1

Crescimento de cristais de rubi e safira pelo método do fluxo/ Growth of ruby and sapphire crystals by the flux method

Ribeiro, Gislene da Silva; Prado, Rogério Junqueira
2010-01-01

Resumo em inglês This work reports the growth of corundum crystals by the flux method. The main objective was the evaluation of versatility, effectiveness and real possibilities of the flux method to the synthesis and doping of monocrystals with impurities of particular interest. In this work the chosen impurities were i) Cr and ii) Fe and Ti, aiming the synthesis of rubies and sapphires, respectively. The crystals were grown by heating a mixture of Al2O3:Cr or Al2O3:Fe:Ti and flux (MoO3) (mais) . The maximum crystal size obtained was 1.0 mm, all transparent, presenting well developed faces, bipiramidal hexagonal shape, and showing a typical red (ruby) and/or light blue (sapphire) color. EDX and XPD experiments were performed in order to characterize some of the synthesized crystals. All crystallized specimens presented the α-alumina atomic structure.

Scientific Electronic Library Online (Portuguese)

2

Envelhecimento acelerado em sementes de trigo/ Accelerated aging in wheat seeds

Pedroso, Daniele Cardoso; Tunes, Lilian Madruga; Barbieri, Ana Paula; Barros, Antonio Carlos Souza Albuquerque; Muniz, Marlove Fátima Brião; Menezes, Vanessa Ocom
2010-11-01

Resumo em português O presente trabalho teve o objetivo de estudar procedimentos de condução do teste de envelhecimento acelerado para determinar o potencial fisiológico de sementes de trigo. Utilizaram-se quatro cultivares: 'Pampeano', 'Safira', 'Ônix' e 'Jaspe'. Foram realizadas determinações de teor de água e avaliações de germinação, emergência, índice de velocidade de emergência e teste de envelhecimento acelerado. O teste de envelhecimento acelerado foi conduzido de três (mais) formas: teste tradicional (água), teste com solução saturada de NaCl (11g de NaCl por 100mL de água) e teste com solução supersaturada de NaCl (40g de NaCl por 100mL de água), nos períodos de 48, 72 e 96h de permanência na câmara de envelhecimento a 42°C. O teste de envelhecimento acelerado com solução saturada de NaCl, no período de 96h, foi o mais adequado para avaliar o potencial fisiológico das sementes de trigo, em alto, médio e baixo vigor. Resumo em inglês This research aimed to study procedures for conducting the accelerated aging test to determine the physiological potential of wheat seeds. The experiment was conducted with four varieties: 'Pampeano', 'Sapphire', Onyx' and 'Jasper'. Tests were performed with water content, germination, seedling emergence, speed of emergence and accelerated aging. The accelerated aging test was conducted in three stages: traditional (water), test using saturated NaCl solution (11g of NaCl (mais) per 100mL of water) and with the use of supersaturated solution of NaCl (40g of NaCl per 100mL of water), each for 48, 72 and 96h at 42°C. The accelerated aging test with saturated solution of NaCl, within 96h was suitable to evaluate the physiological potential of seeds of wheat in high, medium and low vigor.

Scientific Electronic Library Online (Portuguese)

3

Sinterização de filmes finos de LiNbO3 em forno microondas: estudo da influência da direção do fluxo de calor/ Sintering of LiNbO3 thin films in microwave furnace: study of the influence of the heat flow direction

Vasconcelos, N. S. L. S.; Vasconcelos, J. S.; Bouquet, V.; Zanetti, S. M.; Leite, E. R.; Longo, E.; Bernardi, M. I.; Perrin, A.; Guilloux-Viry, M.; Varela, J. A.
2004-06-01

Resumo em português Filmes finos de LiNbO3 foram preparados pelo método dos precursores poliméricos e depositados por "spin coating" sobre substratos de safira (0001). Os filmes foram tratados em forno microondas doméstico a 400 ºC por 15 e 20 min. Um material com alta perda dielétrica (susceptor de SiC) foi usado para absorver energia das microondas e transformá-la em calor. Este calor foi transferido para o filme a fim de promover a sua cristalização. O susceptor foi posicionado ac (mais) ima do filme ou embaixo do substrato. Desta forma, a influência da direção do fluxo de calor na cristalização das amostras foi verificada. Os filmes foram caracterizados por difração de raios X, microscopia de força atômica e espectrofotometria (transmitância) na região UV-visível e o índice de refração foi determinado por elipsometria. O crescimento epitaxial foi observado para o filme com susceptor posicionado embaixo do substrato. Verificou-se que os grãos apresentaram crescimento aleatório quando o susceptor foi posicionado acima do filme. Os filmes apresentaram-se relativamente densos, homogêneos e lisos, com boas propriedades ópticas. Resumo em inglês LiNbO3 thin films were prepared using a polymeric precursor solution deposited by spin coating on (0001) sapphire substrate. Heat treatment of the films was carried out in a microwave oven at 400 ºC for 15 and 20 min. A SiC susceptor (material with high dielectric loss) was used to absorb microwave energy and transfer the heat to the film in order to promote crystallization. The susceptor was placed above the film or below the substrate. Thus, the influence of the heat f (mais) lux direction on the sample crystallization was verified. The films were characterized by X-ray diffraction, atomic force microscopy and spectrophotometry (transmittance) in the UV-Visible region and the refractive index was determined with an ellipsometer. The epitaxial growth was observed for the film with the susceptor placed below the substrate. Random growth was verified when the susceptor was placed above the film. The films were relatively dense, homogeneous and smooth with good optical properties.

Scientific Electronic Library Online (Portuguese)