys themselves such as fatigue have been gradually clarified. In this report, the fundamental action characteristics of shape memory alloys are discribed from the viewpoint of the application, and the possibility of applying these characteristics to nuclear fusion devices and the advantage obtained as the result are explained. Shape memory effect and pseudo-elasticity, reversible shape memory effect, the thermodynamic behavior of shape memory alloys, transformation temperature range and using temperature range and so on are described. (Kako, I.)

  19. Low-Pressure and Low-Temperature Hydriding-Pulverization-Dehydriding Method for Producing Shape Memory Alloy Powders

    Science.gov (United States)

    Murguia, Silvia Briseño; Clauser, Arielle; Dunn, Heather; Fisher, Wendy; Snir, Yoav; Brennan, Raymond E.; Young, Marcus L.

    2018-04-01

    Shape memory alloys (SMAs) are of high interest as active, adaptive "smart" materials for applications such as sensors and actuators due to their unique properties, including the shape memory effect and pseudoelasticity. Binary NiTi SMAs have shown the most desirable properties, and consequently have generated the most commercial success. A major challenge for SMAs, in particular, is their well-known compositional sensitivity. Therefore, it is critical to control the powder composition and morphology. In this study, a low-pressure, low-temperature hydriding-pulverization-dehydriding method for preparing well-controlled compositions, size, and size distributions of SMA powders from wires is presented. Starting with three different diameters of as-drawn martensitic NiTi SMA wires, pre-alloyed NiTi powders of various well-controlled sizes are produced by hydrogen charging the wires in a heated H3PO4 solution. After hydrogen charging for different charging times, the wires are pulverized and subsequently dehydrided. The wires and the resulting powders are characterized using scanning electron microscopy, differential scanning calorimetry, and X-ray diffraction. The relationship between the wire diameter and powder size is investigated as a function of hydrogen charging time. The rate of diameter reduction after hydrogen charging of wire is also examined. Finally, the recovery behavior due to the shape memory effect is investigated after dehydriding.

  20. A simple method to treat an ingrowing toenail with a shape-memory alloy device.

    Science.gov (United States)

    Ishibashi, Masaya; Tabata, Nobuko; Suetake, Takaki; Omori, Toshihiro; Sutou, Yuji; Kainuma, Ryosuke; Yamauchi, Kiyoshi; Ishida, Kiyohito

    2008-01-01

    An ingrowing toenail has no definitive treatment. Previously, effective methods were complicated but easy ones had less effect. We show both an easy and an effective way with Cu-Al-Mn-based shape-memory alloys (SMAs). They have a characteristic shape which patients themselves can detach easily without any pain. But they also have enough corrective force. Cu-based SMAs cost much less than Ni-Ti-based alloys. Despite not being appropriate for all cases of ingrowing toenails, it is an easy, effective and less costly alternative.

  1. Shape memory alloy actuator

    Science.gov (United States)

    Varma, Venugopal K.

    2001-01-01

    An actuator for cycling between first and second positions includes a first shaped memory alloy (SMA) leg, a second SMA leg. At least one heating/cooling device is thermally connected to at least one of the legs, each heating/cooling device capable of simultaneously heating one leg while cooling the other leg. The heating/cooling devices can include thermoelectric and/or thermoionic elements.

  2. Improvement on corrosion resistance of NiTi orthopedic materials by carbon plasma immersion ion implantation

    International Nuclear Information System (INIS)

    Poon, Ray W.Y.; Ho, Joan P.Y.; Luk, Camille M.Y.; Liu Xuanyong; Chung, Jonathan C.Y.; Chu, Paul K.; Yeung, Kelvin W.K.; Lu, William W.; Cheung, Kenneth M.C.

    2006-01-01

    Nickel-titanium shape memory alloys (NiTi) have potential applications as orthopedic implants because of their unique super-elastic properties and shape memory effects. However, the problem of out-diffusion of harmful Ni ions from the alloys during prolonged use inside a human body must be overcome before they can be widely used in orthopedic implants. In this work, we enhance the corrosion resistance of NiTi using carbon plasma immersion ion implantation and deposition (PIII and D). Our corrosion and simulated body fluid tests indicate that either an ion-mixed amorphous carbon coating fabricated by PIII and D or direct carbon PIII can drastically improve the corrosion resistance and block the out-diffusion of Ni from the materials. Results of atomic force microscopy (AFM) indicate that both C 2 H 2 -PIII and D and C 2 H 2 -PIII do not roughen the original flat surface to an extent that can lead to degradation in corrosion resistance

  3. Mechanical behaviour of Nd:YAG laser welded superelastic NiTi

    International Nuclear Information System (INIS)

    Vieira, L. Alberty; Fernandes, F.M. Braz; Miranda, R.M.; Silva, R.J.C.; Quintino, L.; Cuesta, A.; Ocana, J.L.

    2011-01-01

    Highlights: → The main innovations claimed are: understand rolling direction effect on mechanical cycling of laser welded NiTi. → Functionality confirmed by stabilization of hysteretic response up to 8% strain. → Welds tensile cycled exhibited superior functional mechanical behaviour. → For applied stresses of 50 MPa below UTS the joints showed superelastic behaviour. - Abstract: Joining techniques for shape memory alloys (SMA) has become of great interest, as their functional properties, namely shape memory effect (SME) and superelasticity (SE), present unique solutions for state-of-the-art applications, although limited results concerning mechanical properties are reported. This paper reports experimental work performed with Nd:YAG continuous wave laser welding of superelastic cold-rolled plates of NiTi 1 mm thick. The mechanical behaviour was evaluated by means of tensile tests performed both to failure and to cycling. The superelastic behaviour of the welded joints was observed for applied stresses close to about 50 MPa below the ultimate tensile strength of the welds. The functionality was confirmed by analyzing the stabilization of the mechanical hysteretic response to strain levels up to 8%. For tensile cycling involving strain levels larger than 6%, welded specimens were found to exhibit superior functional mechanical behaviour presenting larger recoverable strain levels. The fracture surfaces were observed by scanning electron microscopy (SEM) and the effect of the rolling direction on mechanical properties was evaluated and discussed, reinforcing the importance of joint design when laser welding these alloys.

  4. Characterization of Transformation-Induced Defects in Nickel Titanium Shape Memory Alloys

    Science.gov (United States)

    Bowers, Matthew L.

    Shape memory alloys have remarkable strain recovery properties that make them ideal candidates for many applications that include devices in the automotive, aerospace, medical, and MEMS industries. Although these materials are widely used today, their performance is hindered by poor dimensional stability resulting from cyclic degradation of the martensitic transformation behavior. This functional fatigue results in decreased work output and cyclic accumulation of permanent strain. To date, few studies have taken a fundamental approach to investigating the interaction between plasticity and martensite growth and propagation, which is vitally important to mitigating functional fatigue in future alloy development. The current work focuses on understanding the interplay of these deformation mechanisms in NiTi-based shape memory alloys under a variety of different thermomechanical test conditions. Micron-scale compression testing of NiTi shape memory alloy single crystals is undertaken in an effort to probe the mechanism of austenite dislocation generation. Mechanical testing is paired with post mortem defect analysis via diffraction contrast scanning transmission electron microscopy (STEM). Accompanied by micromechanics-based modeling of local stresses surrounding a martensite plate, these results demonstrate that the previously existing martensite and resulting austenite dislocation substructure are intimately related. A mechanism of transformation-induced dislocation generation is described in detail. A study of pure and load-biased thermal cycling of bulk polycrystalline NiTi is done for comparison of the transformation behavior and resultant defects to the stress-induced case. Post mortem and in situ STEM characterization demonstrate unique defect configurations in this test mode and STEM-based orientation mapping reveals local crystal rotation with increasing thermal cycles. Changes in both martensite and austenite microstructures are explored. The results for

  5. Evaluation of deformation and fracture of three single-file NiTi rotary instruments: ProTaper F2, WaveOne Primary and OneShape in simulated curved canals

    Directory of Open Access Journals (Sweden)

    Mina A. Shenouda

    2018-06-01

    Full Text Available Purpose. The aim of the current study was to compare the incidence of deformation and fracture in three single-file NiTi instruments: ProTaper F2, WaveOne Primary and OneShape. Methods. Fifteen instruments were equally divided into three groups: ProTaper F2 in reciprocation, WaveOne Primary in reciprocation and OneShape in continuous rotation. Each instrument was used to prepare standardized simulated curved canals in resin blocks until fracture had occurred. Following each canal preparation, the instruments were examined for deformation both by naked eye inspection and stereomicroscopic examination. The average number of canals prepared until the first incidence of cracks and the average lifespan of the instruments were calculated. Data were analysed using one-way ANOVA and two-sample t-test. Results. There was no statistically significant difference between ProTaper and WaveOne instruments in both the incidence of cracks and the average lifespan (P > 0.05. OneShape instruments had a significantly delayed incidence of cracks and a longer lifespan than both ProTaper and WaveOne instruments (P < 0.05; however, OneShape instruments showed a noticeable early plastic deformation. Conclusion: PT F2 instrument was comparable to WO Primary instrument in terms of fracture resistance, while OS instrument had more fracture resistance than both PT F2 and WO Primary instruments.

  6. Smear layer and debris removal using manual Ni-Ti files compared with rotary Protaper Ni- Ti files - An In-Vitro SEM study.

    Science.gov (United States)

    Reddy, J M V Raghavendra; Latha, Prasanna; Gowda, Basavana; Manvikar, Varadendra; Vijayalaxmi, D Benal; Ponangi, Kalyana Chakravarthi

    2014-02-01

    Predictable successful endodontic therapy depends on correct diagnosis, effective cleaning, shaping and disinfection of the root canals and adequate obturation. Irrigation serves as a flush to remove debris, tissue solvent and lubricant from the canal irregularities; however these irregularities can restrict the complete debridement of root canal by mechanical instrumentation.Various types of hand and rotary instruments are used for the preparation of the root canal system to obtain debris free canals. The purpose of this study was to evaluate the amount of smear layer and debris removal on canal walls following the using of manual Nickel-Titanium (NiTi) files compared with rotary ProTaperNiTi files using a Scanning Electron Microscope in two individual groups. A comparative study consisting of 50 subjects randomized into two groups - 25 subjects in Group A (manual) and 25 subjects in Group B (rotary) was undertaken to investigate and compare the effects of smear layer and debris between manual and rotary NiTi instruments. Chi square test was used to find the significance of smear layer and debris removal in the coronal, middle and apical between Group A and Group B. Both systems of Rotary ProTaperNiTi and manual NiTi files used in the present study, did not create completely clean root canals. Manual NiTi files produced significantly less smear layer and debris compared to Rotary ProTaperNiTi instruments. Rotary instruments were less time consuming when compared to manual instruments. Instrument separation was not found to be significant with both the groups. Both systems of Rotary ProTaperNiTi and manual NiTi files used did not produce completely clean root canals. Manual NiTi files produced significantly less smear layer and debris compared to Rotary protaper instruments. How to cite the article: Reddy JM, Latha P, Gowda B, Manvikar V, Vijayalaxmi DB, Ponangi KC. Smear layer and debris removal using manual Ni-Ti files compared with rotary Protaper Ni-Ti files

  7. A Constitutive Model for Superelastic Shape Memory Alloys Considering the Influence of Strain Rate

    Directory of Open Access Journals (Sweden)

    Hui Qian

    2013-01-01

    Full Text Available Shape memory alloys (SMAs are a relatively new class of functional materials, exhibiting special thermomechanical behaviors, such as shape memory effect and superelasticity, which enable their applications in seismic engineering as energy dissipation devices. This paper investigates the properties of superelastic NiTi shape memory alloys, emphasizing the influence of strain rate on superelastic behavior under various strain amplitudes by cyclic tensile tests. A novel constitutive equation based on Graesser and Cozzarelli’s model is proposed to describe the strain-rate-dependent hysteretic behavior of superelastic SMAs at different strain levels. A stress variable including the influence of strain rate is introduced into Graesser and Cozzarelli’s model. To verify the effectiveness of the proposed constitutive equation, experiments on superelastic NiTi wires with different strain rates and strain levels are conducted. Numerical simulation results based on the proposed constitutive equation and experimental results are in good agreement. The findings in this paper will assist the future design of superelastic SMA-based energy dissipation devices for seismic protection of structures.

  8. Internal stresses in steel plate generated by shape memory alloy inserts

    Czech Academy of Sciences Publication Activity Database

    Malard, B.; Pilch, Jan; Šittner, Petr; Davydov, V.; Sedlák, Petr; Konstantinidis, K.; Hughes, D. J.

    2012-01-01

    Roč. 60, č. 3 (2012), s. 1378-1394 ISSN 1359-6454 R&D Projects: GA ČR GAP108/10/1296 Grant - others:SMARTNETS(XE) FP7-NMP2-2011-262806 Institutional research plan: CEZ:AV0Z10100520; CEZ:AV0Z20760514 Keywords : shape memory alloy * NiTi * residual stress * neutron diffraction * strain scanning Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.941, year: 2012 http://www.sciencedirect.com/science/article/pii/S1359645411007294

  9. Thermodynamic assessment of the stabilization effect in deformed shape memory alloy martensite

    International Nuclear Information System (INIS)

    Kato, Hiroyuki; Yasuda, Yohei; Sasaki, Kazuaki

    2011-01-01

    When a martensitic shape memory alloy is deformed, the reverse transformation occurs at higher temperature than that of undeformed martensite. This is a typical case of the stabilization effect of martensite that is commonly observed in shape memory alloys. Regarding previous results measured by electric resistance and/or dilatometoric methods in NiTi and CuAlNi shape memory alloys, this study has performed calorimetric measurement in these alloys in order to re-examine the stabilization effect in terms of thermodynamics. Experimental evidence for appreciable changes in the reverse transformation temperature due to variant change of the martensite is presented. The elastic energy stored in the deformed martensite and the irreversible energy dissipated during the reverse transformation are estimated from the transformation temperatures, the stress-strain curves of the martensite and the latent heat of transformation. The temperatures of the reverse martensitic transformation have been related to these energies in explicit form.

  10. A Constitutive Description for Shape Memory Alloys with the Growth of Martensite Band

    Directory of Open Access Journals (Sweden)

    Weiguo Li

    2014-01-01

    Full Text Available Based on the experimental results and the finite element analysis, a constitutive model is proposed for two phase shape memory alloys by introducing a compensative volumetric strain into a constrained relationship between the two phases, accounting for the reduced constraint due to the growth of martensite band. The pseudoelasticity of NiTi shape memory alloy micro-tube, subjected to pure tension, is analyzed and compared with the experimental results. It can be seen that the pseudoelastic behavior, especially the phenomena of a stress drop during tension processes, can be well described with the proposed model. The proposed model separates the complicated constitutive behavior of a shape memory alloy (SMA into simple responses arising respectively from its two phases, taking into account laminar microstructure, the thickness of martensite phase and the interaction between the two phases, and provides an easy but comprehensive method for the description of the constitutive behavior of SMAs under complex thermomechanical loading.

  11. Combining thermodynamic principles with Preisach models for superelastic shape memory alloy wires

    International Nuclear Information System (INIS)

    Doraiswamy, S; Rao, A; Srinivasa, A R

    2011-01-01

    We present a simple model for simulating the response of a superelastic shape memory alloy wire based on the thermodynamics of irreversible processes, which can simulate the full thermomechanical response including internal hysteresis loops, at different temperatures, with minimal data input. The key idea is to separate the dissipative response and the elastic response of shape memory alloys using a Gibbs potential based formulation, and then use a Preisach model for the dissipative part of the response. This enables better handling of the features observed in the superelastic response such as those due to changes in temperature and internal hysteresis loops. We compare the predicted response with experiments performed on 0.75 mm NiTi shape memory alloy wires at three different temperatures

  12. Microstructural evaluation of NiTi-based films deposited by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Crăciunescu, Corneliu M., E-mail: corneliu.craciunescu@upt.ro; Mitelea, Ion, E-mail: corneliu.craciunescu@upt.ro; Budău, Victor, E-mail: corneliu.craciunescu@upt.ro [Department of Materials and Manufacturing Engineering, Politehnica University of Timisoara (Romania); Ercuţa, Aurel [Department of Materials and Manufacturing Engineering, Politehnica University of Timisoara and Department of Physics, West University Timisoara (Romania)

    2014-11-24

    Shape memory alloy films belonging to the NiTi-based systems were deposited on heated and unheated substrates, by magnetron sputtering in a custom made system, and their structure and composition was analyzed using electron microscopy. Several substrates were used for the depositions: glass, Cu-Zn-Al, Cu-Al-Ni and Ti-NiCu shape memory alloy ribbons and kapton. The composition of the Ti-Ni-Cu films showed limited differences, compared to the one of the target and the microstructure for the DC magnetron sputtering revealed crystallized structure with features determined on peel off samples from a Si wafer. Both inter and transcrystalline fractures were observed and related to the interfacial stress developed on cooling from deposition temperature.

  13. Photostress analysis of stress-induced martensite phase transformation in superelastic NiTi

    International Nuclear Information System (INIS)

    Katanchi, B.; Choupani, N.; Khalil-Allafi, J.; Baghani, M.

    2017-01-01

    Phase transformation in shape memory alloys is the most important factor in their unique behavior. In this paper, the formation of stress induced martensite phase transformation in a superelastic NiTi (50.8% Ni) shape memory alloy was investigated by using the photo-stress method. First, the material's fabrication procedure has been described and then the material was studied using the metallurgical tests such as differential scanning calorimetry and X-ray diffraction to characterize the material features and the mechanical tensile test to investigate the superelastic behavior. As a new method in observation of the phase transformation, photo-stress pictures showed the formation of stress induced martensite in a superelastic dog-bone specimen during loading and subsequently it's disappearing during unloading. Finally, finite element analysis was implemented using the constitutive equations derived based on the Boyd-Lagoudas phenomenological model.

  14. Spallation in NiTi under One-Dimensional Shock Loading

    International Nuclear Information System (INIS)

    Wallwork, A.; Workman, A.; Meziere, Y. J. E.; Millett, J. C. F.; Bourne, N. K.

    2006-01-01

    The dynamic response of the shape memory alloy NiTi has been of interest to a number of investigators because it displays a shape memory effect. The dynamic tensile (spall) strength of this material is measured under one-dimensional shock loading. The loading stress pulse length and impact stress were varied to a peak stress of 15 GPa. The pull back stress (σpbs) was found to increase with the applied pulse length. This suggests that the dynamic tensile strength is dependent upon the generation of a deformation micro structure that evolves behind the shock front. In contrast, increasing stress levels result in a near-constant pull back stress, although at the lowest applied stress, spallation did not occur

  15. Photostress analysis of stress-induced martensite phase transformation in superelastic NiTi

    Energy Technology Data Exchange (ETDEWEB)

    Katanchi, B. [Mechanical Engineering Faculty, Sahand University of Technology, Tabriz (Iran, Islamic Republic of); Choupani, N., E-mail: choupani@sut.ac.ir [Mechanical Engineering Faculty, Sahand University of Technology, Tabriz (Iran, Islamic Republic of); Khalil-Allafi, J. [Research Center for Advance Materials, Faculty of Materials Engineering, Sahand University of Technology, Tabriz (Iran, Islamic Republic of); Baghani, M. [School of Mechanical Engineering, College of Engineering, University of Tehran (Iran, Islamic Republic of)

    2017-03-14

    Phase transformation in shape memory alloys is the most important factor in their unique behavior. In this paper, the formation of stress induced martensite phase transformation in a superelastic NiTi (50.8% Ni) shape memory alloy was investigated by using the photo-stress method. First, the material's fabrication procedure has been described and then the material was studied using the metallurgical tests such as differential scanning calorimetry and X-ray diffraction to characterize the material features and the mechanical tensile test to investigate the superelastic behavior. As a new method in observation of the phase transformation, photo-stress pictures showed the formation of stress induced martensite in a superelastic dog-bone specimen during loading and subsequently it's disappearing during unloading. Finally, finite element analysis was implemented using the constitutive equations derived based on the Boyd-Lagoudas phenomenological model.

  16. Self-centering and damping capabilities of a tension-compression device equipped with superelastic NiTi wires

    International Nuclear Information System (INIS)

    Soul, H; Yawny, A

    2015-01-01

    The hysteretic damping capacity and high recoverable strains characterizing the superelastic response of shape memory alloys (SMA) make these materials attractive for protection systems of structures subjected to dynamic loads. A successful implementation however is conditioned by functional fatigue exhibited by the SMA when subjected to cyclic loading. The residual deformation upon cycling and the efficiency in material usage are the two most restrictive issues in this sense. In this paper, a device equipped with superelastic NiTi SMA wires and capable of supporting external tension compression loads with optimized properties is presented. It is shown how the introduction of the wires’ pre-straining allows for the absorption of deleterious residual deformation without affecting the self-centering capabilities upon unloading, in contrast with what occurs for pre-strained tendons. These features were experimentally verified in an in-scale prototype composed of two 1.2 mm diameter superelastic NiTi SMA wires. In order to numerically assess the dynamic response of a simple structure subjected to seismic excitations, a multilinear superelasticity model for the NiTi wires was developed. (paper)

  17. Development of Biomimetic NiTi Alloy: Influence of Thermo-Chemical Treatment on the Physical, Mechanical and Biological Behavior

    Science.gov (United States)

    Rupérez, Elisa; Manero, José María; Bravo-González, Luis-Alberto; Espinar, Eduardo; Gil, F.J.

    2016-01-01

    A bioactive layer, free of nickel, has been performed for its greater acceptability and reliability in clinical applications for NiTi shape memory alloys. In the first step, a safe barrier against Ni release has been produced on the surface by means of a thicker rutile/anastase protective layer free of nickel. In the second step, a sodium alkaline titanate hydrogel, which has the ability to induce apatite formation, has been performed from oxidized surface. An improvement of host tissue–implant integration has been achieved in terms of Ni ions release and the bioactivity of the treated NiTi alloys has been corroborated with both in vitro and in vivo studies. The transformation temperatures (As, Af, Ms, and Mf), as well as the critical stresses (σβ⇔M), have been slightly changed due to this surface modification. Consequently, this fact must be taken into account in order to design new surface modification on NiTi implants. PMID:28773526

  18. Development of Biomimetic NiTi Alloy: Influence of Thermo-Chemical Treatment on the Physical, Mechanical and Biological Behavior

    Directory of Open Access Journals (Sweden)

    Elisa Rupérez

    2016-05-01

    Full Text Available A bioactive layer, free of nickel, has been performed for its greater acceptability and reliability in clinical applications for NiTi shape memory alloys. In the first step, a safe barrier against Ni release has been produced on the surface by means of a thicker rutile/anastase protective layer free of nickel. In the second step, a sodium alkaline titanate hydrogel, which has the ability to induce apatite formation, has been performed from oxidized surface. An improvement of host tissue–implant integration has been achieved in terms of Ni ions release and the bioactivity of the treated NiTi alloys has been corroborated with both in vitro and in vivo studies. The transformation temperatures (As, Af, Ms, and Mf, as well as the critical stresses (σβ⇔M, have been slightly changed due to this surface modification. Consequently, this fact must be taken into account in order to design new surface modification on NiTi implants.

  19. Shape memory heat engines

    Science.gov (United States)

    Salzbrenner, R.

    1984-06-01

    The mechanical shape memory effect associated with a thermoelastic martensitic transformation can be used to convert heat directly into mechanical work. Laboratory simulation of two types of heat engine cycles (Stirling and Ericsson) has been performed to measure the amount of work available/cycle in a Ni-45 at. pct Ti alloy. Tensile deformations at ambient temperature induced martensite, while a subsequent increase in temperature caused a reversion to the parent phase during which a load was carried through the strain recovery (i.e., work was accomplished). The amount of heat necessary to carry the engines through a cycle was estimated from calorimeter measurements and the work performed/cycle. The measured efficiency of the system tested reached a maximum of 1.4 percent, which was well below the theoretical (Carnot) maximum efficiency of 35.6 percent.

  20. Tailoring Selective Laser Melting Process Parameters for NiTi Implants

    Science.gov (United States)

    Bormann, Therese; Schumacher, Ralf; Müller, Bert; Mertmann, Matthias; de Wild, Michael

    2012-12-01

    Complex-shaped NiTi constructions become more and more essential for biomedical applications especially for dental or cranio-maxillofacial implants. The additive manufacturing method of selective laser melting allows realizing complex-shaped elements with predefined porosity and three-dimensional micro-architecture directly out of the design data. We demonstrate that the intentional modification of the applied energy during the SLM-process allows tailoring the transformation temperatures of NiTi entities within the entire construction. Differential scanning calorimetry, x-ray diffraction, and metallographic analysis were employed for the thermal and structural characterizations. In particular, the phase transformation temperatures, the related crystallographic phases, and the formed microstructures of SLM constructions were determined for a series of SLM-processing parameters. The SLM-NiTi exhibits pseudoelastic behavior. In this manner, the properties of NiTi implants can be tailored to build smart implants with pre-defined micro-architecture and advanced performance.

  1. Influence of Thin-Film Adhesives in Pullout Tests Between Nickel-Titanium Shape Memory Alloy and Carbon Fiber-Reinforced Polymer Matrix Composites

    Science.gov (United States)

    Quade, Derek J.; Jana, Sadhan; McCorkle, Linda S.

    2018-01-01

    Strips of nickel-titanium (NiTi) shape memory alloy (SMA) and carbon fiber-reinforced polymer matrix composite (PMC) were bonded together using multiple thin film adhesives and their mechanical strengths were evaluated under pullout test configuration. Tensile and lap shear tests were conducted to confirm the deformation of SMAs at room temperature and to evaluate the adhesive strength between the NiTi strips and the PMC. Optical and scanning electron microscopy techniques were used to examine the interfacial bonding after failure. Simple equations on composite tensile elongation were used to fit the experimental data on tensile properties. ABAQUS models were generated to show the effects of enhanced bond strength and the distribution of stress in SMA and PMC. The results revealed that the addition of thin film adhesives increased the average adhesive strength between SMA and PMC while halting the room temperature shape memory effect within the pullout specimen.

  2. Grippers for the micro assembly containing shape memory actuators and sensors

    International Nuclear Information System (INIS)

    Mertmann, M.; Hornbogen, E.

    1997-01-01

    Shape memory alloys (SMA) show a high ratio of work capacity per material volume. This makes the application of SMA especially useful in micron-sized systems. The development of robotic grippers is one important prerequisite for the successful automation of the assembly of micro systems. Therefore the SMA may also play a role, for example, as actuators in micron-sized grippers. This paper presents the development of micron-sized grippers. Due to a special relation between the electrical resistance and the shape change of a NiTi-wire the actuator may also be used simultaneously as a sensor. Besides these functional properties a superelastic SMA may be used for structural purposes, i.e. as solid-state flexure hinges. The sensoric features of binary and ternary NiTi-based alloys are investigated using different Ti 50 Ni 50-x Cu x alloys with 0 50 Ni 50-x Cu x alloys and their influence on the functional properties are compared. The effect of the TMT on the amount and the stability of the shape memory effect has to be taken into account if the optimum alloy and condition for the use in grippers for micro assembly are investigated. The function and the properties of the developped gripping devices are demonstrated by prototypes. (orig.)

  3. Ferromagnetic shape memory materials

    Science.gov (United States)

    Tickle, Robert Jay

    Ferromagnetic shape memory materials are a new class of active materials which combine the properties of ferromagnetism with those of a diffusionless, reversible martensitic transformation. These materials have been the subject of recent study due to the unusually large magnetostriction exhibited in the martensitic phase. In this thesis we report the results of experiments which characterize the magnetic and magnetomechanical properties of both austenitic and martensitic phases of ferromagnetic shape memory material Ni2MnGa. In the high temperature cubic phase, anisotropy and magnetostriction constants are determined for a range of temperatures from 50°C down to the transformation temperature, with room temperature values of K1 = 2.7 +/- 104 ergs/cm3 and lambda100 = -145 muepsilon. In the low temperature tetragonal phase, the phenomenon of field-induced variant rearrangement is shown to produce anomalous results when traditional techniques for determining anisotropy and magnetostriction properties are employed. The requirement of single variant specimen microstructure is explained, and experiments performed on such a specimen confirm a uniaxial anisotropy within each martensitic variant with anisotropy constant Ku = 2.45 x 106 ergs/cm3 and a magnetostriction constant of lambdasv = -288 +/- 73 muepsilon. A series of magnetomechanical experiments investigate the effects of microstructure bias, repeated field cycling, varying field ramp rate, applied load, and specimen geometry on the variant rearrangement phenomenon in the martensitic phase. In general, the field-induced strain is found to be a function of the variant microstructure. Experiments in which the initial microstructure is biased towards a single variant state with an applied load generate one-time strains of 4.3%, while those performed with a constant bias stress of 5 MPa generate reversible strains of 0.5% over a period of 50 cycles. An increase in the applied field ramp rate is shown to reduce the

  4. My Experience with Ti-Ni-Based and Ti-Based Shape Memory Alloys

    Science.gov (United States)

    Miyazaki, Shuichi

    2017-12-01

    The present author has been studying shape memory alloys including Cu-Al-Ni, Ti-Ni-based, and Ni-free Ti-based alloys since 1979. This paper reviews the present author's research results for the latter two materials since 1981. The topics on the Ti-Ni-based alloys include the achievement of superelasticity in Ti-Ni alloys through understanding of the role of microstructures consisting of dislocations and precipitates, followed by the contribution to the development of application market of shape memory effect and superelasticity, characterization of the R-phase and monoclinic martensitic transformations, clarification of the basic characteristics of fatigue properties, development of sputter-deposited shape memory thin films and fabrication of prototypes of microactuators utilizing thin films, development of high temperature shape memory alloys, and so on. The topics of Ni-free Ti-based shape memory alloys include the characterization of the orthorhombic phase martensitic transformation and related shape memory effect and superelasticity, the effects of texture, omega phase and adding elements on the martensitic transformation and shape memory properties, clarification of the unique effects of oxygen addition to induce non-linear large elasticity, Invar effect and heating-induced martensitic transformation, and so on.

  5. Multimodal Nanoscale Characterization of Transformation and Deformation Mechanisms in Several Nickel Titanium Based Shape Memory Alloys

    Science.gov (United States)

    Casalena, Lee

    The development of viable high-temperature shape memory alloys (HTSMAs) demands a coordinated multimodal characterization effort linking nanoscale crystal structure to macroscale thermomechanical properties. In this work, several high performance NiTi-based shape memory alloys are comprehensively explored with the goal of gaining insight into the complex transformation and deformation mechanisms responsible for their remarkable behavior. Through precise control of alloying and aging parameters, microstructures are optimized to enhance properties such as high-temperature strength and stability. These are crucial requirements for the development of advanced applications such as actuators and adaptive components that operate in demanding automotive and aerospace environments. An array of NiTiHf and NiTiAu alloys are at the core of this effort, offering the possibility of increased capability over traditional pneumatic and hydraulic systems, while simultaneously reducing weight and energy requirements. NiTi-20Hf alloys exhibit a favorable balance of properties, including high strength, stability, and work output at temperatures in excess of 150 °C. The raw material cost of Hf is also much lower compared with Pt, Pd, and Au containing counterparts. Advanced scanning transmission electron microscopy (STEM) and synchrotron X-ray characterization techniques are used to explore unusual nanoscale effects of precipitate-matrix interactions, coherency strain, and dislocation activity in these alloys. Novel use of the 4D STEM strain mapping technique is used to quantify strain fields associated with precipitates, which are being coupled with new phase field modeling approaches to particle/defect interactions. Volume fractions of nanoscale precipitates are measured using STEM-based tomography techniques, atom probe tomography, and synchrotron diffraction of bulk samples. Plastic deformation of the HTSMA austenite phase is shown to occur through B2 type slip for the first time

  6. Internal stresses in steel plate generated by shape memory alloy inserts

    International Nuclear Information System (INIS)

    Malard, B.; Pilch, J.; Sittner, P.; Davydov, V.; Sedlák, P.; Konstantinidis, K.; Hughes, D.J.

    2012-01-01

    Graphical abstract: Display Omitted Highlights: ► Thermoresponsive internal stresses introduced into steel by embedding SMA inclusions. ► Neutron strain scanning on steel plate coupons with NiTi inserts at 21 °C and 130 °C. ► Internal stress field in steel evaluated directly from strains and by FE simulation. ► Internal stress generation by SMA insert resistant to thermal and mechanical fatigue. - Abstract: Neutron strain scanning was employed to investigate the internal stress fields in steel plate coupons with embedded prestrained superelastic NiTi shape memory alloy inserts. Strain fields in steel were evaluated at T = 21 °C and 130 °C on virgin coupons as well as on mechanically and thermally fatigued coupons. Internal stress fields were evaluated by direct calculation of principal stress components from the experimentally measured lattice strains as well as by employing an inverse finite element modeling approach. It is shown that if the NiTi inserts are embedded into the elastic steel matrix following a carefully designed technological procedure, the internal stress fields vary with temperature in a reproducible and predictable way. It is estimated that this mechanism of internal stress generation can be safely applied in the temperature range from −20 °C to 150 °C and is relatively resistant to thermal and mechanical fatigue. The predictability and fatigue endurance of the mechanism are of essential importance for the development of future smart metal matrix composites or smart structures with embedded shape memory alloy components.

  7. Atomic layer-deposited Al.sub.2./sub.O.sub.3./sub. coatings on NiTi alloy

    Czech Academy of Sciences Publication Activity Database

    Kei, C.C.; Yu, Y.S.; Racek, Jan; Vokoun, David; Šittner, Petr

    2014-01-01

    Roč. 23, č. 7 (2014), s. 2641-2649 ISSN 1059-9495. [International Conference on Shape Memory and Superelastic Technologies (SMST 2013). Praha, 21.05.2013-24.05.2013] R&D Projects: GA ČR(CZ) GA101/09/0702; GA MŠk(CZ) 7E11058 EU Projects: European Commission(XE) 262806 - SmartNets Institutional support: RVO:68378271 Keywords : ALD * Al 2 O 3 coating * corrosion * NiTi Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.998, year: 2014

  8. Properties and medical applications of shape memory alloys.

    Science.gov (United States)

    Tarniţă, Daniela; Tarniţă, D N; Bîzdoacă, N; Mîndrilă, I; Vasilescu, Mirela

    2009-01-01

    One of the most known intelligent material is nitinol, which offers many functional advantages over conventional implantable alloys. Applications of SMA to the biomedical field have been successful because of their functional qualities, enhancing both the possibility and the execution of less invasive surgeries. The biocompatibility of these alloys is one of their most important features. Different applications exploit the shape memory effect (one-way or two-way) and the super elasticity, so that they can be employed in orthopedic and cardiovascular applications, as well as in the manufacture of new surgical tools. Therefore, one can say that smart materials, especially SMA, are becoming noticeable in the biomedical field. Super elastic NiTi has become a material of strategic importance as it allows to overcome a wide range of technical and design issues relating to the miniaturization of medical devices and the increasing trend for less invasive and therefore less traumatic procedures. This paper will consider just why the main properties of shape memory alloys hold so many opportunities for medical devices and will review a selection of current applications.

  9. Influence of the thermal treatment on the stability of partially constrained recovery of NiTi actuator wire

    International Nuclear Information System (INIS)

    Mertmann, M.; Bracke, A.; Hornbogen, E.

    1995-01-01

    NiTi shape memory wire may be used for actuation purposes in flexible robotic grippers, which have to be able to handle objects of different size, shape or weight. Therefore it is advantageous to develop an electrically driven shape memory actuator, which may perform any combination of shape change and exerted force within the following limiting boundaries: - free recovery: gripping of a very small and lightweight object, - constrained recovery: gripping of an object with maximum size and weight. Several NiTi actuator wires are fabricated and annealed between 400 and 600 C after cold working in the martensitic state. After prestraining each wire is embedded in a silicone matrix material. The polymer works as a bias spring and is able to store elastic deformation energy. This paper investigates the influence of thermal treatment on the stability of the exerted force between the two boundaries of completely free and constrained recovery, the ''partially constrained recovery''. The stability of recovery strain and stress is measured in a test assembly, in which different modes of partially constrained recovery are simulated. The work is supplemented by dilatometric measurements carried out with each actuator wire before and after the test procedure. (orig.)

  10. Low temperature nickel titanium iron shape memory alloys: Actuator engineering and investigation of deformation mechanisms using in situ neutron diffraction at Los Alamos National Laboratory

    Science.gov (United States)

    Krishnan, Vinu B.

    Shape memory alloys are incorporated as actuator elements due to their inherent ability to sense a change in temperature and actuate against external loads by undergoing a shape change as a result of a temperature-induced phase transformation. The cubic so-called austenite to the trigonal so-called R-phase transformation in NiTiFe shape memory alloys offers a practical temperature range for actuator operation at low temperatures, as it exhibits a narrow temperature-hysteresis with a desirable fatigue response. Overall, this work is an investigation of selected science and engineering aspects of low temperature NiTiFe shape memory alloys. The scientific study was performed using in situ neutron diffraction measurements at the newly developed low temperature loading capability on the Spectrometer for Materials Research at Temperature and Stress (SMARTS) at Los Alamos National Laboratory and encompasses three aspects of the behavior of Ni46.8Ti50Fe3.2 at 92 K (the lowest steady state temperature attainable with the capability). First, in order to study deformation mechanisms in the R-phase in NiTiFe, measurements were performed at a constant temperature of 92 K under external loading. Second, with the objective of examining NiTiFe in one-time, high-stroke, actuator applications (such as in safety valves), a NiTiFe sample was strained to approximately 5% (the R-phase was transformed to B19' phase in the process) at 92 K and subsequently heated to full strain recovery under a load. Third, with the objective of examining NiTiFe in cyclic, low-stroke, actuator applications (such as in cryogenic thermal switches), a NiTiFe sample was strained to 1% at 92 K and subsequently heated to full strain recovery under load. Neutron diffraction spectra were recorded at selected time and stress intervals during these experiments. The spectra were subsequently used to obtain quantitative information related to the phase-specific strain, texture and phase fraction evolution using the

  11. Influence of the particle size on phase transformation temperatures of Ni-49at.%Ti shape memory alloy powders

    International Nuclear Information System (INIS)

    Anselmo, George Carlos. S.; Castro, Walman B. de; Araujo, Carlos Jose de

    2009-01-01

    It is important to control the martensitic transformation start temperature (Ms) of Ti-Ni alloys because it determines the temperature range over which the shape memory effect and superelasticity appear. Powder metallurgy (PM) is known to provide the possibility of material saving and automated fabrication of at least semi-finished products as well as net-shape components for NiTi alloys. In this study powder with different particle sizes was subjected by gas atomization. The evolution of the control the martensitic transformation start temperature (Ms) was studied by differential scanning calorimetry. The effect of the particle size of powders on the transformation temperatures behaviors was discussed. (author)

  12. New developments in Ni/Ti multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Anderson, I; Hoghoj, P [Institut Max von Laue - Paul Langevin (ILL), 38 - Grenoble (France)

    1997-04-01

    It is now 20 years since super-mirrors were first used as a neutron optical element. Since then the field of multilayer neutron-optics has matured with multilayers finding their way to application in many neutron scattering instruments. However, there is still room for progress in terms of multilayer quality, performance and application. Along with work on multilayers for neutron polarisation Ni/Ti super-mirrors have been optimised. The state-of-the-art Ni/Ti super-mirror performance and the results obtained in two neutron-optics applications of Ni/Ti multilayers are presented. (author).

  13. Behavior of NiTiNb SMA wires under recovery stress or prestressing.

    Science.gov (United States)

    Choi, Eunsoo; Nam, Tae-Hyun; Chung, Young-Soo; Kim, Yeon-Wook; Lee, Seung-Yong

    2012-01-05

    The recovery stress of martensitic shape-memory alloy [SMA] wires can be used to confine concrete, and the confining effectiveness of the SMA wires was previously proved through experimental tests. However, the behavior of SMA wires under recovery stress has not been seriously investigated. Thus, this study conducted a series of tests of NiTiNb martensitic SMA wires under recovery stress with varying degrees of prestrain on the wires and compared the behavior under recovery stress with that under prestressing of the wires. The remaining stress was reduced by the procedure of additional strain loading and unloading. More additional strains reduced more remaining stresses. When the SMA wires were heated up to the transformation temperature under prestress, the stress on the wires increased due to the state transformation. Furthermore, the stress decreased with a decreasing temperature of the wires down to room temperature. The stress of the NiTiNb wires was higher than the prestress, and the developed stress seemed to depend on the composition of the SMAs. When an additional strain was subsequently loaded and unloaded on the prestressed SMA wires, the remaining stress decreased. Finally, the remaining stress becomes zero when loading and unloading a specific large strain.

  14. The effect of TiO2 coating on biological NiTi alloys after micro-arc oxidation treatment for corrosion resistance.

    Science.gov (United States)

    Sukuroglu, Ebru Emine; Sukuroglu, Suleyman; Akar, Kubra; Totik, Yasar; Efeoglu, Ihsan; Arslan, Ersin

    2017-08-01

    NiTi alloys exhibit good properties, such as shape memory behavior, high corrosion resistant, having the closest elasticity modulus of a human bone and superior biocompatibility properties. However, the surface problems that arise during the use of this alloy limit the usage in the industry and health sector. In recent years, micro-arc oxidation method is used to improve the surface properties and increase the usage of these alloys. In this study, the TiO 2 coatings were deposited on the NiTi substrates. The surface topography, morphology, crystallographic structure, and thickness of the coatings were determined using scanning electron microscopy and X-ray diffraction. The corrosion properties were investigated using potentiostat test unit in two different media such as NaCl solution and simulated body fluid. The results show that the coated samples have higher corrosion resistance than uncoated samples in the two different media.

  15. Deformation of shape memory alloys associated with twinned domain re-configurations

    International Nuclear Information System (INIS)

    Liu Yong; Van Humbeeck, J.; Xie Zeliang; Delaey, L.

    1999-01-01

    Most of the applications of shape memory alloys (SMAs) imply deformation of martensite; it is therefore one of the fundamental research topics on the shape memory effect. So far, several classifications of the deformation mechanisms have been made as a function of deformation amplitude. However, the deformation details of martensitic SMAs are still not yet satisfactorily understood and these classifications need to be refined, because several incoherencies have been found lately by mechanical testing and transmission electron microscopy (TEM) observations. The present work summarizes some new results on the deformation mechanisms of martensitic NiTi SMAs under tension. As a result, the deformation process of martensite twins as a function of the deformation strain amplitude is refined. (orig.)

  16. Thermo-Mechanical Behavior and Shakedown of Shape Memory Alloy Cable Structures

    Science.gov (United States)

    Biggs, Daniel B.

    Shape memory alloys (SMAs) are a versatile class of smart materials that exhibit adaptive properties which have been applied to solve engineering problems in wide-ranging fields from aerospace to biomedical engineering. Yet there is a lack of understanding of the fundamental nature of SMAs in order to effectively apply them to challenging problems within these engineering fields. Stranding fine NiTi wires into a cable form satisfies the demands of many aerospace and civil engineering applications which require actuators to withstand large tensile loads. The impact of increased bending and twisting in stranded NiTi wire structures, as well as introducing contact mechanics to the unstable phase transformation is not well understood, and this work aims to fill that void. To study the scalability of NiTi cables, thermo-mechanical characterization tests are conducted on cables much larger than those previously tested. These cables are found to have good superelastic properties and repeatable cyclic behavior with minimal induced plasticity. The behavior of additional cables, which have higher transition temperatures that can be used in a shape memory mode as thermo-responsive, high force actuator elements, are explored. These cables are found to scale up the performance of straight wire by maintaining an equivalent work output. Moreover, this work investigates the degradation of the thermal actuation of SMA wires through novel stress-temperature paths, discovering several path dependent behaviors of transformation-induced plasticity. The local mechanics of NiTi cable structures are explored through experiments utilizing digital image correlation, revealing new periodic transformation instabilities. Finite element simulations are presented, which indicate that the instabilities are caused by friction and relative sliding between wires in a cable. Finally, a study of the convective heat transfer of helical wire involving a suite of wind tunnel experiments, numerical

  17. Mechanical characterisation of orthodontic superelastic Ni-Ti wires

    Energy Technology Data Exchange (ETDEWEB)

    Arrigoni, M.; Pietrabissa, R. [Politecnico di Milano, Milano (Italy). Lab. of Biological Structure Mechanics; Auricchio, F.; Petrini, L. [Politecnico di Milano, Milano (Italy). Lab. of Biological Structure Mechanics; Pavia Univ. (Italy). Dept. of Structural Mechanics; Cacciafesta, V. [Politecnico di Milano, Milano (Italy). Lab. of Biological Structure Mechanics; Pavia Univ. (Italy). Dept. of Orthodontia

    2001-11-01

    Nowadays, the orthodontic treatment is improving thanks to the introduction of Ni-Ti super-elastic alloy wires in the ordinary therapy. Indeed, laboratory tests performed in the last decade have shown that Ni-Ti superelastic wires are able to satisfy the ideal requirements for fixed arch-wire appliance: high flexibility, minimal distortion or plastic deformation, light constant force production over a wide range of displacements. On the other hand, many orthodontic companies produce Ni-Ti arch-wires, without giving detailed specifications on their superelastic characteristics. To improve the knowledge on real properties for these products, an experimental campaign on different commercial arch-wires has been started at the Laboratory of Biological Structure Mechanics (LABS) at the Politecnico di Milano (Italy). This work presents the first step of the research, concerning the comparison between the behaviour of four types of wires (two produced by ORMCO and two produced by 3M/Unitek) under monotonic and cyclic isothermal tensile tests. The results show significant differences between the products in terms of elastic modulus, stress values of the loading-unloading plateau, hysteresis amplitude, spring-back capacity, shape recovery capability, strain rate effect and fatigue behaviour. (orig.)

  18. Martensitic phase transformation in shape-memory alloys

    International Nuclear Information System (INIS)

    Golestaneh, A.A.

    1979-01-01

    Isothermal studies are described of the shape-recovery phenomenon, stress-strain behavior, electrical resistivity and thermo-electric power associated with the martensite-parent phase reaction in the Ni-Ti shape-memory alloys. The energy-balance equation that links the reaction kinetics with the strain energy change during the cooling-deforming and heating cycle is analyzed. The strain range in which the Clausius-Clapeyron equation satisfactorily describes this reaction is determined. A large change in the Young's modulus of the specimen is found to be associated with the M → P reaction. A hysteresis loop in the resistivity-temperature plot is found and related to the anomaly in the athermal resistivity changes during cyclic M → P → M transformation. An explanation for the resistivity anomaly is offered. The M structure is found to be electrically negative relative to the P structure. A thermal emf of greater than or equal to 0.12 mV is found at the M-P interface

  19. Thermoviscoelastic shape memory behavior for epoxy-shape memory polymer

    International Nuclear Information System (INIS)

    Chen, Jianguo; Liu, Liwu; Liu, Yanju; Leng, Jinsong

    2014-01-01

    There are various applications for shape memory polymer (SMP) in the smart materials and structures field due to its large recoverable strain and controllable driving method. The mechanical shape memory deformation mechanism is so obscure that many samples and test schemes have to be tried in order to verify a final design proposal for a smart structure system. This paper proposes a simple and very useful method to unambiguously analyze the thermoviscoelastic shape memory behavior of SMP smart structures. First, experiments under different temperature and loading conditions are performed to characterize the large deformation and thermoviscoelastic behavior of epoxy-SMP. Then, a rheological constitutive model, which is composed of a revised standard linear solid (SLS) element and a thermal expansion element, is proposed for epoxy-SMP. The thermomechanical coupling effect and nonlinear viscous flowing rules are considered in the model. Then, the model is used to predict the measured rubbery and time-dependent response of the material, and different thermomechanical loading histories are adopted to verify the shape memory behavior of the model. The results of the calculation agree with experiments satisfactorily. The proposed shape memory model is practical for the design of SMP smart structures. (paper)

  20. Rheological study of feed stock for NiTi alloy molded parts

    International Nuclear Information System (INIS)

    Subuki, I; Abdullah, Z; Razali, R; Ismail, M H

    2015-01-01

    A rheological behaviour of the powder-binder mixture is one of essential analysis upon to success of Metal Injection Moulding (MIM) process. The purpose of this experimental work is to investigate the rheological behavior of feedstock containing mixtures of elemental Ni and Ti powders mixed with composite binder of palm stearin (PS) and polyethylene (PE) binder system. An equiatomic Ni-Ti (50-50) ratio was used in the present work for all formulations owing to excellent shape memory behaviour. The experimental rheological result indicated that all the feedstocks exhibited pseudo plastic flow behaviour; viscosity decreasing with temperature and shear rate. Increasing the powder loading resulted in higher viscosity, particularly at the low-range of shear rate. Owing to pseudo-plastic flow, it was found that the feedstock prepared exhibit promising rheological properties, thus resulting successfully injection moulding at an optimum temperature of 130°C. (paper)

  1. Non-Conventional Techniques for the Study of Phase Transitions in NiTi-Based Alloys

    Science.gov (United States)

    Nespoli, Adelaide; Villa, Elena; Passaretti, Francesca; Albertini, Franca; Cabassi, Riccardo; Pasquale, Massimo; Sasso, Carlo Paolo; Coïsson, Marco

    2014-07-01

    Differential scanning calorimetry and electrical resistance measurements are the two most common techniques for the study of the phase transition path and temperatures of shape memory alloys (SMA) in stress-free condition. Besides, it is well known that internal friction measurements are also useful for this purpose. There are indeed some further techniques which are seldom used for the basic characterization of SMA transition: dilatometric analysis, magnetic measurements, and Seebeck coefficient study. In this work, we discuss the attitude of these techniques for the study of NiTi-based phase transition. Measurements were conducted on several fully annealed Ni50- x Ti50Cu x samples ranging from 3 to 10 at.% in Cu content, fully annealed at 850 °C for 1 h in vacuum and quenched in water at room temperature. Results show that all these techniques are sensitive to phase transition, and they provide significant information about the existence of intermediate phases.

  2. Shape memory effect for titanium nickelide semiproducts

    International Nuclear Information System (INIS)

    Chernov, D.B.; Fatkullina, L.P.; Smirnova, Z.I.; Timonin, G.D.; Olejnikova, S.V.

    1978-01-01

    The thermomechanical properties of titanium nickelide semi-finished products obtained by garnissage melting followed by arc remelting have been studied for the purpose of investigating the NiTi ''form memory'' mechanism. The ingots were subjected to stepped pressing to produce rods. Calcined rods were tension tested. Investigation of the elastic and thermomechanical free return after deformation has shown that the share of elastic return increases as the preliminary deformation degree is increased. The return to the original form began at about 150 deg C; at 200 deg C the process rate decreases and at 300 deg C it stops. The degree of form recovery decreases with the increase of preliminary deformation. The return stress versus preliminary deformation degree relationship has a maximum at 11% strain degree. Maximum thermomechanical return stresses are observed at about 300 deg C. It is noted that yield strength decreases with the increasing degree of deformation to which the semi-finished products are subjected

  3. Shape memory alloy wires turn composites into smart structures: I. Material requirements

    Science.gov (United States)

    Schrooten, Jan; Michaud, Veronique J.; Zheng, Yanjun; Balta-Neumann, J. Antonio; Manson, Jan-Anders E.

    2002-07-01

    Composites containing thin Shape Memory Alloy (SMA) wires show great potential as materials able to adapt their shape, thermal behavior or vibrational properties to external stimuli. The functional properties of SMA-composites are directly related to the constraining effect of the matrix on the reversible martensitic transformation of the embedded pre-strained SMA wires. The present work reports results of a concerted European effort towards a fundamental understanding of the manufacturing and design of SMA composites. This first part investigates the transformational behavior of constrained SMA wires and its translation into functional properties of SMA composites. Thermodynamic and thermomechanical experiments were performed on SMA wires. A model was developed to simulate the thermomechanical behavior of the wires. From the screening of potential wires it was concluded that NiTiCu, as well as R-phase NiTi appeared as best candidates. Requirements for the host composite materials were surveyed. A Kevlar-epoxy system was chosen. Finally, the quality of the SMA wire-resin interface was assessed by two different techniques. These indicated that a thin oxide layer seems to provide the best interfacial strength. A temperature window in which SMA composites can be safely used was also defined. The manufacturing and properties of the SMA composites will be discussed in Part II.

  4. Shape memory polymer foams for endovascular therapies

    Energy Technology Data Exchange (ETDEWEB)

    Wilson, Thomas S.; Maitland, Duncan J.

    2017-03-21

    A system for occluding a physical anomaly. One embodiment comprises a shape memory material body wherein the shape memory material body fits within the physical anomaly occluding the physical anomaly. The shape memory material body has a primary shape for occluding the physical anomaly and a secondary shape for being positioned in the physical anomaly.

  5. Shape memory polymer foams for endovascular therapies

    Science.gov (United States)

    Wilson, Thomas S [Castro Valley, CA; Maitland, Duncan J [Pleasant Hill, CA

    2012-03-13

    A system for occluding a physical anomaly. One embodiment comprises a shape memory material body wherein the shape memory material body fits within the physical anomaly occluding the physical anomaly. The shape memory material body has a primary shape for occluding the physical anomaly and a secondary shape for being positioned in the physical anomaly.

  6. Fabrication of a smart air intake structure using shape memory alloy wire embedded composite

    International Nuclear Information System (INIS)

    Jung, Beom-Seok; Kim, Min-Saeng; Kim, Ji-Soo; Kim, Yun-Mi; Lee, Woo-Yong; Ahn, Sung-Hoon

    2010-01-01

    Shape memory alloys (SMAs) have been actively studied in many fields utilizing their high energy density. Applying SMA wire-embedded composite to aerospace structures, such as air intake of jet engines and guided missiles, is attracting significant attention because it could generate a comparatively large actuating force. In this research, a scaled structure of SMA wire-embedded composite was fabricated for the air intake of aircraft. The structure was composed of several prestrained Nitinol (Ni-Ti) SMA wires embedded in intersection -shape glass fabric reinforced plastic (GFRP), and it was cured at room temperature for 72 h. The SMA wire-embedded GFRP could be actuated by applying electric current through the embedded SMA wires. The activation angle generated from the composite structure was large enough to make a smart air intake structure.

  7. Hydrodynamic characterization of a passive shape memory alloy valve

    International Nuclear Information System (INIS)

    Waddell, A M; Punch, J; Stafford, J; Jeffers, N

    2014-01-01

    Next generation high-performance electronics will have large heat fluxes (>10 2 W/cm 2 ) and an alternative approach to traditional air cooling is required. An attractive solution is micro-channel cooling and micro-valves will be required for refined flow control in the supporting micro-fluidic systems. A NiTi Shape Memory Alloy (SMA) micro-valve design was hydrodynamically characterized in this work to obtain the valve loss coefficient (K) from pressure measurements. The hydrodynamic characterization was important as in the flow regime of the micro-fluidic system K is sensitive to Reynolds number (Re) and geometry. Static replicas of the SMA valve geometry were studied for low Reynolds numbers (110 – 220) in a 1x1 mm CSA miniature channel. The loss coefficients were found to be sensitive to flow rate and decreased rapidly with an increase in Re. The SMA valve was compared to a similar gate micro-valve and loss across both valves was of the same order of magnitude. The valve loss coefficients obtained in this work are important parameters in the modeling and design of micro-fluidic cooling systems.

  8. Shape Memory Alloy (SMA)-Based Launch Lock

    Science.gov (United States)

    Badescu, Mircea; Bao, Xiaoqi; Bar-Cohen, Yoseph

    2014-01-01

    Most NASA missions require the use of a launch lock for securing moving components during the launch or securing the payload before release. A launch lock is a device used to prevent unwanted motion and secure the controlled components. The current launch locks are based on pyrotechnic, electro mechanically or NiTi driven pin pullers and they are mostly one time use mechanisms that are usually bulky and involve a relatively high mass. Generally, the use of piezoelectric actuation provides high precession nanometer accuracy but it relies on friction to generate displacement. During launch, the generated vibrations can release the normal force between the actuator components allowing shaft's free motion which could result in damage to the actuated structures or instruments. This problem is common to other linear actuators that consist of a ball screw mechanism. The authors are exploring the development of a novel launch lock mechanism that is activated by a shape memory alloy (SMA) material ring, a rigid element and an SMA ring holding flexure. The proposed design and analytical model will be described and discussed in this paper.

  9. The elastocaloric effect of Ni50.8Ti49.2 shape memory alloys

    Science.gov (United States)

    Zhou, Min; Li, Yushuang; Zhang, Chen; Li, Shaojie; Wu, Erfu; Li, Wei; Li, Laifeng

    2018-04-01

    Solid-state cooling technologies are considered as possible alternatives for vapor compression cooling systems. The elastocaloric cooling (whose caloric effects are driven by uniaxial stress) technology, as an efficient and clean solid-state cooling technology, is receiving a great deal of attention very recently. Herein, a NiTi-based elastocaloric bulk material was reported. A large coefficient-of-performance of the material (COPmater) of 4.5 was obtained, which was even higher than that of other NiTi bulk materials. The temperature changes (ΔT) increased with increasing applied strain (ɛ), and reached 18 K upon loading and  -11 K upon unloading when the ɛ value increased to 4%. The high temperature changes were attributed to the large stress-induced entropy changes (the maximum ΔS σ value was 37 J kg-1 K-1). The temperature changes decreased with loading-unloading tensile cycles, and stabilized at 6.5 K upon loading and  -6 K upon unloading after tens of mechanical cycles. The Ni50.8Ti49.2 shape memory alloy showed great promise for application in solid-state refrigeration (or as heat pumps).

  10. Production and characterization of stainless steel based Fe-Cr-Ni-Mn-Si(-Co) shape memory alloys

    International Nuclear Information System (INIS)

    Otubo, J.

    1995-01-01

    It is well known that the Fe based alloys can exhibit shape memory effect due to the γ to ε martensitic transformation. The effect may not be as striking as observed in the NiTi alloy but it might become attractive from the practical point of view. In this work, two compositions of Fe-Cr-Ni-Mn-Si(-Co) stainless steel based shape memory alloy, prepared by the VIM technique, will be presented. The results are good with shape recovery of 95% for a pre-strain of 4% after some training cycles. In terms of workability the alloys produced are worse than the usual AISI304. However, adjusting the thermo-mechanical processing, it is perfectly possible to produce wire as thin as 1,20mm in dia. or down. (orig.)

  11. High frequency and magnetoelectrical properties of magnetoresistive memory element based on FeCoNi/TiN/FeCoNi film

    Directory of Open Access Journals (Sweden)

    Kurlyandskaya, G. V.

    2000-08-01

    Full Text Available A miniaturised memory device for information recording and readout processes have been designed on the basis of anisotropic magnetoresistive effect in Fe15Co20Ni65(160Å/ TiN(50Å/Fe15Co20Ni65(160Å three-layered film done by rf diode sputtering. Stable recording and readout processes were available for 32 rectangular element column, where each element had μm dimensions convenient to fabricate memory chip with 106 bits capacity. Rectangles of different sizes with removed corners were used in order to define the geometry of most of all stable recording and readout processes. Magnetoresistance and magnetoimpedance effects of a magnetic memory device have been comparatively analysed. We suggest that the decrease of the absolute value of the magnetoimpedance of the memory device comes from the reduction of the real part via the magnetoresistance.

    Se ha diseñado un dispositivo de memoria para la grabación y lectura de información basado en el efecto de la anisotropía magnetorresistiva de una multicapa fabricada por sputtering mediante diodo de rf. El elemento de memoria se compone de tres películas delgadas, de composición Fe15Co20Ni65(160Å/ TiN(50Å/Fe15Co20Ni65(160Å. El dispositivo permite procesos de grabación y lectura estables, y se compone de 32 elementos de memoria rectangulares por columna, donde cada elemento tiene dimensiones de μm lo que permite la fabricación de memorias integradas con capacidades del orden de 106 bits. Se han ensayado elementos de memoria rectangulares de diferentes tamaños, con las esquinas redondeadas con objeto de conseguir procesos de lectura-escritura lo más estable posible. Se han analizado comparativamente los efectos de magnetorresistencia y magnetoimpedancia de los elementos de memoria de diferentes dimensiones. Sugerimos que la disminución del valor absoluto de la magnetoimpedancia del elemento de memoria es consecuencia de la reducción de la parte real, de origen magnetorresistivo.

  12. Novel micro-patterning processes for thin film NiTi vascular devices

    International Nuclear Information System (INIS)

    Chun, Y J; Mohanchandra, K P; Carman, G P; Levi, D S; Fishbein, M C

    2010-01-01

    In order to create microscale features in thin film NiTi for use in vascular endografts, a novel 'lift-off process' was developed for use with deep reactive ion etching. A wet etching approach is compared to two variations of this new 'lift-off' process. The first lift-off process (lift-off I) used Si posts to define the features of NiTi film deposited on the Si substrate. This method produced fractures in the NiTi when the film was released. The lift-off II process used Si islands as substrate for the film while the Si wafer defined the specific geometric features. Lift-off II process allowed for the creation of various shape patterns (i.e., ellipse, diamond, circle, square, etc) in the range of 5–180 µm. The lift-off II process produced smooth and well aligned micro-patterns in thin film NiTi without the undercutting found in wet etching techniques. The micro-patterned thin film NiTi formed from the lift-off II process was used to cover a stent. In vivo tests were performed to evaluate the endothelialization though patterned thin films. Angiography, histopathology and SEM showed patency of the artery and uniformly promoted endothelial layer covering without thrombosis in both a medium and small artery

  13. Machining NiTi micro-parts by micro-milling

    International Nuclear Information System (INIS)

    Weinert, K.; Petzoldt, V.

    2008-01-01

    The machinability of NiTi by milling has been examined using solid carbide end milling cutters. First results were obtained from machining simple slots applying TiAlN-coated tools with a diameter of 0.4 mm. The machining process was evaluated in terms of tool wear, cutting forces and machining quality. The tool wear and work piece quality was analysed with a scanning electron microscope and a white-light confocal microscope. Despite the poor machinability of NiTi good results concerning tool wear and shape accuracy of the milled slots were achieved. Essential for a good machining result is the application of minimum quantity lubrication. This clearly reduces NiTi adherences compared to dry machining. Work piece quality is improved and tool life is extended. Based on these results different structures could be produced by micro-milling

  14. On the effects of geometry, defects, and material asymmetry on the mechanical response of shape memory alloy cellular lattice structures

    International Nuclear Information System (INIS)

    Ravari, M R Karamooz; Kadkhodaei, M; Ghaei, A; Esfahani, S Nasr; Andani, M Taheri; Elahinia, M; Karaca, H

    2016-01-01

    Shape memory alloy (such as NiTi) cellular lattice structures are a new class of advanced materials with many potential applications. The cost of fabrication of these structures however is high. It is therefore necessary to develop modeling methods to predict the functional behavior of these alloys before fabrication. The main aim of the present study is to assess the effects of geometry, microstructural imperfections and material asymmetric response of dense shape memory alloys on the mechanical response of cellular structures. To this end, several cellular and dense NiTi samples are fabricated using a selective laser melting process. Both cellular and dense specimens were tested in compression in order to obtain their stress–strain response. For modeling purposes, a three -dimensional (3D) constitutive model based on microplane theory which is able to describe the material asymmetry was employed. Five finite element models based on unit cell and multi-cell methods were generated to predict the mechanical response of cellular lattices. The results show the considerable effects of the microstructural imperfections on the mechanical response of the cellular lattice structures. The asymmetric material response of the bulk material also affects the mechanical response of the corresponding cellular structure. (paper)

  15. The effect of hafnium content on the transformation temperatures of Ni49Ti51-xHfx shape memory alloys

    International Nuclear Information System (INIS)

    Angst, D.R.; Thoma, P.E.; Kao, M.Y.

    1995-01-01

    Ternary alloys of NiTiHf, having higher transformation temperatures than binary NiTi shape memory alloys, have been produced and analyzed. Beginning with a base composition of Ni 49 Ti 51 , Hf was substituted for Ti up to 30 atomic percent. Differential scanning calorimetry was used to determine the transformation temperatures of the as-cast alloys. The peak martensite temperature of the Ni 49 Ti 51 alloy was 69 C and increased to 525 C for the Ni 49 Ti 21 Hf 30 alloy. The peak austenite temperature of the Ni 49 Ti 51 alloy was 114 C and increased to 622 C for the Ni 49 Ti 21 Hf 30 alloy. An apparent minimum in the peak transformation temperatures occurred between 0 and 3 atomic percent Hf. Preliminary experiments were also conducted to determine the effect of thermomechanical processing on the shape memory properties of the Ni 49 Ti 41 Hf 10 . Data are presented on the effect of cold work and heat treatment on the transformation temperatures of this alloy. (orig.)

  16. Nanoparticle Netpoints for Shape-Memory Polymers

    KAUST Repository

    Agarwal, Praveen; Chopra, Madhur; Archer, Lynden A.

    2011-01-01

    Forget-me-not: Nanoparticle fillers in shape-memory polymers usually improve mechanical properties at the expense of shape-memory performance. A new approach overcomes these drawbacks by cross-linking the functionalized poly(ethylene glycol) tethers

  17. Thin NiTi Films Deposited on Graphene Substrates

    Science.gov (United States)

    Hahn, S.; Schulze, A.; Böhme, M.; Hahn, T.; Wagner, M. F.-X.

    2017-03-01

    We present experimental results on the deposition of Nickel Titanium (NiTi) films on graphene substrates using a PVD magnetron sputter process. Characterization of the 2-4 micron thick NiTi films by electron microscopy, electron backscatter diffraction, and transmission electron microscopy shows that grain size and orientation of the thin NiTi films strongly depend on the type of combination of graphene and copper layers below. Our experimental findings are supported by density functional theory calculations: a theoretical estimation of the binding energies of different NiTi-graphene interfaces is in line with the experimentally determined microstructural features of the functional NiTi top layer.

  18. Energy-based fatigue model for shape memory alloys including thermomechanical coupling

    Science.gov (United States)

    Zhang, Yahui; Zhu, Jihong; Moumni, Ziad; Van Herpen, Alain; Zhang, Weihong

    2016-03-01

    This paper is aimed at developing a low cycle fatigue criterion for pseudoelastic shape memory alloys to take into account thermomechanical coupling. To this end, fatigue tests are carried out at different loading rates under strain control at room temperature using NiTi wires. Temperature distribution on the specimen is measured using a high speed thermal camera. Specimens are tested to failure and fatigue lifetimes of specimens are measured. Test results show that the fatigue lifetime is greatly influenced by the loading rate: as the strain rate increases, the fatigue lifetime decreases. Furthermore, it is shown that the fatigue cracks initiate when the stored energy inside the material reaches a critical value. An energy-based fatigue criterion is thus proposed as a function of the irreversible hysteresis energy of the stabilized cycle and the loading rate. Fatigue life is calculated using the proposed model. The experimental and computational results compare well.

  19. Energy-based fatigue model for shape memory alloys including thermomechanical coupling

    International Nuclear Information System (INIS)

    Zhang, Yahui; Zhu, Jihong; Moumni, Ziad; Zhang, Weihong; Van Herpen, Alain

    2016-01-01

    This paper is aimed at developing a low cycle fatigue criterion for pseudoelastic shape memory alloys to take into account thermomechanical coupling. To this end, fatigue tests are carried out at different loading rates under strain control at room temperature using NiTi wires. Temperature distribution on the specimen is measured using a high speed thermal camera. Specimens are tested to failure and fatigue lifetimes of specimens are measured. Test results show that the fatigue lifetime is greatly influenced by the loading rate: as the strain rate increases, the fatigue lifetime decreases. Furthermore, it is shown that the fatigue cracks initiate when the stored energy inside the material reaches a critical value. An energy-based fatigue criterion is thus proposed as a function of the irreversible hysteresis energy of the stabilized cycle and the loading rate. Fatigue life is calculated using the proposed model. The experimental and computational results compare well. (paper)

  20. Damage evolution during actuation fatigue in shape memory alloys (SPIE Best Student Paper Award)

    Science.gov (United States)

    Phillips, Francis R.; Wheeler, Robert; Lagoudas, Dimitris C.

    2018-03-01

    Shape Memory Alloys (SMAs) are unique materials able to undergo a thermomechanically induced, reversible phase transformation. Additionally, SMA are subject to two types of fatigue, that is structural fatigue due to cyclic loading as experienced by most materials, as well as actuation fatigue due to repeated thermally induced phase transformation. The evolution of multiple material characteristics is presented over the actuation fatigue lifetime of NiTiHf actuators, including the accumulation of irrecoverable strain, the evolution of internal voids, and the evolution of the effective modulus of the actuator. The results indicate that all three of these material characteristics are clearly interconnected and careful analysis of each of these characteristics can help to understand the evolution of the others, as well as help to understand how actuation fatigue leads to ultimate failure of the actuator.

  1. Characterization of the phase transformations in shape-memory alloys by modulated differential scanning calorimetry

    International Nuclear Information System (INIS)

    Wei, Z.G.; Sandstroem, R.

    1999-01-01

    Modulated differential scanning calorimetry (MDSC) is a recently developed calorimetric technique, which has demonstrated some significant advantages over the conventional differential scanning calorimetry (DSC). By separating the reversing quantity from the non-reversing component in the total thermal events, it provides some new information that can not be obtained from the conventional DSC. The technique has been applied to various polycrystalline and single crystalline shape-memory alloys, including Cu-Zn-Al, Cu-Al-Ni, Ti-Ni(Cu), Ni-Mn-Ga and Fe-Mn-Si, to characterize the martensitic transformations, bainitic transformation, chemical and magnetic ordering transitions, atomic reordering and other kinetic relaxation processes in the alloys. The preliminary results of the MDSC measurements are summarized and the interpretation of the MDSC results and some factors affecting the results are discussed. (orig.)

  2. Anisotropic microstructure and superelasticity of additive manufactured NiTi alloy bulk builds using laser directed energy deposition

    Energy Technology Data Exchange (ETDEWEB)

    Bimber, Beth A. [Department of Engineering Science and Mechanics, The Pennsylvania State University, 212 Earth-Engineering Sciences Building, University Park, PA 16802 (United States); Hamilton, Reginald F., E-mail: rfh13@psu.edu [Department of Engineering Science and Mechanics, The Pennsylvania State University, 212 Earth-Engineering Sciences Building, University Park, PA 16802 (United States); Keist, Jayme; Palmer, Todd A. [Applied Research Laboratory, The Pennsylvania State University, State College, PA 16804 (United States)

    2016-09-30

    The microstructure and superelasticity in additive manufactured NiTi shape memory alloys (SMAs) were investigated. Using elementally blended Ni and Ti powder feedstock, Ni-rich build coupons were fabricated via the laser-based directed energy deposition (LDED) technique. The build volumes were large enough to extract tensile and compressive test specimens from selected locations for spatially resolving microconstituents and the underlying stress-induced martensitic phase transformation (SIMT) morphology. In the as-deposited condition, X-ray diffraction identified the B2 atomic crystal structure of the austenitic parent phase in NiTi SMAs, and Ni{sub 4}Ti{sub 3} precipitates were the predominant microconstituent identified through scanning electron microscopy. The microstructure exhibited anisotropy, which was characterized by the Ni{sub 4}Ti{sub 3} precipitate morphology being coarsest nearest the substrate, while a finer morphology was observed farthest from the substrate. In-situ full-field deformation measurements calculated using digital image correlation confirmed that the SIMT predominately occurred in the finer precipitate morphology. Heat treatment reduced the degree of anisotropy, and DIC analysis revealed localized SIMT strains increased compared to the as-deposited condition.

  3. Selective laser melting of Ni-rich NiTi: selection of process parameters and the superelastic response

    Science.gov (United States)

    Shayesteh Moghaddam, Narges; Saedi, Soheil; Amerinatanzi, Amirhesam; Saghaian, Ehsan; Jahadakbar, Ahmadreza; Karaca, Haluk; Elahinia, Mohammad

    2018-03-01

    Material and mechanical properties of NiTi shape memory alloys strongly depend on the fabrication process parameters and the resulting microstructure. In selective laser melting, the combination of parameters such as laser power, scanning speed, and hatch spacing determine the microstructural defects, grain size and texture. Therefore, processing parameters can be adjusted to tailor the microstructure and mechanical response of the alloy. In this work, NiTi samples were fabricated using Ni50.8Ti (at.%) powder via SLM PXM by Phenix/3D Systems and the effects of processing parameters were systematically studied. The relationship between the processing parameters and superelastic properties were investigated thoroughly. It will be shown that energy density is not the only parameter that governs the material response. It will be shown that hatch spacing is the dominant factor to tailor the superelastic response. It will be revealed that with the selection of right process parameters, perfect superelasticity with recoverable strains of up to 5.6% can be observed in the as-fabricated condition.

  4. Processing of Ni30Pt20Ti50 High-Temperature Shape-Memory Alloy Into Thin Rod Demonstrated

    Science.gov (United States)

    Noebe, Ronald D.; Draper, Susan L.; Biles, Tiffany A.; Leonhardt, Todd

    2005-01-01

    High-temperature shape-memory alloys (HTSMAs) based on nickel-titanium (NiTi) with significant ternary additions of palladium (Pd), platinum (Pt), gold (Au), or hafnium (Hf) have been identified as potential high-temperature actuator materials for use up to 500 C. These materials provide an enabling technology for the development of "smart structures" used to control the noise, emissions, or efficiency of gas turbine engines. The demand for these high-temperature versions of conventional shape-memory alloys also has been growing in the automotive, process control, and energy industries. However these materials, including the NiPtTi alloys being developed at the NASA Glenn Research Center, will never find widespread acceptance unless they can be readily processed into useable forms.

  5. Estudio de polvos y recubrimientos metaestables de NiTi obtenidos por proyección térmica de plasma

    Directory of Open Access Journals (Sweden)

    Cano, I. G.

    2008-06-01

    Full Text Available NiTi intermetallic is widely known for its shape memory effect and pseudoelasticity. Due to its high corrosion resístanse (biocompatibility, most of the studies carried out deal with its use for medical applications. With regard to surface technologies, many reported investigations focus on Vacuum Thermal Spray to provide NiTi coatings with minimal oxide content.The Thermal Spray Center has attempted to obtain metastable NiTi powders and coatings by means of Atmospheric Plasma Spraying with a liquid nitrogen cooling system. Starting from two different Ni-45wt%Ti feedstock powders. One powder is a blend of Ti and Ni particles, whereas the other has been alloyed by gas atomization. Both powders were sprayed obtaining better results starting from the gas atomized powder resulting in a final deposit where NiTi was the main phase with minimal oxidation. Different spraying parameters were tested and microstructural characterization was performed by SEM-EDS. XRD patterns showed some peak broadening; that seems to be produced by structural metastability of the coatings.

    El compuesto intermetálico de NiTi es conocido por su capacidad de memoria de forma así como por su pseudoelasticidad. Debido, además, a su alta resistencia a corrosión (biocompatiblidad, la gran mayoría de estudios se centran en su uso para aplicaciones médicas. Dentro del conjunto de las tecnologías de superficie, las investigaciones actuales utilizan la técnica de Proyección Térmica de Plasma al Vacío para producir recubrimientos de NiTi con contenidos mínimos de porosidad y de óxidos.El Centro de Proyección Térmica se planteó como objetivo la obtención de polvos y recubrimientos metaestables de NiTi a través de la técnica de Proyección de Plasma acoplado a un sistema de refrigeración con nitrógeno líquido. Se estudiaron dos polvos con diferentes características, pero de la misma composición nominal (Ni-45 % peso Ti. Uno de ellos, es el resultado de

  6. Synthesis of shape memory alloys using electrodeposition

    Science.gov (United States)

    Hymer, Timothy Roy

    Shape memory alloys are used in a variety of applications. The area of micro-electro-mechanical systems (MEMS) is a developing field for thin film shape memory alloys for making actuators, valves and pumps. Until recently thin film shape memory alloys could only be made by rapid solidification or sputtering techniques which have the disadvantage of being "line of sight". At the University of Missouri-Rolla, electrolytic techniques have been developed that allow the production of shape memory alloys in thin film form. The advantages of this techniques are in-situ, non "line of sight" and the ability to make differing properties of the shape memory alloys from one bath. This research focused on the electrodeposition of In-Cd shape memory alloys. The primary objective was to characterize the electrodeposited shape memory effect for an electrodeposited shape memory alloy. The effect of various operating parameters such as peak current density, temperature, pulsing, substrate and agitation were investigated and discussed. The electrodeposited alloys were characterized by relative shape memory effect, phase transformation, morphology and phases present. Further tests were performed to optimize the shape memory by the use of a statistically designed experiment. An optimized shape memory effect for an In-Cd alloy is reported for the conditions of the experiments.

  7. Anti-corrosion performance of oxidized and oxygen plasma-implanted NiTi alloys

    International Nuclear Information System (INIS)

    Poon, Ray W.Y.; Ho, Joan P.Y.; Liu, Xuanyong; Chung, C.Y.; Chu, Paul K.; Yeung, Kelvin W.K.; Lu, William W.; Cheung, Kenneth M.C.

    2005-01-01

    Nickel-titanium shape memory alloys are useful orthopedic biomaterials on account of its super-elastic and shape memory properties. However, the problem associated with out-diffusion of harmful nickel ions in prolonged use inside the human body raises a critical safety concern. Titanium oxide films are deemed to be chemically inert and biocompatible and hence suitable to be the barrier layers to impede the leaching of Ni from the NiTi substrate to biological tissues and fluids. In the work reported in this paper, we compare the anti-corrosion efficacy of oxide films produced by atmospheric-pressure oxidation and oxygen plasma ion implantation. Our results show that the oxidized samples do not possess improved corrosion resistance and may even fare worse than the untreated samples. On the other hand, the plasma-implanted surfaces exhibit much improved corrosion resistance. Our work also shows that post-implantation annealing can further promote the anti-corrosion capability of the samples

  8. Monotonic and cyclic bond behavior of confined concrete using NiTiNb SMA wires

    International Nuclear Information System (INIS)

    Choi, Eunsoo; Chung, Young-Soo; Kim, Yeon-Wook; Kim, Joo-Woo

    2011-01-01

    This study conducts bond tests of reinforced concrete confined by shape memory alloy (SMA) wires which provide active and passive confinement of concrete. This study uses NiTiNb SMA which usually shows wide temperature hysteresis; this is a good advantage for the application of shape memory effects. The aims of this study are to investigate the behavior of SMA wire under residual stress and the performance of SMA wire jackets in improving bond behavior through monotonic-loading tests. This study also conducts cyclic bond tests and analyzes cyclic bond behavior. The use of SMA wire jackets transfers the bond failure from splitting to pull-out mode and satisfactorily increases bond strength and ductile behavior. The active confinement provided by the SMA plays a major role in providing external pressure on the concrete because the developed passive confinement is much smaller than the active confinement. For cyclic behavior, slip and circumferential strain are recovered more with larger bond stress. This recovery of slip and circumferential strain are mainly due to the external pressure of the SMA wires since cracked concrete cannot provide any elastic recovery

  9. Finite element modeling of indentation-induced superelastic effect using a three-dimensional constitutive model for shape memory materials with plasticity

    International Nuclear Information System (INIS)

    Zhang, Yijun; Cheng, Yang-Tse; Grummon, David S.

    2007-01-01

    Indentation-induced shape memory and superelastic effects are recently discovered thermo-mechanical behaviors that may find important applications in many areas of science and engineering. Theoretical understanding of these phenomena is challenging because both martensitic phase transformation and slip plasticity exist under complex contact loading conditions. In this paper, we develop a three-dimensional constitutive model of shape memory alloys with plasticity. Spherical indentation-induced superelasticity in a NiTi shape memory alloy was simulated and compared to experimental results on load-displacement curves and recovery ratios. We show that shallow indents have complete recovery upon unloading, where the size of the phase transformation region is about two times the contact radius. Deep indents have only partial recovery when plastic deformation becomes more prevalent in the indent-affected zone

  10. Improvements of anti-corrosion and mechanical properties of NiTi orthopedic materials by acetylene, nitrogen and oxygen plasma immersion ion implantation

    International Nuclear Information System (INIS)

    Poon, Ray W.Y.; Ho, Joan P.Y.; Liu Xuanyong; Chung, C.Y.; Chu, Paul K.; Yeung, Kelvin W.K.; Lu, William W.; Cheung, Kenneth M.C.

    2005-01-01

    Nickel-titanium shape memory alloys (NiTi) are useful materials in orthopedics and orthodontics due to their unique super-elasticity and shape memory effects. However, the problem associated with the release of harmful Ni ions to human tissues and fluids has been raising safety concern. Hence, it is necessary to produce a surface barrier to impede the out-diffusion of Ni ions from the materials. We have conducted acetylene, nitrogen and oxygen plasma immersion ion implantation (PIII) into NiTi alloys in an attempt to improve the surface properties. All the implanted and annealed samples surfaces exhibit outstanding corrosion and Ni out-diffusion resistance. Besides, the implanted layers are mechanically stronger than the substrate underneath. XPS analyses disclose that the layer formed by C 2 H 2 PIII is composed of mainly TiC x with increasing Ti to C concentration ratios towards the bulk. The nitrogen PIII layer is observed to be TiN, whereas the oxygen PIII layer is composed of oxides of Ti 4+ , Ti 3+ and Ti 2+

  11. Cu-Al-Ni Shape Memory Single Crystal Wires with High Transformation Temperature

    Science.gov (United States)

    Hautcoeur, Alain; Fouché, Florian; Sicre, Jacques

    2016-01-01

    CN-250X is a new material with higher performance than Nickel-Titanium Shape Memory Alloy (SMA). For space mechanisms, the main disadvantage of Nickel-Titanium Shape Memory Alloy is the limited transformation temperature. The new CN-250X Nimesis alloy is a Cu-Al-Ni single crystal wire available in large quantity because of a new industrial process. The triggering of actuators made with this Cu-Al-Ni single crystal wire can range from ambient temperature to 200 C in cycling and even to 250 C in one-shot mode. Another advantage of CN-250X is a better shape recovery (8 to 10%) than Ni-Ti (6 to 7%). Nimesis is the first company able to produce this type of material with its new special industrial process. A characterization study is presented in this work, including the two main solicitation modes for this material: tensile and torsion. Different tests measure the shape recovery of Cu-Al-Ni single crystals wires during heating from room temperature to a temperature higher than temperature of end of martensitic transformation.

  12. Forming of shape memory composite structures

    DEFF Research Database (Denmark)

    Santo, Loredana; Quadrini, Fabrizio; De Chiffre, Leonardo

    2013-01-01

    A new forming procedure was developed to produce shape memory composite structures having structural composite skins over a shape memory polymer core. Core material was obtained by solid state foaming of an epoxy polyester resin with remarkably shape memory properties. The composite skin consisted...... of a two-layer unidirectional thermoplastic composite (glass filled polypropylene). Skins were joined to the foamed core by hot compression without any adhesive: a very good adhesion was obtained as experimental tests confirmed. The structure of the foam core was investigated by means of computer axial...... tomography. Final shape memory composite panels were mechanically tested by three point bending before and after a shape memory step. This step consisted of a compression to reduce the panel thickness up to 60%. At the end of the bending test the panel shape was recovered by heating and a new memory step...

  13. Thermomechanical macroscopic model of shape memory alloys

    International Nuclear Information System (INIS)

    Volkov, A.E.; Sakharov, V.Yu.

    2003-01-01

    The phenomenological macroscopic model of the mechanical behaviour of the titanium nickelide-type shape memory alloys is proposed. The model contains as a parameter the average phase shear deformation accompanying the martensite formation. It makes i possible to describe correctly a number of functional properties of the shape memory alloys, in particular, the pseudoelasticity ferroplasticity, plasticity transformation and shape memory effects in the stressed and unstressed samples [ru

  14. Design and Characterization of a Small-Scale Solar Sail Prototype by Integrating NiTi SMA and Carbon Fibre Composite

    Directory of Open Access Journals (Sweden)

    Girolamo Costanza

    2017-01-01

    Full Text Available Solar sails are propellantless systems where the propulsive force is given by the momentum exchange of reflecting photons. In this study, a self-deploying system based on NiTi shape memory wires and sheets has been designed and manufactured. A small-scale prototype of solar sail with carbon fibre loom has been developed. Different configurations have been tested to optimize material and structure design of the small-scale solar sail. In particular the attention has been focused on the surface/weight ratio and the deployment of the solar sail. By reducing weight and enlarging the surface, it is possible to obtain high values of characteristic acceleration that is one of the main parameters for a successful use of the solar sail as propulsion system. Thanks to the use of shape memory alloys for self-actuation of the system, complexity of the structure itself decreases. Moreover, sail deployment is simpler.

  15. Microstructure and corrosion behavior of laser processed NiTi alloy.

    Science.gov (United States)

    Marattukalam, Jithin J; Singh, Amit Kumar; Datta, Susmit; Das, Mitun; Balla, Vamsi Krishna; Bontha, Srikanth; Kalpathy, Sreeram K

    2015-12-01

    Laser Engineered Net Shaping (LENS™), a commercially available additive manufacturing technology, has been used to fabricate dense equiatomic NiTi alloy components. The primary aim of this work is to study the effect of laser power and scan speed on microstructure, phase constituents, hardness and corrosion behavior of laser processed NiTi alloy. The results showed retention of large amount of high-temperature austenite phase at room temperature due to high cooling rates associated with laser processing. The high amount of austenite in these samples increased the hardness. The grain size and corrosion resistance were found to increase with laser power. The surface energy of NiTi alloy, calculated using contact angles, decreased from 61 mN/m to 56 mN/m with increase in laser energy density from 20 J/mm(2) to 80 J/mm(2). The decrease in surface energy shifted the corrosion potentials to nobler direction and decreased the corrosion current. Under present experimental conditions the laser power found to have strong influence on microstructure, phase constituents and corrosion resistance of NiTi alloy. Copyright © 2015 Elsevier B.V. All rights reserved.

  16. Shape Memory of Human Red Blood Cells

    OpenAIRE

    Fischer, Thomas M.

    2004-01-01

    The human red cell can be deformed by external forces but returns to the biconcave resting shape after removal of the forces. If after such shape excursions the rim is always formed by the same part of the membrane, the cell is said to have a memory of its biconcave shape. If the rim can form anywhere on the membrane, the cell would have no shape memory. The shape memory was probed by an experiment called go-and-stop. Locations on the membrane were marked by spontaneously adhering latex spher...

  17. Management of long-term and reversible hysteroscopic sterilization: a novel device with nickel-titanium shape memory alloy

    Science.gov (United States)

    2014-01-01

    Background Female sterilization is the second most commonly used method of contraception in the United States. Female sterilization can now be performed through laparoscopic, abdominal, or hysteroscopic approaches. The hysteroscopic sterilization may be a safer option than sterilization through laparoscopy or laparotomy because it avoids invading the abdominal cavity and undergoing general anaesthesia. Hysteroscopic sterilization mainly includes chemical agents and mechanical devices. Common issues related to the toxicity of the chemical agents used have raised concerns regarding this kind of contraception. The difficulty of the transcervical insertion of such mechanical devices into the fallopian tubes has increased the high incidence of device displacement or dislodgment. At present, Essure® is the only commercially available hysteroscopic sterilization device being used clinically. The system is irreversible and is not effective immediately. Presentation of the hypothesis Our new hysteroscopic sterility system consists of nickel-titanium (NiTi) shape memory alloy and a waterproof membrane. The NiTi alloy is covered with two coatings to avoid toxic Ni release and to prevent stimulation of epithelial tissue growth around the oviducts. Because of the shape memory effect of the NiTi alloy, the device works like an umbrella: it stays collapsed at low temperature before placement and opens by the force of shape memory activated by the body temperature after it is inserted hysteroscopically into the interstitial tubal lumen. The rim of the open device will incise into interstitial myometrium during the process of unfolding. Once the device is fixed, it blocks the tube completely. When the patient no longer wishes for sterilization, the device can be closed by perfusing liquid with low temperature into the uterine cavity, followed by prospective hysteroscopic removal. After the device removal, the fallopian tube will revert to its physiological functions. Testing the

  18. Nanoparticle Netpoints for Shape-Memory Polymers

    KAUST Repository

    Agarwal, Praveen

    2011-08-02

    Forget-me-not: Nanoparticle fillers in shape-memory polymers usually improve mechanical properties at the expense of shape-memory performance. A new approach overcomes these drawbacks by cross-linking the functionalized poly(ethylene glycol) tethers on silica nanoparticles (see picture). Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  19. In situ NiTi/Nb(Ti) composite

    International Nuclear Information System (INIS)

    Jiang, Daqiang; Cui, Lishan; Jiang, Jiang; Zheng, Yanjun

    2013-01-01

    Graphical abstract: - Highlights: • In situ NiTi/Nb(Ti) composites were fabricated. • The transformation temperature was affected by the mixing Ti:Ni atomic ratios. • The NiTi component became micron-scale lamella after forging and rolling. • The composite exhibited high strength and high damping capacity. - Abstract: This paper reports on the creation of a series of in situ NiTi/Nb(Ti) composites with controllable transformation temperatures based on the pseudo-binary hypereutectic transformation of NiTi–Nb system. The composite constituent morphology was controlled by forging and rolling. It is found that the thickness of the NiTi lamella in the composite reached micron level after the hot-forging and cold-rolling. The NiTi/Nb(Ti) composite exhibited high damping capacity as well as high yield strength

  20. Shape Memory Composite Hybrid Hinge

    Science.gov (United States)

    Fang, Houfei; Im, Eastwood; Lin, John; Scarborough, Stephen

    2012-01-01

    There are two conventional types of hinges for in-space deployment applications. The first type is mechanically deploying hinges. A typical mechanically deploying hinge is usually composed of several tens of components. It is complicated, heavy, and bulky. More components imply higher deployment failure probability. Due to the existence of relatively moving components among a mechanically deploying hinge, it unavoidably has microdynamic problems. The second type of conventional hinge relies on strain energy for deployment. A tape-spring hinge is a typical strain energy hinge. A fundamental problem of a strain energy hinge is that its deployment dynamic is uncontrollable. Usually, its deployment is associated with a large impact, which is unacceptable for many space applications. Some damping technologies have been experimented with to reduce the impact, but they increased the risks of an unsuccessful deployment. Coalescing strain energy components with shape memory composite (SMC) components to form a hybrid hinge is the solution. SMCs are well suited for deployable structures. A SMC is created from a high-performance fiber and a shape memory polymer resin. When the resin is heated to above its glass transition temperature, the composite becomes flexible and can be folded or packed. Once cooled to below the glass transition temperature, the composite remains in the packed state. When the structure is ready to be deployed, the SMC component is reheated to above the glass transition temperature, and it returns to its as-fabricated shape. A hybrid hinge is composed of two strain energy flanges (also called tape-springs) and one SMC tube. Two folding lines are placed on the SMC tube to avoid excessive strain on the SMC during folding. Two adapters are used to connect the hybrid hinge to its adjacent structural components. While the SMC tube is heated to above its glass transition temperature, a hybrid hinge can be folded and stays at folded status after the temperature

  1. Efficacy and safety of a NiTi CAR 27 compression ring for end-to-end anastomosis compared with conventional staplers: A real-world analysis in Chinese colorectal cancer patients

    Science.gov (United States)

    Lu, Zhenhai; Peng, Jianhong; Li, Cong; Wang, Fulong; Jiang, Wu; Fan, Wenhua; Lin, Junzhong; Wu, Xiaojun; Wan, Desen; Pan, Zhizhong

    2016-01-01

    OBJECTIVES: This study aimed to evaluate the safety and efficacy of a new nickel-titanium shape memory alloy compression anastomosis ring, NiTi CAR 27, in constructing an anastomosis for colorectal cancer resection compared with conventional staples. METHODS: In total, 234 consecutive patients diagnosed with colorectal cancer receiving sigmoidectomy and anterior resection for end-to-end anastomosis from May 2010 to June 2012 were retrospectively analyzed. The postoperative clinical parameters, postoperative complications and 3-year overall survival in 77 patients using a NiTi CAR 27 compression ring (CAR group) and 157 patients with conventional circular staplers (STA group) were compared. RESULTS: There were no statistically significant differences between the patients in the two groups in terms of general demographics and tumor features. A clinically apparent anastomotic leak occurred in 2 patients (2.6%) in the CAR group and in 5 patients (3.2%) in the STA group (p=0.804). These eight patients received a temporary diverting ileostomy. One patient (1.3%) in the CAR group was diagnosed with anastomotic stricture through an electronic colonoscopy after 3 months postoperatively. The incidence of postoperative intestinal obstruction was comparable between the two groups (p=0.192). With a median follow-up duration of 39.6 months, the 3-year overall survival rate was 83.1% in the CAR group and 89.0% in the STA group (p=0.152). CONCLUSIONS: NiTi CAR 27 is safe and effective for colorectal end-to-end anastomosis. Its use is equivalent to that of the conventional circular staplers. This study suggests that NiTi CAR 27 may be a beneficial alternative in colorectal anastomosis in Chinese colorectal cancer patients. PMID:27276395

  2. Post polymerization cure shape memory polymers

    Energy Technology Data Exchange (ETDEWEB)

    Wilson, Thomas S.; Hearon, II, Michael Keith; Bearinger, Jane P.

    2017-01-10

    This invention relates to chemical polymer compositions, methods of synthesis, and fabrication methods for devices regarding polymers capable of displaying shape memory behavior (SMPs) and which can first be polymerized to a linear or branched polymeric structure, having thermoplastic properties, subsequently processed into a device through processes typical of polymer melts, solutions, and dispersions and then crossed linked to a shape memory thermoset polymer retaining the processed shape.

  3. Post polymerization cure shape memory polymers

    Science.gov (United States)

    Wilson, Thomas S; Hearon, Michael Keith; Bearinger, Jane P

    2014-11-11

    This invention relates to chemical polymer compositions, methods of synthesis, and fabrication methods for devices regarding polymers capable of displaying shape memory behavior (SMPs) and which can first be polymerized to a linear or branched polymeric structure, having thermoplastic properties, subsequently processed into a device through processes typical of polymer melts, solutions, and dispersions and then crossed linked to a shape memory thermoset polymer retaining the processed shape.

  4. Density functional theory simulation of titanium migration and reaction with oxygen in the early stages of oxidation of equiatomic NiTi alloy.

    Science.gov (United States)

    Nolan, Michael; Tofail, Syed A M

    2010-05-01

    The biocompatibility of NiTi shape memory alloys (SMA) has made possible applications in self-expandable cardio-vascular stents, stone extraction baskets, catheter guide wires and other invasive and minimally invasive biomedical devices. The NiTi intermetallic alloy spontaneously forms a thin passive layer of TiO(2), which provides its biocompatibility. The oxide layer is thought to form as the Ti in the alloy surface reacts with oxygen, resulting in a depletion of Ti in the subsurface region - experimental evidence indicates formation of a Ni-rich layer below the oxide film. In this paper, we study the initial stages of oxide growth on the (110) surface of the NiTi alloy to understand the formation of alloy/oxide interface. We initially adsorb atomic and molecular oxygen on the (110) surface and then successively add O(2) molecules, up to 2 monolayer of O(2). Oxygen adsorption always results in a large energy gain. With atomic oxygen, Ti is pulled out of the surface layer leaving behind a Ni-rich subsurface region. Molecular O(2), on the other hand adsorbs dissociatively and pulls a Ti atom farther out of the surface layer. The addition of further O(2) up to 1 monolayer is also dissociative and results in complete removal of Ti from the initial surface layer. When further O(2) is added up to 2 monolayer, Ti is pulled even further out of the surface and a single thin layer of composition O-Ti-O is formed. The electronic structure shows that the metallic character of the alloy is unaffected by interaction with oxygen and formation of the oxide layer, consistent with the oxide layer being a passivant. Copyright 2010 Elsevier Ltd. All rights reserved.

  5. Numerical simulation of the force generated by a superelastic NiTi orthodontic archwire during tooth alignment phase: comparison between different constitutive models

    Science.gov (United States)

    Gannoun, M.; Laroussi Hellara, M.; Bouby, C.; Ben Zineb, T.; Bouraoui, T.

    2018-04-01

    Nickel Titanium (NiTi) Superelastic (SE) Shape Memory Alloys (SMAs) are widely considered for applications that need high reversible strain or high recovery forces. In particular, the SE SMAs present a high interest for biomedical applications such as endodontic and orthodontic apparatus. They are available in a large variety of archwires exerting continuum forces to ensure the dental displacement. The purpose of this study is to report the clinical implications of NiTi SE wires for dental treatment in a given configuration. Three main constitutive models of the literature (Lagoudas and Boyd 1996 Int. J. Plast. 12 805–842, Auricchio and Petrini 2004 Int. J. Numer. Meth. Engng. 61 807–836 and Chemisky et al 2011 Mech. Mater. 68 361–376) are considered for the finite element (FE) numerical simulations of the SMA archwires response. Tensile tests had been carried out in order to identify the material parameters of these constitutive models. The FE numerical study allowed to predict the dental displacement and its corresponding orthodontic force level exerted by the wire in similar conditions to those in the oral environment. This work allows to predict the orthodontic generated load by a NiTi SE archwire with a 0.64 × 0.46 mm2 rectangular cross section under prescribed thermomechanical conditions. The effect of the temperature and the alveolar bone stiffness on the orthodontic load level and the tooth displacement degree has been investigated. The performed numerical simulations demonstrate that the orthodontic load is sensitive to the displacement magnitude, to the tooth stiffness and to the temperature variations. The obtained forces applied continuously and at a constant level are within the acceptable orthodontic force level range. Some directives are therefore provided to help orthodontists to select the optimal archwire.

  6. Shape memory of human red blood cells.

    Science.gov (United States)

    Fischer, Thomas M

    2004-05-01

    The human red cell can be deformed by external forces but returns to the biconcave resting shape after removal of the forces. If after such shape excursions the rim is always formed by the same part of the membrane, the cell is said to have a memory of its biconcave shape. If the rim can form anywhere on the membrane, the cell would have no shape memory. The shape memory was probed by an experiment called go-and-stop. Locations on the membrane were marked by spontaneously adhering latex spheres. Shape excursions were induced by shear flow. In virtually all red cells, a shape memory was found. After stop of flow and during the return of the latex spheres to the original location, the red cell shape was biconcave. The return occurred by a tank-tread motion of the membrane. The memory could not be eliminated by deforming the red cells in shear flow up to 4 h at room temperature as well as at 37 degrees C. It is suggested that 1). the characteristic time of stress relaxation is >80 min and 2). red cells in vivo also have a shape memory.

  7. On the improved adhesion of NiTi wires embedded in polyester and vinylester resins

    Directory of Open Access Journals (Sweden)

    Mattia Merlin

    2015-01-01

    Full Text Available This paper discusses the effect of different surface treatments on shape memory alloy wires embedded in PolyEster (PE and VinylEster (VE polymeric matrices. In particular, two types of chemical etching and a chemical bonding with a silane coupling agent have been performed on the surfaces of the wires. Pull-out tests have been carried out on samples made from a specifically designed Teflon mould. Considering the best results of the pull-out tests obtained with PE resin, the debonding induced by strain recovery of 4%, 5% and 6% pre-strained NiTi wires has been evaluated with the wires being subjected to different surface treatment conditions and then being embedded in the PE matrix. The results prove that the wires functionalised and embedded in the PE resin show the maximum pull-out forces and the highest interfacial adhesion. Finally, it has been found that debonding induced by strain recovery is strongly related to the propagation towards the radial direction of sharp cracks at the debonding region.

  8. Assessment of Shape Memory Alloys - From Atoms To Actuators - Via In Situ Neutron Diffraction

    Science.gov (United States)

    Benafan, Othmane

    2014-01-01

    As shape memory alloys (SMAs) become an established actuator technology, it is important to identify the fundamental mechanisms responsible for their performance by understanding microstructure performance relationships from processing to final form. Yet, microstructural examination of SMAs at stress and temperature is often a challenge since structural changes occur with stress and temperature and microstructures cannot be preserved through quenching or after stress removal, as would be the case for conventional materials. One solution to this dilemma is in situ neutron diffraction, which has been applied to the investigation of SMAs and has offered a unique approach to reveal the fundamental micromechanics and microstructural aspects of bulk SMAs in a non-destructive setting. Through this technique, it is possible to directly correlate the micromechanical responses (e.g., internal residual stresses, lattice strains), microstructural evolutions (e.g., texture, defects) and phase transformation properties (e.g., phase fractions, kinetics) to the macroscopic actuator behavior. In this work, in situ neutron diffraction was systematically employed to evaluate the deformation and transformation behavior of SMAs under typical actuator conditions. Austenite and martensite phases, yield behavior, variant selection and transformation temperatures were characterized for a polycrystalline NiTi (49.9 at. Ni). As the alloy transforms under thermomechanical loading, the measured textures and lattice plane-level variations were directly related to the cyclic actuation-strain characteristics and the dimensional instability (strain ratcheting) commonly observed in this alloy. The effect of training on the shape memory characteristics of the alloy and the development of two-way shape memory effect (TWSME) were also assessed. The final conversion from a material to a useful actuator, typically termed shape setting, was also investigated in situ during constrained heatingcooling and

  9. Nanoscale phase transition behavior of shape memory alloys — closed form solution of 1D effective modelling

    Science.gov (United States)

    Li, M. P.; Sun, Q. P.

    2018-01-01

    We investigate the roles of grain size (lg) and grain boundary thickness (lb) on the stress-induced phase transition (PT) behaviors of nanocrystalline shape memory alloys (SMAs) by using a Core-shell type "crystallite-amorphous composite" model. A non-dimensionalized length scale lbarg(=lg /lb) is identified as the governing parameter which is indicative of the energy competition between the crystallite and the grain boundary. Closed form analytical solutions of a reduced effective 1D model with embedded microstructure length scales of lg and lb are presented in this paper. It is shown that, with lbarg reduction, the energy of the elastic non-transformable grain boundary will gradually become dominant in the phase transition process, and eventually bring fundamental changes of the deformation behaviors: breakdown of two-phase coexistence and vanishing of superelastic hysteresis. The predictions are supported by experimental data of nanocrystalline NiTi SMAs.

  10. Static magnetic susceptibility of radiopaque NiTiPt and NiTiEr

    Science.gov (United States)

    Chovan, Drahomír; Gandhi, Abbasi; Butler, James; Tofail, Syed A. M.

    2018-04-01

    Magnetic properties of metallic alloys used in biomedical industry are important for the magnetic resonance imaging (MRI). If the alloys were to be used for long term implants or as guiding devices, safety of the patient as well as the medical staff has to be ensured. Strong response to the external magnetic field can cause mechanical damage to the patients body. In this paper we present magnetic susceptibility of nickel rich, ternary NiTiPt and NiTiEr to static magnetic field. We show that the magnetic susceptibility of these radiopaque alloys has values in low paramagnetic region comparable to the binary nickel-titanium. Furthermore, we studied the effect of the thermal and mechanical treatments on magnetic properties. Despite deviation from linear M (H) treated samples spanning small region around H = 0 , the linearity of the M (H) and χ =d M /d H values suggest that these ternary alloys are safe to use under MRI conditions.

  11. Resistively heated shape memory polymer device

    Energy Technology Data Exchange (ETDEWEB)

    Marion, III, John E.; Bearinger, Jane P.; Wilson, Thomas S.; Maitland, Duncan J.

    2017-09-05

    A resistively heated shape memory polymer device is made by providing a rod, sheet or substrate that includes a resistive medium. The rod, sheet or substrate is coated with a first shape memory polymer providing a coated intermediate unit. The coated intermediate unit is in turn coated with a conductive material providing a second intermediate unit. The second coated intermediate unit is in turn coated with an outer shape memory polymer. The rod, sheet or substrate is exposed and an electrical lead is attached to the rod, sheet or substrate. The conductive material is exposed and an electrical lead is attached to the conductive material.

  12. Resistively heated shape memory polymer device

    Energy Technology Data Exchange (ETDEWEB)

    Marion, III, John E.; Bearinger, Jane P.; Wilson, Thomas S.; Maitland, Duncan J.

    2016-10-25

    A resistively heated shape memory polymer device is made by providing a rod, sheet or substrate that includes a resistive medium. The rod, sheet or substrate is coated with a first shape memory polymer providing a coated intermediate unit. The coated intermediate unit is in turn coated with a conductive material providing a second intermediate unit. The second coated intermediate unit is in turn coated with an outer shape memory polymer. The rod, sheet or substrate is exposed and an electrical lead is attached to the rod, sheet or substrate. The conductive material is exposed and an electrical lead is attached to the conductive material.

  13. A jumping shape memory alloy under heat.

    Science.gov (United States)

    Yang, Shuiyuan; Omori, Toshihiro; Wang, Cuiping; Liu, Yong; Nagasako, Makoto; Ruan, Jingjing; Kainuma, Ryosuke; Ishida, Kiyohito; Liu, Xingjun

    2016-02-16

    Shape memory alloys are typical temperature-sensitive metallic functional materials due to superelasticity and shape recovery characteristics. The conventional shape memory effect involves the formation and deformation of thermally induced martensite and its reverse transformation. The shape recovery process usually takes place over a temperature range, showing relatively low temperature-sensitivity. Here we report novel Cu-Al-Fe-Mn shape memory alloys. Their stress-strain and shape recovery behaviors are clearly different from the conventional shape memory alloys. In this study, although the Cu-12.2Al-4.3Fe-6.6Mn and Cu-12.9Al-3.8Fe-5.6Mn alloys possess predominantly L2(1) parent before deformation, the 2H martensite stress-induced from L2(1) parent could be retained after unloading. Furthermore, their shape recovery response is extremely temperature-sensitive, in which a giant residual strain of about 9% recovers instantly and completely during heating. At the same time, the phenomenon of the jumping of the sample occurs. It is originated from the instantaneous completion of the reverse transformation of the stabilized 2H martensite. This novel Cu-Al-Fe-Mn shape memory alloys have great potentials as new temperature-sensitive functional materials.

  14. Biodegradable Shape Memory Polymers in Medicine.

    Science.gov (United States)

    Peterson, Gregory I; Dobrynin, Andrey V; Becker, Matthew L

    2017-11-01

    Shape memory materials have emerged as an important class of materials in medicine due to their ability to change shape in response to a specific stimulus, enabling the simplification of medical procedures, use of minimally invasive techniques, and access to new treatment modalities. Shape memory polymers, in particular, are well suited for such applications given their excellent shape memory performance, tunable materials properties, minimal toxicity, and potential for biodegradation and resorption. This review provides an overview of biodegradable shape memory polymers that have been used in medical applications. The majority of biodegradable shape memory polymers are based on thermally responsive polyesters or polymers that contain hydrolyzable ester linkages. These materials have been targeted for use in applications pertaining to embolization, drug delivery, stents, tissue engineering, and wound closure. The development of biodegradable shape memory polymers with unique properties or responsiveness to novel stimuli has the potential to facilitate the optimization and development of new medical applications. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  15. An innovative approach to achieve re-centering and ductility of cement mortar beams through randomly distributed pseudo-elastic shape memory alloy fibers

    Science.gov (United States)

    Shajil, N.; Srinivasan, S. M.; Santhanam, M.

    2012-04-01

    Fibers can play a major role in post cracking behavior of concrete members, because of their ability to bridge cracks and distribute the stress across the crack. Addition of steel fibers in mortar and concrete can improve toughness of the structural member and impart significant energy dissipation through slow pull out. However, steel fibers undergo plastic deformation at low strain levels, and cannot regain their shape upon unloading. This is a major disadvantage in strong cyclic loading conditions, such as those caused by earthquakes, where self-centering ability of the fibers is a desired characteristic in addition to ductility of the reinforced cement concrete. Fibers made from an alternative material such as shape memory alloy (SMA) could offer a scope for re-centering, thus improving performance especially after a severe loading has occurred. In this study, the load-deformation characteristics of SMA fiber reinforced cement mortar beams under cyclic loading conditions were investigated to assess the re-centering performance. This study involved experiments on prismatic members, and related analysis for the assessment and prediction of re-centering. The performances of NiTi fiber reinforced mortars are compared with mortars with same volume fraction of steel fibers. Since re-entrant corners and beam columns joints are prone to failure during a strong ground motion, a study was conducted to determine the behavior of these reinforced with NiTi fiber. Comparison is made with the results of steel fiber reinforced cases. NiTi fibers showed significantly improved re-centering and energy dissipation characteristics compared to the steel fibers.

  16. Applications of shape memory alloys in Japan

    International Nuclear Information System (INIS)

    Asai, M.; Suzuki, Y.

    2000-01-01

    In Japan, a first application of shape memory TiNi alloy was a moving flap in an air-conditioner which was developed as sensing function of shape memory alloy at Matsushista Electric Industrial Co. Then, shape memory utilized in a coffee maker, an electric rice-cooker, a thermal mixing valve and etc. were commercialized in Japan. And brassiere wires, a guide wire for medical treatment, an antenna for portable telephone and others were commercialized utilizing superelasticity. At the same time with these commercial products, there was not only progress in fabrication technology to effect accurate transformation temperature, but also the discovery of small hysteresis alloy such as R-phase or TiNiCu alloy and low transformation temperature alloy such as TiNiFe, TiNiV and TiNiCo alloys. Therefore the shape memory alloy market has expanded widely to electric appliances, automobile, residence, medical care and other field today. (orig.)

  17. Shape Memory Alloy Adaptive Structures, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — This SBIR Phase I effort will demonstrate and scale up an innovative manufacturing process that yields aerospace grade shape memory alloy (SMA) solids and periodic...

  18. A slant type shape memory alloy

    International Nuclear Information System (INIS)

    Kanada, T.; Enokizono, M.

    2000-01-01

    A heat-treated Fe-based shape memory alloy (SMA) has compatible properties, magnetization and shape memory effect (SME). Since SME depends on the heat treatment conditions (temperature and time), we produced a slant-type SMA that has a gradient SME value in the longitudinal direction of the specimen. It is obvious that sheet specimen is superior to wire because the value of SME as a slant SME shows greater efficiency than that of wire

  19. In vitro corrosion behaviour of Ti-Nb-Sn shape memory alloys in Ringer's physiological solution.

    Science.gov (United States)

    Rosalbino, F; Macciò, D; Scavino, G; Saccone, A

    2012-04-01

    The nearly equiatomic Ni-Ti alloy (Nitinol) has been widely employed in the medical and dental fields owing to its shape memory or superelastic properties. The main concern about the use of this alloy derives form the fact that it contains a large amount of nickel (55% by mass), which is suspected responsible for allergic, toxic and carcinogenic reactions. In this work, the in vitro corrosion behavior of two Ti-Nb-Sn shape memory alloys, Ti-16Nb-5Sn and Ti-18Nb-4Sn (mass%) has been investigated and compared with that of Nitinol. The in vitro corrosion resistance was assessed in naturally aerated Ringer's physiological solution at 37°C by corrosion potential and electrochemical impedance spectroscopy (EIS) measurements as a function of exposure time, and potentiodynamic polarization curves. Corrosion potential values indicated that both Ni-Ti and Ti-Nb-Sn alloys undergo spontaneous passivation due to spontaneously formed oxide film passivating the metallic surface, in the aggressive environment. It also indicated that the tendency for the formation of a spontaneous oxide is greater for the Ti-18Nb-5Sn alloy. Significantly low anodic current density values were obtained from the polarization curves, indicating a typical passive behaviour for all investigated alloys, but Nitinol exhibited breakdown of passivity at potentials above approximately 450 mV(SCE), suggesting lower corrosion protection characteristics of its oxide film compared to the Ti-Nb-Sn alloys. EIS studies showed high impedance values for all samples, increasing with exposure time, indicating an improvement in corrosion resistance of the spontaneous oxide film. The obtained EIS spectra were analyzed using an equivalent electrical circuit representing a duplex structure oxide film, composed by an outer and porous layer (low resistance), and an inner barrier layer (high resistance) mainly responsible for the alloys corrosion resistance. The resistance of passive film present on the metals' surface

  20. Physical characterisation of endodontic instruments in NiTi alloy

    International Nuclear Information System (INIS)

    Torrisi, L.

    2000-01-01

    NiTi based endodontic instruments are investigated in functionality and wear. The instrument surfaces have been studied applying Auger electron spectroscopy, mechanical analysis, differential-scanning calorimetry, wear tests, and scanning electron microscopy. (orig.)

  1. Study of shape memory alloy fibers for the development of artificial myocardium.

    Science.gov (United States)

    Hassoulas, Ioannis A; Ladopoulos, Vlassios S; Kalogerakos, Paris-Dimitrios K

    2010-01-01

    Circulatory support devices are employed to treat heart failure. Such a device could be made from shape memory alloy (SMA) fibers. These Ni-Ti fibers contract when electric current flows through them, thus resembling artificial muscles. An artificial myocardium device made from SMA fibers can directly compress the epicardial surface of a failing heart, thus contributing to the pumping action. Unlike modern mechanical circulatory support devices, there is no blood-contacting surface to provoke thromboembolism, hemorrhage, inflammatory response or hemolysis. The experimental setup permitted a detailed study of a sample SMA fiber with great accuracy while the ambient temperature was controlled to resemble that of the human body. The current profile through the fiber was controlled (current shaping, CS) by a microcontroller and a portable computer. Parameters such as strain, contraction and relaxation velocities and the effect of ambient temperature were measured. The contraction and relaxation velocities were measured after applying various effective currents. It was found that the contraction velocity could be manipulated to reach that of the healthy myocardium through CS. On the other hand, the relaxation velocity was independent of the contraction velocity. A cardiac assist device can be made from SMA fibers. More studies need to be conducted in this direction.

  2. Hand Shape Affects Access to Memories

    NARCIS (Netherlands)

    K. Dijkstra (Katinka); M.P. Kaschak; R.A. Zwaan (Rolf)

    2008-01-01

    textabstractThe present study examined the ways that body posture facilitated retrieval of autobiographical memories in more detail by focusing on two aspects of congruence in position of a specific body part: hand shape and hand orientation. Hand shape is important in the tactile perception and

  3. Shape memory system with integrated actuation using embedded particles

    Science.gov (United States)

    Buckley, Patrick R [New York, NY; Maitland, Duncan J [Pleasant Hill, CA

    2009-09-22

    A shape memory material with integrated actuation using embedded particles. One embodiment provides a shape memory material apparatus comprising a shape memory material body and magnetic pieces in the shape memory material body. Another embodiment provides a method of actuating a device to perform an activity on a subject comprising the steps of positioning a shape memory material body in a desired position with regard to the subject, the shape memory material body capable of being formed in a specific primary shape, reformed into a secondary stable shape, and controllably actuated to recover the specific primary shape; including pieces in the shape memory material body; and actuating the shape memory material body using the pieces causing the shape memory material body to be controllably actuated to recover the specific primary shape and perform the activity on the subject.

  4. Automated detection of a prostate Ni-Ti stent in electronic portal images.

    Science.gov (United States)

    Carl, Jesper; Nielsen, Henning; Nielsen, Jane; Lund, Bente; Larsen, Erik Hoejkjaer

    2006-12-01

    Planning target volumes (PTV) in fractionated radiotherapy still have to be outlined with wide margins to the clinical target volume due to uncertainties arising from daily shift of the prostate position. A recently proposed new method of visualization of the prostate is based on insertion of a thermo-expandable Ni-Ti stent. The current study proposes a new detection algorithm for automated detection of the Ni-Ti stent in electronic portal images. The algorithm is based on the Ni-Ti stent having a cylindrical shape with a fixed diameter, which was used as the basis for an automated detection algorithm. The automated method uses enhancement of lines combined with a grayscale morphology operation that looks for enhanced pixels separated with a distance similar to the diameter of the stent. The images in this study are all from prostate cancer patients treated with radiotherapy in a previous study. Images of a stent inserted in a humanoid phantom demonstrated a localization accuracy of 0.4-0.7 mm which equals the pixel size in the image. The automated detection of the stent was compared to manual detection in 71 pairs of orthogonal images taken in nine patients. The algorithm was successful in 67 of 71 pairs of images. The method is fast, has a high success rate, good accuracy, and has a potential for unsupervised localization of the prostate before radiotherapy, which would enable automated repositioning before treatment and allow for the use of very tight PTV margins.

  5. Automated detection of a prostate Ni-Ti stent in electronic portal images

    International Nuclear Information System (INIS)

    Carl, Jesper; Nielsen, Henning; Nielsen, Jane; Lund, Bente; Larsen, Erik Hoejkjaer

    2006-01-01

    Planning target volumes (PTV) in fractionated radiotherapy still have to be outlined with wide margins to the clinical target volume due to uncertainties arising from daily shift of the prostate position. A recently proposed new method of visualization of the prostate is based on insertion of a thermo-expandable Ni-Ti stent. The current study proposes a new detection algorithm for automated detection of the Ni-Ti stent in electronic portal images. The algorithm is based on the Ni-Ti stent having a cylindrical shape with a fixed diameter, which was used as the basis for an automated detection algorithm. The automated method uses enhancement of lines combined with a grayscale morphology operation that looks for enhanced pixels separated with a distance similar to the diameter of the stent. The images in this study are all from prostate cancer patients treated with radiotherapy in a previous study. Images of a stent inserted in a humanoid phantom demonstrated a localization accuracy of 0.4-0.7 mm which equals the pixel size in the image. The automated detection of the stent was compared to manual detection in 71 pairs of orthogonal images taken in nine patients. The algorithm was successful in 67 of 71 pairs of images. The method is fast, has a high success rate, good accuracy, and has a potential for unsupervised localization of the prostate before radiotherapy, which would enable automated repositioning before treatment and allow for the use of very tight PTV margins

  6. The effect of heating rate on the surface chemistry of NiTi.

    Science.gov (United States)

    Undisz, Andreas; Hanke, Robert; Freiberg, Katharina E; Hoffmann, Volker; Rettenmayr, Markus

    2014-11-01

    The impact of the heating rate on the Ni content at the surface of the oxide layer of biomedical NiTi is explored. Heat treatment emulating common shape-setting procedures was performed by means of conventional and inductive heating for similar annealing time and temperature, applying various heating rates from ~0.25 K s(-1) to 250 K s(-1). A glow discharge optical emission spectroscopy method was established and employed to evaluate concentration profiles of Ni, Ti and O in the near-surface region at high resolution. The Ni content at the surface of the differently treated samples varies significantly, with maximum surface Ni concentrations of ~20 at.% at the lowest and ~1.5 at.% at the highest heating rate, i.e. the total amount of Ni contained in the surface region of the oxide layer decreases by >15 times. Consequently, the heating rate is a determinant for the biomedical characteristics of NiTi, especially since Ni available at the surface of the oxide layer may affect the hemocompatibility and be released promptly after surgical application of a respective implant. Furthermore, apparently contradictory results presented in the literature reporting surface Ni concentrations of ~3 at.% to >20 at.% after heat treatment are consistently explained considering the ascertained effect of the heating rate. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  7. Shape memory of polyurethanes with silver nanoparticles

    International Nuclear Information System (INIS)

    Monteiro, Fernanda M.A.; Souza, Patterson P. de; Pereira, Iaci M.; Silva, Livio B.J. da; Orefice, Rodrigo L.

    2011-01-01

    Biodegradable polyurethane nano composites were synthesized in an aqueous environment and have their shape memory properties investigated. The matrix based in isopharane diisocyanate and poly(caprolactone diol) (Mn=1250, 2000 g.mol -1 ) was prepared by the prepolymer mixing process. The silver nanoparticles were produced by mixing AgNO 3 and tannic acid. The shape memory properties were measured using universal testing machine (DL3000, EMIC). The shape memory cycle consisted of the following steps: samples were deformed at room temperature; the mechanical constraints on the polymers were removed; samples were cooled down to 0 deg C and to retain the deformed shape; three processes were tested to recover the shape: (a) samples were heated up to 80 deg C in an oven, (b) immersed in pH 4.0 and (c) immersed in pH 7.0. To study the shape memory effect on the nanostructure, small angle X-ray scattering, wide angle X-ray scattering, infrared spectroscopy experiments were carried on. (author)

  8. A bidirectional shape memory alloy folding actuator

    International Nuclear Information System (INIS)

    Paik, Jamie K; Wood, Robert J

    2012-01-01

    This paper presents a low-profile bidirectional folding actuator based on annealed shape memory alloy sheets applicable for meso- and microscale systems. Despite the advantages of shape memory alloys—high strain, silent operation, and mechanical simplicity—their application is often limited to unidirectional operation. We present a bidirectional folding actuator that produces two opposing 180° motions. A laser-patterned nickel alloy (Inconel 600) heater localizes actuation to the folding sections. The actuator has a thin ( < 1 mm) profile, making it appropriate for use in robotic origami. Various design parameters and fabrication variants are described and experimentally explored in the actuator prototype. (paper)

  9. Applicability of Shape Memory Alloy Wire for an Active, Soft Orthotic

    Science.gov (United States)

    Stirling, Leia; Yu, Chih-Han; Miller, Jason; Hawkes, Elliot; Wood, Robert; Goldfield, Eugene; Nagpal, Radhika

    2011-07-01

    Current treatments for gait pathologies associated with neuromuscular disorders may employ a passive, rigid brace. While these provide certain benefits, they can also cause muscle atrophy. In this study, we examined NiTi shape memory alloy (SMA) wires that were annealed into springs to develop an active, soft orthotic (ASO) for the knee. Actively controlled SMA springs may provide variable assistances depending on factors such as when, during the gait cycle, the springs are activated; ongoing muscle activity level; and needs of the wearer. Unlike a passive brace, an active orthotic may provide individualized control, assisting the muscles so that they may be used more appropriately, and possibly leading to a re-education of the neuro-motor system and eventual independence from the orthotic system. A prototype was tested on a suspended, robotic leg to simulate the swing phase of a typical gait. The total deflection generated by the orthotic depended on the knee angle and the total number of actuators triggered, with a max deflection of 35°. While SMA wires have a high energy density, they require a significant amount of power. Furthermore, the loaded SMA spring response times were much longer than the natural frequency of an average gait for the power conditions tested. While the SMA wires are not appropriate for correction of gait pathologies as currently implemented, the ability to have a soft, actuated material could be appropriate for slower timescale applications.

  10. Oxidation Kinetics of a NiPtTi High Temperature Shape Memory Alloy

    Science.gov (United States)

    Smialek, James L.; Humphrey, Donald L.; Noebe, Ronald D.

    2007-01-01

    A high temperature shape memory alloy (HTSMA), Ni30Pt50Ti, with an M(sub s) near 600 C, was isothermally oxidized in air for 100 hr over the temperature range of 500 to 900 C. Parabolic kinetics were confirmed by log-log and parabolic plots and showed no indication of fast transient oxidation. The overall behavior could be best described by the Arrhenius relationship: k(sub p) = 1.64 x 10(exp 12)[(-250 kJ/mole)/RT] mg(sup 2)/cm(sup 4)hr. This is about a factor of 4 reduction compared to values measured here for a binary Ni47Ti commercial SMA. The activation energy agreed with most literature values for TiO2 scale growth measured for elemental Ti and other NiTi alloys. Assuming uniform alloy depletion of a 20 mil (0.5 mm) dia. HTSMA wire, approx. 1 percent Ti reduction is predicted after 20,000 hr oxidation at 500 C, but becomes much more serious at higher temperatures.

  11. Multi-scale analysis of the fatigue of shape memory alloys

    International Nuclear Information System (INIS)

    Zheng, Lin

    2016-01-01

    Shape Memory Alloy (SMA) is a typical smart material having many applications from aerospace industry, mechanical and civil engineering, to biomedical devices, where the material's fatigue is a big concern. One of the challenging issues in studying the fatigue behaviors of SMA polycrystals is the interaction between the material damage and the martensitic phase transformation which takes place in a macroscopic homogeneous mode or a heterogeneous mode (forming macroscopic patterns (Luders-like bands) due to the localized deformations and localized heating/cooling). Such pattern formation and evolution imply the governing physical mechanisms in the material system such as the fatigue process, but there is still no fatigue study of SMAs by tracing the macro-band patterns and the local material responses. To bridge this gap, systematic tensile fatigue experiments are conducted on pseudo-elastic NiTi polycrystalline strips by in-situ optical observation on the band-pattern evolutions and by tracing the deformation history of the cyclic phase transformation zones where fatigue failure occurs. These experimental results help to better understand the stress- and frequency-dependent fatigue behaviors. Particularly, it is found that the local residual strain rather than the structural nominal/global residual strain is a good indicator on the material's damage leading to the fatigue failure, which is important for understanding and modeling the fatigue process in SMAs. (author)

  12. Crack-closing of cement mortar beams using NiTi cold-drawn SMA short fibers

    Science.gov (United States)

    Choi, Eunsoo; Kim, Dong Joo; Chung, Young-Soo; Kim, Hee Sun; Jung, Chungsung

    2015-01-01

    In this study, crack-closing tests of mortar beams reinforced by shape memory alloy (SMA) short fibers were performed. For this purpose, NiTi SMA fibers with a diameter of 0.965 mm and a length of 30 mm were made from SMA wires of 1.0 mm diameter by cold drawing. Four types of SMA fibers were prepared, namely, straight and dog-bone-shaped fiber and the two types of fibers with paper wrapping in the middle of the fibers. The paper provides an unbonded length of 15 mm. For bending tests, six types of mortar beams with the dimensions of 40 mm × 40 mm × 160 mm (B×H×L) were prepared. The SMA fibers were placed at the bottom center of the beams along with an artificial crack of 10 mm depth and 1 mm thickness. This study investigated the influence of SMA fibers on the flexural strength of the beams from the measured force- deflection curves. After cracking, the beams were heated at the bottom by fire to activate the SMA fibers. Then, the beams recovered the deflection, and the cracks were closed. This study evaluated crack-closing capacity using the degree of crack recovery and deflection-recovery factor. The first factor is estimated from the crack-width before and after crack-closing, and the second one is obtained from the downward deflection due to loading and the upward deflection due to the closing force of the SMA fibers.

  13. Shape memory polymer hybrids of SBS/dl-PLA and their shape memory effects

    International Nuclear Information System (INIS)

    Zhang, Heng; Chen, Zhi; Zheng, Zheng; Zhu, Xiaomin; Wang, Haitao

    2013-01-01

    The hybrids of styrene-butadiene-styrene tri-block copolymer (SBS) and amorphous poly(dl-lactic acid) (dl-PLA) are found to exhibit shape memory effects, which gives an example of a dual-domain shape memory system consisting of an elastic domain and a thermo-switch domain. The dual-domain manner in this hybrid is studied by means of differential scanning calorimetry (DSC) and scanning electron microscope (SEM). Subsequently, the tensile test clarifies the interactions of the two domains on shape memory effects. As an elastic domain, SBS offers good shape recovery when its content exceeds 50 wt%. As a thermo-switch domain, dl-PLA triggers the shape memory effect at ca. 55 °C and offers good shape fixing when the content exceeds 30 wt%. An easy-to-do and easy-to-know feature of the hybrid is that the optimization of shape memory effect can be achieved by generating bicontinous phases of SBS and dl-PLA, in which the dl-PLA content ranges from 30 to 70 wt%. -- Highlights: ► The composite materials of SBS and amorphous dl-PLA were prepared by blending. ► A continuous domain was observed with the increasing content of dl-PLA. ► The composites exhibited shape memory effects.

  14. Characterization and tribocorrosion behavior of sputtered NiTi coatings

    Energy Technology Data Exchange (ETDEWEB)

    Jin, XiaoMin; Gao, Lizhen [Taiyuan University of Technology (China). College of Environmental Science and Engineering; Wang, Hefeng [Taiyuan University of Technology (China). College of Mechanics; Liu, Erqiang [Taiyuan University of Technology (China). Inst. of Applied Mechanics and Biomedical Engineering

    2016-02-15

    In this study, NiTi coatings were deposited onto AISI 316L stainless steel substrates by closed field unbalanced magnetron sputtering. The microstructure and properties of the coatings were characterized by means of X-ray diffraction, scanning electron microscopy, and nano-indentation. The tribocorrosion resistance and corrosion behavior of the stainless steel substrates and NiTi coatings were investigated in Hanks' solution. The experimental results indicated the NiTi coatings show higher corrosion polarization resistance and a more stable corrosion potential in the Hanks' solution than the uncoated stainless steel substrate. The NiTi coatings also exhibited excellent wear resistance and chemical stability in sliding tests with an Si{sub 3}N{sub 4} ball in the Hanks' solution. The tested samples showed different wear mechanisms in the sliding tests. Compared to the SS substrates, the NiTi coatings were more compatible with the Si{sub 3}N{sub 4} ball.

  15. On the Stress-Induced Formation of R-Phase in Ultra-Fine-Grained Ni-Rich NiTi Shape Memory Alloys

    Czech Academy of Sciences Publication Activity Database

    Olbricht, J.; Yawny, A.; Pelegrina, J.L.; Dlouhý, Antonín

    42A, č. 9 (2011), s. 2556-2574 ISSN 1073-5623 R&D Projects: GA ČR GA106/09/1913 Institutional research plan: CEZ:AV0Z20410507 Keywords : martensitic transformations * rietveld method * single-crystals Subject RIV: JG - Metallurgy Impact factor: 1.545, year: 2011

  16. Shape-Memory PVDF Exhibiting Switchable Piezoelectricity.

    Science.gov (United States)

    Hoeher, Robin; Raidt, Thomas; Novak, Nikola; Katzenberg, Frank; Tiller, Joerg C

    2015-12-01

    In this study, a material is designed which combines the properties of shape-memory and electroactive polymers. This is achieved by covalent cross-linking of polyvinylidene fluoride. The resulting polymer network exhibits excellent shape-memory properties with a storable strain of 200%, and fixity as well as recovery values of 100%. Programming upon rolling induces the transformation from the nonelectroactive α-phase to the piezoelectric β-phase. The highest β-phase content is found to be 83% for a programming strain of 200% affording a d33 value of -30 pm V(-1). This is in good accordance with literature known values for piezoelectric properties. Thermal triggering this material does not only result in a shape change but also renders the material nonelectroactive. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  17. Microstructure and martensitic transformation of Ni-Ti-Pr alloys

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Chunwang [Inner Mongolia University of Technology, College of Science, Hohhot (China); Shanghai Maritime University, College of Arts and Sciences, Shanghai (China); Zhao, Shilei; Jin, Yongjun; Hou, Qingyu [Inner Mongolia University of Technology, College of Science, Hohhot (China); Guo, Shaoqiang [Beihang University, Key Laboratory of Micro-nano Measurement, Manipulation and Physics (Ministry of Education), Department of Physics, Beijing (China)

    2017-09-15

    The effect of Pr addition on the microstructure and martensitic transformation behavior of Ni{sub 50}Ti{sub 50-x}Pr{sub x} (x = 0, 0.1, 0.3, 0.5, 0.7, 0.9) alloys were investigated experimentally. Results show that the microstructures of Ni-Ti-Pr alloys consist of the NiTi matrix and the NiPr precipitate with the Ti solute. The martensitic transformation start temperature decreases gradually with the increase in Pr fraction. The stress around NiPr precipitates is responsible for the decrease in martensitic transformation temperature with the increase in Pr fraction in Ni-Ti-Pr alloys. (orig.)

  18. Active frequency tuning of the cantilever nanoresonator utilizing a phase transformation of NiTi thin film

    Czech Academy of Sciences Publication Activity Database

    Stachiv, Ivo; Šittner, Petr; Jeng, Y.-R.; Vokoun, David

    2017-01-01

    Roč. 19, č. 7 (2017), s. 5161-5169 ISSN 1392-8716 R&D Projects: GA ČR GC15-13174J Institutional support: RVO:68378271 Keywords : nanoresonator * resonant frequency * thin film * smart memory alloys * NiTi film Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 0.398, year: 2016

  19. In-situ experimental evidence on R-phase related deformation processes in activated NiTi wires

    Czech Academy of Sciences Publication Activity Database

    Šittner, Petr; Sedlák, Petr; Landa, Michal; Novák, Václav; Lukáš, Petr

    438-440, - (2006), s. 579-584 ISSN 0921-5107 R&D Projects: GA AV ČR IAA1048107; GA ČR GA202/04/2016 Institutional research plan: CEZ:AV0Z10100520; CEZ:AV0Z10480505; CEZ:AV0Z20760514 Keywords : memory alloys * NiTi wires * ultrasonics * neutron diffraction Subject RIV: BM - Solid Matter Physics ; Magnetism

  20. Thermoinduced plastic flow and shape memory effects

    Directory of Open Access Journals (Sweden)

    Xiao Heng

    2011-01-01

    Full Text Available We propose an enhanced form of thermocoupled J2-flow models of finite deformation elastoplasticity with temperature-dependent yielding and hardening behaviour. The thermomechanical constitutive structure of these models is rendered free and explicit in the rigorous sense of thermodynamic consistency. Namely, with a free energy function explicitly introduced in terms of almost any given form of the thermomechanical constitutive functions, the requirements from the second law are identically fulfilled with positive internal dissipation. We study the case when a dependence of yielding and hardening on temperature is given and demonstrate that thermosensitive yielding with anisotropic hardening may give rise to appreciable plastic flow either in a process of heating or in a cyclic process of heating/cooling, thus leading to the findings of one- and two-way thermoinduced plastic flow. We then show that such theoretical findings turn out to be the effects found in shape memory materials, such as one- and two-way memory effects. Thus, shape memory effects may be explained to be thermoinduced plastic flow resulting from thermosensitive yielding and hardening behaviour. These and other relevant facts may suggest that, from a phenomenological standpoint, thermocoupled elastoplastic J2-flow models with thermosensitive yielding and hardening may furnish natural, straightforward descriptions of thermomechanical behaviour of shape memory materials.

  1. Effects of surface finish and mechanical training on Ni-Ti sheets for elastocaloric cooling

    DEFF Research Database (Denmark)

    Engelbrecht, Kurt; Tusek, Jaka; Sanna, Simone

    2016-01-01

    Elastocaloric cooling has emerged as a promising alternative to vapor compression in recent years. Although the technology has the potential to be more efficient than current technologies, there are many technical challenges that must be overcome to realize devices with high performance...... and acceptable durability. We study the effects of surface finish and training techniques on dog bone shaped polycrystalline samples of NiTi. The fatigue life of several samples with four different surface finishes was measured and it was shown that a smooth surface, especially at the edges, greatly improved...

  2. Manufacture and tests of shape memory actuators for bolted joints of the oil and gas industry; Fabricacao e testes de atuadores de ligas com memoria de forma para unioes aparafusadas do setor de petroleo e gas

    Energy Technology Data Exchange (ETDEWEB)

    Silva, Niedson J. da; Silva, Marcos M. da [Universidade Federal de Campina Grande (UFCG), PB (Brazil). Curso de Pos-graduacao em Ciencia e Engenharia de Materiais; Araujo, Carlos J. de; Santos, Marco A. dos [Universidade Federal de Campina Grande (UFCG), PB (Brazil). Dept. de Engenharia Mecanica

    2008-07-01

    Shape memory alloys (SMA) actuators have a great potential for applications in the engineering field due to the ability of mechanical force generation through the Shape Memory Effect (SME). The SME behavior is the capacity of SMA remember a form established previously when submitted to a temperature variation. In the oil and gas industry there is a variety of possible applications for these active materials, from thermostatic valves to safety devices for piping. Thus, the aim of this work was to study the technical viability of developing SMA washers for potential application in bolted joints of pipelines to improve the reliability of these joints. NiTi SMA washer actuators were produced through casting by plasma skull melting and molding by Push Pull method using the Discovery all machine from EDG equipment and controls. The NiTi SMA washers were obtained and analyzed using electrical resistance and force generation as a function of temperature. The results of force generation as a function of the temperature have demonstrated that important mechanical efforts can be obtained, justifying the application of these SMA for pipeline joints employed in the oil and gas industry. (author)

  3. Novel silver-doped NiTiO3: auto-combustion synthesis ...

    African Journals Online (AJOL)

    ... Ag-NiTiO3 film was directly deposited on top of the TiO2 prepared by electrophoresis deposition method. Furthermore, solar cell result indicates that an inexpensive solar cell could be developed by the synthesized Ag-NiTiO3 nanoparticles. Keywords: Ag-NiTiO3, sol-gel method, semiconductor, photovoltaic, doping ...

  4. High-Temperature Shape Memory Polymers

    Science.gov (United States)

    Yoonessi, Mitra; Weiss, Robert A.

    2012-01-01

    physical conformation changes when exposed to an external stimulus, such as a change in temperature. Such materials have a permanent shape, but can be reshaped above a critical temperature and fixed into a temporary shape when cooled under stress to below the critical temperature. When reheated above the critical temperature (Tc, also sometimes called the triggering or switching temperature), the materials revert to the permanent shape. The current innovation involves a chemically treated (sulfonated, carboxylated, phosphonated, or other polar function group), high-temperature, semicrystalline thermoplastic poly(ether ether ketone) (Tg .140 C, Tm = 340 C) mix containing organometallic complexes (Zn++, Li+, or other metal, ammonium, or phosphonium salts), or high-temperature ionic liquids (e.g. hexafluorosilicate salt with 1-propyl-3- methyl imidazolium, Tm = 210 C) to form a network where dipolar or ionic interactions between the polymer and the low-molecular-weight or inorganic compound forms a complex that provides a physical crosslink. Hereafter, these compounds will be referred to as "additives". The polymer is semicrystalline, and the high-melt-point crystals provide a temporary crosslink that acts as a permanent crosslink just so long as the melting temperature is not exceeded. In this example case, the melting point is .340 C, and the shape memory critical temperature is between 150 and 250 C. PEEK is an engineering thermoplastic with a high Young fs modulus, nominally 3.6 GPa. An important aspect of the invention is the control of the PEEK functionalization (in this example, the sulfonation degree), and the thermal properties (i.e. melting point) of the additive, which determines the switching temperature. Because the compound is thermoplastic, it can be formed into the "permanent" shape by conventional plastics processing operations. In addition, the compound may be covalently cross - linked after forming the permanent shape by S-PEEK by applying ionizing

  5. Design of shape memory alloy (SMA) actuators

    CERN Document Server

    Rao, Ashwin; Reddy, J N

    2015-01-01

    This short monograph presents an analysis and design methodology for shape memory alloy (SMA) components such as wires, beams, and springs for different applications. The solid-solid, diffusionless phase transformations in thermally responsive SMA allows them to demonstrate unique characteristics like superelasticity and shape memory effects. The combined sensing and actuating capabilities of such materials allows them to provide a system level response by combining multiple functions in a single material system. In SMA, the combined mechanical and thermal loading effects influence the functionality of such materials. The aim of this book is to make the analysis of these materials accessible to designers by developing a "strength of materials" approach to the analysis and design of such SMA components inspired from their various applications with a review of various factors influencing the design process for such materials.

  6. Constitutive Models for Shape Memory Alloy Polycrystals

    Science.gov (United States)

    Comstock, R. J., Jr.; Somerday, M.; Wert, J. A.

    1996-01-01

    Shape memory alloys (SMA) exhibiting the superelastic or one-way effects can produce large recoverable strains upon application of a stress. In single crystals this stress and resulting strain are very orientation dependent. We show experimental stress/strain curves for a Ni-Al single crystal for various loading orientations. Also shown are model predictions; the open and closed circles indicate recoverable strains obtained at various stages in the transformation process. Because of the strong orientation dependence of shape memory properties, crystallographic texture can be expected to play an important role in the mechanical behavior of polycrystalline SMA. It is desirable to formulate a constitutive model to better understand and exploit the unique properties of SMA.

  7. A bridge column with superelastic NiTi SMA and replaceable rubber hinge for earthquake damage mitigation

    Science.gov (United States)

    Varela, Sebastian; ‘Saiid' Saiidi, M.

    2016-07-01

    This paper reports a unique concept for resilient bridge columns that can undergo intense earthquake loading and remain functional with minimal damage and residual drift. In this concept, the column is designed so that its components can be easily disassembled and reassembled to facilitate material recycling and component reuse. This is meant to foster sustainability of bridge systems while minimizing monetary losses from earthquakes. Self-centering and energy dissipation in the column were provided by unbonded superelastic nickel-titanium (NiTi) shape memory alloy bars placed inside a plastic hinge element made of rubber. This replaceable plastic hinge was in turn attached to a concrete-filled carbon fiber-reinforced polymer tube and a precast concrete footing that were designed to behave elastically. The proposed concept was evaluated experimentally by testing a ¼-scale column model under simulated near-fault earthquake motions on a shake table. After testing, the model was disassembled, reassembled and tested again. The seismic performance of the reassembled model was found to be comparable to that of the ‘virgin’ model. A relatively simple computational model of the column tested that was developed in OpenSees was able to match some of the key experimental response parameters.

  8. Quasistatic isothermal evolution of shape memory alloys

    Czech Academy of Sciences Publication Activity Database

    Frigeri, S.; Krejčí, Pavel; Stefanelli, U.

    2011-01-01

    Roč. 21, č. 12 (2011), s. 2409-2432 ISSN 0218-2025 R&D Projects: GA ČR GAP201/10/2315 Institutional research plan: CEZ:AV0Z10190503 Keywords : shape memory alloys * quasistatic evolution Subject RIV: BA - General Mathematics Impact factor: 1.635, year: 2011 http://www.worldscinet.com/m3as/21/2112/S0218202511005787.html

  9. Guide wire extension for shape memory polymer occlusion removal devices

    Science.gov (United States)

    Maitland, Duncan J [Pleasant Hill, CA; Small, IV, Ward; Hartman, Jonathan [Sacramento, CA

    2009-11-03

    A flexible extension for a shape memory polymer occlusion removal device. A shape memory polymer instrument is transported through a vessel via a catheter. A flexible elongated unit is operatively connected to the distal end of the shape memory polymer instrument to enhance maneuverability through tortuous paths en route to the occlusion.

  10. An in situ Study of NiTi Powder Sintering Using Neutron Diffraction

    Directory of Open Access Journals (Sweden)

    Gang Chen

    2015-04-01

    Full Text Available This study investigates phase transformation and mechanical properties of porous NiTi alloys using two different powder compacts (i.e., Ni/Ti and Ni/TiH2 by a conventional press-and-sinter means. The compacted powder mixtures were sintered in vacuum at a final temperature of 1373 K. The phase evolution was performed by in situ neutron diffraction upon sintering and cooling. The predominant phase identified in all the produced porous NiTi alloys after being sintered at 1373 K is B2 NiTi phase with the presence of other minor phases. It is found that dehydrogenation of TiH2 significantly affects the sintering behavior and resultant microstructure. In comparison to the Ni/Ti compact, dehydrogenation occurring in the Ni/TiH2 compact leads to less densification, yet higher chemical homogenization, after high temperature sintering but not in the case of low temperature sintering. Moreover, there is a direct evidence of the eutectoid decomposition of NiTi at ca. 847 and 823 K for Ni/Ti and Ni/TiH2, respectively, during furnace cooling. The static and cyclic stress-strain behaviors of the porous NiTi alloys made from the Ni/Ti and Ni/TiH2 compacts were also investigated. As compared with the Ni/Ti sintered samples, the samplessintered from the Ni/TiH2 compact exhibited a much higher porosity, a higher close-to-total porosity, a larger pore size and lower tensile and compressive fracture strength.

  11. Ni-Ti Next Generation Bearings for Space Applications

    Science.gov (United States)

    DellaCorte, Christopher

    2018-01-01

    NASA applications challenge traditional bearing materials. The rigors of launch often include heavy shock loads and exposure to corrosive environments (e.g., salt spray). Unfortunately, ball and roller bearings made from hardened steels are vulnerable to Brinell denting and rust which can limit performance and life. Ceramic materials can eliminate corrosion concerns but their high stiffness and extreme hardness actually makes denting problems worse. In this presentation, an emerging superelastic alloy, NiTi, is introduced for rolling element bearing applications. Through a decade of RD, NiTi alloy bearings have been put through a comprehensive series of life and performance tests. Hardness, corrosion, strength, stiffness, and rolling contact fatigue tests have been conducted and reported. Ball bearings ranging in size from 12 to 50mm bore have been successfully engineered and operated over a wide range of speeds and test conditions including being submerged in water. The combination of high hardness, moderate elastic modulus, low density, and intrinsic corrosion immunity provide new possibilities for mechanisms that operate under extreme conditions. Recent preliminary tests indicate that bearings can be made from NiTi alloys that are easily lubricated by conventional oils and greases and exhibit acceptable rolling contact fatigue resistance. This presentation introduces the NiTi materials systems and shows how NASA is using it to alleviate several specific problems encountered in advanced space applications.

  12. An Investigation of the Micro-Electrical Discharge Machining of Nickel-Titanium Shape Memory Alloy Using Grey Relations Coupled with Principal Component Analysis

    Directory of Open Access Journals (Sweden)

    Mustufa Haider Abidi

    2017-11-01

    Full Text Available Shape memory alloys (SMAs are advanced engineering materials which possess shape memory effects and super-elastic properties. Their high strength, high wear-resistance, pseudo plasticity, etc., makes the machining of Ni-Ti based SMAs difficult using traditional techniques. Among all non-conventional processes, micro-electric discharge machining (micro-EDM is considered one of the leading processes for micro-machining, owing to its high aspect ratio and capability to machine hard-to-cut materials with good surface finish.The selection of the most appropriate input parameter combination to provide the optimum values for various responses is very important in micro-EDM. This article demonstrates the methodology for optimizing multiple quality characteristics (overcut, taper angle and surface roughness to enhance the quality of micro-holes in Ni-Ti based alloy, using the Grey–Taguchi method. A Taguchi-based grey relational analysis coupled with principal component analysis (Grey-PCA methodology was implemented to investigate the effect of three important micro-EDM process parameters, namely capacitance, voltage and electrode material.The analysis of the individual responses established the importance of multi-response optimization. The main effects plots for the micro-EDM parameters and Analysis of Variance (ANOVA indicate that every parameter does not produce same effect on individual responses, and also that the percent contribution of each parameter to individual response is highly varied. As a result, multi-response optimization was implemented using Grey-PCA. Further, this study revealed that the electrode material had the strongest effect on the multi-response parameter, followed by the voltage and capacitance. The main effects plot for the Grey-PCA shows that the micro-EDM parameters “capacitance” at level-2 (i.e., 475 pF, “discharge voltage” at level-1 (i.e., 80 V and the “electrode material” Cu provided the best multi-response.

  13. Design of Fatigue Resistant Heusler-strengthened PdTi-based Shape Memory Alloys for Biomedical Applications

    Science.gov (United States)

    Frankel, Dana J.

    The development of non-surgical transcatheter aortic valve implantation (TAVI) techniques, which utilize collapsible artificial heart valves with shape memory alloy (SMA)-based frames, pushes performance requirements for biomedical SMAs beyond those for well-established vascular stent applications. Fatigue life for these devices must extend into the ultra-high cycle fatigue (UHCF) regime (>600M cycles) with zero probability of failure predicted at applied strain levels. High rates of Ni-hypersensitivity raise biocompatibility concerns, driving the development of low-Ni and Ni-free SMAs. This work focuses on the development of biocompatible, precipitation-strengthened, fatigue-resistant PdTi-based SMAs for biomedical applications. Functional and structural fatigue are both manifestations of cyclic instability resulting in accumulation of slip and eventual structural damage. While functional fatigue is easily experimentally evaluated, structural fatigue is more difficult to measure without the proper equipment. Therefore, in this work a theoretical approach using a model well validated in steels is utilized to investigate structural fatigue behavior in NiTi in the UHCF regime, while low cycle functional fatigue is evaluated in order to monitor the core phenomena of the cyclic instability. Results from fatigue simulations modeling crack nucleation at non-metallic inclusions in commercial NiTi underscore the importance of increasing yield strength for UHCF performance. Controlled precipitation of nanoscale, low-misfit, L21 Heusler aluminides can provide effective strengthening. Phase relations, precipitation kinetics, transformation temperature, transformation strain, cyclic stability, and mechanical properties are characterized in both Ni-free (Pd,Fe)(Ti,Al) and low-Ni high-strength "hybrid" (Pd,Ni)(Ti,Zr,Al) systems. Atom probe tomography is employed to measure phase compositions and particle sizes used to calibrate LSW models for coarsening kinetics and Gibbs

  14. Joint made of shape memory alloy

    International Nuclear Information System (INIS)

    Amano, Kazuo; Enomoto, Kunio

    1998-01-01

    The present invention provides a joint which is less loosen even if it is used under a circumference undergoing heat cycles such as in a nuclear power plant. Namely, a liner shape has a structure different between the right-to-left, which is different from existent right and left symmetrical shape. A groove is formed on the side of pipeline to be connected, and upon joint connection, the liner is pushed into the groove formed on the pipeline to connect them by the force caused upon transformation of the shape memory alloy. In the joint having such a structure, the clamping force of the joint is less reduced by the effects of heat cycles. Even when the clamping force is reduced by some or other causes, the joint is not dropped off from the pipeline. Even when the joint made of a shape memory alloy of a type using a liner is used as a joint for connecting longitudinal pipelines of a nuclear power plant, the reliability and the safety can be maintained. (I.S.)

  15. Isothermal recovery rates in shape memory polyurethanes

    International Nuclear Information System (INIS)

    Azra, Charly; Plummer, Christopher J G; Månson, Jan-Anders E

    2011-01-01

    This work compares the time dependence of isothermal shape recovery in thermoset and thermoplastic shape memory polyurethanes (SMPUs) with comparable glass transition temperatures. In each case, tensile tests have been used to quantify the influence of various thermo-mechanical programming parameters (deformation temperature, recovery temperature, and stress and storage times following the deformation step) on strain recovery under zero load (free recovery) and stress recovery under fixed strain (constrained recovery). It is shown that the duration of the recovery event may be tuned over several decades of time with an appropriate choice of programming parameters, but that there is a trade-off between the rate of shape recovery and the recoverable stress level. The results are discussed in terms of the thermal characteristics of the SMPUs in the corresponding temperature range as characterized by modulated differential scanning calorimetry and dynamic mechanical analysis, with the emphasis on the role of the effective width of the glass transition temperature and the stability of the network that gives rise to the shape memory effect. (fast track communication)

  16. Two-way shape memory behavior of shape memory polyurethanes with a bias load

    International Nuclear Information System (INIS)

    Hong, Seok Jin; Yu, Woong-Ryeol; Youk, Ji Ho

    2010-01-01

    Thermo-responsive shape memory polyurethane (SMPU) is a smart material that can respond to external heat by changing its macroscopic shape from a temporary configuration to a memorized permanent one. The temporary shape can be processed using mechanical forces above a certain temperature (the transition temperature) and can be maintained until the material acquires a certain thermal energy. Thereafter, the material will recover its memorized permanent shape. However, it is unclear what will occur if the thermal energy is then dissipated, i.e., the material temperature decreases. There are two possibilities: the material will respond to the dissipated energy, resulting in another macroscopic shape change; or nothing will happen beyond the thermal contraction. The former is called two-way shape memory (TWSM) behavior and the latter is called one-way shape memory behavior. This paper reports novel findings showing that TWSM behavior can be imparted to SMPUs using a thermo-mechanical treatment, i.e., imposing a constant stress on them after their temporary shaping. A series of experiments were carried out to characterize the TWSM behavior of SMPUs and to explain its mechanism

  17. In situ observation and neutron diffraction of NiTi powder sintering

    International Nuclear Information System (INIS)

    Chen, Gang; Liss, Klaus-Dieter; Cao, Peng

    2014-01-01

    This study investigated NiTi powder sintering behaviour from elemental powder mixtures of Ni/Ti and Ni/TiH 2 using in situ neutron diffraction and in situ scanning electron microscopy. The sintered porous alloys have open porosities ranging from 2.7% to 36.0%. In comparison to the Ni/Ti compact, dehydrogenation occurring in the Ni/TiH 2 compact leads to less densification yet higher chemical homogenization only after high-temperature sintering. For the first time, direct evidence of the eutectoid phase transformation of NiTi at 620 °C is reported by in situ neutron diffraction. A comparative study of cyclic stress–strain behaviours of the porous NiTi alloys made from Ni/Ti and Ni/TiH 2 compacts indicate that the samples sintered from the Ni/TiH 2 compact exhibited a much higher porosity, larger pore size, lower fracture strength, lower close-to-overall porosity ratio and lower Young’s modulus. Instead of enhanced densification by the use of TiH 2 as reported in the literature, this study shows an adverse effect of TiH 2 on powder densification in NiTi

  18. Effect of Upper-Cycle Temperature on the Load-Biased, Strain-Temperature Response of NiTi

    Science.gov (United States)

    Padula, Santo, II; Noebe, Ronald; Bigelow, Glen; Qiu, Shipeng; Vaidyanathan, Raj; Gaydosh, Darrell; Garg, Anita

    2011-01-01

    Over the past decade, interest in shape memory alloy based actuators has increased as the primary benefits of these solid-state devices have become more apparent. However, much is still unknown about the characteristic behavior of these materials when used in actuator applications. Recently we have shown that the maximum temperature reached during thermal cycling under isobaric conditions could significantly affect the observed mechanical response of NiTi (55 wt% Ni), especially the amount of transformation strain available for actuation and thus work output. The investigation we report here extends that original work to ascertain whether further increases in the upper-cycle temperature would produce additional changes in the work output of the material, which has a stress-free austenite finish temperature of 113 C, and to determine the optimum cyclic conditions. Thus, isobaric, thermal-cycle experiments were conducted on the aforementioned alloy at various stresses from 50-300 MPa using upper-cycle temperatures of 165, 200, 230, 260, 290, 320 and 350 C. The data indicated that the amount of applied stress influenced the transformation strain, as would be expected. However, the maximum temperature reached during the thermal excursion also plays an equally significant role in determining the transformation strain, with the maximum transformation strain observed during thermal cycling to 290 C. In situ neutron diffraction at stress and temperature showed that the differences in transformation strain were mostly related to changes in martensite texture when cycling to different upper-cycle temperatures. Hence, understanding this effect is important to optimizing the operation of SMA-based actuators and could lead to new methods for processing and training shape memory alloys for optimal performance.

  19. Mechanical Degradation of Porous NiTi Alloys Under Static and Cyclic Loading

    Science.gov (United States)

    Hosseini, Seyyed Alireza

    2017-12-01

    Pore characteristics and morphology have significant effect on mechanical behavior of porous NiTi specimens. In this research, porous NiTi with different pore sizes, shapes and morphology were produced by powder metallurgy methods using space-holder materials. The effect of the pore characteristics on the mechanical properties was investigated by static and cyclic compression tests at body temperature. The results show that specimens with low porosity and isolated pores exhibit more mechanical strength and recoverable strain. The specimen with 36% porosity produced without space holder could preserve its properties up to 10% strain and its strain recovery was complete after cyclic compression tests. On the other hand, the specimens produced by a urea space holder with more than 60% interconnected porosity show rapid degradation of their scaffolds. The highly porous specimens degraded even below 5% strain due to crack formation and propagation in the thin pore walls. For highly porous specimens produced by a NaCl space holder, the pores are partially interconnected with a cubic shape; nevertheless, their mechanical behavior is close to low-porosity specimens.

  20. On the thermomechanical deformation of silver shape memory nanowires

    International Nuclear Information System (INIS)

    Park, Harold S.; Ji, Changjiang

    2006-01-01

    We present an analysis of the uniaxial thermomechanical deformation of single-crystal silver shape memory nanowires using atomistic simulations. We first demonstrate that silver nanowires can show both shape memory and pseudoelastic behavior, then perform uniaxial tensile loading of the shape memory nanowires at various deformation temperatures, strain rates and heat transfer conditions. The simulations show that the resulting mechanical response of the shape memory nanowires depends strongly upon the temperature during deformation, and can be fundamentally different from that observed in bulk polycrystalline shape memory alloys. The energy and temperature signatures of uniaxially loaded silver shape memory nanowires are correlated to the observed nanowire deformation, and are further discussed in comparison to bulk polycrystalline shape memory alloy behavior

  1. The Effect of Shape Memory on Red Blood Cell Motions

    Science.gov (United States)

    Niu, Xiting; Shi, Lingling; Pan, Tsorng-Whay; Glowinski, Roland

    2013-11-01

    An elastic spring model is applied to study the effect of the shape memory on the motion of red blood cell in flows. In shear flow, shape memory also plays an important role to obtain all three motions: tumbling, swinging, and tank-treading. In Poiseuille flow, cell has an equilibrium shape as a slipper or parachute depending on capillary number. To ensure the tank-treading motion while in slippery shape, a modified model is proposed by introducing a shape memory coefficient which describes the degree of shape memory in cells. The effect of the coefficient on the cell motion of red blood cell will be presented.

  2. Shape memory alloys as damping materials

    International Nuclear Information System (INIS)

    Humbeeck, J. van

    2000-01-01

    Shape memory alloys are gaining an increased interest as passive as well as active damping materials. This damping ability when applied in structural elements can lead to a better noise control, improved life time and even better performance of the envisaged tools. By passive damping, it is understood that the material converts a significant part of unwanted mechanical energy into heat. This mechanical energy can be a (resonance) vibration, impact loading or shock waves. This high damping capacity finds its origin in the thermoelastic martensitic phase due to the hysteretic mobility of martensite-variants or different phase interfaces. The damping capacity increases with increasing amplitude of the applied vibration or impact and is almost frequency independent. Special interest exists moreover for damping extreme large displacements by applying the mechanical hysteresis performed during pseudoelastic loading. This aspect is nowadays very strongly studied as a tool for protecting buildings against earthquakes in seismic active regions. Active damping can be obtained in hybrid composites by controlling the recovery stresses or strains of embedded shape memory alloy wires. This controls the internal energy fo a structure which allows controlled modal modification and tuning of the dynamical properties of structural elements. But also impact damage, acoustic radiation, dynamic shape control can be actively controlled. As a consequence improved fatigue-resistance, better performance and a longer lifetime of the structural elements can be obtained. (orig.)

  3. Shape Memory Actuator: thermomechanical training and surface optimization of shape memory wires embedded in a polymeric matrix

    OpenAIRE

    Scoponi, Martina

    2011-01-01

    In the first part of my work I studied the mechanical and thermal behaviour of NiTi wires and strips in order to find the best training cycle to achieve a good compromise between transformation temperatures, recovery forces and phase reversibility. Other parameters such as the stress-rate and maximum recovery deformations, useful to realize smart composites, were evaluated. DSC and DMTA analyses were performed on NiTi thin strips that were cold rolled with different thickness r...

  4. Shape-Memory-Alloy Actuator For Flight Controls

    Science.gov (United States)

    Barret, Chris

    1995-01-01

    Report proposes use of shape-memory-alloy actuators, instead of hydraulic actuators, for aerodynamic flight-control surfaces. Actuator made of shape-memory alloy converts thermal energy into mechanical work by changing shape as it makes transitions between martensitic and austenitic crystalline phase states of alloy. Because both hot exhaust gases and cryogenic propellant liquids available aboard launch rockets, shape-memory-alloy actuators exceptionally suited for use aboard such rockets.

  5. Microfabricated Cantilevers Based on Sputtered Thin-Film Ni50Ti50 Shape Memory Alloy (SMA)

    Science.gov (United States)

    2015-08-01

    surface coating developed during the NiTi deposition or anneal that is relatively resistant to the wet etch. Fig. 2 SEMs after the NiTi wet -etch...SEMs of NiTi devices after the 600 °C anneal , wet -etch patterning of the NiTi. A 120-nm Au capping layer was also sputtered. Figure 3a shows a 200-nm...Ni50Ti50 Cantilever 2 3. Results and Discussion 3 3.1 Wet -Etch Patterning NiTi 3 3.2 Dry-Etch Release of NiTi Devices 5 3.3 Thermal Actuation of

  6. Effect of indentation temperature on nickel-titanium indentation-induced two-way shape-memory surfaces

    International Nuclear Information System (INIS)

    Brinckmann, Stephan A.; Frensemeier, Mareike; Laursen, Christopher M.; Maier, Hans J.; Britz, Dominik; Schneider, Andreas S.; Mücklich, Frank; Frick, Carl P.

    2016-01-01

    This study investigated the effect of temperature on indentation-induced one-way and two-way shape memory properties in Ti-50.3 at% Ni alloy. Indentation temperatures ranged from below the martensite finish temperature (M f ) to above the austenite finish temperature (A f ) with the explicit intent of varying the indented phase. Samples used in the study were characterized by differential scanning calorimetry and transmission electron microscopy (TEM). The topographical behavior of the shape memory effect was investigated through Vickers indentation and laser scanning 3D confocal measurements. The magnitudes of deformation recovery associated with the one-way and two-way shape-memory effect (OWSME, TWSME) decreased with increasing indentation temperatures, which is a reflection of the decreasing volume of material experiencing martensitic reorientation during indentation. Indented and subsequently planarized samples exhibited TWSME protrusions when thermally cycled. Laser scanning measurements were used to characterize the height of the protrusions as increasing depths of material were polished away, which provided insight into the overall affected volume beneath the indent. As indentation temperatures increased, both the height of the protrusions, and consequently the polish depth necessary to completely remove the effect, decreased. TEM investigations revealed that directly underneath a nanoindent the microstructure was very fine due to the high-strain deformation; this was contrasted with a much coarser grain size in the undeformed bulk material. Overall these results strongly imply that the deformation recovery associated with the OWSME and TWSME can be maximized by indenting at temperatures at M f or below because the volume of deformed microstructure beneath the indent is maximized. This finding has important practical value for any potential application that utilizes indentation-induced phase transformation deformation recovery in NiTi.

  7. Effect of indentation temperature on nickel-titanium indentation-induced two-way shape-memory surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Brinckmann, Stephan A. [University of Wyoming, Mechanical Engineering Department, Laramie (United States); Frensemeier, Mareike [INM - Leibniz Institute for New Materials, Saarbrücken (Germany); Laursen, Christopher M. [University of Wyoming, Mechanical Engineering Department, Laramie (United States); Maier, Hans J. [Leibniz Universität Hannover, Institut für Werkstoffkunde (Materials Science), Garbsen (Germany); Britz, Dominik [Saarland University, Department of Materials Science and Engineering, Saarbrücken (Germany); Schneider, Andreas S. [AG der Dillinger Hüttenwerke, Department for Research, Development and Plate-Design, Dillingen (Germany); Mücklich, Frank [Saarland University, Department of Materials Science and Engineering, Saarbrücken (Germany); Frick, Carl P., E-mail: cfrick@uwyo.edu [University of Wyoming, Mechanical Engineering Department, Laramie (United States)

    2016-10-15

    This study investigated the effect of temperature on indentation-induced one-way and two-way shape memory properties in Ti-50.3 at% Ni alloy. Indentation temperatures ranged from below the martensite finish temperature (M{sub f}) to above the austenite finish temperature (A{sub f}) with the explicit intent of varying the indented phase. Samples used in the study were characterized by differential scanning calorimetry and transmission electron microscopy (TEM). The topographical behavior of the shape memory effect was investigated through Vickers indentation and laser scanning 3D confocal measurements. The magnitudes of deformation recovery associated with the one-way and two-way shape-memory effect (OWSME, TWSME) decreased with increasing indentation temperatures, which is a reflection of the decreasing volume of material experiencing martensitic reorientation during indentation. Indented and subsequently planarized samples exhibited TWSME protrusions when thermally cycled. Laser scanning measurements were used to characterize the height of the protrusions as increasing depths of material were polished away, which provided insight into the overall affected volume beneath the indent. As indentation temperatures increased, both the height of the protrusions, and consequently the polish depth necessary to completely remove the effect, decreased. TEM investigations revealed that directly underneath a nanoindent the microstructure was very fine due to the high-strain deformation; this was contrasted with a much coarser grain size in the undeformed bulk material. Overall these results strongly imply that the deformation recovery associated with the OWSME and TWSME can be maximized by indenting at temperatures at M{sub f} or below because the volume of deformed microstructure beneath the indent is maximized. This finding has important practical value for any potential application that utilizes indentation-induced phase transformation deformation recovery in NiTi.

  8. Synthesis, Characterization, and NIR Reflectance of Highly Dispersed NiTiO3 and NiTiO3/TiO2 Composite Pigments

    Directory of Open Access Journals (Sweden)

    Yuping Tong

    2016-01-01

    Full Text Available The highly dispersed nanostructured NiTiO3 pigments and NiTiO3/TiO2 composite pigments can be synthesized at relative low temperature. The activation energy of crystal growth of NiTiO3 during calcinations via salt-assistant combustion method is 9.35 kJ/mol. The UV-vis spectra results revealed that the absorbance decreased with the increasing of calcinations temperature due to small size effect of nanometer particles. The optical data of NiTiO3 nanocrystals were analyzed at the near-absorption edge. SEM showed that the obtained NiTiO3 nanocrystals and NiTiO3/TiO2 nanocomposite were composed of highly dispersed spherical-like and spherical particles with uniform size distribution, respectively. The chromatic properties and diffuse reflectance of samples were investigated. The obtained NiTiO3/TiO2 composite samples have higher NIR reflectance than NiTiO3 pigments.

  9. On the hydrodynamic characterization of a passive Shape Memory Alloy valve

    International Nuclear Information System (INIS)

    Waddell, A.M.; Punch, J.; Stafford, J.; Jeffers, N.

    2015-01-01

    An attractive approach to the thermal management of next generation photonics devices (heat fluxes > 10 2  W/cm 2 ) is micro-channel cooling, and micro-valves will be required for refined flow control in the supporting micro-fluidic systems. In this paper, a NiTi Shape Memory Alloy (SMA) micro-valve design for passive flow control and thermal management was prototyped at the macro scale and hydrodynamically characterized. The dynamic behavior of the valve was observed and the loss coefficient (ζ v ) derived from pressure-flow measurements. The hydrodynamic characterization study is important because ζ v is sensitive to Re and geometry in the flow regime of the micro-fluidic system. Static replicas of the SMA valve geometry were tested for low Re (110–220) and a range of opening ratios (β) in a ø1 mm miniature channel. The loss coefficients were found to be sensitive to flow rate and decreased rapidly with an increase in Re. A correlation was developed to interpolate ζ v from a given Re and β. The valve loss coefficients obtained in this work are important parameters in the modeling and design of future micro-fluidic cooling systems. - Highlights: • A miniature normally closed passive SMA valve for micro-fluidic cooling of Photonics devices is demonstrated in this paper. • The passive dynamic behaviour of the valve in response to temperature change is observed. • The design is hydrodynamically characterized through pressure-flow measurements. • A correlation for head loss across the valve as a function of Re and blockage ratio is presented

  10. Mechanical properties and theoretical modeling of self-centering shape memory alloy pseudo-rubber

    International Nuclear Information System (INIS)

    Li, Suchao; Mao, Chenxi; Li, Hui; Zhao, Yagebai

    2011-01-01

    Pounding between adjacent components and structures has become an important cause of structural damage or even collapse under large excitations such as earthquakes and ship collisions. Shock absorber devices (SAD) are often used to connect the separation gap to reduce the pounding force. However, some shock absorber devices may have residual deformation and need to be repaired or replaced after strong impact. A novel energy absorbing material with residual deformation self-recovery ability, martensitic nickel titanium (NiTi) shape memory alloy pseudo-rubber (SMAPR), is fabricated using three methods in this study. The mechanical properties of SMAPR at room temperature and deformation self-recovery ability of SMAPR material are investigated. After that, the deformation recovery ability of SMAPR specimens even with residual deformation is further tested through heating the specimens in a thermo-control stove. The subsequent mechanical properties after deformation recovery are further investigated to investigate whether degradation in mechanical properties occurs for all kinds of specimens. The experimental results indicate that SMAPR is a kind of material with good potential to develop novel shock absorber devices for engineering applications. Furthermore, theoretical modeling of SMAPR is conducted. Micro-variable-pitch springs in parallel and series, in parallel with a friction component, are employed to model the mechanical behavior of SMAPR. The hysteretic rules are presented and the parameters of this model are derived and identified. Finally, based on micro-variable-pitch springs (MVPS) in parallel and series, a parametric analysis is carried out and the effects of nominal densities, diameters of metal wires, diameters of micro-springs and generalized coefficients of friction of SMAPR are analyzed and discussed

  11. Fast Torsional Artificial Muscles from NiTi Twisted Yarns.

    Science.gov (United States)

    Mirvakili, Seyed M; Hunter, Ian W

    2017-05-17

    Torsional artificial muscles made of multiwalled carbon nanotube/niobium nanowire yarns have shown remarkable torsional speed and gravimetric torque. The muscle structure consists of a twisted yarn with half of its length infiltrated with a stimuli-responsive guest material such as paraffin wax. The volumetric expansion of the guest material creates the torsional actuation in the yarn. In the present work, we show that this type of actuation is not unique to wax-infiltrated carbon multiwalled nanotube (MWCNT) or niobium nanowire yarns and that twisted yarn of NiTi alloy fibers also produces fast torsional actuation. By gold-plating half the length of a NiTi twisted yarn and Joule heating it, we achieved a fully reversible torsional actuation of up to 16°/mm with peak torsional speed of 10 500 rpm and gravimetric torque of 8 N·m/kg. These results favorably compare to those of MWCNTs and niobium nanowire yarns.

  12. Ni-TiC涂层耐磨性研究

    Institute of Scientific and Technical Information of China (English)

    罗文

    2014-01-01

    由于TiC的脆性比较大,而Ni具有良好的延展性,因此将TiC和Ni制作成强度韧性较好的复合涂层。利用超高速电热爆炸定向喷涂装置在A3钢基体上制备了TIC及Ni-TiC复合涂层,使用MLS-225型湿砂橡胶轮式磨损试验机对涂层进行了耐磨性试验,结果表明:Ni-TiC复合涂层具有很好的耐磨性。

  13. The amorphous phase transition in irradiated NiTi alloy

    International Nuclear Information System (INIS)

    Brimhall, J.L.; Kissinger, H.E.; Pelton, A.R.

    1985-01-01

    Observed supralinear dose dependence for the amorphous transformation during irradiation of NiTi is compatible with a cascade overlap model for heavy ion (2.5 MeV Ni + , 6 MeV Ta +++ ) irradiations. A model based on total defect build-up, however, is necessary to explain the amorphous transition induced by electron irradiation and can also be applied to heavy ion irradiation. The cascade effects in this latter model are manifested by non-uniform defect distribution in the lattice. The defect build-up model requires a high activation energy for interstitial migration which is not incompatible with recent findings. The form of the temperature dependence can also be rationalized using a defect build-up model (amorphous phase transition, heavy-ion irradiation, electron irradiation, NiTi, defect build-up, cascade overlap). (author)

  14. NiTi-polyimide composites prepared using thermal imidization process

    Czech Academy of Sciences Publication Activity Database

    Vokoun, David; Sysel, P.; Heller, Luděk; Kadeřávek, L.; Svatuška, Michal; Goryczka, T.; Kafka, Vratislav; Šittner, Petr

    2016-01-01

    Roč. 25, č. 5 (2016), 1993-1999 ISSN 1059-9495 R&D Projects: GA ČR GC15-13174J; GA ČR GA14-15264S Institutional support: RVO:68378271 ; RVO:68378297 Keywords : actuator * composite * model * NiTi * polyimide * residual * stress Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.331, year: 2016

  15. Development of microactuators from shape memory alloys

    International Nuclear Information System (INIS)

    Kohl, M.

    2002-04-01

    Shape memory alloys (SMAs) have the fascinating property of shape recovery, which is associated with the generation of high energy densities. Nowadays, they are already used in several very successful applications. Within the last 10 years, SMA devices have entered also the field of microsystems technology. The present report gives an overview on the current state-of-the-art. For the examples of SMA microvalves and SMA linear actuators, the microactuator development is described from the idea to the prototype in comprehensive breadth. The breadth of research and development activities on SMA microactuators presently ranges from pure scientific topics of materials research to technological problems, e.g. of micromachining, integration and contacting. Further key aspects of development are three-dimensional models for the handling of complex SMA actuator geometries and coupled simulation routines in order to take multifunctional properties into account. For actuator design, mechanical and thermal optimization criteria are introduced, whose systematic implementation allows an optimum use of the shape memory effect. Some of the presented prototypes are already competitive components. One example are normally-open SMA microvalves driven by SMA foil actuators of 20 μm thickness, which are counted among the smallest microvalves and which still are able to control pressures and flows comparable to other valve concepts. Due to their modular design they can be combined with other microfluidic components in a flexible way for realization of fluidic microsystems. Another example are SMA microgrippers, a further development of SMA linear actuators, which presently outperform other microgrippers of comparable size with respect to gripping force and stroke. (orig.)

  16. Welding shape memory alloys with NdYAG lasers Soldadura de ligas de memória de forma com laser Nd-YAG

    Directory of Open Access Journals (Sweden)

    Luisa Quintino

    2012-09-01

    Full Text Available The demand of emerging joining techniques for shape memory alloys (SMA has become of great importance, as their functional properties namely shape memory effect (SME and superelasticity (SE present unique solutions for state-of-the-art applications. Welding of SMAs is a challenge due to the risk of reduced mechanical performance after laser processing. The wider application of these alloys in various sectors as aerospace, medical or electronic industry is hindered by the limitations in its processing. The need to weld SMAs to other materials is pressing for applications in the above referred sectors. In dissimilar joints the need to understand materials behavior is even more challenging since base materials have different physical properties leading to different heat flow, convection processes and residual stress distribution. The chemical composition across the weld pool varies and intermetallic compounds are formed. Research detailing the effects of laser processing on NiTi is essential to overcome many of these challenges. The objectives of the current study are to analyze the effects of laser welding in the weld shape of both similar and dissimilar joints of NiTi to stainless steel and titanium alloys.A procura de técnicas de ligação para ligas de memória de forma tem-se revetido de importância crescente, devido ao desenvolvimento de aplicações deste material com particulares propriedades de memória de forma e superelasticidade. A soldadura de ligas de memória de forma é um desafio devido ao risco de emporbrecimento das propriedades mecânicas depois do processamento laser. A aplicação alargarda destas ligas em vários sectores como o aeroespacial, medico ou electrónico é prejudicado pelas limitações de processamento. A necessidade de soldar ligas de memória de forma a outros materiais é premente para estes sectores. Em juntas dissimilares, o entendimento do comportamento dos materaias é um desafio ainda maior uma vez que

  17. Impaired bacterial attachment to light activated Ni-Ti alloy

    International Nuclear Information System (INIS)

    Chrzanowski, Wojciech; Valappil, Sabeel P.; Dunnill, Charles W.; Abou Neel, Ensanya A.; Lee, Kevin; Parkin, Ivan P.; Wilson, Michael; Armitage, David A.; Knowles, Jonathan C.

    2010-01-01

    Ni-Ti alloy due to its unique mechanical properties, is used for many types of implants. Failure of these implants can be attributed to many different factors; however infections are a common problem. In this paper, the attachment of the bacteria, Staphylococcus aureus, to the Ni-Ti surface modified by a range of processes with and without of light activation (used to elicit antimicrobial properties of materials) was assessed and related to different surface characteristics. Before the light activation the number of bacterial colony forming units was the greatest for the samples thermally oxidised at 600 deg. C. This sample and the spark oxidised samples showed the highest photocatalytic activity but only the thermally oxidised samples at 600 deg. C showed a significant drop of S. aureus attachment. The findings in this study indicate that light activation and treating samples at 600 deg. C is a promising method for Ni-Ti implant applications with inherent antimicrobial properties. Light activation was shown to be an effective way to trigger photocatalytic reactions on samples covered with relatively thick titanium dioxide via accumulation of photons in the surface and a possible increase in defects which may result in free oxygen. Moreover, light activation caused an increase in the total surface energy.

  18. Shape recovery and irrecoverable strain control in polyurethane shape-memory polymer

    International Nuclear Information System (INIS)

    Tobushi, Hisaaki; Ejiri, Yoshihiro; Hayashi, Syunichi; Hoshio, Kazumasa

    2008-01-01

    In shape-memory polymers, large strain can be fixed at a low temperature and thereafter recovered at a high temperature. If the shape-memory polymer is held at a high temperature for a long time, the irrecoverable strain can attain a new intermediate shape between the shape under the maximum stress and the primary shape. Irrecoverable strain control can be applied to the fabrication of a shape-memory polymer element with a complex shape in a simple method. In the present study, the influence of the strain-holding conditions on the shape recovery and the irrecoverable strain control in polyurethane shape-memory polymer is investigated by tension test of a film and three-point bending test of a sheet. The higher the shape-holding temperature and the longer the shape-holding time, the higher the irrecoverable strain rate. The equation that expresses the characteristics of the irrecoverable strain control is formulated

  19. Thin film shape memory alloys for optical sensing applications

    International Nuclear Information System (INIS)

    Fu, Y Q; Luo, J K; Huang, W M; Flewitt, A J; Milne, W I

    2007-01-01

    Based on shape memory effect of the sputtered thin film shape memory alloys, different types of micromirror structures were designed and fabricated for optical sensing application. Using surface micromachining, TiNi membrane mirror structure has been fabricated, which can be actuated based on intrinsic two-way shape memory effect of the free-standing TiNi film. Using bulk micromachining, TiNi/Si and TiNi/Si 3 N 4 microcantilever mirror structures were fabricated

  20. Shape memory effect and super elasticity. Its dental applications.

    Science.gov (United States)

    Kotian, R

    2001-01-01

    The shape memory alloys are quite fascinating materials characterized by a shape memory effect and super elasticity which ordinary metals do not have. This unique behaviour was first found in a Au-47.5 at % Cd alloy in 1951, and was published in 1963 by the discovery of Ti-Ni alloy. Shape memory alloys now being practically used as new functional alloys for various dental and medical applications.

  1. Using Ternary Alloy Additions to Engineer Nitinol Shape Memory Alloys

    Data.gov (United States)

    National Aeronautics and Space Administration — Improving travel capabilities is essential in order to further investigative space exploration. For aerospace applications, weight savings is essential. Shape memory...

  2. Shape Memory Alloy-Based Periodic Cellular Structures, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — This SBIR Phase I effort will develop and demonstrate an innovative shape memory alloy (SMA) periodic cellular structural technology. Periodic cellular structures...

  3. The placement of Y-shaped titanium-nickel memory alloy stent in the carina: a fundamental study in experimental canines

    International Nuclear Information System (INIS)

    Bian Wei; Shen Che

    2010-01-01

    Objective: To investigate the pathological changes of local airway tissue after inserting Yshaped titanium-nickel memory alloy stent in carina, and to evaluate CT three-dimensional reconstruction technique in postoperative and follow-up observation. Methods: Twelve healthy adult canines were enrolled in this study. Based on the information of the carina obtained from CT three-dimensional reconstruction images, the preparation of Y-shape netlike stent was made by knitting method with single Ni-Ti memory alloy wire. The stent was then inserted in canine's carina with the help of a releasing system. After the operation fiberbronchoscopy and CT three-dimensional reconstruction were performed. The animals were sacrificed 12 weeks after the procedure and the bronchus of the stenting segment was removed and sent for histopathologic examination. Results: Technical success was achieved in all canines with the stent right in the carina. The airway remained unobstructed 12 weeks after the procedure. Histopathologic examination revealed that the stent became partial epithelialization. Conclusion: The Y-shaped titanium-nickel memory alloy stent has good histocompatibility and physicochemical stability and no re-stenosis of the airway develops in the follow-up period of three months. The stent-releasing technique is easy and simple. As a non-invasive and convenient exam, CT three-dimensional reconstruction technique is of great value in postoperative follow-up observation. (authors)

  4. Rotor Embedded with Shape Memory Alloy Wires

    Directory of Open Access Journals (Sweden)

    K. Gupta

    2000-01-01

    Full Text Available In the present analysis, the fundamental natural frequency of a Jeffcott and a two-mass rotor with fibre reinforced composite shaft embedded with shape memory alloy (SMA wires is evaluated by Rayleigh's procedure. The flexibility of rotor supports is taken into account. The effect of three factors, either singly or in combination with each other, on rotor critical speed is studied. The three factors are: (i increase in Young's modulus of SMA (NITINOL wires when activated, (ii tension in wires because of phase recovery stresses, and (iii variation of support stiffness by three times because of activation of SMA in rotor supports. It is shown by numerical examples that substantial variation in rotor critical speeds can be achieved by a combination of these factors which can be effectively used to avoid resonance during rotor coast up/down.

  5. Micromechanical modelling of shape memory alloy composites

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Y.F.; Wang, X.M.; Yue, Z.F. [School of Mechanic, Civil Engineering and Architecture, Northwestern Polytechnical University, Xian, 710072 (China)

    2004-03-01

    An isothermal finite element method (FEM) model has been applied to study the behavior of two kinds of shape memory alloy (SMA) composites. For SMA-fiber reinforced normal metal composites, the FEM analysis shows that the mechanical behavior of the composites depends on the SMA volume fraction. For normal metal-fiber reinforced SMA matrix composites, the SMA phase transformation is affected by the increasing Young's modulus of the metal fiber. The phase transformation was also treated using a simple numerical analysis, which assumes that there are uniform stresses and strains distributions in the fiber and the matrix respectively. It is found that there is an obvious difference between the FEM analysis and the simple numerical assessment. Only FEM can provide reasonable predictions of phase transformations in SMA/normal metal composites. (Abstract Copyright [2004], Wiley Periodicals, Inc.)

  6. Shape Memory Effect Actuators from Chlorides, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — Shape Change Technologies is developing a radical new technique for the fabrication of Shape Memory alloys, such as TiNi and its ternary alloys of Hf, Zr, and Cu....

  7. Structural stability of characteristic interface for NiTi/Nb Nanowire: First-Principle study

    Science.gov (United States)

    Li, G. F.; Zheng, H. Z.; Shu, X. Y.; Peng, P.

    2016-01-01

    Compared with some other conventional interface models, the interface of NiTi(211)/Nb(220) in NiTiNb metal nanocomposite had been simulated and analyzed carefully. Results show that only several interface models, i.e., NiTi(100)/Nb(100)(Ni⃡Nb), NiTi(110)/Nb(110) and NiTi(211)/Nb(220), can be formed accordingly with their negative formation enthalpy. Therein the cohesive energy Δ E and Griffith rupture work W of NiTi(211)/Nb(220) interface model are the lowest among them. Density of states shows that there exists only one electronic bonding peak for NiTi(211)/Nb(220) interface model at -2.5 eV. Electron density difference of NiTi(211)/ Nb(220) shows that the Nb-Nb, Nb-Ti and Nb-Ni bonding characters seem like so peaceful as a fabric twisting every atom, which is different from conventional metallic bonding performance. Such appearance can be deduced that the metallic bonding between Nb-Nb, Nb-Ti and Nb-Ni in NiTi(211)/Nb(220) may be affected by its nanostructure called nanometer size effect. Thus, our findings open an avenue for detailed and comprehensive studies of nanocomposite.

  8. AC Electric Field Activated Shape Memory Polymer Composite

    Science.gov (United States)

    Kang, Jin Ho; Siochi, Emilie J.; Penner, Ronald K.; Turner, Travis L.

    2011-01-01

    Shape memory materials have drawn interest for applications like intelligent medical devices, deployable space structures and morphing structures. Compared to other shape memory materials like shape memory alloys (SMAs) or shape memory ceramics (SMCs), shape memory polymers (SMPs) have high elastic deformation that is amenable to tailored of mechanical properties, have lower density, and are easily processed. However, SMPs have low recovery stress and long response times. A new shape memory thermosetting polymer nanocomposite (LaRC-SMPC) was synthesized with conductive fillers to enhance its thermo-mechanical characteristics. A new composition of shape memory thermosetting polymer nanocomposite (LaRC-SMPC) was synthesized with conductive functionalized graphene sheets (FGS) to enhance its thermo-mechanical characteristics. The elastic modulus of LaRC-SMPC is approximately 2.7 GPa at room temperature and 4.3 MPa above its glass transition temperature. Conductive FGSs-doped LaRC-SMPC exhibited higher conductivity compared to pristine LaRC SMP. Applying an electric field at between 0.1 Hz and 1 kHz induced faster heating to activate the LaRC-SMPC s shape memory effect relative to applying DC electric field or AC electric field at frequencies exceeding1 kHz.

  9. Biomedical Applications of Thermally Activated Shape Memory Polymers

    Energy Technology Data Exchange (ETDEWEB)

    Small IV, W; Singhal, P; Wilson, T S; Maitland, D J

    2009-04-10

    Shape memory polymers (SMPs) are smart materials that can remember a primary shape and can return to this primary shape from a deformed secondary shape when given an appropriate stimulus. This property allows them to be delivered in a compact form via minimally invasive surgeries in humans, and deployed to achieve complex final shapes. Here we review the various biomedical applications of SMPs and the challenges they face with respect to actuation and biocompatibility. While shape memory behavior has been demonstrated with heat, light and chemical environment, here we focus our discussion on thermally stimulated SMPs.

  10. Effects of surface finish and mechanical training on Ni-Ti sheets for elastocaloric cooling

    Directory of Open Access Journals (Sweden)

    Kurt Engelbrecht

    2016-06-01

    Full Text Available Elastocaloric cooling has emerged as a promising alternative to vapor compression in recent years. Although the technology has the potential to be more efficient than current technologies, there are many technical challenges that must be overcome to realize devices with high performance and acceptable durability. We study the effects of surface finish and training techniques on dog bone shaped polycrystalline samples of NiTi. The fatigue life of several samples with four different surface finishes was measured and it was shown that a smooth surface, especially at the edges, greatly improved fatigue life. The effects of training both on the structure of the materials and the thermal response to an applied strain was studied. The load profile for the first few cycles was shown to change the thermal response to strain, the structure of the material at failure while the final structure of the material was weakly influenced by the surface finish.

  11. Effect of nano-hydroxyapatite reinforcement in mechanically alloyed NiTi composites for biomedical implant

    International Nuclear Information System (INIS)

    Akmal, Muhammad; Raza, Ahmad; Khan, Muhammad Mudasser; Khan, M. Imran; Hussain, Muhammad Asif

    2016-01-01

    Equi-atomic NiTi alloy composites reinforced with 0, 2, 4 and 6 vol.% nano-hydroxyapatite (HA) were successfully synthesized using pressureless sintering. Pure Ni and Ti elements were ball milled for 10 h in order to produce a mechanically alloyed equi-atomic NiTi alloy (MA-NiTi). Mechanically alloyed NiTi and HA powders were blended, compacted and then sintered for 3 h at 1325 K. The sintered density varied inversely with volume percent of HA reinforcement. The X-Ray diffraction spectra and SEM images showed the formation of multiple phases like NiTi, NiTi 2 , Ni 3 Ti, and Ni 4 Ti 3 . The back scattered-SEM image analysis confirmed the presence of Ni-rich and Ti-rich phases with increasing HA content. The 6 vol.% HA reinforced composite showed Ni 3 Ti as the major phase having the highest hardness value which can be attributed to the presence of relatively harder phases along with higher HA content as a reinforcement. The composite of MA-NiTi with 2 vol.% HA manifested the most desirable results in the form of better sintering density mainly due to the minute decomposition of NiTi into other phases. Therefore, the 2 vol.% reinforced MA-NiTi composite can be exploited as a novel material for manufacturing biomedical implants. - Highlights: • NiTi-HA composites were synthesized using powder metallurgy route. • New phases such as NiTi 2 , Ni 3 Ti and Ni 4 Ti 3 were observed for sintered composites. • Mechanical properties enhanced with the increasing content of HA and new phases. • No martensitic transformation was observed for all composites by DSC analysis. • 2 vol.% HA composite is a novel candidate for biomedical implants.

  12. Effect of nano-hydroxyapatite reinforcement in mechanically alloyed NiTi composites for biomedical implant

    Energy Technology Data Exchange (ETDEWEB)

    Akmal, Muhammad, E-mail: muhammad.akmal@giki.edu.pk [Faculty of Materials and Chemical Engineering, GIK Institute of Engineering Sciences and Technology, Topi 23640 (Pakistan); Raza, Ahmad, E-mail: ahmadrazac@yahoo.com [Faculty of Materials and Chemical Engineering, GIK Institute of Engineering Sciences and Technology, Topi 23640 (Pakistan); Khan, Muhammad Mudasser; Khan, M. Imran [Faculty of Materials and Chemical Engineering, GIK Institute of Engineering Sciences and Technology, Topi 23640 (Pakistan); Hussain, Muhammad Asif [Department of Chemical Engineering, Kangwon National University, Samcheok, 25913 (Korea, Republic of)

    2016-11-01

    Equi-atomic NiTi alloy composites reinforced with 0, 2, 4 and 6 vol.% nano-hydroxyapatite (HA) were successfully synthesized using pressureless sintering. Pure Ni and Ti elements were ball milled for 10 h in order to produce a mechanically alloyed equi-atomic NiTi alloy (MA-NiTi). Mechanically alloyed NiTi and HA powders were blended, compacted and then sintered for 3 h at 1325 K. The sintered density varied inversely with volume percent of HA reinforcement. The X-Ray diffraction spectra and SEM images showed the formation of multiple phases like NiTi, NiTi{sub 2}, Ni{sub 3}Ti, and Ni{sub 4}Ti{sub 3}. The back scattered-SEM image analysis confirmed the presence of Ni-rich and Ti-rich phases with increasing HA content. The 6 vol.% HA reinforced composite showed Ni{sub 3}Ti as the major phase having the highest hardness value which can be attributed to the presence of relatively harder phases along with higher HA content as a reinforcement. The composite of MA-NiTi with 2 vol.% HA manifested the most desirable results in the form of better sintering density mainly due to the minute decomposition of NiTi into other phases. Therefore, the 2 vol.% reinforced MA-NiTi composite can be exploited as a novel material for manufacturing biomedical implants. - Highlights: • NiTi-HA composites were synthesized using powder metallurgy route. • New phases such as NiTi{sub 2}, Ni{sub 3}Ti and Ni{sub 4}Ti{sub 3} were observed for sintered composites. • Mechanical properties enhanced with the increasing content of HA and new phases. • No martensitic transformation was observed for all composites by DSC analysis. • 2 vol.% HA composite is a novel candidate for biomedical implants.

  13. Mechanical and structural properties of sputtered Ni/Ti multilayers

    Energy Technology Data Exchange (ETDEWEB)

    Senthil Kumar, M.; Boeni, P.; Tixier, S.; Clemens, D.; Horisberger, M. [Paul Scherrer Inst. (PSI), Villigen (Switzerland)

    1997-09-01

    Ni/Ti bilayers have been prepared by dc-magnetron sputtering in order to study their mechanical and structural properties. A remarkable reduction of stress is observed when the Ni layers are sputtered reactively in argon with a high partial pressure of air. The high angle x-ray diffraction studies show a tendency towards amorphisation of the Ni layers with increasing air flow. The low angle measurements indicate a substantial reduction of interdiffusion resulting in smoother interfaces with increasing air content. (author) 2 figs., 2 refs.

  14. THE MICROSTRUCTURAL PROPERTIES OF EXPLOSION WELDED Ni/Ti JOINT

    Directory of Open Access Journals (Sweden)

    Kamila Zdrodowska

    2014-06-01

    Full Text Available Explosion welding is one of the ways of bonding materials. This method is used to bond metals which either cannot be joined or they are difficult to bond by other methods. The study investigates the metallographic characteristics of Ni/Ti joints in the form of a plate. Microstructures of the joints are examined and hardness measurements are carried out on the bonded materials and their interfaces. A detailed analysis of the distributions of wave length and width is presented. An average microhardness of the interface is found to be higher than that of the base materials.

  15. Relaxation peak near 200 K in NiTi alloy

    Science.gov (United States)

    Zhu, J. S.; Schaller, R.; Benoit, W.

    1989-10-01

    Internal friction (IF), frequency ( f), electrical resistance ( R) and zero point movement of the torsion pendulum (ɛ) have been measured in near equi-atomic NiTi alloy in order to clarify the mechanism for the relaxation peak near 200 K. The height of the relaxation peak decreases successively with thermal cycling and settles down to a lower stable value in running 15 cycles. However, the electrical resistance of the sample shows a variation in contrast with the internal friction. Both of them will return to the initial state after a single annealing at 773 K for 1 h. The probable mechanism of this relaxation peak was discussed.

  16. Release of metal ions from round and rectangular NiTi wires

    Directory of Open Access Journals (Sweden)

    Arash Azizi

    2016-04-01

    Full Text Available Abstract Background The aim of this study was to evaluate the amount of nickel and titanium ions released from two wires with different shapes and a similar surface area. Methods Forty round nickel-titanium (NiTi arch wires with the diameter of 0.020 in. and 40 rectangular NiTi arch wires with the diameter of 0.016 × 0.016 in. were immersed in artificial saliva during a 21-day period. The surface area of both wires was 0.44 in.2. Wires were separately dipped into polypropylene tubes containing 50 ml of buffer solution and were incubated and maintained at 37 °C. Inductively coupled plasma atomic emission spectrometry (ICP-AES was used to measure the amount of ions released after exposure lengths of 1 h, 24 h, 1 week, and 3 weeks. Repeated measures ANOVA and Tukey tests were used to evaluate the data. Results The results indicated that the amount of nickel and titanium concentrations was significantly higher in the rectangular wire group. The most significant release of all metals was measured after the first hour of immersion. In the rectangular wire group, 243 ± 4.2 ng/ml of nickel was released after 1 h, while 221.4 ± 1.7 ng/ml of nickel was released in the round wire group. Similarly, 243.3 ± 2.8 ng/ml of titanium was released in the rectangular wire group and a significantly lower amount of 211.9 ± 2.3 ng/ml of titanium was released in the round wire group. Conclusions Release of metal ions was influenced by the shape of the wire and increase of time.

  17. Thermomechanical fatigue of shape memory alloys

    International Nuclear Information System (INIS)

    Lagoudas, D C; Kumar, P K; Miller, D A; Rong, L

    2009-01-01

    As shape memory alloys (SMAs) gain popularity as high energy density actuators, one characteristic that becomes particularly important is the thermomechanical transformation fatigue life, in addition to maximum transformation strain and stability of actuation cycles. In this paper, a novel test frame design and testing protocol are discussed, for investigating the thermally activated transformation fatigue characteristics of SMAs under various applied loads for both complete and partial phase transformation. A Ni 50 Ti 40 Cu 10 (at.%) SMA was chosen for this investigation and the effects of various heat treatments on the transformation temperatures and the transformation fatigue lives of actuators were studied. For selected heat treatments, the evolution of recoverable and irrecoverable strains up to failure under different applied stress levels was studied in detail. The influence of complete and partial transformation on the fatigue life is also presented. The irrecoverable strain accumulation as a function of the number of cycles to failure for different stress levels is presented by a relationship similar to the Manson–Coffin law for both partial and complete transformations

  18. Microplane modelling of shape memory alloys

    International Nuclear Information System (INIS)

    Kadkhodaei, M; Salimi, M; Rajapakse, R K N D; Mahzoon, M

    2007-01-01

    A three-dimensional (3D) constitutive model based on a statically constrained microplane theory with volumetric-deviatoric split is proposed for polycrystalline shape memory alloys (SMAs) under multiaxial loading paths. Microplane governing equations are 1D stress-strain relations for normal and shear stresses on each microplane, in which suitable relationships between the microscopic and macroscopic quantities are considered so that switching between elastic and inelastic local responses automatically occurs according to the macroscopic response of SMA without additional constraint. Shear stress on each microplane is expressed by the resultant shear component within the plane to overcome directional bias and to prevent the appearance of shear strain in a pure axial loading or axial strain in a pure shear loading while microplane formulations based on two shear directions may predict such impractical results. The behaviour of SMA under simple and complicated loadings has been studied. In nonproportional loading paths, the model shows interaction between stress components, as well as deviation from normality. Predicted results from the model are in good agreement with those of the existing theoretical and experimental investigations

  19. High-Temperature Shape Memory Alloys

    Science.gov (United States)

    Biffi, C. A.; Tuissi, A.

    2014-10-01

    In this paper, an experimental study of laser micro-processing on a Cu-Zr-based shape memory alloy (SMA), which is suitable for high-temperature (HT) applications, is discussed. A first evaluation of the interaction between a laser beam and Zr50Cu28Ni7Co15 HT SMA is highlighted. Single laser pulses at various levels of power and pulse duration were applied to evaluate their effect on the sample surfaces. Blind and through microholes were produced with sizes on the order of a few hundreds of microns; the results were characterized from the morphological viewpoint using a scanning electron microscope. The high beam quality allows the holes to be created with good circularity and little melted material around the hole periphery. An analysis of the chemical composition was performed using energy dispersive spectroscopy, revealing that compositional changes were limited, while important oxidation occurred on the hole surfaces. Additionally, laser micro-cutting tests were also proposed to evaluate the cut edge morphology and dimensions. The main result of this paper concerned the good behavior of the material upon interaction with the laser beam, which suggests that microfeatures can be successfully produced in this alloy.

  20. Isothermal sections of the Co-Ni-Ti system at 950 and 1 000 C

    Energy Technology Data Exchange (ETDEWEB)

    Li, Han; Jin, Zhanpeng [Central South Univ., Changsha (China). School of Materials Science and Engineering; Zhou, Peng [Hunan Univ. of Science and Technology, Xiangtan (China). Hunan Provincial Key Defense Lab. of High Temperature Wear Resisting Materials and Preparation Technology; Du, Yong [Central South Univ., Changsha (China). State Key Lab. of Powder Metallurgy

    2018-02-15

    The isothermal sections of the Co-Ni-Ti system at 950 and 1000 C were investigated experimentally. Diffusion couples were measured by electron probe microanalysis to construct the phase relations at 950 C, whereas eleven key alloys annealed at 1000 C were investigated using X-ray diffraction and electron probe microanalysis. The ternary phase, τ-(Co,Ni){sub 3}Ti (hP24-VCo{sub 3}), was observed at both temperatures. At 950 C, continuous solid solutions are formed between CoTi{sub 2} and NiTi{sub 2} as well as between CoTi and NiTi. Eight 3-phase regions, i. e. Ni{sub 3}Ti + (Co,Ni)Ti + τ, Ni{sub 3}Ti + γ-(Co,Ni) + τ, τ + c-Co{sub 2}Ti + (Co,Ni)Ti, τ + c-Co{sub 2}Ti + Co{sub 3}Ti, τ + Co{sub 3}Ti + γ-(Co,Ni), c-Co{sub 2}Ti + h-Co{sub 2}Ti + Co{sub 3}Ti, L + β-(Ti) + (Co,Ni)Ti{sub 2} and L + (Co,Ni)Ti{sub 2} + (Co,Ni)Ti, were constructed at 1000 C. Considerable ternary solubilities in Ni{sub 3}Ti, Co{sub 3}Ti and c-Co{sub 2}Ti were determined.

  1. 3D flexible NiTi-braided elastomer composites for smart structure applications

    International Nuclear Information System (INIS)

    Heller, L; Vokoun, D; Šittner, P; Finckh, H

    2012-01-01

    While outstanding functional properties of thin NiTi wires are nowadays well recognized and beneficially utilized in medical NiTi devices, development of 2D/3D wire structures made out of these NiTi wires remains challenging and mostly unexplored. The research is driven by the idea of creating novel 2D/3D smart structures which inherit the functional properties of NiTi wires and actively utilize geometrical deformations within the structure to create new/improved functional properties. Generally, textile technology provides attractive processing methods for manufacturing 2D/3D smart structures made out of NiTi wires. Such structures may be beneficially combined with soft elastomers to create smart deformable composites. Following this route, we carried out experimental work focused on development of 3D flexible NiTi-braided elastomer composites involving their design, laboratory manufacture and thermomechanical testing. We describe the manufacturing technology and structural properties of these composites; and perform thermomechanical tests on the composites, focusing particularly on quasistatic tensile properties, energy absorption, damping and actuation under tensile loading. Functional thermomechanical properties of the composites are discussed with regard to the mechanical properties of the components and architecture of the composites. It is found that the composites indeed inherit all important features of the thermomechanical behavior of NiTi wires but, due to their internal architecture, outperform single NiTi wires in some features such as the magnitude of recoverable strain, superelastic damping capacity and thermally induced actuation strain. (paper)

  2. Mechanical properties of NiTi and CuNiTi wires used in orthodontic treatment. Part 2: Microscopic surface appraisal and metallurgical characteristics

    Directory of Open Access Journals (Sweden)

    Marco Abdo Gravina

    2014-01-01

    Full Text Available OBJECTIVE: This research aimed at comparing the qualitative chemical compositions and the surface morphology of fracture regions of eight types of Nickel (Ni Titanium (Ti conventional wires, superelastic and heat-activated (GAC, TP, Ormco, Masel, Morelli and Unitek, to the wires with addition of copper (CuNiTi 27oC and 35oC, Ormco after traction test. METHODS: The analyses were performed in a scanning electronic microscope (JEOL, model JSM-5800 LV with EDS system of microanalysis (energy dispersive spectroscopy. RESULTS : The results showed that NiTi wires presented Ni and Ti as the main elements of the alloy with minimum differences in their composition. The CuNiTi wires, however, presented Ni and Ti with a significant percentage of copper (Cu. As for surface morphology, the wires that presented the lowest wire-surface roughness were the superelastic ones by Masel and Morelli, while those that presented the greatest wire-surface roughness were the CuNiTi 27oC and 35oC ones by Ormco, due to presence of microcavity formed as a result of pulling out some particles, possibly of NiTi. 4 The fracture surfaces presented characteristics of ductile fracture, with presence of microcavities. The superelastic wires by GAC and the CuNiTi 27oC and the heat-activated ones by Unitek presented the smallest microcavities and the lowest wire-surface roughness with regard to fracture, while the CuNiTi 35oC wires presented inadequate wire-surface roughness in the fracture region. CONCLUSION: CuNiTi 35oC wires did not present better morphologic characteristics in comparison to the other wires with regard to surfaces and fracture region.

  3. A Preisach type model for temperature driven hysteresis memory erasure in shape memory materials

    OpenAIRE

    Kopfová, J.; Krejčí, P. (Pavel)

    2011-01-01

    We establish the well-posedness and thermodynamic consistency of a variational inequality modeling temperature-induced memory erasure in shape memory materials. It is shown that the input-output operator is continuous with respect to uniform convergence.

  4. High-strength shape memory steels alloyed with nitrogen

    International Nuclear Information System (INIS)

    Ullakko, K.; Jakovenko, P.T.; Gavriljuk, V.G.

    1996-01-01

    Since shape memory effect in Fe-Mn-Si systems was observed, increasing attention has been paid to iron based shape memory alloys due to their great technological potential. Properties of Fe-Mn-Si shape memory alloys have been improved by alloying with Cr, Ni, Co and C. A significant improvement on shape memory, mechanical and corrosion properties is attained by introducing nitrogen in Fe-Mn-Si based systems. By increasing the nitrogen content, strength of the matrix increases and the stacking fault energy decreases, which promote the formation of stress induced martensite and decrease permanent slip. The present authors have shown that nitrogen alloyed shape memory steels exhibit recoverable strains of 2.5--4.2% and recovery stresses of 330 MPa. In some cases, stresses over 700 MPa were attained at room temperature after cooling a constrained sample. Yield strengths of these steels can be as high as 1,100 MPa and tensile strengths over 1,500 MPa with elongations of 30%. In the present study, effect of nitrogen alloying on shape memory and mechanical properties of Fe-Mn-Si, Fe-Mn-Si-Cr-Ni and Fe-Mn-Cr-Ni-V alloys is studied. Nitrogen alloying is shown to exhibit a beneficial effect on shape memory properties and strength of these steels

  5. Effect of load deflection on corrosion behavior of NiTi wire.

    Science.gov (United States)

    Liu, I H; Lee, T M; Chang, C Y; Liu, C K

    2007-06-01

    For dental orthodontic applications, NiTi wires are used under bending conditions in the oral environment for a long period. The purpose of this study was to investigate the effect of bending stress on the corrosion of NiTi wires using potentiodynamic and potentiostatic tests in artificial saliva. The results indicated that bending stress induces a higher corrosion rate of NiTi wires in passive regions. It is suggested that the passive oxide film of specimens would be damaged under bending conditions. Auger electron spectroscopic analysis showed a lower thickness of passive films on stressed NiTi wires compared with unstressed specimens in the passive region. By scanning electron microscopy, localized corrosion was observed on stressed Sentalloy specimens after a potentiodynamic test at pH 2. In conclusion, this study indicated that bending stress changed the corrosion properties and surface characteristics of NiTi wires in a simulated intra-oral environment.

  6. Memory for shape reactivates the lateral occipital complex.

    Science.gov (United States)

    Karanian, Jessica M; Slotnick, Scott D

    2015-04-07

    Memory is thought to be a constructive process in which the cortical regions associated with processing event features are reactivated during retrieval. Although there is evidence for non-detailed cortical reactivation during retrieval (e.g., memory for visual or auditory information reactivates the visual or auditory processing regions, respectively), there is limited evidence that memory can reactivate cortical regions associated with processing detailed, feature-specific information. Such evidence is critical to our understanding of the mechanisms of episodic retrieval. The present functional magnetic resonance imaging (fMRI) study assessed whether the lateral occipital complex (LOC), a region that preferentially processes shape, is associated with retrieval of shape information. During encoding, participants were presented with colored abstract shapes that were either intact or scrambled. During retrieval, colored disks were presented and participants indicated whether the corresponding shape was previously "intact" or "scrambled". To assess whether conscious retrieval of intact shapes reactivated LOC, we conducted a conjunction of shape perception/encoding and accurate versus inaccurate retrieval of intact shapes, which produced many activations in LOC. To determine whether activity in LOC was specific to intact shapes, we conducted a conjunction of shape perception/encoding and intact versus scrambled shapes, which also produced many activations in LOC. Furthermore, memory for intact shapes in each hemifield produced contralateral activity in LOC (e.g., memory for left visual field intact shapes activated right LOC), which reflects the specific reinstatement of perception/encoding activity. The present results extend previous feature-specific memory reactivation evidence and support the view that memory is a constructive process. Copyright © 2015 Elsevier B.V. All rights reserved.

  7. Recent Progress on Modeling Slip Deformation in Shape Memory Alloys

    Science.gov (United States)

    Sehitoglu, H.; Alkan, S.

    2018-03-01

    This paper presents an overview of slip deformation in shape memory alloys. The performance of shape memory alloys depends on their slip resistance often quantified through the Critical Resolved Shear Stress (CRSS) or the flow stress. We highlight previous studies that identify the active slip systems and then proceed to show how non- Schmid effects can be dominant in shape memory slip behavior. The work is mostly derived from our recent studies while we highlight key earlier works on slip deformation. We finally discuss the implications of understanding the role of slip on curtailing the transformation strains and also the temperature range over which superelasticity prevails.

  8. Recent Progress on Modeling Slip Deformation in Shape Memory Alloys

    Science.gov (United States)

    Sehitoglu, H.; Alkan, S.

    2018-03-01

    This paper presents an overview of slip deformation in shape memory alloys. The performance of shape memory alloys depends on their slip resistance often quantified through the Critical Resolved Shear Stress (CRSS) or the flow stress. We highlight previous studies that identify the active slip systems and then proceed to show how non-Schmid effects can be dominant in shape memory slip behavior. The work is mostly derived from our recent studies while we highlight key earlier works on slip deformation. We finally discuss the implications of understanding the role of slip on curtailing the transformation strains and also the temperature range over which superelasticity prevails.

  9. A preliminary study of cladding steel with NiTi by microwave-assisted brazing

    International Nuclear Information System (INIS)

    Chiu, K.Y.; Cheng, F.T.; Man, H.C.

    2005-01-01

    Nickel titanium (NiTi) plate of 1.2 mm thickness was successfully clad on AISI 316L stainless steel substrate by a microwave-assisted brazing process. Brazing was conducted in a multimode microwave oven in air using a copper-based brazing material in tape form. The brazing material was melted in a few minutes by microwave-induced plasma initiated by conducting wires surrounding the brazing assembly. Metallographic study by scanning-electron microscopy (SEM) and compositional analysis by energy-dispersive spectroscopy (EDS) of the brazed joint revealed metallurgical bonding formed via inter-diffusion between the brazing filler and the adjacent materials. A shear bonding strength in the range of 100-150 MPa was recorded in shear tests of the brazed joint. SEM and X-ray diffractometry (XRD) analysis for the surface of as-received NiTi plate and NiTi cladding showed similar microstructure and phase composition. Nanoindentation tests also indicated that the superelastic properties of NiTi were essentially retained. The cavitation erosion resistance of the NiTi cladding was essentially the same as that of as-received NiTi plate, and higher than that obtained in laser or TIG (tungsten-inert gas) surfacing. The high resistance could be attributed to avoidance of dilution and defect formation in the NiTi clad since the cladding did not undergo melting and solidification in the brazing process. Electrochemical tests also recorded similar corrosion resistance in both as-received NiTi and NiTi cladding. Thus, the present study indicates that microwave-assisted brazing is a simple, economical, and feasible process for cladding NiTi on 316L stainless steel for enhancing cavitation erosion resistance

  10. 3D Printed Photoresponsive Devices Based on Shape Memory Composites.

    Science.gov (United States)

    Yang, Hui; Leow, Wan Ru; Wang, Ting; Wang, Juan; Yu, Jiancan; He, Ke; Qi, Dianpeng; Wan, Changjin; Chen, Xiaodong

    2017-09-01

    Compared with traditional stimuli-responsive devices with simple planar or tubular geometries, 3D printed stimuli-responsive devices not only intimately meet the requirement of complicated shapes at macrolevel but also satisfy various conformation changes triggered by external stimuli at the microscopic scale. However, their development is limited by the lack of 3D printing functional materials. This paper demonstrates the 3D printing of photoresponsive shape memory devices through combining fused deposition modeling printing technology and photoresponsive shape memory composites based on shape memory polymers and carbon black with high photothermal conversion efficiency. External illumination triggers the shape recovery of 3D printed devices from the temporary shape to the original shape. The effect of materials thickness and light density on the shape memory behavior of 3D printed devices is quantified and calculated. Remarkably, sunlight also triggers the shape memory behavior of these 3D printed devices. This facile printing strategy would provide tremendous opportunities for the design and fabrication of biomimetic smart devices and soft robotics. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  11. The quintuple-shape memory effect in electrospun nanofiber membranes

    Science.gov (United States)

    Zhang, Fenghua; Zhang, Zhichun; Liu, Yanju; Lu, Haibao; Leng, Jinsong

    2013-08-01

    Shape memory fibrous membranes (SMFMs) are an emerging class of active polymers, which are capable of switching from a temporary shape to their permanent shape upon appropriate stimulation. Quintuple-shape memory membranes based on the thermoplastic polymer Nafion, with a stable fibrous structure, are achieved via electrospinning technology, and possess a broad transition temperature. The recovery of multiple temporary shapes of electrospun membranes can be triggered by heat in a single triple-, quadruple-, quintuple-shape memory cycle, respectively. The fiber morphology and nanometer size provide unprecedented design flexibility for the adjustable morphing effect. SMFMs enable complex deformations at need, having a wide potential application field including smart textiles, artificial intelligence robots, bio-medical engineering, aerospace technologies, etc in the future.

  12. The quintuple-shape memory effect in electrospun nanofiber membranes

    International Nuclear Information System (INIS)

    Zhang, Fenghua; Zhang, Zhichun; Lu, Haibao; Leng, Jinsong; Liu, Yanju

    2013-01-01

    Shape memory fibrous membranes (SMFMs) are an emerging class of active polymers, which are capable of switching from a temporary shape to their permanent shape upon appropriate stimulation. Quintuple-shape memory membranes based on the thermoplastic polymer Nafion, with a stable fibrous structure, are achieved via electrospinning technology, and possess a broad transition temperature. The recovery of multiple temporary shapes of electrospun membranes can be triggered by heat in a single triple-, quadruple-, quintuple-shape memory cycle, respectively. The fiber morphology and nanometer size provide unprecedented design flexibility for the adjustable morphing effect. SMFMs enable complex deformations at need, having a wide potential application field including smart textiles, artificial intelligence robots, bio-medical engineering, aerospace technologies, etc in the future. (paper)

  13. Tensile strain induced narrowed bandgap of TiO{sub 2} films: Utilizing the two-way shape memory effect of TiNiNb substrate and in-situ mechanical bending

    Energy Technology Data Exchange (ETDEWEB)

    Du, Minshu, E-mail: dms1223@126.com [Department of Materials Science and Engineering, China University of Petroleum at Beijing, Beijing, 102249 (China); Center for Electrochemistry, Department of Chemistry, The University of Texas at Austin, Austin, Texas, 78712 (United States); Cui, Lishan; Wan, Qiong [Department of Materials Science and Engineering, China University of Petroleum at Beijing, Beijing, 102249 (China)

    2016-05-15

    Graphical abstract: - Highlights: • Imposed tensile strain to anatase TiO{sub 2} nanofilm by using the two-way shape memory effect of NiTiNb substrate. • Imposed tensile strain to rutile TiO{sub 2} thin film by in-situ mechanical bending. • Tauc plot based on the PEC-tested auction spectrum was utilized to precisely determine the bandgap of TiO{sub 2}. • Tensile strain narrowed the bandgap of anatase TiO{sub 2} by 60 meV and rutile TiO{sub 2} by 70 meV. • Tensile strain contributes to a 1.5 times larger photocurrent for the water oxidation reaction. - Abstract: Elastic strain is one of the methods to alter the band gap of semiconductors. However, relevant experimental work is limited due to the difficulty in imposing strain. Two new methods for imposing tensile strain to TiO{sub 2} film were introduced here. One is by utilizing the two-way shape memory effect of NiTiNb substrate, and the other method is in-situ mechanical bending. The former method succeeded in imposing 0.4% tensile strain to anatase TiO{sub 2} nanofilm, and strain narrowed the bandgap of TiO{sub 2} by 60 meV. The latter method enabled rutile TiO{sub 2} thin film under the 0.5% biaxially tensile-strained state, which contributes to a narrowed bandgap with ΔE{sub g} of 70 meV. Also, photocurrents of both strained TiO{sub 2} films increased by 1.5 times compared to the strain-free films, which indirectly verified the previous DFT prediction proposed by Thulin and Guerra in 2008 that tensile strain could improve the mobility and separation of photo-excite carriers.

  14. Synchrotron high energy X-ray diffraction study of microstructure evolution of severely cold drawn NiTi wire during annealing

    International Nuclear Information System (INIS)

    Yu, Cun; Aoun, Bachir; Cui, Lishan; Liu, Yinong; Yang, Hong; Jiang, Xiaohua; Cai, Song; Jiang, Daqiang; Liu, Zunping; Brown, Dennis E.; Ren, Yang

    2016-01-01

    Microstructure evolution of a cold-drawn NiTi shape memory alloy wire was investigated by means of in-situ synchrotron high-energy X-ray diffraction during continuous heating. The cold-drawn wire contained amorphous regions and nano-crystalline domains in its microstructure. Pair distribution function analysis revealed that the amorphous regions underwent structural relaxation via atomic rearrangement when heated above 100 °C. The nano-crystalline domains were found to exhibit a strong cold work induced lattice strain anisotropy along 〈111〉, which coincides with the crystallographic fiber orientation of the domains along the wire axial direction. The lattice strain anisotropy systematically decreased upon heating above 200 °C, implying a structural recovery. Crystallization of the amorphous phase led to a broadening of the angular distribution of 〈111〉 preferential orientations of grains along the axial direction as relative to the original 〈111〉 axial fiber texture of the nanocrystalline domains produced by the severe cold wire drawing deformation.

  15. Magnetic Shape Memory Alloy Actuator for Instrument Applications

    Data.gov (United States)

    National Aeronautics and Space Administration — This project will develop a simple actuator based on magnetic shape memory alloy (MSMA), a novel new family of crystalline materials which exhibit strain deformation...

  16. Shape Memory Alloy-Based Periodic Cellular Structures, Phase II

    Data.gov (United States)

    National Aeronautics and Space Administration — This SBIR Phase II effort will continue to develop and demonstrate an innovative shape memory alloy (SMA) periodic cellular structural technology. Periodic cellular...

  17. Using Shape Memory Alloys: A Dynamic Data Driven Approach

    KAUST Repository

    Douglas, Craig C.; Calo, Victor M.; Cerwinsky, Derrick; Deng, Li; Efendiev, Yalchin R.

    2013-01-01

    Shape Memory Alloys (SMAs) are capable of changing their crystallographic structure due to changes of either stress or temperature. SMAs are used in a number of aerospace devices and are required in some devices in exotic environments. We

  18. Development of Morphing Structures for Aircraft Using Shape Memory Polymers

    National Research Council Canada - National Science Library

    Khan, Fazeel J

    2008-01-01

    ...), aerospace structures. In particular, shape memory polymers (SMP) in filled and unfilled form have been investigated with particular emphasis on the recovery time and force as the materials undergo transformation...

  19. Bifurcations and Crises in a Shape Memory Oscillator

    Directory of Open Access Journals (Sweden)

    Luciano G. Machado

    2004-01-01

    Full Text Available The remarkable properties of shape memory alloys have been motivating the interest in applications in different areas varying from biomedical to aerospace hardware. The dynamical response of systems composed by shape memory actuators presents nonlinear characteristics and a very rich behavior, showing periodic, quasi-periodic and chaotic responses. This contribution analyses some aspects related to bifurcation phenomenon in a shape memory oscillator where the restitution force is described by a polynomial constitutive model. The term bifurcation is used to describe qualitative changes that occur in the orbit structure of a system, as a consequence of parameter changes, being related to chaos. Numerical simulations show that the response of the shape memory oscillator presents period doubling cascades, direct and reverse, and crises.

  20. Simulation of Dislocation and Transformation Plasticity in Shape Memory Alloys

    National Research Council Canada - National Science Library

    Volkov, Alexander

    1999-01-01

    A model of deformation of shape memory alloys has been developed. It takes into account deformation due to the phase transformation and plastic deformation, produced by an external stress or by inter-phase stresses...

  1. High actuation properties of shape memory polymer composite actuator

    International Nuclear Information System (INIS)

    Basit, A; L’Hostis, G; Durand, B

    2013-01-01

    The shape memory polymers (SMPs) possess two shapes: permanent shape and temporary shape. This property leads to replacement of shape memory alloys by SMPs in various applications. In this work, two properties, namely structure activeness and the shape memory property of ‘controlled behavior composite material (CBCM)’ plate and its comparison with the conventional symmetrical composite plate (SYM), are studied. The SMPC plates (CBCM and SYM) are manufactured using epoxy resin with a thermal glass transition temperature (T g ) of 130 °C. The shape memory properties of these composites are investigated (under three-point bending test) and compared by deforming them to the same displacement. Three types of recoveries are conducted: unconstrained recovery, constrained recovery, and partial recovery under load. It is found that by coupling the structure activeness (due to its asymmetry) and its shape memory property, higher activated displacement is obtained during the unconstrained recovery. Also, at a lower recovery temperature (90 °C) than the fixing temperature, a recovery close to 100% is obtained for CBCM, whereas for SYM it is only 25%. During constrained recovery, CBCM produces five times larger recovery force than SYM. In addition, higher actuation properties are demonstrated by calculating recovered work and recovery percentages during partial recovery under load. (paper)

  2. Ti-Ni-based shape memory alloys as smart materials

    International Nuclear Information System (INIS)

    Otsuka, K.; Xu, Y.; Ren, X.

    2003-01-01

    Smart materials consist of three principal materials, ferroelectrics, shape memory alloys (SMA) and electro-active polymers (EAP). Among these SMAs, especially Ti-Ni-based alloys are important, since only they can provide large recoverable strains and high recovery stress. In the present paper the unique characteristics of Ti-Ni-based shape memory alloys are reviewed on an up-to-date basis with the aim of their applications to smart materials and structures. (orig.)

  3. Dynamics of Shape Memory Alloy Systems, Phase 2

    Science.gov (United States)

    2015-12-22

    Nonlinear Dynamics and Chaos in Systems with Discontinuous Support Using a Switch Model”, DINAME 2005 - XI International Conference on Dynamic Problems in...AFRL-AFOSR-CL-TR-2016-0003 Dynamics of Shape Memory Alloy Systems , Phase 2 Marcelo Savi FUNDACAO COORDENACAO DE PROJETOS PESQUISAS E EEUDOS TECNOL...release. 2 AFOSR FINAL REPORT Grant Title: Nonlinear Dynamics of Shape Memory Alloy Systems , Phase 2 Grant #: FA9550-11-1-0284 Reporting Period

  4. Laser welding of Ti-Ni type shape memory alloy

    International Nuclear Information System (INIS)

    Hirose, Akio; Araki, Takao; Uchihara, Masato; Honda, Keizoh; Kondoh, Mitsuaki.

    1990-01-01

    The present study was undertaken to apply the laser welding to the joining of a shape memory alloy. Butt welding of a Ti-Ni type shape memory alloy was performed using 10 kW CO 2 laser. The laser welded specimens showed successfully the shape memory effect and super elasticity. These properties were approximately identical with those of the base metal. The change in super elasticity of the welded specimen during tension cycling was investigated. Significant changes in stress-strain curves and residual strain were not observed in the laser welded specimen after the 50-time cyclic test. The weld metal exhibited the celler dendrite. It was revealed by electron diffraction analysis that the phase of the weld metal was the TiNi phase of B2 structure which is the same as the parent phase of base metal and oxide inclusions crystallized at the dendrite boundary. However, oxygen contamination in the weld metal by laser welding did not occur because there was almost no difference in oxygen content between the base metal and the weld metal. The transformation temperatures of the weld metal were almost the same as those of the base metal. From these results, laser welding is applicable to the joining of the Ti-Ni type shape memory alloy. As the application of laser welding to new shape memory devices, the multiplex shape memory device of welded Ti-50.5 at % Ni and Ti-51.0 at % Ni was produced. The device showed two-stage shape memory effects due to the difference in transformation temperature between the two shape memory alloys. (author)

  5. Working memory for braille is shaped by experience.

    Science.gov (United States)

    Cohen, Henri; Scherzer, Peter; Viau, Robert; Voss, Patrice; Lepore, Franco

    2011-03-01

    Tactile working memory was found to be more developed in completely blind (congenital and acquired) than in semi-sighted subjects, indicating that experience plays a crucial role in shaping working memory. A model of working memory, adapted from the classical model proposed by Baddeley and Hitch1 and Baddeley2 is presented where the connection strengths of a highly cross-modal network are altered through experience.

  6. Working memory for braille is shaped by experience

    OpenAIRE

    Cohen, Henri; Scherzer, Peter; Viau, Robert; Voss, Patrice; Lepore, Franco

    2011-01-01

    Tactile working memory was found to be more developed in completely blind (congenital and acquired) than in semi-sighted subjects, indicating that experience plays a crucial role in shaping working memory. A model of working memory, adapted from the classical model proposed by Baddeley and Hitch1 and Baddeley2 is presented where the connection strengths of a highly cross-modal network are altered through experience.

  7. The industrial applications of shape memory alloys in North America

    International Nuclear Information System (INIS)

    Mc Schetky D, L.

    2000-01-01

    Literature in the recent past on shape memory effect alloys dwelt principally on the physical metallurgy, crystallography and kinetics of the shape memory phenomenon. By contrast, we now have books and conference proceedings devoted to the engineering aspects of SMAs, their technology and application. The dominant role SMAs now play in the field of medical and orthodontic devices is well documented and will be reviewed by others in this conference. In this paper we will discuss the commercial applications for shape memory alloy devices in the North American market; applications which are in many cases also produced in European countries and Japan. The early success of shape memory alloy couplings for joining tubing and pipe in the late 1960's was not followed by other large volume applications until the advent of shape memory eyeglass frames, brassiere underwires and cellular phone antennas. Many other applications have now evolved into mature markets and these will be reviewed. In addition to the many commercial applications cited, there are a number of other fields in which shape memory alloys are destined to play a major role; these include smart materials and adaptive structures, MEMS devices, infrastructure systems and electrical power generation and distribution. These applications are being developed with private and government funding and will also be briefly discussed. (orig.)

  8. Application of Shape Memory Alloys in Seismic Isolation: A Review

    Directory of Open Access Journals (Sweden)

    Shaghayegh Alvandi

    2014-12-01

    Full Text Available In the last two decades, there has been an increasing interest in structural engineering control methods. Shape memory alloys and seismic isolation systems are examples of passive control systems that use of any one alone, effectively improve the seismic performance of the structure. Characteristics such as large strain range without any residual deformation, high damping capacity, excellent re-centering, high resistance to fatigue and corrosion and durability have made shape memory alloy an effective damping device or part of base isolators. A unique characteristic of shape memory alloys is in recovering residual deformations even after strong ground excitations. Seismic isolation is a device to lessen earthquake damage prospects. In the latest research studies, shape memory alloy is utilized in combination with seismic isolation system and their results indicate the effectiveness of the application of them to control the response of the structures. This paper reviews the findings of research studies on base isolation system implemented in the building and/or bridge structures by including the unique behavior of shape memory alloys. This study includes the primary information about the characteristic of the isolation system as well as the shape memory material. The efficiency and feasibility of the two mechanisms are also presented by few cases in point.

  9. The industrial applications of shape memory alloys in North America

    Energy Technology Data Exchange (ETDEWEB)

    Mc Schetky D, L. [Memry Corp., Brookfield, CT (United States)

    2000-07-01

    Literature in the recent past on shape memory effect alloys dwelt principally on the physical metallurgy, crystallography and kinetics of the shape memory phenomenon. By contrast, we now have books and conference proceedings devoted to the engineering aspects of SMAs, their technology and application. The dominant role SMAs now play in the field of medical and orthodontic devices is well documented and will be reviewed by others in this conference. In this paper we will discuss the commercial applications for shape memory alloy devices in the North American market; applications which are in many cases also produced in European countries and Japan. The early success of shape memory alloy couplings for joining tubing and pipe in the late 1960's was not followed by other large volume applications until the advent of shape memory eyeglass frames, brassiere underwires and cellular phone antennas. Many other applications have now evolved into mature markets and these will be reviewed. In addition to the many commercial applications cited, there are a number of other fields in which shape memory alloys are destined to play a major role; these include smart materials and adaptive structures, MEMS devices, infrastructure systems and electrical power generation and distribution. These applications are being developed with private and government funding and will also be briefly discussed. (orig.)

  10. Periodic Cellular Structure Technology for Shape Memory Alloys

    Science.gov (United States)

    Chen, Edward Y.

    2015-01-01

    Shape memory alloys are being considered for a wide variety of adaptive components for engine and airframe applications because they can undergo large amounts of strain and then revert to their original shape upon heating or unloading. Transition45 Technologies, Inc., has developed an innovative periodic cellular structure (PCS) technology for shape memory alloys that enables fabrication of complex bulk configurations, such as lattice block structures. These innovative structures are manufactured using an advanced reactive metal casting technology that offers a relatively low cost and established approach for constructing near-net shape aerospace components. Transition45 is continuing to characterize these structures to determine how best to design a PCS to better exploit the use of shape memory alloys in aerospace applications.

  11. Comparative evaluation of apically extruded debris during root canal instrumentation using two Ni-Ti single file rotary systems: An in vitro study.

    Science.gov (United States)

    Singbal, Kiran; Jain, Disha; Raja, Kranthi; Hoe, Tan Ming

    2017-01-01

    Apical extrusion of debris during instrumentation is detrimental to the patient. The aim of this study was to evaluate the apical extrusion of debris during root canal instrumentation using two single file rotary Ni-Ti systems. Thirty freshly extracted mandibular premolars with straight roots were sterilized and divided into two groups instrumented using: One Shape rotary Ni-Ti system with Endoflare orifice shaper (Group 1) and Neo-Niti rotary Ni-Ti system with C1 orifice shaper (Group 2). Preweighed Eppendorf tubes fitted for each tooth before instrumentation. During instrumentation, 1 mL of distilled water with a 30-gauge needle was used to irrigate after every instrument. Tips of the tooth were irrigated with 2 ml distilled water after removal from Eppendorf tubes. The total volume of irrigant in each group was the same 8 ml. All tubes were incubated at 68°C for 15 days and subsequently weighed. The difference between pre- and post-debris weights was calculated, and statistical analysis was performed using independent t -test and level of significance was set at 0.05. The difference between pre- and post-weights was significantly greater for the One Shape system. The Neolix Niti single file was associated with less extrusion compared to One Shape single file system.

  12. Computational design of precipitation-strengthened titanium-nickel-based shape memory alloys

    Science.gov (United States)

    Bender, Matthew D.

    Motivated by performance requirements of future medical stent applications, experimental research addresses the design of novel TiNi-based, superelastic shape-memory alloys employing nanoscale precipitation strengthening to minimize accommodation slip for cyclic stability and to increase output stress capability for smaller devices. Using a thermodynamic database describing the B2 and L21 phases in the Al-Ni-Ti-Zr system, Thermo-Calc software was used to assist modeling the evolution of phase composition during 600°C isothermal evolution of coherent L21 Heusler phase precipitation from supersaturated TiNi-based B2 phase matrix in an alloy experimentally characterized by atomic-scale Local Electrode Atom Probe (LEAP) microanalysis. Based on measured evolution of the alloy hardness (under conditions stable against martensitic transformation) a model for the combined effects of solid solution strengthening and precipitation strengthening was calibrated, and the optimum particle size for efficient strengthening was identified. Thermodynamic modeling of the evolution of measured phase fractions and compositions identified the interfacial capillary energy enabling thermodynamic design of alloy microstructure with the optimal strengthening particle size. Extension of alloy designs to incorporate Pt and Pd for reducing Ni content, enhancing radiopacity, and improving manufacturability were considered using measured Pt and Pd B2/L2 1 partitioning coefficients. After determining that Pt partitioning greatly increases interphase misfit, full attention was devoted to Pd alloy designs. A quantitative approach to radiopacity was employed using mass attenuation as a metric. Radiopacity improvements were also qualitatively observed using x-ray fluoroscopy. Transformation temperatures were experimentally measured as a function of Al and Pd content. Redlich-Kister polynomial modeling was utilized for the dependence of transformation reversion Af temperature on B2 matrix phase

  13. Investigation of oxidation resistance of Ni-Ti film used as oxygen diffusion barrier layer

    International Nuclear Information System (INIS)

    Liu, B.T.; Yan, X.B.; Zhang, X.; Zhou, Y.; Guo, Y.N.; Bian, F.; Zhang, X.Y.

    2009-01-01

    Ni-Ti films prepared at 10 W and 70 W by rf magnetron sputtering are investigated as the oxygen diffusion barrier layer, it is found that crystallinity of Ni-Ti film does not greatly depend on the deposition power. X-ray photoelectron spectroscopy indicates that Ni is still in the form of metallic state from the binding energies of both Ni 2p 3/2 and Ni 2p 1/2 spectra for the sample with 10 W prepared Ni-Ti, however, Ni is oxidized for 70 W prepared Ni-Ti film. Moreover, the (La 0.5 Sr 0.5 )CoO 3 /Pb(Zr 0.40 Ti 0.60 )O 3 /(La 0.5 Sr 0.5 )CoO 3 capacitor grown on high power prepared Ni-Ti film is leaky, however, the capacitor on low power prepared Ni-Ti film possesses very promising physical properties (i.e. remnant polarization of ∼27 μC/cm 2 at 5 V and maximum dielectric constant of 940). Leakage current density of the capacitor grown on low power prepared Ni-Ti film is further investigated, it meets ohmic behavior ( 1.0 V).

  14. Evolution of microstructure and property of NiTi alloy induced by cold rolling

    International Nuclear Information System (INIS)

    Li, Y.; Li, J.Y.; Liu, M.; Ren, Y.Y.; Chen, F.; Yao, G.C.; Mei, Q.S.

    2015-01-01

    We investigated the combination effect of plastic deformation and phase transformation on the evolution of microstructure and property of NiTi alloy. Samples of Ni 50.9 Ti 49.1 alloy were deformed by cold rolling to different strains/thickness reductions (4%–56%). X-ray diffraction, transmission electronic microscopy (TEM) and microhardness measurements were applied for characterization of the microstructure and property of the cold-rolled samples. Experimental results indicated the non-monotonic variations of microstructure parameters and mechanical property with strain, indicating the different processes in microstructure and property evolution of NiTi subjected to cold rolling. TEM observations further showed the dominating mechanisms of microstructure evolution at different strain levels, leading to the gradual reduction of grain size of NiTi to the nanoscale by cold rolling. The results were discussed and related to deformation of martensite, forward and reverse martensitic transformations and dynamic recrystallization. The present study provided experimental evidences for the enhanced formation of nanograins in NiTi by plastic deformation coupled with phase transformation. - Highlights: • Cold rolling of NiTi to thickness reductions from 4% to 56%. • Fluctuation behaviors in microstructure and property evolutions of NiTi. • Deformation coupled with phase transformation enhanced nanocrystallization of NiTi.

  15. Angular distributions of sputtered particles from NiTi alloy

    International Nuclear Information System (INIS)

    Neshev, I.; Hamishkeev, V.; Chernysh, V.S.; Postnikov, S.; Mamaev, B.

    1993-01-01

    The angular distributions of sputtered Ni and Ti from a polycrystalline NiTi (50-50%) alloy are investigated by Auger electron spectroscopy and Rutherford backscattering spectroscopy. A difference in the angular distributions is observed with Ni being sputtered preferentially near the surface normal. A computer program for the calculation of the angular distributions of constituents sputtered from binary targets is created and used. The mechanisms responsible for the observed differences in the angular distributions are discussed. It is found that the collisional cascade theory is not directly applicable to the results of the constituents' angular distributions obtained in the presence of oxygen. The fitted coefficients of bombardment-induced segregation are found to be greater than the experimentally obtained ones. (author)

  16. Laser cladding of austenitic stainless steel using NiTi strips for resisting cavitation erosion

    International Nuclear Information System (INIS)

    Chiu, K.Y.; Cheng, F.T.; Man, H.C.

    2005-01-01

    Being part of a larger project on using different forms of nickel titanium (NiTi) in the surface modification of stainless steel for enhancing cavitation erosion resistance, the present study employs NiTi strips as the cladding material. Our previous study shows that laser surfacing using NiTi powder can significantly increase the cavitation erosion resistance of AISI 316 L stainless steel [K.Y. Chiu, F.T. Cheng, H.C. Man, Mater. Sci. Eng. A 392 (2005) 348-358]. However, from an engineering point of view, NiTi strips are more attractive than powder because NiTi powder is very expensive due to high production cost. In the present study, NiTi strips were preplaced on AISI 316 L samples and remelted using a high-power CW Nd:YAG laser to form a clad layer. To lower the dilution due to the substrate material, samples doubly clad with NiTi were prepared. The volume dilution ratio in the singly clad sample was high, being in the range of 13-30% depending on the processing parameters, while that of the doubly clad sample was reduced to below 10%. Analysis by scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS) and X-ray diffractometry (XRD) reveals that the clad layer is composed of a NiTi B2 based matrix together with fine precipitates of a tetragonal structure. Vickers indentation shows a tough cladding/substrate interface. The microhardness of the clad layer is increased from 200 HV of the substrate to about 750 HV due to the dissolution of elements like Fe, Cr and N in the matrix. Nanoindentation tests record a recovery ratio near to that of bulk NiTi, a result attributable to a relatively low dilution. The cavitation erosion resistance of the doubly clad samples is higher than that of 316-NiTi-powder (samples laser-surfaced with NiTi powder) and approaches that of NiTi plate. The high erosion resistance is attributed to a high hardness, high indentation recovery ratio and the absence of cracks or pores

  17. Formation Mechanism of Spherical TiC in Ni-Ti-C System during Combustion Synthesis.

    Science.gov (United States)

    Zhu, Guoliang; Wang, Wei; Wang, Rui; Zhao, Chuanbao; Pan, Weitao; Huang, Haijun; Du, Dafan; Wang, Donghong; Shu, Da; Dong, Anping; Sun, Baode; Jiang, Sheng; Pu, Yilong

    2017-08-29

    The formation mechanism of TiC particles in a Ni-Ti-C system were revealed by using differential thermal analysis (DTA), XRD, and SEM to identify the reaction products in different temperature ranges. The results indicated that the synthesis mechanism of TiC in Ni-Ti-C system was complex; several reactions were involved in the combustion synthesis of TiC-Ni composite. The Ni-Ti intermediate phases play important roles during the formation of TiC. Moreover, the influence of heating rate on the size range of TiC was also discussed.

  18. Effects of Fluoride on NiTi Orthodontic Archwires: An X-ray Diffraction Study

    Directory of Open Access Journals (Sweden)

    Sumit Kumar Yadav

    2013-01-01

    Results: Unloading force values of NiTi orthodontic wires were significantly decreased after exposure to both fluoride solutions (p < 0.001. Corrosive changes in surface topography were observed for both fluoride solutions. Wires exposed to acidic fluoride appeared as more severely affected. X-ray diffraction analysis showed no change in crystal lattice of NiTi wires in both solutions. Conclusion: The results suggest that using topical fluoride agents with NiTi wire could decrease the functional unloading mechanical properties of the wire and contribute to prolonged orthodontic treatment.

  19. Neutron, x-ray scattering and TEM studies of Ni-Ti multilayers

    International Nuclear Information System (INIS)

    Keem, J.E.; Wood, J.; Grupido, N.; Hart, K.; Nutt, S.; Reichel, D.G.; Yelon, W.B.

    1988-01-01

    The authors present an analysis of Ni-Ti multilayer neutron reflectors and supermirrors undertaken to identify the causes of the lower than expected observed scattering power and critical angle enhancement of Ni-Ti supermirrors. Results of these investigations focus attention on cusp formation in the Ni-Ti bilayers as probable cause for the reduced neutron scattering power. Grazing angle x-ray and neutron scattering, wide angle neutron diffraction and analytical cross sectional TEM have been used. The multilayers were produced by magnetron sputtering and ion-beam deposition on float glass substrates and silicon wafers

  20. Near Net Shape Fabrication Technology for Shape Memory Alloy Components, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — This STTR Phase I effort proposes to develop an innovative, affordable processing route for larger-sized shape memory alloy (SMA) components. Despite significant...