International Nuclear Information System (INIS)
Navin Vinayak, S.; Sunitha, Y.; Rangarajan, S.; Narasimhan, S.V.
2008-01-01
Nano materials have different properties from the corresponding bulk materials because of fine grain size, large fraction of surface atoms, high surface energy and high grain boundary volume fraction. For similar reasons, the nano-alloy coatings show superior high-temperature corrosion resistance and are generally more resistant to stress corrosion cracking. Hence, it is of interest to know the materials performance, if the structural materials used in nuclear reactors are made of nano-grains. In Indian PHWRs, Incoloy-800 is being used as the steam generator tubing material. It's corrosion resistance property is very important as it forms not only the pressure boundary between the radioactive primary water and non-active secondary water but also from the view point of loss of heavy water, in case of any corrosion damage. In this paper, the corrosion resistance of the oxide films formed on nano-grain nickel film electrodeposited on Incoloy-800 (a) in the presence of saccharine (WS) and (b) in the absence of saccharine (WOS) were compared with that formed on Commercial Ni foil, using electrochemical dc polarization and ac impedance techniques. The surface morphology, elemental analysis and grain size were studied with SEM, EDX and XRD techniques respectively. The nano-grain nickel films were prepared on Incoloy-800 by electrodeposition using Watt's Bath with saccharine sodium as a surfactant. The oxide films were developed by exposing them to LiOH solution (pH-10.0) at 245 deg C for 3 days (A-group) and 7 days (B-group). XRD results showed that the grain size of Ni formed in the absence of saccharine (WOS) was ∼ 60 nm and did not change after being autoclaved. But, for Ni formed in the presence of saccharine (WS), the grain size was ∼ 16 nm which increased to 40-50 nm after being autoclaved. With both A and B-group specimens, the PDAP curves showed an active-passive transition, a passive region and a transpassive region in 2N H 2 SO 4 . However, the critical
Grain Boundary Engineering of Electrodeposited Thin Films
DEFF Research Database (Denmark)
Alimadadi, Hossein
is not yet well-understood. This, at least partly, owes to the lack of robust characterization methods for analyzing the nature of grain boundaries including the grain boundary plane characteristics, until recently. In the past decade, significant improvements in the 2-dimensional and 3-dimensional analysis...... of the favorable boundaries that break the network of general grain boundaries. Successful dedicated synthesis of a textured nickel film fulfilling the requirements of grain boundary engineered materials, suggests improved boundary specific properties. However, the textured nickel film shows fairly low...... thermal stability and growth twins annihilate by thermal treatment at 600 degree C. In contrast, for oriented grains, growth nano-twins which are enveloped within columnar grains show a high thermal stability even after thermal treatment at 600 degree C. In order to exploit the high thermal...
Armstrong, R. W.; Balasubramanian, N.
2017-08-01
It is shown that: (i) nano-grain nickel flow stress and hardness data at ambient temperature follow a Hall-Petch (H-P) relation over a wide range of grain size; and (ii) accompanying flow stress and strain rate sensitivity measurements follow an analogous H-P relationship for the reciprocal "activation volume", (1/v*) = (1/A*b) where A* is activation area. Higher temperature flow stress measurements show a greater than expected reduction both in the H-P kɛ and in v*. The results are connected with smaller nano-grain size (tested at very low imposed strain rates.
Grain size and lattice parameter's influence on band gap of SnS thin nano-crystalline films
Energy Technology Data Exchange (ETDEWEB)
Gupta, Yashika [Department of Electronics, S.G.T.B. Khalsa College, University of Delhi, Delhi 110007 (India); Department of Electronic Science, University of Delhi-South Campus, New Delhi 110021 (India); Arun, P., E-mail: arunp92@physics.du.ac.in [Department of Electronics, S.G.T.B. Khalsa College, University of Delhi, Delhi 110007 (India); Naudi, A.A.; Walz, M.V. [Facultad de Ingeniería, Universidad Nacional de Entre Ríos, 3101 Oro Verde (Argentina); Albanesi, E.A. [Facultad de Ingeniería, Universidad Nacional de Entre Ríos, 3101 Oro Verde (Argentina); Instituto de Física del Litoral (CONICET-UNL), Guemes 3450, 3000 Santa Fe (Argentina)
2016-08-01
Tin sulphide nano-crystalline thin films were fabricated on glass and Indium Tin Oxide (ITO) substrates by thermal evaporation method. The crystal structure orientation of the films was found to be dependent on the substrate. Residual stress existed in the films due to these orientations. This stress led to variation in lattice parameter. The nano-crystalline grain size was also found to vary with film thickness. A plot of band-gap with grain size or with lattice parameter showed the existence of a family of curves. This implied that band-gap of SnS films in the preview of the present study depends on two parameters, lattice parameter and grain size. The band-gap relation with grain size is well known in the nano regime. Experimental data fitted well with this relation for the given lattice constants. The manuscript uses theoretical structure calculations for different lattice constants and shows that the experimental data follows the trend. Thus, confirming that the band gap has a two variable dependency. - Highlights: • Tin sulphide films are grown on glass and ITO substrates. • Both substrates give differently oriented films. • The band-gap is found to depend on grain size and lattice parameter. • Using data from literature, E{sub g} is shown to be two parameter function. • Theoretical structure calculations are used to verify results.
International Nuclear Information System (INIS)
Khorsand, S.; Raeissi, K.; Ashrafizadeh, F.
2014-01-01
A super-hydrophobic nickel film with micro-nano structure was successfully fabricated by electrodeposition process. By controlling electrodeposition parameters and considering different storage times for the coatings in air, various nickel films with different wettability were fabricated. Surface morphology of nickel films was examined by means of scanning electron microscopy (SEM). The results showed that the micro-nano nickel film was well-crystallized and exhibited pine cone-like microstructure with nano-cone arrays randomly dispersed on each micro-protrusion. The wettability of the micro-nano nickel film varied from super-hydrophilicity (water contact angle 5.3°) to super-hydrophobicity (water contact angle 155.7°) by exposing the surface in air at room temperature. The corrosion resistance of the super-hydrophobic film was estimated by electrochemical impedance spectroscopy (EIS) and Tafel polarization measurements. The potentiodynamic curves revealed that the corrosion rate of superhydrophobic surface was only 0.16% of the bare copper substrate. Moreover, EIS measurements and appropriate equivalent circuit models revealed that the corrosion resistance of nickel films considerably improved with an increase in the hydrophobicity. The superhydrophobic surface also exhibited an excellent long-term durability in neutral 3.5 wt.% NaCl solution.
Jeong, Myung-Sun; Ju, Byeong-Kwon; Lee, Jeon-Kook
2015-06-01
We observed the effects of nickel plating temperatures for controlling the surface morphologies of the deposited nickel layers on the alumina nano-pores. The alumina nano-channels were filled with nickel at various processing temperatures of 60-90 degrees C. The electrical properties of the alumina film capacitors were changed with processing temperatures. The electroless nickel plating (ENP) at 60 degrees C improved the nickel penetration into the alumina nano-channels due to the reduced reaction rate. Nickel layers are uniformly formed on the high aspect ratio alumina pores. Due to the uniform nickel electrode, the capacitance density of the alumina film capacitors is improved by the low leakage current, dissipation factor and equivalent series resistance. Alumina film capacitors made by ENP at 60 degrees C had a high capacitance density of 160 nF/cm2.
Investigation of interdiffusion in copper-nickel bilayer thin films
Energy Technology Data Exchange (ETDEWEB)
Abdul-Lettif, Ahmed M. [Physics Department, College of Science, Babylon University, Hilla (Iraq)]. E-mail: abdullettif@yahoo.com
2007-01-15
Auger depth profiling technique and X-ray diffraction analysis have been employed to study the interdiffusion in vacuum-deposited copper-nickel bilayer thin films. An adaptation of the Whipple model was used to determine the diffusion coefficients of both nickel in copper and copper in nickel. The calculated diffusion coefficient is (2.0x10{sup -7} cm{sup 2}/s)exp(-1.0 eV/kT) for nickel in copper, and (6x10{sup -8} cm{sup 2}/s)exp(-0.98 eV/kT) for copper in nickel. The difference between the diffusion parameters obtained in the present work and those extracted by other investigators is attributed essentially to the difference in the films microstructure and to the annealing ambient. It is concluded that interdiffusion in the investigated films is described by type-B kinetics in which rapid grain-boundary diffusion is coupled to defect-enhanced diffusion into the grain interior. The present data raise a question about the effectiveness of nickel as a diffusion barrier between copper and the silicon substrate.
Electrodeposition of nickel nano wire arrays
International Nuclear Information System (INIS)
Nur Ubaidah Saidin; Kok Kuan Ying; Ng Inn Khuan; Nurazila Mat Zali; Siti Salwa Zainal Abidin
2010-01-01
Synthesis, characterization and assembly of one-dimensional nickel nano wires prepared by template directed electrodeposition are discussed in this paper. Parallel arrays of high aspect ratio nickel nano wires were electrodeposited using electrolytes with different cations and pH. The nano wires were characterized using X-ray diffractometry and scanning electron microscopy. It was found that the orientations of the electro deposited Ni nano wires were governed by the deposition current and the electrolyte conditions. Free standing nickel nano wires can be obtained by dissolving the template. Due to the magnetic nature of the nano wires, magnetic alignment was employed to assemble and position the free standing nano wires in the device structure. (author)
Progress on sputter-deposited thermotractive titanium-nickel films
International Nuclear Information System (INIS)
Grummon, D.S.; Hou Li; Zhao, Z.; Pence, T.J.
1995-01-01
It is now well established that titanium-nickel alloys fabricated as thin films by physical vapor deposition can display the same transformation and shape-memory effects as their ingot-metallurgy counterparts. As such they may find important application to microelectromechanical and biomechanical systems. Furthermore, we show here that titanium-nickel films may be directly processed so as to possess extremely fine austenite grain size and very high strength. These films display classical transformational superelasticity, including high elastic energy storage capacity, the expected dependence of martensite-start temperature on transformation enthalpy, and large, fully recoverable anelastic strains at temperatures above A f . Processing depends on elevated substrate temperatures during deposition, which may be manipulated within a certain range to control both grain size and crystallographic texture. It is also possible to deposit crystalline titanium-nickel films onto polymeric substrates, making them amenable to lithographic patterning into actuator elements that are well-suited to electrical excitation of the martensite reversion transformation. Finally, isothermal annealing of nickel-rich films, under conditions of controlled extrinsic residual stress, leads to topotaxial orientation of Ni 4 Ti 3 -type precipitates, and the associated possibility of two-way memory effects. Much work remains to be done, especially with respect to precise control of composition. (orig.)
Desilva, L. A.; Bandara, T. M. W. J.; Hettiarachchi, B. H.; Kumara, G. R. A.; Perera, A. G. U.; Rajapaksa, R. M. G.; Tennakone, K.
Dye-sensitized and perovskite solar cells and other nanostructured heterojunction electronic devices require securing intimate electronic contact between nanostructured surfaces. Generally, the strategy is solution phase coating of a hole -collector over a nano-crystalline high-band gap n-type oxide semiconductor film painted with a thin layer of the light harvesting material. The nano-crystallites of the hole - collector fills the pores of the painted oxide surface. Most ills of these devices are associated with imperfect contact and high resistance of the hole conducting layer constituted of nano-crystallites. Denaturing of the delicate light harvesting material forbid sintering at elevated temperatures to reduce the grain boundary resistance. It is found that the interfacial and grain boundary resistance can be significantly reduced via incorporation of redox species into the interfaces to form ultra-thin layers. Suitable redox moieties, preferably bonded to the surface, act as electron transfer relays greatly reducing the film resistance offerring a promising method of enhancing the effective hole mobility of nano-crystalline hole-collectors and developing hole conductor paints for application in nanostructured devices.
Energy Technology Data Exchange (ETDEWEB)
Kim, Hong-Ki; Lee, Young-Hie, E-mail: yhlee@kw.ac.kr [Department of Electronics Materials Engineering, Kwangwoon University, Seoul (Korea, Republic of); Lee, Seung-Hwan [Department of Electronics Materials Engineering, Kwangwoon University, Seoul (Korea, Republic of); R and D Center, Samwha Capacitor, Yongin (Korea, Republic of); In Kim, Soo; Woo Lee, Chang [Department of Nano and Electronic Physics, Kookmin University, Seoul (Korea, Republic of); Rag Yoon, Jung [R and D Center, Samwha Capacitor, Yongin (Korea, Republic of); Lee, Sung-Gap [Department of Ceramic Engineering, Engineering Research Institute, Gyeongsang National University, Jinju (Korea, Republic of)
2014-01-07
In order to investigate the dielectric strength properties of the BaTiO{sub 3} films with nano-scale grains with uniform grain size and no voids, BaTiO{sub 3} films were fabricated with a thickness of 1 μm by an AD process, and the fabricated films were sintered at 800, 900, and 1000 °C in air and reducing atmosphere. The films have superior dielectric strength properties due to their uniform grain size and high density without any voids. In addition, based on investigation of the leakage current (intrinsic) properties, it was confirmed that the sintering conditions of the reducing atmosphere largely increase leakage currents due to generated electrons and doubly ionized oxygen vacancies following the Poole-Frenkel emission mechanism, and increased leakage currents flow at grain boundary regions. Therefore, we conclude that the extrinsic breakdown factors should be eliminated for superior dielectric strength properties, and it is important to enhance grain boundaries by doping acceptors and rare-earth elements.
Super-hydrophobic nickel films with micro-nano hierarchical structure prepared by electrodeposition
International Nuclear Information System (INIS)
Hang Tao; Hu Anmin; Ling Huiqin; Li Ming; Mao Dali
2010-01-01
Super-hydrophobic nickel films were prepared by a simple and low cost electrodepositing method. The surface morphologies of the films characterized by scanning electronic microscope exhibit hierarchical structure with micro-nanocones array, which can be responsible for their super-hydrophobic characteristic (water contact angle over 150 o ) without chemical modification. The wettability of the film can be varied from super-hydrophobic (water contact angle 154 o ) to relatively hydrophilic (water contact angle 87 o ) by controlling the size of the micro-nanocones. The mechanism of the hydrophobic characteristic of nickel films with this unique structure was illustrated by several models. Such micro-nanostructure and its special wettability are expected to be applied in the practical industry.
International Nuclear Information System (INIS)
Logutenko, O.A.; Titkov, A.I.; Vorobyov, A.M.; Yukhin, Y.M.; Lyakhov, N.Z.
2016-01-01
Nickel linear nano structures were synthesized by reduction of nickel formate with hydrazine hydrate in ethylene glycol medium in the absence of any surfactants or capping agents for direction of the particles growth. The effect of the synthesis conditions such as temperature, reduction time, type of polyol, and nickel formate concentration on the reduction products was studied. The size and morphology of the nickel nano wires were characterized by X-ray diffraction, scanning, and transmission electron microscopy. It was shown that the nickel nano crystallites were wire-shaped with a face-center-cubic phase. Ethylene glycol was found to play a crucial role in the formation of the nickel nano wires. The possible growth processes of the wire-shaped particles taking place at 110 and 130 degree are discussed. It was shown that, under certain synthesis conditions, nickel nano wires grow on the surface of the crystals of the solid intermediate of nickel with hydrazine hydrate.
Huo, Wenyi; Liu, Xiaodong; Tan, Shuyong; Fang, Feng; Xie, Zonghan; Shang, Jianku; Jiang, Jianqing
2018-05-01
Nano-twinned, nanocrystalline CoCrFeNi high-entropy alloy films were produced by magnetron sputtering. The films exhibit a high hardness of 8.5 GPa, the elastic modulus of 161.9 GPa and the resistivity as high as 135.1 μΩ·cm. The outstanding mechanical properties were found to result from the resistance of deformation created by nanocrystalline grains and nano-twins, while the electrical resistivity was attributed to the strong blockage effect induced by grain boundaries and lattice distortions. The results lay a solid foundation for the development of advanced films with structural and functional properties combined in micro-/nano-electronic devices.
Site-selective electroless nickel plating on patterned thin films of macromolecular metal complexes.
Kimura, Mutsumi; Yamagiwa, Hiroki; Asakawa, Daisuke; Noguchi, Makoto; Kurashina, Tadashi; Fukawa, Tadashi; Shirai, Hirofusa
2010-12-01
We demonstrate a simple route to depositing nickel layer patterns using photocross-linked polymer thin films containing palladium catalysts, which can be used as adhesive interlayers for fabrication of nickel patterns on glass and plastic substrates. Electroless nickel patterns can be obtained in three steps: (i) the pattern formation of partially quaterized poly(vinyl pyridine) by UV irradiation, (ii) the formation of macromolecular metal complex with palladium, and (iii) the nickel metallization using electroless plating bath. Metallization is site-selective and allows for a high resolution. And the resulting nickel layered structure shows good adhesion with glass and plastic substrates. The direct patterning of metallic layers onto insulating substrates indicates a great potential for fabricating micro/nano devices.
Energy Technology Data Exchange (ETDEWEB)
Zarebidaki, Arman, E-mail: arman.zare@iauyazd.ac.ir; Mahmoudikohani, Hassan, E-mail: hassanmahmoudi.k@gmail.com; Aboutalebi, Mohammad-Reza
2014-12-05
Highlights: • Activation, zincating, and Cu electrodeposition were used as pretreatment processes for electrodeposition of nickel coatings. • Nano-crystalline nickel coatings were successfully electrodeposited onto the AZ91 Mg alloys. • Effect of nickel electrodeposited coating on the corrosion resistance of AZ91 Mg alloy has been studied. - Abstract: In order to enhance the corrosion resistance, nickel coating was electrodeposited onto AZ91 Mg alloy. Activation, zincating, and Cu electrodeposition used as pretreatment processes for better adhesion and corrosion performance of the nickel over layer. The corrosion properties of the AZ91 Mg alloy, nickel electroplated AZ91 Mg alloy, and pure nickel was assessed via polarization and electrochemical impedance spectroscopy (EIS) methods in 3.5 wt% NaCl solution. Moreover, the structure of the coating was investigated by means of X-ray diffraction, whereas specimen’s morphology and elemental composition were analyzed using scanning electron microscope (SEM) equipped with energy dispersive spectrometer (EDS). Measurements revealed that the coating has a nano-crystalline structure with the grain size of 95 nm. Corrosion results showed superior corrosion resistance for the coated AZ91 Mg alloy as the corrosion current density decreased from 2.5 × 10{sup −4} A cm{sup −2}, for the uncoated sample, to 1.5 × 10{sup −5} A cm{sup −2}, for coated specimen and the corrosion potential increased from −1.55 V to −0.98 V (vs. Ag/AgCl) at the same condition.
Imantalab, O.; Fattah-alhosseini, A.; Keshavarz, M. K.; Mazaheri, Y.
2016-02-01
In this work, electrochemical behavior of annealed (micro-) and nano-grained pure copper (fabricated by accumulative roll bonding process) in phosphate buffer solutions of various pH values ranging from 10.69 to 12.59 has been studied. Before any electrochemical measurements, evaluation of microstructure was obtained by optical microscope and transmission electron microscopy. To investigate the electrochemical behavior of the samples, the potentiodynamic polarization, Mott-Schottky analysis, and electrochemical impedance spectroscopy (EIS) were carried out. Potentiodynamic polarization plots and EIS measurements revealed that as a result of grain refinement, the passive behavior of the nano-grained sample was improved compared to that of annealed pure copper. Also, Mott-Schottky analysis indicated that the passive films behaved as p-type semiconductors and grain refinement did not change the semiconductor type of passive films.
Mechanisms of fatigue in LIGA Ni MEMS thin films
International Nuclear Information System (INIS)
Yang, Y.; Imasogie, B.I.; Allameh, S.M.; Boyce, B.; Lian, K.; Lou, J.; Soboyejo, W.O.
2007-01-01
This paper presents the results of an experimental study of the mechanisms of fatigue in LIGA Ni micro-electro-mechanical systems (MEMS) thin films with micro-scale columnar and nano-scale equiaxed grains. Stress-life behavior is reported for films with thicknesses of 70 and 270 μm. The stress-life data are compared with previously reported data for Ni MEMS films and bulk Ni. The films with the nano-scale grains (15 nm average grain size) are shown to have higher strength and fatigue resistance (stress-life data) than those with columnar grain structures. The thicker films (with a columnar microstructure) are also shown to have comparable fatigue life to annealed Ni, while the thinner films (with a columnar microstructure) have comparable fatigue life to wrought Ni. The underlying mechanisms of crack nucleation and growth are elucidated via scanning and transmission electron microscopy. These reveal the formation of slip bands and surface oxides and crystallographic surface/sub-surface crack nucleation and growth in the films with the columnar structures. Surface and corner crack nucleations (from pre-existing defects) are observed in the nanostructured films. The implications of the results are discussed for the analyses of fatigue in nickel MEMS structures
Platinum nano-cluster thin film formed on glassy carbon and the application for methanol oxidation
International Nuclear Information System (INIS)
Chang, Gang; Oyama, Munetaka; Hirao, Kazuyuki
2007-01-01
As an interesting platinum nanostructured material, a Pt nano-cluster film (PtNCF) attached on glassy carbon (GC) is reported. Through the reduction of PtCl 4 2- by ascorbic acid in the presence of GC substrate, a Pt thin continuous film composed of small nano-clusters which had a further agglomerated nanostructure of small grains could be attached on the GC surface. It was found that the electrocatalytic ability of PtNCF for the methanol oxidation was apparently higher than those of the Pt nano-clusters dispersedly attached on GC or indium in oxides. In addition, the electrocatalytic performance of PtNCF per Pt amount was superior to that of Pt black on GC. These results indicate that, in spite of the continuous nanostructures, nano-grains of PtNCF worked effectively for the catalytic electrolysis. The present PtNCF can be regarded as an interesting thin film material, which can be easily prepared by one-step chemical reduction
Ternary graphene/amorphous carbon/nickel nanocomposite film for outstanding superhydrophobicity
Zhu, Xiaobo; Zhou, Shengguo; Yan, Qingqing
2018-04-01
A novel superhydrophobic ternary graphene/amorphous carbon/nickel (G-Ni/a-C:H) carbon-based film was fabricated by a green approach of high-voltage electrochemical deposition without using aqueous solution, which was systematically investigated including the structure and relating applications on self-cleaning and corrosion resistance. Graphene and nickel nano-particle inserts were effective to tailor the feature of nanocrystallite/amorphous microstructure as well as micro-nanoscale hierarchical rose-petal-like surface for G-Ni/a-C:H carbon-based film. Surprisingly, this deposit could present outstanding superhydrophobicity with the contact angle of 158.98 deg and sliding angle of 2.75 deg without any further surface modification meanwhile it could possess fairly well adhesion. Furthermore, the superhydrophobic G-Ni/a-C:H carbon-based film could exhibit excellent corrosion resistance and self-cleaning performances compared to no graphene incorporated deposit. The procedure of fabricating deposit might be simple, scalable, and environmental friendly, indicating a promising prospect for industrial applications in the field of anti-fouling, anti-corrosion and drag resistance.
The effect of current density and saccharin addition on the grain size of nickel coatings
Energy Technology Data Exchange (ETDEWEB)
Uhm, Young Rang; Park, Keun Yung; Son, Kwang Jae; Shim, Young Ho; Choi, Sun Ju [KAERI, Daejeon (Korea, Republic of)
2012-10-15
Recently, the main advantage of a radioisotope 'fuel' is concentrated, because it is 'burned' at the rate of the isotopes half life. In other words, given a half life of 100 years, a nuclear battery would still produce half of its initial starting power after 100 years. A speck of a radioisotope like nickel 63, for example, contains enough energy to power a nano nuclear battery for decades, and to do so safely. Ni 63, a beta radiation source, is prepared by electrical deposition of radioactive Ni 63 ions on thin non radioactive nickel foil. Ni 63 plating is similar to other electroplating processes that employ soluble metal anodes. It requires the passage of a direct current between two electrodes that are immersed in a conductive, aqueous solution of nickel salts. The charged Ni ions are formed by sulfate, sulfamate, chloride, and a Watts bath. However, the charged Ni 63 ions are formed by dissolving metal Ni 63. To establish the coating condition of Ni 63, non radioactive metal Ni particles were dissolved in an acid solution and electroplated on the Ni sheet. A continuous increase in the grain size versus current density has also been recognized in the direct current electrodeposition of nickel coating. On the other hand, A runa et al. reported that the current density has no significant effect on the grain size of nickel electro deposits. A review of the literature shows that saccharin has often been added to a nickel plating bath since the 1980s to improve the ductility and brightness, and in later periods as a grain refiner agent. In the present paper, not only the preparation of the Ni plating solution prepared by dissolving metal particles but also an optimization of the deposition conditions, such as the influence of current density and saccharin concentration on the grain size, was investigated. The proposed model can also be applied for radioactive Ni 63 electroplating.
The effect of current density and saccharin addition on the grain size of nickel coatings
International Nuclear Information System (INIS)
Uhm, Young Rang; Park, Keun Yung; Son, Kwang Jae; Shim, Young Ho; Choi, Sun Ju
2012-01-01
Recently, the main advantage of a radioisotope 'fuel' is concentrated, because it is 'burned' at the rate of the isotopes half life. In other words, given a half life of 100 years, a nuclear battery would still produce half of its initial starting power after 100 years. A speck of a radioisotope like nickel 63, for example, contains enough energy to power a nano nuclear battery for decades, and to do so safely. Ni 63, a beta radiation source, is prepared by electrical deposition of radioactive Ni 63 ions on thin non radioactive nickel foil. Ni 63 plating is similar to other electroplating processes that employ soluble metal anodes. It requires the passage of a direct current between two electrodes that are immersed in a conductive, aqueous solution of nickel salts. The charged Ni ions are formed by sulfate, sulfamate, chloride, and a Watts bath. However, the charged Ni 63 ions are formed by dissolving metal Ni 63. To establish the coating condition of Ni 63, non radioactive metal Ni particles were dissolved in an acid solution and electroplated on the Ni sheet. A continuous increase in the grain size versus current density has also been recognized in the direct current electrodeposition of nickel coating. On the other hand, A runa et al. reported that the current density has no significant effect on the grain size of nickel electro deposits. A review of the literature shows that saccharin has often been added to a nickel plating bath since the 1980s to improve the ductility and brightness, and in later periods as a grain refiner agent. In the present paper, not only the preparation of the Ni plating solution prepared by dissolving metal particles but also an optimization of the deposition conditions, such as the influence of current density and saccharin concentration on the grain size, was investigated. The proposed model can also be applied for radioactive Ni 63 electroplating
Synthesis of Nickel and Nickel Hydroxide Nano powders by Simplified Chemical Reduction
International Nuclear Information System (INIS)
Tientong, J.; Garcia, S.; Thurber, C.R.; Golden, T.D.
2014-01-01
Nickel nano powders were synthesized by a chemical reduction of nickel ions with hydrazine hydrate at ph ∼ 12.5. Sonication of the solutions created a temperature of 54-65 °C to activate the reduction reaction of nickel nanoparticles. The solution ph affected the composition of the resulting nanoparticles. Nickel hydroxide nanoparticles were formed from an alkaline solution (ph ∼10) of nickel-hydrazine complexed by dropwise titration. X-ray diffraction of the powder and the analysis of the resulting Williamson-Hall plots revealed that the particle size of the powders ranged from 12 to 14 nm. Addition of polyvinylpyrrolidone into the synthesis decreased the nickel nanoparticle size to approximately 7 nm. Dynamic light scattering and scanning electron microscopy confirmed that the particles were in the nanometer range. The structure of the synthesized nickel and nickel hydroxide nanoparticles was identified by X-ray diffraction and Fourier transform infrared spectroscopy.
Deformation strain inhomogeneity in columnar grain nickel
DEFF Research Database (Denmark)
Wu, G.L.; Godfrey, A.; Juul Jensen, D.
2005-01-01
A method is presented for determination of the local deformation strain of individual grains in the bulk of a columnar grain sample. The method, based on measurement of the change in grain area of each grain, is applied to 12% cold rolled nickel. Large variations are observed in the local strain...... associated with each grain. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved....
Hong, Min; Xu, Shusheng; Yao, Lu; Zhou, Chao; Hu, Nantao; Yang, Zhi; Hu, Jing; Zhang, Liying; Zhou, Zhihua; Wei, Hao; Zhang, Yafei
2018-07-06
A self-free-standing core-sheath structured hybrid membrane electrodes based on nickel and nickel based metal-organic complexes (Ni@Ni-OC) was designed and constructed for high volumetric supercapacitors. The self-standing Ni@Ni-OC film electrode had a high volumetric specific capacity of 1225.5 C cm -3 at 0.3 A cm -3 and an excellent rate capability. Moreover, when countered with graphene-carbon nanotube (G-CNT) film electrode, the as-assembled Ni@Ni-OC//G-CNT hybrid supercapacitor device delivered an extraordinary volumetric capacitance of 85 F cm -3 at 0.5 A cm -3 and an outstanding energy density of 33.8 at 483 mW cm -3 . Furthermore, the hybrid supercapacitor showed no capacitance loss after 10 000 cycles at 2 A cm -3 , indicating its excellent cycle stability. These fascinating performances can be ascribed to its unique core-sheath structure that high capacity nano-porous nickel based metal-organic complexes (Ni-OC) in situ coated on highly conductive Ni wires. The impressive results presented here may pave the way to construct s self-standing membrane electrode for applications in high volumetric-performance energy storage.
Dispersion of nano-nickel into γ-Al2O3 studied by positron
International Nuclear Information System (INIS)
Jun Zhu; Wang, S.J.; Luo, X.H.
2003-01-01
The positron annihilation lifetime spectra were measured as a function of the content of the nano-nickel, of temperature, as well as of the heating time for the supported nano-nickel catalyst that was prepared by mechanical mixture nano-metal nickel particles with gamma-alumina (γ-Al 2 O 3 ). The lifetime spectra were well resolved into four lifetime components. The longest lifetime τ 4 was assigned to ortho-positronium annihilating in the secondary pore of the γ-Al 2 O 3 . The results showed that part of the nano-nickel had entered into γ-Al 2 O 3 by thermal diffusion at heating above 200 deg. C and had interacted with the face of the γ-Al 2 O 3 , but the length of diffusion is not very large
Dispersion of nano-nickel into γ-Al 2O 3 studied by positron
Jun, Zhu; Wang, S. J.; Luo, X. H.
2003-10-01
The positron annihilation lifetime spectra were measured as a function of the content of the nano-nickel, of temperature, as well as of the heating time for the supported nano-nickel catalyst that was prepared by mechanical mixture nano-metal nickel particles with gamma-alumina ( γ-Al 2O 3). The lifetime spectra were well resolved into four lifetime components. The longest lifetime τ4 was assigned to ortho-positronium annihilating in the secondary pore of the γ-Al 2O 3. The results showed that part of the nano-nickel had entered into γ-Al 2O 3 by thermal diffusion at heating above 200°C and had interacted with the face of the γ-Al 2O 3, but the length of diffusion is not very large.
Campet, G.; Portier, J.; Morel, B.; Ferry, D.; Chabagno, J. M.; Benotmane, L.; Bourrel, M.
1992-01-01
Thin films of lithium-nickel oxide, whose texture consists of microcrystallites with an average grain size of 50 Å, permit highly reversible electrochemical insertion of lithium ions in Li+ conducting electrolytes. Therefore, the corresponding materials would be of great interest for energy storage applications. In addition, the lithium insertion/extraction reactions in the nickel-based layers are accompanied with a marked color change, making these films of interest for the devel...
Chen, R Z; Sun, H L; Xing, W H; Jin, W Q; Xu, N P
2009-02-01
The catalytic hydrogenation of p-nitrophenol to p-aminophenol over nano-sized nickel catalysts was carried out in a submerged ceramic membrane reactor. It has been demonstrated that the submerged ceramic membrane reactor is more suitable for the p-nitrophenol hydrogenation over nano-sized nickel catalysts compared with the side-stream ceramic membrane reactor, and the membrane module configuration has a great influence on the reaction rate of p-nitrophenol hydrogenation and the membrane treating capacity. The deactivation of nano-sized nickel is mainly caused by the adsorption of impurity on the surface of nickel and the increase of oxidation degree of nickel.
Formation and microstructure of nickel oxide films
Energy Technology Data Exchange (ETDEWEB)
Marcius, Marijan [Ruder Boskovic Institute, P.O. Box 180, HR-10002 Zagreb (Croatia); Ristic, Mira, E-mail: ristic@irb.hr [Ruder Boskovic Institute, P.O. Box 180, HR-10002 Zagreb (Croatia); Ivanda, Mile; Music, Svetozar [Ruder Boskovic Institute, P.O. Box 180, HR-10002 Zagreb (Croatia)
2012-11-15
Highlights: Black-Right-Pointing-Pointer Difference in NiO films formed on Ni plate or glass substrate were found. Black-Right-Pointing-Pointer NiO particle sizes on Ni plate changed from nano to micron dimensions. Black-Right-Pointing-Pointer NiO particle sizes on glass substrate changed from {approx}16 to {approx}27 nm. Black-Right-Pointing-Pointer Raman and UV/Vis/NIR spectra are related to the microstructure of NiO films. - Abstract: The formation and microstructure of NiO films on different substrates were monitored using XRD, Raman, UV/Vis/NIR and FE-SEM/EDS techniques. The formation of NiO films on Ni plates in air atmosphere between 400 and 800 Degree-Sign C was confirmed by XRD and Raman spectroscopy. The origin of Raman bands and corresponding Raman shifts in the samples are discussed. An increase in the size of NiO particles in the films from nano to micro dimensions was demonstrated. A change in the atomic ratio Ni:O with an increase in heating temperature was observed. Polished Ni plates coated with a thin Ni-acetate layer upon heating at high temperatures gave similar NiO microstructures on the surface like in the case of non-treated Ni plates. Glass substrates coated with thin Ni-acetate films upon heating between 400 and 800 Degree-Sign C yielded pseudospherical NiO nanoparticles. The dominant Raman band as an indicator of NiO formation on a glass substrate was shown. The formation of NiO nanoparticles on glass substrates with maximum size distribution from 16 to 27 nm in a broad temperature range from 400 to 800 Degree-Sign C can be explained by the absence of a constant source of metallic nickel which was present in the case of Ni plates.
Su, Jingyu; Jin, Guanping; Li, Changyong; Zhu, Xiaohui; Dou, Yan; Li, Yong; Wang, Xin; Wang, Kunwei; Gu, Qianqian
2014-11-01
Ni was effectively recovered from spent electroless nickel (EN) plating baths by forming a nano-nickel coated activated carbon composite. With the aid of ultrasonication, melamine-formaldehyde-tetraoxalyl-ethylenediamine chelating resins were grafted on activated carbon (MFT/AC). PdCl2 sol was adsorbed on MFT/AC, which was then immersed in spent electroless nickel plating bath; then nano-nickel could be reduced by ascorbic acid to form a nano-nickel coating on the activated carbon composite (Ni/AC) in situ. The materials present were carefully examined by Fourier transform infrared spectroscopy, X-ray diffraction, field emission scanning electron microscopy, X-ray photoelectron spectroscopy and electrochemistry techniques. The resins were well distributed on the inside and outside surfaces of activated carbon with a size of 120 ± 30 nm in MFT/AC, and a great deal of nano-nickel particles were evenly deposited with a size of 3.8 ± 1.1 nm in Ni/MFT. Moreover, Ni/AC was successfully used as a catalyst for ultrasonic degradation of 2,6-dichlorophenol. Copyright © 2014. Published by Elsevier B.V.
International Nuclear Information System (INIS)
Wang, Xiaoping; Wang, Jinye; Wang, Lijun
2016-01-01
A series of single-layer nano-carbon (SNC) films, diamond films, and diamond/nano-carbon (D/NC) composite films have been prepared on the highly doped silicon substrate by using microwave plasma chemical vapor deposition techniques. The films were characterised by scanning electron microscopy, Raman spectroscopy, and field emission I-V measurements. The experimental results indicated that the field emission maximum current density of D/NC composite films is 11.8–17.8 times that of diamond films. And the field emission current density of D/NC composite films is 2.9–5 times that of SNC films at an electric field of 3.0 V/μm. At the same time, the D/NC composite film exhibits the advantage of improved reproducibility and long term stability (both of the nano-carbon film within the D/NC composite cathode and the SNC cathode were prepared under the same experimental conditions). And for the D/NC composite sample, a high current density of 10 mA/cm"2 at an electric field of 3.0 V/μm was obtained. Diamond layer can effectively improve the field emission characteristics of nano-carbon film. The reason may be due to the diamond film acts as the electron acceleration layer.
Nickel films: Nonselective and selective photochemical deposition and properties
International Nuclear Information System (INIS)
Smirnova, N.V.; Boitsova, T.B.; Gorbunova, V.V.; Alekseeva, L.V.; Pronin, V.P.; Kon'uhov, G.S.
2006-01-01
Nickel films deposited on quartz surfaces by the photochemical reduction of a chemical nickel plating solution were studied. It was found that the deposition of the films occurs after an induction period, the length of which depends on the composition of the photolyte and the light intensity. Ni particles with a mean diameter of 20-30 nm were detected initially by transmission electron microscopy. The particles then increased in size (50 nm) upon irradiation and grouped into rings consisting of 4-5 particles. Irradiation with high-intensity light produces three-dimensional films. The calculated extinction coefficient of the nickel film was found to be 4800 L mol -1 cm -1 . Electron diffraction revealed that the prepared amorphous nickel films crystallize after one day of storage. It was determined that the films exhibit catalytic activity in the process of nickel deposition from nickel plating solution. The catalytic action remains for about 5-7 min after exposure of the films to air. The processes of selective and nonselective deposition of the nickel films are discussed. The use of poly(butoxy titanium) in the process of selective photochemical deposition enables negative and positive images to be prepared on quartz surfaces
Evolution of grain structure in nickel oxide scales
International Nuclear Information System (INIS)
Atkinson, H.V.
1987-01-01
In systems such as the oxidation of nickel, in which grain-boundary diffusion in the oxide can control the rate of oxidation, understanding of the factors governing the grain structure is of importance. High-purity mechanically polished polycrystalline nickel was oxidized at 700 0 C, 800 0 C, and 1000 0 C for times up to 20 hr in 1 atm O 2 . The scale microstructures were examined by parallel and transverse cross section transmission electron microscopy (TEM) and scanning electron microscopy (SEM). Texture coefficients were found by x-ray diffraction (XRD). Each grain in the transverse section grain boundary networks was systematically analyzed for width parallel to the Ni-NiO interface and perpendicular length, for boundary radius of curvature and for number of sides. The variation of these parameters with depth in the scale was examined. In particular, grains were increasingly columnar (i.e., with ratio of grain length to width > 1) at higher temperatures and longer times. Columnar grain boundaries tended to be fairly static; the columnar grain width was less than the rate controlling grain size predicted from the oxidation rate. The mean boundary curvature per grain provided a guide to the tendency for grain growth, except in the region of the Ni-NiO interface, where the boundaries were thought to be pinned
Elongated grains in cube textured nickel substrate tapes and flat wires
International Nuclear Information System (INIS)
Eickemeyer, J; Gueth, A; Holzapfel, B
2008-01-01
Cube textured nickel substrate tapes and flat wires with an increased grain aspect ratio were prepared from nickel micro-alloyed with silver plus yttrium and silver, respectively. Whereas the maximum grain aspect ratio for the tapes was about 6, this value reached up to 14 for the flat wires
In-situ Lead Removal by Iron Nano Particles Coated with Nickel
Directory of Open Access Journals (Sweden)
Mohammadreza Fadaei-tehrani
2016-01-01
Full Text Available This study investigates the potential of nano-zero-valent iron particles coated with nickel in the removal of lead (Pb2+ from porous media. For this purpose, the nano-particles were initially synthesized and later stablilized using the strach biopolymer prior to conducting batch and continuous experiments. The results of the batch experiments revealed that the reaction kinetics fitted well with the pseudo-first-order adsorption model and that the reaction rate ranged from 0.001 to 0.035 g/mg/min depending on solution pH and the molar ratio of Fe/Pb. Continuous experiments showed that lead remediation was mostly influenced not only by seepage velocity but also by the quantity and freshness of nZVI as well as the grain type of the porous media. Maximum Pb2+ removal rates obtained in the batch and lab models were 95% and 80%, respectively. Based on the present study, S-nZVI may be suggested as an efficient agent for in-situ remediation of groundwater contaminated with lead.
International Nuclear Information System (INIS)
Li, Tianshu; Liu, Li; Zhang, Bin; Li, Ying; Yan, Fengkai; Tao, Nairong; Wang, Fuhui
2014-01-01
Highlights: • Nanometer-grains (NG) and bundles of nano-twins (NT) is synthesized in 316L. • (NG + NT) and NT enhance the concentration of active Fe Fe in the passive film. • (NG + NT) and NT enhance the passive ability. • A Cr 0 -enriched layer forms at the passive film/metal interface. - Abstract: The passive behavior of a bulk nanostructured 316L austenitic stainless steel consisting of nanometer-sized grains (NG) and nano-twin bundles (NT) are investigated. The electrochemical results indicate that the spontaneous passivation ability and growth rate of passive film are improved. The X-ray photoelectron spectroscopy (XPS) shows that a Cr 0 -enriched layer forms at the passive film/metal interface. More nucleation sites afforded by the nanostructures and the enhanced diffusion rate of charged species across the passive film are believed to be responsible for the improved passive ability. The PDM model is introduced to elaborate the microscopic process of passivation
Avila, José; Razado, Ivy; Lorcy, Stéphane; Fleurier, Romain; Pichonat, Emmanuelle; Vignaud, Dominique; Wallart, Xavier; Asensio, María C.
2013-01-01
The ability to produce large, continuous and defect free films of graphene is presently a major challenge for multiple applications. Even though the scalability of graphene films is closely associated to a manifest polycrystalline character, only a few numbers of experiments have explored so far the electronic structure down to single graphene grains. Here we report a high resolution angle and lateral resolved photoelectron spectroscopy (nano-ARPES) study of one-atom thick graphene films on thin copper foils synthesized by chemical vapor deposition. Our results show the robustness of the Dirac relativistic-like electronic spectrum as a function of the size, shape and orientation of the single-crystal pristine grains in the graphene films investigated. Moreover, by mapping grain by grain the electronic dynamics of this unique Dirac system, we show that the single-grain gap-size is 80% smaller than the multi-grain gap recently reported by classical ARPES. PMID:23942471
Structural transformation of nickel hydroxide films during anodic oxidation
Energy Technology Data Exchange (ETDEWEB)
Crocker, Robert W. [Univ. of California, Berkeley, CA (United States); Muller, Rolf H. [Univ. of California, Berkeley, CA (United States)
1992-05-01
The transformation of anodically formed nickel hydroxide/oxy-hydroxide electrodes has been investigated. A mechanism is proposed for the anodic oxidation reaction, in which the reaction interface between the reduced and oxidized phases of the electrode evolves in a nodular topography that leads to inefficient utilization of the active electrode material. In the proposed nodular transformation model for the anodic oxidation reaction, nickel hydroxide is oxidized to nickel oxy-hydroxide in the region near the metal substrate. Since the nickel oxy-hydroxide is considerably more conductive than the surrounding nickel hydroxide, as further oxidation occurs, nodular features grow rapidly to the film/electrolyte interface. Upon emerging at the electrolyte interface, the reaction boundary between the nickel hydroxide and oxy-hydroxide phases spreads laterally across the film/electrolyte interface, creating an overlayer of nickel oxy-hydroxide and trapping uncharged regions of nickel hydroxide within the film. The nickel oxy-hydroxide overlayer surface facilitates the oxygen evolution side reaction. Scanning tunneling microscopy of the electrode in its charged state revealed evidence of 80 - 100 Angstrom nickel oxy-hydroxide nodules in the nickel hydroxide film. In situ spectroscopic ellipsometer measurements of films held at various constant potentials agree quantitatively with optical models appropriate to the nodular growth and subsequent overgrowth of the nickel oxy-hydroxide phase. A two-dimensional, numerical finite difference model was developed to simulate the current distribution along the phase boundary between the charged and uncharged material. The model was used to explore the effects of the physical parameters that govern the electrode behavior. The ratio of the conductivities of the nickel hydroxide and oxy-hydroxide phases was found to be the dominant parameter in the system.
Structural transformation of nickel hydroxide films during anodic oxidation
Energy Technology Data Exchange (ETDEWEB)
Crocker, R.W.; Muller, R.H.
1992-05-01
The transformation of anodically formed nickel hydroxide/oxy-hydroxide electrodes has been investigated. A mechanism is proposed for the anodic oxidation reaction, in which the reaction interface between the reduced and oxidized phases of the electrode evolves in a nodular topography that leads to inefficient utilization of the active electrode material. In the proposed nodular transformation model for the anodic oxidation reaction, nickel hydroxide is oxidized to nickel oxy-hydroxide in the region near the metal substrate. Since the nickel oxy-hydroxide is considerably more conductive than the surrounding nickel hydroxide, as further oxidation occurs, nodular features grow rapidly to the film/electrolyte interface. Upon emerging at the electrolyte interface, the reaction boundary between the nickel hydroxide and oxy-hydroxide phases spreads laterally across the film/electrolyte interface, creating an overlayer of nickel oxy-hydroxide and trapping uncharged regions of nickel hydroxide within the film. The nickel oxy-hydroxide overlayer surface facilitates the oxygen evolution side reaction. Scanning tunneling microscopy of the electrode in its charged state revealed evidence of 80 {endash} 100 Angstrom nickel oxy-hydroxide nodules in the nickel hydroxide film. In situ spectroscopic ellipsometer measurements of films held at various constant potentials agree quantitatively with optical models appropriate to the nodular growth and subsequent overgrowth of the nickel oxy-hydroxide phase. A two-dimensional, numerical finite difference model was developed to simulate the current distribution along the phase boundary between the charged and uncharged material. The model was used to explore the effects of the physical parameters that govern the electrode behavior. The ratio of the conductivities of the nickel hydroxide and oxy-hydroxide phases was found to be the dominant parameter in the system.
Energy Technology Data Exchange (ETDEWEB)
Lasheen, M.R., E-mail: ragaei24@link.net [Water Pollution Research Department, Environmental Research Division, National Research Centre, 33-El Buhoth St., Dokki, Cairo, 12311 (Egypt); El-Sherif, Iman Y., E-mail: iman57us@yahoo.com [Water Pollution Research Department, Environmental Research Division, National Research Centre, 33-El Buhoth St., Dokki, Cairo, 12311 (Egypt); Tawfik, Magda E., E-mail: magdaemileta@yahoo.com [Polymers and Pigments Department, National Research Centre, 33-El Buhoth St., Dokki, Cairo, 12311 (Egypt); El-Wakeel, S.T., E-mail: shaimaa_tw@yahoo.com [Water Pollution Research Department, Environmental Research Division, National Research Centre, 33-El Buhoth St., Dokki, Cairo, 12311 (Egypt); El-Shahat, M.F., E-mail: elshahatmf@hotmail.com [Faculty of Science, Ain Shams University, Khalifa El-Maamon St., Abbasiya Sq., 11566, Cairo (Egypt)
2016-08-15
Highlights: • Nano magnetite–chitosan films were prepared by casting method. • The efficiency of the prepared films for removing heavy metals was investigated. • The adsorption mechanism was studied using different isotherm and kinetic models. • Films reuse and metals recovery were studied. - Abstract: Nano magnetite chitosan (NMag–CS) film was prepared and characterized with different analytical methods. X-ray diffraction (XRD) patterns confirmed the formation of a pure magnetite structure and NMag–CS nanocomposite. TEM image of the film, revealed the uniform dispersion of magnetite nanoparticles inside chitosan matrix. The adsorption properties of the prepared film for copper, lead, cadmium, chromium and nickel metal ions were evaluated. Different factors affecting the uptake behavior by the composite films such as time, initial pH and film dose were investigated. The adsorption equilibrium attained using 2 g/L of the film after 120 min of reaction. The equilibrium data were analyzed using Langmuir and Freundlich models. The adsorption kinetics followed the mechanism of the pseudo-second-order equation for all metals. The metals regenerated from films with an efficiency greater than 95% using 0.1 M ethylene diamine tetra acetic acid (EDTA) and films were successfully reused for adsorption.
International Nuclear Information System (INIS)
Wu, Mao-Sung; Lin, Ya-Ping
2011-01-01
A nickel-oxide film with monodispersed open macropores was prepared on a stainless-steel substrate by electrophoretic deposition of a polystyrene-sphere monolayer followed by anodic electrodeposition of nickel oxy-hydroxide. The deposited films convert to cubic nickel oxide after annealing at 400 o C for 1 h. Galvanostatic charge and discharge results indicate that the nickel-oxide film with monodispersed open macropores is capable of delivering a higher capacity than the bare nickel-oxide film, especially in high-rate charge and discharge processes. The lithiation capacity of macroporous nickel oxide reaches 1620 mA h g -1 at 1 C current discharge and decreases to 990 mA h g -1 at 15 C current discharge. The presence of monodispersed open macropores in the nickel-oxide film might facilitate the electrolyte penetration, diffusion, and migration. Electrochemical reactions between nickel oxide and lithium ions are therefore markedly improved by this tailored film architecture.
Li, Bin; Zhang, Qin-Jian; Shi, Yan-Chao; Li, Jia-Jun; Li, Hong; Lu, Fan-Xiu; Chen, Guang-Chao
2014-08-01
A nano-crystlline diamond film is grown by the dc arcjet chemical vapor deposition method. The film is characterized by scanning electron microscopy, high-resolution transmission electron microscopy (HRTEM), x-ray diffraction (XRD) and Raman spectra, respectively. The nanocrystalline grains are averagely with 80 nm in the size measured by XRD, and further proven by Raman and HRTEM. The observed novel morphology of the growth surface, pineapple-like morphology, is constructed by cubo-octahedral growth zones with a smooth faceted top surface and coarse side surfaces. The as-grown film possesses (100) dominant surface containing a little amorphous sp2 component, which is far different from the nano-crystalline film with the usual cauliflower-like morphology.
Energy Technology Data Exchange (ETDEWEB)
Fontainha, C.C.P.; Nolasco, A.V. [Depto. de Engenharia Nuclear - DEN / UFMG - MG, Av. Antonio Carlos 6627, 31270-970 Belo Horizonte, MG (Brazil); Santos, A.P.; Faria, L.O. [Centro de Desenvolvimento da Tecnologia Nuclear, Av. Antonio Carlos 6627, C.P. 941, 30270-901, Belo Horizonte, MG (Brazil)
2015-07-01
. This result is discussed in terms of the high Z halides added to the sensitive layer of EB3 film, once the main components are C (42.3%), H (39.7%) and O (16.0%)1-2. Based on the above results, we have speculated about the abilities of XR-AQ films in the detection of the distribution of nano-sized particles that has high mass-energy attenuation coefficients for low energy x-rays, in polymer composites. In another investigation we tested the ability of XR-QA2 Gafchromic{sup R} films to evaluate the dispersion of ZrO{sub 2} nano-sized grain clusters in protective composites. The P(VDFTrFE)/ ZrO{sub 2} film was sandwiched between two XR-QA2 radiochromic films. In this setup, one radiochromic film is directly exposed to 100 mGy of the x-rays beam and another one measures the attenuated beam. After storage for 24 hours at room temperature under no light conditions, the irradiated radiochromic films were scanned under the same conditions in order to obtain a more reliable result. All films were scanned using the same size ROI in high resolution mode and saved as tagged image file format (TIFF). The untreated scanned image of the XR-AQ2 film directed exposed to the X-ray beam and the correspondent treated image with digital filters are shown. The untreated and treated image of the XR-AQ2 film that was exposed to the attenuated x-ray beam is shown. The image treated with digital filters seems to reproduce the dispersion of ZrO{sub 2} nano-sized grain clusters in the P(VDF-TrFE) copolymer matrix. This result is also discussed in terms of the high Z halides added to the sensitive layer of XR-AQ2 film and compared to the MEV images obtained from the P(VDF-TrFE)/ZrO{sub 2} composites. The results indicate a clear correlation between the 2D radiochromic image and the MEV photography.
Retardation of grain boundary self-diffusion in nickel doped with antimony and tin
International Nuclear Information System (INIS)
Padgett, R.A.; White, C.L.
1984-01-01
Many important metallurgical phenomena are strongly influenced or controlled by grain boundary mass transport. There is also much evidence that the composition of grain boundaries is often significantly different from the overall composition of metals and alloys, owing to strong segregation of residual (and often undetected) impurities. This segregation, which does not always advertise its presence through grain boundary brittleness, may vary markedly from heat to heat, and occasionally from specimen to specimen within a given heat. Unfortunately, there are relatively few experimental observations of how such segregation affects grain boundary mass transport, and even less fundamental understanding of how these effects occur. In this paper we present autoradiographic results on self-diffusion of 63 Ni in nickel and nickel doped with antimony and tin. While these results do not permit a quantitative evaluation of the grain boundary diffusivity, D, they qualitatively illustrate the dramatic effect that these solute elements have on the ability of nickel grain boundaries to act as preferential paths for mass transport
Microstructure and properties of ultrafine grain nickel 200 after hydrostatic extrusion processes
Sitek, R.; Krajewski, C.; Kamiński, J.; Spychalski, M.; Garbacz, H.; Pachla, W.; Kurzydłowski, K. J.
2012-09-01
This paper presents the results of the studies of the structure and properties of ultrafine grained nickel 200 obtained by hydrostatic extrusion processes. Microstructure was characterized by means of optical microscopy and electron transmission microscopy. Corrosion resistance was studied by impedance and potentiodynamic methods using an AutoLab PGSTAT 100 potentiostat in 0.1 M Na2SO4 solution and in acidified (by addition of H2SO4) 0.1 M NaCl solution at pH = 4.2 at room temperature. Microhardness tests were also performed. The results showed that hydrostatic extrusion produces a heterogeneous, ultrafine-grained microstructure in nickel 200. The corrosive resistance tests showed that the grain refinement by hydrostatic extrusion is accompanied by a decreased corrosive resistance of nickel 200.
Energy Technology Data Exchange (ETDEWEB)
Sharma, Shilpam; Amaladass, E.P. [Condensed Matter Physics Division, Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Sharma, Neha [Surface & Nanoscience Division, Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Harimohan, V. [Condensed Matter Physics Division, Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Amirthapandian, S. [Materials Physics Division, Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India); Mani, Awadhesh, E-mail: mani@igcar.gov.in [Condensed Matter Physics Division, Materials Science Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603102 (India)
2017-06-01
Disorder driven superconductor to insulator transition via intermediate metallic regime is reported in nano-crystalline thin films of molybdenum. The nano-structured thin films have been deposited at room temperature using DC magnetron sputtering at different argon pressures. The grain size has been tuned using deposition pressure as the sole control parameter. A variation of particle sizes, room temperature resistivity and superconducting transition has been studied as a function of deposition pressure. The nano-crystalline molybdenum thin films are found to have large carrier concentration but very low mobility and electronic mean free path. Hall and conductivity measurements have been used to understand the effect of disorder on the carrier density and mobilities. Ioffe-Regel parameter is shown to correlate with the continuous metal-insulator transition in our samples. - Highlights: • Thin films of molybdenum using DC sputtering have been deposited on glass. • Argon background pressure during sputtering was used to tune the crystallite sizes of films. • Correlation in deposition pressure, disorder and particle sizes has been observed. • Disorder tuned superconductor to insulator transition along with an intermediate metallic phase has been observed. • Enhancement of superconducting transition temperature and a dome shaped T{sub C} vs. deposition pressure phase diagram has been observed.
Jiao, Zhenjun; Ueno, Ai; Suzuki, Yuji; Shikazono, Naoki
2016-10-01
In this study, the reduction processes of nickel oxide at different temperatures were investigated using nickel-film anode to study the influences of reduction temperature on the initial performances and stability of nickel-yttria-stabilized zirconia anode. Compared to conventional nickel-yttria-stabilized zirconia composite cermet anode, nickel-film anode has the advantage of direct observation at nickel-yttria-stabilized zirconia interface. The microstructural changes were characterized by scanning electron microscopy. The reduction process of nickel oxide is considered to be determined by the competition between the mechanisms of volume reduction in nickel oxide-nickel reaction and nickel sintering. Electrochemical impedance spectroscopy was applied to analyze the time variation of the nickel-film anode electrochemical characteristics. The anode performances and microstructural changes before and after 100 hours discharging and open circuit operations were analyzed. The degradation of nickel-film anode is considered to be determined by the co-effect between the nickel sintering and the change of nickel-yttria-stabilized zirconia interface bonding condition.
Structural characterization of the nickel thin film deposited by glad technique
Directory of Open Access Journals (Sweden)
Potočnik J.
2013-01-01
Full Text Available In this work, a columnar structure of nickel thin film has been obtained using an advanced deposition technique known as Glancing Angle Deposition. Nickel thin film was deposited on glass sample at the constant emission current of 100 mA. Glass sample was positioned 15 degrees with respect to the nickel vapor flux. The obtained nickel thin film was characterized by Force Modulation Atomic Force Microscopy and by Scanning Electron Microscopy. Analysis indicated that the formation of the columnar structure occurred at the film thickness of 1 μm, which was achieved for the deposition time of 3 hours. [Projekat Ministarstva nauke Republike Srbije, br. III45005
Diffraction stress analysis of thin films; investigating elastic grain interaction
International Nuclear Information System (INIS)
Kumar, A.
2005-12-01
This work is dedicated to the investigation of specimens exhibiting anisotropic microstructures (and thus macroscopic elastic anisotropy) and/or inhomogeneous microstructures, as met near surfaces and in textured materials. The following aspects are covered: (i) Analysis of specimens with direction-dependent (anisotropic) elastic grain-interaction. Elastic grain-interaction determines the distribution of stresses and strains over the (crystallographically) differently oriented grains of a mechanically stressed polycrystal and the mechanical and diffraction (X-ray) elastic constants (relating (diffraction) lattice strains to mechanical stresses). Grain interaction models that allow for anisotropic, direction-dependent grain interaction have been developed very recently. The notion 'direction-dependent' grain-interaction signifies that different grain-interaction constraints prevail along different directions in a specimen. Practical examples of direction-dependent grain interaction are the occurrence of surface anisotropy in thin films and the surface regions of bulk polycrystals and the occurrence of grain-shape (morphological) texture. In this work, for the first time, stress analyses of thin films have been performed on the basis of these newly developed grain-interaction models. It has also been demonstrated that the identification of the (dominant) source of direction-dependent grain interaction is possible. The results for the grain interaction have been discussed in the light of microstructural investigations of the specimens by microscopic techniques. (ii) Analysis of specimens with depth gradients: Diffraction stress analysis can be hindered if gradients of the stress state, the composition or the microstructure occur in the specimen under investigation, as the so-called information depth varies in the course of a traditional stress measurement: Ambiguous results are thus generally obtained. In this work, a strategy for stress measurements at fixed
Thermal conductivity of nanoscale thin nickel films
Institute of Scientific and Technical Information of China (English)
YUAN Shiping; JIANG Peixue
2005-01-01
The inhomogeneous non-equilibrium molecular dynamics (NEMD) scheme is applied to model phonon heat conduction in thin nickel films. The electronic contribution to the thermal conductivity of the film is deduced from the electrical conductivity through the use of the Wiedemann-Franz law. At the average temperature of T = 300 K, which is lower than the Debye temperature ()D = 450 K,the results show that in a film thickness range of about 1-11 nm, the calculated cross-plane thermal conductivity decreases almost linearly with the decreasing film thickness, exhibiting a remarkable reduction compared with the bulk value. The electrical and thermal conductivities are anisotropic in thin nickel films for the thickness under about 10 nm. The phonon mean free path is estimated and the size effect on the thermal conductivity is attributed to the reduction of the phonon mean free path according to the kinetic theory.
Zhao, Hang; Lu, Yinxiang
2016-01-01
Nickel films were grown on citric acid (CA), malic acid (MA) and oxalic acid (OA) modified cuprammonium fabric (CF) substrates via electroless nickel deposition. The nickel films were examined using scanning electron microscopy (SEM) and X-ray diffraction (XRD). Their individual deposition rate and electromagnetic interference (EMI) shielding effectiveness (SE) were also investigated to compare the properties of electroless nickel films. SEM images illustrated that the nickel film on MA modified CF substrate was smooth and uniform, and the density of nickel nuclei was much higher. Compared with that of CA modified CF, the coverage of nickel nuclei on OA and MA modified CF substrate was very limited and the nickel particles size was too big. XRD analysis showed that the nickel films deposited on the different modified CF substrates had a structure with Ni (1 1 1) preferred orientation. All the nickel coatings via different acid modification were firmly adhered to the CF substrates, as demonstrated by an ultrasonic washing test. The result of tensile test indicated that the electroless nickel plating on CF has ability to strengthen the CF substrate while causes limited effect on tensile elongation. Moreover, the nickel film deposited on MA modified CF substrate showed more predominant in EMI SE than that deposited on CA or OA modified CF.
Columnar structure of reactively sputtered aluminium nitride films
International Nuclear Information System (INIS)
Chen Chisan; Hwang Binghwai; Lu Hongyang; Hsu Tzuchien
2002-01-01
Columnar structure of thin aluminium nitride (AlN) films is examined by x-ray diffractometry (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The films were deposited on SiO 2 /Si(100) substrate using radiofrequency reactive sputtering method. Strong [0001] preferred orientation is observed by XRD and confirmed by selected area diffraction pattern of TEM. Columnar grains of ∼50-100 nm inclined at an angle of ∼10 deg. to the substrate normal are observed by SEM. As revealed by TEM, each columnar grain is composed of nano-grains of the order of 10 nm and no faceting is observed in the nano-grains and columns. The [0001] preferred orientation results as columnar grains are oriented at various azimuthal angles with their c-axes perpendicular to the substrate surface. A slight tilt of a few tenths of a degree between adjacent nano-grains within a column is also observed. The random azimuthal orientation of columnar grains and small tilt between nano-grains in the films are accommodated by the amorphous phase present in the grain boundaries
Energy Technology Data Exchange (ETDEWEB)
Denayer, Jessica [Group of Research in Energy and Environment for MATerials (GREENMAT), University of Liège, allée de la chimie 3, 4000 Liège (Belgium); Bister, Geoffroy [Environmental and Material Research Association (CRIBC-INISMa), avenue gouverneur cornez 4, 7000 Mons (Belgium); Simonis, Priscilla [Laboratory LPS, University of Namur, rue de bruxelles 61, 5000 Namur (Belgium); Colson, Pierre; Maho, Anthony [Group of Research in Energy and Environment for MATerials (GREENMAT), University of Liège, allée de la chimie 3, 4000 Liège (Belgium); Aubry, Philippe [Environmental and Material Research Association (CRIBC-INISMa), avenue gouverneur cornez 4, 7000 Mons (Belgium); Vertruyen, Bénédicte [Group of Research in Energy and Environment for MATerials (GREENMAT), University of Liège, allée de la chimie 3, 4000 Liège (Belgium); Henrist, Catherine, E-mail: catherine.henrist@ulg.ac.be [Group of Research in Energy and Environment for MATerials (GREENMAT), University of Liège, allée de la chimie 3, 4000 Liège (Belgium); Lardot, Véronique; Cambier, Francis [Environmental and Material Research Association (CRIBC-INISMa), avenue gouverneur cornez 4, 7000 Mons (Belgium); Cloots, Rudi [Group of Research in Energy and Environment for MATerials (GREENMAT), University of Liège, allée de la chimie 3, 4000 Liège (Belgium)
2014-12-01
Highlights: • Surfactant-assisted USP: a novel and low cost process to obtain high quality nickel oxide films, with or without lithium dopant. • Increased uniformity and reduced light scattering thanks to the addition of a surfactant. • Improved electrochromic performance (coloration efficiency and contrast) for lithium-doped films by comparison with the undoped NiO film. - Abstract: Lithium-doped nickel oxide and undoped nickel oxide thin films have been deposited on FTO/glass substrates by a surfactant-assisted ultrasonic spray pyrolysis. The addition of polyethylene glycol in the sprayed solution has led to improved uniformity and reduced light scattering compared to films made without surfactant. Furthermore, the presence of lithium ions in NiO films has resulted in improved electrochromic performances (coloration contrast and efficiency), but with a slight decrease of the electrochromic switching kinetics.
Nano Ag-Doped In2O3 Thick Film: A Low-Temperature H2S Gas Sensor
Directory of Open Access Journals (Sweden)
D. N. Chavan
2011-01-01
Full Text Available Thick films of AR grade In2O3 were prepared by standard screen-printing technique. The gas sensing performances of thick films were tested for various gases. It showed maximum sensitivity to ethanol vapour at 350°C for 80 ppm concentration. To improve the sensitivity and selectivity of the film towards a particular gas, In2O3 sensors were surface-modified by dipping them in a solution of 2% nanosilver for different intervals of time. Obtained results indicated that spherical nano-Ag grains are highly dispersed on the surface of In2O3sensor. The surface area of the nano-Ag/ In2O3 sensor is several times larger than that of pure In2O3 sensor. In comparison with pure In2O3 sensor, all of the nano-Ag-doped sensors showed better sensing performance in respect of response, selectivity, and optimum operating temperature. The surface-modified (30 min In2O3 sensor showed larger sensitivity to H2S gas (10 ppm at 100°C. Nano silver on the surface of the film shifts the reactivity of film from ethanol vapour to H2S gas. A systematic study of gas sensing performance of the sensor indicates the key role played by the nano silver species on the surface. The sensitivity, selectivity, response, and recovery time of the sensor were measured and presented.
Film grain noise modeling in advanced video coding
Oh, Byung Tae; Kuo, C.-C. Jay; Sun, Shijun; Lei, Shawmin
2007-01-01
A new technique for film grain noise extraction, modeling and synthesis is proposed and applied to the coding of high definition video in this work. The film grain noise is viewed as a part of artistic presentation by people in the movie industry. On one hand, since the film grain noise can boost the natural appearance of pictures in high definition video, it should be preserved in high-fidelity video processing systems. On the other hand, video coding with film grain noise is expensive. It is desirable to extract film grain noise from the input video as a pre-processing step at the encoder and re-synthesize the film grain noise and add it back to the decoded video as a post-processing step at the decoder. Under this framework, the coding gain of the denoised video is higher while the quality of the final reconstructed video can still be well preserved. Following this idea, we present a method to remove film grain noise from image/video without distorting its original content. Besides, we describe a parametric model containing a small set of parameters to represent the extracted film grain noise. The proposed model generates the film grain noise that is close to the real one in terms of power spectral density and cross-channel spectral correlation. Experimental results are shown to demonstrate the efficiency of the proposed scheme.
Nano-grain SnO{sub 2} electrodes for high conversion efficiency SnO{sub 2}-DSSC
Energy Technology Data Exchange (ETDEWEB)
Lee, Jung-Hoon; Shin, Yu-Ju [Department of Chemistry, the Catholic University of Korea, Bucheon, Gyeonggi-do 422-743 (Korea, Republic of); Park, Nam-Gyu [School of Chemical Engineering, Sungkyunkwan University, Suwon, Gyeonggi-do 440-746 (Korea, Republic of)
2011-01-15
The nano-grain ZnO/SnO{sub 2} composite electrode was prepared by adding 5 w% of the 200-250 nm ZnO particles to the 5 nm SnO{sub 2} colloid in the presence of hydroxypropylcellulose (M.W.=80,000). The nano-grain SnO{sub 2} electrode was obtained by removing the ZnO particles from the composite electrode using acetic acid. The FE-SEM micrographs revealed that both electrodes consisted of interconnected nano-grains that were ca. 800 nm in size, and the large pores between the grains furnished the wide electrolyte diffusion channels within the electrodes. The photovoltaic properties of the nano-grain electrodes were investigated by measuring the I-V behaviors, the IPCE spectra and the ac-impedance spectra. The nano-grain electrodes exhibited remarkably improved conversion efficiencies of 3.96% for the composite and 2.98% for the SnO{sub 2} electrode compared to the value of 1.66% for the usual nano-particle SnO{sub 2} electrode. The improvement conversion efficiencies were mainly attributed to the formation of nano-grains, which facilitated the electron diffusion within the grains. The improved electrolyte diffusion as well as the light-scattering effects enhanced the photovoltaic performance of the SnO{sub 2} electrode. (author)
Energy Technology Data Exchange (ETDEWEB)
Zhao, Hang; Lu, Yinxiang, E-mail: yxlu@fudan.edu.cn
2016-01-30
Graphical abstract: - Highlights: • An etchant-free and moderate surface pre-treatment process was studied. • Citric acid, malic acid and oxalic acid were selected as modification agents. • High adhesive nickel coating on cuprammonium fabric was obtained. • The electromagnetic parameters were evaluated from the experimental data. - Abstract: Nickel films were grown on citric acid (CA), malic acid (MA) and oxalic acid (OA) modified cuprammonium fabric (CF) substrates via electroless nickel deposition. The nickel films were examined using scanning electron microscopy (SEM) and X-ray diffraction (XRD). Their individual deposition rate and electromagnetic interference (EMI) shielding effectiveness (SE) were also investigated to compare the properties of electroless nickel films. SEM images illustrated that the nickel film on MA modified CF substrate was smooth and uniform, and the density of nickel nuclei was much higher. Compared with that of CA modified CF, the coverage of nickel nuclei on OA and MA modified CF substrate was very limited and the nickel particles size was too big. XRD analysis showed that the nickel films deposited on the different modified CF substrates had a structure with Ni (1 1 1) preferred orientation. All the nickel coatings via different acid modification were firmly adhered to the CF substrates, as demonstrated by an ultrasonic washing test. The result of tensile test indicated that the electroless nickel plating on CF has ability to strengthen the CF substrate while causes limited effect on tensile elongation. Moreover, the nickel film deposited on MA modified CF substrate showed more predominant in EMI SE than that deposited on CA or OA modified CF.
Thermal Stress Behavior of Micro- and Nano-Size Aluminum Films
International Nuclear Information System (INIS)
Hanabusa, T.; Kusaka, K.; Nishida, M.
2008-01-01
In-situ observation of thermal stresses in thin films deposited on silicon substrate was made by X-ray and synchrotron radiation. Specimens prepared in this experiment were micro- and nano-size thin aluminum films with and without passivation film. The thickness of the film was 1 micrometer for micro-size films and 10, 20 and 50 nanometer for nano-size films. The stress measurement in micro-size films was made by X-ray radiation whereas the measurement of nano-size films was made by synchrotron radiation. Residual stress measurement revealed tensile stresses in all as-deposited films. Thermal stresses were measured in a series of heating- and cooling-stage. Thermal stress behavior of micro-size films revealed hysteresis loop during a heating and cooling process. The width of a hysteresis loop was larger in passivated film that unpassivated film. No hysteresis loops were observed in nano-size films with SiO 2 passivation. Strengthning mechanism in thin films was discussed on a passivation film and a film thickness
Energy Technology Data Exchange (ETDEWEB)
Miao, Yinbin [Argonne National Lab. (ANL), Argonne, IL (United States); Mo, Kun [Argonne National Lab. (ANL), Argonne, IL (United States); Jamison, Laura M. [Argonne National Lab. (ANL), Argonne, IL (United States); Lian, Jie [Rensselaer Polytechnic Inst., Troy, NY (United States); Yao, Tiankai [Rensselaer Polytechnic Inst., Troy, NY (United States); Bhattacharya, Sumit [Argonne National Lab. (ANL), Argonne, IL (United States); Northwestern Univ., Evanston, IL (United States)
2016-01-01
This activity is supported by the US Nuclear Energy Advanced Modeling and Simulation (NEAMS) Fuels Product Line (FPL) and aims at providing experimental data for the validation of the mesoscale simulation code MARMOT. MARMOT is a mesoscale multiphysics code that predicts the coevolution of microstructure and properties within reactor fuel during its lifetime in the reactor. It is an important component of the Moose-Bison-Marmot (MBM) code suite that has been developed by Idaho National Laboratory (INL) to enable next generation fuel performance modeling capability as part of the NEAMS Program FPL. In order to ensure the accuracy of the microstructure-based materials models being developed within the MARMOT code, extensive validation efforts must be carried out. In this report, we summarize the experimental efforts in FY16 including the following important experiments: (1) in-situ grain growth measurement of nano-grained UO2; (2) investigation of surface morphology in micrograined UO2; (3) Nano-indentation experiments on nano- and micro-grained UO2. The highlight of this year is: we have successfully demonstrated our capability to in-situ measure grain size development while maintaining the stoichiometry of nano-grained UO2 materials; the experiment is, for the first time, using synchrotron X-ray diffraction to in-situ measure grain growth behavior of UO2.
Nano Hydroxyapatite gel for removal of Nickel ions for environmental applications
International Nuclear Information System (INIS)
Abdelfattah, W.I.; Fayed, M.SH.; Gouda, SH.R.; Awwad, S.A.
2006-01-01
Hydroxyapatite (HAp) has been investigated for the removal of heavy metals in environmental application. However, little is known about the influences of surface modifications of the HAp. In the present study, nano HAp - polyvinyl alcohol gel was synthesized under ph control and the formed gel was used for removing nickel ions. The influence of nickel ions on the surface of HAp was studied. Reaction mechanisms were followed by ICP-MS and discussed via continuous variations method (CVM), mole ratio method (MRM) and slope ratio method (SRM). The formed gel with nickel ions was studied by various methods including UV, FTIR, XRD and SEM. The ICP-MS was used to analyze the supernatant solution to confirm the presence of Ca and / or Ni ions. The nickel ions were found to reduce the degree of crystallinity of the synthesized HAp phase. The present results indicated that nickel ions were completely adsorbed on the HAp structure with its anion. The validation of the nature of HAp gel as chelating agent or complex formation as well as physical sorption were discussed
SERS spectra of pyridine adsorbed on nickel film prepared by magnetron sputtering
Li, Daoyong; Ouyang, Yu; Chen, Li; Cao, Weiran; Shi, Shaohua
2011-02-01
As a repeating well and cheaper enhancement substrate, the nickel film was fabricated with magnetron sputtering coating instrument. Surface enhanced Raman spectra (SERS) of pyridine adsorbed on this nickel film are compared with the experimental values of gaseous pyridine, the theoretical value of pyridine solution listed in other literatures and our method is better than electro-chemical etching electrode method for large scale preparation. The enhancement factor of the nickel film is calculated and the result indicates that magnetron sputtering coating technology is feasible for obtaining good SERS active surface.
Energy Technology Data Exchange (ETDEWEB)
Charai, A. [Faculte des Sciences et Techniques de Saint Jerome, Lab. TECSEN, UMR 6122 du CNRS, 13 - Marseille (France); Kutcherinenko, I.; Priester, L. [Paris-11 Univ., ISMA, 91 - Orsay (France); Penisson, J.M. [CEA Grenoble, Dept. de Recherche Fondamentale sur la Matiere Condensee, DRFMC-SP2M, 38 (France); Pontikis, V. [Centre National de la Recherche Scientifique (CNRS), Centre d' Etudes de Chimie Metallurgique, 94 - Vitry-sur-Seine (France); Wolski, K. [Ecole NationaleSuperieure des Mines de Saint Etienne, Centre SMS/MPI, URA 1884 du CNRS, 42 - Saint Etienne (France); Vystavel, T. [Academy of Sciences of Czech Republic, Institute of Physics, Praha (Czech Republic)
2002-09-01
Understanding the mechanism of the intergranular penetration of a liquid phase into a metallic solid is an important problem. The structural and chemical characterization of nano-metric films at grain boundaries is now possible by using high resolution electron microscopy associated with X-ray micro-analysis, electron energy loss spectroscopy and Auger spectroscopy. In order to study this problem, two different classes of model materials were selected according to their crystallographic structure: a bcc metal (molybdenum) and an fcc one (nickel). The wetting element was either lead or tin or nickel. In a first approach, the metallic matrix was polycrystalline. The conditions in which the liquid phase penetrates into the grain boundaries were studied by using special preparation and observation techniques. In particular, the use of a Focused Ion Beam microscope (FIB) allowed the preparation of thin foils located very precisely inside the matrix as well as multi-scale observations. These specimens were further observed in electron microscopy with a very high resolution. (authors)
Energy Technology Data Exchange (ETDEWEB)
Diantoro, Markus, E-mail: markus.diantoro.fmipa@um.ac.id; Hidayati, Nisfi Nahari Sani; Latifah, Rodatul; Fuad, Abdulloh; Nasikhudin,; Sujito,; Hidayat, Arif [Department of Physics, Faculty of Mathematics and Natural Science, Universitas Negeri Malang, Jl. Semarang 5 Malang 65145 (Indonesia)
2016-03-11
Natural polymers can be extracted from leaf or stem of plants. Pterocarpus Indicus W. (PIW) and Jatropha Multifida L. (JIL) plants are good candidate as natural polymer sources. PIW and JIW polymers contain chemical compound so-called flavonoids which has C{sub 6}-C{sub 3}-C{sub 6} carbons conjugated configuration. The renewable type of polymer as well as their abundancy of flavonoid provide us to explore their physical properties. A number of research have been reported related to broad synthesis method and mechanical properties. So far there is no specific report of electrical conductivity associated to PIW and JIL natural polymers. In order to obtain electrical conductivity and its crystallinity of the extracted polymer films, it was induced on them a various fraction of silver nano particles. The film has been prepared by means of spin coating method on nickel substrate. It was revealed that FTIR spectra confirm the existing of rutine flavonoid. The crystallinity of the samples increase from 0.66%, to 4.11% associated to the respective various of silver fractions of 0.1 M to 0.5 M. SEM images show that there are some grains of silver in the film. The nature of electric conductivity increases a long with the addition of silver. The electrical conductivity increase significantly from 3.22 S/cm, to 542.85 S/cm. On the other hand, PIW films also shows similar trends that increase of Ag induce the increase its crystallinity as well as its electrical conductivity at semiconducting level. This result opens a prospective research and application of the green renewable polymer as optoelectronic materials.
Nano-Impact (Fatigue Characterization of As-Deposited Amorphous Nitinol Thin Film
Directory of Open Access Journals (Sweden)
Rehan Ahmed
2012-08-01
Full Text Available This paper presents nano-impact (low cycle fatigue behavior of as-deposited amorphous nitinol (TiNi thin film deposited on Si wafer. The nitinol film was 3.5 µm thick and was deposited by the sputtering process. Nano-impact tests were conducted to comprehend the localized fatigue performance and failure modes of thin film using a calibrated nano-indenter NanoTest™, equipped with standard diamond Berkovich and conical indenter in the load range of 0.5 mN to 100 mN. Each nano-impact test was conducted for a total of 1000 fatigue cycles. Depth sensing approach was adapted to understand the mechanisms of film failure. Based on the depth-time data and surface observations of films using atomic force microscope, it is concluded that the shape of the indenter test probe is critical in inducing the localized indentation stress and film failure. The measurement technique proposed in this paper can be used to optimize the design of nitinol thin films.
Chemical formation of palladium-free surface-nickelized polyimide film for flexible electronics
International Nuclear Information System (INIS)
Hsiao, Y.-S.; Whang, W.-T.; Wu, S.-C.; Chuang, Kuen-Ru
2008-01-01
Flexible polyimide (PI) films for flexible electronics were surface-nickelized using a fully solution-based process and excellent adhesion between the nickel and polyimide phases was observed. Polyimide substrates were modified by alkaline hydrolysis, ion exchange, reduction and nickel electroless deposition without palladium. Atomic force microscopy and field emission scanning electron microscopy were used to follow the growth of nickel nanoparticles (Ni-NPs) and nickel layers on the polyimide surface. The surface resistances of the Ni-NPs/PI films and Ni/PI films, measured using a four-point probe, were 1.6 x 10 7 and 0.83 Ω/cm 2 , respectively. The thicknesses of Ni-NPs and the Ni layer on the polyimide surface were 82 nm and 382 nm, respectively, as determined by transmission electron microscopy, and the Ni layer adhered well to PI, as determined by the adhesive tape testing method
Sputtering of nano-grains by energetic ions
Bringa, E M
2002-01-01
Sputtering from grains with a size of tens of nanometers is important in a number of astrophysical environments having a variety of plasma properties and can have applications in nano-technology. Since energy deposition by incident ions or electrons can create 'hot' regions in a small grain, thermal spike (TS) models have been applied to estimate the sputtering. The excitations produced by a fast ion are often assumed to form a 'hot' cylindrical track. In this paper we use molecular dynamics (MD) calculations to describe the energy transport and sputtering due to the creation of a 'hot' track in a grain with one quarter million atoms. We show the enhancement due to grain size and find that TS models work over a limited range of excitation densities. Discrepancies of several orders of magnitude are found when comparing our MD results for sputtering of small dust grains to those obtained by the astrophysical community using spike models.
International Nuclear Information System (INIS)
Wang, H.M.; Jiang, J.S.; Huang, Z.Y.; Chen, Y.; Liu, K.; Lu, Z.W.; Qi, J.Q.; Li, F.; He, D.W.; Lu, T.C.; Wang, Q.Y.
2016-01-01
Nano-grained ceramics have their unique mechanical characteristics that are not commonly found in their coarse-grained counterparts. In this study, nano-grained YAG transparent ceramics (NG-YAG) were prepared by low-temperature high-pressure technique (LTHP). The peak profile analysis of the X-ray diffraction was employed to investigate the compressive yield strength of NG-YAG. During the temperature at 450 °C, the residual micro-strain (RMS) increased with increasing loading pressure. However when the loading pressure was exceeded to 4.0 GPa the RMS exhibited a severe negative slop. The temperature effects on the compressive yield strength were also studied. It shows that the compressive yield strength of NG-YAG is 4.0 GPa and 5.0 GPa respectively at 450 °C and 350 °C. More importantly according to this investigation, a feasible technique to study the nano-grained ceramics is provided. - Graphical abstract: Fig. 2 shows the significant slope changes of calculated residual micro-strain (RMS) associated with five selected pressure-temperature conditions. Another the grain size estimated from Scherrer's formula, especially when it changes with the pressure-temperature condition is also plotted in Fig. 2. - Highlights: • Prepared the nano-grained YAG transparent ceramic by high pressure technique. • Obtained the compressive yield with different temperature. • Obtained the compressive yield of nano-grained YAG transparent ceramic.
Energy Technology Data Exchange (ETDEWEB)
Muñoz, Alexandra; Costa, Max, E-mail: Max.Costa@nyumc.org
2012-04-01
Nickel (Ni) is a worldwide pollutant and contaminant that humans are exposed to through various avenues resulting in multiple toxic responses — most alarming is its clear carcinogenic nature. A variety of particulate Ni compounds persist in the environment and can be distinguished by characteristics such as solubility, structure, and surface charge. These characteristics influence cellular uptake and toxicity. Some particulate forms of Ni are carcinogenic and are directly and rapidly endocytized by cells. A series of studies conducted in the 1980s observed this process, and we have reanalyzed the results of these studies to help elucidate the molecular mechanism of particulate Ni uptake. Originally the process of uptake observed was described as phagocytosis, however in the context of recent research we hypothesize that the process is macropinocytosis and/or clathrin mediated endocytosis. Primary considerations in determining the route of uptake here include calcium dependence, particle size, and inhibition through temperature and pharmacological approaches. Particle characteristics that influenced uptake include size, charge, surface characteristics, and structure. This discussion is relevant in the context of nanoparticle studies and the emerging interest in nano-nickel (nano-Ni), where toxicity assessments require a clear understanding of the parameters of particulate uptake and where establishment of such parameters is often obscured through inconsistencies across experimental systems. In this regard, this review aims to carefully document one system (particulate nickel compound uptake) and characterize its properties.
Antibacterial Properties of Titanate Nano fiber Thin Films Formed on a Titanium Plate
International Nuclear Information System (INIS)
Yada, M.; Inoue, Y.; Morita, T.; Torikai, T.; Watari, T.; Noda, I.; Hotokebuchi, T.
2013-01-01
A sodium titanate nano fiber thin film and a silver nanoparticle/silver titanate nano fiber thin film formed on the surface of a titanium plate exhibited strong antibacterial activities against methicillin-resistant Staphylococcus aureus, which is one of the major bacteria causing in-hospital infections. Exposure of the sodium titanate nano fiber thin film to ultraviolet rays generated a high antibacterial activity due to photo catalysis and the sodium titanate nano fiber thin film immediately after its synthesis possessed a high antibacterial activity even without exposure to ultraviolet rays. Elution of silver from the silver nanoparticle/silver titanate nano fiber thin film caused by the silver ion exchange reaction was considered to contribute substantially to the strong antibacterial activity. The titanate nano fiber thin films adhered firmly to titanium. Therefore, these titanate nano fiber thin film/titanium composites will be extremely useful as implant materials that have excellent antibacterial activities.
Study of the nickel-fullerene nano-structured thin films
Czech Academy of Sciences Publication Activity Database
Vacík, Jiří; Naramoto, H.; Narumi, K.; Yamamoto, S.; Abe, H.
2004-01-01
Roč. 219, č. 20 (2004), s. 862-866 ISSN 0168-583X Institutional research plan: CEZ:AV0Z1048901 Keywords : nickel * fullerene * magnesium oxide Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.997, year: 2004
Bulletin of Materials Science | Indian Academy of Sciences
Indian Academy of Sciences (India)
Precursor solutions of cobalt/nickel incorporated nano-grain zirconia films were prepared from aquo-organic solutions of zirconium oxychloride octahydrate and corresponding transition metal nitrate. The films were deposited onto silica glass substrate by the dipping technique. Annealing was made at different temperatures ...
International Nuclear Information System (INIS)
Charai, A.; Kutcherinenko, I.; Priester, L.; Penisson, J.M.; Pontikis, V.; Wolski, K.; Vystavel, T.
2002-01-01
Understanding the mechanism of the intergranular penetration of a liquid phase into a metallic solid is an important problem. The structural and chemical characterization of nano-metric films at grain boundaries is now possible by using high resolution electron microscopy associated with X-ray micro-analysis, electron energy loss spectroscopy and Auger spectroscopy. In order to study this problem, two different classes of model materials were selected according to their crystallographic structure: a bcc metal (molybdenum) and an fcc one (nickel). The wetting element was either lead or tin or nickel. In a first approach, the metallic matrix was polycrystalline. The conditions in which the liquid phase penetrates into the grain boundaries were studied by using special preparation and observation techniques. In particular, the use of a Focused Ion Beam microscope (FIB) allowed the preparation of thin foils located very precisely inside the matrix as well as multi-scale observations. These specimens were further observed in electron microscopy with a very high resolution. (authors)
Grain-size distributions and grain boundaries of chalcopyrite-type thin films
International Nuclear Information System (INIS)
Abou-Ras, D.; Schorr, S.; Schock, H.W.
2007-01-01
CuInSe 2 , CuGaSe 2 , Cu(In,Ga)Se 2 and CuInS 2 thin-film solar absorbers in completed solar cells were studied in cross section by means of electronbackscatter diffraction. From the data acquired, grain-size distributions were extracted, and also the most frequent grain boundaries were determined. The grain-size distributions of all chalcopyrite-type thin films studied can be described well by lognormal distribution functions. The most frequent grainboundary types in these thin films are 60 - left angle 221 right angle tet and 71 - left angle 110 right angle tet (near) Σ3 twin boundaries. These results can be related directly to the importance of {112} tet planes during the topotactical growth of chalcopyrite-type thin films. Based on energetic considerations, it is assumed that the most frequent twin boundaries exhibit a 180 - left angle 221 right angle tet constellation. (orig.)
Ultra High Electrical Performance of Nano Nickel Oxide and Polyaniline Composite Materials
Directory of Open Access Journals (Sweden)
Xiaomin Cai
2017-07-01
Full Text Available The cooperative effects between the PANI (polyaniline/nano-NiO (nano nickel oxide composite electrode material and redox electrolytes (potassium iodide, KI for supercapacitor applications was firstly discussed in this article, providing a novel method to prepare nano-NiO by using β-cyelodextrin (β-CD as the template agent. The experimental results revealed that the composite electrode processed a high specific capacitance (2122.75 F·g−1 at 0.1 A·g−1 in 0.05 M KI electrolyte solution, superior energy density (64.05 Wh·kg−1 at 0.2 A·g−1 in the two-electrode system and excellent cycle performance (86% capacitance retention after 1000 cycles at 1.5 A·g−1. All those ultra-high electrical performances owe to the KI active material in the electrolyte and the PANI coated nano-NiO structure.
Torres, E.; Pencer, J.
2018-04-01
Helium impurities, from either direct implantation or transmutation reactions, have been associated with embrittlement in nickel-based alloys. Helium has very low solubility in nickel, and has been found to aggregate at lattice defects such as vacancies, dislocations, and grain boundaries. The retention and precipitation of helium in nickel-based alloys have deleterious effects on the material mechanical properties. However, the underlying mechanisms that lead to helium effects in the host metal are not fully understood. In the present work, we investigate the role of symmetric tilt grain boundary (STGB) structures on the distribution of helium in nickel using molecular dynamics simulations. We investigate the family of STGBs specific to the 〈 110 〉 tilt axis. The present results indicate that accumulation of helium at the grain boundary may be modulated by details of grain boundary geometry. A plausible correlation between the grain boundary energy and misorientation with the accumulation and mobility of helium is proposed. Small clusters with up to 6 helium atoms show significant interstitial mobility in the nickel bulk, but also become sites for nucleation and grow of more stable helium clusters. High-energy GBs are found mainly populated with small helium clusters. The high mobility of small clusters along the GBs indicates the role of these GBs as fast two-dimensional channels for diffusion. In contrast, the accumulation of helium in large helium clusters at low-energy STGB creates a favorable environment for the formation of large helium bubbles, indicating a potential role for low-energy STGB in promoting helium-induced GB embrittlement.
Stripe domains and magnetoresistance in thermally deposited nickel films
International Nuclear Information System (INIS)
Sparks, P.D.; Stern, N.P.; Snowden, D.S.; Kappus, B.A.; Checkelsky, J.G.; Harberger, S.S.; Fusello, A.M.; Eckert, J.C.
2004-01-01
We report a study of the domain structure and magnetoresistance of thermally deposited nickel films. For films thicker than 17 nm, we observe striped domains with period varying with film thickness as a power law with exponent 0.21±0.02 up to 120 nm thickness. There is a negative magnetoresistance for fields out of the plane
Stripe domains and magnetoresistance in thermally deposited nickel films
Sparks, P. D.; Stern, N. P.; Snowden, D. S.; Kappus, B. A.; Checkelsky, J. G.; Harberger, S. S.; Fusello, A. M.; Eckert, J. C.
2004-05-01
We report a study of the domain structure and magnetoresistance of thermally deposited nickel films. For films thicker than 17nm, we observe striped domains with period varying with film thickness as a power law with exponent 0.21+/-0.02 up to 120nm thickness. There is a negative magnetoresistance for fields out of the plane.
Stripe domains and magnetoresistance in thermally deposited nickel films
Energy Technology Data Exchange (ETDEWEB)
Sparks, P.D. E-mail: sparks@hmc.edu; Stern, N.P.; Snowden, D.S.; Kappus, B.A.; Checkelsky, J.G.; Harberger, S.S.; Fusello, A.M.; Eckert, J.C
2004-05-01
We report a study of the domain structure and magnetoresistance of thermally deposited nickel films. For films thicker than 17 nm, we observe striped domains with period varying with film thickness as a power law with exponent 0.21{+-}0.02 up to 120 nm thickness. There is a negative magnetoresistance for fields out of the plane.
Grain-resolved analysis of localized deformation in nickel-titanium wire under tensile load.
Sedmák, P; Pilch, J; Heller, L; Kopeček, J; Wright, J; Sedlák, P; Frost, M; Šittner, P
2016-08-05
The stress-induced martensitic transformation in tensioned nickel-titanium shape-memory alloys proceeds by propagation of macroscopic fronts of localized deformation. We used three-dimensional synchrotron x-ray diffraction to image at micrometer-scale resolution the grain-resolved elastic strains and stresses in austenite around one such front in a prestrained nickel-titanium wire. We found that the local stresses in austenite grains are modified ahead of the nose cone-shaped buried interface where the martensitic transformation begins. Elevated shear stresses at the cone interface explain why the martensitic transformation proceeds in a localized manner. We established the crossover from stresses in individual grains to a continuum macroscopic internal stress field in the wire and rationalized the experimentally observed internal stress field and the topology of the macroscopic front by means of finite element simulations of the localized deformation. Copyright © 2016, American Association for the Advancement of Science.
Use of 2-hydroxylhydrazine as a new modifier in dip-coating nickel films
International Nuclear Information System (INIS)
Syukri, R.; Ito, Yusuke; Ban, Takayuki; Ohya, Yutaka; Takahashi, Yasutaka
2002-01-01
A modified version of the dip-coating technique, which uses 2-hydroxylhydrazine as a mild reducing agent, was applied in the fabrication of nickel thin films. Nickel acetate was used as metal source. Metallic nickel thin films were formed on glass substrates by firing in the range of 400-600 deg. C under nitrogen atmosphere. The deposited layers were composed of cubic Ni crystallites. X-ray photoelectron spectroscopy analysis indicated almost uniformity in composition throughout the film thickness. The morphology of the films analyzed by scanning electron microscopy and atomic force microscopy revealed a very weak roughness after firing at 400 deg. C and the films turned out to be homogeneous. A thin film of approximately 19 nm in thickness exhibited a high resistivity of 86 μΩ cm. However, the resistivity was found to gradually decrease with increasing film thickness up to 110 nm by repeated dip-coating, reaching a minimum value of approximately 10 μΩ cm
Sontu, Uday Bhasker; G, Narsinga Rao; Chou, F. C.; M, V. Ramana Reddy
2018-04-01
Spinel ferrites have come a long way in their versatile applications. The ever growing applications of these materials demand detailed study of material properties and environmental considerations in their synthesis. In this article, we report the effect of temperature and applied magnetic field strength on the magnetic behavior of the cobalt nickel ferrite nano powder samples. Basic structural properties of spinel ferrite nano particles, that are synthesized by an environmentally benign method of auto combustion, are characterized through XRD, TEM, RAMAN spectroscopy. Diffuse Reflectance Spectroscopy (DRS) is done to understand the nickel substitution effect on the optical properties of cobalt ferrite nano particles. Thermo magnetic studies using SQUID in the temperature range 5 K to 400 K and room temperature (300 K) VSM studies are performed on these samples. Fields of 0Oe (no applied field: ZF), 1 kOe (for ZFC and FC curves), 5 kOe (0.5 T), 50 kOe (5T) (for M-H loop study) are used to study the magnetic behavior of these nano particles. The XRD,TEM analysis suggest 40 nm crystallites that show changes in the cation distribution and phase changes in the spinel structure with nickel substitution. Raman micrographs support phase purity changes and cation redistributions with nickel substitution. Diffuse reflectance study on powder samples suggests two band gap values for nickel rich compounds. The Magnetic study of these sample nano particles show varied magnetic properties from that of hard magnetic, positive multi axial anisotropy and single-magnetic-domain structures at 5 K temperature to soft magnetic core shell like structures at 300 K temperature. Nickel substitution effect is non monotonous. Blocking temperature of all the samples is found to be higher than the values suggested in the literature.
Self-assembled metal nano-multilayered film prepared by co-sputtering method
Xie, Tianle; Fu, Licai; Qin, Wen; Zhu, Jiajun; Yang, Wulin; Li, Deyi; Zhou, Lingping
2018-03-01
Nano-multilayered film is usually prepared by the arrangement deposition of different materials. In this paper, a self-assembled nano-multilayered film was deposited by simultaneous sputtering of Cu and W. The Cu/W nano-multilayered film was accumulated by W-rich layer and Cu-rich layer. Smooth interfaces with consecutive composition variation and semi-coherent even coherent relationship were identified, indicating that a spinodal-like structure with a modulation wavelength of about 20 nm formed during co-deposition process. The participation of diffusion barrier element, such as W, is believed the essential to obtain the nano-multilayered structure besides the technological parameters.
Estimation of images degraded by film-grain noise.
Naderi, F; Sawchuk, A A
1978-04-15
Film-grain noise describes the intrinsic noise produced by a photographic emulsion during the process of image recording and reproduction. In this paper we consider the restoration of images degraded by film-grain noise. First a detailed model for the over-all photographic imaging system is presented. The model includes linear blurring effects and the signal-dependent effect of film-grain noise. The accuracy of this model is tested by simulating images according to it and comparing the results to images of similar targets that were actually recorded on film. The restoration of images degraded by film-grain noise is then considered in the context of estimation theory. A discrete Wiener filer is developed which explicitly allows for the signal dependence of the noise. The filter adaptively alters its characteristics based on the nonstationary first order statistics of an image and is shown to have advantages over the conventional Wiener filter. Experimental results for modeling and the adaptive estimation filter are presented.
International Nuclear Information System (INIS)
Garole, Dipak J.; Tetgure, Sandesh R.; Borse, Amulrao U.; Yogesh R Toda; Vaman J Garole; Babasaheb R Sankapal; Prashant K Baviskar
2015-01-01
This paper reports the novel synthesis of uranyl sulphide (UO_2S) thin films using the successive ionic layer adsorption and reaction (SILAR) technique at room temperature. Cationic exchange reaction was used to convert uranyl sulphide (UO_2S) to silver sulphide (Ag_2S). The influence of concentration variation on the structural and optical properties of UO_2S and Ag_2S thin films was investigated. The structural, surface morphological, elemental analysis and optical absorption studies were performed. Structural studies revealed that all the deposited films were nano-sized and amorphous in nature. Surface morphology showed that all the grains were spherical and granular in nature and grains got conglomerated to form a large particle. Also, the variations of the optical band gap and the width of the tail of localized states were represented as a function of various parameters. (authors)
Energy Technology Data Exchange (ETDEWEB)
Muslim, Noormariah, E-mail: 14h8702@ubd.edu.bn [Centre for Advanced Material and Energy Sciences, Universiti Brunei Darussalam, Jalan Tungku Link, Gadong BE1410 (Brunei Darussalam); Soon, Ying Woan [Centre for Advanced Material and Energy Sciences, Universiti Brunei Darussalam, Jalan Tungku Link, Gadong BE1410 (Brunei Darussalam); Physical and Geological Sciences, Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, Gadong BE1410 (Brunei Darussalam); Lim, Chee Ming; Voo, Nyuk Yoong [Centre for Advanced Material and Energy Sciences, Universiti Brunei Darussalam, Jalan Tungku Link, Gadong BE1410 (Brunei Darussalam)
2016-08-01
Pure nickel (Ni) thin films of thicknesses of 100 nm were deposited on glass substrates by radio frequency magnetron sputtering at a power of 100 W and at various substrate temperatures i.e., room temperature, 100, 200, and 300 °C. The crystalline structure, surface topography, surface morphology, electrical resistivity, and optical properties of the deposited films were studied. The properties of the Ni films could be controlled by altering the substrate temperature. Specifically, the films featured a face-centered cubic crystalline structure with predominant (111) crystallite orientation at all the substrate temperatures employed, as observed from the X-ray diffraction analysis. Films deposited at substrate temperatures greater than 200 °C additionally displayed crystalline (200) and (220) diffraction peaks. The surface morphology analysis revealed that the grain size of the Ni thin films increased with increasing substrate temperatures employed. This increase was accompanied with a decrease in the resistivity of the Ni films. The surface roughness of the films increased with increasing substrate temperatures employed, as observed from the atomic force microscopy analysis. - Highlights: • RF magnetron sputtering is a good alternative method to deposit Ni films. • Properties of Ni films could be controlled simply by tuning substrate temperatures. • Crystallite size and surface roughness increased with substrate temperatures. • Electrical resistivity reduced with increasing substrate temperatures. • Optical properties also changed with substrate temperatures.
International Nuclear Information System (INIS)
Jinlong, Lv; Tongxiang, Liang; Chen, Wang
2016-01-01
Graphical abstract: - Highlights: • Improved HER efficiency of Ni-Mo coatings was attributed to ‘cauliflower’ like microstructure. • RGO in nickel-RGO composite coating promoted refined grain and facilitated HER. • Synergistic effect between nickel and RGO facilitated HER due to large specific surface of RGO. - Abstract: The nickel, nickel-molybdenum alloy, nickel-graphite and nickel-reduced graphene oxide composite coatings were obtained by the electrodeposition technique from a nickel sulfate bath. Nanocrystalline molybdenum, graphite and reduced graphene oxide in nickel coatings promoted hydrogen evolution reaction in 0.5 M H_2SO_4 solution at room temperature. However, the nickel-reduced graphene oxide composite coating exhibited the highest electrocatalytic activity for the hydrogen evolution reaction in 0.5 M H_2SO_4 solution at room temperature. A large number of gaps between ‘cauliflower’ like grains could decrease effective area for hydrogen evolution reaction in slight amorphous nickel-molybdenum alloy. The synergistic effect between nickel and reduced graphene oxide promoted hydrogen evolution, moreover, refined grain in nickel-reduced graphene oxide composite coating and large specific surface of reduced graphene oxide also facilitated hydrogen evolution reaction.
Energy Technology Data Exchange (ETDEWEB)
Jinlong, Lv, E-mail: ljlbuaa@126.com [Beijing Key Laboratory of Fine Ceramics, Institute of Nuclear and New Energy Technology, Tsinghua University, Zhongguancun Street, Haidian District, Beijing 100084 (China); State Key Lab of New Ceramic and Fine Processing, Tsinghua University, Beijing 100084 (China); Tongxiang, Liang; Chen, Wang [Beijing Key Laboratory of Fine Ceramics, Institute of Nuclear and New Energy Technology, Tsinghua University, Zhongguancun Street, Haidian District, Beijing 100084 (China); State Key Lab of New Ceramic and Fine Processing, Tsinghua University, Beijing 100084 (China)
2016-03-15
Graphical abstract: - Highlights: • Improved HER efficiency of Ni-Mo coatings was attributed to ‘cauliflower’ like microstructure. • RGO in nickel-RGO composite coating promoted refined grain and facilitated HER. • Synergistic effect between nickel and RGO facilitated HER due to large specific surface of RGO. - Abstract: The nickel, nickel-molybdenum alloy, nickel-graphite and nickel-reduced graphene oxide composite coatings were obtained by the electrodeposition technique from a nickel sulfate bath. Nanocrystalline molybdenum, graphite and reduced graphene oxide in nickel coatings promoted hydrogen evolution reaction in 0.5 M H{sub 2}SO{sub 4} solution at room temperature. However, the nickel-reduced graphene oxide composite coating exhibited the highest electrocatalytic activity for the hydrogen evolution reaction in 0.5 M H{sub 2}SO{sub 4} solution at room temperature. A large number of gaps between ‘cauliflower’ like grains could decrease effective area for hydrogen evolution reaction in slight amorphous nickel-molybdenum alloy. The synergistic effect between nickel and reduced graphene oxide promoted hydrogen evolution, moreover, refined grain in nickel-reduced graphene oxide composite coating and large specific surface of reduced graphene oxide also facilitated hydrogen evolution reaction.
Chemically grown, porous, nickel oxide thin-film for electrochemical supercapacitors
Energy Technology Data Exchange (ETDEWEB)
Inamdar, A.I.; Kim, YoungSam; Im, Hyunsik [Department of Semiconductor Science, Dongguk University, Seoul 100-715 (Korea, Republic of); Pawar, S.M.; Kim, J.H. [Department of Materials Science and Engineering, Chonnam National University, Gwangju 500-757 (Korea, Republic of); Kim, Hyungsang [Department of Physics, Dongguk University, Seoul 100-715 (Korea, Republic of)
2011-02-15
A porous nickel oxide film is successfully synthesized by means of a chemical bath deposition technique from an aqueous nickel nitrate solution. The formation of a rock salt NiO structure is confirmed with XRD measurements. The electrochemical supercapacitor properties of the nickel oxide film are examined using cyclic voltammetery (CV), galvanostatic and impedance measurements in two different electrolytes, namely, NaOH and KOH. A specific capacitance of {proportional_to}129.5 F g{sup -1} in the NaOH electrolyte and {proportional_to}69.8 F g{sup -1} in the KOH electrolyte is obtained from a cyclic voltammetery study. The electrochemical stability of the NiO electrode is observed for 1500 charge-discharge cycles. The capacitative behaviour of the NiO electrode is confirmed from electrochemical impedance measurements. (author)
International Nuclear Information System (INIS)
Vidales-Hurtado, M.A.; Mendoza-Galvan, A.
2008-01-01
Nickel oxide-based thin films were obtained using the chemical bath deposition method on glass and silicon substrates. The precursor solution used was a mixture of nickel nitrate, urea, and deionized water. Molar concentration of nickel (0.3-1.0 M), deposition time, and immersing cycles were considered as deposition variables. Infrared spectroscopy and X-ray diffraction data reveal that all as-deposited films correspond to the transparent turbostratic phase α(II)-Ni(OH) 2 . However, the rate of deposition depends on nickel content in the solution. After annealing in air at temperatures above of 300 deg. C, the films are transformed to the NiO phase and show a grey/black color. In these films, scanning electron microscopy images show aggregates of thin stacked sheets on their surface, such aggregates can be easily removed leaving only a thin NiO layer of about 30 nm adhered firmly to the substrate, regardless of nickel concentration in the solution and deposition time. In order to obtain thicker NiO films with good optical properties a procedure is developed performing several immersing-annealing cycles
Film grain synthesis and its application to re-graining
Schallauer, Peter; Mörzinger, Roland
2006-01-01
Digital film restoration and special effects compositing require more and more automatic procedures for movie regraining. Missing or inhomogeneous grain decreases perceived quality. For the purpose of grain synthesis an existing texture synthesis algorithm has been evaluated and optimized. We show that this algorithm can produce synthetic grain which is perceptually similar to a given grain template, which has high spatial and temporal variation and which can be applied to multi-spectral images. Furthermore a re-grain application framework is proposed, which synthesises based on an input grain template artificial grain and composites this together with the original image content. Due to its modular approach this framework supports manual as well as automatic re-graining applications. Two example applications are presented, one for re-graining an entire movie and one for fully automatic re-graining of image regions produced by restoration algorithms. Low computational cost of the proposed algorithms allows application in industrial grade software.
Investigation of growth, coverage and effectiveness of plasma assisted nano-films of fluorocarbon
International Nuclear Information System (INIS)
Joshi, Pratik P.; Pulikollu, Rajasekhar; Higgins, Steven R.; Hu Xiaoming; Mukhopadhyay, S.M.
2006-01-01
Plasma-assisted functional films have significant potential in various engineering applications. They can be tailored to impart desired properties by bonding specific molecular groups to the substrate surface. The aim of this investigation was to develop a fundamental understanding of the atomic level growth, coverage and functional effectiveness of plasma nano-films on flat surfaces and to explore their application-potential for complex and uneven shaped nano-materials. In this paper, results on plasma-assisted nano-scale fluorocarbon films, which are known for imparting inertness or hydrophobicity to the surface, will be discussed. The film deposition was studied as a function of time on flat single crystal surfaces of silicon, sapphire and graphite, using microwave plasma. X-ray photoelectron spectroscopy (XPS) was used for detailed study of composition and chemistry of the substrate and coating atoms, at all stages of deposition. Atomic force microscopy (AFM) was performed in parallel to study the coverage and growth morphology of these films at each stage. Combined XPS and AFM results indicated complete coverage of all the substrates at the nanometer scale. It was also shown that these films grew in a layer-by-layer fashion. The nano-films were also applied to complex and uneven shaped nano-structured and porous materials, such as microcellular porous foam and nano fibers. It was seen that these nano-films can be a viable approach for effective surface modification of complex or uneven shaped nano-materials
Action of colloidal silica films on different nano-composites
Directory of Open Access Journals (Sweden)
S. Abdalla
Full Text Available Nano-composite films have been the subject of extensive work to develop the energy-storage efficiency of electrostatic capacitors. Factors such as polymer purity, nano-particles size, and film morphology drastically affect the electrostatic efficiency of the dielectric material that form an insulating film between conductive electrodes of a capacitor. This in turn affects the energy storage performance of the capacitor. In the present work, we have studied the dielectric properties of 4 high pure amorphous polymer films: polymethylmethacrylate (PMMA, polystyrene, polyimide and poly-4-vinylpyridine. Comparison between the dielectric properties of these polymers has revealed that the higher break down performance is a character of polyimide PI and PMMA. Also, our experimental data shows that adding colloidal silica to PMMA and PI leads to a net decrease in the dielectric properties compared to the pure polymer. Keywords: Dielectric break down, Polymers, Nano-composite, Colloidal silica
Mechanical properties and microstructure of nano grain nickel alloy deposit
International Nuclear Information System (INIS)
Seo, Moo Hong; Kim, Jung Su; Kim, Seung Ho; Jung, Hyun Kyu; Wyi, Jung Il; Hwang, Woon Suk; Jang, Si Sung; Chun, Byung Sun
2003-01-01
In this study, Ni-P layers were electroplated on the surface of stainless steel in order to investigate the effects of an additive and agitation on their mechanical properties and microstructure. The concentration of the additive in the plating solution increased, the pores formed in the layer decreased, while the residual stress developed in the layers during electroplating increased. Agitation of the solution during electroplating was observed to force to increase local pores in the layer which lowers its tensile properties. Grain growth was suppressed due to very fine Ni 3 P precipitates formed at its grain boundaries during heat treatment at 343 .deg. C for 1 hr in air
X-ray specular reflection and fluorescence study of nano-films
International Nuclear Information System (INIS)
Zheludeva, S.; Novikova, N.
2001-01-01
The techniques that combine the advantages of high-resolution structure sensitive x-ray methods with spectroscopic selectivity of data obtained are shown to be extremely promising for characterization of organic and inorganic nano films and nano structures. Fluorescence yield angular dependences exited by complicated evanescent wave / x-ray standing wave pattern at total reflection and glancing incidence can be used to detect structure position of different ions in organic systems and alien interfacial layers in inorganic multilayers;, to get information about interdiffusion at the interfaces of Langmuir- Blodgett (L-B) films and artificial inorganic - x-ray mirrors; to study ion permeation through L-B nano structures - models of biomembrans; to obtain nano - film thickness and density; to get precisely the parameters of small d-space multilayer mirrors, ets
Directory of Open Access Journals (Sweden)
Hae-Min Lee
2014-01-01
Full Text Available Manganese-nickel (Mn-Ni oxide films were electrodeposited on a graphite sheet in a bath consisting of manganese acetate and nickel chloride, and the structural, morphological, and electrochemical properties of these films were investigated. The electrodeposited Mn-Ni oxide films had porous structures covered with nanofibers. The X-ray diffractometer pattern revealed the presence of separate manganese oxide (g-MnO2 and nickel oxide (NiO in the films. The electrodeposited Mn-Ni oxide electrode exhibited a specific capacitance of 424 F/g in Na2SO4 electrolyte. This electrode maintained 86% of its initial specific capacitance over 2000 cycles of the charge-discharge operation, showing good cycling stability.
Subtle Raman signals from nano-diamond and β-SiC thin films
International Nuclear Information System (INIS)
Kuntumalla, Mohan Kumar; Ojha, Harish; Srikanth, Vadali Venkata Satya Siva
2013-01-01
Micro Raman scattering experiments are carried out in pursuit of subtle but discernable signals from nano-diamond and β-SiC thin films. The thin films are synthesized using microwave plasma assisted chemical vapor deposition technique. Raman scattering experiments in conjunction with scanning electron microscopy and x-ray diffraction were carried out to extract microstructure and phase information of the above mentioned thin films. Certain subtle Raman signals have been identified in this work. In the case of nanodiamond thin films, Raman bands at ∼ 485 and ∼ 1220 cm −1 are identified. These bands have been assigned to the nanodiamond present in nanodiamond thin films. In the case of nano β-SiC thin films, optical phonons are identified using surface enhanced Raman scattering. - Highlights: ► Subtle Raman signals from nano-diamond and β-silicon carbide related thin films. ► Raman bands at ∼ 485 and ∼ 1220 cm −1 from nanodiamond thin films are identified. ► Longitudinal optical phonon from nano β-silicon carbide thin films is identified
Yu, Qian; Zhou, Tianfeng; Jiang, Yonggang; Yan, Xing; An, Zhonglie; Wang, Xibin; Zhang, Deyuan; Ono, Takahito
2018-03-01
To improve the mechanical properties of nickel-phosphorus (Ni-P) mold material for glass molding, an ultrasonic-assisted electroless plating method is proposed for the synthesis of graphene-enhanced nickel-phosphorus (G-Ni-P) composite films on heat-resistant stainless steel (06Cr25Ni20). Graphene flakes are prepared by an electrochemical exfoliation method. The surface roughness of the as-plated G-Ni-P composite plating is Ra 2.84 μm, which is higher than that of the Ni-P plating deposited using the same method. After annealing at 400 ºC for 2 h, the main phase of the G-Ni-P composite is transformed to crystalline Ni3P with an average grain size of 32.8 nm. The Vickers hardness and Young's modulus of the G-Ni-P composite are increased by 8.0% and 8.2% compared with the values of Ni-P, respectively. The detailed plating process is of great significance for the fabrication of G-Ni-P mold materials with enhanced mechanical properties.
Liu, Lifeng
2013-11-01
Nano-aggregates of cobalt nickel oxysulfide (CoNi)OxSy have been synthesized by hydrothermal processing and exhibited specific and areal capacitance as high as 592 F g-1 and 1628 mF cm-2, respectively, at a current density of 0.5 A g-1/1.375 mA cm-2. They also show high capacitance retention upon extended cycling at high rates.Nano-aggregates of cobalt nickel oxysulfide (CoNi)OxSy have been synthesized by hydrothermal processing and exhibited specific and areal capacitance as high as 592 F g-1 and 1628 mF cm-2, respectively, at a current density of 0.5 A g-1/1.375 mA cm-2. They also show high capacitance retention upon extended cycling at high rates. Electronic supplementary information (ESI) available: Experimental details; supplementary tables. See DOI: 10.1039/c3nr03533f
Dynamic studies of nano-confined polymer thin films
Geng, Kun
Polymer thin films with the film thickness (h0 ) below 100 nm often exhibit physical properties different from the bulk counterparts. In order to make the best use of polymer thin films in applications, it is important to understand the physical origins of these deviations. In this dissertation, I will investigate how different factors influence dynamic properties of polymer thin films upon nano-confinement, including glass transition temperature (Tg), effective viscosity (etaeff) and self-diffusion coefficient (D ). The first part of this dissertation concerns the impacts of the molecular weight (MW) and tacticity on the Tg's of nano-confined polymer films. Previous experiments showed that the Tg of polymer films could be depressed or increased as h0 decreases. While these observations are usually attributed to the effects of the interfaces, some experiments suggested that MW's and tacticities might also play a role. To understand the effects of these factors, the Tg's of silica-based poly(alpha-methyl styrene) (PalphaMS/SiOx) and poly(methyl methacrylate) (PMMA/SiOx) thin films were studied, and the results suggested that MW's and tacticities influence Tg in nontrivial ways. The second part concerns an effort to resolve the long-standing controversy about the correlation between different dynamics of polymer thin films upon nano-confinement. Firstly, I discuss the experimental results of Tg, D and etaeff of poly(isobutyl methacrylate) films supported by silica (PiBMA/SiOx). Both T g and D were found to be independent of h 0, but etaeff decreased with decreasing h 0. Since both D and etaeff describe transport phenomena known to depend on the local friction coefficient or equivalently the local viscosity, it is questionable why D and etaeff displayed seemingly inconsistent h 0 dependencies. We envisage the different h0 dependencies to be caused by Tg, D and etaeff being different functions of the local T g's (Tg,i) or viscosities (eta i). By assuming a three
International Nuclear Information System (INIS)
Wang, J.Y.; Wang, X.W.; Rifkin, J.; Li, D.X.
2001-12-01
Using the molecular dynamics simulation method, the microstructure of distortion region near curved amorphous-like grain boundary in nano-NiAl alloy is studied. The results showed that due to the internal elastic force of high energy grain boundary, distortion layer exists between grain and grain boundary. The lattice expansion and structure factor decreasing are observed in this region. Stacking fault in sample with grain size 3.8nm is clearly observed across the distortion region at the site very close to grain. The influences of different grain sizes on average distortion degree and volume fractions of distortion region, grain and grain boundary are also discussed. (author)
Zhang, Dongdong; Bai, Fang; Wang, Yong; Wang, Jinguo; Wang, Wenquan
2017-08-08
The TiC p /Cu master alloy was prepared via thermal explosion reaction. Afterwards, the nano-sized TiC p /Cu master alloy was dispersed by electromagnetic stirring casting into the melting Cu-Cr-Zr alloys to fabricate the nano-sized TiC p -reinforced Cu-Cr-Zr composites. Results show that nano-sized TiC p can effectively refine the grain size of Cu-Cr-Zr alloys. The morphologies of grain in Cu-Cr-Zr composites changed from dendritic grain to equiaxed crystal because of the addition and dispersion of nano-sized TiC p . The grain size decreased from 82 to 28 μm with the nano-sized TiC p content. Compared with Cu-Cr-Zr alloys, the ultimate compressive strength (σ UCS ) and yield strength (σ 0.2 ) of 4 wt% TiC p -reinforced Cu-Cr-Zr composites increased by 6.7% and 9.4%, respectively. The wear resistance of the nano-sized TiCp-reinforced Cu-Cr-Zr composites increased with the increasing nano-sized TiCp content. The wear loss of the nano-sized TiC p -reinforced Cu-Cr-Zr composites decreased with the increasing TiC p content under abrasive particles. The eletrical conductivity of Cu-Cr-Zr alloys, 2% and 4% nano-sized TiCp-reinforced Cu-Cr-Zr composites are 64.71% IACS, 56.77% IACS and 52.93% IACS, respectively.
Picosecond laser micro/nano surface texturing of nickel for superhydrophobicity
Wang, X. C.; Wang, B.; Xie, H.; Zheng, H. Y.; Lam, Y. C.
2018-03-01
A single step direct picosecond laser texturing process was demonstrated to be able to obtain a superhydrophobic surface on a nickel substrate, a key material for mold fabrication in the manufacture of various devices, including polymeric microfluidic devices. A two-scale hierarchical surface structure of regular 2D array micro-bumps with nano-ripples was produced on a nickel surface. The laser textured surface initially showed superhydrophilicity with almost complete wetting of the structured surface just after laser treatment, then quickly changed to nearly superhydrophobic with a water contact angle (WCA) of 140° in less than 1 d, and finally became superhydrophobic with a WCA of more than 150° and a contact angle hysteresis (CAH) of less than 5°. The mechanism involved in the process is discussed in terms of surface morphology and surface chemistry. The ultra-fast laser induced NiO catalytic effect was thought to play a key role in modifying the surface chemistry so as to lower the surface energy. The developed process has the potential to improve the performance of nickel mold in the fabrication of microfluidic devices.
Directory of Open Access Journals (Sweden)
Amira M. Mahmoud
2015-03-01
Full Text Available Environmental pollution by heavy metal is arising as the most endangering tasks to both water sources and atmosphere quality today. The treatment of heavy metals is of special concern due to their recalcitrance and persistence in the environment. To limit the spread of the heavy metals within water sources, nickel oxide nanoparticles adsorbents were synthesized and characterized with the aim of removal of one of the aggressive heavy elements, namely; lead ions. Nano nickel oxide adsorbents were prepared using NaOH and oxalic acid dissolved in ethanol as precursors. The results indicated that adsorption capacity of Pb(II ion by NiO-org catalyst is favored than that prepared using NaOH as a precipitant. Nickel oxide nanoparticles prepared by the two methods were characterized structurally and chemically through XRD, DTA, TGA, BET and FT-IR. Affinity and efficiency sorption parameters of the solid nano NiO particles, such as; contact time, initial concentration of lead ions and the dosage of NiO nano catalyst and competitive adsorption behaviors were studied. The results showed that the first-order reaction law fit the reduction of lead ion, also showed good linear relationship with a correlation coefficient (R2 larger than 0.9.
Optical metrology of Ni and NiSi thin films used in the self-aligned silicidation process
International Nuclear Information System (INIS)
Kamineni, V. K.; Bersch, E. J.; Diebold, A. C.; Raymond, M.; Doris, B. B.
2010-01-01
The thickness-dependent optical properties of nickel metal and nickel monosilicide (NiSi) thin films, used for self-aligned silicidation process, were characterized using spectroscopic ellipsometry. The thickness-dependent complex dielectric function of nickel metal films is shown to be correlated with the change in Drude free electron relaxation time. The change in relaxation time can be traced to the change in grain boundary (GB) reflection coefficient and grain size. A resistivity based model was used as the complementary method to the thickness-dependent optical model to trace the change in GB reflection coefficient and grain size. After silicidation, the complex dielectric function of NiSi films exhibit non-Drude behavior due to superimposition of interband absorptions arising at lower frequencies. The Optical models of the complete film stack were refined using x-ray photoelectron spectroscopy, Rutherford backscattered spectroscopy, and x-ray reflectivity (XRR).
Giant secondary grain growth in Cu films on sapphire
Directory of Open Access Journals (Sweden)
David L. Miller
2013-08-01
Full Text Available Single crystal metal films on insulating substrates are attractive for microelectronics and other applications, but they are difficult to achieve on macroscopic length scales. The conventional approach to obtaining such films is epitaxial growth at high temperature using slow deposition in ultrahigh vacuum conditions. Here we describe a different approach that is both simpler to implement and produces superior results: sputter deposition at modest temperatures followed by annealing to induce secondary grain growth. We show that polycrystalline as-deposited Cu on α-Al2O3(0001 can be transformed into Cu(111 with centimeter-sized grains. Employing optical microscopy, x-ray diffraction, and electron backscatter diffraction to characterize the films before and after annealing, we find a particular as-deposited grain structure that promotes the growth of giant grains upon annealing. To demonstrate one potential application of such films, we grow graphene by chemical vapor deposition on wafers of annealed Cu and obtain epitaxial graphene grains of 0.2 mm diameter.
Energy Technology Data Exchange (ETDEWEB)
Shilpa Harish, T.; Viswanath, P., E-mail: viswanath@cnsms.res.in
2016-01-01
We report our studies on thin films of metallo-phthalocyanine (MPc), Nickel(II)1,4,8,11,15,18,22,25-octabutoxy-29H,31H-phthalocyanine (NiPc(OBu){sub 8}) transferred in a well defined thermodynamic state over a self assembled monolayer (octadecyl trichlorosilane)/SiO{sub 2}/Si substrate using the Langmuir–Blodgett (LB) method. The films are characterized using differential scanning calorimetry (DSC), grazing incidence X-ray diffraction (GIXD) and atomic force microscopy (AFM) techniques. DSC studies on powdered samples in the bulk indicate enantiotropic solid–solid phase transition. GIXD studies on the as-deposited LB film show a Bragg peak indicating crystallinity of the thin film. Annealing (373 K) results in reduction of lattice spacing (1.21 Å) signifying changes in molecular packing within the unit cell. At this stage, an additional Bragg peak is observed which grows at the expense of the former one and they coexist between 373 K and 423 K. A discontinuity in lattice spacing from 20.73 to 15.12 Å with annealing indicates clearly a structural change of the underlying crystalline lattice. Correspondingly, the surface morphology images obtained using AFM show, with annealing, a transformation from spherical granular morphology to elongated, flat crystallites suggesting asymmetric growth process. Statistical parameters of the grain extracted from the AFM images show that the size, fractal dimension and circularity are affected by annealing. Based on these studies, we infer the structural and surface morphological changes of the meta-stable phase (Form I) to the stable phase (Form II) in annealed LB films of phthalocyanine. - Highlights: • Langmuir–Blodgett (LB) films of phthalocyanine subjected to thermal annealing. • Structural transformation and coexistence of polymorphs in LB films • Surface morphology changes from nanoscale grains to elongated crystallites. • Reduction of fractal dimension and circularity index reveals asymmetric growth.
Grain size effect on the electrical response of SnO2 thin and thick film gas sensors
Directory of Open Access Journals (Sweden)
Raluca Savu
2009-03-01
Full Text Available Porous nano and micro crystalline tin oxide films were deposited by RF Magnetron Sputtering and doctor blade techniques, respectively. Electrical resistance and impedance spectroscopy measurements, as a function of temperature and atmosphere, were performed in order to determine the influence of the microstructure and working conditions over the electrical response of the sensors. The conductivity of all samples increases with the temperature and decreases in oxygen, as expected for an n-type semiconducting material. The impedance plots indicated the existence of two time constants related to the grains and the grain boundaries. The Nyquist diagrams at low frequencies revealed the changes that took place in the grain boundary region, with the contribution of the grains being indicated by the formation of a second semicircle at high frequencies. The better sensing performance of the doctor bladed samples can be explained by their lower initial resistance values, bigger grain sizes and higher porosity.
Energy Technology Data Exchange (ETDEWEB)
Ramkumar, S. [Bannari Amman Institute of Technology, Department of Physics, Erode, Tamilnadu (India); Rajarajan, G. [Vidhya Mandhir Institute of Technology, Department of Physics, Erode, Tamilnadu (India)
2017-06-15
Nanocrystalline of pristine and nickel (Ni)-doped tungsten trioxide (WO{sub 3}) thin films was deposited by chemical bath deposition method. The concentrations of Ni ions were varied from 0 to 10 wt%. In order to improve the crystallinity of the films were annealed at 600 C for 2 h in the ambient atmosphere. X-ray diffraction results reveal that the WO{sub 3} doped with nickel crystallizes in monoclinic structure and the results are in good agreement with the standard JCPDS data (card no: 83-0951). AFM micrographs reveal that average grain size of about 27-39 nm for pure and Ni-doped WO{sub 3} thin films. In addition, the band gap of the Ni-doped WO{sub 3} nanostructures is facilely tunable by controlling the Ni contents. The humidity sensor setup was fabricated and measured for pure and Ni-doped WO{sub 3} thin film sensor with various level of RH (10-90%). The Ni-doped WO{sub 3} sensor showed fast response and high sensitivity than pure WO{sub 3}. The photocatalytic activities of the films were evaluated by degradation of methyl orange, methylene blue and phenol in an aqueous solution under visible light irradiation. The photocatalytic activity of WO{sub 3} nanostructures could be remarkably enhanced by doping the Ni impurity. (orig.)
Texture Formation of Electroplated Nickel and Nickel Alloy on Cu Substrate
International Nuclear Information System (INIS)
Lee, Hee Gyoun; Hong, Gye Won; Kim, Jae Geun; Lee, Sun Wang; Kim, Ho Jin
2006-01-01
Nickel and nickel-tungsten alloy were electroplated on a cold rolled and heat treated copper(Cu) substrate. 4 mm-thick high purity commercial grade Cu was rolled to various thicknesses of 50, 70, 100 and 150 micron. High reduction ratio of 30% was applied down to 150 micron. Rolled texture was converted into cube texture via high temperature heat treatment at 400-800 degrees C. Grain size of Cu was about 50 micron which is much smaller compared to >300 micron for the Cu prepared using smaller reduction pass of 5%. 1.5 km-long 150 micron Cu was fabricated with a rolling speed of 33 m/min and texture of Cu was uniform along length. Abnormal grain growth and non-cube texture appeared for the specimen anneal above 900 degrees C. 1-10 micron thick Ni and Ni-W film was electroplated onto an annealed cube-textured Cu or directly on a cold rolled Cu. Both specimens were annealed and the degree of texture was measured. For electroplating of Ni on annealed Cu, Ni layer duplicated the cube-texture of Cu substrate and the FWHM of in plane XRD measurement for annealed Cu layer and electroplated layer was 9.9 degree and 13.4 degree, respectively. But the FWHM of in plane XRD measurement of the specimen which electroplated Ni directly on cold rolled Cu was 8.6 degree, which is better texture than that of nickel electroplated on annealed Cu and it might be caused by the suppression of secondary recrystallization and abnormal grain growth of Cu at high temperature above 900 degrees C by electroplated nickel.
International Nuclear Information System (INIS)
Savaloni, Hadi; Haydari-Nasab, Fatemh; Malmir, Mariam
2011-01-01
Silver chiral nano-flowers with 3-, 4- and 5-fold symmetry were produced using oblique angle deposition method in conjunction with the rotation of sample holder with different speeds at different sectors of each revolution corresponding to symmetry order of the acquired nano-flower. Atomic force microscopy (AFM) and field emission scanning electron microscopy (FESEM), were employed to obtain morphology and nano-structure of the films. Optical characteristics of silver chiral nano-flower thin films were obtained using single beam spectrophotometer with both s- and p-polarization incident light at 30 o and 70 o incidence angles and at different azimuthal angles (φ). Optical spectra showed both TM (TDM (transverse dipole mode) and TQM (transverse quadruple mode)) and LM (longitudinal mode) Plasmon resonance peaks. For 3- and 4-fold symmetry chiral nano-flowers the s-polarization extinction spectra obtained at different azimuthal angles did not show significant change in the Plasmon peak position while 5-fold symmetry chiral nano-flower showed a completely different behavior, which may be the result of increased surface anisotropy, so when the φ angle is changed the s-polarization response from the surface can change more significantly than that for lower symmetries. In general, for 3-, 4- and 5-fold symmetry chiral nano-flowers a sharp peak at lower wavelengths ( o incidence angle.
Energy Technology Data Exchange (ETDEWEB)
Zhao, Xinbao [National Energy R and D Center of Clean and High-Efficiency Fossil-Fired Power Generation Technology, Xi' an Thermal Power Research Institute Co. Ltd., Xi' an (China); Northwestern Polytechnical University, State Key Laboratory of Solidification Processing, Xi' an (China); Liu, Lin; Zhang, Jun [Northwestern Polytechnical University, State Key Laboratory of Solidification Processing, Xi' an (China)
2015-08-15
Grain competitive growth of nickel-based single-crystal superalloys during directional solidification was investigated. A detailed characterization of bi-crystals' competitive growth was performed to explore the competitive grain evolution. It was found that high withdrawal rate improved the efficiency of grain competitive growth. The overgrowth rate was increased when the misorientation increased. Four patterns of grain competitive growth with differently oriented dispositions were characterized. The results indicated that the positive branching of the dendrites played a significant role in the competitive growth process. The effect of crystal orientation and heat flow on the competitive growth can be attributed to the blocking mechanism between the adjacent grains. (orig.)
A study of manufacturing tubes with nano/ultrafine grain structure by stagger spinning
International Nuclear Information System (INIS)
Xia, Qinxiang; Xiao, Gangfeng; Long, Hui; Cheng, Xiuquan; Yang, Baojian
2014-01-01
Highlights: • Proposing a method of manufacturing tubes with nano/ultrafine crystal. • Obtaining the refined ferritic grains with an size of 500 nm after stagger spinning. • Obtaining the equiaxial ferritic grains with an size of 600 nm after annealing. - Abstract: A new method of manufacturing tubes with nano/ultrafine grain structure by stagger spinning and recrystallization annealing is proposed in this study. Two methods of the stagger spinning process are developed, the corresponding macroforming quality, microstructural evolution and mechanical properties of the spun tubes made of ASTM 1020 steel are analysed. The results reveal that a good surface smoothness and an improved spin-formability of spun parts can be obtained by the process combining of 3-pass spinning followed by a 580 °C × 0.5 h static recrystallization and 2-pass spinning with a 580 °C × 1 h static recrystallization annealing under the severe thinning ratio of wall thickness reduction. The ferritic grains with an average initial size of 50 μm are refined to 500 nm after stagger spinning under the 87% thinning ratio of wall thickness reduction. The equiaxial ferritic grains with an average size of 600 nm are generated through re-nucleation and grain growth by subsequent recrystallization annealing at 580 °C for 1 h heat preservation. The tensile strength of spun tubes has been founded to be proportional to the reciprocal of layer spacing of pearlite (LSP), and the elongation is inversely proportional to the reciprocal of LSP. This study shows that the developed method of stagger power spinning has the potential to be used to manufacture bulk metal components with nano/ultrafine grain structure
Ding, Q.; Li, W. L.; Zhao, W. L.; Wang, J. Y.; Xing, Y. P.; Li, X.; Xue, T.; Qi, W.; Zhang, K. L.; Yang, Z. C.; Zhao, J. S.
2017-03-01
A facile synthesis strategy has been developed for fabricating multi-layer graphene/nickel hybrid film as micro-supercapacitor electrodes by using plasma enhanced chemical vapor deposition. The as-presented method is advantageous for rapid graphene growth at relatively low temperature of 650 °C. In addition, after pre-treating for the as-deposited nickel film by using argon plasma bombardment, the surface-to-volume ratio of graphene film on the treated nickel substrate is effectively increased by the increasing of surface roughness. This is demonstrated by the characterization results from transmission electron microscopy, scanning electron microscope and atomic force microscopy. Moreover, the electrochemical performance of the resultant graphene/nickel hybrid film as micro-supercapacitor working electrode was investigated by cyclic voltammetry and galvanostatic charge/discharge measurements. It was found that the increase of the surface-to-volume ratio of graphene/nickel hybrid film improved the specific capacitance of 10 times as the working electrode of micro-supercapacitor. Finally, by using comb columnar shadow mask pattern, the micro-supercapacitor full cell device was fabricated. The electrochemical performance measurements of the micro-supercapacitor devices indicate that the method presented in this study provides an effective way to fabricate micro-supercapacitor device with enhanced energy storage property.
Nanostructured nickel doped β-V{sub 2}O{sub 5} thin films for supercapacitor applications
Energy Technology Data Exchange (ETDEWEB)
Jeyalakshmi, K. [Department of Physics, PSNA College of Engineering and Technology, Dindigul 624622 (India); Vijayakumar, S. [Department of Physics, Gandhigram Rural Institute, Gandhigram 624302 (India); Purushothaman, K.K. [Department of Physics, TRP Engineering College, Trichy (India); Muralidharan, G., E-mail: muralg@rediffmail.com [Department of Physics, Gandhigram Rural Institute, Gandhigram 624302 (India)
2013-07-15
Graphical abstract: - Highlights: • Nanorod with pores has been observed for 5 wt.% nickel doped β-V{sub 2}O{sub 5} thin films. • Film with 5 wt.% of nickel exhibits a specific capacitance of 417 F g{sup −1}. • These films exhibit high energy density. • The charge transfer resistance is 103 Ω. - Abstract: Interesting thin film electrodes of nickel doped vanadium pentoxide with different levels of doping (2.5–10 wt.%) are prepared on FTO and glass substrate at 300 °C using sol–gel spin coating method. The structural and morphological studies are made to understand the nature of the surface of the thin films. The electrochemical characteristics have been investigated through cyclic voltammetry and ac impedance spectroscopy measurements. The doping of nickel with β-V{sub 2}O{sub 5} has led to enhanced intercalation and deintercalation of ions. β-V{sub 2}O{sub 5} films with 5 wt.% of Ni exhibit the maximum specific capacitance of 417 F/g at a scan rate of 5 mV/s, with a good cyclic stability making it a promising candidate for supercapacitor application.
International Nuclear Information System (INIS)
Dirras, G.; Bouvier, S.; Gubicza, J.; Hasni, B.; Szilagyi, T.
2009-01-01
The present work focuses on understanding the mechanical behavior of bulk ultrafine-grained nickel specimens processed by spark plasma sintering of high purity nickel nanopowder and subsequently deformed under large amplitude monotonic simple shear tests and strain-controlled cyclic simple shear tests at room temperature. During cyclic tests, the samples were deformed up to an accumulated von Mises strain of about ε VM = 0.75 (the flow stress was in the 650-700 MPa range), which is extremely high in comparison with the low tensile/compression ductility of this class of materials at quasi-static conditions. The underlying physical mechanisms were investigated by electron microscopy and X-ray diffraction profile analysis. Lattice dislocation-based plasticity leading to cell formation and dislocation interactions with twin boundaries contributed to the work-hardening of these materials. The large amount of plastic strain that has been reached during the shear tests highlights intrinsic mechanical characteristics of the ultrafine-grained nickel studied here.
Energy Technology Data Exchange (ETDEWEB)
Dirras, G., E-mail: dirras@univ-paris13.fr [LPMTM - CNRS, Institut Galilee, Universite Paris 13, 99 Avenue J.B. Clement, 93430 Villetaneuse (France); Bouvier, S. [LPMTM - CNRS, Institut Galilee, Universite Paris 13, 99 Avenue J.B. Clement, 93430 Villetaneuse (France); Gubicza, J. [Department of Materials Physics, Eoetvoes Lorand University, P.O.B. 32, Budapest H-1518 (Hungary); Hasni, B. [LPMTM - CNRS, Institut Galilee, Universite Paris 13, 99 Avenue J.B. Clement, 93430 Villetaneuse (France); Szilagyi, T. [Department of Materials Physics, Eoetvoes Lorand University, P.O.B. 32, Budapest H-1518 (Hungary)
2009-11-25
The present work focuses on understanding the mechanical behavior of bulk ultrafine-grained nickel specimens processed by spark plasma sintering of high purity nickel nanopowder and subsequently deformed under large amplitude monotonic simple shear tests and strain-controlled cyclic simple shear tests at room temperature. During cyclic tests, the samples were deformed up to an accumulated von Mises strain of about {epsilon}{sub VM} = 0.75 (the flow stress was in the 650-700 MPa range), which is extremely high in comparison with the low tensile/compression ductility of this class of materials at quasi-static conditions. The underlying physical mechanisms were investigated by electron microscopy and X-ray diffraction profile analysis. Lattice dislocation-based plasticity leading to cell formation and dislocation interactions with twin boundaries contributed to the work-hardening of these materials. The large amount of plastic strain that has been reached during the shear tests highlights intrinsic mechanical characteristics of the ultrafine-grained nickel studied here.
Preparation by thermal evaporation under vacuum of thin nickel films without support
International Nuclear Information System (INIS)
Prugne, P.; Garin, P.; Lechauguette, G.
1959-01-01
This note deals with the preparation of nickel films without support by means of the technique described but using a new evaporation apparatus. In effect it was necessary, in order to obtain these nickel films, to modify the thermal evaporation conditions. An attempt to obtain a film without support after evaporation in a conventional apparatus led almost invariably to defeat. This appeared to be due to the high concentration of oxygen and of various vapors (diffusion pumps, degassing, etc.) present in the residual atmosphere of the conventional evaporation system. Reprint of a paper published in 'Le Vide, N. 74, March-April 1958, p. 82-83
Chen, Rui; Zhang, Changbo; Zhao, Yanling; Huang, Yongchun; Liu, Zhongqi
2018-01-01
Nano-silicon (Si) may be more effective than regular fertilizers in protecting plants from cadmium (Cd) stress. A field experiment was conducted to study the effects of nano-Si on Cd accumulation in grains and other organs of rice plants (Oryza sativa L. cv. Xiangzaoxian 45) grown in Cd-contaminated farmland. Foliar application with 5~25 mM nano-Si at anthesis stage reduced Cd concentrations in grains and rachises at maturity stage by 31.6~64.9 and 36.1~60.8%, respectively. Meanwhile, nano-Si application significantly increased concentrations of potassium (K), magnesium (Mg), and iron (Fe) in grains and rachises, but imposed little effect on concentrations of calcium (Ca), zinc (Zn), and manganese (Mn) in them. Uppermost nodes under panicles displayed much higher Cd concentration (4.50~5.53 mg kg -1 ) than other aerial organs. After foliar application with nano-Si, translocation factors (TFs) of Cd ions from the uppermost nodes to rachises significantly declined, but TFs of K, Mg, and Fe from the uppermost nodes to rachises increased significantly. High dose of nano-Si (25 mM) was more effective than low dose of nano-Si in reducing TFs of Cd from roots to the uppermost nodes and from the uppermost nodes to rachises. These findings indicate that nano-Si supply reduces Cd accumulation in grains by inhibiting translocation of Cd and, meanwhile, promoting translocation of K, Mg, and Fe from the uppermost nodes to rachises in rice plants.
Influence of Fe(Cr) miscibility on thin film grain size and stress
Energy Technology Data Exchange (ETDEWEB)
Zhou, Xuyang; Kaub, Tyler; Martens, Richard L.; Thompson, Gregory B., E-mail: gthompson@eng.ua.edu
2016-08-01
During the post coalescence portion of thin film deposition, thin film stress is related to the grain size and adatom mobility of the depositing material. Using a Fe(Cr) alloy thin film, the manipulation of the tensile stress for thick films was studied as a function of Cr solute content up to 8 at.%. Solute concentrations up to 4 at.% resulted in an approximate 50% increase in grain size that resulted in a reduction of the tensile stress to be lower than either elemental film. Upon increasing the Cr content, the grain size refined and the tensile stress of the films increased. Atom probe characterization of the grain boundaries confirmed Cr chemical partitioning which refined the grain size and altered the film's texture, both of which contributed to the change in film stress. The use of intrinsic segregation, rather than deposition processing parameters, appears to be another viable option for regulating film stress. - Highlights: • Solute segregation to regulate grain size in controlling film stress • Quantification of Cr interfacial excess as a function of alloy content • Quantification of texture fiber alignment as a function of Cr content.
International Nuclear Information System (INIS)
Lacroix, Monique; Khan, Ruhul A.; Salmieri, Stephane; Huq, Tanzina; Khan, Avik; Safrany, Agnes
2011-01-01
Biopolymeric (methylcellulose, chitosan and alginate) films were prepared by solution casting and their thermo-mechanical properties were evaluated. Nano crystalline cellulose (NCC) was incorporated into the optimized biopolymeric films. It was found that NCC acted as an excellent reinforcing agent which improved the mechanical properties of the films significantly. The NCC containing biopolymeric films were exposed to gamma radiation (2-25 kGy) and it revealed that biopolymeric films gained strength below 5 kGy dose. Monomer grafting onto the biopolymers were carried out to improve the filler (NCC)-matrix (biopolymers) compatibility. Two monomers (Trimethylol propane tri-methacrylate and 2-Hydroxyethyl methacrylate) were grafted using gamma radiation at 5-25 kGy doses. It was found that monomers were successfully grafted with biopolymers and NCC. Grafted films showed excellent mechanical properties. NCC and carbon nanotubes (CNT) were also incorporated in polycaprolactone-based films prepared by compression molding. It was found that NCC (5% by wt) and CNT (0.2% by wt) improved the mechanical properties of the PCL films significantly. The nano materials containing PCL films were gamma irradiated and found better mechanical and barrier properties. Surface morphology of the nano films was studied by scanning electron microscopy. (author)
Energy Technology Data Exchange (ETDEWEB)
Lacroix, Monique; Khan, Ruhul A.; Salmieri, Stephane; Huq, Tanzina; Khan, Avik [INRS-Institut Armand-Frappier, Research Laboratories in Sciences Applied to Food, Canadian Irradiation Center, 531 Boulevard des Prairies, Laval, Quebec, H7V 1B7 (Canada); Safrany, Agnes [International Atomic Energy Agency, Vienna International Centre, A-1400 Vienna (Austria)
2011-07-01
Biopolymeric (methylcellulose, chitosan and alginate) films were prepared by solution casting and their thermo-mechanical properties were evaluated. Nano crystalline cellulose (NCC) was incorporated into the optimized biopolymeric films. It was found that NCC acted as an excellent reinforcing agent which improved the mechanical properties of the films significantly. The NCC containing biopolymeric films were exposed to gamma radiation (2-25 kGy) and it revealed that biopolymeric films gained strength below 5 kGy dose. Monomer grafting onto the biopolymers were carried out to improve the filler (NCC)-matrix (biopolymers) compatibility. Two monomers (Trimethylol propane tri-methacrylate and 2-Hydroxyethyl methacrylate) were grafted using gamma radiation at 5-25 kGy doses. It was found that monomers were successfully grafted with biopolymers and NCC. Grafted films showed excellent mechanical properties. NCC and carbon nanotubes (CNT) were also incorporated in polycaprolactone-based films prepared by compression molding. It was found that NCC (5% by wt) and CNT (0.2% by wt) improved the mechanical properties of the PCL films significantly. The nano materials containing PCL films were gamma irradiated and found better mechanical and barrier properties. Surface morphology of the nano films was studied by scanning electron microscopy. (author)
Nickel-induced crystallization of amorphous silicon
Energy Technology Data Exchange (ETDEWEB)
Schmidt, J A; Arce, R D; Buitrago, R H [INTEC (CONICET-UNL), Gueemes 3450, S3000GLN Santa Fe (Argentina); Budini, N; Rinaldi, P, E-mail: jschmidt@intec.unl.edu.a [FIQ - UNL, Santiago del Estero 2829, S3000AOM Santa Fe (Argentina)
2009-05-01
The nickel-induced crystallization of hydrogenated amorphous silicon (a-Si:H) is used to obtain large grained polycrystalline silicon thin films on glass substrates. a-Si:H is deposited by plasma enhanced chemical vapour deposition at 200 deg. C, preparing intrinsic and slightly p-doped samples. Each sample was divided in several pieces, over which increasing Ni concentrations were sputtered. Two crystallization methods are compared, conventional furnace annealing (CFA) and rapid thermal annealing (RTA). The crystallization was followed by optical microscopy and scanning electron microscopy observations, X-ray diffraction, and reflectance measurements in the UV region. The large grain sizes obtained - larger than 100{mu}m for the samples crystallized by CFA - are very encouraging for the preparation of low-cost thin film polycrystalline silicon solar cells.
Deposition of DLC Film on Stainless Steel Substrates Coated by Nickel Using PECVD Method.
Khalaj, Zahra; Ghoranneviss, Mahmood; Vaghri, Elnaz; Saghaleini, Amir; Diudea, Mircea V
2012-06-01
Research on diamond-like carbon (DLC) films has been devoted to find both optimized conditions and characteristics of the deposited films on various substrates. In the present work, we investigate the quality of the DLC films grown on stainless steel substrates using different thickness of the nickel nanoparticle layers on the surface. Nickel nanoparticles were sputtered on the stainless steel substrates at 200 °C by a DC-sputtering system to make a good adherence between DLC coating and steel substrates. Atomic Force Microscopy was used to characterize the surface roughness and distribution function of the nickel nanoparticles on the substrate surface. Diamond like carbon films were deposited on stainless steel substrates coated by nickel using pure acetylene and C2H2/H2 with 15% flow ratio by DC-Plasma Enhanced Chemical Vapor Deposition (PECVD) systems. Microstructural analysis by Raman spectroscopy showed a low intensity ratio ID/IG for DLC films by increasing the Ni layer thickness on the stainless steel substrates. Fourier Transforms Infrared spectroscopy (FTIR) evidenced the peaks attributed to C-H bending and stretching vibration modes in the range of 1300-1700 cm-1 and 2700-3100 cm-1, respectively, in good agreement with the Raman spectroscopy and confirmed the DLC growth in all samples.
Akinkuade, Shadrach; Mwankemwa, Benanrd; Nel, Jacqueline; Meyer, Walter
2018-04-01
A simple and cheap chemical deposition method was used to produce a nickel oxide (NiO) thin film on glass substrates from a solution that contained Ni2+ and monoethanolamine. Thermal treatment of the film at temperatures above 350 °C for 1 h caused decomposition of the nickel hydroxide into nickel oxide. Structural, optical and electrical properties of the film were studied using X-ray diffraction (XRD), spectrophotometry, current-voltage measurements and scanning electron microscopy (SEM). The film was found to be polycrystalline with interplanar spacing of 0.241 nm, 0.208 nm and 0.148 nm for (111), (200) and (220) planes respectively, the lattice constant a was found to be 0.417 nm. The film had a porous surface morphology, formed from a network of nanowalls of average thickness of 66.67 nm and 52.00 nm for as-deposited and annealed films respectively. Transmittance of visible light by the as-deposited film was higher and the absorption edge of the film blue-shifted after annealing. The optical band gap of the annealed film was 3.8 eV. Electrical resistivity of the film was 378 Ωm.
On the strengthening behavior of ultrafine-grained nickel processed from nanopowders
International Nuclear Information System (INIS)
Bui, Q.H.; Dirras, G.; Ramtani, S.; Gubicza, J.
2010-01-01
Bulk ultrafine-grained nickel specimens having grain sizes in the range of 0.25-5 μm were processed by a spark plasma sintering method. The resulting microstructures were characterized by electron backscattering diffraction, transmission electron microscopy and X-ray diffraction analysis. Compression tests were carried out at room temperature and at a strain rate of 1.6 x 10 -4 s -1 . It was found that the fine-grained microstructure and the presence of NiO phase were the main strengthening factors in the as-processed bulk materials. The contribution of the oxide phase to strengthening was even more pronounced for lower grain sizes. This contribution was calculated as the difference between the measured strength and the value obtained from a Hall-Petch plot of oxide-free samples, and this yielded a flow stress increment of about 635 MPa for the lowest grain size studied here. In addition, a transition from work-hardening to -softening occurred for materials having a mean grain size smaller than about 300 nm and having boundaries that could have been weakened by the presence of a high amount of NiO phase.
International Nuclear Information System (INIS)
Margetan, F.J.; Haldipur, Pranaam; Yu Linxiao; Thompson, R.B.
2005-01-01
For pulse/echo inspections of metals, models which predict backscattered noise characteristics often make a 'single-scattering' assumption, i.e., multiple-scattering events in which sound is scattered from one grain to another before returning to the transducer are ignored. Models based on the single-scattering assumption have proven to be very useful in simulating inspections of engine-alloy billets and forgings. However, this assumption may not be accurate if grain scattering is too 'strong' (e.g., if the mean grain diameter and/or the inspection frequency is too large). In this work, backscattered grain noise measurements and analyses were undertaken to search for evidence of significant multiple scattering in pulse/echo inspections of jet-engine Nickel alloys. At or above about 7 MHz frequency and 50 micron grain diameter, problems were seen with single-scattering noise models that are likely due to the neglect of multiple scattering by the models. The modeling errors were less severe for focused-probe measurements in the focal zone than for planar probe inspections. Single-scattering noise models are likely adequate for simulating current billet inspections which are carried out using 5-MHz focused transducers. However, multiple scattering effects should be taken into account in some fashion when simulating higher-frequency inspections of Nickel-alloy billets having large mean grain diameters (> 40 microns)
International Nuclear Information System (INIS)
Samardak, Alexander; Sukovatitsina, Ekaterina; Ognev, Alexey; Stebliy, Maksim; Davydenko, Alexander; Chebotkevich, Ludmila; Keun Kim, Young; Nasirpouri, Forough; Janjan, Seyed-Mehdi; Nasirpouri, Farzad
2014-01-01
Magnetic states of nickel nanogranular films were studied in two distinct structures of individual and agglomerated granules electrodeposited on n-type Si(1 1 1) surface from a modified Watts bath at a low pH of 2. Magnetic force microscopy and micromagnetic simulations revealed three-dimensional out-of-plane magnetic vortex states in stand-alone hemispherical granules and their arrays, and multi-domain patterns in large agglomerates and integrated films. Once the granules coalesce into small chains or clusters, the coercivity values increased due to the reduction of inter-granular spacing and strengthening of the magnetostatic interaction. Further growth leads to the formation of a continuous granulated film which strongly affected the coercivity and remanence. This was characterized by the domain wall nucleation and propagation leading to a stripe domain pattern. Magnetoresistance measurements as a function of external magnetic field are indicative of anisotropic magnetoresistance (AMR) for the continuous films electrodeposited on Si substrate. - Highlights: • Magnetic states of electrodeposited nickel in isolated spherical and agglomerated nanogranules, and a continuous film. • Preferential magnetization reversal mechanism in isolated granules is vortex state. • Micromagnetic simulations confirm the three-dimensional vortex. • Transition between the vortex state and multi-domain magnetic pattern causes a significant decrease in the coercive force. • Continuous nickel films electrodeposited on silicon substrate exhibit AMR whose magnitude increases with the film thickness
International Nuclear Information System (INIS)
Nan Junmin; Yang Yong; Lin Zugeng
2006-01-01
The oxide films of nickel electrode formed in 30 wt.% KOH solution under potentiodynamic conditions were characterized by means of electrochemical, in situ PhotoElectrochemistry Measurement (PEM) and Confocal Microprobe Raman spectroscopic techniques. The results showed that a composite oxide film was produced on nickel electrode, in which aroused cathodic or anodic photocurrent depending upon polarization potentials. The cathodic photocurrent at -0.8 V was raised from the amorphous film containing nickel hydroxide and nickel monoxide, and mainly attributed to the formation of NiO through the separation of the cavity and electron when laser light irradiates nickel electrode. With the potential increasing to more positive values, Ni 3 O 4 and high-valence nickel oxides with the structure of NiO 2 were formed successively. The composite film formed in positive potential aroused anodic photocurrent from 0.33 V. The anodic photocurrent was attributed the formation of oxygen through the cavity reaction with hydroxyl on solution interface. In addition, it is demonstrated that the reduction resultants of high-valence nickel oxides were amorphous, and the oxide film could not be reduced completely. A stable oxide film could be gradually formed on the surface of nickel electrode with the cycling and aging in 30 wt.% KOH solution
Epitaxial Ni films, e-beam nano-patterning and BMR
Lukaszew, R. Alejandra; Zhang, Zhengdong; Pearson, Dave; Zambano, Antonio
2004-05-01
We have attempted to clarify possible domain-wall processes present in the recently reported large ballistic magnetoresistance effects in nano-contacts. To that effect we have used e-beam lithography applied to epitaxial Ni films to fabricate nano-bridges in more controlled geometry than electrochemical deposition. Our preliminary results indicate that magnetic domains do play a role in the magneto-resistance of these nano-bridges but the order of magnitude of the observed effect is considerably smaller than the reported observations in electrochemically prepared nano-contacts.
Epitaxial Ni films, e-beam nano-patterning and BMR
International Nuclear Information System (INIS)
Lukaszew, R.A.; Zhang Zhengdong; Pearson, Dave; Zambano, Antonio
2004-01-01
We have attempted to clarify possible domain-wall processes present in the recently reported large ballistic magnetoresistance effects in nano-contacts. To that effect we have used e-beam lithography applied to epitaxial Ni films to fabricate nano-bridges in more controlled geometry than electrochemical deposition. Our preliminary results indicate that magnetic domains do play a role in the magneto-resistance of these nano-bridges but the order of magnitude of the observed effect is considerably smaller than the reported observations in electrochemically prepared nano-contacts
Growth and Characteristic of Amorphous Nano-Granular TeO2-V2O5-NiO Thin Films
Hosseinzadeh, Sh.; Rahmati, A.; Bidadi, H.
2016-12-01
TeO2-V2O5-NiO thin films were deposited using thermal evaporation from 40TeO2-(60-y)V2O5-yNiO (y=0-30mol%) target. Structural analysis of the films was identified by X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The amorphous TeO2-V2O5-NiO films have nanosized clear grain structure and sharp grain boundaries. DC conductivity and current-voltage (I-V) characteristic of TeO2-V2O5-NiO thin films were measured in the temperature range of 300-423K. As nickel oxide (NiO) content increases, the DC conductivity decreases up to two orders in value (10-9-10-11Sṡcm-1). Temperature dependence of conductivity is described using the small polaron hopping (SPH) model as well. Poole-Frenkel effect is observed at high external electric field. The optical absorption spectra of the TeO2-V2O5-NiO thin films were recorded in the wavelength range of 380-1100nm. The absorption coefficient revealed bandgap shrinkage (3.01-2.3eV) and band tail widening, due to an increase in NiO content. Energy dispersive X-ray spectroscopy (EDX) was used to determine elemental composition. In TeO2-V2O5-NiO thin films, the NiO content is around fifth of the initial target.
Energy Technology Data Exchange (ETDEWEB)
Savaloni, Hadi, E-mail: savaloni@khayam.ut.ac.ir [Department of Physics, University of Tehran, North-Kargar Street, Tehran (Iran, Islamic Republic of); Haydari-Nasab, Fatemh; Malmir, Mariam [Department of Physics, University of Tehran, North-Kargar Street, Tehran (Iran, Islamic Republic of)
2011-08-15
Silver chiral nano-flowers with 3-, 4- and 5-fold symmetry were produced using oblique angle deposition method in conjunction with the rotation of sample holder with different speeds at different sectors of each revolution corresponding to symmetry order of the acquired nano-flower. Atomic force microscopy (AFM) and field emission scanning electron microscopy (FESEM), were employed to obtain morphology and nano-structure of the films. Optical characteristics of silver chiral nano-flower thin films were obtained using single beam spectrophotometer with both s- and p-polarization incident light at 30{sup o} and 70{sup o} incidence angles and at different azimuthal angles ({phi}). Optical spectra showed both TM (TDM (transverse dipole mode) and TQM (transverse quadruple mode)) and LM (longitudinal mode) Plasmon resonance peaks. For 3- and 4-fold symmetry chiral nano-flowers the s-polarization extinction spectra obtained at different azimuthal angles did not show significant change in the Plasmon peak position while 5-fold symmetry chiral nano-flower showed a completely different behavior, which may be the result of increased surface anisotropy, so when the {phi} angle is changed the s-polarization response from the surface can change more significantly than that for lower symmetries. In general, for 3-, 4- and 5-fold symmetry chiral nano-flowers a sharp peak at lower wavelengths (<450 nm) is observed in the s-polarization spectra, while in addition to this peak a broad peak at longer wavelengths (i.e., LM) observed in the p-polarization spectra, which is more dominant for 70{sup o} incidence angle.
Fabrication and nano-imprintabilities of Zr-, Pd- and Cu-based glassy alloy thin films
International Nuclear Information System (INIS)
Takenaka, Kana; Saidoh, Noriko; Nishiyama, Nobuyuki; Inoue, Akihisa
2011-01-01
With the aim of investigating nano-imprintability of glassy alloys in a film form, Zr 49 Al 11 Ni 8 Cu 32 , Pd 39 Cu 29 Ni 13 P 19 and Cu 38 Zr 47 Al 9 Ag 6 glassy alloy thin films were fabricated on Si substrate by a magnetron sputtering method. These films exhibit a very smooth surface, a distinct glass transition phenomenon and a large supercooled liquid region of about 80 K, which are suitable for imprinting materials. Moreover, thermal nano-imprintability of these obtained films is demonstrated by using a dot array mold with a dot diameter of 90 nm. Surface observations revealed that periodic nano-hole arrays with a hole diameter of 90 nm were successfully imprinted on the surface of these films. Among them, Pd-based glassy alloy thin film indicated more precise pattern imprintability, namely, flatter residual surface plane and sharper hole edge. It is said that these glassy alloy thin films, especially Pd-based glassy alloy thin film, are one of the promising materials for fabricating micro-machines and nano-devices by thermal imprinting.
International Nuclear Information System (INIS)
Ben-David, E.; Landa, M.; Janovská, M.; Seiner, H.; Gutman, O.; Tepper-Faran, T.; Shilo, D.
2015-01-01
This paper presents a comprehensive study of the relationships between deposition conditions, microstructure and mechanical behavior in thin aluminum films commonly used in micro and nano-devices. A particular focus is placed on the effect of porosity, which is present in all thin films deposited by evaporation or sputtering techniques. The influences of the deposition temperature on the grain size, pore size and crystallographic texture were characterized by X-ray diffraction and scanning electron microscopy. The mechanical behavior of the films was investigated using four different methods. Each method is suitable for characterizing different properties and for testing the material at different length scales. Nanoindentation was used to study hardness at the level of individual grains; resonant ultrasound spectroscopy was used to measure the elastic moduli and porosity; and bulge and tensile tests were used to study released films under biaxial and uniaxial tensions. Our results demonstrate that even low porosities may have tremendous effects on the mechanical properties and that different methods allow the capture of different aspects of these effects. Therefore, a combination of several methods is required to obtain a comprehensive understanding of the mechanical behavior of a film. It is also shown that porosity with different pore size leads to very different effects on the mechanical behavior
International Nuclear Information System (INIS)
Huang, Ming; Zhuo, Longchao; Liu, Zhanli; Lu, Xiaogang; Shi, Zhenxue; Li, Jiarong; Zhu, Jing
2015-01-01
The mechanical properties of nickel-based single crystal superalloys deteriorate with increasing misorientation, thus the finished product rate of the casting of single crystal turbine airfoils may be reduced due to the formation of grain boundaries especially when the misorientation angle exceeds to some extent. To this day, evolution of the microstructures at the grain boundaries with misorientation and the relationship between the microstructures and the mechanical properties are still unclear. In this work a detailed characterization of the misorientation related microstructure at the grain boundary in DD6 single crystal superalloy has been carried out using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques; the elemental distribution at the grain boundaries has been analyzed by energy dispersive (EDS) X-ray mapping; and the effect of precipitation of μ phases at the grain boundary on the mechanical property has been evaluated by finite element calculation. It is shown that the proportion of γ phase at the grain boundaries decreases, while the proportion of γ′ phase at the grain boundaries increases with increasing misorientation; the μ phase is precipitated at the grain boundaries when the misorientation angle exceeds about 10° and thus it could lead to a dramatic deterioration of the mechanical properties, as well as that the enrichment of Re and W gradually disappears as the misorientation angle increases. All these factors may result in the degradation of the mechanical properties at the grain boundaries as the misorientation increases. Furthermore, the finite element calculation confirms that precipitation of μ phases at the grain boundary is responsible for the significant deterioration of the mechanical properties when the misorientation exceeds about 10°. This work provides a physical imaging of the microstructure for understanding the relationship between the mechanical properties and the misorientation
International Nuclear Information System (INIS)
Kahng, Yung Ho; Choe, Minhyeok; Jo, Gunho; Park, Woojin; Yoon, Jongwon; Hong, Woong-Ki; Lee, Byoung Hun; Lee, Takhee; Lee, Sangchul; Cho, Chun Hum
2011-01-01
Large-area graphene films, synthesized by the chemical vapor deposition (CVD) method, have the potential to be used as electrodes. However, the electrical properties of CVD-synthesized graphene films fall short of the best results obtained for graphene films prepared by other methods. Therefore, it is important to understand the reason why these electrical properties are inferior to improve the applicability of CVD-grown graphene films. Here, we show that CVD-grown graphene films on nickel substrates contain many small-base-area (SBA) peaks that scatter conducting electrons, thereby decreasing the Hall mobility of charges in the films. These SBA peaks were induced by small peaks on the nickel surface and are likely composed of amorphous carbon. The formation of these SBA peaks on graphene films was successfully suppressed by controlling the surface morphology of the nickel substrate. These findings may be useful for the development of a CVD synthesis method that is capable of producing better quality graphene films with large areas.
Inkjet-printed p-type nickel oxide thin-film transistor
Hu, Hailong; Zhu, Jingguang; Chen, Maosheng; Guo, Tailiang; Li, Fushan
2018-05-01
High-performance inkjet-printed nickel oxide thin-film transistors (TFTs) with Al2O3 high-k dielectric have been fabricated using a sol-gel precursor ink. The "coffee ring" effect during the printing process was facilely restrained by modifying the viscosity of the ink to control the outward capillary flow. The impacts on the device performance was studied in detail in consideration of annealing temperature of the nickel oxide film and the properties of dielectric layer. The optimized switching ability of the device were achieved at an annealing temperature of 280 °C on a 50-nm-thick Al2O3 dielectric layer, with a hole mobility of 0.78 cm2/V·s, threshold voltage of -0.6 V and on/off current ratio of 5.3 × 104. The as-printed p-type oxide TFTs show potential application in low-cost, large-area complementary electronic devices.
Metal nano-film resistivity chemical sensor
Czech Academy of Sciences Publication Activity Database
Podešva, Pavel; Foret, František
2016-01-01
Roč. 37, č. 3 (2016), s. 392-397 ISSN 0173-0835 R&D Projects: GA ČR(CZ) GBP206/12/G014 Institutional support: RVO:68081715 Keywords : adsorption * chemiresistor * nano-film * thiol binding * thiol sensing Subject RIV: CB - Analytical Chemistry, Separation Impact factor: 2.744, year: 2016
Electrical and optical properties of sub-10 nm nickel silicide films for silicon solar cells
International Nuclear Information System (INIS)
Brahmi, Hatem; Ravipati, Srikanth; Yarali, Milad; Wang, Weijie; Ryou, Jae-Hyun; Mavrokefalos, Anastassios; Shervin, Shahab
2017-01-01
Highly conductive and transparent films of ultra-thin p-type nickel silicide films have been prepared by RF magnetron sputtering of nickel on silicon substrates followed by rapid thermal annealing in an inert environment in the temperature range 400–600 °C. The films are uniform throughout the wafer with thicknesses in the range of 3–6 nm. The electrical and optical properties are presented for nickel silicide films with varying thickness. The Drude–Lorentz model and Fresnel equations were used to calculate the dielectric properties, sheet resistance, absorption and transmission of the films. These ultrathin nickel silicide films have excellent optoelectronic properties for p-type contacts with optical transparencies up to 80% and sheet resistance as low as ∼0.15 µΩ cm. Furthermore, it was shown that the use of a simple anti-reflection (AR) coating can recover most of the reflected light approaching the values of a standard Si solar cell with the same AR coating. Overall, the combination of ultra-low thickness, high transmittance, low sheet resistance and ability to recover the reflected light by utilizing standard AR coating makes them ideal for utilization in silicon based photovoltaic technologies as a p-type transparent conductor. (paper)
Electrical and optical properties of sub-10 nm nickel silicide films for silicon solar cells
Brahmi, Hatem; Ravipati, Srikanth; Yarali, Milad; Shervin, Shahab; Wang, Weijie; Ryou, Jae-Hyun; Mavrokefalos, Anastassios
2017-01-01
Highly conductive and transparent films of ultra-thin p-type nickel silicide films have been prepared by RF magnetron sputtering of nickel on silicon substrates followed by rapid thermal annealing in an inert environment in the temperature range 400-600 °C. The films are uniform throughout the wafer with thicknesses in the range of 3-6 nm. The electrical and optical properties are presented for nickel silicide films with varying thickness. The Drude-Lorentz model and Fresnel equations were used to calculate the dielectric properties, sheet resistance, absorption and transmission of the films. These ultrathin nickel silicide films have excellent optoelectronic properties for p-type contacts with optical transparencies up to 80% and sheet resistance as low as ~0.15 µΩ cm. Furthermore, it was shown that the use of a simple anti-reflection (AR) coating can recover most of the reflected light approaching the values of a standard Si solar cell with the same AR coating. Overall, the combination of ultra-low thickness, high transmittance, low sheet resistance and ability to recover the reflected light by utilizing standard AR coating makes them ideal for utilization in silicon based photovoltaic technologies as a p-type transparent conductor.
Grain-size effect on the electrical properties of nanocrystalline indium tin oxide thin films
Energy Technology Data Exchange (ETDEWEB)
Lee, Jong Hoon [Korea Research Institute of Standards and Science, 267 Gajeong-Ro, Yuseong-Gu, Daejeon 305-340 (Korea, Republic of); Kim, Young Heon, E-mail: young.h.kim@kriss.re.kr [Korea Research Institute of Standards and Science, 267 Gajeong-Ro, Yuseong-Gu, Daejeon 305-340 (Korea, Republic of); University of Science & Technology, 217 Gajeong-Ro, Yuseong-Gu, Daejeon 305-350 (Korea, Republic of); Ahn, Sang Jung [Korea Research Institute of Standards and Science, 267 Gajeong-Ro, Yuseong-Gu, Daejeon 305-340 (Korea, Republic of); University of Science & Technology, 217 Gajeong-Ro, Yuseong-Gu, Daejeon 305-350 (Korea, Republic of); Ha, Tae Hwan [University of Science & Technology, 217 Gajeong-Ro, Yuseong-Gu, Daejeon 305-350 (Korea, Republic of); Future Biotechnology Research Division, Korea Research Institute of Bioscience and Biotechnology (KRIBB), 125 Gwahak-ro, Yuseong-Gu, Daejeon 305-806 (Korea, Republic of); Kim, Hong Seung [Department of Nano Semiconductor Engineering, Korea Maritime and Ocean University, 727 Taejong-Ro, Busan 606-791 (Korea, Republic of)
2015-09-15
Highlights: • Nanometer-sized small grains were observed in the ITO thin films. • The grain size increased as the post-thermal annealing temperature increased. • The mobility of ITO thin films increased with increasing grain size. • The ITO film annealed at 300 °C was an amorphous phase, while the others were polycrystalline structure. - Abstract: In this paper, we demonstrate the electrical properties, depending on grain size, of nanocrystalline indium tin oxide (ITO) thin films prepared with a solution process. The size distributions of nanometer-sized ITO film grains increased as the post-annealing temperature increased after deposition; the grain sizes were comparable with the calculated electron mean free path. The mobility of ITO thin films increased with increasing grain size; this phenomenon was explained by adopting the charge-trapping model for grain boundary scattering. These findings suggest that it is possible to improve mobility by reducing the number of trapping sites at the grain boundary.
Effect of nano-silver hydrogel coating film on deep partial thickness scald model of rabbit
Directory of Open Access Journals (Sweden)
Peng Xi
2018-05-01
Full Text Available Objective: Observing the effect of nano-silver hydrogel coating film on deep partial thickness scald model of rabbit. Method: We prepared boiling water scalded rabbits with deep II degree scald models and applied high, medium and low doses of nano-silver hydrogel coating film for different time and area. Then we compared the difference of burned paper weight before administration and after administration model burns, burn local skin irritation points infection, skin crusting and scabs from the time, and the impact of local skin tissue morphology. Result: Rabbits deep II degree burn model successful modeling; on day 12, 18, high, medium and low doses of nano-silver hydrogel coating film significantly reduced skin irritation of rabbits infected with the integral value (P < 0.01, P < 0.05; high, medium and low doses of nano-silver hydrogel coating film group significantly decreased skin irritation, infection integral value (P < 0.01, P < 0.05; high, medium and low doses of nano-silver hydrogel coating film significantly reduced film rabbits’ scalded skin crusting time (P < 0.01, significantly shortened the rabbit skin burns from the scab time (P < 0.01, and significantly improved the treatment of skin diseases in rabbits scald model change (P < 0.01, P < 0.05. Conclusion: The nano-silver hydrogel coating film on the deep partial thickness burns has a significant therapeutic effect; external use has a significant role in wound healing. Keywords: Nano-silver hydrogel coating film, Deep degree burns, Topical, Rabbits
Layer-dependent supercapacitance of graphene films grown by chemical vapor deposition on nickel foam
Chen, Wei
2013-03-01
High-quality, large-area graphene films with few layers are synthesized on commercial nickel foams under optimal chemical vapor deposition conditions. The number of graphene layers is adjusted by varying the rate of the cooling process. It is found that the capacitive properties of graphene films are related to the number of graphene layers. Owing to the close attachment of graphene films on the nickel substrate and the low charge-transfer resistance, the specific capacitance of thinner graphene films is almost twice that of the thicker ones and remains stable up to 1000 cycles. These results illustrate the potential for developing high-performance graphene-based electrical energy storage devices. © 2012 Elsevier B.V. All rights reserved.
Rare-earth nickelates RNiO3: thin films and heterostructures
Catalano, S.; Gibert, M.; Fowlie, J.; Íñiguez, J.; Triscone, J.-M.; Kreisel, J.
2018-04-01
This review stands in the larger framework of functional materials by focussing on heterostructures of rare-earth nickelates, described by the chemical formula RNiO3 where R is a trivalent rare-earth R = La, Pr, Nd, Sm, …, Lu. Nickelates are characterized by a rich phase diagram of structural and physical properties and serve as a benchmark for the physics of phase transitions in correlated oxides where electron–lattice coupling plays a key role. Much of the recent interest in nickelates concerns heterostructures, that is single layers of thin film, multilayers or superlattices, with the general objective of modulating their physical properties through strain control, confinement or interface effects. We will discuss the extensive studies on nickelate heterostructures as well as outline different approaches to tuning and controlling their physical properties and, finally, review application concepts for future devices.
Energy Technology Data Exchange (ETDEWEB)
Tiggelaar, R.M. [Mesoscale Chemical Systems, MESA" + Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500 AE Enschede (Netherlands); Thakur, D.B.; Nair, H.; Lefferts, L.; Seshan, K. [Catalytic Processes and Materials, MESA" + Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500 AE Enschede (Netherlands); Gardeniers, J.G.E., E-mail: j.g.e.gardeniers@utwente.nl [Mesoscale Chemical Systems, MESA" + Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500 AE Enschede (Netherlands)
2013-05-01
Nickel and other metal nanoparticles are known to be active as catalysts in the synthesis of carbon nanofibers. In this paper we investigate how dewetting and break-up of nickel thin films depends on film thickness, film–substrate interaction and pretreatment conditions. This is evaluated for films evaporated on oxidized silicon and fused silica substrates with or without tantalum coating, which were subsequently exposed to different pretreatment atmospheres (vacuum, nitrogen, air and hydrogen; 1 h, 650 °C). Atomic force microscopy, scanning electron microscopy and energy dispersive X-ray analysis were used to characterize the films. Pretreated Ni films were subjected to a thermal catalytic chemical vapor deposition procedure with brief ethylene exposures (0.5–3 min, 635 °C). It was found that only on the spherical nanoparticles originating from a hydrogen pretreatment of a Ni film with Ta adhesion layer, homogeneously distributed, randomly-oriented, well-attached, and semi-crystalline carbon nanofibers be synthesized. - Highlights: • On the formation of nanoparticles required for carbon nanofiber (CNF) synthesis • Various evaporated thin films on oxidized silicon and fused silica: Ni and Ni/Ta • Pretreatment of nickel-based thin films in vacuum, nitrogen, air and hydrogen • Only on reduced Ni/Ta fast – within 3 min – initiation of CNF nucleation and growth.
Directory of Open Access Journals (Sweden)
M. R. Islam
2011-11-01
Full Text Available Nano fiber ZnO films have been deposited on to glass substrate at 200 °C by a simple spray pyrolysis technique under atmospheric pressure. The effect of annealing temperature on the structural and optical properties of the as grown films has been studied by Scanning Electron Microscopy (SEM attached with an EDX, powder X-ray diffraction and UV visible spectroscopy. The atomic weight % of Zinc and Oxygen were found to be 49.22 % and 49.62 % respectively. The SEM micrographs show nano fiber structure and uniform deposition on the substrate. Average grain size of ZnO thin film was found in the range of 21 to 27 nm. The lattice constant a and c of ZnO thin film are determined at different annealing temperatures and values are found slightly larger than those of JCPDS data and lower for the sample annealed at 600 °C. The lattice parameters a and c decrease with increasing temperature. It reveals that the samples are poly-crystalline and having with low densities. Band gap energy of ZnO was found in the range of 3.33 to 3.17 eV and decreases with the increase of the annealing temperature.
Preparation of BiOBr thin films with micro-nano-structure and their photocatalytic applications
Energy Technology Data Exchange (ETDEWEB)
Li, Rui [College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Fan, Caimei, E-mail: fancm@163.com [College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Zhang, Xiaochao, E-mail: zhang13598124761@163.com [College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Wang, Yawen; Wang, Yunfang [College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Zhang, Hui [Particle Technology Research Centre, Department of Chemical and Biochemical Engineering, The University of Western Ontario, London, Ontario N6A 5B9 (Canada)
2014-07-01
A series of micro-nano-structure BiOBr thin films were prepared at a low temperature by the alcoholysis-coating method using BiBr{sub 3} as precursor. The as-prepared films were characterized by X-ray powder diffraction, scanning electron microscopy, and Brunauer–Emmett–Teller surface area. The obtained results indicated that micro-nano-structure tetragonal BiOBr films with different intensity ratios of (110) to (102) characteristic peaks could be synthesized through controlling the reaction temperature and the calcination temperatures. Furthermore, the photocatalytic activities of BiOBr thin films with different preparation conditions have been evaluated by the degradation of methyl orange (MO) under UV light irradiation, suggesting that the photocatalytic activity should be closely related to the solvent, the alcoholysis reaction temperature, and the calcining temperature. The best photocatalytic degradation efficiency of MO for BiOBr thin films reaches 98.5% under 2.5 h UV irradiation. The BiOBr thin films display excellent stability and their photocatalytic activity still remains above 90% after being used five times. The main reasons for the higher photocatalytic activity of micro-nano-structure BiOBr microspheres have been investigated. In addition, the possible formation mechanism of BiOBr thin films with micro-nano-structure and excellent photocatalytic activity was proposed and discussed. - Highlights: • The BiOBr film was prepared at low temperature via alcoholysis-coating method. • The optimum process conditions of preparing BiOBr film were discussed. • As-prepared BiOBr films were composed of micro-nano flake structures. • The BiOBr films demonstrated excellent photocatalytic activity. • The formation mechanism of BiOBr films with high activity was proposed.
Correlated XANES, TEM, and NanoSIMS of presolar graphite grains
Groopman, Evan E.; Nittler, Larry R.
2018-01-01
We report correlated XANES, TEM, and NanoSIMS measurements of twelve presolar graphite grains extracted from primitive meteorites and for which isotopic data indicate predominantly Type-II supernovae origins. We find continued evidence for isotopic heterogeneities in presolar graphite grains, including the first observation of a radial gradient in the inferred initial 26Al/27Al within a presolar graphite grain. The XANES spectra of these samples show a variety of minor absorbances near the C K-edge, attributable to vinyl-keto, aliphatic, carboxyl, and carbonate molecules, as well as possible damage during sample preparation. Each sample exhibits homogeneous C K-edge XANES spectra within the graphite, however, showing no correlation with isotopic heterogeneities. Gradients in the isotope ratios of C, N, O, and Al could be due to both processes during condensation, e.g., mixing in stellar ejecta and granular transport, and post-condensation effects, such as isotope dilution and exchange with isotopically normal material in the early Solar System or laboratory, the latter of which is a significant issue for high-density presolar graphite grains. It remains unknown whether the mechanisms behind isotope exchange would also affect the local chemistry and therefore the XANES spectra. Ti L-edge XANES from most Ti-rich subgrains match standard spectra for TiC and potentially TiCN. A rare rutile (TiO2) subgrain has been identified, though it lacks the lowest energy L3 peak typically seen in standard spectra. Ca has also been identified by EDXS in TiC subgrains, likely due to the decay of live 44Ti at the time of formation. Future NanoSIMS measurements will determine the variability of initial 44Ti in TiC subgrains, an important constraint on mixing in the ejecta of the grains' parent supernovae.
Ultrathin and stable Nickel films as transparent conductive electrodes
Energy Technology Data Exchange (ETDEWEB)
Grilli, M.L., E-mail: marialuisa.grilli@enea.it [ENEA, Materials Technology Unit, Via Anguillarese 301, 00123 Rome (Italy); Di Sarcina, I. [ENEA, Materials Technology Unit, Via Anguillarese 301, 00123 Rome (Italy); Bossi, S. [ENEA, Robotics Laboratory, Via Anguillarese 301, 00123 Rome (Italy); The Biorobotics Institute, Scuola Superiore Sant' Anna, Viale Rinaldo Piaggio 34, 56025 Pontedera, Pisa (Italy); Rinaldi, A.; Pilloni, L.; Piegari, A. [ENEA, Materials Technology Unit, Via Anguillarese 301, 00123 Rome (Italy)
2015-11-02
Ultrathin stable transparent conductive nickel films were deposited on quartz substrates by radio frequency sputtering at room temperature. Such films showed visible transmittance up to 80% and conductivity up to 1.8 × 10{sup 4} S/cm, further increased to 2,3 × 10{sup 5} S/cm by incorporation of a micrometric silver grid. Atomic force microscopy and scanning electron microscopy revealed quite compact, smooth and low surface roughness films. Excellent film stability, ease, fast and low cost process fabrication make these films highly competitive compared to indium tin oxide alternative transparent conductors. Films were characterized regarding their morphological, optical and electrical properties. - Highlights: • Indium-free transparent conductors are proposed. • Ultrathin Ni films are fabricated with a very fast process at room temperature. • Films have conductivity values up to 1.8 × 10{sup 4} S/cm. • Ni ultrathin films are good candidates for UV and NIR optoelectronic applications.
Grain Growth in Nanocrystalline Mg-Al Thin Films
Energy Technology Data Exchange (ETDEWEB)
Kruska, Karen; Rohatgi, Aashish; Vemuri, Venkata Rama Ses; Kovarik, Libor; Moser, Trevor H.; Evans, James E.; Browning, Nigel D.
2017-10-05
An improved understanding of grain growth kinetics in nanocrystalline materials, and in metals and alloys in general, is of continuing interest to the scientific community. In this study, Mg - Al thin films containing ~10 wt.% Al and with 14.5 nm average grain size were produced by magnetron-sputtering and subjected to heat-treatments. The grain growth evolution in the early stages of heat treatment at 423 K (150 °C), 473 K (200 °C) and 573K (300 °C) was observed with transmission electron microscopy and analyzed based upon the classical equation developed by Burke and Turnbull. The grain growth exponent was found to be 7±2 and the activation energy for grain growth was 31.1±13.4 kJ/mol, the latter being significantly lower than in bulk Mg-Al alloys. The observed grain growth kinetics are explained by the Al supersaturation in the matrix and the pinning effects of the rapidly forming beta precipitates and possibly shallow grain boundary grooves. The low activation energy is attributed to the rapid surface diffusion which is dominant in thin film systems.
Energy Technology Data Exchange (ETDEWEB)
Riedel, Hermann, E-mail: hermann.riedel@iwm.fraunhofer.de [Fraunhofer Institute for Materials Mechanics, Wöhlerstr. 11, 79108 Freiburg (Germany); Svoboda, Jiri, E-mail: svobj@ipm.cz [Institute of Physics of Materials, Academy of Science of the Czech Republic, Zizkova 22, Brno (Czech Republic)
2016-05-17
An ensemble of n spherical grains is considered, each of which is characterized by its radius r{sub i} and by a hardening variable a{sub i}. The hardening variable obeys a Chaboche-type evolution equation with dynamic and static recovery. The grain growth law includes the usual contribution of the grain boundary energy, a term for the stored energy associated with the hardening variable, and the Zener pinning force exerted by particles on the migrating grain boundaries. New grains develop by recrystallization in grains whose stored energy density exceeds a critical value. The growth or shrinkage of the particles, which restrain grain boundary migration, obeys a thermodynamic/kinetic evolution equation. This set of first order differential equations for r{sub i}, a{sub i} and the particle radius is integrated numerically. Fictitious model parameters for a virtual nickel base alloy are used to demonstrate the properties and capabilities of the model. For a real nickel alloy, model parameters are adjusted using measured stress-strain curves, as well as recrystallized volume fractions and grain size distributions. Finally the model with adjusted parameters is applied to a forming process with complex temperature-strain rate histories.
Development of helium porosity near-by grain boundaries in nickel-carbon alloys
International Nuclear Information System (INIS)
Reutov, I.V.; Reutov, V.F.
1995-01-01
The peculiarities of development of helium porosity near grain boundaries in nickel with 0.002-0.065 at.% carbon uniformly doped with helium up to 2·10 -2 at.% in the process of post-irradiation isothermal annealing at 800 deg C for 1-50 hours are studied. It is stated that at this annealing temperature intensive nucleation and growth of bubbles are observed in near-boundary region whose width grows both with increase of annealing time and carbon content. The TEM studies have shown that in near-boundary zone itself the process of bubble growth is non-uniform: bubble size increases and their density decreases as the distance from grain boundary is increased. The effect observed is discussed from the point of view of formation of two zones with different level of swelling in a grain (near-by boundary and matrix) and consequently, hydrostatic stress as well conditioning the flux of vacancies and helium-vacancy complexes from matrix to grain boundary. 8 refs., 5 figs
Directory of Open Access Journals (Sweden)
Mohammad Shirdel
2015-06-01
Full Text Available Austenitic stainless steels are extensively used in various applications requiring good corrosion resistance and formability. In the current study, the formation of nano/ ultrafine grained austenitic microstructure in a microalloyed AISI 304L stainless steel was investigated by the advanced thermomechanical process of reversion of strain-induced martensite. For this purpose, samples were subjected to heavy cold rolling to produce a nearly complete martensitic structure. Subsequently, a wide range of annealing temperatures (600 to 800°C and times (1 to 240 min were employed to assess the reversion behavior and to find the best annealing condition for the production of the nano/ultrafine grained austenitic microstructure. Microstructural characterizations have been performed using X-ray diffraction (XRD, scanning electron microscopy (SEM, and magnetic measurement, whereas the mechanical properties were assessed by tensile and hardness tests. After thermomechanical treatment, a very fine austenitic structure was obtained, which was composed of nano sized grains of ~ 85 nm in an ultrafine grained matrix with an average grain size of 480 nm. This microstructure exhibited superior mechanical properties: high tensile strength of about 1280 MPa with a desirable elongation of about 41%, which can pave the way for the application of these sheets in the automotive industry.
Energy Technology Data Exchange (ETDEWEB)
Magana, C. R.; Angeles, M. E.; Rodriguez, F. J.
2006-07-01
The aim of this work is to study the behaviour of both: a nickel thin film deposited on steel AISI 1018 (UNS G 10180) and a superior nickel oxide electrochemically obtained on the film; with the purpose of decreasing the corrosion rate of low carbon steel immersed in a solution of NaCl 3% wt, thus efficient anti corrosive protection could be obtained. Two film deposition techniques were used, electrochemical and magnetron DC sputtering; and the protective properties of deposited films exposed to the aggressive media, were evaluated. The characterization of different films was carried out by using electrochemical techniques: polarization curves and electrochemical impedance. (Author)
Voltammetric and impedance behaviours of surface-treated nano-crystalline diamond film electrodes
International Nuclear Information System (INIS)
Liu, F. B.; Jing, B.; Cui, Y.; Di, J. J.; Qu, M.
2015-01-01
The electrochemical performances of hydrogen- and oxygen-terminated nano-crystalline diamond film electrodes were investigated by cyclic voltammetry and AC impedance spectroscopy. In addition, the surface morphologies, phase structures, and chemical states of the two diamond films were analysed by scanning probe microscopy, Raman spectroscopy, and X-ray photoelectron spectroscopy, respectively. The results indicated that the potential window is narrower for the hydrogen-terminated nano-crystalline diamond film than for the oxygen-terminated one. The diamond film resistance and capacitance of oxygen-terminated diamond film are much larger than those of the hydrogen-terminated diamond film, and the polarization resistances and double-layer capacitance corresponding to oxygen-terminated diamond film are both one order of magnitude larger than those corresponding to the hydrogen-terminated diamond film. The electrochemical behaviours of the two diamond film electrodes are discussed
Columnar grain growth of FePt(L10) thin films
International Nuclear Information System (INIS)
Yang En; Ho Hoan; Laughlin, David E.; Zhu Jiangang
2012-01-01
An experimental approach for obtaining perpendicular FePt-SiOx thin films with a large height to diameter ratio FePt(L1 0 ) columnar grains is presented in this work. The microstructure for FePt-SiOx composite thin films as a function of oxide volume fraction, substrate temperature, and film thickness is studied by plan view and cross section TEM. The relations between processing, microstructure, epitaxial texture, and magnetic properties are discussed. By tuning the thickness of the magnetic layer and the volume fraction of oxide in the film at a sputtering temperature of 410 deg. C, a 16 nm thick perpendicular FePt film with ∼8 nm diameter of FePt grains was obtained. The height to diameter ratio of the FePt grains was as large as 2. Ordering at lower temperature can be achieved by introducing a Ag sacrificial layer.
Determination of grain size by XRD profile analysis and TEM counting in nano-structured Cu
International Nuclear Information System (INIS)
Zhong Yong; Ping Dehai; Song Xiaoyan; Yin Fuxing
2009-01-01
In this work, a serial of pure copper sample with different grain sizes from nano- to micro-scale were prepared by sparkle plasma sintering (SPS) and following anneal treatment at 873 K and 1073 K, respectively. The grain size distributions of these samples were determined by both X-ray diffraction (XRD) profile analysis and transmission electronic microscope (TEM) micrograph counting. Although these two methods give similar distributions of grain size in the case of as-SPS sample with nano-scale grain size (around 10 nm), there are apparent discrepancies between the grain size distributions of the annealed samples obtained from XRD and TEM, especially for the sample annealed at 1073 K after SPS with micro-scale grain size (around 2 μm), which TEM counting provides much higher values of grain sizes than XRD analysis does. It indicates that for large grain-sized material, XRD analysis lost its validity for determination of grain size. It might be due to some small sized substructures possibly existed in even annealed (large grain-sized) samples, whereas there is no substructures in as-SPS (nanocrystalline) sample. Moreover, it has been found that the effective outer cut-off radius R e derived from XRD analysis coincides with the grain sizes given by TEM counting. The potential relationship between grain size and R e was discussed in the present work. These results might provide some new hints for deeper understanding of the physical meaning of XRD analysis and the parameters derived.
International Nuclear Information System (INIS)
Bhaskaran, M; Sriram, S; Sim, L W
2008-01-01
This paper studies the feasibility of using titanium and nickel silicide thin films as mask materials for silicon bulk micro-machining. Thin films of nickel silicide were found to be more resistant to wet etching in potassium hydroxide. The use of nickel silicide as a structural material, by fabricating micro-beams of varying dimensions, is demonstrated. The micro-structures were realized using these thin films with wet etching using potassium hydroxide solution on (1 0 0) and (1 1 0) silicon substrates. These results show that nickel silicide is a suitable alternative to silicon nitride for silicon bulk micro-machining
Structural and magnetic studies of Cr doped nickel ferrite thin films
International Nuclear Information System (INIS)
Panwar, Kalpana; Heda, N. L.; Tiwari, Shailja; Bapna, Komal; Ahuja, B. L.; Choudhary, R. J.; Phase, D. M.
2016-01-01
We have studied the structural and magnetic properties of Cr doped nickel ferrite thin films deposited on Si (100) and Si (111) using pulsed laser deposition technique. The films were deposited under vacuum and substrate temperature was kept at 700°C. X-ray diffraction analysis revealed that films on both substrates have single phase cubic spinel structure. However, the film grown on Si (111) shows better crystalline behavior. Fourier transform infrared spectroscopy suggests that films on both substrates have mixed spinel structure. These films show magnetic hysteresis behavior and magnetization value of film on Si (100) is larger than that on Si (111). It turns out that structural and magnetic properties of these two films are correlated.
International Nuclear Information System (INIS)
Yoshida, Masaaki; Iida, Tsuyoshi; Mineo, Takehiro
2014-01-01
The electrochromic transition of a nickel borate thin film between colorless and brown was examined by means of in situ XAFS and UV/vis spectroscopy. The XAFS spectra showed that the average valence state of the nickel species in the film changed from +2.1 to +3.8 following the application of an electrode potential. Additionally, a broad peak at 700 nm was observed during in situ UV/vis absorption measurements on the application of a positive potential. These results suggest that the nickel borate film reversibly forms a NiOOH structure with a domain size of several nanometers during the electrochromic reaction. (author)
Electrodeposited Ni nanowires-track etched P.E.T. composites as selective solar absorbers
Lukhwa, R.; Sone, B.; Kotsedi, L.; Madjoe, R.; Maaza, M.
2018-05-01
This contribution reports on the structural, optical and morphological properties of nanostructured flexible solar-thermal selective absorber composites for low temperature applications. The candidate material in the system is consisting of electrodeposited nickel nano-cylinders embedded in track-etched polyethylene terephthalate (PET) host membrane of pore sizes ranging between 0.3-0.8µm supported by conductive nickel thin film of about 0.5µm. PET were irradiated with 11MeV/u high charged xenon (Xe) ions at normal incidence. The tubular and metallic structure of the nickel nano-cylinders within the insulator polymeric host forms a typical ceramic-metal nano-composite "Cermet". The produced material was characterized by the following techniques: X-ray diffraction (XRD) for structural characterization to determine preferred crystallographic structure, and grain size of the materials; Scanning electron microscopy (SEM) to determine surface morphology, particle size, and visual imaging of distribution of structures on the surface of the substrate; Atomic force microscopy (AFM) to characterize surface roughness, surface morphology, and film thickness, and UV-Vis-NIR spectrophotometer to measure the reflectance, then to determine solar absorption
Optical Properties and Surface Morphology of Nano-composite PMMA: TiO2 Thin Films
International Nuclear Information System (INIS)
Lyly Nyl Ismail; Ahmad Fairoz Aziz; Habibah Zulkefle
2011-01-01
There are two nano-composite PMMA: TiO 2 solutions were prepared in this research. First solution is nano-composite PMMA commercially available TiO 2 nanopowder and the second solution is nano-composite PMMA with self-prepared TiO 2 powder. The self-prepared TiO 2 powder is obtained by preparing the TiO 2 sol-gel. Solvo thermal method were used to dry the TiO 2 sol-gel and obtained TiO 2 crystal. Ball millers were used to grind the TiO 2 crystal in order to obtained nano sized powder. Triton-X was used as surfactant to stabilizer the composite between PMMA: TiO 2 . Besides comparing the nano-composite solution, we also studied the effect of the thin films thickness on the optical properties and surface morphology of the thin films. The thin films were deposited by sol-gel spin coating method on glass substrates. The optical properties and surface characterization were measured with UV-VIS spectrometer equipment and atomic force microscopy (AFM). The result showed that nano-composite PMMA with self prepared TiO 2 give high optical transparency than nano-composite PMMA with commercially available TiO 2 nano powder. The results also indicate as the thickness is increased the optical transparency are decreased. Both AFM images showed that the agglomerations of TiO 2 particles are occurred on the thin films and the surface roughness is increased when the thickness is increased. High agglomeration particles exist in the AFM images for nano-composite PMMA: TiO 2 with TiO 2 nano powder compare to the other nano-composite solution. (author)
Characterisation of nano-grains in MgB2 superconductors by transmission Kikuchi diffraction
International Nuclear Information System (INIS)
Wong, D.C.K.; Yeoh, W.K.; Trimby, P.W.; De Silva, K.S.B.; Bao, P.; Li, W.X.; Xu, X.; Dou, S.X.; Ringer, S.P.; Zheng, R.K.
2015-01-01
We report the first application of the emerging transmission Kikuchi diffraction technique in the scanning electron microscope to investigate nano-grain structures in polycrystalline MgB 2 superconductors. Two sintering conditions were considered, and the resulting differences in superconducting properties are correlated to differences in grain structure. A brief comparison to X-ray diffraction results is presented and discussed. This work focusses more on the application of this technique to reveal grain structure, rather than on the detailed differences between the two sintering temperatures
Energy Technology Data Exchange (ETDEWEB)
Moallemi, Mohammad; Najafizadeh, Abbas; Kermanpur, Ahmad [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Rezaee, Ahad, E-mail: a.rezaee@ma.iut.ac.ir [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of)
2011-12-15
Highlights: Black-Right-Pointing-Pointer The secondary increase in the martensite content after reversion annealing. Black-Right-Pointing-Pointer Formation of thermally induced martensite due to carbide precipitation. Black-Right-Pointing-Pointer The smallest average grain size of 70 nm is achieved by annealing at 850 Degree-Sign C for 15 s. Black-Right-Pointing-Pointer A fully austenitic structure with grain size of 100 nm and 1370 MPa yield strength. - Abstract: The formation of nano/ultrafine grain structure in a 201 austenitic stainless steel was investigated by the martensite thermomechanical treatment. Cast ingots were first homogenized, then hot-forged and solution-annealed to reduce the initial grain size. Cold rolling was then conducted down to 90% reduction in thickness, followed by reversion annealing at a temperature in the range of 1023-1173 K for 15-1800 s. The effect of reversion parameters on grain refinement was investigated. The resulting microstructures were characterized by a scanning electron microscopy equipped with X-ray energy-dispersive spectrometer, an X-ray diffractometer and a Feritscope. The hardness was measured by the Vickers method. The results show that a nano/ultrafine-grained structure formed in the initial stages of the reversion, but significant grain growth took place during the entire course of reversion. Initially lowered, the volume fraction of martensite increased again during the reversion treatment due to carbide precipitation. A fully austenitic nano grained 201 stainless steel with the average grain size of 100 nm was produced, possessing a yield strength of about 1370 MPa.
Nickel and titanium nanoboride composite coating
International Nuclear Information System (INIS)
Efimova, K A; Galevsky, G V; Rudneva, V V; Kozyrev, N A; Orshanskaya, E G
2015-01-01
Electrodeposition conditions, structural-physical and mechanical properties (microhardness, cohesion with a base, wear resistance, corrosion currents) of electroplated composite coatings on the base of nickel with nano and micro-powders of titanium boride are investigated. It has been found out that electro-crystallization of nickel with boride nanoparticles is the cause of coating formation with structural fragments of small sizes, low porosity and improved physical and mechanical properties. Titanium nano-boride is a component of composite coating, as well as an effective modifier of nickel matrix. Nano-boride of the electrolyte improves efficiency of the latter due to increased permissible upper limit of the cathodic current density. (paper)
Transparent electrode designs based on optimal nano-patterning of metallic films
Catrysse, Peter B.; Fan, Shanhui
2010-01-01
, such as indium tin oxide, are commonly used. There is substantial interest in replacing them, however, motivated by practical problems and recent discoveries regarding the optics of nano-patterned metals. When designing nano-patterned metallic films for use
Energy Technology Data Exchange (ETDEWEB)
Pandey, B., E-mail: pandey.beauty@yahoo.com [Department of Applied Physics, Indian School of Mines, Dhanbad 826004 (India); Das, D. [UGC-DAE CSR, Sector III/LB-8, Bidhan Nagar, Kolkata 700098 (India); Kar, A.K. [Department of Applied Physics, Indian School of Mines, Dhanbad 826004 (India)
2015-05-15
Highlights: • Electrical and magnetic properties of DLC and Ni-DLC thin films are studied. • The ohmicity and conductivity of DLC films rise with nickel addition. • The ohmicity of Ni-DLC is enhanced with increase in dilution of electrolyte. • Dielectric loss is high for Ni-DLC and decreases with frequency till 100 kHz. • (m–H) and (m–T) curves of Ni-DLC indicate superparamagnetic behavior. - Abstract: Nanocomposite diamond-like carbon (DLC) thin films have been synthesized by incorporating nickel (Ni) nanoparticles in DLC matrix with varying concentration of nickel. DLC and Ni-DLC thin films have been deposited on ITO coated glass substrates employing low voltage electrodeposition method. Electrical properties of the samples were studied by measuring current–voltage characteristics and dielectric properties. The current approaches toward an ohmic behavior with metal addition. This tendency of increasing ohmicity is enhanced with increase in dilution of the electrolyte. The conductivity increases with Ni addition and interestingly it continues to increase with dilution of Ni concentration in the electrolyte in the range of our study. Magnetic properties for DLC and Ni-DLC thin film samples were examined by electron paramagnetic resonance (EPR) measurements and Super Conducting Quantum Interference Device (SQUID) measurements. g-Value for DLC is 2.074, whereas it decreases to 2.055 with Ni addition in the electrolyte. This decrement arises from the increased sp{sup 2} content in DLC matrix. The magnetic moment vs. magnetic field (m–H) curves of Ni-DLC indicate superparamagnetic behavior which may be due to ferromagnetic contribution from the incorporated nickel nanoparticles in the DLC matrix. The ZFC curve of Ni-DLC after the blocking temperature shows a combined contribution of ferromagnetic, superparamagnetic and paramagnetic nature of the materials persisting up to 300 K.
DEFF Research Database (Denmark)
Ahmadi, Majid; Younesi, Reza; Vegge, Tejs
2014-01-01
Nickel oxide crystalline nano flakes (NONFs)—only about 10 nm wide—were produced using a simple and inexpensive chemistry method followed by a short annealing in ambient air. In a first step, Ni(OH)2 sheets were synthesized by adding sodium hydroxide (NaOH) drop-wise in a Ni(NO3)2 aqueous solutio...
Magnetically dead layers at sp-impurity-decorated grain boundaries and surfaces in nickel
Czech Academy of Sciences Publication Activity Database
Všianská, Monika; Šob, Mojmír
2011-01-01
Roč. 84, č. 1 (2011), Art.n. 014418 ISSN 1098-0121 R&D Projects: GA AV ČR IAA100100920; GA ČR GD106/09/H035 Institutional research plan: CEZ:AV0Z20410507 Keywords : magnetically dead layers * sp-impurity-decorated grain boundaries and surfaces * nickel Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.691, year: 2011
RICARDO TUCCERI
2018-01-01
The deactivation of nickel hydroxide films after prolonged storage times without use was studied. This study was carried out in the context of the Rotating Disc Electrode Voltammetry (RDEV) and Electrochemical Impedance Spectroscopy (EIS) when the nickel hydroxide film contacts an electroactive solution and a redox reaction occurs at the Au-Ni(OH)2|electrolyte interface. Deferasirox (4-(3,5-bis(2- hydroxyphenyl)-1,2,4-triazol-1-yl) benzoic acid) was employed as redox species in solution. Limi...
Wafer scale nano-membrane supported on a silicon microsieve using thin-film transfer technology
Unnikrishnan, S.; Jansen, Henricus V.; Berenschot, Johan W.; Elwenspoek, Michael Curt
A new micromachining method to fabricate wafer scale nano-membranes is described. The delicate thin-film nano-membrane is supported on a robust silicon microsieve fabricated by plasma etching. The silicon sieve is micromachined independently of the thin-film, which is later transferred onto it by
Molecular dynamics simulations of the embedding of a nano-particle into a polymer film
International Nuclear Information System (INIS)
Ochoa, J G Diaz; Binder, K; Paul, W
2006-01-01
In this work we report on molecular dynamics simulations of the embedding process of a nano-particle into a polymeric film as a function of temperature. This process has been employed experimentally in recent years to test for a shift of the glass transition of a material due to the confined film geometry and to test for the existence of a liquid-like layer on top of a glassy polymer film. The embedding process is governed thermodynamically by the prewetting properties of the polymer on the nano-particle. We show that the dynamics of the process depends on the Brownian motion characteristics of the nano-particle in and on the polymer film. It displays large sample to sample variations, suggesting that it is an activated process. On the timescales of the simulation an embedding of the nano-particle is only observed for temperatures above the bulk glass transition temperature of the polymer, agreeing with experimental observations on noble metal clusters of comparable size
Effect of Nano-Ni Catalyst on the Growth and Characterization of Diamond Films by HFCVD
Directory of Open Access Journals (Sweden)
Chien-Chung Teng
2010-01-01
Full Text Available Four different catalysts, nanodiamond seed, nano-Ni, diamond powder, and mixture of nano-Ni/diamond powder, were used to activate Si wafers for diamond film growth by hot-filament CVD (HFCVD. Diamond crystals were shown to grow directly on both large diamond powder and small nanodiamond seed, but a better crystallinity of diamond film was observed on the ultrasonicated nanodiamond seeded Si substrate. On the other hand, nano-Ni nanocatalysts seem to promote the formation of amorphous carbon but suppress transpolyacetylene (t-PA phases at the initial growth of diamond films. The subsequent nucleation and growth of diamond crystals on the amorphous carbon layer leads to generation of the spherical diamond particles and clusters prior to coalescence into continuous diamond films based on the CH3 addition mechanism as characterized by XRD, Raman, ATR/FT-IR, XPS, TEM, SEM, and AFM techniques. Moreover, a 36% reduction in surface roughness of diamond film assisted by nano-Ni catalyst is quite significant.
Transparent, flexible supercapacitors from nano-engineered carbon films
Jung, Hyun Young; Karimi, Majid B.; Hahm, Myung Gwan; Ajayan, Pulickel M.; Jung, Yung Joon
2012-10-01
Here we construct mechanically flexible and optically transparent thin film solid state supercapacitors by assembling nano-engineered carbon electrodes, prepared in porous templates, with morphology of interconnected arrays of complex shapes and porosity. The highly textured graphitic films act as electrode and current collector and integrated with solid polymer electrolyte, function as thin film supercapacitors. The nanostructured electrode morphology and the conformal electrolyte packaging provide enough energy and power density for the devices in addition to excellent mechanical flexibility and optical transparency, making it a unique design in various power delivery applications.
Directory of Open Access Journals (Sweden)
Castranova Vincent
2009-04-01
Full Text Available Abstract Background Carcinogenicity of nickel compounds has been well documented. However, the carcinogenic effect of metallic nickel is still unclear. The present study investigates metallic nickel nano- and fine particle-induced apoptosis and the signal pathways involved in this process in JB6 cells. The data obtained from this study will be of benefit for elucidating the pathological and carcinogenic potential of metallic nickel particles. Results Using 3-(4,5-dimethylthiazol-2-yl-2,5-diphenyltetrazolium bromide (MTT assay, we found that metallic nickel nanoparticles exhibited higher cytotoxicity than fine particles. Both metallic nickel nano- and fine particles induced JB6 cell apoptosis. Metallic nickel nanoparticles produced higher apoptotic induction than fine particles. Western-blot analysis showed an activation of proapoptotic factors including Fas (CD95, Fas-associated protein with death domain (FADD, caspase-8, death receptor 3 (DR3 and BID in apoptotic cells induced by metallic nickel particles. Immunoprecipitation (IP western blot analysis demonstrated the formation of the Fas-related death-inducing signaling complex (DISC in the apoptotic process. Furthermore, lamin A and beta-actin were cleaved. Moreover, we found that apoptosis-inducing factor (AIF was up-regulated and released from mitochondria to cytoplasm. Interestingly, although an up-regulation of cytochrome c was detected in the mitochondria of metallic nickel particle-treated cells, no cytochrome c release from mitochondria to cytoplasm was found. In addition, activation of antiapoptotic factors including phospho-Akt (protein kinase B and Bcl-2 was detected. Further studies demonstrated that metallic nickel particles caused no significant changes in the mitochondrial membrane permeability after 24 h treatment. Conclusion In this study, metallic nickel nanoparticles caused higher cytotoxicity and apoptotic induction than fine particles in JB6 cells. Apoptotic cell death
Appraisal on Textured Grain Growth and Photoconductivity of ZnO Thin Film SILAR
Directory of Open Access Journals (Sweden)
Deepu Thomas
2014-01-01
Full Text Available ZnO thin films were prepared by successive ionic layer adsorption reaction (SILAR method. The textured grain growth along c-axis in pure ZnO thin films and doped with Sn was studied. The structural analysis of the thin films was done by X-ray diffraction and surface morphology by scanning electron microscopy. Textured grain growth of the samples was measured by comparing the peak intensities. Textured grain growth and photo current in ZnO thin films were found to be enhanced by doping with Sn. ZnO thin film having good crystallinity with preferential (002 orientation is a semiconductor with photonic properties of potential benefit to biophotonics. From energy dispersive X-ray analysis, it is inferred that oxygen vacancy creation is responsible for the enhanced textured grain growth in ZnO thin films.
Nano-scale characterization of white layer in broached Inconel 718
Energy Technology Data Exchange (ETDEWEB)
Chen, Zhe, E-mail: zhe.chen@liu.se [Division of Engineering Materials, Linköping University, 58183 Linköping (Sweden); Colliander, Magnus Hörnqvist; Sundell, Gustav [Department of Physics, Chalmers University of Technology, 41296 Gothenburg (Sweden); Peng, Ru Lin [Division of Engineering Materials, Linköping University, 58183 Linköping (Sweden); Zhou, Jinming [Division of Production and Materials Engineering, Lund University, 22100 Lund (Sweden); Johansson, Sten; Moverare, Johan [Division of Engineering Materials, Linköping University, 58183 Linköping (Sweden)
2017-01-27
The formation mechanism of white layers during broaching and their mechanical properties are not well investigated and understood to date. In the present study, multiple advanced characterization techniques with nano-scale resolution, including transmission electron microscopy (TEM), transmission Kikuchi diffraction (TKD), atom probe tomography (APT) as well as nano-indentation, have been used to systematically examine the microstructural evolution and corresponding mechanical properties of a surface white layer formed when broaching the nickel-based superalloy Inconel 718. TEM observations showed that the broached white layer consists of nano-sized grains, mostly in the range of 20–50 nm. The crystallographic texture detected by TKD further revealed that the refined microstructure is primarily caused by strong shear deformation. Co-located Al-rich and Nb-rich fine clusters have been identified by APT, which are most likely to be γ′ and γ′′ clusters in a form of co-precipitates, where the clusters showed elongated and aligned appearance associated with the severe shearing history. The microstructural characteristics and crystallography of the broached white layer suggest that it was essentially formed by adiabatic shear localization in which the dominant metallurgical process is rotational dynamic recrystallization based on mechanically-driven subgrain rotations. The grain refinement within the white layer led to an increase of the surface nano-hardness by 14% and a reduction in elastic modulus by nearly 10% compared to that of the bulk material. This is primarily due to the greatly increased volume fraction of grain boundaries, when the grain size was reduced down to the nanoscale.
Grain-boundary effects on the magnetoresistance properties of perovskite manganite films
International Nuclear Information System (INIS)
Gupta, A.; Gong, G.Q.; Xiao, G.; Duncombe, P.R.; Lecoeur, P.; Trouilloud, P.; Wang, Y.Y.; Dravid, V.P.; Sun, J.Z.
1996-01-01
The role of grain boundaries in the magnetoresistance (MR) properties of the manganites has been investigated by comparing the properties of epitaxial and polycrystalline films of La 0.67 D 0.33 MnO 3-δ (D=Ca,Sr, or vacancies). While the MR in the epitaxial films is strongly peaked near the ferromagnetic transition temperature and is very small at low temperatures, the polycrystalline films show large MR over a wide temperature range down to 5 K. The results are explained in terms of switching of magnetic domains in the grains and disorder-induced canting of Mn spins in the grain-boundary region. copyright 1996 The American Physical Society
Structural and electrical properties of nickel substituted cadmium ferrite
Chethan, B.; Raj Prakash, H. G.; Vijayakumari, S. C.; Ravikiran, Y. T.
2018-05-01
Spinal nano-sized Cadmium ferrite (CD) and Nickel substituted cadmium ferrite (NSCF) were fabricated by sol-gel auto combustion method. The formation of spinal structure of ferrite materials was confirmed by X-ray diffraction (XRD) analysis. The crystallites size of CF and NSCF as determined by Scherrer's formula were found to be 24.73 nm and 17.70 nm respectively. comparative study of Fourier transform infrared spectroscopy (FTIR) of CF and NSCF revealed tetrahedral absorption bands shifted slightly towards higher frequency where as octahedral bands shifted towards lower frequency side confirming interfacial interaction between Ni and CF. The AC conductivity (σ), loss tangent (tan δ) and complex plane impedance plots for both CF and NSCF are determined at various frequencies ranging from 50 kHz to 5 MHz and comparatively analyzed. The increase in AC conductivity of the NSCF nano particles as compared to CF was explained in the light of hopping model. The impedance measurement of NSCF show presence of a semi-circle corresponding to the grain boundary resistance and hence shows that the conductivity takes place largely through grain boundaries.
Mechanical properties of ultra-thin HfO2 films studied by nano scratches tests
International Nuclear Information System (INIS)
Fu, Wei-En; Chang, Yong-Qing; Chang, Chia-Wei; Yao, Chih-Kai; Liao, Jiunn-Der
2013-01-01
10-nm-thick atomic layer deposited HfO 2 films were characterized in terms of wear resistance and indentation hardness to investigate the thermal annealing induced impacts on mechanical properties. The wear resistance of ultra-thin films at low loads was characterized using nano-scratch tests with an atomic force microscope. The depth of the nano-scratches decreases with increasing annealing temperature, indicating that the hardness of the annealed films increases with the annealing temperatures. Surface nanoindentation was also performed to confirm the nanoscratch test results. The hardness variation of the annealed films is due to the generation of HfSi x O y induced by the thermal annealing. X-ray photoelectron spectroscopy measurements proved that the hardness of formed HfSi x O y with increasing annealing temperatures. The existence of HfSi x O y broadens the interface, and causes the increase of the interfacial layer thickness. As a result, the surface hardness increases with the increasing HfSi x O y induced by the thermal annealing. - Highlights: ► Mechanical properties of HfO 2 films were assessed by nano-scratch and indentation. ► Scratch depth of HfO 2 films decreased with the increase of annealing temperatures. ► Nano-hardness of HfO 2 films increased with the increase of annealing temperatures
Effect of grain size on the melting point of confined thin aluminum films
Energy Technology Data Exchange (ETDEWEB)
Wejrzanowski, Tomasz; Lewandowska, Malgorzata; Sikorski, Krzysztof; Kurzydlowski, Krzysztof J. [Materials Design Division, Faculty of Materials Science and Engineering, Warsaw University of Technology, Woloska 141, 02-507 Warsaw (Poland)
2014-10-28
The melting of aluminum thin film was studied by a molecular dynamics (MD) simulation technique. The effect of the grain size and type of confinement was investigated for aluminum film with a constant thickness of 4 nm. The results show that coherent intercrystalline interface suppress the transition of solid aluminum into liquid, while free-surface gives melting point depression. The mechanism of melting of polycrystalline aluminum thin film was investigated. It was found that melting starts at grain boundaries and propagates to grain interiors. The melting point was calculated from the Lindemann index criterion, taking into account only atoms near to grain boundaries. This made it possible to extend melting point calculations to bigger grains, which require a long time (in the MD scale) to be fully molten. The results show that 4 nm thick film of aluminum melts at a temperature lower than the melting point of bulk aluminum (933 K) only when the grain size is reduced to 6 nm.
International Nuclear Information System (INIS)
Mohr, Markus; Daccache, Layal; Horvat, Sebastian; Brühne, Kai; Jacob, Timo; Fecht, Hans-Jörg
2017-01-01
Diamond combines several outstanding material properties such as the highest thermal conductivity and highest elastic moduli of all materials. This makes diamond an interesting candidate for a multitude of applications. Nonetheless, nanocrystalline diamond films, layers and coatings, usually show properties different to those of single crystalline diamond. This is usually attributed to the larger volume fraction of the grain boundaries with atomic structure different from the single crystal. In this work we measured Young's modulus and thermal conductivity of nanocrystalline diamond films with average grain sizes ranging from 6 to 15 nm. The measured thermal conductivities are modeled considering the thermal boundary conductance between grains as well as a grain size effect on the phonon mean free path. We make a comparison between elastic modulus and thermal boundary conductance of the grain boundaries G_k for different nanocrystalline diamond films. We conclude that the grain boundaries thermal boundary conductance G_k is a measure of the cohesive energy of the grain boundaries and therefore also of the elastic modulus of the nanocrystalline diamond films.
Effect of weak magnetic field on the grain size of electrodeposited nickel
International Nuclear Information System (INIS)
Ansari, M.S.; Gul, N.
2007-01-01
Effect of weak magnetic field on the electro-deposition of nickel onto copper electrode has been investigated. The working conditions were optimized through adjustment of cathodic current density (CCD), deposition time, bath temperature and pH of the medium. For electro-deposition in the absence of magnetic field, the optimum conditions comprised of pH = 4.0+- 0.5, average CCD = 22.5 +- 0.5 mA cm/sup -2/ and bath temperature in the range from 25 to 30 degree C. The same conditions were maintained for the electrodeposition while applying magnetic field of 0.75 kG. The morphological features of the Ni-deposits on copper cathode were compared for the two cases. The applied magnetic field not only enhanced the amount of nickel deposition but also improved the quality of the deposit. Surface morphology of the electro-deposited nickel has been monitored using scanning electron microscopy (SEM); the preliminary investigation has shown that the grain size decreased with the applied magnetic field case. One possible explanation to this behavior is the convection flow of cations close to the electrode surface induced by the Lorentz force which also influences the ion-migration. (author)
Highly conductive grain boundaries in copper oxide thin films
Energy Technology Data Exchange (ETDEWEB)
Deuermeier, Jonas, E-mail: j.deuermeier@campus.fct.unl.pt [Department of Materials Science, Faculty of Science and Technology, i3N/CENIMAT, Universidade NOVA de Lisboa and CEMOP/UNINOVA, Campus de Caparica, 2829-516 Caparica (Portugal); Department of Materials and Earth Sciences, Technische Universität Darmstadt, Jovanka-Bontschits-Straße 2, D-64287 Darmstadt (Germany); Wardenga, Hans F.; Morasch, Jan; Siol, Sebastian; Klein, Andreas, E-mail: aklein@surface.tu-darmstadt.de [Department of Materials and Earth Sciences, Technische Universität Darmstadt, Jovanka-Bontschits-Straße 2, D-64287 Darmstadt (Germany); Nandy, Suman; Calmeiro, Tomás; Martins, Rodrigo; Fortunato, Elvira [Department of Materials Science, Faculty of Science and Technology, i3N/CENIMAT, Universidade NOVA de Lisboa and CEMOP/UNINOVA, Campus de Caparica, 2829-516 Caparica (Portugal)
2016-06-21
High conductivity in the off-state and low field-effect mobility compared to bulk properties is widely observed in the p-type thin-film transistors of Cu{sub 2}O, especially when processed at moderate temperature. This work presents results from in situ conductance measurements at thicknesses from sub-nm to around 250 nm with parallel X-ray photoelectron spectroscopy. An enhanced conductivity at low thickness is explained by the occurrence of Cu(II), which is segregated in the grain boundary and locally causes a conductivity similar to CuO, although the surface of the thick film has Cu{sub 2}O stoichiometry. Since grains grow with an increasing film thickness, the effect of an apparent oxygen excess is most pronounced in vicinity to the substrate interface. Electrical properties of Cu{sub 2}O grains are at least partially short-circuited by this effect. The study focuses on properties inherent to copper oxide, although interface effects cannot be ruled out. This non-destructive, bottom-up analysis reveals phenomena which are commonly not observable after device fabrication, but clearly dominate electrical properties of polycrystalline thin films.
Effect of nano-silver hydrogel coating film on deep partial thickness scald model of rabbit.
Xi, Peng; Li, Yan; Ge, Xiaojin; Liu, Dandan; Miao, Mingsan
2018-05-01
Observing the effect of nano-silver hydrogel coating film on deep partial thickness scald model of rabbit. We prepared boiling water scalded rabbits with deep II degree scald models and applied high, medium and low doses of nano-silver hydrogel coating film for different time and area. Then we compared the difference of burned paper weight before administration and after administration model burns, burn local skin irritation points infection, skin crusting and scabs from the time, and the impact of local skin tissue morphology. Rabbits deep II degree burn model successful modeling; on day 12, 18, high, medium and low doses of nano-silver hydrogel coating film significantly reduced skin irritation of rabbits infected with the integral value ( P film group significantly decreased skin irritation, infection integral value ( P film significantly reduced film rabbits' scalded skin crusting time ( P film on the deep partial thickness burns has a significant therapeutic effect; external use has a significant role in wound healing.
Synthesis of graphene on nickel films by CVD method using methane
International Nuclear Information System (INIS)
Castro, Manuela O. de; Liebold-Ribeiro, Yvonne; Barros, Eduardo B.; Salomao, Francisco C.C.; Mendes Filho, Josue; Souza Filho, Antonio G.; Chesman, Carlos
2011-01-01
Full text: Nanomaterials have opened up many possibilities for groundbreaking innovations in various technologies of modern society. One key example is graphene, which is composed of one-atom-thick sheet of sp2-bonded carbon atoms, arranged in a hexagonal symmetry. However, real world applications of graphene require well-established and large synthesis techniques. The so-called Chemical Vapor Deposition (CVD) is one of the most promising method for synthesizing graphene. The general idea of this technique is to dissolve carbon atoms inside a transition metal melt at a certain temperature, then allowing the dissolved carbon to precipitate at lower temperatures as single layer graphene (SLG). In the present work, we used the CVD method and methane gas as carbon source for the synthesis of graphene on silicon (Si) substrates (300nm thermal oxide) covered with sputtered nickel (Ni) films as catalyst. In order to achieve large-area and defect-free graphene sheets the influence of the different growth parameters (growth temperature and time, gas flow of methane, film thickness and grain size of Ni) on quality and quantity of graphene growth were studied. The obtained graphene films were transferred to a silicon substrate by the polymer coating process, using polymethyl-methacrylate (PMMA) as coating. In order to characterize the transferred graphene we used Scanning Electron Microscopy (SEM), Raman Spectroscopy, Optical Microscopy and Atomic Force Microscopy (AFM). The results show the influence of CVD process parameters on the quality and quantity of graphene growth in our experimental conditions. Acknowledgments: The authors thank Brazilian agencies CNPq and FUNCAP for financial support and Alfonso Reina (MIT, USA) for helpful discussions. (author)
Energy Technology Data Exchange (ETDEWEB)
Maekawa, Y., E-mail: maekawa.yasunari@jaea.go.jp [Japan Atomic Energy Agency (JAEA), Quantum Beam Science Directorate, High Performance Polymer Group, 1233 Watanuki-Machi, Takasaki, Gunma-ken 370-1292 (Japan)
2010-07-01
Introduction of functional regions in nanometer scale in polymeric films using γ-rays, EB, and ion beams are proposed. Two approaches to build nano-scale functional domains in polymer substrates are proposed: 1) Radiation-induced grafting to transfer nano-scale polymer crystalline structures (morphology), acting as a nano-template, to nano-scale graft polymer regions. The obtained polymers with nano structures can be applied to high performance polymer membranes. 2) Fabrication of nanopores and functional domains in engineering plastic films using ion beams, which deposit the energy in very narrow region of polymer films. Hydrophilic grafting polymers are introduced into hydrophobic fluorinated polymers, cross-linked PTFE (cPTFE) and aromatic hydrocarbon polymer, poly(ether ether ketone (PEEK), which is known to have lamella and crystallite in the polymer films. Then, the hierarchical structures of graft domains are analyzed by a small angle neutron scattering (SANS) experiment. From these analyses, the different structures and the different formation of graft domains were observed in fluorinated and hydrocarbon polymer substrates. the grafted domains in the cPTFE film, working as an ion channel, grew as covering the crystallite and the size of domain seems to be similar to that of crystallite. On the other hand, the PEEK-based PEM has a smaller domain size and it seems to grow independently on the crystallites of PEEK substrate. For nano-fabrication of polymer films using heavy ion beams, the energy distribution in radial direction, which is perpendicular to ion trajectory, is mainly concerned. For penumbra, we re-estimated effective radius of penumbra, in which radiation induced grafting took place, for several different ion beams. We observed the different diameters of the ion channels consisting of graft polymers. The channel sizes were quite in good agreement with the effective penumbra which possess the absorption doses more than 1 kGy. (author)
International Nuclear Information System (INIS)
Maekawa, Y.
2010-01-01
Introduction of functional regions in nanometer scale in polymeric films using γ-rays, EB, and ion beams are proposed. Two approaches to build nano-scale functional domains in polymer substrates are proposed: 1) Radiation-induced grafting to transfer nano-scale polymer crystalline structures (morphology), acting as a nano-template, to nano-scale graft polymer regions. The obtained polymers with nano structures can be applied to high performance polymer membranes. 2) Fabrication of nanopores and functional domains in engineering plastic films using ion beams, which deposit the energy in very narrow region of polymer films. Hydrophilic grafting polymers are introduced into hydrophobic fluorinated polymers, cross-linked PTFE (cPTFE) and aromatic hydrocarbon polymer, poly(ether ether ketone (PEEK), which is known to have lamella and crystallite in the polymer films. Then, the hierarchical structures of graft domains are analyzed by a small angle neutron scattering (SANS) experiment. From these analyses, the different structures and the different formation of graft domains were observed in fluorinated and hydrocarbon polymer substrates. the grafted domains in the cPTFE film, working as an ion channel, grew as covering the crystallite and the size of domain seems to be similar to that of crystallite. On the other hand, the PEEK-based PEM has a smaller domain size and it seems to grow independently on the crystallites of PEEK substrate. For nano-fabrication of polymer films using heavy ion beams, the energy distribution in radial direction, which is perpendicular to ion trajectory, is mainly concerned. For penumbra, we re-estimated effective radius of penumbra, in which radiation induced grafting took place, for several different ion beams. We observed the different diameters of the ion channels consisting of graft polymers. The channel sizes were quite in good agreement with the effective penumbra which possess the absorption doses more than 1 kGy. (author)
Highly ordered FEPT and FePd magnetic nano-structures: Correlated structural and magnetic studies
International Nuclear Information System (INIS)
Lukaszew, Rosa Alejandra; Cebollada, Alfonso; Clavero, Cesar; Garcia-Martin, Jose Miguel
2006-01-01
The micro-structure of epitaxial FePt and FePd films grown on MgO (0 0 1) substrates is correlated to their magnetic behavior. The FePd films exhibit high chemical ordering and perpendicular magnetic anisotropy. On the other hand FePt films exhibit low chemical ordering, with nano-grains oriented in two orthogonal directions, forcing the magnetization to remain in the plane of the films
The Effect of Drawing Ratio on Mechanical Property of Nano-Hybrid Polyimide Composite Films
Directory of Open Access Journals (Sweden)
CHEN Hao
2017-06-01
Full Text Available In order to investigate the impact of drawing ratio of inorganic nano-hybrid polyamide three-layer composite films,the stretched composite films with different draw ratio were prepared by drawing partial imido polyamide film and then through the ring closing reaction in the high temperature,and the draw ratio was 0% ,2% , 4% ,6% ,8% ,10% ,12% ,14% etc. Under the same conditions,we made different draw ratio of three-layer composite film tensile test with the electronic universal material testing machine. The results show: doped inorganic nanometer oxide made PI film elastic modulus increase slightly,the tensile strength and elongation at break decrease obviously,but the nano hybrid three-layer composite PI films still had good mechanical properties; The yield of polyimide film should be caused by forced high-elastic deformation of polyimide molecular chain,and it had nothing to do with whether doped inorganic nano-oxide or whether through stretched processing; With the increase of draw ratio,the elastic modulus of the nano hybrid three-layer composite PI films existed the trend of first increased and then slow down gradually,and the tensile strength and elongation at break first decreased and then increased.
Deformation and fracture in micro-tensile tests of freestanding electrodeposited nickel thin films
International Nuclear Information System (INIS)
Yang, Y.; Yao, N.; Soboyejo, W.O.; Tarquinio, C.
2008-01-01
In situ scanning electron microscopy micro-tensile tests were conducted on freestanding LIGA nickel thin films of two thicknesses (70 and 270 μm). The deformation and fracture mechanisms were elucidated by in situ scanning electron microscopy imaging and ex situ fractographic analysis. Due to the film microstructural gradient, an apparent thickness effect on the film yield strengths was observed, which was then rationalized with a continuum micromechanics model
Kibbey, T. C. G.; Adegbule, A.; Yan, S.
2017-12-01
The movement of nonvolatile solutes in unsaturated porous media at low water contents depends on transport in surface-associated water films. The focus of the work described here was on studying solute movement in water films advancing by capillary forces over initially-dry grain surfaces, to understand how microscopic surface roughness features influence the initial velocity of water film advance. For this work, water containing a non-adsorbing conservative tracer was used to track the movement of advancing water films. A stainless steel capillary tube connected to an external reservoir a fixed distance below the grain surface was used to transmit solution to the grain surface under negative pressure (positive capillary pressure), consistent with conditions that might be expected in the unsaturated zone. The small internal diameter of the capillary prevents solution from draining out of the capillary back into the reservoir. When the capillary is contacted with a grain surface, capillary forces that result from contact between the fluid and the rough grain surface cause water films to wick across the grain surface. Multiple experiments were conducted on the same grain, rotating the grain and varying the capillary contact point around the circumference of the grain. Imaging was conducted at fixed intervals using an automated Extended Depth of Field (EDF) imaging system, and images were analyzed to determine initial velocity. Grain surfaces were then characterized through scanning electron microscope (SEM) imaging, using a hybrid stereoscopic reconstruction method designed to extract maximum detail in creating elevation maps of geologic surfaces from tilted pairs of SEM images. The resulting elevation maps were used to relate surface roughness profiles around the grain with initial velocities. Results suggest that velocity varies significant with contact point around an individual grain, and correlates quantitatively with the local grain surface structure
Nano mechanical properties of carbon films modified by ion radiation
International Nuclear Information System (INIS)
Foerster, C.E.; Serbena, F.C.; Lepienski, C.M.; Odo, G.Y.; Zawislak, F.C.; Lopes, J.M.J.; Baptista, D.L.; Garcia, I.T.S.
2000-01-01
In present work it is measured hardness, Young modulus and friction coefficient values for different types of carbon films. These films were submitted to different ion bombardment conditions (energy and fluencies). The mechanical behavior was obtained by nano indentation technique and analyzed by the Oliver/Pharr method. For friction coefficient determination the nano scratch procedure is used. Pristine C 60 films (fullerenes) has a hardness of 0.33 GPa. After irradiation with different ions (He, N and Bi), the hardness raise to about 14 GPa and the Young modulus change from 20 to about 200 GPa. For photoresist film AZ-1350J irradiation with Ar and He change the hardness from 0.4 to about 14 GPa and the Young modulus raise from 4 to 80 GPa. In a-C-H the hardness change from 3.5 to 11 GPa when submitted to N irradiation. In PPA films the hardness value raise from 0.5 to 11 GPa after irradiation with Ar. These mechanical and tribological results were analyzed in terms of deposited energy by the ion irradiation and compared with those presented in the literature. (author)
Energy Technology Data Exchange (ETDEWEB)
Akhtar, Muhammad Saeed [School of Materials, The University of Manchester, Oxford Road, Manchester M13 9PL (United Kingdom); Centre of Excellence in Solid State Physics, University of the Punjab, Lahore 54590 (Pakistan); Malik, Mohammad Azad, E-mail: Azad.malik@manchester.ac.uk [School of Materials, The University of Manchester, Oxford Road, Manchester M13 9PL (United Kingdom); Riaz, Saira; Naseem, Shahzad [Centre of Excellence in Solid State Physics, University of the Punjab, Lahore 54590 (Pakistan)
2015-06-15
The nickel doped nanocrystalline ZnS thin films were deposited onto glass substrates by chemical bath deposition (CBD). Also ZnS:Ni nanoparticles were synthesized by CBD/co-precipitation method. Powder X-ray diffraction (p-XRD) studies demonstrate that both thin films and nanoparticles correspond to sphalerite (cubic) phase of ZnS with slight shift towards higher 2θ values due to incorporation of nickel in the ZnS lattice. The crystallite sizes estimated by Scherrer equation were 4 and 2.6 nm for ZnNiS thin films and nanoparticles, respectively. Scanning Electron Microscopy (SEM) images reveal that the morphology of thin films is based on quasi-spherical particles with nano scale dimensions. Energy Dispersive X-ray (EDX) spectroscopy confirms that the as-deposited thin films have a stoichiometry consistent with the nickel doped ZnS. Full-potential linearized augmented plane wave (FP-L/APW) method based on spin-polarized density functional theory (DFT) was employed to investigate the electronic and magnetic properties of ZnNiS for the doping concentration. Exchange-correlation functional was studied using generalized gradient approximation (GGA + U) method. Electronic band structures and density of states (DOS) demonstrate 100% spin polarization (half metallicity) with ferromagnetic exchange interactions. Superconducting quantum interference device (SQUID) analysis confirms the theoretical observation of ferromagnetism in nickel doped ZnS. These ZnS based half metallic ferromagnets seem to have virtuous applications in future spintronic devices. - Highlights: • ZnS.Ni thin films and nanoparticles were deposited onto glass substrates by CBD. • p-XRD correspond to sphalerite (cubic) phase of ZnS with slight shift in peaks. • DFT was employed to investigate the properties of ZnS.Ni. • DOS demonstrate 100% spin polarization with ferromagnetic exchange interactions. • SQUID analysis confirms the theoretical observations of nickel doped ZnS.
Plasticity analysis of nano-grain-sized NiAl alloy in an atomic scale
International Nuclear Information System (INIS)
Wang Jingyang; Wang Xiaowei; Rifkin, J.; Li Douxing
2001-12-01
The molecular dynamics method is used to simulate a uniaxial tensile deformation of 3.8nm nano-NiAl alloy with curved amorphous-like interfaces at 0K. Plastic deformation behaviour is studied by examining the strain-stress relationship and the microstructural evolution characteristic. Atomic level analysis showed that the micro-strain is essentially heterogeneous in simulated nano-phase samples. The plastic deformation is not only attributed to the plasticity of interfaces, but also accompanied with the plastic shear strain mechanism inside lattice distortion regions and grains. (author)
Yan, Yuping; Lv, Jiajiang; Liu, Sheng
2018-04-01
We investigate chirality and grain boundary (GB) effects on indentation mechanical properties of graphene coated on nickel foil using molecular dynamics simulations. The models of graphene with different chirality angles, different numbers of layers and tilt GBs were established. It was found that the chirality angle of few-layer graphene had a significant effect on the load bearing capacity of graphene/nickel systems, and this turns out to be more significant when the number of layers is greater than one. The enhancement to the contact stiffness, elastic capacity and the load bearing capacity of graphene with tilt GBs was lower than that of pristine graphene.
Noorbakhsh-Soltani, S M; Zerafat, M M; Sabbaghi, S
2018-06-01
Environmental concerns have led to extensive research for replacing polymer-based food packaging with bio-nano-composites. In this study, incorporation of nano-cellulose into gelatin and starch matrices is investigated for this purpose. Chitosan is used to improve mechanical, anti-fungal and waterproof properties. Experiments are designed and analyzed using response surface methodology. Nano-Cellulose is synthesized via acid hydrolysis and incorporated in base matrices through wet processing. Also, tensile strength test, food preservation, transparency in visible and UV and water contact angle are performed on the nano-composite films. DSC/TGA and air permeability tests are also performed on the optimal films. The results show that increasing nano-cellulose composition to 10% leads to increase the tensile strength at break to 8121 MN/m 2 and decrease the elongation at break. Also, increasing chitosan composition from 5% to 30% can enhance food preservation up to 15 days. Copyright © 2018 Elsevier Ltd. All rights reserved.
Energy Technology Data Exchange (ETDEWEB)
Magnfält, D., E-mail: danma@ifm.liu.se; Sarakinos, K. [Nanoscale Engineering Division, Department of Physics, Chemistry and Biology (IFM), Linköping University, SE-581 83 Linköping (Sweden); Fillon, A.; Abadias, G. [Institut P' , Département Physique et Mécanique des Matériaux, Université de Poitiers-CNRS-ENSMA, SP2MI, Téléport 2, Bd M. et P. Curie, F-86962 Chasseneuil-Futuroscope (France); Boyd, R. D.; Helmersson, U. [Plasma and Coatings Physics Division, Department of Physics, Chemistry and Biology (IFM), Linköping University, SE-581 83 Linköping (Sweden)
2016-02-07
Intrinsic stresses in vapor deposited thin films have been a topic of considerable scientific and technological interest owing to their importance for functionality and performance of thin film devices. The origin of compressive stresses typically observed during deposition of polycrystalline metal films at conditions that result in high atomic mobility has been under debate in the literature in the course of the past decades. In this study, we contribute towards resolving this debate by investigating the grain size dependence of compressive stress magnitude in dense polycrystalline Mo films grown by magnetron sputtering. Although Mo is a refractory metal and hence exhibits an intrinsically low mobility, low energy ion bombardment is used during growth to enhance atomic mobility and densify the grain boundaries. Concurrently, the lateral grain size is controlled by using appropriate seed layers on which Mo films are grown epitaxially. The combination of in situ stress monitoring with ex situ microstructural characterization reveals a strong, seemingly linear, increase of the compressive stress magnitude on the inverse grain size and thus provides evidence that compressive stress is generated in the grain boundaries of the film. These results are consistent with models suggesting that compressive stresses in metallic films deposited at high homologous temperatures are generated by atom incorporation into and densification of grain boundaries. However, the underlying mechanisms for grain boundary densification might be different from those in the present study where atomic mobility is intrinsically low.
Influence of nano-inclusions' grain boundaries on crack propagation modes in materials
International Nuclear Information System (INIS)
Karakasidis, T.E.; Charitidis, C.A.
2011-01-01
The effect of nano-inclusions on materials' strength and toughness has attracted great interest in recent years. It has been shown that tuning the morphological and microstructural features of materials can tailor their fracture modes. The existence of a characteristic size of inclusions that favours the fracture mode (i.e. transgranular or intergranular) has been experimentally observed but also predicted by a 2D model based on energetic arguments which relates the crack propagation mode to the ratio of the interface area between the crystalline inclusion and the matrix with the area of the crystallite inclusion in a previous work. In the present work, a 3D model is proposed in order to extend the 2D model and take into account the influence of the size of grain boundary zone on the toughening/hardening behavior of the material as it was observed experimentally in the literature. The model relates crack propagation mode to the ratio of the volume of the grain boundary zone between the crystalline inclusion and the matrix with the volume of the nano-inclusion. For a ratio below a critical value, transgranular propagation is favoured while for larger values, intergranular propagation is favoured. We also demonstrate that the extent of the grain boundary region also can significantly affect this critical value. The results of the model are in agreement with the literature experimental observations related to the toughening/hardening behavior as a function of the size of crystalline inclusions as well as the width of the grain boundary regions.
Techniques for Achieving Zero Stress in Thin Films of Iridium, Chromium, and Nickel
Broadway, David M.; O'Dell, Stephen L.; Ramsey, Brian D.; Weimer, Jeffrey
2015-01-01
We examine techniques for achieving zero intrinsic stress in thin films of iridium, chromium, and nickel deposited by magnetron sputter deposition. The intrinsic stress is further correlated to the microstructural features and physical properties such as surface roughness and optical density at a scale appropriate to soft X-ray wavelengths. The examination of the stress in these materials is motivated by efforts to advance the optical performance of light-weight X-ray space telescopes into the regime of sub-arcsecond resolution through various deposition techniques that rely on control of the film stress to values within 10-100 MPa. A characteristic feature of the intrinsic stress behavior in chromium and nickel is their sensitivity to the magnitude and sign of the intrinsic stress with argon gas pressure and deposition rate, including the existence of a critical argon process pressure that results in zero film stress which scales linearly with the atomic mass of the sputtered species. While the effect of stress reversal with argon pressure has been previously reported by Hoffman and others for nickel and chromium, we report this effect for iridium. In addition to stress reversal, we identify zero stress in the optical functioning iridium layer shortly after island coalescence for low process pressures at a film thickness of approximately 35nm. The measurement of the low values of stress during deposition was achieved with the aid of a sensitive in-situ instrument capable of a minimum detectable level of stress, assuming a 35nm thick film, in the range of 0.40-6.0 MPa for oriented crystalline silicon substrate thicknesses of 70-280 microns, respectively.
Mechanical properties of ultra-thin HfO{sub 2} films studied by nano scratches tests
Energy Technology Data Exchange (ETDEWEB)
Fu, Wei-En; Chang, Yong-Qing [Center for Measurement Standards, Industrial Technology Research Institute, Room 216, Building 8, 321, Kuang Fu Road Sec. 2, Hsinchu, Taiwan (China); Chang, Chia-Wei; Yao, Chih-Kai [Department of Materials Science and Engineering, National Cheng Kung University, 1 University Road, Tainan 70101, Taiwan (China); Liao, Jiunn-Der, E-mail: jdliao@mail.ncku.edu.tw [Department of Materials Science and Engineering, National Cheng Kung University, 1 University Road, Tainan 70101, Taiwan (China); Center for Micro/Nano Science and Technology, National Cheng Kung University, 1 University Road, Tainan 70101, Taiwan (China)
2013-02-01
10-nm-thick atomic layer deposited HfO{sub 2} films were characterized in terms of wear resistance and indentation hardness to investigate the thermal annealing induced impacts on mechanical properties. The wear resistance of ultra-thin films at low loads was characterized using nano-scratch tests with an atomic force microscope. The depth of the nano-scratches decreases with increasing annealing temperature, indicating that the hardness of the annealed films increases with the annealing temperatures. Surface nanoindentation was also performed to confirm the nanoscratch test results. The hardness variation of the annealed films is due to the generation of HfSi{sub x}O{sub y} induced by the thermal annealing. X-ray photoelectron spectroscopy measurements proved that the hardness of formed HfSi{sub x}O{sub y} with increasing annealing temperatures. The existence of HfSi{sub x}O{sub y} broadens the interface, and causes the increase of the interfacial layer thickness. As a result, the surface hardness increases with the increasing HfSi{sub x}O{sub y} induced by the thermal annealing. - Highlights: ► Mechanical properties of HfO{sub 2} films were assessed by nano-scratch and indentation. ► Scratch depth of HfO{sub 2} films decreased with the increase of annealing temperatures. ► Nano-hardness of HfO{sub 2} films increased with the increase of annealing temperatures.
International Nuclear Information System (INIS)
Zhao Xiaofeng; Wen Dianzhong; Zhuang Cuicui; Cao Jingya; Wang Zhiqiang
2013-01-01
A magnetic field sensor based on nano-polysilicon thin films transistors (TFTs) with Hall probes is proposed. The magnetic field sensors are fabricated on 〈100〉 orientation high resistivity (ρ > 500 Ω·cm) silicon substrates by using CMOS technology, which adopt nano-polysilicon thin films with thicknesses of 90 nm and heterojunction interfaces between the nano-polysilicon thin films and the high resistivity silicon substrates as the sensing layers. The experimental results show that when V DS = 5.0 V, the magnetic sensitivities of magnetic field sensors based on nano-polysilicon TFTs with length—width ratios of 160 μm/80 μm, 320 μm/80 μm and 480 μm/80 μm are 78 mV/T, 55 mV/T and 34 mV/T, respectively. Under the same conditions, the magnetic sensitivity of the obtained magnetic field sensor is significantly improved in comparison with a Hall magnetic field sensor adopting silicon as the sensing layers. (semiconductor technology)
Spontaneous nano-gap formation in Ag film using NaCl sacrificial layer for Raman enhancement
Min, Kyungchan; Jeon, Wook Jin; Kim, Youngho; Choi, Jae-Young; Yu, Hak Ki
2018-03-01
We report the method of fabrication of nano-gaps (known as hot spots) in Ag thin film using a sodium chloride (NaCl) sacrificial layer for Raman enhancement. The Ag thin film (20-50 nm) on the NaCl sacrificial layer undergoes an interfacial reaction due to the AgCl formed at the interface during water molecule intercalation. The intercalated water molecules can dissolve the NaCl molecules at interfaces and form the ionic state of Na+ and Cl-, promoting the AgCl formation. The Ag atoms can migrate by the driving force of this interfacial reaction, resulting in the formation of nano-size gaps in the film. The surface-enhanced Raman scattering activity of Ag films with nano-size gaps has been investigated using Raman reporter molecules, Rhodamine 6G (R6G).
Energy Technology Data Exchange (ETDEWEB)
Li, Bao-jia, E-mail: li_bjia@126.com [School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013 (China); Jiangsu Provincial Key Laboratory of Center for Photon Manufacturing Science and Technology, Jiangsu University, Zhenjiang 212013 (China); Huang, Li-jing [School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013 (China); Jiangsu Provincial Key Laboratory of Center for Photon Manufacturing Science and Technology, Jiangsu University, Zhenjiang 212013 (China); Ren, Nai-fei [Jiangsu Provincial Key Laboratory of Center for Photon Manufacturing Science and Technology, Jiangsu University, Zhenjiang 212013 (China); School of Mechanical Engineering, Jiangsu University, Zhenjiang 212013 (China); Kong, Xia; Cai, Yun-long; Zhang, Jie-lu [Jiangsu Tailong Reduction Box Co. Ltd., Taixing 225400 (China)
2015-10-01
Highlights: • Ni/FTO films were prepared by sputtering Ni layers on commercial FTO glass. • The as-prepared Ni/FTO films underwent magnetic-field-assisted laser annealing. • Magnetic field and laser fluence were crucial for improving quality of the films. • All Ni/FTO films displayed enhanced compactness after magnetic laser annealing. • Magnetic laser annealing using a fluence of 0.9 J/cm{sup 2} led to the best film quality. - Abstract: Nickel-coated fluorine-doped tin oxide (Ni/FTO) thin films were prepared by sputtering Ni layers on commercial FTO glass. The as-prepared Ni/FTO films underwent nanosecond pulsed laser annealing in an external magnetic field (0.4 T). The effects of the presence of magnetic field and laser fluence on surface morphology, crystal structure and photoelectric properties of the films were investigated. All the films displayed enhanced compactness after magnetic-field-assisted laser annealing. It was notable that both crystallinity and grain size of the films gradually increased with increasing laser fluence from 0.6 to 0.9 J/cm{sup 2}, and then decreased slightly with an increase in laser fluence to 1.1 J/cm{sup 2}. As a result, the film obtained by magnetic-field-assisted laser annealing using a fluence of 0.9 J/cm{sup 2} had the best overall photoelectric property with an average transmittance of 81.2%, a sheet resistance of 5.5 Ω/sq and a figure of merit of 2.27 × 10{sup −2} Ω{sup −1}, outperforming that of the film obtained by pure laser annealing using the same fluence.
Ding, Junsheng; Wu, Xiaomeng; Qi, Xiaona; Guo, Heng; Liu, Anjun; Wang, Wenhang
2018-05-01
In this paper, two kinds of commonly used vegetable carbon black (VCB, 3000 mesh; nano) at 50 g kg -1 concentration (based on dried gelatin) were added to 48 g kg -1 of fish gelatin (GEL) solutions and their effects on mechanical, barrier and anti-photooxidation properties of GEL films were investigated. From the SEM images, it was shown that compared with 3000 mesh VCB (1-2 μm), nano VCB (100-200 nm) made the microstructure of GEL film more compact and more gelatin chains were cross-linked by nano VCB. The addition of nano VCB significantly increased gelatin film strength with the greatest tensile strength of 52.589 MPa and stiffness with the highest Young's modulus of 968.874 MPa, but led to the reduction of film elongation. Also, the VCB presence significantly improved water vapour and oxygen barrier properties of GEL film. Importantly, nano VCB increased GEL film with better UV barrier property due to its stronger UV absorption nature when compared with micron VCB. This property could help in the preservation of oil samples in the photooxidation accelerated test. With improved properties, the nano VCB-reinforced GEL film may have great potential for application in the edible packaging field, especially for the anti-photooxidation property. © 2017 Society of Chemical Industry. © 2017 Society of Chemical Industry.
Nano-enabled tribological thin film coatings: global patent scenario.
Sivudu, Kurva S; Mahajan, Yashwant R; Joshi, Shrikant V
2014-01-01
The aim of this paper is to present current status and future prospects of nano-enabled tribological thin film coatings based on worldwide patent landscape analysis. The study also presents an overview of technological trends by carrying out state-of-the-art literature analysis, including survey of corporate websites. Nanostructured tribological coatings encompass a wide spectrum of nanoscale microstructures, including nanocrystalline, nanolayered, nano-multilayered, nanocomposite, nanogradient structures or their unique combinations, which are composed of single or multi-component phases. The distinct microstructural features of the coatings impart outstanding tribological properties combined with multifunctional attributes to the coated components. Their unique combination of remarkable properties make them ideal candidates for a wide range of applications in diverse fields such as cutting and metalworking tools, biomedical devices, automotive engine components, wear parts, hard disc drives etc. The patent landscape analysis has revealed that nano-enabled tribological thin film coatings have significant potential for commercial applications in view of the lion's share of corporate industry in patenting activity. The largest patent portfolio is held by Japan followed by USA, Germany, Sweden and China. The prominent players involved in this field are Mitsubishi Materials Corp., Sandvik Aktiebolag, Hitachi Ltd., Sumitomo Electric Industries Ltd., OC Oerlikon Corp., and so on. The outstanding potential of nanostructured thin film tribological coatings is yet to be fully unravelled and, therefore, immense opportunities are available in future for microstructurally engineered novel coatings to enhance their performance and functionality by many folds.
Crystallographic contribution to the formation of the columnar grain structure in cobalt films
International Nuclear Information System (INIS)
Hara, K.; Itoh, K.; Okamoto, K.; Hashimoto, T.
1996-01-01
In order to clarify the crystallographic contribution to the formation of the columnar grain structure, the geometric and crystallographic alignments of columnar grains in cobalt films were investigated on the basis of magnetic and optical measurements. The films were deposited by sputtering at an incidence angle of 45 on glass substrates heated at 332 K. The film thickness ranged from 20 to 850 nm. Above 50 nm the columnar grains align in the direction parallel to the incidence plane and form a two-degree crystallographic orientation. The packing density of columnar grains decreases with increasing thickness when the thickness exceeds 50 nm. From these results we conclude that the crystal habit appearing on column tops induces the two-degree orientation through geometric selection and aligns the selected columnar grains in the parallel direction. (orig.)
In situ AFM analysis investigating disassembly of DNA nanoparticles and nano-films.
Zou, Yi; Wan, Lei; Blacklock, Jenifer; Oupicky, David; Mao, Guangzhao
2013-01-01
Synthetic vector-based gene delivery systems continue to gain strength as viable alternatives to viral vectors due to safety and other concerns. DNA release dynamics is key to the understanding and control of gene delivery from nano-systems. Here we describe atomic force microscope application to the understanding of DNA release dynamics from bioreducible polycation-based nano-systems. The two nano-systems are polyplex nanoparticles and layer-by-layer films.
A microfabricated nickel-hydrogen battery using thick film printing techniques
Tam, Waiping G.; Wainright, Jesse S.
To utilize the distinctive cycle life and safety characteristics of the nickel-hydrogen chemistry while eliminating the high pressure limitations of conventional nickel-hydrogen cells, a microfabricated nickel-hydrogen battery using a low-pressure metal hydride for hydrogen storage is being developed for powering micro-electromechanical systems (MEMS) devices and for biomedical applications where the battery would be implanted within the body. Thick film printing techniques which are simple and low cost were used to fabricate this battery. Inks were developed for each of the different battery components, including the electrodes, current collectors and separator. SEM images on these printed components showed the desired characteristics for each. Positive electrode cycling tests were performed on the printed positive electrodes while cyclic voltammetry was used to characterize the printed negative electrodes. Consistent charge and discharge performance was observed during positive electrode cycling. Full cells with printed positive and negative assemblies were assembled and tested.
A microfabricated nickel-hydrogen battery using thick film printing techniques
Energy Technology Data Exchange (ETDEWEB)
Tam, Waiping G.; Wainright, Jesse S. [Department of Chemical Engineering, Case Western Reserve University, Cleveland, OH 44106 (United States)
2007-02-25
To utilize the distinctive cycle life and safety characteristics of the nickel-hydrogen chemistry while eliminating the high pressure limitations of conventional nickel-hydrogen cells, a microfabricated nickel-hydrogen battery using a low-pressure metal hydride for hydrogen storage is being developed for powering micro-electromechanical systems (MEMS) devices and for biomedical applications where the battery would be implanted within the body. Thick film printing techniques which are simple and low cost were used to fabricate this battery. Inks were developed for each of the different battery components, including the electrodes, current collectors and separator. SEM images on these printed components showed the desired characteristics for each. Positive electrode cycling tests were performed on the printed positive electrodes while cyclic voltammetry was used to characterize the printed negative electrodes. Consistent charge and discharge performance was observed during positive electrode cycling. Full cells with printed positive and negative assemblies were assembled and tested. (author)
Strain-delocalizing effect of a metal substrate on nanocrystalline Ni film
Energy Technology Data Exchange (ETDEWEB)
Qi, Dexing [Department of Mechanical Engineering, Nanjing Tech University, Nanjing, Jiangsu Province 210009 (China); Zhou, Jianqiu, E-mail: zhouj@njut.edu.cn [Department of Mechanical Engineering, Nanjing Tech University, Nanjing, Jiangsu Province 210009 (China); Department of Mechanical Engineering, Wuhan Institute of Technology, Wuhan, Hubei Province 430070 (China); Liu, Hongxi; Dong, Shuhong [Department of Mechanical Engineering, Nanjing Tech University, Nanjing, Jiangsu Province 210009 (China); Wang, Ying [Department of Mechanical and Electronic Engineering, Suzhou Institute of Industrial Technology, Suzhou, Jiangsu 215104 (China)
2015-07-29
Uniaxial tensile test and scanning electron microscopy (SEM) are introduced to study the tensile properties of electrodeposited nanocrystalline nickel/coarse-grained copper (N/C) composite in this paper. Compared to the stress strain response of pure nanocrystalline (NC) nickel (Ni), the tensile ductility of N/C composite is enhanced significantly. Based on the experimental results, a multi-phase composite model is proposed to investigate the micromechanical behaviors of the NC Ni film and N/C composite plate. The constitutive models are implemented into ABAQUS/Explicit in the form of VUMAT subroutine. A series of numerical simulations are carried out and the predications were in good agreement with experimental results. It can be concluded that the coarse-grained (CG) substrate work well in suppressing the strain localization in the NC Ni film.
Optical Detection and Sizing of Single Nano-Particles Using Continuous Wetting Films
Hennequin, Yves; McLeod, Euan; Mudanyali, Onur; Migliozzi, Daniel; Ozcan, Aydogan; Dinten, Jean-Marc
2013-01-01
The physical interaction between nano-scale objects and liquid interfaces can create unique optical properties, enhancing the signatures of the objects with sub-wavelength features. Here we show that the evaporation on a wetting substrate of a polymer solution containing sub-micrometer or nano-scale particles creates liquid micro-lenses that arise from the local deformations of the continuous wetting film. These micro-lenses have properties similar to axicon lenses that are known to create beams with a long depth of focus. This enhanced depth of focus allows detection of single nanoparticles using a low magnification microscope objective lens, achieving a relatively wide field-of-view, while also lifting the constraints on precise focusing onto the object plane. Hence, by creating these liquid axicon lenses through spatial deformations of a continuous thin wetting film, we transfer the challenge of imaging individual nano-particles to detecting the light focused by these lenses. As a proof of concept, we demonstrate the detection and sizing of single nano-particles (100 and 200 nm), CpGV granuloviruses as well as Staphylococcus epidermidis bacteria over a wide field of view of e.g., 5.10×3.75 mm2 using a ×5 objective lens with a numerical aperture of 0.15. In addition to conventional lens-based microscopy, this continuous wetting film based approach is also applicable to lensfree computational on-chip imaging, which can be used to detect single nano-particles over a large field-of-view of e.g., >20-30 mm2. These results could be especially useful for high-throughput field-analysis of nano-scale objects using compact and cost-effective microscope designs. PMID:23889001
Electrical properties of thermally evaporated nickel-dimethylglyoxime thin films
Dakhel, A. A.; Ali-Mohamed Ahmed, Y.
2005-06-01
Thin Bis-(dimethylglyoximato)nickel(II) [Ni(DMG)2] films of amorphous and crystalline structures were prepared by vacuum deposition on Si (P) substrates. The films were characterised by X-ray fluorescence and X-ray diffraction. The constructed Al/Ni(DMG)2/Si(P) metal-insulator-semiconductor devices were characterised by the measurement of the gate-voltage dependence of their capacitance and ac conductance, from which the surface states density Dit of insulator/semiconductor interface and the density of the fixed charges in the oxide were determined. The ac electrical conduction and dielectric properties of the Ni(DMG)2-Silicon structure were studied at room temperature. The data of the ac measurements of the annealed films follow the correlated barrier-hopping CBH mode, from which the fundamental absorption bandgap, the minimum hopping distance, and other parameters of the model were determined.
Pandey, B.; Das, D.; Kar, A. K.
2015-05-01
Nanocomposite diamond-like carbon (DLC) thin films have been synthesized by incorporating nickel (Ni) nanoparticles in DLC matrix with varying concentration of nickel. DLC and Ni-DLC thin films have been deposited on ITO coated glass substrates employing low voltage electrodeposition method. Electrical properties of the samples were studied by measuring current-voltage characteristics and dielectric properties. The current approaches toward an ohmic behavior with metal addition. This tendency of increasing ohmicity is enhanced with increase in dilution of the electrolyte. The conductivity increases with Ni addition and interestingly it continues to increase with dilution of Ni concentration in the electrolyte in the range of our study. Magnetic properties for DLC and Ni-DLC thin film samples were examined by electron paramagnetic resonance (EPR) measurements and Super Conducting Quantum Interference Device (SQUID) measurements. g-Value for DLC is 2.074, whereas it decreases to 2.055 with Ni addition in the electrolyte. This decrement arises from the increased sp2 content in DLC matrix. The magnetic moment vs. magnetic field (m-H) curves of Ni-DLC indicate superparamagnetic behavior which may be due to ferromagnetic contribution from the incorporated nickel nanoparticles in the DLC matrix. The ZFC curve of Ni-DLC after the blocking temperature shows a combined contribution of ferromagnetic, superparamagnetic and paramagnetic nature of the materials persisting up to 300 K.
Energy Technology Data Exchange (ETDEWEB)
Joshi, Anupama [Department of Applied Physics, Defence Institute of Advanced Technology (DU), Girinagar, Pune 411025 (India); Nori, Rajashree [Centre of Excellence in Nanoelectronics, Department of Electrical Engineering, Indian Institute of Technology (IIT Bombay), Mumbai 400076 (India); Dhobale, Sandip [Department of Applied Physics, Defence Institute of Advanced Technology (DU), Girinagar, Pune 411025 (India); Ramgopal Rao, V. [Centre of Excellence in Nanoelectronics, Department of Electrical Engineering, Indian Institute of Technology (IIT Bombay), Mumbai 400076 (India); Kale, S.N., E-mail: sangeetakale2004@gmail.com [Department of Applied Physics, Defence Institute of Advanced Technology (DU), Girinagar, Pune 411025 (India); Datar, Suwarna, E-mail: suwarna.datar@gmail.com [Department of Applied Physics, Defence Institute of Advanced Technology (DU), Girinagar, Pune 411025 (India)
2014-09-01
We employed a Scanning Tunnelling Microscope (STM) to study the surface topography and spatially resolved local electronic properties like local density of states (LDOS) of nanostructured films of La{sub 0.7} Sr{sub 0.3} MnO{sub 3} (LSMO). The nanostructured thin films of LSMO on silicon substrate were prepared using Pulsed Laser Deposition (PLD) technique. The deposition conditions were tuned to yield two different morphologies; one with uniform columnar closely packed islands and other with larger grain distribution in random fashion. The Scanning Tunnelling Spectroscopy (STS) revealed the extent of variation of density of states (DOS) near the Fermi level. From the spectroscopic features obtained we found the occurrence of phase separation between conducting and semiconducting domains and its possible correlation with the properties of the system. Semiconducting nature was observed at the grain boundaries, which could be extremely promising in futuristic nano-devices.
International Nuclear Information System (INIS)
Shakir, Imran
2014-01-01
Highlights: • Two-step fabrication method for nano-architectured spinel nickel cobaltite (NiCo 2 O 4 ) anchored MWCNTs composite. • High performance flexible energy-storage devices. • The NiCo 2 O 4 anchored MWCNTs Exhibits 2032 Fg −1 capacitance which is 1.62 times greater than pristine NiCo 2 O 4 at 1 Ag −1 . - Abstract: We demonstrate a facile two-step fabrication method for nano-architectured spinel nickel cobaltite (NiCo 2 O 4 ) anchored multiwall carbon nanotubes (MWCNTs) based electrodes for high performance flexible energy-storage devices. As electrode materials for flexible supercapacitors, the NiCo 2 O 4 anchored MWCNTs exhibits a high specific capacitance of 2032 Fg −1 , which is nearly 1.62 times greater than pristine NiCo 2 O 4 nanoflakes at 1 Ag −1 . The synthesized NiCo 2 O 4 anchored MWCNTs composite shows excellent rate performance (83.96% capacity retention at 30 Ag −1 ) and stability with coulombic efficiency over 96% after 5,000 cycles when being fully charged/discharged at 1 Ag −1 . Furthermore, NiCo 2 O 4 anchored MWCNTs achieve a maximum energy density of 48.32 Whkg −1 at a power density of 480 Wkg −1 which is 60% higher than pristine NiCo 2 O 4 electrode and significantly outperformed electrode materials based on NiCo 2 O 4 which are currently used in the state-of-the-art supercapacitors throughout the literature. This superior rate performance and high-capacity value offered by NiCo 2 O 4 anchored MWCNTs is mainly due to enhanced electronic and ionic conductivity, which provides a short diffusion path for ions and an easy access of electrolyte flow to nickel cobaltite redox centers besides the high conductivity of MWCNTs
Electron scattering at surfaces and grain boundaries in thin Au films
International Nuclear Information System (INIS)
Henriquez, Ricardo; Flores, Marcos; Moraga, Luis; Kremer, German; González-Fuentes, Claudio; Munoz, Raul C.
2013-01-01
The electron scattering at surfaces and grain boundaries is investigated using polycrystalline Au films deposited onto mica substrates. We vary the three length scales associated with: (i) electron scattering in the bulk, that at temperature T is characterized by the electronic mean free path in the bulk ℓ 0 (T); (ii) electron-surface scattering, that is characterized by the film thickness t; (iii) electron-grain boundary scattering, that is characterized by the mean grain diameter D. We varied independently the film thickness from approximately 50 nm to about 100 nm, and the typical grain size making up the samples from 12 nm to 160 nm. We also varied the scale of length associated with electron scattering in the bulk by measuring the resistivity of each specimen at temperatures T, 4 K 0 (T) by approximately 2 orders of magnitude. Detailed measurements of the grain size distribution as well as surface roughness of each sample were performed with a Scanning Tunnelling Microscope (STM). We compare, for the first time, theoretical predictions with resistivity data employing the two theories available that incorporate the effect of both electron-surface as well as electron-grain boundary scattering acting simultaneously: the theory of A.F. Mayadas and M. Shatzkes, Phys. Rev. 1 1382 (1970) (MS), and that of G. Palasantzas, Phys. Rev. B 58 9685 (1998). We eliminate adjustable parameters from the resistivity data analysis, by using as input the grain size distribution as well as the surface roughness measured with the STM on each sample. The outcome is that both theories provide a fair representation of both the temperature as well as the thickness dependence of the resistivity data, but yet there are marked differences between the resistivity predicted by these theories. In the case of the MS theory, when the average grain diameter D is significantly smaller than ℓ 0 (300) = 37 nm, the electron mean free path in the bulk at 300 K, the effect of electron-grain
International Nuclear Information System (INIS)
Yang Changjun; Gong Chuqing; Peng Tianyou; Deng Kejian; Zan Ling
2010-01-01
A novel photodegradable polyvinyl chloride (PVC)-vitamin C (VC)-TiO 2 nano-composite film was prepared by embedding VC modified nano-TiO 2 photocatalyst into the commercial PVC plastic. The solid-phase photocatalytic degradation behavior of PVC-VC-TiO 2 nano-composite film under UV light irradiation was investigated and compared with those of the PVC-TiO 2 film and the pure PVC film, with the aid of UV-Vis spectroscopy, scanning electron microscopy (SEM), weight loss monitoring, and X-ray diffraction spectra (XRD). The results show that PVC-VC-TiO 2 nano-composite film has a high photocatalytic activity; the photocatalytic degradation rate of it is two times higher than that of PVC-TiO 2 film and fifteen times higher than that of pure PVC film. The optimal mass ratio of VC to TiO 2 is found to be 0.5. The mechanism of enhancing photocatalytic activity is attributed to the formation of a Ti IV -VC charge-transfer complex with five-member chelate ring structure and a rapid photogenerated charge separation is thus achieved.
Nano-volcanic Eruption of Silver
Lin, Shih-Kang; Nagao, Shijo; Yokoi, Emi; Oh, Chulmin; Zhang, Hao; Liu, Yu-Chen; Lin, Shih-Guei; Suganuma, Katsuaki
2016-10-01
Silver (Ag) is one of the seven metals of antiquity and an important engineering material in the electronic, medical, and chemical industries because of its unique noble and catalytic properties. Ag thin films are extensively used in modern electronics primarily because of their oxidation-resistance. Here we report a novel phenomenon of Ag nano-volcanic eruption that is caused by interactions between Ag and oxygen (O). It involves grain boundary liquation, the ejection of transient Ag-O fluids through grain boundaries, and the decomposition of Ag-O fluids into O2 gas and suspended Ag and Ag2O clusters. Subsequent coating with re-deposited Ag-O and the de-alloying of O yield a conformal amorphous Ag coating. Patterned Ag hillock arrays and direct Ag-to-Ag bonding can be formed by the homogenous crystallization of amorphous coatings. The Ag “nano-volcanic eruption” mechanism is elaborated, shedding light on a new mechanism of hillock formation and new applications of amorphous Ag coatings.
International Nuclear Information System (INIS)
Baran, L.V.
2015-01-01
By methods of atomic force microscopy, X-ray diffraction and nano indentation the research of change of structure phase composition and nano hardness of the chrome - fullerite - chrome films, subjected to implantation by B + ions (E = 80 keV, F = 5*10 17 ions/cm 2 ) are submitted. It is established, that as a result of Boron ion implantation of the chrome - fullerite - chrome films, chrome and fullerite inter fusion on sues, that is the solid-phase interaction and as a result of which forms the heterophase with increased nano hardness. (authors)
Oxidation mechanism of nickel particles studied in an environmental transmission electron microscope
DEFF Research Database (Denmark)
Jeangros, Q.; Hansen, Thomas Willum; Wagner, Jakob Birkedal
2014-01-01
The oxidation of nickel particles was studied in situ in an environmental transmission electron microscope in 3.2 mbar of O2 between ambient temperature and 600°C. Several different transmission electron microscopy imaging techniques, electron diffraction and electron energy-loss spectroscopy were...... diffusion of Ni2+ along NiO grain boundaries, self-diffusion of Ni2+ ions and vacancies, growth of NiO grains and nucleation of voids at Ni/NiO interfaces. We also observed the formation of transverse cracks in a growing NiO film in situ in the electron microscope....
International Nuclear Information System (INIS)
Calleja, C.; Torres, A.; Rosales-Quintero, P.; Moreno, M.
2016-01-01
We have optimized the deposition conditions of amorphous silicon-germanium films with embedded nano crystals in a plasma enhanced chemical vapor deposition (PECVD) reactor, working at a standard frequency of 13.56 MHz. The objective was to produce films with very large Temperature Coefficient of Resistance (TCR), which is a signature of the sensitivity in thermal detectors (micro bolometers). Morphological, electrical, and optical characterization were performed in the films, and we found optimal conditions for obtaining films with very high values of thermal coefficient of resistance (TCR = 7.9%K -1 ). Our results show that amorphous silicon-germanium films with embedded nano crystals can be used as thermo sensitive films in high performance infrared focal plane arrays (IRFPAs) used in commercial thermal cameras.
Investigation of bioactivity and cell effects of nano-porous sol–gel derived bioactive glass film
Energy Technology Data Exchange (ETDEWEB)
Ma, Zhijun, E-mail: mokuu@zju.edu.cn [State Key Laboratory of Luminescent Materials and Devices, South China University of Technology, Guangzhou, 510640 (China); Ji, Huijiao [College of Life Science, Zhejiang University, Hangzhou, 310028 (China); Hu, Xiaomeng [School of Materials Science and Engineering, South China University of Technology, Guangzhou, 510640 (China); Teng, Yu [State Key Laboratory of Luminescent Materials and Devices, South China University of Technology, Guangzhou, 510640 (China); Zhao, Guiyun; Mo, Lijuan; Zhao, Xiaoli [College of Life Science, Zhejiang University, Hangzhou, 310028 (China); Chen, Weibo [School of Materials Science and Engineering, South China University of Technology, Guangzhou, 510640 (China); Qiu, Jianrong, E-mail: qjr@scut.edu.cn [State Key Laboratory of Luminescent Materials and Devices, South China University of Technology, Guangzhou, 510640 (China); Zhang, Ming, E-mail: zhangming201201@126.com [College of Life Science, Zhejiang University, Hangzhou, 310028 (China)
2013-11-01
In orthopedic surgery, bioactive glass film coating is extensively studied to improve the synthetic performance of orthopedic implants. A lot of investigations have confirmed that nano-porous structure in bioactive glasses can remarkably improve their bioactivity. Nevertheless, researches on preparation of nano-porous bioactive glasses in the form of film coating and their cell response activities are scarce. Herein, we report the preparation of nano-porous bioactive glass film on commercial glass slide based on a sol–gel technique, together with the evaluation of its in vitro bioactivity through immersion in simulated body fluid and monitoring the precipitation of apatite-like layer. Cell responses of the samples, including attachment, proliferation and osteogenic differentiation, were also investigated using BMSCS (bone marrow derived mesenchymal stem cells) as a model. The results presented here provide some basic information on structural influence of bioactive glass film on the improvement of bioactivity and cellular effects.
Investigation of bioactivity and cell effects of nano-porous sol-gel derived bioactive glass film
Ma, Zhijun; Ji, Huijiao; Hu, Xiaomeng; Teng, Yu; Zhao, Guiyun; Mo, Lijuan; Zhao, Xiaoli; Chen, Weibo; Qiu, Jianrong; Zhang, Ming
2013-11-01
In orthopedic surgery, bioactive glass film coating is extensively studied to improve the synthetic performance of orthopedic implants. A lot of investigations have confirmed that nano-porous structure in bioactive glasses can remarkably improve their bioactivity. Nevertheless, researches on preparation of nano-porous bioactive glasses in the form of film coating and their cell response activities are scarce. Herein, we report the preparation of nano-porous bioactive glass film on commercial glass slide based on a sol-gel technique, together with the evaluation of its in vitro bioactivity through immersion in simulated body fluid and monitoring the precipitation of apatite-like layer. Cell responses of the samples, including attachment, proliferation and osteogenic differentiation, were also investigated using BMSCS (bone marrow derived mesenchymal stem cells) as a model. The results presented here provide some basic information on structural influence of bioactive glass film on the improvement of bioactivity and cellular effects.
Metal-assisted chemical etching of CIGS thin films for grain size analysis
Energy Technology Data Exchange (ETDEWEB)
Xue, Chaowei [Research and Development Centre, Hanergy Thin Film Power Group Limited, Chengdu (China); Loi, Huu-Ha; Duong, Anh; Parker, Magdalena [Failure Analysis Department, MiaSole Hi-Tech Corp., Santa Clara, CA (United States)
2016-09-15
Grain size of the CIGS absorber is an important monitoring factor in the CIGS solar cell manufacturing. Electron backscatter diffraction (EBSD) analysis is commonly used to perform CIGS grain size analysis in the scanning electron microscope (SEM). Although direct quantification on SEM image using the average grain intercept (AGI) method is faster and simpler than EBSD, it is hardly applicable on CIGS thin films. The challenge is that, not like polycrystalline silicon, to define grain boundaries by selective chemical etching is not easily realizable for the multi-component CIGS alloy. In this Letter, we present direct quantification of CIGS thin film grain size using the AGI method by developing metal-assisted wet chemical etching process to define CIGS grain boundaries. The calculated value is similar to EBSD result. (copyright 2016 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)
Film Grain-Size Related Long-Term Stability of Inverted Perovskite Solar Cells.
Chiang, Chien-Hung; Wu, Chun-Guey
2016-09-22
The power conversion efficiency (PCE) of the perovskite solar cell is high enough to be commercially viable. The next important issue is the stability of the device. This article discusses the effect of the perovskite grain-size on the long-term stability of inverted perovskite solar cells. Perovskite films composed of various sizes of grains were prepared by controlling the solvent annealing time. The grain-size related stability of the inverted cells was investigated both in ambient atmosphere at relative humidity of approximately 30-40 % and in a nitrogen filled glove box (H 2 Operovskite film having the grain size larger than 1 μm (D-10) decreases less than 10 % with storage in a glove box and less than 15 % when it was stored under an ambient atmosphere for 30 days. However, the cell using the perovskite film composed of small (∼100 nm) perovskite grains (D-0) exhibits complete loss of PCE after storage under the ambient atmosphere for only 15 days and a PCE loss of up to 70 % with storage in the glove box for 30 days. These results suggest that, even under H 2 O-free conditions, the chemical- and thermal-induced production of pin holes at the grain boundaries of the perovskite film could be the reason for long-term instability of inverted perovskite solar cells. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.
Eco-nano composite films containing copper as potential antimicrobial active packaging
Energy Technology Data Exchange (ETDEWEB)
Bruna, Julio E.; Gonzalez, Valeska; Rodriguez, Francisco; Guarda, Abel; Galotto, Maria Jose, E-mail: julio.bruna@usach.cl [Center for the Development of Nanoscience and Nanotechnology, Packaging Laboratory, University of Santiago de Chile. Santiago (Chile)
2011-07-01
The antimicrobial efficiency of Cellulose Acetate/MMTCu and Chitosan/MMTCu nano composites against Escherichia Coli 0157:H7 n/t has been studied in the present work. The MMT modified with copper were obtained using cation interchange in solution and the nano composites films were prepared using casting solution technique, being the biodegradable polymer (Cellulose Acetate or Chitosan) the main component and the montmorillonite modified with copper, the minority component. Characterization of MMTCu and the nano composites (CA/MMTCu and Ch/MMTCu), were carried out using XRD, AA, TGA, DSC and microbiological analysis. The nano composites showed to be more stable at higher temperature, resulting from the incorporation of MMTCu into the polymer. On the other hand, the results indicated that the antibacterial effect of nano composite increased with the proportion of MMTCu added. (author)
Eco-nano composite films containing copper as potential antimicrobial active packaging
International Nuclear Information System (INIS)
Bruna, Julio E.; Gonzalez, Valeska; Rodriguez, Francisco; Guarda, Abel; Galotto, Maria Jose
2011-01-01
The antimicrobial efficiency of Cellulose Acetate/MMTCu and Chitosan/MMTCu nano composites against Escherichia Coli 0157:H7 n/t has been studied in the present work. The MMT modified with copper were obtained using cation interchange in solution and the nano composites films were prepared using casting solution technique, being the biodegradable polymer (Cellulose Acetate or Chitosan) the main component and the montmorillonite modified with copper, the minority component. Characterization of MMTCu and the nano composites (CA/MMTCu and Ch/MMTCu), were carried out using XRD, AA, TGA, DSC and microbiological analysis. The nano composites showed to be more stable at higher temperature, resulting from the incorporation of MMTCu into the polymer. On the other hand, the results indicated that the antibacterial effect of nano composite increased with the proportion of MMTCu added. (author)
Challenges of sample preparation for cross sectional EBSD analysis of electrodeposited nickel films
DEFF Research Database (Denmark)
Alimadadi, Hossein; Pantleon, Karen
2009-01-01
Thorough microstructure and crystallographic orientation analysis of thin films by means of electron backscatter diffraction requires cross section preparation of the film-substrate compound. During careful preparation, changes of the rather non-stable as-deposited microstructure must be avoided....... Different procedures for sample preparation including mechanical grinding and polishing, electropolishing and focused ion beam milling have been applied to a nickel film electrodeposited on top of an amorphous Ni-P layer on a Cu-substrate. Reliable EBSD analysis of the whole cross section can be obtained...
Nano-engineered pinning centres in YBCO superconducting films
Energy Technology Data Exchange (ETDEWEB)
Crisan, A., E-mail: adrian.crisan@infim.ro [National Institute for Materials Physics Bucharest, 105 bis Atomistilor Str., 077125 Magurele (Romania); School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Dang, V.S. [School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Nano and Energy Center, VNU Hanoi University of Science, 334 Nguyen Trai, Thanh Xuan, Hanoi (Viet Nam); Mikheenko, P. [School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Department of Physics, University of Oslo, P.O. Box 1048 Blindern, N-0316 Oslo (Norway)
2017-02-15
Highlights: • Power applications of YBCO films/coated conductors in technological relevant magnetic fields requires nano-engineered pinning centre. • Three approaches have been proposed: substrate decoration, quasi-multilayers, and targets with secondary phase nano-inclusions. • Combination of all three approaches greatly increased critical current in YBCO films. • Bulk pinning force, pinning potential, and critical current density are estimated and discussed in relation with the type and strength of pinning centres related to the defects evidenced by Transmission Electron Microscopy. - Abstract: For practical applications of superconducting materials in applied magnetic fields, artificial pinning centres in addition to natural ones are required to oppose the Lorentz force. These pinning centres are actually various types of defects in the superconductor matrix. The pinning centres can be categorised on their dimension (volume, surface or point) and on their character (normal cores or Δκ cores). Different samples have been produced by Pulsed Laser Deposition, with various thicknesses, temperatures and nanostructured additions to the superconducting matrix. They have been characterized by SQUID Magnetic Properties Measurement System and Physical Properties Measurement System, as well as by Transmission Electron Microscopy (TEM). Correlations between pinning architecture, TEM images, and critical currents at various fields and field orientations will be shown for a large number of YBa{sub 2}Cu{sub 3}O{sub x} films with various types and architectures of artificial pinning centres.
Electron scattering at surfaces and grain boundaries in thin Au films
Energy Technology Data Exchange (ETDEWEB)
Henriquez, Ricardo [Departamento de Física, Universidad Técnica Federico Santa María, Av. España 1680, Casilla 110-V, Valparaíso (Chile); Flores, Marcos; Moraga, Luis [Departamento de Física, Facultad de Ciencias Físicas y Matemáticas, Universidad de Chile, Blanco Encalada 2008, Casilla 487-3, Santiago 8370449 (Chile); Kremer, German [Bachillerato, Universidad de Chile, Las Palmeras 3425, Santiago 7800024 (Chile); González-Fuentes, Claudio [Departamento de Física, Universidad Técnica Federico Santa María, Av. España 1680, Casilla 110-V, Valparaíso (Chile); Munoz, Raul C., E-mail: ramunoz@ing.uchile.cl [Departamento de Física, Facultad de Ciencias Físicas y Matemáticas, Universidad de Chile, Blanco Encalada 2008, Casilla 487-3, Santiago 8370449 (Chile)
2013-05-15
The electron scattering at surfaces and grain boundaries is investigated using polycrystalline Au films deposited onto mica substrates. We vary the three length scales associated with: (i) electron scattering in the bulk, that at temperature T is characterized by the electronic mean free path in the bulk ℓ{sub 0}(T); (ii) electron-surface scattering, that is characterized by the film thickness t; (iii) electron-grain boundary scattering, that is characterized by the mean grain diameter D. We varied independently the film thickness from approximately 50 nm to about 100 nm, and the typical grain size making up the samples from 12 nm to 160 nm. We also varied the scale of length associated with electron scattering in the bulk by measuring the resistivity of each specimen at temperatures T, 4 K < T < 300 K. Cooling the samples to 4 K increases ℓ{sub 0}(T) by approximately 2 orders of magnitude. Detailed measurements of the grain size distribution as well as surface roughness of each sample were performed with a Scanning Tunnelling Microscope (STM). We compare, for the first time, theoretical predictions with resistivity data employing the two theories available that incorporate the effect of both electron-surface as well as electron-grain boundary scattering acting simultaneously: the theory of A.F. Mayadas and M. Shatzkes, Phys. Rev. 1 1382 (1970) (MS), and that of G. Palasantzas, Phys. Rev. B 58 9685 (1998). We eliminate adjustable parameters from the resistivity data analysis, by using as input the grain size distribution as well as the surface roughness measured with the STM on each sample. The outcome is that both theories provide a fair representation of both the temperature as well as the thickness dependence of the resistivity data, but yet there are marked differences between the resistivity predicted by these theories. In the case of the MS theory, when the average grain diameter D is significantly smaller than ℓ{sub 0}(300) = 37 nm, the electron mean
Motion of Adsorbed Nano-Particles on Azobenzene Containing Polymer Films
Directory of Open Access Journals (Sweden)
Sarah Loebner
2016-12-01
Full Text Available We demonstrate in situ recorded motion of nano-objects adsorbed on a photosensitive polymer film. The motion is induced by a mass transport of the underlying photoresponsive polymer material occurring during irradiation with interference pattern. The polymer film contains azobenzene molecules that undergo reversible photoisomerization reaction from trans- to cis-conformation. Through a multi-scale chain of physico-chemical processes, this finally results in the macro-deformations of the film due to the changing elastic properties of polymer. The topographical deformation of the polymer surface is sensitive to a local distribution of the electrical field vector that allows for the generation of dynamic changes in the surface topography during irradiation with different light interference patterns. Polymer film deformation together with the motion of the adsorbed nano-particles are recorded using a homemade set-up combining an optical part for the generation of interference patterns and an atomic force microscope for acquiring the surface deformation. The particles undergo either translational or rotational motion. The direction of particle motion is towards the topography minima and opposite to the mass transport within the polymer film. The ability to relocate particles by photo-induced dynamic topography fluctuation offers a way for a non-contact simultaneous manipulation of a large number of adsorbed particles just in air at ambient conditions.
Influence of iron doping on tetravalent nickel content in catalytic oxygen evolving films
Energy Technology Data Exchange (ETDEWEB)
Li, Nancy; Bediako, D. Kwabena; Hadt, Ryan G.; Hayes, Dugan; Kempa, Thomas J.; von Cube, Felix; Bell, David C.; Chen, Lin X.; Nocera, Daniel G.
2017-01-30
Iron doping of nickel oxide films results in enhanced activity for promoting the oxygen evolution reaction (OER). Whereas this enhanced activity has been ascribed to a unique iron site within the nickel oxide matrix, we show here that Fe doping influences the Ni valency. The percent of Fe3+ doping promotes the formation of formal Ni4+, which in turn directly correlates with an enhanced activity of the catalyst in promoting OER. The role of Fe3+ is consistent with its behavior as a superior Lewis acid.
Non-linear optics of nano-scale pentacene thin film
Yahia, I. S.; Alfaify, S.; Jilani, Asim; Abdel-wahab, M. Sh.; Al-Ghamdi, Attieh A.; Abutalib, M. M.; Al-Bassam, A.; El-Naggar, A. M.
2016-07-01
We have found the new ways to investigate the linear/non-linear optical properties of nanostructure pentacene thin film deposited by thermal evaporation technique. Pentacene is the key material in organic semiconductor technology. The existence of nano-structured thin film was confirmed by atomic force microscopy and X-ray diffraction. The wavelength-dependent transmittance and reflectance were calculated to observe the optical behavior of the pentacene thin film. It has been observed the anomalous dispersion at wavelength λ 800. The non-linear refractive index of the deposited films was investigated. The linear optical susceptibility of pentacene thin film was calculated, and we observed the non-linear optical susceptibility of pentacene thin film at about 6 × 10-13 esu. The advantage of this work is to use of spectroscopic method to calculate the liner and non-liner optical response of pentacene thin films rather than expensive Z-scan. The calculated optical behavior of the pentacene thin films could be used in the organic thin films base advanced optoelectronic devices such as telecommunications devices.
Directory of Open Access Journals (Sweden)
Rafia Barir
2017-01-01
Full Text Available Undoped nickel oxide (NiO thin films were deposited on 500°C heated glass substrates using spray pyrolysis method at (0.015–0.1 M range of precursor. The latter was obtained by decomposition of nickel nitrate hexahydrate in double distilled water. Effect of precursor concentration on structural, optical, and electrical properties of NiO thin films was investigated. X-ray diffraction (XRD shows the formation of NiO under cubic structure with single diffraction peak along (111 plane at 2θ=37.24°. When precursor concentration reaches 0.1 M, an increment in NiO crystallite size over 37.04 nm was obtained indicating the product nano structure. SEM images reveal that beyond 0.04 M as precursor concentration the substrate becomes completely covered with NiO and thin films exhibit formation of nano agglomerations at the top of the sample surface. Ni-O bonds vibrations modes in the product of films were confirmed by FT-IR analysis. Transparency of the films ranged from 57 to 88% and band gap energy of the films decreases from 3.68 to 3.60 eV with increasing precursor concentration. Electrical properties of the elaborated NiO thin films were correlated to the precursor concentration.
Vergara, José; Favieres, Cristina; Magén, César; de Teresa, José María; Ibarra, Manuel Ricardo; Madurga, Vicente
2017-12-05
We show how nanocrystalline Co films formed by separated oblique nano-sheets display anisotropy in their resistivity, magnetization process, surface nano-morphology and optical transmission. After performing a heat treatment at 270 °C, these anisotropies decrease. This loss has been monitored measuring the resistivity as a function of temperature. The resistivity measured parallel to the direction of the nano-sheets has been constant up to 270 °C, but it decreases when measured perpendicular to the nano-sheets. This suggests the existence of a structural relaxation, which produces the change of the Co nano-sheets during annealing. The changes in the nano-morphology and the local chemical composition of the films at the nanoscale after heating above 270 °C have been analysed by scanning transmission electron microscopy (STEM). Thus, an approach and coalescence of the nano-sheets have been directly visualized. The spectrum of activation energies of this structural relaxation has indicated that the coalescence of the nano-sheets has taken place between 1.2 and 1.7 eV. In addition, an increase in the size of the nano-crystals has occurred in the samples annealed at 400 °C. This study may be relevant for the application in devices working, for example, in the GHz range and to achieve the retention of the anisotropy of these films at higher temperatures.
Directory of Open Access Journals (Sweden)
José Vergara
2017-12-01
Full Text Available We show how nanocrystalline Co films formed by separated oblique nano-sheets display anisotropy in their resistivity, magnetization process, surface nano-morphology and optical transmission. After performing a heat treatment at 270 °C, these anisotropies decrease. This loss has been monitored measuring the resistivity as a function of temperature. The resistivity measured parallel to the direction of the nano-sheets has been constant up to 270 °C, but it decreases when measured perpendicular to the nano-sheets. This suggests the existence of a structural relaxation, which produces the change of the Co nano-sheets during annealing. The changes in the nano-morphology and the local chemical composition of the films at the nanoscale after heating above 270 °C have been analysed by scanning transmission electron microscopy (STEM. Thus, an approach and coalescence of the nano-sheets have been directly visualized. The spectrum of activation energies of this structural relaxation has indicated that the coalescence of the nano-sheets has taken place between 1.2 and 1.7 eV. In addition, an increase in the size of the nano-crystals has occurred in the samples annealed at 400 °C. This study may be relevant for the application in devices working, for example, in the GHz range and to achieve the retention of the anisotropy of these films at higher temperatures.
Synthesis and characterization of cobalt doped nickel oxide thin films by spray pyrolysis method
Sathisha, D.; Naik, K. Gopalakrishna
2018-05-01
Cobalt (Co) doped nickel oxide (NiO) thin films were deposited on glass substrates at a temperature of about 400 °C by spray pyrolysis method. The effect of Co doping concentration on structural, optical and compositional properties of NiO thin films was investigated. X-ray diffraction result shows that the deposited thin films are polycrystalline in nature. Surface morphologies of the deposited thin films were observed by FESEM and AFM. EDS spectra showed the incorporation of Co dopants in NiO thin films. Optical properties of the grown thin films were characterized by UV-visible spectroscopy. It was found that the optical band gap energy and transmittance of the films decrease with increasing Co doping concentration.
Energy Technology Data Exchange (ETDEWEB)
Lu, Liping, E-mail: lipinglu@bjut.edu.cn; Xu, Laihui; Kang, Tianfang; Cheng, Shuiyuan
2013-11-01
DNA damage induced from perfluorooctane sulfonate (PFOS) was further developed on a nano-porous bionic interface. The interface was formed by assembling DNA on nano-gold particles which were embedded in a nano-porous overoxidized polypyrrole film (OPPy). Atomic force microscopy, scanning electron microscope and electrochemical investigations indicate that OPPy can be treated to form nano-pore structures. DNA damage due to PFOS was proved using electrochemistry and X-ray photoelectron spectroscopy (XPS) and was investigated by detecting differential pulse voltammetry (DPV) response of methylene blue (MB) which was used as electro-active indicator in the system. The current of MB attenuates obviously after incubation of DNA in PFOS. Moreover, electrochemical impedance spectroscopy (EIS) demonstrates that PFOS weakens DNA charge transport. The tentative binding ratio of PFOS: DNA base pair was obtained by analyzing XPS data of this system.
Energy Technology Data Exchange (ETDEWEB)
Li, C., E-mail: canli1983@gmail.com; Zhao, Y. F.; Fu, C. X.; Gong, Y. Y. [Center for Coordination Bond Engineering, School of Materials Science and Engineering, China Jiliang University (China); Chi, B. Q. [College of Modem Science and Technology, Jiliang University, Hangzhou, 310018 (China); Sun, C. Q. [Center for Coordination Bond Engineering, School of Materials Science and Engineering, China Jiliang University (China); School of Electrical and Electronic Engineering, Nanyang Technological University, 639798 (Singapore)
2014-10-15
The effects of vertical compressive stress on Sb{sub 2}Te{sub 3} nano-films have been investigated by the first principles calculation, including stability, electronic structure, crystal structure, and bond order. It is found that the band gap of nano-film is sensitive to the stress in Sb{sub 2}Te{sub 3} nano-film and the critical thickness increases under compressive stress. The band gap and band order of Sb{sub 2}Te{sub 3} film has been affected collectively by the surface and internal crystal structures, the contraction ratio between surface bond length of nano-film and the corresponding bond length of bulk decides the band order of Sb{sub 2}Te{sub 3} film.
Energy Technology Data Exchange (ETDEWEB)
Savaloni, Hadi, E-mail: savaloni@khayam.ut.ac.ir [Department of Physics, University of Tehran, North-Kargar Street, Tehran (Iran, Islamic Republic of); Fakharpour, Mahsa [Department of Physics, Islamic Azad University, Science and Research Branch, Tehran (Iran, Islamic Republic of); Siabi-Garjan, Araz [Department of Advanced Technologies, University of Mohaghegh Ardabili, Namin, Ardabil (Iran, Islamic Republic of); Department of Materials Engineering and Nanotechnology, Sabalan University of Advanced Technologies (SUAT), Namin (Iran, Islamic Republic of); Placido, Frank [SUPA and Institute of Thin Films, Sensors and Imaging, University of The West of Scotland, High Street, Paisley (United Kingdom); Babaei, Ferydon [Department of Physics, University of Qom, Qom (Iran, Islamic Republic of)
2017-01-30
Highlights: • Graded helical square tower-like terraced sculptured Mn thin films are produced with different number of arms. • XRD, AFM, FESEM and optical analyses as well as theoretical calculations are carried out. • Intensity of Plasmon peaks depend on the polarization, the incident angle, and the distance from the shadowing block. • The presence of defects in these sculptured structures can be predicted by theoretical investigation. • Experimental and theoretical investigations show consistent results. - Abstract: Graded helical square tower-like terraced sculptured Mn thin films (GHSTTS) are produced in three stages with different number of arms using oblique angle deposition together with rotation of substrate holder about its surface normal, plus a shadowing block fixed at the centre of the substrate holder. The structural characterization of the produced samples was obtained using field emission scanning electron microscope (FESEM) and atomic force microscope (AFM). Results showed a structural gradient with distance from the edge of the shadowing block, which in turn is responsible for the decrease in the volume of void fraction and increase of grain size. Plasmon absorption peaks observed in the optical analysis of these nano-structures showed that their wavelength region and intensity depend on the polarization and the incident angle of light, as well as the distance from the edge of the shadowing block. According to our model and discrete dipole approximation (DDA) calculations, when the number of parallel nano-rods of different lengths and radii are increased the peak in the spectrum shifts to shorter wavelengths (blue shift). Also when the diameters of the nano-rods increases (a situation that occurs with increasing film thickness) the results is again a blue shift in the spectrum. The presence of defects in these sculptured structures caused by the shadowing effect is predicted by the theoretical DDA investigation of their optical spectra
Transparent and conductive electrodes by large-scale nano-structuring of noble metal thin-films
DEFF Research Database (Denmark)
Linnet, Jes; Runge Walther, Anders; Wolff, Christian
2018-01-01
grid, and nano-wire thin-films. The indium and carbon films do not match the chemical stability nor the electrical performance of the noble metals, and many metal films are not uniform in material distribution leading to significant surface roughness and randomized transmission haze. We demonstrate...
Transparent electrode designs based on optimal nano-patterning of metallic films
Catrysse, Peter B.
2010-09-10
Transparent conductive electrodes are critical to the operation of optoelectronic devices, such as photovoltaic cells and light emitting diodes. Effective electrodes need to combine excellent electrical and optical properties. Metal oxides, such as indium tin oxide, are commonly used. There is substantial interest in replacing them, however, motivated by practical problems and recent discoveries regarding the optics of nano-patterned metals. When designing nano-patterned metallic films for use as electrodes, one needs to account for both optical and electrical properties. In general, it is insufficient to optimize nano-structured films based upon optical properties alone, since structural variations will also affect the electrical properties. In this work, we investigate the need for simultaneous optical and electrical performance by analyzing the optical properties of a class of nano-patterned metallic electrodes that is obtained by a constant-sheet-resistance transformation. Within such a class the electrical and optical properties can be separated, i.e., the sheet resistance can be kept constant and the transmittance can be optimized independently. For simple one-dimensional periodic patterns with constant sheet-resistance, we find a transmission maximum (polarization-averaged) when the metal sections are narrow (< 40 nm, ~ 10% metal fill-factor) and tall (> 100 nm). Our design carries over to more complex two-dimensional (2D) patterns. This is significant as there are no previous reports regarding numerical studies on the optical and electrical properties of 2D nano-patterns in the context of electrode design.
Self-cleaning poly(dimethylsiloxane) film with functional micro/nano hierarchical structures.
Zhang, Xiao-Sheng; Zhu, Fu-Yun; Han, Meng-Di; Sun, Xu-Ming; Peng, Xu-Hua; Zhang, Hai-Xia
2013-08-27
This paper reports a novel single-step wafer-level fabrication of superhydrophobic micro/nano dual-scale (MNDS) poly(dimethylsiloxane) (PDMS) films. The MNDS PDMS films were replicated directly from an ultralow-surface-energy silicon substrate at high temperature without any surfactant coating, achieving high precision. An improved deep reactive ion etching (DRIE) process with enhanced passivation steps was proposed to easily realize the ultralow-surface-energy MNDS silicon substrate and also utilized as a post-treatment process to strengthen the hydrophobicity of the MNDS PDMS film. The chemical modification of this enhanced passivation step to the surface energy has been studied by density functional theory, which is also the first investigation of C4F8 plasma treatment at molecular level by using first-principle calculations. From the results of a systematic study on the effect of key process parameters (i.e., baking temperature and time) on PDMS replication, insight into the interaction of hierarchical multiscale structures of polymeric materials during the micro/nano integrated fabrication process is experimentally obtained for the first time. Finite element simulation has been employed to illustrate this new phenomenon. Additionally, hierarchical PDMS pyramid arrays and V-shaped grooves have been developed and are intended for applications as functional structures for a light-absorption coating layer and directional transport of liquid droplets, respectively. This stable, self-cleaning PDMS film with functional micro/nano hierarchical structures, which is fabricated through a wafer-level single-step fabrication process using a reusable silicon mold, shows attractive potential for future applications in micro/nanodevices, especially in micro/nanofluidics.
Transformation from amorphous to nano-crystalline SiC thin films ...
Indian Academy of Sciences (India)
Administrator
phous SiC to cubic nano-crystalline SiC films with the increase in the gas flow ratio. Raman scattering ... Auger electron spectroscopy showed that the carbon incorporation in the .... with a 514 nm Ar+ laser excitation source and the laser.
International Nuclear Information System (INIS)
Costa e Silva, Danilo Lopes
2015-01-01
In this work, carbon thin films were produced by the magnetron sputtering technique using single crystal substrates of alumina c-plane (0001) and Si (111) and Si (100) substrates, employing Co, Ni and Cu as intermediate films (buffer-layers). The depositions were conducted in three stages, first with cobalt buffer-layers where only after the production of a large number of samples, the depositions using cooper buffer-layers were carried out on Si substrates. Then, depositions were performed with nickel buffer layers using single-crystal alumina substrates. The crystallinity of the carbon films was evaluated by using the technique of Raman spectroscopy and, then, by X-ray diffraction (XRD). The morphological characterization of the films was performed by scanning electron microscopy (SEM and FEG-SEM) and high-resolution transmission electron microscopy (HRTEM). The XRD peaks related to the carbon films were observed only in the results of the samples with cobalt and nickel buffer-layers. The Raman spectroscopy showed that the carbon films with the best degree of crystallinity were the ones produced with Si (111) substrates, for the Cu buffers, and sapphire substrates for the Ni and Co buffers, where the latter resulted in a sample with the best crystallinity of all the ones produced in this work. It was observed that the cobalt has low recovering over the alumina substrates when compared to the nickel. Sorption tests of Ce ions by the carbon films were conducted in two samples and it was observed that the sorption did not occur probably because of the low crystallinity of the carbon films in both samples. (author)
Detection of low-contrast images in film-grain noise.
Naderi, F; Sawchuk, A A
1978-09-15
When low contrast photographic images are digitized by a very small aperture, extreme film-grain noise almost completely obliterates the image information. Using a large aperture to average out the noise destroys the fine details of the image. In these situations conventional statistical restoration techniques have little effect, and well chosen heuristic algorithms have yielded better results. In this paper we analyze the noisecheating algorithm of Zweig et al. [J. Opt. Soc. Am. 65, 1347 (1975)] and show that it can be justified by classical maximum-likelihood detection theory. A more general algorithm applicable to a broader class of images is then developed by considering the signal-dependent nature of film-grain noise. Finally, a Bayesian detection algorithm with improved performance is presented.
Directory of Open Access Journals (Sweden)
Guoai He
2017-02-01
Full Text Available Controlling grain size in polycrystalline nickel base superalloy is vital for obtaining required mechanical properties. Typically, a uniform and fine grain size is required throughout forging process to realize the superplastic deformation. Strain amount occupied a dominant position in manipulating the dynamic recrystallization (DRX process and regulating the grain size of the alloy during hot forging. In this article, the high-throughput double cone specimen was introduced to yield wide-range strain in a single sample. Continuous variations of effective strain ranging from 0.23 to 1.65 across the whole sample were achieved after reaching a height reduction of 70%. Grain size is measured to be decreased from the edge to the center of specimen with increase of effective strain. Small misorientation tended to generate near the grain boundaries, which was manifested as piled-up dislocation in micromechanics. After the dislocation density reached a critical value, DRX progress would be initiated at higher deformation region, leading to the refinement of grain size. During this process, the transformations from low angle grain boundaries (LAGBs to high angle grain boundaries (HAGBs and from subgrains to DRX grains are found to occur. After the accomplishment of DRX progress, the neonatal grains are presented as having similar orientation inside the grain boundary.
International Nuclear Information System (INIS)
Adamska, A.M.; Bright, E. Lawrence; Sutcliffe, J.; Liu, W.; Payton, O.D.; Picco, L.; Scott, T.B.
2015-01-01
Polycrystalline uranium dioxide thin films were grown on nickel substrates via aqueous electrodeposition of a precursor uranyl salt. The arising semiconducting uranium dioxide thin films exhibited a tower-like morphology, which may be suitable for future application in 3D solar cell applications. The thickness of the homogenous, tower-like films reached 350 nm. Longer deposition times led to the formation of thicker (up to 1.5 μm) and highly porous films. - Highlights: • Electrodeposition of polycrystalline UO_2 thin films • Tower-like morphology for 3D solar cell applications • Novel technique for separation of heavy elements from radioactive waste streams
Surmeneva, Maria A.; Surmenev, Roman A.; Nikonova, Yulia A.; Selezneva, Irina I.; Ivanova, Anna A.; Putlyaev, Valery I.; Prymak, Oleg; Epple, Matthias
2014-10-01
A series of nanostructured low-crystalline hydroxyapatite (HA) coatings averaging 170, 250, and 440 nm in thickness were deposited onto previously etched titanium substrates through radio-frequency (RF) magnetron sputtering. The HA coatings were analyzed using infrared spectroscopy (FTIR), X-ray diffraction (XRD), and scanning and transmission electron microscopy (SEM and TEM). Cross sections of the thin specimens were prepared by FIB to study the microstructure of the coatings by TEM. The deposition process formed nano-scale grains, generating an amorphous layer at the substrate/coating interface and inducing the growth of a columnar grain structure perpendicular to the substrate surface. A microstructural analysis of the film confirmed that the grain size and crystallinity increased when increasing the deposition time. The nanostructured HA coatings were not cytotoxic, as proven by in vitro assays using primary dental pulp stem cells and mouse fibroblast NCTC clone L929 cells. Low-crystallinity HA coatings with different thicknesses stimulated cells to attach, proliferate and form mineralized nodules on the surface better than uncoated titanium substrates.
Interaction of atomic hydrogen with ethylene adsorbed on nickel films
International Nuclear Information System (INIS)
Korchak, V.N.; Tret'yakov, I.I.; Kislyuk, M.U.
1976-01-01
The reactivity of ethylene adsorbed on the pure films of nickel at various temperatures was studied with respect to hydrogen atoms generated in the gaseous phase. The experiments were conducted in a glass vacuum apparatus enabling one to obtain the highest vacuum up to 2x20 -10 torr. The catalyst, nickel films, was produced by their deposition onto the walls of the glass reactor at a pressure of the residual gas of 10 -9 torr and a temperature of the walls of 25 deg C. Gas purity was analyzed by the mass spectrometric method. The ethylene adsorbed at the temperatures below 173 deg K reacted readily with the hydrogen atoms to yield ethane. The process ran without practically any activation energy involved and was limited by the attachment of the first hydrogen atom to the ethylene molecule. The efficiency of this interaction was 0.02 of the number of the hydrogen atoms collisions against the surface occupied by the ethylene. The adsorption of the ethylene at room and higher temperatures was accompanied by its disproportioning with the release of the hydrogen into the gaseous phase and a serious destruction of the ethylene molecules adsorbed to produce hydrogen residues interacting with neither molecular nor atomic hydrogen [ru
International Nuclear Information System (INIS)
Bora, Pritom J; Ramamurthy, Praveen C; Madras, Giridhar; Vinoy, K J; Kishore
2015-01-01
A solid waste material fly ash cenosphere (FAC) was nickel coated and polyaniline in situ polymerized at −30 ± 2 °C in nitrogen atmosphere. A thin film of this composite material was prepared by solution processing and surface morphology/topography was studied. High electromagnetic shielding effectiveness (SE) was obtained for this film; 59 ± 4 μm and 133 ± 4 μm films show an average of 38 and 60 dB SE, respectively, in the frequency range 8.2–12.4 GHz (X-band). Unlike PANI film, the SE of these composite films is high at high frequency. The presence of magneto dielectric microsphere (Ni-FAC) increases the heterogeneity of the composite film in an efficient way for EMI shielding by changing film topography and increasing ac conductivity and permeability. (paper)
Energy Technology Data Exchange (ETDEWEB)
Yang Changjun; Gong Chuqing; Peng Tianyou [College of Chemistry and Molecular Sciences, Wuhan University, Wuhan 430072 (China); Deng Kejian [Key Laboratory of Catalysis and Materials Science of the State Ethnic Affairs Commission and Ministry of Education, South-Central University for Nationalities, Wuhan 430074 (China); Zan Ling, E-mail: irlab@whu.edu.cn [College of Chemistry and Molecular Sciences, Wuhan University, Wuhan 430072 (China)
2010-06-15
A novel photodegradable polyvinyl chloride (PVC)-vitamin C (VC)-TiO{sub 2} nano-composite film was prepared by embedding VC modified nano-TiO{sub 2} photocatalyst into the commercial PVC plastic. The solid-phase photocatalytic degradation behavior of PVC-VC-TiO{sub 2} nano-composite film under UV light irradiation was investigated and compared with those of the PVC-TiO{sub 2} film and the pure PVC film, with the aid of UV-Vis spectroscopy, scanning electron microscopy (SEM), weight loss monitoring, and X-ray diffraction spectra (XRD). The results show that PVC-VC-TiO{sub 2} nano-composite film has a high photocatalytic activity; the photocatalytic degradation rate of it is two times higher than that of PVC-TiO{sub 2} film and fifteen times higher than that of pure PVC film. The optimal mass ratio of VC to TiO{sub 2} is found to be 0.5. The mechanism of enhancing photocatalytic activity is attributed to the formation of a Ti{sup IV}-VC charge-transfer complex with five-member chelate ring structure and a rapid photogenerated charge separation is thus achieved.
Subcooled film boiling heat transfer on a high temperature sphere in very dilute Al2O3 nano-fluids
International Nuclear Information System (INIS)
Hyun Sun Park; Dereje Shiferaw; Bal Raj Sehgal
2005-01-01
Full text of publication follows: nano-fluids, or conventional liquids, e.g., water, with small concentration of nano-particles uniformly suspended, have attracted attention as a new heat transport medium with enhanced thermo-physical properties. Up to the present, only exploratory experiments on nano-fluids have been reported. Das et al (Int. J. Heat Mass Transfer 43, pp 3701-3707, 2003) conducted boiling experiments with water containing 38 nm Al 2 O 3 nano-particles. They observed deterioration in the nucleate boiling heat transfer due to the deposition of nano-particles. Boiling experiments conducted by Vassallo et al (Int. J. Heat Mass Transfer 47, pp 407-411, 2004) using silica nano-fluid using 0.4 mm diameter NiCr wire showed three times higher critical heat flux (CHF) and the wire traversed the film boiling region before it failed. Another independent experiment performed on 1 cm 2 square plate with a very low concentration of nano-particles ranging from 0.01 to 0.05 g/liter and at under pressure (2.89 psia), nano-fluids resulted in drastic 2∼3 times enhancement of the CHF (You and Kim, Appl. Phys. Lett. 83. No 16, 2003). However in all the aforementioned studies no appropriate explanation of the CHF enhancement has been advanced. The measured 2-3 times higher critical heat flux for very dilute nano-fluids may have high significance if such nano-fluids could be employed in heat transport systems. Recently, we investigated the effect of nano-particles on film boiling, which governs heat transfer during accident conditions in a reactor plant, e.g., in coolability of a degraded core, or a particulate debris bed or a core melt, and in steam explosions. Our previous experiments performed on film boiling in nano-fluids having larger concentrations of 5, 10, and 20 g/liter than those in You's experiments showed that the nano-fluids lower the film boiling temperature, decrease the film boiling heat transfer and provide a much thicker and more stable film than
Effect of nano-silver hydrogel coating film on deep partial thickness scald model of rabbit
Peng Xi; Yan Li; Xiaojin Ge; Dandan Liu; Mingsan Miao
2018-01-01
Objective: Observing the effect of nano-silver hydrogel coating film on deep partial thickness scald model of rabbit. Method: We prepared boiling water scalded rabbits with deep II degree scald models and applied high, medium and low doses of nano-silver hydrogel coating film for different time and area. Then we compared the difference of burned paper weight before administration and after administration model burns, burn local skin irritation points infection, skin crusting and scabs from th...
Nakano, M.; Kondo, H.; Yamashita, A.; Yanai, T.; Itakura, M.; Fukunaga, H.
2018-05-01
PLD (Pulsed Laser Deposition) method with high laser energy density (LED) above 10 J/cm2 followed by a flash annealing enabled us to obtain isotropic nano-composite thick-film magnets with (BH)max ≧ 80 kJ/m3 on polycrystalline Ta substrates. We also have demonstrated that a dispersed structure composed of α-Fe together with Nd2Fe14B phases with the average grain diameter of approximately 20 nm could be formed on the Ta substrates. In this study, we tried to enhance the (BH)max value by controlling the microstructure due to the usage of different metal based substrates with each high melting point such as Ti, Nb, and W. Although it was difficult to vary the microstructure and to improve the magnetic properties of the films deposited on the substrates, we confirmed that isotropic thick-film magnets with (BH)max ≧ 80 kJ/m3 based on the nano-dispersed α-Fe and Nd2Fe14B phases could be obtained on various metal substrates with totally different polycrystalline structure. On the other hand, the use of a glass substrate lead to the deterioration of magnetic properties of a film prepared using the same preparation process.
Study of grain boundary tunneling in barium-titanate ceramic films
Wong, H; Poon, M C
1999-01-01
The temperature and the electric-field dependences of the current-voltage characteristics and the low-frequency noise of barium-titanate ceramic films are studied. An abnormal field dependence is observed in the resistivity of BaTiO sub 3 materials with a small average grain size. In addition, experiments show that the low-frequency noise behaviors are governed by grain-boundary tunneling at room temperature and by trapping-detrapping of grain-boundary states at temperatures above the Curie point. Physical models for the new observations are developed. Results suggest that grain-boundary tunneling of carriers is as important as the double Schottky barrier in the current conduction in BaTiO sub 3 materials with small grain sizes.
Nanoscale strengthening mechanisms in metallic thin film systems
Schoeppner, Rachel Lynn
Nano-scale strengthening mechanisms for thin films were investigated for systems governed by two different strengthening techniques: nano-laminate strengthening and oxide dispersion strengthening. Films were tested under elevated temperature conditions to investigate changes in deformation mechanisms at different operating temperatures, and the structural stability. Both systems exhibit remarkable stability after annealing and thus long-term reliability. Nano-scale metallic multilayers with smaller layer thicknesses show a greater relative resistance to decreasing strength at higher temperature testing conditions than those with larger layer thicknesses. This is seen in both Cu/Ni/Nb multilayers as well as a similar tri-component bi-layer system (Cu-Ni/Nb), which removed the coherent interface from the film. Both nanoindentation and micro-pillar compression tests investigated the strain-hardening ability of these two systems to determine what role the coherent interface plays in this mechanism. Tri-layer films showed a higher strain-hardening ability as the layer thickness decreased and a higher strain-hardening exponent than the bi-layer system: verifying the presence of a coherent interface increases the strain-hardening ability of these multilayer systems. Both systems exhibited hardening of the room temperature strength after annealing, suggesting a change in microstructure has occurred, unlike that seen in other multilayer systems. Oxide dispersion strengthened Au films showed a marked increase in hardness and wear resistance with the addition of ZnO particles. The threshold for stress-induced grain-refinement as opposed to grain growth is seen at concentrations of at least 0.5 vol%. These systems exhibited stable microstructures during thermal cycling in films containing at least 1.0%ZnO. Nanoindentation experiments show the drop in hardness following annealing is almost completely attributed to the resulting grain growth. Four-point probe resistivity
International Nuclear Information System (INIS)
Laitinen, T.; Bojinov, M.; Betova, I.; Maekelae, K.; Saario, T.
1999-01-01
The construction materials used in coolant systems in nuclear power plants become covered with oxide films as a result of exposure to the aqueous environment. The susceptibility of the materials to different forms of corrosion, as well as the extent of the incorporation of radioactive species on the surfaces of the primary circuit, are greatly influenced by the physical and chemical properties of these oxide films. The composition and characteristics of the oxide films in turn depend on the applied water chemistry. This work was undertaken in order to collect and evaluate the present views on the structure and behaviour of oxide films formed on iron- and nickel-based materials in aqueous environments. This survey should serve to recognise the areas in which more understanding and research effort is needed. The review begins with a discussion on the bulk oxides of iron, nickel and chromium, as well as their mixed oxides. In addition to bulk oxides, the structure and properties of oxide films forming on pure iron, nickel and chromium and on iron- and nickel-based engineering alloys are considered. General approaches to model the structure and growth of oxide films on metals are discussed in detail. The specific features of the oxide structures, properties and growth at high temperatures are presented with special focus on the relevance of existing models. Finally, the role of oxide films in localised corrosion, oxide breakdown pitting. Stress corrosion cracking and related phenomena is considered. The films formed on the surfaces of iron- and nickel-based alloys in high-temperature aqueous environments generally comprise two layers, i.e. the so-called duplex structure. The inner part is normally enriched in chromium and has a more compact structure, while the outer part is enriched in iron and has a cracked or porous structure. The information collected clearly indicates the effect of the chemical environment on the properties of oxide films growing on metal surfaces
Energy Technology Data Exchange (ETDEWEB)
Laitinen, T.; Bojinov, M.; Betova, I.; Maekelae, K.; Saario, T. [VTT Manufacturing Technology, Espoo (Finland)
1999-01-01
The construction materials used in coolant systems in nuclear power plants become covered with oxide films as a result of exposure to the aqueous environment. The susceptibility of the materials to different forms of corrosion, as well as the extent of the incorporation of radioactive species on the surfaces of the primary circuit, are greatly influenced by the physical and chemical properties of these oxide films. The composition and characteristics of the oxide films in turn depend on the applied water chemistry. This work was undertaken in order to collect and evaluate the present views on the structure and behaviour of oxide films formed on iron- and nickel-based materials in aqueous environments. This survey should serve to recognise the areas in which more understanding and research effort is needed. The review begins with a discussion on the bulk oxides of iron, nickel and chromium, as well as their mixed oxides. In addition to bulk oxides, the structure and properties of oxide films forming on pure iron, nickel and chromium and on iron- and nickel-based engineering alloys are considered. General approaches to model the structure and growth of oxide films on metals are discussed in detail. The specific features of the oxide structures, properties and growth at high temperatures are presented with special focus on the relevance of existing models. Finally, the role of oxide films in localised corrosion, oxide breakdown pitting. Stress corrosion cracking and related phenomena is considered. The films formed on the surfaces of iron- and nickel-based alloys in high-temperature aqueous environments generally comprise two layers, i.e. the so-called duplex structure. The inner part is normally enriched in chromium and has a more compact structure, while the outer part is enriched in iron and has a cracked or porous structure. The information collected clearly indicates the effect of the chemical environment on the properties of oxide films growing on metal surfaces
Layer-dependent supercapacitance of graphene films grown by chemical vapor deposition on nickel foam
Chen, Wei; Fan, Zhongli; Zeng, Gaofeng; Lai, Zhiping
2013-01-01
High-quality, large-area graphene films with few layers are synthesized on commercial nickel foams under optimal chemical vapor deposition conditions. The number of graphene layers is adjusted by varying the rate of the cooling process. It is found
Energy Technology Data Exchange (ETDEWEB)
Adekunle, Abolanle S.; Ozoemena, Kenneth I. [Department of Chemistry, University of Pretoria, Pretoria 0002 (South Africa)
2008-08-01
The electron transfer behaviour of nickel film-decorated single-walled carbon nanotubes (SWCNTs-Ni) at edge plane pyrolytic graphite electrodes (EPPGEs) was investigated. The impact of SWCNTs on the redox properties of the nickel film was investigated with cyclic voltammetry and electrochemical impedance spectroscopy (EIS). From EIS data, obtained using ferrocyanide/ferricyanide as a redox probe, we show that the electrodes based on nickel and nickel oxide films follow electrical equivalent circuit models typical of partial charge transfer or adsorption-controlled kinetics, resembling the 'electrolyte-insulator-semiconductor sensors (EIS)'. From the models, we prove that EPPGE-SWCNT-Ni exhibits the least resistance to charge transport compared to other electrodes (approximately 30 times faster than the EPPGE-SWCNT-NiO, 25 times faster than EPPGE-SWCNT, and over 300 times faster than the bare EPPGE) suggesting the ability of the SWCNTs to act as efficient conducting species that facilitate electron transport of the integrated nickel and nickel oxide particles. (author)
Abundances of presolar silicon carbide grains in primitive meteorites determined by NanoSIMS
Davidson, Jemma; Busemann, Henner; Nittler, Larry R.; Alexander, Conel M. O.'D.; Orthous-Daunay, François-Régis; Franchi, Ian A.; Hoppe, Peter
2014-08-01
It has been suggested that the matrices of all chondrites are dominated by a common material with Ivuna-like (CI) abundances of volatiles, presolar grains and insoluble organic matter (IOM) (e.g., Alexander, 2005). However, matrix-normalized abundances of presolar silicon carbide (SiC) grains estimated from their noble gas components show significant variations in even the most primitive chondrites (Huss and Lewis, 1995; Huss et al., 2003), in contradiction to there being a common chondrite matrix material. Here we report presolar SiC abundances determined by NanoSIMS raster ion imaging of IOM extracted from primitive members of different meteorite groups. We show that presolar SiC abundance determinations are comparable between NanoSIMS instruments located at three different institutes, between residues prepared by different demineralization techniques, and between microtomed and non-microtomed samples. Our derived SiC abundances in CR chondrites are comparable to those found in the CI chondrites (∼30 ppm) and are much higher than previously determined by noble gas analyses. The revised higher CR SiC abundances are consistent with the CRs being amongst the most primitive chondrites in terms of the isotopic compositions and disordered nature of their organic matter. Similar abundances between CR1, CR2, and CR3 chondrites indicate aqueous alteration on the CR chondrite parent body has not progressively destroyed SiC grains in them. A low SiC abundance for the reduced CV3 RBT 04133 can be explained by parent body thermal metamorphism at an estimated temperature of ∼440 °C. Minor differences between primitive members of other meteorite classes, which did not experience such high temperatures, may be explained by prolonged oxidation at lower temperatures under which SiC grains formed outer layers of SiO2 that were not thermodynamically stable, leading to progressive degassing/destruction of SiC.
International Nuclear Information System (INIS)
Ebothé, Jean
2014-01-01
The present study investigates the influence of surface features on the magnetic properties of thin films by taking into account the role of the surface roughness (σ) /film thickness (d) ratio. Examination of the ratio from microscopic down to mesoscopic d values is then undertaken in connection with the evolution of the films' magnetic properties (p). The double dependence of p on d and σ expected from a real nano-film, emerged into a new relative approach to film characteristics, associated with the described (σ/d) ratio. A direct and consistent link between surface roughness and magnetic properties is established with no film surface treatment. This results in a revisited analytical treatment adapted for the study of nano-structured and mesoscopic-scale films. Application to the topography and magnetic properties of nano-crystallized Ni electrodeposits 60 < d < 1200 nm thick and grown on Au substrate, led to the identification of their Bloch-type acting magnetic structures. (papers)
Directory of Open Access Journals (Sweden)
Yuan Jin
2015-12-01
Full Text Available Grain growth experiments were performed on Inconel™ 718 to investigate the possible correlation of the annealing twin density with grain size and with annealing temperature. Those experiments were conducted at different temperatures in the δ supersolvus domain and under such conditions that only capillarity forces were involved in the grain boundary migration process. In the investigated range, there is a strong inverse correlation of the twin density with the average grain size. On the other hand, the twin density at a given average grain size is not sensitive to annealing temperature. Consistent with previous results for pure nickel, the twin density evolution in Inconel™ 718 is likely to be mainly controlled by the propagation of the pre-existing twins of the growing grains; i.e., the largest ones of the initial microstructure. Almost no new twin boundaries are created during the grain growth process itself. Therefore, the twin density at a given average grain size is mainly dependent on the twin density in the largest grains of the initial microstructure and independent of the temperature at which grains grow. Based on the observations, a mean field model is proposed to predict annealing twin density as a function of grain size during grain growth.
International Nuclear Information System (INIS)
Jang, Jin Nyoung; Song, Byoung Chul; Lee, Dong Hyeok; Yoo, Suk Jae; Lee, Bonju; Hong, MunPyo
2011-01-01
A novel deposition process for nano-crystalline silicon (nc-Si) thin films was developed using neutral beam assisted chemical vapor deposition (NBaCVD) technology for the application of the thin film transistor (TFT) backplane of flexible active matrix organic light emitting diode (AMOLED). During the formation of a nc-Si thin film, the energetic particles enhance nano-sized crystalline rather microcrystalline Si in thin films. Neutral Particle Beam (NPB) affects the crystallinity in two ways: (1) NPB energy enhances nano-crystallinity through kinetic energy transfer and chemical annealing, and (2) heavier NPB (such as Ar) induces damage and amorphization through energetic particle impinging. Nc-Si thin film properties effectively can be changed by the reflector bias. As increase of NPB energy limits growing the crystalline, the performance of TFT supports this NPB behavior. The results of nc-Si TFT by NBaCVD demonstrate the technical potentials of neutral beam based processes for achieving high stability and reduced leakage in TFT backplanes for AMOLEDs.
Antimicrobial and Barrier Properties of Bovine Gelatin Films Reinforced by Nano TiO2
Directory of Open Access Journals (Sweden)
R. Nassiri
2013-11-01
Full Text Available The effects of nano titanium dioxide incorporation were investigated on the water vaporpermeability, oxygen permeability, and antimicrobial properties of bovine gelatin films. The nano TiO2 (TiO2-N was homogenized by sonication and incorporated into bovine gelatin solutions at different concentrations(e.g. 1, 2, 3, and 5% w/w of dried gelatin. The permeability of the films to water vapor and oxygen wassignificantly decreased by incorporating of low concentration TiO2-N to gelatin solutions. TiO2-N gelatin filmsshowed an excellent antimicrobial activity against Staphylococcus aureus and Escherichia coli. Theseproperties suggest that TiO2-N has the potential as filler in gelatin-based films for using as an active packagingmaterials in pharmaceutical and food packaging industries.
Directory of Open Access Journals (Sweden)
Sarıışık Merih
2010-01-01
Full Text Available Abstract ZnO nanoparticle–based multilayer nanocomposite films were fabricated on cationized woven cotton fabrics via layer-by-layer molecular self-assembly technique. For cationic surface charge, cotton fabrics were pretreated with 2,3-epoxypropyltrimethylammonium chloride (EP3MAC by pad-batch method. XPS and SEM were used to examine the deposited nano-ZnO multilayer films on the cotton fabrics. The nano-ZnO films deposited on cotton fabrics exhibited excellent antimicrobial activity against Staphylococcus aureus bacteria. The results also showed that the coated fabrics with nano-ZnO multilayer films enhanced the protection of cotton fabrics from UV radiation. Physical tests (tensile strength of weft and warp yarns, air permeability and whiteness values were performed on the fabrics before and after the treatment with ZnO nanoparticles to evaluate the effect of layer-by-layer (LbL process on cotton fabrics properties.
Microstructural Studies of Ni-P Thick Film Resistor Temperature Sensors
Directory of Open Access Journals (Sweden)
Barbara Holodnik
1986-01-01
Full Text Available Thick Ni-P films have been widely investigated at our Institute. This article tends to visualize by use of various microscopic methods how the growth and sintering of individual conducting grains, results in the formation of nickel dendrites responsible for the metallic character of electrical conduction.
Energy Technology Data Exchange (ETDEWEB)
Fan, Junpeng [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); Bian, Xiufang, E-mail: xfbian@sdu.edu.cn [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); Niu, Yuchao [Department of Materials Science and Engineering, Shandong Jianzhu University, Fengming Road, Lingang Development Zone, Jinan 250101 (China); Bai, Yanwen; Xiao, Xinxin; Yang, Chuncheng; Yang, Jianfei; Yang, Jinyue [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China)
2013-11-15
By using the chemically dealloying method, three-dimensional nano-porous silver films (3-D NPSFs) are fabricated into a novel sensor for detecting hydrogen peroxide. The precursor films are prepared by high vacuum magnetron co-sputtering. High-resolution transmission electron microscope (HRTEM) and scanning electron microscope (SEM) are taken to investigate the structure and the micro morphology of the precursor films and nano-porous films. We find that the precursor films are composed of glassy matrix and nanocrystallines. After dealloying, the films exhibit a combination of homogenously distributed pores and silver filaments, and exhibit an open, three dimensional bicontinuous interpenetrating ligament–channel structure. Thickness and morphology of the films can be easily controlled by the sputtering time and alloy composition of the precursor films, respectively. In addition, NPSFs show a good linear responding for the concentration of hydrogen peroxide in phosphate buffered solutions, which indicates NPSFs could be a promising electrochemical material for hydrogen peroxide detection.
Energy Technology Data Exchange (ETDEWEB)
Arun, B. [Materials Science and Technology Division, CSIR-National Institute for Interdisciplinary Science and Technology, Trivandrum (India); Academy of Scientific and Innovative Research (AcSIR), CSIR, Trivandrum (India); Suneesh, M.V. [Materials Science and Technology Division, CSIR-National Institute for Interdisciplinary Science and Technology, Trivandrum (India); Vasundhara, M., E-mail: vasu.mutta@gmail.com [Materials Science and Technology Division, CSIR-National Institute for Interdisciplinary Science and Technology, Trivandrum (India)
2016-11-15
We have prepared bulk and nano-sized Nd{sub 0.67}Sr{sub 0.33}MnO{sub 3} manganites by solid state and low-temperature mild solgel methods respectively. Both the compounds crystallized into an orthorhombic structure with Pbnm space group confirmed from Rietveld refinement of X-ray powder diffraction patterns. Nano-grained compound shows an average particle size of 22 nm with broad grain size distribution revealed from the Transmission electron micrographs. It appeared that the long range ferromagnetic order becomes unstable upon the reduction of the samples dimension down to nano meter scale. DC magnetization and AC susceptibility results showed frustration of spins in nano-grained compound and thereby it could lead to a cluster glass-like behaviour. Temperature dependence of electrical resistivity under different magnetic fields shows the broad maxima at higher temperatures and a low temperature upturn in both the compounds, however, the latter is more prominent in the nano grained compound. Combination of Kondo effect with electron and phonon interactions govern the low temperature resistivity and a small polaron hopping mechanism dominates at high temperatures for both the compounds. The magnetoresistance is understood by the effect of spin polarized tunneling through the grain boundary. The experimental results revealed that the reduction in particle size influences severely on the magnetic, electrical and magneto transport properties. - Highlights: • Long range ferromagnetic ordered state become unstable in case of nano compound. • It shows broad magnetic transition and cluster glass nature. • Kondo effect with electron-phonon interactions dominate the resistivity at low temperature.
Choi, Woong; Lee, Jung-Kun; Findikoglu, Alp T.
2006-12-01
The authors report studies of the effect of grain alignment on interface trap density of thermally oxidized aligned-crystalline silicon (ACSi) films by means of capacitance-voltage (C-V) measurements. C-V curves were measured on metal-oxide-semiconductor (MOS) capacitors fabricated on ⟨001⟩-oriented ACSi films on polycrystalline substrates. From high-frequency C-V curves, the authors calculated a decrease of interface trap density from 2×1012to1×1011cm-2eV-1 as the grain mosaic spread in ACSi films improved from 13.7° to 6.5°. These results demonstrate the effectiveness of grain alignment as a process technique to achieve significantly enhanced performance in small-grained (⩽1μm ) polycrystalline Si MOS-type devices.
Czech Academy of Sciences Publication Activity Database
Všianská, Monika; Šob, Mojmír
2011-01-01
Roč. 56, č. 6 (2011), s. 817-840 ISSN 0079-6425 R&D Projects: GA AV ČR IAA100100920; GA MŠk(CZ) OC10008; GA ČR GD106/09/H035 Institutional research plan: CEZ:AV0Z20410507 Keywords : grain boundaries * segregation * nickel * embrittlement Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 18.216, year: 2011
Venkatesh, C.; Sundara Moorthy, N.; Venkatesan, R.; Aswinprasad, V.
The moving parts of any mechanism and machine parts are always subjected to a significant wear due to the development of friction. It is an utmost important aspect to address the wear problems in present environment. But the complexity goes on increasing to replace the worn out parts if they are very precise. Technology advancement in surface engineering ensures the minimum surface wear with the introduction of polycrystalline nano nickel coating. The enhanced tribological property of the nano nickel coating was achieved by the development of grain size and hardness of the surface. In this study, it has been decided to focus on the optimized parameters of the pulsed electro deposition to develop such a coating. Taguchi’s method coupled gray relational analysis was employed by considering the pulse frequency, average current density and duty cycle as the chief process parameters. The grain size and hardness were considered as responses. Totally, nine experiments were conducted as per L9 design of experiment. Additionally, response graph method has been applied to determine the most significant parameter to influence both the responses. In order to improve the degree of validation, confirmation test and predicted gray grade were carried out with the optimized parameters. It has been observed that there was significant improvement in gray grade for the optimal parameters.
Onozuka, Tomoya; Chikamatsu, Akira; Katayama, Tsukasa; Hirose, Yasushi; Harayama, Isao; Sekiba, Daiichiro; Ikenaga, Eiji; Minohara, Makoto; Kumigashira, Hiroshi; Hasegawa, Tetsuya
2017-03-29
Perovskite nickel oxides are of fundamental as well as technological interest because they show large resistance modulation associated with phase transition as a function of the temperature and chemical composition. Here, the effects of fluorine doping in perovskite nickelate NdNiO 3 epitaxial thin films are investigated through a low-temperature reaction with polyvinylidene fluoride as the fluorine source. The fluorine content in the fluorinated NdNiO 3-x F x films is controlled with precision by varying the reaction time. The fully fluorinated film (x ≈ 1) is highly insulating and has a bandgap of 2.1 eV, in contrast to NdNiO 3 , which exhibits metallic transport properties. Hard X-ray photoelectron and soft X-ray absorption spectroscopies reveal the suppression of the density of states at the Fermi level as well as the reduction of nickel ions (valence state changes from +3 to +2) after fluorination, suggesting that the strong Coulombic repulsion in the Ni 3d orbitals associated with the fluorine substitution drives the metal-to-insulator transition. In addition, the resistivity of the fluorinated films recovers to the original value for NdNiO 3 after annealing in an oxygen atmosphere. By application of the reversible fluorination process to transition-metal oxides, the search for resistance-switching materials could be accelerated.
Fabrication and characteristics of self-assembly nano-polystyrene films by laser induced CVD
Energy Technology Data Exchange (ETDEWEB)
Xiao, Tingting [Department of Applied Physics, Chongqing University, Chongqing 401331 (China); Science and Technology on Plasma Physics Laboratory, Research Center of Laser Fusion, CAEP, Mianyang 621900 (China); Cai, Congzhong [Department of Applied Physics, Chongqing University, Chongqing 401331 (China); Peng, Liping [Science and Technology on Plasma Physics Laboratory, Research Center of Laser Fusion, CAEP, Mianyang 621900 (China); Wu, Weidong, E-mail: wuweidongding@163.com [Science and Technology on Plasma Physics Laboratory, Research Center of Laser Fusion, CAEP, Mianyang 621900 (China)
2013-10-01
The self-assembly nano-polystyrene (PS) films have been prepared by laser induced CVD at room temperature. The XPS, Raman and UV–vis absorption spectra all indicated that the films were PS. The optical properties, microstructure and controllable nanostructure of PS films have been investigated. Dewetting-like microstructure in PS films was investigated and uniform island structures with a diameter of about 200 nm were observed at the deposition pressure of 14 Pa. The films possess good toughness and precisely controlled thicknesses. The free-standing PS films with thickness of 10 nm could be obtained by this method though a series of process.
Nanostructured CdS thin films deposited by spray pyrolysis method
Energy Technology Data Exchange (ETDEWEB)
Kerimova, A.; Bagiyev, E.; Aliyeva, E.; Bayramov, A. [Institute of Physics, Azerbaijan National Academy of Sciences, Baku (Azerbaijan)
2017-06-15
Influence of solution pH on the structural and optical properties of CdS films deposited by conventional spray pyrolysis technique was studied. X-Ray Diffraction (XRD), Atomic Force Microscopy (AFM), Photoluminescence spectroscopy (PLS), and Spectroscopic Ellipsometry (SE) methods were used for the characterization of the deposited films. PL spectrum of the film deposited from the solution with pH = 10.2 shows broad-band PL emission located at 460 nm (2.7 eV), which can be attributed to the quantum size effect at grain sizes of <10 nm. No shifts of ε{sub 1} and ε{sub 2} due to the quantum size effect are observed in dielectric function spectra, what can be caused by low concentration of nano-sized (<10 nm) CdS grains. The change in the film properties with the pH of the solution was analyzed in terms of variation of grain sizes of the polycrystalline films. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)
Direct imaging of dopant distribution in polycrystalline ZnO films
Czech Academy of Sciences Publication Activity Database
Lorenzo, F.; Aebersold, A.B.; Morales-Masis, M.; Ledinský, Martin; Escrig, S.; Vetushka, Aliaksi; Alexander, D.T.L.; Hessler-Wyser, A.; Fejfar, Antonín; Hébert, C.; Nicolay, S.; Ballif, C.
2017-01-01
Roč. 9, č. 8 (2017), s. 7241-7248 ISSN 1944-8244 R&D Projects: GA ČR GC16-10429J Institutional support: RVO:68378271 Keywords : dopant distribution * film polarity * grain boundaries * NanoSIMS * polycrystalline film * zinc oxide Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 7.504, year: 2016
Texture in equal-channel angular pressed aluminum and nickel
Energy Technology Data Exchange (ETDEWEB)
Vogel, S.C.; Beyerlein, I.J.; Bourke, M.A.M.; Tome, C.N.; Rangaswamy, P. [Los Alamos National Lab., Los Alamos, NM (United States); Xu, C.; Langdon, T.G. [Univ. of Southern California, Los Angeles, CA (United States)
2002-07-01
Nano-structured metals with advantageous mechanical properties can be produced using severe plastic deformation techniques such as equal channel angular pressing (ECAP). Metals and alloys processed by ECAP have much higher yield strengths than the equivalent unprocessed material while retaining high ductilities, an extremely attractive combination of properties. Implicit in the process are the introduction of repetitive shear strains of 100% which introduce texture, the modeling of which is challenging. In this work, we present results from a neutron diffraction study on aluminum and nickel samples processed by ECAP. The results are compared to predictions from a visco-plastic self-consistent (VPSC) model. By taking into account grain-grain interactions in the model the agreement between the predicted and measured orientation distributions is improved. The results show also that the initial texture affects the texture evolution, at least up to strains of the order of {proportional_to}1, i.e. one ECAP pass. (orig.)
Energy Technology Data Exchange (ETDEWEB)
Savaloni, Hadi, E-mail: savaloni@khayam.ut.ac.ir [Department of Physics, University of Tehran, North-Kargar Street, Tehran (Iran, Islamic Republic of); Esfandiar, Ali [Department of Physics, University of Tehran, North-Kargar Street, Tehran (Iran, Islamic Republic of)
2011-09-01
Graded chiral zig-zag shaped nano-sculptured silver thin films (GCZSSTF) were produced in two stages using oblique deposition technique together with rotation of substrate about its surface normal while a shadowing block was also fixed at Center of the substrate holder. Chrystallographic and morphological structure of these films were obtained using X-ray diffraction (XRD) and atomic force microscopy (AFM). Spectrophotometry was used to obtain their optical behavior while their application in both hydrophobicity and gas sensing was also investigated. XRD results showed a dominant (1 1 1) orientation growth on the zig arm of the structure while by addition of the second arm (zag) the crystallographical growth orientation changed to (2 2 0). The anisotropic nano-structure of these films was also distinguished through (1 - R) spectra. A common peak at about 350 nm related to the TM mode of plasmon resonances and a broad shoulder at about 420 nm for the s-polarized light and at 620 nm for the p-polarized light corresponding to the LM mode of plasmon resonances are observed. These peaks are directly related to the nano-columns topography. The film system used here proved to act as a physical method for producing layer-by-layer structure for obtaining enhanced hydrophobic surfaces rather than the usual chemical methods reported in the literature. In addition, the GCZSSTF also acted as good as reported results for nano-tubes when applied as cathode in the field ionization gas sensing setup.
Anodic Aluminum Oxide Templates for Nano wires Array Fabrication
International Nuclear Information System (INIS)
Nur Ubaidah Saidin; Kok, K.Y.; Ng, I.K.
2011-01-01
This paper reports on the process developed to fabricate anodic aluminium oxide (AAO) templates suitable for the fabrication of nano wire arrays. Anodization process has been used to fabricate the AAO templates with pore diameters ranging from 15 nm to 30 nm. Electrodeposition of parallel arrays of high aspect ratio nickel nano wires were demonstrated using these fabricated AAO templates. The nano wires produced were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM). It was found that the orientations of the electrodeposited nickel nano wires were governed by the deposition current and electrolyte conditions. (author)
Influence of grain size on lithium storage performance of germanium oxide films
International Nuclear Information System (INIS)
Feng, J.K.; Lai, M.O.; Lu, L.
2012-01-01
Highlights: ► We deposited GeO 2 thin films at different temperatures to form different grain sizes. ► Li storage of GeO 2 as anode was studied, which shows that the GeO 2 with grain size of about 10 nm reveals high capacity retention. ► Nanograined GeO 2 also shows better rate capability and cyclability. - Abstract: Germanium oxide (GeO 2 ) films with two different grain sizes of 10 nm (GeO 2 (10 nm)) and 100 nm (GeO 2 (100 nm)) were grown via reactive radio frequency sputtering at different temperatures. Electrochemical measurements of the GeO 2 (10 nm) thin film used as an anode in Li ion rechargeable batteries show superior capacity retention and rate capability compared to those of GeO 2 (100 nm). The GeO 2 (10 nm) thin film possesses an initial capacity of 930 mAh g −1 with 89% capacity retention after 100 cycles, compared with 455 mAh g −1 with 53% of GeO 2 (100 nm) and 225 mAh g −1 , 30% (10 cycles) of common macro-size GeO 2 . Microstructural studies reveal that the GeO 2 (10 nm) thin film can better accommodate volume changes during Li–Ge alloying and de-alloying processes.
Energy Technology Data Exchange (ETDEWEB)
Senff-Wollenberg, Ralf [Baumgarte Boiler Systems GmbH, Bielefeld (Germany). Technik; Ansey, Johann-Wilhelm [Baumgarte Boiler Systems GmbH, Bielefeld (Germany). Forschung und Entwicklung; Reinmoeller, Frank [Baumgarte Boiler Systems GmbH, Bielefeld (Germany)
2013-03-01
The ecologic and energetic demands on modern plants fort he thermal utilization of waste materials increase continuously. Beside low costs of investment, enhanced efficiencies, an enhanced availability, long journey times as well as low costs of operation and maintenance are important factors for the investment decision. The primary and secondary measures for the shrinkage of corrosion are decisive for achieving the factors for the decision of investment and maintenance. The authors of the contribution under consideration report on long-term experiences on the thick film nickel plating. Especially, the process of galvanic nickel plating, the fields of application as well as the operational experiences are described.
Study of high mobility carriers in Ni-doped CdO films
Indian Academy of Sciences (India)
Cadmium oxide (CdO) doped with different amounts of nickel ion thin films have been prepared on silicon and glass .... glass substrate have [111] energetically preferred orientation growth, which is ... Bragg angle of the considered (111) reflection. ... boundaries. .... (figure 3), which means that the grain or crystallite bound-.
Heteroepitaxial Growth of Vacuum-Evaporated Si-Ge Films on Nano structured Silicon Substrates
International Nuclear Information System (INIS)
Ayu Wazira Azhari; Ayu Wazira Azhari; Kamaruzzaman Sopian; Saleem Hussain Zaidi
2015-01-01
In this study, a low-cost vacuum-evaporated technique is used in the heteroepitaxial growth of Si-Ge films. Three different surface variations are employed: for example polished Si, Si micro pyramids and Si nano pillars profiles. A simple metal-assisted chemical etching method is used to fabricate the Si nano pillars, with Ag acting as a catalyst. Following deposition, substrates are subjected to post-deposition thermal annealing at 1000 degree Celsius to improve the crystallinity of the Ge layer. Optical and morphological studies of surface area are conducted using field emission scanning electron microscopy (FE-SEM), Energy Dispersive X-ray (EDX), Raman spectroscopy and infrared spectroscopy. From the infrared spectroscopy analysis, the energy bandgap for Si-Ge films is estimated to be around 0.94 eV. This high-quality Si-Ge film is most favourable for optics, optoelectronics and high-efficiency solar cell applications. (author)
Energy Technology Data Exchange (ETDEWEB)
Tientong, J. [University of North Texas, Department of Chemistry, 1155 Union Circle #305070, Denton, TX 76203 (United States); Ahmad, Y.H. [Center for Advanced Materials, P.O. Box 2713, Qatar University, Doha (Qatar); Nar, M.; D' Souza, N. [University of North Texas, Department of Mechanical and Energy Engineering, Denton, TX 76207 (United States); Mohamed, A.M.A. [Center for Advanced Materials, P.O. Box 2713, Qatar University, Doha (Qatar); Golden, T.D., E-mail: tgolden@unt.edu [University of North Texas, Department of Chemistry, 1155 Union Circle #305070, Denton, TX 76203 (United States)
2014-05-01
Layered silicates as exfoliated montmorillonite are incorporated into nickel films by electrodeposition, enhancing both corrosion resistance and hardness. Films were deposited onto stainless steel from a plating solution adjusted to pH 9 containing nickel sulfate, sodium citrate, and various concentrations of exfoliated montmorillonite. The presence of the incorporated layered silicate was confirmed by scanning electron microscopy and energy-dispersive X-ray spectroscopy. The composite films were also compact and smooth like the pure nickel films deposited under the same conditions as shown by scanning electron microscopy. X-ray diffraction results showed that incorporation of layered silicates into the film do not affect the nickel crystalline fcc structure. The nanocomposite films exhibited improved stability and adhesion. Pure nickel films cracked and peeled from the substrate when immersed in 3.5% NaCl solution within 5 days, while the nanocomposite films remained attached even after 25 days. The corrosion resistance of the nickel nanocomposites was also improved compared to nickel films. Nickel-layered silicate composites showed a 25% increase in Young's modulus and a 20% increase in hardness over pure nickel films. - Highlights: • 0.05–2% of layered silicates are incorporated into crystalline nickel films. • Resulting composite films had improved stability and adhesion. • Corrosion resistance improved for the composite films. • Hardness improved 20% and young's modulus improved 25% for the composite films.
International Nuclear Information System (INIS)
Saario, T.; Laitinen, T.; Maekelae, K.; Bojinov, M.; Betova, I.
1998-07-01
The construction materials used in coolant systems in nuclear power plants become covered with oxide films as a result of exposure to the aqueous environment. The susceptibility of the materials to different forms of corrosion, as well as the extent of the incorporation of radioactive species on the surfaces of the primary circuit, are greatly influenced by the physical and chemical properties of these oxide films. The composition and characteristics of the oxide films in turn depend on the applied water chemistry. This work was undertaken in order to collect and evaluate the present views on the structure and behaviour of oxide films formed on iron- and nickel-based materials in aqueous environments. This survey should serve to recognise the areas in which more understanding and research effort is needed. The review begins with a discussion on the bulk oxides of iron, nickel and chromium, as well as their mixed oxides. In addition to bulk oxides, the structure and properties of oxide films forming on pure iron, nickel and chromium and on iron- and nickel-based engineering alloys are considered. General approaches to model the structure and growth of oxide films on metals are discussed in detail. The specific features of the oxide structures, properties and growth at high temperatures are presented with special focus on the relevance of existing models. Finally, the role of oxide films in localised corrosion, oxide breakdown, pitting, stress corrosion cracking and related phenomena is considered. The films formed on the surfaces of iron- and nickel-based alloys in high-temperature aqueous environments generally comprise two layers, i.e. the so-called duplex structure. The inner part is normally enriched in chromium and has a more dense structure, while the outer part is enriched in iron and has a cracked or porous structure. The information collected clearly indicates the effect of the chemical environment on the properties of oxide films growing on metal surfaces
2017-01-01
Pb(Zr0.52Ti0.48)O3 (PZT) films with (001) orientation were deposited on Pt(111)/Ti/SiO2/Si(100) substrates using pulsed laser deposition. Variation of the laser pulse rate during the deposition of the PZT films was found to play a key role in the control of the microstructure and to change strongly the piezoelectric response of the thin film. The film deposited at low pulse rate has a denser columnar microstructure, which improves the transverse piezoelectric coefficient (d31f) and ferroelectric remanent polarization (Pr), whereas the less densely packed columnar grains in the film deposited at high pulse rates give rise to a significantly higher longitudinal piezoelectric coefficient (d33f) value. The effect of film thickness on the ferroelectric and piezoelectric properties of the PZT films was also investigated. With increasing film thickness, the grain column diameter gradually increases, and also the average Pr and d33f values become larger. The largest piezoelectric coefficient of d33f = 408 pm V–1 was found for a 4-μm film thickness. From a series of films in the thickness range 0.5–5 μm, the z-position dependence of the piezoelectric coefficient could be deduced. A local maximum value of 600 pm V–1 was deduced in the 3.5–4.5 μm section of the thickest films. The dependence of the film properties on film thickness is attributed to the decreasing effect of the clamping constraint imposed by the substrate and the increasing spatial separation between the grains with increasing film thickness. PMID:28247756
Catalytic performance and characterization of cobalt-nickel nano catalysts for CO hydrogenation
International Nuclear Information System (INIS)
Feyzi, Mostafa; Gholivand, Mohammad Bagher; Babakhanian, Arash
2014-01-01
A series of Co-Ni nano catalysts were prepared by co-precipitation method. We investigated the effect of Co/Ni molar ratios precipitate and calcination conditions on the catalytic performance of cobalt nickel catalysts for Fisher-Tropsch synthesis (FTS). The catalyst containing 90%Co/10%Ni was found to be optimal for the conversion of synthesis gas to light olefins. The activity and selectivity of the optimal catalyst were studied in different operational conditions. The results show that the best operational conditions are the H 2 /CO=2/1 molar feed ratio at 310 .deg. C and GHSV=1,200 h - 1 under 5 bar of pressure. The prepared catalysts were characterized by powder X-ray diffraction (XRD), N 2 adsorption-desorption measurements such as BET and BJH methods, transmission electron microscopy (TEM) and thermal gravimetric analysis (TGA)
Atomic-Layer-Deposition of Indium Oxide Nano-films for Thin-Film Transistors.
Ma, Qian; Zheng, He-Mei; Shao, Yan; Zhu, Bao; Liu, Wen-Jun; Ding, Shi-Jin; Zhang, David Wei
2018-01-09
Atomic-layer-deposition (ALD) of In 2 O 3 nano-films has been investigated using cyclopentadienyl indium (InCp) and hydrogen peroxide (H 2 O 2 ) as precursors. The In 2 O 3 films can be deposited preferentially at relatively low temperatures of 160-200 °C, exhibiting a stable growth rate of 1.4-1.5 Å/cycle. The surface roughness of the deposited film increases gradually with deposition temperature, which is attributed to the enhanced crystallization of the film at a higher deposition temperature. As the deposition temperature increases from 150 to 200 °C, the optical band gap (E g ) of the deposited film rises from 3.42 to 3.75 eV. In addition, with the increase of deposition temperature, the atomic ratio of In to O in the as-deposited film gradually shifts towards that in the stoichiometric In 2 O 3 , and the carbon content also reduces by degrees. For 200 °C deposition temperature, the deposited film exhibits an In:O ratio of 1:1.36 and no carbon incorporation. Further, high-performance In 2 O 3 thin-film transistors with an Al 2 O 3 gate dielectric were achieved by post-annealing in air at 300 °C for appropriate time, demonstrating a field-effect mobility of 7.8 cm 2 /V⋅s, a subthreshold swing of 0.32 V/dec, and an on/off current ratio of 10 7 . This was ascribed to passivation of oxygen vacancies in the device channel.
Enhanced ductility of surface nano-crystallized materials by modulating grain size gradient
International Nuclear Information System (INIS)
Li, Jianjun; Soh, A K
2012-01-01
Surface nano-crystallized (SNC) materials with a graded grain size distribution on their surfaces have been attracting increasing scientific interest over the past few decades due to their good synergy of high strength and high ductility. However, to date most of the existing studies have focused on the individual contribution of three different aspects, i.e. grain size gradient (GSG), work-hardened region and surface compressive residual stresses, which were induced by surface severe plastic deformation processes, to the improved strength of SNC materials as compared with that of their coarse grained (CG) counterparts. And the ductility of these materials has hardly been studied. In this study, a combination of theoretical analysis and finite element simulations was used to investigate the role of GSG in tuning the ductility of SNC materials. It was found that the ductility of an SNC material can be comparable to that of its CG counterpart, while it simultaneously possessed a much higher strength than its CG core if the optimal GSG thickness and grain size of the topmost phase were adopted. A design map that can be used as a guideline for fabrication of SNC materials was also plotted. Our predictions were also compared with the corresponding experimental results. (paper)
International Nuclear Information System (INIS)
Santhosh, Ch.; Saranya, M.; Ramachandran, R.; Felix, S.; Velmurugan, V.; Grace, A.N.
2014-01-01
A highly sensitive and selective Cr(VI) sensor with graphene-based nano composites film as an enhanced sensing platform is reported. The detection of chromium species is a challenging task because of the different possible oxidation states in which the element can occur. The sensing film was developed by homogeneously distributing Au nanoparticles (AuNPs) onto the two-dimensional (2D) graphene nano sheet matrix by electrochemical method. Such nano structured composite film platforms combine the advantages of AuNPs and graph ene nano sheets because of the synergistic effect between them. This effect greatly facilitates the electron-transfer processes and the sensing behavior for Cr(VI) detection, leading to a remarkably improved sensitivity and selectivity. The interference from other heavy metal ions is studied in detail. Such sensing elements are very promising for practical environmental monitoring applications.
Rapid nano impact printing of silk biopolymer thin films
White, Robert D.; Gray, Caprice; Mandelup, Ethan; Amsden, Jason J.; Kaplan, David L.; Omenetto, Fiorenzo G.
2011-11-01
In this paper, nano impact printing of silk biopolymer films is described. An indenter is rapidly accelerated and transfers the nanopattern from a silicon master into the silk film during an impact event that occurs in less than 1 ms. Contact stresses of greater than 100 MPa can be achieved during the short impact period with low power and inexpensive hardware. Ring shaped features with a diameter of 2 µm and a ring width of 100-200 nm were successfully transferred into untreated silk films using this method at room temperature. Mechanical modeling was carried out to determine the contact stress distribution, and demonstrates that imprinting can occur for contact stresses of less than 2 MPa. Thermal characterization at the impact location shows that raising the temperature to 70 °C has only a limited effect on pattern transfer. Contact stresses of greater than approximately 100 MPa result in excessive deformation of the film and poor pattern transfer.
Rapid nano impact printing of silk biopolymer thin films
International Nuclear Information System (INIS)
White, Robert D; Gray, Caprice; Mandelup, Ethan; Amsden, Jason J; Kaplan, David L; Omenetto, Fiorenzo G
2011-01-01
In this paper, nano impact printing of silk biopolymer films is described. An indenter is rapidly accelerated and transfers the nanopattern from a silicon master into the silk film during an impact event that occurs in less than 1 ms. Contact stresses of greater than 100 MPa can be achieved during the short impact period with low power and inexpensive hardware. Ring shaped features with a diameter of 2 µm and a ring width of 100–200 nm were successfully transferred into untreated silk films using this method at room temperature. Mechanical modeling was carried out to determine the contact stress distribution, and demonstrates that imprinting can occur for contact stresses of less than 2 MPa. Thermal characterization at the impact location shows that raising the temperature to 70 °C has only a limited effect on pattern transfer. Contact stresses of greater than approximately 100 MPa result in excessive deformation of the film and poor pattern transfer.
Energy Technology Data Exchange (ETDEWEB)
Genduso, G. [Dipartimento di Ingegneria Chimica, Gestionale, Informatica, Meccanica, Università di Palermo, Viale delle Scienze, 90100 Palermo (Italy); Institut for Heterogeneous Material Systems, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, Hahn-Meitner-Platz 1, D-14109 Berlin (Germany); Inguanta, R.; Sunseri, C.; Piazza, S. [Dipartimento di Ingegneria Chimica, Gestionale, Informatica, Meccanica, Università di Palermo, Viale delle Scienze, 90100 Palermo (Italy); Kelch, C.; Sáez-Araoz, R. [Institut for Heterogeneous Material Systems, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, Hahn-Meitner-Platz 1, D-14109 Berlin (Germany); Zykov, A. [Institut for Heterogeneous Material Systems, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, Hahn-Meitner-Platz 1, D-14109 Berlin (Germany); present address: Institut für Physik, Humboldt-Universität zu Berlin, Newtonstr. 15,12489 Berlin (Germany); Fischer, Ch.-H., E-mail: fischer@helmholtz-berlin.de [Institut for Heterogeneous Material Systems, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, Hahn-Meitner-Platz 1, D-14109 Berlin (Germany); second affiliation: Free University Berlin, Chemistry Institute, Takustr. 3, D-14195 Berlin (Germany)
2013-12-02
Very thin and uniform layers of indium sulfide were deposited on nickel nano-rods using the sequential and cyclical Spray-ILGAR® (Ion Layer Gas Reaction) technique. Substrates were fabricated by electrodeposition of Ni within the pores of polycarbonate membranes and subsequent chemical dissolution of the template. With respect to the depositions on flat substrates, experimental conditions were modified and optimized for the present geometry. Our results show that nano-rods up to a length of 10 μm were covered uniformly along their full length and with an almost constant film growth rate, thus allowing a good control of the coating thickness; the effect of the deposition temperature was also investigated. However, for high numbers of process steps, i.e. thickness, the films became uneven and crusty, especially at higher temperature, mainly owing to the simultaneous side reaction of the metallic Ni forming nickel sulfide at the surface of the rods. However, such a problem occurs only in the case of reactive nano-rod materials, such as less noble metals. It could be strongly reduced by doubling the spray step duration and thereby sealing the metallic surface before the process step of the sulfurization. Thus, quite smooth, about 100 nm thick coatings could be obtained. - Highlights: • Ni nano-rod substrates were grown within polycarbonate membranes. • We can coat nano-rods uniformly by the Ion Layer Gas Reaction method. • As a model we deposited up to about 100 nm In{sub 2}S{sub 3} on Ni nanorods (250 nm × 10 μm). • Element mapping at insulated rods showed homogenous coating over the full length. • Parameter optimization reduced effectively the Ni sulfide formation.
Compostability assessment of nano-reinforced poly(lactic acid) films.
Balaguer, M P; Aliaga, C; Fito, C; Hortal, M
2016-02-01
Nanomaterials can provide plastics with great advantages on mechanical and active properties (i.e. release and capture of specific substances). Therefore, packaging is expected to become one of the leading applications for these substances by 2020. There are some applications already in the market. Nevertheless, there is still some areas under development. A key issue to be analyzed is the end-of-life of these materials once they become waste, and specifically when nanomaterials are used in biodegradable products. The present study evaluated the disintegration, biodegradability, and ecotoxicity of poly(lactic acid) films reinforced with the three following nanomaterials: (1) montmorillonite modified with an ammonium quaternary salt, (2) calcium carbonate and (3) silicon dioxide. Results on disintegration showed that films completely disintegrated into visually indistinguishable residues after 6-7weeks of incubation in composting environment. Moreover, no differences were observed in the evolution of the bioresidue with respect to color, aspect, and odor in comparison with the control. It was also observed that nanomaterials did not significantly reduce the level of biodegradability of PLA (p>0.05). In fact, biodegradation was higher, without finding significant differences (p>0.05), in all the nano-reinforced samples with respect to PLA after 130days in composting (9.4% in PLA+Nano-SiO2; 34.0% in PLA+Clay1; 48.0% in PLA+Nano-CaCO3). Finally, no significant differences (p>0.05) in ecotoxicity in plants were observed as a result of the incorporation of nanoparticles in the PLA matrix. Copyright © 2015 Elsevier Ltd. All rights reserved.
Application of anodizing as a pre-treatment for nickel plating on aluminum
International Nuclear Information System (INIS)
Mehmood, M.; Ahmad, J.; Aslam, M.; Iqbal, M.; Akhtar, J.I.
2003-01-01
Effect of anodizing on subsequent electroplating of nickel on aluminum was investigated. Electroplated nickel did not exhibit any adhesion with un-anodized aluminum. Formation of a very thin anodized alumina film prior to nickel plating led to an excellent adhesion between the nickel film and the substrate. If the thickness of the alumina film increased, adhesion of electroplated nickel was significantly deteriorated and became similar to that of un-anodized bare aluminum. The study revealed that deposition proceeded through pores and defects in the insulator alumina film. These pores and defects also acted as nucleation and anchor points for nickel deposit. There was larger number of nucleation/ anchor points on thin alumina films. This provided better adhesion of nickel with the substrate as well as excellent coverage in relatively shorter times. On the other hand, very rough and poorly adherent nickel deposits formed on thick anodized films. Therefore, it may be used as precursor for producing nickel powder with controlled particle size as well as a catalyst with high specific surface area for hydrogenation and dehydrogenation reactions. (author)
International Nuclear Information System (INIS)
Tamura, N.; Valek, B.C.; Spolenak, R.; MacDowell, A.A.; Celestre, R.S.; Padmore, H.A.; Brown, W.L.; Marieb, T.; Bravman, J.C.; Batterman, B.W.; Patel, J.R.
2001-01-01
An X-ray microdiffraction dedicated beamline, combining white and monochromatic beam capabilities, has been built at the Advanced Light Source. The purpose of this beamline is to address the myriad of problems in Materials Science and Physics that require submicron x-ray beams for structural characterization. Many such problems are found in the general area of thin films and nano-materials. For instance, the ability to characterize the orientation and strain state in individual grains of thin films allows us to measure structural changes at a very local level. These microstructural changes are influenced heavily by such parameters as deposition conditions and subsequent treatment. The accurate measurement of strain gradients at the micron and sub-micron level finds many applications ranging from the strain state under nano-indenters to gradients at crack tips. Undoubtedly many other applications will unfold in the future as we gain experience with the capabilities and limitations of this instrument. We have applied this technique to measure grain orientation and residual stress in single grains of pure Al interconnect lines and preliminary results on post-electromigration test experiments are presented. It is shown that measurements with this instrument can be used to resolve the complete stress tensor (6 components) in a submicron volume inside a single grain of Al under a passivation layer with an overall precision of about 20 MPa. The microstructure of passivated lines appears to be complex, with grains divided into identifiable subgrains and noticeable local variations of both tensile/compressive and shear stresses within single grains
Fadhil, Sadeem Abbas; Alrawi, Aoday Hashim; Azeez, Jazeel H.; Hassan, Mohsen A.
2018-04-01
In the present work, a multiscale model is presented and used to modify the Hall-Petch relation for different scales from nano to micro. The modified Hall-Petch relation is derived from a multiscale equation that determines the cohesive energy between the atoms and their neighboring grains. This brings with it a new term that was originally ignored even in the atomistic models. The new term makes it easy to combine all other effects to derive one modified equation for the Hall-Petch relation that works for all scales together, without the need to divide the scales into two scales, each scale with a different equation, as it is usually done in other works. Due to that, applying the new relation does not require a previous knowledge of the grain size distribution. This makes the new derived relation more consistent and easier to be applied for all scales. The new relation is used to fit the data for Copper and Nickel and it is applied well for the whole range of grain sizes from nano to micro scales.
Effect of annealing temperature on physical properties of solution processed nickel oxide thin films
Sahoo, Pooja; Thangavel, R.
2018-05-01
In this report, NiO thin films were prepared at different annealing temperatures from nickel acetate precursor by sol-gel spin coating method. These films were characterized by different analytical techniques to obtain their structural, optical morphological and electrical properties using X-ray diffractometer (XRD), Field emission scanning electron microscopy (FESEM), UV-Vis NIR double beam spectrophotometer and Keithley 2450 source meter respectively. FESEM images clearly indicates the formation of a homogenous and porous films. Due to their porosity, they can be used in sensing applications. The optical absorption spectra elucidated that the films are highly transparent and have a suitable band gap which are in similar agreement with earlier reports. The current enhancement under illumination shows the suitability of nanostructured NiO thin films in its application in photovoltaics.
Development of ecofriendly bionanocomposite: Whey protein isolate/pullulan films with nano-SiO2.
Hassannia-Kolaee, Mahbobeh; Khodaiyan, Faramarz; Pourahmad, Rezvan; Shahabi-Ghahfarrokhi, Iman
2016-05-01
During the past decade, the limitation of petroleum based polymers, the high price of oil, and the environmental concern were attracted the attention of researchers to develop biobased polymers. The composition of different biopolymers and the reinforcement with nano filler are common methods to improve the drawbacks of biopolymers. In this study whey protein isolate/pullulan (WPI/PUL) films contain 1%, 3%, and 5% (w/w) nano-SiO2 (NS) were prepared by a casting method. Tensile strength of nanocomposite films increased after increasing NS content, but elongation at break decreased, simultaneously. Water absorption, moisture content, solubility in water improved in the wake of increasing NS content because NS increase the cohesiveness of the polymer matrix and improved the barrier and water resistance properties of the films. water vapor permeability of film specimens decreased by increasing NS content. Uniform distribution of NS into polymer matrix was confirmed by scanning electron microscopy (SEM). XRD pattern and thermal analysis revealed increasing crystallinity and increasing Tg of film specimens with increasing NS content, respectively. According to our result WPI/PUL/NS films possess potential to be used as environment friendly packaging films to improve shelf life of food and can be used as promising alternative to petroleum based packaging films. Copyright © 2016 Elsevier B.V. All rights reserved.
Growth temperature dependence of flux pinning properties in ErBa2Cu3Oy thin films with nano-rods
International Nuclear Information System (INIS)
Haruta, M.; Sueyoshi, T.; Fujiyoshi, T.; Mukaida, M.; Kai, H.; Matsumoto, K.; Mele, P.; Maeda, T.; Horii, S.
2011-01-01
Nano-rods were introduced into ErBa 2 Cu 3 O y thin films to improve J c . Pinning properties depended on the growth temperature of the films. Morphology of nano-rods was affected by the growth temperature. The growth temperature is important to achieve high in-field J c 's. Irreversibility lines and distributions of local critical current density (J cl ) based on the percolation transition model were affected by the growth temperature (T s ) in 3.5 wt.%-BaNb 2 O 6 -doped ErBa 2 Cu 3 O y thin films. The vortex-Bose-glass-like state appeared by the introduction of nano-rods, and this vortex state was affected by T s . The shape and width of the J cl distribution strongly depended on T s . These results are probably caused by variations of the density and the growth direction for nano-rods reflecting T s . The growth temperature is an important factor to achieve higher critical current properties under magnetic fields for coated conductors of rare-earth-based cuprates with nano-rods.
Sun, Ke; Saadi, Fadl H.; Lichterman, Michael F.; Hale, William G.; Wang, Hsinping; Zhou, Xinghao; Plymale, Noah T.; Omelchenko, Stefan T.; He, Jr-Hau; Papadantonakis, Kimberly M.; Brunschwig, Bruce S.; Lewis, Nathan S.
2015-01-01
Reactively sputtered nickel oxide (NiOx) films provide transparent, antireflective, electrically conductive, chemically stable coatings that also are highly active electrocatalysts for the oxidation of water to O2(g). These NiOx coatings provide
Nano indentation of particulate and polymer films
International Nuclear Information System (INIS)
Akram, Aisha
2001-01-01
A detailed knowledge of the formation and rupture mechanisms of agglomerates is essential when seeking to model equipment designed to produce and process such agglomerated particulate solids. In the work to be described the nano-indentation of two-dimensional agglomerate films was carried out in order to establish a means of identifying the generic breakage mechanisms of agglomerated systems. Data analysis techniques are developed that enable the individual inter-particle junction strengths to be calculated for a model system consisting of rather mono-dispersed colloidal silica particles (20-24 nm diameter) bound with a poly(methyl methacrylate). Applied load and penetration depth data in the range (10 mN and 500 nm respectively) are provided as a function of loading time during a continuous loading. It is argued that these data enable the sequence of the discrete binder bridge failures to be observed thus giving a quantitative indication of the breakage mechanism of this agglomerate system as well as reflect the agglomerate structure. The secondary objective of this work was to produce a range of agglomerates with different mechanical properties, without changing the type and amount of binder or prime particles used in the system. This was achieved by altering the mechanical properties of the binder, poly(methyl methacrylate), by the use of a variety of solvents. From data obtained using nano-indentation on thin films of the treated polymer, brittle and ductile forms of poly(methyl methacrylate) could be distinguished. These trends are reflected, to some degree, in the mechanical response of the agglomerated layers. (author)
Improvement of thermal stability of nano-granular TMR films by using a Mg-Al-O insulator matrix
Kanie, S.; Koyama, S.
2018-05-01
A new metal-insulator nano-granular tunneling magnetoresistance (TMR) film made of (Fe-Co)-(Mg-Al-O) has been investigated. It is confirmed that the film has granular structure in which crystal Fe-Co granules are surrounded by an amorphous Mg-Al-O matrix. A large MR ratio of 11.8 % at room temperature is observed for a 42 vol.%(Fe0.6Co0.4)-(Mg-Al-O) film annealed at 395 °C. The electrical resistivity increases rapidly by annealing at above the changing point (500 °C). The changing point is about 300 °C higher than that of conventional (Fe-Co)-(Mg-F) nano-granular TMR films. The 42 vol.%(Fe0.6Co0.4)-(Mg-Al-O) film also exhibits less degradation in the MR ratio at high annealing temperatures such as 600 °C. These results suggest the (Fe-Co)-(Mg-Al-O) film is superior to the (Fe-Co)-(Mg-F) film in thermal stability.
Directory of Open Access Journals (Sweden)
Han Li
2017-12-01
Full Text Available Thermoelectric semiconductors based on CoSb3 hold the best promise for recovering industrial or automotive waste heat because of their high efficiency and relatively abundant, lead-free constituent elements. However, higher efficiency is needed before thermoelectrics reach economic viability for widespread use. In this study, n-type InxCeyCo4Sb12+z skutterudites with high thermoelectric performance are produced by combining several phonon scattering mechanisms in a panoscopic synthesis. Using melt spinning followed by spark plasma sintering (MS-SPS, bulk InxCeyCo4Sb12+z alloys are formed with grain boundaries decorated with nano-phase of InSb. The skutterudite matrix has grains on a scale of 100–200 nm and the InSb nano-phase with a typical size of 5–15 nm is evenly dispersed at the grain boundaries of the skutterudite matrix. Coupled with the presence of defects on the Sb sublattice, this multi-scale nanometer structure is exceptionally effective in scattering phonons and, therefore, InxCeyCo4Sb12/InSb nano-composites have very low lattice thermal conductivity and high zT values reaching in excess of 1.5 at 800 K.
Nano-crystalline Ag–PbTe thermoelectric thin films by a multi-target PLD system
Energy Technology Data Exchange (ETDEWEB)
Cappelli, E., E-mail: emilia.cappelli@ism.cnr.it [CNR-ISM, Montelibretti, Via Salaria Km 29.3, P.O.B. 10, 00016 Rome (Italy); Bellucci, A. [CNR-ISM, Montelibretti, Via Salaria Km 29.3, P.O.B. 10, 00016 Rome (Italy); Dip. Fisica, Un. Roma Sapienza, Piazzale Aldo Moro 2, 00185 Rome (Italy); Medici, L. [CNR-IMAA, Tito Scalo, 85050 Potenza (Italy); Mezzi, A.; Kaciulis, S. [CNR-ISMN, Montelibretti, Via Salaria Km 29.3, P.O.B. 10, 00016 Rome (Italy); Fumagalli, F.; Di Fonzo, F. [Center Nano Science Technology @Polimi, I.I.T., Via Pascoli 70/3, 20133 Milano (Italy); Trucchi, D.M. [CNR-ISM, Montelibretti, Via Salaria Km 29.3, P.O.B. 10, 00016 Rome (Italy)
2015-05-01
Highlights: • Thermoelectric PbTe thin films, with increasing Ag percentage, were deposited by PLD. • Almost stoichiometric PbTe (Ag doped) films were grown, as verified by XPS analysis. • GI-XRD established the formation of cubic PbTe, with nano-metric structure (∼35 nm). • Surface resistivity shows an increase in conductivity, with increasing Ag doping. • From Seebeck values and XPS depth analysis, 10% Ag seems to be the solubility limit. - Abstract: It has been evaluated the ability of ArF pulsed laser ablation to grow nano-crystalline thin films of high temperature PbTe thermoelectric material, and to obtain a uniform and controlled Ag blending, through the entire thickness of the film, using a multi-target system in vacuum. The substrate used was a mirror polished technical alumina slab. The increasing atomic percentage of Ag effect on physical–chemical and electronic properties was evaluated in the range 300–575 K. The stoichiometry and the distribution of the Ag component, over the whole thickness of the samples deposited, have been studied by XPS (X-ray photoelectron spectroscopy) and corresponding depth profiles. The crystallographic structure of the film was analyzed by grazing incidence X-ray diffraction (GI-XRD) system. Scherrer analysis for crystallite size shows the presence of nano-structures, of the order of 30–35 nm. Electrical resistivity of the samples, studied by the four point probe method, as a function of increasing Ag content, shows a typical semi-conductor behavior. From conductivity values, carrier concentration and Seebeck parameter determination, the power factor of deposited films was calculated. Both XPS, Hall mobility and Seebeck analysis seem to indicate a limit value to the Ag solubility of the order of 5%, for thin films of ∼200 nm thickness, deposited at 350 °C. These data resulted to be comparable to theoretical evaluation for thin films but order of magnitude lower than the corresponding bulk materials.
International Nuclear Information System (INIS)
Min, Shudi; Zhao, Chongjun; Chen, Guorong; Qian, Xiuzhen
2014-01-01
Reduced graphene oxide (RGO) on nickel hydroxide (Ni(OH) 2 ) film was synthesized via a green and facile hydrothermal approach. In this process, graphene oxide (GO) was reduced by nickel foam (NF) while the nickel metal was oxidized to Ni(OH) 2 film simultaneously, which resulted in RGO on Ni(OH) 2 structure. The RGO/Ni(OH) 2 composite film was characterized using by X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and field-emission scanning electron microscope (FESEM). The electrochemical performances of the supercapacitor with the as-synthesized RGO/Ni(OH) 2 composite films as electrodes were evaluated using cyclic voltammetry (CV), galvanostatic charge–discharge (GCD), electrochemical impedance spectrometry (EIS) in 1 M KOH aqueous solution. Results indicated that the RGO/Ni(OH) 2 /NF composite electrodes exhibited superior capacitive performance with high capability (2500 mF cm −2 at a current density of 5 mA cm −2 , or 1667 F g −1 at 3.3 A g −1 ), compared with pure Ni(OH) 2 /NF (450 mF cm −2 at 5 mA cm −2 , 409 F g −1 at 3.3 A g −1 ) prepared under the identical conditions. Our study highlights the importance of anchoring RGO films on Ni(OH) 2 surface for maximizing the optimized utilization of electrochemically active Ni(OH) 2 and graphene for energy storage application in supercapacitors
Nano-impact testing of TiFeN and TiFeMoN films for dynamic toughness evaluation
Energy Technology Data Exchange (ETDEWEB)
Beake, B D [Micro Materials Ltd, Willow House, Ellice Way, Yale Business Village, Wrexham LL13 7YL (United Kingdom); Vishnyakov, V M; Colligon, J S, E-mail: ben@micromaterials.co.uk [Dalton Research Institute, Manchester Metropolitan University, Manchester M1 5GD (United Kingdom)
2011-03-02
TiFeN and TiFeMoN films were deposited on silicon wafers by ion-beam-assisted deposition. Their mechanical properties were measured by nanoindentation (quasi-static) and nano-impact (dynamic) techniques. Nano-impact testing enabled assessment of their toughness and resistance to fatigue fracture under repetitive loading. At low impact forces, films with a higher resistance to plastic deformation (H{sup 3}/E{sup 2}) were much more resistant to the formation of cracks throughout the test. At higher impact forces, these films initially show impact resistance but with continued impacts they are unable to protect the Si substrate, performing as poorly as films with lower H{sup 3}/E{sup 2} and suffer delamination from the Si substrate over a large area.
International Nuclear Information System (INIS)
Young, G.A. Jr.; Najafabadi, R.; Strohmayer, W.; Baldrey, D.G.; Hamm, B.; Harris, J.; Sticht, J.; Wimmer, E.
2003-01-01
Atomistic modeling methods were employed to investigate the effects of impurity elements on the metallurgy, irradiation embrittlement, and environmentally assisted cracking of nickel-base alloys exposed to nuclear environments. Calculations were performed via ab initio atomistic modeling methods to ensure the accuracy and reliability of the results. A Griffith-type fracture criterion was used to quantitatively assess the effect of elements or element pairs on the grain boundary cohesive strength. In order of most embrittling to most strengthening, the elements are ranked as: He, Li, S, H, C, Zr, P, Fe, Mn, Nb, Cr, and B. Helium is strongly embrittling (-2.04 eV/atom lowering of the Griffith energy), phosphorus has little effect on the grain boundary (0.1 eV/atom), and boron offers appreciable strengthening (1.03 eV/atom increase in the Griffith energy). Calculations for pairs of elements (H-Li, H-B, H-C, H-P, and H-S) show little interaction on the grain boundary cohesive energy, so that for the conditions studied, linear superposition of elemental effects is a good approximation. These calculations help explain metallurgical effects (e.g. why boron can strengthen grain boundaries), irradiation embrittlement (e.g. how boron transmutation results in grain boundary embrittlement), as well as how grain boundary impurity elements can affect environmentally assisted cracking (i.e. low temperature crack propagation and stress corrosion cracking) of nickel-base alloys
Surface, interface and thin film characterization of nano-materials using synchrotron radiation
International Nuclear Information System (INIS)
Kimura, Shigeru; Kobayashi, Keisuke
2005-01-01
From the results of studies in the nanotechnology support project of the Ministry of Education, Culture, Sports, Science and Technology of Japan, several investigations on the surface, interface and thin film characterization of nano-materials are described; (1) the MgB 2 thin film by X-ray diffraction, (2) the magnetism of the Pt thin film on a Co film by X-ray magnetic circular dichroism measurement, (3) the structure and physical properties of oxygen molecules absorbed in a micro hole of the cheleted polymer crystal by the direct observation in X-ray powder diffraction, and (4) the thin film gate insulator with a large dielectric constant, thermally treated HfO 2 /SiO 2 /Si, by X-ray photoelectron spectroscopy. (M.H.)
Nano-sized copper tungstate thin films as positive electrodes for rechargeable Li batteries
International Nuclear Information System (INIS)
Li Chilin; Fu Zhengwen
2008-01-01
Nano-sized CuWO 4 thin films have been fabricated by radio-frequency (R.F.) sputtering deposition, and are used as positive electrode with both LiClO 4 liquid electrolyte and LiPON solid electrolyte in rechargeable lithium batteries. An initial discharge capacity of 192 and 210 mAh/g is obtainable for CuWO 4 film electrode with and without coated LiPON in liquid electrolyte, respectively. An all-solid-state cell with Li/LiPON/CuWO 4 layers shows a high-volume rate capacity of 145 μAh/cm 2 μm in first discharge, and overcomes the unfavorable electrochemical degradation observed in liquid electrolyte system. A two-step reactive mechanism is investigated by both transmission electron microscopy and selected area electron diffraction techniques. Apart from the extrusion and injection of Cu 2+ /Cu 0 , additional capacity can be achieved by the reversible reactivity of (WO 4 ) 2- framework. The chemical diffusion coefficients of Li intercalation/deintercalation are estimated by cyclic voltammetry. Nano-CuWO 4 thin film is expected to be a promising positive electrode material for high-performance rechargeable thin-film lithium batteries
Sankar, M. S. Ravi; Gangineni, R. B.
2018-04-01
This work aims at understanding the solvent influence upon the throughput and structure of poly vinyledene fluoride (PVDF)nano-patterned films. The PVDF thin films are deposited by spin coating method using Dimethylsulfoxide (DMSO), Tetrahydrofuran (THF) and 2-butanone solvents. The nano-patterns are realized by imprinting SONY 700 MB CD aluminum constructions on PVDF thin filmsusing imprint lithography technique under ambient annealing temperature and pressure. Surface morphology &imprint pattern transfer quality is evaluated with Atomic force microscopy (AFM). Raman spectroscopy is used for evaluating the structural evolutions with respect to solvent & patterning.
International Nuclear Information System (INIS)
Jin, In Ju; Lee, Ik Mo; Kwon, Yeung Gu
2006-02-01
This book introduces background of nano science such as summary, plenty room at the bottom, access way to nano technique, nanoparticles using bottom-up method which are a marvel of nature, and modern alchemy : chemical synthesis of artificial nano structure, understanding of quantum mechanics, STM/AFM, nano metal powder, ceramic nanoparticles, nano structure film, manufacture of nanoparticles using reverse micelle method, carbon nano tube, sol-gel material, nano energy material, nano catalyst nano bio material technology and spintronics.
Energy Technology Data Exchange (ETDEWEB)
Muhunthan, N.; Singh, Om Pal [Compound Semiconductor Solar Cell, Physics of Energy Harvesting Division, New Delhi 110012 (India); Toutam, Vijaykumar, E-mail: toutamvk@nplindia.org [Quantum Phenomena and Applications Division, CSIR-National Physical Laboratory, Dr. K.S. Krishnan Marg, New Delhi 110012 (India); Singh, V.N., E-mail: singhvn@nplindia.org [Compound Semiconductor Solar Cell, Physics of Energy Harvesting Division, New Delhi 110012 (India)
2015-10-15
Graphical abstract: Experimental setup for conducting AFM (C-AFM). - Highlights: • Cu{sub 2}ZnSnS{sub 4} (CZTS) thin film was grown by reactive co-sputtering. • The electronic properties were probed using conducting atomic force microscope, scanning Kelvin probe microscopy and scanning capacitance microscopy. • C-AFM current flow mainly through grain boundaries rather than grain interiors. • SKPM indicated higher potential along the GBs compared to grain interiors. • The SCM explains that charge separation takes place at the interface of grain and grain boundary. - Abstract: Electrical characterization of grain boundaries (GB) of Cu-deficient CZTS (Copper Zinc Tin Sulfide) thin films was done using atomic force microscopic (AFM) techniques like Conductive atomic force microscopy (CAFM), Kelvin probe force microscopy (KPFM) and scanning capacitance microscopy (SCM). Absorbance spectroscopy was done for optical band gap calculations and Raman, XRD and EDS for structural and compositional characterization. Hall measurements were done for estimation of carrier mobility. CAFM and KPFM measurements showed that the currents flow mainly through grain boundaries (GB) rather than grain interiors. SCM results showed that charge separation mainly occurs at the interface of grain and grain boundaries and not all along the grain boundaries.
International Nuclear Information System (INIS)
Winter, Shoshana; Zenou, Michael; Kotler, Zvi
2016-01-01
We present a study of the morphology and electrical properties of copper structures which are printed by laser induced forward transfer from bulk copper. The percentage of voids and the oxidation levels are too low to account for the high resistivities (∼4 to 14 times the resistivity of bulk monocrystalline copper) of these structures. Transmission electron microscope (TEM) images of slices cut from the printed areas using a focused ion beam (FIB) show nano-sized crystal structures with grain sizes that are smaller than the electron free path length. Scattering from such grain boundaries causes a significant increase in the resistivity and can explain the measured resistivities of the structures. The TEM images also show a nano-amorphous layer (∼5 nm) at the droplet boundaries which also contributes to the overall resistivity. Such morphological characteristics are best explained by the ultrafast cooling rate of the molten copper droplets during printing. (paper)
Energy Technology Data Exchange (ETDEWEB)
Surmeneva, Maria A. [Department of Theoretical and Experimental Physics, National Research Tomsk Polytechnic University, Tomsk 634050 (Russian Federation); Surmenev, Roman A., E-mail: rsurmenev@gmail.com [Department of Theoretical and Experimental Physics, National Research Tomsk Polytechnic University, Tomsk 634050 (Russian Federation); Fraunhofer Institute for Interfacial Engineering and Biotechnology IGB, 70569 Stuttgart (Germany); Nikonova, Yulia A.; Selezneva, Irina I. [Institute of Theoretical and Experimental Biophysics, Russian Academy of Sciences, Pushchino 142292 (Russian Federation); Ivanova, Anna A. [Department of Theoretical and Experimental Physics, National Research Tomsk Polytechnic University, Tomsk 634050 (Russian Federation); Putlyaev, Valery I. [Department of Chemistry, Moscow State University, Vorobievi Gory, 1, Moscow 119991 (Russian Federation); Prymak, Oleg; Epple, Matthias [Inorganic Chemistry and Center for Nanointegration Duisburg-Essen (CeNIDE), University of Duisburg-Essen, 45117 Essen (Germany)
2014-10-30
Highlights: • Growth of a columnar grain structure perpendicular to the substrate surface was observed. • Interplanar spacing distances measured using HRTEM were 0.82 and 0.28 nm, corresponding to the (0 0 1) and (2 1 1) lattice planes of hexagonal HA. • Grain size and crystallinity increased when increasing the deposition time. • Nanometer-thick low-crystallinity HA coatings with different thicknesses stimulated cells to attach, proliferate and form mineralized nodules. - Abstract: A series of nanostructured low-crystalline hydroxyapatite (HA) coatings averaging 170, 250, and 440 nm in thickness were deposited onto previously etched titanium substrates through radio-frequency (RF) magnetron sputtering. The HA coatings were analyzed using infrared spectroscopy (FTIR), X-ray diffraction (XRD), and scanning and transmission electron microscopy (SEM and TEM). Cross sections of the thin specimens were prepared by FIB to study the microstructure of the coatings by TEM. The deposition process formed nano-scale grains, generating an amorphous layer at the substrate/coating interface and inducing the growth of a columnar grain structure perpendicular to the substrate surface. A microstructural analysis of the film confirmed that the grain size and crystallinity increased when increasing the deposition time. The nanostructured HA coatings were not cytotoxic, as proven by in vitro assays using primary dental pulp stem cells and mouse fibroblast NCTC clone L929 cells. Low-crystallinity HA coatings with different thicknesses stimulated cells to attach, proliferate and form mineralized nodules on the surface better than uncoated titanium substrates.
Energy Technology Data Exchange (ETDEWEB)
Wu, Wen-Jie; He, Wen-Li; Yu, Hong-Yu [Department of Chemistry, Fudan University, 220 Handan Road, Shanghai 200433 (China); Huang, Hong-Xiang [State Key Laboratory of Molecular Engineering of Polymers, Fudan University, 220 Handan Road, Shanghai 200433 (China); Chen, Meng [Department of Chemistry, Fudan University, 220 Handan Road, Shanghai 200433 (China); Qian, Dong-Jin, E-mail: djqian@fudan.edu.cn [Department of Chemistry, Fudan University, 220 Handan Road, Shanghai 200433 (China)
2017-01-15
Luminescent pyrene-functionalized nano-SiO{sub 2} (nano-SiO{sub 2}Pyr) hybrids were synthesized and characterized using thermogravimetry, infrared, UV–vis absorption and, X-ray photoelectron spectroscopy, as well as field emission transmission electron microscopy (FETEM). The organic substituents immobilized on the nano-SiO{sub 2}Pyr hybrids accounted for approximately 10% of the total weight. Polyethylene glycol 200 (PEG200) was found to be the most suitable solvent to suspend the nano-SiO{sub 2}Pyr hybrids compared to other commonly used organic solvents. FETEM images indicated an average SiO{sub 2} nanoparticle diameter of approximately 12 nm and a 1- to 2-nm thick organic species functionalization layer. Several emission peaks were recorded at wavelengths of 380–580 nm and were designated as emissions arising from either the monomer or excimer of the pyrene substituents. Excimer formation was concentration and solvent polarity dependent, with higher concentrations and a stronger solvent polarity benefiting excimer formation. Further, nano-SiO{sub 2}Pyr hybrids were doped in poly(methyl methacrylate) (PMMA) thin films; fluorescence spectra indicated that the excimer could be formed almost exclusively from neighboring nano-SiO{sub 2}Pyr hybrids. Time-resolved fluorescence decays revealed that the emission lifetimes of nano-SiO{sub 2}Pyr monomers and excimers were approximately 190 ns and 65–100 ns in the PEG200 solution, respectively, which was shortened to 0.45 ns to tens of ns in doped PMMA thin films, depending on the nano-hybrid concentration. Thus, the present study not only provides a method to prepare luminescent nano-materials but also a route to investigate excimer formation in solutions and thin films. - Highlights: • Luminescent pyrene-functionalized nano-SiO{sub 2}Pyr hybrids were prepared. • A 1- to 2- nm thick organic functionalization layer on nano-SiO{sub 2} was observed. • Formation of pyrene excimer was concentration and solvent
Goodman, Samuel M.; Noh, Hyunwoo; Singh, Vivek; Cha, Jennifer N.; Nagpal, Prashant
2015-02-01
Quantum dot (QD), or semiconductor nanocrystal, thin films are being explored for making solution-processable devices due to their size- and shape-tunable bandgap and discrete higher energy electronic states. While DNA has been extensively used for the self-assembly of nanocrystals, it has not been investigated for the simultaneous conduction of multiple energy charges or excitons via exciton shelves (ES) formed in QD-DNA nano-bioelectronic thin films. Here, we present studies on charge conduction through exciton shelves, which are formed via chemically coupled QDs and DNA, between electronic states of the QDs and the HOMO-LUMO levels in the complementary DNA nucleobases. While several challenges need to be addressed in optimizing the formation of devices using QD-DNA thin films, a higher charge collection efficiency for hot-carriers and our detailed investigations of charge transport mechanism in these thin films highlight their potential for applications in nano-bioelectronic devices and biological transducers.
Energy Technology Data Exchange (ETDEWEB)
Goodman, Samuel M.; Singh, Vivek [Department of Chemical and Biological Engineering, University of Colorado Boulder, 3415 Colorado Avenue, Boulder, Colorado 80303 (United States); Noh, Hyunwoo [Department of Chemical and Biological Engineering, University of Colorado Boulder, 3415 Colorado Avenue, Boulder, Colorado 80303 (United States); Materials Science and Engineering Program and Department of Nanoengineering, University of California, 9500 Gilman Drive, La Jolla, San Diego, California 92093 (United States); Cha, Jennifer N. [Department of Chemical and Biological Engineering, University of Colorado Boulder, 3415 Colorado Avenue, Boulder, Colorado 80303 (United States); Materials Science and Engineering Program and Department of Nanoengineering, University of California, 9500 Gilman Drive, La Jolla, San Diego, California 92093 (United States); Materials Science and Engineering, University of Colorado Boulder, 3415 Colorado Avenue, Boulder, Colorado 80303 (United States); Nagpal, Prashant, E-mail: pnagpal@colorado.edu [Department of Chemical and Biological Engineering, University of Colorado Boulder, 3415 Colorado Avenue, Boulder, Colorado 80303 (United States); Materials Science and Engineering, University of Colorado Boulder, 3415 Colorado Avenue, Boulder, Colorado 80303 (United States); BioFrontiers Institute, University of Colorado Boulder, 3415 Colorado Avenue, Boulder, Colorado 80303 (United States); Renewable and Sustainable Energy Institute, University of Colorado Boulder, 2445 Kittredge Loop, Boulder, Colorado 80309 (United States)
2015-02-23
Quantum dot (QD), or semiconductor nanocrystal, thin films are being explored for making solution-processable devices due to their size- and shape-tunable bandgap and discrete higher energy electronic states. While DNA has been extensively used for the self-assembly of nanocrystals, it has not been investigated for the simultaneous conduction of multiple energy charges or excitons via exciton shelves (ES) formed in QD-DNA nano-bioelectronic thin films. Here, we present studies on charge conduction through exciton shelves, which are formed via chemically coupled QDs and DNA, between electronic states of the QDs and the HOMO-LUMO levels in the complementary DNA nucleobases. While several challenges need to be addressed in optimizing the formation of devices using QD-DNA thin films, a higher charge collection efficiency for hot-carriers and our detailed investigations of charge transport mechanism in these thin films highlight their potential for applications in nano-bioelectronic devices and biological transducers.
International Nuclear Information System (INIS)
Goodman, Samuel M.; Singh, Vivek; Noh, Hyunwoo; Cha, Jennifer N.; Nagpal, Prashant
2015-01-01
Quantum dot (QD), or semiconductor nanocrystal, thin films are being explored for making solution-processable devices due to their size- and shape-tunable bandgap and discrete higher energy electronic states. While DNA has been extensively used for the self-assembly of nanocrystals, it has not been investigated for the simultaneous conduction of multiple energy charges or excitons via exciton shelves (ES) formed in QD-DNA nano-bioelectronic thin films. Here, we present studies on charge conduction through exciton shelves, which are formed via chemically coupled QDs and DNA, between electronic states of the QDs and the HOMO-LUMO levels in the complementary DNA nucleobases. While several challenges need to be addressed in optimizing the formation of devices using QD-DNA thin films, a higher charge collection efficiency for hot-carriers and our detailed investigations of charge transport mechanism in these thin films highlight their potential for applications in nano-bioelectronic devices and biological transducers
Grain boundaries and mechanical properties of nanocrystalline diamond films.
Energy Technology Data Exchange (ETDEWEB)
Busmann, H.-G.; Pageler, A.; Gruen, D. M.
1999-08-06
Phase-pure nanocrystalline diamond thin films grown from plasmas of a hydrogen-poor carbon argon gas mixture have been analyzed regarding their hardness and elastic moduli by means of a microindentor and a scanning acoustic microscope.The films are superhard and the moduli rival single crystal diamond. In addition, Raman spectroscopy with an excitation wavelength of 1064 nm shows a peak at 1438 l/cm and no peak above 1500 l/cm, and X-ray photoelectron spectroscopy a shake-up loss at 4.2 eV. This gives strong evidence for the existence of solitary double bonds in the films. The hardness and elasticity of the films then are explained by the assumption, that the solitary double bonds interconnect the nanocrystals in the films, leading to an intergrain boundary adhesion of similar strength as the intragrain diamond cohesion. The results are in good agreement with recent simulations of high-energy grain boundaries.
International Nuclear Information System (INIS)
Wang, Hongbin; Wang, Ning; Hang, Tao; Li, Ming
2016-01-01
Highlights: • A 3D porous micro-nano hierarchical structure Cu films were prepared. • The evolution of morphology and wettability with deposition time was reported. • The effects of EDA on the microscopic morphology were revealed. • A high contact angle of 162.1° was measured when deposition time is 5 s. • The mechanism of super-hydrophobicity was illustrated by two classical models. - Abstract: Three-dimensional porous micro-nano hierarchical structure Cu films were prepared by electrochemical deposition with the Hydrogen bubble dynamic template. The morphologies of the deposited films characterized by Scanning Electronic Microscopy (SEM) exhibit a porous micro-nano hierarchical structure, which consists of three levels in different size scales, namely the honeycomb-like microstructure, the dendritic substructure and the nano particles. Besides, the factors which influenced the microscopic morphology were studied, including the deposition time and the additive Ethylene diamine. By measuring the water contact angle, the porous copper films were found to be super-hydrophobic. The maximum of the contact angles could reach as high as 162.1°. An empirical correlation between morphologies and wetting properties was revealed for the first time. The pore diameter increased simultaneously with the deposition time while the contact angle decreased. The mechanism was illustrated by two classical models. Such super-hydrophobic three-dimensional hierarchical micro-nano structure is expected to have practical application in industry.
Energy Technology Data Exchange (ETDEWEB)
Charpin, P; Hauptman, A [Commissariat a l' Energie Atomique, Saclay (France).Centre d' Etudes Nucleaires
1960-07-01
The method employed is based upon the comparison between computed and measured intensities for conveniently selected X-Ray diffraction lines of each component of the powder. Care must be taken to allow for absorption, both inside each grain and in overall sample. This method has been applied to the determination of nickel oxide and fluoride in a nickel powder. (author) [French] La methode utilisee, dite 'absolue' est basee sur le calcul des intensites theoriques de raies de diffraction convenablement choisies. Elle n'est applicable que si l'absorption est negligeable a travers chaque grain constituant l'echantillon et a travers l'echantillon total. Elle a ete employee pour doser, ensemble ou separement, de l'oxyde et du fluorure de nickel dans une poudre de nickel. (auteur)
Thermal behaviour and corrosion resistance of nano-ZnO/polyurethane film
Virgawati, E.; Soegijono, B.
2018-03-01
Hybrid materials Nano-ZnO/polyurethane film was prepared with different zinc oxide (ZnO) content in polyurethane as a matrix. The film was deposited on low carbon steel plate using high volume low pressure (HVLP) method. To observe thermal behaviour of the film, the sample was investigated using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). Fourier transform infrared spectroscopy (FTIR) was used to see whether any chemical reaction of ZnO in polyurethane occured. TGA and FTIR results showed that the decomposition temperature shifted to a higher point and the chemical reaction of zinc oxide in polyurethane occurred. The surface morphology changed and the corrosion resistance increased with an increase of ZnO content
Directory of Open Access Journals (Sweden)
Jun Gou
2015-06-01
Full Text Available Enhanced terahertz (THz absorption of NiCr film deposited on a dielectric substrate has been proven by applying a reactive ion etching (RIE treatment to the dielectric film. Nano – scale nickel – chromium (NiCr thin films are deposited on RIE treated silicon dioxide (SiO2 dielectric substrates to study the transmission and reflection characteristics. Experimental results suggest that both transmission and reflection of NiCr film are weakened by the RIE treatment. The most significant decrease of transmission is observed in 1 ~ 4 THz while that of reflection occurs in 1.7 ~ 2.5 THz band. The decrease of both transmission and reflection is more significant for NiCr film with higher thickness. The RIE treatment, which induces nano – scale surface structures and increases the effective surface area of NiCr film, enhances the absorption and weakens the transmission and reflection of THz radiation.DOI: http://dx.doi.org/10.5755/j01.ms.21.2.6131
Abbas, K
2015-12-10
© 2016 IOP Publishing Ltd. The mechanical behavior of polycrystalline Pt thin films is reported for thicknesses of 75 nm, 100 nm, 250 nm, and 400 nm. These thicknesses correspond to transitions between nanocrystalline grain morphology types as found in TEM studies. Thinner samples display a brittle behavior, but as thickness increases the grain morphology evolves, leading to a ductile behavior. During evolution of the morphology, dramatic differences in elastic moduli (105-160 GPa) and strengths (560-1700 MPa) are recorded and explained by the variable morphology. This work suggests that in addition to the in-plane grain size of thin films, the transitions in cross-sectional morphologies of the Pt films significantly affect their mechanical behavior.
Thin NiTi Films Deposited on Graphene Substrates
Hahn, S.; Schulze, A.; Böhme, M.; Hahn, T.; Wagner, M. F.-X.
2017-03-01
We present experimental results on the deposition of Nickel Titanium (NiTi) films on graphene substrates using a PVD magnetron sputter process. Characterization of the 2-4 micron thick NiTi films by electron microscopy, electron backscatter diffraction, and transmission electron microscopy shows that grain size and orientation of the thin NiTi films strongly depend on the type of combination of graphene and copper layers below. Our experimental findings are supported by density functional theory calculations: a theoretical estimation of the binding energies of different NiTi-graphene interfaces is in line with the experimentally determined microstructural features of the functional NiTi top layer.
Deactivation of nickel hydroxide-gold modified electrodes
Caram, Bruno; Tucceri, Ricardo
2013-01-01
The aim of the present work was to study how the charge-transport process of a nickel hydroxide film electrochemically synthesized on a gold substrate is modified when the electrode is stored for a long time. It was found that nickel hydroxide films are deactivated under storage, that is, films became less conductive than films immediately prepared (nondeactivated). This study was carried out in the context of the rotating disc electrode voltammetry when the modified electrode contacts an ele...
International Nuclear Information System (INIS)
Hur, Tae-Bong; Kim, Hong Koo; Perello, David; Yun, Minhee; Kulovits, Andreas; Wiezorek, Joerg
2008-01-01
Epitaxial nanocrystalline Ag films were grown on initially native-oxide-covered Si(001) substrates using radio-frequency magnetron sputtering. Mechanisms of grain growth and morphology evolution were investigated. An epitaxially oriented Ag layer (∼5 nm thick) formed on the oxide-desorbed Si surface during the initial growth phase. After a period of growth instability, characterized as kinetic roughening, grain growth stagnation, and increase of step-edge density, a layer of nanocrystalline Ag grains with a uniform size distribution appeared on the quasi-two-dimensional layer. This hierarchical process of film formation is attributed to the dynamic interplay between incoming energetic Ag particles and native oxide. The cyclic interaction (desorption and migration) of the oxide with the growing Ag film is found to play a crucial role in the characteristic evolution of grain growth and morphology change involving an interval of grain growth stagnation
Large-grain polycrystalline silicon film by sequential lateral solidification on a plastic substrate
International Nuclear Information System (INIS)
Kim, Yong-Hae; Chung, Choong-Heui; Yun, Sun Jin; Moon, Jaehyun; Park, Dong-Jin; Kim, Dae-Won; Lim, Jung Wook; Song, Yoon-Ho; Lee, Jin Ho
2005-01-01
A large-grain polycrystalline silicon film was obtained on a plastic substrate by sequential lateral solidification. With various combinations of sputtering powers and Ar working gas pressures, the conditions for producing dense amorphous silicon (a-Si) and SiO 2 films were optimized. The successful crystallization of the a-Si film is attributed to the production of a dense a-Si film that has low argon content and can endure high-intensity laser irradiation
International Nuclear Information System (INIS)
Yu Qiaozhen; Wang Mang; Chen Hongzheng; Dai Zhengwei
2011-01-01
Highlights: → We fabricate PANI nanowire-on-TiO 2 nano/microfiber hierarchical nano/microstructure composite fiber films by electrospinning, calcinations and in situ polymerization. → PANI/TiO 2 composite fiber film exhibits high photocatalytic activity for the degradation of dye MB. → The photocatalytic activity and reusability of PANI/TiO 2 composite fiber film were lower than those of pure TiO 2 fiber film. - Abstract: TiO 2 /PANI composite fiber films were fabricated by electrospinning, calcinations and in situ polymerization. The morphology and structure of the resulting composites were analyzed by scanning electron micrograph, transmission electron micrograph, Fourier transform infrared spectroscopy and X-ray diffraction. It was found that this composite fiber film has a PANI nanowire-on-TiO 2 nano/microfiber hierarchical nano/microstructure. The surface morphology of this hierarchical nano/microstructure was related to the structure of TiO 2 nano/microfiber film, the time and temperature of in situ polymerization. Its photocatalytic property on methylene blue (MB) was studied, and the results showed that TiO 2 /PANI composite fiber film with this hierarchical nano/microstructure exhibited high photocatalytic activity for the degradation of MB under natural light. But both its photocatalytic activity and reusability were lower than those of pure TiO 2 fiber film. To improve the stability and reusability of TiO 2 /PANI composite fiber film, a direct chemical bonding of PANI chains onto TiO 2 surface, such as, the surface-initiated graft polymerization, is a useful method.
Nickel nanostructured materials from liquid phase photodeposition
International Nuclear Information System (INIS)
Giuffrida, Salvatore; Condorelli, Guglielmo G.; Costanzo, Lucia L.; Ventimiglia, Giorgio; Nigro, Raffaella Lo; Favazza, Maria; Votrico, Enrico; Bongiorno, Corrado; Fragala, Ignazio L.
2007-01-01
Liquid Phase Photo-Deposition (LPPD) technique has been used to obtain both colloidal particles and thin films of metallic and chloride nickel from solutions of only precursor Ni(acac) 2 (acac=2,4-pentandionato). Metallic nickel was obtained from ethanol solutions by direct nickel(II) photoreduction at 254 nm and by acetone sensitised reaction at 300 nm. In this latter process the rate was higher than in the first one. NiCl 2 was formed from CCl 4 solution by a solvent-initiated reaction. TEM analysis, performed on colloidal particles of nickel, showed that their dimensions are in the range 2-4 nm. The films did not present carbon contamination and were characterized by AFM, XPS and GIXRD. Metallic films consisted of particles of 20-40 nm that are the result of the aggregation of smaller crystallites (4-5 nm). Larger agglomerations (around 200 nm) have been observed for NiCl 2 films
Nickel nanostructured materials from liquid phase photodeposition
Energy Technology Data Exchange (ETDEWEB)
Giuffrida, Salvatore, E-mail: sgiuffrida@unict.it; Condorelli, Guglielmo G.; Costanzo, Lucia L.; Ventimiglia, Giorgio [Universita degli Studi di Catania and INSTM UdR di, Dipartimento di Scienze Chimiche (Italy); Nigro, Raffaella Lo [IMM-CNR (Italy); Favazza, Maria; Votrico, Enrico [Universita degli Studi di Catania and INSTM UdR di, Dipartimento di Scienze Chimiche (Italy); Bongiorno, Corrado [IMM-CNR (Italy); Fragala, Ignazio L. [Universita degli Studi di Catania and INSTM UdR di, Dipartimento di Scienze Chimiche (Italy)
2007-08-15
Liquid Phase Photo-Deposition (LPPD) technique has been used to obtain both colloidal particles and thin films of metallic and chloride nickel from solutions of only precursor Ni(acac){sub 2} (acac=2,4-pentandionato). Metallic nickel was obtained from ethanol solutions by direct nickel(II) photoreduction at 254 nm and by acetone sensitised reaction at 300 nm. In this latter process the rate was higher than in the first one. NiCl{sub 2} was formed from CCl{sub 4} solution by a solvent-initiated reaction. TEM analysis, performed on colloidal particles of nickel, showed that their dimensions are in the range 2-4 nm. The films did not present carbon contamination and were characterized by AFM, XPS and GIXRD. Metallic films consisted of particles of 20-40 nm that are the result of the aggregation of smaller crystallites (4-5 nm). Larger agglomerations (around 200 nm) have been observed for NiCl{sub 2} films.
Rivnay, Jonathan
2009-11-08
Solution-processable organic semiconductors are central to developing viable printed electronics, and performance comparable to that of amorphous silicon has been reported for films grown from soluble semiconductors. However, the seemingly desirable formation of large crystalline domains introduces grain boundaries, resulting in substantial device-to-device performance variations. Indeed, for films where the grain-boundary structure is random, a few unfavourable grain boundaries may dominate device performance. Here we isolate the effects of molecular-level structure at grain boundaries by engineering the microstructure of the high-performance n-type perylenediimide semiconductor PDI8-CN 2 and analyse their consequences for charge transport. A combination of advanced X-ray scattering, first-principles computation and transistor characterization applied to PDI8-CN 2 films reveals that grain-boundary orientation modulates carrier mobility by approximately two orders of magnitude. For PDI8-CN 2 we show that the molecular packing motif (that is, herringbone versus slip-stacked) plays a decisive part in grain-boundary-induced transport anisotropy. The results of this study provide important guidelines for designing device-optimized molecular semiconductors. © 2009 Macmillan Publishers Limited. All rights reserved.
Organic Nano-Grains in Comet 103P/Hartley 2: The Organic Glue of Porous Aggregate Grains?
Wooden, D. H.; Russo, N.Dello; Li, A.; Woodward, C. E.; Kelley, M. S.; Harker, D. E.; Cook, J. C.; Vervack, R. J.; Geballe, T. R.
2013-01-01
The GNIRS instrument on the Gemini 8--m telescope observed comet 103P/Hartley on 2010-- Dec--04UT, a month after the EPOXI Mission encounter, and detected the 3.3 and 3.4 um bands in emission. The 3.3/3.4 ratio and the broad band widths are consistent with experiments of heated (approximately 600 K) aliphatic carbon (-CH3, -CH2) thin films. For the 3.4 micron band to be in emission, the aliphatic bonds must be attached to a carrier possessing the strongly UV--absorbing C=C aromatic rings, and these rings have to be less than 50--100 carbon atoms (4-6 Angstrom) for attached -CH bonds to also generate a 3.3 micron-band in emission. Slightly larger (=10Å) Very Small Grains (VSGs) can absorb single UV photons comparable to or exceeding their heat capacity, thermally fluctuate and release IR photon(s). The 3.3 micron and 3.4 micron bands observed by GNIRS suggest that organic macromolecules/ nano--grains with both aliphatic and aromatic bonds are fluorescing/thermally fluctuating in the coma. Aliphatic and aromatic materials have been seen in Stardust samples and the primitive carbonaceous chondrite 'Tagish Lake'. The larger the ratio of the -CH2/-CH3 components of the aliphatic 3.4 micron band, the more 'primitive' the organic material. In a Stardust organic globule, some aliphatic bonds were transformed into aromatic bonds during the low dosage of Transmission Electron Microscope imaging. Conversely, lab experiments show irradiation of ices containing small PAHs generates aliphatic organics. Photo--processing of ices also likely forms the ubiquitous aliphatic coatings that appear on the surfaces of all silicate subgrains constituting nine cometary interplanetary dust particles. The aliphatic coatings, dominated by -CH2, likely were important in sticking the aggregates together, and existed prior to incorporation of dust aggregates into comet nuclei. These comet aliphatics may be some of the sought--after precursors to the more robust and complex
Ridhi, R.; Singh, Sukhdeep; Saini, G. S. S.; Tripathi, S. K.
2018-04-01
The present study deals with comparing interaction mechanisms of copper phthalocyanine and nickel phthalocyanine with versatile chemical vapours: reducing, stable aromatic and oxidizing vapours namely; diethylamine, benzene and bromine. The variation in electrical current of phthalocyanines with exposure of chemical vapours is used as the detection parameter for studying interaction behaviour. Nickel phthalocyanine is found to exhibit anomalous behaviour after exposure of reducing vapour diethylamine due to alteration in its spectroscopic transitions and magnetic states. The observed sensitivities of copper phthalocyanine and nickel phthalcyanine films are different in spite of their similar bond numbers, indicating significant role of central metal atom in interaction mechanism. The variations in electronic transition levels after vapours exposure, studied using UV-Visible spectroscopy confirmed our electrical sensing results. Bromine exposure leads to significant changes in vibrational bands of metal phthalocyanines as compared to other vapours.
Crossover And MTF Characteristics Of A Tabular-Grain X-Ray Film
Huff, K. E.; Wagner, P. W.
1984-08-01
An orthochromatic x-ray film made with tabular silver halide grains has a significantly higher MTF when exposed with green-emitting intensifying screens than do conventional films with similar sensitometric properties. The primary reason for the improved MTF is a decrease in the amount of crossover exposure, i.e., exposure by light that has crossed the support one or more times. Two well-established sensitometric procedures for measuring crossover have been compared. One produces results accurate enough for calculations of MTF relationships. Calculated MTF relationships for tabulargrain and conventional films are compared with measured values.
Effect of microscopic structure on deformation in nano-sized copper and Cu/Si interfacial cracking
Energy Technology Data Exchange (ETDEWEB)
Sumigawa, Takashi, E-mail: sumigawa@cyber.kues.kyoto-u.ac.jp; Nakano, Takuya; Kitamura, Takayuki
2013-03-01
The purpose of this work is to examine the effect of microscopic structure on the mechanical properties of nano-sized components (nano-components). We developed a bending specimen with a substructure that can be observed by means of a transmission electron microscope (TEM). We examined the plastic behavior of a Cu bi-crystal and the Cu/Si interfacial cracking in a nano-component. TEM images indicated that an initial plastic deformation takes place near the interface edge (the junction between the Cu/Si interface and the surface) in the Cu film with a high critical resolved shear stress (400–420 MPa). The deformation developed preferentially in a single grain. Interfacial cracking took place at the intersection between the grain boundary and the Cu/Si interface, where a high stress concentration existed due to deformation mismatch. These results indicate that the characteristic mechanical behavior of a nano-component is governed by the microscopic stress field, which takes into account the crystallographic structure. - Highlights: ► A nano-component specimen including a bi-crystal copper layer was prepared. ► A loading test with in-situ transmission electron microscopy was conducted. ► The plastic and cracking behaviors were governed by microscopic stress. ► Stress defined under continuum assumption was still present in nano-components.
Self-organised nano-structuring of thin oxide-films under swift heavy ion bombardment
International Nuclear Information System (INIS)
Bolse, Wolfgang
2006-01-01
Surface instabilities and the resulting self-organisation processes play an important role in nano-technology since they allow for large-array nano-structuring. We have recently found that the occurrence of such instabilities in thin film systems can be triggered by energetic ion bombardment and the subsequent self-assembly of the surface can be nicely controlled by fine-tuning of the irradiation conditions. The role of the ion in such processes is of double nature: If the instability is latently present already in the virgin sample, but self-assembly cannot take place because of kinetic barriers, the ion impact may just supply the necessary atomic mobility. On the other hand, the surface may become instable due to the ion beam induced material modifications and further irradiation then results in its reorganisation. In the present paper, we will review recently observed nano-scale self-organisation processes in thin oxide-films induced by the irradiation with swift heavy ions (SHI) at some MeV/amu energies. The first example is about SHI induced dewetting, which is driven by capillary forces already present in the as-deposited samples. The achieved dewetting pattern show an amazing similarity to those observed for liquid polymer films on Si, although in the present case the samples were kept at 80 K and hence have never reached their melting point. The second example is about self-organised lamellae formation driven by planar stresses, which are induced by SHI bombardment under grazing incidence and result in a surface instability and anisotropic plastic deformation (hammering effect). Taking advantage of these effects and modifying the irradiation procedure, we were able to generate more complex structures like NiO-'nano-towers' of 2 μm height and 200 nm in diameter
Development of nano-sized α-Al2O3:C films for application in digital radiology
International Nuclear Information System (INIS)
Silva, Edna C.
2011-01-01
Ceramic materials are widely used as sensors for ionizing radiation. In nuclear applications, the alpha-alumina doped with carbon (α-Al 2 O 3 :C) is the most widely ceramic used because of its excellent optically stimulated luminescence (OSL) and thermoluminescent (TL) properties applied to detection of ionizing radiation. Another application of OSL and TL materials are in Digital Radiography, with ceramic/polymeric film composites. Recently, Computed Radiography (CR) devices based on OSL materials are replacing the old conventional film radiography. In this study we investigate the thermoluminescence of nano-sized α-Al 2 O 3 samples doped with different percentages of carbon, sintered in reducing atmospheres at temperatures ranging from 1300 to 1750 deg C. The results indicate that the nano-sized α-Al 2 O 3 :C materials have a luminescent response that could be due to both OSL and RPL properties, but without application to radiation dosimetry. Moreover, the results indicate that micro-sized α-Al 2 O 3 :C, doped with 0.5% carbon, and nano-sized ones doped with 2% of carbon, present thermoluminescent signal around 30 to 100 times the TL output signal of commercial TLD-100, the most used TL dosimeter in the world. The results indicate that these ceramic nano-particles have great potential for use in Digital Radiography based on thermoluminescent film imaging, being able to provide image resolutions much higher than the micro-sized α-Al 2 O 3 :C, in view of their improved resolution provided by nano-particulates. (author)
International Nuclear Information System (INIS)
Savaloni, Hadi; Babaei, Reza
2013-01-01
Silver chiral nano-flower sculptured thin films with 3-, 4- and 5-fold symmetry were produced on copper substrates using oblique angle deposition method in conjunction with rotation of sample holder with different speeds at different sectors of each revolution corresponding to symmetry order of the acquired nano-flower. Atomic force microscopy (AFM) and field emission scanning electron microscopy (FESEM) were employed to obtain morphologies and nano-structure of the films. Raman spectroscopy was performed on all samples that were subject to impregnation by 4,4′-bipyridine (C 10 H 8 N 2 ) solution. A high degree of enhancement of the main bands at 1610, 1297, and 1009 cm −1 that can be assigned to the C=C stretching mode, aromatic ring stretching ring and in-plane ring mode of 4,4′-bipyridine, is achieved.
Energy Technology Data Exchange (ETDEWEB)
Savaloni, Hadi, E-mail: savaloni@khayam.ut.ac.ir [Department of Physics, University of Tehran, North-Kargar Street, Tehran (Iran, Islamic Republic of); Babaei, Reza, E-mail: reza_babaee_62@yahoo.com [Department of Physics, Islamic Azad University, Science and Research Branch, Tehran (Iran, Islamic Republic of)
2013-09-01
Silver chiral nano-flower sculptured thin films with 3-, 4- and 5-fold symmetry were produced on copper substrates using oblique angle deposition method in conjunction with rotation of sample holder with different speeds at different sectors of each revolution corresponding to symmetry order of the acquired nano-flower. Atomic force microscopy (AFM) and field emission scanning electron microscopy (FESEM) were employed to obtain morphologies and nano-structure of the films. Raman spectroscopy was performed on all samples that were subject to impregnation by 4,4′-bipyridine (C{sub 10}H{sub 8}N{sub 2}) solution. A high degree of enhancement of the main bands at 1610, 1297, and 1009 cm{sup −1} that can be assigned to the C=C stretching mode, aromatic ring stretching ring and in-plane ring mode of 4,4′-bipyridine, is achieved.
Sreesattabud, Tharathip; Gibbons, Brady J.; Watcharapasorn, Anucha; Jiansirisomboon, Sukanda
2013-07-01
Pb(Zr0.52Ti0.48)O3 or PZT thin films embedded with CuO nano-particles were successfully prepared by a hybrid sol-gel process. In this process, CuO (0, 0.1, 0.2, 0.3, 0.4, 0.5 and 1 wt. %) nanopowder was suspended in an organometallic solution of PZT, and then coated on platinised silicon substrate using a spin-coating technique. The influence of CuO nano-particles' dispersion on the phase of PZT thin films was investigated. XRD results showed a perovskite phase in all films. At the CuO concentration of 0.4-1 wt. %, a second phase was observed. The addition of CuO nano-particles affected the orientation of PZT thin films. The addition was also found to reduce the ferroelectric properties of PZT thin films. However, at 0.2 wt. % CuO concentration, the film exhibited good ferroelectric properties similar to those of PZT films. In addition, the fatigue retention properties of the PZT/CuO system was observed, and it showed 14% fatigue at 108 switching bipolar pulse cycles while the fatigue in PZT thin films was found to be 17% at the same switching bipolar pulse cycles.
Phosphorylated nano-diamond/ Polyimide Nanocomposites
International Nuclear Information System (INIS)
Beyler-Çiǧil, Asli; Çakmakçi, Emrah; Kahraman, Memet Vezir
2014-01-01
In this study, a novel route to synthesize polyimide (PI)/phosphorylated nanodiamond films with improved thermal and mechanical properties was developed. Surface phosphorylation of nano-diamond was performed in dichloromethane. Phosphorylation dramatically enhanced the thermal stability of nano-diamond. Poly(amic acid) (PAA), which is the precursor of PI, was successfully synthesized with 3,3',4,4'-Benzophenonetetracarboxylic dianhydride (BTDA) and 4,4'-oxydianiline (4,4'-ODA) in the solution of N,N- dimethylformamide (DMF). Pure BTDA-ODA polyimide films and phosphorylated nanodiamond containing BTDA-ODA PI films were prepared. The PAA displayed good compatibility with phosphorylated nano-diamond. The morphology of the polyimide (PI)/phosphorylated nano-diamond was characterized by scanning electron microscopy (SEM). Chemical structure of polyimide and polyimide (PI)/phosphorylated nano-diamond was characterized by FTIR. SEM and FTIR results showed that the phosphorylated nano-diamond was successfully prepared. Thermal properties of the polyimide (PI)/phosphorylated nanodiamond was characterized by thermogravimetric analysis (TGA). TGA results showed that the thermal stability of (PI)/phosphorylated nano-diamond film was increased
International Nuclear Information System (INIS)
Bastani, S.; Ebrahimi, M.; Kardar, P.
2007-01-01
In this research, an epoxy acrylate resin was synthesized, then the synthesized resin was used along with different multifunctional acrylate monomers and with a photoinitiator in different formulations and cured with UV radiation. The experiments were designed based on mixture method by using Design-Expert software. To investigate the effect of nano particles on the some of physical and mechanical properties of the UV cured resins, the suspension of nano alumina in TPGDA, was used in formulations. The hardness of prepared films was evaluated by using konig hardness tester and nano indentater. The scratch resistance and gloss of the films were also determined. The results showed that the visibility of scratch decreased when the nano particles were used. It seems that the self-healing property of the film improved in the presence of nano particles. The hardness of the samples with nano particles was found to be less than that the samples of without any nano particles. It was observed that the gloss of the films with the nano particles, almost was the same as the film without nano particles. (Author)
Capacitance measurements and AC conductivity of Nickel Phthalocyanine films
International Nuclear Information System (INIS)
Darwish, S.
2005-01-01
A C dark Current measurements of nickel phthalocyanine thin films using ohmic gold electrodes are investigated in the frequency range 30-10 Hz and within the temperature range 295-385 K. The A C conductivity as D Ac is found to vary as within the index s < 1, indicating a dominant hopping process at low temperatures. From the temperature dependence of A C conductivity, free carrier conduction with mean activation energy of 0.31 eV is observed at higher temperatures. Capacitance and loss tangent are found to be decreased with increasing frequency and increase with increasing temperature. Such characteristics are found to be in good qualitative agreement with existing equivalent circuit model assuming ohmic contacts
International Nuclear Information System (INIS)
Lou, C.
2002-01-01
An advection-diffusion model has been set up to describe normal grain growth. In this model grains are divided into different groups according to their topological classes (number of sides of a grain). Topological transformations are modelled by advective and diffusive flows governed by advective and diffusive coefficients respectively, which are assumed to be proportional to topological classes. The ordinary differential equations governing self-similar time-independent grain size distribution can be derived analytically from continuity equations. It is proved that the time-independent distributions obtained by solving the ordinary differential equations have the same form as the time-dependent distributions obtained by solving the continuity equations. The advection-diffusion model is extended to describe the stagnation of normal grain growth in thin films. Grain boundary grooving prevents grain boundaries from moving, and the correlation between neighbouring grains accelerates the stagnation of normal grain growth. After introducing grain boundary grooving and the correlation between neighbouring grains into the model, the grain size distribution is close to a lognormal distribution, which is usually found in experiments. A vertex computer simulation of normal grain growth has also been carried out to make a cross comparison with the advection-diffusion model. The result from the simulation did not verify the assumption that the advective and diffusive coefficients are proportional to topological classes. Instead, we have observed that topological transformations usually occur on certain topological classes. This suggests that the advection-diffusion model can be improved by making a more realistic assumption on topological transformations. (author)
Feng, Xin-Xing; Zhang, Li-Li; Chen, Jian-Yong; Guo, Yu-Hai; Zhang, Hua-Peng; Jia, Chang-Ian
2007-01-30
This paper describes the synthesis and characterization of new regenerated silk fibroin (SF)/nano-TiO(2) composite films. The preparation method, based on the sol-gel technique using butyl titanate as oxide precursor, could avoid reagglomeration of the prepared nanoparticles. Samples were characterized mainly by X-ray diffraction (XRD), ultra-violet (UV) spectroscopy, atomic force microscopy (AFM), Fourier transform infrared (FT-IR) spectroscopy, and thermogravimetric analysis (TGA). The UV and AFM results indicated that TiO(2) nanoparticles could be well dispersed inside the SF film, and the size of TiO(2) was about 80nm. The XRD and FT-IR analysis implied that the formation of nano-TiO(2) particles may induce the conformational transition of silk fibroin to a typical Silk II structure partly with the increasing of crystallinity in the composite films. Compared to the pure SF films, the mechanical and thermal properties of composite films were improved, and the solubility in water was decreased due to the conformational transition of silk fibroin to Silk II structure.
Effect of texture and grain size on the residual stress of nanocrystalline thin films
Cao, Lei; Sengupta, Arkaprabha; Pantuso, Daniel; Koslowski, Marisol
2017-10-01
Residual stresses develop in thin film interconnects mainly as a result of deposition conditions and multiple thermal loading cycles during the manufacturing flow. Understanding the relation between the distribution of residual stress and the interconnect microstructure is of key importance to manage the nucleation and growth of defects that can lead to failure under reliability testing and use conditions. Dislocation dynamics simulations are performed in nanocrystalline copper subjected to cyclic loading to quantify the distribution of residual stresses as a function of grain misorientation and grain size distribution. The outcomes of this work help to evaluate the effect of microstructure in thin films failure by identifying potential voiding sites. Furthermore, the simulations show how dislocation structures are influenced by texture and grain size distribution that affect the residual stress. For example, when dislocation loops reach the opposite grain boundary during loading, these dislocations remain locked during unloading.
The morphology and structure of PVD ZrN-Cu thin films
International Nuclear Information System (INIS)
Audronis, M; Jimenez, O; Leyland, A; Matthews, A
2009-01-01
ZrN-Cu thin films containing variable amounts of copper, namely 8, 33 and 58 at%, were produced by reactive pulsed unbalanced magnetron sputtering. Coatings were found to possess hardness values of 22.5 GPa, 9.5 GPa and 3.7 GPa, respectively. The morphology of coatings was investigated by field emission gun scanning electron microscopy and the structure (microstructure and nanostructure) was investigated by conventional (bright-field and dark-field imaging) and high-resolution transmission electron microscopy. Complementary x-ray diffraction experiments were also performed. ZrN coatings containing 8 at% of copper were found to possess a nano-columnar structure composed of ZrN columnar grains, the diameter of which was approximately 15-35 nm. The majority of the copper content was apparently dissolved within the ZrN grains, rather than existing as a separate phase. Coatings of the two other compositions were found to be composed of a mixture of mostly equiaxed ZrN and Cu nano-crystalline grains, the diameters of which were in the approximate range 5-25 nm. None of the coatings investigated in this study were found to possess the so-called 'nanocomposite' structure, which is often envisaged as crystalline nano-grains surrounded by a thin amorphous intergranular phase. Instead, coatings were found to be either single-phase ZrN (with Cu in substitutional solid solution for Zr) or a mixture of ZrN and Cu nano-grains.
Nano structured TiO2 thin films by polymeric precursor method
International Nuclear Information System (INIS)
Stroppa, Daniel Grando; Giraldi, Tania Regina; Leite, Edson Roberto; Varela, Jose Arana; Longo, Elson
2008-01-01
This work focuses in optimizing setup for obtaining TiO 2 thin films by polymeric precursor route due to its advantages on stoichiometric and morphological control. Precursor stoichiometry, synthesis pH, solids concentration and rotation speed at deposition were optimized evaluating thin films morphology and thickness. Thermogravimetry and NMR were applied for precursor's characterization and AFM, XRD and ellipsometry for thin films evaluation. Results showed successful attainment of homogeneous nanocrystalline anatase TiO 2 thin films with outstanding control over morphological characteristics, mean grain size of 17 nm, packing densities between 57 and 75%, estimated surface areas of 90 m 2 /g and monolayers thickness within 20 and 128 nm. (author)
Highly efficient electrochemical hydrogen evolution based on nickel diselenide nanowall film
Tang, Chun; Xie, Lisi; Sun, Xuping; Asiri, Abdullah M.; He, Yuquan
2016-05-01
In this letter, we report on hydrothermal growth of nickel diselenide nanowall film on carbon cloth (NiSe2 NW/CC) through topotactic transformation from a Ni(OH)2 precursor based on anion exchange reactions. When tested as an integrated 3D hydrogen-evolving cathode in strongly acidic media, NiSe2 NW/CC exhibits outstanding catalytic activity superior to its powder counterpart and strong long-term durability. It displays 10 and 100 mA cm-2 at overpotentials of 145 and 183 mV, respectively, with its catalytic activity being retained for 40 h.
International Nuclear Information System (INIS)
Zhang, Shu; Wu, Lu; Yue, Ruoyu; Yan, Zongkai; Zhan, Haoran; Xiang, Yong
2013-01-01
To investigate the effects of Sb doping on the kinetics of grain growth in Cu(In,Ga)Se 2 (CIGS) thin films during annealing, CIGS thin films were sputtered onto Mo coated substrates from a single CIGS alloy target, followed by chemical bath deposition of Sb 2 S 3 thin layers on top of CIGS layers and subsequent annealing at different temperatures for 30 min in Se vapors. X-ray diffraction results showed that CIGS thin films were obtained directly using the single-target sputtering method. After annealing, the In/Ga ratio in Sb-doped CIGS thin films remained stable compared to undoped film, possibly because Sb can promote the incorporation of Ga into CIGS. The grain growth in CIGS thin films was enhanced after Sb doping, exhibiting significantly larger grains after annealing at 400 °C or 450 °C compared to films without Sb. In particular, the effect was strikingly significant in grain growth across the film thickness, resulting in columnar grain structure in Sb-doped films. This grain growth improvement may be led by the diffusion of Sb from the front surface to the CIGS-Mo back interface, which promoted the mass transport process in CIGS thin films. - Highlights: ► Cu(In,Ga)Se 2 (CIGS) thin films made by sputtering from a single CIGS target. ► Chemical bath deposition used to introduce antimony into CIGS absorber layers. ► In/Ga ratio decreases in Sb-doped annealed films, comparatively to undoped films. ► Sb-doped CIGS films are superior to undoped films in terms of grain-growth kinetics
Qin, Yang; Zhang, Shuangling; Yu, Jing; Yang, Jie; Xiong, Liu; Sun, Qingjie
2016-08-20
We investigated the effects of chitin nano-whiskers (CNWs) on the antibacterial and physiochemical properties of maize starch-based films. The microstructures, crystalline structures, and thermal, mechanical and barrier properties of the nanocomposite films were characterized by using transmission electron microscopy, X-ray diffraction analysis, thermogravimetric, differential scanning calorimeter, and texture profile analysis. The tensile strength of the maize starch films increased from 1.64MPa to 3.69MPa (Pstarch films. Furthermore, the nanocomposite films exhibited strong antimicrobial activity against Gram-positive Listeria monocytogenes but not against Gram-negative Escherichia coli. Copyright © 2016 Elsevier Ltd. All rights reserved.
Characterization of MAPLE deposited WO3 thin films for electrochromic applications
Boyadjiev, S. I.; Stefan, N.; Szilágyi, I. M.; Mihailescu, N.; Visan, A.; Mihailescu, I. N.; Stan, G. E.; Besleaga, C.; Iliev, M. T.; Gesheva, K. A.
2017-01-01
Tungsten trioxide (WO3) is a widely studied material for electrochromic applications. The structure, morphology and optical properties of WO3 thin films, grown by matrix assisted pulsed laser evaporation (MAPLE) from monoclinic WO3 nano-sized particles, were investigated for their possible application as electrochromic layers. A KrF* excimer (λ=248 nm, ζFWHM=25 ns) laser source was used in all experiments. The MAPLE deposited WO3 thin films were studied by atomic force microscopy (AFM), grazing incidence X-ray diffraction (GIXRD) and Fourier transform infrared spectroscopy (FTIR). Cyclic voltammetry measurements were also performed, and the coloring and bleaching were observed. The morpho-structural investigations disclosed the synthesis of single-phase monoclinic WO3 films consisting of crystalline nano-grains embedded in an amorphous matrix. All thin films showed good electrochromic properties, thus validating application of the MAPLE deposition technique for the further development of electrochromic devices.
Characterization of MAPLE deposited WO3 thin films for electrochromic applications
International Nuclear Information System (INIS)
Boyadjiev, S I; Iliev, M T; Stefan, N; Mihailescu, N; Visan, A; Mihailescu, I N; Szilágyi, I M; Stan, G E; Besleaga, C; Gesheva, K A
2017-01-01
Tungsten trioxide (WO 3 ) is a widely studied material for electrochromic applications. The structure, morphology and optical properties of WO 3 thin films, grown by matrix assisted pulsed laser evaporation (MAPLE) from monoclinic WO 3 nano-sized particles, were investigated for their possible application as electrochromic layers. A KrF* excimer (λ=248 nm, ζ FWHM =25 ns) laser source was used in all experiments. The MAPLE deposited WO 3 thin films were studied by atomic force microscopy (AFM), grazing incidence X-ray diffraction (GIXRD) and Fourier transform infrared spectroscopy (FTIR). Cyclic voltammetry measurements were also performed, and the coloring and bleaching were observed. The morpho-structural investigations disclosed the synthesis of single-phase monoclinic WO 3 films consisting of crystalline nano-grains embedded in an amorphous matrix. All thin films showed good electrochromic properties, thus validating application of the MAPLE deposition technique for the further development of electrochromic devices. (paper)
Study of rapid grain boundary migration in a nanocrystalline Ni thin film
International Nuclear Information System (INIS)
Kacher, Josh; Robertson, I.M.; Nowell, Matt; Knapp, J.; Hattar, Khalid
2011-01-01
Research highlights: → Abnormal growth is distributed randomly in the foil and initiates at different times. → Growth occurs from seemingly uncorrelated regions of the grain boundary. → Growth twins are created during all stages of abnormal grain growth. → Grain growth patterns are qualitatively similar to a vacancy diffusion model. → Grain boundaries and orientations evolve during growth to minimize system energy. - Abstract: Grain boundary migration associated with abnormal grain growth in pulsed-laser deposited Ni was studied in real time by annealing electron transparent films in situ in the transmission electron microscope. The resulting texture evolution and grain boundary types produced were evaluated by ex situ electron backscatter diffraction of interrupted anneals. The combination of these two techniques allowed for the investigation of grain growth rates, grain morphologies, and the evolution of the orientation and grain boundary distributions. Grain boundaries were found to progress in a sporadic, start/stop fashion with no evidence of a characteristic grain growth rate. The orientations of the abnormally growing grains were found to be predominately //ND throughout the annealing process. A high fraction of twin boundaries developed during the annealing process. The intermittent growth from different locations of the grain boundary is discussed in terms of a vacancy diffusion model for grain growth.
Effect of microstructure on helium bubble growth in irradiated nickel
International Nuclear Information System (INIS)
Sattler, M.L.
1986-01-01
Thin nickel films were irradiated with 80 keV helium ions at varying doses and varying temperatures in order to obtain a variety of final microstructures. The growth of bubbles was examined during in-situ irradiations at 950 0 C where migration and coalescence events were observed for bubbles as large as 60 nm. Further direct observations of bubble growth were made during annealing of the irradiated specimens. For sample with no visible bubbles before annealing, the heating to 0.51 T/sub M/ produced bubbles that increased in diameter with annealing time to the power n. For bubbles in the grain interior, n ∼ 1, and on the grain boundaries, n ∼ 0.6. Since no migration and coalescence or ripening theories predict this behavior, a theory described by transient diffusion to spherical sinks was developed to discuss the behavior. This theory predicts that n = 1 for bubbles growing in the grain interior and n = 0.5 for bubbles on the grain boundary. In other annealing of irradiated samples containing large bubble populations, the growth of large bubbles and shrinking of small bubbles was observed at a temperature equal to 0.54 T/sub M/. The theory of Ostwald ripening properly described this type of bubble growth. Mass spectrometer measurements of He content in the irradiated specimens showed a greater He retention in the Ni films that contained a significant bubble population than those with no visible bubbles
Devices for fatigue testing of electroplated nickel (MEMS)
DEFF Research Database (Denmark)
Larsen, Kristian Pontoppidan; Ravnkilde, J. T.; Ginnerup, Morten
2002-01-01
μm and an effective length from 4μm to 27μm. Maximum stresses of the test beam were calculated to be 500MPa to 2100MPa by use of FEM tools. The test results indicate very promising fatigue properties of nano-nickel, as none of the test devices have shown fatigue failure or even initiation of cracks......In-situ fatigue test devices with integrated electrostatic actuator were fabricated in electroplated nanocrystalline nickel (nano-nickel). The devices feature in-plane approximately pure bending with fixed displacement of the test specimen of the dimensions: widths from 2μm to 3.7μm, a height of 7...... after 108 cycles. The combination of high strength and toughness, which is known for nanocrystalline materials, together with very small test specimens and low surface roughness could be the explanation for the good fatigue properties....
Energy Technology Data Exchange (ETDEWEB)
Park, S.H.; Kim, J.Y.; Kim, K.B. [Division of Materials Science and Engineering, Yonsei University, Seoul (Korea, Republic of)
2010-10-15
Nano-structured anhydrous ruthenium oxide (RuO{sub 2}) thin films were prepared using an electrostatic spray deposition (ESD) technique followed by electrochemical lithiation and delithiation. During the electrochemical lithiation process, RuO{sub 2} decomposed to nano-structured metallic ruthenium Ru with the concomitant formation of Li{sub 2}O. Nano-structured RuO{sub 2} was formed upon subsequent electrochemical extraction of Li from the Ru/Li{sub 2}O nanocomposite. Electrochemical lithiation/deliathiation at different charge/discharge rates (C-rate) was used to control the nano-structure of the anhydrous RuO{sub 2}. Electrochemical lithiation/delithiation of the RuO{sub 2} thin film electrode at different C-rates was closely related to the specific capacitance and high rate capability of the nano-structured anhydrous RuO{sub 2} thin film. Nano-structured RuO{sub 2} thin films prepared by electrochemical lithiation and delithiation at 2C rate showed the highest specific capacitance of 653 F g{sup -1} at 20 mV s{sup -1}, which is more than two times higher than the specific capacitance of 269 F g{sup -1} for the as-prepared RuO{sub 2}. In addition, it showed 14% loss in specific capacitance from 653 F g{sup -1} at 20 mV s{sup -1} to 559 F g{sup -1} at 200 mV s{sup -1}, indicating significant improvement in the high rate capability compared to the 26% loss of specific capacitance of the as-prepared RuO{sub 2} electrode from 269 F g{sup -1} at 20 mV s{sup -1} to 198 F g{sup -1} at 200 mV s{sup -1} for the same change in scan rate. (Abstract Copyright [2010], Wiley Periodicals, Inc.)
International Nuclear Information System (INIS)
Todd, N. K.; Mathur, N. D.; Blamire, M. G.
2001-01-01
The magnetoresistance of grain boundaries in the perovskite manganites is being studied, both in polycrystalline materials, and thin films grown on bicrystal substrates, because of interest in low-field applications. In this article we show that epitaxial films grown on SrTiO 3 bicrystal substrates of 45 degree misorientation show magnetoresistance behavior which is strongly dependent on the thickness of the film. Thin films, e.g., 40 nm, can show a large low-field magnetoresistance at low temperatures, with very sharp switching between distinct high and low resistance states for fields applied in plane and parallel to the boundary. Thicker films show a more complex behavior of resistance as a function of field, and the dependence on the angle between the applied field and the grain boundary is altered. These changes in magnetoresistance behavior are linked to the variation in morphology of the films. Thin films are coherently strained, due to the mismatch with the substrate, and very smooth. Thicker films relax, with the formation of defects, and hence different micromagnetic behavior. [copyright] 2001 American Institute of Physics
Solution-processed copper-nickel nanowire anodes for organic solar cells
Stewart, Ian E.; Rathmell, Aaron R.; Yan, Liang; Ye, Shengrong; Flowers, Patrick F.; You, Wei; Wiley, Benjamin J.
2014-05-01
This work describes a process to make anodes for organic solar cells from copper-nickel nanowires with solution-phase processing. Copper nanowire films were coated from solution onto glass and made conductive by dipping them in acetic acid. Acetic acid removes the passivating oxide from the surface of copper nanowires, thereby reducing the contact resistance between nanowires to nearly the same extent as hydrogen annealing. Films of copper nanowires were made as oxidation resistant as silver nanowires under dry and humid conditions by dipping them in an electroless nickel plating solution. Organic solar cells utilizing these completely solution-processed copper-nickel nanowire films exhibited efficiencies of 4.9%.This work describes a process to make anodes for organic solar cells from copper-nickel nanowires with solution-phase processing. Copper nanowire films were coated from solution onto glass and made conductive by dipping them in acetic acid. Acetic acid removes the passivating oxide from the surface of copper nanowires, thereby reducing the contact resistance between nanowires to nearly the same extent as hydrogen annealing. Films of copper nanowires were made as oxidation resistant as silver nanowires under dry and humid conditions by dipping them in an electroless nickel plating solution. Organic solar cells utilizing these completely solution-processed copper-nickel nanowire films exhibited efficiencies of 4.9%. Electronic supplementary information (ESI) available. See DOI: 10.1039/c4nr01024h
Chang, Ho; Lan, Chou-Wei; Guo, Jia-Bin
2011-12-01
This paper studies the influence of addition of 100 nm diameter nickel nano-particles on the friction properties of synthetic grease (Li base, VG100) in pneumatic cylinder. The friction force test of pneumatic cylinder equipment measures the frictional force between seal and cylinder bore in pneumatic cylinders. The lubricants with addition of nickel nano-particles were used for lubricating the contact interface between seal and cylinder bore. The friction force test equipment employ a load cell force sensor to measure the friction force between seals and cylinder bores. Results obtained from experimental tests are compared to determine the friction force between seals and cylinder bore in pneumatic cylinders. The study leads to the conclusion that the addition of nickel nano-particles to synthetic grease results in a decrease in friction force between seals and cylinder bores in pneumatic cylinder. This tribological behavior is closely related to the deposition of nano-particles on the rubbing surfaces
International Nuclear Information System (INIS)
Misra, D.S.; Misra, A.; Tyagi, Pawan K.; Karamakar, S.; Sharma, Surinder M.
2006-01-01
Full text: The nickel and cobalt nano wires of diameters ranging from 5-15 nm are formed inside the multiwalled carbon nantubes using microwave plasma chemical vapor deposition in our laboratory. The nano wires inside the tubes are found to have a perfect crystalline structure and the crystalline planes of (111) orientations are aligned for FCC nickel and cobalt in a particular fashion. We find that the cobalt can exist either in FCC or HCP phase in confinement depending upon the diameter of the tubes. The irradiation of these nanowires with high energy Au + ions alter the orientation of the crystalline planes and generate various types of domains and defects in the nanowires. The complete amorphization of the walls of the nano tubes is observed at the fluence of 5x10 13 /cm 2 and results in amorphization of nickel nano wires as well. The cobalt nano wires have FCC structure in ambient conditions and transform to HCP cobalt irreversibly when subjected to high pressure of ∼9 GPa. Multi-walled carbon nano tubes that encapsulate the cobalt nano wires do not undergo any other structural transformation with pressure except partial reversible amorphization beyond 9 GPa
Yun, Ho-Jin; Ham, Yong-Hyun; Shin, Hong-Sik; Jeong, Kwang-Seok; Park, Jeong-Gyu; Choi, Deuk-Sung; Lee, Ga-Won
2011-07-01
We have fabricated the flexible pentacene based organic thin film transistors (OTFTs) with formulated poly[4-vinylphenol] (PVP) gate dielectrics treated by CF4/O2 plasma on poly[ethersulfones] (PES) substrate. The solution of gate dielectrics is made by adding methylated poly[melamine-co-formaldehyde] (MMF) to PVP. The PVP gate dielectric layer was cross linked at 90 degrees under UV ozone exposure. Source/drain electrodes are formed by micro contact printing (MCP) method using nano particle silver ink for the purposes of low cost and high throughput. The optimized OTFT shows the device performance with field effect mobility of the 0.88 cm2/V s, subthreshold slope of 2.2 V/decade, and on/off current ratios of 1.8 x 10(-6) at -40 V gate bias. We found that hydrophobic PVP gate dielectric surface can influence on the initial film morphologies of pentacene making dense, which is more important for high performance OTFTs than large grain size. Moreover, hydrophobic gate dielelctric surface reduces voids and -OH groups that interrupt the carrier transport in OTFTs.
Elastic properties of porous low-k dielectric nano-films
Zhou, W.; Bailey, S.; Sooryakumar, R.; King, S.; Xu, G.; Mays, E.; Ege, C.; Bielefeld, J.
2011-08-01
Low-k dielectrics have predominantly replaced silicon dioxide as the interlayer dielectric for interconnects in state of the art integrated circuits. In order to further reduce interconnect RC delays, additional reductions in k for these low-k materials are being pursued via the introduction of controlled levels of porosity. The main challenge for such dielectrics is the substantial reduction in elastic properties that accompanies the increased pore volume. We report on Brillouin light scattering measurements used to determine the elastic properties of these films at thicknesses well below 200 nm, which are pertinent to their introduction into present ultralarge scale integrated technology. The observation of longitudinal and transverse standing wave acoustic resonances and their transformation into traveling waves with finite in-plane wave vectors provides for a direct non-destructive measure of the principal elastic constants that characterize the elastic properties of these porous nano-scale films. The mode dispersion further confirms that for porosity levels of up to 25%, the reduction in the dielectric constant does not result in severe degradation in the Young's modulus and Poisson's ratio of the films.
Golden, Gilad; Quinn, Elazar; Shaaya, Eli; Kostyukovsky, Moshe; Poverenov, Elena
2018-04-01
One of the most significant contributors to the global food crisis is grain loss during storage, mainly caused by pest insects. Currently, there are two main methods used for insect pest control: fumigation and grain protection using contact insecticides. As some chemical insecticides can harm humans and the environment, there is a global tendency to reduce their use by finding alternative eco-friendly approaches. In this study, the natural pest-managing agent pulegone was encapsulated into coarse and nano emulsions. The emulsions were characterized using spectroscopic and microscopic methods and their stability and pulegone release ability were examined. The insecticidal activity of the prepared formulations against two stored product insects, rice weevil (Sitophilus oryzae L.) and red flour beetle (Tribolium castaneum Herbst), was demonstrated. The nano emulsion-based formulation offered significant advantages and provided powerful bioactivity, with high (> 90%) mortality rates for as long as 5 weeks for both insects, whereas coarse emulsions showed high efficacy for only 1 week. The developed pulegone-based nano emulsions could serve as a model for an effective alternative method for pest control. Although pulegone is from a natural source, toxicological studies should be performed before the widespread application of pulegone or pulegone-containing essential oils to dry food products. © 2017 Society of Chemical Industry. © 2017 Society of Chemical Industry.
International Nuclear Information System (INIS)
Yodo, T.; Nakamura, T.; Kouyama, T.; Harada, Y.
2005-01-01
We investigated the influences of residual oxygen (O) impurities, cubic indium oxide (β-In 2 O 3 ) grains and indium oxy-nitride (InON) alloy grains in 200 nm-thick hexagonal (α)-InN crystalline films grown on Si(111) substrates by electron cyclotron resonance plasma-assisted molecular beam epitaxy. Although β-In 2 O 3 grains with wide band-gap energy were formed in In film by N 2 annealing, they were not easily formed in N 2 -annealed InN films. Even if they were not detected in N 2 -annealed InN films, the as-grown films still contained residual O impurities with concentrations of less than 0.5% ([O]≤0.5%). Although [O]∝1% could be estimated by investigating In 2 O 3 grains formed in N 2 -annealed InN films, [O]≤0.5% could not be measured by it. However, we found that they can be qualitatively measured by investigating In 2 O 3 grains formed by H 2 annealing with higher reactivity with InN and O 2 , using X-ray diffraction and PL spectroscopy. In this paper, we discuss the formation mechanism of InON alloy grains in InN films. (copyright 2005 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)
International Nuclear Information System (INIS)
Güneri, E.; Göde, F.; Çevik, S.
2015-01-01
In this the paper, we use the successive ion layer adsorption and reaction technique (SILAR) chemical deposition method to fabricate good quality PbS thin films and the effects of grain size on the structural and optical properties of the thin films were determined by varying deposition cases. All of the films obtained in different dipping cycles show cubic rock-salt (NaCl) structure. The preferred orientation changed from the (111) direction to the (200) direction with increasing dipping cycles. Grain size determined from scanning electron microscopy (SEM) increased from 32 nm to 104 nm. Moreover, changing of atomic ratio of the thin films is determined according to the results of energy dispersive X-ray (EDX). The transmission of the thin films was characterized by UV–Vis measurements from 400 nm to 1100 nm. It was determined from the allowed direct graphics that the energy band gaps of the thin films shift from 1.33 eV to 1.92 eV in connection with deposition conditions. The variation in band gap may be attributed to the variation of grain size. Additionally, the refractive index (n), extinction coefficient (k), real (ε 1 ) and imaginary (ε 2 ) dielectric constants varied with increasing immersion cycles. - Highlights: • The effects of grain size on the structural, optical properties of PbS thin films deposited by SILAR were investigated. • The preferred orientation varied from the (111) direction to the (200) direction with changing grain size. • The energy band gaps of the thin films shift from 1.33 eV to 1.92 eV in connection with deposition conditions. • The refractive index, extinction coefficient, real and imaginary dielectric constants varied with increasing dipping cycles
Energy Technology Data Exchange (ETDEWEB)
Güneri, E., E-mail: emineg7@gmail.com [Department of Primary Education, Erciyes University, Kayseri 38039, Turkey. (Turkey); Göde, F.; Çevik, S. [Department of Physics, Mehmet Akif Ersoy University, Burdur 15030, Turkey. (Turkey)
2015-08-31
In this the paper, we use the successive ion layer adsorption and reaction technique (SILAR) chemical deposition method to fabricate good quality PbS thin films and the effects of grain size on the structural and optical properties of the thin films were determined by varying deposition cases. All of the films obtained in different dipping cycles show cubic rock-salt (NaCl) structure. The preferred orientation changed from the (111) direction to the (200) direction with increasing dipping cycles. Grain size determined from scanning electron microscopy (SEM) increased from 32 nm to 104 nm. Moreover, changing of atomic ratio of the thin films is determined according to the results of energy dispersive X-ray (EDX). The transmission of the thin films was characterized by UV–Vis measurements from 400 nm to 1100 nm. It was determined from the allowed direct graphics that the energy band gaps of the thin films shift from 1.33 eV to 1.92 eV in connection with deposition conditions. The variation in band gap may be attributed to the variation of grain size. Additionally, the refractive index (n), extinction coefficient (k), real (ε{sub 1}) and imaginary (ε{sub 2}) dielectric constants varied with increasing immersion cycles. - Highlights: • The effects of grain size on the structural, optical properties of PbS thin films deposited by SILAR were investigated. • The preferred orientation varied from the (111) direction to the (200) direction with changing grain size. • The energy band gaps of the thin films shift from 1.33 eV to 1.92 eV in connection with deposition conditions. • The refractive index, extinction coefficient, real and imaginary dielectric constants varied with increasing dipping cycles.
International Nuclear Information System (INIS)
Wu Wei; Yu Qingkai; Pei, Shin-Shem; Peng Peng; Bao Jiming; Liu Zhihong
2012-01-01
Large-scale and transferable graphene films grown on metal substrates by chemical vapor deposition (CVD) still hold great promise for future nanotechnology. To realize the promise, one of the key issues is to further improve the quality of graphene, e.g., uniform thickness, large grain size, and low defects. Here we grow graphene films on Cu foils by CVD at ambient pressure, and study the graphene nucleation and growth processes under different concentrations of carbon precursor. On the basis of the results, we develop a two-step ambient pressure CVD process to synthesize continuous single-layer graphene films with large grain size (up to hundreds of square micrometers). Scanning electron microscopy and Raman spectroscopy characterizations confirm the film thickness and uniformity. The transferred graphene films on cover glass slips show high electrical conductivity and high optical transmittance that make them suitable as transparent conductive electrodes. The growth mechanism of CVD graphene on Cu is also discussed, and a growth model has been proposed. Our results provide important guidance toward the synthesis of high quality uniform graphene films, and could offer a great driving force for graphene based applications. (paper)
Energy Technology Data Exchange (ETDEWEB)
Bala, Manju, E-mail: manjubala474@gmail.com [Inter-University Accelerator Centre, Aruna Asaf Ali Marg, New Delhi 110067 (India); Meena, Ramcharan; Gupta, Srashti; Pannu, Compesh [Inter-University Accelerator Centre, Aruna Asaf Ali Marg, New Delhi 110067 (India); Tripathi, Tripurari S. [Aalto University, Värmemansgränden 2, 02150 Espoo (Finland); Varma, Shikha [Institute of Physics, Bhubaneshwar, Odisha 751005 (India); Tripathi, Surya K. [Department of Physics, Panjab University, Chandigarh 160 014 (India); Asokan, K., E-mail: asokaniuac@gmail.com [Inter-University Accelerator Centre, Aruna Asaf Ali Marg, New Delhi 110067 (India); Avasthi, Devesh K. [Amity University, Noida 201313, Uttar Pradesh (India)
2016-07-15
Present study demonstrates an enhancement in thermoelectric power of 10% Ag doped PbTe (PbTe:Ag) thin films when irradiated with 200 keV Ar ion. X-ray diffraction showed an increase in crystallinity for both PbTe and PbTe:10Ag nano-composite films after Ar ion irradiation due to annealing of defects in the grain boundaries. The preferential sputtering of Pb and Te ions in comparison to Ag ions resulted in the formation of nano-dots. This was further confirmed by X-ray photoelectron spectroscopy (XPS). Such an enhancement in thermoelectric power of irradiated PbTe:10Ag films in comparison to pristine PbTe:10Ag film is attributed to the decrease in charge carrier concentration that takes part in the transport process via restricting the tunneling of carriers through the wider potential barrier formed at the interface of nano-dots.
The study on corrosion resistance of decorative satin nickel plating
LU Wenya; CHENG Xianhua
2012-01-01
This study examined the corrosion resistance of satin nickel plating on conductive plastic.The electrochemical tests were to analyze the corrosion behavior of satin nickel plating with different processes in 3.5% NaCl solution.The results show that,because the satin nickel plating has an organic film on its surface due to process characteristics,the film results in different corrosion resistance.By increasing satin additive dosage,the nickel plating chroma decreases,the microsurface of the p...
Microstructural studies of carbides in MAR-M247 nickel-based superalloy
Szczotok, A.; Rodak, K.
2012-05-01
Carbides play an important role in the strengthening of microstructures of nickel-based superalloys. Grain boundary carbides prevent or retard grain-boundary sliding and make the grain boundary stronger. Carbides can also tie up certain elements that would otherwise promote phase instability during service. Various types of carbides are possible in the microstructure of nickel-based superalloys, depending on the superalloy composition and processing. In this paper, scanning electron and scanning transmission electron microscopy studies of carbides occurring in the microstructure of polycrystalline MAR-M247 nickel-based superalloy were carried out. In the present work, MC and M23C6 carbides in the MAR-M247 microstructure were examined.
International Nuclear Information System (INIS)
Haustrup, N.; O’Connor, G.M.
2013-01-01
The upsurge in the number of thin film products has encouraged studies into every aspect of their fabrication and application. An additional source of industrial interest is the laser ablation of thin films to generate nanoparticles. This technique offers advantages over other fabrication methods, as no chemical pre-cursers are required, thereby giving rise to a pure product. The main disadvantage lies in the difficulty with controlling the size of the nanoparticles. This study aims to clarify the influence of the microstructure of a thin film on its optical properties and also to establish the size relationship between the film grain and the nanoparticles generated during laser ablation. A comprehensive sample set of Gold (Au) films with different grain sizes was achieved using different deposition rates, temperatures, film thicknesses (<100 nm) and substrates: Silica, Quartz and Sapphire. The microstructure of each film was analyzed using Atomic Force Microscopy (AFM). Single femtosecond laser pulses, above the ablation threshold fluence of each film, were applied to generate nanoparticles. Scanning Electron Microscopy (SEM) was used to image the re-deposited nanoparticles, from which the nanoparticle size distribution was established. Results confirm that the film microstructure is directly linked to the nanoparticles generated during laser ablation.
Energy Technology Data Exchange (ETDEWEB)
Haustrup, N., E-mail: natalie.haustrup@nuigalway.ie [National Centre for Laser Applications, School of Physics, National University of Ireland, Galway (Ireland); O’Connor, G.M. [National Centre for Laser Applications, School of Physics, National University of Ireland, Galway (Ireland)
2013-08-01
The upsurge in the number of thin film products has encouraged studies into every aspect of their fabrication and application. An additional source of industrial interest is the laser ablation of thin films to generate nanoparticles. This technique offers advantages over other fabrication methods, as no chemical pre-cursers are required, thereby giving rise to a pure product. The main disadvantage lies in the difficulty with controlling the size of the nanoparticles. This study aims to clarify the influence of the microstructure of a thin film on its optical properties and also to establish the size relationship between the film grain and the nanoparticles generated during laser ablation. A comprehensive sample set of Gold (Au) films with different grain sizes was achieved using different deposition rates, temperatures, film thicknesses (<100 nm) and substrates: Silica, Quartz and Sapphire. The microstructure of each film was analyzed using Atomic Force Microscopy (AFM). Single femtosecond laser pulses, above the ablation threshold fluence of each film, were applied to generate nanoparticles. Scanning Electron Microscopy (SEM) was used to image the re-deposited nanoparticles, from which the nanoparticle size distribution was established. Results confirm that the film microstructure is directly linked to the nanoparticles generated during laser ablation.
Near band edge emission characteristics of sputtered nano-crystalline ZnO films
International Nuclear Information System (INIS)
Kunj, Saurabh; Sreenivas, K.
2016-01-01
Sputtered zinc oxide (ZnO) thin films deposited on unheated glass substrate under different sputtering gas mixtures (Ar+O_2) have been investigated using X-ray diffraction and photo luminescence spectroscopy. Earlier reported studies on ZnO films prepared by different techniques exhibit either a sharp/broad near band edge (NBE) emission peak depending on the crystalline quality of the film. In the present study zinc oxide films, grown on unheated substrates, are seen to possess a preferred (002) orientation with a microstructure consisting of clustered nano-sized crystallites. The splitting in the near band edge emission (NBE) into three characteristic peaks is attributed to quantum confinement effect, and is observed specifically under an excitation of 270 nm. Deep level emission (DLE) in the range 400 to 700 nm is not observed indicating absence of deep level radiative defects.
Near band edge emission characteristics of sputtered nano-crystalline ZnO films
Kunj, Saurabh; Sreenivas, K.
2016-05-01
Sputtered zinc oxide (ZnO) thin films deposited on unheated glass substrate under different sputtering gas mixtures (Ar+O2) have been investigated using X-ray diffraction and photo luminescence spectroscopy. Earlier reported studies on ZnO films prepared by different techniques exhibit either a sharp/broad near band edge (NBE) emission peak depending on the crystalline quality of the film. In the present study zinc oxide films, grown on unheated substrates, are seen to possess a preferred (002) orientation with a microstructure consisting of clustered nano-sized crystallites. The splitting in the near band edge emission (NBE) into three characteristic peaks is attributed to quantum confinement effect, and is observed specifically under an excitation of 270 nm. Deep level emission (DLE) in the range 400 to 700 nm is not observed indicating absence of deep level radiative defects.
Near band edge emission characteristics of sputtered nano-crystalline ZnO films
Energy Technology Data Exchange (ETDEWEB)
Kunj, Saurabh; Sreenivas, K. [Department of Physics & Astrophysics, University of Delhi, Delhi 110007 INDIA (India)
2016-05-06
Sputtered zinc oxide (ZnO) thin films deposited on unheated glass substrate under different sputtering gas mixtures (Ar+O{sub 2}) have been investigated using X-ray diffraction and photo luminescence spectroscopy. Earlier reported studies on ZnO films prepared by different techniques exhibit either a sharp/broad near band edge (NBE) emission peak depending on the crystalline quality of the film. In the present study zinc oxide films, grown on unheated substrates, are seen to possess a preferred (002) orientation with a microstructure consisting of clustered nano-sized crystallites. The splitting in the near band edge emission (NBE) into three characteristic peaks is attributed to quantum confinement effect, and is observed specifically under an excitation of 270 nm. Deep level emission (DLE) in the range 400 to 700 nm is not observed indicating absence of deep level radiative defects.
International Nuclear Information System (INIS)
Logan, H.; Daly, L.; Masterson, J.
1989-01-01
T-grain film is claimed to give significantly improved image quality, allowing use of faster screens without loss of quality, thus reducing radiation dose. We tested this claim for two systems. In each case comparison was made with our usual screen-film combination, Agfa Curix RP1 film with Kodak Xomatic Regular screens (a nominally 200 speed system). The systems tested were Kodak TMatG in Kodak Lanex Medium screens (300 speed) and Agfa STG in Kodak Lanex Regular screens (400 speed). The Agfa STG-Lanex Regular system performed less well than the standard system for intravenous pyelograms (IVPs), bones and soft-tissue detail. Its speed advantage was not apparent below 70 kV. The Kodak TMatG-Lanex Medium system was better than the standard system for IVPs but not as good for bones. It gave virtually no speed advantage below 90 kV. Kodak T-grain film in a medium-speed, rare-earth screen was found to be better than the standard system for IVPs. Agfa T-grain film in a fast rare-earth screen was unsatisfactory for IVPs. Neither combination was as good as the standard system for bones. (author)
International Nuclear Information System (INIS)
Shakibi Nia, N.; Savall, C.; Creus, J.; Bourgon, J.; Girault, P.; Metsue, A.; Cohendoz, S.; Feaugas, X.
2016-01-01
Nano-crystalline nickel-tungsten alloys are investigated in order to provide evidence of the contribution of the solute content (light elements and tungsten) and grain-boundaries on hardness. For this purpose, Ni-W alloys were elaborated by electrodeposition in an additive free citrate ammonium bath. The variation of electrodeposition conditions leads to W contents up to 18 at%, with a broad range of grain sizes (5–650 nm). The incorporation of light elements (H, O, C, N) depends on the deposition applied conditions and a progressive modification of the texture is observed with the following sequence: {110}, NT (Non-Textured) and {111} textures. We show that the Hall-Petch relationship for these alloys is influenced by the presence of light elements, the nature of the crystallographic texture and the grain boundaries character. The dependence of grain size on flow stress is a direct consequence of the solute content (solute strengthening) and the evolution of the internal stresses with grain size. To explain the experimental data, two competing physical mechanisms are suggested: grain boundary shearing and dislocation emission at grain boundary, which are affected by the nature of the grain boundary and the solute content.
Energy Technology Data Exchange (ETDEWEB)
Shakibi Nia, N., E-mail: Niusha.Shakibi-Nia@uibk.ac.at [LaSIE (UMR 7356) CNRS, Université de La Rochelle, Av. Michel Crépeau, F-17000, La Rochelle (France); Savall, C.; Creus, J. [LaSIE (UMR 7356) CNRS, Université de La Rochelle, Av. Michel Crépeau, F-17000, La Rochelle (France); Bourgon, J. [ICMPE (UMR 7182) CNRS-UPEC, Université Paris Est, 2-8 rue Henri Dunant, F-94320, Thiais (France); Girault, P.; Metsue, A.; Cohendoz, S.; Feaugas, X. [LaSIE (UMR 7356) CNRS, Université de La Rochelle, Av. Michel Crépeau, F-17000, La Rochelle (France)
2016-12-15
Nano-crystalline nickel-tungsten alloys are investigated in order to provide evidence of the contribution of the solute content (light elements and tungsten) and grain-boundaries on hardness. For this purpose, Ni-W alloys were elaborated by electrodeposition in an additive free citrate ammonium bath. The variation of electrodeposition conditions leads to W contents up to 18 at%, with a broad range of grain sizes (5–650 nm). The incorporation of light elements (H, O, C, N) depends on the deposition applied conditions and a progressive modification of the texture is observed with the following sequence: {110}, NT (Non-Textured) and {111} textures. We show that the Hall-Petch relationship for these alloys is influenced by the presence of light elements, the nature of the crystallographic texture and the grain boundaries character. The dependence of grain size on flow stress is a direct consequence of the solute content (solute strengthening) and the evolution of the internal stresses with grain size. To explain the experimental data, two competing physical mechanisms are suggested: grain boundary shearing and dislocation emission at grain boundary, which are affected by the nature of the grain boundary and the solute content.
International Nuclear Information System (INIS)
Lu, Yuming; Cai, Shuang; Liang, Ying; Bai, Chuanyi; Liu, Zhiyong; Guo, Yanqun; Cai, Chuanbing
2015-01-01
Highlights: • Crack-free CeO 2 film thicker than 200 nm was prepared on NiW substrate by ED method. • Different electrochemical processes as hydroxide/metal mechanisms were identified. • The CeO 2 precursor films deposited by ED method were in nano-scales. - Abstract: Comparing with conventional physical vapor deposition methods, electrochemistry deposition technique shows a crack suppression effect by which the thickness of CeO 2 films on Ni–5 at.%W substrate can reach a high value up to 200 nm without any cracks, make it a potential single buffer layer for coated conductor. In the present work, the processes of CeO 2 film deposited by electrochemistry method are detailed investigated. A hydroxide reactive mechanism and an oxide reactive mechanism are distinguished for dimethyl sulfoxide and aqueous solution, respectively. Before heat treatment to achieve the required bi-axial texture performance of buffer layers, the precursor CeO 2 films are identified in nanometer scales. The crack suppression for electrochemistry deposited CeO 2 films is believed to be attributed to the nano-effects of the precursors
International Nuclear Information System (INIS)
Valalaki, K; Nassiopoulou, A G; Vouroutzis, N
2016-01-01
The thermoelectric properties of p-type polycrystalline silicon thin films deposited by low pressure chemical vapour deposition (LPCVD) were accurately determined at room temperature and the thermoelectric figure of merit was deduced as a function of film thickness, ranging from 100 to 500 nm. The effect of film thickness on their thermoelectric performance is discussed. More than threefold increase in the thermoelectric figure of merit of the 100 nm thick polysilicon film was observed compared to the 500 nm thick film, reaching a value as high as 0.033. This enhancement is mainly the result of the smaller grain size in the thinner films. With the decrease in grain size the resistivity of the films is increased twofold and electrical conductivity decreased, however the Seebeck coefficient is increased by 30% and the thermal conductivity is decreased eightfold, being mainly at the origin of the increased figure of merit of the 100 nm film. Our experimental results were compared to known theoretical models and the possible mechanisms involved are presented and discussed. (paper)
Transparent and conductive electrodes by large-scale nano-structuring of noble metal thin-films
DEFF Research Database (Denmark)
Linnet, Jes; Runge Walther, Anders; Wolff, Christian
2018-01-01
grid, and nano-wire thin-films. The indium and carbon films do not match the chemical stability nor the electrical performance of the noble metals, and many metal films are not uniform in material distribution leading to significant surface roughness and randomized transmission haze. We demonstrate...... solution-processed masks for physical vapor-deposited metal electrodes consisting of hexagonally ordered aperture arrays with scalable aperture-size and spacing in an otherwise homogeneous noble metal thin-film that may exhibit better electrical performance than carbon nanotube-based thin-films...... for equivalent optical transparency. The fabricated electrodes are characterized optically and electrically by measuring transmittance and sheet resistance. The presented methods yield large-scale reproducible results. Experimentally realized thin-films with very low sheet resistance, Rsh = 2.01 ± 0.14 Ω...
Preparation of biomimetic nano-structured films with multi-scale roughness
Shelemin, A.; Nikitin, D.; Choukourov, A.; Kylián, O.; Kousal, J.; Khalakhan, I.; Melnichuk, I.; Slavínská, D.; Biederman, H.
2016-06-01
Biomimetic nano-structured films are valuable materials in various applications. In this study we introduce a fully vacuum-based approach for fabrication of such films. The method combines deposition of nanoparticles (NPs) by gas aggregation source and deposition of overcoat thin film that fixes the nanoparticles on a surface. This leads to the formation of nanorough surfaces which, depending on the chemical nature of the overcoat, may range from superhydrophilic to superhydrophobic. In addition, it is shown that by proper adjustment of the amount of NPs it is possible to tailor adhesive force on superhydrophobic surfaces. Finally, the possibility to produce NPs in a wide range of their size (45-240 nm in this study) makes it possible to produce surfaces not only with single scale roughness, but also with bi-modal or even multi-modal character. Such surfaces were found to be superhydrophobic with negligible water contact angle hysteresis and hence truly slippery.
Preparation of biomimetic nano-structured films with multi-scale roughness
International Nuclear Information System (INIS)
Shelemin, A; Nikitin, D; Choukourov, A; Kylián, O; Kousal, J; Khalakhan, I; Melnichuk, I; Slavínská, D; Biederman, H
2016-01-01
Biomimetic nano-structured films are valuable materials in various applications. In this study we introduce a fully vacuum-based approach for fabrication of such films. The method combines deposition of nanoparticles (NPs) by gas aggregation source and deposition of overcoat thin film that fixes the nanoparticles on a surface. This leads to the formation of nanorough surfaces which, depending on the chemical nature of the overcoat, may range from superhydrophilic to superhydrophobic. In addition, it is shown that by proper adjustment of the amount of NPs it is possible to tailor adhesive force on superhydrophobic surfaces. Finally, the possibility to produce NPs in a wide range of their size (45–240 nm in this study) makes it possible to produce surfaces not only with single scale roughness, but also with bi-modal or even multi-modal character. Such surfaces were found to be superhydrophobic with negligible water contact angle hysteresis and hence truly slippery. (paper)
Precipitation formation in recrystallized nickel-plated non-sag tungsten wire
International Nuclear Information System (INIS)
Lai, Z.H.
1994-01-01
It is well established that some metals, such as palladium and nickel, can easily penetrate into tungsten by fast diffusion via crystal defects such as grain boundaries and dislocations. As a result of the fast penetration of these so called activators the recrystallization temperature of heavily drawn non-sag tungsten wire can be lower from about 2,000 C to about 1,000 C, thus the application of the tungsten wire, serving as reinforcement material in metal matrix composites used at high temperatures, is limited. An interesting question is in which form these activators exist in the recrystallized tungsten wire. It is generally believed that W-Ni intermediate compounds could form in the recrystallized material, presumably at grain boundaries. The free energy difference between the pure tungsten fibbers and the precipitating W(Ni) solid solution was suggested as the chemical driving force which governed the recrystallization process. The presence of nickel in small particles had also been observed in recrystallized grains of nickel plated tungsten wires using scanning electron microscopy (SEM) and secondary ion mass spectroscopy. These particles were considered to be nickel rich precipitates. However, a detailed investigation of the precipitation process has not been reported. In the present work an investigation of the structure, composition and distribution of nickel rich particles precipitated in recrystallized grains of nickel plated heavily drawn non-sage tungsten wires was carried out using analytical electron microscopy (AEM)
Abdalla, Soliman; Al-Marzouki, Fahad; Obaid, Abdullah; Gamal, Salah
2016-01-01
Nano-composite films have been the subject of extensive work for developing the energy-storage efficiency of electrostatic capacitors. Factors such as polymer purity, nanoparticle size, and film morphology drastically affect the electrostatic efficiency of the dielectric material that forms the insulating film between the conductive electrodes of a capacitor. This in turn affects the energy storage performance of the capacitor. In the present work, we have studied the dielectric properties of...
International Nuclear Information System (INIS)
Deshmukh, S.B.; Bari, R.H.; Jain, G.H.
2013-01-01
In present work the nano-structured pure ZrO 2 thin films were prepared using spray pyrolysis techniques. The aqueous solution of ZrCl 4 , was used as a precursor with flow rate controlled 5 mI/min. The films were synthesized on glass substrate between temperature 250-400℃ and subjected to different analytical characterization like SEM, XRD, TEM, FTIR, UV, TGA-DTA/DSC. The gas sensing performances of various gases were tested in different operating temperature range. The sensitivity, selectivity, response and recovery time for H 2 S gas was discussed. Also nano structured grain size discussed. (author)
Multiple oxide content media for columnar grain growth in L10 FePt thin films
International Nuclear Information System (INIS)
Ho, Hoan; Yang, En; Laughlin, David E.; Zhu, Jian-Gang
2013-01-01
An approach to enhance the height-to-diameter ratio of FePt grains in heat-assisted magnetic recording media is proposed. The FePt-SiO x thin films are deposited with a decrease of the SiO x percentage along the film growth direction. When bi-layer and tri-layer media are sputtered at 410 °C, we observe discontinuities in the FePt grains at interfaces between layers, which lead to poor epitaxial growth. Due to increased atomic diffusion, the bi-layer media sputtered at 450 °C is shown to (1) grow into continuous columnar grains with similar size as single-layer media but much higher aspect ratio, (2) have better L1 0 ordering and larger coercivity.
Migration of liquid film and grain boundary in Mo-Ni induced by W diffusion
International Nuclear Information System (INIS)
Kang, H.K.; Hackney, S.; Yoon, D.N.
1988-01-01
The liquid films and grain boundaries in liquid phase sintered Mo-Ni alloy are observed to migrate during heat-treatment after adding W to the liquid matrix. Behind the migrating boundaries forms Mo-Ni-W solid solution with the W concentration decreasing with the migration distance because of W depletion in the liquid matrix. The migration rate during the heat-treatment at 1540 0 C after adding W decreases with the decreasing pretreatment sintering temperature. When the sintering temperature is 1420 0 C, the migration rate is almost reduced to O. Under this condition, the coherency strain due to the simultaneous diffusion of W and Ni into the grain surfaces is estimated to be almost O. The results thus show that the coherency strain due to lattice diffusion is the driving force for the liquid film and grain boundary migration
Grain boundary structures in La2/3Ca1/3MnO3 thin films
International Nuclear Information System (INIS)
Miller, D. J.; Lin, Y.-K.; Vlasko-Vlasov, V.; Welp, U.
1999-01-01
As with many other oxide-based compounds that exhibit electronic behavior, structural defects have a strong influence on the electronic properties of the CMR manganites. In this work, the authors have studied the effect of grain boundaries on the transport properties and on the local orientation of magnetization. Thin films of the perovskite-related La 2/3 Ca 1/3 MnO 3 compound were deposited onto bicrystal substrates using pulsed laser deposition. Transport measurements showed some enhancement of magnetoresistance across the grain boundary. The structure of the boundary was evaluated by electron microscopy. In contrast with the highly meandering boundaries typically observed in bicrystals of high temperature superconductors, the boundaries in these films are relatively straight and well defined. However, magneto-optical imaging showed that the local magnetization was oriented out of the plane at the grain boundary while it was oriented within the plane in the grains on either side. This coordinated reorientation of local magnetization near the grain boundary leads to enhanced magnetoresistance across the boundary in low fields
Wrinkling of flexoelectric nano-film/substrate systems
Su, Shengkai; Huang, Huaiwei; Liu, Yijie; Zhu, Zheng H.
2018-02-01
The study of wrinkling mechanisms essentially helps to establish stable and controllable performance in electronic products. To gain some basic understanding of the wrinkling process in flexoelectric dielectrics, this paper models the wrinkling of nano-film/substrate systems, typically seen in stretchable electronics, subjected to substrate prestrain and voltage loading on electrodes. Flexoelectricity is considered through the constitutive equations proposed by Shen and Hu, and Euler-Bernoulli beam theory is applied to formulate the expressions of wrinkling wavelength and amplitude through the Ritz method. The effects of flexoelectricity, surface parameters, prestrain, applied voltage, structural scale etc on wrinkling behaviors, including wrinkling deformation and the wrinkling critical condition, are discussed. Results reveal that the action of both flexoelectric and surface effects is significant over only a small scale range, with film thickness less than 10 nm. Alongside these issues, the fundamental difference between flexoelectric and piezoelectric effects on wrinkling behaviors is highlighted. Piezoelectricity may act as a promoter or suppressor of wrinkling initiation and amplitude, depending on the applied voltage, while flexoelectricity not only reduces the critical prestrain or voltage required for wrinkling, but also decreases the wrinkling wavelength and amplitude.
Energy Technology Data Exchange (ETDEWEB)
Jamshidian, M., E-mail: jamshidian@cc.iut.ac.ir [Department of Mechanical Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Institute of Structural Mechanics, Bauhaus-University Weimar, Marienstrasse 15, 99423 Weimar (Germany); Thamburaja, P., E-mail: prakash.thamburaja@gmail.com [Department of Mechanical & Materials Engineering, Universiti Kebangsaan Malaysia (UKM), Bangi 43600 (Malaysia); Rabczuk, T., E-mail: timon.rabczuk@tdt.edu.vn [Division of Computational Mechanics, Ton Duc Thang University, Ho Chi Minh City (Viet Nam); Faculty of Civil Engineering, Ton Duc Thang University, Ho Chi Minh City (Viet Nam)
2016-12-15
A previously-developed finite-deformation- and crystal-elasticity-based constitutive theory for stressed grain growth in cubic polycrystalline bodies has been augmented to include a description of excess surface energy and grain-growth stagnation mechanisms through the use of surface effect state variables in a thermodynamically-consistent manner. The constitutive theory was also implemented into a multiscale coupled finite-element and phase-field computational framework. With the material parameters in the constitutive theory suitably calibrated, our three-dimensional numerical simulations show that the constitutive model is able to accurately predict the experimentally-determined evolution of crystallographic texture and grain size statistics in polycrystalline copper thin films deposited on polyimide substrate and annealed at high-homologous temperatures. In particular, our numerical analyses show that the broad texture transition observed in the annealing experiments of polycrystalline thin films is caused by grain growth stagnation mechanisms. - Graphical abstract: - Highlights: • Developing a theory for stressed grain growth in polycrystalline thin films. • Implementation into a multiscale coupled finite-element and phase-field framework. • Quantitative reproduction of the experimental grain growth data by simulations. • Revealing the cause of texture transition to be due to the stagnation mechanisms.
Microwave dielectric properties of nanostructured nickel ferrite
Indian Academy of Sciences (India)
Wintec
Abstract. Nickel ferrite is one of the important ferrites used in microwave devices. In the present work, we have synthesized nanoparticles of nickel ferrite using chemical precipitation technique. The crystal structure and grain size of the particles are studied using XRD. The microwave dielectric properties of nanostructured.
Chhetri, Nikita; Chatterjee, Somenath
2018-01-01
Solar cells/photovoltaic, a renewable energy source, is appraised to be the most effective alternative to the conventional electrical energy generator. A cost-effective alternative of crystalline wafer-based solar cell is thin-film polycrystalline-based solar cell. This paper reports the numerical analysis of dependency of the solar cell parameters (i.e., efficiency, fill factor, open-circuit voltage and short-circuit current density) on grain size for thin-film-based polycrystalline silicon (Si) solar cells. A minority carrier lifetime model is proposed to do a correlation between the grains, grain boundaries and lifetime for thin-film-based polycrystalline Si solar cells in MATLAB environment. As observed, the increment in the grain size diameter results in increase in minority carrier lifetime in polycrystalline Si thin film. A non-equivalent series resistance double-diode model is used to find the dark as well as light (AM1.5) current-voltage (I-V) characteristics for thin-film-based polycrystalline Si solar cells. To optimize the effectiveness of the proposed model, a successive approximation method is used and the corresponding fitting parameters are obtained. The model is validated with the experimentally obtained results reported elsewhere. The experimentally reported solar cell parameters can be found using the proposed model described here.
Biofouling of Cr-Nickel Spray Coated Films on Steel Surfaces
International Nuclear Information System (INIS)
Yoshida, Kento; Kanematsu, Hideyuki; Kuroda, Daisuke; Ikigai, Hajime; Kogo, Takeshi; Yokoyama, Seiji
2012-01-01
Nowadays, corrosion of metals brings us serious economic loss and it often reaches several percentage of GNP. Particularly the marine corrosion was serious and the counter measure was very hard to be established, since the number of factors is huge and complicated. One of the complicated factors in marine corrosion is biofouling. Biofouling was classified into two main categories, microfouling and macrofouling. The former is composed of biofilm formation mainly. Marine bacteria are attached to material surfaces, seeking for nutrition in oligotrophic environment and they excrete polysaccharide to form biofilm on metal surfaces. Then larger living matters are attached on the biofilms to develop biofouling on metal surfaces, which often lead loss and failures of metals in marine environments. From the viewpoint of corrosion protection and maintenance of marine structures, biofouling should be mitigated as much as possible. In this study, we applied spray coating to steels and investigated if chromium-nickel spray coating could mitigate the biofouling, being compared with the conventional aluminium-zinc spray coating in marine environments. The specimens used for this investigation are aluminium, zinc, aluminium-zinc, stacked chromium/nickel and those films were formed on carbon steel (JIS SS400). And the pores formed by spray coating were sealed by a commercial reagent for some specimens. All of those specimens were immersed into sea water located at Marina Kawage (854-3, Chisato, Tsu, Mie Prefecture) in Ise Bay for two weeks. The depth of the specimen was two meter from sea water surface and the distance was always kept constant, since they were suspended from the floating pier. The temperature in sea water changed from 10 to 15 degrees Celsius during the immersion test. The biofouling behavior was investigated by low vacuum SEM (Hitachi Miniscope TM1000) and X-ray fluorescent analysis. When the spray coated specimens with and without sealing agents were compared
Dewetting of nickel oxide-films on silicon under swift heavy ion irradiation
International Nuclear Information System (INIS)
Bolse, Thunu; Elsanousi, Ammar; Paulus, Hartmut; Bolse, Wolfgang
2006-01-01
Dewetting, occurring when a thin film on a non-wettable substrate turns into its liquid state, has gained strong interest during the last decade, since it results in nano-scale, large-area covering pattern formation. Recently we found that swift heavy ion (SHI) irradiation of thin NiO films on Si substrates at 80 K results in similar dewetting pattern, although in this case the coating has never reached its melting point. Careful inspection of the SEM images clearly revealed that the same nucleation mechanisms as observed for molten polymer films on Si (heterogeneous and homogeneous nucleation) were active. AFM shows that the circular holes formed in the early stages of the dewetting process exhibit a high and asymmetric rim-structure. RBS analysis was used to measure the coverage of the surface by the oxide films and revealed that the holes grow at constant velocity. This, and the shape of the rims, indicate that the material removed from the substrate surface piles up by plastic deformation, which points at a balance of the capillary driving forces and the hindered material dissipation
Development of nano-sized {alpha}-Al{sub 2}O{sub 3}:C films for application in digital radiology
Energy Technology Data Exchange (ETDEWEB)
Silva, Edna C., E-mail: edca@cdtn.b [Universidade Federal de Minas Gerais (DEN/UFMG), Belo Horizonte (Brazil). Dept. de Engenharia Nuclear; Fontainha, Crissia C. [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte (Brazil). Dept. de Propedeutica Complemetar; Oliveira, Vitor H.; Ferraz, Wilmar B.; Faria, Luiz O. [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)
2011-07-01
Ceramic materials are widely used as sensors for ionizing radiation. In nuclear applications, the alpha-alumina doped with carbon ({alpha}-Al{sub 2}O{sub 3}:C) is the most widely ceramic used because of its excellent optically stimulated luminescence (OSL) and thermoluminescent (TL) properties applied to detection of ionizing radiation. Another application of OSL and TL materials are in Digital Radiography, with ceramic/polymeric film composites. Recently, Computed Radiography (CR) devices based on OSL materials are replacing the old conventional film radiography. In this study we investigate the thermoluminescence of nano-sized {alpha}-Al{sub 2}O{sub 3} samples doped with different percentages of carbon, sintered in reducing atmospheres at temperatures ranging from 1300 to 1750 deg C. The results indicate that the nano-sized {alpha}-Al{sub 2}O{sub 3}:C materials have a luminescent response that could be due to both OSL and RPL properties, but without application to radiation dosimetry. Moreover, the results indicate that micro-sized {alpha}-Al{sub 2}O{sub 3}:C, doped with 0.5% carbon, and nano-sized ones doped with 2% of carbon, present thermoluminescent signal around 30 to 100 times the TL output signal of commercial TLD-100, the most used TL dosimeter in the world. The results indicate that these ceramic nano-particles have great potential for use in Digital Radiography based on thermoluminescent film imaging, being able to provide image resolutions much higher than the micro-sized {alpha}-Al{sub 2}O{sub 3}:C, in view of their improved resolution provided by nano-particulates. (author)
Effects of array arrangements in nano-patterned thin film media
International Nuclear Information System (INIS)
El-Hilo, M.
2010-01-01
In this work, the effect of different arrays arrangements on the magnetic behaviour of patterned thin film media is simulated. The modeled films consist of 80x80 cobalt grains of uniform diameter (20 nm) distributed into two different array arrangement: hexagonal (triangular) or square arrays. In addition to that, for each array arrangement, two cases of anisotropy orientations, random and textured films are considered. For both array arrangements and media orientations, hysteresis loops at different array separation (d) were simulated. Predictions show that for closely packed films, the shearing effects on the magnetization loop are much larger for the square array arrangement than the hexagonal one. According to these predictions, the bit switching field distribution in interacting 2D systems is much narrower for the hexagonal array arrangement. This result could be very important for high-density magnetic recording where a narrow bit switching field distribution is required.
The Effect of Drawing Ratio on Mechanical Property of Nano-Hybrid Polyimide Composite Films
CHEN Hao; YANG Rui-xiao; WU Chuan-gang; FAN Yong
2017-01-01
In order to investigate the impact of drawing ratio of inorganic nano-hybrid polyamide three-layer composite films,the stretched composite films with different draw ratio were prepared by drawing partial imido polyamide film and then through the ring closing reaction in the high temperature,and the draw ratio was 0% ,2% , 4% ,6% ,8% ,10% ,12% ,14% etc. Under the same conditions,we made different draw ratio of three-layer composite film tensile test with the electronic universal material testi...
Research on the combustion properties of propellants with low content of nano metal powders
Energy Technology Data Exchange (ETDEWEB)
Zhi, Jiang; Shu-Fen, Li [Department of Chemical Physics, University of Science and Technology of China, Hefei 230026 (China); Feng-Qi, Zhao; Zi-Ru, Liu; Cui-Mei, Yin; Yang, Luo; Shang-Wen, Li [Xi' an Modern Chemistry Research Inst., Xi' an 710065 (China)
2006-04-15
A comparison of various experimental results for combustionrelated properties evaluation, including burning rates, deflagration heat, flame structures and thermal decomposition properties, of AP/RDX/Al/HTPB composite propellants containing nano metal powders is presented. The thermal behavior of n-Al (nano grain size aluminum) and g-Al (general grain size aluminum i.e., 10 {mu}m) heated in air was also investigated by thermogravimetry. The burning rates results indicate that the usage of bimodal aluminum distribution with the ratio around 4: 1 of n-Al to g-Al or the addition of 2% nano nickel powders (n-Ni) will improve the burning behavior of the propellant, while the usage of grading aluminum powders with the ratio 1: 1 of n-Al to g-Al will impair the combustion of the propellant. Results show that n-Al and n-Ni both have a lower heating capacity, lower ignition threshold and shorter combustion time than g-Al. In addition n-Al is inclined to burn in single particle form. And the thermal analysis results show that n-Ni can catalyze the thermal decomposition of AP in the propellant. The results also confirm the high reactivity of n-Al, which will lead to a lower reaction temperature and rather higher degree of reaction ratio as compared with g-Al in air. All these factors will influence the combustion of propellants. (Abstract Copyright [2006], Wiley Periodicals, Inc.)
Selective Photophysical Modification on Light-Emitting Polymer Films for Micro- and Nano-Patterning
Directory of Open Access Journals (Sweden)
Xinping Zhang
2016-02-01
Full Text Available Laser-induced cross-linking in polymeric semiconductors was utilized to achieve micro- and nano-structuring in thin films. Single- and two-photon cross-linking processes led to the reduction in both the refractive index and thickness of the polymer films. The resultant photonic structures combine the features of both relief- and phase-gratings. Selective cross-linking in polymer blend films based on different optical response of different molecular phases enabled “solidification” of the phase-separation scheme, providing a stable template for further photonic structuring. Dielectric and metallic structures are demonstrated for the fabrication methods using cross-linking in polymer films. Selective cross-linking enables direct patterning into polymer films without introducing additional fabrication procedures or additional materials. The diffraction processes of the emission of the patterned polymeric semiconductors may provide enhanced output coupling for light-emitting diodes or distributed feedback for lasers.
International Nuclear Information System (INIS)
Góral, Anna; Nowak, Marek; Berent, Katarzyna; Kania, Bogusz
2014-01-01
Highlights: • Current density of the electrodeposition affects the incorporation of Al 2 O 3 in Ni matrix. • Ni/Al 2 O 3 composite coatings exhibit changes in crystallographic texture. • The pitting corrosion effects were observed in Ni/Al 2 O 3 coatings. • Residual stresses were decreased with increasing current density and coating thickness. - Abstract: Electrodeposition process is a very promising method for producing metal matrix composites reinforced with ceramic particles. In this method insoluble particles suspended in an electrolytic bath are embedded in a growing metal layer. This paper is focused on the investigations of the nickel matrix nanocomposite coatings with hard α-Al 2 O 3 nano-particles, electrochemically deposited from modified Watts-type baths on steel substrates. The influence of various current densities on the microstructure, residual stresses, texture, hardness and corrosion resistance of the deposited nickel/alumina coatings was investigated. The surface morphology, cross sections of the coatings and distribution of the ceramic particles in the metal matrix were examined by scanning electron microscopy. The phase composition, residual stresses and preferred grain orientation of the coatings were characterized using X-ray diffraction techniques. The coating morphology revealed that α-Al 2 O 3 particles show a distinct tendency to form agglomerates, approximately uniformly distributed into the nickel matrix
Grain size increase in pentacene thin films prepared in low-pressure gas ambient
International Nuclear Information System (INIS)
Yokoyama, Takamichi; Park, Chang Bum; Nagashio, Kosuke; Kita, Koji; Toriumi, Akira
2009-01-01
We studied a mechanism of grain size increase (that is, island density decrease) in pentacene film prepared in hydrogen (H 2 ) ambient. The island densities of pentacene films prepared in helium and deuterium were lower than those of vacuum-deposited films. This indicates that the decrease in the island density was not due to the chemical interaction between H 2 and pentacene or the substrate surface. Furthermore, the temperature dependence of the island density indicates that there is no difference in the surface diffusion energy in a vacuum and in H 2 . We also improved mobility significantly in the pentacene thin film transistor fabricated on film grown in H 2 ambient on a chemically treated substrate.
The study on corrosion resistance of decorative satin nickel plating
Directory of Open Access Journals (Sweden)
LU Wenya
2012-10-01
Full Text Available This study examined the corrosion resistance of satin nickel plating on conductive plastic.The electrochemical tests were to analyze the corrosion behavior of satin nickel plating with different processes in 3.5% NaCl solution.The results show that,because the satin nickel plating has an organic film on its surface due to process characteristics,the film results in different corrosion resistance.By increasing satin additive dosage,the nickel plating chroma decreases,the microsurface of the plating becomes rough,and the corrosion resistance is followed by decrease.
Wu, Mao-Sung; Wang, Min-Jyle
2010-10-07
Nickel oxide film with open macropores prepared by anodic deposition in the presence of surfactant shows a very high capacitance of 1110 F g(-1) at a scan rate of 10 mV s(-1), and the capacitance value reduces to 950 F g(-1) at a high scan rate of 200 mV s(-1).
Directory of Open Access Journals (Sweden)
Jing Chen
2015-08-01
Full Text Available The surface acoustic wave (SAW propagating characteristics of Y-cut nano LiNbO3 (LN film on SiO2/LN substrate have been theoretically calculated. The simulated results showed a shear horizontal (SH SAW with enhanced electromechanical coupling factor K2 owing to a dimensional effect of the nanoscale LN film. However, a Rayleigh SAW and two other resonances related to thickness vibrations caused spurious responses for wideband SAW devices. These spurious waves could be fully suppressed by properly controlling structural parameters including the electrode layer height, thickness, and the Euler angle (θ of the LN thin film. Finally, a pure SH SAW was obtained with a wide θ range, from 0° to 5° and 165° to 180°. The largest K2 achieved for the pure SH SAW was about 35.1%. The calculated results demonstrate the promising application of nano LN film to the realization of ultra-wideband SAW devices.
Energy Technology Data Exchange (ETDEWEB)
Chen, Jing, E-mail: jingchen0408@hotmail.com; Zhang, Qiaozhen; Han, Tao; Zhou, Liu; Tang, Gongbin; Liu, Boquan; Ji, Xiaojun [Department of Instrument Science and Engineering, Shanghai Jiaotong University, Shanghai 200240 (China)
2015-08-15
The surface acoustic wave (SAW) propagating characteristics of Y-cut nano LiNbO{sub 3} (LN) film on SiO{sub 2}/LN substrate have been theoretically calculated. The simulated results showed a shear horizontal (SH) SAW with enhanced electromechanical coupling factor K{sup 2} owing to a dimensional effect of the nanoscale LN film. However, a Rayleigh SAW and two other resonances related to thickness vibrations caused spurious responses for wideband SAW devices. These spurious waves could be fully suppressed by properly controlling structural parameters including the electrode layer height, thickness, and the Euler angle (θ) of the LN thin film. Finally, a pure SH SAW was obtained with a wide θ range, from 0° to 5° and 165° to 180°. The largest K{sup 2} achieved for the pure SH SAW was about 35.1%. The calculated results demonstrate the promising application of nano LN film to the realization of ultra-wideband SAW devices.
Synthesis of nano-crystalline Zn-Ni alloy coatings by D.C plating
International Nuclear Information System (INIS)
Rizwan, R.; Mehmood, M.; Imran, M.; Akhtar, J.I.
2006-01-01
Nano crystalline Zinc-Nickel Alloy coatings were obtained from additive free chloride bath. The aqueous bath composition was varied from ZnCl/sub 2/ -200 g/l to 50 g/l, NiCI/sub 2/ 6H/sub 2/O -200 g/l to 50 g/l and H/sub 3/BO/sub 3/ -40 g/l. XRD patterns of electrodeposited alloys on copper substrate revealed the presence of gamma (Ni/sub 5/Zn/sub 21/) inter-metallic compound and eta (solid solution of nickel in zinc). The apparent grain size measured from FWHM of XRD reflections was found to be about 20nm- 50nm depending upon deposit composition. Analysis by EDX of deposits confirms the presence of Zn (81 to 94%), and Ni (6-19%) depending upon bath composition and current density applied. With increase in bath temperature deposition and dissolution potentials are shifted to nobler values. The temperature also affects the phase composition of alloy deposited. Cyclic Voltametry was performed on platinum substrate and deposits obtained for short duration exhibit voltamograms that reflects strong dependence of alloy components on solution chemistry during initial stage of deposition. Hence, initial composition of the deposit varies with solution chemistry but composition becomes almost independent of solution chemistry for thick deposits. The grain size of the deposits also depends upon the composition of deposit. (author)
Plasmonic enhancement of UV emission from ZnO thin films induced by Al nano-concave arrays
International Nuclear Information System (INIS)
Norek, Małgorzata; Łuka, Grzegorz; Włodarski, Maksymilian
2016-01-01
Highlights: • Al nano-concave arrays with different interpore distance (D c ) were prepared. • PL of ZnO thin films deposited directly on the Al nano-concaves were studied. • The effect of 10 nm Al 2 O 3 spacer on PL emission from ZnO thin films was analyzed. • Plasmonic enhancement of the PL emission was dependent on the D c and the spacer. • The highest 9-fold enhancement was obtained for the Al/ZnO sample with D c ∼333 nm. - Abstract: Surface plasmons (SPs) supported by Al nano-concave arrays with increasing interpore distance (D c ) were used to enhance the ultraviolet light emission from ZnO thin films. Two sets of samples were prepared: in the first set the thin ZnO films were deposited directly on Al nanoconcaves (the Al/ZnO samples) and in the second set a 10 nm − Al 2 O 3 spacer was placed between the textured Al and the ZnO films (the Al/Al 2 O 3 -ALD/ZnO samples). In the Al/ZnO samples the enhancement was limited by a nonradiative energy dissipation due to the Ohmic loss in the Al metal. However, for the ZnO layer deposited directly on Al nanopits synthesized at 150 V (D c = 333 ± 18 nm), the largest 9-fold enhancement was obtained by achieving the best energy fit between the near band-edge (NBE) emission from ZnO and the λ (0,1) SPP resonance mode. In the Al/Al 2 O 3 -ALD/ZnO samples the amplification of the UV emission was smaller than in the Al/ZnO samples due to a big energy mismatch between the NBE emission and the λ (0,1) plasmonic mode. The results obtained in this work indicate that better tuning of the NBE − λ (0,1) SPP resonance mode coupling is possible through a proper modification of geometrical parameters in the Al/Al 2 O 3 -ALD/ZnO system such as Al nano-concave spacing and the thickness of the corresponding layer. This approach will reduce the negative influence of the non-radiative plasmonic modes and most likely will lead to further enhancement of the SP-modulated UV emission from ZnO thin films.
Plasmonic enhancement of UV emission from ZnO thin films induced by Al nano-concave arrays
Energy Technology Data Exchange (ETDEWEB)
Norek, Małgorzata, E-mail: mnorek@wat.edu.pl [Department of Advanced Materials and Technologies, Faculty of Advanced Technologies and Chemistry, Military University of Technology, Kaliskiego 2, 00-908 Warsaw (Poland); Łuka, Grzegorz [Institute of Physics, Polish Academy of Sciences, al. Lotników 32/46, 02-668 Warsaw (Poland); Włodarski, Maksymilian [Institute of Optoelectronics, Military University of Technology, Str. Kaliskiego 2, 00-908 Warszawa (Poland)
2016-10-30
Highlights: • Al nano-concave arrays with different interpore distance (D{sub c}) were prepared. • PL of ZnO thin films deposited directly on the Al nano-concaves were studied. • The effect of 10 nm Al{sub 2}O{sub 3} spacer on PL emission from ZnO thin films was analyzed. • Plasmonic enhancement of the PL emission was dependent on the D{sub c} and the spacer. • The highest 9-fold enhancement was obtained for the Al/ZnO sample with D{sub c} ∼333 nm. - Abstract: Surface plasmons (SPs) supported by Al nano-concave arrays with increasing interpore distance (D{sub c}) were used to enhance the ultraviolet light emission from ZnO thin films. Two sets of samples were prepared: in the first set the thin ZnO films were deposited directly on Al nanoconcaves (the Al/ZnO samples) and in the second set a 10 nm − Al{sub 2}O{sub 3} spacer was placed between the textured Al and the ZnO films (the Al/Al{sub 2}O{sub 3}-ALD/ZnO samples). In the Al/ZnO samples the enhancement was limited by a nonradiative energy dissipation due to the Ohmic loss in the Al metal. However, for the ZnO layer deposited directly on Al nanopits synthesized at 150 V (D{sub c} = 333 ± 18 nm), the largest 9-fold enhancement was obtained by achieving the best energy fit between the near band-edge (NBE) emission from ZnO and the λ{sub (0,1)} SPP resonance mode. In the Al/Al{sub 2}O{sub 3}-ALD/ZnO samples the amplification of the UV emission was smaller than in the Al/ZnO samples due to a big energy mismatch between the NBE emission and the λ{sub (0,1)} plasmonic mode. The results obtained in this work indicate that better tuning of the NBE − λ{sub (0,1)} SPP resonance mode coupling is possible through a proper modification of geometrical parameters in the Al/Al{sub 2}O{sub 3}-ALD/ZnO system such as Al nano-concave spacing and the thickness of the corresponding layer. This approach will reduce the negative influence of the non-radiative plasmonic modes and most likely will lead to further
Self-Assembled Formation of Well-Aligned Cu-Te Nano-Rods on Heavily Cu-Doped ZnTe Thin Films
Liang, Jing; Cheng, Man Kit; Lai, Ying Hoi; Wei, Guanglu; Yang, Sean Derman; Wang, Gan; Ho, Sut Kam; Tam, Kam Weng; Sou, Iam Keong
2016-11-01
Cu doping of ZnTe, which is an important semiconductor for various optoelectronic applications, has been successfully achieved previously by several techniques. However, besides its electrical transport characteristics, other physical and chemical properties of heavily Cu-doped ZnTe have not been reported. We found an interesting self-assembled formation of crystalline well-aligned Cu-Te nano-rods near the surface of heavily Cu-doped ZnTe thin films grown via the molecular beam epitaxy technique. A phenomenological growth model is presented based on the observed crystallographic morphology and measured chemical composition of the nano-rods using various imaging and chemical analysis techniques. When substitutional doping reaches its limit, the extra Cu atoms favor an up-migration toward the surface, leading to a one-dimensional surface modulation and formation of Cu-Te nano-rods, which explain unusual observations on the reflection high energy electron diffraction patterns and apparent resistivity of these thin films. This study provides an insight into some unexpected chemical reactions involved in the heavily Cu-doped ZnTe thin films, which may be applied to other material systems that contain a dopant having strong reactivity with the host matrix.
Grain boundary diffusion of Dy films prepared by magnetron sputtering for sintered Nd–Fe–B magnets
Chen, W.; Luo, J. M.; Guan, Y. W.; Huang, Y. L.; Chen, M.; Hou, Y. H.
2018-05-01
Dy films, deposited on the surface of sintered Nd–Fe–B magnets by magnetron sputtering, were employed for grain boundary diffusion source. High coercivity sintered Nd–Fe–B magnets were successfully prepared. Effects of sputtering power and grain boundary diffusion processes (GBDP) on the microstructure and magnetic properties were investigated in detail. The dense and uniform Dy films were beneficial to prepare high coercivity magnets by GBDP. The maximum coercivity value of 1189 kA m‑1 could be shown, which was an amplification of 22.3%, compared with that of as-prepared Nd–Fe–B magnet. Furthermore, the improved remanence and maximum energy product were also achieved through tuning grain boundary diffusion processes. Our results demonstrated that the formation of (Nd, Dy)2Fe14B shell surrounding Nd2Fe14B grains and fine, uniform and continuous intergranular RE-rich phases jointly contribute to the improved coercivity.
Peng, Zhilong; Chen, Shaohua
2012-10-01
Inspired by the reversible adhesion behaviors of geckos, the effects of pre-tension in a bio-inspired nano-film and a hierarchical structure on adhesion are studied theoretically. In the case with a uniformly distributing pre-tension in a spatula-like nano-film under peeling, a closed-form solution to a critical peeling angle is derived, below or above which the peel-off force is enhanced or reduced, respectively, compared with the case without pre-tension. The effects of a non-uniformly distributing pre-tension on adhesion are further investigated for both a spatula-like nano-film and a hierarchical structure-like gecko's seta. Compared with the case without pre-tension, the pre-tension, no matter uniform or non-uniform, can increase the adhesion force not only for the spatula-like nano-film but also for the hierarchical structure at a small peeling angle, while decrease it at a relatively large peeling angle. Furthermore, if the pre-tension is large enough, the effective adhesion energy of a hierarchical structure tends to vanish at a critical peeling angle, which results in spontaneous detachment of the hierarchical structure from the substrate. The present theoretical predictions can not only give some explanations on the existing experimental observation that gecko's seta always detaches at a specific angle and no apparent adhesion force can be detected above the critical angle but also provide a deep understanding for the reversible adhesion mechanism of geckos and be helpful to the design of biomimetic reversible adhesives.
TEM investigation of DC sputtered carbon-nitride-nickel thin films
International Nuclear Information System (INIS)
Safran, G.; Geszti, O.; Radnoczi, G.
2002-01-01
Deposition of carbon nitride (C-N) and carbon-nitride-nickel (C-N-Ni) films onto glass, NaCl and Si(001) substrates was carried out in a dc magnetron sputtering system. Carbon was deposited from high-purity (99.99%) pyrolytic graphite target, 50 mm in diameter, positioned at 10 cm from a resistance-heated substrate holder. C-N-Ni films were grown by a small Ni plate mounted on the graphite target. The base pressure of the deposition chamber was ∼7x10 -7 Torr. Films were grown at a substrate temperature of 20-700 grad C, in pure N 2 at partial pressures of 1.9 -2.2 mTorr and the substrates were held at ground potential. The typical film thickness of 15-30 nm was deposited on all the substrates at a magnetron current of 0.2 and 0.3 A, which resulted in a deposition rate of 1.5-2 nm/s. Structural characterizations were performed by high-resolution transmission electron microscopy (HRTEM) using a JEOL 3010 operated at 300 kV and a 200 kV Philips CM 20 electron microscope equipped with a Ge detector Noran EDS system. The N content of the C-N samples prepared at room temperature was 22-24% by EDS measurement and showed a decrease to 6-7% at elevated temperatures up to 700 grad C. The N concentration in the C-N-Ni films was higher: ∼38% at RT and ∼9% at 700 grad C. The Ni concentration of C-N-Ni samples was 5-6% and 0.3-0.4% in samples deposited at RT and 700 grad C respectively. The low Ni content in the latter is attributed to a decrease of the sticking coefficient of the carbon co-deposited Ni at elevated temperatures. (Authors)
Water-mediated electrochemical nano-writing on thin ceria films
International Nuclear Information System (INIS)
Yang, Nan; Doria, Sandra; Tebano, Antonello; Licoccia, Silvia; Balestrino, Giuseppe; Kumar, Amit; Arruda, Thomas M; Jesse, Stephen; Ivanov, Ilia N; Baddorf, Arthur P; Strelcov, Evgheni; Kalinin, Sergei V; Jang, Jae Hyuck; Borisevich, Albina Y
2014-01-01
Bias dependent mechanisms of irreversible cathodic and anodic processes on a pure CeO 2 film are studied using modified atomic force microscopy (AFM). For a moderate positive bias applied to the AFM tip an irreversible electrochemical reduction reaction is found, associated with significant local volume expansion. By changing the experimental conditions we are able to deduce the possible role of water in this process. Simultaneous detection of tip height and current allows the onset of conductivity and the electrochemical charge transfer process to be separated, further elucidating the reaction mechanism. The standard anodic/cathodic behavior is recovered in the high bias regime, where a sizable transport current flows between the tip and the film. These studies give insight into the mechanisms of the tip-induced electrochemical reactions as mediated by electronic currents, and into the role of water in these processes, as well as providing a different approach for electrochemical nano-writing. (paper)
The Sustainable Improvement of Manufacturing for Nano-Titanium
Directory of Open Access Journals (Sweden)
Chia-Nan Wang
2016-04-01
Full Text Available Scientists have found that nanomaterials possess many outstanding features in their tiny grain structure compared to other common materials. Titanium at the nano-grain scale shows many novel characteristics which demonstrate suitability for use in surgical implants. In general, equal channel angular pressing (ECAP is the most popular and simple process to produce nano-titanium. However, ECAP is time-consuming, power-wasting, and insufficiently produces the ultrafine grain structure. Therefore, the objective of this research is to propose a new method to improve the ECAP’s performances to reach the ultrafine grain structure, and also to save production costs, based on the innovation theory of Teoriya Resheniya Izobreatatelskih Zadatch (TRIZ. Research results show that the process time is reduced by 80%, and 94% of the energy is saved. Moreover, the grain size of the diameter for nano-titanium can be reduced from 160 nanometers (nm to 80 nm. The results are a 50% reduction of diameter and a 75% improvement of volume. At the same time, the method creates a refined grain size and good mechanical properties in the nano-titanium. The proposed method can be applied to produce any nanomaterial as well as biomaterials.
Energy Technology Data Exchange (ETDEWEB)
Vaxelaire, N; Labat, S; Thomas, O [Aix-Marseille University, IM2NP, FST avenue Escadrille Normandie Niemen, F-13397 Marseille Cedex (France); Proudhon, H; Forest, S [MINES ParisTech, Centre des materiaux, CNRS UMR 7633, BP 87, 91003 Evry Cedex (France); Kirchlechner, C; Keckes, J [Erich Schmid Institute for Material Science, Austrian Academy of Science and Institute of Metal Physics, University of Leoben, Jahnstrasse 12, 8700 Leoben (Austria); Jacques, V; Ravy, S [Synchrotron SOLEIL, L' Orme des merisiers, Saint-Aubin BP 48, 91192 Gif-sur-Yvette Cedex (France)], E-mail: nicolas.vaxelaire@univ-cezanne.fr
2010-03-15
Coherent x-ray diffraction is used to investigate the mechanical properties of a single grain within a polycrystalline thin film in situ during a thermal cycle. Both the experimental approach and finite element simulation are described. Coherent diffraction from a single grain has been monitored in situ at different temperatures. This experiment offers unique perspectives for the study of the mechanical properties of nano-objects.
International Nuclear Information System (INIS)
Vaxelaire, N; Labat, S; Thomas, O; Proudhon, H; Forest, S; Kirchlechner, C; Keckes, J; Jacques, V; Ravy, S
2010-01-01
Coherent x-ray diffraction is used to investigate the mechanical properties of a single grain within a polycrystalline thin film in situ during a thermal cycle. Both the experimental approach and finite element simulation are described. Coherent diffraction from a single grain has been monitored in situ at different temperatures. This experiment offers unique perspectives for the study of the mechanical properties of nano-objects.
Abbas, K; Alaie, S; Ghasemi Baboly, M; Elahi, M M M; Anjum, Dalaver H.; Chaieb, Saharoui; Leseman, Z C
2015-01-01
-1700 MPa) are recorded and explained by the variable morphology. This work suggests that in addition to the in-plane grain size of thin films, the transitions in cross-sectional morphologies of the Pt films significantly affect their mechanical behavior.
Superior light trapping in thin film silicon solar cells through nano imprint lithography
Energy Technology Data Exchange (ETDEWEB)
Soppe, W.J.; Dorenkamper, M.S.; Schropp, R.E.I.; Pex, P.P.A.C.
2013-10-15
ECN and partners have developed a fabrication process based on nanoimprint lithography (NIL) of textures for light trapping in thin film solar cells such as thin-film silicon, OPV, CIGS and CdTe. The process can be applied in roll-to-roll mode when using a foil substrate or in roll-to-plate mode when using a glass substrate. The lacquer also serves as an electrically insulating layer for cells if steel foil is used as substrate, to enable monolithic series interconnection. In this paper we will show the superior light trapping in thin film silicon solar cells made on steel foil with nanotextured back contacts. We have made single junction a-Si and {mu}c-Si and a-Si/{mu}c-Si tandem cells, where we applied several types of nano-imprints with random and periodic structures. We will show that the nano-imprinted back contact enables more than 30% increase of current in comparison with non-textured back contacts and that optimized periodic textures outperform state-of-the-art random textures. For a-Si cells we obtained Jsc of 18 mA/cm{sup 2} and for {mu}c-Si cells more than 24 mA/cm{sup 2}. Tandem cells with a total Si absorber layer thickness of only 1350 nm have an initial efficiency of 11%.
International Nuclear Information System (INIS)
Kauffeldt, Elena; Kauffeldt, Thomas
2006-01-01
Gas phase processes are a successful route for the synthesis of nano materials. Nickel particles are used in applications ranging from catalysis to nano electronics and energy storage. The application field defines the required particle size, morphology, crystallinity and purity. Nickel tetracarbonyl is the most promising precursor for the synthesis of high purity nickel particles. Due to the toxicity of this precursor and to obtain an optimal process control we developed a two-step flow type process. Nickel carbonyl and nickel particles are synthesized in a sequence of reactions. The particles are formed in a hot wall reactor at temperatures below 400 deg. C in different gas compositions. Varying the process conditions enables the adjustment of the particle size in a range from 3 to 140 nm. The controllable crystalline habits are polycrystalline, single crystals or multiple twinned particles (MTP). Spectroscopic investigations show an excellent purity. We report about the process and first investigations of the properties of the synthesized nickel nanomaterial
Directory of Open Access Journals (Sweden)
R. Seyed Sharifi
2016-02-01
promoting rhizobacteria application on yield, yield components and grain filling period of soybean. Materials and Methods In order to study the effects of Nano-Zinc oxide and seed inoculation with Brady rhizobium and plant growth promoting rhizobacteria on yield and some agronomic characteristics of soybean, a factorial experiment based on randomized complete block design with three replications was conducted in 2013 at the research farm of the Islamic Azad University, Ardabil Branch. Factors were included foliar application of Nano-Zinc oxide at four levels (Zero as control, 0.3, 0.6 and 0.9 g l-1 and seed inoculation with Brady rhizobium and plant growth promoting rhizobacteria at five levels (without inoculation as control, seed inoculation with Brady rhizobium japanicum, seed inoculation with Brady rhizobium japanicum+Azosprillum lipoferum strain OF, seed inoculation with Brady rhizobium japanicum+Psedomonas putida, seed inoculation with Brady rhizobium japanicum+ Azosprillum lipoferum strain OF+ Psedomonas putida. Results and Discussion The results of growth indices showed that the maximum total dry matter (530 g m-2, crop growth rate (9.48 g.m-2.day-1 and relative growth rate (0.1 g.g-1.day-1 were obtained at foliar application of 0.9 g l-1 Nano-Zinc oxide×seed inoculation with rhizobium+Azosprillum+ Psedomonas and the least of these indices were obtained without of foliar application Nano-Zinc oxide × seed inoculation. The results showed that plant height, the number of nodules per plant, the number of pod per plant, grain yield and grain 100 weight were significantly affected by Nano-Zinc oxide, seed inoculation and interaction of Nano-Zinc oxide×seed inoculation. Maximum of plant height, grain 100 weight, the number of nodules per plant and grain yield were obtained at foliar application of 0.9 g l-1 of Nano-Zinc oxide×seed inoculation with rhizobium and PGPR. Dry weight of nodules per plant, the number of pod per plant and the number of grains per plant
Prediction Surface Morphology of Nanostructure Fabricated by Nano-Oxidation Technology.
Huang, Jen-Ching; Chang, Ho; Kuo, Chin-Guo; Li, Jeen-Fong; You, Yong-Chin
2015-12-04
Atomic force microscopy (AFM) was used for visualization of a nano-oxidation technique performed on diamond-like carbon (DLC) thin film. Experiments of the nano-oxidation technique of the DLC thin film include those on nano-oxidation points and nano-oxidation lines. The feature sizes of the DLC thin film, including surface morphology, depth, and width, were explored after application of a nano-oxidation technique to the DLC thin film under different process parameters. A databank for process parameters and feature sizes of thin films was then established, and multiple regression analysis (MRA) and a back-propagation neural network (BPN) were used to carry out the algorithm. The algorithmic results are compared with the feature sizes acquired from experiments, thus obtaining a prediction model of the nano-oxidation technique of the DLC thin film. The comparative results show that the prediction accuracy of BPN is superior to that of MRA. When the BPN algorithm is used to predict nano-point machining, the mean absolute percentage errors (MAPE) of depth, left side, and right side are 8.02%, 9.68%, and 7.34%, respectively. When nano-line machining is being predicted, the MAPEs of depth, left side, and right side are 4.96%, 8.09%, and 6.77%, respectively. The obtained data can also be used to predict cross-sectional morphology in the DLC thin film treated with a nano-oxidation process.
He, Ming; Li, Bo; Cui, Xun; Jiang, Beibei; He, Yanjie; Chen, Yihuang; O'Neil, Daniel; Szymanski, Paul; Ei-Sayed, Mostafa A.; Huang, Jinsong; Lin, Zhiqun
2017-07-01
Control over morphology and crystallinity of metal halide perovskite films is of key importance to enable high-performance optoelectronics. However, this remains particularly challenging for solution-printed devices due to the complex crystallization kinetics of semiconductor materials within dynamic flow of inks. Here we report a simple yet effective meniscus-assisted solution printing (MASP) strategy to yield large-grained dense perovskite film with good crystallization and preferred orientation. Intriguingly, the outward convective flow triggered by fast solvent evaporation at the edge of the meniscus ink imparts the transport of perovskite solutes, thus facilitating the growth of micrometre-scale perovskite grains. The growth kinetics of perovskite crystals is scrutinized by in situ optical microscopy tracking to understand the crystallization mechanism. The perovskite films produced by MASP exhibit excellent optoelectronic properties with efficiencies approaching 20% in planar perovskite solar cells. This robust MASP strategy may in principle be easily extended to craft other solution-printed perovskite-based optoelectronics.
2016-01-01
Within the framework of The Heterogeneous dust Evolution Model for Interstellar Solids (THEMIS), this work explores the surface processes and chemistry relating to core/mantle interstellar and cometary grain structures and their influence on the nature of these fascinating particles. It appears that a realistic consideration of the nature and chemical reactivity of interstellar grain surfaces could self-consistently and within a coherent framework explain: the anomalous oxygen depletion, the nature of the CO dark gas, the formation of ‘polar ice’ mantles, the red wing on the 3 μm water ice band, the basis for the O-rich chemistry observed in hot cores, the origin of organic nano-globules and the 3.2 μm ‘carbonyl’ absorption band observed in comet reflectance spectra. It is proposed that the reaction of gas phase species with carbonaceous a-C(:H) grain surfaces in the interstellar medium, in particular the incorporation of atomic oxygen into grain surfaces in epoxide functional groups, is the key to explaining these observations. Thus, the chemistry of cosmic dust is much more intimately related with that of the interstellar gas than has previously been considered. The current models for interstellar gas and dust chemistry will therefore most likely need to be fundamentally modified to include these new grain surface processes. PMID:28083090
Directory of Open Access Journals (Sweden)
A. Benchettara
2014-12-01
Full Text Available In this work, we present the modification of a glassy carbon electrode with nickel oxide film which is performed in two successive steps. In the first one, the electrochemical deposition of metallic nickel on the glassy carbon electrode (GCE is achieved in 0.1M boric acid; in the second step, the metallic deposit is anodically oxidized in 0.1M NaOH. These two operations were carried out in a three electrode cell with a filiform platinum auxiliary electrode, a SCE as potential reference and a working microelectrode of modified glassy carbon with nickel oxides. This electrode is characterized by several electrochemical techniques and is used for the catalytic determination of ethanol, 2-propanol and 1-butanol in 0.1 M NaOH. The proposed chemical mechanism shows that NiO2 acts as a mediator.
Directory of Open Access Journals (Sweden)
A. Benchettara
2015-07-01
Full Text Available In this work, we present the modification of a glassy carbon electrode with nickel oxide film which is performed in two successive steps. In the first one, the electrochemical deposition of metallic nickel on the glassy carbon electrode (GCE is achieved in 0.1M boric acid; in the second step, the metallic deposit is anodically oxidized in 0.1M NaOH. These two operations were carried out in a three electrode cell with a filiform platinum auxiliary electrode, a SCE as potential reference and a working microelectrode of modified glassy carbon with nickel oxides. This electrode is characterized by several electrochemical techniques and is used for the catalytic determination of ethanol, 2-propanol and 1-butanol in 0.1 M NaOH. The proposed chemical mechanism shows that NiO2 acts as a mediator.
International Nuclear Information System (INIS)
Cloud, Andrew N.; Abelson, John R.; Davis, Luke M.; Girolami, Gregory S.
2014-01-01
Thin films of late transition metal nitrides (where the metal is iron, cobalt, or nickel) are grown by low-pressure metalorganic chemical vapor deposition from bis[di(tert-butyl)amido]metal(II) precursors and ammonia. These metal nitrides are known to have useful mechanical and magnetic properties, but there are few thin film growth techniques to produce them based on a single precursor family. The authors report the deposition of metal nitride thin films below 300 °C from three recently synthesized M[N(t-Bu) 2 ] 2 precursors, where M = Fe, Co, and Ni, with growth onset as low as room temperature. Metal-rich phases are obtained with constant nitrogen content from growth onset to 200 °C over a range of feedstock partial pressures. Carbon contamination in the films is minimal for iron and cobalt nitride, but similar to the nitrogen concentration for nickel nitride. X-ray photoelectron spectroscopy indicates that the incorporated nitrogen is present as metal nitride, even for films grown at the reaction onset temperature. Deposition rates of up to 18 nm/min are observed. The film morphologies, growth rates, and compositions are consistent with a gas-phase transamination reaction that produces precursor species with high sticking coefficients and low surface mobilities
Stimulated Brillouin scattering of laser in semiconductor plasma embedded with nano-sized grains
Energy Technology Data Exchange (ETDEWEB)
Sharma, Giriraj, E-mail: grsharma@gmail.com [SRJ Government Girls’ College, Neemuch (M P) (India); Dad, R. C. [Government P G College, Mandsaur (M P) (India); Ghosh, S. [School of Studies in Physics, Vikram University, Ujjain, (M P) (India)
2015-07-31
A high power laser propagating through semiconductor plasma undergoes Stimulated Brillouin scattering (SBS) from the electrostrictively generated acoustic perturbations. We have considered that nano-sized grains (NSGs) ions are embedded in semiconductor plasma by means of ion implantation. The NSGs are bombarded by the surrounding plasma particles and collect electrons. By considering a negative charge on the NSGs, we present an analytically study on the effects of NSGs on threshold field for the onset of SBS and Brillouin gain of generated Brillouin scattered mode. It is found that as the charge on the NSGs builds up, the Brillouin gain is significantly raised and the threshold pump field for the onset of SBS process is lowered.
Energy Technology Data Exchange (ETDEWEB)
Pan, X.F., E-mail: PAN.Xifeng@nims.go.jp [National Institute for Materials Science, Superconducting Materials Research Center, 1-2-1, Sengen, Tsukuba, Ibaraki 305-0047 (Japan)] [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Chengdu 610031 (China); Matsumoto, A.; Kumakura, H. [National Institute for Materials Science, Superconducting Materials Research Center, 1-2-1, Sengen, Tsukuba, Ibaraki 305-0047 (Japan); Cheng, C.H.; Zhao, Y. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Chengdu 610031 (China)] [School of Materials Science and Engineering, University of New South Wales, Sydney 2052, NSW (Australia)
2011-11-15
We studied the cooperative doping effects of Ti and nano-SiC on transport J{sub c} and grain connectivity of MgB{sub 2} tape. Ti doping significantly weakens the current dependence of T{sub c} of MgB{sub 2} tapes at self-field, and does not change T{sub c} or slightly increases T{sub c}. Further Ti adding can enhance in-field J{sub c} performance of SiC doped MgB{sub 2} tapes by a factor of 50-100% at 4.2 K and 10 T. Ti addition improves the J{sub c} performance of undoped and SiC doped MgB{sub 2} by modifying their grains connection. By now, nano-SiC powder (20-30 nm) is still the most effective additive for improving upper critical field and critical current density of MgB{sub 2}-based superconducting materials. However, some decomposed carbon aggregates at grain boundaries and results in serious weak-links of MgB{sub 2} grains, and these weak-links limit the further improvement of critical current density, J{sub c} of MgB{sub 2}, especially at lower fields. Ti doping is reported to increase the compactness of MgB{sub 2}, and modify its intergranular coupling by forming ultrathin TiB{sub 2} layer at grain boundaries. In this work, we studied the cooperative doping effects of Ti and nano-SiC on transport J{sub c} and grain connectivity of MgB{sub 2} and the possibility to improve transport J{sub c} of SiC doped MgB{sub 2} by introducing Ti additive. The results suggest the Ti addition can obviously improve J{sub c} of MgB{sub 2} at lower fields and also enhance the J{sub c} of SiC doped MgB{sub 2} by improving their grain connectivity which shows serious intergranular weak-links.
Directory of Open Access Journals (Sweden)
Kaoru Toko
2015-01-01
Full Text Available Producing large-grained polycrystalline Si (poly-Si film on glass substrates coated with conducting layers is essential for fabricating Si thin-film solar cells with high efficiency and low cost. We investigated how the choice of conducting underlayer affected the poly-Si layer formed on it by low-temperature (500°C Al-induced crystallization (AIC. The crystal orientation of the resulting poly-Si layer strongly depended on the underlayer material: (100 was preferred for Al-doped-ZnO (AZO and indium-tin-oxide (ITO; (111 was preferred for TiN. This result suggests Si heterogeneously nucleated on the underlayer. The average grain size of the poly-Si layer reached nearly 20 µm for the AZO and ITO samples and no less than 60 µm for the TiN sample. Thus, properly electing the underlayer material is essential in AIC and allows large-grained Si films to be formed at low temperatures with a set crystal orientation. These highly oriented Si layers with large grains appear promising for use as seed layers for Si light-absorption layers as well as for advanced functional materials.
DEFF Research Database (Denmark)
Meškinis, Šaru Nas; Gudaitis, Rimantas; Šlapikas, Kęstutis
2018-01-01
deposited by either reactive HIPIMS or dc magnetron sputtering of Ni target was explained by possible clustering of the sp2-bonded carbon and/or formation of areas with the decreased hydrogen content. It was suggested that the tensile stress-induced rearrangements of these conglomerations have resulted......Piezoresistive properties of hydrogenated diamond-like carbon (DLC) and DLC-based nickel nanocomposite (DLC:Ni) films were studied in the range of low concentration of nickel nanoparticles. The films were deposited by reactive high power pulsed magnetron sputtering (HIPIMS) of Ni target, and some...... samples were deposited by direct current (dc) reactive magnetron sputtering for comparison purposes. Raman scattering spectroscopy, energy-dispersive X-ray spectrometry (EDS), and X-ray photoelectron spectroscopy (XPS) were used to study the structure and chemical composition of the films. A four...
Grain Boundaries Act as Solid Walls for Charge Carrier Diffusion in Large Crystal MAPI Thin Films.
Ciesielski, Richard; Schäfer, Frank; Hartmann, Nicolai F; Giesbrecht, Nadja; Bein, Thomas; Docampo, Pablo; Hartschuh, Achim
2018-03-07
Micro- and nanocrystalline methylammonium lead iodide (MAPI)-based thin-film solar cells today reach power conversion efficiencies of over 20%. We investigate the impact of grain boundaries on charge carrier transport in large crystal MAPI thin films using time-resolved photoluminescence (PL) microscopy and numerical model calculations. Crystal sizes in the range of several tens of micrometers allow for the spatially and time resolved study of boundary effects. Whereas long-ranged diffusive charge carrier transport is observed within single crystals, no detectable diffusive transport occurs across grain boundaries. The observed PL transients are found to crucially depend on the microscopic geometry of the crystal and the point of observation. In particular, spatially restricted diffusion of charge carriers leads to slower PL decay near crystal edges as compared to the crystal center. In contrast to many reports in the literature, our experimental results show no quenching or additional loss channels due to grain boundaries for the studied material, which thus do not negatively affect the performance of the derived thin-film devices.
International Nuclear Information System (INIS)
Mukaida, Masashi; Kai, Hideki; Shingai, Yuki
2009-01-01
Cubic perovskite structure has been found to play an important role for the nano-rod formation in REBa 2 Cu 3 O 7-δ films. BaWO 4 , with a sheelite structure, and BaNb 2 O 6 , with a tungsten bronze structure, were doped into REBa 2 Cu 3 O 7-δ targets. Laser-deposited, these materials form nano-rods in REBa 2 Cu 3 O 7-δ films accompanied by Ln elements, resulting in the composition of a pseudo-cubic perovskite structure. This was confirmed by selected area electron diffraction patterns (SADP) and composition mapping using energy-dispersive X-ray spectroscopy scanning transmission electron microscope (EDS-STEM) analysis. BaWO 4 with a sheelite structure, and BaNb 2 O 6 with a tungsten bronze structure, doped into targets no longer retain their structures, but can form pseudo-cubic perovskite structures in laser-deposited REBa 2 Cu 3 O 7-δ films. The perovskite crystal structure is thought to be important for nano-rod formation in the laser deposited REBa 2 Cu 3 O 7-δ film. (author)
Dual-bath electrodeposition of n-type Bi–Te/Bi–Se multilayer thin films
Energy Technology Data Exchange (ETDEWEB)
Matsuoka, Ken; Okuhata, Mitsuaki; Takashiri, Masayuki, E-mail: takashiri@tokai-u.jp
2015-11-15
N-type Bi–Te/Bi–Se multilayer thin films were prepared by dual-bath electrodeposition. We varied the number of layers from 2 to 10 while the total film thickness was maintained at approximately 1 μm. All the multilayer films displayed the X-ray diffraction peaks normally observed from individual Bi{sub 2}Te{sub 3} and Bi{sub 2}Se{sub 3} crystal structures, indicating that both phases coexist in the multilayer. The cross-section of the 10-layer Bi–Te/Bi–Se film was composed of stacked layers with nano-sized grains but the boundaries between the layers were not planar. The Seebeck coefficient was almost constant throughout the entire range of our experiment, but the electrical conductivity of the multilayer thin films increased significantly as the number of layers was increased. This may be because the electron mobility increases as the thickness of each layer is decreased. As a result of the increased electrical conductivity, the power factor also increased with the number of layers. The maximum power factor was 1.44 μW/(cm K{sup 2}) for the 10-layer Bi–Te/Bi–Se film, this was approximately 3 times higher than that of the 2-layer sample. - Highlights: • N-type Bi–Te/Bi–Se multilayer thin films were deposited by electrodeposition. • We employed a dual-bath electrodeposition process for preparing the multilayers. • The Bi–Te/Bi–Se film was composed of stacked layers with nano-sized grains. • The electrical conductivity increased as the number of layers was increased. • The power factor improved by 3 times as the number of layers was increased.
Ion beam assisted deposition of nano-structured C:Ni films
Energy Technology Data Exchange (ETDEWEB)
Abrasonis, G.; Muecklich, A.; Heller, R.; Heinig, K.H.; Gemming, S.; Moeller, W. [Helmholtz-Zentrum Dresden-Rossendorf, Dresden (Germany); Krause, M. [Helmholtz-Zentrum Dresden-Rossendorf, Dresden (Germany); Institute of Physics, TU Dresden (Germany)
2012-07-01
Nanostructures influence material properties dramatically due to size, shape and interface effects. Thus the control of the structure at the nanoscale is a key issue in nanomaterials science. The interaction of hyperthermal ions with solids is confined to the nanometer scale. Thus, it can be used to control the morphology evolution during multiphase film deposition. Ion-induced displacements occur in a thin surface layer of the growing film where they increase the atomic mobility for the phase separation. Here the growth-structure relationship of C:Ni (15 at.%) nanocomposite films grown by oblique incidence (45 ) ion beam assisted deposition is reported. The influences of the flux of an assisting Ar+ ion beam (0-140 eV) as well as of an elevated substrate temperature have been studied. The formation of elongated nickel nanoparticles is strongly promoted by the ion beam assistance. Moreover, the metal nanocolumns no longer align with the advancing surface, but with the incoming ions. A window of conditions is established within which the ion assistance leads to the formation of regular composition modulations with a well defined periodicity and tilt. As the dominating driving force for the pattern formation is of physical origin, this approach might be applicable to other immiscible systems.
Directory of Open Access Journals (Sweden)
M. Nishihara
2018-03-01
Full Text Available In this study, organic-inorganic composite electrolyte membranes are developed for a novel water-absorbing porous electrolyte water electrolysis cell. As the materials of the composite electrolyte membrane, 80 wt% of a proton-conducting nano zeolite (H-MFI as an electrolyte and 20 wt% of poly(vinyl alcohol (PVA as a cross-linkable matrix are used. The nano zeolite is prepared by a milling process. The nano zeolite-PVA composite membrane precursors are prepared by spraying onto a substrate, followed by cross-linking. The resulting nano zeolite-cross-linked PVA composite films are then evaluated for their properties such as proton conductivity as electrolyte membranes for the water-absorbing porous electrolyte water electrolysis cell. It is confirmed that conventional materials such as zeolites and PVA can be used for the water electrolysis as an electrolyte.
Slip activity of persistent slip bands in polycrystalline nickel
International Nuclear Information System (INIS)
Weidner, A.; Beyer, R.; Blochwitz, C.; Holste, C.; Schwab, A.; Tirschler, W.
2006-01-01
The appearance of glide localizations after cyclic deformation in the saturation stage was investigated for polycrystalline nickel. It was shown that persistent slip bands (PSBs) are formed in a wide range of grain orientations. Concerning the grain size it was found, that the probability for the appearance of PSBs is higher for larger grains. The local slip activity of the formed PSBs was studied after half-cycle deformation using atomic force microscopy (AFM) and scanning electron microscopy (SEM). The fraction of grains with glide-active PSBs and the glide-active PSB volume itself is very small after the half-cycle loading. The obtained local shear strain amplitudes are quite high and vary in the range of 0.2-5%. They are comparable with those found in nickel single crystals at the same loading procedure
Magnetic nanofilms of nickel prepared at the liquid-liquid interface
International Nuclear Information System (INIS)
Varghese, Neenu; Rao, C.N.R.
2011-01-01
Highlights: → Formation of nickel thinfims at the organic-aqueous interface at room temperature. → Thickness of nanofilm is ∼20 nm. → Ni nanofilms exhibit superparamagnetic behavior. → Thicker Ni films are obtained at a higher temperature (60 o C). -- Abstract: Thin films of metallic nickel with a thickness of the order of 20 nm have been prepared at the organic-aqueous interface at room temperature by the reaction of nickel cupferronate [Ni(C 6 H 5 N 2 O 2 ) 2 ] in toluene medium and sodium borohydride (NaBH 4 ) in aqueous medium. The films were characterized with transmission electron microscopy, scanning electron microscopy and atomic force microscopy. Thicker Ni films could be prepared by carrying out the reaction at the interface at 60 o C. The Ni nanofilms exhibit superparamagnetic behavior.
On the reflectivity of nickel neutron mirrors
Energy Technology Data Exchange (ETDEWEB)
Adib, M.; Maayouf, R.M.A.; Abdel-Kawy, A.; Habib, N. (Atomic Energy Establishment, Cairo (Egypt). Reactor and Neutron Physics Dept.); Kenawy, M.A.; Wahba, M.; Ashry, A.H. (Ain Shams Univ., Cairo (Egypt))
1991-02-01
Neutron reflectivities were determined for 300 nm thick films of natural nickel and nickel 58 coated on glass plates. The measurements were performed at glancing angles between 40' and 60'. The incident neutron beam from one of the ET-RR-1 reactor horizontal channels covered neutron wavelengths between 0.55 and 0.80 nm. It was found that nickel 58, because of the high value of its critical glancing angle, is more efficient as a neutron mirror than natural nickel. (orig.).
Kane, R. D.; Petrovic, J. J.; Ebert, L. J.
1975-01-01
Techniques are evaluated for chemical, electrochemical, and thermal etching of thoria dispersed (TD) nickel alloys. An electrochemical etch is described which yielded good results only for large grain sizes of TD-nickel. Two types of thermal etches are assessed for TD-nickel: an oxidation etch and vacuum annealing of a polished specimen to produce an etch. It is shown that the first etch was somewhat dependent on sample orientation with respect to the processing direction, the second technique was not sensitive to specimen orientation or grain size, and neither method appear to alter the innate grain structure when the materials were fully annealed prior to etching. An electrochemical etch is described which was used to observe the microstructures in TD-NiCr, and a thermal-oxidation etch is shown to produce better detail of grain boundaries and to have excellent etching behavior over the entire range of grain sizes of the sample.
Energy Technology Data Exchange (ETDEWEB)
Costa e Silva, Danilo Lopes
2015-11-01
In this work, carbon thin films were produced by the magnetron sputtering technique using single crystal substrates of alumina c-plane (0001) and Si (111) and Si (100) substrates, employing Co, Ni and Cu as intermediate films (buffer-layers). The depositions were conducted in three stages, first with cobalt buffer-layers where only after the production of a large number of samples, the depositions using cooper buffer-layers were carried out on Si substrates. Then, depositions were performed with nickel buffer layers using single-crystal alumina substrates. The crystallinity of the carbon films was evaluated by using the technique of Raman spectroscopy and, then, by X-ray diffraction (XRD). The morphological characterization of the films was performed by scanning electron microscopy (SEM and FEG-SEM) and high-resolution transmission electron microscopy (HRTEM). The XRD peaks related to the carbon films were observed only in the results of the samples with cobalt and nickel buffer-layers. The Raman spectroscopy showed that the carbon films with the best degree of crystallinity were the ones produced with Si (111) substrates, for the Cu buffers, and sapphire substrates for the Ni and Co buffers, where the latter resulted in a sample with the best crystallinity of all the ones produced in this work. It was observed that the cobalt has low recovering over the alumina substrates when compared to the nickel. Sorption tests of Ce ions by the carbon films were conducted in two samples and it was observed that the sorption did not occur probably because of the low crystallinity of the carbon films in both samples. (author)
Dudem, Bhaskar; Ko, Yeong Hwan; Leem, Jung Woo; Lim, Joo Ho; Yu, Jae Su
2016-11-09
We report the creation of hybrid energy cells based on hierarchical nano/micro-architectured polydimethylsiloxane (HNMA-PDMS) films with multifunctionality to simultaneously harvest mechanical, solar, and wind energies. These films consist of nano/micro dual-scale architectures (i.e., nanonipples on inverted micropyramidal arrays) on the PDMS surface. The HNMA-PDMS is replicable by facile and cost-effective soft imprint lithography using a nanoporous anodic alumina oxide film formed on the micropyramidal-structured silicon substrate. The HNMA-PDMS film plays multifunctional roles as a triboelectric layer in nanogenerators and an antireflection layer for dye-sensitized solar cells (DSSCs), as well as a self-cleaning surface. This film is employed in triboelectric nanogenerator (TENG) devices, fabricated by laminating it on indium-tin oxide-coated polyethylene terephthalate (ITO/PET) as a bottom electrode. The large effective contact area that emerged from the densely packed hierarchical nano/micro-architectures of the PDMS film leads to the enhancement of TENG device performance. Moreover, the HNMA-PDMS/ITO/PET, with a high transmittance of >90%, also results in highly transparent TENG devices. By placing the HNMA-PDMS/ITO/PET, where the ITO/PET is coated with zinc oxide nanowires, as the top glass substrate of DSSCs, the device is able to add the functionality of TENG devices, thus creating a hybrid energy cell. The hybrid energy cell can successfully convert mechanical, solar, and wind energies into electricity, simultaneously or independently. To specify the device performance, the effects of external pushing frequency and load resistance on the output of TENG devices are also analyzed, including the photovoltaic performance of the hybrid energy cells.
Sun, Ke; Saadi, Fadl H; Lichterman, Michael F; Hale, William G; Wang, Hsin-Ping; Zhou, Xinghao; Plymale, Noah T; Omelchenko, Stefan T; He, Jr-Hau; Papadantonakis, Kimberly M; Brunschwig, Bruce S; Lewis, Nathan S
2015-03-24
Reactively sputtered nickel oxide (NiOx) films provide transparent, antireflective, electrically conductive, chemically stable coatings that also are highly active electrocatalysts for the oxidation of water to O2(g). These NiOx coatings provide protective layers on a variety of technologically important semiconducting photoanodes, including textured crystalline Si passivated by amorphous silicon, crystalline n-type cadmium telluride, and hydrogenated amorphous silicon. Under anodic operation in 1.0 M aqueous potassium hydroxide (pH 14) in the presence of simulated sunlight, the NiOx films stabilized all of these self-passivating, high-efficiency semiconducting photoelectrodes for >100 h of sustained, quantitative solar-driven oxidation of water to O2(g).
International Nuclear Information System (INIS)
Pedrero, E.; Vigil, E.; Zumeta, I.
1999-01-01
The depth of Titanium Oxide thin films grown by Dip Coating in a coloidal suspension of nano structured Titanium Oxide was characterized using Rutherford Backscattering Spectrometry. Film depths are compared in function of bath and suspension parameters
Shiba, Shunsuke; Kato, Dai; Kamata, Tomoyuki; Niwa, Osamu
2016-06-01
We report the fabrication of a nickel (Ni)-copper (Cu) bimetallic nanoalloy (~3 nm) embedded carbon film electrode with the unbalanced magnetron (UBM) co-sputtering technique, which requires only a one-step process at room temperature. Most of each nanoalloy body was firmly embedded in a chemically stable carbon matrix with an atomically flat surface (Ra: 0.21 nm), suppressing the aggregation and/or detachment of the nanoalloy from the electrode surface. The nanoalloy size and composition can be controlled simply by individually controlling the target powers of carbon, Ni and Cu, which also makes it possible to localize the nanoalloys near the electrode surface. This electrode exhibited excellent electrocatalytic activity for d-mannitol, which should be detected with a low detection limit in urine samples for the diagnosis of severe intestinal diseases. With a Ni/Cu ratio of around 64/36, the electrocatalytic current per metal area was 3.4 times larger than that of an alloy film electrode with a similar composition (~70/30). This improved electrocatalytic activity realized higher stability (n = 60, relative standard deviation (RSD): 4.6%) than the alloy film (RSD: 32.2%) as demonstrated by continuous measurements of d-mannitol.We report the fabrication of a nickel (Ni)-copper (Cu) bimetallic nanoalloy (~3 nm) embedded carbon film electrode with the unbalanced magnetron (UBM) co-sputtering technique, which requires only a one-step process at room temperature. Most of each nanoalloy body was firmly embedded in a chemically stable carbon matrix with an atomically flat surface (Ra: 0.21 nm), suppressing the aggregation and/or detachment of the nanoalloy from the electrode surface. The nanoalloy size and composition can be controlled simply by individually controlling the target powers of carbon, Ni and Cu, which also makes it possible to localize the nanoalloys near the electrode surface. This electrode exhibited excellent electrocatalytic activity for d
Atomic layer deposition of superparamagnetic and ferrimagnetic magnetite thin films
International Nuclear Information System (INIS)
Zhang, Yijun; Liu, Ming; Ren, Wei; Zhang, Yuepeng; Chen, Xing; Ye, Zuo-Guang
2015-01-01
One of the key challenges in realizing superparamagnetism in magnetic thin films lies in finding a low-energy growth way to create sufficiently small grains and magnetic domains which allow the magnetization to randomly and rapidly reverse. In this work, well-defined superparamagnetic and ferrimagnetic Fe 3 O 4 thin films are successfully prepared using atomic layer deposition technique by finely controlling the growth condition and post-annealing process. As-grown Fe 3 O 4 thin films exhibit a conformal surface and poly-crystalline nature with an average grain size of 7 nm, resulting in a superparamagnetic behavior with a blocking temperature of 210 K. After post-annealing in H 2 /Ar at 400 °C, the as-grown α−Fe 2 O 3 sample is reduced to Fe 3 O 4 phase, exhibiting a ferrimagnetic ordering and distinct magnetic shape anisotropy. Atomic layer deposition of magnetite thin films with well-controlled morphology and magnetic properties provides great opportunities for integrating with other order parameters to realize magnetic nano-devices with potential applications in spintronics, electronics, and bio-applications
Tang, C. J.; Fernandes, A. J. S.; Girão, A. V.; Pereira, S.; Shi, Fa-Nian; Soares, M. R.; Costa, F.; Neves, A. J.; Pinto, J. L.
2014-03-01
In this work, we study the growth habit of nanocrystalline diamond (NCD) films by exploring the very high power regime, up to 4 kW, in a 5 kW microwave plasma chemical vapour deposition (MPCVD) reactor, through addition of a small amount of nitrogen and oxygen (0.24%) into 4% CH4 in H2 plasma. The coupled effect of high microwave power and substrate temperature on NCD growth behaviour is systematically investigated by varying only power, while fixing the remaining operating parameters. When the power increases from 2 kW to 4 kW, resulting also in rise of the Si substrate temperature higher than 150 °C, the diamond films obtained maintain the NCD habit, while the growth rate increases significantly. The highest growth rate of 4.6 μm/h is achieved for the film grown at 4 kW, which represents a growth rate enhancement of about 15 times compared with that obtained when using 2 kW power. Possible factors responsible for such remarkable growth rate enhancement of the NCD films are discussed. The evolution of NCD growth characteristics such as morphology, microstructure and texture is studied by growing thick films and comparing it with that of large grain polycrystalline (PCD) films. One important characteristic of the NCD films obtained, in contrast to PCD films, is that irrespective of deposition time (i.e. film thickness), their grain size and surface roughness remain in the nanometer range throughout the growth. Finally, based on our present and previous experimental results, a potential parameter window is established for fast growth of NCD films under high power conditions.
Energy Technology Data Exchange (ETDEWEB)
Han, Minmin; Yu, Limin; Chen, Wenyuan [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); University of Chinese Academy of Sciences, Beijing 100080 (China); Wang, Wenzhen, E-mail: wzhwang@licp.cas.cn [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Jia, Junhong, E-mail: jhjia@licp.cas.cn [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou 730000 (China)
2016-04-30
Graphical abstract: - Highlights: • In{sub 2}S{sub 3} nano-flower films are deposited on TiO{sub 2} nanorods by a hydrothermal method. • The roles of PSS and PEG on structure controlling of In{sub 2}S{sub 3} films are discussed. • The energy conversion efficiency of In{sub 2}S{sub 3}/TiO{sub 2} enhances thrice than TiO{sub 2}. - Abstract: The In{sub 2}S{sub 3} nano-flower films on TiO{sub 2}/FTO (Fluorine-doped tin oxide) substrates were synthesized via hydrothermal method and the photoelectrochemical performances of In{sub 2}S{sub 3}/TiO{sub 2} photoelectrodes were characterized. The roles of PSS (poly(sodium-p-styrenesul-fonate)) and PEG (polyethylene glycol) on the structure controlling of In{sub 2}S{sub 3} films were also discussed. The results show that the In{sub 2}S{sub 3} nano-flower films consisted of ultrathin nanoflakes with a thickness of 5 nm are successfully grew on the surface of TiO{sub 2} nanorod arrays. PEG could play a role as the morphology-directing agent by confining crystal growth in certain directions, while PSS could provide coordination sites with long chains and lead to the formation of spherical structure. The energy conversion efficiency of In{sub 2}S{sub 3} nano-flower/TiO{sub 2} photoelectrodes enhances thrice compared with that of bare TiO{sub 2} photoelectrode. This research presents further insight for improving the efficiency of semiconductors by using the suitable electron transfer channels, which may be promising for rational construction of solar conversion and storage devices.
Steiner, Florian; Poelking, Carl; Niedzialek, Dorota; Andrienko, Denis; Nelson, Jenny
2017-05-03
We present a multi-scale model for charge transport across grain boundaries in molecular electronic materials that incorporates packing disorder, electrostatic and polarisation effects. We choose quasi two-dimensional films of tri-isopropylsilylethynyl pentacene (TIPS-P) as a model system representative of technologically relevant crystalline organic semiconductors. We use atomistic molecular dynamics, with a force-field specific for TIPS-P, to generate and equilibrate polycrystalline two-dimensional thin films. The energy landscape is obtained by calculating contributions from electrostatic interactions and polarization. The variation in these contributions leads to energetic barriers between grains. Subsequently, charge transport is simulated using a kinetic Monte-Carlo algorithm. Two-grain systems with varied mutual orientation are studied. We find relatively little effect of long grain boundaries due to the presence of low impedance pathways. However, effects could be more pronounced for systems with limited inter-grain contact areas. Furthermore, we present a lattice model to generalize the model for small molecular systems. In the general case, depending on molecular architecture and packing, grain boundaries can result in interfacial energy barriers, traps or a combination of both with qualitatively different effects on charge transport.
Energy Technology Data Exchange (ETDEWEB)
Tang, Guangze; Luo, Dian; Fan, Guohua [School of Material Science & Engineering, Harbin Institute of Technology, Harbin 150001 (China); Ma, Xinxin, E-mail: maxin@hit.edu.cn [State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001 (China); Wang, Liqin [School of Mechatronics Engineering, Harbin Institute of Technology, Harbin 150001 (China)
2017-05-01
Highlights: • Ta alloying layer are fabricated by magnetron sputtering and high current pulsed electron beam. • Nano-scaled TaC precipitates forms within the δ-Fe grain after tempering treatment. • The mean diameter of TaC particles is about 5–8 nm. • The hardness of alloying layer increased by over 50% after formation of nano-scaled TaC particle. - Abstract: In this study, the combination of magnetron sputtering and high current pulsed electron beam are used for surface alloying treatment of Ta film on high speed steel. And the Ta alloying layer is about 6 μm. After tempering treatment, TaC phase forms in Ta alloying layer when the treated temperature is over 823 K. Through the TEM and HRTEM observation, a large amount of nano-scaled precipitates (mean diameter 5–8 nm) form within the δ-Fe grain in Ta alloying layer after tempering treatment and these nano-scaled precipitates are confirmed as TaC particles, which contribute to the strengthening effect of the surface alloying layer. The hardness of tempered alloying layer can reach to 18.1 GPa when the treated temperature is 823 K which increase by 50% comparing with the untreated steel sample before surface alloying treatment.
Effect of Sb on physical properties and microstructures of laser nano/amorphous-composite film
International Nuclear Information System (INIS)
Li, Jia-Ning; Gong, Shui-Li; Sun, Mei; Shan, Fei-Hu; Wang, Xi-Chang; Jiang, Shuai
2013-01-01
A nano/amorphous-composite film was fabricated by laser cladding (LC) of the Co–Ti–B 4 C–Sb mixed powders on a TA15 alloy. Such film mainly consisted of Ti–Al, Co–Ti, Co–Sb intermetallics, TiC, TiB 2 , TiB, and the amorphous phases. Experimental results indicated that the crystal systems of TiB 2 (hexagonal)/TiC (cubic) and Sb (rhombohedral) played important role on the formation of such film. Due to the mismatch of these crystals systems and mutual immiscibility of the metallic components, Sb was not incorporated in TiB 2 /TiC, but formed separate nuclei during the film growth. Thus, the growth of TiB 2 /TiC was stopped by the Sb nucleus in such LC molten pool, so as to form the nanoscale particles
Effect of Sb on physical properties and microstructures of laser nano/amorphous-composite film
Energy Technology Data Exchange (ETDEWEB)
Li, Jia-Ning, E-mail: jn2369@163.com [Science and Technology on Power Beam Processes Laboratory, Beijing (China); Aviation Industry Corporation of China, Beijing Institute of Aeronautical Materials, Beijing 100095 (China); Beijing Aeronautical Manufacturing Technology Research Institute, Beijing 100024 (China); Gong, Shui-Li, E-mail: gongshuili@sina.com [Science and Technology on Power Beam Processes Laboratory, Beijing (China); Beijing Aeronautical Manufacturing Technology Research Institute, Beijing 100024 (China); Sun, Mei; Shan, Fei-Hu; Wang, Xi-Chang [Science and Technology on Power Beam Processes Laboratory, Beijing (China); Beijing Aeronautical Manufacturing Technology Research Institute, Beijing 100024 (China); Jiang, Shuai [Science and Technology on Power Beam Processes Laboratory, Beijing (China); Beijing Aeronautical Manufacturing Technology Research Institute, Beijing 100024 (China); Department of Materials Science and Engineering, China University of Petroleum, Qingdao 266580 (China)
2013-11-01
A nano/amorphous-composite film was fabricated by laser cladding (LC) of the Co–Ti–B{sub 4}C–Sb mixed powders on a TA15 alloy. Such film mainly consisted of Ti–Al, Co–Ti, Co–Sb intermetallics, TiC, TiB{sub 2}, TiB, and the amorphous phases. Experimental results indicated that the crystal systems of TiB{sub 2} (hexagonal)/TiC (cubic) and Sb (rhombohedral) played important role on the formation of such film. Due to the mismatch of these crystals systems and mutual immiscibility of the metallic components, Sb was not incorporated in TiB{sub 2}/TiC, but formed separate nuclei during the film growth. Thus, the growth of TiB{sub 2}/TiC was stopped by the Sb nucleus in such LC molten pool, so as to form the nanoscale particles.
Zhang, Zihou
Advancement of interconnect technology has imposed significant challenge on interface characterization and reliability for blurred interfaces between layers. There is a need for material properties and these miniaturized length scales and assessment of reliability; including the intrinsic film fracture toughness and the interfacial fracture toughness. The nano-meter range of film thicknesses currently employed, impose significant challenges on evaluating these physical quantities and thereby impose significant challenge on the design cycle. In this study we attempted to use a combined nano-indentation and nano-acoustic emission to qualitatively and quantitatively characterize the failure modes in ultra-thin blanket films on Si substrates or stakes of different characteristics. We have performed and analyzed an exhaustive group of testes that cove many diverge combination of film-substrate combination, provided by both Intel and IBM. When the force-indentation depth curve shows excursion, a direct measure of the total energy release rate is estimated. The collected acoustic emission signal is then used to partition the total energy into two segments, one associated with the cohesive fracture toughness of the film and the other is for the adhesive fracture toughness of the interface. The acoustic emission signal is analyzed in both the time and frequency domain to achieve such energy division. In particular, the signal time domain analysis for signal skewness, time of arrival and total energy content are employed with the proper signal to noise ratio. In the frequency domain, an expansive group of acoustic emission signals are utilized to construct the details of the power spectral density. A bank of band-pass filters are designed to sort the individual signals to those associated with adhesive interlayer cracking, cohesive channel cracking, or other system induced noise. The attenuation time and the energy content within each spectral frequency were the key elements
ZnS nanostructured thin-films deposited by successive ionic layer adsorption and reaction
Deshmukh, S. G.; Jariwala, Akshay; Agarwal, Anubha; Patel, Chetna; Panchal, A. K.; Kheraj, Vipul
2016-04-01
ZnS thin films were grown on glass substrate using successive ionic layer adsorption and reaction (SILAR) technique at room temperature. Aqueous solutions of ZnCl2 and Na2S were used as precursors. The X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), Raman spectroscopy and optical absorption measurements were applied to study the structural, surface morphology and optical properties of as-deposited ZnS thin films. The X-ray diffraction profiles revealed that ZnS thin films consist of crystalline grains with cubic phase. Spherical nano grains of random size and well covered on the glass substrate were observed from FESEM. The average grain size were found to be 77 nm, 100 nm and 124 nm for 20 cycles, 40 cycles and 60 cycles samples respectively. For 60 cycle sample, Raman spectra show two prominent peaks at 554 cm-1 and 1094 cm-1. The optical band gap values were found to be 3.76 eV, 3.72 eV and 3.67 eV for 20 cycle, 40 cycle and 60 cycle samples respectively.
International Nuclear Information System (INIS)
Wu, Jianguo; Wang, Kaige; Zhou, Yukun; Wang, Shuang; Zhang, Chen; Wang, Guiren
2016-01-01
Highlights: • One kind of large area nano-PAA-ZnCl_2 composite film is fabricated, its dimension and morphology is controllable. The properties of nano-composite films have been heavily influenced by the concentration of initial ZnCl_2 solution, the depth of nano-PAAM substrate and the growth time of ZnCl_2 crystals. • At room temperature, the nano-PAA-ZnCl_2 film has the same excitation center (335 nm) and emission center (430 nm) as the nano-PAAM substrate, and the PL intensities can be doubly enhanced. • After annealing at 500 °C, the emission peak spectra of the nano-composite films stabilized at 385 nm, 402 nm, and 430 nm. - Abstract: One kind of ZnCl_2 nano-films with controllable dimension and morphology is successfully synthesized on the top surface of nano-porous anodic alumina membrane (nano-PAAM) by self-organized method. The nano-PAA-ZnCl_2 composite films are characterized by field emission scanning electron microscopy, energy dispersive spectrometer, and laser confocal Raman spectroscopy. The results indicate that the concentration of initial ZnCl_2 solution, the depth of nano-PAAM substrate and the growth time of ZnCl_2 crystals have important influences on the properties of nano-composite films. Furthermore, the characteristics of nano-composites such as the photoluminescence (PL) spectra are investigated. Compared with the nano-PAAM substrate, at room temperature, all of the nano-PAA-ZnCl_2 composite films have both the same excitation center (335 nm) and emission center (430 nm), no matter what the nano-composite morphologies being; and the PL intensity of nano-PAA-ZnCl_2 composite films are all enhanced and the maximum enhancement is two times; after annealing at 500 °C, the emission spectra of the nano-composite films stabilized at the 385 nm, 402 nm and 430 nm. The research provides a new, simple, economical and practical technology to fabricate nano-PAA composite films with higher luminousintensity.
International Nuclear Information System (INIS)
Mompiou, F.; Legros, M.; Boé, A.; Coulombier, M.; Raskin, J.-P.; Pardoen, T.
2013-01-01
The nature of the elementary deformation mechanisms in small-grained metals has been the subject of numerous recent studies. In the submicron range, mechanisms other than intragranular dislocation mechanisms, such as grain boundary (GB)-based mechanisms, are active and can explain the deviations from the Hall–Petch law. Here, we report observations performed during in situ transmission electron microscopy (TEM) tensile tests on initially dislocation-free Al thin films with a mean grain size around 250 nm prepared by microfabrication techniques. Intergranular plasticity is activated at the onset of plasticity. It consists of the motion of dislocations in the GB plane irrespective of the GB character. Surface imperfections, such as GB grooves, are supposed to trigger intergranular plasticity. At larger deformations, the motion of the intergranular dislocations leads to GB sliding and eventually cavitation. In the meantime, GB stress-assisted migration and dislocation emission inside the grain from GB sources have also been observed. The observation of these different mechanisms during the deformation provides an important insight into the understanding of the mechanical properties of metallic thin films.
International Nuclear Information System (INIS)
Idrissi, Hosni; Kobler, Aaron; Amin-Ahmadi, Behnam; Schryvers, Dominique; Coulombier, Michael; Pardoen, Thomas; Galceran, Montserrat; Godet, Stéphane; Raskin, Jean-Pierre; Kübel, Christian
2014-01-01
In-situ bright field transmission electron microscopy (TEM) nanomechanical tensile testing and in-situ automated crystallographic orientation mapping in TEM were combined to unravel the elementary mechanisms controlling the plasticity of ultrafine grained Aluminum freestanding thin films. The characterizations demonstrate that deformation proceeds with a transition from grain rotation to intragranular dislocation glide and starvation plasticity mechanism at about 1% deformation. The grain rotation is not affected by the character of the grain boundaries. No grain growth or twinning is detected
Energy Technology Data Exchange (ETDEWEB)
Idrissi, Hosni, E-mail: hosni.idrissi@ua.ac.be [EMAT, University of Antwerp, Groenenborgerlaan 171, B-2020 Antwerp (Belgium); Institute of Mechanics, Materials and Civil Engineering, Université catholique de Louvain, Place Sainte Barbe 2, B-1348 Louvain-La-Neuve (Belgium); Kobler, Aaron [Institute of Nanotechnology (INT) and Karlsruhe Nano Micro Facility (KNMF), Karlsruhe Institute of Technology - KIT, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Joint Research Laboratory Nanomaterials (KIT and TUD) at Technische Universität Darmstadt (TUD), Petersenstr. 32, 64287 Darmstadt (Germany); Amin-Ahmadi, Behnam; Schryvers, Dominique [EMAT, University of Antwerp, Groenenborgerlaan 171, B-2020 Antwerp (Belgium); Coulombier, Michael; Pardoen, Thomas [Institute of Mechanics, Materials and Civil Engineering, Université catholique de Louvain, Place Sainte Barbe 2, B-1348 Louvain-La-Neuve (Belgium); Galceran, Montserrat; Godet, Stéphane [Matters and Materials Department, Université Libre de Bruxelles, 50 Av. FD Roosevelt CP194/03, 1050 Brussels (Belgium); Raskin, Jean-Pierre [Information and Communications Technologies, Electronics and Applied Mathematics (ICTEAM), Microwave Laboratory, Université catholique de Louvain, B-1348 Louvain-la-Neuve (Belgium); Kübel, Christian [Institute of Nanotechnology (INT) and Karlsruhe Nano Micro Facility (KNMF), Karlsruhe Institute of Technology - KIT, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany)
2014-03-10
In-situ bright field transmission electron microscopy (TEM) nanomechanical tensile testing and in-situ automated crystallographic orientation mapping in TEM were combined to unravel the elementary mechanisms controlling the plasticity of ultrafine grained Aluminum freestanding thin films. The characterizations demonstrate that deformation proceeds with a transition from grain rotation to intragranular dislocation glide and starvation plasticity mechanism at about 1% deformation. The grain rotation is not affected by the character of the grain boundaries. No grain growth or twinning is detected.
Nickel removal from nickel plating waste water using a biologically active moving-bed sand filter.
Pümpel, Thomas; Macaskie, Lynne E; Finlay, John A; Diels, Ludo; Tsezos, Marios
2003-12-01
Efficient removal of dissolved nickel was observed in a biologically active moving-bed 'MERESAFIN' sand filter treating rinsing water from an electroless nickel plating plant. Although nickel is fully soluble in this waste water, its passage through the sand filter promoted rapid removal of approximately 1 mg Ni/l. The speciation of Ni in the waste water was modelled; the most probable precipitates forming under the conditions in the filter were predicted using PHREEQC. Analyses of the Ni-containing biosludge using chemical, electron microscopical and X-ray spectroscopic techniques confirmed crystallisation of nickel phosphate as arupite (Ni3(PO4)2 x 8H2O), together with hydroxyapatite within the bacterial biofilm on the filter sand grains. Biosorption contributed less than 1% of the overall sequestered nickel. Metabolising bacteria are essential for the process; the definitive role of specific components of the mixed population is undefined but the increase in pH promoted by metabolic activity of some microbial components is likely to promote nickel desolubilisation by others.
Annealing texture of rolled nickel alloys
International Nuclear Information System (INIS)
Meshchaninov, I.V.; Khayutin, S.G.
1976-01-01
A texture of pure nickel and binary alloys after the 95% rolling and annealing has been studied. Insoluble additives (Mg, Zr) slacken the cubic texture in nickel and neral slackening of the texture (Zr). In the case of alloying with silicium (up to 2%) the texture practically coinsides with that of a technical-grade nickel. The remaining soluble additives either do not change the texture of pure nickel (C, Nb) or enhance the sharpness and intensity of the cubic compontnt (Al, Cu, Mn, Cr, Mo, W, Co -at their content 0.5 to 2.0%). A model is proposed by which variation of the annealing texture upon alloying is caused by dissimilar effect of the alloying elements on the mobility of high- and low-angle grain boundaries
Fabrication of high-performance fluorine doped-tin oxide film using flame-assisted spray deposition
Energy Technology Data Exchange (ETDEWEB)
Purwanto, Agus, E-mail: Aguspur@uns.ac.id [Department of Chemical Engineering, Faculty of Engineering, Sebelas Maret University, Jl. Ir. Sutami 36 A, Surakarta, Central Java 57126 (Indonesia); Widiyandari, Hendri [Department of Physics, Faculty of Mathematics and Natural Sciences, Diponegoro University, Jl. Prof. Dr. Soedarto, Tembalang, Semarang 50275 (Indonesia); Jumari, Arif [Department of Chemical Engineering, Faculty of Engineering, Sebelas Maret University, Jl. Ir. Sutami 36 A, Surakarta, Central Java 57126 (Indonesia)
2012-01-01
A high-performance fluorine-doped tin oxide (FTO) film was fabricated by flame-assisted spray deposition method. By varying the NH{sub 4}F doping concentration, the optimal concentration was established as 8 at.%. X-ray diffractograms confirmed that the as-grown FTO film was tetragonal SnO{sub 2}. In addition, the FTO film was comprised of nano-sized grains ranging from 40 to 50 nm. The heat-treated FTO film exhibited a sheet resistance of 21.8 {Omega}/{open_square} with an average transmittance of 81.9% in the visible region ({lambda} = 400-800 nm). The figures of merit shows that the prepared FTO film can be used for highly efficient dye-sensitized solar cells electrodes.
Gamma-Irradiation modified polypropylene and nano silver hybrid films: antibacterial activity
International Nuclear Information System (INIS)
Oliani, Washigton L.; Alcantara, Mara T.S.; Lima, Luis F.C.P. de; Bueno, Nelson R.; Rogero, Sizue O.; Lugao, Ademar B.; Parra, Duclerc F.; Huenuman, Nilton E.L.; Santos, Priscila M. dos
2013-01-01
This paper presents a study of films based on blends of polypropylene (PP) with radiation modified PP and insertion of silver nanoparticles aiming bactericide effect. The use of silver (Ag) gives important antibacterial properties since silver is highly toxic for bacteria. The blend of 50/50 PP and gamma irradiated PP was processed in a twin screw extruder. The polypropylene was processed for five PP-Nanocomposite AgNPs in different concentrations of 0.25%; 0.5%; 1.0%; 2.0% and 4.0% in wt%. The material was characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), cytotoxicity assay and reduction colony-forming unit (CFU). The analyzed films showed agglomeration of silver particles and regions with homogeneous distribution of the particles. The interactions of the nano silver bactericidal effect with E. coli and S. aureus were assessed. (author)
Gamma-Irradiation modified polypropylene and nano silver hybrid films: antibacterial activity
Energy Technology Data Exchange (ETDEWEB)
Oliani, Washigton L.; Alcantara, Mara T.S.; Lima, Luis F.C.P. de; Bueno, Nelson R.; Rogero, Sizue O.; Lugao, Ademar B.; Parra, Duclerc F., E-mail: washoliani@usp.br [Instituto de Pesquisas Energeticas Nucleares (IPEN-CNEN/SP), Sao Paulo, SP (Brazil); Huenuman, Nilton E.L.; Santos, Priscila M. dos [Universidade de Sao Paulo (USP), Sao Paulo, SP (Brazil). Dept. of Microbiologia; Riella, Humberto G. [Universidade Federal de Santa Catarina (UFSC), Florianopolis, SC (Brazil)
2013-07-01
This paper presents a study of films based on blends of polypropylene (PP) with radiation modified PP and insertion of silver nanoparticles aiming bactericide effect. The use of silver (Ag) gives important antibacterial properties since silver is highly toxic for bacteria. The blend of 50/50 PP and gamma irradiated PP was processed in a twin screw extruder. The polypropylene was processed for five PP-Nanocomposite AgNPs in different concentrations of 0.25%; 0.5%; 1.0%; 2.0% and 4.0% in wt%. The material was characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), cytotoxicity assay and reduction colony-forming unit (CFU). The analyzed films showed agglomeration of silver particles and regions with homogeneous distribution of the particles. The interactions of the nano silver bactericidal effect with E. coli and S. aureus were assessed. (author)
Fretting and wear behaviors of Ni/nano-WC composite coatings in dry and wet conditions
International Nuclear Information System (INIS)
Benea, Lidia; Başa, Sorin-Bogdan; Dănăilă, Eliza; Caron, Nadège; Raquet, Olivier; Ponthiaux, Pierre; Celis, Jean-Pierre
2015-01-01
Highlights: • The friction and wear properties of Ni/nano-WC composite were studied. • Nano-WC reinforcement decreased friction coefficient in dry and wet conditions. • Nano-WC reinforcement fraction was seen to be 12 wt.%. • Nanohardness increased by 27% compared to nickel without WC reinforcements. • Ennoblement of OCP corresponding to the Ni/nano-WC composite coating. - Abstract: The fretting and wear behaviors of Ni/nano-WC composite coatings were studied by considering the effect of fretting frequency of 1 Hz during 10,000 cycles, at different applied loads in dry or wet conditions. The studies were performed on a ball-on-disk tribometer and the results were compared with pure Ni coating. The nanohardness of pure Ni and Ni/nano-WC composite coatings was tested by nanoindentation technique. To evaluate the wet wear (tribocorrosion) behavior the open circuit potential (OCP) was measured before, during and after the fretting tests at room temperature in the solution that simulates the primary water circuit of Pressurized Water Reactors (PWRs). The results show that Ni/nano-WC composite coatings exhibited a low friction coefficient, high nanohardness and wear resistance compared with pure Ni coatings under similar experimental conditions. Ni/nano-WC composite coatings were obtained on stainless steel support by electrochemical codeposition of nano-sized WC particles (diameter size of ∼60 nm) with nickel, from a standard nickel Watts plating bath. The surface morphology and the composition of the coatings were characterized by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDX) respectively
International Nuclear Information System (INIS)
Fujii, Mami N.; Ishikawa, Yasuaki; Bermundo, Juan Paolo Soria; Uraoka, Yukiharu; Ishihara, Ryoichi; Cingel, Johan van der; Mofrad, Mohammad R. T.; Kawashima, Emi; Tomai, Shigekazu; Yano, Koki
2016-01-01
In a previous work, we reported the high field effect mobility of ZnO-doped In_2O_3 (IZO) thin film transistors (TFTs) irradiated by excimer laser annealing (ELA) [M. Fujii et al., Appl. Phys. Lett. 102, 122107 (2013)]. However, a deeper understanding of the effect of ELA on the IZO film characteristics based on crystallinity, carrier concentrations, and optical properties is needed to control localized carrier concentrations for fabricating self-aligned structures in the same oxide film and to adequately explain the physical characteristics. In the case of as-deposited IZO film used as the channel, a high carrier concentration due to a high density of oxygen vacancies was observed; such a film does not show the required TFT characteristics but can act as a conductive film. We achieved a decrease in the carrier concentration of IZO films by crystallization using ELA. This means that ELA can form localized conductive or semi-conductive areas on the IZO film. We confirmed that the reason for the carrier concentration decrease was the decrease of oxygen-deficient regions and film crystallization. The annealed IZO films showed nano-crystalline phase, and the temperature at the substrate was substantially less than the temperature limit for flexible films such as plastic, which is 50°C. This paves the way for the formation of self-aligned structures and separately formed conductive and semi-conductive regions in the same oxide film.
Fabrication of nano-structured UO2 fuel pellets
International Nuclear Information System (INIS)
Yang, Jae Ho; Kang, Ki Won; Rhee, Young Woo; Kim, Dong Joo; Kim, Jong Heon; Kim, Keon Sik; Song, Kun Woo
2007-01-01
Nano-structured materials have received much attention for their possibility for various functional materials. Ceramics with a nano-structured grain have some special properties such as super plasticity and a low sintering temperature. To reduce the fuel cycle costs and the total mass of spent LWR fuels, it is necessary to extend the fuel discharged burn-up. In order to increase the fuel burn-up, it is important to understand the fuel property of a highly irradiated fuel pellet. Especially, research has focused on the formation of a porous and small grained microstructure in the rim area of the fuel, called High Burn-up Structure (HBS). The average grain size of HBS is about 300nm. This paper deals with the feasibility study on the fabrication of nano-structured UO 2 pellets. The nano sized UO 2 particles are prepared by a combined process of a oxidation-reducing and a mechanical milling of UO 2 powder. Nano-structured UO 2 pellets (∼300nm) with a density of ∼93%TD can be obtained by sintering nano-sized UO 2 compacts. The SEM study reveals that the microstructure of the fabricated nano-structure UO 2 pellet is similar to that of HBS. Therefore, this bulk nano-structured UO 2 pellet can be used as a reference pellet for a measurement of the physical properties of HBS
Chemical vapor deposition of Si/SiC nano-multilayer thin films
International Nuclear Information System (INIS)
Weber, A.; Remfort, R.; Woehrl, N.; Assenmacher, W.; Schulz, S.
2015-01-01
Stoichiometric SiC films were deposited with the commercially available single source precursor Et_3SiH by classical thermal chemical vapor deposition (CVD) as well as plasma-enhanced CVD at low temperatures in the absence of any other reactive gases. Temperature-variable deposition studies revealed that polycrystalline films containing different SiC polytypes with a Si to carbon ratio of close to 1:1 are formed at 1000 °C in thermal CVD process and below 100 °C in the plasma-enhanced CVD process. The plasma enhanced CVD process enables the reduction of residual stress in the deposited films and offers the deposition on temperature sensitive substrates in the future. In both deposition processes the film thickness can be controlled by variation of the process parameters such as the substrate temperature and the deposition time. The resulting material films were characterized with respect to their chemical composition and their crystallinity using scanning electron microscope, energy dispersive X-ray spectroscopy (XRD), atomic force microscopy, X-ray diffraction, grazing incidence X-ray diffraction, secondary ion mass spectrometry and Raman spectroscopy. Finally, Si/SiC multilayers of up to 10 individual layers of equal thickness (about 450 nm) were deposited at 1000 °C using Et_3SiH and SiH_4. The resulting multilayers features amorphous SiC films alternating with Si films, which feature larger crystals up to 300 nm size as measured by transmission electron microscopy as well as by XRD. XRD features three distinct peaks for Si(111), Si(220) and Si(311). - Highlights: • Stoichiometric silicon carbide films were deposited from a single source precursor. • Thermal as well as plasma-enhanced chemical vapor deposition was used. • Films morphology, crystallinity and chemical composition were characterized. • Silicon/silicon carbide multilayers of up to 10 individual nano-layers were deposited.
Nickel hydroxide modified electrodes for urea determination
Directory of Open Access Journals (Sweden)
Luiz Henrique Dall´Antonia
2007-03-01
Full Text Available Nickel hydroxide films were prepared by electrodeposition from a solution Ni(NO32 0,05 mol L ?¹ on ITO electrodes (Tin oxide doped with Indium on PET-like plastic film, applying a current of - 0,1 A cm ?² during different time intervals between 1800 and 7200 s. The electrochemical behavior of the nickel hydroxide electrode was investigated through a cyclic voltammogram, in NaOH 1,0 mol L ?¹, where it was observed two peaks in the profile in 0,410 and 0,280 V, corresponding to redox couple Ni(II/Ni(III. A sensor for urea presenting a satisfactory answer can be obtained when, after the deposit of the film of Ni(OH2 on the electrode of nickel, it is immersed in a solution of NaOH 1,0 mol L ?¹ and applying a potential of + 0,435 V, where the maximum of the anodic current occurs in the cyclic voltammogram. Analyzing the results it can be observed that, for a range of analite concentration between 5 to 50 m mol L ?¹, the behavior is linear and the sensibility found was of 20,3 mA cm?² (mol L?¹?¹, presenting reproducibility confirming the nickel hydroxide electrodes utilization for the determination of urea.
Energy Technology Data Exchange (ETDEWEB)
Sobhani, Azam [Department of Inorganic Chemistry, Faculty of Chemistry, University of Kashan, Kashan, P.O. Box 87317-51167 (Iran, Islamic Republic of); Davar, Fatemeh [Institute of Nano Science and Nano Technology, University of Kashan, Kashan, P.O. Box 87317-51167 (Iran, Islamic Republic of); Salavati-Niasari, Masoud, E-mail: salavati@kashanu.ac.ir [Department of Inorganic Chemistry, Faculty of Chemistry, University of Kashan, Kashan, P.O. Box 87317-51167 (Iran, Islamic Republic of); Institute of Nano Science and Nano Technology, University of Kashan, Kashan, P.O. Box 87317-51167 (Iran, Islamic Republic of)
2011-07-01
Nano-sized nickel selenide powders have been successfully synthesized via an improved hydrothermal route based on the reaction between NiCl{sub 2}.6H{sub 2}O, SeCl{sub 4} and hydrazine (N{sub 2}H{sub 4}.H{sub 2}O) in water, in present of cetyltrimethyl ammonium bromide (CTAB) as surfactant, at various conditions. The products were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and X-ray energy dispersive spectroscopy analysis. Effects of temperature, reaction time and reductant agent on the morphology, the particle sizes and the phase of the final products have been investigated. It was found that the phase and morphology of the products could be greatly influenced by these parameters. The synthesis procedure is simple and uses less toxic reagents than the previously reported methods. Photoluminescence (PL) was used to study the optical properties of NiSe samples.
Electrosynthesis and catalytic activity of polymer-nickel particles composite electrode materials
International Nuclear Information System (INIS)
Melki, Tahar; Zouaoui, Ahmed; Bendemagh, Barkahoum; Oliveira, Ione M.F. de; Oliveira, Gilver F. de; Lepretre, Jean-Claude; Bucher, Christophe; Mou tet, Jean-Claude
2009-01-01
Nickel-polymer composite electrode materials have been synthesized using various strategies, all comprising the electrochemical reduction of nickel(II) cations or complexes, incorporated by either ion-exchange or complexation into various poly(pyrrole-carboxylate) thin films coated by oxidative electropolymerization onto carbon electrodes. The electrocatalytic activity and the stability of the different composites have been then evaluated in the course of the electrocatalytic hydrogenation of ketones and enones in aqueous electrolytes. The best results were obtained using nickel-polymer composites synthesized by electroreduction of nickel(II) ions complexed into polycarboxylate films, which are characterized by a high catalytic activity and a good operational stability. (author)
Electrosynthesis and catalytic activity of polymer-nickel particles composite electrode materials
Energy Technology Data Exchange (ETDEWEB)
Melki, Tahar; Zouaoui, Ahmed; Bendemagh, Barkahoum [Universite Ferhat Abbas, Setif (Algeria). Faculte des Sciences de l' Ingenieur. Dept. du Tronc Commun; Oliveira, Ione M.F. de; Oliveira, Gilver F. de [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte, MG (Brazil). Dept. de Quimica; Lepretre, Jean-Claude [UMR-5631 CNRS-INPG-UJF, St. Martin d' Heres Cedex (France). Lab. d' Electrochimie et de Physicochimie des Materiaux et Interfaces; Bucher, Christophe; Mou tet, Jean-Claude [Universite Joseph Fourier Grenoble 1 (France). Dept. de Chimie Moleculaire], e-mail: Jean-Claude.Moutet@ujf-grenoble.fr
2009-07-01
Nickel-polymer composite electrode materials have been synthesized using various strategies, all comprising the electrochemical reduction of nickel(II) cations or complexes, incorporated by either ion-exchange or complexation into various poly(pyrrole-carboxylate) thin films coated by oxidative electropolymerization onto carbon electrodes. The electrocatalytic activity and the stability of the different composites have been then evaluated in the course of the electrocatalytic hydrogenation of ketones and enones in aqueous electrolytes. The best results were obtained using nickel-polymer composites synthesized by electroreduction of nickel(II) ions complexed into polycarboxylate films, which are characterized by a high catalytic activity and a good operational stability. (author)
Sun, Ke
2015-03-11
Reactively sputtered nickel oxide (NiOx) films provide transparent, antireflective, electrically conductive, chemically stable coatings that also are highly active electrocatalysts for the oxidation of water to O2(g). These NiOx coatings provide protective layers on a variety of technologically important semiconducting photoanodes, including textured crystalline Si passivated by amorphous silicon, crystalline n-type cadmium telluride, and hydrogenated amorphous silicon. Under anodic operation in 1.0 M aqueous potassium hydroxide (pH 14) in the presence of simulated sunlight, the NiOx films stabilized all of these self-passivating, high-efficiency semiconducting photoelectrodes for >100 h of sustained, quantitative solar-driven oxidation of water to O2(g). © 2015, National Academy of Sciences. All rights reserved.
Shang, Xiao; Yan, Kai-Li; Lu, Shan-Shan; Dong, Bin; Gao, Wen-Kun; Chi, Jing-Qi; Liu, Zi-Zhang; Chai, Yong-Ming; Liu, Chen-Guang
2017-09-01
Developing cost-effective electrocatalysts with both high activity and stability remains challenging for oxygen evolution reaction (OER) in water electrolysis. Herein, based on V-doped nickel sulfide nanowire on nickel foam (NiVS/NF), we further conduct controllable electrodeposition of Fe hydroxides film on NiVS/NF (eFe/NiVS/NF) to further improve OER performance and stability. For comparison, ultrafast chemical deposition of Fe hydroxides on NiVS/NF (uFe/NiVS/NF) is also utilized. V-doping of NiVS/NF may introduce more active sites for OER, and nanowire structure can expose abundant active sites and facilitate mass transport. Both of the two depositions generate amorphous Fe hydroxides film covering on the surface of nanowires and lead to enhanced OER activities. Furthermore, electrodeposition strategy realizes uniform Fe hydroxides film on eFe/NiVS/NF confirmed by superior OER activity of eFe/NiVS/NF than uFe/NiVS/NF with relatively enhanced stability. The OER activity of eFe/NiVS/NF depends on various electrodepositon time, and the optimal time (15 s) is obtained with maximum OER activity. Therefore, the controllable electrodeposition of Fe may provide an efficient and simple strategy to enhance the OER properties of electrocatalysts.
Energy Technology Data Exchange (ETDEWEB)
Melo, M.; Araújo, E. B., E-mail: eudes@dfq.feis.unesp.br [Departamento de Física e Química, Faculdade de Engenharia de Ilha Solteira, UNESP—Univ. Estadual Paulista, 15385-000 Ilha Solteira, SP (Brazil); Shvartsman, V. V. [Institute for Materials Science, University Duisburg-Essen, 45141 Essen (Germany); Shur, V. Ya. [Institute of Natural Sciences, Ural Federal University, 620000 Ekaterinburg (Russian Federation); Kholkin, A. L. [Institute of Natural Sciences, Ural Federal University, 620000 Ekaterinburg (Russian Federation); Department of Physics and CICECO—Aveiro Institute of Materials, University of Aveiro, 3810-193 Aveiro (Portugal)
2016-08-07
Polycrystalline lanthanum lead zirconate titanate (PLZT) thin films were deposited on Pt/TiO{sub 2}/SiO{sub 2}/Si substrates to study the effects of the thickness and grain size on their structural and piezoresponse properties at nanoscale. Thinner PLZT films show a slight (100)-orientation tendency that tends to random orientation for the thicker film, while microstrain and crystallite size increases almost linearly with increasing thickness. Piezoresponse force microscopy and autocorrelation function technique were used to demonstrate the existence of local self-polarization effect and to study the thickness dependence of correlation length. The obtained results ruled out the bulk mechanisms and suggest that Schottky barriers near the film-substrate are likely responsible for a build-in electric field in the films. Larger correlation length evidence that this build-in field increases the number of coexisting polarization directions in larger grains leading to an alignment of macrodomains in thinner films.
Energy Technology Data Exchange (ETDEWEB)
Wu, Jianguo [State Key Laboratory of Cultivation Base for Photoelectric Technology and Functional Materials, Laboratory of Optoelectronic Technology of Shaanxi Province, National Center for International Research of Photoelectric Technology & Nano-functional Materials and Application, Institute of Photonics and Photon-Technology, Northwest University, Xi’an 710069 (China); Physics Department, Northwest University, Xi’an 710069 (China); Wang, Kaige, E-mail: wangkg@nwu.edu.cn [State Key Laboratory of Cultivation Base for Photoelectric Technology and Functional Materials, Laboratory of Optoelectronic Technology of Shaanxi Province, National Center for International Research of Photoelectric Technology & Nano-functional Materials and Application, Institute of Photonics and Photon-Technology, Northwest University, Xi’an 710069 (China); Zhou, Yukun; Wang, Shuang; Zhang, Chen [State Key Laboratory of Cultivation Base for Photoelectric Technology and Functional Materials, Laboratory of Optoelectronic Technology of Shaanxi Province, National Center for International Research of Photoelectric Technology & Nano-functional Materials and Application, Institute of Photonics and Photon-Technology, Northwest University, Xi’an 710069 (China); Wang, Guiren [State Key Laboratory of Cultivation Base for Photoelectric Technology and Functional Materials, Laboratory of Optoelectronic Technology of Shaanxi Province, National Center for International Research of Photoelectric Technology & Nano-functional Materials and Application, Institute of Photonics and Photon-Technology, Northwest University, Xi’an 710069 (China); Mechanical Engineering Department & Biomedical Engineering Program, University of South Carolina, Columbia SC 29208 (United States); and others
2016-12-30
Highlights: • One kind of large area nano-PAA-ZnCl{sub 2} composite film is fabricated, its dimension and morphology is controllable. The properties of nano-composite films have been heavily influenced by the concentration of initial ZnCl{sub 2} solution, the depth of nano-PAAM substrate and the growth time of ZnCl{sub 2} crystals. • At room temperature, the nano-PAA-ZnCl{sub 2} film has the same excitation center (335 nm) and emission center (430 nm) as the nano-PAAM substrate, and the PL intensities can be doubly enhanced. • After annealing at 500 °C, the emission peak spectra of the nano-composite films stabilized at 385 nm, 402 nm, and 430 nm. - Abstract: One kind of ZnCl{sub 2} nano-films with controllable dimension and morphology is successfully synthesized on the top surface of nano-porous anodic alumina membrane (nano-PAAM) by self-organized method. The nano-PAA-ZnCl{sub 2} composite films are characterized by field emission scanning electron microscopy, energy dispersive spectrometer, and laser confocal Raman spectroscopy. The results indicate that the concentration of initial ZnCl{sub 2} solution, the depth of nano-PAAM substrate and the growth time of ZnCl{sub 2} crystals have important influences on the properties of nano-composite films. Furthermore, the characteristics of nano-composites such as the photoluminescence (PL) spectra are investigated. Compared with the nano-PAAM substrate, at room temperature, all of the nano-PAA-ZnCl{sub 2} composite films have both the same excitation center (335 nm) and emission center (430 nm), no matter what the nano-composite morphologies being; and the PL intensity of nano-PAA-ZnCl{sub 2} composite films are all enhanced and the maximum enhancement is two times; after annealing at 500 °C, the emission spectra of the nano-composite films stabilized at the 385 nm, 402 nm and 430 nm. The research provides a new, simple, economical and practical technology to fabricate nano-PAA composite films with higher
Energy Technology Data Exchange (ETDEWEB)
Michaelson, Sh.; Akhvlediani, R. [Schulich Faculty of Chemistry, Technion-Israel Institute of Technology, Haifa 32000 (Israel); Petit, T.; Girard, H.A.; Arnault, J.C. [CEA, LIST, Diamond Sensors Laboratory, F-91191 Gif sur Yvette (France); Hoffman, A., E-mail: choffman@tx.technion.ac.il [Schulich Faculty of Chemistry, Technion-Israel Institute of Technology, Haifa 32000 (Israel)
2014-06-01
Nano-diamond films composed of 3–10 nm grains prepared by the detonation method and deposited onto silicon substrates by drop-casting were examined by high resolution electron energy loss spectroscopy (HR-EELS), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and secondary ion mass spectroscopy (SIMS). The impact of (i) ex-situ ambient annealing at 400 °C and (ii) ex-situ hydrogenation on hydrogen bonding and its thermal stability were examined. In order to clarify the changes in hydrogen bonding configuration detected on the different surfaces as a function of thermal annealing, in-situ hydrogenation by thermally activated atomic hydrogen was performed and examined. This study provides direct evidence that the exposure to ambient conditions and medium temperature ambient annealing have a pronounced effect on the hydrogen-carbon bonding configuration onto the nano-diamond surfaces. In-situ 1000 °C annealing results in irreversible changes of the film surface and partial nano-diamond silicidation.
Magnetic properties of electroplated nano/microgranular NiFe thin films for rf application
Zhuang, Y.; Vroubel, M.; Rejaei, B.; Burghartz, J.N.; Attenborough, K.
2005-01-01
A granular NiFe thin film with large in-plane magnetic anisotropy and high ferromagnetic-resonance frequency developed for radio-frequency integrated circuit (IC) applications is presented. During the deposition, three-dimensional (3D) growth occurs, yielding NiFe grains (? ? 1.0??m). Nanonuclei (?
Sachan, Priyanka; Kulkarni, Manish; Sharma, Ashutosh
2015-11-17
Photoresists are the materials of choice for micro/nanopatterning and device fabrication but are rarely used as a self-assembly material. We report for the first time a novel interplay of self-assembly and photolithography for fabrication of hierarchical and ordered micro/nano structures. We create self-organized structures by the intensified dewetting of unstable thin (∼10 nm to 1 μm) photoresist films by annealing them in an optimal solvent and nonsolvent liquid mixture that allows spontaneous dewetting to form micro/nano smooth dome-like structures. The density, size (∼100 nm to millimeters), and curvature/contact angle of the dome/droplet structures are controlled by the film thickness, composition of the dewetting liquid, and time of annealing. Ordered dewetted structures are obtained simply by creating spatial variation of viscosity by ultraviolet exposure or by photopatterning before dewetting. Further, the structures thus fabricated are readily photopatterned again on the finer length scales after dewetting. We illustrate the approach by fabricating several three-dimensional structures of varying complexity with secondary and tertiary features.
International Nuclear Information System (INIS)
Kawano, Hiroyasu; Morikawa, Takeshi; Matsumoto, Koji; Shono, Keiji
2004-01-01
The film structures, magnetic properties, and noise characteristics of soft magnetic multilayers with alternately stacked FeCSi soft magnetic layers and non-magnetic intermediate layers were investigated. The FeCSi layers in an as-deposited multilayer with C or Ta intermediate layers had the same nano-sized fine crystalline grains and low media noise as an as-deposited FeCSi monolayer. Amorphous C intermediate layers suppressed the amplitude of spike noise especially well. In contrast, FeCSi layers in an as-deposited multilayer with Cr or Ti intermediate layers were composed of coarse crystalline grains, which increased the media noise. The crystallographic match at the interface between the layers in a multilayer could explain these phenomena. The similarity of the atomic arrangement at the interface between layers and the crystallographic match of less than a few percent for the distance between atoms crystallized FeCSi layers with nano-sized fine crystalline grains into ones with coarse crystalline grains during deposition
Twardoch, Marek; Messai, Youcef; Vileno, Bertrand; Hoarau, Yannick; Mekki, Djamel E.; Felix, Olivier; Turek, Philippe; Weiss, Jean; Decher, Gero; Martel, David
2018-06-01
An experimental approach involving electron paramagnetic resonance is proposed for studying photo-generated reactive species in semiconductor nano-particle-based films deposited on the internal wall of glass capillaries. This methodology is applied here to nano-TiO2 and allows a semi-quantitative analysis of the kinetic evolutions of radical production using a spin scavenger probe.
Tunable silver-shell dielectric core nano-beads array for thin-film solar cell application
Energy Technology Data Exchange (ETDEWEB)
Chou Chau, Yuan-Fong, E-mail: a0920146302@gmail.com, E-mail: chou.fong@ubd.edu.bn; Lim, Chee Ming [Universiti Brunei Darussalam, Centre for Advanced Material and Energy Sciences (Brunei) (Brunei Darussalam); Chiang, Chien-Ying [National Taipei University of Technology, Department of Electro-Optical Engineering (China); Voo, Nyuk Yoong; Muhammad Idris, Nur Syafi’ie; Chai, Siew Ung [Universiti Brunei Darussalam, Centre for Advanced Material and Energy Sciences (Brunei) (Brunei Darussalam)
2016-04-15
The absorbance spectra of thin-film solar cells (TFSCs) can be enhanced by constructing the tunable periodic Ag-shell nano-bead (PASNB) arrays in the active material. In this paper, we investigated a plasmonic thin-film solar cell (TFSC) which composed of the arrays of PASNB deposited onto a crystalline silicon layer. By performing three-dimensional finite element method, we demonstrate that near field coupling among the PASNB arrays results in SPR modes with enhanced absorbance and field intensity. The proposed structure can significantly enhance the plasmonic activity in a wide range of incident light and enlarge working wavelength of absorbance in the range of near-UV, visible and near-infrared. We show that the sensitivity of the PASNB arrays reveals a linear relationship with the thickness of Ag-shell nano-bead (ASNB) for both the anti-bonding and bonding modes in the absorbance spectra. The broadband of absorbance spectra could be expanded as a wide range by varying the thickness of ASNB while the particle size is kept constant. Simulation results suggest this alternative scheme to the design and improvements on plasmonic enhanced TFSCs can be extended to other nanophotonic applications.
Wang, Song; Liao, Zhenhua; Liu, Yuhong; Liu, Weiqiang
2015-11-01
Three thin films (DLC, a-C, and TiN) were performed on Ti6Al4V by chemical vapor deposition. Carbon ion implantation was pretreated for DLC and a-C films while Ti transition layer was pretreated for TiN film to strengthen the bonding strength. X-ray diffraction, Raman measurement, nano-hardness and nano-scratch tester, and cross-section etching by FIB method were used to analyze film characteristics. Tribological behaviors of these coatings were studied by articulation with both ZrO2 and UHMWPE balls using ball-on-disk sliding. The thickness values reached ~0.46, ~0.33, and ~1.67 μm for DLC, a-C, and TiN film, respectively. Nano-hardness of the coatings compared with that of untreated and bonding strength (critical load in nano-scratch test) values of composite coatings compared with that of monolayer film all increased significantly, respectively. Under destructive test (ZrO2 ball conterface) in bovine serum lubrication, TiN coating revealed the best wear resistance while DLC showed the worst. Film failure was mainly attributed to the plowing by hard ZrO2 ball characterized by abrasive and adhesive wear. Under normal test (UHMWPE ball conterface), all coatings showed significant improvement in wear resistance both in dry sliding and bovine serum lubrication. Both DLC and a-C films showed less surface damage than TiN film due to the self-lubricating phenomenon in dry sliding. TiN film showed the largest friction coefficient both in destructive and normal tests, devoting to the big TiN grains thus leading to much rougher surface and then a higher value. The self-lubricating film formed on DLC and a-C coating could also decrease their friction coefficients. The results indicated that three coatings revealed different wear mechanisms, and thick DLC or a-C film was more promising in application in lower stress conditions such as artificial cervical disk.
Grain-boundary engineering applied to grain growth in a high temperature material
International Nuclear Information System (INIS)
Huda, Z.
1993-01-01
Crystallography of grain boundaries are determined for a high temperature material, before and after grain growth processes, so as to study the induction of special properties useful for application in components of a gas-turbine engine. The philosophy of grain-boundary engineering is applied to grain growth in APK-6, a powder formed nickel-base superalloy so as to establish the possible structure/property relationships. The alloy in the as received condition is shown to possess a strong texture and contained coincident site lattices (CSL) boundaries with most boundaries having sigma values in the range of 3 > sigma > 25. A normal grain-growth heat treatment result in a good population of low angle grain boundaries, and drastically reduces the proportion of CSL boundaries. A strong [011] annealing texture is observed after an intermediate grain growth; most grain boundaries, here, tend to be high angle indicating a possibility of possessing special properties. (author)
International Nuclear Information System (INIS)
Charpin, P.; Hauptman, A.
1960-01-01
The method employed is based upon the comparison between computed and measured intensities for conveniently selected X-Ray diffraction lines of each component of the powder. Care must be taken to allow for absorption, both inside each grain and in overall sample. This method has been applied to the determination of nickel oxide and fluoride in a nickel powder. (author) [fr
Na-assisted grain growth in CZTS nanoparticle thin films for solar cell applications
DEFF Research Database (Denmark)
Engberg, Sara Lena Josefin; Crovetto, Andrea; Hansen, Ole
2017-01-01
signal increased by a factor of 200 after Na-inclusion. Without Na, the grains were very difficult to sinter, the film was porous, and the photoluminescence was low. A concentration of Na/(Cu+Zn+Sn)=30% was necessary for the densification of the absorber, which is significantly higher than that used...
Sarkar, Arup; Suresh, K. A.
2018-04-01
We find negative differential resistance (NDR) at room temperature in ultrathin films of nickel (II) 1,4,8,11,15,18,22,25-octabutoxy-29H,31H-phthalocyanine [NiPc(OBu)8] deposited on highly ordered pyrolytic graphite (HOPG) substrate [NiPc(OBu)8/HOPG] and NiPc(OBu)8 on graphene oxide (GO) deposited on HOPG [NiPc(OBu)8/GO/HOPG]. For the NiPc(OBu)8/HOPG system, NiPc(OBu)8 was transferred four times onto HOPG by the Langmuir-Blodgett (LB) technique. We have prepared a stable Langmuir monolayer of amphiphilic GO at the air-water interface and transferred it onto HOPG by the LB technique. Further, the monolayer of NiPc(OBu)8 was transferred four times for good coverage on GO to obtain the NiPc(OBu)8/GO/HOPG system. The current-voltage characteristics were carried out using a current sensing atomic force microscope (CSAFM) with a platinum (Pt) tip that forms Pt/NiPc(OBu)8/HOPG and Pt/NiPc(OBu)8/GO/HOPG junctions. The CSAFM, UV-visible spectroscopy, and cyclic voltammetry studies show that the NDR effect occurs due to molecular resonant tunneling. In the Pt/NiPc(OBu)8/GO/HOPG junction, we find that due to the presence of GO, the features of NDR become more prominent. Also, GO causes a shift in NDR voltage towards a lower value in the negative bias direction. We attribute this behavior to the role of GO in injecting holes into the NiPc(OBu)8 film.
Formation of Au nano-patterns on various substrates using simplified nano-transfer printing method
Kim, Jong-Woo; Yang, Ki-Yeon; Hong, Sung-Hoon; Lee, Heon
2008-06-01
For future device applications, fabrication of the metal nano-patterns on various substrates, such as Si wafer, non-planar glass lens and flexible plastic films become important. Among various nano-patterning technologies, nano-transfer print method is one of the simplest techniques to fabricate metal nano-patterns. In nano-transfer printing process, thin Au layer is deposited on flexible PDMS mold, containing surface protrusion patterns, and the Au layer is transferred from PDMS mold to various substrates due to the difference of bonding strength of Au layer to PDMS mold and to the substrate. For effective transfer of Au layer, self-assembled monolayer, which has strong bonding to Au, is deposited on the substrate as a glue layer. In this study, complicated SAM layer coating process was replaced to simple UV/ozone treatment, which can activates the surface and form the -OH radicals. Using simple UV/ozone treatments on both Au and substrate, Au nano-pattern can be successfully transferred to as large as 6 in. diameter Si wafer, without SAM coating process. High fidelity transfer of Au nano-patterns to non-planar glass lens and flexible PET film was also demonstrated.
Energy Technology Data Exchange (ETDEWEB)
Eren, B. [Department of Physics, University of Basel, Klingelbergstrasse 82, CH-4056 Basel (Switzerland); Material Sciences Division, Lawrence Berkeley National Laboratory, 1 Cyclotron Road, Berkeley, California 94720 (United States); Gysin, U.; Marot, L., E-mail: Laurent.marot@unibas.ch; Glatzel, Th.; Steiner, R.; Meyer, E. [Department of Physics, University of Basel, Klingelbergstrasse 82, CH-4056 Basel (Switzerland)
2016-01-25
Few layer graphene and graphite are simultaneously grown on a ∼100 nm thick polycrystalline nickel film. The work function of few layer graphene/Ni is found to be 4.15 eV with a variation of 50 meV by local measurements with Kelvin probe force microscopy. This value is lower than the work function of free standing graphene due to peculiar electronic structure resulting from metal 3d-carbon 2p(π) hybridization.
Effect of milling on the damping behavior of nano-structured copper
Energy Technology Data Exchange (ETDEWEB)
Srikanth, Narasimalu; Thein, Maung Aye; Gupta, Manoj
2004-02-05
In the present study, elemental Cu powder was mechanically milled (MMed) for 10 h to reduce the grain (crystalline) size in the nano-range (<100 nm). The mechanically milled powder (10 h-MMed) and elemental powder without mechanical milling (MM) (0 h-MMed) was consolidated by die-cold compaction and were further hot extruded at different temperatures to maintain a crystallite size within the nano-range. Further, the specimen was tested by a novel free-free type suspended beam arrangement, coupled with circle-fit approach to determine damping characteristics. The characterization results help to understand the effect of the nano-size grains on the overall damping capacity of the bulk samples compared to a normal micro-crystalline sample. Results show that the damping capacity of the nano-grained material increases due to the presence of process induced microstructural changes similar to the damping behavior of a micro-grain sized specimen.
Directory of Open Access Journals (Sweden)
Chuan Du
2012-06-01
Full Text Available New approach is presented for growth of pentacene crystalline thin film with large grain size. Modification of dielectric surfaces using a monolayer of small molecule results in the formation of pentacene thin films with well ordered large crystalline domain structures. This suggests that pentacene molecules may have significantly large diffusion constant on the modified surface. An average hole mobility about 1.52 cm2/Vs of pentacene based organic thin film transistors (OTFTs is achieved with good reproducibility.
Early stages of oxidation of ion-implanted nickel at high temperature
International Nuclear Information System (INIS)
Peide, Z.; Grant, W.A.; Procter, R.P.M.
1981-01-01
The early stages of oxidation of nickel implanted with nickel, chromium, or lithium ions in oxygen at 1100 0 C have been studied using various electron-optical techniques. The unimplanted metal develops initially a fine-grained, convoluted scale having a ridged, cellular structure. Subsequently, the oxide grains increase in size significantly and oxidation becomes predominantly controlled by diffusion of Ni /sup 2+/ ions across a compact, columnar scale. Implantation of the surface with nickel ions has no significant effect on the initial oxidation behavior. However, after implantation with chromium or lithium ions, the development of the NiO scale is, in the early stages of oxidation, suppressed by formation of NiCr 2 O 4 or LiO 2 nodules, respectively. Subsequently, the implanted species are incorporated into the steady-state NiO scale where they dope the oxide and thus influence the diffusion rate of Ni /sup 2+/ ions through it. As would be predicted, the steady-state oxidation rate of chromium-implanted nickel is increased while that of lithium- implanted nickel is decreased compared with that of the unimplanted metal
Directory of Open Access Journals (Sweden)
Jian Hao
2017-10-01
Full Text Available Cellulose insulation polymer (paper/pressboard has been widely used in high voltage direct current (HVDC transformers. One of the most challenging issues in the insulation material used for HVDC equipment is the space charge accumulation. Effective ways to suppress the space charge injection/accumulation in insulation material is currently a popular research topic. In this study, an aluminium oxide functional film was deposited on a cellulose insulation pressboard surface using reactive radio frequency (RF magnetron sputtering. The sputtered thin film was characterized by the scanning electron microscopy/energy dispersive spectrometer (SEM/EDS, X-ray photoelectron spectroscopy (XPS, and X-ray diffraction (XRD. The influence of the deposited functional film on the dielectric properties and the space charge injection/accumulation behaviour was investigated. A preliminary exploration of the space charge suppression effect is discussed. SEM/EDS, XPS, and XRD results show that the nano-structured Al2O3 film with amorphous phase was successfully fabricated onto the fibre surface. The cellulose insulation pressboard surface sputtered by Al2O3 film has lower permittivity, conductivity, and dissipation factor values in the lower frequency (<103 Hz region. The oil-impregnated sputtered pressboard presents an apparent space-charge suppression effect. Compared with the pressboard sputtered with Al2O3 film for 90 min, the pressboard sputtered with Al2O3 film for 60 min had a better space charge suppression effect. Ultra-small Al2O3 particles (<10 nm grew on the surface of the larger nanoparticles. The nano-structured Al2O3 film sputtered on the fibre surface could act as a functional barrier layer for suppression of the charge injection and accumulation. This study offers a new perspective in favour of the application of insulation pressboard with a nano-structured function surface against space charge injection/accumulation in HVDC equipment.
International Nuclear Information System (INIS)
Karenko, M.K.
1981-01-01
A specification is given for iron-nickel-chromium age-hardenable alloys suitable for use in fast breeder reactor ducts and cladding, which utilize the gamma-double prime strengthening phase and are characterized in having a delta or eta phase distributed at or near grain boundaries. A range of compositions is given. (author)
Riastuti, R.; Ramadini, C.; Siallagan, S. T.; Rifki, A.; Herdino, F.
2018-04-01
The addition of sodium citrate to nickel electroplating process as additive is useful for refining the grain size of nickel deposit. The refining of grain size in nickel deposit as coating layer can improve surface performance, one of which corrosion resistance. This paper aims to investigate the effect of sodium citrate addition as grain refiner to promote corrosion resistance on SPCC steel. This experiment used Watt’s Bath solution of NiSO4 300 g/L, NiCl4 45 g/L, H3BO3 60 g/L, wetting agent 0.2 cc/L. Sodium citrate was added in composition of 45g/L and 60g/L. Nickel were deposited by direct current using current density on 6 A/dm2 at the acidity level of 5 for 30 minutes by keeping the operating temperature stable at 50°C. The grain size of nickel deposit was observed through Optical Microscope and Atomic Force Microscope (AFM). The corrosion behavior of SPCC was observed by linear polarization and Electrochemical Impedance Spectroscopy (EIS) methods using 3% NaCl solution. Based on the research, the addition of sodium citrate as grain refiner will increasing corrosion resistance on SPCC steel from 0.35 to 0.05 mm/year.