Análise cristalográfica da solução sólida com estrutura tipo Tungstênio Bronze de niobato de potássio e estrôncio dopado com ferro/ Crystallographic analysis of the solid solution of iron doped potassium strontium niobate with tetragonal tungsten bronze structure

Lanfredi, Silvania; Nobre, Marcos A. L.; Lima, Alan R. F.
2010-01-01

Resumo em inglês Solid solution of iron doped potassium strontium niobate with KSr2(FeNb4)O15-Δ stoichiometry was prepared by high efficiency ball milling method. Structural characterization was carried out by X-ray diffraction. Crystalline structure was analyzed by the Rietveld refinements using the FullProf software. The results showed a tetragonal system with the tetragonal tungsten bronze structure - TTB (a = 12.4631 (2) Å and c = 3.9322 (6) Å, V = 610.78 (2) ų). In this wor (mais) k, the sites occupancy by the K+, Sr2+ and Fe3+ cations on the TTB structure were determined. NbO6 polihedra distortion and its correlation with the theoretical polarization are discussed.

Scientific Electronic Library Online (Portuguese)

2

Síntese e caracterização estrutural do niobato de potássio e estrôncio com estrutura tipo Tetragonal Tungstênio Bronze TTB/ Synthesis and structural characterization of strontium potassium niobate oxide with tetragonal tungstenium bronze TTB type structure

Lanfredi, S.; Trindade, L. R.; Barros, A. R.; Feitosa, N. R.; Nobre, M. A. L.
2005-06-01

Resumo em português A fase nanoestruturada KSr2Nb5O15, foi sintetizada pelo método de mistura mecânica de óxidos por moagem de alta eficiência e por via química, utilizando o método dos precursores poliméricos, em forno tipo tubo sob atmosfera de O2 durante 10 h. A análise por difração de raios X dos pós calcinados a 1150 ºC foi realizada pelo método de Rietveld utilizando-se o software FullProf. A análise dos parâmetros estruturais obtidos via método de Rietveld mostrou um s (mais) istema tetragonal com estrutura tipo tetragonal tungstênio bronze. A partir das reflexões observadas, há apenas evidência da regra [(0kl) k = 2n], a qual é compatível com o grupo espacial centrossimétrico P4bm, o qual foi utilizado para o refinamento. O volume da célula unitária obtido na análise dos pós de KSr2Nb5O15 obtidos por síntese química e por moagem de alta eficiência foi 611,90 ų e 611,95 ų, respectivamente. Resumo em inglês The nanostructured KSr2Nb5O15 phase was synthesized by both routes, the high efficiency milling and the polymeric precursor, in a furnace under O2 atmosphere during 10 h. The Rietveld X-ray diffraction analysis of the calcined powders at 1150 ºC was performed using the FullProf software. The XRD pattern analysis showed a tetragonal system with the tetragonal tungsten bronze structure. From the observed reflections, there is only evidence of the rule existence [(0kl) k = (mais) 2n], which is compatible with the centrosymmetric space group P4bm, which was used for the refinement. The unit cell volume obtained for the KSr2Nb5O15 powders prepared by chemical synthesis and by high efficiency milling were equal to 611,90 ų and 611,95 ų, respectively.

Scientific Electronic Library Online (Portuguese)

3

Caracterização ultra-sônica de materiais ferroelétricos com estrutura perovskita e tungstênio-bronze/ Ultrasonic characterization of perovskite and tungsten-bronze ferroelectric materials

Moreno-Gobbi, A.; Paolini, G.; Pérez, M.; Negreira, C. A.; Garcia, D.; Eiras, J. A.
2002-03-01

Resumo em português Atenuação e velocidade ultra-sônicas e, consequentemente, o módulo de Young de cerâmicas ferroelétricas com estrutura do tipo perovskita e tungstênio-bronze foram medidas entre 2,5 e 30 MHz, à temperatura ambiente, utilizando-se a técnica de pulso-eco. Composições com e sem chumbo foram testadas, mostrando que a presença do cátion Pb2+ representa fator importante no comportamento da atenuação. A dependência da atenuação com a freqüência é mais acentua (mais) da no caso dos ferroelétricos com estrutura perovskita. As discussões são baseadas nos modelos de espalhamento por grãos/poros em materiais policristalinos. Resumo em inglês Ultrasonic attenuation and velocity of ferroelectric ceramics with perovskite and tungsten-bronze structures were measured in a range of 2.5 to 30 MHz at room temperature, using the pulse-echo-overlap technique. Lead and non-lead compositions were analyzed, revealing that Pb2+ in the lattice affects the attenuation behavior. The frequency dependence of attenuation is clearly stronger for the lead materials with perovskite structure. The discussions are based on a qualitative analysis of grain/pore scattering models for polycrystalline materials

Scientific Electronic Library Online (Portuguese)

4

Densificação e evolução microestrutural de cerâmicas Pb0,59Ba0,41Nb2O 6/ Densification and microstructural evolution of Pb0.59Ba0.41Nb2O 6 ceramics

Santos, I. A.; Arantes, V. L.; Paula, R. N. de; Radovanovic, E.; Eiras, J. A.
2000-09-01

Resumo em português O niobato de bário e chumbo (PBN) possui uma estrutura cristalina do tipo tungstênio-bronze e apresenta propriedades ferroelétricas muito interessantes tanto do ponto de vista científico quanto do ponto de vista tecnológico, revelando-se como um material bastante promissor para aplicação no desenvolvimento de dispositivos eletro-ópticos, piezoelétricos e piroelétricos. Cerâmicas à base de Pb0(0,59)Ba0,41Nb2O 6 (PBN59) foram preparadas pelo método convencional (mais) de mistura de matérias-primas. Duas rotas distintas de densificação de amostras foram utilizadas nesse trabalho: sinterização convencional e sinterização por prensagem uniaxial a quente. As caracterizações microestruturais efetuadas indicaram que as amostras obtidas via prensagem uniaxial a quente apresentam uma distribuição bimodal de tamanhos de grão e elevadas densidades, indicando que essa técnica propicia uma maior eficiência no processo de densificação das amostras. O tratamento térmico pós-prensagem uniaxial a quente induz o macro-crescimento preferencial de grãos orientados. Resumo em inglês Lead barium niobate ferroelectric ceramics have a crystallographic tungsten bronze structure and present interesting ferroelectric properties from both scientific and technological points of view, making them very attractive for electro-optical, SAW and pyroelectric device applications. Ceramics of Pb0(0.59)Ba0.41Nb2O 6 (PBN59) were prepared through conventional mixed precursors method. Two distinct densification routes were employed in this work: conventional firing and (mais) uniaxial hot pressing. The microstructural characterizations indicated that the samples obtained by the latter method present a bimodal grain size distribution and high densities, indicating that this technique is more suitable for obtaining ceramics with high densification rates. The post-pressing annealing induces the preferentially oriented macro grain growth.

Scientific Electronic Library Online (Portuguese)

5

Análises térmicas e processo de sinterização da cerâmica KSr2Nb5O15 dopada com CuO/ Thermal analysis and sintering process of KSr2Nb5O15 ceramic doped with CuO

Vieira, Delia do Carmo; Cardoso, Celso Xavier; Duran, Rafael Matos
2009-01-01

Resumo em inglês KSr2Nb5O15 is a ferroelectric material. The sintering process of the KSr2Nb5O15 ceramic doped with different amounts of CuO was investigated in this research. It was found that CuO is effective as promoter of the densification process of the KSN ceramic. The developed microstructures were different due to the amount of CuO and secondary phases were observed in the microstructures. However, the results of X - ray diffraction showed that only the tetragonal tungsten bronze (mais) (TTB) structure was identified in all the investigated ceramic systems. The thermal behavior of CuO and also of the CuO - KSN phase mixture was investigated by thermal analysis.

Scientific Electronic Library Online (Portuguese)