Efeito de um resíduo do processo de galvanoplastia sobre a vulcanização da borracha natural (NR)/ Effect from the waste from the electroplating process on the natural rubber (NR) vulcanization

Santos, Alex C. S.; Costa, Helson M. da; Ramos, Valéria D.
2009-01-01

Resumo em português Um resíduo gerado no processo de galvanoplastia (RG), rico em metais, foi incorporado em composições de borracha natural (NR) em substituição parcial ou total ao ativador comum do processo de vulcanização, o óxido de zinco (ZnO). As diferentes misturas foram preparadas em um misturador de calandras e, após a reometria, foram vulcanizadas a 150 °C. As propriedades mecânicas de resistência à tração e rasgo foram determinadas, além do teor de gel. Além dis (mais) so, o efeito do resíduo RG sobre a cinética de vulcanização foi analisado através do modelo de Coran, usando-se as temperaturas de 150, 160 e 170 °C. Os resultados mostraram que RG desenvolve algum efeito catalítico sobre a vulcanização de NR, embora exista uma considerável perda na resistência à tração quando o teor de RG excede o do ZnO nas composições. Quanto ao rasgo, a propriedade é mantida em um patamar satisfatório enquanto teores menores de RG são utilizados. Resumo em inglês A waste generated in the electroplating process (RG), rich in metals, was incorporated in natural rubber (NR) compositions, as a partial or complete replacement of zinc oxide (ZnO), which is a typical activator of the vulcanization process. Different mixtures were prepared in a two-roll mixer, which were vulcanized at 150 ºC after the rheometry measurements. Mechanical properties such as tensile and tear strength were evaluated, as well as the gel content. In addition, t (mais) he effect of RG waste upon the vulcanization kinetics was analyzed with the Coran model using temperatures at 150, 160 and 170 ºC. The results showed that RG develops some catalytic effect upon NR vulcanization, but there is a poor mechanical performance when RG loading is higher than that of ZnO in the compositions. For the tear strength, the property is maintained at a reasonable level if a small RG loading is utilized.

Scientific Electronic Library Online (Portuguese)

2

Eletrorrecuperação de cobre e oxidação de cianeto de efluentes cianídricos diluídos gerados por unidade de galvanoplastia/ Copper electrowinning and cyanide oxidation from diluted cyanide wastewaters generated by an electroplating plant

Pombo, F.R.; Dutra, A.J.B.
2008-09-01

Resumo em português Apesar de sua elevada toxicidade, eletrólitos cianídricos são amplamente empregados pelas indústrias de eletrorrecobrimento devido à qualidade dos depósitos metálicos obtidos. Na Casa da Moeda do Brasil, o processo de eletrodeposição de cobre sobre aço carbono é utilizado para a fabricação das moedas de um e cinco centavos, gerando, ao seu final, dois tipos de efluentes: um concentrado, após a sangria de eletrólitos contaminados; e outro diluído, após a l (mais) avagem dos discos eletrorrevestidos de cobre. Em um trabalho anterior, avaliou-se a possibilidade de se recuperar eletroliticamente o cobre e oxidar parte do cianeto existente nos efluentes concentrados, alcançando-se bons resultados para os teores finais de cobre e cianeto livre partindo-se de uma solução contendo 26g/L de cobre e 27g/L de cianeto total. O presente trabalho visou testar em escala de bancada uma célula eletrolítica para o tratamento dos efluentes diluídos, partindo-se de uma solução sintética contendo 200mg/L de cobre e 130mg/L de cianeto livre. Nas condições de vazão de 0,37mL/s e a 50º C, alcançou-se concentrações finais de 0,7mg/L de cobre e 0,08mg/L de cianeto livre para uma corrente elétrica de 1,5A, e menor que 0,5mg/L de cobre e 0,08mg/L de cianeto livre para uma corrente elétrica de 2A, após três horas de eletrólise. Resumo em inglês Despite their high toxicity, cyanide electrolytes are widely used by metal finishing industries due to the quality of metallic deposits obtained. At the Brazilian Mint, the process of copper electroplating onto carbon steel is used to make coins of one and five cents, generating, at the end, two types of wastewaters: one concentrated, after bleeding the contaminated electrolytes; and another diluted, after washing the disks electroplated with copper. In a previous work th (mais) e possibility of electrolytically recovering copper and oxidizing part of the existing cyanide in the concentrated effluents was evaluated, reaching good results for the final concentration of copper and free cyanide starting with a solution containing 26g/L of copper and 27g/L of total cyanide. The present work aimed at testing in a bench scale an electrolytic cell for the treatment of diluted effluents, starting from a synthetic solution containing 200 mg/L of copper and 130 mg/L of free cyanide. Under flow conditions of 0.37mL/s at 50°C, the final concentrations of 0.7mg/L for copper and 0.08mg/L for free cyanide were obtained for an electric current of 1.5A, and less than 0.5mg/L for copper and 0.08mg/L for free cyanide were obtained for an electric current of 2A, after three hours of electrolysis.

Scientific Electronic Library Online (Portuguese)

3

Estudo de camadas eletrodepositadas a partir de soluções livres de cianeto/ Study of coatings electrodeposited from free cyanide solutions

Casagrande, Delci Fátima M.; Oliveira, Cláudia Trindade; Malfatti, Célia F.; Veit, Hugo M.
2010-06-01

Resumo em português As indústrias galvânicas utilizam, durante o seu processo produtivo, vários tipos de soluções químicas, além de água, que, após o seu ciclo de vida, devem ser descartadas. Entre esses insumos, está o cianeto cúprico, que é tóxico ao ser humano e ao meio ambiente e que está presente em vários tipos de revestimentos nos quais uma camada de cobre é necessária. Esse estudo tem a finalidade de comparar revestimentos eletrodepositados a partir de soluções com (mais) cianetos e livres de cianetos, avaliando a qualidade do tratamento superficial de peças. Dessa forma, buscou-se produzir um revestimento com as mesmas qualidades de peças produzidas pelo processo tradicional. Nesse trabalho, foram utilizadas soluções tradicionais com 25 g.L-1 de cianeto e uma solução alternativa isenta de cianeto. As peças revestidas eram de zamak (liga de zinco com alumínio). Para avaliar a qualidade do revestimento obtido foram realizados ensaios acelerados de corrosão, dureza, comparação de espessura e morfologia da camada eletrodepositada. Os primeiros vestígios de corrosão foram verificados após 432 horas nos corpos de prova tradicionais e 1032 horas nos corpos-de-prova produzidos sem cianeto. Nos ensaios de dureza, obteve-se um pequeno ganho de dureza nas peças sem cianeto. A espessura da camada eletrodepositada, assim como a morfologia, foi similar para os dois tipos de processos. Os resultados obtidos demonstram a viabilidade técnica da utilização de soluções livres de cianeto na galvanoplastia. Resumo em inglês The electroplating industries use in their productive process several types of chemical solutions, besides water, which after their life cycle must be discarded. Among them, there is cupric cyanide, which is highly toxic for humans and the environment, and it is present in many coatings where the copper layer is necessary. This study aims to compare coatings electrodeposited from solutions with cyanide and free cyanide, with those produced by the traditional process. This (mais) comparison involved parts and components of the same quality. In this study, traditional solutions with 25 g.L-1 of cyanide and an alternative solution with 0,015 mg.L-1 of cyanide were used. The parts were produced with Zamak (alloy of Zinc and Aluminum). In order to evaluate the quality of the coating, tests of accelerated corrosion, hardness, comparison of thickness and morphology of the electroplated layer were carried out. The first corrosion traces were detected after 432 hours in the traditional samples and 1032 hours in the free cyanide samples. In hardness tests, there was a better result for the free cyanide samples. The electroplated layer thickness and morphology was similar in both processes. The study results showed that there is technical feasibility in using free cyanide solutions in the electroplating sector.

Scientific Electronic Library Online (Portuguese)

4

Recuperação de cobre eletrolítico a partir de solução gasta de cubas de eletrodeposição em meio cianídrico/ Electrolitic copper recovery from cyanide spent electroplating solutions

Dutra, Achilles Junqueira Bourdot; Rocha, Genilda Pressato da; Pombo, Felipe Ramalho
2007-01-01

Resumo em português Eletrólitos cianídricos, apesar de sua alta toxicidade, são amplamente empregados pelas indústrias de eletrorrecobrimento devido à qualidade dos depósitos metálicos obtidos. No caso dos depósitos de cobre sobre aço-carbono, após algum tempo de operação contínua, o teor de impurezas, especialmente o de carbonatos alcança valores indesejáveis, prejudicando a qualidade do depósito metálico e tornando, portanto, o banho inadequado. Dessa forma, é gerado um e (mais) fluente denominado sangria que requer tratamento para descarte seguro. Nesse trabalho foi avaliada a possibilidade de se recuperar eletroliticamente o cobre dessa solução de modo a se reutilizar o cobre contido e simultaneamente destruir parte do cianeto, diminuindo a carga tóxica do efluente. Recuperações de cobre em torno de 99,9% e oxidação de 99% do cianeto foram obtidas após cinco horas de eletrólise a 50°C com uma densidade de corrente de 9,4A/cm², a partir de um litro de efluente contendo 26g/L de cobre e 27g/L de cianeto total. Resumo em inglês Despite their toxicity, cyanide electrolytes are widely used by electroplating industries due the high quality of the metallic deposits. In the copper deposition on mild steel, after relatively long periods of continuous operation the build up of impurities, especially carbonates, reach undesirable values, decreasing the deposit quality and turning the solution unsuitable for its purpose. Then, a waste solution known as bleed, which requires treatment for a safe discard, (mais) is generated. In this paper, the possibility of simultaneous copper electrowinning and cyanide oxidation from this effluent, decreasing its hazardousness was evaluated. Copper recoveries around 99.9% and oxidation of 99% of the cyanide were achieved, from an effluent containing 26g/L of copper and 27g/L of cyanide after a five-hour electrolysis at 50° C with a current density of 9.4 A/cm².

Scientific Electronic Library Online (Portuguese)

5

O processo eletroquímico como alternativa para o tratamento de efluentes cianídricos

Dutra, Achilles Junqueira Bourdot; Sobral, Luiz Gonzaga Santos; Lemos, Flávio de Almeida; Santos, Fábio Henrique Silva dos
2002-10-01

Resumo em português Embora o cianeto seja um reagente amplamente empregado na lixiviação de metais preciosos e no acabamento superficial de certos metais, sua elevada toxicidade faz com que o uso de tecnologias eficientes no tratamento dos efluentes desses processos seja primordial. Existem diversas técnicas disponíveis para o tratamento de efluentes industriais contendo cianeto, contudo os métodos mais empregados baseiam-se na oxidação química do cianeto a uma espécie menos tóxica (mais) , o cianato, que se hidrolisa produzindo os íons amônio e bicarbonato, além de uma lama contendo hidróxidos de metais pesados, quando presentes no efluente. Entre as técnicas mais recentes para o tratamento de efluentes contendo cianeto, a oxidação eletroquímica apresenta algumas vantagens, como a possibilidade de recuperação dos metais complexados pelo cianeto, além de não necessitar de reagentes químicos adicionais, sendo perfeitamente capaz de atender às exigências dos órgãos ambientais. Esse trabalho apresenta uma comparação entre os diversos processos de tratamento de efluentes contendo cianeto, com ênfase no processo eletroquímico, e também uma revisão sobre estado atual dessa tecnologia. Resumo em inglês Although cyanide is widely employed for leaching precious metals and electroplating certain metals, its high toxicity demands efficient technologies to treat the wastewater generated by these processes. There are a number of available techniques for the treatment of industrial aqueous cyanide-bearing effluents. However, the most employed method is based on its chemical oxidation to the less toxic cyanate which is hydrolyzed to ammonium and bicarbonate ions. The heavy meta (mais) l complexes, when present in the effluent, will form a sludge composed of hydroxides. Among the most recent techniques for the treatment of effluents containing cyanide, electrochemical oxidation presents some advantages, such as: possible metal recovery from the cyano-complexes, no need for further chemicals additions, compliance to environmental agencies directives. This paper presents a comparison among several processes for treating the aforementioned effluents, with emphasis on the electrochemical process, which is briefly reviewed.

Scientific Electronic Library Online (Portuguese)

6

Alternativas de utilização de resíduos sólidos alcalinos na disposição de resíduos contaminados: estudo de caso no estado do Rio de Janeiro, Brasil/ Alkaline residues alternatives for use in the landfill of a contaminated solid residues: case study from Rio de Janeiro, Brazil

Pereira, Wilma de Carvalho; Silva, Dalton Marcondes e; Carvalho, Juremi de Oliveira; Amaral Sobrinho, Nelson Moura Brasil do; Ravelli Neto, Alexandre; Villas Bôas, Roberto Cerrini
2008-06-01

Resumo em português Este trabalho tem como objetivo o estudo dos elementos potencialmente contaminantes presentes nos rejeitos industriais que são dispostos no meio ambiente e, por processo de lixiviação, carreados para os corpos hídricos. Dois tipos de resíduos foram estudados. Um deles, proveniente da indústria de produção de aço (escória da aciaria), de características alcalina. Este rejeito é considerado relativamente estável pelos padrões vigentes devido às suas caracter� (mais) �sticas (Cd Resumo em inglês The goal of this work is to study the potentially contaminating trace elements present in industrial waste that is discharged into the environment though lixiviation process to water resources. Two types of waste were studied. The first one, a refuse slag from steel industry, an alkaline residue. Even though this waste is considered relatively stable within the established standards set by current legislation due to its characteristics (Cd(mais) Kg, Cu=61 mg/Kg, Ni