Sample records for properties mechanical
from WorldWideScience.org

Sample records 1 - 20 shown. Select sample records:



1

Propriedades mecânicas e resistência à corrosão da liga Ti-4Al-4V obtida da reciclagem da liga Ti-6Al-4V

Jesuíno, G.A.; Ribeiro, L.M.F.; Nakazato, R.Z.; Codaro, E.N.; Hein, L.R. de O.
2001-01-01

Resumo em inglês The present work aimed to study the transformation from as-cast structure of the Ti4Al-4V alloy, as a result of the Ti-6Al-4V recycling, after some rapid heat treatments based on martensitic reactions. The effects on mechanical properties were evaluated by Vickers hardness measurements, Charpy and monotonic tensile tests. The corrosion strength was tested by immersion during 4 months in artificial physiological solutions, to evaluate its possible use as a biomaterial. The (mais) data pointed to: a) a reduction on corrosion strength for quenching above beta transus; b) significant increasing on hardness and mechanical strength; c) a maintenance of impact toughness; d) the corrosion strength for immersion in a NaCl 1%+ NaF 0,1% (m/m) was lower in all conditions, specially for those including heating to 900 °C.

Scientific Electronic Library Online (Portuguese)

2

Propriedades mecânicas de espumas cerâmicas produzidas via "gelcasting"/ Mechanical properties of ceramic foams produced by gelcasting

Ortega, F. S.; Paiva, A. E. M.; Rodrigues, J. A.; Pandolfelli, V. C.
2003-03-01

Resumo em português Cerâmicas porosas são materiais de grande interesse tecnológico, devido à associação de propriedades únicas como alta refratariedade e inércia química com alta permeabilidade, alta área superficial e baixa condutividade térmica. No entanto, o aumento da porosidade resulta, invariavelmente, na deterioração das propriedades mecânicas. Este trabalho faz uma investigação sobre as propriedades mecânicas de espumas cerâmicas obtidas pela aeração de suspensõ (mais) es associada à polimerização "in situ" de monômeros orgânicos previamente adicionados (processo gelcasting). A macroestrutura resultante deste processo é constituída por poros que tendem a uma geometria esférica, a qual minimiza a concentração de tensões mecânicas. Além disso, as paredes dos poros podem ser completamente densificadas, proporcionando uma microestrutura homogênea. A resistência mecânica de espumas cerâmicas com várias densidades foi avaliada por flexão em quatro pontos e por compressão. Os resultados mecânicos foram analisados através da estatística de Weilbull. O módulo elástico das amostras foi caracterizado pelo método de ressonância mecânica de barras. Os resultados obtidos possibilitam uma melhor compreensão dos fatores que determinam as propriedades mecânicas desta nova classe de material, fornecendo subsídios para futuros desenvolvimentos. Resumo em inglês Porous ceramics have great technological importance, since they combine ceramics unique properties, such as refractoriness and chemical resistance, with high surface area, high permeability and low thermal conductivity. Nevertheless, increasing porosity generally deteriorates the mechanical behavior of ceramics. In this work, the mechanical properties of ceramic foams produced by the aeration of ceramic suspensions associated to the polymerization of previously added mono (mais) mers (gelcasting process) is investigated. The macrostructure that results from this process is constituted of nearly spherical pores, a geometry that minimizes the concentration of mechanical stresses. Moreover the cell walls can be well densified during sintering, resulting in a homogeneous microstructure. The mechanical strength of ceramic foams with several densities was evaluated under 4-point bending test and compression. The results of flexural strength were used to calculate the Weilbull modulus of the samples. The Young's modulus and shear modulus were measured using a mechanical resonance method. The results allowed a better comprehension of the main factors that affect the mechanical properties of this new material category and provided insights for its improvement.

Scientific Electronic Library Online (Portuguese)

3

Propriedades mecânicas de materiais compósitos à base de cimento Portland e resina epoxi/ Mechanical properties of composite materials based on portland cement and epoxy resin

Panzera, T. H.; Sabariz, A. L. R.; Strecker, K.; Borges, P. H. R.; Vasconcelos, D. C. L.; Wasconcelos, W. L.
2010-03-01

Resumo em português O estudo de materiais de alto desempenho e multifuncionais, como os compósitos poliméricos cimentícios, tem sido o foco de inúmeras pesquisas na indústria da construção civil. Este trabalho investiga o efeito da combinação de uma fase polimérica termorrígida, uma resina epóxi, com cimento Portland branco estrutural, seguido da avaliação da resistência à compressão e módulo de elasticidade. Este compósito, quando comparado individualmente com as suas mat (mais) érias-prima originais, promove um aumento da resistência mecânica à compressão, redução da massa específica e, também uma mudança significativa do comportamento mecânico. As mudanças nas propriedades mecânicas estão associadas à hidratação da fase cimentícia na presença da resina, fato comprovado através da análise espectroscópica na região do infravermelho. Resumo em inglês The study of multi-functional materials of high performance, as the polymeric-cementitious composites, has been the focus of several researches in the industry of the civil engineering. This work investigates the effect of the combination of a thermorigid epoxy phase and the white Portland cement, followed by the evaluation of its compressive strength and modulus of elasticity. This composite, when the phases are individually compared, provides an increase of the compress (mais) ive strength, a reduction of the density, and a significant change of the mechanical behaviour. The changes in mechanical behaviour are associated with the hydration of cement in the presence of resin, which was evident after infrared spectroscopy analysis.

Scientific Electronic Library Online (Portuguese)

4

Propriedades mecânicas do cimento ósseo e da poliuretana de mamona com e sem catalisador/ Mechanical properties of bone cement and castor oil-based polyurethane with and without a catalyst

Lima, A.F.M.; Rahal, S.C.; Muller, S.S.; Correa, M.C.E.; Padovani, C.R.
2008-10-01

Resumo em português Avaliou-se o comportamento mecânico do polímero de mamona, tendo por variáveis o tempo de produção e a presença de catalisador, e utilizando como padrão comparativo o cimento ósseo (polimetilmetacrilato). Foram estabelecidos três grupos experimentais, de acordo com o tipo de corpo de prova (cilindro ou barra) e polímero utilizado, que foram posteriormente subdivididos em subgrupos conforme o tempo após produção, ou seja, 24, 48 e 72 horas. O ensaio de compres (mais) são analisou a carga máxima e a tensão e o ensaio de dobramento estudou o módulo de dobramento e a resistência. Estatisticamente não houve diferenças nos valores de resistência à compressão ou ao dobramento às 24, 48 e 72 horas após a produção do polimetilmetacrilato e da poliuretana, com ou sem catalisador. A poliuretana com catalisador foi a mais resistente nos ensaios de compressão, apresentando módulo de dobramento semelhante ao do polimetilmetacrilato e resistência ao dobramento superior à da poliuretana sem catalisador. Conclui-se que: o tempo não alterou as propriedades mecânicas dos compósitos avaliados; o catalisador melhorou o desempenho mecânico da poliuretana de mamona; na resistência mecânica à compressão, a poliuretana com catalisador suportou mais carga que o polimetilmetacrilato. Resumo em inglês The mechanical properties of castor oil-based polyurethane was evaluated considering post-production time and the presence of a catalyst as variables and using bone cement (polymethylmetacrylate) as a comparative pattern. According to proof body type (cylinders or bars) and the used polymer, three experimental groups were established. Such groups were later subdivided according to post-production time, namely, 24, 48, and 72 hours. A compression assay analyzed maximum loa (mais) d and tension, and a folding assay evaluated the folding module and resistance. There were no statistical differences in the values for resistance to compression or folding at 24, 48, and 72 hours after the production of polymethylmetacrylate and polyurethane with or without a catalyst. Castor oil-based polyurethane with a catalyst showed to be the most resistant during the compression assays as its folding module was similar to that of polymethylmetacrylate, and its folding resistance was higher than that of polyurethane without a catalyst. In conclusion, time did not change the mechanical properties of the evaluated composites; the catalyst improved the mechanical performance of castor oil-based polyurethane; castor oil-based polyurethane with a catalyst supported more load during the assay for mechanical resistance to compression than did polymethylmetacrylate.

Scientific Electronic Library Online (Portuguese)

5

Propriedades mecânicas e termomecânicas de compósitos com partículas de diamante dispersas em matriz epoxídica modificada na razão resina/endurecedor/ Mechanical and thermo-mechanical properties of diamond particles dispersed in PHR modified epoxy matrix composites

Monteiro, Sergio N.; Menezes, Gustavo W. de; Skury, Ana Lúcia D.; Lopes, Felipe P. D.; Rodriguez, Rubén J. S.; Bobrovnitchii, Guerold S.
2006-12-01

Resumo em português Foram estudadas as propriedades mecânicas dos compósitos com partículas dispersas de diamante em matriz de resina epóxi curada com diferentes proporções de endurecedor caracterizadas pela razão resina/endurecedor. Investigou-se também o comportamento termomecânico através de ensaios de DMA (Análise Dinâmico-Mecânica). No presente trabalho foi feita uma completa avaliação das propriedades mecânicas e termomecânicas no amplo intervalo de razão resina/endur (mais) ecedor associado a possíveis aplicações tecnológicas. Foram fabricados compósitos com até 30% em peso de partículas de diamante dispersas em matriz epóxi do tipo DGEBA/TETA com diferentes razões resina/endurecedor, variando de 7 a 21. Para todas as condições investigadas a resistência diminuiu com a quantidade incorporada de diamante. Para matrizes com razão resina/endurecedor acima do estequiométrico 13, os compósitos apresentaram melhor desempenho mecânico. Os resultados dos ensaios termomecânicos mostraram que o módulo de armazenamento dos compósitos aumenta com a quantidade incorporada de diamante. Através da tangente delta foi possível avaliar prováveis mecanismos que contribuem para o desempenho termomecânico destes compósitos. Resumo em inglês The mechanical properties of composites with dispersed diamond particles in epoxy matrix cured with different proportions of hardener to monomer ratio, characterized by the resin/hardener ratio (phr) were studied. An investigation on the thermo-mechanical behavior of these composites was also carried out by dynamical mechanical analysis (DMA). In the present work a complete evaluation of the mechanical properties was carried in a wide interval of phr associated with possi (mais) ble technological applications. Composites with up to 30 wt. % of diamond particles dispersed in type DGEBA/TETA epoxy matrix were fabricated with phr ratios varying from 7 to 21. For all investigated conditions, the composite strength decreased with the amount of incorporated diamond. Matrices with phr above the stoichiometric 13 were associated with composites with better mechanical performance. The DMA results showed that the storage modulus increases with the amount of diamond particles incorporated in the composite. The values obtained for the delta tangent, allowed an evaluation of possible mechanisms that contribute to the thermal mechanical performance of these composites.

Scientific Electronic Library Online (Portuguese)

6

Propriedades mecânicas do músculo gastrocnêmio de ratas, imobilizado e posteriormente submetido a diferentes protocolos de alongamento/ Mechanical properties of gastrocnemius muscle of female rats immobilized and posteriorly submitted to different stretching protocols

Polizello, Juliana Cristina; Carvalho, Leonardo César; Freitas, Fernando Cassiolato; Padula, Natália; Shimano, Antonio Carlos; Mattiello-Sverzut, Ana Claudia
2009-06-01

Resumo em português O alongamento é amplamente utilizado na prática clínica da fisioterapia e no desporto, porém, as alterações mecânicas que essa técnica gera no músculo esquelético são pouco exploradas cientificamente. Este estudo avaliou as alterações mecânicas que acometem o músculo gastrocnêmio de ratas Wistar, adultas jovens, após 14 dias de imobilização e, secundariamente, submetido a alongamento manual passivo por 10 dias consecutivos, aplicado uma ou duas vezes ao (mais) dia. Foram utilizados 50 animais, sendo 10 para cada grupo: Controle (GC); Imobilizado (GI); Imobilizado e Liberado (GIL); Imobilizado e alongado uma vez ao dia (GIA1); e Imobilizado e alongado duas vezes ao dia (GIA2). O músculo gastrocnêmio foi submetido ao ensaio mecânico de tração, onde foram avaliadas as propriedades de carga e alongamento nos limites máximo e proporcional, além de rigidez e resiliência. A imobilização reduziu os valores das propriedades mecânicas de carga no limite máximo (CLM), carga no limite proporcional (CLP), alongamento no limite máximo (ALM), rigidez e resiliência, em 44,4%, 34,4%, 27,6%, 64,4% e 54%, respectivamente, quando comparados com os valores do GC. A remobilização livre e o alongamento restauraram as propriedades de CLM, CLP, ALM, rigidez e resiliência do músculo, exceto para o GIA2, que foi incapaz de restabelecer a propriedade de ALM (31,3% menor que GC). Concluí-se, portanto que, após 14 dias de imobilização segmentar, cargas individuais de alongamento e a livre movimentação permitem restituir as propriedades mecânicas do tecido muscular. Resumo em inglês Stretching is widely employed in physiotherapeutic clinical practice and in sportive activities; however, the mechanical alterations of the skeletal muscle generated by this technique are poorly scientifically investigated. This study evaluated the mechanical alterations suffered by the gastrocnemius muscle of young adult female Wistar rats, submitted to14 days of immobilization followed by passive manual stretching during 10 consecutive days once or twice a day. Fifty an (mais) imals were equally distributed in five groups, Control (CG); Immobilized (IG); Immobilized and liberated (ILG); Immobilized and submitted to stretching once a day (IEG1); Immobilized and submitted to stretching twice a day (IEG2). The gastrocnemius muscle was analyzed by mechanical traction assay and the properties related to load and maximal and proportional stretching evaluated in addition to stiffness and resilience. Immobilization decreased load at maximal thresholds (MTL), load at proportional thresholds (LPT), stretch at maximal thresholds (SMT), stiffness and resilience were reduced in 44.4%, 34.4%, 27.6%, 64.4% and 54% respectively, compared to CG values. With subsequent free remobilization and stretching, all parameters were restored except for IEG2 in which SMT remained reduced in 31.3%, when compared to CG. It is concluded that after 14 days of segmental immobilization, individual stretching loads and free movements contribute to regain muscle mechanical properties.

Scientific Electronic Library Online (Portuguese)

7

Estudo das propriedades mecânicas e térmicas do polímero Poli-3-hidroxibutirato (PHB) e de compósitos PHB/pó de madeira/ Study of mechanical and thermal properties of the polymer Poly-3-hydroxybutyrate (PHB) and PHB/wood flour composites

Machado, Miriam L. C.; Pereira, Nilson C.; Miranda, Leila F. de; Terence, Mauro C.; Pradella, José G. C.
2010-01-01

Resumo em português O PHB (Poli-3-hidroxibutirato) é um termoplástico biodegradável sintetizado por fermentação submersa a partir de matérias-primas renováveis. A utilização de fibras naturais tem sido pesquisada visando melhorar as propriedades e reduzir o custo do PHB. O objetivo deste trabalho foi o estudo das propriedades mecânicas (resistência à tração), térmicas (Análise termogravimétrica,TGA, e Calorimetria Exploratória Diferencial, DSC) e reológicas (torque em câm (mais) era de mistura e Índice de Fluidez) do PHB e de compósitos de PHB/pó de madeira processados e irradiados. Foram preparados compósitos com concentrações de PHB/pó de madeira de 90/10, 80/20 e 70/30 (m/m). Os materiais foram processados através das seguintes etapas de processamento: calandragem, fragmentação, extrusão, granulação, secagem e moldagem por injeção para confecção dos corpos de prova. A incorporação do pó de madeira aumentou o grau de cristalinidade e a temperatura de cristalização do polímero, e nos compósitos PHB/pó de madeira 80/20 e 70/30 a rigidez do material aumentou. A irradiação após o processamento (dose de 30 kGy) provocou aumento da rigidez do PHB puro e dos compósitos PHB/pó de madeira 90/10 e 80/20, embora outras propriedades tenham decrescido. O compósito PHB/pó de madeira 70/30 apresentou os melhores resultados em termos econômicos e de processamento. Resumo em inglês PHB (Polyhydroxybutyrate) is a biodegradable thermoplastic synthesized by submerse fermentation of renewable raw materials. The use of natural fibers has been largely researched to improve PHB properties, as well as reducing its cost. The purpose of this work was the study of the mechanical, thermal properties and rheological analyses (torque in mixer camera and melt flow index) of processed and irradiated PHB, as well as PHB/wood flour composites. PHB/wood flour composit (mais) es were prepared with PHB/wood relation of 90/10, 80/20 and 70/30 (w/w). Both pure PHB and composites were processed through the following steps: calendering, milling, extrusion, second milling, drying and injection molding to make test specimens. Mechanical properties (strength resistance) and thermo analyses (Thermogravimetric Analysis, TGA and Differential Scanning Calorimeter, DSC) tests were carried out. The introduction of the wood flour increased both polymer crystallinity and crystallization temperature. The material stiffness increased in PHB/wood flour composites (80/20 and 70/30). The irradiation after processing in 30 kGy doses led to increased stiffness of pure PHB and PHB/wood flour composites (90/10 and 80/20) while other properties have decreased. The PHB/wood flour composite 70/30 showed the best results in terms of economy and processing.

Scientific Electronic Library Online (Portuguese)

8

Estudo das propriedades mecânicas de um composto de PVC modificado com fibras de bananeira/ Study of the mechanical properties of PVC/banana fiber composites

Balzer, Palova S.; Vicente, Lawrence L.; Briesemeister, Ricardo; Becker, Daniela; Soldi, Valdir; Rodolfo Jr., Antonio; Feltran, Murilo B.
2007-03-01

Resumo em português Neste trabalho foram avaliadas as propriedades de compósitos de poli (cloreto de vinila) - PVC rígido com adição de fibras de bananeira. As fibras foram extraídas do pseudocaule da bananeira e incorporadas nas proporções de 5, 10 e 20% em volume em um composto de PVC rígido pelo processo de extrusão. Para a obtenção dos corpos de prova utilizados na caracterização das formulações foi utilizado o processo de injeção. A utilização de fibras extraídas do (mais) pseudocaule da bananeira, tratadas manualmente em um processo simples desenvolvido na SOCIESC, mostra-se como alternativa viável na forma de fibra de reforço para a produção de compósitos de PVC rígido, tendo mostrado aumento da resistência à tração, discreta redução no alongamento na ruptura e aumento da resistência ao impacto, bem como redução, mesmo que discreta, no peso específico do compósito resultante, potencializando a obtenção de componentes com melhor desempenho mecânico e menor peso. Resumo em inglês Mechanical properties (tensile and impact resistance), specific weight and phase morphology of PVC/banana tree fiber composites were evaluated in this paper. The fibers were extracted from de pseudostem of the banana tree and mixed with a rigid PVC compound in the proportions of 5, 10 and 20% in volume by the extrusion process. Specimens were obtained by injection molding. The composites showed improvement of the impact and tensile properties, reduction of the specific weight, making possible the production of final products.

Scientific Electronic Library Online (Portuguese)

9

Estudo das propriedades mecânicas e elétricas de fibras de curauá modificada com polianilina/ Study on mechanical and electrical properties of curaua fibers modified with polianiline

S. Junior, Fernando G. de; Picciani, Paulo H. S; Rocha, Eli V. da; Oliveira, Geiza E. de
2010-01-01

Resumo em português Fibras naturais têm sido empregadas em diversos compósitos, principalmente na indústria automobilística. Dentre as diversas fibras naturais, a fibra de curauá é atraente por apresentar elevada propriedade mecânica associada a baixos valores de densidade. Neste trabalho a fibra de curauá é modificada quimicamente pelo recobrimento de uma camada condutora de polianilina, PAni. O material obtido foi caracterizado pelas técnicas espectrometria de infravermelho por t (mais) ransformada de Fourier (FTIR), análise termogravimétrica (TG) e microscopia ótica. As técnicas de caracterização utilizadas demonstraram que a metodologia empregada foi eficiente para formar um recobrimento parcial, porém efetivo, uma vez que o recobrimento permitiu a formação de caminhos condutores ao longo de toda a fibra. As propriedades eletro-mecânicas das fibras também foram avaliadas e os compósitos apresentaram um grande potencial para a construção de sensores de pressão a baixos custos. Resumo em inglês Natural fibers have been employed as reinforcement filler in composite materials for the automobile industry. Among the natural fibers, the curauá fiber is promising due to its high mechanical resistance associated with low density values. In this work curauá fibers are chemically modified by a conducting polyaniline coating, with the aim of using this new conductive composite as pressure sensors. The composite material obtained was characterized using Fourier transform (mais) infrared spectroscopy (FTIR), thermogravimetric analysis (TG) and optical microscopy. The results demonstrated that the methodology adopted was efficient in forming a partial, but effective, coating of the fiber, thus leading to conducting paths along the whole fiber. The electro-mechanical properties of the fibers were also evaluated and the composites have potential for low cost pressure sensors. Furthermore, the modified fibers had good thermal stability and the partial coating allows the composite to be naturally degraded as an environmentally-friendly material.

Scientific Electronic Library Online (Portuguese)

10

Efeitos da adição de níquel em ligas ferro-cromo. Parte I: propriedades mecânicas

Bubani, Franco de Castro; Decarli, Célia Cristina Moretti; Marques, Daniel Cirillo; Barbosa, Celso Antonio; Diniz, Anselmo Eduardo; Mei, Paulo Roberto
2007-03-01

Resumo em português O objetivo desse trabalho é estudar a influência de adições de níquel sobre as propriedades mecânicas de ligas Fe-Cr. Para atender a esse propósito, foram preparadas diversas ligas com a composição básica 18%Cr - 0,01%C - 0,2%Si - 0,4%Mn, variando-se o teor de níquel (0, 10, 20, 40 e 60 % em peso). A caracterização das ligas foi feita por difração de raios X e análise térmica. Foi determinada a dureza das ligas no estado como recebido e após a imposiçã (mais) o de deformação a frio. Foram realizados ensaios de tração à temperatura ambiente e a 350ºC, para verificar o efeito da temperatura sobre o comportamento mecânico das mesmas. O objetivo da caracterização mecânica das ligas é o de associar as propriedades mecânicas com as propriedades de usinabilidade, obtidas em estudo que está sendo desenvolvido em paralelo. Resumo em inglês The aim of this work was to study the influence of Ni additions on the mechanical properties of Fe-Cr alloys. For this purpose, alloys were prepared with an 18%Cr-0.01%C-0.2%Si-0.4%Mn base composition and variable Ni content (0, 10, 20, 40 and 60 weight %). The alloys were characterized by X-Ray diffraction and thermal analyses. Their hardness was determined before and after cold deformation. Tension tests were carried out at room temperature and 350ºC to verify the effe (mais) ct of temperature on the mechanical behavior of the alloys. The mechanical characterization aim was to use these figures to correlate mechanical properties and machinability (results originating from a parallel study).

Scientific Electronic Library Online (Portuguese)

11

Avaliação de propriedades mecânicas de concretos contendo escória de cobre como agregado miúdo/ Evaluation of mechanical properties of concrete with copper slag as fine aggregate

Moura, Washington Almeida; Gonçalves, Jardel Pereira; Leite, Mônica Batista
2009-06-01

Resumo em português Nesse trabalho, são apresentados os resultados do estudo sobre a utilização da escória de cobre como agregado miúdo para concreto. Foi avaliada a influência da utilização de diferentes teores de escória de cobre granulada, como agregado miúdo, nas propriedades mecânicas (resistência à compressão e tração) do concreto. Os resultados mostram que a utilização de escória de cobre como agregado miúdo, até 40% de substituição em volume, promove um increme (mais) nto no desempenho mecânico do concreto, demonstrando a possibilidade de utilização em substituição parcial do agregado miúdo natural. Resumo em inglês This work presents the results of the study about the use of copper slag as fine aggregate for concrete. The influence of the use of different percentages of granulated copper slag, as fine aggregate, in the mechanical properties (compression strength and splitting tensile strength) of the concrete was evaluated. The results show that the use of copper slag as fine aggregate, up to 40% of substitution in volume, promotes an increment in the mechanical performance of the concrete. The work shows the possibility of using copper slag in partial substitution of the natural aggregate.

Scientific Electronic Library Online (Portuguese)

12

Avaliação das propriedades mecânicas de atadura gessada de três diferentes fabricantes, utilizada para confecção de órteses/ Evaluation of the mechanical properties of plaster bandages used for orthosis manufacture, marketed by three different manufacturers

Vieira, Gustavo Cardoso; Fonseca, Marisa de Cássia Registro; Shimano, Antônio Carlos; Mazzer, Nilton; Barbieri, Cláudio Henrique; Elui, Valéria Carril Meirelles
2006-01-01

Resumo em português Foram realizados testes mecânicos com atadura gessada de três diferentes fabricantes, utilizada para confecção de órteses. Para isso, foram confeccionados corpos de provas (CDPs) na forma de placas e de cilindros. Os CDPs foram submetidos a dois tipos de ensaios mecânicos: para o grupo das placas foi realizado ensaio de flexão em três pontos e para o grupo dos cilindros, ensaio de compressão. Os ensaios mecânicos foram realizados na Máquina Universal de Ensaios (mais) EMIC®. Três propriedades mecânicas foram avaliadas após os ensaios: carga no limite máximo, carga no limite de proporcionalidade e rigidez. Os resultados mostraram que um fabricante foi superior aos demais para as propriedades avaliadas. Resumo em inglês Mechanical tests have been performed in plaster bandages used in orthosis supplied by three different manufacturers. For this, bodies of evidence (BOEs) were made with plates and cylinders shapes. BOEs were submitted to two kinds of mechanical assays: for the plate group, a flexion assay was performed at three points, and, for the cylinder group, a compression assay was performed. Mechanical assays were performed on the Universal Assay Machine EMIC®. Three mechanical pro (mais) perties were assessed after assays: maximum limit load, proportional limit load and stiffness. Results show that a manufacturer was superior over the others for the properties assessed.

Scientific Electronic Library Online (Portuguese)

13

Avaliação das propriedades mecânicas de material polimérico utilizado na confecção de caixas de medição de energia elétrica/ Evaluation of mechanical properties of a polymeric material used in the construction of boxes for electrical energy measurements

Ferracin, Ricardo J.; Ruvolo Filho, Adhemar; Marconcini, José M.; Diniz, José H. de O.
2009-06-01

Resumo em português As propriedades mecânicas de materiais poliméricos apresentam forte correlação com o processamento do material. Neste trabalho foram estudadas blendas de poli(óxido de fenileno)/poliestireno (PPO/PS) e policarbonatos utilizados na confecção de caixas, comparando-se as propriedades mecânicas de amostras injetadas nos formatos de corpo de prova, segundo a norma ASTM D638, e de amostras retiradas diretamente das caixas. A partir dos resultados de ensaio de impacto Iz (mais) od verificou-se uma grande variabilidade nos valores antes e após envelhecimento em água, de todas as caixas. Isto se deve, principalmente, às diferentes tensões internas em cada região da caixa provenientes do processamento. Também foi observada uma grande diferença entre os valores encontrados para resistência ao impacto Izod dos corpos de prova retirados da parte inferior das caixas comparados com os valores encontrados para os respectivos materiais injetados, indicando também uma significativa influência dos parâmetros de processamento de injeção, tanto nas caixas como nos corpos de prova injetados. De modo geral, os valores de resistência à tração no ponto de máxima deformação elástica não diferem significativamente entre os corpos de prova injetados e os corpos de prova retirados das caixas do mesmo material; contudo, observou-se que esta variação é significativa nos valores de alongamento à ruptura, demonstrando que esta propriedade deve ser considerada nas avaliações do comportamento mecânico dos materiais poliméricos. Resumo em inglês The mechanical properties of polymeric materials depend strongly on the processing. In this work, blends of Poly(phenylene oxide)/polystyrene (PPO/PS) and polycarbonates used in electrical cabinet boxes have been studied. A comparison was made of the mechanical properties of samples injected in the form of test specimens, according to the standard practice ASTM D638, with test specimens removed from the boxes. From the results of impact Izod test, a great variability in t (mais) he values was verified before and after ageing in water, for all the boxes. This is due to the different internal tensions in each region of the box arising from the processing. A large difference was observed among the values found for resistance to the impact Izod test of the removed test specimens of the lower part of the boxes compared with the values found for the respective injected materials. This indicates a significant influence from the parameters of injection processing, in the boxes as well as in the injected test specimens. Overall, the values of tensile strength in the point of maximum elastic deformation do not differ significantly among the test specimens injected and the removed from the boxes of the same material; however, it was observed that this variation is significant in the values of elongation at break, demonstrating that this property must be considered in the evaluations of the mechanical behavior of the polymeric materials.

Scientific Electronic Library Online (Portuguese)

14

Estudo de algumas propriedades mecânicas da madeira de um híbrido clonal de Eucalyptus urophylla X Eucalyptus grandis/ Study of some mechanical properties of wood in a clonal hybrid of Eucalyptus urophylla X Eucalyptus grandis

Gonçalves, Fabrício Gomes; Oliveira, José Tarcísio da Silva; Lucia, Ricardo Marius Della; Sartório, Robert Cardoso
2009-06-01

Resumo em português A procura por madeiras oriundas de reflorestamentos destinadas à serraria é uma realidade já há muitos anos, principalmente aquelas das espécies do gênero Eucalyptus. Visando buscar novas informações importantes para esse mercado, este trabalho objetivou determinar algumas propriedades mecânicas da madeira de um híbrido clonal de Eucalyptus urophylla x Eucalyptus grandis de duas idades e provenientes de talhadia simples e de reforma. Os resultados indicaram que (mais) a madeira desse híbrido apresenta boas características tecnológicas, destacando-se a segunda tora (a partir de 3 m) com as melhores propriedades de flexão estática (Módulo de Elasticidade - MOE e Módulo de Ruptura - MOR) e Compressão Axial das fibras. As árvores de maior idade (166 meses) e que sofreram dois desbastes apresentaram as melhores propriedades de flexão estática e compressão axial. Resumo em inglês The search for wood originated from reforestations destined to sawmill has been observed for many years, mainly for the Eucalyptus species. Searching for information to assist this market, the aim of this study was to determine some mechanical properties of the wood from a Eucalyptus urophylla x Eucalyptus grandis clonal hybrid, at two different ages and coming from coppice and reform. The results show that the wood of this clonal hybrid presents good technological charac (mais) teristics and is the second best log (starting from 3,0 m), as to static bending properties (Module of Elasticity - MOE and Module of Rupture - MOR). The oldest trees (166 months - E2) which suffered two thinning presented the best results for the property of static bending and axial crushing (CA).

Scientific Electronic Library Online (Portuguese)

15

Misturas BR/SBR: propriedades mecânicas em função do modo de preparo/ BR/SBR blends: mechanical properties as a function of the preparation mode

Alcantara, Adriana F. de; Nunes, Regina Célia R.; Visconte, Leila L. Y.
2004-01-01

Resumo em português Misturas com borracha são freqüentemente usadas para se conseguir o balanço das propriedades desejadas e também, em alguns casos, a redução de custos. As misturas elastoméricas são normalmente sistemas multifásicos e a distribuição dos aditivos entre as fases não é necessariamente uniforme. Neste trabalho, o polibutadieno (BR) foi misturado ao elastômero de butadieno-estireno (SBR) na proporção 1:1 em peso. As composições foram preparadas utilizando um m (mais) isturador de rolos, segundo a norma ASTM D3182, sendo que a incorporação dos aditivos foi realizada de quatro formas diferentes. Após a avaliação das propriedades reométricas e a vulcanização, foram estudadas as propriedades mecânicas para cada composição, avaliadas de acordo com as normas ASTM específicas para cada ensaio. Os resultados mostram que os diferentes modos de preparo de uma mesma formulação podem provocar mudança significativa nas propriedades mecânicas de misturas envolvendo essas duas borrachas. No caso das misturas BR/SBR estudadas, as propriedades apresentaram valores intermediários aos das borrachas isoladas. Resumo em inglês Rubber blends are frequently prepared to give a balance of the desired properties and, in some cases, reduction of cost as well. Elastomeric mixtures are usually multiphase systems and the dispersion of the additives may not be uniform throughout the phases. In this work, polybutadiene rubber (BR) was mixed with polybutadiene-styrene rubber (SBR) in a 50:50 w/w ratio. The compositions were prepared in a two-roll mill, according to ASTM D3182, and the incorporation of the (mais) ingredients was carried out according to four different modes. After the determination of the rheometric properties and the vulcanization of the compounds, mechanical properties were evaluated according to specific ASTM procedures. The results show that the mechanical properties may be altered by changing the procedure to prepare a given formulation. In the case of BR/SBR mixtures, the properties were found to be intermediate to the values presented by the compositions with the separate rubbers.

Scientific Electronic Library Online (Portuguese)

16

Influência da mica nas propriedades mecânicas e dinâmico-mecânicas de composições de borracha natural/ Influence of mica on mechanical and dynamic mechanical properties of natural rubber compositions

Escócio, Viviane A.; Martins, Agnes F.; Visconte, Leila L.Y.; Nunes, Regina C.R.; Costa, Djanira M. R.
2003-06-01

Resumo em português Neste trabalho foi estudada a influência da adição de mica em composições vulcanizáveis de borracha natural quanto às propriedades mecânicas e dinâmico-mecânicas. As diversas composições também foram avaliadas quanto à densidade de ligações cruzadas. Todos os dados foram comparados aos da composição sem carga. Os resultados mostraram que a adição de teores crescentes de mica na borracha natural aumentou o módulo a 300%, a dureza, a densidade de ligaç (mais) ões cruzadas e a deformação permanente à compressão (DPC) das composições, por outro lado diminuiu a resiliência e a resistência à abrasão. O melhor desempenho quanto à resistência ao rasgamento e à tensão na ruptura foi obtido com 30phr de mica. As propriedades dinâmico-mecânicas (DMTA) corroboraram as propriedades mecânicas obtidas. Resumo em inglês In this work the influence of mica on the mechanical and dynamic mechanical properties of vulcanized natural rubber compositions was studied. The crosslinking density of the compositions was also determined. The data were compared to those of the unfilled composition. The results indicate an increase in modulus, hardness, crosslinking density and compression set as well as a decrease in resilience and abrasion resistance for the natural rubber compositions with increasing (mais) mica contents. The best performance for tear strength and stress at break was achieved with 30 phr of mica. The dynamic mechanical behavior of the compositions (DMTA) is in agreement with their mechanical properties.

Scientific Electronic Library Online (Portuguese)

17

Efeito do envelhecimento nas propriedades mecânicas e dinâmico-mecânicas de composições de borracha natural com mica/ Effect of ageing on mechanical and dynamic mechanical properties of natural rubber compositions with mica

Escócio, Viviane A.; Martins, Agnes F.; Visconte, Leila L. Y.; Nunes, Regina C. R.
2004-03-01

Resumo em português O estudo do efeito do envelhecimento em artefatos é principalmente importante quanto ao custo e qualidade, tornando o material atrativo ou não para produtos expostos a condições climáticas mais exigentes. Neste trabalho foi estudado o efeito do envelhecimento acelerado em composições vulcanizáveis de borracha natural com mica. O teor da carga mineral variou entre 0 e 40phr. As diferentes composições foram avaliadas, antes e após envelhecimento, quanto às propr (mais) iedades mecânicas e dinâmico-mecânicas, e também quanto à densidade de ligações cruzadas. Todos os dados foram comparados aos da composição sem carga. Os resultados mostraram que o teor de mica na formulação estudada, antes e após envelhecimento, não deve ser superior a 30phr. Pôde também ser concluído que as características da mica foram as responsáveis pela resistência ao envelhecimento das composições de borracha natural, nas condições escolhidas. As propriedades dinâmico-mecânicas, obtidas por DMTA, corroboraram as propriedades mecânicas avaliadas. Resumo em inglês The effects from ageing of materials is important in terms of cost and quality, particularly if the products are to be used under severe weather conditions. In this work, the effect of accelerated ageing in vulcanizable compositions of natural rubber and mica was studied. The amount of the mineral filler employed varied from 0 to 40 phr. The mechanical and dynamic-mechanical properties of different compositions were evaluated as well as crosslink density, before and after (mais) ageing, and the results were compared to those obtained for the unfilled composition. It was found that, either before or after ageing, the amount of mica must not exceed 30 phr. It was also concluded that mica is responsible for the protection of natural rubber composites from ageing under the selected conditions. The dynamic mechanical properties obtained from DMTA analysis corroborate the mechanical properties evaluated.

Scientific Electronic Library Online (Portuguese)

18

Caracterização das propriedades mecânicas e durabilidade biológica da madeira de Quercus faginea

Ramos, Sofia Isabel Nunes

Although the Portuguese oak wood (Quercus faginea L.) has been used in shipbuilding in the past, nowadays it has hardly any use and the knowledge about it is scarce, which requires the characterization and study of its potential for noble use. In this study physical and mechanical properties of Port...

DRIVER (Portuguese)

19

Efeitos do ultra-som terapêutico nas propriedades mecânicas do músculo esquelético após contusão/ Effects of therapeutic ultrasound on the mechanical properties of skeletal muscles after contusion

Matheus, JPC; Oliveira, FB; Gomide, LB; Milani, JGPO; Volpon, JB; Shimano, AC
2008-06-01

Resumo em português CONTEXTUALIZAÇÃO: O ultra-som terapêutico (UST) é um recurso comumente aplicado na aceleração do reparo tecidual de lesões musculares. A absorção das ondas ultra-sônicas é determinada pela freqüência e pela intensidade, sendo que, em uma mesma intensidade, a profundidade atingida por 1MHz é maior quando comparada a 3MHz. OBJETIVO: Analisar o comportamento das propriedades mecânicas de músculos submetidos à lesão aguda por impacto e tratados com UST, util (mais) izando as freqüências de 1 e 3MHz. MATERIAIS E MÉTODOS: Foram utilizadas 40 ratas Wistar (200,1±17,8g), divididas em quatro grupos: (1) controle; (2) lesão muscular sem tratamento; (3) lesão muscular tratada com UST de freqüência 1MHz (0,5W/cm²) e (4) lesão muscular tratada com UST de freqüência 3MHz (0,5W/cm²). A lesão foi provocada no músculo gastrocnêmio por mecanismo de impacto. O tratamento foi de cinco minutos diários durante seis dias consecutivos. Os músculos foram submetidos a ensaios mecânicos de tração em uma máquina universal de ensaios. RESULTADOS: As médias e desvios-padrão das propriedades mecânicas dos grupos lesionados e tratados com UST foram significativamente maiores quando comparadas ao grupo lesionado sem tratamento (p Resumo em inglês BACKGROUND: Therapeutic ultrasound is a resource commonly applied to speed up tissue repair in muscle injuries. The absorption of the ultrasound waves is determined by their frequency and intensity. For a given intensity, the depth reached by 1MHz is greater than the depth reached by 3MHz. OBJECTIVE: To analyze the mechanical properties of muscles subjected to acute impact injury treated with therapeutic ultrasound at the frequencies of 1 and 3MHz. METHODS: Forty female W (mais) istar rats (200.1±17.8g) were used, divided into four groups: (1) control; (2) muscle injury without treatment; (3) muscle injury treated with therapeutic ultrasound at the frequency of 1MHz (0.5W/cm²); and (4) muscle injury treated with therapeutic ultrasound at the frequency of 3MHz (0.5W/cm²). The injury was produced in the gastrocnemius muscle by means of an impact mechanism. The treatment consisted of a single five-minute session per day, for six consecutive days. The muscles were subjected to mechanical traction tests in a universal test machine. RESULTS: Means and standard deviations for the mechanical properties of the injured groups that received therapeutic ultrasound were significantly greater than those of the injured group without treatment (p

Scientific Electronic Library Online (Portuguese)

20

O ultra-som terapêutico não aumentou as propriedades mecânicas de tendões flexores após reparo/ Therapeutic ultrasound did not increase the mechanical properties of flexor tendons after their repair

Romano, Cristiane Vitaliano Graminha; Barbieri, Cláudio Henrique; Mazzer, Nilton; Volpon, José Batista; Shimano, Antônio Carlos; Roncaglia, Frederico Balbão
2010-01-01

Resumo em português OBJETIVO: Estudo experimental idealizado para investigar as propriedades mecânicas de tendões flexores profundos de coelhos submetidos à tenotomia seguida de tenorrafia e aplicação precoce de ultra-som terapêutico com diferentes intensidades, em comparação com tendões submetidos somente à tenorrafia. MATERIAL E MÉTODOS: Quarenta e quatro coelhos foram divididos em quatro grupos experimentais de acordo com a aplicação do ultra-som. Todos foram submetidos a uma (mais) secção do tendão flexor profundo na zona 2 e imobilizados com uma órtese mantida durante todo o experimento. O grupo A recebeu tratamento ultra-sônico com uma intensidade de 1,4 W/cm², o grupo B com 0,6 W/cm², ambos no modo contínuo, o grupo C com 0,6 W/cm² SATA, no modo pulsado à 50% e o grupo D não recebeu tratamento ultra-sônico algum. A frequência ultra-sônica empregada foi de 1 MHz. Após a eutanásia os tendões foram dissecados e submetidos ao ensaio mecânico de tração e análise histológica qualitativa. As propriedades mecânicas avaliadas foram: força máxima, deformação na força máxima e rigidez. RESULTADO: Não houve diferença estatisticamente significante entre os grupos experimentais. CONCLUSÃO: O ultra-som terapêutico não melhorou as propriedades mecânicas dos tendões flexores após reparo. Resumo em inglês OBJECTIVE: Experimental study idealized to investigate the mechanical properties of deep flexor tendons of rabbits that underwent the tenotomy followed by tenorrhaphy and early application of therapeutic ultrasound with different intensities, in comparison to tendons submitted to tenorrhaphy only. MATERIAL AND METHOD: Forty-four rabbits were divided into four experimental groups according to the ultrasound application. They were all submitted to a section of deep flexor t (mais) endon in zone 2 and immobilized with an orthosis maintained throughout the experiment. Group A received ultrasonic treatment with an intensity of 1.4 W/cm², group B with 0.6 W/cm², both in continuous mode, group C with 0.6 W/cm² SATA, in pulsated mode at 50% and group D did not receive any ultrasonic treatment. The ultrasonic frequency employed was 1 MHz. After euthanasia, the tendons were dissected and submitted to the mechanical test of traction and qualitative histological analysis. The evaluated mechanical properties were: maximum force, deformation in maximum force and stiffness. RESULTS: There were no statistically significant differences among the experimental groups. CONCLUSION: Therapeutic ultrasound did not improve the mechanical properties of the flexor tendons after repair.

Scientific Electronic Library Online (Portuguese)

21

Efeitos da estimulação elétrica neuromuscular durante a imobilização nas propriedades mecânicas do músculo esquelético/ Effects of neuromuscular electric stimulation during immobilization in the mechanical properties of the skeletal muscle/ Efectos de la estimulación eléctrica neuromuscular durante la inmovilización en las propiedades mecánicas del músculo esquelético

Matheus, João Paulo Chieregato; Gomide, Liana Barbaresco; Oliveira, Juliana Goulart Prata de; Volpon, José Batista; Shimano, Antônio Carlos
2007-02-01

Resumo em português A estimulação elétrica neuromuscular (EENM) é um importante recurso utilizado em medicina esportiva para acelerar processos de recuperação. O objetivo deste estudo foi analisar os efeitos da EENM durante a imobilização do músculo gastrocnêmio, em posições de alongamento (LP) e encurtamento (SP). Para tanto, 60 ratas fêmeas jovens Wistar foram distribuídas em seis grupos e acompanhadas durante sete dias: controle (C), eletroestimuladas (EE), imobilizadas em e (mais) ncurtamento (ISP), imobilizadas em alongamento (ILP), imobilizadas em encurtamento e eletroestimuladas (ISP + EE) e imobilizadas em alongamento e eletroestimuladas (ILP + EE). Para a imobilização, o membro posterior direito foi envolvido por uma malha tubular e ataduras de algodão juntamente à atadura gessada. A EENM foi utilizada com freqüência de 50Hz, 10 minutos por dia, totalizando 20 contrações em cada sessão. Após sete dias os animais foram submetidos a eutanásia e os músculos gastrocnêmios retirados para a realização do ensaio mecânico de tração em uma máquina universal de ensaios (EMIC®). A partir dos gráficos carga versus alongamento, foram calculadas as seguintes propriedades mecânicas: alongamento no limite de proporcionalidade (ALP), carga no limite de proporcionalidade (CLP) e rigidez. As imobilizações SP e LP promoveram reduções significativas (p Resumo em espanhol La estimulación eléctrica neuromuscular (EENM) es un importante recurso utilizado en medicina deportiva para acelerar procesos de recuperación. El objetivo de este estudio ha sido analizar los efectos de la EENM durante la inmovilización del músculo gastrocnemio, en posiciones de alongamiento (LP) y contracción (SP). Para tal fin, 60 ratones hembras jóvenes Wistar fueron distribuidas en seis grupos y monitoreadas durante 7 días: control (C), electro estimuladas (E (mais) E), inmovilizadas en contracción (ISP), inmovilizadas en alongamiento (ILP), inmovilizadas en contracción y electro estimuladas (ISP + EE) e inmovilizadas en alongamiento y electro estimuladas (ILP + EE). Para la inmovilización, el miembro posterior derecho fue envuelto por una malla tubular y vendas de algodón en conjunto con vendas de escayola. La EENM fue utilizada con una frecuencia de 50 Hz, 10 minutos por día, totalizando 20 contracciones en cada sesión. Después de 7 días los animales fueron sometidos a eutanasia y los músculos gastrocnemios fueron retirados para la realización del ensayo mecánico de tracción en una máquina universal de ensayos (EMIC®). A partir de los gráficos carga versus alongamiento se calculó las siguientes propiedades mecánicas: alongamiento en el límite de proporcionalidad (ALP), carga en el límite de proporcionalidad (CLP) y rigidez. Las inmovilizaciones SP y LP dieron reducciones significativas (p Resumo em inglês The neuromuscular electric stimulation (NMES) is an important tool used in sports medicine to accelerate the recovery process. The objective of this study was to analyze the effects of NMES during immobilization of the gastrocnemius muscle, in lengthened (LP) and shortened positions (SP). Sixty young female Wistar rats were distributed into six groups and followed for 7 days: control (C); electric stimulation (ES); immobilized in shortening (ISP); immobilized in lengtheni (mais) ng (ILP); immobilized in shortening and electric stimulation (ISP + ES) and immobilized in lengthening and electric stimulation (ILP + ES). For the immobilization, a tubular mesh and cotton rolls together with the plaster were wrapped around the rat's right posterior paw. NMES in a frequency of 50 Hz was used 10 minutes a day, totaling 20 contractions in each session. After 7 days the animals were sacrificed and their gastrocnemius muscles of the right paw were submitted to a mechanical test of traction in a universal test machine (EMIC®). From the load versus elongation curves the following mechanical properties were obtained: elongation in the yield limit (EPL), load in the yield limit (LPL) and stiffness. The SP and LP immobilizations promoted significant reductions (p

Scientific Electronic Library Online (Portuguese)

22

Influência da Estrutura química do co-monômero nas propriedades mecânicas e adesivas de redes epoxídicas/ Influence of chemical structure of co-monomer on mechanical and adhesive properties of epoxy networks

Garcia, Filiberto González; Leyva, Maria E.; Queiroz, Alvaro A. A. de
2010-06-01

Resumo em português As propriedades mecânicas e adesivas de formulações à base do prepolímero do éter diglicidílico do bisfenol A curadas com várias aminas alifáticas foram avaliadas no estado vítreo. Ensaios de impacto do tipo Izod e compressão uniaxial foram usados para determinar a energia de impacto, o módulo de elasticidade e a tensão de escoamento. Ensaios de adesão usando substrato de aço para uniões de simples sobreposição, descascamento em T, e de impacto foram rea (mais) lizados. O melhor comportamento mecânico e adesivo dos polímeros foi obtido quando existe alta flexibilidade entre as cadeias e/ou alto módulo elástico. O sistema DGEBA/AEP mostrou as melhores propriedades adesivas, alta flexibilidade e maior energia de impacto nos ensaios mecânicos. No entanto, apresentou baixo modulo elástico e tensão de escoamento. Além disso, exibe incremento nos ensaios de adesão de descascamento em T e nas uniões de impacto, por outro lado, apresenta uma redução na resistência das uniões de simples sobreposição. Resumo em inglês The mechanical and adhesive properties of epoxy formulations based on diglycidyl ether of bisphenol A cured with various aliphatic amines were evaluated in the glass state. Impact and uniaxial compression tests were used to determine the impact energy, elastic modulus and yield stress, respectively. The adhesion tests were carried out in steel-steel joints using single lap shear, T-peel and impact adhesive joints geometry. The better mechanical and adhesive behavior of th (mais) e networks is obtained for highly flexible chains and/or a high elastic modulus. The 1-(2-aminoethyl)piperazine epoxy network presents the best adhesive properties, high flexibility, and the largest impact energy. However, it possesses low elastic modulus and yield stress. Also, it exhibits increased peel strength and impact energy with a reduction in the lap shear strength.

Scientific Electronic Library Online (Portuguese)

23

Efeito da temperatura de queima em algumas propriedades mecânicas de cerâmica vermelha/ Effect of the firing temperature on some mechanical properties of red ceramic

Pinheiro, B. C. A.; Holanda, J. N. F.
2010-07-01

Resumo em português O objetivo deste trabalho foi avaliar algumas propriedades mecânicas de cerâmica vermelha como uma função da temperatura de queima. A massa argilosa usada foi caracterizada por meio da determinação da composição química, difração de raios X, distribuição do tamanho de partícula, morfologia, plasticidade e comportamento dilatométrico. Foram conformadas peças cerâmicas por prensagem uniaxial e queimadas a 850 ºC, 950 ºC e 1050 ºC. As peças queimadas for (mais) am avaliadas em termos de tensão de ruptura a flexão, módulo de elasticidade flexural, parâmetro de Weibull, tensão característica, massa específica aparente, absorção de água e área superficial específica. A evolução da microestrutura foi acompanhada via microscopia eletrônica de varredura e difração de raios X. Os resultados mostram que a temperatura de queima influencia diretamente nas propriedades mecânicas de cerâmica vermelha. Uma quantidade significativa de poros abertos foi eliminada, principalmente para temperaturas acima de 950 ºC. Os dados de tensão de ruptura a flexão resultaram em distribuição de Weibull, cujos parâmetros de Weibull estão compreendidos na faixa 8,59 -12,42. Resumo em inglês The aim of this work was to evaluate some mechanical properties of red ceramic as a function of the firing temperature. The clayey mass was characterized in terms of chemical composition, X-ray diffraction, particle size distribution, morphology, plasticity, and dilatometric behavior. Test specimens were prepared by uniaxial pressing and fired at 850 ºC, 950 ºC, and 1050 ºC. Fired test specimens were characterized in terms of flexural strength, elastic modulus, Weibull (mais) parameter, characteristic strength, apparent density, water absorption, and specific surface area. The microstructural evolution was accompanied by scanning electron microscopy and X-ray diffraction. The results showed that the firing temperature directly influenced in the mechanical properties of red ceramic. A high content of open pores was eliminated mainly above 950 ºC. The flexural strength test data resulted in Weibull distributions, whose Weibull parameters are in the range 8.59-12.42.

Scientific Electronic Library Online (Portuguese)

24

Modelos matemáticos para a relação entre composição química, microestrutura e propriedades mecânicas de ligas de alumínio fundidas hipoeutéticas e eutéticas/ Mathematical models for the chemical composition, the microstructure and the mechanical property relationship of hypoeutectics and eutectics aluminium foundry alloys

Corradi, Christiano Alves de Lima; Moita, Gray Farias; Biazi, Elenice
2010-09-01

Resumo em português Para realização de qualquer projeto mecânico, é necessário conhecer as características do material que será utilizado e projetar o equipamento, de tal maneira que qualquer tensão resultante não seja excessiva e não provoque falha. As propriedades mecânicas dos materiais são verificadas pela execução de experimentos ou ensaios de laboratório cuidadosamente programados, que reproduzem, o mais fielmente possível, as condições de serviço. Entretanto esses e (mais) nsaios mecânicos são destrutivos. Essa característica destrutiva do ensaio pode ser um problema, quando as peças que precisam de ser testadas não podem ser danificadas. Um outro complicador é a determinação de propriedades mecânicas em pontos específicos da peça, que se justifica, principalmente, em peças fundidas, onde as condições de resfriamento, as microssegregações e a ocorrência de defeitos se distribuem de maneira heterogêneas ao longo da peça. Uma vez que o processo de determinação da composição química e da estrutura metalográfi ca é realizado através de ensaios não destrutivos, eles poderiam substituir os ensaios mecânicos, se fosse estabelecida uma relação entre eles. Esse trabalho apresenta alguns modelos matemáticos gerados através de técnicas estatísticas de regressão linear múltipla, para a determinação das propriedades mecânicas de ligas de alumínio fundidas hipoeutéticas e eutéticas, a partir da realização de ensaios não destrutivos de microscopia e análise química. Resumo em inglês For the satisfactory accomplishment of any mechanical project, it is essential to know the characteristics of the materials that will be applied in the manufacturing process, in such a way that the resulting tension should not cause failure. The mechanical properties of the materials are established by the use of experiments or laboratory tests, carefully programmed, that reproduce, as accurately as possible, the real working conditions. However, these mechanical tests ar (mais) e destructive. The destructive characteristic of the experiments can be a problem when the parts that need to be tested cannot be damaged. Another complexity is the determination of mechanical properties in specifi c points of the assembly, which is justifi ed mainly in foundry pieces where the cooling conditions, the microssegregations and the occurrence of defects are distributed in a heterogeneous way along the part. Moreover, since the determination of the chemical composition and the microstructure is performed using non-destructive tests, they should be able to substitute the mechanical experiments, if a relationship between them could be established. This work presents mathematical models generated through statistical techniques of multiple linear regression, for the determination of the mechanical properties of hypoeutectic and eutectic aluminium foundry alloys using no destructive analyses, microstructure and chemical composition.

Scientific Electronic Library Online (Portuguese)

25

Influência de defeitos e diferentes processos de fabricação nas propriedades mecânicas finais de cerâmicas/ Influence of defects and different processes of manufacture on the final mechanical properties of ceramics

Schuller, D.; Bianchi, E. C.; Aguiar, P. R.
2008-12-01

Resumo em português Os materiais cerâmicos são atualmente cada vez utilizados como opção na engenharia mundial. Por se tratar de materiais com alta resistência mecânica, possuem muitas aplicações em diversas áreas, como por exemplo a de mancais, a automotiva (sensores, isoladores, catalisadores, pistões, válvulas, revestimentos), a de implantes biocompatíveis (dentário, substituição óssea, válvulas cardíacas), a de produtos sujeitos ao desgaste (guias), a de refratários (r (mais) evestimento de equipamento bélico, componentes de fornos), a eletrônica, e outras. Nos processos de fabricação da cerâmica há uma gama de fatores que contribuem para as características do produto final. Devido a isso, muitos pesquisadores têm trabalhado no estudo da influência de determinados defeitos e técnicas de produção de cerâmicas nas características do produto final. Este trabalho tem como objetivo fazer uma revisão bibliográfica de recentes artigos que analisam a influência de fatores como velocidade de queima, surgimento de trincas, porosidade, fases cristalinas, e tamanho de partículas, nas propriedades mecânicas finais das cerâmicas. Pode-se concluir que é possível aperfeiçoar o processo de fabricação da cerâmica a fim de promover as melhores propriedades mecânicas possíveis, conhecendo-se fatores prejudiciais e métodos adequados para se obter o melhor produto final. Resumo em inglês Currently, the ceramic materials are widely used as options in the engineering world. Because they are materials with high mechanical strength, they have many applications in several areas like: bearings components, automotive (sensors, insulators, catalysts, pistons, valves, coatings), biocompatible implants (dental, replacement bone, heart valves), products subject to wear (guides), refractories (coating of military equipment, components of ovens), electronics, and othe (mais) rs. In ceramic manufacturing there are many factors that contribute to the final features of the product. In this way many researchers have been working on the influences of defects and production technique on the final mechanical properties. This work has as objective to review the recent literature that study the influence of some factors like burn rates, crack growth, porosity, crystalline phases and particles size on the final mechanical characteristics of ceramics. We may conclude that is possible to improve the manufacturing process to promote the best possible mechanical properties knowing the harmful factors and the best techniques to take the optimized final products.

Scientific Electronic Library Online (Portuguese)

26

Estimulação elétrica neuromuscular e o alongamento passivo manual na recuperação das propriedades mecânicas do músculo gastrocnêmio imobilizado/ Neuromuscular electric stimulation and manual passive stretching when recovering mechanical properties of immobilized gastrocnemius muscles

Carvalho, Leonardo César; Shimano, Antonio Carlos; Picado, Celso Hermínio Ferraz
2008-01-01

Resumo em português Avaliamos a influência da imobilização, remobilização livre, remobilização com alongamento passivo manual, remobilização com estimulação elétrica neuromuscular (NMES) e remobilização por NMES e alongamento passivo manual associados sobre algumas propriedades mecânicas do músculo gastrocnêmio de ratas. Foram avaliadas 60 ratas divididas em seis grupos.Um destes grupos foi usado como controle. Todos os outros grupos tiveram o membro posterior direito imobil (mais) izado por 14 dias consecutivos. Destes grupos um foi imobilizado e em seguida avaliado, um foi liberado da imobilização e permaneceu nas gaiolas plásticas por 10 dias, outro foi submetido a técnica de alongamento passivo manual por 10 dias consecutivos, outro foi submetido a NMES por 10 dias consecutivos e o último foi submetido a NMES somado ao alongamento passivo manual por 10 dias consecutivos. Observamos que a imobilização reduziu os valores das propriedades mecânicas avaliadas no músculo. A remobilização livre não restabeleceu nenhuma das propriedades avaliadas. A remobilização por alongamento passivo manual devolveu ao músculo as propriedades de alongamento no limite de proporcionalidade, rigidez e resiliência. A remobilização estimulada por NMES restabeleceu todas as propriedades estudadas. A remobilização por NMES somada ao alongamento passivo restabeleceu as propriedades mecânicas de alongamento no limite máximo e de proporcionalidade e rigidez. Resumo em inglês We evaluated the influence of immobilization, free remobilization, remobilization with manual passive stretching, remobilization with neuromuscular electric stimulation (NMES) and remobilization with electric stimulation and associated passive stretching on some mechanical properties of the gastrocnemius muscle of female rats. Sixty female rats were assessed, being distributed into 6 experimental groups. One of these groups served as control. The animals of the five remai (mais) ning groups had their right posterior limb immobilized for 14 consecutive days. From the five groups, one was sacrificed right after the immobilization period, a second group was released from immobilization, a third was submitted to the manual passive stretching technique for 10 consecutive days, a fourth was submitted to NMES for 10 consecutive days and the last one was submitted to NMES and manual passive stretching for 10 consecutive days. We found that the immobilization caused a significant reduction of the mechanical properties values evaluated on the muscle. The free remobilization could not reestablish any of the properties. The remobilization by manual passive stretching restored the mechanical properties of stretching at the proportionality limit, stiffness and resilience. The remobilization stimulated by NMES reestablished all of studied properties. The remobilization by electric stimulation and passive stretching reestablished the mechanical properties of stretching at the maximum limit, proportionality limit, and stiffness.

Scientific Electronic Library Online (Portuguese)

27

Propriedades físico-mecânicas da madeira de canafístula aos 10 anos de idade/ Physical and mechanical properties of 10 years old wood trees of canafístula

Vivian, Magnos Alan; Modes, Karina Soares; Beltrame, Rafael; Souza, Joel Telles de; Santini, Elio José; Haselein, Clóvis Roberto
2010-05-01

Resumo em português A presente pesquisa objetivou caracterizar as propriedades físico-mecânicas da madeira de canafístula (Peltophorum dubium (Spreng.) Taub.) proveniente de árvores com 10 anos, por meio da determinação da massa específica básica, da retratibilidade, do módulo de elasticidade e do módulo de ruptura em flexão estática, do módulo de elasticidade em compressão perpendicular, da resistência máxima à compressão paralela à grã, da dureza de Janka, da resistênc (mais) ia máxima ao cisalhamento e da resistência ao choque. A determinação da massa específica básica e da retratibilidade seguiu as normas COPANT 30:1-004 (1971) e 30:1-005 (1971), respectivamente, e os ensaios mecânicos seguiram as normas ASTM D 143-94 (2000) e NF B 51-009 (1942). A massa específica básica e o coeficiente de anisotropia encontrado para a espécie permitiram classificar sua madeira como leve e medianamente estável, respectivamente; já os valores médios das propriedades mecânicas encontradas definem a madeira como de resistência fraca a média. As características tecnológicas determinadas indicam que sua madeira, quando proveniente de plantios jovens, deve ser utilizada com cautela em situações que exijam elevada estabilidade dimensional e resistência mecânica, sendo, portanto, aconselhável seu corte em idades mais avançadas. Resumo em inglês This research aimed to characterize the physic-mechanical properties of the canafístula wood (Peltophorum dubium (Spreng.) Taub.) from 10 years' old trees. There was determined the specific gravity, shrinkage, modulus of elasticity and modulus of rupture in static bending, modulus of elasticity in compression perpendicular to the grain, compression strength parallel to the grain, hardness, shear and impact resistance. Specific gravity and shrinkage determination were con (mais) ducted according to COPANT 30:1:004 (1971) and 30:1-005 (1971), respectively, and the mechanical tests followed ASTM D 143-94 (2000) and NF B51-009 (1942). The specific gravity and the ratio of tangential to radial shrinkage observed, ranked the wood as light and moderately stable, respectively, since the average values of mechanical properties classified the wood as weak to average strength. The technological characteristics observed indicate that when the wood is originated from short rotation plantation, it should be used with caution in situation which requires high dimensional stability and mechanical strength, suggesting the need of older trees.

Scientific Electronic Library Online (Portuguese)

28

Misturas NR/SBR: influência da composição e do modo de preparação sobre propriedades mecânicas e reométricas/ NR/SBR mixtures: influence of composition and preparation mode on the mechanical and rheological properties

Abreu Junior, Hérlon M. B.; Nunes, Regina C. R.; Visconte, Leila L. Y.
2010-01-01

Resumo em português Aplicações de produtos à base de borracha diversas vezes requerem um conjunto de propriedades as quais, geralmente, não são fornecidas por um único elastômero. Dessa forma, um dos recursos utilizados é a mistura de dois ou mais polímeros para obtenção de novas propriedades. Neste caso, os demais ingredientes que são adicionados, normalmente distribuem-se de forma irregular, dependendo de sua afinidade com cada uma das borrachas. O grau de dispersão de cada um (mais) desses ingredientes em cada fase elastomérica irá então influenciar a velocidade de cura e o grau de vulcanização e, certamente, terá conseqüências nas propriedades do produto final. Neste trabalho, a borracha natural (NR) foi misturada ao elastômero de butadieno-estireno (SBR) nas proporções de 75:25 e 50:50, em massa. As composições foram preparadas empregando-se quatro maneiras distintas para a incorporação dos aditivos. Os resultados das propriedades mecânicas mostraram que, apesar da utilização de uma mesma formulação, o modo de preparo tem grande influência sobre as propriedades. No caso da mistura NR/SBR as melhores propriedades são obtidas quando é favorecida a vulcanização da borracha que, isoladamente, apresenta propriedades inferiores. Resumo em inglês Frequently a set of properties required for a given application cannot be accomplished by one elastomer only and, thus, mixtures of two or more polymers must be employed. In these cases, the other ingredients added are normally dispersed in a non homogeneous way, depending on their affinity to each polymer. The degree of dispersion each additive experiences in each elastomeric phase will influence the rate and the degree of vulcanization and will certainly have consequenc (mais) es on the properties of the final product. In this work, natural rubber (NR) was mixed with styrene-butadiene elastomer (SBR) in 75:25 and 50:50 w/w ratios. The compositions were prepared in a two-roll mill, by introducing the additives according to four different modes. The results of mechanical properties show that, although having been prepared following the same formulation, the properties of these mixtures are influenced by the preparation mode. For NR/SBR blends, the best properties are achieved when one favours the vulcanization of the rubber with inferior properties.

Scientific Electronic Library Online (Portuguese)

29

Influência da adição de plastificante do processo de reticulação na morfologia, absorção de aguá e propriedades mecânicas de filmes de alginato de sódio/ Influence of plasticizer addition and crosslinking process on morohology, water absoption and mechanical properties of sodium alginate films

Lima, Aline Margarete Furuyama; Andreani, Larissa; Soldi, Valdir; Borsali, Redouane
2007-08-01

Resumo em inglês The effects of sorbitol and formaldehyde on the morphology, water absorption and mechanical properties of sodium alginate films were analyzed. The morphology of the films indicated the presence of small aggregates in the surface of uncrosslinked films, which disappeared with the crosslinking process. The water uptake and percentage of elongation increased with the addition of sorbitol in uncrosslinked films. At the same time, a decrease in tensile strength and Young's mod (mais) ulus occurred. The swelling ratio and water uptake of crosslinked alginate/sorbitol films decreased with an increase in sorbitol content suggesting an enhanced crosslinking density due to the presence of plasticizer.

Scientific Electronic Library Online (Portuguese)

30

Propriedades reométricas e mecânicas e morfologia de compósitos desenvolvidos com resíduos elastoméricos vulcanizados/ Cure characteristics, mechanical properties and morphology of composites developed with addition of elastomeric vulcanized ground scraps

Zanchet, Aline; Dal’Acqua, Nicolle; Weber, Tatiana; Crespo, Janaina S.; Brandalise, Rosmary N.; Nunes, Regina C. R.
2007-03-01

Resumo em português Uma alternativa para as empresas geradoras de resíduos elastoméricos é a incorporação dos mesmos em suas formulações. Esse trabalho tem como objetivo preparar compósitos a partir da incorporação de resíduos industriais de SBR (copolímero de butadieno-estireno) e de EPDM (terpolímero de etileno-propileno-dieno), em formulação ASTM específica para cada tipo de elastômero. Foram avaliadas as propriedades reométricas, mecânicas e morfológicas dos compósit (mais) os desenvolvidos. A incorporação do resíduo permitiu a obtenção de produtos que vulcanizam em menores tempos quando comparados a composições sem resíduo. A quantidade de resíduo, para o melhor resultado de resistência à tração foi de 37 e de 196 phr para os compósitos com SBR e EPDM, respectivamente. As micrografias de MEV corroboraram os resultados mecânicos dessas composições, indicando melhor homogeneidade do resíduo na respectiva matriz elastomérica. Resumo em inglês One alternative for elastomeric scraps generation is its incorporation in conventional formulations in the industry itself. In this work, compositions with incorporation of SBR (styrene butadiene rubber) and EPDM (ethylene propylene diene rubber) industrial scraps, in specific ASTM formulation for each elastomer, were prepared. Rheometric characteristics, mechanical properties and the morphology of the compounds developed were evaluated. With the ground scraps incorporati (mais) on the vulcanization time decreases, comparing with compounds without ground scraps. The amount of scraps for the best tensile strength properties was 37 and 196 phr for SBR and EPDM compositions, respectively. Micrographs corroborated the mechanical results, indicating the best homogeneity of the scraps in the elastomeric matrix for these compositions.

Scientific Electronic Library Online (Portuguese)

31

Nanocompósitos de PEAD/PEBDL: avaliação da esfoliação da argila organofílica pela aplicação do modelo de Nielsen e das propriedades mecânicas, ópticas e permeabilidade/ PEAD/PEBDL composites: evaluation of the exfoliation of organophilic clay using the Nielsen model and of the mechanical, optical and permeability properties

Morales, Ana R.; Cruz, Carolina V. M. da; Peres, Leila; Ito, Edson N.
2010-01-01

Resumo em português Uma blenda de polietileno de alta densidade e polietileno de baixa densidade (PEAD/PEBDL) comumente utilizada em filmes de embalagem foi modificada com argila montmorilonita organofílica comercial para obter nanocompósitos com melhores propriedades de barreira. Amostras com 5 e 7,5% de argila (em massa) foram estudadas em diferentes condições de processamento. Filmes produzidos com os nanocompósitos foram avaliados quanto à dispersão da argila por difração de rai (mais) o X e Microscopia Eletrônica de Transmissão. As propriedades de barreira dos filmes foram determinadas pelas medições de permeabilidade ao oxigênio e ao vapor d'água. As propriedades mecânicas e ópticas também foram determinadas. Observou-se uma estrutura com a argila parcialmente esfoliada e intercalada. A permeabilidade ao oxigênio diminuiu significativamente enquanto a permeabilidade à água foi pouco influenciada. As propriedades mecânicas e a transparência dos filmes foram pouco alteradas. O modelo de Nielsen foi aplicado para os dados de permeabilidade relativa e demonstrou ser um ótimo recurso para a avaliação do grau de esfoliação da argila para as diferentes amostras, que foram confirmadas pelas análises realizadas em microscopia eletrônica de transmissão. Resumo em inglês A typical high density polyethylene and linear low density polyethylene (HDPE/LLDPE) blend used in flexible packaging was modified with commercial organophylic montmorilonite clay to obtain nanocomposites with superior barrier properties. Samples with 5 and 7.5% of clay were prepared under different processing conditions. Films produced from the nanocomposites were evaluated in terms of oxygen and water vapor permeation and also by X-ray diffraction and Transmission Elect (mais) ron Microscopy. Tensile and optical properties were also evaluated. The clay showed to be intercalated and partially exfoliated. The oxygen permeation was mainly reduced and the vapor permeation was weakly modified. The mechanical properties and transparency did not change significantly. Nielsen's model was applied considering the relative permeability coefficient. This method was able to give an estimate of the exfoliation state of the samples, supported by the transmission electron microscopy.

Scientific Electronic Library Online (Portuguese)

32

Avaliação das propriedades termo-mecânicas de borracha nitrílica após ensaio de compatibilidade de acordo com ASTM D 3455/ Thermal-mechanical properties evaluation of nitrilic rubber after compatibility test according to ASTM D 3455

Meyer, Adailze L.; Souza, Gabriel P. de; Oliveira, Suely M. de; Tomczak, Fábio; Wasilkoski, Cleuza; Pinto, Carlos Eduardo da S.
2006-01-01

Resumo em português O copolímero butadieno - acrilonitrila - NBR é comumente aplicado na confecção de gaxetas e anéis de vedação para transformadores elétricos isolados a óleo mineral. Durante o uso esses materiais permanecem em contato com óleo em temperaturas próximas a 90 ºC provocando alterações físicas e químicas no material elastomérico e no óleo. Neste trabalho, estudou-se a variação das propriedades mecânicas do elastômero resultantes do ensaio de compatibilidad (mais) e (ASTM D 3455)[3]. A caracterização mecânica foi realizada por ensaios de resistência a tração, dureza e análise dinâmico-mecânica (DMA). A verificação da estabilidade térmica e a composição do NBR foram obtidas através de análise termogravimétrica (TGA). Resumo em inglês The copolymer of acrylonitrile and butadiene - NBR is commonly used to manufacture gaskets and seals to be used in electrical transformers insulated by mineral oil. During operation those materials are constantly in contact with oil at temperatures that can reach 90 ºC, causing physical and chemicals changes in both gaskets and oil. In this paper the changes in elastomer mechanical properties after the compatibility test were studied (ASTM D 3455)[3]. This characterizati (mais) on was done by tension properties, hardness and dynamical mechanical analysis (DMA). The evaluation of thermal stability and composition of the NBR was carried out through thermogravimetry analysis (TG).

Scientific Electronic Library Online (Portuguese)

33

Nanocompósitos de poliamida 6 e argila organofílica: estudo da cristalinidade e propriedades mecânicas/ Nanocomposites of polyamide 6 and organoclay: crystallinity and study of mechanical properties

Oliveira, Marcelo F. L. de; Oliveira, Márcia G. de; Leite, Márcia C. A. M.
2011-01-01

Resumo em português Nanocompósitos de poliamida 6 e argila organofílica claytone 40 foram preparados por intercalação por fusão, utilizando misturador de câmara interna equipado com rotores do tipo Roller. A adição de teores crescentes de claytone 40 na matriz de PA6 foi avaliada quanto ao grau de dispersão, cristalinidade, propriedades térmicas e as propriedades mecânicas. As composições obtidas foram caracterizadas por difração de raios X (DRX), calorimetria diferencial de v (mais) arredura (DSC), microscopia eletrônica de varredura (MEV) e propriedades mecânicas. Os difratogramas e as micrografias sugeriram a ocorrência de formação de estruturas parcialmente esfoliadas e/ ou intercaladas, fato que foi associado com o aumento nos valores de tensão e o módulo elástico. A comparação entre os resultados de DSC e DRX das misturas revelaram alterações estruturais na cristalinidade em relação à PA6 correlacionando a cristalinidade à variação nas propriedades mecânicas. Resumo em inglês Nanocomposites of polyamide 6 and Claytone 40 organoclay were prepared with the melt intercalation technique using an internal mixer chamber coupled with roller type rotors. The addition of increasing amounts of Claytone 40 into the PA6 matrix was evaluated for the degree of dispersion, crystallinity, thermal and mechanical properties. The compositions were characterized with X-ray diffraction (XRD), differential scanning calorimetry (DSC), scanning electron microscopy (S (mais) EM) and mechanical properties. The diffraction patterns and microscope images suggest the formation of partially exfoliated or intercalated structures, which was associated with an increase in stress values and elastic modulus. The comparison of DSC and XRD results from the mixtures revealed changes in the behavior of crystalline structures, thus indicating that the PA6 crystallinity is correlated with the mechanical properties.

Scientific Electronic Library Online (Portuguese)

34

Avaliação das propriedades físicas e mecânicas de papéis reciclados artesanais com resíduos de bananeira ou palha de arroz/ Evaluation of physical and mechanical properties of handmade recycled papers reinforced with pulp of banana tree or rice straw

Bastianello, S.F.; Testa, R.C.; Pezzin, A.P.T.; Silva, D.A.K.
2009-01-01

Resumo em português As culturas de banana e arroz são predominantes na região Nordeste do Estado de Santa Catarina e no caso da banana chegam a gerar 200 toneladas/ano de resíduos entre, pseudocaules, engaços e folhas, que geralmente são incorporados ao solo. Desta forma, este trabalho teve como objetivo avaliar a influência da adição de polpa de fibras vegetais nas propriedades físicas e mecânicas de papéis reciclados de forma artesanal, bem como reaproveitar os resíduos gerados (mais) por estas culturas. As polpas contendo fibras de palha de arroz ou de pseudocaule de bananeira foram acrescentadas à polpa de papel nas proporções de 0, 10, 20 e 30 % em massa (m/m) e as folhas obtidas foram submetidas aos ensaios de gramatura, espessura, permeância ao ar, resistência à tração, resistência ao esmagamento do anel e resistência ao arrebentamento segundo normas NBR apropriadas. Analisados os ensaios físicos e mecânicos, constatou-se que os resultados mais expressivos foram registrados para as folhas que continham 20 % (m/m) de pasta de bananeira. Resumo em inglês The cultures of bananas and rice are predominant in the Northeast of Santa Catarina State and in the case of banana the, reach 200 ton/year of waste, including pseudo-stem, stalks and leaves, which are usually incorporated into the soil. Thus, this work analyzed the physical-mechanics properties of handmade papers produced with recycled fibers with local agro-industry resources, pulps of banana tree (Musa cavendishii) and rice straw (Oriza sativa). Handmade papers were pr (mais) oduced with the mixtures whose compositions had 10 %, 20 % and 30 wt% of banana or rice pulps. The compounds produced were using physical and mechanical tests, such as: gramature, thickness, porosity, tensile strength, crushing of the ring strength, and stretching strength in agreement with appropriated NBRs. The physical and mechanical tests pointed out that the samples with 20 % of banana pulp present more expressive results.

Scientific Electronic Library Online (Portuguese)

35

Desenvolvimento de nanocompósitos polipropileno/argila bentonita brasileira: I tratamento da argila e influência de compatibilizantes polares nas propriedades mecânicas/ Development of polypropylene/brazilian bentonite clay nanocomposites: I treatment of clay and the influence of the compatibilizers on the mechanical properties

Rodrigues, André W.; Brasileiro, Maria I.; Araújo, Williane D.; Araújo, Edcleide M.; Neves, Gelmires A.; Melo, Tomás J. A. de
2007-09-01

Resumo em português Os nanocompósitos de polipropileno/ bentonita e polipropileno/compatibilizante/bentonita foram preparados empregando uma extrusora dupla rosca acoplada a um Reômetro de Torque Haake. A argila bentonita natural proveniente do Município de Boa Vista - PB passou por um processo de purificação para em seguida ser aditivada com carbonato de sódio e posteriormente tratadas com o sal quaternário de amônia, visando a obter argila organofílica. As argilas foram caracteriz (mais) adas por granulometria por difração de laser, análise química, espectroscopia de infravermelho e DR-X. Os resultados de granulometria e análise química mostraram que o processo de purificação foi eficiente em retirar as frações mais grosseiras mantendo as frações finas bem como na eliminação de minerais acessórios. Os resultados de FTIR e DR-X mostraram que o sal quaternário de amônio foi incorporado à argila confirmando a organofilização. Posteriormente a argila bentonita organofílica foi incorporada ao polipropileno (PP) e PP/compatibilizante (PP-g-AA e PP-g-MA são polipropilenos enxertados com ácido acrílico e anidrido maleico, respectivamente). A formação dos nanocompósitos bem como as propriedades das misturas PP/ORG (ORG - argila organofílica) e PP/compatibilizante/ORG foram verificadas por DR-X, MET e propriedades mecânicas. As análises de DR-X, MET mostraram que pode ter ocorrido a formação de nanocompósitos intercalado devido aos deslocamentos dos picos para ângulos de 2q inferiores. Os resultados das propriedades mecânicas mostraram que houve uma melhoria em algumas propriedades mecânicas. Resumo em inglês In this work, polypropylene/bentonite and polypropylene/compatibilizer/bentonite nanocomposites were prepared by the melt intercalation method, using a counter-rotating intermeshing twin-screw extruder attached to a Haake System 90 Rheometer. Initially the natural bentonite clay, from Boa Vista - PB, was subjected to a purification process and then treated with sodium carbonate. Further, it was treated with ammonium quaternary salt to obtain an organoclay. The clays were (mais) characterized, according to granulometric, by laser diffraction, chemical analysis, infrared spectroscopy - FTIR, and X ray diffraction - XRD. The granulometric and chemical analysis results showed that the purification process was effective for removing the coarse fractions and eliminating some accessory minerals. FTIR and XRD results showed that the ammonium quaternary salt was incorporated to the clay, confirming the organophilization. In the subsequent stage of this work, the bentonite organoclay was incorporated to both polypropylene (PP) and PP/compatibilizer (PPgAA and PPgMA are polypropylenes grafting acrylic acid and maleic anhydride, respectively). The formation of nanocomposites as well as the properties of PP/ORG (ORG - organoclay) and PP/compatibilizer/ORG mixtures were analyzed by XRD, MET and mechanical properties. XRD and MET results showed that the formation of interlayer/flocculated nanocomposites has occurred for PP/compatibilizer/ORG systems. The mechanical properties results showed that some mechanical properties (final elongation and toughness) have been considerably improved.

Scientific Electronic Library Online (Portuguese)

36

Avaliação da morfologia e propriedades termo-mecânicas em nanocompósitos de PVC/ Evaluation of mechanical-thermal properties and morphological in PVC nanocomposites

Silva, Rodrigo P. da; Mauler, Raquel S.; Oliveira, Ricardo V. B. de; Salles, Cleia A.
2010-01-01

Resumo em português A busca pela utilização de cargas de reforço aos materiais poliméricos tem sido o grande alvo dos pesquisadores e da indústria. Neste trabalho nanocompósitos de PVC foram obtidos mediante a mistura no estado fundido utilizando-se uma extrusora monorosca. Adicionalmente, três diferentes concentrações de montmorilonita organofílica 1, 2 e 5% em massa foram incorporadas. Estes foram caracterizados por suas morfologias, propriedades térmicas e termo-dinâmico-mecâ (mais) nicas. O grau de intercalação e esfoliação dos nanocompósitos foi caracterizado por MET. As análises termogravimétricas não demonstraram um aumento na estabilidade térmica dos nanocompósitos com a concentração de argila. Resumo em inglês The search for the use of reinforcement fillers into polymeric materials has been the great objective of researchers and industry. In this work PVC nanocomposites were obtained by melt blending in a single-screw extruder. Additionally, three different organophilic montmorillonite concentrations of 1, 2 and 5% wt were incorporated. These were characterized by morphology, thermal and thermo-dynamic-mechanical properties. The degree of intercalation and exfoliation of nanoco (mais) mposites was characterized by MET. The thermogravimetric analysis did not show an increase in the thermal stability of the nanocomposites with the clay content.

Scientific Electronic Library Online (Portuguese)

37

Influência da Massa Específica nas Propriedades Físico-Mecânicas de Painéis Aglomerados/ Influence of the Density in Physical-Mechanical Properties of Particleboards/ Influence de la Masse Spécifique dans les Propriétés Physico - Mécaniques de Panneaux Agglomérats

Melo, Rafael Rodolfo de; Menezzi, Cláudio Henrique Soares Del
2010-06-01

Resumo em português O objectivo desse trabalho foi avaliar a influência da massa específica nas propriedades físico-mecânicas de chapas aglomeradas confeccionadas com partículas de Eucalyptus grandis W. Hill ex Maiden. Para isso, foram testadas três densidades: 0,6; 0,7 e 0,8g/cm³. Para cada nível de densidade foram produzidos quatro painéis com as seguintes características: 8% de resina ureia-formaldeído, 1% de parafina. A prensagem foi feita a 3,0 MPa por 8 minutos a uma tempera (mais) tura de 180ºC. Foram retirados corpos-de-prova para ensaios físicos (massa específica, teor de humidade, absorção de água e inchamento em espessura) e mecânicos (flexão estática, tracção perpendicular à superfície do painel e resistência ao arrancamento de parafusos). De acordo com os resultados, ficou evidenciado que o aumento da massa específica proporcionou um aumento significativo nas propriedades mecânicas. Por outro lado, as propriedades de estabilidade dimensional tiveram um comportamento antagónico: maior massa específica, menor absorção e maior inchamento em espessura. Resumo em inglês This paper aimed at evaluating the effect of the board density on physical and mechanical properties of particleboards made from Eucalyptus grandis W. Hill ex Maiden. Three board densities were tested: 0.6, 0.7, and 0.8g/cm³. For each density level four boards were manufactured as follow: 8% urea-formaldehyde resin, 1% wax, 180ºC hot-pressing for 8 minutes and 3.0 MPa. For each treatment, samples for the physical assays (density, moisture content, water absorption and t (mais) hickness swelling) and mechanical assays (static bending, internal bonding and screw withdrawal) had been removed. Results indicated relations between board density and properties evaluated, with the best relations for mechanical properties, that increased with panels' densification. The water absorption reduced with increased board density and thickness swelling, as an inverse behavior presented.

Scientific Electronic Library Online (Portuguese)

38

Efeito de reticulante na morfologia e propriedades físico-mecânicas de espumas poliméricas obtidas com EVA e EPDM/ The effect of a crosslinking agent on the morphology and physical and mechanical properties of polymer foams based on EVA and EPDM

Azevedo, Joyce B; Chávez, Manuel Alpire; Rabello, Marcelo S
2011-01-01

Resumo em português Espumas poliméricas são materiais bifásicos constituídos por uma matriz polimérica sólida e por uma fase gasosa proveniente de um agente de expansão. Produtos obtidos com estes materiais vêm ganhando bastante espaço no mercado por apresentar boas propriedades mecânicas aliadas à baixa densidade e baixo custo. O uso de EVA com elastômeros tem sido uma alternativa para proporcionar propriedades mais nobres a esses compostos expansíveis. Dentre os elastômeros u (mais) tilizados, o EPDM apresenta um potencial de aplicação elevado por apresentar boa compatibilidade com as poliolefinas. Como na fabricação da espuma tem-se simultaneamente reações de reticulação e de formação gases de expansão, o balanço desses efeitos tem forte influência sobre as características físicas do produto. Neste estudo, avaliou-se o efeito de um agente reticulante nas formulações de espumas de EVA/EPDM. As propriedades físico-mecânicas, reométricas e morfológicas de misturas EVA/EPDM com diversas proporções de peróxido de dicumila, utilizado como agente de reticulação, foram avaliadas. Os resultados mostraram que o teor de reticulante apresenta forte influência nas características técnicas das espumas obtidas. Resumo em inglês Polymer foams are biphasic materials prepared with a polymer matrix and a gaseous phase from a foaming agent. Products based on this type of material are currently in a good market position due to the good mechanical properties, low density and competitive cost. Blending EVA with elastomers is a feasible alternative to enhance the properties of the expandable compounds. Among the elastomers used as a blend component with EVA, EPDM has a high potential since it has a good (mais) compatibility with polyolefins. Considering that during the foam processing there are simultaneous crosslinking reactions and the formation of gases, the balance between these two effects has a strong influence over the physical characteristics of the final product. In this study the effect of a crosslinking agent on EVA/EPDM foams was investigated. The physical, mechanical and rheometric properties, as well as the foam morphology, were analyzed as a function of dicumil peroxide, used as a crosslinking agent. The results showed that this additive has a strong influence in the crooking and expansion of the compounds, affecting their properties.

Scientific Electronic Library Online (Portuguese)

39

Influência da carga mecânica de máquina sobre propriedades físicas de um cambissolo háplico/ Influence of mechanical load levels on physical properties of a eutric cambisol

Cavalieri, Karina Maria Vieira; Silva, Álvaro Pires da; Arvidsson, Johan; Tormena, Cássio Antonio
2009-06-01

Resumo em português O objetivo deste estudo foi avaliar os efeitos de diferentes cargas mecânicas de máquinas sobre as propriedades físicas de um Cambissolo Háplico classe textural franco-arenoso/franco-argilo-arenoso. A distribuição das pressões (kPa) no solo foi detectada por sensores localizados em diferentes camadas no solo. As propriedades físicas avaliadas foram a densidade do solo (Ds) e a resistência à penetração (RP) na linha e na entrelinha da cultura da beterraba-açuc (mais) areira (Beta vulgaris L.), até a profundidade de 0,30 m. Os tratamentos foram: sem pressão extra exercida pela semeadora, denominado sem compactação (SC); pressão exercida pela semeadora considerada de baixa carga (BC); pressão exercida pela semeadora considerada de alta carga (AC); e pressão exercida pelas rodas do trator usado no preparo do solo ou carga do trator (CT). Em relação à distribuição das cargas no solo, na camada de 0-0,10 m foram detectados valores de pressão no solo acima de 120 kPa, considerados muito altos. O incremento de pressão do tratamento SC para AC resultou em maiores pressões na camada de 0-0,10 m comparada à de 0,10-0,20 m, enquanto o tratamento CT resultou em maiores pressões no solo na camada de 0,10-0,20 m, em relação aos outros tratamentos. Em decorrência das cargas mecânicas aplicadas, verificou-se aumento da Ds em superfície, na sequência SC Resumo em inglês The objective of this study was to evaluate the effects of different mechanical loads on soil physical properties of a Eutric Cambisol with loam sandy texture. The soil load distribution (kPa) was measured in situ by sensors placed in different soil layers. The soil physical properties evaluated were the bulk density (Ds) and the soil penetration resistance (RP) on sugarbeet (Beta vulgaris L.) row and interrow down to 0.30 m depth. The treatments were: without extra press (mais) ure exerted by the sowing machine, or no-compaction (SC); low pressure exerted by the sowing machine, named low load (BC); high pressure exerted the sowing machine, named high load (AC) and load pressure exerted by the tractor wheels used in the seedbed preparation, or tractor load (CT). The soil load distribution data indicated that the 0-0.10 m layer had soil stresses values higher than 120 kPa, which are considered very high. The increase on soil stresses from treatments SC to AC caused higher stress on topsoil than in the 0.10-0.20 m depth, while that under CT treatment showed higher stress at the 0.10-0.20 m layer. As a consequence of the soil stress load it was verified an increase on Ds in the more superficial soil layer (0-10 cm), and it followed the sequence: SC

Scientific Electronic Library Online (Portuguese)

40

Efeitos da agitação mecânica e de adição de refinador de grão na microestrutura e propriedade mecânica de fundidos da liga Al-Sn/ Effects of mechanical agitation and of the addition of grain refiner on the microstructure and mechanical properties of castings of the Al-Sn alloy

Osório, W. R.; Peixoto, L. C.; Garcia, A.
2009-01-01

Resumo em português O objetivo deste artigo foi avaliar os efeitos da agitação mecânica e de adição de refinador de grão na macro e microestrutura e propriedades mecânicas resultantes de três (03) diferentes procedimentos de fundição utilizando-se de uma liga Al-10%Sn. Os processos de fundição para obtenção das amostras foram: i)fundição por gravidade convencional, ii) fundição por gravidade com agitação mecânica do líquido em resfriamento, iii) fundição por gravidade (mais) com adição de refinadores de grão, particularmente adição de 1,5% (em peso) da liga-mãe Al-5%Ti-1%B e iv) fundição por gravidade com adição de refinador de grão e agitação mecânica. Resultados experimentais mostraram que os diferentes procedimentos de fundição propiciaram diferentes valores médios dos tamanhos dos grãos correlacionados com diferentes taxas de resfriamento. Taxas na ordem de 0,60 a 0,75 ºC/s propiciaram microestruturas celulares e taxas na ordem de 1,75 a 2,55 ºC/s resultaram em morfologias dendríticas. Foram avaliados também os níveis de porosidade entre as amostras estudadas. Foram correlacionados os resultados do comportamento mecânico, particularmente, limite de resistência à tração, limite de escoamento e alongamento específico com os tamanhos dos grãos, os espaçamentos dendríticos e celulares e os níveis de porosidade resultantes dos três diferentes procedimentos de obtenção das amostras. Conclui-se que o controle da microestrutura do lingote pode ser usado como um método alternativo para produzir componentes fundidos com melhores resultados de propriedades mecânicas e qualidade dos fundidos. Resumo em inglês The aim of this article was to evaluate the effects of mechanical stirring and grain refiner addition in three different Al-10wt%Sn casting alloys on their resulting macro and microstructures and mechanical properties. These samples were obtained by using: i) die casting, ii) casting with mechanical stirring, iii) die casting using grain refiner (master alloy Al-5wt%Ti-1wt%B) and iv) die casting with grain refiner and mechanical stirring. Experimental results presented di (mais) fferent mean grain sizes and different cooling rates when different casting procedures were applied. Cellular and dendritic morphologies were observed when ranges of cooling rates of about 0.6 to 0.75 ºC/s and of 1.75 to 2.55 ºC/s were employed, respectively. Porosity levels of all studied alloy samples were also analyzed. Results of the mechanical behavior, particularly, ultimate tensile strength, yield strength and specific elongation were correlated with mean grain sizes, dendritic arm and cellular spacings and porosity levels attained for the three different cast Al-10wt%Sn alloy samples. The control of the resulting microstructure of the as-cast product may be used as an alternative way to produce sound casting alloy components with improvement in the mechanical properties.

Scientific Electronic Library Online (Portuguese)

41

Influência da adição de uma carga nanoparticulada no desempenho de compósitos poliuretano/fibra de juta/ Influence of a nanoparticulate filler addition on the mechanical properties of polyurethane/jute fiber composites

Neto, José R. A.; Carvalho, Laura H. de; Araújo, Edcleide M.
2007-03-01

Resumo em português Neste trabalho as propriedades mecânicas de um compósito, formado a partir de uma matriz de poliuretano derivado do óleo de mamona e reforçada por um tecido tramado de juta, foram avaliadas. O efeito da adição de pequenos teores de bentonita cálcica e sódica sobre as propriedades mecânicas da matriz de poliuretano e de compósitos poliuretano/juta também foi investigado. Os resultados indicam que a incorporação de fibra de juta à matriz poliuretana promoveu m (mais) elhora significativa nas propriedades sob tração dos compósitos. A adição de pequenos teores de argila à matriz alterou o desempenho mecânico dos compósitos, porém os resultados não foram os esperados. O compósito híbrido poliuretano/argila/fibra de juta, contudo, apresentou propriedades mecânicas superiores às dos compósitos reforçados unicamente com tecido de juta, o que indica uma atuação sinérgica dos reforços híbridos argila/juta. Resumo em inglês In this work the mechanical properties of polyurethane/jute fiber composites were evaluated as a function of fiber content and mineral filler addition. A polyurethane (PU) derived from castor oil was used as the matrix and hessian cloth as reinforcement. The effect of the incorporation of small amounts of local clay (bentonite), in its calcium and sodium forms, on the mechanical properties of polyurethane/jute composites was also investigated. The results indicate that th (mais) e tensile properties of the composites substantially increased with jute fiber addition and that although the mechanical properties of the matrix were affected by the addition of nanoparticulate clay, the improvement was not as expected. This was attributed to poor mixing and dispersion of the filler, which was confirmed by SEM. A synergistic effect was observed for the hybrid clay/jute fiber composites, with considerable improvement in the mechanical performance of the hybrid composites.

Scientific Electronic Library Online (Portuguese)

42

Compósitos de polietileno reciclado e partículas de madeira de reflorestamento tratadas com polietileno modificado/ Composites of recycled polyethylene and reforestation wood particles treated with modified polyethylene

Redighieri, Karla I.; Costa, Dilma A.
2008-03-01

Resumo em português Neste trabalho foram obtidos compósitos poliméricos de partículas de madeira de eucalipto e polietileno de baixa densidade reciclado (LDPE reciclado). O polietileno funcionalizado com anidrido maleico (PE-g-MA) foi utilizado como agente compatibilizante para conferir melhor adesão entre a matriz e a fase dispersa. As propriedades mecânicas de tração e flexão foram determinadas de acordo com as normas da American Society for Testing and Materials (ASTM). Os resulta (mais) dos mostraram que o tratamento das partículas de eucalipto com PE-g-MA aumentou as propriedades mecânicas dos compósitos, em relação aos compósitos contendo partículas sem tratamento. Entretanto, as propriedades mecânicas de tração desses compósitos foram reduzidas depois de longo tempo de imersão em água. Resumo em inglês In this work polymeric composites were obtained from eucalypt wood particles and recycled low density polyethylene (recycled LDPE). The maleic anhydride functionalized PE (PE-g-MA) was used as compatibiliser agent to provide better adhesion between the matrix and the dispersed phase. The mechanical properties of tensile and flexural were determined in accordance with the American Society for Testing and Materials (ASTM) procedures. The results showed that PE-g-MA as compa (mais) tibiliser agent increased the mechanical properties, in relation to the composites containing particles without treatment. However, the tensile mechanical properties of these polymeric composites were reduced after long time of immersion in water.

Scientific Electronic Library Online (Portuguese)

43

Efeito da sequência de mistura nas propriedades de blendas PA6/ABS compatibilizadas com o copolímero SMA/ Effect from the blending sequence on the properties of PA6/ABS blends compatibilized with SMA copolymer

Oliveira, Amanda D. de; Larocca, Nelson M; Pessan, Luiz A
2011-01-01

Resumo em português Blendas de poliamida 6 (PA6) com acrilonitrila-butadieno-estireno (ABS) foram preparadas em uma extrusora de rosca dupla, utilizando-se o copolímero estireno-anidrido maleico (SMA), com 7% de anidrido maleico, como compatibilizante. O efeito de três sequências de mistura na microestrutura e propriedades das blendas foi estudado. A morfologia e as propriedades mecânicas dos materiais foram caracterizadas por microscopia eletrônica de transmissão (MET) e testes de res (mais) istência ao impacto e módulo de elasticidade, respectivamente. Os resultados mostraram que a morfologia e propriedades mecânicas das blendas ternárias foram bastante diferentes e dependem da sequência de mistura. A blenda preparada pela mistura simultânea de todos os componentes, em uma única extrusão, apresentou melhor tenacidade. Por outro lado, quando o ABS e o SMA foram misturados juntos em uma primeira extrusão, antes da incorporação da PA6 em uma segunda extrusão, o valor da resistência ao impacto encontrado foi menor que o da matriz PA6 e da blenda sem compatibilizante PA6/ABS. Evidências de reações químicas entre o compatibilizante SMA e a matriz PA6 também foram investigadas através de reometria de torque. Resumo em inglês Blends of polyamide 6 (PA6) with acrylonitrile-butadiene-estyrene (ABS) were prepared in a twin-screw extruder, using the styrene-maleic anhydride (SMA) copolymer containing 7% of maleic anhydride as compatibilizer. The effects from three blending sequences on the microstructure and properties of the blends were investigated. The morphology and mechanical properties of the materials were characterized by transmission electron microscopy and tensile and impact tests. The r (mais) esults showed that the morphology and mechanical properties of ternary blends depend on the sequence of blend preparation. The blend prepared using the mixture of all components in a single-pass extrusion showed the more significant improvement in the material toughness. However, when the ABS and SMA were melt mixed together in a first extrusion step prior to incorporating PA6 in a second extrusion, the impact strength is lower than that of the blend without compatibilizer PA6/ABS and PA6 matrix. Evidence of chemical reactions between the compatibilizer SMA and PA6 was also obtained using a torque rheometer.

Scientific Electronic Library Online (Portuguese)

44

Stress cracking e ataque químico do PET em diferentes agentes químicos/ Stress cracking and chemical attack of pet under different chemicals

Teófilo, Edvânia T.; Melo, Rafaela N.; Silva, Suédina M. L.; Rabello, Marcelo S.
2009-01-01

Resumo em português A análise de resistência ao stress cracking (ESCR) do PET foi feita em corpos de prova de tração moldados por injeção, utilizando vários agentes químicos (metanol, etanol, propanol, butanol e soluções de hidróxido de sódio em diferentes concentrações). Foram realizados ensaios dinâmicos e estáticos de tração. Durante os testes os corpos de prova foram mantidos em contato com os agentes e as propriedades mecânicas monitoradas. Os resultados evidenciam qu (mais) e todas as soluções de hidróxidos de sódio testadas são agentes agressivos de ESC por diminuírem as propriedades mecânicas do polímero, ocasionando falha catastrófica. Já os demais fluidos, apesar de não terem efeito significativo nas propriedades do PET, afetam drasticamente sua aparência superficial. Observou-se também a ocorrência de ataque químico nos ensaios com NaOH, resultando em redução nas massas molares. Resumo em inglês The investigation of stress cracking resistance (ESCR) of PET was done in injection-moulded tensile test bars using different fluids as active agents. These were methanol, ethanol, propanol, butanol and solutions based on sodium hydroxide. Both dynamic and static tensile experiments were conducted. During the tensile experiments, the samples were kept in contact with the fluids and the mechanical properties were monitored. The results showed that all sodium hydroxide solu (mais) tions were aggressive stress cracking agents for PET, reducing mechanical properties and causing catastrophic failure. On the other hand, the other fluids did not cause much influence on the mechanical behaviour but changed drastically the surface appearance. Also observed was a chemical attack when NaOH solutions were used, causing a reduction in molar mass of PET molecules.

Scientific Electronic Library Online (Portuguese)

45

Compósitos biodegradáveis a base de polihidroxibutirato-hidroxivalerato (PHB-HV) reforçados com resíduos do beneficiamento do café/ Biodegradable polyhydroxybutyrate-hydroxyvalerate (PHB-HV) composites reinforced with residue of processing coffee

Machado, A.R.T.; Martins, P.F.Q.; Fonseca, E.M.B.; Reis, K.C.
2010-01-01

Resumo em português Compósitos de polihidroxibutirato - hidroxivalerato (PHB-HV) reforçados com resíduos da produção de café foram preparados a partir de PHB-HV com dois diferentes tipos de resíduos, o pergaminho e a casca de café, através da técnica de evaporação de solvente "casting". Para avaliar o efeito dos resíduos na matriz, os compósitos foram avaliados por difração de raios x (DRX), Microscopia eletrônica de Varredura (MEV) e através das propriedades mecânicas. Es (mais) tas técnicas forneceram fortes evidencias da formação de uma estrutura intercalada e homogênea entre os precursores, sem que isto alterasse a cristalinidade do PHB-HV. As propriedades mecânicas foram avaliadas quanto à força de punctura e deformação antes da ruptura indicando que a presença da carga orgânica eleva ambas as propriedades, gerando um novo material com um campo de aplicação ampliado em relação ao PHB-HV. Resumo em inglês Polyhydroxybutyrate-hydroxyvalerate (PHB-HV) coffee residue composites were prepared from PHB-HV and two different loadings of residue the husk and pill of coffee. The solvent evaporation technique "casting'' was used to form the films. To evaluate the residue effect in the PHB-HV properties and the material dispersion, the films were analyzed by X-ray diffraction (XRD), Scanning Electronic Microscopy (SEM) and from mechanical properties. These techniques provided strong (mais) evidence that the residue formed a homogeneous intercalated structure, although it did not altered the cristalinity of PHB-HV. The mechanical properties were evaluated by puncture force and deformation before the rupture, indicating that the presence of the organic charge elevates both properties. The composite obtained is a new material with a wider application field than the PHB-HV.

Scientific Electronic Library Online (Portuguese)

46

Colagem de barbotina de aluminas submicrométricas comerciais/ Slip casting of commercial aluminas with fine powder

Catafesta, J.; Andreola, R.; Perottoni, C. A.; Zorzi, J. E.
2007-03-01

Resumo em português O processo de moldagem de peças cerâmicas conhecido como colagem de barbotina é um processo antigo, mas que ainda é muito utilizado devido ao seu baixo custo, simplicidade e pelas excelentes propriedades mecânicas das peças sinterizadas. Boas propriedades mecânicas são obtidas quando o pó de partida tem tamanho de partícula submicrométrico. Neste trabalho foram moldadas peças cerâmicas por colagem de barbotina com três aluminas comerciais com partículas sub (mais) micrométricas e, após a sinterização, foram medidas algumas de suas propriedades, como dureza, densidade e resistência ao desgaste. As barbotinas não flocularam e foram obtidas peças de excelente qualidade, sendo que as peças moldadas com a alumina de menor tamanho de partícula apresentaram a melhor dureza, elevada densidade (chegando a 99% da densidade teórica) e o menor coeficiente de desgaste. Peças de alumina de alta qualidade podem ser usadas em inúmeras aplicações, desde a indústria têxtil até em aplicações biomédicas. Resumo em inglês The molding of ceramics parts by slip casting is an ancient process, but it is still very used because of low cost, simplicity and excellent mechanical properties of sintered parts. Better mechanical properties are obtained when the initial powder have small average particle size. In this work, ceramic parts were molded by slip casting of three commercial submicrometer-sized alumina powders. After sintering, some properties of these ceramic parts were measured, including (mais) hardness, density and wear coefficient. The slips do not flocullate, resulting in ceramic parts with excellent quality. Ceramic parts made with the alumina powder of smaller particle size exhibited high hardness, high density (99% TD) and lower wear coefficient. High quality alumina parts such as that produced in this work can be used in many applications, from textile industry to biological applications.

Scientific Electronic Library Online (Portuguese)

47

Estudo da viabilidade de utilização de fibras naturais curtas em matrizes de resina epóxi/ Properties of natural amorphous silica fibers as epoxy resin reinforcement

Martins, R.R.; Pires, A.T.N.; Al-Qureshi, H.A.; Barra, G.M.O.
2008-01-01

Resumo em português Fibras curtas de origem mineral, constituídas, predominantemente, de sílica amorfa, foram caracterizadas e avaliadas quanto a sua viabilidade de utilização como agente de reforço em matrizes de resina epóxi. As fibras naturais de sílica amorfa, denotadas por FNSA, foram incorporadas em matrizes de resina epóxi e as propriedades mecânicas avaliadas através de ensaios de tração. Foi estudada a influência do tratamento superficial da FNSA com agente aminossilano (mais) (AS), nas propriedades micro e macroscópicas dos compósitos, e comparado o comportamento mecânico dos compósitos obtidos com fibras naturais de sílica amorfa e fibras de vidro moídas (FV) comerciais. Os resultados sugerem que as fibras de sílica amorfa podem substituir fibras de vidro moídas, as quais vêm sendo utilizadas como agente de reforço em matriz de resina epóxi, uma vez que as propriedades mecânicas dos compósitos foram comparáveis ou superiores aos compósitos reforçados com fibras de vidro moídas. Resumo em inglês A novel kind of short natural fiber obtained from mineral resources, which consists mainly of pure amorphous SiO2, was characterized and applied as a reinforcing agent in epoxy resin. Natural amorphous silica fibers (NASF) were incorporated in epoxy resin and the obtained composites were mechanically tested. The effect of the treatment of NASF chemically modified with aminosilane as well as the aspect ratio of the fibers on the mechanical properties of the composite were (mais) evaluated and compared with properties obtained with FNSA without treatment. The results obtained show that these natural fibers are potential candidates for the substitution of short glass fibers as a reinforcement phase in polymer composites, since the mechanical properties obtained were in all cases similar or superior to the ones obtained with commercial short glass fibers.

Scientific Electronic Library Online (Portuguese)

48

Influência do tratamento térmico no comportamento mecânico não-linear elástico da liga Ti-13Nb-13Zr/ Influence of heat treatment on non-elastic mechanical behavior of Ti-13Nb-13Zr alloy

Schneider, S.; Schneider, S.G.; Silva, H.M. da
2007-01-01

Resumo em português A liga Ti-13Nb-13Zr foi produzida por fusão a arco, solubilizada a 1000ºC/1h resfriada em água, forjada a frio, e recozida nas seguintes condições: 1000ºC/1h e 900ºC/30min resfriada em água. As propriedades mecânicas da liga recozida foram avaliadas pelo ensaio de tração em temperatura ambiente. A região elástica foi analisada de acordo com a equação modificada de Ramberg-Osgood, cujo grau de não-linearidade está associado ao parâmetro n. Verificou-se qu (mais) e um tratamento posterior de envelhecimento a 400ºC/3h diminui as diferenças existentes em algumas propriedades mecânicas e melhora a linearidade na região elástica. Resumo em inglês Ti-13Nb-13Zr alloy was produced by arc melting, solution treated at 1000°C/1h followed by water quenching, cold forged and annealed at 1000°C/1h or 900°C/30min followed by water quenching. Mechanical properties of this alloy were evaluated by tension tests at room temperature. The elastic region of the stress-strain curve was analyses according to the modified equation of Ramberg-Osgood, which degree of non-linearity is associated to parameter n. It was observed that a (mais) ging treatment at 400°C/3h, after the annealing, decreases the differences between mechanical properties; moreover, the linearity of elastic region improves.

Scientific Electronic Library Online (Portuguese)

49

Poliuretana derivada de óleos vegetais exposta ao intemperismo artificial/ Polyurethane derived from vegetal oil exposed to artificial weathering

Almeida, Alessandra E. F. S.; Ferreira, Osny P.
2006-01-01

Resumo em português Foram obtidas as propriedades mecânicas e viscoelásticas da poliuretana derivada do óleo de mamona após sua exposição ao intemperismo artificial, a fim de avaliar a aplicabilidade deste material como revestimento polimérico para substratos de concreto na Construção Civil. Os procedimentos experimentais foram realizados em conformidade com a ASTM G 53 for "Operating Light and Water Exposure Apparatus (Fluorescent UV - Condensation Type) for Exposure of Nonmetallic (mais) Materials"[1]. O ensaio para a caracterização mecânica dos corpos-de-prova após exposição ao intemperismo artificial foi realizado conforme a norma ASTM D 638M-96 "Standard Test Method for Tensile Properties of Plastics (Metric)"[2]. Foi empregado o método de análise dinâmico-mecânica para a obtenção das propriedades viscoelásticas da poliuretana vegetal. Os resultados mostraram que a exposição ao intemperismo artificial não ocasionou mudanças significativas nas propriedades do revestimento polimérico para o tempo de exposição estudado. Resumo em inglês The mechanical and viscoelastic properties of polyurethane derived from castor oil were obtained after being exposed to artificial weathering with the purpose of evaluating their applicability as polymeric coatings on concrete substrate for Civil Construction. The procedures followed the ASTM G53 for "Operating Light and Water Exposure Apparatus (Fluorescent UV - Condensation Type) for Exposure of Nonmetallic Materials"[1]. Mechanical properties were obtained by means of (mais) the ASTM D 638M-96 "Standard Test Method for Tensile Properties of Plastics (Metric)"[2]. Furthermore, a Dynamic Mechanical Analysis (DMA) was carried out in order to study the viscoelastic properties of polyurethane. The results showed that the properties were altered slightly considering the time studied.

Scientific Electronic Library Online (Portuguese)

50

Caracterização físico-mecânica de filmes de borracha natural epoxidada curáveis em temperatura ambiente/ Physical-mechanical characterization of epoxidized natural rubber films curable at ambient temperature

Jorge, Rosane M.; Ferreira, Marcos T.; Picciani, Paulo H. S.; Gomes, Ailton S.; Nunes, Regina C. R.
2009-01-01

Resumo em português Neste trabalho é apresentado o estudo da formação de reticulações na temperatura ambiente, de borracha natural epoxidada (ENR) de 25% de grau de epoxidação, com um agente de cura contendo o tiol trimetilolpropano tris(2-mercaptoacetato) (TMP-SH). As composições foram realizadas a partir de solubilização da ENR e, posterior reação com o TMP-SH. Foram preparadas composições com 5, 10 e 20 phr de ENR e controles contendo NR e ENR. Também foi preparada uma com (mais) posição com NR e 10 phr de TMP-SH para comprovar o efeito do grupo epóxido. A formação de reticulação dos filmes foi determinada pelas propriedades físico-mecânicas como grau de inchamento no equilíbrio, resistência à tração e propriedades dinâmico-mecânicas. Os resultados mostraram a eficiência do agente de cura e a influência do teor incorporado de TMP-SH nas propriedades determinadas, e a composição de ENR com 10 phr do agente de cura foi a que apresentou melhor desempenho físico-mecânico. Resumo em inglês This paper presents the crosslinking study at room temperature of epoxidised natural rubber (ENR), of 25% of epoxidation level, with a curing agent containing thiol trimethylolpropane tris(2-mercaptoacetate) (TMP-SH). The compositions were made from solubilization of ENR, and subsequent reaction with TMP-SH. Compositions with 5, 10 and 20 phr of TMP-SH, NR and ENR controls were prepared. It was also prepared a composition with NR and 10 phr of TMP-SH to demonstrate the ef (mais) fect of epoxide group. The crosslinking formation of the films was determined by physical-mechanical properties as equilibrium swelling index, tensile strength and dynamic-mechanical properties. The results showed the efficiency of the cure agent and the influence of TMP-SH content incorporated, in the studied properties, and the ENR composition with 10 phr of curing agent presented the best physical-mechanical performance.

Scientific Electronic Library Online (Portuguese)

51

Efeito da acetilação das partículas de madeira de Eucalyptus grandis e da inclusão de partículas de polietileno e de embalagens cartonadas nas propriedades de chapas de aglomerado/ Effect of particle acetylation of Eucalyptus grandis wood and the inclusion of particles of polyethylene and cardboard packaging of properties in crowded plates

Oliveira, Fernando Vitor; Vital, Benedito Rocha; Silva, José de Castro; Carneiro, Angelica de Cassia Oliveira; Pimenta, Alexandre Santos
2010-10-01

Resumo em português O objetivo deste trabalho foi avaliar o efeito da acetilação das partículas de madeira de Eucalyptus grandis e da inclusão de partículas de polietileno de baixa densidade (PEBD) e de alta densidade (PEAD) e de embalagens cartonadas nas propriedades de chapas de aglomerado. As partículas de madeira foram produzidas em laboratório a partir de toras que foram desdobradas em tábuas, convertidas em baguetas, depois em flocos e, finalmente, transformadas em partículas. (mais) Embalagens cartonadas e de polietino de alta e baixa densidades foram coletadas em depósitos de material reciclável e processadas em moinho de martelo. A acetilação foi realizada em autoclave com controle de pressão e temperatura. A acetilação promoveu significativa estabilização dimensional dos painéis, entretanto diminuiu algumas propriedades mecânicas. A adição de polietileno reduziu as propriedades mecânicas, em especial a flexão estática (MOR e MOE), porém, de modo geral, melhorou a estabilidade dimensional dos painéis, independentemente do tipo de partícula. No entanto, a adição de embalagens cartonadas reduziu a resistência mecânica e promoveu maior adsorção de vapor de água, inchamento em espessura e expansão linear, tanto nas chapas contendo partículas acetiladas quanto naquelas que não as continham. Resumo em inglês The objective of this study was to evaluate the effect of eucalyptus grandis particles acetylation and the addition of polyethylene of low (pebd) and high density (pead) and paperboard particles in the properties particleboard. Wood particles were produced in laboratory from logs that were split into plaks, baguettes and then converted into flakes and finally transformed into particles. Paperboard and polyethylene collected in recyclable material stores and processed in a (mais) hammer mil. Acetylation was performed in autoclave with pressure and temperature control. Wood particles acetylation promoted a significant stabilization of the particleboards but decrease some mechanical properties. The addition of paperboard reduced all the mechanical properties and promoted a greater adsorption of water vapor, thickness swelling and linear expansion, for boards containing acetylated or non acetylated wood particles. The addition of polyethylene reduced the mechanical properties, specially the static bending (mor and moe), however resulted in more stable boards.

Scientific Electronic Library Online (Portuguese)

52

Estimativa da susceptibilidade à compactação e do suporte de carga do solo com base em propriedades físicas de solos do Rio Grande do Sul/ Estimating soil susceptibility to compaction and load support capacity based on physical parameters of soils from Rio Grande do Sul State

Suzuki, Luis Eduardo Akiyoshi Sanches; Reinert, Dalvan José; Reichert, José Miguel; Lima, Cláudia Liane Rodrigues de
2008-06-01

Resumo em português O conhecimento das relações entre propriedades físicas e mecânicas do solo pode contribuir no desenvolvimento de funções de pedotransferência, que permitam estimar outras propriedades do solo de difícil mensuração. Neste trabalho, objetivou-se avaliar a relação entre a susceptibilidade à compactação e o suporte de carga com propriedades físicas de solos do sul do Brasil. Foram avaliadas a resistência à penetração, a umidade, a densidade e a compressibi (mais) lidade de seis solos. A resistência à penetração pode ser estimada pelo modelo que considera a umidade e densidade do solo. Solos com maior densidade inicial apresentaram menor susceptibilidade à compactação e menor deformação, quando submetidos a pressões externas. Quanto maior a resistência do solo à penetração, menor é a deformação e maior é a capacidade de suporte de carga, embora isso não indique solos com qualidade física adequada para as culturas; quanto maior a deformação do solo, maior a susceptibilidade à compactação e menor a capacidade de suporte de carga. A susceptibilidade de um solo à compactação e sua capacidade de suporte de carga podem ser estimadas, respectivamente, pela densidade inicial e pela resistência do solo à penetração. Resumo em inglês Quantifying the relationship between physical and mechanical soil properties can contribute to the development of pedotransfer functions that allow estimating hard-to-measure soil properties. The objective of this study was to evaluate the interrelations between susceptibility to compaction and load support with some physical properties of soils from Southern Brazil. Penetration resistance, moisture, bulk density and compressibility of six soils were evaluated. In a model (mais) including soil moisture and bulk density as independent variables, the relation with penetration resistance values obtained in the field was high. Soils with higher initial bulk density were less susceptible to compaction and exhibited less deformation under external loads. With increasing soil penetration resistance, less deformation and greater load support were observed, which does not necessarily indicate a satisfactory soil physical quality for crop cultivation. The greater the soil deformation, the higher is the susceptibility to compaction and the lower is its load support. The compaction susceptibility and load support of a soil can be estimated, respectively, by its initial bulk density and resistance to penetration.

Scientific Electronic Library Online (Portuguese)

53

Fios ortodônticos: conhecer para otimizar a aplicação clínica/ Orthodontic wires: knowledge to optimize clinical application

Quintão, Cátia Cardoso Abdo; Brunharo, Ione Helena Vieira Portella
2009-12-01

Resumo em português A grande variedade de fios ortodônticos presente no mercado pode gerar dúvidas quanto à melhor escolha para situações clínicas. Assim, o conhecimento das propriedades mecânicas dos mesmos facilita a escolha para aplicação do movimento ortodôntico na dependência da fase em que o tratamento se encontra. A evolução da tecnologia de manufatura dos fios e a elaboração de novas técnicas ortodônticas geraram a busca por uma melhor qualidade das ligas, a fim de t (mais) orná-los biologicamente mais efetivos no que diz respeito aos dentes e tecidos de suporte. O presente artigo resume as principais características dos fios utilizados em Ortodontia, em relação ao histórico, propriedades mecânicas e aplicação clínica, de acordo com fases específicas de tratamento. Resumo em inglês The huge variety of orthodontic wires brands available in market might generate confusion as regard to the best choice for clinical application. Therefore mechanical properties knowledge about wires would help the professional to apply the best orthodontic technique depending on the treatment phase. The wires manufacturing evolution and the new orthodontic techniques proposed guided the market into the search for better quality alloys, in order to make them biologically m (mais) ore effective to teeth and support tissues. This paper aims to summarize some main characteristics of orthodontic wires related to their history, mechanical properties and clinical application as regard to individual phase of treatment.

Scientific Electronic Library Online (Portuguese)

54

Avaliação dos efeitos da acetilação nas propriedades das fibras de caroá/ Evaluation of the effects of acetylation surface treatments on ‘caroá’ fiber

Lopes, Fernanda F. M.; Araújo, Gilmar T. de; Nascimento, José W. B. do; Vasconcelos, Robelsa F.; Dantas, Júlio M. E.
2011-01-01

Resumo em português As fibras de vegetais são altamente higroscópicas, característica que se apresenta como um dos principais problemas em sua aplicabilidade na produção de fibrocimentos, induzindo a variações dimensionais sob a influência da umidade, deposição dos produtos da matriz em seus poros e a degradação. Visando encontrar alternativas para minimizar os impasses gerados nos compósitos cimentíceos com relação às fibras de caroá objetivou-se, neste trabalho, avaliar a (mais) aplicação do tratamento de acetilação em diferentes níveis. Sua eficiência foi determinada considerando-se a redução da hidrofilicidade, a manutenção do desempenho mecânico das fibras e as modificações na composição química, avaliadas por meio de ensaios de determinação das propriedades físicas, químicas, mecânicas e térmicas. Os tratamentos de acetilação conduzidos a 120 °C e/ou por 3 h, apresentaram reduções de 42 a 47% na hidrofilicidade. Na acetilação a 120 °C, durante 1 h o incremento nas propriedades mecânicas foi superior a 110%. O tratamento também promoveu modificações na composição das fibras com a implantação de grupos acetil, aumentou a estabilidade térmica e reduziu consideravelmente a cristalinidade da celulose, sem gerar degradações que comprometessem sua superfície de adesão. Resumo em inglês Fiber plants are highly hygroscopic and this feature appears as a major problem in its applicability to production of cement composites, inducing dimensional changes under the moisture influence, deposition of the matrix products and degradation. To find alternatives to minimize the problems in cementitious composites with respect to Neoglaziovia variegata fibers, it was aimed in this study to evaluate the application of the treatment of acetylation at different levels. T (mais) heir efficiency was determined by reduction of hydrophilicity, maintaining the mechanical performance of fibers, and changes in chemical composition, measured through the physical, chemical, mechanical and thermal properties. The acetylation at 120 °C and/or 3 h showed reductions of 42 to 47% in hydrophilicity. In the acetylation at 120 °C for 1 h, the increase in mechanical properties was more than 110%. The treatment also changed the composition of the fibers with the introduction of acetyl groups, increased the thermal stability and reduced the crystallinity of cellulose, without degradation in its surface of adhesion.

Scientific Electronic Library Online (Portuguese)

55

Caracterização química e estrutural de fibra de sisal da variedade Agave sisalana/ Chemical and structural characterization of sisal fibers from Agave sisalana variety

Martin, Adriana R.; Martins, Maria A.; Mattoso, Luiz H. C.; Silva, Odilon R. R. F.
2009-01-01

Resumo em português Nos últimos anos, o interesse pelo uso de fibras naturais em materiais compósitos poliméricos tem aumentado significativamente. Neste trabalho foram investigadas as propriedades, químicas, físicas, térmicas e estruturais da fibra de sisal brasileira da variedade Agave sisalana. Nosso objetivo foi avaliar a qualidade e o desempenho desta fibra para aplicações industriais. Foram realizados ensaios de resistência à tração, análise da composição química, difra (mais) ção de raios X, e estudos por microscopia eletrônica de varredura (MEV) ao longo do comprimento da fibra. A fibra de sisal brasileira apresentou propriedades mecânicas e térmicas dentro da faixa relatada na literatura, mostrando-se adequada para ser utilizada em materiais compósitos poliméricos. Resumo em inglês In recent years, the interest in the use of natural fibers in polymeric composite materials has increased significantly. In this work were investigated the structural, thermal, chemical, and physical properties of Brazilian sisal fiber from Agave sisalana variety. Our aim was to evaluate the quality and the performance of this fiber for industrial applications. Mechanical properties, chemical composition, X ray diffraction, and scanning electron microscopy (SEM) have been (mais) investigated with fibers along their length. The Brazilian sisal fibers studied have exhibited mechanical and thermal properties within the range reported in the literature and were suitable for use in polymeric composites.

Scientific Electronic Library Online (Portuguese)

56

Caracterização mecânica de polipropileno reciclado para a indústria automotiva/ Mechanical characterization of recycled polypropylene for automotive industry

Fernandes, Beatriz L.; Domingues, Antonio J.
2007-06-01

Resumo em português A indústria automotiva responde, atualmente, por uma grande parte do mercado de consumo de plásticos, por isso existe um crescente interesse no investimento em processos de reciclagem, inclusive devido à vinculação às atividades relacionadas à proteção ambiental. Dentre as peças automotivas, os pára-choques são relativamente fáceis de serem reciclados devido às suas dimensões e por constituírem, geralmente, de um único material, o polipropileno (PP). Nest (mais) e trabalho, analisaram-se as propriedades mecânicas de misturas de PP virgem e reciclado, em três porcentagens diferentes, a fim de detectar as alterações das mesmas, relacionando-as à qualidade do produto. Concluiu-se que porcentagens de reciclado acima de 30% causam deterioração das propriedades mecânicas do produto. Este estudo visa a fornecer uma contribuição para o aumento na utilização de plásticos reciclados na indústria automotiva. Resumo em inglês The automotive industry is now responsible for a large share of plastic consumption, which prompted increasing investments in recycling processes, also due to the need of ambient protection. Among the automotives parts, bumpers are relatively easy to be recycled due to their dimensions and because they are made of a single material, polypropylene (PP). In this work, the mechanical properties of mixtures of virgin and recycled PP, in three different percentages, were analy (mais) zed in order to detect alterations and associate them with the product quality. It was concluded that percentages of recycled material above 30% deteriorate the mechanical properties of the product. This study aims to provide a contribution to the increase in the recycled plastic use in the automotive industry.

Scientific Electronic Library Online (Portuguese)

57

Recuperação mecânica muscular com laser/ Muscular mechanical recovery with laser

Sene, Giovana Leitão; Shimano, Antônio Carlos; Picado, Celso Hermínio Ferraz
2009-01-01

Resumo em português OBJETIVO: Avaliamos a influência da irradiação a laser, associada ou não a imobilização, nas propriedades mecânicas do músculo gastrocnêmio submetido à lesão experimental. MÉTODOS: Foram utilizadas 70 ratas (Wistar), divididas em 7 grupos: grupo 1- controle; grupo2 - lesão; grupo3 - lesão-irradiação laser; grupo 4 - lesão-imobilização 24 horas-irradiação laser; grupo 5 - lesão- imobilização 72 horas-irradiação laser; grupo 6 - lesão-imobilizaç� (mais) �o 24 horas; grupo 7 - lesão-imobilização 72 horas. Os músculos foram submetidos a ensaios mecânicos de tração e, utilizando gráficos carga x alongamento calculadas as propriedades mecânicas no limite de proporcionalidade e no limite máximo. RESULTADOS: A lesão provocou diminuição da carga nos limites máximo e de proporcionalidade em relação ao grupo1 (p Resumo em inglês OBJECTIVE: We evaluated the influence of low-power laser irradiation, either associated or not with immobilization, on the mechanical properties of the gastrocnemius muscle submitted to experimental injury with an impact mechanism. METHODS: Seventy female Wistar rats were divided into 7 experimental groups: group 1 - control; group 2 - injury; group 3 - injury-laser irradiation; group 4 - injury-immobilization for 24-hour laser irradiation; group 5 - injury-immobilization (mais) for 72-hour laser irradiation; group 6 - injury-immobilization for 24 hours; group 7 - injury-immobilization for 72 hours. The IBRAMED® Laserpulse equipment (670 nm) was used for biostimulation. The muscles were submitted to mechanical assays in an EMIC® universal testing machine and load x stretching graphs were used to calculate the mechanical properties, i.e., at the proportionality limit and maximum limit. RESULTS: The injury provoked a reduction of load at the proportionality limit and at the maximum limit compared to group 1 (p

Scientific Electronic Library Online (Portuguese)

58

Incorporação de cinza de lenha, lodo de estação de tratamento de água e cinza de casca de arroz em massa cerâmica: utilização da técnica de planejamento/ Grog incorporation in ceramic mass to manufacture of bricks: a study of the physical-mechanical properties

Medeiros, E. N. M de; Sposto, R. M.; Neves, G. de A.; Menezes, R. R.
2010-12-01

Resumo em português Este trabalho apresenta um estudo das propriedades físico-mecânicas de massas cerâmicas com a incorporação de resíduos de cinza de lenha, lodo de estação de tratamento de água e cinza de casca de arroz, visando a sua futura utilização na produção de blocos. Os procedimentos metodológicos consistiram na caracterização química e mineralógica, na análise granulométrica e no delineamento de misturas com argila e resíduos por meio da técnica de planejamen (mais) to. Foram produzidos corpos de prova por prensagem, com variações de composições no intervalo de 0 a 50% de resíduo e 50 a 100% de argila. A queima foi realizada em forno tipo mufla. As propriedades físico-mecânicas avaliadas foram absorção de água e módulo de ruptura à flexão. Como resultados principais, concluiu-se sobre a viabilidade em se utilizar composições com até 25% de resíduo nas temperaturas de 800, 900 e 1000 ºC. Resumo em inglês This paper presents a study of the physical and mechanical properties of ceramic mass with the incorporation of waste ash wood, sludge from water treatment and rice husk ash to determine whether its future use manufacture of bricks. The procedures consisted in the chemical and mineralogical characterization, particle size analysis and design of mixtures with clay and waste through planning technique. Bodies were produced by uniaxial pressing, with variations of compositio (mais) ns in the range of 0 to 50% waste and 50 to 100% clay. The burning was carried out in muffle furnace. The physical and mechanical properties evaluated were water absorption and modulus of rupture strength. The main result, it was concluded on the feasibility of using compositions with up to 25% of waste at temperatures of 800, 900 and 1000ºC.

Scientific Electronic Library Online (Portuguese)

59

Desenvolvimento de um compósito laminado híbrido com fibras natural e sintética/ Development of a hybrid composite with synthetic and natural fibers

Da Silva, R.V.; Aquino, E.M.F.; Rodrigues, L.P.S.; Barros, A.R.F.
2008-03-01

Resumo em português Compósitos poliméricos com fibras naturais vêm sendo bastante estudados nas duas últimas décadas com algumas aplicações já bem estabelecidas, principalmente no setor automotivo. No entanto, suas aplicações são limitadas pelo seu baixo desempenho mecânico e alta absorção de umidade, comparado aos compósitos com fibras sintéticas. Buscando minimizar estes problemas e ampliar o leque de aplicações, propõe-se neste trabalho desenvolver um compósito laminad (mais) o híbrido associando fibras naturais (curauá) e sintéticas (vidro-E) em uma matriz de resina poliéster. Foi realizado um estudo comparativo das propriedades mecânicas em flexão do laminado híbrido e de dois outros laminados, um apenas com fibras de vidro e um apenas com fibras de curauá. Ensaios de absorção de água foram também realizados sendo obtidas as curvas de saturação para os três laminados. Por fim, foi analisada a influência da absorção de água nas propriedades mecânicas em flexão do laminado híbrido. As propriedades do laminado híbrido foram muito próximas do laminado de fibra de vidro, já o laminado de curauá teve um desempenho bastante inferior. Nos ensaios de absorção de água foi comprovada a eficiência da hibridização na redução do percentual de absorção de água do laminado apenas com fibra natural. O laminado híbrido vidro/curaua mostrou ser um promissor substituto para os laminados de fibra de vidro mesmo em aplicações de contato direto com água. Resumo em inglês Natural fibre composites are being quite studied in the last two decades with some applications consolidated mainly in the automobile industry. However, the applications are limited due to its poor mechanical properties and high moisture absorption, compared to composites with synthetic fibres. Looking for to minimize these problems and to enlarge the possible applications, the objective of this work is to develop a hybrid composite combining natural (curaua) and syntheti (mais) c fibres (glass-E) in a polyester matrix. A comparative study of the flexural mechanical properties among the hybrid composite and two others, one just with fibreglass and other just with curaua fibres, was accomplished. Besides, water absorption tests were carried out for all composites and it was analyzed the water absorption influence in the mechanical properties of the hybrid composite. The mechanical properties of the hybrid and fibreglass composites were very close, on the other hand the composite just with natural fibre showed a quite inferior performance. The hybridization was efficient in the sense of reducing the water absorption of the natural fibre composite (curaua). The hybrid glass/curauá composite showed to be a promising substitute for fibreglass composites even in applications of contact with water.

Scientific Electronic Library Online (Portuguese)

60

Parâmetros dendrométricos e correlações com propriedades tecnológicas em um híbrido clonal de Eucalyptus urophylla x Eucalyptus grandis/ Dendrometric parameters and correlations with technological properties in a clonal hybrid of Eucalyptus urophylla x Eucalyptus grandis

Gonçalves, Fabricio Gomes; Oliveira, José Tarcísio da Silva; Silva, Gilson Fernandes da; Nappo, Mauro Eloi; Tomazelo Filho, Mario
2010-10-01

Resumo em português A qualidade da madeira aparentemente está associada às características dendrométricas, que por sua vez são influenciadas pelas condições de crescimento. Os objetivos deste estudo foram a caracterização dendrométrica e a realização de correlações de Pearson entre alguns parâmetros tecnológicos da madeira do híbrido clonal de Eucalyptus urophylla x Eucalyptus grandis sob três estratos silviculturais. Os dados dendrométricos foram analisados mediante a an� (mais) �lise de regressão. Os resultados mostraram que o híbrido apresenta comportamento similar ao das demais madeiras da mesma espécie que cresceram em outras regiões, destacando-se a espessura do alburno no E1 (talhadia simples, 70 meses e com um desbaste), com pouca variação ao longo do fuste. Todas as árvores apresentaram, em geral, baixa conicidade ao longo do fuste e baixo volume de casca entre os estratos. Na correlação de Pearson foram avaliados entre si nove parâmetros dendrométricos, sete físicos e três mecânicos, longitudinalmente em seções de 3 m e na posição medula-casca nas duas primeiras toras. Os coeficientes encontrados demonstram haver fortes correlações entre as propriedades, destacando-se a densidade básica em relação às demais características e o coeficiente de anisotropia, ambas importantes no processo de desdobro e secagem da madeira. Não houve correlações significativas nas contrações lineares e volumétricas ao longo do comprimento do fuste. A variação radial mostrou boas correlações entre todas as propriedades mecânicas avaliadas nas duas primeiras toras. Em contrapartida, as propriedades físicas avaliadas na posição radial não apresentaram correlações significativas. Resumo em inglês Wood quality is apparently associated with the dendrometric characteristics that are influenced by growth conditions. The aim of this study was the dendrometric characterization and realization of Pearson Correlations among some technological parameters in the clonal hybrid wood Eucalyptus urophylla x Eucalyptus grandis grown in three silvicultural extracts. The dendrometric data were analyzed by regression analysis. The results show that the hybrid presents similar behav (mais) ior to other eucalypt of the same species grown in other places with sapwood thickness in E1 (coppice with 70 months and one thinning), with little variation along the stem. All evaluated trees presented, in general, a low taper along the stem with very little bark volume among the extracts. The Pearson Correlation studied nine dendrometric parameters, seven physical and three mechanical properties. The parameters were evaluated, longitudinally, in three meter sections along the stem and in the pith-bark position in the first two logs according to the Pearson's Correlation. The coefficients demonstrated a strong correlation among the properties, with basic density being highly correlated to the other characteristics and anisotropic coefficient, important in the process of sawing and drying wood, as well as sapwood thickness. The correlation to the height relationship wasn't significant to the linear and volumetric shrinkage. Radial variation showed a good correlation among all the evaluated mechanical properties in the two first logs. On the other hand, the physical properties in the radial position didn't present significant correlations with tangential shrinkage.

Scientific Electronic Library Online (Portuguese)

61

Utilização de Algoritmos de Processamento e Análise de Imagem na Avaliação do Dano em Placas Compósitas

Durão, L. M. P.; Magalhães, A. G.; Marques, A. T.; Tavares, João Manuel R. S.
2008-06-01

Resumo em português A utilização de materiais compósitos tem vindo a aumentar nas últimas décadas em virtude das suas notáveis propriedades mecânicas. Referem-se como vantagens no seu uso o baixo peso, elevada resistência e rigidez. A furação de placas compósitas é um desafio que se coloca às indústrias que trabalham com este tipo de materiais, sendo frequente o recurso a ferramentas convencionais com adaptações. Contudo, a presença de defeitos devidos a operações de maqui (mais) nagem pode afectar severamente as propriedades mecânicas das peças maquinadas, nomeadamente em zonas de ligação. Neste trabalho, apresenta-se uma técnica baseada no uso de algoritmos de Processamento e de Análise de Imagem que permite a avaliação de defeitos causados pela maquinagem de placas compósitas e que pode ser utilizada no estudo e definição de estratégias de maquinagem tendentes à minimização do dano envolvido. As conclusões obtidas mostram que tal redução do dano permite um aumento da resistência mecânica das peças e a aplicação de algoritmos de Processamento e Análise de Imagem revela-se adequada. Resumo em inglês The use of fiber reinforced plastics has increased in the last decades due to their unique properties. Advantages of their use are related with low weight, high strength and stiffness. Drilling of composite plates is a challenge to the industries related with these materials. Normally, machining can be carried out in conventional machinery with some adaptations. However, the presence of typical defects like delamination can severely affect mechanical properties of produce (mais) d parts. In this paper, a technique for delamination measurement based on algorithms of Image Processing and Analysis is presented. This technique can be helpful in the evaluation of damage for the comparison of drilling parameters or tools. Conclusions show that damage minimization is an important mean to improve mechanical properties of joint areas of plates and the appropriateness of the algorithms of Image Processing and Analysis used.

Scientific Electronic Library Online (Portuguese)

62

Obtenção de compósitos de resíduos de ardósia e polipropileno/ Composites obtained by the combination of slate powder and polypropylene

Carvalho, Giovanna M. X. de; Mansur, Herman S.; Vasconcelos, Wander L.; Oréfice, Rodrigo L.
2007-06-01

Resumo em português O uso de ardósia em construções tem frequentemente resultado na produção de uma grande quantidade de resíduos particulados que tem pequeno valor mercadológico e grande potencial de danificação do meio ambiente. Neste trabalho, partículas de ardósia foram testadas como agente de reforço em polipropileno. Polipropileno e partículas de ardósia foram misturados em um misturador em diferentes frações. Anidrido maleico foi também usado durante a mistura para in (mais) duzir modificações no polipropileno que levassem a um aumento na interação entre os componentes. As amostras foram caracterizadas por espectroscopia no infravermelho (FTIR) e microscopia eletrônica de varredura. Materiais contendo 5 e 10% de ardósia produziram amostras com características ópticas semelhantes à rocha original. As análises por FTIR e microscopia eletrônica de varredura sugeriram que as modificações químicas no polipropileno levaram a uma melhoria parcial das interações interfaciais entre as partículas de ardósia e o polímero. Propriedades mecânicas, avaliadas por meio de ensaios de resistência à tração, mostraram que a adição das partículas de ardósia não alterou significativamente a resistência mecânica do polipropileno. Assim sendo, a incorporação de partículas de ardósia em polipropileno surge como uma tecnologia potencial para a produção de sistemas com algumas propriedades mecânicas comparáveis ao polipropileno puro, baixo custo, propriedades ópticas próximas às da ardósia e habilidade de minimizar problemas ambientais decorrentes da presença de resíduos derivados de atividades industriais. Resumo em inglês The use of slate rock in constructions often results in the production of large amount of residual powder that has very low economical value and can also damage the environment. In this work, slate powder was tested as a reinforcing agent for polypropylene. Polypropylene and slate powder were mixed in different ratios in a mixer. Maleic anhydride was also used during the mixing to induce chemical modification of polypropylene in order to improve interactions between the p (mais) olymer and the inorganic powder. Samples were characterized by infrared spectroscopy and scanning electron microscopy. Samples obtained by adding 5 and 10 wt. % of slate powder in polypropylene had optical properties close to those of commercial slate. FTIR and electron microscopy results suggested that chemical modification of polypropylene led to a partial improvement on the interfacial interactions between slate powder and the polymer. Mechanical properties evaluated by using tensile tests showed that the slate powder did not affect substantially the mechanical strength of polypropylene. Therefore, the incorporation of slate powder in polypropylene emerges as a potential technology for production of systems with some mechanical properties comparable to pure polypropylene, low cost, optical properties close to pure slate and ability to minimize environment problems caused by the presence of residual powder derived from industrial activities.

Scientific Electronic Library Online (Portuguese)

63

Análise biomecânica dos efeitos da crioterapia no tratamento da lesão muscular aguda/ Biomechanical analysis of the cryotherapy effects in the treatment of acute muscular injury

Matheus, João Paulo Chieregato; Milani, Juliana Goulart Prata Oliveira; Gomide, Liana Barbaresco; Volpon, José Batista; Shimano, Antônio Carlos
2008-08-01

Resumo em português A crioterapia é amplamente utilizada por atletas profissionais e amadores no tratamento agudo de lesões musculares. Este trabalho teve como objetivo analisar as propriedades mecânicas do músculo gastrocnêmio lesionado por impacto direto e tratado com crioterapia. Para tanto, foram utilizadas 24 ratas Wistar, divididas em três grupos experimentais: grupo controle (C): animais mantidos em gaiolas-padrão por seis dias; grupo lesionado (L): animais submetidos à lesão (mais) por mecanismo de impacto no gastrocnêmio, sem tratamento e mantidos em gaiolas-padrão por seis dias; grupo lesionado e tratado com crioterapia (LC): animais submetidos à lesão, tratados com uma sessão de crioterapia, imediatamente após a lesão e mantidos em gaiolas-padrão por seis dias. Após essas etapas, os animais foram submetidos à eutanásia para que fossem realizados os ensaios mecânicos de tração dos músculos gastrocnêmios direitos, na máquina universal de ensaios (EMIC®). A partir dos gráficos carga versus alongamento de cada ensaio, foram calculadas as seguintes propriedades mecânicas: carga no limite máximo (CLM), alongamento no limite máximo (ALM) e rigidez (R). No ALM, o grupo C apresentou diferença estatística (p Resumo em inglês Cryotherapy is widespread used in the acute treatment of muscle injuries of professional and unprofessional athletes. The purpose of this study was the investigation of mechanical properties of gastrocnemius muscle submitted to a impact mechanism of injury and treated with cryoterapy. Therefore, twenty four female Wistar rats were divided into three groups: Control (C): animals housed in standard cages for six days; Lesion (L): animals submitted to a direct impact mechani (mais) sm of injury in the gastrocnemius muscle, without any treatment and kept into standard cages during six days; Lesion e cryotherapy (LC): animals submitted to the contusion, treated with a single session of cryotherapy immediately after lesion and housed in standard cages during six days. After those protocols, the rats were killed and their right gastrocnemius muscle were dissected and submitted to a mechanical test of traction in a universal assays machine (EMIC®). From the load versus elongation curves, the following mechanical properties were obtained: Maximum limit load (MLL), maximum limit elongation (MLE) and stiffness (St). There was a statistically difference between all groups in MLL and St. However, in the MLE there was statistically difference only between groups C and L (p

Scientific Electronic Library Online (Portuguese)

64

Influência da adição de amido de mandioca na biodegradação da blenda polimérica PHBV/Ecoflex®/ Influence of cassava starch incorporation on the biodegradability of the polymeric blend PHBV/Ecoflex®

Pellicano, Marilia; Pachekoski, Wagner; Agnelli, José A. M.
2009-01-01

Resumo em português Os polímeros derivados do petróleo são amplamente utilizados devido à sua versatilidade, propriedades mecânicas e custo relativamente baixo, mas causam impacto ambiental como conseqüência da grande quantidade de resíduos lançados ao meio ambiente. Os problemas gerados pelo descarte de plásticos de origem petroquímica impulsionam o desenvolvimento, produção e aplicação de polímeros biodegradáveis. Entretanto, estes polímeros apresentam custo elevado e pro (mais) priedades nem sempre satisfatórias. Portanto, neste trabalho fez-se um estudo do composto polimérico formado por poli(hidroxibutirato-co-valerato) - PHBV (Biocycle®), poli(butilenoadipato-tereftalato) - Ecoflex® e amido de mandioca. Este composto polimérico foi avaliado quanto ao índice de fluidez (MFI), Microscopia Eletrônica de Varredura (MEV), ensaios mecânicos de tração e de impacto, e ensaio de biodegradação. Os resultados obtidos nas diversas técnicas indicaram: que o amido de mandioca atua como uma carga inerte; que existe uma baixa adesão matriz/carga no composto polimérico e que a adição de amido aumenta a taxa de biodegradação do composto, em relação aos polímeros puros. No estudo realizado foi possível obter um material para aplicação no curto prazo, com um custo viável, propriedades físico-mecânicas adequadas e excelente taxa de biodegradação. Resumo em inglês Plastic materials produced from petrochemicals are widely used due to their versatility, mechanical properties and low cost, but they cause environmental impact as a consequence of the accumulation of great amount of these conventional synthetic polymers. The problems caused by the waste disposal of these plastics have motivated the development, production and application of biodegradable polymers; however these polymers have high costs and non-suitable mechanical and phy (mais) sical properties. Therefore, a study of polymeric compounds made of poly(hydroxyburyrate-co-valerate) - PHBV, poly(butylyneadiapate-therefhtalate) - Ecoflex® and cassava starch has been done. This polymeric compound was evaluated using Melt Flow Index (MFI), Scanning Electron Microscopy (SEM), mechanical and biodegradation tests. The results indicate that the cassava starch acts as an inert filler, and that there is no significant adhesion between cassava starch and PHBV/Ecoflex®. More importantly, adding cassava led to good biodegradation results. This study therefore demonstrates that it is possible to obtain viable materials for short-term applications, with adequate physical and mechanical properties and excellent biodegradation results.

Scientific Electronic Library Online (Portuguese)

65

Influência da temperatura no desempenho mecânico de compósitos PEI/fibras de vidro/ Influence from the temperature on the mechanical behavior of PEI/glass fiber composites

Oliveira, Gustavo H.; Guimarães, Valdir A.; Botelho, Edson C.
2009-01-01

Resumo em português Os compósitos poliméricos vêm ganhando grande destaque devido aos avanços tecnológicos conquistados pelas indústrias, principalmente a aeroespacial. Estes avanços têm como uma de várias finalidades a obtenção de compósitos com baixa massa específica associada às elevadas resistência mecânica e rigidez. Comparando os compósitos termoplásticos aos termorrígidos, pode ser destacado como suas principais vantagens: processamento mais rápido pela ausência d (mais) e um ciclo de cura; baixa absorção de umidade; excelente resistência química; maior temperatura de serviço; baixo custo de transporte e estocagem; maior resistência ao impacto; maior rigidez e a possibilidade de serem reciclados. Devido às grandes variações de temperatura que estes materiais estão sujeitos durante sua vida útil como artefatos de aplicação aeronáutica, é de extrema importância a realização de estudos do seu comportamento mecânico a elevadas temperaturas, uma vez que a estas temperaturas as propriedades do compósito podem ser modificadas. O presente trabalho visa avaliar o comportamento mecânico (tração, fadiga e cisalhamento interlaminar, tanto em temperatura ambiente como a 80 °C) de compósitos termoplásticos de matriz PEI (poli(éter-imida)) reforçados com fibras de vidro. Observou-se que os valores de resistências à tração, cisalhamento e fadiga do laminado PEI/fibras de vidro foram superiores aos encontrados para o laminado de epóxi/fibras de vidro. Entretanto, em todos os casos foram observadas quedas significativas nas propriedades mecânicas obtidas a 80 °C, em comparação com aquelas à temperatura ambiente. Resumo em inglês Polymeric composites have been used due to the technological progress in industries, mainly the aerospace. These advances are aimed at obtaining composites with low specific gravity associated with high mechanical properties and stiffness. The main advantages of thermoplastics over thermoset laminates include: fast processing due to the absence of a cure cycle, low moisture absorption, excellent chemical resistance; higher service temperature; low costs of transport and s (mais) torage, higher impact resistance; higher stiffness and possibility of recycling. It is therefore important to investigate the mechanical properties at high temperatures since these materials are subjected to large temperature variations in aeronautical applications. This work is aimed at evaluating the mechanical properties (tensile, fatigue and interlaminar shear behavior) of PEI reinforced with glass fiber at 25 and 80 °C. The tensile, shear and fatigue stresses for PEI/glass fiber were found to be higher than in epoxy/glass fiber laminates. However, in all cases a significant deterioration in the mechanical properties was observed at 80 °C in comparison to those at room temperature.

Scientific Electronic Library Online (Portuguese)

66

Modificação das propriedades das fibras de curauá por acetilação/ Modification of the properties of curauá fibers by acetylation

Lopes, Fernanda F. M.; Araújo, Gilmar T.; Luna, Saionara; Nascimento, José W. B. do; Silva, Valneide R. da
2011-03-01

Resumo em português Nos compósitos cimentíceos as fibras vegetais podem sofrer vários graus de degradação quando expostas ao ambiente alcalino. O meio alcalino degrada os componentes macromoleculares das fibras, principalmente pela solubilização da lignina e a desfibrilação da celulose, comprometendo suas propriedades físicas e mecânicas. A resistência das fibras vegetais ao ataque alcalino pode ser aumentada por meio de tratamentos químicos superficiais como a acetilação que (mais) apresenta capacidade de reduzir a natureza higroscópica de compostos lignocelulósicos pela introdução de grupos funcionais hidrofóbicos em sua estrutura química. Objetivou-se, então neste trabalho, a aplicação do tratamento de acetilação em diferentes níveis, visando melhorias na durabilidade das fibras. O tratamento de acetilação nas fibras de curauá foi aplicado em diferentes temperaturas e tempos reacionais e sua eficiência, considerando-se a redução da hidrofilicidade e a manutenção do desempenho físico-mecânico das fibras, foi avaliada pelos ensaios de absorção de água por imersão, resistência mecânica, espectroscopia de infravermelho, microscopia eletrônica de varredura, análise termogravimétrica e difratometria de raios-x. Quando acetiladas, as fibras de curauá apresentaram absorções até 55% menores que nas fibras não tratadas. As perdas na resistência mecânica foram próximas aos 52%. O tratamento de acetilação agregou grupos químicos hidrofóbicos na composição e alterou o caráter cristalino das fibras. Resumo em inglês In cementitious composite the vegetable fibers may suffer various degrees of degradation when exposed to alkaline medium. The alkaline degradation of macromolecular components of fibers mainly by lignin solubilization and cellulose defibrillation, compromising the physical and mechanical properties. The resistance of plant fiber to alkali attack can be improved by chemical surface treatments such as acetylation that can reduce the hygroscopic nature of lignocellulosic int (mais) roducing hydrophobic functional groups in its chemical structure. Thus, the aim of this study was the application of the acetylation treatment at different levels to improve the durability of the fibers.The acetylation treatment in curauá fiber was applied at different temperatures and reaction times, and its efficiency, considering the reduction of hydrophilicity and maintenance of the physical-mechanical performance of fibers was evaluated by water absorption, mechanical resistance, infrared spectroscopy, scanning electron microscopy, thermogravimetric analysis and diffraction of x-rays. When acetylated curauá fibers absorbed up to 55% less water than untreated fibers. In strength, losses were up 52%. The acetylation treatment introduced hydrophobic chemical groups in the composition and changed crystalline character of fibers.

Scientific Electronic Library Online (Portuguese)

67

Escarificação mecânica e biológica para a redução da compactação em argissolo franco-arenoso sob plantio direto/ Mechanical and biological chiseling to reduce compaction of a sandy loam alfisol under no-tillage

Abreu, S. L.; Reichert, J. M.; Reinert, D. J.
2004-06-01

Resumo em português O manejo influi nas propriedades físicas no campo, alterando a dinâmica do ar, da água e de solutos no solo. Propriedades físicas em sistemas de manejo conservacionista do solo foram avaliadas em um Argissolo Vermelho-Amarelo distrófico arênico (Typic Hapludalf) de textura franco-arenosa no horizonte A. Os tratamentos foram estabelecidos em solo com histórico de 10 anos de plantio direto, a saber: soja em sistema plantio direto; soja em solo escarificado; crotalár (mais) ia em cultivo mínimo e solo descoberto sem preparo. Foram determinadas: a resistência mecânica à penetração; a densidade do solo; a porosidade total; a distribuição do tamanho de poros; a condutividade hidráulica do solo saturado e não saturado; a infiltração de água no solo pelos métodos de anéis concêntricos e sob chuva natural; a variação da umidade volumétrica do solo durante o ciclo das culturas e a curva característica de água no solo. Observou-se que a resistência mecânica à penetração (RP) foi máxima na camada de 0,075 m, nos tratamentos sem preparo do solo, enquanto, no solo escarificado (Esc-soja), a RP máxima ocorreu em maior profundidade (0,175 m). A mobilização subsuperficial (escarificação) e a superficial (discagem e semeadura) do solo não se refletiram em redução na densidade do solo (Ds). O solo sob plantio direto de soja apresentou maior volume de macroporos que o solo sob cultivo de crotalária e descoberto, na profundidade 0,02 a 0,05 m, favorecendo a maior condutividade hidráulica do solo saturado e a menor retenção de água no solo em situação de déficit hídrico. Dentre as propriedades físico-mecânicas analisadas, a RP mostrou-se mais sensível em detectar a compactação do que a Ds e porosidades, especialmente para camadas de solo pouco espessas. A eficácia da ruptura da camada compactada do solo depende da propriedade hídrica ou mecânica do solo usada como indicadora. Usando a condutividade hidráulica do solo saturado, em médio prazo, a "escarificação biológica" (CM-crot) mostrou-se mais eficaz na ruptura da camada compactada e estabelecimento de poros condutores de água do que a escarificação mecânica (Esc-soja) do solo. Em contrapartida, se o indicador for a RP, o resultado é inverso. Assim, a propriedade hídrica ou mecânica do solo a ser usada como indicadora para a avaliação da eficácia da ruptura da camada compactada do solo depende do processo físico priorizado: a infiltração e redistribuição de água ou a penetração e crescimento de raízes. Resumo em inglês Soil management alters the physical soil properties and changes the soil air, water, and solute dynamics. Physical soil properties as affected by conservationist soil management systems were studied in a sandy loam Typic Hapludalf. The treatments were established on a soil that has been under no-tillage for 10 years, and consisted of: no-tillage soybeans, chisel tillage soybeans, reduced tillage Crotalaria, and bare soil without tillage. The evaluated soil properties were (mais) soil penetration resistance, bulk density, porosity, pore size distribution, saturated and unsaturated hydraulic conductivity, water infiltration using concentric rings or natural rainfall, variation of the volumetric soil moisture throughout the cropping cycle, and water retention curve. Soil penetration resistance (PR) was highest at 0.075 m and 0.175 m depth in no-tillage and chiseled soil, respectively. Soil subsurface mobilization with chiseling and surface mobilization due to disking and sowing did not influence the bulk density (BD) after the crop harvest. No-till soil under soybean crop had greater macroporosity than reduced tillage crotalaria and bare soil at 0.02 to 0.05 m depth, resulting in a greater saturated hydraulic conductivity and lower water retention during periods of low water availability. Among the analyzed soil physical-mechanical properties, PR seemed to be more sensitive to detect soil compaction than BD or porosities, particularly for thinner soil layers. The effectiveness in rupturing compacted soil depended on the hydraulic or mechanical soil property used as indicator. When using K(thetas) as indicator, in the medium term (4.5 months), "biological chiseling" by Crotalaria roots was more efficient at ameliorating soil compaction and establishing a network of conductive pores compared to mechanical chiseling. However, inverse results were observed when PR was used as indicator. Thus, the choice of a soil physical property as indicator to evaluate the effectiveness of compaction reduction depends on which physical process is considered more important: water infiltration and redistribution or root penetration and growth.

Scientific Electronic Library Online (Portuguese)

68

Caracterização microestrutural e comportamento mecânico das ligas de alumínio AA2139 T3 e T8 soldadas por fricção rotativa com mistura/ Microstructural characterization and mechanical behavior of an AA2139 T3 and T8 aluminum alloy joined by friction stir welding (FSW)

Saccon, Vinícius Toledo; Parra, Bruno Serafim; Olea, Cesar Weis; Santos, Jorge Fernandes dos; Alcântara, Nelson Guedes de
2010-12-01

Resumo em português Este trabalho visou analisar a caracterização microestrutural e o comportamento mecânico das ligas de alumínio AA2139 T3 e T8 quando são soldadas pelo processo Soldagem por Fricção Rotativa com Mistura, o qual é realizado na fase sólida. A análise microestrutural foi realizada utilizando microscopia óptica e eletrônica de varredura, e o comportamento mecânico foi avaliado através de medidas de microdureza e ensaio de tração convencional complementado pelo (mais) sistema ARAMIS. As ligas foram soldadas nos mesmos parâmetros de soldagem e com a mesma ferramenta, a fim de avaliar a qualidade da junta soldada para as duas condições de tratamento térmico, T3 e T8. Os resultados obtidos mostraram soldas resistentes para ambos os tratamentos térmicos, porém com melhores propriedades mecânicas para a liga AA2139 T3. Resumo em inglês This work aimed to study the microstructural characterization and mechanical behavior of AA2139 T3 and T8 aluminum alloys joined by FSW - Friction Stir Welding. The microstructural analysis has been done using optical microscope and scanning electron microscopy, and the mechanical analysis were evaluate through microhardness testing and conventional tensile test using the ARAMIS system . Each alloy were welded using the same welding parameters and the same tool in order t (mais) o evaluate the joint quality for both heat treatment used for this work, T3 and T8. The result showed sounds joints for both heat treatments, although with better mechanical properties for the alloy AA2139 T3.

Scientific Electronic Library Online (Portuguese)

69

Blendas PVC/NBR por processamento reativo II: caracterização físico-mecânica e morfológica/ PVC/NBR blends by reactive processing II: physical-mechanical and morphological characterization

Passador, Fábio R.; Pessan, Luiz A.; Rodolfo Jr., Antonio
2008-06-01

Resumo em português Vulcanização dinâmica é o processo de vulcanização de um elastômero durante a mistura no estado fundido com um termoplástico. Por este processo, o elastômero adquire resistência mecânica através do aumento do módulo de elasticidade, dureza, resistência à fadiga e abrasão. Neste trabalho, buscou-se avaliar as propriedades físico-mecânicas e as características morfológicas de blendas poliméricas constituídas de Poli(cloreto de Vinila) e borracha nitrí (mais) lica, PVC/NBR, obtidas por processamento reativo. A vulcanização dinâmica melhorou o desempenho mecânico destas blendas, notadamente pelo aumento da rigidez desses sistemas, sendo obtido um aumento de 205% no módulo elástico de blendas vulcanizadas com 10% em massa de NBR em comparação com blendas convencionais. Através de análises de MEV, revelou-se uma morfologia bifásica, sendo que a formação de ligações cruzadas deve ocorrer preferencialmente no interior das partículas do elastômero, contribuindo para o aumento na resistência mecânica final das blendas obtidas por processamento reativo. Resumo em inglês Dynamic vulcanization is a process of vulcanization of an elastomer during melt mixing with a thermoplastic. This process increases the mechanical resistance of elastomers through the increase of elastic modulus, hardness and abrasion/fatigue resistance. In this study, it was evaluated the physical-mechanical and morphological behaviors of the PVC/NBR blends obtained by reactive processing. The dynamic vulcanized blends have a better performance compared to the similar co (mais) nventional ones. It was observed an increase of 205% in the elastic modulus to the dynamic vulcanized blend PVC/NBR (90/10) compared with the conventional blends. The morphology of the blends examined by scanning electron microscopy evidenced the crosslinking formation only in the elastomeric phase. The vulcanized rubber particles are responsible by the increase of stiffness and consequently displayed better mechanical properties.

Scientific Electronic Library Online (Portuguese)

70

Estudo comparativo entre os fios de polidioxanona e poliamida na tenorrafia de coelhos/ The use of polidioxanone and poliamide sutures in rabbit's tenorraphy

Silva, Roberto Antoniolli da; Fagundes, Djalma José; Silva, Andréia C.M. Antoniolli da; Figueiredo, Arthur Silveira de; Cantero, Wilson de Barros
2002-02-01

Resumo em português OBJETIVO: estabelecer comparação entre as propriedades mecânicas das tenorrafias realizadas com poliamida (náilon) e polidioxanona (PDS). MÉTODOS: Foram utilizados 56 coelhos adultos, machos, Nova Zelândia, distribuídos em dois grupos e quatro subgrupos: GIA - tenorrafias com polidioxanona e avaliação após duas semanas; GIB - tenorrafias com polidioxanona e avaliação após quatro semanas; GIIA - tenorrafias com náilon e avaliação após duas semanas; GIIB - (mais) tenorrafias com náilon e avaliação após quatro semanas. Foram realizados ensaios de tração nas tenorrafias dos tendões dos coelhos. RESULTADOS: na avaliação aos quinze dias de pós-operatório, o náilon apresentou como resultados dos ensaios mecânicos, valores superiores que os do PDS para carga máxima, coeficiente de rigidez, deformação, deformação no limite de proporcionalidade, carga no limite de proporcionalidade, que foram as variáveis analisadas. CONCLUSÃO: aos trinta dias de pós-operatório não houve diferença significante entre o uso do náilon e o PDS. Resumo em inglês OBJECTIVE: comparative study between the mechanical properties of the tenorraphies with poliamida (nylon) and polidioxanone (PDS). METHODS: 56 adult, male, New Zealand rabbits were used, distributed in two groups and four sub groups: GIA-tenorraphies with polidioxanone and evaluation after two weeks; GIB-tenorraphies with polidioxanone and evaluation after four weeks; GIIA-tenorraphies with nylon and evaluation after two weeks; GIIB-tenorraphies with nylon and evaluation (mais) after four weeks. Traction tests were done in tenorraphies of the rabbits. RESULTS: after fifteen days nylon presented as results of the mechanical tests, superior values that the one of PDS for maximum load, rigidity coefficient, deformation, deformation in the proportionality limit, load in the proportionality limit, that were the variable analysed. CONCLUSION: after thirty days there was not significant difference between nylon and PDS.

Scientific Electronic Library Online (Portuguese)

71

Efeitos do treinamento físico sobre a resistência mecânica do terço proximal do fêmur de ratos/ Effects of physical training on the mechanical resistance of rat femur proximal thirds

Aguiar, Andreo Fernando; Agati, Leandro Barile; Müller, Sérgio Swain; Pereira, Oduvaldo Camara; Dal-Pai-Silva, Maeli
2010-01-01

Resumo em português OBJETIVO: Analisar o comportamento mecânico do terço proximal do fêmur de ratos submetidos ao treinamento aeróbio e resistido crônicos. MÉTODOS: Ratos Wistar machos (80 dias, 300 a 350 g) foram divididos em 3 grupos (n=8 por grupo): Treinamento aeróbio/8 semanas (TA), Treinamento resistido/8 semanas (TR) e controle/8 semanas (CO). Ao término do período de treinamento os animais foram sacrificados e o fêmur direito coletado. Para análise do comportamento mecâni (mais) co do fêmur foram realizados ensaios de flexo-compressão. RESULTADOS: O treinamento resistido ocasionou redução significante da força máxima (Fmáx) do fêmur. Por outro lado, promoveu um aumento (23,7%) relevante, porém não significante, da deformação da força máxima (DFmáx). O treinamento aeróbio não afetou a Fmáx, porém promoveu uma redução (26,6%) considerável, também não significante, da DFmáx. CONCLUSÕES: Os resultados demonstram que o treinamento resistido e aeróbio, promoveram redução da Fmáx e da DFmáx óssea, respectivamente. Os dados evidenciam uma ação diferencial de ambos os modelos de treinamento físico sobre as propriedades mecânicas do fêmur de ratos. Resumo em inglês OBJECTIVE: To analyze the mechanical behavior of rat femur proximal thirds submitted to chronic aerobic and resistance training. METHODS: Male Wistar rats (80 days of age, weighing 300 to 350 g) were divided into 3 groups (n=8 per group): control (CO), aerobic training (TA) and resistance training (TR). At the end of the training, the animals were euthanized and the right femur was collected. Flexion-compression tests were carried out to analyze the mechanical behavior of (mais) the femurs. RESULTS: The resistance training promoted a significant reduction in maximum force (Fmáx) of the femur. However, it also promoted a relevant increase (23.7%), though without statistical significance, in maximum force deformation (DFmáx). The aerobic training did not affect maximum force, however, it caused a considerable reduction in DFmáx (26.6%), though this was also not statistically significant. CONCLUSIONS: The results show that resistance and aerobic training promoted a reduction in the Fmáx and DFmáx, respectively. The data showed a different response of both physical training models on the mechanical properties of the rat femurs.

Scientific Electronic Library Online (Portuguese)

72

Efeito da temperatura de queima nas propriedades e microestrutura de cerâmica vermelha contendo chamote/ Effect of the firing temperature on the properties and microstructure of red ceramic incorporated with grog

Vieira, C. M. F.; Teixeira, S. S.; Monteiro, S. N.
2009-09-01

Resumo em português Este trabalho tem por objetivo avaliar o efeito da temperatura de queima nas propriedades de uma cerâmica constituída por argila caulinítica e incorporada com até 20% em peso de chamote. Foram preparados corpos de prova cilíndricos por prensagem uniaxial a 20 MPa para queima em forno de laboratório de 500 a 1100 ºC. As propriedades avaliadas foram densidade aparente, retração diametral, absorção de água e resistência mecânica. A microestrutura das cerâmicas (mais) foi avaliada por microscopia eletrônica de varredura e porosimetria de mercúrio. Os resultados indicaram que não houve variação significativa nas propriedades avaliadas entre 500 e 900 ºC. A partir daí, ocorreu uma redução brusca da porosidade que ocasionou um decréscimo da absorção de água e melhoria da resistência mecânica. A incorporação de 5% de chamote praticamente não alterou as propriedades da cerâmica. Entretanto, foi observado que a adição de maiores quantidades de chamote reduziu a resistência mecânica de queima da cerâmica. Resumo em inglês This work has the objective of evaluating the effect of the firing temperature on the properties and microstructure of a kaolinitic clay incorporated with up to 20 wt. % of grog. Cylindrical specimens uniaxially pressed under 20 MPa were prepared and fired at temperatures ranging from 500 to 1100 ºC in a laboratory furnace. The properties evaluated were bulk density, diametral shrinkage, water absorption and mechanical strength. The microstructure of the ceramics was eva (mais) luated by scanning electron microscopy and mercury porosimetry. The results showed that no significant changes occurred in the evaluated properties of the compositions upon firing between 500 and 900 ºC. For higher firing temperatures, an abrupt decrease in the porosity resulted in a decrease in water absorption and an increase in mechanical strength. The incorporation of 5 wt.% of grog practically did not alter the properties of the ceramic. However, it was observed that higher amounts of grog decreased the fired mechanical strength of the clayey ceramic.

Scientific Electronic Library Online (Portuguese)

73

Utilização de finos de brita em cerâmica argilosa/ Use of stone fines into clayey ceramic

Camara, R.S.; Monteiro, S.N.; Vieira, C.M.F.
2010-01-01

Resumo em português Este trabalho tem por objetivo a avaliar a influência da incorporação de finos de brita na microestrutura e nas propriedades de queima de uma massa cerâmica argilosa. As propriedades avaliadas foram: retração linear, absorção de água e tensão de ruptura à flexão. Foram preparadas composições com 0% e 25% em peso de finos de brita para a obtenção de corpos-de-prova por extrusão para queima em temperaturas de 800 a 1200ºC. A microestrutura das cerâmicas q (mais) ueimadas foi avaliada por microscopia ótica. Os resultados mostraram que a incorporação de finos de brita é benéfica para a produção de cerâmica vermelha possibilitando redução da retração linear e da absorção de água, sem muito efeito na resistência mecânica. Resumo em inglês This work has as its objective to evaluate the incorporation of stone fines in the microstructure and fired properties of a clayey ceramic. The evaluated properties were: linear shrinkage, water absorption and flexural strength. Compositions were prepared with 0 and 25 wt.% of stone fines to obtain specimens by extrusion that were fired at temperatures varying from 800 to 1200ºC. The microstructure of the fired ceramics was evaluated by optical microscopy. The results sh (mais) owed that the incorporation of stone fines is beneficial to the production of red ceramic by decreasing both the linear shrinkage and the water absorption, without much effect on the mechanical strength.

Scientific Electronic Library Online (Portuguese)

74

Características da sílica coloidal e seus efeitos em concretos refratários/ Characteristics of colloidal silica and its effects on refractory castables

Magliano, M. V. M; Pandolfelli, V. C
2010-06-01

Resumo em português A sílica coloidal se apresenta como um promissor substituto do cimento de aluminato de cálcio para utilização em concretos mulitizáveis. O uso deste ligante promove adequada resistência mecânica a verde, facilidade de secagem, inibe a formação de fases de baixo ponto de fusão, além de favorecer a formação de mulita in-situ. Entretanto, as propriedades finais do concreto dependem das características da solução coloidal utilizada. O objetivo deste trabalho � (mais) � comparar as propriedades a verde e a quente de sistemas mulitizáveis ligados por sílica coloidal, variando suas características, tais como teor de sólidos, área superficial e tipo de estabilizante. Os resultados indicaram que sílicas coloidais com alta área superficial reduzem a trabalhabilidade dos concretos e diminuem as propriedades a quente devido ao acentuado trincamento durante a cura. A refratariedade dos sistemas é ainda comparada com concretos ligados por cimento de aluminato de cálcio e alumina hidratável, ressaltando a superioridade do ligante coloidal. Resumo em inglês The colloidal silica has been shown as a promising substitute for the aluminate cement as a binder for refractory castables. It can promote suitable mechanical strength for green bodies, reduce the explosion risk and does not develop phases with low melting point in the alumina systems. In addition, they can induce the in-situ mullite formation. Nevertheless, the final properties of the castable can also depend on the colloidal suspension characteristics such as, solid co (mais) ncentration, surface area and stabilizing agents. This paper aims to compare the green and high temperature properties of castables using different types of colloidal silicas. The results showed that colloidal silica containing a high surface area builds up internal tensions and cracks during the drying process, which deteriorate the hot mechanical properties of the castables. Besides that, they also reduce the workability and the free flow of the system. The results presented were also compared with the refractoriness of others binding systems such as aluminate cement and reactive alumina on colloidal silica containing castables.

Scientific Electronic Library Online (Portuguese)

75

Síntese e caracterização de dispersões aquosas de poliuretanos à base de copolímeros em bloco de poli(glicol etilênico) e poli(glicol propilênico)/ Synthesis and characterization of polyurethane aquous dispersions based on poly(ethylene glycol) and poly(propylene glycol) block copolymers

Coutinho, Fernanda M. B.; Delpech, Marcia C.; Santos, Cristiane C.; Almeida, Rosiléa B. L.
2008-01-01

Resumo em inglês Non-polluting polyurethane aqueous dispersions, with 40% of solids content, were synthesized based on block copolymers of poly(ethylene glycol) and poly(propylene glycol) (PEG-b-PPG), with PEG hydrophilic segments content of 7 and 25%, poly(propylene glycol) (PPG), dimethylolpropionic acid (DMPA), isophorone diisocyanate (IPDI), and hydrazine. Different formulations were synthesized by varying the equivalent-grams ratios between isocyanate and hydroxyl groups (NCO/OH) and (mais) PPG and (PEG-b-PPG). The presence of high amounts of PEG in the formulations provoked the formation of gels. Average particle size and viscosity of the dispersions were determined. Mechanical properties and water absorption resistance of cast films were evaluated.

Scientific Electronic Library Online (Portuguese)

76

Simulador de propagação de ondas mecânicas em meios sólidos para o ensino da física/ A simulator of mechanical wave propagation in a solid for the teaching of physics

Piubelli, Sérgio Luiz; Errobidart, Hudson Azevedo; Gobara, Shirley Takeco; Errobidart, Nádia Cristina Guimarães
2010-03-01

Resumo em português O artigo apresenta a descrição de um aparato experimental construído, com materiais de baixo custo, para simular e evidenciar a influência das características inerciais e elásticas do meio na velocidade de propagação de uma onda mecânica longitudinal. O dispositivo foi construído com o objetivo de minimizar as dificuldades relacionadas ao processo de ensino e aprendizagem de conceitos da física, em especial do conteúdo de ondas. Trata-se de um experimento demonstrativo que pode ser feito em sala de aula ou em laboratórios didáticos. Resumo em inglês The article describes a low-cost experimental apparatus built to simulate and highlight the influence of inertia and elastic properties of matter on the speed of propagation of a mechanical wave. The aim for building this device was to minimize the difficulties associated with the teaching and learning process of physical concepts, particularly in the context of waves. It is about a demonstrative experiment that can be done in classrooms or in a teaching lab.

Scientific Electronic Library Online (Portuguese)

77

Resistência mecânica de hidrogéis termo-sensíveis constituídos de Alginato-Ca2+ / PNIPAAm, tipo Semi-IPN/ Mechanicals resistance of thermosensitive hydrogels consisting of alginate-Ca2+ / PNIPAAm, type Semi-IPN

Campese, Gilsinei Marques; Tambourgi, Elias Basile; Guilherme, Marcos Rogério; Moura, Márcia Regina de; Muniz, Edvani Curti; Youssef, Elza Youssef
2007-01-01

Resumo em inglês Thermosensitive hydrogels were synthesized using alginate-Ca2+ in association with a thermosensitive polymer, such as PNIPAAm. The mechanical properties of the hydrogels were determined measuring the maximum tension of deformation. With the increase of the temperature by 25 to 40 ºC above the LCST the chains of PNIPAAm collapsed, dragging the alginate net and diminishing the size of the pores. The decrease in the size of the pores of the hydrogel was followed by an increase in the mechanicals resistance of the material.

Scientific Electronic Library Online (Portuguese)

78

Relações entre produtividade de Brachiaria Brizantha e atributos físicos de um latossolo do cerrado/ Relationships between yield of Brachiaria Brizantha and physical properties of a savannah oxisol

Cavallini, Maria Cecília; Andreotti, Marcelo; Oliveira, Letícia Lisbôa; Pariz, Cristiano Magalhães; Carvalho, Morel de Passos e
2010-08-01

Resumo em português Em sistema de integração lavoura-pecuária, os diversos cultivos em sistema plantio direto alteram os atributos físicos do solo, refletindo sobre a produtividade e a composição vegetal. O objetivo deste trabalho foi indicar atributos do solo com melhor correlação com a produtividade e teor de proteína da Brachiaria brizantha. Foram analisadas as correlações lineares e espaciais entre a produtividade de matéria seca (MS) e o teor de proteína bruta (PB) de Brach (mais) iaria brizantha (cv. Marandu) e de alguns atributos físicos de um Latossolo Vermelho distroférrico (Oxisol), em três profundidades (zero-0,10; 0,10-0,20; e 0,20-0,30 m). Para isso, foi instalada a malha geoestatística (entre 20 º 18 ' 05 '' S e 20 º 18 ' 28 '' S, e entre 52 º 39 ' 02 '' W e 52 º 40 ' 28 '' W) para a coleta dos dados, contendo 124 pontos amostrais, numa área de 4.000 m². A produtividade e o teor de proteína bruta de Brachiaria brizantha não variaram aleatoriamente e seguiram padrões espaciais bem definidos, com semivariogramas do tipo esférico, com alcances da dependência espacial, aproximadamente, entre 40 e 50 m. O aumento da resistência mecânica à penetração e da umidade do solo na camada superficial, no cultivo de Brachiaria brizantha, promove a redução do teor de proteína bruta e da matéria seca. A porosidade total na camada de 0,20-0,30 m, é um importante indicador da qualidade física do solo e apresenta confiabilidade para estimativa da produtividade de matéria seca de Brachiaria brizantha. Resumo em inglês Crop-livestock integration can affect soil physical properties, altering the yield and plant composition during the various no-tillage crop cycles. The objective of this study was to select the soil properties with the clearest relationship with yield and crude protein content of Brachiaria brizantha. Linear and spatial correlations were analyzed between dry matter yield and crude protein of Brachiaria brizantha and of some physical properties of a Dystroferric Red Latoso (mais) l (Oxisol), in three layers (0-0.10; 0.10-0.20; 0.20-0.30 m). A geostatistical grid was installed for data collection, containing 124 points in an area of 4,000 m² (20 º 18 ' 05 '' S - 20 º 18 ' 28 '' S and 52 º 39 ' 02 '' W - 52 º 40 ' 28 '' W). No random variation was observed for the yield and crude protein content of Brachiaria brizantha, but well-defined spatial standards with spherical semivariograms reaching a spatial dependence of approximately 40-50 m. The increase of mechanical penetration resistance and of soil moisture in the surface layer of soil under Brachiaria brizantha resulted in lower crude protein content and dry matter. Total porosity in the 0.20-0.30 m layer is an important indicator of the soil physical quality and proved reliable for estimations of the dry matter yield of Brachiaria brizantha.

Scientific Electronic Library Online (Portuguese)

79

Propelente sólido compósito polibutadiênico: I- influência do agente de ligação/ Solid polyurethane-based composite propellant: I- influence of the bonding agent

Sciamareli, Jairo; Takahashi, Marta Ferreira Koyama; Teixeira, José Maria; Iha, Koshun
2002-02-01

Resumo em inglês In the Brazilian Complete Spacial Mission, the research of Vehicle Satellite Launcher is important. The solid propellant composite used in this vehicle is made with ammonium perchlorate, aluminiun powder and hydroxy terminated polibutadiene resin. In the propellant the bonding agent has a function to promote the interaction between solids and polimeric matrix, improving mechanical properties as stress, strain, aging characteristics and moisture embrittlement. Due its impo (mais) rtance in propellant, bonding agent is consider as industrial secret and the literature about it is generic, without greater informations.

Scientific Electronic Library Online (Portuguese)

80

Processamento e caracterização de espumas vitrocerâmicas do sistema sncp (Sio2-Na2o-Cao-P2 O5)/ Processing and characterization of sncp (Sio2-Na2o-Cao-P2o5) glass-ceramic foams

Mundstock, Karoline Bastos; Moraes, Elizangela Guzi de; Hotza, Dachamir; Oliveira, Antonio Pedro Novaes de; Siligardi, Cristina; Rogero, Sizue Ota
2010-01-01

Resumo em inglês Glass-ceramics foams prepared from glasses of the SiO2-Na2O-CaO-P2O5 by replication process were obtained and characterized in terms of their chemical and physical properties by X-ray fluorescence, X-ray diffraction, laser diffraction, thermal analysis, density, mechanical strength, microstructural and cytotoxic analysis. The results showed that it is possible to produce glass-ceramic foams by the replication method with optimized properties but cytotoxic analysis indicat (mais) es that the glass-ceramic foams are not bioactive materials. Mechanical strength values varying from 0.5 to 1.0 MPa and from 0.8 to 2.3 MPa were reached for mean particle sizes of 10 and 6 µm, respectively.

Scientific Electronic Library Online (Portuguese)

81

Preparação e caracterização de blendas de quitosana/poli(álcool vinílico) reticuladas quimicamente com glutaraldeído para aplicação em engenharia de tecido/ Preparation and characterization of chitosan/poly(vinyl alcohol)blend chemically crosslinked by glutaraldehyde for tissue engineering application

Costa Jr., Ezequiel de Souza; Mansur, Herman Sander
2008-01-01

Resumo em inglês In this study, novel Chitosan/PVA based films were chemically crosslinked by glutaraldehyde, under pH=(4,00 ±0,05), in order to achieve structures tailored for wound tissue engineering applications. Both precursors and developed films were characterized by FTIR, SEM and XRD in order to determine the presence of chemicals groups and nanostructural order, respectively. The results have shown that the glutaraldehyde crosslinking have altered the crystallinity of pure chitos (mais) an and the increase on the C=N bands and simultaneous decrease on NH2 bands suggested that Chitosan/GA crosslinking has preference to occur in carbon-2 of the saccharide ring by the Schiff's base reaction. Also, FTIR spectroscopy clearly showed that crosslinking has also taken place with blends of PVA and chitosan. The mechanical properties presented high degree dependence with on the increase of the content of chitosan and glutaraldehyde. The results have indicated that, by controlling the ratio [PVA]/[chitosan] in the blends and the extent of chemical crosslinking, it was possible to tailor the hybrid network produced aiming to obtain properties of interest for the specific application.

Scientific Electronic Library Online (Portuguese)

82

Nano vitrocerâmica de escória de aciaria/ Glass-ceramic from steelmaking slag

Ferreira, Eduardo Bellini; Zanotto, Edgar Dutra; Scudeller, Luis Augusto Marconi
2002-09-01

Resumo em inglês The manufacture of glass-ceramics is an alternative route for the commercial use of metallurgical slags. Such types of glass-ceramics may find commercial applications owing to their low cost, good mechanical properties and superior visual aspect. Besides, due to the elimination of that industrial residue from the environment and also due to the possibility of replacement of natural stones such as marbles and granites, the use of slags is an activity with strong ecological (mais) appeal. While the use of blast-furnace slags for the production of glass-ceramics is well known, the utilization of steel making slags constitutes a challenge, because these materials possess low concentration of SiO2. In this work a novel composition for producing glasses and glass-ceramics from a steelmaking slag is presented. The crystal nucleation kinetics, the characterization of the resulting microstructures for two different thermal treatments and mechanical properties of the glass-ceramics are discussed. A glass-ceramic having a marble aspect, fine volumetric crystallization, high degree of crystallization and improved mechanical strength was obtained.

Scientific Electronic Library Online (Portuguese)

83

Estudo dos efeitos da acetilação em fibras de sisal/ Study of the effects of acetylation treatments on sisal fiber

Lopes, Fernanda F. M.; Araújo, Gilmar T. de; Nascimento, José W. B. do; Gadelha, Tatiana S.; Silva, Valneide R. da
2010-07-01

Resumo em português O emprego de fibras vegetais na confecção de compósitos tem grande viabilidade, no que diz respeito ao uso de materiais oriundos de fontes renováveis, à biodegradabilidade e aos benefícios socioeconômicos gerados na produção de matéria-prima vegetal. As fibras de sisal são altamente higroscópicas e esta característica se apresenta como um dos principais problemas na produção de compósitos induzindo a variações dimensionais sob a influência da umidade, d (mais) eposição dos produtos da matriz em seus poros e a degradação. Os tratamentos de acetilação nas fibras de sisal foram aplicados em diferentes temperaturas e tempos reacionais, e a eficiência desses tratamentos, considerando-se a redução da hidrofilicidade e a manutenção do desempenho mecânico das fibras, foi avaliada pela capacidade de absorção de água por imersão, ensaios de resistência mecânica e por espectroscopia de infravermelho. Fibras acetiladas apresentaram reduções de peso por absorção de até 50% quando comparadas com as não tratadas. Os tratamentos por 3 h apresentaram as maiores perdas na resistência mecânica e a 120 °C por 1h indicaram as melhores características físico-mecânicas, além de incremento satisfatório de grupos apolares com o tratamento. Resumo em inglês The use of vegetable fibers in composites is highly viable regarding about the use of materials from renewable sources, the biodegradability and the socioeconomic advantages in the production of raw vegetable. The sisal fibers are highly hygroscopic and this is a main problem in the production of composites, inducing dimensional changes under moisture influence, deposition of the matrix products and degradation. The treatment of the acetylation was applied at different te (mais) mperatures and reaction times, and the efficiency of treatments, considering the reduction of the hydrophilicity and maintenance of the mechanical properties, was evaluated by water sorption, mechanical properties and the infrared spectroscopy. With acetylation the fibers had weight reductions for water sorption up to 50% compared to untreated. The treatments for 3 h decreased the mechanical properties while the 120 °C for 1 h showed better physico-mechanical properties and increase of apolar groups.

Scientific Electronic Library Online (Portuguese)

84

Estudo de misturas asfálticas com ligante modificado pelo polímero EVA para pavimentos urbanos de Manaus - AM/ Study of asphalt mixtures containing a binder modified with EVA polymer for use in urban pavements in Manaus

D'Antona, Daniela M. G.; Frota, Consuelo A. Da
2011-01-01

Resumo em português A presente pesquisa buscou soluções com materiais alternativos visando à construção de pavimentos urbanos para Manaus (AM) com maior vida útil e condizente com as suas condições de serviço, em particular, o seu desempenho mecânico frente às temperaturas regionais. Estudou-se o ligante regional, CAP 50/70, misturado com 4% do polímero EVA, e como partícipe em compósitos asfálticos. A incorporação do mencionado polímero teve como objetivo melhorar suas pro (mais) priedades reológicas e, por conseguinte, o comportamento mecânico desse compósito - concreto asfáltico, empregado como revestimento nas vias urbanas da Capital do Estado do Amazonas. Os ligantes (virgem e modificado) foram caracterizados conforme a especificação da ANP e a metodologia Superpave. As misturas asfálticas foram avaliadas pelo ensaio de fluência por compressão axial, com carregamento dinâmico à temperatura de 40 ºC. O material asfáltico modificado com EVA (AMP EVA) demonstrou melhores propriedades reológicas ou equivalentes ao asfalto convencional (REMAN), ao longo de todos os ensaios de caracterização. As misturas alternativas compostas com o CAP modificado (SEVA) obtiveram desempenho mecânico superior ao de misturas com cimento asfáltico habitualmente comercializado na região (SMAN). Resumo em inglês In this research we investigated alternative materials to build urban pavements in Manaus, seeking for pavements with longer lifetime for usage and suitable mechanical properties to withstand the local temperatures. The asphaltic mixtures contained a regional binder, namely CAP 50/70, mixed with 4% of EVA polymer. The incorporation of the latter polymer was aimed at improving the rheological properties of asphaltic concrete used in roads in the Amazonas' capital. The asph (mais) alt binders (original and modified) were characterized in accordance with the ANP (National Petroleum Agency) specification and the Superpave methodology. The asphalt mixtures had their mechanical properties studied using creep dynamics at 40 ºC. The EVA modified binder (AMP EVA) yielded either better rheological properties or properties equivalent to the conventional asphalt (REMAN) throughout all the characterization experiments. The alternative mixtures composed by the binder modified with 4% EVA (SEVA) had superior mechanical performance compared to mixtures made up with the binder commonly commercialized in the region (SMAN).

Scientific Electronic Library Online (Portuguese)

85

Estudo das propriedades e biodegradabilidade de blendas de poliéster/amido submetidas ao ataque microbiano/ Study of the properties and biodegradability of polyester/starch blends submitted to microbial attack

Vinhas, Glória M.; Almeida, Yêda M. B. de; Lima, Maria Alice Gomes de Andrade; Santos, Lívia Almeida
2007-01-01

Resumo em inglês This work deals with the biodegradation of blends of poly(beta-hydroxybutyrate)/starch and poly(beta-hydroxybutyrate-co-hydroxyvalerate)/starch. The blends were obtained by evaporation of the solvent in the mixture of the polymers in chloroform. Tests were carried out in presence of micro-organisms which acted as biodegradation agents. The blends were consumed as carbon substrate and the production of CO2 was evaluated in the process. In addition, the polyesters' mechanic (mais) al properties were reduced by the incorporation of starch in its structure. (¹H) NMR and infrared spectroscopy detected some characteristic polyester degradation groups in the polyesters' chemical structure, thus confirming the alteration suffered by it.

Scientific Electronic Library Online (Portuguese)

86

Estudo da influência de tratamentos químicos da fibra de sisal nas propriedades de compósitos com borracha nitrílica/ Study of the influence from chemical treatments of sisal fibers on the properties of composites with nitrile rubber

Iozzi, Marco A.; Martins, Gilson S.; Martins, Maria A.; Ferreira, Fábio C.; Job, Aldo E.; Mattoso, Luiz H. C.
2010-01-01

Resumo em português A influência de diferentes tratamentos das fibras de sisal nas propriedades dos compósitos de borracha nitrílica/fibras de sisal, e borracha nitrílica/carbonato de cálcio/fibras de sisal foi investigada. Os compósitos, com fibras curtas aleatoriamente distribuídas, foram processados em moinho de dois rolos e caracterizados através de ensaios mecânicos de resistência à tração, microscopia eletrônica de varredura (MEV), análise por termogravimetria (TG) e cal (mais) orimetria exploratória diferencial (DSC). O tratamento de mercerização das fibras levou a uma maior adesão na interface fibra/matriz. O uso combinado de 67 pcr de carbonato com 33 pcr de fibras de sisal mercerizadas produziu um compósito com aumento significativo no módulo de elasticidade e sem perda da resistência à tração de ruptura. Os resultados da análise térmica mostraram que os compósitos são termicamente estáveis até cerca de 300 °C. Os materiais obtidos possuem uma boa relação custo/benefício tornando promissora sua utilização. Resumo em inglês In this work, composites were produced with nitrile rubber and sisal fibers, and nitrile rubber with calcium carbonate and sisal fibers. The composites were processed on a two-roll mixing mill and their properties were investigated with regard to the influence of chemical treatments of the fibers. The composites, with short fibers randomly distributed, were characterized by mechanical analysis, scanning electron microscopy (SEM), thermogravimetric analysis (TGA) and diffe (mais) rential scanning calorimetry (DSC). Mercerization treatment of the fibers promoted increasing the adhesion between the fiber and the rubber matrix. The composites of nitrile rubber with 67 pcr of calcium carbonate and 33 pcr of mercerized sisal fibers showed the best mechanical properties. Thermal analysis demonstrated that the composites are thermally stable up to 300 °C. The materials developed have a good cost/benefit relationship making their utilization promising.

Scientific Electronic Library Online (Portuguese)

87

Estrutura e propriedades de elipticinas/ Structure and properties of ellipticines

Cirino, José J. V.; Belletato, Paulo; Dantas, Sócrates de O.; Ribeiro, Lucicleide; Ferreira, Gilson R.; Santos, Hélio F. dos
2005-02-01

Resumo em inglês The ellipticines constitute a broad class of molecules with antitumor activity. In the present work we analyzed the structure and properties of a series of ellipticine derivatives in the gas phase and in solution using quantum mechanical and Monte Carlo methods. The results showed a good correlation between the solvation energies in water obtained with the continuum model and the Monte Carlo simulation. Molecular descriptors were considered in the development of QSAR mode (mais) ls using the DNA association constant (log Kapp) as biological data. The results showed that the DNA binding is dominated by electronic parameters, with small contributions from the molecular volume and area.

Scientific Electronic Library Online (Portuguese)

88

Eficiência da escarificação mecânica e biológica na melhoria dos atributos físicos de um latossolo muito argiloso e no incremento do rendimento de soja/ Efficiency of mechanical and biological chiseling in the improvement of physical attributes of a heavy clay oxisol and the increment of soybean yield

Nicoloso, Rodrigo da Silveira; Amado, Telmo Jorge Carneiro; Schneider, Sérgio; Lanzanova, Mastrângello Enívar; Girardello, Vitor Cauduro; Bragagnolo, Jardes
2008-08-01

Resumo em português A compactação é uma das principais causas de decréscimo da produtividade dos solos agrícolas. A escarificação mecânica tem sido sugerida para reduzir a compactação do solo em áreas sob sistema de semeadura direta consolidada. Outra opção para aliviar a compactação é o uso de plantas de cobertura com sistema radicular pivotante e bem desenvolvido, como o nabo-forrageiro, com capacidade de crescer em camadas compactadas, formar bioporos estáveis e melhorar (mais) os atributos físicos do solo. O objetivo deste trabalho foi avaliar a eficiência do método mecânico (escarificador) e do método biológico (nabo-forrageiro) de descompactação do solo, ou de ambos associados, em promover a melhoria dos atributos físicos de um Latossolo de textura muito argilosa e o rendimento de grãos da cultura da soja manejada sob semeadura direta. Os tratamentos utilizados foram: aveia-preta em semeadura direta (SD-Av), consórcio de nabo-forrageiro e aveia-preta em semeadura direta (SD-Nb+Av), aveia-preta em solo escarificado (ESC-Av) e consórcio de nabo-forrageiro e aveia-preta em solo escarificado (ESC-Nb+Av). Foram avaliadas a densidade, macroporosidade, microporosidade e porosidade total do solo nas camadas 0-0,05; 0,05-0,10; 0,10-0,15; e 0,15-0,20 m, resistência do solo à penetração, umidade gravimétrica e infiltração de água no solo, no momento do pleno florescimento da soja. Além disso, foram determinadas a produção de matéria seca das plantas de cobertura de solo de inverno e o rendimento de soja no verão. Os tratamentos não afetaram significativamente a densidade do solo em nenhuma das camadas avaliadas, no entanto os tratamentos SD-Nb+Av e ESC-Nb+Av duplicaram os valores de macroporosidade do solo na média da camada 0-0,20 m, com efeitos mais pronunciados nas camadas mais superficiais do solo. Os tratamentos SD-Nb+Av e ESC-Nb+Av reduziram a resistência do solo à penetração em relação ao tratamento SD-Av, enquanto o tratamento ESC-Av teve comportamento intermediário. Os tratamentos SD-Nb+Av e ESC-Nb+Av aumentaram, em média, 46,6 % a lâmina de água infiltrada em relação aos tratamentos SD-Av e ESC-Av. O maior rendimento de grãos de soja foi observado no tratamento ESC-Nb+Av (3,73 Mg ha-1), que não diferiu significativamente do SD-Nb+Av (3,49 Mg ha-1). A escarificação mecânica do solo teve efeito temporário, e não foram constatadas melhores condições físicas do solo após nove meses, com exceção do aumento da porosidade total e macroporosidade do solo na camada 0-0,05 m. Por outro lado, a escarificação biológica aumentou a macroporosidade do solo, diminuiu sua resistência à penetração e melhorou a infiltração de água. A escarificação mecânica foi uma alternativa eficiente em melhorar as condições físicas do Latossolo textura muito argilosa quando associada à escarificação biológica, que preveniu a reconsolidação do solo. Resumo em inglês Compaction is one of the main causes of yield decreases in agricultural soils. Mechanical chiseling has been suggested to reduce soil compaction in long-term no-tillage systems. Another option to alleviate soil compaction is the use of cover crops, such as forage radish, with a well-developed tap root system and the capacity of growing into soil compacted layers, forming stable biopores and improving the soil physical properties. This study aimed to evaluate the efficienc (mais) y of a mechanical (chisel plow) and biological (forage radish) soil decompaction method or the combination of both to improve the physical properties of a very clayey texture Oxisol and to increase soybean grain yield under no-tillage. The treatments were: black oat on no-till (NT-O), consortium of forage radish and black oat on no-till (NT-R+O), black oat on chiseled soil (CH-O) and consortium of forage radish and black oat on chiseled soil (CH-R+O). The following properties were evaluated: soil bulk density, macroporosity, microporosity and total porosity in the layers 0-0.05, 0.05-0.10, 0.10-0.15 and 0.15-0.20 m, soil penetration resistance, soil moisture and soil water infiltration at soybean flowering. The winter cover biomass production and soybean yield were also measured. The treatments did not affect the soil bulk density significantly at any of the soil depths. However, the treatments NT-R+O and CH-R+O doubled the mean soil macroporosity values in the 0-0.20 m layer, with more pronounced effects in the upper soil layers. The treatments NT-R+O and CH-R+O reduced soil penetration resistance compared to NT+O, while treatment CH-O had intermediate results. The treatments NT-R+O and CH-R+O increased the accumulated infiltrated water by 44.6 as compared to treatments NT-O and CH-O .The highest soybean yields were observed in the treatment CH-R+O (3.73 Mg ha-1), which did not differ significantly from treatment NT-R+O (3.49 Mg ha-1). The effect of winter mechanical chiseling was temporary and nine months later no soil physical improvements were observed, apart from the increase of total porosity and macroporosity in the 0-0.05 m layer. Biological chiseling increased soil macroporosity, reduced soil penetration resistance and improved soil water infiltration. Mechanical chiseling was only efficient to improve the soil physical conditions when associated with biological chiseling, which prevented soil reconsolidation.

Scientific Electronic Library Online (Portuguese)

89

Efeitos da incorporação de peneiras moleculares 3A, 4A, 5A e 13X em membranas compósitas de quitosana/poli(vinil álcool)/ Effect of molecular sieves 3A, 4A, 5A and 13X incorporation on the chitosan/poly(vinyl alcohol) composites membranes

Vicentini, Denice Schulz; Lima, João Cardoso de; Laranjeira, Mauro Cesar Marghetti
2010-01-01

Resumo em inglês The composite membranes prepared via incorporation of 12.5% of molecular sieves 3A, 4A, 5A and 13X into chitosan/poly(vinyl alcohol) (1:1). The composite membranes were immersed in the cross-linker sulfuric acid in order to acquire high proton conductivity for applications in electrolytes in PEMCF and DMF. The influence of the molecular sieves on the structural, optical, thermal, mechanical, morphologic and protonic conductivity properties and water/methanol swelling degree of membranes were investigated.

Scientific Electronic Library Online (Portuguese)

90

Determinação de diagramas de bandas de energia e da borda de absorção em SnO2, depositado via sol-gel, sobre quartzo/ Determination of the band energy diagram and absorption fundamental edge in SnO2, deposited via sol-gel, on quartz

Floriano, E. A.; Scalvi, L. V. A.; Sambrano, J. R.
2009-03-01

Resumo em português Propriedades ópticas e estruturais de filmes finos de SnO2, depositados sobre substratos de quartzo, são apresentadas. Os filmes são preparados pela técnica de molhamento via sol-gel. Uma avaliação das propriedades eletrônicas do cristal (bulk) e das superfícies (110) e (101) do material é também efetuada, através de cálculos baseados em um método mecânico-quântico que utiliza a Teoria do Funcional da Densidade (DFT) em conjunto com o funcional hibrido B3LY (mais) P. A borda fundamental de absorção, obtida experimentalmente, é então comparada com os diagramas de bandas de energia do bulk e superfícies (110) e (101), calculadas. Resumo em inglês Optical and structural properties of SnO2 thin films, deposited on quartz substrates, are presented. Films are prepared by the sol-gel-dip-coating technique. An evaluation of the electronic properties of bulk and surfaces (110) and (101) of the material is also carried out, through calculation based on a quantum-mechanical method using the Density Functional Theory (DFT) in conjunction with the hybrid functional B3LYP. The absorption fundamental edge, experimentally obtained, is compared to the calculated band energy diagram of bulk and surfaces (110) and (101).

Scientific Electronic Library Online (Portuguese)

91

Desenvolvimento, caracterização e aplicação eletroanalítica de um compósito fluido de adesivo epóxi, grafite e ciclo-hexanona/ Development, characterization and electroanalytical application of a fluid composite made of epoxy adhesive, graphite, and ciclohexanone

Silva, Rodrigo Amorim Bezerra da; Rabelo, Adriano César; Bottecchia, Otávio Luiz; Muñoz, Rodrigo Alejandro Abarza; Richter, Eduardo Mathias
2010-01-01

Resumo em inglês A fluid conducting composite material prepared from graphite powder, commercial epoxy resin Araldite®, and cyclohexanone has been developed. The composition was optimized considering the mechanical properties as conductivity and adhesiveness using response surface methodology. This work employed cyclic voltammetry and amperometry to investigate the characteristics of such composite electrodes without and with the insertion of Prussian blue in the electrode body (bulk mod (mais) ified electrode). The composite electrodes were also successfully used for the amperometric detection of hydrogen peroxide at 0.0V vs Ag/AgCl.

Scientific Electronic Library Online (Portuguese)

92

Controle de tráfego agrícola e atributos físicos do solo em área cultivada com cana-de-açúcar/ Agricultural traffic control and soil physical attributes in sugarcane areas

Roque, Antoniane Arantes de Oliveira; Souza, Zigomar Menezes de; Barbosa, Ronny Sobreira; Souza, Gustavo Soares de
2010-07-01

Resumo em português O objetivo deste trabalho foi avaliar o efeito do controle de tráfego agrícola na compactação do solo em áreas cultivadas com cana-de-açúcar no sistema de colheita mecanizada. O trabalho foi realizado em delineamento de blocos ao acaso, em parcelas subsubdivididas com os tratamentos: colheita mecanizada tradicional; corte mecanizado com controle de tráfego; e corte mecanizado com controle de tráfego e uso do piloto automático. Os atributos físicos do solo foram (mais) avaliados nas camadas de 0,0-0,1, 0,1-0,2 e 0,2-0,3 m de profundidade, na linha de plantio, no local em que o rodado passa e no entrerrodado. Avaliaram-se também os efeitos desses tratamentos sobre a produtividade da cana-de-açucar, respectivamente. O tráfego das máquinas agrícolas aumenta a densidade do solo e diminui o diâmetro médio ponderado dos agregados e a macroporosidade na linha de rodado em relação à linha de plantio, o que causa a degradação cumulativa da qualidade física do solo, ao longo dos anos de cultivo. Os dois anos de controle de tráfego agrícola da colheita não influenciaram os atributos físicos do solo estudados. Resumo em inglês The objective of this work was to evaluate the effect of traffic control on soil compaction in sugarcane areas with mechanical harvesting system. The study was carried out in a randomized complete block design in a split plot arrangement, with the following treatments: traditional mechanical harvesting, mechanical harvesting with traffic control, mechanical harvesting with traffic control and automatic tractor guidance. Soil physical properties were assessed at 0.0-0.1, 0 (mais) .1-0.2 and 0.2-0.3-m depths, at the planting row, at the wheel tracks, and between wheel tracks. The effects of these treaments on sugarcane yield were evaluated, respectively, too. Agricultural traffic increases soil density, and reduces aggregate mean geometric diameters and macroporosity at the wheel tracks in comparison to the planting row, which leads to cumulative soil physical quality degradation throughout the years. The two years of agricultural traffic control did not influence the studied soil physical attributes.

Scientific Electronic Library Online (Portuguese)

93

Comportamento dinâmico-mecânico e relaxações em polímeros e blendas poliméricas/ Dynamic mechanical behavior and relaxations in polymers and polymeric blends

Cassu, Silvana Navarro; Felisberti, Maria Isabel
2005-03-01

Resumo em inglês Dynamic mechanical analysis (DMA) is widely used in materials characterization. In this work, we briefly introduce the main concepts related to this technique such as, linear and non-linear viscoelasticity, relaxation time, response of material when it is submitted to a sinusoidal or other periodic stress. Moreover, the main applications of this technique in polymers and polymer blends are also presented. The discussion includes: phase behavior, crystallization; spectrum (mais) of relaxation as a function of frequency or temperature; correlation between the material damping and its acoustic and mechanical properties.

Scientific Electronic Library Online (Portuguese)

94

Blends of poly(hydroxybutyrate) and poly (epsilon-caprolactone) obtained from melting mixture

Antunes, Maria Cecília M.; Felisberti, Maria Isabel
2005-06-01

Resumo em inglês Poly(3-hydroxybutyrate) (PHB) is a thermoplastic polyester with a great potential owing to its biodegradability, bioreabsorbation and biological synthesis from a renewable source. Despite these characteristics, the applications of this polymer are very restricted due to its poor mechanical properties and thermal instability at temperatures above its melting point (around 175°C). Among the possibilities of improvement of these materials, the development of blends is a rel (mais) atively fast and inexpensive option. Poly(epsilon-caprolactone) (PCL) is a semi-crystalline polymer that may be used as a biomaterial. It presents good mechanical properties, a low melting point (around 55 °C), and could be a good option to develop PHB blends, maintaining the biodegradability and bioreabsorption properties. The objective of the present work was to obtain blends of PHB and PCL by melting mixture in an internal mixer. The compositions varied from 0 to 30 wt% of PCL. DSC, DMA, and SEM were used to characterize the blends. The blends were found to be imiscible with no indication of interaction either the amorphous or crystalline state. The morphology shows PHB as the matrix and PCL as the dispersed phase.

Scientific Electronic Library Online (Portuguese)

95

Blendas de PHB e seus copolímeros: miscibilidade e compatibilidade/ Blends of PHB and its copolymers: miscibility and compatibility

Quental, Antonio Carlos; Carvalho, Fabiana Pires de; Tada, Eduardo dos Santos; Felisberti, Maria Isabel
2010-01-01

Resumo em inglês Poly(hydroxybutyrate) and its copolymers are linear polyesters behaving as conventional thermoplastic materials. However, they are totally biodegradable and produced by a wide variety of bacteria from renewable sources. Some properties and high production cost are still preventing future applications. In an attempt to improve the properties and to reduce cost blending PHB with others polymeric materials is one of the most efficient method. In this paper, miscibility, comp (mais) atibility, morphological and mechanical aspects of PHB blends will be reviewed. An extensive revision over twenty last years was realized about works of blends based on PHB and its copolymers.

Scientific Electronic Library Online (Portuguese)

96

Avaliação da fotodegradação de poliolefinas através de exposição natural e artificial/ The evaluation of polyolefin photodegradation with natural and artificial exposure

Fechine, Guilhermino José Macêdo; Santos, João Antônio Belmino dos; Rabello, Marcelo Silveira
2006-07-01

Resumo em inglês Samples of polypropylene (PP) and low-density polyethylene (LDPE) were submitted to ultraviolet radiation, in the natural environment and also in the laboratory. Chemical modifications were quantified by the carbonyl index (CI), mechanical properties and melt flow index. The degradation in the laboratory was comparatively faster than in the environment for both types of polymers. The accelerating factor was determined for the various properties investigated. This paramete (mais) r, however, showed a large variation with the degradation criteria and the type of polymer. The existence of a "universal accelerating factor", therefore, was not observed in the current study.

Scientific Electronic Library Online (Portuguese)

97

Atributos químicos do solo e produtividade de videiras alterados pelo manejo de coberturas verdes na Serra Gaúcha/ Soil chemical properties and grapevine yield affected by cover crop management in Serra Gaucha, Southern Brazil

Rosa, Jaqueline Dalla; Mafra, Álvaro Luiz; Nohatto, Marcos André; Ferreira, Evandro Zacca; Oliveira, Odoni Loris Pereira de; Miquelluti, David José; Cassol, Paulo Cezar; Medeiros, João Carlos
2009-02-01

Resumo em português O manejo do solo pode interferir na disponibilidade de nutrientes e na produtividade de frutos. O objetivo deste estudo foi avaliar o efeito de formas de manejo da fitomassa de diferentes espécies de plantas de cobertura verde sobre características químicas do solo, relacionadas à matéria orgânica e à disponibilidade de nutrientes, e sobre a produtividade de uva. O experimento foi realizado na Embrapa Uva e Vinho, em Bento Gonçalves, RS, sobre um Cambissolo Hápli (mais) co, num parreiral implantado em 1989, com os cultivares Niágara Branca e Niágara Rosada, no sistema de latada. Os tratamentos testados foram implantados em 2002 e consistiram em três coberturas vegetais: vegetação espontânea, aveia-preta e consórcio de trevo-branco + trevo-vermelho + azevém; e dois sistemas de manejo: dessecado com herbicida e roçado, os quais foram realizados no outono, previamente à ressemeadura das espécies. O delineamento experimental foi de blocos ao acaso com três repetições. Os atributos químicos indicadores da acidez e da disponibilidade de nutrientes no solo foram pouco influenciados pelas espécies de cobertura. A dessecação das plantas aumentou os teores de Ca e Mg trocáveis, P disponível e C orgânico total em relação ao manejo roçado. A produtividade de uva nas safras de 2004 e 2006 foi baixa em relação ao potencial dos cultivares, possivelmente por restrições climáticas, contudo foi maior quando se utilizou a aveia como planta de cobertura do que com o consórcio de plantas. Resumo em inglês Soil management can have effects on nutrient availability and fruit yield. The objective of this study was to evaluate the effect of phytomass management forms of different cover crop species on soil chemical properties related to organic matter, nutrient availability, and on grapevine yields. The experiment was carried out in Embrapa Uva e Vinho, in Bento Gonçalves, RS, in Southern Brazil, on a Haplic Cambissol, in a vineyard established in 1989, using White and Rose Ni (mais) agara grape in a horizontal overhead trelling system. The treatments established in 2002 were three cover crops: spontaneous native species, black oat (Avena strigosa), and a mixture of white clover (Trifolium repens) + red clover (Trifolium pratense) + annual ryegrass (Lolium multiflorum); and two management systems: desiccation by herbicide spraying and mechanical mowing, performed each autumn prior to cover crop resowing. The experiment had a completely randomized block design, with three replications. Soil acidity and nutrient contents were little influenced by the plant cover. In comparison with the mowed management, herbicide application increased exchangeable Ca and Mg, extracted P, and organic C levels in the soil. The grape yield in the seasons 2004 and 2006 was low in view to the cultivar potential, probably affect by climatic limitations, but was higher when black oat was used as plant cover instead of the mixture of plant covers.

Scientific Electronic Library Online (Portuguese)

98

Atributos físicos e químicos de um latossolo vermelho-amarelo sob pastagens com diferentes históricos de uso/ Physical and chemical properties of an oxisol cultivated under pastures with distinct use history

Netto, Iara Terezinha Pignataro; Kato, Eiyti; Goedert, Wenceslau J.
2009-10-01

Resumo em português O uso sustentável dos sistemas de pastagens depende, principalmente, de um manejo que possa promover a qualidade do solo. O objetivo deste estudo foi avaliar as alterações nos atributos físicos e químicos do solo sob quatro pastagens, formadas com as espécies Andropogon gayanus, Brachiaria decumbens e Brachiaria brizantha cv. marandu, com diferentes históricos de uso, empregando como referência o Cerrado nativo. O solo foi avaliado pela quantificação dos seguint (mais) es atributos: capacidade de troca de cátions, matéria orgânica, densidade do solo, porosidade total e resistência mecânica à penetração. A capacidade de troca de cátions e o teor de matéria orgânica mostraram-se pouco afetados pelo manejo e pelo tempo de uso. A densidade do solo, a porosidade total e a resistência mecânica à penetração foram bastante afetadas, tendo grande influência na redução da qualidade do solo. Quantidade grande de animais, uso de máquinas e implementos, e cobertura deficiente, ocasionada pelo manejo inadequado, foram os principais fatores que promoveram as alterações no solo. O índice de qualidade do solo mostrou uma sequência decrescente, 0,83, 0,62, 0,51 e 0,23, respectivamente, para as áreas sob Andropogon gayanus (AN), Andropogon gayanus (AV), Brachiaria brizantha (BN) e Brachiaria decumbens (BV). Resumo em inglês The sustainable use of pasture systems depends mainly on a management that promotes soil quality. This study aimed to evaluate changes in the physical and chemical soil properties of four areas under pasture growing the species Andropogon gayanus, Brachiaria decumbens and Brachiaria brizantha, cv. marandu, with different usage histories, in comparison to the reference of the natural Cerrado. The soil was evaluated based on the following properties: cation exchange capacit (mais) y, soil organic matter, bulk density, porosity and soil mechanical penetration resistance. The cation exchange capacity and soil organic matter content were little affected by the management and by usage time. Bulk density, total porosity and soil mechanical penetration resistance were highly affected, with a strong influence on soil quality reduction. The factors high animal load, use of agricultural machines and implements, and deficient groundcover caused by inefficient management were mainly responsible for the soil alterations. The soil quality index showed a decreasing sequence (0.83, 0.62, 0.51 and 0.23, respectively) for the areas under Andropogon gayanus (AN), Andropogon gayanus (AV), Brachiaria brizantha (BN) and Brachiaria decumbens (BV).

Scientific Electronic Library Online (Portuguese)

99

Análise conformacional de modelos de lignina/ Conformational analysis of lignin models

Dos Santos, Hélio F.
2001-08-01

Resumo em inglês The conformational equilibrium for two 5,5' biphenyl lignin models have been analyzed using a quantum mechanical semiempirical method. The gas phase and solution structures are discussed based on the NMR and X-ray experimental data. The results obtained showed that the observed conformations are solvent-dependent, being the geometries and the thermodynamic properties correlated with the experimental information. This study shows how a systematic theoretical conformational analysis can help to understand chemical processes at a molecular level.

Scientific Electronic Library Online (Portuguese)

101

Propriedades eletrônicas, estruturais e constantes elásticas do ZnO/ Structural, electronic properties and elastic constants of ZnO

Marana, Naiara Letícia; Sambrano, Julio Ricardo; Souza, Aguinaldo Robinson de
2010-01-01

Resumo em inglês The electronic, structural properties and elastic constants of the wurtzite phase of zinc oxide, ZnO, was investigated using computer simulation at Density Functional Theory level, with B3LYP hybrid functional and Hartree-Fock methodology. The electronic properties as well the band energy was investigated through the analysis of the band structures and density of states (DOS), and the mechanical properties was studied through the calculus of the elastic constants C11, C33 (mais) , C44, C12 e C13. The results are in good agreement with experimental data found in the literature and in accordance with results obtained by another theoretical methodology.

Scientific Electronic Library Online (Portuguese)

102

Propriedades de chapas fabricadas com partículas de madeira de paricá (Schyzolobium amazonicum Huber ex. Ducke) e fibras de coco (Cocos nucifera L.)/ Properties of particleboards made of paricá (Schyzolobium amazonicum Huber ex. Ducke) particles and coconut (Cocus nucifera L.) fibers

Colli, Andrea; Vital, Benedito Rocha; Carneiro, Angêlica de Cássia Oliveira; Silva, José de Castro; Carvalho, Ana Márcia Macedo Ladeira; Lucia, Ricardo Marius Della
2010-04-01

Resumo em português Este trabalho teve como objetivo determinar as propriedades de chapas fabricadas com partículas de madeira de paricá (Schyzolobium amazonicum Huber ex. Ducke), às quais foram adicionadas diferentes proporções de fibras de coco (Cocos nucifera L.). As chapas foram fabricadas com 6 ou 8% de adesivo, à base de ureia-formaldeído e tendo como meta uma massa específica de 360 kg/m³. Observou-se que a adição de fibras de coco não afetou a estabilidade dimensional, hi (mais) groscopicidade e absorção de água, porém aumentou significativamente as demais propriedades. As chapas fabricadas com 8% de adesivo foram mais estáveis e mais resistentes do que aquelas feitas com 6% de adesivo. Resumo em inglês This work had as its objective to determine the properties of particleboards fabricated with paricá particles (Schyzolobium amazonicum Huber ex. Ducke), with increasing proportions of coconut fibers (Coconuts nucifera L.). Boards were fabricated with 6 or 8% of urea-formaldehyde adhesive. Particleboard mean density was equal to 360 kg/m³. The addition of coconut fibers didn't affected boards' dimensional stability, higrospicidity, water absorption capability. However it increased its mechanical properties. The addition of 8% of adhesive improved all board properties.