Sample records for molecular epitaxial growth

  1. Surface chemistry and growth mechanisms studies of homo epitaxial (1 0 0) GaAs by laser molecular beam epitaxy

    International Nuclear Information System (INIS)

    Yan Dawei; Wu Weidong; Zhang Hong; Wang Xuemin; Zhang Hongliang; Zhang Weibin; Xiong Zhengwei; Wang Yuying; Shen Changle; Peng Liping; Han Shangjun; Zhou Minjie

    2011-01-01

    In this paper, GaAs thin film has been deposited on thermally desorbed (1 0 0) GaAs substrate using laser molecular beam epitaxy. Scanning electron microscopy, in situ reflection high energy electron diffraction and in situ X-ray photoelectron spectroscopy are applied for evaluation of the surface morphology and chemistry during growth process. The results show that a high density of pits is formed on the surface of GaAs substrate after thermal treatment and the epitaxial thin film heals itself by a step flow growth, resulting in a smoother surface morphology. Moreover, it is found that the incorporation of As species into GaAs epilayer is more efficient in laser molecular beam epitaxy than conventional molecular beam epitaxy. We suggest the growth process is impacted by surface chemistry and morphology of GaAs substrate after thermal treatment and the growth mechanisms are discussed in details.

  2. Molecular Beam Epitaxy Growth of Transition Metal Dichalcogenides

    Science.gov (United States)

    Yue, Ruoyu

    The exponential growth of Si-based technology has finally reached its limit, and a new generation of devices must be developed to continue scaling. A unique class of materials, transition metal dichalcogenides (TMD), have attracted great attention due to their remarkable optical and electronic properties at the atomic thickness scale. Over the past decade, enormous efforts have been put into TMD research for application in low-power devices. Among these studies, a high-quality TMD synthesis method is essential. Molecular beam epitaxy (MBE) can enable high-quality TMD growth by combining high purity elemental sources and an ultra-high vacuum growth environment, together with the back-end-of-line compatible growth temperatures. Although many TMD candidates have been grown by MBE with promising microstructure, the limited grain size (improvement in grain size was achieved through this study. Results from both experiment and simulation showed that reducing the growth rate, enabled by high growth temperature and low metal flux, is vital to nucleation density control. Meanwhile, providing a chalcogen-rich growth environment will promote larger grain lateral growth by suppressing vertical growth. Applying the knowledge learned from the nucleation study, we sucessfully integrated the MBE-grown WSe2 into Si complementary metal-oxide-semiconductor (CMOS) compatible field-effect transistors (FETs). Excellent transport properties, such as field effect hole mobilities (40 cm 2/V·s) with orders of magnitude improvement over the reported values of MBE-grown TMDs, are shown. These studies provide a comprehensive understanding of the MBE synthesis of TMDs and devices, indicating the great potential of integrating TMDs into CMOS process flows for the future electronics.

  3. Molecular-beam epitaxial growth and ion-beam analysis systems for functional materials research

    International Nuclear Information System (INIS)

    Takeshita, H.; Aoki, Y.; Yamamoto, S.; Naramoto, H.

    1992-01-01

    Experimental systems for molecular beam epitaxial growth and ion beam analysis have been designed and constructed for the research of inorganic functional materials such as thin films and superlattices. (author)

  4. Epitaxial growth and new phase of single crystal Dy by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Yang, Kai-Yueh; Homma, Hitoshi; Schuller, I.K.

    1987-09-01

    We have grown two novel epitaxial phases of dysprosium (Dy) on vanadium (V) by molecular beam epitaxy technique. Surface and bulk structures are studied by in-situ reflection high energy electron diffraction (RHEED) and x-ray diffraction techniques. The new hcp phases are ∼4% expanded uniformly in-plane (0001), and ∼9% and ∼4% expanded out of plane along the c-axes for non-interrupted and interrupted deposition case, respectively. We also observed (2 x 2), (3 x 3), and (4 x 4) Dy surface reconstruction patterns and a series of transitions as the Dy film thickness increases. 12 refs., 3 figs

  5. Abstracts of 4. International Workshop on Molecular Beam Epitaxy and Vapour Phase Epitaxy Growth Physics and Technology

    International Nuclear Information System (INIS)

    2001-01-01

    4. International Workshop on Molecular Beam Epitaxy and Vapour Phase Epitaxy Growth Physics and Technology is the periodically held forum for discussion the problems connected with manufacturing of different nanostructures (thin films, quantum wells, quantum dots) needed in microelectronics. Preparation of such materials with desirable optical, electrical and magnetic properties being determined by their chemical composition and crystal structure has been discussed in detail during the workshop sessions. Optimization of crystal growth methods such as VPE and MBE from the view point of obtained material properties has also been extensively discussed

  6. Epitaxial growth of ZnO layers on (111) GaAs substrates by laser molecular beam epitaxy

    International Nuclear Information System (INIS)

    Ding Jian; Zhang Di; Konomi, Takaharu; Saito, Katsuhiko; Guo Qixin

    2012-01-01

    ZnO layers were grown on (111) GaAs substrates by laser molecular epitaxy at substrate temperatures between 200 and 550 °C. X-ray diffraction analysis revealed that c-axis of ZnO epilayer with a wurtzite structure is perpendicular to the substrate surface. X-ray rocking curves and Raman spectroscopy showed that the crystal quality of ZnO epilayers depends on the substrate temperature during the growth. Strong near-band-edge emission in the UV region without any deep-level emissions was observed from the ZnO epilayers at room temperature. The results indicate that laser molecular beam epitaxy is a promising growth method for obtaining high-quality ZnO layers on (111) GaAs substrates.

  7. Molecular beam epitaxy growth of InSb1−xBix thin films

    DEFF Research Database (Denmark)

    Song, Yuxin; Wang, Shumin; Saha Roy, Ivy

    2013-01-01

    Molecular beam epitaxy growth for InSb1−xBix thin films on (100) GaAs substrates is reported. Successful Bi incorporation for 2% is achieved, and up to 70% of the incorporated Bi atoms are at substitutional sites. The effects of growth parameters on Bi incorporation and surface morphology are stu...

  8. Molecular-beam epitaxy growth and characterization of 5-μm quantum cascade laser

    International Nuclear Information System (INIS)

    Mamutin, V V; Ustinov, V M; Ilyinskaya, N D; Baydakova, M V; Ber, B Ya; Kasantsev, D Yu

    2011-01-01

    Molecular-beam epitaxy growth of 5 μm emitting strain-compensated quantum semiconductor laser (QCL) is reported. The QCL structure is characterized by complementary techniques: high-resolution X-ray diffraction and dynamical secondary-ion mass-spectrometry, that reveal the high quality of QCL structure and in-depth distribution of chemical composition, respectively.

  9. Growth of Gold-assisted Gallium Arsenide Nanowires on Silicon Substrates via Molecular Beam Epitaxy

    Directory of Open Access Journals (Sweden)

    Ramon M. delos Santos

    2008-06-01

    Full Text Available Gallium arsenide nanowires were grown on silicon (100 substrates by what is called the vapor-liquid-solid (VLS growth mechanism using a molecular beam epitaxy (MBE system. Good quality nanowires with surface density of approximately 108 nanowires per square centimeter were produced by utilizing gold nanoparticles, with density of 1011 nanoparticles per square centimeter, as catalysts for nanowire growth. X-ray diffraction measurements, scanning electron microscopy, transmission electron microscopy and Raman spectroscopy revealed that the nanowires are epitaxially grown on the silicon substrates, are oriented along the [111] direction and have cubic zincblende structure.

  10. Effect of growth temperature on defects in epitaxial GaN film grown by plasma assisted molecular beam epitaxy

    Directory of Open Access Journals (Sweden)

    S. S. Kushvaha

    2014-02-01

    Full Text Available We report the effect of growth temperature on defect states of GaN epitaxial layers grown on 3.5 μm thick GaN epi-layer on sapphire (0001 substrates using plasma assisted molecular beam epitaxy. The GaN samples grown at three different substrate temperatures at 730, 740 and 750 °C were characterized using atomic force microscopy and photoluminescence spectroscopy. The atomic force microscopy images of these samples show the presence of small surface and large hexagonal pits on the GaN film surfaces. The surface defect density of high temperature grown sample is smaller (4.0 × 108 cm−2 at 750 °C than that of the low temperature grown sample (1.1 × 109 cm−2 at 730 °C. A correlation between growth temperature and concentration of deep centre defect states from photoluminescence spectra is also presented. The GaN film grown at 750 °C exhibits the lowest defect concentration which confirms that the growth temperature strongly influences the surface morphology and affects the optical properties of the GaN epitaxial films.

  11. Adsorption-controlled growth of BiMnO3 films by molecular-beam epitaxy

    International Nuclear Information System (INIS)

    Lee, J. H.; Ke, X.; Misra, R.; Schiffer, P.; Ihlefeld, J. F.; Mei, Z. G.; Liu, Z. K.; Xu, X. S.; Musfeldt, J. L.; Heeg, T.; Schlom, D. G.; Roeckerath, M.; Schubert, J.

    2010-01-01

    We have developed the means to grow BiMnO 3 thin films with unparalleled structural perfection by reactive molecular-beam epitaxy and determined its band gap. Film growth occurs in an adsorption-controlled growth regime. Within this growth window bounded by oxygen pressure and substrate temperature at a fixed bismuth overpressure, single-phase films of the metastable perovskite BiMnO 3 may be grown by epitaxial stabilization. X-ray diffraction reveals phase-pure and epitaxial films with ω rocking curve full width at half maximum values as narrow as 11 arc sec (0.003 deg. ). Optical absorption measurements reveal that BiMnO 3 has a direct band gap of 1.1±0.1 eV.

  12. Molecular Beam Epitaxial Growth of GaAs on (631) Oriented Substrates

    International Nuclear Information System (INIS)

    Cruz Hernandez, Esteban; Rojas Ramirez, Juan-Salvador; Contreras Hernandez, Rocio; Lopez Lopez, Maximo; Pulzara Mora, Alvaro; Mendez Garcia, Victor H.

    2007-01-01

    In this work, we report the study of the homoepitaxial growth of GaAs on (631) oriented substrates by molecular beam epitaxy (MBE). We observed the spontaneous formation of a high density of large scale features on the surface. The hilly like features are elongated towards the [-5, 9, 3] direction. We show the dependence of these structures with the growth conditions and we present the possibility of to create quantum wires structures on this surface

  13. Real-time reflectance-difference spectroscopy of GaAs molecular beam epitaxy homoepitaxial growth

    Energy Technology Data Exchange (ETDEWEB)

    Lastras-Martínez, A., E-mail: alm@cactus.iico.uaslp.mx, E-mail: alastras@gmail.com; Ortega-Gallegos, J.; Guevara-Macías, L. E.; Nuñez-Olvera, O.; Balderas-Navarro, R. E.; Lastras-Martínez, L. F. [Instituto de Investigación en Comunicación Optica, Universidad Autónoma de San Luis Potosí, Alvaro Obregón 64, San Luis Potosí, SLP 78000 (Mexico); Lastras-Montaño, L. A. [IBM T. J. Watson Research Center, Yorktown Heights, New York 10598 (United States); Lastras-Montaño, M. A. [Department of Electrical and Computer Engineering, University of California, Santa Barbara, Santa Barbara, California 93106 (United States)

    2014-03-01

    We report on real time-resolved Reflectance-difference (RD) spectroscopy of GaAs(001) grown by molecular beam epitaxy, with a time-resolution of 500 ms per spectrum within the 2.3–4.0 eV photon energy range. Through the analysis of transient RD spectra we demonstrated that RD line shapes are comprised of two components with different physical origins and determined their evolution during growth. Such components were ascribed to the subsurface strain induced by surface reconstruction and to surface stoichiometry. Results reported in this paper render RD spectroscopy as a powerful tool for the study of fundamental processes during the epitaxial growth of zincblende semiconductors.

  14. Real-time reflectance-difference spectroscopy of GaAs molecular beam epitaxy homoepitaxial growth

    Directory of Open Access Journals (Sweden)

    A. Lastras-Martínez

    2014-03-01

    Full Text Available We report on real time-resolved Reflectance-difference (RD spectroscopy of GaAs(001 grown by molecular beam epitaxy, with a time-resolution of 500 ms per spectrum within the 2.3–4.0 eV photon energy range. Through the analysis of transient RD spectra we demonstrated that RD line shapes are comprised of two components with different physical origins and determined their evolution during growth. Such components were ascribed to the subsurface strain induced by surface reconstruction and to surface stoichiometry. Results reported in this paper render RD spectroscopy as a powerful tool for the study of fundamental processes during the epitaxial growth of zincblende semiconductors.

  15. Electron molecular beam epitaxy: Layer-by-layer growth of complex oxides via pulsed electron-beam deposition

    International Nuclear Information System (INIS)

    Comes, Ryan; Liu Hongxue; Lu Jiwei; Gu, Man; Khokhlov, Mikhail; Wolf, Stuart A.

    2013-01-01

    Complex oxide epitaxial film growth is a rich and exciting field, owing to the wide variety of physical properties present in oxides. These properties include ferroelectricity, ferromagnetism, spin-polarization, and a variety of other correlated phenomena. Traditionally, high quality epitaxial oxide films have been grown via oxide molecular beam epitaxy or pulsed laser deposition. Here, we present the growth of high quality epitaxial films using an alternative approach, the pulsed electron-beam deposition technique. We demonstrate all three epitaxial growth modes in different oxide systems: Frank-van der Merwe (layer-by-layer); Stranski-Krastanov (layer-then-island); and Volmer-Weber (island). Analysis of film quality and morphology is presented and techniques to optimize the morphology of films are discussed.

  16. Self-regulated growth of LaVO3 thin films by hybrid molecular beam epitaxy

    International Nuclear Information System (INIS)

    Zhang, Hai-Tian; Engel-Herbert, Roman; Dedon, Liv R.; Martin, Lane W.

    2015-01-01

    LaVO 3 thin films were grown on SrTiO 3 (001) by hybrid molecular beam epitaxy. A volatile metalorganic precursor, vanadium oxytriisopropoxide (VTIP), and elemental La were co-supplied in the presence of a molecular oxygen flux. By keeping the La flux fixed and varying the VTIP flux, stoichiometric LaVO 3 films were obtained for a range of cation flux ratios, indicating the presence of a self-regulated growth window. Films grown under stoichiometric conditions were found to have the largest lattice parameter, which decreased monotonically with increasing amounts of excess La or V. Energy dispersive X-ray spectroscopy and Rutherford backscattering measurements were carried out to confirm film compositions. Stoichiometric growth of complex vanadate thin films independent of cation flux ratios expands upon the previously reported self-regulated growth of perovskite titanates using hybrid molecular beam epitaxy, thus demonstrating the general applicability of this growth approach to other complex oxide materials, where a precise control over film stoichiometry is demanded by the application

  17. Growth of CrTe thin films by molecular-beam epitaxy

    International Nuclear Information System (INIS)

    Sreenivasan, M.G.; Hou, X.J.; Teo, K.L.; Jalil, M.B.A.; Liew, T.; Chong, T.C.

    2006-01-01

    We report the growth of Cr 1-δ Te films on (100) GaAs substrates using ZnTe buffer layers by solid-source molecular-beam epitaxial technique. RHEED patterns indicate a clear structural change during the initial stages of deposition. Temperature-dependent magnetization results reveal that different NiAs-related phases of Cr 1-δ Te can be obtained at different substrate temperatures. By varying the film thickness, a metastable zinc blende structure of CrTe could be obtained at lower substrate temperature

  18. Mathematical model for predicting molecular-beam epitaxy growth rates for wafer production

    International Nuclear Information System (INIS)

    Shi, B.Q.

    2003-01-01

    An analytical mathematical model for predicting molecular-beam epitaxy (MBE) growth rates is reported. The mathematical model solves the mass-conservation equation for liquid sources in conical crucibles and predicts the growth rate by taking into account the effect of growth source depletion on the growth rate. Assumptions made for deducing the analytical model are discussed. The model derived contains only one unknown parameter, the value of which can be determined by using data readily available to MBE growers. Procedures are outlined for implementing the model in MBE production of III-V compound semiconductor device wafers. Results from use of the model to obtain targeted layer compositions and thickness of InP-based heterojunction bipolar transistor wafers are presented

  19. Molecular-beam epitaxial growth and characterization of quaternary III-nitride compounds

    International Nuclear Information System (INIS)

    Monroy, E.; Gogneau, N.; Enjalbert, F.; Fossard, F.; Jalabert, D.; Bellet-Amalric, E.; Dang, Le Si; Daudin, B.

    2003-01-01

    We report on the controlled growth and characterization of quaternary AlGaInN compounds by plasma-assisted molecular beam epitaxy. Two-dimensional growth is achieved with a monolayer of In segregating at the growth front. In incorporation is hindered by increasing growth temperature and Al mole fraction, which is explained by the lower binding energy of InN compared to GaN and AlN. The mosaicity of the layers is determined by the substrate quality, whereas the alloy disorder increases with the Al content, independent of the In mole fraction. Room temperature photoluminescence is dominated by a narrow band-edge emission, whose Stokes shift and activation energy increase with the In content. This behavior is interpreted in terms of carrier localization in self-formed alloy inhomogeneities. An In-related band bowing parameter of 2.5 eV has been estimated

  20. Investigation of the silicon ion density during molecular beam epitaxy growth

    CERN Document Server

    Eifler, G; Ashurov, K; Morozov, S

    2002-01-01

    Ions impinging on a surface during molecular beam epitaxy influence the growth and the properties of the growing layer, for example, suppression of dopant segregation and the generation of crystal defects. The silicon electron gun in the molecular beam epitaxy (MBE) equipment is used as a source for silicon ions. To use the effect of ion bombardment the mechanism of generation and distribution of ions was investigated. A monitoring system was developed and attached at the substrate position in the MBE growth chamber to measure the ion and electron densities towards the substrate. A negative voltage was applied to the substrate to modify the ion energy and density. Furthermore the current caused by charge carriers impinging on the substrate was measured and compared with the results of the monitoring system. The electron and ion densities were measured by varying the emission current of the e-gun achieving silicon growth rates between 0.07 and 0.45 nm/s and by changing the voltage applied to the substrate betw...

  1. Growth of GaSb1-xBix by molecular beam epitaxy

    DEFF Research Database (Denmark)

    Song, Yuxin; Wang, Shumin; Roy, Ivy Saha

    2012-01-01

    Molecular beam epitaxy for GaSb1-xBix is investigated in this article. The growth window for incorporation of Bi in GaSb was found. Strategies of avoiding formation of Bi droplets and enhancing Bi incorporation were studied. The Bi incorporation was confirmed by SIMS and RBS measurements. The Bi ......As substrates were compared and no apparent difference for Bi incorporation was found.......Molecular beam epitaxy for GaSb1-xBix is investigated in this article. The growth window for incorporation of Bi in GaSb was found. Strategies of avoiding formation of Bi droplets and enhancing Bi incorporation were studied. The Bi incorporation was confirmed by SIMS and RBS measurements. The Bi...... concentration in the samples was found to increase with increasing growth temperature and Bi flux. The position of GaSb1-xBix layer peak in XRD rocking curves is found to be correlated to Bi composition. Surface and structural properties of the samples were also investigated. Samples grown on GaSb and Ga...

  2. Epitaxial growth and characterization of CuGa2O4 films by laser molecular beam epitaxy

    OpenAIRE

    Hongling Wei; Zhengwei Chen; Zhenping Wu; Wei Cui; Yuanqi Huang; Weihua Tang

    2017-01-01

    Ga2O3 with a wide bandgap of ∼ 4.9 eV can crystalize in five crystalline phases. Among those phases, the most stable monoclinic β-Ga2O3 has been studied most, however, it is hard to find materials lattice matching with β-Ga2O3 to grown epitaxial thin films for optoelectronic applications. In this work, CuGa2O4 bulk were prepared by solid state reaction as target, and the films were deposited on sapphire substrates by laser molecular beam epitaxy (L-MBE) at different substrate temperatures. Th...

  3. Epitaxial growth of SrTiO3 thin film on Si by laser molecular beam epitaxy

    International Nuclear Information System (INIS)

    Zhou, X. Y.; Miao, J.; Dai, J. Y.; Chan, H. L. W.; Choy, C. L.; Wang, Y.; Li, Q.

    2007-01-01

    SrTiO 3 thin films have been deposited on Si (001) wafers by laser molecular beam epitaxy using an ultrathin Sr layer as the template. X-ray diffraction measurements indicated that SrTiO 3 was well crystallized and epitaxially aligned with Si. Cross-sectional observations in a transmission electron microscope revealed that the SrTiO 3 /Si interface was sharp, smooth, and fully crystallized. The thickness of the Sr template was found to be a critical factor that influenced the quality of SrTiO 3 and the interfacial structure. Electrical measurements revealed that the SrTiO 3 film was highly resistive

  4. Molecular-beam epitaxy growth of high-performance midinfrared diode lasers

    International Nuclear Information System (INIS)

    Turner, G.W.; Choi, H.K.; Calawa, D.R.

    1994-01-01

    Recent advances in the performance of GaInAsSb/AlGaAsSb quantum-well diode lasers have been directly related to improvements in the quality of the molecular-beam epitaxy (MBE)-grown epitaxial layers. These improvements have been based on careful measurement and control of lattice matching and intentional strain, changes in shutter sequencing at interfaces, and a generally better understanding of the growth of Sb-based epitaxial materials. By using this improved MBE-grown material, significantly enhanced performance has been obtained for midinfrared lasers. These lasers, which are capable of ∼2-μm emission at room temperature, presently exhibit threshold current densities of 143 A/cm 2 , continuous wave powers of 1.3 W, and diffraction-limited powers of 120 mW. Such high-performance midinfrared diode lasers are of interest for a wide variety of applications, including eye-safe laser radar, remote sensing of atmospheric contaminants and wind turbulence, laser surgery, and pumping of solid-state laser media. 12 refs., 3 figs

  5. Hybrid molecular beam epitaxy for the growth of stoichiometric BaSnO{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Prakash, Abhinav, E-mail: praka019@umn.edu; Dewey, John; Yun, Hwanhui; Jeong, Jong Seok; Mkhoyan, K. Andre; Jalan, Bharat, E-mail: bjalan@umn.edu [Department of Chemical Engineering and Materials Science, University of Minnesota, Minneapolis, Minnesota 55455 (United States)

    2015-11-15

    Owing to its high room-temperature electron mobility and wide bandgap, BaSnO{sub 3} has recently become of significant interest for potential room-temperature oxide electronics. A hybrid molecular beam epitaxy (MBE) approach for the growth of high-quality BaSnO{sub 3} films is developed in this work. This approach employs hexamethylditin as a chemical precursor for tin, an effusion cell for barium, and a radio frequency plasma source for oxygen. BaSnO{sub 3} films were thus grown on SrTiO{sub 3} (001) and LaAlO{sub 3} (001) substrates. Growth conditions for stoichiometric BaSnO{sub 3} were identified. Reflection high-energy electron diffraction (RHEED) intensity oscillations, characteristic of a layer-by-layer growth mode were observed. A critical thickness of ∼1 nm for strain relaxation was determined for films grown on SrTiO{sub 3} using in situ RHEED. Scanning transmission electron microscopy combined with electron energy-loss spectroscopy and energy dispersive x-ray spectroscopy confirmed the cube-on-cube epitaxy and composition. The importance of precursor chemistry is discussed in the context of the MBE growth of BaSnO{sub 3}.

  6. InAs/GaAs(001) molecular beam epitaxial growth in a scanning tunnelling microscope

    International Nuclear Information System (INIS)

    Bastiman, F; Cullis, A G; Hopkinson, M

    2010-01-01

    The growth on InAs on GaAs(001) has attracted great interest and investigation over the past few decades primarily due to the opto-electronic properties of the self-assembled quantum dot (QD) arrays formed. Scanning tunnelling microscopy (STM) has been extensively employed to investigate the complicated and spontaneous mechanism of QD growth via molecular beam epitaxy (MBE). Classically, combined MBE-STM requires quenching the sample after growth and transferring it to an arsenic-free high vacuum chamber which houses the STM system. However, without access to the phenomenon as a dynamic process a basic understanding remains elusive. In order to access surface dynamics, MBE and STM must be combined into a single element. The system herein discussed allows the operation of MBE sources in an STM system relating to InAs/GaAs(001) surfaces.

  7. Study of molecular-beam epitaxy growth on patterned GaAs (311)A substrates with different mesa height

    NARCIS (Netherlands)

    Gong, Q.; Nötzel, R.; Schönherr, H.-P.; Ploog, K.

    2000-01-01

    We report on the evolution of the growth front during molecular-beam epitaxy on GaAs (3 1 1)A substrates stripe patterned along the [ ] direction as a function of the mesa height. During growth (1 0 0) and (2 1 1)A facets are formed and expand at the corners near the two opposite lying ( )A and (1 1

  8. Molecular beam epitaxy growth of InSb1-xBix thin films

    DEFF Research Database (Denmark)

    Yuxin Song; Shumin Wang; Saha Roy, Ivy

    2013-01-01

    Molecular beam epitaxy growth for InSb1-xBix thin films on (100) GaAs substrates is reported. Successful Bi incorporation for 2% is achieved, and up to 70% of the incorporated Bi atoms are at substitutional sites. The effects of growth parameters on Bi incorporation and surface morphology are stu...

  9. Growth, structural, and electrical properties of germanium-on-silicon heterostructure by molecular beam epitaxy

    Directory of Open Access Journals (Sweden)

    Aheli Ghosh

    2017-09-01

    Full Text Available The growth, morphological, and electrical properties of thin-film Ge grown by molecular beam epitaxy on Si using a two-step growth process were investigated. High-resolution x-ray diffraction analysis demonstrated ∼0.10% tensile-strained Ge epilayer, owing to the thermal expansion coefficient mismatch between Ge and Si, and negligible epilayer lattice tilt. Micro-Raman spectroscopic analysis corroborated the strain-state of the Ge thin-film. Cross-sectional transmission electron microscopy revealed the formation of 90  ° Lomer dislocation network at Ge/Si heterointerface, suggesting the rapid and complete relaxation of Ge epilayer during growth. Atomic force micrographs exhibited smooth surface morphology with surface roughness < 2 nm. Temperature dependent Hall mobility measurements and the modelling thereof indicated that ionized impurity scattering limited carrier mobility in Ge layer. Capacitance- and conductance-voltage measurements were performed to determine the effect of epilayer dislocation density on interfacial defect states (Dit and their energy distribution. Finally, extracted Dit values were benchmarked against published Dit data for Ge MOS devices, as a function of threading dislocation density within the Ge layer. The results obtained were comparable with Ge MOS devices integrated on Si via alternative buffer schemes. This comprehensive study of directly-grown epitaxial Ge-on-Si provides a pathway for the development of Ge-based electronic devices on Si.

  10. Growth, structural, and electrical properties of germanium-on-silicon heterostructure by molecular beam epitaxy

    Science.gov (United States)

    Ghosh, Aheli; Clavel, Michael B.; Nguyen, Peter D.; Meeker, Michael A.; Khodaparast, Giti A.; Bodnar, Robert J.; Hudait, Mantu K.

    2017-09-01

    The growth, morphological, and electrical properties of thin-film Ge grown by molecular beam epitaxy on Si using a two-step growth process were investigated. High-resolution x-ray diffraction analysis demonstrated ˜0.10% tensile-strained Ge epilayer, owing to the thermal expansion coefficient mismatch between Ge and Si, and negligible epilayer lattice tilt. Micro-Raman spectroscopic analysis corroborated the strain-state of the Ge thin-film. Cross-sectional transmission electron microscopy revealed the formation of 90° Lomer dislocation network at Ge/Si heterointerface, suggesting the rapid and complete relaxation of Ge epilayer during growth. Atomic force micrographs exhibited smooth surface morphology with surface roughness published Dit data for Ge MOS devices, as a function of threading dislocation density within the Ge layer. The results obtained were comparable with Ge MOS devices integrated on Si via alternative buffer schemes. This comprehensive study of directly-grown epitaxial Ge-on-Si provides a pathway for the development of Ge-based electronic devices on Si.

  11. Growth of conductive HfO{sub 2-x} thin films by reactive molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Hildebrandt, Erwin; Kurian, Jose; Alff, Lambert [Institut fuer Materialwissenschaft, TU Darmstadt (Germany); Kleebe, Hans-Joachim [Institut fuer Angewandte Geowissenschaften, TU Darmstadt (Germany)

    2009-07-01

    Thin films of oxygen deficient hafnium oxide were grown on single crystal c-cut and r-cut sapphire substrates by reactive molecular beam epitaxy. The oxidation conditions during growth were varied within a wide range using RF-activated oxygen. Hafnium oxide thin films were characterized using X-ray diffraction, resistivity measurements ({rho}-T) and transmission electron microscopy (TEM). The results show a dramatic increase in conductivity of the deposited oxygen deficient hafnium oxide thin films with decreasing oxidation conditions during growth. The electrical properties of deficient hafnium oxide thin films varied from insulating over semiconducting to conducting. X-ray diffraction data as well as TEM data rule out the possibility of conductivity due to metallic hafnium.

  12. Investigation into the use of molecular hydrogen on the growth of gallium nitride via metal-organic molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Billingsley, Daniel; Pritchett, David; Henderson, Walter; Carver, Alexander G.; Burnham, Shawn D.; Doolittle, W.A. [Georgia Institute of Technology, School of Electrical and Computer Engineering, 777 Atlantic Dr., Atlanta, GA 30332 (United States)

    2008-07-01

    Molecular hydrogen (H{sub 2}) has been investigated as a means to improve ammonia nitridation efficiency and attempts to reduce carbon contamination in ammonia-based metal-organic molecular beam epitaxy (MOMBE). A 30% improvement in crystalline quality, inferred from XRD, as well as an increase in subsequent GaN bulk growth rate was observed when bare sapphire was subject to H{sub 2} annealing before nitridation. However, the use of H{sub 2} during GaN homoepitaxy on GaN templates resulted in increased carbon contamination and decreased growth rate of GaN. The results demonstrate promise and proper uses of H{sub 2} during GaN growth under certain conditions. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  13. Investigation of the silicon ion density during molecular beam epitaxy growth

    Science.gov (United States)

    Eifler, G.; Kasper, E.; Ashurov, Kh.; Morozov, S.

    2002-05-01

    Ions impinging on a surface during molecular beam epitaxy influence the growth and the properties of the growing layer, for example, suppression of dopant segregation and the generation of crystal defects. The silicon electron gun in the molecular beam epitaxy (MBE) equipment is used as a source for silicon ions. To use the effect of ion bombardment the mechanism of generation and distribution of ions was investigated. A monitoring system was developed and attached at the substrate position in the MBE growth chamber to measure the ion and electron densities towards the substrate. A negative voltage was applied to the substrate to modify the ion energy and density. Furthermore the current caused by charge carriers impinging on the substrate was measured and compared with the results of the monitoring system. The electron and ion densities were measured by varying the emission current of the e-gun achieving silicon growth rates between 0.07 and 0.45 nm/s and by changing the voltage applied to the substrate between 0 to -1000 V. The dependencies of ion and electron densities were shown and discussed within the framework of a simple model. The charged carrier densities measured with the monitoring system enable to separate the ion part of the substrate current and show its correlation to the generation rate. Comparing the ion density on the whole substrate and in the center gives a hint to the ion beam focusing effect. The maximum ion and electron current densities obtained were 0.40 and 0.61 μA/cm2, respectively.

  14. Dynamic grazing incidence fast atom diffraction during molecular beam epitaxial growth of GaAs

    Energy Technology Data Exchange (ETDEWEB)

    Atkinson, P., E-mail: atkinson@insp.jussieu.fr; Eddrief, M. [Sorbonne Universités, UPMC Univ. Paris 06, UMR 7588, INSP, F-75005 Paris (France); CNRS, UMR 7588, Institut des NanoSciences de Paris, 4 place Jussieu, F-75005 Paris (France); Etgens, V. H. [CNRS, UMR 7588, Institut des NanoSciences de Paris, 4 place Jussieu, F-75005 Paris (France); VeDeCom-Université Versailles Saint-Quentin en Yvelines, Versailles (France); Khemliche, H., E-mail: hocine.khemliche@u-psud.fr; Debiossac, M.; Mulier, M.; Lalmi, B.; Roncin, P. [ISMO UMR8214 CNRS-Université Paris-Sud, Orsay F-91400 (France); Momeni, A. [ISMO UMR8214 CNRS-Université Paris-Sud, Orsay F-91400 (France); Univ. Cergy Pontoise, F-95031 Cergy (France)

    2014-07-14

    A Grazing Incidence Fast Atom Diffraction (GIFAD) system has been mounted on a commercial molecular beam epitaxy chamber and used to monitor GaAs growth in real-time. In contrast to the conventionally used Reflection High Energy Electron Diffraction, all the GIFAD diffraction orders oscillate in phase, with the change in intensity related to diffuse scattering at step edges. We show that the scattered intensity integrated over the Laue circle is a robust method to monitor the periodic change in surface roughness during layer-by-layer growth, with oscillation phase and amplitude independent of incidence angle and crystal orientation. When there is a change in surface reconstruction at the start of growth, GIFAD intensity oscillations show that there is a corresponding delay in the onset of layer-by-layer growth. In addition, changes in the relative intensity of different diffraction orders have been observed during growth showing that GIFAD has the potential to provide insight into the preferential adatom attachment sites on the surface reconstruction during growth.

  15. Effects of film polarities on InN growth by molecular-beam epitaxy

    International Nuclear Information System (INIS)

    Xu, K.; Yoshikawa, A.

    2003-01-01

    Effects of the film polarity on InN growth were investigated in molecular-beam epitaxy (MBE). It was found that N-polarity InN could be grown at higher temperatures than In-polarity one. For the In-polarity films, which were grown on Ga-polar GaN template, the highest growth temperature was limited below 500 deg. C, and the surface morphology and crystal quality tended to be poor mainly because of the tolerated low growth temperature. While for the N-polarity InN films, which were grown on MBE-grown N-polar GaN, the growth temperature could be as high as 600 deg. C. The step-flow-like growth morphology was achieved for the InN films grown with N polarity at 580 deg. C. The resulting full widths of half maximum of x-ray rocking curve around InN (002) and (102) reflections were about 200-250 and 950-1100 arc sec, respectively. The photoluminescence of the InN films peaked at 0.697 eV. The recording Hall mobility of InN film grown in N polarity is 1400 cm 2 /V s with a background carrier concentration of 1.56x10 18 cm -3 at room temperature. For both-polarity films, we found N-rich condition was necessary for the stable InN growth

  16. Molecular Beam Epitaxy Growth of High Crystalline Quality LiNbO3

    Science.gov (United States)

    Tellekamp, M. Brooks; Shank, Joshua C.; Goorsky, Mark S.; Doolittle, W. Alan

    2016-12-01

    Lithium niobate is a multi-functional material with wide reaching applications in acoustics, optics, and electronics. Commercial applications for lithium niobate require high crystalline quality currently limited to bulk and ion sliced material. Thin film lithium niobate is an attractive option for a variety of integrated devices, but the research effort has been stagnant due to poor material quality. Both lattice matched and mismatched lithium niobate are grown by molecular beam epitaxy and studied to understand the role of substrate and temperature on nucleation conditions and material quality. Growth on sapphire produces partially coalesced columnar grains with atomically flat plateaus and no twin planes. A symmetric rocking curve shows a narrow linewidth with a full width at half-maximum (FWHM) of 8.6 arcsec (0.0024°), which is comparable to the 5.8 arcsec rocking curve FWHM of the substrate, while the film asymmetric rocking curve is 510 arcsec FWHM. These values indicate that the individual grains are relatively free of long-range disorder detectable by x-ray diffraction with minimal measurable tilt and twist and represents the highest structural quality epitaxial material grown on lattice mismatched sapphire without twin planes. Lithium niobate is also grown on lithium tantalate producing high quality coalesced material without twin planes and with a symmetric rocking curve of 193 arcsec, which is nearly equal to the substrate rocking curve of 194 arcsec. The surface morphology of lithium niobate on lithium tantalate is shown to be atomically flat by atomic force microscopy.

  17. Growth of semiconductor alloy InGaPBi on InP by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Wang, K; Wang, P; Pan, W W; Wu, X Y; Yue, L; Gong, Q; Wang, S M

    2015-01-01

    We report the first successful growth of InGaPBi single crystals on InP substrate with Bi concentration far beyond the doping level by gas source molecular beam epitaxy. The InGaPBi thin films reveal excellent surface and structural qualities, making it a promising new III–V compound family member for heterostructures. The strain can be tuned between tensile and compressive by adjusting Ga and Bi compositions. The maximum achieved Bi concentration is 2.2 ± 0.4% confirmed by Rutherford backscattering spectroscopy. Room temperature photoluminescence shows strong and broad light emission at energy levels much smaller than the InP bandgap. (paper)

  18. Diffusion-driven growth of nanowires by low-temperature molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Rueda-Fonseca, P.; Orrù, M. [Univ. Grenoble Alpes, F-38000 Grenoble (France); CNRS, Institut NEEL, F-38000 Grenoble (France); CEA, INAC, F-38000 Grenoble (France); Bellet-Amalric, E.; Robin, E. [Univ. Grenoble Alpes, F-38000 Grenoble (France); CEA, INAC, F-38000 Grenoble (France); Den Hertog, M.; Genuist, Y.; André, R.; Tatarenko, S.; Cibert, J., E-mail: joel.cibert@neel.cnrs.fr [Univ. Grenoble Alpes, F-38000 Grenoble (France); CNRS, Institut NEEL, F-38000 Grenoble (France)

    2016-04-28

    With ZnTe as an example, we use two different methods to unravel the characteristics of the growth of nanowires (NWs) by gold-catalyzed molecular beam epitaxy at low temperature. In the first approach, CdTe insertions have been used as markers, and the nanowires have been characterized by scanning transmission electron microscopy, including geometrical phase analysis and energy dispersive electron spectrometry; the second approach uses scanning electron microscopy and the statistics of the relationship between the length of the tapered nanowires and their base diameter. Axial and radial growth are quantified using a diffusion-limited model adapted to the growth conditions; analytical expressions describe well the relationship between the NW length and the total molecular flux (taking into account the orientation of the effusion cells), and the catalyst-nanowire contact area. A long incubation time is observed. This analysis allows us to assess the evolution of the diffusion lengths on the substrate and along the nanowire sidewalls, as a function of temperature and deviation from stoichiometric flux.

  19. Molecular beam epitaxial growth of graphene and ridge-structure networks of graphene

    International Nuclear Information System (INIS)

    Maeda, Fumihiko; Hibino, Hiroki

    2011-01-01

    By gas-source molecular beam epitaxy (MBE) using cracked ethanol, we grew graphene at substrate temperatures between 600 and 915 °C on graphene formed on SiC(0 0 0 1) by thermal decomposition. To investigate the substrate temperature dependence of graphene growth we analysed the MBE-grown graphene by Raman spectroscopy and in situ x-ray photoelectron spectroscopy (XPS) and observed it by atomic force microscopy (AFM) and cross-sectional transmission electron microscopy (TEM). Analyses using the G-band peak and the peak intensity ratio between D- and G-band peaks in the Raman spectra revealed that growth at higher temperatures improved the crystallinity and increased the domain size. Although the growth rate decreased at higher temperatures, as revealed by XPS, these results indicated that growth at a higher temperature is effective in obtaining graphene of higher quality. Furthermore, the AFM and TEM observations revealed a network of fin-like ridge structures of graphene sticking out from the surface. The presence of these 'graphene nanofins' indicated that two-dimensional islands of graphene are surrounded by the nanofins, and the island size was estimated to be 67 nm using the average distance between the nanofins.

  20. Epitaxial growth and characterization of CuGa2O4 films by laser molecular beam epitaxy

    Directory of Open Access Journals (Sweden)

    Hongling Wei

    2017-11-01

    Full Text Available Ga2O3 with a wide bandgap of ∼ 4.9 eV can crystalize in five crystalline phases. Among those phases, the most stable monoclinic β-Ga2O3 has been studied most, however, it is hard to find materials lattice matching with β-Ga2O3 to grown epitaxial thin films for optoelectronic applications. In this work, CuGa2O4 bulk were prepared by solid state reaction as target, and the films were deposited on sapphire substrates by laser molecular beam epitaxy (L-MBE at different substrate temperatures. The influences of substrate temperature on structural and optical properties have been systematically investigated by means of X-ray diffraction, Transmission electron microscope and UV-vis absorption spectra. High quality cubic structure and [111] oriented CuGa2O4 film can be obtained at substrate temperature of 750 °C. It’s also demonstrated that the CuGa2O4 film has a bandgap of ∼ 4.4 eV and a best crystal quality at 750 °C, suggesting that CuGa2O4 film is a promising candidate for applications in ultraviolet optoelectronic devices.

  1. Ga-assisted catalyst-free growth mechanism of GaAs nanowires by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Colombo, C.; Spirkoska, D.; Frimmer, M.; Abstreiter, G.; Fontcuberta i Morral, A.

    2008-01-01

    The mechanisms of Ga-assisted GaAs nanowires grown by molecular beam epitaxy are addressed. The axial and radial growth rates as a function of the Ga rate and As pressure indicate that on the opposite of what is observed in thin film epitaxy, the growth rate of the nanowires is arsenic limited. As a consequence, the axial growth rate of the wires can be controlled by the As 4 pressure. Additionally, due to the small As 4 pressure leading to nanowire growth, the deposition on the facets is very slow, leading to a much lower radial growth rate. Finally, we present a model that is able to accurately describe the presented observations and predicts a maximum length of nontapered nanowires of 40 μm

  2. Growth of HfO{sub x} thin films by reactive molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Hildebrandt, Erwin; Kurian, Jose; Alff, Lambert [Institut fuer Materialwissenschaft, TU Darmstadt (Germany)

    2008-07-01

    Thin films of hafnium oxide were grown on single crystal r-cut and c-cut sapphire by reactive molecular beam epitaxy. The conditions for the growth of single oriented hafnium oxide thin films have been established. Hafnium oxide thin films were characterized by X-ray diffraction and optical absorption measurements. It was found that hafnium oxide thin films grown on r-cut sapphire were (00l) oriented whereas, on c-cut sapphire, hafnium oxide films showed different orientations depending on the growth temperature and oxidation conditions. The hafnium oxide films grown at higher temperature and under strong oxidation conditions yielded (001) oriented films on c-cut sapphire whereas slightly weaker oxidation condition leads to (111) oriented hafnium oxide films. The bandgap deducted from optical absorption measurement carried out on hafnium oxide films grown under optimized conditions agreed well with the values reported in literature. A range of oxygen deficient thin films of hafnium oxide were also grown on single crystal sapphire substrates in order to investigate the effect of oxygen vacancies on dielectric properties of hafnium oxide. The oxygen deficient thin films of hafnium oxide show a decrease in bandgap with increase in oxygen deficiency.

  3. Growth kinetics and properties of ZnO/ZnMgO heterostructures grown by radical-source molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Ivanov, S.V. [Institute of Semiconductor Technology, Technical University Braunschweig, Hans-Sommer-Str. 66, 38106 Braunschweig (Germany); Ioffe Physico-Technical Institute, Polytekhnicheskaya Street 26, 194021 St. Petersburg (Russian Federation); El-Shaer, A.; Bakin, A.; Waag, A. [Institute of Semiconductor Technology, Technical University Braunschweig, Hans-Sommer-Str. 66, 38106 Braunschweig (Germany); Shubina, T.V.; Listoshin, S.B. [Ioffe Physico-Technical Institute, Polytekhnicheskaya Street 26, 194021 St. Petersburg (Russian Federation)

    2007-07-01

    A phenomenological approach to quantitative description of Zn(Mg)O growth by radical-source molecular beam epitaxy, based on the experimental studies of RHEED intensity oscillations, has been developed. It allows a precise control of growth rate, composition and stoichiometry at any growth temperature, Along with optimization of a growth initiation procedure on a c-sapphire, it is necessary condition for fabrication of high quality ZnO epilayers and ZnO/ZnMgO heterostructures in a wide Mg composition range. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  4. Growth of layered superconductor β-PdBi{sub 2} films using molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Denisov, N.V., E-mail: denisov@iacp.dvo.ru [Institute of Automation and Control Processes FEB RAS, 5 Radio Street, 690041 Vladivostok (Russian Federation); Matetskiy, A.V.; Tupkalo, A.V. [Institute of Automation and Control Processes FEB RAS, 5 Radio Street, 690041 Vladivostok (Russian Federation); Zotov, A.V. [Institute of Automation and Control Processes FEB RAS, 5 Radio Street, 690041 Vladivostok (Russian Federation); School of Natural Sciences, Far Eastern Federal University, 690950 Vladivostok (Russian Federation); Department of Electronics, Vladivostok State University of Economics and Service, 690600 Vladivostok (Russian Federation); Saranin, A.A. [Institute of Automation and Control Processes FEB RAS, 5 Radio Street, 690041 Vladivostok (Russian Federation); School of Natural Sciences, Far Eastern Federal University, 690950 Vladivostok (Russian Federation)

    2017-04-15

    Highlights: • Bulk β-PdBi{sub 2} is layered material with advanced properties of topological superconductor. • We present a method for growing β-PdBi{sub 2} films of a desired thickness. • Method utilizes MBE growth of β-PdBi{sub 2}, using Bi(111) film on Si(111) as a template. • Electronic and superconducting properties of the films are similar to those of bulk β-PdBi{sub 2}. - Abstract: Bulk β-PdBi{sub 2} layered material exhibits advanced properties and is supposed to be probable topological superconductor. We present a method based on molecular beam epitaxy that allows us to grow β-PdBi{sub 2} films from a single β-PdBi{sub 2} triple layer up to the dozens of triple layers, using Bi(111) film on Si(111) as a template. The grown films demonstrate structural, electronic and superconducting properties similar to those of bulk β-PdBi{sub 2} crystals. Ability to grow the β-PdBi{sub 2} films of desired thickness opens the promising possibilities to explore fascinating properties of this advanced material.

  5. Thin film growth of CaFe2As2 by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Hatano, T; Fujimoto, R; Nakamura, I; Mori, Y; Ikuta, H; Kawaguchi, T; Harada, S; Ujihara, T

    2016-01-01

    Film growth of CaFe 2 As 2 was realized by molecular beam epitaxy on six different substrates that have a wide variation in the lattice mismatch to the target compound. By carefully adjusting the Ca-to-Fe flux ratio, we obtained single-phase thin films for most of the substrates. Interestingly, an expansion of the CaFe 2 As 2 lattice to the out-of-plane direction was observed for all films, even when an opposite strain was expected. A detailed microstructure observation of the thin film grown on MgO by transmission electron microscope revealed that it consists of cube-on-cube and 45°-rotated domains. The latter domains were compressively strained in plane, which caused a stretching along the c-axis direction. Because the domains were well connected across the boundary with no appreciable discontinuity, we think that the out-of-plane expansion in the 45°-rotated domains exerted a tensile stress on the other domains, resulting in the unexpectedly large c-axis lattice parameter, despite the apparently opposite lattice mismatch. (paper)

  6. Thin film growth of CaFe2As2 by molecular beam epitaxy

    Science.gov (United States)

    Hatano, T.; Kawaguchi, T.; Fujimoto, R.; Nakamura, I.; Mori, Y.; Harada, S.; Ujihara, T.; Ikuta, H.

    2016-01-01

    Film growth of CaFe2As2 was realized by molecular beam epitaxy on six different substrates that have a wide variation in the lattice mismatch to the target compound. By carefully adjusting the Ca-to-Fe flux ratio, we obtained single-phase thin films for most of the substrates. Interestingly, an expansion of the CaFe2As2 lattice to the out-of-plane direction was observed for all films, even when an opposite strain was expected. A detailed microstructure observation of the thin film grown on MgO by transmission electron microscope revealed that it consists of cube-on-cube and 45°-rotated domains. The latter domains were compressively strained in plane, which caused a stretching along the c-axis direction. Because the domains were well connected across the boundary with no appreciable discontinuity, we think that the out-of-plane expansion in the 45°-rotated domains exerted a tensile stress on the other domains, resulting in the unexpectedly large c-axis lattice parameter, despite the apparently opposite lattice mismatch.

  7. Molecular beam epitaxy a short history

    CERN Document Server

    Orton, J W

    2015-01-01

    This volume describes the development of molecular beam epitaxy from its origins in the 1960s through to the present day. It begins with a short historical account of other methods of crystal growth, both bulk and epitaxial, to set the subject in context, emphasising the wide range of semiconductor materials employed. This is followed by an introduction to molecular beams and their use in the Stern-Gerlach experiment and the development of the microwave MASER.

  8. In silico carbon molecular beam epitaxial growth of graphene on the h-BN substrate: carbon source effect on van der Waals epitaxy

    Science.gov (United States)

    Lee, Jonghoon; Varshney, Vikas; Park, Jeongho; Farmer, Barry L.; Roy, Ajit K.

    2016-05-01

    Against the presumption that hexagonal boron-nitride (h-BN) should provide an ideal substrate for van der Waals (vdW) epitaxy to grow high quality graphene films, carbon molecular beam epitaxy (CMBE) techniques using solid carbon sublimation have reported relatively poor quality of the graphene. In this article, the CMBE growth of graphene on the h-BN substrate is numerically studied in order to identify the effect of the carbon source on the quality of the graphene film. The carbon molecular beam generated by the sublimation of solid carbon source materials such as graphite and glassy carbon is mostly composed of atomic carbon, carbon dimers and carbon trimers. Therefore, the graphene film growth becomes a complex process involving various deposition characteristics of a multitude of carbon entities. Based on the study of surface adsorption and film growth characteristics of these three major carbon entities comprising graphite vapour, we report that carbon trimers convey strong traits of vdW epitaxy prone to high quality graphene growth, while atomic carbon deposition is a surface-reaction limited process accompanied by strong chemisorption. The vdW epitaxial behaviour of carbon trimers is found to be substantial enough to nucleate and develop into graphene like planar films within a nanosecond of high flux growth simulation, while reactive atomic carbons tend to impair the structural integrity of the crystalline h-BN substrate upon deposition to form an amorphous interface between the substrate and the growing carbon film. The content of reactive atomic carbons in the molecular beam is suspected to be the primary cause of low quality graphene reported in the literature. A possible optimization of the molecular beam composition towards the synthesis of better quality graphene films is suggested.Against the presumption that hexagonal boron-nitride (h-BN) should provide an ideal substrate for van der Waals (vdW) epitaxy to grow high quality graphene films, carbon

  9. Growth of InN on 6H-SiC by plasma assisted molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Brown, April S.; Kim, Tong-Ho; Choi, Soojeong; Wu, Pae; Morse, Michael [Department of Electrical and Computer Engineering, Duke University, 128 Hudson Hall, Durham, NC (United States); Losurdo, Maria; Giangregorio, Maria M.; Bruno, Giovanni [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy); Moto, Akihiro [Innovation Core SEI, Inc., 3235 Kifer Road, Santa Clara, CA 95051 (United States)

    2006-06-15

    We have investigated the growth of InN films by plasma assisted molecular beam epitaxy on the Si-face of 6H-SiC(0001). Growth is performed under In-rich conditions using a two-step process consisting of the deposition of a thin, low-temperature 350 C InN buffer layer, followed by the subsequent deposition of the InN epitaxial layer at 450 C. The effect of buffer annealing is investigated. The structural and optical evolution of the growing layer has been monitored in real time using RHEED and spectroscopic ellipsometry. Structural, morphological, electrical and optic properties are discussed. (copyright 2006 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  10. Growth and characterization of molecular beam epitaxial GaAs layers on porous silicon

    Science.gov (United States)

    Lin, T. L.; Liu, J. K.; Sadwick, L.; Wang, K. L.; Kao, Y. C.

    1987-01-01

    GaAs layers have been grown on porous silicon (PS) substrates with good crystallinity by molecular beam epitaxy. In spite of the surface irregularity of PS substrates, no surface morphology deterioration was observed on epitaxial GaAs overlayers. A 10-percent Rutherford backscattering spectroscopy minimum channeling yield for GaAs-on-PS layers as compared to 16 percent for GaAs-on-Si layers grown under the same condition indicates a possible improvement of crystallinity when GaAs is grown on PS. Transmission electron microscopy reveals that the dominant defects in the GaAs-on-PS layers are microtwins and stacking faults, which originate from the GaAs/PS interface. GaAs is found to penetrate into the PS layers. n-type GaAs/p-type PS heterojunction diodes were fabricated with good rectifying characteristics.

  11. Reactive molecular beam epitaxial growth and in situ photoemission spectroscopy study of iridate superlattices

    Directory of Open Access Journals (Sweden)

    C. C. Fan

    2017-08-01

    Full Text Available High-quality (001-oriented perovskite [(SrIrO3m/(SrTiO3] superlattices (m=1/2, 1, 2, 3 and ∞ films have been grown on SrTiO3(001 epitaxially using reactive molecular beam epitaxy. Compared to previously reported superlattices synthesized by pulsed laser deposition, our superlattices exhibit superior crystalline, interface and surface structure, which have been confirmed by high-resolution X-ray diffraction, scanning transmission electron microscopy and atomic force microscopy, respectively. The transport measurements confirm a novel insulator-metal transition with the change of dimensionality in these superlattices, and our first systematic in situ photoemission spectroscopy study indicates that the increasing strength of effective correlations induced by reducing dimensionality would be the dominating origin of this transition.

  12. Roles of kinetics and energetics in the growth of AlN by plasma-assisted molecular beam epitaxy

    International Nuclear Information System (INIS)

    Im, I. H.; Minegishi, T.; Hanada, T.; Lee, S. W.; Cho, M. W.; Yao, T.; Oh, D. C.; Chang, J. H.

    2006-01-01

    The roles of kinetics and energetics in the growth processes of AlN on c-sapphire by plasma assisted molecular beam epitaxy are investigated by varying the growth rate from 1 to 31 A/min and the substrate temperature from 800 to 1000 .deg. C. The energetics is found to govern the growth of AlN in the low-growth rate region even at a low substrate temperature of 800 .deg. C owing to the enhanced residence time of adatoms, thereby increasing the surface migration length. As the growth rate increases, the growth tends to be governed by kinetics because of a reduction in the residence time of adatoms. Consequently, the surface roughness and crystal quality are greatly improved for the low-growth-rate case. In addition, the lattice strain relaxation is completed from the beginning of epitaxy for energetics-limiting growth while lattice strain relaxation is retarded for kinetics-limiting growth because of pre-existing partial strain relaxation. Energetics becomes more favorable as the substrate temperature is raised because of an increase in the surface diffusion length owing to an enhanced diffusion coefficient. Consequently high-crystal-quality AlN layers are grown under the energetics-limiting growth condition with a screw dislocation density of 7.4 x 10 8 cm -2 even for a thin 42-nm thick film.

  13. Molecular Beam Epitaxial Growth and Characterization of Graphene and Hexagonal Boron Nitride Two-Dimensional Layers

    Science.gov (United States)

    Zheng, Renjing

    Van der Waals (vdW) materials (also called as two-dimensional (2D) material in some literature) systems have received extensive attention recently due to their potential applications in next-generation electronics platform. Exciting properties have been discovered in this field, however, the performance and properties of the systems rely on the materials' quality and interface significantly, leading to the urgent need for scalable synthesis of high-quality vdW crystals and heterostructures. Toward this direction, this dissertation is devoted on the study of Molecular Beam Epitaxy (MBE) growth and various characterization of vdW materials and heterostructures, especially graphene and hexagonal boron nitride (h-BN). The goal is to achieve high-quality vdW materials and related heterostructures. There are mainly four projects discussed in this dissertation. The first project (Chapter 2) is about MBE growth of large-area h-BN on copper foil. After the growth, the film was transferred onto SiO2 substrate for characterization. It is observed that as-grown film gives evident h-BN Raman spectrum; what's more, h-BN peak intensity and position is dependent on film thickness. N-1s and B-1s XPS peaks further suggest the formation of h-BN. AFM and SEM images show the film is flat and continuous over large area. Our synthesis method shows it's possible to use MBE to achieve h-BN growth and could also pave a way for some unique structure, such as h-BN/graphene heterostructures and doped h-BN films by MBE. The second project (Chapter 3) is focused on establishment of grapehene/h-BN heterostructure on cobalt (Co) film. In-situ epitaxial growth of graphene/h-BN heterostructures on Co film substrate was achieved by using plasma-assisted MBE. The direct graphene/h-BN vertical stacking structures were demonstrated and further confirmed by various characterizations, such as Raman spectroscopy, SEM, XPS and TEM. Large area heterostructures consisting of single- /bilayer graphene and

  14. Molecular beam epitaxy growth and characterization of two-six materials for visible semiconductor lasers

    Science.gov (United States)

    Zeng, Linfei

    This thesis proposes the molecular beam epitaxy (MBE) growth and characterization of a new Znsb{x}Cdsb{y}Mgsb{(1-x-y)}Se based semiconductor materials system on InP substrates for visible light emitting diodes (LED) and lasers. The growth conditions for lattice-matched Znsb{x}Cdsb{y}Mgsb{(1-x-y)}Se layers with the desired bandgap have been established and optimized. A chemical etching technique to measure the defect density of Znsb{x}Cdsb{y}Mgsb{(1-x-y)}Se materials has been established. The accuracy of this method for revealing stacking faults and dislocations was verified by plan-view TEM. Using the techniques such as III-V buffer layer, Zn-irradiation, low-temperature growth, ZnCdSe interfacial layer and growth interruption to improve the quality of the interface of III-V and II-VI, the material quality of Znsb{x}Cdsb{y}Mgsb{(1-x-y)}Se has been improved dramatically. Defect density has been reduced from 10sp{10}\\ cmsp{-2} to {˜}5×10sp4\\ cmsp{-2}. The properties of this material system such as the quality and strain state in the epilayer, the dependence of bandgap on temperature, and the band offset have been studied by using double crystal x-ray diffraction, photoluminescence and capacitance voltage measurements. The ZnCdSe/ZnCdMgSe based quantum well (QW) structures have been grown and studied. Optically pumped lasing with emission range from red to blue has been obtained from ZnCdSe/ZnCdMgSe based separate-confinement single QW laser structures. The results demonstrate the potential for these materials as integrated full color display devices. Preliminary studies of the degradation behavior of ZnCdSe/ZnCdMgSe QW were performed. No dark line defects (DLDs) were observed during the degradation. A very strong room temperature differential negative resistance behavior was observed from Al/Znsb{0.61}Cdsb{0.39}Se/nsp+-InP devices, which is useful in millimeter-wave applications. We also found that these devices can be set to either in highly conductive or

  15. Growth mechanisms of plasma-assisted molecular beam epitaxy of green emission InGaN/GaN single quantum wells at high growth temperatures

    International Nuclear Information System (INIS)

    Yang, W. C.; Wu, C. H.; Tseng, Y. T.; Chiu, S. Y.; Cheng, K. Y.

    2015-01-01

    The results of the growth of thin (∼3 nm) InGaN/GaN single quantum wells (SQWs) with emission wavelengths in the green region by plasma-assisted molecular beam epitaxy are present. An improved two-step growth method using a high growth temperature up to 650 °C is developed to increase the In content of the InGaN SQW to 30% while maintaining a strong luminescence intensity near a wavelength of 506 nm. The indium composition in InGaN/GaN SQW grown under group-III-rich condition increases with increasing growth temperature following the growth model of liquid phase epitaxy. Further increase in the growth temperature to 670 °C does not improve the photoluminescence property of the material due to rapid loss of indium from the surface and, under certain growth conditions, the onset of phase separation

  16. Epitaxial growth of hybrid nanostructures

    Science.gov (United States)

    Tan, Chaoliang; Chen, Junze; Wu, Xue-Jun; Zhang, Hua

    2018-02-01

    Hybrid nanostructures are a class of materials that are typically composed of two or more different components, in which each component has at least one dimension on the nanoscale. The rational design and controlled synthesis of hybrid nanostructures are of great importance in enabling the fine tuning of their properties and functions. Epitaxial growth is a promising approach to the controlled synthesis of hybrid nanostructures with desired structures, crystal phases, exposed facets and/or interfaces. This Review provides a critical summary of the state of the art in the field of epitaxial growth of hybrid nanostructures. We discuss the historical development, architectures and compositions, epitaxy methods, characterization techniques and advantages of epitaxial hybrid nanostructures. Finally, we provide insight into future research directions in this area, which include the epitaxial growth of hybrid nanostructures from a wider range of materials, the study of the underlying mechanism and determining the role of epitaxial growth in influencing the properties and application performance of hybrid nanostructures.

  17. A Molecular Dynamics Study of the Epitaxial Growth of Metallic Nanoclusters Softly Deposited on Substrates with Very Different Lattice Parameter

    International Nuclear Information System (INIS)

    Jimenez-Saez, J C; Perez-MartIn, A M C; Jimenez-RodrIguez, J J

    2007-01-01

    The soft deposition of Cu and Au clusters on Au(001) and Cu(001) surfaces respectively is studied by constant-temperature molecular-dynamics simulations. The initial shape of the nanoclusters is icosahedral or truncated octahedral (Wulff type). Their number of atoms ranges between 12 and 1289 atoms. Bombardment energy is of the order of a few meV/atom. The atomic interactions are mimicked by a many-body potential based on the tightbinding model. The effect of the temperature as activation to get the complete epitaxy is analysed. We have found that Cu clusters manage to align their {002} planes with the substrate by increasing the temperature. However, there is not epitaxial growth in any case since the lattice becomes bcc or important stacking faults are generated. For Au clusters, the alignment of these planes is practically independent of the temperature

  18. The growth of III-V nitrides heterostructure on Si substrate by plasma-assisted molecular beam epitaxy

    International Nuclear Information System (INIS)

    Beh, K.P.; Yam, F.K.; Chin, C.W.; Tneh, S.S.; Hassan, Z.

    2010-01-01

    This paper reports the growth of InGaN/GaN/AlN epitaxial layer on Si(1 1 1) substrate by utilizing plasma-assisted molecular beam epitaxy (PA-MBE) system. The as-grown film was characterized using high-resolution X-ray diffraction (HR-XRD) and photoluminescence (PL). High work function metals, iridium and gold were deposited on the film as metal contacts and their electrical characteristics at pre- and post-annealing were studied. The structural quality of this film is comparative to the values reported in the literature, and the indium molar fraction is 0.57 by employing Vegard's law. The relatively low yellow band emission signifies the grown film is of high quality. For metal contact studies it was found that the post-annealed sample for 5 min shows good conductivity as compared to the other samples.

  19. Molecular beam epitaxial growth and characterization of GaSb layers on GaAs (0 0 1) substrates

    International Nuclear Information System (INIS)

    Li Yanbo; Zhang Yang; Zhang Yuwei; Wang Baoqiang; Zhu Zhanping; Zeng Yiping

    2012-01-01

    We report on the growth of GaSb layers on GaAs (0 0 1) substrates by molecular beam epitaxy (MBE). We investigate the influence of the GaAs substrate surface treatment, growth temperature, and V/III flux ratios on the crystal quality and the surface morphology of GaSb epilayers. Comparing to Ga-rich GaAs surface preparation, the Sb-rich GaAs surface preparation can promote the growth of higher-quality GaSb material. It is found that the crystal quality, electrical properties, and surface morphology of the GaSb epilayers are highly dependent on the growth temperature, and Sb/Ga flux ratios. Under the optimized growth conditions, we demonstrate the epitaxial growth of high quality GaSb layers on GaAs substrates. The p-type nature of the unintentionally doped GaSb is studied and from the growth conditions dependence of the hole concentrations of the GaSb, we deduce that the main native acceptor in the GaSb is the Ga antisite (Ga Sb ) defect.

  20. Growth and etching characteristics of (001) β-Ga2O3 by plasma-assisted molecular beam epitaxy

    Science.gov (United States)

    Oshima, Yuichi; Ahmadi, Elaheh; Kaun, Stephen; Wu, Feng; Speck, James S.

    2018-01-01

    We investigated the homoepitaxial growth and etching characteristics of (001) β-Ga2O3 by plasma-assisted molecular beam epitaxy. The growth rate of β-Ga2O3 increased with increasing Ga-flux, reaching a clear plateau of 56 nm h-1, and then decreased at higher Ga-flux. The growth rate decreased from 56 to 42 nm h-1 when the substrate temperature was increased from 750 °C to 800 °C. The growth rate was negative (net etching) when only Ga-flux was supplied. The etching rate proportionally increased with increasing the Ga-flux, reaching 84 nm h-1. The etching was enhanced at higher temperatures. It was found that Ga-etching of (001) β-Ga2O3 substrates prior to the homoepitaxial growth markedly improved the surface roughness of the film.

  1. Direct growth of hexagonal boron nitride/graphene heterostructures on cobalt foil substrates by plasma-assisted molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Zhongguang; Khanaki, Alireza; Tian, Hao; Zheng, Renjing; Suja, Mohammad; Liu, Jianlin, E-mail: jianlin@ece.ucr.edu [Quantum Structures Laboratory, Department of Electrical and Computer Engineering, University of California, Riverside, California 92521 (United States); Zheng, Jian-Guo [Irvine Materials Research Institute, University of California, Irvine, California 92697-2800 (United States)

    2016-07-25

    Graphene/hexagonal boron nitride (G/h-BN) heterostructures have attracted a great deal of attention because of their exceptional properties and wide variety of potential applications in nanoelectronics. However, direct growth of large-area, high-quality, and stacked structures in a controllable and scalable way remains challenging. In this work, we demonstrate the synthesis of h-BN/graphene (h-BN/G) heterostructures on cobalt (Co) foil by sequential deposition of graphene and h-BN layers using plasma-assisted molecular beam epitaxy. It is found that the coverage of h-BN layers can be readily controlled on the epitaxial graphene by growth time. Large-area, uniform-quality, and multi-layer h-BN films on thin graphite layers were achieved. Based on an h-BN (5–6 nm)/G (26–27 nm) heterostructure, capacitor devices with Co(foil)/G/h-BN/Co(contact) configuration were fabricated to evaluate the dielectric properties of h-BN. The measured breakdown electric field showed a high value of ∼2.5–3.2 MV/cm. Both I-V and C-V characteristics indicate that the epitaxial h-BN film has good insulating characteristics.

  2. Pumping requirements and options for molecular beam epitaxy and gas source molecular beam epitaxy/chemical beam epitaxy

    International Nuclear Information System (INIS)

    McCollum, M.J.; Plano, M.A.; Haase, M.A.; Robbins, V.M.; Jackson, S.L.; Cheng, K.Y.; Stillman, G.E.

    1989-01-01

    This paper discusses the use of gas sources in growth by MBE as a result of current interest in growth of InP/InGaAsP/InGaAs lattice matched to InP. For gas flows greater than a few sccm, pumping speed requirements dictate the use of turbomolecular or diffusion pumps. GaAs samples with high p-type mobilities have been grown with diffusion pumped molecular beam epitaxial system. According to the authors, this demonstration of the inherent cleanliness of a properly designed diffusion pumping system indicates that a diffusion pump is an excellent inexpensive and reliable choice for growth by molecular beam epitaxy and gas source molecular beam epitaxy/chemical beam epitaxy

  3. Enhanced growth of highly lattice-mismatched CdSe on GaAs substrates by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Wang, Jyh-Shyang; Tsai, Yu-Hsuan; Wang, Hsiao-Hua; Ke, Han-Xiang; Tong, Shih-Chang; Yang, Chu-Shou; Wu, Chih-Hung; Shen, Ji-Lin

    2013-01-01

    This work demonstrates the improvement of the molecular beam epitaxial growth of zinc-blende CdSe on (0 0 1) GaAs substrate with a large lattice mismatch by introducing a small amount of Te atoms. Exposing the growing surface to Te atoms changes the reflection high-energy electron diffraction pattern from spotty to streaky together with (2 × 1) surface reconstruction, and greatly reduces the full width at half maximum of the X-ray rocking curve and increases the integral intensity of room-temperature photoluminescence by a factor of about nine.

  4. Atomic layer epitaxy of ZnO for applications in molecular beam epitaxy growth of GaN and InGaN

    International Nuclear Information System (INIS)

    Godlewski, M.; Szczerbakow, A.; Ivanov, V. Yu.; Barski, A.; Goldys, E.M.

    2000-01-01

    We report the successful atomic layer epitaxy growth of thin ZnO films and their use for GaN and InGaN epitaxy. The properties of ZnO epilayers, obtained by four different procedures, are analysed, as well as of GaN and InGaN films grown on ZnO-coated Si and GaAs by MBE. (author)

  5. Nickel enhanced graphene growth directly on dielectric substrates by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Wofford, Joseph M., E-mail: joewofford@gmail.com, E-mail: lopes@pdi-berlin.de; Lopes, Joao Marcelo J., E-mail: joewofford@gmail.com, E-mail: lopes@pdi-berlin.de; Riechert, Henning [Paul-Drude-Institut für Festkörperelektronik, Hausvogteiplatz 5-7, 10117 Berlin (Germany); Speck, Florian; Seyller, Thomas [Technische Universität Chemnitz, Institut für Physik, Reichenhainer Str. 70, 09126 Chemnitz (Germany)

    2016-07-28

    The efficacy of Ni as a surfactant to improve the crystalline quality of graphene grown directly on dielectric Al{sub 2}O{sub 3}(0001) substrates by molecular beam epitaxy is examined. Simultaneously exposing the substrate to a Ni flux throughout C deposition at 950 °C led to improved charge carrier mobility and a Raman spectrum indicating less structural disorder in the resulting nanocrystalline graphene film. X-ray photoelectron spectroscopy confirmed that no residual Ni could be detected in the film and showed a decrease in the intensity of the defect-related component of the C1s level. Similar improvements were not observed when a lower substrate temperature (850 °C) was used. A close examination of the Raman spectra suggests that Ni reduces the concentration of lattice vacancies in the film, possibly by catalytically assisting adatom incorporation.

  6. Effects of substrate anisotropy and edge diffusion on submonolayer growth during molecular beam epitaxy: A Kinetic Monte Carlo study

    International Nuclear Information System (INIS)

    Devkota, J.; Shrestha, S.P.

    2007-12-01

    We have performed Kinetic Monte Carlo simulation work to study the effect of diffusion anisotropy, bonding anisotropy and edge diffusion on island formation at different temperatures during the sub-monolayer film growth in Molecular Beam Epitaxy. We use simple cubic solid on solid model and event based Bortz, Kalos and Labowitch (BKL) algorithm on the Kinetic Monte Carlo method to simulate the physical phenomena. We have found that the island morphology and growth exponent are found to be influenced by substrate anisotropy as well as edge diffusion, however they do not play a significant role in island elongation. The growth exponent and island size distribution are observed to be influenced by substrate anisotropy but are negligibly influenced by edge diffusion. We have found fractal islands when edge diffusion is excluded and compact islands when edge diffusion is included. (author)

  7. Molecular-beam epitaxy growth and structural characterization of semiconductor-ferromagnet heterostructures by grazing incidence X-ray diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Satapathy, D.K.

    2005-12-19

    The present work is devoted to the growth of the ferromagnetic metal MnAs on the semiconductor GaAs by molecular-beam epitaxy (MBE). The MnAs thin films are deposited on GaAs by molecular-beam epitaxy (MBE). Grazing incidence diffraction (GID) and reflection high-energy electron diffraction (RHEED) are used in situ to investigate the nucleation, evolution of strain, morphology and interfacial structure during the MBE growth. Four stages of the nucleation process during growth of MnAs on GaAs(001) are revealed by RHEED azimuthal scans. GID shows that further growth of MnAs films proceed via the formation of relaxed islands at a nominal thickness of 2.5 ML which increase in size and finally coalesce to form a continuous film. Early on, an ordered array of misfit dislocations forms at the interface releasing the misfit strain even before complete coalescence occurs. The fascinating complex nucleation process of MnAs on GaAs(0 0 1) contains elements of both Volmer-Weber and Stranski-Krastanov growth. A nonuniform strain amounting to 0.66%, along the [1 -1 0] direction and 0.54%, along the [1 1 0] direction is demonstrated from x-ray line profile analysis. A high correlation between the defects is found along the GaAs[1 1 0] direction. An extremely periodic array of misfit dislocations with a period of 4.95{+-}0.05 nm is formed at the interface along the [1 1 0] direction which releases the 7.5% of misfit. The inhomogeneous strain due to the periodic dislocations is confined at the interface within a layer of 1.6 nm thickness. The misfit along the [1 -1 0] direction is released by the formation of a coincidence site lattice. (orig.)

  8. Germanium growth on electron beam lithography patterned Si3N4/Si(001) substrate using molecular beam epitaxy

    Science.gov (United States)

    Sarkar, Subhendu Sinha; Katiyar, Ajit K.; Sarkar, Arijit; Dhar, Achintya; Rudra, Arun; Khatri, Ravinder K.; Ray, Samit Kumar

    2018-04-01

    It is important to investigate the growth dynamics of Ge adatoms under different surface stress regimes of the patterned dielectric to control the selective growth of self-assembled Ge nanostructures on silicon. In the present work, we have studied the growth of Ge by molecular beam epitaxy on nanometer scale patterned Si3N4/Si(001) substrates generated using electron beam lithography. The pitch of the patterns has been varied to investigate its effect on the growth of Ge in comparison to un-patterned Si3N4. For the patterned Si3N4 film, Ge did not desorbed completely from the Si3N4 film and hence no site selective growth pattern is observed. Instead, depending upon the pitch, Ge growth has occurred in different growth modes around the openings in the Si3N4. For the un-patterned substrate, the morphology exhibits the occurrence of uniform 3D clustering of Ge adatoms on Si3N4 film. This variation in the growth modes of Ge is attributed to the variation of residual stress in the Si3N4 film for different pitch of holes, which has been confirmed theoretically through Comsol Multiphysics simulation. The variation in stress for different pitches resulted in modulation of surface energy of the Si3N4 film leading to the different growth modes of Ge.

  9. Numerical approximations for the molecular beam epitaxial growth model based on the invariant energy quadratization method

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Xiaofeng, E-mail: xfyang@math.sc.edu [Department of Mathematics, University of South Carolina, Columbia, SC 29208 (United States); Zhao, Jia, E-mail: zhao62@math.sc.edu [Department of Mathematics, University of South Carolina, Columbia, SC 29208 (United States); Department of Mathematics, University of North Carolina at Chapel Hill, Chapel Hill, NC 27599 (United States); Wang, Qi, E-mail: qwang@math.sc.edu [Department of Mathematics, University of South Carolina, Columbia, SC 29208 (United States); Beijing Computational Science Research Center, Beijing (China); School of Materials Science and Engineering, Nankai University, Tianjin (China)

    2017-03-15

    The Molecular Beam Epitaxial model is derived from the variation of a free energy, that consists of either a fourth order Ginzburg–Landau double well potential or a nonlinear logarithmic potential in terms of the gradient of a height function. One challenge in solving the MBE model numerically is how to develop proper temporal discretization for the nonlinear terms in order to preserve energy stability at the time-discrete level. In this paper, we resolve this issue by developing a first and second order time-stepping scheme based on the “Invariant Energy Quadratization” (IEQ) method. The novelty is that all nonlinear terms are treated semi-explicitly, and the resulted semi-discrete equations form a linear system at each time step. Moreover, the linear operator is symmetric positive definite and thus can be solved efficiently. We then prove that all proposed schemes are unconditionally energy stable. The semi-discrete schemes are further discretized in space using finite difference methods and implemented on GPUs for high-performance computing. Various 2D and 3D numerical examples are presented to demonstrate stability and accuracy of the proposed schemes.

  10. Backward diodes using heavily Mg-doped GaN growth by ammonia molecular-beam epitaxy

    Science.gov (United States)

    Okumura, Hironori; Martin, Denis; Malinverni, Marco; Grandjean, Nicolas

    2016-02-01

    We grew heavily Mg-doped GaN using ammonia molecular-beam epitaxy. The use of low growth temperature (740 °C) allows decreasing the incorporation of donor-like defects (p-type doping compensation. As a result, a net acceptor concentration of 7 × 1019 cm-3 was achieved, and the hole concentration measured by Hall effect was as high as 2 × 1019 cm-3 at room temperature. Using such a high Mg doping level, we fabricated GaN backward diodes without polarization-assisted tunneling. The backward diodes exhibited a tunneling-current density of 225 A/cm2 at a reverse bias of -1 V at room temperature.

  11. Molecular beam epitaxial growth and characterization of Al(Ga)N nanowire deep ultraviolet light emitting diodes and lasers

    International Nuclear Information System (INIS)

    Mi, Z; Zhao, S; Djavid, M; Liu, X; Kang, J; Woo, S Y; Bugnet, M; Botton, G A; Kong, X; Guo, H; Ji, W; Liu, Z

    2016-01-01

    We report on the detailed molecular beam epitaxial growth and characterization of Al(Ga)N nanowire heterostructures on Si and their applications for deep ultraviolet light emitting diodes and lasers. The nanowires are formed under nitrogen-rich conditions without using any metal catalyst. Compared to conventional epilayers, Mg-dopant incorporation is significantly enhanced in nearly strain- and defect-free Al(Ga)N nanowire structures, leading to efficient p -type conduction. The resulting Al(Ga)N nanowire LEDs exhibit excellent performance, including a turn-on voltage of ∼5.5 V for an AlN nanowire LED operating at 207 nm. The design, fabrication, and performance of an electrically injected AlGaN nanowire laser operating in the UV-B band is also presented. (paper)

  12. Effects of growth rate on structural property and adatom migration behaviors for growth of GaInNAs/GaAs (001) by molecular beam epitaxy

    Science.gov (United States)

    Li, Jingling; Gao, Peng; Zhang, Shuguang; Wen, Lei; Gao, Fangliang; Li, Guoqiang

    2018-03-01

    We have investigated the structural properties and the growth mode of GaInNAs films prepared at different growth rates (Rg) by molecular beam epitaxy. The crystalline structure is studied by high resolution X-ray diffraction, and the evolution of GaInNAs film surface morphologies is studied by atomic force microscopy. It is found that both the crystallinity and the surface roughness are improved by increasing Rg, and the change in the growth mode is attributed to the adatom migration behaviors particularly for In atoms, which is verified by elemental analysis. In addition, we have presented some theoretical calculation results related to the N adsorption energy to show the unique N migration behavior, which is instructive to interpret the growth mechanism of GaInNAs films.

  13. Growth temperature and dopant species effects on deep levels in Si grown by low temperature molecular beam epitaxy

    International Nuclear Information System (INIS)

    Chung, Sung-Yong; Jin, Niu; Rice, Anthony T.; Berger, Paul R.; Yu, Ronghua; Fang, Z-Q.; Thompson, Phillip E.

    2003-01-01

    Deep-level transient spectroscopy measurements were performed in order to investigate the effects of substrate growth temperature and dopant species on deep levels in Si layers during low-temperature molecular beam epitaxial growth. The structures studied were n + -p junctions using B doping for the p layer and p + -n junctions using P doping for the n layer. While the density of hole traps H1 (0.38-0.41 eV) in the B-doped p layers showed a clear increase with decreasing growth temperature from 600 to 370 degree sign C, the electron trap density was relatively constant. Interestingly, the minority carrier electron traps E1 (0.42-0.45 eV) and E2 (0.257 eV), found in the B-doped p layers, are similar to the majority carrier electron traps E11 (0.48 eV) and E22 (0.269 eV) observed in P-doped n layers grown at 600 degree sign C. It is hypothesized that these dominating electron traps are associated with pure divacancy defects and are independent of the dopant species

  14. Growth of defect-free GaAsSbN axial nanowires via self-catalyzed molecular beam epitaxy

    Science.gov (United States)

    Sharma, Manish; Deshmukh, Prithviraj; Kasanaboina, Pavan; Reynolds, C. Lewis, Jr.; Liu, Yang; Iyer, Shanthi

    2017-12-01

    Bandgap reduction of 10% by incorporation of a dilute amount of N is reported for the first time, in axial GaAsSb nanowires (NWs) grown on Si (111) via Ga-assisted molecular beam epitaxy. Impact of N incorporation on the surface morphology, NW growth kinetics, and their structural and optical properties were examined. Dilute nitride NWs with Sb composition of 7 at% did not exhibit any noticeable planar defects, as revealed by the absence of satellite twin peaks in the selected-area diffraction pattern and high-resolution transmission electron microscopy imaging. Point defects were also minimal in as-grown dilute nitride NWs, as ascertained from the comparison of low-temperature photoluminescence spectra as well as the shape and shift of Raman modes, with in situ annealed NWs in different ambients. Evidence of enhanced incorporation of N was found in the NWs in situ annealed in N ambient, but with deteriorated optical quality due to simultaneous creation of N-induced defects. The lack of any noticeable defects in the as-grown GaAsSbN NWs demonstrates the advantage of the vapor-liquid-solid mechanism responsible for growth of axial configuration over the vapor-solid growth mechanism for core-shell NWs as well as their thin film counterpart, which commonly exhibit N-induced point defects.

  15. Molecular beam epitaxy of quasi-freestanding transition metal disulphide monolayers on van der Waals substrates: a growth study

    Science.gov (United States)

    Hall, Joshua; Pielić, Borna; Murray, Clifford; Jolie, Wouter; Wekking, Tobias; Busse, Carsten; Kralj, Marko; Michely, Thomas

    2018-04-01

    Based on an ultra-high vacuum compatible two-step molecular beam epitaxy synthesis with elemental sulphur, we grow clean, well-oriented, and almost defect-free monolayer islands and layers of the transition metal disulphides MoS2, TaS2 and WS2. Using scanning tunneling microscopy and low energy electron diffraction we investigate systematically how to optimise the growth process, and provide insight into the growth and annealing mechanisms. A large band gap of 2.55 eV and the ability to move flakes with the scanning tunneling microscope tip both document the weak interaction of MoS2 with its substrate consisting of graphene grown on Ir(1 1 1). As the method works for the synthesis of a variety of transition metal disulphides on different substrates, we speculate that it could be of great use for providing hitherto unattainable high quality monolayers of transition metal disulphides for fundamental spectroscopic investigations.

  16. Growth of Pb(Ti,Zr)O 3 thin films by metal-organic molecular beam epitaxy

    Science.gov (United States)

    Avrutin, V.; Liu, H. Y.; Izyumskaya, N.; Xiao, B.; Özgür, Ü.; Morkoç, H.

    2009-02-01

    Single-crystal Pb(Zr xTi 1-x)O 3 thin films have been grown on (0 0 1) SrTiO 3 and SrTiO 3:Nb substrates by molecular beam epitaxy using metal-organic source of Zr and two different sources of reactive oxygen—RF plasma and hydrogen-peroxide sources. The same growth modes and comparable structural properties were observed for the films grown with both oxygen sources, while the plasma source allowed higher growth rates. The films with x up to 0.4 were single phase, while attempts to increase x beyond gave rise to the ZrO 2 second phase. The effects of growth conditions on growth modes, Zr incorporation, and phase composition of the Pb(Zr xTi 1-x)O 3 films are discussed. Electrical and ferroelectric properties of the Pb(Zr xTi 1-x)O 3 films of ~100 nm in thickness grown on SrTiO 3:Nb were studied using current-voltage, capacitance-voltage, and polarization-field measurements. The single-phase films show low leakage currents and large breakdown fields, while the values of remanent polarization are low (around 5 μC/cm 2). It was found that, at high sweep fields, the contribution of the leakage current to the apparent values of remanent polarization can be large, even for the films with large electrical resistivity (˜10 8-10 9 Ω cm at an electric filed of 1 MV/cm). The measured dielectric constant ranges from 410 to 260 for Pb(Zr 0.33Ti 0.67)O 3 and from 313 to 213 for Pb(Zr 0.2Ti 0.8)O 3 in the frequency range from 100 to 1 MHz.

  17. Avoiding polar catastrophe in the growth of polarly orientated nickel perovskite thin films by reactive oxide molecular beam epitaxy

    International Nuclear Information System (INIS)

    Yang, H. F.; Liu, Z. T.; Fan, C. C.; Xiang, P.; Zhang, K. L.; Li, M. Y.; Liu, J. S.; Yao, Q.; Shen, D. W.

    2016-01-01

    By means of the state-of-the-art reactive oxide molecular beam epitaxy, we synthesized (001)- and (111)-orientated polar LaNiO 3 thin films. In order to avoid the interfacial reconstructions induced by polar catastrophe, screening metallic Nb-doped SrTiO 3 and iso-polarity LaAlO 3 substrates were chosen to achieve high-quality (001)-orientated films in a layer-by-layer growth mode. For largely polar (111)-orientated films, we showed that iso-polarity LaAlO 3 (111) substrate was more suitable than Nb-doped SrTiO 3 . In situ reflection high-energy electron diffraction, ex situ high-resolution X-ray diffraction, and atomic force microscopy were used to characterize these films. Our results show that special attentions need to be paid to grow high-quality oxide films with polar orientations, which can prompt the explorations of all-oxide electronics and artificial interfacial engineering to pursue intriguing emergent physics like proposed interfacial superconductivity and topological phases in LaNiO 3 based superlattices.

  18. Band offsets and growth mode of molecular beam epitaxy grown MgO (111) on GaN (0002) by x-ray photoelectron spectroscopy

    Science.gov (United States)

    Craft, H. S.; Collazo, R.; Losego, M. D.; Mita, S.; Sitar, Z.; Maria, J.-P.

    2007-10-01

    MgO is a proposed dielectric for use as a tunneling barrier in devices integrating GaN and ferroelectric oxides. In this study, we present data regarding the growth mode and band offsets of MgO grown epitaxially on GaN (0002) surfaces using molecular beam epitaxy. Using in situ x-ray photoelectron spectroscopy (XPS) and molecular beam epitaxy, we determine, from sequential growth experiments, that the growth of MgO proceeds via the Volmer-Weber (three-dimensional) mode, and full coalescence of the film does not occur until approximately 12nm of MgO has been deposited. The observation of a three-dimensional growth mode is in agreement with previously published data. For the valence band offset, we find a value of 1.2±0.2eV, which corresponds to a 3.2eV conduction band offset. XPS measurements suggest a chemically abrupt interface and no effect on band lineup due to the slow coalescence behavior.

  19. Band offsets and growth mode of molecular beam epitaxy grown MgO (111) on GaN (0002) by x-ray photoelectron spectroscopy

    International Nuclear Information System (INIS)

    Craft, H. S.; Collazo, R.; Losego, M. D.; Mita, S.; Sitar, Z.; Maria, J.-P.

    2007-01-01

    MgO is a proposed dielectric for use as a tunneling barrier in devices integrating GaN and ferroelectric oxides. In this study, we present data regarding the growth mode and band offsets of MgO grown epitaxially on GaN (0002) surfaces using molecular beam epitaxy. Using in situ x-ray photoelectron spectroscopy (XPS) and molecular beam epitaxy, we determine, from sequential growth experiments, that the growth of MgO proceeds via the Volmer-Weber (three-dimensional) mode, and full coalescence of the film does not occur until approximately 12 nm of MgO has been deposited. The observation of a three-dimensional growth mode is in agreement with previously published data. For the valence band offset, we find a value of 1.2±0.2 eV, which corresponds to a 3.2 eV conduction band offset. XPS measurements suggest a chemically abrupt interface and no effect on band lineup due to the slow coalescence behavior

  20. Epitaxial growth and magnetic properties of Fe4-xMnxN thin films grown on MgO(0 0 1) substrates by molecular beam epitaxy

    Science.gov (United States)

    Anzai, Akihito; Takata, Fumiya; Gushi, Toshiki; Toko, Kaoru; Suemasu, Takashi

    2018-05-01

    Epitaxial Fe4-xMnxN (x = 0, 1, 2, 3, and 4) thin films were successfully grown on MgO(0 0 1) single-crystal substrates by molecular beam epitaxy, and their crystalline qualities and magnetic properties were investigated. It was found that the lattice constants of Fe4-xMnxN obtained from X-ray diffraction measurement increased with the Mn content. The ratio of the perpendicular lattice constant c to the in-plane lattice constant a of Fe4-xMnxN was found to be about 0.99 at x ⩾ 2. The magnetic properties evaluated using a vibrating sample magnetometer at room temperature revealed that all of the Fe4-xMnxN films exhibited ferromagnetic behavior regardless of the value of x. In addition, the saturation magnetization decreased non-linearly as the Mn content increased. Finally, FeMn3N and Mn4N exhibited perpendicular anisotropy and their uniaxial magnetic anisotropy energies were 2.2 × 105 and 7.5 × 105 erg/cm3, respectively.

  1. Three-dimensional lattice rotation in GaAs nanowire growth on hydrogen-silsesquioxane covered GaAs (001) using molecular beam epitaxy

    Science.gov (United States)

    Tran, Dat Q.; Pham, Huyen T.; Higashimine, Koichi; Oshima, Yoshifumi; Akabori, Masashi

    2018-05-01

    We report on crystallographic behaviors of inclined GaAs nanowires (NWs) self-crystallized on GaAs (001) substrate. The NWs were grown on hydrogen-silsesquioxane (HSQ) covered substrates using molecular beam epitaxy (MBE). Commonly, the epitaxial growth of GaAs B (B-polar) NWs is prominently observed on GaAs (001); however, we yielded a remarkable number of epitaxially grown GaAs A (A-polar) NWs in addition to the majorly obtained B-polar NWs. Such NW orientations are always accompanied by a typical inclined angle of 35° from (001) plane. NWs with another inclined angle of 74° were additionally observed and attributed to be -oriented, not in direct epitaxial relation with the substrate. Such 74° NWs' existence is related to first-order three-dimensional (3D) lattice rotation taking place at the very beginning of the growth. It turns out that spatially 60° lattice rotation around directions at GaAs seeds is essentially in charge of A- and B-polar 74° NWs. Transmission electron microscope observations reveal a high density of twinning in the B-polar NWs and twin-free characteristic in the A-polar NWs.

  2. Epitaxial growth of M-plane GaN on ZnO micro-rods by plasma-assisted molecular beam epitaxy

    Directory of Open Access Journals (Sweden)

    Shuo-Ting You

    2015-12-01

    Full Text Available We have studied the GaN grown on ZnO micro-rods by plasma-assisted molecular beam epitaxy. From the analyses of GaN microstructure grown on non-polar M-plane ZnO surface ( 10 1 ̄ 0 by scanning transmission electron microscope, we found that the ZnGa2O4 compound was formed at the M-plane hetero-interface, which was confirmed by polarization-dependent photoluminescence. We demonstrated that the M-plane ZnO micro-rod surface can be used as an alternative substrate to grow high quality M-plane GaN epi-layers.

  3. Molecular beam epitaxial growth and characterization of zinc-blende ZnMgSe on InP (001)

    International Nuclear Information System (INIS)

    Sohel, Mohammad; Munoz, Martin; Tamargo, Maria C.

    2004-01-01

    High crystalline quality zinc-blende structure Zn (1-x) Mg x Se epitaxial layers were grown on InP (001) substrates by molecular beam epitaxy. Their band gap energies were determined as a function of Mg concentration and a linear dependence was observed. The band gap of the Zn (1-x) Mg x Se closely lattice matched to InP was found to be 3.59 eV at 77 K and the extrapolated value for zinc-blende MgSe was determined to be 3.74 eV. Quantum wells of Zn (1-x) Cd x Se with Zn (1-x) Mg x Se as the barrier layer were grown which exhibit near ultraviolet emission

  4. Adsorption-controlled growth of La-doped BaSnO3 by molecular-beam epitaxy

    Directory of Open Access Journals (Sweden)

    Hanjong Paik

    2017-11-01

    Full Text Available Epitaxial La-doped BaSnO3 films were grown in an adsorption-controlled regime by molecular-beam epitaxy, where the excess volatile SnOx desorbs from the film surface. A film grown on a (001 DyScO3 substrate exhibited a mobility of 183 cm2 V−1 s−1 at room temperature and 400 cm2 V−1 s−1 at 10 K despite the high concentration (1.2 × 1011 cm−2 of threading dislocations present. In comparison to other reports, we observe a much lower concentration of (BaO2 Ruddlesden-Popper crystallographic shear faults. This suggests that in addition to threading dislocations, other defects—possibly (BaO2 crystallographic shear defects or point defects—significantly reduce the electron mobility.

  5. Growth of high-quality hexagonal InN on 3C-SiC (001) by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Yaguchi, Hiroyuki; Hijikata, Yasuto; Yoshida, Sadafumi; Kitamura, Yoshihiro; Nishida, Kenji; Iwahashi, Yohei

    2005-01-01

    We have grown hexagonal InN (h-InN) films on 3C-SiC (001) substrates by RF-N 2 plasma molecular beam epitaxy taking account of small lattice mismatch between h-InN (10-10) and 3C-SiC (110). It was found from X-ray diffraction (XRD) measurements that h-InN grows with h-InN (0001) vertical stroke vertical stroke 3C-SiC (001) and h-InN (1-100) vertical stroke vertical stroke 3C-SiC (110). XRD measurements also revealed that the h-InN epitaxial layers grown on 3C-SiC (001) are composed of single domain. Strong and sharp photoluminescence from the h-InN was clearly observed at around 0.69 eV. (copyright 2005 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  6. Growth and characterization of metamorphic InAs/GaSb tunnel heterojunction on GaAs by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Jheng-Sin; Clavel, Michael B.; Hudait, Mantu K., E-mail: mantu.hudait@vt.edu [Advanced Devices and Sustainable Energy Laboratory (ADSEL), Bradley Department of Electrical and Computer Engineering, Virginia Tech, Blacksburg, Virginia 24061 (United States); Pandey, Rahul [Electrical Engineering, The Pennsylvania State University, University Park, Pennsylvania 16802 (United States); Datta, Suman [Electrical Engineering, University of Notre Dame, Notre Dame, Indiana 46556 (United States); Meeker, Michael; Khodaparast, Giti A. [Department of Physics, Virginia Tech, Blacksburg, Virginia 24061 (United States)

    2016-06-28

    The structural, morphological, optical, and electrical transport characteristics of a metamorphic, broken-gap InAs/GaSb p-i-n tunnel diode structure, grown by molecular beam epitaxy on GaAs, were demonstrated. Precise shutter sequences were implemented for the strain-balanced InAs/GaSb active layer growth on GaAs, as corroborated by high-resolution X-ray analysis. Cross-sectional transmission electron microscopy and detailed micrograph analysis demonstrated strain relaxation primarily via the formation of 90° Lomer misfit dislocations (MDs) exhibiting a 5.6 nm spacing and intermittent 60° MDs at the GaSb/GaAs heterointerface, which was further supported by a minimal lattice tilt of 180 arc sec observed during X-ray analysis. Selective area diffraction and Fast Fourier Transform patterns confirmed the full relaxation of the GaSb buffer layer and quasi-ideal, strain-balanced InAs/GaSb heteroepitaxy. Temperature-dependent photoluminescence measurements demonstrated the optical band gap of the GaSb layer. Strong optical signal at room temperature from this structure supports a high-quality material synthesis. Current–voltage characteristics of fabricated InAs/GaSb p-i-n tunnel diodes measured at 77 K and 290 K demonstrated two bias-dependent transport mechanisms. The Shockley–Read–Hall generation–recombination mechanism at low bias and band-to-band tunneling transport at high bias confirmed the p-i-n tunnel diode operation. This elucidated the importance of defect control in metamorphic InAs/GaSb tunnel diodes for the implementation of low-voltage and high-performance tunnel field effect transistor applications.

  7. Molecular beam epitaxy for the future

    International Nuclear Information System (INIS)

    Takahashi, K.

    1984-01-01

    Molecular beam epitaxy (MBE) is most commonly used to fabricate super-lattices, high electron mobility transistors, multi-quantum well lasers and other new semiconductor devices by utilizing its excellent controlability. MBE for the future is presumed to include techniques such as metalorganic chemical vapor deposition, photochemical reaction process using gas sources and ion implantation. A report on the crystal growth of GaAs using metalorganics, trimethylgallium and triethylgallium, which are usually used in chemical vapor deposition, as gaseous sources of gallium in an MBE system is made. (Author) [pt

  8. Critical parameters for the molecular beam epitaxial growth of 1.55 μm (Ga,In)(N,As) multiple quantum wells

    International Nuclear Information System (INIS)

    Ishikawa, Fumitaro; Luna, Esperanza; Trampert, Achim; Ploog, Klaus H.

    2006-01-01

    The authors discuss the effect of substrate temperature and As beam equivalent pressure (BEP) on the molecular beam epitaxial growth of (Ga,In)(N,As) multiple quantum wells (MQWs). Transmission electron microscopy studies reveal that a low substrate temperature essentially prevents composition modulations. Secondary ion mass spectrometry results indicate that a low As BEP reduces the incorporation competition of group V elements. The low substrate temperature and low As BEP growth condition leads to (Ga,In)(N,As) MQWs containing more than 4% N preserving good structural and optical properties, and hence demonstrating 1.55 μm photoluminescence emission at room temperature

  9. Highly c-axis oriented growth of GaN film on sapphire (0001 by laser molecular beam epitaxy using HVPE grown GaN bulk target

    Directory of Open Access Journals (Sweden)

    S. S. Kushvaha

    2013-09-01

    Full Text Available Growth temperature dependant surface morphology and crystalline properties of the epitaxial GaN layers grown on pre-nitridated sapphire (0001 substrates by laser molecular beam epitaxy (LMBE were investigated in the range of 500–750 °C. The grown GaN films were characterized using high resolution x-ray diffraction, atomic force microscopy (AFM, micro-Raman spectroscopy, and secondary ion mass spectroscopy (SIMS. The x-ray rocking curve full width at a half maximum (FWHM value for (0002 reflection dramatically decreased from 1582 arc sec to 153 arc sec when the growth temperature was increased from 500 °C to 600 °C and the value further decreased with increase of growth temperature up to 720 °C. A highly c-axis oriented GaN epitaxial film was obtained at 720 °C with a (0002 plane rocking curve FWHM value as low as 102 arc sec. From AFM studies, it is observed that the GaN grain size also increased with increasing growth temperature and flat, large lateral grains of size 200-300 nm was obtained for the film grown at 720 °C. The micro-Raman spectroscopy studies also exhibited the high-quality wurtzite nature of GaN film grown on sapphire at 720 °C. The SIMS measurements revealed a non-traceable amount of background oxygen impurity in the grown GaN films. The results show that the growth temperature strongly influences the surface morphology and crystalline quality of the epitaxial GaN films on sapphire grown by LMBE.

  10. Plasmas for the low-temperature growth of high-quality GaN films by molecular beam epitaxy and remote plasma MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Losurdo, M.; Capezzuto, P.; Bruno, G. [Plasmachemistry Research Center, CNR, Bari (Italy); Namkoong, G.; Doolittle, W.A.; Brown, A.S. [Georgia Inst. of Tech., Atlanta (United States). School of Electrical and Computer Engineering, Microelectronic Research Center

    2002-03-16

    GaN heteroepitaxial growth on sapphire (0001) substrates was carried out by both radio-frequency (rf) remote plasma metalorganic chemical vapor deposition (RP-MOCVD) and molecular beam epitaxy (MBE). A multistep growth process including substrate plasma cleaning and nitridation, buffer growth, its subsequent annealing and epilayer growth was used. In order to achieve a better understanding of the GaN growth, in-situ real time investigation of the surface chemistry is performed for all the steps using the conventional reflection high-energy electron spectroscopy (RHEED) during the MBE process, while laser reflectance interferometry (LRI) and spectroscopic ellipsometry (SE), which do not require UHV conditions, are used for the monitoring of the RP-MOCVD process. The chemistry of the rf N{sub 2} plasma sapphire nitridation and its effect on the epilayer growth and quality are discussed in both MBE and RP-MOCVD. (orig.)

  11. Growth of pseudomorphic structures through organic epitaxy

    International Nuclear Information System (INIS)

    Kaviyil, Sreejith Embekkat; Sassella, Adele; Borghesi, Alessandro; Campione, Marcello; Su Genbo; He Youping; Chen Chenjia

    2012-01-01

    The control of molecular orientation in thin solid film phases of organic semiconductors is a basic factor for the exploitation of their physical properties for optoelectronic devices. We compare structural and optical properties of thin films of the organic semiconductor α-quarterthiophene grown by molecular beam epitaxy on different organic substrates. We show how epitactic interactions, characteristic of the surface of organic crystals, can drive the orientation of the crystalline overlayer and the selection of specific polymorphs and new pseudomorphic phases. We identify a key role in this phenomenon played by the marked groove-like corrugations present in some organic crystal surfaces. Since different polymorphs possess rather different performance in terms of, e.g., charge carrier mobility, this strategy is demonstrated to allow for the growth of oriented phases with enhanced physical properties, while keeping the substrate at room temperature. These results provide useful guidelines for the design of technological substrates for organic epitaxy and they substantiate the adoption of an organic epitaxy approach for the fabrication of optoelectronic devices based on thin films of organic semiconductors.

  12. Investigation of the growth of In2O3 on Y-stabilized ZrO2(100) by oxygen plasma assisted molecular beam epitaxy

    International Nuclear Information System (INIS)

    Bourlange, A.; Payne, D.J.; Palgrave, R.G.; Foord, J.S.; Egdell, R.G.; Jacobs, R.M.J.; Schertel, A.; Hutchison, J.L.; Dobson, P.J.

    2009-01-01

    Thin films of In 2 O 3 have been grown on Y-stabilised ZrO 2 (100) substrates by oxygen plasma assisted molecular beam epitaxy over a range of substrate temperatures between 650 o C and 900 o C. Growth at 650 o C leads to continuous but granular films and complete extinction of substrate core level structure in X-ray photoelectron spectroscopy. However with increasing substrate temperature the films break up into a series of discrete micrometer sized islands. Both the continuous and the island films have excellent epitaxial relationship with the substrate as gauged by X-ray diffraction and selected area electron diffraction and lattice imaging in high resolution transmission electron microscopy.

  13. Nanostructure formation during relatively high temperature growth of Mn-doped GaAs by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Del Río-De Santiago, A.; Méndez-García, V.H. [CIACyT-UASLP, Sierra Leona Av. # 550, Lomas 2a Secc, San Luis Potosí, S.L.P. 78210, México (Mexico); Martínez-Velis, I.; Casallas-Moreno, Y.L. [Physics Department, CINVESTAV-IPN, Apdo. Postal 14470 D. F. México, México (Mexico); López-Luna, E. [CIACyT-UASLP, Sierra Leona Av. # 550, Lomas 2a Secc, San Luis Potosí, S.L.P. 78210, México (Mexico); Yu Gorbatchev, A. [IICO-UASLP, Av. Karakorum 1470, Lomas 4a. Sección, San Luis Potosí, S.L.P. 78210, México (Mexico); López-López, M. [Physics Department, CINVESTAV-IPN, Apdo. Postal 14470 D. F. México, México (Mexico); Cruz-Hernández, E., E-mail: esteban.cruz@uaslp.mx [CIACyT-UASLP, Sierra Leona Av. # 550, Lomas 2a Secc, San Luis Potosí, S.L.P. 78210, México (Mexico)

    2015-04-01

    Highlights: • The formation of different kind of nanostructures in GaMnAs layers depending on Mn concentration at relative HT-MBE is reported. In this Mn% range, it is found the formation of nanogrooves, nanoleaves, and nanowires. • It is shown the progressive photoluminescence transitions from purely GaAsMn zinc blende (for Mn% = 0.01) to a mixture of zinc blende and wurtzite GaAsMn (for Mn% = 0.2). • A critical thickness for the Mn catalyst effect was determined by RHEED. - Abstract: In the present work, we report on molecular beam epitaxy growth of Mn-doped GaAs films at the relatively high temperature (HT) of 530 °C. We found that by increasing the Mn atomic percent, Mn%, from 0.01 to 0.2, the surface morphology of the samples is strongly influenced and changes from planar to corrugated for Mn% values from 0.01 to 0.05, corresponding to nanostructures on the surface with dimensions of 200–300 nm and with the shape of leave, to nanowire-like structures for Mn% values above 0.05. From reflection high-energy electron diffraction patterns, we observed the growth mode transition from two- to three-dimensional occurring at a Mn% exceeding 0.05. The optical and electrical properties were obtained from photoluminescence (PL) and Hall effect measurements, respectively. For the higher Mn concentration, besides the Mn related transitions at approximately 1.41 eV, PL spectra sharp peaks are present between 1.43 and 1.49 eV, which we related to the coexistence of zinc blende and wurtzite phases in the nanowire-like structures of this sample. At Mn% of 0.04, an increase of the carrier mobility up to a value of 1.1 × 10{sup 3} cm{sup 2}/Vs at 77 K was found, then decreases as Mn% is further increased due to the strengthening of the ionized impurity scattering.

  14. Twenty years of molecular beam epitaxy

    Science.gov (United States)

    Cho, A. Y.

    1995-05-01

    The term "molecular beam epitaxy" (MBE) was first used in one of our crystal growth papers in 1970, after having conducted extensive surface physics studies in the late 1960's of the interaction of atomic and molecular beams with solid surfaces. The unique feature of MBE is the ability to prepare single crystal layers with atomic dimensional precision. MBE sets the standard for epitaxial growth and has made possible semiconductor structures that could not be fabricated with either naturally existing materials or by other crystal growth techniques. MBE led the crystal growth technologies when it prepared the first semiconductor quantum well and superlattice structures that gave unexpected and exciting electrical and optical properties. For example, the discovery of the fractional quantized Hall effect. It brought experimental quantum physics to the classroom, and practically all major universities throughout the world are now equipped with MBE systems. The fundamental principles demonstrated by the MBE growth of III-V compound semiconductors have also been applied to the growth of group IV, II-VI, metal, and insulating materials. For manufacturing, the most important criteria are uniformity, precise control of the device structure, and reproducibility. MBE has produced more lasers (3 to 5 million per month for compact disc application) than any other crystal growth technique in the world. New directions for MBE are to incorporate in-situ, real-time monitoring capabilities so that complex structures can be precisely "engineered". In the future, as environmental concerns increase, the use of toxic arsine and phosphine may be limited. Successful use of valved cracker cells for solid arsenic and phosphorus has already produced InP based injection lasers.

  15. Accompanying growth and room-temperature ferromagnetism of η-Mn3N2 thin films by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Yu, Fengmei; Liu, Yajing; Yang, Mei; Wu, Shuxiang; Zhou, Wenqi; Li, Shuwei

    2013-01-01

    η-phase manganese nitride films have been grown on LaAlO 3 (100) and LaSrAlO 4 (001) substrates by using plasma-assisted molecular beam epitaxy. On the basis of reflective high energy electron diffraction, X-ray diffraction, and X-ray photoemission spectroscopy, it is confirmed that two types of η-Mn 3 N 2 with different lattice constants coexist in the films due to the lattice mismatches between the Mn 3 N 2 films and the substrates. Magnetic properties of the films were characterized by a superconducting quantum interference device magnetometer at room temperature. The Mn 3 N 2 films on LaAlO 3 substrate were found to have room-temperature ferromagnetism. Two potential interaction mechanisms are proposed regarding the origin of the observed ferromagnetism. - Highlights: ► The films of two types of η-Mn 3 N 2 have been grown by molecular beam epitaxy. ► Mn 3 N 2 A and Mn 3 N 2 B coexisted in the films on LaAlO 3 and LaSrAlO 4 . ► The room-temperature ferromagnetism of the Mn 3 N 2 films on LaAlO 3 was obtained

  16. Si(001):B gas-source molecular-beam epitaxy: Boron surface segregation and its effect on film growth kinetics

    Energy Technology Data Exchange (ETDEWEB)

    Kim, H.; Glass, G.; Spila, T.; Taylor, N.; Park, S.Y.; Abelson, J.R.; Greene, J.E. [Department of Materials Science, Coordinated Science Laboratory, and Materials Research Laboratory, University of Illinois, 1101 West Springfield, Urbana, Illinois 61801 (United States)

    1997-09-01

    B-doped Si(001) films, with concentrations C{sub B} up to 1.7{times}10{sup 22}cm{sup {minus}3}, were grown by gas-source molecular-beam epitaxy from Si{sub 2}H{sub 6} and B{sub 2}H{sub 6} at T{sub s}=500{endash}800{degree}C. D{sub 2} temperature-programed desorption (TPD) spectra were then used to determine B coverages {theta}{sub B} as a function of C{sub B} and T{sub s}. In these measurements, as-deposited films were flash heated to desorb surface hydrogen, cooled, and exposed to atomic deuterium until saturation coverage. Strong B surface segregation was observed with surface-to-bulk B concentration ratios ranging up to 1200. TPD spectra exhibited {beta}{sub 2} and {beta}{sub 1} peaks associated with dideuteride and monodeuteride desorption as well as lower-temperature B-induced peaks {beta}{sub 2}{sup {asterisk}} and {beta}{sub 1}{sup {asterisk}}. Increasing {theta}{sub B} increased the area under {beta}{sub 2}{sup {asterisk}} and {beta}{sub 1}{sup {asterisk}} at the expense of {beta}{sub 2} and {beta}{sub 1} and decreased the total D coverage {theta}{sub D}. The TPD results were used to determine the B segregation enthalpy, {minus}0.53eV, and to explain and model the effects of high B coverages on Si(001) growth kinetics. Film deposition rates R increase by {ge}50{percent} with increasing C{sub B}{tilde {gt}}1{times}10{sup 19}cm{sup {minus}3} at T{sub s}{le}550{degree}C, due primarily to increased H desorption rates from B-backbonded Si adatoms, and decrease by corresponding amounts at T{sub s}{ge}600{degree}C due to decreased adsorption site densities. At T{sub s}{ge}700{degree}C, high B coverages also induce {l_brace}113{r_brace} facetting. {copyright} {ital 1997 American Institute of Physics.}

  17. Real-time observation of rotational twin formation during molecular-beam epitaxial growth of GaAs on Si (111) by x-ray diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Suzuki, Hidetoshi, E-mail: hsuzuki@cc.miyazaki-u.ac.jp [Faculty of Engineering, University of Miyazaki, 1-1 Gakuen-Kibanadai-Nishi, Miyazaki 889-2192 (Japan); Nakata, Yuka; Takahasi, Masamitu [Graduate School of Materials Science, University of Hyogo, 3-2-1 Koto, Kamigori-cho, Hyogo 678-1297 (Japan); Quantum Beam Science Center, Japan Atomic Energy Agency, 1-1-1 Koto, Sayo-cho, Hyogo 679-5148 (Japan); Ikeda, Kazuma [Toyota Technological Institute, 2-12-1 Hisakata, Tempaku, Nagoya 468-8511 (Japan); Ohshita, Yoshio; Morohara, Osamu; Geka, Hirotaka; Moriyasu, Yoshitaka [Advanced Devices and Sensor Systems Development Center, Asahi Kasei Co. Ltd., 2-1 Samejima, Fuji 416-8501 (Japan)

    2016-03-15

    The formation and evolution of rotational twin (TW) domains introduced by a stacking fault during molecular-beam epitaxial growth of GaAs on Si (111) substrates were studied by in situ x-ray diffraction. To modify the volume ratio of TW to total GaAs domains, GaAs was deposited under high and low group V/group III (V/III) flux ratios. For low V/III, there was less nucleation of TW than normal growth (NG) domains, although the NG and TW growth rates were similar. For high V/III, the NG and TW growth rates varied until a few GaAs monolayers were deposited; the mean TW domain size was smaller for all film thicknesses.

  18. Ge(001):B gas-source molecular beam epitaxy: B surface segregation, hydrogen desorption, and film growth kinetics

    Energy Technology Data Exchange (ETDEWEB)

    Kim, H.; Greene, J.E. [Materials Science Department, the Coordinated Science Laboratory and the Materials Research Laboratory, University of Illinois, Urbana, Illinois 61801 (United States)

    1999-03-01

    Ultrahigh B-doped Ge(001) layers, with concentrations C{sub B} up to 8{times}10{sup 21} cm{sup {minus}3}, were grown by gas-source molecular beam epitaxy from Ge{sub 2}H{sub 6} and B{sub 2}H{sub 6} at temperatures T{sub s}=325{degree}C (in the surface-reaction-limited regime) and 600{degree}C (in the flux-limited regime). The samples were quenched, D site exchanged for H, and D{sub 2} temperature-programed desorption (TPD) used to determine B coverages {theta}{sub B} as a function of C{sub B} and T{sub s} by comparison with B-adsorbed Ge(001) reference samples with known {theta}{sub B} values. During Ge(001):B film growth, strong surface B segregation to the second layer was observed with surface-to-bulk B concentration ratios ranging up to 6000. The TPD spectra exhibited {alpha}{sub 2} and {alpha}{sub 1} peaks associated with dideuteride and monodeuteride desorption as well as lower-temperature B-induced {alpha}{sub 2}{sup {asterisk}} and {alpha}{sub 1}{sup {asterisk}} peaks associated with deuterium desorption from Ge{sup {asterisk}} surface atoms with B backbonds. Increasing {theta}{sub B} expanded the area under {alpha}{sub 2}{sup {asterisk}} and {alpha}{sub 1}{sup {asterisk}} at the expense of {alpha}{sub 2} and {alpha}{sub 1} and decreased the total D coverage {theta}{sub D}. The TPD results were used to determine the B segregation enthalpy, {minus}0.64 eV, and to explain and model the effects of high B coverages on Ge(001) growth kinetics. At T{sub s}=325{degree}C, where B segregation is kinetically hindered, film deposition rates R{sub Ge} are not a strong function of C{sub B}, exhibiting only a small decrease at C{sub B}{approx_gt}5{times}10{sup 18} cm{sup {minus}3}. However, at T{sub s}=600{degree}C, R{sub Ge} decreases by up to 40{percent} with increasing C{sub B}{approx_gt}1{times}10{sup 18} cm{sup {minus}3}. This is due primarily to the combination of B-induced Ge dimer vacancies and the deactivation of surface dangling bonds caused by charge transfer

  19. Selective-area growth of GaN nanowires on SiO{sub 2}-masked Si (111) substrates by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Kruse, J. E.; Doundoulakis, G. [Department of Physics, University of Crete, P. O. Box 2208, 71003 Heraklion (Greece); Institute of Electronic Structure and Laser, Foundation for Research and Technology–Hellas, N. Plastira 100, 70013 Heraklion (Greece); Lymperakis, L. [Max-Planck-Institut für Eisenforschung, Max-Planck-Straße 1, 40237 Düsseldorf (Germany); Eftychis, S.; Georgakilas, A., E-mail: alexandr@physics.uoc.gr [Department of Physics, University of Crete, P. O. Box 2208, 71003 Heraklion (Greece); Adikimenakis, A.; Tsagaraki, K.; Androulidaki, M.; Konstantinidis, G. [Institute of Electronic Structure and Laser, Foundation for Research and Technology–Hellas, N. Plastira 100, 70013 Heraklion (Greece); Olziersky, A.; Dimitrakis, P.; Ioannou-Sougleridis, V.; Normand, P. [Institute of Nanoscience and Nanotechnology, NCSR Demokritos, Patriarchou Grigoriou and Neapoleos 27, 15310 Aghia Paraskevi, Athens (Greece); Koukoula, T.; Kehagias, Th.; Komninou, Ph. [Department of Physics, Aristotle University of Thessaloniki, 54124 Thessaloniki (Greece)

    2016-06-14

    We analyze a method to selectively grow straight, vertical gallium nitride nanowires by plasma-assisted molecular beam epitaxy (MBE) at sites specified by a silicon oxide mask, which is thermally grown on silicon (111) substrates and patterned by electron-beam lithography and reactive-ion etching. The investigated method requires only one single molecular beam epitaxy MBE growth process, i.e., the SiO{sub 2} mask is formed on silicon instead of on a previously grown GaN or AlN buffer layer. We present a systematic and analytical study involving various mask patterns, characterization by scanning electron microscopy, transmission electron microscopy, and photoluminescence spectroscopy, as well as numerical simulations, to evaluate how the dimensions (window diameter and spacing) of the mask affect the distribution of the nanowires, their morphology, and alignment, as well as their photonic properties. Capabilities and limitations for this method of selective-area growth of nanowires have been identified. A window diameter less than 50 nm and a window spacing larger than 500 nm can provide single nanowire nucleation in nearly all mask windows. The results are consistent with a Ga diffusion length on the silicon dioxide surface in the order of approximately 1 μm.

  20. Systematic study of influence of growth parameters on island morphology during molecular beam epitaxy growth: A Monte Carlo study

    International Nuclear Information System (INIS)

    Shankar Prasad Shrestha; Park, C.-Y.

    2006-05-01

    We have made a systematic study of influence of diffusion flux ratio (D/F), diffusional anisotropy (DA) and sticking anisotropy (SA) on island morphology to show the influence of each growth parameter on island morphology in presence of the other growth parameters. Our results show that the influence of D/F ratio and DA on island morphology depends on the sticking anisotropy of the adatoms. At the intermediate anisotropic case, increase in D/F ratio results in transition of the island morphology from 1d nature to 2 d nature. In anisotropic diffusion case, D/F ratio can change the growth direction of the island morphology. We also find that only sticking anisotropy is not sufficient to produce elongated islands, low D/F ratio is also essential. (author)

  1. Molecular beam epitaxy applications to key materials

    CERN Document Server

    Farrow, Robin F C

    1995-01-01

    In this volume, the editor and contributors describe the use of molecular beam epitaxy (MBE) for a range of key materials systems that are of interest for both technological and fundamental reasons. Prior books on MBE have provided an introduction to the basic concepts and techniques of MBE and emphasize growth and characterization of GaAs-based structures. The aim in this book is somewhat different; it is to demonstrate the versatility of the technique by showing how it can be utilized to prepare and explore a range of distinct and diverse materials. For each of these materials systems MBE has played a key role both in their development and application to devices.

  2. Impact of growth and annealing conditions on the parameters of Ge/Si(001) relaxed layers grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Yurasov, D. V., E-mail: Inquisitor@ipm.sci-nnov.ru [Russian Academy of Sciences, Institute for Physics of Microstructures (Russian Federation); Bobrov, A. I. [Lobachevsky State University of Nizhny Novgorod (Russian Federation); Daniltsev, V. M.; Novikov, A. V. [Russian Academy of Sciences, Institute for Physics of Microstructures (Russian Federation); Pavlov, D. A. [Lobachevsky State University of Nizhny Novgorod (Russian Federation); Skorokhodov, E. V.; Shaleev, M. V.; Yunin, P. A. [Russian Academy of Sciences, Institute for Physics of Microstructures (Russian Federation)

    2015-11-15

    Influence of the Ge layer thickness and annealing conditions on the parameters of relaxed Ge/Si(001) layers grown by molecular beam epitaxy via two-stage growth is investigated. The dependences of the threading dislocation density and surface roughness on the Ge layer thickness, annealing temperature and time, and the presence of a hydrogen atmosphere are obtained. As a result of optimization of the growth and annealing conditions, relaxed Ge/Si(001) layers which are thinner than 1 μm with a low threading dislocation density on the order of 10{sup 7} cm{sup –2} and a root mean square roughness of less than 1 nm are obtained.

  3. Growth of strained InGaAs/GaAs quantum wells and index guided injection lasers over nonplanar substrates by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Arent, D.J.; Galeuchet, Y.D.; Nilsson, S.; Meier, H.P.

    1990-01-01

    Strained InGaAs/GaAs quantum wells were grown on nonplanar substrates by molecular beam epitaxy and studied by scanning electron microscopy and low temperature spatially and spectrally resolved cathodoluminescence spectroscopy. For (100) ridges and grooves formed with (311)A sidewalls, almost complete removal of In from the strained quantum wells on the (311)A facet is observed. Corresponding increases of In content in the quantum wells grown on the (100) facets indicate that most if not all of the In is displaced from the (311)A facet via interplanar adatom migration. Ga adatom migration is also observed under our growth conditions such that quantum wells grown nominally near the critical layer thickness on structures less than ≅2.5 μm wide are no longer pseudomorphically strained, as detected by luminescence linewidth analysis. We present the first results of strained InGaAs/GaAs index guided injection lasers grown by single-step molecular beam epitaxy over nonplanar substrates and show that differences greater than 50 meV in the effective band gap of a 70 A quantum well can be achieved between the gain region and the nonabsorbing waveguide without relaxing the strain. Room temperature threshold currents as low as 6 mA for 4 μmx750 μm uncoated devices lasing continuously at a wavelength of 1.01 μm have been achieved

  4. Influence of growth conditions and surface reaction byproducts on GaN grown via metal organic molecular beam epitaxy: Toward an understanding of surface reaction chemistry

    Science.gov (United States)

    Pritchett, David; Henderson, Walter; Burnham, Shawn D.; Doolittle, W. Alan

    2006-04-01

    The surface reaction byproducts during the growth of GaN films via metal organic molecular beam epitaxy (MOMBE) were investigated as a means to optimize material properties. Ethylene and ethane were identified as the dominant surface reaction hydrocarbon byproducts, averaging 27.63% and 7.15% of the total gas content present during growth. Intense ultraviolet (UV) photoexcitation during growth was found to significantly increase the abundance of ethylene and ethane while reducing the presence of H2 and N2. At 920°C, UV excitation was shown to enhance growth rate and crystalline quality while reducing carbon incorporation. Over a limited growth condition range, a 4.5×1019-3.4×1020 cm-3 variation in carbon incorporation was achieved at constant high vacuum. Coupled with growth rate gains, UV excitation yielded films with ˜58% less integrated carbon content. Structural material property variations are reported for various ammonia flows and growth temperatures. The results suggest that high carbon incorporation can be achieved and regulated during MOMBE growth and that in-situ optimization through hydrocarbon analysis may provide further enhancement in the allowable carbon concentration range.

  5. Molecular beam epitaxy growth of [CrGe/MnGe/FeGe] superlattices: Toward artificial B20 skyrmion materials with tunable interactions

    Science.gov (United States)

    Ahmed, Adam S.; Esser, Bryan D.; Rowland, James; McComb, David W.; Kawakami, Roland K.

    2017-06-01

    Skyrmions are localized magnetic spin textures whose stability has been shown theoretically to depend on material parameters including bulk Dresselhaus spin orbit coupling (SOC), interfacial Rashba SOC, and magnetic anisotropy. Here, we establish the growth of a new class of artificial skyrmion materials, namely B20 superlattices, where these parameters could be systematically tuned. Specifically, we report the successful growth of B20 superlattices comprised of single crystal thin films of FeGe, MnGe, and CrGe on Si(1 1 1) substrates. Thin films and superlattices are grown by molecular beam epitaxy and are characterized through a combination of reflection high energy electron diffraction, X-ray diffraction, and cross-sectional scanning transmission electron microscopy (STEM). X-ray energy dispersive spectroscopy (XEDS) distinguishes layers by elemental mapping and indicates good interface quality with relatively low levels of intermixing in the [CrGe/MnGe/FeGe] superlattice. This demonstration of epitaxial, single-crystalline B20 superlattices is a significant advance toward tunable skyrmion systems for fundamental scientific studies and applications in magnetic storage and logic.

  6. Molecular beam epitaxy of graphene on mica

    International Nuclear Information System (INIS)

    Lippert, G.; Dabrowski, J.; Yamamoto, Y.; Mehr, W.; Lupina, G.; Herziger, F.; Maultzsch, J.; Baringhaus, J.; Tegenkamp, C.; Lemme, M.C.

    2012-01-01

    Realization of graphene devices is often hindered by the fact that the known layer growth methods do not meet the requirements of the device fabrication in silicon mainstream technology. For example, the relatively straightforward method of decomposition of hexagonal SiC is not CMOS-compatible due to the high-thermal budget it requires [Moon et al., IEEE Electron Device Lett. 31, 260 (2010)]. Techniques based on layer transfer are restricted because of the uncertainty of residual metal contaminants, particles, and structural defects. Of interest is thus a method that would allow one to grow a graphene film directly in the device area where graphene is needed. Production of large area graphene is not necessarily required in this case, but high quality of the film and metal-free growth on an insulating substrate at temperatures below 1000 C are important requirements. We demonstrate direct growth of defect-free graphene on insulators at moderate temperatures by molecular beam epitaxy. The quality of the graphene was probed by high-resolution Raman spectroscopy, indicating a negligible density of defects. The spectra are compared with those from graphene flakes mechanically exfoliated from native graphite onto mica. These results are combined with insights from density functional theory calculations. A model of graphene growth on mica and similar substrates is proposed. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  7. Growth and characterization of β-Ga2O3 thin films by molecular beam epitaxy for deep-UV photodetectors

    Science.gov (United States)

    Ghose, Susmita; Rahman, Shafiqur; Hong, Liang; Rojas-Ramirez, Juan Salvador; Jin, Hanbyul; Park, Kibog; Klie, Robert; Droopad, Ravi

    2017-09-01

    The growth of high quality epitaxial beta-gallium oxide (β-Ga2O3) using a compound source by molecular beam epitaxy has been demonstrated on c-plane sapphire (Al2O3) substrates. The compound source provides oxidized gallium molecules in addition to oxygen when heated from an iridium crucible in a high temperature effusion cell enabling a lower heat of formation for the growth of Ga2O3, resulting in a more efficient growth process. This source also enabled the growth of crystalline β-Ga2O3 without the need for additional oxygen. The influence of the substrate temperatures on the crystal structure and quality, chemical bonding, surface morphology, and optical properties has been systematically evaluated by x-ray diffraction, scanning transmission electron microscopy, x-ray photoelectron spectroscopy, atomic force microscopy, spectroscopic ellipsometry, and UV-vis spectroscopy. Under optimized growth conditions, all films exhibited pure (" separators="|2 ¯01 ) oriented β-Ga2O3 thin films with six-fold rotational symmetry when grown on a sapphire substrate. The thin films demonstrated significant absorption in the deep-ultraviolet (UV) region with an optical bandgap around 5.0 eV and a refractive index of 1.9. A deep-UV photodetector fabricated on the high quality β-Ga2O3 thin film exhibits high resistance and small dark current (4.25 nA) with expected photoresponse for 254 nm UV light irradiation suggesting that the material grown using the compound source is a potential candidate for deep-ultraviolet photodetectors.

  8. Epitaxial growth of silicon for layer transfer

    Science.gov (United States)

    Teplin, Charles; Branz, Howard M

    2015-03-24

    Methods of preparing a thin crystalline silicon film for transfer and devices utilizing a transferred crystalline silicon film are disclosed. The methods include preparing a silicon growth substrate which has an interface defining substance associated with an exterior surface. The methods further include depositing an epitaxial layer of silicon on the silicon growth substrate at the surface and separating the epitaxial layer from the substrate substantially along the plane or other surface defined by the interface defining substance. The epitaxial layer may be utilized as a thin film of crystalline silicon in any type of semiconductor device which requires a crystalline silicon layer. In use, the epitaxial transfer layer may be associated with a secondary substrate.

  9. Molecular-beam epitaxial growth of insulating AlN on surface-controlled 6H-SiC substrate by HCl gas etching

    International Nuclear Information System (INIS)

    Onojima, Norio; Suda, Jun; Matsunami, Hiroyuki

    2002-01-01

    Insulating AlN layers were grown on surface-controlled 6H-SiC subtrates by molecular-beam epitaxy (MBE) using elemental Al and rf plasma-excited nitrogen (N*). HCl gas etching was introduced as an effective pretreatment method of substrate for MBE growth of AlN. 6H-SiC substrates pretreated by HCl gas etching had no surface polishing scratches and an atomically flat surface. In addition, evident ( 3 √x 3 √)R30 deg. surface reconstruction was observed even before thermal cleaning. AlN layers grown on this substrate had no defects related to surface polishing scratches and excellent insulating characteristics

  10. Reflectance-anisotropy study of the dynamics of molecular beam epitaxy growth of GaAs and InGaAs on GaAs(001)

    Energy Technology Data Exchange (ETDEWEB)

    Ortega-Gallegos, J.; Lastras-Martinez, A.; Lastras-Martinez, L.F. [Instituto de Investigacion en Comunicacion Optica, Universidad Autonoma de San Luis Potosi. Alvaro Obregon 64, San Luis Potosi (Mexico); Balderas-Navarro, R.E. [Instituto de Investigacion en Comunicacion Optica, Universidad Autonoma de San Luis Potosi. Alvaro Obregon 64, San Luis Potosi (Mexico); Facultad de Ciencias, Universidad Autonoma de San Luis Potosi. Alvaro Obregon 64, San Luis Potosi (Mexico)

    2008-07-01

    Reflectance-Anisotropy (RA) observations during the Molecular Beam Epitaxy (MBE) growth of zincblende semiconductors films were carried out using the E{sub 1} optical transition as a probe. We follow the kinetics of the deposition of GaAs and In{sub 0.3}Ga{sub 0.7}As on GaAs(001) at growth rates of 0.2 and 0.25 ML/s, respectively. During growth we used a constant As{sub 4} or As{sub 2} flux pressure of 5 x 10{sup -6} Torr. Clear RA-oscillations were observed during growth with a period that nearly coincides with the growth period for a Ga-As bilayer. RHEED was used as an auxiliary technique in order to obtain a correlation between RHEED and RA oscillations. On the basis of our results, we argue that RAS oscillations are mainly associated to periodic changes in surface atomic structure. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  11. Growth-temperature- and thermal-anneal-induced crystalline reorientation of aluminum on GaAs (100) grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Liu, H. F.; Chua, S. J.; Xiang, N.

    2007-01-01

    The authors investigated the growth of Al thin films on GaAs (100) substrates by molecular beam epitaxy. It is found that the growth at 550 degree sign C results in a texture that consists of (100)Al[010](parallel sign)(100)GaAs[011] and (100)Al[010](parallel sign)(100)GaAs[010] rotated 45 degree sign with respect to each other, while the growth at 300 degree sign C leads to a mixture phase of (100)Al[010](parallel sign)(100)GaAs[011] and (110)Al[001](parallel sign)(100)GaAs[011]. In situ annealing of the Al film grown at 300 degree sign C causes a reorientation of the crystalline from (100)Al[010](parallel sign)(100)GaAs[011] to (110)Al[001](parallel sign)(100)GaAs[011]. The grain sizes of the Al film are increased by the increased growth temperature and in situ annealing; the ratio of the exposed to the covered surface is not changed significantly by changing the growth temperature but decreased by annealing; and the small islands in between the large ones are removed by annealing. These observations are explained based on island migration and coalescence

  12. High-Temperature Growth of GaN and Al x Ga1- x N via Ammonia-Based Metalorganic Molecular-Beam Epitaxy

    Science.gov (United States)

    Billingsley, Daniel; Henderson, Walter; Doolittle, W. Alan

    2010-05-01

    The effect of high-temperature growth on the crystalline quality and surface morphology of GaN and Al x Ga1- x N grown by ammonia-based metalorganic molecular-beam epitaxy (NH3-MOMBE) has been investigated as a means of producing atomically smooth films suitable for device structures. The effects of V/III ratio on the growth rate and surface morphology are described herein. The crystalline quality of both GaN and AlGaN was found to mimic that of the GaN templates, with (002) x-ray diffraction (XRD) full-widths at half- maximum (FWHMs) of ~350 arcsec. Nitrogen-rich growth conditions have been found to provide optimal surface morphologies with a root-mean-square (RMS) roughness of ~0.8 nm, yet excessive N-rich environments have been found to reduce the growth rate and result in the formation of faceted surface pitting. AlGaN exhibits a decreased growth rate, as compared with GaN, due to increased N recombination as a result of the increased pyrolysis of NH3 in the presence of Al. AlGaN films grown directly on GaN templates exhibited Pendellösung x-ray fringes, indicating an abrupt interface and a planar AlGaN film. AlGaN films grown for this study resulted in an optimal RMS roughness of ~0.85 nm with visible atomic steps.

  13. Reflectance-anisotropy study of the dynamics of molecular beam epitaxy growth of GaAs and InGaAs on GaAs(001)

    International Nuclear Information System (INIS)

    Ortega-Gallegos, J.; Lastras-Martinez, A.; Lastras-Martinez, L.F.; Balderas-Navarro, R.E.

    2008-01-01

    Reflectance-Anisotropy (RA) observations during the Molecular Beam Epitaxy (MBE) growth of zincblende semiconductors films were carried out using the E 1 optical transition as a probe. We follow the kinetics of the deposition of GaAs and In 0.3 Ga 0.7 As on GaAs(001) at growth rates of 0.2 and 0.25 ML/s, respectively. During growth we used a constant As 4 or As 2 flux pressure of 5 x 10 -6 Torr. Clear RA-oscillations were observed during growth with a period that nearly coincides with the growth period for a Ga-As bilayer. RHEED was used as an auxiliary technique in order to obtain a correlation between RHEED and RA oscillations. On the basis of our results, we argue that RAS oscillations are mainly associated to periodic changes in surface atomic structure. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  14. Optical Epitaxial Growth of Gold Nanoparticle Arrays.

    Science.gov (United States)

    Huang, Ningfeng; Martínez, Luis Javier; Jaquay, Eric; Nakano, Aiichiro; Povinelli, Michelle L

    2015-09-09

    We use an optical analogue of epitaxial growth to assemble gold nanoparticles into 2D arrays. Particles are attracted to a growth template via optical forces and interact through optical binding. Competition between effects determines the final particle arrangements. We use a Monte Carlo model to design a template that favors growth of hexagonal particle arrays. We experimentally demonstrate growth of a highly stable array of 50 gold particles with 200 nm diameter, spaced by 1.1 μm.

  15. Epitaxial growth mechanisms of graphene and effects of substrates

    OpenAIRE

    Özçelik, V. Ongun; Cahangirov, S.; Ciraci, S.

    2012-01-01

    The growth process of single layer graphene with and without substrate is investigated using ab initio, finite temperature molecular dynamic calculations within density functional theory. An understanding of the epitaxial graphene growth mechanisms in the atomic level is provided by exploring the transient stages which occur at the growing edges of graphene. These stages are formation and collapse of large carbon rings together with the formation and healing of Stone-Wales like pentagon-hepta...

  16. Buffer-layer enhanced crystal growth of BaB6 (1 0 0) thin films on MgO (1 0 0) substrates by laser molecular beam epitaxy

    International Nuclear Information System (INIS)

    Kato, Yushi; Yamauchi, Ryosuke; Arai, Hideki; Tan, Geng; Tsuchimine, Nobuo; Kobayashi, Susumu; Saeki, Kazuhiko; Takezawa, Nobutaka; Mitsuhashi, Masahiko; Kaneko, Satoru; Yoshimoto, Mamoru

    2012-01-01

    Crystalline BaB 6 (1 0 0) thin films can be fabricated on MgO (1 0 0) substrates by inserting a 2-3 nm-thick epitaxial SrB 6 (1 0 0) buffer layer by pulsed laser deposition (PLD) in ultra-high vacuum (i.e., laser molecular beam epitaxy). Reflection high-energy electron diffraction and X-ray diffraction measurements indicated the heteroepitaxial structure of BaB 6 (1 0 0)/SrB 6 (1 0 0)/MgO (1 0 0) with the single domain of the epitaxial relationship. Conversely, BaB 6 thin films without the buffer layer were not epitaxial instead they developed as polycrystalline films with a random in-plane configuration and some impurity phases. As a result, the buffer layer is considered to greatly affect the initial growth of epitaxial BaB 6 thin films; therefore, in this study, buffering effects have been discussed. From the conventional four-probe measurement, it was observed that BaB 6 epitaxial thin films exhibit n-type semiconducting behavior with a resistivity of 2.90 × 10 -1 Ω cm at room temperature.

  17. Effect of the growth temperature and the AlN mole fraction on In incorporation and properties of quaternary III-nitride layers grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Fernandez-Garrido, S.; Pereiro, J.; Munoz, E.; Calleja, E.; Redondo-Cubero, A.; Gago, R.; Bertram, F.; Christen, J.; Luna, E.; Trampert, A.

    2008-01-01

    Indium incorporation into wurtzite (0001)-oriented In x Al y Ga 1-x-y N layers grown by plasma-assisted molecular beam epitaxy was studied as a function of the growth temperature (565-635 deg. C) and the AlN mole fraction (0.01< y<0.27). The layer stoichiometry was determined by Rutherford backscattering spectrometry (RBS). RBS shows that indium incorporation decreased continuously with increasing growth temperature due to thermally enhanced dissociation of In-N bonds and for increasing AlN mole fractions. High resolution x-ray diffraction and transmission electron microscopy (TEM) measurements did not show evidence of phase separation. The mosaicity of the quaternary layers was found to be mainly determined by the growth temperature and independent on alloy composition within the range studied. However, depending on the AlN mole fraction, nanometer-sized composition fluctuations were detected by TEM. Photoluminescence spectra showed a single broad emission at room temperature, with energy and bandwidth S- and W-shaped temperature dependences typical of exciton localization by alloy inhomogeneities. Cathodoluminescence measurements demonstrated that the alloy inhomogeneities, responsible of exciton localization, occur on a lateral length scale below 150 nm, which is corroborated by TEM

  18. Epitaxial growth of rhenium with sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Oh, Seongshik [National Institute of Standards and Technology, Boulder, CO 80305 (United States) and Department of Physics, University of Illinois, Urbana, IL 61801 (United States)]. E-mail: soh@boulder.nist.gov; Hite, Dustin A. [National Institute of Standards and Technology, Boulder, CO 80305 (United States); Cicak, K. [National Institute of Standards and Technology, Boulder, CO 80305 (United States); Osborn, Kevin D. [National Institute of Standards and Technology, Boulder, CO 80305 (United States); Simmonds, Raymond W. [National Institute of Standards and Technology, Boulder, CO 80305 (United States); McDermott, Robert [University of California, Santa Barbara, CA 93106 (United States); Cooper, Ken B. [University of California, Santa Barbara, CA 93106 (United States); Steffen, Matthias [University of California, Santa Barbara, CA 93106 (United States); Martinis, John M. [University of California, Santa Barbara, CA 93106 (United States); Pappas, David P. [National Institute of Standards and Technology, Boulder, CO 80305 (United States)

    2006-02-21

    We have grown epitaxial Rhenium (Re) (0001) films on {alpha}-Al{sub 2}O{sub 3} (0001) substrates using sputter deposition in an ultra high vacuum system. We find that better epitaxy is achieved with DC rather than with RF sputtering. With DC sputtering, epitaxy is obtained with the substrate temperatures above 700 deg. C and deposition rates below 0.1 nm/s. The epitaxial Re films are typically composed of terraced hexagonal islands with screw dislocations, and island size gets larger with high temperature post-deposition annealing. The growth starts in a three dimensional mode but transforms into two dimensional mode as the film gets thicker. With a thin ({approx}2 nm) seed layer deposited at room temperature and annealed at a high temperature, the initial three dimensional growth can be suppressed. This results in larger islands when a thick film is grown at 850 deg. C on the seed layer. We also find that when a room temperature deposited Re film is annealed to higher temperatures, epitaxial features start to show up above {approx}600 deg. C, but the film tends to be disordered.

  19. Epitaxial growth of CZT(S,Se) on silicon

    Science.gov (United States)

    Bojarczuk, Nestor A.; Gershon, Talia S.; Guha, Supratik; Shin, Byungha; Zhu, Yu

    2016-03-15

    Techniques for epitaxial growth of CZT(S,Se) materials on Si are provided. In one aspect, a method of forming an epitaxial kesterite material is provided which includes the steps of: selecting a Si substrate based on a crystallographic orientation of the Si substrate; forming an epitaxial oxide interlayer on the Si substrate to enhance wettability of the epitaxial kesterite material on the Si substrate, wherein the epitaxial oxide interlayer is formed from a material that is lattice-matched to Si; and forming the epitaxial kesterite material on a side of the epitaxial oxide interlayer opposite the Si substrate, wherein the epitaxial kesterite material includes Cu, Zn, Sn, and at least one of S and Se, and wherein a crystallographic orientation of the epitaxial kesterite material is based on the crystallographic orientation of the Si substrate. A method of forming an epitaxial kesterite-based photovoltaic device and an epitaxial kesterite-based device are also provided.

  20. Self-Catalyzed Growth of Axial GaAs/GaAsSb Nanowires by Molecular Beam Epitaxy for Photodetectors

    Science.gov (United States)

    2015-06-01

    MOVPE Metal organic vapor phase epitaxy NCA Nano Channel Aluminum NW Nanowire PL Photoluminescence PMMA Poly methyl methacrylate...GaAs (111) B substrate. The NWs were grown using a nanochannel alumina ( NCA ) template. It was later shown by Dubrovskii et al. [16], that the NWs... cathode gun. The type of signals produced are secondary electron (SE), back scattered electron (BSE), characteristic X- rays, specimen current and

  1. Impact of P/In flux ratio and epilayer thickness on faceting for nanoscale selective area growth of InP by molecular beam epitaxy.

    Science.gov (United States)

    Fahed, M; Desplanque, L; Coinon, C; Troadec, D; Wallart, X

    2015-07-24

    The impact of the P/In flux ratio and the deposited thickness on the faceting of InP nanostructures selectively grown by molecular beam epitaxy (MBE) is reported. Homoepitaxial growth of InP is performed inside 200 nm wide stripe openings oriented either along a [110] or [1-10] azimuth in a 10 nm thick SiO2 film deposited on an InP(001) substrate. When varying the P/In flux ratio, no major shape differences are observed for [1-10]-oriented apertures. On the other hand, the InP nanostructure cross sections strongly evolve for [110]-oriented apertures for which (111)B facets are more prominent and (001) ones shrink for large P/In flux ratio values. These results show that the growth conditions allow tailoring the nanocrystal shape. They are discussed in the framework of the equilibrium crystal shape model using existing theoretical calculations of the surface energies of different low-index InP surfaces as a function of the phosphorus chemical potential, directly related to the P/In ratio. Experimental observations strongly suggest that the relative (111)A surface energy is probably smaller than the calculated value. We also discuss the evolution of the nanostructure shape with the InP-deposited thickness.

  2. Molecular beam epitaxial growth of oriented and uniform Ge{sub 2}Sb{sub 2}Te{sub 5} nanoparticles with compact dimensions

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Beining; Sun, Yu; Wu, Jie; Yuan, Long; Wu, Xiaofeng; Huang, Keke; Feng, Shouhua, E-mail: shfeng@jlu.edu.cn [Jilin University, State Key Laboratory of Inorganic Synthesis and Preparative Chemistry, College of Chemistry (China)

    2017-02-15

    The scaling-down of phase change memory cell is critical to achieve high-performance and high-density memory devices. Herein, we report that Ge{sub 2}Sb{sub 2}Te{sub 5} nanoparticles along the [1 1 1] direction were synthesized without templates or etching in a molecular beam epitaxy system. Under non-stoichiometric Ge:Sb:Te beam ratio condition, the growth of high-density Ge{sub 2}Sb{sub 2}Te{sub 5} nanoparticles was achieved by Zn-doping. The average diameter of the nanoparticles is 8 nm, and the full width at half maximum of the size distribution is 2.7 nm. Our results suggest that the size and shape modifications of Ge{sub 2}Sb{sub 2}Te{sub 5} nanoparticles could be induced by Zn-doping which influences the nucleation in the growth process. In addition, the bonding states of Zn and Te verified by X-ray photoelectron spectroscopy proved that Zn atoms located in the Ge{sub 2}Sb{sub 2}Te{sub 5} matrix. This approach exemplified here can be applied to the sub-20 nm phase change memory devices and may also be extendable to be served in the design and development of more materials with phase transitions.

  3. InGaN nanocolumn growth self-induced by in-situ annealing and ion irradiation during growth process with molecular beam epitaxy method

    Science.gov (United States)

    Xue, Junjun; Cai, Qing; Zhang, Baohua; Ge, Mei; Chen, Dunjun; Zheng, Jianguo; Zhi, Ting; Tao, Zhikuo; Chen, Jiangwei; Wang, Lianhui; Zhang, Rong; Zheng, Youdou

    2017-11-01

    Incubation and shape transition are considered as two essential processes for nucleating of self-assembly InGaN nanocolumns (NCs) in traditional way. We propose a new approach for nuclei forming directly by in-situ annealing and ion irradiating the InGaN template during growing process. The nanoislands, considered as the nuclei of NCs, were formed by a combinational effect of thermal and ion etching (TIE), which made the gaps of the V-pits deeper and wider. On account of the decomposition of InGaN during TIE process, more nitride-rich amorphous alloys would intent to accumulate in the corroded V-pits. The amorphous alloys played a key role to promote the following growth from 2D regime into Volmer-Weber growth regime so that the NC morphology took place, rather than a compact film. As growth continued, the subsequently epitaxial InGaN alloys on the annealed NC nuclei were suffered in biaxial compressive stress for losing part of indium content from the NC nuclei during the TIE process. Strain relaxation, accompanied by thread dislocations, came up and made the lattice planes misoriented, which prevented the NCs from coalescence into a compact film at later period of growing.

  4. A modified gradient approach for the growth of low-density InAs quantum dot molecules by molecular beam epitaxy

    Science.gov (United States)

    Sharma, Nandlal; Reuter, Dirk

    2017-11-01

    Two vertically stacked quantum dots that are electronically coupled, so called quantum dot molecules, are of great interest for the realization of solid state building blocks for quantum communication networks. We present a modified gradient approach to realize InAs quantum dot molecules with a low areal density so that single quantum dot molecules can be optically addressed. The individual quantum dot layers were prepared by solid source molecular beam epitaxy depositing InAs on GaAs(100). The bottom quantum dot layer has been grown without substrate rotation resulting in an In-gradient across the surface, which translated into a density gradient with low quantum dot density in a certain region of the wafer. For the top quantum dot layer, separated from the bottom quantum dot layer by a 6 nm thick GaAs barrier, various InAs amounts were deposited without an In-gradient. In spite of the absence of an In-gradient, a pronounced density gradient is observed for the top quantum dots. Even for an In-amount slightly below the critical thickness for a single dot layer, a density gradient in the top quantum dot layer, which seems to reproduce the density gradient in the bottom layer, is observed. For more or less In, respectively, deviations from this behavior occur. We suggest that the obvious influence of the bottom quantum dot layer on the growth of the top quantum dots is due to the strain field induced by the buried dots.

  5. Direct observation of strain in InAs quantum dots and cap layer during molecular beam epitaxial growth using in situ X-ray diffraction

    International Nuclear Information System (INIS)

    Shimomura, Kenichi; Ohshita, Yoshio; Kamiya, Itaru; Suzuki, Hidetoshi; Sasaki, Takuo; Takahasi, Masamitu

    2015-01-01

    Direct measurements on the growth of InAs quantum dots (QDs) and various cap layers during molecular beam epitaxy are performed by in situ X-ray diffraction (XRD). The evolution of strain induced both in the QDs and cap layers during capping is discussed based on the XRD intensity transients obtained at various lattice constants. Transients with different features are observed from those obtained during InGaAs and GaAs capping. The difference observed is attributed to In-Ga intermixing between the QDs and the cap layer under limited supply of In. Photoluminescence (PL) wavelength can be tuned by controlling the intermixing, which affects both the strain induced in the QDs and the barrier heights. The PL wavelength also varies with the cap layer thickness. A large redshift occurs by reducing the cap thickness. The in situ XRD observation reveals that this is a result of reduced strain. We demonstrate how such information about strain can be applied for designing and preparing novel device structures

  6. Direct observation of strain in InAs quantum dots and cap layer during molecular beam epitaxial growth using in situ X-ray diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Shimomura, Kenichi; Ohshita, Yoshio; Kamiya, Itaru, E-mail: kamiya@toyota-ti.ac.jp [Toyota Technological Institute, 2-12-1 Hisakata, Tempaku, Nagoya 468-8511 (Japan); Suzuki, Hidetoshi [Faculty of Engineering, University of Miyazaki, 1-1 Gakuen Kibanadai-nishi, Miyazaki 889-2192 (Japan); Sasaki, Takuo; Takahasi, Masamitu [Quantum Beam Science Center, Japan Atomic Energy Agency, Koto 1-1-1, Sayo-cho, Hyogo 679-5148 (Japan)

    2015-11-14

    Direct measurements on the growth of InAs quantum dots (QDs) and various cap layers during molecular beam epitaxy are performed by in situ X-ray diffraction (XRD). The evolution of strain induced both in the QDs and cap layers during capping is discussed based on the XRD intensity transients obtained at various lattice constants. Transients with different features are observed from those obtained during InGaAs and GaAs capping. The difference observed is attributed to In-Ga intermixing between the QDs and the cap layer under limited supply of In. Photoluminescence (PL) wavelength can be tuned by controlling the intermixing, which affects both the strain induced in the QDs and the barrier heights. The PL wavelength also varies with the cap layer thickness. A large redshift occurs by reducing the cap thickness. The in situ XRD observation reveals that this is a result of reduced strain. We demonstrate how such information about strain can be applied for designing and preparing novel device structures.

  7. Self-assembled GaInNAs/GaAsN quantum dot lasers: solid source molecular beam epitaxy growth and high-temperature operation

    Directory of Open Access Journals (Sweden)

    Yoon SF

    2006-01-01

    Full Text Available AbstractSelf-assembled GaInNAs quantum dots (QDs were grown on GaAs (001 substrate using solid-source molecular-beam epitaxy (SSMBE equipped with a radio-frequency nitrogen plasma source. The GaInNAs QD growth characteristics were extensively investigated using atomic-force microscopy (AFM, photoluminescence (PL, and transmission electron microscopy (TEM measurements. Self-assembled GaInNAs/GaAsN single layer QD lasers grown using SSMBE have been fabricated and characterized. The laser worked under continuous wave (CW operation at room temperature (RT with emission wavelength of 1175.86 nm. Temperature-dependent measurements have been carried out on the GaInNAs QD lasers. The lowest obtained threshold current density in this work is ∼1.05 kA/cm2from a GaInNAs QD laser (50 × 1,700 µm2 at 10 °C. High-temperature operation up to 65 °C was demonstrated from an unbonded GaInNAs QD laser (50 × 1,060 µm2, with high characteristic temperature of 79.4 K in the temperature range of 10–60 °C.

  8. Molecular beam epitaxy of GaAs nanowires and their sustainability for optoelectronic applications. Comparing Au- and self-assisted growth methods

    Energy Technology Data Exchange (ETDEWEB)

    Breuer, Steffen

    2011-09-28

    In this work the synthesis of GaAs nanowires by molecular beam epitaxy (MBE) using the vapour-liquid-solid (VLS) mechanism is investigated. A comparison between Au- and self-assisted VLS growth is at the centre of this thesis. While the Au-assisted method is established as a versatile tool for nanowire growth, the recently developed self-assisted variation results from the exchange of Au by Ga droplets and thus eliminates any possibility of Au incorporation. By both methods, we achieve nanowires with epitaxial alignment to the Si(111) substrates. Caused by differences during nanowire nucleation, a parasitic planar layer grows between the nanowires by the Au-assisted method, but can be avoided by the self-assisted method. Au-assisted nanowires grow predominantly in the metastable wurtzite crystal structure, while their self-assisted counterparts have the zincblende structure. All GaAs nanowires are fully relaxed and the strain arising from the lattice mismatch between GaAs and Si of 4.1 % is accommodated by misfit dislocations at the interface. Self-assisted GaAs nanowires are generally found to have vertical and non-polar side facets, while tilted and polar nanofacets were described for Au-assisted GaAs nanowires. We employ VLS nucleation theory to understand the effect of the droplet material on the lateral facets. Optoelectronic applications require long minority carrier lifetimes at room temperature. We fabricate GaAs/(Al,Ga)As core-shell nanowires and analyse them by transient photoluminescence (PL) spectroscopy. The results are 2.5 ns for the self-assisted nanowires as well as 9 ps for the Au-assisted nanowires. By temperature-dependent PL measurements we find a characteristic activation energy of 77 meV that is present only in the Au-assisted nanowires. We conclude that most likely Au is incorporated from the droplets into the GaAs nanowires and acts as a deep, non-radiative recombination centre.

  9. Influence of V/III growth flux ratio on trap states in m-plane GaN grown by ammonia-based molecular beam epitaxy

    International Nuclear Information System (INIS)

    Zhang, Z.; Arehart, A. R.; Hurni, C. A.; Speck, J. S.; Ringel, S. A.

    2012-01-01

    Deep level transient spectroscopy (DLTS) and deep level optical spectroscopy (DLOS) were utilized to investigate the behavior of deep states in m-plane, n-type GaN grown by ammonia-based molecular beam epitaxy (NH 3 -MBE) as a function of systematically varied V/III growth flux ratios. Levels were detected at E C - 0.14 eV, E C - 0.21 eV, E C - 0.26 eV, E C - 0.62 eV, E C - 0.67 eV, E C - 2.65 eV, and E C - 3.31 eV, with the concentrations of several traps exhibiting systematic dependencies on V/III ratio. The DLTS spectra are dominated by traps at E C - 0.14 eV and E C - 0.67 eV, whose concentrations decreased monotonically with increasing V/III ratio and decreasing oxygen impurity concentration, and by a trap at E C - 0.21 eV that revealed no dependence of its concentration on growth conditions, suggestive of different physical origins. Higher concentrations of deeper trap states detected by DLOS with activation energies of E C - 2.65 eV and E C - 3.31 eV in each sample did not display measureable sensitivity to the intentionally varied V/III ratio, necessitating further study on reducing these deep traps through growth optimization for maximizing material quality of NH 3 -MBE grown m-plane GaN.

  10. Formation of grown-in defects in molecular beam epitaxial Ga(In)NP: Effects of growth conditions and postgrowth treatments

    International Nuclear Information System (INIS)

    Dagnelund, D.; Buyanova, I. A.; Wang, X. J.; Chen, W. M.; Utsumi, A.; Furukawa, Y.; Wakahara, A.; Yonezu, H.

    2008-01-01

    Effects of growth conditions and post-growth treatments, such as presence of N ions, N 2 flow, growth temperature, In alloying, and postgrowth rapid thermal annealing (RTA), on formation of grown-in defects in Ga(In)NP prepared by molecular beam epitaxy are studied in detail by the optically detected magnetic resonance (ODMR) technique. Several common residual defects, such as two Ga-interstitial defects (i.e., Ga i -A and Ga i -B) and two unidentified defects with a g factor around 2 (denoted by S1 and S2), are closely monitored. Bombardment of impinging N ions on grown sample surface is found to facilitate formation of these defects. Higher N 2 flow is shown to have an even more profound effect than a higher number of ions in introducing these defects. Incorporation of a small amount of In (e.g., 5.1%) in GaNP seems to play a minor role in the formation of the defects. In GaInNP with 45% of In; however, the defects were found to be abundant. Effect of RTA on the defects is found to depend on initial configurations of Ga i -related defects formed during the growth. In the alloys where the Ga i -A and Ga i -B defects are absent in the as-grown samples (i.e., GaNP grown at a low temperature of 460 deg. C), the concentrations of the two Ga i defects are found to increase after postgrowth RTA. This indicates that the defects originally introduced in the as-grown alloys have been transformed into the more thermally stable Ga i -A and Ga i -B during RTA. On the other hand, when the Ga i -A and Ga i -B are readily abundant (e.g., at higher growth temperatures (≥500 deg. C), RTA leads to a slight reduction of the Ga i -A and Ga i -B ODMR signals. The S2 defect is also shown to be thermally stable upon the RTA treatment

  11. The effect of metal-rich growth conditions on the microstructure of Sc{sub x}Ga{sub 1-x}N films grown using molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Tsui, H.C.L.; Moram, M.A. [Department of Materials, Imperial College London (United Kingdom); Goff, L.E. [Department of Materials, Imperial College London (United Kingdom); Department of Physics, University of Cambridge (United Kingdom); Barradas, N.P. [CTN - Centro de Ciencias e Tecnologias Nucleares, Instituto Superior Tecnico, Universidade de Lisboa, Bobadela LRS (Portugal); Alves, E. [IPFN - Instituto de Plasmas e Fusao Nuclear, Lisboa (Portugal); Laboratorio de Aceleradores e Tecnologias de Radiacao, Instituto Superior Tecnico, Universidade de Lisboa, Bobadela LRS (Portugal); Pereira, S. [CICECO and Department of Physics, Universidade de Aveiro (Portugal); Beere, H.E.; Farrer, I.; Nicoll, C.A.; Ritchie, D.A. [Department of Physics, University of Cambridge (United Kingdom)

    2015-12-15

    Epitaxial Sc{sub x}Ga{sub 1-x}N films with 0 ≤ x ≤ 0.50 were grown using molecular beam epitaxy under metal-rich conditions. The Sc{sub x}Ga{sub 1-x}N growth rate increased with increasing Sc flux despite the use of metal-rich growth conditions, which is attributed to the catalytic decomposition of N{sub 2} induced by the presence of Sc. Microstructural analysis showed that phase-pure wurtzite Sc{sub x}Ga{sub 1-x}N was achieved up to x = 0.26, which is significantly higher than that previously reported for nitrogen-rich conditions, indicating that the use of metal-rich conditions can help to stabilise wurtzite phase Sc{sub x}Ga{sub 1-x}N. (copyright 2015 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  12. Heteroepitaxial growth of In-face InN on GaN (0001) by plasma-assisted molecular-beam epitaxy

    International Nuclear Information System (INIS)

    Dimakis, E.; Iliopoulos, E.; Tsagaraki, K.; Kehagias, Th.; Komninou, Ph.; Georgakilas, A.

    2005-01-01

    The thermodynamic aspects of indium-face InN growth by radio frequency plasma-assisted molecular-beam epitaxy (rf-MBE) and the nucleation of InN on gallium-face GaN (0001) surface were investigated. The rates of InN decomposition and indium desorption from the surface were measured in situ using reflected high-energy electron diffraction and the rf-MBE 'growth window' of In-face InN (0001) was identified. It is shown that sustainable growth can be achieved only when the arrival rate of active nitrogen species on the surface is higher than the arrival rate of indium atoms. The maximum substrate temperature permitting InN growth as a function of the active nitrogen flux was determined. The growth mode of InN on Ga-face GaN (0001) surface was investigated by reflected high-energy electron diffraction and atomic force microscopy. It was found to be of the Volmer-Weber-type for substrate temperatures less than 350 deg. C and of the Stranski-Krastanov for substrate temperatures between 350 and 520 deg. C. The number of monolayers of initial two-dimensional growth, in the case of Stranski-Krastanov mode, varies monotonically with substrate temperature, from 2 ML at 400 deg. C to about 12 ML at 500 deg. C. The evolution and coalescence of nucleated islands were also investigated as a function of substrate temperature. It was found that at higher temperature their coalescence is inhibited leading to porous-columnar InN thin films, which exhibit growth rates higher than the nominal value. Therefore, in order to achieve continuous InN layers on GaN (0001) a two-step growth approach is introduced. In that approach, InN is nucleated at low temperatures on GaN and the growth continues until full coalescence of the nucleated islands. Subsequently, this nucleation layer is overgrown at higher substrate temperature in order to achieve high-quality continuous films. The InN films grown by the two-step method were investigated by x-ray diffraction, Hall-effect measurements, and

  13. Molecular beam epitaxial growth mechanism of ZnSe epilayers on (100) GaAs as determined by reflection high-energy electron diffraction, transmission electron microscopy and X-ray diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Ruppert, P.; Hommel, D.; Behr, T.; Heinke, H.; Waag, A.; Landwehr, G. (Physikalisches Inst., Univ. Wuerzburg (Germany))

    1994-04-14

    The properties of molecular beam epitaxial growth of ZnSe epilayers deposited directly on a GaAs substrate are compared to those grown on a GaAs buffer layer. The superior quality of the latter is confirmed by RHEED, TEM and X-ray diffraction. Based on RHEED oscillation studies, a model explaining the dependence of the ZnSe growth rate on Zn and Se fluxes and the substrate temperature is developed taking into account physisorbed and chemisorbed states. For partially relaxed epilayers, the correlation between the relaxation state and the crystalline mosaicity, as found by high resolution X-ray diffraction, is discussed

  14. Lateral epitaxial overgrowth of GaN on a patterned GaN-on-silicon substrate by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Wang, Yongjin; Hu, Fangren; Hane, Kazuhiro

    2011-01-01

    We report here the lateral epitaxial overgrowth (LEO) of GaN on a patterned GaN-on-silicon substrate by molecular beam epitaxy (MBE) growth with radio frequency nitrogen plasma as a gas source. Two kinds of GaN nanostructures are defined by electron beam lithography and realized on a GaN substrate by fast atom beam etching. The epitaxial growth of GaN by MBE is performed on the prepared GaN template, and the selective growth of GaN takes place with the assistance of GaN nanostructures. The LEO of GaN produces novel GaN epitaxial structures which are dependent on the shape and the size of the processed GaN nanostructures. Periodic GaN hexagonal pyramids are generated inside the air holes, and GaN epitaxial strips with triangular section are formed in the grating region. This work provides a promising way for producing novel GaN-based devices by the LEO of GaN using the MBE technique

  15. Growth of 1.5 micron gallium indium nitrogen arsenic antimonide vertical cavity surface emitting lasers by molecular beam epitaxy

    Science.gov (United States)

    Wistey, Mark Allan

    Fiber optics has revolutionized long distance communication and long haul networks, allowing unimaginable data speeds and noise-free telephone calls around the world for mere pennies per hour at the trunk level. But the high speeds of optical fiber generally do not extend to individual workstations or to the home, in large part because it has been difficult and expensive to produce lasers which emitted light at wavelengths which could take advantage of optical fiber. One of the most promising solutions to this problem is the development of a new class of semiconductors known as dilute nitrides. Dilute nitrides such as GaInNAs can be grown directly on gallium arsenide, which allows well-established processing techniques. More important, gallium arsenide allows the growth of vertical-cavity surface-emitting lasers (VCSELs), which can be grown in dense, 2D arrays on each wafer, providing tremendous economies of scale for manufacturing, testing, and packaging. Unfortunately, GaInNAs lasers have suffered from what has been dubbed the "nitrogen penalty," with high thresholds and low efficiency as the fraction of nitrogen in the semiconductor was increased. This thesis describes the steps taken to identify and essentially eliminate the nitrogen penalty. Protecting the wafer surface from plasma ignition, using an arsenic cap, greatly improved material quality. Using a Langmuir probe, we further found that the nitrogen plasma source produced a large number of ions which damaged the wafer during growth. The ions were dramatically reduced using deflection plates. Low voltage deflection plates were found to be preferable to high voltages, and simulations showed low voltages to be adequate for ion removal. The long wavelengths from dilute nitrides can be partly explained by wafer damage during growth. As a result of these studies, we demonstrated the first CW, room temperature lasers at wavelengths beyond 1.5mum on gallium arsenide, and the first GaInNAs(Sb) VCSELs beyond 1

  16. Molecular beam epitaxial growth of Bi2Te3 and Sb2Te3 topological insulators on GaAs (111 substrates: a potential route to fabricate topological insulator p-n junction

    Directory of Open Access Journals (Sweden)

    Zhaoquan Zeng

    2013-07-01

    Full Text Available High quality Bi2Te3 and Sb2Te3 topological insulators films were epitaxially grown on GaAs (111 substrate using solid source molecular beam epitaxy. Their growth and behavior on both vicinal and non-vicinal GaAs (111 substrates were investigated by reflection high-energy electron diffraction, atomic force microscopy, X-ray diffraction, and high resolution transmission electron microscopy. It is found that non-vicinal GaAs (111 substrate is better than a vicinal substrate to provide high quality Bi2Te3 and Sb2Te3 films. Hall and magnetoresistance measurements indicate that p type Sb2Te3 and n type Bi2Te3 topological insulator films can be directly grown on a GaAs (111 substrate, which may pave a way to fabricate topological insulator p-n junction on the same substrate, compatible with the fabrication process of present semiconductor optoelectronic devices.

  17. Molecular beam epitaxy growth of niobium oxides by solid/liquid state oxygen source and lithium assisted metal-halide chemistry

    Science.gov (United States)

    Tellekamp, M. Brooks; Greenlee, Jordan D.; Shank, Joshua C.; Doolittle, W. Alan

    2015-09-01

    In order to consistently grow high quality niobium oxides and lithium niobium oxides, a novel solid/liquid state oxygen source, LiClO4, has been implemented in a molecular beam epitaxy (MBE) system. LiClO4 is shown to decompose into both molecular and atomic oxygen upon heating. This allows oxidation rates similar to that of molecular oxygen but at a reduced overall beam flux, quantified by in situ Auger analysis. LiClO4 operation is decomposition limited to less than 400 °C, and other material limitations are identified. The design of a custom near-ambient NbCl5 effusion cell is presented, which improves both short and long term stability. Films of Nb oxidation state +2, +3, and +5 are grown using these new tools, including the multi-functional sub-oxide LiNbO2.

  18. Epitaxial growth by monolayer restricted galvanic displacement

    Directory of Open Access Journals (Sweden)

    Vasilić Rastko

    2012-01-01

    Full Text Available The development of a new method for epitaxial growth of metals in solution by galvanic displacement of layers pre-deposited by underpotential deposition (UPD was discussed and experimentally illustrated throughout the lecture. Cyclic voltammetry (CV and scanning tunneling microscopy (STM are employed to carry out and monitor a “quasi-perfect”, two-dimensional growth of Ag on Au(111, Cu on Ag(111, and Cu on Au(111 by repetitive galvanic displacement of underpotentially deposited monolayers. A comparative study emphasizes the displacement stoichiometry as an efficient tool for thickness control during the deposition process and as a key parameter that affects the deposit morphology. The excellent quality of layers deposited by monolayer-restricted galvanic displacement is manifested by a steady UPD voltammetry and ascertained by a flat and uniform surface morphology maintained during the entire growth process.

  19. Epitaxial growth mechanisms of graphene and effects of substrates

    Science.gov (United States)

    Özçelik, V. Ongun; Cahangirov, S.; Ciraci, S.

    2012-06-01

    The growth process of single layer graphene with and without substrate is investigated using ab initio, finite temperature molecular dynamic calculations within density functional theory. An understanding of the epitaxial graphene growth mechanisms in the atomic level is provided by exploring the transient stages which occur at the growing edges of graphene. These stages are formation and collapse of large carbon rings together with the formation and healing of Stone-Wales like pentagon-heptagon defects. The activation barriers for the healing of these growth induced defects on various substrates are calculated using the climbing image nudge elastic band method and compared with that of the Stone-Wales defect. It is found that the healing of pentagon-heptagon defects occurring near the edge in the course of growth is much easier than that of Stone-Wales defect. The role of the substrate in the epitaxial growth and in the healing of defects are also investigated in detail, along with the effects of using carbon dimers as the building blocks of graphene growth.

  20. Shaping metal nanocrystals through epitaxial seeded growth

    Energy Technology Data Exchange (ETDEWEB)

    Habas, Susan E.; Lee, Hyunjoo; Radmilovic, Velimir; Somorjai,Gabor A.; Yang, Peidong

    2008-02-17

    Morphological control of nanocrystals has becomeincreasingly important, as many of their physical and chemical propertiesare highly shape-dependent. Nanocrystal shape control for both single andmultiple material systems, however, remains fairly empirical andchallenging. New methods need to be explored for the rational syntheticdesign of heterostructures with controlled morphology. Overgrowth of adifferent material on well-faceted seeds, for example, allows for the useof the defined seed morphology to control nucleation and growth of thesecondary structure. Here, we have used highly faceted cubic Pt seeds todirect the epitaxial overgrowth of a secondary metal. We demonstrate thisconcept with lattice matched Pd to produce conformal shape-controlledcore-shell particles, and then extend it to lattice mismatched Au to giveanisotropic growth. Seeding with faceted nanocrystals may havesignificant potential towards the development of shape-controlledheterostructures with defined interfaces.

  1. Modelling, Design, Growth and Characterization of Strain Balanced Quantum Cascade Lasers (3-11mum), grown by Gas Source Molecular Beam Epitaxy

    Science.gov (United States)

    Bandyopadhyay, Neelanjan

    Quantum Cascade Laser (QCL) is a compact room temperature (RT) source of mid-infrared radiation, which can be used for spectroscopic detection of trace amount of chemicals. The mid-infrared spectral range between (3-11 microm), has a dense array of absorption lines of numerous molecules, due to the presence of fundamental vibrational modes. The goal of this thesis can be subdivided into two parts. Firstly, short wavelength QCLs, emitting below 4microm, perform poorly at RT, due to inter-valley Gamma --- L carrier scattering, carrier escape to the continuum, heat removal from the core region at high power density corresponding to short wavelength operation, and large interface scattering due to highly strained materials. Secondly, it is desirable to have a single QCL based source emitting between 6-10microm, which be used to detect multiple molecules having their peak absorptions far apart, inside this spectral range. However, gain bandwidth of a single core QCL is relatively small, so laser emission cannot be tuned over a wide spectral range. This thesis describes the working principle of a QCL based on superlattice transport, rate equations, scattering mechanism, and waveguide design. The choice of the material system for this work and the fundamentals of band structure engineering has been derived. Gas source molecular beam epitaxy - growth optimization and characterization is one of the most important features of this work, especially for short wavelength QCLs, and has been explained in depth. Different strategies for design of active region design of short wavelength QCL and heterogeneous broadband QCL has been explored. The major milestones, of this research was the world's first watt level continuous wave (CW), RT demonstration at 3.76 microm, which was followed by another milestone of the first CW, RT demonstration at 3.39microm and 3.55microm, and finally the elusive result of QCL emitting at CW, RT at a wavelength as short as lambda ~3microm, a record. In

  2. Growth of low disorder GaAs/AlGaAs heterostructures by molecular beam epitaxy for the study of correlated electron phases in two dimensions

    Science.gov (United States)

    Watson, John D.

    The unparalleled quality of GaAs/AlGaAs heterostructures grown by molecular beam epitaxy has enabled a wide range of experiments probing interaction effects in two-dimensional electron and hole gases. This dissertation presents work aimed at further understanding the key material-related issues currently limiting the quality of these 2D systems, particularly in relation to the fractional quantum Hall effect in the 2nd Landau level and spin-based implementations of quantum computation. The manuscript begins with a theoretical introduction to the quantum Hall effect which outlines the experimental conditions necessary to study the physics of interest and motivates the use of the semiconductor growth and cryogenic measurement techniques outlined in chapters 2 and 3, respectively. In addition to a generic introduction to the molecular beam epitaxy growth technique, chapter 2 summarizes some of what was learned about the material purity issues currently limiting the low temperature electron mobility. Finally, a series of appendices are included which detail the experimental methods used over the course of the research. Chapter 4 presents an experiment examining transport in a low density two-dimensional hole system in which the hole density could be varied by means of an evaporated back gate. At low temperature, the mobility reached a maximum of 2.6 x 106 cm2/Vs at a density of 6.2 x 1010 cm-2 which is the highest reported mobility in a two-dimensional hole system to date. In addition, it was found that the mobility as a function of density did not follow a power law with a single exponent. Instead, it was found that the power law varied with density, indicating a cross-over between dominant scattering mechanisms at low density and high density. At low density the mobility was found to be limited by remote ionized impurity scattering, while at high density the dominant scattering mechanism was found to be background impurity scattering. Chapter 5 details an experiment

  3. Growth of a delta-doped silicon layer by molecular beam epitaxy on a charge-coupled device for reflection-limited ultraviolet quantum efficiency

    Science.gov (United States)

    Hoenk, Michael E.; Grunthaner, Paula J.; Grunthaner, Frank J.; Terhune, R. W.; Fattahi, Masoud; Tseng, Hsin-Fu

    1992-01-01

    Low-temperature silicon molecular beam epitaxy is used to grow a delta-doped silicon layer on a fully processed charge-coupled device (CCD). The measured quantum efficiency of the delta-doped backside-thinned CCD is in agreement with the reflection limit for light incident on the back surface in the spectral range of 260-600 nm. The 2.5 nm silicon layer, grown at 450 C, contained a boron delta-layer with surface density of about 2 x 10 exp 14/sq cm. Passivation of the surface was done by steam oxidation of a nominally undoped 1.5 nm Si cap layer. The UV quantum efficiency was found to be uniform and stable with respect to thermal cycling and illumination conditions.

  4. Growth of epitaxial thin films by pulsed laser ablation

    International Nuclear Information System (INIS)

    Lowndes, D.H.

    1992-01-01

    High-quality, high-temperature superconductor (HTSc) films can be grown by the pulsed laser ablation (PLA) process. This article provides a detailed introduction to the advantages and curent limitations of PLA for epitaxial film growth. Emphasis is placed on experimental methods and on exploitation of PLA to control epitaxial growth at either the unit cell or the atomic-layer level. Examples are taken from recent HTSc film growth. 33 figs, 127 refs

  5. Molecular beam epitaxy of InN nanowires on Si

    Science.gov (United States)

    Golam Sarwar, A. T. M.; Carnevale, Santino D.; Kent, Thomas F.; Laskar, Masihhur R.; May, Brelon J.; Myers, Roberto C.

    2015-10-01

    We report on a systematic growth study of the nucleation process of InN nanowires on Si(1 1 1) substrates using plasma assisted molecular beam epitaxy (PAMBE). Samples are grown with various substrate temperatures and III/V ratios. Scanning electron microscopy, X-ray diffraction spectroscopy, energy dispersive X-ray spectroscopy, and photoluminescence are carried out to map out the variation in structural and optical properties versus growth conditions. Statistical averages of areal density, height, and radius are mapped as a function of substrate temperature and III/V ratio. Three different morphological phases are identified on the growth surface: InN, α-In and β-In. Based on SEM image analysis of samples grown at different conditions, the formation mechanism of these phases is proposed. Finally, the growth phase diagram of PAMBE grown InN on Si under N-rich condition is presented, and tapered versus non-tapered growth conditions are identified. It is found that high growth temperature and low III/V ratio plays a critical role in the growth of non-tapered InN nanowires.

  6. Growth of BaSi2 continuous films on Ge(111) by molecular beam epitaxy and fabrication of p-BaSi2/n-Ge heterojunction solar cells

    Science.gov (United States)

    Takabe, Ryota; Yachi, Suguru; Tsukahara, Daichi; Toko, Kaoru; Suemasu, Takashi

    2017-05-01

    We grew BaSi2 films on Ge(111) substrates by various growth methods based on molecular beam epitaxy (MBE). First, we attempted to form BaSi2 films directly on Ge(111) by MBE without templates. We next formed BaSi2 films using BaGe2 templates as commonly used for MBE growth of BaSi2 on Si substrates. Contrary to our prediction, the lateral growth of BaSi2 was not promoted by these two methods; BaSi2 formed not into a continuous film but into islands. Although streaky patterns of reflection high-energy electron diffraction were observed inside the growth chamber, no X-ray diffraction lines of BaSi2 were observed in samples taken out from the growth chamber. Such BaSi2 islands were easily to get oxidized. We finally attempted to form a continuous BaSi2 template layer on Ge(111) by solid phase epitaxy, that is, the deposition of amorphous Ba-Si layers onto MBE-grown BaSi2 epitaxial islands, followed by post annealing. We achieved the formation of an approximately 5-nm-thick BaSi2 continuous layer by this method. Using this BaSi2 layer as a template, we succeeded in forming a-axis-oriented 520-nm-thick BaSi2 epitaxial films on Ge substrates, although (111)-oriented Si grains were included in the grown layer. We next formed a B-doped p-BaSi2(20 nm)/n-Ge(111) heterojunction solar cell. A wide-spectrum response from 400 to 2000 nm was achieved. At an external bias voltage of 1 V, the external quantum efficiency reached as high as 60%, demonstrating the great potential of BaSi2/Ge combination. However, the efficiency of a solar cell under AM1.5 illumination was quite low (0.1%). The origin of such a low efficiency was examined.

  7. One-step Ge/Si epitaxial growth.

    Science.gov (United States)

    Wu, Hung-Chi; Lin, Bi-Hsuan; Chen, Huang-Chin; Chen, Po-Chin; Sheu, Hwo-Shuenn; Lin, I-Nan; Chiu, Hsin-Tien; Lee, Chi-Young

    2011-07-01

    Fabricating a low-cost virtual germanium (Ge) template by epitaxial growth of Ge films on silicon wafer with a Ge(x)Si(1-x) (0 deposition method in one step by decomposing a hazardousless GeO(2) powder under hydrogen atmosphere without ultra-high vacuum condition and then depositing in a low-temperature region. X-ray diffraction analysis shows that the Ge film with an epitaxial relationship is along the in-plane direction of Si. The successful growth of epitaxial Ge films on Si substrate demonstrates the feasibility of integrating various functional devices on the Ge/Si substrates.

  8. Molecular beam epitaxy of single crystal colossal magnetoresistive material

    International Nuclear Information System (INIS)

    Eckstein, J.N.; Bozovic, I.; Rzchowski, M.; O'Donnell, J.; Hinaus, B.; Onellion, M.

    1996-01-01

    The authors have grown films of (LaSr)MnO 3 (LSMO) and (LaCa)MnO 3 (LCMO) using atomic layer-by-layer molecular beam epitaxy (ALL-MBE). Depending on growth conditions, substrate lattice constant and the exact cation stoichiometry, the films are either pseudomorphic or strain relaxed. The pseudomorphic films show atomically flat surfaces, with a unit cell terrace structure that is a replica of that observed on the slightly vicinal substrates, while the strain relaxed films show bumpy surfaces correlated with a dislocation network. All films show tetragonal structure and exhibit anisotropic magnetoresistance, with a low field response, (1/R)(dR/dH) as large as 5 T -1

  9. Growth of high mobility GaN and AlGaN/GaN high electron mobility transistor structures on 4H-SiC by ammonia molecular-beam epitaxy

    International Nuclear Information System (INIS)

    Webb, James B.; Tang, H.; Bardwell, J. A.; Coleridge, P.

    2001-01-01

    Ammonia molecular-beam epitaxy has been used to grow high-quality epilayers of GaN and AlGaN/GaN heterostructure field-effect transistor (HFET) structures on insulating 4H-SiC. The growth process, which used a magnetron sputter epitaxy deposited buffer layer of AlN, has been described previously. Ex situ pretreatment of the SiC substrate was found to be unnecessary. For a single 2.0 μm thick silicon doped epilayer, a room temperature (RT) electron mobility of 500 cm2/Vs was measured at a carrier density of 6.6x10 16 cm -3 . For the HFET structure, a room temperature mobility of 1300 cm2/Vs at a sheet carrier density of 3.3x10 12 cm -2 was observed, increasing to 11000 cm2/Vs at 77 K. The surface morphology of the layers indicated a coalesced mesa structure similar to what we observed for growth on sapphire, but with a lower overall defect density and correspondingly larger grain size. The observation of well-resolved Shubnikov de Haas oscillations at fields as low as 3 T indicated a relatively smooth interface. [copyright] 2001 American Institute of Physics

  10. Self-catalyzed growth of dilute nitride GaAs/GaAsSbN/GaAs core-shell nanowires by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Kasanaboina, Pavan Kumar [Department of Electrical and Computer Engineering, North Carolina A& T State University, Greensboro, North Carolina 27411 (United States); Ahmad, Estiak [Nanoengineering, Joint School of Nanoscience and Nanoengineering, NCA& T State University, Greensboro, North Carolina 27401 (United States); Li, Jia; Iyer, Shanthi [Department of Electrical and Computer Engineering, North Carolina A& T State University, Greensboro, North Carolina 27411 (United States); Nanoengineering, Joint School of Nanoscience and Nanoengineering, NCA& T State University, Greensboro, North Carolina 27401 (United States); Reynolds, C. Lewis; Liu, Yang [Department of Materials Science and Engineering, North Carolina State University, Raleigh, North Carolina 27695 (United States)

    2015-09-07

    Bandgap tuning up to 1.3 μm in GaAsSb based nanowires by incorporation of dilute amount of N is reported. Highly vertical GaAs/GaAsSbN/GaAs core-shell configured nanowires were grown for different N contents on Si (111) substrates using plasma assisted molecular beam epitaxy. X-ray diffraction analysis revealed close lattice matching of GaAsSbN with GaAs. Micro-photoluminescence (μ-PL) revealed red shift as well as broadening of the spectra attesting to N incorporation in the nanowires. Replication of the 4K PL spectra for several different single nanowires compared to the corresponding nanowire array suggests good compositional homogeneity amongst the nanowires. A large red shift of the Raman spectrum and associated symmetric line shape in these nanowires have been attributed to phonon localization at point defects. Transmission electron microscopy reveals the dominance of stacking faults and twins in these nanowires. The lower strain present in these dilute nitride nanowires, as opposed to GaAsSb nanowires having the same PL emission wavelength, and the observation of room temperature PL demonstrate the advantage of the dilute nitride system offers in the nanowire configuration, providing a pathway for realizing nanoscale optoelectronic devices in the telecommunication wavelength region.

  11. STM investigation of epitaxial Si growth for the fabrication of a Si-based quantum computer

    Energy Technology Data Exchange (ETDEWEB)

    Oberbeck, Lars; Hallam, Toby; Curson, Neil J.; Simmons, Michelle Y.; Clark, Robert G

    2003-05-15

    We investigate the morphology of epitaxial Si layers grown on clean and on hydrogen terminated Si(0 0 1) to explore the growth strategy for the fabrication of a Si-based quantum computer. We use molecular beam epitaxy to deposit 5 monolayers of silicon at a temperature of 250 deg. C and scanning tunnelling microscopy to image the surface at room temperature after growth and after various rapid annealing steps in the temperature range of 350-600 deg. C. The epitaxial layer grown on the hydrogenated surface shows a significantly higher surface roughness due to a lower mobility of silicon surface atoms in the presence of hydrogen. Annealing at temperatures {>=}550 deg. C reduces the roughness of both epitaxial layers to the value of a clean silicon surface. However, the missing dimer defect density of the epitaxial layer grown on the hydrogenated surface remains higher by a factor of two compared to the layer grown on clean Si(0 0 1). Our results suggest a quantum computer growth strategy in which the hydrogen resist layer is desorbed before the epitaxial silicon layer is grown at low temperature to encapsulate phosphorus quantum bits.

  12. Creating Ruddlesden-Popper phases by hybrid molecular beam epitaxy

    International Nuclear Information System (INIS)

    Haislmaier, Ryan C.; Stone, Greg; Alem, Nasim; Engel-Herbert, Roman

    2016-01-01

    The synthesis of a 50 unit cell thick n = 4 Sr_n_+_1Ti_nO_3_n_+_1 (Sr_5Ti_4O_1_3) Ruddlesden-Popper (RP) phase film is demonstrated by sequentially depositing SrO and TiO_2 layers in an alternating fashion using hybrid molecular beam epitaxy (MBE), where Ti was supplied using titanium tetraisopropoxide (TTIP). A detailed calibration procedure is outlined for determining the shuttering times to deposit SrO and TiO_2 layers with precise monolayer doses using in-situ reflection high energy electron diffraction (RHEED) as feedback. Using optimized Sr and TTIP shuttering times, a fully automated growth of the n = 4 RP phase was carried out over a period of >4.5 h. Very stable RHEED intensity oscillations were observed over the entire growth period. The structural characterization by X-ray diffraction and high resolution transmission electron microscopy revealed that a constant periodicity of four SrTiO_3 perovskite unit cell blocks separating the double SrO rocksalt layer was maintained throughout the entire film thickness with a very little amount of planar faults oriented perpendicular to the growth front direction. These results illustrate that hybrid MBE is capable of layer-by-layer growth with atomic level precision and excellent flux stability.

  13. Creating Ruddlesden-Popper phases by hybrid molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Haislmaier, Ryan C.; Stone, Greg; Alem, Nasim; Engel-Herbert, Roman, E-mail: rue2@psu.edu [Department of Materials Science and Engineering, The Pennsylvania State University, University Park, Pennsylvania 16802 (United States)

    2016-07-25

    The synthesis of a 50 unit cell thick n = 4 Sr{sub n+1}Ti{sub n}O{sub 3n+1} (Sr{sub 5}Ti{sub 4}O{sub 13}) Ruddlesden-Popper (RP) phase film is demonstrated by sequentially depositing SrO and TiO{sub 2} layers in an alternating fashion using hybrid molecular beam epitaxy (MBE), where Ti was supplied using titanium tetraisopropoxide (TTIP). A detailed calibration procedure is outlined for determining the shuttering times to deposit SrO and TiO{sub 2} layers with precise monolayer doses using in-situ reflection high energy electron diffraction (RHEED) as feedback. Using optimized Sr and TTIP shuttering times, a fully automated growth of the n = 4 RP phase was carried out over a period of >4.5 h. Very stable RHEED intensity oscillations were observed over the entire growth period. The structural characterization by X-ray diffraction and high resolution transmission electron microscopy revealed that a constant periodicity of four SrTiO{sub 3} perovskite unit cell blocks separating the double SrO rocksalt layer was maintained throughout the entire film thickness with a very little amount of planar faults oriented perpendicular to the growth front direction. These results illustrate that hybrid MBE is capable of layer-by-layer growth with atomic level precision and excellent flux stability.

  14. Epitaxial Growth and Cracking Mechanisms of Thermally Sprayed Ceramic Splats

    Science.gov (United States)

    Chen, Lin; Yang, Guan-jun

    2018-02-01

    In the present study, the epitaxial growth and cracking mechanisms of thermally sprayed ceramic splats were explored. We report, for the first time, the epitaxial growth of various splat/substrate combinations at low substrate temperatures (100 °C) and large lattice mismatch (- 11.26%). Our results suggest that thermal spray deposition was essentially a liquid-phase epitaxy, readily forming chemical bonding. The interface temperature was also estimated. The results convincingly demonstrated that atoms only need to diffuse and rearrange over a sufficiently short range during extremely rapid solidification. Concurrently, severe cracking occurred in the epitaxial splat/substrate systems, which indicated high tensile stress was produced during splat deposition. The origin of the tensile stress was attributed to the strong constraint of the locally heated substrate by its cold surroundings.

  15. Effect of Al/N ratio during nucleation layer growth on Hall mobility and buffer leakage of molecular-beam epitaxy grown AlGaN/GaN heterostructures

    International Nuclear Information System (INIS)

    Storm, D.F.; Katzer, D.S.; Binari, S.C.; Shanabrook, B.V.; Zhou Lin; Smith, David J.

    2004-01-01

    AlGaN/GaN high electron mobility transistor structures have been grown by plasma-assisted molecular beam epitaxy on semi-insulating 4H-SiC utilizing an AlN nucleation layer. The electron Hall mobility of these structures increases from 1050 cm 2 /V s to greater than 1450 cm 2 /V s when the Al/N flux ratio during the growth of the nucleation layer is increased from 0.90 to 1.07. Buffer leakage currents increase abruptly by nearly three orders of magnitude when the Al/N ratio increases from below to above unity. Transmission electron microscopy indicates that high buffer leakage is correlated with the presence of stacking faults in the nucleation layer and cubic phase GaN in the buffer, while low mobilities are correlated with high dislocation densities

  16. Mg doping of GaN by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Lieten, R R; Buchowicz, G; Dubon, O; Motsnyi, V; Zhang, L; Cheng, K; Leys, M; Degroote, S; Borghs, G

    2011-01-01

    We present a systematic study on the influence of growth conditions on the incorporation and activation of Mg in GaN layers grown by plasma-assisted molecular beam epitaxy. We show that high quality p-type GaN layers can be obtained on GaN-on-silicon templates. The Mg incorporation and the electrical properties have been investigated as a function of growth temperature, Ga : N flux ratio and Mg : Ga flux ratio. It was found that the incorporation of Mg and the electrical properties are highly sensitive to the Ga : N flux ratio. The highest hole mobility and lowest resistivity were achieved for slightly Ga-rich conditions. In addition to an optimal Ga : N ratio, an optimum Mg : Ga flux ratio was also observed at around 1%. We observed a clear Mg flux window for p-type doping of GaN : 0.31% 17 cm -3 and a mobility of 15 cm 2 V -1 s -1 . Temperature-dependent Hall effect measurements indicate an acceptor depth in these samples of 100 meV for a hole concentration of 5.5 x 10 17 cm -3 . The corresponding Mg concentration is 5 x 10 19 cm -3 , indicating approximately 1% activation at room temperature. In addition to continuous growth of Mg-doped GaN layers we also investigated different modulated growth procedures. We show that a modulated growth procedure has only limited influence on Mg doping at a growth temperature of 800 deg. or higher. This result is thus in contrast to previously reported GaN : Mg doping at much lower growth temperatures of 500 deg. C.

  17. Molecular beam epitaxy of Cd3As2 on a III-V substrate

    Directory of Open Access Journals (Sweden)

    Timo Schumann

    2016-12-01

    Full Text Available Epitaxial, strain-engineered Dirac semimetal heterostructures promise tuning of the unique properties of these materials. In this study, we investigate the growth of thin films of the recently discovered Dirac semimetal Cd3As2 by molecular beam epitaxy. We show that epitaxial Cd3As2 layers can be grown at low temperatures (110 °C–220 °C, in situ, on (111 GaSb buffer layers deposited on (111 GaAs substrates. The orientation relationship is described by ( 112 Cd 3 As 2 || (111 GaSb and [ 1 1 ¯ 0 ] Cd 3 As 2 || [ 1 ¯ 01 ] GaSb . The films are shown to grow in the low-temperature, vacancy ordered, tetragonal Dirac semimetal phase. They exhibit high room temperature mobilities of up to 19300 cm2/Vs, despite a three-dimensional surface morphology indicative of island growth and the presence of twin variants. The results indicate that epitaxial growth on more closely lattice matched buffer layers, such as InGaSb or InAlSb, which allow for imposing different degrees of epitaxial coherency strains, should be possible.

  18. Epitaxial growth of silicon and germanium on (100-oriented crystalline substrates by RF PECVD at 175 °C

    Directory of Open Access Journals (Sweden)

    Mauguin O.

    2012-11-01

    Full Text Available We report on the epitaxial growth of crystalline Si and Ge thin films by standard radio frequency plasma enhanced chemical vapor deposition at 175 °C on (100-oriented silicon substrates. We also demonstrate the epitaxial growth of silicon films on epitaxially grown germanium layers so that multilayer samples sustaining epitaxy could be produced. We used spectroscopic ellipsometry, Raman spectroscopy, transmission electron microscopy and X-ray diffraction to characterize the structure of the films (amorphous, crystalline. These techniques were found to provide consistent results and provided information on the crystallinity and constraints in such lattice-mismatched structures. These results open the way to multiple quantum-well structures, which have been so far limited to few techniques such as Molecular Beam Epitaxy or MetalOrganic Chemical Vapor Deposition.

  19. Molecular beam epitaxy of GaN(0001) utilizing NH3 and/or NH+x ions: Growth kinetics and defect structure

    International Nuclear Information System (INIS)

    Lee, N.; Powell, R.C.; Kim, Y.; Greene, J.E.

    1995-01-01

    Gas-source molecular beam epitaxy (GS-MBE), utilizing Ga and NH 3 , and reactive-ion MBE (RIMBE), incorporating both thermal NH 3 and low-energy NH + x ions, were used to grow single crystal GaN(0001) layers on Al 2 O 3 (0001) at temperatures T s between 700 and 850 degree C with deposition rates of 0.2--0.5 μm h -1 . The RIMBE experiments were carried out with incident NH + x /Ga flux ratios J NH + x /J Ga =1.9--3.2 and NH + x acceleration energies E NH + x =45--90 eV. Plan-view and cross-sectional transmission electron microscopy analyses showed that the primary defects in the GS-MBE films were threading dislocations having either pure edge or mixed edge/screw characteristics with Burgers vectors bar b=1/3 left-angle 2 bar 1 bar 10 right-angle, basal-plane stacking faults with displacement vectors bar R=1/6 left-angle 02 bar 23 right-angle, and prismatic stacking faults with bar R=1/2 left-angle bar 1101 right-angle. In the case of RIMBE films, no stacking faults or residual ion-induced defects were observed with E NH + x =45 eV and T s ≥800 degree C. However, increasing E NH + x to ≥60 eV at T s =800 degree C gave rise to the formation of residual ion-induced point-defect clusters observable by transmission electron microscopy (TEM). Increasing T s to 850 degree C with E NH + x ≥60 eV resulted in the ion-induced defects aggregating to form interstitial basal and prismatic dislocation loops, whose number densities depended upon the ion flux, with Burgers vectors 1/2 left-angle 0001 right-angle and 1/3 left-angle 2 bar 1 bar 10 right-angle, respectively. (Abstract Truncated)

  20. Growth Interruption Effect on the Fabrication of GaAs Concentric Multiple Rings by Droplet Epitaxy

    Directory of Open Access Journals (Sweden)

    Fedorov A

    2010-01-01

    Full Text Available Abstract We present the molecular beam epitaxy fabrication and optical properties of complex GaAs nanostructures by droplet epitaxy: concentric triple quantum rings. A significant difference was found between the volumes of the original droplets and the final GaAs structures. By means of atomic force microscopy and photoluminescence spectroscopy, we found that a thin GaAs quantum well-like layer is developed all over the substrate during the growth interruption times, caused by the migration of Ga in a low As background.

  1. Epitaxial thin film growth and properties of unconventional oxide superconductors. Cuprates and cobaltates

    International Nuclear Information System (INIS)

    Krockenberger, Y.

    2006-01-01

    The discovery of high-temperature superconductors has strongly driven the development of suited thin film fabrication methods of complex oxides. One way is the adaptation of molecular beam epitaxy (MBE) for the growth of oxide materials. Another approach is the use of pulsed laser deposition (PLD) which has the advantage of good stoichiometry transfer from target to the substrate. Both techniques are used within this thesis. Epitaxial thin films of new materials are of course needed for future applications. In addition, the controlled synthesis of thin film matter which can be formed far away from thermal equilibrium allows for the investigation of fundamental physical materials properties. (orig.)

  2. Epitaxial thin film growth and properties of unconventional oxide superconductors. Cuprates and cobaltates

    Energy Technology Data Exchange (ETDEWEB)

    Krockenberger, Y.

    2006-07-01

    The discovery of high-temperature superconductors has strongly driven the development of suited thin film fabrication methods of complex oxides. One way is the adaptation of molecular beam epitaxy (MBE) for the growth of oxide materials. Another approach is the use of pulsed laser deposition (PLD) which has the advantage of good stoichiometry transfer from target to the substrate. Both techniques are used within this thesis. Epitaxial thin films of new materials are of course needed for future applications. In addition, the controlled synthesis of thin film matter which can be formed far away from thermal equilibrium allows for the investigation of fundamental physical materials properties. (orig.)

  3. Direct Measurements of Island Growth and Step-Edge Barriers in Colloidal Epitaxy

    KAUST Repository

    Ganapathy, R.; Buckley, M. R.; Gerbode, S. J.; Cohen, I.

    2010-01-01

    -scale particles into microstructures that have numerous technological applications. To determine whether atomic epitaxial growth laws are applicable to the epitaxy of larger particles with attractive interactions, we investigated the nucleation and growth dynamics

  4. Comparison of the growth kinetics of In{sub 2}O{sub 3} and Ga{sub 2}O{sub 3} and their suboxide desorption during plasma-assisted molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Vogt, Patrick, E-mail: vogt@pdi-berlin.de; Bierwagen, Oliver, E-mail: bierwagen@pdi-berlin.de [Paul-Drude-Institut für Festkörperelektronik, Hausvogteiplatz 5–7, D-10117 Berlin (Germany)

    2016-08-08

    We present a comprehensive study of the In{sub 2}O{sub 3} growth kinetics during plasma-assisted molecular beam epitaxy and compare it to that of the related oxide Ga{sub 2}O{sub 3} [P. Vogt and O. Bierwagen, Appl. Phys. Lett. 108, 072101 (2016)]. The growth rate and desorbing fluxes were measured during growth in-situ by a laser reflectometry set-up and line-of-sight quadrupole mass spectrometer, respectively. We extracted the In incorporation as a function of the provided In flux, different growth temperatures T{sub G}, and In-to-O flux ratios r. The data are discussed in terms of the competing formation of In{sub 2}O{sub 3} and desorption of the suboxide In{sub 2}O and O. The same three growth regimes as in the case of Ga{sub 2}O{sub 3} can be distinguished: (i) In-transport limited, O-rich (ii) In{sub 2}O-desorption limited, O-rich, and (iii) O-transport limited, In-rich. In regime (iii), In droplets are formed on the growth surface at low T{sub G}. The growth kinetics follows qualitatively that of Ga{sub 2}O{sub 3} in agreement with their common oxide and suboxide stoichiometry. The quantitative differences are mainly rationalized by the difference in In{sub 2}O and Ga{sub 2}O desorption rates and vapor pressures. For the In{sub 2}O, Ga{sub 2}O, and O desorption, we extracted the activation energies and frequency factors by means of Arrhenius-plots.

  5. Ge films grown on Si substrates by molecular-beam epitaxy below 450 deg. C

    International Nuclear Information System (INIS)

    Liu, J.; Kim, H.J.; Hul'ko, O.; Xie, Y.H.; Sahni, S.; Bandaru, P.; Yablonovitch, E.

    2004-01-01

    Ge thin films are grown on Si(001) substrates by molecular-beam epitaxy at 370 deg. C. The low-temperature epitaxial growth is compatible with the back-end thermal budget of current generation complementary metal-oxide-semiconductor technology, which is restricted to less than 450 deg. C. Reflection high-energy electron diffraction shows that single-crystal Ge thin films with smooth surfaces could be achieved below 450 deg. C. Double-axis x-ray θ/2θ scans also show that the epitaxial Ge films are almost fully strain-relaxed. As expected, cross-sectional transmission electron microscopy shows a network of dislocations at the interface. Hydrogen and oxide desorption techniques are proved to be necessary for improving the quality of the Ge films, which is reflected in improved minority carrier diffusion lengths and exceptionally low leakage currents

  6. High-mobility BaSnO{sub 3} grown by oxide molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Raghavan, Santosh; Schumann, Timo; Kim, Honggyu; Zhang, Jack Y.; Cain, Tyler A.; Stemmer, Susanne, E-mail: stemmer@mrl.ucsb.edu [Materials Department, University of California, Santa Barbara, California 93106-5050 (United States)

    2016-01-01

    High-mobility perovskite BaSnO{sub 3} films are of significant interest as new wide bandgap semiconductors for power electronics, transparent conductors, and as high mobility channels for epitaxial integration with functional perovskites. Despite promising results for single crystals, high-mobility BaSnO{sub 3} films have been challenging to grow. Here, we demonstrate a modified oxide molecular beam epitaxy (MBE) approach, which supplies pre-oxidized SnO{sub x}. This technique addresses issues in the MBE of ternary stannates related to volatile SnO formation and enables growth of epitaxial, stoichiometric BaSnO{sub 3}. We demonstrate room temperature electron mobilities of 150 cm{sup 2} V{sup −1} s{sup −1} in films grown on PrScO{sub 3}. The results open up a wide range of opportunities for future electronic devices.

  7. Effect of III/V ratio on the polarity of AlN and GaN layers grown in the metal rich growth regime on Si(111) by plasma assisted molecular beam epitaxy

    International Nuclear Information System (INIS)

    Agrawal, Manvi; Dharmarasu, Nethaji; Radhakrishnan, K.; Pramana, Stevin Snellius

    2015-01-01

    Wet chemical etching, reflection high energy electron diffraction, scanning electron microscope and convergent beam electron diffraction have been employed to study the polarities of AlN and the subsequently grown GaN as a function of metal flux in the metal rich growth regime. Both AlN and GaN exhibited metal polarity in the intermediate growth conditions. However, in the droplet growth regime, the polarity of AlN and GaN were N polar and Ga polar, respectively. It was observed that Ga polar GaN could be obtained on both Al and N polar AlN. AlGaN/GaN high electron mobility transistor (HEMT) heterostructure exhibiting hall mobility of 900 cm 2 V -1 s -1 and sheet carrier density of 1.2 × 10 13 cm -2 was demonstrated using N polar AlN which confirmed Ga polarity of GaN. Al metal flux was likely to play an important role in controlling the polarity of AlN and determining the polarity of the subsequent GaN grown on Si(111) by plasma assisted molecular beam epitaxy (PA-MBE). (author)

  8. Epitaxial growth with pulsed deposition: Submonolayer scaling and Villain instability

    DEFF Research Database (Denmark)

    Hinnemann, Berit; Hinrichsen, H.; Wolf, D.E.

    2003-01-01

    It has been observed experimentally that under certain conditions, pulsed laser deposition (PLD) produces smoother surfaces than ordinary molecular beam epitaxy (MBE). So far, the mechanism leading to the improved quality of surfaces in PLD is not yet fully understood. In the present work, we...

  9. Reclamation of a molecular beam epitaxy system and conversion for oxide epitaxy

    International Nuclear Information System (INIS)

    Carver, Alexander G.; Henderson, Walter; Doolittle, W. Alan

    2008-01-01

    An early 1980s vintage molecular beam epitaxy system, a Varian Gen II system, originally used for HgCdTe epitaxy, was converted into a system capable of growing thin-film complex metal oxides. The nature of some of the alternative oxides requires a thorough cleaning and, in some cases, complete replacement of system components. Details are provided regarding the chemistry of the etchants used, safety requirements for properly handling, and disposal of large quantities of etchants and etch by-products, and components that can be reused versus components that require replacement are given. Following the given procedures, an ultimate base pressure of 2x10 -10 Torr was obtained. Films grown in the system after reclamation contained no evidence of previously present materials down to the detection limit of secondary ion mass spectrometry

  10. Growth of high purity semiconductor epitaxial layers by liquid phase ...

    Indian Academy of Sciences (India)

    Unknown

    semiconductor materials in high purity form by liquid phase epitaxy (LPE) technique. Various possible sources of impurities in such ... reference to the growth of GaAs layers. The technique of growing very high purity layers ... the inner walls of the gas lines and (e) the containers for storing, handling and cleaning of the mate-.

  11. Gas Source Techniques for Molecular Beam Epitaxy of Highly Mismatched Ge Alloys

    Directory of Open Access Journals (Sweden)

    Chad A. Stephenson

    2016-12-01

    Full Text Available Ge and its alloys are attractive candidates for a laser compatible with silicon integrated circuits. Dilute germanium carbide (Ge1−xCx offers a particularly interesting prospect. By using a precursor gas with a Ge4C core, C can be preferentially incorporated in substitutional sites, suppressing interstitial and C cluster defects. We present a method of reproducible and upscalable gas synthesis of tetrakis(germylmethane, or (H3Ge4C, followed by the design of a hybrid gas/solid-source molecular beam epitaxy system and subsequent growth of defect-free Ge1−xCx by molecular beam epitaxy (MBE. Secondary ion mass spectroscopy, transmission electron microscopy and contactless electroreflectance confirm the presence of carbon with very high crystal quality resulting in a decrease in the direct bandgap energy. This technique has broad applicability to growth of highly mismatched alloys by MBE.

  12. Molecular beam epitaxy growth of In0.52Al0.48As/In0.53Ga0.47As metamorphic high electron mobility transistor employing growth interruption and in situ rapid thermal annealing

    International Nuclear Information System (INIS)

    Ihn, Soo-Ghang; Jo, Seong June; Song, Jong-In

    2006-01-01

    We investigated the effects of high temperature (∼700 deg. C) in situ rapid thermal annealing (RTA) carried out during growth interruption between spacer and δ-doping layers of an In 0.52 Al 0.48 As/In 0.53 Ga 0.47 As metamorphic high electron mobility transistor (MHEMT) grown on a compositionally graded InGaAlAs buffer layer. The in situ RTA improved optical and structural properties of the MHEMT without degradation of transport property, while postgrowth RTA improved the structural property of the MHEMT but significantly degraded mobility due to the defect-assisted Si diffusion. The results indicate the potential of the in situ RTA for use in the growth of high-quality metamorphic epitaxial layers for optoelectronic applications requiring improved optical and electrical properties

  13. Molecular beam epitaxy of three-dimensional Dirac material Sr3PbO

    Science.gov (United States)

    Samal, D.; Nakamura, H.; Takagi, H.

    2016-07-01

    A series of anti-perovskites including Sr3PbO are recently predicted to be a three-dimensional Dirac material with a small mass gap, which may be a topological crystalline insulator. Here, we report the epitaxial growth of Sr3PbO thin films on LaAlO3 using molecular beam epitaxy. X-ray diffraction indicates (001) growth of Sr3PbO, where [110] of Sr3PbO matches [100] of LaAlO3. Measurements of the Sr3PbO films with parylene/Al capping layers reveal a metallic conduction with p-type carrier density of ˜1020 cm-3. The successful growth of high quality Sr3PbO film is an important step for the exploration of its unique topological properties.

  14. Control of ion content and nitrogen species using a mixed chemistry plasma for GaN grown at extremely high growth rates >9 μm/h by plasma-assisted molecular beam epitaxy

    Science.gov (United States)

    Gunning, Brendan P.; Clinton, Evan A.; Merola, Joseph J.; Doolittle, W. Alan; Bresnahan, Rich C.

    2015-10-01

    Utilizing a modified nitrogen plasma source, plasma assisted molecular beam epitaxy (PAMBE) has been used to achieve higher growth rates in GaN. A higher conductance aperture plate, combined with higher nitrogen flow and added pumping capacity, resulted in dramatically increased growth rates up to 8.4 μm/h using 34 sccm of N2 while still maintaining acceptably low operating pressure. It was further discovered that argon could be added to the plasma gas to enhance growth rates up to 9.8 μm/h, which was achieved using 20 sccm of N2 and 7.7 sccm Ar flows at 600 W radio frequency power, for which the standard deviation of thickness was just 2% over a full 2 in. diameter wafer. A remote Langmuir style probe employing the flux gauge was used to indirectly measure the relative ion content in the plasma. The use of argon dilution at low plasma pressures resulted in a dramatic reduction of the plasma ion current by more than half, while high plasma pressures suppressed ion content regardless of plasma gas chemistry. Moreover, different trends are apparent for the molecular and atomic nitrogen species generated by varying pressure and nitrogen composition in the plasma. Argon dilution resulted in nearly an order of magnitude achievable growth rate range from 1 μm/h to nearly 10 μm/h. Even for films grown at more than 6 μm/h, the surface morphology remained smooth showing clear atomic steps with root mean square roughness less than 1 nm. Due to the low vapor pressure of Si, Ge was explored as an alternative n-type dopant for high growth rate applications. Electron concentrations from 2.2 × 1016 to 3.8 × 1019 cm-3 were achieved in GaN using Ge doping, and unintentionally doped GaN films exhibited low background electron concentrations of just 1-2 × 1015 cm-3. The highest growth rates resulted in macroscopic surface features due to Ga cell spitting, which is an engineering challenge still to be addressed. Nonetheless, the dramatically enhanced growth rates demonstrate

  15. Control of ion content and nitrogen species using a mixed chemistry plasma for GaN grown at extremely high growth rates >9 μm/h by plasma-assisted molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Gunning, Brendan P.; Clinton, Evan A.; Merola, Joseph J.; Doolittle, W. Alan, E-mail: alan.doolittle@ece.gatech.edu [Georgia Institute of Technology, Atlanta, Georgia 30332 (United States); Bresnahan, Rich C. [Veeco Instruments, St. Paul, Minnesota 55127 (United States)

    2015-10-21

    Utilizing a modified nitrogen plasma source, plasma assisted molecular beam epitaxy (PAMBE) has been used to achieve higher growth rates in GaN. A higher conductance aperture plate, combined with higher nitrogen flow and added pumping capacity, resulted in dramatically increased growth rates up to 8.4 μm/h using 34 sccm of N{sub 2} while still maintaining acceptably low operating pressure. It was further discovered that argon could be added to the plasma gas to enhance growth rates up to 9.8 μm/h, which was achieved using 20 sccm of N{sub 2} and 7.7 sccm Ar flows at 600 W radio frequency power, for which the standard deviation of thickness was just 2% over a full 2 in. diameter wafer. A remote Langmuir style probe employing the flux gauge was used to indirectly measure the relative ion content in the plasma. The use of argon dilution at low plasma pressures resulted in a dramatic reduction of the plasma ion current by more than half, while high plasma pressures suppressed ion content regardless of plasma gas chemistry. Moreover, different trends are apparent for the molecular and atomic nitrogen species generated by varying pressure and nitrogen composition in the plasma. Argon dilution resulted in nearly an order of magnitude achievable growth rate range from 1 μm/h to nearly 10 μm/h. Even for films grown at more than 6 μm/h, the surface morphology remained smooth showing clear atomic steps with root mean square roughness less than 1 nm. Due to the low vapor pressure of Si, Ge was explored as an alternative n-type dopant for high growth rate applications. Electron concentrations from 2.2 × 10{sup 16} to 3.8 × 10{sup 19} cm{sup −3} were achieved in GaN using Ge doping, and unintentionally doped GaN films exhibited low background electron concentrations of just 1–2 × 10{sup 15} cm{sup −3}. The highest growth rates resulted in macroscopic surface features due to Ga cell spitting, which is an engineering challenge still to be

  16. Control of ion content and nitrogen species using a mixed chemistry plasma for GaN grown at extremely high growth rates >9 μm/h by plasma-assisted molecular beam epitaxy

    International Nuclear Information System (INIS)

    Gunning, Brendan P.; Clinton, Evan A.; Merola, Joseph J.; Doolittle, W. Alan; Bresnahan, Rich C.

    2015-01-01

    Utilizing a modified nitrogen plasma source, plasma assisted molecular beam epitaxy (PAMBE) has been used to achieve higher growth rates in GaN. A higher conductance aperture plate, combined with higher nitrogen flow and added pumping capacity, resulted in dramatically increased growth rates up to 8.4 μm/h using 34 sccm of N 2 while still maintaining acceptably low operating pressure. It was further discovered that argon could be added to the plasma gas to enhance growth rates up to 9.8 μm/h, which was achieved using 20 sccm of N 2 and 7.7 sccm Ar flows at 600 W radio frequency power, for which the standard deviation of thickness was just 2% over a full 2 in. diameter wafer. A remote Langmuir style probe employing the flux gauge was used to indirectly measure the relative ion content in the plasma. The use of argon dilution at low plasma pressures resulted in a dramatic reduction of the plasma ion current by more than half, while high plasma pressures suppressed ion content regardless of plasma gas chemistry. Moreover, different trends are apparent for the molecular and atomic nitrogen species generated by varying pressure and nitrogen composition in the plasma. Argon dilution resulted in nearly an order of magnitude achievable growth rate range from 1 μm/h to nearly 10 μm/h. Even for films grown at more than 6 μm/h, the surface morphology remained smooth showing clear atomic steps with root mean square roughness less than 1 nm. Due to the low vapor pressure of Si, Ge was explored as an alternative n-type dopant for high growth rate applications. Electron concentrations from 2.2 × 10 16 to 3.8 × 10 19 cm −3 were achieved in GaN using Ge doping, and unintentionally doped GaN films exhibited low background electron concentrations of just 1–2 × 10 15 cm −3 . The highest growth rates resulted in macroscopic surface features due to Ga cell spitting, which is an engineering challenge still to be addressed. Nonetheless, the

  17. Vapor-solid-solid grown Ge nanowires at integrated circuit compatible temperature by molecular beam epitaxy

    Science.gov (United States)

    Zhu, Zhongyunshen; Song, Yuxin; Zhang, Zhenpu; Sun, Hao; Han, Yi; Li, Yaoyao; Zhang, Liyao; Xue, Zhongying; Di, Zengfeng; Wang, Shumin

    2017-09-01

    We demonstrate Au-assisted vapor-solid-solid (VSS) growth of Ge nanowires (NWs) by molecular beam epitaxy at the substrate temperature of ˜180 °C, which is compatible with the temperature window for Si-based integrated circuit. Low temperature grown Ge NWs hold a smaller size, similar uniformity, and better fit with Au tips in diameter, in contrast to Ge NWs grown at around or above the eutectic temperature of Au-Ge alloy in the vapor-liquid-solid (VLS) growth. Six ⟨110⟩ growth orientations were observed on Ge (110) by the VSS growth at ˜180 °C, differing from only one vertical growth direction of Ge NWs by the VLS growth at a high temperature. The evolution of NWs dimension and morphology from the VLS growth to the VSS growth is qualitatively explained by analyzing the mechanism of the two growth modes.

  18. Laser molecular beam epitaxy of ZnO thin films and heterostructures

    International Nuclear Information System (INIS)

    Opel, Matthias; Geprägs, Stephan; Althammer, Matthias; Brenninger, Thomas; Gross, Rudolf

    2014-01-01

    We report on the growth of epitaxial ZnO thin films and ZnO-based heterostructures on sapphire substrates by laser molecular beam epitaxy (MBE). We first discuss some recent developments in laser-MBE such as flexible ultraviolet laser beam optics, infrared laser heating systems or the use of atomic oxygen and nitrogen sources, and describe the technical realization of our advanced laser-MBE system. Then we describe the optimization of the deposition parameters for ZnO films such as laser fluence and substrate temperature and the use of buffer layers. The detailed structural characterization by x-ray analysis and transmission electron microscopy shows that epitaxial ZnO thin films with high structural quality can be achieved, as demonstrated by a small out-of-plane and in-plane mosaic spread as well as the absence of rotational domains. We also demonstrate the heteroepitaxial growth of ZnO-based multilayers as a prerequisite for spin transport experiments and the realization of spintronic devices. As an example, we show that TiN/Co/ZnO/Ni/Au multilayer stacks can be grown on (0 0 0 1)-oriented sapphire with good structural quality of all layers and well defined in-plane epitaxial relations. (paper)

  19. Epitaxial growth of semiconducting β-FeSi2 and its application to light-emitting diodes

    International Nuclear Information System (INIS)

    Suemasu, T.; Takakura, K.; Li, Cheng; Ozawa, Y.; Kumagai, Y.; Hasegawa, F.

    2004-01-01

    In this paper, we review the detailed study of epitaxial growth of β-FeSi 2 films by reactive deposition epitaxy (RDE), multilayer technique and molecular beam epitaxy (MBE). The p- and n-type β-FeSi 2 was formed when it was grown under an Fe-rich and an Si-rich condition, respectively. The maximum electron and hole mobilities of the β-FeSi 2 epitaxial films reached 6900 and 13000 cm 2 /V·s for the n- and p-type β-FeSi 2 , respectively, at around 50 K. Room temperature (RT) 1.6 μm electroluminescence (EL) was realized by optimizing the growth conditions for p-Si/β-FeSi 2 particles/n-Si structures prepared by RDE for β-FeSi 2 and by MBE for Si

  20. Cyan laser diode grown by plasma-assisted molecular beam epitaxy

    International Nuclear Information System (INIS)

    Turski, H.; Muziol, G.; Wolny, P.; Cywiński, G.; Grzanka, S.; Sawicka, M.; Perlin, P.; Skierbiszewski, C.

    2014-01-01

    We demonstrate AlGaN-cladding-free laser diodes (LDs), operating in continuous wave (CW) mode at 482 nm grown by plasma-assisted molecular beam epitaxy (PAMBE). The maximum CW output power was 230 mW. LDs were grown on c-plane GaN substrates obtained by hydride vapor phase epitaxy. The PAMBE process was carried out in metal-rich conditions, supplying high nitrogen flux (Φ N ) during quantum wells (QWs) growth. We found that high Φ N improves quality of high In content InGaN QWs. The role of nitrogen in the growth of InGaN on (0001) GaN surface as well as the influence of LDs design on threshold current density are discussed

  1. Liquid phase epitaxial growth of heterostructured hierarchical MOF thin films

    KAUST Repository

    Chernikova, Valeriya; Shekhah, Osama; Spanopoulos, Ioannis; Trikalitis, Pantelis N.; Eddaoudi, Mohamed

    2017-01-01

    Precise control of epitaxial growth of MOF-on-MOF thin films, for ordered hierarchical tbo-type structures is demonstrated. The heterostructured MOF thin film was fabricated by successful sequential deposition of layers from two different MOFs. The 2-periodic layers, edge-transitive 4,4-square lattices regarded as supermolecular building layers, were commendably cross-linked using a combination of inorganic/organic and organic pillars.

  2. Liquid phase epitaxial growth of heterostructured hierarchical MOF thin films

    KAUST Repository

    Chernikova, Valeriya

    2017-05-10

    Precise control of epitaxial growth of MOF-on-MOF thin films, for ordered hierarchical tbo-type structures is demonstrated. The heterostructured MOF thin film was fabricated by successful sequential deposition of layers from two different MOFs. The 2-periodic layers, edge-transitive 4,4-square lattices regarded as supermolecular building layers, were commendably cross-linked using a combination of inorganic/organic and organic pillars.

  3. Epitaxial growth on porous GaAs substrates

    Czech Academy of Sciences Publication Activity Database

    Grym, Jan; Nohavica, Dušan; Gladkov, Petar; Hulicius, Eduard; Pangrác, Jiří; Piksová, K.

    2013-01-01

    Roč. 16, č. 1 (2013), s. 59-64 ISSN 1631-0748 R&D Projects: GA ČR GAP102/10/1201; GA ČR GAP108/10/0253 Institutional support: RVO:67985882 ; RVO:68378271 Keywords : Electrochemical etching * Porous semiconductors * Epitaxial growth * GaAs Subject RIV: BH - Optics, Masers, Lasers; JA - Electronics ; Optoelectronics, Electrical Engineering (FZU-D) Impact factor: 1.483, year: 2013

  4. Epitaxial growth of lithium fluoride on the (1 1 1) surface of CaF 2

    Science.gov (United States)

    Klumpp, St; Dabringhaus, H.

    1999-08-01

    Growth of lithium fluoride by molecular beam epitaxy on the (1 1 1) surface of calcium fluoride crystals was studied by TEM and LEED for crystal temperatures from 400 to 773 K and impinging lithium fluoride fluxes from 3×10 11 to 3×10 14 cm -2 s -1. Growth starts, usually, at the steps on the (1 1 1) surface of CaF 2. For larger step distances and at later growth stages also growth on the terraces between the steps is found. Preferably, longish, roof-like crystallites are formed, which can be interpreted by growth of LiF(2 0 1¯)[0 1 0] parallel to CaF 2(1 1 1)[ 1¯ 0 1]. To a lesser extent square crystallites, i.e. growth with LiF(0 0 1), and, rarely, three-folded pyramidal crystallites, i.e. growth with LiF(1 1 1) parallel to CaF 2(1 1 1), are observed. While the pyramidal crystallites show strict epitaxial orientation with LiF[ 1¯ 0 1]‖CaF 2[ 1¯ 0 1] and LiF[ 1¯ 0 1]‖CaF 2[1 2¯ 1], only about 80% of the square crystallites exhibit an epitaxial alignment, where LiF[1 0 0]‖CaF 2[ 1¯ 0 1] is preferred to LiF[1 1 0]‖CaF 2[ 1¯ 0 1]. The epitaxial relationships are discussed on the basis of theoretically calculated adsorption positions of the lithium fluoride monomer and dimer on the terrace and at the steps of the CaF 2(1 1 1) surface.

  5. Layered growth model and epitaxial growth structures for SiCAlN alloys

    International Nuclear Information System (INIS)

    Liu Zhaoqing; Ni Jun; Su Xiaoao; Dai Zhenhong

    2009-01-01

    Epitaxial growth structures for (SiC) 1-x (AlN) x alloys are studied using a layered growth model. First-principle calculations are used to determine the parameters in the layered growth model. The phase diagrams of epitaxial growth are given. There is a rich variety of the new metastable polytype structures at x=1/6 ,1/5 ,1/4 ,1/3 , and 1/2 in the layered growth phase diagrams. We have also calculated the electronic properties of the short periodical SiCAlN alloys predicted by our layered growth model. The results show that various ordered structures of (SiC) 1-x (AlN) x alloys with the band gaps over a wide range are possible to be synthesized by epitaxial growth.

  6. Self-assembled InAs quantum dots formed by molecular beam epitaxy at low temperature and postgrowth annealing

    NARCIS (Netherlands)

    Zhan, H.H.; Nötzel, R.; Hamhuis, G.J.; Eijkemans, T.J.; Wolter, J.H.

    2003-01-01

    Self-assembled InAs quantum dots are grown at low temperature (LT) by molecular beam epitaxy (MBE) on GaAs substrates. The growth is in situ monitored by reflection high-energy electron diffraction, and ex situ evaluated by atomic force microscopy for the morphological properties, and by

  7. Molecular-beam epitaxy on shallow mesa gratings patterned on GaAs(311)A and (100) substrates

    NARCIS (Netherlands)

    Gong, Q.; Nötzel, R.; Schönherr, H.-P.; Ploog, K.H.

    2002-01-01

    We report on the morphology and properties of the surface formed by molecular-beam epitaxy on shallow mesa gratings on patterned GaAs(311)A and GaAs(100). On GaAs(311)A substrates, the corrugated surface formed after GaAs growth on shallow mesa gratings along [011] is composed of monolayer high

  8. Growth and characterization of Hg 1– Cd Te epitaxial films by ...

    Indian Academy of Sciences (India)

    Growth of Hg1–CdTe epitaxial films by a new technique called asymmetric vapour phase epitaxy (ASVPE) has been carried out on CdTe and CZT substrates. The critical problems faced in normal vapour phase epitaxy technique like poor surface morphology, composition gradient and dislocation multiplication have ...

  9. Growth and characterization of Hg1–xCdxTe epitaxial films by ...

    Indian Academy of Sciences (India)

    Unknown

    Abstract. Growth of Hg1–xCdxTe epitaxial films by a new technique called asymmetric vapour phase epitaxy. (ASVPE) has been carried out on CdTe and CZT substrates. The critical problems faced in normal vapour phase epitaxy technique like poor surface morphology, composition gradient and dislocation multiplication.

  10. Direct Measurements of Island Growth and Step-Edge Barriers in Colloidal Epitaxy

    KAUST Repository

    Ganapathy, R.

    2010-01-21

    Epitaxial growth, a bottom-up self-assembly process for creating surface nano- and microstructures, has been extensively studied in the context of atoms. This process, however, is also a promising route to self-assembly of nanometer- and micrometer-scale particles into microstructures that have numerous technological applications. To determine whether atomic epitaxial growth laws are applicable to the epitaxy of larger particles with attractive interactions, we investigated the nucleation and growth dynamics of colloidal crystal films with single-particle resolution. We show quantitatively that colloidal epitaxy obeys the same two-dimensional island nucleation and growth laws that govern atomic epitaxy. However, we found that in colloidal epitaxy, step-edge and corner barriers that are responsible for film morphology have a diffusive origin. This diffusive mechanism suggests new routes toward controlling film morphology during epitaxy.

  11. European Conference on Molecular Beam Epitaxy and Related Growth Methods (6th) Held in Tampere, Finland on 21-14 April 1991

    Science.gov (United States)

    1991-04-24

    2X2) structure caracteristic of a cation rich surface. During the growth we observe intense RHEED oscillations, which show that the growth of Hg...layer which then suffers plastic deformation when the energy stored in the epilayer (proportional to its thickness) is sufficient to create dislocations...table I we present the variation of the in plane lattice mismatch vs. layerthickness. Plastic deformation of the layer starts around 4 to 5 ML, which can

  12. SiC epitaxy growth using chloride-based CVD

    International Nuclear Information System (INIS)

    Henry, Anne; Leone, Stefano; Beyer, Franziska C.; Pedersen, Henrik; Kordina, Olof; Andersson, Sven; Janzén, Erik

    2012-01-01

    The growth of thick epitaxial SiC layers needed for high-voltage, high-power devices is investigated with the chloride-based chemical vapor deposition. High growth rates exceeding 100 μm/h can be obtained, however to obtain device quality epilayers adjustments of the process parameters should be carried out appropriately for the chemistry used. Two different chemistry approaches are compared: addition of hydrogen chloride to the standard precursors or using methyltrichlorosilane, a molecule that contains silicon, carbon and chlorine. Optical and electrical techniques are used to characterize the layers.

  13. High quality atomically thin PtSe2 films grown by molecular beam epitaxy

    Science.gov (United States)

    Yan, Mingzhe; Wang, Eryin; Zhou, Xue; Zhang, Guangqi; Zhang, Hongyun; Zhang, Kenan; Yao, Wei; Lu, Nianpeng; Yang, Shuzhen; Wu, Shilong; Yoshikawa, Tomoki; Miyamoto, Koji; Okuda, Taichi; Wu, Yang; Yu, Pu; Duan, Wenhui; Zhou, Shuyun

    2017-12-01

    Atomically thin PtSe2 films have attracted extensive research interests for potential applications in high-speed electronics, spintronics and photodetectors. Obtaining high quality thin films with large size and controlled thickness is critical. Here we report the first successful epitaxial growth of high quality PtSe2 films by molecular beam epitaxy. Atomically thin films from 1 ML to 22 ML have been grown and characterized by low-energy electron diffraction, Raman spectroscopy and x-ray photoemission spectroscopy. Moreover, a systematic thickness dependent study of the electronic structure is revealed by angle-resolved photoemission spectroscopy (ARPES), and helical spin texture is revealed by spin-ARPES. Our work provides new opportunities for growing large size single crystalline films to investigate the physical properties and potential applications of PtSe2.

  14. Real time ellipsometry for monitoring plasma-assisted epitaxial growth of GaN

    Energy Technology Data Exchange (ETDEWEB)

    Bruno, Giovanni [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy); Losurdo, Maria [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy)]. E-mail: maria.losurdo@ba.imip.cnr.it; Giangregorio, Maria M. [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy); Capezzuto, Pio [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy); Brown, April S. [Department of Electrical and Computer Engineering, Duke University, 128 Hudson Hall, Durham, NC (United States); Kim, Tong-Ho [Department of Electrical and Computer Engineering, Duke University, 128 Hudson Hall, Durham, NC (United States); Choi, Soojeong [Department of Electrical and Computer Engineering, Duke University, 128 Hudson Hall, Durham, NC (United States)

    2006-10-31

    GaN is grown on Si-face 4H-SiC(0 0 0 1) substrates using remote plasma-assisted methods including metalorganic chemical vapour deposition (RP-MOCVD) and molecular beam epitaxy (MBE). Real time spectroscopic ellipsometry is used for monitoring all the steps of substrate pre-treatments and the heteroepitaxial growth of GaN on SiC. Our characterization emphasis is on understanding the nucleation mechanism and the GaN growth mode, which depend on the SiC surface preparation.

  15. Importance of growth temperature on achieving lattice-matched and strained InAlN/GaN heterostructure by plasma-assisted molecular beam epitaxy

    Directory of Open Access Journals (Sweden)

    K. Jeganathan

    2014-09-01

    Full Text Available We investigate the role of growth temperature on the optimization of lattice-matched In0.17Al0.83N/GaN heterostructure and its structural evolutions along with electrical transport studies. The indium content gradually reduces with the increase of growth temperature and approaches lattice-matched with GaN having very smooth and high structural quality at 450ºC. The InAlN layers grown at high growth temperature (480ºC retain very low Indium content of ∼ 4 % in which cracks are mushroomed due to tensile strain while above lattice matched (>17% layers maintain crack-free compressive strain nature. The near lattice-matched heterostructure demonstrate a strong carrier confinement with very high two-dimensional sheet carrier density of ∼2.9 × 1013 cm−2 with the sheet resistance of ∼450 Ω/□ at room temperature as due to the manifestation of spontaneous polarization charge differences between InAlN and GaN layers.

  16. Raman investigation of GaP–Si interfaces grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Bondi, A.; Cornet, C.; Boyer, S.; Nguyen Thanh, T.; Létoublon, A.; Pedesseau, L.; Durand, O. [Université Européenne de Bretagne, INSA, FOTON, UMR CNRS 6082, 20 Avenue des Buttes de Coësmes, F-35708 Rennes (France); Moreac, A. [Institut de Physique de Rennes, UMR-CNRS n°6251, Université Rennes1, Campus de Beaulieu — 35042 Rennes cedex (France); Ponchet, A. [CEMES, UPR CNRS 8011, F-31055 Toulouse (France); Le Corre, A. [Université Européenne de Bretagne, INSA, FOTON, UMR CNRS 6082, 20 Avenue des Buttes de Coësmes, F-35708 Rennes (France); Even, J., E-mail: jacky.even@insa.rennes.fr [Université Européenne de Bretagne, INSA, FOTON, UMR CNRS 6082, 20 Avenue des Buttes de Coësmes, F-35708 Rennes (France)

    2013-08-31

    Raman spectroscopy was used to investigate the residual strain in thin GaP layers deposited on Si substrates by molecular beam epitaxy. Different growth conditions were used to obtain a clean GaP–Si interface, including migration enhanced epitaxy. The strain induced Raman shifts of the longitudinal and the transverse optical GaP lattice modes were analyzed. The effects of crystalline defects are discussed, supported by high resolution transmission electron microscopy and X-ray scattering studies. Finally, Raman Spectroscopy reveals the presence of disorder (or surface)-activated optical phonons. This result is discussed in the light of surface morphology analyses. - Highlights: ► GaP thin layers grown by molecular beam epitaxy on Si substrates. ► Strain-induced Raman shifts of the optical GaP modes are analyzed. ► Simulation of optical GaP modes by density functional perturbation theory. ► Comparison with X-ray diffraction and electron and scanning probe microscopy data.

  17. Nanoscale abnormal grain growth in (001) epitaxial ceria

    International Nuclear Information System (INIS)

    Solovyov, Vyacheslav F.; Develos-Bagarinao, Katherine; Nykypanchuk, Dmytro

    2009-01-01

    X-ray reciprocal-space mapping and atomic force microscopy (AFM) are used to study kinetics and mechanisms of lateral grain growth in epitaxial (001) ceria (CeO 2 ) deposited by pulsed laser deposition on (001) yttria-stabilized zirconia (YSZ) and (12 lowbar 10) (r-cut) sapphire. Rate and character of the grain growth during postannealing at 1050 deg. C are found to be strongly dependent on the type of the epitaxial substrate. Films deposited on YSZ exhibit signatures of normal grain growth, which stagnated after the lateral grain size reaches 40 nm, consistent with the grain-boundary pinning by the thermal grooving. In contrast, when r-cut sapphire substrate was used, abnormal (secondary) grain growth is observed. A small population of grains grow to well over 100 nm consuming smaller, 100 nm large (001) terminations and rendering the sample single-crystalline quality. The grain growth is accompanied by reduction in lateral rms strain, resulting in a universal grain size--rms strain dependence. Analysis of the AFM and x-ray diffraction data leads to the conclusion that bimodal initial grain population consisting of grains with very different sizes is responsible for initiation of the abnormal growth in (001) CeO 2 films on r-cut sapphire. Due to different surface chemistry, when a YSZ substrate is used, the initial grain distribution is monomodal, therefore only normal growth is active. We demonstrate that a 2.2 deg. miscut of the sapphire substrate eliminates the large-grain population, thus suppressing abnormal grain growth. It is concluded that utilization of abnormal grain growth is a promising way for synthesis of large (001) ceria terminations.

  18. Big-data reflection high energy electron diffraction analysis for understanding epitaxial film growth processes.

    Science.gov (United States)

    Vasudevan, Rama K; Tselev, Alexander; Baddorf, Arthur P; Kalinin, Sergei V

    2014-10-28

    Reflection high energy electron diffraction (RHEED) has by now become a standard tool for in situ monitoring of film growth by pulsed laser deposition and molecular beam epitaxy. Yet despite the widespread adoption and wealth of information in RHEED images, most applications are limited to observing intensity oscillations of the specular spot, and much additional information on growth is discarded. With ease of data acquisition and increased computation speeds, statistical methods to rapidly mine the data set are now feasible. Here, we develop such an approach to the analysis of the fundamental growth processes through multivariate statistical analysis of a RHEED image sequence. This approach is illustrated for growth of La(x)Ca(1-x)MnO(3) films grown on etched (001) SrTiO(3) substrates, but is universal. The multivariate methods including principal component analysis and k-means clustering provide insight into the relevant behaviors, the timing and nature of a disordered to ordered growth change, and highlight statistically significant patterns. Fourier analysis yields the harmonic components of the signal and allows separation of the relevant components and baselines, isolating the asymmetric nature of the step density function and the transmission spots from the imperfect layer-by-layer (LBL) growth. These studies show the promise of big data approaches to obtaining more insight into film properties during and after epitaxial film growth. Furthermore, these studies open the pathway to use forward prediction methods to potentially allow significantly more control over growth process and hence final film quality.

  19. Molecular beam epitaxy of GeTe-Sb2Te3 phase change materials studied by X-ray diffraction

    International Nuclear Information System (INIS)

    Shayduk, Roman

    2010-01-01

    The integration of phase change materials into semiconductor heterostructures may lead to the development of a new generation of high density non-volatile phase change memories. Epitaxial phase change materials allow to study the detailed structural changes during the phase transition and to determine the scaling limits of the memory. This work is dedicated to the epitaxial growth of Ge-Sb-Te phase change alloys on GaSb(001). We deposit Ge-Sb-Te (GST) films on GaSb(001) substrates by means of molecular beam epitaxy (MBE). The film orientation and lattice constant evolution is determined in real time during growth using grazing incidence X-ray diffraction (GID). The nucleation stage of the growth is studied in situ using reflection high energy electron diffraction (RHEED). Four growth regimes of GST on GaSb(001) were observed: amorphous, polycrystalline, incubated epitaxial and direct epitaxial. Amorphous film grows for substrate temperatures below 100 C. For substrate temperatures in the range 100-160 C, the film grows in polycrystalline form. Incubated epitaxial growth is observed at temperatures from 180 to 210 C. This growth regime is characterized by an initial 0.6nm thick amorphous layer formation, which crystallizes epitaxially as the film thickness increases. The determined lattice constant of the films is 6.01 A, very close to that of the metastable GST phase. The films predominantly possess an epitaxial cube-on-cube relationship. At higher temperatures the films grow epitaxially, however the growth rate is rapidly decreasing with temperature. At temperatures above 270 C the growth rate is zero. The composition of the grown films is close to 2:2:5 for Ge, Sb and Te, respectively. The determined crystal structure of the films is face centered cubic (FCC) with a rhombohedral distortion. The analysis of X-ray peak widths gives a value for the rhombohedral angle of 89.56 . We observe two types of reflections in reciprocal space indicating two FCC sublattices in

  20. Origin of green luminescence in ZnO thin film grown by molecular-beam epitaxy

    International Nuclear Information System (INIS)

    Heo, Y.W.; Norton, D.P.; Pearton, S.J.

    2005-01-01

    The properties of ZnO films grown by molecular-beam epitaxy are reported. The primary focus was on understanding the origin of deep-level luminescence. A shift in deep-level emission from green to yellow is observed with reduced Zn pressure during the growth. Photoluminescence and Hall measurements were employed to study correlations between deep-level/near-band-edge emission and carrier density. With these results, we suggest that the green emission is related to donor-deep acceptor (Zn vacancy V Zn - ) and the yellow to donor-deep acceptor (oxygen vacancy, O i - )

  1. Low defect densities in molecular beam epitaxial GaAs achieved by isoelectronic In doping

    Science.gov (United States)

    Bhattacharya, P. K.; Dhar, S.; Berger, P.; Juang, F.-Y.

    1986-01-01

    A study has been made of the effects of adding small amounts of In (0.2-1.2 pct) to GaAs grown by molecular beam epitaxy. The density of four electron traps decreases in concentration by an order of magnitude, and the peak intensities of prominent emissions in the excitonic spectra are reduced with increase in In content. Based on the higher surface migration rate of In, compared to Ga, at the growth temperatures it is apparent that the traps and the excitonic transitions are related to point defects. This agrees with earlier observations by Briones and Collins (1982) and Skromme et al. (1985).

  2. Epitaxial properties of ZnO thin films on SrTiO3 substrates grown by laser molecular beam epitaxy

    International Nuclear Information System (INIS)

    Wei, X. H.; Li, Y. R.; Zhu, J.; Huang, W.; Zhang, Y.; Luo, W. B.; Ji, H.

    2007-01-01

    Epitaxial ZnO thin films with different orientations have been grown by laser molecular beam epitaxy on (001)- (011)-, and (111)-orientated SrTiO 3 single-crystal substrates. The growth behavior was in situ monitored by reflection high-energy electron diffraction, and the epitaxial orientation relations were reconfirmed by ex situ x-ray diffraction measurements. In the case of ZnO on SrTiO 3 (001), four orthogonal domains coexisted in the ZnO epilayer, i.e., ZnO(110) parallel SrTiO 3 (001) and ZnO[-111] parallel SrTiO 3 . For (011)- and (111)-orientated substrates, single-domain epitaxy with c axial orientation was observed, in which the in-plane relationship was ZnO[110] parallel SrTiO 3 [110] irrespective of the substrate orientations. Additionally, the crystalline quality of ZnO on SrTiO 3 (111) was better than that of ZnO on SrTiO 3 (011) because of the same symmetry between the (111) substrates and (001) films. The obtained results can be attributed to the difference of the in-plane crystallographic symmetry. Furthermore, those alignments can be explained by the interface stress between the substrates and the films

  3. Epitaxy physical principles and technical implementation

    CERN Document Server

    Herman, Marian A; Sitter, Helmut

    2004-01-01

    Epitaxy provides readers with a comprehensive treatment of the modern models and modifications of epitaxy, together with the relevant experimental and technological framework. This advanced textbook describes all important aspects of the epitaxial growth processes of solid films on crystalline substrates, including a section on heteroepitaxy. It covers and discusses in details the most important epitaxial growth techniques, which are currently widely used in basic research as well as in manufacturing processes of devices, namely solid-phase epitaxy, liquid-phase epitaxy, vapor-phase epitaxy, including metal-organic vapor-phase epitaxy and molecular-beam epitaxy. Epitaxy’s coverage of science and texhnology thin-film is intended to fill the need for a comprehensive reference and text examining the variety of problems related to the physical foundations and technical implementation of epitaxial crystallization. It is intended for undergraduate students, PhD students, research scientists, lecturers and practic...

  4. Improvement of GaN epilayer by gradient layer method with molecular-beam epitaxy

    International Nuclear Information System (INIS)

    Chen, Yen-Liang; Lo, Ikai; Gau, Ming-Hong; Hsieh, Chia-Ho; Sham, Meng-Wei; Pang, Wen-Yuan; Hsu, Yu-Chi; Tsai, Jenn-Kai; Schuber, Ralf; Schaadt, Daniel

    2012-01-01

    We demonstrated a molecular beam epitaxy method to resolve the dilemma between structural and morphological quality in growth of the GaN epilayer. A gradient buffer layer was grown in such a way that the N/Ga ratio was gradually changed from nitrogen-rich to gallium-rich. The GaN epitaxial layer was then grown on the gradient buffer layer. In the X-ray diffraction analysis of GaN(002) rocking curves, we found that the full width at half-maximum was improved from 531.69″ to 59.43″ for the sample with a gradient buffer layer as compared to a purely gallium-rich grown sample. Atomic force microscopy analysis showed that the root-mean-square roughness of the surface was improved from 18.28 nm to 1.62 nm over an area of 5 × 5 μm 2 with respect to a purely nitrogen-rich grown sample. Raman scattering showed the presence of a slightly tilted plane in the gradient layer. Furthermore we showed that the gradient layer can also slash the strain force caused by either Ga-rich GaN epitaxial layer or AlN buffer layer. - Highlights: ► The samples were grown by plasma-assisted molecular beam epitaxy. ► The GaN epilayer was grown on sapphire substrate. ► The samples were characterized by X-ray diffraction and atomic force microscopy. ► The sample quality was improved by gradient buffer layer.

  5. Improvement of GaN epilayer by gradient layer method with molecular-beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Yen-Liang [Department of Physics, Institute of Material Science and Engineering, Center for Nanoscience and Nanotechnology, National Sun Yat-Sen University, Kaohsiung 80424, Taiwan, ROC (China); Lo, Ikai, E-mail: ikailo@mail.phys.nsysu.edu.tw [Department of Physics, Institute of Material Science and Engineering, Center for Nanoscience and Nanotechnology, National Sun Yat-Sen University, Kaohsiung 80424, Taiwan, ROC (China); Gau, Ming-Hong; Hsieh, Chia-Ho; Sham, Meng-Wei; Pang, Wen-Yuan; Hsu, Yu-Chi [Department of Physics, Institute of Material Science and Engineering, Center for Nanoscience and Nanotechnology, National Sun Yat-Sen University, Kaohsiung 80424, Taiwan, ROC (China); Tsai, Jenn-Kai [Department of Electronics Engineering, National Formosa University, Hu-Wei, Yun-Lin County 63208, Taiwan, ROC (China); Schuber, Ralf; Schaadt, Daniel [Institute of Applied Physics/DFG-Center for Functional Nanostructures (CFN), Karlsruhe Institute of Technology (KIT), Karlsruhe (Germany)

    2012-07-31

    We demonstrated a molecular beam epitaxy method to resolve the dilemma between structural and morphological quality in growth of the GaN epilayer. A gradient buffer layer was grown in such a way that the N/Ga ratio was gradually changed from nitrogen-rich to gallium-rich. The GaN epitaxial layer was then grown on the gradient buffer layer. In the X-ray diffraction analysis of GaN(002) rocking curves, we found that the full width at half-maximum was improved from 531.69 Double-Prime to 59.43 Double-Prime for the sample with a gradient buffer layer as compared to a purely gallium-rich grown sample. Atomic force microscopy analysis showed that the root-mean-square roughness of the surface was improved from 18.28 nm to 1.62 nm over an area of 5 Multiplication-Sign 5 {mu}m{sup 2} with respect to a purely nitrogen-rich grown sample. Raman scattering showed the presence of a slightly tilted plane in the gradient layer. Furthermore we showed that the gradient layer can also slash the strain force caused by either Ga-rich GaN epitaxial layer or AlN buffer layer. - Highlights: Black-Right-Pointing-Pointer The samples were grown by plasma-assisted molecular beam epitaxy. Black-Right-Pointing-Pointer The GaN epilayer was grown on sapphire substrate. Black-Right-Pointing-Pointer The samples were characterized by X-ray diffraction and atomic force microscopy. Black-Right-Pointing-Pointer The sample quality was improved by gradient buffer layer.

  6. New phenomena in epitaxial growth: solid films on quasicrystalline substrates

    International Nuclear Information System (INIS)

    Fournee, V; Thiel, P A

    2005-01-01

    An overview is given of the research conducted in the field of solid film growth on quasiperiodic surfaces. An atomistic description of quasicrystalline surfaces is presented and discussed in relation to bulk structural models. The various systems for which thin film growth has been attempted so far are reviewed. Emphasis is placed on the nucleation mechanisms of the solid films, on their growth modes in relation to the nature of the deposited metals, on the possibility of intermixing or alloying at the interface and on the epitaxial relationships at the crystal-quasicrystal interfaces. We also describe situations where the deposited elements adopt a quasiperiodic structure, which opens up the possibility of extending our understanding of the relation between quasiperiodicity and the physical properties of such structurally and chemically complex solids. (topical review)

  7. The competing oxide and sub-oxide formation in metal-oxide molecular beam epitaxy

    International Nuclear Information System (INIS)

    Vogt, Patrick; Bierwagen, Oliver

    2015-01-01

    The hetero-epitaxial growth of the n-type semiconducting oxides β-Ga 2 O 3 , In 2 O 3 , and SnO 2 on c- and r-plane sapphire was performed by plasma-assisted molecular beam epitaxy. The growth-rate and desorbing flux from the substrate were measured in-situ under various oxygen to metal ratios by laser reflectometry and quadrupole mass spectrometry, respectively. These measurements clarified the role of volatile sub-oxide formation (Ga 2 O, In 2 O, and SnO) during growth, the sub-oxide stoichiometry, and the efficiency of oxide formation for the three oxides. As a result, the formation of the sub-oxides decreased the growth-rate under metal-rich growth conditions and resulted in etching of the oxide film by supplying only metal flux. The flux ratio for the exclusive formation of the sub-oxide (e.g., the p-type semiconductor SnO) was determined, and the efficiency of oxide formation was found to be the highest for SnO 2 , somewhat lower for In 2 O 3 , and the lowest for Ga 2 O 3 . Our findings can be generalized to further oxides that possess related sub-oxides

  8. P-N junction solar cell grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Hazrati Fard, M.

    2001-01-01

    Growth of GaAs epilayers by Molecular Beam Epitaxy was accomplished for the first time in Iran. The layers were grown on GaAs (001) substrates (p+ wafer) with Si impurity for p n junction solar cell fabrication at a rate of nearly one micron per hour and 0.25 micron per quarter. Crystalline quality of grown layers had been monitored during growth by Reflection High Energy Electron Diffraction system. Doping profile and layer thickness was assessed by electrochemical C-V profiling method. Then Hall measurements were conducted on small samples both in room temperature and liquid nitrogen temperature so giving average carrier concentration and compensation ratio. The results as like: V oc , I sc , F F, η were comparable with other laboratory reports. information for obtaining good and repeatable growths was collected. Therefore, the conditions of repeatable quality growth p n junction solar cells onto GaAs (001) substrates were determined

  9. In situ surface/interface x-ray diffractometer for oxide molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Lee, J. H.; Freeland, J. W.; Hong, Hawoong, E-mail: hhong@aps.anl.gov [Advanced Photon Source, Argonne National Laboratory, Argonne, Illinois 60439 (United States); Tung, I. C. [Advanced Photon Source, Argonne National Laboratory, Argonne, Illinois 60439 (United States); Department of Materials Science and Engineering, Northwestern University, Evanston, Illinois 60208 (United States); Chang, S.-H.; Bhattacharya, A.; Fong, D. D. [Materials Science Division, Argonne National Laboratory, Argonne, Illinois 60439 (United States)

    2016-01-15

    In situ studies of oxide molecular beam epitaxy by synchrotron x-ray scattering has been made possible by upgrading an existing UHV/molecular beam epitaxy (MBE) six-circle diffractometer system. For oxide MBE growth, pure ozone delivery to the chamber has been made available, and several new deposition sources have been made available on a new 12 in. CF (ConFlat, a registered trademark of Varian, Inc.) flange. X-ray diffraction has been used as a major probe for film growth and structures for the system. In the original design, electron diffraction was intended for the secondary diagnostics available without the necessity of the x-ray and located at separate positions. Deposition of films was made possible at the two diagnostic positions. And, the aiming of the evaporation sources is fixed to the point between two locations. Ozone can be supplied through two separate nozzles for each location. Also two separate thickness monitors are installed. Additional features of the equipment are also presented together with the data taken during typical oxide film growth to illustrate the depth of information available via in situ x-ray techniques.

  10. In situ surface/interface x-ray diffractometer for oxide molecular beam epitaxy

    International Nuclear Information System (INIS)

    Lee, J. H.; Freeland, J. W.; Hong, Hawoong; Tung, I. C.; Chang, S.-H.; Bhattacharya, A.; Fong, D. D.

    2016-01-01

    In situ studies of oxide molecular beam epitaxy by synchrotron x-ray scattering has been made possible by upgrading an existing UHV/molecular beam epitaxy (MBE) six-circle diffractometer system. For oxide MBE growth, pure ozone delivery to the chamber has been made available, and several new deposition sources have been made available on a new 12 in. CF (ConFlat, a registered trademark of Varian, Inc.) flange. X-ray diffraction has been used as a major probe for film growth and structures for the system. In the original design, electron diffraction was intended for the secondary diagnostics available without the necessity of the x-ray and located at separate positions. Deposition of films was made possible at the two diagnostic positions. And, the aiming of the evaporation sources is fixed to the point between two locations. Ozone can be supplied through two separate nozzles for each location. Also two separate thickness monitors are installed. Additional features of the equipment are also presented together with the data taken during typical oxide film growth to illustrate the depth of information available via in situ x-ray techniques

  11. Molecular beam epitaxy of LiMnAs

    Czech Academy of Sciences Publication Activity Database

    Novák, Vít; Cukr, Miroslav; Šobáň, Zbyněk; Jungwirth, Tomáš; Martí, X.; Holý, V.; Horodyská, P.; Němec, P.

    2011-01-01

    Roč. 323, č. 1 (2011), s. 348-350 ISSN 0022-0248 R&D Projects: GA MŠk LC510; GA AV ČR KAN400100652; GA MŠk(CZ) 7E08087 EU Projects: European Commission(XE) 215368 - SemiSpinNet; European Commission(XE) 214499 - NAMASTE Grant - others:AV ČR(CZ) AP0801 Program:Akademická prémie - Praemium Academiae Institutional research plan: CEZ:AV0Z10100520; CEZ:AV0Z10100521 Keywords : crystal structure * molecular beam epitaxy * lithium compounds * magnetic semiconductors Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.726, year: 2011

  12. Self-consistent expansion for the molecular beam epitaxy equation.

    Science.gov (United States)

    Katzav, Eytan

    2002-03-01

    Motivated by a controversy over the correct results derived from the dynamic renormalization group (DRG) analysis of the nonlinear molecular beam epitaxy (MBE) equation, a self-consistent expansion for the nonlinear MBE theory is considered. The scaling exponents are obtained for spatially correlated noise of the general form D(r-r('),t-t('))=2D(0)[r-->-r(')](2rho-d)delta(t-t(')). I find a lower critical dimension d(c)(rho)=4+2rho, above which the linear MBE solution appears. Below the lower critical dimension a rho-dependent strong-coupling solution is found. These results help to resolve the controversy over the correct exponents that describe nonlinear MBE, using a reliable method that proved itself in the past by giving reasonable results for the strong-coupling regime of the Kardar-Parisi-Zhang system (for d>1), where DRG failed to do so.

  13. Disorder and defect formation mechanisms in molecular-beam-epitaxy grown silicon epilayers

    International Nuclear Information System (INIS)

    Akbari-Sharbaf, Arash; Baribeau, Jean-Marc; Wu, Xiaohua; Lockwood, David J.; Fanchini, Giovanni

    2013-01-01

    We investigate the role of disorder, stress and crystallite size in determining the density of defects in disordered and partially ordered silicon thin films deposited at low or moderate temperatures by molecular beam epitaxy. We find that the paramagnetic defect density measured by electron spin resonance (ESR) is strongly dependent on the growth temperature of the films, decreasing from ∼ 2 · 10 19 cm −3 at 98 °C to ∼ 1 · 10 18 cm −3 at 572 °C. The physical nature of the defects is strongly dependent on the range of order in the films: ESR spectra consistent with dangling bonds in an amorphous phase are observed at the lowest temperatures, while the ESR signal gradually becomes more anisotropic as medium-range order improves and the stress level (measured both by X-ray diffraction and Raman spectroscopy) is released in more crystalline films. Anisotropic ESR spectra consistent with paramagnetic defects embedded in an epitaxial phase are observed at the highest growth temperature (572 °C). - Highlights: ► Disordered Si epilayers were grown by molecular beam epitaxy. ► Growth has been carried out at temperatures T = 98 °C–514 °C. ► A correlation between defect density and disorder in the films has been found. ► Lack of medium range order and stress cause the formation of defects at low T. ► At high T, defects are associated to grain boundaries and oriented stacking faults

  14. Epitaxial Growth of an Organic p-n Heterojunction: C60 on Single-Crystal Pentacene.

    Science.gov (United States)

    Nakayama, Yasuo; Mizuno, Yuta; Hosokai, Takuya; Koganezawa, Tomoyuki; Tsuruta, Ryohei; Hinderhofer, Alexander; Gerlach, Alexander; Broch, Katharina; Belova, Valentina; Frank, Heiko; Yamamoto, Masayuki; Niederhausen, Jens; Glowatzki, Hendrik; Rabe, Jürgen P; Koch, Norbert; Ishii, Hisao; Schreiber, Frank; Ueno, Nobuo

    2016-06-01

    Designing molecular p-n heterojunction structures, i.e., electron donor-acceptor contacts, is one of the central challenges for further development of organic electronic devices. In the present study, a well-defined p-n heterojunction of two representative molecular semiconductors, pentacene and C60, formed on the single-crystal surface of pentacene is precisely investigated in terms of its growth behavior and crystallographic structure. C60 assembles into a (111)-oriented face-centered-cubic crystal structure with a specific epitaxial orientation on the (001) surface of the pentacene single crystal. The present experimental findings provide molecular scale insights into the formation mechanisms of the organic p-n heterojunction through an accurate structural analysis of the single-crystalline molecular contact.

  15. Epitaxial growth of cubic Gd{sub 2}O{sub 3} thin films on Ge substrates

    Energy Technology Data Exchange (ETDEWEB)

    Molle, A; Wiemer, C; Bhuiyan, M D N K; Tallarida, G; Fanciulli, M [CNR-INFM, Laboratorio Nazionale MDM, via C. Olivetti 2, I-20041 Agrate Brianza (Italy)], E-mail: alessandro.molle@mdm.infm.it

    2008-03-15

    Gd{sub 2}O{sub 3} thin films were grown on Ge (001) substrates by molecular beam epitaxy. The epitaxial character of the film is demonstrated by electron diffraction during the growth. The structural characterization of the films shows that the Gd{sub 2}O{sub 3} forms a bixbyite polymorph with a (110) out-of-plane orientation. The formation of bixbyite structured Gd{sub 2}O{sub 3} is discussed in terms of the atomic arrangement of the oxide planes on the Ge(001) surface.

  16. Epitaxial growth of Cu on Cu(001): Experiments and simulations

    International Nuclear Information System (INIS)

    Furman, Itay; Biham, Ofer; Zuo, Jiang-Kai; Swan, Anna K.; Wendelken, John

    2000-01-01

    A quantitative comparison between experimental and Monte Carlo simulation results for the epitaxial growth of Cu/Cu(001) in the submonolayer regime is presented. The simulations take into account a complete set of hopping processes whose activation energies are derived from semiempirical calculations using the embedded-atom method. The island separation is measured as a function of the incoming flux and the temperature. A good quantitative agreement between the experiment and simulation is found for the island separation, the activation energies for the dominant processes, and the exponents that characterize the growth. The simulation results are then analyzed at lower coverages, which are not accessible experimentally, providing good agreement with theoretical predictions as well

  17. Microstructure of InxGa1−xN nanorods grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Webster, R F; Soundararajah, Q Y; Griffiths, I J; Cherns, D; Novikov, S V; Foxon, C T

    2015-01-01

    Transmission electron microscopy is used to examine the structure and composition of In x Ga 1−x N nanorods grown by plasma-assisted molecular beam epitaxy. The results confirm a core–shell structure with an In-rich core and In-poor shell resulting from axial and lateral growth sectors respectively. Atomic resolution mapping by energy-dispersive x-ray microanalysis and high angle annular dark field imaging show that both the core and the shell are decomposed into Ga-rich and In-rich platelets parallel to their respective growth surfaces. It is argued that platelet formation occurs at the surfaces, through the lateral expansion of surface steps. Studies of nanorods with graded composition show that decomposition ceases for x ≥ 0.8 and the ratio of growth rates, shell:core, decreases with increasing In concentration. (paper)

  18. Si Incorporation in InP Nanowires Grown by Au-Assisted Molecular Beam Epitaxy

    Directory of Open Access Journals (Sweden)

    Lorenzo Rigutti

    2009-01-01

    Full Text Available We report on the growth, structural characterization, and conductivity studies of Si-doped InP nanowires grown by Au-assisted molecular beam epitaxy. It is shown that Si doping reduces the mean diffusion length of adatoms on the lateral nanowire surface and consequently reduces the nanowire growth rate and promotes lateral growth. A resistivity as low as 5.1±0.3×10−5 Ω⋅cm is measured for highly doped nanowires. Two dopant incorporation mechanisms are discussed: incorporation via catalyst particle and direct incorporation on the nanowire sidewalls. The first mechanism is shown to be less efficient than the second one, resulting in inhomogeneous radial dopant distribution.

  19. Tin-Assisted Synthesis of ɛ -Ga2O3 by Molecular Beam Epitaxy

    Science.gov (United States)

    Kracht, M.; Karg, A.; Schörmann, J.; Weinhold, M.; Zink, D.; Michel, F.; Rohnke, M.; Schowalter, M.; Gerken, B.; Rosenauer, A.; Klar, P. J.; Janek, J.; Eickhoff, M.

    2017-11-01

    The synthesis of ɛ -Ga2O3 and β -Ga2O3 by plasma-assisted molecular beam epitaxy on (001 )Al2O3 substrates is studied. The growth window of β -Ga2O3 in the Ga-rich regime, usually limited by the formation of volatile gallium suboxide, is expanded due to the presence of tin during the growth process, which stabilizes the formation of gallium oxides. X-ray diffraction, transmission electron microscopy, time-of-flight secondary-ion mass spectrometry, Raman spectroscopy, and atomic force microscopy are used to analyze the influence of tin on the layer formation. We demonstrate that it allows the synthesis of phase-pure ɛ -Ga2O3 . A growth model based on the oxidation of gallium suboxide by reduction of an intermediate sacrificial tin oxide is suggested.

  20. Growth and characterization of III-N ternary thin films by plasma assisted atomic layer epitaxy at low temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Nepal, Neeraj; Anderson, Virginia R.; Hite, Jennifer K.; Eddy, Charles R.

    2015-08-31

    We report the growth and characterization of III-nitride ternary thin films (Al{sub x}Ga{sub 1−x}N, In{sub x}Al{sub 1−x}N and In{sub x}Ga{sub 1−x}N) at ≤ 500 °C by plasma assisted atomic layer epitaxy (PA-ALE) over a wide stoichiometric range including the range where phase separation has been an issue for films grown by molecular beam epitaxy and metal organic chemical vapor deposition. The composition of these ternaries was intentionally varied through alterations in the cycle ratios of the III-nitride binary layers (AlN, GaN, and InN). By this digital alloy growth method, we are able to grow III-nitride ternaries by PA-ALE over nearly the entire stoichiometry range including in the spinodal decomposition region (x = 15–85%). These early efforts suggest great promise of PA-ALE at low temperatures for addressing miscibility gap challenges encountered with conventional growth methods and realizing high performance optoelectronic and electronic devices involving ternary/binary heterojunctions, which are not currently possible. - Highlights: • III-N ternaries grown at ≤ 500 °C by plasma assisted atomic layer epitaxyGrowth of InGaN and AlInN in the spinodal decomposition region (15–85%) • Epitaxial, smooth and uniform III-N film growth at low temperatures.

  1. Growth and characterization of III-N ternary thin films by plasma assisted atomic layer epitaxy at low temperatures

    International Nuclear Information System (INIS)

    Nepal, Neeraj; Anderson, Virginia R.; Hite, Jennifer K.; Eddy, Charles R.

    2015-01-01

    We report the growth and characterization of III-nitride ternary thin films (Al x Ga 1−x N, In x Al 1−x N and In x Ga 1−x N) at ≤ 500 °C by plasma assisted atomic layer epitaxy (PA-ALE) over a wide stoichiometric range including the range where phase separation has been an issue for films grown by molecular beam epitaxy and metal organic chemical vapor deposition. The composition of these ternaries was intentionally varied through alterations in the cycle ratios of the III-nitride binary layers (AlN, GaN, and InN). By this digital alloy growth method, we are able to grow III-nitride ternaries by PA-ALE over nearly the entire stoichiometry range including in the spinodal decomposition region (x = 15–85%). These early efforts suggest great promise of PA-ALE at low temperatures for addressing miscibility gap challenges encountered with conventional growth methods and realizing high performance optoelectronic and electronic devices involving ternary/binary heterojunctions, which are not currently possible. - Highlights: • III-N ternaries grown at ≤ 500 °C by plasma assisted atomic layer epitaxyGrowth of InGaN and AlInN in the spinodal decomposition region (15–85%) • Epitaxial, smooth and uniform III-N film growth at low temperatures

  2. Epitaxial growth of fcc Ti films on Al(001) surfaces

    International Nuclear Information System (INIS)

    Saleh, A.A.; Shutthanandan, V.; Shivaparan, N.R.; Smith, R.J.; Tran, T.T.; Chambers, S.A.

    1997-01-01

    High-energy ion scattering (HEIS), x-ray photoelectron spectroscopy, and x-ray photoelectron diffraction (XPD) were used to study the growth of thin Ti films on Al(001) surfaces. The Al surface peak area in the backscattered ion spectrum of MeV He + ions, incident along the [00 bar 1] direction, was used to monitor the atomic structure of the Ti films during growth. An initial decrease in the area was observed indicating epitaxial film growth. This decrease continued up to a critical film thickness of about 5.5 ML, after which point the structure of the film changed. Titanium films 3, 5, and 9 ML thick were characterized using XPD in the same chamber. Both the HEIS and XPD results show that the Ti films grow with an fcc structure on Al(001). A tetragonal distortion of 2.4% in the fcc Ti film was measured using ions incident along the [10 bar 1] direction. Although there is a general similarity of fcc Ti growth on both Al(001) and Al(110), the submonolayer growth regime does show differences for the two surfaces. copyright 1997 The American Physical Society

  3. Radical-source molecular beam epitaxy of ZnO-based heterostructures

    Energy Technology Data Exchange (ETDEWEB)

    Sadofiev, Sergey

    2009-10-27

    This work focuses on the development of the novel growth approaches for the fabrication of Group II-oxide materials in the form of epitaxial films and heterostructures. It is shown that molecular-beam epitaxial growth far from thermal equilibrium allows one to overcome the standard solubility limit and to alloy ZnO with MgO or CdO in strict wurtzite phase up to mole fractions of several 10 %. In this way, a band-gap range from 2.2 to 4.4 eV can be covered. A clear layer-by-layer growth mode controlled by oscillations in reflection high-energy electron diffraction makes it possible to fabricate atomically smooth heterointerfaces and well-defined quantum well structures exhibiting prominent band-gap related light emission in the whole composition range. On appropriately designed structures, laser action from the ultraviolet down to green wavelengths and up to room temperature is achieved. The properties and potential of the ''state-of-the-art'' materials are discussed in relation to the advantages for their applications in various optoelectronic devices. (orig.)

  4. Pseudomorphic growth of organic semiconductor thin films driven by incommensurate epitaxy

    International Nuclear Information System (INIS)

    Sassella, A.; Campione, M.; Raimondo, L.; Borghesi, A.; Bussetti, G.; Cirilli, S.; Violante, A.; Goletti, C.; Chiaradia, P.

    2009-01-01

    A stable pseudomorphic phase of α-quaterthiophene, a well known organic semiconductor, is obtained by growing films with organic molecular beam epitaxy (OMBE) on a single crystal of another organic semiconductor, namely, tetracene. The structural characteristics of the new phase are investigated by monitoring in situ the OMBE process by reflectance anisotropy spectroscopy; thus assessing that incommensurate epitaxy is in this case, the driving force for tuning the molecular packing in organic molecular films and in turn, their solid state properties

  5. AlGaAs and AlGaAs/GaAs/AlGaAs nanowires grown by molecular beam epitaxy on silicon substrates

    DEFF Research Database (Denmark)

    Cirlin, G E; Reznik, R R; Shtrom, I V

    2017-01-01

    The data on growth peculiarities and physical properties of GaAs insertions embedded in AlGaAs nanowires grown on different (1 1 1) substrates by Au-assisted molecular beam epitaxy are presented. The influence of nanowires growth conditions on structural and optical properties is studied in detail...

  6. Computer graphic investigation on the epitaxial growth of superconductor films

    International Nuclear Information System (INIS)

    Miyamoto, A.; Iwamoto, S.; Inui, T.; Agusa, K.

    1989-01-01

    A mechanism of the epitaxial growth the oxide superconductor films has been investigated by using the computer graphics for the combination of orthorhombic Ba 2 YCu 3 O 7-x with substrate crystals such as SrTiO 3 MgO, and ZrO 2 . The (001) plane Ba 2 YCu 3 O 7-x with substrate crystals such as SrTiO 3 , MgO, and ZrO 2 . The (001) plane of Ba 2 YCu 3 O 7-x has been shown to fit the (100) plane of SrTiO 3 , MgO, and ZrO 2 . A crystallographic fit has also been proved between the (110) plane of Ba 2 YCu 3 O 7-x and the (110) plane of SrTiO 3 . These results are consistent with the experimental data about the epitaxial growth of the Ba 2 YCu 3 O 7-x films. Furthermore, detailed investigation of atomic arrangements has indicated some differences in the ionic interaction at the superconductor-substrate interface among SrTiO 3 , MgO, and ZrO 2 substrates. As for ZrO 2 (100) plane, for examples, ionic arrangements at the oxide layer is favorable only for the interaction with Y 3+ layer of Ba 2 YCu 3 O 7-x , while the Zr-O layer of ZrO 2 can interact with both Ba-O layer and Cu-O layer of Ba 2 YCu 3 O 7-x

  7. Cu-doped AlN: A possible spinaligner at room-temperature grown by molecular beam epitaxy?

    Science.gov (United States)

    Ganz, P. R.; Schaadt, D. M.

    2011-12-01

    Cu-doped AlN was prepared by plasma assisted molecular beam epitaxy on C-plane sapphire substrates. The growth conditions were investigated for different Cu to Al flux ratios from 1.0% to 4.0%. The formation of Cu-Al alloys on the surface was observed for all doping level. In contrast to Cu-doped GaN, all samples showed diamagnetic behavior determined by SQUID measurements.

  8. Ge-on-Si : Single-Crystal Selective Epitaxial Growth in a CVD Reactor

    NARCIS (Netherlands)

    Sammak, A.; De Boer, W.B.; Nanver, L.K.

    2012-01-01

    A standard Si/SiGe ASM CVD reactor that was recently modified for merging GaAs and Si epitaxial growth in one system is utilized to achieve intrinsic and doped epitaxial Ge-on-Si with low threading dislocation and defect densities. For this purpose, the system is equipped with 2% diluted GeH4 as the

  9. Epitaxial thin film growth of LiH using a liquid-Li atomic template

    Energy Technology Data Exchange (ETDEWEB)

    Oguchi, Hiroyuki, E-mail: oguchi@nanosys.mech.tohoku.ac.jp [Department of Nanomechanics, Tohoku University, Sendai 980-8579 (Japan); Micro System Integration Center (muSIC), Tohoku University, Sendai 980-0845 (Japan); Ikeshoji, Tamio; Orimo, Shin-ichi [Institute for Materials Research, Tohoku University, Sendai 980-8577 (Japan); Advanced Institute for Materials Research (AIMR), Tohoku University, Sendai 980-8577 (Japan); Ohsawa, Takeo; Shiraki, Susumu; Hitosugi, Taro [Advanced Institute for Materials Research (AIMR), Tohoku University, Sendai 980-8577 (Japan); Kuwano, Hiroki [Department of Nanomechanics, Tohoku University, Sendai 980-8579 (Japan)

    2014-11-24

    We report on the synthesis of lithium hydride (LiH) epitaxial thin films through the hydrogenation of a Li melt, forming abrupt LiH/MgO interface. Experimental and first-principles molecular dynamics studies reveal a comprehensive microscopic picture of the crystallization processes, which sheds light on the fundamental atomistic growth processes that have remained unknown in the vapor-liquid-solid method. We found that the periodic structure that formed, because of the liquid-Li atoms at the film/MgO-substrate interface, serves as an atomic template for the epitaxial growth of LiH crystals. In contrast, films grown on the Al{sub 2}O{sub 3} substrates indicated polycrystalline films with a LiAlO{sub 2} secondary phase. These results and the proposed growth process provide insights into the preparation of other alkaline metal hydride thin films on oxides. Further, our investigations open the way to explore fundamental physics and chemistry of metal hydrides including possible phenomena that emerge at the heterointerfaces of metal hydrides.

  10. Epitaxial thin film growth of LiH using a liquid-Li atomic template

    International Nuclear Information System (INIS)

    Oguchi, Hiroyuki; Ikeshoji, Tamio; Orimo, Shin-ichi; Ohsawa, Takeo; Shiraki, Susumu; Hitosugi, Taro; Kuwano, Hiroki

    2014-01-01

    We report on the synthesis of lithium hydride (LiH) epitaxial thin films through the hydrogenation of a Li melt, forming abrupt LiH/MgO interface. Experimental and first-principles molecular dynamics studies reveal a comprehensive microscopic picture of the crystallization processes, which sheds light on the fundamental atomistic growth processes that have remained unknown in the vapor-liquid-solid method. We found that the periodic structure that formed, because of the liquid-Li atoms at the film/MgO-substrate interface, serves as an atomic template for the epitaxial growth of LiH crystals. In contrast, films grown on the Al 2 O 3 substrates indicated polycrystalline films with a LiAlO 2 secondary phase. These results and the proposed growth process provide insights into the preparation of other alkaline metal hydride thin films on oxides. Further, our investigations open the way to explore fundamental physics and chemistry of metal hydrides including possible phenomena that emerge at the heterointerfaces of metal hydrides

  11. Emission control of InGaN nanocolumns grown by molecular-beam epitaxy on Si(111) substrates

    International Nuclear Information System (INIS)

    Albert, S.; Bengoechea-Encabo, A.; Sanchez-Garcia, M. A.; Calleja, E.; Lefebvre, P.; Jahn, U.; Trampert, A.

    2011-01-01

    This work studies the effect of the growth temperature on the morphology and emission characteristics of self-assembled InGaN nanocolumns grown by plasma assisted molecular beam epitaxy. Morphology changes are assessed by scanning electron microscopy, while emission is measured by photoluminescence. Within the growth temperature range of 750 to 650 deg. C, an increase in In incorporation for decreasing temperature is observed. This effect allows tailoring the InGaN nanocolumns emission line shape by using temperature gradients during growth. Depending on the gradient rate, span, and sign, broad emission line shapes are obtained, covering the yellow to green range, even yielding white emission.

  12. The molecular beam epitaxy growth and characterization of zinc cadmium selenide/zinc cadmium magnesium selenide-indium phosphide quantum cascade structures for operation in the 3 - 5 um range

    Science.gov (United States)

    Charles, William O.

    The quantum cascade (QC) laser has captured the interest of researchers for almost three decades. In the early stages, researchers were very interested in proving the QC concept1 proposed by Kazarinov and Suris in 1971. This new concept gave researchers hope that very bulky energy inefficient infra-red (IR) lasers would be replaced with ones that are very compact, tunable and portable. Since the proposal of the QC laser concept and its first demonstration by researchers at Bell Laboratories2 in 1994, this technology has progressed to the point where it is now finding commercial applications in a variety of areas such as military counter measures, free space telecommunications, infra-red imaging and chemical spectroscopy.3-5 The success of this technology can be attributed to the coming of age of the techniques of molecular beam epitaxy (MBE) semiconductor growth and bandgap engineering. 6,7 Using MBE technology, the temperature of the source material can be stabilized by making use of a combination of proportional integral derivative (PID) controllers and thermocouple feedbacks. As a result, the material flux from the effusion cells can achieve stability better than (+/-) 1%. This flux stability together with a well-developed computer controlled shuttering mechanism make it possible to grow multi-quantum well (MQW) structures with excellent layer thickness precision (mono-layer scale) and interface quality. This stringent control of material flux is also a tool that is used by MBE growers to vary the material compositions for the growth of lattice matched and strain compensated QC structures. Today, MBE stands out as one of the premier methods for growing high performing QC lasers. The first successful demonstration of a QC laser2 was done using the InGaAs/InAlAs-InP material system. This demonstration was then repeated a few years later using GaAs/AlGaAs-InP.8 These III-V material systems were extensively studied to establish their material parameters. Given that

  13. The role of Si as surfactant and donor in molecular-beam epitaxy of AlN

    International Nuclear Information System (INIS)

    Lebedev, V.; Morales, F.M.; Romanus, H.; Krischok, S.; Ecke, G.; Cimalla, V.; Himmerlich, M.; Stauden, T.; Cengher, D.; Ambacher, O.

    2005-01-01

    The growth of Si-doped AlN(0001) thin films on Al 2 O 3 (0001) substrates by plasma-induced molecular-beam epitaxy is reported. We have found that Si positively affects the epitaxy being an effective surfactant for AlN growth with a remarkable impact on the crystal quality. It was proven that the characteristic surface reconstruction sequences frequently related to the Al adatoms are obviously Si induced on AlN(0001) surfaces. It was also observed that heavy doping conditions result in volume segregation of Si on the threading dislocation network and in the formation of an amorphous (AlO)(SiO)N cap layer caused by surface oxidation of the accumulated Al and segregated Si. The electron affinity was measured to be smaller than 0.5 eV on the clean AlN surface after removing of the cap layer using Ar + sputtering

  14. Solution-phase epitaxial growth of quasi-monocrystalline cuprous oxide on metal nanowires

    NARCIS (Netherlands)

    Sciacca, Beniamino; Mann, Sander A.; Tichelaar, Frans D.; Zandbergen, Henny W.; Van Huis, Marijn A.; Garnett, Erik C.

    2014-01-01

    The epitaxial growth of monocrystalline semiconductors on metal nanostructures is interesting from both fundamental and applied perspectives. The realization of nanostructures with excellent interfaces and material properties that also have controlled optical resonances can be very challenging. Here

  15. GaN Bulk Growth and Epitaxy from Ca-Ga-N Solutions, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — This SBIR proposal addresses the liquid phase epitaxy (LPE) of gallium nitride (GaN) films using nitrogen-enriched metal solutions. Growth of GaN from solutions...

  16. GaN Bulk Growth and Epitaxy from Ca-Ga-N Solutions, Phase II

    Data.gov (United States)

    National Aeronautics and Space Administration — The innovations proposed here are Ka-band (38 GHz) group III-nitride power FETs and the dislocation density reducing epitaxial growth methods (LPE) needed for their...

  17. Temperature conditions for GaAs nanowire formation by Au-assisted molecular beam epitaxy

    International Nuclear Information System (INIS)

    Tchernycheva, M; Harmand, J C; Patriarche, G; Travers, L; Cirlin, G E

    2006-01-01

    Molecular beam epitaxial growth of GaAs nanowires using Au particles as a catalyst was investigated. Prior to the growth during annealing, Au alloyed with Ga coming from the GaAs substrate, and melted. Phase transitions of the resulting particles were observed in situ by reflection high-energy electron diffraction (RHEED). The temperature domain in which GaAs nanowire growth is possible was determined. The lower limit of this domain (320 deg. C) is close to the observed catalyst solidification temperature. Below this temperature, the catalyst is buried by GaAs growth. Above the higher limit (620 deg. C), the catalyst segregates on the surface with no significant nanowire formation. Inside this domain, the influence of growth temperature on the nanowire morphology and crystalline structure was investigated in detail by scanning electron microscopy and transmission electron microscopy. The correlation of the nanowire morphology with the RHEED patterns observed during the growth was established. Wurtzite GaAs was found to be the dominant crystal structure of the wires

  18. Single orientation graphene synthesized on iridium thin films grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Dangwal Pandey, A., E-mail: arti.pandey@desy.de; Grånäs, E.; Shayduk, R.; Noei, H.; Vonk, V. [Deutsches Elektronen-Synchrotron (DESY), D-22607 Hamburg (Germany); Krausert, K.; Franz, D.; Müller, P.; Keller, T. F.; Stierle, A., E-mail: andreas.stierle@desy.de [Deutsches Elektronen-Synchrotron (DESY), D-22607 Hamburg (Germany); Fachbereich Physik, Universität Hamburg, D-22607 Hamburg (Germany)

    2016-08-21

    Heteroepitaxial iridium thin films were deposited on (0001) sapphire substrates by means of molecular beam epitaxy, and subsequently, one monolayer of graphene was synthesized by chemical vapor deposition. The influence of the growth parameters on the quality of the Ir films, as well as of graphene, was investigated systematically by means of low energy electron diffraction, x-ray reflectivity, x-ray diffraction, Auger electron spectroscopy, scanning electron microscopy, and atomic force microscopy. Our study reveals (111) oriented iridium films with high crystalline quality and extremely low surface roughness, on which the formation of large-area epitaxial graphene is achieved. The presence of defects, like dislocations, twins, and 30° rotated domains in the iridium films is also discussed. The coverage of graphene was found to be influenced by the presence of 30° rotated domains in the Ir films. Low iridium deposition rates suppress these rotated domains and an almost complete coverage of graphene was obtained. This synthesis route yields inexpensive, air-stable, and large-area graphene with a well-defined orientation, making it accessible to a wider community of researchers for numerous experiments or applications, including those which use destructive analysis techniques or irreversible processes. Moreover, this approach can be used to tune the structural quality of graphene, allowing a systematic study of the influence of defects in various processes like intercalation below graphene.

  19. Recent Advances on p-Type III-Nitride Nanowires by Molecular Beam Epitaxy

    Directory of Open Access Journals (Sweden)

    Songrui Zhao

    2017-09-01

    Full Text Available p-Type doping represents a key step towards III-nitride (InN, GaN, AlN optoelectronic devices. In the past, tremendous efforts have been devoted to obtaining high quality p-type III-nitrides, and extraordinary progress has been made in both materials and device aspects. In this article, we intend to discuss a small portion of these processes, focusing on the molecular beam epitaxy (MBE-grown p-type InN and AlN—two bottleneck material systems that limit the development of III-nitride near-infrared and deep ultraviolet (UV optoelectronic devices. We will show that by using MBE-grown nanowire structures, the long-lasting p-type doping challenges of InN and AlN can be largely addressed. New aspects of MBE growth of III-nitride nanostructures are also discussed.

  20. YCo5±x thin films with perpendicular anisotropy grown by molecular beam epitaxy

    Science.gov (United States)

    Sharma, S.; Hildebrandt, E.; Sharath, S. U.; Radulov, I.; Alff, L.

    2017-06-01

    The synthesis conditions of buffer-free (00l) oriented YCo5 and Y2Co17 thin films onto Al2O3 (0001) substrates have been explored by molecular beam epitaxy (MBE). The manipulation of the ratio of individual atomic beams of Yttrium, Y and Cobalt, Co, as well as growth rate variations allows establishing a thin film phase diagram. Highly textured YCo5±x thin films were stabilized with saturation magnetization of 517 emu/cm3 (0.517 MA/m), coercivity of 4 kOe (0.4 T), and anisotropy constant, K1, equal to 5.34 ×106 erg/cm3 (0.53 MJ/m3). These magnetic parameters and the perpendicular anisotropy obtained without additional underlayers make the material system interesting for application in magnetic recording devices.

  1. Thin film phase diagram of iron nitrides grown by molecular beam epitaxy

    Science.gov (United States)

    Gölden, D.; Hildebrandt, E.; Alff, L.

    2017-01-01

    A low-temperature thin film phase diagram of the iron nitride system is established for the case of thin films grown by molecular beam epitaxy and nitrided by a nitrogen radical source. A fine-tuning of the nitridation conditions allows for growth of α ‧ -Fe8Nx with increasing c / a -ratio and magnetic anisotropy with increasing x until almost phase pure α ‧ -Fe8N1 thin films are obtained. A further increase of nitrogen content below the phase decomposition temperature of α ‧ -Fe8N (180 °C) leads to a mixture of several phases that is also affected by the choice of substrate material and symmetry. At higher temperatures (350 °C), phase pure γ ‧ -Fe4N is the most stable phase.

  2. Unusual strain in homoepitaxial CdTe(001) layers grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Heinke, H.; Waag, A.; Moeller, M.O.; Regnet, M.M.; Landwehr, G. [Physikalisches Institut, Univ. Wuerzburg (Germany)

    1994-01-01

    For homoepitaxial CdTe(001) films grown by molecular beam epitaxy onto CdTe(001) substrates, a difference between the lattice constants of the substrate and the layer was systematically observed using high resolution X-ray diffraction. Reciprocal space maps point out an unusual strain state of such layers which is indicated by the position of their reciprocal lattice points. They lie in a section of reciprocal space which is usually forbidden by elasticity theory. The strain is laterally anisotropic leading to a monoclinic symmetry of the thin films. The lateral strain is depth dependent. Possible reasons for the formation of the unusual strain are discussed, and a correlation of the unusual strain with the growth conditions is attempted

  3. Molecular beam epitaxy grown Ge/Si pin layer sequence for photonic devices

    International Nuclear Information System (INIS)

    Schulze, J.; Oehme, M.; Werner, J.

    2012-01-01

    A key challenge to obtain a convergence of classical Si-based microelectronics and optoelectronics is the manufacturing of photonic integrated circuits integrable into classical Si-based integrated circuits. This integration would be greatly enhanced if similar facilities and technologies could be used. Therefore one approach is the development of optoelectronic components and devices made from group-IV-based materials such as SiGe, Ge or Ge:Sn. In this paper the optoelectronic performances of a pin diode made from a Ge/Si heterostructure pin layer sequence grown by molecular beam epitaxy are discussed. After a detailed description of the layer sequence growth and the device manufacturing process it will be shown that – depending on the chosen operating point and device design – the diode serves as a broadband high speed photo detector, Franz–Keldysh effect modulator or light emitting diode.

  4. Molecular beam epitaxy grown Ge/Si pin layer sequence for photonic devices

    Energy Technology Data Exchange (ETDEWEB)

    Schulze, J., E-mail: schulze@iht.uni-stuttgart.de; Oehme, M.; Werner, J.

    2012-02-01

    A key challenge to obtain a convergence of classical Si-based microelectronics and optoelectronics is the manufacturing of photonic integrated circuits integrable into classical Si-based integrated circuits. This integration would be greatly enhanced if similar facilities and technologies could be used. Therefore one approach is the development of optoelectronic components and devices made from group-IV-based materials such as SiGe, Ge or Ge:Sn. In this paper the optoelectronic performances of a pin diode made from a Ge/Si heterostructure pin layer sequence grown by molecular beam epitaxy are discussed. After a detailed description of the layer sequence growth and the device manufacturing process it will be shown that - depending on the chosen operating point and device design - the diode serves as a broadband high speed photo detector, Franz-Keldysh effect modulator or light emitting diode.

  5. Photoluminescence characteristics of Pb-doped, molecular-beam-epitaxy grown ZnSe crystal layers

    International Nuclear Information System (INIS)

    Mita, Yoh; Kuronuma, Ryoichi; Inoue, Masanori; Sasaki, Shoichiro; Miyamoto, Yoshinobu

    2004-01-01

    The characteristic green photoluminescence emission and related phenomena in Pb-doped, molecular-beam-epitaxy (MBE)-grown ZnSe crystal layers were investigated to explore the nature of the center responsible for the green emission. The intensity of the green emission showed a distinct nonlinear dependence on excitation intensity. Pb-diffused polycrystalline ZnSe was similarly examined for comparison. The characteristic green emission has been observed only in MBE-grown ZnSe crystal layers with moderate Pb doping. The results of the investigations on the growth conditions, luminescence, and related properties of the ZnSe crystal layers suggest that the green emission is due to isolated Pb replacing Zn and surrounded with regular ZnSe lattice with a high perfection

  6. Growth of c-plane ZnO on γ-LiAlO2 (1 0 0) substrate with a GaN buffer layer by plasma assisted molecular beam epitaxy

    International Nuclear Information System (INIS)

    Yan, T.; Lu, C.-Y.J.; Schuber, R.; Chang, L.; Schaadt, D.M.; Chou, M.M.C.; Ploog, K.H.; Chiang, C.-M.

    2015-01-01

    Highlights: • ZnO epilayers were grown on LiAlO 2 (1 0 0) substrate with a GaN buffer layer by MBE. • A high Zn/O flux ratio is beneficial for reducing the density of screw dislocations. • Reciprocal space maps demonstrate that the misfit strain in ZnO has been relaxed. • No interfacial layer is formed at ZnO/GaN interface using a Zn pre-exposure strategy. - Abstract: C-plane ZnO epilayers were grown on LiAlO 2 (1 0 0) substrate with a GaN buffer layer by plasma assisted molecular beam epitaxy. Both the X-ray rocking curves and the transmission electron microscopy analyses indicate that the ZnO epilayers exhibit a lower threading dislocation density (∼1 × 10 10 cm −2 ) as compared to those grown on LiAlO 2 substrate without the buffer layer. A high Zn/O flux ratio is beneficial for reducing the density of screw-type dislocations. Reciprocal space maps demonstrate that the misfit strain has been relaxed. No interfacial layer is formed at the ZnO/GaN interface by using a Zn pre-exposure strategy. The ZnO epilayers exhibit a strong near band edge emission at 3.28 eV at room temperature with a negligible green band emission

  7. Inhomogeneous Si-doping of gold-seeded InAs nanowires grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Rolland, Chloe; Coinon, Christophe; Wallart, Xavier; Leturcq, Renaud [Institute of Electronics Microelectronics and Nanotechnology, UMR CNRS 8520, ISEN Department, Avenue Poincare, CS60069, 59652 Villeneuve d' Ascq Cedex (France); Caroff, Philippe [Institute of Electronics Microelectronics and Nanotechnology, UMR CNRS 8520, ISEN Department, Avenue Poincare, CS60069, 59652 Villeneuve d' Ascq Cedex (France); Department of Electronic Materials Engineering, Research School of Physics and Engineering, The Australian National University, Canberra, ACT 0200 (Australia)

    2013-06-03

    We have investigated in situ Si doping of InAs nanowires grown by molecular beam epitaxy from gold seeds. The effectiveness of n-type doping is confirmed by electrical measurements showing an increase of the electron density with the Si flux. We also observe an increase of the electron density along the nanowires from the tip to the base, attributed to the dopant incorporation on the nanowire facets whereas no detectable incorporation occurs through the seed. Furthermore, the Si incorporation strongly influences the lateral growth of the nanowires without giving rise to significant tapering, revealing the complex interplay between axial and lateral growth.

  8. Molecular beam epitaxy for high-performance Ga-face GaN electron devices

    International Nuclear Information System (INIS)

    Kaun, Stephen W; Speck, James S; Wong, Man Hoi; Mishra, Umesh K

    2013-01-01

    Molecular beam epitaxy (MBE) has emerged as a powerful technique for growing GaN-based high electron mobility transistor (HEMT) epistructures. Over the past decade, HEMT performance steadily improved, mainly through the optimization of device fabrication processes. Soon, HEMT performance will be limited by the crystalline quality of the epistructure. MBE offers heterostructure growth with highly abrupt interfaces, low point defect concentrations, and very low carbon and hydrogen impurity concentrations. Minimizing parasitic leakage pathways and resistances is essential in the growth of HEMTs for high-frequency and high-power applications. Through growth on native substrates with very low threading dislocation density, low-leakage HEMTs with very low on-resistance can be realized. Ga-rich plasma-assisted MBE (PAMBE) has been studied extensively, and it is clear that this technique has inherent limitations, including a high density of leakage pathways and a very small growth parameter space. Relatively new MBE growth techniques—high-temperature N-rich PAMBE and ammonia-based MBE—are being developed to circumvent the shortcomings of Ga-rich PAMBE. (invited review)

  9. Facility for low-temperature spin-polarized-scanning tunneling microscopy studies of magnetic/spintronic materials prepared in situ by nitride molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Lin, Wenzhi; Foley, Andrew; Alam, Khan; Wang, Kangkang; Liu, Yinghao; Chen, Tianjiao; Pak, Jeongihm; Smith, Arthur R., E-mail: smitha2@ohio.edu [Department of Physics and Astronomy, Nanoscale and Quantum Phenomena Institute, Ohio University, Athens, Ohio 45701 (United States)

    2014-04-15

    Based on the interest in, as well as exciting outlook for, nitride semiconductor based structures with regard to electronic, optoelectronic, and spintronic applications, it is compelling to investigate these systems using the powerful technique of spin-polarized scanning tunneling microscopy (STM), a technique capable of achieving magnetic resolution down to the atomic scale. However, the delicate surfaces of these materials are easily corrupted by in-air transfers, making it unfeasible to study them in stand-alone ultra-high vacuum STM facilities. Therefore, we have carried out the development of a hybrid system including a nitrogen plasma assisted molecular beam epitaxy/pulsed laser epitaxy facility for sample growth combined with a low-temperature, spin-polarized scanning tunneling microscope system. The custom-designed molecular beam epitaxy growth system supports up to eight sources, including up to seven effusion cells plus a radio frequency nitrogen plasma source, for epitaxially growing a variety of materials, such as nitride semiconductors, magnetic materials, and their hetero-structures, and also incorporating in situ reflection high energy electron diffraction. The growth system also enables integration of pulsed laser epitaxy. The STM unit has a modular design, consisting of an upper body and a lower body. The upper body contains the coarse approach mechanism and the scanner unit, while the lower body accepts molecular beam epitaxy grown samples using compression springs and sample skis. The design of the system employs two stages of vibration isolation as well as a layer of acoustic noise isolation in order to reduce noise during STM measurements. This isolation allows the system to effectively acquire STM data in a typical lab space, which during its construction had no special and highly costly elements included, (such as isolated slabs) which would lower the environmental noise. The design further enables tip exchange and tip coating without

  10. Facility for low-temperature spin-polarized-scanning tunneling microscopy studies of magnetic/spintronic materials prepared in situ by nitride molecular beam epitaxy.

    Science.gov (United States)

    Lin, Wenzhi; Foley, Andrew; Alam, Khan; Wang, Kangkang; Liu, Yinghao; Chen, Tianjiao; Pak, Jeongihm; Smith, Arthur R

    2014-04-01

    Based on the interest in, as well as exciting outlook for, nitride semiconductor based structures with regard to electronic, optoelectronic, and spintronic applications, it is compelling to investigate these systems using the powerful technique of spin-polarized scanning tunneling microscopy (STM), a technique capable of achieving magnetic resolution down to the atomic scale. However, the delicate surfaces of these materials are easily corrupted by in-air transfers, making it unfeasible to study them in stand-alone ultra-high vacuum STM facilities. Therefore, we have carried out the development of a hybrid system including a nitrogen plasma assisted molecular beam epitaxy/pulsed laser epitaxy facility for sample growth combined with a low-temperature, spin-polarized scanning tunneling microscope system. The custom-designed molecular beam epitaxy growth system supports up to eight sources, including up to seven effusion cells plus a radio frequency nitrogen plasma source, for epitaxially growing a variety of materials, such as nitride semiconductors, magnetic materials, and their hetero-structures, and also incorporating in situ reflection high energy electron diffraction. The growth system also enables integration of pulsed laser epitaxy. The STM unit has a modular design, consisting of an upper body and a lower body. The upper body contains the coarse approach mechanism and the scanner unit, while the lower body accepts molecular beam epitaxy grown samples using compression springs and sample skis. The design of the system employs two stages of vibration isolation as well as a layer of acoustic noise isolation in order to reduce noise during STM measurements. This isolation allows the system to effectively acquire STM data in a typical lab space, which during its construction had no special and highly costly elements included, (such as isolated slabs) which would lower the environmental noise. The design further enables tip exchange and tip coating without

  11. Facility for low-temperature spin-polarized-scanning tunneling microscopy studies of magnetic/spintronic materials prepared in situ by nitride molecular beam epitaxy

    International Nuclear Information System (INIS)

    Lin, Wenzhi; Foley, Andrew; Alam, Khan; Wang, Kangkang; Liu, Yinghao; Chen, Tianjiao; Pak, Jeongihm; Smith, Arthur R.

    2014-01-01

    Based on the interest in, as well as exciting outlook for, nitride semiconductor based structures with regard to electronic, optoelectronic, and spintronic applications, it is compelling to investigate these systems using the powerful technique of spin-polarized scanning tunneling microscopy (STM), a technique capable of achieving magnetic resolution down to the atomic scale. However, the delicate surfaces of these materials are easily corrupted by in-air transfers, making it unfeasible to study them in stand-alone ultra-high vacuum STM facilities. Therefore, we have carried out the development of a hybrid system including a nitrogen plasma assisted molecular beam epitaxy/pulsed laser epitaxy facility for sample growth combined with a low-temperature, spin-polarized scanning tunneling microscope system. The custom-designed molecular beam epitaxy growth system supports up to eight sources, including up to seven effusion cells plus a radio frequency nitrogen plasma source, for epitaxially growing a variety of materials, such as nitride semiconductors, magnetic materials, and their hetero-structures, and also incorporating in situ reflection high energy electron diffraction. The growth system also enables integration of pulsed laser epitaxy. The STM unit has a modular design, consisting of an upper body and a lower body. The upper body contains the coarse approach mechanism and the scanner unit, while the lower body accepts molecular beam epitaxy grown samples using compression springs and sample skis. The design of the system employs two stages of vibration isolation as well as a layer of acoustic noise isolation in order to reduce noise during STM measurements. This isolation allows the system to effectively acquire STM data in a typical lab space, which during its construction had no special and highly costly elements included, (such as isolated slabs) which would lower the environmental noise. The design further enables tip exchange and tip coating without

  12. Structure and optical band gaps of (Ba,Sr)SnO{sub 3} films grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Schumann, Timo; Raghavan, Santosh; Ahadi, Kaveh; Kim, Honggyu; Stemmer, Susanne, E-mail: stemmer@mrl.ucsb.edu [Materials Department, University of California, Santa Barbara, California 93106-5050 (United States)

    2016-09-15

    Epitaxial growth of (Ba{sub x}Sr{sub 1−x})SnO{sub 3} films with 0 ≤ x ≤ 1 using molecular beam epitaxy is reported. It is shown that SrSnO{sub 3} films can be grown coherently strained on closely lattice and symmetry matched PrScO{sub 3} substrates. The evolution of the optical band gap as a function of composition is determined by spectroscopic ellipsometry. The direct band gap monotonously decreases with x from to 4.46 eV (x = 0) to 3.36 eV (x = 1). A large Burnstein-Moss shift is observed with La-doping of BaSnO{sub 3} films. The shift corresponds approximately to the increase in Fermi level and is consistent with the low conduction band mass.

  13. Molecular beam epitaxial growth of Bi{sub 2}Te{sub 3} and Sb{sub 2}Te{sub 3} topological insulators on GaAs (111) substrates: a potential route to fabricate topological insulator p-n junction

    Energy Technology Data Exchange (ETDEWEB)

    Zeng, Zhaoquan; Morgan, Timothy A.; Li, Chen; Hirono, Yusuke; Hu, Xian; Hawkridge, Michael E.; Benamara, Mourad; Salamo, Gregory J. [Arkansas Institute for Nanoscale Material Sciences and Engineering, University of Arkansas, Fayetteville, AR 72701 (United States); Fan, Dongsheng; Yu, Shuiqing [Arkansas Institute for Nanoscale Material Sciences and Engineering, University of Arkansas, Fayetteville, AR 72701 (United States); Department of Electrical Engineering, University of Arkansas, Fayetteville, AR 72701 (United States); Zhao, Yanfei [International Center for Quantum Materials, School of Physics, Peking University, Beijing, 100871 (China); Lee, Joon Sue [The Center for Nanoscale Science and Department of Physics, The Pennsylvania State University, University Park, PA 16802 (United States); Wang, Jian [International Center for Quantum Materials, School of Physics, Peking University, Beijing, 100871 (China); The Center for Nanoscale Science and Department of Physics, The Pennsylvania State University, University Park, PA 16802 (United States); Wang, Zhiming M. [Arkansas Institute for Nanoscale Material Sciences and Engineering, University of Arkansas, Fayetteville, AR 72701 (United States); State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054 (China); Engineering Research Center for Semiconductor Integrated Technology, Institute of Semiconductors, Chinese Academy of Science, Beijing 100083 (China)

    2013-07-15

    High quality Bi{sub 2}Te{sub 3} and Sb{sub 2}Te{sub 3} topological insulators films were epitaxially grown on GaAs (111) substrate using solid source molecular beam epitaxy. Their growth and behavior on both vicinal and non-vicinal GaAs (111) substrates were investigated by reflection high-energy electron diffraction, atomic force microscopy, X-ray diffraction, and high resolution transmission electron microscopy. It is found that non-vicinal GaAs (111) substrate is better than a vicinal substrate to provide high quality Bi{sub 2}Te{sub 3} and Sb{sub 2}Te{sub 3} films. Hall and magnetoresistance measurements indicate that p type Sb{sub 2}Te{sub 3} and n type Bi{sub 2}Te{sub 3} topological insulator films can be directly grown on a GaAs (111) substrate, which may pave a way to fabricate topological insulator p-n junction on the same substrate, compatible with the fabrication process of present semiconductor optoelectronic devices.

  14. Vertical epitaxial wire-on-wire growth of Ge/Si on Si(100) substrate.

    Science.gov (United States)

    Shimizu, Tomohiro; Zhang, Zhang; Shingubara, Shoso; Senz, Stephan; Gösele, Ulrich

    2009-04-01

    Vertically aligned epitaxial Ge/Si heterostructure nanowire arrays on Si(100) substrates were prepared by a two-step chemical vapor deposition method in anodic aluminum oxide templates. n-Butylgermane vapor was employed as new safer precursor for Ge nanowire growth instead of germane. First a Si nanowire was grown by the vapor liquid solid growth mechanism using Au as catalyst and silane. The second step was the growth of Ge nanowires on top of the Si nanowires. The method presented will allow preparing epitaxially grown vertical heterostructure nanowires consisting of multiple materials on an arbitrary substrate avoiding undesired lateral growth.

  15. Use of halide transport in epitaxial growth of InP and related compounds

    Energy Technology Data Exchange (ETDEWEB)

    Somogyi, K. [Hungarian Academy of Sciences, Budapest (Hungary). Research Inst. for Technical Physics

    1996-12-31

    In this paper methods and results in the InP (and related) growth practice are reviewed, classified and summarized on the basis of the recent literature. The aim is to show the present place and role of the halogen transport in the epitaxial growth. In the case of InP the importance of the classical hydride method is still high. Though MOVPE technique dominates in the case of growth of the compounds with In content, atomic layer epitaxy and selective area growth are successful with auxiliary application of the halogen transport. Chlorine assisted MOVPE has an increasing role.

  16. Epitaxial growth of tungsten layers on MgO(001)

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Pengyuan; Ozsdolay, Brian D.; Gall, Daniel, E-mail: galld@rpi.edu [Department of Materials Science and Engineering, Rensselaer Polytechnic Institute, Troy, New York 12180 (United States)

    2015-11-15

    Smooth single crystal W(001) layers were grown on MgO(001) substrates by magnetron sputtering at 900 °C. X-ray diffraction ω–2θ scans, ω-rocking curves, pole figures, and reciprocal space maps indicate a 45°-rotated epitaxial relationship: (001){sub W}‖(001){sub MgO} and [010]{sub W}‖[110]{sub MgO}, and a relaxed lattice constant of 3.167 ± 0.001 nm. A residual in-plane biaxial compressive strain is primarily attributed to differential thermal contraction after growth and decreases from −0.012 ± 0.001 to −0.001 ± 0.001 with increasing layer thickness d = 4.8–390 nm, suggesting relaxation during cooling by misfit dislocation growth through threading dislocation glide. The in-plane x-ray coherence length increases from 3.4 to 33.6 nm for d = 4.8–390 nm, while the out-of-plane x-ray coherence length is identical to the layer thickness for d ≤ 20 nm, but is smaller than d for d ≥ 49.7 nm, indicating local strain variations along the film growth direction. X-ray reflectivity analyses indicate that the root-mean-square surface roughness increases from 0.50 ± 0.05 to 0.95 ± 0.05 nm for d = 4.8–19.9 nm, suggesting a roughness exponent of 0.38, but remains relatively constant for d > 20 nm with a roughness of 1.00 ± 0.05 nm at d = 47.9 nm.

  17. Epitaxial growth of pentacene on alkali halide surfaces studied by Kelvin probe force microscopy.

    Science.gov (United States)

    Neff, Julia L; Milde, Peter; León, Carmen Pérez; Kundrat, Matthew D; Eng, Lukas M; Jacob, Christoph R; Hoffmann-Vogel, Regina

    2014-04-22

    In the field of molecular electronics, thin films of molecules adsorbed on insulating surfaces are used as the functional building blocks of electronic devices. Control of the structural and electronic properties of the thin films is required for reliably operating devices. Here, noncontact atomic force and Kelvin probe force microscopies have been used to investigate the growth and electrostatic landscape of pentacene on KBr(001) and KCl(001) surfaces. We have found that, together with molecular islands of upright standing pentacene, a new phase of tilted molecules appears near step edges on KBr. Local contact potential differences (LCPD) have been studied with both Kelvin experiments and density functional theory calculations. Our images reveal that differently oriented molecules display different LCPD and that their value is independent of the number of molecular layers. These results point to the formation of an interface dipole, which may be explained by a partial charge transfer from the pentacene to the surface. Moreover, the monitoring of the evolution of the pentacene islands shows that they are strongly affected by dewetting: Multilayers build up at the expense of monolayers, and in the Kelvin images, previously unknown line defects appear, which reveal the epitaxial growth of pentacene crystals.

  18. Control growth of silicon nanocolumns' epitaxy on silicon nanowires

    Energy Technology Data Exchange (ETDEWEB)

    Chong, Su Kong, E-mail: sukong1985@yahoo.com.my [University of Malaya, Low Dimensional Materials Research Centre, Department of Physics (Malaysia); Dee, Chang Fu [Universiti Kebangsaan Malaysia (UKM), Institute of Microengineering and Nanoelectronics (IMEN) (Malaysia); Yahya, Noorhana [Universiti Teknologi PETRONAS, Faculty of Science and Information Technology (Malaysia); Rahman, Saadah Abdul [University of Malaya, Low Dimensional Materials Research Centre, Department of Physics (Malaysia)

    2013-04-15

    The epitaxial growth of Si nanocolumns on Si nanowires was studied using hot-wire chemical vapor deposition. A single-crystalline and surface oxide-free Si nanowire core (core radius {approx}21 {+-} 5 nm) induced by indium crystal seed was used as a substance for the vapor phase epitaxial growth. The growth process is initiated by sidewall facets, which then nucleate upon certain thickness to form Si islands and further grow to form nanocolumns. The Si nanocolumns with diameter of 10-20 nm and aspect ratio up to 10 can be epitaxially grown on the surface of nanowires. The results showed that the radial growth rate of the Si nanocolumns remains constant with the increase of deposition time. Meanwhile, the radial growth rates are controllable by manipulating the hydrogen to silane gas flow rate ratio. The optical antireflection properties of the Si nanocolumns' decorated SiNW arrays are discussed in the text.

  19. Constructing oxide interfaces and heterostructures by atomic layer-by-layer laser molecular beam epitaxy

    OpenAIRE

    Lei, Qingyu; Golalikhani, Maryam; Davidson, Bruce A.; Liu, Guozhen; Schlom, D. G.; Qiao, Qiao; Zhu, Yimei; Chandrasena, Ravini U.; Yang, Weibing; Gray, Alexander X.; Arenholz, Elke; Farrar, Andrew K.; Tenne, Dmitri A.; Hu, Minhui; Guo, Jiandong

    2016-01-01

    Advancements in nanoscale engineering of oxide interfaces and heterostructures have led to discoveries of emergent phenomena and new artificial materials. Combining the strengths of reactive molecular-beam epitaxy and pulsed-laser deposition, we show here, with examples of Sr1+xTi1-xO3+delta, Ruddlesden-Popper phase Lan+1NinO3n+1 (n = 4), and LaAl1+yO3(1+0.5y)/SrTiO3 interfaces, that atomic layer-by-layer laser molecular-beam epitaxy (ALL-Laser MBE) significantly advances the state of the art...

  20. Molecular beam epitaxy of GeTe-Sb{sub 2}Te{sub 3} phase change materials studied by X-ray diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Shayduk, Roman

    2010-05-20

    The integration of phase change materials into semiconductor heterostructures may lead to the development of a new generation of high density non-volatile phase change memories. Epitaxial phase change materials allow to study the detailed structural changes during the phase transition and to determine the scaling limits of the memory. This work is dedicated to the epitaxial growth of Ge-Sb-Te phase change alloys on GaSb(001). We deposit Ge-Sb-Te (GST) films on GaSb(001) substrates by means of molecular beam epitaxy (MBE). The film orientation and lattice constant evolution is determined in real time during growth using grazing incidence X-ray diffraction (GID). The nucleation stage of the growth is studied in situ using reflection high energy electron diffraction (RHEED). Four growth regimes of GST on GaSb(001) were observed: amorphous, polycrystalline, incubated epitaxial and direct epitaxial. Amorphous film grows for substrate temperatures below 100 C. For substrate temperatures in the range 100-160 C, the film grows in polycrystalline form. Incubated epitaxial growth is observed at temperatures from 180 to 210 C. This growth regime is characterized by an initial 0.6nm thick amorphous layer formation, which crystallizes epitaxially as the film thickness increases. The determined lattice constant of the films is 6.01 A, very close to that of the metastable GST phase. The films predominantly possess an epitaxial cube-on-cube relationship. At higher temperatures the films grow epitaxially, however the growth rate is rapidly decreasing with temperature. At temperatures above 270 C the growth rate is zero. The composition of the grown films is close to 2:2:5 for Ge, Sb and Te, respectively. The determined crystal structure of the films is face centered cubic (FCC) with a rhombohedral distortion. The analysis of X-ray peak widths gives a value for the rhombohedral angle of 89.56 . We observe two types of reflections in reciprocal space indicating two FCC sublattices in

  1. Efficient n-type doping of CdTe epitaxial layers grown by photo-assisted molecular beam epitaxy with the use of chlorine

    Energy Technology Data Exchange (ETDEWEB)

    Hommel, D.; Scholl, S.; Kuhn, T.A.; Ossau, W.; Waag, A.; Landwehr, G. (Univ. Wuerzburg, Physikalisches Inst. (Germany)); Bilger, G. (Univ. Stuttgart, Inst. fuer Physikalische Elektronik (Germany))

    1993-01-30

    Chlorine has been used successfully for the first time for n-type doping of CdTe epitaxial layers (epilayers) grown by photo-assisted molecular beam epitaxy. Similar to n-type doping of ZnSe layers, ZnCl[sub 2] has been used as source material. The free-carrier concentration can be varied over more than three orders of magnitude by changing the ZnCl[sub 2] oven temperature. Peak mobilities are 4700 cm[sup 2] V[sup -1] s[sup -1] for an electron concentration of 2x10[sup 16] cm[sup -3] and 525 cm[sup 2] V[sup -1] s[sup -1] for 2x10[sup 18] cm[sup -3]. The electrical transport data obtained by Van der Pauw configuration and Hall structure measurements are consistent with each other, indicating a good uniformity of the epilayers. In photoluminescence the donor-bound-exciton emission dominates for all chlorine concentrations. This contasts significantly with results obtained for indium doping, commonly used for obtaining n-type CdTe epilayers. The superiority of chlorine over indium doping and the influence of growth parameters on the behaviour of CdTe:Cl layers will be discussed on the basis of transport, luminescence, secondary ion mass spectroscopy and X-ray photoelectron spectroscopy data. (orig.).

  2. Structural characterization of ZnO films grown by molecular beam epitaxy on sapphire with MgO buffer

    International Nuclear Information System (INIS)

    Pecz, B.; El-Shaer, A.; Bakin, A.; Mofor, A.-C.; Waag, A.; Stoemenos, J.

    2006-01-01

    The structural characteristics of the ZnO film grown on sapphire substrate using a thin MgO buffer layer were studied using transmission electron microscopy and high-resolution x-ray diffraction. The growth was carried out in a modified plasma-molecular beam epitaxy system. The observed misfit dislocations were well confined at the sapphire overgrown interface exhibiting domain matching epitaxy, where the integral multiples of lattice constants match across the interface. The main extended defects in the ZnO film were the threading dislocations having a mean density of 4x10 9 cm -2 . The formation of the MgO buffer layer as well as the ZnO growth were monitored in situ by reflection high-energy electron diffraction. The very thin ∼1 nm, MgO buffer layer can partially interdiffuse with the ZnO as well as react with the Al 2 O 3 substrate forming an intermediate epitaxial layer having the spinel (MgO/Al 2 O 3 ) structure

  3. Fast growth rate of epitaxial β-Ga2O3 by close coupled showerhead MOCVD

    Science.gov (United States)

    Alema, Fikadu; Hertog, Brian; Osinsky, Andrei; Mukhopadhyay, Partha; Toporkov, Mykyta; Schoenfeld, Winston V.

    2017-10-01

    We report on the growth of epitaxial β-Ga2O3 thin films on c-plane sapphire substrates using a close coupled showerhead MOCVD reactor. Ga(DPM)3 (DPM = dipivaloylmethanate), triethylgallium (TEGa) and trimethylgallium (TMGa) metal organic (MO) precursors were used as Ga sources and molecular oxygen was used for oxidation. Films grown from each of the Ga sources had high growth rates, with up to 10 μm/hr achieved using a TMGa precursor at a substrate temperature of 900 °C. As confirmed by X-ray diffraction, the films grown from each of the Ga sources were the monoclinic (2 bar 0 1) oriented β-Ga2O3 phase. The optical bandgap of the films was also estimated to be ∼4.9 eV. The fast growth rate of β-Ga2O3 thin films obtained using various Ga-precursors has been achieved due to the close couple showerhead design of the MOCVD reactor as well as the separate injection of oxygen and MO precursors, preventing the premature oxidation of the MO sources. These results suggest a pathway to overcoming the long-standing challenge of realizing fast growth rates for Ga2O3 using the MOCVD method.

  4. Control over the morphology of AlN during molecular beam epitaxy with the plasma activation of nitrogen on Si (111) substrates

    International Nuclear Information System (INIS)

    Mizerov, A. M.; Kladko, P. N.; Nikitina, E. V.; Egorov, A. Yu.

    2015-01-01

    The results of studies of the growth kinetics of AlN layers during molecular beam epitaxy with the plasma activation of nitrogen using Si (111) substrates are presented. The possibility of the growth of individual AlN/Si (111) nanocolumns using growth conditions with enrichment of the surface with metal near the formation mode of Al drops, at a substrate temperature close to maximal, during molecular beam epitaxy with the plasma activation of nitrogen (T s ≈ 850°C) is shown. The possibility of growing smooth AlN layers on a nanocolumnar AlN/Si (111) buffer with the use of T s ≈ 750°C and growth conditions providing enrichment with metal is shown

  5. Control over the morphology of AlN during molecular beam epitaxy with the plasma activation of nitrogen on Si (111) substrates

    Energy Technology Data Exchange (ETDEWEB)

    Mizerov, A. M., E-mail: mizerov@beam.ioffe.ru; Kladko, P. N.; Nikitina, E. V.; Egorov, A. Yu. [Russian Academy of Sciences, St. Petersburg Academic University-Nanotechnology Research and Education Centre (Russian Federation)

    2015-02-15

    The results of studies of the growth kinetics of AlN layers during molecular beam epitaxy with the plasma activation of nitrogen using Si (111) substrates are presented. The possibility of the growth of individual AlN/Si (111) nanocolumns using growth conditions with enrichment of the surface with metal near the formation mode of Al drops, at a substrate temperature close to maximal, during molecular beam epitaxy with the plasma activation of nitrogen (T{sub s} ≈ 850°C) is shown. The possibility of growing smooth AlN layers on a nanocolumnar AlN/Si (111) buffer with the use of T{sub s} ≈ 750°C and growth conditions providing enrichment with metal is shown.

  6. Growth and properties of epitaxial iron oxide layers

    NARCIS (Netherlands)

    Voogt, F.C; Fujii, T; Hibma, T; Zhang, G.L.; Smulders, P.J M

    1996-01-01

    Epitaxial layers of iron oxides have been grown on a MgO(001) substrate by evaporating natural Fe or Fe-57 from Knudsen cells in the presence of a NO2 flow directed to the substrate. The resulting layers have been investigated in situ with LEED, RHEED, AES and XPS and ex situ with GEMS and ion beam

  7. Physical properties and band structure of reactive molecular beam epitaxy grown oxygen engineered HfO{sub 2{+-}x}

    Energy Technology Data Exchange (ETDEWEB)

    Hildebrandt, Erwin; Kurian, Jose; Alff, Lambert [Institute of Materials Science, Technische Universitaet Darmstadt, 64287 Darmstadt (Germany)

    2012-12-01

    We have conducted a detailed thin film growth structure of oxygen engineered monoclinic HfO{sub 2{+-}x} grown by reactive molecular beam epitaxy. The oxidation conditions induce a switching between (111) and (002) texture of hafnium oxide. The band gap of oxygen deficient hafnia decreases with increasing amount of oxygen vacancies by more than 1 eV. For high oxygen vacancy concentrations, defect bands form inside the band gap that induce optical transitions and p-type conductivity. The resistivity changes by several orders of magnitude as a function of oxidation conditions. Oxygen vacancies do not give rise to ferromagnetic behavior.

  8. InAs nanocrystals on SiO2/Si by molecular beam epitaxy for memory applications

    International Nuclear Information System (INIS)

    Hocevar, Moiera; Regreny, Philippe; Descamps, Armel; Albertini, David; Saint-Girons, Guillaume; Souifi, Abdelkader; Gendry, Michel; Patriarche, Gilles

    2007-01-01

    We studied a memory structure based on InAs nanocrystals grown by molecular beam epitaxy directly on thermal SiO 2 on silicon. Both nanocrystal diameter and density can be controlled by growth parameters. Transmission electron microscopy analysis shows high crystallinity and low size dispersion. In an electrical test structure with a 3.5 nm tunnel oxide, we observed that 80% of the initial injected electrons remain stored in the InAs nanocrystals after 3 months and that the retention time for electrons in InAs nanocrystals is four orders of magnitude higher than in silicon nanocrystals

  9. Large-area selective CVD epitaxial growth of Ge on Si substrates

    NARCIS (Netherlands)

    Sammak, A.; De Boer, W.; Nanver, L.K.

    2011-01-01

    Selective epitaxial growth of crystalline Ge on Si in a standard ASM Epsilon 2000 CVD reactor is investigated for the fabrication of Ge p+n diodes. At the deposition temperature of 700?C, most of the lattice mismatch-defects are trapped within first 300nm of Ge growth and good quality single crystal

  10. Bromine doping of CdTe and CdMnTe epitaxial layers grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Waag, A. (Physikalisches Inst. der Univ. Wuerzburg (Germany)); Scholl, S. (Physikalisches Inst. der Univ. Wuerzburg (Germany)); Schierstedt, K. von (Physikalisches Inst. der Univ. Wuerzburg (Germany)); Hommel, D. (Physikalisches Inst. der Univ. Wuerzburg (Germany)); Landwehr, G. (Physikalisches Inst. der Univ. Wuerzburg (Germany)); Bilger, G. (Zentrum fuer Sonnenenergie und Wasserstoff-Forschung, Stuttgart (Germany))

    1993-03-01

    We report on the n-type doping of CdTe and CdMnTe with bormine as a novel dopant material. /the thin films were grown by molecular beam epitaxy. ZnBr[sub 2] was used as a source material for the n-type doping. Free carrier concentrations at room temperature of up to 2.8x10[sup 18] cm[sup -3] could be readily obtained for both CdTe as well as CdMnTe thin films with Mn concentrations below 10%. This is to our knowledge the highest value ever obtained for the dilute magnetic semiconductor CdMnTe. For ZnBr[sub 2] source temperatures up to 60 C - corresponding to a free carrier concentration of (2-3)x10[sup 18] cm[sup -3] - the free carrier concentration of the epitaxial film increases with ZnBr[sub 2] source temperature. For higher ZnBr[sub 2] source temperatures compensation becomes dominant, which is indicated by a steep decrease of the free carrier concentration with increasing ZnBr[sub 2] source temperature. In addition the carrier mobility decreases drastically for such high dopant fluxes. A model of bromine incorporation is proposed. (orig.)

  11. Origin of Spontaneous Core-Shell AIGaAs Nanowires Grown by Molecular Beam Epitaxy

    DEFF Research Database (Denmark)

    Dubrovskii, V. G.; Shtrom, I. V.; Reznik, R. R.

    2016-01-01

    Based on the high-angle annular dark-field scanning transmission electron microscopy and energy dispersive X-ray spectroscopy studies, we unravel the origin of spontaneous core shell AlGaAs nanowires grown by gold-assisted molecular beam epitaxy. Our AlGaAs nanowires have a cylindrical core...

  12. Molecular beam epitaxy of CdSe epilayers and quantum wells on ZnTe substrate

    International Nuclear Information System (INIS)

    Park, Y.M.; Andre, R.; Kasprzak, J.; Dang, Le Si; Bellet-Amalric, E.

    2007-01-01

    We have grown zinc-blende cadmium selenide (CdSe) epilayers on ZnTe-(0 0 1) substrate by molecular beam epitaxy (MBE). By controlling the substrate temperature and beam-equivalent pressure (BEP) ratio, of Se to Cd, we determined the most suitable growth condition based on reflection high-energy electron diffraction (RHEED) pattern. At a substrate temperature of 280 deg. C and a BEP ratio of 3.6, the RHEED pattern showed a V-like feature, indicating a rough surface with facets. As the substrate temperature was increased to 360 deg. C at the same BEP ratio, a V-like RHEED pattern moved to a clear streaky pattern. Moreover when the BEP ratio was increased to 4.8 at 360 deg. C of substrate temperature, a clear (2 x 1) reconstruction of the CdSe layer was observed. A CdSe/CdMgSe single quantum well structure was also grown on ZnTe-(0 0 1) substrate by MBE. The RHEED pattern showed a clear (2 x 1) surface reconstruction during the growth. By photoluminescence measurement, a good optical property of the structure was obtained

  13. Plasma-assisted molecular beam epitaxy of (11-22)-oriented 3-nitrides

    International Nuclear Information System (INIS)

    Lahourcade, L.

    2009-10-01

    This work reports on the molecular-beam epitaxial growth of (1122)-oriented semi-polar nitride semiconductors using m-sapphire substrates. The (1122) crystallographic orientation is predefined by AlN deposition on m-sapphire under N excess. On top of this AlN buffer layer, undoped or Si-doped two-dimensional GaN(1122) films are formed under Ga-rich conditions, with a stabilized Ga-excess ad-layer of about 1.05±0.10 ML. In contrast, Mg tends to segregate on the GaN surface, inhibiting the self-regulated Ga excess film. Nevertheless, uniform Mg incorporation can be obtained, and p-type conductivity was achieved. GaN/AlN quantum wells are synthesized by deposition of the binary compounds under the above-described conditions. In the case of GaN/AlN quantum dots, the three-dimensional transition is induced by a growth interruption under vacuum. The reduction of the internal electric field in GaN/AlN nano-structures is confirmed by the blue shift of the photoluminescence spectrum and by the short photoluminescence decay times measured at low temperature. These results are consistent with theoretical calculations of the electronic structure. (author)

  14. Powder free PECVD epitaxial silicon by plasma pulsing or increasing the growth temperature

    Science.gov (United States)

    Chen, Wanghua; Maurice, Jean-Luc; Vanel, Jean-Charles; Cabarrocas, Pere Roca i.

    2018-06-01

    Crystalline silicon thin films are promising candidates for low cost and flexible photovoltaics. Among various synthesis techniques, epitaxial growth via low temperature plasma-enhanced chemical vapor deposition is an interesting choice because of two low temperature related benefits: low thermal budget and better doping profile control. However, increasing the growth rate is a tricky issue because the agglomeration of clusters required for epitaxy leads to powder formation in the plasma. In this work, we have measured precisely the time evolution of the self-bias voltage in silane/hydrogen plasmas at millisecond time scale, for different values of the direct-current bias voltage applied to the radio frequency (RF) electrode and growth temperatures. We demonstrate that the decisive factor to increase the epitaxial growth rate, i.e. the inhibition of the agglomeration of plasma-born clusters, can be obtained by decreasing the RF OFF time or increasing the growth temperature. The influence of these two parameters on the growth rate and epitaxial film quality is also presented.

  15. Epitaxial growth of topological insulator Bi{sub 2}Se{sub 3} film on Si(111) with atomically sharp interface

    Energy Technology Data Exchange (ETDEWEB)

    Bansal, Namrata [Department of Electrical and Computer Engineering, Rutgers, State University of New Jersey, Piscataway, NJ 08854 (United States); Kim, Yong Seung [Graphene Research Institute, Sejong University, Seoul 143-747 (Korea, Republic of); Edrey, Eliav; Brahlek, Matthew; Horibe, Yoichi [Department of Physics and Astronomy, Rutgers, State University of New Jersey, Piscataway, NJ 08854 (United States); Iida, Keiko; Tanimura, Makoto [Research Department, Nissan Arc, Ltd. Yokosuka, Kanagawa 237-0061 (Japan); Li Guohong; Feng Tian; Lee, Hang-Dong; Gustafsson, Torgny; Andrei, Eva [Department of Physics and Astronomy, Rutgers, State University of New Jersey, Piscataway, NJ 08854 (United States); Oh, Seongshik, E-mail: ohsean@physics.rutgers.edu [Department of Physics and Astronomy, Rutgers, the State University of New Jersey, Piscataway, NJ 08854 (United States)

    2011-10-31

    Atomically sharp epitaxial growth of Bi{sub 2}Se{sub 3} films is achieved on Si(111) substrate with molecular beam epitaxy. Two-step growth process is found to be a key to achieve interfacial-layer-free epitaxial Bi{sub 2}Se{sub 3} films on Si substrates. With a single-step high temperature growth, second phase clusters are formed at an early stage. On the other hand, with low temperature growth, the film tends to be disordered even in the absence of a second phase. With a low temperature initial growth followed by a high temperature growth, second-phase-free atomically sharp interface is obtained between Bi{sub 2}Se{sub 3} and Si substrate, as verified by reflection high energy electron diffraction (RHEED), transmission electron microscopy (TEM) and X-ray diffraction. The lattice constant of Bi{sub 2}Se{sub 3} is observed to relax to its bulk value during the first quintuple layer according to RHEED analysis, implying the absence of strain from the substrate. TEM shows a fully epitaxial structure of Bi{sub 2}Se{sub 3} film down to the first quintuple layer without any second phase or an amorphous layer.

  16. Plasma-assisted Molecular Beam Epitaxy of N-polar InAlN-barrier High-electron-mobility Transistors.

    Science.gov (United States)

    Hardy, Matthew T; Storm, David F; Katzer, D Scott; Downey, Brian P; Nepal, Neeraj; Meyer, David J

    2016-11-24

    Plasma-assisted molecular beam epitaxy is well suited for the epitaxial growth of III-nitride thin films and heterostructures with smooth, abrupt interfaces required for high-quality high-electron-mobility transistors (HEMTs). A procedure is presented for the growth of N-polar InAlN HEMTs, including wafer preparation and growth of buffer layers, the InAlN barrier layer, AlN and GaN interlayers and the GaN channel. Critical issues at each step of the process are identified, such as avoiding Ga accumulation in the GaN buffer, the role of temperature on InAlN compositional homogeneity, and the use of Ga flux during the AlN interlayer and the interrupt prior to GaN channel growth. Compositionally homogeneous N-polar InAlN thin films are demonstrated with surface root-mean-squared roughness as low as 0.19 nm and InAlN-based HEMT structures are reported having mobility as high as 1,750 cm 2 /V∙sec for devices with a sheet charge density of 1.7 x 10 13 cm -2 .

  17. Superconducting thin films of As-free pnictide LaPd{sub 1-x}Sb{sub 2} grown by reactive molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Retzlaff, Reiner; Buckow, Alexander; Kurian, Jose; Alff, Lambert [Institute of Materials Science, Technische Universitaet Darmstadt, Petersenstr. 23, 64287 Darmstadt (Germany)

    2013-07-01

    We use reactive molecular beam epitaxy as synthesis technique for the search of arsenic free pnictide superconductors. Epitaxial thin films of LaPd{sub 1-x}Sb{sub 2} were grown on (100) MgO substrates from elemental sources by simultaneous evaporation of high purity La, Pd and Sb metals by e-gun. LaPd{sub 1-x}Sb{sub 2} belongs to a novel class of pnictide superconductors with a peculiar pnictide square net layer. Previously, we have reported epitaxial growth of isostructural Bi based compounds. The substitution of Bi by Sb leads to thin films with metallic behavior and room temperature resistivity of about 85 μΩ cm. The highest observed transition temperature T{sub c} inLaPd{sub 1-x}Sb{sub 2} is 3.1 K and does not depend on x. We discuss strategies to increase T{sub c} in this pnictide subfamily.

  18. Zirconia thin films from aqueous precursors: Processing, microstructural development, and epitaxial growth

    International Nuclear Information System (INIS)

    Miller, K.T.

    1991-01-01

    Thin films of ZrO 2 (Y 2 O 3 ) were prepared from aqueous salt precursors by spin coating. Films were pyrolyzed to produce porous polycrystalline thin films of 5-10 nm grain size. Subsequent microstructural development depends greatly upon the nature of the substrate. Upon randomly oriented sapphire, the films initially sintered to full density; further heat treatment and grain growth causes these films to break into interconnected islands and finally isolated particles. Thermodynamic calculations predict that breakup is energetically favorable when the grain-size film-thickness ratio exceeds a critical value. Upon basal-plane-oriented sapphire, grain growth and breakup prefer the (100) oriented grains, presumably because this orientation is a special interface of low energy. The isolated, oriented grains produced by film breakup act as seeds for the growth of newly deposited material. Upon (100) cubic zirconia, true epitaxial films develop. Epitaxial growth was observed for lattice mismatches up to 1.59%. Growth proceeds from a fine epitaxial layer which is produced during the initial stages of heat treatment, consuming the porous polycrystalline material and producing a dense epitaxial thin film whose misfit is accommodated by a combination of film strain and misfit dislocations

  19. Real time spectroscopic ellipsometry investigation of homoepitaxial GaN grown by plasma assisted molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Tong-Ho; Choi, Soojeong; Wu, Pae; Brown, April [Department of Electrical and Computer Engineering, Duke University, 128 Hudson Hall, Durham, NC (United States); Losurdo, Maria; Giangregorio, Maria M.; Bruno, Giovanni [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy); Moto, Akihiro [Innovation Core SEI, Inc., 3235 Kifer Road, Santa Clara, CA 95051 (United States)

    2006-06-15

    The growth of GaN by plasma assisted molecular beam epitaxy on GaN template substrates (GaN on sapphire) is investigated with in-situ multi-channel spectroscopic ellipsometry. Growth is performed under various Ga/N flux ratios at growth temperatures in the range 710-780 C. The thermal roughening of the GaN template caused by decomposition of the surface is investigated through the temporal variation of the GaN pseudodielectric function over the temperature range of 650 C to 850 C. The structural, morphological, and optical properties are also discussed. (copyright 2006 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  20. Morphology of self-catalyzed GaN nanowires and chronology of their formation by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Galopin, E; Largeau, L; Patriarche, G; Travers, L; Glas, F; Harmand, J C

    2011-01-01

    GaN nanowires are synthesized by plasma-assisted molecular beam epitaxy on Si(111) substrates. The strong impact of the cell orientation relative to the substrate on the nanowire morphology is shown. To study the kinetics of growth, thin AlN markers are introduced periodically during NW growth. These markers are observed in single nanowires by transmission electron microscopy, giving access to the chronology of the nanowire formation and to the time evolution of the nanowire morphology. A long delay precedes the beginning of nanowire formation. Then, their elongation proceeds at a constant rate. Later, shells develop on the side-wall facets by ascending growth of layer bunches which first agglomerate at the nanowire foot.

  1. P-type doping of semipolar GaN(11 anti 22) by plasma-assisted molecular-beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Das, A.; Lahourcade, L. [Equipe Mixte CEA-CNRS, Nanophysique et Semiconducteurs, CEA-Grenoble, INAC/SP2M, Grenoble (France); Pernot, J. [Institut Neel, CNRS et Universite Joseph Fourier, Grenoble (France); Valdueza-Felip, S. [Equipe Mixte CEA-CNRS, Nanophysique et Semiconducteurs, CEA-Grenoble, INAC/SP2M, Grenoble (France); Dept. Electronica, Escuela Politecnica, Universidad de Alcala, Alcala de Henares, Madrid (Spain); Ruterana, P. [CIMAP, UMR6252, CNRS-ENSICAEN-CEA-UCBN, Caen (France); Laufer, A.; Eickhoff, M. [I. Physikalisches Institut, Justus-Liebig-Universitaet Giessen (Germany); Monroy, E.

    2010-07-15

    We report the effect of Mg doping on the growth kinetics of semipolar GaN(11-22) synthesized by plasma-assisted molecular-beam epitaxy. Mg tends to segregate on the surface, inhibiting the formation of the self-regulated Ga film which is used as a surfactant for the growth of undoped and Si-doped GaN(11-22). As a result, the growth widow is reduced for Mg doped layers, and we observe a certain deterioration of the surface morphology. In spite of this difficulties, homogenous Mg incorporation is achieved and layers display p -type conductivity for Mg atomic concentration higher than 7 x 10{sup 18} cm{sup -3}. Microscopy studies show no evidence of the pyramidal defects or polarity inversion domains found in Mg-doped GaN(0001). (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  2. Photo-irradiation effects on GaAs atomic layer epitaxial growth. GaAs no genshiso epitaxial seicho ni okeru hikari reiki koka

    Energy Technology Data Exchange (ETDEWEB)

    Mashita, M.; Kawakyu, Y.; Sasaki, M.; Ishikawa, H. (Toshiba Corp., Kawasaki (Japan). Research and Development Center)

    1990-08-10

    Single atomic layer epitaxy (ALE) aims at controlling a growing film at a precision of single molecular layer. In this article, it is reported that the growth temperature range of ALE was expanded by the vertical irradiation of KrF exima laser (248 nm) onto the substrate for the ALE growth of GaAs using the metalorganic chemical vapor deposition (MOCVD) method. Thanks for the results of the above experiment, it was demonstrated that the irradiation effect was not thermal, but photochemical. In addition, this article studies the possibility of adsorption layer irradiation and surface irradiation as the photo-irradiation mechanism, and points out that coexistence of both irradiation mechanisms can be considered and, in case of exima laser, strong possibility of direct irradiation of the adsorption layer because of its high power density. Hereinafter, by using both optical growth ALE and thermal growth ALE jointly, the degree of freedom of combination of hetero ALE increases and its application to various material systems becomes possible. 16 refs., 6 figs.

  3. Layer-by-Layer Epitaxial Growth of Defect-Engineered Strontium Cobaltites

    Energy Technology Data Exchange (ETDEWEB)

    Andersen, Tassie K. [Materials Science; Department of Materials Science and Engineering, Northwestern University, Evanston, Illinois 60208, United States; Cook, Seyoung [Materials Science; Department of Materials Science and Engineering, Northwestern University, Evanston, Illinois 60208, United States; Wan, Gang [Materials Science; Hong, Hawoong [Advanced Photon Source, Argonne National Laboratory, Argonne, Illinois 60439, United States; Marks, Laurence D. [Department of Materials Science and Engineering, Northwestern University, Evanston, Illinois 60208, United States; Fong, Dillon D. [Materials Science

    2018-01-31

    Control over structure and composition of (ABO(3)) perovskite oxides offers exciting opportunities since these materials possess unique, tunable properties. Perovskite oxides with cobalt B-site cations are particularly promising, as the range of the cations stable oxidation states leads to many possible structural frameworks. Here, we report growth of strontium cobalt oxide thin films by molecular beam epitaxy, and conditions necessary to stabilize different defect concentration phases. In situ X-ray scattering is used to monitor structural evolution during growth, while in situ X-ray absorption near-edge spectroscopy is used to probe oxidation state and measure changes to oxygen vacancy concentration as a function of film thickness. Experimental results are compared to kinetically limited thermodynamic predictions, in particular, solute trapping, with semiquantitative agreement. Agreement between observations of dependence of cobaltite phase on oxidation activity and deposition rate, and predictions indicates that a combined experimental/theoretical approach is key to understanding phase behavior in the strontium cobalt oxide system.

  4. Epitaxial Growth of Germanium on Silicon for Light Emitters

    Directory of Open Access Journals (Sweden)

    Chengzhao Chen

    2012-01-01

    Full Text Available This paper describes the role of Ge as an enabler for light emitters on a Si platform. In spite of the large lattice mismatch of ~4.2% between Ge and Si, high-quality Ge layers can be epitaxially grown on Si by ultrahigh-vacuum chemical vapor deposition. Applications of the Ge layers to near-infrared light emitters with various structures are reviewed, including the tensile-strained Ge epilayer, the Ge epilayer with a delta-doping SiGe layer, and the Ge/SiGe multiple quantum wells on Si. The fundamentals of photoluminescence physics in the different Ge structures are discussed briefly.

  5. Merging Standard CVD Techniques for GaAs and Si Epitaxial Growth

    NARCIS (Netherlands)

    Sammak, A.; De Boer, W.; Van den Bogaard, A.; Nanver, L.K.

    2010-01-01

    A commercial Chemical Vapor Deposition (CVD) system, the ASMI Epsilon 2000 designed for Si and SiGe epitaxy, has, for the first time, been equipped for the growth of GaAs compounds in a manner that does not exclude the use of the system also for Si-based depositions. With the new system, intrinsic,

  6. Epitaxial Growth of a Methoxy-Functionalized Quaterphenylene on Alkali Halide Surfaces

    DEFF Research Database (Denmark)

    Balzer, Frank; Sun, Rong; Parisi, Jürgen

    2015-01-01

    The epitaxial growth of the methoxy functionalized para-quaterphenylene (MOP4) on the (001) faces of the alkali halides NaCl and KCl and on glass is investigated by a combination of lowenergy electron diffraction (LEED), polarized light microscopy (PLM), atomic force microscopy (AFM), and X...

  7. The structural evolution of InN nanorods to microstructures on Si (111) by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Anyebe, E A; Zhuang, Q; Kesaria, M; Krier, A

    2014-01-01

    We report the catalyst free growth of wurtzite InN nanorods (NRs) and microislands on bare Si (111) by plasma-assisted molecular beam epitaxy at various temperatures. The morphological evolution from NRs to three dimensional (3D) islands as a function of growth temperature is investigated. A combination of tapered, non-tapered, and pyramidal InN NRs are observed at 490 °C, whereas the InN evolves to faceted microislands with an increase in growth temperature to 540 °C and further developed to indented and smooth hemispherical structures at extremely high temperatures (630 °C). The evolution from NRs to microislands with increase in growth temperature is attributed to the lowering of the surface free energy of the growing crystals with disproportionate growth velocities along different growth fronts. The preferential adsorption of In atoms on the (0001) c-plane and (10-10) m-plane promotes the growth of NRs at relatively low growth temperature and 3D microislands at higher temperatures. The growth rate imbalance along different planes facilitates the development of facets on 3D microislands. A strong correlation between the morphological and structural properties of the 3D films is established. XRD studies reveal that the NRs and the faceted microislands are crystalline, whereas the hemispherical microislands grown at extremely high growth temperature contain In adlayers. Finally, photoluminescent emissions were observed at ∼0.75 eV from the InN NRs. (paper)

  8. Multiferroic fluoride BaCoF4 Thin Films Grown Via Molecular Beam Epitaxy

    Science.gov (United States)

    Borisov, Pavel; Johnson, Trent; García-Castro, Camilo; Kc, Amit; Schrecongost, Dustin; Cen, Cheng; Romero, Aldo; Lederman, David

    Multiferroic materials exhibit exciting physics related to the simultaneous presence of multiple long-range orders, in many cases consisting of antiferromagnetic (AF) and ferroelectric (FE) orderings. In order to provide a new, promising route for fluoride-based multiferroic material engineering, we grew multiferroic fluoride BaCoF4 in thin film form on Al2O3 (0001) substrates by molecular beam epitaxy. The films grow with the orthorhombic b-axis out-of-plane and with three in-plane structural twin domains along the polar c-axis directions. The FE ordering in thin films was verified by FE remanent hysteresis loops measurements at T = 14 K and by room temperature piezoresponse force microscopy (PFM). An AF behavior was found below Neel temperature TN ~ 80 K, which is in agreement with the bulk properties. At lower temperatures two additional magnetic phase transitions at 19 K and 41 K were found. First-principles calculations demonstrated that the growth strain applied to the bulk BaCoF4 indeed favors two canted spin orders, along the b- and a-axes, respectively, in addition to the main AF spin order along the c-axis. Supported by FAME (Contract 2013-MA-2382), WV Research Challenge Grant (HEPC.dsr.12.29), and DMREF-NSF 1434897.

  9. Molecular beam epitaxy of iodine-doped CdTe and (CdMg)Te

    Energy Technology Data Exchange (ETDEWEB)

    Fischer, F.; Waag, A.; Litz, Th.; Scholl, S.; Schmitt, M.; Landwehr, G. (Physikalisches Inst. der Univ. Wuerzburg (Germany)); Bilger, G. (Zentrum fuer Sonnenenergie und Wasserstofforschung, Stuttgart (Germany))

    1994-08-01

    The n-type doping of CdTe and (CdMg)Te by the use of the solid dopant source material ZnI[sub 2] is reported. Doping levels as high as 7x10[sup 18] cm[sup -3] have been obtained in CdTe with carrier mobilities around 500 cm[sup 2]/V[center dot]s at room temperature. For a dopant incorporation higher than 1x10[sup 19] cm[sup -3] the free carrier concentration decreases, indicating the onset of a compensation mechanism, which is observed in the case of chlorine and bromine doping, too. Preliminary experiments show that with increasing Mg concentration the free carrier concentration decreases. Nevertheless, CdMgTe with a magnesium concentration x=0.37 (band gap 2.2 eV at room temperature) can be doped up to 2x10[sup 17] cm[sup -3]. The existence of deep donor levels in this CdTe based ternary is not supposed to be the only reason for the reduction of the free carrier concentration. For high Mg support during molecular beam epitaxial (MBE) growth of wide gap (CdMg)Te layers, the ZnI[sub 2] incorporation is reduced, leading to low doping levels, too

  10. Hollow-anode plasma source for molecular beam epitaxy of gallium nitride

    International Nuclear Information System (INIS)

    Anders, A.; Newman, N.; Rubin, M.; Dickinson, M.; Jones, E.; Phatak, P.; Gassmann, A.

    1996-01-01

    GaN films have been grown by molecular beam epitaxy (MBE) using a hollow-anode nitrogen plasma source. The source was developed to minimize defect formation as a result of contamination and ion damage. The hollow-anode discharge is a special form of glow discharge with very small anode area. A positive anode voltage drop of 30 endash 40 V and an increased anode sheath thickness leads to ignition of a relatively dense plasma in front of the anode hole. Driven by the pressure gradient, the open-quote open-quote anode close-quote close-quote plasma forms a bright plasma jet streaming with supersonic velocity towards the substrate. Films of GaN have been grown on (0001) SiC and (0001) Al 2 O 3 at 600 endash 800 degree C. The films were investigated by photoluminescence, cathodoluminescence, x-ray diffraction, Rutherford backscattering, and particle-induced x-ray emission. The film with the highest structural quality had a rocking curve width of 5 arcmin, the lowest reported value for MBE growth to date. copyright 1996 American Institute of Physics

  11. New synthesis method for the growth of epitaxial graphene

    Energy Technology Data Exchange (ETDEWEB)

    Yu, X.Z. [Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA 94720 (United States); Laboratory of Condensed Matter Spectroscopy and Opto-Electronic Physics, Department of Physics, Shanghai Jiao Tong University, 1954 Hua Shan Road, Shanghai 200030 (China); Hwang, C.G.; Jozwiak, C.M.; Koehl, A. [Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA 94720 (United States); Schmid, A.K. [National Center for Electron Microscopy, Lawrence Berkeley National Laboratory, Berkeley, CA 94709 (United States); Lanzara, A., E-mail: ALanzara@lbl.gov [Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, CA 94720 (United States); Department of Physics, University of California, Berkeley, CA 94720 (United States)

    2011-04-15

    Highlights: {yields} We report a new straightforward method for the synthesis of micrometer scale graphene sheets. {yields} The process is based on a face to face mehtod in which two SiC substrates are placed one on top of the other and are heated simultaneously, leading to highly homogeneous samples. {yields} The number of graphene layers is determined by the annealing temperature. - Abstract: As a viable candidate for an all-carbon post-CMOS electronics revolution, epitaxial graphene has attracted significant attention. To realize its application potential, reliable methods for fabricating large-area single-crystalline graphene domains are required. A new way to synthesize high quality epitaxial graphene, namely 'face-to-face' method, has been reported in this paper. The structure and morphologies of the samples are characterized by low-energy electron diffraction, atomic force microscopy, angle-resolved photoemission spectroscopy and Raman spectroscopy. The grown samples show better quality and larger length scales than samples grown through conventional thermal desorption. Moreover, the graphene thickness can be easily controlled by changing annealing temperature.

  12. Structural disorder of natural BimSen superlattices grown by molecular beam epitaxy

    Science.gov (United States)

    Springholz, G.; Wimmer, S.; Groiss, H.; Albu, M.; Hofer, F.; Caha, O.; Kriegner, D.; Stangl, J.; Bauer, G.; Holý, V.

    2018-05-01

    The structure and morphology of BimSen epitaxial layers with compositions ranging from Bi2Se3 to the Bi1Se1 grown by molecular beam epitaxy with different flux compositions are investigated by transmission electron microscopy, high-resolution x-ray diffraction, and atomic force microscopy. It is shown that the lattice structure changes significantly as a function of the beam flux composition, i.e., Se/BiSe flux ratio that determines the stoichiometry of the layers. A perfect Bi2Se3 phase is formed only with a sufficiently high additional Se flux, whereas Bi1Se1 is obtained when only a BiSe compound source without additional Se is used. For intermediate values of the excess Se flux during growth, Bi2Se3 -δ layers are obtained with the Se deficit δ varying between 0 and 1. This Se deficit is accommodated by incorporation of additional Bi-Bi double layers into the Bi2Se3 structure that otherwise exclusively consists of Se-Bi-Se-Bi-Se quintuple layers. While a periodic insertion of such Bi double layers would result in the formation of natural BimSen superlattices, we find that this Bi double-layer insertion is rather stochastic with a high degree of disorder depending on the film composition. Therefore, the structure of such epilayers is better described by a one-dimensional paracrystal model, consisting of disordered sequences of quintuple and double layers rather than by strictly periodic natural superlattices. From detailed analysis of the x-ray diffraction data, we determine the dependence of the lattice parameters a and c and distances of the individual (0001) planes dj as a function of composition, evidencing that only the in-plane lattice parameter a shows a linear dependence on composition. The simulation of the diffraction curves with the random stacking paracrystal model yields an excellent agreement with the experimental data and it brings quantitative information on the randomness of the stacking sequence, which is compared to growth modeling using Monte

  13. Comparative study of LaNiO$_3$/LaAlO$_3$ heterostructures grown by pulsed laser deposition and oxide molecular beam epitaxy

    OpenAIRE

    Wrobel, F.; Mark, A. F.; Christiani, G.; Sigle, W.; Habermeier, H. -U.; van Aken, P. A.; Logvenov, G.; Keimer, B.; Benckiser, E.

    2017-01-01

    Variations in growth conditions associated with different deposition techniques can greatly affect the phase stability and defect structure of complex oxide heterostructures. We synthesized superlattices of the paramagnetic metal LaNiO3 and the large band gap insulator LaAlO3 by atomic layer-by-layer molecular beam epitaxy (MBE) and pulsed laser deposition (PLD) and compared their crystallinity, microstructure as revealed by high-resolution transmission electron microscopy images and resistiv...

  14. Non-adiabatic ab initio molecular dynamics of supersonic beam epitaxy of silicon carbide at room temperature

    Energy Technology Data Exchange (ETDEWEB)

    Taioli, Simone [Interdisciplinary Laboratory for Computational Science, FBK-Center for Materials and Microsystems and University of Trento, Trento (Italy); Department of Physics, University of Trento, Trento (Italy); Istituto Nazionale di Fisica Nucleare, Sezione di Perugia (Italy); Department of Chemistry, University of Bologna, Bologna (Italy); Garberoglio, Giovanni [Interdisciplinary Laboratory for Computational Science, FBK-Center for Materials and Microsystems and University of Trento, Trento (Italy); Simonucci, Stefano [Interdisciplinary Laboratory for Computational Science, FBK-Center for Materials and Microsystems and University of Trento, Trento (Italy); Istituto Nazionale di Fisica Nucleare, Sezione di Perugia (Italy); Department of Physics, University of Camerino, Camerino (Italy); Beccara, Silvio a [Interdisciplinary Laboratory for Computational Science, FBK-Center for Materials and Microsystems and University of Trento, Trento (Italy); Department of Physics, University of Trento, Trento (Italy); Aversa, Lucrezia [Institute of Materials for Electronics and Magnetism, IMEM-CNR, Trento (Italy); Nardi, Marco [Institute of Materials for Electronics and Magnetism, IMEM-CNR, Trento (Italy); Institut fuer Physik, Humboldt-Universitaet zu Berlin, Berlin (Germany); Verucchi, Roberto [Institute of Materials for Electronics and Magnetism, FBK-CNR, Trento (Italy); Iannotta, Salvatore [Institute of Materials for Electronics and Magnetism, IMEM-CNR, Parma (Italy); Dapor, Maurizio [Interdisciplinary Laboratory for Computational Science, FBK-Center for Materials and Microsystems and University of Trento, Trento (Italy); Department of Materials Engineering and Industrial Technologies, University of Trento, Trento (Italy); Istituto Nazionale di Fisica Nucleare, Sezione di Padova (Italy); and others

    2013-01-28

    In this work, we investigate the processes leading to the room-temperature growth of silicon carbide thin films by supersonic molecular beam epitaxy technique. We present experimental data showing that the collision of fullerene on a silicon surface induces strong chemical-physical perturbations and, for sufficient velocity, disruption of molecular bonds, and cage breaking with formation of nanostructures with different stoichiometric character. We show that in these out-of-equilibrium conditions, it is necessary to go beyond the standard implementations of density functional theory, as ab initio methods based on the Born-Oppenheimer approximation fail to capture the excited-state dynamics. In particular, we analyse the Si-C{sub 60} collision within the non-adiabatic nuclear dynamics framework, where stochastic hops occur between adiabatic surfaces calculated with time-dependent density functional theory. This theoretical description of the C{sub 60} impact on the Si surface is in good agreement with our experimental findings.

  15. Epitaxial growth of Ge-Sb-Te based phase change materials

    Energy Technology Data Exchange (ETDEWEB)

    Perumal, Karthick

    2013-07-30

    Ge-Sb-Te based phase change materials are considered as a prime candidate for optical and electrical data storage applications. With the application of an optical or electrical pulse, they can be reversibly switched between amorphous and crystalline state, thereby exhibiting large optical and electrical contrast between the two phases, which are then stored as information in the form of binary digits. Single crystalline growth is interesting from both the academic and industrial perspective, as ordered Ge-Sb-Te based metamaterials are known to exhibit switching at reduced energies. The present study deals with the epitaxial growth and analysis of Ge-Sb-Te based thin films. The first part of the thesis deals with the epitaxial growth of GeTe. Thin films of GeTe were grown on highly mismatched Si(111) and (001) substrates. On both the substrate orientations the film grows along [111] direction with an amorphous-to-crystalline transition observed during the initial stages of growth. The amorphous-to-crystalline transition was studied in-vivo using azimuthal reflection high-energy electron diffraction scans and grazing incidence X-ray diffraction. In the second part of the thesis epitaxy and characterization of Sb{sub 2}Te{sub 3} thin films are presented. The third part of the thesis deals with the epitaxy of ternary Ge-Sb-Te alloys. The composition of the films are shown to be highly dependent on growth temperatures and vary along the pseudobinary line from Sb{sub 2}Te{sub 3} to GeTe with increase in growth temperatures. A line-of-sight quadrupole mass spectrometer was used to reliably control the GeSbTe growth temperature. Growth was performed at different Ge, Sb, Te fluxes to study the compositional variation of the films. Incommensurate peaks are observed along the [111] direction by X-ray diffraction. The possibility of superstructural vacancy ordering along the [111] direction is discussed.

  16. Epitaxial growth of Ge-Sb-Te based phase change materials

    International Nuclear Information System (INIS)

    Perumal, Karthick

    2013-01-01

    Ge-Sb-Te based phase change materials are considered as a prime candidate for optical and electrical data storage applications. With the application of an optical or electrical pulse, they can be reversibly switched between amorphous and crystalline state, thereby exhibiting large optical and electrical contrast between the two phases, which are then stored as information in the form of binary digits. Single crystalline growth is interesting from both the academic and industrial perspective, as ordered Ge-Sb-Te based metamaterials are known to exhibit switching at reduced energies. The present study deals with the epitaxial growth and analysis of Ge-Sb-Te based thin films. The first part of the thesis deals with the epitaxial growth of GeTe. Thin films of GeTe were grown on highly mismatched Si(111) and (001) substrates. On both the substrate orientations the film grows along [111] direction with an amorphous-to-crystalline transition observed during the initial stages of growth. The amorphous-to-crystalline transition was studied in-vivo using azimuthal reflection high-energy electron diffraction scans and grazing incidence X-ray diffraction. In the second part of the thesis epitaxy and characterization of Sb 2 Te 3 thin films are presented. The third part of the thesis deals with the epitaxy of ternary Ge-Sb-Te alloys. The composition of the films are shown to be highly dependent on growth temperatures and vary along the pseudobinary line from Sb 2 Te 3 to GeTe with increase in growth temperatures. A line-of-sight quadrupole mass spectrometer was used to reliably control the GeSbTe growth temperature. Growth was performed at different Ge, Sb, Te fluxes to study the compositional variation of the films. Incommensurate peaks are observed along the [111] direction by X-ray diffraction. The possibility of superstructural vacancy ordering along the [111] direction is discussed.

  17. Control of chemical bonding of the ZnO surface grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Ogata, K.; Komuro, T.; Hama, K.; Koike, K.; Sasa, S.; Inoue, M.; Yano, M.

    2004-01-01

    Toward the fabrication of enzyme modified field effect transistors (EnFETs) as one of organic/inorganic hybridized structures, surface bonding of the ZnO grown by molecular beam epitaxy was controlled by ex situ treatments. Angle resolved X-ray photoelectron spectroscopy (XPS) measurement revealed that O-H bonds exist at the surface of ZnO. It was found that the number of O-H bond could be changed with reversibility using plasma and thermal treatments

  18. Dynamical x-ray diffraction studies of interfacial strain in superlattices grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Vandenberg, J.M.; Chu, S.N.G.; Hamm, R.A.; Panish, M.B.; Ritter, D.; Mancrander, A.T.

    1992-01-01

    This paper reports on dynamical X-ray diffraction studies that have been carried out for lattice-matched InGaAs/InP superlattices grown by modified molecular beam epitaxy (MBE) techniques. The (400) X-ray satellite pattern, which is predominantly affected by the strain modulation, was analyzed. The strain and thickness of the actual layers including the presence of strained interfacial regions were determined

  19. Epitaxial growth of manganese oxide films on MgAl2O4 (001) substrates and the possible mechanism

    Science.gov (United States)

    Ren, Lizhu; Wu, Shuxiang; Zhou, Wenqi; Li, Shuwei

    2014-03-01

    Three types of manganese oxide films were grown on MgAl2O4 (001) substrates by plasma-assisted molecular beam epitaxy (PA-MBE) under different growth rates and substrate temperatures. The structural characteristics and chemical compositions of the films were investigated by using in-situ reflection high-energy electron diffraction (RHEED), ex-situ X-ray diffraction, Raman, and X-ray photoelectron spectra (XPS). At a lower substrate temperature (730 K), the epitaxial film tends to form mixed phases with a coexistence of Mn3O4 and Mn5O8 in order to relieve the mismatch-strain. However, at a higher substrate temperature (750 K), all of the films crystallize into Mn3O4; the critical thickness of the film grown under a lower growth rate (7 Å/min) is much larger than that under a high growth rate (10 Å/min). When the film reaches a certain critical thickness, the surface will become fairly rough, and another oriented phase Mn3O4 would crystallize on such a surface.

  20. Epitaxial growth and optical investigations of ZnTeO alloys

    International Nuclear Information System (INIS)

    Nabetani, Y.; Okuno, T.; Aoki, K.; Kato, T.; Matsumoto, T.; Hirai, T.

    2006-01-01

    We have grown zincblende-structured ZnTeO alloy semiconductors on GaAs substrates by molecular beam epitaxy using RF-excited O. O concentrations measured by secondary ion mass spectroscopy were found to increase with the increase of O 2 flow rate supplied during the growth, while the change of lattice constant measured by X-ray diffraction does not follow Vegard's law. It is considered that the O atoms are incorporated not only into group-VI sites but also as interstitials. Formation of other compounds such as ZnTeO 3 , Zn 2 Te 3 O 8 , and TeO 2 was not detected. Optical reflectance spectroscopy revealed the increase of the band-gap energy with O concentration that can be interpreted as the repulsive interaction between the energy states originated in the localized states of O and the conduction-band edge of host ZnTe. (copyright 2006 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (Abstract Copyright [2006], Wiley Periodicals, Inc.)

  1. Boron, arsenic and phosphorus dopant incorporation during low temperature low pressure silicon epitaxial growth

    International Nuclear Information System (INIS)

    Borland, J.O.; Thompson, T.; Tagle, V.; Benzing, W.

    1987-01-01

    Submicron silicon epitaxial structures with very abrupt epi/substrate transition widths have been realized through the use of low temperature silicon epitaxial growth techniques. At these low temperature and low pressure epitaxial growth conditions there is minimal, if any, dopant diffusion from the substrate into the epilayer during deposition. The reincorporation of autodoped dopant as well as the incorporation of intentional dopant can be a trade-off at low temperatures and low pressures. For advanced CMOS and Bi-CMOS technologies, five to six orders of magnitude change in concentration levels are desirable. In this investigation, all of the epitaxial depositions were carried out in an AMC-7810 epi-reactor with standard jets for a turbulent mixing system, and using a modified center inject configuration to achieve a single pass laminar flow system. To simulate the reincorporation of various autodoped dopant, the authors ran a controlled dopant flow of 100 sccm for each of the three dopants (boron, phosphorus and arsenic) to achieve the controlled background dopant level in the reactor gas stream

  2. Growth mechanisms for Si epitaxy on O atomic layers: Impact of O-content and surface structure

    Energy Technology Data Exchange (ETDEWEB)

    Jayachandran, Suseendran, E-mail: suseendran.jayachandran@imec.be [Imec, Kapeldreef 75, 3001 Leuven (Belgium); KU Leuven (University of Leuven), Department of Metallurgy and Materials, Castle Arenberg 44, B-3001 Leuven (Belgium); Billen, Arne [Imec, Kapeldreef 75, 3001 Leuven (Belgium); KU Leuven (University of Leuven), Department of Chemistry, Celestijnenlaan 200F, B-3001 Leuven (Belgium); Douhard, Bastien; Conard, Thierry; Meersschaut, Johan; Moussa, Alain; Caymax, Matty; Bender, Hugo [Imec, Kapeldreef 75, 3001 Leuven (Belgium); Vandervorst, Wilfried [Imec, Kapeldreef 75, 3001 Leuven (Belgium); KU Leuven (University of Leuven), Department of Physics and Astronomy, Celestijnenlaan 200D, B-3001 Leuven (Belgium); Heyns, Marc [Imec, Kapeldreef 75, 3001 Leuven (Belgium); KU Leuven (University of Leuven), Department of Metallurgy and Materials, Castle Arenberg 44, B-3001 Leuven (Belgium); Delabie, Annelies [Imec, Kapeldreef 75, 3001 Leuven (Belgium); KU Leuven (University of Leuven), Department of Chemistry, Celestijnenlaan 200F, B-3001 Leuven (Belgium)

    2016-10-30

    Highlights: • O{sub 3} or O{sub 2} exposures on H-Si(100) result in O ALs with different surface structures. • Si-EPI on O AL using O{sub 3} process is by direct epitaxial growth mechanism. • Si-EPI on O AL using O{sub 2} process is by epitaxial lateral overgrowth mechanism. • Distortions by O AL, SiH{sub 4} flux rate and Si thickness has an impact on Si-EPI quality. - Abstract: The epitaxial growth of Si layers on Si substrates in the presence of O atoms is generally considered a challenge, as O atoms degrade the epitaxial quality by generating defects. Here, we investigate the growth mechanisms for Si epitaxy on O atomic layers (ALs) with different O-contents and structures. O ALs are deposited by ozone (O{sub 3}) or oxygen (O{sub 2}) exposure on H-terminated Si at 50 °C and 300 °C respectively. Epitaxial Si is deposited by chemical vapor deposition using silane (SiH{sub 4}) at 500 °C. After O{sub 3} exposure, the O atoms are uniformly distributed in Si-Si dimer/back bonds. This O layer still allows epitaxial seeding of Si. The epitaxial quality is enhanced by lowering the surface distortions due to O atoms and by decreasing the arrival rate of SiH{sub 4} reactants, allowing more time for surface diffusion. After O{sub 2} exposure, the O atoms are present in the form of SiO{sub x} clusters. Regions of hydrogen-terminated Si remain present between the SiO{sub x} clusters. The epitaxial seeding of Si in these structures is realized on H-Si regions, and an epitaxial layer grows by a lateral overgrowth mechanism. A breakdown in the epitaxial ordering occurs at a critical Si thickness, presumably by accumulation of surface roughness.

  3. A high resolution cross section transmission electron microscopy study of epitaxial rare earth fluoride/GaAs(111) interfaces prepared by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Chien, C.J.; Bravman, J.C.

    1990-01-01

    The authors report the HRXTEM study of epitaxial rare earth fluoride/GaAs(111) interfaces. Such interfaces are of interest because they are the starting point for growth of buried epitaxial rare earth/rare earth fluoride sandwich structures which exhibit interesting and non bulk-like magnetic properties. Also, the optical transitions in ultrathin epitaxial NdF 3 films may be influenced by strain and defects in the NdF 3 film and the nature of the interface to GaAs. The authors find that the rare earth fluoride/GaAs interfaces are semi-coherent but chemically abrupt with the transition taking place within 3 Angstrom. However, the interface is physically rough and multiple monolayer steps in the GaAs surface tend to tilt boundaries in the fluoride. The origin of these steps is believed to be thermal etching of the GaAs during the heat- cleaning stage prior to epitaxy. The surface of the fluoride film is much smoother than the initial GaAs surface indicating planarization during epitaxy

  4. Abnormal growth kinetics of h-BN epitaxial monolayer on Ru(0001) enhanced by subsurface Ar species

    Science.gov (United States)

    Wei, Wei; Meng, Jie; Meng, Caixia; Ning, Yanxiao; Li, Qunxiang; Fu, Qiang; Bao, Xinhe

    2018-04-01

    Growth kinetics of epitaxial films often follows the diffusion-limited aggregation mechanism, which shows a "fractal-to-compact" morphological transition with increasing growth temperature or decreasing deposition flux. Here, we observe an abnormal "compact-to-fractal" morphological transition with increasing growth temperature for hexagonal boron nitride growth on the Ru(0001) surface. The unusual growth process can be explained by a reaction-limited aggregation (RLA) mechanism. Moreover, introduction of the subsurface Ar atoms has enhanced this RLA growth behavior by decreasing both reaction and diffusion barriers. Our work may shed light on the epitaxial growth of two-dimensional atomic crystals and help to control their morphology.

  5. Molecular Beam Epitaxy of lithium niobium oxide multifunctional materials

    Science.gov (United States)

    Tellekamp, M. Brooks; Shank, Joshua C.; Doolittle, W. Alan

    2017-04-01

    The role of stoichiometry and growth temperature in the preferential nucleation of material phases in the Li-Nb-O family are explored yielding an empirical growth phase diagram. It is shown that while single parameter variation often produces multi-phase films, combining substrate temperature control with the previously published lithium flux limited growth allows the repeatable growth of high quality single crystalline films of many different oxide phases. Higher temperatures (800-1050 °C) than normally used in MBE were necessary to achieve high quality materials. At these temperatures the desorption of surface species is shown to play an important role in film composition. Using this method single phase films of NbO, NbO2, LiNbO2, Li3NbO4, LiNbO3, and LiNb3O8 have been achieved in the same growth system, all on c-plane sapphire. Finally, the future of these films in functional oxide heterostructures is briefly discussed.

  6. Epitaxial growth of a methoxy-functionalized quaterphenylene on alkali halide surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Balzer, F., E-mail: fbalzer@mci.sdu.dk [University of Southern Denmark, Mads Clausen Institute, Alsion 2, DK-6400 Sønderborg (Denmark); Sun, R. [University of Southern Denmark, Mads Clausen Institute, Alsion 2, DK-6400 Sønderborg (Denmark); Parisi, J. [University of Oldenburg, Energy and Semiconductor Research Laboratory, Institute of Physics, Carl-von-Ossietzky-Str. 9-11, D-26111 Oldenburg (Germany); Rubahn, H.-G. [University of Southern Denmark, Mads Clausen Institute, Alsion 2, DK-6400 Sønderborg (Denmark); Lützen, A. [University of Bonn, Kekulé Institute of Organic Chemistry and Biochemistry, Gerhard-Domagk-Str. 1, D-53121 Bonn (Germany); Schiek, M. [University of Oldenburg, Energy and Semiconductor Research Laboratory, Institute of Physics, Carl-von-Ossietzky-Str. 9-11, D-26111 Oldenburg (Germany)

    2015-12-31

    The epitaxial growth of the methoxy functionalized para-quaterphenylene (MOP4) on the (001) faces of the alkali halides NaCl and KCl and on glass is investigated by a combination of low energy electron diffraction (LEED), polarized light microscopy (PLM), atomic force microscopy (AFM), and X-ray diffraction (XRD). Both domains from upright molecules as well as fiber-like crystallites from lying molecules form. Neither a wetting layer from lying molecules nor widespread epitaxial fiber growth on the substrates is detected. Our results focus on the upright standing molecules, which condense into a thin film phase with an enlarged layer spacing compared to the bulk phase. - Highlights: • Growth of a methoxy-functionalized para-phenylene on dielectric surfaces is investigated. • Low-energy electron diffraction and X-ray diffraction techniques are employed for structural characterization. • Epitaxial growth of upright molecules only is documented. • Polarized optical microscopy together with atomic force microscopy complements the findings.

  7. Epitaxial growth of a methoxy-functionalized quaterphenylene on alkali halide surfaces

    International Nuclear Information System (INIS)

    Balzer, F.; Sun, R.; Parisi, J.; Rubahn, H.-G.; Lützen, A.; Schiek, M.

    2015-01-01

    The epitaxial growth of the methoxy functionalized para-quaterphenylene (MOP4) on the (001) faces of the alkali halides NaCl and KCl and on glass is investigated by a combination of low energy electron diffraction (LEED), polarized light microscopy (PLM), atomic force microscopy (AFM), and X-ray diffraction (XRD). Both domains from upright molecules as well as fiber-like crystallites from lying molecules form. Neither a wetting layer from lying molecules nor widespread epitaxial fiber growth on the substrates is detected. Our results focus on the upright standing molecules, which condense into a thin film phase with an enlarged layer spacing compared to the bulk phase. - Highlights: • Growth of a methoxy-functionalized para-phenylene on dielectric surfaces is investigated. • Low-energy electron diffraction and X-ray diffraction techniques are employed for structural characterization. • Epitaxial growth of upright molecules only is documented. • Polarized optical microscopy together with atomic force microscopy complements the findings.

  8. Sidewall GaAs tunnel junctions fabricated using molecular layer epitaxy

    Directory of Open Access Journals (Sweden)

    Takeo Ohno and Yutaka Oyama

    2012-01-01

    Full Text Available In this article we review the fundamental properties and applications of sidewall GaAs tunnel junctions. Heavily impurity-doped GaAs epitaxial layers were prepared using molecular layer epitaxy (MLE, in which intermittent injections of precursors in ultrahigh vacuum were applied, and sidewall tunnel junctions were fabricated using a combination of device mesa wet etching of the GaAs MLE layer and low-temperature area-selective regrowth. The fabricated tunnel junctions on the GaAs sidewall with normal mesa orientation showed a record peak current density of 35 000 A cm-2. They can potentially be used as terahertz devices such as a tunnel injection transit time effect diode or an ideal static induction transistor.

  9. Epitaxial growth of fcc-CoxNi100-x thin films on MgO(110) single-crystal substrates

    International Nuclear Information System (INIS)

    Ohtake, Mitsuru; Nukaga, Yuri; Sato, Yoichi; Futamoto, Masaaki; Kirino, Fumiyoshi

    2009-01-01

    Co x Ni 100-x (x=100, 80, 20, 0 at. %) epitaxial thin films were prepared on MgO(110) single-crystal substrates heated at 300 deg. C by ultrahigh vacuum molecular beam epitaxy. The growth mechanism is discussed based on lattice strain and crystallographic defects. CoNi(110) single-crystal films with a fcc structure are obtained for all compositions. Co x Ni 100-x film growth follows the Volmer-Weber mode. X-ray diffraction analysis indicates that the out-of-plane and the in-plane lattice spacings of the Co x Ni 100-x films are in agreement within ±0.5% with the values of the respective bulk Co x Ni 100-x crystals, suggesting that the strain in the film is very small. High-resolution cross-sectional transmission microscopy shows that an atomically sharp boundary is formed between a Co(110) fcc film and a MgO(110) substrate, where periodical misfit dislocations are preferentially introduced in the film at the Co/MgO interface. The presence of such periodical misfit dislocations relieves the strain caused by the lattice mismatch between the film and the substrate.

  10. In situ synchrotron X-ray diffraction study on epitaxial-growth dynamics of III–V semiconductors

    Science.gov (United States)

    Takahasi, Masamitu

    2018-05-01

    The application of in situ synchrotron X-ray diffraction (XRD) to the molecular-beam epitaxial (MBE) growth of III–V semiconductors is overviewed along with backgrounds of the diffraction theory and instrumentation. X-rays are sensitive not only to the surface of growing films but also to buried interfacial structures because of their large penetration depth. Moreover, a spatial coherence length up to µm order makes X-rays widely applicable to the characterization of low-dimensional structures, such as quantum dots and wires. In situ XRD studies during growth were performed using an X-ray diffractometer, which was combined with an MBE chamber. X-ray reciprocal space mapping at a speed matching a typical growth rate was achieved using intense X-rays available from a synchrotron light source and an area detector. The importance of measuring the three-dimensional distribution of XRD intensity in a reciprocal space map is demonstrated for the MBE growth of two-, one-, and zero-dimensional structures. A large amount of information about the growth process of two-dimensional InGaAs/GaAs(001) epitaxial films has been provided by three-dimensional X-ray reciprocal mappings, including the anisotropic strain relaxation, the compositional inhomogeneity, and the evolution of surface and interfacial roughness. For one-dimensional GaAs nanowires grown in a Au-catalyzed vapor-liquid–solid mode, the relationship between the diameter of the nanowires and the formation of polytypes has been suggested on the basis of in situ XRD measurements. In situ three-dimensional X-ray reciprocal space mapping is also shown to be useful for determining the lateral and vertical sizes of self-assembled InAs/GaAs(001) quantum dots as well as their internal strain distributions during growth.

  11. Epitaxial growth of zinc on ferritic steel under high current density electroplating conditions

    International Nuclear Information System (INIS)

    Greul, Thomas; Comenda, Christian; Preis, Karl; Gerdenitsch, Johann; Sagl, Raffaela; Hassel, Achim Walter

    2013-01-01

    Highlights: •EBSD of electroplated Zn on Fe or steel was performed. •Zn grows epitaxially on electropolished ferritic steel following Burger's orientation relation. •Surface deformation of steel leads to multiple electroplated zinc grains with random orientation. •Zn grows epitaxially even on industrial surfaces with little surface deformation. •Multiple zinc grains on one steel grain can show identical orientation relations. -- Abstract: The dependence of the crystal orientation of electrodeposited zinc of the grain orientation on ferritic steel substrate at high current density deposition (400 mA cm −2 ) during a pulse-plating process was investigated by means of EBSD (electron backscatter diffraction) measurements. EBSD-mappings of surface and cross-sections were performed on samples with different surface preparations. Furthermore an industrial sample was investigated to compare lab-coated samples with the industrial process. The epitaxial growth of zinc is mainly dependent on the condition of the steel grains. Deformation of steel grains leads to random orientation while zinc grows epitaxially on non-deformed steel grains even on industrial surfaces

  12. Liquid phase electro epitaxy growth kinetics of GaAs-A three-dimensional numerical simulation study

    International Nuclear Information System (INIS)

    Mouleeswaran, D.; Dhanasekaran, R.

    2006-01-01

    A three-dimensional numerical simulation study for the liquid phase electro epitaxial growth kinetic of GaAs is presented. The kinetic model is constructed considering (i) the diffusive and convective mass transport, (ii) the heat transfer due to thermoelectric effects such as Peltier effect, Joule effect and Thomson effect, (iii) the electric current distribution with electromigration and (iv) the fluid flow coupled with concentration and temperature fields. The simulations are performed for two configurations namely (i) epitaxial growth from the arsenic saturated gallium rich growth solution, i.e., limited solution model and (ii) epitaxial growth from the arsenic saturated gallium rich growth solution with polycrystalline GaAs feed. The governing equations of liquid phase electro epitaxy are solved numerically with appropriate initial and boundary conditions using the central difference method. Simulations are performed to determine the following, a concentration profiles of solute atoms (As) in the Ga-rich growth solution, shape of the substrate evolution, the growth rate of the GaAs epitaxial film, the contributions of Peltier effect and electromigration of solute atoms to the growth with various experimental growth conditions. The growth rate is found to increase with increasing growth temperature and applied current density. The results are discussed in detail

  13. Epitaxial growth of atomically flat gadolinia-doped ceria thin films by pulsed laser deposition

    DEFF Research Database (Denmark)

    Chen, Yunzhong; Pryds, Nini; Schou, Jørgen

    2011-01-01

    Epitaxial growth of Ce0.8Gd0.2O2(CGO) films on (001) TiO2-terminated SrTiO3 substrates by pulsed laser deposition was investigated using in situ reflective high energy electron diffraction. The initial film growth shows a Stransky–Krastanov growth mode. However, this three-dimensional island...... formation is replaced by a two-dimensional island nucleation during further deposition, which results in atomically smooth CGO films. The obtained high-quality CGO films may be attractive for the electrolyte of solid-oxide fuel cells operating at low temperature....

  14. Oxygen engineering of HfO{sub 2-x} thin films grown by reactive molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Hildebrandt, Erwin; Kurian, Jose; Alff, Lambert [Institut fuer Materialwissenschaft, TU-Darmstadt (Germany); Zaumseil, Peter; Schroeder, Thomas [IHP, Frankfurt, Oder (Germany)

    2010-07-01

    Reactive molecular beam epitaxy (R-MBE) is an ideal tool for tailoring physical properties of thin films to specific needs. For the development of cutting-edge oxides for thin film applications a precise control of oxygen defects is crucial. R-MBE in combination with rf-activated oxygen allows reproducibly growing oxide thin films with precise oxidation conditions enabling oxygen engineering. R-MBE was used to grow Hf and HfO{sub 2{+-}}{sub x} thin films with different oxidation conditions on sapphire single crystal substrates. Structural characterization was carried out using rotating anode x-ray diffraction revealing highly textured to epitaxial thin films on c-cut sapphire. Furthermore, switching of film orientation by varying the oxidation conditions was observed demonstrating the role of oxygen in the growth procedure. The investigation of electrical properties using a four probe measurement setup showed conductivities in the range of 1000 {mu}{omega}cm for oxygen deficient HfO{sub 2-x} thin films. Optical properties were investigated using a photospectrometer and additionally x-ray photoelectron spectroscopy was carried out to study the band gap and valence states. Both techniques were used to monitor the oxygen content in deficient HfO{sub 2-x} thin films. Our results demonstrate the importance of oxygen engineering even in the case of 'simple' oxides.

  15. Electrical transport in n-type ZnMgSSe grown by molecular beam epitaxy on GaAs

    International Nuclear Information System (INIS)

    Marshall, T.; Petruzzello, J.A.; Herko, S.P.

    1994-01-01

    Significant progress in improving the Performance of blue-green II-VI semiconductor injection lasers has come about from advances in the epitaxial growth and doping of ZnMgSSe on GaAs substrates. This paper investigates electrical transport and its relation to structural quality in n-type Zn 1-y Mg y S x Se 1-x epilayers doped with Cl, grown by molecular beam epitaxy. The composition parameters x and y vary from about 0.12-0.18 and 0.08-0.15, respectively. The quaternary epilayers studied are lattice-matched (or nearly so) to the GaAs substrate. Temperature-dependent Hall-effect measurements are performed on seven n-type ZnMgSSe:Cl epilayers, and a technique is presented whereby the resulting mobility-vs-temperature data is compared with data for ZnSe to obtain a structural figure of merit that is useful in characterizing the quaternary epilayer. 29 refs., 4 figs

  16. Epitaxial growth of InP on SI by MOCVD

    International Nuclear Information System (INIS)

    Konushi, F.; Seki, A.; Kudo, J.; Sato, H.; Kakimoto, S.; Fukushima, T.; Kubota, Y.; Koba, M.

    1988-01-01

    The authors have studied the heteroepitaxial growth of InP on large diameter Si substrates using MOCVD. A new MOCVD system with four inch wafer size capability was utilized in the growth. Single domain InP films have been successfully grown on four inch Si substrates by using a new heterostructure with a thin GaAs intermediate layer. In this paper, the authors describe the crystalline quality and residual stress of InP epilayers, estimated by etch pit density and x-ray diffraction, respectively. The authors also reports on the reduction of EPD by post-growth annealing

  17. Thin film evolution equations from (evaporating) dewetting liquid layers to epitaxial growth

    International Nuclear Information System (INIS)

    Thiele, U

    2010-01-01

    In the present contribution we review basic mathematical results for three physical systems involving self-organizing solid or liquid films at solid surfaces. The films may undergo a structuring process by dewetting, evaporation/condensation or epitaxial growth, respectively. We highlight similarities and differences of the three systems based on the observation that in certain limits all of them may be described using models of similar form, i.e. time evolution equations for the film thickness profile. Those equations represent gradient dynamics characterized by mobility functions and an underlying energy functional. Two basic steps of mathematical analysis are used to compare the different systems. First, we discuss the linear stability of homogeneous steady states, i.e. flat films, and second the systematics of non-trivial steady states, i.e. drop/hole states for dewetting films and quantum-dot states in epitaxial growth, respectively. Our aim is to illustrate that the underlying solution structure might be very complex as in the case of epitaxial growth but can be better understood when comparing the much simpler results for the dewetting liquid film. We furthermore show that the numerical continuation techniques employed can shed some light on this structure in a more convenient way than time-stepping methods. Finally we discuss that the usage of the employed general formulation does not only relate seemingly unrelated physical systems mathematically, but does allow as well for discussing model extensions in a more unified way.

  18. Understanding the Growth Mechanism of GaN Epitaxial Layers on Mechanically Exfoliated Graphite.

    Science.gov (United States)

    Li, Tianbao; Liu, Chenyang; Zhang, Zhe; Yu, Bin; Dong, Hailiang; Jia, Wei; Jia, Zhigang; Yu, Chunyan; Gan, Lin; Xu, Bingshe; Jiang, Haiwei

    2018-04-27

    The growth mechanism of GaN epitaxial layers on mechanically exfoliated graphite is explained in detail based on classic nucleation theory. The number of defects on the graphite surface can be increased via O-plasma treatment, leading to increased nucleation density on the graphite surface. The addition of elemental Al can effectively improve the nucleation rate, which can promote the formation of dense nucleation layers and the lateral growth of GaN epitaxial layers. The surface morphologies of the nucleation layers, annealed layers and epitaxial layers were characterized by field-emission scanning electron microscopy, where the evolution of the surface morphology coincided with a 3D-to-2D growth mechanism. High-resolution transmission electron microscopy was used to characterize the microstructure of GaN. Fast Fourier transform diffraction patterns showed that cubic phase (zinc-blend structure) GaN grains were obtained using conventional GaN nucleation layers, while the hexagonal phase (wurtzite structure) GaN films were formed using AlGaN nucleation layers. Our work opens new avenues for using highly oriented pyrolytic graphite as a substrate to fabricate transferable optoelectronic devices.

  19. Strain-symmetrized Si/SiGe multi-quantum well structures grown by molecular beam epitaxy for intersubband engineering

    International Nuclear Information System (INIS)

    Zhao, M.; Karim, A.; Ni, W.-X.; Pidgeon, C.R.; Phillips, P.J.; Carder, D.; Murdin, B.N.; Fromherz, T.; Paul, D.J.

    2006-01-01

    Three strain-symmetrized Si/SiGe multi-quantum well structures, designed for probing the carrier lifetime of intrawell intersubband transitions between heavy hole 1 (HH1) and light hole 1 (LH1) states with transition energies below the optical phonon energy, were grown by molecular beam epitaxy at low temperature on fully relaxed SiGe virtual substrates. The grown structures were characterized by using various experimental techniques, showing a high crystalline quality and very precise growth control. The lifetime of the LH1 excited state was determined directly with pump-probe spectroscopy. The measurements indicated an increase of the lifetime by a factor of ∼2 due to the increasingly unconfined LH1 state, which agreed very well with the design. It also showed a very long lifetime of several hundred picoseconds for the holes excited out of the well to transit back to the well through a diagonal process

  20. Mg doping of GaN grown by plasma-assisted molecular beam epitaxy under nitrogen-rich conditions

    International Nuclear Information System (INIS)

    Zhang Meng; Bhattacharya, Pallab; Guo Wei; Banerjee, Animesh

    2010-01-01

    Acceptor doping of GaN with Mg during plasma-assisted molecular beam epitaxy, under N-rich conditions and a relatively high growth temperature of 740 deg. C, was investigated. The p-doping level steadily increases with increasing Mg flux. The highest doping level achieved, determined from Hall measurements, is 2.1x10 18 cm -3 . The corresponding doping efficiency and hole mobility are ∼4.9% and 3.7 cm 2 /V s at room temperature. Cross-sectional transmission electron microscopy and photoluminescence measurements confirm good crystalline and optical quality of the Mg-doped layers. An InGaN/GaN quantum dot light emitting diode (λ peak =529 nm) with p-GaN contact layers grown under N-rich condition exhibits a low series resistance of 9.8 Ω.

  1. Nucleation of single GaN nanorods with diameters smaller than 35 nm by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Chen, Yen-Ting; Araki, Tsutomu; Palisaitis, Justinas; Persson, Per O. Å.; Olof Holtz, Per; Birch, Jens; Chen, Li-Chyong; Chen, Kuei-Hsien; Nanishi, Yasushi

    2013-01-01

    Nucleation mechanism of catalyst-free GaN nanorod grown on Si(111) is investigated by the fabrication of uniform and narrow (<35 nm) nanorods without a pre-defined mask by molecular beam epitaxy. Direct evidences show that the nucleation of GaN nanorods stems from the sidewall of the underlying islands down to the Si(111) substrate, different from commonly reported ones on top of the island directly. Accordingly, the growth and density control of the nanorods is exploited by a “narrow-pass” approach that only narrow nanorod can be grown. The optimal size of surrounding non-nucleation area around single nanorod is estimated as 88 nm

  2. Nucleation of single GaN nanorods with diameters smaller than 35 nm by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Yen-Ting [Institute of Atomic and Molecular Sciences, Academia Sinica, 10617 Taipei, Taiwan (China); Department of Physics, Chemistry and Biology (IFM), Linköping University, S-58183 Linköping (Sweden); Araki, Tsutomu [Department of Electrical and Electronic Engineering, Ritsumeikan University, 525-8577 Shiga (Japan); Palisaitis, Justinas; Persson, Per O. Å.; Olof Holtz, Per; Birch, Jens [Department of Physics, Chemistry and Biology (IFM), Linköping University, S-58183 Linköping (Sweden); Chen, Li-Chyong [Center for Condensed Matter Sciences, National Taiwan University, 10617 Taipei, Taiwan (China); Chen, Kuei-Hsien [Institute of Atomic and Molecular Sciences, Academia Sinica, 10617 Taipei, Taiwan (China); Center for Condensed Matter Sciences, National Taiwan University, 10617 Taipei, Taiwan (China); Nanishi, Yasushi [Global Innovation Research Organization, Ritsumeikan University, 525-8577 Shiga (Japan)

    2013-11-11

    Nucleation mechanism of catalyst-free GaN nanorod grown on Si(111) is investigated by the fabrication of uniform and narrow (<35 nm) nanorods without a pre-defined mask by molecular beam epitaxy. Direct evidences show that the nucleation of GaN nanorods stems from the sidewall of the underlying islands down to the Si(111) substrate, different from commonly reported ones on top of the island directly. Accordingly, the growth and density control of the nanorods is exploited by a “narrow-pass” approach that only narrow nanorod can be grown. The optimal size of surrounding non-nucleation area around single nanorod is estimated as 88 nm.

  3. Electrical performance of phase change memory cells with Ge3Sb2Te6 deposited by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Boschker, Jos E.; Riechert, Henning; Calarco, Raffaella; Boniardi, Mattia; Redaelli, Andrea

    2015-01-01

    Here, we report on the electrical characterization of phase change memory cells containing a Ge 3 Sb 2 Te 6 (GST) alloy grown in its crystalline form by Molecular Beam Epitaxy (MBE). It is found that the high temperature growth on the amorphous substrate results in a polycrystalline film exhibiting a rough surface with a grain size of approximately 80–150 nm. A detailed electrical characterization has been performed, including I-V characteristic curves, programming curves, set operation performance, crystallization activation at low temperature, and resistance drift, in order to determine the material related parameters. The results indicate very good alignment of the electrical parameters with the current state-of-the-art GST, deposited by physical vapor deposition. Such alignment enables a possible employment of the MBE deposition technique for chalcogenide materials in the phase change memory technology, thus leading to future studies of as-deposited crystalline chalcogenides as integrated in electrical vehicles

  4. Influence of substrate quality on structural properties of AlGaN/GaN superlattices grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Schubert, F. [NaMLab gGmbH, Nöthnitzer Straße 64, 01187 Dresden (Germany); Merkel, U.; Schmult, S. [TU Dresden, Institute of Semiconductors and Microsystems, Nöthnitzer Straße 64, 01187 Dresden (Germany); Mikolajick, T. [NaMLab gGmbH, Nöthnitzer Straße 64, 01187 Dresden (Germany); TU Dresden, Institute of Semiconductors and Microsystems, Nöthnitzer Straße 64, 01187 Dresden (Germany)

    2014-02-28

    Short-period AlGaN/GaN superlattices were established as versatile test structures to investigate the structural properties of molecular beam epitaxy (MBE)-grown GaN and AlGaN layers and their dependence on the GaN substrate quality. X-ray diffractometry data of the investigated superlattices allow access to relevant structural parameters such as aluminum mole fraction and layer thicknesses. The occurrence of theoretically predicted intense high-order satellite peaks and pronounced interface fringes in the diffraction pattern reflects abrupt interfaces and perfect 2-dimensional growth resulting in smooth surfaces. The data unambiguously demonstrate that the structural quality of the MBE grown layers is limited by the structural properties of the GaN substrate.

  5. Far-infrared phonon spectroscopy of Pb1-xMn xTe layers grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Romcevic, N.; Nadolny, A.J.; Romcevic, M.; Story, T.; Taliashvili, B.; Milutinovic, A.; Trajic, J.; Lusakowska, E.; Vasiljevic-Radovic, D.; Domukhovski, V.; Osinniy, V.; Hadzic, B.; Dziawa, P.

    2007-01-01

    In this paper we used far-infrared spectroscopy, reflection high energy electron diffraction (RHEED), X-ray diffraction and atomic force microscopy (AFM) to investigate structural and optical properties of Pb 1-x Mn x Te layers grown by molecular beam epitaxy (MBE). A numerical model for calculating the reflectivity coefficient for complex systems which include films, buffer layer and substrate has been applied. The infrared reflectivity spectra consist of Pb 1-x Mn x Te phonons, which exhibit intermediate one-two mode behavior, and MnTe phonons. A good agreement between calculated and experimental spectra is achieved. We registered the local distribution of Mn impurities depending on substrate type. For films growth on BaF 2 substrate we registered the orthorhombic local structure of MnTe clusters, while in the case of KCl substrate this structure is cubic. The Pb 1-x Mn x Te long wavelength optical phonons were described by the modified Genzel's model

  6. Characterization of structural defects in SnSe2 thin films grown by molecular beam epitaxy on GaAs (111)B substrates

    Science.gov (United States)

    Tracy, Brian D.; Li, Xiang; Liu, Xinyu; Furdyna, Jacek; Dobrowolska, Margaret; Smith, David J.

    2016-11-01

    Tin selenide thin films have been grown by molecular beam epitaxy on GaAs (111)B substrates at a growth temperature of 150 °C, and a microstructural study has been carried out, primarily using the technique of transmission electron microscopy. The Se:Sn flux ratio during growth was systematically varied and found to have a strong impact on the resultant crystal structure and quality. Low flux ratios (Se:Sn=3:1) led to defective films consisting primarily of SnSe, whereas high flux ratios (Se:Sn>10:1) gave higher quality, single-phase SnSe2. The structure of the monoselenide films was found to be consistent with the Space Group Pnma with the epitaxial growth relationship of [011]SnSe// [ 1 1 bar 0 ] GaAs, while the diselenide films were consistent with the Space Group P 3 bar m1 , and had the epitaxial growth relationship [ 2 1 bar 1 bar 0 ]SnSe2// [ 1 1 bar 0 ] GaAs.

  7. Molecular Beam Epitaxy-Grown InGaN Nanowires and Nanomushrooms for Solid State Lighting

    KAUST Repository

    Gasim, Anwar A.

    2012-05-01

    InGaN is a promising semiconductor for solid state lighting thanks to its bandgap which spans the entire visible regime of the electromagnetic spectrum. InGaN is grown heteroepitaxially due to the absence of a native substrate; however, this results in a strained film and a high dislocation density—two effects that have been associated with efficiency droop, which is the disastrous drop in efficiency of a light-emitting diode (LED) as the input current increases. Heteroepitaxially grown nanowires have recently attracted great interest due to their property of eliminating the detrimental effects of the lattice mismatch and the corollary efficiency droop. In this study, InGaN nanowires were grown on a low-cost Si (111) substrate via molecular beam epitaxy. Unique nanostructures, taking the form of mushrooms, have been observed in localized regions on the samples. These nanomushrooms consist of a nanowire body with a wide cap on top. Photoluminescence characterization revealed that the nanowires emit violet-blue, whilst the nanomushrooms emit a broad yellow-orange-red luminescence. The simultaneous emission from the nanowires and nanomushrooms forms white light. Structural characterization of a single nanomushroom via transmission electron microscopy revealed a simultaneous increase in indium and decrease in gallium at the interface between the body and the cap. Furthermore, the cap itself was found to be indium-rich, confirming it as the source of the longer wavelength yellow-orange-red luminescence. It is believed that the nanomushroom cap formed as a consequence of the saturation of growth on the c-plane of the nanowire. It is proposed that the formation of an indium droplet on the tip of the nanowire saturated growth on the c-plane, forcing the indium and gallium adatoms to incorporate on the sidewall m-planes instead, but only at the nanowire tip. This resulted in the formation of a mushroom-like cap on the tip. How and why the indium droplets formed is not

  8. Epitaxial growth of nobel metals on alumina substrates

    International Nuclear Information System (INIS)

    Al-Mohammad, A.

    2007-06-01

    The influence of the reconstructed (0001) α-Al 2 O 3 surface on the heteroepitaxial growth and adhesion properties of small metal particles (gold, silver and copper) of noncontinuous thin films has been investigated. The crystallographic structure and morphology of substrate surfaces were examined by Reflection High Energy Electron Diffraction and Atomic Force Microscopy techniques. The reconstructed surfaces are terminated by one or more Aluminum atomic layers. By means of the Transmission Electronic Microscopy, the various granulometric and lattice parameters variations are investigated during different stages of the heteroepitaxial growth of metallic thin films. We estimated the adhesion energy values for each case of metal//(0001)α-Al 2 O 3 interfaces by two methods: the maximum cluster density and the Lifshits theory of Van der Waals energy of interfaces. The results of both methods are in good agreement. Using these methods, we found interfaces Hamaker's constants values and we investigated all the heteroepitaxial growth steps.(author)

  9. Effect of growth temperature on the epitaxial growth of ZnO on GaN by ALD

    Science.gov (United States)

    Särkijärvi, Suvi; Sintonen, Sakari; Tuomisto, Filip; Bosund, Markus; Suihkonen, Sami; Lipsanen, Harri

    2014-07-01

    We report on the epitaxial growth of ZnO on GaN template by atomic layer deposition (ALD). Diethylzinc (DEZn) and water vapour (H2O) were used as precursors. The structure and the quality of the grown ZnO layers were studied with scanning electron microscope (SEM), X-ray diffraction (XRD), photoluminescence (PL) measurements and positron annihilation spectroscopy. The ZnO films were confirmed epitaxial, and the film quality was found to improve with increasing deposition temperature in the vicinity of the threshold temperature of two dimensional growth. We conclude that high quality ZnO thin films can be grown by ALD. Interestingly only separate Zn-vacancies were observed in the films, although ZnO thin films typically contain fairly high density of surface pits and vacancy clusters.

  10. Nanoselective area growth of GaN by metalorganic vapor phase epitaxy on 4H-SiC using epitaxial graphene as a mask

    International Nuclear Information System (INIS)

    Puybaret, Renaud; Jordan, Matthew B.; Voss, Paul L.; Ougazzaden, Abdallah; Patriarche, Gilles; Sundaram, Suresh; El Gmili, Youssef; Salvestrini, Jean-Paul; Heer, Walt A. de; Berger, Claire

    2016-01-01

    We report the growth of high-quality triangular GaN nanomesas, 30-nm thick, on the C-face of 4H-SiC using nanoselective area growth (NSAG) with patterned epitaxial graphene grown on SiC as an embedded mask. NSAG alleviates the problems of defects in heteroepitaxy, and the high mobility graphene film could readily provide the back low-dissipative electrode in GaN-based optoelectronic devices. A 5–8 graphene-layer film is first grown on the C-face of 4H-SiC by confinement-controlled sublimation of silicon carbide. Graphene is then patterned and arrays of 75-nm-wide openings are etched in graphene revealing the SiC substrate. A 30-nm-thick GaN is subsequently grown by metal organic vapor phase epitaxy. GaN nanomesas grow epitaxially with perfect selectivity on SiC, in the openings patterned through graphene. The up-or-down orientation of the mesas on SiC, their triangular faceting, and cross-sectional scanning transmission electron microscopy show that they are biphasic. The core is a zinc blende monocrystal surrounded with single-crystal wurtzite. The GaN crystalline nanomesas have no threading dislocations or V-pits. This NSAG process potentially leads to integration of high-quality III-nitrides on the wafer scalable epitaxial graphene/silicon carbide platform.

  11. Nanoselective area growth of GaN by metalorganic vapor phase epitaxy on 4H-SiC using epitaxial graphene as a mask

    Energy Technology Data Exchange (ETDEWEB)

    Puybaret, Renaud; Jordan, Matthew B.; Voss, Paul L.; Ougazzaden, Abdallah, E-mail: aougazza@georgiatech-metz.fr [School of Electrical and Computer Engineering, Georgia Institute of Technology, Atlanta, Georgia 30332 (United States); CNRS UMI 2958, Georgia Institute of Technology, 2 Rue Marconi, 57070 Metz (France); Patriarche, Gilles [CNRS, Laboratoire de Photonique et de Nanostructures, Route de Nozay, 91460 Marcoussis (France); Sundaram, Suresh; El Gmili, Youssef [CNRS UMI 2958, Georgia Institute of Technology, 2 Rue Marconi, 57070 Metz (France); Salvestrini, Jean-Paul [Université de Lorraine, CentraleSupélec, LMOPS, EA4423, 57070 Metz (France); Heer, Walt A. de [School of Physics, Georgia Institute of Technology, Atlanta, Georgia 30332 (United States); Berger, Claire [School of Physics, Georgia Institute of Technology, Atlanta, Georgia 30332 (United States); CNRS, Institut Néel, BP166, 38042 Grenoble Cedex 9 (France)

    2016-03-07

    We report the growth of high-quality triangular GaN nanomesas, 30-nm thick, on the C-face of 4H-SiC using nanoselective area growth (NSAG) with patterned epitaxial graphene grown on SiC as an embedded mask. NSAG alleviates the problems of defects in heteroepitaxy, and the high mobility graphene film could readily provide the back low-dissipative electrode in GaN-based optoelectronic devices. A 5–8 graphene-layer film is first grown on the C-face of 4H-SiC by confinement-controlled sublimation of silicon carbide. Graphene is then patterned and arrays of 75-nm-wide openings are etched in graphene revealing the SiC substrate. A 30-nm-thick GaN is subsequently grown by metal organic vapor phase epitaxy. GaN nanomesas grow epitaxially with perfect selectivity on SiC, in the openings patterned through graphene. The up-or-down orientation of the mesas on SiC, their triangular faceting, and cross-sectional scanning transmission electron microscopy show that they are biphasic. The core is a zinc blende monocrystal surrounded with single-crystal wurtzite. The GaN crystalline nanomesas have no threading dislocations or V-pits. This NSAG process potentially leads to integration of high-quality III-nitrides on the wafer scalable epitaxial graphene/silicon carbide platform.

  12. Factors influencing epitaxial growth of three-dimensional Ge quantum dot crystals on pit-patterned Si substrate

    International Nuclear Information System (INIS)

    Ma, Y J; Zhong, Z; Yang, X J; Fan, Y L; Jiang, Z M

    2013-01-01

    We investigated the molecular beam epitaxy growth of three-dimensional (3D) Ge quantum dot crystals (QDCs) on periodically pit-patterned Si substrates. A series of factors influencing the growth of QDCs were investigated in detail and the optimized growth conditions were found. The growth of the Si buffer layer and the first quantum dot (QD) layer play a key role in the growth of QDCs. The pit facet inclination angle decreased with increasing buffer layer thickness, and its optimized value was found to be around 21°, ensuring that all the QDs in the first layer nucleate within the pits. A large Ge deposition amount in the first QD layer favors strain build-up by QDs, size uniformity of QDs and hence periodicity of the strain distribution; a thin Si spacer layer favors strain correlation along the growth direction; both effects contribute to the vertical ordering of the QDCs. Results obtained by atomic force microscopy and cross-sectional transmission electron microscopy showed that 3D ordering was achieved in the Ge QDCs with the highest ever areal dot density of 1.2 × 10 10 cm −2 , and that the lateral and the vertical interdot spacing were ∼10 and ∼2.5 nm, respectively. (paper)

  13. Factors influencing epitaxial growth of three-dimensional Ge quantum dot crystals on pit-patterned Si substrate.

    Science.gov (United States)

    Ma, Y J; Zhong, Z; Yang, X J; Fan, Y L; Jiang, Z M

    2013-01-11

    We investigated the molecular beam epitaxy growth of three-dimensional (3D) Ge quantum dot crystals (QDCs) on periodically pit-patterned Si substrates. A series of factors influencing the growth of QDCs were investigated in detail and the optimized growth conditions were found. The growth of the Si buffer layer and the first quantum dot (QD) layer play a key role in the growth of QDCs. The pit facet inclination angle decreased with increasing buffer layer thickness, and its optimized value was found to be around 21°, ensuring that all the QDs in the first layer nucleate within the pits. A large Ge deposition amount in the first QD layer favors strain build-up by QDs, size uniformity of QDs and hence periodicity of the strain distribution; a thin Si spacer layer favors strain correlation along the growth direction; both effects contribute to the vertical ordering of the QDCs. Results obtained by atomic force microscopy and cross-sectional transmission electron microscopy showed that 3D ordering was achieved in the Ge QDCs with the highest ever areal dot density of 1.2 × 10(10) cm(-2), and that the lateral and the vertical interdot spacing were ~10 and ~2.5 nm, respectively.

  14. Step driven competitive epitaxial and self-limited growth of graphene on copper surface

    Directory of Open Access Journals (Sweden)

    Lili Fan

    2011-09-01

    Full Text Available The existence of surface steps was found to have significant function and influence on the growth of graphene on copper via chemical vapor deposition. The two typical growth modes involved were found to be influenced by the step morphologies on copper surface, which led to our proposed step driven competitive growth mechanism. We also discovered a protective role of graphene in preserving steps on copper surface. Our results showed that wide and high steps promoted epitaxial growth and yielded multilayer graphene domains with regular shape, while dense and low steps favored self-limited growth and led to large-area monolayer graphene films. We have demonstrated that controllable growth of graphene domains of specific shape and large-area continuous graphene films are feasible.

  15. Growth of Sr2CrReO6 epitaxial thin films by pulsed laser deposition

    International Nuclear Information System (INIS)

    Orna, J.; Morellon, L.; Algarabel, P.A.; Pardo, J.A.; Magen, C.; Varela, M.; Pennycook, S.J.; De Teresa, J.M.; Ibarra, M.R.

    2010-01-01

    We report the growth, structural, magnetic, and electrical transport properties of epitaxial Sr 2 CrReO 6 thin films. We have succeeded in depositing films with a high crystallinity and a relatively large cationic order in a narrow window of growth parameters. The epitaxy relationship is Sr 2 CrReO 6 (SCRO) (0 0 1) [1 0 0]-parallel SrTiO 3 (STO) (0 0 1) [1 1 0] as determined by high-resolution X-ray diffraction and scanning transmission electron microscopy (STEM). Typical values of saturation magnetization of M S (300 K)=1 μ B /f.u. and ρ (300 K)=2.8 mΩ cm have been obtained in good agreement with previous published results in sputtered epitaxial thin films. We estimate that the antisite defects concentration in our thin films is of the order of 14%, and the measured Curie temperature is T C =481(2) K. We believe these materials be of interest as electrodes in spintronic devices.

  16. Epitaxial Growth of Hard Ferrimagnetic Mn3Ge Film on Rhodium Buffer Layer

    Directory of Open Access Journals (Sweden)

    Atsushi Sugihara

    2015-06-01

    Full Text Available Mn\\(_3\\Ge has a tetragonal Heusler-like D0\\(_{22}\\ crystal structure, exhibiting a large uniaxial magnetic anisotropy and small saturation magnetization due to its ferrimagnetic spin structure; thus, it is a hard ferrimagnet. In this report, epitaxial growth of a Mn\\(_3\\Ge film on a Rh buffer layer was investigated for comparison with that of a film on a Cr buffer layer in terms of the lattice mismatch between Mn\\(_3\\Ge and the buffer layer. The film grown on Rh had much better crystalline quality than that grown on Cr, which can be attributed to the small lattice mismatch. Epitaxial films of Mn\\(_3\\Ge on Rh show somewhat small coercivity (\\(H_{\\rm c}\\ = 12.6 kOe and a large perpendicular magnetic anisotropy (\\(K_{\\rm u}\\ = 11.6 Merg/cm\\(^3\\, comparable to that of the film grown on Cr.

  17. Demonstration of molecular beam epitaxy and a semiconducting band structure for I-Mn-V compounds

    International Nuclear Information System (INIS)

    Jungwirth, T.; Novak, V.; Cukr, M.; Zemek, J.; Marti, X.; Horodyska, P.; Nemec, P.; Holy, V.; Maca, F.; Shick, A. B.; Masek, J.; Kuzel, P.; Nemec, I.; Gallagher, B. L.; Campion, R. P.; Foxon, C. T.; Wunderlich, J.

    2011-01-01

    Our ab initio theory calculations predict a semiconducting band structure of I-Mn-V compounds. We demonstrate on LiMnAs that high-quality materials with group-I alkali metals in the crystal structure can be grown by molecular beam epitaxy. Optical measurements on the LiMnAs epilayers are consistent with the theoretical electronic structure. Our calculations also reproduce earlier reports of high antiferromagnetic ordering temperature and predict large, spin-orbit-coupling-induced magnetic anisotropy effects. We propose a strategy for employing antiferromagnetic semiconductors in high-temperature semiconductor spintronics.

  18. Near-bandgap optical properties of pseudomorphic GeSn alloys grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    D' Costa, Vijay Richard, E-mail: vdcosta@asu.edu; Wang, Wei; Yeo, Yee-Chia, E-mail: eleyeoyc@nus.edu.sg [Department of Electrical and Computer Engineering, National University of Singapore, Singapore 117583 (Singapore)

    2016-08-14

    We investigated the compositional dependence of the near-bandgap dielectric function and the E{sub 0} critical point in pseudomorphic Ge{sub 1-x}Sn{sub x} alloys grown on Ge (100) substrate by molecular beam epitaxy. The complex dielectric functions were obtained using spectroscopic ellipsometry from 0.5 to 4.5 eV at room temperature. Analogous to the E{sub 1} and E{sub 1}+Δ{sub 1} transitions, a model consisting of the compositional dependence of relaxed alloys along with the strain contribution predicted by the deformation potential theory fully accounts for the observed compositional dependence in pseudomorphic alloys.

  19. Perspective: Extremely fine tuning of doping enabled by combinatorial molecular-beam epitaxy

    Directory of Open Access Journals (Sweden)

    J. Wu

    2015-06-01

    Full Text Available Chemical doping provides an effective method to control the electric properties of complex oxides. However, the state-of-art accuracy in controlling doping is limited to about 1%. This hampers elucidation of the precise doping dependences of physical properties and phenomena of interest, such as quantum phase transitions. Using the combinatorial molecular beam epitaxy, we improve the accuracy in tuning the doping level by two orders of magnitude. We illustrate this novel method by two examples: a systematic investigation of the doping dependence of interface superconductivity, and a study of the competing ground states in the vicinity of the insulator-to-superconductor transition.

  20. Molecular mechanisms of crystal growth

    International Nuclear Information System (INIS)

    Pina, C. M.

    2000-01-01

    In this paper I present an example of the research that the Mineral Surface Group of the Munster University is conducting in the field of Crystal Growth. Atomic Force Microscopy (Am) in situ observations of different barite (BaSO4) faces growing from aqueous solutions, in combination with computer simulations of the surface attachment of growth units allows us to test crystal growth models. Our results demonstrate the strong structural control that a crystal can exert on its own growth, revealing also the limitation of the classical crystal growth theories (two dimensional nucleation and spiral growth models) in providing a complete explanation for the growth behaviour at a molecular scale. (Author) 6 refs

  1. Liquid Solution Phase Epitaxial Growth of Al-doped f-SiC for LEDs

    DEFF Research Database (Denmark)

    Tang, Kai; Ma, Xiang; van der Eijk, Casper

    light quality and longer lifespan, compared to the current yellow phosphor based white LEDs. Liquid phase epitaxy technology is able to yield a high crystalline quality in terms of structural perfection owing to the fact that it is a near equilibrium process. In addition, the technological equipment...... are presented and discussed. Since operational temperature of LPE growth is much lower than that currently used in physical vapour transport (PVT) process, it is expected to save the energy consumption for SiC crystal growth....

  2. Monitoring the beam flux in molecular beam epitaxy using laser multiphoton ionization

    International Nuclear Information System (INIS)

    Chien, R.; Sogard, M.R.

    1990-01-01

    In this paper, we will describe a method using laser nonresonant multiphoton ionization to measure beam flux in molecular beam epitaxy (MBE) systems. The results were obtained in a test chamber where a focused excimer laser beam was used to photoionize a small fraction of the atomic and molecular beams. The constituents of the beams were identified by a time-of-flight mass spectrometer. Ion signal strength was found to be directly correlated to the temperature of the atomic beam oven. Good stability and sensitivity on gallium, aluminum, and silicon atomic beams was demonstrated. Arsenic was also detected. We demonstrated very sensitive detection of contaminant atomic and molecular constituents of our system. We have also detected the presence of short-term fluctuations in the gallium flux from an effusion source. These fluctuations, previously suspected, can be in excess of ±10%

  3. Sintered tantalum carbide coatings on graphite substrates: Highly reliable protective coatings for bulk and epitaxial growth

    International Nuclear Information System (INIS)

    Nakamura, Daisuke; Suzumura, Akitoshi; Shigetoh, Keisuke

    2015-01-01

    Highly reliable low-cost protective coatings have been sought after for use in crucibles and susceptors for bulk and epitaxial film growth processes involving wide bandgap materials. Here, we propose a production technique for ultra-thick (50–200 μmt) tantalum carbide (TaC) protective coatings on graphite substrates, which consists of TaC slurry application and subsequent sintering processes, i.e., a wet ceramic process. Structural analysis of the sintered TaC layers indicated that they have a dense granular structure containing coarse grain with sizes of 10–50 μm. Furthermore, no cracks or pinholes penetrated through the layers, i.e., the TaC layers are highly reliable protective coatings. The analysis also indicated that no plastic deformation occurred during the production process, and the non-textured crystalline orientation of the TaC layers is the origin of their high reliability and durability. The TaC-coated graphite crucibles were tested in an aluminum nitride (AlN) sublimation growth process, which involves extremely corrosive conditions, and demonstrated their practical reliability and durability in the AlN growth process as a TaC-coated graphite. The application of the TaC-coated graphite materials to crucibles and susceptors for use in bulk AlN single crystal growth, bulk silicon carbide (SiC) single crystal growth, chemical vapor deposition of epitaxial SiC films, and metal-organic vapor phase epitaxy of group-III nitrides will lead to further improvements in crystal quality and reduced processing costs

  4. Sintered tantalum carbide coatings on graphite substrates: Highly reliable protective coatings for bulk and epitaxial growth

    Energy Technology Data Exchange (ETDEWEB)

    Nakamura, Daisuke; Suzumura, Akitoshi; Shigetoh, Keisuke [Toyota Central R and D Labs., Inc., Nagakute, Aichi 480-1192 (Japan)

    2015-02-23

    Highly reliable low-cost protective coatings have been sought after for use in crucibles and susceptors for bulk and epitaxial film growth processes involving wide bandgap materials. Here, we propose a production technique for ultra-thick (50–200 μmt) tantalum carbide (TaC) protective coatings on graphite substrates, which consists of TaC slurry application and subsequent sintering processes, i.e., a wet ceramic process. Structural analysis of the sintered TaC layers indicated that they have a dense granular structure containing coarse grain with sizes of 10–50 μm. Furthermore, no cracks or pinholes penetrated through the layers, i.e., the TaC layers are highly reliable protective coatings. The analysis also indicated that no plastic deformation occurred during the production process, and the non-textured crystalline orientation of the TaC layers is the origin of their high reliability and durability. The TaC-coated graphite crucibles were tested in an aluminum nitride (AlN) sublimation growth process, which involves extremely corrosive conditions, and demonstrated their practical reliability and durability in the AlN growth process as a TaC-coated graphite. The application of the TaC-coated graphite materials to crucibles and susceptors for use in bulk AlN single crystal growth, bulk silicon carbide (SiC) single crystal growth, chemical vapor deposition of epitaxial SiC films, and metal-organic vapor phase epitaxy of group-III nitrides will lead to further improvements in crystal quality and reduced processing costs.

  5. Epitaxial growth of thin single-crystals and their quality study by Rutherford scattering in channeling conditions

    International Nuclear Information System (INIS)

    Kirsch, Robert.

    1975-01-01

    Some aspects of thin crystalline layers are reminded: vacuum deposition, epitaxial growth, annealing and interdiffusion ion channeling and scattering of 1-2MeV helium ions are used to study the crystalline quality, the annealing effects and in some cases the interdiffusion in epitaxial multilayers of silver, copper gold and nickel. Thin single-crystals of gold and nickel oriented (III) plan parallel to the surface were obtained by successive epitaxial growth from muscovite mica clivages. The mounting techniques of single crystalline, self-supporting, 300 to 1200 Angstroems thick, gold and nickel targets of 3mm diameter are described. The gold single-crystals have dislocation densities of 10 8 cm -2 and the various epitaxial layers are obtained without twinning [fr

  6. Non-Epitaxial Thin-Film Indium Phosphide Photovoltaics: Growth, Devices, and Cost Analysis

    Science.gov (United States)

    Zheng, Maxwell S.

    In recent years, the photovoltaic market has grown significantly as module prices have continued to come down. Continued growth of the field requires higher efficiency modules at lower manufacturing costs. In particular, higher efficiencies reduce the area needed for a given power output, thus reducing the downstream balance of systems costs that scale with area such as mounting frames, installation, and soft costs. Cells and modules made from III-V materials have the highest demonstrated efficiencies to date but are not yet at the cost level of other thin film technologies, which has limited their large-scale deployment. There is a need for new materials growth, processing and fabrication techniques to address this major shortcoming of III-V semiconductors. Chapters 2 and 3 explore growth of InP on non-epitaxial Mo substrates by MOCVD and CSS, respectively. The results from these studies demonstrate that InP optoelectronic quality is maintained even by growth on non-epitaxial metal substrates. Structural characterization by SEM and XRD show stoichiometric InP can be grown in complete thin films on Mo. Photoluminescence measurements show peak energies and widths to be similar to those of reference wafers of similar doping concentrations. In chapter 4 the TF-VLS growth technique is introduced and cells fabricated from InP produced by this technique are characterized. The TF-VLS method results in lateral grain sizes of >500 mum and exhibits superior optoelectronic quality. First generation devices using a n-TiO2 window layer along with p-type TF-VLS grown InP have reached ˜12.1% power conversion efficiency under 1 sun illumination with VOC of 692 mV, JSC of 26.9 mA/cm2, and FF of 65%. The cells are fabricated using all non-epitaxial processing. Optical measurements show the InP in these cells have the potential to support a higher VOC of ˜795 mV, which can be achieved by improved device design. Chapter 5 describes a cost analysis of a manufacturing process using an

  7. Epitaxial Growth of Permalloy Thin Films on MgO Single-Crystal Substrates

    International Nuclear Information System (INIS)

    Ohtake, Mitsuru; Tanaka, Takahiro; Matsubara, Katsuki; Futamoto, Masaaki; Kirino, Fumiyoshi

    2011-01-01

    Permalloy (Py: Ni - 20 at. % Fe) thin films were prepared on MgO single-crystal substrates of (100), (110), and (111) orientations by molecular beam epitaxy. Py crystals consisting of fcc(100) and hcp(112-bar 0) orientations epitaxially nucleate on MgO(100) substrates. With increasing the substrate temperature, the volume ratio of fcc(100) to hcp(112-bar 0) crystal increases. The metastable hcp(112-bar 0) structure transforms into more stable fcc(110) structure with increasing the film thickness. Py(110) fcc single-crystal films are obtained on MgO(110) substrates, whereas Py films epitaxially grow on MgO(111) substrates with two types of fcc(111) variants whose orientations are rotated around the film normal by 180 deg. each other. X-ray diffraction analysis indicates that the out-of-plane and the in-plane lattice spacings of these fcc-Py films agree within ±0.4% with the values of bulk fcc-Py crystal, suggesting that the strains in the films are very small. High-resolution transmission electron microscopy shows that periodical misfit dislocations are preferentially introduced in the films around the Py/MgO(100) and the Py/MgO(110) interfaces to reduce the lattice mismatches. The magnetic properties are considered to be reflecting the magnetocrystalline anisotropies of bulk fcc-Py and/or metastable hcp-Py crystals and the shape anisotropy caused by the surface undulations.

  8. Epitaxial Growth of Permalloy Thin Films on MgO Single-Crystal Substrates

    Energy Technology Data Exchange (ETDEWEB)

    Ohtake, Mitsuru; Tanaka, Takahiro; Matsubara, Katsuki; Futamoto, Masaaki [Faculty of Science and Engineering, Chuo University, 1-13-27 Kasuga, Bunkyo-ku, Tokyo 112-8551 (Japan); Kirino, Fumiyoshi, E-mail: ohtake@futamoto.elect.chuo-u.ac.jp [Graduate School of Fine Arts, Tokyo National University of Fine Arts and Music, 12-8 Ueno-koen, Taito-ku, Tokyo 110-8714 (Japan)

    2011-07-06

    Permalloy (Py: Ni - 20 at. % Fe) thin films were prepared on MgO single-crystal substrates of (100), (110), and (111) orientations by molecular beam epitaxy. Py crystals consisting of fcc(100) and hcp(112-bar 0) orientations epitaxially nucleate on MgO(100) substrates. With increasing the substrate temperature, the volume ratio of fcc(100) to hcp(112-bar 0) crystal increases. The metastable hcp(112-bar 0) structure transforms into more stable fcc(110) structure with increasing the film thickness. Py(110){sub fcc} single-crystal films are obtained on MgO(110) substrates, whereas Py films epitaxially grow on MgO(111) substrates with two types of fcc(111) variants whose orientations are rotated around the film normal by 180 deg. each other. X-ray diffraction analysis indicates that the out-of-plane and the in-plane lattice spacings of these fcc-Py films agree within {+-}0.4% with the values of bulk fcc-Py crystal, suggesting that the strains in the films are very small. High-resolution transmission electron microscopy shows that periodical misfit dislocations are preferentially introduced in the films around the Py/MgO(100) and the Py/MgO(110) interfaces to reduce the lattice mismatches. The magnetic properties are considered to be reflecting the magnetocrystalline anisotropies of bulk fcc-Py and/or metastable hcp-Py crystals and the shape anisotropy caused by the surface undulations.

  9. Vertical transport in isotype InAlN/GaN dipole induced diodes grown by molecular beam epitaxy

    Science.gov (United States)

    Fireman, M. N.; Li, Haoran; Keller, Stacia; Mishra, Umesh K.; Speck, James S.

    2017-05-01

    InAlN dipole diodes were developed and fabricated on both (0001) Ga-Face and (" separators="| 000 1 ¯) N-face oriented GaN on sapphire templates by molecular beam epitaxy. The orientation and direction of the InAlN polarization dipole are functions of the substrate orientation and composition, respectively. Special consideration was taken to minimize growth differences and impurity uptake during growth on these orientations of opposite polarity. Comparison of devices on similarly grown structures with In compositions in excess of 50% reveals that dipole diodes shows poorer forward bias performance and exhibited an increase in reverse bias leakage, regardless of orientation. Similarly, (0001) Ga-face oriented InAlN at a lowered 40% In composition had poor device characteristics, namely, the absence of expected exponential turn on in forward bias. By contrast, at In compositions close to 40%, (" separators="| 000 1 ¯) N-face oriented InAlN devices had excellent performance, with over five orders of magnitude of rectification and extracted barrier heights of 0.53- 0.62 eV; these values are in close agreement with simulation. Extracted ideality factors ranging from 1.08 to 1.38 on these devices are further evidence of their optimal performance. Further discussion focuses on the growth and orientation conditions that may lead to this discrepancy yet emphasizes that with proper design and growth strategy, the rectifying dipole diodes can be achieved with InAlN nitride dipole layers.

  10. Manipulation of morphology and structure of the top of GaAs nanowires grown by molecular-beam epitaxy

    Science.gov (United States)

    Li, Lixia; Pan, Dong; Yu, Xuezhe; So, Hyok; Zhao, Jianhua

    2017-10-01

    Self-catalyzed GaAs nanowires (NWs) are grown on Si (111) substrates by molecular-beam epitaxy. The effect of different closing sequences of the Ga and As cell shutters on the morphology and structural phase of GaAs NWs is investigated. For the sequences of closing the Ga and As cell shutters simultaneously or closing the As cell shutter 1 min after closing the Ga cell shutter, the NWs grow vertically to the substrate surface. In contrast, when the As cell shutter is closed first, maintaining the Ga flux is found to be critical for the following growth of GaAs NWs, which can change the growth direction from [111] to . The evolution of the morphology and structural phase transition at the tips of these GaAs NWs confirm that the triple-phase-line shift mode is at work even for the growth with different cell shutter closing sequences. Our work will provide new insights for better understanding of the growth mechanism and realizing of the morphology and structure control of the GaAs NWs. Project supported partly by the MOST of China (No. 2015CB921503), the National Natural Science Foundation of China (Nos. 61504133, 61334006, 61404127), and Youth Innovation Promotion Association, CAS (No. 2017156).

  11. X-ray diffraction study of InAlAs-InGaAs on InP high electron mobility transistor structure prepared by molecular-beam epitaxy

    International Nuclear Information System (INIS)

    Liu, H.Y.; Kao, Y.C.; Kim, T.S.

    1990-01-01

    High-electron mobility transistors (HEMTs) can be prepared by growing alternating epitaxial layers of InAlAs and InGaAs on InP substrates. Lattice matched HEMTs are obtained by growing layers of IN x Al (1-x) As and In y Ga (1-y) As with x ≅ 0.5227 and y ≅ 0.5324. Varying the values of x and y by controlling the individual flux during molecular-beam epitaxial (MBE) growth, one can obtain pseudomorphic HEMTs. Pseudomorphic HEMTs may have superior electronic transport properties and larger conduction band discontinuity when compared to an unstrained one. The precise control of the composition is thus important to the properties of HEMTs. This control is however very difficult and the values of x and y may vary from run to run. The authors demonstrate in this paper the capability of a double crystal rocking curve (DCRC) on the structure characterization

  12. Effects of substrate material on carbon films grown by laser molecular beam epitaxy

    International Nuclear Information System (INIS)

    Liu, M.; Xu, X.Y.; Man, B.Y.; Kong, D.M.; Xu, S.C.

    2012-01-01

    Highlights: ► We prepared tri-layers by laser molecular beam epitaxy (LMBE) on sapphire substrate. ► We found that the formation of the graphene film has a strong relation to the structure and properties of the substrate. ► The different carbon film formation mechanism of the buffer layers can affect the morphology of the film. - Abstract: The carbon thin films were grown on different substrates with different buffer layers by laser molecular beam epitaxy (LMBE) with a high purity graphite carbon target. A UV pulsed KrF excimer laser with a wavelength of 248 nm was used as laser source. The structure, surface morphology and other properties of the carbon thin films were characterized by Raman spectroscopy, transmission electron microscopy (TEM), selected area electron diffraction (SAED) and atomic force microscopy (AFM). The results show that the properties of the carbon thin films and the formation of the graphene film have a strong relation to the structure and properties of the substrate. The substrate with a hexagonal wurtzite structure which is similar to the hexagonal honeycomb structure of the carbon atoms arranged in the graphene is more beneficial for the formation of the graphene thin film. In our experiment conditions, the carbon films grown on sapphire substrates with different buffer layers have an ordered structure and a smooth surface, and form high quality tri-layer graphene films.

  13. Combinatorial screening of halide perovskite thin films and solar cells by mask-defined IR laser molecular beam epitaxy

    OpenAIRE

    Kawashima, Kazuhiro; Okamoto, Yuji; Annayev, Orazmuhammet; Toyokura, Nobuo; Takahashi, Ryota; Lippmaa, Mikk; Itaka, Kenji; Suzuki, Yoshikazu; Matsuki, Nobuyuki; Koinuma, Hideomi

    2017-01-01

    Abstract As an extension of combinatorial molecular layer epitaxy via ablation of perovskite oxides by a pulsed excimer laser, we have developed a laser molecular beam epitaxy (MBE) system for parallel integration of nano-scaled thin films of organic?inorganic hybrid materials. A pulsed infrared (IR) semiconductor laser was adopted for thermal evaporation of organic halide (A-site: CH3NH3I) and inorganic halide (B-site: PbI2) powder targets to deposit repeated A/B bilayer films where the thic...

  14. Small fluctuations in epitaxial growth via conservative noise

    International Nuclear Information System (INIS)

    Patrone, Paul N; Wang Rongrong; Margetis, Dionisios

    2011-01-01

    We study the combined effect of growth (material deposition from above) and nearest-neighbor entropic and force-dipole interactions in a stochastically perturbed system of N line defects (steps) on a vicinal crystal surface in 1+1 dimensions. First, we formulate a general model of conservative white noise and derive simplified formulas for the terrace width distribution and terrace width correlations in the limit N → ∞ for small step fluctuations. Our general result expresses terrace width correlations as an interplay of noise covariance and step interaction strength. Second, we apply our formalism to two specific noise models which stem, respectively, from (i) the fluctuation-dissipation theorem for diffusion of adsorbed atoms; and (ii) the phenomenological consideration of deposition-flux-induced asymmetric attachment and detachment of atoms at step edges. In both cases of noise, we find that terrace width correlations decay exponentially with the step number difference; this behavior leads to vanishing correlations in the macroscopic limit. Our analysis may be used to (i) determine the noise in quasi-one-dimensional surfaces and (ii) assess the validity of previous mean field approximations.

  15. Epitaxial growth of GaSb on V-grooved Si (001) substrates with an ultrathin GaAs stress relaxing layer

    Science.gov (United States)

    Li, Qiang; Lai, Billy; Lau, Kei May

    2017-10-01

    We report epitaxial growth of GaSb nano-ridge structures and planar thin films on V-groove patterned Si (001) substrates by leveraging the aspect ratio trapping technique. GaSb was deposited on {111} Si facets of the V-shaped trenches using metal-organic chemical vapor deposition with a 7 nm GaAs growth initiation layer. Transmission electron microscopy analysis reveals the critical role of the GaAs layer in providing a U-shaped surface for subsequent GaSb epitaxy. A network of misfit dislocations was uncovered at the GaSb/GaAs hetero-interface. We studied the evolution of the lattice relaxation as the growth progresses from closely pitched GaSb ridges to coalesced thin films using x-ray diffraction. The omega rocking curve full-width-at-half-maximum of the resultant GaSb thin film is among the lowest values reported by molecular beam epitaxy, substantiating the effectiveness of the defect necking mechanism. These results thus present promising opportunities for the heterogeneous integration of devices based on 6.1 Å family compound semiconductors.

  16. Quantum wire spectroscopy and epitaxial growth velocities in InGaAs-InP heterostructures

    International Nuclear Information System (INIS)

    Worlock, J.M.; Peeters, F.M.; Cox, H.M.; Morais, P.C.

    1990-06-01

    We study excitons bound to quantum wires of InGaAs embedded in an InP matrix, where the wires vary from 2.93A angstrom to a.1172A angstrom (one to four monolayers) thick and from 25A angstrom to 250A angstrom wide. We combine spectroscopic data from measurements of photoluminescence with variational calculations of the binding energies of excitons to the wires to deduce the wire widths and thickness. The widths are then related to the growth times to deduce lateral growth velocities in the vapor levitation epitaxial technique. Monolayer growth rates, at ∼ 80A angstrom/sec, are significantly faster than growth rates for the multilayer wires. (author)

  17. Growth and characterization of AlGaN/GaN/AlGaN double-heterojunction high-electron-mobility transistors on 100-mm Si(111) using ammonia-molecular beam epitaxy

    International Nuclear Information System (INIS)

    Ravikiran, L.; Radhakrishnan, K.; Yiding, Lin; Ng, G. I.; Dharmarasu, N.; Agrawal, M.; Arulkumaran, S.; Vicknesh, S.

    2015-01-01

    To improve the confinement of two-dimensional electron gas (2DEG) in AlGaN/GaN high electron mobility transistor (HEMT) heterostructures, AlGaN/GaN/AlGaN double heterojunction HEMT (DH-HEMT) heterostructures were grown using ammonia-MBE on 100-mm Si substrate. Prior to the growth, single heterojunction HEMT (SH-HEMT) and DH-HEMT heterostructures were simulated using Poisson-Schrödinger equations. From simulations, an AlGaN buffer with “Al” mole fraction of 10% in the DH-HEMT was identified to result in both higher 2DEG concentration (∼10 13  cm −2 ) and improved 2DEG confinement in the channel. Hence, this composition was considered for the growth of the buffer in the DH-HEMT heterostructure. Hall measurements showed a room temperature 2DEG mobility of 1510 cm 2 /V.s and a sheet carrier concentration (n s ) of 0.97 × 10 13  cm −2 for the DH-HEMT structure, while they are 1310 cm 2 /V.s and 1.09 × 10 13  cm −2 , respectively, for the SH-HEMT. Capacitance-voltage measurements confirmed the improvement in the confinement of 2DEG in the DH-HEMT heterostructure, which helped in the enhancement of its room temperature mobility. DH-HEMT showed 3 times higher buffer break-down voltage compared to SH-HEMT, while both devices showed almost similar drain current density. Small signal RF measurements on the DH-HEMT showed a unity current-gain cut-off frequency (f T ) and maximum oscillation frequency (f max ) of 22 and 25 GHz, respectively. Thus, overall, DH-HEMT heterostructure was found to be advantageous due to its higher buffer break-down voltages compared to SH-HEMT heterostructure

  18. Hydrogen assisted growth of high quality epitaxial graphene on the C-face of 4H-SiC

    Energy Technology Data Exchange (ETDEWEB)

    Cai, Tuocheng; Jia, Zhenzhao; Yan, Baoming; Yu, Dapeng; Wu, Xiaosong, E-mail: xswu@pku.edu.cn [State Key Laboratory for Artificial Microstructure and Mesoscopic Physics, Peking University, Beijing 100871 (China); Collaborative Innovation Center of Quantum Matter, Beijing 100871 (China)

    2015-01-05

    We demonstrate hydrogen assisted growth of high quality epitaxial graphene on the C-face of 4H-SiC. Compared with the conventional thermal decomposition technique, the size of the growth domain by this method is substantially increased and the thickness variation is reduced. Based on the morphology of epitaxial graphene, the role of hydrogen is revealed. It is found that hydrogen acts as a carbon etchant. It suppresses the defect formation and nucleation of graphene. It also improves the kinetics of carbon atoms via hydrocarbon species. These effects lead to increase of the domain size and the structure quality. The consequent capping effect results in smooth surface morphology and suppression of multilayer growth. Our method provides a viable route to fine tune the growth kinetics of epitaxial graphene on SiC.

  19. Molecular beam epitaxy of InN layers on Sapphire, GaN and indium tin oxide

    Energy Technology Data Exchange (ETDEWEB)

    Denker, Christian; Landgraf, Boris; Schuhmann, Henning; Malindretos, Joerg; Seibt, Michael; Rizzi, Angela [IV. Physikalisches Institut, Georg-August-Universitaet Goettingen (Germany); Segura-Ruiz, Jaime; Gomez-Gomez, Maribel; Cantarero, Andres [Materials Science Institute, University of Valencia, Paterna (Spain)

    2009-07-01

    Among the group-III nitrides semiconductors, InN is the one with the narrowest gap (0.67 eV), lowest effective electron mass and highest peak drift velocity. It is therefore a very interesting material for several applications, in particular semiconductor solar cells. Furthermore, the high electron affinity makes it suitable also as electrode material for organic solar cells. InN layers were grown by molecular beam epitaxy on MOCVD GaN templates, on bare c-plane sapphire and on polycrystalline indium tin oxide. On all substrates the III-V ratio as well as the substrate temperature was varied. A RHEED analysis of InN growth on GaN showed a relatively sharp transition from N-rich and columnar growth to In-rich growth with droplet formation by increasing the In flux impinging on the surface. The InN layers on single crystalline substrates were characterized by SEM, AFM, XRD, PL and Raman. The InN layers on ITO were mainly analyzed with respect to the surface morphology with SEM. HRTEM in cross section gives insight into the structure of the interface to the ITO substrate.

  20. Low temperature step-graded InAlAs/GaAs metamorphic buffer layers grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Shang, X Z; Wu, S D; Liu, C; Wang, W X; Guo, L W; Huang, Q; Zhou, J M

    2006-01-01

    Low-temperature step-graded InAlAs metamorphic buffer layers on GaAs substrate grown by molecular beam epitaxy were investigated. The strain relaxation and the composition of the top InAlAs layer were determined by high-resolution triple-axis x-ray diffraction measurements, which show that the top InAlAs layer is nearly fully relaxed. Surface morphology was observed by reflection high-energy electron diffraction pattern and atomic force microscopy. Under a selected range of growth parameters, the root mean square surface roughness of the sample grown at 380 deg. C is 0.802 nm, which has the smallest value compared with those of other samples. Furthermore, The ω-2θ and ω scans of the triple-axis x-ray diffraction, and photoluminescence show the sample grown at 380 deg. C has better crystalline quality. With decreasing As overpressure at this growth temperature, crystalline quality became poor and could not maintain two dimensional growth with increasing overpressure. The carrier concentrations and Hall mobilities of the InAlAs/ InGaAs/GaAs MM-HEMT structure on low-temperature step-graded InAlAs metamorphic buffer layers grown in optimized conditions are high enough to make devices

  1. Growth and characterization of AlGaN/GaN/AlGaN double-heterojunction high-electron-mobility transistors on 100-mm Si(111) using ammonia-molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Ravikiran, L.; Radhakrishnan, K., E-mail: ERADHA@ntu.edu.sg; Yiding, Lin; Ng, G. I. [NOVITAS-Nanoelectronics Centre of Excellence, School of Electrical and Electronic Engineering, Nanyang Technological University, Singapore 639798 (Singapore); Dharmarasu, N.; Agrawal, M.; Arulkumaran, S.; Vicknesh, S. [Temasek Laboratories@NTU, Nanyang Technological University, Singapore 637553 (Singapore)

    2015-01-14

    To improve the confinement of two-dimensional electron gas (2DEG) in AlGaN/GaN high electron mobility transistor (HEMT) heterostructures, AlGaN/GaN/AlGaN double heterojunction HEMT (DH-HEMT) heterostructures were grown using ammonia-MBE on 100-mm Si substrate. Prior to the growth, single heterojunction HEMT (SH-HEMT) and DH-HEMT heterostructures were simulated using Poisson-Schrödinger equations. From simulations, an AlGaN buffer with “Al” mole fraction of 10% in the DH-HEMT was identified to result in both higher 2DEG concentration (∼10{sup 13 }cm{sup −2}) and improved 2DEG confinement in the channel. Hence, this composition was considered for the growth of the buffer in the DH-HEMT heterostructure. Hall measurements showed a room temperature 2DEG mobility of 1510 cm{sup 2}/V.s and a sheet carrier concentration (n{sub s}) of 0.97 × 10{sup 13 }cm{sup −2} for the DH-HEMT structure, while they are 1310 cm{sup 2}/V.s and 1.09 × 10{sup 13 }cm{sup −2}, respectively, for the SH-HEMT. Capacitance-voltage measurements confirmed the improvement in the confinement of 2DEG in the DH-HEMT heterostructure, which helped in the enhancement of its room temperature mobility. DH-HEMT showed 3 times higher buffer break-down voltage compared to SH-HEMT, while both devices showed almost similar drain current density. Small signal RF measurements on the DH-HEMT showed a unity current-gain cut-off frequency (f{sub T}) and maximum oscillation frequency (f{sub max}) of 22 and 25 GHz, respectively. Thus, overall, DH-HEMT heterostructure was found to be advantageous due to its higher buffer break-down voltages compared to SH-HEMT heterostructure.

  2. Contribution of numerical simulation to silicon carbide bulk growth and epitaxy

    International Nuclear Information System (INIS)

    Meziere, Jerome; Pons, Michel; Cioccio, Lea Di; Blanquet, Elisabeth; Ferret, Pierre; Dedulle, Jean-Marc; Baillet, Francis; Pernot, Etienne; Anikin, Michail; Madar, Roland; Billon, Thierry

    2004-01-01

    High temperature epitaxial processes for SiC bulk and thin films by physical vapour transport and chemical vapour deposition are reviewed from an academic point of view using heat and mass transfer modelling and simulation. The objective is to show that this modelling approach could provide information on fabrication and characterization for the improvement of the knowledge of the growth history. Recent results of our integrated research programme on SiC, taking into account the fabrication, process modelling and characterization, will be presented

  3. Epitaxial growth of textured YBa2Cu3O7-δ films on silver

    International Nuclear Information System (INIS)

    Liu Dan-Min; Liu Wei-Peng; Suo Hong-Li; Zhou Mei-Ling

    2005-01-01

    YBa 2 Cu 3 O 7-δ (YBCO) films were deposited on (100), (110) and (111) oriented silver single crystals and {100} left angle 100 right angle, {110} left angle 211 right angle, {110} left angle 100 right angle +{110} left angle 011 right angle {110} left angle 011 right angle and {012} left angle 100 right angle textured Ag substrates using pulsed laser deposition. The relationship between the epitaxial growth YBCO film and silver substrate has been determined. It is shown that among polycrystalline Ag substrates, {110} left angle 011 right angle textured tape is suitable for the deposition of YBCO thin films having strong texture. (orig.)

  4. Epitaxial growth of quantum rods with high aspect ratio and compositional contrast

    International Nuclear Information System (INIS)

    Li, L. H.; Patriarche, G.; Fiore, A.

    2008-01-01

    The epitaxial growth of quantum rods (QRs) on GaAs was investigated. It was found that GaAs thickness in the GaAs/InAs superlattice used for QR formation plays a key role in improving the QR structural properties. Increasing the GaAs thickness results in both an increased In compositional contrast between the QRs and surrounding layer, and an increased QR length. QRs with an aspect ratio of up to 10 were obtained, representing quasiquantum wires in a GaAs matrix. Due to modified confinement and strain potential, such nanostructure is promising for controlling gain polarization

  5. Modelling of epitaxial film growth with an Ehrlich-Schwoebel barrier dependent on the step height

    International Nuclear Information System (INIS)

    Leal, F F; Ferreira, S C; Ferreira, S O

    2011-01-01

    The formation of mounded surfaces in epitaxial growth is attributed to the presence of barriers against interlayer diffusion in the terrace edges, known as Ehrlich-Schwoebel (ES) barriers. We investigate a model for epitaxial growth using an ES barrier explicitly dependent on the step height. Our model has an intrinsic topological step barrier even in the absence of an explicit ES barrier. We show that mounded morphologies can be obtained even for a small barrier while a self-affine growth, consistent with the Villain-Lai-Das Sarma equation, is observed in the absence of an explicit step barrier. The mounded surfaces are described by a super-roughness dynamical scaling characterized by locally smooth (facetted) surfaces and a global roughness exponent α > 1. The thin film limit is featured by surfaces with self-assembled three-dimensional structures having an aspect ratio (height/width) that may increase or decrease with temperature depending on the strength of the step barrier. (fast track communication)

  6. High efficiency green/yellow and red InGaN/AlGaN nanowire light-emitting diodes grown by molecular beam epitaxy

    Directory of Open Access Journals (Sweden)

    M.R. Philip

    2017-06-01

    Full Text Available We report on the achievement of high efficiency green, yellow, and red InGaN/AlGaN dot-in-a-wire nanowire light-emitting diodes grown on Si(111 by molecular beam epitaxy. The peak emission wavelengths were altered by varying the growth conditions, including the substrate temperature, and In/Ga flux ratio. The devices demonstrate relatively high (>40% internal quantum efficiency at room temperature, relative to that measured at 5 K. Moreover, negligible blue-shift in peak emission spectrum associated with no efficiency droop was measured when injection current was driven up to 556 A/cm2.

  7. Hydride vapor phase epitaxy growth of GaN, InGaN, ScN, and ScAIN

    NARCIS (Netherlands)

    Bohnen, T.

    2010-01-01

    Chemical vapor deposition (CVD); hydride vapor phase epitaxy (HVPE); gallium nitride (GaN); indium gallium nitride (InGaN); scandium nitride (ScN); scandium aluminum nitride (ScAlN); semiconductors; thin films; nanowires; III nitrides; crystal growth - We studied the HVPE growth of different III

  8. Epitaxial growth of bcc-FexCo100-x thin films on MgO(1 1 0) single-crystal substrates

    International Nuclear Information System (INIS)

    Ohtake, Mitsuru; Nishiyama, Tsutomu; Shikada, Kouhei; Kirino, Fumiyoshi; Futamoto, Masaaki

    2010-01-01

    Fe x Co 100-x (x=100, 65, 50 at%) epitaxial thin films were prepared on MgO(1 1 0) single-crystal substrates heated at 300 deg. C by ultra-high vacuum molecular beam epitaxy. The film structure and the growth mechanism are discussed. FeCo(2 1 1) films with bcc structure grow epitaxially on MgO(1 1 0) substrates with two types of variants whose orientations are rotated around the film normal by 180 deg. each other for all compositions. Fe x Co 100-x film growth follows the Volmer Weber mode. X-ray diffraction analysis indicates the out-of-plane and the in-plane lattice spacings are in agreement with the values of respective bulk Fe x Co 100-x crystals with very small errors less than ±0.4%, suggesting the strains in the films are very small. High-resolution cross-sectional transmission electron microscopy shows that periodical misfit dislocations are preferentially introduced in the film at the Fe 50 Co 50 /MgO interface along the MgO[1 1-bar 0] direction. The presence of such periodical dislocations decreases the large lattice mismatch of about -17% existing at the FeCo/MgO interface along the MgO[1 1-bar 0] direction.

  9. Epitaxial growth of bcc-Fe{sub x}Co{sub 100-x} thin films on MgO(1 1 0) single-crystal substrates

    Energy Technology Data Exchange (ETDEWEB)

    Ohtake, Mitsuru, E-mail: ohtake@futamoto.elect.chuo-u.ac.j [Faculty of Science and Engineering, Chuo University, 1-13-27 Kasuga, Bunkyo-ku, Tokyo 112-8551 (Japan); Nishiyama, Tsutomu; Shikada, Kouhei [Faculty of Science and Engineering, Chuo University, 1-13-27 Kasuga, Bunkyo-ku, Tokyo 112-8551 (Japan); Kirino, Fumiyoshi [Graduate School of Fine Arts, Tokyo National University of Fine Arts and Music, 12-8 Ueno-koen, Taito-ku, Tokyo 110-8714 (Japan); Futamoto, Masaaki [Faculty of Science and Engineering, Chuo University, 1-13-27 Kasuga, Bunkyo-ku, Tokyo 112-8551 (Japan)

    2010-07-15

    Fe{sub x}Co{sub 100-x} (x=100, 65, 50 at%) epitaxial thin films were prepared on MgO(1 1 0) single-crystal substrates heated at 300 deg. C by ultra-high vacuum molecular beam epitaxy. The film structure and the growth mechanism are discussed. FeCo(2 1 1) films with bcc structure grow epitaxially on MgO(1 1 0) substrates with two types of variants whose orientations are rotated around the film normal by 180 deg. each other for all compositions. Fe{sub x}Co{sub 100-x} film growth follows the Volmer Weber mode. X-ray diffraction analysis indicates the out-of-plane and the in-plane lattice spacings are in agreement with the values of respective bulk Fe{sub x}Co{sub 100-x} crystals with very small errors less than +-0.4%, suggesting the strains in the films are very small. High-resolution cross-sectional transmission electron microscopy shows that periodical misfit dislocations are preferentially introduced in the film at the Fe{sub 50}Co{sub 50}/MgO interface along the MgO[1 1-bar 0] direction. The presence of such periodical dislocations decreases the large lattice mismatch of about -17% existing at the FeCo/MgO interface along the MgO[1 1-bar 0] direction.

  10. Molecular Beam Epitaxy on Gas Cluster Ion Beam Prepared GaSb Substrates: Towards Improved Surfaces and Interfaces

    National Research Council Canada - National Science Library

    Krishnaswami, Kannan; Vangala, Shivashankar R; Dauplaise, Helen M; Allen, Lisa P; Dallas, Gordon; Bakken, Daniel; Bliss, David F; Goodhue, WIlliam D

    2007-01-01

    ... at temperatures ranging 530 degrees C to 560 degrees C. Cross-sectional transmission electron microscopy of molecular beam epitaxy grown GaSb/AlGaSb layers showed that the HBr-GCIB surface produced a smooth dislocation-free substrate-to-epi transition...

  11. Selective epitaxial growth of Ge1-xSnx on Si by using metal-organic chemical vapor deposition

    Science.gov (United States)

    Washizu, Tomoya; Ike, Shinichi; Inuzuka, Yuki; Takeuchi, Wakana; Nakatsuka, Osamu; Zaima, Shigeaki

    2017-06-01

    Selective epitaxial growth of Ge and Ge1-xSnx layers on Si substrates was performed by using metal-organic chemical vapor deposition (MOCVD) with precursors of tertiary-butyl-germane (t-BGe) and tri-butyl-vinyl-tin (TBVSn). We investigated the effects of growth temperature and total pressure during growth on the selectivity and the crystallinity of the Ge and Ge1-xSnx epitaxial layers. Under low total pressure growth conditions, the dominant mechanism of the selective growth of Ge epitaxial layers is the desorption of the Ge precursors. At a high total pressure case, it is needed to control the surface migration of precursors to realize the selectivity because the desorption of Ge precursors was suppressed. The selectivity of Ge growth was improved by diffusion of the Ge precursors on the SiO2 surfaces when patterned substrates were used at a high total pressure. The selective epitaxial growth of Ge1-xSnx layer was also realized using MOCVD. We found that the Sn precursors less likely to desorb from the SiO2 surfaces than the Ge precursors.

  12. Improving surface smoothness and photoluminescence of CdTe(1 1 1)A on Si(1 1 1) substrates grown by molecular beam epitaxy using Mn atoms

    International Nuclear Information System (INIS)

    Wang, Jyh-Shyang; Tsai, Yu-Hsuan; Chen, Chang-Wei; Dai, Zi-Yuan; Tong, Shih-Chang; Yang, Chu-Shou; Wu, Chih-Hung; Yuan, Chi-Tsu; Shen, Ji-Lin

    2014-01-01

    Highlights: • CdTe(1 1 1)A epilayers were grown on Si(1 1 1) substrates by molecular beam epitaxy. • We report an enhanced growth using Mn atoms. • The significant improvements in surface quality and optical properties were found. - Abstract: This work demonstrates an improvement of the molecular beam epitaxial growth of CdTe(1 1 1)A epilayer on Si(1 1 1) substrates using Mn atoms. The reflection high-energy electron diffraction patterns show that the involvement of some Mn atoms in the growth of CdTe(1 1 1)A is even more effective than the use of a buffer layer with a smooth surface for forming good CdTe(1 1 1)A epilayers. 10 K Photoluminescence spectra show that the incorporation of only 2% Mn significantly reduced the intensity of defect-related emissions and considerably increased the integral intensity of exciton-related emissions by a large factor of about 400

  13. Epitaxial growth of AlN on single crystal Mo substrates

    International Nuclear Information System (INIS)

    Okamoto, Koichiro; Inoue, Shigeru; Nakano, Takayuki; Kim, Tae-Won; Oshima, Masaharu; Fujioka, Hiroshi

    2008-01-01

    We have grown AlN films on single-crystalline Mo(110), (100), and (111) substrates using a low temperature pulsed laser deposition (PLD) growth technique and investigated their structural properties. Although c-axis oriented AlN films grow on Mo(100), the films contain 30 o rotated domains due to the difference in the rotational symmetry between AlN(0001) and Mo(100). AlN films with only poor crystalline quality grow on Mo(111) substrates, probably due to the poor surface morphology and high reactivity of the substrates. On the other hand, single crystal AlN films grow epitaxially on Mo(110) substrates with an in-plane relationship of AlN[11-20] // Mo[001]. Reflection high-energy electron diffraction or electron backscattered diffraction analysis has revealed that neither in-plane 30 deg. rotated domains nor cubic phase domains exist in the AlN films. X-ray reflectivity measurements have revealed that the heterointerface between AlN and Mo prepared by PLD at 450 deg. C is quite abrupt. These results indicate that PLD epitaxial growth of AlN on single crystal Mo substrates is quite promising for the fabrication of future high frequency filter devices

  14. Epitaxial growth of AlN on single crystal Mo substrates

    Energy Technology Data Exchange (ETDEWEB)

    Okamoto, Koichiro; Inoue, Shigeru [Institute of Industrial Science, University of Tokyo, 4-6-1 Komaba, Meguro-ku, Tokyo, 153-8505 (Japan); Nakano, Takayuki; Kim, Tae-Won [Kanagawa Academy of Science and Technology (KAST) KSP east 301, 3-2-1 Sakado, Takatsu-ku, Kawasaki, Kanagawa, 213-0012 (Japan); Oshima, Masaharu [Department of Applied Chemistry, University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo, 113-8656 (Japan); Fujioka, Hiroshi [Institute of Industrial Science, University of Tokyo, 4-6-1 Komaba, Meguro-ku, Tokyo, 153-8505 (Japan); Kanagawa Academy of Science and Technology (KAST) KSP east 301, 3-2-1 Sakado, Takatsu-ku, Kawasaki, Kanagawa, 213-0012 (Japan)], E-mail: hfujioka@iis.u-tokyo.ac.jp

    2008-06-02

    We have grown AlN films on single-crystalline Mo(110), (100), and (111) substrates using a low temperature pulsed laser deposition (PLD) growth technique and investigated their structural properties. Although c-axis oriented AlN films grow on Mo(100), the films contain 30{sup o} rotated domains due to the difference in the rotational symmetry between AlN(0001) and Mo(100). AlN films with only poor crystalline quality grow on Mo(111) substrates, probably due to the poor surface morphology and high reactivity of the substrates. On the other hand, single crystal AlN films grow epitaxially on Mo(110) substrates with an in-plane relationship of AlN[11-20] // Mo[001]. Reflection high-energy electron diffraction or electron backscattered diffraction analysis has revealed that neither in-plane 30 deg. rotated domains nor cubic phase domains exist in the AlN films. X-ray reflectivity measurements have revealed that the heterointerface between AlN and Mo prepared by PLD at 450 deg. C is quite abrupt. These results indicate that PLD epitaxial growth of AlN on single crystal Mo substrates is quite promising for the fabrication of future high frequency filter devices.

  15. SiC epitaxial layer growth in a novel multi-wafer VPE reactor

    Energy Technology Data Exchange (ETDEWEB)

    Burk, A.A. Jr.; O`Loughlin, M.J. [Northrop Grumman Advanced Technology Lab., Baltimore, MD (United States); Mani, S.S. [Northrop Grumman Science and Technology Center, Pittsburgh, PA (United States)

    1998-06-01

    Preliminary results are presented for SiC epitaxial layer growth employing a unique planetary SiC-VPE reactor. The high-throughput, multi-wafer (7 x 2-inch) reactor, was designed for atmospheric and reduced pressure operation at temperatures up to and exceeding 1600 C. Specular epitaxial layers have been grown in the reactor at growth rates from 3-5 {mu}m/hr. The thickest layer grown to data was 42 {mu}m. The layers exhibit minimum unintentional n-type doping of {proportional_to}1 x 10{sup 15} cm{sup -3}, room temperature mobilities of {proportional_to}1000 cm{sup 2}/Vs, and intentional n-type doping from {proportional_to}5 x 10{sup 15} cm{sup -3} to >1 x 10{sup 19} cm{sup -3}. Intrawafer thickness and doping uniformities of 4% and 7% (standard deviation/mean) have been obtained, respectively, on 35 mm diameter substrates. Recently, 3% thickness uniformity has been demonstrated on a 50 mm substrate. Within a run, wafer-to-wafer thickness deviation is {proportional_to}4-14%. Doping variation is currently larger, ranging as much as a factor of two from the highest to the lowest doped wafer. Continuing efforts to improve the susceptor temperature uniformity and reduce unintentional hydrocarbon generation to improve layer uniformity and reproducibility, are presented. (orig.) 18 refs.

  16. Abnormal optical behaviour of InAsSb quantum dots grown on GaAs substrate by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Rihani, J.; Ben Sedrine, N.; Sallet, V.; Harmand, J.C.; Oueslati, M.; Chtourou, R.

    2008-01-01

    InAs(Sb) quantum dots (QDs) samples were grown on GaAs (001) substrate by Molecular Beam Epitaxy (MBE). The structural characterization by Atomic Force Microscopy (AFM) of samples shows that InAsSb islands size increases strongly with antimony incorporation in InAs/GaAs QDs and decreases with reducing the growth temperature from 520 deg. C to 490 deg. C. Abnormal optical behaviour was observed in room temperature (RT) photoluminescence (PL) spectra of samples grown at high temperature (520 deg. C). Temperature dependent PL study was investigated and reveals an anomalous evolution of emission peak energy (EPE) of InAsSb islands, well-known as 'S-inverted curve' and attributed to the release of confined carriers from the InAsSb QDs ground states to the InAsSb wetting layer (WL) states. With only decreasing the growth temperature, the S-inverted shape was suppressed indicating a fulfilled 3D-confinement of carriers in the InAsSb/GaAs QD sample

  17. H{sub 2}O{sub 2}-molecular beam epitaxy of high quality ZnO

    Energy Technology Data Exchange (ETDEWEB)

    El Shaer, A.; Bakin, A.; Che Mofor, A.; Kreye, M.; Waag, A. [Technical University Braunschweig, Institute of Semiconductor Technology, Braunschweig (Germany); Blaesing, J.; Krost, A. [Otto-von-Guericke-University, Institute of Experimental Physics, Magdeburg (Germany); Stoimenos, J. [Aristotele University, Physics Department, Thessaloniki (Greece); Pecz, B. [Hungarian Academy of Sciences, Research Institute for Technical Physics and Materials Science, P.O. Box 49, Budapest (Hungary)

    2007-07-15

    We have studied the growth and characterization of ZnO epilayers on (0001)-sapphire by H{sub 2}O{sub 2}-molecular beam epitaxy (MBE). A high temperature (HT) MgO buffer followed by a low-temperature ZnO buffer was introduced in order to accommodate the lattice mismatch between ZnO and sapphire. The surface morphology of the samples was studied using atomic force microscopy (AFM), and scanning electron microscopy (SEM). The crystalline quality of the layers was investigated by employing high resolution X-ray diffractometry (HRXRD) and high resolution transmission electron microscopy (HRTEM). The electrical properties of the grown ZnO layers were studied by Hall-effect measurements in a standard van der Pauw configuration. The measured surface roughness for the best layers is as low as 0.26 nm rms. HRXRD measurements of the obtained ZnO layers show excellent quality of the single crystalline ZnO heteroepitaxially grown on (0001)-sapphire with a HT MgO buffer layers. The influence of the growth conditions on the crystalline quality is discussed. The FWHM of the HRXRD (0002) rocking curves measured for the 2-inch ZnO-on-sapphire is as low as 27 arcsec with a very high lateral homogeneity across the whole 2-inch ZnO epilayers. The results indicate that H{sub 2}O{sub 2}-MBE is a suitable technique to fabricate ZnO epilayers of very high quality. (orig.)

  18. Evolution of spirals during molecular beam epitaxy of GaN on 6H-SiC(0001)

    International Nuclear Information System (INIS)

    Cui, Y.; Li, L.

    2002-01-01

    Evolution of spirals during molecular beam epitaxy growth of GaN films on 6H-SiC(0001) was studied by in situ scanning tunneling microscopy. It was found that dislocations emerge at the film surface, creating straight steps with orientation along directions with a density of 10 10 cm -2 for 40-nm-thick films. During subsequent growth, these straight steps wind around dislocations and develop into spirals with a density of 10 9 cm -2 for 100-nm-thick films. The spirals can be classified into three types: single arm, interlocking double arm, and closed loop. The first two types originate from steps with one end pinned, and the third type results from steps with both ends pinned. At film thickness larger than 200 nm, these spirals further evolve into spiral mounds with a density of 10 7 cm -2 . Based on the Burton, Cabrera, and Frank theory, a model is proposed to explain the formation of different types of spirals and the reduction of their densities

  19. Substrate temperature dependence of ZnTe epilayers grown on GaAs(0 0 1) by molecular beam epitaxy

    Science.gov (United States)

    Zhao, Jie; Zeng, Yiping; Liu, Chao; Li, Yanbo

    2010-04-01

    ZnTe thin films have been grown on GaAs(0 0 1) substrates at different temperatures with constant Zn and Te beam equivalent pressures (BEPs) by molecular beam epitaxy (MBE). In situ reflection high-energy electron diffraction (RHEED) observation indicates that two-dimensional (2D) growth mode can be established after around one-minute three-dimensional (3D) nucleation by increasing the substrate temperature to 340 °C. We found that Zn desorption from the ZnTe surface is much greater than that of Te at higher temperatures, and estimated the Zn sticking coefficient by the evolution of growth rate. The Zn sticking coefficient decreases from 0.93 to 0.58 as the temperature is elevated from 320 to 400 °C. The ZnTe epilayer grown at 360 °C displays the narrowest full-width at half-maximum (FWHM) of 660 arcsec from (0 0 4) reflection in double-crystal X-ray rocking curve (DCXRC) measurements. The surface morphology of ZnTe epilayers is strongly dependent on the substrate temperature, and the root-mean-square (RMS) roughness diminishes drastically with the increase in temperature.

  20. EuO and Gd-doped EuO thin films. Epitaxial growth and properties

    International Nuclear Information System (INIS)

    Sutarto, Ronny

    2009-01-01

    quality of many of the doped EuO samples used in the past bulk studies. The focus of this thesis is on the preparation and the properties of high-quality single-crystalline EuO and Gd-doped EuO thin films. The so-called Eu-distillation-assisted molecular beam epitaxy (MBE) has been employed to achieve full control of the stoichiometry. The films have been epitaxially grown on yttria-stabilized cubic zirconia (YSZ) (001) substrates. By a systematic variation of the oxygen deposition rates, we have been able to observe sustained oscillations in the intensity of the reflection high-electron energy diffraction (RHEED) pattern during growth. We thus have demonstrated that layer-by-layer growth has been achieved for the first time. We also have confirmed that YSZ indeed supplies oxygen during the initial stages of growth, yet the EuO stoichiometry can still be well maintained. In the case of Gd-doped EuO films, the presence of Gd even helps to stabilize the layer-by-layer growth mode. It is important to achieve this growth mode, since it enables the preparation of films with very smooth and at surfaces. This in turn facilitates the capping of the films with a thin Al overlayer in order to protect the films against degradation under ambient conditions. More important, the smoothness of the lm will enable the preparation of high quality device structures. By using ex-situ soft x-ray absorption spectroscopy (XAS) at the Eu and Gd M 4,5 edges, we have confirmed that the films are completely free from Eu 3+ contaminants, and we were able to determine reliably the actual Gd concentration. This actual Gd concentration could in fact significantly deviate from the nominal Gd/Eu evaporation ratio. From magnetization and susceptibility measurements, we found the Curie temperature to increase smoothly as a function of doping from 69 K up to a maximum of 125 K, all with a saturation moment of 7 μB. A threshold behavior was not observed for Gd concentrations as low as 0.2 %. Analysis of the

  1. EuO and Gd-doped EuO thin films. Epitaxial growth and properties

    Energy Technology Data Exchange (ETDEWEB)

    Sutarto, Ronny

    2009-07-06

    this respect the quality of many of the doped EuO samples used in the past bulk studies. The focus of this thesis is on the preparation and the properties of high-quality single-crystalline EuO and Gd-doped EuO thin films. The so-called Eu-distillation-assisted molecular beam epitaxy (MBE) has been employed to achieve full control of the stoichiometry. The films have been epitaxially grown on yttria-stabilized cubic zirconia (YSZ) (001) substrates. By a systematic variation of the oxygen deposition rates, we have been able to observe sustained oscillations in the intensity of the reflection high-electron energy diffraction (RHEED) pattern during growth. We thus have demonstrated that layer-by-layer growth has been achieved for the first time. We also have confirmed that YSZ indeed supplies oxygen during the initial stages of growth, yet the EuO stoichiometry can still be well maintained. In the case of Gd-doped EuO films, the presence of Gd even helps to stabilize the layer-by-layer growth mode. It is important to achieve this growth mode, since it enables the preparation of films with very smooth and at surfaces. This in turn facilitates the capping of the films with a thin Al overlayer in order to protect the films against degradation under ambient conditions. More important, the smoothness of the lm will enable the preparation of high quality device structures. By using ex-situ soft x-ray absorption spectroscopy (XAS) at the Eu and Gd M{sub 4,5} edges, we have confirmed that the films are completely free from Eu{sup 3+} contaminants, and we were able to determine reliably the actual Gd concentration. This actual Gd concentration could in fact significantly deviate from the nominal Gd/Eu evaporation ratio. From magnetization and susceptibility measurements, we found the Curie temperature to increase smoothly as a function of doping from 69 K up to a maximum of 125 K, all with a saturation moment of 7 {mu}B. A threshold behavior was not observed for Gd concentrations

  2. CeCo5 thin films with perpendicular anisotropy grown by molecular beam epitaxy

    Science.gov (United States)

    Sharma, S.; Hildebrandt, E.; Major, M.; Komissinskiy, P.; Radulov, I.; Alff, L.

    2018-04-01

    Buffer-free, highly textured (0 0 1) oriented CeCo5 thin films showing perpendicular magnetic anisotropy were synthesized on (0 0 1) Al2O3 substrates by molecular beam epitaxy. Ce exists in a mixture of Ce3+ and Ce4+ valence states as shown by X-ray photoelectron spectroscopy. The first anisotropy constant, K1, as measured by torque magnetometry was 0.82 MJ/m3 (8.2 ×106erg /cm3) . A maximum coercivity of 5.16 kOe with a negative temperature coefficient of -0.304%K-1 and a magnetization of 527.30 emu/cm3 was measured perpendicular to the film plane at 5 K. In addition, a large anisotropy of the magnetic moment of 15.5% was observed. These magnetic parameters make CeCo5 a potential candidate material for spintronic and magnetic recording applications.

  3. Molecular-Beam Epitaxially Grown MgB2 Thin Films and Superconducting Tunnel Junctions

    Directory of Open Access Journals (Sweden)

    Jean-Baptiste Laloë

    2011-01-01

    Full Text Available Since the discovery of its superconducting properties in 2001, magnesium diboride has generated terrific scientific and engineering research interest around the world. With a of 39 K and two superconducting gaps, MgB2 has great promise from the fundamental point of view, as well as immediate applications. Several techniques for thin film deposition and heterojunction formation have been established, each with its own advantages and drawbacks. Here, we will present a brief overview of research based on MgB2 thin films grown by molecular beam epitaxy coevaporation of Mg and B. The films are smooth and highly crystalline, and the technique allows for virtually any heterostructure to be formed, including all-MgB2 tunnel junctions. Such devices have been characterized, with both quasiparticle and Josephson tunneling reported. MgB2 remains a material of great potential for a multitude of further characterization and exploration research projects and applications.

  4. Characterization of InGaGdN layers prepared by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Tawil, Siti Nooraya Mohd [Institute of Scientific and Industrial Research, Osaka University, 8-1 Mihagaoka, Ibaraki, 567-0047 Osaka (Japan); Faculty of Electrical and Electronic Engineering, Tun Hussein Onn University of Malaysia, 86400 Batu Pahat Johor (Malaysia); Kakimi, Rina; Krishnamurthy, Daivasigamani; Emura, Shuichi; Tambo, Hiroyuki; Hasegawa, Shigehiko; Asahi, Hajime [Institute of Scientific and Industrial Research, Osaka University, 8-1 Mihagaoka, Ibaraki, 567-0047 Osaka (Japan)

    2010-11-15

    Gd-doped InGaN layers were prepared by plasma-assisted molecular-beam epitaxy in search of new functional diluted magnetic semiconductors for their potential use in spintronics. The local structure around the Gd atoms was examined by the Gd L{sub III}-edge of X-ray absorption fine structure. It was found that the majority of Gd atoms substitutionally occupied the cation sites in the InGaGdN layers. Clear hysteresis and saturation magnetization were observed from the magnetization versus field curves examined by means of a superconducting quantum interference device magnetometer at low and room temperatures. In addition, the incorporation of extra shallow donors by co-doping InGaN with both Gd and Si showed higher magnetization than the undoped InGaGdN. (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  5. SIMS studies of CI- doped Zn Se epilayers grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Gard, F.S.; Riley, J.D.; Lekey, R.; Usher, B.F.; Prine, K.

    2004-01-01

    Chlorine is one of the most used species to produce n-type zinc selenium epilayers. In this paper, we present secondary ion mass spectrometry profiles of a series of chlorine-doped zinc selenium samples, which were grown in a molecular beam epitaxy chamber. These profiles have been used to examine the limitation of secondary ion mass spectrometry analysis of narrow chlorine-delta layers. In order to covert secondary ion mass spectrometry raw data to quantified data, the depth profile from a chlorine-implanted standard sample has been used to estimate the u seful ion yield o f chlorine and thus the instrument sensitivity for chlorine in a zinc selenium matrix. The u seful ion yield a nd detection limit of chlorine in the zinc selenium host matrix were calculated to be 4.7 X 10 -17 atoms/ cm 3 , respectively

  6. High electron mobility in Ga(In)NAs films grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Miyashita, Naoya; Ahsan, Nazmul; Monirul Islam, Muhammad; Okada, Yoshitaka; Inagaki, Makoto; Yamaguchi, Masafumi

    2012-01-01

    We report the highest mobility values above 2000 cm 2 /Vs in Si doped GaNAs film grown by molecular beam epitaxy. To understand the feature of the origin which limits the electron mobility in GaNAs, temperature dependences of mobility were measured for high mobility GaNAs and referential low mobility GaInNAs. Temperature dependent mobility for high mobility GaNAs is similar to the GaAs case, while that for low mobility GaInNAs shows large decrease in lower temperature region. The electron mobility of high quality GaNAs can be explained by intrinsic limiting factor of random alloy scattering and extrinsic factor of ionized impurity scattering.

  7. Structural evolution of dilute magnetic (Sn,Mn)Se films grown by molecular beam epitaxy

    Science.gov (United States)

    Kanzyuba, Vasily; Dong, Sining; Liu, Xinyu; Li, Xiang; Rouvimov, Sergei; Okuno, Hanako; Mariette, Henri; Zhang, Xueqiang; Ptasinska, Sylwia; Tracy, Brian D.; Smith, David J.; Dobrowolska, Margaret; Furdyna, Jacek K.

    2017-02-01

    We describe the structural evolution of dilute magnetic (Sn,Mn)Se films grown by molecular beam epitaxy on GaAs (111) substrates, as revealed by transmission electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. When the Mn concentration is increased, the lattice of the ternary (Sn,Mn)Se films evolves quasi-coherently from a SnSe2 two-dimensional (2D) crystal structure into a more complex quasi-2D lattice rearrangement, ultimately transforming into the magnetically concentrated antiferromagnetic MnSe 3D rock-salt structure as Mn approaches 50 at. % of this material. These structural transformations are expected to underlie the evolution of magnetic properties of this ternary system reported earlier in the literature.

  8. High efficiency thin film solar cells grown by molecular beam epitaxy (HEFTY)

    Energy Technology Data Exchange (ETDEWEB)

    Mason, N.B.; Barnham, K.W.J.; Ballard, I.M.; Zhang, J. [Imperial College, London (United Kingdom)

    2006-05-04

    The project sought to show the UK as a world leader in the field of thin film crystalline solar cells. A premise was that the cell design be suitable for large-scale manufacturing and provide a basis for industrial exploitation. The study demonstrated (1) that silicon films grown at temperatures suitable for deposition on glass by Gas Phase Molecular Beam Epitaxy gives better PV cells than does Ultra Low Pressure Chemical Vapor Deposition; (2) a conversion energy of 15 per cent was achieved - the project target was 18 per cent and (3) one of the highest reported conversion efficiencies for a 15 micrometre silicon film was achieved. The study was carried out by BP Solar Limited under contract to the DTI.

  9. Demonstration of molecular beam epitaxy and a semiconducting band structure for I-Mn-V compounds

    Czech Academy of Sciences Publication Activity Database

    Jungwirth, Tomáš; Novák, Vít; Martí, X.; Cukr, Miroslav; Máca, František; Shick, Alexander; Mašek, Jan; Horodyská, P.; Němec, P.; Holý, V.; Zemek, Josef; Kužel, Petr; Němec, I.; Gallagher, B. L.; Campion, R. P.; Foxon, C. T.; Wunderlich, Joerg

    2011-01-01

    Roč. 83, č. 3 (2011), , , "035321-1"-"035321-6" ISSN 1098-0121 R&D Projects: GA MŠk LC510; GA AV ČR KAN400100652; GA MŠk(CZ) 7E08087 EU Projects: European Commission(XE) 215368 - SemiSpinNet; European Commission(XE) 214499 - NAMASTE; European Commission(XE) 268066 - 0MSPIN Grant - others:AV ČR(CZ) AP0801 Program:Akademická prémie - Praemium Academiae Institutional research plan: CEZ:AV0Z10100520; CEZ:AV0Z10100521 Keywords : antiferromagnetic semiconductors * spintronics * molecular beam epitaxy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.691, year: 2011

  10. Group III nitride-arsenide long wavelength lasers grown by elemental source molecular beam epitaxy

    International Nuclear Information System (INIS)

    Coldren, C. W.; Spruytte, S. G.; Harris, J. S.; Larson, M. C.

    2000-01-01

    Elemental source molecular beam epitaxy was used to grow InGaNAs quantum well samples, edge-emitting laser diodes, and vertical-cavity laser diodes on GaAs substrates. The quantum well samples exhibited an as-grown room temperature photoluminescence peak beyond 1310 nm which both increased dramatically in intensity and blueshifted with thermal annealing. Edge emitting laser diodes had threshold current densities as low as 450 and 750 A/cm 2 for single and triple quantum well active regions, respectively, and emitted light at 1220-1250 nm. The vertical cavity laser diodes emitted light at 1200 nm and had threshold current densities of 3 kA/cm 2 and efficiencies of 0.066 W/A. (c) 2000 American Vacuum Society

  11. High power ultraviolet light emitting diodes based on GaN/AlGaN quantum wells produced by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Cabalu, J. S.; Bhattacharyya, A.; Thomidis, C.; Friel, I.; Moustakas, T. D.; Collins, C. J.; Komninou, Ph.

    2006-01-01

    In this paper, we report on the growth by molecular beam epitaxy and fabrication of high power nitride-based ultraviolet light emitting diodes emitting in the spectral range between 340 and 350 nm. The devices were grown on (0001) sapphire substrates via plasma-assisted molecular beam epitaxy. The growth of the light emitting diode (LED) structures was preceded by detailed materials studies of the bottom n-AlGaN contact layer, as well as the GaN/AlGaN multiple quantum well (MQW) active region. Specifically, kinetic conditions were identified for the growth of the thick n-AlGaN films to be both smooth and to have fewer defects at the surface. Transmission-electron microscopy studies on identical GaN/AlGaN MQWs showed good quality and well-defined interfaces between wells and barriers. Large area mesa devices (800x800 μm 2 ) were fabricated and were designed for backside light extraction. The LEDs were flip-chip bonded onto a Si submount for better heat sinking. For devices emitting at 340 nm, the measured differential on-series resistance is 3 Ω with electroluminescence spectrum full width at half maximum of 18 nm. The output power under dc bias saturates at 0.5 mW, while under pulsed operation it saturates at approximately 700 mA to a value of 3 mW, suggesting that thermal heating limits the efficiency of these devices. The output power of the investigated devices was found to be equivalent with those produced by the metal-organic chemical vapor deposition and hydride vapor-phase epitaxy methods. The devices emitting at 350 nm were investigated under dc operation and the output power saturates at 4.5 mW under 200 mA drive current

  12. Aluminum Gallium Nitride Alloys Grown via Metalorganic Vapor-Phase Epitaxy Using a Digital Growth Technique

    Science.gov (United States)

    Rodak, L. E.; Korakakis, D.

    2011-04-01

    This work investigates the use of a digital growth technique as a viable method for achieving high-quality aluminum gallium nitride (Al x Ga1- x N) films via metalorganic vapor-phase epitaxy. Digital alloys are superlattice structures with period thicknesses of a few monolayers. Alloys with an AlN mole fraction ranging from 0.1 to 0.9 were grown by adjusting the thickness of the AlN layer in the superlattice. High-resolution x-ray diffraction was used to determine the superlattice period and c-lattice parameter of the structure, while reciprocal-space mapping was used to determine the a-lattice parameter and evaluate growth coherency. A comparison of the measured lattice parameter with both the nominal value and also the underlying buffer layer is discussed.

  13. Defect distribution in low-temperature molecular beam epitaxy grown Si/Si(100), improved depth profiling with monoenergetic positrons

    International Nuclear Information System (INIS)

    Szeles, C.; Asoka-Kumar, P.; Lynn, K.G.; Gossmann, H.; Unterwald, F.C.; Boone, T.

    1995-01-01

    The depth distribution of open-volume defects has been studied in Si(100) crystals grown by molecular beam epitaxy at 300 degree C by the variable-energy monoenergetic positron beam technique combined with well-controlled chemical etching. This procedure gave a 10 nm depth resolution which is a significant improvement over the inherent depth resolving power of the positron beam technique. The epitaxial layer was found to grow defect-free up to 80 nm, from the interface, where small vacancy clusters, larger than divacancies, appear. The defect density then sharply increases toward the film surface. The result clearly shows that the nucleation of small open-volume defects is a precursor state to the breakdown of epitaxy and to the evolution of an amorphous film

  14. Investigation of microstructure and morphology for the Ge on porous silicon/Si substrate hetero-structure obtained by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Gouder, S.; Mahamdi, R.; Aouassa, M.; Escoubas, S.; Favre, L.; Ronda, A.; Berbezier, I.

    2014-01-01

    Thick porous silicon (PS) buffer layers are used as sacrificial layers to epitaxially grow planar and fully relaxed Ge membranes. The single crystal Ge layers have been deposited by molecular beam epitaxy (MBE) on PS substrate. During deposition, the pore network of PS layers has been filled with Ge. We investigate the structure and morphology of PS as fabricated and after annealing at various temperatures. We show that the PS crystalline lattice is distorted and expanded in the direction perpendicular to the substrate plane due to the presence of chemisorbed –OH. An annealing at high temperature (> 500 °C), greatly changes the PS morphology and structure. This change is marked by an increase of the pore diameter while the lattice parameter becomes tensily strained in the plane (compressed in the direction perpendicular). The morphology and structure of Ge layers are investigated by transmission electron microscopy, high resolution X-ray diffraction and atomic force microscopy as a function of the deposition temperature and deposited thickness. The results show that the surface roughness, level of relaxation and Si-Ge intermixing (Ge content) depend on the growth temperature and deposited thickness. Two sub-layers are distinguished: the layer incorporated inside the PS pores (high level of intermixing) and the layer on top of the PS surface (low level of intermixing). When deposited at temperature > 500 °C, the Ge layers are fully relaxed with a top Si 1−x Ge x layer x = 0.74 and a very flat surface. Such layer can serve as fully relaxed ultra-thin SiGe pseudo-substrate with high Ge content. The epitaxy of Ge on sacrificial soft PS pseudo-substrate in the experimental conditions described here provides an easy way to fabricate fully relaxed SiGe pseudo-substrates. Moreover, Ge thin films epitaxially deposited by MBE on PS could be used as relaxed pseudo-substrate in conventional microelectronic technology. - Highlights: • We have developed a rapid and low

  15. From epitaxial growth of ferrite thin films to spin-polarized tunnelling

    International Nuclear Information System (INIS)

    Moussy, Jean-Baptiste

    2013-01-01

    This paper presents a review of the research which is focused on ferrite thin films for spintronics. First, I will describe the potential of ferrite layers for the generation of spin-polarized currents. In the second step, the structural and chemical properties of epitaxial thin films and ferrite-based tunnel junctions will be presented. Particular attention will be given to ferrite systems grown by oxygen-assisted molecular beam epitaxy. The analysis of the structure and chemistry close to the interfaces, a key-point for understanding the spin-polarized tunnelling measurements, will be detailed. In the third part, the magnetic and magneto-transport properties of magnetite (Fe 3 O 4 ) thin films as a function of structural defects such as the antiphase boundaries will be explained. The spin-polarization measurements (spin-resolved photoemission, tunnel magnetoresistance) on this oxide predicted to be half-metallic will be discussed. Fourth, the potential of magnetic tunnel barriers, such as CoFe 2 O 4 , NiFe 2 O 4 or MnFe 2 O 4 , whose insulating behaviour and the high Curie temperatures make it exciting candidates for spin filtering at room temperature will be described. Spin-polarized tunnelling experiments, involving either Meservey–Tedrow or tunnel magnetoresistance measurements, will reveal significant spin-polarizations of the tunnelling current at low temperatures but also at room temperatures. Finally, I will mention a few perspectives with ferrite-based heterostructures. (topical review)

  16. Selective epitaxial growth of stepwise SiGe:B at the recessed sources and drains: A growth kinetics and strain distribution study

    Directory of Open Access Journals (Sweden)

    Sangmo Koo

    2016-09-01

    Full Text Available The selective epitaxial growth of Si1-xGex and the related strain properties were studied. Epitaxial Si1-xGex films were deposited on (100 and (110 orientation wafers and on patterned Si wafers with recessed source and drain structures via ultrahigh vacuum chemical vapor deposition using different growing steps and Ge concentrations. The stepwise process was split into more than 6 growing steps that ranged in thicknesses from a few to 120 nm in order to cover the wide stages of epitaxial growth. The growth rates of SiGe on the plane and patterned wafers were examined and a dependence on the surface orientation was identified. As the germanium concentration increased, defects were generated with thinner Si1-xGex growth. The defect generation was the result of the strain evolution which was examined for channel regions with a Si1-xGex source/drain (S/D structure.

  17. Real-time growth study of plasma assisted atomic layer epitaxy of InN films by synchrotron x-ray methods

    Energy Technology Data Exchange (ETDEWEB)

    Nepal, Neeraj [U.S. Naval Research Laboratory, 4555 Overlook Avenue SW, Washington, DC 20375; Anderson, Virginia R. [American Society for Engineering Education, 1818 N Street NW, Washington, DC 20036; Johnson, Scooter D. [U.S. Naval Research Laboratory, 4555 Overlook Avenue SW, Washington, DC 20375; Downey, Brian P. [U.S. Naval Research Laboratory, 4555 Overlook Avenue SW, Washington, DC 20375; Meyer, David J. [U.S. Naval Research Laboratory, 4555 Overlook Avenue SW, Washington, DC 20375; DeMasi, Alexander [Physics Department, Boston University, 590 Commonwealth Avenue, Boston, Massachusetts 02215; Robinson, Zachary R. [Department of Physics, SUNY College at Brockport, 350 New Campus Dr, Brockport, New York 14420; Ludwig, Karl F. [Physics Department, Boston University, 590 Commonwealth Avenue, Boston, Massachusetts 02215; Eddy, Charles R. [U.S. Naval Research Laboratory, 4555 Overlook Avenue SW, Washington, DC 20375

    2017-03-13

    The temporal evolution of high quality indium nitride (InN) growth by plasma-assisted atomic layer epitaxy (ALEp) on a-plane sapphire at 200 and 248 °C was probed by synchrotron x-ray methods. The growth was carried out in a thin film growth facility installed at beamline X21 of the National Synchrotron Light Source at Brookhaven National Laboratory and at beamline G3 of the Cornell High Energy Synchrotron Source, Cornell University. Measurements of grazing incidence small angle x-ray scattering (GISAXS) during the initial cycles of growth revealed a broadening and scattering near the diffuse specular rod and the development of scattering intensities due to half unit cell thick nucleation islands in the Yoneda wing with correlation length scale of 7.1 and 8.2 nm, at growth temperatures (Tg) of 200 and 248 °C, respectively. At about 1.1 nm (two unit cells) of growth thickness nucleation islands coarsen, grow, and the intensity of correlated scattering peak increased at the correlation length scale of 8.0 and 8.7 nm for Tg = 200 and 248 °C, respectively. The correlated peaks at both growth temperatures can be fitted with a single peak Lorentzian function, which support single mode growth. Post-growth in situ x-ray reflectivity measurements indicate a growth rate of ~0.36 Å/cycle consistent with the growth rate previously reported for self-limited InN growth in a commercial ALEp reactor. Consistent with the in situ GISAXS study, ex situ atomic force microscopy power spectral density measurements also indicate single mode growth. Electrical characterization of the resulting film revealed an electron mobility of 50 cm2/V s for a 5.6 nm thick InN film on a-plane sapphire, which is higher than the previously reported mobility of much thicker InN films grown at higher temperature by molecular beam epitaxy directly on sapphire. These early results indicated that in situ synchrotron x-ray study of the epitaxial growth kinetics of InN films is a very powerful method to

  18. Morphology and grain structure evolution during epitaxial growth of Ag films on native-oxide-covered Si surface

    International Nuclear Information System (INIS)

    Hur, Tae-Bong; Kim, Hong Koo; Perello, David; Yun, Minhee; Kulovits, Andreas; Wiezorek, Joerg

    2008-01-01

    Epitaxial nanocrystalline Ag films were grown on initially native-oxide-covered Si(001) substrates using radio-frequency magnetron sputtering. Mechanisms of grain growth and morphology evolution were investigated. An epitaxially oriented Ag layer (∼5 nm thick) formed on the oxide-desorbed Si surface during the initial growth phase. After a period of growth instability, characterized as kinetic roughening, grain growth stagnation, and increase of step-edge density, a layer of nanocrystalline Ag grains with a uniform size distribution appeared on the quasi-two-dimensional layer. This hierarchical process of film formation is attributed to the dynamic interplay between incoming energetic Ag particles and native oxide. The cyclic interaction (desorption and migration) of the oxide with the growing Ag film is found to play a crucial role in the characteristic evolution of grain growth and morphology change involving an interval of grain growth stagnation

  19. Epitaxial growth of higher transition-temperature VO2 films on AlN/Si

    Directory of Open Access Journals (Sweden)

    Tetiana Slusar

    2016-02-01

    Full Text Available We report the epitaxial growth and the mechanism of a higher temperature insulator-to-metal-transition (IMT of vanadium dioxide (VO2 thin films synthesized on aluminum nitride (AlN/Si (111 substrates by a pulsed-laser-deposition method; the IMT temperature is TIMT ≈ 350 K. X-ray diffractometer and high resolution transmission electron microscope data show that the epitaxial relationship of VO2 and AlN is VO2 (010 ‖ AlN (0001 with VO2 [101] ‖   AlN   [ 2 1 ̄ 1 ̄ 0 ] zone axes, which results in a substrate-induced tensile strain along the in-plane a and c axes of the insulating monoclinic VO2. This strain stabilizes the insulating phase of VO2 and raises TIMT for 10 K higher than TIMT single crystal ≈ 340 K in a bulk VO2 single crystal. Near TIMT, a resistance change of about four orders is observed in a thick film of ∼130 nm. The VO2/AlN/Si heterostructures are promising for the development of integrated IMT-Si technology, including thermal switchers, transistors, and other applications.

  20. Sub-monolayer growth of titanium, cobalt, and palladium on epitaxial graphene

    Energy Technology Data Exchange (ETDEWEB)

    Sokolova, Anastasia; Kilchert, Franziska; Schneider, M. Alexander [Lehrstuhl fuer Festkoerperphysik, Friedrich-Alexander Universitaet Erlangen-Nuernberg (FAU), Erlangen (Germany); Link, Stefan; Stoehr, Alexander; Starke, Ulrich [Max-Planck-Institut fuer Festkoerperforschung, Stuttgart (Germany)

    2017-11-15

    We deposited metals (Ti, Co, Pd) typically used as seed layers for contacts on epitaxial graphene on SiC(0001) and studied the early stages of growth in the sub-monolayer regime by Scanning Tunneling Microscopy (STM). All three metals do not wet the substrate and Ostwalt ripening occurs at temperatures below 400 K. The analysis of the epitaxial orientation of the metal adislands revealed their specific alignment to the graphene lattice. It is found that the apparent height of the islands as measured by STM strongly deviates from their true topographic height. This is interpreted as an indication of the presence of scattering processes within the metal particles that increase the transparency of the metal-graphene interface for electrons. Even large islands are easily picked up by the tip of the STM allowing insight into the bonding between metal island and graphene surface and into mechanisms leading to metal intercalation. (copyright 2017 by WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  1. Growth of CoSi2 on Si(001) by reactive deposition epitaxy

    International Nuclear Information System (INIS)

    Lim, C.W.; Shin, C.-S.; Gall, D.; Zuo, J.M.; Petrov, I.; Greene, J.E.

    2005-01-01

    CaF 2 -structure CoSi 2 layers were formed on Si(001) by reactive deposition epitaxy (RDE) and compared with CoSi 2 layers obtained by conventional solid phase growth (SPG). In both sets of experiments, Co was deposited by ultrahigh-vacuum magnetron sputtering and CoSi 2 formed at 600 deg. C. However, in the case of RDE, CoSi 2 formation occurred during Co deposition while for SPG, Co was deposited at 25 deg. C and silicidation took place during subsequent annealing. X-ray diffraction pole figures and transmission electron microscopy results demonstrate that RDE CoSi 2 layers are epitaxial with a cube-on-cube relationship (001) CoSi 2 parallel (001) Si and [100] CoSi 2 parallel[100] Si . In contrast, SPG films are polycrystalline with an average grain size of ≅1000 A and a mixed 111/002/022/112 orientation. We attribute the striking difference to rapid Co diffusion into the Si(001) substrate during RDE for which the high Co/Si reactivity gives rise to a flux-limited reaction resulting in the direct formation of the disilicide phase. In contrast, sequential nucleation and transformation among increasingly Si-rich phases--from orthorhombic Co 2 Si to cubic CoSi to CoSi 2 --during SPG results in polycrystalline layers with a complex texture

  2. Step-flow anisotropy of the m-plane GaN (1100) grown under nitrogen-rich conditions by plasma-assisted molecular beam epitaxy

    International Nuclear Information System (INIS)

    Sawicka, Marta; Siekacz, Marcin; Skierbiszewski, Czeslaw; Turski, Henryk; Krysko, Marcin; DziePcielewski, Igor; Grzegory, Izabella; Smalc-Koziorowska, Julita

    2011-01-01

    The homoepitaxial growth of m-plane (1100) GaN was investigated by plasma-assisted molecular beam epitaxy under nitrogen-rich conditions. The surface morphologies as a function of sample miscut were studied, providing evidence for a strong growth anisotropy that is a consequence of the anisotropy of Ga adatom diffusion barriers on the m-plane surface recently calculated ab initio[Lymperakis and Neugebauer, Phys. Rev. B 79, 241308(R) (2009)]. We found that substrate miscut toward [0001] implies a step flow toward while substrate miscut toward [0001] causes formation of atomic steps either perpendicular or parallel to the [0001] direction, under N-rich conditions at 730 deg C. We describe the growth conditions for achieving atomically flat m-plane GaN layers with parallel atomic steps.

  3. Epitaxial growth and magnetic properties of ultraviolet transparent Ga2O3/(Ga1−xFex)2O3 multilayer thin films

    Science.gov (United States)

    Guo, Daoyou; An, Yuehua; Cui, Wei; Zhi, Yusong; Zhao, Xiaolong; Lei, Ming; Li, Linghong; Li, Peigang; Wu, Zhenping; Tang, Weihua

    2016-01-01

    Multilayer thin films based on the ferromagnetic and ultraviolet transparent semiconductors may be interesting because their magnetic/electronic/photonic properties can be manipulated by the high energy photons. Herein, the Ga2O3/(Ga1−xFex)2O3 multilayer epitaxial thin films were obtained by alternating depositing of wide band gap Ga2O3 layer and Fe ultrathin layer due to inter diffusion between two layers at high temperature using the laser molecular beam epitaxy technique. The multilayer films exhibits a preferred growth orientation of crystal plane, and the crystal lattice expands as Fe replaces Ga site. Fe ions with a mixed valence of Fe2+ and Fe3+ are stratified distributed in the film and exhibit obvious agglomerated areas. The multilayer films only show a sharp absorption edge at about 250 nm, indicating a high transparency for ultraviolet light. What’s more, the Ga2O3/(Ga1−xFex)2O3 multilayer epitaxial thin films also exhibits room temperature ferromagnetism deriving from the Fe doping Ga2O3. PMID:27121446

  4. Epitaxial growth and magnetic properties of ultraviolet transparent Ga2O3/(Ga1-xFex)2O3 multilayer thin films.

    Science.gov (United States)

    Guo, Daoyou; An, Yuehua; Cui, Wei; Zhi, Yusong; Zhao, Xiaolong; Lei, Ming; Li, Linghong; Li, Peigang; Wu, Zhenping; Tang, Weihua

    2016-04-28

    Multilayer thin films based on the ferromagnetic and ultraviolet transparent semiconductors may be interesting because their magnetic/electronic/photonic properties can be manipulated by the high energy photons. Herein, the Ga2O3/(Ga1-xFex)2O3 multilayer epitaxial thin films were obtained by alternating depositing of wide band gap Ga2O3 layer and Fe ultrathin layer due to inter diffusion between two layers at high temperature using the laser molecular beam epitaxy technique. The multilayer films exhibits a preferred growth orientation of crystal plane, and the crystal lattice expands as Fe replaces Ga site. Fe ions with a mixed valence of Fe(2+) and Fe(3+) are stratified distributed in the film and exhibit obvious agglomerated areas. The multilayer films only show a sharp absorption edge at about 250 nm, indicating a high transparency for ultraviolet light. What's more, the Ga2O3/(Ga1-xFex)2O3 multilayer epitaxial thin films also exhibits room temperature ferromagnetism deriving from the Fe doping Ga2O3.

  5. Semiconductors and semimetals epitaxial microstructures

    CERN Document Server

    Willardson, Robert K; Beer, Albert C; Gossard, Arthur C

    1994-01-01

    Newly developed semiconductor microstructures can now guide light and electrons resulting in important consequences for state-of-the-art electronic and photonic devices. This volume introduces a new generation of epitaxial microstructures. Special emphasis has been given to atomic control during growth and the interrelationship between the atomic arrangements and the properties of the structures.Key Features* Atomic-level control of semiconductor microstructures* Molecular beam epitaxy, metal-organic chemical vapor deposition* Quantum wells and quantum wires* Lasers, photon(IR)detectors, heterostructure transistors

  6. Low Cost, Epitaxial Growth of II-VI Materials for Multijunction Photovoltaic Cells

    Energy Technology Data Exchange (ETDEWEB)

    Hardin, Brian E. [PLANT PV, Inc., Oakland, CA (United States); Peters, Craig H. [PLANT PV, Inc., Oakland, CA (United States)

    2014-04-30

    Multijunction solar cells have theoretical power conversion efficiencies in excess of 29% under one sun illumination and could become a highly disruptive technology if fabricated using low cost processing techniques to epitaxially grow defect tolerant, thin films on silicon. The PLANT PV/Molecular Foundry team studied the feasibility of using cadmium selenide (CdSe) as the wide band-gap, top cell and Si as the bottom cell in monolithically integrated tandem architecture. The greatest challenge in developing tandem solar cells is depositing wide band gap semiconductors that are both highly doped and have minority carrier lifetimes greater than 1 ns. The proposed research was to determine whether it is possible to rapidly grow CdSe films with sufficient minority carrier lifetimes and doping levels required to produce an open-circuit voltage (Voc) greater than 1.1V using close-space sublimation (CSS).

  7. Growth and characterization of ultrathin epitaxial MnO film on Ag(001)

    Science.gov (United States)

    Kundu, Asish K.; Menon, Krishnakumar S. R.

    2016-07-01

    We present here a comprehensive growth procedure to obtain a well-ordered MnO(001) ultrathin film on Ag(001) substrate. Depending upon the oxygen partial pressure during the growth, different phases of manganese oxide have been detected by Low Energy Electron Diffraction (LEED) and X-ray Photoelectron Spectroscopic (XPS) studies. A modified growth scheme has been adopted to get well-ordered and stoichiometric MnO(001) ultrathin film. The detailed growth mechanism of epitaxial MnO film on Ag(001) has been studied step by step, using LEED and XPS techniques. Observation of sharp (1 × 1) LEED pattern with a low inelastic background, corresponds to a long-range atomic order with low defect densities indicating the high structural quality of the film. The Mn 2p and Mn 3s core-level spectra confirm the oxidation state as well as the stoichiometry of the grown MnO films. Apart from the growth optimization, the evolution of strain relaxation of the MnO(001) film with film thickness has been explored.

  8. Surface Reaction Kinetics of Ga(1-x)In(x)P Growth During Pulsed Chemical Beam Epitaxy

    National Research Council Canada - National Science Library

    Dietz, N; Beeler, S. C; Schmidt, J. W; Tran, H. T

    2000-01-01

    ... into the surface reaction kinetics during an organometallic deposition process. These insights will allow us to move the control point closer to the point where the growth occurs, which in a chemical been epitaxy process is a surface reaction layer (SRL...

  9. Existence and nonexistence results for a singular boundary value problem arising in the theory of epitaxial growth

    Czech Academy of Sciences Publication Activity Database

    Escudero, C.; Hakl, Robert; Peral, I.; Torres, P.J.

    2014-01-01

    Roč. 37, č. 6 (2014), s. 793-807 ISSN 0170-4214 Institutional support: RVO:67985840 Keywords : singular boundary value problem * epitaxial growth * radial solution Subject RIV: BA - General Mathematics Impact factor: 0.918, year: 2014 http://onlinelibrary.wiley.com/doi/10.1002/mma.2836/full

  10. Impact of GaN transition layers in the growth of GaN epitaxial layer on silicon

    International Nuclear Information System (INIS)

    Zhao Danmei; Zhao Degang; Jiang Desheng; Liu Zongshun; Zhu Jianjun; Chen Ping; Liu Wei; Li Xiang; Shi Ming

    2015-01-01

    A method for growing GaN epitaxial layer on Si (111) substrate is investigated. Due to the large lattice mismatch between GaN and AlN, GaN grown directly above an AlN buffer layer on the Si substrate turns out to be of poor quality. In this study, a GaN transition layer is grown additionally on the AlN buffer before the GaN epitaxial growth. By changing the growth conditions of the GaN transition layer, we can control the growth and merging of islands and control the transfer time from 3D to 2D growth mode. With this method, the crystalline quality of the GaN epitaxial layer can be improved and the crack density is reduced. Here, we have investigated the impact of a transition layer on the crystalline quality and stress evolution of a GaN epitaxial layer with methods of X-ray diffraction, optical microscopy and in situ reflectivity trace. With the increasing thickness of transition layer, the crack decreases and the crystalline quality is improved. But when the transition layer exceeds a critical thickness, the crystalline quality of the epilayer becomes lower and the crack density increases. (paper)

  11. Structural properties of In0.53Ga0.47As epitaxial films grown on Si (111) substrates by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Gao, Fangliang; Wen, Lei; Zhang, Xiaona; Guan, Yunfang; Li, Jingling; Zhang, Shuguang; Li, Guoqiang

    2015-01-01

    In 0.53 Ga 0.47 As epitaxial films are grown on 2-inch diameter Si (111) substrates by growing a low-temperature In 0.4 Ga 0.6 As buffer layer using molecular beam epitaxy. The effect of the buffer layer thickness on the as-grown In 0.53 Ga 0.47 As films is characterized by X-ray diffraction, scanning electron microscopy, atomic force microscopy and transmission electron microscopy (TEM). It is revealed that the crystalline quality and surface morphology of as-grown In 0.53 Ga 0.47 As epilayer are strongly affected by the thickness of the In 0.4 Ga 0.6 As buffer layer. From TEM investigation, we understand that the type and the distribution of dislocations of the buffer layer and the as-grown In 0.53 Ga 0.47 As film are different. We have demonstrated that the In 0.4 Ga 0.6 As buffer layer with a thickness of 12 nm can advantageously release the lattice mismatch stress between the In 0.53 Ga 0.47 As and Si substrate, ultimately leading to a high-quality In 0.53 Ga 0.47 As epitaxial film with low surface roughness. - Highlights: • We provide a simple approach to achieve high-quality In 0.53 Ga 0.47 As films on Si. • An appropriate thickness of In 0.4 Ga 0.6 As buffer layer can release mismatch strain. • High-quality In 0.53 Ga 0.47 As film is grown on Si using 12-nm-thick buffer layer. • Smooth surface In 0.53 Ga 0.47 As film is grown on Si using 12-nm-thick buffer layer

  12. Growth of InP directly on Si by corrugated epitaxial lateral overgrowth

    International Nuclear Information System (INIS)

    Metaferia, Wondwosen; Kataria, Himanshu; Sun, Yan-Ting; Lourdudoss, Sebastian

    2015-01-01

    In an attempt to achieve an InP–Si heterointerface, a new and generic method, the corrugated epitaxial lateral overgrowth (CELOG) technique in a hydride vapor phase epitaxy reactor, was studied. An InP seed layer on Si (0 0 1) was patterned into closely spaced etched mesa stripes, revealing the Si surface in between them. The surface with the mesa stripes resembles a corrugated surface. The top and sidewalls of the mesa stripes were then covered by a SiO 2 mask after which the line openings on top of the mesa stripes were patterned. Growth of InP was performed on this corrugated surface. It is shown that growth of InP emerges selectively from the openings and not on the exposed silicon surface, but gradually spreads laterally to create a direct interface with the silicon, hence the name CELOG. We study the growth behavior using growth parameters. The lateral growth is bounded by high index boundary planes of {3 3 1} and {2 1 1}. The atomic arrangement of these planes, crystallographic orientation dependent dopant incorporation and gas phase supersaturation are shown to affect the extent of lateral growth. A lateral to vertical growth rate ratio as large as 3.6 is achieved. X-ray diffraction studies confirm substantial crystalline quality improvement of the CELOG InP compared to the InP seed layer. Transmission electron microscopy studies reveal the formation of a direct InP–Si heterointerface by CELOG without threading dislocations. While CELOG is shown to avoid dislocations that could arise due to the large lattice mismatch (8%) between InP and Si, staking faults could be seen in the layer. These are probably created by the surface roughness of the Si surface or SiO 2 mask which in turn would have been a consequence of the initial process treatments. The direct InP–Si heterointerface can find applications in high efficiency and cost-effective Si based III–V semiconductor multijunction solar cells and optoelectronics integration. (paper)

  13. Scalable solution-phase epitaxial growth of symmetry-mismatched heterostructures on two-dimensional crystal soft template.

    Science.gov (United States)

    Lin, Zhaoyang; Yin, Anxiang; Mao, Jun; Xia, Yi; Kempf, Nicholas; He, Qiyuan; Wang, Yiliu; Chen, Chih-Yen; Zhang, Yanliang; Ozolins, Vidvuds; Ren, Zhifeng; Huang, Yu; Duan, Xiangfeng

    2016-10-01

    Epitaxial heterostructures with precisely controlled composition and electronic modulation are of central importance for electronics, optoelectronics, thermoelectrics, and catalysis. In general, epitaxial material growth requires identical or nearly identical crystal structures with small misfit in lattice symmetry and parameters and is typically achieved by vapor-phase depositions in vacuum. We report a scalable solution-phase growth of symmetry-mismatched PbSe/Bi 2 Se 3 epitaxial heterostructures by using two-dimensional (2D) Bi 2 Se 3 nanoplates as soft templates. The dangling bond-free surface of 2D Bi 2 Se 3 nanoplates guides the growth of PbSe crystal without requiring a one-to-one match in the atomic structure, which exerts minimal restriction on the epitaxial layer. With a layered structure and weak van der Waals interlayer interaction, the interface layer in the 2D Bi 2 Se 3 nanoplates can deform to accommodate incoming layer, thus functioning as a soft template for symmetry-mismatched epitaxial growth of cubic PbSe crystal on rhombohedral Bi 2 Se 3 nanoplates. We show that a solution chemistry approach can be readily used for the synthesis of gram-scale PbSe/Bi 2 Se 3 epitaxial heterostructures, in which the square PbSe (001) layer forms on the trigonal/hexagonal (0001) plane of Bi 2 Se 3 nanoplates. We further show that the resulted PbSe/Bi 2 Se 3 heterostructures can be readily processed into bulk pellet with considerably suppressed thermal conductivity (0.30 W/m·K at room temperature) while retaining respectable electrical conductivity, together delivering a thermoelectric figure of merit ZT three times higher than that of the pristine Bi 2 Se 3 nanoplates at 575 K. Our study demonstrates a unique epitaxy mode enabled by the 2D nanocrystal soft template via an affordable and scalable solution chemistry approach. It opens up new opportunities for the creation of diverse epitaxial heterostructures with highly disparate structures and functions.

  14. Antimony segregation in Ge and formation of n-type selectively doped Ge films in molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Yurasov, D. V., E-mail: Inquisitor@ipm.sci-nnov.ru; Antonov, A. V.; Drozdov, M. N.; Schmagin, V. B.; Novikov, A. V. [Institute for Physics of Microstructures, Russian Academy of Sciences, GSP-105, 603950 Nizhny Novgorod (Russian Federation); Lobachevsky State University of Nizhni Novgorod, 23 Prospekt Gagarina, 603950 Nizhny Novgorod (Russian Federation); Spirin, K. E. [Institute for Physics of Microstructures, Russian Academy of Sciences, GSP-105, 603950 Nizhny Novgorod (Russian Federation)

    2015-10-14

    Antimony segregation in Ge(001) films grown by molecular beam epitaxy was studied. A quantitative dependence of the Sb segregation ratio in Ge on growth temperature was revealed experimentally and modeled theoretically taking into account both the terrace-mediated and step-edge-mediated segregation mechanisms. A nearly 5-orders-of-magnitude increase in the Sb segregation ratio in a relatively small temperature range of 180–350 °C was obtained, which allowed to form Ge:Sb doped layers with abrupt boundaries and high crystalline quality using the temperature switching method that was proposed earlier for Si-based structures. This technique was employed for fabrication of different kinds of n-type Ge structures which can be useful for practical applications like heavily doped n{sup +}-Ge films or δ-doped layers. Estimation of the doping profiles sharpness yielded the values of 2–5 nm per decade for the concentration gradient at the leading edge and 2–3 nm for the full-width-half-maximum of the Ge:Sb δ-layers. Electrical characterization of grown Ge:Sb structures revealed nearly full electrical activation of Sb atoms and the two-dimensional nature of charge carrier transport in δ-layers.

  15. Ellipsometry of rough CdTe(211)B-Ge(211) surfaces grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Badano, Giacomo; Ballet, Philippe; Zanatta, Jean-Paul; Baudry, Xavier; Million, Alain; Garland, James W.

    2006-01-01

    The effect of surface roughness on the ellipsometric response of semiconductor surfaces is investigated. CdTe(211)B layers were grown on Ge(211) by molecular beam epitaxy using less than optimal growth conditions to enhance the formation of surface roughness. Their optical properties, measured by rotating-compensator ellipsometry, showed small but significant sample-to-sample differences not explainable in terms of nanometer-scale roughness. A critical-point analysis established that the critical-point structure of the dielectric function was the same for all samples. This result suggested that the observed sample-to-sample variations were due to macroscopic roughness, which scatters off-specular light into the detector, thereby causing errors. We introduced tentative corrections for off-specular reflection that fitted the observed differences and thus supported the idea that off-specular reflection was responsible for the observed differences. These results were obtained using CdTe but are easily extensible to other rough opaque materials

  16. Nucleation of two-dimensional islands on Si (111) during high-temperature epitaxial growth

    Energy Technology Data Exchange (ETDEWEB)

    Sitnikov, S. V., E-mail: sitnikov@isp.nsc.ru; Kosolobov, S. S.; Latyshev, A. V. [Russian Academy of Sciences, Institute of Semiconductor Physics, Siberian Branch (Russian Federation)

    2017-02-15

    The process of two-dimensional island nucleation at the surface of ultra large Si (111) during hightemperature epitaxial growth is studied by in situ ultrahigh-vacuum reflection electron microscopy. The critical terrace size D{sub crit}, at which a two-dimensional island is nucleated in the center, is measured in the temperature range 900–1180°C at different silicon fluxes onto the surface. It is found that the parameter D{sub crit}{sup 2} is a power function of the frequency of island nucleation, with the exponent χ = 0.9 ± 0.05 in the entire temperature range under study. It is established that the kinetics of nucleus formation is defined by the diffusion of adsorbed silicon atoms at temperatures of up to 1180°C and the minimum critical nucleus size corresponds to 12 silicon atoms.

  17. Homo-epitaxial diamond film growth on ion implanted diamond substrates

    Energy Technology Data Exchange (ETDEWEB)

    Weiser, P.S.; Prawer, S.; Nugent, K.W.; Bettiol, A.A.; Kostidis, L.I.; Jamieson, D.N. [Melbourne Univ., Parkville, VIC (Australia). School of Physics

    1996-12-31

    The nucleation of CVD diamond is a complicated process, governed by many interrelated parameters. In the present work we attempt to elucidate the effect of strain on the growth of a homo-epitaxial CVD diamond. We have employed laterally confined high dose (MeV) Helium ion implantation to produce surface swelling of the substrate. The strain is enhanced by the lateral confinement of the implanted region to squares of 100 x 100 {mu}m{sup 2}. After ion implantation, micro-Raman spectroscopy was employed to map the surface strain. The substrates were then inserted into a CVD reactor and a CVD diamond film was grown upon them. Since the strained regions were laterally confined, it was then possible to monitor the effect of strain on diamond nucleation. The substrates were also analysed using Rutherford Backscattering Spectroscopy (RBS), Proton induced X-ray Emission (PIXE) and Ion Beam induced Luminescence (IBIL). 7 refs., 5 figs.

  18. Epitaxial growth and characterization of CoO/Fe(001) thin film layered structures

    International Nuclear Information System (INIS)

    Brambilla, A.; Sessi, P.; Cantoni, M.; Duo, L.; Finazzi, M.; Ciccacci, F.

    2008-01-01

    By means of X-ray photoemission spectroscopy and low energy electron diffraction, we show that it is possible to grow good quality thin epitaxial CoO films on Fe(001) substrates, through deposition in oxygen atmosphere. In particular, the composition and the structure of CoO(001)/Fe(001) bilayer systems and Fe(001)/CoO(001)/Fe(001) trilayer systems have been investigated by monitoring the evolution of the chemical interactions at the interfaces as a function of CoO thickness and growth temperature. We observe the presence of Fe oxides at the CoO/Fe interface and of a thin layer of metallic cobalt at the upper Fe/CoO interface of trilayer systems

  19. Homo-epitaxial diamond film growth on ion implanted diamond substrates

    Energy Technology Data Exchange (ETDEWEB)

    Weiser, P S; Prawer, S; Nugent, K W; Bettiol, A A; Kostidis, L I; Jamieson, D N [Melbourne Univ., Parkville, VIC (Australia). School of Physics

    1997-12-31

    The nucleation of CVD diamond is a complicated process, governed by many interrelated parameters. In the present work we attempt to elucidate the effect of strain on the growth of a homo-epitaxial CVD diamond. We have employed laterally confined high dose (MeV) Helium ion implantation to produce surface swelling of the substrate. The strain is enhanced by the lateral confinement of the implanted region to squares of 100 x 100 {mu}m{sup 2}. After ion implantation, micro-Raman spectroscopy was employed to map the surface strain. The substrates were then inserted into a CVD reactor and a CVD diamond film was grown upon them. Since the strained regions were laterally confined, it was then possible to monitor the effect of strain on diamond nucleation. The substrates were also analysed using Rutherford Backscattering Spectroscopy (RBS), Proton induced X-ray Emission (PIXE) and Ion Beam induced Luminescence (IBIL). 7 refs., 5 figs.

  20. Homo-epitaxial diamond film growth on ion implanted diamond substrates

    International Nuclear Information System (INIS)

    Weiser, P.S.; Prawer, S.; Nugent, K.W.; Bettiol, A.A.; Kostidis, L.I.; Jamieson, D.N.

    1996-01-01

    The nucleation of CVD diamond is a complicated process, governed by many interrelated parameters. In the present work we attempt to elucidate the effect of strain on the growth of a homo-epitaxial CVD diamond. We have employed laterally confined high dose (MeV) Helium ion implantation to produce surface swelling of the substrate. The strain is enhanced by the lateral confinement of the implanted region to squares of 100 x 100 μm 2 . After ion implantation, micro-Raman spectroscopy was employed to map the surface strain. The substrates were then inserted into a CVD reactor and a CVD diamond film was grown upon them. Since the strained regions were laterally confined, it was then possible to monitor the effect of strain on diamond nucleation. The substrates were also analysed using Rutherford Backscattering Spectroscopy (RBS), Proton induced X-ray Emission (PIXE) and Ion Beam induced Luminescence (IBIL). 7 refs., 5 figs

  1. Epitaxial Reactor Development for Growth of Silicon-on-Insulator Devices.

    Science.gov (United States)

    1987-04-01

    emision from substrate reflected from interface 40 Constructive interference condition 2tc= n X / 1 * Destrictive interference condition 2tD= (2n+1) X...combinations of growth conditions resulted in no oxide growth on the original silicon wafer. Growths occurred for Si:O molecular ratios higher than 1:1...growth rates occurred at 1050 0 C with water vapor at 1250 cc/min and silane at 50 cc/min. These results are shown in Table 6. The molecular ratio was 2:1

  2. Strain in epitaxial high-index Bi{sub 2}Se{sub 3}(221) films grown by molecular-beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Li, Bin [Physics Department, The University of Hong Kong, Pokfulam Road (Hong Kong); Chen, Weiguang [College of Physics and Electronic Engineering, Henan Normal University, Xinxiang, Henan 453007 (China); School of Physics and Electronic Engineering, Zhengzhou Normal University, Zhengzhou, Henan 450044 (China); Guo, Xin; Ho, Wingkin [Physics Department, The University of Hong Kong, Pokfulam Road (Hong Kong); Dai, Xianqi [College of Physics and Electronic Engineering, Henan Normal University, Xinxiang, Henan 453007 (China); School of Physics and Electronic Engineering, Zhengzhou Normal University, Zhengzhou, Henan 450044 (China); Jia, Jinfeng [Key Laboratory of Artificial Structures and Quantum Control (Ministry of Education), Collaborative Innovation Center of Advanced Microstructures, Department of Physics and Astronomy, Shanghai Jiaotong University, 800 Dongchuan Road, Shanghai 200240 (China); Xie, Maohai, E-mail: mhxie@hku.hk [Physics Department, The University of Hong Kong, Pokfulam Road (Hong Kong)

    2017-02-28

    Highlights: • High-index, off c-axis, Bi{sub 2}Se{sub 3} has been grown by molecular beam epitaxy on In{sub 2}Se{sub 3}. • A retarded strain relaxation process in such high-index Bi{sub 2}Se{sub 3} is observed, enabling experimentally probe strain effect on topological insulators. • It has been shown by calculation that the Dirac electrons participate in chemical bonding at the heterointerface. - Abstract: High-index Bi{sub 2}Se{sub 3}(221) film has been grown on In{sub 2}Se{sub 3}-buffered GaAs(001), in which a much retarded strain relaxation dynamics is recorded. The slow strain-relaxation process of in epitaxial Bi{sub 2}Se{sub 3}(221) can be attributed to the layered structure of Bi{sub 2}Se{sub 3} crystal, where the epifilm grown along [221] is like a pile of weakly-coupled quintuple layer slabs stacked side-by-side on substrate. Finally, we reveal strong chemical bonding at the interface of Bi{sub 2}Se{sub 3} and In{sub 2}Se{sub 3} by plotting differential charge contour calculated by first-principle method. This study points to the feasibility of achieving strained TIs for manipulating the properties of topological systems.

  3. Optimization of hetero-epitaxial growth for the threading dislocation density reduction of germanium epilayers

    Science.gov (United States)

    Chong, Haining; Wang, Zhewei; Chen, Chaonan; Xu, Zemin; Wu, Ke; Wu, Lan; Xu, Bo; Ye, Hui

    2018-04-01

    In order to suppress dislocation generation, we develop a "three-step growth" method to heteroepitaxy low dislocation density germanium (Ge) layers on silicon with the MBE process. The method is composed of 3 growth steps: low temperature (LT) seed layer, LT-HT intermediate layer as well as high temperature (HT) epilayer, successively. Threading dislocation density (TDD) of epitaxial Ge layers is measured as low as 1.4 × 106 cm-2 by optimizing the growth parameters. The results of Raman spectrum showed that the internal strain of heteroepitaxial Ge layers is tensile and homogeneous. During the growth of LT-HT intermediate layer, TDD reduction can be obtained by lowering the temperature ramping rate, and high rate deposition maintains smooth surface morphology in Ge epilayer. A mechanism based on thermodynamics is used to explain the TDD and surface morphological dependence on temperature ramping rate and deposition rate. Furthermore, we demonstrate that the Ge layer obtained can provide an excellent platform for III-V materials integrated on Si.

  4. Crystallography and Growth of Epitaxial Oxide Films for Fundamental Studies of Cathode Materials Used in Advanced Li-Ion Batteries

    Directory of Open Access Journals (Sweden)

    Leonid A. Bendersky

    2017-05-01

    Full Text Available Li-ion battery systems, synthesized as epitaxial thin films, can provide powerful insights into their electrochemical processes. Crystallographic analysis shows that many important cathode oxides have an underlying similarity: their structures can be considered as different ordering schemes of Li and transition metal ions within a pseudo-cubic sublattice of oxygen anions arranged in a face-center cubic (FCC fashion. This oxygen sublattice is compatible with SrTiO3 and similar perovskite oxides, thus perovskites can be used as supporting substrates for growing epitaxial cathode films. The predicted epitaxial growth and crystallographic relations were experimentally verified for different oxide films deposited by pulsed laser deposition (PLD on SrTiO3 or SrRuO3/SrTiO3 of different orientations. The results based on cross-sectional high-resolution TEM of the following films are presented in the paper: (a trigonal LiCoO2; (b orthorhombic LiMnO2; (c monoclinic Li2MnO3; (d compositionally-complex monoclinic Li1.2Mn0.55Ni0.15Co0.1O2. All results demonstrated the feasibility of epitaxial growth for these materials, with the growth following the predicted cube-on-cube orientation relationship between the cubic and pseudo-cubic oxygen sublattices of a substrate and a film, respectively.

  5. Fabrication and characterization of silicon nanowires by means of molecular beam epitaxy; Herstellung und Charakterisierung von Silizium-Nanodraehten mittels Molekularstrahlepitaxie

    Energy Technology Data Exchange (ETDEWEB)

    Schubert, Luise

    2007-06-19

    In this work, basic processes of silicon whisker growth were examined. For the first time, Si nanowhiskers were produced under UHV conditions by Molecular Beam Epitaxy (MBE) and characterized by different analysis methods afterwards. The existence of Au/Si droplets on a Si(111) substrate surface is a precondition of this growth method. Analyses of the temporal development of the Au/Si droplets during the whisker growth show a decrease of the number of small droplets resp. whiskers during the whisker growth with increasing growth time. This behaviour, i.e. the dissolution of smaller droplets/whiskers and the growth of larger ones in parallel can be explained by Ostwald ripenning. The diffusion-determined material transition of gold, which occurs during this process, is theoretically described by the Lifshitz-Slyozov-Wagner (LSW)-Theory. After this theory only whiskers grow which radii are larger than the critical radius. The whisker radii are temperature dependend whereas analogous whisker radii exist for identical growth times. Electron microscopy analysis show that all whiskers possess a hexagonal but no cylindrical habitus. The planes that form during the growth are crystallographic (111) planes. The growth of Si nanowhiskers under MBE conditions is determined by the Vapour Liquid Solid (VLS) mechanism and by surface diffusion of Si atoms. (orig.)

  6. Interfacial stability of CoSi2/Si structures grown by molecular beam epitaxy

    Science.gov (United States)

    George, T.; Fathauer, R. W.

    1992-01-01

    The stability of CoSi2/Si interfaces was examined in this study using columnar silicide structures grown on (111) Si substrates. In the first set of experiments, Co and Si were codeposited using MBE at 800 C and the resulting columnar silicide layer was capped by epitaxial Si. Deposition of Co on the surface of the Si capping layer at 800 C results in the growth of the buried silicide columns. The buried columns grow by subsurface diffusion of the deposited Co, suppressing the formation of surface islands of CoSi2. The column sidewalls appear to be less stable than the top and bottom interfaces, resulting in preferential lateral growth and ultimately in the coalescence of the columns to form a continuous buried CoSi2 layer. In the second set of experiments, annealing of a 250 nm-thick buried columnar layer at 1000 C under a 100 nm-thick Si capping layer results in the formation of a surface layer of CoSi2 with a reduction in the sizes of the CoSi2 columns. For a sample having a thicker Si capping layer the annealing leads to Ostwald ripening producing buried equiaxed columns. The high CoSi2/Si interfacial strain could provide the driving force for the observed behavior of the buried columns under high-temperature annealing.

  7. Plasma-assisted atomic layer epitaxial growth of aluminum nitride studied with real time grazing angle small angle x-ray scattering

    Energy Technology Data Exchange (ETDEWEB)

    Anderson, Virginia R.; Nepal, Neeraj; Johnson, Scooter D.; Robinson, Zachary R.; Nath, Anindya; Kozen, Alexander C.; Qadri, Syed B.; DeMasi, Alexander; Hite, Jennifer K.; Ludwig, Karl F.; Eddy, Charles R.

    2017-05-01

    Wide bandgap semiconducting nitrides have found wide-spread application as light emitting and laser diodes and are under investigation for further application in optoelectronics, photovoltaics, and efficient power switching technologies. Alloys of the binary semiconductors allow adjustments of the band gap, an important semiconductor material characteristic, which is 6.2 eV for aluminum nitride (AlN), 3.4 eV for gallium nitride, and 0.7 eV for (InN). Currently, the highest quality III-nitride films are deposited by metalorganic chemical vapor deposition and molecular beam epitaxy. Temperatures of 900 °C and higher are required to deposit high quality AlN. Research into depositing III-nitrides with atomic layer epitaxy (ALEp) is ongoing because it is a fabrication friendly technique allowing lower growth temperatures. Because it is a relatively new technique, there is insufficient understanding of the ALEp growth mechanism which will be essential to development of the process. Here, grazing incidence small angle x-ray scattering is employed to observe the evolving behavior of the surface morphology during growth of AlN by ALEp at temperatures from 360 to 480 °C. Increased temperatures of AlN resulted in lower impurities and relatively fewer features with short range correlations.

  8. Molecular beam epitaxy of alternating-strain ZnSe-based multilayer heterostructures for blue-green lasers

    International Nuclear Information System (INIS)

    Ivanov, S.V.; Toropov, A.A.; Sorokin, S.V.; Shubina, T.V.; Il'inskaya, N.D.; Lebedev, A.V.; Sedova, I.V.; Kop'ev, P.S.; Alferov, Zh.I.; Lugauer, H.-J.; Reuscher, G.; Keim, M.; Fischer, F.; Waag, A.; Landwehr, G.

    1998-01-01

    High-quality ZnSe-based heterostructures are grown by uninterrupted molecular beam epitaxy using the concept of strain compensation and alternating-strain multilayers. To verify the advantages of this technique, optically pumped ZnSSe/ZnCdSe laser structures containing short-period superlattices or multiple quantum wells have been grown and studied. A room-temperature injection laser diode with a BeZnSe/ZnSe superlattice waveguide is described

  9. Stress evolution of GaN/AlN heterostructure grown on 6H-SiC substrate by plasma assisted molecular beam epitaxy

    Science.gov (United States)

    Agrawal, M.; Ravikiran, L.; Dharmarasu, N.; Radhakrishnan, K.; Karthikeyan, G. S.; Zheng, Y.

    2017-01-01

    The stress evolution of GaN/AlN heterostructure grown on 6H-SiC substrate by plasma assisted molecular beam epitaxy (PA-MBE) has been studied. AlN nucleation layer and GaN layer were grown as a function of III/V ratio. GaN/AlN structure is found to form buried cracks when AlN is grown in the intermediate growth regime(III/V˜1)and GaN is grown under N-rich growth regime (III/VHEMT) heterostructure was demonstrated on 2-inch SiC that showed good two dimensional electron gas (2DEG) properties with a sheet resistance of 480 Ω/sq, mobility of 1280 cm2/V.s and sheet carrier density of 1×1013 cm-2.

  10. Epitaxial growth and properties of YBaCuO thin films

    International Nuclear Information System (INIS)

    Geerk, J.; Linker, G.; Meyer, O.

    1989-08-01

    The growth quality of YBaCuO thin films deposited by sputtering on different substrates (Al 2 O 3 , MgO, SrTiO 3 , Zr(Y)O 2 ) has been studied by X-ray diffraction and channeling experiments as a function of the deposition temperature. Besides the substrate orientation, the substrate temperature is the parameter determining whether films grow in c-, a-, (110) or mixed directions. Epitaxial growth correlates with high critical current values in the films of up to 5.5x10 6 A/cm 2 at 77 K. Ultrathin films with thicknesses down to 2 nm were grown revealing three-dimensional superconducting behaviour. Films on (100) SrTiO 3 of 9 nm thickness and below are partially strained indicating commensurate growth. From the analysis of the surface disorder 1 displaced Ba atom per Ba 2 Y row was obtained indicating that the disordered layer thickness is about 0.6 nm. Tunnel junctions fabricated on these films reveal gap-like structures near ±16 mV and ±30 mV. (orig.) [de

  11. Controlling the growth of epitaxial graphene on metalized diamond (111) surface

    International Nuclear Information System (INIS)

    Cooil, S. P.; Wells, J. W.; Hu, D.; Evans, D. A.; Niu, Y. R.; Zakharov, A. A.; Bianchi, M.

    2015-01-01

    The 2-dimensional transformation of the diamond (111) surface to graphene has been demonstrated using ultrathin Fe films that catalytically reduce the reaction temperature needed for the conversion of sp 3 to sp 2 carbon. An epitaxial system is formed, which involves the re-crystallization of carbon at the Fe/vacuum interface and that enables the controlled growth of monolayer and multilayer graphene films. In order to study the initial stages of single and multilayer graphene growth, real time monitoring of the system was preformed within a photoemission and low energy electron microscope. It was found that the initial graphene growth occurred at temperatures as low as 500 °C, whilst increasing the temperature to 560 °C was required to produce multi-layer graphene of high structural quality. Angle resolved photoelectron spectroscopy was used to study the electronic properties of the grown material, where a graphene-like energy momentum dispersion was observed. The Dirac point for the first layer is located at 2.5 eV below the Fermi level, indicating an n-type doping of the graphene due to substrate interactions, while that of the second graphene layer lies close to the Fermi level

  12. Amorphous inclusions during Ge and GeSn epitaxial growth via chemical vapor deposition

    Energy Technology Data Exchange (ETDEWEB)

    Gencarelli, F., E-mail: federica.gencarelli@imec.be [imec, Kapeldreef 75, 3001 Leuven (Belgium); Dept. of Metallurgy and Materials Engineering, KU Leuven, B-3001 Leuven (Belgium); Shimura, Y. [imec, Kapeldreef 75, 3001 Leuven (Belgium); Nuclear and Radiation Physics Section, KU Leuven, B-3001 Leuven (Belgium); Kumar, A. [imec, Kapeldreef 75, 3001 Leuven (Belgium); Nuclear and Radiation Physics Section, KU Leuven, B-3001 Leuven (Belgium); Vincent, B.; Moussa, A.; Vanhaeren, D.; Richard, O.; Bender, H. [imec, Kapeldreef 75, 3001 Leuven (Belgium); Vandervorst, W. [imec, Kapeldreef 75, 3001 Leuven (Belgium); Nuclear and Radiation Physics Section, KU Leuven, B-3001 Leuven (Belgium); Caymax, M.; Loo, R. [imec, Kapeldreef 75, 3001 Leuven (Belgium); Heyns, M. [imec, Kapeldreef 75, 3001 Leuven (Belgium); Dept. of Metallurgy and Materials Engineering, KU Leuven, B-3001 Leuven (Belgium)

    2015-09-01

    In this work, we discuss the characteristics of particular island-type features with an amorphous core that are developed during the low temperature epitaxial growth of Ge and GeSn layers by means of chemical vapor deposition with Ge{sub 2}H{sub 6}. Although further investigations are needed to unambiguously identify the origin of these features, we suggest that they are originated by the formation of clusters of H and/or contaminants atoms during growth. These would initially cause the formation of pits with crystalline rough facets over them, resulting in ring-shaped islands. Then, when an excess surface energy is overcome, an amorphous phase would nucleate inside the pits and fill them. Reducing the pressure and/or increasing the growth temperature can be effective ways to prevent the formation of these features, likely due to a reduction of the surface passivation from H and/or contaminant atoms. - Highlights: • Island features with amorphous cores develop during low T Ge(Sn) CVD with Ge{sub 2}H{sub 6.} • These features are thoroughly characterized in order to understand their origin. • A model is proposed to describe the possible evolution of these features. • Lower pressures and/or higher temperatures avoid the formation of these features.

  13. Electron-diffraction and spectroscopical characterisation of ultrathin ZnS films grown by molecular beam epitaxy on GaP(0 0 1)

    International Nuclear Information System (INIS)

    Zhang, L.; Szargan, R.; Chasse, T.

    2004-01-01

    ZnS films were grown by molecular beam epitaxy employing a single compound effusion cell on GaP(0 0 1) substrate at different temperatures, and characterised by means of low energy electron diffraction, X-ray and ultra-violet photoelectron spectroscopy, angle-resolved ultra-violet photoelectron spectroscopy and X-ray emission spectroscopy. The GaP(0 0 1) substrate exhibits a (4x2) reconstruction after Ar ion sputtering and annealing at 370 deg. C. Crystal quality of the ZnS films depends on both film thickness and growth temperature. Thinner films grown at higher temperatures and thicker films grown at lower temperatures have better crystal quality. The layer-by-layer growth mode of the ZnS films at lower (25, 80 and 100 deg. C) temperatures changes to layer-by-layer-plus-island mode at higher temperatures (120, 150 and 180 deg. C). A chemical reaction takes place and is confined to the interface. The valence band offset of the ZnS-GaP heterojunction was determined to be 0.8±0.1 eV. Sulphur L 2,3 emission spectra of ZnS powder raw material and the epitaxial ZnS films display the same features, regardless of the existence of the Ga-S bonding in the film samples

  14. Defect properties of InGaAsN layers grown as sub-monolayer digital alloys by molecular beam epitaxy

    Science.gov (United States)

    Baranov, Artem I.; Gudovskikh, Alexander S.; Kudryashov, Dmitry A.; Lazarenko, Alexandra A.; Morozov, Ivan A.; Mozharov, Alexey M.; Nikitina, Ekaterina V.; Pirogov, Evgeny V.; Sobolev, Maxim S.; Zelentsov, Kirill S.; Egorov, Anton Yu.; Darga, Arouna; Le Gall, Sylvain; Kleider, Jean-Paul

    2018-04-01

    The defect properties of InGaAsN dilute nitrides grown as sub-monolayer digital alloys (SDAs) by molecular beam epitaxy for photovoltaic application were studied by space charge capacitance spectroscopy. Alloys of i-InGaAsN (Eg = 1.03 eV) were lattice-matched grown on GaAs wafers as a superlattice of InAs/GaAsN with one monolayer of InAs (solar cells. Low p-type background doping was demonstrated at room temperature in samples with InGaAsN layers 900 nm and 1200 nm thick (less 1 × 1015 cm-3). According to admittance spectroscopy and deep-level transient spectroscopy measurements, the SDA approach leads to defect-free growth up to a thickness of 900 nm. An increase in thickness to 1200 nm leads to the formation of non-radiative recombination centers with an activation energy of 0.5 eV (NT = 8.4 × 1014 cm-3) and a shallow defect level at 0.20 eV. The last one leads to the appearance of additional doping, but its concentration is low (NT = 5 × 1014 cm-3) so it does not affect the photoelectric properties. However, further increase in thickness to 1600 nm, leads to significant growth of its concentration to (3-5) × 1015 cm-3, while the concentration of deep levels becomes 1.3 × 1015 cm-3. Therefore, additional free charge carriers appearing due to ionization of the shallow level change the band diagram from p-i-n to p-n junction at room temperature. It leads to a drop of the external quantum efficiency due to the effect of pulling electric field decrease in the p-n junction and an increased number of non-radiative recombination centers that negatively impact lifetimes in InGaAsN.

  15. Positron annihilation studies of defects in molecular beam epitaxy grown III-V layers

    International Nuclear Information System (INIS)

    Umlor, M.T.; Keeble, D.J.; Cooke, P.W.

    1994-01-01

    A summary of recent positron annihilation experiments on molecular beam epitaxy (MBE) grown III-V layers is Presented. Variable energy positron beam measurements on Al 0.32 Ga 0.68 As undoped and Si doped have been completed. Positron trapping at a open volume defect in Al 0.32 Ga 0.68 :Si for temperatures from 300 to 25 K in the dark was observed. The positron trap was lost after 1.3 eV illumination at 25K. These results indicate an open volume defect is associated with the local structure of the deep donor state of the DX center. Stability of MBE GaAs to thermal annealing war, investigated over the temperature range of 230 to 700 degrees C, Proximity wafer furnace anneals in flowing argon were used, Samples grown above 450 degrees C were shown to be stable but for sample below this temperature an anneal induced vacancy related defect was produced for anneals between 400 and 500 degrees C. The nature of the defect was shown to be different for material grown at 350 and 230 degrees C. Activation energies of 2.5 eV to 2.3 eV were obtained from isochronal anneal experiments for samples grown at 350 and 230 degrees C, respectively

  16. Polarized infrared reflectance study of free standing cubic GaN grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Lee, S.C.; Ng, S.S.; Hassan, H. Abu; Hassan, Z.; Zainal, N.; Novikov, S.V.; Foxon, C.T.; Kent, A.J.

    2014-01-01

    Optical properties of free standing cubic gallium nitride grown by molecular beam epitaxy system are investigated by a polarized infrared (IR) reflectance technique. A strong reststrahlen band, which reveals the bulk-like optical phonon frequencies, is observed. Meanwhile, continuous oscillation fringes, which indicate the sample consists of two homogeneous layers with different dielectric constants, are observed in the non-reststrahlen region. By obtaining the first derivative of polarized IR reflectance spectra measured at higher angles of incidence, extra phonon resonances are identified at the edges of the reststrahlen band. The observations are verified with the theoretical results simulated based on a multi-oscillator model. - Highlights: • First time experimental studies of IR optical phonons in bulk like, cubic GaN layer. • Detection of extra phonon modes of cubic GaN by polarized IR reflectance technique. • Revelation of IR multiphonon modes of cubic GaN by first derivative numerical method. • Observation of multiphonon modes requires very high angle of incidence. • Resonance splitting effect induced by third phonon mode is a qualitative indicator

  17. Ellipsometric study of GaN/AIN/Si(111) heterostructures grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Nabi, M. A. U.; Ashfaq, A.; Arshad, M. I.; Ali, A.; Mahmood, K.; Hasan, M. A.; Asghar, M.

    2013-01-01

    GaN and related structures attracted a great interest in the recent years for electronic and optoelectronic applications due to their promising properties. GaN is grown popularly on foreign substrates like sapphire and SiC. However, silicon due to its favourable properties attended the great attention of material scientists and researchers to utilize as substrate for heteroepitaxy of GaN based structures and devices. Silicon substrates are low cost, available in large diameters and have well characterized thermal and electrical properties. In this study, GaN/AlN/Si(111) heterostructures were grown by molecular beam epitaxy. We performed x-ray diffraction spectroscopy and spectroscopic ellipsometry on these samples to study their structural and optical properties. XRD measurements performed on these samples revealed the presence of high quality GaN films as well as the presence of AlN buffer layer with the following miller indices: GaN (002), GaN (004), GaN (006) and GaN (110) along with Si peak of phase (111). The ellipsometric data obtained were used to characterize the GaN/Si samples as a function of film thickness. Refractive index, extinction coefficient and dielectric constant were calculated by the measured data. (author)

  18. Effects of magnesium contents in ZnMgO ternary alloys grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Hu, Sheng-Yao, E-mail: shenghu2729@yahoo.com [Department of Digital Technology Design, Tungfang Design Institute, Hunei, Kaohsiung 82941, Taiwan (China); Chou, Wu-Ching [Department of Electrophysics, National Chiao Tung University, Hsinchu 30010, Taiwan (China); Weng, Yu-Hsiang [Department of Electrical Engineering, National Taiwan Ocean University, Keelung 20224, Taiwan (China)

    2015-07-05

    Highlights: • ZnMgO alloys with different Mg contents have been produced by MBE. • Optical and structural properties have been measured and investigated. • Stress is tensile and is increased as the increasing of Mg contents. • The asymmetric behavior of the Raman mode was influenced due to the Mg contents. - Abstract: Ternary alloys of ZnMgO samples with different magnesium contents have been grown by molecular beam epitaxy on the sapphire substrates. Room temperature photoluminescence energy of ZnMgO shifted as high as 3.677 eV by increasing Mg contents corresponding to the higher Urbach average localization energy which indicates more randomness in the alloys with higher Mg contents. XRD results are also verified that the c-axis length decreases as the increasing Mg contents linking to the increased tensile stress produced by the Mg atoms. Raman spectra analyzed by the spatial correlation model to describe that the linewidth Γ is decreased but the correlation length L is increased as the increasing of Mg contents.

  19. Effects of magnesium contents in ZnMgO ternary alloys grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Hu, Sheng-Yao; Chou, Wu-Ching; Weng, Yu-Hsiang

    2015-01-01

    Highlights: • ZnMgO alloys with different Mg contents have been produced by MBE. • Optical and structural properties have been measured and investigated. • Stress is tensile and is increased as the increasing of Mg contents. • The asymmetric behavior of the Raman mode was influenced due to the Mg contents. - Abstract: Ternary alloys of ZnMgO samples with different magnesium contents have been grown by molecular beam epitaxy on the sapphire substrates. Room temperature photoluminescence energy of ZnMgO shifted as high as 3.677 eV by increasing Mg contents corresponding to the higher Urbach average localization energy which indicates more randomness in the alloys with higher Mg contents. XRD results are also verified that the c-axis length decreases as the increasing Mg contents linking to the increased tensile stress produced by the Mg atoms. Raman spectra analyzed by the spatial correlation model to describe that the linewidth Γ is decreased but the correlation length L is increased as the increasing of Mg contents

  20. Redundant Sb condensation on GaSb epilayers grown by molecular beam epitaxy during cooling procedure

    International Nuclear Information System (INIS)

    Arpapay, B.; Şahin, S.; Arıkan, B.; Serincan, U.

    2014-01-01

    The effect of four different cooling receipts on the surface morphologies of unintentionally-doped GaSb epilayers on GaSb (100) substrates grown by molecular beam epitaxy is reported. Those receipts include three different Sb beam equivalent pressure (BEP) levels and two different termination temperatures. Surface morphologies of epilayers were examined by wet etching, surface profiler, atomic force microscopy, scanning electron microscopy and Raman spectroscopy. The results demonstrate that during the cooling period, a Sb BEP of 4.00 × 10 −4 Pa at a termination temperature of 400 °C induces a smooth surface without Sb condensation whereas same Sb BEP at a termination temperature of 350 °C forms a 300 nm thick Sb layer on the surface. In addition, it is revealed that by applying a wet etching procedure and using a surface profiler it is possible to identify this condensed layer from the two-sloped feature of mesa profile. - Highlights: • Sb beam flux termination temperature is crucial for redundant Sb condensation. • Sb beam flux level has a role on the thickness of redundant condensed Sb layer. • Redundant Sb layer thickness can be measured by two-sloped mesa structure

  1. Polycrystalline indium phosphide on silicon by indium assisted growth in hydride vapor phase epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Metaferia, Wondwosen; Sun, Yan-Ting, E-mail: yasun@kth.se; Lourdudoss, Sebastian [Laboratory of Semiconductor Materials, Department of Materials and Nano Physics, KTH—Royal Institute of Technology, Electrum 229, 164 40 Kista (Sweden); Pietralunga, Silvia M. [CNR-Institute for Photonics and Nanotechnologies, P. Leonardo da Vinci, 32 20133 Milano (Italy); Zani, Maurizio; Tagliaferri, Alberto [Department of Physics Politecnico di Milano, P. Leonardo da Vinci, 32 20133 Milano (Italy)

    2014-07-21

    Polycrystalline InP was grown on Si(001) and Si(111) substrates by using indium (In) metal as a starting material in hydride vapor phase epitaxy (HVPE) reactor. In metal was deposited on silicon substrates by thermal evaporation technique. The deposited In resulted in islands of different size and was found to be polycrystalline in nature. Different growth experiments of growing InP were performed, and the growth mechanism was investigated. Atomic force microscopy and scanning electron microscopy for morphological investigation, Scanning Auger microscopy for surface and compositional analyses, powder X-ray diffraction for crystallinity, and micro photoluminescence for optical quality assessment were conducted. It is shown that the growth starts first by phosphidisation of the In islands to InP followed by subsequent selective deposition of InP in HVPE regardless of the Si substrate orientation. Polycrystalline InP of large grain size is achieved and the growth rate as high as 21 μm/h is obtained on both substrates. Sulfur doping of the polycrystalline InP was investigated by growing alternating layers of sulfur doped and unintentionally doped InP for equal interval of time. These layers could be delineated by stain etching showing that enough amount of sulfur can be incorporated. Grains of large lateral dimension up to 3 μm polycrystalline InP on Si with good morphological and optical quality is obtained. The process is generic and it can also be applied for the growth of other polycrystalline III–V semiconductor layers on low cost and flexible substrates for solar cell applications.

  2. Growth and characterization of epitaxial anatase TiO2(001) on SrTiO3-buffered Si(001) using atomic layer deposition

    International Nuclear Information System (INIS)

    McDaniel, M.D.; Posadas, A.; Wang, T.; Demkov, A.A.; Ekerdt, J.G.

    2012-01-01

    Epitaxial anatase titanium dioxide (TiO 2 ) films have been grown by atomic layer deposition (ALD) on Si(001) substrates using a strontium titanate (STO) buffer layer grown by molecular beam epitaxy (MBE) to serve as a surface template. The growth of TiO 2 was achieved using titanium isopropoxide and water as the co-reactants at a substrate temperature of 225–250 °C. To preserve the quality of the MBE-grown STO, the samples were transferred in-situ from the MBE chamber to the ALD chamber. After ALD growth, the samples were annealed in-situ at 600 °C in vacuum (10 −7 Pa) for 1–2 h. Reflection high-energy electron diffraction was performed during the MBE growth of STO on Si(001), as well as after deposition of TiO 2 by ALD. The ALD films were shown to be highly ordered with the substrate. At least four unit cells of STO must be present to create a stable template on the Si(001) substrate for epitaxial anatase TiO 2 growth. X-ray diffraction revealed that the TiO 2 films were anatase with only the (004) reflection present at 2θ = 38.2°, indicating that the c-axis is slightly reduced from that of anatase powder (2θ = 37.9°). Anatase TiO 2 films up to 100 nm thick have been grown that remain highly ordered in the (001) direction on STO-buffered Si(001) substrates. - Highlights: ► Epitaxial anatase films are grown by atomic layer deposition (ALD) on Si(001). ► Four unit cells of SrTiO 3 on silicon create a stable template for ALD. ► TiO 2 thin films have a compressed c-axis and an expanded a-axis. ► Up to 100 nm thick TiO 2 films remain highly ordered in the (001) direction.

  3. Molecular beam epitaxy of large-area SnSe2 with monolayer thickness fluctuation

    Science.gov (United States)

    Park, Young Woon; Jerng, Sahng-Kyoon; Jeon, Jae Ho; Roy, Sanjib Baran; Akbar, Kamran; Kim, Jeong; Sim, Yumin; Seong, Maeng-Je; Kim, Jung Hwa; Lee, Zonghoon; Kim, Minju; Yi, Yeonjin; Kim, Jinwoo; Noh, Do Young; Chun, Seung-Hyun

    2017-03-01

    The interest in layered materials is largely based on the expectation that they will be beneficial for a variety of applications, from low-power-consuming, wearable electronics to energy harvesting. However, the properties of layered materials are highly dependent on thickness, and the difficulty of controlling thickness over a large area has been a bottleneck for commercial applications. Here, we report layer-by-layer growth of SnSe2, a layered semiconducting material, via van der Waals epitaxy. The films were fabricated on insulating mica substrates with substrate temperatures in the range of 210 °C-370 °C. The surface consists of a mixture of N and (N ± 1) layers, showing that the thickness of the film can be defined with monolayer accuracy (±0.6 nm). High-resolution transmission electron microscopy reveals a polycrystalline film with a grain size of ˜100 nm and clear Moiré patterns from overlapped grains with similar thickness. We also report field effect mobility values of 3.7 cm2 V-1 s-1 and 6.7 cm2 V-1 s-1 for 11 and 22 nm thick SnSe2, respectively. SnSe2 films with customizable thickness can provide valuable platforms for industry and academic researchers to fully exploit the potential of layered materials.

  4. Thickness and growth-condition dependence of in-situ mobility and carrier density of epitaxial thin-film Bi2Se3

    International Nuclear Information System (INIS)

    Hellerstedt, Jack; Fuhrer, Michael S.; Edmonds, Mark T.; Zheng, C. X.; Chen, J. H.; Cullen, William G.

    2014-01-01

    Bismuth selenide Bi 2 Se 3 was grown by molecular beam epitaxy, while carrier density and mobility were measured directly in situ as a function of film thickness. Carrier density shows high interface n-doping (1.5 × 10 13  cm −2 ) at the onset of film conduction and bulk dopant density of ∼5 × 10 11  cm −2 per quintuple-layer unit, roughly independent of growth temperature profile. Mobility depends more strongly on the growth temperature and is related to the crystalline quality of the samples quantified by ex-situ atomic force microscopy measurements. These results indicate that Bi 2 Se 3 as prepared by widely employed parameters is n-doped before exposure to atmosphere, the doping is largely interfacial in origin, and dopants are not the limiting disorder in present Bi 2 Se 3 films.

  5. Epitaxial growth of sexi-thiophene and para-hexaphenyl and its implications for the fabrication of self-assembled lasing nano-fibres

    International Nuclear Information System (INIS)

    Simbrunner, Clemens

    2013-01-01

    Over the last few years, epitaxially grown self-assembled organic nano-structures became of increasing interest due to their high potential for implementation within opto-electronic devices. Exemplarily, the epitaxial growth of the rod-like molecules para-hexaphenyl (p-6P) and α-sexi-thiophene (6T) is discussed within this review. Both molecules tend to crystallize in highly asymmetric elongated entities which are also called nano-fibres. It is demonstrated that the obtained needle orientations and morphologies result from a complex interplay between various parameters e.g. substrate surface symmetry, molecular adsorption, crystal structure and contact plane. The interplay and its implications on the fabrication of self-assembled waveguiding nano-fibres and optical resonator structures are discussed and substantiated by a comparison with the reported literature. In further consequence, it is demonstrated that a precise control on the molecular adsorption geometry and the crystal contact plane represents a fundamental key parameter for the fabrication of self-assembled nano-fibres. As both parameters are basically determined by the chosen molecule–substrate material couple, the possible spectrum of molecular building blocks for the fabrication of waveguiding and lasing nano-structures can be predicted by the discussed growth model. A possible expansion of this common valid concept is presented by the utilization of organic–organic heteroepitaxy. Based on the reported p-6P/6T heterostructures which have been fabricated on various substrate surfaces, it is substantiated that the fabrication of organic–organic interfaces can be effectively used to gain control on the molecular adsorption geometry. As the proposed strategy still lacks a precise control of the obtained crystal contact plane, further strategies are discussed which potentially lead to a controlled fabrication of opto-electronic devices based on self-assembled organic nano-structures. (invited review)

  6. Multiple growths of epitaxial lift-off solar cells from a single InP substrate

    International Nuclear Information System (INIS)

    Lee, Kyusang; Shiu, Kuen-Ting; Zimmerman, Jeramy D.; Forrest, Stephen R.; Renshaw, Christopher K.

    2010-01-01

    We demonstrate multiple growths of flexible, thin-film indium tin oxide-InP Schottky-barrier solar cells on a single InP wafer via epitaxial lift-off (ELO). Layers that protect the InP parent wafer surface during the ELO process are subsequently removed by selective wet-chemical etching, with the active solar cell layers transferred to a thin, flexible plastic host substrate by cold welding at room temperature. The first- and second-growth solar cells exhibit no performance degradation under simulated Atmospheric Mass 1.5 Global (AM 1.5G) illumination, and have a power conversion efficiency of η p =14.4±0.4% and η p =14.8±0.2%, respectively. The current-voltage characteristics for the solar cells and atomic force microscope images of the substrate indicate that the parent wafer is undamaged, and is suitable for reuse after ELO and the protection-layer removal processes. X-ray photoelectron spectroscopy, reflection high-energy electron diffraction observation, and three-dimensional surface profiling show a surface that is comparable or improved to the original epiready wafer following ELO. Wafer reuse over multiple cycles suggests that high-efficiency; single-crystal thin-film solar cells may provide a practical path to low-cost solar-to-electrical energy conversion.

  7. MBE growth and design of II-VI heterostructures for epitaxial lift-off

    Energy Technology Data Exchange (ETDEWEB)

    Davidson, Ian A.; Vallance, Erin C.; Prior, Kevin A. [School of Engineering and Physical Science, Heriot-Watt University, Edinburgh (United Kingdom); Moug, Richard T.; Tamargo, Maria C. [Department of Chemistry, City College of New York, New York, NY (United States)

    2012-08-15

    Epitaxial lift-off (ELO) is a post-growth process that allows the active part of a semiconductor structure to be transferred from its growth substrate to a new one. This is a well established technique for III-V semiconductors, and has previously been demonstrated for ZnSe-based alloys grown on GaAs using a metastable MgS sacrificial layer, taking advantage of the huge difference in etch rates of MgS and ZnSe. We report here the first successful extension of this process to II-VI layers grown on InP by using a MgSe sacrificial layer. By using the correct etching conditions, MgSe has been found to work effectively as a sacrificial layer. 5 x 5 mm{sup 2} square pieces of material can be lifted and deposited on glass substrates without any deterioration in the structural or optical properties; as confirmed by optical microscopy and photoluminescence (PL) measurements. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  8. Point defect balance in epitaxial GaSb

    International Nuclear Information System (INIS)

    Segercrantz, N.; Slotte, J.; Makkonen, I.; Kujala, J.; Tuomisto, F.; Song, Y.; Wang, S.

    2014-01-01

    Positron annihilation spectroscopy in both conventional and coincidence Doppler broadening mode is used for studying the effect of growth conditions on the point defect balance in GaSb:Bi epitaxial layers grown by molecular beam epitaxy. Positron annihilation characteristics in GaSb are also calculated using density functional theory and compared to experimental results. We conclude that while the main positron trapping defect in bulk samples is the Ga antisite, the Ga vacancy is the most prominent trap in the samples grown by molecular beam epitaxy. The results suggest that the p–type conductivity is caused by different defects in GaSb grown with different methods.

  9. Critical thickness and strain relaxation in molecular beam epitaxy-grown SrTiO3 films

    International Nuclear Information System (INIS)

    Wang, Tianqi; Ganguly, Koustav; Marshall, Patrick; Xu, Peng; Jalan, Bharat

    2013-01-01

    We report on the study of the critical thickness and the strain relaxation in epitaxial SrTiO 3 film grown on (La 0.3 Sr 0.7 )(Al 0.65 Ta 0.35 )O 3 (001) (LSAT) substrate using the hybrid molecular beam epitaxy approach. No change in the film's lattice parameter (both the in-plane and the out-of-plane) was observed up to a film thickness of 180 nm, which is in sharp contrast to the theoretical critical thickness of ∼12 nm calculated using the equilibrium theory of strain relaxation. For film thicknesses greater than 180 nm, the out-of-plane lattice parameter was found to decrease hyperbolically in an excellent agreement with the relaxation via forming misfit dislocations. Possible mechanisms are discussed by which the elastic strain energy can be accommodated prior to forming misfit dislocations leading to such anomalously large critical thickness

  10. GaN Schottky diodes with single-crystal aluminum barriers grown by plasma-assisted molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Tseng, H. Y.; Yang, W. C.; Lee, P. Y.; Lin, C. W.; Cheng, Kai-Yuan; Hsieh, K. C.; Cheng, K. Y., E-mail: kycheng@ee.nthu.edu.tw [Department of Electrical Engineering, National Tsing Hua University, Hsinchu 30013, Taiwan (China); Hsu, C.-H. [Division of Scientific Research, National Synchrotron Radiation Research Center, Hsinchu 30076, Taiwan (China)

    2016-08-22

    GaN-based Schottky barrier diodes (SBDs) with single-crystal Al barriers grown by plasma-assisted molecular beam epitaxy are fabricated. Examined using in-situ reflection high-energy electron diffractions, ex-situ high-resolution x-ray diffractions, and high-resolution transmission electron microscopy, it is determined that epitaxial Al grows with its [111] axis coincident with the [0001] axis of the GaN substrate without rotation. In fabricated SBDs, a 0.2 V barrier height enhancement and 2 orders of magnitude reduction in leakage current are observed in single crystal Al/GaN SBDs compared to conventional thermal deposited Al/GaN SBDs. The strain induced piezoelectric field is determined to be the major source of the observed device performance enhancements.

  11. Optical and electrical properties of semiconducting BaSi2 thin films on Si substrates grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Morita, K.; Inomata, Y.; Suemasu, T.

    2006-01-01

    The electrical properties and optical absorption (OA) spectra of undoped BaSi 2 films grown by molecular beam epitaxy were investigated The electron density and mobility of BaSi 2 grown epitaxially on Si(111) were 5 x 10 15 cm -3 and 820 cm 2 /V.s at room temperature, respectively. The conduction-band discontinuity at the BaSi 2 /Si heterojunction was estimated to be 0.7 eV from the current-voltage characteristics of n-BaSi 2 /n-Si isotype diodes. OA spectra were measured on polycrystalline BaSi 2 films grown on transparent fused silica substrates with predeposited polycrystalline Si layer. The indirect absorption edge was derived to be 1.3 eV, and the optical absorption coefficient reached 10 5 cm -1 at 1.5 eV

  12. Epitaxial growth of YBa2Cu3O7-δ thin films on LiNbO3 substrates

    International Nuclear Information System (INIS)

    Lee, S.G.; Koren, G.; Gupta, A.; Segmuller, A.; Chi, C.C.

    1989-01-01

    In situ epitaxial growth of YBa 2 Cu 3 O 7-δ thin films on Y-cut LiNbO 3 substrates using a standard laser ablation technique is reported. Resistance of the films shows a normal metallic behavior and a very sharp ( c (R=0) of 92 K. High critical current density of J c (77 K)=2x10 5 A/cm 2 is observed, which is in accordance with epitaxial growth. Film orientation observed from x-ray diffraction spectra indicates that the c axis is normal to the substrate plane and the a axis is at 45 degree to the [11.0] direction of the hexagonal lattice of the substrate with two domains in mirror image to the (110) plane

  13. Chirality-Controlled Growth of Single-Wall Carbon Nanotubes Using Vapor Phase Epitaxy: Mechanistic Understanding and Scalable Production

    Science.gov (United States)

    2016-09-15

    AFRL-AFOSR-VA-TR-2016-0319 Chirality -Controlled Growth of Single-Wall Carbon Nanotubes Using Vapor Phase Epitaxy: Mechanistic Understanding and...TELEPHONE NUMBER (Include area code) DISTRIBUTION A: Distribution approved for public release. 15-06-2016 final Jun 2014 - Jun 2016 Chirality ...for Public Release; Distribution is Unlimited. In this report, we present our efforts in establishing a novel and effective approach for chirality

  14. Study on initial stage of hetero-epitaxial growth by glancing angle scattering of fast ions from surfaces

    International Nuclear Information System (INIS)

    Fujii, Yoshikazu; Toba, Kazuaki; Narumi, Kazumasa; Kimura, Kenji; Mannami, Michihiko

    1993-01-01

    Initial stages of epitaxial growth of lead chalcogenides on the (100) surface of SnTe under UHV conditions are studied from the angular distribution of scattered ions at glancing angle incidence of 0.7 MeV He ions on the growing surfaces. Real time measurement of the angular distribution is performed during the growth. Anomalous broadening of the angular distribution is observed at the initial stage of the growth. The broadening is attributed to the surface wrinkles induced by a square network of misfit edge dislocations. (author)

  15. Liquid Phase Epitaxial Growth of Al-doped f-SiC for White Light-Emitting Diodes

    DEFF Research Database (Denmark)

    Tang, Kai; Ma, Xiang; can der Eijk, Casper

    efficiency, better light quality and longer lifespan, compared to the current yellow phosphor based white LEDs.Liquid phase epitaxy technology can yield a high crystalline quality in terms of structural perfection owing to the fact that it is a near equilibrium crystalline growth process. In addition....... The experimental results are presented and discussed. Since operational temperature of LPE growth is much lower than that currently used in physical vapour transport (PVT) process, it is expected to save the energy consumption for SiC crystal growth....

  16. Comprehensive modeling of solid phase epitaxial growth using Lattice Kinetic Monte Carlo

    International Nuclear Information System (INIS)

    Martin-Bragado, Ignacio

    2013-01-01

    Damage evolution of irradiated silicon is, and has been, a topic of interest for the last decades for its applications to the semiconductor industry. In particular, sometimes, the damage is heavy enough to collapse the lattice and to locally amorphize the silicon, while in other cases amorphization is introduced explicitly to improve other implanted profiles. Subsequent annealing of the implanted samples heals the amorphized regions through Solid Phase Epitaxial Regrowth (SPER). SPER is a complicated process. It is anisotropic, it generates defects in the recrystallized silicon, it has a different amorphous/crystalline (A/C) roughness for each orientation, leaving pits in Si(1 1 0), and in Si(1 1 1) it produces two modes of recrystallization with different rates. The recently developed code MMonCa has been used to introduce a physically-based comprehensive model using Lattice Kinetic Monte Carlo that explains all the above singularities of silicon SPER. The model operates by having, as building blocks, the silicon lattice microconfigurations and their four twins. It detects the local configurations, assigns microscopical growth rates, and reconstructs the positions of the lattice locally with one of those building blocks. The overall results reproduce the (a) anisotropy as a result of the different growth rates, (b) localization of SPER induced defects, (c) roughness trends of the A/C interface, (d) pits on Si(1 1 0) regrown surfaces, and (e) bimodal Si(1 1 1) growth. It also provides physical insights of the nature and shape of deposited defects and how they assist in the occurrence of all the above effects

  17. Formation and properties of epitaxial CdSe, ZnSe quantum dots. Conventional molecular beam epitaxy and related techniques

    International Nuclear Information System (INIS)

    Mahapatra, Suddhasatta

    2008-01-01

    This thesis systematically investigates three such alternative approaches, along with conventional MBE, with emphasis on the formation-mechanism of QDs, and optimization of their morphological and optical attributes. it is shown here that no distinct 3D islands are formed in MBE growth of CdSe on ZnSe. While CdSe heteroepitaxy occurs in the multilayer-mode at T G =300 C, a reentrant recovery of the layer-by-layer mode is reported in this thesis, for growth at T G D =230 C). The process steps of the third variant technique, developed in course of this work, are very similar to those of the previous one-the only alteration being the substitution of selenium with tellurium as the cap-forming-material. (orig.)

  18. Investigation of CuGaSe2/CuInSe2 double heterojunction interfaces grown by molecular beam epitaxy

    Directory of Open Access Journals (Sweden)

    Sathiabama Thiru

    2015-02-01

    Full Text Available In-situ reflection high-energy electron diffraction (RHEED observation and X-ray diffraction measurements were performed on heterojunction interfaces of CuGaSe2/CnInSe2/CuGaSe2 grown on GaAs (001 using migration-enhanced epitaxy. The streaky RHEED pattern and persistent RHEED intensity oscillations caused by the alternate deposition of migration-enhanced epitaxy sequence are observed and the growths of smooth surfaces are confirmed. RHEED observation results also confirmed constituent material interdiffusion at the heterointerface. Cross-sectional transmission electron microscopy showed a flat and abrupt heterointerface when the substrate temperature is as low as 400 °C. These have been confirmed even by X-ray diffraction and photoluminescence measurements.

  19. Polarized Emission from Conjugated Polymer Chains Aligned by Epitaxial Growth during Off-Center Spin-Coating

    Directory of Open Access Journals (Sweden)

    Takuya Anzai

    2017-01-01

    Full Text Available Due to their macromolecular nature, conjugated polymers can be relatively easily aligned by applying a variety of processes resulting in either elongation or ordering of their conjugated backbones. Processes that induce chain alignment include electrospinning, mechanical rubbing, epitaxial growth, and nanoconfinement and unidirectional deposition techniques such as off-center spin-coating. In this study, we compare these deposition techniques by applying them to a green-emitting conjugated polymer material that exhibits liquid crystalline phase behavior. Our study reveals that while methods such as electrospinning and mechanical rubbing can be useful to locally generate polymer chain alignment, the combination of epitaxial growth using 1,3,5-trichlorobenzene as crystallizing agent with off-center spin-coating results in the formation of anisotropic nanofiber-like structures with enhanced crystallinity degree and polarized light-emission properties. The unidirectional epitaxial growth was also applied to a red-emitting polymer that exhibits polarization ratios up to 4.1. Our results emphasize that this simple solution formulation and process can be used for the fabrication of polarized thin films of a variety of conjugated polymers with potential applications in the advanced display technologies or analytical equipment fields.

  20. Low temperature p-type doping of (Al)GaN layers using ammonia molecular beam epitaxy for InGaN laser diodes

    Science.gov (United States)

    Malinverni, M.; Lamy, J.-M.; Martin, D.; Feltin, E.; Dorsaz, J.; Castiglia, A.; Rossetti, M.; Duelk, M.; Vélez, C.; Grandjean, N.

    2014-12-01

    We demonstrate state-of-the-art p-type (Al)GaN layers deposited at low temperature (740 °C) by ammonia molecular beam epitaxy (NH3-MBE) to be used as top cladding of laser diodes (LDs) with the aim of further reducing the thermal budget on the InGaN quantum well active region. Typical p-type GaN resistivities and contact resistances are 0.4 Ω cm and 5 × 10-4 Ω cm2, respectively. As a test bed, we fabricated a hybrid laser structure emitting at 400 nm combining n-type AlGaN cladding and InGaN active region grown by metal-organic vapor phase epitaxy, with the p-doped waveguide and cladding layers grown by NH3-MBE. Single-mode ridge-waveguide LD exhibits a threshold voltage as low as 4.3 V for an 800 × 2 μm2 ridge dimension and a threshold current density of ˜5 kA cm-2 in continuous wave operation. The series resistance of the device is 6 Ω and the resistivity is 1.5 Ω cm, confirming thereby the excellent electrical properties of p-type Al0.06Ga0.94N:Mg despite the low growth temperature.

  1. The Study of Al0.29Ga0.71N-BASED Schottky Photodiodes Grown on Silicon by Plasma-Assisted Molecular Beam Epitaxy

    Science.gov (United States)

    Mohd Yusoff, M. Z.; Hassan, Z.; Chin, C. W.; Hassan, H. Abu; Abdullah, M. J.; Mohammad, N. N.; Ahmad, M. A.; Yusof, Y.

    2013-05-01

    In this paper, the growth and characterization of epitaxial Al0.29Ga0.71N grown on Si(111) by RF-plasma assisted molecular beam epitaxy (MBE) are described. The Al mole fraction was derived from the HR-XRD symmetric rocking curve (RC) ω/2θ scans of (0002) plane as x = 0.29. PL spectrum of sample has shown sharp and intense band edge emission of GaN without the existence of yellow emission band, showing that it is comparable in crystal quality of the sample when compared with previous reports. From the Raman measurement of as-grown Al0.29Ga0.71N layer on GaN/AlN/Si sample. We found that the dominant E2 (high) phonon mode of GaN appears at 572.7 cm-1. The E2 (high) mode of AlN appears at 656.7 cm-1 and deviates from the standard value of 655 cm-1 for unstrained AlN. Finally, AlGaN Schottky photodiode have been fabricated and analyzed by mean of electrical characterization, using current-voltage (I-V) measurement to evaluate the performance of this device.

  2. Blue-violet InGaN laser diodes grown on bulk GaN substrates by plasma-assisted molecular-beam epitaxy

    International Nuclear Information System (INIS)

    Skierbiszewski, C.; Wasilewski, Z.R.; Siekacz, M.; Feduniewicz, A.; Perlin, P.; Wisniewski, P.; Borysiuk, J.; Grzegory, I.; Leszczynski, M.; Suski, T.; Porowski, S.

    2005-01-01

    We report on the InGaN multiquantum laser diodes (LDs) made by rf plasma-assisted molecular beam epitaxy (PAMBE). The laser operation at 408 nm is demonstrated at room temperature with pulsed current injections using 50 ns pulses at 0.25% duty cycle. The threshold current density and voltage for the LDs with cleaved uncoated mirrors are 12 kA/cm 2 (900 mA) and 9 V, respectively. High output power of 0.83 W is obtained during pulse operation at 3.6 A and 9.6 V bias with the slope efficiency of 0.35 W/A. The laser structures are deposited on the high-pressure-grown low dislocation bulk GaN substrates taking full advantage of the adlayer enhanced lateral diffusion channel for adatoms below the dynamic metallic cover. Our devices compare very favorably to the early laser diodes fabricated using the metalorganic vapor phase epitaxy technique, providing evidence that the relatively low growth temperatures used in this process pose no intrinsic limitations on the quality of the blue optoelectronic components that can be fabricated using PAMBE

  3. Impact of extended defects on recombination in CdTe heterostructures grown by molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Zaunbrecher, Katherine N. [Department of Physics, Colorado State University, Fort Collins, Colorado 80523 (United States); National Renewable Energy Laboratory, Golden, Colorado 80401 (United States); Kuciauskas, Darius; Dippo, Pat; Barnes, Teresa M. [National Renewable Energy Laboratory, Golden, Colorado 80401 (United States); Swartz, Craig H.; Edirisooriya, Madhavie; Ogedengbe, Olanrewaju S.; Sohal, Sandeep; Hancock, Bobby L.; LeBlanc, Elizabeth G.; Jayathilaka, Pathiraja A. R. D.; Myers, Thomas H. [Materials Science, Engineering and Commercialization Program, Texas State University, San Marcos, Texas 78666 (United States)

    2016-08-29

    Heterostructures with CdTe and CdTe{sub 1-x}Se{sub x} (x ∼ 0.01) absorbers between two wider-band-gap Cd{sub 1-x}Mg{sub x}Te barriers (x ∼ 0.25–0.3) were grown by molecular beam epitaxy to study carrier generation and recombination in bulk materials with passivated interfaces. Using a combination of confocal photoluminescence (PL), time-resolved PL, and low-temperature PL emission spectroscopy, two extended defect types were identified and the impact of these defects on charge-carrier recombination was analyzed. The dominant defects identified by confocal PL were dislocations in samples grown on (211)B CdTe substrates and crystallographic twinning-related defects in samples on (100)-oriented InSb substrates. Low-temperature PL shows that twin-related defects have a zero-phonon energy of 1.460 eV and a Huang-Rhys factor of 1.50, while dislocation-dominated samples have a 1.473-eV zero-phonon energy and a Huang-Rhys factor of 1.22. The charge carrier diffusion length near both types of defects is ∼6 μm, suggesting that recombination is limited by diffusion dynamics. For heterostructures with a low concentration of extended defects, the bulk lifetime was determined to be 2.2 μs with an interface recombination velocity of 160 cm/s and an estimated radiative lifetime of 91 μs.

  4. Solution-Based Epitaxial Growth of Magnetically Responsive Cu@Ni Nanowires

    KAUST Repository

    Zhang, Shengmao

    2010-02-23

    An experiment was conducted to show the solution-based epitaxial growth of magnetically responsive Cu@Ni nanowires. The Ni-sheathed Cu nanowires were synthesized with a one-pot approach. 30 mL of high concentration NaOH, Cu(NO3)2. 3H2O, Cu(NO3)2. 3H2O and 0.07-0.30 mL of Ni(NO3)2. 6H 2O aqueous solutions were added into a plastic reactor with a capacity of 50.0 mL. A varying amount of ethylenediamine (EDA) and hydrazine were also added sequentially, followed by thorough mixing of all reagents. The dimension, morphology, and chemical composition of the products were examined with scanning electron microscopy with energy dispersive X-ray spectroscopy. The XPS analysis on the as formed Cu nanowires confirms that there is indeed no nickel inclusion in the nanowires prior to the formation of nickel overcoat, which rules out the possibility of Cu-Ni alloy formation.

  5. Solution-Based Epitaxial Growth of Magnetically Responsive Cu@Ni Nanowires

    KAUST Repository

    Zhang, Shengmao; Zeng, Hua Chun

    2010-01-01

    An experiment was conducted to show the solution-based epitaxial growth of magnetically responsive Cu@Ni nanowires. The Ni-sheathed Cu nanowires were synthesized with a one-pot approach. 30 mL of high concentration NaOH, Cu(NO3)2. 3H2O, Cu(NO3)2. 3H2O and 0.07-0.30 mL of Ni(NO3)2. 6H 2O aqueous solutions were added into a plastic reactor with a capacity of 50.0 mL. A varying amount of ethylenediamine (EDA) and hydrazine were also added sequentially, followed by thorough mixing of all reagents. The dimension, morphology, and chemical composition of the products were examined with scanning electron microscopy with energy dispersive X-ray spectroscopy. The XPS analysis on the as formed Cu nanowires confirms that there is indeed no nickel inclusion in the nanowires prior to the formation of nickel overcoat, which rules out the possibility of Cu-Ni alloy formation.

  6. Growth of Ferromagnetic Epitaxial Film of Hexagonal FeGe on (111) Ge Surface

    Science.gov (United States)

    Kumar, Dushyant; Joshi, P. C.; Hossain, Z.; Budhani, R. C.

    2014-03-01

    The realization of semiconductors showing ferromagnetic order at easily accessible temperatures has been of interest due to their potential use in spintronic devices where long spin life times are of key interest. We have realized the growth of FeGe thin films on Ge (111) wafers using pulsed laser deposition (PLD). The stoichiometric and single phase FeGe target used in PLD chamber has been made by arc melting. A typical θ-2 θ diffraction spectra performed on 40 nm thick FeGe film suggests the stabilization of β-Ni2In (B82-type) hexagonal phase with an epitaxial orientation of (0001)FeGe ||(111)Ge and [11-20]FeGe ||[-110]Ge. SEM images shows a granular structure with the formation of very large grains of about 100 to 500 nm in lateral dimension. The magnetization vs. temperature data taken from SQUID reveal the TC of ~ 270K. Since, PLD technique makes it easier to stabilize the B82 (Ni2In) hexagonal phase in thin FeGe films, this work opens opportunities to reinvestigate many conflicting results on various properties of the FeGe system.

  7. Growth, structure and phase transitions of epitaxial nanowires of III-V semiconductors

    International Nuclear Information System (INIS)

    Glas, F; Patriarche, G; Harmand, J C

    2010-01-01

    We review and illustrate the impact of TEM on the study of nanowires of non-nitride III-V semiconductors, with particular emphasis on the understanding of the thermodynamics and kinetics of their formation assisted by nano-sized catalyst particles. Besides providing basic information about the morphology of the nanowires and their growth rate as a function of diameter, TEM offers insights into the peculiar crystalline structure that they adopt. We discuss the formation of the unusual wurtzite hexagonal crystalline phase and that of planar stacking defects in these nanowires and show that they are kinetically controlled. We also demonstrate the transformation of wurtzite into cubic sphalerite upon epitaxial burying of the nanowires. Nanowires are particularly interesting in that they allow the fabrication of precisely positioned quantum dots with well-defined geometries. In this respect, we discuss the formation of strained quantum-size inclusions in nanowires, their critical dimensions and the kinetic and thermodynamic factors governing the changes of the crystalline structure that sometimes occur around a hetero-interface.

  8. Single-mode molecular beam epitaxy grown PbEuSeTe/PbTe buried-heterostructure diode lasers for CO2 high-resolution spectroscopy

    International Nuclear Information System (INIS)

    Feit, Z.; Kostyk, D.; Woods, R.J.; Mak, P.

    1991-01-01

    Buried-heterostructure tunable PbEuSeTe/PbTe lasers were fabricated using a two-stage molecular beam epitaxy growth procedure. Improvements in the processing technique yielded lasers that show performance characteristics significantly better than those reported previously. A continuous wave (cw) operating temperature of 203 K was realized, which is the highest cw operating temperature ever reported for lead-chalcogenides diode lasers. This laser exhibited exceptionally low-threshold currents of 1.4 mA at 90 K and 43 mA at 160 K with single-mode operation for injection currents up to 30I th and 0.18 mW power at 100 K. The usefulness of the laser, when operating cw at 200 K, was demonstrated by the ability to perform high-resolution spectroscopy of a low-pressure CO 2 gas sample

  9. Study of the structural and optical properties of GaP(N) layers synthesized by molecular-beam epitaxy on Si(100) 4° substrates

    Energy Technology Data Exchange (ETDEWEB)

    Kryzhanovskaya, N. V., E-mail: NataliaKryzh@gmail.com; Polubavkina, Yu. S. [Russian Academy of Sciences, St. Petersburg National Research Academic University–Nanotechnology Research and Education Center (Russian Federation); Nevedomskiy, V. N. [Russian Academy of Sciences, Ioffe Physical–Technical Institute (Russian Federation); Nikitina, E. V.; Lazarenko, A. A. [Russian Academy of Sciences, St. Petersburg National Research Academic University–Nanotechnology Research and Education Center (Russian Federation); Egorov, A. Yu. [St. Petersburg National Research University of Information Technologies, Mechanics, and Optics (Russian Federation); Maximov, M. V.; Moiseev, E. I.; Zhukov, A. E. [Russian Academy of Sciences, St. Petersburg National Research Academic University–Nanotechnology Research and Education Center (Russian Federation)

    2017-02-15

    The structural and optical properties of GaP and GaPN layers synthesized by molecular-beam epitaxy on Si(100) substrates misoriented by 4° are studied. The possibility of producing GaP buffer layers that exhibit a high degree of heterointerface planarity and an outcropping dislocation density of no higher than ~2 × 10{sup 8} cm{sup –2} is shown. Emission from the Si/GaP/GaPN structure in the spectral range of 630–640 nm at room temperature is observed. Annealing during growth of the Si/GaP/GaPN structure makes it possible to enhance the room-temperature photoluminescence intensity by a factor of 2.6, with no shift of the maximum of the emission line.

  10. Characterization of GaN P-N Junction Grown on Si (111) Substrate by Plasma-assisted Molecular Beam Epitaxy

    International Nuclear Information System (INIS)

    Rosfariza Radzali; Rosfariza Radzali; Mohd Anas Ahmad; Zainuriah Hassan; Norzaini Zainal; Kwong, Y.F.; Woei, C.C.; Mohd Zaki Mohd Yusoff; Mohd Zaki Mohd Yusoff

    2011-01-01

    In this report, the growth of GaN pn junction on Si (111) substrate by plasma assisted molecular beam epitaxy (PAMBE) is presented. Doping of GaN p-n junction has been carried out using Si and Mg as n-type dopant and p-type dopants, respectively. The sample had been characterized by PL, Raman spectroscopy, HR-XRD and SEM. PL spectrum showed strong band edge emission of GaN at ∼364 nm, indicating good quality of the sample. The image of SEM cross section of the sample showed sharp interfaces. The presence of peak ∼657 cm -1 in Raman measurement exhibited successful doping of Mg in the sample. (author)

  11. Structural, optical, and hydrogenation properties of ZnO nanowall networks grown on a Si (1 1 1) substrate by plasma-assisted molecular beam epitaxy

    International Nuclear Information System (INIS)

    Su, S.C.; Lu, Y.M.; Zhang, Z.Z.; Li, B.H.; Shen, D.Z.; Yao, B.; Zhang, J.Y.; Zhao, D.X.; Fan, X.W.

    2008-01-01

    ZnO nanowall networks were grown on a Si (1 1 1) substrate by plasma-assisted molecular beam epitaxy (P-MBE) without using catalysts. Scanning electronic microscopy (FE-SEM) confirmed the formation of nanowalls with a thickness of about 10-20 nm. X-ray diffraction (XRD) showed that the ZnO nanowall networks were crystallized in a wurtzite structure with their height parallel to the direction. Photoluminescence (PL) of the ZnO nanowall networks exhibited free excitons (FEs), donor-bound exciton (D 0 X), donor-acceptor pair (DAP), and free exciton to acceptor (FA) emissions. The growth mechanism of the ZnO nanowall networks was discussed, and their hydrogenation was also studied

  12. Study of the structural and optical properties of GaP(N) layers synthesized by molecular-beam epitaxy on Si(100) 4° substrates

    International Nuclear Information System (INIS)

    Kryzhanovskaya, N. V.; Polubavkina, Yu. S.; Nevedomskiy, V. N.; Nikitina, E. V.; Lazarenko, A. A.; Egorov, A. Yu.; Maximov, M. V.; Moiseev, E. I.; Zhukov, A. E.

    2017-01-01

    The structural and optical properties of GaP and GaPN layers synthesized by molecular-beam epitaxy on Si(100) substrates misoriented by 4° are studied. The possibility of producing GaP buffer layers that exhibit a high degree of heterointerface planarity and an outcropping dislocation density of no higher than ~2 × 10"8 cm"–"2 is shown. Emission from the Si/GaP/GaPN structure in the spectral range of 630–640 nm at room temperature is observed. Annealing during growth of the Si/GaP/GaPN structure makes it possible to enhance the room-temperature photoluminescence intensity by a factor of 2.6, with no shift of the maximum of the emission line.

  13. Formation and properties of epitaxial CdSe, ZnSe quantum dots. Conventional molecular beam epitaxy and related techniques

    Energy Technology Data Exchange (ETDEWEB)

    Mahapatra, Suddhasatta

    2008-01-16

    This thesis systematically investigates three such alternative approaches, along with conventional MBE, with emphasis on the formation-mechanism of QDs, and optimization of their morphological and optical attributes. it is shown here that no distinct 3D islands are formed in MBE growth of CdSe on ZnSe. While CdSe heteroepitaxy occurs in the multilayer-mode at T{sub G}=300 C, a reentrant recovery of the layer-by-layer mode is reported in this thesis, for growth at T{sub G}<{proportional_to}240 C. In the second variant technique, formation of large and distinct islands is demonstrated by deposition of amorphous selenium (a-Se) onto a 2D CdSe epilayer at room temperature and its subsequent desorption at a higher temperature (T{sub D}=230 C). The process steps of the third variant technique, developed in course of this work, are very similar to those of the previous one-the only alteration being the substitution of selenium with tellurium as the cap-forming-material. (orig.)

  14. Ge quantum dot arrays grown by ultrahigh vacuum molecular-beam epitaxy on the Si(001) surface: nucleation, morphology, and CMOS compatibility.

    Science.gov (United States)

    Yuryev, Vladimir A; Arapkina, Larisa V

    2011-09-05

    Issues of morphology, nucleation, and growth of Ge cluster arrays deposited by ultrahigh vacuum molecular beam epitaxy on the Si(001) surface are considered. Difference in nucleation of quantum dots during Ge deposition at low (≲600°C) and high (≳600°C) temperatures is studied by high resolution scanning tunneling microscopy. The atomic models of growth of both species of Ge huts--pyramids and wedges-- are proposed. The growth cycle of Ge QD arrays at low temperatures is explored. A problem of lowering of the array formation temperature is discussed with the focus on CMOS compatibility of the entire process; a special attention is paid upon approaches to reduction of treatment temperature during the Si(001) surface pre-growth cleaning, which is at once a key and the highest-temperature phase of the Ge/Si(001) quantum dot dense array formation process. The temperature of the Si clean surface preparation, the final high-temperature step of which is, as a rule, carried out directly in the MBE chamber just before the structure deposition, determines the compatibility of formation process of Ge-QD-array based devices with the CMOS manufacturing cycle. Silicon surface hydrogenation at the final stage of its wet chemical etching during the preliminary cleaning is proposed as a possible way of efficient reduction of the Si wafer pre-growth annealing temperature.

  15. Ge quantum dot arrays grown by ultrahigh vacuum molecular-beam epitaxy on the Si(001 surface: nucleation, morphology, and CMOS compatibility

    Directory of Open Access Journals (Sweden)

    Yuryev Vladimir

    2011-01-01

    Full Text Available Abstract Issues of morphology, nucleation, and growth of Ge cluster arrays deposited by ultrahigh vacuum molecular beam epitaxy on the Si(001 surface are considered. Difference in nucleation of quantum dots during Ge deposition at low (≲600°C and high (≳600°C temperatures is studied by high resolution scanning tunneling microscopy. The atomic models of growth of both species of Ge huts--pyramids and wedges-- are proposed. The growth cycle of Ge QD arrays at low temperatures is explored. A problem of lowering of the array formation temperature is discussed with the focus on CMOS compatibility of the entire process; a special attention is paid upon approaches to reduction of treatment temperature during the Si(001 surface pre-growth cleaning, which is at once a key and the highest-temperature phase of the Ge/Si(001 quantum dot dense array formation process. The temperature of the Si clean surface preparation, the final high-temperature step of which is, as a rule, carried out directly in the MBE chamber just before the structure deposition, determines the compatibility of formation process of Ge-QD-array based devices with the CMOS manufacturing cycle. Silicon surface hydrogenation at the final stage of its wet chemical etching during the preliminary cleaning is proposed as a possible way of efficient reduction of the Si wafer pre-growth annealing temperature.

  16. Selective growth of Ge1- x Sn x epitaxial layer on patterned SiO2/Si substrate by metal-organic chemical vapor deposition

    Science.gov (United States)

    Takeuchi, Wakana; Washizu, Tomoya; Ike, Shinichi; Nakatsuka, Osamu; Zaima, Shigeaki

    2018-01-01

    We have investigated the selective growth of a Ge1- x Sn x epitaxial layer on a line/space-patterned SiO2/Si substrate by metal-organic chemical vapor deposition. We examined the behavior of a Sn precursor of tributyl(vinyl)tin (TBVSn) during the growth on Si and SiO2 substrates and investigated the effect of the Sn precursor on the selective growth. The selective growth of the Ge1- x Sn x epitaxial layer was performed under various total pressures and growth temperatures of 300 and 350 °C. The selective growth of the Ge1- x Sn x epitaxial layer on the patterned Si region is achieved at a low total pressure without Ge1- x Sn x growth on the SiO2 region. In addition, we found that the Sn content in the Ge1- x Sn x epitaxial layer increases with width of the SiO2 region for a fixed Si width even with low total pressure. To control the Sn content in the selective growth of the Ge1- x Sn x epitaxial layer, it is important to suppress the decomposition and migration of Sn and Ge precursors.

  17. Growth kinetics and mass transport mechanisms of GaN columns by selective area metal organic vapor phase epitaxy

    Science.gov (United States)

    Wang, Xue; Hartmann, Jana; Mandl, Martin; Sadat Mohajerani, Matin; Wehmann, Hergo-H.; Strassburg, Martin; Waag, Andreas

    2014-04-01

    Three-dimensional GaN columns recently have attracted a lot of attention as the potential basis for core-shell light emitting diodes for future solid state lighting. In this study, the fundamental insights into growth kinetics and mass transport mechanisms of N-polar GaN columns during selective area metal organic vapor phase epitaxy on patterned SiOx/sapphire templates are systematically investigated using various pitch of apertures, growth time, and silane flow. Species impingement fluxes on the top surface of columns Jtop and on their sidewall Jsw, as well as, the diffusion flux from the substrate Jsub contribute to the growth of the GaN columns. The vertical and lateral growth rates devoted by Jtop, Jsw and Jsub are estimated quantitatively. The diffusion length of species on the SiOx mask surface λsub as well as on the sidewall surfaces of the 3D columns λsw are determined. The influences of silane on the growth kinetics are discussed. A growth model is developed for this selective area metal organic vapor phase epitaxy processing.

  18. Epitaxial growth of hetero-Ln-MOF hierarchical single crystals for domain- and orientation-controlled multicolor luminescence 3D coding capability

    Energy Technology Data Exchange (ETDEWEB)

    Pan, Mei; Zhu, Yi-Xuan; Wu, Kai; Chen, Ling; Hou, Ya-Jun; Yin, Shao-Yun; Wang, Hai-Ping; Fan, Ya-Nan [MOE Laboratory of Bioinorganic and Synthetic Chemistry, Lehn Institute of Functional Materials, School of Chemistry, Sun Yat-Sen University, Guangzhou (China); Su, Cheng-Yong [MOE Laboratory of Bioinorganic and Synthetic Chemistry, Lehn Institute of Functional Materials, School of Chemistry, Sun Yat-Sen University, Guangzhou (China); State Key Laboratory of Applied Organic Chemistry, Lanzhou University, Lanzhou (China)

    2017-11-13

    Core-shell or striped heteroatomic lanthanide metal-organic framework hierarchical single crystals were obtained by liquid-phase anisotropic epitaxial growth, maintaining identical periodic organization while simultaneously exhibiting spatially segregated structure. Different types of domain and orientation-controlled multicolor photophysical models are presented, which show either visually distinguishable or visible/near infrared (NIR) emissive colors. This provides a new bottom-up strategy toward the design of hierarchical molecular systems, offering high-throughput and multiplexed luminescence color tunability and readability. The unique capability of combining spectroscopic coding with 3D (three-dimensional) microscale spatial coding is established, providing potential applications in anti-counterfeiting, color barcoding, and other types of integrated and miniaturized optoelectronic materials and devices. (copyright 2017 Wiley-VCH Verlag GmbH and Co. KGaA, Weinheim)

  19. Epitaxial Growth of Hetero-Ln-MOF Hierarchical Single Crystals for Domain- and Orientation-Controlled Multicolor Luminescence 3D Coding Capability.

    Science.gov (United States)

    Pan, Mei; Zhu, Yi-Xuan; Wu, Kai; Chen, Ling; Hou, Ya-Jun; Yin, Shao-Yun; Wang, Hai-Ping; Fan, Ya-Nan; Su, Cheng-Yong

    2017-11-13

    Core-shell or striped heteroatomic lanthanide metal-organic framework hierarchical single crystals were obtained by liquid-phase anisotropic epitaxial growth, maintaining identical periodic organization while simultaneously exhibiting spatially segregated structure. Different types of domain and orientation-controlled multicolor photophysical models are presented, which show either visually distinguishable or visible/near infrared (NIR) emissive colors. This provides a new bottom-up strategy toward the design of hierarchical molecular systems, offering high-throughput and multiplexed luminescence color tunability and readability. The unique capability of combining spectroscopic coding with 3D (three-dimensional) microscale spatial coding is established, providing potential applications in anti-counterfeiting, color barcoding, and other types of integrated and miniaturized optoelectronic materials and devices. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  20. Epitaxial growth of hetero-Ln-MOF hierarchical single crystals for domain- and orientation-controlled multicolor luminescence 3D coding capability

    International Nuclear Information System (INIS)

    Pan, Mei; Zhu, Yi-Xuan; Wu, Kai; Chen, Ling; Hou, Ya-Jun; Yin, Shao-Yun; Wang, Hai-Ping; Fan, Ya-Nan; Su, Cheng-Yong

    2017-01-01

    Core-shell or striped heteroatomic lanthanide metal-organic framework hierarchical single crystals were obtained by liquid-phase anisotropic epitaxial growth, maintaining identical periodic organization while simultaneously exhibiting spatially segregated structure. Different types of domain and orientation-controlled multicolor photophysical models are presented, which show either visually distinguishable or visible/near infrared (NIR) emissive colors. This provides a new bottom-up strategy toward the design of hierarchical molecular systems, offering high-throughput and multiplexed luminescence color tunability and readability. The unique capability of combining spectroscopic coding with 3D (three-dimensional) microscale spatial coding is established, providing potential applications in anti-counterfeiting, color barcoding, and other types of integrated and miniaturized optoelectronic materials and devices. (copyright 2017 Wiley-VCH Verlag GmbH and Co. KGaA, Weinheim)

  1. Raman Scattering analysis of InGaAs and AlGaAs superlattices grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Oeztuerk, N.; Bahceli, S.

    2010-01-01

    InGaAs/GaAs and AlGaAs/GaAs multiple quantum well structures were grown by molecular beam epitaxy and investigated by X-ray diffraction and micro Raman spectroscopy. Phonon modes are investigated in backscattering from (001) surface. In the measured micro Raman spectrum for both structure, phonon peaks can be resolved for GaAs. These are longitudinal optical (LO) mode at 293 cm - 1 and 294 cm - 1 for InGaAs and AlGaAs, respectively.

  2. Improving stability of photoluminescence of ZnSe thin films grown by molecular beam epitaxy by incorporating Cl dopant

    International Nuclear Information System (INIS)

    Wang, J. S.; Shen, J. L.; Chen, W. J.; Tsai, Y. H.; Wang, H. H.; Yang, C. S.; Chen, R. H.; Tsai, C. D.

    2011-01-01

    This investigation studies the effect of chlorine (Cl) dopant in ZnSe thin films that were grown by molecular beam epitaxy on their photoluminescence (PL) and the stability thereof. Free excitonic emission was observed at room-temperature in the Cl-doped sample. Photon irradiation with a wavelength of 404 nm and a power density of 9.1 W/cm 2 has a much stronger effect on PL degradation than does thermal heating to a temperature of 150 deg. C. Additionally, this study shows that the generation of nonradiative centers by both photon irradiation and thermal heating can be greatly inhibited by incorporating Cl dopant.

  3. Chirped-pulse manipulated carrier dynamics in low-temperature molecular-beam-epitaxy grown GaAs

    International Nuclear Information System (INIS)

    Lee, Chao-Kuei; Lin, Yuan-Yao; Lin, Sung-Hui; Lin, Gong-Ru; Pan, Ci-Ling

    2014-01-01

    Chirped pulse controlled carrier dynamics in low-temperature molecular-beam-epitaxy grown GaAs are investigated by degenerate pump-probe technique. Varying the chirped condition of excited pulse from negative to positive increases the carrier relaxation time so as to modify the dispersion and reshape current pulse in time domain. The spectral dependence of carrier dynamics is analytically derived and explained by Shockley-Read Hall model. This observation enables the new feasibility of controlling carrier dynamics in ultrafast optical devices via the chirped pulse excitations

  4. Growth and Characterization of (211)B Cadmium Telluride Buffer Layer Grown by Metal-organic Vapor Phase Epitaxy on Nanopatterned Silicon for Mercury Cadmium Telluride Based Infrared Detector Applications

    Science.gov (United States)

    Shintri, Shashidhar S.

    Mercury cadmium telluride (MCT or Hg1-xCdxTe) grown by molecular beam epitaxy (MBE) is presently the material of choice for fabricating infrared (IR) detectors used in night vision based military applications. The focus of MCT epitaxy has gradually shifted since the last decade to using Si as the starting substrate since it offers several advantages. But the ˜19 % lattice mismatch between MCT and Si generates lots of crystal defects some of which degrade the performance of MCT devices. Hence thick CdTe films are used as buffer layers on Si to accommodate the defects. However, growth of high quality single crystal CdTe on Si is challenging and to date, the best MBE CdTe/Si reportedly has defects in the mid-105 cm -2 range. There is a critical need to reduce the defect levels by at least another order of magnitude, which is the main motivation behind the present work. The use of alternate growth technique called metal-organic vapor phase epitaxy (MOVPE) offers some advantages over MBE and in this work MOVPE has been employed to grow the various epitaxial films. In the first part of this work, conditions for obtaining high quality (211)B CdTe epitaxy on (211)Si were achieved, which also involved studying the effect of having additional intermediate buffer layers such as Ge and ZnTe and incorporation of in-situ thermal cyclic annealing (TCA) to reduce the dislocation density. A critical problem of Si cross-contamination due to 'memory effect' of different reactant species was minimized by introducing tertiarybutylArsine (TBAs) which resulted in As-passivation of (211)Si. The best 8-10 µm thick CdTe films on blanket (non-patterned) Si had dislocations around 3×105 cm-2, which are the best reported by MOVPE till date and comparable to the highest quality films available by MBE. In the second part of the work, nanopatterned (211)Si was used to study the effect of patterning on the crystal quality of epitaxial CdTe. In one such study, patterning of ˜20 nm holes in SiO2

  5. Stabilisation of late transition metal and noble metal films in hexagonal and body centred tetragonal phases by epitaxial growth

    Energy Technology Data Exchange (ETDEWEB)

    Hueger, E.

    2005-08-26

    In this work ultrathin metallic films with a crystal phase different to their natural bulk structure were produced by hetero-epitaxial growth on metallic substrates. A further aim of this work was to understand the initiation, growth and stability of crystal phase modifications of these films. there exist cases where the films turn beyond the pseudomorphic-growth to a crystal phase different from their natural bulk structure. The present work presents and discusses such a case in addition to the general phenomenon of pseudomorphic-growth. In particular it is shown that metals whose natural phase is face centred cubic (fcc) can be grown in body centred tetragonal (bct) or hexagonal close packed (hcp) phases in the form of thin films on (001) surfaces of appropriate substrates. The growth behavior, electron diffraction analysis, appearance conditions, geometric fit considerations, examples and a discussion of the phase stability of non-covered films and superlattices is given reviewing all epitaxial-systems whose diffraction pattern can be explained by the hexagonal or pseudomorphic bct phase. (orig.)

  6. One-pot growth of two-dimensional lateral heterostructures via sequential edge-epitaxy

    Science.gov (United States)

    Sahoo, Prasana K.; Memaran, Shahriar; Xin, Yan; Balicas, Luis; Gutiérrez, Humberto R.

    2018-01-01

    Two-dimensional heterojunctions of transition-metal dichalcogenides have great potential for application in low-power, high-performance and flexible electro-optical devices, such as tunnelling transistors, light-emitting diodes, photodetectors and photovoltaic cells. Although complex heterostructures have been fabricated via the van der Waals stacking of different two-dimensional materials, the in situ fabrication of high-quality lateral heterostructures with multiple junctions remains a challenge. Transition-metal-dichalcogenide lateral heterostructures have been synthesized via single-step, two-step or multi-step growth processes. However, these methods lack the flexibility to control, in situ, the growth of individual domains. In situ synthesis of multi-junction lateral heterostructures does not require multiple exchanges of sources or reactors, a limitation in previous approaches as it exposes the edges to ambient contamination, compromises the homogeneity of domain size in periodic structures, and results in long processing times. Here we report a one-pot synthetic approach, using a single heterogeneous solid source, for the continuous fabrication of lateral multi-junction heterostructures consisting of monolayers of transition-metal dichalcogenides. The sequential formation of heterojunctions is achieved solely by changing the composition of the reactive gas environment in the presence of water vapour. This enables selective control of the water-induced oxidation and volatilization of each transition-metal precursor, as well as its nucleation on the substrate, leading to sequential edge-epitaxy of distinct transition-metal dichalcogenides. Photoluminescence maps confirm the sequential spatial modulation of the bandgap, and atomic-resolution images reveal defect-free lateral connectivity between the different transition-metal-dichalcogenide domains within a single crystal structure. Electrical transport measurements revealed diode-like responses across the

  7. Halogen doping of II-VI semiconductors during molecular beam epitaxy

    Energy Technology Data Exchange (ETDEWEB)

    Waag, A.; Litz, Th.; Fischer, F.; Heinke, H.; Scholl, S.; Hommel, D.; Landwehr, G. (Physikalisches Inst. der Univ. Wuerzburg (Germany)); Bilger, G. (Zentrum fuer Sonnenenergie und Wasserstoff-Forschung, Stuttgart (Germany))

    1994-04-14

    Results on the halogen doping of CdTe, (CdMn)Te as well as (CdMg)Te thin films and quantum well structures are reported. The structures were grown by molecular beam epitaxy. The samples have been investigated by Van der Pauw, photoconductivity, X-ray diffraction, XPS and SIMS measurements. ZnCl[sub 2] and ZnBr[sub 2] have been used as dopant sources. Free carrier concentrations at room temperature above 10[sup 18] cm[sup -3] can easily be achieved for CdTe for a wide range of Cd/Te flux ratios and substrate temperatures. In the ternary alloys, the free carrier concentration decreases drastically with increasing x-values, despite a constant incorporation of the dopant species. In addition, persistent photoconductivity has been observed in n-type doped ternary thin films at low temperatures. The decrease of the free carrier concentration with x-value is common to other wide-gap ternary alloys, and the reason for it is discussed in the frame of DX-like deep donor impurities in ternary II-VI compounds. In first experiments on planar halogen doping of CdTe, a doping level of 5x10[sup 18] cm[sup -3] could be reached in the doped regions, the highest value ever reported for CdTe. A clear influence of dopant incorporation on the structural quality of CdTe thin films has been seen even for dopant concentrations of as low as 10[sup 18] cm[sup -3]. The FWHM of the rocking curves decreased by a factor of 2 with increasing dopant incorporation. SIMS as well as XPS measurements demonstrate that the Cl/Zn and Br/Zn ratio in the doped films is 2/1, but no chemical shift corresponding to Zn-Cl or Zn-Br bonds could be detected. A model for the incorporation of the halogens is proposed on the basis of these results

  8. GaAs structures with InAs and As quantum dots produced in a single molecular beam epitaxy process

    International Nuclear Information System (INIS)

    Nevedomskii, V. N.; Bert, N. A.; Chaldyshev, V. V.; Preobrazhenskii, V. V.; Putyato, M. A.; Semyagin, B. R.

    2009-01-01

    Epitaxial GaAs layers containing InAs semiconductor quantum dots and As metal quantum dots are grown by molecular beam epitaxy. The InAs quantum dots are formed by the Stranskii-Krastanow mechanism, whereas the As quantum dots are self-assembled in the GaAs layer grown at low temperature with a large As excess. The microstructure of the samples is studied by transmission electron microscopy. It is established that the As metal quantum dots formed in the immediate vicinity of the InAs semiconductor quantum dots are larger in size than the As quantum dots formed far from the InAs quantum dots. This is apparently due to the effect of strain fields of the InAs quantum dots upon the self-assembling of As quantum dots. Another phenomenon apparently associated with local strains around the InAs quantum dots is the formation of V-like defects (stacking faults) during the overgrowth of the InAs quantum dots with the GaAs layer by low-temperature molecular beam epitaxy. Such defects have a profound effect on the self-assembling of As quantum dots. Specifically, on high-temperature annealing needed for the formation of large-sized As quantum dots by Ostwald ripening, the V-like defects bring about the dissolution of the As quantum dots in the vicinity of the defects. In this case, excess arsenic most probably diffuses towards the open surface of the sample via the channels of accelerated diffusion in the planes of stacking faults.

  9. n-type dopants in (001) β-Ga2O3 grown on (001) β-Ga2O3 substrates by plasma-assisted molecular beam epitaxy

    Science.gov (United States)

    Han, Sang-Heon; Mauze, Akhil; Ahmadi, Elaheh; Mates, Tom; Oshima, Yuichi; Speck, James S.

    2018-04-01

    Ge and Sn as n-type dopants in (001) β-Ga2O3 films were investigated using plasma-assisted molecular beam epitaxy. The Ge concentration showed a strong dependence on the growth temperature, whereas the Sn concentration remains independent of the growth temperature. The maximum growth temperature at which a wide range of Ge concentrations (from 1017 to 1020 cm-3) could be achieved was 675 °C while the same range of Sn concentration could be achieved at growth temperature of 750 °C. Atomic force microscopy results revealed that higher growth temperature shows better surface morphology. Therefore, our study reveals a tradeoff between higher Ge doping concentration and high quality surface morphology on (001) β-Ga2O3 films grown by plasma-assisted molecular beam epitaxy. The Ge doped films had an electron mobility of 26.3 cm2 V-1 s-1 at the electron concentration of 6.7 × 1017 cm-3 whereas the Sn doped films had an electron mobility of 25.3 cm2 V-1 s-1 at the electron concentration of 1.1 × 1018 cm-3.

  10. Organometallic vapor-phase epitaxy theory and practice

    CERN Document Server

    Stringfellow, Gerald B

    1989-01-01

    Here is one of the first single-author treatments of organometallic vapor-phase epitaxy (OMVPE)--a leading technique for the fabrication of semiconductor materials and devices. Also included are metal-organic molecular-beam epitaxy (MOMBE) and chemical-beam epitaxy (CBE) ultra-high-vacuum deposition techniques using organometallic source molecules. Of interest to researchers, students, and people in the semiconductor industry, this book provides a basic foundation for understanding the technique and the application of OMVPE for the growth of both III-V and II-VI semiconductor materials and the

  11. Epitaxial Growth of Two-Dimensional Layered Transition-Metal Dichalcogenides: Growth Mechanism, Controllability, and Scalability

    KAUST Repository

    Li, Henan

    2017-07-06

    Recently there have been many research breakthroughs in two-dimensional (2D) materials including graphene, boron nitride (h-BN), black phosphors (BPs), and transition-metal dichalcogenides (TMDCs). The unique electrical, optical, and thermal properties in 2D materials are associated with their strictly defined low dimensionalities. These materials provide a wide range of basic building blocks for next-generation electronics. The chemical vapor deposition (CVD) technique has shown great promise to generate high-quality TMDC layers with scalable size, controllable thickness, and excellent electronic properties suitable for both technological applications and fundamental sciences. The capability to precisely engineer 2D materials by chemical approaches has also given rise to fascinating new physics, which could lead to exciting new applications. In this Review, we introduce the latest development of TMDC synthesis by CVD approaches and provide further insight for the controllable and reliable synthesis of atomically thin TMDCs. Understanding of the vapor-phase growth mechanism of 2D TMDCs could benefit the formation of complicated heterostructures and novel artificial 2D lattices.

  12. Growth of epitaxial Pt thin films on (0 0 1) SrTiO{sub 3} by rf magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Kahsay, A. [Departament de Física Aplicada i Òptica, Universitat de Barcelona, 08028 Barcelona (Spain); Polo, M.C., E-mail: mcpolo@ub.edu [Departament de Física Aplicada i Òptica, Universitat de Barcelona, 08028 Barcelona (Spain); Ferrater, C.; Ventura, J. [Departament de Física Aplicada i Òptica, Universitat de Barcelona, 08028 Barcelona (Spain); Rebled, J.M. [Departament d’Electrònica, Universitat de Barcelona Institut de Nanociència i Nanotecnologia IN 2UB, 08028 Barcelona (Spain); Varela, M. [Departament de Física Aplicada i Òptica, Universitat de Barcelona, 08028 Barcelona (Spain)

    2014-07-01

    The growth of platinum thin film by rf magnetron sputtering on SrTiO{sub 3}(0 0 1) substrates for oxide based devices was investigated. Platinum films grown at temperatures higher than 750 °C were epitaxial ([1 0 0]Pt(0 0 1)//[1 0 0]STO(0 0 1)), whereas at lower temperatures Pt(1 1 1) films were obtained. The surface morphology of the Pt films showed a strong dependence on the deposition temperature as was revealed by atomic force microscopy (AFM). At elevated temperatures there is a three-dimensional (3D) growth of rectangular atomically flat islands with deep boundaries between them. On the other hand, at low deposition temperatures, a two-dimensional (2D) layered growth was observed. The transition from 2D to 3D growth modes was observed that occurs for temperatures around 450 °C. The obtained epitaxial thin films also formed an atomically sharp interface with the SrTiO{sub 3}(0 0 1) substrate as confirmed by HRTEM.

  13. Initial stages of the ion-beam assisted epitaxial GaN film growth on 6H-SiC(0001)

    International Nuclear Information System (INIS)

    Neumann, L.; Gerlach, J.W.; Rauschenbach, B.

    2012-01-01

    Ultra-thin gallium nitride (GaN) films were deposited using the ion-beam assisted molecular-beam epitaxy technique. The influence of the nitrogen ion to gallium atom flux ratio (I/A ratio) during the early stages of GaN nucleation and thin film growth directly, without a buffer layer on super-polished 6H-SiC(0001) substrates was studied. The deposition process was performed at a constant substrate temperature of 700 °C by evaporation of Ga and irradiation with hyperthermal nitrogen ions from a constricted glow-discharge ion source. The hyperthermal nitrogen ion flux was kept constant and the kinetic energy of the ions did not exceed 25 eV. The selection of different I/A ratios in the range from 0.8 to 3.2 was done by varying the Ga deposition rate between 5 × 10 13 and 2 × 10 14 at. cm −2 s −1 . The crystalline surface structure during the GaN growth was monitored in situ by reflection high-energy electron diffraction. The surface topography of the films as well as the morphology of separated GaN islands on the substrate surface was examined after film growth using a scanning tunneling microscope without interruption of ultra-high vacuum. The results show, that the I/A ratio has a major impact on the properties of the resulting ultra-thin GaN films. The growth mode, the surface roughness, the degree of GaN coverage of the substrate and the polytype mixture depend notably on the I/A ratio. - Highlights: ► Ultra-thin epitaxial GaN films prepared by hyperthermal ion-beam assisted deposition. ► Surface structure and topography studied during and after initial growth stages. ► Growth mode dependent on nitrogen ion to gallium atom flux ratio. ► Change from three-dimensional to two-dimensional growth for Ga-rich growth conditions.

  14. Epitaxial growth of a monolayer WSe2-MoS2 lateral p-n junction with an atomically sharp interface

    KAUST Repository

    Li, Ming Yang

    2015-07-30

    Two-dimensional transition metal dichalcogenides (TMDCs) such as molybdenum sulfide MoS2 and tungsten sulfide WSe2 have potential applications in electronics because they exhibit high on-off current ratios and distinctive electro-optical properties. Spatially connected TMDC lateral heterojunctions are key components for constructing monolayer p-n rectifying diodes, light-emitting diodes, photovoltaic devices, and bipolar junction transistors. However, such structures are not readily prepared via the layer-stacking techniques, and direct growth favors the thermodynamically preferred TMDC alloys. We report the two-step epitaxial growth of lateral WSe2-MoS2 heterojunction, where the edge of WSe2 induces the epitaxial MoS2 growth despite a large lattice mismatch. The epitaxial growth process offers a controllable method to obtain lateral heterojunction with an atomically sharp interface.

  15. Growth of Ca2MnO4 Ruddlesden-Popper structured thin films using combinatorial substrate epitaxy

    International Nuclear Information System (INIS)

    Lacotte, M.; David, A.; Pravarthana, D.; Prellier, W.; Grygiel, C.; Rohrer, G. S.; Salvador, P. A.; Velazquez, M.; Kloe, R. de

    2014-01-01

    The local epitaxial growth of pulsed laser deposited Ca 2 MnO 4 films on polycrystalline spark plasma sintered Sr 2 TiO 4 substrates was investigated to determine phase formation and preferred epitaxial orientation relationships (ORs) for isostructural Ruddlesden-Popper (RP) heteroepitaxy, further developing the high-throughput synthetic approach called Combinatorial Substrate Epitaxy (CSE). Both grazing incidence X-ray diffraction and electron backscatter diffraction patterns of the film and substrate were indexable as single-phase RP-structured compounds. The optimal growth temperature (between 650 °C and 800 °C) was found to be 750 °C using the maximum value of the average image quality of the backscattered diffraction patterns. Films grew in a grain-over-grain pattern such that each Ca 2 MnO 4 grain had a single OR with the Sr 2 TiO 4 grain on which it grew. Three primary ORs described 47 out of 49 grain pairs that covered nearly all of RP orientation space. The first OR, found for 20 of the 49, was the expected RP unit-cell over RP unit-cell OR, expressed as [100][001] film ||[100][001] sub . The other two ORs were essentially rotated from the first by 90°, with one (observed for 17 of 49 pairs) being rotated about the [100] and the other (observed for 10 of 49 pairs) being rotated about the [110] (and not exactly by 90°). These results indicate that only a small number of ORs are needed to describe isostructural RP heteroepitaxy and further demonstrate the potential of CSE in the design and growth of a wide range of complex functional oxides

  16. InGaAs quantum dots grown by molecular beam epitaxy for light emission on Si substrates.

    Science.gov (United States)

    Bru-Chevallier, C; El Akra, A; Pelloux-Gervais, D; Dumont, H; Canut, B; Chauvin, N; Regreny, P; Gendry, M; Patriarche, G; Jancu, J M; Even, J; Noe, P; Calvo, V; Salem, B

    2011-10-01

    The aim of this study is to achieve homogeneous, high density and dislocation free InGaAs quantum dots grown by molecular beam epitaxy for light emission on silicon substrates. This work is part of a project which aims at overcoming the severe limitation suffered by silicon regarding its optoelectronic applications, especially efficient light emission device. For this study, one of the key points is to overcome the expected type II InGaAs/Si interface by inserting the InGaAs quantum dots inside a thin silicon quantum well in SiO2 fabricated on a SOI substrate. Confinement effects of the Si/SiO2 quantum well are expected to heighten the indirect silicon bandgap and then give rise to a type I interface with the InGaAs quantum dots. Band structure and optical properties are modeled within the tight binding approximation: direct energy bandgap is demonstrated in SiO2/Si/InAs/Si/SiO2 heterostructures for very thin Si layers and absorption coefficient is calculated. Thinned SOI substrates are successfully prepared using successive etching process resulting in a 2 nm-thick Si layer on top of silica. Another key point to get light emission from InGaAs quantum dots is to avoid any dislocations or defects in the quantum dots. We investigate the quantum dot size distribution, density and structural quality at different V/III beam equivalent pressure ratios, different growth temperatures and as a function of the amount of deposited material. This study was performed for InGaAs quantum dots grown on Si(001) substrates. The capping of InGaAs quantum dots by a silicon epilayer is performed in order to get efficient photoluminescence emission from quantum dots. Scanning transmission electronic microscopy images are used to study the structural quality of the quantum dots. Dislocation free In50Ga50As QDs are successfully obtained on a (001) silicon substrate. The analysis of QDs capped with silicon by Rutherford Backscattering Spectrometry in a channeling geometry is also presented.

  17. Deep levels in a-plane, high Mg-content MgxZn1−xO epitaxial layers grown by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Gür, Emre; Tabares, G.; Hierro, A.; Arehart, A.; Ringel, S. A.; Chauveau, J. M.

    2012-01-01

    Deep level defects in n-type unintentionally doped a-plane Mg x Zn 1−x O, grown by molecular beam epitaxy on r-plane sapphire were fully characterized using deep level optical spectroscopy (DLOS) and related methods. Four compositions of Mg x Zn 1−x O were examined with x = 0.31, 0.44, 0.52, and 0.56 together with a control ZnO sample. DLOS measurements revealed the presence of five deep levels in each Mg-containing sample, having energy levels of E c − 1.4 eV, 2.1 eV, 2.6 V, and E v + 0.3 eV and 0.6 eV. For all Mg compositions, the activation energies of the first three states were constant with respect to the conduction band edge, whereas the latter two revealed constant activation energies with respect to the valence band edge. In contrast to the ternary materials, only three levels, at E c − 2.1 eV, E v + 0.3 eV, and 0.6 eV, were observed for the ZnO control sample in this systematically grown series of samples. Substantially higher concentrations of the deep levels at E v + 0.3 eV and E c − 2.1 eV were observed in ZnO compared to the Mg alloyed samples. Moreover, there is a general invariance of trap concentration of the E v + 0.3 eV and 0.6 eV levels on Mg content, while at least and order of magnitude dependency of the E c − 1.4 eV and E c − 2.6 eV levels in Mg alloyed samples.

  18. Metal modulation epitaxy growth for extremely high hole concentrations above 1019 cm-3 in GaN

    Science.gov (United States)

    Namkoong, Gon; Trybus, Elaissa; Lee, Kyung Keun; Moseley, Michael; Doolittle, W. Alan; Look, David C.

    2008-10-01

    The free hole carriers in GaN have been limited to concentrations in the low 1018cm-3 range due to the deep activation energy, lower solubility, and compensation from defects, therefore, limiting doping efficiency to about 1%. Herein, we report an enhanced doping efficiency up to ˜10% in GaN by a periodic doping, metal modulation epitaxy growth technique. The hole concentrations grown by periodically modulating Ga atoms and Mg dopants were over ˜1.5×1019cm-3.

  19. Metal modulation epitaxy growth for extremely high hole concentrations above 1019 cm-3 in GaN

    International Nuclear Information System (INIS)

    Namkoong, Gon; Trybus, Elaissa; Lee, Kyung Keun; Moseley, Michael; Doolittle, W. Alan; Look, David C.

    2008-01-01

    The free hole carriers in GaN have been limited to concentrations in the low 10 18 cm -3 range due to the deep activation energy, lower solubility, and compensation from defects, therefore, limiting doping efficiency to about 1%. Herein, we report an enhanced doping efficiency up to ∼10% in GaN by a periodic doping, metal modulation epitaxy growth technique. The hole concentrations grown by periodically modulating Ga atoms and Mg dopants were over ∼1.5x10 19 cm -3

  20. One unit-cell seed layer induced epitaxial growth of heavily nitrogen doped anatase TiO{sub 2} films

    Energy Technology Data Exchange (ETDEWEB)

    Chen, T L; Hirose, Y; Hitosugi, T; Hasegawa, T [Kanagawa Academy of Science and Technology (KAST), Kawasaki 213-0012 (Japan)], E-mail: chen@ksp.or.jp

    2008-03-21

    We present a novel way to obtain heavily nitrogen doped anatase TiO{sub 2} films by using a solid-state nitrogen source. Epitaxial growth of the films was realized by introducing one unit-cell seed layer, which was indicated by reflection high-energy electron diffraction as intensity oscillation. Results of x-ray diffraction and x-ray photoelectron spectroscopy confirmed that the films were in the anatase phase heavily doped with nitrogen of {approx}15 at%. The films obtained exhibited considerable narrowing of the optical bandgap, resulting in an enhancement of absorption in the visible-light region. (fast track communication)