Análise cristalográfica da solução sólida com estrutura tipo Tungstênio Bronze de niobato de potássio e estrôncio dopado com ferro/ Crystallographic analysis of the solid solution of iron doped potassium strontium niobate with tetragonal tungsten bronze structure

Lanfredi, Silvania; Nobre, Marcos A. L.; Lima, Alan R. F.
2010-01-01

Resumo em inglês Solid solution of iron doped potassium strontium niobate with KSr2(FeNb4)O15-Δ stoichiometry was prepared by high efficiency ball milling method. Structural characterization was carried out by X-ray diffraction. Crystalline structure was analyzed by the Rietveld refinements using the FullProf software. The results showed a tetragonal system with the tetragonal tungsten bronze structure - TTB (a = 12.4631 (2) Å and c = 3.9322 (6) Å, V = 610.78 (2) ų). In this wor (mais) k, the sites occupancy by the K+, Sr2+ and Fe3+ cations on the TTB structure were determined. NbO6 polihedra distortion and its correlation with the theoretical polarization are discussed.

Scientific Electronic Library Online (Portuguese)

2

Fotocromismo em filmes finos de óxidos de tungstênio de diferentes composições/ Photochromism in tungsten oxide thin films of different compositions

Galvão, José R.; Scarminio, Jair
2003-08-01

Resumo em inglês Tungsten oxide thin films with three different compositions were deposited by reactive sputtering in an oxygen-argon plasma. In a system composed of a home made photochemical reactor coupled with an optic fiber spectrophotometer, the photochromic effect was studied in these oxide films as function of UV irradiation time, in ethanol, methanol and formaldehyde atmospheres. It was observed that the photochromic efficiency depends on the vapor chemical nature where the film i (mais) s irradiated as well as the film composition. Kinetic analysis suggest that two kinds of optical absorption centers should respond by the photochromic effect in these films, one generated at film surface and other inside it, which one presenting a different time constant.

Scientific Electronic Library Online (Portuguese)

3

Espectrometria de absorção atômica com atomização eletrotérmica em filamento de tungstênio: uma re-visão crítica/ Electrothermal atomic absorption spectrometry with tungsten coil: a critical re-view

Ribeiro, Anderson Schwingel; Arruda, Marco Aurélio Zezzi; Cadore, Solange
2002-05-01

Resumo em inglês In this review it is presented some aspects of electrothermal atomic absorption spectrometry with tungsten coil (ETAW-AAS) since its beginning until the present days as well as the perspectives for this technique. Some aspects concerning its development and theoretical concepts are discussed. The analytical figures of merit such as limit of detection (LD), characteristic mass (m0), relative standard deviation (RSD), accuracy and precision are evaluated, compared and discu (mais) ssed considering published works. It is also evaluated its advantages, applications, limitations and instrumental development. The use of diode laser as radiation source and its perspectives to ETAW are also discussed.

Scientific Electronic Library Online (Portuguese)

4

Síntese e caracterização estrutural do niobato de potássio e estrôncio com estrutura tipo Tetragonal Tungstênio Bronze TTB/ Synthesis and structural characterization of strontium potassium niobate oxide with tetragonal tungstenium bronze TTB type structure

Lanfredi, S.; Trindade, L. R.; Barros, A. R.; Feitosa, N. R.; Nobre, M. A. L.
2005-06-01

Resumo em português A fase nanoestruturada KSr2Nb5O15, foi sintetizada pelo método de mistura mecânica de óxidos por moagem de alta eficiência e por via química, utilizando o método dos precursores poliméricos, em forno tipo tubo sob atmosfera de O2 durante 10 h. A análise por difração de raios X dos pós calcinados a 1150 ºC foi realizada pelo método de Rietveld utilizando-se o software FullProf. A análise dos parâmetros estruturais obtidos via método de Rietveld mostrou um s (mais) istema tetragonal com estrutura tipo tetragonal tungstênio bronze. A partir das reflexões observadas, há apenas evidência da regra [(0kl) k = 2n], a qual é compatível com o grupo espacial centrossimétrico P4bm, o qual foi utilizado para o refinamento. O volume da célula unitária obtido na análise dos pós de KSr2Nb5O15 obtidos por síntese química e por moagem de alta eficiência foi 611,90 ų e 611,95 ų, respectivamente. Resumo em inglês The nanostructured KSr2Nb5O15 phase was synthesized by both routes, the high efficiency milling and the polymeric precursor, in a furnace under O2 atmosphere during 10 h. The Rietveld X-ray diffraction analysis of the calcined powders at 1150 ºC was performed using the FullProf software. The XRD pattern analysis showed a tetragonal system with the tetragonal tungsten bronze structure. From the observed reflections, there is only evidence of the rule existence [(0kl) k = (mais) 2n], which is compatible with the centrosymmetric space group P4bm, which was used for the refinement. The unit cell volume obtained for the KSr2Nb5O15 powders prepared by chemical synthesis and by high efficiency milling were equal to 611,90 ų and 611,95 ų, respectively.

Scientific Electronic Library Online (Portuguese)

5

Caracterização ultra-sônica de materiais ferroelétricos com estrutura perovskita e tungstênio-bronze/ Ultrasonic characterization of perovskite and tungsten-bronze ferroelectric materials

Moreno-Gobbi, A.; Paolini, G.; Pérez, M.; Negreira, C. A.; Garcia, D.; Eiras, J. A.
2002-03-01

Resumo em português Atenuação e velocidade ultra-sônicas e, consequentemente, o módulo de Young de cerâmicas ferroelétricas com estrutura do tipo perovskita e tungstênio-bronze foram medidas entre 2,5 e 30 MHz, à temperatura ambiente, utilizando-se a técnica de pulso-eco. Composições com e sem chumbo foram testadas, mostrando que a presença do cátion Pb2+ representa fator importante no comportamento da atenuação. A dependência da atenuação com a freqüência é mais acentua (mais) da no caso dos ferroelétricos com estrutura perovskita. As discussões são baseadas nos modelos de espalhamento por grãos/poros em materiais policristalinos. Resumo em inglês Ultrasonic attenuation and velocity of ferroelectric ceramics with perovskite and tungsten-bronze structures were measured in a range of 2.5 to 30 MHz at room temperature, using the pulse-echo-overlap technique. Lead and non-lead compositions were analyzed, revealing that Pb2+ in the lattice affects the attenuation behavior. The frequency dependence of attenuation is clearly stronger for the lead materials with perovskite structure. The discussions are based on a qualitative analysis of grain/pore scattering models for polycrystalline materials

Scientific Electronic Library Online (Portuguese)

6

Construção de espectrômetro de emissão atômica com atomização eletrotérmica em filamento de tungstênio (WCAES)/ Construction of a tungsten coil atomic emission spectrometer (WCAES)

Gonzalez, Mário H.; Santos, Luana N.; Nóbrega, Joaquim A.; Rocha, Fábio R. P.
2010-01-01

Resumo em inglês It is here discussed the development of a low cost analytical instrument with capacity for metals determination using atomic emission measurements in an electrothermal atomization system with a tungsten coil atomizer. The main goal was to show a new frontier for using this atomizer and to demonstrate that the simple instrumental arrangement here proposed has potential for portability and for solving analytical tasks related to metals determination. Atomic emission of calc (mais) ium was selected for the adjustment of instrumental parameters and to evaluate the main characteristics of the lab-built instrument. Cobalt was determined in medicines and one alloy to demonstrate its feasibility.

Scientific Electronic Library Online (Portuguese)

7

Avaliacão de programas de aquecimento para espectrometria de absorção atômica com atomizacão eletrotérmica em filamento de tungstênio/ Evaluation of heating programs for electrothermal atomic absorption spectrometry using a tungsten coil

Oliveira, Pedro V.; Catanho, Marciana; Nóbrega, Joaquim A.; Luccas, Pedro O.
2000-10-01

Resumo em inglês A tungsten coil atomizer was used to investigate the effect of heating programs with constant or variable drying temperatures on the atomization of Al, Cd, Cr and Pb. The variation of the surface temperature in the tungsten coil furnace can occur during each heating step due to the design of the power supply, that may apply constant voltages during a programmed time. For volatile elements (Cd), losses in sensitivity were observed when the program with a variable temperatu (mais) re was used. On the other hand, these effects are negligible for less volatile elements (Al and Cr) and any tested program, in different acidic media, could be used without appreciable changes in sensitivities. The results allow the establishment of proper heating programs for elements with different thermochemical behavior in the tungsten coil atomizer.

Scientific Electronic Library Online (Portuguese)

8

Avaliação da tenacidade à fratura através do ensaio de indentação em pastilhas de metal duro/ Evaluation of fracture toughness by indentation testing in hardmetal tools

Dias, A.M.S.; Miranda, J.S.; Godoy, G.C.
2009-08-01

Resumo em português O teste de indentação Vickers tem sido muito utilizado para avaliação da dureza superficial em diferentes tipos de materiais. Devido à sua versatilidade, esta metodologia também é utilizada para avaliar diferentes propriedades mecânicas, como o módulo de Young (E) e a tenacidade à fratura (K IC), principalmente em materiais sinterizados como, por exemplo, o carboneto de tungstênio com cobalto (WC-Co). Este material é usado na fabricação de ferramentas de cor (mais) te, uma vez que possui altas dureza e resistência à compressão, porém baixa tenacidade à fratura, diminuindo sua vida útil quando submetido a severas condições de desgastes. Entretanto, devido a essas características mecânicas peculiares, o WC-Co apresenta análise difícil através dos ensaios convencionais, principalmente para avaliação da tenacidade à fratura. Por isso, o objetivo do presente trabalho foi avaliar experimentalmente a dureza e a tenacidade à fratura de duas pastilhas comerciais de carboneto de tungstênio contendo cobalto a partir do ensaio Vickers. Um procedimento simples e barato de preparação da amostra consistiu de um polimento seletivo foi utilizado com o intuito de se evitar tensões residuais superficiais. Em seguida, avaliou-se a distribuição dos carbonetos de tungstênio na matriz de cobalto através da microscopia eletrônica de varredura (MEV). Os resultados desta análise mostraram uniformidade na dispersão do carboneto de tungstênio na matriz de cobalto, indicando que o processo de preparação da amostra não acarretou grandes tensões residuais superficiais. Determinaram-se os valores de dureza e de tenacidade à fratura das pastilhas estudadas e estes resultados se mostraram de acordo com os dados encontrados na literatura. Resumo em inglês The Vickers indentation testing is commonly used for hardness surface measurement for different types of materials. This testing method is quite versatile and it is used to evaluate different mechanical properties, such as Young modulus (E) and fracture toughness (KIC), particularly in sintered materials like the tungsten carbide with cobalt (WC-Co). This material is used in the manufacturing of cutting tools, once it has very high surface hardness and also compression st (mais) rength, although low fracture toughness values, which decreases its service life when submitted to high wear conditions. However, due to those peculiar mechanical properties, the WC-Co presents difficult analysis through conventional testing techniques, mainly considering fracture toughness evaluation. For that reason, the aim of this work was to evaluate experimentally the hardness and fracture toughness in two commercial tools, made of tungsten carbide with cobalt, through Vickers indentation testing. A simple and low cost procedure of sample preparation was used, consisted of a selective polishing, in order to avoid superficial residual stresses. In sequence, the scanning electron microscope (SEM) was used to evaluate the distribution of tungsten carbide in the cobalt matrix. The results of this analysis have shown uniformity in the tungsten carbide dispersion in the cobalt matrix, indicating that the sample preparation process did not create great values of superficial residual stresses. The experimental hardness and fracture toughness values were obtained, which have agreed with the ones found in the literature.

Scientific Electronic Library Online (Portuguese)

9

Compostos heterometálicos. Interação do tricarbonil com ligação W-Hg, [WCl(CO)3(bipy)(HgCl)], com tiouréias/ Heterometallic compounds. Interaction of the tricarbonyl containing W-Hg bond, [WCl(CO)3(bipy)(HgCl)], with thioureas

KAZUKO MURAOKA, Tereza; MAURO, Antonio Eduardo; MARTINS NOGUEIRA, Vânia; HADDAD, Paula Silvia
1997-01-01

Resumo em português Foram efetuadas reações entre o heterometálico [WCl(CO)3(bipy)(HgCl)], (bipy = 2,2'-bipiridina) e tiouréias que levaram à formação de compostos do tipo [WCl(CO)3(bipy)(HgCl)L] [L = tiouréia (tu); N-metiltiouréia (mtu); N,N-dimetiltiouréia (dmtu)]. Os espectros de absorção no infravermelho mostram que a esfera de coordenação do tungstênio mantêm-se inalterada e que as tiouréias encontram-se ligadas ao átomo de mercúrio através do átomo de enxofre. Resumo em inglês Reactions of [WCl(CO)3(bipy)(HgCl)], [bipy = 2,2’-bipyridine], with thioureas were performed giving compounds of the type [WCl(CO)3(bipy)(HgCl)], [L= thiourea (tu); N-methylthiourea (mtu); N,N-dimethylthiourea (dmtu)] in which the coordination sphere of the tungsten atom remained unchanged. The coordination of the thioureas to mercury atom was proved to occur, in accord to infrared spectra, through the sulphur atom.

Scientific Electronic Library Online (Portuguese)

10

Estudo da adsorção de íons fosfato em matriz inorgânica/ Adsorption study of phosphate from aqueous solution in inorganic matrix

Rodrigues, L. A.; Silva, M. L. C. P. da
2008-03-01

Resumo em português Este trabalho visa a preparação, caracterização e estudo da adsorção de íons fosfato em óxido de tungstênio hidratado preparado pela lixiviação ácida do tungstato de sódio. Parte desse material (S1) foi tratado termicamente a 100 °C para a obtenção de um material com características diferenciadas (S1/delta). Os materiais obtidos foram caracterizados por difração de raios X, análise termogravimétrica, microscopia eletrônica de varredura e espectroscop (mais) ia de energia dispersiva. Através da constante Q0, relacionada com a capacidade de adsorção máxima, observou-se que o S1 possui maior capacidade de adsorção para íons fosfato que o S1/delta. Pelos resultados de deltaG, observou-se que os íons fosfato foram adsorvidos através de reações energeticamente favoráveis para toda a faixa de concentração estudada. Resumo em inglês This work reports the preparation, characterization and adsorption study of phosphate on hydrous tungsten oxides prepared by acid lixiviation of sodium tungstate. Part of this material (S1) was heated at 100 °C resulting in a material with differentiated characteristics (S1/delta). The materials prepared were characterized by X-ray diffraction, thermal analysis, scanning electron microscopy and energy dispersive spectroscopy. Through the Q0 constant, related with the cap (mais) acity of maximum adsorption, it was observed that the S1 sample presented better adsorption capacity than the S1/delta. The deltaG values show that PO4-3 had been adsorbed through favorable reactions for all range of studied concentration.

Scientific Electronic Library Online (Portuguese)

11

Densificação e evolução microestrutural de cerâmicas Pb0,59Ba0,41Nb2O 6/ Densification and microstructural evolution of Pb0.59Ba0.41Nb2O 6 ceramics

Santos, I. A.; Arantes, V. L.; Paula, R. N. de; Radovanovic, E.; Eiras, J. A.
2000-09-01

Resumo em português O niobato de bário e chumbo (PBN) possui uma estrutura cristalina do tipo tungstênio-bronze e apresenta propriedades ferroelétricas muito interessantes tanto do ponto de vista científico quanto do ponto de vista tecnológico, revelando-se como um material bastante promissor para aplicação no desenvolvimento de dispositivos eletro-ópticos, piezoelétricos e piroelétricos. Cerâmicas à base de Pb0(0,59)Ba0,41Nb2O 6 (PBN59) foram preparadas pelo método convencional (mais) de mistura de matérias-primas. Duas rotas distintas de densificação de amostras foram utilizadas nesse trabalho: sinterização convencional e sinterização por prensagem uniaxial a quente. As caracterizações microestruturais efetuadas indicaram que as amostras obtidas via prensagem uniaxial a quente apresentam uma distribuição bimodal de tamanhos de grão e elevadas densidades, indicando que essa técnica propicia uma maior eficiência no processo de densificação das amostras. O tratamento térmico pós-prensagem uniaxial a quente induz o macro-crescimento preferencial de grãos orientados. Resumo em inglês Lead barium niobate ferroelectric ceramics have a crystallographic tungsten bronze structure and present interesting ferroelectric properties from both scientific and technological points of view, making them very attractive for electro-optical, SAW and pyroelectric device applications. Ceramics of Pb0(0.59)Ba0.41Nb2O 6 (PBN59) were prepared through conventional mixed precursors method. Two distinct densification routes were employed in this work: conventional firing and (mais) uniaxial hot pressing. The microstructural characterizations indicated that the samples obtained by the latter method present a bimodal grain size distribution and high densities, indicating that this technique is more suitable for obtaining ceramics with high densification rates. The post-pressing annealing induces the preferentially oriented macro grain growth.

Scientific Electronic Library Online (Portuguese)

12

Efeitos do carbono na evolução de segundas-fases e na densificação do nitreto de alumínio com Y2O3/ Effects of carbon on second-phase evolution and densification of aluminum nitride with Y2O3

Molisani, A. L.; Goldenstein, H.; Yoshimura, H. N.
2010-12-01

Resumo em português Foi investigado o efeito da adição do carbono na evolução de segundas-fases e na densificação do AlN com 4% em massa de Y2O3. A mudança de composição da segunda-fase do AlN com Y2O3 foi induzida pela adição de 0,5% e 1,0% em massa de carbono. A sinterização sob atmosfera de nitrogênio foi realizada em forno com elemento resistivo de tungstênio entre 1650 ºC e 1850 ºC. A evolução de segunda-fase mostrou uma tendência para formar fases mais ricas em ítr (mais) io com o aumento do teor de carbono, o que atrasou a densificação do AlN com Y2O3 devido ao aumento da temperatura de formação de fase líquida. O efeito prejudicial causado pela adição de carbono diminuiu com o aumento da temperatura de sinterização, pois todas as amostras atingiram quase completa densificação após sinterização a 1800 ºC. A adição de carbono induziu uma evaporação significativa de compostos durante a sinterização, mas o comportamento de densificação foi pouco influenciado pela redução na fração de fase líquida existente na temperatura de sinterização e pelo gás aprisionado no interior dos poros fechados. Resumo em inglês The effect of carbon addition on the second-phases evolution and on the densification of AlN with 4wt.%.Y2O3 was investigated. The change of second-phase composition of AlN with Y2O3 was induced by the addition of 0.5wt.% and 1.0wt.% carbon. Sintering under nitrogen atmosphere was performed in tungsten heated furnace between 1650 ºC and 1850 ºC. The second-phase evolution had a tendency to form Y-richer phases with increasing carbon content, which delayed the densificat (mais) ion of AlN with Y2O3 due to the increase of liquid-phase formation temperature. The harmful effect caused by the addition of carbon was diminished with increasing sintering temperature, since all samples achieved almost full densification after sintering at 1800 ºC. The addition of carbon induced significant evaporation of compounds during sintering, but the densification behavior was little influenced by the reduction in liquid-phase fraction formed at sintering temperature or the entrapped gas inside the closed pores.

Scientific Electronic Library Online (Portuguese)

13

Remoção de braquetes cerâmicos com alicate de How associado à broca diamantada: avaliação da topografia do esmalte/ Removal of ceramic brackets with How-type pliers in association with diamond drill: a topographic evaluation of the enamel

Pithon, Matheus Melo; Oliveira, Márlio Vinícius de; Ruellas, Antônio Carlos de Oliveira
2008-08-01

Resumo em português OBJETIVO: avaliar a topografia do esmalte dentário após a descolagem de braquetes cerâmicos Allure (GAC/Dentsply) através de dois diferentes métodos. METODOLOGIA: foram utilizados 20 incisivos inferiores permanentes bovinos divididos em dois grupos (n = 10). Em ambos os grupos foram feitas colagens de braquetes cerâmicos Allure utilizando-se Concise (3M Unitek) seguindo as recomendações do fabricante. Após a colagem, os espécimes foram mantidos em estufa, a 37° (mais) C por 24 horas, para completa polimerização do compósito. Após isso foi realizada a remoção dos braquetes, sendo que no grupo A foi utilizado alicate de corte de amarrilho e no grupo B alicate tipo How em braquete previamente fragilizado com broca diamantada. Em ambos os grupos o remanescente de compósito foi removido com broca de carboneto de tungstênio. Após descolagem, os espécimes foram preparados para análise em microscopia eletrônica de varredura, para posterior análise da superfície do esmalte. RESULTADOS E CONCLUSÕES: os resultados mostraram maior quantidade de arranhões nos dentes do grupo A, esses resultados foram estatisticamente superiores ao grupo B com p Resumo em inglês OBJECTIVE: to evaluate the topography of the tooth enamel after debonding Allure ceramic brackets using two different methods. METHODS: Twenty bovine permanent lower incisors were divided into two groups (n = 10). In groups A and B Allure ceramic brackets were bonded to the teeth using Concise composite according to manufacture’s recommendations. After the bonding procedures, the samples were kept in stove at 37ºC for 24 hours for complete composite polymerization. Next (mais) , the brackets of group A were removed by using wire pliers, whereas the brackets of group B, which had been previously weakened with diamond drill, were debonded by using How-type pliers. In both groups the composite remnant was removed by using a tungsten carbide-tipped drill. Following the debonding procedures, the samples were prepared for scanning electronic microscopy so that their enamel surfaces could be analyzed. RESULTS AND COCLUSION: showing more scratch marks on the surfaces of the group A teeth were statistically superior to those found in group B (p

Scientific Electronic Library Online (Portuguese)

14

A influência do tempo de atuação da polaridade positiva na soldagem TIG CA do alumínio/ The influence of positive polarity time on AC-GTAW of aluminum

Cirino, Luciano Machado; Dutra, Jair Carlos
2009-06-01

Resumo em português Neste trabalho, experimentos foram conduzidos para determinar o comportamento de fusão do alumínio 1200 diante do aumento do tempo de atuação da polaridade positiva na soldagem TIG CA deste metal. Para atingir este objetivo, foi desenvolvido um conjunto de experimentos, de tal forma que a intensidade da corrente elétrica na polaridade positiva e negativa foi a mesma; apenas os tempos de duração de cada polaridade eram modificados. Durante os experimentos foram real (mais) izadas aquisições dos sinais de corrente e tensão. Por intermédio destes foi possível determinar a tensão e a potência de arco para cada condição testada. No aspecto comportamento de fusão, um aumento na penetração e nas áreas de fusão foi verificado à medida que maiores tempos de polaridade positiva eram utilizados. Este comportamento difere daquele indicado comumente pela literatura sobre processos de soldagem com eletrodos nãoconsumíveis, que infere uma diminuição na penetração com o aumento do tempo de atuação da polaridade positiva. Entretanto, esta tendência crescente constatada durante os experimentos ocorre a partir de um determinado ponto, onde os tempos de atuação da polaridade positiva são maiores do que 4,0 ms em um período total de 20,0 ms. O uso de um tempo mínimo de polaridade positiva (1,3 ms) mostrou-se eficiente em realizar a limpeza catódica, produziu soldas com características de fusão satisfatórias e com desgaste mínimo do eletrodo de tungstênio. A boa capacidade de fusão obtida em soldas realizadas com altos tempos de atuação da polaridade positiva foi atribuída a fenômenos decorrentes da emissão de elétrons por efeito de campo que ocorre durante as fases de eletrodo positivo. Resumo em inglês In this work, experiments were carried out to determine the fusion behavior of 1200 aluminum with an increase in the positive polarity time in the VP-GTAW of this metal. To achieve this objective, a set of experiments was developed, in such way that the electrical current intensity was the same in both the positive and negative polarity; only the lengths in each polarity were modified. During the experiments the acquisition of the current and voltage signals was performed (mais) . Through these it was possible to determine the arc voltage and power for each condition tested. In relation to the fusion behavior there was an increase in the weld depth and fusion zones when longer positive polarity times were used. This behavior differs from the literature relating to welding processes with non-consumable electrodes, which suggest a decrease in the weld depth with an increase in the positive polarity acting time. However, the increase noticed during the experiments occurs from a certain point, when the positive polarity time is longer than 4.0 ms over a total period of 20.0 ms. The use of a minimal electrode positive time (1.3 ms) was found to be sufficient to perform the oxide removal, yielding weld beads with satisfactory fusion characteristics and with minimal wear of the tungsten electrode. The good melt capacity obtained in the welds carried out with high positive polarity times, was attributed to phenomena related to the field emission of electrons which takes place in the current positive half cycles.

Scientific Electronic Library Online (Portuguese)

15

Análise numérica do ensaio de indentação em materiais com comportamento frágil/ Analysis of pyramidal vickers testing in brittles materials

Dias, A.M.S.; Godoy, G.C.; Modenesi, P.J.
2010-01-01

Resumo em português O ensaio piramidal Vickers é uma técnica utilizada há décadas para avaliação da dureza superficial de materiais metálicos, cerâmicos, compósitos e, recentemente, filmes finos. Diversos estudos têm sido desenvolvidos a fim de utilizar esta metodologia como ferramenta para avaliação de outras propriedades mecânicas como, por exemplo, a tenacidade à fratura. Contudo, a sua implementação na determinação desta propriedade mecânica e os seus resultados ainda (mais) ocasionam dúvidas no meio científico. Estas dúvidas são mais intensas quando se pretende analisar materiais com comportamento frágil. Por isso, utilizou-se um modelo numérico através do método dos elementos finitos para avaliar os campos de tensões e de deformações durante o ciclo de indentação, auxiliando em uma interpretação mais segura deste ensaio. No presente trabalho, obteve-se o comportamento da curva carga versus deslocamento para o ensaio Vickers em uma amostra de carboneto de tungstênio com cobalto e em uma amostra de alumina. Também foram encontrados os valores numéricos da dureza superficial destes dois materiais. Estes resultados se encontram compatíveis com os dados experimentais presentes na literatura especializada, mostrando que o modelo numérico foi capaz de representar o comportamento global deste ensaio. Por fim, foi determinada a distribuição da máxima tensão principal e das deformações para o ciclo de carregamento e descarregamento do teste, utilizando-se um modelo numérico de trinca difusa. Baseado nestes resultados de tensões e de deformações estudou-se os mecanismos de nucleação e de crescimento de trincas que ocorrem nestes materiais sob ensaios de indentação piramidais. Resumo em inglês The experimental indentation testing is a methodology used during decades to obtain the surface hardness of different kinds of materials. Nowadays, these tests have been reported in the literature as a reliable tool for mechanical properties determination, such as hardness, Young modulus, yielding stress and fracture toughness. However, the implementation of this indentation technique to evaluate the mechanical properties and also the results therefrom obtained has still (mais) brought doubts on research areas. These doubts are really intense when they involve problems which aim to analyse the mechanical behaviour of brittle materials. Because of those testing analysis limitations, the use of a numerical technique, able to evaluate the stress and strain fields during the indentation cycle, may help on a more accurate interpretation of the testing. In this study, the numerical simulation of Vickers hardness testing is modelled with three-dimensional elements making use of commercial explicit finite element code. Two different brittle materials were analyzed, tungsten carbide with cobalt and alumina. The numerical analysis indicated that the model represents well the strain and stress fields during the loading and unloading phases of the Vickers indentation cycle. Those results were found to agree well with the experimental trends presented in the literature. Finally, a diffuse crack constitutive model was used to identify the most probable crack nucleation sites that usually occur during real indentation testing.

Scientific Electronic Library Online (Portuguese)

16

Efeito do teor de Y2O3 na sinterização do nitreto de alumínio/ Effect of Y2O3 content on the sintering of aluminum nitride

Molisani, A. L.; Yoshimura, H. N.; Goldenstein, H.
2006-06-01

Resumo em português O Y2O3 é o principal aditivo usado na sinterização de cerâmicas de AlN com elevada condutividade térmica, que são destinadas a produção de dispositivos eletrônicos de alta performance. Neste trabalho, investigou-se o efeito do teor de aditivo na sinterização de AlN com 0,5 a 4% em peso de Y2O3, correlacionado os resultados de densidade, análise microestrutural e a evolução das segundas fases em função da temperatura de sinterização. Os corpos compactados (mais) foram sinterizados em atmosfera de nitrogênio usando um forno com elemento resistivo de tungstênio entre 1650 e 2000 ºC por 1 h. Os resultados mostraram que a densificação das amostras de AlN com até 4% de Y2O3 ocorreu por sinterização no estado sólido até 1700 ºC. Acima desta temperatura, a densificação ocorreu por sinterização assistida por fase líquida. A fusão da fase YAG foi responsável pela formação de líquido ao redor de 1725 ºC nas amostras de AlN com até 4% de Y2O3. A quantidade de fase líquida aumentou em função do teor de aditivo nas amostras somente após a densificação total devido à fusão das partículas grandes refratárias de aluminatos de ítrio (YAP e YAM) em altas temperaturas. Assim, o aumento do teor de Y2O3 (0,5 a 4% em peso) não causou variações significativas no comportamento de densificação do AlN porque a quantidade de fase líquida foi próxima na faixa de temperatura em que ocorreu a densificação. A adição de apenas 0,5% em peso de Y2O3 aumentou significativamente a sinterabilidade do AlN. O uso de Y2O3 com larga distribuição granulométrica em relação a do AlN não causou a formação de poros grandes. Os resultados mostraram uma tendência de evaporação de compostos óxidos nas amostras de AlN com Y2O3 sinterizadas principalmente acima de 1850 ºC. Resumo em inglês Y2O3 is the main sintering aid for high thermal conductivity AlN ceramics for the production of electronic devices. The effect of varying the amount of Y2O3 as sintering aid for AlN from 0.5 to 4 wt% was investigated. The effects of different amounts of Y2O3 were correlated with results of density and microstructural analysis, as well as the evolution of second phases, as a function of sintering temperature. Green bodies were sintered in nitrogen atmosphere using a tungst (mais) en element furnace, between 1650 and 2000 ºC for 1 h. The results showed the densification of AlN samples with Y2O3 by solid state sintering up to 1700 ºC; above this temperature, densification occurred by liquid-phase sintering. The melting of a YAG phase caused the formation of liquid phase at around 1725 ºC, in samples of AlN with up to 4 wt% Y2O3. The amount of liquid-phase increased with increasing sintering aid content only after the full densification of the samples, due to the melting of large refractory particles of yttrium aluminates (YAP and YAM) at high temperatures. As a result, the increase of the Y2O3 content (0.5 to 4 wt%) did not cause significant variations in the densification behavior of the AlN, as the amount of liquid-phase was similar for all temperatures in the range at which densification occurred. The addition of only 0.5 wt% Y2O3 increased significantly the sinterability of AlN. The use of Y2O3 with large particle size distribution in relation to AlN did not cause the formation of large pores. The results showed a trend towards oxide compounds evaporation in AlN samples with Y2O3, when sintered above 1850 ºC.

Scientific Electronic Library Online (Portuguese)

17

Transição de Fase Difusa e Propriedades Dielétricas de Cerâmicas Ferroelétricas de (Pb, Ba)Nb2O6

Santos, I.A.; Arantes, V.L.; Garcia, D.; Eiras, J.A.
2002-03-01

Resumo em inglês Tungsten bonze structured lead barium niobate (Pb1-xBa xNb2O6) ferroelectric ceramics were prepared by the conventional mixed oxide method and their dielectric properties were carefully investigated. All studied samples presented elevated values of maximum dielectric constant (epsilon'm) and its corresponding temperature of maximum (Tm) in comparison with perovskite structured ones. The phase transition features indicate that the PBN samples do not present a complete diff (mais) use phase transition. Indeed, the diffuseness degree of the ferroelectric phase transition is highly dependent of the ions Pb2+ content in the sample compositions. The diffuseness of the ferroelectric phase transition is enhanced while the temperature of maximum dielectric constant is decreased with the Pb2+ content decreasing. In addition, the maximum dielectric constant shows an opposite behavior.

Scientific Electronic Library Online (Portuguese)

18

Investigations of tungsten mine waste geopolymeric binder : strength and microstructure

Torgal, Fernando Pacheco; Gomes, J. P. Castro; Jalali, Said

This paper reports some results of a research project related to the development of a new binder using mineral waste mud from the Portuguese mine. Some aspects related to the effect of aggregates in the microstructure and mechanical behaviour of tungsten mine waste geopolymeric binder are reported i...

DRIVER (Portuguese)

19

Construção de célula eletroquímica para observação de amostras in situ em estereomicroscópio/ Construction of an electrochemical cell to visualize samples in situ in stereomicroscope

Alencar, Mônica Alessandra Silva; Benedetti, Assis Vicente; Fugivara, Cecílio Sadao; Messaddeq, Younès
2010-01-01

Resumo em inglês The electrochemical study of glass like tungsten oxide derivatives requires the construction of special electrodes due to the fact that these glasses are not conductive. Electrodes modified with WO3 change their color when submitted to some potential perturbation. The color change of the electrochromic materials was observed in situ by coupling an electrochemical cell to a stereomicroscope. The constructed cell is versatile and may represent a great contribution to the el (mais) ectrochemical studies of materials, especially in the systems where it is interest to observe the working electrode surface during the electrochemical experiment.

Scientific Electronic Library Online (Portuguese)

20

Caracterização por XPS de filmes passivos formados sobre aços de baixa liga em meio de bicarbonato/ XPS characterization of passive films formed on mild steels in bicarbonate medium

Alves, Valéria Almeida; Brett, Christopher Michael Ashton; Montemor, Maria de Fátima
2005-03-01

Resumo em inglês Passive films formed in bicarbonate solutions on carbon steel, chromium steel and high speed steel have been characterized by XPS. The passive films formed on chromium and high speed steels showed superior protective properties than those formed on carbon steel. It was confirmed by XPS that the steel composition influences the passive film composition. Chromium oxide and hydroxide, as well as molybdenum and tungsten oxides and hydroxides are present in the passive film of (mais) chromium steel and high speed steel, respectively, besides iron oxide and hydroxide. The more complex composition of the oxide film on high speed steel explains its electrochemical behaviour and highest corrosion resistance.

Scientific Electronic Library Online (Portuguese)

21

Caracterização microestrutural de soldas dissimilares dos aços ASTM A-508 e AISI 316L/ Characterization of dissimilar metal weld between low alloy steel ASTM A-508 and 316L stainless steel

Lima, Luciana Iglésias Lourenço; Silva, Guilherme Marconi; Chilque, Angel Raphael Arce; Schvartzman, Mônica Maria de Abreu Mendonça; Bracarense, Alexandre Queiroz; Quinan, Marco Antônio Dutra
2010-06-01

Resumo em português As soldas dissimilares (dissimilar metal welds - DMWs) são utilizadas em diversos segmentos da indústria. No caso específico de usinas nucleares, tais soldas são necessárias para conectar tubulações de aço inoxidável com componentes fabricados em aços baixa liga. Os materiais de adição mais utilizados neste tipo de solda são as ligas de níquel 82 e 182. Este trabalho consistiu na soldagem de uma junta dissimilar de aço baixa liga ASTM A-508 G3 e aço inoxid (mais) ável austenítico AISI 316L utilizando as ligas de níquel 82 e 182 como metais de adição. A soldagem foi realizada manualmente empregando os processos de soldagem ao arco SMAW (Shielded Metal Arc Welding) e GTAW (Gas Tungsten Arc Welding). Os corpos de prova foram caracterizados microestruturalmente utilizando-se microscópio óptico e microscópio eletrônico de varredura com microanálise por dispersão de energia de raios X (EDS) e ensaios de microdureza Vickers. Observou-se uma microestrutura constituída de dendritas de austenita com a presença de precipitados com formas e dimensões definidas pelo aporte térmico e pela direção de soldagem. Não houve variação significativa da dureza ao longo da junta soldada, demonstrando a adequação dos parâmetros de soldagem utilizados. Resumo em inglês The dissimilar metal welds (DMWs) are used in several areas of the industries. In the nuclear power plant, this weld using nickel alloy welding wires is used to connect stainless steel pipes to low alloy steel components on the reactor pressured vessels. The filler materials commonly used in this type of weld are nickel alloys 82 and 182.. In this study, dissimilar metal welds composed of low alloy steel ASTM A-508 G3, nickel alloys 82 e 182 as weld metals, and austenitic (mais) stainless steel AISI 316L were prepared by manual shielded metal arc welding (SMAW) and gas tungsten arc welding techniques (GTAW). Samples were microstructural characterized by optical microscopy and scanning electron microscopy using energy dispersive X ray microanalysis (EDS). It was noticed that there was a microstructure consisting of austenite dendrites with the presence of precipitates with shapes and dimensions set by the thermal contribution and direction of welding. There was no significant variation of hardness along the weld joint, demonstrating the suitability of the welding parameters used.

Scientific Electronic Library Online (Portuguese)

22

Avaliação biogeoquímica dos solos e do medronheiro na área mineira da Panasqueira/ Biogeochemistry evaluation of soils and arbutus trees in the Panasqueira mine area

Godinho, B.; Abreu, M.M.; Magalhães, M.C.
2010-01-01

Resumo em português As Minas da Panasqueira são uma das mais importantes minas em laboração em Portugal. Ao longo de 100 anos de explora­ção de tungsténio, cobre e estanho produzi­ram-se resíduos que foram amontoados à superfície, em escombreiras, provocando impactos ambientais elevados. Este trabalho teve como objectivo o estudo biogeoquími­co da envolvente das Minas da Panasqueira através da avaliação de solos e plantas de medronheiro (Arbutus unedo L.). Os solos apresentam (mais) -se contaminados (mg kg-1) em As (922), Cd (3), Cu (215), Pb (77), W (138) e Zn (260). Nas plantas, apenas o cádmio ocorre em concentrações médias (1,53 mg kg-1) acima do limite tolerável pela generalidade das plantas, no entanto, nenhuma planta apresentava sinais de toxi­cidade. O medronheiro parece ser tolerante às elevadas concentrações totais e da frac­ção disponível (solução DTPA) desses ele­mentos nos solos, podendo por isso, ser usado em programas de fitoestabilização e para aproveitamento dos frutos com o objectivo de produzir aguardente. Resumo em inglês Panasqueira mine is one of the most im­portant mines in Portugal. Over the last cen­tury exploration of tungsten, copper and tin has contributed to produce many waste ma­terials that constitute tailings with huge di­mensions generating high visual and chemi­cal impacts. The objective of this work was to study the biogeochemical impact of min­ing on the soils and arbutus trees (Arbutus unedo L.) in this area. Soils developed on waste materials or hosted rocks are con (mais) taminated with (mg kg-1) As (922), Cd (3), Cu (215), Pb (77), W (138) and Zn (260). In plants, cadmium is the only element that exceeded the vege­tation tolerant limit, but none of the sampled plants showed visual signs of toxicity. Ar­butus tree seems to be tolerant to the high soil concentrations (total and available frac­tion) of the hazardous elements. Therefore arbutus trees can be used in phytostabiliza­tion as a soil remediation strategy. Further studies could also allow the use of their fruits for alcohol production.

Scientific Electronic Library Online (Portuguese)

23

Análises térmicas e processo de sinterização da cerâmica KSr2Nb5O15 dopada com CuO/ Thermal analysis and sintering process of KSr2Nb5O15 ceramic doped with CuO

Vieira, Delia do Carmo; Cardoso, Celso Xavier; Duran, Rafael Matos
2009-01-01

Resumo em inglês KSr2Nb5O15 is a ferroelectric material. The sintering process of the KSr2Nb5O15 ceramic doped with different amounts of CuO was investigated in this research. It was found that CuO is effective as promoter of the densification process of the KSN ceramic. The developed microstructures were different due to the amount of CuO and secondary phases were observed in the microstructures. However, the results of X - ray diffraction showed that only the tetragonal tungsten bronze (mais) (TTB) structure was identified in all the investigated ceramic systems. The thermal behavior of CuO and also of the CuO - KSN phase mixture was investigated by thermal analysis.

Scientific Electronic Library Online (Portuguese)

24

Análise por componentes principais de espectros nexafs na especiação do molibdênio em catalisadores de hidrotratamento/ Principal component analysis of nexafs spectra for molybdenum speciation in hydrotreating catalysts

Faro Jr, Arnaldo da C.; Rodrigues, Victor de O.; Eon, Jean-G.; Rocha, Angela S.
2010-01-01

Resumo em inglês Bulk and supported molybdenum based catalysts, modified by nickel, phosphorous or tungsten were studied by NEXAFS spectroscopy at the Mo L III and L II edges. The techniques of principal component analysis (PCA) together with a linear combination analysis (LCA) allowed the detection and quantification of molybdenum atoms in two different coordination states in the oxide form of the catalysts, namely tetrahedral and octahedral coordination.

Scientific Electronic Library Online (Portuguese)

25

Alkali activated geopolymeric binder using tungesten mine waste : preliminary investigation

Torgal, Fernando Pacheco; Gomes, J. P. Castro; Jalali, Said

This paper reports preliminary results of a PhD research project related to the development of an alkaliactivated geopolymeric binder using mineral waste mud from the Portuguese tungsten mine Panasqueira which is still operating. Mineralogical analysis indicates that the waste mud is compose mainly ...