  1. Improvement of corrosion protection property of Mg-alloy by DLC and Si-DLC coatings with PBII technique and multi-target DC-RF magnetron sputtering

    International Nuclear Information System (INIS)

    Masami, Ikeyama; Setsuo, Nakao; Tsutomu, Sonoda; Junho, Choi

    2009-01-01

    Magnesium alloys have been considered as one of the most promising light weight materials with potential applications for automobile and aircraft components. Their poor corrosion resistance, however, has to date prevented wider usage. Diamond-like carbon (DLC) and silicon-incorporated DLC (Si-DLC) coatings are known to provide a high degree of corrosion protection, and hold accordingly promise for enhancing the corrosion resistance of the magnesium alloys. In this work we have studied the effect of coating conditions of DLC coatings as well as Si incorporation into coating on corrosion resistance, deposited onto AZ91 magnesium alloy substrates by plasma based ion implantation (PBII). The influences of a Ti interlayer beneath the DLC, Si-DLC and Ti incorporated DLC (Ti-DLC) coatings fabricated by multi-target direct-current radio-frequency (DC-RF) magnetron sputtering were also examined on both the adhesion strength and corrosion resistance of the materials. We have also examined the effect of the Si content in the Si-DLC coatings made by magnetron sputtering on the alloys' corrosion resistance. The results of potentiodynamic polarization measurements demonstrate that Si-DLC coating deposited by PBII exhibits the highest corrosion resistance in an aqueous 0.05 M NaCl solution. Although Ti layer is helpful in increasing adhesion between DLC coating and AZ91 substrate, it also influences adversely corrosion protection. The ozone treatment of the magnesium alloy's surface before the formation of coatings has been found to improve both adhesion strength and corrosion resistance.

  2. Improvement of corrosion protection property of Mg-alloy by DLC and Si-DLC coatings with PBII technique and multi-target DC-RF magnetron sputtering

    Science.gov (United States)

    Masami, Ikeyama; Setsuo, Nakao; Tsutomu, Sonoda; Junho, Choi

    2009-05-01

    Magnesium alloys have been considered as one of the most promising light weight materials with potential applications for automobile and aircraft components. Their poor corrosion resistance, however, has to date prevented wider usage. Diamond-like carbon (DLC) and silicon-incorporated DLC (Si-DLC) coatings are known to provide a high degree of corrosion protection, and hold accordingly promise for enhancing the corrosion resistance of the magnesium alloys. In this work we have studied the effect of coating conditions of DLC coatings as well as Si incorporation into coating on corrosion resistance, deposited onto AZ91 magnesium alloy substrates by plasma based ion implantation (PBII). The influences of a Ti interlayer beneath the DLC, Si-DLC and Ti incorporated DLC (Ti-DLC) coatings fabricated by multi-target direct-current radio-frequency (DC-RF) magnetron sputtering were also examined on both the adhesion strength and corrosion resistance of the materials. We have also examined the effect of the Si content in the Si-DLC coatings made by magnetron sputtering on the alloys' corrosion resistance. The results of potentiodynamic polarization measurements demonstrate that Si-DLC coating deposited by PBII exhibits the highest corrosion resistance in an aqueous 0.05 M NaCl solution. Although Ti layer is helpful in increasing adhesion between DLC coating and AZ91 substrate, it also influences adversely corrosion protection. The ozone treatment of the magnesium alloy's surface before the formation of coatings has been found to improve both adhesion strength and corrosion resistance.

  3. Mechanical properties, chemical analysis and evaluation of antimicrobial response of Si-DLC coatings fabricated on AISI 316 LVM substrate by a multi-target DC-RF magnetron sputtering method for potential biomedical applications

    Science.gov (United States)

    Bociaga, Dorota; Sobczyk-Guzenda, Anna; Szymanski, Witold; Jedrzejczak, Anna; Jastrzebska, Aleksandra; Olejnik, Anna; Jastrzebski, Krzysztof

    2017-09-01

    In this study silicon doped diamond-like carbon (Si-DLC) coatings were synthesized on two substrates: silicon and AISI 316LVM stainless steel using a multi-target DC-RF magnetron sputtering method. The Si content in the films ranged between 4 and 16 at.%, and was controlled by the electrical power applied in RF regime to Si cathode target. The character of the chemical bonds was revealed by FTIR analysis. With the addition of silicon the hydroxyl absorption (band in the range of 3200-3600 cm-1) increased what suggests more hydrophilic character of the coating. There were also observed significant changes in bonding of Si atoms. For low content of dopant, Si-O-Si bond system is predominant, while for the highest content of silicon there is an evidence of the shift to Si-C bonds in close proximity to methyl groups. The Raman spectroscopy revealed that the G peak position is shifted to a lower wavenumber and the ID/IG ratio decreased with increasing Si content, which indicates an increase in the C-sp3 content. Regardless of the coatings' composition, the improvement of hardness in comparison to pure substrate material (AISI 316 LVM) was observed. Although the reduction of the level of hardness from the level of 10.8 GPa for pure DLC to about 9.4 GPa for the silicon doped coatings was observed, the concomitant improvement of films adhesion with higher amount of Si was revealed. Although incorporation of the dopant to DLC coatings increases the number of E. coli cells which adhered to the examined surfaces, the microbial colonisation remains on the level of substrate material. The presented results prove the potential of Si-DLC coatings in biomedical applications from the point of view of their mechanical properties.

  4. Optical properties and thermal stability of TiAlN/AlON tandem absorber prepared by reactive DC/RF magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Barshilia, Harish C.; Selvakumar, N.; Rajam, K.S. [Surface Engineering Division, National Aerospace Laboratories, Bangalore 560 017 (India); Biswas, A. [Spectroscopy Division, Bhabha Atomic Research Center, Mumbai 400 085 (India)

    2008-11-15

    Spectrally selective TiAlN/AlON tandem absorbers were deposited on copper and stainless steel substrates using a reactive DC/RF magnetron sputtering system. The compositions and thicknesses of the individual component layers were optimized to achieve high absorptance ({alpha}=0.931-0.942) and low emittance ({epsilon}=0.05-0.06) on copper substrate. The experimental spectroscopic ellipsometric data have been fitted with the theoretical models to derive the dispersion of the optical constants (n and k). In order to study the thermal stability of the tandem absorbers, they were subjected to heat treatment (in air and vacuum) for different durations and temperatures. The tandem absorber deposited on Cu substrates exhibited high solar selectivity ({alpha}/{epsilon}) of 0.946/0.07 even after heat treatment in air up to 600 C for 2 h. At 625 C, the solar selectivity decreased significantly on Cu substrates (e.g., {alpha}/{epsilon}=0.924/0.30). The tandem absorber on Cu substrates was also stable in air up to 100 h at 400 C with a solar selectivity of 0.919/0.06. Studies on the accelerated aging tests indicated that the activation energy for the degradation of the tandem absorber is of the order of 100 kJ/mol. (author)

  5. DESIGN OF A DC/RF PHOTOELECTRON GUN

    International Nuclear Information System (INIS)

    YU, D.; NEWSHAM, Y.; SMIRONOV, A.; YU, J.; SMEDLEY, J.; SRINIVASAN RAU, T.; LEWELLEN, J.; ZHOLENTS, A.

    2003-01-01

    An integrated dc/rf photoelectron gun produces a low-emittance beam by first rapidly accelerating electrons at a high gradient during a short (∼1 ns), high-voltage pulse, and then injecting the electrons into an rf cavity for subsequent acceleration. Simulations show that significant improvement of the emittance appears when a high field (∼ 0.5-1 GV/m) is applied to the cathode surface. An adjustable dc gap ((le) 1 mm) which can be integrated with an rf cavity is designed for initial testing at the Injector Test Stand at Argonne National Laboratory using an existing 70-kV pulse generator. Plans for additional experiments of an integrated dc/rf gun with a 250-kV pulse generator are being made

  6. Geometry Optimization of DC/RF Photoelectron Gun

    CERN Document Server

    Chen Ping; Yu, David

    2005-01-01

    Pre-acceleration of photoelectrons in a pulsed, high voltage, short, dc gap and its subsequent injection into an rf gun is a promising method to improve electron beam emittance in rf accelerators. Simulation work has been performed in order to optimize the geometric shapes of a dc/rf gun and improve electron beam properties. Variations were made on cathode and anode shapes, dc gap distance, and inlet shape of the rf cavity. Simulations showed that significant improvement on the normalized emittance (< 1 mm-mrad), compared to a dc gun with flat cathode, could be obtained after the geometric shapes of the gun were optimized.

  7. Diagnostics of ballistic electrons in a dc/rf hybrid capacitively coupled discharge

    International Nuclear Information System (INIS)

    Xu Lin; Chen, Lee; Funk, Merritt; Ranjan, Alok; Hummel, Mike; Bravenec, Ron; Sundararajan, Radha; Economou, Demetre J.; Donnelly, Vincent M.

    2008-01-01

    The energy distribution of ballistic electrons in a dc/rf hybrid parallel-plate capacitively coupled plasma reactor was measured. Ballistic electrons originated as secondaries produced by ion and electron bombardment of the electrodes. The energy distribution of ballistic electrons peaked at the value of the negative bias applied to the dc electrode. As that bias became more negative, the ballistic electron current on the rf substrate electrode increased dramatically. The ion current on the dc electrode also increased

  8. Transparent conducting Al-doped ZnO thin films prepared by magnetron sputtering with dc and rf powers applied in combination

    International Nuclear Information System (INIS)

    Minami, Tadatsugu; Ohtani, Yuusuke; Miyata, Toshihiro; Kuboi, Takeshi

    2007-01-01

    A newly developed Al-doped ZnO (AZO) thin-film magnetron-sputtering deposition technique that decreases resistivity, improves resistivity distribution, and produces high-rate depositions has been demonstrated by dc magnetron-sputtering depositions that incorporate rf power (dc+rf-MS), either with or without the introduction of H 2 gas into the deposition chamber. The dc+rf-MS preparations were carried out in a pure Ar or an Ar+H 2 (0%-2%) gas atmosphere at a pressure of 0.4 Pa by adding a rf component (13.56 MHz) to a constant dc power of 80 W. The deposition rate in a dc+rf-MS deposition incorporating a rf power of 150 W was approximately 62 nm/min, an increase from the approximately 35 nm/min observed in dc magnetron sputtering with a dc power of 80 W. A resistivity as low as 3x10 -4 Ω cm and an improved resistivity distribution could be obtained in AZO thin films deposited on substrates at a low temperature of 150 deg. C by dc+rf-MS with the introduction of hydrogen gas with a content of 1.5%. This article describes the effects of adding a rf power component (i.e., dc+rf-MS deposition) as well as introducing H 2 gas into dc magnetron-sputtering preparations of transparent conducting AZO thin films

  9. Research on DC-RF superconducting photocathode injector for high average power FELs

    International Nuclear Information System (INIS)

    Zhao Kui; Hao Jiankui; Hu Yanle; Zhang Baocheng; Quan Shengwen; Chen Jiaer; Zhuang Jiejia

    2001-01-01

    To obtain high average current electron beams for a high average power Free Electron Laser (FEL), a DC-RF superconducting injector is designed. It consists of a DC extraction gap, a 1+((1)/(2)) superconducting cavity and a coaxial input system. The DC gap, which takes the form of a Pierce configuration, is connected to the 1+((1)/(2)) superconducting cavity. The photocathode is attached to the negative electrode of the DC gap. The anode forms the bottom of the ((1)/(2)) cavity. Simulations are made to model the beam dynamics of the electron beams extracted by the DC gap and accelerated by the superconducting cavity. High quality electron beams with emittance lower than 3 π-mm-mrad can be obtained. The optimization of experiments with the DC gap, as well as the design of experiments with the coaxial coupler have all been completed. An optimized 1+((1)/(2)) superconducting cavity is in the process of being studied and manufactured

  10. Improvement of In-Flight Alumina Spheroidization Process Using a Small Power Argon DC-RF Hybrid Plasma Flow System by Helium Mixture

    Science.gov (United States)

    Takana, Hidemasa; Jang, Juyong; Igawa, Junji; Nakajima, Tomoki; Solonenko, Oleg P.; Nishiyama, Hideya

    2011-03-01

    For the further improvement of in-flight alumina spheroidization process with a low-power direct-current radiofrequency (DC-RF) hybrid plasma flow system, the effect of a small amount of helium gas mixture in argon main gas and also the effect of increasing DC nozzle diameter on powder spheroidization ratio have been experimentally clarified with correlating helium gas mixture percentage, plasma enthalpy, powder in-flight velocity, and temperature. The alumina spheroidization ratio increases by helium gas mixture as a result of enhancement of plasma enthalpy. The highest spheroidization ratio is obtained by 4% mixture of helium in central gas with enlarging nozzle diameter from 3 to 4 mm, even under the constant low input electric power given to a DC-RF hybrid plasma flow system.

  11. Influence of DC arc jets on flow fields analyzed by an integrated numerical model for a DC-RF hybrid plasma

    International Nuclear Information System (INIS)

    Seo, Jun Ho; Park, Jin Myung; Hong, Sang Hee

    2008-01-01

    The influence of DC arc jets on the flow fields in a hybrid plasma torch is numerically analyzed by an integrated direct current-radio frequency (DC-RF) plasma model based on magneto-hydrodynamic formulations. The calculated results reveal that the increase in DC arc gas flow rate raises the axial flow velocity along the central column of the DC-RF hybrid plasma together with the enhanced backflow streams in the peripheral wall region. The temperature profiles on the torch exit plane are little affected due to the reheating process of the central column by the combined RF plasma. Accordingly, the exit enthalpy emitted from the DC-RF hybrid torch can be concentrated to the central column of the plasma and controlled by adjusting the DC arc gas flow rate. The swirl in the sheath gas flow turns out to have the opposite effect on the DC arc gas flow rate. The swirling motion of the sheath gas can reduce the back flows near the induction tube wall as well as the axial velocities in the central column of the plasma. Accordingly, the swirl in the sheath gas flow can be used for the functional operation of the DC-RF hybrid plasma along with the DC arc gas flow rate to suppress the back flows at the wall region and to reduce the excessive interactions between the DC arc jet and the ambient RF plasmas. The effects of DC input current on the flow fields of hybrid plasma are similar to those of the DC arc gas flow rate, but the axial velocities for the higher current relatively quickly decay along the centerline. This is in contrast to the increase in the axial velocity remaining in proportion to the increase in the DC arc gas flow rate all the way up to the exit of the DC-RF hybrid plasma. Accordingly, the present integrated numerical analysis suggests that the hybrid plasma field profiles and the entrainment of ambient air from the torch exit are controllable by adjusting the DC arc gas flow rate, the DC input current and swirl in the sheath gas flow taking advantage of

  12. Research and Development for an Alternative RF Source Using Magnetrons in CEBAF

    Science.gov (United States)

    Jacobs, Andrew

    2016-09-01

    At Jefferson Lab, klystrons are currently used as a radiofrequency (RF) power source for the 1497 MHz Continuous Electron Beam Accelerator Facility (CEBAF) Continuous Wave (CW) system. A drop-in replacement for the klystrons in the form of a system of magnetrons is being developed. The klystron DC-RF efficiency at CEBAF is 35-51% while the estimated magnetron efficiency is 80-90%. Thus, the introduction of magnetrons to CEBAF will have enormous benefits in terms of electrical power saving. The primary focus of this project was to characterize a magnetron's frequency pushing and pulling curves at 2.45 GHz with stub tuner and anode current adjustments so that a Low Level RF controller for a new 1.497 GHz magnetron can be built. A Virtual Instrument was created in LabVIEW, and data was taken. The resulting data allowed for the creation of many constant lines of frequency and output power. Additionally, the results provided a characterization of magnetron oven temperature drift over the operation time and the relationship between anode current and frequency. Using these results, the control model of different variables and their feedback or feedforward that affect the frequency pushing and pulling of the magnetron is better developed. Department of Energy, Science Undergraduate Laboratory Internships, and Jefferson Lab.

  13. Characterization of In-Flight Processing of Alumina Powder Using a DC-RF Hybrid Plasma Flow System at Constant Low Operating Power

    Science.gov (United States)

    Nishiyama, H.; Onodera, M.; Igawa, J.; Nakajima, T.

    2009-12-01

    The aim of this study is to provide the optimum operating conditions for enhancing in-flight alumina particle heating as much as possible for particle spheroidization and aggregation of melted particles using a DC-RF hybrid plasma flow system even at constant low operating power based on the thermofluid considerations. It is clarified that the swirl flow and higher operating pressure enhance the particle melting and aggregation of melted particles coupled with increasing gas temperature downstream of a plasma uniformly in the radial direction at constant electrical discharge conditions.

  14. Advancement of In-Flight Alumina Powder Spheroidization Process with Water Droplet Injection Using a Small Power DC-RF Hybrid Plasma Flow System

    Science.gov (United States)

    Jang, Juyong; Takana, Hidemasa; Park, Sangkyu; Nishiyama, Hideya

    2012-09-01

    The correlation between plasma thermofluid characteristics and alumina powder spheroidization processes with water droplet injection using a small power DC-RF hybrid plasma flow system was experimentally clarified. Micro-sized water droplets with a low water flow rate were injected into the tail of thermal plasma flow so as not to disturb the plasma flow directly. Injected water droplets were vaporized in the thermal plasma flow and were transported upstream in the plasma flow to the torch by the backflow. After dissociation of water, the production of hydrogen was detected by the optical emission spectroscopy in the downstream RF plasma flow. The emission area of the DC plasma jet expanded and elongated in the vicinity of the RF coils. Additionally, the emission area of RF plasma flow enlarged and was visible as red emission in the downstream RF plasma flow in the vicinity below the RF coils due to hydrogen production. Therefore, the plasma flow mixed with produced hydrogen increased the plasma enthalpy and the highest spheroidization rate of 97% was obtained at a water flow rate of 15 Sm l/min and an atomizing gas flow rate of 8 S l/min using a small power DC-RF hybrid plasma flow system.

  15. Development of the DC-RF Hybrid Plasma Source and the Application to the Etching and Texturing of the Silicon Surface

    International Nuclear Information System (INIS)

    Kim, Ji Hun

    2011-02-01

    the vacuum chamber for vacuum processing. The experiment was provided on the mono-crystalline silicon wafer. The etching was carried out with plasma consisting of SF 6 (50 sccm) as a reactive etching gas with O 2 (300 sccm) as a supporting gas and Argon (2000 ∼ 3000 sccm) as a cathode protecting gas. Etching rates were 60 μm/min at low pressure (3-5 torr) and 300 μm/min at a atmospheric pressure. The sample was positioned in such as way that the plasma flow axis would coincide with the side facet of the silicon crystal. A texturing process was performed on a crystalline silicon (c-Si) wafer to increase the efficiency of a solar cell by using a high durability DC arc plasma source at atmospheric pressure and low pressure. CF 4 and SF 6 were used as the reactive etching gases at flow rates 2 as the supporting gas in the range of the 5 - 15 %. To survey the characteristics of the pyramid formation process, plasma texturing experiments were performed by varying the working time. The optimal operating conditions of the gas flow (Ar, O 2 , CF 4 , SF 6 ), plasmatron current and processing time were determined. The pyramid angle was approximately 50 .deg. to 60 .deg. when a single-crystalline silicon surface was textured in a vacuum whereas it was approximately 75 .deg. to 90 .deg. when textured at atmospheric pressure. The reflectance decreases with decreasing pyramid angle. The reflectance of the bare silicon ranged from 40 % to the 60 % but that of the textured silicon was approximately 5 % to 20 %. This reflectance is quite low, approximately half that reported by other studies using wet and reactive ion etching (RIE) texturing. Even though DC arc plasmatron has many advantages, it is difficult to apply an industry due to the small applied area. To increase an effective processing area, we suggest a DC-RF hybrid plasma system. The DC-RF hybrid plasma system was designed and made. This system consists of a DC arc plasmatron, RF parts, reaction chamber, power feeder

  16. Fabrication and characterization of He-charged ODS-FeCrNi films deposited by a radio-frequency plasma magnetron sputtering technique

    Science.gov (United States)

    Song, Liang; Wang, Xianping; Wang, Le; Zhang, Ying; Liu, Wang; Jiang, Weibing; Zhang, Tao; Fang, Qianfeng; Liu, Changsong

    2017-04-01

    He-charged oxide dispersion strengthened (ODS) FeCrNi films were prepared by a radio-frequency (RF) plasma magnetron sputtering method in a He and Ar mixed atmosphere at 150 °C. As a comparison, He-charged FeCrNi films were also fabricated at the same conditions through direct current (DC) plasma magnetron sputtering. The doping of He atoms and Y2O3 in the FeCrNi films was realized by the high backscattered rate of He ions and Y2O3/FeCrNi composite target sputtering method, respectively. Inductive coupled plasma (ICP) and x-ray photoelectron spectroscopy (XPS) analysis confirmed the existence of Y2O3 in FeCrNi films, and Y2O3 content hardly changed with sputtering He/Ar ratio. Cross-sectional scanning electron microscopy (SEM) shows that the FeCrNi films were composed of dense columnar nanocrystallines and the thickness of the films was obviously dependent on He/Ar ratio. Nanoindentation measurements revealed that the FeCrNi films fabricated through DC/RF plasma magnetron sputtering methods exhibited similar hardness values at each He/Ar ratio, while the dispersion of Y2O3 apparently increased the hardness of the films. Elastic recoil detection (ERD) showed that DC/RF magnetron sputtered FeCrNi films contained similar He amounts (˜17 at.%). Compared with the minimal change of He level with depth in DC-sputtered films, the He amount decreases gradually in depth in the RF-sputtered films. The Y2O3-doped FeCrNi films were shown to exhibit much smaller amounts of He owing to the lower backscattering possibility of Y2O3 and the inhibition effect of nano-sized Y2O3 particles on the He element.

  17. Low-communication parallel quantum multi-target preimage search

    NARCIS (Netherlands)

    Banegas, G.S.; Bernstein, D.J.; Adams, Carlisle; Camenisch, Jan

    2017-01-01

    The most important pre-quantum threat to AES-128 is the 1994 van Oorschot–Wiener “parallel rho method”, a low-communication parallel pre-quantum multi-target preimage-search algorithm. This algorithm uses a mesh of p small processors, each running for approximately 2 128 /pt 2128/pt fast steps, to

  18. Multi-target molecular imaging and its progress in research and application

    International Nuclear Information System (INIS)

    Tang Ganghua

    2011-01-01

    Multi-target molecular imaging (MMI) is an important field of research in molecular imaging. It includes multi-tracer multi-target molecular imaging(MTMI), fusion-molecule multi-target imaging (FMMI), coupling-molecule multi-target imaging (CMMI), and multi-target multifunctional molecular imaging(MMMI). In this paper,imaging modes of MMI are reviewed, and potential applications of positron emission tomography MMI in near future are discussed. (author)

  19. Magnetron plasma and nanotechnology

    International Nuclear Information System (INIS)

    Kashtanov, Pavel V; Smirnov, Boris M; Hippler, Rainer

    2007-01-01

    Magnetron plasma processes involving metal atoms and clusters are reviewed. The formation of metal atoms near the cathode and their nucleation in a buffer gas flow are discussed. The flow of a buffer gas with metal clusters through a magnetron chamber disturbs the equilibrium between the buffer gas flow and clusters near the exit orifice and is accompanied by cluster attachment to the chamber walls. Cluster charging far off the cathode, the disturbance of equilibrium between the buffer gas flow and cluster drift, and the attachment of charged clusters to the chamber walls - the factors determining the output parameters of the cluster beam escaping the magnetron chamber - are analyzed. Cluster deposition on a solid surface and on dusty plasma particles is considered. (reviews of topical problems)

  20. Multi-Target Tracking via Mixed Integer Optimization

    Science.gov (United States)

    2016-05-13

    an easily interpretable global objective function. Furthermore, we propose a greedy heuristic which quickly finds good solutions. We extend both the... heuristic and the MIO model to scenarios with missed detections and false alarms. Index Terms—optimization; multi-target tracking; data asso- ciation...energy in [14] and then again as a minimization of discrete-continuous energy in [15]. These algorithms aim to more accurately represent the nature of the

  1. Magnetron injection gun scaling

    International Nuclear Information System (INIS)

    Lawson, W.

    1988-01-01

    Existing analytic design equations for magnetron injection guns (MIG's) are approximated to obtain a set of scaling laws. The constraints are chosen to examine the maximum peak power capabilities of MIG's. The scaling laws are compared with exact solutions of the design equations and are supported by MIG simulations

  2. Ring magnetron ionizer

    International Nuclear Information System (INIS)

    Alessi, J.G.

    1986-01-01

    A ring magnetron D - charge exchange ionizer has been built and tested. An H - current of 500 μA was extracted with an estimated H 0 density in the ionizer of 10 12 cm -3 . This exceeds the performance of ionizers presently in use on polarized H - sources. The ionizer will soon be tested with a polarized atomic beam

  3. Linear transform of the multi-target survival curve

    Energy Technology Data Exchange (ETDEWEB)

    Watson, J V [Cambridge Univ. (UK). Dept. of Clinical Oncology and Radiotherapeutics

    1978-07-01

    A completely linear transform of the multi-target survival curve is presented. This enables all data, including those on the shoulder region of the curve, to be analysed. The necessity to make a subjective assessment about which data points to exclude for conventional methods of analysis is, therefore, removed. The analysis has also been adapted to include a 'Pike-Alper' method of assessing dose modification factors. For the data cited this predicts compatibility with the hypothesis of a true oxygen 'dose-modification' whereas the conventional Pike-Alper analysis does not.

  4. Geometric considerations in magnetron sputtering

    International Nuclear Information System (INIS)

    Thornton, J.A.

    1982-01-01

    The recent development of high performance magnetron type discharge sources has greatly enhaced the range of coating applications where sputtering is a viable deposition process. Magnetron sources can provide high current densities and sputtering rates, even at low pressures. They have much reduced substrate heating rates and can be scaled to large sizes. Magnetron sputter coating apparatuses can have a variety of geometric and plasma configurations. The target geometry affects the emission directions of both the sputtered atoms and the energetic ions which are neutralized and reflected at the cathode. This fact, coupled with the long mean free particle paths which are prevalent at low pressures, can make the coating properties very dependent on the apparatus geometry. This paper reviews the physics of magnetron operation and discusses the influences of apparatus geometry on the use of magnetrons for rf sputtering and reactive sputtering, as well as on the microstructure and internal stresses in sputtered metallic coatings. (author) [pt

  5. Real-Time Multi-Target Localization from Unmanned Aerial Vehicles

    Directory of Open Access Journals (Sweden)

    Xuan Wang

    2016-12-01

    Full Text Available In order to improve the reconnaissance efficiency of unmanned aerial vehicle (UAV electro-optical stabilized imaging systems, a real-time multi-target localization scheme based on an UAV electro-optical stabilized imaging system is proposed. First, a target location model is studied. Then, the geodetic coordinates of multi-targets are calculated using the homogeneous coordinate transformation. On the basis of this, two methods which can improve the accuracy of the multi-target localization are proposed: (1 the real-time zoom lens distortion correction method; (2 a recursive least squares (RLS filtering method based on UAV dead reckoning. The multi-target localization error model is established using Monte Carlo theory. In an actual flight, the UAV flight altitude is 1140 m. The multi-target localization results are within the range of allowable error. After we use a lens distortion correction method in a single image, the circular error probability (CEP of the multi-target localization is reduced by 7%, and 50 targets can be located at the same time. The RLS algorithm can adaptively estimate the location data based on multiple images. Compared with multi-target localization based on a single image, CEP of the multi-target localization using RLS is reduced by 25%. The proposed method can be implemented on a small circuit board to operate in real time. This research is expected to significantly benefit small UAVs which need multi-target geo-location functions.

  6. Study of static properties of magnetron-type space charges

    International Nuclear Information System (INIS)

    Delcroix, Jean-Loup

    1953-01-01

    This research thesis reports an in-depth analysis of physical properties of static regimes to address the issue of space charges. This theoretical study of the Hull magnetron is followed by the description of experiments on the Hull magnetron which highlight transitions between the different regimes. Then, another theoretical approach aims at generalising the magnetron theory, based on other types of magnetron theory (general equations of magnetron-type space charges, inverted Hull magnetron theory, circular field magnetron theory)

  7. A modified high-intensity Cs sputter negative-ion source with multi-target mechanism

    International Nuclear Information System (INIS)

    Si Houzhi; Zhang Weizhong; Zhu Jinhau; Du Guangtian; Zhang Tiaorong; Gao Xiang

    1993-01-01

    The source is based on Middleton's high-intensity mode, but modified to a multi-target version. It is equipped with a spherical molybdenum ionizer, a 20-position target wheel and a vacuum lock for loading and unloading sample batches. A metal-ceramic bonded section protected by a specially designed labyrinth shielding system results in reliable insulation of the cathode and convenient control of cesium vapor. The latter is particularly important when an oversupply of cesium occurs. The source was developed for accelerator mass spectrometry (AMS) applications. Recently, three versions based on the prototype of the source have been successfully tested to meet different requirements: (a) Single target version, (b) multi-target version with manual sample change, and (c) multi-target version with remote control sample change. Some details of the technical and operational characteristics are presented. (orig.)

  8. Box-Particle Cardinality Balanced Multi-Target Multi-Bernoulli Filter

    OpenAIRE

    L. Song; X. Zhao

    2014-01-01

    As a generalized particle filtering, the box-particle filter (Box-PF) has a potential to process the measurements affected by bounded error of unknown distributions and biases. Inspired by the Box-PF, a novel implementation for multi-target tracking, called box-particle cardinality balanced multi-target multi-Bernoulli (Box-CBMeMBer) filter is presented in this paper. More important, to eliminate the negative effect of clutters in the estimation of the numbers of targets, an improved generali...

  9. An Automatic Multi-Target Independent Analysis Framework for Non-Planar Infrared-Visible Registration.

    Science.gov (United States)

    Sun, Xinglong; Xu, Tingfa; Zhang, Jizhou; Zhao, Zishu; Li, Yuankun

    2017-07-26

    In this paper, we propose a novel automatic multi-target registration framework for non-planar infrared-visible videos. Previous approaches usually analyzed multiple targets together and then estimated a global homography for the whole scene, however, these cannot achieve precise multi-target registration when the scenes are non-planar. Our framework is devoted to solving the problem using feature matching and multi-target tracking. The key idea is to analyze and register each target independently. We present a fast and robust feature matching strategy, where only the features on the corresponding foreground pairs are matched. Besides, new reservoirs based on the Gaussian criterion are created for all targets, and a multi-target tracking method is adopted to determine the relationships between the reservoirs and foreground blobs. With the matches in the corresponding reservoir, the homography of each target is computed according to its moving state. We tested our framework on both public near-planar and non-planar datasets. The results demonstrate that the proposed framework outperforms the state-of-the-art global registration method and the manual global registration matrix in all tested datasets.

  10. Fusion-based multi-target tracking and localization for intelligent surveillance systems

    Science.gov (United States)

    Rababaah, Haroun; Shirkhodaie, Amir

    2008-04-01

    In this paper, we have presented two approaches addressing visual target tracking and localization in complex urban environment. The two techniques presented in this paper are: fusion-based multi-target visual tracking, and multi-target localization via camera calibration. For multi-target tracking, the data fusion concepts of hypothesis generation/evaluation/selection, target-to-target registration, and association are employed. An association matrix is implemented using RGB histograms for associated tracking of multi-targets of interests. Motion segmentation of targets of interest (TOI) from the background was achieved by a Gaussian Mixture Model. Foreground segmentation, on other hand, was achieved by the Connected Components Analysis (CCA) technique. The tracking of individual targets was estimated by fusing two sources of information, the centroid with the spatial gating, and the RGB histogram association matrix. The localization problem is addressed through an effective camera calibration technique using edge modeling for grid mapping (EMGM). A two-stage image pixel to world coordinates mapping technique is introduced that performs coarse and fine location estimation of moving TOIs. In coarse estimation, an approximate neighborhood of the target position is estimated based on nearest 4-neighbor method, and in fine estimation, we use Euclidean interpolation to localize the position within the estimated four neighbors. Both techniques were tested and shown reliable results for tracking and localization of Targets of interests in complex urban environment.

  11. A Bayesian solution to multi-target tracking problems with mixed labelling

    NARCIS (Netherlands)

    Aoki, E.H.; Boers, Y.; Svensson, Lennart; Mandal, Pranab K.; Bagchi, Arunabha

    In Multi-Target Tracking (MTT), the problem of assigning labels to tracks (track labelling) is vastly covered in literature and has been previously formulated using Bayesian recursion. However, the existing literature lacks an appropriate measure of uncertainty related to the assigned labels which

  12. Multi-targeted priming for genome-wide gene expression assays

    Directory of Open Access Journals (Sweden)

    Adomas Aleksandra B

    2010-08-01

    Full Text Available Abstract Background Complementary approaches to assaying global gene expression are needed to assess gene expression in regions that are poorly assayed by current methodologies. A key component of nearly all gene expression assays is the reverse transcription of transcribed sequences that has traditionally been performed by priming the poly-A tails on many of the transcribed genes in eukaryotes with oligo-dT, or by priming RNA indiscriminately with random hexamers. We designed an algorithm to find common sequence motifs that were present within most protein-coding genes of Saccharomyces cerevisiae and of Neurospora crassa, but that were not present within their ribosomal RNA or transfer RNA genes. We then experimentally tested whether degenerately priming these motifs with multi-targeted primers improved the accuracy and completeness of transcriptomic assays. Results We discovered two multi-targeted primers that would prime a preponderance of genes in the genomes of Saccharomyces cerevisiae and Neurospora crassa while avoiding priming ribosomal RNA or transfer RNA. Examining the response of Saccharomyces cerevisiae to nitrogen deficiency and profiling Neurospora crassa early sexual development, we demonstrated that using multi-targeted primers in reverse transcription led to superior performance of microarray profiling and next-generation RNA tag sequencing. Priming with multi-targeted primers in addition to oligo-dT resulted in higher sensitivity, a larger number of well-measured genes and greater power to detect differences in gene expression. Conclusions Our results provide the most complete and detailed expression profiles of the yeast nitrogen starvation response and N. crassa early sexual development to date. Furthermore, our multi-targeting priming methodology for genome-wide gene expression assays provides selective targeting of multiple sequences and counter-selection against undesirable sequences, facilitating a more complete and

  13. The Pulsed Cylindrical Magnetron for Deposition

    Science.gov (United States)

    Korenev, Sergey

    2012-10-01

    The magnetron sputtering deposition of films and coatings broadly uses in microelectronics, material science, environmental applications and etc. The rate of target evaporation and time for deposition of films and coatings depends on magnetic field. These parameters link with efficiency of gas molecules ionization by electrons. The cylindrical magnetrons use for deposition of films and coatings on inside of pipes for different protective films and coatings in oil, chemical, environmental applications. The classical forming of magnetic field by permanent magnets or coils for big and long cylindrical magnetrons is complicated. The new concept of pulsed cylindrical magnetron for high rate deposition of films and coating for big and long pipes is presented in this paper. The proposed cylindrical magnetron has azimuthally pulsed high magnetic field, which allows forming the high ionized plasma and receiving high rate of evaporation material of target (central electrode). The structure of proposed pulsed cylindrical magnetron sputtering system is given. The main requirements to deposition system are presented. The preliminary data for forming of plasma and deposition of Ta films and coatings on the metal pipers are discussed. The comparison of classical and proposed cylindrical magnetrons is given. The analysis of potential applications is considered.

  14. Negative Ion Sources: Magnetron and Penning

    International Nuclear Information System (INIS)

    Faircloth, D C

    2013-01-01

    The history of the magnetron and Penning electrode geometry is briefly outlined. Plasma generation by electrical discharge-driven electron impact ionization is described and the basic physics of plasma and electrodes relevant to magnetron and Penning discharges are explained. Negative ions and their applications are introduced, along with their production mechanisms. Caesium and surface production of negative ions are detailed. Technical details of how to build magnetron and Penning surface plasma sources are given, along with examples of specific sources from around the world. Failure modes are listed and lifetimes compared. (author)

  15. Negative Ion Sources: Magnetron and Penning

    CERN Document Server

    Faircloth, D.C.

    2013-12-16

    The history of the magnetron and Penning electrode geometry is briefly outlined. Plasma generation by electrical discharge-driven electron impact ionization is described and the basic physics of plasma and electrodes relevant to magnetron and Penning discharges are explained. Negative ions and their applications are introduced, along with their production mechanisms. Caesium and surface production of negative ions are detailed. Technical details of how to build magnetron and Penning surface plasma sources are given, along with examples of specific sources from around the world. Failure modes are listed and lifetimes compared.

  16. Two-phase framework for optimal multi-target Lambert rendezvous

    OpenAIRE

    Bang, Jun; Ahn, Jaemyung

    2017-01-01

    This paper proposes a two-phase framework to solve an optimal multi-target Lambert rendezvous problem. The first phase solves a series of single-target rendezvous problems for all departure-arrival object pairs to generate the elementary solutions, which provides candidate rendezvous trajectories (elementary solutions). The second phase formulates a variant of traveling salesman problem (TSP) using the elementary solutions prepared in the first phase and determines the best rendezvous sequenc...

  17. Analysis and Simulation of Multi-target Echo Signals from a Phased Array Radar

    OpenAIRE

    Jia Zhen; Zhou Rui

    2017-01-01

    The construction of digital radar simulation systems has been a research hotspot of the radar field. This paper focuses on theoretical analysis and simulation of multi-target echo signals produced in a phased array radar system, and constructs an array antenna element and a signal generation environment. The antenna element is able to simulate planar arrays and optimizes these arrays by adding window functions. And the signal environment can model and simulate radar transmission signals, rada...

  18. Multi-Target Screening and Experimental Validation of Natural Products from Selaginella Plants against Alzheimer's Disease

    Directory of Open Access Journals (Sweden)

    Yin-Hua Deng

    2017-08-01

    Full Text Available Alzheimer's disease (AD is a progressive and irreversible neurodegenerative disorder which is considered to be the most common cause of dementia. It has a greater impact not only on the learning and memory disturbances but also on social and economy. Currently, there are mainly single-target drugs for AD treatment but the complexity and multiple etiologies of AD make them difficult to obtain desirable therapeutic effects. Therefore, the choice of multi-target drugs will be a potential effective strategy inAD treatment. To find multi-target active ingredients for AD treatment from Selaginella plants, we firstly explored the behaviors effects on AD mice of total extracts (TE from Selaginella doederleinii on by Morris water maze test and found that TE has a remarkable improvement on learning and memory function for AD mice. And then, multi-target SAR models associated with AD-related proteins were built based on Random Forest (RF and different descriptors to preliminarily screen potential active ingredients from Selaginella. Considering the prediction outputs and the quantity of existing compounds in our laboratory, 13 compounds were chosen to carry out the in vitro enzyme inhibitory experiments and 4 compounds with BACE1/MAO-B dual inhibitory activity were determined. Finally, the molecular docking was applied to verify the prediction results and enzyme inhibitory experiments. Based on these study and validation processes, we explored a new strategy to improve the efficiency of active ingredients screening based on trace amount of natural product and numbers of targets and found some multi-target compounds with biological activity for the development of novel drugs for AD treatment.

  19. Identification and characterization of carprofen as a multi-target FAAH/COX inhibitor

    Science.gov (United States)

    Favia, Angelo D.; Habrant, Damien; Scarpelli, Rita; Migliore, Marco; Albani, Clara; Bertozzi, Sine Mandrup; Dionisi, Mauro; Tarozzo, Glauco; Piomelli, Daniele; Cavalli, Andrea; De Vivo, Marco

    2013-01-01

    Pain and inflammation are major therapeutic areas for drug discovery. Current drugs for these pathologies have limited efficacy, however, and often cause a number of unwanted side effects. In the present study, we identify the non-steroid anti-inflammatory drug, carprofen, as a multi-target-directed ligand that simultaneously inhibits cyclooxygenase-1 (COX-1), COX-2 and fatty acid amide hydrolase (FAAH). Additionally, we synthesized and tested several racemic derivatives of carprofen, sharing this multi-target activity. This may result in improved analgesic efficacy and reduced side effects (Naidu, et al (2009) J Pharmacol Exp Ther 329, 48-56; Fowler, C.J. et al. (2012) J Enzym Inhib Med Chem Jan 6; Sasso, et al (2012) Pharmacol Res 65, 553). The new compounds are among the most potent multi-target FAAH/COXs inhibitors reported so far in the literature, and thus may represent promising starting points for the discovery of new analgesic and anti-inflammatory drugs. PMID:23043222

  20. Designing multi-targeted agents: An emerging anticancer drug discovery paradigm.

    Science.gov (United States)

    Fu, Rong-Geng; Sun, Yuan; Sheng, Wen-Bing; Liao, Duan-Fang

    2017-08-18

    The dominant paradigm in drug discovery is to design ligands with maximum selectivity to act on individual drug targets. With the target-based approach, many new chemical entities have been discovered, developed, and further approved as drugs. However, there are a large number of complex diseases such as cancer that cannot be effectively treated or cured only with one medicine to modulate the biological function of a single target. As simultaneous intervention of two (or multiple) cancer progression relevant targets has shown improved therapeutic efficacy, the innovation of multi-targeted drugs has become a promising and prevailing research topic and numerous multi-targeted anticancer agents are currently at various developmental stages. However, most multi-pharmacophore scaffolds are usually discovered by serendipity or screening, while rational design by combining existing pharmacophore scaffolds remains an enormous challenge. In this review, four types of multi-pharmacophore modes are discussed, and the examples from literature will be used to introduce attractive lead compounds with the capability of simultaneously interfering with different enzyme or signaling pathway of cancer progression, which will reveal the trends and insights to help the design of the next generation multi-targeted anticancer agents. Copyright © 2017 Elsevier Masson SAS. All rights reserved.

  1. A Plasma Lens for Magnetron Sputtering

    International Nuclear Information System (INIS)

    Anders, Andre; Brown, Jeff

    2010-01-01

    A plasma lens, consisting of a solenoid and potential-defining ring electrodes, has been placed between a magnetron and substrates to be coated. Photography reveals qualitative information on excitation, ionization, and the transport of plasma to the substrate.

  2. Pulsed dc self-sustained magnetron sputtering

    International Nuclear Information System (INIS)

    Wiatrowski, A.; Posadowski, W. M.; Radzimski, Z. J.

    2008-01-01

    The magnetron sputtering has become one of the commonly used techniques for industrial deposition of thin films and coatings due to its simplicity and reliability. At standard magnetron sputtering conditions (argon pressure of ∼0.5 Pa) inert gas particles (necessary to sustain discharge) are often entrapped in the deposited films. Inert gas contamination can be eliminated during the self-sustained magnetron sputtering (SSS) process, where the presence of the inert gas is not a necessary requirement. Moreover the SSS process that is possible due to the high degree of ionization of the sputtered material also gives a unique condition during the transport of sputtered particles to the substrate. So far it has been shown that the self-sustained mode of magnetron operation can be obtained using dc powering (dc-SSS) only. The main disadvantage of the dc-SSS process is its instability related to random arc formation. In such case the discharge has to be temporarily extinguished to prevent damaging both the magnetron source and power supply. The authors postulate that pulsed powering could protect the SSS process against arcs, similarly to reactive pulsed magnetron deposition processes of insulating thin films. To put this concept into practice, (i) the high enough plasma density has to be achieved and (ii) the type of pulsed powering has to be chosen taking plasma dynamics into account. In this article results of pulsed dc self-sustained magnetron sputtering (pulsed dc-SSS) are presented. The planar magnetron equipped with a 50 mm diameter and 6 mm thick copper target was used during the experiments. The maximum target power was about 11 kW, which corresponded to the target power density of ∼560 W/cm 2 . The magnetron operation was investigated as a function of pulse frequency (20-100 kHz) and pulse duty factor (50%-90%). The discharge (argon) extinction pressure level was determined for these conditions. The plasma emission spectra (400-410 nm range) and deposition

  3. Study of static properties of magnetron-type space charges; Etude des proprietes statiques des charges d'espace du type magnetron

    Energy Technology Data Exchange (ETDEWEB)

    Delcroix, Jean-Loup

    1953-05-30

    This research thesis reports an in-depth analysis of physical properties of static regimes to address the issue of space charges. This theoretical study of the Hull magnetron is followed by the description of experiments on the Hull magnetron which highlight transitions between the different regimes. Then, another theoretical approach aims at generalising the magnetron theory, based on other types of magnetron theory (general equations of magnetron-type space charges, inverted Hull magnetron theory, circular field magnetron theory)

  4. Identifying natural compounds as multi-target-directed ligands against Alzheimer's disease: an in silico approach.

    Science.gov (United States)

    Ambure, Pravin; Bhat, Jyotsna; Puzyn, Tomasz; Roy, Kunal

    2018-04-23

    Alzheimer's disease (AD) is a multi-factorial disease, which can be simply outlined as an irreversible and progressive neurodegenerative disorder with an unclear root cause. It is a major cause of dementia in old aged people. In the present study, utilizing the structural and biological activity information of ligands for five important and mostly studied vital targets (i.e. cyclin-dependant kinase 5, β-secretase, monoamine oxidase B, glycogen synthase kinase 3β, acetylcholinesterase) that are believed to be effective against AD, we have developed five classification models using linear discriminant analysis (LDA) technique. Considering the importance of data curation, we have given more attention towards the chemical and biological data curation, which is a difficult task especially in case of big data-sets. Thus, to ease the curation process we have designed Konstanz Information Miner (KNIME) workflows, which are made available at http://teqip.jdvu.ac.in/QSAR_Tools/ . The developed models were appropriately validated based on the predictions for experiment derived data from test sets, as well as true external set compounds including known multi-target compounds. The domain of applicability for each classification model was checked based on a confidence estimation approach. Further, these validated models were employed for screening of natural compounds collected from the InterBioScreen natural database ( https://www.ibscreen.com/natural-compounds ). Further, the natural compounds that were categorized as 'actives' in at least two classification models out of five developed models were considered as multi-target leads, and these compounds were further screened using the drug-like filter, molecular docking technique and then thoroughly analyzed using molecular dynamics studies. Finally, the most potential multi-target natural compounds against AD are suggested.

  5. Multi-target drugs: the trend of drug research and development.

    Science.gov (United States)

    Lu, Jin-Jian; Pan, Wei; Hu, Yuan-Jia; Wang, Yi-Tao

    2012-01-01

    Summarizing the status of drugs in the market and examining the trend of drug research and development is important in drug discovery. In this study, we compared the drug targets and the market sales of the new molecular entities approved by the U.S. Food and Drug Administration from January 2000 to December 2009. Two networks, namely, the target-target and drug-drug networks, have been set up using the network analysis tools. The multi-target drugs have much more potential, as shown by the network visualization and the market trends. We discussed the possible reasons and proposed the rational strategies for drug research and development in the future.

  6. Data association approaches in bearings-only multi-target tracking

    Science.gov (United States)

    Xu, Benlian; Wang, Zhiquan

    2008-03-01

    According to requirements of time computation complexity and correctness of data association of the multi-target tracking, two algorithms are suggested in this paper. The proposed Algorithm 1 is developed from the modified version of dual Simplex method, and it has the advantage of direct and explicit form of the optimal solution. The Algorithm 2 is based on the idea of Algorithm 1 and rotational sort method, it combines not only advantages of Algorithm 1, but also reduces the computational burden, whose complexity is only 1/ N times that of Algorithm 1. Finally, numerical analyses are carried out to evaluate the performance of the two data association algorithms.

  7. Stability of Brillouin flow in planar, conventional, and inverted magnetrons

    International Nuclear Information System (INIS)

    Simon, D. H.; Lau, Y. Y.; Greening, G.; Wong, P.; Gilgenbach, R. M.; Hoff, B. W.

    2015-01-01

    The Brillouin flow is the prevalent flow in crossed-field devices. We systematically study its stability in the conventional, planar, and inverted magnetron geometry. To investigate the intrinsic negative mass effect in Brillouin flow, we consider electrostatic modes in a nonrelativistic, smooth bore magnetron. We found that the Brillouin flow in the inverted magnetron is more unstable than that in a planar magnetron, which in turn is more unstable than that in the conventional magnetron. Thus, oscillations in the inverted magnetron may startup faster than the conventional magnetron. This result is consistent with simulations, and with the negative mass property in the inverted magnetron configuration. Inclusion of relativistic effects and electromagnetic effects does not qualitatively change these conclusions

  8. CEERI-CAT joint venture for development of accelerator magnetrons

    International Nuclear Information System (INIS)

    Prasad, Sharda; Kaushik, S.C.; Mahesh Kumar; Chaudhary, P.; Shrivastava, Purushottam; Wanmode, Y.; Hannurkar, P.R.

    2003-01-01

    LINAC and Microtron systems for electron acceleration up to few tens of MeV, requires pulsed RF sources such as magnetron and klystron in S-Band frequency range with peak power in the range of few MW. The major emphasis under this program was to develop critical technologies involved in the development of 2 MW magnetron. This paper discusses the development of 2 MW magnetron along with critical technologies involved and test facilities developed by CAT for testing of this magnetron

  9. Analysis of peer-to-peer locking of magnetrons

    International Nuclear Information System (INIS)

    Pengvanich, P.; Lau, Y. Y.; Cruz, E.; Gilgenbach, R. M.; Hoff, B.; Luginsland, J. W.

    2008-01-01

    The condition for mutual, or peer-to-peer, locking of two magnetrons is derived. This condition reduces to Adler's classical phase-locking condition in the limit where one magnetron becomes the ''master'' and the other becomes the ''slave.'' The formulation is extended to the peer-to-peer locking of N magnetrons, under the assumption that the electromagnetic coupling among the N magnetrons is modeled by an N-port network.

  10. Pharmacological characterization of memoquin, a multi-target compound for the treatment of Alzheimer's disease.

    Directory of Open Access Journals (Sweden)

    Valeria Capurro

    Full Text Available Alzheimer's disease (AD is characterized by progressive loss of cognitive function, dementia and altered behavior. Over 30 million people worldwide suffer from AD and available therapies are still palliative rather than curative. Recently, Memoquin (MQ, a quinone-bearing polyamine compound, has emerged as a promising anti-AD lead candidate, mainly thanks to its multi-target profile. MQ acts as an acetylcholinesterase and β-secretase-1 inhibitor, and also possesses anti-amyloid and anti-oxidant properties. Despite this potential interest, in vivo behavioral studies with MQ have been limited. Here, we report on in vivo studies with MQ (acute and sub-chronic treatments; 7-15 mg/kg per os carried out using two different mouse models: i scopolamine- and ii beta-amyloid peptide- (Aβ- induced amnesia. Several aspects related to memory were examined using the T-maze, the Morris water maze, the novel object recognition, and the passive avoidance tasks. At the dose of 15 mg/kg, MQ was able to rescue all tested aspects of cognitive impairment including spatial, episodic, aversive, short and long-term memory in both scopolamine- and Aβ-induced amnesia models. Furthermore, when tested in primary cortical neurons, MQ was able to fully prevent the Aβ-induced neurotoxicity mediated by oxidative stress. The results support the effectiveness of MQ as a cognitive enhancer, and highlight the value of a multi-target strategy to address the complex nature of cognitive dysfunction in AD.

  11. Pharmacological characterization of memoquin, a multi-target compound for the treatment of Alzheimer's disease.

    Science.gov (United States)

    Capurro, Valeria; Busquet, Perrine; Lopes, Joao Pedro; Bertorelli, Rosalia; Tarozzo, Glauco; Bolognesi, Maria Laura; Piomelli, Daniele; Reggiani, Angelo; Cavalli, Andrea

    2013-01-01

    Alzheimer's disease (AD) is characterized by progressive loss of cognitive function, dementia and altered behavior. Over 30 million people worldwide suffer from AD and available therapies are still palliative rather than curative. Recently, Memoquin (MQ), a quinone-bearing polyamine compound, has emerged as a promising anti-AD lead candidate, mainly thanks to its multi-target profile. MQ acts as an acetylcholinesterase and β-secretase-1 inhibitor, and also possesses anti-amyloid and anti-oxidant properties. Despite this potential interest, in vivo behavioral studies with MQ have been limited. Here, we report on in vivo studies with MQ (acute and sub-chronic treatments; 7-15 mg/kg per os) carried out using two different mouse models: i) scopolamine- and ii) beta-amyloid peptide- (Aβ-) induced amnesia. Several aspects related to memory were examined using the T-maze, the Morris water maze, the novel object recognition, and the passive avoidance tasks. At the dose of 15 mg/kg, MQ was able to rescue all tested aspects of cognitive impairment including spatial, episodic, aversive, short and long-term memory in both scopolamine- and Aβ-induced amnesia models. Furthermore, when tested in primary cortical neurons, MQ was able to fully prevent the Aβ-induced neurotoxicity mediated by oxidative stress. The results support the effectiveness of MQ as a cognitive enhancer, and highlight the value of a multi-target strategy to address the complex nature of cognitive dysfunction in AD.

  12. Multi-Targeted Antithrombotic Therapy for Total Artificial Heart Device Patients.

    Science.gov (United States)

    Ramirez, Angeleah; Riley, Jeffrey B; Joyce, Lyle D

    2016-03-01

    To prevent thrombotic or bleeding events in patients receiving a total artificial heart (TAH), agents have been used to avoid adverse events. The purpose of this article is to outline the adoption and results of a multi-targeted antithrombotic clinical procedure guideline (CPG) for TAH patients. Based on literature review of TAH anticoagulation and multiple case series, a CPG was designed to prescribe the use of multiple pharmacological agents. Total blood loss, Thromboelastograph(®) (TEG), and platelet light-transmission aggregometry (LTA) measurements were conducted on 13 TAH patients during the first 2 weeks of support in our institution. Target values and actual medians for postimplant days 1, 3, 7, and 14 were calculated for kaolinheparinase TEG, kaolin TEG, LTA, and estimated blood loss. Protocol guidelines were followed and anticoagulation management reduced bleeding and prevented thrombus formation as well as thromboembolic events in TAH patients postimplantation. The patients in this study were susceptible to a variety of possible complications such as mechanical device issues, thrombotic events, infection, and bleeding. Among them all it was clear that patients were at most risk for bleeding, particularly on postoperative days 1 through 3. However, bleeding was reduced into postoperative days 3 and 7, indicating that acceptable hemostasis was achieved with the anticoagulation protocol. The multidisciplinary, multi-targeted anticoagulation clinical procedure guideline was successful to maintain adequate antithrombotic therapy for TAH patients.

  13. PMHT Approach for Multi-Target Multi-Sensor Sonar Tracking in Clutter.

    Science.gov (United States)

    Li, Xiaohua; Li, Yaan; Yu, Jing; Chen, Xiao; Dai, Miao

    2015-11-06

    Multi-sensor sonar tracking has many advantages, such as the potential to reduce the overall measurement uncertainty and the possibility to hide the receiver. However, the use of multi-target multi-sensor sonar tracking is challenging because of the complexity of the underwater environment, especially the low target detection probability and extremely large number of false alarms caused by reverberation. In this work, to solve the problem of multi-target multi-sensor sonar tracking in the presence of clutter, a novel probabilistic multi-hypothesis tracker (PMHT) approach based on the extended Kalman filter (EKF) and unscented Kalman filter (UKF) is proposed. The PMHT can efficiently handle the unknown measurements-to-targets and measurements-to-transmitters data association ambiguity. The EKF and UKF are used to deal with the high degree of nonlinearity in the measurement model. The simulation results show that the proposed algorithm can improve the target tracking performance in a cluttered environment greatly, and its computational load is low.

  14. Multi-target-qubit unconventional geometric phase gate in a multi-cavity system.

    Science.gov (United States)

    Liu, Tong; Cao, Xiao-Zhi; Su, Qi-Ping; Xiong, Shao-Jie; Yang, Chui-Ping

    2016-02-22

    Cavity-based large scale quantum information processing (QIP) may involve multiple cavities and require performing various quantum logic operations on qubits distributed in different cavities. Geometric-phase-based quantum computing has drawn much attention recently, which offers advantages against inaccuracies and local fluctuations. In addition, multiqubit gates are particularly appealing and play important roles in QIP. We here present a simple and efficient scheme for realizing a multi-target-qubit unconventional geometric phase gate in a multi-cavity system. This multiqubit phase gate has a common control qubit but different target qubits distributed in different cavities, which can be achieved using a single-step operation. The gate operation time is independent of the number of qubits and only two levels for each qubit are needed. This multiqubit gate is generic, e.g., by performing single-qubit operations, it can be converted into two types of significant multi-target-qubit phase gates useful in QIP. The proposal is quite general, which can be used to accomplish the same task for a general type of qubits such as atoms, NV centers, quantum dots, and superconducting qubits.

  15. Multi-target Wastage Phenomena on Steam Generator Tubes During an SWR Event

    International Nuclear Information System (INIS)

    Jeong, Ji Young; Kim, Jong Man; Kim, Tae Joon; Eoh, Jae Hyuk; Choi, Jong Hyeun; Lee, Yong Bum

    2011-01-01

    The Korean sodium cooled fast reactor, KALIMER- 600 (Korea Advanced LIquid MEtal Reactor) of which the electric output is 600MWe, was developed. The steam generator (SG) of this system is a shell-and-tube type counter-current flow heat exchanger, which is vertically oriented with fixed tube-sheets. A direct heat exchange occurs between the shell-side sodium and the tube-side water at the SG unit. Feed-water enters the inlet nozzle at the lower part of the unit and it flows upward along the helically coiled heat transfer tubes. The inflow sodium is cooled down at the bundle region and then flows out through the sodium outlet nozzle at the bottom of the unit. The typical configuration of the KALIMER-600 SG is shown in Figure 1. In a steam generator, sodium and water are separated by the heat transfer tube wall and it makes a strong pressure boundary between the shell-side sodium and the tube-side water/steam. For this reason, if there is a small hole or crack, even with a pin hole, on heat transfer tubes, a large amount of water/steam would leak into the liquid sodium due to the high pressure difference more than 150 bars, and an exothermic sodium-water chemical reaction takes place as a result. This type of sodium-water reaction (SWR) has been considered as one of the most important safety issues to be resolved. From previous studies, it was obviously figured out that the number of ruptured tubes during an SWR event is one of the most significant factors to determine the temperature and pressure transient. Any subsequent tube rupture behavior in the vicinity of the initially postulated single ruptured tube should be evaluated by considering the single- and multi-target wastage phenomena. Wastage is defined as damage to the structural material (e.g. heat transfer tubes) due to an impingement of the highly corrosive reaction product. Since the impingement may cause wastage of the neighboring heat transfer tubes, a subsequent tube failure can occur in a very short time

  16. The Development and Application of the Magnetron,

    Science.gov (United States)

    1982-03-31

    of *medicine. The power of the magnetron used is from several tens of watts to several hundred watts. Microwave physiotherapy has been used in...clinical practice for the fast cure of arthritis , rheumatism and the subsidence of swelling. Therapeutic results have been excellent. In recent years

  17. Image-Based Multi-Target Tracking through Multi-Bernoulli Filtering with Interactive Likelihoods

    Directory of Open Access Journals (Sweden)

    Anthony Hoak

    2017-03-01

    Full Text Available We develop an interactive likelihood (ILH for sequential Monte Carlo (SMC methods for image-based multiple target tracking applications. The purpose of the ILH is to improve tracking accuracy by reducing the need for data association. In addition, we integrate a recently developed deep neural network for pedestrian detection along with the ILH with a multi-Bernoulli filter. We evaluate the performance of the multi-Bernoulli filter with the ILH and the pedestrian detector in a number of publicly available datasets (2003 PETS INMOVE, Australian Rules Football League (AFL and TUD-Stadtmitte using standard, well-known multi-target tracking metrics (optimal sub-pattern assignment (OSPA and classification of events, activities and relationships for multi-object trackers (CLEAR MOT. In all datasets, the ILH term increases the tracking accuracy of the multi-Bernoulli filter.

  18. Multi-targeted and aggressive treatment of patients with type 2 diabetes at high risk

    DEFF Research Database (Denmark)

    Gaede, P; Pedersen, O

    2005-01-01

    Results from many single risk factor intervention trials and the multi-targeted Steno-2 trial in the last few years have provided a strong case that management of type 2 diabetes in all age groups requires a structured and intensified approach that is far more than just glucocentric, an approach...... addressing additional cardiovascular risk factors including hypertension, dyslipidaemia, sedentary behaviour, smoking and dietary habits causing insulin resistance and pro-inflammation. This type of integrated therapy applied for almost 8 years to high-risk type 2 diabetic patients has cut the relative risk......-driven polypharmacy and simple but focused behaviour modelling with continuous education, motivation and trouble-shooting for treatment barriers identified for the patient and the care giver. It is high time we transfer these experiences and major health benefits gained in the 'green house' of controlled clinical...

  19. A PZT Actuated Triple-Finger Gripper for Multi-Target Micromanipulation

    Directory of Open Access Journals (Sweden)

    Tao Chen

    2017-01-01

    Full Text Available This paper presents a triple-finger gripper driven by a piezoceramic (PZT transducer for multi-target micromanipulation. The gripper consists of three fingers assembled on adjustable pedestals with flexible hinges for a large adjustable range. Each finger has a PZT actuator, an amplifying structure, and a changeable end effector. The moving trajectories of single and double fingers were calculated and finite element analyses were performed to verify the reliability of the structures. In the gripping experiment, various end effectors of the fingers such as tungsten probes and fibers were tested, and different micro-objects such as glass hollow spheres and iron spheres with diameters ranging from 10 to 800 μm were picked and released. The output resolution is 145 nm/V, and the driven displacement range of the gripper is 43.4 μm. The PZT actuated triple-finger gripper has superior adaptability, high efficiency, and a low cost.

  20. A multi target approach to control chemical reactions in their inhomogeneous solvent environment

    International Nuclear Information System (INIS)

    Keefer, Daniel; Thallmair, Sebastian; Zauleck, Julius P P; Vivie-Riedle, Regina de

    2015-01-01

    Shaped laser pulses offer a powerful tool to manipulate molecular quantum systems. Their application to chemical reactions in solution is a promising concept to redesign chemical synthesis. Along this road, theoretical developments to include the solvent surrounding are necessary. An appropriate theoretical treatment is helpful to understand the underlying mechanisms. In our approach we simulate the solvent by randomly selected snapshots from molecular dynamics trajectories. We use multi target optimal control theory to optimize pulses for the various arrangements of explicit solvent molecules simultaneously. This constitutes a major challenge for the control algorithm, as the solvent configurations introduce a large inhomogeneity to the potential surfaces. We investigate how the algorithm handles the new challenges and how well the controllability of the system is preserved with increasing complexity. Additionally, we introduce a way to statistically estimate the efficiency of the optimized laser pulses in the complete thermodynamical ensemble. (paper)

  1. Image-Based Multi-Target Tracking through Multi-Bernoulli Filtering with Interactive Likelihoods.

    Science.gov (United States)

    Hoak, Anthony; Medeiros, Henry; Povinelli, Richard J

    2017-03-03

    We develop an interactive likelihood (ILH) for sequential Monte Carlo (SMC) methods for image-based multiple target tracking applications. The purpose of the ILH is to improve tracking accuracy by reducing the need for data association. In addition, we integrate a recently developed deep neural network for pedestrian detection along with the ILH with a multi-Bernoulli filter. We evaluate the performance of the multi-Bernoulli filter with the ILH and the pedestrian detector in a number of publicly available datasets (2003 PETS INMOVE, Australian Rules Football League (AFL) and TUD-Stadtmitte) using standard, well-known multi-target tracking metrics (optimal sub-pattern assignment (OSPA) and classification of events, activities and relationships for multi-object trackers (CLEAR MOT)). In all datasets, the ILH term increases the tracking accuracy of the multi-Bernoulli filter.

  2. Multi-Robot, Multi-Target Particle Swarm Optimization Search in Noisy Wireless Environments

    Energy Technology Data Exchange (ETDEWEB)

    Kurt Derr; Milos Manic

    2009-05-01

    Multiple small robots (swarms) can work together using Particle Swarm Optimization (PSO) to perform tasks that are difficult or impossible for a single robot to accomplish. The problem considered in this paper is exploration of an unknown environment with the goal of finding a target(s) at an unknown location(s) using multiple small mobile robots. This work demonstrates the use of a distributed PSO algorithm with a novel adaptive RSS weighting factor to guide robots for locating target(s) in high risk environments. The approach was developed and analyzed on multiple robot single and multiple target search. The approach was further enhanced by the multi-robot-multi-target search in noisy environments. The experimental results demonstrated how the availability of radio frequency signal can significantly affect robot search time to reach a target.

  3. AVN-101: A Multi-Target Drug Candidate for the Treatment of CNS Disorders.

    Science.gov (United States)

    Ivachtchenko, Alexandre V; Lavrovsky, Yan; Okun, Ilya

    2016-05-25

    Lack of efficacy of many new highly selective and specific drug candidates in treating diseases with poorly understood or complex etiology, as are many of central nervous system (CNS) diseases, encouraged an idea of developing multi-modal (multi-targeted) drugs. In this manuscript, we describe molecular pharmacology, in vitro ADME, pharmacokinetics in animals and humans (part of the Phase I clinical studies), bio-distribution, bioavailability, in vivo efficacy, and safety profile of the multimodal drug candidate, AVN-101. We have carried out development of a next generation drug candidate with a multi-targeted mechanism of action, to treat CNS disorders. AVN-101 is a very potent 5-HT7 receptor antagonist (Ki = 153 pM), with slightly lesser potency toward 5-HT6, 5-HT2A, and 5HT-2C receptors (Ki = 1.2-2.0 nM). AVN-101 also exhibits a rather high affinity toward histamine H1 (Ki = 0.58 nM) and adrenergic α2A, α2B, and α2C (Ki = 0.41-3.6 nM) receptors. AVN-101 shows a good oral bioavailability and facilitated brain-blood barrier permeability, low toxicity, and reasonable efficacy in animal models of CNS diseases. The Phase I clinical study indicates the AVN-101 to be well tolerated when taken orally at doses of up to 20 mg daily. It does not dramatically influence plasma and urine biochemistry, nor does it prolong QT ECG interval, thus indicating low safety concerns. The primary therapeutic area for AVN-101 to be tested in clinical trials would be Alzheimer's disease. However, due to its anxiolytic and anti-depressive activities, there is a strong rational for it to also be studied in such diseases as general anxiety disorders, depression, schizophrenia, and multiple sclerosis.

  4. A network-based multi-target computational estimation scheme for anticoagulant activities of compounds.

    Directory of Open Access Journals (Sweden)

    Qian Li

    Full Text Available BACKGROUND: Traditional virtual screening method pays more attention on predicted binding affinity between drug molecule and target related to a certain disease instead of phenotypic data of drug molecule against disease system, as is often less effective on discovery of the drug which is used to treat many types of complex diseases. Virtual screening against a complex disease by general network estimation has become feasible with the development of network biology and system biology. More effective methods of computational estimation for the whole efficacy of a compound in a complex disease system are needed, given the distinct weightiness of the different target in a biological process and the standpoint that partial inhibition of several targets can be more efficient than the complete inhibition of a single target. METHODOLOGY: We developed a novel approach by integrating the affinity predictions from multi-target docking studies with biological network efficiency analysis to estimate the anticoagulant activities of compounds. From results of network efficiency calculation for human clotting cascade, factor Xa and thrombin were identified as the two most fragile enzymes, while the catalytic reaction mediated by complex IXa:VIIIa and the formation of the complex VIIIa:IXa were recognized as the two most fragile biological matter in the human clotting cascade system. Furthermore, the method which combined network efficiency with molecular docking scores was applied to estimate the anticoagulant activities of a serial of argatroban intermediates and eight natural products respectively. The better correlation (r = 0.671 between the experimental data and the decrease of the network deficiency suggests that the approach could be a promising computational systems biology tool to aid identification of anticoagulant activities of compounds in drug discovery. CONCLUSIONS: This article proposes a network-based multi-target computational estimation

  5. A network-based multi-target computational estimation scheme for anticoagulant activities of compounds.

    Science.gov (United States)

    Li, Qian; Li, Xudong; Li, Canghai; Chen, Lirong; Song, Jun; Tang, Yalin; Xu, Xiaojie

    2011-03-22

    Traditional virtual screening method pays more attention on predicted binding affinity between drug molecule and target related to a certain disease instead of phenotypic data of drug molecule against disease system, as is often less effective on discovery of the drug which is used to treat many types of complex diseases. Virtual screening against a complex disease by general network estimation has become feasible with the development of network biology and system biology. More effective methods of computational estimation for the whole efficacy of a compound in a complex disease system are needed, given the distinct weightiness of the different target in a biological process and the standpoint that partial inhibition of several targets can be more efficient than the complete inhibition of a single target. We developed a novel approach by integrating the affinity predictions from multi-target docking studies with biological network efficiency analysis to estimate the anticoagulant activities of compounds. From results of network efficiency calculation for human clotting cascade, factor Xa and thrombin were identified as the two most fragile enzymes, while the catalytic reaction mediated by complex IXa:VIIIa and the formation of the complex VIIIa:IXa were recognized as the two most fragile biological matter in the human clotting cascade system. Furthermore, the method which combined network efficiency with molecular docking scores was applied to estimate the anticoagulant activities of a serial of argatroban intermediates and eight natural products respectively. The better correlation (r = 0.671) between the experimental data and the decrease of the network deficiency suggests that the approach could be a promising computational systems biology tool to aid identification of anticoagulant activities of compounds in drug discovery. This article proposes a network-based multi-target computational estimation method for anticoagulant activities of compounds by

  6. Multi-target consensus circle pursuit for multi-agent systems via a distributed multi-flocking method

    Science.gov (United States)

    Pei, Huiqin; Chen, Shiming; Lai, Qiang

    2016-12-01

    This paper studies the multi-target consensus pursuit problem of multi-agent systems. For solving the problem, a distributed multi-flocking method is designed based on the partial information exchange, which is employed to realise the pursuit of multi-target and the uniform distribution of the number of pursuing agents with the dynamic target. Combining with the proposed circle formation control strategy, agents can adaptively choose the target to form the different circle formation groups accomplishing a multi-target pursuit. The speed state of pursuing agents in each group converges to the same value. A Lyapunov approach is utilised to analyse the stability of multi-agent systems. In addition, a sufficient condition is given for achieving the dynamic target consensus pursuit, and which is then analysed. Finally, simulation results verify the effectiveness of the proposed approaches.

  7. Combined analgesics in (headache) pain therapy: shotgun approach or precise multi-target therapeutics?

    Science.gov (United States)

    Straube, Andreas; Aicher, Bernhard; Fiebich, Bernd L; Haag, Gunther

    2011-03-31

    Pain in general and headache in particular are characterized by a change in activity in brain areas involved in pain processing. The therapeutic challenge is to identify drugs with molecular targets that restore the healthy state, resulting in meaningful pain relief or even freedom from pain. Different aspects of pain perception, i.e. sensory and affective components, also explain why there is not just one single target structure for therapeutic approaches to pain. A network of brain areas ("pain matrix") are involved in pain perception and pain control. This diversification of the pain system explains why a wide range of molecularly different substances can be used in the treatment of different pain states and why in recent years more and more studies have described a superior efficacy of a precise multi-target combination therapy compared to therapy with monotherapeutics. In this article, we discuss the available literature on the effects of several fixed-dose combinations in the treatment of headaches and discuss the evidence in support of the role of combination therapy in the pharmacotherapy of pain, particularly of headaches. The scientific rationale behind multi-target combinations is the therapeutic benefit that could not be achieved by the individual constituents and that the single substances of the combinations act together additively or even multiplicatively and cooperate to achieve a completeness of the desired therapeutic effect.As an example the fixed-dose combination of acetylsalicylic acid (ASA), paracetamol (acetaminophen) and caffeine is reviewed in detail. The major advantage of using such a fixed combination is that the active ingredients act on different but distinct molecular targets and thus are able to act on more signalling cascades involved in pain than most single analgesics without adding more side effects to the therapy. Multitarget therapeutics like combined analgesics broaden the array of therapeutic options, enable the completeness

  8. Combined analgesics in (headache pain therapy: shotgun approach or precise multi-target therapeutics?

    Directory of Open Access Journals (Sweden)

    Fiebich Bernd L

    2011-03-01

    Full Text Available Abstract Background Pain in general and headache in particular are characterized by a change in activity in brain areas involved in pain processing. The therapeutic challenge is to identify drugs with molecular targets that restore the healthy state, resulting in meaningful pain relief or even freedom from pain. Different aspects of pain perception, i.e. sensory and affective components, also explain why there is not just one single target structure for therapeutic approaches to pain. A network of brain areas ("pain matrix" are involved in pain perception and pain control. This diversification of the pain system explains why a wide range of molecularly different substances can be used in the treatment of different pain states and why in recent years more and more studies have described a superior efficacy of a precise multi-target combination therapy compared to therapy with monotherapeutics. Discussion In this article, we discuss the available literature on the effects of several fixed-dose combinations in the treatment of headaches and discuss the evidence in support of the role of combination therapy in the pharmacotherapy of pain, particularly of headaches. The scientific rationale behind multi-target combinations is the therapeutic benefit that could not be achieved by the individual constituents and that the single substances of the combinations act together additively or even multiplicatively and cooperate to achieve a completeness of the desired therapeutic effect. As an example the fixesd-dose combination of acetylsalicylic acid (ASA, paracetamol (acetaminophen and caffeine is reviewed in detail. The major advantage of using such a fixed combination is that the active ingredients act on different but distinct molecular targets and thus are able to act on more signalling cascades involved in pain than most single analgesics without adding more side effects to the therapy. Summary Multitarget therapeutics like combined analgesics broaden

  9. Combined analgesics in (headache) pain therapy: shotgun approach or precise multi-target therapeutics?

    Science.gov (United States)

    2011-01-01

    Background Pain in general and headache in particular are characterized by a change in activity in brain areas involved in pain processing. The therapeutic challenge is to identify drugs with molecular targets that restore the healthy state, resulting in meaningful pain relief or even freedom from pain. Different aspects of pain perception, i.e. sensory and affective components, also explain why there is not just one single target structure for therapeutic approaches to pain. A network of brain areas ("pain matrix") are involved in pain perception and pain control. This diversification of the pain system explains why a wide range of molecularly different substances can be used in the treatment of different pain states and why in recent years more and more studies have described a superior efficacy of a precise multi-target combination therapy compared to therapy with monotherapeutics. Discussion In this article, we discuss the available literature on the effects of several fixed-dose combinations in the treatment of headaches and discuss the evidence in support of the role of combination therapy in the pharmacotherapy of pain, particularly of headaches. The scientific rationale behind multi-target combinations is the therapeutic benefit that could not be achieved by the individual constituents and that the single substances of the combinations act together additively or even multiplicatively and cooperate to achieve a completeness of the desired therapeutic effect. As an example the fixesd-dose combination of acetylsalicylic acid (ASA), paracetamol (acetaminophen) and caffeine is reviewed in detail. The major advantage of using such a fixed combination is that the active ingredients act on different but distinct molecular targets and thus are able to act on more signalling cascades involved in pain than most single analgesics without adding more side effects to the therapy. Summary Multitarget therapeutics like combined analgesics broaden the array of therapeutic

  10. Electron relaxation properties of Ar magnetron plasmas

    Science.gov (United States)

    Xinjing, CAI; Xinxin, WANG; Xiaobing, ZOU

    2018-03-01

    An understanding of electron relaxation properties in plasmas is of importance in the application of magnetrons. An improved multi-term approximation of the Boltzmann equation is employed to study electron transport and relaxation properties in plasmas. Elastic, inelastic and nonconservative collisions between electrons and neutral particles are considered. The expressions for the transport coefficients are obtained using the expansion coefficients and the collision operator term. Numerical solutions of the matrix equations for the expansion coefficients are also investigated. Benchmark calculations of the Reid model are presented to demonstrate the accuracy of the improved multi-term approximation. It is shown that the two-term approximation is generally not accurate enough and the magnetic fields can reduce the anisotropy of the velocity distribution function. The electron relaxation properties of Ar plasmas in magnetrons for various magnetic fields are studied. It is demonstrated that the energy parameters change more slowly than the momentum parameters.

  11. Fuzzy tungsten in a magnetron sputtering device

    Energy Technology Data Exchange (ETDEWEB)

    Petty, T.J., E-mail: tjpetty@liv.ac.uk [Department of Electrical Engineering and Electronics, University of Liverpool, Brownlow Hill, Liverpool, L69 3GJ (United Kingdom); Khan, A. [Pariser Building-G11, School of Mechanical, Aerospace and Civil Engineering, The University of Manchester, Manchester, M13 9PL (United Kingdom); Heil, T. [NiCaL, Block C Waterhouse Building, 1-3 Brownlow Street, Liverpool, L69 3GL (United Kingdom); Bradley, J.W., E-mail: j.w.bradley@liverpool.ac.uk [Department of Electrical Engineering and Electronics, University of Liverpool, Brownlow Hill, Liverpool, L69 3GJ (United Kingdom)

    2016-11-15

    Helium ion induced tungsten nanostructure (tungsten fuzz) has been studied in a magnetron sputtering device. Three parameters were varied, the fluence from 3.4 × 10{sup 23}–3.0 × 10{sup 24} m{sup −2}, the He ion energy from 25 to 70 eV, and the surface temperature from 900 to 1200 K. For each sample, SEM images were captured, and measurements of the fuzz layer thickness, surface roughness, reflectivity, and average structure widths are provided. A cross-over point from pre-fuzz to fully formed fuzz is found at 2.4 ± 0.4 × 10{sup 24} m{sup −2}, and a temperature of 1080 ± 60 K. No significant change was observed in the energy sweep. The fuzz is compared to low fluence fuzz created in the PISCES-A linear plasma device. Magnetron fuzz is less uniform than fuzz created by PISCES-A and with generally larger structure widths. The thicknesses of the magnetron samples follow the original Φ{sup 1/2} relation as opposed to the incubation fluence fit. - Highlights: • Fuzz has been created in a magnetron sputtering device. • Three parameters for fuzz formation have been swept. • A cross-over from pre-fuzz to fully formed fuzz is seen. • Evidence for annealing out at lower temperatures than has been seen before. • Evidence to suggest that fuzz grown in discrete exposures is not consistent with fuzz grown in one long exposure.

  12. Fuzzy tungsten in a magnetron sputtering device

    International Nuclear Information System (INIS)

    Petty, T.J.; Khan, A.; Heil, T.; Bradley, J.W.

    2016-01-01

    Helium ion induced tungsten nanostructure (tungsten fuzz) has been studied in a magnetron sputtering device. Three parameters were varied, the fluence from 3.4 × 10 23 –3.0 × 10 24  m −2 , the He ion energy from 25 to 70 eV, and the surface temperature from 900 to 1200 K. For each sample, SEM images were captured, and measurements of the fuzz layer thickness, surface roughness, reflectivity, and average structure widths are provided. A cross-over point from pre-fuzz to fully formed fuzz is found at 2.4 ± 0.4 × 10 24  m −2 , and a temperature of 1080 ± 60 K. No significant change was observed in the energy sweep. The fuzz is compared to low fluence fuzz created in the PISCES-A linear plasma device. Magnetron fuzz is less uniform than fuzz created by PISCES-A and with generally larger structure widths. The thicknesses of the magnetron samples follow the original Φ 1/2 relation as opposed to the incubation fluence fit. - Highlights: • Fuzz has been created in a magnetron sputtering device. • Three parameters for fuzz formation have been swept. • A cross-over from pre-fuzz to fully formed fuzz is seen. • Evidence for annealing out at lower temperatures than has been seen before. • Evidence to suggest that fuzz grown in discrete exposures is not consistent with fuzz grown in one long exposure.

  13. Crawling and walking infants encounter objects differently in a multi-target environment.

    Science.gov (United States)

    Dosso, Jill A; Boudreau, J Paul

    2014-10-01

    From birth, infants move their bodies in order to obtain information and stimulation from their environment. Exploratory movements are important for the development of an infant's understanding of the world and are well established as being key to cognitive advances. Newly acquired motor skills increase the potential actions available to the infant. However, the way that infants employ potential actions in environments with multiple potential targets is undescribed. The current work investigated the target object selections of infants across a range of self-produced locomotor experience (11- to 14-month-old crawlers and walkers). Infants repeatedly accessed objects among pairs of objects differing in both distance and preference status, some requiring locomotion. Overall, their object actions were found to be sensitive to object preference status; however, the role of object distance in shaping object encounters was moderated by movement status. Crawlers' actions appeared opportunistic and were biased towards nearby objects while walkers' actions appeared intentional and were independent of object position. Moreover, walkers' movements favoured preferred objects more strongly for children with higher levels of self-produced locomotion experience. The multi-target experimental situation used in this work parallels conditions faced by foraging organisms, and infants' behaviours were discussed with respect to optimal foraging theory. There is a complex interplay between infants' agency, locomotor experience, and environment in shaping their motor actions. Infants' movements, in turn, determine the information and experiences offered to infants by their micro-environment.

  14. HCIDL: Human-computer interface description language for multi-target, multimodal, plastic user interfaces

    Directory of Open Access Journals (Sweden)

    Lamia Gaouar

    2018-06-01

    Full Text Available From the human-computer interface perspectives, the challenges to be faced are related to the consideration of new, multiple interactions, and the diversity of devices. The large panel of interactions (touching, shaking, voice dictation, positioning … and the diversification of interaction devices can be seen as a factor of flexibility albeit introducing incidental complexity. Our work is part of the field of user interface description languages. After an analysis of the scientific context of our work, this paper introduces HCIDL, a modelling language staged in a model-driven engineering approach. Among the properties related to human-computer interface, our proposition is intended for modelling multi-target, multimodal, plastic interaction interfaces using user interface description languages. By combining plasticity and multimodality, HCIDL improves usability of user interfaces through adaptive behaviour by providing end-users with an interaction-set adapted to input/output of terminals and, an optimum layout. Keywords: Model driven engineering, Human-computer interface, User interface description languages, Multimodal applications, Plastic user interfaces

  15. UPA-sensitive ACPP-conjugated nanoparticles for multi-targeting therapy of brain glioma.

    Science.gov (United States)

    Zhang, Bo; Zhang, Yujie; Liao, Ziwei; Jiang, Ting; Zhao, Jingjing; Tuo, Yanyan; She, Xiaojian; Shen, Shun; Chen, Jun; Zhang, Qizhi; Jiang, Xinguo; Hu, Yu; Pang, Zhiqing

    2015-01-01

    Now it is well evidenced that tumor growth is a comprehensive result of multiple pathways, and glioma parenchyma cells and stroma cells are closely associated and mutually compensatory. Therefore, drug delivery strategies targeting both of them simultaneously might obtain more promising therapeutic benefits. In the present study, we developed a multi-targeting drug delivery system modified with uPA-activated cell-penetrating peptide (ACPP) for the treatment of brain glioma (ANP). In vitro experiments demonstrated nanoparticles (NP) decorated with cell-penetrating peptide (CPP) or ACPP could significantly improve nanoparticles uptake by C6 glioma cells and nanoparticles penetration into glioma spheroids as compared with traditional NP and thus enhanced the therapeutic effects of its payload when paclitaxel (PTX) was loaded. In vivo imaging experiment revealed that ANP accumulated more specifically in brain glioma site than NP decorated with or without CPP. Brain slides further showed that ACPP contributed to more nanoparticles accumulation in glioma site, and ANP could co-localize not only with glioma parenchyma cells, but also with stroma cells including neo-vascular cells and tumor associated macrophages. The pharmacodynamics results demonstrated ACPP could significantly improve the therapeutic benefits of nanoparticles by significantly prolonging the survival time of glioma bearing mice. In conclusion, the results suggested that nanoparticles modified with uPA-sensitive ACPP could reach multiple types of cells in glioma tissues and provide a novel strategy for glioma targeted therapy.

  16. Molecular investigations of protriptyline as a multi-target directed ligand in Alzheimer's disease.

    Directory of Open Access Journals (Sweden)

    Sneha B Bansode

    Full Text Available Alzheimer's disease (AD is a complex neurodegenerative disorder involving multiple cellular and molecular processes. The discovery of drug molecules capable of targeting multiple factors involved in AD pathogenesis would greatly facilitate in improving therapeutic strategies. The repositioning of existing non-toxic drugs could dramatically reduce the time and costs involved in developmental and clinical trial stages. In this study, preliminary screening of 140 FDA approved nervous system drugs by docking suggested the viability of the tricyclic group of antidepressants against three major AD targets, viz. Acetylcholinesterase (AChE, β-secretase (BACE-1, and amyloid β (Aβ aggregation, with one member, protriptyline, showing highest inhibitory activity. Detailed biophysical assays, together with isothermal calorimetry, fluorescence quenching experiments, kinetic studies and atomic force microscopy established the strong inhibitory activity of protriptyline against all three major targets. The molecular basis of inhibition was supported with comprehensive molecular dynamics simulations. Further, the drug inhibited glycation induced amyloid aggregation, another important causal factor in AD progression. This study has led to the discovery of protriptyline as a potent multi target directed ligand and established its viability as a promising candidate for AD treatment.

  17. ESAM: Endocrine inspired Sensor Activation Mechanism for multi-target tracking in WSNs

    Science.gov (United States)

    Adil Mahdi, Omar; Wahab, Ainuddin Wahid Abdul; Idris, Mohd Yamani Idna; Znaid, Ammar Abu; Khan, Suleman; Al-Mayouf, Yusor Rafid Bahar

    2016-10-01

    Target tracking is a significant application of wireless sensor networks (WSNs) in which deployment of self-organizing and energy efficient algorithms is required. The tracking accuracy increases as more sensor nodes are activated around the target but more energy is consumed. Thus, in this study, we focus on limiting the number of sensors by forming an ad-hoc network that operates autonomously. This will reduce the energy consumption and prolong the sensor network lifetime. In this paper, we propose a fully distributed algorithm, an Endocrine inspired Sensor Activation Mechanism for multi target-tracking (ESAM) which reflecting the properties of real life sensor activation system based on the information circulating principle in the endocrine system of the human body. Sensor nodes in our network are secreting different hormones according to certain rules. The hormone level enables the nodes to regulate an efficient sleep and wake up cycle of nodes to reduce the energy consumption. It is evident from the simulation results that the proposed ESAM in autonomous sensor network exhibits a stable performance without the need of commands from a central controller. Moreover, the proposed ESAM generates more efficient and persistent results as compared to other algorithms for tracking an invading object.

  18. Complex interactions between phytochemicals. The multi-target therapeutic concept of phytotherapy.

    Science.gov (United States)

    Efferth, Thomas; Koch, Egon

    2011-01-01

    Drugs derived from natural resources represent a significant segment of the pharmaceutical market as compared to randomly synthesized compounds. It is a goal of drug development programs to design selective ligands that act on single disease targets to obtain highly effective and safe drugs with low side effects. Although this strategy was successful for many new therapies, there is a marked decline in the number of new drugs introduced into clinical practice over the past decades. One reason for this failure may be due to the fact that the pathogenesis of many diseases is rather multi-factorial in nature and not due to a single cause. Phytotherapy, whose therapeutic efficacy is based on the combined action of a mixture of constituents, offers new treatment opportunities. Because of their biological defence function, plant secondary metabolites act by targeting and disrupting the cell membrane, by binding and inhibiting specific proteins or they adhere to or intercalate into RNA or DNA. Phytotherapeutics may exhibit pharmacological effects by the synergistic or antagonistic interaction of many phytochemicals. Mechanistic reasons for interactions are bioavailability, interference with cellular transport processes, activation of pro-drugs or deactivation of active compounds to inactive metabolites, action of synergistic partners at different points of the same signalling cascade (multi-target effects) or inhibition of binding to target proteins. "-Omics" technologies and systems biology may facilitate unravelling synergistic effects of herbal mixtures.

  19. Multi-Source Multi-Target Dictionary Learning for Prediction of Cognitive Decline.

    Science.gov (United States)

    Zhang, Jie; Li, Qingyang; Caselli, Richard J; Thompson, Paul M; Ye, Jieping; Wang, Yalin

    2017-06-01

    Alzheimer's Disease (AD) is the most common type of dementia. Identifying correct biomarkers may determine pre-symptomatic AD subjects and enable early intervention. Recently, Multi-task sparse feature learning has been successfully applied to many computer vision and biomedical informatics researches. It aims to improve the generalization performance by exploiting the shared features among different tasks. However, most of the existing algorithms are formulated as a supervised learning scheme. Its drawback is with either insufficient feature numbers or missing label information. To address these challenges, we formulate an unsupervised framework for multi-task sparse feature learning based on a novel dictionary learning algorithm. To solve the unsupervised learning problem, we propose a two-stage Multi-Source Multi-Target Dictionary Learning (MMDL) algorithm. In stage 1, we propose a multi-source dictionary learning method to utilize the common and individual sparse features in different time slots. In stage 2, supported by a rigorous theoretical analysis, we develop a multi-task learning method to solve the missing label problem. Empirical studies on an N = 3970 longitudinal brain image data set, which involves 2 sources and 5 targets, demonstrate the improved prediction accuracy and speed efficiency of MMDL in comparison with other state-of-the-art algorithms.

  20. Multi-target camera tracking, hand-off and display LDRD 158819 final report

    International Nuclear Information System (INIS)

    Anderson, Robert J.

    2014-01-01

    Modern security control rooms gather video and sensor feeds from tens to hundreds of cameras. Advanced camera analytics can detect motion from individual video streams and convert unexpected motion into alarms, but the interpretation of these alarms depends heavily upon human operators. Unfortunately, these operators can be overwhelmed when a large number of events happen simultaneously, or lulled into complacency due to frequent false alarms. This LDRD project has focused on improving video surveillance-based security systems by changing the fundamental focus from the cameras to the targets being tracked. If properly integrated, more cameras shouldn't lead to more alarms, more monitors, more operators, and increased response latency but instead should lead to better information and more rapid response times. For the course of the LDRD we have been developing algorithms that take live video imagery from multiple video cameras, identifies individual moving targets from the background imagery, and then displays the results in a single 3D interactive video. In this document we summarize the work in developing this multi-camera, multi-target system, including lessons learned, tools developed, technologies explored, and a description of current capability.

  1. Monoaminergic Mechanisms in Epilepsy May Offer Innovative Therapeutic Opportunity for Monoaminergic Multi-Target Drugs

    Directory of Open Access Journals (Sweden)

    Dubravka Svob Strac

    2016-11-01

    Full Text Available A large body of experimental and clinical evidence has strongly suggested that monoamines play an important role in regulating epileptogenesis, seizure susceptibility, convulsions and comorbid psychiatric disorders commonly seen in people with epilepsy. However, neither the relative significance of individual monoamines nor their interaction has yet been fully clarified due to the complexity of these neurotransmitter systems. In addition, epilepsy is diverse, with many different seizure types and epilepsy syndromes, and the role played by monoamines may vary from one condition to another. In this review, we will focus on the role of serotonin, dopamine, noradrenaline, histamine and melatonin in epilepsy. Recent experimental, clinical and genetic evidence, will be reviewed in consideration of the mutual relationship of monoamines with the other putative neurotransmitters. The complexity of epileptic pathogenesis may explain why the currently available drugs, developed according to the classic drug discovery paradigm of one-molecule-one-target, have turned out to be effective only in a percentage of people with epilepsy. Although no antiepileptic drugs currently target specifically monoaminergic systems, multi-target directed ligands acting on different monoaminergic proteins present on both neurons and glia cells may represent a new approach in the management of seizures and their generation as well as comorbid neuropsychiatric disorders.

  2. Topology of classical molecular optimal control landscapes for multi-target objectives

    Energy Technology Data Exchange (ETDEWEB)

    Joe-Wong, Carlee [Program in Applied and Computational Mathematics, Princeton University, Princeton, New Jersey 08544-1000 (United States); Ho, Tak-San; Rabitz, Herschel, E-mail: hrabitz@princeton.edu [Department of Chemistry, Princeton University, Princeton, New Jersey 08544-1009 (United States); Wu, Rebing [Department of Automation, Tsinghua University, Beijing (China)

    2015-04-21

    This paper considers laser-driven optimal control of an ensemble of non-interacting molecules whose dynamics lie in classical phase space. The molecules evolve independently under control to distinct final states. We consider a control landscape defined in terms of multi-target (MT) molecular states and analyze the landscape as a functional of the control field. The topology of the MT control landscape is assessed through its gradient and Hessian with respect to the control. Under particular assumptions, the MT control landscape is found to be free of traps that could hinder reaching the objective. The Hessian associated with an optimal control field is shown to have finite rank, indicating an inherent degree of robustness to control noise. Both the absence of traps and rank of the Hessian are shown to be analogous to the situation of specifying multiple targets for an ensemble of quantum states. Numerical simulations are presented to illustrate the classical landscape principles and further characterize the system behavior as the control field is optimized.

  3. Multi-target camera tracking, hand-off and display LDRD 158819 final report

    Energy Technology Data Exchange (ETDEWEB)

    Anderson, Robert J. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2014-10-01

    Modern security control rooms gather video and sensor feeds from tens to hundreds of cameras. Advanced camera analytics can detect motion from individual video streams and convert unexpected motion into alarms, but the interpretation of these alarms depends heavily upon human operators. Unfortunately, these operators can be overwhelmed when a large number of events happen simultaneously, or lulled into complacency due to frequent false alarms. This LDRD project has focused on improving video surveillance-based security systems by changing the fundamental focus from the cameras to the targets being tracked. If properly integrated, more cameras shouldn't lead to more alarms, more monitors, more operators, and increased response latency but instead should lead to better information and more rapid response times. For the course of the LDRD we have been developing algorithms that take live video imagery from multiple video cameras, identifies individual moving targets from the background imagery, and then displays the results in a single 3D interactive video. In this document we summarize the work in developing this multi-camera, multi-target system, including lessons learned, tools developed, technologies explored, and a description of current capability.

  4. Multi-Target Camera Tracking, Hand-off and Display LDRD 158819 Final Report

    Energy Technology Data Exchange (ETDEWEB)

    Anderson, Robert J. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States). Robotic and Security Systems Dept.

    2014-10-01

    Modern security control rooms gather video and sensor feeds from tens to hundreds of cameras. Advanced camera analytics can detect motion from individual video streams and convert unexpected motion into alarms, but the interpretation of these alarms depends heavily upon human operators. Unfortunately, these operators can be overwhelmed when a large number of events happen simultaneously, or lulled into complacency due to frequent false alarms. This LDRD project has focused on improving video surveillance-based security systems by changing the fundamental focus from the cameras to the targets being tracked. If properly integrated, more cameras shouldn’t lead to more alarms, more monitors, more operators, and increased response latency but instead should lead to better information and more rapid response times. For the course of the LDRD we have been developing algorithms that take live video imagery from multiple video cameras, identify individual moving targets from the background imagery, and then display the results in a single 3D interactive video. In this document we summarize the work in developing this multi-camera, multi-target system, including lessons learned, tools developed, technologies explored, and a description of current capability.

  5. Monoaminergic Mechanisms in Epilepsy May Offer Innovative Therapeutic Opportunity for Monoaminergic Multi-Target Drugs

    Science.gov (United States)

    Svob Strac, Dubravka; Pivac, Nela; Smolders, Ilse J.; Fogel, Wieslawa A.; De Deurwaerdere, Philippe; Di Giovanni, Giuseppe

    2016-01-01

    A large body of experimental and clinical evidence has strongly suggested that monoamines play an important role in regulating epileptogenesis, seizure susceptibility, convulsions, and comorbid psychiatric disorders commonly seen in people with epilepsy (PWE). However, neither the relative significance of individual monoamines nor their interaction has yet been fully clarified due to the complexity of these neurotransmitter systems. In addition, epilepsy is diverse, with many different seizure types and epilepsy syndromes, and the role played by monoamines may vary from one condition to another. In this review, we will focus on the role of serotonin, dopamine, noradrenaline, histamine, and melatonin in epilepsy. Recent experimental, clinical, and genetic evidence will be reviewed in consideration of the mutual relationship of monoamines with the other putative neurotransmitters. The complexity of epileptic pathogenesis may explain why the currently available drugs, developed according to the classic drug discovery paradigm of “one-molecule-one-target,” have turned out to be effective only in a percentage of PWE. Although, no antiepileptic drugs currently target specifically monoaminergic systems, multi-target directed ligands acting on different monoaminergic proteins, present on both neurons and glia cells, may represent a new approach in the management of seizures, and their generation as well as comorbid neuropsychiatric disorders. PMID:27891070

  6. ATP as a Multi-target Danger Signal in the Brain

    Directory of Open Access Journals (Sweden)

    Ricardo J Rodrigues

    2015-04-01

    Full Text Available ATP is released in an activity-dependent manner from different cell types in the brain, fulfilling different roles as a neurotransmitter, neuromodulator, astrocyte-to-neuron communication, propagating astrocytic responses and formatting microglia responses. This involves the activation of different ATP P2 receptors (P2R as well as adenosine receptors upon extracellular ATP catabolism by ecto-nucleotidases. Notably, brain noxious stimuli trigger a sustained increase of extracellular ATP, which plays a key role as danger signal in the brain. This involves a combined action of extracellular ATP in different cell types, namely increasing the susceptibility of neurons to damage, promoting astrogliosis and recruiting and formatting microglia to mount neuroinflammatory responses. Such actions involve the activation of different receptors, as heralded by neuroprotective effects resulting from blockade mainly of P2X7R, P2Y1R and adenosine A2A receptors (A2AR, which hierarchy, cooperation and/or redundancy is still not resolved. These pleiotropic functions of ATP as a danger signal in brain damage prompt a therapeutic interest to multi-target different purinergic receptors to provide maximal opportunities for neuroprotection.

  7. A PLL based automated magnetron tuning mechanism for electron accelerators

    International Nuclear Information System (INIS)

    Khan, A M; Mahfooz, Mohammed; Sanjeev, Ganesh

    2008-01-01

    In this paper we report on a control system developed to tune the magnetron frequency to get the maximum beam pulse in a Microtron (an electron accelerator facility at Mangalore University). The control system so designed consists of a Microcontroller Unit (MCU), a Phase Locked Loop (PLL) and a Digital to Analog Converter (DAC) to track and tune the magnetron frequency. A PLL is used to track the deviation of the magnetron output frequency, and by monitoring the reflected wave voltage level, the microcontroller unit tunes the magnetron with the help of a tuner mechanism connected through a stepper motor.

  8. A PLL based automated magnetron tuning mechanism for electron accelerators

    Energy Technology Data Exchange (ETDEWEB)

    Khan, A M; Mahfooz, Mohammed [Dept. of Electronics, Mangalore University, Mangalagangotri, Karnataka State, India - 574 199 (India); Sanjeev, Ganesh [Microtron Centre, Mangalore University, Mangalagangotri, Karnataka State, India - 574 199 (India)], E-mail: mahfooz_81@yahoo.com

    2008-09-15

    In this paper we report on a control system developed to tune the magnetron frequency to get the maximum beam pulse in a Microtron (an electron accelerator facility at Mangalore University). The control system so designed consists of a Microcontroller Unit (MCU), a Phase Locked Loop (PLL) and a Digital to Analog Converter (DAC) to track and tune the magnetron frequency. A PLL is used to track the deviation of the magnetron output frequency, and by monitoring the reflected wave voltage level, the microcontroller unit tunes the magnetron with the help of a tuner mechanism connected through a stepper motor.

  9. Nanostructured multilayers of TiN/ZrN obtained by magnetron sputtering

    International Nuclear Information System (INIS)

    Caicedo A, J.C.; Bejarano G, G.; Gomez, M.E.; Prieto, P.; Cortez, C.; Munoz, J.

    2007-01-01

    In order to find an industrial application for thin films of TiN and ZrN monolayers, as well as TiN/ZrN multilayers were deposited onto silicon (100) and AISI 5160 steel substrates by r.f. (13.56 MHz) multi-target magnetron sputtering from high-purity (99.5%) Ti and (99.5%) Zr targets in an Ar (93%)/N 2 (7%) gas mixture. For their deposition, we applied a substrate bias voltage of -100 V and a target power of 350 W. The films were deposited at a pressure of 6x10 -3 mbar and a temperature of 250 C. The structure, composition, morphology, and topography were characterized by, XRD, FTIR, SEM, AFM, and optical microscopy. Mechanical properties like hardness and elastic modulus were determined by Nanoindentation. Hardness and elastic modulus of the films increased proportionally to the number of bilayers. Finally, cutting tools were coated with 1, 2, 3, 4, 5, 6, 7, and 8 bilayers of TiN/ZrN. Cutting tests on paper blades were conducted. Increased cut quality performance was observed for cutting tools coated with 8 bilayers, as compared to uncoated tools. This work opens the possibility to use coated AISI 5160 as cutting tools for the paper industry, reducing the import of expensive high-quality tool steel. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  10. Nanostructured multilayers of TiN/ZrN obtained by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Caicedo A., J.C. [CDT ASTIN, SENA Regional Valle, Cali (Colombia); Grupo de Peliculas Delgadas, Universidad del Valle (Colombia); Centro de Excelencia en Nuevos Materiales, CENM, Universidad del Valle (Colombia); Bejarano G., G. [CDT ASTIN, SENA Regional Valle, Cali (Colombia); Group of Corrosion and Protection, Antioquia University, Medellin (Colombia); Gomez, M.E. [Grupo de Peliculas Delgadas, Universidad del Valle (Colombia); Centro de Excelencia en Nuevos Materiales, CENM, Universidad del Valle (Colombia); Prieto, P. [Centro de Excelencia en Nuevos Materiales, CENM, Universidad del Valle (Colombia); Cortez, C.; Munoz, J. [Centro de Investigacion y Estudios Avanzados del CINVESTAV-IPN, Queretaro (Mexico)

    2007-07-01

    In order to find an industrial application for thin films of TiN and ZrN monolayers, as well as TiN/ZrN multilayers were deposited onto silicon (100) and AISI 5160 steel substrates by r.f. (13.56 MHz) multi-target magnetron sputtering from high-purity (99.5%) Ti and (99.5%) Zr targets in an Ar (93%)/N{sub 2} (7%) gas mixture. For their deposition, we applied a substrate bias voltage of -100 V and a target power of 350 W. The films were deposited at a pressure of 6x10{sup -3} mbar and a temperature of 250 C. The structure, composition, morphology, and topography were characterized by, XRD, FTIR, SEM, AFM, and optical microscopy. Mechanical properties like hardness and elastic modulus were determined by Nanoindentation. Hardness and elastic modulus of the films increased proportionally to the number of bilayers. Finally, cutting tools were coated with 1, 2, 3, 4, 5, 6, 7, and 8 bilayers of TiN/ZrN. Cutting tests on paper blades were conducted. Increased cut quality performance was observed for cutting tools coated with 8 bilayers, as compared to uncoated tools. This work opens the possibility to use coated AISI 5160 as cutting tools for the paper industry, reducing the import of expensive high-quality tool steel. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  11. Multi-target directed donepezil-like ligands for Alzheimer's disease

    Directory of Open Access Journals (Sweden)

    Mercedes eUnzeta

    2016-05-01

    Full Text Available Alzheimer's disease (AD, the most common form of adult onset dementia, is an age-related neurodegenerative disorder characterized by progressive memory loss, decline in language skills and other cognitive impairments. Although its etiology is not completely known, several factors including deficits of acetylcholine, β-amyloid deposits, τ-protein phosphorylation, oxidative stress and neuroinflammation are considered to play significant roles in the pathophysiology of this disease. For a long time, AD patients have been treated with acetylcholinesterase inhibitors such as donepezil (Aricept® but with limited therapeutic success. This might be due to the complex multifactorial nature of AD, a fact that has prompted the design of new Multi-Target-Directed Ligands (MTDL based on the one molecule, multiple targets paradigm. Thus, in this context, different series of novel multifunctional molecules with antioxidant, anti-amyloid, anti-inflammatory and metal-chelating properties able to interact with multiple enzymes of therapeutic interest in AD pathology including acetylcholinesterase, butyrylcholinesterase and monoamine oxidases A and B have been designed and assessed biologically. This review describes the multiple targets, the design rationale and an in-house MTDL library, bearing the N-benzylpiperidine motif present in donepezil, linked to different heterocyclic ring systems (indole, pyridine or 8-hydroxyquinoline with special emphasis on compound ASS234, an N-propargylindole derivative. The description of the in vitro biological properties of the compounds and discussion of the corresponding structure-activity-relationships allows us to highlight new issues for the identification of more efficient MTDL for use in AD therapy.

  12. Harnessing the fruits of nature for the development of multi-targeted cancer therapeutics.

    Science.gov (United States)

    Sarkar, Fazlul H; Li, Yiwei

    2009-11-01

    Cancer cells exhibit deregulation in multiple cellular signaling pathways. Therefore, treatments using specific agents that target only one pathway usually fail in cancer therapy. The combination treatments using chemotherapeutic agents with distinct molecular mechanisms are considered more promising for higher efficacy; however, using multiple agents contributes to added toxicity. Emerging evidence has shown that some "natural products" such as isoflavones, indole-3-carbinol (I3C) and its in vivo dimeric product 3,3'-diindolylmethane (DIM), and curcumin among many others, have growth inhibitory and apoptosis inducing effects on human and animal cancer cells mediated by targeting multiple cellular signaling pathways in vitro without causing unwanted toxicity in normal cells. Therefore, these non-toxic "natural products" from natural resources could be useful in combination with conventional chemotherapeutic agents for the treatment of human malignancies with lower toxicity and higher efficacy. In fact, recently increasing evidence from pre-clinical in vivo studies and clinical trials have shown some success in support of the use of rational design of multi-targeted therapies for the treatment of cancers using conventional chemotherapeutic agents in combination with "natural products". These studies have provided promising results and further opened-up newer avenues for cancer therapy. In this review article, we have succinctly summarized the known effects of "natural products" especially by focusing on isoflavones, indole-3-carbinol (I3C) and its in vivo dimeric product 3,3'-diindolylmethane (DIM), and curcumin, and provided a comprehensive view on the molecular mechanisms underlying the principle of cancer therapy using combination of "natural products" with conventional therapeutics.

  13. DEVICE FOR INVESTIGATION OF MAGNETRON AND PULSED-LASER PLASMA

    Directory of Open Access Journals (Sweden)

    A. P. Burmakov

    2012-01-01

    Full Text Available Various modifications of complex pulsed laser and magnetron deposition thin-film structures unit are presented. They include joint and separate variants of layer deposition. Unit realizes the plasma parameters control and enhances the possibility of laser-plasma and magnetron methods of coatings deposition.

  14. A microcontroller based tuning mechanism for the magnetron

    International Nuclear Information System (INIS)

    Khan, A.M.; Mahfooz, M.; Hanumaiah, B.; Ganesh; Siddappa, K.

    2006-01-01

    In this paper we report on a control system developed to tune the magnetron frequency to get the maximum beam pulse in the microtron (electron accelerator facility at Mangalore University). The control system so designed consists of a microcontroller, a phase locked loop (PLL) and a digital to analog converter (DAC) to control the magnetron frequency. The voltage value given by the microcontroller through the DAC decides the reference frequency. The PLL gives the error voltage whenever there is difference between the reference and the magnetron frequencies. The microcontroller unit tracks the error voltage and tunes the magnetron with the help of a tuner mechanism connected through a stepper motor. The microcontroller also monitors the beam current level and accordingly adjusts the reference frequency to successfully tune the magnetron. (author)

  15. Improved genome-scale multi-target virtual screening via a novel collaborative filtering approach to cold-start problem.

    Science.gov (United States)

    Lim, Hansaim; Gray, Paul; Xie, Lei; Poleksic, Aleksandar

    2016-12-13

    Conventional one-drug-one-gene approach has been of limited success in modern drug discovery. Polypharmacology, which focuses on searching for multi-targeted drugs to perturb disease-causing networks instead of designing selective ligands to target individual proteins, has emerged as a new drug discovery paradigm. Although many methods for single-target virtual screening have been developed to improve the efficiency of drug discovery, few of these algorithms are designed for polypharmacology. Here, we present a novel theoretical framework and a corresponding algorithm for genome-scale multi-target virtual screening based on the one-class collaborative filtering technique. Our method overcomes the sparseness of the protein-chemical interaction data by means of interaction matrix weighting and dual regularization from both chemicals and proteins. While the statistical foundation behind our method is general enough to encompass genome-wide drug off-target prediction, the program is specifically tailored to find protein targets for new chemicals with little to no available interaction data. We extensively evaluate our method using a number of the most widely accepted gene-specific and cross-gene family benchmarks and demonstrate that our method outperforms other state-of-the-art algorithms for predicting the interaction of new chemicals with multiple proteins. Thus, the proposed algorithm may provide a powerful tool for multi-target drug design.

  16. Biological evaluation and molecular docking of Rhein as a multi-targeted radiotherapy sensitization agent of nasopharyngeal carcinoma

    Science.gov (United States)

    Su, Zhengying; Tian, Wei; Li, Jing; Wang, Chunmiao; Pan, Zhiyu; Li, Danrong; Hou, Huaxin

    2017-11-01

    Radiation resistance of nasopharyngeal carcinoma (NPC) is a joint effect caused by complex molecular mechanisms. The development of multi-target radiotherapy sensitization agents offered a promising method for the treatment of NPC. In this work, the probability of Rhein to be a multi-target radiotherapy sensitization agent was explored through computer aid virtual screening by inverse docking study. In order to validate the accuracy of the computational results, radiotherapy sensitization of Rhein to NPC cells and its effects on the expression of target proteins were evaluated separately by CCK8 assay and Western blotting analysis. Our result demonstrated that Rhein possessed strong binding affinity with RAC1 and HSP90. No cytotoxic concentration of Rhein had radiosensitization effect on nasopharyngeal carcinoma CNE1 cells. After treatment with Rhein and 2Gy radiation, the expression of RAC1 upregulated and the expression of HSP90 down-regulated in cells. Based on the above data, Rhein is likely to become an attractive lead compound for the future design of multi-target radiotherapy sensitization agents.

  17. Combinatorial support vector machines approach for virtual screening of selective multi-target serotonin reuptake inhibitors from large compound libraries.

    Science.gov (United States)

    Shi, Z; Ma, X H; Qin, C; Jia, J; Jiang, Y Y; Tan, C Y; Chen, Y Z

    2012-02-01

    Selective multi-target serotonin reuptake inhibitors enhance antidepressant efficacy. Their discovery can be facilitated by multiple methods, including in silico ones. In this study, we developed and tested an in silico method, combinatorial support vector machines (COMBI-SVMs), for virtual screening (VS) multi-target serotonin reuptake inhibitors of seven target pairs (serotonin transporter paired with noradrenaline transporter, H(3) receptor, 5-HT(1A) receptor, 5-HT(1B) receptor, 5-HT(2C) receptor, melanocortin 4 receptor and neurokinin 1 receptor respectively) from large compound libraries. COMBI-SVMs trained with 917-1951 individual target inhibitors correctly identified 22-83.3% (majority >31.1%) of the 6-216 dual inhibitors collected from literature as independent testing sets. COMBI-SVMs showed moderate to good target selectivity in misclassifying as dual inhibitors 2.2-29.8% (majority virtual hits correlate with the reported effects of their predicted targets. COMBI-SVM is potentially useful for searching selective multi-target agents without explicit knowledge of these agents. Copyright © 2011 Elsevier Inc. All rights reserved.

  18. Systems biology approaches and tools for analysis of interactomes and multi-target drugs.

    Science.gov (United States)

    Schrattenholz, André; Groebe, Karlfried; Soskic, Vukic

    2010-01-01

    diseases" remains a most pressing medical need. Currently, a change of paradigm can be observed with regard to a new interest in agents that modulate multiple targets simultaneously, essentially "dirty drugs." Targeting cellular function as a system rather than on the level of the single target, significantly increases the size of the drugable proteome and is expected to introduce novel classes of multi-target drugs with fewer adverse effects and toxicity. Multiple target approaches have recently been used to design medications against atherosclerosis, cancer, depression, psychosis and neurodegenerative diseases. A focussed approach towards "systemic" drugs will certainly require the development of novel computational and mathematical concepts for appropriate modelling of complex data. But the key is the extraction of relevant molecular information from biological systems by implementing rigid statistical procedures to differential proteomic analytics.

  19. Free-time and fixed end-point multi-target optimal control theory: Application to quantum computing

    International Nuclear Information System (INIS)

    Mishima, K.; Yamashita, K.

    2011-01-01

    Graphical abstract: The two-state Deutsch-Jozsa algortihm used to demonstrate the utility of free-time and fixed-end point multi-target optimal control theory. Research highlights: → Free-time and fixed-end point multi-target optimal control theory (FRFP-MTOCT) was constructed. → The features of our theory include optimization of the external time-dependent perturbations with high transition probabilities, that of the temporal duration, the monotonic convergence, and the ability to optimize multiple-laser pulses simultaneously. → The advantage of the theory and a comparison with conventional fixed-time and fixed end-point multi-target optimal control theory (FIFP-MTOCT) are presented by comparing data calculated using the present theory with those published previously [K. Mishima, K. Yamashita, Chem. Phys. 361 (2009) 106]. → The qubit system of our interest consists of two polar NaCl molecules coupled by dipole-dipole interaction. → The calculation examples show that our theory is useful for minor adjustment of the external fields. - Abstract: An extension of free-time and fixed end-point optimal control theory (FRFP-OCT) to monotonically convergent free-time and fixed end-point multi-target optimal control theory (FRFP-MTOCT) is presented. The features of our theory include optimization of the external time-dependent perturbations with high transition probabilities, that of the temporal duration, the monotonic convergence, and the ability to optimize multiple-laser pulses simultaneously. The advantage of the theory and a comparison with conventional fixed-time and fixed end-point multi-target optimal control theory (FIFP-MTOCT) are presented by comparing data calculated using the present theory with those published previously [K. Mishima, K. Yamashita, Chem. Phys. 361, (2009), 106]. The qubit system of our interest consists of two polar NaCl molecules coupled by dipole-dipole interaction. The calculation examples show that our theory is useful for minor

  20. Phase and Frequency Locked Magnetrons for SRF Sources

    International Nuclear Information System (INIS)

    Neubauer, M.; Johnson, R.P.; Popovic, M.; Moretti, A.

    2009-01-01

    Magnetrons are low-cost highly-efficient microwave sources, but they have several limitations, primarily centered about the phase and frequency stability of their output. When the stability requirements are low, such as for medical accelerators or kitchen ovens, magnetrons are the very efficient power source of choice. But for high energy accelerators, because of the need for frequency and phase stability - proton accelerators need 1-2 degrees source phase stability, and electron accelerators need .1-.2 degrees of phase stability - they have rarely been used. We describe a novel variable frequency cavity technique which will be utilized to phase and frequency lock magnetrons.

  1. Unbalanced Cylindrical Magnetron for Accelerating Cavities Coating

    CERN Document Server

    Rosaz, Guillaume; Calatroni, Sergio; Sublet, Alban; Tobarelli, Mauro

    2016-01-01

    We report in this paper the design and qualification of a cylindrical unbalanced magnetron source. The dedicated magnetic assemblies were simulated using a finite element model. A hall-effect magnetic probe was then used to characterize those assemblies and compared to the theoretical magnet profiles. These show a good agreement between the expected and actual values. the qualification of the different magnetic assemblies was then performed by measuring the ion flux density reaching the surface of the sample to be coated using a commercial retarding field energy analyzer. The strongest unbalanced configuration shows an increase from 0.016A.cm^-2 to 0.074A.cm^-2 of the ion flux density reaching the sample surface compared to the standard balanced configuration for a pressure 5.10^-3 mbar and a plasma source power of 300W.

  2. Characterization and Optimization of the Magnetron Directional Amplifier

    National Research Council Canada - National Science Library

    Hatfield, Michael

    1999-01-01

    .... A conventional microwave oven magnetron may be converted into a two-port amplifier capable of delivering over 30 dB of gain, while remaining phase-locked to the input signal over a wide frequency range...

  3. Life test on indigenous s-band pulsed magnetron

    International Nuclear Information System (INIS)

    Wanmode, Y.D.; Shrivastava, P.; Hannurkar, P.R.

    1999-01-01

    A 2 MW S-band pulsed magnetron has been developed under joint collaboration between CAT and CEERI. In this development effort several lab prototypes were evaluated on 2 MW microwave test facility developed at CAT. One magnetron is subjected to life test. The present paper describes the setup and procedures used for life test. Various observations and corrections made during the life tests are also described. Results of the tests are discussed. (author)

  4. Inverted relativistic magnetron with a single axial output

    International Nuclear Information System (INIS)

    Ballard, W.P.; Earley, L.M.; Wharton, C.B.

    1986-01-01

    A twelve vane, 1 MV, S-band magnetron has been designed and tested. An inverted design was selected to minimize the parasitic axial electron losses. The stainless steel anode is approximately one wavelength long. One end is partially short-circuited to rf, while the other end has a mode transformer to couple the 3.16 GHz π-mode out into a TM 01 circular waveguide. The magnetron has a loaded output Q of about 100. Operation at 1 MV, 0.31 T, 5 kA routinely produces approx.150 MW peak rms and 100 MW average rms with pulse lengths adjustable from 5 to 70 ns. The microwave power pulse has a rise time of approx.2 ns. The output power is diagnosed using four methods: calorimetry, two circular-waveguide directional couplers installed on the magnetron, two transmitting-receiving systems, and gaseous breakdown. Operation at other voltages and magnetic fields shows that the oscillation frequency is somewhat dependent on the magnetron current. Frequency changes of approx.20 MHz/kA occur as the operating conditions are varied. A series of experiments varying the anode conductivity, the electron emission profile, and the output coupling transformer design showed that none of these significantly increased the output power. Therefore, we have concluded that this magnetron operates in saturation. Because of the anode lifetime and repeatability, this magnetron has the potential to be repetitively pulsed. 36 refs., 16 figs

  5. A Student’s t Mixture Probability Hypothesis Density Filter for Multi-Target Tracking with Outliers

    Science.gov (United States)

    Liu, Zhuowei; Chen, Shuxin; Wu, Hao; He, Renke; Hao, Lin

    2018-01-01

    In multi-target tracking, the outliers-corrupted process and measurement noises can reduce the performance of the probability hypothesis density (PHD) filter severely. To solve the problem, this paper proposed a novel PHD filter, called Student’s t mixture PHD (STM-PHD) filter. The proposed filter models the heavy-tailed process noise and measurement noise as a Student’s t distribution as well as approximates the multi-target intensity as a mixture of Student’s t components to be propagated in time. Then, a closed PHD recursion is obtained based on Student’s t approximation. Our approach can make full use of the heavy-tailed characteristic of a Student’s t distribution to handle the situations with heavy-tailed process and the measurement noises. The simulation results verify that the proposed filter can overcome the negative effect generated by outliers and maintain a good tracking accuracy in the simultaneous presence of process and measurement outliers. PMID:29617348

  6. Development and application of a multi-targeting reference plasmid as calibrator for analysis of five genetically modified soybean events.

    Science.gov (United States)

    Pi, Liqun; Li, Xiang; Cao, Yiwei; Wang, Canhua; Pan, Liangwen; Yang, Litao

    2015-04-01

    Reference materials are important in accurate analysis of genetically modified organism (GMO) contents in food/feeds, and development of novel reference plasmid is a new trend in the research of GMO reference materials. Herein, we constructed a novel multi-targeting plasmid, pSOY, which contained seven event-specific sequences of five GM soybeans (MON89788-5', A2704-12-3', A5547-127-3', DP356043-5', DP305423-3', A2704-12-5', and A5547-127-5') and sequence of soybean endogenous reference gene Lectin. We evaluated the specificity, limit of detection and quantification, and applicability of pSOY in both qualitative and quantitative PCR analyses. The limit of detection (LOD) was as low as 20 copies in qualitative PCR, and the limit of quantification (LOQ) in quantitative PCR was 10 copies. In quantitative real-time PCR analysis, the PCR efficiencies of all event-specific and Lectin assays were higher than 90%, and the squared regression coefficients (R(2)) were more than 0.999. The quantification bias varied from 0.21% to 19.29%, and the relative standard deviations were from 1.08% to 9.84% in simulated samples analysis. All the results demonstrated that the developed multi-targeting plasmid, pSOY, was a credible substitute of matrix reference materials, and could be used as a reliable reference calibrator in the identification and quantification of multiple GM soybean events.

  7. Dual-acting of Hybrid Compounds - A New Dawn in the Discovery of Multi-target Drugs: Lead Generation Approaches.

    Science.gov (United States)

    Abdolmaleki, Azizeh; Ghasemi, Jahan B

    2017-01-01

    Finding high quality beginning compounds is a critical job at the start of the lead generation stage for multi-target drug discovery (MTDD). Designing hybrid compounds as selective multitarget chemical entity is a challenge, opportunity, and new idea to better act against specific multiple targets. One hybrid molecule is formed by two (or more) pharmacophore group's participation. So, these new compounds often exhibit two or more activities going about as multi-target drugs (mtdrugs) and may have superior safety or efficacy. Application of integrating a range of information and sophisticated new in silico, bioinformatics, structural biology, pharmacogenomics methods may be useful to discover/design, and synthesis of the new hybrid molecules. In this regard, many rational and screening approaches have followed by medicinal chemists for the lead generation in MTDD. Here, we review some popular lead generation approaches that have been used for designing multiple ligands (DMLs). This paper focuses on dual- acting chemical entities that incorporate a part of two drugs or bioactive compounds to compose hybrid molecules. Also, it presents some of key concepts and limitations/strengths of lead generation methods by comparing combination framework method with screening approaches. Besides, a number of examples to represent applications of hybrid molecules in the drug discovery are included. Copyright© Bentham Science Publishers; For any queries, please email at epub@benthamscience.org.

  8. Multi-target QSPR modeling for simultaneous prediction of multiple gas-phase kinetic rate constants of diverse chemicals

    Science.gov (United States)

    Basant, Nikita; Gupta, Shikha

    2018-03-01

    The reactions of molecular ozone (O3), hydroxyl (•OH) and nitrate (NO3) radicals are among the major pathways of removal of volatile organic compounds (VOCs) in the atmospheric environment. The gas-phase kinetic rate constants (kO3, kOH, kNO3) are thus, important in assessing the ultimate fate and exposure risk of atmospheric VOCs. Experimental data for rate constants are not available for many emerging VOCs and the computational methods reported so far address a single target modeling only. In this study, we have developed a multi-target (mt) QSPR model for simultaneous prediction of multiple kinetic rate constants (kO3, kOH, kNO3) of diverse organic chemicals considering an experimental data set of VOCs for which values of all the three rate constants are available. The mt-QSPR model identified and used five descriptors related to the molecular size, degree of saturation and electron density in a molecule, which were mechanistically interpretable. These descriptors successfully predicted three rate constants simultaneously. The model yielded high correlations (R2 = 0.874-0.924) between the experimental and simultaneously predicted endpoint rate constant (kO3, kOH, kNO3) values in test arrays for all the three systems. The model also passed all the stringent statistical validation tests for external predictivity. The proposed multi-target QSPR model can be successfully used for predicting reactivity of new VOCs simultaneously for their exposure risk assessment.

  9. Extending multi-tenant architectures: a database model for a multi-target support in SaaS applications

    Science.gov (United States)

    Rico, Antonio; Noguera, Manuel; Garrido, José Luis; Benghazi, Kawtar; Barjis, Joseph

    2016-05-01

    Multi-tenant architectures (MTAs) are considered a cornerstone in the success of Software as a Service as a new application distribution formula. Multi-tenancy allows multiple customers (i.e. tenants) to be consolidated into the same operational system. This way, tenants run and share the same application instance as well as costs, which are significantly reduced. Functional needs vary from one tenant to another; either companies from different sectors run different types of applications or, although deploying the same functionality, they do differ in the extent of their complexity. In any case, MTA leaves one major concern regarding the companies' data, their privacy and security, which requires special attention to the data layer. In this article, we propose an extended data model that enhances traditional MTAs in respect of this concern. This extension - called multi-target - allows MT applications to host, manage and serve multiple functionalities within the same multi-tenant (MT) environment. The practical deployment of this approach will allow SaaS vendors to target multiple markets or address different levels of functional complexity and yet commercialise just one single MT application. The applicability of the approach is demonstrated via a case study of a real multi-tenancy multi-target (MT2) implementation, called Globalgest.

  10. Changing paradigm from one target one ligand towards multi target directed ligand design for key drug targets of Alzheimer disease: An important role of Insilco methods in multi target directed ligands design.

    Science.gov (United States)

    Kumar, Akhil; Tiwari, Ashish; Sharma, Ashok

    2018-03-15

    Alzheimer disease (AD) is now considered as a multifactorial neurodegenerative disorder and rapidly increasing to an alarming situation and causing higher death rate. One target one ligand hypothesis is not able to provide complete solution of AD due to multifactorial nature of disease and one target one drug seems to fail to provide better treatment against AD. Moreover, current available treatments are limited and most of the upcoming treatments under clinical trials are based on modulating single target. So the current AD drug discovery research shifting towards new approach for better solution that simultaneously modulate more than one targets in the neurodegenerative cascade. This can be achieved by network pharmacology, multi-modal therapies, multifaceted, and/or the more recently proposed term "multi-targeted designed drugs. Drug discovery project is tedious, costly and long term project. Moreover, multi target AD drug discovery added extra challenges such as good binding affinity of ligands for multiple targets, optimal ADME/T properties, no/less off target side effect and crossing of the blood brain barrier. These hurdles may be addressed by insilico methods for efficient solution in less time and cost as computational methods successfully applied to single target drug discovery project. Here we are summarizing some of the most prominent and computationally explored single target against AD and further we discussed successful example of dual or multiple inhibitors for same targets. Moreover we focused on ligand and structure based computational approach to design MTDL against AD. However is not an easy task to balance dual activity in a single molecule but computational approach such as virtual screening docking, QSAR, simulation and free energy are useful in future MTDLs drug discovery alone or in combination with fragment based method. However, rational and logical implementations of computational drug designing methods are capable of assisting AD drug

  11. Development of new cylindrical magnetrons for industrial use

    International Nuclear Information System (INIS)

    Clayton, B.

    2000-09-01

    A number of alternative techniques were considered and tested with a view to the construction of a cylindrical sputtering device. This device was required to be capable of depositing tribological coatings inside approximately cylindrical substrates of diameters less than 100mm, in an industrial situation. A cylindrical magnetron device was designed, and constructed as a prototype, using a magnetic assembly inside a cylindrical target with outside diameter (o.d.) 40mm. Two alternative magnetic assemblies were tested, and found to have complimentary advantages. The magnetron characteristics of the device were tested, as were key properties (such as adhesion level and hardness) of the coatings deposited. In all cases good results were obtained. A 22mm o.d. device based on the same design was shown to operate, but with less satisfactory characteristics. In an attempt to improve the miniaturised design, the feasibility of gas cooling (rather than water cooling) the cylindrical magnetron was demonstrated. A system incorporating four 40mm o.d. cylindrical magnetrons was designed, constructed and briefly tested. This was intended to prove the feasibility of using a multi-magnetron system to reduce the cost to coat. Its dimensions and design were tailored to an industrially specified engine block. In use the plasma rings formed on the 40mm magnetron target surfaces during operation were found to be of unequal intensities, especially on the shorter magnetron design used in the four-fold system. In an attempt to tackle this problem, a finite element model of the magnetic field generated by the magnetic assembly was built, run and verified. Changes were made to this model, and a new .magnet assembly was built and tested based on the results obtained. This did not lead to a final solution of the problem, but has set bounds within which the solution must lie. (author)

  12. Evolution of film temperature during magnetron sputtering

    International Nuclear Information System (INIS)

    Shaginyan, L.R.; Han, J.G.; Shaginyan, V.R.; Musil, J.

    2006-01-01

    We report on the results of measurements of the temperature T F surf which developed on the surface of films deposited by magnetron sputtering of chromium and copper targets on cooling and non-cooling silicon substrates. The T F surf and substrate temperature (T s ) were simultaneously measured using high-resolution IR camera and thermocouple, respectively. We revealed that the T F surf steeply grows, keeps constant when it achieves saturation level, and rapidly drops to the value of the T s after stopping the deposition. At the same time, the T s either does not change for the case of cooling substrate or increases to a certain level for noncooling substrate. However, in both cases the T s remains several times lower than the T F surf . The T F surf is proportional to the flux of energy delivered to the growth surface by sputtered atoms and other fast particles, weakly depends on the depositing metal and can achieve several hundreds of deg. C. This phenomenon is explained by a model assuming formation of a hot thin surface layer (HTSL) on the top of the growing film, which exists only during film deposition and exhibits extremely low thermal conductivity. Due to this unique property the temperature T F surf of HTSL is several times higher than the T s . Variations in the T F surf fairly correlate with structure changes of Cr films along thickness investigated in detail previously

  13. TimeLapseAnalyzer: Multi-target analysis for live-cell imaging and time-lapse microscopy

    DEFF Research Database (Denmark)

    Huth, Johannes; Buchholz, Malte; Kraus, Johann M.

    2011-01-01

    The direct observation of cells over time using time-lapse microscopy can provide deep insights into many important biological processes. Reliable analyses of motility, proliferation, invasive potential or mortality of cells are essential to many studies involving live cell imaging and can aid in...... counting and tube formation analysis in high throughput screening of live-cell experiments. TimeLapseAnalyzer is freely available (MATLAB, Open Source) at http://www.informatik.uniulm. de/ni/mitarbeiter/HKestler/tla......., we developed TimeLapseAnalyzer. Apart from general purpose image enhancements and segmentation procedures, this extensible, self-contained, modular cross-platform package provides dedicated modalities for fast and reliable analysis of multi-target cell tracking, scratch wound healing analysis, cell...

  14. A multi-target caffeine derived rhodium(i) N-heterocyclic carbene complex: evaluation of the mechanism of action.

    Science.gov (United States)

    Zhang, Jing-Jing; Muenzner, Julienne K; Abu El Maaty, Mohamed A; Karge, Bianka; Schobert, Rainer; Wölfl, Stefan; Ott, Ingo

    2016-08-16

    A rhodium(i) and a ruthenium(ii) complex with a caffeine derived N-heterocyclic carbene (NHC) ligand were biologically investigated as organometallic conjugates consisting of a metal center and a naturally occurring moiety. While the ruthenium(ii) complex was largely inactive, the rhodium(i) NHC complex displayed selective cytotoxicity and significant anti-metastatic and in vivo anti-vascular activities and acted as both a mammalian and an E. coli thioredoxin reductase inhibitor. In HCT-116 cells it increased the reactive oxygen species level, leading to DNA damage, and it induced cell cycle arrest, decreased the mitochondrial membrane potential, and triggered apoptosis. This rhodium(i) NHC derivative thus represents a multi-target compound with promising anti-cancer potential.

  15. Reactive dual magnetron sputtering for large area application

    International Nuclear Information System (INIS)

    Struempfel, J.

    2002-01-01

    Production lines for large area coating demand high productivity of reactive magnetron sputtering processes. Increased dynamic deposition rates for oxides and nitrides were already obtained by using of highly powered magnetrons in combination with advanced sputter techniques. However, besides high deposition rates the uniformity of such coatings has to be carefully considered. First the basics of reactive sputtering processes and dual magnetron sputtering are summarized. Different methods for process stabilization and control are commonly used for reactive sputtering. The Plasma Emission Monitor (PE M) offers the prerequisite for fast acting process control derived from the in-situ intensity measurements of a spectral line of the sputtered target material. Combined by multiple Plasma Emission Monitor control loops segmented gas manifolds are able to provide excellent thin film uniformity at high deposition rates. The Dual Magnetron allows a broad range of processing by different power supply modes. Medium frequency, DC and pulsed DC power supplies can be used for high quality layers. Whereas the large area coating of highly isolating layers like TiO 2 or SiO 2 is dominated by MF sputtering best results for coating with transparent conductive oxides are obtained by dual DC powering of the dual magnetron arrangement. (Author)

  16. Multi-targeted therapy for leprosy: insilico strategy to overcome multi drug resistance and to improve therapeutic efficacy.

    Science.gov (United States)

    Anusuya, Shanmugam; Natarajan, Jeyakumar

    2012-12-01

    Leprosy remains a major public health problem, since single and multi-drug resistance has been reported worldwide over the last two decades. In the present study, we report the novel multi-targeted therapy for leprosy to overcome multi drug resistance and to improve therapeutic efficacy. If multiple enzymes of an essential metabolic pathway of a bacterium were targeted, then the therapy would become more effective and can prevent the occurrence of drug resistance. The MurC, MurD, MurE and MurF enzymes of peptidoglycan biosynthetic pathway were selected for multi targeted therapy. The conserved or class specific active site residues important for function or stability were predicted using evolutionary trace analysis and site directed mutagenesis studies. Ten such residues which were present in at least any three of the four Mur enzymes (MurC, MurD, MurE and MurF) were identified. Among the ten residues G125, K126, T127 and G293 (numbered based on their position in MurC) were found to be conserved in all the four Mur enzymes of the entire bacterial kingdom. In addition K143, T144, T166, G168, H234 and Y329 (numbered based on their position in MurE) were significant in binding substrates and/co-factors needed for the functional events in any three of the Mur enzymes. These are the probable residues for designing newer anti-leprosy drugs in an attempt to reduce drug resistance. Copyright © 2012 Elsevier B.V. All rights reserved.

  17. Influence of Magnetron Effect on Barium Hexaferrite Thin Layers

    International Nuclear Information System (INIS)

    Hassane, H.; Chatelon, J.P.; Rousseau, J.J; Siblini, A.; Kriga, A.

    2011-01-01

    In this paper, we study the effects of a magnet, located in the cathode, on barium hexaferrite thin films deposited by RF magnetron sputtering technique. During the process, these effects can modify thickness, roughness and stress of coatings. The characteristics of the deposited layers depend on the substrate position that is located opposite of magnetron cathode. In the m agnetron area , one can observe that the high stress can produce cracks or detachment of layers and the increasing of both depositing rate and surface roughness. After sputtering elaboration, barium hexaferrite films are in a compressive stress mode. But, after the post-deposition heat treatment these films are in a tensile stress mode. To improve the quality of BaM films, the subsrtate has to be set outside the magnetron area. (author)

  18. Very low pressure high power impulse triggered magnetron sputtering

    Science.gov (United States)

    Anders, Andre; Andersson, Joakim

    2013-10-29

    A method and apparatus are described for very low pressure high powered magnetron sputtering of a coating onto a substrate. By the method of this invention, both substrate and coating target material are placed into an evacuable chamber, and the chamber pumped to vacuum. Thereafter a series of high impulse voltage pulses are applied to the target. Nearly simultaneously with each pulse, in one embodiment, a small cathodic arc source of the same material as the target is pulsed, triggering a plasma plume proximate to the surface of the target to thereby initiate the magnetron sputtering process. In another embodiment the plasma plume is generated using a pulsed laser aimed to strike an ablation target material positioned near the magnetron target surface.

  19. Substrate heating and cooling during magnetron sputtering of copper target

    Energy Technology Data Exchange (ETDEWEB)

    Shapovalov, Viktor I.; Komlev, Andrey E.; Bondarenko, Anastasia S., E-mail: stopnastia@gmail.com; Baykov, Pavel B.; Karzin, Vitaliy V.

    2016-02-22

    Heating and cooling processes of the substrate during the DC magnetron sputtering of the copper target were investigated. The sensitive element of a thermocouple was used as a substrate. It was found, that the heat outflow rate from the substrate is lower when the magnetron is turned off rather than when it is turned on. Furthermore, the heating rate, the ultimate temperature, and the heat outflow rate related to the deposition of copper atoms are directly proportional to the discharge current density. - Highlights: • New effect of heat outflow from substrate when magnetron is on was discovered. • This new effect is linear in terms of heat outflow rate to target current ratio. • Kinetic equation for heating process additively considers this effect.

  20. High-current magnetron discharge with magnetic insulation of anode

    International Nuclear Information System (INIS)

    Bizyukov, A.A.; Sereda, K.N.; Sleptsov, V.V.

    2008-01-01

    In magnetron discharge at currents higher then critical which magnitude is in the range of 15...30 A the transition from glow discharge in transverse magnetic field to arc discharge occurs. In the present time the problem of arc blowout is solved at the expense of pulse and HF power supply applying. In this paper the alternative method of limiting current of magnetron discharge increasing at the expense of increasing of discharge gap resistance by means of additional anode layer transverse magnetic field and arc current interruption by sectioning of current collector of anode surface is carrying out

  1. Nanoporous zinc oxide films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Ghimpu, L.; Lupan, O.; Popescu, L.; Tiginyanu, I.M.

    2011-01-01

    In this paper we demonstrate an inexpensive approach for the fabrication of nanoporous zinc oxide films by using magnetron sputtering. Study of the structural properties proves the crystallographic perfection of porous nanostructures and the possibility of its controlling by adjusting the technological parameters in the growth process. The XRD pattern of nanoporous ZnO films exhibits high intensity of the peaks relative to the background signal which is indicative of the ZnO hexagonal phase and a good crystallinity of the samples grown by magnetron sputtering.

  2. Plasma diagnostics during magnetron sputtering of aluminum doped zinc oxide

    DEFF Research Database (Denmark)

    Stamate, Eugen; Crovetto, Andrea; Sanna, Simone

    2016-01-01

    Plasma parameters during magnetron sputtering of aluminum-doped zinc oxide are investigated with optical emission spectroscopy, electrostatic probes and mass spectrometry with the aim of understanding the role of negative ions of oxygen during the film growth and improving the uniformity of the f......Plasma parameters during magnetron sputtering of aluminum-doped zinc oxide are investigated with optical emission spectroscopy, electrostatic probes and mass spectrometry with the aim of understanding the role of negative ions of oxygen during the film growth and improving the uniformity...

  3. Variable Power, Short Microwave Pulses Generation using a CW Magnetron

    Directory of Open Access Journals (Sweden)

    CIUPA, R.

    2011-05-01

    Full Text Available Fine control of microwave power radiation in medical and scientific applications is a challenging task. Since a commercial Continuous Wave (CW magnetron is the most inexpensive microwave device available today on the market, it becomes the best candidate for a microwave power generator used in medical diathermy and hyperthermia treatments or high efficiency chemical reactions using microwave reactors as well. This article presents a new method for driving a CW magnetron with short pulses, using a modified commercial Zero Voltage Switching (ZVS inverter, software driven by a custom embedded system. The microwave power generator designed with this method can be programmed for output microwave pulses down to 1% of the magnetron's power and allows microwave low frequency pulse modulation in the range of human brain electrical activity, intended for medical applications. Microwave output power continuous control is also possible with the magnetron running in the oscillating area, using a dual frequency Pulse Width Modulation (PWM, where the low frequency PWM pulse is modulating a higher resonant frequency required by the ZVS inverter's transformer. The method presented allows a continuous control of both power and energy (duty-cycle at the inverter's output.

  4. Geometrical Aspects of a Hollow-cathode Magnetron (HCM)

    International Nuclear Information System (INIS)

    Cohen, Samuel A.; Wang, Zhehui

    1998-01-01

    A hollow-cathode magnetron (HCM), built by surrounding a planar sputtering-magnetron cathode with a hollow-cathode structure (HCS), is operable at substantially lower pressures than its planar-magnetron counterpart. We have studied the dependence of magnetron operational parameters on the inner diameter D and length L of a cylindrical HCS. Only when L is greater than L sub zero, a critical length, is the HCM operable in the new low-pressure regime. The critical length varies with HCS inner diameter D. Explanations of the lower operational pressure regime, critical length, and plasma shape are proposed and compared with a one-dimension diffusion model for energetic or primary electron transport. At pressures above 1 mTorr, an electron-impact ionization model with Bohm diffusion at a temperature equivalent to one-half the primary electron energy and with an ambipolar constraint can explain the ion-electron pair creation required to sustain the discharge. The critical length L sub zero is determined by the magnetization length of the primary electrons

  5. Operational experience with the BNL magnetron H- source

    International Nuclear Information System (INIS)

    Witkover, R.L.

    1983-01-01

    A magnetron H - source with a grooved cathode has been in operation at the BNL Linac for over 18 months. The source has run at 5 pps with a 600 μsec pulse width for periods as long as 5 months. Its development and performance will be discussed

  6. RF Reactive Magnetron Sputter Deposition of Silicon Sub-Oxides

    NARCIS (Netherlands)

    Hattum, E.D. van

    2007-01-01

    RF reactive magnetron plasma sputter deposition of silicon sub oxide E.D. van Hattum Department of Physics and Astronomy, Faculty of Sciences, Utrecht University The work described in the thesis has been inspired and stimulated by the use of SiOx layers in the direct inductive printing technology,

  7. Spatiotemporal synchronization of drift waves in a magnetron sputtering plasma

    Czech Academy of Sciences Publication Activity Database

    Martines, E.; Zuin, M.; Cavazzana, R.; Adámek, Jiří; Antoni, V.; Serianni, G.; Spolaore, M.; Vianello, N.

    2014-01-01

    Roč. 21, č. 10 (2014), s. 102309-102309 ISSN 1070-664X Institutional support: RVO:61389021 Keywords : Drift waves * Magnetron sputtering plasma * Spatiotemporal synchronization Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 2.142, year: 2014 http://dx.doi.org/10.1063/1.4898693

  8. Real-time multi-target ranging based on chaotic polarization laser radars in the drive-response VCSELs.

    Science.gov (United States)

    Zhong, Dongzhou; Xu, Geliang; Luo, Wei; Xiao, Zhenzhen

    2017-09-04

    According to the principle of complete chaos synchronization and the theory of Hilbert phase transformation, we propose a novel real-time multi-target ranging scheme by using chaotic polarization laser radar in the drive-response vertical-cavity surface-emitting lasers (VCSELs). In the scheme, to ensure each polarization component (PC) of the master VCSEL (MVCSEL) to be synchronized steadily with that of the slave VCSEL, the output x-PC and y-PC from the MVCSEL in the drive system and those in the response system are modulated by the linear electro-optic effect simultaneously. Under this condition, by simulating the influences of some key parameters of the system on the synchronization quality and the relative errors of the two-target ranging, related operating parameters can be optimized. The x-PC and the y-PC, as two chaotic radar sources, are used to implement the real-time ranging for two targets. It is found that the measured distances of the two targets at arbitrary position exhibit strong real-time stability and only slight jitter. Their resolutions are up to millimeters, and their relative errors are very small and less than 2.7%.

  9. TargetNet: a web service for predicting potential drug-target interaction profiling via multi-target SAR models.

    Science.gov (United States)

    Yao, Zhi-Jiang; Dong, Jie; Che, Yu-Jing; Zhu, Min-Feng; Wen, Ming; Wang, Ning-Ning; Wang, Shan; Lu, Ai-Ping; Cao, Dong-Sheng

    2016-05-01

    Drug-target interactions (DTIs) are central to current drug discovery processes and public health fields. Analyzing the DTI profiling of the drugs helps to infer drug indications, adverse drug reactions, drug-drug interactions, and drug mode of actions. Therefore, it is of high importance to reliably and fast predict DTI profiling of the drugs on a genome-scale level. Here, we develop the TargetNet server, which can make real-time DTI predictions based only on molecular structures, following the spirit of multi-target SAR methodology. Naïve Bayes models together with various molecular fingerprints were employed to construct prediction models. Ensemble learning from these fingerprints was also provided to improve the prediction ability. When the user submits a molecule, the server will predict the activity of the user's molecule across 623 human proteins by the established high quality SAR model, thus generating a DTI profiling that can be used as a feature vector of chemicals for wide applications. The 623 SAR models related to 623 human proteins were strictly evaluated and validated by several model validation strategies, resulting in the AUC scores of 75-100 %. We applied the generated DTI profiling to successfully predict potential targets, toxicity classification, drug-drug interactions, and drug mode of action, which sufficiently demonstrated the wide application value of the potential DTI profiling. The TargetNet webserver is designed based on the Django framework in Python, and is freely accessible at http://targetnet.scbdd.com .

  10. Multi-Targeted Molecular Effects of Hibiscus sabdariffa Polyphenols: An Opportunity for a Global Approach to Obesity.

    Science.gov (United States)

    Herranz-López, María; Olivares-Vicente, Mariló; Encinar, José Antonio; Barrajón-Catalán, Enrique; Segura-Carretero, Antonio; Joven, Jorge; Micol, Vicente

    2017-08-20

    Improper diet can alter gene expression by breaking the energy balance equation and changing metabolic and oxidative stress biomarkers, which can result in the development of obesity-related metabolic disorders. The pleiotropic effects of dietary plant polyphenols are capable of counteracting by modulating different key molecular targets at the cell, as well as through epigenetic modifications. Hibiscus sabdariffa (HS)-derived polyphenols are known to ameliorate various obesity-related conditions. Recent evidence leads to propose the complex nature of the underlying mechanism of action. This multi-targeted mechanism includes the regulation of energy metabolism, oxidative stress and inflammatory pathways, transcription factors, hormones and peptides, digestive enzymes, as well as epigenetic modifications. This article reviews the accumulated evidence on the multiple anti-obesity effects of HS polyphenols in cell and animal models, as well as in humans, and its putative molecular targets. In silico studies reveal the capacity of several HS polyphenols to act as putative ligands for different digestive and metabolic enzymes, which may also deserve further attention. Therefore, a global approach including integrated and networked omics techniques, virtual screening and epigenetic analysis is necessary to fully understand the molecular mechanisms of HS polyphenols and metabolites involved, as well as their possible implications in the design of safe and effective polyphenolic formulations for obesity.

  11. TargetNet: a web service for predicting potential drug-target interaction profiling via multi-target SAR models

    Science.gov (United States)

    Yao, Zhi-Jiang; Dong, Jie; Che, Yu-Jing; Zhu, Min-Feng; Wen, Ming; Wang, Ning-Ning; Wang, Shan; Lu, Ai-Ping; Cao, Dong-Sheng

    2016-05-01

    Drug-target interactions (DTIs) are central to current drug discovery processes and public health fields. Analyzing the DTI profiling of the drugs helps to infer drug indications, adverse drug reactions, drug-drug interactions, and drug mode of actions. Therefore, it is of high importance to reliably and fast predict DTI profiling of the drugs on a genome-scale level. Here, we develop the TargetNet server, which can make real-time DTI predictions based only on molecular structures, following the spirit of multi-target SAR methodology. Naïve Bayes models together with various molecular fingerprints were employed to construct prediction models. Ensemble learning from these fingerprints was also provided to improve the prediction ability. When the user submits a molecule, the server will predict the activity of the user's molecule across 623 human proteins by the established high quality SAR model, thus generating a DTI profiling that can be used as a feature vector of chemicals for wide applications. The 623 SAR models related to 623 human proteins were strictly evaluated and validated by several model validation strategies, resulting in the AUC scores of 75-100 %. We applied the generated DTI profiling to successfully predict potential targets, toxicity classification, drug-drug interactions, and drug mode of action, which sufficiently demonstrated the wide application value of the potential DTI profiling. The TargetNet webserver is designed based on the Django framework in Python, and is freely accessible at http://targetnet.scbdd.com.

  12. Targeting MDM2 by the small molecule RITA: towards the development of new multi-target drugs against cancer

    Directory of Open Access Journals (Sweden)

    Espinoza-Fonseca L Michel

    2005-09-01

    Full Text Available Abstract Background The use of low-molecular-weight, non-peptidic molecules that disrupt the interaction between the p53 tumor suppressor and its negative regulator MDM2 has provided a promising alternative for the treatment of different types of cancer. Among these compounds, RITA (reactivation of p53 and induction of tumor cell apoptosis has been shown to be effective in the selective induction of apoptosis, and this effect is due to its binding to the p53 tumor suppressor. Since biological systems are highly dynamic and MDM2 may bind to different regions of p53, new alternatives should be explored. On this basis, the computational "blind docking" approach was employed in this study to see whether RITA would bind to MDM2. Results It was observed that RITA binds to the MDM2 p53 transactivation domain-binding cleft. Thus, RITA can be used as a lead compound for designing improved "multi-target" drugs. This novel strategy could provide enormous benefits to enable effective anti-cancer strategies. Conclusion This study has demonstrated that a single molecule can target at least two different proteins related to the same disease.

  13. Multi-target parallel processing approach for gene-to-structure determination of the influenza polymerase PB2 subunit.

    Science.gov (United States)

    Armour, Brianna L; Barnes, Steve R; Moen, Spencer O; Smith, Eric; Raymond, Amy C; Fairman, James W; Stewart, Lance J; Staker, Bart L; Begley, Darren W; Edwards, Thomas E; Lorimer, Donald D

    2013-06-28

    Pandemic outbreaks of highly virulent influenza strains can cause widespread morbidity and mortality in human populations worldwide. In the United States alone, an average of 41,400 deaths and 1.86 million hospitalizations are caused by influenza virus infection each year (1). Point mutations in the polymerase basic protein 2 subunit (PB2) have been linked to the adaptation of the viral infection in humans (2). Findings from such studies have revealed the biological significance of PB2 as a virulence factor, thus highlighting its potential as an antiviral drug target. The structural genomics program put forth by the National Institute of Allergy and Infectious Disease (NIAID) provides funding to Emerald Bio and three other Pacific Northwest institutions that together make up the Seattle Structural Genomics Center for Infectious Disease (SSGCID). The SSGCID is dedicated to providing the scientific community with three-dimensional protein structures of NIAID category A-C pathogens. Making such structural information available to the scientific community serves to accelerate structure-based drug design. Structure-based drug design plays an important role in drug development. Pursuing multiple targets in parallel greatly increases the chance of success for new lead discovery by targeting a pathway or an entire protein family. Emerald Bio has developed a high-throughput, multi-target parallel processing pipeline (MTPP) for gene-to-structure determination to support the consortium. Here we describe the protocols used to determine the structure of the PB2 subunit from four different influenza A strains.

  14. Sample Preparation Strategies for the Effective Quantitation of Hydrophilic Metabolites in Serum by Multi-Targeted HILIC-MS/MS

    Directory of Open Access Journals (Sweden)

    Elisavet Tsakelidou

    2017-03-01

    Full Text Available The effect of endogenous interferences of serum in multi-targeted metabolite profiling HILIC-MS/MS analysis was investigated by studying different sample preparation procedures. A modified QuEChERS dispersive SPE protocol, a HybridSPE protocol, and a combination of liquid extraction with protein precipitation were compared to a simple protein precipitation. Evaluation of extraction efficiency and sample clean-up was performed for all methods. SPE sorbent materials tested were found to retain hydrophilic analytes together with endogenous interferences, thus additional elution steps were needed. Liquid extraction was not shown to minimise matrix effects. In general, it was observed that a balance should be reached in terms of recovery, efficient clean-up, and sample treatment time when a wide range of metabolites are analysed. A quick step for removing phospholipids prior to the determination of hydrophilic endogenous metabolites is required, however, based on the results from the applied methods, further studies are needed to achieve high recoveries for all metabolites.

  15. Multi-Targeted Molecular Effects of Hibiscus sabdariffa Polyphenols: An Opportunity for a Global Approach to Obesity

    Science.gov (United States)

    Herranz-López, María; Olivares-Vicente, Mariló; Barrajón-Catalán, Enrique; Segura-Carretero, Antonio; Joven, Jorge; Micol, Vicente

    2017-01-01

    Improper diet can alter gene expression by breaking the energy balance equation and changing metabolic and oxidative stress biomarkers, which can result in the development of obesity-related metabolic disorders. The pleiotropic effects of dietary plant polyphenols are capable of counteracting by modulating different key molecular targets at the cell, as well as through epigenetic modifications. Hibiscus sabdariffa (HS)-derived polyphenols are known to ameliorate various obesity-related conditions. Recent evidence leads to propose the complex nature of the underlying mechanism of action. This multi-targeted mechanism includes the regulation of energy metabolism, oxidative stress and inflammatory pathways, transcription factors, hormones and peptides, digestive enzymes, as well as epigenetic modifications. This article reviews the accumulated evidence on the multiple anti-obesity effects of HS polyphenols in cell and animal models, as well as in humans, and its putative molecular targets. In silico studies reveal the capacity of several HS polyphenols to act as putative ligands for different digestive and metabolic enzymes, which may also deserve further attention. Therefore, a global approach including integrated and networked omics techniques, virtual screening and epigenetic analysis is necessary to fully understand the molecular mechanisms of HS polyphenols and metabolites involved, as well as their possible implications in the design of safe and effective polyphenolic formulations for obesity. PMID:28825642

  16. Modeling and experimental studies of a side band power re-injection locked magnetron

    Science.gov (United States)

    Ye, Wen-Jun; Zhang, Yi; Yuan, Ping; Zhu, Hua-Cheng; Huang, Ka-Ma; Yang, Yang

    2016-12-01

    A side band power re-injection locked (SBPRIL) magnetron is presented in this paper. A tuning stub is placed between the external injection locked (EIL) magnetron and the circulator. Side band power of the EIL magnetron is reflected back to the magnetron. The reflected side band power is reused and pulled back to the central frequency. A phase-locking model is developed from circuit theory to explain the process of reuse of side band power in SBPRIL magnetron. Theoretical analysis proves that the side band power is pulled back to the central frequency of the SBPRIL magnetron, then the amplitude of the RF voltage increases and the phase noise performance is improved. Particle-in-cell (PIC) simulation of a 10-vane continuous wave (CW) magnetron model is presented. Computer simulation predicts that the frequency spectrum’s peak of the SBPRIL magnetron has an increase of 3.25 dB compared with the free running magnetron. The phase noise performance at the side band offset reduces 12.05 dB for the SBPRIL magnetron. Besides, the SBPRIL magnetron experiment is presented. Experimental results show that the spectrum peak rises by 14.29% for SBPRIL magnetron compared with the free running magnetron. The phase noise reduces more than 25 dB at 45-kHz offset compared with the free running magnetron. Project supported by the National Basic Research Program of China (Grant No. 2013CB328902) and the National Natural Science Foundation of China (Grant No. 61501311).

  17. Phase and Frequency Locked Magnetrons for SRF Sources

    Energy Technology Data Exchange (ETDEWEB)

    Neubauer, Michael [Muons, Inc.; Johnson, Rolland

    2014-09-12

    There is great potential for a magnetron power source that can be controlled both in phase and frequency. Such a power source could revolutionize many particle accelerator systems that require lower capital cost and/or higher power efficiency. Beyond the accelerator community, phase and frequency locked magnetons could improve radar systems around the world and make affordable phased arrays for wireless power transmission for solar powered satellites. This joint project of Muons, Inc., Fermilab, and L-3 CTL was supported by an STTR grant monitored by the Nuclear Physics Office of the DOE Office of Science. The object of the program was to incorporate ferrite materials into the anode of a magnetron and, with appropriate biasing of the ferrites, to maintain frequency lock and to allow for frequency adjustment of the magnetron without mechanical tuners. If successful, this device would have a dual use both as a source for SRF linacs and for military applications where fast tuning of the frequency is a requirement. In order to place the materials in the proper location, several attributes needed to be modeled. First the impact of the magnetron’s magnetic field needed to be shielded from the ferrites so that they were not saturated. And second, the magnetic field required to change the frequency of the magnetron at the ferrites needed to be shielded from the region containing the circulating electrons. ANSYS calculations of the magnetic field were used to optimize both of these parameters. Once the design for these elements was concluded, parts were fabricated and a complete test assembly built to confirm the predictions of the computer models. The ferrite material was also tested to determine its compatibility with magnetron tube processing temperatures. This required a vacuum bake out of the chosen material to determine the cleanliness of the material in terms of outgassing characteristics, and a subsequent room temperature test to verify that the characteristics of

  18. Inorganic nanocomposite films with polymer nanofillers made by the concurrent multi-beam multi-target pulsed laser deposition

    Science.gov (United States)

    Darwish, Abdalla M.; Sarkisov, Sergey S.; Mele, Paolo; Saini, Shrikant; Moore, Shaelynn; Bastian, Tyler; Dorlus, Wydglif; Zhang, Xiaodong; Koplitz, Brent

    2017-08-01

    We report on the new class of inorganic nanocomposite films with the inorganic phase hosting the polymer nanofillers made by the concurrent multi-beam multi-target pulsed laser deposition of the inorganic target material and matrix assisted pulsed laser evaporation of the polymer (MBMT-PLD/MAPLE). We used the exemplary nanocomposite thermoelectric films of aluminum-doped ZnO known as AZO with the nanofillers made of poly(methyl methacrylate) known as PMMA on various substrates such as SrTiO3, sapphire, fused silica, and polyimide. The AZO target was ablated with the second harmonic (532 nm) of the Nd:YAG Q-switched laser while PMMA was evaporated from its solution in chlorobenzene frozen in liquid nitrogen with the fundamental harmonic (1064 nm) of the same laser (50 Hz pulse repetition rate). The introduction of the polymer nanofillers increased the electrical conductivity of the nanocomposite films (possibly due to the carbonization of PMMA and the creation of additional channels of electric current) three times and reduced the thermal conductivity by 1.25 times as compared to the pure AZO films. Accordingly, the increase of the thermoelectric figure-of merit ZT would be 4 times. The best performance was observed for the sapphire substrates where the films were the most uniform. The results point to a huge potential of the optimization of a broad variety of optical, opto-electronic, and solar-power nanocomposite inorganic films by the controllable introduction of the polymer nanofillers using the MBMT-PLD/MAPLE method.

  19. The multi-targeted kinase inhibitor sorafenib inhibits enterovirus 71 replication by regulating IRES-dependent translation of viral proteins.

    Science.gov (United States)

    Gao, Meng; Duan, Hao; Liu, Jing; Zhang, Hao; Wang, Xin; Zhu, Meng; Guo, Jitao; Zhao, Zhenlong; Meng, Lirong; Peng, Yihong

    2014-06-01

    The activation of ERK and p38 signal cascade in host cells has been demonstrated to be essential for picornavirus enterovirus 71 (EV71) replication and up-regulation of virus-induced cyclooxygenase-2 (COX-2)/prostaglandins E2 (PGE2) expression. The aim of this study was to examine the effects of sorafenib, a clinically approved anti-cancer multi-targeted kinase inhibitor, on the propagation and pathogenesis of EV71, with a view to its possible mechanism and potential use in the design of therapy regimes for Hand foot and mouth disease (HFMD) patients with life threatening neurological complications. In this study, non-toxic concentrations of sorafenib were shown to inhibit the yield of infectious progeny EV71 (clinical BC08 strain) by about 90% in three different cell types. A similar inhibitory effect of sorafenib was observed on the synthesis of both viral genomic RNA and the VP1 protein. Interestingly, sorafenib exerted obvious inhibition of the EV71 internal ribosomal entry site (IRES)-mediated translation, the first step in picornavirus replication, by linking it to a firefly luciferase reporter gene. Sorafenib was also able to prevent both EV71-induced CPE and the activation of ERK and p38, which contributes to up-regulation COX-2/PGE2 expression induced by the virus. Overall, this study shows that sorafenib strongly inhibits EV71 replication at least in part by regulating viral IRES-dependent translation of viral proteins, indicating a novel potential strategy for the treatment of HFMD patients with severe neurological complications. To our knowledge, this is the first report that investigates the mechanism by which sorafenib inhibits EV71 replication. Copyright © 2014 Elsevier B.V. All rights reserved.

  20. Corrosion of thin, magnetron sputtered Nb_2O_5 films

    International Nuclear Information System (INIS)

    Pillis, Marina Fuser; Geribola, Guilherme Altomari; Scheidt, Guilherme; Gonçalves de Araújo, Edval; Lopes de Oliveira, Mara Cristina; Antunes, Renato Altobelli

    2016-01-01

    Highlights: • Niobium oxide based films were obtained by DC magnetron sputtering. • Different deposition times were tested. • The best corrosion resistance was obtained for the Nb_2O_5 film produced at 15′. • Film porosity determines the corrosion resistance. - Abstract: Niobium oxide based thin films were deposited on AISI 316 stainless steel substrates using reactive DC magnetron sputtering. Structure, composition and corrosion resistance of the niobium oxide films were studied. The corrosion behavior of the specimens was evaluated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The concentration of niobium and oxygen in the films was obtained by Rutherford backscattering spectroscopy (RBS). The film structure was analyzed by X-ray diffractometry. The corrosion resistance of the substrate was improved by the Nb_2O_5 layers. The best protective performance was achieved for the deposition time of 15 min.

  1. Blue Diode Laser Absorption Spectroscopy of Pulsed Magnetron Discharge

    Czech Academy of Sciences Publication Activity Database

    Olejníček, Jiří; Do, H.T.; Hubička, Zdeněk; Hippler, R.; Jastrabík, Lubomír

    2006-01-01

    Roč. 45, 10B (2006), s. 8090-8094 ISSN 0021-4922 R&D Projects: GA AV ČR 1QS100100563; GA ČR GA202/05/2242 Institutional research plan: CEZ:AV0Z10100521; CEZ:AV0Z10100520 Keywords : laser absorption spectroscopy * pulsed magnetron * sputtering parameters Subject RIV: BH - Optics, Masers, Lasers Impact factor: 1.222, year: 2006

  2. Magnetron based high energy S-band linac system

    International Nuclear Information System (INIS)

    Tiwari, T.; Krishnan, R.; Phatangare, Manoj

    2012-01-01

    This paper deals with the study of magnetron based high energy S-band linear accelerator (linac) system operating at spot frequency 2.998 GHz. The energy and dose are two important parameters of linac system which depend on input power of microwave source and length of linac tube. Here the author has studied how these parameters can be improved for side coupled standing wave S-band linac system

  3. Magnetron co-sputtering system for coating ICF targets

    International Nuclear Information System (INIS)

    Hsieh, E.J.; Meyer, S.F.; Halsey, W.G.; Jameson, G.T.; Wittmayer, F.J.

    1981-01-01

    Fabrication of Inertial Confinement Fusion (ICF) targets requires deposition of various types of coatings on microspheres. The mechanical strength, and surface finish of the coatings are of concern in ICF experiments. The tensile strength of coatings can be controlled through grain refinement, selective doping and alloy formation. We have constructed a magnetron co-sputtering system to produce variable density profile coatings with high tensile strength on microspheres

  4. Deposition of copper coatings in a magnetron with liquid target

    Energy Technology Data Exchange (ETDEWEB)

    Tumarkin, A. V., E-mail: sanyahrustal@mail.ru; Kaziev, A. V.; Kolodko, D. V.; Pisarev, A. A.; Kharkov, M. M.; Khodachenko, G. V. [National Research Nuclear University MEPhI (Moscow Engineering Physics Institute) (Russian Federation)

    2015-12-15

    Copper coatings were deposited on monocrystalline Si substrates using a magnetron discharge with a liquid cathode in the metal vapour plasma. During the deposition, the bias voltage in the range from 0 V to–400 V was applied to the substrate. The prepared films were investigated by a scanning electron microscope, and their adhesive properties were studied using a scratch tester. It was demonstrated that the adhesion of the deposited films strongly depends on the bias voltage and varies in a wide range.

  5. TOPICAL REVIEW: Physics and phenomena in pulsed magnetrons: an overview

    Science.gov (United States)

    Bradley, J. W.; Welzel, T.

    2009-05-01

    This paper reviews the contribution made to the observation and understanding of the basic physical processes occurring in an important type of magnetized low-pressure plasma discharge, the pulsed magnetron. In industry, these plasma sources are operated typically in reactive mode where a cathode is sputtered in the presence of both chemically reactive and noble gases typically with the power modulated in the mid-frequency (5-350 kHz) range. In this review, we concentrate mostly, however, on physics-based studies carried out on magnetron systems operated in argon. This simplifies the physical-chemical processes occurring and makes interpretation of the observations somewhat easier. Since their first recorded use in 1993 there have been more than 300 peer-reviewed paper publications concerned with pulsed magnetrons, dealing wholly or in part with fundamental observations and basic studies. The fundamentals of these plasmas and the relationship between the plasma parameters and thin film quality regularly have whole sessions at international conferences devoted to them; however, since many different types of magnetron geometries have been used worldwide with different operating parameters the important results are often difficult to tease out. For example, we find the detailed observations of the plasma parameter (particle density and temperature) evolution from experiment to experiment are at best difficult to compare and at worst contradictory. We review in turn five major areas of studies which are addressed in the literature and try to draw out the major results. These areas are: fast electron generation, bulk plasma heating, short and long-term plasma parameter rise and decay rates, plasma potential modulation and transient phenomena. The influence of these phenomena on the ion energy and ion energy flux at the substrate is discussed. This review, although not exhaustive, will serve as a useful guide for more in-depth investigations using the referenced

  6. Physics and phenomena in pulsed magnetrons: an overview

    International Nuclear Information System (INIS)

    Bradley, J W; Welzel, T

    2009-01-01

    This paper reviews the contribution made to the observation and understanding of the basic physical processes occurring in an important type of magnetized low-pressure plasma discharge, the pulsed magnetron. In industry, these plasma sources are operated typically in reactive mode where a cathode is sputtered in the presence of both chemically reactive and noble gases typically with the power modulated in the mid-frequency (5-350 kHz) range. In this review, we concentrate mostly, however, on physics-based studies carried out on magnetron systems operated in argon. This simplifies the physical-chemical processes occurring and makes interpretation of the observations somewhat easier. Since their first recorded use in 1993 there have been more than 300 peer-reviewed paper publications concerned with pulsed magnetrons, dealing wholly or in part with fundamental observations and basic studies. The fundamentals of these plasmas and the relationship between the plasma parameters and thin film quality regularly have whole sessions at international conferences devoted to them; however, since many different types of magnetron geometries have been used worldwide with different operating parameters the important results are often difficult to tease out. For example, we find the detailed observations of the plasma parameter (particle density and temperature) evolution from experiment to experiment are at best difficult to compare and at worst contradictory. We review in turn five major areas of studies which are addressed in the literature and try to draw out the major results. These areas are: fast electron generation, bulk plasma heating, short and long-term plasma parameter rise and decay rates, plasma potential modulation and transient phenomena. The influence of these phenomena on the ion energy and ion energy flux at the substrate is discussed. This review, although not exhaustive, will serve as a useful guide for more in-depth investigations using the referenced

  7. Special traits of the millimeter wave relativistic magnetron

    International Nuclear Information System (INIS)

    Berdin, S.A.; Chizhov, K.V.; Gadetski, N.P.; Korenev, V.G.; Lebedenko, A.N.; Marchenko, M.I.; Magda, I.I.; Melezhik, O.G.; Sinitsin, V.G.; Soshenko, V.A.

    2014-01-01

    A 8 mm band relativistic magnetron is investigated experimentally and by means of numerical simulation. The physical effects are analyzed which influence negatively the r.f. generation. The processes capable of reducing effectiveness of the generation and duration of the generated pulse include forward and backward axial flows of electrons, and intense electric fields - the generated microwaves and the fields owing to the space charge

  8. Methods of Phase and Power Control in Magnetron Transmitters for Superconducting Accelerators

    Energy Technology Data Exchange (ETDEWEB)

    Kazadevich, G. [MUONS Inc., Batavia; Johnson, R. [MUONS Inc., Batavia; Neubauer, M. [MUONS Inc., Batavia; Lebedev, V. [Fermilab; Schappert, W. [Fermilab; Yakovlev, V. [Fermilab

    2017-05-01

    Various methods of phase and power control in magnetron RF sources of superconducting accelerators intended for ADS-class projects were recently developed and studied with conventional 2.45 GHz, 1 kW, CW magnetrons operating in pulsed and CW regimes. Magnetron transmitters excited by a resonant (injection-locking) phasemodulated signal can provide phase and power control with the rates required for precise stabilization of phase and amplitude of the accelerating field in Superconducting RF (SRF) cavities of the intensity-frontier accelerators. An innovative technique that can significantly increase the magnetron transmitter efficiency at the widerange power control required for superconducting accelerators was developed and verified with the 2.45 GHz magnetrons operating in CW and pulsed regimes. High efficiency magnetron transmitters of this type can significantly reduce the capital and operation costs of the ADSclass accelerator projects.

  9. Reconstruction of the static magnetic field of a magnetron

    Science.gov (United States)

    Krüger, Dennis; Köhn, Kevin; Gallian, Sara; Brinkmann, Ralf Peter

    2018-06-01

    The simulation of magnetron discharges requires a quantitatively correct mathematical model of the magnetic field structure. This study presents a method to construct such a model on the basis of a spatially restricted set of experimental data and a plausible a priori assumption on the magnetic field configuration. The example in focus is that of a planar circular magnetron. The experimental data are Hall probe measurements of the magnetic flux density in an accessible region above the magnetron plane [P. D. Machura et al., Plasma Sources Sci. Technol. 23, 065043 (2014)]. The a priori assumption reflects the actual design of the device, and it takes the magnetic field emerging from a center magnet of strength m C and vertical position d C and a ring magnet of strength m R , vertical position d R , and radius R. An analytical representation of the assumed field configuration can be formulated in terms of generalized hypergeometric functions. Fitting the ansatz to the experimental data with a least square method results in a fully specified analytical field model that agrees well with the data inside the accessible region and, moreover, is physically plausible in the regions outside of it. The outcome proves superior to the result of an alternative approach which starts from a multimode solution of the vacuum field problem formulated in terms of polar Bessel functions and vertical exponentials. As a first application of the obtained field model, typical electron and ion Larmor radii and the gradient and curvature drift velocities of the electron guiding center are calculated.

  10. Geometrical aspects of a hollow-cathode planar magnetron

    International Nuclear Information System (INIS)

    Wang, Z.; Cohen, S.A.

    1999-01-01

    A hollow-cathode planar magnetron (HCPM), built by surrounding a planar sputtering-magnetron cathode with a hollow-cathode structure (HCS) [Z. Wang and S. A. Cohen, J. Vac. Sci. Technol. A 17, 77 (1999)], is operable at substantially lower pressures than its planar-magnetron counterpart. HCPM operational parameters depend on the inner diameter D and length L of its cylindrical HCS. Only when L is greater than L 0 , a critical length, is the HCPM operable in the new low-pressure regime. The critical length varies with HCS inner diameter D. Explanations of the lower operational pressure regime, critical length, and plasma shape are proposed and compared with a one-dimension diffusion model for energetic electron transport. At pressures above 1 mTorr, Bohm diffusion (temperature congruent primary electron energy), with an ambipolar constraint, can explain the ion - electron pair creation required to sustain the discharge. At the lowest pressure, ∼0.3 mTorr, collision-limited diffusion creates fewer ion - electron pairs than required for steady state and therefore cannot explain the experimental data. The critical length L 0 is consistent with the magnetization length of the primary electrons. copyright 1999 American Institute of Physics

  11. Detection and identification of 700 drugs by multi-target screening with a 3200 Q TRAP LC-MS/MS system and library searching.

    Science.gov (United States)

    Dresen, S; Ferreirós, N; Gnann, H; Zimmermann, R; Weinmann, W

    2010-04-01

    The multi-target screening method described in this work allows the simultaneous detection and identification of 700 drugs and metabolites in biological fluids using a hybrid triple-quadrupole linear ion trap mass spectrometer in a single analytical run. After standardization of the method, the retention times of 700 compounds were determined and transitions for each compound were selected by a "scheduled" survey MRM scan, followed by an information-dependent acquisition using the sensitive enhanced product ion scan of a Q TRAP hybrid instrument. The identification of the compounds in the samples analyzed was accomplished by searching the tandem mass spectrometry (MS/MS) spectra against the library we developed, which contains electrospray ionization-MS/MS spectra of over 1,250 compounds. The multi-target screening method together with the library was included in a software program for routine screening and quantitation to achieve automated acquisition and library searching. With the help of this software application, the time for evaluation and interpretation of the results could be drastically reduced. This new multi-target screening method has been successfully applied for the analysis of postmortem and traffic offense samples as well as proficiency testing, and complements screening with immunoassays, gas chromatography-mass spectrometry, and liquid chromatography-diode-array detection. Other possible applications are analysis in clinical toxicology (for intoxication cases), in psychiatry (antidepressants and other psychoactive drugs), and in forensic toxicology (drugs and driving, workplace drug testing, oral fluid analysis, drug-facilitated sexual assault).

  12. Nano-crystalline Ag–PbTe thermoelectric thin films by a multi-target PLD system

    Energy Technology Data Exchange (ETDEWEB)

    Cappelli, E., E-mail: emilia.cappelli@ism.cnr.it [CNR-ISM, Montelibretti, Via Salaria Km 29.3, P.O.B. 10, 00016 Rome (Italy); Bellucci, A. [CNR-ISM, Montelibretti, Via Salaria Km 29.3, P.O.B. 10, 00016 Rome (Italy); Dip. Fisica, Un. Roma Sapienza, Piazzale Aldo Moro 2, 00185 Rome (Italy); Medici, L. [CNR-IMAA, Tito Scalo, 85050 Potenza (Italy); Mezzi, A.; Kaciulis, S. [CNR-ISMN, Montelibretti, Via Salaria Km 29.3, P.O.B. 10, 00016 Rome (Italy); Fumagalli, F.; Di Fonzo, F. [Center Nano Science Technology @Polimi, I.I.T., Via Pascoli 70/3, 20133 Milano (Italy); Trucchi, D.M. [CNR-ISM, Montelibretti, Via Salaria Km 29.3, P.O.B. 10, 00016 Rome (Italy)

    2015-05-01

    Highlights: • Thermoelectric PbTe thin films, with increasing Ag percentage, were deposited by PLD. • Almost stoichiometric PbTe (Ag doped) films were grown, as verified by XPS analysis. • GI-XRD established the formation of cubic PbTe, with nano-metric structure (∼35 nm). • Surface resistivity shows an increase in conductivity, with increasing Ag doping. • From Seebeck values and XPS depth analysis, 10% Ag seems to be the solubility limit. - Abstract: It has been evaluated the ability of ArF pulsed laser ablation to grow nano-crystalline thin films of high temperature PbTe thermoelectric material, and to obtain a uniform and controlled Ag blending, through the entire thickness of the film, using a multi-target system in vacuum. The substrate used was a mirror polished technical alumina slab. The increasing atomic percentage of Ag effect on physical–chemical and electronic properties was evaluated in the range 300–575 K. The stoichiometry and the distribution of the Ag component, over the whole thickness of the samples deposited, have been studied by XPS (X-ray photoelectron spectroscopy) and corresponding depth profiles. The crystallographic structure of the film was analyzed by grazing incidence X-ray diffraction (GI-XRD) system. Scherrer analysis for crystallite size shows the presence of nano-structures, of the order of 30–35 nm. Electrical resistivity of the samples, studied by the four point probe method, as a function of increasing Ag content, shows a typical semi-conductor behavior. From conductivity values, carrier concentration and Seebeck parameter determination, the power factor of deposited films was calculated. Both XPS, Hall mobility and Seebeck analysis seem to indicate a limit value to the Ag solubility of the order of 5%, for thin films of ∼200 nm thickness, deposited at 350 °C. These data resulted to be comparable to theoretical evaluation for thin films but order of magnitude lower than the corresponding bulk materials.

  13. Simulation Research Framework with Embedded Intelligent Algorithms for Analysis of Multi-Target, Multi-Sensor, High-Cluttered Environments

    Science.gov (United States)

    Hanlon, Nicholas P.

    nearly identical performance metrics at orders of magnitude faster in execution. Second, a fuzzy inference system is presented that alleviates air traffic controllers from information overload by utilizing flight plan data and radar/GPS correlation values to highlight aircraft that deviate from their intended routes. Third, a genetic algorithm optimizes sensor placement that is robust and capable of handling unexpected routes in the environment. Fourth, a fuzzy CUSUM algorithm more accurately detects and corrects aircraft mode changes. Finally, all the work is packaged in a holistic simulation research framework that provides evaluation and analysis of various multi-sensor, multi-target scenarios.

  14. Magnetron with smooth anode. Statistical theory and ordered oscillations; Magnetron a anode lisse. Theorie statistique et oscillations ordonnees

    Energy Technology Data Exchange (ETDEWEB)

    Coste, J.

    1961-03-15

    We have to investigate the equilibrium regime that appears between a hot cathode and the electronic cloud that is confined around the cathode by a magnetic field parallel to its axis. The densities being high enough to involve the effect of space charge. The challenge of the magnetron theory is to face 2 issues: first the structure of the electronic cloud in a diode submitted to a magnetic field and secondly the oscillations that are likely to appear in this cloud. In this work we have made 2 attempts to clarify the situation, we have extended the classical theory of the static charge of space through a study of its oscillation modes on one hand and on the other hand we have tackled the issue of the structure of the electronic cloud with the tool of statistics. This document is divided into 2 chapters. In the first chapter we present a static study of the magnetron in which we take a statistical approach deliberately. We give answers to the issue of the thermodynamical equilibrium of the electronic cloud and we have found a mode very close to the Brillouin mode. The statistical approach has made us discuss the boundary conditions on the cathode, it means the coupling between the cathode and the electronic cloud. In the second chapter we present the theoretical study of the oscillations in a magnetron operating in the Brillouin mode. The resonances that appear in experimental data stay difficult to explain.

  15. Computer-aided design of multi-target ligands at A1R, A2AR and PDE10A, key proteins in neurodegenerative diseases.

    Science.gov (United States)

    Kalash, Leen; Val, Cristina; Azuaje, Jhonny; Loza, María I; Svensson, Fredrik; Zoufir, Azedine; Mervin, Lewis; Ladds, Graham; Brea, José; Glen, Robert; Sotelo, Eddy; Bender, Andreas

    2017-12-30

    Compounds designed to display polypharmacology may have utility in treating complex diseases, where activity at multiple targets is required to produce a clinical effect. In particular, suitable compounds may be useful in treating neurodegenerative diseases by promoting neuronal survival in a synergistic manner via their multi-target activity at the adenosine A 1 and A 2A receptors (A 1 R and A 2A R) and phosphodiesterase 10A (PDE10A), which modulate intracellular cAMP levels. Hence, in this work we describe a computational method for the design of synthetically feasible ligands that bind to A 1 and A 2A receptors and inhibit phosphodiesterase 10A (PDE10A), involving a retrosynthetic approach employing in silico target prediction and docking, which may be generally applicable to multi-target compound design at several target classes. This approach has identified 2-aminopyridine-3-carbonitriles as the first multi-target ligands at A 1 R, A 2A R and PDE10A, by showing agreement between the ligand and structure based predictions at these targets. The series were synthesized via an efficient one-pot scheme and validated pharmacologically as A 1 R/A 2A R-PDE10A ligands, with IC 50 values of 2.4-10.0 μM at PDE10A and K i values of 34-294 nM at A 1 R and/or A 2A R. Furthermore, selectivity profiling of the synthesized 2-amino-pyridin-3-carbonitriles against other subtypes of both protein families showed that the multi-target ligand 8 exhibited a minimum of twofold selectivity over all tested off-targets. In addition, both compounds 8 and 16 exhibited the desired multi-target profile, which could be considered for further functional efficacy assessment, analog modification for the improvement of selectivity towards A 1 R, A 2A R and PDE10A collectively, and evaluation of their potential synergy in modulating cAMP levels.

  16. Reactive magnetron sputtering model at making Ti-TiOx coatings

    International Nuclear Information System (INIS)

    Luchkin, A G; Kashapov, N F

    2014-01-01

    Mathematical model of reactive magnetron sputtering for plant VU 700-D is described. Approximating curves for experimental current-voltage characteristic for two gas input schemas are shown. Choice of gas input schema influences on model parameters (mainly on pumping speed). Reactive magnetron sputtering model allows develop technology of Ti - TiO x coatings deposition without changing atmosphere and pressure in vacuum chamber

  17. A Compact, Pi-Mode Extraction Scheme for the Axial B-Field Recirculating Planar Magnetron

    Science.gov (United States)

    2012-07-23

    Figure 4). Thus, in a planar magnetron, the minimum phase velocity, vph , to stay above cutoff in the rectangular waveguide is ℎ = ...as magnetrons, electrons must be accelerated such that they are in synchronism with the phase velocity, vph , of the electromagnetic wave for an

  18. High power impulse magnetron sputtering and its applications

    Science.gov (United States)

    Yan, YUAN; Lizhen, YANG; Zhongwei, LIU; Qiang, CHEN

    2018-04-01

    High power impulse magnetron sputtering (HiPIMS) has attracted a great deal of attention because the sputtered material is highly ionized during the coating process, which has been demonstrated to be advantageous for better quality coating. Therefore, the mechanism of the HiPIMS technique has recently been investigated. In this paper, the current knowledge of HiPIMS is described. We focus on the mechanical properties of the deposited thin film in the latest applications, including hard coatings, adhesion enhancement, tribological performance, and corrosion protection layers. A description of the electrical, optical, photocatalytic, and functional coating applications are presented. The prospects for HiPIMS are also discussed in this work.

  19. Heteroepitaxial Ge-on-Si by DC magnetron sputtering

    Directory of Open Access Journals (Sweden)

    Martin Steglich

    2013-07-01

    Full Text Available The growth of Ge on Si(100 by DC Magnetron Sputtering at various temperatures is studied by Spectroscopic Ellipsometry and Transmission Electron Microscopy. Smooth heteroepitaxial Ge films are prepared at relatively low temperatures of 380°C. Typical Stransky-Krastanov growth is observed at 410°C. At lower temperatures (320°C, films are essentially amorphous with isolated nanocrystallites at the Si-Ge interface. A minor oxygen contamination at the interface, developing after ex-situ oxide removal, is not seen to hinder epitaxy. Compensation of dislocation-induced acceptors in Ge by sputtering from n-doped targets is proposed.

  20. Pd-catalysts for DFAFC prepared by magnetron sputtering

    Czech Academy of Sciences Publication Activity Database

    Bieloshapka, Igor; Jiříček, Petr; Vorokhta, M.; Tomšík, Elena; Rednyk, A.; Perekrestov, R.; Jurek, Karel; Ukraintsev, Egor; Hruška, Karel; Romanyuk, Olexandr; Lesiak, B.

    2017-01-01

    Roč. 419, Oct (2017), s. 838-846 ISSN 0169-4332 R&D Projects: GA ČR(CZ) GBP108/12/G108; GA MŠk LM2015088 Institutional support: RVO:68378271 ; RVO:61389013 Keywords : Pd catalyst * formic acid fuel cell * magnetron sputtering * DFAFC * surface morphology Subject RIV: BM - Solid Matter Physics ; Magnetism; BM - Solid Matter Physics ; Magnetism (UMCH-V) OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.); Condensed matter physics (including formerly solid state physics, supercond.) (UMCH-V) Impact factor: 3.387, year: 2016

  1. Some properties of the gas magnetron; neke osobine gasnog magnetrona

    Energy Technology Data Exchange (ETDEWEB)

    Miljevic, V [Boris Kidric Institute of nuclear sciences, Vinca, Belgrade (Yugoslavia)

    1979-07-01

    The cylindrical magnetron diode with directly heated cathode, filled with argon at low pressure, has been studied. In the case of high magnetic fields and low gas pressure the motion of electrons is reduced to the rotation around the cathode with superimposed allow radial drift. It is found that the plasma formation time in in the msec region. The critical magnetic field in the vacuum diode (B{sub c}), and its value increases with the increase of the anode voltage and working pressure. (author)

  2. Phase Grouping of Larmor Electrons by a Synchronous Wave in Controlled Magnetrons

    Energy Technology Data Exchange (ETDEWEB)

    Kazakevich, G. [MUONS Inc., Batavia; Johnson, R. [MUONS Inc., Batavia; Lebedev, V. [Fermilab; Yakovlev, V. [Fermilab

    2018-04-01

    A simplified analytical model based on the charge drift approximation has been developed. It considers the resonant interaction of the synchronous wave with the flow of Larmor electrons in a magnetron. The model predicts stable coherent generation of the tube above and below the threshold of self-excitation. This occurs if the magnetron is driven by a sufficient resonant injected signal (up to -10 dB). The model substantiates precise stability, high efficiency and low noise at the range of the magnetron power control over 10 dB by variation of the magnetron current. The model and the verifying experiments with 2.45 GHz, 1 kW magnetrons are discussed.

  3. High temperature superconducting films by rf magnetron sputtering

    International Nuclear Information System (INIS)

    Kadin, A.M.; Ballentine, P.H.

    1989-01-01

    The authors have produced sputtered films of Y-Ba-Cu-O and Bi-Sr-Ca-Cu-O by rf magnetron sputtering from an oxide target consisting of loose reacted powder. The use of a large 8-inch stoichiometric target in the magnetron mode permits films located above the central region to be free of negative-ion resputtering effects, and hence yields reproducible, uniform stoichiometric compositions for a wide range of substrate temperatures. Superconducting YBCO films have been obtained either by sputtering at low temperatures followed by an 850 0 C oxygen anneal, or alternatively by depositing onto substrates heated to ∼600 - 650 0 C and cooling in oxygen. Films prepared by the former method on cubic zirconia substrate consist of randomly oriented crystallites with zero resistance above 83 K. Those deposited on zirconia at medium temperatures without the high-temperature anneal contain smooth partially oriented crystallites, with a slightly depressed T/sub c/ ∼75K. Finally, superconducting films have been deposited on MgO using a BiSrCaCu/sub 2/O/sub x/ powder target

  4. Recent operation of the FNAL magnetron H- ion source

    Science.gov (United States)

    Karns, P. R.; Bollinger, D. S.; Sosa, A.

    2017-08-01

    This paper will detail changes in the operational paradigm of the Fermi National Accelerator Laboratory (FNAL) magnetron H- ion source due to upgrades in the accelerator system. Prior to November of 2012 the H- ions for High Energy Physics (HEP) experiments were extracted at ˜18 keV vertically downward into a 90 degree bending magnet and accelerated through a Cockcroft-Walton accelerating column to 750 keV. Following the upgrade in the fall of 2012 the H- ions are now directly extracted from a magnetron at 35 keV and accelerated to 750 keV by a Radio Frequency Quadrupole (RFQ). This change in extraction energy as well as the orientation of the ion source required not only a redesign of the ion source, but an updated understanding of its operation at these new values. Discussed in detail are the changes to the ion source timing, arc discharge current, hydrogen gas pressure, and cesium delivery system that were needed to maintain consistent operation at >99% uptime for HEP, with an increased ion source lifetime of over 9 months.

  5. Plasma properties of RF magnetron sputtering system using Zn target

    Energy Technology Data Exchange (ETDEWEB)

    Nafarizal, N.; Andreas Albert, A. R.; Sharifah Amirah, A. S.; Salwa, O.; Riyaz Ahmad, M. A. [Microelectronic and Nanotechnology - Shamsuddin Research Centre (MiNT-SRC), Faculty of Electrical and Electronic Engineering, Universiti Tun Hussein Onn Malaysia 86400 Parit Raja, Batu Pahat, Johor (Malaysia)

    2012-06-29

    In the present work, we investigate the fundamental properties of magnetron sputtering plasma using Zn target and its deposited Zn thin film. The magnetron sputtering plasma was produced using radio frequency (RF) power supply and Argon (Ar) as ambient gas. A Langmuir probe was used to collect the current from the plasma and from the current intensity, we calculate the electron density and electron temperature. The properties of Zn sputtering plasma at various discharge conditions were studied. At the RF power ranging from 20 to 100 W and gas pressure 5 mTorr, we found that the electron temperature was almost unchanged between 2-2.5 eV. On the other hand, the electron temperature increased drastically from 6 Multiplication-Sign 10{sup 9} to 1 Multiplication-Sign 10{sup 10}cm{sup -3} when the discharge gas pressure increased from 5 to 10 mTorr. The electron microscope images show that the grain size of Zn thin film increase when the discharge power is increased. This may be due to the enhancement of plasma density and sputtered Zn density.

  6. Prediction of Multi-Target Networks of Neuroprotective Compounds with Entropy Indices and Synthesis, Assay, and Theoretical Study of New Asymmetric 1,2-Rasagiline Carbamates

    Directory of Open Access Journals (Sweden)

    Francisco J. Romero Durán

    2014-09-01

    Full Text Available In a multi-target complex network, the links (Lij represent the interactions between the drug (di and the target (tj, characterized by different experimental measures (Ki, Km, IC50, etc. obtained in pharmacological assays under diverse boundary conditions (cj. In this work, we handle Shannon entropy measures for developing a model encompassing a multi-target network of neuroprotective/neurotoxic compounds reported in the CHEMBL database. The model predicts correctly >8300 experimental outcomes with Accuracy, Specificity, and Sensitivity above 80%–90% on training and external validation series. Indeed, the model can calculate different outcomes for >30 experimental measures in >400 different experimental protocolsin relation with >150 molecular and cellular targets on 11 different organisms (including human. Hereafter, we reported by the first time the synthesis, characterization, and experimental assays of a new series of chiral 1,2-rasagiline carbamate derivatives not reported in previous works. The experimental tests included: (1 assay in absence of neurotoxic agents; (2 in the presence of glutamate; and (3 in the presence of H2O2. Lastly, we used the new Assessing Links with Moving Averages (ALMA-entropy model to predict possible outcomes for the new compounds in a high number of pharmacological tests not carried out experimentally.

  7. A Novel, Multi-Target Natural Drug Candidate, Matrine, Improves Cognitive Deficits in Alzheimer's Disease Transgenic Mice by Inhibiting Aβ Aggregation and Blocking the RAGE/Aβ Axis.

    Science.gov (United States)

    Cui, Lili; Cai, Yujie; Cheng, Wanwen; Liu, Gen; Zhao, Jianghao; Cao, Hao; Tao, Hua; Wang, Yan; Yin, Mingkang; Liu, Tingting; Liu, Yu; Huang, Pengru; Liu, Zhou; Li, Keshen; Zhao, Bin

    2017-04-01

    The treatment of AD is a topic that has puzzled researchers for many years. Current mainstream theories still consider Aβ to be the most important target for the cure of AD. In this study, we attempted to explore multiple targets for AD treatments with the aim of identifying a qualified compound that could both inhibit the aggregation of Aβ and block the RAGE/Aβ axis. We believed that a compound that targets both Aβ and RAGE may be a feasible strategy for AD treatment. A novel and small natural compound, Matrine (Mat), was identified by high-throughput screening of the main components of traditional Chinese herbs used to treat dementia. Various experimental techniques were used to evaluate the effect of Mat on these two targets both in vitro and in AD mouse model. Mat could inhibit Aβ42-induced cytotoxicity and suppress the Aβ/RAGE signaling pathway in vitro. Additionally, the results of in vivo evaluations of the effects of Mat on the two targets were consistent with the results of our in vitro studies. Furthermore, Mat reduced proinflammatory cytokines and Aβ deposition and attenuated the memory deficits of AD transgenic mice. We believe that this novel, multi-target strategy to inhibit both Aβ and RAGE, is worthy of further exploration. Therefore, our future studies will focus on identifying even more effective multi-target compounds for the treatment of AD based on the molecular structure of Mat.

  8. An inverted cylindrical sputter magnetron as metal vapor supply for electron cyclotron resonance ion sources

    Energy Technology Data Exchange (ETDEWEB)

    Weichsel, T., E-mail: tim.weichsel@fep.fraunhofer.de; Hartung, U.; Kopte, T. [Fraunhofer Institute for Electron Beam and Plasma Technology, 01277 Dresden (Germany); Zschornack, G. [Institute of Solid State Physics, Dresden University of Technology, 01062 Dresden, Germany and Helmholtz-Zentrum Dresden-Rossendorf e.V., Institute of Ion Beam Physics and Materials Research, Dresden (Germany); Kreller, M.; Silze, A. [DREEBIT GmbH, 01900 Grossroehrsdorf (Germany)

    2014-05-15

    An inverted cylindrical sputter magnetron device has been developed. The magnetron is acting as a metal vapor supply for an electron cyclotron resonance (ECR) ion source. FEM simulation of magnetic flux density was used to ensure that there is no critical interaction between both magnetic fields of magnetron and ECR ion source. Spatially resolved double Langmuir probe and optical emission spectroscopy measurements show an increase in electron density by one order of magnitude from 1 × 10{sup 10} cm{sup −3} to 1 × 10{sup 11} cm{sup −3}, when the magnetron plasma is exposed to the magnetic mirror field of the ECR ion source. Electron density enhancement is also indicated by magnetron plasma emission photography with a CCD camera. Furthermore, photographs visualize the formation of a localized loss-cone - area, when the magnetron is operated at magnetic mirror field conditions. The inverted cylindrical magnetron supplies a metal atom load rate of R > 1 × 10{sup 18} atoms/s for aluminum, which meets the demand for the production of a milliampere Al{sup +} ion beam.

  9. Simulation Study Using an Injection Phase-locked Magnetron as an Alternative Source for SRF Accelerators

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Haipeng [Thomas Jefferson National Accelerator Facility, Newport News, VA (United States); Plawski, Tomasz E. [Thomas Jefferson National Accelerator Facility, Newport News, VA (United States); Rimmer, Robert A. [Thomas Jefferson National Accelerator Facility, Newport News, VA (United States)

    2015-09-01

    As a drop-in replacement for the CEBAF CW klystron system, a 1497 MHz, CW-type high-efficiency magnetron using injection phase lock and amplitude variation is attractive. Amplitude control using magnetic field trimming and anode voltage modulation has been studied using analytical models and MATLAB/Simulink simulations. Since the 1497 MHz magnetron has not been built yet, previously measured characteristics of a 2.45GHz cooker magnetron are used as reference. The results of linear responses to the amplitude and phase control of a superconducting RF (SRF) cavity, and the expected overall benefit for the current CEBAF and future MEIC RF systems are presented in this paper.

  10. Spatiotemporal synchronization of drift waves in a magnetron sputtering plasma

    Energy Technology Data Exchange (ETDEWEB)

    Martines, E.; Zuin, M.; Cavazzana, R.; Antoni, V.; Serianni, G.; Spolaore, M.; Vianello, N. [Consorzio RFX, Padova (Italy); Adámek, J. [Institute of Plasma Physics AS CR, Prague (Czech Republic)

    2014-10-15

    A feedforward scheme is applied for drift waves control in a magnetized magnetron sputtering plasma. A system of driven electrodes collecting electron current in a limited region of the explored plasma is used to interact with unstable drift waves. Drift waves actually appear as electrostatic modes characterized by discrete wavelengths of the order of few centimeters and frequencies of about 100 kHz. The effect of external quasi-periodic, both in time and space, travelling perturbations is studied. Particular emphasis is given to the role played by the phase relation between the natural and the imposed fluctuations. It is observed that it is possible by means of localized electrodes, collecting currents which are negligible with respect to those flowing in the plasma, to transfer energy to one single mode and to reduce that associated to the others. Due to the weakness of the external action, only partial control has been achieved.

  11. Spatiotemporal synchronization of drift waves in a magnetron sputtering plasma

    International Nuclear Information System (INIS)

    Martines, E.; Zuin, M.; Cavazzana, R.; Antoni, V.; Serianni, G.; Spolaore, M.; Vianello, N.; Adámek, J.

    2014-01-01

    A feedforward scheme is applied for drift waves control in a magnetized magnetron sputtering plasma. A system of driven electrodes collecting electron current in a limited region of the explored plasma is used to interact with unstable drift waves. Drift waves actually appear as electrostatic modes characterized by discrete wavelengths of the order of few centimeters and frequencies of about 100 kHz. The effect of external quasi-periodic, both in time and space, travelling perturbations is studied. Particular emphasis is given to the role played by the phase relation between the natural and the imposed fluctuations. It is observed that it is possible by means of localized electrodes, collecting currents which are negligible with respect to those flowing in the plasma, to transfer energy to one single mode and to reduce that associated to the others. Due to the weakness of the external action, only partial control has been achieved

  12. Dependence of plasma characteristics on dc magnetron sputter parameters

    International Nuclear Information System (INIS)

    Wu, S.Z.

    2005-01-01

    Plasma discharge characteristics of a dc magnetron system were measured by a single Langmuir probe at the center axis of the dual-side process chamber. Plasma potential, floating potential, electron and ion densities, and electron temperature were extracted with varying dc power and gas pressure during sputter deposition of a metal target; strong correlations were shown between these plasma parameters and the sputter parameters. The electron density was controlled mostly by secondary electron generation in constant power mode, while plasma potential reflects the confinement space variation due to change of discharge voltage. When discharge pressure was varied, plasma density increases with the increased amount of free stock molecules, while electron temperature inversely decreased, due to energy-loss collision events. In low-pressure discharges, the electron energy distribution function measurements show more distinctive bi-Maxwellian distribution, with the fast electron temperature gradually decreases with increased gas pressure

  13. Magnetron with flux switching cathode and method of operation

    Science.gov (United States)

    Aaron, D.B.; Wiley, J.D.

    1989-09-12

    A magnetron sputtering apparatus is formed with a plurality of cells each for generating an independent magnetic field within a different region in the chamber of the apparatus. Each magnetic field aids in maintaining an ion plasma in the respective region of the chamber. One of a plurality of sputtering material targets is positioned on an electrode adjacent to each region so that said ions strike the target ejecting some of the target material. By selectively generating each magnetic field, the ion plasma may be moved from region to region to sputter material from different targets. The sputtered material becomes deposited on a substrate mounted on another electrode within the chamber. The duty cycle of each cell can be dynamically varied during the deposition to produce a layer having a graded composition throughout its thickness. 5 figs.

  14. Crystalline silicon films grown by pulsed dc magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Reinig, Peter; Fenske, Frank; Fuhs, Walther; Selle, Burkhardt [Hahn-Meitner-Institut Berlin, Abt. Silizium-Photovoltaik, Kekulestr. 5, D-12489 Berlin (Germany)

    2002-04-01

    Pulsed dc magnetron sputtering is used as a novel method for the deposition of crystalline silicon films on glass substrates. Hydrogen-free polycrystalline Si-films are deposited with high deposition rates at temperatures of 400-450 C and pulse frequencies f in the range 0-250 kHz. Strong preferential (100) orientation of the crystallites is observed with increasing f. High frequency and similarly high negative substrate bias cause an increase of the Ar content and an enhancement of structural disorder. Measurements of the transient floating potential suggest that the observed structural effects are related to bombardment of the growing film by Ar{sup +} ions of high energy.

  15. Characterisation of magnetron sputtered SmCo5 thin films

    International Nuclear Information System (INIS)

    Wang, Y.; Sood, D.K.; Kothari

    1999-01-01

    SmCo 5 thin films were deposited using DC magnetron sputtering on single crystal silicon substrate with chromium and SiO 2 top layers. Deposition was carried out at three different substrate temperatures: room temperature, 400 deg C and 600 deg C. Films were characterised by using Rutherford Backscattering Spectroscopy (RBS), X-ray Diffraction (XRD), Secondary Ion Mass Spectrometry (SIMS) and SQUID magnetometer. RBS analysis indicated that the films have excellent stoichiometry with the Sm to Co ratio of 1:5. This analysis also showed that the films deposited or annealed at high temperatures (≥600 deg C) indicated significant inter-diffusion at the interface between the barrier layer and the film. Oxygen was found to be the major impurity in the films. XRD data indicated that the films formed 1:5 and 2:17 phases under different deposition conditions. The preliminary studies of these films using magnetic force microscopy revealed the presence of magnetic domains

  16. Monte Carlo simulation of ionization in a magnetron plasma

    International Nuclear Information System (INIS)

    Miranda, J.E.; Goeckner, M.J.; Goree, J.; Sheridan, T.E.

    1990-01-01

    A Monte Carlo simulation of electrons emitted from the cathode of a planar magnetron is tested against experiments that were reported by Wendt, Lieberman, and Meuth [J. Vac. Sci. Technol. A 6, 1827 (1988)] and by Gu and Lieberman [J. Vac. Sci. Technol. A 6, 2960 (1988)]. Comparing their measurements of the radial profile of current and the axial profile of optical emission to the ionization profiles predicted by the model, we find good agreement for a typical magnetic field strength of 456 G. We also find that at 456 G the product of the average number of ionizations left-angle N i right-angle and the secondary electron emission coefficient γ is ∼1. This indicates that secondary emission contributes significantly to the ionization that sustains the discharge. At 171 G, however, left-angle N i right-angle γ much-lt 1, revealing that cathode emission is inadequate to sustain a discharge at a low magnetic field

  17. Preclinical FLT-PET and FDG-PET imaging of tumor response to the multi-targeted Aurora B kinase inhibitor, TAK-901

    International Nuclear Information System (INIS)

    Cullinane, Carleen; Waldeck, Kelly L.; Binns, David; Bogatyreva, Ekaterina; Bradley, Daniel P.; Jong, Ron de; McArthur, Grant A.; Hicks, Rodney J.

    2014-01-01

    Introduction: The Aurora kinases play a key role in mitosis and have recently been identified as attractive targets for therapeutic intervention in cancer. The aim of this study was therefore to investigate the utility of 3′-[ 18 F]fluoro-3′-deoxythymidine (FLT) and 2-deoxy-2-[ 18 F]fluoro-D-glucose (FDG) for assessment of tumor response to the multi-targeted Aurora B kinase inhibitor, TAK-901. Methods: Balb/c nude mice bearing HCT116 colorectal xenografts were treated with up to 30 mg/kg TAK 901 or vehicle intravenously twice daily for two days on a weekly cycle. Tumor growth was monitored by calliper measurements and PET imaging was performed at baseline, day 4, 8, 11 and 15. Tumors were harvested at time points corresponding to days of PET imaging for analysis of ex vivo markers of cell proliferation and metabolism together with markers of Aurora B kinase inhibition including phospho-histone H3 (pHH3) and senescence associated β-galactosidase. Results: Tumor growth was inhibited by 60% on day 12 of 30 mg/kg TAK-901 therapy. FLT uptake was significantly reduced by day 4 of treatment and this corresponded with reduction in bromodeoxyuridine and pHH3 staining by immunohistochemistry. All biomarkers rebounded towards baseline levels by the commencement of the next treatment cycle, consistent with release of Aurora B kinase suppression. TAK-901 therapy had no impact on glucose metabolism as assessed by FDG uptake and GLUT1 staining by immunohistochemistry. Conclusions: FLT-PET, but not FDG-PET, is a robust non-invasive imaging biomarker of early HCT116 tumor response to the on-target effects of the multi-targeted Aurora B kinase inhibitor, TAK-901. Advances in knowledge and implications for patient care: This is the first report to demonstrate the impact of the multi-targeted Aurora B kinase inhibitor, TAK-901 on tumor FLT uptake. The findings provide a strong rationale for the evaluation of FLT-PET as an early biomarker of tumor response in the early phase

  18. Contribution to crystallographical and mechanical analysis of molybdenum coatings prepared by magnetron cathode sputtering

    International Nuclear Information System (INIS)

    Bosland, P.

    1989-07-01

    Molybdenum coatings with different compression stresses are obtained by magnetron cathode sputtering by varying negative voltage applied to the substrate during deposition. Stress evolution, crystal texture and argon content are studied [fr

  19. CrN thin films prepared by reactive DC magnetron sputtering for symmetric supercapacitors

    KAUST Repository

    Wei, Binbin; Liang, Hanfeng; Zhang, Dongfang; Wu, Zhengtao; Qi, Zhengbing; Wang, Zhoucheng

    2016-01-01

    stability are promising candidates as supercapacitor electrode materials. In this work, we report the fabrication of CrN thin films using reactive DC magnetron sputtering and further their applications for symmetric supercapacitors for the first time. The Cr

  20. Chromium-nanodiamond coatings obtained by magnetron sputtering and their tribological properties

    Science.gov (United States)

    Atamanov, M. V.; Khrushchov, M. M.; Marchenko, E. A.; Shevchenko, N. V.; Levin, I. S.; Petrzhik, M. I.; Miroshnichenko, V. I.; Relianu, M. D.

    2017-07-01

    Peculiarities of structure, chemical and phase composition, micromechanical and tribological properties of chromium-based coatings obtained by magnetron-sputtering of composite and/or compacted chromium-nanodiamond targets have been investigated.

  1. NOVEL TECHNIQUE OF POWER CONTROL IN MAGNETRON TRANSMITTERS FOR INTENSE ACCELERATORS

    Energy Technology Data Exchange (ETDEWEB)

    Kazakevich, G. [MUONS Inc., Batavia; Johnson, R. [MUONS Inc., Batavia; Neubauer, M.; Lebedev, V. [Fermilab; Schappert, W. [Fermilab; Yakovlev, V. [Fermilab

    2016-10-21

    A novel concept of a high-power magnetron transmitter allowing dynamic phase and power control at the frequency of locking signal is proposed. The transmitter compensating parasitic phase and amplitude modulations inherent in Superconducting RF (SRF) cavities within closed feedback loops is intended for powering of the intensity-frontier superconducting accelerators. The con- cept uses magnetrons driven by a sufficient resonant (in- jection-locking) signal and fed by the voltage which can be below the threshold of self-excitation. This provides an extended range of power control in a single magnetron at highest efficiency minimizing the cost of RF power unit and the operation cost. Proof-of-principle of the proposed concept demonstrated in pulsed and CW regimes with 2.45 GHz, 1kW magnetrons is discussed here. A conceptual scheme of the high-power transmitter allowing the dynamic wide-band phase and y power controls is presented and discussed.

  2. Additive manufactured Ti6Al4V scaffolds with the RF- magnetron sputter deposited hydroxyapatite coating

    International Nuclear Information System (INIS)

    Chudinova, E; Surmeneva, M; Surmenev, R; Koptioug, A; Scoglund, P

    2016-01-01

    Present paper reports on the results of surface modification of the additively manufactured porous Ti6Al4V scaffolds. Radio frequency (RF) magnetron sputtering was used to modify the surface of the alloy via deposition of the biocompatible hydroxyapatite (HA) coating. The surface morphology, chemical and phase composition of the HA-coated alloy were studied. It was revealed that RF magnetron sputtering allows preparing a homogeneous HA coating onto the entire surface of scaffolds. (paper)

  3. Recent progress in thin film processing by magnetron sputtering with plasma diagnostics

    International Nuclear Information System (INIS)

    Han, Jeon G

    2009-01-01

    The precise control of the structure and related properties becomes crucial for sophisticated applications of thin films deposited by magnetron sputtering in emerging industries including the flat panel display, digital electronics and nano- and bio-industries. The film structure is closely related to the total energy delivered to the substrate surface for nucleation and growth during all kinds of thin film processes, including magnetron sputtering. Therefore, the energy delivered to the surface for nucleation and growth during magnetron sputtering should be measured and analysed by integrated diagnostics of the plasma parameters which are closely associated with the process parameters and other external process conditions. This paper reviews the background of thin film nucleation and growth, the status of magnetron sputtering technology and the progress of plasma diagnostics for plasma processing. The evolution of the microstructure during magnetron sputtering is then discussed with respect to the change in the process variables in terms of the plasma parameters along with empirical data of the integrated plasma diagnostics for various magnetron sputtering conditions with conventional dc, pulsed dc and high power pulsed dc sputtering modes. Among the major energy terms to be discussed are the temperature change in the top surface region and the energies of ions and neutral species. (topical review)

  4. Pulsed Power Generators For Two-section Lia Relativistic Magnetron Driver

    CERN Document Server

    Agafonov, A V; Pevchev, V P

    2004-01-01

    Two prototypes of pulsed power generators for a two-sectional LIA - specialized driver of a relativistic magnetron were constructed and tested. The driver for the double-sided powering of a relativistic magnetron consists of two identical sets of induction modules (two sections of LIA) with inner electrodes - vacuum adders connected to both sides of a coaxial magnetron. It provides the symmetric power flowing in a magnetron and a possibility of localising of the electron flow in magnetron interaction region. The first generator designed for a small-scale laboratory installation provides the output pulses of 100 ns in duration with voltage amplitude of 50 kV at repetition rate of 1 pps. The construction of the generator is based on the application of experimental capacitor banks designed as a pulse forming line with the next parameters: charging voltage - 80 kV, impedance - 1,7 Ohm, pulse duration - 80 ns at a matched load. The second generator was designed for 1 MV integrated LIA - magnetron system. It cons...

  5. A novel injection-locked amplitude-modulated magnetron at 1497 MHz

    Energy Technology Data Exchange (ETDEWEB)

    Neubauer, Michael [Muons Inc., Batavia, IL (United States); Wang, Haipeng [Thomas Jefferson National Accelerator Facility (TJNAF), Newport News, VA (United States)

    2015-12-15

    Thomas Jefferson National Accelerator Facility (JLab) uses low efficiency klystrons in the CEBAF machine. In the older portion they operate at 30% efficiency with a tube mean time between failure (MTBF) of five to six years. A highly efficient source (>55-60%) must provide a high degree of backwards compatibility, both in size and voltage requirements, to replace the klystron presently used at JLab, while providing energy savings. Muons, Inc. is developing a highly reliable, highly efficient RF source based upon a novel injection-locked amplitude modulated (AM) magnetron with a lower total cost of ownership, >80% efficiency, and MTBF of six to seven years. The design of the RF source is based upon a single injection-locked magnetron system at 8 kW capable of operating up to 13 kW, using the magnetron magnetic field to achieve the AM required for backwards compatibility to compensate for microphonics and beam loads. A novel injection-locked 1497 MHz 8 kW AM magnetron with a trim magnetic coil was designed and its operation numerically simulated during the Phase I project. The low-level RF system to control the trim field and magnetron anode voltage was designed and modeled for operation at the modulation frequencies of the microphonics. A plan for constructing a prototype magnetron and control system was developed.

  6. The experience with JET's combined dc/Rf glow discharge cleaning (GDC) system

    International Nuclear Information System (INIS)

    Pearce, R.J.H.; Andrew, P.; Bryan, S.

    1996-01-01

    The JET Tokamak was fitted with four new electrodes of novel design, each powered from individual computer controlled dc and RF supplies. Details of enhancements and problems from 15 months experience with the system are outlined. Experiments were performed to assess the effect of RF on the glow discharge characteristics, and to establish stable glow at low pressure and high voltage. JET combined RF/dc glow discharge cleaning (GDC) had no significant advantages over pure dc GDC, provided highly stable dc current control was obtained. In fact, the mechanically weak electrode inductor spiral required to allow RF posed a distinct disadvantage. The electrodes were converted to simple plates, following damage caused by halo currents during Tokamak plasma disruptions. The performance of these electrodes was assessed. Future developments in the JET GDC system are outlined. (Author)

  7. First demonstration and performance of an injection locked continuous wave magnetron to phase control a superconducting cavity

    Directory of Open Access Journals (Sweden)

    A. C. Dexter

    2011-03-01

    Full Text Available The applications of magnetrons to high power proton and cw electron linacs are discussed. An experiment is described where a 2.45 GHz magnetron has been used to drive a single cell superconducting cavity. With the magnetron injection locked, a modest phase control accuracy of 0.95° rms has been demonstrated. Factors limiting performance have been identified.

  8. Photoluminescence of Mg_2Si films fabricated by magnetron sputtering

    International Nuclear Information System (INIS)

    Liao, Yang-Fang; Xie, Quan; Xiao, Qing-Quan; Chen, Qian; Fan, Meng-Hui; Xie, Jing; Huang, Jin; Zhang, Jin-Min; Ma, Rui; Wang, Shan-Lan; Wu, Hong-Xian; Fang, Di

    2017-01-01

    Highlights: • High quality Mg_2Si films were grown on Si (111) and glass substrates with magnetron sputtering, respectively. • The first observation of Photoluminescence (PL) of Mg_2Si films was reported. • The Mg_2Si PL emission wavelengths are almost independence on temperature in the range of 77–300 K. • The strongest PL emissions may be attributed to interstitial Mg donor level to valence band transitions. • The activation energy of Mg_2Si is determined from the quenching of major luminescence peaks. - Abstract: To understand the photoluminescence mechanisms and optimize the design of Mg_2Si-based light-emitting devices, Mg_2Si films were fabricated on silicon (111) and glass substrates by magnetron sputtering technique, and the influences of different substrates on the photoelectric properties of Mg_2Si films were investigated systematically. The crystal structure, cross-sectional morphology, composition ratios and temperature-dependent photoluminescence (PL) of the Mg_2Si films were examined using X-ray diffraction (XRD), Scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDS) and PL measurement system, respectively. XRD results indicate that the Mg_2Si film on Si (111) displays polycrystalline structure, whereas Mg_2Si film on glass substrate is of like-monocrystalline structure.SEM results show that Mg_2Si film on glass substrate is very compact with a typical dense columnar structure, and the film on Si substrate represents slight delamination phenomenon. EDS results suggest that the stoichiometry of Mg and Si is approximately 2:1. Photoluminescence (PL) of Mg_2Si films was observed for the first time. The PL emission wavelengths of Mg_2Si are almost independence on temperature in the range of 77–300 K. The PL intensity decreases gradually with increasing temperature. The PL intensity of Mg_2Si films on glass substrate is much larger than that of Mg_2Si film on Si (111) substrate. The activation energy of 18 meV is

  9. Influence of the surface properties on bactericidal and fungicidal activity of magnetron sputtered Ti–Ag and Nb–Ag thin films

    Energy Technology Data Exchange (ETDEWEB)

    Wojcieszak, D., E-mail: damian.wojcieszak@pwr.edu.pl [Faculty of Microsystem Electronics and Photonics, Wroclaw University of Technology, Janiszewskiego 11/17, 50-372 Wrocław (Poland); Mazur, M.; Kaczmarek, D. [Faculty of Microsystem Electronics and Photonics, Wroclaw University of Technology, Janiszewskiego 11/17, 50-372 Wrocław (Poland); Mazur, P. [Institute of Experimental Physics, University of Wrocław, Max Born 9, 50-204 Wrocław (Poland); Szponar, B. [Institute of Immunology and Experimental Therapy, Polish Academy of Sciences, Rudolfa Weigla 12, 53–114 Wrocław (Poland); Domaradzki, J. [Faculty of Microsystem Electronics and Photonics, Wroclaw University of Technology, Janiszewskiego 11/17, 50-372 Wrocław (Poland); Kepinski, L. [Institute of Low Temperature and Structure Research, Polish Academy of Sciences, Okólna 2, 50-422 Wrocław (Poland)

    2016-05-01

    In this study the comparative investigations of structural, surface and bactericidal properties of Ti–Ag and Nb–Ag thin films have been carried out. Ti–Ag and Nb–Ag coatings were deposited on silicon and fused silica substrates by magnetron co-sputtering method using innovative multi-target apparatus. The physicochemical properties of prepared thin films were examined with the aid of X-ray diffraction, grazing incidence X-ray diffraction, scanning electron microscopy, atomic force microscopy and X-ray photoelectron spectroscopy methods. Moreover, the wettability of the surface was determined. It was found that both, Ti–Ag and Nb–Ag thin films were nanocrystalline. In the case of Ag–Ti film presence of AgTi{sub 3} and Ag phases was identified, while in the structure of Nb–Ag only silver occurred in a crystal form. In both cases the average size of crystallites was ca. 11 nm. Moreover, according to scanning electron microscopy and atomic force microscopy investigations the surface of Nb–Ag thin films was covered with Ag-agglomerates, while Ti–Ag surface was smooth and devoid of silver particles. Studies of biological activity of deposited coatings in contact with Bacillus subtilis, Pseudomonas aeruginosa, Enterococcus hirae, Klebisiella pneumoniae, Escherichia coli, Staphylococcus aureus and Candida albicans were performed. It was found that prepared coatings were bactericidal and fungicidal even in a short term-contact, i.e. after 2 h. - Highlights: • Surface and biological properties of Ti–Ag and Nb–Ag thin films were examined. • Ag content was related to sputtering yields and nucleation of Ti and Nb. • For Nb–Ag film the agglomeration of silver at the surface was observed. • Composition and surface topography had an impact on antimicrobial properties. • Fine-grained surface was important in Ag ions release process.

  10. Influence of the surface properties on bactericidal and fungicidal activity of magnetron sputtered Ti–Ag and Nb–Ag thin films

    International Nuclear Information System (INIS)

    Wojcieszak, D.; Mazur, M.; Kaczmarek, D.; Mazur, P.; Szponar, B.; Domaradzki, J.; Kepinski, L.

    2016-01-01

    In this study the comparative investigations of structural, surface and bactericidal properties of Ti–Ag and Nb–Ag thin films have been carried out. Ti–Ag and Nb–Ag coatings were deposited on silicon and fused silica substrates by magnetron co-sputtering method using innovative multi-target apparatus. The physicochemical properties of prepared thin films were examined with the aid of X-ray diffraction, grazing incidence X-ray diffraction, scanning electron microscopy, atomic force microscopy and X-ray photoelectron spectroscopy methods. Moreover, the wettability of the surface was determined. It was found that both, Ti–Ag and Nb–Ag thin films were nanocrystalline. In the case of Ag–Ti film presence of AgTi_3 and Ag phases was identified, while in the structure of Nb–Ag only silver occurred in a crystal form. In both cases the average size of crystallites was ca. 11 nm. Moreover, according to scanning electron microscopy and atomic force microscopy investigations the surface of Nb–Ag thin films was covered with Ag-agglomerates, while Ti–Ag surface was smooth and devoid of silver particles. Studies of biological activity of deposited coatings in contact with Bacillus subtilis, Pseudomonas aeruginosa, Enterococcus hirae, Klebisiella pneumoniae, Escherichia coli, Staphylococcus aureus and Candida albicans were performed. It was found that prepared coatings were bactericidal and fungicidal even in a short term-contact, i.e. after 2 h. - Highlights: • Surface and biological properties of Ti–Ag and Nb–Ag thin films were examined. • Ag content was related to sputtering yields and nucleation of Ti and Nb. • For Nb–Ag film the agglomeration of silver at the surface was observed. • Composition and surface topography had an impact on antimicrobial properties. • Fine-grained surface was important in Ag ions release process.

  11. Discharge Characteristic of VHF-DC Superimposed Magnetron Sputtering System

    Science.gov (United States)

    Toyoda, Hirotaka; Fukuoka, Yushi; Fukui, Takashi; Takada, Noriharu; Sasai, Kensuke

    2014-10-01

    Magnetron plasmas are one of the most important tools for sputter deposition of thin films. However, energetic particles from the sputtered target such as backscattered rare gas atoms or oxygen negative ions from oxide targets sometimes induce physical and chemical damages as well as surface roughening to the deposited film surface during the sputtering processes. To suppress kinetic energy of such particles, superposition of RF or VHF power to the DC power has been investigated. In this study, influence of the VHF power superposition on the DC target voltage, which is important factor to determine kinetic energy of high energy particles, is investigated. In the study, 40 MHz VHF power was superimposed to an ITO target and decrease in the target DC voltage was measured as well as deposited film deposition properties such as deposition rate or electrical conductivity. From systematic measurement of the target voltage, it was revealed that the target voltage can be determined by a very simple parameter, i.e., a ratio of VHF power to the total input power (DC and VHF powers) in spite of the DC discharge current. Part of this work was supported by ASTEP, JST.

  12. High power pulsed magnetron sputtering of transparent conducting oxides

    International Nuclear Information System (INIS)

    Sittinger, V.; Ruske, F.; Werner, W.; Jacobs, C.; Szyszka, B.; Christie, D.J.

    2008-01-01

    High power pulsed magnetron sputtering (HPPMS) has been used in order to study the deposition of transparent conducting oxides. We summarize the studies carried out on different materials (indium tin oxide-ITO and aluminium-doped zinc oxide-AZO) using rather different technological approaches, namely sputtering of ceramic targets and reactive sputtering. For the deposition of AZO reactive HPPMS for metallic targets has been used. A feedback control loop has been implemented in order to stabilize the discharge at any given setpoint on the hysteresis curve. The hysteresis was also found to have a rather untypical form. Reactive HPPMS was found to be a promising tool for obtaining high quality films of low total thickness. In the case of ITO deposition a ceramic target has been used. The process has been characterized in terms of its plasma emission and increasing indium ionization was found for higher peak power densities. The properties of the deposited films were compared to DC sputtered films. While for DC sputtering the choice of oxygen addition and shieldings is crucial for determining surface morphology and resistivity, in HPPMS sputtering peak power density has been found to be a good parameter for influencing the crystal structure. The morphologies obtained differ strongly from those seen in DC sputtering. At high power densities films with low surface roughness and excellent resistivity could be deposited without the use of shieldings

  13. Rhodium coated mirrors deposited by magnetron sputtering for fusion applications

    International Nuclear Information System (INIS)

    Marot, L.; De Temmerman, G.; Oelhafen, P.; Covarel, G.; Litnovsky, A.

    2007-01-01

    Metallic mirrors will be essential components of all optical spectroscopy and imaging systems for ITER plasma diagnostics. Any change in the mirror performance, in particular, its reflectivity, due to erosion of the surface by charge exchange neutrals or deposition of impurities will influence the quality and reliability of the detected signals. Due to its high reflectivity in the visible wavelength range and its low sputtering yield, rhodium appears as an attractive material for first mirrors in ITER. However, the very high price of the raw material calls for using it in the form of a film deposited onto metallic substrates. The development of a reliable technique for the preparation of high reflectivity rhodium films is therefore of the highest importance. Rhodium layers with thicknesses of up to 2 μm were produced on different substrates of interest (Mo, stainless steel, Cu) by magnetron sputtering. Produced films exhibit a low roughness and crystallite size of about 10 nm with a dense columnar structure. No impurities were detected on the surface after deposition. Scratch tests demonstrate that adhesion properties increase with substrate hardness. Detailed optical characterizations of Rh-coated mirrors as well as results of erosion tests performed both under laboratory conditions and in the TEXTOR tokamak are presented in this paper

  14. DC Magnetron Sputtered IZTO Thin Films for Organic Photovoltaic Application.

    Science.gov (United States)

    Lee, Hye Ji; Noviyana, Imas; Putri, Maryane; Koo, Chang Young; Lee, Jung-A; Kim, Jeong-Joo; Jeong, Youngjun; Lee, Youngu; Lee, Hee Young

    2018-02-01

    IZTO20 (In0.6Zn0.2Sn0.2O1.5) ceramic target was prepared from oxide mixture of In2O3, ZnO, and SnO2 powders. IZTO20 thin films were then deposited onto glass substrate at 400 °C by DC magnetron sputtering. The average optical transmittance determined by ultraviolet-visible spectroscopy was higher than 85% for all films. The minimum resistivity of the annealed IZTO20 thin film was approximately 6.1×10-4 Ω·cm, which tended to increase with decreasing indium content. Substrate heating and annealing were found to be important parameters affecting the electrical and optical properties. An organic photovoltaic (OPV) cell was fabricated using the IZTO20 film deposited under the optimized condition as an anode electrode and the efficiency of up to 80% compared to that of a similar OPV cell using ITO film was observed. Reduction of surface roughness and electrical resistivity through annealing treatment was found to contribute to the improved efficiency of the OPV cell.

  15. Textured ZnO thin films by RF magnetron sputtering

    CERN Document Server

    Ginting, M; Kang, K H; Kim, S K; Yoon, K H; Park, I J; Song, J S

    1999-01-01

    Textured thin films ZnO has been successfully grown by rf magnetron sputtering method using a special technique of introducing a small amount of water and methanol on the deposition chamber. The grain size of the textured surface is highly dependent on the argon pressure during the deposition. The pressure in this experiment was varied from 50 mTorr down to 5 mTorr and the highest grain size of the film is obtained at 5 mTorr. The total transmittance of the films are more than 85% in the wavelength of 400 to 800 nm, and haze ratio of about 14% is obtained at 400 nm wavelength. Beside the textured surface, these films also have very low resistivity, which is lower than 1.4x10 sup - sup 3 OMEGA centre dot cm. X-ray analysis shows that the films with textured surface have four diffraction peaks on the direction of (110), (002), (101) and (112), while the non-textured films have only (110) and (002) peaks. Due to the excellent characteristics of this film, it will make the film very good TCO alternatives for the ...

  16. Mechanical properties of nanocrystalline palladium prepared by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Castrup, Anna; Hahn, Horst [Forschungszentrum Karlsruhe (Germany); Technical University of Darmstadt (Germany); Scherer, Torsten; Ivanisenko, Yulia; Choi, In-Suk; Kraft, Oliver [Forschungszentrum Karlsruhe (Germany)

    2009-07-01

    Nanocrystalline metals and alloys with grain sizes well below 100 nm often demonstrate unique deformation behaviour and therefore attract a great interest in material science. The understanding of deformation mechanisms operating in nanocrystalline materials is important to predict their mechanical properties. In the present study Pd films of 1{mu}m thickness were prepared using UHV rf magnetron sputtering on dog bone shaped Kapton substrates and on Si/SiO2 wafers. The films were sputtered using multilayer technology with an individual layer thickness of 10 nm. This resulted in grain sizes of about 20 nm. Initial microstructure and texture were characterized using conventional XRD measurements and transmission electron microscopy (TEM) in both cross section- and plane view. The mechanical properties were investigated using tensile testing and nanoindentation at several strain rates. An increased hardness and strength as compared to coarse grained Pd was observed, as well as high strain rate sensitivity. The microstructure in the gauge section after tensile testing was again analyzed using TEM in order to reveal signatures of deformation mechanisms like dislocation motion or twinning.

  17. Multilayer DLC coatings via alternating bias during magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Li Fengji [School of Mechanical and Aerospace Engineering, Nanyang Technological University (Singapore); Zhang, Sam, E-mail: msyzhang@ntu.edu.sg [School of Mechanical and Aerospace Engineering, Nanyang Technological University (Singapore); Kong Junhua [School of Materials Science and Engineering, Nanyang Technological University (Singapore); Zhang Yujuan [Key Laboratory of Special Functional Material, Henan University (China); Zhang Wali [School of Mechanical and Aerospace Engineering, Nanyang Technological University (Singapore)

    2011-05-31

    To combat the high residual stress problem in monolayer diamond-like carbon coatings, this paper fabricated multilayer diamond-like carbon coatings with alternate soft and hard layers via alternating bias during magnetron sputtering. The surface, cross sectional morphology, bonding structures and mechanical properties are investigated. The atomic force microscopy images indicate low bias results in rougher surface with large graphite clusters and voids suggesting low coating density. The multilayered coatings demonstrate relatively smooth surface stemming from higher bias. The cross sectional images from field emission scanning electron microscopy indicate coating thickness decreases as substrate bias increases and confirm that higher bias results in denser coating. Delamination is observed in monolayer coatings due to high residual stress. The trend of sp{sup 3}/sp{sup 2} fraction estimated by X-ray photoelectron spectroscopy is consistent with that of I{sub D}/I{sub G} ratios from Raman spectra, indicating the change of bonding structure with change of substrate bias. Hardness of multilayer diamond-like carbon coating is comparable to the coatings deposited at low constant bias but the adhesion strength and toughness are significantly improved. Alternately biased sputtering deposition provides an alternative when combination of hardness, toughness and adhesion strength is needed in an all diamond-like carbon coating.

  18. Functional nanostructured titanium nitride films obtained by sputtering magnetron

    International Nuclear Information System (INIS)

    Sanchez, O.; Hernandez-Velez, M.; Navas, D.; Auger, M.A.; Baldonedo, J.L.; Sanz, R.; Pirota, K.R.; Vazquez, M.

    2006-01-01

    Development of new methods in the formation of hollow structures, in particular, nanotubes and nanocages are currently generating a great interest as a consequence of the growing relevance of these nanostructures on many technological fields, ranging from optoelectronics to biotechnology. In this work, we report the formation of titanium nitride (TiN) nanotubes and nanohills via reactive sputtering magnetron processes. Anodic Alumina Membranes (AAM) were used as template substrates to grow the TiN nanostructures. The AAM were obtained through electrochemical anodization processes by using oxalic acid solutions as electrolytes. The nanotubes were produced at temperatures below 100 deg. C, and using a pure titanium (99.995%) sputtering target and nitrogen as reactive gas. The obtained TiN thin films showed surface morphologies adjusted to pore diameter and interpore distance of the substrates, as well as ordered arrays of nanotubes or nanohills depending on the sputtering and template conditions. High Resolution Scanning Electron Microscopy (HRSEM) was used to elucidate both the surface order and morphology of the different grown nanostructures. The crystalline structure of the samples was examined using X-ray Diffraction (XRD) patterns and their qualitative chemical composition by using X-ray Energy Dispersive Spectroscopy (XEDS) in a scanning electron microscopy

  19. Spokes and charged particle transport in HiPIMS magnetrons

    International Nuclear Information System (INIS)

    Brenning, N; Lundin, D; Minea, T; Vitelaru, C; Costin, C

    2013-01-01

    Two separate scientific communities are shown to have studied one common phenomenon, azimuthally rotating dense plasma structures, also called spokes, in pulsed-power E × B discharges, starting from quite different approaches. The first body of work is motivated by fundamental plasma science and concerns a phenomenon called the critical ionization velocity, CIV, while the other body of work is motivated by the applied plasma science of high power impulse magnetron sputtering (HiPIMS). Here we make use of this situation by applying experimental observations, and theoretical analysis, from the CIV literature to HiPIMS discharges. For a practical example, we take data from observed spokes in HiPIMS discharges and focus on their role in charged particle transport, and in electron energization. We also touch upon the closely related questions of how they channel the cross-B discharge current, how they maintain their internal potential structure and how they influence the energy spectrum of the ions? New particle-in-cell Monte Carlo collisional simulations that shed light on the azimuthal drift and expansion of the spokes are also presented. (paper)

  20. Algan/Gan Hemt By Magnetron Sputtering System

    Science.gov (United States)

    Garcia Perez, Roman

    In this thesis, the growth of the semiconductor materials AlGaN and GaN is achieved by magnetron sputtering for the fabrication of High Electron Mobility Transistors (HEMTs). The study of the deposited nitrides is conducted by spectroscopy, diffraction, and submicron scale microscope methods. The preparation of the materials is performed using different parameters in terms of power, pressure, temperature, gas, and time. Silicon (Si) and Sapphire (Al2O3) wafers are used as substrates. The chemical composition and surface topography of the samples are analyzed to calculate the materials atomic percentages and to observe the devices surface. The instruments used for the semiconductors characterization are X-ray Photoelectron Spectroscopy (XPS), X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM), and Atomic Force Microscope (AFM). The project focused its attention on the reduction of impurities during the deposition, the controlled thicknesses of the thin-films, the atomic configuration of the alloy AlxGa1-xN, and the uniformity of the surfaces.

  1. Superconducting niobium nitride films deposited by unbalanced magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Olaya, J.J. [Departamento de Ingenieria Mecanica y Mecatronica, Universidad Nacional de Colombia, Ciudad Universitaria, Carrera 30 Numero 45-03, Bogota (Colombia); Huerta, L. [Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de Mexico, Circuito exterior s/n, CU Coyoacan, Mexico D.F. 04510 (Mexico); Rodil, S.E. [Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de Mexico, Circuito exterior s/n, CU Coyoacan, Mexico D.F. 04510 (Mexico)], E-mail: ser42@iim.unam.mx; Escamilla, R. [Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de Mexico, Circuito exterior s/n, CU Coyoacan, Mexico D.F. 04510 (Mexico)

    2008-10-01

    Niobium nitride (NbN) thin films were deposited under different configurations of the magnetic field using a magnetron sputtering system. The magnetic field configuration varied from balanced to unbalanced leading to different growth conditions and film properties. The aim of the paper was to identify correlations between deposition conditions, film properties and the electrical properties, specially the superconductive critical temperature (T{sub C}). The results suggested that there is a critical deposition condition, having an optimum ion-atom arrival ratio that promotes a well ordered and textured nanocrystalline structure (cubic phase) with the minimum residual stress and only under this condition a high critical temperature (16K) was obtained. Lower T{sub C} values around 12K were obtained for the NbN samples having a lower degree of structural perfection and texture, and a larger fraction of intergranular voids. On the other hand, analysis of valence-band spectra showed that the contribution of the Nb 4d states remained essentially constant while the higher T{sub C} was correlated to a higher contribution of the N 2p states.

  2. Superconducting niobium nitride films deposited by unbalanced magnetron sputtering

    International Nuclear Information System (INIS)

    Olaya, J.J.; Huerta, L.; Rodil, S.E.; Escamilla, R.

    2008-01-01

    Niobium nitride (NbN) thin films were deposited under different configurations of the magnetic field using a magnetron sputtering system. The magnetic field configuration varied from balanced to unbalanced leading to different growth conditions and film properties. The aim of the paper was to identify correlations between deposition conditions, film properties and the electrical properties, specially the superconductive critical temperature (T C ). The results suggested that there is a critical deposition condition, having an optimum ion-atom arrival ratio that promotes a well ordered and textured nanocrystalline structure (cubic phase) with the minimum residual stress and only under this condition a high critical temperature (16K) was obtained. Lower T C values around 12K were obtained for the NbN samples having a lower degree of structural perfection and texture, and a larger fraction of intergranular voids. On the other hand, analysis of valence-band spectra showed that the contribution of the Nb 4d states remained essentially constant while the higher T C was correlated to a higher contribution of the N 2p states

  3. Properties of tungsten films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Ahn, K.Y.; Ting, C.Y.; Brodsky, S.B.; Fryer, P.M.; Davari, B.; Angillelo, J.; Herd, S.R.; Licata, T.

    1986-01-01

    High-rate magnetron sputtering is a relatively simple process to produce tungsten films with good electrical and mechanical properties, and it offers good uniformity, reproducibility, process flexibility, and high throughput. The purity of the sputtered films is affected by the target purity (cold-pressed 99.95%, chemical vapor deposited 99.99% and cast 99.999%), base pressure, deposition rate, and substrate bias. Typical resistivity in films of 2000 to 3000A thickness deposited on Si, poly-Si, and SiO/sub 2/ ranges from 10 to 12 μΩ-cm, and this may be compared with 6 and 11 μΩ-cm by high-temperature evaporation and chemical vapor deposition, respectively. The presence of biaxial stress caused by substrate scanning was determined by x-ray technique. The sputtered films exhibit high compressive stress when deposited at low Ar pressure. It decreases with increasing pressure, and eventually changes sign to become tensile, and increases further with increasing pressure. Effects of processing parameters on films properties, and a comparison of film properties prepared by evaporation and chemical vapor deposition are discussed

  4. A Study of volumetric modulated arc therapy for stereotactic body radiation therapy in case of multi-target liver cancer using flattening filter free beam

    International Nuclear Information System (INIS)

    Yeom, Mi Sook; Yoon, In Ha; Hong, Dong Gi; Back, Geum Mun

    2015-01-01

    Stereotactic body radiation therapy (SBRT) has proved its efficacy in several patient populations with primary and metastatic limited tumors. Because SBRT prescription is high dose level than Conventional radiation therapy. SBRT plan is necessary for effective Organ at risk (OAR) protection and sufficient Planning target volume (PTV) dose coverage. In particular, multi-target cases may result excessive doses to OAR and hot spot due to dose overlap. This study evaluate usefulness of Volumetric modulated arc therapy (VMAT) in dosimetric and technical considerations using Flattening filter free (FFF) beam. The treatment plans for five patients, being treated on TrueBeam STx(Varian™, USA) with VMAT using 10MV FFF beam and Standard conformal radiotherapy (CRT) using 15MV Flattening filter (FF) beam. PTV, liver, duodenum, bowel, spinal cord, esophagus, stomach dose were evaluated using the dose volume histogram(DVH). Conformity index(CI), homogeneity index(HI), Paddick's index(PCI) for the PTV was assessed. Total Monitor unit (MU) and beam on time was assessed. Average value of CI, HI and PCI for PTV was 1.381±0.028, 1.096±0.016, 0.944±0.473 in VMAT and 1.381± 0.042, 1.136±0.042, 1.534±0.465 in CRT respectively. OAR dose in CRT plans evaluated 1.8 times higher than VMAT. Total MU in VMAT evaluated 1.3 times increase than CRT. Average beam on time was 6.8 minute in VMAT and 21.3 minute in CRT respectively. OAR dose in CRT plans evaluated 1.8 times higher than VMAT. Total MU in VMAT evaluated 1.3 times increase than CRT. Average beam on time was 6.8 minute in VMAT and 21.3 minute in CRT. VMAT for SBRT in multi-target liver cancer using FFF beam is effective treatment techniqe in dosimetric and technical considerations. VMAT decrease intra-fraction error due to treatment time shortening using high dose rate of FFF beam

  5. A Study of volumetric modulated arc therapy for stereotactic body radiation therapy in case of multi-target liver cancer using flattening filter free beam

    Energy Technology Data Exchange (ETDEWEB)

    Yeom, Mi Sook; Yoon, In Ha; Hong, Dong Gi; Back, Geum Mun [Dept. of Radiation Oncology, ASAN Medical Center, Seoul (Korea, Republic of)

    2015-06-15

    Stereotactic body radiation therapy (SBRT) has proved its efficacy in several patient populations with primary and metastatic limited tumors. Because SBRT prescription is high dose level than Conventional radiation therapy. SBRT plan is necessary for effective Organ at risk (OAR) protection and sufficient Planning target volume (PTV) dose coverage. In particular, multi-target cases may result excessive doses to OAR and hot spot due to dose overlap. This study evaluate usefulness of Volumetric modulated arc therapy (VMAT) in dosimetric and technical considerations using Flattening filter free (FFF) beam. The treatment plans for five patients, being treated on TrueBeam STx(Varian™, USA) with VMAT using 10MV FFF beam and Standard conformal radiotherapy (CRT) using 15MV Flattening filter (FF) beam. PTV, liver, duodenum, bowel, spinal cord, esophagus, stomach dose were evaluated using the dose volume histogram(DVH). Conformity index(CI), homogeneity index(HI), Paddick's index(PCI) for the PTV was assessed. Total Monitor unit (MU) and beam on time was assessed. Average value of CI, HI and PCI for PTV was 1.381±0.028, 1.096±0.016, 0.944±0.473 in VMAT and 1.381± 0.042, 1.136±0.042, 1.534±0.465 in CRT respectively. OAR dose in CRT plans evaluated 1.8 times higher than VMAT. Total MU in VMAT evaluated 1.3 times increase than CRT. Average beam on time was 6.8 minute in VMAT and 21.3 minute in CRT respectively. OAR dose in CRT plans evaluated 1.8 times higher than VMAT. Total MU in VMAT evaluated 1.3 times increase than CRT. Average beam on time was 6.8 minute in VMAT and 21.3 minute in CRT. VMAT for SBRT in multi-target liver cancer using FFF beam is effective treatment techniqe in dosimetric and technical considerations. VMAT decrease intra-fraction error due to treatment time shortening using high dose rate of FFF beam.

  6. Multi-target retrieval (MTR): the simultaneous retrieval of pressure, temperature and volume mixing ratio profiles from limb-scanning atmospheric measurements

    International Nuclear Information System (INIS)

    Dinelli, B.M.; Alpaslan, D.; Carlotti, M.; Magnani, L.; Ridolfi, M.

    2004-01-01

    In this paper we describe a retrieval approach for the simultaneous determination of the altitude distributions of p, T and VMR of atmospheric constituents from limb-scanning measurements of the atmosphere. This analysis method, named multi-target retrieval (MTR), has been designed and implemented in a computer code aimed at the analysis of MIPAS-ENVISAT observations; however, the concepts implemented in MTR have a general validity and can be extended to the analysis of all type of limb-scanning observations. In order to assess performance and advantages of the proposed approach, MTR has been compared with the sequential analysis system implemented by ESA as the level-2 processor for MIPAS measurements. The comparison has been performed on a common set of target species and spectral intervals. The performed tests have shown that MTR produces results of better quality than a sequential retrieval. However, the simultaneous retrieval of p, T and water VMR has not lead to satisfactory results below the tropopause, because of the high correlation occurring between p and water VMR in the troposphere. We have shown that this problem can be fixed extending the MTR analysis to at least one further target whose spectral features decouple the retrieval of pressure and water VMR. Ozone was found to be a suitable target for this purpose. The advantages of the MTR analysis system in terms of systematic errors have also been discussed

  7. Multi-target determination of organic ultraviolet absorbents in organism tissues by ultrasonic assisted extraction and ultra-high performance liquid chromatography-tandem mass spectrometry.

    Science.gov (United States)

    Peng, Xianzhi; Jin, Jiabin; Wang, Chunwei; Ou, Weihui; Tang, Caiming

    2015-03-06

    A sensitive and reliable method was developed for multi-target determination of 13 most widely used organic ultraviolet (UV) absorbents (including UV filters and UV stabilizers) in aquatic organism tissues. The organic UV absorbents were extracted using ultrasonic-assisted extraction, purified via gel permeation chromatography coupled with silica gel column chromatography, and determined by ultra-high performance liquid chromatography-tandem mass spectrometry. Recoveries of the UV absorbents from organism tissues mostly ranged from 70% to 120% from fish filet with satisfactory reproducibility. Method quantification limits were 0.003-1.0ngg(-1) dry weight (dw) except for 2-ethylhexyl 4-methoxycinnamate. This method has been applied to analysis of the UV absorbents in wild and farmed aquatic organisms collected from the Pearl River Estuary, South China. 2-Hydroxy-4-methoxybenzophenone and UV-P were frequently detected in both wild and farmed marine organisms at low ngg(-1)dw. 3-(4-Methylbenzylidene)camphor and most of the benzotriazole UV stabilizers were also frequently detected in maricultured fish. Octocrylene and 2-ethylhexyl 4-methoxycinnamate were not detected in any sample. This work lays basis for in-depth study about bioaccumulation and biomagnification of the UV absorbents in marine environment. Copyright © 2015 Elsevier B.V. All rights reserved.

  8. Novel multi-targeted agents for Alzheimer's disease: Synthesis, biological evaluation, and molecular modeling of novel 2-[4-(4-substitutedpiperazin-1-yl)phenyl]benzimidazoles.

    Science.gov (United States)

    Ozadali-Sari, Keriman; Tüylü Küçükkılınç, Tuba; Ayazgok, Beyza; Balkan, Ayla; Unsal-Tan, Oya

    2017-06-01

    The present study describes the synthesis, pharmacological evaluation (BChE/AChE inhibition, Aβ antiaggregation, and neuroprotective effects), and molecular modeling studies of novel 2-[4-(4-substitutedpiperazin-1-yl)phenyl]benzimidazole derivatives. The alkyl-substituted derivatives exhibited selective inhibition on BChE with varying efficiency. Compounds 3b and 3d were found to be the most potent inhibitors of BChE with IC 50 values of 5.18 and 5.22μM, respectively. The kinetic studies revealed that 3b is a partial non-competitive BChE inhibitor. Molecular modeling studies also showed that the alkyl-substituted derivatives were able to reach the catalytic anionic site of the BChE. The compounds with an inhibitory effect on BChE were subsequently screened for their Aβ antiaggregating and neuroprotective activities. Compounds 3a and 3b exerted a potential neuroprotective effect against H 2 O 2 and Aβ-induced cytotoxicity in SH-SY5Y cells. Collectively, 3b was found as the most promising compound for the development of multi-target directed ligands against Alzheimer's disease. Copyright © 2017 Elsevier Inc. All rights reserved.

  9. Setup for in situ X-ray diffraction studies of thin film growth by magnetron sputtering

    CERN Document Server

    Ellmer, K; Weiss, V; Rossner, H

    2001-01-01

    A novel method is described for the in situ-investigation of nucleation and growth of thin films during magnetron sputtering. Energy dispersive X-ray diffraction with synchrotron light is used for the structural analysis during film growth. An in situ-magnetron sputtering chamber was constructed and installed at a synchrotron radiation beam line with a bending magnet. The white synchrotron light (1-70 keV) passes the sputtering chamber through Kapton windows and hits one of the substrates on a four-fold sample holder. The diffracted beam, observed under a fixed diffraction angle between 3 deg. and 10 deg., is energy analyzed by a high purity Ge-detector. The in situ-EDXRD setup is demonstrated for the growth of tin-doped indium oxide (ITO) films prepared by reactive magnetron sputtering from a metallic target.

  10. Solid-state pulse modulator for a 1.7-MW X-band magnetron

    International Nuclear Information System (INIS)

    Choi, Jaegu; Shin, Yongmoon; Choi, Youngwook; Kim, Kwanho

    2014-01-01

    Medical linear accelerators (LINAC) for cancer treatment require pulse modulators to generate high-power pulses with a fast rise time, flat top and short duration to drive high-power magnetrons. Solid-state pulse modulators (SSPM) for medical LINACs that use high power semiconductor switches with high repetition rates, high stability and long lifetimes have been introduced to replace conventional linear-type pulse generators that use gaseous discharge switches. In this paper, the performance of a developed SSPM, which mainly consists of a capacitor charger, an insulated-gate bipolar transistor (IGBT) - capacitor stack and a pulse transformer, is evaluated with a dummy load and an X-band magnetron load. A theoretical analysis of the pulse transformer, which is a critical element of the SSPM, is carried out. The output pulse has a fast rise time and low droop, such that the modulator can drive the X-band magnetron.

  11. Improved Magnetron Stability and Reduced Noise in Efficient Transmitters for Superconducting Accelerators

    Energy Technology Data Exchange (ETDEWEB)

    Kazakevich, G. [MUONS Inc., Batavia; Johnson, R. [MUONS Inc., Batavia; Lebedev, V. [Fermilab; Yakovlev, V. [Fermilab

    2018-04-01

    State of the art high-current superconducting accelerators require efficient RF sources with a fast dynamic phase and power control. This allows for compensation of the phase and amplitude deviations of the accelerating voltage in the Superconducting RF (SRF) cavities caused by microphonics, etc. Efficient magnetron transmitters with fast phase and power control are attractive RF sources for this application. They are more cost effective than traditional RF sources such as klystrons, IOTs and solid-state amplifiers used with large scale accelerator projects. However, unlike traditional RF sources, controlled magnetrons operate as forced oscillators. Study of the impact of the controlling signal on magnetron stability, noise and efficiency is therefore important. This paper discusses experiments with 2.45 GHz, 1 kW tubes and verifies our analytical model which is based on the charge drift approximation.

  12. Computer simulation of sputtering of graphite target in magnetron sputtering device with two zones of erosion

    Directory of Open Access Journals (Sweden)

    Bogdanov R.V.

    2015-03-01

    Full Text Available A computer simulation program for discharge in a magnetron sputtering device with two erosion zones was developed. Basic laws of the graphite target sputtering process and transport of sputtered material to the substrate were taken into account in the Monte Carlo code. The results of computer simulation for radial distributions of density and energy flux of carbon atoms on the substrate (at different values of discharge current and pressure of the working gas confirmed the possibility of obtaining qualitative homogeneous films using this magnetron sputtering device. Also the discharge modes were determined for this magnetron sputtering device, in which it was possible to obtain such energy and density of carbon atoms fluxes, which were suitable for deposition of carbon films containing carbon nanotubes and other nanoparticles.

  13. Commissioning of indigenous microwave test facility for development and pilot production of 2 MW S-band magnetrons

    International Nuclear Information System (INIS)

    Shrivastava, Purushottam; Wanmode, Y.D.; Hannurkar, P.R.; Prasad, Sharda

    2005-01-01

    To have self reliance in the field of microwave devices and to have consistent supply of pulsed magnetrons for the Indian accelerator programme. CAT initiated development of 2 MW S-Band pulsed magnetrons in collaboration with CEERI, Pilani. The design, development and testing of the microwave test facilities for ageing. conditioning and performance testing of Indian magnetrons, was successfully done by CAT indigenously. After the rigorous testing. the test facility was shifted, installed and commissioned at CEERI, Pilani by CAT. Over a period of 10 years, nine prototypes were aged and tested, two magnetrons were life tested and five magnetrons under production programme have been successfully conditioned and tested. Testing of more numbers is underway. The system details. commissioning aspects are discussed, results are shown. (author)

  14. Arc-discharge and magnetron sputtering combined equipment for nanocomposite coating deposition

    International Nuclear Information System (INIS)

    Koval, N.N.; Borisov, D.P.; Savostikov, V.M.

    2005-01-01

    It is known that characteristics of nanocomposite coatings produced by reactive magnetron sputtering undergo an essential influence on the following parameters such as original component composition of targets being sputtered, as well as abundance ratio of such components in the coatings deposited, relative content of inert and reactionary gases in a gas mixture used and a value of operating pressure in a chamber, substrate temperature, and a value of substrate bias potential, determining energy of ionized atoms, ionized atoms flow density, i.e. ion current density on a substrate. The multifactor character of production process of nanocomposite coatings with certain physical and mechanical properties demands a purposeful and complex control on all above-mentioned parameters. To solve such a problem, an arc-discharge and magnetron sputtering combined equipment including a vacuum chamber of approximately ∼ 0.5 m 3 with a built-in low-pressure plasma generator made on the basis of non-self-sustained discharge with a thermal cathode and a planar magnetron combined with two sputtered targets has been created. Construction of such a complex set-up provides both an autonomous mode of operation and simultaneous operation of an arc plasma generator and magnetron sputtering system. Magnetron sputtering of either one or two targets simultaneously is provided as well. An arc plasma generator enables ions current density control on a substrate in a wide range due to discharge current varying from 1 to 100 A. Energy of ions is also being controlled in a wide range by a negative bias potential from 0 to 1000 V applied to a substrate. The wide control range of gas plasma density of a arc discharge of approximately 10 9 -10 11 cm -3 and high uniformity of its distribution over the total volume of an operating chamber (about 15% error with regard to the mean value) provides a purposeful and simultaneous control either of magnetron discharge characteristics (operating pressure of

  15. SERS spectra of pyridine adsorbed on nickel film prepared by magnetron sputtering

    Science.gov (United States)

    Li, Daoyong; Ouyang, Yu; Chen, Li; Cao, Weiran; Shi, Shaohua

    2011-02-01

    As a repeating well and cheaper enhancement substrate, the nickel film was fabricated with magnetron sputtering coating instrument. Surface enhanced Raman spectra (SERS) of pyridine adsorbed on this nickel film are compared with the experimental values of gaseous pyridine, the theoretical value of pyridine solution listed in other literatures and our method is better than electro-chemical etching electrode method for large scale preparation. The enhancement factor of the nickel film is calculated and the result indicates that magnetron sputtering coating technology is feasible for obtaining good SERS active surface.

  16. Computer analysis, design and construction of the BNL Mk V magnetron

    International Nuclear Information System (INIS)

    McKenzie-Wilson, R.B.; Kovarik, V.J.

    1981-01-01

    As part of a program to develop a high energy neutral beam injector for fusion reactor applications, the BNL Neutral Beam Group is studying, among other options, a surface plasma source of the magnetron type. This source has been developed to the point at which a large compact model, known as the Mk V magnetron, has been designed and constructed. The source is designed to operate in the steady state mode and to produce 1-2A of H - (D - ) ions at 25 kV. Under these conditions, 18 KW of heat are removed from the source by the cooling system

  17. Increase in the accuracy of approximating the profile of the erosion zone in planar magnetrons

    Science.gov (United States)

    Rogov, A. V.; Kapustin, Yu. V.

    2017-09-01

    It has been shown that the use of the survival function of the Weibull distribution shifted along the ordinate axis allows one to increase the accuracy of the approximation of the normalized profile of an erosion zone in the area from the axis to the maximum sputtering region compared with the previously suggested distribution function of the extremum values. The survival function of the Weibull distribution is used in the area from the maximum to the outer boundary of an erosion zone. The major advantage of using the new approximation is observed for magnetrons with a large central nonsputtered spot and for magnetrons with substantial sputtering in the paraxial zone.

  18. Pro-neurogenic, Memory-Enhancing and Anti-stress Effects of DF302, a Novel Fluorine Gamma-Carboline Derivative with Multi-target Mechanism of Action.

    Science.gov (United States)

    Strekalova, Tatyana; Bahzenova, Nataliia; Trofimov, Alexander; Schmitt-Böhrer, Angelika G; Markova, Nataliia; Grigoriev, Vladimir; Zamoyski, Vladimir; Serkova, Tatiana; Redkozubova, Olga; Vinogradova, Daria; Umriukhin, Alexei; Fisenko, Vladimir; Lillesaar, Christina; Shevtsova, Elena; Sokolov, Vladimir; Aksinenko, Alexey; Lesch, Klaus-Peter; Bachurin, Sergey

    2018-01-01

    A comparative study performed in mice investigating the action of DF302, a novel fluoride-containing gamma-carboline derivative, in comparison to the structurally similar neuroprotective drug dimebon. Drug effects on learning and memory, emotionality, hippocampal neurogenesis and mitochondrial functions, as well as AMPA-mediated currents and the 5-HT6 receptor are reported. In the step-down avoidance and fear-conditioning paradigms, bolus administration of drugs at doses of 10 or 40 mg/kg showed that only the higher dose of DF302 improved long-term memory while dimebon was ineffective at either dosage. Short-term memory and fear extinction remained unaltered across treatment groups. During the 5-day predation stress paradigm, oral drug treatment over a period of 2 weeks at the higher dosage regimen decreased anxiety-like behaviour. Both compounds supressed inter-male aggression in CD1 mice, the most eminent being the effects of DF302 in its highest dose. DF302 at the higher dose decreased floating behaviour in a 2-day swim test and after 21-day ultrasound stress. The density of Ki67-positive cells, a marker of adult neurogenesis, was reduced in the dentate gyrus of stressed dimebon-treated and non-treated mice, but not in DF302-treated mice. Non-stressed mice that received DF302 had a higher density of Ki67-positive cells than controls unlike dimebon-treated mice. Similar to dimebon, DF302 effectively potentiated AMPA receptor-mediated currents, bound to the 5-HT6 receptor, inhibited mitochondrial permeability transition and displayed cytoprotective properties in cellular models of neurodegeneration. Thus, DF302 exerts multi-target effects on the key mechanisms of neurodegenerative pathologies and can be considered as an optimized novel analogue of the neuroprotective agent dimebon.

  19. High-throughput screening for various classes of doping agents using a new 'dilute-and-shoot' liquid chromatography-tandem mass spectrometry multi-target approach.

    Science.gov (United States)

    Guddat, S; Solymos, E; Orlovius, A; Thomas, A; Sigmund, G; Geyer, H; Thevis, M; Schänzer, W

    2011-01-01

    A new multi-target approach based on liquid chromatography--electrospray ionization tandem mass spectrometry (LC-(ESI)-MS/MS) is presented to screen for various classes of prohibited substances using direct injection of urine specimens. With a highly sensitive new generation hybrid mass spectrometer classic groups of drugs--for example, diuretics, beta2-agonists--stimulants and narcotics are detectable at concentration levels far below the required limits. Additionally, more challenging and various new target compounds could be implemented. Model compounds of stimulant conjugates were studied to investigate a possible screening without complex sample preparation. As a main achievement, the integration of the plasma volume expanders dextran and hydroxyethyl starch (HES), commonly analyzed in time-consuming, stand-alone procedures, is accomplished. To screen for relatively new prohibited compounds, a common metabolite of the selective androgen receptor modulator (SARMs) andarine, a metabolite of growth hormone releasing peptide (GHRP-2), and 5-amino-4-imidazolecarboxyamide ribonucleoside (AICAR) are analyzed. Following a completely new approach, conjugates of di(2-ethylhexyl) phthalate (DEHP) metabolites are monitored to detect abnormally high levels of plasticizers indicating for illicit blood transfusion. The assay was fully validated for qualitative purposes considering the parameters specificity, intra- (3.2-16.6%) and inter-day precision (0.4-19.9%) at low, medium and high concentration, robustness, limit of detection (1-70 ng/ml, dextran: 30 µg/ml, HES: 10 µg/ml) and ion suppression/enhancement effects. The analyses of post-administration and routine doping control samples demonstrates the applicability of the method for sports drug testing. This straightforward and reliable approach accomplishes the combination of different screening procedures resulting in a high-throughput method that increases the efficiency of the labs daily work. Copyright © 2011 John

  20. [Multi-Target Recognition of Internal and External Defects of Potato by Semi-Transmission Hyperspectral Imaging and Manifold Learning Algorithm].

    Science.gov (United States)

    Huang, Tao; Li, Xiao-yu; Jin, Rui; Ku, Jing; Xu, Sen-miao; Xu, Meng-ling; Wu, Zhen-zhong; Kong, De-guo

    2015-04-01

    The present paper put forward a non-destructive detection method which combines semi-transmission hyperspectral imaging technology with manifold learning dimension reduction algorithm and least squares support vector machine (LSSVM) to recognize internal and external defects in potatoes simultaneously. Three hundred fifteen potatoes were bought in farmers market as research object, and semi-transmission hyperspectral image acquisition system was constructed to acquire the hyperspectral images of normal external defects (bud and green rind) and internal defect (hollow heart) potatoes. In order to conform to the actual production, defect part is randomly put right, side and back to the acquisition probe when the hyperspectral images of external defects potatoes are acquired. The average spectrums (390-1,040 nm) were extracted from the region of interests for spectral preprocessing. Then three kinds of manifold learning algorithm were respectively utilized to reduce the dimension of spectrum data, including supervised locally linear embedding (SLLE), locally linear embedding (LLE) and isometric mapping (ISOMAP), the low-dimensional data gotten by manifold learning algorithms is used as model input, Error Correcting Output Code (ECOC) and LSSVM were combined to develop the multi-target classification model. By comparing and analyzing results of the three models, we concluded that SLLE is the optimal manifold learning dimension reduction algorithm, and the SLLE-LSSVM model is determined to get the best recognition rate for recognizing internal and external defects potatoes. For test set data, the single recognition rate of normal, bud, green rind and hollow heart potato reached 96.83%, 86.96%, 86.96% and 95% respectively, and he hybrid recognition rate was 93.02%. The results indicate that combining the semi-transmission hyperspectral imaging technology with SLLE-LSSVM is a feasible qualitative analytical method which can simultaneously recognize the internal and

  1. Novel multi-target-directed ligands for Alzheimer's disease: Combining cholinesterase inhibitors and 5-HT6 receptor antagonists. Design, synthesis and biological evaluation.

    Science.gov (United States)

    Więckowska, Anna; Kołaczkowski, Marcin; Bucki, Adam; Godyń, Justyna; Marcinkowska, Monika; Więckowski, Krzysztof; Zaręba, Paula; Siwek, Agata; Kazek, Grzegorz; Głuch-Lutwin, Monika; Mierzejewski, Paweł; Bienkowski, Przemysław; Sienkiewicz-Jarosz, Halina; Knez, Damijan; Wichur, Tomasz; Gobec, Stanislav; Malawska, Barbara

    2016-11-29

    As currently postulated, a complex treatment may be key to an effective therapy for Alzheimer's disease (AD). Recent clinical trials in patients with moderate AD have shown a superior effect of the combination therapy of donepezil (a selective acetylcholinesterase inhibitor) with idalopirdine (a 5-HT 6 receptor antagonist) over monotherapy with donepezil. Here, we present the first report on the design, synthesis and biological evaluation of a novel class of multifunctional ligands that combines a 5-HT 6 receptor antagonist with a cholinesterase inhibitor. Novel multi-target-directed ligands (MTDLs) were designed by combining pharmacophores directed against the 5-HT 6 receptor (1-(phenylsulfonyl)-4-(piperazin-1-yl)-1H-indole) and cholinesterases (tacrine or N-benzylpiperidine analogues). In vitro evaluation led to the identification of tacrine derivative 12 with well-balanced potencies against the 5-HT 6 receptor (K b  = 27 nM), acetylcholinesterase and butyrylcholinesterase (IC 50 hAChE  = 12 nM, IC 50 hBuChE  = 29 nM). The compound also showed good in vitro blood-brain-barrier permeability (PAMPA-BBB assay), which was confirmed in vivo (open field study). Central cholinomimetic activity was confirmed in vivo in rats using a scopolamine-induced hyperlocomotion model. A novel class of multifunctional ligands with compound 12 as the best derivative in a series represents an excellent starting point for the further development of an effective treatment for AD. Copyright © 2016 Elsevier Masson SAS. All rights reserved.

  2. Safety, pharmacokinetics, and antitumor properties of anlotinib, an oral multi-target tyrosine kinase inhibitor, in patients with advanced refractory solid tumors

    Directory of Open Access Journals (Sweden)

    Yongkun Sun

    2016-10-01

    Full Text Available Abstract Background Anlotinib is a novel multi-target tyrosine kinase inhibitor that is designed to primarily inhibit VEGFR2/3, FGFR1-4, PDGFR α/β, c-Kit, and Ret. We aimed to evaluate the safety, pharmacokinetics, and antitumor activity of anlotinib in patients with advanced refractory solid tumors. Methods Anlotinib (5–16 mg was orally administered in patients with solid tumor once a day on two schedules: (1 four consecutive weeks (4/0 or (2 2-week on/1-week off (2/1. Pharmacokinetic sampling was performed in all patients. Twenty-one patients were further enrolled in an expanded cohort study on the recommended dose and schedule. Preliminary tumor response was also assessed. Results On the 4/0 schedule, dose-limiting toxicity (DLT was grade 3 hypertension at 10 mg. On the 2/1 schedule, DLT was grade 3 hypertension and grade 3 fatigue at 16 mg. Pharmacokinetic assessment indicated that anlotinib had long elimination half-lives and significant accumulation during multiple oral doses. The 2/1 schedule was selected, with 12 mg once daily as the maximum tolerated dose for the expanding study. Twenty of the 21 patients (with colon adenocarcinoma, non-small cell lung cancer, renal clear cell cancer, medullary thyroid carcinoma, and soft tissue sarcoma were assessable for antitumor activity of anlotinib: 3 patients had partial response, 14 patients had stable disease including 12 tumor burden shrinkage, and 3 had disease progression. The main serious adverse effects were hypertension, triglyceride elevation, hand-foot skin reaction, and lipase elevation. Conclusions At the dose of 12 mg once daily at the 2/1 schedule, anlotinib displayed manageable toxicity, long circulation, and broad-spectrum antitumor potential, justifying the conduct of further studies.

  3. Identification of Ideal Multi-targeting Bioactive Compounds Against Mur Ligases of Enterobacter aerogenes and Its Binding Mechanism in Comparison with Chemical Inhibitors.

    Science.gov (United States)

    Chakkyarath, Vijina; Natarajan, Jeyakumar

    2017-10-31

    Enterobacter aerogenes have been reported as important opportunistic and multi-resistant bacterial pathogens for humans during the last three decades in hospital wards. The emergence of drug-resistant E. aerogenes demands the need for developing new drugs. Peptidoglycan is an important component of the cell wall of bacteria and the peptidoglycan biochemical pathway is considered as the best source of antibacterial targets. Within this pathway, four Mur ligases MurC, MurD, MurE, and MurF are responsible for the successive additions of L-alanine and suitable targets for developing novel antibacterial drugs. As an inference from this fact, we modeled the three-dimensional structure of above Mur ligases using best template structures available in PDB and analyzed its common binding features. Structural refinement and energy minimization of the predicted Mur ligases models is also being done using molecular dynamics studies. The models of Mur ligases were further investigated for in silico docking studies using bioactive plant compounds from the literature. Interestingly, these results indicate that four plant compounds Isojuripidine, Atroviolacegenin, Porrigenin B, and Nummularogenin showing better docking results in terms of binding energy and number of hydrogen bonds. All these four compounds are spirostan-based compounds with differences in side chains and the amino acid such as ASN, LYS, THR, HIS, ARG (polar) and PHE, GLY, VAL, ALA, MET (non-polar) playing active role in binding site of all four Mur ligases. Overall, in the predicted model, the four plant compounds with its binding features could pave way to design novel multi-targeted antibacterial plant-based bioactive compounds specific to Mur ligases for the treatment of Enterobacter infections.

  4. Rational drug design for anti-cancer chemotherapy: multi-target QSAR models for the in silico discovery of anti-colorectal cancer agents.

    Science.gov (United States)

    Speck-Planche, Alejandro; Kleandrova, Valeria V; Luan, Feng; Cordeiro, M Natália D S

    2012-08-01

    The discovery of new and more potent anti-cancer agents constitutes one of the most active fields of research in chemotherapy. Colorectal cancer (CRC) is one of the most studied cancers because of its high prevalence and number of deaths. In the current pharmaceutical design of more efficient anti-CRC drugs, the use of methodologies based on Chemoinformatics has played a decisive role, including Quantitative-Structure-Activity Relationship (QSAR) techniques. However, until now, there is no methodology able to predict anti-CRC activity of compounds against more than one CRC cell line, which should constitute the principal goal. In an attempt to overcome this problem we develop here the first multi-target (mt) approach for the virtual screening and rational in silico discovery of anti-CRC agents against ten cell lines. Here, two mt-QSAR classification models were constructed using a large and heterogeneous database of compounds. The first model was based on linear discriminant analysis (mt-QSAR-LDA) employing fragment-based descriptors while the second model was obtained using artificial neural networks (mt-QSAR-ANN) with global 2D descriptors. Both models correctly classified more than 90% of active and inactive compounds in training and prediction sets. Some fragments were extracted from the molecules and their contributions to anti-CRC activity were calculated using mt-QSAR-LDA model. Several fragments were identified as potential substructural features responsible for the anti-CRC activity and new molecules designed from those fragments with positive contributions were suggested and correctly predicted by the two models as possible potent and versatile anti-CRC agents. Copyright © 2012 Elsevier Ltd. All rights reserved.

  5. Particle-balance models for pulsed sputtering magnetrons

    Science.gov (United States)

    Huo, Chunqing; Lundin, D.; Gudmundsson, J. T.; Raadu, M. A.; Bradley, J. W.; Brenning, N.

    2017-09-01

    The time-dependent plasma discharge ionization region model (IRM) has been under continuous development during the past decade and used in several studies of the ionization region of high-power impulse magnetron sputtering (HiPIMS) discharges. In the present work, a complete description of the most recent version of the IRM is given, which includes improvements, such as allowing for returning of the working gas atoms from the target, a separate treatment of hot secondary electrons, addition of doubly charged metal ions, etc. To show the general applicability of the IRM, two different HiPIMS discharges are investigated. The first set concerns 400 μs long discharge pulses applied to an Al target in an Ar atmosphere at 1.8 Pa. The second set focuses on 100 μs long discharge pulses applied to a Ti target in an Ar atmosphere at 0.54 Pa, and explores the effects of varying the magnetic field strength. The model results show that Al2+ -ions contribute negligibly to the production of secondary electrons, while Ti2+ -ions effectively contribute to the production of secondary electrons. Similarly, the model results show that for an argon discharge with Al target the contribution of Al+-ions to the discharge current at the target surface is over 90% at 800 V. However, at 400 V the Al+-ions and Ar+-ions contribute roughly equally to the discharge current in the initial peak, while in the plateau region Ar+-ions contribute to roughly \\frac{2}{3} of the current. For high currents the discharge with Al target develops almost pure self-sputter recycling, while the discharge with Ti target exhibits close to a 50/50 combination of self-sputter recycling and working gas-recycling. For a Ti target, a self-sputter yield significantly below unity makes working gas-recycling necessary at high currents. For the discharge with Ti target, a decrease in the B-field strength, resulted in a corresponding stepwise increase in the discharge resistivity.

  6. Properties of RF magnetron sputtered gallium nitride semiconductors doped with erbium

    Czech Academy of Sciences Publication Activity Database

    Peřina, Vratislav; Macková, Anna; Hnatowicz, Vladimír; Prajzler, V.; Machovič, V.; Matějka, P.; Schröfel, J.

    2004-01-01

    Roč. 36, č. 8 (2004), s. 952-954 ISSN 0142-2421 R&D Projects: GA ČR GA104/03/0387 Institutional research plan: CEZ:AV0Z1048901 Keywords : Er-doped GaN * luminescence * magnetron sputtering Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders Impact factor: 1.209, year: 2004

  7. High frequency pulse anodising of magnetron sputtered Al–Zr and Al–Ti Coatings

    DEFF Research Database (Denmark)

    Gudla, Visweswara Chakravarthy; Bordo, Kirill; Engberg, Sara

    2016-01-01

    High frequency pulse anodising of Al–Zr and Al–Ti coatings is studied as a surface finishing technique and compared to conventional decorative DC anodising. The Al–Zr and Al–Ti coatings were deposited using DC magnetron sputtering and were heat treated after deposition to generate a multiphase mi...

  8. Structure of AlN films deposited by magnetron sputtering method

    Directory of Open Access Journals (Sweden)

    Nowakowska-Langier K.

    2015-09-01

    Full Text Available AlN films on a Si substrate were synthesized by magnetron sputtering method. A dual magnetron system operating in AC mode was used in the experiment. Processes of synthesis were carried out in the atmosphere of a mixture of Ar/N2. Morphology and phase structure of the AlN films were investigated at different pressures. Structural characterizations were performed by means of SEM and X-ray diffraction methods. Our results show that the use of magnetron sputtering method in a dual magnetron sputtering system is an effective way to produce AlN layers which are characterized by a good adhesion to the silicon substrate. The morphology of the films is strongly dependent on the Ar/N2 gas mixture pressure. An increase of the mixture pressure is accompanied by a columnar growth of the layers. The films obtained at the pressure below 1 Pa are characterized by finer and compacter structure. The AlN films are characterized by a polycrystalline hexagonal (wurtzite structure in which the crystallographic orientation depends on the gas mixture pressure.

  9. A comparison of plasma in laser and hybrid laser-magnetron SiC deposition systems

    Czech Academy of Sciences Publication Activity Database

    Novotný, Michal; Bulíř, Jiří; Lančok, Ján; Jelínek, Miroslav

    2007-01-01

    Roč. 4, - (2007), S1017-S1021 ISSN 1612-8850 R&D Projects: GA AV ČR KJB1010417; GA ČR GA202/06/0216 Institutional research plan: CEZ:AV0Z10100522 Keywords : laser ablation * magnetron sputtering * optical emission spectroscopy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.132, year: 2007

  10. Polyester fabric coated with Ag/ZnO composite film by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Yuan, Xiaohong, E-mail: yxhong1981_2004@126.com [Key Laboratory of Eco-Textiles, Ministry of Education, Jiangnan University, Wuxi 214122, Jiangsu (China); Faculty of Clothing and Design, Minjiang University, Fuzhou 350121, Fujian (China); Xu, Wenzheng, E-mail: xwz8199@126.com [Key Laboratory of Eco-Textiles, Ministry of Education, Jiangnan University, Wuxi 214122, Jiangsu (China); Huang, Fenglin, E-mail: windhuang325@163.com [Key Laboratory of Eco-Textiles, Ministry of Education, Jiangnan University, Wuxi 214122, Jiangsu (China); Chen, Dongsheng, E-mail: mjuchen@126.com [Faculty of Clothing and Design, Minjiang University, Fuzhou 350121, Fujian (China); Wei, Qufu, E-mail: qfwei@jiangnan.edu.cn [Key Laboratory of Eco-Textiles, Ministry of Education, Jiangnan University, Wuxi 214122, Jiangsu (China)

    2016-12-30

    Highlights: • Ag/ZnO composite film was successfully deposited on polyester fabric by magnetron sputtering technique. • Ag film was easily oxidized into Ag{sub 2}O film in high vacuum oxygen environment. • The zinc film coated on the surface of Ag film before RF reactive sputtering could protect the silver film from oxidation. • Polyester fabric coated with Ag/ZnO composite film can obtained structural color. • The anti-ultraviolet and antistatic properties of polyester fabric coated with Ag/ZnO composite film all were good. - Abstract: Ag/ZnO composite film was successfully deposited on polyester fabric by using direct current (DC) magnetron sputtering and radio frequency (RF) magnetron reaction sputtering techniques with pure silver (Ag) and zinc (Zn) targets. X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) were used to examine the deposited film on the fabric. It was found that the zinc film coated on Ag film before RF reactive sputtering could protect the silver film from oxidation. Anti-ultraviolet property and antistatic property of the coated samples using different magnetron sputtering methods were also investigated. The experimental results showed that Ag film was oxidized into in Ag{sub 2}O film in high vacuum oxygen environment. The deposition of Zn film on the surface of the fabric coated with Ag film before RF reactive sputtering, could successfully obtained Ag/ZnO composite film, and also generated structural color on the polyester fabric.

  11. Magnetron sputtered gadolinia-doped ceria diffusion barriers for metal-supported solid oxide fuel cells

    DEFF Research Database (Denmark)

    Sønderby, Steffen; Klemensø, Trine; Christensen, Bjarke H.

    2014-01-01

    Gadolinia-doped ceria (GDC) thin films are deposited by reactive magnetron sputtering in an industrial-scale setup and implemented as barrier layers between the cathode and electrolyte in metal-based solid oxide fuel cells consisting of a metal support, an electrolyte of ZrO2 co-doped with Sc2O3...

  12. Analysis of conditions for magnetron discharge initiation at vacuum camera testing

    International Nuclear Information System (INIS)

    Tzeneva, Raina; Dineff, Peter; Darjanova, Denitza

    2002-01-01

    Models of electric field distribution for two typical cases of vacuum camera internal pressure control are investigated. New relations between the maximum magnetron discharge current value I max and the maximum electric field strength radial component value E τ max are established. (Author)

  13. Multi-sided metallization of textile fibres by using magnetron system with grounded cathode

    Directory of Open Access Journals (Sweden)

    Chodun Rafał

    2017-10-01

    Full Text Available The synthesis of coatings on textiles fibers enables functionalization of their properties e.g.: changing the reaction on IR radiation. In our experiment, a magnetron with a grounded cathode and positively biased anode was used as a source of plasma. A ring anode was positioned at 8 cm distance from the cathode. Samples of glass and cotton textile were placed at the plane of the anode. Ti and TiN coatings were deposited by sputtering of titanium target in Ar or Ar+ N2 atmosphere. SEM studies showed that, using the magnetron system described above, the textile fibers were covered by the 2 μm to 3 μm thick coatings. Unexpectedly, the coatings were deposited at both sides of the samples: the front side was exposed to glow discharge plasma and the backside was completely shaded from the plasma. IR optical investigation exhibited significant change in reflectance and transmittance of the coated textiles. The using of standard magnetron system (grounded anode and cathode at negative potential resulted in a coating deposition at the textile side exposed to the plasma action only. We believe that the multi-sided deposition of coatings observed during the process run with magnetron with grounded cathode is a result of an ambipolar diffusion mechanism in the anodic potential drop region.

  14. Interfacial Structure and Photocatalytic Activity of Magnetron Sputtered TiO2 on Conducting Metal Substrates

    DEFF Research Database (Denmark)

    Daviðsdóttir, Svava; Petit, Jean-Pierre; Mermoux, Michel

    2014-01-01

    The photocatalytic behavior of magnetron sputtered anatase TiO2 coatings on copper, nickel, and gold was investigated with the aim of understanding the effect of the metallic substrate and coating-substrate interface structure. Stoichiometry and nanoscale structure of the coating were investigated...

  15. Examination of the radiation of magnetron discharge in the process of spraying thin films

    International Nuclear Information System (INIS)

    Sokolov, V.F.; Sokolova, Yu.A.; Protasevich, A.A.

    1999-01-01

    In this work, we investigated the light radiation of the magnetron discharge in order to develop a method of spectral control and regulation of the process of deposition of thin films in UVN-25 industrial equipment used for metallising of superlarge integrated circuits and other components

  16. High rate deposition of thin film cadmium sulphide by pulsed direct current magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Lisco, F., E-mail: F.Lisco@lboro.ac.uk [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire LE11 3TU (United Kingdom); Kaminski, P.M.; Abbas, A.; Bowers, J.W.; Claudio, G. [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire LE11 3TU (United Kingdom); Losurdo, M. [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR, via Orabona 4, 70126 Bari (Italy); Walls, J.M. [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire LE11 3TU (United Kingdom)

    2015-01-01

    Cadmium Sulphide (CdS) is an important n-type semiconductor widely used as a window layer in thin film photovoltaics Copper Indium Selenide, Copper Indium Gallium (di)Selenide, Copper Zinc Tin Sulphide and Cadmium Telluride (CdTe). Cadmium Sulphide has been deposited using a number of techniques but these techniques can be slow (chemical bath deposition and Radio Frequency sputtering) or the uniformity and the control of thickness can be relatively difficult (close space sublimation). In this paper we report on the development of a process using pulsed Direct Current magnetron sputtering which allows nanometre control of thin film thickness using time only. The CdS thin films deposited in this process are highly uniform and smooth. They exhibit the preferred hexagonal structure at room temperature deposition and they have excellent optical properties. Importantly, the process is highly stable despite the use of a semi-insulating magnetron target. Moreover, the process is very fast. The deposition rate using 1.5 kW of power to a 6-inch circular magnetron was measured to be greater than 8 nm/s. This makes the process suitable for industrial deployment. - Highlights: • Pulsed DC magnetron sputtering of CdS • High deposition rate deposition • Uniform, pinhole free films.

  17. Advanced TiC/a-C : H nanocomposite coatings deposited by magnetron sputtering

    NARCIS (Netherlands)

    Pei, Y.T.; Galvan, D.; Hosson, J.Th.M. De; Strondl, C.

    2006-01-01

    TiC/a-C:H nanocomposite coatings have been deposited by magnetron Sputtering. They consist of 2-5 nm TiC nanocrystallites embedded in the amorphous hydrocarbon (a-C:H) matrix. A transition from a Columnar to a glassy microstructure has been observed in the nanocomposite coatings with increasing

  18. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    NARCIS (Netherlands)

    Rafieian Boroujeni, Damon; Ogieglo, Wojciech; Savenije, Tom; Lammertink, Rob G.H.

    2015-01-01

    We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to

  19. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    OpenAIRE

    Rafieian Boroujeni, Damon; Ogieglo, Wojciech; Savenije, Tom; Lammertink, Rob G.H.

    2015-01-01

    We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to anatase or rutile, depending on the initial sputtering conditions. Substoichiometric films (TiOx

  20. Magnetic field effects on coating deposition rate and surface morphology coatings using magnetron sputtering

    International Nuclear Information System (INIS)

    Yang, Yu-Sen; Huang, Wesley

    2010-01-01

    Chromium nitride coatings exhibit superior hardness, excellent wear and oxidation resistance, and are widely applied in the die and mold industries. The aim of this study was to investigate magnetic field effects on the deposition rate and surface morphology of chromium nitride coatings deposited by magnetron sputtering. Four types of magnetic field configurations, including the magnetron sputtering system, SNSN, SNNN, and intermediate magnetron modification, are discussed in this paper. SKD11 cold work die steel and a silicon (100) chip were used as substrates in the chromium nitride depositions. The process parameters, such as target current, substrate bias, and the distance between the substrate and target, are at fixed conditions, except for the magnetic arrangement type. The experimental results showed that the deposition rates of the four types of magnetic field configurations were 1.06, 1.38, 1.67 and 1.26 µm h −1 , respectively. In these cases, the SNNN type performs more than 58% faster than the unbalanced magnetron configuration does for the deposition rate. The surface morphology of chromium nitride films was also examined by SEM and is discussed in this paper

  1. A novel DC Magnetron sputtering facility for space research and synchrotron radiation optics

    DEFF Research Database (Denmark)

    Hussain, A.M.; Christensen, Finn Erland; Pareschi, G.

    1998-01-01

    A new DC magnetron sputtering facility has been build up at the Danish Space Research Institute (DSRI), specially designed to enable uniform coatings of large area curved optics, such as Wolter-I mirror optics used in space telescopes and curved optics used in synchrotron radiation facilities...

  2. Growth behavior of rat bone marrow cells on RF magnetron sputtered hydroxyapatite and dicalcium pyrophosphate coatings.

    NARCIS (Netherlands)

    Yan, Y.; Wolke, J.G.C.; Ruijter, A. De; Yubao, L.; Jansen, J.A.

    2006-01-01

    The aim of this study was to evaluate the osteogenic properties of magnetron sputtered dicalcium pyrophaosphate (DCPP) and hydroxylapatite (HA) coatings. Therefore, DCPP and HA coatings were deposited on grit-blasted titanium discs. The substrates were used as-prepared or received an additional heat

  3. Time-resolved investigation of an asymmetric bipolar pulsed magnetron deposition discharge: Influence of pressure

    NARCIS (Netherlands)

    Dunger, Th.; Welzel, Th.; Welzel, S.; Richter, F.

    2005-01-01

    A bipolar pulsed magnetron deposition discharge has been studied with pulse frequencies of 100 and 150 kHz, respectively. The discharge was operated in an argon/oxygen mixture at different total pressures with a circular magnesium target as cathode. Time-resolved Langmuir double probe measurements

  4. High rate deposition of thin film cadmium sulphide by pulsed direct current magnetron sputtering

    International Nuclear Information System (INIS)

    Lisco, F.; Kaminski, P.M.; Abbas, A.; Bowers, J.W.; Claudio, G.; Losurdo, M.; Walls, J.M.

    2015-01-01

    Cadmium Sulphide (CdS) is an important n-type semiconductor widely used as a window layer in thin film photovoltaics Copper Indium Selenide, Copper Indium Gallium (di)Selenide, Copper Zinc Tin Sulphide and Cadmium Telluride (CdTe). Cadmium Sulphide has been deposited using a number of techniques but these techniques can be slow (chemical bath deposition and Radio Frequency sputtering) or the uniformity and the control of thickness can be relatively difficult (close space sublimation). In this paper we report on the development of a process using pulsed Direct Current magnetron sputtering which allows nanometre control of thin film thickness using time only. The CdS thin films deposited in this process are highly uniform and smooth. They exhibit the preferred hexagonal structure at room temperature deposition and they have excellent optical properties. Importantly, the process is highly stable despite the use of a semi-insulating magnetron target. Moreover, the process is very fast. The deposition rate using 1.5 kW of power to a 6-inch circular magnetron was measured to be greater than 8 nm/s. This makes the process suitable for industrial deployment. - Highlights: • Pulsed DC magnetron sputtering of CdS • High deposition rate deposition • Uniform, pinhole free films

  5. SU-E-T-453: Image-Guided Patient-Specific Quality Assurance for Multi-Target Single Isocenter Intracranial VMAT Radiosurgery

    Energy Technology Data Exchange (ETDEWEB)

    Huang, M; Brezovich, I; Duan, J; Wu, X; Shen, S; Cardan, R.; Fiveash, J; Popple, R [Univ Alabama Birmingham, Birmingham, AL (United States)

    2015-06-15

    Purpose: To demonstrate a patient specific, image-guided quality assurance method that tests both dosimetric and geometric accuracy for single-isocenter multiple-target VMAT radiosurgery (SIMT-VMAT-SRS) Method: We used a new film type, EBT-XD (optimal range 0.4–40Gy), and an in-house PMMA phantom having a coronal plane for film and a 0.125 cm3 ionization chamber (IC). The phantom contained fiducial features for kV image guided setup and for accurate film marking. Five patient plans with multiple targets sizes ranging from 3 to 21mm in diameter and prescribed doses from 14 to 18 Gy were selected. Two verification plans were generated for each case with the film plane passing through the center of the largest and smallest targets. For the four largest targets we obtained an IC measurement. For each case, a calibration film was irradiated using a custom designed step pattern. The films were scanned using a flatbed color scanner and converted to dose using the calibration film and the three channel calibration method. Image registration was performed between film and treatment planning system calculations to evaluate the geometric accuracy. Results: The mean registration vector had an average magnitude of 0.47 mm (range from 0.13mm to 0.64 mm). For the four largest targets, the mean ratio of the IC and film measurement to expected dose was 0.990 (range 0.968 to 1.009) and 1.032 (1.021 to 1.046), respectively. The fraction of pixels having gamma index < 1 for criteria of 3%/3mm, 3%/2mm, 3%/1mm was 98.8%, 97.5% and 87.2% before geometric registration and 99.1%, 98.3% and 94.8% after registration. Conclusion: We have demonstrated an image-guided QA method can assess both geometric and dosimetric accuracy. The phantom was positioned with sub-millimeter accuracy. Absolute film dosimetry using EBT-XD film was sufficiently accurate for assessment of dose to multi-targets too small for IC measurement in SRS VMAT plans.

  6. Effect of deposition parameters on properties of ITO films prepared by reactive middle frequency pulsed dual magnetron sputtering

    International Nuclear Information System (INIS)

    Rogozin, A.I.; Vinnichenko, M.V.; Kolitsch, A.; Moeller, W.

    2004-01-01

    ITO layers with low resistivity and high visible transmittance were produced by means of middle frequency reactive dual magnetron sputtering. The influence of base pressure, Ar/O 2 ratio and magnetron pulse duration on the film composition, structure, electrical, and optical properties has been investigated. The deposition rate is proportional to the magnetron operation power at changing pulse duration and constant Ar and O 2 flows. At enhanced O 2 flows an onset of the magnetron target oxidation is discussed as a reason for the decrease of the deposition rate. The presence of water vapor in the residual gas is determined to be a reason for deterioration of resistivity and optical transmittance observed for ITO films produced at a base pressures higher than 5·10 -4 Pa. It is demonstrated that spectroscopic ellipsometry can be used as a noncontact tool to monitor the resistivity of ITO films

  7. Deposition of thin films by magnetron sputtering molybdenum in samples of pure copper; Deposicao de filmes finos de molibdenio por magnetron sputtering em amostra de cobre puro

    Energy Technology Data Exchange (ETDEWEB)

    Ferreira, N.M.; Almeida, E.O. de; Alves Junior, C. [Universidade Federal do Rio Grande do Norte, Campus Universitario Lagoa Nova, PPGCEM - Natal, RN (Brazil); Lourenco, J.M. [Instituto Federal de Educacao, Ciencias e Tecnologia do Rio Grande do Norte (IFRN), Natal, RN (Brazil)

    2010-07-01

    The deposition surface is a process of thermochemical treatment, which involves the deposition of a thin film usually about one to two microns on a metallic substrate, which constitutes one of the most important surface engineering techniques. The plasma deposition process with the configuration of magnetron sputtering it is removing material from a solid surface (target) through the impact of energetic particles from plasma. The aim of this study is to characterize the microstructure of the material under study using the techniques of optical microscopy and scanning electron microscopy. (author)

  8. Magnetron sputtering system with an annual discharge zone and two cathode modules

    International Nuclear Information System (INIS)

    Savich, V. A.; Yasyunas, A. A.; Kovrigo, V. M.; Kotov, D. A.; Shiripov, V. Ya.

    2013-01-01

    In this article, general discharge characteristics of a cylindrical magnetron sputtering system with an annual sputtering zone and a high target usage coefficient designed for transparent conducting coatings are shown. Two coupled DC-cathodes are used to improve coating uniformity. Radial sputtered material fluxes are being created. The engineered magnetic system is extremely balanced (G-factor is much higher than 2) and thus provides maximal effective operating power higher than 6 kW. The effectiveness of a magnetic trap results in a fast work cycle (less than 1.5 min) and a high target material usage coefficient (higher than 40%). A multipole magnetic field with null magnetic flux density zones lower target’s surface is being created. There is an influence between cathode modules despite mutual magnetic isolation, so magnetic conductors-shunts are used to weaken it. The magnetron can be used to sputter both metals and conducting ceramics (including ITO). (authors)

  9. Preparation and Characterization of FC Films Coated on PET Substrates by RF Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Huang Mei-lin

    2018-01-01

    Full Text Available Fluorocarbon (FC films were prepared on polyethylene terephthalate (PET plates and PET fabrics respectively by a radiofrequency (RF magnetron sputtering technique using polytetrafluoroethylene (PTFE as a target. Scanning electron microscope and X-ray photoelectron spectroscopy were used to investigate the morphology, structure and composition of the obtained FC films. The hydrophobicity and uvioresistant properties of the FC film coated fabric were studied. The results show that the FC films were successfully deposited on the PET substrates by a RF magnetron sputtering. The deposited films are made up of four components -CF3, -CF2-, CF- and -C-. The proportions of the four components and surface morphologies of the deposited films vary with the sputtering conditions. Compared with the original fabric samples, the hydrophobicity of the FC film coated fabrics is quite good and improved significantly.

  10. Microstructural evaluation of NiTi-based films deposited by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Crăciunescu, Corneliu M., E-mail: corneliu.craciunescu@upt.ro; Mitelea, Ion, E-mail: corneliu.craciunescu@upt.ro; Budău, Victor, E-mail: corneliu.craciunescu@upt.ro [Department of Materials and Manufacturing Engineering, Politehnica University of Timisoara (Romania); Ercuţa, Aurel [Department of Materials and Manufacturing Engineering, Politehnica University of Timisoara and Department of Physics, West University Timisoara (Romania)

    2014-11-24

    Shape memory alloy films belonging to the NiTi-based systems were deposited on heated and unheated substrates, by magnetron sputtering in a custom made system, and their structure and composition was analyzed using electron microscopy. Several substrates were used for the depositions: glass, Cu-Zn-Al, Cu-Al-Ni and Ti-NiCu shape memory alloy ribbons and kapton. The composition of the Ti-Ni-Cu films showed limited differences, compared to the one of the target and the microstructure for the DC magnetron sputtering revealed crystallized structure with features determined on peel off samples from a Si wafer. Both inter and transcrystalline fractures were observed and related to the interfacial stress developed on cooling from deposition temperature.

  11. Heat treatable indium tin oxide films deposited with high power pulse magnetron sputtering

    International Nuclear Information System (INIS)

    Horstmann, F.; Sittinger, V.; Szyszka, B.

    2009-01-01

    In this study, indium tin oxide (ITO) films were prepared by high power pulse magnetron sputtering [D. J. Christie, F. Tomasel, W. D. Sproul, D. C. Carter, J. Vac. Sci. Technol. A, 22 (2004) 1415. ] without substrate heating. The ITO films were deposited from a ceramic target at a deposition rate of approx. 5.5 nm*m/min kW. Afterwards, the ITO films were covered with a siliconoxynitride film sputtered from a silicon alloy target in order to prevent oxidation of the ITO film during annealing at 650 deg. C for 10 min in air. The optical and electrical properties as well as the texture and morphology of these films were investigated before and after annealing. Mechanical durability of the annealed films was evaluated at different test conditions. The results were compared with state-of-the art ITO films which were obtained at optimized direct current magnetron sputtering conditions

  12. Investigation of photocatalytic activity of titanium dioxide deposited on metallic substrates by DC magnetron sputtering

    DEFF Research Database (Denmark)

    Daviðsdóttir, Svava; Canulescu, Stela; Dirscherl, Kai

    2013-01-01

    The photocatalytic properties of titanium dioxide (TiO2) coating in the anatase crystalline structure deposited on aluminium AA1050 alloy and stainless steel S316L substrates were investigated. The coating was prepared by DC magnetron sputtering. The microstructure and surface morphology of the c......The photocatalytic properties of titanium dioxide (TiO2) coating in the anatase crystalline structure deposited on aluminium AA1050 alloy and stainless steel S316L substrates were investigated. The coating was prepared by DC magnetron sputtering. The microstructure and surface morphology...... sweep voltammetry, impedance measurements. The microstructure and surface morphology of the coating were similar irrespective of the nature of the substrate, while the photocatalytic behaviour was found to vary depending on the substrate type. In general the TiO2 coating on stainless steel was shown...

  13. Catalytic growth of ZnO nanostructures by r.f. magnetron sputtering

    Directory of Open Access Journals (Sweden)

    Arroyo-Hernández María

    2011-01-01

    Full Text Available Abstract The catalytic effect of gold seed particles deposited on a substrate prior to zinc oxide (ZnO thin film growth by magnetron sputtering was investigated. For this purpose, selected ultra thin gold layers, with thicknesses close to the percolation threshold, are deposited by thermal evaporation in ultra high vacuum (UHV conditions and subsequently annealed to form gold nanodroplets. The ZnO structures are subsequently deposited by r.f. magnetron sputtering in a UHV chamber, and possible morphological differences between the ZnO grown on top of the substrate and on the gold are investigated. The results indicate a moderate catalytic effect for a deposited gold underlayer of 4 nm, quite close to the gold thin film percolation thickness.

  14. Low temperature magnetron sputter deposition of polycrystalline silicon thin films using high flux ion bombardment

    International Nuclear Information System (INIS)

    Gerbi, Jennifer E.; Abelson, John R.

    2007-01-01

    We demonstrate that the microstructure of polycrystalline silicon thin films depends strongly on the flux of low energy ions that bombard the growth surface during magnetron sputter deposition. The deposition system is equipped with external electromagnetic coils which, through the unbalanced magnetron effect, provide direct control of the ion flux independent of the ion energy. We report the influence of low energy ( + on the low temperature ( + ions to silicon neutrals (J + /J 0 ) during growth by an order of magnitude (from 3 to 30) enables the direct nucleation of polycrystalline Si on glass and SiO 2 coated Si at temperatures below 400 degree sign C. We discuss possible mechanisms for this enhancement of crystalline microstructure, including the roles of enhanced adatom mobility and the formation of shallow, mobile defects

  15. Properties of H- and D- beams from magnetron and Penning sources

    International Nuclear Information System (INIS)

    Sluyters, T.; Kovarik, V.

    1979-01-01

    The quality of negative hydrogen isotope beams are evaluated after extraction from magnetron and Penning sources. The general conclusions of these measurements are that: (a) the beam quality from these plasma sources are adequate for the transport of high current negative ion beams in bending magnets; (b) there is evidence of practically complete space charge neutralization in the drift space beyond the extractor; (c) the beam performance from the Penning source appears to be better compared with the magnetron source; and (d) it is likely that the high electric field gradient and a concave ion emission boundary are responsible for a beam cross-over near the anode aperture, which causes beam divergence practically independent of the extraction geometry

  16. The microstructure and properties of titanium dioxide films synthesized by unbalanced magnetron sputtering

    International Nuclear Information System (INIS)

    Leng, Y.X.; Chen, J.Y.; Yang, P.; Sun, H.; Huang, N.

    2007-01-01

    In this work, titanium oxide films were deposited on Ti6Al4V and Si (1 0 0) by DC unbalanced magnetron sputtering method at different oxygen pressure. X-ray diffraction (XRD), microhardness tests, pin-on-disk wear experiments, surface contact angle tests and platelet adhesion investigation were conducted to evaluate the properties of the films. The corrosion behavior of titanium dioxide films was characterized by potentiodynamic polarization. The results showed that titanium oxide films deposited by unbalance magnetron sputtering were compact and could obviously enhance microhardness, wear resistance of titanium alloy substrate. Potentiodynamic polarization curves showed that Ti-6Al-4V deposited with titanium dioxide films had lower dissolution currents than that of the uncoated one. The results of in vitro hemocompatibility analyses indicated that the blood compatibility of the titanium dioxide films with bandgap 3.2 eV have better blood compatibility

  17. High power pulsed magnetron sputtering: A method to increase deposition rate

    International Nuclear Information System (INIS)

    Raman, Priya; McLain, Jake; Ruzic, David N; Shchelkanov, Ivan A.

    2015-01-01

    High power pulsed magnetron sputtering (HPPMS) is a state-of-the-art physical vapor deposition technique with several industrial applications. One of the main disadvantages of this process is its low deposition rate. In this work, the authors report a new magnetic field configuration, which produces deposition rates twice that of conventional magnetron's dipole magnetic field configuration. Three different magnet pack configurations are discussed in this paper, and an optimized magnet pack configuration for HPPMS that leads to a higher deposition rate and nearly full-face target erosion is presented. The discussed magnetic field produced by a specially designed magnet assembly is of the same size as the conventional magnet assembly and requires no external fields. Comparison of deposition rates with different power supplies and the electron trapping efficiency in complex magnetic field arrangements are discussed

  18. Investigation of the time evolution of plasma parameters in a pulsed magnetron discharge

    Czech Academy of Sciences Publication Activity Database

    Straňák, V.; Hubička, Zdeněk; Adámek, P.; Blažek, J.; Tichý, M.; Špatenka, P.; Hippler, R.; Wrehde, S.

    2006-01-01

    Roč. 56, - (2006), s. 1364-1370 ISSN 0011-4626 R&D Projects: GA ČR GA202/05/2242; GA ČR GA202/06/0776 Grant - others:Deutsche Forschungsgemeinschaft(DE) SFB/TR 24 Institutional research plan: CEZ:AV0Z10100522 Keywords : pulsed magnetron * time resolved measurements * Langmuir probe Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 0.568, year: 2006

  19. Generation of positive and negative oxygen ions in magnetron discharge during reactive sputtering of alumina

    Czech Academy of Sciences Publication Activity Database

    Pokorný, Petr; Bulíř, Jiří; Lančok, Ján; Musil, Jindřich; Novotný, Michal

    2010-01-01

    Roč. 7, č. 11 (2010), s. 910-914 ISSN 1612-8850 R&D Projects: GA AV ČR IAA100100718; GA AV ČR KAN400100653; GA ČR GP202/09/P324 Institutional research plan: CEZ:AV0Z10100522 Keywords : aluminium oxide * ion-energy distribution function * magnetron * mass spectrometry * pulsed discharges Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.643, year: 2010

  20. Reactive magnetron sputtering of Si-C-N films with controlled mechanical and optical properties

    Czech Academy of Sciences Publication Activity Database

    Vlček, J.; Kormunda, M.; Čížek, J.; Soukup, Z.; Peřina, Vratislav; Zemek, Josef

    2003-01-01

    Roč. 12, č. 8 (2003), s. 1287-1294 ISSN 0925-9635 R&D Projects: GA MŠk ME 203; GA MŠk OC 527.90 Institutional research plan: CEZ:MSM 235200002 Keywords : silicon-carbon-nitride films * magnetron co-sputtering Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders Impact factor: 1.867, year: 2003

  1. Nucleation of ultrathin silver layer by magnetron sputtering in Ar/N2 plasma

    Czech Academy of Sciences Publication Activity Database

    Bulíř, Jiří; Novotný, Michal; Lančok, Ján; Fekete, Ladislav; Drahokoupil, Jan; Musil, Jindřich

    2013-01-01

    Roč. 228, č. 1 (2013), S86-S90 ISSN 0257-8972 R&D Projects: GA ČR(CZ) GAP108/11/1298; GA ČR GP202/09/P324 Institutional support: RVO:68378271 Keywords : ultrathin silver * magnetron sputtering * spectral ellipsometry * in-situ monitoring Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.199, year: 2013

  2. RF magnetron sputtering and evaporation of polyisobutylene and low density polyethylene

    Czech Academy of Sciences Publication Activity Database

    Kousal, J.; Hanuš, J.; Choukourov, A.; Hlídek, P.; Biederman, H.; Slavinská, D.; Zemek, Josef

    2005-01-01

    Roč. 200, 1-4 (2005), s. 472-475 ISSN 0257-8972 R&D Projects: GA MŠk(CZ) OC 527.10; GA MŠk(CZ) ME 553 Institutional research plan: CEZ:AV0Z10100521 Keywords : magnetron * radio frequency * sputtering * polyethylene * polyisobutylene Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.646, year: 2005

  3. Deposition of thin titanium-copper films with antimicrobial effect by advanced magnetron sputtering methods

    Czech Academy of Sciences Publication Activity Database

    Straňák, V.; Wulff, H.; Rebl, H.; Zietz, C.; Arndt, K.; Bogdanowicz, R.; Nebe, B.; Bader, R.; Podbielski, A.; Hubička, Zdeněk; Hippler, R.

    2011-01-01

    Roč. 31, č. 7 (2011), s. 1512-1519 ISSN 0928-4931 R&D Projects: GA ČR(CZ) GAP205/11/0386; GA MŠk(CZ) 1M06002 Institutional research plan: CEZ:AV0Z10100520 Keywords : implant coating * titanium-copper film * pulsed magnetron sputtering Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.686, year: 2011

  4. Epitaxial growth of "infinite layer” thin films and multilayers by rf magnetron sputtering

    OpenAIRE

    Fàbrega, L.; Koller, E.; Triscone, J. M.; Fischer, Ø.

    2017-01-01

    We report on the preparation and characterization of epitaxial ACuO2 (A = Sr, Ca, Ba) thin films and multilayers with the so- called infinite layer (IL) structure, by rf magnetron sputtering. Films and multilayers without Ba have a remarkable crystal quality, whereas those containing this large ion are often multiphased and unstable. In spite of the excellent crystalline quality of these samples, obtaining thin films having both IL structure and displaying superconducting properties has not s...

  5. Rutile TiO2 thin films grown by reactive high power impulse magnetron sputtering

    International Nuclear Information System (INIS)

    Agnarsson, B.; Magnus, F.; Tryggvason, T.K.; Ingason, A.S.; Leosson, K.; Olafsson, S.; Gudmundsson, J.T.

    2013-01-01

    Thin TiO 2 films were grown on Si(001) substrates by reactive dc magnetron sputtering (dcMS) and high power impulse magnetron sputtering (HiPIMS) at temperatures ranging from 300 to 700 °C. Optical and structural properties of films were compared both before and after post-annealing using scanning electron microscopy, low angle X-ray reflection (XRR), grazing incidence X-ray diffractometry and spectroscopic ellipsometry. Both dcMS- and HiPIMS-grown films reveal polycrystalline rutile TiO 2 , even prior to post-annealing. The HiPIMS-grown films exhibit significantly larger grains compared to that of dcMC-grown films, approaching 100% of the film thickness for films grown at 700 °C. In addition, the XRR surface roughness of HiPIMS-grown films was significantly lower than that of dcMS-grown films over the whole temperature range 300–700 °C. Dispersion curves could only be obtained for the HiPIMS-grown films, which were shown to have a refractive index in the range of 2.7–2.85 at 500 nm. The results show that thin, rutile TiO 2 films, with high refractive index, can be obtained by HiPIMS at relatively low growth temperatures, without post-annealing. Furthermore, these films are smoother and show better optical characteristics than their dcMS-grown counterparts. - Highlights: • We demonstrate growth of rutile TiO 2 on Si (111) by high power impulse magnetron sputtering. • The films exhibit significantly larger grains than dc magnetron sputtered films • TiO 2 films with high refractive index are obtained without post-growth annealing

  6. Test stand for magnetron H negative ion source at IPP-Nagoya

    Energy Technology Data Exchange (ETDEWEB)

    Okamura, H; Kuroda, T; Miyahara, A

    1981-02-01

    Test facilities for the development of magnetron H(-) ion source consists of the vacuum system, power supplies, diagnostic equipment, and their controlling electronics. Schematics are presented and relevant items described including sequence control, optical links, the charged pulse forming network, the extractor power supply, magnet power supply, temperature control of the cesium feeder, and the pulsed valve driver. Noise problems and diagnostics are also considered.

  7. Advanced TiC/a-C: H nanocomposite coatings deposited by magnetron sputtering

    OpenAIRE

    Pei, Y.T.; Galvan, D.; Hosson, J.Th.M. De; Strondl, C.

    2006-01-01

    TiC/a-C:H nanocomposite coatings have been deposited by magnetron Sputtering. They consist of 2-5 nm TiC nanocrystallites embedded in the amorphous hydrocarbon (a-C:H) matrix. A transition from a Columnar to a glassy microstructure has been observed in the nanocomposite coatings with increasing substrate bias or carbon content. Micro-cracks induced by nanoindentation or wear tests readily propagate through the column boundaries whereas the coatings without a columnar inicrostructure exhibit s...

  8. Overview of recent studies and design changes for the FNAL magnetron ion source

    Science.gov (United States)

    Bollinger, D. S.; Sosa, A.

    2017-08-01

    This paper presents several studies and design changes that will eventually be implemented to the Fermi National Accelerator Laboratory (FNAL) magnetron ion source. The topics include tungsten cathode insert, solenoid gas valves, current controlled arc pulser, cesium boiler redesign, gas mixtures of hydrogen and nitrogen, and duty factor reduction. The studies were performed on the FNAL test stand described in [1], with the aim to improve source lifetime, stability, and reducing the amount of tuning needed.

  9. Overview of Recent Studies and Design Changes for the FNAL Magnetron Ion Source

    Energy Technology Data Exchange (ETDEWEB)

    Bollinger, D. S. [Fermilab; Sosa, A. [Fermilab

    2016-09-06

    This paper will cover several studies and design changes that will eventually be implemented to the Fermi National Accelerator Laboratory (FNAL) magnetron ion source. The topics include tungsten cathode insert, solenoid gas valves, current controlled arc pulser, cesium boiler redesign, gas mixtures of hydrogen and nitrogen, and duty factor reduction. The studies were performed on the FNAL test stand described in [1], with the aim to improve source lifetime, stability, and reducing the amount of tuning needed.

  10. Contribution to mechanical and crystallographic analysis of molyledenum layers prepared by magnetron cathode sputtering

    International Nuclear Information System (INIS)

    Bosland, P.

    1988-01-01

    Molybdenum coatings presenting different compression stresses are elaborated by magnetron cathode sputtering by varying the negative voltage of the substrate during deposition. Stress evolution is accompanied by crystal texture evolution and argon content incorporated in the layers. Crystallite orientation is explained by a phenomenon similar to canalisation observed in ion implantation. In a same deposit each component presents its own deformations different from neighbouring components [fr

  11. Status and prospects of a compact FIR FEL driven by a magnetron-based microtron

    International Nuclear Information System (INIS)

    Jeong, Young Uk; Kazakevitch, Grigori M.; Lee, Byung Cheol; Kim, Sun Kook; Cho, Sung Oh; Gavrilov, Nicolai G.; Lee, Jongmin

    2002-01-01

    A magnetron-based microtron as a driver of FIR FEL has several prominent advantages in cost, size, beam quality and operation convenience. However, it has some disadvantages due to the instability of the RF frequency and a low current. In order to overcome these disadvantages, the frequency stability of the magnetron was improved, and the interaction between the electron beam and the FIR radiation was enhanced by using a high-performance undulator and a low-loss waveguide-mode optical resonator. The FEL is now under upgrade in order to extend the wavelength range to cover 90-300 μm, which can be done by increasing the energy range of electron beam to 4.3-7 MeV. In this paper, we report the results of investigations on output characteristics of the FEL depending on cavity detuning, electron beam matching, and RF instability. Based on the results, we discuss the prospects of wide-band FIR FELs driven by magnetron-based microtrons as potent sources of radiation for scientific applications

  12. Estimation of Sputtering Damages on a Magnetron H- Ion Source Induced by Cs+ and H+ Ions

    CERN Document Server

    Pereira, H; Alessi, J; Kalvas, t

    2013-01-01

    An H− ion source is being developed for CERN’s Linac4 accelerator. A beam current requirement of 80 mA and a reliability above 99% during 1 year with 3 month uninterrupted operation periods are mandatory. To design a low-maintenance long life-time source, it is important to investigate and understand the wear mechanisms. A cesiated plasma discharge ion source, such as the BNL magnetron source, is a good candidate for the Linac4 ion source. However, in the magnetron source operated at BNL, the removal of material from the molybdenum cathode and the stainless steel anode cover plate surfaces is visible after extended operation periods. The observed sputtering traces are shown to result from cesium vapors and hydrogen gas ionized in the extraction region and subsequently accelerated by the extraction field. This paper presents a quantitative estimate of the ionization of cesium and hydrogen by the electron and H− beams in the extraction region of BNL’s magnetron ion source. The respective contributions o...

  13. Hybrid plasma system for magnetron deposition of coatings with ion assistance

    International Nuclear Information System (INIS)

    Vavilin, K V; Kralkina, E A; Nekludova, P A; Petrov, A. K; Nikonov, A M; Pavlov, V B; Airapetov, A A; Odinokov, V V; Pavlov, G Ya; Sologub, V A

    2016-01-01

    The results of the study of the plasma hybrid system based on the combined magnetron discharge and high-frequency inductive discharge located in the external magnetic field is presented. Magnetron discharge provides the generation of atoms and ions of the target materials while the flow of accelerated ions used for the ion assistance is provided by the RF inductive discharge. An external magnetic field is used to optimize the power input to the discharge, to increase the ion current density in the realm of substrate and to enhance the area of uniform plasma. The joint operation of magnetron and RF inductive discharge leads to a substantial increase (not equal to the sum of the parameters obtained under separate operation of two hybrid system channels) of the ion current density and intensity of sputtered material spectral lines radiation. Optimal mode of the hybrid plasma system operation provides uniform ion current density on the diameter of at least 150mm at 0.7PA argon pressure. The optimal values of the magnetic fields in the region of the substrate location lie in the range 2-8 mTl, while in the region of the RF input power unit lie in the range 0.5-25 mTl. (paper)

  14. Plasma ``anti-assistance'' and ``self-assistance'' to high power impulse magnetron sputtering

    Science.gov (United States)

    Anders, André; Yushkov, Georgy Yu.

    2009-04-01

    A plasma assistance system was investigated with the goal to operate high power impulse magnetron sputtering (HiPIMS) at lower pressure than usual, thereby to enhance the utilization of the ballistic atoms and ions with high kinetic energy in the film growth process. Gas plasma flow from a constricted plasma source was aimed at the magnetron target. Contrary to initial expectations, such plasma assistance turned out to be contraproductive because it led to the extinction of the magnetron discharge. The effect can be explained by gas rarefaction. A better method of reducing the necessary gas pressure is operation at relatively high pulse repetition rates where the afterglow plasma of one pulse assists in the development of the next pulse. Here we show that this method, known from medium-frequency (MF) pulsed sputtering, is also very important at the much lower pulse repetition rates of HiPIMS. A minimum in the possible operational pressure is found in the frequency region between HiPIMS and MF pulsed sputtering.

  15. Plasma 'anti-assistance' and 'self-assistance' to high power impulse magnetron sputtering

    International Nuclear Information System (INIS)

    Anders, Andre; Yushkov, Georgy Yu.

    2009-01-01

    A plasma assistance system was investigated with the goal to operate high power impulse magnetron sputtering (HiPIMS) at lower pressure than usual, thereby to enhance the utilization of the ballistic atoms and ions with high kinetic energy in the film growth process. Gas plasma flow from a constricted plasma source was aimed at the magnetron target. Contrary to initial expectations, such plasma assistance turned out to be contraproductive because it led to the extinction of the magnetron discharge. The effect can be explained by gas rarefaction. A better method of reducing the necessary gas pressure is operation at relatively high pulse repetition rates where the afterglow plasma of one pulse assists in the development of the next pulse. Here we show that this method, known from medium-frequency (MF) pulsed sputtering, is also very important at the much lower pulse repetition rates of HiPIMS. A minimum in the possible operational pressure is found in the frequency region between HiPIMS and MF pulsed sputtering

  16. Comparative study of niobium nitride coatings deposited by unbalanced and balanced magnetron sputtering

    International Nuclear Information System (INIS)

    Olaya, J.J.; Rodil, S.E.; Muhl, S.

    2008-01-01

    Niobium nitride (NbN) coatings have many interesting properties such as chemical inertness, excellent mechanical properties, high electrical conductivity, high melting point, and a superconducting transition temperature between 16 and 17 K. For this reason, these compounds have many potential thin film applications. In this work we compare the properties of NbN x films deposited using well-characterized balanced and unbalanced magnetron sputtering systems. Samples of NbN were deposited in the two systems under almost identical deposition conditions, that is, the same substrate temperature, plasma power, gas pressure, substrate to target distance and Ar/N 2 ratio. Prior to the film preparation both the magnetic field geometry and the characteristics of the plasma were determined. The microstructure and composition of the deposits were analyzed by X-ray diffraction, scanning electron microscopy and X-ray photoelectron spectroscopy. The corrosion resistance and the micro-abrasion wear resistance were measured by anodic polarization potentiodynamic studies and by ball cratering, respectively. The NbN films grown using the highly unbalanced magnetron configuration had a preferential (111) crystal orientation and a composite hardness of up to 2400 HV 0.025 . While the films deposited using the balanced magnetron had a mixed crystalline orientation and a hardness of 2000 HV 0.025 . The results demonstrate the strong effect of magnetic field configuration on the ion bombardment, and the resultant coating characteristics

  17. Comparative study of niobium nitride coatings deposited by unbalanced and balanced magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Olaya, J.J. [Departamento de Ingenieria Mecanica y Mecatronica, Universidad Nacional de Colombia, Bogota Colombia (Colombia); Rodil, S.E. [Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de Mexico, Mexico D. F. 04510 (Mexico); Muhl, S. [Instituto de Investigaciones en Materiales, Universidad Nacional Autonoma de Mexico, Mexico D. F. 04510 (Mexico)], E-mail: muhl@servidor.unam.mx

    2008-10-01

    Niobium nitride (NbN) coatings have many interesting properties such as chemical inertness, excellent mechanical properties, high electrical conductivity, high melting point, and a superconducting transition temperature between 16 and 17 K. For this reason, these compounds have many potential thin film applications. In this work we compare the properties of NbN{sub x} films deposited using well-characterized balanced and unbalanced magnetron sputtering systems. Samples of NbN were deposited in the two systems under almost identical deposition conditions, that is, the same substrate temperature, plasma power, gas pressure, substrate to target distance and Ar/N{sub 2} ratio. Prior to the film preparation both the magnetic field geometry and the characteristics of the plasma were determined. The microstructure and composition of the deposits were analyzed by X-ray diffraction, scanning electron microscopy and X-ray photoelectron spectroscopy. The corrosion resistance and the micro-abrasion wear resistance were measured by anodic polarization potentiodynamic studies and by ball cratering, respectively. The NbN films grown using the highly unbalanced magnetron configuration had a preferential (111) crystal orientation and a composite hardness of up to 2400 HV{sub 0.025}. While the films deposited using the balanced magnetron had a mixed crystalline orientation and a hardness of 2000 HV{sub 0.025}. The results demonstrate the strong effect of magnetic field configuration on the ion bombardment, and the resultant coating characteristics.

  18. Implementation of Design Changes Towards a More Reliable, Hands-off Magnetron Ion Source

    Energy Technology Data Exchange (ETDEWEB)

    Sosa, A. [Fermilab; Bollinger, D. S. [Fermilab; Karns, P. R. [Fermilab; Tan, C. Y. [Fermilab

    2017-12-07

    As the main H- ion source for the accelerator complex, magnetron ion sources have been used at Fermilab since the 1970’s. At the offline test stand, new R&D is carried out to develop and upgrade the present magnetron-type sources of H- ions of up to 80 mA and 35 keV beam energy in the context of the Proton Improvement Plan. The aim of this plan is to provide high-power proton beams for the experiments at FNAL. In order to reduce the amount of tuning and monitoring of these ion sources, a new electronic system consisting of a current-regulated arc discharge modulator allow the ion source to run at a constant arc current for improved beam output and operation. A solenoid-type gas valve feeds H2 gas into the source precisely and independently of ambient temperature. This summary will cover several studies and design changes that have been tested and will eventually be implemented on the operational magnetron sources at Fermilab. Innovative results for this type of ion source include cathode geometries, solenoid gas valves, current controlled arc pulser, cesium boiler redesign, gas mixtures of hydrogen and nitrogen, and duty factor reduction, with the aim to improve source lifetime, stability, and reducing the amount of tuning needed. In this summary, I will highlight the advances made in ion sources at Fermilab and will outline the directions of the continuing R&D effort.

  19. Fabrication and characterization of flaky core-shell particles by magnetron sputtering silver onto diatomite

    Science.gov (United States)

    Wang, Yuanyuan; Zhang, Deyuan; Cai, Jun

    2016-02-01

    Diatomite has delicate porous structures and various shapes, making them ideal templates for microscopic core-shell particles fabrication. In this study, a new process of magnetron sputtering assisted with photoresist positioning was proposed to fabricate lightweight silver coated porous diatomite with superior coating quality and performance. The diatomite has been treated with different sputtering time to investigate the silver film growing process on the surface. The morphologies, constituents, phase structures and surface roughness of the silver coated diatomite were analyzed with SEM, EDS, XRD and AFM respectively. The results showed that the optimized magnetron sputtering time was 8-16 min, under which the diatomite templates were successfully coated with uniform silver film, which exhibits face centered cubic (fcc) structure, and the initial porous structures were kept. Moreover, this silver coating has lower surface roughness (RMS 4.513 ± 0.2 nm) than that obtained by electroless plating (RMS 15.692 ± 0.5 nm). And the infrared emissivity of coatings made with magnetron sputtering and electroless plating silver coated diatomite can reach to the lowest value of 0.528 and 0.716 respectively.

  20. [Effects of magnetron sputtered ZrN on the bonding strength of titanium porcelain].

    Science.gov (United States)

    Zhou, Shu; Zhang, Wen-yan; Guang, Han-bing; Xia, Yang; Zhang, Fei-min

    2009-04-01

    To investigate the effect of magnetron sputtered ZrN on the bonding strength between a low-fusing porcelain (Ti/Vita titankeramik system) and commercially pure cast titanium. Sixteen specimens were randomly assigned to test group and control group (n=8). The control group received no surface treated. Magnetron sputtered ZrN film was deposited on the surface of specimens in the test group. Then the sixteen titanium-porcelain specimens were prepared in a rectangular shape and went through three-point bending test on a universal test machine. The bond strength of Ti/porcelain was recorded. The phase composition of the specimens was analyzed using X-ray diffraction (XRD). The interface at titanium and porcelain and the titanium surface after debonding were observed with a scanning electron microscopy (SEM) and analyzed using energy depressive spectrum (EDS). New phase of ZrN was found with XRD in the test group. Statistical analysis showed higher bond strength following ZrN surface treatment in the test group [(45.991+/-0.648) MPa] than that in the control group [(29.483+/-1.007) MPa] (P=0.000). Bonded ceramic could be observed in test group, the amount of bonded ceramic was more than that in the control group. No obvious bonded ceramic in control group was found. Magnetron sputtered ZrN can improve bond strength of Ti/Vita titankeramik system significantly.

  1. Simulation of the electric potential and plasma generation coupling in magnetron sputtering discharges

    Science.gov (United States)

    Trieschmann, Jan; Krueger, Dennis; Schmidt, Frederik; Brinkmann, Ralf Peter; Mussenbrock, Thomas

    2016-09-01

    Magnetron sputtering typically operated at low pressures below 1 Pa is a widely applied deposition technique. For both, high power impulse magnetron sputtering (HiPIMS) as well as direct current magnetron sputtering (dcMS) the phenomenon of rotating ionization zones (also referred to as spokes) has been observed. A distinct spatial profile of the electric potential has been associated with the latter, giving rise to low, mid, and high energy groups of ions observed at the substrate. The adherent question of which mechanism drives this process is still not fully understood. This query is approached using Monte Carlo simulations of the heavy particle (i.e., ions and neutrals) transport consistently coupled to a pre-specified electron density profile via the intrinsic electric field. The coupling between the plasma generation and the electric potential, which establishes correspondingly, is investigated. While the system is observed to strive towards quasi-neutrality, distinct mechanisms governing the shape of the electric potential profile are identified. This work is supported by the German Research Foundation (DFG) in the frame of the transregional collaborative research centre TRR 87.

  2. Electrochemical behavior of single layer CrN, TiN, TiAlN coatings and nanolayered TiAlN/CrN multilayer coatings prepared by reactive direct current magnetron sputtering

    International Nuclear Information System (INIS)

    William Grips, V.K.; Barshilia, Harish C.; Selvi, V. Ezhil; Kalavati; Rajam, K.S.

    2006-01-01

    The corrosion behaviors of single layer TiN, CrN, TiAlN and multilayer TiAlN/CrN coatings, deposited on steel substrate using a multi-target reactive direct current magnetron sputtering process, were studied in 3.5% NaCl solution by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The total thickness of the coatings was about 1.5 μm. About 0.5 μm thick chromium interlayer was used for improved adhesion of the coatings. The potentiodynamic polarization measurements showed that for all the coatings the corrosion potential shifted to higher values as compared to the uncoated substrate. Similarly, the corrosion current density decreased for coated samples, indicating better corrosion resistance of the coated samples. The multilayer coatings of TiAlN/CrN exhibited superior corrosion behavior as compared to the single layer coatings. The Nyquist and the Bode plots obtained from the EIS measurements were fitted by appropriate equivalent circuits to calculate the pore resistance, the charge transfer resistance and the capacitance. These studies revealed that the pore resistance was lowest for TiN coatings, which increased for TiAlN coatings. TiAlN/CrN multilayer coatings exhibited highest pore resistance. No significant change in the capacitive behavior of the coatings was observed, suggesting minimal morphological changes as a result of immersion in the electrolyte. This could be attributed to shorter immersion durations. These studies were confirmed by examining the corroded samples under scanning electron microscope. Preliminary experiments conducted with additional interlayer of electroless nickel (5.0 μm thick) have shown significant improvement in the corrosion resistance of the coatings

  3. Development of a Magnetron Resonance Frequency Auto Tuning System for Medical Xband [9300 MHz] RF Linear Accelerator

    Energy Technology Data Exchange (ETDEWEB)

    Cha, Sung Su; Lee, Byung Cheol [University of Science and Technology, Daejeon (Korea, Republic of); Kim, Yujong; Park, Hyung Dal; Lee, Byeong-No; Joo, Youngwoo; Cha, Hyungki; Lee, Soo Min; Song, Ki Baek [KAERI, Daejeon (Korea, Republic of); Lee, Seung Hyun [Sungkyunkwan University, Suwon (Korea, Republic of)

    2015-05-15

    The total components of the accelerator are the magnetron, electron gun, accelerating structure, a set of solenoid magnets, four sets of steering coils, a modulator, and a circulator. One of the accelerator components of the accelerating structure is made of oxygen-free high-conductivity copper (OFHC), and its volume is changed according to the ambient temperature. As the volume changes, the resonant frequency of the accelerating structure is changed. Accordingly, the resonance frequency is mismatched between the source of the magnetron and the accelerating structure. An automatic frequency tuning system is automatically matched with the resonant frequency of the magnetron and accelerating structure, which allows a high output power and reliable accelerator operation. An automatic frequency tuning system is composed of a step motor control part for correcting the frequency of the source and power measuring parts, i.e., the forward and reflected power between the magnetron and accelerating structure. In this paper, the design, fabrication, and RF power test of the automatic frequency tuning system for the X-band linac are presented. A frequency tuning system was developed to overcome an unstable accelerator operation owing to the frequency mismatch between the magnetron and accelerating structure. The frequency measurement accuracy is 100 kHz and 0.72 degree per pulse.

  4. Deposition and characterization of TaAIN thin films by reactive magnetron sputtering; Deposicao e caracterizacao de filmes finos de TaAIN depositados por magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, G.B.; Fernandez, D.R.; Fontes Junior, A.S.; Felix, L.C.; Tentardini, E.K. [Universidade Federal de Sergipe (UFS), Sao Cristovao, SE (Brazil). Departamento de Ciencia e Engenharia de Materiais; Hubler, R. [Pontificia Universidade Catolica do Rio Grande do Sul (PUC-RS), RS (Brazil); Silva Junior, A.H. da, E-mail: brito-g@hotmail.com [Universidade Federal do Rio Grande do Sul (UFRGS), RS (Brazil)

    2016-07-01

    Phase stability, oxidation resistance and great mechanical properties are the main objectives when synthesizing protective coatings. The tantalum nitride (TaN) has aroused interest because of its high temperature stability, chemical inertness and thermal conductivity. However, it has a low hardness value when compared to other coatings. Researches has shown that one way to improvements in the properties of a thin film is by adding other elements in the deposition process. Therefore, the objective of this study was to deposit thin films of TaAlN by magnetron sputtering, changing the aluminum concentration of 2, 5, 7, to 14%. Then the coatings were characterized by EDS, RBS, GIXRD and nanohardness. In this study was found that the aluminum deposited did not change the oxidation resistance of the coating, and the highest value of hardness was 28 GPa for the sample with 14 at.%. (author)

  5. Tribological properties, corrosion resistance and biocompatibility of magnetron sputtered titanium-amorphous carbon coatings

    International Nuclear Information System (INIS)

    Dhandapani, Vishnu Shankar; Subbiah, Ramesh; Thangavel, Elangovan; Arumugam, Madhankumar; Park, Kwideok; Gasem, Zuhair M.; Veeraragavan, Veeravazhuthi; Kim, Dae-Eun

    2016-01-01

    Highlights: • a-C:Ti nanocomposite coatings were prepared on 316L stainless steel by using R.F. magnetron sputtering method. • Properties of the nanocomposite coatings were analyzed with respect to titanium content. • Corrosion resistance, biocompatibility and hydrophobicity of nanocomposite coating were enhanced with increasing titanium content. • Coating with 2.33 at.% titanium showed superior tribological properties compared to other coatings. - Abstract: Amorphous carbon incorporated with titanium (a-C:Ti) was coated on 316L stainless steel (SS) by magnetron sputtering technique to attain superior tribological properties, corrosion resistance and biocompatibility. The morphology, topography and functional groups of the nanostructured a-C:Ti coatings in various concentrations were analyzed using atomic force microscopy (AFM), Raman, X-Ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Raman and XPS analyses confirmed the increase in sp"2 bonds with increasing titanium content in the a-C matrix. TEM analysis confirmed the composite nature of the coating and the presence of nanostructured TiC for Ti content of 2.33 at.%. This coating showed superior tribological properties compared to the other a-C:Ti coatings. Furthermore, electrochemical corrosion studies were performed against stimulated body fluid medium in which all the a-C:Ti coatings showed improved corrosion resistance than the pure a-C coating. Preosteoblasts proliferation and viability on the specimens were tested and the results showed that a-C:Ti coatings with relatively high Ti (3.77 at.%) content had better biocompatibility. Based on the results of this work, highly durable coatings with good biocompatibility could be achieved by incorporation of optimum amount of Ti in a-C coatings deposited on SS by magnetron sputtering technique.

  6. Hydroxyapatite formation on biomedical Ti–Ta–Zr alloys by magnetron sputtering and electrochemical deposition

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Hyun-Ju [Department of Dental Materials, Research Center of Nano-Interface Activation for Biomaterials, and Research Center for Oral Disease Regulation of the Aged, School of Dentistry, Chosun University, Gwangju (Korea, Republic of); Jeong, Yong-Hoon [Biomechanics and Tissue Engineering Laboratory, Division of Orthodontics, College of Dentistry, The Ohio State University, Columbus, OH (United States); Choe, Han-Cheol, E-mail: hcchoe@chosun.ac.kr [Department of Dental Materials, Research Center of Nano-Interface Activation for Biomaterials, and Research Center for Oral Disease Regulation of the Aged, School of Dentistry, Chosun University, Gwangju (Korea, Republic of); Brantley, William A. [Division of Prosthodontics and Restorative Science, College of Dentistry, The Ohio State University, Columbus, OH (United States)

    2014-12-01

    The purpose of this study was to investigate hydroxyapatite formation on Ti-25Ta-xZr titanium alloys resulting from radio-frequency magnetron sputtering and electrochemical deposition. Electrochemical deposition of hydroxyapatite (HA) was first carried out using a cyclic voltammetry (CV) method at 80 °C in 5 mM Ca (NO{sub 3}){sub 2} + 3 mM NH{sub 4}H{sub 2}PO{sub 4}. Then a physical vapor deposition (PVD) coating was obtained by a radio-frequency (RF) magnetron sputtering technique. The microstructures, phase transformations, and morphologies of the hydroxyapatite films deposited on the titanium alloys were analyzed by optical microscopy (OM), X-ray diffractometer (XRD), energy dispersive X-ray spectroscopy (EDS) and field-emission scanning electron microscopy (FE-SEM). The morphologies of electrochemically deposited HA showed plate-like shapes on the titanium alloys, and the morphologies of the RF-sputtered HA coating had the appearance droplet particles on the plate-like precipitates that had formed by electrochemical deposition. For the RF-sputtered HA coatings, the Ca/P ratio was increased, compared to that for the electrochemically deposited HA surface. Moreover, the RF-sputtered HA coating, consisting of agglomerated droplet particles on the electrochemically deposited HA surface, had better wettability compared to the bulk titanium alloy surface. - Highlights: • Hydroxyapatite (HA) was deposited on Ti–Ta–Zr alloys by radio-frequency (RF) magnetron sputtering and a cyclic voltammetry. • The morphologies of the RF-sputtered HA coating on electrochemical deposits presented plate-like shapes with a droplet particle. • The Ca/P ratio for RF-sputtered HA coatings was greater than that for electrochemical deposited HA coatings. • The RF-sputtered and electrochemical HA coatings had superior wettability compared to the electrochemically deposited coatings.

  7. Computer investigations of the influences of magnets for magnetron-sputtering

    International Nuclear Information System (INIS)

    Knotek, O.; Loeffler, F.; Schnaut, U.; Guan, W.

    1993-01-01

    For a long time PVD (Physical-Vapour-Deposition) technology has been applied in various modern technical fields, owing to the wide range of possible coating materials whose potential is virtually unlimited. Besides electronic, optical and decorative applications for PVD films, hard films, in particular, have been widely applied for tool coatings which play important roles for the resistance against wear and corrosion. The MSIP (Magnetron-Sputter-Ion-Plating) coating process is one of the PVD-processes, providing 1) relatively high deposition rates, 2) large deposition areas, and 3) low substrate heating. The magnetron behind the target influences the distribution of the electrons moving in the plasma and the space between the cathode and anode, thus the distribution of the ions impinging on the surface of the target. Since the electrons are distributed unevenly in front of the target, the working gas atoms are therefore unevenly ionized in the plasma and the ions also unevenly bombard the target surface and the erosion of the target surface is uneven. Therefore the investigations of the magnetic field in the MSIP are very important for the optimization of the deposition process and the usage of the target. Generally, the accurate calculations or measurements of the direction and strength of the magnetic field (magnetic induction or magnetic flux density vector B) is difficult in comparison to measurements of the electrical field, because vector B is a vector with varying direction and magnitude. In this paper, it is shown that a magnetic field of a cylindrical magnetron in MSIP-equipment can be quickly simulated through a simple model and the distribution of the field is discussed. (orig.)

  8. Hydroxyapatite formation on biomedical Ti–Ta–Zr alloys by magnetron sputtering and electrochemical deposition

    International Nuclear Information System (INIS)

    Kim, Hyun-Ju; Jeong, Yong-Hoon; Choe, Han-Cheol; Brantley, William A.

    2014-01-01

    The purpose of this study was to investigate hydroxyapatite formation on Ti-25Ta-xZr titanium alloys resulting from radio-frequency magnetron sputtering and electrochemical deposition. Electrochemical deposition of hydroxyapatite (HA) was first carried out using a cyclic voltammetry (CV) method at 80 °C in 5 mM Ca (NO 3 ) 2 + 3 mM NH 4 H 2 PO 4 . Then a physical vapor deposition (PVD) coating was obtained by a radio-frequency (RF) magnetron sputtering technique. The microstructures, phase transformations, and morphologies of the hydroxyapatite films deposited on the titanium alloys were analyzed by optical microscopy (OM), X-ray diffractometer (XRD), energy dispersive X-ray spectroscopy (EDS) and field-emission scanning electron microscopy (FE-SEM). The morphologies of electrochemically deposited HA showed plate-like shapes on the titanium alloys, and the morphologies of the RF-sputtered HA coating had the appearance droplet particles on the plate-like precipitates that had formed by electrochemical deposition. For the RF-sputtered HA coatings, the Ca/P ratio was increased, compared to that for the electrochemically deposited HA surface. Moreover, the RF-sputtered HA coating, consisting of agglomerated droplet particles on the electrochemically deposited HA surface, had better wettability compared to the bulk titanium alloy surface. - Highlights: • Hydroxyapatite (HA) was deposited on Ti–Ta–Zr alloys by radio-frequency (RF) magnetron sputtering and a cyclic voltammetry. • The morphologies of the RF-sputtered HA coating on electrochemical deposits presented plate-like shapes with a droplet particle. • The Ca/P ratio for RF-sputtered HA coatings was greater than that for electrochemical deposited HA coatings. • The RF-sputtered and electrochemical HA coatings had superior wettability compared to the electrochemically deposited coatings

  9. Rotating dust ring in an RF discharge coupled with a dc-magnetron sputter source. Experiment and simulation

    International Nuclear Information System (INIS)

    Matyash, K; Froehlich, M; Kersten, H; Thieme, G; Schneider, R; Hannemann, M; Hippler, R

    2004-01-01

    During an experiment involving coating of dust grains trapped in an RF discharge using a sputtering dc-magnetron source, a rotating dust ring was observed and investigated. After the magnetron was switched on, the dust cloud levitating above the RF electrode formed a ring rotating as a rigid body. Langmuir probe diagnostics were used for the measurement of plasma density and potential. It was discovered that the coupling of the dc-magnetron source to the RF discharge causes steep radial gradients in electron density and plasma potential. The rotation of the dust ring is attributed to the azimuthal component of the ion drag force, which appears due to the azimuthal drift of the ions caused by crossed radial electric and axial magnetic fields. In order to get more insight into the mechanism of dust ring rotation, a Particle-in-Cell simulation of a rotating dust cloud was performed. The results of the experiment and simulation are presented and discussed

  10. Rotating dust ring in an RF discharge coupled with a dc-magnetron sputter source. Experiment and simulation

    Energy Technology Data Exchange (ETDEWEB)

    Matyash, K [Institut fuer Niedertemperaturplasmaphysik Greifswald, Fr.-L.-Jahn-Strasse 19, 17489 Greifswald (Germany); Froehlich, M [Institut fuer Physik, Ernst-Moritz-Arndt-Universitaet Greifswald, Domstrasse 10a, 17487 Greifswald (Germany); Kersten, H [Institut fuer Niedertemperaturplasmaphysik Greifswald, Fr.-L.-Jahn-Strasse 19, 17489 Greifswald (Germany); Thieme, G [Institut fuer Physik, Ernst-Moritz-Arndt-Universitaet Greifswald, Domstrasse 10a, 17487 Greifswald (Germany); Schneider, R [Max-Planck-Institut fuer Plasmaphysik, Teilinstitut Greifswald, Wendelsteinstrasse 1, 17489 Greifswald (Germany); Hannemann, M [Institut fuer Niedertemperaturplasmaphysik Greifswald, Fr.-L.-Jahn-Strasse 19, 17489 Greifswald (Germany); Hippler, R [Institut fuer Physik, Ernst-Moritz-Arndt-Universitaet Greifswald, Domstrasse 10a, 17487 Greifswald (Germany)

    2004-10-07

    During an experiment involving coating of dust grains trapped in an RF discharge using a sputtering dc-magnetron source, a rotating dust ring was observed and investigated. After the magnetron was switched on, the dust cloud levitating above the RF electrode formed a ring rotating as a rigid body. Langmuir probe diagnostics were used for the measurement of plasma density and potential. It was discovered that the coupling of the dc-magnetron source to the RF discharge causes steep radial gradients in electron density and plasma potential. The rotation of the dust ring is attributed to the azimuthal component of the ion drag force, which appears due to the azimuthal drift of the ions caused by crossed radial electric and axial magnetic fields. In order to get more insight into the mechanism of dust ring rotation, a Particle-in-Cell simulation of a rotating dust cloud was performed. The results of the experiment and simulation are presented and discussed.

  11. Influence of substrate temperature on the optical and electrical properties magnetron sputtering ITO films

    International Nuclear Information System (INIS)

    Khripunov, G.S.; Yurchenko, G.V.

    1999-01-01

    Electrical and optical properties of ITO films obtained at substrate temperature from 200 degree C to 500 degree C by magnetron sputtering of target 95% In 2 O 3 - 5% SnO 2 were studied. It was shown that the ITO film obtained at the substrate temperature 300 i N have optimum combination of the optical and electrical characteristics: resistivity 2.1 centre dot 10 -4 Ω cm, transmittance in visible spectral range about 88% at the thickness film 0.61 μ, factor of quality reaches 8.2 centre dot 10 -2 Ω 1

  12. Deposition of indium tin oxide films on acrylic substrates by radiofrequency magnetron sputtering

    International Nuclear Information System (INIS)

    Chiou, B.S.; Hsieh, S.T.; Wu, W.F.

    1994-01-01

    Indium tin oxide (ITO) films were deposited onto acrylic substrates by rf magnetron sputtering. Low substrate temperature (< 80 C) and low rf power (< 28 W) were maintained during sputtering to prevent acrylic substrate deformation. The influence of sputtering parameters, such as rf power, target-to-substrate distance, and chamber pressure, on the film deposition rate, the electrical properties, as well as the optical properties of the deposited films was investigated. Both the refractive index and the extinction coefficient were derived. The high reflection at wavelengths greater than 3 μm made these sputtered ITO films applicable to infrared mirrors

  13. Contamination of magnetron sputtered metallic films by oxygen from residual atmosphere in deposition chamber

    Czech Academy of Sciences Publication Activity Database

    Pokorný, Petr; Musil, Jindřich; Fitl, Přemysl; Novotný, Michal; Lančok, Ján; Bulíř, Jiří

    2015-01-01

    Roč. 12, č. 5 (2015), s. 416-421 ISSN 1612-8850 R&D Projects: GA ČR(CZ) GAP108/11/1298; GA ČR(CZ) GAP108/11/1312; GA ČR(CZ) GAP108/11/0958; GA ČR(CZ) GA14-10279S Institutional support: RVO:68378271 Keywords : contamination * low-pressure discharges * magnetron * metallic films * sputtering Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.713, year: 2015

  14. FAST TRACK COMMUNICATION: Deposition of amino-rich thin films by RF magnetron sputtering of nylon

    Science.gov (United States)

    Kylián, O.; Hanuš, J.; Choukourov, A.; Kousal, J.; Slavínská, D.; Biederman, H.

    2009-07-01

    RF magnetron sputtering of a nylon target in different gas mixtures was studied in order to evaluate the capability of this process to deposit amino-rich coatings needed in a wide range of biomedical applications. It has been demonstrated that both the deposition rate of the coatings and the surface density of primary amino groups are strongly linked with working gas mixture composition. From this point of view, a sufficiently high deposition rate as well as the highest amine efficiency reaching a NH2/C value of 18% was observed in the N2/H2 discharge, which leads to the surface exhibiting a high rate of protein adsorption.

  15. Spectroscopic imaging of self-organization in high power impulse magnetron sputtering plasmas

    International Nuclear Information System (INIS)

    Andersson, Joakim; Ni, Pavel; Anders, André

    2013-01-01

    Excitation and ionization conditions in traveling ionization zones of high power impulse magnetron sputtering plasmas were investigated using fast camera imaging through interference filters. The images, taken in end-on and side-on views using light of selected gas and target atom and ion spectral lines, suggest that ionization zones are regions of enhanced densities of electrons, and excited atoms and ions. Excited atoms and ions of the target material (Al) are strongly concentrated near the target surface. Images from the highest excitation energies exhibit the most localized regions, suggesting localized Ohmic heating consistent with double layer formation

  16. DC Magnetron sputtering of Y-Ba-Cu-O thin films

    International Nuclear Information System (INIS)

    Larsson, Gunnar.

    1990-01-01

    I have been studying dc magnetron sputtering of thin film YBa 2 Cu 3 O 6+x , one of the recently discovered high- temperatures superconductors. In the introduction a brief review of the subjects sputtering and superconductivity is given. Since partial pressure measurements, especially for oxygen, have been important in the work I include a short description of the operating principles of mass spectroscopy. Experimental results in addition to what is given in the papers concerning plasma are presented in an appendix at the end of the introduction. (au)

  17. Highly -oriented growth of polycrystalline silicon films on glass by pulsed magnetron sputtering

    International Nuclear Information System (INIS)

    Reinig, P.; Selle, B.; Fenske, F.; Fuhs, W.; Alex, V.; Birkholz, M.

    2002-01-01

    Nominally undoped polycrystalline silicon (poly-Si) thin films were deposited on glass at 450 deg. C at high deposition rate (>100 nm/min) by pulsed dc magnetron sputtering. The pulse frequency was found to have a significant influence on the preferred grain orientation. The x-ray diffraction pattern exhibits a strong enhancement of the (400) reflex with increasing pulse frequency. The quantitative evaluation reveals that over 90% of the grains are oriented. The observed change in preferred grain orientation in poly-Si films at low temperatures is associated with concurrent ion bombardment of the growing film

  18. Microstructural variation in titanium oxide thin films deposited by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Pandian, Ramanathaswamy; Natarajan, Gomathi; Kamruddin, M.; Tyagi, A.K.

    2013-01-01

    We report on the microstructural evolution of titanium oxide thin films deposited by reactive DC magnetron sputtering using titanium metal target. By varying the ratio of sputter-gas mixture containing argon, oxygen and nitrogen various phases of titanium oxide, almost pure rutile, rutile-rich and anatase-rich nano-crystalline, were deposited on Si substrates at room temperature. Using high-resolution scanning electron microscopy, X-ray diffraction and micro-Raman techniques the microstructure of the films were revealed. The relationship between the microstructure of the films and the oxygen partial pressure during sputtering is discussed

  19. Applying RF Magnetron sputtering to prepare ZnO thin films and their characterization

    International Nuclear Information System (INIS)

    Saad, M.; Kassis, A.

    2009-05-01

    ZnO thin films were prepared using Rf magnetron sputtering under several preparation conditions (different values of deposition pressure, Rf power, substrate temperature). The optical properties of these films were investigated by measuring their transmission in the spectral range (300-1000 nm), and the electrical properties were investigated by measuring their electrical resistance. Results have been discussed in terms of the modified Thornton model for sputtered thin metal oxide films. Preparation conditions for depositing the highly resistive transparent i-ZnO buffer layer and the highly conducting transparent n-ZnO window layer for solar cells were proposed. (author)

  20. Recent advances in Pt coating of microspheres by a batch magnetron sputtering process

    International Nuclear Information System (INIS)

    Hsieh, E.J.; Meyer, S.F.

    1980-01-01

    Some proposed inertial confinement fusion targets require high-Z, high density metal coatings on glass microspheres. Platinum, which satisfies the high-Z and density requirements, can be coated onto microspheres with a batch magnetron sputtering process incorporating oxygen as a dopant gas to prevent the microspheres from sticking. This paper outlines recent progress in three areas: First, the coating process has been improved; second, the oxygen content and resistivity of the oxygen doped platinum films are analyzed; and third, the roles oxygen may play in reducing microsphere sticking during sputtering are discussed in regard to cold welding, Van der Waals bonding, electrostatic sticking, and sintering

  1. Post-deposition annealing effects in RF reactive magnetron sputtered indium tin oxide thin films

    Energy Technology Data Exchange (ETDEWEB)

    Martinez, M A; Herrero, J; Gutierrez, M T [Inst. de Energias Renovables (CIEMAT), Madrid (Spain)

    1992-05-01

    Indium tin oxide films have been grown by RF reactive magnetron sputtering. The influence of the deposition parameters on the properties of the films has been investigated and optimized, obtaining a value for the figure of merit of 6700 ({Omega} cm){sup -1}. As-grown indium tin oxide films were annealed in vacuum and O{sub 2} atmosphere. After these heat treatments the electro-optical properties were improved, with values for the resistivity of 1.9x10{sup -4} {Omega} cm and the figure of merit of 26700 ({Omega} cm){sup -1}. (orig.).

  2. Development of low temperature RF magnetron sputtered ITO films on flexible substrate

    Energy Technology Data Exchange (ETDEWEB)

    Muneshwar, T.P.; Varma, V.; Meshram, N; Soni, S.; Dusane, R.O. [Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Powai, Mumbai 400076 (India)

    2010-09-15

    Indium tin oxide (ITO) is one of the important materials used as transparent conducting oxide (TCO) layer in thin film solar cells, digital displays and other similar applications. For applications involving flexible polymeric substrates, it is important that deposition of ITO is carried out at near room temperature. This requirement puts constraint on stoichiometry leading to undesired electrical and optical properties. Effect of oxygen partial pressure on ITO films deposited on flexible Kapton {sup registered} by the RF magnetron sputtering is reported in this paper. (author)

  3. Magnetron deposition of metal-ceramic protective coatings on glasses of windows of space vehicles

    OpenAIRE

    Sergeev, Viktor Petrovich; Panin, Viktor Evgenyevich; Psakhie, Sergey Grigorievich; Chernyavskii, Alexandr; Svechkin, Valerii; Khristenko, Yurii; Kalashnikov, Mark Petrovich; Voronov, Andrei

    2014-01-01

    Transparent refractory metal-ceramic nanocomposite coatings with a high coefficient of elasticrecovery and microhardness on the basis of Ni/Si-Al-N are formed on a glass substrate by the pulse magnetron deposition method. The structure-phase states were investigated by TEM, SEM. It was established that the first layer consists of Ni nanograins with a fcc crystalline lattice, the second layer is two-phase: 5-10 nm nanocrystallites of the AlN phase with the hcp crystalline lattice in amorphous ...

  4. Improving the Tribological Properties of Spark-Anodized Titanium by Magnetron Sputtered Diamond-Like Carbon

    OpenAIRE

    Zhaoxiang Chen; Xipeng Ren; Limei Ren; Tengchao Wang; Xiaowen Qi; Yulin Yang

    2018-01-01

    Spark-anodization of titanium can produce adherent and wear-resistant TiO2 film on the surface, but the spark-anodized titanium has lots of surface micro-pores, resulting in an unstable and high friction coefficient against many counterparts. In this study, the diamond-like carbon (DLC) was introduced into the micro-pores of spark-anodized titanium by the magnetron sputtering technique and a TiO2/DLC composite coating was fabricated. The microstructure and tribological properties of TiO2/DLC ...

  5. Study of deposition rae coating of Ag thin films by magnetron sputtering

    International Nuclear Information System (INIS)

    Ghanati, M.; Zendehnam, A.

    2003-01-01

    Exact knowledge about deposition rate and its distribution and variation of them with respect to coating parameters (Gas pressure, Distance, discharge current,..) is very vital. In this experimental research coating of Ag thin films by magnetron sputtering have been carried out over Ar pressure range of 10 -2 -10 -1 mbar, and discharge current up to 1000 m.A, and distance between glass substrates to silver target (Cathode) was changed from 5 to 15 cm. The obtained results have been investigated by help of computer curve fitting, and these studies show a very good agreement for the conditions used in this work

  6. Nitrogen Atom Energy Distributions in a Hollow-cathode Planar Sputtering Magnetron

    International Nuclear Information System (INIS)

    Ruzic, D.N.; Goeckner, M.J.; Cohen, S.A.; Wang, Zhehui

    1999-01-01

    Energy distributions of N atoms in a hollow-cathode planar sputtering magnetron were obtained by use of optical emission spectroscopy. A characteristic line, N I 8216.3 , well-separated from molecular nitrogen emission bands, was identified. Jansson's nonlinear spectral deconvolution method, refined by minimization of χ w ampersand sup2; , was used to obtain the optimal deconvolved spectra. These showed nitrogen atom energies from 1 eV to beyond 500 eV. Based on comparisons with VFTRIM results, we propose that the energetic N atoms are generated from N 2 + ions after these ions are accelerated through the sheath and dissociatively reflect from the cathode

  7. Venting temperature determines surface chemistry of magnetron sputtered TiN films

    Energy Technology Data Exchange (ETDEWEB)

    Greczynski, G. [Thin Film Physics Division, Department of Physics (IFM), Linköping University, SE-581 83 Linköping (Sweden); Materials Chemistry, RWTH Aachen University, Kopernikusstr. 10, D-52074 Aachen (Germany); Mráz, S.; Schneider, J. M. [Materials Chemistry, RWTH Aachen University, Kopernikusstr. 10, D-52074 Aachen (Germany); Hultman, L. [Thin Film Physics Division, Department of Physics (IFM), Linköping University, SE-581 83 Linköping (Sweden)

    2016-01-25

    Surface properties of refractory ceramic transition metal nitride thin films grown by magnetron sputtering are essential for resistance towards oxidation necessary in all modern applications. Here, typically neglected factors, including exposure to residual process gases following the growth and the venting temperature T{sub v}, each affecting the surface chemistry, are addressed. It is demonstrated for the TiN model materials system that T{sub v} has a substantial effect on the composition and thickness-evolution of the reacted surface layer and should therefore be reported. The phenomena are also shown to have impact on the reliable surface characterization by x-ray photoelectron spectroscopy.

  8. [Effect of niobium nitride on the bonding strength of titanium porcelain by magnetron sputtering].

    Science.gov (United States)

    Wang, Shu-shu; Zhang, La-bao; Guang, Han-bing; Zhou, Shu; Zhang, Fei-min

    2010-05-01

    To investigate the effect of magnetron sputtered niobium nitride (NbN) on the bonding strength of commercially pure cast titanium (Ti) and low-fusing porcelain (Ti/Vita titankeramik system). Sixty Ti specimens were randomly divided into four groups, group T1, T2, T3 and T4. All specimens of group T1 and T2 were first treated with 120 microm blasted Al2O3 particles, and then only specimens of group T2 were treated with magnetron sputtered NbN film. All specimens of group T3 and T4 were first treated with magnetron sputtered NbN film and then only specimens of group T4 were treated with 120 microm blasted Al2O3 particles. The composition of the deposits were analyzed by X-ray diffraction (XRD). A universal testing machine was used to perform the three-point bending test to evaluate the bonding strength of Ti and porcelain. The microstructure of NbN, the interface of Ti-porcelain and the fractured Ti surface were observed with scanning electron microscopy (SEM) and energy depressive spectrum (EDS), and the results were compared. The XRD results showed that the NbN deposits were cubic crystalline phases. The bonding strength of Ti and porcelain in T1 to T4 group were (27.2+/-0.8), (43.1+/-0.6), (31.4+/-1.0) and (44.9+/-0.6) MPa. These results were analyzed by one-way analysis of variance and differences between groups were compared using least significant difference test. Significant inter-group differences were found among all groups (Pporcelain, while samples treated with both Al2O3 and NbN had better bond. EDS of Ti-porcelain interface showed oxidation occurred in T1, T2 and T3, but was well controlled in T4. Magnetron sputtered NbN can prevent Ti from being oxidized, and can improve the bonding strength of Ti/Vita titankeramik system. Al2O3 blast can also improve the bonding strength of Ti/Vita titankeramik system.

  9. Domino Platform: PVD Coaters for Arc Evaporation and High Current Pulsed Magnetron Sputtering

    International Nuclear Information System (INIS)

    Vetter, J; Müller, J; Erkens, G

    2012-01-01

    AlTiN and CrN coatings were deposited in hybrid DOMINO platforms by magnetron sputtering (DC-MS, DC-MS+HCP-MS, HCP-MS) and vacuum arc evaporation. The ion cleaning was done by the AEGD process. The coating rates and the energy efficiency of both deposition processes were compared. The roughness effects of the different coating types were discussed. Preliminary results of the change of pulse characteristics during simultaneously running of HCP-MS plus vacuum arc evaporation are shown.

  10. Effect of residual gas on structural, electrical and mechanical properties of niobium films deposited by magnetron sputtering deposition

    Science.gov (United States)

    Wang, Lanruo; Zhong, Yuan; Li, Jinjin; Cao, Wenhui; Zhong, Qing; Wang, Xueshen; Li, Xu

    2018-04-01

    Magnetron sputtering is an important method in the superconducting thin films deposition. The residual gas inside the vacuum chamber will directly affect the quality of the superconducting films. In this paper, niobium films are deposited by magnetron sputtering under different chamber residual gas conditions. The influence of baking and sputtering process on residual gas are studied as well. Surface morphology, electrical and mechanical properties of the films are analysed. The residual gas analysis result before the sputtering process could be regarded as a reference condition to achieve high quality superconducting thin films.

  11. A novel hetero-material gate-underlap electrically doped TFET for improving DC/RF and ambipolar behaviour

    Science.gov (United States)

    Yadav, Shivendra; Sharma, Dheeraj; Chandan, Bandi Venkata; Aslam, Mohd; Soni, Deepak; Sharma, Neeraj

    2018-05-01

    In this article, the impact of gate-underlap with hetero material (low band gap) has been investigated in terms of DC and Analog/RF parameters by proposed device named as hetero material gate-underlap electrically doped TFET (HM-GUL-ED-TFET). Gate-underlap resolves the problem of ambipolarity, gate leakage current (Ig) and slightly improves the gate to drain capacitance, but DC performance is almost unaffected. Further, the use of low band gap material (Si0.5 Ge) in proposed device causes a drastic improvement in the DC as well as RF figures of merit. We have investigated the Si0.5 Ge as a suitable candidate among different low band gap materials. In addition, the sensitivity of gate-underlap in terms of gate to drain inversion and parasitic capacitances has been studied for HM-GUL-ED-TFET. Further, relatively it is observed that gate-underlap is a better way than drain-underlap in the proposed structure to improve Analog/RF performances without degrading the DC parameters of device. Additionally, hetero-junction alignment analysis has been done for fabrication feasibility.

  12. Deposition Rates of High Power Impulse Magnetron Sputtering: Physics and Economics

    Energy Technology Data Exchange (ETDEWEB)

    Anders, Andre

    2009-11-22

    Deposition by high power impulse magnetron sputtering (HIPIMS) is considered by some as the new paradigm of advanced sputtering technology, yet this is met with skepticism by others for the reported lower deposition rates, if compared to rates of more conventional sputtering of equal average power. In this contribution, the underlying physical reasons for the rate changes are discussed, including (i) ion return to the target and self-sputtering, (ii) the less-than-linear increase of the sputtering yield with increasing ion energy, (iii) yield changes due to the shift of species responsible for sputtering, (iv) changes to due to greater film density, limited sticking, and self-sputtering on the substrate, (v) noticeable power losses in the switch module, (vi) changes of the magnetic balance and particle confinement of the magnetron due to self-fields at high current, and (vii) superposition of sputtering and sublimation/evaporation for selected materials. The situation is even more complicated for reactive systems where the target surface chemistry is a function of the reactive gas partial pressure and discharge conditions. While most of these factors imply a reduction of the normalized deposition rate, increased rates have been reported for certain conditions using hot targets and less poisoned targets. Finally, some points of economics and HIPIMS benefits considered.

  13. Heating of polymer substrate by discharge plasma in radiofrequency magnetron sputtering deposition

    International Nuclear Information System (INIS)

    Sirghi, Lucel; Popa, Gheorghe; Hatanaka, Yoshinori

    2006-01-01

    The substrate used for the thin film deposition in a radiofrequency magnetron sputtering deposition system is heated by the deposition plasma. This may change drastically the surface properties of the polymer substrates. Deposition of titanium dioxide thin films on polymethyl methacrylate and polycarbonate substrates resulted in buckling of the substrate surfaces. This effect was evaluated by analysis of atomic force microscopy topography images of the deposited films. The amount of energy received by the substrate surface during the film deposition was determined by a thermal probe. Then, the results of the thermal probe measurements were used to compute the surface temperature of the polymer substrate. The computation revealed that the substrate surface temperature depends on the substrate thickness, discharge power and substrate holder temperature. For the case of the TiO 2 film depositions in the radiofrequency magnetron plasma, the computation indicated substrate surface temperature values under the polymer melting temperature. Therefore, the buckling of polymer substrate surface in the deposition plasma may not be regarded as a temperature driven surface instability, but more as an effect of argon ion bombardment

  14. Microstructural control of TiC/a-C nanocomposite coatings with pulsed magnetron sputtering

    International Nuclear Information System (INIS)

    Pei, Y.T.; Chen, C.Q.; Shaha, K.P.; De Hosson, J.Th.M.; Bradley, J.W.; Voronin, S.A.; Cada, M.

    2008-01-01

    In this paper, we report some striking results on the microstructural control of TiC/a-C nanocomposite coatings with pulsed direct current (DC) magnetron sputtering. The interface morphology and microstructure evolution as a function of pulse frequency and duty cycle were scrutinized using atomic force microscopy, scanning electron microscopy and high-resolution transmission electron microscopy techniques. It is shown that, with increasing pulse frequency, the nanocomposite coatings exhibit evolutions in morphology of the growing interface from rough to smooth and in the microstructure from strongly columnar to fully columnar-free. In addition, the smoothly growing interface favors the formation of a tailor-made multilayered nanocomposite structure. The fundamental mechanisms are analyzed with the assistance of plasma diagnostic experiments. Ion mass/energy spectrometry measurements reveal that, depending on the frequency and duty cycle of DC pulses, pulsing of the magnetrons can control the flux and energy distribution of Ar + ions over a very broad range for concurrent impingement on the growing interface of deposited coatings, in comparison with DC sputtering. The significantly enhanced energy flux density is thought to be responsible for the 'adatom transfer' in interface smoothening and thus the restraint of columnar growth

  15. Composite Ag/C:H:N films prepared by planar magnetron deposition

    Energy Technology Data Exchange (ETDEWEB)

    Hlidek, P. [Charles University, Faculty of Mathematics and Physics, Praha (Czech Republic)], E-mail: hlidek@karlov.mff.cuni.cz; Hanus, J.; Biederman, H.; Slavinska, D.; Pesicka, J. [Charles University, Faculty of Mathematics and Physics, Praha (Czech Republic)

    2008-05-30

    Composite Ag/C:H:N films were deposited by means of an unbalanced magnetron operated in a gas mixture of nitrogen and n-hexane. Composition of the films was controlled by electric power delivered to the magnetron and by ratio of nitrogen and n-hexane in the working gas mixture. The films were characterized using transmission electron microscopy, by the absorption spectra in visible and near infrared regions and by Fourier transform infrared spectroscopy. Immediately after film deposition and without breaking vacuum (in situ) corresponding vibration infrared spectra were scanned and their evolution during ageing of the films was monitored. Wettability as determined from water contact angle was improved with raising nitrogen contents, i.e. with increasing the electric power and the ratio of nitrogen/n-hexane in the working gas mixture. The increased wettability is likely caused by presence of NH{sub x} groups in Ag/C:H:N films. The incorporation of nitrogen effectively prevents the formation of carboxylate groups on the silver inclusions surfaces during the aging in the open air. In addition, the oxidation mechanism of the polymer matrix is modified.

  16. Deposition of Al/Cu Multilayer By Double Targets Cylindrical DC Magnetron Sputtering System

    Directory of Open Access Journals (Sweden)

    P. Balashabadi

    2013-12-01

    Full Text Available A cylindrical direct current magnetron sputtering coater with two targets for deposition of multilayer thin films and cermet solar selective surfaces has been constructed. The substrate holder was able to rotate around the target for obtaining the uniform layer and separated multilayer phases. The Al/ Cu multilayer film was deposited on the glass substrate at the following conditions: Working gas = Pure argon, Working pressure = 1 Pa, Cathode current = 8 A and cathode voltage = -600 V .Microstructure of the film was investigated by X-Ray Diffraction and the scanning electron microscopy analyses. The elements profile was determined by glow discharge–optical emission spectroscopy analysis. During deposition, both targets with magnetron configuration were sputtered simultaneously by argon ions. A Plasma column on the targets surface was generated by a 290 G permanent magnet unit. Two DC power supply units with three phases input and maximum output of 12 A/1000V were used to deposit the multilayer thin films. A control phase system was used to adjust output voltage.

  17. Properties of nickel films growth by radio frequency magnetron sputtering at elevated substrate temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Muslim, Noormariah, E-mail: 14h8702@ubd.edu.bn [Centre for Advanced Material and Energy Sciences, Universiti Brunei Darussalam, Jalan Tungku Link, Gadong BE1410 (Brunei Darussalam); Soon, Ying Woan [Centre for Advanced Material and Energy Sciences, Universiti Brunei Darussalam, Jalan Tungku Link, Gadong BE1410 (Brunei Darussalam); Physical and Geological Sciences, Faculty of Science, Universiti Brunei Darussalam, Jalan Tungku Link, Gadong BE1410 (Brunei Darussalam); Lim, Chee Ming; Voo, Nyuk Yoong [Centre for Advanced Material and Energy Sciences, Universiti Brunei Darussalam, Jalan Tungku Link, Gadong BE1410 (Brunei Darussalam)

    2016-08-01

    Pure nickel (Ni) thin films of thicknesses of 100 nm were deposited on glass substrates by radio frequency magnetron sputtering at a power of 100 W and at various substrate temperatures i.e., room temperature, 100, 200, and 300 °C. The crystalline structure, surface topography, surface morphology, electrical resistivity, and optical properties of the deposited films were studied. The properties of the Ni films could be controlled by altering the substrate temperature. Specifically, the films featured a face-centered cubic crystalline structure with predominant (111) crystallite orientation at all the substrate temperatures employed, as observed from the X-ray diffraction analysis. Films deposited at substrate temperatures greater than 200 °C additionally displayed crystalline (200) and (220) diffraction peaks. The surface morphology analysis revealed that the grain size of the Ni thin films increased with increasing substrate temperatures employed. This increase was accompanied with a decrease in the resistivity of the Ni films. The surface roughness of the films increased with increasing substrate temperatures employed, as observed from the atomic force microscopy analysis. - Highlights: • RF magnetron sputtering is a good alternative method to deposit Ni films. • Properties of Ni films could be controlled simply by tuning substrate temperatures. • Crystallite size and surface roughness increased with substrate temperatures. • Electrical resistivity reduced with increasing substrate temperatures. • Optical properties also changed with substrate temperatures.

  18. Urea impedimetric biosensor based on reactive RF magnetron sputtered zinc oxide nanoporous transducer

    International Nuclear Information System (INIS)

    Mozaffari, Sayed Ahmad; Rahmanian, Reza; Abedi, Mohammad; Amoli, Hossein Salar

    2014-01-01

    Graphical abstract: - Highlights: • Application and optimization of reactive RF magnetron sputtering for homogeneous nanoporous ZnO thin film formation. • Exploiting nanoporous ZnO thin film as a good porous framework with large surface area/volume for having stable immobilized enzyme with minimum loss of activity. • Application of impedimetric assessment for urea biosensing due to its rapidity, sensitivity, and repeatability. - Abstract: Uniform sputtered nanoporous zinc oxide (Nano-ZnO) thin film on the conductive fluorinated-tin oxide (FTO) layer was applied to immobilize urease enzyme (Urs) for urea detection. Highly uniform nanoporous ZnO thin film were obtained by reactive radio frequency (RF) magnetron sputtering system at the optimized instrumental deposition conditions. Characterization of the surface morphology and roughness of ZnO thin film by field emission-scanning electron microscopy (FE-SEM) exhibits cavities of nanoporous film as an effective biosensing area for enzyme immobilization. Step by step monitoring of FTO/Nano-ZnO/Urs biosensor fabrication were performed using electrochemical methods such as cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) techniques. Fabricated FTO/Nano-ZnO/Urs biosensor was used for urea determination using EIS experiments. The impedimetric results show high sensitivity for urea detection within 0.83–23.24 mM and limit of detection as 0.40 mM

  19. Surface functionalization of nanostructured LaB{sub 6}-coated Poly Trilobal fabric by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Yan, E-mail: wuyanchn@hotmail.com [Mechanical and Electrical Engineering Branch, Jiaxing Nanyang Polytechnic Institute, Jiaxing 314003 (China); Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Zhang, Lin, E-mail: zhanglin2007@sdu.edu.cn [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Min, Guanghui, E-mail: ghmin@sdu.edu.cn [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Yu, Huashun; Gao, Binghuan; Liu, Huihui; Xing, Shilong; Pang, Tao [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China)

    2016-10-30

    Highlights: • Nanostructured LaB{sub 6} films were deposited on flexible textile substrates by dc magnetron sputtering. • The pronounced influence of the working pressure on the morphologies and optical properties of LaB{sub 6} films has been revealed. • The concept of Ultraviolet Protection Factor (UPF) was employed and LaB{sub 6}-coated PET textiles with ultraviolet protection ability were obtained. - Abstract: Nanostructured LaB{sub 6} films were deposited on flexible Poly Trilobal substrates (PET textiles) through direct current magnetron sputtering in order to broaden its applications and realize surface functionalization of polyester fabrics. Characterizations and performances were investigated by employing a scanning electron microscope (SEM), Fourier transformation infrared spectroscopy (FT-IR) and ultraviolet-visible (UV–vis) spectrophotometer. Ultraviolet Protection Factor (UPF) conducted by the integral conversion was employed to measure the ultraviolet protection ability. As expected, the growth of LaB{sub 6} film depending on the pressure variation enhanced UV-blocking ability (UPF rating at 30.17) and absorption intensity of the textiles.

  20. Study on the preparation of boron-rich film by magnetron sputtering in oxygen atmosphere

    Energy Technology Data Exchange (ETDEWEB)

    Pan, Zhangmin; Yang, Yiming; Huang, Jian; Ren, Bing; Yu, Hongze; Xu, Run; Ji, Huanhuan; Wang, Lin; Wang, Linjun, E-mail: ljwang@shu.edu.cn

    2016-12-01

    Highlights: • Boron ({sup 10}B) oxide films were successfully grown using RF magnetron sputtering. • Effects of oxygen partial pressure on the property of the films were studied. • Substrates were covered with B-rich film and film surface was covered with B{sub 2}O{sub 3}. • The growth mechanism of films in oxygen atmosphere was analyzed using XPS. - Abstract: In this paper, the growth of boron ({sup 10}B) oxide films on (1 0 0) silicon substrate were achieved by radio frequency (r.f.) magnetron sputtering under the different oxygen partial pressure with a target of boron and boron oxide. The structure and properties of deposited films were characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy spectrometer (FTIR), X-ray photoelectron spectroscopy (XPS), respectively. The results showed that the substrate was covered with boron-rich films tightly and the surface of films was covered with B{sub 2}O{sub 3}. And the growth mechanism of boron-rich film in oxygen atmosphere was also analyzed.

  1. ZrN coatings deposited by high power impulse magnetron sputtering and cathodic arc techniques

    Energy Technology Data Exchange (ETDEWEB)

    Purandare, Yashodhan, E-mail: Y.Purandare@shu.ac.uk; Ehiasarian, Arutiun; Hovsepian, Papken [Nanotechnology Centre for PVD Research, Materials and Engineering Research Institute, Sheffield Hallam University, Sheffield S1 1WB (United Kingdom); Santana, Antonio [Ionbond AG Olten, Industriestrasse 211, CH-4600 Olten (Switzerland)

    2014-05-15

    Zirconium nitride (ZrN) coatings were deposited on 1 μm finish high speed steel and 316L stainless steel test coupons. Cathodic Arc (CA) and High Power Impulse Magnetron Sputtering (HIPIMS) + Unbalanced Magnetron Sputtering (UBM) techniques were utilized to deposit coatings. CA plasmas are known to be rich in metal and gas ions of the depositing species as well as macroparticles (droplets) emitted from the arc sports. Combining HIPIMS technique with UBM in the same deposition process facilitated increased ion bombardment on the depositing species during coating growth maintaining high deposition rate. Prior to coating deposition, substrates were pretreated with Zr{sup +} rich plasma, for both arc deposited and HIPIMS deposited coatings, which led to a very high scratch adhesion value (L{sub C2}) of 100 N. Characterization results revealed the overall thickness of the coatings in the range of 2.5 μm with hardness in the range of 30–40 GPa depending on the deposition technique. Cross-sectional transmission electron microscopy and tribological experiments such as dry sliding wear tests and corrosion studies have been utilized to study the effects of ion bombardment on the structure and properties of these coatings. In all the cases, HIPIMS assisted UBM deposited coating fared equal or better than the arc deposited coatings, the reasons being discussed in this paper. Thus H+U coatings provide a good alternative to arc deposited where smooth, dense coatings are required and macrodroplets cannot be tolerated.

  2. RF Magnetron Sputtering Coating Of Hydroxyapatite On Alkali Solution Treated Titanate Nanorods

    Directory of Open Access Journals (Sweden)

    Lee K.

    2015-06-01

    Full Text Available Hydroxyapatite (HA is a material with outstanding biocompatibility. It is chemically similar to natural bone tissue, and has therefore been favored for use as a coating material for dental and orthopedic implants. In this study, RF magnetron sputtering was applied for HA coating. And Alkali treatment was performed in a 5 M NaOH solution at 60°C. The coated HA thin film was heat-treated at a range of temperatures from 300 to 600°C. The morphological characterization and crystal structures of the coated specimens were then obtained via FE-SEM, XRD, and FT-IR. The amorphous thin film obtained on hydrothermally treated nanorods transformed into a crystalline thin film after the heat treatment. The change in the phase transformation, with an enhanced crystallinity, showed a reduced wettability. The hydrothermally treated nanorods with an amorphous thin film, on the other hand, showed an outstanding wettability. The HA thin film perpendicularly coated the nanorods in the upper and inner parts via RF magnetron sputtering, and the FT-IR results confirmed that the molecular bonding of the coated film had an HA structure.

  3. Indium zinc oxide films deposited on PET by LF magnetron sputtering

    International Nuclear Information System (INIS)

    Kim, Eun Lyoung; Jung, Sang Kooun; Sohn, Sang Ho; Park, Duck Kyu

    2007-01-01

    Indium zinc oxide (IZO) has attracted much attention recently for use in transparent oxide films compared with the ITO film. We carried out the deposition of IZO on a polyethylene terapthalate (PET) substrate at room temperature by a low-frequency (LF) magnetron sputtering system. These films have amorphous structures with excellent electrical stability, surface uniformity and high optical transmittance. The effects of LF applied voltage and O 2 flow rate were investigated. The electrical and optical properties were studied. At optimal deposition conditions, thin films of IZO with a sheet resistance of 32 Ω/sq and an optical transmittance of over 80% in the visible spectrum range were achieved. The IZO thin films fabricated by this method do not require substrate heating during the film preparation of any additional post-deposition annealing treatment. The experimental results show that films with good qualities of surface morphology, transmittance and electrical conduction can be grown by the LF magnetron sputtering method on PET which is recommendable

  4. Tribological properties, corrosion resistance and biocompatibility of magnetron sputtered titanium-amorphous carbon coatings

    Science.gov (United States)

    Dhandapani, Vishnu Shankar; Subbiah, Ramesh; Thangavel, Elangovan; Arumugam, Madhankumar; Park, Kwideok; Gasem, Zuhair M.; Veeraragavan, Veeravazhuthi; Kim, Dae-Eun

    2016-05-01

    Amorphous carbon incorporated with titanium (a-C:Ti) was coated on 316L stainless steel (SS) by magnetron sputtering technique to attain superior tribological properties, corrosion resistance and biocompatibility. The morphology, topography and functional groups of the nanostructured a-C:Ti coatings in various concentrations were analyzed using atomic force microscopy (AFM), Raman, X-Ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Raman and XPS analyses confirmed the increase in sp2 bonds with increasing titanium content in the a-C matrix. TEM analysis confirmed the composite nature of the coating and the presence of nanostructured TiC for Ti content of 2.33 at.%. This coating showed superior tribological properties compared to the other a-C:Ti coatings. Furthermore, electrochemical corrosion studies were performed against stimulated body fluid medium in which all the a-C:Ti coatings showed improved corrosion resistance than the pure a-C coating. Preosteoblasts proliferation and viability on the specimens were tested and the results showed that a-C:Ti coatings with relatively high Ti (3.77 at.%) content had better biocompatibility. Based on the results of this work, highly durable coatings with good biocompatibility could be achieved by incorporation of optimum amount of Ti in a-C coatings deposited on SS by magnetron sputtering technique.

  5. Structure and morphology of magnetron sputter deposited ultrathin ZnO films on confined polymeric template

    Science.gov (United States)

    Singh, Ajaib; Schipmann, Susanne; Mathur, Aakash; Pal, Dipayan; Sengupta, Amartya; Klemradt, Uwe; Chattopadhyay, Sudeshna

    2017-08-01

    The structure and morphology of ultra-thin zinc oxide (ZnO) films with different film thicknesses on confined polymer template were studied through X-ray reflectivity (XRR) and grazing incidence small angle X-ray scattering (GISAXS). Using magnetron sputter deposition technique ZnO thin films with different film thicknesses (weight of polystyrene). The detailed internal structure, along the surface/interfaces and the growth direction of the system were explored in this study, which provides insight into the growth procedure of ZnO on confined polymer and reveals that a thin layer of ZnO, with very low surface and interface roughness, can be grown by DC magnetron sputtering technique, with approximately full coverage (with bulk like electron density) even in nm order of thickness, in 2-7 nm range on confined polymer template, without disturbing the structure of the underneath template. The resulting ZnO-polystyrene hybrid systems show strong ZnO near band edge (NBE) and deep-level (DLE) emissions in their room temperature photoluminescence spectra, where the contribution of DLE gets relatively stronger with decreasing ZnO film thickness, indicating a significant enhancement of surface defects because of the greater surface to volume ratio in thinner films.

  6. Microstructure and electrical properties of bismuth and bismuth oxide deposited by magnetron sputtering UBM

    International Nuclear Information System (INIS)

    Otalora B, D. M.; Dussan, A.; Olaya F, J. J.

    2015-01-01

    In this work, bismuth (Bi) and bismuth oxide (Bi 2 O 3 ) thin films were prepared, at room temperature, by Sputtering Unbalanced Magnetron (UBM - Unbalance Magnetron) technique under glass substrates. Microstructural and electrical properties of the samples were studied by X-ray diffraction (XRD) and System for Measuring Physical Properties - PPMS (Physical Property Measurement System). Dark resistivity of the material was measured for a temperature range between 100 and 400 K. From the XRD measurements it was observed a polycrystalline character of the Bi associated to the presence of phases above the main peak, 2θ = 26.42 grades and a growth governed by a rhombohedral structure. Crystal parameters were obtained for both compounds, Bi and Bi 2 O 3 . From the analysis of the spectra of the conductivity as a function of temperature, it was established that the transport mechanism that governs the region of high temperature (T>300 K) is thermally activated carriers. From conductivity measurements the activation energies were obtained of 0.0094 eV and 0.015 eV for Bi 2 O 3 and Bi, respectively. (Author)

  7. Electrical and Optical Properties of Fluorine Doped Tin Oxide Thin Films Prepared by Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Ziad Y. Banyamin

    2014-10-01

    Full Text Available Fluorine doped tin oxide (FTO coatings have been prepared using the mid-frequency pulsed DC closed field unbalanced magnetron sputtering technique in an Ar/O2 atmosphere using blends of tin oxide and tin fluoride powder formed into targets. FTO coatings were deposited with a thickness of 400 nm on glass substrates. No post-deposition annealing treatments were carried out. The effects of the chemical composition on the structural (phase, grain size, optical (transmission, optical band-gap and electrical (resistivity, charge carrier, mobility properties of the thin films were investigated. Depositing FTO by magnetron sputtering is an environmentally friendly technique and the use of loosely packed blended powder targets gives an efficient means of screening candidate compositions, which also provides a low cost operation. The best film characteristics were achieved using a mass ratio of 12% SnF2 to 88% SnO2 in the target. The thin film produced was polycrystalline with a tetragonal crystal structure. The optimized conditions resulted in a thin film with average visible transmittance of 83% and optical band-gap of 3.80 eV, resistivity of 6.71 × 10−3 Ω·cm, a carrier concentration (Nd of 1.46 × 1020 cm−3 and a mobility of 15 cm2/Vs.

  8. Type II textured molybdenum disulphide films produced by direct vapour transport and rf-magnetron sputtering

    International Nuclear Information System (INIS)

    Bohlken, S.F.; Lemon, K.D.; Jakovidis, G.; Taheri, E.H.

    1999-01-01

    Full text: Molybdenum disulphide (MoS 2 ) is one of the few naturally occurring Layered Transition Metal Dichalcogenides and is the primary source for elemental molybdenum. It displays exceptional lubrication performance in both vacuum and atmospheric conditions over a wide temperature range. An important emerging application of MoS 2 and related materials is photovoltaics. Films of MoS 2 exhibit several morphologies described by the orientation of platelets with respect to the substrate. Films with platelets perpendicular or parallel to the substrate are referred to by their morphology, which is type-I or type-II respectively. Production of exclusive type-II films is highly desirable in applications involving lubrication and photovoltaics. For example, type-II morphology reduces friction and minority carrier recombination centres, thus improving tribological and photovoltaic performance. We have successfully produced type-II films using both direct vapour transport and rf-magnetron sputtering Continuous polycrystalline films (∼ 10 μm thick) grown in our laboratory using vapour transport have typical areas 1000 mm 2 . A novel ejecta filtration technique was applied to rf-magnetron sputtering. Films produced using this approach retain exclusive type-II morphology at thicknesses where type-I would normally be observed (∼ 200nm)

  9. Deposition rates of high power impulse magnetron sputtering: Physics and economics

    International Nuclear Information System (INIS)

    Anders, Andre

    2010-01-01

    Deposition by high power impulse magnetron sputtering (HIPIMS) is considered by some as the new paradigm of advanced sputtering technology, yet this is met with skepticism by others for the reported lower deposition rates, if compared to rates of more conventional sputtering of equal average power. In this contribution, the underlying physical reasons for the rate changes are discussed, including (i) ion return to the target and self-sputtering, (ii) the less-than-linear increase in the sputtering yield with increasing ion energy, (iii) yield changes due to the shift of species responsible for sputtering, (iv) changes due to greater film density, limited sticking, and self-sputtering on the substrate, (v) noticeable power losses in the switch module, (vi) changes in the magnetic balance and particle confinement of the magnetron due to self-fields at high current, and (vii) superposition of sputtering and sublimation/evaporation for selected materials. The situation is even more complicated for reactive systems where the target surface chemistry is a function of the reactive gas partial pressure and discharge conditions. While most of these factors imply a reduction in the normalized deposition rate, increased rates have been reported for certain conditions using hot targets and less poisoned targets. Finally, some points of economics and HIPIMS benefits are considered.

  10. Composite SiOx/hydrocarbon plasma polymer films prepared by RF magnetron sputtering of SiO2 and polyimide

    Czech Academy of Sciences Publication Activity Database

    Drabik, M.; Kousal, J.; Pinosh, Y.; Choukourov, A.; Biederman, H.; Slavínská, D.; Macková, Anna; Boldyryeva, Hanna; Pešička, J.

    2007-01-01

    Roč. 81, č. 7 (2007), s. 920-927 ISSN 0042-207X Institutional research plan: CEZ:AV0Z10480505 Keywords : composite films * magnetron * sputtering * polyimide * SiO2 Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 0.881, year: 2007

  11. Comparative analysis of electrophysical properties of ceramic tantalum pentoxide coatings, deposited by electron beam evaporation and magnetron sputtering methods

    Science.gov (United States)

    Donkov, N.; Mateev, E.; Safonov, V.; Zykova, A.; Yakovin, S.; Kolesnikov, D.; Sudzhanskaya, I.; Goncharov, I.; Georgieva, V.

    2014-12-01

    Ta2O5 ceramic coatings have been deposited on glass substrates by e-beam evaporation and magnetron sputtering methods. For the magnetron sputtering process Ta target was used. X-ray diffraction measurements show that these coatings are amorphous. XPS survey spectra of the ceramic Ta2O5 coatings were obtained. All spectra consist of well-defined XPS lines of Ta 4f, 4d, 4p and 4s; O 1s; C 1s. Ta 4f doublets are typical for Ta2O5 coatings with two main peaks. Scanning electron microscopy and atomic force microscopy images of the e-beam evaporated and magnetron sputtered Ta2O5 ceramic coatings have revealed a relatively flat surface with no cracks. The dielectric properties of the tantalum pentoxide coatings have been investigated in the frequency range of 100 Hz to 1 MHz. The electrical behaviour of e-beam evaporated and magnetron sputtered Ta2O5 ceramic coatings have also been compared. The deposition process conditions principally effect the structure parameters and electrical properties of Ta2O5 ceramic coatings. The coatings deposited by different methods demonstrate the range of dielectric parameters due to the structural and stoichiometric composition changes

  12. Experimental study on an S-band near-field microwave magnetron power transmission system on hundred-watt level

    Science.gov (United States)

    Zhang, Biao; Jiang, Wan; Yang, Yang; Yu, Chengyang; Huang, Kama; Liu, Changjun

    2015-11-01

    A multi-magnetron microwave source, a metamaterial transmitting antenna, and a large power rectenna array are presented to build a near-field 2.45 GHz microwave power transmission system. The square 1 m2 rectenna array consists of sixteen rectennas with 2048 Schottky diodes for large power microwave rectifying. It receives microwave power and converts them into DC power. The design, structure, and measured performance of a unit rectenna as well as the entail rectenna array are presented in detail. The multi-magnetron microwave power source switches between half and full output power levels, i.e. the half-wave and full-wave modes. The transmission antenna is formed by a double-layer metallic hole array, which is applied to combine the output power of each magnetron. The rectenna array DC output power reaches 67.3 W on a 1.2 Ω DC load at a distance of 5.5 m from the transmission antenna. DC output power is affected by the distance, DC load, and the mode of microwave power source. It shows that conventional low power Schottky diodes can be applied to a microwave power transmission system with simple magnetrons to realise large power microwave rectifying.

  13. Depth profile analyses of nc-TiC/a-C:H coating prepared by balanced magnetron sputtering

    Czech Academy of Sciences Publication Activity Database

    Vašina, P.; Souček, P.; Schmidtová, T.; Eliáš, M.; Buršíková, V.; Jílek, M.; Jílek Jr., M.; Schäfer, C.; Buršík, Jiří

    2011-01-01

    Roč. 205, Suppl. 2 (2011), S53-S56 ISSN 0257-8972 Institutional research plan: CEZ:AV0Z20410507 Keywords : composite * mechanical properties * magnetron Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 1.867, year: 2011

  14. Combined optical emission and resonant absorption diagnostics of an Ar-O{sub 2}-Ce-reactive magnetron sputtering discharge

    Energy Technology Data Exchange (ETDEWEB)

    El Mel, A.A. [Chimie des Interactions Plasma-Surface (ChIPS), Research Institute for Materials Science and Engineering, Université de Mons, Place du Parc 23, Mons B-7000 (Belgium); Institut des Matériaux Jean Rouxel, Université de Nantes, CNRS, 2 rue de la Houssinière B.P. 32229, Nantes Cedex 3 44322 (France); Ershov, S. [Chimie des Interactions Plasma-Surface (ChIPS), Research Institute for Materials Science and Engineering, Université de Mons, Place du Parc 23, Mons B-7000 (Belgium); Britun, N., E-mail: nikolay.britun@umons.ac.be [Chimie des Interactions Plasma-Surface (ChIPS), Research Institute for Materials Science and Engineering, Université de Mons, Place du Parc 23, Mons B-7000 (Belgium); Ricard, A. [Université de Toulouse, UPS, INPT, LAPLACE (Laboratoire Plasma et Conversion d' Energie), 118 route de Narbonne, Toulouse Cedex 9 F-31062 (France); Konstantinidis, S. [Chimie des Interactions Plasma-Surface (ChIPS), Research Institute for Materials Science and Engineering, Université de Mons, Place du Parc 23, Mons B-7000 (Belgium); Snyders, R. [Chimie des Interactions Plasma-Surface (ChIPS), Research Institute for Materials Science and Engineering, Université de Mons, Place du Parc 23, Mons B-7000 (Belgium); Materia Nova Research Center, Parc Initialis, Avenue Copernic 1, Mons B-7000 (Belgium)

    2015-01-01

    We report the results on combined optical characterization of Ar-O{sub 2}-Ce magnetron sputtering discharges by optical emission and resonant absorption spectroscopy. In this study, a DC magnetron sputtering system equipped with a movable planar magnetron source with a Ce target is used. The intensities of Ar, O, and Ce emission lines, as well as the absolute densities of Ar metastable and Ce ground state atoms are analyzed as a function of the distance from the magnetron target, applied DC power, O{sub 2} content, etc. The absolute number density of the Ar{sup m} is found to decrease exponentially as a function of the target-to-substrate distance. The rate of this decrease is dependent on the sputtering regime, which should be due to the different collisional quenching rates of Ar{sup m} by O{sub 2} molecules at different oxygen contents. Quantitatively, the absolute number density of Ar{sup m} is found to be equal to ≈ 3 × 10{sup 8} cm{sup −3} in the metallic, and ≈ 5 × 10{sup 7} cm{sup −3} in the oxidized regime of sputtering, whereas Ce ground state densities at the similar conditions are found to be few times lower. The absolute densities of species are consistent with the corresponding deposition rates, which decrease sharply during the transition from metallic to poisoned sputtering regime. - Highlights: • Optical emission and resonant absorption spectroscopy are employed to study Ar-O{sub 2}-Ce magnetron sputtering discharges. • The density of argon metastables is found to decrease exponentially when increasing the target-to-substrate distance. • The collision-quenching rates of Ar{sup m} by O{sub 2} molecules at different oxygen contents is demonstrated. • The deposition rates of cerium and cerium oxide thin films decrease sharply during the transition from the metallic to the poisoned sputtering regime.

  15. Antibacterial properties of nano-silver coated PEEK prepared through magnetron sputtering.

    Science.gov (United States)

    Liu, Xiuju; Gan, Kang; Liu, Hong; Song, Xiaoqing; Chen, Tianjie; Liu, Chenchen

    2017-09-01

    We aimed to investigate the cytotoxicity and antibacterial properties of nano-silver-coated polyetheretherketone (PEEK) produced through magnetron sputtering and provide a theoretical basis for its use in clinical applications. The surfaces of PEEKs were coated with nano-silver at varying thicknesses (3, 6, 9, and 12nm) through magnetron sputtering technology. The resulting coated PEEK samples were classified into the following groups according to the thickness of the nano-silver coating: PEEK-3 (3nm), PEEK-6 (6nm), PEEK-9 (9nm), PEEK-12 (12nm), and PEEK control group. The surface microstructure and composition of each sample were observed by scanning electron microscopy (SEM), atomic force microscopy (AFM), and energy dispersive spectrum (EDS) analysis. The water contact angle of each sample was then measured by contact angle meters. A cell counting kit (CCK-8) was used to analyze the cytotoxicity of the mouse fibroblast cells (L929) in the coated groups (n=5) and group test samples (n=6), negative control (polyethylene, PE) (n=6), and positive control group (phenol) (n=6). The antibacterial properties of the samples were tested by co-culturing Streptococcus mutans and Straphylococcus aureus. The bacteria that adhered to the surface of samples were observed by SEM. The antibacterial adhesion ability of each sample was then evaluated. SEM and AFM analysis results showed that the surfaces of control group samples were smooth but compact. Homogeneous silver nano-particles (AgNPs) and nano-silver coating were uniformly distributed on the surface of the coated group samples. Compared with the control samples, the nano-silver coated samples had a significant increase in surface roughness (Pnano-silver coating increased. EDS analysis showed that not only C and O but also Ag were present on the surface of the coated samples. Moreover, the water contact angle of modified samples significantly increased after nano-silver coating modification (Pnano-silver coating can

  16. Deposition and characterization of single magnetron deposited Fe:SnO{sub x} coatings

    Energy Technology Data Exchange (ETDEWEB)

    Kormunda, Martin, E-mail: martin.kormunda@ujep.cz [J.E. Purkinje University, Faculty of Science, Department of Physics, Ceske mladeze 8, 400 96 Usti nad Labem (Czech Republic); Fischer, Daniel; Hertwig, Andreas; Beck, Uwe [BAM Federal Institute for Materials Research and Testing, Division 6 4 Surface Technologies, Unter den Eichen 44-46, 12203 Berlin (Germany); Sebik, Matej; Pavlik, Jaroslav [J.E. Purkinje University, Faculty of Science, Department of Physics, Ceske mladeze 8, 400 96 Usti nad Labem (Czech Republic); Esser, Norbert [Leibniz-Institut für Analytische Wissenschaften — ISAS e.V., Department Berlin, Schwarzschildstr. 12, 12489 Berlin (Germany)

    2015-11-30

    Coatings deposited by magnetron co-sputtering from a single RF magnetron with a ceramic SnO{sub 2} target with iron inset in argon plasma were studied. The mass spectra of the process identified Sn{sup +} and SnO{sup +} species as the dominant species sputtered from the target, but no SnO{sub 2}{sup +} species were detected. The dominant positive ions in argon plasma are Ar{sup +} species. The only detected negative ions were O{sup −}. Sputtered neutral tin related species were not detected. Iron related species were also not detected because their concentration is below the detection limit. The concentration of iron dopant in the tin oxide coatings was controlled by the RF bias applied on the substrate holder while the discharge pressure also has some influence. The iron concentration was in the range from 0.9 at.% up to 19 at.% increasing with the substrate bias while the sheet resistivity decreases. The stoichiometry ratio of O/(Sn + Fe) in the coatings increased from 1.7 up to 2 in dependence on the substrate bias from floating bias (− 5 V) up to − 120 V of RF self-bias, respectively. The tin in the coatings was mainly bonded in Sn{sup 4+} state and iron was mainly in Fe{sup 2+} state when other tin bonding states were detected only in a small amounts. Iron bonding states in contrary to elemental compositions of the coatings were not influenced by the RF bias applied on the substrate. The coatings showed high transparency in the visible spectral range. However, an increased metallic behavior could be detected by using a higher RF bias for the deposition. The X-ray diffraction patterns and electron microscopy pictures made on the coatings confirmed the presence of an amorphous phase. - Highlights: • RF magnetron sputtering of SnO{sub 2} target with Fe inset in argon investigated by mass spectrometry • Optical properties of Fe doped SnO{sub x} coatings characterized • Analyses of overlapped XPS peaks at a spectrum from Fe doped SnO{sub x} coatings

  17. Reactive magnetron sputtering deposition of bismuth tungstate onto titania nanoparticles for enhancing visible light photocatalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    Ratova, Marina, E-mail: marina_ratova@hotmail.com [Surface Engineering Group, School of Engineering, Manchester Metropolitan University, Manchester, M1 5GD (United Kingdom); Kelly, Peter J.; West, Glen T. [Surface Engineering Group, School of Engineering, Manchester Metropolitan University, Manchester, M1 5GD (United Kingdom); Tosheva, Lubomira; Edge, Michele [School of Science and the Environment, Manchester Metropolitan University, Manchester M1 5GD (United Kingdom)

    2017-01-15

    Highlights: • Bismuth tungstate coatings were deposited by reactive magnetron sputtering. • Oscillating bowl was introduced to the system to enable coating of nanopartulates. • Deposition of Bi{sub 2}WO{sub 6} enhanced visible light activity of titania nanoparticles. • The best results were obtained for coating with Bi:W ratio of approximately 2:1. • Deposition of Bi{sub 2}WO{sub 6} onto TiO{sub 2} resulted in more efficient electron-hole separation. - Abstract: Titanium dioxide − bismuth tungstate composite materials were prepared by pulsed DC reactive magnetron sputtering of bismuth and tungsten metallic targets in argon/oxygen atmosphere onto anatase and rutile titania nanoparticles. The use of an oscillating bowl placed beneath the two magnetrons arranged in a co-planar closed field configuration enabled the deposition of bismuth tungstate onto loose powders, rather than a solid substrate. The atomic ratio of the bismuth/tungsten coatings was controlled by varying the power applied to each target. The effect of the bismuth tungstate coatings on the phase, optical and photocatalytic properties of titania was investigated by X-ray diffraction, energy-dispersive X-ray spectroscopy (EDX), Brunauer–Emmett–Teller (BET) surface area measurements, transmission electron microscopy (TEM), UV–vis diffuse reflectance spectroscopy and an acetone degradation test. The latter involved measurements of the rate of CO{sub 2} evolution under visible light irradiation of the photocatalysts, which indicated that the deposition of bismuth tungstate resulted in a significant enhancement of visible light activity, for both anatase and rutile titania particles. The best results were achieved for coatings with a bismuth to tungsten atomic ratio of 2:1. In addition, the mechanism by which the photocatalytic activity of the TiO{sub 2} nanoparticles was enhanced by compounding it with bismuth tungstate was studied by microwave cavity perturbation. The results of these

  18. Structure and morphology of magnetron sputter deposited ultrathin ZnO films on confined polymeric template

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Ajaib [Discipline of Metallurgy Engineering and Materials Science, Indian Institute of Technology Indore, Indore 453552 (India); Schipmann, Susanne [II. Insatitute of Physics and JARA-FIT, RWTH Aachen University, 52056 Aachen (Germany); Mathur, Aakash; Pal, Dipayan [Discipline of Metallurgy Engineering and Materials Science, Indian Institute of Technology Indore, Indore 453552 (India); Sengupta, Amartya [Department of Physics, Indian Institute of Technology Delhi, Delhi 110016 (India); Klemradt, Uwe [II. Insatitute of Physics and JARA-FIT, RWTH Aachen University, 52056 Aachen (Germany); Chattopadhyay, Sudeshna, E-mail: sudeshna@iiti.ac.in [Discipline of Metallurgy Engineering and Materials Science, Indian Institute of Technology Indore, Indore 453552 (India); Discipline of Physics, Indian Institute of Technology Indore, Indore 453552 (India); Centre for Biosciences and Biomedical Engineering, Indian Institute of Technology Indore, Indore 453552 (India)

    2017-08-31

    Highlights: • Ultra-thin ZnO films grown on confined polymeric (polystyrene, PS) template. • XRR and GISAXS explore the surface/interfaces structure and morphology of ZnO/PS. • Insights into the growth mechanism of magnetron sputtered ZnO thin film on PS template. • Nucleated disk-like cylindrical particles are the basis of the formation of ZnO layers. • Effect of ZnO film thickness on room temperature PL spectra in ZnO/PS systems. - Abstract: The structure and morphology of ultra-thin zinc oxide (ZnO) films with different film thicknesses on confined polymer template were studied through X-ray reflectivity (XRR) and grazing incidence small angle X-ray scattering (GISAXS). Using magnetron sputter deposition technique ZnO thin films with different film thicknesses (<10 nm) were grown on confined polystyrene with ∼2R{sub g} film thickness, where R{sub g} ∼ 20 nm (R{sub g} is the unperturbed radius of gyration of polystyrene, defined by R{sub g} = 0.272 √M{sub 0}, and M{sub 0} is the molecular weight of polystyrene). The detailed internal structure, along the surface/interfaces and the growth direction of the system were explored in this study, which provides insight into the growth procedure of ZnO on confined polymer and reveals that a thin layer of ZnO, with very low surface and interface roughness, can be grown by DC magnetron sputtering technique, with approximately full coverage (with bulk like electron density) even in nm order of thickness, in 2–7 nm range on confined polymer template, without disturbing the structure of the underneath template. The resulting ZnO-polystyrene hybrid systems show strong ZnO near band edge (NBE) and deep-level (DLE) emissions in their room temperature photoluminescence spectra, where the contribution of DLE gets relatively stronger with decreasing ZnO film thickness, indicating a significant enhancement of surface defects because of the greater surface to volume ratio in thinner films.

  19. Photoelectron-spectroscopic and reactivity investigation of thin Pd-Sn films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Skala, T.; Veltruska, K.; Sedlacek, L.; Masek, K.; Matolinova, I.; Matolin, V.

    2007-01-01

    We have studied Pd-Sn layers with different composition prepared by magnetron sputtering. Layers were sputtered onto Al 2 O 3 and SiO 2 substrates and studied by X-ray photoelectron spectroscopy (XPS). Spectra confirmed that after vacuum annealing residual oxygen and carbon have been removed and bimetallic bonds have been created. The shift of Pd 3d 5/2 core level to higher binding energy followed by the peak narrowing in dependence on the composition was observed, accompanied by the shift of the Pd 4d in the valence band region, induced by hybridization of Pd-d and Sn-s,p states. Experiments carried out on a gas-flow reactor indicate increasing temperature of the CO oxidation with tin ratio in the alloy

  20. Morphological analysis of TiB2 thin film prepared by rf magnetron sputtering

    International Nuclear Information System (INIS)

    Dai Wei; Zhang Tongjun; Yang Junyou; Sun Rongxing; Xu Juliang

    2008-01-01

    Superhard TiB 2 thin films were deposited on steel substrates using the radio-frequency magnetron-sputtering technique with a low normalized substrate temperature (0.1 s /T m 2 thin films were overstoichiometric and that the diffusion of Ti and B atoms on the substrate surface was greatly improved at a temperature of 350 deg. C. Moreover, a new dense structure, named the ''equiaxed'' grain structure, was observed by FESEM at this substrate temperature. GIXRD was carried out at different directions with same the grazing-incidence method and the variation of diffraction intensity of the nonrandom textured grains was confirmed. Combined with FESEM and AES analysis, it is suggested that the equiaxed grain structure was located in zone 2 at the normalized substrate temperature as low as 0.18

  1. Development of nanocrystalline Indium Tin Oxide (ITO) thin films using RF-magnetron sputtering

    International Nuclear Information System (INIS)

    Tamilselvan, N.; Thilakan, Periyasamy

    2013-01-01

    ITO thin films have been deposited on glass substrate using RF Magnetron puttering Technique from the pre-synthesized ITO target. The sputtering parameters such as the deposition temperature, gas composition and the RF power densities were varied. X-ray diffraction studies revealed that the crystallization of the films is mostly depending on the RF power density and substrate temperature. Crystallized films exhibited a change in the preferred orientation from (111) plane to (100) plane at specific conditions such as high RF power density and high oxygen mixing to the plasma. Change in the film microstructure and a shift in the optical bandgap were recorded from the SEM and UV-Visible measurements respectively. (author)

  2. Metal doped fluorocarbon polymer films prepared by plasma polymerization using an RF planar magnetron target

    International Nuclear Information System (INIS)

    Biederman, H.; Holland, L.

    1983-01-01

    Fluorocarbon films have been prepared by plasma polymerization of CF 4 using an RF planar magnetron with an aluminium target. More than one order of magnitude higher deposition rate has been achieved in comparison with an r.f. diode system operated under similar conditions of monomer pressure and flow rate and power input. A glow discharge in a CF 4 [25%]-argon[75%] mixture was used to incorporate aluminium from a target electrode into the polymer films. The foregoing mixture and another based on CF 4 [87%]-argon[13%] were used in the RF discharge with a copper target. Some experiments with a gold target and pure CF 4 as the inlet gas were also made. The film structure was examined by SEM and TEM and characteristic micrographs are presented here. The composition of the films was estimated from an EAS study. The sheet resistivity of the metal/polymer film complexes was determined. (orig.)

  3. Effects of Annealing on TiN Thin Film Growth by DC Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Azadeh Jafari

    2014-07-01

    Full Text Available We have reviewed the deposition of titanium nitride (TiN thin films on stainless steel substrates by a DC magnetron sputtering method and annealing at different annealing temperatures of 500, 600, and 700°C for 120 min in nitrogen/argon atmospheres. Effects of annealing temperatures on the structural and the optical properties of TiN films were investigated using X-ray diffraction (XRD, atomic force microscope (AFM, field emission scanning electron microscopy (FESEM, and UV-VIS spectrophotometer. Our experimental studies reveal that the annealing temperature appreciably affected the structures, crystallite sizes, and reflection of the films. By increasing the annealing temperature to 700°C crystallinity and reflection of the film increase. These results suggest that annealed TiN films can be good candidate for tokamak first wall due to their structural and optical properties.

  4. Deposition of a conductive near-infrared cutoff filter by radio-frequency magnetron sputtering

    International Nuclear Information System (INIS)

    Lee, Jang-Hoon; Lee, Seung-Hyu; Yoo, Kwang-Lim; Kim, Nam-Young; Hwangbo, Chang Kwon

    2002-01-01

    We have designed a conductive near-infrared (NIR) cutoff filter for display application, i.e., a modified low-emissivity filter based on the three periods of the basic design of [TiO2|Ti|Ag| TiO2] upon a glass substrate and investigated the optical, structural, chemical, and electrical properties of the conductive NIR cutoff filter prepared by a radio frequency magnetron sputtering system. The results show that the average transmittance is 61.1% in the visible, that the transmittance in the NIR is less than 6.6%, and that the sheet resistance and emissivity are 0.9 Ω/□ (where □ stands for a square film) and 0.012, respectively, suggesting that the conductive NIR cutoff filter can be employed as a shield against the hazard of electromagnetic waves as well as to cut off the NIR

  5. Arsenic doped p-type zinc oxide films grown by radio frequency magnetron sputtering

    International Nuclear Information System (INIS)

    Fan, J. C.; Zhu, C. Y.; Fung, S.; To, C. K.; Yang, B.; Beling, C. D.; Ling, C. C.; Zhong, Y. C.; Wong, K. S.; Xie, Z.; Brauer, G.; Skorupa, W.; Anwand, W.

    2009-01-01

    As-doped ZnO films were grown by the radio frequency magnetron sputtering method. As the substrate temperature during growth was raised above ∼400 deg. C, the films changed from n type to p type. Hole concentration and mobility of ∼6x10 17 cm -3 and ∼6 cm 2 V -1 s -1 were achieved. The ZnO films were studied by secondary ion mass spectroscopy, x-ray photoelectron spectroscopy (XPS), low temperature photoluminescence (PL), and positron annihilation spectroscopy (PAS). The results were consistent with the As Zn -2V Zn shallow acceptor model proposed by Limpijumnong et al. [Phys. Rev. Lett. 92, 155504 (2004)]. The results of the XPS, PL, PAS, and thermal studies lead us to suggest a comprehensive picture of the As-related shallow acceptor formation.

  6. Substantial difference in target surface chemistry between reactive dc and high power impulse magnetron sputtering

    Science.gov (United States)

    Greczynski, G.; Mráz, S.; Schneider, J. M.; Hultman, L.

    2018-02-01

    The nitride layer formed in the target race track during the deposition of stoichiometric TiN thin films is a factor 2.5 thicker for high power impulse magnetron sputtering (HIPIMS), compared to conventional dc processing (DCMS). The phenomenon is explained using x-ray photoelectron spectroscopy analysis of the as-operated Ti target surface chemistry supported by sputter depth profiles, dynamic Monte Carlo simulations employing the TRIDYN code, and plasma chemical investigations by ion mass spectrometry. The target chemistry and the thickness of the nitride layer are found to be determined by the implantation of nitrogen ions, predominantly N+ and N2+ for HIPIMS and DCMS, respectively. Knowledge of this method-inherent difference enables robust processing of high quality functional coatings.

  7. Tribological characterization of TiN coatings prepared by magnetron sputtering

    Science.gov (United States)

    Makwana, Nishant S.; Chauhan, Kamlesh V.; Sonera, Akshay L.; Chauhan, Dharmesh B.; Dave, Divyeshkumar P.; Rawal, Sushant K.

    2018-05-01

    Titanium nitride (TiN) coating deposited on aluminium and brass pin substrates using RF reactive magnetron sputtering. The structural properties and surface morphology were characterized by X-ray diffraction (XRD), atomic force microscope (AFM) and field emission scanning electron microscope (FE-SEM). There was formation of (101) Ti2N, (110) TiN2 and (102) TiN0.30 peaks at 3.5Pa, 2Pa and 1.25Pa sputtering pressure respectively. The tribological properties of coating were inspected using pin on disc tribometer equipment. It was observed that TiN coated aluminium and brass pins demonstrated improved wear resistance than uncoated aluminium and brass pins.

  8. Implementation and initial test result of a prototype solid state modulator for pulsed magnetron

    International Nuclear Information System (INIS)

    Dake, Vishal; Mangalvedekar, H.A.; Tillu, Abhijit; Dixit, Kavita P.; Sarukte, Hemant

    2014-01-01

    A solid-state modulator rated for 50 kV, 120A, 4μs and 250 Hz has been designed. The discharging circuit of the modulator is being tested at ∼ 33 kV, 40-80A, at a maximum pulse repetition rate of 30 pps. The paper discusses development and testing of prototype discharging circuit on resistive load and magnetron. The technique used for measurement of pulse transformer leakage inductance, distributed capacitance and stray primary circuit series inductance will also be discussed in detail. It is necessary to have Energy Storage Capacitors with low ESL for these applications (ESL < 40 nH). The method used for evaluating the ESL of locally available metalized polypropylene capacitors will also be presented. (author)

  9. Implementation and initial test result of a prototype solid state modulator for pulsed magnetron

    Energy Technology Data Exchange (ETDEWEB)

    Dake, Vishal; Mangalvedekar, H.A., E-mail: vishaldake90@gmail.com [Veermata Jijabai Technological Institute, Mumbai (India); Tillu, Abhijit; Dixit, Kavita P.; Sarukte, Hemant [Accelerator and Pulse Power Division, Bhabha Atomic Research Centre, Mumbai (India)

    2014-07-01

    A solid-state modulator rated for 50 kV, 120A, 4μs and 250 Hz has been designed. The discharging circuit of the modulator is being tested at ∼ 33 kV, 40-80A, at a maximum pulse repetition rate of 30 pps. The paper discusses development and testing of prototype discharging circuit on resistive load and magnetron. The technique used for measurement of pulse transformer leakage inductance, distributed capacitance and stray primary circuit series inductance will also be discussed in detail. It is necessary to have Energy Storage Capacitors with low ESL for these applications (ESL < 40 nH). The method used for evaluating the ESL of locally available metalized polypropylene capacitors will also be presented. (author)

  10. Synthesis and characterization of DC magnetron sputtered nano structured molybdenum thin films

    Energy Technology Data Exchange (ETDEWEB)

    Rondiya, S. R.; Rokade, A. V.; Jadhavar, A. A.; Pandharkar, S. M.; Kulkarni, R. R.; Karpe, S. D.; Diwate, K. D. [School of Energy Studies, Savitribai Phule Pune University, Pune 411007 (India); Jadkar, S. R., E-mail: sandesh@physics.unipune.ac.in [Department of Physics, Savitribai Phule Pune University, Pune 411007 (India)

    2016-04-13

    Molybdenum (Mo) thin films were deposited on corning glass (#7059) substrates using DC magnetron sputtering system. The effect of substrate temperature on the structural, morphology and topological properties have been investigated. Films were characterized by variety of techniques such as low angle x-ray diffraction (low angle XRD), field emission scanning electron microscopy (FE-SEM), atomic force microscopy (AFM). The low angle XRD analysis revealed that the synthesized Mo films are nanocrystalline having cubic crystal structure with (110) preferential orientation. The microstructure of the deposited Mo thin films observed with FE-SEM images indicated that films are homogeneous and uniform with randomly oriented leaf shape morphology. The AFM analysis shows that with increase in substrate temperature the rms roughness of Mo films increases. The obtained results suggest that the synthesized nanostructured Mo thin films have potential application as a back contact material for high efficiency solar cells like CdTe, CIGS, CZTS etc.

  11. Deposition of amino-rich thin films by RF magnetron sputtering of nylon

    Energy Technology Data Exchange (ETDEWEB)

    Kylian, O; Hanus, J; Choukourov, A; Kousal, J; SlavInska, D; Biederman, H, E-mail: ondrej.kylian@gmail.co [Charles University, Faculty of Mathematics and Physics, V Holesovickach 2, Prague 8, 180 00 (Czech Republic)

    2009-07-21

    RF magnetron sputtering of a nylon target in different gas mixtures was studied in order to evaluate the capability of this process to deposit amino-rich coatings needed in a wide range of biomedical applications. It has been demonstrated that both the deposition rate of the coatings and the surface density of primary amino groups are strongly linked with working gas mixture composition. From this point of view, a sufficiently high deposition rate as well as the highest amine efficiency reaching a NH{sub 2}/C value of 18% was observed in the N{sub 2}/H{sub 2} discharge, which leads to the surface exhibiting a high rate of protein adsorption. (fast track communication)

  12. Annealing induced morphological modifications in PTFE films deposited by magnetron sputtering

    Science.gov (United States)

    Tripathi, S.; De, Rajnarayan; Rao, K. Divakar; Haque, S. Maidul; Misal, J. S.; Prathap, C.; Das, S. C.; Ganesan, V.; Sahoo, N. K.

    2017-05-01

    As grown RF magnetron sputtered polytetrafluoroethylene (PTFE) thin films were subjected to vacuum annealing at optimized elevated temperature of 200° C for varying time duration and corresponding surface morphological changes were recorded. The columnar structures appearing after an annealing duration of 2 hours are interesting for fabrication of rough PTFE surfaces towards possible applications in hydrophobicity along with high transmission. Supported by transmission data, the AFM images show a transformation of smooth PTFE surface with less than 2 nm rms roughness to a very rough surface. The results are interpreted in terms of thermal energy induced modifications only at the surface without any change in the original bonding structure on the surface and inside the sample. Preliminary studies indicate that the optimization of roughness and transmission together on such surfaces may lead to high water contact angles.

  13. Influence of the microstructure on the corrosion behavior of magnetron sputter-quenched amorphous metallic alloys

    Science.gov (United States)

    Thakoor, A. P.; Khanna, S. K.; Williams, R. M.; Landel, R. F.

    1983-01-01

    The microstructure and corrosion behavior of magnetron sputter deposited amorphous metallic films of (Mo6ORu40)82B18 under varying sputtering atmospheres have been investigated. The microstructural details and topology of the films have been studied by scanning electron microscopy and correlated with the deposition conditions. By reducing the pressure of pure argon gas, the characteristic features of rough surface and columnar growth full of vertical voids can be converted into a mirror-smooth finish with very dense deposits. Films deposited in the presence of O2 or N2 exhibit columnar structure with vertical voids. Film deposited in pure argon at low pressure show remarkably high corrosion resistance due to the formation of a uniform passive surface layer. The influence of the microstructure and surface texture on the corrosion behavior is discussed.

  14. Non-channel magnetron gun as the electron source for resonance linear accelerator

    International Nuclear Information System (INIS)

    Ivanov, G.M.; Makhnenko, L.A.; Cherenshchikov, S.A.

    1999-01-01

    Studies on the magnetron gun with a cold cathode being part of linear accelerator on the travelling wave are described. Two modes of the gun operation differing by presence of UHF field of the pre-buncher near the gun are observed. In the mode without UHF field the short (about 2 ns) pulses of accelerated electrons with amplitude up to 0.5 A at the gun current up to 20 A were obtained. The presence of UHF field near the gun makes it possible to obtain the beam of higher duration (up to 1.0 μs), but with current up to 20 mA at the accelerator outlet and up to 1 A at the gun outlet. The mechanism of the gun operation is concerned with the secondary-electron current increase and setting self-sustaining secondary emission. Gun characteristics under study are acceptable for the purposes of injection into accelerator [ru

  15. Reversible superhydrophilicity and hydrophobicity switching of V2O5 thin films deposited by magnetron sputtering

    Science.gov (United States)

    Zhang, Chunzi; Peng, Zhiguang; Cui, Xiaoyu; Neil, Eric; Li, Yuanshi; Kasap, Safa; Yang, Qiaoqin

    2018-03-01

    V2O5 thin films are well-known "smart" materials due to their reversible wettability under UV irradiation and dark storage. Their surfaces are usually hydrophobic and turn into hydrophilic under UV irradiation. However, the V2O5 thin films deposited by magnetron sputtering in present work are superhydrophilic and turned into hydrophobic after days' of storage in air. This change can be recovered by heating. The effects of many factors including surface roughness, irradiation from visible light, UV, & X-ray, and storage in air & vacuum on the reversible switching of wettability were investigated. The results show that air absorption is the main factor causing the film surface change from superhydrophilicity to hydrophobicity.

  16. UV-Enhanced Ethanol Sensing Properties of RF Magnetron-Sputtered ZnO Film.

    Science.gov (United States)

    Huang, Jinyu; Du, Yu; Wang, Quan; Zhang, Hao; Geng, Youfu; Li, Xuejin; Tian, Xiaoqing

    2017-12-26

    ZnO film was deposited by the magnetron sputtering method. The thickness of ZnO film is approximately 2 μm. The influence of UV light illumination on C₂H₅OH sensing properties of ZnO film was investigated. Gas sensing results revealed that the UV-illuminated ZnO film displays excellent C₂H₅OH characteristics in terms of high sensitivity, excellent selectivity, rapid response/recovery, and low detection limit down to 0.1 ppm. The excellent sensing performance of the sensor with UV activation could be attributed to the photocatalytic oxidation of ethanol on the surface of the ZnO film, the planar film structure with high utilizing efficiency of UV light, high electron mobility, and a good surface/volume ratio of of ZnO film with a relatively rough and porous surface.

  17. Fabrication of hydroxyapatite thin films for biomedical applications using RF magnetron sputtering

    International Nuclear Information System (INIS)

    Yamaguchi, Tetsuro; Tanaka, Yoshikazu; Ide-Ektessabi, Ari

    2006-01-01

    The calcium phosphate thin films for medical applications require similar chemical properties as those of natural bone as well as a uniform surface without any defect, such as cracks and pinholes. In this study, the calcium phosphate thin films were fabricated using RF magnetron sputtering deposition technique at discharge power of 200W, 300W and 400W. The target used for the deposition was sintered HAp. RBS analysis showed that the Ca/P ratio increased with the discharge power becoming close to that of Ca/P=1.67 in ideal HAp. XPS analysis revealed the presence of PO 4 3- and OH - bonds in the calcium phosphate films fabricated. The chemical properties of the calcium phosphate thin films were similar to those of ideal HAp. The AFM results revealed that the thin films prepared had a uniform surface

  18. Numerical Simulation of a Double-anode Magnetron Injection Gun for 110 GHz, 1 MW Gyrotron

    Science.gov (United States)

    Singh, Udaybir; Kumar, Nitin; Purohit, L. P.; Sinha, Ashok K.

    2010-07-01

    A 40 A double-anode magnetron injection gun for a 1 MW, 110 GHz gyrotron has been designed. The preliminary design has been obtained by using some trade-off equations. The electron beam analysis has been performed by using the commercially available code EGUN and the in-house developed code MIGANS. The operating mode of the gyrotron is TE22,6 and it is operated in the fundamental harmonic. The electron beam with a low transverse velocity spread ( δ {β_{ bot max }} = 2.26% ) and the transverse-to-axial velocity ratio of the electron beam (α) = 1.37 is obtained. The simulated results of the MIG obtained with the EGUN code have been validated with another trajectory code TRAK. The results on the design output parameters obtained by both the codes are in good agreement. The sensitivity analysis has been carried out by changing the different gun parameters to decide the fabrication tolerance.

  19. Magnetron injection gun for a broadband gyrotron backward-wave oscillator

    International Nuclear Information System (INIS)

    Yuan, C. P.; Chang, T. H.; Chen, N. C.; Yeh, Y. S.

    2009-01-01

    The magnetron injection gun is capable of generating relativistic electron beam with high velocity ratio and low velocity spread for a gyrotron backward-wave oscillator (gyro-BWO). However, the velocity ratio (α) varies drastically against both the magnetic field and the beam voltage, which significantly limits the tuning bandwidth of a gyro-BWO. This study remedies this drawback by adding a variable trim field to adjust the magnetic compression ratio when changing the operating conditions. Theoretical results obtained by employing a two-dimensional electron gun code (EGUN) demonstrate a constant velocity ratio of 1.5 with a low axial velocity spread of 6% from 3.4-4.8 Tesla. These results are compared with a three-dimensional particle-tracing code (computer simulation technology, CST). The underlying physics for constant α will be discussed in depth.

  20. Magnetron injection gun for a broadband gyrotron backward-wave oscillator

    Science.gov (United States)

    Yuan, C. P.; Chang, T. H.; Chen, N. C.; Yeh, Y. S.

    2009-07-01

    The magnetron injection gun is capable of generating relativistic electron beam with high velocity ratio and low velocity spread for a gyrotron backward-wave oscillator (gyro-BWO). However, the velocity ratio (α) varies drastically against both the magnetic field and the beam voltage, which significantly limits the tuning bandwidth of a gyro-BWO. This study remedies this drawback by adding a variable trim field to adjust the magnetic compression ratio when changing the operating conditions. Theoretical results obtained by employing a two-dimensional electron gun code (EGUN) demonstrate a constant velocity ratio of 1.5 with a low axial velocity spread of 6% from 3.4-4.8 Tesla. These results are compared with a three-dimensional particle-tracing code (computer simulation technology, CST). The underlying physics for constant α will be discussed in depth.

  1. Design of a double-anode magnetron-injection gun for the W-band gyrotron

    Science.gov (United States)

    Jang, Kwang Ho; Choi, Jin Joo; So, Joon Ho

    2015-07-01

    A double-anode magnetron-injection gun (MIG) was designed. The MIG is for a W-band 10-kW gyrotron. Analytic equations based on adiabatic theory and angular momentum conservation were used to examine the initial design parameters such as the cathode angle, and the radius of the beam emitting surface. The MIG's performances were predicted by using an electron trajectory code, the EGUN code. The beam spread of the axial velocity, Δvz/vz, obtained from the EGUN code was observed to be 1.34% at α = 1.3. The cathode edge emission and the thermal effect were modeled. The cathode edge emission was found to have a major effect on the velocity spread. The electron beam's quality was significantly improved by affixing non-emissive cylinders to the cathode.

  2. Design of a magnetron injection gun for a 17.5-GHz

    International Nuclear Information System (INIS)

    Ha, H. J.; Kim, J. E.; Park, G. S.

    1996-01-01

    A gyrotwystron which is composed of cavities (gyro-klystron) and waveguides (gyro-TWT) is under investigation for broader bandwidth with high efficiency. A magnetron injection gun (MIG) for the gyrotwystron is designed with the trade-off equation for the MIG and optimized by computer simulation using the e-gun code. A 300-kW, 60-kV MIG with α ≡ υ t /υ z = 1.2 and Δυ z ≤ 5% designed for a 17.5-GHz gyrotwystron is discussed in this paper. Also, the effect of various MIG parameters, such as the beam voltage, the beam current, the magnetic field, the cathode radius and angle, and the MIG dimensions, on the characteristics of the beam (α, Δυ z ) is studied. (author)

  3. A study of the transient plasma potential in a pulsed bi-polar dc magnetron discharge

    International Nuclear Information System (INIS)

    Bradley, J W; Karkari, S K; Vetushka, A

    2004-01-01

    The temporal evolution of the plasma potential, V p , in a pulsed dc magnetron plasma has been determined using the emissive probe technique. The discharge was operated in the 'asymmetric bi-polar' mode, in which the discharge voltage changes polarity during part of the pulse cycle. The probe measurements, with a time-resolution of 20 ns or better, were made along a line above the racetrack, normal to the plane of the cathode target, for a fixed frequency (100 kHz), duty cycle (50%), argon pressure (0.74 Pa) and discharge power (583 W). At all the measured positions, V p was found to respond to the large and rapid changes in the cathode voltage, V d , during the different phases of the pulse cycle, with V p always more positive than V d . At a typical substrate position (>80 mm from the target), V p remains a few volts above the most positive surface in the discharge at all times. In the 'on' phase of the pulse, the measurements show a significant axial electric field is generated in the plasma, with the plasma potential dropping by a total of about 30 V over a distance of 70 mm, from the bulk plasma to a position close to the beginning of the cathode fall. This is consistent with measurements made in the dc magnetron. During the stable 'reverse' phase of the discharge, for distances greater than 18 mm from the target, the axial electric field is found to collapse, with V p elevated uniformly to about 3 V above V d . Between the target and this field-free region an ion sheath forms, and the current flowing to the target is still an ion current in this 'reverse' period. During the initial 200 ns of the voltage 'overshoot' phase (between 'on' and 'reverse' phases), V d reached a potential of +290 V; however, close to the target, V p was found to attain a much higher value, namely +378 V. Along the line of measurement, the axial electric field reverses in direction in this phase, and an electron current of up to 9 A flows to the target. The spatial and temporal

  4. Synthesis of ReN3 Thin Films by Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    G. Soto

    2014-01-01

    Full Text Available In this work ReNx films were prepared by reactive magnetron sputtering at room temperature and deposited on a silicon wafer. It was found that the diffractograms of the nitrogen-rich rhenium film are consistent with those produced by high-pressure high-temperature methods, under the assumption that the film is oriented on the substrate. Using density functional calculations it was found that the composition of this compound could be ReN3, instead of ReN2, as stated on previous works. The ReN3 compound fits in the Ama2 (40 orthorhombic space group, and due to the existence of N3 anions between Re layers it should be categorized as an azide. The material is exceptionally brittle and inherently unstable under indentation testing.

  5. Optical properties of ITO films obtained by high-frequency magnetron sputtering with accompanying ion treatment

    Energy Technology Data Exchange (ETDEWEB)

    Krylov, P. N., E-mail: ftt@uni.udm.ru; Zakirova, R. M.; Fedotova, I. V. [Udmurt State University (Russian Federation)

    2013-10-15

    A variation in the properties of indium-tin-oxide (ITO) films obtained by the method of reactive magnetron sputtering with simultaneous ion treatment is reported. The ITO films feature the following parameters in the optical range of 450-1100 nm: a transmission coefficient of 80%, band gap of 3.50-3.60 eV, and a refractive index of 1.97-2.06. All characteristics of the films depend on the ion-treatment current. The latter, during the course of deposition, reduces the resistivity of the ITO films with the smallest value of the resistivity being equal to 2 Multiplication-Sign 10{sup -3} {Omega} cm. The degradation of films with a high resistivity when kept in air is observed.

  6. Coating multilayer material with improved tribological properties obtained by magnetron sputtering

    Science.gov (United States)

    Mateescu, A. O.; Mateescu, G.; Balasoiu, M.; Pompilian, G. O.; Lungu, M.

    2017-02-01

    This work is based on the Patent no. RO 128094 B1, granted by the Romanian State Office for Inventions and Trademarks. The goal of the work is to obtain for investigations tribological coatings with multilayer structure with improved tribological properties, deposited by magnetron sputtering process from three materials (sputtering targets). Starting from compound chemical materials (TiC, TiB2 and WC), as sputtering targets, by deposition in argon atmosphere on polished stainless steel, we have obtained, based on the claims of the above patent, thin films of multilayer design with promising results regarding their hardness, elastic modulus, adherence, coefficient of friction and wear resistance. The sputtering process took place in a special sequence in order to ensure better tribological properties to the coating, comparing to those of the individual component materials. The tribological properties, such as the coefficient of friction, are evaluated using the tribometer test.

  7. Mechanical and tribological properties of crystalline aluminum nitride coatings deposited on stainless steel by magnetron sputtering

    Science.gov (United States)

    Choudhary, R. K.; Mishra, S. C.; Mishra, P.; Limaye, P. K.; Singh, K.

    2015-11-01

    Aluminum nitride (AlN) coating is a potential candidate for addressing the problems of MHD pressure drop, tritium permeation and liquid metal corrosion of the test blanket module of fusion reactor. In this work, AlN coatings were grown on stainless steel by magnetron sputtering. Grazing incidence X-ray diffraction measurement revealed that formation of mixed phase (wurtzite and rock salt) AlN was favored at low discharge power and substrate negative biasing. However, at sufficiently high discharge power and substrate bias, (100) oriented wurtzite AlN was obtained. Secondary ion mass spectroscopy showed presence of oxygen in the coatings. The highest value of hardness and Young's modulus were 14.1 GPa and 215 GPa, respectively. Scratch test showed adhesive failure at a load of about 20 N. Wear test showed improved wear resistance of the coatings obtained at higher substrate bias.

  8. Deposition and characterization of ZrMoN thin films by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Fontes Junir, A.S.; Felix, L.C.; Oliveira, G.B. de; Fernandez, D.R.; Carvalho, R.G.; Tentardini, E.K.; Silva Junior, A.H. da

    2016-01-01

    Thin films of ZrMoN were deposited by magnetron reactive sputtering technique in order to study the molybdenum influence on the mechanical properties and oxidation resistance of these coatings. Three thin films with molybdenum concentrations from 25 to 40 at.% were selected. The displacement of characteristic peaks of ZrN where identified by GIXRD results of films with larger Mo content. This result is indicative of the Mo accommodation in the lattice structure. Hardness tests revealed favorable results with values up to 33 GPa. Oxidation tests showed that ZrN oxidized at 500 °C with a monoclinic ZrO 2 and tetragonal formation; whereas the thin films with Mo addition impeded the formation of the monoclinic ZrO 2 phase at partial oxidation. (author)

  9. Vanadium oxide thin films deposited on silicon dioxide buffer layers by magnetron sputtering

    International Nuclear Information System (INIS)

    Chen Sihai; Ma Hong; Wang Shuangbao; Shen Nan; Xiao Jing; Zhou Hao; Zhao Xiaomei; Li Yi; Yi Xinjian

    2006-01-01

    Thin films made by vanadium oxide have been obtained by direct current magnetron sputtering method on SiO 2 buffer layers. A detailed electrical and structural characterization has been performed on the deposited films by four-point probe method and scanning electron microscopy (SEM). At room temperature, the four-point probe measurement result presents the resistance of the film to be 25 kU/sheet. The temperature coefficient of resistance is - 2.0%/K. SEM image indicates that the vanadium oxide exhibits a submicrostructure with lamella size ranging from 60 nm to 300 nm. A 32 x 32-element test microbolometer was fabricated based on the deposited thin film. The infrared response testing showed that the response was 200 mV. The obtained results allow us to conclude that the vanadium oxide thin films on SiO 2 buffer layers is suitable for uncooled focal plane arrays applications

  10. Effect of interelectrode distance on dc magnetron current-pressure characteristics

    Science.gov (United States)

    Mankelevich, Yu A.; Pal, A. F.; Ryabinkin, A. N.; Serov, A. O.

    2018-01-01

    The current-pressure (I-P) non-monotonic characteristic in the magnetron discharge dc in argon at different interelectrode distances was investigated. The ion spatial distribution was obtained with optical emission spectroscopy and the characteristic dimensions of the discharge structure in near cathode region were determined. It is shown that decreasing the distance between electrodes does not affect the shape and position of the nonmonotonic part of I-P characteristic until this distance become comparable with the dimensions of the ionization region near cathode. The existence of non-monotonic part of I-P characteristic is determined by the processes in the near cathode region and is probably unrelated with the cold electron transfer in the rest of the plasma.

  11. AlN/Al dual protective coatings on NdFeB by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Li Jinlong; Mao Shoudong; Sun Kefei [Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); Li Xiaomin [Shanghai Institute of Ceramics Chinese Academy of Sciences, Shanghai 200050 (China); Song Zhenlun [Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China)], E-mail: songzhenlun@nimte.ac.cn

    2009-11-15

    AlN/Al dual protective coatings were prepared on NdFeB by DC magnetron sputtering in a home-made industrial apparatus. Comparing with Al coating, AlN/Al coatings have a denser structure of an outmost AlN amorphous layer following an inner Al columnar crystal layer. The coatings and NdFeB substrate combine well, and moreover, there is occurrence of metallurgy bonding in the interface layer. Both Al and AlN/Al coatings have a good protective ability to NdFeB. Especially, the corrosion resistance of AlN/Al coated NdFeB is improved largely. AlN/Al and Al protective coatings not only do not deteriorate the magnetic properties of NdFeB, but contribute to their slight increase.

  12. AlN/Al dual protective coatings on NdFeB by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Li Jinlong; Mao Shoudong; Sun Kefei; Li Xiaomin; Song Zhenlun

    2009-01-01

    AlN/Al dual protective coatings were prepared on NdFeB by DC magnetron sputtering in a home-made industrial apparatus. Comparing with Al coating, AlN/Al coatings have a denser structure of an outmost AlN amorphous layer following an inner Al columnar crystal layer. The coatings and NdFeB substrate combine well, and moreover, there is occurrence of metallurgy bonding in the interface layer. Both Al and AlN/Al coatings have a good protective ability to NdFeB. Especially, the corrosion resistance of AlN/Al coated NdFeB is improved largely. AlN/Al and Al protective coatings not only do not deteriorate the magnetic properties of NdFeB, but contribute to their slight increase.

  13. Operational limit of a planar DC magnetron cluster source due to target erosion

    International Nuclear Information System (INIS)

    Rai, A.; Mutzke, A.; Bandelow, G.; Schneider, R.; Ganeva, M.; Pipa, A.V.; Hippler, R.

    2013-01-01

    The binary collision-based two dimensional SDTrimSP-2D model has been used to simulate the erosion process of a Cu target and its influence on the operational limit of a planar DC magnetron nanocluster source. The density of free metal atoms in the aggregation region influences the cluster formation and cluster intensity during the target lifetime. The density of the free metal atoms in the aggregation region can only be predicted by taking into account (i) the angular distribution of the sputtered flux from the primary target source and (ii) relative downwards shift of the primary source of sputtered atoms during the erosion process. It is shown that the flux of the sputtered atoms smoothly decreases with the target erosion

  14. DC magnetron sputtering prepared Ag-C thin film anode for thin film lithium ion microbatteries

    International Nuclear Information System (INIS)

    Li, Y.; Tu, J.P.; Shi, D.Q.; Huang, X.H.; Wu, H.M.; Yuan, Y.F.; Zhao, X.B.

    2007-01-01

    An Ag-C thin film was prepared by DC magnetron co-sputtering, using pure silver and graphite as the targets. The microstructure and morphology of the deposited thin film were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Electrochemical performances of the Ag-C thin film anode were investigated by means of discharge/charge and cyclic voltammogram (CV) tests in model cells. The electrochemical impedance spectrum (EIS) characteristics and the chemical diffusion coefficient, D Li of the Ag-C thin film electrode at different discharging states were discussed. It was believed that the excellent cycling performance of the Ag-C electrode was ascribed to the good conductivity of silver and the volume stability of the thin film

  15. Arsenic doped p-type zinc oxide films grown by radio frequency magnetron sputtering

    Science.gov (United States)

    Fan, J. C.; Zhu, C. Y.; Fung, S.; Zhong, Y. C.; Wong, K. S.; Xie, Z.; Brauer, G.; Anwand, W.; Skorupa, W.; To, C. K.; Yang, B.; Beling, C. D.; Ling, C. C.

    2009-10-01

    As-doped ZnO films were grown by the radio frequency magnetron sputtering method. As the substrate temperature during growth was raised above ˜400 °C, the films changed from n type to p type. Hole concentration and mobility of ˜6×1017 cm-3 and ˜6 cm2 V-1 s-1 were achieved. The ZnO films were studied by secondary ion mass spectroscopy, x-ray photoelectron spectroscopy (XPS), low temperature photoluminescence (PL), and positron annihilation spectroscopy (PAS). The results were consistent with the AsZn-2VZn shallow acceptor model proposed by Limpijumnong et al. [Phys. Rev. Lett. 92, 155504 (2004)]. The results of the XPS, PL, PAS, and thermal studies lead us to suggest a comprehensive picture of the As-related shallow acceptor formation.

  16. Synthesis and characterization of DC magnetron sputtered ZnO thin films under high working pressures

    International Nuclear Information System (INIS)

    Hezam, M.; Tabet, N.; Mekki, A.

    2010-01-01

    ZnO thin films were deposited on glass substrates using direct current (dc) magnetron sputtering under high working pressures. A pure zinc target was used, and sputtering was carried out in an oxygen atmosphere. The working pressure was varied between 50 and 800 mTorr. XRD characterization showed that for a window of working pressures between 300 and 500 mTorr, the deposited films were polycrystalline, with strong preferential orientation of grains along the c-axis. The film deposited at 400 mTorr had the highest (002) peak with the largest estimated grain size. Outside this window, the crystallinity and c-orientation of grains are lost. The microstructure of the films was investigated by Atomic Force microscopy (AFM). Optical transparency of the films was about 85%. The films produced were highly resistive, which might provide new alternatives for the synthesis of ZnO thin films aimed for SAW devices.

  17. Direct current magnetron sputter-deposited ZnO thin films

    International Nuclear Information System (INIS)

    Hoon, Jian-Wei; Chan, Kah-Yoong; Krishnasamy, Jegenathan; Tou, Teck-Yong; Knipp, Dietmar

    2011-01-01

    Zinc oxide (ZnO) is a very promising electronic material for emerging transparent large-area electronic applications including thin-film sensors, transistors and solar cells. We fabricated ZnO thin films by employing direct current (DC) magnetron sputtering deposition technique. ZnO films with different thicknesses ranging from 150 nm to 750 nm were deposited on glass substrates. The deposition pressure and the substrate temperature were varied from 12 mTorr to 25 mTorr, and from room temperature to 450 deg. C, respectively. The influence of the film thickness, deposition pressure and the substrate temperature on structural and optical properties of the ZnO films was investigated using atomic force microscopy (AFM) and ultraviolet-visible (UV-Vis) spectrometer. The experimental results reveal that the film thickness, deposition pressure and the substrate temperature play significant role in the structural formation and the optical properties of the deposited ZnO thin films.

  18. Control of the optical properties of silicon and chromium mixed oxides deposited by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Vergara, L.; Galindo, R. Escobar; Martinez, R.; Sanchez, O.; Palacio, C.; Albella, J.M.

    2011-01-01

    The development of mixed-oxide thin films allows obtaining materials with better properties than those of the different binary oxides, which makes them suitable for a great number of applications in different fields, such as tribology, optics or microelectronics. In this paper we investigate the deposition of mixed chromium and silicon oxides deposited by reactive magnetron sputtering with a view to use them as optical coatings with an adjustable refractive index. These films have been characterized by means of Rutherford backscattering spectrometry, Auger electron spectroscopy, X-ray diffraction, scanning electron microscopy, Fourier-transform infrared spectroscopy and spectroscopic ellipsometry so as to determine how the deposition conditions influence the characteristics of the material. We have found that the deposition parameter whose influence determines the properties of the films to a greater extent is the amount of oxygen in the reactive sputtering gas.

  19. Structural and morphological properties of ITO thin films grown by magnetron sputtering

    Science.gov (United States)

    Ghorannevis, Z.; Akbarnejad, E.; Ghoranneviss, M.

    2015-10-01

    Physical properties of transparent and conducting indium tin oxide (ITO) thin films grown by radiofrequency (RF) magnetron sputtering are studied systematically by changing deposition time. The X-ray diffraction (XRD) data indicate polycrystalline thin films with grain orientations predominantly along the (2 2 2) and (4 0 0) directions. From atomic force microscopy (AFM) it is found that by increasing the deposition time, the roughness of the film increases. Scanning electron microscopy (SEM) images show a network of a high-porosity interconnected nanoparticles, which approximately have a pore size ranging between 20 and 30 nm. Optical measurements suggest an average transmission of 80 % for the ITO films. Sheet resistances are investigated using four-point probes, which imply that by increasing the film thickness the resistivities of the films decrease to 2.43 × 10-5 Ω cm.

  20. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    Directory of Open Access Journals (Sweden)

    Damon Rafieian

    2015-09-01

    Full Text Available We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to anatase or rutile, depending on the initial sputtering conditions. Substoichiometric films (TiOx<2, obtained by sputtering at relatively low oxygen concentration, formed rutile upon annealing in air, whereas stoichiometric films formed anatase. This route therefore presents a formation route for rutile films via lower (<500 °C temperature pathways. The dynamics of the annealing process were followed by in situ ellipsometry, showing the optical properties transformation. The final crystal structures were identified by XRD. The anatase film obtained by this deposition method displayed high carriers mobility as measured by time-resolved microwave conductance. This also confirms the high photocatalytic activity of the anatase films.

  1. Ionic conductivity and thermal stability of magnetron-sputtered nanocrystalline yttria-stabilized zirconia

    DEFF Research Database (Denmark)

    Sillassen, M.; Eklund, P.; Sridharan, M.

    2009-01-01

    Thermally stable, stoichiometric, cubic yttria-stabilized zirconia (YSZ) thin-film electrolytes have been synthesized by reactive pulsed dc magnetron sputtering from a Zr–Y (80/20 at. %) alloy target. Films deposited at floating potential had a texture. Single-line profile analysis of the 111 x.......5% at bias voltages of −175 and −200 V with additional incorporation of argon. The films were thermally stable; very limited grain coarsening was observed up to an annealing temperature of 800 °C. Temperature-dependent impedance spectroscopy analysis of the YSZ films with Ag electrodes showed that the in......-plane ionic conductivity was within one order of magnitude higher in films deposited with substrate bias corresponding to a decrease in grain size compared to films deposited at floating potential. This suggests that there is a significant contribution to the ionic conductivity from grain boundaries...

  2. Effect of sputtering power on structure and properties of Bi film deposited by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Liao Guo; He Zhibing; Xu Hua; Li Jun; Chen Taihua; Chen Jiajun

    2012-01-01

    Bi film was fabricated at different sputtering powers by DC magnetron sputtering. The deposition rate of Bi film as the function of sputtering power was studied. The surface topography of Bi film was observed by SEM, and the growth mode of Bi film was investigated. The crystal structure was analyzed by XRD. The grain size and stress of Bi film were calculated. The SEM images show that all the films are columnar growth. The average grain size firstly increases as the sputtering power increases, then decreases at 60 W. The film becomes loose with the increase of sputtering power, while, the film gets compact when the sputtering power becomes from 45 to 60 W. The XRD results show that films are polycrystalline of hexagonal. And the stress transforms from the tensile stress to compressive stress as the sputtering power increases. (authors)

  3. Characteristics of W Doped Nanocrystalline Carbon Films Prepared by Unbalanced Magnetron Sputtering.

    Science.gov (United States)

    Park, Yong Seob; Park, Chul Min; Kim, Nam-Hoon; Kim, Jae-Moon

    2016-05-01

    Nanocrystalline tungsten doped carbon (WC) films were prepared by unbalanced magnetron sputtering. Tungsten was used as the doping material in carbon thin films with the aim of application as a contact strip in an electric railway. The structural, physical, and electrical properties of the fabricated WC films with various DC bias voltages were investigated. The films had a uniform and smooth surface. Hardness and frication characteristics of the films were improved, and the resistivity and sheet resistance decreased with increasing negative DC bias voltage. These results are associated with the nanocrystalline WC phase and sp(2) clusters in carbon networks increased by ion bombardment enhanced with increasing DC bias voltage. Consequently, the increase of sp(2) clusters containing WC nanocrystalline in the carbon films is attributed to the improvement in the physical and electrical properties.

  4. Nanopatterned Silicon Substrate Use in Heterojunction Thin Film Solar Cells Made by Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Shao-Ze Tseng

    2014-01-01

    Full Text Available This paper describes a method for fabricating silicon heterojunction thin film solar cells with an ITO/p-type a-Si : H/n-type c-Si structure by radiofrequency magnetron sputtering. A short-circuit current density and efficiency of 28.80 mA/cm2 and 8.67% were achieved. Novel nanopatterned silicon wafers for use in cells are presented. Improved heterojunction cells are formed on a nanopatterned silicon substrate that is prepared with a self-assembled monolayer of SiO2 nanospheres with a diameter of 550 nm used as an etching mask. The efficiency of the nanopattern silicon substrate heterojunction cells was 31.49% greater than that of heterojunction cells on a flat silicon wafer.

  5. Structural and thermal properties of nanocrystalline CuO synthesized by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Verma, M. [Department of Chemistry, IIT Roorkee, Roorkee-247667, India and Nano Science Laboratory, Institute Instrumentation Centre, IIT Roorkee, Roorkee-247667 (India); Gupta, V. K. [Department of Chemistry, IIT Roorkee, Roorkee-247667 (India); Gautam, Y. K.; Dave, V.; Chandra, R. [Nano Science Laboratory, Institute Instrumentation Centre, IIT Roorkee, Roorkee-247667 (India)

    2014-01-28

    Recent research has shown immense application of metal oxides like CuO, MgO, CaO, Al{sub 2}O{sub 3}, etc. in different areas which includes chemical warfare agents, medical drugs, magnetic storage media and solar energy transformation. Among the metal oxides, CuO nanoparticles are of special interest because of their excellent gas sensing and catalytic properties. In this paper we report structural and thermal properties of CuO synthesized by reactive magnetron DC sputtering. The synthesized nanoparticles were characterized by X-ray diffractometer. The XRD result reveals that as DC power increased from 30W to 80W, size of the CuO nanoparticles increased. The same results have been verified through TEM analysis. Thermal properties of these particles were studied using thermogravimetry.

  6. Characterization of barium strontium titanate thin films on sapphire substrate prepared via RF magnetron sputtering system

    Science.gov (United States)

    Jamaluddin, F. W.; Khalid, M. F. Abdul; Mamat, M. H.; Zoolfakar, A. S.; Zulkefle, M. A.; Rusop, M.; Awang, Z.

    2018-05-01

    Barium Strontium Titanate (Ba0.5Sr0.5TiO3) is known to have a high dielectric constant and low loss at microwave frequencies. These unique features are useful for many electronic applications. This paper focuses on material characterization of BST thin films deposited on sapphire substrate by RF magnetron sputtering system. The sample was then annealed at 900 °C for two hours. Several methods were used to characterize the structural properties of the material such as X-ray diffraction (XRD) and atomic force microscopy (AFM). Field emission scanning electron microscopy (FESEM) was used to analyze the surface morphology of the thin film. From the results obtained, it can be shown that the annealed sample had a rougher surface and better crystallinity as compared to as-deposited sample.

  7. Direct current magnetron sputtering deposition of InN thin films

    International Nuclear Information System (INIS)

    Cai Xingmin; Hao Yanqing; Zhang Dongping; Fan Ping

    2009-01-01

    In this paper, InN thin films were deposited on Si (1 0 0) and K9 glass by reactive direct current magnetron sputtering. The target was In metal with the purity of 99.999% and the gases were Ar (99.999%) and N 2 (99.999%). The properties of InN thin films were studied. Scanning electron microscopy (SEM) shows that the film surface is very rough and energy dispersive X-ray spectroscopy (EDX) shows that the film contains In, N and very little O. X-ray diffraction (XRD) and Raman scattering reveal that the film mainly contains hexagonal InN. The four-probe measurement shows that InN film is conductive. The transmission measurement demonstrates that the transmission of InN deposited on K9 glass is as low as 0.5% from 400 nm to 800 nm.

  8. RF magnetron-sputtered coatings deposited from biphasic calcium phosphate targets for biomedical implant applications

    Directory of Open Access Journals (Sweden)

    K.A. Prosolov

    2017-09-01

    Full Text Available Bioactive calcium phosphate coatings were deposited by radio-frequency magnetron sputtering from biphasic targets of hydroxyapatite and tricalcium phosphate, sintered at different mass % ratios. According to Raman scattering and X-ray diffraction data, the deposited hydroxyapatite coatings have a disordered structure. High-temperature treatment of the coatings in air leads to a transformation of the quasi-amorphous structure into a crystalline one. A correlation has been observed between the increase in the Ca content in the coatings and a subsequent decrease in Ca in the biphasic targets after a series of deposition processes. It was proposed that the addition of tricalcium phosphate to the targets would led to a finer coating's surface topography with the average size of 78 nm for the structural elements.

  9. Experimental investigation on photoelectric properties of ZAO thin film deposited on flexible substrate by magnetron sputtering

    Science.gov (United States)

    Hao, Ming; Liu, Kun; Liu, Xinghua; Wang, Dongyang; Ba, Dechun; Xie, Yuanhua; Du, Guangyu; Ba, Yaoshuai

    2016-12-01

    Transparent conductive ZAO (Zinc Aluminum Oxide) films on flexible substrates have a great potential for low-cost mass-production solar cells. ZAO thin films were achieved on flexible PET (polyethylene terephthalate) substrates by RF magnetron sputtering technology. The surface morphology and element content, the transmittance and the sheet resistance of the films were measured to determine the optical process parameters. The results show that the ZAO thin film shows the best parameters in terms of photoelectric performance including sputtering power, working pressure, sputtering time, substrate temperature (100 W, 1.5 Pa, 60 min, 125 °C). The sheet resistance of 510 Ω and transmittance in visible region of 92% were obtained after characterization. Surface morphology was uniform and compact with a good crystal grain.

  10. Deposition and characterization of TaAIN thin films by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Oliveira, G.B.; Fernandez, D.R.; Fontes Junior, A.S.; Felix, L.C.; Tentardini, E.K.; Silva Junior, A.H. da

    2016-01-01

    Phase stability, oxidation resistance and great mechanical properties are the main objectives when synthesizing protective coatings. The tantalum nitride (TaN) has aroused interest because of its high temperature stability, chemical inertness and thermal conductivity. However, it has a low hardness value when compared to other coatings. Researches has shown that one way to improvements in the properties of a thin film is by adding other elements in the deposition process. Therefore, the objective of this study was to deposit thin films of TaAlN by magnetron sputtering, changing the aluminum concentration of 2, 5, 7, to 14%. Then the coatings were characterized by EDS, RBS, GIXRD and nanohardness. In this study was found that the aluminum deposited did not change the oxidation resistance of the coating, and the highest value of hardness was 28 GPa for the sample with 14 at.%. (author)

  11. Fabricating Pinhole-Free YSZ Sub-Microthin Films by Magnetron Sputtering for Micro-SOFCs

    Directory of Open Access Journals (Sweden)

    T. Hill

    2011-01-01

    Full Text Available Submicron thin yttria stabilized zirconia (YSZ films were prepared on a variety of substrates with different surface morphologies by magnetron sputtering followed by thermal oxidation. Pinholes were observed in the films deposited on nanoporous alumina substrates. Initial dense Y/Zr films developed nanocracks after thermal oxidation on smooth Si wafer substrates. At optimal sputtering and oxidation conditions, smooth and crack/pore-free films were achieved on Si wafer substrates. The thin YSZ films exhibited fully ionic conduction with ionic conductivities, and activation energy corroborated well with the values from commercial YSZ plates. The thin YSZ films can be utilized in Solid Oxide Fuel Cells (SOFCs for intermediate temperature operations.

  12. RF Magnetron Sputtering Deposited W/Ti Thin Film For Smart Window Applications

    Science.gov (United States)

    Oksuz, Lutfi; Kiristi, Melek; Bozduman, Ferhat; Uygun Oksuz, Aysegul

    2014-10-01

    Electrochromic (EC) devices can change reversible and persistent their optical properties in the visible region (400-800 nm) upon charge insertion/extraction according to the applied voltage. A complementary type EC is a device containing two electrochromic layers, one of which is anodically colored such as vanadium oxide (V2 O5) while the other cathodically colored such as tungsten oxide (WO3) which is separated by an ionic conduction layer (electrolyte). The use of a solid electrolyte such as Nafion eliminates the need for containment of the liquid electrolyte, which simplifies the cell design, as well as improves safety and durability. In this work, the EC device was fabricated on a ITO/glass slide. The WO3-TiO2 thin film was deposited by reactive RF magnetron sputtering using a 2-in W/Ti (9:1%wt) target with purity of 99.9% in a mixture gas of argon and oxygen. As a counter electrode layer, V2O5 film was deposited on an ITO/glass substrate using V2O3 target with the same conditions of reactive RF magnetron sputtering. Modified Nafion was used as an electrolyte to complete EC device. The transmittance spectra of the complementary EC device was measured by optical spectrophotometry when a voltage of +/-3 V was applied to the EC device by computer controlled system. The surface morphology of the films was characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM) (Fig. 2). The cyclic voltammetry (CV) for EC device was performed by sweeping the potential between +/-3 V at a scan rate of 50 mV/s.

  13. Fractal features of CdTe thin films grown by RF magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Hosseinpanahi, Fayegh, E-mail: f.hosseinpanahi@yahoo.com [Department of Physics, Payame Noor University, P.O. Box 19395-4697, Tehran (Iran, Islamic Republic of); Raoufi, Davood [Department of Physics, University of Bu Ali Sina, P.O. Box 65174, Hamedan (Iran, Islamic Republic of); Ranjbarghanei, Khadijeh [Department of Physics, Plasma Physics Research Center, Science & Research Branch Islamic Azad University, Tehran (Iran, Islamic Republic of); Karimi, Bayan [Department of Physics, Payame Noor University, P.O. Box 19395-4697, Tehran (Iran, Islamic Republic of); Babaei, Reza [Department of Physics, Plasma Physics Research Center, Science & Research Branch Islamic Azad University, Tehran (Iran, Islamic Republic of); Hasani, Ebrahim [Department of Physics, University of Bu Ali Sina, P.O. Box 65174, Hamedan (Iran, Islamic Republic of)

    2015-12-01

    Graphical abstract: - Highlights: • CdTe thin films were deposited on glass substrates by RF magnetron sputtering at room temperature with different deposition time 5, 10 and 15 min. • Nanostructure of CdTe layer indicates that CdTe films are polycrystalline and have zinc blende structure, irrespective of their deposition time. • Complexity and roughness of the CdTe films and strength of multifractality increase with increasing deposition time. • Detrended fluctuation analysis (DFA) and also multifractal detrended fluctuation analysis (MFDFA) methods showed that prepared CdTe films have multifractal nature. - Abstract: Cadmium telluride (CdTe) thin films were prepared by RF magnetron sputtering on glass substrates at room temperature (RT). The film deposition was performed for 5, 10, and 15 min at power of 30 W with a frequency of 13.56 MHz. The crystal structure of the prepared CdTe thin films was studied by X-ray diffraction (XRD) technique. XRD analyses indicate that the CdTe films are polycrystalline, having zinc blende structure of CdTe irrespective of their deposition time. All CdTe films showed a preferred orientation along (1 1 1) crystalline plane. The surface morphology characterization of the films was studied using atomic force microscopy (AFM). The quantitative AFM characterization shows that the RMS surface roughness of the prepared CdTe thin films increases with increasing the deposition time. The detrended fluctuation analysis (DFA) and also multifractal detrended fluctuation analysis (MFDFA) methods showed that prepared CdTe thin films have multifractal nature. The complexity, roughness of the CdTe thin films and strength of the multifractality increase as deposition time increases.

  14. Bioactivity response of Ta_1_-_xO_x coatings deposited by reactive DC magnetron sputtering

    International Nuclear Information System (INIS)

    Almeida Alves, C.F.; Cavaleiro, A.; Carvalho, S.

    2016-01-01

    The use of dental implants is sometimes accompanied by failure due to periimplantitis disease and subsequently poor esthetics when soft–hard tissue margin recedes. As a consequence, further research is needed for developing new bioactive surfaces able to enhance the osseous growth. Tantalum (Ta) is a promising material for dental implants since, comparing with titanium (Ti), it is bioactive and has an interesting chemistry which promotes the osseointegration. Another promising approach for implantology is the development of implants with oxidized surfaces since bone progenitor cells interact with the oxide layer forming a diffusion zone due to its ability to bind with calcium which promotes a stronger bond. In the present report Ta-based coatings were deposited by reactive DC magnetron sputtering onto Ti CP substrates in an Ar + O_2 atmosphere. In order to assess the osteoconductive response of the studied materials, contact angle and in vitro tests of the samples immersed in Simulated Body Fluid (SBF) were performed. Structural results showed that oxide phases where achieved with larger amounts of oxygen (70 at.% O). More compact and smooth coatings were deposited by increasing the oxygen content. The as-deposited Ta coating presented the most hydrophobic character (100°); with increasing oxygen amount contact angles progressively diminished, down to the lowest measured value, 63°. The higher wettability is also accompanied by an increase on the surface energy. Bioactivity tests demonstrated that highest O-content coating, in good agreement with wettability and surface energy values, showed an increased affinity for apatite adhesion, with higher Ca/P ratio formation, when compared to the bare Ti substrates. - Highlights: • Ta_1_-_xO_x coatings were deposited by reactive DC magnetron sputtering. • Amorphous oxide phases were achieved with higher oxygen amounts. • Contact angles progressively diminished, with increasing oxygen content. • Ta oxide surface

  15. Understanding deposition rate loss in high power impulse magnetron sputtering: I. Ionization-driven electric fields

    International Nuclear Information System (INIS)

    Brenning, N; Huo, C; Raadu, M A; Lundin, D; Helmersson, U; Vitelaru, C; Stancu, G D; Minea, T

    2012-01-01

    The lower deposition rate for high power impulse magnetron sputtering (HiPIMS) compared with direct current magnetron sputtering for the same average power is often reported as a drawback. The often invoked reason is back-attraction of ionized sputtered material to the target due to a substantial negative potential profile, sometimes called an extended presheath, from the location of ionization toward the cathode. Recent studies in HiPIMS devices, using floating-emitting and swept-Langmuir probes, show that such extended potential profiles do exist, and that the electric fields E z directed toward the target can be strong enough to seriously reduce ion transport to the substrate. However, they also show that the potential drops involved can vary by up to an order of magnitude from case to case. There is a clear need to understand the underlying mechanisms and identify the key discharge variables that can be used for minimizing the back-attraction. We here present a combined theoretical and experimental analysis of the problem of electric fields E z in the ionization region part of HiPIMS discharges, and their effect on the transport of ionized sputtered material. In particular, we have investigated the possibility of a ‘sweet spot’ in parameter space in which the back-attraction of ionized sputtered material is low. It is concluded that a sweet spot might possibly exist for some carefully optimized discharges, but probably in a rather narrow window of parameters. As a measure of how far a discharge is from such a window, a Townsend product Π Townsend is proposed. A parametric analysis of Π Townsend shows that the search for a sweet spot is complicated by the fact that contradictory demands appear for several of the externally controllable parameters such as high/low working gas pressure, short/long pulse length, high/low pulse power and high/low magnetic field strength. (paper)

  16. Metal-oxide-junction, triple point cathodes in a relativistic magnetron

    International Nuclear Information System (INIS)

    Jordan, N. M.; Gilgenbach, R. M.; Hoff, B. W.; Lau, Y. Y.

    2008-01-01

    Triple point, defined as the junction of metal, dielectric, and vacuum, is the location where electron emission is favored in the presence of a sufficiently strong electric field. To exploit triple point emission, metal-oxide-junction (MOJ) cathodes consisting of dielectric ''islands'' over stainless steel substrates have been fabricated. The two dielectrics used are hafnium oxide (HfO x ) for its high dielectric constant and magnesium oxide (MgO) for its high secondary electron emission coefficient. The coatings are deposited by ablation-plasma-ion lithography using a KrF laser (0-600 mJ at 248 nm) and fluence ranging from 3 to 40 J/cm 2 . Composition and morphology of deposited films are analyzed by scanning electron microscopy coupled with x-ray energy dispersive spectroscopy, as well as x-ray diffraction. Cathodes are tested on the Michigan Electron Long-Beam Accelerator with a relativistic magnetron, at parameters V=-300 kV, I=1-15 kA, and pulse lengths of 0.3-0.5 μs. Six variations of the MOJ cathode are tested, and are compared against five baseline cases. It is found that particulate formed during the ablation process improves the electron emission properties of the cathodes by forming additional triple points. Due to extensive electron back bombardment during magnetron operation, secondary electron emission also may play a significant role. Cathodes exhibit increases in current densities of up to 80 A/cm 2 , and up to 15% improvement in current start up time, as compared to polished stainless steel cathodes

  17. Titanium dioxide (TIO2) thin film and plasma properties in RF magnetron sputtering

    International Nuclear Information System (INIS)

    Ali, Riyaz Ahmad Mohamed; Nayan, Nafarizal

    2013-01-01

    Lately, titanium dioxide (TiO 2 ) films with anatase crystalline property received numerous attentions as unique material properties. There are wide applications of TiO 2 thin film such as for photocatalytic application in solar cell. In the present study, radio frequency (RF) magnetron sputtering technique has been used to produce high dense, homogeneously controllable film layer at low deposition temperature using titanium (Ti) target. The diameter of the Ti target is 3 inch with fixed discharge power of 400W. Magnetron sputtering plasma has been produced in high purity 99.99% Argon (Ar) and 99.99% Oxygen (O 2 ) environment pressure ranging from 5 to 20 mTorr. The TiO2 were growth on silicon and glass substrates. Substrate temperature during deposition was kept constant at 400°C. The distance between target and substrate holder was maintain at 14 cm with rotation of 10 rotation-per-minutes. Our X-ray diffraction result, shows anatase crystalline successfully formed with characterization peaks of plane (101) at 2θ = 25.28°, plane (202) at 2θ = 48.05° and plane (211) at 2θ = 55.06°. In addition, it is our interest to study the plasma properties and optical spectrum of Ti, Ti+ , O- , ArM and Ar+ in the chamber during the deposition process. Result of emission line intensities, electron density and temperature from optical spectroscope and Langmuir probe will be discuss further during the workshop. This works were supported by Graduate Incentive Scheme of Universiti Tun Hussein Onn Malaysia (UTHM) and Fundamental Research Grant Scheme of Ministry of Higher Education, Malaysia. (author)

  18. Electrochromic properties of bipolar pulsed magnetron sputter deposited tungsten–molybdenum oxide films

    Energy Technology Data Exchange (ETDEWEB)

    Lin, Tai-Nan [Chemical Engineering Division, Institute of Nuclear Energy Research, Taoyuan 325, Taiwan, ROC (China); Lin, Yi Han; Lee, Chin Tan [Department of Electronic Engineering, National Quemoy University, Kinmen 892, Taiwan, ROC (China); Han, Sheng [Center of General Education, National Taichung Institute of Technology, Taichung 404, Taiwan, ROC (China); Weng, Ko-Wei, E-mail: kowei@nqu.edu.tw [Department of Electronic Engineering, National Quemoy University, Kinmen 892, Taiwan, ROC (China)

    2015-06-01

    There are great interests in electrochromic technology for smart windows and displays over past decades. In this study, the WMoO{sub x} thin films were deposited onto indium tin oxide glass and silicon substrates by pulsed magnetron sputter system with W and Mo targets. The films were deposited with fixed W target power while the variant parameter of Mo target power in the range 50, 100, 150 and 200 W was investigated. The working pressure was fixed at 1.33 Pa with a gas mixture of Ar (30 sccm) and O{sub 2} (15 sccm). The film thickness increased with the Mo target power. Higher plasma power resulted in a crystalline structure which would reduce the electrochromic property of the film. The influence of plasma powers applied to Mo target on the structural, optical and electrochromic properties of the WMoO{sub x} thin films has been investigated. WMoO{sub x} films grown at Mo target powers less than 100 W were found to be amorphous. The films deposited at 150 W, which is the optimal fabrication condition, exhibit better electrochromic properties with high optical modulation, high coloration efficiency and less color memory effect at wavelength 400, 550 and 800 nm. The improvement resulted from the effect of doping Mo has been tested. The maximum ΔT (%) values are 36.6% at 400 nm, 65.6% at 550 nm, and 66.6% at 800 nm for pure WO{sub 3} film. The addition of Mo content in the WMoO{sub x} films provides better resistance to the short wavelength light source and can be used in the concerned application. - Highlights: • WMoO{sub x} films are deposited by pulsed magnetron sputter with pure W and Mo targets. • Mo addition in WMoO{sub x} provides better resistance to short wavelength light source. • WMoO{sub x} films exhibit electrochemical stability in the cycling test.

  19. Compositionally graded SiCu thin film anode by magnetron sputtering for lithium ion battery

    Energy Technology Data Exchange (ETDEWEB)

    Polat, B.D., E-mail: bpolat@itu.edu.tr [Department of Metallurgical and Materials Engineering, Istanbul Technical University, Maslak, Istanbul 34469 (Turkey); Eryilmaz, O.L. [Energy Systems Division, Argonne National Laboratory, Argonne, IL 60439 (United States); Keleş, O., E-mail: ozgulkeles@itu.edu.tr [Department of Metallurgical and Materials Engineering, Istanbul Technical University, Maslak, Istanbul 34469 (Turkey); Erdemir, A. [Energy Systems Division, Argonne National Laboratory, Argonne, IL 60439 (United States); Amine, K. [Chemical Sciences and Engineering Division, Argonne National Laboratory, Argonne, IL 60439 (United States)

    2015-12-01

    Compositionally graded and non-graded composite SiCu thin films were deposited by magnetron sputtering technique on Cu disks for investigation of their potentials in lithium ion battery applications. The compositionally graded thin film electrodes with 30 at.% Cu delivered a 1400 mAh g{sup −1} capacity with 80% Coulombic efficiency in the first cycle and still retained its capacity at around 600 mAh g{sup −1} (with 99.9% Coulombic efficiency) even after 100 cycles. On the other hand, the non-graded thin film electrodes with 30 at.% Cu exhibited 1100 mAh g{sup −1} as the first discharge capacity with 78% Coulombic efficiency but the cycle life of this film degraded very quickly, delivering only 250 mAh g{sup −1} capacity after 100th cycles. Not only the Cu content but also the graded film thickness were believed to be the main contributors to the much superior performance of the compositionally graded SiCu films. We also believe that the Cu-rich region of the graded film helped reduce internal stress build-up and thus prevented film delamination during cycling. In particular, the decrease of Cu content from interface region to the top of the coating reduced the possibility of stress build-up across the film during cycling, thus leading to a high electrochemical performance.b - Highlights: • Highly adherent SiCu films are deposited by magnetron sputtering. • Compositionally graded SiCu film is produced and characterized. • Decrease of Cu content diverted the propagation of stress in the anode. • Cu rich layer at the bottom improves the adherence of the film.

  20. Turbostratic-like carbon nitride coatings deposited by industrial-scale direct current magnetron sputtering

    International Nuclear Information System (INIS)

    Louring, S.; Madsen, N.D.; Berthelsen, A.N.; Christensen, B.H.; Almtoft, K.P.; Nielsen, L.P.; Bøttiger, J.

    2013-01-01

    Carbon nitride thin films were deposited by direct current magnetron sputtering in an industrial-scale equipment at different deposition temperatures and substrate bias voltages. The films had N/(N + C) atomic fractions between 0.2 and 0.3 as determined by X-ray photoelectron spectroscopy (XPS). Raman spectroscopy provided insight into the ordering and extension of the graphite-like clusters, whereas nanoindentation revealed information on the mechanical properties of the films. The internal compressive film stress was evaluated from the substrate bending method. At low deposition temperatures the films were amorphous, whereas the film deposited at approximately 380 °C had a turbostratic-like structure as confirmed by high-resolution transmission electron microscopy images. The turbostratic-like film had a highly elastic response when subjected to nanoindentation. When a CrN interlayer was deposited between the film and the substrate, XPS and Raman spectroscopy indicated that the turbostratic-like structure was maintained. However, it was inconclusive whether the film still exhibited an extraordinary elastic recovery. An increased substrate bias voltage, without additional heating and without deposition of an interlayer, resulted in a structural ordering, although not to the extent of a turbostratic-like structure. - Highlights: • Carbon nitride films were deposited by industrial-scale magnetron sputtering. • The deposition temperature and the substrate bias voltage were varied. • A turbostratic-like structure was obtained at an elevated deposition temperature. • The turbostratic-like film exhibited a very high elastic recovery. • The influence of a CrN interlayer on the film properties was investigated

  1. Structure dependent resistivity and dielectric characteristics of tantalum oxynitride thin films produced by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Cristea, D., E-mail: daniel.cristea@unitbv.ro [Department of Materials Science, Transilvania University, 500036 Brasov (Romania); Crisan, A. [Department of Materials Science, Transilvania University, 500036 Brasov (Romania); Cretu, N. [Electrical Engineering and Applied Physics Department, Transilvania University, 500036 Brasov (Romania); Borges, J. [Centro de Física, Universidade do Minho, Campus de Gualtar, 4710 - 057 Braga (Portugal); Instituto Pedro Nunes, Laboratório de Ensaios, Desgaste e Materiais, Rua Pedro Nunes, 3030-199 Coimbra (Portugal); SEG-CEMUC, Mechanical Engineering Department, University of Coimbra, 3030-788 Coimbra (Portugal); Lopes, C.; Cunha, L. [Centro de Física, Universidade do Minho, Campus de Gualtar, 4710 - 057 Braga (Portugal); Ion, V.; Dinescu, M. [National Institute for Lasers, Plasma and Radiation Physics, Lasers Department, “Photonic Processing of Advanced Materials” Group, PO Box MG-16, RO 77125 Magurele-Bucharest (Romania); Barradas, N.P. [Centro de Ciências e Tecnologias Nucleares, Instituto Superior Técnico, Universidade de Lisboa, E.N. 10 ao km 139,7, 2695-066 Bobadela LRS (Portugal); Alves, E. [Instituto de Plasmas e Fusão Nuclear, Instituto Superior Técnico, Universidade de Lisboa, E.N. 10 ao km 139,7, 2695-066 Bobadela LRS (Portugal); Apreutesei, M. [MATEIS Laboratory-INSA de Lyon, 21 Avenue Jean Capelle, 69621 Villeurbanne cedex (France); Université de Lyon, Institut des Nanotechnologies de Lyon INL-UMR5270, CNRS, Ecole Centrale de Lyon, Ecully F-69134 (France); Munteanu, D. [Department of Materials Science, Transilvania University, 500036 Brasov (Romania)

    2015-11-01

    Highlights: • Tantalum oxynitride thin films have been deposited by magnetron sputtering, in various configurations. • The rising of the reactive gases mixture flow has the consequence of a gradual increase in the non-metallic content in the films, which results in a 10 orders of magnitude resistivity domain. • The higher resistivity films exhibit dielectric constants up to 41 and quality factors up to 70. - Abstract: The main purpose of this work is to present and to interpret the change of electrical properties of Ta{sub x}N{sub y}O{sub z} thin films, produced by DC reactive magnetron sputtering. Some parameters were varied during deposition: the flow of the reactive gases mixture (N{sub 2} and O{sub 2}, with a constant concentration ratio of 17:3); the substrate voltage bias (grounded, −50 V or −100 V) and the substrate (glass, (1 0 0) Si or high speed steel). The obtained films exhibit significant differences. The variation of the deposition parameters induces variations of the composition, microstructure and morphology. These differences cause variation of the electrical resistivity essentially correlated with the composition and structural changes. The gradual decrease of the Ta concentration in the films induces amorphization and causes a raise of the resistivity. The dielectric characteristics of some of the high resistance Ta{sub x}N{sub y}O{sub z} films were obtained in the samples with a capacitor-like design (deposited onto high speed steel, with gold pads deposited on the dielectric Ta{sub x}N{sub y}O{sub z} films). Some of these films exhibited dielectric constant values higher than those reported for other tantalum based dielectric films.

  2. Properties of reactively radio frequency-magnetron sputtered (Zr,Sn)TiO4 dielectric films

    International Nuclear Information System (INIS)

    Huang, C.-L.; Hsu, C.-H.

    2004-01-01

    Zirconium tin titanium oxide doped 1 wt % ZnO thin films on n-type Si substrate were deposited by rf magnetron sputtering at a fixed rf power of 350 W with various argon-oxygen (Ar/O 2 ) mixture and different substrate temperatures. Electrical properties and microstructures of ZnO-doped (Zr 0.8 Sn 0.2 )TiO 4 thin films prepared by rf magnetron sputtering on n-type Si(100) substrates at different Ar/O 2 ratios and substrate temperatures have been investigated. The surface structural and morphological characteristics analyzed by x-ray diffraction, scanning electron microscopy, and atomic force microscope were sensitive to the deposition conditions, such as Ar/O 2 ratio (100/0-80/20) and substrate temperature (350 deg. C-450 deg. C). The selected-area diffraction pattern showed that the deposited films exhibited a polycrystalline microstructure. All films exhibited ZST (111) orientation perpendicular to the substrate surface and the grain size as well as the deposition rate of the films increased with the increase of both the Ar partial pressure and the substrate temperature. At a Ar/O 2 ratio of 100/0, rf power level of 350 W and substrate temperature of 450 deg. C, the Zr 0.8 Sn 0.2 TiO 4 films with 6.44 μm thickness possess a dielectric constant of 42 (at 10 MHz), a dissipation factor of 0.065 (at 10 MHz), and a leakage current density of 2x10 -7 A/cm 2 at an electrical field of 1 kV/cm

  3. A Magnetron Sputter Deposition System for the Development of X-Ray Multilayer Optics

    Science.gov (United States)

    Broadway, David

    2015-01-01

    The project objective is to establish the capability to deposit multilayer structures for x-ray, neutron, and extreme ultraviolet (EUV) optic applications through the development of a magnetron sputtering deposition system. A specific goal of this endeavor is to combine multilayer deposition technology with the replication process in order to enhance NASA Marshall Space Flight Center's (MSFC's) position as a world leader in the design of innovative x-ray instrumentation through the development of full shell replicated multilayer optics. The development of multilayer structures are absolutely necessary in order to advance the field of x-ray astronomy by pushing the limit for observing the universe to ever-increasing photon energies (i.e., up to 200 keV or higher), well beyond Chandra's (approx.10 keV) and NuStar's (approx.75 keV) capability. The addition of multilayer technology would significantly enhance the x-ray optics capability at MSFC and allow NASA to maintain its world leadership position in the development, fabrication, and design of innovative x-ray instrumentation, which would be the first of its kind by combining multilayer technology with the mirror replication process. This marriage of these technologies would allow astronomers to see the universe in a new light by pushing to higher energies that are out of reach with today's instruments. To this aim, a magnetron vacuum sputter deposition system for the deposition of novel multilayer thin film x-ray optics is proposed. A significant secondary use of the vacuum deposition system includes the capability to fabricate multilayers for applications in the field of EUV optics for solar physics, neutron optics, and x-ray optics for a broad range of applications including medical imaging.

  4. A Magnetron Sputter Deposition System for the Development of Multilayer X-Ray Optics

    Science.gov (United States)

    Broadway, David; Ramsey, Brian; Gubarev, Mikhail

    2014-01-01

    The proposal objective is to establish the capability to deposit multilayer structures for x-ray, neutron, and EUV optic applications through the development of a magnetron sputtering deposition system. A specific goal of this endeavor is to combine multilayer deposition technology with the replication process in order to enhance the MSFC's position as a world leader in the design of innovative X-ray instrumentation through the development of full shell replicated multilayer optics. The development of multilayer structures is absolutely necessary in order to advance the field of X-ray astronomy by pushing the limit for observing the universe to ever increasing photon energies (i. e. up to 200 keV or higher); well beyond Chandra (approx. 10 keV) and NuStar's (approx. 75 keV) capability. The addition of multilayer technology would significantly enhance the X-ray optics capability at MSFC and allow NASA to maintain its world leadership position in the development, fabrication and design of innovative X-ray instrumentation which would be the first of its kind by combining multilayer technology with the mirror replication process. This marriage of these technologies would allow astronomers to see the universe in a new light by pushing to higher energies that are out of reach with today's instruments.To this aim, a magnetron vacum sputter deposition system for the deposition of novel multilayer thin film X-ray optics is proposed. A significant secondary use of the vacuum deposition system includes the capability to fabricate multilayers for applications in the field of EUV optics for solar physics, neutron optics, and X-ray optics for a broad range of applications including medical imaging.

  5. Fractal features of CdTe thin films grown by RF magnetron sputtering

    International Nuclear Information System (INIS)

    Hosseinpanahi, Fayegh; Raoufi, Davood; Ranjbarghanei, Khadijeh; Karimi, Bayan; Babaei, Reza; Hasani, Ebrahim

    2015-01-01

    Graphical abstract: - Highlights: • CdTe thin films were deposited on glass substrates by RF magnetron sputtering at room temperature with different deposition time 5, 10 and 15 min. • Nanostructure of CdTe layer indicates that CdTe films are polycrystalline and have zinc blende structure, irrespective of their deposition time. • Complexity and roughness of the CdTe films and strength of multifractality increase with increasing deposition time. • Detrended fluctuation analysis (DFA) and also multifractal detrended fluctuation analysis (MFDFA) methods showed that prepared CdTe films have multifractal nature. - Abstract: Cadmium telluride (CdTe) thin films were prepared by RF magnetron sputtering on glass substrates at room temperature (RT). The film deposition was performed for 5, 10, and 15 min at power of 30 W with a frequency of 13.56 MHz. The crystal structure of the prepared CdTe thin films was studied by X-ray diffraction (XRD) technique. XRD analyses indicate that the CdTe films are polycrystalline, having zinc blende structure of CdTe irrespective of their deposition time. All CdTe films showed a preferred orientation along (1 1 1) crystalline plane. The surface morphology characterization of the films was studied using atomic force microscopy (AFM). The quantitative AFM characterization shows that the RMS surface roughness of the prepared CdTe thin films increases with increasing the deposition time. The detrended fluctuation analysis (DFA) and also multifractal detrended fluctuation analysis (MFDFA) methods showed that prepared CdTe thin films have multifractal nature. The complexity, roughness of the CdTe thin films and strength of the multifractality increase as deposition time increases.

  6. Magnetron Sputtering as a Fabrication Method for a Biodegradable Fe32Mn Alloy

    Directory of Open Access Journals (Sweden)

    Till Jurgeleit

    2017-10-01

    Full Text Available Biodegradable metals are a topic of great interest and Fe-based materials are prominent examples. The research task is to find a suitable compromise between mechanical, corrosion, and magnetic properties. For this purpose, investigations regarding alternative fabrication processes are important. In the present study, magnetron sputtering technology in combination with UV-lithography was used in order to fabricate freestanding, microstructured Fe32Mn films. To adjust the microstructure and crystalline phase composition with respect to the requirements, the foils were post-deposition annealed under a reducing atmosphere. The microstructure and crystalline phase composition were investigated by scanning electron microscopy, energy dispersive X-ray spectroscopy, and X-ray diffraction. Furthermore, for mechanical characterization, uniaxial tensile tests were performed. The in vitro corrosion rates were determined by electrochemical polarization measurements in pseudo-physiological solution. Additionally, the magnetic properties were measured via vibrating sample magnetometry. The foils showed a fine-grained structure and a tensile strength of 712 MPa, which is approximately a factor of two higher compared to the sputtered pure Fe reference material. The yield strength was observed to be even higher than values reported in literature for alloys with similar composition. Against expectations, the corrosion rates were found to be lower in comparison to pure Fe. Since the annealed foils exist in the austenitic, and antiferromagnetic γ-phase, an additional advantage of the FeMn foils is the low magnetic saturation polarization of 0.003 T, compared to Fe with 1.978 T. This value is even lower compared to the SS 316L steel acting as a gold standard for implants, and thus enhances the MRI compatibility of the material. The study demonstrates that magnetron sputtering in combination with UV-lithography is a new concept for the fabrication of already in situ

  7. Dielectric properties of DC reactive magnetron sputtered Al2O3 thin films

    International Nuclear Information System (INIS)

    Prasanna, S.; Mohan Rao, G.; Jayakumar, S.; Kannan, M.D.; Ganesan, V.

    2012-01-01

    Alumina (Al 2 O 3 ) thin films were sputter deposited over well-cleaned glass and Si substrates by DC reactive magnetron sputtering under various oxygen gas pressures and sputtering powers. The composition of the films was analyzed by X-ray photoelectron spectroscopy and an optimal O/Al atomic ratio of 1.59 was obtained at a reactive gas pressure of 0.03 Pa and sputtering power of 70 W. X-ray diffraction results revealed that the films were amorphous until 550 °C. The surface morphology of the films was studied using scanning electron microscopy and the as-deposited films were found to be smooth. The topography of the as-deposited and annealed films was analyzed by atomic force microscopy and a progressive increase in the rms roughness of the films from 3.2 nm to 4.53 nm was also observed with increase in the annealing temperature. Al-Al 2 O 3 -Al thin film capacitors were then fabricated on glass substrates to study the effect of temperature and frequency on the dielectric property of the films. Temperature coefficient of capacitance, AC conductivity and activation energy were determined and the results are discussed. - Highlights: ► Al 2 O 3 thin films were deposited by DC reactive magnetron sputtering. ► The films were found to be amorphous up to annealing temperature of 550 C. ► An increase in rms roughness of the films was observed with annealing. ► Al-Al 2 O 3 -Al thin film capacitors were fabricated and dielectric constant was 7.5. ► The activation energy decreased with increase in frequency.

  8. Effect of electroless nickel interlayer on the electrochemical behavior of single layer CrN, TiN, TiAlN coatings and nanolayered TiAlN/CrN multilayer coatings prepared by reactive dc magnetron sputtering

    International Nuclear Information System (INIS)

    Grips, V.K. William; Ezhil Selvi, V.; Barshilia, Harish C.; Rajam, K.S.

    2006-01-01

    The electrochemical behavior of single layer TiN, CrN, TiAlN and multilayer TiAlN/CrN coatings, deposited on steel substrates using a multi-target reactive direct current (dc) magnetron sputtering process, was studied in 3.5% NaCl solution. The total thickness of the coatings was about 1.5 μm. About 0.5 μm thick chromium interlayer was used to improve adhesion of the coatings. With an aim to improve the corrosion resistance, an additional interlayer of approximately 5 μm thick electroless nickel (EN) was deposited on the substrate. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) were used to study the corrosion behavior of the coatings. Scanning electron microscopy and energy dispersive X-ray analysis were used to characterize the corroded samples. The potentiodynamic polarization tests showed lower corrosion current density and higher polarization resistance (R p ) for the coatings with EN interlayer. For example, the corrosion current density of TiN coated steel was decreased by a factor of 10 by incorporating 5 μm thick EN interlayer. Similarly, multilayer coatings of TiAlN/CrN with EN interlayer showed about 30 times improved corrosion resistance as compared to the multilayers without EN interlayer. The porosity values were calculated from the potentiodynamic polarization data. The Nyquist and the Bode plots obtained from the EIS data were fitted by appropriate equivalent circuits. The pore resistance (R pore ), the charge transfer resistance (R ct ), the coating capacitance (Q coat ) and the double layer capacitance (Q dl ) of the coatings were obtained from the equivalent circuit. Multilayer coatings showed higher R pore and R ct values as compared to the single layer coatings. Similarly, the Q coat and Q dl values decreased from uncoated substrate to the multilayer coatings, indicating a decrease in the defect density by the addition of EN interlayer. These studies were confirmed by examining the corroded samples under

  9. Discovery of 1-(4-((3-(4-methylpiperazin-1-yl)propyl)amino)benzyl)-5-(trifluoromethyl)pyridin-2(1H)-one, an orally active multi-target agent for the treatment of diabetic nephropathy.

    Science.gov (United States)

    Chen, Jun; Peng, Zhangzhe; Lu, Miaomiao; Xiong, Xuan; Chen, Zhuo; Li, Qianbin; Cheng, Zeneng; Jiang, Dejian; Tao, Lijian; Hu, Gaoyun

    2018-01-15

    Oxidative stress, inflammation and fibrosis can cause irreversible damage on cell structure and function of kidney and are key pathological factors in Diabetic Nephropathy (DN). Therefore, multi-target agents are urgently need for the clinical treatment of DN. Using Pirfenidone as a lead compound and based on the previous research, two novel series (5-trifluoromethyl)-2(1H)-pyridone analogs were designed and synthesized. SAR of (5-trifluoromethyl)-2(1H)-pyridone derivatives containing nitrogen heterocyclic ring have been established for in vitro potency. In addition, compound 8, a novel agent that act on multiple targets of anti-DN with IC 50 of 90μM in NIH3T3 cell lines, t 1/2 of 4.89±1.33h in male rats and LD 50 >2000mg/kg in mice, has been advanced to preclinical studies as an oral treatment for DN. Copyright © 2017 Elsevier Ltd. All rights reserved.

  10. Searching for Multi-Targeting Neurotherapeutics against Alzheimer’s: Discovery of Potent AChE-MAO B Inhibitors through the Decoration of the 2H-Chromen-2-one Structural Motif

    Directory of Open Access Journals (Sweden)

    Leonardo Pisani

    2016-03-01

    Full Text Available The need for developing real disease-modifying drugs against neurodegenerative syndromes, particularly Alzheimer’s disease (AD, shifted research towards reliable drug discovery strategies to unveil clinical candidates with higher therapeutic efficacy than single-targeting drugs. By following the multi-target approach, we designed and synthesized a novel class of dual acetylcholinesterase (AChE-monoamine oxidase B (MAO-B inhibitors through the decoration of the 2H-chromen-2-one skeleton. Compounds bearing a propargylamine moiety at position 3 displayed the highest in vitro inhibitory activities against MAO-B. Within this series, derivative 3h emerged as the most interesting hit compound, being a moderate AChE inhibitor (IC50 = 8.99 µM and a potent and selective MAO-B inhibitor (IC50 = 2.8 nM. Preliminary studies in human neuroblastoma SH-SY5Y cell lines demonstrated its low cytotoxicity and disclosed a promising neuroprotective effect at low doses (0.1 µM under oxidative stress conditions promoted by two mitochondrial toxins (oligomycin-A and rotenone. In a Madin-Darby canine kidney (MDCKII-MDR1 cell-based transport study, Compound 3h was able to permeate the BBB-mimicking monolayer and did not result in a glycoprotein-p (P-gp substrate, showing an efflux ratio = 0.96, close to that of diazepam.

  11. Residual stress and texture in Aluminum doped Zinc Oxide layers deposited by reactive radio frequency magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Azanza Ricardo, C.L., E-mail: Cristy.Azanza@ing.unitn.it [Department of Civil, Environmental and Mechanical Engineering, University of Trento, 38123 via Mesiano 77, Trento (Italy); Pastorelli, M.; D' Incau, M. [Department of Civil, Environmental and Mechanical Engineering, University of Trento, 38123 via Mesiano 77, Trento (Italy); Aswath, P. [College of Engineering, University of Texas at Arlington, TX (United States); Scardi, P. [Department of Civil, Environmental and Mechanical Engineering, University of Trento, 38123 via Mesiano 77, Trento (Italy)

    2016-04-30

    Aluminum doped Zinc Oxide thin films were deposited on standard soda-lime substrates by reactive radio frequency magnetron sputtering. Residual stress and texture were studied by X-ray diffraction, while X-ray Absorption Near Edge Spectroscopy provided information on the Al environment in the best performing thin films. The influence of deposition parameters on structural and microstructural properties is discussed. A correlation between microstructure and residual stress state with electrical and optical properties is proposed. - Highlights: • Al doped ZnO thin films were obtained by reactive radio frequency magnetron sputtering. • Correlation of stresses and texture with electrical and optical properties is shown. • Homogeneous and stress-free thin-films are the best performing ones. • XANES confirmed the doping mechanism and excluded some spurious phases.

  12. ZnO film deposition by DC magnetron sputtering: Effect of target configuration on the film properties

    Energy Technology Data Exchange (ETDEWEB)

    Arakelova, E.; Khachatryan, A.; Kteyan, A.; Avjyan, K.; Grigoryan, S.

    2016-08-01

    Ballistic transport model for target-to-substrate atom transfer during magnetron sputter deposition was used to develop zinc target (cathode) configuration that enabled growth of uniform zinc oxide films on extensive surfaces and provided reproducibility of films characteristics irrespective of the cathode wear-out. The advantage of the developed target configuration for high-quality ZnO film deposition was observed in the sputtering pressure range of 5− 50 mTorr, and in the range of cathode-to-substrate distances 7–20 cm. Characteristics of the deposited films were demonstrated by using X-ray diffraction analysis, as well as optical and electrical measurements. - Highlights: • Change of target configuration for optimization of magnetron sputtering deposition is proposed. • Improvement of ZnO film properties due to use of this target is demonstrated. • This configuration provided reproducibility of the deposited films properties.

  13. Nanoscale Cu{sub 2}O films: Radio-frequency magnetron sputtering and structural and optical studies

    Energy Technology Data Exchange (ETDEWEB)

    Kudryashov, D. A., E-mail: kudryashovda@apbau.ru; Gudovskikh, A. S. [Russian Academy of Sciences, St. Petersburg National Research Academic University — Nanotechnology Research and Education Center (Russian Federation); Babichev, A. V.; Filimonov, A. V. [Connector Optics LLC (Russian Federation); Mozharov, A. M. [Russian Academy of Sciences, St. Petersburg National Research Academic University — Nanotechnology Research and Education Center (Russian Federation); Agekyan, V. F.; Borisov, E. V.; Serov, A. Yu.; Filosofov, N. G. [St. Petersburg State University (Russian Federation)

    2017-01-15

    Nanoscale copper (I) oxide layers are formed by magnetron-assisted sputtering onto glassy and silicon substrates in an oxygen-free environment at room temperature, and the structural and optical properties of the layers are studied. It is shown that copper oxide formed on a silicon substrate exhibits a lower degree of disorder than that formed on a glassy substrate, which is supported by the observation of a higher intensity and a smaller half-width of reflections in the diffraction pattern. The highest intensity of reflections in the diffraction pattern is observed for Cu{sub 2}O films grown on silicon at a magnetron power of 150 W. The absorption and transmittance spectra of these Cu{sub 2}O films are in agreement with the well-known spectra of bulk crystals. In the Raman spectra of the films, phonons inherent in the crystal lattice of cubic Cu{sub 2}O crystals are identified.

  14. Silicon oxynitride films deposited by reactive high power impulse magnetron sputtering using nitrous oxide as a single-source precursor

    Energy Technology Data Exchange (ETDEWEB)

    Hänninen, Tuomas, E-mail: tuoha@ifm.liu.se; Schmidt, Susann; Jensen, Jens; Hultman, Lars; Högberg, Hans [Thin Film Physics Division, Department of Physics, Chemistry, and Biology (IFM), Linköping University, Linköping SE-581 83 (Sweden)

    2015-09-15

    Silicon oxynitride thin films were synthesized by reactive high power impulse magnetron sputtering of silicon in argon/nitrous oxide plasmas. Nitrous oxide was employed as a single-source precursor supplying oxygen and nitrogen for the film growth. The films were characterized by elastic recoil detection analysis, x-ray photoelectron spectroscopy, x-ray diffraction, x-ray reflectivity, scanning electron microscopy, and spectroscopic ellipsometry. Results show that the films are silicon rich, amorphous, and exhibit a random chemical bonding structure. The optical properties with the refractive index and the extinction coefficient correlate with the film elemental composition, showing decreasing values with increasing film oxygen and nitrogen content. The total percentage of oxygen and nitrogen in the films is controlled by adjusting the gas flow ratio in the deposition processes. Furthermore, it is shown that the film oxygen-to-nitrogen ratio can be tailored by the high power impulse magnetron sputtering-specific parameters pulse frequency and energy per pulse.

  15. High-speed deposition of protective films of aluminium oxide by the method of reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Bugaev, S.P.; Zakhrov, A.N.; Ladyzhenskii, O.P.; Sochugov, M.S.

    2001-01-01

    The high optical characteristics of aluminium films made them attractive for different functional and decorative applications. It is well-known that the corrosion resistance of alloying is determined by the presence of the oxide film on its surface, but on the aluminium films, deposited by vacuum methods, the resistance is extremely low resulting in the relatively rapid failure of the coating. At present, there is a large number of methods of depositing the films of aluminium oxide. In most cases, it is recommended to use reactive magnetron sputtering of an aluminium target in a magnetron spraying system (MSS) using direct current, on dispersion of the target of aluminium oxide in a high-frequency MSS

  16. INFLUENCE OF SUBSTRATE TEMPERATURE ON STRUCTURAL, ELECTRICAL AND OPTICAL PROPERTIES OF ITO THIN FILMS PREPARED BY RF MAGNETRON SPUTTERING

    OpenAIRE

    BO HE; LEI ZHAO; JING XU; HUAIZHONG XING; SHAOLIN XUE; MENG JIANG

    2013-01-01

    In this paper, we investigated indium-tin-oxide (ITO) thin films on glass substrates deposited by RF magnetron sputtering using ceramic target to find the optimal condition for fabricating optoelectronic devices. The structural, electrical and optical properties of the ITO films prepared at various substrate temperatures were investigated. The results indicate the grain size increases with substrate temperature increases. As the substrate temperature grew up, the resistivity of ITO films grea...

  17. Fabrication and characterization of anatase/rutile–TiO2 thin films by magnetron sputtering: a review

    Directory of Open Access Journals (Sweden)

    Sakae Tanemura, Lei Miao, Wilfried Wunderlich, Masaki Tanemura, Yukimasa Mori, Shoichi Toh and Kenji Kaneko

    2005-01-01

    Full Text Available This review article summarizes briefly some important achievements of our recent reserach on anatase and/or rutile TiO2 thin films, fabricated by helicon RF magnetron sputtering, with good crystal quality and high density, and gives the-state-of-the-art of the knowledge on systematic interrelationship for fabrication conditions, crystal structure, composition, optical properties, and bactericidal abilities, and on the effective surface treatment to improve the optical reactivity of the obtained films.

  18. Influence of reactive oxygen species during deposition of iron oxide films by high power impulse magnetron sputtering

    Czech Academy of Sciences Publication Activity Database

    Straňák, V.; Hubička, Zdeněk; Čada, Martin; Bogdanowicz, R.; Wulff, H.; Helm, C.A.; Hippler, R.

    2018-01-01

    Roč. 51, č. 9 (2018), s. 1-12, č. článku 095205. ISSN 0022-3727 R&D Projects: GA ČR GA17-08389S Institutional support: RVO:68378271 Keywords : high power impulse magnetron sputtering (HiPIMS) * iron oxide thin films * wüstite * magnetite * maghemite * hematite Subject RIV: BL - Plasma and Gas Discharge Physics OBOR OECD: Fluids and plasma physics (including surface physics ) Impact factor: 2.588, year: 2016

  19. Morphology control of tungsten nanorods grown by glancing angle RF magnetron sputtering under variable argon pressure and flow rate

    International Nuclear Information System (INIS)

    Khedir, Khedir R.; Kannarpady, Ganesh K.; Ishihara, Hidetaka; Woo, Justin; Ryerson, Charles; Biris, Alexandru S.

    2010-01-01

    Morphologically novel tungsten nanorods (WNRs) with the co-existence of two crystalline phases, α-W (thermodynamically stable) and β-W, were fabricated by glancing angle RF magnetron sputtering technique under various Ar pressures and flow rates. For these nanorods, a significant variation in their morphology and surface roughness was observed. These structures could be useful in a wide range of applications such as field emission, robust superhydrophobic coatings, energy, and medicine.

  20. Recent Developments in R.F. Magnetron Sputtered Thin Films for pH Sensing Applications—An Overview

    OpenAIRE

    D. K. Maurya; A. Sardarinejad; K. Alameh

    2014-01-01

    pH sensors are widely used in chemical and biological applications. Metal oxides-based pH sensors have many attractive features including insolubility, stability, mechanical strength, electrocatalyst and manufacturing technology. Various metal oxide thin films prepared by radio frequency (R.F.) magnetron sputtering have attractive features, including high pH sensitivity, fast response, high resolution, good stability and reversibility as well as potential for measuring pH under conditions th...

  1. Electrical resistivity of CuAlMo thin films grown at room temperature by dc magnetron sputtering

    OpenAIRE

    Birkett, Martin; Penlington, Roger

    2016-01-01

    We report on the thickness dependence of electrical resistivity of CuAlMo films grown by dc magnetron sputtering on glass substrates at room temperature. The electrical resistance of the films was monitored in situ during their growth in the thickness range 10–1000 nm. By theoretically modelling the evolution of resistivity during growth we were able to gain an insight into the dominant electrical conduction mechanisms with increasing film thickness. For thicknesses in the range 10–25 nm the ...

  2. Two-dimensional spatial survey of the plasma potential and electric field in a pulsed bipolar magnetron discharge

    International Nuclear Information System (INIS)

    Vetushka, A.; Karkari, S.K.; Bradley, J.W.

    2004-01-01

    Emissive and Langmuir probe techniques have been used to obtain two-dimensional (2D) spatial maps of the plasma potential V p , electric field E, and ion trajectories in a pulsed bipolar magnetron discharge. The magnetron was pulsed at a frequency of 100 kHz, with a 50% duty cycle and operated at an argon pressure of 0.74 Pa. The pulse wave form was characterized by three distinct phases: the 'overshoot', 'reverse', and 'on' phases. In the 'on' phase of the pulse, when the cathode voltage is driven to -670 V, the 2D spatial distribution of V p has a similar form to that in dc magnetron, with significant axial and radial electric fields in the bulk plasma, accelerating ions to the sheath edge above the cathode racetrack region. During the 'overshoot' phase (duration 200 ns), V p is raised to values greater than +330 V, more than 100 V above the cathode potential, with E pointing away from the target. In the 'reverse' phase V p has a value of +45 V at all measured positions, 2 V more positive than the target potential. In this phase there is no electric field present in the plasma. In the bulk of the plasma, the results from Langmuir probe and the emissive probe are in good agreement, however, in one particular region of the plasma outside the radius of the cathode, the emissive probe measurements are consistently more positive (up to 45 V in the 'on' time). This discrepancy is discussed in terms of the different frequency response of the probes and their perturbation of the plasma. A simple circuit model of the plasma-probe system has been proposed to explain our results. A brief discussion of the effect of the changing plasma potential distribution on the operation of the magnetron is given

  3. Vacuum system for applying reflective coatings on large-size optical components using the method of magnetron sputtering

    Science.gov (United States)

    Azerbaev, Alexander A.; Abdulkadyrov, Magomed A.; Belousov, Sergey P.; Ignatov, Aleksandr N.; Mukhammedzyanov, Timur R.

    2016-10-01

    Vacuum system for reflective coatings deposition on large-size optical components up to 4.0 m diameter using the method of magnetron sputtering was built at JSC LZOS. The technological process for deposition of reflective Al coating with protective SiO2 layer was designed and approved. After climatic tests the lifetime of such coating was estimated as 30 years. Uniformity of coating thickness ±5% was achieved on maximum diameter 4.0 m.

  4. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    OpenAIRE

    Rafieian, Damon; Ogieglo, Wojciech; Savenije, T.J.; Lammertink, Rob G H

    2015-01-01

    We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to anatase or rutile, depending on the initial sputtering conditions. Substoichiometric films (TiOx), obtained by sputtering at relatively low oxygen concentration, formed rutile upon annealing in air, ...

  5. Optical emission and mass spectroscopy of plasma processes in reactive DC pulsed magnetron sputtering of aluminium oxide

    Czech Academy of Sciences Publication Activity Database

    Novotný, Michal; Bulíř, Jiří; Pokorný, Petr; Bočan, Jiří; Fitl, Přemysl; Lančok, Ján; Musil, Jindřich

    2010-01-01

    Roč. 12, č. 3 (2010), 697-700 ISSN 1454-4164 R&D Projects: GA AV ČR IAA100100718; GA AV ČR KAN400100653; GA ČR GP202/09/P324 Institutional research plan: CEZ:AV0Z10100522 Keywords : reactive magnetron sputtering * alumina * plasma spectroscopy * mass spectroscopy * optical emission spectroscopy Subject RIV: BH - Optics, Masers, Lasers Impact factor: 0.412, year: 2010

  6. Features of copper coatings growth at high-rate deposition using magnetron sputtering systems with a liquid metal target

    Czech Academy of Sciences Publication Activity Database

    Bleykher, G.A.; Borduleva, A.O.; Yuryeva, A.V.; Krivobokov, V.P.; Lančok, Ján; Bulíř, Jiří; Drahokoupil, Jan; Klimša, Ladislav; Kopeček, Jaromír; Fekete, Ladislav; Čtvrtlík, Radim; Tomáštík, Jan

    2017-01-01

    Roč. 324, Sep (2017), s. 111-120 ISSN 0257-8972 R&D Projects: GA MŠk LO1409; GA MŠk LM2015088 Institutional support: RVO:68378271 Keywords : magnetron sputtering * evaporation * high-rate coating deposition * coating properties * Cu coatings Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 2.589, year: 2016

  7. The structural properties of CdS deposited by chemical bath deposition and pulsed direct current magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Lisco, F., E-mail: F.Lisco@lboro.ac.uk [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire, LE11 3TU (United Kingdom); Kaminski, P.M.; Abbas, A.; Bass, K.; Bowers, J.W.; Claudio, G. [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire, LE11 3TU (United Kingdom); Losurdo, M. [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR, via Orabona 4, 70126 Bari (Italy); Walls, J.M. [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire, LE11 3TU (United Kingdom)

    2015-05-01

    Cadmium sulphide (CdS) thin films were deposited by two different processes, chemical bath deposition (CBD), and pulsed DC magnetron sputtering (PDCMS) on fluorine doped-tin oxide coated glass to assess the potential advantages of the pulsed DC magnetron sputtering process. The structural, optical and morphological properties of films obtained by CBD and PDCMS were investigated using X-ray photoelectron spectroscopy, X-ray diffraction, scanning and transmission electron microscopy, spectroscopic ellipsometry and UV-Vis spectrophotometry. The as-grown films were studied and comparisons were drawn between their morphology, uniformity, crystallinity, and the deposition rate of the process. The highest crystallinity is observed for sputtered CdS thin films. The absorption in the visible wavelength increased for PDCMS CdS thin films, due to the higher density of the films. The band gap measured for the as-grown CBD-CdS is 2.38 eV compared to 2.34 eV for PDCMS-CdS, confirming the higher density of the sputtered thin film. The higher deposition rate for PDCMS is a significant advantage of this technique which has potential use for high rate and low cost manufacturing. - Highlights: • Pulsed DC magnetron sputtering (PDCMS) of CdS films • Chemical bath deposition of CdS films • Comparison between CdS thin films deposited by chemical bath and PDCMS techniques • High deposition rate deposition for PDCMS deposition • Uniform, pinhole free CdS thin films.

  8. Magnetic properties of in-plane oriented barium hexaferrite thin films prepared by direct current magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Xiaozhi; Yue, Zhenxing, E-mail: yuezhx@mail.tsinghua.edu.cn; Meng, Siqin; Yuan, Lixin [State Key Laboratory of New Ceramics and Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China)

    2014-12-28

    In-plane c-axis oriented Ba-hexaferrite (BaM) thin films were prepared on a-plane (112{sup ¯}0) sapphire (Al{sub 2}O{sub 3}) substrates by DC magnetron sputtering followed by ex-situ annealing. The DC magnetron sputtering was demonstrated to have obvious advantages over the traditionally used RF magnetron sputtering in sputtering rate and operation simplicity. The sputtering power had a remarkable influence on the Ba/Fe ratio, the hematite secondary phase, and the grain morphology of the as-prepared BaM films. Under 80 W of sputtering power, in-plane c-axis highly oriented BaM films were obtained. These films had strong magnetic anisotropy with high hysteresis loop squareness (M{sub r}/M{sub s} of 0.96) along the in-plane easy axis and low M{sub r}/M{sub s} of 0.03 along the in-plane hard axis. X-ray diffraction patterns and pole figures revealed that the oriented BaM films grew via an epitaxy-like growth process with the crystallographic relationship BaM (101{sup ¯}0)//α-Fe{sub 2}O{sub 3}(112{sup ¯}0)//Al{sub 2}O{sub 3}(112{sup ¯}0)

  9. The structural properties of CdS deposited by chemical bath deposition and pulsed direct current magnetron sputtering

    International Nuclear Information System (INIS)

    Lisco, F.; Kaminski, P.M.; Abbas, A.; Bass, K.; Bowers, J.W.; Claudio, G.; Losurdo, M.; Walls, J.M.

    2015-01-01

    Cadmium sulphide (CdS) thin films were deposited by two different processes, chemical bath deposition (CBD), and pulsed DC magnetron sputtering (PDCMS) on fluorine doped-tin oxide coated glass to assess the potential advantages of the pulsed DC magnetron sputtering process. The structural, optical and morphological properties of films obtained by CBD and PDCMS were investigated using X-ray photoelectron spectroscopy, X-ray diffraction, scanning and transmission electron microscopy, spectroscopic ellipsometry and UV-Vis spectrophotometry. The as-grown films were studied and comparisons were drawn between their morphology, uniformity, crystallinity, and the deposition rate of the process. The highest crystallinity is observed for sputtered CdS thin films. The absorption in the visible wavelength increased for PDCMS CdS thin films, due to the higher density of the films. The band gap measured for the as-grown CBD-CdS is 2.38 eV compared to 2.34 eV for PDCMS-CdS, confirming the higher density of the sputtered thin film. The higher deposition rate for PDCMS is a significant advantage of this technique which has potential use for high rate and low cost manufacturing. - Highlights: • Pulsed DC magnetron sputtering (PDCMS) of CdS films • Chemical bath deposition of CdS films • Comparison between CdS thin films deposited by chemical bath and PDCMS techniques • High deposition rate deposition for PDCMS deposition • Uniform, pinhole free CdS thin films

  10. Non-isothermal kinetics of phase transformations in magnetron sputtered alumina films with metastable structure

    International Nuclear Information System (INIS)

    Zuzjaková, Š.; Zeman, P.; Kos, Š.

    2013-01-01

    Highlights: • Non-isothermal kinetics of phase transformations in alumina films was investigated. • The structure of alumina films affects kinetics of the transformation processes. • Kinetic triplets of all transformation processes were determined. • The KAS, FWO, FR and IKP methods for determination of E a and A were used. • The Málek method for determination of the kinetic model was used. - Abstract: The paper reports on non-isothermal kinetics of transformation processes in magnetron sputtered alumina thin films with an amorphous and γ-phase structure leading ultimately to the formation of the thermodynamically stable α-Al 2 O 3 phase. Phase transformation sequences in the alumina films were investigated using differential scanning calorimetry (DSC) at four different heating rates (10, 20, 30, 40 °C/min). Three isoconversional methods (Kissinger–Akahira–Sunose (KAS), Flynn–Wall–Ozawa (FWO) and Friedman (FR) method) as well as the invariant kinetic parameters (IKP) method were used to determine the activation energies for transformation processes. Moreover, the pre-exponential factors were determined using the IKP method. The kinetic models of the transformation processes were determined using the Málek method. It was found that the as-deposited structure of alumina films affects kinetics of the transformation processes. The film with the amorphous as-deposited structure heated at 40 °C/min transforms to the crystalline γ phase at a temperature of ∼930 °C (E a,IKP = 463 ± 10 kJ/mol) and subsequently to the crystalline α phase at a temperature of ∼1200 °C (E a,IKP = 589 ± 10 kJ/mol). The film with the crystalline γ-phase structure heated at 40 °C/min is thermally stable up to ∼1100 °C and transforms to the crystalline α phase (E a,IKP = 511 ± 16 kJ/mol) at a temperature of ∼1195 °C. The empirical two-parameter Šesták–Berggren kinetic model was found to be the most adequate one to describe all transformation processes

  11. Bonding and bio-properties of hybrid laser/magnetron Cr-enriched DLC layers

    Energy Technology Data Exchange (ETDEWEB)

    Jelinek, Miroslav, E-mail: jelinek@fzu.cz [Institute of Physics, Academy of Sciences of the Czech Republic, v.v.i, Na Slovance 2, 18221 Prague (Czech Republic); Czech Technical University in Prague, Faculty of Biomedical Engineering, nam. Sitna 3105, 27201 Kladno (Czech Republic); Zemek, Josef [Institute of Physics, Academy of Sciences of the Czech Republic, v.v.i, Na Slovance 2, 18221 Prague (Czech Republic); Vandrovcová, Marta; Bačáková, Lucie [Institute of Physiology of the Czech Academy of Sciences of the Czech Republic, v.v.i., Videnska 1083, 14220 Prague 4 (Czech Republic); Kocourek, Tomáš; Remsa, Jan; Písařík, Petr [Institute of Physics, Academy of Sciences of the Czech Republic, v.v.i, Na Slovance 2, 18221 Prague (Czech Republic); Czech Technical University in Prague, Faculty of Biomedical Engineering, nam. Sitna 3105, 27201 Kladno (Czech Republic)

    2016-01-01

    Chromium-enriched diamond-like carbon (DLC) layers were prepared by a hybrid technology using a combination of pulsed laser deposition (PLD) and magnetron sputtering. XRD revealed no chromium peaks, indicating that the layers are mostly amorphous. Carbon (sp{sup 2} and sp{sup 3} bonds) and chromium bonds were determined by XPS from C 1s, O 1s, and Cr 2p photoelectron peaks. Depending on the deposition conditions, the concentration of Cr in DLC layers moved from zero to 10 at.% for as-received sample surfaces, and to about 31 at.% after mild sputter-cleaning by argon ion cluster beam. It should be noted that the most stable Cr{sup 3+} bonding state is in Cr{sub 2}O{sub 3} and Cr(OH){sub 3}, and that there is the toxic Cr{sup 6+} state in CrO{sub 3}. The surface content of hexavalent chromium in the Cr 2p3/2 spectra is rather low, but discernible. The population density of Saos-2 cells was the highest in samples containing higher concentrations of chromium 7.7 and 10 at.%. This means that higher concentrations of chromium supported the cell adhesion and proliferation. In addition, as revealed by a LIVE/DEAD viability/cytotoxicity kit, the cells on all Cr-containing samples maintained high viability (96 to 99%) on days 1 and 3 after seeding. However, this seemingly positive cell behavior could be associated with the risk of dedifferentiation and oncogenic transformation of cells. - Highlights: • DLC and chromium-enriched DLC layers were prepared by hybrid laser–magnetron deposition. • The content of chromium in DLC varied up to 10 at.% (31 at.% after ion beam sputtering). • The surface content of toxic hexavalent chromium in the Cr 2p3/2 spectra is rather low but discernible. • Higher concentrations of chromium supported the cell adhesion and proliferation. • Cells on all Cr-containing samples maintained high viability (96 to 99%).

  12. An investigation of material properties and tribological performance of magnetron sputtered thin film coatings

    Science.gov (United States)

    Singh, Harpal

    This dissertation is divided into two categories based upon lubrication functionality and its application. The categories are: Dry film lubrication and Fluid film lubrication with thin film coatings. Thin film coatings examined in this work were deposited using closed field unbalanced magnetron sputtering and RF-DC coupled magnetron sputtering systems. In Dry/Solid film lubrication, the mechanical, structural and tribological properties of two Molybdenum disulphide (MoS2) based coatings are examined and evaluated. Among the two coatings, one coating is doped with Ti (Ti-MoS2) and the other is a combination of metal, lubricant and oxide (Sb2O3/Au - MoS2). These coatings are known to provide low friction in vacuum environments. The goal of this work was to evaluate friction and wear performance of MoS2 doped coatings in unidirectional and reciprocating sliding contact under different environmental conditions. Sliding contact results showed friction and wear dependence on temperature and humidity. The formation and removal of transfer films and the recrystallization and reorientation of basal layers on the steel counterface was observed as the mechanism for low friction. Structural analysis revealed a relationship between the microstructural properties and tribological performance. It was also observed that the addition of dopants (Ti, Au, Sb 2O3) improved the mechanical properties as compared to pure MoS2 coatings. Further, the rolling contact performance of the coatings was measured on a five ball on rod tribometer and a Thrust bearing tribometer under vacuum and air environments. The rolling contact experiments indicated that life of the rolling components depend on the amount of material present between the contacts. Fluid film lubrication with thin film coatings investigates the possibilities to improve the performance and durability of tribological components when oils and thin films are synergistically coupled. In this work, the ability of a Diamond Like Carbon

  13. "Dilute-and-inject" multi-target screening assay for highly polar doping agents using hydrophilic interaction liquid chromatography high resolution/high accuracy mass spectrometry for sports drug testing.

    Science.gov (United States)

    Görgens, Christian; Guddat, Sven; Orlovius, Anne-Katrin; Sigmund, Gerd; Thomas, Andreas; Thevis, Mario; Schänzer, Wilhelm

    2015-07-01

    In the field of LC-MS, reversed phase liquid chromatography is the predominant method of choice for the separation of prohibited substances from various classes in sports drug testing. However, highly polar and charged compounds still represent a challenging task in liquid chromatography due to their difficult chromatographic behavior using reversed phase materials. A very promising approach for the separation of hydrophilic compounds is hydrophilic interaction liquid chromatography (HILIC). Despite its great potential and versatile advantages for the separation of highly polar compounds, HILIC is up to now not very common in doping analysis, although most manufacturers offer a variety of HILIC columns in their portfolio. In this study, a novel multi-target approach based on HILIC high resolution/high accuracy mass spectrometry is presented to screen for various polar stimulants, stimulant sulfo-conjugates, glycerol, AICAR, ethyl glucuronide, morphine-3-glucuronide, and myo-inositol trispyrophosphate after direct injection of diluted urine specimens. The usage of an effective online sample cleanup and a zwitterionic HILIC analytical column in combination with a new generation Hybrid Quadrupol-Orbitrap® mass spectrometer enabled the detection of highly polar analytes without any time-consuming hydrolysis or further purification steps, far below the required detection limits. The methodology was fully validated for qualitative and quantitative (AICAR, glycerol) purposes considering the parameters specificity; robustness (rRT  0.99); intra- and inter-day precision at low, medium, and high concentration levels (CV < 20%); limit of detection (stimulants and stimulant sulfo-conjugates < 10 ng/mL; norfenefrine; octopamine < 30 ng/mL; AICAR < 10 ng/mL; glycerol 100 μg/mL; ETG < 100 ng/mL); accuracy (AICAR 103.8-105.5%, glycerol 85.1-98.3% at three concentration levels) and ion suppression/enhancement effects.

  14. Ge Nanoislands Grown by Radio Frequency Magnetron Sputtering: Comprehensive Investigation of Surface Morphology and Optical Properties

    Directory of Open Access Journals (Sweden)

    Alireza Samavati

    2015-01-01

    Full Text Available The comprehensive investigation of the effect of growth parameters on structural and optical properties of Si-based single layer Ge nanoislands grown via Stranski-Krastanov mechanism employing radio frequency magnetron sputtering due to its high deposition rate, easy procedure, economical cost, and safety is carried out. The estimated width and height of Ge nanoislands produced by this technique are in the range of ∼8 to ∼30 and ∼2 to 8 nm, respectively. Varieties parameters are manipulated to optimize the surface morphology and structural and optical behavior of Ge nanoislands. The resulted nanoislands are analyzed using various analytical techniques including atomic force microscope, X-ray diffraction, energy dispersive X-ray spectroscopy, room temperature photoluminescence, and Raman spectroscopy. The optimum parameters for growing high quality samples having high number density and homogenous and small size distribution are found to be 400°C for substrate temperature, 300 sec for deposition time, 10 sccm for Ar flow, and 100 W for radio frequency power. The excellent features of the results suggest that our systematic investigation on the organized growth factors and their effects on surface parameters and photoluminescence emission energy may constitute a basis for the tunable growth of Ge nanoislands (100 nanoislands suitable in nanophotonics.

  15. Characterization of Ta–Si–N coatings prepared using direct current magnetron co-sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Yung-I, E-mail: yichen@mail.ntou.edu.tw; Lin, Kun-Yi; Wang, Hsiu-Hui; Cheng, Yu-Ru

    2014-06-01

    Ta–Si–N coatings were prepared using reactive direct current magnetron co-sputtering on silicon substrates. When the sputtering powers and N{sub 2} flow ratio were varied, Ta–Si–N coatings exhibited various chemical compositions and crystalline characteristics. The high-Si-content Ta–Si–N coatings exhibited an amorphous phase in the as-deposited states, whereas the low-Si-content coatings exhibited a face-centered cubic phase or an amorphous phase depending on the N content. This study evaluated the application of amorphous Ta–Si–N coatings, such as the protective coatings on glass molding dies, in high-temperature and oxygen-containing atmospheres for longed operation durations. To explore the oxidation resistance and mechanical properties of the Ta–Si–N coatings, annealing treatments were conducted in a 1%O{sub 2}–99%Ar atmosphere at 600 °C for 4–100 h. The material characteristics and oxidation behavior of the annealed Ta–Si–N coatings were examined using atomic force microscopy, transmission electron microscopy, X-ray photoelectron spectroscopy, and a nanoindentation tester. The Si oxidized preferentially in the Ta–Si–N coatings. The in-diffusion of oxygen during 600 °C annealing was restricted by the formation of an amorphous oxide scale consisting of Si and O.

  16. Experimental investigation of plasma dynamics in dc and short-pulse magnetron discharges

    International Nuclear Information System (INIS)

    Seo, Sang-Hun; In, Jung-Hwan; Chang, Hong-Young

    2006-01-01

    The spatiotemporal evolution of the electron energy distribution function (EEDF) and of plasma parameters such as the electron density, the electron temperature and the plasma and floating potentials has been investigated using spatially and temporally resolved single Langmuir probe measurements in dc and mid-frequency, short-pulse magnetron discharges with a repetition frequency of 10 kHz and a duty cycle of 10%. In the pulsed discharge of the short duty cycle, a peak electron temperature higher than 10 eV was observed near the cathode fall region during the early phase of the pulse-on, which is about three times higher than the steady-state value of the electron temperature in the dc discharge. The temporal evolution of the measured EEDFs showed the initial efficient electron heating during the early phase of the pulse-on and the subsequent relaxation of electron energy by the inelastic collisions and the diffusive loss. The high-energy electrons generated during the pulse-on phase diffused the downstream region toward the grounded substrate, resulting in a bi-Maxwellian EEDF consisting of the background low-energy electrons and the high-energy electrons. The results of the spatially and temporally resolved probe measurements will be presented and the enhanced efficiency of the electron heating in the short-pulse discharge will be explained on the basis of the global model of a pulsed discharge

  17. Antimicrobial brass coatings prepared on poly(ethylene terephthalate) textile by high power impulse magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Ying-Hung, E-mail: tieamo2002@gmail.com; Wu, Guo-Wei; He, Ju-Liang

    2015-03-01

    The goal of this work is to prepare antimicrobial, corrosion-resistant and low-cost Cu65Zn35 brass film on poly(ethylene terephthalate) (PET) fabric by high-power impulse magnetron sputtering (HIPIMS), which is known to provide high-density plasma, so as to generate a strongly adherent film at a reduced substrate temperature. The results reveal that the brass film grows in a layer-plus-island mode. Independent of their deposition time, the obtained films retain a Cu/Zn elemental composition ratio of 1.86 and exhibit primarily an α copper phase structure. Oxygen plasma pre-treatment for 1 min before coating can significantly increase film adhesion such that the brass-coated fabric of Grade 5 or Grade 4–5 can ultimately be obtained under dry and wet rubbing tests, respectively. However, a deposition time of 1 min suffices to provide effective antimicrobial properties for both Staphylococcus aureus and Escherichia coli. As a whole, the feasibility of using such advanced HIPIMS coating technique to develop durable antimicrobial textile was demonstrated. - Highlights: • Prepare antimicrobial, corrosion-resistant and low-cost Cu65Zn35 brass film on PET fabric by HIPIMS • Brass-coated fabric with excellent durability, even undergone rubbing and washing tests • Brass-coated fabric provides effective antimicrobial properties for E. coli and S. aureus. • After brass coating, PET fabric still retained its mechanical property.

  18. Chemical mechanical polishing characteristics of ITO thin film prepared by RF magnetron sputtering

    International Nuclear Information System (INIS)

    Lee, Kang-Yeon; Choi, Gwon-Woo; Kim, Yong-Jae; Choi, Youn-Ok; Kim, Nam-Oh

    2012-01-01

    Indium-tin-oxide (ITO) thin films have attracted intensive interest because of their unique properties of good conductivity, high optical transmittance over the visible region and easy patterning ability. ITO thin films have found many applications in anti-static coatings, thermal heaters, solar cells, flat panel displays (FPDs), liquid crystal displays (LCDs), electroluminescent devices, sensors and organic light-emitting diodes (OLEDs). ITO thin films are generally fabricated by using various methods, such as spraying, chemical vapor deposition (CVD), evaporation, electron gun deposition, direct current electroplating, high frequency sputtering, and reactive sputtering. In this research, ITO films were grown on glass substrates by using a radio-frequency (RF) magnetron sputtering method. In order to achieve a high transmittance and a low resistivity, we examined the various film deposition conditions, such as substrate temperature, working pressure, annealing temperature, and deposition time. Next, in order to improve the surface quality of the ITO thin films, we performed a chemical mechanical polishing (CMP) with different process parameters and compared the electrical and the optical properties of the polished ITO thin films. The best CMP conditions with a high removal rate, low nonuniformity, low resistivity and high transmittance were as follows: platen speed, head speed, polishing time, and slurry flow rate of 30 rpm, 30 rpm, 60 sec, and 60 ml/min, respectively.

  19. Room temperature deposition of crystalline indium tin oxide films by cesium-assisted magnetron sputtering

    International Nuclear Information System (INIS)

    Lee, Deuk Yeon; Baik, Hong-Koo

    2008-01-01

    Indium tin oxide (ITO) films were deposited on a Si (1 0 0) substrate at room temperature by cesium-assisted magnetron sputtering. Including plasma characteristics, the structural, electrical, and optical properties of deposited films were investigated as a function of cesium partial vapor pressure controlled by cesium reservoir temperature. We calculated the cesium coverage on the target surface showing maximum formation efficiency of negative ions by means of the theoretical model. Cesium addition promotes the formation efficiency of negative ions, which plays important role in enhancing the crystallinity of ITO films. In particular, the plasma density was linearly increased with cesium concentrations. The resultant decrease in specific resistivity and increase in transmittance (82% in the visible region) at optimum cesium concentration (4.24 x 10 -4 Ω cm at 80 deg. C of reservoir temperature) may be due to enhanced crystallinity of ITO films. Excess cesium incorporation into ITO films resulted in amorphization of its microstructure leading to degradation of ITO crystallinity. We discuss the cesium effects based on the growth mechanism of ITO films and the plasma density

  20. Properties of Ce-doped ITO films deposited on polymer substrate by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Kang, Y.M.; Kwon, S.H.; Choi, J.H.; Cho, Y.J.; Song, P.K.

    2010-01-01

    Ce-doped indium tin oxide (ITO:Ce) films were deposited on flexible polyimide substrates by DC magnetron sputtering using ITO targets containing various CeO 2 contents (CeO 2 : 0, 0.5, 3.0, 4.0, 6.0 wt.%) at room temperature and post-annealed at 200 o C. The crystallinity of the ITO films decreased with increasing Ce content, and it led to a decrease in surface roughness. In addition, a relatively small change in resistance in dynamic stress mode was obtained for ITO:Ce films even after the annealing at high temperature (200 o C). The minimum resistivity of the amorphous ITO:Ce films was 3.96 x 10 -4 Ωcm, which was deposited using a 3.0 wt.% CeO 2 doped ITO target. The amorphous ITO:Ce films not only have comparable electrical properties to the polycrystalline films but also have a crystallization temperature > 200 o C. In addition, the amorphous ITO:Ce film showed stable mechanical properties in the bended state.

  1. Indium tin oxide thin films by bias magnetron rf sputtering for heterojunction solar cells application

    International Nuclear Information System (INIS)

    Zhao Liang; Zhou Zhibin; Peng Hua; Cui Rongqiang

    2005-01-01

    In this investigation ITO thin films were prepared by bias magnetron rf sputtering technique at substrate temperature of 180 deg. C and low substrate-target distance for future a-Si:H/c-Si heterojunction (HJ) solar cells application. Microstructure, surface morphology, electrical and optical properties of these films were characterized and analyzed. The effects of ion bombardments on growing ITO films are well discussed. XRD analysis revealed a change in preferential orientation of polycrystalline structure from (2 2 2) to (4 0 0) plane with the increase of negative bias voltage. Textured surface were observed on AFM graphs of samples prepared at high negative bias. Hall measurements showed that the carrier density and Hall mobility of these ITO films are sensitive to the bias voltage applied. We attributed these effects to the sensitivity of energy of Ar + ions bombarding on growing films to the applied bias voltage in our experiments. At last the figure of merit was calculated to evaluate the quality of ITO thin films, the results of which show that sample prepared at bias voltage of -75 V is good to be used in HJ cells application

  2. Fracture toughness and sliding properties of magnetron sputtered CrBC and CrBCN coatings

    Science.gov (United States)

    Wang, Qianzhi; Zhou, Fei; Ma, Qiang; Callisti, Mauro; Polcar, Tomas; Yan, Jiwang

    2018-06-01

    CrBC and CrBCN coatings with low and high B contents were deposited on 316L steel and Si wafers using an unbalanced magnetron sputtering system. Mechanical properties including hardness (H), elastic modulus (E) and fracture toughness (KIc) as well as residual stresses (σ) were quantified. A clear correlation between structural, mechanical and tribological properties of coatings was found. In particular, structural analyses indicated that N incorporation in CrBC coatings with high B content caused a significant structural evolution of the nanocomposite structure (crystalline grains embedded into an amorphous matrix) from nc-CrB2/(a-CrBx, a-BCx) to nc-CrN/(a-BCx, a-BN). As a result, the hardness of CrBC coating with high B content decreased from 23.4 to 16.3 GPa but the fracture toughness was enhanced. Consequently, less cracks initiated on CrBCN coatings during tribological tests, which combined with the shielding effect of a-BN on wear debris, led to a low friction coefficient and wear rate.

  3. Damp heat stability and annealing behavior of aluminum doped zinc oxide films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Tohsophon, T.; Huepkes, J.; Calnan, S.; Reetz, W.; Rech, B.; Beyer, W.; Sirikulrat, N.

    2006-01-01

    The damp heat stability and subsequent vacuum annealing behavior of aluminum doped zinc oxide (AZO) films was investigated using Hall effect measurements, X-ray diffraction (XRD) and optical spectrometry techniques. The AZO films were deposited on glass or silicon wafers using reactive and non-reactive magnetron sputtering from metallic and ceramic targets, respectively. Additionally, we characterized surface textured AZO films, which are used as light scattering transparent conductive oxide (TCO) in silicon thin film solar cells. For all films a degradation of the electrical film properties was found after the damp heat treatment. For thick compact films, with large grain size, only a small increase in the electrical resistivity was observed, whereas less compact films prepared at high deposition pressures or very thin films (< 300 nm) showed an increase in resistivity by up to a factor of three already after 300 h. The conductivity degradation during damp heat treatment could be largely reversed by annealing in vacuum. However, annealing temperatures of at least 150 deg. C were required. Possible mechanisms explaining the experimental results are discussed

  4. Synthesis and characterization of CdTe nanostructures grown by RF magnetron sputtering method

    Science.gov (United States)

    Akbarnejad, Elaheh; Ghoranneviss, Mahmood; Hantehzadeh, Mohammad Reza

    2017-08-01

    In this paper, we synthesize Cadmium Telluride nanostructures by radio frequency (RF) magnetron sputtering system on soda lime glass at various thicknesses. The effect of CdTe nanostructures thickness on crystalline, optical and morphological properties has been studied by means of X-ray diffraction (XRD), UV-VIS-NIR spectrophotometry, field emission scanning electron microscopy (FESEM) and atomic force microscopy (AFM), respectively. The XRD parameters of CdTe nanostructures such as microstrain, dislocation density, and crystal size have been examined. From XRD analysis, it could be assumed that increasing deposition time caused the formation of the wurtzite hexagonal structure of the sputtered films. Optical properties of the grown nanostructures as a function of film thickness have been observed. All the films indicate more than 60% transmission over a wide range of wavelengths. The optical band gap values of the films have obtained in the range of 1.62-1.45 eV. The results indicate that an RF sputtering method succeeded in depositing of CdTe nanostructures with high purity and controllable physical properties, which is appropriate for photovoltaic and nuclear detector applications.

  5. RHEED oscillations in spinel ferrite epitaxial films grown by conventional planar magnetron sputtering

    Science.gov (United States)

    Ojima, T.; Tainosho, T.; Sharmin, S.; Yanagihara, H.

    2018-04-01

    Real-time in situ reflection high energy electron diffraction (RHEED) observations of Fe3O4, γ-Fe2O3, and (Co,Fe)3O4 films on MgO(001) substrates grown by a conventional planar magnetron sputtering was studied. The change in periodical intensity of the specular reflection spot in the RHEED images of three different spinel ferrite compounds grown by two different sputtering systems was examined. The oscillation period was found to correspond to the 1/4 unit cell of each spinel ferrite, similar to that observed in molecular beam epitaxy (MBE) and pulsed laser deposition (PLD) experiments. This suggests that the layer-by-layer growth of spinel ferrite (001) films is general in most physical vapor deposition (PVD) processes. The surfaces of the films were as flat as the surface of the substrate, consistent with the observed layer-by-layer growth process. The observed RHEED oscillation indicates that even a conventional sputtering method can be used to control film thickness during atomic layer depositions.

  6. Magnetron sputtered TiN thin films toward enhanced performance supercapacitor electrodes

    KAUST Repository

    Wei, Binbin

    2018-04-09

    Supercapacitors as a new type of energy storage devices bridging the gap between conventional capacitors and batteries have aroused widespread concern. Herein, binder-free titanium nitride (TiN) thin film electrodes for supercapacitors prepared by reactive magnetron sputtering technology are reported. The effect of N2 content on the supercapacitor performance is evaluated. A highest specific capacitance of 27.3 mF cm−2 at a current density of 1.0 mA cm−2, together with excellent cycling performance (98.2% capacitance retention after 20,000 cycles at 2.0 mA cm−2) is achieved in a 0.5 M H2SO4 aqueous electrolyte. More importantly, a symmetric supercapacitor device assembled on the basis of TiN thin films can deliver a maximum energy density of 17.6 mWh cm−3 at a current density of 0.2 mA cm−2 and a maximum power density of 10.8 W cm−3 at a current density of 2 mA cm−2 with remarkable cycling stability. As a consequence, TiN thin films demonstrate great potential as promising supercapacitor electrode materials.

  7. Investigation and optimization of the magnetic field configuration in high-power impulse magnetron sputtering

    International Nuclear Information System (INIS)

    Yu, He; Meng, Liang; Szott, Matthew M; Meister, Jack T; Cho, Tae S; Ruzic, David N

    2013-01-01

    An effort to optimize the magnetic field configuration specifically for high-power impulse magnetron sputtering (HiPIMS) was made. Magnetic field configurations with different field strengths, race track widths and race track patterns were designed using COMSOL. Their influence on HiPIMS plasma properties was investigated using a 36 cm diameter copper target. The I–V discharge characteristics were measured. The temporal evolution of electron temperature (T e ) and density (n e ) was studied employing a triple Langmuir probe, which was also scanned in the whole discharge region to characterize the plasma distribution and transport. Based on the studies, a closed path for electrons to drift along was still essential in HiPIMS in order to efficiently confine electrons and achieve a high pulse current. Very dense plasmas (10 19 –10 20 m −3 ) were generated in front of the race tracks during the pulse, and expanded downstream afterwards. As the magnetic field strength increased from 200 to 800 G, the expansion became faster and less isotropic, i.e. more directional toward the substrate. The electric potential distribution accounted for these effects. Varied race track widths and patterns altered the plasma distribution from the target to the substrate. A spiral-shaped magnetic field design was able to produce superior plasma uniformity on the substrate in addition to improved target utilization. (paper)

  8. Thickness characteristics of YBaCuO system thin films prepared by RF magnetron sputtering

    International Nuclear Information System (INIS)

    Furuhashi, Hideo; Jinno, Makoto; Takashima, Osamu; Uchida, Yoshiyuki; Maeda, Akinori; Kojima, Kenzo; Ochiai, Shizuyasu; Ohashi, Asao

    1994-01-01

    The practical use of oxide high temperature superconductors for electronics field has been advanced. The oxide high temperature superconductor thin films is very sensitive to the production conditions, and their making with good reproducibility is difficult. In this study, the method of producing the thin films having good quality with good reproducibility by RF magnetron sputtering, and the relation of the film thickness with the superconductivity characteristics of YBaCuO system thin films in the different methods of substrate washing were examined. The sputtering conditions are shown. For the purpose of preventing the worsening of the film quality due to the reverse sputtering of oxygen negative ions to the thin film surface, sputtering gas pressure was set up high at 30 Pa. The film thickness and the temperature-resistance characteristics were measured. The experimental method and the experimental results are reported. By keeping the temperature on substrate surfaces constant, the reproducibility in the production of the thin films was improved remarkably. The effect of substrate washing was large. (K.I.)

  9. Resputtering effect during MgO buffer layer deposition by magnetron sputtering for superconducting coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Xiao, Shaozhu; Shi, Kai; Deng, Shutong; Han, Zhenghe [Applied Superconductivity Research Center, Department of Physics, Tsinghua University, Beijing 100084 (China); Feng, Feng, E-mail: feng.feng@sz.tsinghua.edu.cn; Lu, Hongyuan [Division of Advanced Manufacturing, Graduate School at Shenzhen, Tsinghua University, Shenzhen 518055 (China); Qu, Timing; Zhu, Yuping [Department of Mechanical Engineering, Tsinghua University, Beijing 100084 (China); Huang, Rongxia [School of Electromechanical Engineering, Guangdong University of Technology, Guangzhou 510006 (China)

    2015-07-15

    In this study, MgO thin films were deposited by radio-frequency magnetron sputtering. The film thickness in the deposition area directly facing the target center obviously decreased compared with that in other areas. This reduction in thickness could be attributed to the resputtering effect resulting from bombardment by energetic particles mainly comprising oxygen atoms and negative oxygen ions. The influences of deposition position and sputtering pressure on the deposition rate were investigated. Resputtering altered the orientation of the MgO film from (111) to (001) when the film was deposited on a single crystal yttria-stabilized zirconia substrate. The density distribution of energetic particles was calculated on the basis of the measured thicknesses of the MgO films deposited at different positions. The divergence angle of the energetic particle flux was estimated to be approximately 15°. The energetic particle flux might be similar to the assisting ion flux in the ion beam assisted deposition process and could affect the orientation of the MgO film growth.

  10. CrN thin films prepared by reactive DC magnetron sputtering for symmetric supercapacitors

    KAUST Repository

    Wei, Binbin

    2016-12-29

    Supercapacitors have been becoming indispensable energy storage devices in micro-electromechanical systems and have been widely studied over the past few decades. Transition metal nitrides with excellent electrical conductivity and superior cycling stability are promising candidates as supercapacitor electrode materials. In this work, we report the fabrication of CrN thin films using reactive DC magnetron sputtering and further their applications for symmetric supercapacitors for the first time. The CrN thin film electrodes fabricated under the deposition pressure of 3.5 Pa show an areal specific capacitance of 12.8 mF cm at 1.0 mA cm and high cycling stability with 92.1% capacitance retention after 20 000 cycles in a 0.5 M HSO electrolyte. Furthermore, our developed CrN//CrN symmetric supercapacitor can deliver a high energy density of 8.2 mW h cm at the power density of 0.7 W cm along with outstanding cycling stability. Thus, the CrN thin films have great potential for application in supercapacitors and other energy storage systems.

  11. PHYSICAL PROPERTIES OF InN PARTICLES OBTAINED BY RF MAGNETRON SPUTTERING

    Directory of Open Access Journals (Sweden)

    Roberto Bernal Correa

    2014-01-01

    Full Text Available InN layers were prepared by magnetron sputtering, in a mixed atmosphere of argon and nitrogen on Si substrates (100, Si (111, and glass. The substrate temperature Ts was varied (300-500 oC in order to correlate it with the optical, structural, and morphological properties of the layers. X-ray results have revealed a presence of hexagonal InN type wurtzite in each of the layers in addition to oxides of indium (InxOy attributed to different factors. Dependence was evident on the crystalline quality of each layer according to Ts. The optical absorption coefficient and the band gap were determined from the absorbance and transmittance spectra obtained by UV/Vis. Vibration modes associated with the semiconductor InN and InxOy were identified by Raman microscopy. The morphology of the layers and the grain size was analyzed from SEM micrographs where it was determined the formation of particulates  ~ 0.5 mm and ~ 50 nm of different geometries.

  12. Experimental studies of thin films deposition by magnetron sputtering method for CIGS solar cell fabrication

    Directory of Open Access Journals (Sweden)

    Gułkowski Sławomir

    2017-01-01

    Full Text Available Among a variety of the thin film solar cell technologies of second generation, copper-indium-gallium-diselenide device (CIGS with the latest highest lab cell efficiency record of 22.4 % seems to be the most promising for the power generation. This is partly due to the advantages of using low cost films of few microns thick not only as a metallic contacts but also as a main structure of the solar cell consisted of high quality semiconductor layers. This paper reports the experimental studies of the CIGS absorber formation on Soda Lime Glass substrate covered by thin molybdenum film as a back contact layer. All structures were deposited with the use of magnetron sputtering method only. Technological parameters of the deposition process such as deposition power, pressure and deposition time were optimized for each layer of the structure. Mo back contact was examined in terms of resistivity. EDS measurements were carried out to verify stoichiometric composition of CIGS absorber. Thin film of Al was used as a top contact in order to examine the quality of p-n junction. The I-V electrical characteristic of the p-n junction was analysed in terms of solar cell application.

  13. Metal doped fluorocarbon polymer films prepared by plasma polymerization using an RF planar magnetron target

    Energy Technology Data Exchange (ETDEWEB)

    Biederman, H.; Holland, L. (Sussex Univ., Brighton (UK). Lab. for Plasma Materials Processing)

    1983-07-01

    Fluorocarbon films have been prepared by plasma polymerization of CF/sub 4/ using an RF planar magnetron with an aluminium target. More than one order of magnitude higher deposition rate has been achieved in comparison with an R.F. diode system operated under similar conditions of monomer pressure and flow rate and power input. A glow discharge in a CF/sub 4/(25%)-argon(75%) mixture was used to incorporate aluminium from a target electrode into the polymer films. The foregoing mixture and another based on CF/sub 4/(87%)-argon(13%) were used in the RF discharge with a copper target. Some experiments with a gold target and pure CF/sub 4/ as the inlet gas were also made. The film structure was examined by SEM and TEM and characteristic micrographs are presented here. The composition of the films was estimated from an EAS study. The sheet resistivity of the metal/polymer film complexes was determined.

  14. Deposition of nanostructured fluorocarbon plasma polymer films by RF magnetron sputtering of polytetrafluoroethylene

    Energy Technology Data Exchange (ETDEWEB)

    Kylian, Ondrej, E-mail: ondrej.kylian@gmail.com; Drabik, Martin; Polonskyi, Oleksandr; Cechvala, Juraj; Artemenko, Anna; Gordeev, Ivan; Choukourov, Andrei; Matolinova, Iva; Slavinska, Danka; Biederman, Hynek, E-mail: bieder@kmf.troja.mff.cuni.cz

    2011-07-29

    The RF magnetron sputtering of polytetrafluoroethylene target is studied with the aim to find out conditions leading to the deposition of super-hydrophobic thin films. It is shown that such coatings can be prepared at elevated pressures and a longer distance between the sputtered target and the substrate. This is explained by an increase in the density of longer C{sub x}F{sub y} molecules that reach the substrate and a lower flux of ions and CF{sub 2} radicals on the surface of growing film under such deposition conditions, as observed by optical emission spectroscopy and mass spectrometry. Such changes in plasma composition result in a deposition of rough films having F/C ratio close to 2 as observed by scanning electron microscopy and X-ray photoelectron spectroscopy, respectively. These findings clearly distinguish our results from the previous investigations of polytetrafluoroethylene sputtering performed at shorter distances from the target, where either low F/C ratio or low roughness of the deposited films did not allow reaching super-hydrophobic character of the coatings.

  15. Corrosion resistance of ZrNxOy thin films obtained by rf reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Ariza, E.; Rocha, L.A.; Vaz, F.; Cunha, L.; Ferreira, S.C.; Carvalho, P.; Rebouta, L.; Alves, E.; Goudeau, Ph.; Riviere, J.P.

    2004-01-01

    The main aim of this work is the investigation of the corrosion resistance of single layered zirconium oxynitride, ZrN x O y , thin films in artificial sweat solution at ambient temperature. The films were produced by rf reactive magnetron sputtering, using a pure Zr target at a constant temperature of 300 deg. C. Two different sets of samples were produced. In the first set of films, the substrate bias voltage was the main variable, whereas in the second set, the flow rate of reactive gases (oxygen/nitrogen ratio) was varied. The control of the amount of oxygen allowed the film properties to be tailored from those of covalent zirconium nitride to those of the correspondent ionic oxide. The corrosion behaviour was evaluated by potentiodynamic polarization and Electrochemical Impedance Spectroscopy (EIS) tests. The analysis of EIS data provided detailed information of the corrosion processes occurring at the surface of the system throughout the immersion time. The modifications of the coating microstructure and/or chemical composition induced by the variation of the deposition parameters were also evaluated and correlated with the corrosion mechanisms occurring in each system

  16. Electrical and optical properties of reactive DC magnetron sputtered silver oxide thin films: role of oxygen

    Energy Technology Data Exchange (ETDEWEB)

    Kumar Barik, Ullash; Srinivasan, S; Nagendra, C L; Subrahmanyam, A

    2003-04-01

    Silver oxide thin films have been prepared on soda lime glass substrates at room temperature (300 K) by reactive DC Magnetron sputtering technique using pure silver metal target; the oxygen flow rates have been varied in the range 0.00-2.01 sccm. The X-ray diffraction data on these films show a systematic change from metallic silver to silver (sub) oxides. The electrical resistivity increases with increasing oxygen flow. The films show a p-type behavior (by both Hall and Seebeck measurements) for the oxygen flow rates of 0.54, 1.09 and 1.43 sccm. The refractive index of the films (at 632.8 nm) decreases with increasing oxygen content and is in the range 1.167-1.145, whereas the p-type films show a higher refractive index (1.186-1.204). The work function of these silver oxide films has been measured by Kelvin Probe technique. The results, in specific, the p-type conductivity in the silver oxide films, have been explained on the basis of the theory of partial ionic charge proposed by Sanderson.

  17. Electrical and optical properties of reactive DC magnetron sputtered silver oxide thin films: role of oxygen

    International Nuclear Information System (INIS)

    Kumar Barik, Ullash; Srinivasan, S.; Nagendra, C.L.; Subrahmanyam, A.

    2003-01-01

    Silver oxide thin films have been prepared on soda lime glass substrates at room temperature (300 K) by reactive DC Magnetron sputtering technique using pure silver metal target; the oxygen flow rates have been varied in the range 0.00-2.01 sccm. The X-ray diffraction data on these films show a systematic change from metallic silver to silver (sub) oxides. The electrical resistivity increases with increasing oxygen flow. The films show a p-type behavior (by both Hall and Seebeck measurements) for the oxygen flow rates of 0.54, 1.09 and 1.43 sccm. The refractive index of the films (at 632.8 nm) decreases with increasing oxygen content and is in the range 1.167-1.145, whereas the p-type films show a higher refractive index (1.186-1.204). The work function of these silver oxide films has been measured by Kelvin Probe technique. The results, in specific, the p-type conductivity in the silver oxide films, have been explained on the basis of the theory of partial ionic charge proposed by Sanderson

  18. Aluminum oxide films deposited in low pressure conditions by reactive pulsed dc magnetron sputtering

    CERN Document Server

    Seino, T

    2002-01-01

    The reactive pulsed dc sputtering technique is widely used for the deposition of oxide films. The operating pressure for sputtering is commonly above 0.13 Pa. In this study, however, aluminum oxide (alumina) films were deposited at operating pressures from 0.06 to 0.4 Pa using a sputtering system equipped with a scanning magnetron cathode and a pulsed dc power supply. The pulsed dc power was found to be useful not only to reduce arcing, but also to sustain the discharge at low pressure. The electrical breakdown field, intrinsic stress, O/Al ratio, refractive index, and surface roughness were investigated. Both a low intrinsic stress and an O/Al ratio around the stoichiometry were required to get the film having a high breakdown field. A low operating pressure of 0.1 Pa was found to provide the necessary stress and O/Al ratio targets. A 50-nm-thick alumina film having a maximum breakdown field of 7.4 MV/cm was obtained.

  19. Time resolved 2-D optical imaging of a pulsed unbalanced magnetron plasma

    International Nuclear Information System (INIS)

    Bradley, J W; Clarke, G C B; Braithwaite, N St J; Bryant, P M; Kelly, P J

    2006-01-01

    Using wavelength filtered two dimensional (2-D) optical imaging, the temporal and spatial evolution of selected excited species in a pulsed magnetron discharge has been studied. A titanium target was sputtered at a pulse frequency of 100 kHz, in an argon atmosphere, at an operating pressure of 0.27 Pa. The radial information of the emissivity was determined using the Abel inversion technique. The results show strong excitation of the observed species above the racetrack in the on-time, and the possible development of an ion-acoustic wave, initiated after the off-on transition. The on-off transition is accompanied by a burst of light from the plasma bulk consistent with the transient plasma potential reaching about +200 V. During this phase, we argue that there is a release of secondary electrons from the grounded substrate and walls due to ion bombardment, as well as an increased confinement of energetic plasma electrons. The characteristic decay times of the selected transitions at 750.4, 751.5, 810.4 and 811.5 nm (ArI), present within the bandpass width of our filters, is briefly discussed in terms of the production of fast electrons in the system

  20. Experimental studies of thin films deposition by magnetron sputtering method for CIGS solar cell fabrication

    Science.gov (United States)

    Gułkowski, Sławomir; Krawczak, Ewelina

    2017-10-01

    Among a variety of the thin film solar cell technologies of second generation, copper-indium-gallium-diselenide device (CIGS) with the latest highest lab cell efficiency record of 22.4 % seems to be the most promising for the power generation. This is partly due to the advantages of using low cost films of few microns thick not only as a metallic contacts but also as a main structure of the solar cell consisted of high quality semiconductor layers. This paper reports the experimental studies of the CIGS absorber formation on Soda Lime Glass substrate covered by thin molybdenum film as a back contact layer. All structures were deposited with the use of magnetron sputtering method only. Technological parameters of the deposition process such as deposition power, pressure and deposition time were optimized for each layer of the structure. Mo back contact was examined in terms of resistivity. EDS measurements were carried out to verify stoichiometric composition of CIGS absorber. Thin film of Al was used as a top contact in order to examine the quality of p-n junction. The I-V electrical characteristic of the p-n junction was analysed in terms of solar cell application.

  1. Growth of TiO2 Thin Film on Various Substrates using RF Magnetron Sputtering

    International Nuclear Information System (INIS)

    Ali, Riyaz Ahmad Mohamed; Nayan, Nafarizal

    2011-01-01

    The conductivity of Titanium Dioxide (TiO 2 ) thin film fabricated using Radio Frequency (RF) Magnetron Sputtering on Silicon (Si), Indium doped--Tin Oxide (ITO) and microscope glass (M) substrates is presented in this paper. The dependant of thin film thickness and type of substrate been discussed. TiO 2 was deposited using Ti target in Ar+O 2 (45:10) mixture at 250 W for 45, 60, 75, 90, 105 and 120 minute. Resultant thickness varies from 295 nm to 724 nm with deposition rate 6.4 nm/min. On the other hand, resistivity, Rs value for ITO substrate is between 5.72x10 -7 to 1.54x10 -6 Ω.m, Si substrate range is between 3.52x10 -6 to 1.76x10 -5 Ω.m and M substrate range is between 99 to 332 Ω.m. The value of resistivity increases with the thickness of the thin film.

  2. Microstructure of ZnO thin films deposited by high power impulse magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Reed, A.N., E-mail: amber.reed.5@us.af.mil [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States); Department of Chemical and Materials Engineering, University of Dayton, Dayton, OH 45469 (United States); Shamberger, P.J. [Department of Materials Science and Engineering, Texas A& M University, College Station, TX 77843 (United States); Hu, J.J. [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States); University of Dayton Research Institute, University of Dayton, Dayton, OH 45469 (United States); Muratore, C. [Department of Chemical and Materials Engineering, University of Dayton, Dayton, OH 45469 (United States); Bultman, J.E. [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States); University of Dayton Research Institute, University of Dayton, Dayton, OH 45469 (United States); Voevodin, A.A., E-mail: andrey.voevodin@us.af.mil [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States)

    2015-03-31

    High power impulse magnetron sputtering was used to deposit thin (~ 100 nm) zinc oxide (ZnO) films from a ceramic ZnO target onto substrates heated to 150 °C. The resulting films had strong crystallinity, highly aligned (002) texture and low surface roughness (root mean square roughness less than 10 nm), as determined by X-ray diffraction, transmission electron microscopy, scanning electron microscopy and atomic force spectroscopy measurements. Deposition pressure and target–substrate distance had the greatest effect on film microstructure. The degree of alignment in the films was strongly dependent on the gas pressure. Deposition at pressures less than 0.93 Pa resulted in a bimodal distribution of grain sizes. An initial growth layer with preferred orientations (101) and (002) parallel to the interface was observed at the film–substrate interface under all conditions examined here; the extent of that competitive region was dependent on growth conditions. Time-resolved current measurements of the target and ion energy distributions, determined using energy resolved mass spectrometry, were correlated to film microstructure in order to investigate the effect of plasma conditions on film nucleation and growth. - Highlights: • Low temperature growth of nanocrystalline zinc oxide (ZnO) films. • ZnO films had a highly (002) textured, smooth, dense microstructure. • Dominant (002) orientation of films was pressure dependent. • Interfacial (101)/(002) mixed orientation layer controlled by substrate location.

  3. Annealing dependent evolution of columnar nanostructures in RF magnetron sputtered PTFE films for hydrophobic applications

    Science.gov (United States)

    Tripathi, S.; De, Rajnarayan; Maidul Haque, S.; Divakar Rao, K.; Misal, J. S.; Prathap, C.; Das, S. C.; Patidar, Manju M.; Ganesan, V.; Sahoo, N. K.

    2018-01-01

    Present communication focuses on a relatively less explored direction of producing rough polytetrafluoroethylene (PTFE) surfaces for possible hydrophobic applications. The experiments were carried out to make rough PTFE films without losing much of the transmission, which is an important factor while designing futuristic solar cell protection covers. After annealing temperature optimization, as grown RF magnetron sputtered PTFE films (prepared at 160 W RF power) were subjected to vacuum annealing at 200 °C for different time durations ranging from 1 to 4 h. The films show morphological evolution exhibiting formation and growth of columnar nanostructures that are responsible for roughening of the films due to annealing induced molecular migration and rearrangement. In agreement with this, qualitative analysis of corresponding x-ray reflectivity data shows modification in film thickness, which may again be attributed to the growth of columns at the expense of the atoms of remaining film molecules. However, the observations reveal that the film annealed at 200 °C for 2 h gives a combination of patterned columnar structures and reasonable transmission of >85% (in 500-1000 nm wavelength range), both of which are deteriorated when the films are annealed either at high temperature beyond 200 °C or for long durations >3 h. In addition, attenuated total reflection-Fourier transform infrared spectroscopy results reveal that the molecular bonds remain intact upon annealing at any temperature within the studied range indicating the stable nature of the films.

  4. Environmental effects on electrical properties of Cr-Si-Ni resistive films deposited by magnetron sputtering

    International Nuclear Information System (INIS)

    Zhang Yuqin; Dong Xianping; Wu Jiansheng

    2005-01-01

    The present paper investigated the environmental effects on electrical properties stability and long-term reliability of magnetron sputtered Cr-Si-Ni resistive films in 3.5% NaCl, 0.5 M Na 2 SO 4 and 0.5 M HCl solutions at 25 deg. C, which simulated marine, industrial and acidic environments. The relative resistance change (ΔR/R) for the annealed films revealed that the films had the best electrical properties stability and long-term reliability in industrial environments at 25 deg. C. After immersion in corrosion solutions for 480 h, the value of ΔR/R for the films was only 0.41% in industrial environments, and the values were 0.56 and 1.96% in marine and acidic environments, respectively. The polarization measurements and AES results indicated that the films presented a spontaneous trend to passivation, and could form a dense and stable protective oxide layer (Si oxide) on its surface rapidly that protected the films from further corrosion in three different environments. Furthermore, the formed passive film in industrial environments exhibited much more protective effects on the films than in marine and acidic environments

  5. Initial growth and texture formation during reactive magnetron sputtering of TiN on Si(111)

    CERN Document Server

    Li, T Q; Tsuji, Y; Ohsawa, T; Komiyama, H

    2002-01-01

    The initial growth and texture formation mechanism of titanium nitride (TiN) films were investigated by depositing TiN films on (111) silicon substrates by using reactive magnetron sputtering of a Ti metallic target under a N sub 2 /Ar atmosphere, and then analyzing the films in detail by using transmission electron microscopy (TEM) and x-ray diffraction (XRD). Two power sources for the sputtering, dc and rf, were compared. At the initial growth stage, a continuous amorphous film containing randomly oriented nuclei was observed when the film thickness was about 3 nm. The nuclei grew and formed a polycrystalline layer when the film thickness was about 6 nm. As the film grew further, its orientation changed depending on the deposition conditions. For dc sputtering, the appearance of (111) or (200)-preferred orientations depended on the N sub 2 partial pressure, and the intensity of the preferred orientation increased with increasing film thickness. For rf sputtering, however, when the film thickness was small (...

  6. Characteristics of ZnO/diamond thin films prepared by RF magnetron sputtering

    CERN Document Server

    Park, Y W; Lee, J G; Baik, Y J; Kim, H J; Jung, H J; Choi, W K; Cho, B H; Park, C Y

    1999-01-01

    Due to its high Young's modulus, diamond has the highest acoustic wave velocity among all materials and is expected to be a candidate substrate for high-frequency surface acoustic wave(SAW) devices. In this study, the deposition of ZnO, as a piezoelectric layer, on a diamond substrate is investigated. ZnO has been fabricated by using RF magnetron sputtering with a ZnO target and various Ar/O sub 2 gas ratios, RF powers, and substrate temperatures at a vacuum of 10 sup - sup 5 Torr. The sputtered ZnO films are characterized by X-ray diffraction (XRD), Rutherford backscattering spectroscopy (RBS), X-ray photoelectron spectroscopy (XPS), and I-V characteristics. All the films show only a (002) orientation. The atomic concentration of the sputtered ZnO films is changed by the oxygen gas ratio, and the ZnO films are grown with a homogeneous composition over their entire thickness. The electrical resistivity of the films varied from 4x10 sup 3 to 7x10 sup 8 OMEGA cm, depending on the Ar/O sub 2 gas ratio. The phase...

  7. Biocompatibility of GaSb thin films grown by RF magnetron sputtering

    Science.gov (United States)

    Nishimoto, Naoki; Fujihara, Junko; Yoshino, Katsumi

    2017-07-01

    GaSb may be suitable for biological applications, such as cellular sensors and bio-medical instrumentation because of its low toxicity compared with As (III) compounds and its band gap energy. Therefore, the biocompatibility and the film properties under physiological conditions were investigated for GaSb thin films with or without a surface coating. GaSb thin films were grown on quartz substrates by RF magnetron sputtering, and then coated with (3-mercaptopropyl) trimethoxysilane (MPT). The electrical properties, surface morphology, and crystal structure of the GaSb thin film were unaffected by the MPT coating. The cell viability assay suggested that MPT-coated GaSb thin films are biocompatible. Bare GaSb was particularly unstable in pH9 buffer. Ga elution was prevented by the MPT coating, although the Ga concentration in the pH 9 buffer was higher than that in the other solutions. The surface morphology and crystal structure were not changed by exposure to the solutions, except for the pH 9 buffer, and the thin film properties of MPT-coated GaSb exposed to distilled water and H2O2 in saline were maintained. These results indicate that MPT-coated GaSb thin films are biocompatible and could be used for temporary biomedical devices.

  8. Characterization and properties Ti-Al-Si-N nanocomposite coatings prepared by middle frequency magnetron sputtering

    Science.gov (United States)

    Zou, C. W.; Zhang, J.; Xie, W.; Shao, L. X.; Guo, L. P.; Fu, D. J.

    2011-10-01

    TiN-containing amorphous Ti-Al-Si-N (nc-TiN/a-Si 3N 4 or a-AlN) nanocomposite coatings were deposited by using a modified closed field twin unbalanced magnetron sputtering system which is arc assisted and consists of two circles of targets, at a substrate temperature of 300 °C. XRD, XPS and High-resolution TEM experiments showed that the coatings contain TiN nanocrystals embedded in the amorphous Si 3N 4 or AlN matrix. The coatings exhibit good mechanical properties that are greatly influenced by the Si contents. The hardness of the Ti-Al-Si-N coatings deposited at Si targets currents of 5, 8, 10, and 12 A were 45, 47, 54 and 46 GPa, respectively. The high hardness of the deposited Ti-Al-Si-N coatings may be own to the plastic distortion and dislocation blocking by the nanocrystalline structure. On the other hand, the friction coefficient decreases monotonously with increasing Si contents. This result would be caused by tribo-chemical reactions, which often take place in many ceramics, e.g. Si 3N 4 reacts with H 2O to produce SiO 2 or Si(OH) 2 tribolay-layer.

  9. Helium-Charged La-Ni-Al Thin Films Deposited by Magnetron Sputtering

    International Nuclear Information System (INIS)

    Shi Liqun; Chen Deming; Xu Shilin; Liu Chaozhu; Hao Wanli; Zhou Zhuyin

    2005-01-01

    An advanced implantation of low energy helium-4 atoms during the La-Ni-Al film growth by adopting magnetron sputtering with Ar/He mixture gases is discussed. Both proton backscattering spectroscopy (PBS) and elastic recoil detection (ERD) analyses were adopted to measure helium concentration of the films and distribution in the near-surface region. Helium atoms with a high concentration incorporate evenly in deposited film. The introduction of the helium with no extra irradiation damage is expected by choosing suitable deposition conditions. It was found that amorphous and crystalline LaNi 5 -type structures can be achieved when sputtered with pure Ar and Ar/He mixture gases at room temperature, respectively. Thermal desorption experiments proposes that a part of hydrogen atoms are bound to trapped helium at crystal and releases together with helium. Only a small fraction of helium is released from the helium-vacancy clusters in lower temperature range and most of helium is released from small size helium bubbles in the high temperature range

  10. Chemical environment of iron atoms in iron oxynitride films synthesized by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Grafoute, M.; Petitjean, C.; Rousselot, C.; Pierson, J.F.; Greneche, J.M.

    2007-01-01

    An iron oxynitride film was deposited on silicon and glass substrates by magnetron sputtering in an Ar-N 2 -O 2 reactive mixture. Rutherford back-scattering spectrometry was used to determine the film composition (Fe 1.06 O 0.35 N 0.65 ). X-ray diffraction revealed the formation of a face-centred cubic (fcc) structure with a lattice parameter close to that of γ'''-FeN. X-ray photoelectron spectroscopy showed the occurrence of Fe-N and Fe-O bonds in the film. The local environment of iron atoms studied by 57 Fe Moessbauer spectrometry at both 300 and 77 K gives clear evidence that the Fe 1.06 O 0.35 N 0.65 is not a mixture of iron oxide and iron nitride phases. Despite a small amount of an iron nitride phase, the main sample consists of an iron oxynitride phase with an NaCl-type structure where oxygen atoms partially substitute for nitrogen atoms, thus indicating the formation of a iron oxynitride with an fcc structure

  11. Field emission from ZnS nanorods synthesized by radio frequency magnetron sputtering technique

    Science.gov (United States)

    Ghosh, P. K.; Maiti, U. N.; Jana, S.; Chattopadhyay, K. K.

    2006-11-01

    The field emission property of zinc sulphides nanorods synthesized in the thin film form on Si substrates has been studied. It is seen that ZnS nanorod thin films showed good field emission properties with a low-macroscopic turn-on field (2.9-6.3 V/μm). ZnS nanorods were synthesized by using radio frequency magnetron sputtering of a polycrystalline prefabricated ZnS target at a relatively higher pressure (10 -1 mbar) and at a lower substrate temperature (233-273 K) without using any catalyst. Transmission electron microscopic image showed the formation of ZnS nanorods with high aspect ratio (>60). The field emission data were analysed using Fowler-Nordhiem theory and the nearly straight-line nature of the F-N plots confirmed cold field emission of electrons. It was also found that the turn-on field decreased with the decrease of nanorod's diameters. The optical properties of the ZnS nanorods were also studied. From the measurements of transmittance of the films deposited on glass substrates, the direct allowed bandgap values have been calculated and they were in the range 3.83-4.03 eV. The thickness of the films was ˜600 nm.

  12. Substrates effect on Zn1-xMnxO thin films grown by RF magnetron sputtering

    International Nuclear Information System (INIS)

    Elanchezhiyan, J.; Bhuvana, K.P.; Gopalakrishnan, N.; Balasubramanian, T.

    2008-01-01

    In this paper, we have presented the surface effect of the substrates on Mn doped ZnO (Zn 1-x Mn x O) thin films grown on Si(1 0 0) and sapphire [i.e. Al 2 O 3 (0 0 0 1)] by RF magnetron sputtering. These grown films have been characterized by X-ray diffraction (XRD), photoluminescence (PL) and vibrating sample magnetometer (VSM) to know its structural, optical and magnetic properties. All these properties have been found to be strongly influenced by the substrate surface on which the films have been deposited. The XRD results show that the Mn doped ZnO films deposited on Si(1 0 0) exhibit a polycrystalline nature whereas the films on sapphire substrate have only (0 0 2) preferential orientations indicating that the films are single crystalline. The studies of room temperature PL spectra reveal that the Zn 1-x Mn x O/Si(1 0 0) system is under severe compressive strain while the strain is almost relaxed in Zn 1-x Mn x O/Al 2 O 3 (0 0 0 1) system. It has been observed from VSM studies that Zn 1-x Mn x O/Al 2 O 3 (0 0 0 1) system shows ferromagnetic nature while the paramagnetic behaviour observed in Zn 1-x Mn x O/Si(1 0 0) system

  13. Structure evolution of zinc oxide thin films deposited by unbalance DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Aryanto, Didik, E-mail: didi027@lipi.go.id [Research Center for Physics, Indonesian Institute of Sciences, Serpong 15314, Tangerang Selatan (Indonesia); Materials Research Group, Physics Department, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Marwoto, Putut; Sugianto [Physics Department, Faculty of Mathematics and Science, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Materials Research Group, Physics Department, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Sudiro, Toto [Research Center for Physics, Indonesian Institute of Sciences, Serpong 15314, Tangerang Selatan (Indonesia); Birowosuto, Muhammad D. [Research Center for Physics, Indonesian Institute of Sciences, Serpong 15314, Tangerang Selatan (Indonesia); CINTRA UMI CNRS/NTU/THALES 3288 Research Techno Plaza, 50 Nanyang Drive, Border X Block, level 6, 637553 (Singapore); Sulhadi [Physics Department, Faculty of Mathematics and Science, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia)

    2016-04-19

    Zinc oxide (ZnO) thin films are deposited on corning glass substrates using unbalanced DC magnetron sputtering. The effect of growth temperature on surface morphology and crystallographic orientation of ZnO thin film is studied using atomic force microscopy (AFM) and X-ray diffraction (XRD) techniques. The surface morphology and crystallographic orientation of ZnO thin film are transformed against the increasing of growth temperature. The mean grain size of film and the surface roughness are inversely and directly proportional towards the growth temperature from room temperature to 300 °C, respectively. The smaller grain size and finer roughness of ZnO thin film are obtained at growth temperature of 400 °C. The result of AFM analysis is in good agreement with the result of XRD analysis. ZnO thin films deposited in a series of growth temperatures have hexagonal wurtzite polycrystalline structures and they exhibit transformations in the crystallographic orientation. The results in this study reveal that the growth temperature strongly influences the surface morphology and crystallographic orientation of ZnO thin film.

  14. Thermal stability of tungsten sub-nitride thin film prepared by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, X.X. [School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050 (China); State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730050 (China); Wu, Y.Z., E-mail: youzhiwu@163.com [School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050 (China); Mu, B. [College of Petrochemical Technology, Lanzhou University of Technology, Lanzhou, 730050 (China); Qiao, L. [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730050 (China); Li, W.X.; Li, J.J. [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China); Wang, P., E-mail: pengwang@licp.cas.cn [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730050 (China)

    2017-03-15

    Tungsten sub-nitride thin films deposited on silicon samples by reactive magnetron sputtering were used as a model system to study the phase stability and microstructural evolution during thermal treatments. XRD, SEM&FIB, XPS, RBS and TDS were applied to investigate the stability of tungsten nitride films after heating up to 1473 K in vacuum. At the given experimental parameters a 920 nm thick crystalline film with a tungsten and nitrogen stoichiometry of 2:1 were achieved. The results showed that no phase and microstructure change occurred due to W{sub 2}N film annealing in vacuum up to 973 K. Heating up to 1073 K led to a partial decomposition of the W{sub 2}N phase and the formation of a W enrichment layer at the surface. Increasing the annealing time at the same temperature, the further decomposition of the W{sub 2}N phase was negligible. The complete decomposition of W{sub 2}N film happened as the temperature reached up to 1473 K.

  15. Development of Nb$_3$Sn coatings by magnetron sputtering for SRF cavities

    CERN Document Server

    Rosaz, G.; Leaux, F.; Motschmann, F.; Mydlarz, Z.; Taborelli, M.; Vollenberg, W.

    2016-01-01

    Cost and energy savings are an integral requirement in the design of future particle accelerators. Very low losses SRF accelerating systems, together with high-efficiency cryogenics systems, have the potential of low running costs. The association to the capital cost reduction allowed by thin films coated copper cavities may represent the best overall cost-performance compromise. This strategy has been applied for instance in LEP, the LHC and HIE-ISOLDE with the niobium thin films technology. New materials must be considered to improve the quality factor of the cavities, such as Nb$_{3}$Sn, which could also ideally operate at higher temperature thus allowing further energy savings. The study considers the possibility to coat a copper resonator with an Nb$_{3}$Sn layer by means of magnetron sputtering using an alloyed target. We present the impact of the process parameters on the as-deposited layer stoichiometry. The latter is in good agreement with previous results reported in the literature and can be tuned ...

  16. Characterization of AZO and Ag based films prepared by RF magnetron sputtering

    International Nuclear Information System (INIS)

    Miao, Dagang; Jiang, Shouxiang; Zhao, Hongmei; Shang, Songmin; Chen, Zhuoming

    2014-01-01

    Highlights: • Highly infrared reflective AZO and Ag based films were prepared. • Ag showed better crystallization on AZO film than on glass substrate. • Infrared reflection rate was inversely proportional to the film sheet resistance. • Film with infrared reflection of 97% in FIR region was acquired. - Abstract: Ag, AZO/Ag, Ag/AZO and AZO/Ag/AZO films were prepared on glass substrates by radio frequency (RF) magnetron sputtering technology. The prepared films were systematically investigated by X-ray Diffraction (XRD), Atomic Force Microscopy (AFM), UV–visible spectrophotometer, a four-point probe system and Fourier Transform Infrared Spectroscopy. The results indicated that Ag inner layer starts forming a continuous film at the thickness of 10 nm and Ag layer presents superior crystallization on AZO substrate than that on glass substrate. The continuous Ag inner layer film provided the highest average visible transmittance of 85.4% (AZO/Ag/AZO). The lowest sheet resistance of 3.21 Ω/sq and the highest infrared reflection rate of 97% in FIR region can be obtained on AZO/Ag (15 nm)/AZO film. The high infrared reflection property of the AZO/Ag/AZO coating makes it a promising candidate for solar control films

  17. Composition and optical properties tunability of hydrogenated silicon carbonitride thin films deposited by reactive magnetron sputtering

    Science.gov (United States)

    Bachar, A.; Bousquet, A.; Mehdi, H.; Monier, G.; Robert-Goumet, C.; Thomas, L.; Belmahi, M.; Goullet, A.; Sauvage, T.; Tomasella, E.

    2018-06-01

    Radiofrequency reactive magnetron sputtering was used to deposit hydrogenated amorphous silicon carbonitride (a-SiCxNy:H) at 400 °C by sputtering a silicon target under CH4 and N2 reactive gas mixture. Rutherford backscattering spectrometry revealed that the change of reactive gases flow rate (the ratio R = FN2/(FN2+FCH4)) induced a smooth chemical composition tunability from a silicon carbide-like film for R = 0 to a silicon nitride-like one at R = 1 with a large area of silicon carbonitrides between the two regions. The deconvolution of Fourier Transform InfraRed and X-ray photoelectron spectroscopy spectrum highlighted a shift of the chemical environment of the deposited films corresponding to the changes seen by RBS. The consequence of these observations is that a control of refractive index in the range of [1.9-2.5] at λ = 633 nm and optical bandgap in the range [2 eV-3.8 eV] have been obtained which induces that these coatings can be used as antireflective coatings in silicon photovoltaic cells.

  18. Characteristics of a-IGZO/ITO hybrid layer deposited by magnetron sputtering.

    Science.gov (United States)

    Bang, Joon-Ho; Park, Hee-Woo; Cho, Sang-Hyun; Song, Pung-Keun

    2012-04-01

    Transparent a-IGZO (In-Ga-Zn-O) films have been actively studied for use in the fabrication of high-quality TFTs. In this study, a-IGZO films and a-IGZO/ITO double layers were deposited by DC magnetron sputtering under various oxygen flow rates. The a-IGZO films showed an amorphous structure up to 500 degrees C. The deposition rate of these films decreased with an increase in the amount of oxygen gas. The amount of indium atoms in the film was confirmed to be 11.4% higher than the target. The resistivity of double layer follows the rules for parallel DC circuits The maximum Hall mobility of the a-IGZO/ITO double layers was found to be 37.42 cm2/V x N s. The electrical properties of the double layers were strongly dependent on their thickness ratio. The IGZO/ITO double layer was subjected to compressive stress, while the ITO/IGZO double layer was subjected to tensile stress. The bending tolerance was found to depend on the a-IGZO thickness.

  19. Mechanical and tribological properties of crystalline aluminum nitride coatings deposited on stainless steel by magnetron sputtering

    International Nuclear Information System (INIS)

    Choudhary, R.K.; Mishra, S.C.; Mishra, P.; Limaye, P.K.; Singh, K.

    2015-01-01

    Aluminum nitride (AlN) coating is a potential candidate for addressing the problems of MHD pressure drop, tritium permeation and liquid metal corrosion of the test blanket module of fusion reactor. In this work, AlN coatings were grown on stainless steel by magnetron sputtering. Grazing incidence X-ray diffraction measurement revealed that formation of mixed phase (wurtzite and rock salt) AlN was favored at low discharge power and substrate negative biasing. However, at sufficiently high discharge power and substrate bias, (100) oriented wurtzite AlN was obtained. Secondary ion mass spectroscopy showed presence of oxygen in the coatings. The highest value of hardness and Young's modulus were 14.1 GPa and 215 GPa, respectively. Scratch test showed adhesive failure at a load of about 20 N. Wear test showed improved wear resistance of the coatings obtained at higher substrate bias. - Highlights: • Crystalline AlN coatings obtained on stainless steel by reactive sputtering. • Wurtzite AlN formed at higher discharge power and higher substrate biasing. • Mixture of wurtzite and rock salt AlN formed at low power and low biasing. • Substrate negative biasing improved adhesion of AlN coatings. • Substrate negative biasing improved wear resistance and hardness of AlN coatings.

  20. Deposition and characterization of NbAIN thin films by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Carvalho, R.G.; Felix, L.C.; Fernandez, D.A.R.; Fontes Junior, A.S.; Oliveira, G.B.; Tentardini, E.K.

    2016-01-01

    The objective of this work was to study NbAlN thin films and the influence of variation in the concentration of aluminum in the crystal structure and oxidation resistance of these coatings. The thin films were deposited by reactive magnetron sputtering and characterized by Grazing Incidence X-ray Diffraction (GIXRD), Energy Dispersive Spectroscopy (EDS) and oxidation tests at high temperatures. NbAlN thin films were deposited and present at concentration of 10, 20 and 42 at% Al. The NbAlN crystalline phase obtained was the δ-NbN, however it was observed a shift of the peaks in the patterns obtained GIXRD of regions for larger angles for these samples, indicating the formation of a solid solution. The higher oxidation resistance temperature was 700° C for the sample with 42 in at% Al. From the SEM analysis it was possible to observe the surface of the film after oxidation, all films showed defects, however the amount of such defects was lower in samples with higher aluminum concentrations. (author)

  1. Deposition and characterization of IrOx nanofoils on carbon nanotube templates by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Chen, Yi-Min; Cai, Jhen-Hong; Huang, Ying-Sheng; Lee, Kuei-Yi; Tsai, Dah-Shyang; Tiong, Kwong-Kau

    2012-01-01

    Large surface area IrO x nanofoils (IrO x NF) were deposited on multi-wall carbon nanotube (MWCNT) templates, forming IrO x /MWCNT nanocomposites, by reactive radio frequency magnetron sputtering using Ir metal target. The structural and spectroscopic properties of IrO x NF were characterized. The micrographs of field emission scanning electron microscopy showed the formation of foil-like structure for the as-deposited samples. Transmission electron microscopy analysis revealed the contiguous presence of glassy iridium oxide, iridium metal, and iridium dioxide nanocrystals in the foil. X-ray photoelectron spectroscopy analysis provided the information of the oxidation states and the stoichiometry of IrO x NF. Raman spectra revealed the amorphous-like phase of the as-deposited IrO x NF. The nanofoil structure provided ultra-high surface area for electrical charge storage which made the IrO x /MWCNT nanocomposites as an attractive candidate for the supercapacitor applications.

  2. Biocompatibility and Surface Properties of TiO2 Thin Films Deposited by DC Magnetron Sputtering

    Science.gov (United States)

    López-Huerta, Francisco; Cervantes, Blanca; González, Octavio; Hernández-Torres, Julián; García-González, Leandro; Vega, Rosario; Herrera-May, Agustín L.; Soto, Enrique

    2014-01-01

    We present the study of the biocompatibility and surface properties of titanium dioxide (TiO2) thin films deposited by direct current magnetron sputtering. These films are deposited on a quartz substrate at room temperature and annealed with different temperatures (100, 300, 500, 800 and 1100 °C). The biocompatibility of the TiO2 thin films is analyzed using primary cultures of dorsal root ganglion (DRG) of Wistar rats, whose neurons are incubated on the TiO2 thin films and on a control substrate during 18 to 24 h. These neurons are activated by electrical stimuli and its ionic currents and action potential activity recorded. Through X-ray diffraction (XRD), the surface of TiO2 thin films showed a good quality, homogeneity and roughness. The XRD results showed the anatase to rutile phase transition in TiO2 thin films at temperatures between 500 and 1100 °C. This phase had a grain size from 15 to 38 nm, which allowed a suitable structural and crystal phase stability of the TiO2 thin films for low and high temperature. The biocompatibility experiments of these films indicated that they were appropriated for culture of living neurons which displayed normal electrical behavior. PMID:28788667

  3. Experimental investigation on photoelectric properties of ZAO thin film deposited on flexible substrate by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Hao, Ming [School of Mechanical Engineering and Automation, Northeastern University, 3-11 WenHua Rd., 319#, Shenyang, 110004 (China); Liu, Kun, E-mail: kliu@mail.neu.edu.cn [School of Mechanical Engineering and Automation, Northeastern University, 3-11 WenHua Rd., 319#, Shenyang, 110004 (China); Liu, Xinghua [Hubei Aerospace Industry Technology Academe Special Vehicle Technology Center, Wuhan (China); Wang, Dongyang; Ba, Dechun; Xie, Yuanhua; Du, Guangyu; Ba, Yaoshuai [School of Mechanical Engineering and Automation, Northeastern University, 3-11 WenHua Rd., 319#, Shenyang, 110004 (China)

    2016-12-01

    Highlights: • ZAO thin films were deposited on PET substrate. • A set of experimental parameters were systematically investigated. • Change rule of film photoelectric properties was obtained. • ZAO films with optimal properties were obtained at our working conditions. - Abstract: Transparent conductive ZAO (Zinc Aluminum Oxide) films on flexible substrates have a great potential for low-cost mass-production solar cells. ZAO thin films were achieved on flexible PET (polyethylene terephthalate) substrates by RF magnetron sputtering technology. The surface morphology and element content, the transmittance and the sheet resistance of the films were measured to determine the optical process parameters. The results show that the ZAO thin film shows the best parameters in terms of photoelectric performance including sputtering power, working pressure, sputtering time, substrate temperature (100 W, 1.5 Pa, 60 min, 125 °C). The sheet resistance of 510 Ω and transmittance in visible region of 92% were obtained after characterization. Surface morphology was uniform and compact with a good crystal grain.

  4. Adhesion analysis for chromium nitride thin films deposited by reactive magnetron sputtering

    Science.gov (United States)

    Rusu, F. M.; Merie, V. V.; Pintea, I. M.; Molea, A.

    2016-08-01

    The thin film industry is continuously growing due to the wide range of applications that require the fabrication of advanced components such as sensors, biological implants, micro-electromechanical devices, optical coatings and so on. The selection regarding the deposition materials, as well as the deposition technology influences the properties of the material and determines the suitability of devices for certain real-world applications. This paper is focused on the adhesion force for several chromium nitride thin films obtained by reactive magnetron sputtering. All chromium nitride thin films were deposited on a silicon substrate, the discharge current and the argon flow being kept constant. The main purpose of the paper is to determine the influence of deposition parameters on the adhesion force. Therefore some of the deposition parameters were varied in order to study their effect on the adhesion force. Experimentally, the values of the adhesion force were determined in multiple points for each sample using the spectroscopy in point mode of the atomic force microscope. The obtained values were used to estimate the surface energy of the CrN thin films based on two existing mathematical models for the adhesion force when considering the contact between two bodies.

  5. Origin of stress in radio frequency magnetron sputtered zinc oxide thin films

    International Nuclear Information System (INIS)

    Menon, Rashmi; Gupta, Vinay; Sreenivas, K.; Tan, H. H.; Jagadish, C.

    2011-01-01

    Highly c-axis oriented ZnO thin films have been deposited on silicon substrates by planar rf magnetron sputtering under varying pressure (10-50 mTorr) and oxygen percentage (50-100%) in the reactive gas (Ar + O 2 ) mixture. The as-grown films were found to be stressed over a wide range from -1 x 10 11 to -2 x 10 8 dyne/cm 2 that in turn depends strongly on the processing conditions, and the film becomes stress free at a unique combination of sputtering pressure and reactive gas composition. Raman spectroscopy and photoluminescence (PL) analyses identified the origin of stress as lattice distortion due to defects introduced in the ZnO thin film. FTIR study reveals that Zn-O bond becomes stronger with the increase in oxygen fraction in the reactive gas mixture. The lattice distortion or stress depends on the type of defects introduced during deposition. PL spectra show the formation of a shoulder in band emission with an increase in the processing pressure and are related to the presence of stress. The ratio of band emission to defect emission decreases with the increase in oxygen percentage from 50 to 100%. The studies show a correlation of stress with the structural, vibrational, and photoluminescence properties of the ZnO thin film. The systematic study of the stress will help in the fabrication of efficient devices based on ZnO film.

  6. Structural and optical properties of DC reactive magnetron sputtered zinc aluminum oxide thin films

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, B. Rajesh, E-mail: rajphyind@gmail.com [Department of Physics, GITAM Institute of Technology, GITAM University, Visakhapatnam - 530 045, A.P. (India); Rao, T. Subba, E-mail: thotasubbarao6@gmail.com [Department of Physics, Sri Krishnadevaraya University, Anantapuramu - 515 003, A.P. (India)

    2014-10-15

    Highly transparent conductive Zinc Aluminum Oxide (ZAO) thin films have been deposited on glass substrates using DC reactive magnetron sputtering method. The thin films were deposited at 200 °C and post-deposition annealing from 15 to 90 min. XRD patterns of ZAO films exhibit only (0 0 2) diffraction peak, indicating that they have c-axis preferred orientation perpendicular to the substrate. Scanning electron microscopy (SEM) is used to study the surface morphology of the films. The grain size obtained from SEM images of ZAO thin films are found to be in the range of 20 - 26 nm. The minimum resistivity of 1.74 × 10{sup −4} Ω cm and an average transmittance of 92% are obtained for the thin film post annealed for 30 min. The optical band gap of ZAO thin films increased from 3.49 to 3.60 eV with the increase of annealing time due to Burstein-Moss effect. The optical constants refractive index (n) and extinction coefficient (k) were also determined from the optical transmission spectra.

  7. Improvement of dielectric properties of BLT thin films deposited by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Besland, M P; Barroy, P R J; Richard-Plouet, M; Tessier, P Y; Brohan, L; Djouadi, M A [Universite de Nantes - Institut des Materiaux Jean Rouxel, UMR CNRS 6502, 2, rue de la Houssiniere BP32229, 44322 Nantes Cedex (France); Borderon, C; Tacon, S Le; Averty, D; Gundel, H W [Institut de Recherche en Electrotechnique et Electronique de Nantes Atlantique, UPRES-EA 1770, IREENA, Universite de Nantes, 2, rue de la Houssiniere, BP 92208, 44322 Nantes Cedex (France)], E-mail: Marie-Paule.Besland@cnrs-imn.fr

    2008-01-15

    Well crystallized BLT thin films were deposited by RF magnetron sputtering using a target of Aurivillius phase Bi{sub 3.25}La{sub 0.75}Ti{sub 3}O{sub 12}(BLT{sub 0,75}), elaborated in our institute. RF sputtering experiments were performed at room temperature with an argon/oxygen mixture, in a pressure range of 20-50 mTorr. Optimisation of the plasma parameters, namely deposition pressure, RF power and oxygen content in the gas phase, allows obtaining BLT films with a chemical composition close to Bi{sub 3.25}La{sub 0.75}Ti{sub 3}O{sub 12}. After ex-situ annealing under oxygen atmosphere at 650 deg. C, BLT films deposited on Pt/TiO{sub 2}/SiO{sub 2}/Si (multilayer) substrates exhibit well defined rod-like grains morphology. A two step deposition process appeared to be necessary in order to reach satisfying dielectric properties. The effect of the plasma parameters on the chemical composition and electrical properties are presented and discussed.

  8. Improvement of dielectric properties of BLT thin films deposited by magnetron sputtering

    International Nuclear Information System (INIS)

    Besland, M P; Barroy, P R J; Richard-Plouet, M; Tessier, P Y; Brohan, L; Djouadi, M A; Borderon, C; Tacon, S Le; Averty, D; Gundel, H W

    2008-01-01

    Well crystallized BLT thin films were deposited by RF magnetron sputtering using a target of Aurivillius phase Bi 3.25 La 0.75 Ti 3 O 12 (BLT 0,75 ), elaborated in our institute. RF sputtering experiments were performed at room temperature with an argon/oxygen mixture, in a pressure range of 20-50 mTorr. Optimisation of the plasma parameters, namely deposition pressure, RF power and oxygen content in the gas phase, allows obtaining BLT films with a chemical composition close to Bi 3.25 La 0.75 Ti 3 O 12 . After ex-situ annealing under oxygen atmosphere at 650 deg. C, BLT films deposited on Pt/TiO 2 /SiO 2 /Si (multilayer) substrates exhibit well defined rod-like grains morphology. A two step deposition process appeared to be necessary in order to reach satisfying dielectric properties. The effect of the plasma parameters on the chemical composition and electrical properties are presented and discussed

  9. Application of high rate magnetron sputtering to the fabrication of A-15 compounds

    International Nuclear Information System (INIS)

    Kampwirth, R.T.; Hafstrom, J.W.; Wu, C.T.

    1976-01-01

    High quality Nb 3 Sn films have been fabricated using a recently developed magnetron sputtering process capable of deposition rates approaching 1 μm/min. at sputtering voltages less than 500 V and power levels of about 5 KW. Low sputtering voltages allow more complete thermalization at lower pressures of the material condensing on the substrate which can improve long range order. Transition temperatures of up to 18.3 0 K, J/sub c/(O)'s of 15 x 10 6 A/cm 2 and Hc 2 as high as 240 kOe have been achieved in 1-3 μm films deposited from a Nb 3 Sn reacted powder target with substrate temperatures between 600 and 800 0 C. The films exhibit smooth surfaces and, generally, a [200] preferred orientation. The growth of the film is columnar in nature. The sputtering parameters, substrate material and temperature will be related to film structure T/sub c/ and J/sub c/(H,T) and the Nb/Sn ratio as determined by Rutherford backscattering

  10. Low temperature ITO thin film deposition on PES substrate using pulse magnetron sputtering

    International Nuclear Information System (INIS)

    Lin, Y.C.; Li, J.Y.; Yen, W.T.

    2008-01-01

    Experiments were conducted using pulse magnetron sputtering (PMS) to deposit transparent conducting indium tin oxide (ITO) thin film onto flexible polyethersulfone (PES) plastic substrates. The thin film microstructure, optoelectronic and residual stress were analyzed using the modulating PMS power, work pressure, pulse frequency, duty cycle and cycle time process parameters. The residual stress of the thin film was determined by scanning electron microscopy (SEM) combined with the Sony equation. The experimental results show that PMS has a lower process temperature, higher deposition rate and lower resistivity compared with the radio frequency process at the same output power. The duty cycle increase produces the optimum optoelectronic characteristics. When the pressure, power, duty cycle and sputter time are increased, the thin film stress will also increase, causing flexural distortion in the PES plastic substrate. When the deposition thickness reaches 1.5 μm, ITO thin film will appear with a distinct split. Under 5 mtorr work pressure, 60 W power, 33 μs duty time and 2 μs pulse reverse time at duty cycle 95%, thin film with an optimized electrical 3.0 x 10 -4 Ω-cm, RMS surface roughness of 0.85 nm and visible region optical transmittance will be achieved with acquisition of over 85%

  11. Corrosion resistance of CrN thin films produced by dc magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Ruden, A. [Laboratorio de Física del Plasma, Universidad Nacional de Colombia Sede Manizales, Km. 9 vía al Magdalena, Manizales (Colombia); Laboratorio de Recubrimientos Duros y Aplicaciones Industriales–RDAI, Universidad del Valle, Calle 13 N° 100-00 Ciudadela Meléndez, Cali (Colombia); Departamento de matemáticas, Universidad Tecnológica de Pereira, Pereira (Colombia); Restrepo-Parra, E., E-mail: erestrepopa@unal.edu.co [Laboratorio de Física del Plasma, Universidad Nacional de Colombia Sede Manizales, Km. 9 vía al Magdalena, Manizales (Colombia); Paladines, A.U.; Sequeda, F. [Laboratorio de Recubrimientos Duros y Aplicaciones Industriales–RDAI, Universidad del Valle, Calle 13 N° 100-00 Ciudadela Meléndez, Cali (Colombia)

    2013-04-01

    In this study, the electrochemical behavior of chromium nitride (CrN) coatings deposited on two steel substrates, AISI 304 and AISI 1440, was investigated. The CrN coatings were prepared using a reactive d.c. magnetron sputtering deposition technique at two different pressures (P1 = 0.4 Pa and P2 = 4 Pa) with a mixture of N{sub 2}–Ar (1.5-10). The microstructure and crystallinity of the CrN coatings were investigated using X-ray diffraction. The aqueous corrosion behavior of the coatings was evaluated using two methods. The polarization resistance (Tafel curves) and electrochemical impedance spectra (EIS) in a saline (3.5% NaCl solution) environment were measured in terms of the open-circuit potentials and polarization resistance (R{sub p}). The results indicated that the CrN coatings present better corrosion resistance and R{sub p} values than do the uncoated steel substrates, especially for the coatings produced on the AISI 304 substrates, which exhibited a strong enhancement in the corrosion resistance. Furthermore, better behavior was observed for the coatings produced at lower pressures (0.4 Pa) than those grown at 4 Pa.

  12. Spatial survey of a magnetron plasma sputtering system using a Langmuir probe

    International Nuclear Information System (INIS)

    Field, D.J.; Dew, S.K.; Burrell, R.E.

    2002-01-01

    A two-dimensional spatial survey is conducted for a magnetron sputtering plasma at two pressures (40 and 5 mTorr) using a Langmuir probe. The plasma density is found to be highest (up to 6.0x10 10 cm -3 ) above the etch region of the cathode, near the magnetic trap. The density drops between the etch regions, near the edges of the cathode and also at distances farther away from the cathode. The floating potential was found to be most negative (down to -12 V) in regions where the highest electron temperatures were observed (up to almost 4 eV) and became less negative (near 0 V) in regions where the electron temperature was lowest (less than 0.5 eV). This complementary trend was consistent in all spatial locations and at both pressures. The plasma potential was found to have very weak dependence, if any, on spatial location and pressure. The relationship between electron transport processes, collision processes and electron temperatures is discussed. Electron energy distribution functions were found to be either Maxwellian or bi-Maxwellian in nature, depending on pressure and spatial location. Maxwellian distributions were found near the magnetic trap or source of the plasma. Bi-Maxwellian distributions were found further away from the source, and it appears they result from Maxwellian distributions bifurcating as they diffuse away from the source. The suitability of the popular models for this bifurcation is discussed

  13. Electronic motion in the pre-oscillation phase of a smooth bore magnetron

    International Nuclear Information System (INIS)

    Garelis, E.; Hickman, R.B.

    1979-01-01

    The calculation of the electronic motion in the pre-oscillation phase of a smooth bore magnetron is the problem of calculating the electronic motion in the region between two concentric cylinders with an applied radial electric field and a constant axial B/sub z/ magnetic field. The inner cylinder represents the electron emitting cathode and the outer cylinder represents the anode. The emission is assumed to be space charge limited. This results in an electronic cloud surrounding the cathode. The radial velocity of the electrons is limited by the space charge and in addition the axial magnetic field tends to curve the path of the electrons so that they return to the cathode. Consequently, the electronic orbit extends to some distance r 0 from the cathode and for values of the radius r > r 0 exists a charge free region. The model assumes relativistic electronic motion with self-consistent magnetic fields. The magnetic flux is assumed to be conserved; i.e., conducting cylindrical walls

  14. Study on helium-charged titanium films deposited by DC-magnetron sputtering

    International Nuclear Information System (INIS)

    Shi Liqun; Jin Qinhua; Liu Chaozhuo; Xu Shilin; Zhou Zhuying

    2005-01-01

    Helium trapping in the Ti films deposited by DC magnetron sputtering with a He/Ar mixture was studied. He atoms with a surprisingly high concentration (He/Ti atomic ratio is as high as 56%) incorporate evenly in deposited film. The trapped amount of He can be controlled by the helium partial amount. The introduction of the helium with no extra damage (or very low damage) can be realized by choosing suitable deposition conditions. It was also found that because of the formation of nanophase Ti film a relative high He flux for bubble formation is needed and the amount of the retaining He in sputtering Ti films is much higher than that in the coarse-grain Ti films. The nanophase Ti film can accommodate larger concentration of trapped sites to He, which results in a high density and small size of the He bubbles. With increasing He irradiation flux, the grain size of Ti film decreases and the lattice spacing and width of the X-ray diffraction peak increase due to the He introduction, and the film tends to amorphous phase. (authors)

  15. Downstream plasma transport and metal ionization in a high-powered pulsed-plasma magnetron

    International Nuclear Information System (INIS)

    Meng, Liang; Szott, Matthew M.; McLain, Jake T.; Ruzic, David N.; Yu, He

    2014-01-01

    Downstream plasma transport and ionization processes in a high-powered pulsed-plasma magnetron were studied. The temporal evolution and spatial distribution of electron density (n e ) and temperature (T e ) were characterized with a 3D scanning triple Langmuir probe. Plasma expanded from the racetrack region into the downstream region, where a high n e peak was formed some time into the pulse-off period. The expansion speed and directionality towards the substrate increased with a stronger magnetic field (B), largely as a consequence of a larger potential drop in the bulk plasma region during a relatively slower sheath formation. The fraction of Cu ions in the deposition flux was measured on the substrate using a gridded energy analyzer. It increased with higher pulse voltage. With increased B field from 200 to 800 Gauss above racetrack, n e increased but the Cu ion fraction decreased from 42% to 16%. A comprehensive model was built, including the diffusion of as-sputtered Cu flux, the Cu ionization in the entire plasma region using the mapped n e and T e data, and ion extraction efficiency based on the measured plasma potential (V p ) distribution. The calculations matched the measurements and indicated the main causes of lower Cu ion fractions in stronger B fields to be the lower T e and inefficient ion extraction in a larger pre-sheath potential.

  16. TiOx deposited by magnetron sputtering: a joint modelling and experimental study

    Science.gov (United States)

    Tonneau, R.; Moskovkin, P.; Pflug, A.; Lucas, S.

    2018-05-01

    This paper presents a 3D multiscale simulation approach to model magnetron reactive sputter deposition of TiOx⩽2 at various O2 inlets and its validation against experimental results. The simulation first involves the transport of sputtered material in a vacuum chamber by means of a three-dimensional direct simulation Monte Carlo (DSMC) technique. Second, the film growth at different positions on a 3D substrate is simulated using a kinetic Monte Carlo (kMC) method. When simulating the transport of species in the chamber, wall chemistry reactions are taken into account in order to get the proper content of the reactive species in the volume. Angular and energy distributions of particles are extracted from DSMC and used for film growth modelling by kMC. Along with the simulation, experimental deposition of TiOx coatings on silicon samples placed at different positions on a curved sample holder was performed. The experimental results are in agreement with the simulated ones. For a given coater, the plasma phase hysteresis behaviour, film composition and film morphology are predicted. The used methodology can be applied to any coater and any films. This paves the way to the elaboration of a virtual coater allowing a user to predict composition and morphology of films deposited in silico.

  17. Surface treatment effect on Si (111) substrate for carbon deposition using DC unbalanced magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Aji, A. S., E-mail: aji.ravazes70@gmail.com; Sahdan, M. F.; Hendra, I. B.; Dinari, P.; Darma, Y. [Quantum Semiconductor and Devices Lab., Physics of Material Electronics Research Division, Department of Physics, Institut Teknologi Bandung (Indonesia)

    2015-04-16

    In this work, we studied the effect of HF treatment in silicon (111) substrate surface for depositing thin layer carbon. We performed the deposition of carbon by using DC Unbalanced Magnetron Sputtering with carbon pallet (5% Fe) as target. From SEM characterization results it can be concluded that the carbon layer on HF treated substrate is more uniform than on substrate without treated. Carbon deposition rate is higher as confirmed by AFM results if the silicon substrate is treated by HF solution. EDAX characterization results tell that silicon (111) substrate with HF treatment have more carbon fraction than substrate without treatment. These results confirmed that HF treatment on silicon Si (111) substrates could enhance the carbon deposition by using DC sputtering. Afterward, the carbon atomic arrangement on silicon (111) surface is studied by performing thermal annealing process to 900 °C. From Raman spectroscopy results, thin film carbon is not changing until 600 °C thermal budged. But, when temperature increase to 900 °C, thin film carbon is starting to diffuse to silicon (111) substrates.

  18. Influence of Continuous and Discontinuous Depositions on Properties of Ito Films Prepared by DC Magnetron Sputtering

    Science.gov (United States)

    Aiempanakit, K.; Rakkwamsuk, P.; Dumrongrattana, S.

    Indium tin oxide (ITO) films were deposited on glass substrate without external heating by DC magnetron sputtering with continuous deposition of 800 s (S1) and discontinuous depositions of 400 s × 2 times (S2), 200 s × 4 times (S3) and 100 s × 8 times (S4). The structural, surface morphology, optical transmittance and electrical resistivity of ITO films were measured by X-ray diffraction, atomic force microscope, spectrophotometer and four-point probe, respectively. The deposition process of the S1 condition shows the highest target voltage due to more target poisoning occurrence. The substrate temperature of the S1 condition increases with the saturation curve of the RC charging circuit while other conditions increase and decrease due to deposition steps as DC power turns on and off. Target voltage and substrate temperature of ITO films decrease when changing the deposition conditions from S1 to S2, S3 and S4, respectively. The preferential orientation of ITO films were changed from dominate (222) plane to (400) plane with the increasing number of deposition steps. The ITO film for the S4 condition shows the lowest electrical resistivity of 1.44 × 10-3 Ω·cm with the highest energy gap of 4.09 eV and the highest surface roughness of 3.43 nm. These results were discussed from the point of different oxygen occurring on the surface ITO target between the sputtering processes which affected the properties of ITO films.

  19. Chromium-doped DLC for implants prepared by laser-magnetron deposition.

    Science.gov (United States)

    Jelinek, Miroslav; Kocourek, Tomáš; Zemek, Josef; Mikšovský, Jan; Kubinová, Šárka; Remsa, Jan; Kopeček, Jaromir; Jurek, Karel

    2015-01-01

    Diamond-like carbon (DLC) thin films are frequently used for coating of implants. The problem of DLC layers lies in bad layer adhesion to metal implants. Chromium is used as a dopant for improvement of adhesion of DLC films. DLC and Cr-DLC layers were deposited on silicon, Ti6Al4V and CoCrMo substrates by a hybrid technology using combination of pulsed laser deposition (PLD) and magnetron sputtering. The topology of layers was studied using SEM, AFM and mechanical profilometer. Carbon and chromium content and concentration of trivalent and toxic hexavalent chromium bonds were determined by XPS and WDS. It follows from the scratch tests that Cr doping improved adhesion of DLC layers. Ethylene glycol, diiodomethane and deionized water were used to measure the contact angles. The surface free energy (SFE) was calculated. The antibacterial properties were studied using Pseudomonas aeruginosa and Staphylococcus aureus bacteria. The influence of SFE, hydrophobicity and surface roughness on antibacterial ability of doped layers is discussed. Copyright © 2014 Elsevier B.V. All rights reserved.

  20. Improving the Tribological Properties of Spark-Anodized Titanium by Magnetron Sputtered Diamond-Like Carbon

    Directory of Open Access Journals (Sweden)

    Zhaoxiang Chen

    2018-02-01

    Full Text Available Spark-anodization of titanium can produce adherent and wear-resistant TiO2 film on the surface, but the spark-anodized titanium has lots of surface micro-pores, resulting in an unstable and high friction coefficient against many counterparts. In this study, the diamond-like carbon (DLC was introduced into the micro-pores of spark-anodized titanium by the magnetron sputtering technique and a TiO2/DLC composite coating was fabricated. The microstructure and tribological properties of TiO2/DLC composite coating were investigated and compared with the anodic TiO2 mono-film and DLC mono-film. Results show that the DLC deposition significantly decreased the surface roughness and porosity of spark-anodized titanium. The fabricated TiO2/DLC composite coating exhibited a more stable and much lower friction coefficient than anodic TiO2 mono-film. Although the friction coefficient of the composite coating and the DLC mono-film was similar under both light load and heavy load conditions, the wear life of the composite coating was about 43% longer than that of DLC mono-film under heavy load condition. The wear rate of titanium with protective composite coating was much lower than that of titanium with DLC mono-film. The superior low friction coefficient and wear rate of the TiO2/DLC composite coating make it a good candidate as protective coating on titanium alloys.