1

Síntesis de catalizadores a base de nitruros y carburos de Nb y Mo para la la hidrodesulfuración de tiofeno/ Synthesis of catalysts based on nitrides and cardides of Nb and Mo for thiophene hydrodesulfurization

García, Elizabeth; González, Yolanda; Dìaz, Yraida; Albornoz, Alberto; Brito, Joaquín L
2009-03-01

Resumen en español Se sintetizaron nitruros y carburos de Nb y Mo a presión atmosférica, a partir de los compuestos precursores: Oxalato de niobio y amonio, heptamolibdato de amonio y trióxido de molibdeno. Los nitruros se sintetizaron por amonólisis bajo una atmósfera de NH3 con un flujo 100 ml/min calentando a razón de 3 °C/min en un rango de temperaturas finales de 700-800 °C. Para la síntesis de los carburos se utilizaron dos métodos: el primero tratando los nitruros de Nb y M (mas) o ya sintetizados bajo corriente de 20% CH4 / balance H2 con un flujo de 100 ml/min calentando a razón de 5ºC/min en un rango de temperaturas finales de 700-800ºC; el segundo método consiste de un tratamiento carbotérmico que se realizó sometiendo mezclas mecánicas de los compuestos precursores de Nb o Mo con carbón activado, en relación molar 1:3, a una atmósfera de H2 con un flujo de 100 ml/min y 3 ºC/min hasta temperaturas finales de 700-800°C. Los sólidos obtenidos se caracterizaron por difracción de rayos-X (DRX), medidas de área superficial específica calculada por el método BET (ASE), Espectroscopia Fotoelectrónica de rayos-X (XPS) y finalmente fueron evaluados catalíticamente en la reacción de hidrodesulfuración (HDS) de tiofeno a presión atmosférica y temperatura de 350°C. De los resultados obtenidos por DRX y XPS se concluye que, a las condiciones a las cuales se sintetizaron los catalizadores se obtienen los nitruros y carburos de Nb y Mo excepto para la mezcla mecánica de carbón activado y la sal de niobio; las medidas de ASE mostraron valores en el rango de 10 a 35 m2/g para los carburos y nitruros preparados por nitración y carburación directa y evidenciaron la influencia del carbón activado en las áreas superficiales de los sólidos obtenidos por carboreducción de las mezclas mecánicas, observándose que a mayor área superficial es mayor la actividad del catalizador. De los sólidos sintetizados, los nitruros y carburos de molibdeno resultaron ser los más activos en la reacción de HDS. Resumen en inglés Niobium and molybdenum nitride- and carbide-based catalysts were synthesized from the precursor compounds: ammonium and niobium oxalate, molybdenum heptamolybdate and molybdenum trioxide. Nitrides were prepared by ammonolysis under a NH3 atmosphere with a flow of 100 ml/min, heating at 3 ºC/min up to final temperatures in the 700-800 ºC range. For the carbides synthesis two methods were employed: The first treating the Nb or Mo nitrides previously synthesized under flow (mas) of 100 ml/min of 20% CH4/balance H2 up to a final temperature of 700 or 800 ºC, at a rate of 3 ºC/min. The second method consisted of a carbothermal treatment of mechanical mixtures of the Nb or Mo precursor compounds with activated carbon, in a molar ratio 1:3, under a 100 ml/min flow of H2 and heating at a rate of 3 ºC/min up to 700-800 ºC. The solid products were characterized by X-ray diffraction (XRD), BET specific surface areas (SSA), X-ray photoelectron spectroscopy (XPS) and finally were catalytically evaluated in the hydrodesulfurization (HDS) of thiophene at atmospheric pressure and 350 ºC. From XRD and XPS results it is concluded that, under the employed experimental conditions, Nb and Mo nitrides and carbides could be synthesized with the exception of the mechanical mixture of activated carbon and the niobium precursor; SSA values were in the range 10 - 35 m2/g for nitrides and carbides prepared by direct nitriding and carbiding, and a strong influence of activated carbon residua in the areas of samples obtained by carboreduction of mechanical mixtures was evident. It was also observed that the higher the SSA, the higher the catalytic activity. Among all the synthesized solids, the molybdenum nitrides and carbides proved to be the more active catalysts in HDS.

Scientific Electronic Library Online (Spanish)

2

Procesamiento y caracterización microestructural del material cerámico ferroeléctrico PbBi4Ti4Nb0,06O15,15/ Processing and Microstructural Characterization of PbBi4Ti4Nb0,06O15,15 Ferroelectric Ceramic Material

Arciniegas, Carlos; Solis Alulima, Byron; Lascano Lascano, Luis
2008-11-01

Resumen en español En la búsqueda de materiales que mantengan buenas propiedades piezoeléctricas a temperaturas mayores que 150 ºC, se ha puesto atención a los compuestos ferroeléctricos con estructura laminar de bismuto. En el presente trabajo, se ha procesado en forma cerámica un compuesto de dicha familia, el PbBi4Ti4Nb0.06O15, 15, por el método convencional de mezcla de óxidos en estado sólido a partir del compuesto PbBi4Ti4O15 (PBIT) ya formado y de óxido de niobio. Se ha est (mas) udiado la estructura cristalina y la microestructura del material sinterizado a diferentes temperaturas. La caracterización estructural muestra la formación de una fase mayoritaria con simetría ortorrómbica, la del PBIT dopado con niobio. La microestructura está formada por granos tipo placa con relación de aspecto menor que la de los granos del compuesto PBIT. Resumen en inglés Searching for materials with good piezoelectric properties above 150 ºC, special attention has been given to the family of ferroelectrics compounds of bismuth with laminar structure. We report the processing of a ceramic form of a member of such family, namely the PbBi4Ti4Nb0.06O15,15. Following the conventional method, we mixed PbBi4Ti4O15 (PBIT) and niobium oxide. We have studied the crystal structure and the microstructure of the sinterized material at several tempera (mas) tures. The structural characterization suggest that the PBIT doped with niobium is the only phase present with orthorrombic simetry. The microstructure shows plaque - like grains smaller than the ones in PBIT.

Scientific Electronic Library Online (Spanish)

3

Nonlinear optical susceptibility of multicomponent tellurite thin film glasses

Muñoz-Martín, David; Fernández Martínez, Héctor; Fernández Navarro, José María; Gonzalo de los Reyes, José

5 pags.; 3 figs.; 2 tabs. | Tellurite (TeO2–TiO2–Nb2O5) thin film glasses have been produced by pulsed laser deposition. The dispersion of the real and imaginary parts of the linear refractive index has been measured in the range from 300 to 1700 nm. Films present high refractive index (n=2.01) and ...

DRIVER (Spanish)