XPS characterization of porous and sealed anodic films on aluminum alloys

Feliu Jr., S.; Bartolomé, Mª. J.; González, J. A.; Feliu, S.
2007-03-16

Digital.CSIC (Spain)

2

XPS analysis of down stream plasma treated wool: Influence of the nature of the gas on the surface modification of wool

Molina Mansilla, Ricardo; Espinós Manzorro, Juan Pedro; Yubero Valencia, Francisco; Erra Serrabasa, Pilar; González-Elipe, Agustín R.
2005-06-04

Digital.CSIC (Spain)

3

Whiskers in indium tin oxide films obtained by electron beam evaporation

Castañeda, S. I.; Rueda, F.; Díaz, R.; Ripalda, J. María; Montero Herrero, Isabel
1998-02-15

Digital.CSIC (Spain)

5

Síntesis por carbonitruración térmica de nitruros refractarios: Parte 1: nitruro de vanadio

Serrano, Rosevelyn; Díaz, Yraida; Castro, Gustavo; Barrios, Esteban; Albornoz, Alberto; Brito, Joaquín L; Arenas, Freddy
2008-12-01

Resumen en español Se sintetizó nitruro de vanadio (VN) mediante la reducción carbotérmica de mezclas de óxido de vanadio (ex vanadato de amonio) y carbón activado en atmósfera de N2. El método de disolución utilizado para la mezcla de los precursores NH4VO3 y C, permitió obtener VN de morfología uniforme con tamaño de cristalita submicrométrica, a temperaturas inferiores a aquellas utilizadas en procesos convencionales. El producto obtenido fue caracterizado por difracción de (mas) rayos X (DRX), microscopía electrónica de barrido (MEB), espectroscopia de fotoelectrones de rayos X (XPS) y área superficial-BET. Para posible aplicación en catálisis, el producto sintetizado fue evaluado en la hidrodesulfuración (HDS) de tiofeno a presión atmosférica y T = 400°C, encontrándose que la actividad catalítica de los sólidos sintetizados durante 120 min. a 1100ºC fue mayor a aquella de polvos de VN obtenidos con tratamientos térmicos más cortos. Resumen en inglés It has been synthesized vanadium nitride (VN) by carbothermal reduction of vanadium oxide (ex ammonium vanadate) and activated carbon mixtures in a N2 atmosphere. The solution-derived precursor method used to mix NH4VO3 and C promoted the formation of submicrometer and morphologically uniform crystallites of VN at a lower temperature in comparison with conventional methods. The products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-r (mas) ay photoelectron spectroscopy (XPS) and BET-surface area. In order to consider catalytic uses the synthesized product has been evaluated in the reaction of hydrodesulfuration of thiophene under atmospheric pressure and T = 400°C. It was found that the catalytic activity of the heat treated solids during 120 min. at 1100ºC was larger than those of VN powders obtained at shorter heat treatment times.

Scientific Electronic Library Online (Spanish)

6

Síntesis de catalizadores a base de nitruros y carburos de Nb y Mo para la la hidrodesulfuración de tiofeno/ Synthesis of catalysts based on nitrides and cardides of Nb and Mo for thiophene hydrodesulfurization

García, Elizabeth; González, Yolanda; Dìaz, Yraida; Albornoz, Alberto; Brito, Joaquín L
2009-03-01

Resumen en español Se sintetizaron nitruros y carburos de Nb y Mo a presión atmosférica, a partir de los compuestos precursores: Oxalato de niobio y amonio, heptamolibdato de amonio y trióxido de molibdeno. Los nitruros se sintetizaron por amonólisis bajo una atmósfera de NH3 con un flujo 100 ml/min calentando a razón de 3 °C/min en un rango de temperaturas finales de 700-800 °C. Para la síntesis de los carburos se utilizaron dos métodos: el primero tratando los nitruros de Nb y M (mas) o ya sintetizados bajo corriente de 20% CH4 / balance H2 con un flujo de 100 ml/min calentando a razón de 5ºC/min en un rango de temperaturas finales de 700-800ºC; el segundo método consiste de un tratamiento carbotérmico que se realizó sometiendo mezclas mecánicas de los compuestos precursores de Nb o Mo con carbón activado, en relación molar 1:3, a una atmósfera de H2 con un flujo de 100 ml/min y 3 ºC/min hasta temperaturas finales de 700-800°C. Los sólidos obtenidos se caracterizaron por difracción de rayos-X (DRX), medidas de área superficial específica calculada por el método BET (ASE), Espectroscopia Fotoelectrónica de rayos-X (XPS) y finalmente fueron evaluados catalíticamente en la reacción de hidrodesulfuración (HDS) de tiofeno a presión atmosférica y temperatura de 350°C. De los resultados obtenidos por DRX y XPS se concluye que, a las condiciones a las cuales se sintetizaron los catalizadores se obtienen los nitruros y carburos de Nb y Mo excepto para la mezcla mecánica de carbón activado y la sal de niobio; las medidas de ASE mostraron valores en el rango de 10 a 35 m2/g para los carburos y nitruros preparados por nitración y carburación directa y evidenciaron la influencia del carbón activado en las áreas superficiales de los sólidos obtenidos por carboreducción de las mezclas mecánicas, observándose que a mayor área superficial es mayor la actividad del catalizador. De los sólidos sintetizados, los nitruros y carburos de molibdeno resultaron ser los más activos en la reacción de HDS. Resumen en inglés Niobium and molybdenum nitride- and carbide-based catalysts were synthesized from the precursor compounds: ammonium and niobium oxalate, molybdenum heptamolybdate and molybdenum trioxide. Nitrides were prepared by ammonolysis under a NH3 atmosphere with a flow of 100 ml/min, heating at 3 ºC/min up to final temperatures in the 700-800 ºC range. For the carbides synthesis two methods were employed: The first treating the Nb or Mo nitrides previously synthesized under flow (mas) of 100 ml/min of 20% CH4/balance H2 up to a final temperature of 700 or 800 ºC, at a rate of 3 ºC/min. The second method consisted of a carbothermal treatment of mechanical mixtures of the Nb or Mo precursor compounds with activated carbon, in a molar ratio 1:3, under a 100 ml/min flow of H2 and heating at a rate of 3 ºC/min up to 700-800 ºC. The solid products were characterized by X-ray diffraction (XRD), BET specific surface areas (SSA), X-ray photoelectron spectroscopy (XPS) and finally were catalytically evaluated in the hydrodesulfurization (HDS) of thiophene at atmospheric pressure and 350 ºC. From XRD and XPS results it is concluded that, under the employed experimental conditions, Nb and Mo nitrides and carbides could be synthesized with the exception of the mechanical mixture of activated carbon and the niobium precursor; SSA values were in the range 10 - 35 m2/g for nitrides and carbides prepared by direct nitriding and carbiding, and a strong influence of activated carbon residua in the areas of samples obtained by carboreduction of mechanical mixtures was evident. It was also observed that the higher the SSA, the higher the catalytic activity. Among all the synthesized solids, the molybdenum nitrides and carbides proved to be the more active catalysts in HDS.

Scientific Electronic Library Online (Spanish)

7

SÍNTESIS, CARACTERIZACIÓN Y PRUEBAS CATALÍTICAS DE FILOSILICATOS DE HIERRO EN LA SÍNTESIS DE ALCOHOLES SUPERIORES

Loaiza-Gil1, A; Olivo, M.; Casanova, R; Mendialdua, J.; Rueda, F; Rodriguez, A; Ng Lee, Y
2002-06-01

Resumen en español El método del amonio modificado fue utilizado para preparar catalizadores del tipo filosilicatos de hierro. Los estudios de caracterización por reducción a temperatura programada (RTP) de los catalizadores, indican que en los sólidos sintetizados se encuentran presentes por lo menos dos fases. Una fase de baja temperatura correspondiente a óxidos ó hidróxidos del metal y una fase de alta temperatura (1054 °C) correspondiente a filosilicatos de hierro. La presen (mas) cia de estas fases también fue observada por espectroscopia infrarroja con transformada de Fourier (IRFT) y difracción de rayos X (DRX). Estudios realizados por espectroscopia de fotoelectrones de rayos X de éstos sólidos indican que la relación O/Si entre la parte del pico O1s que no está enlazada al hierro y el pico Si2p es de 2.5 típica de los filosilicatos. La actividad y selectividad a la formación de alcoholes superiores de éstos catalizadores fue estudiada, en un sistema de reacción de alta presión, después de someter estos sólidos a un pretratamiento térmico reductivo a 450°C. Los resultados indican que los sólidos reducidos usando velocidades de calentamiento de 0.5°C/min mantienen una superficie hidroxilada estable en las condiciones de reacción y son muy selectivos a la formación de alcoholes superiores. En estas condiciones, los catalizadores presentan valores de actividad y selectividad superiores a aquella obtenida para catalizadores de mayor carga metálica. Resumen en inglés The modified ammonia method was used to prepare iron Phyllosilicates catalyst type. The temperature programmed reduction profiles studies (TPR) show at least two phases in such catalysts. One phase at lower temperature corresponding to one metal oxide or hydroxide and an iron Phyllosilicate phase at higher temperature (1054 °C). Such phases were observed by Fourier Transformed Infrared Spectroscopy (IRFT) and X-ray Diffraction (XRD). Studies by X-ray Photoelectron Spe (mas) ctroscopy (XPS) indicated that the O/Si ratio between the part of the O1s peak not bonded to iron, and the Si2p peak is about 2.5 typical of Phyllosilicates. The activity and selectivity to the synthesis of higher alcohols of these catalysts was studied in a high pressure reaction system after a thermal reductive pretreatment at 450°C. The results indicated that the solids pretreated using a heating rate of 0.5°C/min kept an stable hydroxide surface under the reaction conditions and are very selective to the higher alcohols formation. In such conditions, the activity and selectivity is higher than for the high loading catalysts.

Scientific Electronic Library Online (Spanish)

8

Surface modification of activated carbons for CO2 capture

Pevida García, Covadonga; González Plaza, Marta; Arias Rozada, Borja; Fermoso Domínguez, Javier; Rubiera González, Fernando; Pis Martínez, José Juan
2008-05-18

Digital.CSIC (Spain)

9

Surface localized nitrogen incorporation in epitaxial FePd films and its effect in the Magneto-Optical properties

Martín-González, Marisol S.; Huttel, Y.; Cebollada, Alfonso; Armelles Reig, Gaspar; Briones Fernández-Pola, Fernando
2004-11-01

Digital.CSIC (Spain)

10

Surface characterization of Mn(x)Ge(1−x) and Cr(y)Mn(x)Ge(1−x−y) dilute magnetic semiconductors

Gambardella, Pietro; Claude, L.; Rusponi, S.; Franke, K. J.; Brune, H.; Raabe, J.; Nolting, F.; Bencok, Peter

7 pages, 7 figures.-- PACS nrs.: 75.50.Pp; 75.70.-i; 78.70.Dm; 75.20.Hr. | We have used x-ray photoemission electron microscopy (XPEEM) and x-ray absorption spectroscopy (XAS) to characterize Mn(x)Ge(1−x) and Cr(y)Mn(x)Ge(1−x−y) films grown by molecular beam epitaxy. The surface layers of the as-gro...

DRIVER (Spanish)

11

Surface characterization of Mn(x)Ge(1−x) and Cr(y)Mn(x)Ge(1−x−y) dilute magnetic semiconductors

Gambardella, Pietro; Claude, L.; Rusponi, S.; Franke, K. J.; Brune, H.; Raabe, J.; Nolting, F.; Bencok, Peter; Hanbicki, A. T.; Jonker, B. T.; Grazioli, C.; Veronese, M.; Carbone, C.
2007-03-28

Digital.CSIC (Spain)

12

Study of the effect of acetic acid vapor on copper corrosion at 40 and 80% relative humidity

Cano Díaz, Emilio; Bastidas Rull, José María; Polo, J. L.; Mora, N.
2001-09-20

Digital.CSIC (Spain)

13

Structure and magnetism in the Zn–Mn–O system: A candidate for room temperature ferromagnetic semiconductor

Fernández Lozano, José Francisco; Caballero Cuesta, Amador; Villegas, Marina; Khatib, S. J.; Bañares González, Miguel Ángel; Fierro, Jose L. G.; Costa Krämer, José Luis; López-Ponce, E.; Martín-González, Marisol S.; Briones Fernández-Pola, Fernando; Quesada, Adrián; García, M.; Hernando, A.
2006-01-01

Digital.CSIC (Spain)

14

Straindashinduced enhanced solubility of Au in epitaxial films of Fe

Pastor, C. J.; Limones, C.; Hinarejos, J. J.; García, Jorge M.; Miranda, Rodolfo; Gómez-Goñi, J.; Ortega, J. E.; Abruña, H. D.
1996-08-10

Digital.CSIC (Spain)

15

Size and shape of supported zirconia nanoparticles determined by x-ray photoelectron spectroscopy

Yubero Valencia, Francisco; Mansilla, C.; Ferrer, F. J.; Holgado, Juan P.; González-Elipe, Agustín R.
2007-06-26

Digital.CSIC (Spain)

16

Plasma-activated multi-walled carbon nanotube–polystyrene composite substrates for biosensing

Fernández Sánchez, César; Pellicer, Eva; Orozco, Jahir; Jiménez-Jorquera, Cecilia; Lechuga, Laura M.; Mendoza Gómez, Ernest
2009-08-01

Digital.CSIC (Spain)

17

Origin of Room Temperature Magnetism in Thin (ZnO)1-x(MnO2)x Films and ZnO/MnO2 Multilayers

López-Ponce, E.; Wennberg, A.; Martín-González, Marisol S.; Costa Krämer, José Luis; García, Miguel Ángel; Quesada, Adrián; Hernando, A.; Caballero Cuesta, Amador; Villegas, Marina; Fernández Lozano, José Francisco
2006-01-01

Digital.CSIC (Spain)

18

Nitrogen in aramid-based activated carbon fibers by TPD, XPS and XANES

Boudou, J. P.; Parent, Ph.; Suárez García, Fabián; Villar Rodil, Silvia; Martínez Alonso, Amelia; Díez Tascón, Juan Manuel

11 pages, 6 figures.-- Printed version published Oct 2006.-- Issue title: "Carbon for Energy Storage and Environment Protection". | Activated carbon fibers were prepared from Nomex® [poly(m-phenylene isophthalamide)] by either H3PO4 activation, H3PO4–CO2 activation, or simply CO2 or steam activation...

DRIVER (Spanish)

19

Nitrogen in aramid-based activated carbon fibers by TPD, XPS and XANES

Boudou, J. P.; Parent, Ph.; Suárez García, Fabián; Villar Rodil, Silvia; Martínez Alonso, Amelia; Díez Tascón, Juan Manuel
2006-06-21

Digital.CSIC (Spain)

21

Microscopic and macroscopic dielectric description of mixed oxide thin films

Ferrer, F. J.; Yubero Valencia, Francisco; Mejías, J. A.; García-López, F. J.; González-Elipe, Agustín R.
2007-10-30

Digital.CSIC (Spain)

22

Metal carbide/amorphous C-based nanocomposite coatings for tribological applications

Sánchez López, Juan Carlos; Martínez-Martínez, D.; Abad Roldán, Manuel David; Fernández Camacho, Asunción
2009-01-01

Digital.CSIC (Spain)

23

Mechanical behavior and oxidation resistance of Cr(Al)N coatings

Sánchez López, Juan Carlos; Martínez-Martínez, D.; López Cartes, C.; Fernández Camacho, Asunción; Brizuela, M.; García Luis, A.; Oñate, J. I.
2005-06-21

Digital.CSIC (Spain)

24

Interface alloying effects in the magnetic properties of Fe nanoislands capped with different materials

Huttel, Y.; Navarro, E.; Telling, N. D.; Van der Laan, G.; Pigazo, F.; Palomares, F. J.; Quintana, C.; Román, Eduardo H.; Armelles Reig, Gaspar; Cebollada, Alfonso
2008-09-05

Digital.CSIC (Spain)

26

Influence of the linker type on the Au–S binding properties of thiol and disulfide-modified DNA self-assembly on polycrystalline gold

Martinez, Lidia; Carrascosa, Laura G.; Huttel, Yves; Lechuga, Laura M.; Román García, Elisa Leonor
2010-04-07

Digital.CSIC (Spain)

28

Estudio de la corrosión del cobre por vapores de ácido acético al 40 y 80 % de humedad relativa

Cano Díaz, Emilio; Simancas Peco, Joaquín; Narváez, L.; Bastidas Rull, José María
2004-03-01

Digital.CSIC (Spain)

29

Electronic state characterization of SiOx thin films prepared by evaporation

Barranco Quero, Ángel; Yubero Valencia, Francisco; Espinós Manzorro, Juan Pedro; Groening, P.; González-Elipe, Agustín R.
2005-06-08

Digital.CSIC (Spain)

30

Efecto de las heterogeneidades superficiales de las aleaciones de aluminio sobre el crecimiento y propiedades de las capas anódicas

Bartolomé, Mª. J.; Feliu Jr., S.; López, V.; Escudero, E.; González, J. A.; Feliu Batlle, Sebastián
2007-08-30

Digital.CSIC (Spain)

31

Do peptide nucleic acids form self-assembled monolayers on pyrite surfaces?

Mateo Martí, Eva; Rogero, Celia; Briones, Carlos; Martín Gago, José Ángel
2007-04-18

Digital.CSIC (Spain)

32

Desarrollo y propiedades de recubrimientos nanocomposities lubricantes

Martínez-Martínez, D.; López-Cartes, C.; Sánchez-López, J.C.; Fernández, A.
2006-01-01

Resumen en español El desarrollo de recubrimientos que combinen propiedades de alta dureza con bajos valores de fricción y desgaste constituye un área de investigación de notable interés por su impacto en la mejora del rendimiento de multitud de piezas y herramientas que se utilizan en operaciones industriales tales como corte, mecanizado, etc. En este trabajo se presentan los resultados conseguidos a partir de nuevos sistemas nanoestructurados lubricantes formados por nanocristales de (mas) una fase dura (nc-TiC) que se integran dentro de una masa de material amorfo de bajo coeficiente de fricción (a-C). La síntesis se ha realizado mediante la técnica de "magnetron sputtering" a partir de blancos de Ti y grafito. La caracterización microestructural y química de los recubrimientos se ha llevado a cabo por microscopía electrónica de transmisión (TEM), difracción de rayos X (XRD), espectroscopía de fotoelectrones de rayos X (XPS), microscopía de fuerzas atómicas (AFM) y espectroscopía de pérdida de energía de electrones (EELS). Las propiedades tribológicas se han estudiado a temperatura y humedad ambientales utilizando un tribómetro pin-on-disk con acero como antagonista a presiones de contacto de ~1 GPa. Controlando las condiciones de síntesis se pueden conseguir rangos de fricción (0,1 a 0,4) y durezas (7-27 GPa) con razonables tasas de desgaste (k~10-7 mm³/Nm). El estudio de la relación existente entre la microestructura, composición química y las propiedades medidas nos permitirá la optimización de tales sistemas nanoestructurados para su mejor aprovechamiento tecnológico. Resumen en inglés The development of coatings which combine high hardness and low values of friction and wear is an interesting research area due to the improvement of the performance of many pieces and tools used in industrial processes, such as casting, cutting, etc. In this work we present the results obtained from novel lubricant nanostructured systems formed by nanocrystals of a hard phase (nc-TiC) embedded in a low-friction amorphous matrix (a-C). Synthesis was performed by magnetron (mas) sputtering of Ti and C targets. Chemical and miscrostructural characterization were carried out by transmission electron microscopy (TEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and electron energy loss spectroscopy (EELS). Tribological properties were studied at ambient environmental conditions by means of a pin-on-disk tribometer employing steel as counterpart at Hertzian pressures of ~1 GPa. Depending on synthesis conditions, friction (0,1 to 0,4) and hardness (7-27 GPa) values can be achieved at moderate wear rates (k~10-7 mm³/Nm). The study of the relationship among microstructure, chemical composition and tribo-mechanical properties allows us the optimization of these nanostructured systems to improve the technological applications.

Scientific Electronic Library Online (Spanish)

33

Copper corrosion initiated by butyric acid vapors

Cano Díaz, Emilio; Mora, E. M.; Azcaray, H.; Bastidas Rull, José María
2004-02-18

Digital.CSIC (Spain)

34

Composition and morphology of metal-containing diamond-like carbon films obtained by reactive magnetron sputtering

Corbella, C.; Pascual, E.; Oncins, G.; Canal, Cristina; Andújar, J. L.; Bertrán, Enric
2005-01-06

Digital.CSIC (Spain)

35

Caracterización de los ladrillos constitutivos de un puente histórico en Popayán (Colombia)/ Characterising a historical bridge’s bricks in Popayán ( Colombia )

Galindo Díaz, Jorge Alberto; Muñoz, Andrés Mauricio; Caicedo Muñoz, Marisol
2008-08-01

Resumen en español El objetivo de este artículo es presentar los procedimientos y resultados del estudio y caracterización físico-mecánica y químico-mineralógica de los ladrillos empleados originalmente en un puente de arco de albañilería cuya construcción data de la primera mitad del siglo XVIII, ubicado en la ciudad de Popayán, Colombia. Para ello se extrajeron núcleos de las zonas bajas del puente a partir de los cuales se obtuvieron especímenes que fueron sometidos a diferen (mas) tes pruebas de laboratorio. La caracterización físico-mecánica cuantificó valores relativos a peso seco, peso suspendido, peso saturado, porosidad, gravedad aparente, densidad aparente, y por último, valores de carga máxima, resistencia a la compresión en frío y módulo de elasticidad. Los resultados obtenidos hacen ver la alta porosidad de los ladrillos y su baja capacidad resistente a esfuerzos de compresión. La caracterización químico-mineralógica se llevó a cabo mediante una combinación de pruebas que incluyeron difracción de rayos X (XRD), espectroscopia de fotoelectrones de rayos X (XPS) y espectroscopia infrarroja por transformada de Fourier (FTIR). Varios minerales encontrados permiten deducir la fuente del material crudo, así como verificar algunas características de la producción de ladrillo de la época en esta región. Tridimita, cristobalita, magnetita y carbonato de calcio son algunas de las fases formadas por las temperaturas alcanzadas en la cocción, mientras que la presencia de sulfato de potasio en una de las muestras da razón de características de producción de material para la construcción. La combinación de los análisis XRD y XPS suministra información sobre la temperatura de quemado y las nuevas fases mineralógicas que aparecen al final de este proceso, mientras que FTIR permite comprobar la presencia de grupos funcionales OH y Si-O-Si, principalmente. Las características de estos ladrillos proporcionan datos valiosos para el propósito de restauración, formulando un nuevo ladrillo a partir del material crudo que se ajuste a los requerimientos de la construcción existente. Resumen en inglés This article presents the procedures and results of studying the physical-mechanical and chemical-mineralogical characterisation of the bricks originally used in a masonry arch bridge; the bridge was built in the first half of the 18th century in the city of Popayán, Colombia . Coresamples were thus extracted from the bridge’s lower area and subjected to different laboratory tests. Physical-mechanical characterisation quantified values related to dry weight, suspended w (mas) eight, saturated weight, porosity, apparent gravity, apparent density and maximum load values, cold compression resistance and elasticity modulus. The results revealed the bricks’ high porosity and their low resistance to compression stress. Chemical-mineralogical characterisation involved a combination of tests including X-ray diffracttion (XRD), X-ray photoelectron spectroscopy (XPS) and Fourier transformed infrared spectroscopy (FTIR). Several minerals found led to deducting the source of the raw material, as well as verifying some brick production characteristics of the time in the said region. Tridimite, cristobalite, magnetite and calcium carbonate were some of the phases formed by the temperatures reached while firing the bricks, while potassium sulphate presence in one of the samples conveyed the nature of the construction materials’ production characteristics. Combining XRD and XPS analysis provided information about firing temperature and the new mineralogical phases appearing at the end of this process; FTIR proved functional OH and Si-O-Si group presence. These bricks’ characteristics provided valuable data for restoration purposes, formulating a new brick from raw material complying with reconstruction requirements.

Scientific Electronic Library Online (Spanish)

36

Bonding structure and mechanical properties of Ti-B-C coatings

Abad Roldán, Manuel David; Cáceres, Daniel; Pogozhev, Yury S.; Shtansky, Dmitry V.; Sánchez López, Juan Carlos
2009-01-01

Digital.CSIC (Spain)

37

Behavior of oxygen doped SiC thin films: An x-ray photoelectron spectroscopy study

Ávila, A.; Montero Herrero, Isabel; Galán, L.; Ripalda, J. María; Levy, R. A.
2001-01-01

Digital.CSIC (Spain)

38

X-ray photoelectron spectroscopy study of low-temperature molybdenum oxidation process

Castañeda, S. I.; Montero Herrero, Isabel; Ripalda, J. María; Díaz, N.; Galán, L.; Rueda, F.