WorldWideScience

Sample records for mocvd ybco films

  1. Deposition studies and coordinated characterization of MOCVD YBCO films on IBAD-MgO templates

    International Nuclear Information System (INIS)

    Aytug, T; Paranthaman, M; Heatherly, L; Zuev, Y; Zhang, Y; Kim, K; Goyal, A; Maroni, V A; Chen, Y; Selvamanickam, V

    2009-01-01

    A recently installed research-scale metal-organic chemical vapor deposition (MOCVD) system at Oak Ridge National Laboratory, provided by SuperPower, Inc., has been used to investigate processing variables for MOCVD YBCO precursors and trends in the resulting properties. Systematic studies of YBCO film growth on LaMnO 3 /IBAD-MgO templates were carried out by optimizing deposition temperature and oxygen flow rate. Microstructural and superconducting properties of the YBCO films were analyzed by x-ray diffraction, scanning electron microscopy and transport measurements. The identification of intermediate phases formed during the YBCO precursor transformation was investigated by coordinated reel-to-reel Raman microprobe analysis. With this combination of various characterization techniques, an improved understanding of the growth characteristics of MOCVD YBCO films was established. Finally, critical current densities greater than 2 MA cm -2 for film thicknesses of 0.8 μm were demonstrated.

  2. Deposition studies and coordinated characterization of MOCVD YBCO films on IBAD-MgO templates

    Energy Technology Data Exchange (ETDEWEB)

    Aytug, T; Paranthaman, M [Oak Ridge National Laboratory, Chemical Sciences Division, Oak Ridge, TN 37831 (United States); Heatherly, L; Zuev, Y; Zhang, Y; Kim, K; Goyal, A [Oak Ridge National Laboratory, Materials Science and Technology Division, Oak Ridge, TN 37831 (United States); Maroni, V A [Argonne National Laboratory, Chemical Sciences and Engineering Division, Argonne, IL 60439 (United States); Chen, Y; Selvamanickam, V [SuperPower, Incorporated, 450 Duane Avenue, Schenectady, NY 12304 (United States)], E-mail: aytugt@ornl.gov

    2009-01-15

    A recently installed research-scale metal-organic chemical vapor deposition (MOCVD) system at Oak Ridge National Laboratory, provided by SuperPower, Inc., has been used to investigate processing variables for MOCVD YBCO precursors and trends in the resulting properties. Systematic studies of YBCO film growth on LaMnO{sub 3}/IBAD-MgO templates were carried out by optimizing deposition temperature and oxygen flow rate. Microstructural and superconducting properties of the YBCO films were analyzed by x-ray diffraction, scanning electron microscopy and transport measurements. The identification of intermediate phases formed during the YBCO precursor transformation was investigated by coordinated reel-to-reel Raman microprobe analysis. With this combination of various characterization techniques, an improved understanding of the growth characteristics of MOCVD YBCO films was established. Finally, critical current densities greater than 2 MA cm{sup -2} for film thicknesses of 0.8 {mu}m were demonstrated.

  3. In-situ deposition of YBCO high-Tc superconducting thin films by MOCVD and PE-MOCVD

    International Nuclear Information System (INIS)

    Zhao, J.; Noh, D.W.; Chern, C.; Li, Y.Q.; Norris, P.E.; Kear, B.; Gallois, B.

    1991-01-01

    Metal-Organic Chemical Vapor Deposition (MOCVD) offers the advantages of a high degree of compositional control, adaptability for large scale production, and the potential for low temperature fabrication. The capability of operating at high oxygen partial pressure is particularly suitable for in situ formation of high temperature superconducting (HTSC) films. Yttrium barium copper oxide (YBCO) thin films having a sharp zero-resistance transition with T(sub c) greater than 90 K and J(sub c) of approximately 10(exp 4) A on YSZ have been prepared, in situ, at a substrate temperature of about 800 C. Moreover, the ability to form oxide films at low temperature is very desirable for device applications of HTSC materials. Such a process would permit the deposition of high quality HTSC films with a smooth surface on a variety of substrates. Highly c-axis oriented, dense, scratch resistant, superconducting YBCO thin films with mirror-like surfaces have been prepared, in situ, at a reduced substrate temperature as low as 570 C by a remote microwave-plasma enhanced metal-organic chemical vapor deposition (PE-MOCVD) process. Nitrous oxide was used as a reactant gas to generate active oxidizing species. This process, for the first time, allows the formation of YBCO thin films with the orthorhombic superconducting phase in the as-deposited state. The as-deposited films grown by PE-MOCVD show attainment of zero resistance at 72 K with a transition width of about 5 K. MOCVD was carried out in a commercial production scale reactor with the capability of uniform deposition over 100 sq cm per growth run. Preliminary results indicate that PE-MOCVD is a very attractive thin film deposition process for superconducting device technology

  4. Enhanced flux pinning in MOCVD-YBCO films through Zr additions : systematic feasibility studies.

    Energy Technology Data Exchange (ETDEWEB)

    Aytug, T.; Paranthaman, M.; Specht, E. D.; Zhang, Y.; Kim, K.; Zuev, Y. L.; Cantoni, C.; Goyal, A.; Christen, D. K.; Maroni, V. A.; Chen, Y.; Selvamanickam, V.; ORNL; SuperPower, Inc.

    2010-01-01

    Systematic effects of Zr additions on the structural and flux pinning properties of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) films deposited by metal-organic chemical vapor deposition (MOCVD) have been investigated. Detailed characterization, conducted by coordinated transport, x-ray diffraction, scanning and transmission electron microscopy analyses, and imaging Raman microscopy have revealed trends in the resulting property/performance correlations of these films with respect to varying mole percentages (mol%) of added Zr. For compositions {le} 7.5 mol%, Zr additions lead to improved in-field critical current density, as well as extra correlated pinning along the c-axis direction of the YBCO films via the formation of columnar, self-assembled stacks of BaZrO{sub 3} nanodots.

  5. Enhanced flux pinning in MOCVD-YBCO films through Zr additions: systematic feasibility studies

    International Nuclear Information System (INIS)

    Aytug, T; Paranthaman, M; Specht, E D; Zhang, Y; Kim, K; Zuev, Y L; Cantoni, C; Goyal, A; Christen, D K; Maroni, V A; Chen, Y; Selvamanickam, V

    2010-01-01

    Systematic effects of Zr additions on the structural and flux pinning properties of YBa 2 Cu 3 O 7-δ (YBCO) films deposited by metal-organic chemical vapor deposition (MOCVD) have been investigated. Detailed characterization, conducted by coordinated transport, x-ray diffraction, scanning and transmission electron microscopy analyses, and imaging Raman microscopy have revealed trends in the resulting property/performance correlations of these films with respect to varying mole percentages (mol%) of added Zr. For compositions ≤7.5 mol%, Zr additions lead to improved in-field critical current density, as well as extra correlated pinning along the c-axis direction of the YBCO films via the formation of columnar, self-assembled stacks of BaZrO 3 nanodots.

  6. Enhanced flux pinning in MOCVD-YBCO films through Zr additions: systematic feasibility studies

    Energy Technology Data Exchange (ETDEWEB)

    Aytug, T; Paranthaman, M; Specht, E D; Zhang, Y; Kim, K; Zuev, Y L; Cantoni, C; Goyal, A; Christen, D K [Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States); Maroni, V A [Argonne National Laboratory, Argonne, IL 60439 (United States); Chen, Y; Selvamanickam, V, E-mail: aytugt@ornl.go [SuperPower, Incorporated, 450 Duane Avenue, Schenectady, NY 12304 (United States)

    2010-01-15

    Systematic effects of Zr additions on the structural and flux pinning properties of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) films deposited by metal-organic chemical vapor deposition (MOCVD) have been investigated. Detailed characterization, conducted by coordinated transport, x-ray diffraction, scanning and transmission electron microscopy analyses, and imaging Raman microscopy have revealed trends in the resulting property/performance correlations of these films with respect to varying mole percentages (mol%) of added Zr. For compositions {<=}7.5 mol%, Zr additions lead to improved in-field critical current density, as well as extra correlated pinning along the c-axis direction of the YBCO films via the formation of columnar, self-assembled stacks of BaZrO{sub 3} nanodots.

  7. Preparation of SmBCO layer for the surface optimization of GdYBCO film by MOCVD process based on a simple self-heating technology

    Science.gov (United States)

    Zhao, Ruipeng; Zhang, Fei; Liu, Qing; Xia, Yudong; Lu, Yuming; Cai, Chuanbing; Tao, Bowan; Li, Yanrong

    2018-07-01

    The MOCVD process was adopted to grow the REBa2Cu3O7-δ ((REBCO), RE = rare earth elements) films on the LaMnO3 (LMO) templates. Meanwhile, the LMO-template tapes are heated by the joule effect after applying a heating current through the Hastelloy metal substrates. The surface of GdYBCO films prepared by MOCVD method is prone to form outgrowths. So the surface morphology of GdYBCO film is optimized by depositing the SmBCO layer, which is an important process method for the preparation of high-quality multilayer REBCO films. At last, the GdYBCO/SmBCO/GdYBCO multilayer films were successfully prepared on the LMO templates based on the simple self-heating method. It is demonstrated that the GdYBCO surface was well improved by the characterization analysis of scanning electron microscope. And the Δω of REBCO (005) and Δφ of REBCO (103), which were performed by an X-ray diffraction system, are respectively 1.3° and 3.3° What's more, the critical current density (Jc) has been more than 3 MA/cm2 (77 K, 0 T) and the critical current (Ic) basically shows a trend of good linear increase with the increase of the number of REBCO layers.

  8. Preparation of YBCO on YSZ layers deposited on silicon and sapphire by MOCVD: influence of the intermediate layer on the quality of the superconducting film

    International Nuclear Information System (INIS)

    Garcia, G.; Casado, J.; Llibre, J.; Doudkowski, M.; Santiso, J.; Figueras, A.; Schamm, S.; Dorignac, D.; Grigis, C.; Aguilo, M.

    1995-01-01

    YSZ buffer layers were deposited on silicon and sapphire by MOCVD. The layers deposited on silicon were highly oriented along [100] direction without in-plane orientation, probably because the existence of the SiO 2 amorphous interlayer. In contrast, epitaxial YSZ was obtained on (1-102) sapphire showing an in-plane texture defined by the following relationships: (100) YSZ // (1-102) sapphire and (110) YSZ // (01-12) sapphire. Subsequently, YBCO films were deposited on YSZ by MOCVD. Structural, morphological and electrical characterization of the superconducting layers were correlated with the in-plane texture of the buffer layers. (orig.)

  9. Textured YBCO films grown on wires: application to superconducting cables

    International Nuclear Information System (INIS)

    Dechoux, N; Jiménez, C; Chaudouët, P; Rapenne, L; Sarigiannidou, E; Robaut, F; Petit, S; Garaudée, S; Porcar, L; Soubeyroux, J L; Odier, P; Bruzek, C E; Decroux, M

    2012-01-01

    Efforts to fabricate superconducting wires made of YBa 2 Cu 3 O 7 (YBCO) on La 2 Zr 2 O 7 (LZO) buffered and biaxially textured Ni-5 at.%W (NiW) are described. Wires were manually shaped from LZO buffered NiW tapes. Different diameters were produced: 1.5, 2 and 3 mm. The wires were further covered with YBCO grown by metal organic chemical vapor deposition (MOCVD). We developed an original device in which the round substrate undergoes an alternated rotation of 180° around its axis in addition to a reel-to-reel translation. This new approach allows covering the whole circumference of the wire with a YBCO layer. This was confirmed by energy dispersive x-ray spectroscopy (EDX) analysis coupled to a scanning electron microscope (SEM). For all wire diameters, the YBCO layer thickness varied from 300 to 450 nm, and the cationic composition was respected. Electron backscattering diffraction (EBSD) measurements were performed directly on an as-deposited wire without surface preparation allowing the investigation of the crystalline quality of the film surface. Combining EBSD with XRD results we show that YBCO grows epitaxially on the LZO buffered NiW wires. For the first time, superconductive behaviors have been detected on round substrates in both the rolling and circular direction. J c reached 0.3 MA cm −2 as measured at 77 K by transport and third-harmonic detection. Those preliminary results confirm the effectiveness of the MOCVD for complex geometries, especially for YBCO deposition on small diameter wires. This approach opens huge perspectives for the elaboration of a new generation of YBCO-based round conductors. (paper)

  10. Microstructural and compositional analysis of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} films grown by MOCVD before and after GCIB smoothing

    Energy Technology Data Exchange (ETDEWEB)

    Hatzistergos, M.S.; Efstathiadis, H.; Reeves, J.L.; Selvamanickam, V.; Allen, L.P.; Lifshin, E.; Haldar, P

    2004-06-15

    The microstructural and compositional evolution of thick (>1 {mu}m) high temperature superconducting YBa{sub 2}Cu{sub 3}O{sub 7-x} (YBCO) films grown on single crystal SrTiO{sub 3} substrates by the metal organic chemical vapor deposition (MOCVD) process was investigated by focused ion beam microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, and atomic force microscopy. This study showed that as the MOCVD YBCO film thickness increased above 0.5 {mu}m, defects such as second phase particles, pores, and misaligned grains preferentially nucleated and grew at the YBCO surface. A portion of this defective top layer was eliminated from all the samples using a gas cluster ion beam (GCIB) process that first removed material with a focused argon cluster beam. Next, an oxygen cluster beam was used to smooth the surface and re-oxygenate the YBCO. Comparing the critical current (I{sub c}) measured before and after GCIB processing showed that the I{sub c} remained the same, and even improved, when part of the defective top layer was removed. This microstructural and electromagnetic 'dead layer' is believed to be responsible for the overall I{sub c} decrease of MOCVD YBCO films thicker than 0.5 {mu}m.

  11. Microstructural and compositional analysis of YBa2Cu3O7-δ films grown by MOCVD before and after GCIB smoothing

    International Nuclear Information System (INIS)

    Hatzistergos, M.S.; Efstathiadis, H.; Reeves, J.L.; Selvamanickam, V.; Allen, L.P.; Lifshin, E.; Haldar, P.

    2004-01-01

    The microstructural and compositional evolution of thick (>1 μm) high temperature superconducting YBa 2 Cu 3 O 7-x (YBCO) films grown on single crystal SrTiO 3 substrates by the metal organic chemical vapor deposition (MOCVD) process was investigated by focused ion beam microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, and atomic force microscopy. This study showed that as the MOCVD YBCO film thickness increased above 0.5 μm, defects such as second phase particles, pores, and misaligned grains preferentially nucleated and grew at the YBCO surface. A portion of this defective top layer was eliminated from all the samples using a gas cluster ion beam (GCIB) process that first removed material with a focused argon cluster beam. Next, an oxygen cluster beam was used to smooth the surface and re-oxygenate the YBCO. Comparing the critical current (I c ) measured before and after GCIB processing showed that the I c remained the same, and even improved, when part of the defective top layer was removed. This microstructural and electromagnetic 'dead layer' is believed to be responsible for the overall I c decrease of MOCVD YBCO films thicker than 0.5 μm

  12. Flux pinning in MOD YBCO films by chemical doping

    International Nuclear Information System (INIS)

    Zhou, Y X; Ghalsasi, S; Rusakova, I; Salama, K

    2007-01-01

    A novel nanomaterial synthesis technique has been developed to introduce 0D (particles), 1D (columnar defects) and 3D (domains) nanoscale pinning centres in MOD Y 1 Ba 2 Cu 3 O 7 (YBCO) coated conductors. We have succeeded in introducing nanoscale Y enriched particles, nanoscale 90 0 rotated Y 1/3 Sm 2/3 Ba 2 Cu 3 O 7 domains and nanoscale Zr enriched columnar defects into YBCO layers by different chemical doping. The pinning force density in Y 2 O 3 -doped YBCO film is found to be larger than that of pure YBCO film at all fields. Also it was found that YBCO films with Sm substituting for Y have yielded improved critical current density characteristics over a wide range of magnetic fields. Maximum pinning force densities exceeding 7 and 8 GN m -3 are obtained in 5% BZO-doped and Sm substituted YBCO films, respectively. Additionally, TEM studies revealed nanoscale Zr enriched columnar defects distributing in the matrix of the c-oriented YBCO film throughout the whole cross section. This indicates that chemical doping is a promising fabrication technique to create specific pinning landscapes in YBCO coated conductors

  13. Deposition of Y-Sm Oxide on Metallic Substrates for the YBCO Coated Conductor by MOCVD Method

    International Nuclear Information System (INIS)

    Choi, Jun Kyu; Kim, Min Woo; Jun, Byung Hyuk; Kim, Chan Joong; Lee, Hee Gyoun; Hong, Gye Won

    2005-01-01

    Complex single buffer composed of yttrium and samarium oxide was deposited on the metallic substrates by MOCVD (metal organic chemical vapor deposition) method using single liquid source. Two different types of the substrates with in-plane textures of about 8 - 10 degree of Ni and 3at.%W-Ni alloy were used. Y(tmhd: 2,2,6,6-tetramethyl-3,5-heptane dionate) 3 :Sm(tmhd) 3 of liquid source was adjusted to 0.4:0.6 to minimize the lattice mismatch between the complex single buffer and the YBCO. The epitaxial growth of (Y x Sm 1-x ) 2 O 3 was achieved at the temperature higher than 500 degree C in O 2 atmosphere. However, it was found that the formation of NiO accelerated with increasing deposition temperature. By supplying H 2 O vapor, this oxidation of the substrate could be suppressed throughout the deposition temperatures. We could get the epitaxial growth on pure Ni substrate without the formation of NiO. The competitive (222) and (400) growths were observed at the deposition temperatures of 650 - 750 degree C, but the (400) growth became dominant above 800 degree. The (Y x Sm 1-x ) 2 O 3 -buffered metallic substrates can be used as the buffer for YBCO coated conductor.

  14. YBa2Cu3O7-δ thin films deposited by MOCVD vertical reactor with a flow guide

    International Nuclear Information System (INIS)

    Sujiono, E.H.; Negeri Makassar; Sani, R.A.; Saragi, T.; Arifin, P.; Barmawi, M.

    2001-01-01

    The effect of a flow guide in a vertical MOCVD reactor on the deposition uniformity and growth rate of thin YBCO films has been studied. Without the flow guide the growth rates are low, have a poor uniformity and the film composition is not stoichiometric. The growth rate of the films grown using a reactor with the flow guide was approximately twice that without the flow guide. Using this flow guide the growth rates were 0.4-0.7 μm/h for growth temperatures varying between 600 and 750 C, and the crystalline quality as well as the surface morphology of YBCO films on MgO substrates is improved. For films grown at temperatures above 650 C the composition of Y:Ba:Cu is 1:2:3, as confirmed by EDAX spectra. Films deposited without and with the flow guide at 700 C have critical temperatures around 85 and 88 K, respectively. The reduction in ΔT c (T c,zero -T c,onset ) also shows an improvement of the superconducting properties of YBCO thin films deposited with a flow guide. (orig.)

  15. Thermodynamic investigation of the MOCVD of copper films from bis ...

    Indian Academy of Sciences (India)

    Equilibrium concentrations of various condensed and gaseous phases have been thermodynamically calculated, using the free energy minimization criterion, for the metalorganic chemical vapour deposition (MOCVD) of copper films using bis(2,2,6,6-tetramethyl-3,5-heptadionato)copper(II) as the precursor material.

  16. Preparation of YBCO superconducting films by spray pyrolysis method

    International Nuclear Information System (INIS)

    Mora Alonso, M.; Leyva Fabelo, A.; Rubio Frias, E.; Pupo Gonzalez, I.; Lopez Sanchez, D.

    1994-01-01

    The methodology for the preparation of YBCO superconducting films on Zr 2O (Y) substrates by spray pyrolysis method is reported. The transition temperature of these films is superior than the boiling temperature of liquid 2N . Other critical parameters are similar to those reported by other authors using the same technique

  17. Thermoelectric properties of ZnSb films grown by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Venkatasubramanian, R; Watko, E; Colpitts, T

    1997-07-01

    The thermoelectric properties of ZnSb films grown by metallorganic chemical vapor deposition (MOCVD) are reported. The growth conditions necessary to obtain stoichiometric ZnSb films and the effects of various growth parameters on the electrical conductivity and Seebeck coefficients of the films are described. The as-grown ZnSb films are p-type. It was observed that the thicker ZnSb films offer improved carrier mobilities and lower free-carrier concentration levels. The Seebeck coefficient of ZnSb films was found to rise rapidly at approximately 160 C. The thicker films, due to the lower doping levels, indicate higher Seebeck coefficients between 25 to 200 C. A short annealing of the ZnSb film at temperatures of {approximately}200 C results in reduced free-carrier level. Thermal conductivity measurements of ZnSb films using the 3-{omega} method are also presented.

  18. Two different mechanisms of fatigue damage due to cyclic stress loading at 77 K for MOCVD-YBCO-coated conductors

    International Nuclear Information System (INIS)

    Sugano, M; Yoshida, Y; Hojo, M; Shikimachi, K; Hirano, N; Nagaya, S

    2008-01-01

    Tensile fatigue tests were carried out at 77 K for YBCO-coated conductors fabricated by metal-organic chemical vapor deposition (MOCVD). The S-N relationship, variation of critical current (I c ) during cyclic loading and microscopic fatigue damage were investigated. Fatigue strength at 10 6 cycles was evaluated to be σ max = 1300 MPa and 890 MPa under the stress ratios of 0.5 and 0.1. Two different mechanisms of fatigue damage, depending on the number of stress cycles to failure, were observed. In one of the fracture mechanisms, fatigue behavior is characterized by overall fracture which occurs at 10 4 -10 5 cycles. For these specimens, I c after unloading does not degrade before overall fracture. Although only shallow slip bands were found at the Ag surface, fatigue cracks were found on the Hastelloy C-276 surface of the fractured specimen. These results suggest that overall fracture due to cyclic stress was caused by fatigue of the Hastelloy substrate. In the other fracture mechanism, even though overall fracture did not occur at 10 6 cycles, a slight decrease of I c was detected after 10 5 cycles. No fatigue crack was found on the Hastelloy surface, while deep slip bands corresponding to the initial stage of fatigue crack were observed on the Ag surface. From these results, we concluded that I c degradation at a high cycle number is attributed to the fatigue of the Ag stabilizing layer

  19. Strong Flux Pinning of Nano-Sized Ysz Particles in Ybco Films Prepared by Mod Method

    Science.gov (United States)

    Ye, S.; Suo, H. L.; Liu, M.; Tang, X.; Wu, Z. P.; Zhao, Y.; Zhou, M. L.

    The YBCO films with doped YSZ nanoparticles have been prepared successfully by metal organic doepositon method using trifluoroacetates (TFA-MOD) through dissolving Zr organic salt into the YBCO precursor solution. The doped films have well in-plane and out-plane textures detected by both XRD Φ-scan and ω-scan. The YSZ nanoparticles with the size of about 5 ~ 15 nm were observed on the surface of the YBCO films using both FE-SEM and TEM. By comparing the superconducting properties, it was found that the doped YBCO films had lower Tc than that of undoped YBCO films. However, as increasing the applied magnetic field, Jc of the doped YBCO films were much better than that of undoped one. The Jc was as higher as 2.5 times than that of undoped YBCO film at 77 K and 1 T applied field.

  20. Vortex pinning landscape in MOD-TFA YBCO nanostroctured films

    Science.gov (United States)

    Gutierrez, J.; Puig, T.; Pomar, A.; Obradors, X.

    2008-03-01

    A methodology of general validity to study vortex pinning in YBCO based on Jc transport measurements is described. It permits to identify, separate and quantify three basic vortex pinning contributions associated to anisotropic-strong, isotropic-strong and isotropic-weak pinning centers. Thereof, the corresponding vortex pinning phase diagrams are built up. This methodology is applied to the new solution-derived YBCO nanostructured films, including controlled interfacial pinning by the growth of nanostructured templates by means of self-assembled processes [1] and YBCO-BaZrO3 nanocomposites prepared by modified solution precursors. The application of the methodology and comparison with a standard solution-derived YBCO film [2], enables us to identify the nature and the effect of the additional pinning centers induced. The nanostructured templates films show c-axis pinning strongly increased, controlling most of the pinning phase diagram. On the other hand, the nanocomposites have achieved so far, the highest pinning properties in HTc-superconductors [3], being the isotropic-strong defects contribution the origin of their unique properties. [1] M. Gibert et al, Adv. Mat. vol 19, p. 3937 (2007) [2] Puig.T et al, SuST EUCAS 2007 (to be published) [3] J. Gutierrez et al, Nat. Mat. vol. 6, p. 367 (2007) * Work supported by HIPERCHEM, NANOARTIS and MAT2005-02047

  1. Quality of YBCO thin films grown on LAO substrates exposed to the film deposition - film removal processes

    Energy Technology Data Exchange (ETDEWEB)

    Blagoev, B; Nurgaliev, T [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tzarigradsko Chaussee, 1784 Sofia (Bulgaria); Mozhaev, P B [Institute of Physics and Technology, Russian Academy of Sciences, 117218 Moscow (Russian Federation); Sardela, M; Donchev, T [Materials Research Laboratory, University of Illinois, 104 South Goodwin Ave., Urbana, IL 61801 (United States)], E-mail: blago_sb@yahoo.com

    2008-05-01

    The characteristics are investigated of high temperature superconducting YBa{sub 2}Cu{sub 3}O{sub 7} (YBCO) films grown on LaAlO{sub 3} (LAO) substrates being exposed a different number of times to YBCO film deposition and acid-solution-based cleaning procedures. Possible mechanisms of degradation of the substrate surface quality reflecting on the growing YBCO film parameters are discussed and analyzed.

  2. Alkaline-doped manganese perovskite thin films grown by MOCVD

    International Nuclear Information System (INIS)

    Bibes, M.; Gorbenko, O.; Martinez, B.; Kaul, A.; Fontcuberta, J.

    2000-01-01

    We report on the preparation and characterization of La 1-x Na x MnO 3 thin films grown by MOCVD on various single-crystalline substrates. Under appropriate conditions epitaxial thin films have been obtained. The Curie temperatures of the films, which are very similar to those of bulk samples of similar composition, reflect the residual strain caused by the substrate. The anisotropic magnetoresistance AMR of the films has been analyzed in some detail, and it has been found that it has a two-fold symmetry at any temperature. Its temperature dependence mimics that of the electrical resistivity and magnetoresistance measured at similar fields, thus suggesting that the real structure of the material contributes to the measured AMR besides the intrinsic component

  3. Thermoelectric properties of ZnSb films grown by MOCVD

    International Nuclear Information System (INIS)

    Venkatasubramanian, R.; Watko, E.; Colpitts, T.

    1997-04-01

    The thermoelectric properties of metallorganic chemical vapor deposited (MOCVD) ZnSb films are reported. The growth conditions necessary to obtain stoichiometric ZnSb films and the effects of various growth parameters on the electrical conductivity and Seebeck coefficients of the films are described. The as-grown ZnSb films are p-type. It was observed that the growth of thicker ZnSb films lead to improved carrier mobilities and lower free-carrier concentrations. The Seebeck coefficient of ZnSb films was found to rise rapidly at approximately 160 to 170 C, with peak Seebeck coefficients as high as 470 microV/K at 220 C. The various growth conditions, including the use of intentional dopants, to improve the Seebeck coefficients at room temperature and above, are discussed. A short annealing of the ZnSb films at temperatures of ∼ 200 C resulted in reduced free-carrier levels and higher Seebeck coefficients at 300 K. Finally, ZT values based on preliminary thermal conductivity measurements using the 3-ω method are reported

  4. Preparation of molybdenum oxide thin films by MOCVD

    International Nuclear Information System (INIS)

    Guerrero, R. Martinez; Garcia, J.R. Vargas; Santes, V.; Gomez, E.

    2007-01-01

    In this study, molybdenum oxide films were prepared in a horizontal hot-wall MOCVD apparatus using molybdenum dioxide acetylacetonate as precursor. The molybdenum precursor was synthesized from acetylacetone and molybdenum oxide powder. Thermal gravimetric (TG) and differential thermal analyses (DTA) of the precursor suggested the formation of molybdenum oxides around 430 o C (703 K). Thus, a range of deposition temperatures varying from 350 to 630 o C (623-903 K) was explored to investigate the effects on the nature of the molybdenum oxide films. X-ray diffraction (XRD) results showed that the films consisted of α-MoO 3 phase at deposition temperatures ranging from 400 to 560 o C (673-833 K). Crystalline α-MoO 3 films can be obtained from molybdenum dioxide acetylacetonate precursor, without need of a post-annealing treatment. The best crystalline quality was found in films having needle-like crystallites grown at deposition temperature of about 560 o C (833 K), which exhibit a strong (0 1 0) preferred orientation and a transparent visual appearance

  5. Preparation of molybdenum oxide thin films by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Guerrero, R. Martinez [Depto. de Ingenieria Metalurgica, ESIQIE-IPN, Mexico 07300, D.F. (Mexico); Garcia, J.R. Vargas [Depto. de Ingenieria Metalurgica, ESIQIE-IPN, Mexico 07300, D.F. (Mexico)]. E-mail: rvargasga@ipn.mx; Santes, V. [CIIEMAD-IPN, Miguel Othon de Mendizabal 485, Mexico 07700, D.F. (Mexico); Gomez, E. [Instituto de Quimica-UNAM, Circuito Exterior-Ciudad Universitaria, Mexico 04510, D.F. (Mexico)

    2007-05-31

    In this study, molybdenum oxide films were prepared in a horizontal hot-wall MOCVD apparatus using molybdenum dioxide acetylacetonate as precursor. The molybdenum precursor was synthesized from acetylacetone and molybdenum oxide powder. Thermal gravimetric (TG) and differential thermal analyses (DTA) of the precursor suggested the formation of molybdenum oxides around 430 {sup o}C (703 K). Thus, a range of deposition temperatures varying from 350 to 630 {sup o}C (623-903 K) was explored to investigate the effects on the nature of the molybdenum oxide films. X-ray diffraction (XRD) results showed that the films consisted of {alpha}-MoO{sub 3} phase at deposition temperatures ranging from 400 to 560 {sup o}C (673-833 K). Crystalline {alpha}-MoO{sub 3} films can be obtained from molybdenum dioxide acetylacetonate precursor, without need of a post-annealing treatment. The best crystalline quality was found in films having needle-like crystallites grown at deposition temperature of about 560 {sup o}C (833 K), which exhibit a strong (0 1 0) preferred orientation and a transparent visual appearance.

  6. Flux pinning characteristics of Sn-doped YBCO film by the MOD process

    International Nuclear Information System (INIS)

    Choi, S.M.; Shin, G.M.; Yoo, S.I.

    2013-01-01

    Highlights: ► The pinning effects of undoped and Sn-doped YBCO films by MOD were characterized. ► Sn-containing nanoparticles were trapped in Sn-doped YBCO films by MOD. ► Sn-containing nanoparticles were identified as the YBa 2 SnO 5.5 (YBSO) phase by TEM. ► The YBSO nanoparticles are responsible for improved flux pinning effect. ► We report the orientation relationship between YBSO nanoparticles and YBCO matrix. -- Abstract: Compared with the undoped YBa 2 Cu 3 O 7−δ (YBCO) film, 10 mol% Sn-doped YBCO film exhibited significantly enhanced critical current densities (J c ) in magnetic fields up to 5 T at 65 and 77 K for H//c, indicating that the Sn-doped YBCO film possesses more effective flux pinning centers. Both samples were grown on the SrTiO 3 (STO) (1 0 0) single crystal substrates by the metal-organic deposition (MOD) process. Larger J c (77 K, 1 T) values of Sn-doped YBCO film are observed over a wide field-orientation angle (θ) except the field-orientations close to the ab-plane of YBCO (85° c values for 85° 2 SnO 5.5 (YBSO) phase by STEM (scanning transmission electron microscopy)-EDS (energy dispersive X-ray spectroscopy) analysis. Further analyses by HR-TEM (high resolution-transmission electron microscopy) revealed that YBSO nanoparticles completely surrounded by the YBCO matrix had random orientation with YBCO while those located at the interface of YBCO/STO substrate had epitaxial relationship with YBCO

  7. Growth of YBCO superconducting thin films on CaF sub 2 buffered silicon

    CERN Document Server

    Bhagwat, S S; Patil, J M; Shirodkar, V S

    2000-01-01

    CaF sub 2 films were grown on silicon using the neutral cluster beam deposition technique. These films were highly crystalline and c-axis oriented. Superconducting YBCO thin films were grown on the Ca F sub 2 buffered silicon using the laser ablation technique. These films showed T sub c (onset) at 90 K and Tc(zero) at 86 K. X-ray diffraction analysis showed that the YBCO films were also oriented along the c-axis.

  8. Nano-engineered pinning centres in YBCO superconducting films

    Energy Technology Data Exchange (ETDEWEB)

    Crisan, A., E-mail: adrian.crisan@infim.ro [National Institute for Materials Physics Bucharest, 105 bis Atomistilor Str., 077125 Magurele (Romania); School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Dang, V.S. [School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Nano and Energy Center, VNU Hanoi University of Science, 334 Nguyen Trai, Thanh Xuan, Hanoi (Viet Nam); Mikheenko, P. [School of Metallurgy and Materials, University of Birmingham, Edgbaston, B15 2TT Birmingham (United Kingdom); Department of Physics, University of Oslo, P.O. Box 1048 Blindern, N-0316 Oslo (Norway)

    2017-02-15

    Highlights: • Power applications of YBCO films/coated conductors in technological relevant magnetic fields requires nano-engineered pinning centre. • Three approaches have been proposed: substrate decoration, quasi-multilayers, and targets with secondary phase nano-inclusions. • Combination of all three approaches greatly increased critical current in YBCO films. • Bulk pinning force, pinning potential, and critical current density are estimated and discussed in relation with the type and strength of pinning centres related to the defects evidenced by Transmission Electron Microscopy. - Abstract: For practical applications of superconducting materials in applied magnetic fields, artificial pinning centres in addition to natural ones are required to oppose the Lorentz force. These pinning centres are actually various types of defects in the superconductor matrix. The pinning centres can be categorised on their dimension (volume, surface or point) and on their character (normal cores or Δκ cores). Different samples have been produced by Pulsed Laser Deposition, with various thicknesses, temperatures and nanostructured additions to the superconducting matrix. They have been characterized by SQUID Magnetic Properties Measurement System and Physical Properties Measurement System, as well as by Transmission Electron Microscopy (TEM). Correlations between pinning architecture, TEM images, and critical currents at various fields and field orientations will be shown for a large number of YBa{sub 2}Cu{sub 3}O{sub x} films with various types and architectures of artificial pinning centres.

  9. Structure and oxygen incorporation in low pressure sputtered YBCO films

    International Nuclear Information System (INIS)

    Chaudhary, S.; Pandya, D. K.; Kashyap, S. C.

    2002-01-01

    Thin films of YBa 2 Cu 3 O 7- δ (YBCO) have been successfully grown by reactive RF-magnetron sputtering technique at low pressure. The oxygen partial pressure of 0.95 mTorr, a total pressure (argon and oxygen) of 1.9 mTorr, and a substrate temperature of 775 grad C resulted in good quality films with T C (R=0) = 85.3 K and J Cmag (4.2 K) ≅ 2x10 7 A/cm 2 . The incorporation of oxygen in the as-grown films has been controlled by using different ambient - oxygen, air or argon during in-situ cooling. The superconducting behaviour of the films was studied using resistance-temperature and low field ac-susceptibility measurements and correlated with their structure. All the films exhibited metallic conduction in the normal state. The oxygen- and air- cooled films were superconducting, possessing the usual orthorhombic structure. The argon-cooled films were non-superconducting possessing the tetragonal structure, thus implying that the structure of the film during deposition is tetragonal which transforms to either of the oxygen rich orthorhombic-I or -II phases depending upon the oxygen/air ambient. The 'δ' values of 0.14, 0.32 and 0.70 and higher 'c'-parameters of 1.1785, 1.180 and 1.183 nm have been obtained for oxygen, air and argon cooled films respectively. (Authors)

  10. Preparation and structural properties of YBCO films grown on GaN/c-sapphire hexagonal substrate

    Energy Technology Data Exchange (ETDEWEB)

    Chromik, S., E-mail: stefan.chromik@savba.sk [Institute of Electrical Engineering, SAS, Dubravska cesta 9, 84104 Bratislava (Slovakia); Gierlowski, P. [Institute of Physics, Polish Academy of Sciences, Al. Lotnikow 32/46, 02-668 Warsaw (Poland); Spankova, M.; Dobrocka, E.; Vavra, I.; Strbik, V.; Lalinsky, T.; Sojkova, M. [Institute of Electrical Engineering, SAS, Dubravska cesta 9, 84104 Bratislava (Slovakia); Liday, J.; Vogrincic, P. [Department of Microelectronics, Slovak Technical University, Ilkovicova 3, 81219 Bratislava (Slovakia); Espinos, J.P. [Instituto de Ciencia de Materiales de Sevilla, Avda Americo Vespucio 49, 41092 Sevilla (Spain)

    2010-07-01

    Epitaxial YBCO thin films have been grown on hexagonal GaN/c-sapphire substrates using DC magnetron sputtering and pulsed laser deposition. An MgO buffer layer has been inserted between the substrate and the YBCO film as a diffusion barrier. X-ray diffraction analysis indicates a c-axis oriented growth of the YBCO films. {Phi}-scan shows surprisingly twelve maxima. Transmission electron microscopy analyses confirm an epitaxial growth of the YBCO blocks with a superposition of three a-b YBCO planes rotated by 120 deg. to each other. Auger electron spectroscopy and X-ray photoelectron spectroscopy reveal no surface contamination with Ga even if a maximum substrate temperature of 700 deg. C is applied.

  11. Growth and BZO-doping of the nanostructured YBCO thin films on buffered metal substrates

    DEFF Research Database (Denmark)

    Huhtinen, H.; Irjala, M.; Paturi, P.

    2010-01-01

    The growth of the nanostructured YBa2Cu3O6+x (YBCO) films is investigated for the first time on biaxially textured NiW substrates used in coated conductor technology. The optimization process of superconducting layers is made in wide magnetic field and temperature range in order to understand...... the vortex pinning structure and mechanism in our films prepared from nanostructured material. Structural analysis shows that growth mechanism in YBCO films grown on NiW is completely different when compared to YBCO on STO. Films on NiW are much rougher, there is huge in-plane variation of YBCO crystals...... and moreover out-of-plane long range lattice ordering is greatly reduced. Magnetic measurements demonstrate that jc in films grown on NiW is higher in high magnetic fields and low temperatures. This effect is connected to the amount of pinning centres observed in films on metal substrates which are effective...

  12. Enhanced flux-pinning in fluorine-free MOD YBCO films by chemical doping

    Energy Technology Data Exchange (ETDEWEB)

    Wang, W.T.; Pu, M.H.; Yang, Y. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Zhang, H. [Department of Physics, Peking University, Beijing 100871 (China); Cheng, C.H. [Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia); Zhao, Y., E-mail: yzhao@swjtu.edu.c [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia)

    2010-11-01

    YBCO films without and with dilute cobalt and zinc doping were prepared on (0 0 l) LaAlO{sub 3} substrate by non-fluorine metal organic deposition method. Effects of dilute cobalt and zinc doping on biaxial texture, microstructure and flux-pinning properties of YBCO films were investigated. The surface density and smoothness of the doped YBCO films have been distinctly improved compared with that of the pure film. Dilute cobalt- and zinc-doped YBCO films exhibit significantly enhanced J{sub c} values in the magnetic field. The best result is achieved in the cobalt-doped YBCO film. At 77 K, J{sub c} values of cobalt-doped film are 1.7 and 5.4 times higher than that of pure film in 0.5 T and 1.5 T, respectively. These results strongly suggest that dilute cobalt and zinc doping is a promising way to increase the current carrying capability of YBCO films.

  13. YBa2Cu3O7 films prepared by aerosol MOCVD

    International Nuclear Information System (INIS)

    Weiss, F.; Froehlich, K.; Haase, R.; Labeau, M.; Selbmann, D.; Senateur, J.P.; Thomas, O.

    1993-01-01

    In the present study we report on properties of YBa 2 Cu 3 O 7 films prepared by aerosol MOCVD. We give a short description of the process and we focus on the superconducting and related properties of the films deposited on SrTiO 3 , LaAlO 3 and NdGaO 3 single crystalline substrates. (orig.)

  14. High quality uniform YBCO film growth by the metalorganic deposition using trifluoroacetates

    Energy Technology Data Exchange (ETDEWEB)

    Wang, S.S., E-mail: wangssh@tsinghua.edu.cn [Key Laboratory of Micro-nano Measurement, Manipulation and Physics (Beihang University), Ministry of Education, Beijing 100191 (China); Beijing Dingchen Superconducting Technology Co., Ltd., Beijing 100084 (China); Zhang, Z.L. [Key Laboratory of Micro-nano Measurement, Manipulation and Physics (Beihang University), Ministry of Education, Beijing 100191 (China); Wang, L. [Applied superconductivity research center, Department of Physics, Tsinghua University, Beijing 100084 (China); Gao, L.K.; Liu, J. [Beijing Dingchen Superconducting Technology Co., Ltd., Beijing 100084 (China)

    2017-03-15

    Highlights: • High quality double-sided YBCO films are fabricated on LaAlO3 substrates by TFA-MOD method with diameters up to 2 in. • Large area YBCO films were very uniform in microstructure and thickness distribution, an average inductive Jc in excess of 6 MA/cm{sup 2} and low R{sub s} (10 GHz) of 0.3 mΩ at 77 K were obtained. • It will greatly promoted the research and applications of large-area YBCO films by chemical solution method. - Abstract: A need exists for the large-area superconducting YBa{sub 2}Cu{sub 3}O{sub 7-x} (YBCO) films with high critical current density for microwave communication and/or electric power applications. Trifluoroacetic metalorganic (TFA-MOD) method is a promising low cost technique for large-scale production of YBCO films, because it does not need high vacuum device and is easily applicable to substrates of various shape and size. In this paper, double-sided YBCO films with maximum 2 in diameter were prepared on LaAlO{sub 3} substrates by TFA-MOD method. Inductive critical current densitiy J{sub c}, microwave surface resistance R{sub s}, as well as the microstructure were characterized. A newly homemade furnace system was used to epitaxially grown YBCO films, which can improve the uniformity of YBCO film significantly by gas supply and temperature distribution proper design. Results showed that the large area YBCO films were very uniform in microstructure and thickness distribution, an average inductive J{sub c} in excess of 6 MA/cm{sup 2} with uniform distribution, and low R{sub s} (10 GHz) below 0.3 mΩ at 77 K were obtained. Andthe film filter may be prepared to work at temperatures lower than 74 K. These results are very close to the highest value of YBCO films made by conventional vacuum method, so we show a very promising route for large-scale production of high quality large-area YBCO superconducting films at a lower cost.

  15. Chemical solution deposition of YBCO thin film by different polymer additives

    International Nuclear Information System (INIS)

    Wang, W.T.; Li, G.; Pu, M.H.; Sun, R.P.; Zhou, H.M.; Zhang, Y.; Zhang, H.; Yang, Y.; Cheng, C.H.; Zhao, Y.

    2008-01-01

    A polymer-assisted chemical solution deposition approach has been proposed for the preparation of YBCO thin film. Different additives like PVB (polyvinyl butyral), PEG (polyethylene glycol) and PVP (polyvinylpyrrolidone) have been used to adjust the final viscosity of the precursor solution and thus the film formation. In this fluorine-free approach, YBCO has been deposited on single crystal substrates with metal acetates being starting materials. Biaxially textured YBCO thin films have been obtained. However, different additives lead to different microstructure. Dense, smooth and crack-free YBCO film prepared with PVB as additive yields sharp superconducting transition around T c = 90 K as well as high J c (0 T, 77 K) over 3 MA/cm 2

  16. Chemical solution deposition of YBCO thin film by different polymer additives

    Energy Technology Data Exchange (ETDEWEB)

    Wang, W.T.; Li, G.; Pu, M.H.; Sun, R.P.; Zhou, H.M.; Zhang, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); Zhang, H. [Department of Physics, Peking University, Beijing 100871 (China); Yang, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); Cheng, C.H. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia); Zhao, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains, Ministry of Education of China, Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia)], E-mail: yzhao@swjtu.edu.cn

    2008-09-15

    A polymer-assisted chemical solution deposition approach has been proposed for the preparation of YBCO thin film. Different additives like PVB (polyvinyl butyral), PEG (polyethylene glycol) and PVP (polyvinylpyrrolidone) have been used to adjust the final viscosity of the precursor solution and thus the film formation. In this fluorine-free approach, YBCO has been deposited on single crystal substrates with metal acetates being starting materials. Biaxially textured YBCO thin films have been obtained. However, different additives lead to different microstructure. Dense, smooth and crack-free YBCO film prepared with PVB as additive yields sharp superconducting transition around T{sub c} = 90 K as well as high J{sub c} (0 T, 77 K) over 3 MA/cm{sup 2}.

  17. BaF2 POST-DEPOSITION REACTION PROCESS FOR THICK YBCO FILMS

    International Nuclear Information System (INIS)

    SUENAGA, M.; SOLOVYOV, V.F.; WU, L.; WIESMANN, H.J.; ZHU, Y.

    2001-01-01

    The basic processes of the so-called BaF 2 process for the formation of YBa 2 Cu 3 O 7 , YBCO, films as well as its advantages over the in situ formation processes are discussed in the previous chapter. The process and the properties of YBCO films by this process were also nicely described in earlier articles by R. Feenstra, (et al.) Here, we will discuss two pertinent subjects related to fabrication of technologically viable YBCO conductors using this process. These are (1) the growth of thick (>> 1 microm) c-axis-oriented YBCO films and (2) their growth rates. Before the detail discussions of these subjects are given, we first briefly discuss what geometrical structure a YBCO-coated conductor should be. Then, we will provide examples of simple arguments for how thick the YBCO films and how fast their growth rates need to be. Then, the discussions in the following two sections are devoted to: (1) the present understanding of the nucleation and the growth process for YBCO, and why it is so difficult to grow thick c-axis-oriented films (> 3 microm), and (2) our present understanding of the YBCO growth-limiting mechanism and methods to increase the growth rates. The values of critical-current densities J c in these films are of primary importance for the applications,. and the above two subjects are intimately related to the control of J c of the films. In general, the lower the temperatures of the YBCO formation are the higher the values of J c of the films. Thus, the present discussion is limited to those films which are reacted at ∼735 C. This is the lowest temperature at which c-axis-oriented YBCO films (1-3 microm thick) are comfortably grown. It is also well known that the non-c-axis oriented YBCO platelets are extremely detrimental to the values of J c such that their effects on J c dwarf essentially all of other microstructural effects which control J c . Hence, the discussion given below is mainly focused on how to avoid the growth of these crystallites

  18. Magnetron sputtering of Fe-oxides on the top of HTS YBCO films

    International Nuclear Information System (INIS)

    Nurgaliev, T.; Blagoev, B.; Buchkov, K.; Mateev, E.; Gajda, G.; Nedkov, I.; Kovacheva, D.; Slavov, L.; Starbova, I.; Starbov, N.; Nankovski, M.

    2017-01-01

    The possibilities for preparation of bilayers containing magnetic Fe-oxide (Fe-O) and high temperature superconducting (HTS) YBa 2 Cu 3 O 7−x (YBCO) thin films were investigated. For this purpose, Fe-O films were deposited using reactive magnetron sputtering at comparatively low temperatures T≤250 °C onto dielectric (for example, LaAlO 3 (LAO)) substrates, covered with a HTS YBCO film. The sputtering of the Fe-O layer at such conditions did not lead to a crucial damage of the critical temperature T C of the YBCO film, but could affect the width of the superconducting transition. A decrease of the critical temperature of the (Fe-O)/YBCO/LAO bilayer kept at ambient conditions was observed, possibly due to the negative effects of the water vapour on the sample characteristics. The double peak structure of the imaginary component of the response signal to the AC harmonic magnetic field, observed in such a (Fe-O)/YBCO/LAO sample, was ascribed from two possible views: as a consequence of morphology determined inter- and intra-granular contributions and/or as transitions from dominant irreversible processes as Bean-Livingston barrier to vortex state chains formation. - Highlights: • Iron-oxide (Fe-O) film sputtered on the top of superconducting HTS YBCO film at not very high temperatures. • No crucially damaged superconducting properties of YBCO film during Fe-O sputtering process. • A negative effect of the ambient conditions on the critical temperature of the obtained samples. • A double peak structure of the response signal to the AC harmonic magnetic field in a (Fe-O)/YBCO/LAO is observed.

  19. Magnetron sputtering of Fe-oxides on the top of HTS YBCO films

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Blagoev, B. [Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Laboratory of High Magnetic Fields and Low Temperatures, 95 Gajowicka Str., 53-421 Wroclaw (Poland); Buchkov, K. [Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Mateev, E. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Gajda, G. [Laboratory of High Magnetic Fields and Low Temperatures, 95 Gajowicka Str., 53-421 Wroclaw (Poland); Nedkov, I. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Kovacheva, D. [Institute of General and Inorganic Chemistry, Bulgarian Academy of Sciences, Acad. G. Bonchev Street, bl. 10, 1113 Sofia (Bulgaria); Slavov, L. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Laboratory of High Magnetic Fields and Low Temperatures, 95 Gajowicka Str., 53-421 Wroclaw (Poland); Starbova, I.; Starbov, N. [Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Nankovski, M. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Sofia university “St. Kliment Ohridski”, Faculty of Physics, 5 James Bourchier Blvd., 1164 Sofia (Bulgaria)

    2017-05-01

    The possibilities for preparation of bilayers containing magnetic Fe-oxide (Fe-O) and high temperature superconducting (HTS) YBa{sub 2}Cu{sub 3}O{sub 7−x} (YBCO) thin films were investigated. For this purpose, Fe-O films were deposited using reactive magnetron sputtering at comparatively low temperatures T≤250 °C onto dielectric (for example, LaAlO{sub 3} (LAO)) substrates, covered with a HTS YBCO film. The sputtering of the Fe-O layer at such conditions did not lead to a crucial damage of the critical temperature T{sub C} of the YBCO film, but could affect the width of the superconducting transition. A decrease of the critical temperature of the (Fe-O)/YBCO/LAO bilayer kept at ambient conditions was observed, possibly due to the negative effects of the water vapour on the sample characteristics. The double peak structure of the imaginary component of the response signal to the AC harmonic magnetic field, observed in such a (Fe-O)/YBCO/LAO sample, was ascribed from two possible views: as a consequence of morphology determined inter- and intra-granular contributions and/or as transitions from dominant irreversible processes as Bean-Livingston barrier to vortex state chains formation. - Highlights: • Iron-oxide (Fe-O) film sputtered on the top of superconducting HTS YBCO film at not very high temperatures. • No crucially damaged superconducting properties of YBCO film during Fe-O sputtering process. • A negative effect of the ambient conditions on the critical temperature of the obtained samples. • A double peak structure of the response signal to the AC harmonic magnetic field in a (Fe-O)/YBCO/LAO is observed.

  20. Thermodynamic analysis of growth of iron oxide films by MOCVD ...

    Indian Academy of Sciences (India)

    Abstract. Thermodynamic calculations, using the criterion of minimization of total Gibbs free energy of the system, have been carried out for the metalorganic chemical vapour deposition (MOCVD) process involving the -ketoesterate complex of iron [tris(-butyl-3-oxo-butanoato)iron(III) or Fe(tbob)3] and molecular oxygen.

  1. Enhancement of flux pinning of TFA-MOD YBCO thin films by embedded nanoscale Y2O3

    International Nuclear Information System (INIS)

    Cui, X M; Tao, B W; Tian, Z; Xiong, J; Zhang, X F; Li, Y R

    2006-01-01

    YBCO films with different levels of excess yttrium were prepared on single-crystal LaAlO 3 with metal-organic deposition using trifluoroacetates (TFA-MOD). X-ray diffraction and transmission electron microscope measurements revealed excess yttrium in YBCO in the form of nanoscale Y 2 O 3 with (400) preferred orientation. The field dependence of J c demonstrated that YBCO films with Y 2 O 3 doping had enhanced J c in comparison with stoichiometric YBCO films in the magnetic fields. We think the reason for this is that the Y 2 O 3 nanoparticles act as pinning centres. YBCO films with 60% yttrium excess display 43% increased J c compared to stoichiometric YBCO films at a magnetic field of 1 T

  2. The effect of a thin silver layer on the critical current of epitaxial YBCO films

    International Nuclear Information System (INIS)

    Polturak, E.; Koren, G.; Cohen, D.; Cohen, D.; Snapiro, I.

    1992-01-01

    We compare measurements of the critical current density of an epitaxial YBCO film with that of an identical film overlaid by a thin silver layer. We find that the presence of the silver lowers Tc of the film by about 1.5 K, which is two orders of magnitude larger than predicted by the theory of the proximity effect for our experimental conditions. In addition, J c of the Ag/YBCO film near Tc is also significantly lower than that of the bare YBCO film. We propose two alternate interpretations of this effect, one in terms of destabilization of the flux distribution in the film and the other making use of the effect of the silver on the Bean-Livingston surface barrier for the initial penetration of flux. The latter seems the more plausible explanation of our results. (orig.)

  3. Low energy electron beam processing of YBCO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Chromik, Š., E-mail: stefan.chromik@savba.sk [Institute of Electrical Engineering, SAS, Dúbravská cesta 9, 841 04 Bratislava (Slovakia); Camerlingo, C. [CNR-SPIN, Istituto Superconduttori, Materiali Innovativi e Dispositivi, via Campi Flegrei 34, 80078 Pozzuoli (Italy); Sojková, M.; Štrbík, V.; Talacko, M. [Institute of Electrical Engineering, SAS, Dúbravská cesta 9, 841 04 Bratislava (Slovakia); Malka, I.; Bar, I.; Bareli, G. [Department of Physics, Ben Gurion University of the Negev, P.O.B. 653, 84105 Beer Sheva (Israel); Jung, G. [Department of Physics, Ben Gurion University of the Negev, P.O.B. 653, 84105 Beer Sheva (Israel); Institute of Physics, Polish Academy of Sciences, Al. Lotników 32/46, 02-668 Warsaw (Poland)

    2017-02-15

    Highlights: • Improvement of superconducting properties of irradiated bridges under certain conditions. • 30 keV irradiation influence CuO{sub 2} planes as well as oxygen chains. • Direct confirmation of changes in oxygen chains using micro-Raman spectroscopy. • Possibility of electron writing. - Abstract: Effects of low energy 30 keV electron irradiation of superconducting YBa{sub 2}Cu{sub 3}O{sub 7−δ} thin films have been investigated by means of transport and micro-Raman spectroscopy measurements. The critical temperature and the critical current of 200 nm thick films initially increase with increasing fluency of the electron irradiation, reach the maximum at fluency 3 − 4 × 10{sup 20} electrons/cm{sup 2}, and then decrease with further fluency increase. In much thinner films (75 nm), the critical temperature increases while the critical current decreases after low energy electron irradiation with fluencies below 10{sup 20} electrons/cm{sup 2}. The Raman investigations suggest that critical temperature increase in irradiated films is due to healing of broken Cu−O chains that results in increased carrier’s concentration in superconducting CuO{sub 2} planes. Changes in the critical current are controlled by changes in the density of oxygen vacancies acting as effective pinning centers for flux vortices. The effects of low energy electron irradiation of YBCO turned out to result from a subtle balance of many processes involving oxygen removal, both by thermal activation and kick-off processes, and ordering of chains environment by incident electrons.

  4. Effect of argon addition into oxygen atmosphere on YBCO thin films deposition

    International Nuclear Information System (INIS)

    Mozhaev, P. B.; Borisenko, I. V.; Ovsyannikov, G. A.; Kuehle, A.; Bindslev-Hansen, J.; Johannes, L.; Skov, J. L.

    2002-01-01

    Multicomponent nature of the YBa 2 Cu 3 O x (YBCO) high-temperature superconductor makes difficult fabrication of smooth thin films: every local deviation from stoichiometry can result in seeding of a non-superconducting oxide particle. High density of such particles on typical YBCO thin film surface, however, presumes overall non-stoichiometry of the film. Such an effect can result from (i) non-uniform material transport from target to substrate, and (ii) re-evaporation or re-sputtering from the growing film surface. The first reason is more usual for laser ablation deposition technique, the second is typical for long sputtering deposition processes. Substitution of oxygen with argon in the deposition atmosphere improves surface quality of YBCO thin films deposited both by laser ablation and DC-sputtering at high pressure techniques. In the first case, the ablated species are scattered different ways in the oxygen atmosphere. Addition of argon decreases the inelastic scattering of barium; the proper part of Ar in the deposition atmosphere makes scattering and, hence, transport of all atoms uniform. The YBCO films deposited by DC-sputtering at high pressure technique are Ba-deficient also, but the reason is re-sputtering of Ba from the growing film as a result of negative oxygen ions bombardment. Such bombardment can lead also to chemical interaction of the deposited material with the substrate, as in the case of deposition of YBCO thin film on the CeO 2 buffer layer on sapphire. Substitution of oxygen with argon not only suppresses ion bombardment of the film, but also increases discharge stability due to presence of positive Ar + ions. The limiting factor of argon substitution is sufficient oxygenation of the growing oxide film. When oxygen partial pressure is too small, the superconducting quality of the YBCO thin film decreases and such a decrease cannot be overcome by prolonged oxygenation after deposition. (Authors)

  5. Intermediate Phase Study on YBCO Films Coated by Precursor Solutions With F/Ba Atomic Ratio of 2

    DEFF Research Database (Denmark)

    Wu, W.; Feng, F.; Zhao, Y.

    2016-01-01

    In the chemical solution deposition process of YBCO superconducting films, fluorine is widely regarded to be of significant importance in avoiding the formation of BaCO3, which hinders the growth of high-quality YBCO films. On the other hand, great efforts have been made to decrease the fluorine......) could be routinely obtained on lanthanum aluminate single-crystal substrates....

  6. Pulsed laser deposition of YBCO films on ISD MgO buffered metal tapes

    CERN Document Server

    Ma, B; Koritala, R E; Fisher, B L; Markowitz, A R; Erck, R A; Baurceanu, R; Dorris, S E; Miller, D J; Balachandran, U

    2003-01-01

    Biaxially textured magnesium oxide (MgO) films deposited by inclined-substrate deposition (ISD) are desirable for rapid production of high-quality template layers for YBCO-coated conductors. High-quality YBCO films were grown on ISD MgO buffered metallic substrates by pulsed laser deposition (PLD). Columnar grains with a roof-tile surface structure were observed in the ISD MgO films. X-ray pole figure analysis revealed that the (002) planes of the ISD MgO films are tilted at an angle from the substrate normal. A small full-width at half maximum (FWHM) of approx 9deg was observed in the phi-scan for ISD MgO films deposited at an inclination angle of 55deg . In-plane texture in the ISD MgO films developed in the first approx 0.5 mu m from the substrate surface, and then stabilized with further increases in film thickness. Yttria-stabilized zirconia and ceria buffer layers were deposited on the ISD MgO grown on metallic substrates prior to the deposition of YBCO by PLD. YBCO films with the c-axis parallel to the...

  7. An all-field-range description of the critical current density in superconducting YBCO films

    International Nuclear Information System (INIS)

    Golovchanskiy, I A; Pan, A V; Shcherbakova, O V; Fedoseev, S A; Dou, S X

    2011-01-01

    A new critical current density (J c ) model for high-quality YBCO (YBa 2 Cu 3 O 7 ) thin films has been proposed, combining thermally activated flux creep with a vortex pinning potential for columnar defects. The pinning for thermally activated vortices has been described as strong pinning on chains of individual edge dislocations that form low-angle domain boundaries in high-quality YBCO thin films. The model yields an adequate description of the J c behaviour over the whole applied field range, as verified by direct measurements of J c in YBCO thin films grown by pulsed-laser deposition. It also indicates that the effective pinning landscape changes under the influence of the external conditions. Remarkably, the pinning potential obtained from the model is consistent with the values obtained for columnar defects, which confirms the validity of the overall approach.

  8. Mechanical characterization of YBCO thin films using nanoindentation and finite element method

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Weixing [The Ministry of Education of China (China). Key Lab. of Mechanics on Environment and Disaster in Western China; Lanzhou Univ. (China). College of Civil Engineering and Mechanics

    2017-09-15

    The mechanical properties of YBCO thin film deposited on SrTiO{sub 3} (100) substrates by magnetron sputtering were determined using Berkovich nanoindentation and scanning electron microscopy. Hardness and elastic modulus were determined via the Oliver-Pharr method from indentation load-depth curves. The hardness values of the YBCO thin film show depth dependence, i. e., indentation size effect, which arose from the surface roughness as detected by scanning electron microscopy. Multiple pop-in events were observed on the loading curves, however, no obvious pop-out takes place during the elastic recovery. In addition, an effective analytical method accommodating the indenter imperfection was proposed and validated against experimental data in terms of elastic modulus, yield stress and friction angle using the Drucker-Prager yield criterion for the YBCO thin film.

  9. Surface resistances of 5-cm-diameter YBCO films prepared by MOD for microwave applications

    International Nuclear Information System (INIS)

    Manabe, T.; Sohma, M.; Yamaguchi, I.; Tsukada, K.; Kondo, W.; Kamiya, K.; Tsuchiya, T.; Mizuta, S.; Kumagai, T.

    2006-01-01

    Large-area high-T c superconducting films with low surface resistances R s are required for use in microwave applications such as band pass filters. In this paper, preparation of 5-cm-diameter YBCO films on LaAlO 3 (LAO) and CeO 2 -buffered sapphire (CbS) substrates by metalorganic deposition (MOD) using a fluorine-free coating solution and their superconducting properties are described. The optimum firing conditions for YBCO films greatly depend on the substrate materials; a heating rate at ramp as high as 200 deg. C /min is necessary for films on LAO whereas a lower heating rate, e.g., 20 deg. C /min, is required for films on CbS. Accordingly, the suitable furnace systems for these substrates have been varied. As a result, a YBCO film with high J c (77 K) of 2.7 MA/cm 2 and a low R s (12 GHz, 77 K) of 0.54 mΩ was prepared on LAO by using an infrared image furnace. On the other hand, a YBCO film with a higher J c (77 K) of 4.0 MA/cm 2 and the same R s (12 GHz, 77 K) of 0.54 mΩ was prepared on CbS by using a tube furnace

  10. Transparent conductive Ga-doped ZnO films fabricated by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Behrends, Arne; Wagner, Alexander; Al-Suleiman, Mohamed Aid Mansur; Waag, Andreas; Bakin, Andrey [Institute of Semiconductor Technology, University of Technology Braunschweig, Hans-Sommer-Str. 66, 38106 Braunschweig (Germany); Lugauer, Hans-Juergen; Strassburg, Martin; Walter, Robert; Weimar, Andreas [OSRAM Opto Semiconductors GmbH, Leibnizstr. 4, 93055 Regensburg (Germany)

    2012-04-15

    Transparent conductive oxides (TCOs) are used for a variety of different applications, e.g., in solar cells and light emitting diodes (LEDs). Mostly, sputtering is used, which often results in a degradation of the underlying semiconductor material. In this work we report on a ''soft'' method for the fabrication of ZnO films as TCO layers by using metal organic chemical vapor deposition (MOCVD) at particularly low temperatures. The MOCVD approach has been studied focusing on the TCO key issues: fabrication temperature, morphology, optical, and electrical properties. Very smooth ZnO films with rms values down to 0.8 nm were fabricated at a substrate temperature of only 300 C. Ga-doping is well controllable even for high carrier concentrations up to 2 x 10{sup 20} cm{sup -3}, which is above the Mott-density leading to metallic-like behavior of the films. Furthermore all films show excellent optical transparency in the visible spectral range. As a consequence, our MOCVD approach is well suited for the soft fabrication of ZnO-based TCO layers. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  11. Electrical properties of ZnO thin films grown by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Pagni, O. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa); Somhlahlo, N.N. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa); Weichsel, C. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa); Leitch, A.W.R. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa)]. E-mail: andrew.leitch@nmmu.ac.za

    2006-04-01

    We report on the electrical characterization of ZnO films grown by MOCVD on glass and sapphire substrates. After correcting our temperature variable Hall measurements by applying the standard two-layer model, which takes into account an interfacial layer, scattering mechanisms in the ZnO films were studied as well as donor activation energies determined. ZnO films grown at different oxygen partial pressures indicated the importance of growth conditions on the defect structure by means of their conductivities and conductivity activation energies.

  12. Electrical properties of ZnO thin films grown by MOCVD

    International Nuclear Information System (INIS)

    Pagni, O.; Somhlahlo, N.N.; Weichsel, C.; Leitch, A.W.R.

    2006-01-01

    We report on the electrical characterization of ZnO films grown by MOCVD on glass and sapphire substrates. After correcting our temperature variable Hall measurements by applying the standard two-layer model, which takes into account an interfacial layer, scattering mechanisms in the ZnO films were studied as well as donor activation energies determined. ZnO films grown at different oxygen partial pressures indicated the importance of growth conditions on the defect structure by means of their conductivities and conductivity activation energies

  13. MOCVD growth of transparent conducting Cd2SnO4 thin films

    International Nuclear Information System (INIS)

    Metz, A.W.; Poeppelmeier, K.R.; Marks, T.J.; Lane, M.A.; Kannewurt, C.R.

    2004-01-01

    The first preparation of transparent conducting Cd 2 SnO 4 thin films by a simple MOCVD process is described. As-deposited films using Cd(hfa) 2 (TMEDA) (Figure), at 365 C are found to be highly crystalline with a relatively wide range of grain size of 100-300 nm. XRD indicates a cubic spinel Cd 2 SnO 4 crystal structure and the possible presence of a small amount of CdO. The films exhibit conductivities of 2170 S/cm and a bandgap of 3.3 eV, rivaling those of commercial tin-doped indium oxide. (Abstract Copyright [2004], Wiley Periodicals, Inc.)

  14. Resistive switching phenomenon and hole wind effect in YBCO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Truchly, Martin; Plecenik, Tomas [Department of Experimental Physics, Comenius University, Bratislava (Slovakia); Zhitlukhina, Elena [Donetsk Institute for Physics and Engineering, Kyiv (Ukraine)

    2016-07-01

    We present an overview of our experimental and theoretical activities aimed to clarify the mechanism of resistive memory effects in YBCO thin layers. The phenomenon was studied by scanning spreading resistance microscopy (SSRM) and scanning tunneling microscopy (STM) techniques. The most striking feature uncovered (in contrast to previous experiments on planar bilayers with YBCO films) was the opposite voltage-bias polarity of the switching effect in all SSRM and a number of STM measurements. Observed hysteresis in current-voltage characteristics is interpreted as a movement of oxygen vacancies in the vicinity of the tip-YBCO contact. Since the charge distribution in YBCO samples is expected to be strongly inhomogeneous, the balance between the direct electrostatic force on activated oxygen ions and that caused by momentum exchange with the current carriers (holes) hitting them determines direction in which the oxygen vacancies are moving. We propose a minimalist model with the only fitting parameter that accounts for the resistance hysteresis phenomenon in the YBCO films studied.

  15. Influence of interface reactions on the YBCO films grown by fluorine-free solution route

    DEFF Research Database (Denmark)

    Zhao, Yue; Wu, Wei; Tang, Xiao

    2015-01-01

    Fabrication of full-stacked coated conductors by all-chemical-solution routes exhibit a great potential in view of further reducing the cost and increasing the throughput for industrialization. Growth of YBa2Cu3O7−x (YBCO) superconducting films by fluorine-free metal organic deposition routes (FF......-MOD) which are environmental friendly has attracted more attentions recently. In this work, comparison study was performed on the YBCO-Ag superconducting thin films deposited on two types of single crystal substrates, LaAlO3 and Ce0.9La0.9O2−y/YSZ. The structural characterization and superconducting...... properties studies reveal that the interface reactions between the YBCO-Ag film and the CLO cap layer play an essential role on the nucleation and growth of YBCO-Ag films from the FF solution. Weak texture caused by serious interface reactions at high growth temperature is the main explanations for the poor...

  16. Pulsed-laser-deposited YBCO thin films using modified MTG processed targets

    CERN Document Server

    Kim, C H; Kim, I T; Hahn, T S

    1999-01-01

    YBCO thin films were deposited by pulsed laser deposition from targets fabricated using the modified melt-textured growth (MTG) method and the solid-state sintering (SSS) method. All of the films showed c-axis orientations, but the films from the MTG targets had better crystallinity than those from the SSS targets. As the substrate temperature was increased, T sub c and J sub c of the films increased. The films from the MTG targets showed better superconducting properties than those from the SSS targets. From the composition analysis of the targets, the Y-richer vapor species arriving at the substrate from the MTG targets are thought to form a thermodynamically more stable YBCO phase with less cation disorder.

  17. MOCVD ZnO/Screen Printed Ag Back Reflector for Flexible Thin Film Silicon Solar Cell Application

    Directory of Open Access Journals (Sweden)

    Amornrat Limmanee

    2014-01-01

    Full Text Available We have prepared Ag back electrode by screen printing technique and developed MOCVD ZnO/screen printed Ag back reflector for flexible thin film silicon solar cell application. A discontinuity and poor contact interface between the MOCVD ZnO and screen printed Ag layers caused poor open circuit voltage (Voc and low fill factor (FF; however, an insertion of a thin sputtered ZnO layer at the interface could solve this problem. The n type hydrogenated amorphous silicon (a-Si:H film is preferable for the deposition on the surface of MOCVD ZnO film rather than the microcrystalline film due to its less sensitivity to textured surface, and this allowed an improvement in the FF. The n-i-p flexible amorphous silicon solar cell using the MOCVD ZnO/screen printed Ag back reflector showed an initial efficiency of 6.2% with Voc=0.86 V, Jsc=12.4 mA/cm2, and FF = 0.58 (1 cm2. The identical quantum efficiency and comparable performance to the cells using conventional sputtered Ag back electrode have verified the potential of the MOCVD ZnO/screen printed Ag back reflector and possible opportunity to use the screen printed Ag thick film for flexible thin film silicon solar cells.

  18. TiO2 thin film growth using the MOCVD method

    Directory of Open Access Journals (Sweden)

    Bernardi M.I.B.

    2001-01-01

    Full Text Available Titanium oxide (TiO2 thin films were obtained using the MOCVD method. In this report we discuss the properties of a film, produced using a ordinary deposition apparatus, as a function of the deposition time, with constant deposition temperature (90 °C, oxygen flow (7,0 L/min and substrate temperature (400 °C. The films were characterized by X-ray diffraction (XRD, scanning electron microscopy (SEM, atomic force microscopy (AFM and visible and ultra-violet region spectroscopy (UV-Vis. The films deposited on Si (100 substrates showed the anatase polycrystalline phase, while the films grown on glass substrates showed no crystallinity. Film thickness increased with deposition time as expected, while the transmittance varied from 72 to 91% and the refractive index remained close to 2.6.

  19. Distribution analysis of thermal effusivity for sub-micrometer YBCO thin films using thermal microscope

    International Nuclear Information System (INIS)

    Yagi, T.; Taketoshi, N.; Kato, H.

    2004-01-01

    Thermal effusivity measurements have been carried out for sub-micrometer YBCO superconducting films using thermal microscope based upon thermoreflectance technique. Two samples were prepared: c-axis aligned YBCO thin films with 800 nm in thickness synthesized on MgO and SrTiO 3 substrates. Measured thermal effusivities perpendicular to the surface, i.e. in parallel with c-axis were determined to be 1770 J/m 2 s 0.5 K on MgO substrate and 1420 J/m 2 s 0.5 K for that on SrTiO 3 substrate, respectively. The scatter of the measurements is estimated to be lower than ±5.2%. These values are consistent with reported values of YBCO single crystal in the direction of c-axis. In addition, 2D profiling image, that is, in-plane distribution of thermal effusivity was well obtained for the YBCO film on MgO substrate by operating this thermal microscope in a scanning mode. Its standard deviation of the in-plane thermal effusivity scattering due to the non-uniformity is evaluated to be ±5.7%

  20. Plasma-enhanced chemical vapor deposition for YBCO film fabrication of superconducting fault-current limiter

    Energy Technology Data Exchange (ETDEWEB)

    Jun, Byung Hyuk; Kim, Chan Joong

    2006-05-15

    Since the high-temperature superconductor of oxide type was founded, many researches and efforts have been performed for finding its application field. The YBCO superconducting film fabricated on economic metal substrate with uniform critical current density is considered as superconducting fault-current limiter (SFCL). There are physical and chemical processes to fabricate superconductor film, and it is understood that the chemical methods are more economic to deposit large area. Among them, chemical vapor deposition (CVD) is a promising deposition method in obtaining film uniformity. To solve the problems due to the high deposition temperature of thermal CVD, plasma-enhanced chemical vapor deposition (PECVD) is suggested. This report describes the principle and fabrication trend of SFCL, example of YBCO film deposition by PECVD method, and principle of plasma deposition.

  1. Crystalline, Optical and Electrical Properties of NiZnO Thin Films Fabricated by MOCVD

    International Nuclear Information System (INIS)

    Wang Jin; Wang Hui; Zhao Wang; Ma Yan; Li Wan-Cheng; Shi Zhi-Feng; Zhao Long; Zhang Bao-Lin; Dong Xin; Du Guo-Tong; Xia Xiao-Chuan

    2011-01-01

    NiZnO thin films are grown on c-plane sapphire substrates by using a photo-assisted metal organic chemical vapor deposition (MOCVD) system. The effect of the Ni content on the crystalline, optical and electrical properties of the films are researched in detail. The NiZnO films could retain a basic wurtzite structure when the Ni content is less than 0.18. As Ni content increases, crystal quality degradation could be observed in the x-ray diffraction patterns and a clear red shift of the absorption edge can be observed in the transmittance spectrum. Furthermore, the donor defects in the NiZnO film can be compensated for effectively by increasing the Ni content. The change of Ni content has an important effect on the properties of NiZnO films. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  2. Characterisation of titanium nitride films obtained by metalorganic chemical vapor deposition (MOCVD); Caracterizacao de filmes de nitreto de titanio obtidos por MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Pillis, M.F., E-mail: mfpillis@ipen.b [Instituto de Pesquisas Energeticas e Nucleares (CCTM/IPEN/CNEN-SP), Sao Paulo, SP (Brazil). Centro de Ciencia e Tecnologia de Materiais; Franco, A.C. [Universidade de Sao Paulo (IF/USP), SP (Brazil). Inst. de Fisica; Araujo, E.G. de [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil); Sacilotti, M. [Universidade Federal de Pernambuco (IF/UFPE), Recife, PE (Brazil). Inst. de Fisica; Fundacao de Amparo a Ciencia e Tecnologia de Pernambuco (FACEPE), Recife, PE (Brazil)

    2009-07-01

    Ceramic coatings have been widely used as protective coating to improve the life of cutting tools, for corrosion protection and in microelectronics, optical and medical areas. Transition metals nitrides are of special interest due to its high hardness and thermal stability. In this work thin films of titanium nitride were obtained by MOCVD (metalorganic chemical vapor deposition) process. The tests were carried out for 1h at 700 deg C under 80 and 100 mbar of pressure. The characterization was made by using scanning electron microscopy coupled with dispersive energy analysis, and X-ray diffraction. Preliminary results suggested that Ti{sub 2}N phase was formed and that the growth rate varied between 4 and 13 nm/min according to the process parameter considered. (author)

  3. Preparation of PZT thin films on YBCO electrodes by KrF excimer laser ablation technique

    International Nuclear Information System (INIS)

    Kurogi, H.; Yamagata, Y.; Ebihara, K.

    1998-01-01

    Pb(Zr X Ti 1-X )O 3 (PZT) films have excellent ferroelectric, optical, piezoelectric, and pyroelectric properties. We prepared PZT thin films by the excimer laser ablation technique. A pulsed KrF excimer laser (Lambda Physik LPX305icc, pulse duration of 25 ns, λ=248 nm, 850 mJ Max.) was used to ablate the bulk targets. We investigated the influence of bottom electrode materials on the characteristics of the PZT thin films prepared on Pt and YBCO underlayers. The X-ray diffraction (XRD) patterns showed that the PZT films prepared with a laser fluence of 2 Jcm -2 on YBCO/MgO(100) substrate at a wide temperature range of 550-680 C have a perovskite (001) structure. At the same laser fluence, the PZT films prepared on Pt/MgO(100) substrate have a perovskite (001) structure only at 650 C. The polarization-electric field (P-E) characteristics and fatigue properties of PZT thin films were measured by the Sawyer-Tower circuit. The remnant polarization and coercive field have been found to be P r =15 μC cm -2 , 30 μC cm -2 and E c =200 kV cm -1 , 100 kV cm -1 for Au/PZT/Pt/MgO and Au/PZT/YBCO/MgO correspondingly. The remnant polarization of Au/PZT/YBCO/MgO thin film was reduced to one-half after about 10 8 cycles of switching. (orig.)

  4. Preparation of PZT thin films on YBCO electrodes by KrF excimer laser ablation technique

    Energy Technology Data Exchange (ETDEWEB)

    Kurogi, H; Yamagata, Y; Ebihara, K [Kumamoto Univ. (Japan). Dept. of Electr. Eng. and Comput. Sci.; Inoue, N [Kyushu Electric Power Co., Inc., Suizenji, 1-6-36, Kumamoto 862 (Japan)

    1998-03-01

    Pb(Zr{sub X}Ti{sub 1-X})O{sub 3} (PZT) films have excellent ferroelectric, optical, piezoelectric, and pyroelectric properties. We prepared PZT thin films by the excimer laser ablation technique. A pulsed KrF excimer laser (Lambda Physik LPX305icc, pulse duration of 25 ns, {lambda}=248 nm, 850 mJ Max.) was used to ablate the bulk targets. We investigated the influence of bottom electrode materials on the characteristics of the PZT thin films prepared on Pt and YBCO underlayers. The X-ray diffraction (XRD) patterns showed that the PZT films prepared with a laser fluence of 2 Jcm{sup -2} on YBCO/MgO(100) substrate at a wide temperature range of 550-680 C have a perovskite (001) structure. At the same laser fluence, the PZT films prepared on Pt/MgO(100) substrate have a perovskite (001) structure only at 650 C. The polarization-electric field (P-E) characteristics and fatigue properties of PZT thin films were measured by the Sawyer-Tower circuit. The remnant polarization and coercive field have been found to be P{sub r}=15 {mu}C cm{sup -2}, 30 {mu}C cm{sup -2} and E{sub c}=200 kV cm{sup -1}, 100 kV cm{sup -1} for Au/PZT/Pt/MgO and Au/PZT/YBCO/MgO correspondingly. The remnant polarization of Au/PZT/YBCO/MgO thin film was reduced to one-half after about 10{sup 8} cycles of switching. (orig.) 7 refs.

  5. Evaluation on current-limiting performance of the YBCO thin-film wire considering electric coupling condition

    International Nuclear Information System (INIS)

    Du, H.-I.; Han, B.-S.; Kim, Y.-J.; Lee, D.-H.; Song, S.-S.; Han, T.-H.; Han, S.-C.

    2011-01-01

    The basic way to improve the performance of a superconducting current limiter is to apply and evaluate a superconducting device that is appropriate to the superconducting current limiter. Among the many types of superconducting devices, the YBCO thin film wire has excellent current-limiting performance that is appropriate for actual system application. For the application of the YBCO thin film wire to superconducting current limiters, its current-limiting performance as a unit device must be accurately evaluated, and measures to improve its current-limiting performance must be sought. Accordingly, to evaluate the current-limiting performance of the YBCO thin film wire, this study was conducted to evaluate its resistance-increasing trend, V max , T r , I max , I qt , and current-limiting rate as a unit device, after which the electric coupling condition that consists of a core and windings was used to evaluate the current-limiting performance of the YBCO thin film wire.

  6. Composition and microstructure of beryllium carbide films prepared by thermal MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    He, Yu-dan; Luo, Jiang-shan; Li, Jia; Meng, Ling-biao; Luo, Bing-chi; Zhang, Ji-qiang; Zeng, Yong; Wu, Wei-dong, E-mail: wuweidongding@163.com

    2016-02-15

    Highlights: • Non-columnar-crystal Be{sub 2}C films were firstly prepared by thermal MOCVD. • Beryllium carbide was always the dominant phase in the films. • α-Be and carbon existed in films deposited below and beyond 400 °C, respectively. • Morphology evolved with temperatures and no columnar grains were characterized. • The preferred substrate temperature for depositing high quality Be{sub 2}C films was 400 °C. - Abstract: Beryllium carbide films without columnar-crystal microstructures were prepared on the Si (1 0 0) substrate by thermal metal organic chemical vapor deposition using diethylberyllium as precursor. The influence of the substrate temperature on composition and microstructure of beryllium carbide films was systematically studied. Crystalline beryllium carbide is always the dominant phase according to XRD analysis. Meanwhile, a small amount of α-Be phase exists in films when the substrate temperature is below 400 °C, and hydrocarbon or amorphous carbon exists when the temperature is beyond 400 °C. Surfaces morphology shows transition from domes to cylinders, to humps, and to tetraquetrous crystalline needles with the increase of substrate temperature. No columnar grains are characterized throughout the thickness as revealed from the cross-section views. The average densities of these films are determined to be 2.04–2.17 g/cm{sup 3}. The findings indicate the substrate temperature has great influences on the composition and microstructure of the Be{sub 2}C films grown by thermal MOCVD.

  7. Intermediate phase evolution in YBCO thin films grown by the TFA process

    International Nuclear Information System (INIS)

    Zalamova, K; Pomar, A; Palau, A; Puig, T; Obradors, X

    2010-01-01

    The YBCO thin film growth process from TFA precursors involves a complex reaction path which includes several oxide, fluoride and oxyfluoride intermediate phases, and the final microstructure and properties of the films are strongly influenced by the morphological and chemical evolution of these intermediate phases. In this work we present a study of the evolution of the intermediate phases involved in the TFA YBCO growth process under normal pressure conditions and we show that the oxygen partial pressure during pyrolysis of the TFA precursors is an important parameter. The Cu phase after the TFA pyrolysis can be either CuO, Cu 2 O or a mixture of both as the oxygen partial pressure is modified. The kinetics evolution of the intermediate phases has been determined for films pyrolysed in oxygen and nitrogen atmospheres and it is concluded that non-equilibrium phase transformations influence the reaction path towards epitaxial YBCO films and its microstructure. The intermediate phase evolution in these two series of films is summarized in kinetic phase diagrams.

  8. Dependence of critical current density on crystalline direction in thin YBCO films

    DEFF Research Database (Denmark)

    Paturi, P.; Peurla, M.; Raittila, J.

    2005-01-01

    The dependence of critical current density (J(c)) on the angle between the current direction and the (100) direction in the ab-plane of thin YBCO films deposited on (001)-SrTiO3 from natiocrystalline and microcrystalline targets is studied using magneto-optical microscopy. In the films made from...... the nanocrystalline target it is found that J(c) does not depend on the angle whereas J(c) decreases with increasing angle in the films made from the microcrystalline target. The films were characterized by detailed X-ray diffraction measurements. The findings are explained in terms of a network of planar defects...

  9. Photodegradative properties of TiO{sub 2} films prepared by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Justicia, I.; Ayllon, J.A.; Figueras, A. [Consejo Superior de Investigaciones Cientificas, Barcelona (Spain). Inst. de Ciencia de Materiales; Battiston, G.A.; Gerbasi, R. [Consejo Superior de Investigaciones Cientificas, Barcelona (Spain). Inst. de Ciencia de Materiales; Ist. di Chimica e Tecnologie Inorganiche e dei Materiali Avanzati del CNR, Padova (Italy)

    2001-08-01

    TiO{sub 2} is a well-known photocatalyst for the air-oxydation of organic compounds. This paper deals with the preparation of TiO{sub 2} layers by MOCVD. The photodegradation rate has been studied in the presence of aqueous suspensions (methylene blue) as a function of the film thickness, roughness and crystallite preferred orientation. These results are compared with aqueous suspensions of Degussa P-25 powders. Deposits obtained on fused quartz showed a higher photodegradation rate than those prepared on glass, while Degussa powders exhibited an intermediate value. (orig.)

  10. MOCVD of zirconium oxide thin films: Synthesis and characterization

    International Nuclear Information System (INIS)

    Torres-Huerta, A.M.; Dominguez-Crespo, M.A.; Ramirez-Meneses, E.; Vargas-Garcia, J.R.

    2009-01-01

    The synthesis of thin films of zirconia often produces tetragonal or cubic phases, which are stable at high temperatures, but that can be transformed into the monoclinic form by cooling. In the present study, we report the deposition of thin zirconium dioxide films by metalorganic chemical vapor deposition using zirconium (IV)-acetylacetonate as precursor. Colorless, porous, homogeneous and well adherent ZrO 2 thin films in the cubic phase were obtained within the temperature range going from 873 to 973 K. The deposits presented a preferential orientation towards the (1 1 1) and (2 2 0) planes as the substrate temperature was increased, and a crystal size ranging between 20 and 25 nm. The kinetics is believed to result from film growth involving the deposition and aggregation of nanosized primary particles produced during the CVD process. A mismatch between the experimental results obtained here and the thermodynamic prediction was found, which can be associated with the intrinsic nature of the nanostructured materials, which present a high density of interfaces.

  11. MOCVD of zirconium oxide thin films: Synthesis and characterization

    Energy Technology Data Exchange (ETDEWEB)

    Torres-Huerta, A.M., E-mail: atohuer@hotmail.com [Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada, Unidad Altamira, Instituto Politecnico Nacional, Km. 14.5 Carr. Tampico-Puerto Industrial, C.P. 89600, Altamira, Tamaulipas (Mexico); Dominguez-Crespo, M.A.; Ramirez-Meneses, E. [Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada, Unidad Altamira, Instituto Politecnico Nacional, Km. 14.5 Carr. Tampico-Puerto Industrial, C.P. 89600, Altamira, Tamaulipas (Mexico); Vargas-Garcia, J.R. [ESIQIE, Departamento de Metalurgia y Materiales, Instituto Politecnico Nacional. A.P. 75-876, 07300 Mexico, D.F. (Mexico)

    2009-02-15

    The synthesis of thin films of zirconia often produces tetragonal or cubic phases, which are stable at high temperatures, but that can be transformed into the monoclinic form by cooling. In the present study, we report the deposition of thin zirconium dioxide films by metalorganic chemical vapor deposition using zirconium (IV)-acetylacetonate as precursor. Colorless, porous, homogeneous and well adherent ZrO{sub 2} thin films in the cubic phase were obtained within the temperature range going from 873 to 973 K. The deposits presented a preferential orientation towards the (1 1 1) and (2 2 0) planes as the substrate temperature was increased, and a crystal size ranging between 20 and 25 nm. The kinetics is believed to result from film growth involving the deposition and aggregation of nanosized primary particles produced during the CVD process. A mismatch between the experimental results obtained here and the thermodynamic prediction was found, which can be associated with the intrinsic nature of the nanostructured materials, which present a high density of interfaces.

  12. Response of thick-film bridge junction of high-Tc YBCO to nuclear radiation

    International Nuclear Information System (INIS)

    Ding Honglin; Wang Jun; Zhang Wanchang

    1992-01-01

    The response of thick-film Josephson junction based on high-T c YBCO to nuclear radiation is described. The lengths of the junction are 2000 μm, 1000 μm, and 500 μm and the widths are 500 μm, 300 μm and 100 μm. When the junction is irradiated by low energy γ-ray of 59.5 KeV from 241 Am at temperature of 77 K and the transport current I b is more than I c , the authors obtained the reduction of 1.6 mA of critical current and volt-signal as high as 17 μV without amplifier. It has been noted that the signal amplitude is related to the distance between the junction and the radiation source. Finally the advantages and shortcomings of detector based on thick films of high T c YBCO are discussed in the paper

  13. The mechanism of sputter-induced orientation change in YBCO films on MgO (001)

    International Nuclear Information System (INIS)

    Huang, Y.; Vuchic, B.V.; Baldo, P.; Merkle, K.L.; Buchholz, D.B.; Mahajan, S.; Lei, J.S.; Markworth, P.R.; Chang, R.P.H.

    1996-12-01

    The mechanisms of the sputter-induced orientation change in YBa 2 Cu 3 O 7-x (YBCO) films grown on MgO (001) substrates by pulsed organometallic beam epitaxy (POMBE) are investigated by x-ray diffraction. Rutherford backscatter spectroscopy (RBS), cross-section TEM (XTEM) and microanalysis. It is found that the W atom implantation concurring with the ion sputtering plays an important role in effecting the orientation change. This implantation changes the surface structure of the substrate and induces an intermediate layer in the initial growth of the YBCO film, which in turn acts as a template that induces the orientation change. It seems that the surface morphology change caused by ion sputtering has only a minor effect on the orientation change

  14. Flux flow and flux creep in thick films of YBCO. [Y-Ba-Cu-O

    Energy Technology Data Exchange (ETDEWEB)

    Rickets, J.; Vinen, W.F.; Abell, J.S.; Shields, T.C. (Superconductivity Research Group, Univ. of Birmingham (United Kingdom))

    1991-12-01

    The results are described of new experiments designed to study flux creep and flux flow along a single flux percolation path in thick films of YBCO. The flux flow regime is studied by a four-point resistive technique using pulsed currents, and the flux creep regime by observing the rate at which flux enters a superconducting loop in parallel with the resistance that is associated with the flux percolation path. (orig.).

  15. Magnetoresistivity and Hall resistivity of a YBCO thin film in a tilted magnetic field

    International Nuclear Information System (INIS)

    Amirfeiz, M.; Cimberle, M. R.; Ferdeghini, C.; Giannini, E.; Grassano, G.; Marre', D.; Putti, M.; Siri, A. S.

    1997-01-01

    In this paper they present magnetoresistivity and Hall effect measurements performed on a YBCO epitaxial film as a function of the angle θ between the external magnetic field and the a-b planes. The resistivity and Hall effect measurements are analyzed in term of the general scaling approach proposed by Blatter and coworkers; the Hall conductivity data are examined to separate the contributions due to vortices and quasi particles

  16. Characteristics of the electrical response of YBCO films with different morphologies to optical irradiation

    International Nuclear Information System (INIS)

    Frack, E.K.; Madhavrao, L.; Patl, R.; Drake, R.E.; Radparvar, M.

    1991-01-01

    The authors have fabricated YBCO films of varying thicknesses (300 Angstrom - 3000 Angstrom) and morphologies, and measured their electrical response to optical radiation. This paper reports on these measurements, emphasizing the dependence on temperature, light chopping frequency, and cryogenic environment. The temperature dependence of the film resistance is determined in part by the film morphology. This morphology may be represented by a simple model consisting of a two-dimensional array of coupled grains. The magnitude of the bolometric response correlates as expected with the sharpness of the superconducting transition. The increased response observed at lower temperatures (non-equilibrium) correlates with the temperature dependence of the resistance above the transition

  17. Quench and recovery characteristics of Au/YBCO thin film type SFCL

    International Nuclear Information System (INIS)

    Yim, S.-W.; Kim, H.-R.; Hyun, O.-B.; Sim, J.

    2007-01-01

    Although, a superconducting fault current limiter (SFCL) guarantees the fast limiting operation, it usually needs a considerably long time to recover to superconducting state after the quench. Considering the reclosing time in the protection coordination of power systems, the time required for the recovery should be investigated clearly. In this study, the quench and recovery characteristics of Au/YBCO thin films designed as an SFCL element with a bi-spiral pattern were investigated. The quench development of the SFCL was measured by two kinds of methods. Firstly, after applying the fault current of 5.5 cycles, we measured the resistance of the YBCO by a small current flowing through the pattern of Au/YBCO thin film. The temperature variation above the critical temperature, 85 K, was investigated indirectly from the resistance variation. Secondly, in order to measure the temperature from 85 K to 77 K, a meander line shape of Au thin film was evaporated on the back side and used as a temperature detecting sensor. The temperature variations detected by both methods were compared and analyzed. For the investigation of the recovery characteristics, the required time for the recovery of the superconductivity was measured for various magnitude and duration of the applied voltages. In addition, for the purpose of examining the dependence of the line impedance on the recovery time, resistors of various resistances were inserted in the fault current testing circuit and the recovery time was measured and analyzed

  18. State of the art and prospective of large scale applications of YBCO thick films grown on metallic substrates

    International Nuclear Information System (INIS)

    Boffa, Vincenzo

    1997-09-01

    In the framework of the high temperature superconducting materials, YBa 2 Cu 3 O 7 (YBCO) shows very interesting intrinsic superconducting transport properties at temperature higher than the liquid nitrogen temperature. These properties are very important in large scale applications: transport of energy, magnets, transformers, etc. Unfortunately the potential of this material cannot be achieved today, since it is very difficult to manufacture YBCO based tapes or cables. In the last years several groups have tried to overcome the problems with new fabrication techniques. In the present report the state of the art and the prospective in the field of YBCO film fabrication on metallic substrates are presented

  19. Development of high-temperature superconducting coated conductor by MOCVD method

    International Nuclear Information System (INIS)

    Kim, Chan Joong; Jun, Byung Hyuk; Jung, Choung Hwan

    2004-07-01

    To fabricate the second generation superconductor wire, coated conductor, we selected MOCVD (Metal organic chemical vapor deposition) method which is commercially available and whose growth rate is very high. The first buffer layer CeO 2 was successfully deposited on the Ni tape. The thick Y-stabilized ZrO 2 layer was thus inserted between two CeO 2 layers by MOCVD method. The c-axis growth of the first CeO 2 , the inserted YSZ and top CeO 2 layer was achieved by optimized the deposition condition for the three buffers. It was found that the YBCO deposition was fairly dependant on the depostion temperature, time, oxygen partial pressure, amount of the source supplied. Especially the thickness of the YBCO films was linearly dedendant on the deposition temperature and time, but current properties was not linearly dependant on the film thickness. The critical current (Ic) of the YBCO film grown on SrTiO 3 and IBAD template were over 100 A/cm-width and 50 A/cm-width at 77 K and 0 field. To establish the MOCVD process, collaboration work with several organizations was made

  20. Thin RuO2 conducting films grown by MOCVD for microelectronic applications

    International Nuclear Information System (INIS)

    Froehlich, K.; Cambel, V.; Machajdik, D.; Pignard, S.; Baumann, P. K.; Lindner, J.; Schumacher, M.

    2002-01-01

    We have prepared thin RuO 2 films by MOCVD using thermal evaporation of Ru(thd) 2 (cod) solid precursor. The films were prepared at deposition temperatures between 250 and 500 grad C on silicon and sapphire substrates. Different structure was observed for the RuO 2 films on these substrates; the films on Si substrate were polycrystalline, while X-ray diffraction analysis revealed epitaxial growth of RuO 2 on sapphire substrates. Polycrystalline RuO 2 films prepared at temperatures below 300 grad C on Si substrate exhibit smooth surface and excellent step coverage. Highly conformal growth of the RuO 2 films at low temperature and low pressure results in nearly 100% step coverage for sub-mm features with 1:1 aspect ratio. Resistivity of the polycrystalline RuO 2 at room temperature ranged between 100 and 200 μ x Ω x cm. These films are suitable for CMOS and RAM applications. (Authors)

  1. Correlating properties and microstructure of YBCO thin films by magnetic X-ray microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Ruoss, Stephen; Stahl, Claudia; Weigand, Markus; Schuetz, Gisela [Max-Planck-Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Zahn, Patrick; Bayer, Jonas [Max-Planck-Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Research Institute for Innovative Surfaces, FINO, Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany); Albrecht, Joachim [Research Institute for Innovative Surfaces, FINO, Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany)

    2016-07-01

    The magnetic flux distribution in high-temperature superconductors namely YBCO has been observed using a novel high-resolution technique based on the X-ray magnetic circular dichroism (XMCD). Therefore, a CoFeB layer is deposited on the superconductor which exhibits a strong XMCD-effect. X-ray absorption measurements with circular polarized radiation allows the analysis of the magnetic flux distribution in the superconductor via the soft-magnetic sensor layer [3,4]. In the total electron yield (TEY) mode of the scanning X-ray microscope (SXM) the surface structure and the magnetic domains can be imaged at the same time. Having obtained such high resolution images, the correlation of magnetic flux penetration and defect structure of YBCO thin films can be analyzed. The measurements have been performed at the scanning X-ray microscope MAXYMUS at Bessy II, HZB Berlin.

  2. MOCVD and ALD of rare earth containing multifunctional materials. From precursor chemistry to thin film deposition and applications

    International Nuclear Information System (INIS)

    Milanov, Andrian Petrov

    2010-01-01

    The present thesis deals with the development of metal-organic complexes of rare elements. They should be used as novel precursors for the production of rare earth thin films by metal-organic chemical vapor deposition (MOCVD) and Atomic Layer Deposition (ALD). Within the work two precursor classes were examined, the tris-Malonato-complexes as well as the tris-Guanidinato-complexes of a series of rare earth metals. The latter showed excellent properties regarding to their volatility, their thermal stability, the defined decomposition and high reactivity towards water. They have been successfully used as precursors for the MOCVD of rare earth oxide layers. By using of a gadolinium guanidinate it could also be shown that the rare earth guanidinates are promising precursors for ALD of rare earth oxide and MOCVD of rare earth nitride layers. [de

  3. Properties of second phase (BaSnO3, Sn) added-YBCO thick films

    International Nuclear Information System (INIS)

    Ban, E.; Matsuoka, Y.

    1997-01-01

    The improvement of the critical current density J c of YBCO thick films has been attempted by adding BaSnO 3 powder and ultrafine Sn particles, whose diameter is about 2 μm and 7 x 10 -2 μm, respectively. It was found that the addition of a small amount of these particles was effective for the enhancement of J c of thick films prepared by a liquid-phase processing method. The 1 wt.% BaSnO 3 films fired at T s =1040-1060 C and the 3 wt.% Sn films (T s =1030-1060 C) showed J c values (77 K, 0 T) of about 2.1-2.4 x 10 3 Acm -2 and 3.1-3.5 x 10 3 Acm -2 , respectively, as compared to 2.0 x 10 3 Acm -2 for the undoped films. (orig.)

  4. Photocatalysis in the visible range of sub-stoichiometric anatase films prepared by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Justicia, I. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain); Garcia, G. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain)]. E-mail: gemma@icmab.es; Battiston, G.A. [ICIS/CNR, Corso Stati Uniti 4, 35127 Padova (Italy); Gerbasi, R. [ICIS/CNR, Corso Stati Uniti 4, 35127 Padova (Italy); Ager, F. [CNA/CSIC Parque Tecnologico Cartuja 93, Avda Thomas A, Edison, 41092 Sevilla (Spain); Guerra, M. [IIQAB/CSIC Jordi Girona, 18 08034 Barcelona (Spain); Caixach, J. [IIQAB/CSIC Jordi Girona, 18 08034 Barcelona (Spain); Pardo, J.A. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain); Rivera, J. [IIQAB/CSIC Jordi Girona, 18 08034 Barcelona (Spain); Figueras, A. [ICMAB/CSIC, Campus UAB, 08193 Bellaterra (Spain); Instituto de Fisica, UNAM, Campus UNAM Juriquilla, 76230 Queretaro (Mexico)

    2005-08-25

    Anatase phase of titanium oxide is the most promising photocatalyst material for organic pollutant degradation. However, due to its large band gap energy (3.2 eV) it is not viable to use sunlight as an energy source for the photocatalysis activation, and so, ultraviolet (UV) radiation below the wavelength of 380 nm is required. This paper focuses on the experimental demonstration of the reduction of this large band gap energy by inducing defects in the anatase structure under the form of oxygen sub-stoichiometry. TiO{sub 2} thin films were prepared in a metal organic chemical vapour deposition (MOCVD) reactor. The samples stoichiometry was measured by the Rutherford backscattering spectrometry (RBS) technique. Optical characterisation was also performed and the photodegradation activity in the visible range was tested using nonylphenol, which is one of the most harmful pollutants present in waste waters.

  5. Influence of artificial pinning centers on structural and superconducting properties of thick YBCO films on ABAD-YSZ templates

    Science.gov (United States)

    Pahlke, Patrick; Sieger, Max; Ottolinger, Rick; Lao, Mayraluna; Eisterer, Michael; Meledin, Alexander; Van Tendeloo, Gustaaf; Hänisch, Jens; Holzapfel, Bernhard; Schultz, Ludwig; Nielsch, Kornelius; Hühne, Ruben

    2018-04-01

    Recent efforts in the development of YBa2Cu3O7-x (YBCO) coated conductors are devoted to the increase of the critical current I c in magnetic fields. This is typically realized by growing thicker YBCO layers as well as by the incorporation of artificial pinning centers. We studied the growth of doped YBCO layers with a thickness of up to 7 μm using pulsed laser deposition with a growth rate of about 1.2 nm s-1. Industrially fabricated ion-beam textured YSZ templates based on metal tapes were used as substrates for this study. The incorporation of BaHfO3 (BHO) or Ba2Y(Nb0.5Ta0.5)O6 (BYNTO) secondary phase additions leads to a denser microstructure compared to undoped films. A purely c-axis-oriented YBCO growth is preserved up to a thickness of about 4 μm, whereas misoriented texture components were observed in thicker films. The critical temperature is slightly reduced compared to undoped films and independent of film thickness. The critical current density J c of the BHO- and BYNTO-doped YBCO layers is lower at 77 K and self-field compared to pure YBCO layers; however, I c increases up to a thickness of 5 μm. A comparison between films with a thickness of 1.3 μm revealed that the anisotropy of the critical current density J c(θ) strongly depends on the incorporated pinning centers. Whereas BHO nanorods lead to a strong B∣∣c-axis peak, the overall anisotropy is significantly reduced by the incorporation of BYNTO forming a mixture of short c-axis-oriented nanorods and small (a-b)-oriented platelets. As a result, the J c values of the doped films outperform the undoped samples at higher fields and lower temperatures for most magnetic field directions.

  6. Ag induced suppression of irradiation response in YBCO/Ag composite thin films

    International Nuclear Information System (INIS)

    Behera, D.; Mohanty, T.; Mohanta, D.; Patnaik, K.; Mishra, N.C.; Senapati, L.; Kanjilal, D.; Mehta, G.K.; Pinto, R.

    1999-01-01

    Practical application of cuprate superconductors in radiation environment demands that these systems remain insensitive to the irradiation induced defects. The cuprate superconductors however are many orders of magnitude more sensitive than the conventional low T c superconductors. To suppress the irradiation sensitivity of cuprates we consider a crystal engineering approach where metal ions as Ag is made to occupy inter and intra-granular sites of YBa 2 Cu 3 O 7 thin films. We show that superconducting and normal state properties of YBCO/Ag composite thin films prepared by laser ablation remain unchanged under 140 MeV Si ion irradiation up to fluence of 8 x 10 14 ions/cm 2 . The inter- and intra-granular occupancy of Ag is shown to induce microstructural modifications and rigidity to the CuO chains respectively which in turn lead to the radiation insensitivity of the composite films. (author)

  7. Effects of LP-MOCVD prepared TiO2 thin films on the in vitro behavior of gingival fibroblasts

    International Nuclear Information System (INIS)

    Cimpean, Anisoara; Popescu, Simona; Ciofrangeanu, Cristina M.; Gleizes, Alain N.

    2011-01-01

    We report on the in vitro response of human gingival fibroblasts (HGF-1 cell line) to various thin films of titanium dioxide (TiO 2 ) deposited on titanium (Ti) substrates by low pressure metal-organic chemical vapor deposition (LP-MOCVD). The aim was to study the influence of film structural parameters on the cell behavior comparatively with a native-oxide covered titanium specimen, this objective being topical and interesting for materials applications in implantology. HGF-1 cells were cultured on three LP-MOCVD prepared thin films of TiO 2 differentiated by their thickness, roughness, transversal morphology, allotropic composition and wettability, and on a native-oxide covered Ti substrate. Besides traditional tests of cell viability and morphology, the biocompatibility of these materials was evaluated by fibronectin immunostaining, assessment of cell proliferation status and the zymographic evaluation of gelatinolytic activities specific to matrix metalloproteinases secreted by cells grown in contact with studied specimens. The analyzed surfaces proved to influence fibronectin fibril assembly, cell proliferation and capacity to degrade extracellular matrix without considerably affecting cell viability and morphology. The MOCVD of TiO 2 proved effective in positively modifying titanium surface for medical applications. Surface properties playing a crucial role for cell behavior were the wettability and, secondarily, the roughness, HGF-1 cells preferring a moderately rough and wettable TiO 2 coating.

  8. State of the art and prospective of large scale applications of YBCO thick films grown on metallic substrates; Possibilita` applicative a larga scala dei film spessi di YBCO su substrati metallici: Stato dell`arte e prospettive

    Energy Technology Data Exchange (ETDEWEB)

    Boffa, Vincenzo [ENEA, Centro Ricerche Frascati, Rome (Italy). Dipt. Energia

    1997-09-01

    In the framework of the high temperature superconducting materials, YBa{sub 2}Cu{sub 3}O{sub 7} (YBCO) shows very interesting intrinsic superconducting transport properties at temperature higher than the liquid nitrogen temperature. These properties are very important in large scale applications: transport of energy, magnets, transformers, etc. Unfortunately the potential of this material cannot be achieved today, since it is very difficult to manufacture YBCO based tapes or cables. In the last years several groups have tried to overcome the problems with new fabrication techniques. In the present report the state of the art and the prospective in the field of YBCO film fabrication on metallic substrates are presented.

  9. Thermodynamical fluctuations and critical behavior in weakly disordered YBCO thin and ultra-thin films

    International Nuclear Information System (INIS)

    Lesueur, J.; Aprili, M.; Degoy, S.; Chambonnet, D.; Keller, D.

    1996-01-01

    The specific role of disorder in the transport properties of YBCO has been investigated, using both light-ion irradiation of thin films to finely tune the amount of atomic disorder, and ultra-thin films grown to study possible dimensional effects. For weak disorder, the samples display a resistive transition typical of the mean-field paraconductive regime of a homogeneous media, well described by the Lawrence and Doniach model for layered superconductors. As the disorder increases, two effects take place. First, the c-axis coherence length becomes shorter, leading to a more anisotropic material, as shown by the excess conductivity above T c . Second, an incipient granularity is revealed, leading to a less sharper transition, which is analyzed within the random 3D XY critical model for the paracoherence transition. Two main results are derived: an experimental test of the Ginzburg criteria for the paracoherence transition, and a new fluctuation regime in nanometric grain size superconductors

  10. Tunable pinning effects produced by non-uniform antidot arrays in YBCO thin films

    Energy Technology Data Exchange (ETDEWEB)

    George, J.; Jones, A.; Al-Qurainy, M. [Institute for Superconducting and Electronic Materials, University of Wollongong, NSW (Australia); Fedoseev, S.A. [Institute for Superconducting and Electronic Materials, University of Wollongong, NSW (Australia); Centre for Medical Radiation Physics, University of Wollongong, NSW (Australia); Rosenfeld, A. [Centre for Medical Radiation Physics, University of Wollongong, NSW (Australia); Pan, A.V. [Institute for Superconducting and Electronic Materials, University of Wollongong, NSW (Australia); National Research Nuclear University MEPhI (Moscow Engineering Physics Institute), Moscow (Russian Federation)

    2017-04-15

    Uniform, graded and spaced arrays of 3 μm triangular antidots in pulsed laser deposited YBa{sub 2}Cu{sub 3}O{sub 7} (YBCO) superconducting thin films are compared by examining the improvements in the critical current density J{sub c} they produced. The comparison is made to establish the role of their lithographically defined (non-)uniformity and the effectiveness to control and/or enhance the critical current density. It is found that almost all types of non-uniform arrays, including graded ones enhance J{sub c} over the broad applied magnetic field and temperature range due to the modified critical state. Whereas uniform arrays of antidots either reduce or produce no effect on J{sub c} compared to the original (as-deposited) thin films. (copyright 2017 by WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  11. Surface characterization of III-V MOCVD films from heterocyclic single-source precursors; Oberflaechencharakterisierung von III-V MOCVD-Filmen aus heterozyklischen Single Source Precursoren

    Energy Technology Data Exchange (ETDEWEB)

    Seemayer, Andreas

    2009-07-13

    In the present thesis the sublimation and evaporation properties of heterocyclic gallium and antimony containing single-source precursors as well as the chemical composition and morphology of the films fabricated from this were studied. The single-source precursors available by a new synthesis route were characterized concerning their evaporation properties and the obtained films studied surface-physically. By this way the process parameters were optimized and the applicability of the single-source precursors in HV-MOCVD processes studied. By evaporation experiments in the UHV it could be shown that thereby lighter ligands like ethyl- and methyl-groups lead to a lower contamination of the reaction space with carbon containing molecules. Furthermore it was expected that the 6-rings synthetized with short ligands exhibit a high stability. This however could not be confirmed. By unwanted parasitary reactions in the gaseous phase respectively dissociative sublimation in the gaseous phase a deposition of GaSb with these precursors was not possible. The 4-ring stabilized with tertiary-butyl and ethyl-groups caused in the evaporation the largest contamination of the gaseous phase, becauselonger-chain hydrocarbons exhibil only a bad pump cross section. By parasitary reactions originating elementary antimony is detectable in the gaseous phase. The films were studied concerning their chemical composition and their transport- respectively storage-conditioned surface contamination. Furthermore it has become clear that not only a purely synthetized precursor substance but also the reactor design is deciding for a successful deposition and a high film quality. First by successive optimization of the evaporation geometry it was possible to reduce the roughness of the produced GaSb films down to about 10 nm-30 nm.

  12. Quick screening for new flux pinning materials in YBCO films with the combinatorial-PLD method

    International Nuclear Information System (INIS)

    Yoshimura, T.; Ichino, Y.; Yoshida, Y.; Takai, Y.; Kita, R.; Suzuki, K.; Takeuchi, T.

    2011-01-01

    An effective way to improve the superconducting properties in REBa 2 Cu 3 O y (REBCO) films under a magnetic field is to dope artificial pinning centers (APC). The pinning performance depends on the content of the APC materials. Usually, the optimal APC content is explored by preparing films one at a time from the REBCO target using different APC material content, which is an extremely time-consuming process. The combinatorial-PLD (C-PLD) method allowed us to prepare films that continuously changed in composition across a single substrate. In this study, we used the C-PLD method to prepare BaSnO 3 (BSO)-doped YBCO films. The films were deposited on SrTiO 3 substrate using a fourth-harmonic Nd:YAG laser. From the results of the J c -B curves at 77 K and B//c, the film that contained 3.2 vol.% of BSO exhibited the best pinning performance in this study. We showed that the C-PLD method was efficient for quick screening of the optimal APC content with only one deposition. We also used the C-PLD method to explore new APC materials, and proved that it can quickly evaluate the new APC materials Ba 3 Cu 3 In 4 O 12 and BaTbO 3 .

  13. Epitaxial growth and processing of InP films in a ``novel`` remote plasma-MOCVD apparatus

    Energy Technology Data Exchange (ETDEWEB)

    Bruno, G. [Bari Univ. (Italy). Centro di Studio per la Chimica; Losurdo, M. [Bari Univ. (Italy). Centro di Studio per la Chimica; Capezzuto, P. [Bari Univ. (Italy). Centro di Studio per la Chimica; Capozzi, V. [Bari Univ. (Italy). Ist. di Fisica; Lorusso, F.G. [Bari Univ. (Italy). Ist. di Fisica; Minafra, A. [Bari Univ. (Italy). Ist. di Fisica

    1996-06-01

    A new remote plasma MOCVD apparatus for the treatment and deposition of III-V materials and, specifically, of indium phosphide, has been developed. The plasma source is used to produce hydrogen atoms and to predissociate phosphine for, respectively, the reduction of native oxide on InP substrate surface and the InP deposition. In situ diagnostics by optical emission spectroscopy, mass spectrometry, and spectroscopic ellipsometry are used to fingerprint the gas phase and the growth surface. The plasma cleaning process effectively reduce the InP oxide layer without surface damage. Indium phosphide epilayers deposited from trimethylindium and plasma activated PH{sub 3} show singular photoluminescence spectra with signal intensity higher than that of the best InP film deposited under conventional MOCVD condition (without PH{sub 3} plasma preactivation). (orig.)

  14. Influence of the growth parameters on TiO2 thin films deposited using the MOCVD method

    Directory of Open Access Journals (Sweden)

    Bernardi M. I. B.

    2002-01-01

    Full Text Available In this work we report the synthesis of TiO2 thin films by the Organometallic Chemical Vapor Deposition (MOCVD method. The influence of deposition parameters used during the growth in the obtained structural characteristics was studied. Different temperatures of the organometallic bath, deposition time, temperature and type of the substrate were combined. Using Scanning Electron Microscopy associated to Electron Dispersive X-Ray Spectroscopy, Atomic Force Microscopy and X-ray Diffraction, the strong influence of these parameters in the thin films final microstructure was verified.

  15. High critical current density YBCO films and fabrication of dc-SQUIDs

    CERN Document Server

    Kuriki, S; Kawaguchi, Y; Matsuda, M; Otowa, T

    2002-01-01

    In order to improve the sensitivity of SQUID magnetometers made of high-T sub c films, we have studied the conditions of pulsed-laser deposition of YBCO films. Among the different deposition parameters examined, extensive degassing of the vacuum chamber before and precise control of the substrate temperature during the film deposition were found effective for obtaining high critical temperature T sub c and high critical current density J sub c. It was also found that the residual-resistance ratio has a clear correlation with J sub c , indicating that it can be a good, and easy to measure, index of the film quality. Films having T sub c approx 89-90 K and J sub c >= 5x10 sup 6 A cm sup - sup 2 at 77 K were used to fabricate SQUIDs without a pickup loop. Grain-boundary junctions formed on bicrystal substrates with a 30 deg. misorientation angle exhibited I sub c R sub n values of more than 100 mu V at 77 K. The well-known scaling behaviour of the relation I sub c R sub n propor to (J sup G sup B sub c) sup 1 su...

  16. Planar intrinsic Josephson junctions with in-plane aligned YBCO films

    CERN Document Server

    Zhang, L; Kobayashi, T; Goto, T; Mukaida, M

    2002-01-01

    Planar type devices were fabricated by patterning in-plane aligned YBa sub 2 Cu sub 3 O sub 7 sub - subdelta (YBCO) films. The current-voltage characteristics along the c-axis at various temperatures and oxygen contents were measured. The current voltage curves showing supercurrent and hysteresis were obtained for the samples annealed at an oxygen pressure of 1.3 x 10 sup 4 Pa, while the supercurrent and hysteresis became smaller and even disappeared as the oxygen pressure decreased. The relationships between the critical currents and temperatures are similar to those of d-wave superconducting tunnel junctions. These results indicate the formation of stacks of intrinsic Josephson junctions, which are useful for developing high-frequency electron devices.

  17. Planar intrinsic Josephson junctions with in-plane aligned YBCO films

    International Nuclear Information System (INIS)

    Zhang, L; Moriya, M; Kobayashi, T; Goto, T; Mukaida, M

    2002-01-01

    Planar type devices were fabricated by patterning in-plane aligned YBa 2 Cu 3 O 7-δ (YBCO) films. The current-voltage characteristics along the c-axis at various temperatures and oxygen contents were measured. The current voltage curves showing supercurrent and hysteresis were obtained for the samples annealed at an oxygen pressure of 1.3 x 10 4 Pa, while the supercurrent and hysteresis became smaller and even disappeared as the oxygen pressure decreased. The relationships between the critical currents and temperatures are similar to those of d-wave superconducting tunnel junctions. These results indicate the formation of stacks of intrinsic Josephson junctions, which are useful for developing high-frequency electron devices

  18. Formation and physical properties of YBCO thick films grown by using the electrophoretic deposition method

    CERN Document Server

    Kim, U J; Kim, Y C; Han, S K; Kang, K Y

    1999-01-01

    Thick films of the YBa sub 2 Cu sub 3 O subgamma sub - subdelta (YBCO) superconductor were prepared by using the electrophoretic deposition technique and a flexible wire as the substrate. The transition temperature of the wires was 91 K, the intragranular magnetic critical current density J sub c sub g sup m sup a sup g was about 10 sup 5 A/cm sup 2 at 77 K in a weak field, and the transport J sub c sup t sup r sup a sup n sup s was about 365 A/cm sup 2 at 77 K. We calculated the intergranular magnetic critical current J sub c sub J sup m sup a sup g and the activation energy from the AC-susceptibility measurements, and their values were about 444 A/cm sup 2 at 77 K and 2.02 eV, respectively.

  19. Structural and morphological characterizations of ZnO films grown on GaAs substrates by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Agouram, S.; Zuniga Perez, J.; Munoz-Sanjose, V. [Universitat de Valencia, Departamento de Fisica Aplicada y Electromagnetismo, Burjassot (Spain)

    2007-07-15

    ZnO films were grown on GaAs(100), GaAs(111)A and GaAs(111)B substrates by metal organic chemical vapour deposition (MOCVD). Diethylzinc (DEZn) and tertiarybutanol (t-butanol) were used as Zn and O precursors, respectively. The influence of the growth temperature and GaAs substrate orientation on the crystalline orientation and morphology of the ZnO grown films has been analysed. Crystallinity of grown films was studied by X-ray diffraction (XRD); thickness and morphology of ZnO films were investigated by scanning electron microscopy (SEM). SEM results reveal significant differences between morphologies depending on growth temperature but not significant differences were detected on the texture of grown films. (orig.)

  20. Friction and wear behavior of nitrogen-doped ZnO thin films deposited via MOCVD under dry contact

    Directory of Open Access Journals (Sweden)

    U.S. Mbamara

    2016-06-01

    Full Text Available Most researches on doped ZnO thin films are tilted toward their applications in optoelectronics and semiconductor devices. Research on their tribological properties is still unfolding. In this work, nitrogen-doped ZnO thin films were deposited on 304 L stainless steel substrate from a combination of zinc acetate and ammonium acetate precursor by MOCVD technique. Compositional and structural studies of the films were done using Rutherford Backscattering Spectroscopy (RBS and X-ray Diffraction (XRD. The frictional behavior of the thin film coatings was evaluated using a ball-on-flat configuration in reciprocating sliding under dry contact condition. After friction test, the flat and ball counter-face surfaces were examined to assess the wear dimension and failure mechanism. Both friction behavior and wear (in the ball counter-face were observed to be dependent on the crystallinity and thickness of the thin film coatings.

  1. In-plane aligned YBCO film on textured YSZ buffer layer deposited on NiCr alloy tape by laser ablation with only O+ ion beam assistance

    International Nuclear Information System (INIS)

    Xin Tang Huang

    2000-01-01

    High critical current density and in-plane aligned YBa 2 Cu 3 O 7-x (YBCO) film on a textured yttria-stabilized zirconia (YSZ) buffer layer deposited on NiCr alloy (Hastelloy c-275) tape by laser ablation with only O + ion beam assistance was fabricated. The values of the x-ray phi-scan full width at half-maximum (FWHM) for YSZ(202) and YBCO(103) are 18 deg. and 11 deg., respectively. The critical current density of YBCO film is 7.9 x 105 A cm -2 at liquid nitrogen temperature and zero field, and its critical temperature is 90 K. (author)

  2. Effect of processing conditions and methods on residual stress in CeO2 buffer layers and YBCO superconducting films

    International Nuclear Information System (INIS)

    Xiong Jie; Qin Wenfeng; Cui Xumei; Tao Bowan; Tang Jinlong; Li Yanrong

    2006-01-01

    CeO 2 layers have been fabricated by pulsed laser deposition (PLD) technique on (1 1 0 2) sapphire substrate. Microstructure of CeO 2 layers is characterized by X-ray diffraction as functions of substrate temperature. The effects of the substrate temperature on the residual stress have been studied. The results show that residual stress in CeO 2 film decreased with increasing substrate temperature, not the same development tendency as that of thermal stress. This means that the thermal stress is only a fraction of the residual stress. Moreover, YBCO superconducting films were prepared by direct current (DC) sputtering and pulsed laser deposition (PLD) technique. The residual stress and thermal stress of both YBCO films were measured. PLD processing apparently generated higher intrinsic compressive stresses in comparison to DC sputtering

  3. The effects of H sub 2 addition on the enhanced deposition rate and high quality Cu films by MOCVD

    CERN Document Server

    Lee, J H; Park, S J; Choi, S Y

    1998-01-01

    High-quality Cu thin films were deposited on the TiN/Si substrate from the hexafluoroacetylacetonate Copper thrmethylvinylsilane [Cu (hfac) (tmvs)] source using a metal organic chemical vapor deposition (MOCVD) technique. The optimum deposition condition is with a substrate temperature of 200 .deg. C and the hydrogen flow rate of 80 sccm. The deposition rate, electrical resistivity, surface morphology, grain size, and optical properties of the deposited Cu films were investigated by the AES, four-point probe, SEM, XRD, and the visible spectrophotometer as a function of hydrogen gas flow rate, The results indicated that additional hydrogen gas affects the CVD hydrogen reduction reaction improving the purity, deposition rate, and electrical resistivity of Cu thin films. A prospective idea will be discussed for the preparation of Cu thin films showing a more enhanced electromigration resistance applicable to the next-generation interconnection.

  4. Influence of different carrier gases on the properties of ZnO films grown by MOCVD

    Directory of Open Access Journals (Sweden)

    Wang, Jinzhong

    2008-08-01

    Full Text Available ZnO films were grown on sapphire (001 substrate by atmospheric MOCVD using diethyl zinc and tertiary butanol precursors. The influence of different carrier gases (H2 and He on the properties was analyzed by their structural (XRD, microstructural (SEM and compositional (SIMS characterization. The intensity of the strongest diffraction peak from ZnO (002 plane was increased by about 2 orders of magnitude when He is used as carrier gas, indicating the significant enhancement in crystallinity. The surface of the samples grown using H2 and He carrier gases was composed of leaf-like and spherical grains respectively. Hydrogen [H] content in the film grown using H2 is higher than that using He, indicating that the [H] was influenced by the H2 carrier gas. Ultraviolet emission dominates the low temperature PL spectra. The emission from ZnO films grown using He show higher optical quality and more emission centers.

    Se depositaron películas de ZnO sobre sustratos de zafiro (001 utilizando dietil zinc y butanol terciario como precursores. La influencia de los diferentes gases portadores (H2 y He sobre las propiedades se estudió mediante la caracterización estructural (XRD, microestructural (SEM y composicional (SIMS. La intensidad del pico de difracción más importante del plano (002 del ZnO aumentó en dos órdenes de magnitud cuando se utiliza He como gas portador indicando un incremento significativo de la cristalinidad. La superficie de las muestras crecidas utilizando H2 y He está formada por granos en forma de hoja y de forma esférica respectivamente. El contenido en hidrógeno (H en la película es mayor cuando se utiliza H2 que cuando se utiliza He, indicando que la cantidad de hidrógeno está influenciada por el H2 del gas portador. La emisión ultravioleta domina el espectro PL de baja temperatura. La emisión de las películas de ZnO utilizando

  5. Enhanced Light Scattering by Preferred Orientation Control of Ga Doped ZnO Films Prepared through MOCVD

    Directory of Open Access Journals (Sweden)

    Long Giang Bach

    2016-01-01

    Full Text Available We have explored the effective approach to fabricate GZO/ZnO films that can make the pyramidal surface structures of GZO films for effective light scattering by employing a low temperature ZnO buffer layer prior to high temperature GZO film growth. The GZO thin films exhibit the typical preferred growth orientations along the (002 crystallographic direction at deposition temperature of 400°C and SEM showed that column-like granule structure with planar surface was formed. In contrast, GZO films with a pyramidal texture surface were successfully developed by the control of (110 preferred orientation. We found that the light diffuse transmittance of the film with a GZO (800 nm/ZnO (766 nm exhibited 13% increase at 420 nm wavelength due to the formed large grain size of the pyramidal texture surface. Thus, the obtained GZO films deposited over ZnO buffer layer have high potential for use as front TCO layers in Si-based thin film solar cells. These results could develop the potential way to fabricate TCO based ZnO thin film using MOCVD or sputtering techniques by depositing a low temperature ZnO layer to serve as a template for high temperature GZO film growth. The GZO films exhibited satisfactory optoelectric properties.

  6. Effect of the microscopic correlated-pinning landscape on the macroscopic critical current density in YBCO films

    Science.gov (United States)

    Ghigo, G.; Chiodoni, A.; Gerbaldo, R.; Gozzelino, L.; Laviano, F.; Mezzetti, E.; Minetti, B.; Camerlingo, C.

    This paper deals with the mechanisms controlling the critical current density vs. field behavior in YBCO films. We base our analysis on a suitable model concerning the existence of a network of intergrain Josephson junctions whose length is modulated by defects. Irradiation with 0.25 GeV Au ions provide a useful tool to check the texture of the sample, in particular to give a gauge length reference to separate “weak” links and high- J c links.

  7. MOCVD Growth and Characterization of n-type Zinc Oxide Thin Films

    Science.gov (United States)

    Ben-Yaacov, Tammy

    , and we investigate the n-ZnO/p-GaN interface. We show that ZnO has potential as an effective p-contact for these devices, and determine properties that still need improvement in order for ZnO to compete with other contact materials. We also compare the device performance to metal-contacted devices. In summary, this thesis describes the growth of ZnO(0001) films by MOCVD, the progress in developing ZnO material with excellent surface morphology, high crystal quality, and controllable n-type doping, as well as its application to GaN-based optoelectronic devices as a p-contact material.

  8. Greatly enhanced flux pinning properties of fluorine-free metal-organic decomposition YBCO films by co-addition of halogens (Cl, Br) and metals (Zr, Sn, Hf)

    Science.gov (United States)

    Motoki, Takanori; Ikeda, Shuhei; Nakamura, Shin-ichi; Honda, Genki; Nagaishi, Tatsuoki; Doi, Toshiya; Shimoyama, Jun-ichi

    2018-04-01

    Additive-free YBCO films, as well as those with halogen (X) added, metal (M) added and (X, M) co-added, have been prepared by the fluorine-free metal-organic decomposition method on SrTiO3(100) single crystalline substrates, where X = Cl, Br and M = Zr, Sn, Hf. It was revealed that the addition of both Cl and Br to the starting solution resulted in the generation of oxyhalide, Ba2Cu3O4 X 2, in the YBCO films, and that the oxyhalide was found to promote the bi-axial orientation of the YBCO crystals. By adding a decent amount of Cl or Br, highly textured YBCO films with high J c were reproducibly obtained, even when an impurity metal, M, was co-added, while the addition of M without X did not greatly improve J c owing to the poor bi-axial orientation of the YBCO crystals. Our results suggest that the addition of Br more effectively enhances J c than the addition of Cl. The pinning force density at 40 K in 4.8 T reached ˜55 GN m-3 with the co-addition of (Br, M). This value is much larger than that of the pure YBCO film, reaching ˜17 GN m-3.

  9. 10 GHz surface impedance measurements of (Y9Er)BaCuO films produced by MOCVD, laser ablation, and sputtering

    International Nuclear Information System (INIS)

    Luine, J.; Daly, K.; Hu, R.; Kain, A.; Lee, A.; Manasevit, H.; Pettiette-Hall, C.; Simon, R.; St John, D.; Wagner, M.

    1991-01-01

    This paper reports on a parallel-plate resonator technique previously used to measure microwave surface resistance R s (T) extended to also measure absolute penetration depth λ(T). Measurements of both quantities near 10 GHz from 4.2 K to Tc are reported for ErBaCuO thin films produced by metal-organic chemical vapor deposition (MOCVD) and YBaCuO think films produced by laser ablation and single-target off-axis sputtering. All the films were made at TRW. Each production method gives rise to films whose surface resistance is below 1 milliohm at temperatures below 40K. The low temperature penetration depths range from 250 nm for the laser ablation and sputtered films to 800 nm for the MOCVD films. The penetration depths in all cases increase with temperature according to the Gorter-Casimir temperature dependence

  10. Final report: High current capacity high temperature superconducting film based tape for high field magnets

    International Nuclear Information System (INIS)

    Ying Xin

    2000-01-01

    The primary goal of the program was to establish the process parameters for the continuous deposition of high quality, superconducting YBCO films on one meter lengths of buffered RABiTS tape using MOCVD and to characterize the potential utility of the resulting tapes in high field magnet applications

  11. HCl Flow-Induced Phase Change of α-, β-, and ε-Ga2O3 Films Grown by MOCVD

    KAUST Repository

    Sun, Haiding

    2018-03-06

    Precise control of the heteroepitaxy on a low-cost foreign substrate is often the key to drive the success of fabricating semiconductor devices in scale when a large low-cost native substrate is not available. Here, we successfully synthesized three different phases of Ga2O3 (α, β, and ε) films on c-plane sapphire by only tuning the flow rate of HCl along with other precursors in an MOCVD reactor. A 3-fold increase in the growth rate of pure β-Ga2O3 was achieved by introducing only 5 sccm of HCl flow. With continuously increased HCl flow, a mixture of β- and ε-Ga2O3 was observed, until the Ga2O3 film transformed completely to a pure ε-Ga2O3 with a smooth surface and the highest growth rate (∼1 μm/h) at a flow rate of 30 sccm. At 60 sccm, we found that the film tended to have a mixture of α- and ε-Ga2O3 with a dominant α-Ga2O3, while the growth rate dropped significantly (∼0.4 μm/h). The film became rough as a result of the mixture phases since the growth rate of ε-Ga2O3 is much higher than that of α-Ga2O3. In this HCl-enhanced MOCVD mode, the Cl impurity concentration was almost identical among the investigated samples. On the basis of our density functional theory calculation, we found that the relative energy between β-, ε-, and α-Ga2O3 became smaller, thus inducing the phase change by increasing the HCl flow in the reactor. Thus, it is plausible that the HCl acted as a catalyst during the phase transformation process. Furthermore, we revealed the microstructure and the epitaxial relationship between Ga2O3 with different phases and the c-plane sapphire substrates. Our HCl-enhanced MOCVD approach paves the way to achieving highly controllable heteroepitaxy of Ga2O3 films with different phases for device applications.

  12. Study on optimization of YBCO thin film stack for compact NMR magnets

    International Nuclear Information System (INIS)

    Kim, S.B.; Kimoto, T.; Hahn, S.; Iwasa, Y.; Voccio, J.; Tomita, M.

    2013-01-01

    Highlights: ► Stacking methods for compact NMR magnet using YBCO thin films were tested. ► The stacking angles are 0°, 22.5° and 90° against the rolling direction. ► The best spatial field homogeneity was obtained in rotation angle of 22.5°. ► The maximum trapped magnetic fields of 0.4 T was obtained at 77.4 K. ► The maximum trapped magnetic fields of 0.95 T was obtained at 21 K. -- Abstract: A compact high temperature superconducting (HTS) magnet, which consists of a stack of 500 HTS thin film annuli, was constructed and tested. Each thin film annulus, manufactured by the AMSC using the Rolling Assisted Bi-axially Textured Substrate (RABiTS) method, has a square cross-section of 40 mm × 40 mm with a thickness of 80 m. It has a 25-mm center hole created by machining. This paper reports a study on the anisotropic J c issue due to the rolling procedure of the Ni substrate direction and its impact on field homogeneity. Also, three different stacking methods with rotation angles of 22.5°, 90°, and 0° against the rolling direction have been tested to study their impacts on strength, spatial homogeneity, and temporal stability of trapped fields. Finally, the 500-annulus magnet was tested at 21 K under a cryogen-free environment using a GM cryocooler. The spatial field homogeneity and temporal stability were measured at 21 K and compared with those obtained in a bath of liquid nitrogen at 77 K

  13. Preparation of PZT/YBCO/YAlO heterostructure thin films by KrF excimer laser ablation

    International Nuclear Information System (INIS)

    Ebihara, Kenji; Kurogi, Hiromitsu; Yamagata, Yukihiko; Ikegami, Tomoaki; Grishin, A.M.

    1998-01-01

    The perovskite oxide YBa 2 Cu 3 O 7-x (YBCO) and Pb(Zr x Ti 1-x )O 3 (PZT) thin films have been deposited for superconducting-ferroelectric devices. KrF excimer laser ablation technique was used at the deposition conditions of 200--600 mTorr O 2 , 2-3J/cm 2 and 5--10 Hz operation frequency. Heterostructures of PZT-YBCO-YAlO 3 :Nd show the zero resistivity critical temperature of 82 K and excellent ferroelectric properties of remnant polarization 32 microC/cm 2 , coercive force of 80 kV/cm and dielectric constant 800. Cycling fatigue characteristics and leakage current are also discussed

  14. Hardware Modifications to the US Army Research Laboratory’s Metalorganic Chemical Vapor Deposition (MOCVD) System for Optimization of Complex Oxide Thin Film Fabrication

    Science.gov (United States)

    2015-04-01

    the total absorbance, or the fraction of radiation absorbed at the measured wavelength; is the calculated molar extinction coefficient for the...of PZT thin films by liquid delivery MOCVD. Integrated Ferroelectrics. 2002;46:125–131. 14. Hiskes R, Dicarolis SA, Jacowitz RD, Lu Z, Feigelson RS

  15. Improved interface growth and enhanced flux pinning in YBCO films deposited on an advanced IBAD-MgO based template

    Science.gov (United States)

    Khan, M. Z.; Zhao, Y.; Wu, X.; Malmivirta, M.; Huhtinen, H.; Paturi, P.

    2018-02-01

    The growth mechanism is studied from the flux pinning point of view in small-scale YBa2Cu3O6+x (YBCO) thin films deposited on a polycrystalline hastelloy with advanced IBAD-MgO based buffer layer architecture. When compared the situation with YBCO films grown on single crystal substrates, the most critical issues that affect the suitable defect formation and thus the optimal vortex pinning landscape, have been studied as a function of the growth temperature and the film thickness evolution. We can conclude that the best critical current property in a wide applied magnetic field range is observed in films grown at relatively low temperature and having intermediate thickness. These phenomena are linked to the combination of the improved interface growth, to the film thickness related crystalline relaxation and to the formation of linear array of edge dislocations that forms the low-angle grain boundaries through the entire film thickness and thus improve the vortex pinning properties. Hence, the optimized buffer layer structure proved to be particularly suitable for new coated conductor solutions.

  16. A comparative study on the flux pinning properties of Zr-doped YBCO film with those of Sn-doped one prepared by metal-organic deposition

    International Nuclear Information System (INIS)

    Choi, S. M.; Shin, G. M.; Joo, Y.S.; Yoo, S. I.

    2013-01-01

    We investigated the flux pinning properties of both 10 mol% Zr-and Sn-doped YBa 2 Cu 3 O 7-δ (YBCO) films with the same thickness of ∽350 nm for a comparative purpose. The films were prepared on the SrTiO 3 (STO) single crystal substrate by the metal-organic deposition (MOD) process. Compared with Sn-doped YBCO film, Zr-doped one exhibited a significant enhancement in the critical current density (J c ) and pinning force density (F p ). The anisotropic J c ,min/J c ,max ratio in the field-angle dependence of J c at 77 K for 1 T was also improved from 0.23 for Sn-doped YBCO to 0.39 for Zr-doped YBCO. Thus, the highest magnetic J c values of 9.0 and 2.9 MA/cm 2 with the maximum F p (F p ,max) values of 19 and 5 GN/m 3 at 65 and 77 K for H // c, respectively, could be achieved from Zr-doped YBCO film. The stronger pinning effect in Zr-doped YBCO film is attributable to smaller BaZrO-3 (BZO) nanoparticles (the average size ≈ 28.4 nm) than YBa 2 SnO 5. 5 (YBSO) nanoparticles (the average size ≈ 45.0 nm) incorporated in Sn-doped YBCO film since smaller nanoparticles can generate more defects acting as effective flux pinning sites due to larger incoherent interfacial area for the same doping concentration.

  17. Effect of deposition conditions on the growth rate and electrical properties of ZnO thin films grown by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Roro, K.T.; Botha, J.R.; Leitch, A.W.R. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa)

    2008-07-01

    ZnO thin films have been grown on glass substrates by MOCVD. The effect of deposition conditions such as VI/II molar ratio, DEZn flow rate and total reactor pressure on the growth rate and electrical properties of the films was studied. It is found that the growth rate decreases with an increase in the VI/II molar ratio. This behaviour is ascribed to the competitive adsorption of reactant species on the growth surface. The growth rate increases with an increase in DEZn flow rate, as expected. It is shown that the carrier concentration is independent of the DEZn flow rate. An increase in the total reactor pressure yields a decrease in growth rate. This phenomenon is attributed to the depletion of the gas phase due to parasitic prereactions between zinc and oxygen species at high pressure. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  18. Tailoring the vortex pinning strength of YBCO thin films by systematic incorporation of hybrid artificial pinning centers

    International Nuclear Information System (INIS)

    Jha, Alok K; Matsumoto, Kaname; Horide, Tomoya; Saini, Shrikant; Mele, Paolo; Ichinose, Ataru; Yoshida, Yutaka; Awaji, Satoshi

    2015-01-01

    The effect of hybrid (columnar and spherical together) artificial pinning centers (APCs) on the vortex pinning properties of YBa 2 Cu 3 O 7−δ (YBCO) thin films is investigated in detail on the basis of variation of critical current density (J C ) with applied magnetic field and also with the orientation of the applied magnetic field at 65 K and 77 K. Premixed YBCO + BaSnO 3 composite targets are used for the deposition of the YBCO films which consist of self-assembled BaSnO 3 nanocolumns (1D APCs); on the other hand, for the deposition of the YBCO films with hybrid APCs (BaSnO 3 nanocolumns together with Y 2 O 3 nanoparticles), the surface of the premixed YBCO + BaSnO 3 composite targets are modified by putting a thin Y 2 O 3 sectored piece on the premixed YBCO + BaSnO 3 composite targets by means of silver paste. F pmax value increases systematically with incorporation of 1D and 1D and 3D APCs and it also shifts towards higher applied magnetic fields. Films with 1D APCs exhibit a strong J C peak at Θ = 0° (H//c-axis) whereas films consisting of hybrid APCs exhibit enhanced J C at all the investigated angular regimes. A possible mechanism of vortex pinning in samples with hybrid APCs is also discussed suggesting the role of 1D and 3D APCs. (paper)

  19. Enhancement of YBCO thin film thermal stability under 1 ATM oxygen pressure by Intermediate Cu.sub.2./sub. O nanolayer

    Czech Academy of Sciences Publication Activity Database

    Cheng, L.; Wang, X.; Yao, X.; Wan, W.; Li, F.H.; Xiong, J.; Tao, B.W.; Jirsa, Miloš

    2010-01-01

    Roč. 114, č. 22 (2010), s. 7543-7547 ISSN 1520-6106 R&D Projects: GA MŠk(CZ) ME10069 Institutional research plan: CEZ:AV0Z10100520 Keywords : YBCO thin films * thermal stability * thin film growth orientation * temperature optical microscopy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.603, year: 2010

  20. Preparation of YBa2Cu3O7 films by low pressure MOCVD using liquid solution sources

    International Nuclear Information System (INIS)

    Weiss, F.; Froehlich, K.; Haase, R.; Labeau, M.; Selbmann, D.; Senateur, J.P.; Thomas, O.

    1993-01-01

    A hybrid low pressure MOCVD process is described for reproducible preparation of superconducting thin films of YBa 2 Cu 3 O 7 . The process uses a single solution source of Y, Ba, and Cu β-diketonates dissolved in suitable organic solvents. This liquid precursor is atomized using an ultrasonic aerosol generator and transported as small droplets (∼1μm) into a CVD reactor where solvent and precursor are first evaporated before deposition takes place at low pressure on heated substrates in a cold wall geometry. This process allows, with stable evaporation rates for all three precursors, to grow in-situ superconducting films with constant composition from film to film. Thin and thick films with high critical temperatures and critical currents have been obtained (Tc>80K, Jc>10 4 A/cm 2 at 77K in self field) which are highly c-axis oriented. Experimental details of this new process are described and the effects of different process parameters are studied in order to improve the quality of the deposited layers. (orig.)

  1. Stoichiometry-, phase- and orientation-controlled growth of polycrystalline pyrite (FeS 2) thin films by MOCVD

    Science.gov (United States)

    Höpfner, C.; Ellmer, K.; Ennaoui, A.; Pettenkofer, C.; Fiechter, S.; Tributsch, H.

    1995-06-01

    The growth process of polycrystalline pyrite thin films employing low pressure metalorganic chemical vapor deposition (LP-MOCVD) in a vertical cold wall reactor has been investigated. Iron pentacarbonyl (IPC) and t-butyldisulfide (TBDS) were utilized as precursors. Study of the growth rate as a function of temperature reveals a kinetically controlled growth process with an activation energy of 73 kJ / mol over the temperature range from 250 to 400°C. From 500 to 630°C, the growth rate is mainly mass transport limited. Decomposition of the films into pyrrhotite (Fe 1 - xS) occurs at higher growth temperatures. The {S}/{Fe} ratio in the films has been controlled from 1.23 up to 2.03 by changing the TBDS partial pressure. With increasing deposition temperature, the crystallites in the films show the tendency to grow [100]-oriented on amorphous substrates at a growth rate of 2.5 Å / s. The grains show a preferential orientation in the [111] direction upon lowering the growth rate down to 0.3 Å / s. Temperatures above 550°C are beneficial in enhancing the grain size in the columnar structured films up to 1.0 μm.

  2. Stoichiometry-, phase- and orientation-controlled growth of polycrystalline pyrite (FeS{sub 2}) thin films by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Hoepfner, C.; Ellmer, K.; Ennaoui, A.; Pettenkofer, C.; Fiechter, S.; Tributsch, H. [Hahn-Meitner-Institut Berlin, Abteilung Solare Energetik, Berlin (Germany)

    1995-06-01

    The growth process of polycrystalline pyrite thin films employing low pressure metalorganic chemical vapor deposition (LP-MOCVD) in a vertical cold wall reactor has been investigated. Iron pentacarbonyl (IPC) and t-butyldisulfide (TBDS) were utilized as precursors. Study of the growth rate as a function of temperature reveals a kinetically controlled growth process with an activation energy of 73 kJ/mol over the temperature range from 250 to 400C. From 500 to 630C, the growth rate is mainly mass transport limited. Decomposition of the films into pyrrhotite (Fe{sub 1-x}S) occurs at higher growth temperatures. The S/Fe ratio in the films has been controlled from 1.23 up to 2.03 by changing the TBDS partial pressure. With increasing deposition temperature, the crystallites in the films show the tendency to grow [100]-oriented on amorphous substrates at a growth rate of 2.5 A/s. The grains show a preferential orientation in the [111] direction upon lowering the growth rate down to 0.3 A/s. Temperatures above 550C are beneficial in enhancing the grain size in the columnar structured films up to 1.0 {mu}m

  3. Cauliflower hillock formation through crystallite migration of SnO2 thin films prepared on alumina substrates by using MOCVD

    International Nuclear Information System (INIS)

    Choi, Gwangpyo; Ryu, Hyunwook; Lee, Woosun; Hong, Kwangjun; Shin, Dongcharn; Park, Jinseong; Seo, Yongjin; Akbar, Sheikh A.

    2003-01-01

    Tin-oxide thin films were deposited at 375 .deg. C on α-alumina substrates by using metalorganic chemical vapor deposition (MOCVD) process. A number of hillocks were formed on the film after annealing in air at 500 .deg. C for 30 min, but fewer hillocks were formed for annealing in N 2 . The hillocks on the film and the grains on the alumina substrate were composed of crystallites. The oxygen content and the binding energy after annealing in air came to close to values for the stoichiometric SnO 2 . There was no relationship between the film thickness and the binding energy shift, but the binding energy did change with the annealing atmosphere and the oxygen content. The cauliflower hillocks on the film seem to be formed by the continuous migration of crystallites from cauliflower grains on the substrate to release the stress due to the increased oxygen content and volume. A cauliflower hillock can be grown by continuous migration of crystallites from nearby grains to the hillock.

  4. A-axis oriented superconductive YBCO thin films. Growth mechanism on MgO substrate. [Y-Ba-Cu-O

    Energy Technology Data Exchange (ETDEWEB)

    Hamet, J F; Mercey, B; Hervieu, M; Poullain, G; Raveau, B [Centre de Materiaux Supraconducteurs, CRISMAT-ISMRa, 14 - Caen (France)

    1992-08-01

    The growth mechanism of a-axis oriented YBCO thin films has been studied by TEM. At 650degC, a disordered cubic perovskite is first formed with a[sub p]parallela[sub MgO], then a strained tetragonal a-axis oriented perovskite is observed, with c=3a[sub p], slightly misoriented with respect to MgO and showing a marquetry-like contrast. At 750degC, a [1anti 10] axis oriented perovskite is formed whose lattice exhibits a rotation with respect to MgO lattice, but also a tilting of the [CuO[sub 2

  5. Studies of proximity-effect and tunneling in YBCO/metal layered films

    Energy Technology Data Exchange (ETDEWEB)

    Greene, L.H.; Barner, J.B.; Feldmann, W.L.; Farrow, L.A.; Miceli, P.F.; Ramesh, R.; Wilkens, B.J.; Bagley, B.G.; Tarascon, J.M.; Wernick, J.H. (Bellcore, Red Bank, NJ (USA)); Giroud, M. (CRTBT-CNRS, Grenoble (France)); Rowell, J.M. (Conductus, Sunnyvale, CA (USA))

    1989-12-01

    The short coherence length of the high-Tc superconductors, coupled with their tendency to form non-superconducting surface layers, accounts for the difficulty in achieving good tunnel junctions. A proximity layer of a longer coherence length normal metal (N) is expected to ''draw out'' Cooper pairs. Our goal is to fabricate reproducible, planar tunnel junctions of SNIS layered structures for proximity tunneling spectroscopy. Such structures of YBCO/N/I/Pb and SNS structures of YBCO/N/Pb indicate that the normal metal produces a low resistance contact to the YBCO surface with a supercurrent observed in the SNS. The insulating barrier in the SNIS is reproducible, insulating and continuous: A sharp Pb gap and phonons from the counter-electrode are routinely observed. (orig.).

  6. Studies of proximity-effect and tunneling in YBCO/metal layered films

    International Nuclear Information System (INIS)

    Greene, L.H.; Barner, J.B.; Feldmann, W.L.; Farrow, L.A.; Miceli, P.F.; Ramesh, R.; Wilkens, B.J.; Bagley, B.G.; Tarascon, J.M.; Wernick, J.H.; Giroud, M.; Rowell, J.M.

    1989-01-01

    The short coherence length of the high-T c superconductors, coupled with their tendency to form non-superconducting surface layers, accounts for the difficulty in achieving good tunnel junctions. A proximity layer of a longer coherence length normal metal (N) is expected to draw out Cooper pairs. The authors' goal is to fabricate reproducible, planar tunnel junctions of SNIS layered structures for proximity tunneling spectroscopy. They discuss how such structures of YBCO/N/I/Pb and SNS structures of YBCO/N/Pb indicate that the normal metal produces a low resistance contact to the YBCO surface with a supercurrent observed in the SNS. The insulating barrier in the SNIS is reproducible, insulating and continuous: A sharp Pb gap and phonons from the counter-electrode are routinely observed

  7. Microstructures and precipitates in laser-ablated YBCO thin films on SrTiO[sub 3] (110). [Y-Ba-Cu-O

    Energy Technology Data Exchange (ETDEWEB)

    Catana, A. (IBM Research Div., Zurich Research Lab., Rueschlikon (Switzerland)); Rossel, C. (IBM Research Div., Zurich Research Lab., Rueschlikon (Switzerland)); Perrin, A. (Lab. de Chimie du Solide et Inorganique Moleculaire, Univ. de Rennes 1, 35 (France)); Guilloux-Viry, M. (Lab. de Chimie du Solide et Inorganique Moleculaire, Univ. de Rennes 1, 35 (France)); Thivet, C. (Lab. de Chimie du Solide et Inorganique Moleculaire, Univ. de Rennes 1, 35 (France))

    1993-05-10

    Thin YBCO films ([proportional to] 100 nm) have been deposited by laser ablation on SrTiO[sub 3] (110) substrates. Microstructural investigations have been performed by scanning tunneling and high-resolution electron microscopy. The results show that the surface corrugation is related to the growth of twisted YBCO domains that nucleate at the film/substrate interface. The twist is characterized by a 90 rotation of YBCO around the 100 and/or 010 axes, which results in [l brace]013[r brace] and/or [l brace]103[r brace] planes parallel to the substrate surface. Precipitates belonging to Y[sub 2]O[sub 3] are densely distributed on the film surface. No such second phases have been identified inside the YBCO films. The orientational relationship between precipitates and film is such that the lattice mismatch is minimized in the interface planes. A large number of precipitates grow from the film surface outwards. This phenomenon can be explained on the basis of lattice matching arguments and favorable growth kinetics. (orig.)

  8. Mocvd Growth of Group-III Nitrides on Silicon Carbide: From Thin Films to Atomically Thin Layers

    Science.gov (United States)

    Al Balushi, Zakaria Y.

    Group-III nitride semiconductors (AlN, GaN, InN and their alloys) are considered one of the most important class of materials for electronic and optoelectronic devices. This is not limited to the blue light-emitting diode (LED) used for efficient solid-state lighting, but other applications as well, such as solar cells, radar and a variety of high frequency power electronics, which are all prime examples of the technological importance of nitride based wide bandgap semiconductors in our daily lives. The goal of this dissertation work was to explore and establish new growth schemes to improve the structural and optical properties of thick to atomically thin films of group-III nitrides grown by metalorganic chemical vapor deposition (MOCVD) on SiC substrates for future novel devices. The first research focus of this dissertation was on the growth of indium gallium nitride (InGaN). This wide bandgap semiconductor has attracted much research attention as an active layer in LEDs and recently as an absorber material for solar cells. InGaN has superior material properties for solar cells due to its wavelength absorption tunability that nearly covers the entire solar spectrum. This can be achieved by controlling the indium content in thick grown material. Thick InGaN films are also of interest as strain reducing based layers for deep-green and red light emitters. The growth of thick films of InGaN is, however, hindered by several combined problems. This includes poor incorporation of indium in alloys, high density of structural and morphological defects, as well as challenges associated with the segregation of indium in thick films. Overcoming some of these material challenges is essential in order integrate thick InGaN films into future optoelectronics. Therefore, this dissertation research investigated the growth mechanism of InGaN layers grown in the N-polar direction by MOCVD as a route to improve the structural and optical properties of thick InGaN films. The growth

  9. Nucleation and growth of copper oxide films in MOCVD processes using the β-ketoiminate precursor 4,4'-(1,2-ethanediyldinitrilo)bis(2-pentanonate) copper(II)

    International Nuclear Information System (INIS)

    Condorelli, G.G.; Malandrino, G.; Fragala, I.L.

    1999-01-01

    The MOCVD of CuO has attracted much attention because of its application in high-T c superconducting films and gas sensors. This work focuses on the potential of a β-ketoiminate copper complex as an alternative MOCVD source to β-diketonate complexes. Particular attention has been given to factors such as texturing, roughness, and grain size of the deposit. (orig.)

  10. Optimization of Strontium Titanate (SrTiO3) Thin Films Fabricated by Metal Organic Chemical Vapor Deposition (MOCVD) for Microwave-Tunable Devices

    Science.gov (United States)

    2015-12-01

    characteristics . Our work demonstrated a significant increase in the quality of the optimized STO thin films with respect to STO films grown prior to the MOCVD...deposition, the reactor and precursor supply lines were baked at 250 °C for at least 4 h with a total Ar carrier gas flow of 5,000 sccm to remove...S. Thermal leakage characteristics of Pt/SrTiO3/Pt structures. Journal of Vacuum Science & Technology A. 2008;26:555–557. 31. Ryen L, Olsson E

  11. Excess hall effect in epitaxial YBCO film under moderate magnetic fields, approached by renormalized superconducting fluctuations model

    International Nuclear Information System (INIS)

    Puica, I.; Lang, W.; Goeb, W.; Sobolewski, R.

    2002-01-01

    Full text: Measurements of the Hall effect and the resistivity on precisely-patterned YBCO thin film in moderate magnetic fields B from 0.5 to 6 T oriented parallel to the crystallographic c axis reveal a sign reversal of the Hall coefficient for B < 3 T. The data are confronted with the full quantitative expressions given by the renormalized fluctuation model for the excess Hall conductivity. The model offers a satisfactory quantitative approach to the experimental results, for moderate fields and temperatures near the critical region, provided the inhomogeneity of the critical temperature distribution is also taken into account. For lower fields and temperatures, the adequacy of the model is altered by vortex pinning. (author)

  12. Preparation and microstructural properties of erbium doped alumina–yttria oxide thin films deposited by aerosol MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Salhi, Rached, E-mail: salhi_rached@yahoo.fr [Laboratoire de Science et Ingénierie des MAtériaux et Procédés 1130 rue de la PiscineBP 75-F-38402 Saint Martin D’Hères Cedex 1 (France); Laboratoire des Matériaux et du Génie Physique, CNRS UMR 5628, INP Grenoble-Minatec, 3 parvis Louis Néel BP 257, 38 016 Grenoble Cedex 1 (France); Jimenez, Carmen; Deschanvres, Jean-Luc [Laboratoire des Matériaux et du Génie Physique, CNRS UMR 5628, INP Grenoble-Minatec, 3 parvis Louis Néel BP 257, 38 016 Grenoble Cedex 1 (France); Guyot, Yannick [LPCML-UMR 5620 CNRS/UCBL Universite´ Claude Bernard Lyon 110 Rue Ada Byron 69622 Villeurbanne Cedex (France); Chaix-Pluchery, Odette; Rapenne, Laetitia [Laboratoire des Matériaux et du Génie Physique, CNRS UMR 5628, INP Grenoble-Minatec, 3 parvis Louis Néel BP 257, 38 016 Grenoble Cedex 1 (France); Maâlej, Ramzi [LPCML-UMR 5620 CNRS/UCBL Universite´ Claude Bernard Lyon 110 Rue Ada Byron 69622 Villeurbanne Cedex (France); Fourati, Mohieddine [Laboratoire de Chimie Industrielle, Ecole Nationale d’Ingénieur de Sfax, University of Sfax BP W 3038 Sfax (Tunisia); Laboratoire de Physique Appliquée, Groupe de Physique Théorique, Département de Physique, Faculté des Sciences de Sfax, University of Sfax 3018 Sfax (Tunisia)

    2013-10-15

    Erbium-doped aluminum–yttrium oxide films (Er: Al{sub 2}O{sub 3}–Y{sub 2}O{sub 3}) were prepared by aerosol-UV assisted Metalorganic Chemical Vapor Deposition (MOCVD) at 410 °C and annealed at 1000 °C. The effects of humidity of carrier gas and UV-assistance on their structure and optical properties were investigated using scanning electron microscope, X-ray diffraction and Transmission electron microscopy. It was found that under low air humidity and without UV-assistance the films present a low mol% Al{sub 2}O{sub 3} (10 mol%) two different structural phases are observed corresponding to the cubic and the monoclinic structures of Y{sub 2}O{sub 3}. When the deposition takes place under high air humidity and with UV assistance the Er:Al{sub 2}O{sub 3}–Y{sub 2}O{sub 3} films present a very high mol% Al{sub 2}O{sub 3} (88 mol%) and crystallize in the Y{sub 3}Al{sub 5}O{sub 12} (YAG) compound mixed with an amorphous phase. The Er{sup 3+} luminescence analyzed in the visible and IR regions, shows the classical green transitions. The best optical properties were obtained with the Er:Al{sub 2}O{sub 3}–Y{sub 2}O{sub 3} films grown under high air humidity with UV-assistance. Under such deposition conditions, {sup 4}I{sub 13/2} lifetimes was found to be 1.1 ms. This indicates that the deposition conditions, in particular air humidity, play an important role in the luminescent properties even after annealing. -- Highlights: • We investigate the effects of humidity and UV on the properties of Er:Al{sub 2}O{sub 3}–Y{sub 2}O{sub 3}. • Under low air humidity and without UV-assistance the films present a low mol% Al{sub 2}O{sub 3}. • Under high air humidity and with UV the Er:Al{sub 2}O{sub 3}–Y{sub 2}O{sub 3} present high mol% Al{sub 2}O{sub 3}. • The film crystallize in the YAG phase mixed with an amorphous phase. • The best optical properties were obtained under high air humidity with UV-assistance.

  13. Contribution towards ALD and MOCVD of rare earth oxides and hafnium oxide. From precursor evaluation to process development and thin film characterization

    International Nuclear Information System (INIS)

    Xu, Ke

    2013-01-01

    This PhD thesis is consisted of two major parts: precursor development for ALD and MOCVD applications as well as thin film deposition using ALD and MOCVD with self developed precursors. The first part of this work presents the synthesis, characterization and detailed thermal property investigations of different novel group IV and rare earth precursor classes (guandinate, guanidine and ketoiminate). The second part of this work presents the ALD and MOCVD depositions using various guanidinate precursors for forming corresponding metal oxide thin films. The overall motivation of this work is to fulfill the lack of precursors of rare earth and group IV elements for ALD and MOCVD applications that satisfy the stringent requirements for the modern microelectronic and optoelectronic technologies. The aspect of the precursor engineering part is focusing on influence of ligand sphere on precursors' chemical and thermal properties. In this way, we successfully introduced guanidine and ketoiminate as potential ligands for the precursor design. The thin film deposition part of this work is ALD of rare earth oxides and group IV oxides employing literature known compounds which were previously developed in our research group. The main focus was dedicated to the process optimization, the characterization of the structural, morphological, compositional and functional properties of the deposited thin films. Certain film properties were discussed comparatively with the corresponding thin films deposited with literature known precursors. It was already shortly demonstrated in Chapter 6 that the guanidine ligand showed potential interest as suitable ligand for precursor engineering. This titan guanidine precursor [Ti(NC(NMe 2 ) 2 ) 4 ] (GD1) possesses higher thermal stability compared to its parent amide, [Ti(NMe 2 ) 4 ], while reactivity against water is not significantly affected. It could be very interesting to transfer this ligand for the precursor development of rare earth

  14. Synthesis, characterization, and thermal properties of homoleptic rare-earth guanidinates: promising precursors for MOCVD and ALD of rare-earth oxide thin films.

    Science.gov (United States)

    Milanov, Andrian P; Fischer, Roland A; Devi, Anjana

    2008-12-01

    Eight novel homoleptic tris-guanidinato complexes M[(N(i)Pr)(2)CNR(2)](3) [M = Y (a), Gd (b), Dy (c) and R = Me (1), Et (2), (i)Pr (3)] have been synthesized and characterized by NMR, CHN-analysis, mass spectrometry and infrared spectroscopy. Single crystal structure analysis revealed that all the compounds are monomers with the rare-earth metal center coordinated to six nitrogen atoms of the three chelating guanidinato ligands in a distorted trigonal prism geometry. With the use of TGA/DTA and isothermal TGA analysis, the thermal characteristics of all the complexes were studied in detail to evaluate their suitability as precursors for thin film deposition by MOCVD and ALD. The (i)Pr-Me(2)N-guanidinates of Y, Gd and Dy (1a-c) showed excellent thermal characteristics in terms of thermal stability and volatility. Additionally, the thermal stability of the (i)Pr-Me(2)N-guanidinates of Y and Dy (1a, c) in solution was investigated by carrying out NMR decomposition experiments and both the compounds were found to be remarkably stable. All these studies indicate that (i)Pr-Me(2)N-guanidinates of Y, Gd and Dy (1a-c) have the prerequisites for MOCVD and ALD applications which were confirmed by the successful deposition of Gd(2)O(3) and Dy(2)O(3) thin films on Si(100) substrates. The MOCVD grown films of Gd(2)O(3) and Dy(2)O(3) were highly oriented in the cubic phase, while the ALD grown films were amorphous.

  15. MOCVD with gas phase composition control for the growth of high quality YBa2Cu3O7-x thin films for microwave applications

    International Nuclear Information System (INIS)

    Musolf, J.

    1997-01-01

    The MOCVD growth technique has demonstrated YBa 2 Cu 3 O 7-x thin films with adequate transport properties (T c >90 K, J c > x 10 6 A cm -2 , R s p /C v ) and the species concentrations. After determining the correlation between gas phase and solid phase composition this technique enables the reproducible growth of YBa 2 Cu 3 O 7-x thin films by MOCVD with composition very close to 123. Further refinement of growth temperature, total pressure, oxygen partial pressure and total flow rates has produced films with excellent properties. Smooth surface morphology with a low density of outgrowths ( 4 cm -2 ), narrow XRD rocking curve peaks FWHM c =92 K), low surface resistance (device R s <350 μΩ at 77 K, 10 GHz) have been demonstrated using this growth concept. Special focus was placed on optimization of the performance of a microwave test device which serves as a process control monitor of the suitability of these films for passive microwave applications. (orig.)

  16. Study on the optimization of the deposition rate of planetary GaN-MOCVD films based on CFD simulation and the corresponding surface model

    Science.gov (United States)

    Li, Jian; Fei, Ze-yuan; Xu, Yi-feng; Wang, Jie; Fan, Bing-feng; Ma, Xue-jin; Wang, Gang

    2018-02-01

    Metal-organic chemical vapour deposition (MOCVD) is a key technique for fabricating GaN thin film structures for light-emitting and semiconductor laser diodes. Film uniformity is an important index to measure equipment performance and chip processes. This paper introduces a method to improve the quality of thin films by optimizing the rotation speed of different substrates of a model consisting of a planetary with seven 6-inch wafers for the planetary GaN-MOCVD. A numerical solution to the transient state at low pressure is obtained using computational fluid dynamics. To evaluate the role of the different zone speeds on the growth uniformity, single factor analysis is introduced. The results show that the growth rate and uniformity are strongly related to the rotational speed. Next, a response surface model was constructed by using the variables and the corresponding simulation results. The optimized combination of the matching of different speeds is also proposed as a useful reference for applications in industry, obtained by a response surface model and genetic algorithm with a balance between the growth rate and the growth uniformity. This method can save time, and the optimization can obtain the most uniform and highest thin film quality.

  17. Structural and optical properties of GaN thin films grown on Al2O3 substrates by MOCVD at different reactor pressures

    International Nuclear Information System (INIS)

    Guillén-Cervantes, A.; Rivera-Álvarez, Z.; López-López, M.; Ponce-Pedraza, A.; Guarneros, C.; Sánchez-Reséndiz, V.M.

    2011-01-01

    GaN thin films grown by MOCVD on (0 0 0 1) Al 2 O 3 substrates at different growth pressures were characterized by field-emission scanning electron microscopy, atomic force microscopy, micro-Raman, and photoluminescence at room temperature. It was found that there is an optimum pressure of 76 Torr at which the structural and optical properties of the GaN samples are superior. On the other hand samples grown at higher pressure exhibited hexagonal surface pits and surface spirals. The results showed that the growth pressure strongly influences the morphology, and significantly affects the structural and optical properties of the GaN epilayers.

  18. Growth and characterization of germanium epitaxial film on silicon (001 with germane precursor in metal organic chemical vapour deposition (MOCVD chamber

    Directory of Open Access Journals (Sweden)

    Kwang Hong Lee

    2013-09-01

    Full Text Available The quality of germanium (Ge epitaxial film grown directly on a silicon (Si (001 substrate with 6° off-cut using conventional germane precursor in a metal organic chemical vapour deposition (MOCVD system is studied. The growth sequence consists of several steps at low temperature (LT at 400 °C, intermediate temperature ramp (LT-HT of ∼10 °C/min and high temperature (HT at 600 °C. This is followed by post-growth annealing in hydrogen at temperature ranging from 650 to 825 °C. The Ge epitaxial film of thickness ∼ 1 μm experiences thermally induced tensile strain of 0.11 % with a treading dislocation density (TDD of ∼107/cm2 and the root-mean-square (RMS roughness of ∼ 0.75 nm. The benefit of growing Ge epitaxial film using MOCVD is that the subsequent III-V materials can be grown in-situ without the need of breaking the vacuum hence it is manufacturing worthy.

  19. MOCVD of hexagonal boron nitride thin films on Si(100) using new single source precursors

    CERN Document Server

    Boo, J H; Yu, K S; Kim, Y S; Kim, Y S; Park, J T

    1999-01-01

    We have been carried out the growth of hexagonal boron nitride (h-BN) thin films on Si(100) substrates by low pressure metal-organic chemical vapor deposition (LPMOCVD) method using triethylborane tert-butylamine complex (TEBTBA), Et sub 3 BNH sub 2 ( sup t Bu), and triethylborane isopropylamine complex (TEBIPA), Et sub 3 BNH sub 2 ( sup t Pr) as a new single molecular precursors in the temperature range of 850 approx 1000 .deg. C. polycrystalline, crack-free h-BN film was successfully grown on Si(100) substrate at 850 .deg. C using TEBTBA. This growth temperature is very lower than those in previous reports. Carbon-rich polycrystalline BN was also obtained at 900 .deg. C from TEBIPA. With increasing substrate temperature to 1000 .deg. C, however, BC sub 4 N-like species are strongly formed along with h-BN and the BN films obtained from both TEBTBA and TEBIPA but almost polycrystalline. To our best knowledge, this is the first report of the growth of h-BN films formed with the new single source precursors of ...

  20. Rare earth [beta]-diketonate and carboxylate metal complexes as precursors for MOCVD of oxide films

    Energy Technology Data Exchange (ETDEWEB)

    Kuzmina, N.P. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Martynenko, L.I. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Tu, Z.A. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Kaul, A.R. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Girichev, G.V. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Giricheva, N.I. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Rykov, A.N. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Korenev, Y.M. (Dept. of Chemistry, Moscow State Univ. (Russian Federation))

    1993-08-01

    Volatile and thermostable complexes of lanthanide acetylacetonates and pivalates were obtained and investigated by different methods. These compounds were used for lanthanide oxide containing film producing and for fabrication of silica optical fibers doped by lanthanide oxide. The properties of these and already known volatile precursors are compared. (orig.).

  1. Rare earth β-diketonate and carboxylate metal complexes as precursors for MOCVD of oxide films

    International Nuclear Information System (INIS)

    Kuzmina, N.P.; Martynenko, L.I.; Tu, Z.A.; Kaul, A.R.; Girichev, G.V.; Giricheva, N.I.; Rykov, A.N.; Korenev, Y.M.

    1993-01-01

    Volatile and thermostable complexes of lanthanide acetylacetonates and pivalates were obtained and investigated by different methods. These compounds were used for lanthanide oxide containing film producing and for fabrication of silica optical fibers doped by lanthanide oxide. The properties of these and already known volatile precursors are compared. (orig.)

  2. Surface Passivation for 3-5 Semiconductor Processing: Stable Gallium Sulphide Films by MOCVD

    Science.gov (United States)

    Macinnes, Andrew N.; Jenkins, Phillip P.; Power, Michael B.; Kang, Soon; Barron, Andrew R.; Hepp, Aloysius F.; Tabib-Azar, Massood

    1994-01-01

    Gallium sulphide (GaS) has been deposited on GaAs to form stable, insulating, passivating layers. Spectrally resolved photoluminescence and surface recombination velocity measurements indicate that the GaS itself can contribute a significant fraction of the photoluminescence in GaS/GaAs structures. Determination of surface recombination velocity by photoluminescence is therefore difficult. By using C-V analysis of metal-insulator-semiconductor structures, passivation of the GaAs with GaS films is quantified.

  3. Optimization of the low-temperature MOCVD process for PZT thin films

    CERN Document Server

    Wang, C H; Choi, D J

    2000-01-01

    Pb(Zr sub X Ti sub 1 sub - sub X)O sub 3 (PZT) thin films of about 0.34 nm were successfully grown at a low temperature of 500 .deg. C by metalorganic chemical vapor deposition with a beta-diketonate complex of Pb(tmhd) sub 2 , zirconium t-butoxide, and titanium isopropoxide as source precursors. Ferroelectric capacitors of a Pt/PZT/Pt configuration were fabricated, and their structural and electrical properties were investigated as a function of the input Pb/(Zr+Ti) and Zr/(Zr+Ti) source ratios. The structure of the as-grown films at 500 .deg. C changed from tetragonal to pseudocubic with increasing the Zr/(Zr+Ti) ratio above an input Pb/(Zr+Ti) source ratio of 5.0 while a 2nd phase of ZrO sub 2 was only observed below Pb/(Zr+Ti) ratio of 5.0, regardless of the Zr/(Zr+Ti) ratio. The dielectric constant and loss of the PZT films were 150-1200 and 0.01-0.04 at 100 kHz, respectively, Leakage current densities decreased with increasing the Zr/(Zr+Ti) ratio. The process window for growing a single phase PZT is ve...

  4. Superconducting thin films of YBa2Cu3O7-x

    International Nuclear Information System (INIS)

    Hudner, J.

    1993-01-01

    Thin films of the high temperature superconductor YBa 2 Cu 3 O 7-x (YBCO) are of significance in fundamental studies of oxide superconductors and for prospected electronic applications based on superconductors operating at liquid nitrogen temperatures (T= 77 K). Synthesis of YBCO thin films is complex and a large part of this thesis has been devoted to the elaboration of various techniques in forming YBCO thin films. A general observation was that synthesis of YBCO films exhibiting high zero-resistivity temperatures temperatures (T c ) ≥ 88 K and elevated critical current densities (J c ) ≥ 10 6 A/cm 2 at 77 K was possible under widely different conditions of film growth. For the BaF 2 -based method, various substrate materials were investigated. Among perovskite related substrates with low losses in the high frequency regime, LaA10 3 was found to yield YBCO films exhibiting the highest quality electrical properties. A study of YBCO film interaction with sapphire substrates was performed. It was suggested that the YBCO film on sapphire consists of weakly coupled superconducting grains. Compositional effects of Y, BA and Cu for MOCVD-YBCO films were examined with respect to morphology, structure, resistivity, as susceptibility and J c (T). High T c :s and J c :s were observed for an anomalous large compositional range of Cu in off-compositional YBCO films. This was shown to be related to the formation of Cu-rich precipitates embedded within a c-Axis oriented stoichiometric YBCO film matrix. Thermal critical current behavior at zero field in thin films of YBCO fabricated by various methods has been studied by three techniques: transport measurements on patterned microbridges, dc magnetization hysteresis loops using the Bean model and non-linear ac susceptibility analysis. Absolute critical current values obtained form the two former techniques when measured on the same YBCO film were observed to differ about a factor of two. The feasibility of non-linear ac

  5. Different defect levels configurations between double layers of nanorods and film in ZnO grown on c-Al2O3 by MOCVD

    International Nuclear Information System (INIS)

    Wu, Bin; Zhang, Yuantao; Shi, Zhifeng; Li, Xiang; Cui, Xijun; Zhuang, Shiwei; Zhang, Baolin; Du, Guotong

    2014-01-01

    Epitaxial ZnO structures with inherent two layers of nanorods layer on film layer were fabricated on c-Al 2 O 3 by metal-organic chemical vapor deposition (MOCVD) and studied by photoluminescence. Specially, photoluminescence spectra for the film layer were obtained by rendering the excitation from the substrate side. Different defect levels configurations between nanorods and film were revealed. Zinc vacancies tend to form in top nanorods layer, whereas abundant zinc–oxygen divacancies accumulate in bottom film layer. An acceptor state with activation energy of ∼200 meV is exclusive to the film layer. The stacking fault related acceptor and Al introduced donor are present in both layers. Besides, two other defect related donors contained in the nanorods layer perhaps also exist within the film layer. - Highlights: • Inherent double layer ZnO of nanorods on film layer were studied by PL. • V Zn tend to form in the nanorods layer, and V ZnO accumulate in the film layer. • An acceptor with activation energy of ∼200 meV is exclusive to the film layer. • Pure NBE emission without DLE in RT PL spectrum does not mean good crystallinity

  6. Preparation of Anatase TiO2 Thin Films with (OiPr)2Ti(CH3COCHCONEt2)2 Precursor by MOCVD

    International Nuclear Information System (INIS)

    Bae, Byoung Jae; Seo, Won Seok; Miah, Arzu; Park, Joon T.; Lee, Kwang Yeol; Kim, Keun Chong

    2004-01-01

    The reaction of titanium tetraisopropoxide with 2 equiv of N,N-diethyl acetoacetamide affords Ti(O i Pr) 2 (CH 3 COCHCONEt 2 ) 2 (1) as colorless crystals in 80% yield. Compound 1 is characterized by spectroscopic (Mass and 1 H/ 13 C NMR) and microanalytical data. Molecular structure of 1 has been determined by a single crystal X-ray diffraction study, which reveals that it is a monomeric, cis-diisopropoxide and contains a six coordinate Ti(IV) atom with a cis(CONEt 2 ), trans(COCH 3 ) configuration (1a) in a distorted octahedral environment. Variable-temperature 1 H NMR spectra of 1 indicate that it exists as an equilibrium mixture of cis, trans (1a) and cis, cis (1b) isomers in a 0.57 : 0.43 ratio at -20 .deg. C in toluene-d 8 solution. Thermal properties of 1 as a MOCVD precursor for titanium dioxide films have been evaluated by thermal gravimetric analysis and vapor pressure measurement. Thin films of pure anatase titanium dioxide (after annealing above 500 .deg. C under oxygen) have been grown on Si(100) with precursor 1 in the substrate temperature range of 350- 500 .deg. C using a bubbler-based MOCVD method

  7. Thermal activation of nitrogen acceptors in ZnO thin films grown by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Dangbegnon, J.K.; Talla, K.; Botha, J.R. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth (South Africa)

    2010-06-15

    Nitrogen doping in ZnO is inhibited by spontaneous formation of compensating defects. Perfect control of the nitrogen doping concentration is required, since a high concentration of nitrogen could induce the formation of donor defects involving nitrogen. In this work, the effect of post-growth annealing in oxygen ambient on ZnO thin films grown by Metalorganic Chemical Vapor Deposition, using NO as both oxidant and nitrogen dopant, is studied. After annealing at 700 C and above, low-temperature photoluminescence shows the appearance of a transition at {proportional_to}3.23 eV which is interpreted as pair emission involving a nitrogen acceptor. A second transition at {proportional_to}3.15 eV is also discussed. This work suggests annealing as a potential means for p-type doping using nitrogen (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  8. Advanced high temperature superconductor film-based process using RABiTS

    International Nuclear Information System (INIS)

    Goyal, A.; Hawsey, R.A.; Hack, J.; Moon, D.

    2000-01-01

    The purpose of this Cooperative Research and Development Agreement (CRADA) between Lockheed Martin Energy Research Corporation (Contractor), Managing contractor for Oak Ridge National Laboratory (ORNL) and Midwest Superconductivity, Inc. (MSI) and Westinghouse Science and Electric Company (WEC) was to develop the basis for a commercial process for the manufacturing of superconducting tape based on the RABiTS technology developed at ORNL. The chosen method for deposition of YBCO films on RABiTS was Metal Organic chemical Vapor Deposition (MOCVD)

  9. Modeling flux pinning in thin undoped and BazRo3-doped YBCO films

    DEFF Research Database (Denmark)

    Paturi, P.; Irjala, M.; Huhtinen, H.

    2009-01-01

    A simple model based on distributions of twin boundaries, dislocations, and BaZrO3 nanorods is presented to describe the Jc properties of undoped and BaZrO3 (BZO)-doped YBa2Cu3Ox thin films. The model accurately describes the shape of Jc(B,T) curves of the films, when the pinning site distributions...... are taken from distributions of twin spacings and BZO nanorods from transmission electron microscope images. Thus, assuming that the model can be used for prediction of the Jc properties, we conclude that for enhancement of undoped films more crystalline defects are needed and for doped films a dopant...

  10. Critical current density and microwave surface resistance of 5-cm-diameter YBCO films on LaAlO3 substrates prepared by MOD using an infrared image furnace

    International Nuclear Information System (INIS)

    Manabe, T.; Kondo, W.; Yamaguchi, I.; Sohma, M.; Tsuchiya, T.; Tsukada, K.; Mizuta, S.; Kumagai, T.

    2005-01-01

    Inductive critical current density (J c ) and microwave surface resistance (R s ) were investigated for 0.7-μm-thick epitaxial YBa 2 Cu 3 O 7-y (YBCO) films on 5-cm-diameter LaAlO 3 substrates prepared by a chemical solution-based metal organic deposition (MOD) process using an infrared image furnace. By varying the heating rate at ramp during the final heat treatment, we obtained various orientations of YBCO; the c- and a-axis orientation at a slower rate, i.e., 20-100 deg C/min while the pure c-axis orientation at a faster rate, 200 deg C/min. The c-axis-oriented YBCO films showed excellent superconducting properties; for example, a high inductive-J c (77 K) of 2.6 MA/cm 2 and low R s (12 GHz)'s of 0.24 and 0.52 mΩ at 50 and 77 K, respectively, by a sapphire rod resonator method. The c- and a-axis-oriented films exhibited a lower J c and a higher R s . It was found that the J c and R s values of MOD-derived YBCO films showed a strong correlation; approximately, R s is inversely proportional to J c . This correlation is in good agreement with a previous report by Ohshima et al. for sputtered-YBCO films on BaSnO 3 -buffered MgO substrates

  11. Vaporization of a mixed precursors in chemical vapor deposition for YBCO films

    Science.gov (United States)

    Zhou, Gang; Meng, Guangyao; Schneider, Roger L.; Sarma, Bimal K.; Levy, Moises

    1995-01-01

    Single phase YBa2Cu3O7-delta thin films with T(c) values around 90 K are readily obtained by using a single source chemical vapor deposition technique with a normal precursor mass transport. The quality of the films is controlled by adjusting the carrier gas flow rate and the precursor feed rate.

  12. Properties of HTS YBCO thin films deposited on tilted NdGaO{sub 3} substrates

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T. [Laboratory of Superconductivity and Cryoelectronics, Institute of Electronics BAS, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria)]. E-mail: timur@ie.bas.bg; Donchev, T. [Laboratory of Superconductivity and Cryoelectronics, Institute of Electronics BAS, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Mateev, E. [Laboratory of Superconductivity and Cryoelectronics, Institute of Electronics BAS, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Miteva, S. [Laboratory of Superconductivity and Cryoelectronics, Institute of Electronics BAS, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Mozhaev, P.B. [Institute of Physics and Technology RAS, Nakhimovsky Ave. 36, 117218 Moscow (Russian Federation); Mozhaeva, J.E. [Institute of Physics and Technology RAS, Nakhimovsky Ave. 36, 117218 Moscow (Russian Federation)

    2005-03-15

    Thin YBa{sub 2}Cu{sub 3}O{sub 7} films were fabricated by 2-opposed DC magnetron sputtering onto NdGaO{sub 3} substrates, tilted from standard (1 1 0) orientation by 0-26 deg , and their surface morphology and electrical characteristics were investigated. Normal state resistivity (at 295 K) and microwave surface resistance (at 77 K and {approx}8 GHz) of the films demonstrated anisotropy, introduced by the tilted substrate, and some improvement of the superconducting parameters of the films was observed at small tilt angles ({theta} {approx} 1.5-3 deg ). The increase of the microwave surface resistance at high tilt angles for the current tracks, perpendicular to the steps of the substrate, was described in the framework of a simple model, which takes into account the complex conductivity of the film and the weak links between the film terraces.

  13. Properties of HTS YBCO thin films deposited on tilted NdGaO3 substrates

    International Nuclear Information System (INIS)

    Nurgaliev, T.; Donchev, T.; Mateev, E.; Miteva, S.; Mozhaev, P.B.; Mozhaeva, J.E.

    2005-01-01

    Thin YBa 2 Cu 3 O 7 films were fabricated by 2-opposed DC magnetron sputtering onto NdGaO 3 substrates, tilted from standard (1 1 0) orientation by 0-26 deg , and their surface morphology and electrical characteristics were investigated. Normal state resistivity (at 295 K) and microwave surface resistance (at 77 K and ∼8 GHz) of the films demonstrated anisotropy, introduced by the tilted substrate, and some improvement of the superconducting parameters of the films was observed at small tilt angles (θ ∼ 1.5-3 deg ). The increase of the microwave surface resistance at high tilt angles for the current tracks, perpendicular to the steps of the substrate, was described in the framework of a simple model, which takes into account the complex conductivity of the film and the weak links between the film terraces

  14. High temperature superconducting YBCO microwave filters

    Science.gov (United States)

    Aghabagheri, S.; Rasti, M.; Mohammadizadeh, M. R.; Kameli, P.; Salamati, H.; Mohammadpour-Aghdam, K.; Faraji-Dana, R.

    2018-06-01

    Epitaxial thin films of YBCO high temperature superconductor are widely used in telecommunication technology such as microwave filter, antenna, coupler and etc., due to their lower surface resistance and lower microwave loss than their normal conductor counterparts. Thin films of YBCO were fabricated by PLD technique on LAO substrate. Transition temperature and width were 88 K and 3 K, respectively. A filter pattern was designed and implemented by wet photolithography method on the films. Characterization of the filter at 77 K has been compared with the simulation results and the results for a made gold filter. Both YBCO and gold filters show high microwave loss. For YBCO filter, the reason may be due to the improper contacts on the feedlines and for gold filter, low thickness of the gold film has caused the loss increased.

  15. Defining B-c, B* and B-phi for YBCO Thin Films

    DEFF Research Database (Denmark)

    Paturi, Petriina; Irjala, Matti; Abrahamsen, Asger Bech

    2009-01-01

    of superconducting films. Similarly, the characteristic field, B c, can be obtained from magneto-optical (MO) images from when the flux fronts meet in the middle of the film. The matching field, B phi, at which there is one vortex line per pinning site, is sometimes thought to be the same as B*, but in BaZrO3-doped...... YBa2Cu3O7 films the calculated B phi is much higher than the observed B*. B phi can be determined from angular dependent transport measurements. All of the field values correspond to some special case in the flux pinning in the film and relate to J c. In this work we have determined B c, B* and B phi...

  16. Factors that determine the presence of particles in YBCO films grown by PLD

    International Nuclear Information System (INIS)

    Barrales-Guadarrama, V R; Rodríguez-Rodríguez, E M; Barrales-Guadarrama, R; Reyes Ayala, N

    2017-01-01

    The method of growing thin films PLD, is widely used in applications and possesses great potential in thin YBa 2 Cu 3 O 7-δ films production with outstanding physical properties. However, it is limited in nano and micro technology due to the presence of particles on the surface of the films. This article describes some causes that create these particles. YBa 2 Cu 3 O 7-δ films have been grown on electrolytic copper used as a variable model the distance target-substrate. The effects are studied through Scanning Electronic Microscopy. It is observed particles with a large variety of shapes and distributions. The results show that ranging the target-substrate distance, the superficial morphology is modified. An evidence of it, is that the evaporation of d B-S = 7 cm, is more coherent that d B-S = 3 cm. Therefore, exist a relation between the morphology and the parameters of growing. Also affect, the structural change that exists among the substrate and the film formation, the substrate preparation and it must not be monocrystalline, these factors define a kinetic and a mechanism of growing that promotes a heterogeneous nucleation. (paper)

  17. The effect of a slight mis-orientation angle of c-plane sapphire substrate on surface and crystal quality of MOCVD grown GaN thin films

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Seong-Woo; Suzuki, Toshimasa [Nippon Institute of Technology, 4-1 Gakuendai, Miyashiro, Saitama, 345-8501 (Japan); Aida, Hideo [NAMIKI Precision Jewel Co. Ltd., 3-8-22 Shinden, Adachi-ku, Tokyo, 123-8511 (Japan)

    2004-09-01

    The effect of a slight mis-orientation of c-plane sapphire substrate on the surface morphology and crystal quality of GaN thin films grown by MOCVD has been investigated. The mis-orientation angle of vicinal c-plane sapphire substrate was changed within the range of 0.00(zero)-1.00(one) degree, and the experimental results were compared with those on just angle (zero degree) c-plane sapphire substrate. The surface morphology and crystal quality were found to be very sensitive to mis-orientation angle. Consequently, the mis-orientation angle was optimized to be 0.15 . (copyright 2004 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  18. Microwave absorption in YBCO/PrBCO superlattices

    International Nuclear Information System (INIS)

    Carlos, W.E.; Kaplan, R.; Lowndes, D.H.; Norton, D.P.

    1992-01-01

    In this paper, non-resonant microwave absorption is employed to probe YBCO/PrBCO superlattices and compare the response to that of a YBCO film. Near the transition temperatures, the response of the superlattice samples and the YBCO film have similar amplitudes and orientation dependencies. At lower temperatures, the response of the superlattices is much stronger than that of the YBCO film and, while both responses are hysteretic at low temperatures, the widths of the hysteresis have opposite orientation dependencies, which the authors attribute to the role of the PrBCO layers

  19. A low-fluorine solution with a 2:1 F/Ba mole ratio for the fabrication of YBCO films

    DEFF Research Database (Denmark)

    Wu, Wei; Feng, Feng; Yue, Zhao

    2014-01-01

    must be at least 2 for full conversion of the Ba-precursor to BaF2 to avoid the formation of BaCO3, which is detrimental to the superconducting performance of YBCO films. In this study, a solution with a 2:1 F/Ba mole ratio was developed, and the fluorine content of this solution was approximately only...... 10.3% of that used in the conventional TFA-MOD method. Attenuated total reflectance-Fourier transform-infrared spectra (ATR-FT-IR) revealed that BaCO3 was remarkably suppressed in the as-pyrolyzed film—and eliminated at 700 °C. Thus, YBCO films with a critical current density (Jc) of over 5 MA cm−2...... (77 K, 0 T, 200 nm thickness) could be obtained on lanthanum aluminate single-crystal substrates. In situ FT-IR spectra showed that no obvious fluorinated gaseous by-products were detected in the pyrolysis step, which indicated that all F atoms might remain in the film as fluorides. X-ray diffraction...

  20. Nonlinear surface impedance of YBCO thin films: Measurements, modeling, and effects in devices

    International Nuclear Information System (INIS)

    Oates, D.E.; Koren, G.; Polturak, E.

    1995-01-01

    High-T c thin films continue to be of interest for passive device applications at microwave frequencies, but nonlinear effects may limit the performance. To understand these effects we have measured the nonlinear effects may limit the performance. To understand these effects we have measured the nonlinear surface impedance Z s in a number of YBa 2 Cu 3 O 7-x thin films as a function of frequency from 1 to 18 GHz, rf surface magnetic field H rf to 1500 Oe, and temperature from 4 K to T c . The results at low H rf are shown to agree quantitatively with a modified coupled-grain model and at high H rf with hysteresis-loss calculations using the Bean critical-state model applied to a thin strip. The loss mechanisms are extrinsic properties resulting from defects in the films. We also report preliminary measurements of the nonlinear impedance of Josephson junctions, and the results are related to the models of nonlinear Z s . The implications of nonlinear Z s for devices are discussed using the example of a five-pole bandpass filter

  1. High-spatial resolution resistivity mapping of large-area YBCO films by a near-field millimeter-wave microscope

    International Nuclear Information System (INIS)

    Golosovsky, M.; Galkin, A.; Davidov, D.

    1996-01-01

    The authors demonstrate a new millimeter-wave technique for the resistivity mapping of large-area conducting films, namely, a near-field resistivity microscope. The microscope is based on the idea that electromagnetic waves are transmitted through a narrow resonant slit with high efficiency. By scanning this slit at fixed height above an inhomogeneous conducting surface and measuring the intensity and phase of the reflected wave, the resistivity of this surface may be determined with a 10--100 microm spatial resolution using 80-GHz radiation. Using this technique, they map normal-sate resistivity of 1 in x 1 in YBCO films at ambient temperature. In some films they find inhomogeneities of the normal-state sheet resistance of the order of 10%--20%

  2. Measurements and analysis of the noise spectral density of YBCO films

    International Nuclear Information System (INIS)

    Taoufik, A.; Bghour, M.; Labrag, A.; Bouaaddi, A.; Abaragh, A.; Ramzi, A.; Senoussi, S.; Tirbiyine, A.

    2006-01-01

    We studied the voltage noise spectral density S V (f,T,H) dependence on frequency f, temperature T and applied magnetic field H in YBa 2 Cu 3 O 7-δ films. The voltage noise spectral density S V (f) as a function of frequency exhibits 1/f behavior according to a Lorentzian shape A [(1+πf/f 0 ) B ] C , where A, f 0 , B, C constants which are determined and compared for many values of H. The influence of temperature and magnetic field is clearly observed as a function of temperature, S V (T) is found to vanish at T g , the temperature of vortex glass transition, according to a (T-T g ) x law. We interpreted those results by the formation of a large distribution of glass vortex domains. Approaching T g , these domains grow in size and lifetime, while at T g those parameters diverge. (copyright 2006 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (Abstract Copyright [2006], Wiley Periodicals, Inc.)

  3. Fabrication and characterization of hybrid Nb-YBCO dc SQUIDs

    International Nuclear Information System (INIS)

    Frack, E.K.; Drake, R.E.; Patt, R.; Radparvar, M.

    1991-01-01

    This paper reports on the fabrication of hybrid low T c /high T c dc SQUIDs of two flavors. The first kind utilizes niobium tunnel junctions and a YBCO film strip as the most inductive portion of the SQUID loop. This configuration allows a direct measurement of the inductance of the YBCO microstrip from which the effective penetration depth can be calculated. The successful fabrication of these SQUIDs has required 1. superconducting Nb-to-YBCO contacts, 2. deposition and patterning of an SiO 2 insulation layer over YBCO, and 3. selective patterning of niobium and SiO 2 relative to YBCO. All these process steps are pertinent to the eventual use of YBCO thin films in electronic devices

  4. Plasmas for the low-temperature growth of high-quality GaN films by molecular beam epitaxy and remote plasma MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Losurdo, M.; Capezzuto, P.; Bruno, G. [Plasmachemistry Research Center, CNR, Bari (Italy); Namkoong, G.; Doolittle, W.A.; Brown, A.S. [Georgia Inst. of Tech., Atlanta (United States). School of Electrical and Computer Engineering, Microelectronic Research Center

    2002-03-16

    GaN heteroepitaxial growth on sapphire (0001) substrates was carried out by both radio-frequency (rf) remote plasma metalorganic chemical vapor deposition (RP-MOCVD) and molecular beam epitaxy (MBE). A multistep growth process including substrate plasma cleaning and nitridation, buffer growth, its subsequent annealing and epilayer growth was used. In order to achieve a better understanding of the GaN growth, in-situ real time investigation of the surface chemistry is performed for all the steps using the conventional reflection high-energy electron spectroscopy (RHEED) during the MBE process, while laser reflectance interferometry (LRI) and spectroscopic ellipsometry (SE), which do not require UHV conditions, are used for the monitoring of the RP-MOCVD process. The chemistry of the rf N{sub 2} plasma sapphire nitridation and its effect on the epilayer growth and quality are discussed in both MBE and RP-MOCVD. (orig.)

  5. Towards Isotropic Vortex Pinning in YBCO Films with Double-doping BHO-Y2O3 and BZO-Y2O3 Artificial Pining Centers

    Science.gov (United States)

    Gautam, Bibek; Sebastian, Mary Ann; Chen, Shihong; Haugan, Timothy; Chen, Yanbin; Xing, Zhongwen; Prestigiacomo, Joseph; Osofsky, Mike; Wu, Judy

    2017-12-01

    Strong and isotropic vortex pinning landscape is demanded for high field applications of YaBa2Cu3O7-x (YBCO) epitaxial thin films. Double-doping (DD) of artificial pinning centers (APCs) of mixed morphologies has been identified as a viable approach for this purpose. This work presents a comparative study on the transport critical current density J c (H, θ) of 3.0 vol.%Y2O3+2.0 (or 6.0) vol.% BaZrO3 (BZO DD) and 3.0 vol.%Y2O3+ 2.0 (or 6.0) vol.% BaHfO3 (BHO DD) films. Based on the elastic strain model, BaHfO3 (BHO) nanorods have lower rigidity than their BaZrO3 (BZO) counterparts, which means their c-axis alignment is more susceptible to the local strain generated by the secondary dopant of Y2O3. Considering the increasing strain field with higher BZO (or BHO doping), the higher susceptibility may result in a large portion of the BHO APCs moving away from perfect c-axis alignment and enhancing isotropic pinning with respect to the H orientation. This is confirmed since the BHO DD films illustrate a less pronounced J c peak at H//c-axis and hence more isotropic J c(θ) than their BZO DD counterparts. At 9.0 T, the variation of the J c across the entire θ range (0-90 degree) is less than 18% for the BHO DD film, in contrast to about 100% for the 2.0 vol.% BZO DD counterpart. At the higher BHO concentration of 6.0 vol.%, this higher tunability of the Y2O3 leads to increased ab-plane aligned BHO APCs and hence enhanced J c at H//ab-plane.

  6. Effect of substrate mis-orientation on GaN thin films grown by MOCVD under different carrier gas condition

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Seong-Woo; Suzuki, Toshimasa [Nippon Institute of Technology, 4-1 Gakuendai, Miyashiro, Saitama, 345-8501 (Japan); Aida, Hideo [NAMIKI Precision Jewel Co. Ltd., 3-8-22 Shinden, Adachi-ku, Tokyo, 123-8511 (Japan)

    2005-05-01

    We have studied the effect of a slight mis-orientation angle on surface and crystal quality of GaN thin films grown under different carrier gas conditions. Two types of carrier gas conditions were applied to the growth. One was pure H{sub 2} and the other was mixed N{sub 2}/H{sub 2}. As the result, we found dependence of surface and crystal quality of GaN thin films on the substrate mis-orientation angle, and they indicated almost the same tendency under both growth conditions. Therefore, it was confirmed that mis-orientation angle of sapphire substrate was one of the most critical factors for GaN thin films. Then, the effect of the additional N{sub 2} into the conventional H{sub 2} carrier gas was studied, and we found that the conversion of carrier gas from the conventional H{sub 2} to N{sub 2}/H{sub 2} mixture was effective against degradation of GaN crystallinity at any mis-orientation angle. Considering that the crystal quality of GaN thin films became insensitive to mis-orientation angle as the condition became more suitable for GaN growth, the optimal substrate mis-orientation angle was consequently decided to be approximately 0.15 from the morphological aspect. (copyright 2005 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  7. Plasma-assisted MOCVD growth of superconducting NbN thin films using Nb dialkylamide and Nb alkylimide precursors

    International Nuclear Information System (INIS)

    Liu Xiang; Ott, A.W.; Chang, R.P.H.; Babcok, J.R.; Belot, J.A.; Metz, M.V.; Marks, T.J.; Lane, M.A.; Kannewurf, C.R.

    2001-01-01

    The first example of the use of metal-organic precursors for depositing NbN superconducting thin films is described. The study, which employed niobium(IV) and niobium(V) pulsed source precursors and hydrazine plasma as the nitrogen source, indicates that T c is highly dependent on the lattice parameters and level of oxygen impurities, which are in turn governed by growth and post-deposition annealing temperatures. (orig.)

  8. YSZ thin films deposited on NiO-CSZ anodes by pulsed injection MOCVD for intermediate temperature-SOFC applications

    International Nuclear Information System (INIS)

    Garcia, G.; Pardo, J.A.; Santiso, J.; Merino, R.I.; Orera, V.M.; Larrea, A.; Pena, J.I.; Laguna-Bercero, M.A.; Figueras, A.

    2004-01-01

    Yttria-stabilized zirconia (YSZ) films are prepared on NiO-CaSZ by PIMOCVD (pulsed injection metal organic chemical vapor deposition). High quality, 5 to 10 μm thick, totally dense YSZ layers are prepared by controlling the oxygen partial pressure during the deposition. YSZ solid electrolyte deposition onto Ni-YSZ eutectic substrate is found to be a promising combination with regard to intermediate-temperature solid-oxide fuel cell applications. (Abstract Copyright [2004], Wiley Periodicals, Inc.)

  9. Preparation of Anatase TiO{sub 2} Thin Films with (O{sup i}Pr){sub 2}Ti(CH{sub 3}COCHCONEt{sub 2}){sub 2} Precursor by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Bae, Byoung Jae; Seo, Won Seok; Miah, Arzu; Park, Joon T. [Korea Advanced Institute of Science and Technology, Daejeon (Korea, Republic of); Lee, Kwang Yeol [Korea University, Seoul (Korea, Republic of); Kim, Keun Chong [Hong-Ik University, Chochiwon (Korea, Republic of)

    2004-11-15

    The reaction of titanium tetraisopropoxide with 2 equiv of N,N-diethyl acetoacetamide affords Ti(O{sup i}Pr){sub 2}(CH{sub 3}COCHCONEt{sub 2}){sub 2} (1) as colorless crystals in 80% yield. Compound 1 is characterized by spectroscopic (Mass and {sup 1}H/{sup 13}C NMR) and microanalytical data. Molecular structure of 1 has been determined by a single crystal X-ray diffraction study, which reveals that it is a monomeric, cis-diisopropoxide and contains a six coordinate Ti(IV) atom with a cis(CONEt{sub 2}), trans(COCH{sub 3}) configuration (1a) in a distorted octahedral environment. Variable-temperature {sup 1}H NMR spectra of 1 indicate that it exists as an equilibrium mixture of cis, trans (1a) and cis, cis (1b) isomers in a 0.57 : 0.43 ratio at -20 .deg. C in toluene-d{sub 8} solution. Thermal properties of 1 as a MOCVD precursor for titanium dioxide films have been evaluated by thermal gravimetric analysis and vapor pressure measurement. Thin films of pure anatase titanium dioxide (after annealing above 500 .deg. C under oxygen) have been grown on Si(100) with precursor 1 in the substrate temperature range of 350- 500 .deg. C using a bubbler-based MOCVD method.

  10. Transport AC losses in YBCO coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Majoros, M [Ohio State University, Columbus, OH 43210 (United States); Ye, L [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Velichko, A V [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Coombs, T A [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Sumption, M D [Ohio State University, Columbus, OH 43210 (United States); Collings, E W [Ohio State University, Columbus, OH 43210 (United States)

    2007-09-15

    Transport AC loss measurements have been made on YBCO-coated conductors prepared on two different substrate templates-RABiTS (rolling-assisted biaxially textured substrate) and IBAD (ion-beam-assisted deposition). RABiTS samples show higher losses compared with the theoretical values obtained from the critical state model, with constant critical current density, at currents lower than the critical current. An origin of this extra AC loss was demonstrated experimentally by comparison of the AC loss of two samples with different I-V curves. Despite a difference in I-V curves and in the critical currents, their measured losses, as well as the normalized losses, were practically the same. However, the functional dependence of the losses was affected by the ferromagnetic substrate. An influence of the presence of a ferromagnetic substrate on transport AC losses in YBCO film was calculated numerically by the finite element method. The presence of a ferromagnetic substrate increases transport AC losses in YBCO films depending on its relative magnetic permeability. The two loss contributions-transport AC loss in YBCO films and ferromagnetic loss in the substrate-cannot be considered as mutually independent.

  11. MOCVD waste gas treatment

    International Nuclear Information System (INIS)

    Geelen, A. van; Bink, P.H.M.; Giling, L.J.

    1993-01-01

    A large scale production of GaAs based solar cells with MOCVD will give rise to a considerable use of arsine. Therefore a gas treatment system is needed to convert the waste gases into less toxic compounds. In this study seven different gas treatment systems for MOCVD are compared by quantifying the environmental aspects. The systems are divided in wet systems, adsorption systems and thermal systems. The smallest amount of waste is produced by adsorption and thermal systems. Adsorption systems use the smallest amount of energy. The amount of primary materials used for the equipment varies per system. All systems are safe, but adsorption systems are simplest. At the moment, adsorption systems are probably the best choice from an environmental point of view. Nevertheless thermal systems have some potential advantages which make them interesting for the future

  12. Epitaxial Oxide Thin Films Grown by Solid Source Metal-Organic Chemical Vapor Deposition.

    Science.gov (United States)

    Lu, Zihong

    1995-01-01

    The conventional liquid source metal-organic chemical vapor deposition (MOCVD) technique is capable of producing large area, high quality, single crystal semiconductor films. However, the growth of complex oxide films by this method has been hampered by a lack of suitable source materials. While chemists have been actively searching for new source materials, the research work reported here has demonstrated the successful application of solid metal-organic sources (based on tetramethylheptanedionate) to the growth of high quality thin films of binary compound cerium dioxide (CeO_2), and two more complex materials, the ternary compound lithium niobate (LiNbO_3), with two cations, and the quaternary compound strontium barium niobate (SBN), with three cations. The growth of CeO_2 thin films on (1012)Al_2O_3 substrates has been used as a model to study the general growth behavior of oxides. Factors affecting deposition rate, surface morphology, out-of-plane mosaic structure, and film orientation have been carefully investigated. A kinetic model based on gas phase prereaction is proposed to account for the substrate temperature dependence of film orientation found in this system. Atomically smooth, single crystal quality cerium dioxide thin films have been obtained. Superconducting YBCO films sputtered on top of solid source MOCVD grown thin cerium dioxide buffer layers on sapphire have been shown to have physical properties as good as those of YBCO films grown on single crystal MgO substrates. The thin film growth of LiNbO_3 and Sr_{1-x}Ba _{x}Nb_2 O_6 (SBN) was more complex and challenging. Phase purity, transparency, in-plane orientation, and the ferroelectric polarity of LiNbO _3 films grown on sapphire substrates was investigated. The first optical quality, MOCVD grown LiNbO _3 films, having waveguiding losses of less than 2 dB/cm, were prepared. An important aspect of the SBN film growth studies involved finding a suitable single crystal substrate material. Mg

  13. YBCO coated conductors by reactive thermal co-evaporation

    Energy Technology Data Exchange (ETDEWEB)

    Schmatz, U.; Hoffmann, Ch.; Bauer, M.; Metzger, R.; Berberich, P.; Kinder, H. [Technische Univ. Muenchen, Garching (Germany). Physik-Department

    2001-12-01

    Coated tape conductors of YBCO require a deposition process allowing to obtain a high volume growth rate in order to produce long lengths of tape in a reasonable amount of time. We present our tape coating system where 15 parallel loops of travelling tape of 1 cm width can be coated simultaneously by reactive thermal co-evaporation. For high critical current densities, in-plane alignment of the YBCO film is necessary. Inclined substrate deposition (ISD) is a technique that allows to deposit in-plane oriented buffer layers suitable for YBCO growth at high deposition rates. We present results obtained for YBCO films grown on MgO-ISD buffer layers deposited by e-gun evaporation onto metallic tape substrates. (orig.)

  14. Detection of second harmonic of phase dependence of superconducting current in Nb/Au/YBCO heterojunctions

    CERN Document Server

    Komissinskij, F V; Ilichev, E V; Ivanov, Z G

    2001-01-01

    The results of the experimental study on the current phase dependence (CPD) of the heterotransitions, consisting of the niobium and the YBa sub 2 Cu sub 3 O sub x (YBCO) film with an additional interlayer from gold (Nb/Au/YBCO) are presented. The CPD measurement is carried out through the radiofrequency superconducting quantum interferometer. The CPD second harmonic is determined in the Nb/Au/YBCO heterotransitions. Possible causes of its appearance are discussed within the frames of the d +- s combined symmetry of the YBCO order parameter. One of the causes of the CPD second harmonic appearance is the twinning of the YBCO films (001). The second cause of existing the anomalously high critical current consists in the availability of the Nb/Au boundary with the transparence of approx 10 sup - sup 1 in the Nb/Au/YBCO

  15. Critical current behaviour of YBCO thin films described by vortex pinning on low-angle domain boundaries and vortex creep

    International Nuclear Information System (INIS)

    Golovchanskiy, I.A.; Pan, A.V.; Fedoseev, S.A.; Shcherbakova, O.V.; Dou, S.X.

    2012-01-01

    A pinning potential for vortices was introduced assuming plastic pinning of vortex lattice on chains of out-of-plane individual edge dislocations that form low-angle domain boundaries in high quality YBa 2 Cu 3 O 7 thin films. Using this pinning potential with the classical Kim-Anderson vortex creep approach a model for critical current dependence on field has been successfully developed. The model shows a plausible description of J c (B a ) over the entire field range. Electrical field criterion is incorporated providing the ability to compare measurements made with different criteria (including different measurement techniques). Applicability of this model has been verified by experimental data obtained by direct transport and magnetisation measurements on high quality films grown by pulsed laser deposition. Pinning potential obtained from the fitting procedure is consistent with theoretical predictions. The model showed that the effective pinning landscape changes under influence of external conditions.

  16. Critical Current Properties in Longitudinal Magnetic Field of YBCO Superconductor with APC

    Science.gov (United States)

    Kido, R.; Kiuchi, M.; Otabe, E. S.; Matsushita, T.; Jha, A. K.; Matsumoto, K.

    The critical current density (Jc) properties of the Artificial Pinning Center (APC) introduced YBa2Cu3O7 (YBCO) films in the longitudinal magnetic field were measured. Y2O3 or Y2BaCuO5 (Y211) was introduced as APCs to YBCO, and YBCO films with APC were fabricated on SrTiO3 single crystal substrate. The sizes of Y2O3 and Y211 were 5-10 nm and 10-20 nm, respectively. As a result, Jc enhancement in the longitudinal magnetic field was observed in Y2O3 introduced YBCO films. However, it was not observed in Y211 introduced YBCO films. Therefore, it was considered that Jc properties in the longitudinal magnetic field were affected by introducing of small size APC, and it was necessary that APC does not disturb the current pathway in the superconductor.

  17. Epitaxial growth of InP on SI by MOCVD

    International Nuclear Information System (INIS)

    Konushi, F.; Seki, A.; Kudo, J.; Sato, H.; Kakimoto, S.; Fukushima, T.; Kubota, Y.; Koba, M.

    1988-01-01

    The authors have studied the heteroepitaxial growth of InP on large diameter Si substrates using MOCVD. A new MOCVD system with four inch wafer size capability was utilized in the growth. Single domain InP films have been successfully grown on four inch Si substrates by using a new heterostructure with a thin GaAs intermediate layer. In this paper, the authors describe the crystalline quality and residual stress of InP epilayers, estimated by etch pit density and x-ray diffraction, respectively. The authors also reports on the reduction of EPD by post-growth annealing

  18. Reduced thermal budget processing of Y-Ba-Cu-O films by rapid isothermal processing assisted metalorganic chemical vapor deposition

    International Nuclear Information System (INIS)

    Singh, R.; Sinha, S.; Hsu, N.J.; Ng, J.T.C.; Chou, P.; Thakur, R.P.S.; Narayan, J.

    1991-01-01

    Metalorganic chemical vapor deposition (MOCVD) has the potential of emerging as a viable technique to fabricate ribbons, tapes, coated wires, and the deposition of films of high-temperature superconductors, and related materials. As a reduced thermal budget processing technique, rapid isothermal processing (RIP) based on incoherent radiation as the source of energy can be usefully coupled to conventional MOCVD. In this paper we report on the deposition and characterization of high quality superconducting thin films of Y-Ba-Cu-O (YBCO) on yttrium stabilized zirconia substrates by RIP assisted MOCVD. Using O 2 gas as the source of oxygen, YBCO films deposited initially at 600 degree C for 1 min and at 745 degree C for 25 min followed by deposition at 780 degree C for 45 s are primarily c-axis oriented and zero resistance is observed at 89--90 K. The zero magnetic field current density at 53 and 77 K are 1.2x10 6 and 3x10 5 A/cm 2 , respectively. By using a mixture of N 2 O and O 2 as the oxygen source substrate temperature was further reduced in the deposition of YBCO films. The films deposited initially at 600 degree C for 1 min and than at 720 degree C for 30 min are c-axis oriented and with zero resistance being observed at 91 K. The zero magnetic field current densities at 53 and 77 K are 3.4x10 6 and 1.2x10 6 A/cm 2 , respectively. To the best of our knowledge this is the highest value of critical current density, J c for films deposited by MOCVD at a substrate temperature as low as 720 degree C. It is envisioned that high energy photons from the incoherent light source and the use of a mixture of N 2 O and O 2 as the oxygen source, assist chemical reactions and lower overall thermal budget for processing of these films

  19. Reduced thermal budget processing of Y--Ba--Cu--O high temperature superconducting thin films by metalorganic chemical vapor deposition

    International Nuclear Information System (INIS)

    Singh, R.; Sinha, S.; Hsu, N.J.; Ng, J.T.C.; Chou, P.; Thakur, R.P.S.; Narayan, J.

    1991-01-01

    Metalorganic chemical vapor deposition (MOCVD) has the potential of emerging as a viable technique to fabricate ribbons, tapes, coated wires, and the deposition of films of high temperature superconductors, and related materials. As a reduced thermal budget processing technique, rapid isothermal processing (RIP) based on incoherent radiation as the source of energy can be usefully coupled to conventional MOCVD. In this paper we report on the deposition and characterization of high quality superconducting thin films of Y--Ba--Cu--O (YBCO) on MgO and SrTiO 3 substrates by RIP assisted MOCVD. By using a mixture of N 2 O and O 2 as the oxygen source films deposited initially at 600 degree C for 1 min and then at 740 degree C for 30 min are primarily c-axis oriented and with zero resistance being observed at 84 and 89 K for MgO and SrTiO 3 substrates, respectively. The zero magnetic field current densities at 77 K for MgO and SrTiO 3 substrates are 1.2x10 6 and 1.5x10 6 A/cm 2 , respectively. It is envisaged that high energy photons from the incoherent light source and the use of a mixture of N 2 O and O 2 as the oxygen source, assist chemical reactions and lower overall thermal budget for processing of these films

  20. New principle of feeding for flash evaporation MOCVD devices

    International Nuclear Information System (INIS)

    Kaul, A.R.; Seleznev, B.V.

    1993-01-01

    A novel scheme of flash evaporation feeding for MOCVD processes of multi-component oxide films deposition is proposed. The scheme comprises 1) microdozage of organic solution of solid volatile precursors on the glass fiber belt, 2) evaporation of the solvent and 3) flash evaporation of MOC microdoses from the belt. The functioning of the designed feeder is described and the features of proposed scheme in comparison to existing feeding principles are discussed. (orig.)

  1. YBCO/manganite layered structures on NdGaO{sub 3} substrates

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Blagoev, B [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Donchev, T [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Miteva, S [Institute of Electronics BAS, 72 Tsarigradsko Chaussee, 1784 Sofia (Bulgaria); Mozhaev, P B [Institute of Physics and Technology RAS, Nakhimovsky ave. 36, 117218 Moscow (Russian Federation); Mozhaeva, J E [Institute of Physics and Technology RAS, Nakhimovsky ave. 36, 117218 Moscow (Russian Federation); Ovsyannikov, G A [Institute of Radio Engineering and Electronics RAS, Mokhovaya st.11, 103907 Moscow (Russian Federation); Kotelyanskii, I M [Institute of Radio Engineering and Electronics RAS, Mokhovaya st.11, 103907 Moscow (Russian Federation); Jacobsen, C [Technical University of Denmark, Building 307-309, DK-2800, Kgs.Lyngby, Denmark (Denmark)

    2006-06-01

    Results of deposition of YBa{sub 2}Cu{sub 3}O{sub 7-x}/CeO{sub 2}/(La{sub 0.7}Ca{sub 0.3}MnO{sub 3} or La{sub 0.7}Sr{sub 0.3}MnO{sub 3}) structures on the standard oriented and tilted ( 8{sup 0}) NdGaO{sub 3} substrates and results of investigation of electrical parameters of YBa{sub 2}Cu{sub 3}O{sub 7-x} (YBCO) films in such structures are presented. The YBCO component of the structure exhibits lower value of the critical parameters in comparison with those of single YBCO films. The contribution of the magnetic layer to the microwave losses of the YBCO film in the layered structure is evaluated.

  2. YBCO/manganite layered structures on NdGaO3 substrates

    International Nuclear Information System (INIS)

    Nurgaliev, T; Blagoev, B; Donchev, T; Miteva, S; Mozhaev, P B; Mozhaeva, J E; Ovsyannikov, G A; Kotelyanskii, I M; Jacobsen, C

    2006-01-01

    Results of deposition of YBa 2 Cu 3 O 7-x /CeO 2 /(La 0.7 Ca 0.3 MnO 3 or La 0.7 Sr 0.3 MnO 3 ) structures on the standard oriented and tilted ( 8 0 ) NdGaO 3 substrates and results of investigation of electrical parameters of YBa 2 Cu 3 O 7-x (YBCO) films in such structures are presented. The YBCO component of the structure exhibits lower value of the critical parameters in comparison with those of single YBCO films. The contribution of the magnetic layer to the microwave losses of the YBCO film in the layered structure is evaluated

  3. Magnetorefractive effect in the La{sub 1−x}K{sub x}MnO{sub 3} thin films grown by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Sukhorukov, Yu.P., E-mail: suhorukov@imp.uran.ru [Institute of Metal Physics, Ural Division of RAS, 620990 Ekaterinburg (Russian Federation); Telegin, A.V. [Institute of Metal Physics, Ural Division of RAS, 620990 Ekaterinburg (Russian Federation); Bessonov, V.D. [Institute of Metal Physics, Ural Division of RAS, 620990 Ekaterinburg (Russian Federation); University of Bialystok, 15-424 Bialystok (Poland); Gan’shina, E.A.; Kaul’, A.R.; Korsakov, I.E.; Perov, N.S.; Fetisov, L.Yu. [Faculty of Physics, Moscow State University, Moscow 119991 (Russian Federation); Yurasov, A.N. [Moscow State Technical University of Radioengineering, Electronics and Automation, 119454 Moscow (Russian Federation)

    2014-10-01

    Thin epitaxial La{sub 1−x}K{sub x}MnO{sub 3} films were grown using two-stage procedure. Influence of substitution of La{sup 3+} ions with K{sup +} ions on the optical and electrical properties of La{sub 1−x}K{sub x}MnO{sub 3} films (x=0.05, 0.10, 0.15 i 0.18) has been studied in detail. A noticeable magnetorefractive effect in the films under study was detected in the infrared range. Magnetorefractive effect as well as transverse magneto-optical Kerr effect and magnetoresistance have the maximum in optimally doped sample with x=0.18 corresponding to the highest Curie temperature. The experimental data for compositions close to optimally doped films are in good agreement with the data calculated in the framework of a theory developed for manganites. The resonance-like contribution to magnetoreflection spectra of manganite films has been observed in the vicinity of the phonon bands. It is shown that magnetic and charge inhomogeneities strongly influence on the magneto-optical effects in films. Thin films of La{sub 1−x}K{sub x}MnO{sub 3} with the large values of Kerr and magnetorefractive effect are promising magneto-optical material in the infrared range. - Highlights: • Giant magnetorefractive effect was obtained in La{sub 1−x}K{sub x}MnO{sub 3} films in the infrared. • Inhomogeneity as well as doping level strongly influences the value of magnetorefractive effect. • Resonance-like bands have been observed in the magnetoreflection spectra of the films. • The obtained experimental data can be explained in the framework of the MRE theory.

  4. Study of the optical properties and structure of ZnSe/ZnO thin films grown by MOCVD with varying thicknesses

    Energy Technology Data Exchange (ETDEWEB)

    Jabri, S., E-mail: slaheddine.jabri@fst.rnu.tn [Unité des nanomatériaux et photoniques, Faculté des Sciences de Tunis, Campus Universitaire Ferhat Hachad, El Manar, 2092 Tunis (Tunisia); Amiri, G.; Sallet, V. [Groupe d’Etude de la Matière Condensée, CNRS-Université de Versailles St Quentin, Université Paris-Saclay, 45 avenue des Etats Unis, 78035 Versailles Cedex (France); Souissi, A. [Laboratoire de Photovoltaïque, Centre de Recherches et des Technologies de l’Energie, Technopole Borj Cedria, B.P. 95, Hammammlif 2050 (Tunisia); Meftah, A. [Unité des nanomatériaux et photoniques, Faculté des Sciences de Tunis, Campus Universitaire Ferhat Hachad, El Manar, 2092 Tunis (Tunisia); Galtier, P. [Groupe d’Etude de la Matière Condensée, CNRS-Université de Versailles St Quentin, Université Paris-Saclay, 45 avenue des Etats Unis, 78035 Versailles Cedex (France); Oueslati, M. [Unité des nanomatériaux et photoniques, Faculté des Sciences de Tunis, Campus Universitaire Ferhat Hachad, El Manar, 2092 Tunis (Tunisia)

    2016-05-15

    ZnSe layers were grown on ZnO substrates by the metal organic chemical vapor deposition technique. A new structure appeared at lower thicknesses films. The structural properties of the thin films were studied by the X-ray diffraction (XRD) and Raman spectroscopy methods. First, Raman selection rules are explicitly put forward from a theoretical viewpoint. Second, experimentally-retrieved-intensities of the Raman signal as a function of polarization angle of incident light are fitted to the obtained theoretical dependencies in order to confirm the crystallographic planes of zinc blend ZnSe thin film, and correlate with DRX measurements. Raman spectroscopy has been used to characterize the interfacial disorder that affects energy transport phenomena at ZnSe/ZnO interfaces and the Photoluminescence (PL) near the band edge of ZnSe thin films.

  5. Effect of annealing time and NH3 flow on GaN films deposited on amorphous SiO2 by MOCVD

    Science.gov (United States)

    Li, Tianbao; Liu, Chenyang; Zhang, Zhe; Yu, Bin; Dong, Hailiang; Jia, Wei; Jia, Zhigang; Yu, Chunyan; Xu, Bingshe

    2018-05-01

    GaN polycrystalline films were successfully grown on amorphous SiO2 by metal-organic chemical vapour deposition to fabricate transferable devices using inorganic films. Field-emission scanning electron microscopy images show that by prolonging the annealing time, re-evaporation is enhanced, which reduced the uniformity of the nucleation layer and GaN films. X-ray diffraction patterns indicate that the decomposition rate of the nucleation layer increases when the annealing flow rate of NH3 is 500 sccm, which makes the unstable plane and amorphous domains decompose rapidly, thereby improving the crystallinity of the GaN films. Photoluminescence spectra also indicate the presence of fewer defects when the annealing flow rate of NH3 is 500 sccm. The excellent crystal structure of the GaN films grown under optimized conditions was revealed by transmission electron microscopy analysis. More importantly, the crystal structure and orientation of GaN grown on SiO2 are the same as that of GaN grown on conventional sapphire substrate when a buffer layer is used. This work can aid in the development of transferable devices using GaN films.

  6. In-plane aligned YBCO tape on textured YSZ buffer layer deposited on stainless steel substrate by laser ablation only with O{sup +} ion beam assistance

    Energy Technology Data Exchange (ETDEWEB)

    Huang Xintang [Huazhong Univ. of Sci. and Technol., Wuhan (China). Nat. Lab. of Laser Technol.]|[Huazhong Normal Univ., Wuhan, HB (China). Dept. of Physics; Wang Youqing; Wang Qiuliang; Chen Qingming [Huazhong Univ. of Sci. and Technol., Wuhan (China). Nat. Lab. of Laser Technol.

    1999-08-16

    In this paper we have prepared YSZ buffer layers on stainless steel substrates by laser ablation only with O{sup +} ion beam assistance and YBCO films on YSZ/steel consequently. The relevant parameters of YSZ and YBCO film deposition are indicated. (orig.) 8 refs.

  7. In-plane aligned YBCO tape on textured YSZ buffer layer deposited on stainless steel substrate by laser ablation only with O+ ion beam assistance

    International Nuclear Information System (INIS)

    Huang Xintang; Huazhong Normal Univ., Wuhan, HB; Wang Youqing; Wang Qiuliang; Chen Qingming

    1999-01-01

    In this paper we have prepared YSZ buffer layers on stainless steel substrates by laser ablation only with O + ion beam assistance and YBCO films on YSZ/steel consequently. The relevant parameters of YSZ and YBCO film deposition are indicated. (orig.)

  8. Investigation on orientation, epitaxial growth and microstructure of a-axis-, c-axis-, (103)/(110)- and (113)-oriented YBa2Cu3O7-δ films prepared on (001), (110) and (111) SrTiO3 single crystal substrates by spray atomizing and coprecipitating laser chemical vapor deposition

    Science.gov (United States)

    Zhao, Pei; Wang, Ying; Huang, Zhi liang; Mao, Yangwu; Xu, Yuan Lai

    2015-04-01

    a-axis-, c-axis-, (103)/(110)- and (113)-oriented YBa2Cu3O7-δ (YBCO) films were pareared by spray atomizing and coprecipitating laser chemical vapor deposition. The surface of the a-axis-oriented YBCO film consisted of rectangular needle-like grains whose in-plane epitaxial growth relationship was YBCO [100] // STO [001] (YBCO [001] // STO [100]), and that of the c-axis-oriented YBCO film consisted of dense flat surface with epitaxial growth relationship of YBCO [001] // STO [001] (YBCO [100] //STO [100]). For the (103)/(110)-oriented and (113)-oriented YBCO film, they showed wedge-shaped and triangle-shaped grains, with corresponding in-plane epitaxial growth relationship of YBCO [110] // STO [110] (YBCO [010] // STO [010]) and YBCO [100] // STO [100] (YBCO [113] // STO [111], respectively.

  9. Development of YBCO Superconductor for Electric Systems: Cooperative Research and Development Final Report, CRADA Number CRD-04-150

    Energy Technology Data Exchange (ETDEWEB)

    Bhattacharya, R.

    2013-03-01

    The proposed project will be collaborative in exploration of high temperature superconductor oxide films between SuperPower, Inc. and the National Renewable Energy Laboratory. This CRADA will attempt to develop YBCO based high temperature oxide technology.

  10. PBCO/YBCO bilayer growth and optimization for the fabrication of buffered step-edge Josephson junctions

    CSIR Research Space (South Africa)

    Van Staden, WF

    2009-04-01

    Full Text Available Bilayers of PBCO and YBCO are grown epitaxially on MgO substrates using PLD. In this paper, researchers discuss the entire optimization process in detail, giving quantitative parameter values. Film characterization included XRD, AFM and susceptance...

  11. AC over-current characteristics of YBCO coated conductor with copper stabilizer layer considering insulation layer

    International Nuclear Information System (INIS)

    Du, H.-I.; Kim, M.-J.; Kim, Y.-J.; Lee, D.-H.; Han, B.-S.; Song, S.-S.

    2010-01-01

    Compared with the first-generation BSCCO wire, the YBCO thin-film wire boasts low material costs and high J c and superior magnetic-field properties, among other strengths. Meanwhile, the previous BSCCO wire material for superconducting cables has been researched on considerably with regard to its post-wire quenching characteristics during the application of an alternating over-current. In this regard, the promising YBCO thin-film wire has yet to be further researched on. Moreover, still lacking is research on the YBCO thin-film wire with insulating layers, which is essential in the manufacture of superconducting cables, along with the testing of the application of an alternating over-current to the wire. In this study, YBCO thin-film wires with copper-stabilizing layers were used in testing alternating over-current application according to the presence or absence of insulating layers and to the thickness of such layers, to examine the post-quenching wire resistance increase and quenching trends. The YBCO thin-film wire with copper-stabilizing layers has a critical temperature of 90 K and a critical current of 85 A rms . Moreover, its current application cycle is 5.5 cycles, and its applied currents are 354, 517, 712, and 915 A peak . These figures enabled the YBCO thin-film wires with copper-stabilizing layers to reach 90, 180, 250, and 300 K, respectively, in this study. These temperatures serve as a relative reference to examine the post-quenching wire properties following the application of an alternating over-current.

  12. Microstructure imaging of the YBCO thin film/MgO substrate interface: HRTEM and Fourier analysis of the Moire fringe pattern

    International Nuclear Information System (INIS)

    Auzary, S.; Pailloux, F.; Denanot, M.F.; Gaboriaud, R.J.

    1998-01-01

    Detailed microstructural aspects of the interface between YBaCuO thin films and MgO substrate are studied by means of a Fourier analysis of Moire fringe pattern obtained from HRTEM investigations of plan view samples. The main features of the observations are large, well oriented crystallographic domains surrounded by wide boundaries. HRTEM investigations together with the Fourier analysis show evidence of both orthorhombic and pseudo-tetragonal structure in the YBaCuO film. An accommodation mechanism is suggested from the Fourier analysis of the Moire fringe pattern. (orig.)

  13. Control of Flux Pinning in MOD YBCO Coated Conductor

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, W. [American Superconductor Corporation, Westborough, MA; Huang, Y. [American Superconductor Corporation, Westborough, MA; Li, X. [American Superconductor Corporation, Westborough, MA; Kodenkandath, Thomas [American Superconductor Corporation, Westborough, MA; Rupich, Marty [American Superconductor Corporation, Westborough, MA; Schoop, U. [American Superconductor Corporation, Westborough, MA; Verebelyi, D. T. [American Superconductor Corporation, Westborough, MA; Thieme, C. L. H. [American Superconductor Corporation, Westborough, MA; Siegal, E. E. [American Superconductor Corporation, Westborough, MA; Holesinger, T. G. [Los Alamos National Laboratory (LANL); Maiorov, B. [Los Alamos National Laboratory (LANL); Miller, D. J. [Argonne National Laboratory (ANL); Maroni, V. A. [Argonne National Laboratory (ANL); Goyal, Amit [ORNL; Specht, Eliot D [ORNL; Paranthaman, Mariappan Parans [ORNL

    2007-01-01

    Two different types of defect structures have been identified to be responsible for the enhanced pinning in metal organic deposited YBCO films. Rare earth additions result in the formation of nanodots in the YBCO matrix, which form uncorrelated pinning centers, increasing pinning in all magnetic field orientations. 124-type intergrowths, which form as laminar structures parallel to the ab-plane, are responsible for the large current enhancement when the magnetic field is oriented in the ab-plane. TEM studies showed that the intergrowths emanate from cuprous containing secondary phase particles, whose density is partially controlled by the rare earth doping level. Critical process parameters have been identified to control this phase formation, and therefore, control the f 24 intergrowth formation. This work has shown that through process control and proper conductor design, either by adjusting the composition or by multiple coatings of different functional layers, the desired angular dependence can be achieved.

  14. Control of flux pinning in MOD YBCO coated conductor.

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, W.; Huang, Y.; Li, X.; Kodenkandath, T.; Rupich, M. W.; Schoop, U.; Verebelyi, D. T.; Thieme, C. L. H.; Siegal, E.; Holesinger, T. G.; Maiorov, B.; Civale, L.; Miller, D. J.; Maroni, V. A.; Li, J.; Martin, P. M.; Specht, E. D.; Goyal, A.; Paranthaman, M. P.; American Superconductor Corp.; LANL; ORNL

    2007-06-01

    NTwo different types of defect structures have been identified to be responsible for the enhanced pinning in metal organic deposited YBCO films. Rare earth additions result in the formation of nanodots in the YBCO matrix, which form uncorrelated pinning centers, increasing pinning in all magnetic field orientations. 124-type intergrowths, which form as laminar structures parallel to the ab-plane, are responsible for the large current enhancement when the magnetic field is oriented in the ab-plane. TEM studies showed that the intergrowths emanate from cuprous containing secondary phase particles, whose density is partially controlled by the rare earth doping level. Critical process parameters have been identified to control this phase formation, and therefore, control the f 24 intergrowth formation. This work has shown that through process control and proper conductor design, either by adjusting the composition or by multiple coatings of different functional layers, the desired angular dependence can be achieved.

  15. Zone refining of sintered, microwave-derived YBCO superconductors

    International Nuclear Information System (INIS)

    Warrier, K.G.K.; Varma, H.K.; Mani, T.V.; Damodaran, A.D.; Balachandran, U.

    1993-07-01

    Post-sintering treatments such as zone melting under thermal gradient has been conducted on sintered YBCO tape cast films. YBCO precursor powder was derived through decomposition of a mixture of nitrates of cations in a microwave oven for ∼4 min. The resulting powder was characterized and made into thin sheets by tape casting and then sintered at 945 C for 5 h. The sintered tapes were subjected to repeated zone refining operations at relatively high speeds of ∼30 mm/h. A microstructure having uniformly oriented grains in the a-b plane throughout the bulk of the sample was obtained by three repeated zone refining operations. Details of precursor preparation, microwave processing and its advantages, zone refining conditions, and microstructural features are presented in this paper

  16. Measurements and removal of substrate effects on the microwave surface impedance of YBCO films on SrTiO{sub 3}

    Energy Technology Data Exchange (ETDEWEB)

    Pompeo, N [Dipartimento di Fisica ' E Amaldi' and Unita CNISM, Universita Roma Tre, Via dellaVasca Navale 84, 00146 Rome (Italy); Muzzi, L [Dipartimento di Fisica ' E Amaldi' and Unita CNISM, Universita Roma Tre, Via dellaVasca Navale 84, 00146 Rome (Italy); Galluzzi, V [ENEA-Frascati, Via Enrico Fermi 45, 00044 Frascati, Rome (Italy); Marcon, R [Dipartimento di Fisica ' E Amaldi' and Unita CNISM, Universita Roma Tre, Via dellaVasca Navale 84, 00146 Rome (Italy); Silva, E [Dipartimento di Fisica ' E Amaldi' and Unita CNISM, Universita Roma Tre, Via dellaVasca Navale 84, 00146 Rome (Italy)

    2007-10-15

    We reconsider the problem of the measurements of the microwave complex surface impedance in thin superconducting films deposited on SrTiO{sub 3} substrates. We perform measurements of the complex surface impedance Z{sub s}' = R{sub s}'+i{delta}X{sub s}' of thin YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} films deposited by laser ablation on SrTiO{sub 3} substrates. The typical oscillations due to the strong temperature variation of the SrTiO{sub 3} permittivity are confirmed in R{sub s}' and observed in {delta}X{sub s}'. The effects of the SrTiO{sub 3} substrate are evident even well below the superconducting transition temperature of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}}. Similarly to previous works, we describe the overall response in terms of impedance transformations. We extend the known results by (i) considering the measurements of the imaginary part (ii) comparing the measurements to the absolute dc resistivity measured on the same sample, and (iii) suggesting a method for measuring the intrinsic thin film surface impedance by adjusting the substrate impedance. To demonstrate the feasibility of microwave measurements of intrinsic properties of films grown onto SrTiO{sub 3} substrates, we check the proposed method by measuring the field dependent surface impedance before and after removal of the substrate resonance.

  17. Characterization of long-length, MOCVD-derived REBCO coated conductors.

    Energy Technology Data Exchange (ETDEWEB)

    Miller, D. J.; Maroni, V. A.; Hiller, J. M.; Koritala, R. E.; Chen, Y.; Reeves Black, J. L.; Selvamanickam, V.; SuperPower, Inc.; Development Dimensions International, Inc.

    2009-06-01

    A leading approach to the fabrication of long-length, high-performance REBa{sub 2}Cu{sub 3}O{sub 7} (REBCO) coated conductor is by metal-organic chemical vapor deposition (MOCVD) of REBCO on buffered templates. Templates are produced by ion beam assisted deposition of textured MgO onto polished metal substrates. The overall performance of MOCVD coated conductors achieved to date is impressive, but further improvement is desired. We have used a coordinated set of characterization techniques to identify the underlying causes for critical current (Ic) performance variations in long-length MOCVD conductors. Using electron microscopy and Raman spectroscopy, we studied tape specimens from specially designed experiments performed in SuperPower's MOCVD manufacturing equipment with its six-track ldquohelixrdquo tape path. We find that in multi-pass depositions used to produce thicker REBCO films, the REBCO phase uniformity and texture quality in the first pass play key roles in pass-to-pass microstructure evolution, with nucleation of second phase particles in the first layer promoting misoriented grains that propagate through subsequent layers. These misoriented grains, many growing in close proximity with second phase particles, present current-blocking obstacles that limit Ic performance. Our results show that achieving more uniform deposition in the very first deposited layer plays a critical role that in turn leads to reduced misoriented grain content and REBCO lattice disorder in the second and subsequent layers of the REBCO film.

  18. Fast growth rate of epitaxial β-Ga2O3 by close coupled showerhead MOCVD

    Science.gov (United States)

    Alema, Fikadu; Hertog, Brian; Osinsky, Andrei; Mukhopadhyay, Partha; Toporkov, Mykyta; Schoenfeld, Winston V.

    2017-10-01

    We report on the growth of epitaxial β-Ga2O3 thin films on c-plane sapphire substrates using a close coupled showerhead MOCVD reactor. Ga(DPM)3 (DPM = dipivaloylmethanate), triethylgallium (TEGa) and trimethylgallium (TMGa) metal organic (MO) precursors were used as Ga sources and molecular oxygen was used for oxidation. Films grown from each of the Ga sources had high growth rates, with up to 10 μm/hr achieved using a TMGa precursor at a substrate temperature of 900 °C. As confirmed by X-ray diffraction, the films grown from each of the Ga sources were the monoclinic (2 bar 0 1) oriented β-Ga2O3 phase. The optical bandgap of the films was also estimated to be ∼4.9 eV. The fast growth rate of β-Ga2O3 thin films obtained using various Ga-precursors has been achieved due to the close couple showerhead design of the MOCVD reactor as well as the separate injection of oxygen and MO precursors, preventing the premature oxidation of the MO sources. These results suggest a pathway to overcoming the long-standing challenge of realizing fast growth rates for Ga2O3 using the MOCVD method.

  19. AFM studies on heavy ion irradiated YBCO single crystals

    International Nuclear Information System (INIS)

    Lakhani, Archana; Marhas, M.K.; Saravanan, P.; Ganesan, V.; Srinivasan, R.; Kanjilal, D.; Mehta, G.K.; Elizabeth, Suja; Bhat, H.L.

    2000-01-01

    Atomic Force Microscopy (AFM) is extensively used to characterise the surface morphology of high energy ion irradiated single crystals of high temperature superconductor - YBCO. Our earlier systematic studies on thin films of YBCO under high energy and heavy ion irradiation shows clear evidence of ion induced sputtering or erosion, even though the effect is more on the grain boundaries. These earlier results were supported by electrical resistance measurements. In order to understand more clearly, the nature of surface modification at these high energies, AFM studies were carried out on single crystals of YBCO. Single crystals were chosen in order to see the effect on crystallites alone without interference from grain boundaries. 200 MeV gold ions were used for investigation using the facilities available at Nuclear Science Centre, New Delhi. The type of ion and the range of energies were chosen to meet the threshold for electronically mediated defect production. The results are in conformity with our earlier studies and will be described in detail in the context of electronic energy loss mediated sputtering or erosion. (author)

  20. MOCVD of zirconium oxide from the zirconium guanidinate complex |ZrCp′{2-(iPrN)2CNMe2}2Cl

    NARCIS (Netherlands)

    Blackman, C.S.; Carmalt, C.J.; Moniz, S.J.A.; Potts, S.E.; Davies, H.O.; Pugh, D.C.

    2009-01-01

    Parallel to successful studies into use of [ZrCp'{¿ 2-(iPrN)2CNMe2} 2Cl] as a precursor to the deposition of zirconium carbonitride via CVD the same precursor was utilised for the MOCVD of thin films of ZrO 2 using borosilicate glass substrates. The deposited films were of mixed phase; films

  1. Critical current in nonhomogeneous YBCO coated conductors

    International Nuclear Information System (INIS)

    Rostila, L; Mikkonen, R; Lehtonen, J

    2008-01-01

    The critical current of an YBCO tape is determined by the magnetic field inside the YBCO layer and the quality of YBCO material. In thick YBCO layers the average critical current density is reduced by the self-field and decreased material quality. In this paper the combined influence of the material nonhomogeneities and self-field on the critical current of YBCO tapes is scrutinised. First, the zero field critical current density was assumed to decrease along the YBCO thickness. Secondly, the possible defects created in the cutting of YBCO tapes were modelled as a function of lowered critical current density near the tape edges. In both cases the critical current was computed numerically with integral element method. The results suggest that the variation of zero field critical current density, J c0 , along the tape thickness does not effect on the critical current if the mean value of J c0 is kept constant. However, if J c0 is varied along the tape width the critical current can change due to the variated self-field. The computations can be used to determine when it is possible to evaluate the average zero field critical current density from a voltage-current measurement with an appropriate accuracy

  2. High trapped fields in bulk YBCO superconductors

    Science.gov (United States)

    Fuchs, Günter; Gruss, Stefan; Krabbes, Gernot; Schätzle, Peter; Verges, Peter; Müller, Karl-Hartmut; Fink, Jörg; Schultz, Ludwig

    The trapped field properties of bulk melt-textured YBCO material were investigated at different temperatures. In the temperature range of liquid nitrogen, maximum trapped fields of 1.1 T were found at 77 K by doping of YBCO with small amounts of zinc. The improved pinning of zinc-doped YBa2Cu3O7-x (YBCO) results in a pronounced peak effect in the field dependence of the critical current density. the trapped field at lower temperatures increases due to the increasing critical current density, however, at temperatures around 50 K cracking of the material is observed which is exposed to considerably tensile stresses due to Lorentz forces. Very high trapped fields up to 14.4 T were achieved at 22.5 K for a YBCO disk pair by the addition of silver improving the tensile strength of YBCO and by using a bandage made of a steel tube. The steel tube produces a compressive stress on YBCO after cooling down from 300 K to the measuring temperature, which is due to the higher coeeficient of thermal expansion of steel compared with that of YBCO in the a,b plane. The application of superconducting permanent magnets with trapped fields of 10 T and more in superconducting bearings would allow to obtain very high levitation pressures up to 2500 N/cm2 which is two orders of magnitude higher than the levitation pressure achievable in superconducting bearings with conventional permanent magnets. The most important problem for the application of superconducting permanent magnets is the magnetizing procedure of the YBCO material. Results of magnetizing YBCO disks by using of pulsed magnetic fields will be presented.

  3. Study of electrical properties of single GaN nanowires grown by MOCVD with a Ti mask

    International Nuclear Information System (INIS)

    Vasiliev, A A; Mozharov, A M; Mukhin, I S; Rozhavskaya, M M; Lundin, V V

    2016-01-01

    We researched electrical characteristics of GaN nanowires (NWs) grown by MOCVD through solid titanium film. The technology of creating the ohmic contacts and MESFET structure on single NWs has been developed. The optimal annealing temperature of contacts has been found and conductivity structure, the free carrier concentration and mobility has been evaluated. (paper)

  4. Investigation of DC current injection effect on the microwave characteristics of HTS YBCO microstrip resonators

    Energy Technology Data Exchange (ETDEWEB)

    Nurgaliev, T., E-mail: timur@ie.bas.bg [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Blagoev, B.; Mateev, E.; Neshkov, L. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Strbik, V. [Institute of Electrical Engineering, Slovak Academy of Sciences, Dúbravská cesta 9, 841 04 Bratislava (Slovakia); Uspenskaya, L. [Institute of Solid State Physics, Russian Academy of Sciences, 142432 Chernogolovka, Moscow (Russian Federation); Nedkov, I. [Institute of Electronics, Bulgarian Academy of Sciences, 72 Tsarigradsko Chausse, 1784 Sofia (Bulgaria); Chromik, Š. [Institute of Electrical Engineering, Slovak Academy of Sciences, Dúbravská cesta 9, 841 04 Bratislava (Slovakia)

    2014-03-15

    Highlights: • Current (spin) injection effect in LSMO/YBCO was studied by impedance measurements. • Complex impedance of YBCO increases at current injection from LSMO to YBCO at 77 K. • This increase is due to an increase of the quasiparticle conductivity of YBCO. • Injection does not significantly affect the relaxation time of the quasiparticles. - Abstract: The DC current injection effect from a ferromagnetic (FM) La{sub 0.7}Sr{sub 0.3}MnO{sub 3} (LSMO) to a high temperature superconducting (HTS) Y{sub 1}Ba{sub 2}Cu{sub 3}O{sub 7−x} (YBCO) thin film was investigated by the microwave surface impedance measurements in a FM/HTS structure, formed as a microstrip resonator for improving the sensitivity of the experiments. The quality factor and the resonance frequency of this structure were found to strongly depend on the current strength, injected from the LSMO electrode into the HTS microstrip electrode. The magnetic penetration depth and the quasiparticle conductivity of the HTS component were determined to increase under DC current injection process, which in all probability stimulated breaking of Cooper pairs and led to a decrease of the superfluid concentration and an increase of the normal fluid concentration without significantly affecting the relaxation time of the quasiparticles.

  5. Pinning Mechanisms in YBCO Tapes

    CERN Document Server

    Spera, Marcello; Ballarino, Amalia

    2015-01-01

    In this thesis work, a study on flux pinning mechanisms of commercial YBCO tapes is presented. This study has been performed via critical current characterization using transport (via direct I-V curves) and magnetization (via a Vibrating Sample Magnetometer) measurements. The latter ones turned out to be better concerning the comprehension of the pinning landscape of the provided samples, as a wider range of magnetic fields and temperatures is available for those measurements in the setup I used. The comparison of the experimental data with existing theoretical models allowed me to draw a picture of the pinning mechanisms underlying in each sample, and they turned out to be quite different one another. Moreover, for high-performance research tapes, another interesting feature has been found: the counterplay between the self-field critical current and the in-field one. Very well engineered artificial pinning structures limit the self-field critical current density due to the hi...

  6. Development of YBCO tape conductor fabrication technology

    Energy Technology Data Exchange (ETDEWEB)

    Hong, G W; Kim, C J; Lee, H G. and others

    2001-08-01

    Superconductor when fabricated into wire shape is applied for developing electric power transmission cable, transformer, generator and SMES. Such superconducting power devices are capable of maximizing the efficiency of electricity and are anticipated to contribute for solving the energy problem of humankind. Furthermore the high temperature oxide superconductor developed in late 1980s is superconducting above boiling temperature of liquid nitrogen temperature has strong potential to realize superconducting power device and a lot of researches are being done in this field. Superconducting wire is the most important core material for developing superconducting power device and thermo-mechanical powder in tube process was developed to fabricated Ag/Bi-2223 conductor in long length having high critical current carrying capacity. Several companies fabricate and sell Ag/Bi-2223 superconducting wire longer than km length and used for developed electrical power device. But because of its inherent property of sharp decrease in current carrying capacity when applying high magnetic field, the application of Bi-2223 sire is limited as low as 20 K when the power device is in operating under high magnetic field. The YBCO tape conductor has the advantages of maintaining high critical current applying high magnetic field and can be used to most of the power device without special limitation. The metal substrate having good crystallographic texture and deposition technique which can deposit the good quality superconducting thin film continuously in large area are need to fabricate coated conductor, and this technique can be applied to develop the superconducting current limiter or magnetic field shielding device. A superconducting wire for using in high magnetic field is play a critical role in developing maglev, MRI, SMES, transformer, generator and motor and the continuous film deposition technique can be applied in other industry very much.

  7. Passivation of Flexible YBCO Superconducting Current Lead With Amorphous SiO2 Layer

    Science.gov (United States)

    Johannes, Daniel; Webber, Robert

    2013-01-01

    across a thermal gradient with as little flow of heat as possible to make an efficient current lead. By protecting YBCO on a flexible substrate of low thermal conductivity with SiO2, a thermally efficient and flexible current lead can be fabricated. The technology is also applicable to current leads for 4 K superconducting electronics current biasing. A commercially available thin-film YBCO composite tape conductor is first stripped of its protective silver coating. It is then mounted on a jig that holds the sample flat and acts as a heat sink. Silicon dioxide is then deposited onto the YBCO to a thickness of about 1 micron using PECVD (plasma-enhanced chemical vapor deposition), without heating the YBCO to the point where degradation occurs. Since SiO2 can have good high-frequency electrical properties, it can be used to coat YBCO cable structures used to feed RF signals across temperature gradients. The prime embodiment concerns the conduction of DC current across the cryogenic temperature gradient. The coating is hard and electrically insulating, but flexible.

  8. GaN epitaxial layers grown on multilayer graphene by MOCVD

    Science.gov (United States)

    Li, Tianbao; Liu, Chenyang; Zhang, Zhe; Yu, Bin; Dong, Hailiang; Jia, Wei; Jia, Zhigang; Yu, Chunyan; Gan, Lin; Xu, Bingshe

    2018-04-01

    In this study, GaN epitaxial layers were successfully deposited on a multilayer graphene (MLG) by using metal-organic chemical vapor deposition (MOCVD). Highly crystalline orientations of the GaN films were confirmed through electron backscatter diffraction (EBSD). An epitaxial relationship between GaN films and MLG is unambiguously established by transmission electron microscope (TEM) analysis. The Raman spectra was used to analyze the internal stress of GaN films, and the spectrum shows residual tensile stress in the GaN films. Moreover, the results of the TEM analysis and Raman spectra indicate that the high quality of the MLG substrate is maintained even after the growth of the GaN film. This high-quality MLG makes it possible to easily remove epitaxial layers from the supporting substrate by micro-mechanical exfoliation technology. This work can aid in the development of transferable devices using GaN films.

  9. Development and construction of a novel MOCVD facility for the growth of ferroelectric thin layers

    International Nuclear Information System (INIS)

    Schaefer, P.R.

    2002-02-01

    This thesis deals with the production of ferroelectric thin films using the MOCVD technology. The main focus is put on the design and construction of a complete MOCVD research system that is equipped with a novel non-contact vaporizer system. The precursors are nebulized in an ultrasonic atomizer and injected into a hot gas stream, so they can vaporize without getting into contact with a hot surface. Hence, one of the biggest disadvantages of conventional vaporizer concepts, the contamination of the vaporizing element with decomposing chemicals, could be avoided completely, resulting in a nearly maintenance-free system. In a direct comparison with the well-established Direct Liquid Injection Subsystem DLI-25C from MKS Instruments, the advantages of non-contact evaporation were clearly demonstrated. Additionally, the scope of this work included the development of standard deposition processes for the ternary oxides SrTiO 3 , BaTiO 3 und PbTiO 3 and growth studies were performed. Electrical measurements performed on MIM structures with Pt electrodes and SrTiO 3 as dielectric indicate a high film quality comparable with results presented in the literature. Furthermore, for the first time the solid solution (Pb x Ba 1-x )TiO 3 has been deposited by MOCVD. This material system is widely unknown in thin film form and it is well suited as a model system to investigate the influence of mechanical stresses on the film properties, because it represents a transition between the (as a thin film) superparaelectric barium titanate and the ferroelectric lead titanate. Through variation of the lead/barium ratio the tetragonal distortion of the lattice cell could be adjusted in a wide range. (orig.)

  10. Detection of smaller Jc region and damage in YBCO coated conductors by using permanent magnet method

    International Nuclear Information System (INIS)

    Hattori, K.; Saito, A.; Takano, Y.; Suzuki, T.; Yamada, H.; Takayama, T.; Kamitani, A.; Ohshima, S.

    2011-01-01

    We developed a non-destructive method for measuring the critical current density (J c ) in YBCO-coated conductors by using a permanent magnet (Sm 2 Co 17 ). J c could be determined from the repulsive force (F r ) generated between a permanent magnet and a coated conductor where shielding current flows. We also examined the influence of damage to the film on the J c distribution. The measured F r when the permanent magnet approached the cut part was smaller than that of the undamaged area. We developed a non-destructive method for measuring the critical current density (J c ) in YBCO-coated conductors by using a permanent magnet (Sm 2 Co 17 ). J c could be determined from the repulsive force (F r ) generated between a permanent magnet and a coated conductor where shielding current flows. We tried to detect a smaller J c region in the coated conductor by using the system. The J c distribution could be determined without influence from the thick copper film on YBCO thin film. We also examined the influence of damage to the film on the J c distribution. The surface of the coated conductors was cut by using a knife. The measured F r when the permanent magnet approached the cut part was smaller than that of the undamaged area. This J c measurement technique will be useful for detecting smaller J c regions and defects in coated conductors.

  11. Flux pinning characteristics of YBCO coated conductor

    International Nuclear Information System (INIS)

    Matsushita, T.; Watanabe, T.; Fukumoto, Y.; Yamauchi, K.; Kiuchi, M.; Otabe, E.S.; Kiss, T.; Watanabe, T.; Miyata, S.; Ibi, A.; Muroga, T.; Yamada, Y.; Shiohara, Y.

    2005-01-01

    Flux pinning properties of PLD-processed YBCO coated conductors deposited on IBAD substrate are investigated. The thickness of YBCO layer is changed in the range of 0.27-1.0 μm. The thickness dependence of critical current density, n-value and irreversibility field are measured in a wide range of magnetic field. The results are compared with the theoretical flux creep-flow model. It is found that these pinning properties are strongly influenced by the thickness as well as the pinning strength. Optimum condition for high field application of this superconductor is discussed

  12. Theoretical analysis of a YBCO squirrel-cage type induction motor based on an equivalent circuit

    International Nuclear Information System (INIS)

    Morita, G; Nakamura, T; Muta, I

    2006-01-01

    A HTS induction motor, with a HTS squirrel-cage rotor, is analysed using an electrical equivalent circuit. The squirrel-cage winding in the rotor consists of rotor bars and end rings, and both are considered to be made of YBCO film conductors. A wide range of electric field versus current density in YBCO film is formulated based on the Weibull function, and analysed as a non-linear resistance in the equivalent circuit. It is shown that starting and accelerating torques of the HTS induction motor are improved drastically compared to those of a conventional induction motor. Furthermore, large synchronous torque can also be realized by trapping the magnetic flux in the rotor circuit because of the persistent current mode

  13. Dependences of microstructure and critical current density on the thickness of YBa2Cu3O7-x film prepared by pulsed laser deposition on buffered Ni–W tape

    International Nuclear Information System (INIS)

    Xu, Da; Wang, Ying; Liu, Linfei; Li, Yijie

    2013-01-01

    YBa 2 Cu 3 O 7−x (YBCO) films with different thicknesses were fabricated on buffered Ni–W tapes by pulsed laser deposition. The thickness dependences of microstructure and critical current density (J c ) of YBCO film were systematically investigated. The microstructure and surface morphology of YBCO film were characterized by X-ray diffraction, optical microscopy, field emission scanning electron microscopy and atomic force microscopy. And the critical current (I c ) of YBCO film was measured by the conventional four-probe method. We found that the full width at half maximum values of both omega and phi scan rocking curves, the content of a-axis oriented grain, and surface roughness of YBCO film all increased with augmenting the thickness of YBCO film. It was also found that with increasing the thickness of YBCO film from 0.3 μm to 1.5 μm, the I c of YBCO film increased from 72 A/cm to 248 A/cm and yet J c of YBCO film decreased from 2.1 × 10 6 A/cm 2 to 1.6 × 10 6 A/cm 2 . Our results indicated that the microstructure and J c of YBCO film were largely dependent on the thickness of YBCO film under the optimized deposition condition of substrate temperature. - Highlights: ► YBa 2 Cu 3 O 7−x (YBCO) films with different thicknesses were grown on metallic tapes. ► The texture and critical current were dependent on the thickness of YBCO film. ► Thickness effect was weakened by fabricating YBCO film layer by layer

  14. Jc enhancement by La-Al-O doping in Y-Ba-Cu-O films both in self-field and under magnetic field

    DEFF Research Database (Denmark)

    Xu, Yan; Suo, Hong-Li; Yue, Zhao

    2016-01-01

    a good epitaxial growth relationship with LAO. Compared with a pure YBCO film, the Jc value of a 5.0% LAO-doped sample is enhanced more than three times in self-field 77 K and seven times at 77 K and 1.5 T, respectively. These results indicate that LAO doping can effectively enhance the Jc of YBCO films...... toward YBCO. A series of YBCO films with different LAO doping contents was fabricated on LAO single-crystal substrates by metal organic deposition. We observed by X-ray diffractometer measurements and scanning electron microscopy observations that although a large amount of LAO is added, YBCO still keeps...

  15. Point defects in MnSi and YBCO studied by Doppler Broadening Spectroscopy using a positron beam

    Energy Technology Data Exchange (ETDEWEB)

    Reiner, Markus

    2015-10-28

    The positron beam NEPOMUC was used in order to investigate MnSi and YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) single crystals. The Doppler broadening of the annihilation radiation of electron-positron pairs was analyzed. Thus, the concentration of Mn vacancies in MnSi crystals was determined. In thin YBCO films, the Doppler broadening is correlated with the oxygen deficiency δ. Its spatial distribution and its high-temperature behavior were studied using positrons.

  16. AFM plough YBCO micro bridges: substrate effects

    CSIR Research Space (South Africa)

    Elkaseh, A

    2009-04-01

    Full Text Available AFM nanolithography was used as a novel cutting technique to define micro-size YBCO superconducting constrictions. Researchers studied the substrate effects on MgO and STO substrates and showed that the observed Shapiro steps from the bridges on STO...

  17. Measurement of noise in YBCO bi-crystal junctions

    International Nuclear Information System (INIS)

    Kuznik, J.; Hao, L.; Macfarlane, J.C.; Pegrum, C.M.; Fischer, G.M.; Mygind, J.; Pedersen, N.F.; Beck, A.; Gross, R.

    1993-01-01

    This paper describes collaborative work between three institutions as part of an ESPRIT programme to fabricate and characterise grain-boundary junctions. Bi-crystal junctions were fabricated at Tuebingen on SrTiO 3 substrates with a 24 misorientation angle and a-b tilt. 200nm of c-axis YBCO was sputter-deposited using a hollow-cathode magnetron, and the films patterned with optical lithography and Ar ion beam etching (3). For test purposes junctions with a range of sizes were made, with widths between 4 and 20μm. These have been characterised for noise properties at 0.3 - 1kHz and 60kHz at Strathclyde, and at 70GHz at Lyngby. (orig.)

  18. Introduction of Artificial Pinning Center into PLD-YBCO Coated Conductor on IBAD and Self-Epitaxial CeO2 Buffered Metal Substrate

    International Nuclear Information System (INIS)

    Kobayashi, H.; Yamada, Y.; Ishida, S.; Takahashi, K.; Konishi, M.; Ibi, A.; Miyata, S.; Kato, T.; Hirayama, T.; Shiohara, Y.

    2006-01-01

    In order to fabricate YBa2Cu3O7-x (YBCO) coated conductors with high critical current density Jc in magnetic fields, we fabricated YBCO coated conductors with artificial pinning centers by the pulsed laser deposition (PLD) method on a self epitaxial PLD-CeO2 layer and ion-beam assisted deposition (IBAD)-Gd2Zr2O7 (GZO) buffered Hastelloy tape. Artificial pinning centers were introduced by the PLD deposition using the yttria-stabilized zirconia (YSZ) oxide target (nano-dot method) and YBCO target including YSZ particles (mixed target method). In the experiments using YSZ oxide target, YSZ nano-dots were observed. They were approximately 15 nm in height and 10 nm to 70 nm in diameter. We found that the density of nano-dots was controlled by the number of laser pulses. These samples exhibited higher Jc than YBCO films in magnetic fields. Furthermore, a similar improvement of Jc was observed in the experiments using YBCO target including YSZ particles. TEM observation revealed that columnar nano-structure made of BaZrO3 was formed during YBCO deposition and it was effective for pinning. We call this new epitaxial nano-structure 'bamboo structure' from its anisotropic growth and morphology

  19. Positron annihilation studies in Hf doped YBCO

    International Nuclear Information System (INIS)

    Gopalan, P.; Priya, E.R.; Premila, M.; Sundar, C.S.; Gopinathan, K.P.

    1992-01-01

    The variation of positron lifetime and oxygen stoichiometry as a function of quench temperature has been measured in undoped and 0.5at%, 0.75at%, and 1.0 at% Hf doped YBCO. In both the undoped and Hf doped samples, the lifetime decreases and the oxygen content increases as the quench temperature is lowered from 900degC to 300degC. The lifetime in the tetragonal phase (900degC) decreases with the increase in Hf content, whereas in the orthorhombic phase (450degC) it increases. The difference in lifetime between the tetragonal and orthorhombic phases decreases with the increase in the Hf content. These trends are discussed in terms of the influence of Hf doping on the oxygen content and the positron density distribution in YBCO

  20. Rapid processing method for solution deposited YBa2Cu3O7-δ thin films

    International Nuclear Information System (INIS)

    Dawley, J.T.; Clem, P.G.; Boyle, T.J.; Ottley, L.M.; Overmyer, D.L.; Siegal, M.P.

    2004-01-01

    YBa 2 Cu 3 O 7-δ (YBCO) films, deposited on buffered metal substrates, are the primary candidate for second-generation superconducting (SC) wires, with applications including expanded power grid transmission capability, compact motors, and enhanced sensitivity magnetic resonance imaging. Feasibility of manufacturing such superconducting wires is dependent on high processing speed, often a limitation of vapor and solution-based YBCO deposition processes. In this work, YBCO films were fabricated via a new diethanolamine-modified trifluoroacetic film solution deposition method. Modifying the copper chemistry of the YBCO precursor solution with diethanolamine enables a hundredfold decrease in the organic pyrolysis time required for MA/cm 2 current density (J c ) YBCO films, from multiple hours to ∼20 s in atmospheric pressure air. High quality, ∼0.2 μm thick YBCO films with J c (77 K) values ≥2 MA/cm 2 at 77 K are routinely crystallized from these rapidly pyrolyzed films deposited on LaAlO 3 . This process has also enabled J c (77 K)=1.1 MA/cm 2 YBCO films via 90 m/h dip-coating on Oak Ridge National Laboratory RABiTS textured metal tape substrates. This new YBCO solution deposition method suggests a route toward inexpensive and commercializable ∼$10/kA m solution deposited YBCO coated conductor wires

  1. A study for designing YBCO power transformer

    International Nuclear Information System (INIS)

    Hayashi, H.; Okamoto, H.; Harimoto, T.; Imayoshi, T.; Tomioka, A.; Bouno, T.; Konno, M.; Iwakuma, M.

    2007-01-01

    It is highly expected that superconducting transformers, which are characterized by incombustibility, light weight, and compactness, will be used practically for equipment in substations and office buildings sited in urban areas. In recent years, remarkable improvements in the performance of YBaCuO (YBCO) tape wire have been seen. This kind of tape wire has the property that its critical current is large in a highly magnetic field; and, its use is expected to reduce AC loss by applying slit processing on the tape wire, contributing to future cost reductions. In addition, the development of efficient, economical cryogenic units is also expected. The authors have developed a conceptual design for a 66 kV/20 MVA power transformer using YBCO tape wires, or an YBCO power transformer. As a result, we were able to identify the transformer's optimal system structure including coil winding comprised of coils and tape wires; and, we confirmed that the devised transformer can made to be both compact and highly efficient

  2. Remarkable weakness against cleavage stress for YBCO-coated conductors and its effect on the YBCO coil performance

    International Nuclear Information System (INIS)

    Yanagisawa, Y.; Nakagome, H.; Takematsu, T.; Takao, T.; Sato, N.; Takahashi, M.; Maeda, H.

    2011-01-01

    Cleavage strength for YBCO-coated conductor is extremely low, typically 0.5 MPa. The remarkable weakness is due to cracks on the slit edge of the conductor. The cleavage stress appears on YBCO double pancake coils impregnated with epoxy. The cleavage stress should be avoided in the coil winding. Cleavage strength for an YBCO-coated conductor at 77 K was investigated with a model experiment. The nominal cleavage strength for an YBCO-coated conductor is extremely low, typically 0.5 MPa. This low nominal cleavage strength is due to stress concentration on a small part of the YBCO-coated conductor in cleavage fracture. Debonding by the cleavage stress occurs at the interface between the buffer layer and the Hastelloy substrate. The nominal cleavage strength for a slit edge of the conductor is 2.5-times lower than that for the original edge of the conductor; cracks and micro-peel existing over the slit edge reduce the cleavage strength for the slit edge. Cleavage stress and peel stress should be avoided in coil winding, as they easily delaminate the YBCO-coated conductor, resulting in substantial degradation of coil performance. These problems are especially important for epoxy impregnated YBCO-coated conductor coils. It appears that effect of cleavage stress and peel stress are mostly negligible for paraffin impregnated YBCO-coated conductor coils or dry wound YBCO-coated conductor coils.

  3. AC Loss Reduction in Filamentized YBCO Coated Conductors with Virtual Transverse Cross-cuts

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Yifei [ORNL; Duckworth, Robert C [ORNL; Ha, Tam T [ORNL; List III, Frederick Alyious [ORNL; Gouge, Michael J [ORNL; Chen, Y [SuperPower Incorporated, Schenectady, New York; X, Xiong, [SuperPower Incorporated, Schenectady, New York; Selvamanickam, V. [SuperPower Incorporated, Schenectady, New York

    2011-01-01

    While the performance of YBa{sub 2}Cu{sub 3}O{sub 7-x} (YBCO)-based coated conductors under dc currents has improved significantly in recent years, filamentization is being investigated as a technique to reduce ac loss so that the 2nd generation (2G) high temperature superconducting (HTS) wires can also be utilized in various ac power applications such as cables, transformers and fault current limiters. Experimental studies have shown that simply filamentizing the superconducting layer is not effective enough to reduce ac loss because of incomplete flux penetration in between the filaments as the length of the tape increases. To introduce flux penetration in between the filaments more uniformly and further reduce the ac loss, virtual transverse cross-cuts were made in superconducting filaments of the coated conductors fabricated using the metal organic chemical vapor deposition (MOCVD) method. The virtual transverse cross-cuts were formed by making cross-cuts (17 - 120 {micro}m wide) on the IBAD (ion beam assisted deposition)-MgO templates using laser scribing followed by depositing the superconducting layer ({approx} 0.6 {micro}m thick). AC losses were measured and compared for filamentized conductors with and without the cross-cuts under applied peak ac fields up to 100 mT. The results were analyzed to evaluate the efficacy of filament decoupling and the feasibility of using this method to achieve ac loss reduction.

  4. Sm-doped CeO2 single buffer layer for YBCO coated conductors by polymer assisted chemical solution deposition (PACSD) method

    International Nuclear Information System (INIS)

    Li, G.; Pu, M.H.; Sun, R.P.; Wang, W.T.; Wu, W.; Zhang, X.; Yang, Y.; Cheng, C.H.; Zhao, Y.

    2008-01-01

    An over 150 nm thick Sm 0.2 Ce 0.8 O 1.9-x (SCO) single buffer layer has been deposited on bi-axially textured NiW (2 0 0) alloy substrate. Highly in-plane and out-of-plane oriented, dense, smooth and crack free SCO single layer has been obtained via a polymer-assisted chemical solution deposition (PACSD) approach. YBCO thin film has been deposited equally via a PACSD route on the SCO-buffered NiW, the as grown YBCO yielding a sharp transition at T c0 = 87 K as well as J c (0 T, 77 K) ∼ 1 MA/cm 2 . These results indicates that RE (lanthanides other than Ce) doping may be an effective approach to improve the critical thickness of solution derived CeO 2 film, which renders it a promising candidate as single buffer layer for YBCO coated conductors

  5. Novel tri-modal defect structure in Nb-doped MOCVD Y Ba2Cu3O7: a paradigm for pinning landscape control

    International Nuclear Information System (INIS)

    Aytug, Tolga; Zuev, Yuri; Specht, Eliot D; Parans Paranthaman, M; Maroni, Victor A; Miller, Dean J; Chen, Zhijun; Jeremy Kropf, A; Zaluzec, Nestor J

    2012-01-01

    Immobilization of vortices, or flux pinning, is both an enduring scientific issue and one of the most important problems in optimizing high temperature superconductors (HTSs) for commercial use. Here, we demonstrate a practical approach to the creation of a multi-modal flux pinning landscape in Y Ba 2 Cu 3 O 7 (YBCO) films employing an industrially scalable metal–organic chemical vapor deposition technique. Through controlled additions of Nb, we have achieved a novel distribution of crystallographic defects that immobilize (pin) vortices in the YBCO matrix. That is, with only the addition of a single dopant element, a tri-modal, non-superconducting defect structure is induced that threads through the YBCO matrix laterally (parallel to the ab planes of YBCO), vertically (parallel to the YBCO c-axis), and isotropically in the form of random spherical defects. For optimally doped samples, the influence of these multi-modal nanocrystalline defect structures on the flux pinning properties manifests itself as a significant improvement in the critical current density (J c ) for all magnetic field orientations. The results demonstrate the possibility of achieving an ideal flux pinning landscape (from an orientation and strength viewpoint), which permits the design of HTS wires with fully-tunable properties by processes suitable for large-scale manufacturing. (paper)

  6. Interaction of ultra soft magnetic materials with the high-T{sub c} superconductor YBCO

    Energy Technology Data Exchange (ETDEWEB)

    Stahl, Claudia; Treiber, Sebastian; Schuetz, Gisela [Max Planck Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Walker, Patrick [Max Planck Institute for Intelligent Systems, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany); Albrecht, Joachim [Aalen University, Beethovenstrasse 1, 73430 Aalen (Germany)

    2013-07-01

    We have grown bilayers of optimally doped YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) and ferromagnetic CoFeB on single-crystalline substrates by pulsed laser deposition and sputtering. These heterostructures are typically composed of about 100 nm YBCO and several 10 nm of CoFeB. Regarding the superconductor, the properties of the YBCO film change as a consequence of the vicinity of the ferromagnet. In detail we investigated the critical current density as a function of temperature, applied field and time as well as the transition temperature by SQUID magnetization measurements and quantitative magneto-optical measurements. The amorphous material CoFeB exhibits an in plane anisotropy and a very low coercivity. From magneto-optical images we find that the flux line lattice of the superconductor is mapped into the magnet and still visible as significant magnetic out-of-plane contrast at room temperature. We discuss this phenomenon as a new route to high-resolution mapping of the flux line distribution on a nanometer scale.

  7. Incorporation of self-organised gold nano crystals in YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} thin films: Modification of superconducting properties

    Energy Technology Data Exchange (ETDEWEB)

    Katzer, Christian; Michalowski, Peter; Westerhausen, Markus; Koch, Stefanie; Schmidl, Frank; Seidel, Paul [Institut fuer Festkoerperphysik, Friedrich-Schiller-Universitaet Jena, Helmholtzweg 5, 07743 Jena (Germany); Treiber, Sebastian [Max-Planck-Institut fuer Intelligente Systeme, Heisenbergstrasse 3, 70569 Stuttgart (Germany); Albrecht, Joachim [Hochschule Aalen, Beethovenstrasse 1, 73430 Aalen (Germany)

    2012-07-01

    Using pulsed laser deposition we are able to fabricate and examine Yttrium-Barium-Copper-Oxide (YBCO) thin films of high quality. A particular point of interest thereby is the influence of a pre-deposited gold layer with a well-defined film thickness. During the growth of the YBCO thin film the intermediate gold layer self assembles into crystalline nano particles, which modify the growth conditions and hence the physical properties of the growing YBCO. We report on the modification of structural and superconducting properties of our YBCO thin films (such as rocking curve widths, critical temperature T{sub c} and critical current density j{sub c}) comparing conventional to Au added YBCO. The temperature dependence of the critical current density thereby was determined using transport measurements as well as magneto-optical measurements. Furthermore investigations of the flux noise of our gold modified YBCO films are presented.

  8. Anomalous diffusion of Ga and As from semi-insulating GaAs substrate into MOCVD grown ZnO films as a function of annealing temperature and its effect on charge compensation

    Directory of Open Access Journals (Sweden)

    Pranab Biswas

    2014-05-01

    Full Text Available The diffusion behavior of arsenic (As and gallium (Ga atoms from semi-insulating GaAs (SI-GaAs into ZnO films upon post-growth annealing vis-à-vis the resulting charge compensation was investigated with the help of x-ray photoelectron spectroscopy (XPS and secondary ion mass spectroscopy. The films, annealed at 600 ºC and 700 ºC showed p-type conductivity with a hole concentration of 1.1 × 1018 cm−3 and 2.8 × 1019 cm−3 respectively, whereas those annealed at 800 ºC showed n-type conductivity with a carrier concentration of 6.5 × 1016 cm−3. It is observed that at lower temperatures, large fraction of As atoms diffused from the SI-GaAs substrates into ZnO and formed acceptor related complex, (AsZn–2VZn, by substituting Zn atoms (AsZn and thereby creating two zinc vacancies (VZn. Thus as-grown ZnO which was supposed to be n-type due to nonstoichiometric nature showed p-type behavior. On further increasing the annealing temperature to 800 ºC, Ga atoms diffused more than As atoms and substitute Zn atoms thereby forming shallow donor complex, GaZn. Electrons from donor levels then compensate the p-type carriers and the material reverts back to n-type. Thus the conversion of carrier type took place due to charge compensation between the donors and acceptors in ZnO and this compensation is the possible origin of anomalous conduction in wide band gap materials.

  9. Growth and characterization of InP/GaAs on SOI by MOCVD

    International Nuclear Information System (INIS)

    Karam, N.H.; Haven, V.; Vernon, S.M.; Namavar, F.; El-Masry, N.; Haegel, N.; Al-Jassin, M.M.

    1990-01-01

    This paper reports that epitaxial InP films have been successfully deposited on GaAs coated silicon wafers with a buried oxide for the first time by MOCVD. The SOI wafers were prepared using the Separation by Implantation of Oxygen (SIMOX) process. The quality of InP on SIMOX is comparable to the best of InP on Si deposited in the same reactor. Preliminary results on defect reduction techniques such as Thermal Cycle Growth (TCG) show an order of magnitude increase in the photoluminescence intensity and a factor of five reduction in the defect density. TCG has been found more effective than Thermal Cycle Annealing (TCA) in improving the crystalline perfection and optical properties of the deposited films

  10. SmBa2NbO6 Nanopowders, an Effective Percolation Network Medium for YBCO Superconductors

    Directory of Open Access Journals (Sweden)

    S. Vidya

    2013-01-01

    Full Text Available The percolation behavior of superconductor-insulator composite, YBa2Cu3O7–δ, and nano SmBa2NbO2 synthesized by modified combustion technique was studied. Particle size of nano SmBa2NBO6 was determined using transmission electron microscopy. The chemical nonreactivity of nano SmBa2NbO6 with YBCO is evident from the X-Ray diffraction study which makes it a suitable nanoceramic substrate material for high temperature superconducting films. A systematic increase in the sintered density, approaching the optimum value of the insulating nanophase is clearly observed, as the vol.% of YBCO in the composite decreases. SEM micrograph showed uniform distribution of nanopowder among the large clusters of YBCO. The obtained percolation threshold is ~26 vol% of YBCO in the composite. All the composites below the threshold value showed TC(0~92 K even though the room resistivity increases with increase in vol.% of nano SmBa2NbO6. The values of critical exponents obtained matches well with the theoretically expected ones for an ideal superconductor-insulator system.

  11. Shot noise in YBCO bicrystal Josephson junctions

    DEFF Research Database (Denmark)

    Constantinian, K.Y.; Ovsyannikov, G.A.; Borisenko, I.V.

    2003-01-01

    We measured spectral noise density in YBCO symmetric bicrystal Josephson junctions on sapphire substrates at bias voltages up to 100 mV and T 4.2 K. Normal state resistance of the Josephson junctions, R-N = 20-90 Omega and ICRN up to 2.2 mV have been observed in the experimental samples. Noise...... may explain the experimentally measured linewidth broadening of Josephson oscillations at mm and submm wave frequencies in high-Tc superconducting junctions. Experimental results are discussed in terms of bound states existing at surfaces of d-wave superconducting electrodes....

  12. Maximum permissible voltage of YBCO coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Wen, J.; Lin, B.; Sheng, J.; Xu, J.; Jin, Z. [Department of Electrical Engineering, Shanghai Jiao Tong University, Shanghai (China); Hong, Z., E-mail: zhiyong.hong@sjtu.edu.cn [Department of Electrical Engineering, Shanghai Jiao Tong University, Shanghai (China); Wang, D.; Zhou, H.; Shen, X.; Shen, C. [Qingpu Power Supply Company, State Grid Shanghai Municipal Electric Power Company, Shanghai (China)

    2014-06-15

    Highlights: • We examine three kinds of tapes’ maximum permissible voltage. • We examine the relationship between quenching duration and maximum permissible voltage. • Continuous I{sub c} degradations under repetitive quenching where tapes reaching maximum permissible voltage. • The relationship between maximum permissible voltage and resistance, temperature. - Abstract: Superconducting fault current limiter (SFCL) could reduce short circuit currents in electrical power system. One of the most important thing in developing SFCL is to find out the maximum permissible voltage of each limiting element. The maximum permissible voltage is defined as the maximum voltage per unit length at which the YBCO coated conductors (CC) do not suffer from critical current (I{sub c}) degradation or burnout. In this research, the time of quenching process is changed and voltage is raised until the I{sub c} degradation or burnout happens. YBCO coated conductors test in the experiment are from American superconductor (AMSC) and Shanghai Jiao Tong University (SJTU). Along with the quenching duration increasing, the maximum permissible voltage of CC decreases. When quenching duration is 100 ms, the maximum permissible of SJTU CC, 12 mm AMSC CC and 4 mm AMSC CC are 0.72 V/cm, 0.52 V/cm and 1.2 V/cm respectively. Based on the results of samples, the whole length of CCs used in the design of a SFCL can be determined.

  13. Growth techniques for monolithic YBCO solenoidal magnets

    International Nuclear Information System (INIS)

    Scruggs, S.J.; Putman, P.T.; Fang, H.; Alessandrini, M.; Salama, K.

    2006-01-01

    The possibility of growing large single domain YBCO solenoids by the use of a large seed has been investigated. There are two known methods for producing a similar solenoid. This first is a conventional top seeded melt growth process followed by a post processing machining step to create the bore. The second involves using multiple seeds spaced around the magnet bore. The appeal of the new technique lies in decreasing processing time compared to the single seed technique, while avoiding alignment problems found in the multiple seeding technique. By avoiding these problems, larger diameter monoliths can be produced. Large diameter monoliths are beneficial because the maximum magnetic field produced by a trapped field magnet is proportional to the radius of the sample. Furthermore, the availability of trapped field magnets with large diameter could enable their use in applications that traditionally have been considered to require wound electromagnets, such as beam bending magnets for particle accelerators or electric propulsion. A comparison of YBCO solenoids grown by the use of a large seed and grown by the use of two small seeds simulating multiple seeding is made. Trapped field measurements as well as microstructure evaluation were used in characterization of each solenoid. Results indicate that high quality growth occurs only in the vicinity of the seeds for the multiple seeded sample, while the sample with the large seeded exhibited high quality growth throughout the entire sample

  14. Growth techniques for monolithic YBCO solenoidal magnets

    Energy Technology Data Exchange (ETDEWEB)

    Scruggs, S.J. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States)]. E-mail: Sscruggs2@uh.edu; Putman, P.T. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States); Fang, H. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States); Alessandrini, M. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States); Salama, K. [Texas Center for Superconductivity at University of Houston, 4800 Calhoun, Houston, TX 77204 (United States)

    2006-10-01

    The possibility of growing large single domain YBCO solenoids by the use of a large seed has been investigated. There are two known methods for producing a similar solenoid. This first is a conventional top seeded melt growth process followed by a post processing machining step to create the bore. The second involves using multiple seeds spaced around the magnet bore. The appeal of the new technique lies in decreasing processing time compared to the single seed technique, while avoiding alignment problems found in the multiple seeding technique. By avoiding these problems, larger diameter monoliths can be produced. Large diameter monoliths are beneficial because the maximum magnetic field produced by a trapped field magnet is proportional to the radius of the sample. Furthermore, the availability of trapped field magnets with large diameter could enable their use in applications that traditionally have been considered to require wound electromagnets, such as beam bending magnets for particle accelerators or electric propulsion. A comparison of YBCO solenoids grown by the use of a large seed and grown by the use of two small seeds simulating multiple seeding is made. Trapped field measurements as well as microstructure evaluation were used in characterization of each solenoid. Results indicate that high quality growth occurs only in the vicinity of the seeds for the multiple seeded sample, while the sample with the large seeded exhibited high quality growth throughout the entire sample.

  15. P-type Ge epitaxy on GaAs (100) substrate grown by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Jin, Y.J.; Chia, C.K.; Liu, H.F.; Wong, L.M.; Chai, J.W.; Chi, D.Z.; Wang, S.J., E-mail: sj-wang@imre.a-star.edu.sg

    2016-07-15

    Highlights: • The heterogeneous integration of p-Ge/GaAs by MOCVD indicates significance for the application in optoelectronic devices such as p-MOSFET, dual band photodetector, etc. • Many undesired pillar-structures were observed on the p-Ge epilayers and we found that the cause of the pillar-like structures was related to the Ge-Ga dimers formed during the growth. • We found that a GaAs substrate with fewer Ga or Ge danglings was helpful in suppressing the formation of the unwanted pillar-like structures and thus obtaining high quality p-Ge epilayers. - Abstract: In this work, Ga-doped Geranium (Ge) films have been grown on GaAs (100) substrates by metal-organic chemical vapor deposition (MOCVD). Undesired pillar structures have been observed on the epilayers prepared at relatively lower temperatures. Energy dispersive X-ray spectroscopy (EDX) indicated that the pillars are mainly consisted of Ga atoms, which is totally different from that of the Ge film. It was demonstrated that the pillar structures could be reduced by simply raising the growth temperature while keeping the other growth conditions unchanged. In this regard, the growth mechanism of the pillars was related to the Ge-Ga dimers formed during the growth of p-Ge films. By further studying the influence of a GaAs or Ge buffer layer on the growth of p-Ge layers, we found that the GaAs substrate with lower density of Ga or Ge dangling bonds was helpful in suppressing the formation of the undesired pillar structures.

  16. Rapid processing method for solution deposited YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Dawley, J.T.; Clem, P.G.; Boyle, T.J.; Ottley, L.M.; Overmyer, D.L.; Siegal, M.P

    2004-02-01

    YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) films, deposited on buffered metal substrates, are the primary candidate for second-generation superconducting (SC) wires, with applications including expanded power grid transmission capability, compact motors, and enhanced sensitivity magnetic resonance imaging. Feasibility of manufacturing such superconducting wires is dependent on high processing speed, often a limitation of vapor and solution-based YBCO deposition processes. In this work, YBCO films were fabricated via a new diethanolamine-modified trifluoroacetic film solution deposition method. Modifying the copper chemistry of the YBCO precursor solution with diethanolamine enables a hundredfold decrease in the organic pyrolysis time required for MA/cm{sup 2} current density (J{sub c}) YBCO films, from multiple hours to {approx}20 s in atmospheric pressure air. High quality, {approx}0.2 {mu}m thick YBCO films with J{sub c} (77 K) values {>=}2 MA/cm{sup 2} at 77 K are routinely crystallized from these rapidly pyrolyzed films deposited on LaAlO{sub 3}. This process has also enabled J{sub c} (77 K)=1.1 MA/cm{sup 2} YBCO films via 90 m/h dip-coating on Oak Ridge National Laboratory RABiTS textured metal tape substrates. This new YBCO solution deposition method suggests a route toward inexpensive and commercializable {approx}$10/kA m solution deposited YBCO coated conductor wires.

  17. Synthesis and properties of barium diketonates as precursors for MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Drozdov, A.A. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Troyanov, S.I. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Kuzmina, N.P. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Martynenko, L.I. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Alikhanyan, A.S. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Malkerova, I.P. (Dept. of Chemistry, Moscow State Univ. (Russian Federation))

    1993-08-01

    The structures of barium diketonates depend on the way in which they are synthesized. It is shown that there is a correlation between the volatility of these compounds and their crystal structures. A new volatile mononuclear adduct of barium dipivaloylmethanate suitable for MOCVD is suggested. (orig.).

  18. Synthesis and properties of barium diketonates as precursors for MOCVD

    International Nuclear Information System (INIS)

    Drozdov, A.A.; Troyanov, S.I.; Kuzmina, N.P.; Martynenko, L.I.; Alikhanyan, A.S.; Malkerova, I.P.

    1993-01-01

    The structures of barium diketonates depend on the way in which they are synthesized. It is shown that there is a correlation between the volatility of these compounds and their crystal structures. A new volatile mononuclear adduct of barium dipivaloylmethanate suitable for MOCVD is suggested. (orig.)

  19. Photoluminescence of Mg-doped m-plane GaN grown by MOCVD on bulk GaN substrates

    OpenAIRE

    Monemar, Bo; Paskov, Plamen; Pozina, Galia; Hemmingsson, Carl; Bergman, Peder; Lindgren, David; Samuelson, Lars; Ni, Xianfeng; Morkoç, Hadis; Paskova, Tanya; Bi, Zhaoxia; Ohlsson, Jonas

    2011-01-01

    Photoluminescence (PL) properties are reported for a set of m-plane GaN films with Mg doping varied from mid 1018cm-3 to well above 1019 cm-3. The samples were grown with MOCVD at reduced pressure on low defect density m-plane bulk GaN templates. The sharp line near bandgap bound exciton (BE) spectra observed below 50 K, as well as the broader donor-acceptor pair (DAP) PL bands at 2.9 eV to 3.3 eV give evidence of several Mg related acceptors, similar to the case of c-plane GaN. The dependenc...

  20. Atomic oxygen effect on the in situ growth of stoichiometric YBa2Cu3O7 - delta epitaxial films by facing targets 90° off-axis radiofrequency magnetron sputtering

    Science.gov (United States)

    Oya, Gin-ichiro; Diao, Chien Chen; Imai, Syozo; Uzawa, Takaaki; Sawada, Yasuji; Sugai, Tokuko; Nakajima, Kensuke; Yamashita, Tsutomu

    1995-06-01

    (110)- and (103)-oriented almost stoichiometric YBa2Cu3O7-δ (YBCO) films have been grown epitaxially on hot SrTiO3 (110) substrates using a 90° off-axis rf magnetron sputtering technique, for fabrication of vertical sandwich-type YBCO/insulator/YBCO or YBCO/normal metal/YBCO Josephson junctions utilizing the high-quality YBCO films. The YBCO epitaxial films with high transition temperatures Tc of ˜90 K have been deposited in situ only under the conditions of substrate temperatures Ts of ˜650-˜700 °C and oxygen partial pressure PO2 of ˜5×10-3-˜10×10-3 Torr, which are in close proximity to the critical stability/decomposition line for YBa2Cu3O6 in the ordinary Y-Ba-Cu-O phase diagram. Using a quadrupole mass spectrometer, a high density of atomic oxygen has directly been observed to be efficiently produced in the sputter glow discharge under the above optimum conditions of PO2. This atomic oxygen has played a key role in promoting the formation of the perovskite structure and the epitaxial growth of the YBCO films. Furthermore, Shapiro steps have successfully been observed for a Nb-YBCO point-contact junction, which is made by pressing a Nb needle on a surface-etched YBCO epitaxial film, under 525.4 GHz submillimeter-wave irradiation.

  1. Microwave dynamics of YBCO bi-epitaxial Josephson structures

    DEFF Research Database (Denmark)

    Constantinian, K. Y.; Ovsyannikov, G. A.; Mashtakov, A. D.

    1996-01-01

    The processes of interaction of microwaves (frequency View the MathML source) with a single high-Tc superconducting YBa2Cu3Ox (YBCO) bi-epitaxial grain-boundary junction and with an array of two junctions connected in series, have been investigated experimentally at temperatures T = 4.2− 77 K......, as well as the subharmonic detector response at weak magnetic fields φ microwave field induced frequency synchronization of two series connected bi-epitaxial YBCO junctions....

  2. Adhesion strength study of IBAD-MOCVD-based 2G HTS wire using a peel test

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Y., E-mail: yzhang@superpower-inc.com [SuperPower Inc., 450 Duane Avenue, Schenectady, NY 12304 (United States); Hazelton, D.W.; Knoll, A.R.; Duval, J.M.; Brownsey, P.; Repnoy, S.; Soloveichik, S.; Sundaram, A.; McClure, R.B. [SuperPower Inc., 450 Duane Avenue, Schenectady, NY 12304 (United States); Majkic, G.; Selvamanickam, V. [University of Houston, 4800 Calhoun Road, Houston, TX 77204 (United States)

    2012-02-15

    A peel test was used to study the adhesion strength of a commercial grade 2G HTS wire which features a characteristic multilayer structure with the rare earth-based MOCVD superconducting film deposited on an IBAD-MgO template. The peel test could be carried out at various peeling angles (from 90 Degree-Sign to 180 Degree-Sign) and the peel strength of a wire was defined as the steady-state peeling load determined from a load-displacement curve. The test results had good reproducibility and accuracy, making the test a reliable and useful method for studying the adhesion strength of the wire. By characterizing the peeled surfaces the weakest interface in a wire could be identified. The peel strength data of the wire was analyzed together with the performance of the experimental magnet coils fabricated using the wire. The effect of the silver contact layer annealing on the peel strength is discussed.

  3. Adhesion strength study of IBAD-MOCVD-based 2G HTS wire using a peel test

    International Nuclear Information System (INIS)

    Zhang, Y.; Hazelton, D.W.; Knoll, A.R.; Duval, J.M.; Brownsey, P.; Repnoy, S.; Soloveichik, S.; Sundaram, A.; McClure, R.B.; Majkic, G.; Selvamanickam, V.

    2012-01-01

    A peel test was used to study the adhesion strength of a commercial grade 2G HTS wire which features a characteristic multilayer structure with the rare earth-based MOCVD superconducting film deposited on an IBAD-MgO template. The peel test could be carried out at various peeling angles (from 90° to 180°) and the peel strength of a wire was defined as the steady-state peeling load determined from a load-displacement curve. The test results had good reproducibility and accuracy, making the test a reliable and useful method for studying the adhesion strength of the wire. By characterizing the peeled surfaces the weakest interface in a wire could be identified. The peel strength data of the wire was analyzed together with the performance of the experimental magnet coils fabricated using the wire. The effect of the silver contact layer annealing on the peel strength is discussed.

  4. Synthesis and Characterization of Nano Scale YBCO

    International Nuclear Information System (INIS)

    Sukirman, E.; Wisnu AA; Yustinus P; Sahidin W, D.; Rina M, Th.

    2009-01-01

    Synthesis and characterization of the nano scale YBCO superconductor have been performed. The nano scale superconductor was synthesized from YBCO system (YBa 2 Cu 3 O 7-X ). Raw materials, namely Y 2 O 3 , BaCO 3 , and Cu°, were balanced and mixed with ethanol using magnetic steering as a churn in a beaker glass. Then, the precursor was calcined at T k = 900°C for 5 hours and repeated it until three times. The resulting precursor was ground by using High Energy Milling (HEM) for t = 0, 30, 50, 70, and 90 hour and hereinafter precursors are successively referred as YKM-00, YKM-30, YKM-50, YKM-70, and YKM-90. The resulting powders phase were characterized by means of x-ray diffraction technique using the Rietveld analysis method. Precursor of YKM-90 was pressed into pellets, and then sintered at various temperatures and periods. The sample phase was then characterized by using the Rietveld analysis method based on the x-ray diffraction data. The crystallites size were calculated using Scherrer formula. Results of analysis indicate that by minimizing crystallites size, period of sinter can be shortened from 10 to 1 hour, resulting crystallite size of D = 925 Å, critical current density of J c = 4 A / cm 2 , and can be grown of about 15 weight % of 211-phase in a matrix of 123-phase. The decrease of crystallite size will generate a change in physical properties dramatically, if the crystallite size of the material, D is smaller or equal to the coherence length of 10 Å. (author)

  5. Effect of Y2O3 Nanoparticles on Critical Current Density of YBa2Cu3O7-x Thin Films

    International Nuclear Information System (INIS)

    Tran, H. D.; Reddy, Sreekantha; Wie, C. H.; Kang, B.; Oh, Sang Jun; Lee, Sung Ik

    2009-01-01

    Introduction of proper impurity into YBa 2 Cu 3 O 7-x (YBCO) thin films is an effective way to enhance its flux-pinning properties. We investigate effect of Y 2 O 3 nanoparticles on the critical current density J c of the YBCO thin films. The Y 2 O 3 nanoparticles were created perpendicular to the film surface (parallel with the c-axis) either between YBCO and substrate or on top of YBCO, YBCO/Y 2 O 3 /LAO or Y 2 O 3 /YBCO/STO, by pulsed laser deposition. The deposition temperature of the YBCO films were varied (780 degree C and 800 degree C) to modify surface morphology of the YBCO films. Surface morphology characterization revealed that the lower deposition temperature of 780 degree C created nano-sized holes on the YBCO film surface which may behave as intrinsic pinning centers, while the higher deposition temperature produced much denser and smoother surface. J-c values of the YBCO films with Y 2 O 3 particles were either remained nearly the same or decreased for the samples in which YBCO is grown at 780 degree C. On the other hand, J-c values were enhanced for the samples in which YBCO is grown at higher temperature of 800 degree C. The difference in the effect of Y 2 O 3 can be explained by the fact that the higher deposition temperature of 800 degree C reduces intrinsic pinning centers and J c is enhanced by introduction of artificial pinning centers in the form of Y 2 O 3 nanoparticles.

  6. Pulsed laser deposition of YBCO coated conductor using Y2O3 as the seed and cap layer

    International Nuclear Information System (INIS)

    Barnes, P N; Nekkanti, R M; Haugan, T J; Campbell, T A; Yust, N A; Evans, J M

    2004-01-01

    Although a variety of buffer layers have been routinely reported, a standard architecture commonly used for the Y Ba 2 Cu 3 O 7-x (YBCO) coated conductor is Y BCO/CeO 2 /Y SZ/CeO 2 /substrate or Y BCO/CeO 2 /Y SZ/Y 2 O 3 /substrate where ceria is typically the cap layer. CeO 2 is generally used as only a seed (or cap layer) since cracking within the film occurs in thicker CeO 2 layers due to the stress of lattice mismatching. Y 2 O 3 has been proposed as a seed and as a cap layer but usually not for both in a given architecture, especially with all layers deposited in situ. Yttrium oxide films grown on nickel by electron beam evaporation processes were found to be dense and crack free with good epitaxy. In this report, pulsed laser deposition (PLD) of Y 2 O 3 is given where Y 2 O 3 serves as both the seed and cap layer in the YBCO architecture. A comparison to PLD CeO 2 is provided. Deposited layers of the YBCO coated conductor are also grown by laser ablation. Initial deposition resulted in specimens on textured Ni substrates with current densities of more than 1 MA cm -2 at 77 K, self-field

  7. Weakening of thickness dependence of J{sub C} in YBa{sub 2}Cu{sub 3}O{sub 7-δ} films using a titanium-added MOD precursor solution

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, H.L., E-mail: zhanghuiliang@mail.iee.ac.cn [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); School of Science, Hebei University of Engineering, Handan 056038 (China); Ding, F.Z., E-mail: dingfazhu@mail.iee.ac.cn [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Gu, H.W., E-mail: guhw@mail.iee.ac.cn [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Dong, Z.B. [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Qu, F.; Zhang, H.; Shang, H.J. [Key Laboratory of Applied Superconductivity, Institute of Electrical Engineering, Chinese Academy of Sciences, Beijing 100190 (China)

    2017-04-15

    Highlights: • The thickness dependence of J{sub C} in YBCO film was weakened by introducing BaTiO{sub 3} nanoparticles into YBCO matrix. • The high I{sub C} value of 430 MA/cm-width was obtained in the BaTiO{sub 3}-doped YBCO film prepared by the MOD method. • The YBCO composite thick film prepared by using the precursor solution with polyethyleneglycol shows a compact and smooth surface. - Abstract: BaTiO{sub 3} (BTO)-doped YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) films were prepared by the metal-organic deposition method using a precursor solution with titanium ion. These YBCO films were deposited on (00l)-oriented LaAlO{sub 3} single-crystal substrates using an automated dip coater. The thickness dependence of critical current density (J{sub C}) in the BTO-doped YBCO films was investigated. The J{sub C} value of the YBCO composite film was reduced from 6.3 to 4.6 MA/cm{sup 2} with increasing film thickness from 450 to 930 nm in self-filed at 77 K, which arose mainly from degradation of texture and roughening of the film. However, relative to undoped YBCO thick films, J{sub C} values of the YBCO composite thick films were greatly improved, and more importantly, the reduction in J{sub C} with increasing film thickness was hindered, especially in a high magnetic field. This result indicated that the introduction of BTO nanoparticles as pinning centers into YBCO matrix weakened the thickness dependence of J{sub C}.

  8. Oriented growth of thin films of samarium oxide by MOCVD

    Indian Academy of Sciences (India)

    Unknown

    Very thin layers of rare earth oxides, such as Sm2O3 and epitaxial Gd2O3, grown by thermal ... As the inorganic salts of the lanthanides, such as their halides, are ... sodium hydroxide, followed by the addition of ethanolic. 1,10-phenanthroline ...

  9. The effects of the firing temperature of YBCO coated conductors fabricated by TFA-MOD process

    International Nuclear Information System (INIS)

    Jang, Seok Hern; Lim, Jun Hyung; Kim, Kyu Tae; Lee, Jin Sung; Yoon, Kyung Min; Kim, Ho-Jin; Joo, Jinho; Kim, Hyoungsub; Lee, Hee-Gyoun; Hong, Gye-Won

    2006-01-01

    We fabricated YBCO films on LAO substrates using the TFA-MOD method and evaluated the effects of the heat treatment temperature on the microstructure, degree of texture, and critical properties. The phase formation and microstructure were characterized by X-ray diffraction, Raman spectroscopy and scanning electron microscopy (SEM) and the degree of texture was evaluated by pole-figure analysis. The firing was performed in the temperature range of 750-800 deg. C and we found that the phase purity, grain size and orientation, degree of texture, and oxygen content varied with the firing temperature. The films fired at 775 deg. C showed the highest critical temperature (T C -onset) of 89.5 K and critical current (I C ) of 40 A/cm-width, which corresponds to a critical current density (J C ) of 1.8 MA/cm 2 . According to the results of the XRD, pole-figure, SEM and Raman analyses, these optimum critical properties can probably be attributed to the formation of a pure YBCO phase, stronger c-axis orientation and higher oxygen content

  10. X-ray diffractometry of 10 nm thick YBa2Cu3O7-x films

    International Nuclear Information System (INIS)

    Drozdov, Yu.N.; Moldavskaya, L.D.; Parafin, A.E.

    1998-01-01

    We report on some specific features of the X-ray diffraction spectra for ultrathin c-axis-oriented YBCO films. The films were prepared by laser deposition on LaAlO 3 substrates. A DRON-4 powder diffractometer was used to analyze a structure and to measure thickness of the films. We find that this conventional technique can detect the YBCO films as thin as 5 nm. The X-ray interference fringes in the vicinity of the (005) YBCO reflections for the films from 10 to 20 nm thick were clearly visible. The oscillation period of the fringes depends on the thickness of the film and the intensity modulation yields some structural information. The I(-1)/I(+1) fringes intensity ratio was found to be sensitive to the type of atomic layer at the top and bottom of YBCO film [ru

  11. Numerical analysis of the influence of buffer layer thickness on the residual stresses in YBCO/La2Zr2O7/Ni superconducting materials

    International Nuclear Information System (INIS)

    Celik, Erdal; Sayman, Onur; Karakuzu, Ramazan; Ozman, Yilmaz

    2007-01-01

    The present paper addresses a numerical investigation of the influence of buffer layer thickness on the residual stress in YBCO/La 2 Zr 2 O 7 /Ni architectured materials under cryogenic conditions by using classical lamination theory (CLT) and finite element method (FEM) for coated conductor applications. YBCO/La 2 Zr 2 O 7 multilayer films were fabricated on Ni tape substrate using reel-to-reel sol-gel and pulse laser deposition (PLD) systems. The microstructural evolution of high temperature superconducting YBCO film and buffer layers with La 2 Zr 2 O 7 configuration grown on textured Ni tape substrates was investigated by using a scanning electron microscope (SEM). Thermal stress analysis of YBCO/La 2 Zr 2 O 7 /Ni multilayer sample was performed by using CLT in the temperature range of 298-175 K in liquid helium media. The YBCO/La 2 Zr 2 O 7 /Ni sample strip was solved by using FEM for linear or nonlinear cases in the temperature range of 298-3 K in liquid helium media. SEM observations revealed that crack-free, pinhole-free, continuous superconducting film and buffer layer were obtained by sol-gel and PLD systems. In addition to microstructural observations, it was found that the largest compressive stresses and failure occur in La 2 Zr 2 O 7 buffer layer due to its smallest thermal expansion coefficient. The thickness of La 2 Zr 2 O 7 buffer layer affects the failure. The stress component of σ x is the smallest in Ni tape substrate due to its largest thickness

  12. The infrared Hall effect in YBCO: Temperature and frequency dependence of Hall scattering

    International Nuclear Information System (INIS)

    Grayson, M.; Cerne, J.; Drew, H.D.; Schmadel, D.C.; Hughes, R.; Preston, J.S.; Kung, P.J.; Vale, L.

    1999-01-01

    The authors measure the Hall angle, θ H , in YBCO films in the far- and mid-infrared to determine the temperature and frequency dependence of the Hall scattering. Using novel modulation techniques they measure both the Faraday rotation and ellipticity induced by these films in high magnetic fields to deduce the complex conductivity tensor. They observe a strong temperature dependence of the mid-infrared Hall conductivity in sharp contrast to the weak dependence of the longitudinal conductivity. By fitting the frequency dependent normal state Hall angle to a Lorentzian θ H (ω) = ω H /(γ H minus iω) they find the Hall frequency, ω H , is nearly independent of temperature. The Hall scattering rate, γ H , is consistent with γ H ∼ T 2 up to 200 K and is remarkably independent of IR frequency suggesting non-Fermi liquid behavior

  13. Mode I type delamination fracture toughness of YBCO coated conductor with additional Cu layer

    International Nuclear Information System (INIS)

    Miyazato, T.; Hojo, M.; Sugano, M.; Adachi, T.; Inoue, Y.; Shikimachi, K.; Hirano, N.; Nagaya, S.

    2011-01-01

    A fracture toughness test method was developed for a YBCO coated conductor with an additional Cu layer. Mode I type tests were carried out using double cantilever beam (DCB) specimens. Delamination propagated into the YBCO layer, and sometimes reached the Ag/YBCO interface. The fracture toughness for YBCO was about 10 J/m 2 . That for Ag/YBCO interface was about 100 J/m 2 . Although interlaminar fracture at a YBa 2 Cu 3 O 7-δ (YBCO)/CeO 2 interface was reported for YBCO coated conductors, this has not yet been investigated by a fracture mechanical approach. In the present study, we developed a mode I type fracture toughness test method for a YBCO coated conductor with an additional Cu layer using double cantilever beam (DCB) specimens. Fracture mechanism was investigated by microscopic observation by a scanning electron microscope (SEM), together with composition analysis by an energy dispersive X-ray spectroscope (EDS). A pre-crack introduced at the YBCO/CeO 2 interface deviated from the interface, and propagated into the YBCO layer, and sometimes reached the Ag/YBCO interface. The fracture toughness, G R , for YBCO and the Ag/YBCO interface was evaluated to be 7-10 J/m 2 and 80-120 J/m 2 , respectively. The complex stress intensity factor ratio, K 2 /K 1 , at YBCO/CeO 2 interface was evaluated to be -0.19, and this ratio controlled the formation of microcracks in the YBCO layer. The main crack propagated into the YBCO layer accompanied with the formation of microcracks.

  14. Photoluminescence and photoluminescence excitation studies in 80 MeV Ni ion irradiated MOCVD grown GaN

    Energy Technology Data Exchange (ETDEWEB)

    Devaraju, G. [School of Physics, University of Hyderabad, Central University P.O., Hyderabad 500 046 (India); Pathak, A.P., E-mail: appsp@uohyd.ernet.in [School of Physics, University of Hyderabad, Central University P.O., Hyderabad 500 046 (India); Srinivasa Rao, N.; Saikiran, V. [School of Physics, University of Hyderabad, Central University P.O., Hyderabad 500 046 (India); Enrichi, Francesco [Coordinamento Interuniversitario Veneto per le Nanotecnologie (CIVEN), via delle Industrie 5, Marghera, I-30175Venice (Italy); Trave, Enrico [Dipartimento di Chimica Fisica, Universita Ca' Foscari Venezia, Dorsoduro 2137, I-30123 Venice (Italy)

    2011-09-01

    Highlights: {yields} MOCVD grown GaN samples are irradiated with 80 MeV Ni ions at room temperature. {yields} PL and PLE studies have been carried out for band to band, BL and YL emissions. {yields} Ni ions irradiated GaN shows BL band at 450 nm besides YL band. {yields} Radiation annealed Ga vacancies have quenching effect on YL intensity. {yields} We speculated that BL and YL are associated with N and Ga vacancies, respectively. - Abstract: We report damage creation and annihilation under energetic ion bombardment at a fixed fluence. MOCVD grown GaN thin films were irradiated with 80 MeV Ni ions at a fluence of 1 x 10{sup 13} ions/cm{sup 2}. Irradiated GaN thin films were subjected to rapid thermal annealing for 60 s in nitrogen atmosphere to anneal out the defects. The effects of defects on luminescence were explored with photoluminescence measurements. Room temperature photoluminescence spectra from pristine sample revealed presence of band to band transition besides unwanted yellow luminescence. Irradiated GaN does not show any band to band transition but there is a strong peak at 450 nm which is attributed to ion induced defect blue luminescence. However, irradiated and subsequently annealed samples show improved band to band transitions and a significant decrease in yellow luminescence intensity due to annihilation of defects which were created during irradiation. Irradiation induced effects on yellow and blue emissions are discussed.

  15. Low ac loss geometries in YBCO coated conductors

    International Nuclear Information System (INIS)

    Duckworth, R.C.; List, F.A.; Paranthaman, M.P.; Rupich, M.W.; Zhang, W.; Xie, Y.Y.; Selvamanickam, V.

    2007-01-01

    Reduction of ac losses in applied ac fields can be accomplished through either the creation of filaments and bridging in YBCO coated conductors or by an assembly of narrow width YBCO tapes. The ac losses for each of these geometries were measured at 77 K in perpendicular ac fields up to 100 mT. Despite physical isolation of the filaments, coupling losses were still present in the samples when compared to the expected hysteretic loss. In addition to filamentary conductors the assembly of stacked YBCO conductor provides an alternative method of ac loss reduction. When compared to a 4-mm wide YBCO coated conductor with a critical current of 60 A, the ac loss in a stack of 2-mm wide YBCO coated conductors with a similar total critical current was reduced. While the reduction in ac loss in a 2-mm wide stack coincided with the reduction in the engineering current density of the conductor, further reduction of ac loss was obtained through the splicing of the 2-mm wide tapes with low resistance solders

  16. Low ac loss geometries in YBCO coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Duckworth, R.C. [Oak Ridge National Laboratory, One Bethel Valley Road, P.O. Box 2008, MS-6305, Oak Ridge, TN 37831-6305 (United States)], E-mail: duckworthrc@ornl.gov; List, F.A.; Paranthaman, M.P. [Oak Ridge National Laboratory, One Bethel Valley Road, P.O. Box 2008, MS-6305, Oak Ridge, TN 37831-6305 (United States); Rupich, M.W.; Zhang, W. [American Superconductor, Two Technology Drive, Westborough, MA 01581 (United States); Xie, Y.Y.; Selvamanickam, V. [SuperPower, 450 Duane Ave, Schenectady, NY 12304 (United States)

    2007-10-01

    Reduction of ac losses in applied ac fields can be accomplished through either the creation of filaments and bridging in YBCO coated conductors or by an assembly of narrow width YBCO tapes. The ac losses for each of these geometries were measured at 77 K in perpendicular ac fields up to 100 mT. Despite physical isolation of the filaments, coupling losses were still present in the samples when compared to the expected hysteretic loss. In addition to filamentary conductors the assembly of stacked YBCO conductor provides an alternative method of ac loss reduction. When compared to a 4-mm wide YBCO coated conductor with a critical current of 60 A, the ac loss in a stack of 2-mm wide YBCO coated conductors with a similar total critical current was reduced. While the reduction in ac loss in a 2-mm wide stack coincided with the reduction in the engineering current density of the conductor, further reduction of ac loss was obtained through the splicing of the 2-mm wide tapes with low resistance solders.

  17. High-Jc YBa2Cu3O7-x-Ag superconducting thin films synthesized through a fluorine-free MOD method

    DEFF Research Database (Denmark)

    Tang, Xiao; Yue, Zhao; Wu, W.

    2015-01-01

    Obtaining a high critical current density (Jc) remains the main challenge in developing fluorine-free metal organic deposition (MOD) methods to fabricate YBCO superconducting thin films. Silver addition was used to raise the Jc values in this research work. By reacting with propionic acid...... and ammonia, AgNO3 was initially mixed with YBCO carboxylate precursors dissolved in methanol. High-temperature in situ XRD measurements on the YBCO-Ag powders revealed that silver addition lowers the incongruent melting temperature of YBCO to 760°C and resulted in a smooth surface morphology of the YBCO...... films at a temperature as low as 760°C. Grain growth and intergranular conductivity were also found to be improved by silver doping. After annealing under optimized conditions, a high Jc of 4.6MA/cm2 was obtained in a YBCO-Ag thin film with 10 wt% Ag....

  18. YBCO SQUIDs with unconventional current phase relation

    International Nuclear Information System (INIS)

    Bauch, T.; Johansson, J.; Cedergren, K.; Lindstroem, T.; Lombardi, F.

    2007-01-01

    We have studied the dynamics of YBa 2 Cu 3 O 7-δ (YBCO) dc sperconducting quantum interference devices (SQUIDs) characterized by an unconventional Josephson current phase relation (CPR). We have focused on SQUID configurations with Josephson junctions where the lobe of the order parameter in one electrode is facing a node in the other electrode. This order parameter arrangement should enhance the appearance of a sin(2φ) term in the CPR. The response of the critical current of the dc SQUID, under the effect of an external magnetic field, has been measured in temperature, down to 20 mK. Our experimental data have been compared with numerical simulations of the SQUIDs dynamics by considering a CPR of a single junction of the form I(φ) = I I sin(φ) - I II sin(2φ) where I I and I II are, respectively, the first and second harmonic component. In our devices the values of the sin(2φ) term are such that the fundamental state of the SQUID is naturally double degenerate. This is of great relevance for applications of d-wave SQUIDs in quantum information processing

  19. Detection of smaller J{sub c} region and damage in YBCO coated conductors by using permanent magnet method

    Energy Technology Data Exchange (ETDEWEB)

    Hattori, K., E-mail: tey88221@st.yamagata-u.ac.jp [Graduate School of Science and Engineering, Yamagata University, 4-3-16 Jonan, Yonezawa, Yamagata 992-8510 (Japan); Saito, A. [Graduate School of Science and Engineering, Yamagata University, 4-3-16 Jonan, Yonezawa, Yamagata 992-8510 (Japan); Takano, Y.; Suzuki, T. [Tohoku Seiki Industries, Ltd., 3-1246, Tachiyagawa, Yamagata 990-2251 (Japan); Yamada, H.; Takayama, T.; Kamitani, A.; Ohshima, S. [Graduate School of Science and Engineering, Yamagata University, 4-3-16 Jonan, Yonezawa, Yamagata 992-8510 (Japan)

    2011-11-15

    We developed a non-destructive method for measuring the critical current density (J{sub c}) in YBCO-coated conductors by using a permanent magnet (Sm{sub 2}Co{sub 17}). J{sub c} could be determined from the repulsive force (F{sub r}) generated between a permanent magnet and a coated conductor where shielding current flows. We also examined the influence of damage to the film on the J{sub c} distribution. The measured F{sub r} when the permanent magnet approached the cut part was smaller than that of the undamaged area. We developed a non-destructive method for measuring the critical current density (J{sub c}) in YBCO-coated conductors by using a permanent magnet (Sm{sub 2}Co{sub 17}). J{sub c} could be determined from the repulsive force (F{sub r}) generated between a permanent magnet and a coated conductor where shielding current flows. We tried to detect a smaller J{sub c} region in the coated conductor by using the system. The J{sub c} distribution could be determined without influence from the thick copper film on YBCO thin film. We also examined the influence of damage to the film on the J{sub c} distribution. The surface of the coated conductors was cut by using a knife. The measured F{sub r} when the permanent magnet approached the cut part was smaller than that of the undamaged area. This J{sub c} measurement technique will be useful for detecting smaller J{sub c} regions and defects in coated conductors.

  20. YBCO hot-electron bolometers dedicated to THz detection and imaging: Embedding issues

    International Nuclear Information System (INIS)

    Aurino, M; Tuerer, I; Martinez, A; Gensbittel, A; Degardin, A F; Kreisler, A J

    2010-01-01

    High-T c hot-electron bolometers (HEB) are an interesting alternative to other superconducting heterodyne mixers in the terahertz frequency range because of low-cost cooling investment, ultra-wide instantaneous bandwidth and low intrinsic noise level, even at 80 K. A technological process to fabricate stacked yttrium-based (YBCO) / praseodymium-based (PBCO) ultra-thin films (in the 15 to 40 nm thickness range) etched to form 0.5 μm x 0.5 μm constrictions, elaborated on (100) MgO substrates, has been previously described. Ageing effects were also considered, with the consequence of increased electrical resistance, significant degradation of the regular THz response and no HEB mixing action. Electron and UV lithography steps are revisited here to realize HEB mixers based on nano-bridges covered by a log-periodic planar gold antenna, dedicated to the 1 to 7 THz range. Several measures have been attempted to reduce the conversion losses, mainly by considering the embedding issues related to the YBCO nano-bridge impedance matching to the antenna and the design of optimized intermediate frequency circuitry. Antenna simulations were performed and validated through experiments on scaled models at GHz frequencies. Electromagnetic coupling to the incoming radiation was also studied, including crosstalk between neighbour antennas forming a linear imaging array.

  1. Epitaxial growth of textured YBa2Cu3O7-δ films on silver

    International Nuclear Information System (INIS)

    Liu Dan-Min; Liu Wei-Peng; Suo Hong-Li; Zhou Mei-Ling

    2005-01-01

    YBa 2 Cu 3 O 7-δ (YBCO) films were deposited on (100), (110) and (111) oriented silver single crystals and {100} left angle 100 right angle, {110} left angle 211 right angle, {110} left angle 100 right angle +{110} left angle 011 right angle {110} left angle 011 right angle and {012} left angle 100 right angle textured Ag substrates using pulsed laser deposition. The relationship between the epitaxial growth YBCO film and silver substrate has been determined. It is shown that among polycrystalline Ag substrates, {110} left angle 011 right angle textured tape is suitable for the deposition of YBCO thin films having strong texture. (orig.)

  2. Enhanced 77 K vortex-pinning in Y Ba2Cu3O7−x films with Ba2Y TaO6 and mixed Ba2Y TaO6 + Ba2Y NbO6 nano-columnar inclusions with irreversibility field to 11 T

    Directory of Open Access Journals (Sweden)

    F. Rizzo

    2016-06-01

    Full Text Available Pulsed laser deposited thin Y Ba2Cu3O7−x (YBCO films with pinning additions of 5 at. % Ba2Y TaO6 (BYTO were compared to films with 2.5 at. % Ba2Y TaO6 + 2.5 at. % Ba2Y NbO6 (BYNTO additions. Excellent magnetic flux-pinning at 77 K was obtained with remarkably high irreversibility fields greater than 10 T (YBCO-BYTO and 11 T (YBCO-BYNTO, representing the highest ever achieved values in YBCO films.

  3. MOD approach for the growth of epitaxial CeO2 buffer layers on biaxially textured Ni-W substrates for YBCO coated conductors

    International Nuclear Information System (INIS)

    Bhuiyan, M S; Paranthaman, M; Sathyamurthy, S; Aytug, T; Kang, S; Lee, D F; Goyal, A; Payzant, E A; Salama, K

    2003-01-01

    We have grown epitaxial CeO 2 buffer layers on biaxially textured Ni-W substrates for YBCO coated conductors using a newly developed metal organic decomposition (MOD) approach. Precursor solution of 0.25 M concentration was spin coated on short samples of Ni-3 at%W (Ni-W) substrates and heat-treated at 1100 C in a gas mixture of Ar-4%H 2 for 15 min. Detailed x-ray studies indicate that CeO 2 films have good out-of-plane and in-plane textures with full-width-half-maximum values of 5.8 deg. and 7.5 deg., respectively. High temperature in situ XRD studies show that the nucleation of CeO 2 films starts at 600 C and the growth completes within 5 min when heated at 1100 C. SEM and AFM investigations of CeO 2 films reveal a fairly dense microstructure without cracks and porosity. Highly textured YSZ barrier layers and CeO 2 cap layers were deposited on MOD CeO 2 -buffered Ni-W substrates using rf-magnetron sputtering. Pulsed laser deposition (PLD) was used to grow YBCO films on these substrates. A critical current, J c , of about 1.5 MA cm -2 at 77 K and self-field was obtained on YBCO (PLD)/CeO 2 (sputtered)/YSZ (sputtered)/CeO 2 (spin-coated)/Ni-W

  4. The magnetoresistance of YBCO/BZO composite superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Malik, Bilal A. [Department of Physics, University of Kashmir, Srinagar- 190006 (India); Asokan, K. [Materials Science Division, Inter University Accelerator Centre, New Delhi -110067 (India); Ganesan, V; Singh, Durgesh [UGC-DAE Consortium for Scientific Research, Khandwa Road, Indore (MP) 452 001 (India); Malik, Manzoor A., E-mail: mmalik@kashmiruniversity.ac.in [Department of Physics, University of Kashmir, Srinagar- 190006 (India)

    2016-12-15

    Highlights: • Limited addition of BZO in YBCO shows low resistive tailing behavior. • Limited addition of BZO in YBCO increases the activation energy of flux lines. • Vortex glass transition temperature increases with the limited addition of BZO. • Significant enhancement of H{sub C2}(0) is observed up to 4% BZO addition. - Abstract: We study the effect of addition of BaZrO{sub 3} (BZO) on normal and superconducting state of YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO). We find that in general both room temperature and residual resistivity increase with the addition of BZO except at low concentration of BZO. The temperature dependence of resistivity in presence of magnetic field also shows less resistivity broadening in composites containing low concentration of BZO below transition temperature (T{sub C}). The zero temperature upper critical field (H{sub c2}(0)), estimated by using Werthamer, Helfand and Hohenberg theory and Ginzburg Landau theory, shows an increase by the finite addition of BZO in YBCO. Further, the activation energy (U{sub 0}) determined from Arrhenius plots and vortex glass transition temperature (T{sub g}) also increase with the limited addition of BZO. Such an enhancement in H{sub c2}(0), U{sub o} and T{sub g} has been attributed to the increase in grain connectivity of YBCO . We conclude that the limited addition of BZO in YBCO significantly improves its superconducting performance in magnetic environment.

  5. Fabrication and characterization of melt-processed YBCO

    International Nuclear Information System (INIS)

    Sengupta, S.; Corpus, J.; Gaines, J.R. Jr.; Todt, V.R.; Zhang, X.F.; Miller, D.J.; Varanasi, C.; McGinn, P.J.

    1996-01-01

    Large domain YBCO are fabricated by using a melt processing technique for magnetic levitation applications. A Nd 1+x Ba 2-x Cu 3 O y seed is used to initiate grain growth and to control the orientation of YBCO grains. Samples as large as 2 inch have been fabricated by utilizing this method. Microstructural studies reveals two distinct regions in these levitators due to different growth mechanism along a/b and c axis. Some initial results on the mass production of these levitators are also reported

  6. Raman scattering studies of YBa2Cu3O7-x thin films grown by chemical vapor deposition and metal-organic deposition

    International Nuclear Information System (INIS)

    Lee, E.; Yoon, S.; Um, Y.M.; Jo, W.; Seo, C.W.; Cheong, H.; Kim, B.J.; Lee, H.G.; Hong, G.W.

    2007-01-01

    We present results of Raman scattering studies of superconducting YBa 2 Cu 3 O 7-x (YBCO) films grown by chemical vapor deposition and metal-organic deposition methods. It is shown by X-ray diffraction that all the as-grown YBCO films have a highly c-axis oriented and in-plane aligned texture. Raman scattering measurements were used to investigate optical phonon modes, oxygen contents, structural properties, and second-phases of the YBCO coated conductors. Raman spectra of YBCO films with lower-transport qualities exhibit additional phonon modes at ∼300 cm -1 , ∼600 cm -1 , and ∼630 cm -1 , which are related to second-phases such as Ba 2 Cu 3 O 5.9 and BaCuO 2 . Our results strongly suggest that Raman scattering be useful for optimizing YBCO film growth conditions

  7. AC over-current test results of YBCO conductor for YBCO power transformer with fault current limiting function

    International Nuclear Information System (INIS)

    Tomioka, A.; Otonari, T.; Ogata, T.; Iwakuma, M.; Okamoto, H.; Hayashi, H.; Iijima, Y.; Saito, T.; Gosho, Y.; Tanabe, K.; Izumi, T.; Shiohara, Y.

    2011-01-01

    The single-layer coils with a diameter of 250 mm and 12 turns were manufactured with YBCO tapes with a CuNi- or Cu-Tape. The AC over-current tests were carried out in subcooled liquid nitrogen at 66 K and 74 K to develop power transformers with current limiting function. The AC over-current was two to seven times larger than the I c of conductor and it was reduced to the same level of I c . The I c of model coils did not degrade. The test results showed the possibility of YBCO superconducting transformers with current limiting function. We are developing elemental technology for 66 kV/6.9 kV 20 MVA-class YBCO power transformer. The YBCO transformer is considered to have a possibility to stabilize the power system by improving function of fault current limiting. Current limiting behavior functions over critical current flows. There is a possibility that superconducting characteristic may be damaged due to increase in temperature of YBCO tapes. Therefore, we have taken a measure to combine YBCO tape with CuNi tape or Cu Tape. We manufactured model coils using these conductors and conducted the AC over-current tests. The test current was two to seven times larger than the I c of conductor and it was damped with time from its maximum value according to the generation of conductor resistance. We verified the effectiveness of current limiting characteristics. In these tests, the I c of model coil did not degrade. We consider this conductor to be able to withstand AC over-current with the function of current limiting.

  8. Experimental study of structural and optical properties of integrated MOCVD GaAs/Si(001) heterostructures

    Science.gov (United States)

    Seredin, P. V.; Lenshin, A. S.; Zolotukhin, D. S.; Arsentyev, I. N.; Nikolaev, D. N.; Zhabotinskiy, A. V.

    2018-02-01

    This is the first report of the control of the structural and optical functional characteristics of integrated GaAs/Si(001) heterostructures due to the use of misoriented Si(001) substrates with protoporous sublayer. The growth of the epitaxial GaAs layer on silicon substrates without formation of the antiphase domains can be performed on substrates deviating less than 4°-6° from the singular (001) plane or without the use of a transition layer of GaAs nano-columns. Preliminary etching of the silicon substrate with protoporous Si sublayer formation facilitated the acquisition of an epitaxial GaAs film in a single-crystalline state with a considerably less residual strain factor using MOCVD, which has a positive effect on the structural quality of the film. These data are in a good agreement with the results of IR reflection spectroscopy as well as PL and UV spectroscopy. The optical properties of the integrated GaAs/Si (001) heterostructures in the IR and UV spectral regions were also determined by the residual strain value.

  9. High Critical Current in Metal Organic Derived YBCO Films

    Science.gov (United States)

    2010-10-31

    process, particularly in reel-to- reel manufacturing equipment. During Phase I, a “three-step” conversion process was developed to de- convolute the...Task 3. After reaction, the 40-mm web was coated on both sides with a silver layer then slit into eight 4-mm width tapes which were laminated between

  10. Photoluminescence of Mg-doped m-plane GaN grown by MOCVD on bulk GaN substrates

    Energy Technology Data Exchange (ETDEWEB)

    Monemar, Bo [Department of Physics, Chemistry and Biology, Linkoeping University, 581 83 Linkoeping (Sweden); Solid State Physics-The Nanometer Structure Consortium, Lund University, Box 118, 221 00 Lund (Sweden); Paskov, Plamen; Pozina, Galia; Hemmingsson, Carl; Bergman, Peder [Department of Physics, Chemistry and Biology, Linkoeping University, 581 83 Linkoeping (Sweden); Lindgren, David; Samuelson, Lars [Solid State Physics-The Nanometer Structure Consortium, Lund University, Box 118, 221 00 Lund (Sweden); Ni, Xianfeng; Morkoc, Hadis [Department of Electrical and Computer Engineering, Virginia Commonwealth University, Richmond, Virginia 23284-3072 (United States); Paskova, Tanya [Kyma Technologies Inc., Raleigh, North Carolina 27617 (United States); Bi, Zhaoxia; Ohlsson, Jonas [Glo AB, Ideon Science Park, Scheelevaegen 17, 223 70 Lund (Sweden)

    2011-07-15

    Photoluminescence (PL) properties are reported for a set of m-plane GaN films with Mg doping varied from mid 10{sup 18} cm{sup -3} to above 10{sup 20} cm{sup -3}. The samples were grown with MOCVD at reduced pressure on low defect density bulk GaN templates. The sharp line near bandgap bound exciton (BE) spectra observed below 50 K, as well as the broader donor-acceptor pair (DAP) PL bands at 2.9-3.3 eV give evidence of several Mg related acceptors, similar to the case of c-plane GaN. The dependence of the BE spectra on excitation intensity as well as the transient decay behaviour demonstrate acoustic phonon assisted transfer between the acceptor BE states. The lower energy donor-acceptor pair spectra suggest the presence of deep acceptors, in addition to the two main shallower ones at about 0.23 eV. Similar spectra from Mg-doped GaN nanowires (NWs) grown by MOCVD are also briefly discussed. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  11. Heat conduction and thermal stabilization in YBCO tape

    Indian Academy of Sciences (India)

    Yttrium barium copper oxide (YBCO) based 2G/3G tech- nical superconductors ... off-normal scenarios, these superconductors do exceed in an irreversible fashion .... ler G 2007 Factory testing of a 36·5 MW high temperature superconducting ...

  12. Contamination of YBCO bulk superconductors by samarium and ytterbium

    Czech Academy of Sciences Publication Activity Database

    Volochová, D.; Jurek, Karel; Radušovská, M.; Piovarči, S.; Antal, V.; Kováč, J.; Jirsa, Miloš; Diko, P.

    2014-01-01

    Roč. 496, JAN (2014), s. 14-17 ISSN 0921-4534 Institutional support: RVO:68378271 Keywords : YBCO bulk superconductors * critical temperature * critical current density * peak effect Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.942, year: 2014

  13. Fabrication and properties of sub-micrometric YBCO biepitaxial junctions

    Energy Technology Data Exchange (ETDEWEB)

    Stornaiuolo, D; Born, D; Barone, A [CNR-INFM Coherentia, Napoli (Italy); Cedergren, K; Bauch, T; Lombardi, F [MC2 Chalmers University of Technology, Goteborg (Sweden); Rotoli, G [CNISM and Universita dell' Aquila (Italy); Tafuri, F, E-mail: stornaiuolo@na.infh.i [Seconda Universita degli Studi di Napoli, Aversa (Italy)

    2009-03-01

    We report on the fabrication procedure and the transport properties of submicron grain boundary biepitaxial YBCO Josephson junctions. These first results are very encouraging and justify further expectations on improved performances for such types of devices. A reduced and more controlled faceting along the grain boundary interface, for instance, will better preserve intrinsic d-wave effects, and favour the study of fluxons dynamics.

  14. A Thermally Actuated Flux Pump for Energizing YBCO Pucks

    Science.gov (United States)

    2016-05-01

    a Hall sensor with an advertised active area of approximately 1.016 mm diameter supplied by Lakeshore was positioned in the centre of the YBCO as...top and the coldhead (green) along the bottom. The brown colour is the light green of the coldhead and the orange of the dysprosium centre

  15. Modelling of MOCVD reactor: new 3D approach

    International Nuclear Information System (INIS)

    Raj, E; Lisik, Z; Niedzielski, P; Ruta, L; Turczynski, M; Wang, X; Waag, A

    2014-01-01

    The paper presents comparison of two different 3D models of vertical, rotating disc MOCVD reactor used for 3D GaN structure growth. The first one is based on the reactor symmetry, while the second, novel one incorporates only single line of showerhead nozzles. It is shown that both of them can be applied interchangeably regarding the phenomena taking place within the processing area. Moreover, the importance of boundary conditions regarding proper modelling of showerhead cooling and the significance of thermal radiation on temperature field within the modelled structure are presented and analysed. The last phenomenon is erroneously neglected in most of the hitherto studies.

  16. Modelling of MOCVD Reactor: New 3D Approach

    Science.gov (United States)

    Raj, E.; Lisik, Z.; Niedzielski, P.; Ruta, L.; Turczynski, M.; Wang, X.; Waag, A.

    2014-04-01

    The paper presents comparison of two different 3D models of vertical, rotating disc MOCVD reactor used for 3D GaN structure growth. The first one is based on the reactor symmetry, while the second, novel one incorporates only single line of showerhead nozzles. It is shown that both of them can be applied interchangeably regarding the phenomena taking place within the processing area. Moreover, the importance of boundary conditions regarding proper modelling of showerhead cooling and the significance of thermal radiation on temperature field within the modelled structure are presented and analysed. The last phenomenon is erroneously neglected in most of the hitherto studies.

  17. Growth and characterization of high-Tc Y1Ba2Cu3O7-x superconducting thin films by chemical vapor deposition

    International Nuclear Information System (INIS)

    Feng, A.

    1992-01-01

    In chapter I, the current status of high-Tc superconductors (especially Y 1 Ba 2 Cu 3 O 7-x ), their microstructures and their unique physical properties are reviewed. An introduction to the potential and importance of those high-Tc superconductors in practical applications, especially for the application of YBCO thin films in microelectronics, is given. A general description of the common YBCO thin film fabrication and characterization techniques is also presented in this first chapter. Chapter II describes a new CVD process, temperature-controlled chemical vapor deposition (TC-CVD) for the growth of YBCO superconducting thin films on substrates of practical importance, such as sapphire (Al 2 O 3 ) and on substrates of lattice matched perovskite-type single crystals, such as LaAlO 3 . In order to verify the viability of this new CVD process the qualities of YBCO superconducting thin films were examined by various characterization methods, such as resistivity vs. temperature (R vs. T), scanning electron microscopy (SEM), X-ray diffraction (XRD), and magnetic susceptibility (x) measurements. Chapter III deals with the effect of substrate temperature on the properties of YBCO thin films made by TC-CVD. The principle objective of this study is to raise the transition temperature and critical current densities of CVD YBCO superconducting thin films. Understanding the relations between YBCO film growth process and varying substrate temperatures proved to be crucial in reaching this goal. The authors present the characterization results of YBCO thin films produced by different temperature schemes, to illustrate the importance of varying substrate temperature during the film growth. In chapter IV, the Rutherford backscattering (RBS) channeling technique is described. They have used RBS channeling to characterize the epitaxial YBCO thin film's crystallinity and lattice alignment. Transmission electron microscopy studies are also included

  18. Suppression of Mg propagation into subsequent layers grown by MOCVD

    Science.gov (United States)

    Agarwal, Anchal; Tahhan, Maher; Mates, Tom; Keller, Stacia; Mishra, Umesh

    2017-01-01

    Low temperature (LT) flow modulation epitaxy (FME) or "pulsed" growth was successfully used to prevent magnesium from Metalorganic Chemical Vapor Deposition (MOCVD) grown p-GaN:Mg layers riding into subsequently deposited n-type layers. Mg concentration in the subsequent layers was lowered from ˜1 × 1018 cm-3 for a medium temperature growth at 950 °C to ˜1 × 1016 cm-3 for a low temperature growth at 700 °C via FME. The slope of the Mg concentration drop in the 700 °C FME sample was 20 nm/dec—the lowest ever demonstrated by MOCVD. For growth on Mg implanted GaN layers, the drop for a medium temperature regrowth at 950 °C was ˜10 nm/dec compared to >120 nm/dec for a high temperature regrowth at 1150 °C. This drop-rate obtained at 950 °C or lower was maintained even when the growth temperature in the following layers was raised to 1150 °C. A controlled silicon doping series using LT FME was also demonstrated with the lowest and highest achieved doping levels being 5 × 1016 cm-3 and 6 × 1019 cm-3, respectively.

  19. Fabrication and examination of epitaxial HTSC/isolator thin films on sapphire substrates for application in high frequency devices; Herstellung und Untersuchung von epitaktischen HTSL/Isolator-Schichten auf Saphirsubstraten zur Anwendung in HF-Bauelementen

    Energy Technology Data Exchange (ETDEWEB)

    Kittel, H.

    1995-10-01

    The use of high temperature superconductors (HTSC) like YBCO with distinct lower surface resistance compared to normal conductors allows miniaturisation of high frequency (HF) circuits. The object of this work was the fabrication of YBCO thin films on low loss sapphire substrates applicable for stripline devices. To induce epitaxial growth and to avoid chemical reaction at the film-substrate boundary buffer layers were investigated. The examination of the growth properties and especially of the surface impedance has been allotted particular importance. In contrast to CaTiO{sub 3} it was possible to deposit CeO{sub 2}-buffer layers in direct growth up to a thickness of about 30 nm without cracks. The films show all growth properties required and even Laue-oscillations being a feature of high quality growth enabling the determination of film thickness distribution without destruction. The YBCO growth-, transport- and HF-properties meet the ones of YBCO films on standard substrates. A remarkable result is that the mosaic distribution of the CEO film, itself strongly dependend on film thickness, does not influence that of the YBCO film considerably. Rather it changes its shape subsequently due to YBCO deposition. A further particularity in contrast to deposition on standard substrates is the need to adjust the substrate heater tempeature for deposition of YBCO films with thicknesses {>=}300 nm needed for HF application. To demonstrate their usefullness some stripline devices like planar coils and side coupled filters have been fabricated and characterised. (orig.)

  20. Synthesis of in-plane aligned a-axis YBa2Cu3O7-δ thin films

    International Nuclear Information System (INIS)

    Young, K.H.; Sun, J.Z.

    1991-01-01

    We report the successful synthesis of superconducting YBa 2 Cu 3 O 7-δ (YBCO) (100) thin films with alignment of the in-plane c axis. These films were grown on single crystal NdGaO 3 (110) substrates. The twofold symmetry of the substrate surface is believed to lead to anisotropic alignment of the in-plane c axis of the epitaxial YBCO (100) film. X-ray diffraction studies indicate that over 80% of the film grew epitaxially with the YBCO [100] perpendicular to the substrate surface, and YBCO [001] aligned along one pseudo-cubic axis of the NdGaO 3 . The superconductivity onset of the film was measured to be 89 K by ac susceptibility

  1. Buffer free MOCVD growth of GaN on 4H-SiC: Effect of substrate treatments and UV-photoirradiation

    Energy Technology Data Exchange (ETDEWEB)

    Losurdo, Maria; Giangregorio, Maria M.; Bruno, Giovanni [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy); Kim, Tong-Ho; Choi, Soojeong; Brown, April [Department of Electrical and Computer Engineering, Duke University, Durham, NC 27709 (United States)

    2006-05-15

    GaN has been grown directly on the Si-face 4H-SiC(0001) substrates using remote plasma-assisted metalorganic chemical vapour deposition (RP-MOCVD) with UV-light irradiation. The effects of substrate pre-treatments and UV-photoirradiation of the growth surface on GaN nucleation and film morphology are investigated. Optical data from spectroscopic ellipsometry measurements and morphological data show an improvement in nucleation and material quality with UV-light irradiation. (copyright 2006 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  2. Sm-doped CeO{sub 2} single buffer layer for YBCO coated conductors by polymer assisted chemical solution deposition (PACSD) method

    Energy Technology Data Exchange (ETDEWEB)

    Li, G.; Pu, M.H.; Sun, R.P.; Wang, W.T.; Wu, W.; Zhang, X.; Yang, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); Cheng, C.H. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); School of Materials Science and Engineering, University of New South Wales, Sydney, 2052 NSW (Australia); Zhao, Y. [Key Laboratory of Magnetic Levitation Technologies and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu 610031 (China); School of Materials Science and Engineering, University of New South Wales, Sydney, 2052 NSW (Australia)], E-mail: yzhao@home.swjtu.edu.cn

    2008-10-20

    An over 150 nm thick Sm{sub 0.2}Ce{sub 0.8}O{sub 1.9-x} (SCO) single buffer layer has been deposited on bi-axially textured NiW (2 0 0) alloy substrate. Highly in-plane and out-of-plane oriented, dense, smooth and crack free SCO single layer has been obtained via a polymer-assisted chemical solution deposition (PACSD) approach. YBCO thin film has been deposited equally via a PACSD route on the SCO-buffered NiW, the as grown YBCO yielding a sharp transition at T{sub c0} = 87 K as well as J{sub c}(0 T, 77 K) {approx} 1 MA/cm{sup 2}. These results indicates that RE (lanthanides other than Ce) doping may be an effective approach to improve the critical thickness of solution derived CeO{sub 2} film, which renders it a promising candidate as single buffer layer for YBCO coated conductors.

  3. Fabrication of InP-pentacene inorganic-organic hybrid heterojunction using MOCVD grown InP for photodetector application

    Science.gov (United States)

    Sarkar, Kalyan Jyoti; Pal, B.; Banerji, P.

    2018-04-01

    We fabricated inorganic-organic hybrid heterojunction between indium phosphide (InP) and pentacene for photodetector application. InP layer was grown on n-Si substrate by atmospheric pressure metal organic chemical vapour deposition (MOCVD) technique. Morphological properties of InP and pentacene thin film were characterized by atomic force microscopy (AFM). Current-voltage characteristics were investigated in dark and under illumination condition at room temperature. During illumination, different wavelengths of visible and infrared light source were employed to perform the electrical measurement. Enhancement of photocurrent was observed with decreasing in wavelength of incident photo radiation. Ideality factor was found to be 1.92. High rectification ratio of 225 was found at ± 3 V in presence of infrared light source. This study provides new insights of inorganic-organic hybrid heterojunction for broadband photoresponse in visible to near infrared (IR) region under low reverse bias condition.

  4. Study of the inhomogeneity of critical current under in-situ tensile stress for YBCO tape

    Science.gov (United States)

    Zhu, Y. P.; Chen, W.; Zhang, H. Y.; Liu, L. Y.; Pan, X. F.; Yang, X. S.; Zhao, Y.

    2018-07-01

    A Hall sensor system was used to measure the local critical current of YBCO tape with high spatial resolution under in-situ tensile stress. The hot spot generation and minimum quench energy of YBCO tape, which depended on the local critical current, was calculated through the thermoelectric coupling model. With the increase in tensile stress, the cracks which have different dimensions and critical current degradation arose more frequently and lowered the thermal stability of the YBCO tape.

  5. Multiseeding with (100)/(100) Grain Junctions in Top Seeded Melt Growth Processed YBCO Superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Kim, C.J.; Gee, Y.A.; Hong, G.W. [Korea Atomic Energy Research Institute, Taejon (Korea); Kim, H.J.; Joo, J.H. [Sungkyunkwan University, Suwon (Korea); Han, S.C.; Han, Y.H.; Sung, T.H.; Kim, S.J. [Korea Electric Power Research Institute, Taejon (Korea)

    2000-06-01

    Multiseeding with (100)/(100) grain junctions of top-seeded melt growth (TSMG) processed YBCO superconductors was studied. Multiple seeding shortened the processing time for the fabrication of TSMG-processed YBCO superconductors. The relationship among the number of seeds, the levitation forces and the trapped magnetic fields of the TSMG-processed YBCO samples is reported. The characteristic of the (100)/(100) grain junction is discussed in terms of a wetting angle of a melt. (author). 25 refs., 7 figs.

  6. Microstructure Characteristics of High Lift Factor MOCVD REBCO Coated Conductors With High Zr Content

    Energy Technology Data Exchange (ETDEWEB)

    Galstyan, E; Gharahcheshmeh, MH; Delgado, L; Xu, AX; Majkic, G; Selvamanickam, V

    2015-06-01

    We report the microstructural characteristics of high levels of Zr-added REBa2Cu3O7-x (RE = Gd, Y rare earth) coated conductors fabricated by Metal Organic Chemical Vapor Deposition (MOCVD). The enhancements of the lift factor defined as a ratio of the in-field (3 T, B parallel to c-axis) critical current density (J(c)) at 30 K and self-field J(c) at 77 K have been achieved for Zr addition levels of 20 and 25 mol% via optimization of deposition parameters. The presence of strong flux pinning is attributed to the aligned nanocolumns of BaZrO3 and nanoprecipitates embedded in REBa2Cu3O7-x matrix with good crystal quality. A high density of BZO nanorods with a typical size 6-8 nm and spacing of 20 nm has been observed. Moreover, the high Zr content was found to induce a high density of intrinsic defects, including stacking faults and dislocations. The correlation between in-field performance along the c-axis and microstructure of (Gd, Y) BCO film with a high level of Zr addition is discussed.

  7. Structural and superconducting properties of (Y,Gd)Ba2Cu3O7-δ grown by MOCVD on samarium zirconate buffered IBAD-MgO

    International Nuclear Information System (INIS)

    Stan, L; Holesinger, T G; Maiorov, B; Feldmann, D M; Usov, I O; DePaula, R F; Civale, L; Foltyn, S R; Jia, Q X; Chen, Y; Selvamanickam, V

    2008-01-01

    Textured samarium zirconate (SZO) films have been grown by reactive cosputtering directly on an ion beam assisted deposited (IBAD) MgO template, without an intermediate homoepitaxial MgO layer. The subsequent growth of 0.9 μm thick (Y,Gd)Ba 2 Cu 3 O 7-δ ((Y, Gd)BCO) films by metal organic chemical vapor deposition (MOCVD) yielded well textured films with a full width at half maximum of 1.9 0 and 3.4 0 for the out-of-plane and in-plane texture, respectively. Microstructural characterizations of the SZO buffered samples revealed clean interfaces. This indicates that the SZO not only provides a diffusion barrier, but also functions as a buffer for (Y, Gd)BCO grown by MOCVD. The achievement of self-field critical current densities (J c ) of over 2 MA cm -2 at 75.5 K is another proof of the effectiveness of SZO as a buffer on the IBAD-MgO template. The in-field measurements revealed an asymmetric angular dependence of J c and a shift of the ab-plane maxima due to the tilted nature of the template and (Y,Gd) 2 O 3 particles existing in the (Y, Gd)BCO matrix. The present results are especially important because they demonstrate that high temperature superconducting coated conductors with simpler architecture can be fabricated using commercially viable processes

  8. Impact of oxygen precursor flow on the forward bias behavior of MOCVD-Al2O3 dielectrics grown on GaN

    Science.gov (United States)

    Chan, Silvia H.; Bisi, Davide; Liu, Xiang; Yeluri, Ramya; Tahhan, Maher; Keller, Stacia; DenBaars, Steven P.; Meneghini, Matteo; Mishra, Umesh K.

    2017-11-01

    This paper investigates the effects of the oxygen precursor flow supplied during metalorganic chemical vapor deposition (MOCVD) of Al2O3 films on the forward bias behavior of Al2O3/GaN metal-oxide-semiconductor capacitors. The low oxygen flow (100 sccm) delivered during the in situ growth of Al2O3 on GaN resulted in films that exhibited a stable capacitance under forward stress, a lower density of stress-generated negative fixed charges, and a higher dielectric breakdown strength compared to Al2O3 films grown under high oxygen flow (480 sccm). The low oxygen grown Al2O3 dielectrics exhibited lower gate current transients in stress/recovery measurements, providing evidence of a reduced density of trap states near the GaN conduction band and an enhanced robustness under accumulated gate stress. This work reveals oxygen flow variance in MOCVD to be a strategy for controlling the dielectric properties and performance.

  9. Recent results in characterization of melt-grown and quench-melt- grown YBCO superconductors

    International Nuclear Information System (INIS)

    Balachandran, U.; Poeppel, R.B.; Gangopadhyay, A.K.

    1992-02-01

    From the standpoint of applications, melt-grown (MG) and quench-melt-grown (QMG) bulk YBCO superconductors are of considerable interest. In this paper, we studied the intragranular critical current density (J c ), the apparent pinning potential (U o ), and the irreversibility temperature (T irr ) of MG and QMG samples and compared the results to those for conventionally sintered YBCO. A systematic increase in U o and a slower drop in J c with temperature indicate a systematic improvement in flux-pinning properties in progressing from the sintered YBCO to QMG and MG samples. Weaker pinning is observed in the QMG YBCO than in the MG samples

  10. Development of an YBCO coil with SSTC conductors for high field application

    Science.gov (United States)

    Shi, Y.; Liu, H. J.; Liu, F.; Tan, Y. F.; Jin, H.; Yu, M.; Lei, L.; Guo, L.; Hong, Z. Y.

    2018-07-01

    With the continuous reduction of the production costs and improvement of the transport performance, YBCO coated conductor is the most promising candidate for the high field magnet application due to its high irreversibility field and strong mechanical properties. Presently a stable production capacity of the YBCO conductors has been achieved by Shanghai Superconducting Technology Co., Ltd (SSTC) in China. Therefore, the demand in high field application with YBCO conductors is growing in China. This paper describes the design, fabrication and preliminary experiment of a solenoid coil with YBCO conductors supplied by SSTC to validate the possibility of high field application. Four same double pancakes were manufactured and assembled for the YBCO coil where the outer diameter and height was 54.3 and 48 mm respectively to match the dimensional limitation of the 14 T background magnets. The critical current (Ic) of YBCO conductors was obtained by measuring as a function of the applied field perpendicular to the YBCO conductor surface which provides the necessary input parameters for preliminary performance evaluation of the coil. Finally the preliminary test and discussion at 77 and 4.2 K were carried out. The consistency of four double pancakes Ic was achieved. The measured results indicate that the fabrication technology of HTS coil is reliable which gives the conference for the in-field test in high field application. This YBCO coil is the first demonstration of the SSTC YBCO coated conductors.

  11. FLUX PINNING EFFECTS IN Ag-DOPED YBCO (123 SUPERCONDUCTOR

    Directory of Open Access Journals (Sweden)

    Madelen Pérez

    2010-07-01

    Full Text Available Polycrystalline samples of Ag+-doped YBCO (123 (YBa2 (Cu1-xAgx3O7-δwith 0≤x≤0.3 were produced by solid state reaction method. The Ag- doped YBCO samples showed higher critical current densities (Jc with a Jc maximum for samples doped with x=0.05. This behavior can be assigned to an increase of pinning forces. The irreversibility temperature (Tirr, also increased in doped samples as a function of Ag content, with the highest temperature for the sample doped with x=0.05, wich correlates well with the observed Jc increasing. However, samples doped with x>0.05 displayed a decreasing of electrical properties (less Tirr, less Jc, etc. atributed to an excess of Ag in the grain boundaries which, reduces the grain sizes and increases the number of weak- links.

  12. Oxygenation and cracking in melt-textured YBCO bulk superconductors

    International Nuclear Information System (INIS)

    Kracunovska, S; Diko, P; Litzkendorf, D; Habisreuther, T; Bierlich, J; Gawalek, W

    2005-01-01

    Microstructural changes during the oxygenation of YBCO bulks were studied. It was shown that a lower temperature of oxygenation leads to the formation of a denser structure of a/b- and c-macrocracks and causes faster and more homogeneous oxygenation of the sample. The opening of created macrocracks is the way in which the macroscopic stresses induced by macroscopic 211 particle concentration inhomogeneity are released. This is very important, because it prevents the formation of fatal c-macrocracks, which divide the sample into more domains, during cooling from oxygenation temperature or during sample performance. Oxygenation with a multistage programme causes the oxygen concentration difference between the oxygenated layer and the tetragonal matrix to be smaller, and consequently fewer macrocracks are formed. This leads to the prolongation of oxygenation times for full oxygenation and to the insufficient release of macroscopic stresses. 211 low concentration regions and pores also enhance the oxygenation rate of YBCO bulks

  13. Thermoelectric power of the Ni and Cd substituted YBCO system

    International Nuclear Information System (INIS)

    Mukherjee, C.D.; Ranganathan, R.; Raychaudhuri, A.K.; Chatterjee, N.

    1989-01-01

    The thermoelectric power behaviour in the range between 250 K and the superconducting transition temperature T c of YBa 2 Cu 3-x A x O 7-y (where A = Ni or Cd and x = 0.2 and 0.4) samples has been examined. The normalized resistance and thermopower of substituted samples as functions of temperature are plotted and discussed. It was concluded that nickel has a slight positive role in causing overall thermopower generation in the YBCO system

  14. Applications of YBCO melt textured bulks in Maglev technology

    International Nuclear Information System (INIS)

    Zhao, Y.; Wang, J.S.; Wang, S.Y.; Ren, Z.Y.; Song, H.H.; Wang, X.R.; Cheng, C.H.

    2004-01-01

    In this paper we report the present status and progress of HTS Maglev project undertaken at the Southwest Jiaotong University. The efforts and results towards solving the material-related issues in HTS Maglev system are emphasized, including the levitation and guidance forces, the magnetic and thermal stabilities related to the ac loss of YBCO superconducting material during a high speed movement, and the low stiffness of HTS Maglev system

  15. Observation of Sinusoidal Voltage Behaviour in Silver Doped YBCO

    Science.gov (United States)

    Altinkok, Atilgan; Olutas, Murat; Kilic, Kivilcim; Kilic, Atilla

    The influence of bi-directional square wave (BSW) current was investigated on the evolution of the V - t curves at different periods (P) , temperatures and external magnetic fields. It was observed that slow transport relaxation measurements result in regular sinusoidal voltage oscillations which were discussed mainly in terms of the dynamic competition between pinning and depinning.The symmetry in the voltage oscillations was attributed to the elastic coupling between the flux lines and the pinning centers along grain boundaries and partly inside the grains. This case was also correlated to the equality between flux entry and exit along the YBCO/Ag sample during regular oscillations. It was shown that the voltage oscillations can be described well by an empirical expression V (t) sin(wt + φ) . We found that the phase angle φgenerally takes different values for the repetitive oscillations. Fast Fourier Transform analysis of the V - t oscillations showed that the oscillation period is comparable to that (PI) of the BSW current. This finding suggests a physical mechanism associated with charge density waves (CDWs), and, indeed, the weakly pinned flux line system in YBCO/Ag resembles the general behavior of CDWs. At certain values of PI, amplitude of BSW current, H and T, the YBCO/Ag sample behaves like a double-integrator, since it converts the BSW current to sinusoidal voltage oscillations in time.

  16. Simulation of YBCO Tape and Coils in HTS Maglev System

    Directory of Open Access Journals (Sweden)

    Song Mengxiao

    2017-01-01

    Full Text Available In the process of running high temperature superconducting maglev train, the AC(Alternating Current loss of superconducting coil is directly related to its safe operation and operating cost. In this paper, the simulation model was built based on the finite element software COMSOL Multiphysics, and mainly simulated and calculated the AC losses of YBCO(Yttrium Barium Copper Oxide tape and coils. In this model, as the solving object, the singular and infinite long YBCO tape and coils model was solved with H-formulation and the nonlinear characteristic (E-J constitutive law and anisotrophy (B-J characteristic were taken into consideration as the theoretical foundation. Then on the basis of the model under maglev suspension system, AC losses under different amplitude and frequence AC currents were calculated. The results shows that under different frequencies and dynamic components, the local maximum AC loss of YBCO tape and coils occurs when the steady-state DC(Direct Current current is 30A. Then comparing with old maglev suspension system, the new system can greatly reduce the energy consumption and the material cost.

  17. Investigation of (Y,Gd)Ba2Cu3O7-x grown by MOCVD on a simplified IBAD MgO template

    International Nuclear Information System (INIS)

    Stan, L; Holesinger, T G; Maiorov, B; Civale, L; DePaula, R F; Jia, Q X; Chen, Y; Xiong, X; Selvamanickam, V

    2010-01-01

    We have used an ion beam sputtered Y 2 O 3 -Al 2 O 3 (YALO) composite to simplify the architecture of high temperature superconducting (HTS) coated conductors (CCs) based on a IBAD MgO template. By implementing YALO, we have reduced the total non-superconducting layers between the polycrystalline metal substrate and the superconducting film from five (the standard architecture) to four. Well textured (Y,Gd)Ba 2 Cu 3 O 7-x ((Y, Gd)BCO) films have been successfully grown by MOCVD on this simplified template. The microstructural characterization revealed that all layers are continuous and uniform with sharp and clean interfaces. Additionally, the YALO maintained its amorphous nature after the deposition of the superconductive layer, which is a plus in terms of its efficiency as a diffusion barrier. The achievement of a self-field critical current of 230 A cm -1 at 75.5 K is another proof of the effectiveness of YALO as a diffusion barrier and nucleation seed for the MgO. The transport properties under an applied magnetic field of MOCVD grown (Y, Gd)BCO on LMO buffered MgO/YALO/Ni-alloy are comparable with those of (Y, Gd)BCO on a standard architecture, thus demonstrating good compatibility between the simplified template with the MOCVD grown (Y, Gd)BCO. The use of a single composite YALO layer instead of individual layers of Y 2 O 3 and Al 2 O 3 for the large scale fabrication of HTS CCs based on IBAD MgO provides advantages such as potentially reduced cost due to the reduced number of fabrication steps.

  18. Investigation of (Y,Gd)Ba{sub 2}Cu{sub 3}O{sub 7-x} grown by MOCVD on a simplified IBAD MgO template

    Energy Technology Data Exchange (ETDEWEB)

    Stan, L; Holesinger, T G; Maiorov, B; Civale, L; DePaula, R F; Jia, Q X [Los Alamos National Laboratory, PO Box 1663, Los Alamos, NM 87545 (United States); Chen, Y [SuperPower, Incorporated, 450 Duane Avenue, Schenectady, NY 12304 (United States); Xiong, X; Selvamanickam, V [Mechanical Engineering Department, University of Houston, Houston, TX 77204-4006 (United States)

    2010-01-15

    We have used an ion beam sputtered Y{sub 2}O{sub 3}-Al{sub 2}O{sub 3} (YALO) composite to simplify the architecture of high temperature superconducting (HTS) coated conductors (CCs) based on a IBAD MgO template. By implementing YALO, we have reduced the total non-superconducting layers between the polycrystalline metal substrate and the superconducting film from five (the standard architecture) to four. Well textured (Y,Gd)Ba{sub 2}Cu{sub 3}O{sub 7-x} ((Y, Gd)BCO) films have been successfully grown by MOCVD on this simplified template. The microstructural characterization revealed that all layers are continuous and uniform with sharp and clean interfaces. Additionally, the YALO maintained its amorphous nature after the deposition of the superconductive layer, which is a plus in terms of its efficiency as a diffusion barrier. The achievement of a self-field critical current of 230 A cm{sup -1} at 75.5 K is another proof of the effectiveness of YALO as a diffusion barrier and nucleation seed for the MgO. The transport properties under an applied magnetic field of MOCVD grown (Y, Gd)BCO on LMO buffered MgO/YALO/Ni-alloy are comparable with those of (Y, Gd)BCO on a standard architecture, thus demonstrating good compatibility between the simplified template with the MOCVD grown (Y, Gd)BCO. The use of a single composite YALO layer instead of individual layers of Y{sub 2}O{sub 3} and Al{sub 2}O{sub 3} for the large scale fabrication of HTS CCs based on IBAD MgO provides advantages such as potentially reduced cost due to the reduced number of fabrication steps.

  19. Quantification of oxygen and carbon in high Tc superconducting films by (α,α) elastic resonance technique

    International Nuclear Information System (INIS)

    Vizkelethy, G.; Revesz, P.

    1993-01-01

    The quantification of oxygen and carbon in high-temperature (T c ) superconducting oxide thin films was made by employing elastic resonance in He backscattering analysis. A method combining the oxygen resonance technique and channeling was presented for measuring the nature of the oxygen disorder near the surface and the interface in a YBCO superconducting film grown on an MgO substrate. The oxygen resonance technique was used to quantify the oxygen profiling in the metal/YBCO contacts, showing that Zr and Nb act as sinks to oxygen from YBCO films and are oxidized in the forms Zr/ZrO 2 /YBCO/MgO and Nb 0.2 O/YBCO/MgO after annealing in a vacuum at 350 o C. We combined the carbon and oxygen resonances to determine the carbon contamination and oxygen concentration changes on the YBCO surface after coating and baking the photoresist. Residual carbon on the surface and a thin layer of oxygen depletion near the YBCO surface have been observed. The residual carbon in Bi 2 Sr 2 CaCu 2 O 8 films made by the decomposition of metallo-organic precursors was quantified using carbon resonance. (author)

  20. Microstructure of epitaxial YBa2Cu3O7-x thin films grown on LaAlO3 (001)

    International Nuclear Information System (INIS)

    Hsieh, Y.; Siegal, M.P.; Hull, R.; Phillips, J.M.

    1990-01-01

    We report a microstructural investigation of the epitaxial growth of YBa 2 Cu 3 O 7-x (YBCO) thin films on LaAlO 3 (001) substrates using transmission electron microscopy (TEM). Epitaxial films grow with two distinct modes: c epitaxy (YBCO) single crystal with the c (axis normal to the surface and a epitaxy (YBCO) single crystal with the c axis in the interfacial plane), where c epitaxy is the dominant mode grown in all samples 35--200 nm thick. In 35 nm YBCO films annealed at 850 degree C, 97±1% of the surface area is covered by c epitaxy with embedded anisotropic a-epitaxial grains. Quantitative analysis reveals the effect of film thickness and annealing temperature on the density, grain sizes, areal coverages, and anisotropic growth of a epitaxy

  1. Effects of process parameters on sheet resistance uniformity of fluorine-doped tin oxide thin films

    Science.gov (United States)

    Hudaya, Chairul; Park, Ji Hun; Lee, Joong Kee

    2012-01-01

    An alternative indium-free material for transparent conducting oxides of fluorine-doped tin oxide [FTO] thin films deposited on polyethylene terephthalate [PET] was prepared by electron cyclotron resonance - metal organic chemical vapor deposition [ECR-MOCVD]. One of the essential issues regarding metal oxide film deposition is the sheet resistance uniformity of the film. Variations in process parameters, in this case, working and bubbler pressures of ECR-MOCVD, can lead to a change in resistance uniformity. Both the optical transmittance and electrical resistance uniformity of FTO film-coated PET were investigated. The result shows that sheet resistance uniformity and the transmittance of the film are affected significantly by the changes in bubbler pressure but are less influenced by the working pressure of the ECR-MOCVD system.

  2. RBS and ion channeling studies of Ag-doped YBa2Cu3O7-δ targets and films

    International Nuclear Information System (INIS)

    Li Yupu; Liu, J.R.; Cui, X.T.; Chu, W.K.

    1998-01-01

    The location of Ag in Ag-doped YBa 2 Cu 3 O 7-δ (YBCO) films and other high-T c materials (such as Ag-doped BiSrCaCuO films and Ag-sheathed textured BiSrCaCuO wires) is a very important issue for improving high-T c materials. In this work, laser ablated and DC magnetron sputtered YBCO films on (100) LaAlO 3 and (100) SrTiO 3 were prepared from sintered Ag-YBCO composite targets (nominally containing 5 wt% Ag) and studied by Rutherford backscattering spectrometry (RBS) and ion channeling techniques using 2.0 MeV 4 He + and 7 Li + beams. We have found that the Ag-YBCO targets contain about 3 wt% Ag and most of the retained Ag atoms form some small size Ag precipitates with a typical size smaller than a few microns. We have demonstrated that in very good single crystalline YBCO films, the percentage of retained Ag in substitutional sites can be estimated by ion channeling technique. For example, we have found that about 1.2 wt% Ag atoms remain in the laser ablated Ag-doped films prepared from the Ag-YBCO target and about two-thirds of the retained Ag atoms occupy substitutional sites. The sputtered films contain less retained Ag atoms since the deposition temperature is higher and deposition time is longer than those for laser ablated films. (orig.)

  3. Novel method for fabrication of integrated resistors on bilayer Ag/YBa2Cu3O7 films using Ni implantation

    International Nuclear Information System (INIS)

    LaGraff, J.R.; Chan, H.; Murduck, J.M.; Hong, S.H.; Ma, Q.Y.

    1997-01-01

    A novel ion implantation method is described for fabricating low inductance integrated resistors on Ag/YBa 2 Cu 3 O 7 (YBCO) bilayer thin films. Parallel high and low value resistors were simultaneously formed by patterning bilayer films into 10-μm-wide lines, then masking and implanting with Ni to selectively inhibit superconductivity in YBCO. Low value resistors (<1Ω/sq) were formed at 77 K as the supercurrent bypassed the Ni-doped nonsuperconducting YBCO and was shunted through the overlying low resistivity Ag metal. High value resistors (20 - 140 Ω/sq) were formed by removing Ag from above the implanted YBCO forcing the current through the implanted YBCO region. The sheet resistance of both types of resistors was found to increase systematically with increasing Ni implant energy. copyright 1997 American Institute of Physics

  4. Irreversible properties of YBCO coated conductors

    International Nuclear Information System (INIS)

    Vostner, A.

    2001-02-01

    Over the past few years substantial efforts were made to optimize the fabrication techniques of various high temperature superconductors for commercial applications. In addition to Bi-2223 tapes, Y-123 coated conductors have the potential for large-scale production and are considered as the second generation of superconducting 'wires' for high current applications. This work reports on magnetic and transport current investigations of Y-123 thick films deposited on either single crystalline substrates by liquid phase epitaxy (LPE) or on metallic substrates by pulsed laser deposition (PLD). At the beginning, a short introduction of the general idea of a coated conductor and of the different production techniques is presented, followed by a description of the different experimental set-ups and the evaluation methods. The main part starts with the results obtained from SQUID magnetometry and ac-susceptibility measurements including the transition temperatures T c , the field dependence of the magnetic critical current densities and the irreversibility lines. In addition, some issues concerning the granular structure and the inter- and intragranular current distribution of the superconducting films are discussed. The investigations by transport currents are focused on the behavior of the application relevant irreversible parameters. These are the angular and the field dependence of the critical transport current densities at 77 and 60 K, as well as the temperature dependence of the irreversibility fields up to 6 T. To gain more insight into the defect structure of the films, neutron irradiation studies were performed on some samples. The introduction of these artificial pinning centers causes large enhancements of the magnetic J c in LPE specimens for the field parallel to the c-axis (H//c) at higher temperatures and magnetic fields. The granular structure of the samples does not change up to the highest neutron fluences. However, the enhancements of the transport J c

  5. Protection of the 6 T YBCO insert in the 13 T Nb$_{3}$Sn Fresca II dipole

    CERN Document Server

    Stenvall, A.; Fazilleau, Ph.; Devaux, M.; Durante, M.; Lecrevisse, T.; Rey, J. -M.; Fleiter, J.; Sorbi, M.; Volpini, G.; Tixador, P.

    2013-01-01

    In the EuCARD project, we aim to construct a dipole magnet in YBCO producing 6 T in the background field of a 13 T Nb$_{3}$Sn dipole FRESCA II. This paper reviews the quench analysis and protection of the YBCO coil. In addition, a recommendation for the protection system of the YBCO coil is presented.

  6. Bi axially textured YBCO coated tape prepared using dynamic magnetic grain alignment

    International Nuclear Information System (INIS)

    Genoud, Jean-Yves; Quinton, William

    1999-01-01

    A new magnetic grain alignment technique has been applied to produce bi axially aligned YBCO coated tapes. A bi axially aligned dispersion of orthorhombic Y 2 Ba 4 Cu 7 O 15 (Y-247) powder was settled on un textured silver substrates. The Y-247 tapes were then melt processed to achieve high critical current YBa 2 Cu 3 O 7 (Y-123) tapes with CuO as a secondary phase. The biaxial alignment is preserved after the densification process and a clear enhancement of J c relative to identically prepared un textured or uniaxially textured samples is obtained. Critical current densities of up to 5000 A cm -2 at 77 K in self-field and 1500 A cm -2 in 0.5 T magnetic field at 65 K were obtained in films from 20 to 40 μm thick. Problems were experienced in achieving fully densified thick films while retaining biaxial texture. The initial grain size distribution was found to have a major influence on the final microstructure. Provided significant improvements in J c can be obtained this method offers an alternative to coated tape processes based on epitaxial growth which has the advantage that it does not require textured substrates. The biaxial alignment technique described here intrinsically acts on the bulk material rather than at surfaces. This offers the possibility of texturing without thickness limitations. (author)

  7. Solderability study of RABiTS-based YBCO coated conductors

    International Nuclear Information System (INIS)

    Zhang Yifei; Duckworth, Robert C.; Ha, Tam T.; Gouge, Michael J.

    2011-01-01

    Study examines the implication of solder and flux selection in YBCO splice joints. Focus is on commercially available RABiTS-based YBCO coated conductors. Solderability varied with solder and flux for three different stabilizations tested. Resistivity of stabilizer was dominant factor in splice joint resistance. Solder materials affected splice joint resistance when solderability was poor. The solderability of commercially available YBa 2 Cu 3 O 7-x (YBCO) coated conductors that were made from Rolling Assisted Biaxially Textured Substrates (RABiTS)-based templates was studied. The coated conductors, also known as second-generation (2G) high temperature superconductor (HTS) wires (in the geometry of flat tapes about 4 mm wide), were laminated with copper, brass, or stainless steel strips as stabilizers. To understand the factors that influence their solderability, surface profilometry and scanning electron microscopy were used to characterize the wire surfaces. The solderability of three solders, 52In48Sn, 67Bi33In, and 100In (wt.%), was evaluated using a standard test (IPC/ECA J-STD-002) and with two different commercial fluxes. It was found that the solderability varied with the solder and flux but the three different wires showed similar solderability for a fixed combination of solder and flux. Solder joints of the 2G wires were fabricated using the tools and the procedures recommended by the HTS wire manufacturer. The solder joints were made in a lap-joint geometry and with the superconducting sides of the two wires face-to-face. The electrical resistances of the solder joints were measured at 77 K, and the results were analyzed to qualify the soldering materials and evaluate the soldering process. It was concluded that although the selection of soldering materials affected the resistance of a solder joint, the resistivity of the stabilizer was the dominant factor.

  8. Growth and domain structure of YBa2Cu3Ox films on neodymium gallate substrates with deviation of surface normal from [110] NdGaO3

    International Nuclear Information System (INIS)

    Bdikin, I.K.; Mozhaev, P.B.; Ovsyannikov, G.A.; Komissinskij, F.V.; Kotelyanskij, I.M.; Raksha, E.I.

    2001-01-01

    One investigated into growth, crystalline structure and electrophysical properties of YBa 2 Cu 3 O x (YBCO) epitaxial films grown on NdGaO 3 (NGO) substrates with substrate surface normal deviation from [110] by 5-26.6 deg angle around [001] with CeO 2 epitaxial sublayer or without it. Orientation of YBCO epitaxial films grown at these substrates is shown to be governed by occurrence of symmetrically equipment directions in substrates and in CeO 2 layer, as well as, by film precipitation rate. At precipitation high rate YBCO films on CeO 2 sublayer grow in [001] orientation independently of orientation of substrate and sublayer. One determined that at increase of substrate plane deviation angle from (110) NGO twinning of one or of both twin complexes in YBCO might be suppressed [ru

  9. A small Maglev car model using YBCO bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Yang, W M [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China); Zhou, L [Northwest Institute for Nonferrous Metal Research, PO Box 51, Xi' an, Shaanxi 710016 (China); Yong, Feng [Northwest Institute for Nonferrous Metal Research, PO Box 51, Xi' an, Shaanxi 710016 (China); Zhang, P X [Northwest Institute for Nonferrous Metal Research, PO Box 51, Xi' an, Shaanxi 710016 (China); Chao, X X [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China); Bian, X B [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China); Zhu, S H [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China); Wu, X L [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China); Liu, P [Department of Physics, Shaanxi Normal University, Xi' an, Shaanxi 710016 (China)

    2006-07-15

    Models of two small Maglev cars have been made. The track was paved with NdFeB magnets. The arrangement of the magnets made it easy to get a uniform magnetic field distribution along the length of the track and a magnetic field gradient in the lateral direction. When the car with YBCO bulk superconductors was field cooled to LN{sub 2} temperature at a certain distance above the track, the car could be automatically levitated over the track and moved along the track without any obvious friction. The model can be used to demonstrate the Meissner effect and a fast transportation system to students and adults.

  10. Preparing superconducting nanopowder based YBCO/Ag tapes

    DEFF Research Database (Denmark)

    Paturi, P.; Raittila, J.; Grivel, J.C.

    2002-01-01

    YBCO nanopowder consisting of 1-3 nm thick and 40 nm wide particles has been used to make silver clad superconducting tapes. After annealing in nitrogen at 945 degreesC for 10 h a critical current of 5.02 A (3300 A/cm(2)) was attained, Annealing in mixed atmosphere of oxygen and nitrogen was also...... carried out and this procedure produced tapes with a critical current of 2.83 A (2200 A/cm(2)). These tapes show very good characteristics in magnetic fields. (C) 2002 Elsevier Science B.V. All rights reserved....

  11. A small Maglev car model using YBCO bulk superconductors

    International Nuclear Information System (INIS)

    Yang, W M; Zhou, L; Yong, Feng; Zhang, P X; Chao, X X; Bian, X B; Zhu, S H; Wu, X L; Liu, P

    2006-01-01

    Models of two small Maglev cars have been made. The track was paved with NdFeB magnets. The arrangement of the magnets made it easy to get a uniform magnetic field distribution along the length of the track and a magnetic field gradient in the lateral direction. When the car with YBCO bulk superconductors was field cooled to LN 2 temperature at a certain distance above the track, the car could be automatically levitated over the track and moved along the track without any obvious friction. The model can be used to demonstrate the Meissner effect and a fast transportation system to students and adults

  12. Magnetic response of superconducting mesoscopic-size YBCO powder

    Energy Technology Data Exchange (ETDEWEB)

    Deimling, C.V. [Grupo de Supercondutividade e Magnetismo, Departamento de Fisica, Universidade Federal de Sao Carlos, Sao Carlos, SP (Brazil)], E-mail: cesard@df.ufscar.br; Motta, M.; Lisboa-Filho, P.N. [Laboratorio de Materiais Supercondutores, Departamento de Fisica, Universidade Estadual Paulista, Bauru, SP Brazil (Brazil); Ortiz, W.A. [Grupo de Supercondutividade e Magnetismo, Departamento de Fisica, Universidade Federal de Sao Carlos, Sao Carlos, SP (Brazil)

    2008-07-15

    In this work it is reported the magnetic behavior of submicron and mesoscopic-size superconducting YBCO powders, prepared by a modified polymeric precursors method. The grain size and microstructure were analyzed using scanning electron microscopy (SEM). Measurements of magnetization and AC-susceptibility as a function of temperature were performed with a quantum design SQUID magnetometer. Our results indicated significant differences on the magnetic propreties, in connection with the calcination temperature and the pressure used to pelletize the samples. This contribution is part of an effort to study vortex dynamics and magnetic properties of submicron and mesoscopic-size superconducting samples.

  13. Harmonic response of coupled and uncoupled granular YBCO

    International Nuclear Information System (INIS)

    Torralba, Maria Veronica S; Sarmago, Roland V

    2004-01-01

    The harmonic responses of granular YBCO were obtained via mutual inductance measurements. Two samples, one with and another without intergranular coupling, were investigated in terms of the harmonic components of magnetization at various field amplitudes and frequencies. By comparing the behaviour of the features in the harmonics to that of the peaks in the fundamental response, we explicitly identified which features in the harmonics originate from intragranular harmonic generation and which arise due to a contribution of intergranular coupling. Harmonic responses were obtained despite the absence of vortices and even harmonics were detected in a purely AC magnetic field

  14. LaNiO3 buffer layers for high critical current density YBa2Cu3O7-δ and Tl2Ba2CaCu2O8-δ films

    International Nuclear Information System (INIS)

    Carlson, C.M.; Parilla, P.A.; Siegal, M.P.; Ginley, D.S.; Wang, Y.; Blaugher, R.D.; Price, J.C.; Overmyer, D.L.; Venturini, E.L.

    1999-01-01

    We demonstrate high critical current density superconducting films of YBa 2 Cu 3 O 7-δ (YBCO) and Tl 2 Ba 2 CaCu 2 O 8-δ (Tl-2212) using LaNiO 3 (LNO) buffer layers. YBCO films grown on an LNO buffer layer have only a slightly lower J c (5 K, H=0) than films grown directly on a bare LaAlO 3 substrate. YBCO films grown on LNO buffer layers exhibit minor microstructural disorder and enhanced flux pinning. LNO-buffered Tl-2212 samples show large reductions in J c at all temperatures and fields compared to those grown on bare LaAlO 3 , correlating to both a-axis grain and nonsuperconducting phase formation. LNO could be a promising buffer layer for both YBCO and Tl-based superconducting films in coated conductor applications. copyright 1999 American Institute of Physics

  15. LaNiO3 Buffer Layers for High Critical Current Density YBa2Cu3O7δ and Tl2Ba2CaCu2O8δ Films

    International Nuclear Information System (INIS)

    Carlson, C.M.; Parilla, P.A.; Siegal, M.P.; Ginley, D.S.; Wang, Y.-T.; Blaugher, R.D.; Price, J.C.; Overmyer, D.L.; Venturini, E.L.

    1999-01-01

    We demonstrate high critical current density superconducting films of YBa 2 Cu 3 O 7-δ (YBCO) and Tl 2 Ba 2 CaCu 2 O 8-δ (Tl-2212) using LaNiO 3 (LNO) buffer layers. YBCO films grown on an LNO buffer layer have only a slightly lower J c (5K, H=0) than films grown directly on a bare LaAlO 3 substrate. It is noteworthy that YBCO films grown on LNO buffer layers exhibit minor microstructural disorder and enhanced flux pinning. LNO-buffered Tl-2212 samples show large reductions in J c at all temperatures and fields compared to those grown on bare LaAlO 3 , correlating to both a-axis grain and nonsuperconducting phase formation. With additional optimization, LNO could be a promising buffer layer for both YBCO and Tl-based superconducting films, perhaps ideally suited for coated conductor applications

  16. Effect of BaZrO3/Ag hybrid doping to the microstructure and performance of fluorine-free MOD method derived YBa2Cu3O7−x superconducting thin films

    DEFF Research Database (Denmark)

    Tang, Xiao; Yue, Zhao; Wu, W.

    2015-01-01

    It is known that BaZrO3 and Ag can improve the magnetic and transport performance of YBCO thin film through totally disparate ways. BaZrO3 plays the role of flux pinning centers and Ag improves the transparency of the YBCO grain boundaries. However, similar research is rare on the fluorine-free d...

  17. All-MOCVD-grown BH laser on P-InP substrates

    Science.gov (United States)

    Nishimura, Tadashi; Ishimura, E.; Nakajima, Yasuo; Tada, Hitoshi; Kimura, T.; Ohkura, Y.; Goto, Katsuhiko; Omura, Etsuji; Aiga, Masao

    1993-07-01

    A very low cw threshold current of 2.5 mA ( 25 degree(s)C) and 8.0 mA ( 80 degree(s)C) with high reliability has been realized in the all-MOCVD grown BH lasers on p-InP substrates. A strained MQW active layer of 1.3 micrometers wavelength and the precise carrier confinement buried structure by MOCVD is employed for the BH lasers. The excellent potential of long lifetime of the all-MOCVD grown laser has also been confirmed. After the high temperature and the high current (100 degree(s)C, 200 mA) aging test, no significant degradation is observed which is comparable with the well-established LPE grown lasers. The BH laser is also operating stably over 3700 hrs under the APC condition of 50 degree(s)C, 10 mW. Finally, an extremely uniform 10-element all-MOCVD grown LD array is demonstrated, which has the threshold current uniformity of 2.4 +/- 0.1 mA ( 25 degree(s)C) and 9.2 +/- 0.2 mA ( 80 degree(s)C). The growth mechanism in the MOCVD is also described.

  18. MOCVD growth of CdTe and HgTe on GaAs in a vertical, high-speed, rotating-disc reactor

    International Nuclear Information System (INIS)

    Tompa, G.S.; Nelson, C.R.; Reinert, P.D.; Saracino, M.A.; Terrill, L.A.; Colter, P.C.

    1989-01-01

    The metalorganic chemical vapor deposition (MOCVD) growth of CdTe and HgTe on GaAs (111) and (100) substrates in a vertical, high-speed, rotating-disc reactor was investigated. A range of total reactor pressure, carrier gas flow rate, chemical concentrations, deposition temperature, and rotation rate have been investigated in an attempt to optimize growth conditions. Diisopropyltelluride (DIPTe) and Dimethylcadmium (DMCd) were used as growth precursors. Thickness uniformity varies less than +/- 1.5% over 50 mm diameter wafers. Films having FWHM X-ray rocking curves less than 90 arcsec were obtained on GaAs (111) substrates. The films have excellent surface morphology, exhibiting less than 5 x 10 4 cm - 2 orange peel dents which are much-lt 1 μm in size. An elemental mercury source was added to the growth system. Initial results for the growth of HgTe and HgCdTe are discussed

  19. Thermogravimetric evaluation of the suitability of precursors for MOCVD

    International Nuclear Information System (INIS)

    Kunte, G V; Shivashankar, S A; Umarji, A M

    2008-01-01

    A method based on the Langmuir equation for the estimation of vapour pressure and enthalpy of sublimation of subliming compounds is described. The variable temperature thermogravimetric/differential thermogravimetric (TG/DTG) curve of benzoic acid is used to arrive at the instrument parameters. Employing these parameters, the vapour pressure–temperature curves are derived for salicylic acid and camphor from their TG/DTG curves. The values match well with vapour pressure data in the literature, obtained by effusion methods. By employing the Clausius–Clapeyron equation, the enthalpy of sublimation could be calculated. Extending the method further, two precursors for metal-organic chemical vapour deposition (MOCVD) of titanium oxide bis-isopropyl bis tert-butyl 2-oxobutanoato titanium, Ti(O i Pr) 2 (tbob) 2 , and bis-oxo-bis-tertbutyl 2-oxobutanoato titanium, [TiO(tbob) 2 ] 2 , have been evaluated. The complex Ti(O i Pr) 2 (tbob) 2 is found to be a more suitable precursor. This approach can be helpful in quickly screening for the suitability of a compound as a CVD precursor

  20. The growth of large-area superconducting YBa2Cu3O7-x thin films by pulsed laser ablation

    International Nuclear Information System (INIS)

    Lai, H.C.; Chang, C.M.; Lin, R.J.; Liu, R.S.

    1996-01-01

    In-situ growth of 2-in. diameter superconducting YBa 2 Cu 3 O 7-x (YBCO) thin films using an excimer KrF pulsed laser has been studied. Films with critical transition temperature (T c,0 ) of 89±1 K and critical current density (J c,77K ) in excess of 1 x 10 6 A cm -2 have been prepared routinely. Uniformity in film thickness of below ±15% and film composition of ±5% have been measured. The effects of gas nozzle geometry and target evolution during ablation on the superconducting properties and surface morphology of YBCO thin films have also been investigated. (orig.)

  1. Low ac loss geometries in YBCO coated conductors and impact on conductor stability

    Energy Technology Data Exchange (ETDEWEB)

    Duckworth, Robert C [ORNL; List III, Frederick Alyious [ORNL; Paranthaman, Mariappan Parans [ORNL; Rupich, M. W. [American Superconductor Corporation, Westborough, MA; Zhang, W. [American Superconductor Corporation, Westborough, MA; Xie, Y. Y. [SuperPower Incorporated, Schenectady, New York; Selvamanickam, V. [SuperPower Incorporated, Schenectady, New York

    2007-01-01

    Reduction of ac losses in applied ac fields can be accomplished through either the creation of filaments and bridging in YBCO coated conductors or an assembly of narrow width YBCO tapes. The ac losses for each of these geometries were measured at 77 K in perpendicular ac fields up to 100 mT. While ac loss reduction was achieved with YBCO filaments created through laser scribing and inkjet deposition, the assembly of stacked YBCO conductor provides an alternative method of ac loss reduction. When compared to a 4-mm wide YBCO coated conductor with a critical current of 60 A, the ac loss in a stack of 2-mm wide YBCO coated conductors with a similar total critical current was reduced. While the reduction in ac loss in a 2-mm wide stack coincided with the reduction in the engineering current density of the conductor, further reduction of ac loss was obtained through the splicing of the 2-mm wide tapes with low resistance solders. To better determine the practicality of these methods from a stability point of view, a numerical analysis was carried out to determine the influence of bridging and splicing on stability of a YBCO coated conductor for both liquid nitrogen-cooled and conduction cooled geometries.

  2. Superconducting fault current limiter using high-resistive YBCO tapes

    Energy Technology Data Exchange (ETDEWEB)

    Yazawa, T. [Power and Industrial System R and D Center, Toshiba Corporation, 2-4 Suehiro, Tsurumi, Yokohama 230-0045 (Japan)], E-mail: takashi.yazawa@toshiba.co.jp; Koyanagi, K.; Takahashi, M.; Ono, M.; Toba, K.; Takigami, H.; Urata, M. [Power and Industrial System R and D Center, Toshiba Corporation, 2-4 Suehiro, Tsurumi, Yokohama 230-0045 (Japan); Iijima, Y.; Saito, T. [Fujikura Ltd., 1-5-1 Kiba, Koto, Tokyo 135-0042 (Japan); Ameniya, N. [Yokohama National University, 79-1 Tokiwadai, Hodogaya, Yokohama 240-8501 (Japan); Shiohara, Y. [Superconductivity Research Laboratory, ISTEC, 1-10-13 Shinonome, Koto, Tokyo 135-0062 (Japan)

    2008-09-15

    One of the programs in the Ministry of Economy and Trade and Industry (METI) project regarding R and D on YBCO conductor is to evaluate the applicability of the developed conductor toward several applications. This paper focuses on a fault current limiter (FCL) as one of the expected power applications. YBCO tape conductors with ion beam assisted deposition (IBAD) substrate are used in this work. In order to obtain high resistance of the conductor, which is preferable to an FCL, the thickness of the protecting layer made of silver was decreased as possible. Then high-resistive metal stabilizing layer is attached on the silver layer to improve stability. Obtaining the relevant current limiting performance on short sample experiments, model coils were developed to aim the 6.6 kV-class FCL. Short circuit experiments were implemented with a short circuit generator. The coil successfully restricted the short circuit current over 17 kA to about 700 A by the applied voltage of 3.8 kV, which is nominal phase-to-ground voltage. The experimental results show good agreement with computer analyses and show promising toward the application.

  3. Dynamics of vortex matter in YBCO sub-micron bridges

    Energy Technology Data Exchange (ETDEWEB)

    Papari, G., E-mail: papari@fisica.unina.it [Dipartimento di Fisica, Università degli Studi di Napoli Federico II, I-80126 Napoli (Italy); Carillo, F. [NEST, CNR-NANO and Scuola Normale Superiore, Piazza San Silvestro 12, 56127 Pisa (Italy); Stornaiuolo, D.; Massarotti, D. [Dipartimento di Fisica, Università degli Studi di Napoli Federico II, I-80126 Napoli (Italy); CNR-SPIN UOS Napoli, Complesso Universitario di Monte SantAngelo, via Cinthia, 80126 Napoli (Italy); Longobardi, L. [American Physical Society, 1 Research Road, Ridge, NY 11961 (United States); Beltram, F. [NEST, CNR-NANO and Scuola Normale Superiore, Piazza San Silvestro 12, 56127 Pisa (Italy); Tafuri, F. [CNR-SPIN UOS Napoli, Complesso Universitario di Monte SantAngelo, via Cinthia, 80126 Napoli (Italy); Dipartimento di Ingegneria Industriale e dell' informazione, Seconda Universit‘a di Napoli, via Roma 29, 81031 Aversa (CE) (Italy)

    2014-11-15

    Highlights: • Superconducting properties of YBCO nanowires in the width range ξYBCO nanowires displaying robust superconductivity at widths w as low as 160 nm. We can modify the process in order to maintain a Au protective layer. This allows us to scale our nanowires even further to widths as low as 50 nm. We have studied how the presence of vortices and the occurrence of phase slips affect the transport properties of nanowires in the width range ξ

  4. The fabrication of YBCO superconductor polycrystalline powder by CCSO

    International Nuclear Information System (INIS)

    Martirosyan, K S; Luss, D; Galstyan, E; Xue, Y Y

    2008-01-01

    We present a novel, cost-effective and simple method to produce polycrystalline superconductor YBa 2 Cu 3 O 7-δ (YBCO) powder by a self-sustaining one-step process called carbon combustion synthesis of oxides (CCSO). In this process the exothermic oxidation of carbon nanoparticles generates a thermal wave that propagates at a velocity of about 1 mm s -1 through the solid yttrium, barium, and copper precursors, converting them rapidly (in the order of seconds) to polycrystalline YBCO. The carbon is not incorporated in the product and is emitted as carbon dioxide (CO 2 ) from the sample, generating a highly porous (∼70%) and friable product. Most of the grains have a plate-like shape, are well connected, and have a size of between 1 and 3 μm. The concentration of the residual carbon was less than 0.06 wt%. The magnetization of as-synthesized samples (without external post-annealing in oxygen), as determined by a SQUID magnetometer, showed an onset of the superconducting (SC) transition at ∼91 K, with a 44% shielding fraction of the -1/(4π) value

  5. MOCVD process technology for affordable, high-yield, high-performance MESFET structures. Phase 3: MIMIC

    Science.gov (United States)

    1993-01-01

    Under the MIMIC Program, Spire has pursued improvements in the manufacturing of low cost, high quality gallium arsenide MOCVD wafers for advanced MIMIC FET applications. As a demonstration of such improvements, Spire was tasked to supply MOCVD wafers for comparison to MBE wafers in the fabrication of millimeter and microwave integrated circuits. In this, the final technical report for Spire's two-year MIMIC contract, we report the results of our work. The main objectives of Spire's MIMIC Phase 3 Program, as outlined in the Statement of Work, were as follows: Optimize the MOCVD growth conditions for the best possible electrical and morphological gallium arsenide. Optimization should include substrate and source qualification as well as determination of the optimum reactor growth conditions; Perform all work on 75 millimeter diameter wafers, using a reactor capable of at least three wafers per run; and Evaluate epitaxial layers using electrical, optical, and morphological tests to obtain thickness, carrier concentration, and mobility data across wafers.

  6. Solution processing of YBa2Cu3O7-x thin films

    International Nuclear Information System (INIS)

    Singhal, A.; Paranthaman, M.; Specht, E.D.; Hunt, R.D.; Beach, D.B.; Martin, P.M.; Lee, D.F.

    1997-12-01

    The aim of this work was to develop a non-vacuum chemical deposition technique for YBa 2 Cu 3 O 7-x (YBCO) coated conductors on rolling-assisted biaxially textured substrates (RABiTS). The authors have chosen the metal-organic decomposition (MOD) and sol-gel precursor routes to grow textured YBCO films. In the MOD process, yttrium 2-ethylhexonate, barium neodecanoate, copper 2-ethylhexonate and toluene were used as the starting reagents. YBCO films processed by the MOD method on SrTiO 3 (100) single crystal substrates were consisted of c and a-axis oriented materials. These films also contained some amount of the random phase. The c and a-axis oriented materials were epitaxial on SrTiO 3 substrates. Films have a T c,onset of 89K and the best superconducting transition temperature of 63K. Films pyrolyzed at 525 C and subsequently annealed at 780 C in a p(O 2 ) of 3.5 x 10 -4 atm contained YBCO phase predominantly in a-axis orientation. In the sol-gel route, yttrium-isopropoxide, barium metal, copper methoxide and 2-methoxyethanol were used as the starting reagents. Sol-gel YBCO films on SrTiO 3 substrates were epitaxial and c-axis oriented

  7. Fabrication of 5 cm long epitaxial Sm{sub 0.2}Ce{sub 0.8}O{sub 1.9-x} single buffer layer on textured Ni-5%W substrate for YBCO coated conductors via dip-coating PACSD method

    Energy Technology Data Exchange (ETDEWEB)

    Lei, M.; Wang, W.T.; Pu, M.H.; Yang, X.S.; He, L.J. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Cheng, C.H. [Science and Engineering, University of New South Wales, Sydney 2052, New South Wales (Australia); Zhao, Y., E-mail: yzhao@home.swjtu.edu.cn [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Mail Stop 165, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China)] [Science and Engineering, University of New South Wales, Sydney 2052, New South Wales (Australia)

    2011-11-15

    Epitaxial Sm{sub 0.2}Ce{sub 0.8}O{sub 1.9-x} single buffer layer for YBCO coated conductors was deposited via fluorine-free dip-coating CSD. Flat, dense and crack-free SCO films with sharp (2 0 0) c-axis texture were obtained by carefully controlling the processing. YBCO thin films with a homogeneous surface microstructure were deposited on the SCO-buffered NiW substrate via CSD approach. Five centimeters long epitaxial Sm{sub 0.2}Ce{sub 0.8}O{sub 1.9-x} (SCO) single buffer layer for YBCO coated conductors was deposited via dip-coating polymer-assisted chemical solution deposition (PACSD) approach on bi-axially textured Ni-5%W (2 0 0) alloy substrate. The film formation and texture evolution were investigated using X-ray diffraction and scanning electron microscopy. Flat, dense and crack-free SCO films with sharp (2 0 0) c-axis texture were obtained by way of carefully controlling the concentration of precursor solution, withdrawing speed, annealing temperature and dwelling time. On consideration of both microstructure and texture, epitaxial SCO single buffer layers were fabricated using precursor solution of 0.3 M cationic concentration, the withdrawing speed of 10 mm/min and heat treatment at 1100 deg. C in Ar-5%H{sub 2} mixture gas for 0.5 h. Epitaxial YBCO thin films with a homogeneous surface microstructure were deposited on the SCO-buffered NiW substrate via dip-coating PACSD approach. The PACSD approach was a promising way to fabricate long and low-cost YBCO coated conductors.

  8. Thermal stability analysis of YBCO-coated conductors subject to over-currents

    Energy Technology Data Exchange (ETDEWEB)

    MartInez, E; Angurel, L A; Pelegrin, J [Instituto de Ciencia de Materiales de Aragon, CSIC-Universidad de Zaragoza, C/Maria de Luna 3, E-50018 Zaragoza (Spain); Xie, Y Y; Selvamanickam, V [SuperPower Incorporated, Schenectady, NY 12304 (United States)

    2010-02-15

    The thermal stability of superconducting YBCO-coated conductors subject to over-currents are analysed. We have studied the effect of DC and AC over-current pulses in Cu-stabilized and non-stabilized coated conductors by measuring the electric field and temperature profiles of these conductors immersed in liquid nitrogen. Current pulses of short duration of about 90 ms and long duration of a few seconds were applied to the samples. Three different cooling regimes of liquid nitrogen-convection, nucleate boiling and film boiling-were observed and their influence on the recovery time of superconductivity in the coated conductors after the over-current pulses has been analysed. We have studied the recovery behaviour under two different conditions, in which the current was set to zero and to the operating current after the current pulses. These experiments simulated the conditions during an over-current situation in different electric power applications with special attention given to the behaviour of these coated conductors acting as in-fault current limiters.

  9. Thermal stability analysis of YBCO-coated conductors subject to over-currents

    International Nuclear Information System (INIS)

    MartInez, E; Angurel, L A; Pelegrin, J; Xie, Y Y; Selvamanickam, V

    2010-01-01

    The thermal stability of superconducting YBCO-coated conductors subject to over-currents are analysed. We have studied the effect of DC and AC over-current pulses in Cu-stabilized and non-stabilized coated conductors by measuring the electric field and temperature profiles of these conductors immersed in liquid nitrogen. Current pulses of short duration of about 90 ms and long duration of a few seconds were applied to the samples. Three different cooling regimes of liquid nitrogen-convection, nucleate boiling and film boiling-were observed and their influence on the recovery time of superconductivity in the coated conductors after the over-current pulses has been analysed. We have studied the recovery behaviour under two different conditions, in which the current was set to zero and to the operating current after the current pulses. These experiments simulated the conditions during an over-current situation in different electric power applications with special attention given to the behaviour of these coated conductors acting as in-fault current limiters.

  10. Recent developments in the MOCVD and ALD of rare earth oxides and silicates

    International Nuclear Information System (INIS)

    Jones, Anthony C.; Aspinall, Helen C.; Chalker, Paul R.; Potter, Richard J.; Kukli, Kaupo; Rahtu, Antti; Ritala, Mikko; Leskelae, Markku

    2005-01-01

    Lanthanide, or rare-earth oxides are currently being investigated as alternatives to SiO 2 as the dielectric insulating layer in sub-0.1 μm CMOS technology. Metalorganic chemical vapour deposition (MOCVD) and atomic layer deposition (ALD) are promising techniques for the deposition of these high-κ dielectric oxides and in this paper some of our recent research into the MOCVD and ALD of PrO x , La 2 O 3 , Gd 2 O 3 , Nd 2 O 3 and their related silicates are reviewed

  11. YBa2Cu3O7-x thin films prepared by chemical solution deposition

    International Nuclear Information System (INIS)

    Apetrii, Claudia

    2009-01-01

    The discovery of superconductivity in ceramic materials by Bednorz and Mueller in early 1987, immediately followed by Wu et al., who showed that YBa 2 Cu 3 O 7-x (YBCO) becomes superconducting (92 K) well above the boiling point of nitrogen (77 K) created a great excitement in superconductivity research. Potential applications of high T c -superconductors require large critical currents and high-applied magnetic fields. Effective ways to increase the critical current density at high magnetic fields in YBCO are the introduction of nanoparticles and chemical substitution of yttrium by other rare earth elements. Since low costs and environmental compatibility are essential conditions for the preparation of long length YBCO films, the cost effective chemical solution deposition (CSD) procedure was selected, given that no vacuum technology is required. To reveal the flexibility and the good optimization possibilities of the CSD approach two main processes were chosen for comparison: a fluorine-free method, namely the polymer-metal precursor technique, and a fluorine-based method, the metalorganic deposition (MOD) using the trifluoroacetates (TFA) technique. Sharp transition temperature widths ΔT c of 1.1 K for the polymer metal method, 0.8 K for TFA method and critical current densities J c of ∼3.5 MA/cm 2 shows that high quality YBCO thin films can be produced using both techniques. Especially interesting is the magnetic field dependence of the critical current density J c (B) of the Y(Dy)BCO (80 %) films showing that for the lower magnetic fields the critical current density J c (B) is higher for a standard YBCO film, but at fields higher than 4.5 T the critical current density J c (B) of Y(Dy)BCO is larger than that for the YBCO. Above 8 T, J c (B) of the Y(Dy)BCO film is more than one order of magnitude higher than in pure YBCO film. (orig.)

  12. Enhancement of critical current density of YBa2Cu3O7-δ thin films by nanoscale CeO2 pretreatment of substrate surfaces

    International Nuclear Information System (INIS)

    Cui, X.M.; Liu, G.Q.; Wang, J.; Huang, Z.C.; Zhao, Y.T.; Tao, B.W.; Li, Y.R.

    2007-01-01

    YBa 2 Cu 3 O 7-δ (YBCO) films were prepared on single-crystal SrTiO 3 substrates with metal-organic deposition using trifluoroacetates (TFA-MOD). Positive results have been acquired in controlled study to investigate the effects of substrate surface modification on the growth-induced flux-pinning nanostructures in YBCO films. Nanoscale CeO 2 particles were applied to single-crystal SrTiO 3 substrate surfaces using pulsed laser deposition before YBCO precursors coating. Superconducting properties of the YBCO films grown on the controlled CeO 2 -modified substrates have shown substantial improvement in the critical current densities (J c ) at 77 K over those grown on untreated substrates in almost all the field (78% increment at 1 T, 77 K). We think the reason is that the CeO 2 nanoparticles act as pinning centers

  13. Enhanced Flux Pinning and Critical Current Density via Incorporation of Self-Assembled Rare-Earth Barium Tantalate Nanocolumns within YBa2Cu3O7-δ Films

    Energy Technology Data Exchange (ETDEWEB)

    Wee, Sung Hun [ORNL; Goyal, Amit [ORNL; Specht, Eliot D [ORNL; Cantoni, Claudia [ORNL; Zuev, Yuri L [ORNL; Selvamanickam, V. [SuperPower Incorporated, Schenectady, New York; Cook, Sylvester W [ORNL

    2010-01-01

    We report rare earth barium tantalates, Ba2RETaO6 (BRETO, RE = rare earth elements) as a new class of additives for superior flux-pinning in YBa2Cu3O7- (YBCO) films. BRETO compounds have excellent chemical inertness to and large lattice mismatch with YBCO. This results in phase separation and strain minimization driven self-assembly of BRETO nanocolumns within YBCO films. YBCO+4 vol% Ba2GdTaO6 films show similar Tc to that of an un-doped film of ~ 88.3 K, a higher self-field Jc of 3.8 MA/cm2 at 77 K, and significantly improved in-field Jc higher by a factor of 1.5-6 over entire magnetic field and angular ranges.

  14. Growth orientation and superconducting properties of YBa2Cu3O7-δ films prepared by the low-fluorine sol-gel process

    International Nuclear Information System (INIS)

    Lei Li; Zhao Gaoyang; Xu Hui; Zhao Juanjuan

    2010-01-01

    YBa 2 Cu 3 O 7-δ (YBCO) films were deposited on (100)-oriented LaAlO 3 (LAO) single crystal substrates by the dip-coating process using low-fluorine solution. Their microstructures were characterized with the aid of X-ray diffractometry, scanning electron microscopy and high-resolution transmission electron microscopy. Their superconducting properties were measured by the standard four-probe method. The experiment results show that the film obtained under high enough humidity conditions exhibits better c-axis texture and superconducting properties than the film under a relatively low humidity conditions. Based on the classical nucleation and chemical reaction thermodynamics theory, the underlying crystalline and growth mechanisms of YBCO films under certain humidity conditions are explained in combination with our experimental results. It is suggested that the unreacted intermediate phases such as BaF 2 and CuO aggregated in the YBCO grain boundary will cause lattice distortion in the YBCO matrix and further induce the formation of a-axis oriented YBCO grains as crystallization proceeds. Therefore, it is believed that the relative content of water vapor within the heat-treatment atmosphere plays quite an important role in the preparation of c-axis oriented YBCO film with good superconducting properties. (semiconductor materials)

  15. Microstructure and transport current characterization of YBa2Cu3O7-x thick films prepared by modified solid-liquid melt growth and powder melt process routes

    International Nuclear Information System (INIS)

    Langhorn, J.; McGinn, P.J.

    1999-01-01

    From the characterization of superconducting YBa 2 Cu 3 O 7-x (YBCO) thick films processed by melt texturing on yttria-stabilized zirconia substrates from YBCO precursors it is clear that the properties are highly dependent on the precursor powder. Increased YBCO grain sizes have been induced in thick films processed from by modified solid-liquid melt growth (SLMG) and powder melt (PMP) processes with respect to those processed from pre-reacted YBCO materials. The SLMG and PMP routes utilize precursors consisting of BaCuO 2 -CuO flux material mixed with Y 2 O 3 and Y 2 BaCuO 5 respectively. Cross-sectional analysis of films textured by these routes shows a decreased Y 2 BaCuO 5 size and an increased homogeneity within the matrix with respect to films processed from YBCO powder. Such microstructural improvements lead to an improvement of both the flux pinning and current-carrying characteristics of the processed YBCO films. (author)

  16. Magnetic-field dependence of electrothermal conductivity in YBCO

    Energy Technology Data Exchange (ETDEWEB)

    Marino, A.; Uribe, R. [Universidad del Tolima, Ibague (Colombia); Grupo de Superconductividad y Nuevos Materiales, Universidad Nacional de Colombia, Bogota (Colombia)

    2008-11-15

    Experimental measurements of the electrothermal conductivity (P) near T{sub c}, as a function of external magnetic field were carried out in undoped YBCO (123) superconducting samples. The electrothermal conductivity which relates electrical and thermal currents, depends on the applied magnetic field in high T{sub c} materials, contrary to conventional low T{sub c} superconductors where P is nearly independent of the magnetic field. The experimental P(B,T) data determined from resistivity and thermopower measurements were analyzed in terms of theoretical models and showed a behavior consistent with an order-parameter symmetry (OPS) of d{sub x{sup 2}-y{sup 2}}-wave type. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  17. Variation of Quench Propagation Velocities in YBCO Cables

    CERN Document Server

    Härö, E.; Stenvall, A.; 10.1007/s10948-015-2976-y

    2015-01-01

    changes during the quench. Due to the large temperature margin between the operation and the current sharing temperatures, the normal zone does not propagate with the temperature front. This means that the temperature will rise in a considerably larger volume when compared to the quenched volume. Thus, the evolution of the temperature distribution below current sharing temperature Tcs after the quench onset affects the normal zone propagation velocity in HTS more than in LTS coils. This can be seen as an acceleration of the quench propagation velocities while the quench evolves when margin to Tcs is high. In this paper we scrutinize quench propagation in a stack of YBCO cables with an in-house finite element method software which solves the heat diffusion equation. We compute the longitudinal and transverse normal zone propagation velocities at various distances from the hot spot to demonstrate the distance-variation...

  18. Experimental study of the plasma fluorination of Y-Ba-Cu-O thin films

    CERN Document Server

    Li Qi; Ji Zheng Ming; Feng Yi Jun; Kang Lin; Yang Sen Zu; Wu Pei Heng; Wang Xiao Shu; Ye Yuda

    2002-01-01

    The authors have experimentally studied the surface modifications of Y-Ba-Cu-O (YBCO) thin films using CF sub 4 plasma. The intensity of the plasma fluorination was controlled by changing the biasing voltage and the time of the plasma treatment. Microstructural analyses reveal that the oxygen content of the YBCO thin films was changed. Transport measurements of sufficient fluorinated YBCO films imply that the films changed totally into an oxygen-deficient semi-conducting state. From these experimental results, the authors believe that plasma fluorination is quite a useful method to form controllable a thin barrier layer in fabricating interface engineered junctions and to form a stable narrow weak-link region in fabricating planar superconductor-normal-superconductor junctions

  19. Growth rate of YBCO-Ag superconducting single grains

    Science.gov (United States)

    Congreve, J. V. J.; Shi, Y. H.; Dennis, A. R.; Durrell, J. H.; Cardwell, D. A.

    2017-12-01

    The large scale use of (RE)Ba2Cu3O7 bulk superconductors, where RE=Y, Gd, Sm, is, in part, limited by the relatively poor mechanical properties of these inherently brittle ceramic materials. It is reported that alloying of (RE)Ba2Cu3O7 with silver enables a significant improvement in the mechanical strength of bulk, single grain samples without any detrimental effect on their superconducting properties. However, due to the complexity and number of inter-related variables involved in the top seeded melt growth (TSMG) process, the growth of large single grains is difficult and the addition of silver makes it even more difficult to achieve successful growth reliably. The key processing variables in the TSMG process include the times and temperatures of the stages within the heating profile, which can be derived from the growth rate during the growth process. To date, the growth rate of the YBa2Cu3O7-Ag system has not been reported in detail and it is this lacuna that we have sought to address. In this work we measure the growth rate of the YBCO-Ag system using a method based on continuous cooling and isothermal holding (CCIH). We have determined the growth rate by measuring the side length of the crystallised region for a number of samples for specified isothermal hold temperatures and periods. This has enabled the growth rate to be modelled and from this an optimized heating profile for the successful growth of YBCO-Ag single grains to be derived.

  20. Development of 1 m HTS conductor using YBCO on textured metal substrate

    International Nuclear Information System (INIS)

    Yagi, M.; Sakamoto, H.; Mukoyama, S.; Yamamoto, K.; Amemiya, N.; Nagaya, S.; Kashima, N.; Shiohara, Y.

    2009-01-01

    We fabricated 1 m high temperature superconducting conductor (HTS conductor) using YBa 2 Cu 3 O 7-x coated conductors (YBCO tapes) on textured metal substrates, which are expected to be lower in cost than YBCO tapes using ion-beam assisted deposition. Those substrate and intermediate layers were manufactured by Furukawa Electric, and YBCO and a protective layer were applied to the intermediate layer by Chubu Electric Power. Before fabricating the conductor, a 0.1 mm thick copper tape was soldered to the YBCO tape, and 10 mm wide YBCO tape was divided into three strips by a YAG laser. To have sufficient current capacity for 1 kA, a two-layer conductor was fabricated, and its critical current (I c ) was 1976 A, but the magnetic properties of the textured metal substrates affected the increase in AC loss. In a low current region, the AC loss in this conductor was much higher than the Norris strip model, but approached the Norris strip model in the high current region because the magnetization was almost saturated. Low AC loss of 0.144 W/m at 1 kA rms was achieved even though the conductor had a small outer diameter of 20 mm and was composed of YBCO tapes with magnetic substrates.

  1. Thermally actuated magnetization flux pump in single-grain YBCO bulk

    Energy Technology Data Exchange (ETDEWEB)

    Yan Yu; Li Quan; Coombs, T A, E-mail: yy300@cam.ac.u, E-mail: ql229@cam.ac.u, E-mail: tac1000@cam.ac.u [EPEC Superconductivity Group, Electrical Engineering Department, Cambridge University, 9 J J Thomson Avenue, Cambridge CB3 0FA (United Kingdom)

    2009-10-15

    Recent progress in material processing has proved that high temperature superconductors (HTS) have a great potential to trap large magnetic fields at cryogenic temperatures. For example, HTS are widely used in MRI scanners and in magnetic bearings. However, using traditional ways to magnetize, the YBCO will always need the applied field to be as high as the expected field on the superconductor or much higher than it, leading to a much higher cost than that of using permanent magnets. In this paper, we find a method of YBCO magnetization in liquid nitrogen that only requires the applied field to be at the level of a permanent magnet. Moreover, rather than applying a pulsed high current field on the YBCO, we use a thermally actuated material (gadolinium) as an intermedia and create a travelling magnetic field through it by changing the partial temperature so that the partial permeability is changed to build up the magnetization of the YBCO gradually after multiple pumps. The gadolinium bulk is located between the YBCO and the permanent magnet and is heated and cooled repeatedly from the outer surface to generate a travelling thermal wave inwards. In the subsequent experiment, an obvious accumulation of the flux density is detected on the surface of the YBCO bulk.

  2. Thermally actuated magnetization flux pump in single-grain YBCO bulk

    International Nuclear Information System (INIS)

    Yan Yu; Li Quan; Coombs, T A

    2009-01-01

    Recent progress in material processing has proved that high temperature superconductors (HTS) have a great potential to trap large magnetic fields at cryogenic temperatures. For example, HTS are widely used in MRI scanners and in magnetic bearings. However, using traditional ways to magnetize, the YBCO will always need the applied field to be as high as the expected field on the superconductor or much higher than it, leading to a much higher cost than that of using permanent magnets. In this paper, we find a method of YBCO magnetization in liquid nitrogen that only requires the applied field to be at the level of a permanent magnet. Moreover, rather than applying a pulsed high current field on the YBCO, we use a thermally actuated material (gadolinium) as an intermedia and create a travelling magnetic field through it by changing the partial temperature so that the partial permeability is changed to build up the magnetization of the YBCO gradually after multiple pumps. The gadolinium bulk is located between the YBCO and the permanent magnet and is heated and cooled repeatedly from the outer surface to generate a travelling thermal wave inwards. In the subsequent experiment, an obvious accumulation of the flux density is detected on the surface of the YBCO bulk.

  3. Raman spectra, microstructure and superconducting properties of Sb(III)-YBCO composite superconductor

    Energy Technology Data Exchange (ETDEWEB)

    Elsabawy, Khaled M. [Chemistry Department, Faculty of Science, Tanta University, Tanta (Egypt)]. E-mail: ksabawy@yahoo.com

    2005-11-15

    The pure YBCO (YBa{sub 2}Cu{sub 3}O{sub 7}) and its variant antimony containing composites with general formula; Y{sub 1+x}Sb {sub x}Ba{sub 2}Cu{sub 3}O {sub z}, where x = 0.1, 0.2, 0.4 and 0.6 mol%, respectively, were prepared by the solid-state reaction route. X-ray measurements indicated that Sb{sup 3+} ions have a negligible effect on the main crystalline structure and substitutes Y-sites successfully in lattice structure of 123-YBCO at low concentrations of doping (x = 0.1 {sup {yields}} 0.2). From SE-microscopy mapping and EDX elemental analysis, Sb{sup 3+} was detected qualitatively with good approximation to the actual molar ratio but not observed at 123-YBCO grain boundaries which confirm that antimony (III) has diffused regularly into material bulk of superconducting 123-YBCO-phase at low concentrations. Additions of Sb(III) affected sharply on the main vibrating modes of YBCO regime particularly, on the apical oxygen (O{sub 4}) vibrational mode A {sub 1g}. Magnetic susceptibility measurements proved that antimony oxide additions have slight effect on the transport properties of YBCO-composites regime.

  4. Thin films for emerging applications v.16

    CERN Document Server

    Francombe, Maurice H

    1992-01-01

    Following in the long-standing tradition of excellence established by this serial, this volume provides a focused look at contemporary applications. High Tc superconducting thin films are discussed in terms of ion beam and sputtering deposition, vacuum evaporation, laser ablation, MOCVD, and other deposition processes in addition to their ultimate applications. Detailed treatment is also given to permanent magnet thin films, lateral diffusion and electromigration in metallic thin films, and fracture and cracking phenomena in thin films adhering to high-elongation substrates.

  5. Film thickness determination by grazing incidence diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Battiston, G A; Gerbasi, R [CNR, Padua (Italy). Istituto di Chimica e Tecnologie Inorganiche e dei Materiali Avanzati

    1996-09-01

    Thin films deposited via MOCVD (Metal Organic Chemical Vapour Deposition) are layers in the thickness range of a few manometers to about ten micrometers. An understanding of the physics and chemistry of films is necessary for a better comprehension of the phenomena involved in the film deposition procedure and its optimisation. Together with the crystalline phase a parameter that must be determined is the thickness of the layer. In this work the authors present a method for the measurement of the film thickness. This procedure, based on diffraction intensity absorption of the X-rays, both incident and diffracted in passing through the layers, resulted quite simple, rapid and non-destructive.

  6. Film thickness determination by grazing incidence diffraction

    International Nuclear Information System (INIS)

    Battiston, G. A.; Gerbasi, R.

    1996-01-01

    Thin films deposited via MOCVD (Metal Organic Chemical Vapour Deposition) are layers in the thickness range of a few manometers to about ten micrometers. An understanding of the physics and chemistry of films is necessary for a better comprehension of the phenomena involved in the film deposition procedure and its optimisation. Together with the crystalline phase a parameter that must be determined is the thickness of the layer. In this work the authors present a method for the measurement of the film thickness. This procedure, based on diffraction intensity absorption of the X-rays, both incident and diffracted in passing through the layers, resulted quite simple, rapid and non-destructive

  7. Strain analysis of I-c(epsilon) characteristic of YBCO coated conductor measured by a Walters spring

    OpenAIRE

    Sugano, M; Choi, S; Miyazoe, A; Miyamatsu, K; Ando, T; Itoh, K; Kiyoshi, T; Wada, H; Selvamanickam, V

    2008-01-01

    lc-strain characteristic of YBCO coated conductor was measured using a Walters spring (WASP). In this technique, additional bending and thermal strains induced to the YBCO layer should be considered. In order to produce different initial bending strain to the YBCO layer, the conductor was wound around the springs with different diameters and in the different bending directions. The clear evidence was obtained that -strain curves using a WASP strongly depend on the initial bending strain state...

  8. Yttrium-enriched YBa2Cu3Ox thin films for coated conductors fabricated by pulsed laser deposition

    International Nuclear Information System (INIS)

    Khoryushin, Alexey V.; Mozhaev, Peter B.; Mozhaeva, Julia E.; Andersen, Niels H.; Grivel, Jean-Claude; Hansen, Jørn Bindslev; Jacobsen, Claus S.

    2013-01-01

    Highlights: ► YBCO films were fabricated by PLD from targets of various elemental compositions. ► The Y-enriched films contain yttria nanoparticles which provide efficient pinning. ► The best film has 5.5× higher j c (5 T,50 K) = 2.6MA/cm 2 comparing with a reference film. ► The Y-enriched films remain c-oriented up to 500 nm. ► Films demonstrate no j c suppression with thickness and remarkable stability with time. -- Abstract: The effects of excess yttria on the structural and electrical properties of the YBa 2 Cu 3 O x (YBCO) thin films are studied. The films were deposited on (LaAlO 3 ) 0.3 –(Sr 2 AlTaO 8 ) 0.7 substrates by pulsed laser ablation from targets with different elemental composition. An increase of yttrium content of the target leads to formation of porous films with significantly improved current-carrying capabilities. Structural studies of these films reveal presence of yttria nanoparticles embedded into the YBCO matrix. The highest obtained critical current density in an external magnetic field of 5 T was 2.6 MA/cm 2 at 50 K and 9.4 MA/cm 2 at 20 K. The fabricated Y-enriched YBCO films remain c-oriented at least up to 600 nm thickness with no significant suppression of the critical current density

  9. Out-of-substrate plane orientation control of thin YBa2Cu3O x films on NdGaO3 tilted-axes substrates

    International Nuclear Information System (INIS)

    Mozhaev, Peter B.; Mozhaeva, Julia E.; Bdikin, Igor K.; Kotelyanskii, Iosif M.; Lusanov, Valery A.; Hansen, Jorn Bindslev; Jacobsen, Claus S.; Kholkin, Andrey L.

    2006-01-01

    Epitaxial heterostructures YBa 2 Cu 3 O x (YBCO)/CeO 2 /NdGaO 3 were prepared on tilted-axes NdGaO 3 substrates using laser ablation technique. Morphology, crystal structure and electrical properties of the obtained films were characterized. The seeding mechanisms are affected by the tilt angle, resulting in superior YBCO films on NdGaO 3 substrates in an intermediate range of tilt angles of 6-14 o . The introduction of CeO 2 layer leads to change of the YBCO film orientation: at low deposition rate c-oriented films are formed, while at high deposition rates the film grows with c-axis tilted along the [1 1 0] NdGaO 3 direction. Bi-epitaxial films and structures were prepared by removal of part of the CeO 2 layer using ion-beam milling

  10. Fiber optic quench detection via optimized Rayleigh Scattering in high-field YBCO accelerator magnets

    Energy Technology Data Exchange (ETDEWEB)

    Flanagan, Gene [North Carolina State Univ., Raleigh, NC (United States)

    2016-02-17

    Yttrium barium copper oxide (YBCO) coated conductors are known for their ability to operate in the superconducting state at relatively high temperatures, even above the boiling point of liquid nitrogen (77 K). When these same conductors are operated at lower temperatures, they are able to operate in much higher magnetic fields than traditional superconductors like NiTi or Nb3Sn. Thus, YBCO superconducting magnets are one of the primary options for generating the high magnetic fields needed for future high energy physics devices. Due to slow quench propagation, quench detection remains one of the primary limitations to YBCO magnets. Fiber optic sensing, based upon Rayleigh scattering, has the potential for spatial resolution approaching the wavelength of light, or very fast temporal resolution at low spatial resolution, and a continuum of combinations in between. This project has studied, theoretically and experimentally, YBCO magnets and Rayleigh scattering quench detection systems to demonstrate feasibility of the systems for YBCO quench protection systems. Under this grant an experimentally validated 3D quench propagation model was used to accurately define the acceptable range of spatial and temporal resolutions for effective quench detection in YBCO magnets and to evaluate present-day and potentially improved YBCO conductors. The data volume and speed requirements for quench detection via Rayleigh scattering required the development of a high performance fiber optic based quench detection/data acquisition system and its integration with an existing voltage tap/thermo-couple based system. In this project, optical fibers are tightly co-wound into YBCO magnet coils, with the fiber on top of the conductor as turn-to-turn insulation. Local changes in the temperature or strain of the conductor are sensed by the optical fiber, which is in close thermal and mechanical contact with the conductor. Intrinsic imperfections in the fiber reflect Rayleigh

  11. Broad Temperature Pinning Study of 15 mol.% Zr-Added (Gd, Y)-Ba-Cu-O MOCVD Coated Conductors

    Energy Technology Data Exchange (ETDEWEB)

    Xu, AX; Khatri, N; Liu, YH; Majkic, G; Galstyan, E; Selvamanickam, V; Chen, YM; Lei, CH; Abraimov, D; Hu, XB; Jaroszynski, J; Larbalestier, D

    2015-06-01

    BaZrO3 (BZO) nanocolumns have long been shown to be very effective for raising the pinning force F-p of REBa2Cu3Ox (REBCO, where RE = rare earth) films at high temperatures and recently at low temperatures too. We have successfully incorporated a high density of BZO nanorods into metal organic chemical vapor deposited (MOCVD) REBCO coated conductors via Zr addition. We found that, compared to the 7.5% Zr-added coated conductor, dense BZO nanorod arrays in the 15% Zr-added conductor are effective over the whole temperature range from 77 K down to 4.2 K. We attribute the substantially enhanced J(c) at 30 K to the weak uncorrelated pinning as well as the strong correlated pinning. Meanwhile, by tripling the REBCO layer thickness to similar to 2.8 mu m, the engineering critical current density J(e) at 30 K exceeds J(e) of optimized Nb-Ti wires at 4.2 K.

  12. Alloying, co-doping, and annealing effects on the magnetic and optical properties of MOCVD-grown Ga1-xMn xN

    International Nuclear Information System (INIS)

    Kane, Matthew H.; Strassburg, Martin; Asghar, Ali; Fenwick, William E.; Senawiratne, Jayantha; Song, Qing; Summers, Christopher J.; Zhang, Z. John; Dietz, Nikolaus; Ferguson, Ian T.

    2006-01-01

    Recent theoretical work for Ga 1-x Mn x N predicts ferromagnetism in this materials system with Curie temperatures above room temperature. Ferromagnetic behavior observed in Ga 1-x Mn x N is still controversial, as there are conflicting experimental reports owing to the disparity in crystalline quality and phase purity of Ga 1-x Mn x N produced by different methods. In this work, metal-organic chemical vapor deposition (MOCVD) has been used to grow high-quality epitaxial films of Ga 1-x Mn x N of varying thickness and manganese doping levels using Cp 2 Mn as the Mn source. Crystalline quality and phase purity were determined by high-resolution X-ray diffraction, indicating that no macroscopic second phases are formed. Atomic force microscopy revealed MOCVD-like step flow growth patterns and a mean surface roughness of 0.378 nm in optimally grown films, which is close to that from the as-grown template layer of 0.330 nm. No change in the growth mechanism and morphology with Mn incorporation is observed. A uniform Mn concentration in the epitaxial layers is confirmed by secondary ion mass spectroscopy. SQUID measurements showed an apparent room temperature ferromagnetic hysteresis with saturation magnetizations of over 2 μ B /Mn at x = 0.008, which decreases with increasing Mn incorporation. Upon high-temperature annealing, numerous changes are observed in these properties, including an increase in surface roughness due to surface decomposition and a large decrease in the magnetic signature. A similar decrease in the magnetic signature is observed upon co-doping with the shallow donor silicon during the growth process. These results demonstrate the critical importance of controlling the Fermi level relative to the Mn 2+/3+ acceptor level in Ga 1-x Mn x N in order to achieve strong ferromagnetism

  13. Optical characterization of YBa{sub 2}Cu{sub 3}O{sub 7−δ} thin film modified gold nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Naujok, P.; Katzer, C. [Friedrich Schiller University Jena, Institute of Solid State Physics, Helmholtzweg 5, 07743 Jena (Germany); Schmidl, G., E-mail: gabriele.schmidl@ipht-jena.de [Leibniz Institute of Photonic Technology (IPHT), Albert-Einstein-Straße 9, 07745 Jena (Germany); Jatschka, J.; Fritzsche, W. [Leibniz Institute of Photonic Technology (IPHT), Albert-Einstein-Straße 9, 07745 Jena (Germany); Schmidl, F. [Friedrich Schiller University Jena, Institute of Solid State Physics, Helmholtzweg 5, 07743 Jena (Germany)

    2015-12-01

    Highlights: • Different thick YBCO layers allow an active control of particle sizes and density distributions on film surfaces. • The gold volume on the YBCO film surface decreases with increasing YBCO layer thickness. • Combining SEM and dark-field microscopy via image processing. • Clear correlation of scattering spectrum and addressed particles supporting by a new Ti-marker technology. - Abstract: We report on the influence of YBa{sub 2}Cu{sub 3}O{sub 7−δ} (YBCO) thin films on the self-organized formation of gold nanoparticles. A thickness variation of the YBCO film allows one to actively control the size of the particles and their density distribution. In this context, the particle forming process is discussed. The YBCO matrix can be removed in order to reduce the particle density on the substrate. The remaining modified particles can be used in plasmonic applications. Combining scanning electron microscopy and dark-field microscopy permits one to identify a correlation of the measured scattering spectra with the physical properties of each studied particle. A clear assignment of spectrum and particle is supported by a new Ti-marker technology and image processing. Growth parameters allow the scientist to tune the spectral peak position of the plasmon resonance and the spectral bandwidth.

  14. Structure/Property Relationships for Sol-gel Derived YBa2Cu3O7-d and SrTiO3 Films

    Science.gov (United States)

    Dawley, Jeff; Clem, Paul; Siegal, Michael; Overmyer, Don

    2001-03-01

    Solution deposition of c-axis oriented YBa2Cu3O7-d (YBCO) films on buffered RABiT substrates is a potential method for rapid, low cost production of superconducting tapes for power transmission and other applications. For this work, 100-250 nm thick YBCO and SrTiO3 (STO) films have been prepared by spin-coating and dip-coating sol-gel solutions onto LaAlO3 (100) and RABiT Ni (200) substrates. Biaxially textured STO coatings have been deposited on LaAlO3 and RABiT Ni by using a "templating" technique and controlling growth temperature and pO2. YBCO films grown on STO coated LaAlO3 possess comparable superconducting properties to YBCO films grown directly on LaAlO3 ( 1 MA/cm2 at 77K), indicating that a high quality STO layer does not degrade the crystalline quality of the YBCO. The effects of processing parameters on the STO buffer layer and novel processing techniques for decreasing the processing time and simplifying the integration of sol-gel YBCO with Ni substrates will be discussed. Sandia is a multiprogram laboratory operated by Sandia Corp., a Lockheed Martin Company, for the US Dept. Of Energy under contract DE-AC04-94A185000.

  15. The growth and characterisation of YBa2Cu3O7-δ superconducting thin films

    International Nuclear Information System (INIS)

    McCurry, M.P.

    1999-02-01

    The normal state properties of YBa 2 Cu 3 O 7-δ (YBCO) are not completely understood. It is known that the oxygen doping play a large part in determining these properties. The optical conductivity of a series of c-axis YBCO thin films was investigated in this thesis. The films were grown on (100) MgO substrates using a pulsed laser deposition (PLD) system and characterised using X-ray diffraction, atomic force microscopy and resistance-temperature measurements. The optimum parameters for c-axis YBCO thin film growth were determined by systematically varying the main deposition parameters. The best quality films had a transition temperature T c ∼ 88K, with a transition width ∼ 1-2K. Critical current densities of J c ∼ 10 7 Acm -2 were obtained. Substrate and target morphology affected the quality of the films. a-axis YBCO films were grown using a PrBa 2 Cu 3 O 7 (PBCO) film as a template for growth. The choice of target and substrate were again important, with a smooth substrate essential for the multi-layering. T c ∼ 83K and J c ∼ 10 6 Acm -2 were the best values obtained. These values compare with data published on the 'best' YBCO films deposited by PLD. A series of c-axis films was controllably under-doped using an ex-situ annealing process. The as-grown films were assumed to be optimally doped with δ ∼ 0.05. Doping levels in the 'metallic' region, 0.05 -2 mbar. Another tetragonal film was obtained by cooling it after deposition in a nitrogen atmosphere. Neither had a superconducting transition; the c-axes of both films were elongated. The films could be successfully re-doped with oxygen, with a subsequent return to optimal values of T c and c-axis lattice parameter. The dielectric function of optimally doped and under-doped c-axis YBCO films was determined using the attenuated total reflection (ATR) technique. This data was obtained at a fixed frequency of 2984 cm -1 , (0.366eV), at temperatures ranging from 300K to 80K. The data was analysed in

  16. Growth orientation and superconducting properties of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} films prepared by the low-fluorine sol-gel process

    Energy Technology Data Exchange (ETDEWEB)

    Lei Li; Zhao Gaoyang; Xu Hui; Zhao Juanjuan, E-mail: leili813@gmail.co [School of Materials Science and Engineering, Xi' an University of Technology, Xi' an 710048 (China)

    2010-08-15

    YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) films were deposited on (100)-oriented LaAlO{sub 3} (LAO) single crystal substrates by the dip-coating process using low-fluorine solution. Their microstructures were characterized with the aid of X-ray diffractometry, scanning electron microscopy and high-resolution transmission electron microscopy. Their superconducting properties were measured by the standard four-probe method. The experiment results show that the film obtained under high enough humidity conditions exhibits better c-axis texture and superconducting properties than the film under a relatively low humidity conditions. Based on the classical nucleation and chemical reaction thermodynamics theory, the underlying crystalline and growth mechanisms of YBCO films under certain humidity conditions are explained in combination with our experimental results. It is suggested that the unreacted intermediate phases such as BaF{sub 2} and CuO aggregated in the YBCO grain boundary will cause lattice distortion in the YBCO matrix and further induce the formation of a-axis oriented YBCO grains as crystallization proceeds. Therefore, it is believed that the relative content of water vapor within the heat-treatment atmosphere plays quite an important role in the preparation of c-axis oriented YBCO film with good superconducting properties. (semiconductor materials)

  17. Untangling surface oxygen exchange effects in YBa2Cu3O6+x thin films by electrical conductivity relaxation.

    Science.gov (United States)

    Cayado, P; Sánchez-Valdés, C F; Stangl, A; Coll, M; Roura, P; Palau, A; Puig, T; Obradors, X

    2017-05-31

    The kinetics of oxygen incorporation (in-diffusion process) and excorporation (out-diffusion process), in YBa 2 Cu 3 O 6+x (YBCO) epitaxial thin films prepared using the chemical solution deposition (CSD) methodology by the trifluoroacetate route, was investigated by electrical conductivity relaxation measurements. We show that the oxygenation kinetics of YBCO films is limited by the surface exchange process of oxygen molecules prior to bulk diffusion into the films. The analysis of the temperature and oxygen partial pressure influence on the oxygenation kinetics has drawn a consistent picture of the oxygen surface exchange process enabling us to define the most likely rate determining step. We have also established a strategy to accelerate the oxygenation kinetics at low temperatures based on the catalytic influence of Ag coatings thus allowing us to decrease the oxygenation temperature in the YBCO thin films.

  18. Growth of Highly Epitaxial YBa2Cu3O7-δ Films from a Simple Propionate-Based Solution

    DEFF Research Database (Denmark)

    Yue, Zhao; Torres, Pol; Tang, Xiao

    2015-01-01

    Intensive investigations have been conducted to develop epitaxial oxide thin films with superior electromagnetic performance by low-cost chemical solution deposition routes. In this paper, a novel propionate-based precursor solution without involving any other additive was proposed and employed...... to grow superconducting YBa2Cu3O7-δ (YBCO) films on LaAlO3 (LAO) single crystals. The precursor solutions are stable with a long shelf life of up to several months. Since the primary compositions are propionates after evaporating the solvent, the toxic reagents and evolved gases during solution synthesis...... and heat treatment can be eliminated completely. In this process, rapid pyrolysis and high conversation rate can also be achieved during growth of YBCO films in comparison with the conventional trifluoroacetate metal organic deposition routes. Remarkably, a 210 nm YBCO film exhibits high superconducting...

  19. Enhanced flux pinning properties in superconducting YBa{sub 2}Cu{sub 3}O{sub 7−z} films by a novel chemical doping approach

    Energy Technology Data Exchange (ETDEWEB)

    Wang, W.T., E-mail: wtwang@swjtu.edu.cn [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Pu, M.H.; Lei, M.; Zhang, H.; Wang, Z. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Zhang, H. [Department of Physics, Peking University, Beijing 100871 (China); Cheng, C.H. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia); Zhao, Y., E-mail: yzhao@swjtu.edu.cn [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Mail Stop 165, Chengdu, Sichuan 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney, 2052 NSW (Australia)

    2013-10-15

    Highlights: • Pure and Co-doped YBCO films were prepared by newly-developed chemical method. • The doped films have much denser and smoother surface microstructures. • Significantly enhanced fux-pinning properties have been obtained for dilute Co-doped flm. -- Abstract: Pure and cobalt-doped superconducting YBa{sub 2}Cu{sub 3}O{sub 7−z} (YBCO) films were prepared on (0 0 l) LaAlO{sub 3} substrate by a newly developed polymer-assisted metal organic deposition method. The cobalt-doped YBCO films display much denser and smoother surface microstructures and the superconducting transition temperature T{sub c} spans a small range of 1.7 K with the doping levels. Significantly enhanced flux-pinning properties have been obtained for dilute cobalt-doped film. This may be attributed to the good grain connections and the effective flux pinning centers introduced by cobalt doping.

  20. Enhanced flux pinning properties in superconducting YBa2Cu3O7−z films by a novel chemical doping approach

    International Nuclear Information System (INIS)

    Wang, W.T.; Pu, M.H.; Lei, M.; Zhang, H.; Wang, Z.; Zhang, H.; Cheng, C.H.; Zhao, Y.

    2013-01-01

    Highlights: • Pure and Co-doped YBCO films were prepared by newly-developed chemical method. • The doped films have much denser and smoother surface microstructures. • Significantly enhanced fux-pinning properties have been obtained for dilute Co-doped flm. -- Abstract: Pure and cobalt-doped superconducting YBa 2 Cu 3 O 7−z (YBCO) films were prepared on (0 0 l) LaAlO 3 substrate by a newly developed polymer-assisted metal organic deposition method. The cobalt-doped YBCO films display much denser and smoother surface microstructures and the superconducting transition temperature T c spans a small range of 1.7 K with the doping levels. Significantly enhanced flux-pinning properties have been obtained for dilute cobalt-doped film. This may be attributed to the good grain connections and the effective flux pinning centers introduced by cobalt doping

  1. Improving superconducting properties of YBCO high temperature superconductor by Graphene Oxide doping

    Energy Technology Data Exchange (ETDEWEB)

    Dadras, S., E-mail: dadras@alzahra.ac.ir; Dehghani, S.; Davoudiniya, M.; Falahati, S.

    2017-06-01

    In this research, we report the synthesis and characterization of YBa{sub 2}Cu{sub 3}O{sub 7-δ} (YBCO) high temperature superconductor prepared by sol-gel method and doped with Graphene Oxide (GO) in different weight percentages, 0, 0.1, 0.7 and 1 % wt. The x-ray diffraction (XRD) analysis confirms the formation of orthorhombic phase of superconductivity for all the prepared samples. We found that GO doping reduces the crystalline size of the samples. We evaluated the effects of GO doping on the normal state resistivity (ρ), superconducting transition temperature (T{sub c}) and critical current density (J{sub c}). The results show that the GO doping has a positive effect on these properties. Also, the highest J{sub c} is obtained for the 0.7 %wt GO doped YBCO compound that its critical current density is about 15 times more than the J{sub c} of pure one in 0.4 T magnetic field. The scanning electron microscope (SEM) analysis shows that there are better connections between the grains of GO doped samples. - Highlights: • Graphene Oxide doping increased the YBCO critical current density. • Graphene Oxide creates a better connection between the YBCO grains. • The normal resistivity of samples were decreased by GO doping to YBCO compounds. • Graphene Oxide doping has a positive effect on the critical transition temperature.

  2. Critical current survival in the YBCO superconducting layer of a delaminated coated conductor

    Science.gov (United States)

    Feng, Feng; Fu, Qishu; Qu, Timing; Mu, Hui; Gu, Chen; Yue, Yubin; Wang, Linli; Yang, Zhirong; Han, Zhenghe; Feng, Pingfa

    2018-04-01

    A high-temperature superconducting coated conductor can be practically applied in electric equipment due to its favorable mechanical properties and critical current (I c) performance. However, the coated conductor can easily delaminate because of its poor stress tolerance along the thickness direction. It would be interesting to investigate whether the I c of the delaminated YBa2Cu3O7-δ (YBCO) layer can be preserved. In this study, coated conductor samples manufactured through the metal organic deposition route were delaminated by liquid nitrogen immersion. Delaminated samples, including the YBCO layer and silver stabilizer, were obtained. Delamination occurred inside the YBCO layer and near the YBCO-CeO2 interface, as suggested by the results of scanning electron microscopy (SEM) and x-ray diffraction. A scanning Hall probe system was employed to measure the I c distribution of the original sample and the delaminated sample. It was found that approximately 50% of the I c can be preserved after delamination, which was verified by I c measurements using the four-probe method. Dense and crack-free morphologies of the delaminated surfaces were observed by SEM, which accounts for the I c survival of the delaminated YBCO layer. The potential application of the delaminated sample in superconducting joints was discussed based on the oxygen diffusion estimation.

  3. Coaxial magnetic brakes using single-domain YBCO

    International Nuclear Information System (INIS)

    Putman, P.T.; Salama, K.

    2008-01-01

    In coaxial magnetic brakes, the changing field produced by movement of a solenoidal magnet induces a current in the wall of a conductive tube. The interaction of the field and current leads to a repulsive force that slows the motion of the magnet. For brake applications that require high force density, melt-textured YBCO is a clear choice of material for the magnet because it can carry high currents at a given field and temperature, and is inherently capable of operating in persistent current mode. We present calculations of the performance of this type of brake as a function of magnet current density for catch tubes composed of aluminum and titanium. These results are validated with low speed (20 m/s) tests. Calculations indicate that melt-textured magnets can decelerate projectiles with a mass of 1 kg from 2000 m/s to rest in distances on the order of 10 m. This suggests that this type of brake is suitable for use in hypervelocity experiments, which sometimes requires nondestructive deceleration of projectiles for diagnostic purposes

  4. The homogeneity of levitation force in single domain YBCO bulk

    International Nuclear Information System (INIS)

    Zhou Keran; Xu Kexi; Wu Xingda; Pan Pengjun

    2007-01-01

    The pellet homogeneity of levitation force versus the position in comparison to the seed or to the top surface has been studied in the entire volume of a single domain YBa 2 Cu 3 O 7-δ bulk sample processed by the top-seeded melt texturing growth (TSMTG). It is found that the levitation forces increase and peak at a depth of 3 mm from the top of the sample at liquid nitrogen temperature. In other words, the second disk has the largest levitation force density. The phenomenon can be interpreted by the interaction between the microcracks or pores produced by crystal growth and the oxygenation. We propose a model in which Y211 particles distribution leading to microcracks and pores reduces the effective induced shielding current loops (ISCL) and increases the perimeters of ISCL. This corresponds to a decrease in the grain size and results in greatly reduced levitation forces of the bottom of the bulk. From the research, we know that the density of the YBCO bulk is also an important parameter for the levitation properties. The result is very attractive and useful for the fundamental studies and fabrication of TSMTG YBa 2 Cu 3 O 7-δ bulk

  5. The homogeneity of levitation force in single domain YBCO bulk

    Science.gov (United States)

    Zhou, Keran; Xu, Ke-Xi; Wu, Xing-da; Pan, Peng-jun

    2007-11-01

    The pellet homogeneity of levitation force versus the position in comparison to the seed or to the top surface has been studied in the entire volume of a single domain YBa 2Cu 3O 7-δ bulk sample processed by the top-seeded melt texturing growth (TSMTG). It is found that the levitation forces increase and peak at a depth of 3 mm from the top of the sample at liquid nitrogen temperature. In other words, the second disk has the largest levitation force density. The phenomenon can be interpreted by the interaction between the microcracks or pores produced by crystal growth and the oxygenation. We propose a model in which Y211 particles distribution leading to microcracks and pores reduces the effective induced shielding current loops (ISCL) and increases the perimeters of ISCL. This corresponds to a decrease in the grain size and results in greatly reduced levitation forces of the bottom of the bulk. From the research, we know that the density of the YBCO bulk is also an important parameter for the levitation properties. The result is very attractive and useful for the fundamental studies and fabrication of TSMTG YBa 2Cu 3O 7-δ bulk.

  6. Phase dynamics of low critical current density YBCO Josephson junctions

    Energy Technology Data Exchange (ETDEWEB)

    Massarotti, D., E-mail: dmassarotti@na.infn.it [Dipartimento di Fisica, Università degli Studi di Napoli Federico II, Via Cinthia, 80126 Napoli (Italy); CNR-SPIN UOS Napoli, Complesso Universitario di Monte Sant’Angelo, Via Cinthia, 80126 Napoli (Italy); Stornaiuolo, D. [Dipartimento di Fisica, Università degli Studi di Napoli Federico II, Via Cinthia, 80126 Napoli (Italy); Rotoli, G. [Dipartimento di Ingegneria Industriale e dell’Informazione, Seconda Università di Napoli, Via Roma 29, 81031 Aversa (CE) (Italy); Carillo, F. [Nest, Scuola Normale Superiore, Piazza San Silvestro 12, 56126 Pisa (Italy); Galletti, L. [Dipartimento di Fisica, Università degli Studi di Napoli Federico II, Via Cinthia, 80126 Napoli (Italy); CNR-SPIN UOS Napoli, Complesso Universitario di Monte Sant’Angelo, Via Cinthia, 80126 Napoli (Italy); Longobardi, L. [Dipartimento di Ingegneria Industriale e dell’Informazione, Seconda Università di Napoli, Via Roma 29, 81031 Aversa (CE) (Italy); American Physical Society, 1 Research Road, Ridge, NY 11961 (United States); Beltram, F. [Nest, Scuola Normale Superiore, Piazza San Silvestro 12, 56126 Pisa (Italy); Tafuri, F. [CNR-SPIN UOS Napoli, Complesso Universitario di Monte Sant’Angelo, Via Cinthia, 80126 Napoli (Italy); Dipartimento di Ingegneria Industriale e dell’Informazione, Seconda Università di Napoli, Via Roma 29, 81031 Aversa (CE) (Italy)

    2014-08-15

    Highlights: • We study the phase dynamics of YBaCuO Josephson junctions using various tools. • We derive information on the dissipation in a wide range of transport parameters. • Dissipation in such devices can be described by a frequency dependent damping model. • The use of different substrates allows us to tune the shell circuit. - Abstract: High critical temperature superconductors (HTS) based devices can have impact in the study of the phase dynamics of Josephson junctions (JJs) thanks to the wide range of junction parameters they offer and to their unconventional properties. Measurements of current–voltage characteristics and of switching current distributions constitute a direct way to classify different regimes of the phase dynamics and of the transport, also in nontrivial case of the moderately damped regime (MDR). MDR is going to be more and more common in JJs with advances in nanopatterning superconductors and synthesizing novel hybrid systems. Distinctive signatures of macroscopic quantum tunneling and of thermal activation in presence of different tunable levels of dissipation have been detected in YBCO grain boundary JJs. Experimental data are supported by Monte Carlo simulations of the phase dynamics, in a wide range of temperatures and dissipation levels. This allows us to quantify dissipation in the MDR and partially reconstruct a phase diagram as guideline for a wide range of moderately damped systems.

  7. In-plane optical response in underdoped YBCO

    Science.gov (United States)

    Kakeshita, Teruhisa; Masui, Takahiko; Tajima, Setsuko

    2005-03-01

    The recent STM experiments demonstrated that the electronic state in CuO2 plane is inhomogeneous [1], which becomes conspicuous in the underdoped regime. In such an inhomogeneous state, it is not obvious whether a superfluid density is correctly estimated by a conventional way. We investigated the in-plane optical response for underdoped YBCO crystal to discuss the relation between inhomogeneity and superfluid density in the pseudo-gapped state. The a-axis optical spectrum shows a larger residual conductivity than that for the optimum doping. The superfluid density estimated from our optical spectrum at the lowest temperature is substantially smaller than that determined by μSR. We discuss this strongly suppressed superfluid density and the large residual conductivity in terms of the inhomogeneity in real- and k-space. This work was supported by the New Energy and Industrial Technology Development Organization(NEDO) through ISTEC as the Collaborative Research and Development of Fundamental Technologies for Superconductivity Applications. [1]K.M.Lang et al., Nature 415, 412 (2002). *present address: Dept. of Physics, Osaka University, Machikaneyama 1-1, Toyonaka, Osaka 560-0043, Japan

  8. Structural characterization of one-dimensional ZnO-based nanostructures grown by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Sallet, Vincent; Falyouni, Farid; Marzouki, Ali; Haneche, Nadia; Sartel, Corinne; Lusson, Alain; Galtier, Pierre [Groupe d' Etude de la Matiere Condensee (GEMAC), CNRS-Universite de Versailles St-Quentin, Meudon (France); Agouram, Said [SCSIE, Universitat de Valencia, Burjassot (Spain); Enouz-Vedrenne, Shaima [Thales Research and Technology France, Palaiseau (France); Munoz-Sanjose, Vicente [Departamento de Fisica Aplicada y Electromagnetismo, Universitat de Valencia, Burjassot (Spain)

    2010-07-15

    Various one-dimensional (1D) ZnO-based nanostructures, including ZnO nano-wires (NWs) grown using vapour-liquid-solid (VLS) process, ZnO/ZnSe core/shell, nitrogen-doped ZnO and ZnMgO NWs were grown by metalorganic chemical vapour deposition (MOCVD). Transmission electron microscopy (TEM) analysis is presented. For all the samples, a high crystalline quality is observed. Some features are emphasized such as the gold contamination of ZnO wires grown under the metal droplets in the VLS process. It is concluded that MOCVD is a suitable technique for the realization of original ZnO nanodevices. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

  9. Epitaxial Ge Solar Cells Directly Grown on Si (001) by MOCVD Using Isobutylgermane

    Science.gov (United States)

    Kim, Youngjo; Kim, Kangho; Lee, Jaejin; Kim, Chang Zoo; Kang, Ho Kwan; Park, Won-Kyu

    2018-03-01

    Epitaxial Ge layers have been grown on Si (001) substrates by metalorganic chemical vapor deposition (MOCVD) using an isobutylgermane (IBuGe) metalorganic source. Low and high temperature two-step growth and post annealing techniques are employed to overcome the lattice mismatch problem between Ge and Si. It is demonstrated that high quality Ge epitaxial layers can be grown on Si (001) by using IBuGe with surface RMS roughness of 2 nm and an estimated threading dislocation density of 4.9 × 107 cm -2. Furthermore, single-junction Ge solar cells have been directly grown on Si substrates with an in situ MOCVD growth. The epitaxial Ge p- n junction structures are investigated with transmission electron microscopy and electrochemical C- V measurements. As a result, a power conversion efficiency of 1.69% was achieved for the Ge solar cell directly grown on Si substrate under AM1.5G condition.

  10. Multilayer porous structures of HVPE and MOCVD grown GaN for photonic applications

    Science.gov (United States)

    Braniste, T.; Ciers, Joachim; Monaico, Ed.; Martin, D.; Carlin, J.-F.; Ursaki, V. V.; Sergentu, V. V.; Tiginyanu, I. M.; Grandjean, N.

    2017-02-01

    In this paper we report on a comparative study of electrochemical processes for the preparation of multilayer porous structures in hydride vapor phase epitaxy (HVPE) and metal organic chemical vapor phase deposition (MOCVD) grown GaN. It was found that in HVPE-grown GaN, multilayer porous structures are obtained due to self-organization processes leading to a fine modulation of doping during the crystal growth. However, these processes are not totally under control. Multilayer porous structures with a controlled design have been produced by optimizing the technological process of electrochemical etching in MOCVD-grown samples, consisting of five pairs of thin layers with alternating-doping profiles. The samples have been characterized by SEM imaging, photoluminescence spectroscopy, and micro-reflectivity measurements, accompanied by transfer matrix analysis and simulations by a method developed for the calculation of optical reflection spectra. We demonstrate the applicability of the produced structures for the design of Bragg reflectors.

  11. Overgrowth of cracks in YBa{sub 2}Cu{sub 3}O{sub 6+δ}-thin films grown on SrTiO{sub 3}- and Al{sub 2}O{sub 3}-substrates

    Energy Technology Data Exchange (ETDEWEB)

    Ackermann, Kai; Haenisch, Jens; Holzapfel, Bernhard [Institut fuer Technische Physik, Karlsruher Institut fuer Technologie, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany)

    2016-07-01

    High temperature superconducting materials like REBCO-thin films offer a wide range of applications like superconducting transformers, cables, coils or fault current limiters. Although the number of applications is increasing the REBCO-coated conductor length is still limited due to substrate and thin film fabrication defects. In order to improve the manufacturing processes of REBCO-coated conductors the growth behavior of REBCO-thin films on defective or broken substrate surfaces has to be understood. Therefore we investigated the structural and electronic properties of YBCO-thin films grown on cracked SrTiO{sub 3}- and Al{sub 2}O{sub 3}-substrates. The YBCO-films were prepared by using metalorganic (MOD) and pulsed laser deposition (PLD). Structural and electronic properties of the YBCO-films were investigated by using x-ray diffractometry, atomic force microscopy, scanning electron microscopy and temperature- and magnetic field-dependent conductivity measurements.

  12. Final report on LDRD project : outstanding challenges for AlGaInN MOCVD.

    Energy Technology Data Exchange (ETDEWEB)

    Mitchell, Christine Charlotte; Follstaedt, David Martin; Russell, Michael J.; Cross, Karen Charlene; Wang, George T.; Creighton, James Randall; Allerman, Andrew Alan; Koleske, Daniel David; Lee, Stephen Roger; Coltrin, Michael Elliott

    2005-03-01

    The AlGaInN material system is used for virtually all advanced solid state lighting and short wavelength optoelectronic devices. Although metal-organic chemical vapor deposition (MOCVD) has proven to be the workhorse deposition technique, several outstanding scientific and technical challenges remain, which hinder progress and keep RD&A costs high. The three most significant MOCVD challenges are: (1) Accurate temperature measurement; (2) Reliable and reproducible p-doping (Mg); and (3) Low dislocation density GaN material. To address challenge (1) we designed and tested (on reactor mockup) a multiwafer, dual wavelength, emissivity-correcting pyrometer (ECP) for AlGaInN MOCVD. This system simultaneously measures the reflectance (at 405 and 550 nm) and emissivity-corrected temperature for each individual wafer, with the platen signal entirely rejected. To address challenge (2) we measured the MgCp{sub 2} + NH{sub 3} adduct condensation phase diagram from 65-115 C, at typical MOCVD concentrations. Results indicate that it requires temperatures of 80-100 C in order to prevent MgCp{sub 2} + NH{sub 3} adduct condensation. Modification and testing of our research reactor will not be complete until FY2005. A new commercial Veeco reactor was installed in early FY2004, and after qualification growth experiments were conducted to improve the GaN quality using a delayed recovery technique, which addresses challenge (3). Using a delayed recovery technique, the dislocation densities determined from x-ray diffraction were reduced from 2 x 10{sup 9} cm{sup -2} to 4 x 10{sup 8} cm{sup -2}. We have also developed a model to simulate reflectance waveforms for GaN growth on sapphire.

  13. Prospects for enhancement of critical current of HTSC: thin films with artificial pinning centres

    Energy Technology Data Exchange (ETDEWEB)

    Mozhaev, P.B. (Institute of Physics and Technology RAS, Moscow (Russian Federation)); Mozhaev, J.E.; Khoryushin, A.V.; Bindslev Hansen, J.; Jacobsen, C.S. (Technical Univ. of Denmark, Dept. of Physics, Kgs. Lyngby (Denmark)); Kotelyanskil, I.M.; Luzanov, V.A. (Institute of Radio Engineering and Electronics RAS, Moscow (Russian Federation)); Puriy, A.V. (Moscow Institute of Physics and Technology, Moscow (Russian Federation)); Yurchenko, V.; Johansen, T. (Univ. of Oslo, Dept. of Physics, Oslo (Norway))

    2008-10-15

    Improvement of the critical current of YBCO thin films and heterostructures remains one of the main tasks for fabrication of modern superconducting wires and connectors. Possible ways of achieving the goal are choice of superconductor composition, engineering of artificial pinning centres, and combination of the superconducting layer with other materials. The team of the Department of Physics at Technical University of Denmark is working in all these fields and this paper is a short review of our achievements in an attempt to improve the critical current density of YBCO thin films. (au)

  14. Ba2NdZrO5.5 as a potential substrate material for YBa2Cu3O7-δ superconducting films

    International Nuclear Information System (INIS)

    Tovar, H.; Ortiz Diaz, O.; Landinez Tellez, D.A.; Roa-Rojas, J.

    2007-01-01

    The new oxide Ba 2 NdZrO 5.5 (BNZO) has been produced by the standard solid state reaction method. X-ray diffraction analysis (XRD) revealed that this synthesized material has an ordered complex cubic perovskite structure characteristic of A 2 BB'O 6 crystalline structure with a lattice parameter of a = 8.40 Aa. It was established through EDX analysis that there is no trace of impurities. Chemical stability of BNZO with YBa 2 Cu 3 O 7-δ (YBCO) has been studied by means of Rietveld analysis of experimental XRD data on several samples of BNZO-YBCO composites. Quantitative analysis of phases on XRD patterns show that all peaks have been indexed for both BNZO and YBCO, and no extra peak is detectable. YBCO and BNZO remain as two different separate phases in the composites with no chemical reaction. Electrical measurements also revealed that superconducting transition temperature of pure YBCO and BNZO-YBCO composites is 90 K. These favorable characteristics of BNZO show that it can be used as a potential substrate material for deposition of YBCO superconducting films. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  15. Influence of stabilizer thickness on over-current test of YBCO-coated conductors

    International Nuclear Information System (INIS)

    Kwon, N Y; Kim, H S; Kim, K L; Lee, H G; Yim, S W; Kim, H-R; Hyun, O-B; Kim, H M

    2009-01-01

    The increased use of distributed power generation has led to increasingly high fault current levels. A superconducting fault current limiter (SFCL) is a potential solution to prevent the problem of short-circuit currents. YBCO-coated conductors (CCs) are one of the most promising superconducting materials for SFCLs. Most YBCO CCs have stabilizers, which play a significant role in limiting the fault current in the SFCL. Therefore, the selection of the appropriate material and the thickness of the stabilizer of the CC used for the SFCL may affect its quench/recovery characteristics. In this paper, the quench/recovery characteristics of YBCO CC tapes having stabilizers with various thicknesses were investigated. The quench/recovery test results showed that, as the thickness of the stabilizer decreased, both the final approach temperature and the recovery time decreased.

  16. Finite-element analysis and comparison of the AC loss performance of BSCCO and YBCO conductors

    International Nuclear Information System (INIS)

    Stavrev, Svetlomir; Grilli, Francesco; Dutoit, Bertrand; Ashworth, Stephen

    2006-01-01

    The AC loss performance of two BSCCO and two YBCO conductors of different geometry, characterized by the same self-field critical current of 150 A, is analysed and compared quantitatively. The comparison is made using the finite-element method with a nonlinear B-dependent E-J relation. A new shell-region model is utilised for the simulations of thin YBCO strips. Different AC working conditions are simulated: self-field, applied external field, and combined transport current and external perpendicular field application. Magnetic field and current density profiles are investigated in order to illustrate the reasons for the loss difference in the conductors. Depending on the application, the advantages of using BSCCO or YBCO conductors with specific geometry are outlined

  17. Study of TiO{sub 2} nanomembranes obtained by an induction heated MOCVD reactor

    Energy Technology Data Exchange (ETDEWEB)

    Crisbasan, A., E-mail: andreea.crisbasan@yahoo.com [NANOFORM Group, ICB, Université de Bourgogne, BP 47 870, 21078 Dijon (France); Chaumont, D. [NANOFORM Group, ICB, Université de Bourgogne, BP 47 870, 21078 Dijon (France); Sacilotti, M. [NANOFORM Group, ICB, Université de Bourgogne, BP 47 870, 21078 Dijon (France); Departamento de Fisica – Universidade Federal de Pernambuco, Recife (Brazil); Crisan, A.; Lazar, A.M.; Ciobanu, I. [Science and Materials Engineering Faculty, University of Transilvania, Brasov (Romania); Lacroute, Y.; Chassagnon, R. [Université de Bourgogne, BP 47 870, 21078 Dijon (France)

    2015-12-15

    Highlights: • The TiO{sub 2} structures have been obtained by the MOCVD technique using ferrocene, cobalt layer (annealed at 350 °C) and Ti(OC{sub 3}H{sub 7}){sub 4}. • The TiO{sub 2} growth at 550 °C, during 20 min on the cobalt layer (obtained by electron beam evaporation method) on soda-lime glass has as result TiO{sub 2} nanomembranes. • The TiO{sub 2} nanomembranes grow on the cobalt nuclei. • The TiO{sub 2} nanomembranes are polycrystalline, built from TiO{sub 2} anatase and rutile crystals. - Abstract: Nanostructures of TiO{sub 2} were grown using the metal oxide chemical vapor deposition (MOCVD) technique. The procedure used induction heating on a graphite susceptor. This specific feature and the use of cobalt and ferrocene catalysts resulted in nanomembranes never obtained by common MOCVD reactors. The present study discusses the preparation of TiO{sub 2} nanomembranes and the dependence of nanomembrane structure and morphology on growth parameters.

  18. Anisotrophic currents and flux jumps in high-T-c superconducting films with self-organized arrays of planar defects

    DEFF Research Database (Denmark)

    Yurchenko, V.V.; Qviller, A.J.; Mozhaev, P.B.

    2010-01-01

    Regular arrays of planar defects with a period of a few nanometers can be introduced in superconducting YBa2Cu3O7-delta (YBCO) thin films by depositing them on vicinal (also called miscut or tilted) substrates. This results in the anisotropy of critical currents flowing in the plane of the film. ...

  19. Acoustic emission behavior under bending deformation of YBCO bulk superconductor

    International Nuclear Information System (INIS)

    Yoneda, K.; Ye, J.; Tomita, M.

    2005-01-01

    Bending tests were conducted on U-notched specimens cut from a YBCO bulk superconductor. Acoustic emission (AE) signals obtained under loading parallel or perpendicular to the c-axis were analyzed to investigate the correlation between crack growth behavior and the AE signals. As a result of analyzing log-log plots of strength (σ B ) versus total AE energy (ΣE AE ), a linear relationship was found between ΣE AE and σ B n . Cracks could be broadly divided into two types based on the value of n as an index of crack growth behavior. One type consisted of microcracks originating from cleavage planes and gas holes; these crack propagated parallel to the c-axis and had an n index value of approximately 0.7. The other type was a main crack that originated from the U-notch and had an n index value of approximately 6.5. A sample (A) loaded parallel to the c-axis showed mean bending strength of 74.8MPa. Cracks displaying two different growth patterns of n=0.7 and 6.5 were presented in this sample. Microcracks parallel to the c-axis occurred in the vicinity of 5-10MPa. This sample was characterized by mixed crack growth of a main crack and microcracks. A sample (B) loaded perpendicular to the c-axis displayed mean bending strength of 43MPa. A main crack occurred in the vicinity of 20MPa and displayed a single growth pattern of n=6.5. By analyzing AE signals in this way in the process of conducting a strength evaluation, it was possible to evaluate the failure process of the bulk superconductor in relation to the strength level induced by the applied load

  20. Effects of crystalline quality and electrode material on fatigue in Pb(Zr,Ti)O3 thin film capacitors

    Science.gov (United States)

    Lee, J.; Johnson, L.; Safari, A.; Ramesh, R.; Sands, T.; Gilchrist, H.; Keramidas, V. G.

    1993-07-01

    Pb(Zr(0.52)Ti(0.48))O3 (PZT)/Y1Ba2Cu3O(x) (YBCO) heterostructures were grown by pulsed laser deposition, in which PZT films were epitaxial, highly oriented, or polycrystalline. These PZT films were obtained by varying the deposition temperature from 550 to 760 C or by using various substrates such as SrTiO3 (100), MgO (100), and r-plane sapphire. PZT films with Pt top electrodes exhibited large fatigue with 35-50 percent loss of the remanent polarization after 10 exp 9 cycles, depending on the crystalline quality. Polycrystalline films showed better fatigue resistance than epitaxial or highly oriented films. However, PZT films with both top and bottom YBCO electrodes had significantly improved fatigue resistance for both epitaxial and polycrystalline films. Electrode material seems to be a more important parameter in fatigue than the crystalline quality of the PZT films.

  1. Application of HTSC-thin films in microwave bandpass filters

    International Nuclear Information System (INIS)

    Jha, A.R.

    1993-01-01

    This paper reveals unique performance capabilities of High-Temperature Superconducting Thin-Film (HTSCTFs) for possible applications in microwave bandpass filters (BPFs). Microwave filters fabricated with HTSCTFs have demonstrated lowest insertion loss, highest rejection, and sharpest skirt selectivity. Thin films of Yttrium Barium Copper Oxide (YBCO), Bismuth Strontium Calcium Copper Oxide (BSCCO) and Thallium Calcium Barium Copper Oxide (TCBCO) will be most attractive for filters

  2. Buffer optimization for crack-free GaN epitaxial layers grown on Si(1 1 1) substrate by MOCVD

    International Nuclear Information System (INIS)

    Arslan, Engin; Ozbay, Ekmel; Ozturk, Mustafa K; Ozcelik, Suleyman; Teke, Ali

    2008-01-01

    We report the growth of GaN films on the Si(1 1 1) substrate by metalorganic chemical vapour phase deposition (MOCVD). Different buffer layers were used to investigate their effects on the structural and optical properties of GaN layers. A series of GaN layers were grown on Si(1 1 1) with different buffer layers and buffer thicknesses and were characterized by Nomarski microscopy, atomic force microscopy, high-resolution x-ray diffraction (XRD) and photoluminescence (PL) measurements. We first discuss the optimization of the LT-AlN/HT-AlN/Si(1 1 1) templates and then the optimization of the graded AlGaN intermediate layers. In order to prevent stress relaxation, step-graded AlGaN layers were introduced along with a crack-free GaN layer of thickness exceeding 2.6 μm. The XRD and PL measurements results confirmed that a wurtzite GaN was successfully grown. The resulting GaN film surfaces were flat, mirror-like and crack-free. The mosaic structure in the GaN layers was investigated. With a combination of Williamson-Hall measurements and the fitting of twist angles, it was found that the buffer thickness determines the lateral coherence length, vertical coherence length, as well as the tilt and twist of the mosaic blocks in GaN films. The PL spectra at 8 K show that a strong band edge photoluminescence of GaN on Si (1 1 1) emits light at an energy of 3.449 eV with a full width at half maximum (FWHM) of approximately 16 meV. At room temperature, the peak position and FWHM of this emission become 3.390 eV and 58 meV, respectively. The origin of this peak was attributed to the neutral donor bound exciton. It was found that the optimized total thickness of the AlN and graded AlGaN layers played a very important role in the improvement of quality and in turn reduced the cracks during the growth of GaN/Si(1 1 1) epitaxial layers

  3. Research on resistance characteristics of YBCO tape under short-time DC large current impact

    Science.gov (United States)

    Zhang, Zhifeng; Yang, Jiabin; Qiu, Qingquan; Zhang, Guomin; Lin, Liangzhen

    2017-06-01

    Research of the resistance characteristics of YBCO tape under short-time DC large current impact is the foundation of the developing DC superconducting fault current limiter (SFCL) for voltage source converter-based high voltage direct current system (VSC-HVDC), which is one of the valid approaches to solve the problems of renewable energy integration. SFCL can limit DC short-circuit and enhance the interrupting capabilities of DC circuit breakers. In this paper, under short-time DC large current impacts, the resistance features of naked tape of YBCO tape are studied to find the resistance - temperature change rule and the maximum impact current. The influence of insulation for the resistance - temperature characteristics of YBCO tape is studied by comparison tests with naked tape and insulating tape in 77 K. The influence of operating temperature on the tape is also studied under subcooled liquid nitrogen condition. For the current impact security of YBCO tape, the critical current degradation and top temperature are analyzed and worked as judgment standards. The testing results is helpful for in developing SFCL in VSC-HVDC.

  4. Preparation of Superconductor YBCO-123/Ag Composite Through Urea Molten Salt

    International Nuclear Information System (INIS)

    Yustinus, P.; Indra-Gunawan; Wuryanto

    1996-01-01

    Superconductor YBCO-123/Ag composite has been prepared through Urea molten salt by mixing salt nitrate of Yttrium, Barium, Copper and Silver. The weight of Silver content varied from 0 % - 50 %. After pyrolysis process the powder was subjected to calcination at 300, 500 and 700 o C subsequently for 1 hour. The calcined powders was pelletized into a disk of 1.0 cm in diameter and thickness of 2-3 mm. Sintering of pellet samples was done at 900 o C for 16 hours. Meissner effect on all samples displayed superconductivity phenomena. Samples were examined by XRD, SEM, measurement of critical temperature by using susceptibility magnet vs temperature, and critical current density measurement by using four point probe. Based on orthorhombic structure of YBCO-123 the result of the lattice crystal calculation were is a = 3.8167 - 3.8241 A o ; b = 3.8561 - 3.8895 A o and c = 11.6518 - 11.7104 A o , this showed that silver did not influence the structure of YBCO. Superconductor YBCO-123/Ag composite was prepared. This was proved by critical current density. Jc data which showed increased with increasing of silver content and the highest result was 9.71 x 10 5 Amp/m 2

  5. Multilayered structures of (RE = rare earth)Ba2Cu3Ox films: an approach for the growth of superior quality large-area superconducting films on sapphire substrates

    International Nuclear Information System (INIS)

    Develos-Bagarinao, K; Yamasaki, H; Ohki, K; Nakagawa, Y

    2007-01-01

    Relatively thick REBa 2 Cu 3 O 7-δ (RE = rare earth) films (thickness ∼400-600 nm) with significantly improved surface morphology and critical current properties using a multilayered structure which alternates main layers of YBa 2 Cu 3 O 7-δ (YBCO) with intermediate DyBa 2 Cu 3 O 7-δ (DyBCO) layers on CeO 2 -buffered sapphire substrates were investigated. The DyBCO layer, which has a close lattice matching with YBCO, functions as a good starting template for the growth of high-quality YBCO layers. Critical current density (J c ) drastically increased up to a factor of 2 for YBCO/DyBCO multilayer films, compared to YBCO monolayer films in both the self-field and applied magnetic field. The significant improvement in J c is attributed to the improvement of surface smoothness and enhanced flux pinning properties as revealed by the magnetic-field angular dependence of J c . (rapid communication)

  6. Oxygenation of the traditional and thin-walled MT-YBCO in flowing oxygen and under high evaluated oxygen pressure

    International Nuclear Information System (INIS)

    Prikhna, Tatiana; Chaud, Xavier; Gawalek, Wolfgang; Rabier, Jaques; Savchuk, Yaroslav; Joulain, Anne; Vlasenko, Andrey; Moshchil, Viktor; Sergienko, Nina; Dub, Sergey; Melnikov, Vladimir; Litzkendorf, Doris; Habisreuther, Tobias; Sverdun, Vladimir

    2007-01-01

    The high pressure-high temperature oxygenation of thin-walled MT-YBCO (with artificially produced holes) allows decreasing the amount of macrocracks and increasing j c of the material. The MT-YBCO produced from Y123 and Y211 in the fields higher than 2 T showed higher j c in the ab-planes and lower j c in the c-direction than the MT-YBCO manufactured from Y123 and Y 2 O 3 and can be explained by the difference in twin and microcrack density that in turn can be affected by the difference in Y211 phase distribution

  7. Development of a 20kA current feedthrough using YBCO bulk conductors

    International Nuclear Information System (INIS)

    Maehata, Keisuke; Ishibashi, Kenji; Shintomi, Takakazu; Iwamoto, Akifumi; Maekawa, Ryuji; Mito, Toshiyuki

    2004-01-01

    In the phase II experiment of the Large Helical Device (LHD) of the National Institute for Fusion Science (NIFS), it is planned to operate the helical coils at 1.8 K by employing pressurized superfluid cooling to raise the magnetic field to 4 T with 17.3 kA. It is important to develop a 20kA-class current feedthrough into the 1.8 K region, but it must have a high current capacity and low heat leakage in the maximum magnetic leakage field of 1 T. Rectangle-shaped YBCO bulk conductors measuring 20 mm wide, 140 mm long and 10 mm thick were manufactured from square-pillar-shaped YBCO bulk materials for a 20 kA current. To check the quality of the bulk conductors, internal defects or cracks were detected by carrying out a precise survey of trapped magnetic flux. An assembled 20 kA current feedthrough was mounted in the λ-plate of a pressurized superfluid cooling cryostat. Experiments of current feeding into the 1.8 K region were carried out by operating the 20 kA current feedthrough. In the experiments, the transport current was kept at 20 kA for longer than 1,200 s. During the 20 kA operation, the current transport section of the YBCO bulk conductors remained in the superconducting state and the voltage drop between the YBCO bulk conductors and the copper electrode was observed to be constant. A contact resistance and the Joule heat generation in the joint region between the YBCO bulk conductors and the copper electrode were obtained as 1.45 nΩ and 0.72 W, respectively in the 20 kA operation. We have demonstrated the feasibility of using a 20 kA current feedthrough for the phase II experiment of the LHD. (author)

  8. New method for introducing nanometer flux pinning centers into single domain YBCO bulk superconductors

    International Nuclear Information System (INIS)

    Yang, W.M.; Wang, Miao

    2013-01-01

    Highlights: • Single domain YBCO bulks with Bi 2 O 3 additions fabricated by TSIG process. • Nanoscale Y 2 Ba 4 CuBiOx(YBi2411) particles introduced by Bi 2 O 3 additions. • The YBi2411 particles are about 150 nm, can act as effective flux pinning centers. • The optimal addition of Bi 2 O 3 is 0.7wt% to achieve higher levitation force. • The result is helpful to improve the quality of REBCO bulk superconductors. -- Abstract: Single domain YBCO superconductors with different additions of Bi 2 O 3 have been fabricated by top seeded infiltration and growth process (TSIG). The effect of Bi 2 O 3 additions on the growth morphology, microstructure and levitation force of the YBCO bulk superconductor has been investigated. The results indicate that single domain YBCO superconductors can be fabricated with the additions of Bi 2 O 3 less than 2 wt%; Bi 2 O 3 can be reacted with Y 2 BaCuO 5 and liquid phase and finally form Y 2 Ba 4 CuBiO x (YBi2411) nanoscale particles; the size of the YBi2411 particles is about 100 nm, which can act as effective flux pinning centers. It is also found that the levitation force of single domain YBCO bulks is increasing from 13 N to 34 N and decreasing to 11 N with the increasing of Bi 2 O 3 addition from 0.1 wt% to 0.7 wt% and 2 wt%. This result is helpful for us to improve the physical properties of REBCO bulk superconductors

  9. Effect of Ag doping on the structural, electrical and optical properties of ZnO grown by MOCVD at different substrate temperatures

    Science.gov (United States)

    Ievtushenko, A.; Karpyna, V.; Eriksson, J.; Tsiaoussis, I.; Shtepliuk, I.; Lashkarev, G.; Yakimova, R.; Khranovskyy, V.

    2018-05-01

    ZnO films and nanostructures were deposited on Si substrates by MOCVD using single source solid state zinc acetylacetonate (Zn(AA)) precursor. Doping by silver was realized in-situ via adding 1 and 10 wt. % of Ag acetylacetonate (Ag(AA)) to zinc precursor. Influence of Ag on the microstructure, electrical and optical properties of ZnO at temperature range 220-550 °C was studied by scanning, transmission electron and Kelvin probe force microscopy, photoluminescence and four-point probe electrical measurements. Ag doping affects the ZnO microstructure via changing the nucleation mode into heterogeneous and thus transforming the polycrystalline films into a matrix of highly c-axis textured hexagonally faceted nanorods. Increase of the work function value from 4.45 to 4.75 eV was observed with Ag content increase, which is attributed to Ag behaviour as a donor impurity. It was observed, that near-band edge emission of ZnO NS was enhanced with Ag doping as a result of quenching deep-level emission. Upon high doping of ZnO by Ag it tends to promote the formation of basal plane stacking faults defect, as it was observed by HR TEM and PL study in the case of 10 wt.% of Ag. Based on the results obtained, it is suggested that NS deposition at lower temperatures (220-300 °C) is more favorable for p-type doping of ZnO.

  10. Impact of the substrate misorientation and its preliminary etching on the structural and optical properties of integrated GaAs/Si MOCVD heterostructures

    Science.gov (United States)

    Seredin, P. V.; Lenshin, A. S.; Zolotukhin, D. S.; Arsentyev, I. N.; Zhabotinskiy, A. V.; Nikolaev, D. N.

    2018-03-01

    This is the first attempt to make a report regarding the control of the structural and optical functional characteristics of integrated GaAs/Si heterostructures owing to the employment of preliminary etched misoriented Si substrates. The epitaxial GaAs layer on silicon substrates with no formation of the antiphase domains can be grown using substrates deviating less than 4°-6° from the singular (100) plane or without the use of a transition layer of GaAs nano-stakes. Preliminary etching of the Si substrate made it easier to acquire an epitaxial GaAs film in a single-crystalline state with a significantly less relaxation factor MOCVD, which positively influences on the structural performance of the film. These data agree with the results of Infrared reflection spectroscopy as well as Photoluminescence and UV-Vis spectroscopy. The optical properties of the integrated GaAs/Si (100) heterostructures in the IR and UV spectral regions were also identified by means of the relaxation coefficients.

  11. Formation of Self-Assembled Ba2YNbO6 Nanocolumns and their Contribution to Flux-Pinning and Jc in Nb-doped YBa2Cu3O7- Films

    Energy Technology Data Exchange (ETDEWEB)

    Wee, Sung Hun [ORNL; Goyal, Amit [ORNL; Zuev, Yuri L [ORNL; Cantoni, Claudia [ORNL; Selvamanickam, V. [SuperPower Incorporated, Schenectady, New York; Specht, Eliot D [ORNL

    2010-01-01

    Ba{sub 2}RENbO{sub 6} (RE = rare earth elements including Y) compounds are considered new additives for superior flux-pinning in YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) films due to their excellent chemical inertness to and large lattice mismatches with YBCO. Simultaneous laser ablation of a YBCO target and a Nb metal foil attached to the surface of the target resulted in epitaxial growth of YBCO films having columnar defects comprised of self-aligned Ba{sub 2}YNbO{sub 6} (BYNO) nanorods parallel to the c-axis of the film. Compared to pure YBCO, YBCO+BYNO films exhibited no T{sub c} reduction as well as superior J{sub c} performance with higher self- and in-field J{sub c} by a factor of 1.5-7 and also exhibited a strong J{sub c} peak for H {parallel} c indicative of strong c-axis correlated flux-pinning.

  12. Precipitates in YBa2Cu3O7-δ thin films annealed at low oxygen partial pressure

    International Nuclear Information System (INIS)

    Hou, S.Y.; Phillips, J.M.; Werder, D.J.; Tiefel, T.H.; Fleming, R.M.; Marshall, J.H.; Siegal, M.P.

    1993-01-01

    We have studied the precipitates in YBa 2 Cu 3 O 7-δ (YBCO) thin films grown by the BaF 2 process in p O 2 =4 Torr and 700 degree C. While stoichiometric films result in BaCuO 2 surface precipitates, we have found Y 2 Cu 2 O 5 precipitates embedded in the matrix of the same film. Off stoichiometric films with Ba/Y 2 Cu 2 O 5 in the film matrix. The estimated densities of the two precipitates favor a stoichiometric YBCO film matrix. This behavior is not explainable in terms of phase equilibria and is attributed to kinetic effects. The electrical properties of the films degrade as the Ba/Y ratio deviates from 2.00

  13. Characterization of photoluminescent europium doped yttrium oxide thin-films prepared by metallorganic chemical vapor deposition

    International Nuclear Information System (INIS)

    McKittrick, J.; Bacalski, C.F.; Hirata, G.A.; Hubbard, K.M.; Pattillo, S.G.; Salazar, K.V.; Trkula, M.

    1998-01-01

    Europium doped yttrium oxide, (Y 1-x Eu x ) 2 O 3 , thin-films were deposited on silicon and sapphire substrates by metallorganic chemical vapor deposition (MOCVD). The films were grown in a MOCVD chamber reacting yttrium and europium tris(2,2,6,6-tetramethyl-3,5,-heptanedionates) precursors in an oxygen atmosphere at low pressures (5 Torr) and low substrate temperatures (500--700 C). The films deposited at 500 C were flat and composed of nanocrystalline regions of cubic Y 2 O 3 , grown in a textured [100] or [110] orientation to the substrate surface. Films deposited at 600 C developed from the flat, nanocrystalline morphology into a plate-like growth morphology oriented in the [111] with increasing deposition time. Monoclinic Y 2 O 3 :Eu 3+ was observed in x-ray diffraction for deposition temperatures ≥600 C on both (111) Si and (001) sapphire substrates. This was also confirmed by the photoluminescent emission spectra

  14. Surface Science in an MOCVD Environment: Arsenic on Vicinal Ge(100)

    International Nuclear Information System (INIS)

    Olson, J.M.; McMahon, W.E.

    1998-01-01

    Scanning tunneling microscope (STM) images of arsine-exposed vicinal Ge(100) surfaces show that most As/Ge steps are reconstructed, and that a variety of different step structures exist. The entire family of reconstructed As/Ge steps can be divided into two types, which we have chosen to call ''single-row'' steps and ''double-row'' steps. In this paper we propose a model for a double-row step created by annealing a vicinal Ge(100) substrate under an arsine flux in a metal-organic chemical vapor deposition (MOCVD) chamber

  15. Structural and superconducting properties of (Y,Gd)Ba{sub 2}Cu{sub 3}O{sub 7-{delta}} grown by MOCVD on samarium zirconate buffered IBAD-MgO

    Energy Technology Data Exchange (ETDEWEB)

    Stan, L; Holesinger, T G; Maiorov, B; Feldmann, D M; Usov, I O; DePaula, R F; Civale, L; Foltyn, S R; Jia, Q X [Los Alamos National Laboratory, PO Box 1663, Los Alamos, NM 87545 (United States); Chen, Y; Selvamanickam, V [SuperPower, Incorporated, 450 Duane Avenue, Schenectady, NY 12304 (United States)

    2008-10-01

    Textured samarium zirconate (SZO) films have been grown by reactive cosputtering directly on an ion beam assisted deposited (IBAD) MgO template, without an intermediate homoepitaxial MgO layer. The subsequent growth of 0.9 {mu}m thick (Y,Gd)Ba{sub 2}Cu{sub 3}O{sub 7-{delta}} ((Y, Gd)BCO) films by metal organic chemical vapor deposition (MOCVD) yielded well textured films with a full width at half maximum of 1.9{sup 0} and 3.4{sup 0} for the out-of-plane and in-plane texture, respectively. Microstructural characterizations of the SZO buffered samples revealed clean interfaces. This indicates that the SZO not only provides a diffusion barrier, but also functions as a buffer for (Y, Gd)BCO grown by MOCVD. The achievement of self-field critical current densities (J{sub c}) of over 2 MA cm{sup -2} at 75.5 K is another proof of the effectiveness of SZO as a buffer on the IBAD-MgO template. The in-field measurements revealed an asymmetric angular dependence of J{sub c} and a shift of the ab-plane maxima due to the tilted nature of the template and (Y,Gd){sub 2}O{sub 3} particles existing in the (Y, Gd)BCO matrix. The present results are especially important because they demonstrate that high temperature superconducting coated conductors with simpler architecture can be fabricated using commercially viable processes.

  16. Study of dependence upon the magnetic field and transport current of the magnetoresistive effect in YBCO-based bulk composites

    International Nuclear Information System (INIS)

    Balaev, D A; Prus, A G; Shaykhutdinov, K A; Gokhfeld, D M; Petrov, M I

    2007-01-01

    The magnetoresistive properties of bulk YBCO + CuO and YBCO+BaPb 0.75 Sn 0.25 O 3 composites for different orientations of external magnetic field H and macroscopic transport current j have been measured. These composites exhibit large magnetoresistance in weak magnetic fields ( 2 θ. This fact suggests that the flux flow in the intergrain boundaries is responsible for the large magnetoresistive effect observed in the composites

  17. Harmonic generation effect in high-Tc films

    International Nuclear Information System (INIS)

    Khare, Neeraj; Shrivastava, S.K.; Padmanabhan, V.P.N.; Khare, Sangeeta; Gupta, A.K.

    1997-01-01

    Harmonic generation in thick BPSCCO and thin YBCO films are reported. The application of an ac field (H ac > H c1 ) of frequency f causes the generation of odd harmonics of frequency (2n+1)f. The application of dc field in addition to the ac field causes the appearance of even harmonics also in the BPSCCO film. However, the appearance of even harmonics is not observed in YBCO film with high J c ∼ 1.6x10 6 A/cm 2 and appearance of second harmonic with small magnitude is observed in YBCO film with low J c ∼ 2x10 3 A/cm 2 . The variation of amplitudes of these harmonics are studied as a function of magnitude of ac and dc field and the results are explained in the framework of critical state model. A high-T c film magnetometer based on the measurement of the amplitude of second harmonic has been developed whose field sensitivity is ∼ 1.5x10 -8 T. (author)

  18. Growth of epitaxial Pb(Zr,Ti)O3 films by pulsed laser deposition

    Science.gov (United States)

    Lee, J.; Safari, A.; Pfeffer, R. L.

    1992-10-01

    Lead zirconate titanate (PZT) thin films with a composition near the morphotropic phase boundary have been grown on MgO (100) and Y1Ba2Cu3Ox (YBCO) coated MgO substrates. Substrate temperature and oxygen pressure were varied to achieve ferroelectric films with a perovskite structure. Films grown on MgO had the perovskite structure with an epitaxial relationship with the MgO substrate. On the other hand, films grown on the YBCO/MgO substrate had an oriented structure to the surface normal with a misorientation in the plane parallel to the surface. The measured dielectric constant and loss tangent at 1 kHz were 670 and 0.05, respectively. The remnant polarization and coercive field were 42 μC/cm2 and 53 kV/cm. A large internal bias field (12 kV/cm) was observed in the as-deposited state of the undoped PZT films.

  19. Preparation of epitaxial YBa2Cu3O7-y films on CeO2-buffered yttria-stabilized zirconia substrates by fluorine-free metalorganic deposition

    International Nuclear Information System (INIS)

    Tsukada, Kenichi; Yamaguchi, Iwao; Sohma, Mitsugu; Kondo, Wakichi; Kamiya, Kunio; Kumagai, Toshiya; Manabe, Takaaki

    2007-01-01

    Epitaxial YBa 2 Cu 3 O 7-y (YBCO) films of 120-550 nm thickness have been prepared by fluorine-free metalorganic deposition using a metal acetylacetonate-based coating solution on yttria-stabilized zirconia (YSZ) substrates with an evaporated CeO 2 buffer layer. The YBCO films were highly (0 0 1)-oriented by X-ray diffraction θ-2θ scanning and φ scanning. The YBCO films 120-400 nm in thickness demonstrated high critical current densities (J c ) with an average in excess of 3 MA/cm 2 at 77 K using an inductive method. In particular, a 210-nm-thick film showed a J c of 4.5 MA/cm 2 . These excellent properties are attributed to the high crystallinity, small in-plane fluctuation due to high epitaxy and to the microstructure free from grain boundaries in the YBCO films. Further increase of film thickness increased the fraction of irregularities, i.e., precipitates and micropores, in the film surfaces, resulting in lower J c values

  20. Depth profiling of transport properties of in-situ grown YBa_2Cu_3O_7-x films for coated conductor applications

    Science.gov (United States)

    Jo, William; Huh, J.-U.; Hammond, R. H.; Beasley, M. R.

    2003-03-01

    We report depth profiling of the local critical current density and resistivity of YBa_2Cu_3O_7-x (YBCO) films grown by in-situ electron beam evaporation. The method provides important information on the uniformity of the films, and therefore on the commonly observed property that the critical currents of coated conductor high temperature superconductor films do not scale linearly with thickness. Using a methodology of layer-by-layer etching, depth profiling of critical currents and resistivity of the films has been achieved. We use a Bromine methanol mixture to etch down YBCO films with an etch rate of 60 nm/min. At each step, we also observe surface morphology using high resolution scanning electron microscopy. In this talk, we report further study of the results found earlier that YBCO films deposited at high rates are composed of an upper layer of defected YBCO with a local Jc of 5 - 7 MA/cm^2 and a lower more perfect layer with no critical current capacity. The information derived may be useful in the characterization and optimization of superconducting thin films for electrical power and other applications.

  1. Deuterium permeation of amorphous alumina coating on 316L prepared by MOCVD

    International Nuclear Information System (INIS)

    Li Shuai; He Di; Liu Xiaopeng; Wang Shumao; Jiang Lijun

    2012-01-01

    Highlights: ► Deuterium permeation behavior of alumina coating by MOCVD is investigated. ► The as-prepared alumina is amorphous. ► The alumina coating is dense and well adherent to substrate. ► Deuterium permeation rate of alumina coating is 2–3 orders of magnitude lower than martensitic steels. - Abstract: The deuterium permeation behavior of the alumina coating on 316L stainless steel prepared by metal organic chemical vapor deposition (MOCVD) was investigated. The alumina coating was also characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscope (SEM). It was found that the as-prepared coating consisted of amorphous alumina. This alumina coating had a dense, crack-free and homogeneous morphology. Although the alumina coating was amorphous, effective suppression of deuterium permeation was demonstrated. The deuterium permeability of the alumina coating was 51–60 times less than that of the 316L stainless steel and 153–335 times less than that of the referred low activation martensitic steels at 860–960 K.

  2. Microwave properties of HTS films

    International Nuclear Information System (INIS)

    Cooke, D.W.; Arendt, P.M.; Grey, E.R.; Muenchausen, R.E.; Bennett, B.L.; Foltyn, S.R.; Estler, R.C.; Wu, X.D.; Reeves, G.A.; Elliott, N.E.; Brown, D.R.; Portis, A.M.; Taber, R.C.; Mogrocampero, A.

    1990-01-01

    High-frequency applications of high- temperature superconductors generally fall into two categories: 1) devices that require low values (relative to Cu) of surface resistance R S in ambient surface magnetic fields H rf ; and 2) devices that require low R S in modest fields (H rf ∼ 250 Oe). Moreover, many applications can be realized with small- surface-area films (∼ 1 cm 2 ) whereas others require larger areas - radiofrequency (rf) cavities, for example. Regardless of the application, the potential of HTS films is predicted on satisfying one or both of the above-stated requirements. The authors have measured the surface resistance of small-area (1 cm 2 ) and large-area (6.5 cm 2 ) YBa 2 Cu 3 O 7 (YBCO) films that have been laser ablated onto LaA ell O 3 substrates, large-area (5.1 cm 2 YBCO films that have been e-beam deposited onto LaA ell O 3 , and large-area (11.4 cm 2 ) T ell-based films that have been magnetron sputtered onto metallic substrates. The best R S values are obtained from the 1-cm 2 laser-ablated films; they are 40 μΩ and 340 μΩ at 4 K And 77 K, respectively (ω/2π = 10 GHz). Comparable values for Cu are 6 and 13 mΩ, respectively. Large-area T ell-based films yield typical R S values of 4 mΩ and 14 mΩ at 4 K and 77 K, respectively (ω/2π = 18 GHz). The dependence of R S on H rf for these films indicates that surface fields as large as 55 Oe can be achieved with R S increasing only by a factor of 10. This field dependence is associated with c-axis texturing

  3. Thin film YBa{sub 2}Cu{sub 3}O{sub 7} junctions with La{sub 2/3}Ca{sub 1/3}MnO{sub 3} barrier

    Energy Technology Data Exchange (ETDEWEB)

    Hepting, Matthias; Stoehr, Andreas; Werner, Robert; Kleiner, Reinhold; Koelle, Dieter [Physikalisches Institut - Experimentalphysik II and Center for Collective Quantum Phenomena in LISAplus, Universitaet Tuebingen, Auf der Morgenstelle 14, 72076 Tuebingen (Germany)

    2012-07-01

    We report on the fabrication and electric transport properties of thin film YBa{sub 2}Cu{sub 3}O{sub 7} (YBCO) junctions with La{sub 2/3}Ca{sub 1/3}MnO{sub 3} (LCMO) barrier. Heteroepitaxial YBCO/LCMO/YBCO multilayers were grown in-situ by pulsed laser deposition and subsequently patterned by photolithography and Ar ion milling to form rectangular junctions with typical area 5 {mu}m x 30 {mu}m. A self-alignment process was used for electrical contact via an Au wiring layer to the upper YBCO electrode, similarly as described. Samples were characterized at temperature T=4.2 K either in magnetically shielded environment or in in-plane magnetic fields B up to the Tesla range. We present and discuss current-voltage-characteristics and measurements of critical current vs B.

  4. Study of microstructure and electrical properties of bulk YBCO prepared by melt textured growth technique

    International Nuclear Information System (INIS)

    Gonal, M. R.; Krishnan, Madangopal; Tewari, R.; Tyagi, A. K.; Gyore, A.; Vajda, I.

    2015-01-01

    Bulk YBCO components were prepared using Melt Texture Growth (MTG) technique. Components were fabricated using MTG by addition of Y 2 BaCuO 5 (Y211) and Ag to YBCO, which leads to improved grain size without affecting superconducting properties. Green compacts prepared by cold isostatic pressing were pre-sintered at 930°C before subjecting melt texturing. Cooling rates lower than 1 °C.h −1 was used, in between (peritectic) temperature of about 995 and 1025°C, to obtain large grained components. Microstructure studies in details were carried out by Scanning Electron Microscope (SEM), Electron Probe Micro Analysis (EPMA), Orientation Imaging Microscope (OIM) and TEM correlated with electrical properties like Critical current density (J c )

  5. Role of oxygen partial pressure in microstructural development and properties of YBCO superconductors

    International Nuclear Information System (INIS)

    Singh, J.P.; Guttschow, R.; Dusek, J.T.; Poeppel, R.B.

    1991-01-01

    Results are presented for the effect of oxygen partial pressure (pO 2 ) on the sintered density and microstructure of YBCO superconductors. Extruded YBCO wires were sintered at 910C at different values of pO 2 . Generally, the density increased with decreasing pO 2 , and a density of 91% was achieved at pO 2 = 0.01 atm. Wires sintered at pO 2 = 0.01 atm had a fine microstructure with an average grain size of ∼3 μm and an average strength of 191 MPa. The high strength is due to the small grain size, which causes a decrease in residual tensile stress because of grain anisotropy

  6. Levitation force of melt-textured YBCO superconductors under non-quasi-static situation

    Science.gov (United States)

    Zhao, Z. M.; Xu, J. M.; Yuan, X. Y.; Zhang, C. P.

    2018-06-01

    The superconducting levitation force of a simple superconductor-magnet system under non-quasi-static situation is investigated experimentally. Two yttrium barium copper oxide (YBCO) samples with different performances are chosen from two small batches of samples prepared by the top-seeded melt-textured growth process. The residual carbon content of the precursor powders of the two batches is different due to different heat treatment processes. During the experimental process for measuring the levitation force, the value of the relative speed between the YBCO sample and the permanent magnet is higher than that in conventional studies. The variation characteristics of the superconducting levitation force are analyzed and a crossing phenomenon in the force-displacement hysteresis curves is observed. The results indicate that the superconducting levitation force is different due to the different residual carbon contents. As residual carbon contents reduce, the crossing phenomenon is more obvious accordingly.

  7. Static Test for a Gravitational Force Coupled to Type 2 YBCO Superconductors

    Science.gov (United States)

    Li, Ning; Noever, David; Robertson, Tony; Koczor, Ron; Brantley, Whitt

    1997-01-01

    As a Bose condensate, superconductors provide novel conditions for revisiting previously proposed couplings between electromagnetism and gravity. Strong variations in Cooper pair density, large conductivity and low magnetic permeability define superconductive and degenerate condensates without the traditional density limits imposed by the Fermi energy (approx. 10(exp -6) g cc. Recent experiments have reported anomalous weight loss for a test mass suspended above a rotating type II, YBCO superconductor, with the percentage change (0.05 - 2.1 %) independent of the test mass' chemical composition and diamagnetic properties. A variation of 5 parts per 10' was reported above a stationary (non-rotating) superconductor. In experiments using a sensitive gravimeter, bulk YBCO superconductors were stably levitated in a DC magnetic field. Changes in acceleration were measured to be less than 2 parts in 108 of the normal gravitational acceleration. This result puts new limits on the strength and range of the proposed coupling between static superconductors and gravity.

  8. Calibration of Hall sensor array for critical current measurement of YBCO tape with ferromagnetic substrate

    International Nuclear Information System (INIS)

    Zhu, Yunpeng; Wang, Gang; Liu, Liyuan; Yang, Xinsheng; Zhao, Yong

    2015-01-01

    Abstract : HAS (Hall sensor array) is a powerful tool to detect the uniformity of HTS (high temperature superconductor) tape through mapping the distribution of remanent or shielding field along the surface of the tape. However, measurement of HTS tape with ferromagnetic parts by HSA is still an issue because the ferromagnetic substrate has influence on the magnetic field around the HTS layer. In this work, a continuous HSA system has been designed to measure the critical current of the YBCO tape with ferromagnetic substrate. The relationship between the remanent field and critical current was calibrated by the finite element method. The result showed that the HSA is an effective method for evaluating the critical current of the HTS tape with ferromagnetic substrate. - Highlight: • A continuous Hall sensor array system has been designed. • The inhomogeneity of YBCO tape with ferromagnetic substrate can be detected by HAS. • Finite element method is an effective method for calibrating the remanent field.

  9. Calibration of Hall sensor array for critical current measurement of YBCO tape with ferromagnetic substrate

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Yunpeng; Wang, Gang; Liu, Liyuan [Key laboratory of Magnetic levitation Technologies and Maglev Trains (Ministry of Education), Superconductor and New Energy R& D Center, Mail Stop 165#, Southwest Jiaotong University, Chengdu, 610031 (China); Yang, Xinsheng, E-mail: xsyang@swjtu.edu.cn [Key laboratory of Magnetic levitation Technologies and Maglev Trains (Ministry of Education), Superconductor and New Energy R& D Center, Mail Stop 165#, Southwest Jiaotong University, Chengdu, 610031 (China); Zhao, Yong [Key laboratory of Magnetic levitation Technologies and Maglev Trains (Ministry of Education), Superconductor and New Energy R& D Center, Mail Stop 165#, Southwest Jiaotong University, Chengdu, 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney 2052, NSW (Australia)

    2015-12-15

    Abstract : HAS (Hall sensor array) is a powerful tool to detect the uniformity of HTS (high temperature superconductor) tape through mapping the distribution of remanent or shielding field along the surface of the tape. However, measurement of HTS tape with ferromagnetic parts by HSA is still an issue because the ferromagnetic substrate has influence on the magnetic field around the HTS layer. In this work, a continuous HSA system has been designed to measure the critical current of the YBCO tape with ferromagnetic substrate. The relationship between the remanent field and critical current was calibrated by the finite element method. The result showed that the HSA is an effective method for evaluating the critical current of the HTS tape with ferromagnetic substrate. - Highlight: • A continuous Hall sensor array system has been designed. • The inhomogeneity of YBCO tape with ferromagnetic substrate can be detected by HAS. • Finite element method is an effective method for calibrating the remanent field.

  10. First steps towards cube textured nickel profile wires for YBCO-coated conductors

    International Nuclear Information System (INIS)

    Eickemeyer, J.; Gueth, A.; Freudenberger, J.; Holzapfel, B.; Schultz, L.

    2011-01-01

    The cube texture as a typical sheet texture can also be formed by cold drawing and recrystallization in profile wires. Cube textured Ni profile wires containing up to 96.2% cube oriented grains in the central region were obtained. Forthcoming investigations are promising to get a textured substrate wire for YBCO-coated conductors. Cube textured nickel alloy tapes prepared by cold rolling and annealing (RABiTS method) represent a standard metallic substrate for superconductor coatings of the YBa 2 Cu 3 O 7-δ (YBCO) type. These tapes have a width to thickness ratio of about 30-100. However, a value of close to one is optimal concerning low energetic losses under alternating current applications. First experiments on micro-alloyed nickel prove that the cube texture as a typical sheet texture can also be formed in profile wires with a rectangular cross-section after cold drawing and recrystallization treatment.

  11. Design of a 30 m long 1 kA 10 kV YBCO cable

    Energy Technology Data Exchange (ETDEWEB)

    Rostila, L [Institute of Electromagnetics, Tampere University of Technology, PO Box 692, FIN-33101 Tampere (Finland); Lehtonen, J [Institute of Electromagnetics, Tampere University of Technology, PO Box 692, FIN-33101 Tampere (Finland); Masti, M [Institute of Electromagnetics, Tampere University of Technology, PO Box 692, FIN-33101 Tampere (Finland); Lallouet, N [Nexas France, rue Mozart 4-10, 92587 Clichy (France); Saugrain, J-M [Nexas France, rue Mozart 4-10, 92587 Clichy (France); Allais, A [Nexans Deutschland Industries GmbH and Co. KG, Kabelkamp 20, D-30179 Hannover (Germany); Schippl, K [Nexans Deutschland Industries GmbH and Co. KG, Kabelkamp 20, D-30179 Hannover (Germany); Schmidt, F [Nexans Deutschland Industries GmbH and Co. KG, Kabelkamp 20, D-30179 Hannover (Germany); Balog, G [Nexans Norway, PO Box 6450, Etterstad, N-0605, Oslo, Norway (Norway); Marot, G [Air Liquide DTA, 2 rue de Clemenciere BP15, 38360 Sassenage (France); Ravex, A [Air Liquide DTA, 2 rue de Clemenciere BP15, 38360 Sassenage (France); Usoskin, A [European High Temperature Superconductors Gmbh and Co. KG, Windausweg 2, 37037 Goettingen (Germany); Goemoery, F [Institute of Electrical Engineering, Slovak Academy of Sciences, Dubravska cesta 9, 84104 Bratislava (Slovakia); Klincok, B [Institute of Electrical Engineering, Slovak Academy of Sciences, Dubravska cesta 9, 84104 Bratislava (Slovakia); Souc, J [Institute of Electrical Engineering, Slovak Academy of Sciences, Dubravska cesta 9, 84104 Bratislava (Slovakia); Freyhardt, H C [Institute of Materialphysic, University of Goettingen, Friedrich-Hund-Platz 1, D-37077 Goettingen (Germany)

    2006-04-15

    In this paper a 30 m long one-phase coaxial YBCO cable with 1 kA transport current and 10 kV operating voltage was designed for the Super3C project to check the feasibility of YBCO tapes for low-loss cables. The final design incorporates cryogenic, mechanical and electromagnetic aspects. The electromagnetic losses during normal operation must be minimized. The cryogenic design must also take into account the generation of heat during short circuit conditions. Mechanical restrictions set the minimum gaps between the coated conductor tapes and the minimum lay angles in order to make the cabling feasible and to enable handling of the cable. The design of the electric insulation should be according to the international standard as far as applicable. The final design has to take into account all of the above restrictions.

  12. Dynamic regimes in YBCO in applied magnetic field probed by swept frequency microwave measurements

    International Nuclear Information System (INIS)

    Sarti, S; Silva, E; Giura, M; Fastampa, R; Boffa, M; Cucolo, A M

    2004-01-01

    We report measurements of the microwave resistivity in YBa 2 Cu 3 O 7-δ (YBCO), in the presence of an applied magnetic field. Measurements are performed as a function of frequency, over a continuum spectrum between 6 and 20 GHz, by means of a Corbino disc geometry. These data allow for a direct identification of different dynamical regimes in the dissipation of YBCO in the presence of an applied magnetic field. While at high temperatures a frequency independent resistivity is observed, at lower temperatures we find a marked frequency dependence. The line in the (H,T) plane at which this change in the dynamical regime is observed is clearly identified and discussed in terms of vortex motion and fluctuational resistivity

  13. Design of a 30 m long 1 kA 10 kV YBCO cable

    International Nuclear Information System (INIS)

    Rostila, L; Lehtonen, J; Masti, M; Lallouet, N; Saugrain, J-M; Allais, A; Schippl, K; Schmidt, F; Balog, G; Marot, G; Ravex, A; Usoskin, A; Goemoery, F; Klincok, B; Souc, J; Freyhardt, H C

    2006-01-01

    In this paper a 30 m long one-phase coaxial YBCO cable with 1 kA transport current and 10 kV operating voltage was designed for the Super3C project to check the feasibility of YBCO tapes for low-loss cables. The final design incorporates cryogenic, mechanical and electromagnetic aspects. The electromagnetic losses during normal operation must be minimized. The cryogenic design must also take into account the generation of heat during short circuit conditions. Mechanical restrictions set the minimum gaps between the coated conductor tapes and the minimum lay angles in order to make the cabling feasible and to enable handling of the cable. The design of the electric insulation should be according to the international standard as far as applicable. The final design has to take into account all of the above restrictions

  14. Positron annihilation study on the superconductivity of Gd-doped YBCO system

    International Nuclear Information System (INIS)

    Chen Zhenping; Su Yuling; Xue Yuncai; Liu Haizeng; Gong Shicheng; Zhao Jingxun; Li Xigui

    2006-01-01

    To make clear the influence of magnetic rare-earth ion Gd 3+ doping in the Y site on crystal structure and localized electron structure of YBCO system, the Gd-doped Y 1-x Gd x Ba 2 Cu 3 O 7-δ (x=0-1.0) systems were studied systematically by the positron annihilation technique and X-ray diffraction (XRD). The XRD analysis reveals that Gd 3+ with bigger radius doping in Y site makes the crystal parameters and crystal volume increase, while all the samples remain the single orthorhombic phase as YBa 2 Cu 3 O 7-δ (YBCO) system does. The temperature dependence of resistance measurement shows that T c is above 90 K for all samples, and T c increases with increasing Gd 3+ content. The positron experiment indicates that the localized electronic density n e decreases with increasing Gd 3+ content. (authors)

  15. Numerical simulation and analysis of single grain YBCO processed from graded precursor powders

    OpenAIRE

    Zou, J; Ainslie, Mark Douglas; Hu, D; Zhai, W; Kumar, N Devendra; Durrell, John Hay; Shi, Yunhua; Cardwell, David Anthony

    2015-01-01

    Large single-grain bulk high-temperature superconducting materials can trap high magnetic fields in comparison with conventional permanent magnets, making them ideal candidates to develop more compact and efficient devices, such as actuators, magnetic levitation systems, flywheel energy storage systems and electric machines. However, macro-segregation of Y-211 inclusions in melt processed Y–Ba–Cu–O (YBCO) limits the macroscopic critical current density Jc of such bulk supercond...

  16. Nonequilibrium states of high tc YBCO superconductors under tunnel injection of quasiparticles

    International Nuclear Information System (INIS)

    Iguchi, I.; Wang, Q.; Lee, K.; Yoshida, K.

    1995-01-01

    The nonequilibrium states of high Tc superconductors are investigated by means of tunnel injection of quasiparticles using Pb(or Au)/MgO/YBCO tunnel junctions. The effective critical-current reduction due to tunnel injection is observed, whose behaviour is different from simple heating. The observed results suggest that the resultant nonequilibrium states may also differ from those described by conventional nonequilibrium models

  17. Effect of Au nano-particles doping on polycrystalline YBCO high temperature superconductor

    Energy Technology Data Exchange (ETDEWEB)

    Dadras, Sedigheh, E-mail: dadras@alzahra.ac.ir; Gharehgazloo, Zahra

    2016-07-01

    In this research, we prepared different Au nanoparticles (0.1–2 wt%) doped YBCO high temperature superconductor samples by sol-gel method. To characterize the samples, we used X-Ray diffraction (XRD) and scanning electron microscope (SEM) analysis. Results show the formation of orthorhombic phase of superconductivity for all prepared samples. We observed that by adding Au nanoparticles, the grains' size of the samples reduces from 76 nm to 47 nm as well. The critical current density (J{sub c}) and transition temperature (T{sub c}) were determined using current versus voltage (I–V) and resistivity versus temperature (ρ-T) measurements, respectively. We found that by increasing Au nanoparticles in the compound, in comparison to the pure YBCO sample, the transition temperature, pinning energy and critical current density will increase. Also, the highest J{sub c} is for 1 wt% Au doped YBCO compound that its critical current density is about 8 times more than the J{sub c} of pure one in 0.7 T magnetic field.

  18. Transport ac loss studies of YBCO coated conductors with nickel alloy substrates

    International Nuclear Information System (INIS)

    Duckworth, R C; Thompson, J R; Gouge, M J; Lue, J W; Ijaduola, A O; Yu, D; Verebelyi, D T

    2003-01-01

    Transport alternating current (ac) loss measurements were performed on a series of rolling-assisted biaxially textured substrate (RABiTS) processed YBa 2 Cu 3 O x (YBCO) coated conductors at 77 K. While each sample possessed a 1 μm layer of YBCO and a 3 μm silver cap layer, two different nickel alloy substrates were used and their impact on the ac loss was examined. Both substrates possessed a 75 μm Ni-5 at%W base, but one substrate also had a 2 μm nickel overlayer as part of the buffer layer architecture. The ac losses, which were determined by thermal and electrical measurements, contained two dominant contributions: superconductive hysteresis in the YBCO and ferromagnetic hysteresis in the substrates. The superconductive component followed the Norris elliptic model for the substrate with the nickel overlayer and the Norris thin strip model for the substrate without the nickel overlayer. The substrates' ferromagnetic loss was determined separately through magnetization measurements, which showed that this loss contribution was independent of the presence of the nickel overlayer for effective ac currents less than 50 A. While the overall loss was lower for the thin-strip-like conductor with no nickel overlayer, further research is necessary to strengthen this connection

  19. Bulk YBCO seeded with 45°–45° bridge-seeds of different lengths

    International Nuclear Information System (INIS)

    Shi, Y-H; Durrell, J H; Dennis, A R; Cardwell, D A

    2013-01-01

    Single grain, (RE)BCO (rare earth–barium–copper oxide) bulk superconductors in large or complicated geometries are required for a variety of potential applications, such as in motors and generators and magnetic shielding devices. As a result, top, multi-seeded, melt growth has been investigated over the past 15 years in an attempt to enlarge the size of (RE)BCO single grains specifically for such applications. Of these multi-seeding techniques, so-called bridge-seeding provides the best alignment of two seeds in a single grain growth process. Here we report, for the first time, the successful growth of YBCO (yttrium–barium–copper oxide) using a special, 45°–45°, arrangement of bridge-seeds. The superconducting properties, including trapped field, of the multi-seeded YBCO grains have been measured for different bridge lengths of the 45°–45° bridge-seeds. The boundaries at the impinging growth front and the growth features of the top, multi-seeded surface and cross-section of the multi-seeded, samples have been analysed using optical microscopy. The results suggest that an impurity-free boundary between the two seeds of each leg of the bridge-seed can form when 45°–45° bridge-seeds are used to enlarge the size of YBCO grains. (paper)

  20. Magnetic levitation and its application for education devices based on YBCO bulk superconductors

    International Nuclear Information System (INIS)

    Yang, W.M.; Chao, X.X.; Guo, F.X.; Li, J.W.; Chen, S.L.

    2013-01-01

    Highlights: • A small superconducting maglev propeller system has been designed and constructed based on YBCO bulk superconductors. • Several small maglev vehicle models have been designed and constructed based on YBCO bulk superconductors. • The models can be used as experimental or demonstration devices for the magnetic levitation applications. -- Abstract: A small superconducting maglev propeller system, a small spacecraft model suspending and moving around a terrestrial globe, several small maglev vehicle models and a magnetic circuit converter have been designed and constructed. The track was paved by NdFeB magnets, the arrangement of the magnets made us easy to get a uniform distribution of magnetic field along the length direction of the track and a high magnetic field gradient in the lateral direction. When the YBCO bulks mounted inside the vehicle models or spacecraft model was field cooled to LN 2 temperature at a certain distance away from the track, they could be automatically floating over and moving along the track without any obvious friction. The models can be used as experimental or demonstration devices for the magnetic levitation applications

  1. Iron-YBCO heterostructures and their application for trapped field superconducting motor

    Energy Technology Data Exchange (ETDEWEB)

    Granados, X [Institut de Ciencia de Materials de Barcelona, ICMAB-CSIC, Campus U.A. Barcelona, 08193 Bellaterra (Spain); Bartolome, E [Institut de Ciencia de Materials de Barcelona, ICMAB-CSIC, Campus U.A. Barcelona, 08193 Bellaterra (Spain); Obradors, X [Institut de Ciencia de Materials de Barcelona, ICMAB-CSIC, Campus U.A. Barcelona, 08193 Bellaterra (Spain); Tornes, M [ETSE-UAB, Barcelona (Spain); Rodrigues, L [UNL, Lisbon (Portugal); Gawalek, W [IPHT, Jena (Germany); McCulloch, M [Department Engineering Science, University of Oxford, Oxford (United Kingdom); Hughes, D Dew [Department Engineering Science, University of Oxford, Oxford (United Kingdom); Campbell, A [IRC-UCAM, Cambridge (United Kingdom); Coombs, T [IRC-UCAM, Cambridge (United Kingdom); Ausloos, M [SUPRATEC, Liege (Belgium); Cloots, R [SUPRATEC, Liege (Belgium)

    2006-06-01

    In this work we report on the magnetic behavior of the heterostructures formed by bulk based YBCO rings and ferromagnetic yoke. The magnetization cycle has been performed by an In-Field Hall Mapping technique. A video-like recording of the magnetization process makes it possible to obtain the magnetization of selected areas. The current flowing through the superconducting rings can be deduced from the magnetic field maps. The displacement of the peak of magnetization due to the flux reversal produced by the magnetization of the yoke is also considered. These hybrid heterostructures formed by ferromagnetic and superconducting material have been applied in the construction of the rotor for a brushless AC motor. The design and construction of this machine was carried out within the framework of the TMR Network SUPERMACHINES. The rotor has been designed in a quadrupolar configuration by cutting large YBCO 'window frames' from seeded melt-textured single domain YBCO pellets. This rotor has been coupled to a conventional stator of copper coils wound on an iron armature. The stator can be excited both in bipolar or quadrupolar mode. We report on the behaviour of the motor after a field cooling process when excited in quadrupolar mode.

  2. Magnetic levitation and its application for education devices based on YBCO bulk superconductors

    Energy Technology Data Exchange (ETDEWEB)

    Yang, W.M., E-mail: yangwm@snnu.edu.cn; Chao, X.X.; Guo, F.X.; Li, J.W.; Chen, S.L.

    2013-10-15

    Highlights: • A small superconducting maglev propeller system has been designed and constructed based on YBCO bulk superconductors. • Several small maglev vehicle models have been designed and constructed based on YBCO bulk superconductors. • The models can be used as experimental or demonstration devices for the magnetic levitation applications. -- Abstract: A small superconducting maglev propeller system, a small spacecraft model suspending and moving around a terrestrial globe, several small maglev vehicle models and a magnetic circuit converter have been designed and constructed. The track was paved by NdFeB magnets, the arrangement of the magnets made us easy to get a uniform distribution of magnetic field along the length direction of the track and a high magnetic field gradient in the lateral direction. When the YBCO bulks mounted inside the vehicle models or spacecraft model was field cooled to LN{sub 2} temperature at a certain distance away from the track, they could be automatically floating over and moving along the track without any obvious friction. The models can be used as experimental or demonstration devices for the magnetic levitation applications.

  3. Iron-YBCO heterostructures and their application for trapped field superconducting motor

    International Nuclear Information System (INIS)

    Granados, X; Bartolome, E; Obradors, X; Tornes, M; Rodrigues, L; Gawalek, W; McCulloch, M; Hughes, D Dew; Campbell, A; Coombs, T; Ausloos, M; Cloots, R

    2006-01-01

    In this work we report on the magnetic behavior of the heterostructures formed by bulk based YBCO rings and ferromagnetic yoke. The magnetization cycle has been performed by an In-Field Hall Mapping technique. A video-like recording of the magnetization process makes it possible to obtain the magnetization of selected areas. The current flowing through the superconducting rings can be deduced from the magnetic field maps. The displacement of the peak of magnetization due to the flux reversal produced by the magnetization of the yoke is also considered. These hybrid heterostructures formed by ferromagnetic and superconducting material have been applied in the construction of the rotor for a brushless AC motor. The design and construction of this machine was carried out within the framework of the TMR Network SUPERMACHINES. The rotor has been designed in a quadrupolar configuration by cutting large YBCO 'window frames' from seeded melt-textured single domain YBCO pellets. This rotor has been coupled to a conventional stator of copper coils wound on an iron armature. The stator can be excited both in bipolar or quadrupolar mode. We report on the behaviour of the motor after a field cooling process when excited in quadrupolar mode

  4. Observation of dark pulses in 10 nm thick YBCO nanostrips presenting hysteretic current voltage characteristics

    Science.gov (United States)

    Ejrnaes, M.; Parlato, L.; Arpaia, R.; Bauch, T.; Lombardi, F.; Cristiano, R.; Tafuri, F.; Pepe, G. P.

    2017-12-01

    We have fabricated several 10 nm thick and 65 nm wide YBa2Cu3O7-δ (YBCO) nanostrips. The nanostrips with the highest critical current densities are characterized by hysteretic current voltage characteristics (IVCs) with a direct bistable switch from the zero-voltage to the finite voltage state. The presence of hysteretic IVCs allowed the observation of dark pulses due to fluctuations phenomena. The key role of the bistable behavior is its ability to transform a small disturbance (e.g. an intrinsic fluctuation) into a measurable transient signal, i.e. a dark pulse. On the contrary, in devices characterized by lower critical current density values, the IVCs are non-hysteretic and dark pulses have not been observed. To investigate the physical origin of the dark pulses, we have measured the bias current dependence of the dark pulse rate: the observed exponential increase with the bias current is compatible with mechanisms based on thermal activation of magnetic vortices in the nanostrip. We believe that the successful amplification of small fluctuation events into measurable signals in nanostrips of ultrathin YBCO is a milestone for further investigation of YBCO nanostrips for superconducting nanostrip single photon detectors and other quantum detectors for operation at higher temperatures.

  5. Chemical characterization of melt-textured YBCO produced by hybrid powder metallurgy

    International Nuclear Information System (INIS)

    To, P.-C.; Meen, James K.

    2008-01-01

    Monolithic YBCO samples were made by traditional top-seeded melt-texturing processes from cold-milled mixtures of Y123 (YBa 2 Cu 3 O 7-δ ) and elemental Y. The bulk composition does not lie on the Y211 (Y 2 BaCuO 5 )-Y123 join so, formation of Y123 from liquid and Y211 is not an essentially isothermal process on cooling. The reaction liquid + Y211 = Y123 is a ternary reaction and occurs over several tens of degrees. The Y123 thus produced has a range in compositions - particularly in Cu:(Y + Ba) - which may reflect crystallization over the thermal interval. The liquid migrates to an invariant point at which CuO also crystallizes with complete loss of liquid. The presence of trains of CuO grains in the YBCO indicates the locations of the last liquids to be preserved in the sample. These trains are dominantly in an annulus 1-3 mm from the edge of the 20-mm diameter sample. Mapping the compositional variation in Y123 may allow mapping the path of crystallization of these monolithic YBCO samples

  6. Chemical characterization of melt-textured YBCO produced by hybrid powder metallurgy

    Energy Technology Data Exchange (ETDEWEB)

    To, P.-C. [Texas Center for Superconductivity and Department of Chemistry, University of Houston, 4800 Calhoun Street, Houston, TX 77035 (United States); Meen, James K. [Texas Center for Superconductivity and Department of Chemistry, University of Houston, 4800 Calhoun Street, Houston, TX 77035 (United States)], E-mail: jmeen@uh.edu

    2008-06-15

    Monolithic YBCO samples were made by traditional top-seeded melt-texturing processes from cold-milled mixtures of Y123 (YBa{sub 2}Cu{sub 3}O{sub 7-{delta}}) and elemental Y. The bulk composition does not lie on the Y211 (Y{sub 2}BaCuO{sub 5})-Y123 join so, formation of Y123 from liquid and Y211 is not an essentially isothermal process on cooling. The reaction liquid + Y211 = Y123 is a ternary reaction and occurs over several tens of degrees. The Y123 thus produced has a range in compositions - particularly in Cu:(Y + Ba) - which may reflect crystallization over the thermal interval. The liquid migrates to an invariant point at which CuO also crystallizes with complete loss of liquid. The presence of trains of CuO grains in the YBCO indicates the locations of the last liquids to be preserved in the sample. These trains are dominantly in an annulus 1-3 mm from the edge of the 20-mm diameter sample. Mapping the compositional variation in Y123 may allow mapping the path of crystallization of these monolithic YBCO samples.

  7. Sensitive YBCO nanoSQUIDs for the investigation of small spin systems

    Energy Technology Data Exchange (ETDEWEB)

    Mueller, Benedikt; Schwarz, Tobias; Woelbing, Roman; Martinez-Perez, Maria Jose; Kleiner, Reinhold; Koelle, Dieter [Tuebingen Univ. (Germany). Physikalisches Inst. and Center for Collective Quantum Phenomena in LISA+; Reiche, Christopher F.; Muehl, Thomas; Buechner, Bernd [Leibniz Institute for Solid State and Materials Research IFW Dresden (Germany)

    2015-07-01

    We report on advances in the realization of dc YBCO nanoSQUIDs for continuous measurement of magnetic nanoparticle magnetization loops in strong magnetic fields up to the Tesla range, applied in the plane of the SQUID loop at temperatures of 4 K and below. Our grain boundary junction based YBCO SQUIDs are patterned by focused ion beam milling and feature a constriction next to the SQUID loop, allowing for on-chip SQUID modulation and bias reversal readout schemes. Using numerical simulations based on London theory, the spin sensitivity S{sub μ}{sup 1/2} = S{sub Φ}{sup 1/2} / φ{sub μ} was improved by optimizing both the flux noise S{sub Φ}{sup 1/2} and the coupling factor φ{sub μ} = Φ / μ (Φ is the magnetic flux coupled into the SQUID loop by a particle with magnetic moment μ). For optimized experimental devices, flux noise levels down to 50 nΦ{sub 0} / Hz{sup 1/2} in the white noise limit have been achieved, corresponding to a calculated spin sensitivity of only a few μ{sub B} / Hz{sup 1/2}. Further, the magnetization reversal of a Fe filled carbon nanotube attached to a YBCO nanoSQUID was traced out.

  8. Nature of exponents found in the critical regime of YBCO

    International Nuclear Information System (INIS)

    Marhas, Manmeet Kaur; Saravanan, P.; Balakrishnan, K.; Srinivasan, R.; Kanjilal, D.; Metha, G.K.; Pai, S.P.; Pinto, R.; Vedvyas, M.; Ogale, S.B.; Mohan Rao, G.; Nathan, Senthil; Mohan, S.

    1997-01-01

    Full text: Fluctuation effects in electrical conductivity near T c is an important tool for studying the nature of phase transition in high T c ceramics. Probing critical regime by way of experiments demand data of good precision. Measurements were carried out on well characterised high T c films prepared by laser ablation and high pressure oxygen sputtering. High energy ion irradiation carried out to see the effect of disorder. Precise electrical resistivity measurements were carried out near T c with a temperature control accuracy better than 10 mK and large number of data points were collected in this regime. 100 MeV oxygen and 200 MeV Ag ions were used with varying fluences for irradiation at 77K. The data was analysed using existing models of critical fluctuation effects. The exponent of electrical conductivity in laser ablated thin films whose transition widths are less than 1 K was 1.33 and is independent of disorder caused by high energy ion irradiation and this could be identified as the exponent for excess conductivity in the critical intermediate charged fluctuation regime as proposed by Fisher. The exponent is around 2.7 in those films whose transition widths are greater than 1 K and also was independent of disorder and this could be identified as exponent in the para coherence regime

  9. XPS-nanocharacterization of organic layers electrochemically grafted on the surface of SnO_2 thin films to produce a new hybrid material coating

    International Nuclear Information System (INIS)

    Drevet, R.; Dragoé, D.; Barthés-Labrousse, M.G.; Chaussé, A.; Andrieux, M.

    2016-01-01

    Graphical abstract: An innovative hybrid material layer is synthesized by combining two processes. SnO_2 thin films are deposited by MOCVD on Si substrates and an organic layer made of carboxyphenyl moieties is electrochemically grafted by the reduction of a diazonium salt. XPS characterizations are carried out to assess the efficiency of the electrochemical grafting. Display Omitted - Highlights: • An innovative hybrid material layer is synthesized by combining two processes. • SnO_2 thin films are deposited by MOCVD on Si substrates. • An organic layer is electrochemically grafted by the reduction of a diazonium salt. • The efficiency of the grafting is accurately assessed by XPS. • Three electrochemical grafting models are proposed. - Abstract: This work presents the synthesis and the characterization of hybrid material thin films obtained by the combination of two processes. The electrochemical grafting of organic layers made of carboxyphenyl moieties is carried out from the reduction of a diazonium salt on tin dioxide (SnO_2) thin films previously deposited on Si substrates by metal organic chemical vapor deposition (MOCVD). Since the MOCVD experimental parameters impact the crystal growth of the SnO_2 layer (i.e. its morphology and its texturation), various electrochemical grafting models can occur, producing different hybrid materials. In order to evidence the efficiency of the electrochemical grafting of the carboxyphenyl moieties, X-ray Photoelectron Spectroscopy (XPS) is used to characterize the first nanometers in depth of the synthesized hybrid material layer. Then three electrochemical grafting models are proposed.

  10. Properties of alumina films prepared by metal-organic chemical vapour deposition at atmospheric pressure in hte presence of small amounts of water

    NARCIS (Netherlands)

    Haanappel, V.A.C.; Haanappel, V.A.C.; van Corbach, H.D.; Rem, J.B.; Fransen, T.; Gellings, P.J.

    1995-01-01

    Thin alumina films were deposited on stainless steel, type AISI 304. The deposition process was carried out in nitrogen with low partial pressures of water (0–2.6 × 10−2 kPa (0−0.20 mmHg)) by metal-organic chemical vapour deposition (MOCVD) with aluminium-tri-sec-butoxide (ATSB) as the precursor.

  11. Temperature Uniformity of Wafer on a Large-Sized Susceptor for a Nitride Vertical MOCVD Reactor

    International Nuclear Information System (INIS)

    Li Zhi-Ming; Jiang Hai-Ying; Han Yan-Bin; Li Jin-Ping; Yin Jian-Qin; Zhang Jin-Cheng

    2012-01-01

    The effect of coil location on wafer temperature is analyzed in a vertical MOCVD reactor by induction heating. It is observed that the temperature distribution in the wafer with the coils under the graphite susceptor is more uniform than that with the coils around the outside wall of the reactor. For the case of coils under the susceptor, we find that the thickness of the susceptor, the distance from the coils to the susceptor bottom and the coil turns significantly affect the temperature uniformity of the wafer. An optimization process is executed for a 3-inch susceptor with this kind of structure, resulting in a large improvement in the temperature uniformity. A further optimization demonstrates that the new susceptor structure is also suitable for either multiple wafers or large-sized wafers approaching 6 and 8 inches

  12. Deuterium permeation of amorphous alumina coating on 316L prepared by MOCVD

    Science.gov (United States)

    Li, Shuai; He, Di; Liu, Xiaopeng; Wang, Shumao; Jiang, Lijun

    2012-01-01

    The deuterium permeation behavior of the alumina coating on 316L stainless steel prepared by metal organic chemical vapor deposition (MOCVD) was investigated. The alumina coating was also characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscope (SEM). It was found that the as-prepared coating consisted of amorphous alumina. This alumina coating had a dense, crack-free and homogeneous morphology. Although the alumina coating was amorphous, effective suppression of deuterium permeation was demonstrated. The deuterium permeability of the alumina coating was 51-60 times less than that of the 316L stainless steel and 153-335 times less than that of the referred low activation martensitic steels at 860-960 K.

  13. Optical properties of hybrid quantum-well–dots nanostructures grown by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Mintairov, S. A., E-mail: mintairov@scell.ioffe.ru; Kalyuzhnyy, N. A.; Nadtochiy, A. M.; Maximov, M. V. [St. Petersburg Academic University (Russian Federation); Rouvimov, S. S. [University of Notre Dame (United States); Zhukov, A. E. [St. Petersburg Academic University (Russian Federation)

    2017-03-15

    The deposition of In{sub x}Ga{sub 1–x}As with an indium content of 0.3–0.5 and an average thickness of 3–27 single layers on a GaAs wafer by metalorganic chemical vapor deposition (MOCVD) at low temperatures results in the appearance of thickness and composition modulations in the layers being formed. Such structures can be considered to be intermediate nanostructures between ideal quantum wells and quantum dots. Depending on the average thickness and composition of the layers, the wavelength of the photoluminescence peak for the hybrid InGaAs quantum well–dots nanostructures varies from 950 to 1100 nm. The optimal average In{sub x}Ga{sub 1–x}As thicknesses and compositions at which the emission wavelength is the longest with a high quantum efficiency retained are determined.

  14. Pulsed injection metal organic chemical vapour deposition and characterisation of thin CaO films

    International Nuclear Information System (INIS)

    Borges, R.P.; Ferreira, P.; Saraiva, A.; Goncalves, R.; Rosa, M.A.; Goncalves, A.P.; Silva, R.C. da; Magalhaes, S.; Lourenco, M.J.V.; Santos, F.J.V.; Godinho, M.

    2009-01-01

    Thin films of CaO were grown on silicon (Si) and lanthanum aluminate (LaAlO 3 ) substrates by pulsed injection metal-organic chemical vapour deposition in a vertical injection MOCVD system. Growth parameters were systematically varied to study their effect on film growth and quality and to determine the optimal growth conditions for this material. Film quality and growth rate were evaluated by atomic force microscopy, X-ray diffraction and Rutherford Backscattering Spectroscopy measurements. Optimised conditions allowed growing transparent, single phase films textured along the (0 0 l) direction.

  15. Role of plasma activation in tailoring the nanostructure of multifunctional oxides thin films

    Energy Technology Data Exchange (ETDEWEB)

    Giangregorio, Maria M.; Losurdo, Maria; Capezzuto, Pio [Institute of Inorganic Methodologies and Plasmas, IMIP-CNR, and Department of Chemistry, University of Bari, via Orabona, 4-70125 Bari (Italy); Bruno, Giovanni [Institute of Inorganic Methodologies and Plasmas, IMIP-CNR, and Department of Chemistry, University of Bari, via Orabona, 4-70125 Bari (Italy)], E-mail: giovanni.bruno@ba.imip.cnr.it

    2009-03-01

    Potential of O{sub 2} remote plasmas for improving structural, morphological and optical properties of various multifunctional oxides thin films both during plasma assisted growth as well as by post-growth treatments is discussed. In particular, an O{sub 2} remote plasma metalorganic chemical vapor deposition (RP-MOCVD) route is presented for tailoring the structural, morphological and optical properties of Er{sub 2}O{sub 3} and ZnO films. Furthermore, post-growth room-temperature remote O{sub 2} plasma treatments of indium-tin-oxides (ITO) films are demonstrated to be effective in improving morphology of ITO films.

  16. Secondary phase formation in YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} thin films and YBa{sub 2}Cu{sub 3}O{sub 7-{delta}}/SrTiO{sub 3} superlattices

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, C.N.L.

    1996-06-01

    Studies of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) thin films and YBCO/STO superlattices has been performed. The dc magnetron sputtered YBCO single layer investigation concerned the dependence of the secondary phase formation and superconducting transport properties on sputtering target and ambient gas composition. YBCO/STO superlattices, grown by dc and rf magnetron sputtering, respectively, were analyzed with respect to microstructure and formation of secondary phases. The main characterization techniques used in this study have been x-ray diffraction to identify phases and to obtain orientational relationships, scanning electron microscopy to study surface morphology, transmission electron microscopy for microstructural characterization, and energy-dispersive x-ray spectroscopy for chemical characterization. With the aim to reduce or avoid the formation of copper-rich surface particles and still maintain satisfactory superconducting transport properties, YBCO films were deposited using copper-poor or yttrium-rich sputtering targets in an Ar:O{sub 2} or Ar:O{sub 2}:N{sub 2}O sputtering gas mixture. It was found that the use of yttrium-rich targets and N{sub 2}O in the sputtering gas is a reliable way to achieve smooth films without surface particles and with satisfactory superconducting properties, while the use of copper-poor targets and N{sub 2}O deteriorates those properties. Based on the previous results, YBCO/STO superlattices were grown using yttrium-rich YBCO targets and stoichiometric STO targets, respectively, in a Ar:O{sub 2}:N{sub 2}O sputtering gas mixture. The superlattices were found to have sharp interfaces and no indications of interface reactions were detected. 61 refs, 18 figs, 3 tabs

  17. Bi-epitaxial YBa2Cu3Ox Thin Films on Tilted-axes NdGaO3 Substrates with CeO2 Seeding Layer

    International Nuclear Information System (INIS)

    Mozhaev, P B; Mozhaeva, J E; Jacobsen, C S; Hansen, J Bindslev; Bdikin, I K; Luzanov, V A; Kotelyanskii, I M; Zybtsev, S G

    2006-01-01

    Bi-epitaxial YBa 2 Cu 3 O x (YBCO) thin films with out-of-plane tilt angle in the range 18 - 27 0 were manufactured using pulsed laser deposition on NdGaO 3 tilted-axes substrates with CeO 2 seeding layers. The YBCO thin film orientation over the seeding layer depended on deposition conditions. Removal of the seeding layer from part of the substrate surface by ionbeam etching resulted in formation of a bi-epitaxial thin film with different c-axis orientation of two parts of the film. The bi-epitaxial film orientation and structure were studied using X-ray diffraction techniques, and surface morphology was observed with atomic force microscope (AFM). Photolithography and ion-beam etching techniques were used for patterning bi-epitaxial thin films. Electrical characterization of the obtained structures was performed

  18. Epitaxial growth of SrTiO3 (001) films on multilayer buffered GaN (0002) by pulsed laser deposition

    International Nuclear Information System (INIS)

    Luo, W B; Jing, J; Shuai, Y; Zhu, J; Zhang, W L; Zhou, S; Gemming, S; Du, N; Schmidt, H

    2013-01-01

    SrTiO 3 films were grown on CeO 2 /YSZ/TiO 2 multilayer buffered GaN/Al 2 O 3 (0001) substrates with and without the YBa 2 Cu 3 O 7-x (YBCO) bridge layer by pulsed laser deposition (PLD). The deposition process of the buffer layers was in situ monitored by reflection high-energy electron diffraction. The crystallographical orientation of the heterostructure was studied by x-ray diffraction (XRD). With the introduction of the YBCO (001) layer, the STO (001) film was epitaxially grown on the GaN substrate. There were three sets of inplane domains separated from each other by 30° in both STO and YBCO buffer layers. The epitaxial relationship was STO (002)[110]∥YBCO(001)[110]∥CeO 2 (002)[010]∥YSZ (002)[010]∥GaN(0001)[1 1 -2 0] according to XRD results. By comparing the orientation of STO grown on GaN with and without the YBCO top buffer layer, the surface chemical bonding was found to be a very important factor in determining the orientation relationship of STO.

  19. Interface studies on the tunneling contact of a MOCVD-prepared tandem solar cell; Grenzflaechenuntersuchungen am Tunnelkontakt einer MOCVD-praeparierten Tandemsolarzelle

    Energy Technology Data Exchange (ETDEWEB)

    Seidel, U.

    2007-07-10

    In this thesis a tandem solar cell with a novel tunneling contact was developed. For the development of the monolithic preparation especailly critical hetero-interfaces were studied in the region of the tunneling contact with surface-sensitive measuring method. The tandem solar cell consisted of single solar cells with absorber layers of In{sub 0.53}Ga{sub 0.47}As (E{sub g}=0.73 eV) and In{sub 0.78}Ga{sub 0.22}As{sub 0.491}P{sub 0.51} (E{sub g}=1.03 eV), the serial switching of which was pursued with a tunneling contact (ESAKI diode, which consisted of a very thin n-doped InGaAs and a p-doped GaAsSb layer. The III-V semiconductor layers were prepared by metalorganic gas phase epitaxy (MOCVD) monocrystallinely on an InP(100) substrate lattice-matchedly. Especially the influence of the preparation of InGaAs surfaces on the sharpness of the InGaAs/GaAsSb interface was in-situ studied by reflection-anisotropy spectroscopy and after a contamination-free transfer into the ultrahigh vacuum with photoelectron spectroscopy and with low-energetic electron diffraction (LEED). Thereby for the first time three different reconstructions of the MOCVD-prepared InGaAs surfaces could be observed, which were dependent on the heating temperature under pure hydrogen. The arsenic-rich InGaAs surface was observed for temperatures less than 300 C and showed in the LEED picture a (4 x 3) reconstruction. In the temperature range from 300 C until about 500 C a (2 x 4) reconstruction was observed, above 500 C the InGaAs surface 94 x 2)/c(8 x 2) was reconstructed. Subsequently the study of the growth of thin GaAsSb layers on these three InGaAs surface reconstructions followed. XPS measurements showed that the Sb/As ratio in GaAsSb at the growth on the As-rich (4 x 3) reconstructed surface in the first monolayers was too low. The preparation of the GaAsSb on the two other InGaAs surfaces yielded however in both cases a distinctly higher Sb/As ratio. Finally tandem solar cells with differently

  20. Epitaxial growth and superconducting properties of YBa23Cu3O7 thin films and YBa2Cu3O7/Dy(Pr)Ba2Cu3O7 superlattices

    International Nuclear Information System (INIS)

    Triscone, J.M.; Brunner, O.; Antognazza, L.; Kent, A.D.; Fischer, O.; Karkut, M.G.

    1990-01-01

    The authors have prepared in situ REBa 2 Cu 3 O 7 (REBCO) (RE = Y, Pr, Dy) thin films and YBCO/Dy(Pr)BCO superlattices by single target dc planar magnetron sputtering. YBCO/DyBCO superlattices have been realized with modulation wavelength as short as 24 Angstrom, i.e., a unit cell of YBCO alternates with a unit cell of DyBCO, on average. The superconducting properties of such superlattices are indistinguishable from those of single layers. T co 's (zero resistance) are between 85 and 89K, and the residual resistivity ratios are between 2.5 and 3. In contrast to these results, when YBCO is layered with PrBCO, which is insulating, a dramatic change in the superconducting properties is observed. The authors have been able to artificially vary the coupling between single 12 Angstrom unit cell of YBCO by interposing insulating planes of PrBCO. As the YBCO layer separation increases, T c is reduced and the transition broadens showing evidence of 2-D superconducting fluctuations

  1. Influence of initial pH on the microstructure of YBa2Cu3O7−x superconducting thin films derived from DEA-aqueous sol–gel method

    DEFF Research Database (Denmark)

    Xiao, Tang; Yue, Zhao; Grivel, Jean-Claude

    2013-01-01

    A fluorine-free aqueous sol–gel technique was used to fabricate YBCO superconducting thin films. Acetic acid was added in order to modify the complexation process taking place between the metal cations and the organic chelating agents. The electrical resistance and the pH value were used as indic......A fluorine-free aqueous sol–gel technique was used to fabricate YBCO superconducting thin films. Acetic acid was added in order to modify the complexation process taking place between the metal cations and the organic chelating agents. The electrical resistance and the pH value were used...

  2. Oxygenation of the traditional and thin-walled MT-YBCO in flowing oxygen and under high evaluated oxygen pressure

    Energy Technology Data Exchange (ETDEWEB)

    Prikhna, Tatiana [Institute for Superhard Materials, 2 Avtozavodskaya Street, Kiev 04074 (Ukraine)], E-mail: prikhna@iptelecom.net.ua; Chaud, Xavier [CNRS/CRETA, 25, Avenue des Martyrs BP 166, 38042 Grenoble, Cedex 9 (France); Gawalek, Wolfgang [Institut fuer Physikalische Hochtechnologie, Albert-Einstein-Strasse 9, Jena (Germany); Rabier, Jaques [Universite de Poitiers, CNRS/Lab. de Metallurgie Physique, UMR 6630 CNRS-Universite de Poitiers SP2MI, BP 30179, F-86962 Chasseneuil Futuroscope Cedex (France); Savchuk, Yaroslav [Institute for Superhard Materials, 2 Avtozavodskaya Street, Kiev 04074 (Ukraine); Joulain, Anne [Universite de Poitiers, CNRS/Lab. de Metallurgie Physique, UMR 6630 CNRS-Universite de Poitiers SP2MI, BP 30179, F-86962 Chasseneuil Futuroscope Cedex (France); Vlasenko, Andrey; Moshchil, Viktor; Sergienko, Nina; Dub, Sergey; Melnikov, Vladimir [Institute for Superhard Materials, 2 Avtozavodskaya Street, Kiev 04074 (Ukraine); Litzkendorf, Doris; Habisreuther, Tobias [Institut fuer Physikalische Hochtechnologie, Albert-Einstein-Strasse 9, Jena (Germany); Sverdun, Vladimir [Institute for Superhard Materials, 2 Avtozavodskaya Street, Kiev 04074 (Ukraine)

    2007-09-01

    The high pressure-high temperature oxygenation of thin-walled MT-YBCO (with artificially produced holes) allows decreasing the amount of macrocracks and increasing j{sub c} of the material. The MT-YBCO produced from Y123 and Y211 in the fields higher than 2 T showed higher j{sub c} in the ab-planes and lower j{sub c} in the c-direction than the MT-YBCO manufactured from Y123 and Y{sub 2}O{sub 3} and can be explained by the difference in twin and microcrack density that in turn can be affected by the difference in Y211 phase distribution.

  3. YBa{sub 2}Cu{sub 3}O{sub 7-x} thin films prepared by chemical solution deposition

    Energy Technology Data Exchange (ETDEWEB)

    Apetrii, Claudia

    2009-11-25

    The discovery of superconductivity in ceramic materials by Bednorz and Mueller in early 1987, immediately followed by Wu et al., who showed that YBa{sub 2}Cu{sub 3}O{sub 7-x} (YBCO) becomes superconducting (92 K) well above the boiling point of nitrogen (77 K) created a great excitement in superconductivity research. Potential applications of high T{sub c}-superconductors require large critical currents and high-applied magnetic fields. Effective ways to increase the critical current density at high magnetic fields in YBCO are the introduction of nanoparticles and chemical substitution of yttrium by other rare earth elements. Since low costs and environmental compatibility are essential conditions for the preparation of long length YBCO films, the cost effective chemical solution deposition (CSD) procedure was selected, given that no vacuum technology is required. To reveal the flexibility and the good optimization possibilities of the CSD approach two main processes were chosen for comparison: a fluorine-free method, namely the polymer-metal precursor technique, and a fluorine-based method, the metalorganic deposition (MOD) using the trifluoroacetates (TFA) technique. Sharp transition temperature widths {delta}T{sub c} of 1.1 K for the polymer metal method, 0.8 K for TFA method and critical current densities J{sub c} of {approx}3.5 MA/cm{sup 2} shows that high quality YBCO thin films can be produced using both techniques. Especially interesting is the magnetic field dependence of the critical current density J{sub c}(B) of the Y(Dy)BCO (80 %) films showing that for the lower magnetic fields the critical current density J{sub c}(B) is higher for a standard YBCO film, but at fields higher than 4.5 T the critical current density J{sub c}(B) of Y(Dy)BCO is larger than that for the YBCO. Above 8 T, J{sub c}(B) of the Y(Dy)BCO film is more than one order of magnitude higher than in pure YBCO film. (orig.)

  4. Electrically conducting oxide buffer layers on biaxially textured nickel alloy tapes by reel-to-reel MOCVD process

    International Nuclear Information System (INIS)

    Stadel, O; Samoilenkov, S V; Muydinov, R Yu; Schmidt, J; Keune, H; Wahl, G; Gorbenko, O Yu; Korsakov, I E; Melnikov, O V; Kaul, A R

    2006-01-01

    Reel-to-reel MOCVD process for continuous growth of electrically conducting buffer layers on biaxially textured Ni5W tapes has been developed. The new buffer layer architechture is presented: 200 nm (La, Ba) 2 CuO 4 /40 nm (La, Ba)MnO 3 /Ni5W. Constituting layers with high structural quality have been grown on moving tapes (in plane FWHM ≤ 6 0 and out of plane FWHM ≤ 3 0 )

  5. Influence of pH during modified sol-gel process to synthesized pure phased YBCO

    International Nuclear Information System (INIS)

    Barekat Rezaee, S.; Daadmehr, V.; Saeb, F.; Falahati, S.

    2007-01-01

    Full text: Among numerous studies of high-Tc superconductor compound, the YBCO system is the most studied system. During 3 last decades synthesized of high quality pure homogeneous powder were done. One of these methods was modified citrate gel that was widely used to obtain nanosized single phase YBCO. One of the most important factors to yield pure product is adjustment of the pH during the gelation. Then in this work, we adjusted different pH for gelatin and compare phase purity and elemental composition by using XRD and EDS. To synthesize the YBCO, we used Nitrate of metal (Y, Ba, Cu) as precursor. stoichiometric (1:2:3) amount of metal nitrate were solved in distilled water and mixed with constant stirring, (for each equivalent gram of metal nitrate add one equivalent gram of citric acid) and stirred up to have unclear light blue solution and the ethylendiamine was added drop wise to adjust pH from 4.56 to 7.45. Then the solution was heated up 80 C to achieve viscous gel. The color changed from dark blue to purple according to pH. The gel was heated on furnace up to 520 C and kept for 2 hours. During heating the gel swell and filled the baker then special attention is needed to use over sized baker. Obtained powder was calcined for 22h at 900 C to yield homogeneous pure phase and then pellets with 1 sm diameter in 10 ton pressure were produced and sintered for 19 h at 930 C and annealed to room temperature in oxygen. Resistivity measurement using standard four probe technique exhibit Tc (zero) from 90 K to 94 K. The samples were discussed by XRD, SEM and EDS. (authors)

  6. Intermodulation distortion and surface resistance in impurity-doped YBCO and MgB{sub 2}

    Energy Technology Data Exchange (ETDEWEB)

    Agassi, Y.D. [Naval Surface Warfare Center, Carderock Division, Bethesda, MD 20817 (United States); Oates, D.E., E-mail: oates@ll.mit.edu [MIT-Lincoln Laboratory, Lexington, MA 02420 (United States)

    2014-11-15

    Highlights: • Calculations of impurity-doping effects on surface resistance and intermodulation distortion. • The calculations are compared with previously published measurements in YBCO and MgB{sub 2}. • Excellent agreement between calculations and experiments are shown. • The effects of the symmetry of the energy gap are presented and discussed. - Abstract: Calculations of the microwave intermodulation distortion (IMD) and surface resistance of impurity-doped YBCO, MgB{sub 2} and Nb are presented. These are qualitatively distinct superconductors due to their energy-gap symmetries, d-wave (ℓ = 2), i-wave (ℓ = 6) and s-wave (ℓ = 0), respectively. The calculations are compared with previously published IMD and surface-resistance measurements of impurity-doped YBCO and Nb. The agreement between the data and fitted calculations is excellent in all cases. In the absence of IMD and surface-resistance measurements for doped MgB{sub 2}, we present representative predictions. The calculations are based on a Green’s-function approach that yields analytical expressions for the penetration depth and the nonlinear kernel in the constitutive relation. This penetration-depth expression reproduces the measured T{sup 2} low-temperature variation for doped superconductors and the surface-resistance reduction over that of the pure material. Regarding the IMD in superconductors with a nodal energy gap, the effect of doping is to enhance its magnitude and suppress its low-temperature 1/T{sup 2} divergence predicted by the nonlinear Meissner effect.

  7. Monte Carlo simulation study of the positron contribution to displacements per atom production in YBCO superconductors

    International Nuclear Information System (INIS)

    Pinera, I.; Cruz, C.M.; Abreu, Y.; Leyva, A.

    2008-01-01

    The contribution from positrons to the displacements per atom (dpa) distribution induced by the gamma irradiation on YBCO superconducting slabs is presented. The procedure implemented previously by the authors was adapted to take into account the contribution from positrons to dpa induced by the gamma radiation. The results show that, when positrons are considered in the atom displacement process, the total dpa almost doubles at 10 MeV of incident gamma radiation. At that energy positrons contribute 7% more to the total dpa than electrons, although electrons maintain having the highest contribution up to about 8 MeV.

  8. HTS current lead units prepared by the TFA-MOD processed YBCO coated conductors

    International Nuclear Information System (INIS)

    Shiohara, K.; Sakai, S.; Ishii, Y.; Yamada, Y.; Tachikawa, K.; Koizumi, T.; Aoki, Y.; Hasegawa, T.; Tamura, H.; Mito, T.

    2010-01-01

    Two superconducting current lead units have been prepared using ten coated conductors of the Tri-Fluoro-Acetate - Metal Organic Deposition (TFA-MOD) processed Y 1 Ba 2 Cu 3 O 7-δ (YBCO) coated conductors with critical current (I c ) of about 170 A at 77 K in self-field. The coated conductors are 5 mm in width, 190 mm in length and about 120 μm in overall thickness. The 1.5 μm thick superconducting YBCO layer was synthesized through the TFA-MOD process on Hastelloy TM C-276 substrate tape with two buffer oxide layers of Gd 2 Zr 2 O 7 and CeO 2 . The five YBCO coated conductors are attached on a 1 mm thick Glass Fiber Reinforced Plastics (GFRP) board and soldered to Cu caps at the both ends. We prepared two 500 A-class current lead units. The DC transport current of 800 A was stably applied at 77 K without any voltage generation in all coated conductors. The voltage between both Cu caps linearly increased with increasing the applied current, and was about 350 μV at 500 A in both current lead units. According to the estimated values of the heat leakage from 77 K to 4.2 K, the heat leakage for the current lead unit was 46.5 mW. We successfully attained reduction of the heat leakage because of improvement of the transport current performance (I c ), a thinner Ag layer of YBCO coated conductor and usage of the GFRP board for reinforcement instead of a stainless steel board used in the previous study. The DC transport current of 1400 A was stably applied when the two current lead units were joined in parallel. The sum of the heat leakages from 77 K to 4.2 K for the combined the current lead units was 93 mW. In comparison with the conventional Cu current leads by gas-cooling, it could be noted that the heat leakage of the current lead is about one order of magnitude smaller than that of the Cu current lead.

  9. Measurement of oxygen disorder and nano-twin microstructure associated with columnar defects in YBCO

    International Nuclear Information System (INIS)

    Yan, Y.

    1998-01-01

    Studies of defects generated by high energy (>1 GeV) heavy ion irradiation in high-Tc superconductors have been performed by transmission electron microscopy (TEM). Our study shows that high dose irradiation leads to the formation of nano-twins, by which the columnar defects are connected. An analysis of the local Fourier components of the image intensity in [001] lattice images indicates that these new ''twin'' boundaries are much more diffuse than pre-existing twin boundaries in YBCO. The mechanism of the formation of nano-twin boundaries on {110} planes and their possible relation to superconducting properties are discussed

  10. Effects of electron irradiation on the resistive behaviour of YBCO-type ceramics

    International Nuclear Information System (INIS)

    Galatanu, A.; Novac, A.; Mosteanu, T.; Magureanu, M.

    1998-01-01

    YBCO-123 ceramic samples were irradiated with electron beams (E=0.5 MeV), the particle fluxes ranging between 10 15 and 10 19 e - /cm 2 . The induced structure modifications are analyzed through X-ray diffraction and their effects on the resistive behaviour are estimated. It is shown that a direct correlation can be established between the irradiation effects, oxygen disorder and hence the modification of the sample resistivity. A particular attention is given to the effects on the fluctuation mechanism arising near the transition temperature. (authors)

  11. AC susceptibility response of bulk YBCO superconductors in the presence of a temperature gradient

    International Nuclear Information System (INIS)

    Bodi, A.C.; Kirschner, I.

    1997-01-01

    Low-frequency AC susceptibility measurements on ceramic YBCO superconductors carried out at the presence of a quasi-one-dimensional temperature gradient are compared with those made without the temperature gradient. The values of the different characteristic temperatures measured on samples without and with a temperature gradient are identical but in the second case its characteristic temperature is a medium value. When the temperature gradient is constant on the sample the arithmetic medium value of the local temperatures is the effective characteristic temperature different phenomena. (orig.)

  12. Morphology, structure, and electrical properties of YBa2Cu3Ox thin films on tilted NdGaO3 substrates, deposited by DC-sputtering

    International Nuclear Information System (INIS)

    Mozhaev, Peter B.; Kotelyanskii, Iosif M.; Luzanov, Valery A.; Mozhaeva, Julia E.; Donchev, Todor; Mateev, Emil; Nurgaliev, Timur; Bdikin, Igor K.; Narymbetov, Bakhyt Zh.

    2005-01-01

    Thin YBa 2 Cu 3 O x (YBCO) films were deposited using DC-sputtering technique on NdGaO 3 substrates, tilted from (1 1 0) orientation by 0-26 deg . The structure and surface quality of the substrates were carefully characterized to obtain reliable results of thin films deposition. Structural, morphological and electrical properties of the YBCO thin films show three different ranges of inclination angle: vicinal, intermediate and high. In the vicinal range the properties of the film are generally the same as of the standard films deposited on (1 1 0) NdGaO 3 substrate. An increase of the inclination angle to the intermediate range results in a significant improvement of morphology and structural quality of the film. Best electrical parameters are measured for the films of the intermediate range also. Probable reason for such behavior is simultaneous and regular seeding of the film in the joints of facets on the substrate surface. Further increase of inclination angle leads to step bunching and oxygen out-diffusion, destroying both structural and electrical perfection of the tilted-axes YBCO film

  13. Yttrium-enriched YBa{sub 2}Cu{sub 3}O{sub x} thin films for coated conductors fabricated by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Khoryushin, Alexey V., E-mail: khoryushin@ya.ru [Department of Physics, Technical University of Denmark, DK-2800 Kgs. Lyngby (Denmark); Mozhaev, Peter B.; Mozhaeva, Julia E.; Andersen, Niels H. [Department of Physics, Technical University of Denmark, DK-2800 Kgs. Lyngby (Denmark); Grivel, Jean-Claude [Department of Energy Conversion and Storage, Technical University of Denmark, DK-4000 Roskilde (Denmark); Hansen, Jørn Bindslev; Jacobsen, Claus S. [Department of Physics, Technical University of Denmark, DK-2800 Kgs. Lyngby (Denmark)

    2013-02-14

    Highlights: ► YBCO films were fabricated by PLD from targets of various elemental compositions. ► The Y-enriched films contain yttria nanoparticles which provide efficient pinning. ► The best film has 5.5× higher j{sub c}(5 T,50 K) = 2.6MA/cm{sup 2} comparing with a reference film. ► The Y-enriched films remain c-oriented up to 500 nm. ► Films demonstrate no j{sub c} suppression with thickness and remarkable stability with time. -- Abstract: The effects of excess yttria on the structural and electrical properties of the YBa{sub 2}Cu{sub 3}O{sub x} (YBCO) thin films are studied. The films were deposited on (LaAlO{sub 3}){sub 0.3}–(Sr{sub 2}AlTaO{sub 8}){sub 0.7} substrates by pulsed laser ablation from targets with different elemental composition. An increase of yttrium content of the target leads to formation of porous films with significantly improved current-carrying capabilities. Structural studies of these films reveal presence of yttria nanoparticles embedded into the YBCO matrix. The highest obtained critical current density in an external magnetic field of 5 T was 2.6 MA/cm{sup 2} at 50 K and 9.4 MA/cm{sup 2} at 20 K. The fabricated Y-enriched YBCO films remain c-oriented at least up to 600 nm thickness with no significant suppression of the critical current density.

  14. Structural and superconducting characteristics of YBa2Cu3O7 films grown by fluorine-free metal-organic deposition route

    DEFF Research Database (Denmark)

    Zhao, Yue; Chu, Jingyuan; Qureishy, Thomas

    2018-01-01

    Microstructure and superconducting performance of YBa2Cu3O7 (YBCO) films deposited on LaAlO3 single crystal (LAO) substrates by a fluorine-free metal-organic deposition (FF-MOD) technique, have been studied by means of X-ray reciprocal space mapping (RSM), cross-sectional transmission electron mi...... external magnetic field at 77 K. This work offers an in-depth insight into the correlation between the microstructure and superconductivity in the MOD YBCO films.......Microstructure and superconducting performance of YBa2Cu3O7 (YBCO) films deposited on LaAlO3 single crystal (LAO) substrates by a fluorine-free metal-organic deposition (FF-MOD) technique, have been studied by means of X-ray reciprocal space mapping (RSM), cross-sectional transmission electron....... It is suggested that associated partial dislocations formed at the boundary between the stacking faults and YBCO matrix act as strong linear (or dot) pinning centers. These structural characteristics are well in line with the better superconducting performance of the low fluorine-MOD film, in particular under...

  15. Characterization of Microstructure and Performance of YBa2Cu3O7−x Films Synthesized Through Sol–Gel Aqueous Precursors with DEA/TEA Addition

    DEFF Research Database (Denmark)

    Tang, Xiao; He, Dong; Zhao, Yichun

    2013-01-01

    YBa2Cu3O7−x (YBCO) superconducting thin films are synthesized through non-fluorine sol–gel aqueous processes. Diethanolamine (DEA) and triethonalamine (TEA), which have similar molecular structures but different complexation abilities and molecular weights, are separately used as chelating agents...

  16. High index of refraction films for dielectric mirrors prepared by metal-organic chemical vapor deposition

    International Nuclear Information System (INIS)

    Brusasco, R.M.

    1989-01-01

    A wide variety of metal oxides with high index of refraction can be prepared by Metal-Organic Chemical Vapor Deposition. We present some recent optical and laser damage results on oxide films prepared by MOCVD which could be used in a multilayer structure for highly reflecting (HR) dielectric mirror applications. The method of preparation affects both optical properties and laser damage threshold. 10 refs., 8 figs., 4 tabs

  17. Anatase thin film with diverse epitaxial relationship grown on yttrium stabilized zirconia substrate by chemical vapor deposition

    International Nuclear Information System (INIS)

    Miyagi, Takahira; Ogawa, Tomoyuki; Kamei, Masayuki; Wada, Yoshiki; Mitsuhashi, Takefumi; Yamazaki, Atsushi

    2003-01-01

    An anatase epitaxial thin film with diverse epitaxial relationship, YSZ (001) // anatase (001), YSZ (010) // anatase (110), was grown on a single crystalline yttrium stabilized zirconia (YSZ) (001) substrate by metal organic chemical vapor deposition (MOCVD). The full width at half maximum (FWHM) of the (004) reflection of this anatase epitaxial film was 0.4deg, and the photoluminescence of this anatase epitaxial film showed visible emission with broad spectral width and large Stokes shift at room temperature. These results indicate that this anatase epitaxial film possessed almost equal crystalline quality compared with that grown under identical growth conditions on single crystalline SrTiO 3 substrate. (author)

  18. Pinning potentials of the vortex lattice in YBCO crystals in the peak effect region

    International Nuclear Information System (INIS)

    Pasquini, G.; Bekeris, V.

    2004-01-01

    Memory effects in the dynamic response of the vortex lattice (VL) in type II superconductors and its relationship with the controversial peak effect, have attracted great interest for a long time. In the last years, these features have been observed in YBCO single crystals, with the DC magnetic field tilted away from the twin planes and were related with robust dynamical states characterized by different degrees of mobility. Recently, we reported that the previous dynamical history of the VL can modify not only its dynamic response, but can even modify its static properties as well. In the present work, we try to understand the nature of the peak effect in YBCO crystals by sensing the effective AC penetration depth in the linear Campbell regime. We report history dependent effective pinning potential well curvatures and study the stability of the different static configurations. Interestingly, we observe that the more pinned VL configuration is not the more stable. Results agree with a dynamic scenario undergoing the Peak Effect

  19. Second Generation HTs Wire Based on RABiTS Substrates and MOD YBCO

    Energy Technology Data Exchange (ETDEWEB)

    Schoop, U. [American Superconductor Corporation, Westborough, MA; Rupich, Marty [American Superconductor Corporation, Westborough, MA; Thieme, C. L. H. [American Superconductor Corporation, Westborough, MA; Verebelyi, D. T. [American Superconductor Corporation, Westborough, MA; Zhang, W. [American Superconductor Corporation, Westborough, MA; Li, Xiaoping [American Superconductor Corporation, Westborough, MA; Kodenkandath, Thomas [American Superconductor Corporation, Westborough, MA; Nguyen, N. [American Superconductor Corporation, Westborough, MA; Siegal, E. E. [American Superconductor Corporation, Westborough, MA; Civale, L. [Los Alamos National Laboratory (LANL); Holesinger, T. G. [Los Alamos National Laboratory (LANL); Maiorov, B. [Los Alamos National Laboratory (LANL); Goyal, Amit [ORNL; Paranthaman, Mariappan Parans [ORNL

    2005-01-01

    The performance of Second Generation (2G) high temperature superconducting wire manufactured by continuous reel-to-reel processes is nearing the 300 A/cm-width (77 K, self field) performance threshold for commercial power cable applications. The 2G manufacturing approach under development at American Superconductor is based on the combination of the RABiTS substrate-buffer technology with metal organic deposition (MOD) of the YBCO layer. The capability of this process has been demonstrated in multiple 10 meter lengths with critical currents exceeding 250 A/cm-width with high uniformity and reproducibility. Critical currents of 380 A/cm-width have been achieved in short length samples prepared by the same basic process. The incorporation of nanoparticles ('nanodots') into the YBCO layer using the MOD process has resulted in a 2-fold improvement in the critical current at 65 K in a 3 T field. The research and development focus at ASMC is now directed toward the economical scale-up of the RABiTS/MOD process, optimization of the conductor properties for targeted applications and the use of 2G wire in initial demonstration applications.

  20. Preliminary experiments of a tubular linear actuator in the vertical direction using YBCO bulk

    Energy Technology Data Exchange (ETDEWEB)

    Sugawara, A; Ueda, H; Ishiyama, A [Department of Electrical Engineering and Bioscience, Waseda University, 3-4-1 Ohkubo, Shinjuku-ku, Tokyo 169-8555 (Japan)

    2004-05-01

    We have been developing a new type of active-maglev system composed of field-cooled disc-shaped YBCO bulk and multiple ring-shaped electromagnets, which are vertically piled up. One of the useful features of the active-maglev system is that the levitation height is adjustable by varying the operating current through an electromagnet. Maximum levitation height in stable levitation, however, is restricted by the magnetic field distribution produced by the electromagnet. To enhance the levitation height, we have fabricated and tested an active-maglev system with multiple ring-shaped electromagnets instead of using a larger single electromagnet. Up to now, we have reported the experimental results in a model active-maglev system composed of five electromagnets and showed that the levitation height, as well as stability, can be remarkably improved by adjusting the operating current of each electromagnet individually. In this study, we constructed a model system operated as a tubular linear synchronous actuator in the vertical direction in expectation of it being applied in factory automation upgrading. The primary consists of six ring-shaped copper-winding coils without iron core and is supplied with three-phase sinusoidal excitation. A disc-shaped YBCO bulk, which was magnetized by a field-cooling process, was adopted as a secondary (mover). We carried out preliminary experiments to confirm the feasibility of synchronous operation and also numerically investigated the electromagnetic phenomenon within the bulk superconductor by a developed computer program based on the finite element method.

  1. Preliminary experiments of a tubular linear actuator in the vertical direction using YBCO bulk

    International Nuclear Information System (INIS)

    Sugawara, A; Ueda, H; Ishiyama, A

    2004-01-01

    We have been developing a new type of active-maglev system composed of field-cooled disc-shaped YBCO bulk and multiple ring-shaped electromagnets, which are vertically piled up. One of the useful features of the active-maglev system is that the levitation height is adjustable by varying the operating current through an electromagnet. Maximum levitation height in stable levitation, however, is restricted by the magnetic field distribution produced by the electromagnet. To enhance the levitation height, we have fabricated and tested an active-maglev system with multiple ring-shaped electromagnets instead of using a larger single electromagnet. Up to now, we have reported the experimental results in a model active-maglev system composed of five electromagnets and showed that the levitation height, as well as stability, can be remarkably improved by adjusting the operating current of each electromagnet individually. In this study, we constructed a model system operated as a tubular linear synchronous actuator in the vertical direction in expectation of it being applied in factory automation upgrading. The primary consists of six ring-shaped copper-winding coils without iron core and is supplied with three-phase sinusoidal excitation. A disc-shaped YBCO bulk, which was magnetized by a field-cooling process, was adopted as a secondary (mover). We carried out preliminary experiments to confirm the feasibility of synchronous operation and also numerically investigated the electromagnetic phenomenon within the bulk superconductor by a developed computer program based on the finite element method

  2. Estimation of magnetic relaxation property for CVD processed YBCO-coated conductors

    International Nuclear Information System (INIS)

    Takahashi, Y.; Kiuchi, M.; Otabe, E.S.; Matsushita, T.; Shikimachi, K.; Watanabe, T.; Kashima, N.; Nagaya, S.

    2010-01-01

    Ion Beam Assist Deposition/Chemical Vapor Deposition(IBAD/CVD)-processed YBCO-coated conductors with high critical current density J c at high magnetic fields are expected to be applied to superconducting equipments such as superconducting magnetic energy storage (SMES). For application to superconducting magnet in SMES one of the most important properties for superconductors is the relaxation property of superconducting current. In this paper, the relaxation property is investigated for IBAD/CVD-processed YBCO-coated conductors of the superconducting layer in the range of 0.18-0.90 μm. This property can be quantitatively characterized by the apparent pinning potential, U 0 *. It is found that U 0 * takes a smaller value due to the two-dimensional pinning mechanism at high magnetic fields for conductor with thinner superconducting layer. Although U 0 * decreases with increasing thickness at low magnetic fields at 20 K, it increases at high magnetic fields. The results are theoretically explained by the model of the flux creep and flow based on the dimensionality of flux pinning. Scaling analysis is examined for the dependence of U 0 * on the magnetic field, temperature and the layer thickness.

  3. Inkjet printing of multifilamentary YBCO for low AC loss coated conductors

    International Nuclear Information System (INIS)

    Hopkins, S C; Joseph, D; Mitchell-Williams, T B; Glowacki, B A; Calleja, A; Vlad, V R; Vilardell, M; Ricart, S; Granados, X; Puig, T; Obradors, X; Usoskin, A; Falter, M; Bäcker, M

    2014-01-01

    Considerable progress has been made with the development of REBCO coated conductors in recent years, and high performance conductors are available commercially. For many applications, however, the cost remains prohibitive, and AC losses discourage their selection for higher frequency applications. Chemical solution deposition (CSD) methods are attractive for low-cost, scalable preparation of buffer and superconductor layers, and in many respects inkjet printing is the method of choice, permitting non-contact deposition with minimal materials wastage and excellent control of coating thickness. Highly textured coatings of YBCO and Gd-doped CeO 2 have previously been reported on buffered metal substrates. Inkjet printing also introduces the possibility of patterning - directly depositing two and three dimensional structures without subtractive processing - offering a low-cost route to coated conductors with reduced AC losses. In this contribution, the inkjet deposition of superconducting YBCO tracks is reported on industrially relevant buffered metal substrates both by direct printing and an inverse patterning approach. In the latter approach, ceria tracks were printed reported, which are a candidate both for resistive filament spacers and buffer layers. TFA-based precursor solutions have been printed on SS/ABAD-YSZ/CeO 2 and Ni-W/LZO/CeO 2 RABiTS substrates, and the resulting multifilamentary samples characterised by microscopy and scanning Hall probe measurements. The prospects for future inkjet-printed low AC loss coated conductors are discussed, including control of interfilamentary resistivity and bridging, transposed filamentary structures and stabilisation material.

  4. Single domain YBCO/Ag bulk superconductors fabricated by seeded infiltration and growth

    International Nuclear Information System (INIS)

    Iida, K; Babu, N H; Shi, Y; Cardwell, D A; Miyazaki, T; Murakami, M; Sakai, N

    2008-01-01

    We have applied the seeded infiltration and growth (IG) technique to the processing of samples containing Ag in an attempt to fabricate Ag-doped Y-Ba-Cu-O (YBCO) bulk superconductors with enhanced mechanical properties. The IG technique has been used successfully to grow bulk Ag-doped YBCO superconductors of up to 25 mm in diameter in the form of single grains. The distribution of Ag in the parent Y-123 matrix fabricated by the IG technique is observed to be at least as uniform as that in samples grown by conventional top seeded melt growth (TSMG). Fine Y-211 particles were observed to be embedded within the Y-123 matrix for the IG processed samples, leading to a high critical current density, J c , of over 70 kA/cm 2 at 77.3 K in self-field. The distribution of Y-211 in the IG sample microstructure, however, is inhomogeneous, which leads to a variation in the spatial distribution of J c throughout the bulk matrix. A maximum-trapped field of around 0.43 T at 1.2 mm above the sample surface (i.e. including 0.7 mm for the sensor mould thickness) is observed at liquid nitrogen temperature, despite the relatively small grain size of the sample (20 mm diameter x 7 mm thickness)

  5. Bi-epitaxial YBa{sub 2}Cu{sub 3}O{sub x} Thin Films on Tilted-axes NdGaO{sub 3} Substrates with CeO{sub 2} Seeding Layer

    Energy Technology Data Exchange (ETDEWEB)

    Mozhaev, P B [Institute of Physics and Technology RAS, 117218, Moscow (Russian Federation); Mozhaeva, J E [Institute of Physics and Technology RAS, 117218, Moscow (Russian Federation); Jacobsen, C S [Technical University of Denmark, Physics Department, Lyngby, DK-2800, Denmark (Denmark); Hansen, J Bindslev [Technical University of Denmark, Physics Department, Lyngby, DK-2800, Denmark (Denmark); Bdikin, I K [CICECO, University of Aveiro, Aveiro, 3810-193 (Portugal); Luzanov, V A [Institute of Radio Engineering and Electronics, Moscow, 125009 (Russian Federation); Kotelyanskii, I M [Institute of Radio Engineering and Electronics, Moscow, 125009 (Russian Federation); Zybtsev, S G [Institute of Radio Engineering and Electronics, Moscow, 125009 (Russian Federation)

    2006-06-01

    Bi-epitaxial YBa{sub 2}Cu{sub 3}O{sub x} (YBCO) thin films with out-of-plane tilt angle in the range 18 - 27{sup 0} were manufactured using pulsed laser deposition on NdGaO{sub 3} tilted-axes substrates with CeO{sub 2} seeding layers. The YBCO thin film orientation over the seeding layer depended on deposition conditions. Removal of the seeding layer from part of the substrate surface by ionbeam etching resulted in formation of a bi-epitaxial thin film with different c-axis orientation of two parts of the film. The bi-epitaxial film orientation and structure were studied using X-ray diffraction techniques, and surface morphology was observed with atomic force microscope (AFM). Photolithography and ion-beam etching techniques were used for patterning bi-epitaxial thin films. Electrical characterization of the obtained structures was performed.

  6. Mechanical and Magnetic Properties of YBCO Superconductor with Bi/CNT Composite and Resin/CNT Impregnation

    International Nuclear Information System (INIS)

    Oh, W. S.; Jang, G. E.; Han, Y. H.; Sung, T. H.

    2007-01-01

    Bi/CNT composite and resin/CNT were chosen to improve the mechanical properties of YBa 2 Cu 3 O 7 (YBCO) superconductor. In order to elucidate the effects of Bi/CNT composite and resin/CNT in YBCO superconductors, melt texture superconductor were impregnated by mixed compound of Bi and CNT into the artificial holes parallel to the c-axis, which were drilled on the YBCO superconductor. Various amount of Bi/CNT and resin/CNT were impregnated to YBCO superconductor with different holes diameters. Typical artificial holes diameters were 0.5, 0.7, and 1.0 mm respectively. Result of three-point bending test measurement, the bending strength with resin/CNT impregnation was improved up to 59.64 MPa as compared with 50.79 MPa of resin/CNT free bulk. Resin/CNT impregnation has been found to be one of the effective ways in improving the mechanical properties of bulk superconductor.

  7. Study of the inhomogeneous characteristics of modified YBa_2Cu_3O_7_-_d thin films and (YBa_2Cu_3O_7_-_d /LaAlO_3)_n superlattices: growth and properties

    International Nuclear Information System (INIS)

    Thimont, Yohann

    2009-01-01

    This manuscript is devoted to the study of crystallographic and physical properties of superconductor YBCO thin films and superconductor/insulator (YBCO/LAO)_n superlattices. The first stage of this work was to optimize the YBCO thin film deposition. Elaboration of a new physical model allows us to determine a critical temperature distribution inside the films thickness. Nevertheless, no homogeneous critical temperature inside the films can be obtained. This work shows that the interface strains modify the crystallographic and physical properties. We developed a new simulation method concerning the XRD peak shape analysis which allows us to determine YBCO cell deformation profile along the c-bar axis. About superlattices, effects of thickness on the physical and structural properties have been noticed. Transmission Electron Microscopy exhibits existence of structural defects in the films. Ending, the physical model proposed in the present work provides important information regarding the magnetic interaction between two superconductor layers, which seems to limit application of these superlattices in the realization of complex electronic devices. (author) [fr

  8. An evaluation of phase separated, self-assembled LaMnO3-MgO nanocomposite films directly on IBAD-MgO as buffer layers for flux pinning enhancements in YBa2YCu3O7-& coated conductors

    Energy Technology Data Exchange (ETDEWEB)

    Polat, Ozgur [ORNL; Aytug, Tolga [ORNL; Paranthaman, Mariappan Parans [ORNL; Leonard, Keith J [ORNL; Lupini, Andrew R [ORNL; Pennycook, Stephen J [ORNL; Meyer III, Harry M [ORNL; Kim, Kyunghoon [ORNL; Qiu, Xiaofeng [ORNL; Cook, Sylvester W [ORNL; Thompson, James R [ORNL; Christen, David K [ORNL; Goyal, Amit [ORNL; Selvamanickam, V. [SuperPower Incorporated, Schenectady, New York; Xiong, X. [SuperPower Incorporated, Schenectady, New York

    2010-01-01

    Technological applications of high temperature superconductors (HTS) require high critical current density, Jc, under operation at high magnetic field strengths. This requires effective flux pinning by introducing artificial defects through creative processing. In this work, we evaluated the feasibility of mixed-phase LaMnO3:MgO (LMO:MgO) films as a potential cap buffer layer for the epitaxial growth and enhanced performance of YBa2Cu3O7-d (YBCO) films. Such composite films were sputter deposited directly on IBAD-MgO templates (with no additional homo-epitaxial MgO layer) and revealed the formation of two phase-separated, but at the same time vertically aligned, self-assembled composite nanostructures that extend throughout the entire thickness of the film. The YBCO coatings deposited on these nanostructured cap layers showed correlated c-axis pinning and improved in-field Jc performance compared to those of YBCO films fabricated on standard LMO buffers. Microstructural characterization revealed additional extended disorder in the YBCO matrix. The present results demonstrate the feasibility of novel and potentially practical approaches in the pursuit of more efficient, economical, and high performance superconducting devices.

  9. LaNiO(3) Buffer Layers for High Critical Current Density YBa(2)Cu(3)O(7-delta) and Tl(2)Ba(2)CaCu(2)O(8-delta) Films

    Energy Technology Data Exchange (ETDEWEB)

    Carlson, C.M.; Parilla, P.A.; Siegal, M.P.; Ginley, D.S.; Wang, Y.-T.; Blaugher, R.D.; Price, J.C.; Overmyer, D.L.; Venturini, E.L.

    1999-08-24

    We demonstrate high critical current density superconducting films of YBa{sub 2}Cu{sub 3}O{sub 7{minus}{delta}} (YBCO) and Tl{sub 2}Ba{sub 2}CaCu{sub 2}O{sub 8{minus}{delta}} (Tl-2212) using LaNiO{sub 3} (LNO) buffer layers. YBCO films grown on an LNO buffer layer have only a slightly lower J{sub c} (5K, H=0) than films grown directly on a bare LaAlO{sub 3} substrate. It is noteworthy that YBCO films grown on LNO buffer layers exhibit minor microstructural disorder and enhanced flux pinning. LNO-buffered Tl-2212 samples show large reductions in J{sub c} at all temperatures and fields compared to those grown on bare LaAlO{sub 3}, correlating to both a-axis grain and nonsuperconducting phase formation. With additional optimization, LNO could be a promising buffer layer for both YBCO and Tl-based superconducting films, perhaps ideally suited for coated conductor applications.

  10. Carbon analysis in MOCVD grown HgCdMnTe by charged particle activation

    International Nuclear Information System (INIS)

    Stannard, W.B.; Walker, S.R.; Johnston, P.N.; Bubb, I.F.

    1994-01-01

    Charged Particle Activation Analysis (CPAA) has been used for the determination of the concentration of carbon in HgCdMnTe grown by Metal Organic Chemical Vapour Deposition (MOCVD). The samples were irradiated with a beam of 3.0 MeV 3 He ions. 11 C is produced by the reaction 12 C( 3 He, α) 11 C and is a positron (β + ) emitting radionuclide with a half-life of 20.38 min. At the same time the reaction 16 O( 3 He, p) 18 F produces 18 F which is also a β + emitter and has a half-life of 109.72 min. A post-irradiation etching technique has been developed to enable removal of surface contaminants. The radioactivity is determined by a β + spectrometer consisting of two NaI γ-ray detectors (3x3 in.) oriented at 180 . The two coincident 511 keV γ-rays emitted at 180 during the positron annihilation are detected. The initial 11 C and 18 F activities, and hence the oxygen and carbon contributions, can be separated by analysis of the count rate versus time. Analysis shows significant carbon levels in the HgCdMnTe samples. ((orig.))

  11. Wurtzite InP nanowire arrays grown by selective area MOCVD

    International Nuclear Information System (INIS)

    Chu, Hyung-Joon; Stewart, Lawrence; Yeh, Ting-Wei; Dapkus, P.D.

    2010-01-01

    InP nanowires are a unique material phase because this normally zincblende material forms in the wurtzite crystal structure below a critical diameter owing to the contribution of sidewalls to the total formation energy. This may allow control of the carrier transport and optical properties of InP nanowires for applications such as nano scale transistors, lasers and detectors. In this work, we describe the fabrication of InP nanowire arrays by selective area growth using MOCVD in the diameter range where the wurtzite structure is formed. The spatial growth rate in selective area growth is modeled by a diffusion model for the precursors. The proposed model achieves an average error of 9%. Electron microscopy shows that the grown InP nanowires are in the wurtzite crystal phase with many stacking faults. The threshold diameter of the crystal phase transition of InP nanowires is larger than the thermodynamic estimation. In order to explain this tendency, we propose a surface kinetics model based on a 2 x 2 reconstruction. This model can explain the increased tendency for wurtzite nanowire formation on InP (111)A substrates and the preferred growth direction of binary III-V compound semiconductor nanowires. (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  12. Model Research On Deposition Of Pure Aluminium Oxide Layers By MOCVD Method

    Directory of Open Access Journals (Sweden)

    Sawka A.

    2015-06-01

    Full Text Available The purpose of this research is to develop an optimal method for synthesizing of nanocrystalline Al2O3 monolayers at high growth rates on cemented carbides coated with an intermediate layer of pre-Al2O3-C (composite layers Al2O3-C/Al2O3. The use of quartz glass substrate allows for obtaining information about the quality of the layers such the thickness and density, because of its high transparency. The Al2O3 layers that do not containing carbon were synthesized on quartz glass by MOCVD using aluminum acetylacetonate and air as the reactants at temperatures of 700-1000°C. Argon was also a carrier gas. The resulting layers were transparent, as homogeneous nucleation did not occur during the synthesis process. The layers synthesized at lower temperatures were subjected to a crystallization process at temperatures above 900°C. The crystallization process was studied as a function of time and temperature. The obtained layers were characterized by their nanocrystalline microstructure.

  13. Induction-heating MOCVD reactor with significantly improved heating efficiency and reduced harmful magnetic coupling

    KAUST Repository

    Li, Kuang-Hui; Alotaibi, Hamad S.; Sun, Haiding; Lin, Ronghui; Guo, Wenzhe; Torres-Castanedo, Carlos G.; Liu, Kaikai; Galan, Sergio V.; Li, Xiaohang

    2018-01-01

    In a conventional induction-heating III-nitride metalorganic chemical vapor deposition (MOCVD) reactor, the induction coil is outside the chamber. Therefore, the magnetic field does not couple with the susceptor well, leading to compromised heating efficiency and harmful coupling with the gas inlet and thus possible overheating. Hence, the gas inlet has to be at a minimum distance away from the susceptor. Because of the elongated flow path, premature reactions can be more severe, particularly between Al- and B-containing precursors and NH3. Here, we propose a structure that can significantly improve the heating efficiency and allow the gas inlet to be closer to the susceptor. Specifically, the induction coil is designed to surround the vertical cylinder of a T-shaped susceptor comprising the cylinder and a top horizontal plate holding the wafer substrate within the reactor. Therefore, the cylinder coupled most magnetic field to serve as the thermal source for the plate. Furthermore, the plate can block and thus significantly reduce the uncoupled magnetic field above the susceptor, thereby allowing the gas inlet to be closer. The results show approximately 140% and 2.6 times increase in the heating and susceptor coupling efficiencies, respectively, as well as a 90% reduction in the harmful magnetic flux on the gas inlet.

  14. Integrated MSM-FET photoreceiver fabricated on MOCVD grown Hg2-xCdxTe

    International Nuclear Information System (INIS)

    Leech, P.W.; Gwynn, P.J.; Pain, G.N.; Petkovic, N.R.; Thompson, J.; Jamieson, D.N.

    1991-01-01

    This paper reports on progress in the monolithic integration of a metal-semiconductor-metal (MSM) detector and transimpedance amplifier and of a photoconductive detector (PCD) with a metal-semiconductor field effect transistor (MESFET) in Hg 1-x Cd x Te. The layers of CdTe/n-type Hg 1-x Cd x Te were grown by MOCVD on semi-insulating GaAs substrates (2 0 misoriented 100). Fabrication of the devices was by an FET planar process; with a standard lift-off used to form Schottky metallization on both the interdigitated electrodes of the MSM detector (2 μm width, 2 μm spacing) and the gate of the MESFETs (5μm length, 100μm width). The MSM photodetectors exhibited breakdown voltages in the range 60 to 80V, a dark current of 10na at 5V bias, and responsivities of >1.0 A/W measured at 40V using CW 1.3 μm illumination

  15. Induction-heating MOCVD reactor with significantly improved heating efficiency and reduced harmful magnetic coupling

    KAUST Repository

    Li, Kuang-Hui

    2018-02-23

    In a conventional induction-heating III-nitride metalorganic chemical vapor deposition (MOCVD) reactor, the induction coil is outside the chamber. Therefore, the magnetic field does not couple with the susceptor well, leading to compromised heating efficiency and harmful coupling with the gas inlet and thus possible overheating. Hence, the gas inlet has to be at a minimum distance away from the susceptor. Because of the elongated flow path, premature reactions can be more severe, particularly between Al- and B-containing precursors and NH3. Here, we propose a structure that can significantly improve the heating efficiency and allow the gas inlet to be closer to the susceptor. Specifically, the induction coil is designed to surround the vertical cylinder of a T-shaped susceptor comprising the cylinder and a top horizontal plate holding the wafer substrate within the reactor. Therefore, the cylinder coupled most magnetic field to serve as the thermal source for the plate. Furthermore, the plate can block and thus significantly reduce the uncoupled magnetic field above the susceptor, thereby allowing the gas inlet to be closer. The results show approximately 140% and 2.6 times increase in the heating and susceptor coupling efficiencies, respectively, as well as a 90% reduction in the harmful magnetic flux on the gas inlet.

  16. An RBS study of thin PLD and MOCVD strontium copper oxide layers

    Energy Technology Data Exchange (ETDEWEB)

    Kantor, Z. [Institute of Physics, University of Pannonia, H-8200 Veszprem (Hungary); Papadopoulou, E.L.; Aperathitis, E. [Inst. Electronic Struture and Laser, Foundation for Research and Technology - Hellas, P.O. Box 1527, Heraklion 71110 (Greece); Deschanvres, J.-L. [LMPG INP Grenoble-Minatec, BP 257, 38016 Grenoble Cedex 1 (France); Somogyi, K. [MicroVacuum Ltd., Kerekgyarto u.: 10, H-1147 Budapest (Hungary)], E-mail: karoly.somogyi@microvacuum.com; Szendro, I. [MicroVacuum Ltd., Kerekgyarto u.: 10, H-1147 Budapest (Hungary)

    2008-09-30

    Strontium copper oxide (SCO) has been studied as p-type transparent (VIS) conductive oxide material. Also theoretical studies suggested p-type conductivity of the SrCu{sub 2}O{sub 2} composition. SCO thin layers, with thicknesses of 30-2000 nm, were deposited on glass and silicon substrates both by pulsed laser deposition (PLD) and by MOCVD method. The as-grown layers showed high electrical resistance. Due to an annealing process, the resistivity significantly decreased and the layers showed p-type conductivity. Optical transparency measured on samples grown on glass substrates was found about or above 80%, including also thickness dependence. RBS measurements were applied for the determination of the chemical composition profile of the layers. A comparison revealed some specific differences between as-grown and annealed PLD samples. Due to the annealing, the ratio of oxide phases was changed and a vertical inhomogeneity in chemical composition was observed. Our measurements revealed also the influence of the deposition technique and of the substrate.

  17. The controlled growth of GaN microrods on Si(111) substrates by MOCVD

    Science.gov (United States)

    Foltynski, Bartosz; Garro, Nuria; Vallo, Martin; Finken, Matthias; Giesen, Christoph; Kalisch, Holger; Vescan, Andrei; Cantarero, Andrés; Heuken, Michael

    2015-03-01

    In this paper, a selective area growth (SAG) approach for growing GaN microrods on patterned SiNx/Si(111) substrates by metal-organic chemical vapor deposition (MOCVD) is studied. The surface morphology, optical and structural properties of vertical GaN microrods terminated by pyramidal shaped facets (six { 10 1 bar 1} planes) were characterized using scanning electron microscopy (SEM), room temperature photoluminescence (PL) and Raman spectroscopy, respectively. Measurements revealed high-quality GaN microcolumns grown with silane support. Characterized structures were grown nearly strain-free (central frequency of Raman peak of 567±1 cm-1) with crystal quality comparable to bulk crystals (FWHM=4.2±1 cm-1). Such GaN microrods might be used as a next-generation device concept for solid-state lighting (SSL) applications by realizing core-shell InGaN/GaN multi-quantum wells (MQWs) on the n-GaN rod base.

  18. Bi-epitaxial tilted out-of-plane YBCO junctions on NdGaO{sub 3} substrates with YSZ seeding layer

    Energy Technology Data Exchange (ETDEWEB)

    Mozhaev, P.B. (Institute of Physics and Technology RAS, Moscow (Russian Federation)); Mozhaev, J.E.; Bindslev Hansen, J.; Jacobsen, C.S. (Technical Univ. of Denmark, Dept. of Physics, Kgs. Lyngby (Denmark)); Kotelyanskil, I.M.; Luzanov, V.A. (Institute of Radio Engineering and Electronics RAS, Moscow (Russian Federation)); Benacka, S.; Strbik, V. (Institute of Electrical Engineering SAS, Bratislava (SK))

    2008-10-15

    Bi-epitaxial junctions with out-of plane tilt of the c axis were fabricated of YBCO superconducting thin films on NdGaO{sub 3} substrates with different miscut angles. Bi-epitaxial growth was provided by implementation of an Y:ZrO{sub 2} seeding layer on a certain part of the substrate. Junctions with different orientation of the bi-epitaxial boundaries were fabricated, their DC electrical properties were studied as a function of the boundary orientation angle. The junctions showed extremely high critical current densities for all tested miscut angles and bi-epitaxial boundary orientations (about 105 A/cm2 at 77 K and up to 106 A/cm2 at 4.2 K). The dependence of critical current density on the bi-epitaxial boundary orientation angle may be explained as an effect of a d-wave pairing mechanism in the HTSC with the simple Sigrist-Rice model. The studied boundaries may be considered as model structures for the grain boundaries in the coated conductors. (au)

  19. Probing localized strain in solution-derived YB a2C u3O7 -δ nanocomposite thin films

    Science.gov (United States)

    Guzman, Roger; Gazquez, Jaume; Mundet, Bernat; Coll, Mariona; Obradors, Xavier; Puig, Teresa

    2017-07-01

    Enhanced pinning due to nanoscale strain is unique to the high-Tc cuprates, where pairing may be modified with lattice distortion. Therefore a comprehensive understanding of the defect landscape is required for a broad range of applications. However, determining the type and distribution of defects and their associated strain constitutes a critical task, and for this aim, real-space techniques for atomic resolution characterization are necessary. Here, we use scanning transmission electron microscopy (STEM) to study the atomic structure of individual defects of solution-derived YB a2C u3O7 (YBCO) nanocomposites, where the inclusion of incoherent secondary phase nanoparticles within the YBCO matrix dramatically increases the density of Y1B a2C u4O8 (Y124) intergrowths, the commonest defect in YBCO thin films. The formation of the Y124 is found to trigger a concatenation of strain-derived interactions with other defects and the concomitant nucleation of intrinsic defects, which weave a web of randomly distributed nanostrained regions that profoundly transform the vortex-pinning landscape of the YBCO nanocomposite thin films.

  20. Microstructural Characterisation of Cuprate/Manganate Films on (110) SrTiO3 Deposited by Laser Ablation

    International Nuclear Information System (INIS)

    Tse, Y Y; Chakalov, R I; Joshi, M M; Jones, I P; Muirhead, C M; Palai, R

    2006-01-01

    Cross-sectional TEM and microanalysis were carried out to understand at a microscopic level the effects of microstructure and chemistry on the physical properties of manganites and manganite/cuprate films. TEM observations on pure LCMO grown on a (110) STO substrate were carried out first to determine the defect structure and detect any formation of second phase precipitates, as well as microstructural changes not detectable by X-ray reflections. La 0.7 Ca 0.3 MnO 3 (LCMO) grows epitaxially on a (110) SrTiO 3 (STO) substrate. HRTEM reveals a nearly defect-free interface between LCMO and STO with a few irregularly arranged misfit dislocations. The microstructure obtained from laser ablated nanometre scaled La 0.7 Ca 0.3 MnO 3 (LCMO)/YBa 2 Cu 3 O 7 -δ (YBCO)/PrBa 2 Cu 3 O 7 (PBCO) multilayers on (110) STO was also studied. Diffraction patterns show that all films grow epitaxially on top of the (110) STO substrate, with the c-axis of YBCO in plane. There is a roughness of about 10nm between PBCO and YBCO and the roughness is increased at the YBCO - LCMO interface

  1. Morphology, structure, and electrical properties of YBa{sub 2}Cu{sub 3}O{sub x} thin films on tilted NdGaO{sub 3} substrates, deposited by DC-sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Mozhaev, Peter B. [Institute of Radio Engineering and Electronics RAS, Moscow 125009 (Russian Federation)]. E-mail: pbmozh@nm.ru; Kotelyanskii, Iosif M. [Institute of Radio Engineering and Electronics RAS, Moscow 125009 (Russian Federation); Luzanov, Valery A. [Institute of Radio Engineering and Electronics RAS, Moscow 125009 (Russian Federation); Mozhaeva, Julia E. [Institute of Radio Engineering and Electronics RAS, Moscow 125009 (Russian Federation); Donchev, Todor [Institute of Electronics BAS, Sofia (Bulgaria); Mateev, Emil [Institute of Electronics BAS, Sofia (Bulgaria); Nurgaliev, Timur [Institute of Electronics BAS, Sofia (Bulgaria); Bdikin, Igor K. [Institute of Solid State Physics RAS, Chernogolovka, Moscow 142432 (Russian Federation); Department of Ceramic and Glass Engineering, CICECO, University of Aveiro, Aveiro 3810-193 (Portugal); Narymbetov, Bakhyt Zh. [Complex Institute of Natural Sciences UzAS, Nukus (Uzbekistan)

    2005-02-15

    Thin YBa{sub 2}Cu{sub 3}O{sub x} (YBCO) films were deposited using DC-sputtering technique on NdGaO{sub 3} substrates, tilted from (1 1 0) orientation by 0-26 deg . The structure and surface quality of the substrates were carefully characterized to obtain reliable results of thin films deposition. Structural, morphological and electrical properties of the YBCO thin films show three different ranges of inclination angle: vicinal, intermediate and high. In the vicinal range the properties of the film are generally the same as of the standard films deposited on (1 1 0) NdGaO{sub 3} substrate. An increase of the inclination angle to the intermediate range results in a significant improvement of morphology and structural quality of the film. Best electrical parameters are measured for the films of the intermediate range also. Probable reason for such behavior is simultaneous and regular seeding of the film in the joints of facets on the substrate surface. Further increase of inclination angle leads to step bunching and oxygen out-diffusion, destroying both structural and electrical perfection of the tilted-axes YBCO film.

  2. A rapid process of Yba2Cu3O7-δ thin film fabrication using trifluoroacetate metal-organic deposition with polyethylene glycol additive

    DEFF Research Database (Denmark)

    Wu, Wei; Feng, Feng; Shi, Kai

    2013-01-01

    Trifluoroacetate metal-organic deposition (TFA-MOD) is a promising technique to fabricate YBa2Cu3O7-δ (YBCO) superconducting films. However, its slow pyrolysis process, which usually takes more than 10 h, constitutes a barrier for industrial production. In this study, polyethylene glycol (PEG......) was utilized to reduce the stress generation inside the coated films when the strong pyrolysis reactions happen. With the addition of 30 wt% PEG2000 to the precursor solution, a smooth film surface could be obtained through a rapid pyrolysis process of 15 min. After the optimizations of the crystallization...... and oxygenation processes, mass percentage and molecular weight of PEG additive, YBCO thin films with Jc of about 4.5 MA cm-2 (77 K, self-field) could be routinely fabricated using (20-30) wt% PEG(1000-2000) additive with a total treatment time of about 2 h including the 15 min pyrolysis process time. The effects...

  3. Study by Hall probe mapping of the trapped flux modification produced by local heating in YBCO HTS bulks for different surface/volume ratios

    International Nuclear Information System (INIS)

    Laurent, Ph; Mathieu, J-P; Mattivi, B; Fagnard, J-F; Meslin, S; Noudem, J G; Ausloos, M; Cloots, R; Vanderbemden, Ph

    2005-01-01

    The aim of this report is to compare the trapped field distribution under a local heating created at the sample edge for different sample morphologies. Hall probe mappings of the magnetic induction trapped in YBCO bulk samples maintained out of thermal equilibrium were performed on YBCO bulk single domains, YBCO single domains with regularly spaced hole arrays, and YBCO superconducting foams. The capability of heat draining was quantified by two criteria: the average induction decay and the size of the thermally affected zone caused by a local heating of the sample. Among the three investigated sample shapes, the drilled single domain displays a trapped induction which is weakly affected by the local heating while displaying a high trapped field. Finally, a simple numerical modelling of the heat flux spreading into a drilled sample is used to suggest some design rules about the hole configuration and their size

  4. Analysis of YBCO high temperature superconductor doped with silver nanoparticles and carbon nanotubes using Williamson-Hall and size-strain plot

    Science.gov (United States)

    Dadras, Sedigheh; Davoudiniya, Masoumeh

    2018-05-01

    This paper sets out to investigate and compare the effects of Ag nanoparticles and carbon nanotubes (CNTs) doping on the mechanical properties of Y1Ba2Cu3O7-δ (YBCO) high temperature superconductor. For this purpose, the pure and doped YBCO samples were synthesized by sol-gel method. The microstructural analysis of the samples is performed using X-ray diffraction (XRD). The crystalline size, lattice strain and stress of the pure and doped YBCO samples were estimated by modified forms of Williamson-Hall analysis (W-H), namely, uniform deformation model (UDM), uniform deformation stress model (UDSM) and the size-strain plot method (SSP). These results show that the crystalline size, lattice strain and stress of the YBCO samples declined by Ag nanoparticles and CNTs doping.

  5. The elastic limit of vortex movement in superconducting thin films

    International Nuclear Information System (INIS)

    Doyle, R.A.; Kumar, D.; Pullan, P.; Gross, R.; Campbell, A.M.; Blamire, M.G.; Somekh, R.E.; Evetts, J.E.

    1993-01-01

    Here we report four point ac transport FD measurements on epitaxial YBCO films and also polycrystalline NbTa films. Considerable efforts have recently been put into investigating low T c systems (11) in order to model high Tc materials in which the pinning and other properties are less easily controlled by microstructural modification and in which the parameter values are less well known. Moreover no reports exist of the FD behaviour of low T c thin film systems. In the case of the YBCO films, the results will be seen to be able to be reconciled with IP effects due to the superconducting CuO layers. In the case of the NbTa films, the results are in agreement with extrinsic pinning expected from the columnar defects (grain boundaries) observed in microstructural (SEM) studies (11). The data on all samples suggests core pinning in both (high Κ) systems. Features in the FD curves of the YBCO system when the field is carefully applied parallel to the planes occur at distances corresponding to the interlayer spacing providing direct evidence for IP. The technique also offers the possibility of investigating the frequency dependence of the effect as well as looking for curvature in the FD response below the onset of dissipation in the resistive component. The former study should be able to separate resistive from hysteretic (Bean) type losses whereas the latter might expose information about the shape of the pinning wells in addition to their sizes. These are discussed briefly here but will form the basis of further more detailed study. It will be argued that the FD technique is a powerful approach for investigation of the mixed state, allowing information to be extracted which is unavailable from other techniques. (orig.)

  6. Fabrication and characterization of Ba sub x Sr sub 1 sub - sub x TiO sub 3 /YBa sub 2 Cu sub 3 O sub x /SrTiO sub 3 structure

    CERN Document Server

    Choi, J; Park, S Y; Lee Jae Sik; No, K; Sung, T H; Park, Y

    2002-01-01

    Ba sub x Sr sub 1 sub - sub x TiO sub 3 (BST)/YBa sub 2 Cu sub 3 O sub x (YBCO)/SrTiO sub 3 (STO) structures were deposited, and the microstructure, orientation and electrical characteristics were investigated. (00l) oriented YBCO thin films were deposited on STO substrates using pulsed laser deposition, and (h00) oriented BST thin films were deposited on YBCO/STO substrates using electron cyclotron resonance (ECR) plasma assisted metal organic chemical vapor deposition (MOCVD). A new phase was formed at the interface between YBCO and BST films and was speculated to be (Ba sub x Y sub 1 sub - sub x)(Ti sub y Y sub 1 sub - sub y)O sub 3. Ba-rich BST films showed a higher dielectric loss than Sr-rich BST films did, which indicates that Sr-rich BST films are more suited for application to microwave devices. The dielectric loss of the films was reduced as temperature decreased, which may be due to the conductivity change of YBCO film and the formation of a conduction path rather than a dielectric property change ...

  7. Properties of recent IBAD-MOCVD Coated Conductors relevant to their high field, low temperature magnet use

    OpenAIRE

    Braccini, V; Xu, A; Jaroszynski, J; Xin, Y; Larbalestier, D C; Chen, Y; Carota, G; Dackow, J; Kesgin, I; Yao, Y; Guevara, A; Shi, T; Selvamanickam, V

    2010-01-01

    BaZrO3 (BZO) nanorods are now incorporated into production IBAD-MOCVD coated conductors. Here we compare several examples of both BZO-free and BZO-containing coated conductors using critical current (Ic) characterizations at 4.2 K over their full angular range up to fields of 31 T. We find that BZO nanorods do not produce any c-axis distortion of the critical current density Jc(theta) curve at 4.2 K at any field, but also that pinning is nevertheless strongly enhanced compared to the non-BZO ...

  8. Various types of GaN/InGaN nanostructures grown by MOCVD on Si(111) substrate

    Energy Technology Data Exchange (ETDEWEB)

    Rozhavskaya, Mariya M.; Lundin, Wsevolod V.; Zavarin, Evgeniy E.; Lundina, Elena Yu.; Troshkov, Sergey I.; Davydov, Valery Yu.; Yagovkina, Mariya A.; Brunkov, Pavel N.; Tsatsulnikov, Andrey F. [Ioffe Physico-Technical Institute of the RAS, Politekhnicheskaya 26, 194021 St. Petersburg (Russian Federation)

    2013-03-15

    In this paper we obtained GaN and InGaN nanowires on AlN/Si (111) templates via pulsed Metal Organic Chemical Vapour Deposition (MOCVD). The growth modes were investigated, in which selective growth is possible. The impact of NH{sub 3} flow and TMG flow and exposure time were investigated. Also the possibility of using indium catalyst was studied. It was shown that In can be used in Au-In melt and as self-sufficient catalyst. (copyright 2013 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  9. Angular dependence of Jc for YBCO coated conductors at low temperature and very high magnetic fields

    International Nuclear Information System (INIS)

    Xu, A; Jaroszynski, J J; Kametani, F; Chen, Z; Larbalestier, D C; Viouchkov, Y L; Chen, Y; Xie, Y; Selvamanickam, V

    2010-01-01

    We present very high field angle dependent critical current density (J c ) data for three recently obtained YBa 2 Cu 3 O 7-x (YBCO) coated conductors used in the construction of high field solenoids. We find that strongly correlated pins, such as BaZrO 3 (BZO) nanorods, while yielding strong c-axis peaks at 77 K, produce almost no measurable contribution at 4 K. Raising the field from c (θ) at low fields to a marked cusp-like behavior at high fields. Transmission electron micrographs show that all samples contain a high density of stacking faults which strengthen the plane correlated pinning parallel to the ab planes produced by the intrinsic ab-plane pinning of the Cu-O charge reservoir layers.

  10. Magnetization Losses of Roebel Cable Samples with 2G YBCO Coated Conductor Strands

    CERN Document Server

    Yang, Y.; Falorio, I.; Young, E.A.; Kario, A.; Goldacker, W.; Dhallé, M. M. J.; van Nugteren, J.; Kirby, G.; Bottura, L.; Ballarino, A.

    2016-01-01

    Roebel cable with 2G YBCO strands is one of the promising HTS solutions of fully transposed high current conductors for high field accelerator magnets. Following the considerable research effort on the manufacturing of Roebel cables in recent years, sample conductors are now available in useful lengths with reproducible performances to allow detailed characterizations beyond the standard critical current measurements. The ac loss and strands coupling are of significant interest for the field quality of the accelerator magnets. We report a set of systematic ac loss measurements on two different Roebel cable samples prepared for the EuCARD2 collaboration. The measurements were performed over a wide range of temperature between 5 K and 90 K and the results were analyzed in the context of strands architecture and coupling. The results show that the transposed bundles are partially decoupled and the strands in transposition sections behave as an isolated single tape if the strands are insulated.

  11. Simulation and experiment of a YBCO SMES prototype in voltage sag compensation

    International Nuclear Information System (INIS)

    Zhu Jiahui; Yuan Weijia; Coombs, T.A.; Ming, Q.

    2011-01-01

    Research highlights: → YBCO conductors are used in SMES. → The SMES is successfully used to compensate voltage sag by both simulation and experiment. → A new control strategy for the power converter in the SMES. - Abstract: This paper gives a introduction of a SMES unit using 2G HTS wires. A complete SMES system including both superconducting coils and control circuit has been designed to operate at 77 K. Three single-phase H-bridge converters have been used in the control circuit. A loop control signal is sent out by using 32 fixed point Digital Signal Processor (DSP). The complete circuit has been both modelled in simulation and built experimentally. The results validate that this SMES successfully compensates a voltage sag in a power system.

  12. Microstructure of Josephson junctions: Effect on supercurrent transport in YBCO grain boundary and barrier layer junctions

    International Nuclear Information System (INIS)

    Merkle, K.L.; Huang, Y.

    1998-01-01

    The electric transport of high-temperature superconductors, such as YBa 2 Cu 3 O 7-x (YBCO), can be strongly restricted by the presence of high-angle grain boundaries (GB). This weak-link behavior is governed by the macroscopic GB geometry and the microscopic grain boundary structure and composition at the atomic level. Whereas grain boundaries present a considerable impediment to high current applications of high T c materials, there is considerable commercial interest in exploiting the weak-link-nature of grain boundaries for the design of microelectronic devices, such as superconducting quantum interference devices (SQUIDs). The Josephson junctions which form the basis of this technology can also be formed by introducing artificial barriers into the superconductor. The authors have examined both types of Josephson junctions by EM techniques in an effort to understand the connection between microstructure/chemistry and electrical transport properties. This knowledge is a valuable resource for the design and production of improved devices

  13. Simulation and experiment of a YBCO SMES prototype in voltage sag compensation

    Energy Technology Data Exchange (ETDEWEB)

    Zhu Jiahui, E-mail: zhujiahui@epri.sgcc.com.c [China Electric Power Research Institute, No. 15 Xiaoying Rd(E), Qinghe, Beijing 100192 (China); Yuan Weijia; Coombs, T.A. [Electrical Engineering Division, Engineering Department, University of Cambridge, CB3 0FA (United Kingdom); Ming, Q. [China Electric Power Research Institute, No. 15 Xiaoying Rd(E), Qinghe, Beijing 100192 (China)

    2011-03-15

    Research highlights: {yields} YBCO conductors are used in SMES. {yields} The SMES is successfully used to compensate voltage sag by both simulation and experiment. {yields} A new control strategy for the power converter in the SMES. - Abstract: This paper gives a introduction of a SMES unit using 2G HTS wires. A complete SMES system including both superconducting coils and control circuit has been designed to operate at 77 K. Three single-phase H-bridge converters have been used in the control circuit. A loop control signal is sent out by using 32 fixed point Digital Signal Processor (DSP). The complete circuit has been both modelled in simulation and built experimentally. The results validate that this SMES successfully compensates a voltage sag in a power system.

  14. Experimental and numerical study of a YBCO pancake coil with a magnetic substrate

    International Nuclear Information System (INIS)

    Zhang Min; Coombs, T A; Kvitkovic, J; Pamidi, S V

    2012-01-01

    A finite element model for a YBCO pancake coil with a magnetic substrate is developed in this paper. An axial symmetrical H formulation and the E–J power law are used to construct the model, with the magnetic substrate considered by introducing an extra time-dependent term in the formula. A pancake coil is made and tested. The measurement of critical current and transport loss is compared to the model result, showing good consistency. The influence of magnetic substrate in the condition of AC and DC current is studied. The AC loss decreases without a magnetic substrate. It is observed that when the applied DC current approaches the critical current the coil turn loss profile changes completely in the presence of magnetic substrate due to the change of magnetic field distribution. (paper)

  15. Monte Carlo study of electron irradiation effect on YBCO dpa profiles

    International Nuclear Information System (INIS)

    Pinnera, I.; Cruz, C.; Abreu, Y.; Leyva, A.; Van Espen, P.

    2011-01-01

    The Monte Carlo assisted Classical Method (MCCM) consists on a calculation procedure for determining the displacements per atom (dpa) distribution in solid materials. This algorithm allows studying the gamma and electron irradiation damage in different materials. It is based on the electrons elastic scattering classic theories and the use of Monte Carlo simulation for the physical processes involved. The present study deals with the Monte Carlo simulation of electron irradiation effects on YBa 2 Cu 3 O 7-x (YBCO) slabs using the MCNPX code system. Displacements per atom distributions are obtained through the MCCM for electron irradiation up to 10 MeV. In-depth dpa profiles for electrons and positrons are obtained and analyzed. Also, for each atomic species in the material, the dpa distributions are calculated. All the results are discussed in the present contribution. (Author)

  16. Phonon spectrum of YBCO obtained by specific heat inversion method for real data

    CERN Document Server

    Tao Wen; Dai Xian Xi; Dai Ji Xin; Evenson, W E

    2003-01-01

    In this paper, the phonon spectrum of YBCO is obtained from experimental specific heat data by an exact inversion formula with a parameter for eliminating divergences. The results can be compared to those of neutron inelastic scattering, which can only be carried out in a few laboratories. Some key points of specific heat-phonon spectrum inversion (SPI) theory and a method of asymptotic behaviour control are discussed. An improved unique existence theorem is presented, and a universal function set for numerical calculation of SPI is calculated with high accuracy, which makes the inversion method applicable and convenient in practice. This is the first time specific heat-phonon SPI has been realized for a concrete system.

  17. Magnetic levitation and its application for education devices based on YBCO bulk superconductors

    Science.gov (United States)

    Yang, W. M.; Chao, X. X.; Guo, F. X.; Li, J. W.; Chen, S. L.

    2013-10-01

    A small superconducting maglev propeller system, a small spacecraft model suspending and moving around a terrestrial globe, several small maglev vehicle models and a magnetic circuit converter have been designed and constructed. The track was paved by NdFeB magnets, the arrangement of the magnets made us easy to get a uniform distribution of magnetic field along the length direction of the track and a high magnetic field gradient in the lateral direction. When the YBCO bulks mounted inside the vehicle models or spacecraft model was field cooled to LN2 temperature at a certain distance away from the track, they could be automatically floating over and moving along the track without any obvious friction. The models can be used as experimental or demonstration devices for the magnetic levitation applications.

  18. Test results of fault current limiter using YBCO tapes with shunt protection

    Energy Technology Data Exchange (ETDEWEB)

    Baldan, Carlos A; Lamas, Jerika S; Shigue, Carlos Y [Escola de Engenharia de Lorena, EEL USP, Lorena - SP (Brazil); Filho, Ernesto Ruppert, E-mail: cabaldan@gmail.co [Faculdade de Engenharia Eletrica, FEEC Unicamp, Campinas - SP (Brazil)

    2010-06-01

    A Fault Current Limiter (FCL) based on high temperature superconducting elements with four tapes in parallel were designed and tested in 220 V line for a fault current peak between 1 kA to 4 kA. The elements employed second generation (2G) HTS tapes of YBCO coated conductor with stainless steel reinforcement. The tapes were electrically connected in parallel with effective length of 0.4 m per element (16 elements connected in series) constituting a single-phase unit. The FCL performance was evaluated through over-current tests and its recovery characteristics under load current were analyzed using optimized value of the shunt protection. The projected limiting ratio achieved a factor higher than 4 during fault of 5 cycles without degradation. Construction details and further test results will be shown in the paper.

  19. Substrate decoration for improvement of current-carrying capabilities of YBa2Cu3Ox thin films

    DEFF Research Database (Denmark)

    Khoryushin, Alexey; Mozhaev, Peter; Mozhaeva, Julia

    2013-01-01

    The effects of substrate decoration with yttria and Y:ZrO2 on the structural and electrical properties of the YBa2Cu3Ox (YBCO) thin films are studied. The films were deposited on (LaAlO3)3–(Sr2AlTaO8)7 substrates by pulsed laser deposition. Two different structures of decoration layer were applie...

  20. High-Tc film development for electronic applications

    International Nuclear Information System (INIS)

    Talvacchio, J.; Wagner, G.R.

    1990-01-01

    In this paper, the authors describe the requirements and status of high-T c superconductor (HTS) films for the development of electronic applications with an emphasis on passive microwave devices. One of the most general requirements, a low rf Surface resistance relative to Cu, has been achieved in films of several different HTS compounds. However the best films, made of YBa 2 Cu 3 O 7 (YBCO) by any one of several techniques, have in common a residual surface resistance that is much greater than predicted by conventional superconductivity theory. Improvement in films is also limited by the current size and selection of single-crystal substrate materials. Other issues that must be resolved to develop a full integrated circuit technology for HTS are substrate heating during film deposition, deposited epitaxial insulators, and determination of which interfaces in a multilevel circuit must be formed in situ