WorldWideScience

Sample records for milled precursor powder

  1. Analysis of the influence of two different milling processes in the properties of precursor powder and [Beta]-TCP cement

    International Nuclear Information System (INIS)

    Cardoso, H.A.I.; Pereira, C.H.R.; Zavaglia, C.A.C.; Motisuke, M.

    2011-01-01

    There are several characteristics that put calcium phosphate cements in evidence, like its bioactivity and in vivo resorption. The influence of two milling processes in the morphological properties of the [beta]-tricalcium phosphate powder, [beta]-TCP, and in the mechanical properties of the cement were analyzed. The powder was obtained by solid state reaction of CaCO_3 and CaHPO_4 at 1050 ° C. It showed high phase purity and absence of toxic elements. The powder was processed in ball mill (A) and high-energy vibratory mill (B), with posterior analyze by SEM and particle size distribution. The powders showed different average and distribution of grain size. Finally, the cement obtained by the process (B) showed values of axial tensile strength significantly greater than that obtained by the process (A). The milling process (B) is much more efficient than the process (A). (author)

  2. Preparation of superconductor precursor powders

    Science.gov (United States)

    Bhattacharya, Raghunath

    1998-01-01

    A process for the preparation of a precursor metallic powder composition for use in the subsequent formation of a superconductor. The process comprises the steps of providing an electrodeposition bath comprising an electrolyte medium and a cathode substrate electrode, and providing to the bath one or more soluble salts of one or more respective metals which are capable of exhibiting superconductor properties upon subsequent appropriate treatment. The bath is continually energized to cause the metallic and/or reduced particles formed at the electrode to drop as a powder from the electrode into the bath, and this powder, which is a precursor powder for superconductor production, is recovered from the bath for subsequent treatment. The process permits direct inclusion of all metals in the preparation of the precursor powder, and yields an amorphous product mixed on an atomic scale to thereby impart inherent high reactivity. Superconductors which can be formed from the precursor powder include pellet and powder-in-tube products.

  3. CVD carbon powders modified by ball milling

    Directory of Open Access Journals (Sweden)

    Kazmierczak Tomasz

    2015-09-01

    Full Text Available Carbon powders produced using a plasma assisted chemical vapor deposition (CVD methods are an interesting subject of research. One of the most interesting methods of synthesizing these powders is using radio frequency plasma. This method, originally used in deposition of carbon films containing different sp2/sp3 ratios, also makes possible to produce carbon structures in the form of powder. Results of research related to the mechanical modification of these powders have been presented. The powders were modified using a planetary ball mill with varying parameters, such as milling speed, time, ball/powder mass ratio and additional liquids. Changes in morphology and particle sizes were measured using scanning electron microscopy and dynamic light scattering. Phase composition was analyzed using Raman spectroscopy. The influence of individual parameters on the modification outcome was estimated using statistical method. The research proved that the size of obtained powders is mostly influenced by the milling speed and the amount of balls. Powders tend to form conglomerates sized up to hundreds of micrometers. Additionally, it is possible to obtain nanopowders with the size around 100 nm. Furthermore, application of additional liquid, i.e. water in the process reduces the graphitization of the powder, which takes place during dry milling.

  4. The effect of precursor powder size on the microstructure and integranular properties of Bi2223 superconductors

    Directory of Open Access Journals (Sweden)

    I. Abdolhosseini

    2006-09-01

    Full Text Available  We have studied the effect of precursor powder size on the microstructure and intergranular behavior of polycrystalline Bi2223 superconductors using the XRD, SEM, electrical resistivity and AC susceptibility techniques. Polycrystalline Bi2223 superconductors were prepared from the powders with different milling times. The XRD results show that by decreasing the precursor powder size the Bi2223 phase fraction increases. It was found that the grain size and grain connectivity improved by decreasing the precursor powder size. Analysis of the temperature dependence of the AC susceptibility near the transition temperature (Tc has been done employing Beans critical state model. The observed variation of intergranular critical current densities (Jc with temperature indicates that the decreasing of precursor powder size in the Bi2223 system cases an increase in the intergranular critical current density.

  5. Nanograin formation in milled MoO3 powders

    International Nuclear Information System (INIS)

    Guerrero-Paz, J; Dorantes-Rosales, H; Aguilar-Martínez, J A; Garibay-Febles, V

    2013-01-01

    Powder of Molybdenum trioxide was milled for different times in horizontal ball mills. Such powder was characterized by TEM and XRD. Powder was rapidly de-agglomerated and fragmented up to attain nanoplates of two types, amorphous and crystalline. Finally, cold-welding of nanoplates occurred permitting some relaxation process to obtain a more stable energized structure consisting of equiaxial crystalline nanograins after 16 hours of milling.

  6. Properties and sinterability of wet and dry attrition-milled OREOXed powder

    International Nuclear Information System (INIS)

    Lee, J. W.; Kim, J. H.; Kim, W. K.; Park, K. I.; Lee, J. W.

    2001-01-01

    The powder properties and sinterability were investigated with the powder prepared by wet and dry attrition milling of OREOX-treated powder. The OREOX-treated powder was prepared from the simulated spent fuel. Powder having less than 1 μm of average particle size could be obtained by dry milling, but not be obtained by wet milling. Thus, specific surface area of dry milled powder was higher than that of wet milled powder. With increasing of milling time, dry milled powder formed dense agglomerate while wet milled powder showed loose agglomerate. The pellets with higher than 95% T.D. of sintered density and larger than 7 μm of grain size were made with the milled powder regardless of milling method. The milling time in wet milling has greatly improved the sinterability. The pellets produced with dry milled powder have higher sintered density and larger grain size

  7. Effect of thermal treatment on mechanically milled cobalt powder

    CSIR Research Space (South Africa)

    Bolokang, AS

    2012-03-01

    Full Text Available Stabilization of the metastable FCC phase has been achieved after 10 h milled Co powder sintering at 1400 °C. Phase identification of the Co powders was performed by the X-ray diffraction analysis, while the microstructural analyses were performed...

  8. Production of nanocrystalline cermet thermal spray powders for wear resistant coatings by high-energy milling

    International Nuclear Information System (INIS)

    Eigen, N.; Klassen, T.; Aust, E.; Bormann, R.; Gaertner, F.

    2003-01-01

    TiC-Ni based nanocrystalline cermet powders for thermal spraying were produced by high-energy milling. Milling experiments were performed in an attrition mill and a vibration mill in kilogram scale, and powder morphologies and microstructures were characterized using scanning electron microscopy, X-ray diffraction, and laser scattering for particle size analysis. Milling time and powder input were optimized with respect to the desired microstructure and particle sizes, and the results using both types of mill were compared. Powders with homogeneously dispersed hard phase particles below 300 nm could be produced in both mills. Additional processes for the refinement of powder morphology and particle size distribution are discussed

  9. Al-doped ZnO mechanical milled powders for dye sensitized cells

    International Nuclear Information System (INIS)

    Damonte, L.C.; Donderis, V.; Ferrari, S.; Orozco, J.; Hernandez-Fenollosa, M.A.

    2010-01-01

    Mixtures of Al 2 O 3 and ZnO powders were prepared by mechanical milling. The resulting samples were analyzed and characterized by X-ray diffraction (XRD), positron annihilation lifetime spectroscopy (PALS), scanning electron microscopy (SEM) and optical reflection spectroscopy (OPS). XRD and PALS measurements confirm Al incorporation into ZnO wurtzite structure. Powders obtained from Al 2 O 3 precursors display better reflectivity than those prepared from Al metal so they might be better materials for implementation in photovoltaic solar devices.

  10. Al-doped ZnO mechanical milled powders for dye sensitized cells

    Energy Technology Data Exchange (ETDEWEB)

    Damonte, L.C., E-mail: damonte@fisica.unlp.edu.a [Departamento de Fisica, UNLP, IFLP-CCT-CONICET, C.C.67(1900), La Plata (Argentina); Dto. de Fisica Aplicada, Universidad Politecnica de Valencia, Cami de Vera s/n, 46022 Valencia (Spain); Donderis, V. [Dto. de Ingenieria Electrica, Universidad Politecnica de Valencia, Cami de Vera s/n, 46022 Valencia (Spain); Ferrari, S. [Departamento de Fisica, UNLP, IFLP-CCT-CONICET, C.C.67(1900), La Plata (Argentina); Orozco, J. [ITM, Universidad Politecnica de Valencia, Cami de Vera s/n, 46022 Valencia (Spain); Hernandez-Fenollosa, M.A. [Dto. de Fisica Aplicada, Universidad Politecnica de Valencia, Cami de Vera s/n, 46022 Valencia (Spain)

    2010-04-16

    Mixtures of Al{sub 2}O{sub 3} and ZnO powders were prepared by mechanical milling. The resulting samples were analyzed and characterized by X-ray diffraction (XRD), positron annihilation lifetime spectroscopy (PALS), scanning electron microscopy (SEM) and optical reflection spectroscopy (OPS). XRD and PALS measurements confirm Al incorporation into ZnO wurtzite structure. Powders obtained from Al{sub 2}O{sub 3} precursors display better reflectivity than those prepared from Al metal so they might be better materials for implementation in photovoltaic solar devices.

  11. Nanocrystalline TiAl powders synthesized by high-energy ball milling: effects of milling parameters on yield and contamination

    International Nuclear Information System (INIS)

    Bhattacharya, Prajina; Bellon, Pascal; Averback, Robert S.; Hales, Stephen J.

    2004-01-01

    High-energy ball milling was employed to produce nanocrystalline Ti-Al powders. As sticking of the powders can be sufficiently severe to result in a near zero yield, emphasis was placed on varying milling conditions so as to increase the yield, while avoiding contamination of the powders. The effects of milling parameters such as milling tools, initial state of the powders and addition of process control agents (PCA's) were investigated. Cyclohexane, stearic acid and titanium hydride were used as PCA's. Milling was conducted either in a Cr-steel vial with C-steel balls, or in a tungsten carbide (WC) vial with WC balls, using either elemental or pre-alloyed powders. Powder samples were characterized using X-ray diffraction, scanning and transmission electron microscopy. In the absence of PCA's mechanical alloying in a WC vial and attrition milling in a Cr-steel vial were shown to lead to satisfactory yields, about 65-80%, without inducing any significant contamination of the powders. The results suggest that sticking of the powders on to the milling tools is correlated with the phase evolution occurring in these powders during milling

  12. Milling uranium silicide powder for dispersion nuclear fuels

    Energy Technology Data Exchange (ETDEWEB)

    Vieira, E.; Silva, D.G.; Souza, J.A.B.; Durazzo, M. [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil); Riella, H.G. [Universidade Federal de Santa Catarina (UFSC), Florianopolis, SC (Brazil)

    2009-07-01

    Full text: Uranium silicide (U3Si2) is presently considered the best fuel qualified so far in terms of uranium loading and performance. Stability of the U3Si2 fuel with uranium density of 4.8 g/cm3 was confirmed by burnup stability tests performed during the Reduced Enrichment for Research and Test Reactors (RERTR) program. This fuel was chosen to compose the first core of the new Brazilian Multipurpose Research Reactor (RMB), planned to be constructed in the next years. This new reactor will consume bigger quantities of U3Si2 powder, when compared with the small consumption of the IEA-R1 research reactor of IPEN-CNEN/SP, the unique MTR type research reactor operating in the country. At the present time, the milling operation of U3Si2 ingots is made manually. In order to increase the powder production capacity, the manual milling must be replaced by an automated procedure. This paper describes a new milling machine and procedure developed to produce U3Si2 powder with higher efficiency. (author)

  13. Dry Powder Precursors of Cubic Liquid Crystalline Nanoparticles (cubosomes)

    International Nuclear Information System (INIS)

    Spicer, Patrick T.; Small, William B.; Small, William B.; Lynch, Matthew L.; Burns, Janet L.

    2002-01-01

    Cubosomes are dispersed nanostructured particles of cubic phase liquid crystal that have stimulated significant research interest because of their potential for application in controlled-release and drug delivery. Despite the interest, cubosomes can be difficult to fabricate and stabilize with current methods. Most of the current work is limited to liquid phase processes involving high shear dispersion of bulk cubic liquid crystalline material into sub-micron particles, limiting application flexibility. In this work, two types of dry powder cubosome precursors are produced by spray-drying: (1) starch-encapsulated monoolein is produced by spray-drying a dispersion of cubic liquid crystalline particles in an aqueous starch solution and (2) dextran-encapsulated monoolein is produced by spray-drying an emulsion formed by the ethanol-dextran-monoolein-water system. The encapsulants are used to decrease powder cohesion during drying and to act as a soluble colloidal stabilizer upon hydration of the powders. Both powders are shown to form (on average) 0.6 μm colloidally-stable cubosomes upon addition to water. However, the starch powders have a broader particle size distribution than the dextran powders because of the relative ease of spraying emulsions versus dispersions. The developed processes enable the production of nanostructured cubosomes by end-users rather than just specialized researchers and allow tailoring of the surface state of the cubosomes for broader application

  14. Flaking behavior and microstructure evolution of nickel and copper powder during mechanical milling in liquid environment

    International Nuclear Information System (INIS)

    Xiao Xiao; Zeng Zigao; Zhao Zhongwei; Xiao Songwen

    2008-01-01

    To prepare metal flakes with a high flaking level and investigate the microstructure of metal flakes, nickel and copper powder were mechanically milled in liquid environment and the microstructure of powders was investigated by X-ray diffraction. The milling process can be divided into flaking and broken stages. At the flaking stage, milled metal powders exhibited high flaking level and flaky microshape, and became preferred orientation. While at the broken stage, the milled powders presented a low flaking level and irregular microshape, and was not preferred orientation any longer. The grain size, microstrain and dislocation density along direction varied with milling time differently from that along direction. The flaking level of the milled powders was related to the preferred orientation, and more closely to the deformation mechanism. We can strengthen the formation of preferred orientation to obtain metal powders with a high flaking level

  15. Flaking behavior and microstructure evolution of nickel and copper powder during mechanical milling in liquid environment

    Energy Technology Data Exchange (ETDEWEB)

    Xiao Xiao [College of Metallurgical Science and Engineering, Central South University, Changsha 410083, Hunan (China); Changsha Research Institute of Mining and Metallurgy, Changsha 410012, Hunan (China); Zeng Zigao [Changsha Research Institute of Mining and Metallurgy, Changsha 410012, Hunan (China); Zhao Zhongwei [College of Metallurgical Science and Engineering, Central South University, Changsha 410083, Hunan (China); Xiao Songwen [Changsha Research Institute of Mining and Metallurgy, Changsha 410012, Hunan (China)], E-mail: swinxiao@yahoo.com.cn

    2008-02-25

    To prepare metal flakes with a high flaking level and investigate the microstructure of metal flakes, nickel and copper powder were mechanically milled in liquid environment and the microstructure of powders was investigated by X-ray diffraction. The milling process can be divided into flaking and broken stages. At the flaking stage, milled metal powders exhibited high flaking level and flaky microshape, and <2 0 0> became preferred orientation. While at the broken stage, the milled powders presented a low flaking level and irregular microshape, and <2 0 0> was not preferred orientation any longer. The grain size, microstrain and dislocation density along <2 0 0> direction varied with milling time differently from that along <1 1 1> direction. The flaking level of the milled powders was related to the <2 0 0> preferred orientation, and more closely to the deformation mechanism. We can strengthen the formation of <2 0 0> preferred orientation to obtain metal powders with a high flaking level.

  16. Milling and Drilling Evaluation of Stainless Steel Powder Metallurgy Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Lazarus, L.J.

    2001-12-10

    Near-net-shape components can be made with powder metallurgy (PM) processes. Only secondary operations such as milling and drilling are required to complete these components. In the past and currently production components are made from powder metallurgy (PM) stainless steel alloys. process engineers are unfamiliar with the difference in machining properties of wrought versus PM alloys and have had to make parts to develop the machining parameters. Design engineers are not generally aware that some PM alloy variations can be furnished with machining additives that greatly increase tool life. Specimens from a MANTEC PM alloy property study were made available. This study was undertaken to determine the machining properties of a number of stainless steel wrought and PM alloys under the same conditions so that comparisons of their machining properties could be made and relative tool life determined.

  17. Phase transition of Ni-Mn-Ga alloy powders prepared by vibration ball milling

    International Nuclear Information System (INIS)

    Tian, B.; Chen, F.; Tong, Y.X.; Li, L.; Zheng, Y.F.; Liu, Y.; Li, Q.Z.

    2011-01-01

    Research highlights: → The vibration ball milling with a high milling energy introduces the atomic disorder and large lattice distortion in the alloy during milling and makes the formation of disordered fcc structure phase in the alloy. → The transition temperature and activation energy for disordered fcc → disordered bcc are ∼320 o C and 209 ± 8 kJ/mol, respectively. → The alloy powders annealed at 800 o C for 1 h show a one-stage martensitic transformation with quite lower latent heat compared to the bulk alloy. - Abstract: This study investigated the phase transformation of the flaky shaped Ni-Mn-Ga powder particles with thickness around 1 μm prepared by vibration ball milling and post-annealing. The SEM, XRD, DSC and ac magnetic susceptibility measurement techniques were used to characterize the Ni-Mn-Ga powders. The structural transition of Heusler → disordered fcc occurred in the powders prepared by vibration ball milling (high milling energy) for 4 h, which was different from the structural transition of Heusler → disordered fct of the powders fabricated by planetary ball milling (low milling energy) for 4 h. The two different structures after ball milling should be due to the larger lattice distortion occurred in the vibration ball milling process than in the planetary ball milling process. The structural transition of disordered fcc → disordered bcc took place at ∼320 o C during heating the as-milled Ni-Mn-Ga powders, which was attributed to the elimination of lattice distortion caused by ball milling. The activation energy for this transition was 209 ± 8 kJ/mol. The Ni-Mn-Ga powder annealed at 800 o C mainly contained Heusler austenite phase at room temperature and showed a low volume of martensitic transformation upon cooling. The inhibition of martensitic transformation might be attributed to the reduction of grain size in the annealed Ni-Mn-Ga particles.

  18. Fabrication of Ti-Ni-Cu shape memory alloy powders by ball milling method

    International Nuclear Information System (INIS)

    Kang, S.; Nam, T.

    2001-01-01

    Ti-Ni and Ti-Ni-Cu shape memory alloy powders have been fabricated by ball milling method, and then alloying behavior and transformation behavior were investigated by means of optical microscopy, electron microscopy, X-ray diffraction and differential scanning calorimetry. As milled Ti-Ni powders fabricated with milling time less than 20 hrs was a mixture of pure elemental Ti and Ni, and therefore it was unable to obtain alloy powders because the combustion reaction between Ti and Ni occurred during heat treatment. Since those fabricated with milling time more than 20 hrs was a mixture of Ti-rich and Ni-rich Ti-Ni solid solution, however, it was possible to obtain alloy powders without the combustion reaction during heat treatment. Clear exothermic and endothermic peaks appeared in the cooling and heating curves, respectively in DSC curves of 20 hrs and 30 hrs milled Ti-Ni powders. On the other hand, in DSC curves of 1 hr, 10 hrs, 50 hrs and 100 hrs, the thermal peaks were almost discernible. The most optimum ball milling time for fabricating Ti-Ni alloy powders was 30 hrs. Ti-40Ni-10Cu(at%) alloy powders were fabricated successfully by ball milling conditions with rotating speed of 100 rpm and milling time of 30 hrs. (author)

  19. Characterization of prealloyed copper powders treated in high energy ball mill

    International Nuclear Information System (INIS)

    Rajkovic, Viseslava; Bozic, Dusan; Jovanovic, Milan T.

    2006-01-01

    The inert gas atomised prealloyed copper powders containing 3.5 wt.% Al were milled up to 20 h in the planetary ball mill in order to oxidize aluminium in situ with oxygen from the air. In the next procedure compacts from milled powder were synthesized by hot-pressing in argon atmosphere. Compacts from as-received Cu-3.5 wt.% Al powder and electrolytic copper powder were also prepared under the same conditions. Microstructural and morphological changes of high energy milled powder as well as changes of thermal stability and electrical conductivity of compacts were studied as a function of milling time and high temperature exposure at 800 deg. C. Optical, scanning electron microscopy (SEM) and X-ray diffraction analysis were performed for microstructural characterization, whereas thermal stability and electrical conductivity were evaluated by microhardness measurements and conductometer Sigmatest, respectively. The prealloyed 5 h-milled and compacted powder showed a significant increase in microhardness reaching the value of 2600 MPa, about 4 times greater than that of compacts synthesized from as-received electrolytic copper powder (670 MPa). The electrical conductivity of compacts from 5 h-milled powder was 52% IACS. The results were discussed in terms of the effect of small grain size and finely distributed alumina dispersoids on hardening and thermal stability of compacts

  20. Design and Testing of UMM Vertical Ball Mill (UVBM) for producing Aluminium Powder

    Science.gov (United States)

    Aisyah, I. S.; Caesarendra, Wahyu; Suprihanto, Agus

    2018-04-01

    UMM Vertical Ball Mill (UVBM) was intended to be the apparatus to produce metal powder with superior characteristic in production rate while retaining good quality of metal powder. The concept of design was adopting design theory of Phal and Beitz with emphasis on increasing of probability of success in engineering and economy aspects.Since it was designed as vertical ball mill, a new way to produce powder, then it need to be tested for the performance after manufactured. The test on UVBM was carried out by milling of aluminium chip for 5 (five) different milling time of 0.5 hours, 1 hour, 3 hours, 5 hours and 7 hours, and the powder product then be characterized for it morphology and size using Scanning Electron Microscope (SEM) and Sieve.The results of the study were the longer of the milling time, the finer of the powder. From the test results of SEM, the morphology of the powder with 5 variations of milling time were most of the powder in form of flake (flat), small round and angular (irregular). The distribution of powder size was best obtained on the variation of milling time 3 hours, 5 hours, and 7 hours with percentage of 200 mesh in size of 22.14 %, 64 % and 91.25 % respectively.

  1. High-energy ball milling of powder B-C mixtures

    International Nuclear Information System (INIS)

    Ramos, Alfeu S.; Taguchi, Simone P.; Ramos, Erika C.T.; Arantes, Vera L.; Ribeiro, Sebastiao

    2006-01-01

    The present work reports on the preparation of B-10 at.% C and B-18 at.% C powders by high-energy ball milling and further heat treatment. The milling process was carried out in a planetary ball mill. Following the milling process, powder samples were heat-treated at 1200 deg. C for 4 h using inert atmosphere. The milled and heat-treated B-10C and B-18C powders were characterized by means of X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. A reduction on the intensity of B and C peaks was noticed after milling for 2 h, probably due the fine powder particle sizes because the pronounced fracture mechanism during ball milling of brittle starting components. The XRD patterns of B-10C and B-18C powders milled for 6 h indicated the presence of other peaks, suggesting that a metastable structure could have been formed. After milling for 90 h, these unknown peaks were still present. A large amount of B 4 C was formed after heat treatment at 1200 deg. C for 4 h beside these unknown peaks

  2. Behaviour of CaO coating of gas atomized Mg powders using mechanical milling process

    International Nuclear Information System (INIS)

    Kim, Sun-Mi; Kim, Yong Hwan; Kim, Young Do; Kim, Taek-Soo

    2011-01-01

    Highlights: → This work is very new, since behaviour of CaO coating with milling time as desulfurizer is not frequently reported. → The manuscript reports the new manner of Mg powders desulfurizer development by the innovative process. - Abstract: In order to synthesize a thermally stable Mg powder as a desulfurizer of iron, pure Mg was gas atomized to powders and coated by CaO powders, to produce a thermally stable desulfurizer using a mechanical milling process. Since the effect of desulfurization is dependent on the degree of surface modification, coating behaviours such as the size, morphology and layer thickness were investigated as a function of milling condition. As the milling conducted from 10 min to 30 min, 1 h, 3 h, 6 h, 12 h, CaO particles began to stick on the surface of Mg powders. The layer of CaO formed from 1 h milling was about 17 μm thick and gradually thickened to be 28 μm, 32 μm and 37 μm with increasing the milling time to 3 h, 6 h and 12 h, respectively. The shape of coated powder became more spherical after 1 h milling, being mostly spherical after 6 h. Desulfurization rate and uniformity were evaluated for the various thickness of the coating layer.

  3. Influence of the milling time in the microstructural parameters of TA2O5-Al powder refined by Rietveld method

    International Nuclear Information System (INIS)

    Brito, R.A.; Mendes, M.W.D.; Alves Junior, C.; Costa, F.A. da; Gomes, U.U.

    2009-01-01

    Mechanical alloying (MA) is a solid-state powder processing technique involving repeated welding, fracturing, and re-welding of powder particles in a high energy mill. This process is used for producing of fine powders containing unique microstructures. The process starts with mixing of the powders in the desired proportion. Then, the mixture is milled using the established time in the high-energy mill. The powder particles are submitted to repeated cycles of cold working and fracture, and the final product correspond to a composite powder, containing characteristics different of the initial constituents. Ta 2 O 5 -Al powders were milled in a planetary ball mill for different times in order to evaluate the influence of the milling time in their microstructural parameters like crystallite size and micro deformation. The microstructural parameters were obtained by the Rietveld Method. The results showed that the microstructural parameters were influenced by the increase of the milling time. (author)

  4. Quantitative analysis of mineral powders by DRIFTS: Determination of SrCO3 in superconductor precursor powders

    DEFF Research Database (Denmark)

    Bak, J.; Kindl, B.

    1997-01-01

    An application of diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) has been demonstrated to be able to determine small concentrations, down to the 100-ppm level, of carbonates in powdery superconductor (SPC) precursor samples, The detection of carbonates in SPC precursor powders...

  5. Influence of pin and hammer mill on grinding characteristics, thermal and antioxidant properties of coriander powder.

    Science.gov (United States)

    Barnwal, P; Singh, K K; Sharma, Alka; Choudhary, A K; Saxena, S N

    2015-12-01

    In present study, influence of grinding (hammer and pin mills) and moisture content (range: 6.4-13.6 % dry basis) on the quality traits of coriander powder were investigated. These include grinding parameters, colour parameters, specific heat, thermal conductivity, thermal diffusivity, glass transition temperature, essential oil, total phenolic content, total flavonoid content and DPPH scavenging (%) of coriander powder. For coriander seed, the geometric properties such as major, medium, minor dimensions, geometric mean diameter, arithmetic mean diameter, sphericity, surface area and volume of coriander seeds increased significantly with increasing moisture (6.4-13.6 % db). For coriander powder, the grinding parameters such as average particle size, volume surface mean diameter and volume mean diameter increased significantly with increasing moisture (6.4-13.6 % db). With the grinding method, the colour attributes of coriander powder such as L-value, a-value, b-value, hue angle and browning index varied significantly. It was observed that the specific heat followed second order polynomial relationship with temperature and moisture whereas thermal conductivity varied linearly with temperature and moisture content. The variation of glass transition temperature with moisture can be best represented in quadratic manner. Total flavonoid content (mg QE/g crude seed extract) and DPPH scavenging % activity of coriander powder is significantly affected by grinding methods. A lower value of specific heat was observed for hammer ground coriander powder as compared to pin mill ground coriander powder. The thermal conductivity of hammer mill ground coriander powder was higher as compared to pin mill ground coriander. It was observed that hammer mill yields more fine coriander powder in comparison to pin mill. The browning index was more in hammer mill ground coriander powder.

  6. Cold compaction behavior and pressureless sinterability of ball milled WC and WC/Cu powders

    Directory of Open Access Journals (Sweden)

    Hashemi Seyed R.

    2016-01-01

    Full Text Available In this research, cold compaction behavior and pressureless sinterability of WC, WC-10%wtCu and WC-30%wtCu powders were investigated. WC and WC/Cu powders were milled in a planetary ball mill for 20h. The milled powders were cold compacted at 100, 200, 300 and 400 MPa pressures. The compressibility behavior of the powders was evaluated using the Heckel, Panelli-Ambrosio and Ge models. The results showed that the Panelli-Ambrosio was the preferred equation for description the cold compaction behavior of the milled WC and WC-30%wtCu powders. Also, the most accurate model for describing the compressibility of WC-10%wtCu powders was the Heckel equation. The cold compacts were sintered at 1400°C. It was found that by increasing the cold compaction pressure of powder compacts before sintering, the sinterability of WC-30%wtCu powder compacts was enhanced. However, the cold compaction magnitude was not affected significantly on the sinterability of WC and WC-10%wtCu powders. The microstructural investigations of the sintered samples by Scanning Electron Microscopy (SEM confirmed the presence of porosities at the interface of copper-tungsten carbide phases.

  7. Response to Thermal Exposure of Ball-Milled Aluminum-Borax Powder Blends

    Science.gov (United States)

    Birol, Yucel

    2013-04-01

    Aluminum-borax powder mixtures were ball milled and heated above 873 K (600 °C) to produce Al-B master alloys. Ball-milled powder blends reveal interpenetrating layers of deformed aluminum and borax grains that are increasingly refined with increasing milling time. Thermal exposure of the ball-milled powder blends facilitates a series of thermite reactions between these layers. Borax, dehydrated during heating, is reduced by Al, and B thus generated reacts with excess Al to produce AlB2 particles dispersed across the aluminum grains starting at 873 K (600 °C). AlB2 particles start to form along the interface of the aluminum and borax layers. Once nucleated, these particles grow readily to become hexagonal-shaped crystals that traverse the aluminum grains with increasing temperatures as evidenced by the increase in the size as well as in the number of the AlB2 particles. Ball milling for 1 hour suffices to achieve a thermite reaction between borax and aluminum. Ball milling further does not impact the response of the powder blend to thermal exposure. The nucleation-reaction sites are multiplied, however, with increasing milling time and thus insure a higher number of smaller AlB2 particles. The size of the AlB2 platelets may be adjusted with the ball milling time.

  8. Agglomeration during wet milling of LAST (lead-antimony-silver-tellurium) powders

    International Nuclear Information System (INIS)

    Hall, B.D.; Case, E.D.; Ren, F.; Johnson, J.R.; Timm, E.J.

    2009-01-01

    LAST (lead-antimony-silver-tellurium) compounds comprise a family of semiconducting materials with good thermoelectric properties. However, the as-cast form of LAST exhibits large grain size and hence low mechanical strength. Powder processing can produce a fine powder particle size that enhances fracture strength, however the powders tend to agglomerate if the individual powder diameters are less than a few microns across. Dry milling or wet milling (hexane additions of 0 cm 3 and 10 cm 3 ) produced hard agglomerates roughly 40 μm in diameter while wet milling with hexane additions of 25 cm 3 , 30 cm 3 or 50 cm 3 resulted in small, porous agglomerates roughly 20 μm in diameter. Thus, by adjusting the amount of milling liquid used while milling LAST powders, one can shift from hard to soft agglomerates, where the literature shows that soft agglomerates are less harmful to the final, sintered product. Also, in agreement with the results from the literature on other materials, wet milling of LAST powders produced smaller particle sizes but required longer times to reach the grindability limit

  9. Synthesis of niobium carbide by a high energy milling technique of powder metallurgy

    International Nuclear Information System (INIS)

    Antonello, Rodrigo Tecchio; Gonzalez, Cezar Henrique; Urtiga Filho, Severino Leopoldino; Araujo Filho, Oscar Olimpio de; Ambrozio Filho, Francisco

    2010-01-01

    The aim of this work is to obtain and characterize the Niobium Carbide (NbC) by a suitable high energy milling technique using a SPEX Mill vibratory type and niobium and carbon (graphite) powders. Since this carbide is scarced in the national market and it's necessary to apply this NbC as a reinforcement in two molybdenum high speed steels (AISI M2 and AISI M3:2) object of another work motivated this research. The powders were submitted to a high energy milling procedure for suitable times and conditions and then were characterized by means of Scanning Electronic Microscopy (SEM), Energy Dispersive Spectroscopy (EDS) and X-ray diffraction (DRX) techniques. The ball-to-powder weight ratio was 10:1. The analysed samples showed that the high-energy milling is an alternative route of the NbC synthesis. (author)

  10. Synthesis of niobium carbide (NbC) by powder metallurgy high energy milling technique

    International Nuclear Information System (INIS)

    Antonello, Rodrigo Tecchio; Urtiga Filho, Severino Leopoldino; Araujo Filho, Oscar Olimpio de; Ambrozio Filho, Francisco; Gonzalez, Cezar Henrique

    2009-01-01

    The aim of this work is to obtain and characterize the Niobium Carbide (NbC) by a suitable high energy milling technique using a SPEX Mill vibratory type and niobium and carbon (graphite) powders. Since this carbide is scarce in the national market and it's necessary to apply this NbC as a reinforcement in two molybdenum high speed steels (AISI M2 and AISI M3:2) object of another work motivated this research. The powders were submitted to a high energy milling procedure for suitable times and conditions and then were characterized by means of Scanning Electronic Microscopy (SEM) and X-ray diffraction (DRX) techniques. The ball-to-powder weight ratio was 10:1. The analysed samples showed that the high-energy milling is an alternative route of the NbC synthesis. (author)

  11. Attritor milling of WC + 6% Co: Effects on powder characteristics and compaction behavior

    International Nuclear Information System (INIS)

    Mashl, S.J.; Smith, D.W.; Becking, G.H.; Hale, T.E.

    1987-01-01

    This study examines the effects of attritor milling on the characteristics and bulk behavior of fine tungsten carbide powders (initial median particle size ≅ 1.5 μm) blended with 6 wt. % cobalt (mps ≅ 1.5 μm). Experiments are performed in order to: Develop a process model relating the specific energy input to the milled median particle size. Examine the effect that changes in milling variables have on the specific energy - median particle size relationship. Observe the effects of variation in the initial particle size distribution on the as-milled particle size distribution, the compaction characteristics of the powder, and the shrinkage which will occur during sintering. The process model is based on Charles' equation, E-bar = A (d/sup -α/ - d/sub o//sup -α/) in which E-bar = the specific energy consumed in milling, d and d = the initial and milled median particle sizes respectively, and A and α are constants. Computer curve fitting techniques are employed to determine the values of the coefficient and exponent in the above equation. The resulting model predicts the experimental data within about +- over 10% over a significant range of d/sub o/ and E-Bar values. The apparent density and compactibility of the attritor milled powders are observed to be very sensitive to the milled particle size distribution

  12. Tungsten-nanodiamond composite powders produced by ball milling

    Energy Technology Data Exchange (ETDEWEB)

    Nunes, D., E-mail: daniela.nunes@ist.utl.pt [Associacao Euratom/IST, Instituto de Plasmas e Fusao Nuclear, Instituto Superior Tecnico, Universidade Tecnica de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa (Portugal); LNEG, Estrada do Paco do Lumiar, 1649-038 Lisboa (Portugal); ICEMS, Instituto Superior Tecnico, Av. Rovisco Pais, 1049-001 Lisboa (Portugal); Livramento, V. [Associacao Euratom/IST, Instituto de Plasmas e Fusao Nuclear, Instituto Superior Tecnico, Universidade Tecnica de Lisboa, Av. Rovisco Pais, 1049-001 Lisboa (Portugal); LNEG, Estrada do Paco do Lumiar, 1649-038 Lisboa (Portugal); Mardolcar, U.V. [Departamento de Fisica, Instituto Superior Tecnico, Av. Rovisco Pais, 1049-001 Lisboa (Portugal); Centro de Ciencias Moleculares e Materiais, Faculdade de Ciencias da Universidade de Lisboa, Campo Grande, 1749-016 Lisboa (Portugal); Correia, J.B. [LNEG, Estrada do Paco do Lumiar, 1649-038 Lisboa (Portugal); Carvalho, P.A. [ICEMS, Instituto Superior Tecnico, Av. Rovisco Pais, 1049-001 Lisboa (Portugal); Departamento de Bioengenharia, Instituto Superior Tecnico, Av. Rovisco Pais, 1049-001 Lisboa (Portugal)

    2012-07-15

    The major challenge in producing tungsten-nanodiamond composites by ball milling lies in successfully dispersing carbon nanoparticles in the metallic matrix while keeping carbide formation at a minimum. Processing windows for carbide minimization have been established through systematic variation of the nanodiamond fraction, milling energy and milling time. Materials characterization has been carried out by X-ray diffraction, scanning and transmission electron microscopy and microhardness testing. Nanostructured matrices with homogeneously dispersed particles that preserved the diamond structure have been produced. Differential thermal analysis has been used to evaluate the composites thermal stability.

  13. High resolution Transmission Electron Microscopy characterization of a milled oxide dispersion strengthened steel powder

    Energy Technology Data Exchange (ETDEWEB)

    Loyer-Prost, M., E-mail: marie.loyer-prost@cea.fr [DEN-Service de Recherches de Métallurgie Physique, CEA, Université Paris-Saclay, F-91191, Gif-sur-Yvette (France); Merot, J.-S. [Laboratoire d’Etudes des Microstructures – UMR 104, CNRS/ONERA, BP72-29, Avenue de la Division Leclerc, 92 322, Châtillon (France); Ribis, J. [DEN-Service de Recherches de Métallurgie Appliquée, CEA, Université Paris-Saclay, F-91191, Gif-sur-Yvette (France); Le Bouar, Y. [Laboratoire d’Etudes des Microstructures – UMR 104, CNRS/ONERA, BP72-29, Avenue de la Division Leclerc, 92 322, Châtillon (France); Chaffron, L. [DEN-Service de Recherches de Métallurgie Appliquée, CEA, Université Paris-Saclay, F-91191, Gif-sur-Yvette (France); Legendre, F. [DEN-Service de la Corrosion et du Comportement des Matériaux dans leur Environnement, CEA, Université Paris-Saclay, F-91191, Gif-sur-Yvette (France)

    2016-10-15

    Oxide Dispersion Strengthened (ODS) steels are promising materials for generation IV fuel claddings as their dense nano-oxide dispersion provides good creep and irradiation resistance. Even if they have been studied for years, the formation mechanism of these nano-oxides is still unclear. Here we report for the first time a High Resolution Transmission Electron Microscopy and Energy Filtered Transmission Electron Microscopy characterization of an ODS milled powder. It provides clear evidence of the presence of small crystalline nanoclusters (NCs) enriched in titanium directly after milling. Small NCs (<5 nm) have a crystalline structure and seem partly coherent with the matrix. They have an interplanar spacing close to the (011) {sub bcc} iron structure. They coexist with larger crystalline spherical precipitates of 15–20 nm in size. Their crystalline structure may be metastable as they are not consistent with any Y-Ti-O or Ti-O structure. Such detailed observations in the as-milled grain powder confirm a mechanism of Y, Ti, O dissolution in the ferritic matrix followed by a NC precipitation during the mechanical alloying process of ODS materials. - Highlights: • We observed an ODS ball-milled powder by high resolution transmission microscopy. • The ODS ball-milled powder exhibits a lamellar microstructure. • Small crystalline nanoclusters were detected in the milled ODS powder. • The nanoclusters in the ODS milled powder are enriched in titanium. • Larger NCs of 15–20 nm in size are, at least, partly coherent with the matrix.

  14. Solid-state reactions to synthesize nanostructured lead selenide semiconductor powders by high-energy milling

    Energy Technology Data Exchange (ETDEWEB)

    Rojas-Chavez, H., E-mail: uu_gg_oo@yahoo.com.mx [Centro de Investigacion e Innovacion Tecnologica - IPN, Cerrada de CECATI s/n, Col. Santa Catarina, Del. Azcapotzalco (Mexico) and Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada - IPN, Legaria 694, Col. Irrigacion, Del. Miguel Hidalgo (Mexico); Reyes-Carmona, F. [Facultad de Quimica - UNAM, Circuito de la Investigacion Cientifica s/n, C.U. Del. Coyoacan (Mexico); Jaramillo-Vigueras, D. [Centro de Investigacion e Innovacion Tecnologica - IPN, Cerrada de CECATI s/n, Col. Santa Catarina, Del. Azcapotzalco (Mexico)

    2011-10-15

    Highlights: {yields} PbSe synthesized from PbO instead of Pb powder do not require an inert atmosphere. {yields} During high-energy milling oxygen has to be chemically reduced from the lead oxide. {yields} Solid-state and solid-gas chemical reactions promote both solid and gaseous products. -- Abstract: Both solid-solid and gas-solid reactions have been traced during high-energy milling of Se and PbO powders under vial (P, T) conditions in order to synthesize the PbSe phase. Chemical and thermodynamic arguments are postulated to discern the high-energy milling mechanism to transform PbO-Se micropowders onto PbSe-nanocrystals. A set of reactions were evaluated at around room temperature. Therefore an experimental campaign was designed to test the nature of reactions in the PbO-Se system during high-energy milling.

  15. Solid-state reactions to synthesize nanostructured lead selenide semiconductor powders by high-energy milling

    International Nuclear Information System (INIS)

    Rojas-Chavez, H.; Reyes-Carmona, F.; Jaramillo-Vigueras, D.

    2011-01-01

    Highlights: → PbSe synthesized from PbO instead of Pb powder do not require an inert atmosphere. → During high-energy milling oxygen has to be chemically reduced from the lead oxide. → Solid-state and solid-gas chemical reactions promote both solid and gaseous products. -- Abstract: Both solid-solid and gas-solid reactions have been traced during high-energy milling of Se and PbO powders under vial (P, T) conditions in order to synthesize the PbSe phase. Chemical and thermodynamic arguments are postulated to discern the high-energy milling mechanism to transform PbO-Se micropowders onto PbSe-nanocrystals. A set of reactions were evaluated at around room temperature. Therefore an experimental campaign was designed to test the nature of reactions in the PbO-Se system during high-energy milling.

  16. Powder production of U-Mo alloy, HMD process (Hydriding- Milling- Dehydriding)

    Energy Technology Data Exchange (ETDEWEB)

    Pasqualini, E. E.; Garcia, J.H.; Lopez, M.; Cabanillas, E.; Adelfang, P. [Dept. Combustibles Nucleares. Comision Nacional de Energia Atomica, Av. Gral. Paz 1499, 1650 Buenos Aires (Argentina)

    2002-07-01

    Uranium-molybdenum (U-Mo) alloys can be hydrided massively in metastable {gamma} (gamma) phase. The brittle hydride can be milled and dehydrided to acquire the desired size distributions needed for dispersion nuclear fuels. The developments of the different steps of this process called hydriding-milling- dehydriding (HMD Process) are described. Powder production scales for industrial fabrication is easily achieved with conventional equipment, small man-power and low investment. (author)

  17. Powder production of U-Mo alloy, HMD process (Hydriding- Milling- Dehydriding)

    International Nuclear Information System (INIS)

    Pasqualini, E. E.; Garcia, J.H.; Lopez, M.; Cabanillas, E.; Adelfang, P.

    2002-01-01

    Uranium-molybdenum (U-Mo) alloys can be hydrided massively in metastable γ (gamma) phase. The brittle hydride can be milled and dehydrided to acquire the desired size distributions needed for dispersion nuclear fuels. The developments of the different steps of this process called hydriding-milling- dehydriding (HMD Process) are described. Powder production scales for industrial fabrication is easily achieved with conventional equipment, small man-power and low investment. (author)

  18. Fabrication of Al-20 wt%Si powder using scrap Si by ultra high-energy milling process

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Won-Kyung [Division of Advanced Materials Engineering and Institute for Rare Metals, Kongju National University, 275, Budae-dong, Cheonan, Chungnam 330-717 (Korea, Republic of); Y Latin-Small-Letter-Dotless-I lmaz, Fikret [Department of Physics, Faculty of Art and Science, Gaziosmanpasa University, Tasliciftlik Campus, 60240 Tokat (Turkey); Kim, Hyo-Seob; Koo, Jar-Myung [Division of Advanced Materials Engineering and Institute for Rare Metals, Kongju National University, 275, Budae-dong, Cheonan, Chungnam 330-717 (Korea, Republic of); Hong, Soon-Jik, E-mail: hongsj@kongju.ac.kr [Division of Advanced Materials Engineering and Institute for Rare Metals, Kongju National University, 275, Budae-dong, Cheonan, Chungnam 330-717 (Korea, Republic of)

    2012-09-25

    Highlights: Black-Right-Pointing-Pointer High energy ball milling process has been successfully employed to produce Al-20Si alloy using scrap Si powders. Black-Right-Pointing-Pointer Fully finer and homogenous structure could be achieved after 60 min of milling time. Black-Right-Pointing-Pointer Si particles were not dissolved but uniformly dispersed in the Al matrix in a milled state. Black-Right-Pointing-Pointer The hardness of as-milled Al-20Si powder increased steadily with the increase of milling time. Black-Right-Pointing-Pointer Grain size and dispersion strengthening are two mechanisms being responsible for hardness increment. - Abstract: In this study, microstructural evolution and mechanical properties of Al-20 wt%Si and pure Al powders fabricated by ultra high-energy ball milling technique were investigated as a function of milling time. The microstructure and mechanical properties of the as-milled powders were examined by scanning electron microscope (SEM), energy dispersive spectrometry (EDS), X-ray diffractometer (XRD) and Vickers hardness tester. SEM observation showed that the particle size increased at an early stage of milling, and then decreased drastically with further milling. XRD and cross-sectional EDS-mapping analyses revealed that Si particles were not dissolved but uniformly dispersed in the Al matrix in a milled state. Vickers hardness of both pure Al and Al-Si powder increases with milling time, which attributes to the grain size strengthening and dispersion strengthening.

  19. Influence of starting powder milling on magnetic properties of Mn-Zn ferrite

    Directory of Open Access Journals (Sweden)

    Miodrag M. Milutinov

    2017-06-01

    Full Text Available In this paper, the influence of additional sieving and milling of starting industrial Mn-Zn powders on magnetic properties was investigated. The starting powder was milled for 60 minutes, followed by sieving through 325 and 400 meshes. The starting and milled powders were used to fabricate toroid shaped samples sintered at 1200°C for 2 hours. Structural parameters of the fabricated samples were analysed by X-ray diffraction and scanning electron microscopy. Complex permeability, core loss density, and hysteresis were measured using the modified watt-meter method. The complex permeability and hysteresis loop were modelled with a new model proposed in the paper. The core loss density was modelled with the Steinmetz empirical equation. The experimental results and calculations show the significance of the additional milling and sieving process on magnetic properties of Mn-Zn ferrite in the frequency range 0.1-10MHz. These processes increase the relative permeability about 3 times and decrease the core loss 4 times by milling of the starting powder.

  20. The precursors effects on biomimetic hydroxyapatite ceramic powders.

    Science.gov (United States)

    Yoruç, Afife Binnaz Hazar; Aydınoğlu, Aysu

    2017-06-01

    In this study, effects of the starting material on chemical, physical, and biological properties of biomimetic hydroxyapatite ceramic powders (BHA) were investigated. Characterization and chemical analysis of BHA powders were performed by using XRD, FT-IR, and ICP-AES. Microstructural features such as size and morphology of the resulting BHA powders were characterized by using BET, nano particle sizer, pycnometer, and SEM. Additionally, biological properties of the BHA ceramic powders were also investigated by using water-soluble tetrazolium salts test (WST-1). According to the chemical analysis of BHA ceramic powders, chemical structures of ceramics which are prepared under different conditions and by using different starting materials show differences. Ceramic powders which are produced at 80°C are mainly composed of hydroxyapatite, dental hydroxyapatite (contain Na and Mg elements in addition to Ca), and calcium phosphate sulfide. However, these structures are altered at high temperatures such as 900°C depending on the features of starting materials and form various calcium phosphate ceramics and/or their mixtures such as Na-Mg-hydroxyapatite, hydroxyapatite, Mg-Whitlockit, and chloroapatite. In vitro cytotoxicity studies showed that amorphous ceramics produced at 80°C and ceramics containing chloroapatite structure as main or secondary phases were found to be extremely cytotoxic. Furthermore, cell culture studies showed that highly crystalline pure hydroxyapatite structures were extremely cytotoxic due to their high crystallinity values. Consequently, the current study indicates that the selection of starting materials which can be used in the production of calcium phosphate ceramics is very important. It is possible to produce calcium phosphate ceramics which have sufficient biocompatibility at physiological pH values and by using appropriate starting materials. Copyright © 2017 Elsevier B.V. All rights reserved.

  1. Fabrication, characterization and application of Cu{sub 2}ZnSn(S,Se){sub 4} absorber layer via a hybrid ink containing ball milled powders

    Energy Technology Data Exchange (ETDEWEB)

    Li, Chunran [State Key Laboratory of Superhard Materials and College of Physics, Jilin University, Changchun 130023 (China); Key Laboratory of Physics and Technology for Advanced Batteries (Ministry of Education), College of Physics, Jilin University, Changchun 130012 (China); College of Mathematics and Physics, Bohai University, Jinzhou 121013 (China); Yao, Bin, E-mail: binyao@jlu.edu.cn [State Key Laboratory of Superhard Materials and College of Physics, Jilin University, Changchun 130023 (China); Key Laboratory of Physics and Technology for Advanced Batteries (Ministry of Education), College of Physics, Jilin University, Changchun 130012 (China); Li, Yongfeng, E-mail: liyongfeng@jlu.edu.cn [Key Laboratory of Physics and Technology for Advanced Batteries (Ministry of Education), College of Physics, Jilin University, Changchun 130012 (China); Xiao, Zhenyu [State Key Laboratory of Superhard Materials and College of Physics, Jilin University, Changchun 130023 (China); Ding, Zhanhui [Key Laboratory of Physics and Technology for Advanced Batteries (Ministry of Education), College of Physics, Jilin University, Changchun 130012 (China); Zhao, Haifeng; Zhang, Ligong; Zhang, Zhenzhong [State Key Laboratory of Luminescence and Applications, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, No. 3888 Dongnanhu Road, Changchun 130033 (China)

    2015-09-15

    Highlights: • CZTS powders are prepared from binary sulfides by a low cost ball milling process. • Elaborated on phase evolution and formation mechanism of CZTS. • Proposed a hybrid ink approach to resolve difficulty in deposition of CZTS film. • CZTSSe solar cells with highest efficiency of 4.2% are fabricated. • Small-grained CZTS layer hinders the collection of minority carriers. - Abstract: Cu{sub 2}ZnSnS{sub 4} (CZTS) powder with kesterite structure was prepared by ball milling of mixture of Cu{sub 2}S, ZnS and SnS{sub 2} powders for more than 15 h. By dispersing the milled CZTS powder in a Cu-, Zn- and Sn-chalcogenide precursor solution, a hybrid ink was fabricated. With the hybrid ink, a precursor CZTS film was deposited on Mo coated soda-lime glass by spin-coating. In order to obtain Cu{sub 2}ZnSn(S,Se){sub 4} (CZTSSe) absorber film with kesterite structure, the CZTS film was annealed at 560 °C for 15 min in Se ambient. It is demonstrated that the annealed film is dominated by a thick layer of kesterite CZTSSe with larger grain size and Cu{sub 8}Fe{sub 3}Sn{sub 2}(S,Se){sub 12} impurity phase with the exception of a very thin layer of kesterite CZTS with smaller grain size at interface between the CZTSSe and Mo layers. Solar cell device was fabricated by using the annealed CZTSSe film as absorber layer, and its conversion efficiency reached 4.2%. Mechanism of formation of the kesterite CZTS powder and CZTSSe film as well as effect of impurity phases on conversion efficiency are discussed in the present paper. The present results suggest that the hybrid ink approach combining with ball milling is a simple, low cost and promising method for preparation of kesterite CZTSSe absorber film and CZTSSe-based solar cell.

  2. Microstructural analysis of sinterized aluminum powder obtained by the high energy milling of beverage cans

    International Nuclear Information System (INIS)

    Souza, Jose Raelson Pereira de; Peres, Mauricio Mhirdaui

    2016-01-01

    The objective is the study of the effect of high energy milling on the sintering of aluminum from beverage cans. The selected aluminum cans were cut and subjected to high energy milling under a common atmosphere (in the air). In milling, three grams of aluminum was used to maintain the ratio of 10/1 between the mass of the beads and the material. The milling time was varied in 1h, 1.5h and 2h, keeping the other variables constant. The particle size distribution was measured by laser granulometry, for further compaction and sintering at a temperature of 600 ° C for 2 h. The samples were characterized by scanning electron microscopy (SEM). The granulometric analysis of the powders found that higher milling times produced finer particles. Powders with granulometry of less than 45 μm were obtained at 1 h, 1.5 h and 2 h times. The times of 1.5h and 2h promoted finer particles with better distribution of size. The SEM analyzes showed little variation in the shape of the particles as a function of the variation of the grinding times, presenting irregularities in the platelet geometry. The sintering time and temperature were effective in the densification of the powder particles, which were influenced by the average particle size

  3. Comprehensive characterization of ball-milled powders simulating a tribofilm system

    Energy Technology Data Exchange (ETDEWEB)

    Häusler, I., E-mail: ines.haeusler@bam.de; Dörfel, I., E-mail: Ilona.doerfel@bam.de; Peplinski, B., E-mail: Burkhard.peplinski@bam.de; Dietrich, P.M., E-mail: Paul.dietrich@yahoo.de; Unger, W.E.S., E-mail: Wolfgang.Unger@bam.de; Österle, W., E-mail: Werner.Oesterle@bam.de

    2016-01-15

    A model system was used to simulate the properties of tribofilms which form during automotive braking. The model system was prepared by ball milling of a blend of 70 vol.% iron oxides, 15 vol.% molybdenum disulfide and 15 vol.% graphite. The resulting mixture was characterized by X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and various transmission electron microscopic (TEM) methods, including energy dispersive X-ray spectroscopy (EDXS), high resolution investigations (HRTEM) with corresponding simulation of the HRTEM images, diffraction methods such as scanning nano-beam electron diffraction (SNBED) and selected area electron diffraction (SAED). It could be shown that the ball milling caused a reduction of the grain size of the initial components to the nanometer range. Sometimes even amorphization or partial break-down of the crystal structure was observed for MoS{sub 2} and graphite. Moreover, chemical reactions lead to a formation of surface coverings of the nanoparticles by amorphous material, molybdenum oxides, and iron sulfates as derived from XPS. - Highlights: • Ball milling of iron oxides, MoS{sub 2}, and graphite to simulate a tribofilm • Increasing coefficient of friction after ball milling of the model blend • Drastically change of the diffraction pattern of the powder mixture • TEM & XPS showed the components of the milled mixture and the process during milling. • MoS{sub 2} and graphite suffered a loss in translation symmetry or became amorphous.

  4. The influence of precursor powders on the microstructure and properties of B-2212 blocks

    International Nuclear Information System (INIS)

    Santos, F.F.M.; Polasek, A.; Saleh, L.A.; Sena, C.V. de; Serra, E.T.; Rizzo, F.

    2006-01-01

    The Bi-2212 is one of the main HTSC's for applications development. The present work reports our investigations on the partial melt processing of bulk-2212. The precursors were uniaxially pressed into silver molds, which were partially melted, slow cooled and subsequently annealed. Precursor powders with different nominal compositions, with and without silver powder addition were employed. Samples were analyzed by XRD, SEM/EDS and DTA. The DC critical current (lc) was measured by the four-points method (77 K). Although the partial melt processing has been intensively studied, there is still a lack of knowledge on the influence on the final properties of bulk Bi-2212. (author)

  5. Simplification of the processing of milled aluminium powder and mechanical evaluation properties

    International Nuclear Information System (INIS)

    Cintas, J.; Rodriguez, J. A.; Gallardo, J. M.; Herrera, E. J.

    2001-01-01

    An alternative powder.metallurgy consolidation method of milled aluminium (M Al) powder, consisting in a double cycle of cold pressing and vacuum sintering, has been developed. The aim of the present investigation is to simplify this consolidation method, from the original five steps to only three steps. This would be possible since milled powders soften during desassing, at high temperature. The mechanical properties of compacts (hardness at room and high temperature, ultimate tensile strength and elongation) obtained by the three-step and the five-step processing are comparable. This process could be ol special interest for the manufacturing of large series of small parts, such as are used in the automotive industry. (Author) 10 refs

  6. Obtaining beta phase in Ti through processing in high energy mill powders of Ti and Nb

    International Nuclear Information System (INIS)

    Milanez, Mateus; Ferretto, Aline; Rocha, Marcio Roberto da; Arnt, Angela Coelho; Milanez, Alexandre; Schaeffer, Lirio

    2014-01-01

    An orthopedic implant, ideal, must meet the requirements of biocompatibility, have good mechanical properties among others. Titanium and Niobium exhibit biocompatibility and the β-Ti phase relationships have the highest strength / weight among all titanium alloys, presenting lower values of elastic modulus. The alloy has mechanically produced specific microstructural characteristics and improved mechanical properties compared with conventional powder metallurgy. In this study, a titanium alloy with different additions of niobium was used. The metal powders were mixed via mechanical alloy in high energy mill (attritor). The powder samples were analyzed by X-ray diffraction (X-RD) and property held by adhesive wear testing with a Pin-on-Disk. The present study revealed that through the high-energy milling is possible the atomic interaction between Ti and Nb particles and the mechanical properties are affected by the concentration of Nb. (author)

  7. Positron annihilation lifetime spectroscopy of mechanically milled protein fibre powders and their free volume aspects

    International Nuclear Information System (INIS)

    Patil, K; Rajkhowa, R; Tsuzuki, T; Lin, T; Wang, X; Sellaiyan, S; Smith, S V; Uedono, A

    2013-01-01

    The present study reports the fabrication of ultra-fine powders from animal protein fibres such as cashmere guard hair, merino wool and eri silk along with their free volume aspects. The respectively mechanically cleaned, scoured and degummed cashmere guard hair, wool and silk fibres were converted into dry powders by a process sequence: Chopping, Attritor Milling, and Spray Drying. The fabricated protein fibre powders were characterised by scanning electron microscope, particle size distribution and positron annihilation lifetime spectroscopy (PALS). The PALS results indicated that the average free volume size in protein fibres increased on their wet mechanical milling with a decrease in the corresponding intensities leading to a resultant decrease in their fractional free volumes.

  8. Alloying and microstructural changes in platinum–titanium milled and annealed powders

    International Nuclear Information System (INIS)

    Maweja, Kasonde; Phasha, M.J.; Yamabe-Mitarai, Y.

    2012-01-01

    Graphical abstract: (a) SE-SEM micrographs of PtTi martensite formed in powder milled for short time annealed at 1500 °C and quenched in helium gas flow (b) BSE-SEM of structure formed after slow cooling. Highlights: ► A disordered metastable FCC Pt(Ti) solid solution was formed after longer milling period. ► HCP Ti crystals were first deformed and then the atoms were dissolved in strained FCC Pt lattices. ► Longer milling time suppressed the occurrence of martensitic transformation after annealing. ► Martensite phase was formed in products that went through a short milling time then annealed and quenched. ► The width of the martensite features formed was smaller at higher cooling rates. - Abstract: Equiatomic platinum–titanium powder mixtures were processed by high energy ball milling under argon atmosphere and sintered under vacuum. Evolution of the crystal structures and microstructures of the products formed were investigated by XRD and SEM techniques, respectively. The HCP crystals of Ti were first deformed and then a disordered metastable FCC Pt(Ti) solid solution was formed during milling due to semi-coherency of FCC lattices. A nanostructured Pt(Ti) product was formed after long milling time, which contained 44–47 at.% Ti and 53–56 at.% Pt. An ordered PtTi intermetallic was formed by annealing the metastable Pt(Ti) at temperature above 1300 °C. The crystal structure and microstructure of the TiPt phase depended on the milling time, annealing temperature and the cooling rate. The B19 PtTi plate martensite was formed after annealing at 1500 °C and quenching at a cooling rate of 23 °C/min to 200 °C/min for short time milled products. The width of martensite features was smaller at high cooling rate. In PtTi products milled for longer time, no martensitic transformation was observed on cooling the annealed samples. Small amounts of Pt 5 Ti 3 were formed in the powders milled for 16 h or more, followed by annealing at 1500 °C and furnace

  9. An investigation on the compressibility of aluminum/nano-alumina composite powder prepared by blending and mechanical milling

    International Nuclear Information System (INIS)

    Razavi Hesabi, Z.; Hafizpour, H.R.; Simchi, A.

    2007-01-01

    The densification response of aluminum powder reinforced with 5 vol.% nanometric alumina particles (35 nm) during uniaxial compaction in a rigid die was studied. The composite powder was prepared by blending and mechanical milling procedures. To determine the effect of the reinforcement nanoparticles on the compressibility of aluminum powder, monolithic Al powder, i.e. without the addition of alumina, was also examined. It was shown that at the early stage of compaction when the rearrangement of particles is the dominant mechanism of the densification, disintegration of the nanoparticle clusters and agglomerates under the applied load contributes in the densification of the composite powder prepared by blending method. As the compaction pressure increases, however, the load partitioning effect of the nanoparticles decreases the densification rate of the powder mixture, resulting in a lower density compared to the monolithic aluminum. It was also shown that mechanical milling significantly impacts the compressibility of the unreinforced and reinforced aluminum powders. Morphological changes of the particles upon milling increase the contribution of particle rearrangement in densification whilst the plastic deformation mechanism is significantly retarded due to the work-hardening effect of the milling process. Meanwhile, the distribution of alumina nanoparticles is improved by mechanical milling, which in fact, affects the compressibility of the composite powder. This paper addresses the effect of mechanical milling and reinforcement nanoparticles on the compressibility of aluminum powder

  10. Effect of milling variables on powder character and sintering behaviour of 434L ferritic stainless steel-Al2O3 composites

    International Nuclear Information System (INIS)

    Mukherjee, S.K.; Upadhyaya, G.S.

    1985-01-01

    Ball milling of ferritic stainless steel-4 vol% Al 2 O 3 powder was carried out for the duration up to 222 ks. Attritor milling of ferritic stainless steel-6 vol% Al 2 O 3 were also carried out for the duration up to 32.4 ks. The characterization of the milled powders were performed. The sintering of ball milled powders was carried out at 1623 K for 10.8 ks in hydrogen. The premix of as received stainless steel powder and the attritor milled powder was also sintered at 1623 K for 3.6 ks in hydrogen. The results showed that an optimum ball milling period in between 58 and 173 ks was required to achieve better sintered properties. The attritor milling was more effective in grinding the powders as compared to ball milling, and the sinterability was also higher for such powders. (author)

  11. Fabrication of Biochips with Micro Fluidic Channels by Micro End-milling and Powder Blasting

    Directory of Open Access Journals (Sweden)

    Dong Sam Park

    2008-02-01

    Full Text Available For microfabrications of biochips with micro fluidic channels, a large number of microfabrication techniques based on silicon or glass-based Micro-Electro-Mechanical System (MEMS technologies were proposed in the last decade. In recent years, for low cost and mass production, polymer-based microfabrication techniques by microinjection molding and micro hot embossing have been proposed. These techniques, which require a proper photoresist, mask, UV light exposure, developing, and electroplating as a preprocess, are considered to have some problems. In this study, we propose a new microfabrication technology which consists of micro end-milling and powder blasting. This technique could be directly applied to fabricate the metal mold without any preprocesses. The metal mold with micro-channels is machined by micro end-milling, and then, burrs generated in the end-milling process are removed by powder blasting. From the experimental results, micro end-milling combined with powder blasting could be applied effectively for fabrication of the injection mold of biochips with micro fluidic channels.

  12. Characterization of Tool Wear in High-Speed Milling of Hardened Powder Metallurgical Steels

    Directory of Open Access Journals (Sweden)

    Fritz Klocke

    2011-01-01

    Full Text Available In this experimental study, the cutting performance of ball-end mills in high-speed dry-hard milling of powder metallurgical steels was investigated. The cutting performance of the milling tools was mainly evaluated in terms of cutting length, tool wear, and cutting forces. Two different types of hardened steels were machined, the cold working steel HS 4-2-4 PM (K490 Microclean/66 HRC and the high speed steel HS 6-5-3 PM (S790 Microclean/64 HRC. The milling tests were performed at effective cutting speeds of 225, 300, and 400 m/min with a four fluted solid carbide ball-end mill (0 = 6, TiAlN coating. It was observed that by means of analytically optimised chipping parameters and increased cutting speed, the tool life can be drastically enhanced. Further, in machining the harder material HS 4-2-4 PM, the tool life is up to three times in regard to the less harder material HS 6-5-3 PM. Thus, it can be assumed that not only the hardness of the material to be machined plays a vital role for the high-speed dry-hard cutting performance, but also the microstructure and thermal characteristics of the investigated powder metallurgical steels in their hardened state.

  13. XRD analysis and microstructure of milled and sintered V, W, C, and Co powders

    CSIR Research Space (South Africa)

    Bolokang, AS

    2011-01-01

    Full Text Available on the starting compositions of pure elements, their lattice coherency according to Hume-Rothery rules on crystal structure and atomic size, and enough milling time that provides adequate kinetics. Keywords ? X-ray analysis; ? (V,W)C; ? Co15W8C6...-1 International Journal of Refractory Metals and Hard Materials Volume 29, Issue 1, January 2011, Pages 108?111 XRD analysis and microstructure of milled and sintered V, W, C, and Co powders ? A.S. Bolokang ? M.J. Phasha ? C. Oliphant ? D. Motaung ? a...

  14. NiTiO3 powders obtained by polymeric precursor method: Synthesis and characterization

    International Nuclear Information System (INIS)

    Lopes, K.P.; Cavalcante, L.S.; Simoes, A.Z.; Varela, J.A.; Longo, E.; Leite, E.R.

    2009-01-01

    Nickel titanate (NiTiO 3 ) powders were synthesized by the polymeric precursor method after thermal treatment at different temperatures for 2 h in air atmosphere. The decomposition of the precursors was monitored by differential scanning calorimetry and thermogravimetric analysis. The NiTiO 3 powders presented a reduction in the specific surface area and increase of the average particle size with the evolution of the temperature. The structural evolution of NiTiO 3 phase was accompanied by X-ray diffraction and Fourier transform Raman spectroscopy. By scanning electron microscopy was revealed the agglomerated nature of very fine particles of NiTiO 3 powders annealed from 600 to 1000 deg. C

  15. Nanocrystallite characterization of milled simulated dry process fuel powders by neutron diffraction

    International Nuclear Information System (INIS)

    Ryu, Ho Jin; Kang, Kwon Ho; Moon, Je Sun; Song, Kee Chan; Choi, Yong Nam

    2003-01-01

    The nano-scale crystallite sizes of simulated spent fuel powders were measured by the neutron diffraction line broadening method in order to analyze the sintering behavior of the dry process fuel. The mixed U0 2 and fission product oxide powders were dry-milled in an attritor for 30, 60, and 120 min. The diffraction patterns of the powders were obtained by using the high resolution powder diffractometer in the HANARO research reactor. Diffraction line broadening due to crystallite size was measured using various techniques such as the Stokes' deconvolution, profile fitting methods using Cauchy function, Gaussian function, and Voigt function, and the Warren-Averbach method. The r.m.s. strain, stacking fault, twin and dislocation density were measured using the information from the diffraction pattern. The realistic crystallite size can be obtained after separation of the contribution from the non-uniform strain, stacking fault and twin

  16. Effect of Milling Time on the Microstructure, Physical and Mechanical Properties of Al-Al2O3 Nanocomposite Synthesized by Ball Milling and Powder Metallurgy

    Directory of Open Access Journals (Sweden)

    Meysam Toozandehjani

    2017-10-01

    Full Text Available The effect of milling time on the morphology, microstructure, physical and mechanical properties of pure Al-5 wt % Al2O3 (Al-5Al2O3 has been investigated. Al-5Al2O3 nanocomposites were fabricated using ball milling in a powder metallurgy route. The increase in the milling time resulted in the homogenous dispersion of 5 wt % Al2O3 nanoparticles, the reduction of particle clustering, and the reduction of distances between the composite particles. The significant grain refining during milling was revealed which showed as a reduction of particle size resulting from longer milling time. X-Ray diffraction (XRD analysis of the nanocomposite powders also showed that designated ball milling contributes to the crystalline refining and accumulation of internal stress due to induced severe plastic deformation of the particles. It can be argued that these morphological and microstructural variations of nanocomposite powders induced by designated ball milling time was found to contribute to an improvement in the density, densification, micro-hardness (HV, nano-hardness (HN, and Young’s modulus (E of Al-5Al2O3 nanocomposites. HV, HN, and E values of nanocomposites were increased by ~48%, 46%, and 40%, after 12 h of milling, respectively.

  17. Effect of Milling Time on the Microstructure, Physical and Mechanical Properties of Al-Al2O3 Nanocomposite Synthesized by Ball Milling and Powder Metallurgy

    Science.gov (United States)

    Matori, Khamirul Amin; Ostovan, Farhad; Abdul Aziz, Sidek; Mamat, Md Shuhazlly

    2017-01-01

    The effect of milling time on the morphology, microstructure, physical and mechanical properties of pure Al-5 wt % Al2O3 (Al-5Al2O3) has been investigated. Al-5Al2O3 nanocomposites were fabricated using ball milling in a powder metallurgy route. The increase in the milling time resulted in the homogenous dispersion of 5 wt % Al2O3 nanoparticles, the reduction of particle clustering, and the reduction of distances between the composite particles. The significant grain refining during milling was revealed which showed as a reduction of particle size resulting from longer milling time. X-Ray diffraction (XRD) analysis of the nanocomposite powders also showed that designated ball milling contributes to the crystalline refining and accumulation of internal stress due to induced severe plastic deformation of the particles. It can be argued that these morphological and microstructural variations of nanocomposite powders induced by designated ball milling time was found to contribute to an improvement in the density, densification, micro-hardness (HV), nano-hardness (HN), and Young’s modulus (E) of Al-5Al2O3 nanocomposites. HV, HN, and E values of nanocomposites were increased by ~48%, 46%, and 40%, after 12 h of milling, respectively. PMID:29072632

  18. Effect of Milling Time on the Microstructure, Physical and Mechanical Properties of Al-Al₂O₃ Nanocomposite Synthesized by Ball Milling and Powder Metallurgy.

    Science.gov (United States)

    Toozandehjani, Meysam; Matori, Khamirul Amin; Ostovan, Farhad; Abdul Aziz, Sidek; Mamat, Md Shuhazlly

    2017-10-26

    The effect of milling time on the morphology, microstructure, physical and mechanical properties of pure Al-5 wt % Al₂O₃ (Al-5Al₂O₃) has been investigated. Al-5Al₂O₃ nanocomposites were fabricated using ball milling in a powder metallurgy route. The increase in the milling time resulted in the homogenous dispersion of 5 wt % Al₂O₃ nanoparticles, the reduction of particle clustering, and the reduction of distances between the composite particles. The significant grain refining during milling was revealed which showed as a reduction of particle size resulting from longer milling time. X-Ray diffraction (XRD) analysis of the nanocomposite powders also showed that designated ball milling contributes to the crystalline refining and accumulation of internal stress due to induced severe plastic deformation of the particles. It can be argued that these morphological and microstructural variations of nanocomposite powders induced by designated ball milling time was found to contribute to an improvement in the density, densification, micro-hardness ( HV ), nano-hardness ( HN ), and Young's modulus ( E ) of Al-5Al₂O₃ nanocomposites. HV , HN , and E values of nanocomposites were increased by ~48%, 46%, and 40%, after 12 h of milling, respectively.

  19. Preparation of 50Ni-45Ti-5Zr powders by high-energy ball milling and hot pressing

    Energy Technology Data Exchange (ETDEWEB)

    Marinzeck de Alcantara Abdala, Julia, E-mail: juabdala@yahoo.com.b [Instituto de Pesquisa e Desenvolvimento, Universidade do Vale do Paraiba, Av. Shishima Hifumi, 2911, 12244-000 Sao Jose dos Campos (Brazil); Bacci Fernandes, Bruno, E-mail: brunobacci@yahoo.com.b [Divisao de Engenharia Mecanica, Instituto Tecnologico de Aeronautica, Praca Marechal-do-Ar Eduardo Gomes, 50, 12228-904 Sao Jose dos Campos (Brazil); Santos, Dalcy Roberto dos, E-mail: dalcy@iae.cta.b [Instituto de Aeronautica e Espaco, Centro Tecnologico Aeroespacial, Praca Marechal-do-Ar Eduardo Gomes, 50, 12228-904 Sao Jose dos Campos (Brazil); Rodrigues Henriques, Vinicius Andre, E-mail: vinicius@iae.cta.b [Instituto de Aeronautica e Espaco, Centro Tecnologico Aeroespacial, Praca Marechal-do-Ar Eduardo Gomes, 50, 12228-904 Sao Jose dos Campos (Brazil); Moura Neto, Carlos de, E-mail: mneto@ita.b [Divisao de Engenharia Mecanica, Instituto Tecnologico de Aeronautica, Praca Marechal-do-Ar Eduardo Gomes, 50, 12228-904 Sao Jose dos Campos (Brazil); Saraiva Ramos, Alfeu, E-mail: alfeu@univap.b [Instituto de Pesquisa e Desenvolvimento, Universidade do Vale do Paraiba, Av. Shishima Hifumi, 2911, 12244-000 Sao Jose dos Campos (Brazil)

    2010-04-16

    This study reports on the preparation of the 50Ni-45Ti-5Zr (at.%) alloy by high-energy ball milling and hot pressing. The elemental powder mixture was processed in silicon nitride and hardened steel vials, and samples were collected after different milling times. To recover the previous powders in addition wet milling isopropyl alcohol (for 20 min) was adopted. The mechanically alloyed powders were hot-pressed under vacuum at 900 {sup o}C for 1 h using pressure levels close to 200 MPa. The milled powders were characterized by means of scanning electron microscopy, X-ray diffraction, and energy dispersive spectrometry techniques. It was noted that the ductile starting powders were continuously cold-welded during ball milling. This fact was more pronounced during the processing of 50Ni-45Ti-5Zr powders in hardened steel vial. After milling for 5 h, the results suggested that amorphous and nanocrystalline structures were achieved. The complete consolidation was found after hot pressing of mechanically alloyed 50Ni-45Ti-5Zr powders, and a large amount of the B2-NiTi phase was formed mainly after processing in stainless steel balls and vial.

  20. Sintered Fe-Ni-Cu-Sn-C Alloys Made of Ball-Milled Powders

    Directory of Open Access Journals (Sweden)

    Romański A.

    2014-10-01

    Full Text Available The main objective of this paper was to perform sinterability studies of ball-milled Fe-12%Ni-6.4%Cu-1.6%Sn-0.6%C powders. A mixture of precisely weighed amounts of elemental iron, nickel and graphite, and pre-alloyed 80/20 bronze powders was ball-milled for 8, 30 and 120 hours. After cold-pressing at 400 MPa the specimens were sintered at 900oC for 30 minutes in a reducing atmosphere and subsequently tested for density and hardness as well as subjected to structural studies using scanning electron microscopy (SEM and X-ray diffraction (XRD analysis.

  1. Dopants incorporation in ZnO mechanical milled powders sensed by positrons

    International Nuclear Information System (INIS)

    Damonte, L. C.; Donderis, V.; Hernandez Fenollosa, M. A.

    2007-01-01

    M-doped ZnO (M: Cd, Mg) powders obtained by mechanical milling were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and positron lifetime annihilation spectroscopy (PALS). The mixing of the oxides is followed by means of XRD and SEM. As milling proceeds, a clear reduction of grain size and homogenization are observed. The evolution of annihilation parameters with milling time and cation content were analyzed and related with the kind of mechanical induced defect involved. Ternary oxides Zn 1-x M x O were efficiency obtained for certain compositions. The results showed that positrons constitute a well suited probe to characterize the cation substitution in the ZnO oxide lattice.

  2. Dopants incorporation in ZnO mechanical milled powders sensed by positrons

    Energy Technology Data Exchange (ETDEWEB)

    Damonte, L. C., E-mail: damonte@fisica.unlp.edu.ar; Donderis, V.; Hernandez Fenollosa, M. A. [Universidad Politecnica de Valencia, Departamento de Fisica Aplicada (Spain)

    2007-09-15

    M-doped ZnO (M: Cd, Mg) powders obtained by mechanical milling were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and positron lifetime annihilation spectroscopy (PALS). The mixing of the oxides is followed by means of XRD and SEM. As milling proceeds, a clear reduction of grain size and homogenization are observed. The evolution of annihilation parameters with milling time and cation content were analyzed and related with the kind of mechanical induced defect involved. Ternary oxides Zn{sub 1-x}M{sub x}O were efficiency obtained for certain compositions. The results showed that positrons constitute a well suited probe to characterize the cation substitution in the ZnO oxide lattice.

  3. Synthesis and characterization of high volume fraction Al-Al2O3 nanocomposite powders by high-energy milling

    International Nuclear Information System (INIS)

    Prabhu, B.; Suryanarayana, C.; An, L.; Vaidyanathan, R.

    2006-01-01

    Al-Al 2 O 3 metal matrix composite (MMC) powders with volume fractions of 20, 30, and 50% Al 2 O 3 were synthesized by high-energy milling of the blended component powders. The particle sizes of Al 2 O 3 studied were 50 nm, 150 nm, and 5 μm. A uniform distribution of the Al 2 O 3 reinforcement in the Al matrix was successfully obtained after milling the powders for a period of 20 h at a ball-to-powder ratio of 10:1 in a SPEX mill. The uniform distribution of Al 2 O 3 in the Al matrix was confirmed by characterizing these nanocomposite powders by scanning electron microscopy (SEM), energy dispersive spectrometry (EDS), X-ray mapping, and X-ray diffraction (XRD) techniques

  4. Synthesis and optical properties of Mg-Al layered double hydroxides precursor powders

    Directory of Open Access Journals (Sweden)

    Chia-Hsuan Lin

    2017-12-01

    Full Text Available The synthesis and optical properties of Mg-Al layered double hydroxide (LDH precursor powders were investigated using X-ray diffraction (XRD, Fourier transform-infrared (FT-IR spectroscopy, transmission electron microscopy (TEM, selected area electron diffraction (SAED, high-resolution TEM (HRTEM, UV-transmission spectrometer, and fluorescence spectrophotometer. The FT-IR results show that the intense absorption at around 1363–1377 cm-1 can be assigned to the antisymmetric ν3 mode of interlayer carbonate anions because the LDH phase contains some CO32-. The XRD results show that all of the Mg-Al LDH precursor powders contain only a single phase of [Mg0.833Al0.167(OH2](CO30.083·(H2O0.75 but have broad and weak intensities of peaks. All of Mg-Al LDHs precursor powders before calcination have the same photoluminescence (PL spectra. Moreover, these spectra were excited at λex = 235 nm, and the broad emission band was in the range 325-650 nm. In the range, there were relatively strong intensity at around 360, 407 and 510 nm, respectively.

  5. Processing of Polysulfone to Free Flowing Powder by Mechanical Milling and Spray Drying Techniques for Use in Selective Laser Sintering

    Directory of Open Access Journals (Sweden)

    Nicolas Mys

    2016-04-01

    Full Text Available Polysulfone (PSU has been processed into powder form by ball milling, rotor milling, and spray drying technique in an attempt to produce new materials for Selective Laser Sintering purposes. Both rotor milling and spray drying were adept to make spherical particles that can be used for this aim. Processing PSU pellets by rotor milling in a three-step process resulted in particles of 51.8 μm mean diameter, whereas spray drying could only manage a mean diameter of 26.1 μm. The resulting powders were characterized using Differential Scanning Calorimetry (DSC, Gel Permeation Chromatography (GPC and X-ray Diffraction measurements (XRD. DSC measurements revealed an influence of all processing techniques on the thermal behavior of the material. Glass transitions remained unaffected by spray drying and rotor milling, yet a clear shift was observed for ball milling, along with a large endothermic peak in the high temperature region. This was ascribed to the imparting of an orientation into the polymer chains due to the processing method and was confirmed by XRD measurements. Of all processed powder samples, the ball milled sample was unable to dissolve for GPC measurements, suggesting degradation by chain scission and subsequent crosslinking. Spray drying and rotor milling did not cause significant degradation.

  6. Structural evolution of Ni-20Cr alloy during ball milling of elemental powders

    International Nuclear Information System (INIS)

    Lopez B, I.; Trapaga M, L. G.; Martinez F, E.; Zoz, H.

    2011-01-01

    The ball milling (B M) of blended Ni and Cr elemental powders was carried out in a Simoloyer performing on high-energy scale mode at maximum production to obtain a nano structured Ni-20Cr alloy. The phase transformations and structural changes occurring during mechanical alloying were investigated by X-ray diffraction (XRD) and optical microscopy (Om). A gradual solid solubility of Cr and the subsequent formation of crystalline metastable solid solutions described in terms of the Avrami-Ero fe ev kinetics model were calculated. The XRD analysis of the structure indicates that cumulative lattice strain contributes to the driving force for solid solution between Ni and Cr during B M. Microstructure evolution has shown, additionally to the lamellar length refinement commonly observed, the folding of lamellae in the final processing stage. Om observations revealed that the lamellar spacing of Ni rich zones reaches a steady value near 500 nm and almost disappears after 30 h of milling. (Author)

  7. Structural evolution of Ni-20Cr alloy during ball milling of elemental powders

    Energy Technology Data Exchange (ETDEWEB)

    Lopez B, I.; Trapaga M, L. G. [IPN, Centro de Investigacion y de Estudios Avanzados, Unidad Queretaro, Libramiento Norponiente No. 2000, Juriquilla, 76230 Queretaro (Mexico); Martinez F, E. [Centro de Investigacion e Innovacion Tecnologica, Cerrada de Cecati s/n, Col. Santa Catarina Azcapotzalco, 02250 Mexico D. F. (Mexico); Zoz, H., E-mail: israelbaez@gmail.co [Zoz GmbH, D-57482, Wenden (Germany)

    2011-07-01

    The ball milling (B M) of blended Ni and Cr elemental powders was carried out in a Simoloyer performing on high-energy scale mode at maximum production to obtain a nano structured Ni-20Cr alloy. The phase transformations and structural changes occurring during mechanical alloying were investigated by X-ray diffraction (XRD) and optical microscopy (Om). A gradual solid solubility of Cr and the subsequent formation of crystalline metastable solid solutions described in terms of the Avrami-Ero fe ev kinetics model were calculated. The XRD analysis of the structure indicates that cumulative lattice strain contributes to the driving force for solid solution between Ni and Cr during B M. Microstructure evolution has shown, additionally to the lamellar length refinement commonly observed, the folding of lamellae in the final processing stage. Om observations revealed that the lamellar spacing of Ni rich zones reaches a steady value near 500 nm and almost disappears after 30 h of milling. (Author)

  8. Effect of heat absorbing powder addition on cell morphology of porous titanium composite manufactured by reactive precursor method

    International Nuclear Information System (INIS)

    Kobashi, Makoto; Kamiya, Yoshinori; Kanetake, Naoyuki

    2012-01-01

    Open-cell structured porous titanium/ceramics composite was synthesized by a reactive precursor method using titanium and boron carbide (B 4 C) as reactant powders. Pore morphology was controlled by adding heat absorbing powder (titanium diboride: TiB 2 ) in the Ti+B 4 C blended powder. The effects of molar blending ratio of titanium and B 4 C and the amount of heat absorbing powder addition on the cell morphology (either open or closed) were investigated. Fine and homogeneous open-cell structure was achieved by adding appropriate amount of heat absorbing agent powder (>15 vol%), and the relative density of the specimen after the reaction became closer to that of the precursor by increasing TiB 2 volume fraction. When the volume fraction of TiB 2 addition was 20%, the open-cell fraction was maintained as 1.0 regardless of the relative density of the precursor.

  9. The crystallization of amorphous Fe2MnGe powder prepared by ball milling

    International Nuclear Information System (INIS)

    Zhang, L.; Brueck, E.; Tegus, O.; Buschow, K.H.J.; Boer, F.R. de

    2003-01-01

    We synthesized for the first time the intermetallic compound Fe 2 MnGe. To avoid preferential evaporation of volatile components we exploited mechanical alloying. Amorphous Fe 2 MnGe alloy powder was prepared by planetary ball milling elemental starting materials. The amorphous-to-crystalline transition was studied by means of differential scanning calorimetry (DSC) and X-ray diffraction (XRD). A cubic D0 3 phase is formed at low temperature and transforms to a high-temperature hexagonal D0 19 phase. The apparent activation energy was determined by means of the Kissinger method

  10. Fabrication of Al2O3–20 vol.% Al nanocomposite powders using high energy milling and their sinterability

    International Nuclear Information System (INIS)

    Zawrah, M.F.; Abdel-kader, H.; Elbaly, N.E.

    2012-01-01

    Highlights: ► Al 2 O 3 /Al nanocomposite powders were prepared via high energy ball milling. After 20 h milling, the size of Al 2 O 3 –20 vol.% Al nanocomposite particles was in the range of 23–29 nm. A uniform distribution of nanosized Al reinforcement throughout the Al 2 O 3 matrix, coating the particles was successfully obtained. ► There was no any sign of phase changes during the milling. A competition between the cold welding mechanism and the fracturing mechanism were found during milling and finally the above two mechanisms reached an equilibrium. ► The highest value of relative density was obtained for the sintered bodies at 1500 °C. ► The harness of the sintered composite was decreased while the fracture toughness was improved after addition Al into alumina. -- Abstract: In this study, alumina-based matrix nanocomposite powders reinforced with Al particles were fabricated and investigated. The sinterability of the prepared nanocomposite powder at different firing temperature was also conducted. Their mechanical properties in terms of hardness and toughness were tested. Alumina and aluminum powder mixtures were milled in a planetary ball mill for various times up to 30 h in order to produce Al 2 O 3 –20% Al nanocomposite. The phase composition, morphological and microstructural changes during mechanical milling of the nanocomposite particles were characterized by X-ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscope (SEM) techniques, respectively. The crystallite size and internal strain were evaluated by XRD patterns using Scherrer methods. A uniform distribution of the Al reinforcement in the Al 2 O 3 matrix was successfully obtained after milling the powders. The results revealed that there was no any sign of phase changes during the milling. The crystal size decreased with the prolongation of milling times, while the internal strain increased. A simple model is presented to illustrate the mechanical

  11. Adsorption of N-nitrosodimethylamine precursors by powdered and granular activated carbon.

    Science.gov (United States)

    Hanigan, David; Zhang, Jinwei; Herckes, Pierre; Krasner, Stuart W; Chen, Chao; Westerhoff, Paul

    2012-11-20

    Activated carbon (AC) has been shown to remove precursors of halogenated disinfection byproducts. Granular and powdered activated carbon (GAC, PAC) were investigated for their potential to adsorb N-nitrosodimethylamine (NDMA) precursors from blends of river water and effluent from a wastewater treatment plant (WWTP). At bench scale, waters were exposed to lignite or bituminous AC, either as PAC in bottle point experiments or as GAC in rapid small-scale column tests (RSSCTs). NDMA formation potential (FP) was used as a surrogate for precursor removal. NDMA FP was reduced by 37, 59, and 91% with 3, 8, and 75 mg/L of one PAC, respectively, with a 4-h contact time. In RSSCTs and in full-scale GAC contactors, NDMA FP removal always exceeded that of the bulk dissolved organic carbon (DOC) and UV absorbance at 254 nm. For example, whereas DOC breakthrough exceeded 90% of its influent concentration after 10,000 bed volumes of operation in an RSSCT, NDMA FP was less than 40% of influent concentration after the same bed life of the GAC. At full or pilot scale, high NDMA FP reduction ranging from >60 to >90% was achieved across GAC contactors, dependent upon the GAC bed life and/or use of a preoxidant (chlorine or ozone). In all experiments, NDMA formation was not reduced to zero, which suggests that although some precursors are strongly sorbed, others are not. This is among the first studies to show that AC is capable of adsorbing NDMA precursors, but further research is needed to better understand NDMA precursor chemical properties (e.g., hydrophobicity, molecular size) and evaluate how best to incorporate this finding into full-scale designs and practice.

  12. Consolidation of mechanically milled powder mixture of aluminum and quasicrystalline particle; Mechanical milling shita junkessho ryushi / aluminium gokin funmatsu no koka seikeisei

    Energy Technology Data Exchange (ETDEWEB)

    Yuasa, E.; Kawamura, C.; Sugiyama, T. [Musashi Institute of Technology, Tokyo (Japan)

    1998-10-15

    A quasi-crystalline Al65Cu20Fe15 powder prepared from alloy cast rapidly solidified by metal-mold casting, and then it was mixed to aluminum powder with various volume fractions by mechanical milling. The powder milled for above 50ks made homogeneous dispersion of quasi-crystalline phase with particle size less than 1{mu}m. The powder was hot-pressed under various conditions and then its features of consolidation were examined by the observation of microstructure and fracture strength in 3-point-bending of the compacts. When the milled powder was hot-pressed at higher compacting temperature than 673K for 3.6ks under pressure of 600MPa, the compact became to dense. Hardness of the obtained compact increases and its fracture strength decreases with increasing volume fraction of quasi-crystalline particles. Intermetallic compound Al7Cu2Fe forms in the interface of aluminum matrix and quasi-crystalline particle. 11 refs., 10 figs.

  13. The effect of intermediate stop and ball size in fabrication of recycled steel powder using ball milling from machining steel chips

    International Nuclear Information System (INIS)

    Fitri, M.W.M.; Shun, C.H.; Rizam, S.S.; Shamsul, J.B.

    2007-01-01

    A feasibility study for producing recycled steel powder from steel scrap by ball milling was carried out. Steel scrap from machining was used as a raw material and was milled using planetary ball milling. Three samples were prepared in order to study the effect of intermediate stop and ball size. Sample with intermediate stop during milling process showed finer particle size compared to the sample with continuous milling. Decrease in the temperature of the vial during the intermediate stop milling gives less ductile behaviour to the steel powder, which is then easily work-hardened and fragmented to fine powder. Mixed small and big size ball give the best production of recycled steel powder where it gives higher impact force to the scrap and accelerate the fragmentation of the steel scrap into powder. (author)

  14. Effects of milling method and calcination condition on phase and morphology characteristics of Mg4Nb2O9 powders

    International Nuclear Information System (INIS)

    Wongmaneerung, R.; Sarakonsri, T.; Yimnirun, R.; Ananta, S.

    2006-01-01

    Magnesium niobate, Mg 4 Nb 2 O 9 , powders has been synthesized by a solid-state reaction. Both conventional ball- and rapid vibro-milling have been investigated as milling methods, with the formation of the Mg 4 Nb 2 O 9 phase investigated as a function of calcination conditions by DTA and XRD. The particle size distribution of the calcined powders was determined by laser diffraction technique, while morphology, crystal structure and phase composition were determined via a combination of SEM, TEM and EDX techniques. The type of milling method together with the designed calcination condition was found to show a considerable effect on the phase and morphology evolution of the calcined Mg 4 Nb 2 O 9 powders. It is seen that optimization of calcination conditions can lead to a single-phase Mg 4 Nb 2 O 9 in both milling methods. However, the formation temperature and dwell time for single-phase Mg 4 Nb 2 O 9 powders were lower with the rapid vibro-milling technique

  15. Spark-plasma sintering and mechanical property of mechanically alloyed NiAl powder compact and ball-milled (Ni+Al) mixed powder compact

    International Nuclear Information System (INIS)

    Kim, J.S.; Jang, Y.I.; Kwon, Y.S.; Kim, Y.D.; Ahn, I.S.

    2001-01-01

    Mechanically-alloyed NiAl powder and (Ni+Al) powder mixture prepared by ball-milling were sintered by spark-plasma sintering (SPS) process. Densification behavior and mechanical property were determined from the experimental results and analysis such as changes in linear shrinkage, shrinkage rate, microstructure, and phase during sintering process, Vicker's hardness and transverse rupture strength tests. Densification mechanisms for MA-NiAl powder compact and (Ni+Al) powder mixture were different from each other. While the former showed a rapid increase in densification rate only at higher temperature region of 800-900 o C, the latter revealed firstly a rapid increase in densification rate even at low temperature of 300 o C and a subsequent increase up to 500 o C. Densities of both powder compact (MA and mixture) sintered at 1150 o C for 5 min were 98 and above 99 %, respectively. Sintered bodies were composed mainly of NiAl phase with Ni 3 Al as secondary phase for both powders. Sintered body of MA-NiAl powder showed a very fine grain structure. Crystallite size determined by XRD result and the Sherrer's equation was approximately 80 nm. Vicker's hardness for the sintered bodies of (Ni+Al) powder mixture and MA-NiAl powder were 410±12 H v and 555±10 H v , respectively, whereas TRS values 1097±48 MPa and 1393±75 MPa. (author)

  16. Preparation of zinc ferrite nano powders by high energy wet-milling method and investigation of Crystallites size variation during this process

    International Nuclear Information System (INIS)

    Masoudi, H.; Aftabi, A.; Mozafari, M.; Amighian, J.

    2007-01-01

    In this research work ZnFe 2 O 4 nano powders were prepared by high-energy wet-milling process, using metallic Fe and Zn powders. The process was investigated by XRD technique. 10% of the zinc ferrite was formed after 10 h milling. The as-milled sample was annealed at 500, 550 and 600 d egree C . Ultimately a single sample was obtained at 600 d egree C . Using sherrer's formula, the mean crystallite size of the as-milled and annealed powders were calculated. These were in the range of 17.9 to 20.4 nm.

  17. Spark Plasma Co-Sintering of Mechanically Milled Tool Steel and High Speed Steel Powders.

    Science.gov (United States)

    Pellizzari, Massimo; Fedrizzi, Anna; Zadra, Mario

    2016-06-16

    Hot work tool steel (AISI H13) and high speed steel (AISI M3:2) powders were successfully co-sintered to produce hybrid tool steels that have properties and microstructures that can be modulated for specific applications. To promote co-sintering, which is made difficult by the various densification kinetics of the two steels, the particle sizes and structures were refined by mechanical milling (MM). Near full density samples (>99.5%) showing very fine and homogeneous microstructure were obtained using spark plasma sintering (SPS). The density of the blends (20, 40, 60, 80 wt % H13) was in agreement with the linear rule of mixtures. Their hardness showed a positive deviation, which could be ascribed to the strengthening effect of the secondary particles altering the stress distribution during indentation. A toughening of the M3:2-rich blends could be explained in view of the crack deviation and crack arrest exerted by the H13 particles.

  18. Effect of the Milling Time of the Precursors on the Physical Properties of Sprayed Aluminum-Doped Zinc Oxide (ZnO:Al Thin Films

    Directory of Open Access Journals (Sweden)

    María De La Luz Olvera

    2012-08-01

    Full Text Available Aluminum doped zinc oxide (ZnO:Al thin films were deposited on soda-lime glass substrates by the chemical spray technique. The atomization of the solution was carried out by ultrasonic excitation. Six different starting solutions from both unmilled and milled Zn and Al precursors, dissolved in a mix of methanol and acetic acid, were prepared. The milling process was carried out using a planetary ball mill at a speed of 300 rpm, and different milling times, namely, 15, 25, 35, 45, and 60 min. Molar concentration, [Al]/[Zn] atomic ratio, deposition temperature and time, were kept at constant values; 0.2 M, 3 at.%, 475 °C, and 10 min, respectively. Results show that, under the same deposition conditions, electrical resistivities of ZnO:Al thin films deposited from milled precursors are lower than those obtained for films deposited from unmilled precursors. X-ray diffraction analysis revealed that all films display a polycrystalline structure, fitting well with the hexagonal wurtzite structure. Changes in surface morphology were observed by scanning electron microscopy (SEM as well, since films deposited from unmilled precursors show triangular shaped grains, in contrast to films deposited from 15 and 35 min milled precursors that display thin slices with hexagonal shapes. The use of milled precursors to prepare starting solutions for depositing ZnO:Al thin films by ultrasonic pyrolysis influences their physical properties.

  19. Influence of Process Control Agent on Characterization and Structure of Micron Chitosan Powders Prepared by Ball Milling Method

    Directory of Open Access Journals (Sweden)

    ZHANG Chuan-jie

    2016-12-01

    Full Text Available With ethyl alcohol or distilled water as process control agent (PCA, micron chitosan powder was prepared by ball milling method. The yield rate, particle size distribution, micro morphology, viscosity average molecular mass, chemical and crystal structures, and thermal properties of these different micron chitosan powders were measured. The results indicate that the yield rate of micron chitosan powders prepared with ethyl alcohol as PCA increases significantly, and improves to 94.7% from 25% while the amount of ethyl alcohol is 0.75mL/g. The particle size distribution of micron chitosan powder prepared with ethyl alcohol as PCA is concentrated, while the D50 and D90 in size are 824nm and 1629nm respectively. Chitosan do not react with ethyl alcohol used as PCA, but the viscosity average molecular mass of prepared micron chitosan powder decreases by 23%, the crystal structures are destroyed slightly, and its thermal stability is slightly weakened.

  20. Microstructural Evolution, Thermodynamics, and Kinetics of Mo-Tm2O3 Powder Mixtures during Ball Milling

    Directory of Open Access Journals (Sweden)

    Yong Luo

    2016-10-01

    Full Text Available The microstructural evolution, thermodynamics, and kinetics of Mo (21 wt % Tm2O3 powder mixtures during ball milling were investigated using X-ray diffraction and transmission electron microscopy. Ball milling induced Tm2O3 to be decomposed and then dissolved into Mo crystal. After 96 h of ball milling, Tm2O3 was dissolved completely and the supersaturated nanocrystalline solid solution of Mo (Tm, O was obtained. The Mo lattice parameter increased with increasing ball-milling time, opposite for the Mo grain size. The size and lattice parameter of Mo grains was about 8 nm and 0.31564 nm after 96 h of ball milling, respectively. Ball milling induced the elements of Mo, Tm, and O to be distributed uniformly in the ball-milled particles. Based on the semi-experimental theory of Miedema, a thermodynamic model was developed to calculate the driving force of phase evolution. There was no chemical driving force to form a crystal solid solution of Tm atoms in Mo crystal or an amorphous phase because the Gibbs free energy for both processes was higher than zero. For Mo (21 wt % Tm2O3, it was mechanical work, not the negative heat of mixing, which provided the driving force to form a supersaturated nanocrystalline Mo (Tm, O solid solution.

  1. Production of dispersed nanometer sized YAG powders from alkoxide, nitrate and chloride precursors and spark plasma sintering to transparency

    International Nuclear Information System (INIS)

    Suarez, M.; Fernandez, A.; Menendez, J.L.; Torrecillas, R.

    2010-01-01

    Yttrium aluminum garnet (YAG) was synthesized from different starting materials, i.e., alkoxide, nitrate and chloride precursors. The conversion steps from the precursors to crystalline YAG were studied by Raman spectroscopy. Dispersed YAG powders were formed at a relatively low temperature, around 800 o C by the chlorides route, whereas alkoxide precursors needed firing over 900 o C and nitrates even over 1100 o C. Lyophilized YAG gel was sintered to transparency by the spark plasma sintering method at 1500 o C with in-line transmittances close to 60% at 680 nm and over 80% in the infrared range.

  2. Gas atomized precursor alloy powder for oxide dispersion strengthened ferritic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Rieken, Joel [Iowa State Univ., Ames, IA (United States)

    2011-12-13

    Gas atomization reaction synthesis (GARS) was employed as a simplified method for producing precursor powders for oxide dispersion strengthened (ODS) ferritic stainless steels (e.g., Fe-Cr-Y-(Ti,Hf)-O), departing from the conventional mechanical alloying (MA) process. During GARS processing a reactive atomization gas (i.e., Ar-O2) was used to oxidize the powder surfaces during primary break-up and rapid solidification of the molten alloy. This resulted in envelopment of the powders by an ultra-thin (t < 150 nm) metastable Cr-enriched oxide layer that was used as a vehicle for solid-state transport of O into the consolidated microstructure. In an attempt to better understand the kinetics of this GARS reaction, theoretical cooling curves for the atomized droplets were calculated and used to establish an oxidation model for this process. Subsequent elevated temperature heat treatments, which were derived from Rhines pack measurements using an internal oxidation model, were used to promote thermodynamically driven O exchange reactions between trapped films of the initial Cr-enriched surface oxide and internal Y-enriched intermetallic precipitates. This novel microstructural evolution process resulted in the successful formation of nano-metric Y-enriched dispersoids, as confirmed using high energy X-ray diffraction and transmission electron microscopy (TEM), equivalent to conventional ODS alloys from MA powders. The thermal stability of these Y-enriched dispersoids was evaluated using high temperature (1200°C) annealing treatments ranging from 2.5 to 1,000 hrs of exposure. In a further departure from current ODS practice, replacing Ti with additions of Hf appeared to improve the Y-enriched dispersoid thermal stability by means of crystal structure modification. Additionally, the spatial distribution of the dispersoids was found to depend strongly on the original rapidly solidified microstructure. To exploit this, ODS microstructures were engineered from

  3. Powder of a copper oxide superconductor precursor, fabrication process and use for the preparation of superconducting oxide

    International Nuclear Information System (INIS)

    Dehaudt, P.

    1990-01-01

    The precursor powder comprises at least a copper compound (hydroxide, oxide and hydroxynitrates), at least a rare earth and/or yttrium compound (nitrates, hydroxides and hydroxynitrates) or bismuth oxide and at least an alkaline earth nitrate. It can be prepared by atomization drying of a suspension a copper precipitate or coprecipitate and other elements of the superconducting oxide in solution [fr

  4. Effects of surfactant addition and high-speed ball milling on magnetic powders based on Pr-Fe-B obtained by HDDR

    International Nuclear Information System (INIS)

    Santos, Patricia Brissi

    2011-01-01

    This work verified the effect caused by adding the surfactant in the high speed/energy milling in order to obtain Pr 12 Fe 65.9 Co 16 B 6 Nb 0.1 magnetic nano powders. The first part of this work involved the magnetic powder obtainment through the process of hydrogenation, disproportionation, desorption and recombination (HDDR). The pressure of H2 during the hydrogenation and disproportion steps was 930 mbar and the temperature of desorption and recombination was 840 deg C. Initially, the HDDR powders were subjected a high speed milling process at 900 rpm, with quantity variations of the milling medium (cyclohexane) and without the addition of oleic acid. Then, the HDDR powders were subjected to the milling process with the addition of oleic acid and with milling time variations. After the milling process, heat treatments of the powder were carried out at 700 deg C or 800 deg C for 30 minutes in order to obtain the crystallization of the powder. By performing the procedures, it was verified that the milling efficiency improved with the addition of 6.6 ml of cyclohexane as the milling medium and with the addition of oleic acid. It was determined that for the surfactant additions of 0.02 ml to 0.05 ml, with a milling time of up to 360 minutes, powder agglomeration does not occur in the milling pot and the milling efficiency is higher than 90%. The second stage of this work involved the magnetic powder's characterization obtained by using vibrating sample magnetometer, scanning electron microscopy, transmission electron microscopy and X-ray diffraction. Through the characterizations it was found that the powder's magnetic properties improved when the addition of oleic acid in a high-speed /energy milling occurred. It was also verified that the α-Fe phase, present in the powder, shows a crystallite size decrease (from 35 nm to ∼ 10 nm) when the time milling variation occurred; meanwhile, the crystallinity degree was lower in the Pr 2 Fe 14 B phase when the time

  5. The influence of the long time milling on the structure and magnetic properties of the Fe-Cu-Nb-Si-B powder

    International Nuclear Information System (INIS)

    Fechova, E.; Kollar, P.; Fuezer, J.; Kovac, J.; Petrovic, P.; Kavecansky, V.

    2004-01-01

    We have studied the influence of milling on the structure and magnetic properties of Fe 73.5 Cu 1 Nb 3 Si 13.5 B 9 powder prepared in a vibratory micro-mill as a function of long milling time. Three powder samples have been prepared and investigated (the first one was prepared by the milling of amorphous ribbon, the second one by milling of the same ribbon in a partially nanocrystallized state and the third one by milling of pure elements). Structural analysis shows the decrease of the grain size with the increasing time of milling. The coercivity of the samples prepared from pure elements increases almost linearly up to 1700 h of milling while further milling leads to the saturation at 25 kA/m (at the milling time of 3500 h). The coercivity of the samples milled from ribbons increases to its maximum of 8 kA/m for the milling time of 800 h and then decreases

  6. Spark Plasma Co-Sintering of Mechanically Milled Tool Steel and High Speed Steel Powders

    Directory of Open Access Journals (Sweden)

    Massimo Pellizzari

    2016-06-01

    Full Text Available Hot work tool steel (AISI H13 and high speed steel (AISI M3:2 powders were successfully co-sintered to produce hybrid tool steels that have properties and microstructures that can be modulated for specific applications. To promote co-sintering, which is made difficult by the various densification kinetics of the two steels, the particle sizes and structures were refined by mechanical milling (MM. Near full density samples (>99.5% showing very fine and homogeneous microstructure were obtained using spark plasma sintering (SPS. The density of the blends (20, 40, 60, 80 wt % H13 was in agreement with the linear rule of mixtures. Their hardness showed a positive deviation, which could be ascribed to the strengthening effect of the secondary particles altering the stress distribution during indentation. A toughening of the M3:2-rich blends could be explained in view of the crack deviation and crack arrest exerted by the H13 particles.

  7. Structural and morphological characterization of TiO2-ZrO2 powders obtained by the polymeric precursors method

    International Nuclear Information System (INIS)

    Ribeiro, M.A.; Gama, L.; Bispo, A.; Neiva, L.S.; Bernardi, M.I.B.; Kiminami, R.H.G.A.

    2010-01-01

    This work aims to characterize the structure and morphology of TiO 2 -ZrO 2 powders obtained by polymeric precursor method. For this we studied the following compositions: 0.25, 0.5 and 0.75 moles of Zr and calcined at 800 deg C for one hour. The powders obtained were characterized by XRD, SEM and nitrogen adsorption (BET). The analysis of X-ray diffraction showed that the powders had a phase of TiO 2 in the anatase form and a tetragonal phase of ZrO 2 . The crystallite size was between 8, 13 and 11 nm respectively. The analysis of scanning electron microscopy showed the growth of ZrO 2 nanoparticles and that these comprise spherical agglomerates of less than 100 nm. Particle size determined by the BET ranging 28.1-29.5 nm, showing thereby the character of nanosized powders. (author)

  8. Tungsten oxide coatings deposited by plasma spray using powder and solution precursor for detection of nitrogen dioxide gas

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Chao, E-mail: zhangc@yzu.edu.cn [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); Wang, Jie [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); Geng, Xin [College of Mechanical Engineering, Yangzhou University, Yangzhou 225127 (China); College of Chemistry and Chemical Engineering, Yangzhou University, Yangzhou 225002 (China)

    2016-05-25

    Increasing attention has been paid on preparation methods for resistive-type gas sensors based on semiconductor metal oxides. In this work, tungsten oxide (WO{sub 3}) coatings were prepared on alumina substrates and used as gas sensitive layers. The coatings were deposited by atmospheric plasma spray using powder, solution precursor, or a combination of both. Tungsten oxide powder through a powder port and ammonium tungstate aqueous solution through a liquid port were injected into plasma stream respectively or together to deposit WO{sub 3} coatings. Phase structures in the coatings were characterized by X-ray diffraction analyzer. The field-emission scanning electron microscopy images confirmed that the coatings were in microstructure, nanostructure or micro-nanostructure. The sensing properties of the sensors based on the coatings exposed to 1 ppm nitrogen dioxide gas were characterized in a home-made instrument. Sensing properties of the coatings were compared and discussed. The influences of gas humidity and working temperature on the sensor responses were further studied. - Highlights: • Porous gas sensitive coatings were deposited by plasma spray using powder and solution precursor. • Crystallized WO{sub 3} were obtained through hybrid plasma spray plus a pre-conditioned step. • Plasma power had an important influence on coating microstructure. • The particle size of atmospheric plasma-sprayed microstructured coating was stable. • Solution precursor plasma-sprayed WO{sub 3} coatings had nanostructure and showed good responses to 1 ppm NO{sub 2}.

  9. Effect of high energy milling time of the aluminum bronze alloy obtained by powder metallurgy with niobium carbide addition

    Energy Technology Data Exchange (ETDEWEB)

    Dias, Alexandre Nogueira Ottoboni; Silva, Aline da; Rodrigues, Carlos Alberto; Melo, Mirian de Lourdes Noronha Motta; Rodrigues, Geovani; Silva, Gilbert, E-mail: aottoboni@yahoo.com.br [Universidade Federal de Itajuba (UNIFEI), Itajuba, MG (Brazil)

    2017-05-15

    The aluminum bronze alloy is part of a class of highly reliable materials due to high mechanical strength and corrosion resistance being used in the aerospace and shipbuilding industry. It's machined to produce parts and after its use cycle, it's discarded, but third process is considered expensive and besides not being correct for environment reasons. Thus, reusing this material through the powder metallurgy (PM) route is considered advantageous. The aluminum bronze chips were submitted to high energy ball milling process with 3% of niobium carbide (NbC) addition. The NbC is a metal-ceramic composite with a ductile-brittle behaviour. It was analyzed the morphology of powders by scanning electron microscopy as well as particle size it was determined. X ray diffraction identified the phases and the influence of milling time in the diffractogram patterns. Results indicates that milling time and NbC addition improves the milling efficiency significantly and being possible to obtain nanoparticles. (author)

  10. Nano-composite powders Ag-SnO2 prepared by reactive milling sintering and microstructural evolution

    International Nuclear Information System (INIS)

    Lorrain, Nathalie

    2000-01-01

    This work aims at controlling the synthesis and the sintering of nano-composite powders Ag-SnO 2 in order to obtain a dense and nano-structured material for electrical contact as a substitute of the toxic compound Ag - CdO. The powder is prepared by reactive milling from silver oxide (Ag 2 O) and silver bronze (Ag 3 Sn) powders. This process leads to a fine dispersion of silver and tin oxide nanometer sized particles. We first studied the mechanisms of reaction promoted by milling in vacuum and in air. A two-stage oxidation of tin in Ag 3 Sn occurs: during forced contact with Ag 2 O, tin oxidises in SnO, then in SnO 2 . In air, gaseous oxygen also participates to the oxidation of tin in SnO 2 but the reaction is slower because of the formation of silver carbonates from a reaction of Ag 2 O with CO 2 .Then the sintering behaviour of the nano-composite powder as a function of the compacting pressure and of the heating rate has been studied. We show: (i) a diffusion of pure silver towards porosity and free surfaces (exo-diffusion) which destroys the nano-structure and (ii) a severe de-densification. We show that the origin of these phenomena is due to carbonates on to the Ag 2 O starting powder, which are incorporated, in the milled Ag-SnO 2 powder in course of milling; during sintering, decomposition gases generate internal stresses. Low stresses lead to a diffusional creep with exo-diffusion whereas high stresses induce an intensive de-densification by local plastic deformation but no exo-diffusion. A modelling shows that exo-diffusion is limited by heating very quickly a strongly compacted powder that contains a high quantity of carbonates. The experimental results confirm the predictions of the model. Finally, we propose solutions allowing a full densification and a process for decreasing the tin oxide concentration. (author) [fr

  11. Electrochemical properties of the ball-milled LaMg10NiMn alloy with Ni powders

    International Nuclear Information System (INIS)

    Wang Yi; Wang Xin; Gao Xueping; Shen Panwen

    2008-01-01

    The electrochemical characteristics of the ball-milled LaMg 10 NiMn alloys with Ni powders were investigated. It was found that the ball-milled LaMg 10 NiMn + 150 wt.% Ni composite exhibited higher first discharge capacity and better cycle performance. By means of the analysis of electrochemical impedance spectra (EIS), it was shown that the existence of manganese in LaMg 10 NiMn alloy increased the electrocatalytic activity due to its catalytic effect, and destabilized metal hydrides, and so reduced the hydrogen diffusion resistance. These contributed to the higher discharge capacity of the ball-milled LaMg 10 NiMn-Ni composite. According to the analytical results of X-ray diffraction (XRD), EIS and steady-state polarization (SSP) experiments, the inhibition of metal corrosion is not the main reason for the better cycle performance. The main reason is that the electrochemical reaction resistance of the ball-milled LaMg 10 NiMn-Ni composite is always lower than that of the ball-milled LaMg 10 Ni 2 -Ni composite because the former one contains manganese, which is a catalyst for the electrode reaction

  12. The Powdering Process with a Set of Ceramic Mills for Green Tea Promoted Catechin Extraction and the ROS Inhibition Effect

    Directory of Open Access Journals (Sweden)

    Kouki Fujioka

    2016-04-01

    Full Text Available For serving green tea, there are two prominent methods: steeping the leaf or the powdered leaf (matcha style in hot water. The purpose of the present study was to reveal chemical and functional differences before and after the powdering process of green tea leaf, since powdered green tea may contribute to expanding the functionality because of the different ingesting style. In this study, we revealed that the powdering process with a ceramic mill and stirring in hot water increased the average extracted concentration of epigallocatechin gallate (EGCG by more than three times compared with that in leaf tea using high-performance liquid chromatography (HPLC and liquid chromatography–tandem mass Spectrometry (LC-MS/MS analyses. Moreover, powdered green tea has a higher inhibition effect of reactive oxygen species (ROS production in vitro compared with the same amount of leaf tea. Our data suggest that powdered green tea might have a different function from leaf tea due to the higher catechin contents and particles.

  13. Polarization-dependent NEXAFS study of adsorption of long-chain surfactants on mechanically milled iron powder

    Energy Technology Data Exchange (ETDEWEB)

    Syugaev, A.V., E-mail: syual@mail.ru; Maratkanova, A.N.

    2014-08-15

    Highlights: • Plate-like particles modified with surfactant molecules were obtained under high-energy ball milling. • Adsorption layers were studied with polarization-dependent NEXAFS spectroscopy. • For the first time, arrangement of surfactants molecules on the powdered metal surface has been determined. • Tails of surfactant molecules (C-F/C-H) are shown to be oriented perpendicular to the particle surface. • Arrangement of carboxylate groups on the particle surfaces is discussed. - Abstract: In this work we have demonstrated the possibility of using the polarization-dependent NEXAFS spectra to study the structure of organic layers at the surface of powdered materials with plate-like shaped particles. The polarization dependence of the NEXAFS spectra may be easily obtained by just changing the angle between the X-ray beam direction and the substrate onto which the powder particles are set. For the first time, we have carried out a detailed study of the surfactant layers (n-perfluorononanoic and stearic acid), which are formed at the surface of iron plate-like particles under mechanical milling of iron powder with an addition of corresponding surfactants. The surfactant molecules are predominantly oriented perpendicular to the surface of the mechanically milled particles. Such orientation is similar to the arrangement of the molecules in the layers formed under equilibrium conditions, e.g. deposition from solutions. The changes in the chemical environment occurring in the molecule tails (defluorination or dehydrogenation) under mechanochemical treatment, do not result in a significant change in the molecular orientation and disordering of the adsorbed layer.

  14. High-Yield Preparation and Electrochemical Properties of Few-Layer MoS2 Nanosheets by Exfoliating Natural Molybdenite Powders Directly via a Coupled Ultrasonication-Milling Process

    Science.gov (United States)

    Dong, Huina; Chen, Deliang; Wang, Kai; Zhang, Rui

    2016-09-01

    Cost-effective and scalable preparation of two-dimensional (2D) molybdenum disulfide (MoS2) has been the bottleneck that limits their applications. This paper reports a novel coupled ultrasonication-milling (CUM) process to exfoliate natural molybdenite powders to achieve few-layer MoS2 (FL-MoS2) nanosheets in the solvent of N-methyl-2-pyrrolidone (NMP) with polyvinylpyrrolidone (PVP) molecules. The synergistic effect of ultrasonication and sand milling highly enhanced the exfoliation efficiency, and the precursor of natural molybdenite powders minimizes the synthetic cost of FL-MoS2 nanosheets. The exfoliation of natural molybdenite powders was conducted in a home-made CUM system, mainly consisting of an ultrasonic cell disruptor and a ceramic sand mill. The samples were characterized by X-ray diffraction, UV-vis spectra, Raman spectra, FT-IR, SEM, TEM, AFM, and N2 adsorption-desorption. The factors that influence the exfoliation in the CUM process, including the initial concentration of natural molybdenite powders ( C in, 15-55 g L-1), ultrasonic power ( P u, 200-350 W), rotation speed of sand mill ( ω s, 1500-2250 r.p.m), exfoliation time ( t ex, 0.5-6 h), and the molar ratio of PVP unit to MoS2 ( R pm, 0-1), were systematically investigated. Under the optimal CUM conditions (i.e., C in = 45 g L-1, P u = 280 W, ω s = 2250 r.p.m and R pm = 0.5), the yield at t ex = 6 h reaches 21.6 %, and the corresponding exfoliation rate is as high as 1.42 g L-1 h-1. The exfoliation efficiency of the CUM mode is much higher than that of either the ultrasonication (U) mode or the milling (M) mode. The synergistic mechanism and influencing rules of the CUM process in exfoliating natural molybdenite powders were elaborated. The as-obtained FL-MoS2 nanosheets have a high specific surface area of 924 m2 g-1 and show highly enhanced electrocatalytic performance in hydrogen evolution reaction and good electrochemical sensing property in detecting ascorbic acid. The CUM process

  15. Characterisation of Mn0.63Zn0.37Fe2O4 powders after intensive milling and subsequent thermal treatment

    Directory of Open Access Journals (Sweden)

    Labus Nebojša

    2017-01-01

    Full Text Available Commercial Mn-Zn powder (Mn0.63Zn0.37Fe2O4, 93 wt. % and Fe2O3 7 wt. % was milled 0.5, 1, 2 and 4 hours in a planetary ball mill. The goal was to observe intensive milling influences on oxidation and reduction processes that will happen during subsequent heating. Powders were characterized with XRD, SEM and particle seizer. Subsequent heating was monitored on TGA/DTA in an air atmosphere. After compaction of the milled powders, sintering was also performed in a dilatometric device. Sintered specimens were characterized micro structurally with SEM on a fresh breakage. Obtained differential TGA diagrams suggest intensive changes during prolonged milling of the oxidation kinetics on heating. Ferrite powders changed with milling as well as with second run heating were characterized to enable determination of the potentially best ratio of milling and heating to be applied to obtain the desired microstructure. [Project of the Serbian Ministry of Education, Science and Technological Development, Grant no. OI172057 and Grant no. III45014

  16. Swelling of radiation-cured polymer precursor powder for silicon carbide by pyrolysis

    Directory of Open Access Journals (Sweden)

    Akinori Takeyama

    2015-12-01

    Full Text Available Ceramic yield, density, volume change and pore size distribution were measured for radiation- and thermally cured PCS powder when they were pyrolyzed in the temperature range of 673–973 K. Higher ceramic yield was obtained for radiation-cured powder due to smaller amount of evolved gas. Temperature dependence of volume change and the total pore volume show that the formation and disappearance of pores in the powders were determined by the volume shrinkage and evolution of decomposed gases. Volume shrinkage narrowed the pore size distribution for radiation-cured powder. For thermally cured powder, the narrowing of size distribution was disturbed by aggregated pores. Smaller amount of evolved gas from radiation-cured powder relative to thermally cured powder prevented the aggregation of pores and provided the narrow size distribution.

  17. Colloidal Precursors from 'Ball-Milling in Liquid Medium' Process for CuInSe{sub 2} Thin Film

    Energy Technology Data Exchange (ETDEWEB)

    Chung, Jae Hoon; Kim, Seung Joo [Ajou University, Suwon (Korea, Republic of)

    2010-09-15

    CIS thin film can be fabricated by using the precursor obtained through ball-milling the elemental reagents in liquid media. The amorphous colloidal precursor with good dispersity was prepared in the medium that contains strong base and polar solvent (2 M ethylenediamine in DMF solution as used in this study). The 'ball-milling in liquid medium' method requires only elemental sources as starting materials and a proper solution so that it can be employed without additional processes for separation and purification. As a simple and less-toxic preparative route, this method would be practically available to prepare CIS-related solar cells. CuInSe{sub 2} (CIS) and related chalcopyrite compounds are very promising materials for thin film solar cells due to their favorable band gap, high optical absorption coefficient and long-term stability. CIS-based solar cells have shown the highest conversion efficiency reaching a value of 20%. However, the vacuum-based processes that are used to fabricate CIS thin-films have some drawbacks such as the complexity in process, high production cost and difficulty in scaling up. Recently, several research groups have proposed different non-vacuum deposition processes for CIS solar cell. For example, H. W. Hillhouse et al. prepared the CIS absorber layer by using 'nanocrystal ink method' in which a colloidal nanocrystal ink was obtained from reaction of CuCl, InCl{sub 3} and Se in oleylamine. D. B. Mitzi et al. used a solution-based precursor that was prepared by dissolution of Cu{sub 2}Se, In{sub 2}Se{sub 3}, Ga{sub 2}Se{sub 3} and Se in hydrazine to fabricate the Ga-containing absorber layer, Cu(In,Ga)Se{sub 2}.

  18. In situ Fabrication of Fe-TiB{sub 2} Nanocomposite Powder by Planetary Ball Milling and Subsequent Heat-treatment of FeB and TiH{sub 2} Powder Mixture

    Energy Technology Data Exchange (ETDEWEB)

    Huynh, Xuan-Khoa [Hanoi Uneversity of Science and Technology, Hanoi (Viet Nam); Bae, Sun-Woo; Kim, Ji Soon [University of Ulsan, Ulsan (Korea, Republic of)

    2017-01-15

    Fe-TiB{sub 2} powder was synthesized in-situ by the planetary ball milling and subsequent heat-treatment of an iron boride (FeB) and titanium hydride (TiH{sub 2}) powder mixture. Mechanical activation of the (FeB+TiH{sub 2}) powder mixtures was observed after a milling time of 3 hours at 700 rpm of rotation speed, but activation was not the same after 1 hour milling time. The particle size of the (FeB+ TiH{sub 2}) powder mixture was reduced to the nanometer scale, and each constituent was homogeneously distributed. A sharp exothermic peak was observed at a lower temperature (749 ℃) on the DSC curves for the (FeB+TiH{sub 2}) powder mixture milled for 3 hours, compared to the one milled for 1 hour (774 ℃). These peaks were confirmed to have resulted from the formation reaction of the TiB{sub 2} phase, from Ti and B elements in the FeB. The Fe-TiB{sub 2} composite powder fabricated in situ exhibited only two phases of Fe and TiB{sub 2} with homogeneous distribution. The size of the TiB{sub 2} particulates in the Fe matrix was less than 5 nm.

  19. Superfine powdered activated carbon (S-PAC) coatings on microfiltration membranes: Effects of milling time on contaminant removal and flux.

    Science.gov (United States)

    Amaral, Pauline; Partlan, Erin; Li, Mengfei; Lapolli, Flavio; Mefford, O Thompson; Karanfil, Tanju; Ladner, David A

    2016-09-01

    In microfiltration processes for drinking water treatment, one method of removing trace contaminants is to add powdered activated carbon (PAC). Recently, a version of PAC called superfine PAC (S-PAC) has been under development. S-PAC has a smaller particle size and thus faster adsorption kinetics than conventionally sized PAC. Membrane coating performance of various S-PAC samples was evaluated by measuring adsorption of atrazine, a model micropollutant. S-PACs were created in-house from PACs of three different materials: coal, wood, and coconut shell. Milling time was varied to produce S-PACs pulverized with different amounts of energy. These had different particles sizes, but other properties (e.g. oxygen content), also differed. In pure water the coal based S-PACs showed superior atrazine adsorption; all milled carbons had over 90% removal while the PAC had only 45% removal. With addition of calcium and/or NOM, removal rates decreased, but milled carbons still removed more atrazine than PAC. Oxygen content and specific external surface area (both of which increased with longer milling times) were the most significant predictors of atrazine removal. S-PAC coatings resulted in loss of filtration flux compared to an uncoated membrane and smaller particles caused more flux decline than larger particles; however, the data suggest that NOM fouling is still more of a concern than S-PAC fouling. The addition of calcium improved the flux, especially for the longer-milled carbons. Overall the data show that when milling S-PAC with different levels of energy there is a tradeoff: smaller particles adsorb contaminants better, but cause greater flux decline. Fortunately, an acceptable balance may be possible; for example, in these experiments the coal-based S-PAC after 30 min of milling achieved a fairly high atrazine removal (overall 80%) with a fairly low flux reduction (under 30%) even in the presence of NOM. This suggests that relatively short duration (low energy

  20. Simultaneous removal of ammonia and N-nitrosamine precursors from high ammonia water by zeolite and powdered activated carbon.

    Science.gov (United States)

    Xue, Runmiao; Donovan, Ariel; Zhang, Haiting; Ma, Yinfa; Adams, Craig; Yang, John; Hua, Bin; Inniss, Enos; Eichholz, Todd; Shi, Honglan

    2018-02-01

    When adding sufficient chlorine to achieve breakpoint chlorination to source water containing high concentration of ammonia during drinking water treatment, high concentrations of disinfection by-products (DBPs) may form. If N-nitrosamine precursors are present, highly toxic N-nitrosamines, primarily N-nitrosodimethylamine (NDMA), may also form. Removing their precursors before disinfection should be a more effective way to minimize these DBPs formation. In this study, zeolites and activated carbon were examined for ammonia and N-nitrosamine precursor removal when incorporated into drinking water treatment processes. The test results indicate that Mordenite zeolite can remove ammonia and five of seven N-nitrosamine precursors efficiently by single step adsorption test. The practical applicability was evaluated by simulation of typical drinking water treatment processes using six-gang stirring system. The Mordenite zeolite was applied at the steps of lime softening, alum coagulation, and alum coagulation with powdered activated carbon (PAC) sorption. While the lime softening process resulted in poor zeolite performance, alum coagulation did not impact ammonia and N-nitrosamine precursor removal. During alum coagulation, more than 67% ammonia and 70%-100% N-nitrosamine precursors were removed by Mordenite zeolite (except 3-(dimethylaminomethyl)indole (DMAI) and 4-dimethylaminoantipyrine (DMAP)). PAC effectively removed DMAI and DMAP when added during alum coagulation. A combination of the zeolite and PAC selected efficiently removed ammonia and all tested seven N-nitrosamine precursors (dimethylamine (DMA), ethylmethylamine (EMA), diethylamine (DEA), dipropylamine (DPA), trimethylamine (TMA), DMAP, and DMAI) during the alum coagulation process. Copyright © 2017. Published by Elsevier B.V.

  1. Effect of milling duration on the evolution of shape memory properties in a powder processed Cu-Al-Ni-Ti alloy

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, Mohit; Gupta, Gaurav K.; Shafeeq, Muhamed M.; Modi, Om P.; Prasad, Braj K. [CSIR - Advanced Materials and Processes Research Institute, Bhopal (India)

    2013-09-15

    The present work describes the effect of milling duration on the properties of a powder metallurgy processed Cu-Al-Ni-Ti shape memory alloy employing mechanical alloying. Powder mixtures milled for different durations were sintered in order to investigate the formation of solid solution and evolution of martensitic structure. The idea was to optimize the duration of milling (mechanical alloying) to obtain chemical homogeneity as well as shape memory properties in the processed material without undergoing extensive post homogenization treatment. The martensitic structure was noted to evolve in the powder mix milled for at least 16 hrs, whereas complete transformation to martensite occurred after milling for 40 hrs. Interestingly, the dissolution of alloying elements (to form the {beta} phase prior to the formation of martensite) was noted to complete partially only during mechanical alloying for 40 hrs and remaining during subsequent sintering for 1 hr. The hot pressed compacts of the powders milled for 40 hrs were chemically homogeneous and consisted of fully martensite phase, which is essential for the realization of shape memory properties. They also revealed almost 100% shape recovery at the applied pre-strain levels of 1 and 2%. (orig.)

  2. Milling condition effects on the Nd15 Fe77 B8 powder magnetic properties

    International Nuclear Information System (INIS)

    Landgraf, Fernando J.G.; Missell, Frank P.

    1992-01-01

    As a result of the first part of a study of the development of permanent magnets, an investigation of the effect of milling on the magnetic properties of the alloy Nd 15 Fe 77 B 8 showed differences in efficiency between ball milling and vibration milling, as well as a dependence of the intrinsic coercive field on particle size. The maximum value of the coercive field was obtained for a particle size of 1.7 μm in samples compacted without magnetic orientation. (author)

  3. Removal of fluoride from drinking water using modified ultrafine tea powder processed using a ball-mill

    Energy Technology Data Exchange (ETDEWEB)

    Cai, Huimei; Xu, Lingyun; Chen, Guijie; Peng, Chuanyi [School of Tea & Food Science and Technology, Anhui Agricultural University/State Key Laboratory of Tea Plant Biology and Utilization, Anhui Agricultural University, Hefei 230036, Anhui (China); Ke, Fei [School of Tea & Food Science and Technology, Anhui Agricultural University/State Key Laboratory of Tea Plant Biology and Utilization, Anhui Agricultural University, Hefei 230036, Anhui (China); School of Science, Anhui Agricultural University, Hefei 230036 (China); Liu, Zhengquan; Li, Daxiang; Zhang, Zhengzhu [School of Tea & Food Science and Technology, Anhui Agricultural University/State Key Laboratory of Tea Plant Biology and Utilization, Anhui Agricultural University, Hefei 230036, Anhui (China); Wan, Xiaochun, E-mail: xcwan@ahau.edu.cn [School of Tea & Food Science and Technology, Anhui Agricultural University/State Key Laboratory of Tea Plant Biology and Utilization, Anhui Agricultural University, Hefei 230036, Anhui (China)

    2016-07-01

    Highlights: • Ultrafine tea powder (UTP) was prepared by ball-milling. • A novel and high efficient biosorbent from ultrafine tea powder (UTP) for the removal of fluoride from drinking water was prepared. • Loaded ultrafine tea powder adsorbed more fluoride adsorption than loaded tea waste. • UTP-Zr performed well over a considerably wide pH range, from 3.0 to 10.0. • UTP-Zr retains Zr metal ion during defluoridation, limiting secondary pollution. - Abstract: A low-cost and highly efficient biosorbent was prepared by loading zirconium(IV) onto ball-milled, ultrafine tea powder (UTP-Zr) for removal of fluoride from drinking water. To evaluate the fluoride adsorption capacity of UTP-Zr over a wide range of conditions, the biosorbent dosage, contact time, initial pH, initial fluoride concentration and presence of other ions were varied. UTP-Zr performed well over the considerably wide pH range of 3–10. The residual concentration of Zr in the treated water was below the limit of detection (0.01 mg/L). Fluoride adsorption by the UTP-Zr biosorbent followed the Langmuir model, with a maximum adsorption capacity of 12.43 mgF/g at room temperature. The fluoride adsorption kinetics fit the pseudo-second-order kinetic model. The synthesized biosorbent was characterized by BET, SEM, EDS, XRD and XPS to reveal how UTP-Zr interacts with fluoride. Results from this study demonstrated that UTP-based biosorbents will be useful and safe for the removal of fluoride from drinking water.

  4. Removal of fluoride from drinking water using modified ultrafine tea powder processed using a ball-mill

    International Nuclear Information System (INIS)

    Cai, Huimei; Xu, Lingyun; Chen, Guijie; Peng, Chuanyi; Ke, Fei; Liu, Zhengquan; Li, Daxiang; Zhang, Zhengzhu; Wan, Xiaochun

    2016-01-01

    Highlights: • Ultrafine tea powder (UTP) was prepared by ball-milling. • A novel and high efficient biosorbent from ultrafine tea powder (UTP) for the removal of fluoride from drinking water was prepared. • Loaded ultrafine tea powder adsorbed more fluoride adsorption than loaded tea waste. • UTP-Zr performed well over a considerably wide pH range, from 3.0 to 10.0. • UTP-Zr retains Zr metal ion during defluoridation, limiting secondary pollution. - Abstract: A low-cost and highly efficient biosorbent was prepared by loading zirconium(IV) onto ball-milled, ultrafine tea powder (UTP-Zr) for removal of fluoride from drinking water. To evaluate the fluoride adsorption capacity of UTP-Zr over a wide range of conditions, the biosorbent dosage, contact time, initial pH, initial fluoride concentration and presence of other ions were varied. UTP-Zr performed well over the considerably wide pH range of 3–10. The residual concentration of Zr in the treated water was below the limit of detection (0.01 mg/L). Fluoride adsorption by the UTP-Zr biosorbent followed the Langmuir model, with a maximum adsorption capacity of 12.43 mgF/g at room temperature. The fluoride adsorption kinetics fit the pseudo-second-order kinetic model. The synthesized biosorbent was characterized by BET, SEM, EDS, XRD and XPS to reveal how UTP-Zr interacts with fluoride. Results from this study demonstrated that UTP-based biosorbents will be useful and safe for the removal of fluoride from drinking water.

  5. Particle and powder characterisation of Bi-based superconductors

    International Nuclear Information System (INIS)

    Yavuz, M.; Guo, Y. C.; Liu, H. L.; Dou, S. X.; Vance, E. R.

    1996-01-01

    Full text: Superconductor precursor powder was ground in a planetary and an attrition mill using various combinations of grinding container, balls and carrier (dry and wet). Dry milling was found to be more effective than wet milling for reducing particle size irrespective of container and ball materials used in the planetary milling. On the other hand, wet milling was found more effective in the attrition milling. Serious Si contamination was observed in powders milled using agate grinding materials. Some C from polypropylene container was found after milling, but no Zr from YSZ balls. Effect of particle size on the property of Bi 2223/Ag tapes was investigated in terms of critical current density (J c ). Fine particle size was found to show high J c

  6. Improved critical current densities in bulk FeSe superconductor using ball milled powders and high temperature sintering

    Energy Technology Data Exchange (ETDEWEB)

    Muralidhar, M.; Furutani, K.; Murakami, M. [Graduate School of Science and Engineering, Superconducting Materials Laboratory, Shibaura Institute of Technology, Tokyo (Japan); Kumar, Dinesh; Rao, M.S. Ramachandra [Department of Physics, Nano Functional Materials Technology Centre and Materials Science Research Centre, Indian Institute of Technology Madras, Chennai (India); Koblischka, M.R. [Institute of Experimental Physics, Saarland University, Saarbruecken (Germany)

    2016-12-15

    The present study is investigating the effect of high temperature sintering combined with ball milled powders for the preparation of FeSe material via solid state sintering technique. The commercial powders of Fe (99.9% purity) and Se (99.9% purity) were mixed in a nominal ratio Fe:Se = 1:1 and thoroughly ground and ball-milled in a glove box during 6 h. Then, the powder mixture was pressed into pellets of 5 mm in diameter and 2 mm thickness using an uniaxial pressure of 100 MPa. The samples were sealed in quartz tubes and sintered at 600 C for 24 h. Then, the pellets were again thoroughly ground and ball-milled in the glove box and pressed into pellets, and the final sintering was performed at two different temperatures, namely at 900 C for 24 h and at 950 C for 24 h. X-ray diffraction results confirmed that both samples showed mainly of the β-FeSe with tetragonal structure. The temperature dependence of magnetization (M-T) curves revealed a sharp superconducting transition T{sub c,} {sub onset} = 8.16 K for the sample sintered at 900 C. Further, scanning electron microscopy observations proved that samples sintered at 900 C show a platelike grain structure with high density. As a result, improved irreversibility fields around 5 T and the critical current density (J{sub c}) values of 6252 A cm{sup -2} at 5 K and self-field are obtained. Furthermore, the normalized volume pinning force versus the reduced field plots indicated a peak position at 0.4 for the sample sintered at 900 C. Improved flux pinning and the high J{sub c} values are attributed to the textured microstructure of the material, produced by a combination of high temperature sintering and ball milling. (copyright 2016 The Authors. Phys. Status Solidi A published by WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  7. Synthesis of (Cr,V){sub 2}(C,N) solid solution powders by thermal processing precursors

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Anrui [School of Materials Science & Engineering, Sichuan University, Chengdu, 610065 (China); Liu, Ying [School of Materials Science & Engineering, Sichuan University, Chengdu, 610065 (China); Key Laboratory of Advanced Special Material & Technology, Ministry of Education, Chengdu, 610065 (China); Ma, Shiqing; Qiu, Yuchong; Rong, Pengcheng; Ye, Jinwen [School of Materials Science & Engineering, Sichuan University, Chengdu, 610065 (China)

    2017-06-01

    The single-phase (Cr,V){sub 2}(C,N) solid solution powders were fabricated via carbothermal reduction-nitridation (CRN) processing technique. The effects of heat treatment temperature, nitrogen pressure and carbon proportion were experimentally studied in detail by X-ray Diffraction (XRD), Scanning Electron Microscope (SEM), Transmission Electron Microscope (TEM) and thermal analysis. The chemical transformations of vanadium and chromium compounds were as follows: precursors → V{sub 2}O{sub 3}, Cr{sub 2}O{sub 3} → Cr{sub 3}C{sub 2}, Cr{sub 2}O{sub 3}, (Cr,V){sub 2}(C,N) → (Cr,V){sub 2}(C,N). When the heat-treated temperature was below 1200 °C, chromium oxides didn’t completely react. However, higher temperature ∼1300 °C could not only lead to the segregation of some nitrides and carbon black, but also to the occurrence of fiber-bridged particles. The system nitrogen pressure over 0.03 MPa would cause a subtle transformation of (Cr,V){sub 2}(C,N) to VCrN{sub 2}. When the carbon proportion was below 15 wt%, the oxides could not be completely reduced, while when the carbon proportion was above 15.5 wt%, some undesired carbides, like Cr{sub 23}C{sub 6} and Cr{sub 3}C{sub 2}, would form. Ultimately, the homogeneously distributed pure-phase (Cr,V){sub 2}(C,N) spherical particles with the average size of ∼1.5 μm were obtained at the optimal conditions of the treatment of precursors at 1200 °C for 1 h with the nitrogen pressure of 0.03 MPa and carbon content of 15.5 wt%. The chemical composition of the solid solution with the optimal process could be drawn as (Cr{sub 0.85}V{sub 0.15}){sub 2}(C{sub 0.57}N{sub 0.43}). Thermal processing precursors method shows the advantages of lower synthesis temperature, shorter period and finer particles when comparing with the conventional preparations. - Highlights: • Single phase of (Cr,V){sub 2}(C,N) powders were synthesized for the first time. • Precursors were used to prepared the powders by carbothermal

  8. Process optimization and particle engineering of micronized drug powders via milling.

    Science.gov (United States)

    Brunaugh, A; Smyth, H D C

    2017-11-13

    Process control and optimization is a critical aspect of process analytical technology (PAT), quality by design (QbD), and the implementation of continuous manufacturing procedures. While process control and optimization techniques have been utilized in other manufacturing industries for decades, the pharmaceutical industry has only recently begun to adopt these procedures. Micronization, particularly milling, is a generally low-yield, high-energy consumption process that is well suited for a process optimization mindset. This review discusses optimization of the pharmaceutical milling process through design space development, theoretical and empirical modeling, and monitoring of critical quality attributes.

  9. Process variables in the obtention of U-Mo powder by the hydriding-milling-dehydriding method (HMD process)

    International Nuclear Information System (INIS)

    Pasqualini, Enrique E.; Helzel Garcia, Javier; Lopez, Marisol

    2003-01-01

    In the next few years nuclear fuels based on uranium oxides, aluminides and silicides for MTR reactors will be replaced by the high density alloy uranium- 7% (w/w) molybdenum (U-7 Mo). Actually there is only one commercial supplier of this raw material that has to be provided as powder containing 20% enriched uranium ( 235 U). In the Nuclear Fuels Department of the National Atomic Energy Commission (CNEA) at Buenos Aires was developed an alternative way of producing U-7 Mo powder in a production scale. Meanwhile CNEA is participating in the International Program (RERTR) for final qualification of this nuclear material. This new method of production consists in the hydriding of the alloy, milling the hydride to final size and dehydriding the powder. These results were achieved because a special technique was discovered for the massive hydriding of the U-7 Mo alloy. The production method is simple, requires conventional equipment and low investment. Argentine can have important comparative advantages for its production and exportation. A scale production plant is being planed. (author)

  10. Nano crystalline high energy milled 5083 Al powder deposited using cold spray

    Energy Technology Data Exchange (ETDEWEB)

    Rokni, M.R., E-mail: mohammadreza.rokni@mines.sdsmt.edu [Department of Materials and Metallurgical Engineering, Advanced Materials Processing Center, South Dakota School of Mines and Technology (SDSM and T), SD (United States); Widener, C.A. [Department of Materials and Metallurgical Engineering, Advanced Materials Processing Center, South Dakota School of Mines and Technology (SDSM and T), SD (United States); Nardi, A.T. [United Technologies Research Center, East Hartford, CT (United States); Champagne, V.K. [U.S. Army Research Laboratory, Weapons and Materials Research Directorate, Aberdeen Proving Ground, MD (United States)

    2014-06-01

    Electron microscopy and nanoindentation are used to investigate the relationship between microstructure and nanohardness of a non-cryomilled, nanocrystalline 5083 Al alloy powder before and after being deposited by cold spray. Microstructural investigations observed the presence of nano grains in the powder microstructure, ranging from 20 to 80 nm and with a typical grain size of 40–50 nm. It was also revealed that the nanocrystalline structure of the powder is retained after cold spraying. As a result, almost no change in nanohardness was indicated between the powder and the particles interior in the cold sprayed layer. However, hardness was substantially higher in some regions in the cold sprayed layer, which was attributed to the particle–particle interfaces or other areas with very small nano grain size. The presence of some un-joined particle remnant lines was also found in the deposition and explained through Critical Velocity Ratio (CVR) of powder particles. Although cold spray is a high deformation process, there is little evidence of dislocations within the nanograins of the cold sprayed layer. The latter observation is rationalized through intragranular dislocation slip and recovery mechanisms.

  11. Reverse martensitic transformation in alumina-15 vol% zirconia nanostructured powder synthesized by high energy ball milling

    Energy Technology Data Exchange (ETDEWEB)

    Maneshian, M.H. [Department of Materials Science and Engineering, Sharif University of Technology, Azadi Avenue, P.O. Box 11365-9466, Tehran (Iran, Islamic Republic of)], E-mail: mh_maneshian@yahoo.com; Banerjee, M.K. [National Institute of Foundry and Forge Technology, Hatia, Ranchi 834003 (India)

    2008-07-14

    In the present work, three alumina-15 vol% zirconia composites with Y{sub 2}O{sub 3}, MgO as dopants and without oxide as dopant have been investigated. High energy ball milling (HEBM) provides the positive thermodynamic driving force for monoclinic to tetragonal transformation and it reduces starting temperature for the reverse martensitic transformation, meanwhile mobility of zirconium cations and oxygen anions are enhanced in zirconia by HEBM. The general, albeit heuristic, reasoning is corroborated by nanocrystallity, particle size and also the retained monoclinic seem to play an important role. After 10 h HEBM, approximately 28% zirconia tetragonal phase is achieved. Non-stoichiometric tetragonal zirconia phase; Zr{sub 0.95}O{sub 2} is seen to have been achieved by high energy ball milling (HEBM). The structural and compositional evolutions during HEBM have been investigated using X-ray diffraction method (XRD) and scanning electron microscopy (SEM). High resolution transmission electron microscope (TEM) is also used for further understanding about the phenomenological changes taking place during high energy ball milling.

  12. A Mössbauer and magnetic study of ball milled Fe-doped ZnO Powders

    Energy Technology Data Exchange (ETDEWEB)

    Zamora, Ligia E., E-mail: ligia.zamora@correounivalle.edu.co; Paz, J. C.; Piamba, J. F.; Tabares, J. A.; Alcázar, G. A. Pérez [Universidad del Valle, Departamento de física (Colombia)

    2015-06-15

    The structural and magnetic properties of Fe-doped ZnO are reported in this study, as obtained by mechanical alloying from elemental powders of ZnO and Fe. The properties of Zn{sub 0.90}Fe{sub 0.10}O samples alloying while varying the milling time (6, 12, 24 and 36 h) are also reported. The Rietveld refinement of X-ray Diffraction (XRD) patterns revealed that the system presents two structures: the würtzite structure of ZnO and the bcc structure of α-Fe. The Mössbauer spectra show that the samples present three components: a ferromagnetic component, associated with the Fe phase and two paramagnetic components, associated with the Fe atoms, which penetrate inside the ZnO matrix behaving as Fe{sup 3+} and Fe{sup 2+}. The milling time contributes to an increase in the paramagnetic sites, and a solubility limit of the Fe atoms in the ZnO lattice was detected. The VSM measurements at room temperature detected ferromagnetic behavior with a saturation magnetization of 11 emu/g and a coercive field of 330 Oe for the sample alloyed over 24 h. A similar behavior was shown by the other samples.

  13. A novel use of Moringa oleifera seed powder in enhancing the primary treatment of paper mill effluent.

    Science.gov (United States)

    Boulaadjoul, Soumia; Zemmouri, Hassiba; Bendjama, Zoubida; Drouiche, Nadjib

    2018-05-02

    In this study, Moringa oleifera (M. oleifera) performance as an eco-friendly coagulant in the enhanced primary treatment of paper mill effluent was investigated. Its performance in terms of turbidity removal and COD abatement was examined. Local M. oleifera seed powder from ADRAR-city, South of Algeria, was used. Conventional jar tests were conducted for enhancing the primary treatment of paper mill effluent from paper factory. For this reason, comparative coagulation tests were performed using aluminum sulfate (alum). Indeed, in terms of turbidity abatement, 96.02% and 97.1% were obtained for Moringa and alum, respectively. However, in the case of COD abatement, the abatement rate of M. oleifera seeds was slightly higher than that of alum, 97.28% and 92.67%, respectively. Because M. oleifera is a natural resource that is locally available, an eco-friendly coagulant, non-toxic, and biodegradable and does not affect the pH of water; thus, its use allows to avoid numerous disadvantages of conventional coagulants like alum. Copyright © 2018 Elsevier Ltd. All rights reserved.

  14. Surface area, crystal morphology and characterization of transition alumina powders from a new gibbsite precursor

    Directory of Open Access Journals (Sweden)

    Antonio Carlos Vieira Coelho

    2007-06-01

    Full Text Available A new procedure was used to prepare a microcrystalline powder constituted by thin euhedral hexagonal gibbsite plates, 0.2 to 0.6 µm in diameter and 32 nm thick. The powder, fired between 200 and 1000 °C, produced chi and kappa transition aluminas. Alpha-alumina is formed from 1000 °C and recrystallized up to 1500 °C. At 1000 °C, kappa- and alpha-alumina coexisted, but kappa-alumina could only be characterized by SAED. The details of the internal organization of the transition alumina pseudomorphs were clearly observable in TEM due to the great thinness of the I-gibbsite plates. The specific surface area varied from pristine I-gibbsite (24.9 m².g-1 to chi- and kappa transition aluminas (25.4 m².g-1 at 1000 °C to alpha-alumina (4.0 m².g-1 at 1500 °C. The maximum value of specific surface area is 347 m².g-1 in chi-alumina powder at 300 °C, a difference from Bayer gibbsite, in which the chi-alumina highest surface area is 370 m².g-1 at 400 °C.

  15. The effect of surfactant addition on high-energy milling upon the magnetic properties and microstructure of the Pr-Fe-B HDDR magnetic powders

    International Nuclear Information System (INIS)

    Santos, P.B.; Silva, S.C.; Faria, R.N.; Takiishia, H.

    2010-01-01

    Nanomagnetic powders based on the composition Pr 12 Fe 65.9 Co 16 B 6 Nb 0.1 have been obtained from using (a) the hydrogenation, disproportionation, desorption and recombination (HDDR) process; (b) by varying of milling time and (c) with the addition of an oleic acid as a surfactant. The latter has been used to enhance milling condition by preventing the agglomeration of particles and hence to improve the intrinsic coercivity of the material. High-energy mechanical milling has been used to yield magnetic nanoparticles. Powders were characterized magnetically using vibrating sample magnetometer (VSM) and microstructurally by Scanning Electron Microscopy (SEM), Field Emission Gun SEM (FEG-SEM) and X-ray diffraction. (author)

  16. Effect of milling time and annealing temperature on nanoparticles evolution for 13.5% Cr ODS ferritic steel powders by joint application of XAFS and TEM

    Science.gov (United States)

    He, P.; Hoffmann, J.; Möslang, A.

    2018-04-01

    The characteristics of strengthening nanoparticles have a major influence on the mechanical property and irradiation resistance of oxide dispersion strengthened (ODS) steels. To determine how to control nanoparticles evolution, 0.3% Ti with 0.3% Y2O3 were added in 13.5%Cr pre-alloyed steel powders via different milling and consolidation conditions, then characterized by transmission electron microscopy (TEM) and X-ray absorption fine structure (XAFS) at synchrotron irradiation facility. The dissolution of Y2O3 is greatly dependent on the milling time at fixed milling speeds. After 24 h of milling, only minor amounts of the initially added Y2O3 dissolve into the steel matrix whereas TEM results reveal nearly complete dissolution of Y2O3 in 80-h-milled powder. The annealed powder FT-A800 (at 800 °C for 1 h) exhibits a structure near to the initially added Y2O3. The slightly deviation may be accounted for considerable lattice distortion related to the presence of atomic vacancies or formation of Y-Ti-O nucleus. The annealed powders FT-A1000 and FT-A1100 contain complex mixtures of Y-O/Y-Ti-O oxides, which cannot be fitted by any single thermally stable compounds. The coordination numbers of these first two shells in the annealed powders significantly raise as a function of the annealing temperature, indicating the formation of more ordered Y-O or Y-Ti-O particles. The extended X-ray absorption fine structure (EXAFS) spectrum could not necessarily distinguish the dominant oxide species.

  17. Production of a Powder Metallurgical Hot Work Tool Steel with Harmonic Structure by Mechanical Milling and Spark Plasma Sintering

    Science.gov (United States)

    Deirmina, Faraz; Pellizzari, Massimo; Federici, Matteo

    2017-04-01

    Commercial AISI-H13 gas atomized powders (AT) were mechanically milled (MM) to refine both the particle size and the microstructure. Different volume fractions of coarser grained (CG) AT powders were mixed with the ultra-fine grained (UFG) MM and consolidated by spark plasma sintering to obtain bulks showing a harmonic structure ( i.e. a 3D interconnected network of UFG areas surrounding the CG atomized particles). The low sintering temperature, 1373.15 K (1100 °C) and the short sintering time (30 minutes) made it possible to obtain near full density samples while preserving the refined microstructure induced by MM. A combination of high hardness and significantly improved fracture toughness is achieved by the samples containing 50 to 80 vol pct MM, essentially showing harmonic structure. The design allows to easily achieve specific application oriented properties by varying the MM volume fraction in the initial mixture. Hardness is governed by the fine-grained MM matrix and improved toughening is due to (1) deviatory effect of AT particles and (2) energy dissipation as a result of the decohesion in MM regions or AT and MM interface.

  18. Milling Behavior of Matrix Graphite Powders with Different Binder Materials in HTGR Fuel Element Fabrication: I. Variation in Particle Size Distribution

    International Nuclear Information System (INIS)

    Lee, Young Woo; Cho, Moon Sung

    2011-01-01

    The fuel element for HTGR is manufactured by mixing coated fuel particles with matrix graphite powder and forming into either pebble type or cylindrical type compacts depending on their use in different HTGR cores. The coated fuel particle, the so-called TRISO particle, consists of 500-μm spherical UO 2 particles coated with the low density buffer Pyrolytic Carbon (PyC) layer, the inner and outer high density PyC layer and SiC layer sandwiched between the two inner and outer PyC layers. The coated TRISO particles are mixed with a matrix graphite powder properly prepared and pressed into a spherical shape or a cylindrical compact finally heat-treated at about 1900 .deg. C. These fuel elements can have different sizes and forms of compact. The basic steps for manufacturing a fuel element include preparation of graphite matrix powder, overcoating the fuel particles, mixing the fuel particles with a matrix powder, carbonizing green compact, and the final high-temperature heat treatment of the carbonized fuel compact. In order to develop a fuel compact fabrication technology, it is important to develop a technology to prepare the matrix graphite powder (MGP) with proper characteristics, which has a strong influence on further steps and the material properties of fuel element. In this work, the milling behavior of matrix graphite powder mixture with different binder materials and their contents was investigated by analyzing the change in particle size distribution with different milling time

  19. Influence of spark plasma sintering conditions on the sintering and functional properties of an ultra-fine grained 316L stainless steel obtained from ball-milled powder

    Energy Technology Data Exchange (ETDEWEB)

    Keller, C., E-mail: clement.keller@insa-rouen.fr [Groupe de Physique des Matériaux, CNRS-UMR 6634, Université de Rouen, INSA de Rouen, Avenue de l' Université, 76800 Saint-Etienne du Rouvray (France); Tabalaiev, K.; Marnier, G. [Groupe de Physique des Matériaux, CNRS-UMR 6634, Université de Rouen, INSA de Rouen, Avenue de l' Université, 76800 Saint-Etienne du Rouvray (France); Noudem, J. [Laboratoire de Cristallographie des Matériaux, CNRS-UMR 6508, Université de Caen, ENSICAEN, 7 bd du Maréchal Juin, 14050 Caen (France); Sauvage, X. [Groupe de Physique des Matériaux, CNRS-UMR 6634, Université de Rouen, INSA de Rouen, Avenue de l' Université, 76800 Saint-Etienne du Rouvray (France); Hug, E. [Laboratoire de Cristallographie des Matériaux, CNRS-UMR 6508, Université de Caen, ENSICAEN, 7 bd du Maréchal Juin, 14050 Caen (France)

    2016-05-17

    In this work, 316L samples with submicrometric grain size were sintered by spark plasma sintering. To this aim, 316L powder was first ball-milled with different conditions to obtain nanostructured powder. The process control agent quantity and milling time were varied to check their influence on the crystallite size of milled powder. Samples were then sintered by spark plasma sintering using different sets of sintering parameters (temperature, dwell time and pressure). For each sample, grain size and density were systematically measured in order to investigate the influence of the sintering process on these two key microstructure parameters. Results show that suitable ball-milling and subsequent sintering can be employed to obtain austenitic stainless steel samples with grain sizes in the nanometer range with porosity lower than 3%. However, ball-milling and subsequent sintering enhance chromium carbides formation at the sample surface in addition to intragranular and intergranular oxides in the sample as revealed by X-ray diffraction and transmission electron microscopy. It has been shown that using Boron nitride together with graphite foils to protect the mold from powder welding prevent such carbide formation. For mechanical properties, results show that the grain size refinement strongly increases the hardness of the samples without deviation from Hall-Petch relationship despite the oxides formation. For corrosion resistance, grain sizes lower than a few micrometers involve a strong decrease in the pitting potential and a strong increase in passivation current. As a consequence, spark plasma sintering can be considered as a promising tool for ultra-fine grained austenitic stainless steel.

  20. The Effect of Milling Time on the Microstructural Characteristics and Strengthening Mechanisms of NiMo-SiC Alloys Prepared via Powder Metallurgy

    Science.gov (United States)

    Yang, Chao; Muránsky, Ondrej; Zhu, Hanliang; Thorogood, Gordon J.; Avdeev, Maxim; Huang, Hefei; Zhou, Xingtai

    2017-01-01

    A new generation of alloys, which rely on a combination of various strengthening mechanisms, has been developed for application in molten salt nuclear reactors. In the current study, a battery of dispersion and precipitation-strengthened (DPS) NiMo-based alloys containing varying amounts of SiC (0.5–2.5 wt %) were prepared from Ni-Mo-SiC powder mixture via a mechanical alloying (MA) route followed by spark plasma sintering (SPS) and rapid cooling. Neutron Powder Diffraction (NPD), Electron Back Scattering Diffraction (EBSD), and Transmission Electron Microscopy (TEM) were employed in the characterization of the microstructural properties of these in-house prepared NiMo-SiC DPS alloys. The study showed that uniformly-dispersed SiC particles provide dispersion strengthening, the precipitation of nano-scale Ni3Si particles provides precipitation strengthening, and the solid-solution of Mo in the Ni matrix provides solid-solution strengthening. It was further shown that the milling time has significant effects on the microstructural characteristics of these alloys. Increased milling time seems to limit the grain growth of the NiMo matrix by producing well-dispersed Mo2C particles during sintering. The amount of grain boundaries greatly increases the Hall–Petch strengthening, resulting in significantly higher strength in the case of 48-h-milled NiMo-SiC DPS alloys compared with the 8-h-milled alloys. However, it was also shown that the total elongation is considerably reduced in the 48-h-milled NiMo-SiC DPS alloy due to high porosity. The porosity is a result of cold welding of the powder mixture during the extended milling process. PMID:28772747

  1. The Effect of Milling Time on the Microstructural Characteristics and Strengthening Mechanisms of NiMo-SiC Alloys Prepared via Powder Metallurgy

    Directory of Open Access Journals (Sweden)

    Chao Yang

    2017-04-01

    Full Text Available A new generation of alloys, which rely on a combination of various strengthening mechanisms, has been developed for application in molten salt nuclear reactors. In the current study, a battery of dispersion and precipitation-strengthened (DPS NiMo-based alloys containing varying amounts of SiC (0.5–2.5 wt % were prepared from Ni-Mo-SiC powder mixture via a mechanical alloying (MA route followed by spark plasma sintering (SPS and rapid cooling. Neutron Powder Diffraction (NPD, Electron Back Scattering Diffraction (EBSD, and Transmission Electron Microscopy (TEM were employed in the characterization of the microstructural properties of these in-house prepared NiMo-SiC DPS alloys. The study showed that uniformly-dispersed SiC particles provide dispersion strengthening, the precipitation of nano-scale Ni3Si particles provides precipitation strengthening, and the solid-solution of Mo in the Ni matrix provides solid-solution strengthening. It was further shown that the milling time has significant effects on the microstructural characteristics of these alloys. Increased milling time seems to limit the grain growth of the NiMo matrix by producing well-dispersed Mo2C particles during sintering. The amount of grain boundaries greatly increases the Hall–Petch strengthening, resulting in significantly higher strength in the case of 48-h-milled NiMo-SiC DPS alloys compared with the 8-h-milled alloys. However, it was also shown that the total elongation is considerably reduced in the 48-h-milled NiMo-SiC DPS alloy due to high porosity. The porosity is a result of cold welding of the powder mixture during the extended milling process.

  2. The Effect of Milling Time on the Microstructural Characteristics and Strengthening Mechanisms of NiMo-SiC Alloys Prepared via Powder Metallurgy.

    Science.gov (United States)

    Yang, Chao; Muránsky, Ondrej; Zhu, Hanliang; Thorogood, Gordon J; Avdeev, Maxim; Huang, Hefei; Zhou, Xingtai

    2017-04-06

    A new generation of alloys, which rely on a combination of various strengthening mechanisms, has been developed for application in molten salt nuclear reactors. In the current study, a battery of dispersion and precipitation-strengthened (DPS) NiMo-based alloys containing varying amounts of SiC (0.5-2.5 wt %) were prepared from Ni-Mo-SiC powder mixture via a mechanical alloying (MA) route followed by spark plasma sintering (SPS) and rapid cooling. Neutron Powder Diffraction (NPD), Electron Back Scattering Diffraction (EBSD), and Transmission Electron Microscopy (TEM) were employed in the characterization of the microstructural properties of these in-house prepared NiMo-SiC DPS alloys. The study showed that uniformly-dispersed SiC particles provide dispersion strengthening, the precipitation of nano-scale Ni₃Si particles provides precipitation strengthening, and the solid-solution of Mo in the Ni matrix provides solid-solution strengthening. It was further shown that the milling time has significant effects on the microstructural characteristics of these alloys. Increased milling time seems to limit the grain growth of the NiMo matrix by producing well-dispersed Mo₂C particles during sintering. The amount of grain boundaries greatly increases the Hall-Petch strengthening, resulting in significantly higher strength in the case of 48-h-milled NiMo-SiC DPS alloys compared with the 8-h-milled alloys. However, it was also shown that the total elongation is considerably reduced in the 48-h-milled NiMo-SiC DPS alloy due to high porosity. The porosity is a result of cold welding of the powder mixture during the extended milling process.

  3. Preparation of (Bi,Pb)2Sr2Ca2Cu3Ox precursor powders by a modified polyethylene glycol based sol-gel process

    DEFF Research Database (Denmark)

    Grivel, Jean-Claude; Andersen, N.H.

    2002-01-01

    A modified sol-gel process based on polyethylene glycol has been developed for preparing (Bi,Pb)(2)Sr2Ca2Cu3Ox precursor powders in view of Ag-sheeted tape manufacture. A careful control of the pH and concentration temperature yields an amorphous gel, which can be converted to a fine and extremely...

  4. High heat generation ability in AC magnetic field for nano-sized magnetic Y3Fe5O12 powder prepared by bead milling

    International Nuclear Information System (INIS)

    Aono, Hiromichi; Ebara, Hiroki; Senba, Ryota; Naohara, Takashi; Maehara, Tsunehiro; Hirazawa, Hideyuki; Watanabe, Yuji

    2012-01-01

    Nano-sized magnetic Y 3 Fe 5 O 12 ferrite having a high heat generation ability in an AC magnetic field was prepared by bead milling. A commercial powder sample (non-milled sample) of ca. 2.9 μm in particle size did not show any temperature enhancement in the AC magnetic field. The heat generation ability in the AC magnetic field improved with a decrease in the average crystallite size for the bead-milled Y 3 Fe 5 O 12 ferrites. The highest heat ability in the AC magnetic field was for the fine Y 3 Fe 5 O 12 powder with a 15-nm crystallite size (the samples were milled for 4 h using 0.1 mmφ beads). The heat generation ability of the excessively milled Y 3 Fe 5 O 12 samples decreased. The main reason for the high heat generation property of the milled samples was ascribed to an increase in the Néel relaxation of the superparamagnetic material. The heat generation ability was not influenced by the concentration of the ferrite powder. For the samples milled for 4 h using 0.1 mmφ beads, the heat generation ability (W g −1 ) was estimated using a 3.58×10 −4 fH 2 frequency (f/kHz) and the magnetic field (H/kA m −1 ), which is the highest reported value of superparamagnetic materials. - Highlights: ► The nano-sized Y 3 Fe 5 O 12 powder prepared by bead-milling has the highest heat generation ability in an AC magnetic field. ► The heat generation properties are ascribed to an increase in the Néel relaxation of the superparamagnetic material. ► The heat ability (W g −1 ) can be estimated using 3.58×10 −4 fH 2 (f=kHz, H=kA m −1 ). ► This is an expectable material for use in a drug delivery system for the thermal coagulation therapy of cancer tumors.

  5. On modeling the CNC end milling characteristics of Al-7075/WC powder metallurgy composites

    Science.gov (United States)

    Hanuman, N. S. V. N.; Rao, P. Gangadhara; Kumar, B. Sudheer; Karthik, N.

    2017-07-01

    Surface finish and material removal rate are two important factors in the manufacturing which affect acceptability of the product which in turn reflects on the profitability of the organization. The worth of the production setup to produce the components with high material removal rate (MRR) without sacrificing the surface requirements can play vital role in sustainability and profitability of the organization. In this paper, the effect of process parameters on metal removal rate and surface roughness has been investigated in milling of Al7075-MMC with WC as reinforcement element. Cutting speed, feed and depth of cut have been taken as input factors in three level response surface methodologies used for experimentation. Mathematical models have been developed using response surface methodology to predict surface finish, and metal removal rate in term of machining parameters. Depth of cut and feed rate are found to be a dominant parameter for surface roughness; whereas feed rate mainly affects the metal removal rate. The results of mathematical models have been compared with the experimental and found to be in good agreement. The results of predicted model can be used in selection of process parameters to insure desired quality and improved productivity.

  6. Growth kinetics of tetragonal and monoclinic ZrO2 crystallites in 3 mol% yttria partially stabilized ZrO2 (3Y-PSZ) precursor powder

    International Nuclear Information System (INIS)

    Kuo, Chih-Wei; Lee, Kuen-Chan; Yen, Feng-Lin; Shen, Yun-Hwei; Lee, Huey-Er; Wen, Shaw-Bing; Wang, Moo-Chin; Stack, Margaret Mary

    2014-01-01

    Highlights: • The crystalline structures were composed of tetragonal and monoclinic ZrO 2 . • Growth kinetics of t-ZrO 2 in the 3Y-PSZ precursor powder is described as: D te 2 =(4.57±0.55)t 0.12±0.02 exp(-((24.79±0.38)×10 3 )/(RT) ). • Growth kinetics of m-ZrO 2 in the 3Y-PSZ precursor powder is described as: D m 2 =(4.40±1.63)t 0.17±0.08 exp(-((66.47±3.97)×10 3 )/(RT) ). - Abstract: The growth kinetics of tetragonal and monoclinic ZrO 2 crystallites in 3 mol% yttria partially stabilized ZrO 2 (3Y-PSZ) precursor powder has been investigated using X-ray diffraction (XRD), Brunauer–Emmett–Teller (BET) specific surface area analysis, transmission electron microscopy (TEM) and high resolution TEM (HRTEM). After calcination of the 3Y-PSZ precursor powder between 773 and 1073 K for 2 h, the crystalline structures were composed of tetragonal and monoclinic ZrO 2 as the primary and secondary phases, respectively. When the 3Y-PSZ precursor powder was calcined at 773 K for 2 h, the BET specific surface area was 97.13 m 2 /g, which is equivalent to a particle size of 10.30 nm. The crystallite sizes determined via XRD and BET agreed well, indicating that the powder was virtually non-agglomerated. The growth kinetics of tetragonal and monoclinic ZrO 2 crystallite isothermal growth in the 3Y-PSZ precursor powder are described by: D te 2 =(4.57±0.55)t 0.12±0.02 exp(-((24.79±0.38)×10 3 )/(RT) ) and D m 2 =(4.40±1.63)t 0.17±0.08 exp(-((66.47±3.97)×10 3 )/(RT) ), respectively, for 773K≤T≤1073K. D te and D m denote the crystallite size of tetragonal and monoclinic ZrO 2 at time t and temperature T, respectively

  7. Preparation and Characterization of Activated Cow Bone Powder for the Adsorption of Cadmium from Palm Oil Mill Effluent

    Science.gov (United States)

    AbdulRahman, A.; Latiff, A. A. A.; Daud, Z.; Ridzuan, M. B.; D, N. F. M.; Jagaba, A. H.

    2016-07-01

    Several studies have been conducted on the removal of heavy metals from palm oil mill effluent. In this study, cow bones were developed as an adsorbent for the removal of cadmium II from POME. A batch experiment was conducted to investigate the effectiveness of the prepared activated cow bone powder for the sorption of cadmium II from raw POME. The experiment was carried out under fixed conditions using 100mg/L raw POME combined with different adsorbent dosage of CBP of 184.471 Ra(nm) surface roughness. The equilibrium adsorption capacity of the hydrophobic CBP of average contact angle 890 was determined from the relationship between the initial and equilibrium liquid phase concentrations of POME. The optimum adsorption of cadmium II on CBP was at 10g adsorbent dosage for sample 1 and 2 at 97.8% and 96.93% respectively. The least uptake was at 30g adsorbent weight for both samples at average of 95.1% for both samples. The effective removal of cadmium ion showed that CBP has a great potential for the treatment of heavy metal in POME.

  8. The Effect of Powder Ball Milling on the Microstructure and Mechanical Properties of Sintered Fe-Cr-Mo-Mn-(Cu) Steel

    Science.gov (United States)

    Kulecki, P.; Lichańska, E.

    2017-12-01

    The effect of ball milling powder mixtures of Höganäs pre-alloyed iron Astaloy CrM, low-carbon ferromanganese Elkem, elemental electrolytic Cu and C-UF graphite on the sintered structure and mechanical properties was evaluated. The mixing was conducted using Turbula mixer for 30 minutes and CDI-EM60 frequency inverter for 1 and 2 hours. Milling was performed on 150 g mixtures with (in weight %) CrM + 1% Mn, CrM + 2% Mn, CrM + 1% Mn + 1% Cu and CrM + 2% Mn + 1% Cu, all with 0.6%C. The green compacts were single pressed at 660 MPa according to PN-EN ISO 2740. Sintering was carried out in a laboratory horizontal furnace Carbolite STF 15/450 at 1250°C for 60 minutes in 5%H2 - 95%N2 atmosphere with a heating rate of 75°C/min, followed by sintering hardening at 60°C/min cooling rate. All the steels were characterized by martensitic structures. Mechanical testing revealed that steels based on milled powders have slightly higher mechanical properties compared to those only mixed and sintered. The best combination of mechanical properties, for ball milled CrM + 1% Mn + 1% Cu was UTS 1046 MPa, TRS 1336 MPa and A 1.94%.

  9. Heat generation ability in AC magnetic field of nano MgFe2O4-based ferrite powder prepared by bead milling

    International Nuclear Information System (INIS)

    Hirazawa, Hideyuki; Aono, Hiromichi; Naohara, Takashi; Maehara, Tsunehiro; Sato, Mitsunori; Watanabe, Yuji

    2011-01-01

    Nanosized MgFe 2 O 4 -based ferrite powder having heat generation ability in an AC magnetic field was prepared by bead milling and studied for thermal coagulation therapy applications. The crystal size and the particle size significantly decreased by bead milling. The heat generation ability in an AC magnetic field improved with the milling time, i.e. a decrease in crystal size. However, the heat generation ability decreased for excessively milled samples with crystal sizes of less than 5.5 nm. The highest heat ability (ΔT=34 o C) in the AC magnetic field (370 kHz, 1.77 kA/m) was obtained for fine MgFe 2 O 4 powder having a ca. 6 nm crystal size (the samples were milled for 6-8 h using 0.1 mm φ beads). The heat generation of the samples was closely related to hysteresis loss, a B-H magnetic property. The reason for the high heat generation properties of the samples milled for 6-8 h using 0.1 mm φ beads was ascribed to the increase in hysteresis loss by the formation of a single domain. Moreover, the improvement in heating ability was obtained by calcination of the bead-milled sample at low temperature. In this case, the maximum heat generation (ΔT=41 o C) ability was obtained for a ca. 11 nm crystal size sample was prepared by crystal growth during the sample calcination. On the other hand, the ΔT value for Mg 0.5 Ca 0.5 Fe 2 O 4 was synthesized using a reverse precipitation method decreased by bead milling. - Research Highlights: →The crystal and particle size for MgFe 2 O 4 based ferrite were decreased by bead milling. →The highest heat ability was obtained for MgFe 2 O 4 having a ca. 6 nm crystal size. →This high heat generation ability was ascribed to the increase in hysteresis loss. →Hysteresis loss was increased by the formation of a single domain.

  10. The grinding behavior of ground copper powder for Cu/CNT nanocomposite fabrication by using the dry grinding process with a high-speed planetary ball mill

    Science.gov (United States)

    Choi, Heekyu; Bor, Amgalan; Sakuragi, Shiori; Lee, Jehyun; Lim, Hyung-Tae

    2016-01-01

    The behavior of ground copper powder for copper-carbon nanotube (copper-CNT) nanocomposite fabrication during high-speed planetary ball milling was investigated because the study of the behavior characteristics of copper powder has recently gained scientific interest. Also, studies of Cu/CNT composites have widely been done due to their useful applications to enhanced, advanced nano materials and components, which would significantly improve the properties of new mechatronics-integrated materials and components. This study varied experimental conditions such as the rotation speed and the grinding time with and without CNTs, and the particle size distribution, median diameter, crystal structure and size, and particle morphology were monitored for a given grinding time. We observed that pure copper powders agglomerated and that the morphology changed with changing rotation speed. The particle agglomerations were observed with maximum experiment conditions (700 rpm, 60 min) in this study of the grinding process for mechanical alloys in the case of pure copper powders because the grinding behavior of Cu/CNT agglomerations was affected by the addition of CNTs. Indeed, the powder morphology and the crystal size of the composite powder could be changed by increasing the grinding time and the rotation speed.

  11. Synthesis and characterization of scandia ceria stabilized zirconia powders prepared by polymeric precursor method for integration into anode-supported solid oxide fuel cells

    Science.gov (United States)

    Tu, Hengyong; Liu, Xin; Yu, Qingchun

    2011-03-01

    Scandia ceria stabilized zirconia (10Sc1CeSZ) powders are synthesized by polymeric precursor method for use as the electrolyte of anode-supported solid oxide fuel cell (SOFC). The synthesized powders are characterized in terms of crystalline structure, particle shape and size distribution by X-ray diffraction (XRD), transmission electron microscopy (TEM) and photon correlation spectroscopy (PCS). 10Sc1CeSZ electrolyte films are deposited on green anode substrate by screen-printing method. Effects of 10Sc1CeSZ powder characteristics on sintered films are investigated regarding the integration process for application as the electrolytes in anode-supported SOFCs. It is found that the 10Sc1CeSZ films made from nano-sized powders with average size of 655 nm are very porous with many open pores. In comparison, the 10Sc1CeSZ films made from micron-sized powders with average size of 2.5 μm, which are obtained by calcination of nano-sized powders at higher temperatures, are much denser with a few closed pinholes. The cell performances are 911 mW cm-2 at the current density of 1.25 A cm-2 and 800 °C by application of Ce0.8Gd0.2O2 (CGO) barrier layer and La0.6Sr0.4CoO3 (LSC) cathode.

  12. Obtaining aluminas from the thermal decomposition of their different precursors: An {sup 27}Al MAS NMR and X-ray powder diffraction studies

    Energy Technology Data Exchange (ETDEWEB)

    Chagas, L.H.; De Carvalho, G.S.G. [Universidade Federal de Juiz de Fora, Departamento de Química, Grupo de Físico-Química de Sólidos e Interfaces, 36036-330 Juiz de Fora, MG (Brazil); San Gil, R.A.S. [Universidade Federal do Rio de Janeiro, Instituto de Química, 21949-900 Rio de Janeiro, RJ (Brazil); Chiaro, S.S.X. [PETROBRAS-CENPES, 21941-915 Rio de Janeiro, RJ (Brazil); Leitão, A.A. [Universidade Federal de Juiz de Fora, Departamento de Química, Grupo de Físico-Química de Sólidos e Interfaces, 36036-330 Juiz de Fora, MG (Brazil); Diniz, R., E-mail: renata.diniz@ufjf.edu.br [Universidade Federal de Juiz de Fora, Departamento de Química, Grupo de Físico-Química de Sólidos e Interfaces, 36036-330 Juiz de Fora, MG (Brazil)

    2014-01-01

    Graphical abstract: - Highlights: • We synthesized three precursors of alumina from different methods. • The calcination of the precursors generated several alumina polymorphs. • XRD and NMR were used for structural investigation of the polymorphs. • The synthesis route determines the structural and textural properties of the solids. - Abstract: A commercial sample of Boehmite was used as precursor of alumina polymorphs. For comparison, three other precursors were synthesized from different methods. Particularly, the use of excess of urea promoted a very crystalline form of basic aluminum carbonate. The characteristics of the four precursors were investigated by thermal, vibrational and X-ray powder diffraction (XRD) analysis. Additionally, the nuclear magnetic resonance, with magic angle spinning ({sup 27}Al MAS NMR), was used to verify the coordination of aluminum cations. Each precursor was calcined at various temperatures generating alumina polymorphs, which were structurally analyzed by XRD and {sup 27}Al MAS NMR. Due to interest in catalysis supports, special attention was given to the γ-Al{sub 2}O{sub 3} phase, which in addition to structural investigation was subjected to textural analysis. The results showed that, from different synthesis procedures and common route of calcination, one can obtain materials with the same composition but with different structural and textural properties, which in turn can significantly influence the performance of a supported catalyst.

  13. Phase transformation and magnetic properties of MnAl powders prepared by elemental-doping and salt-assisted ball milling

    Science.gov (United States)

    Qian, Hui-Dong; Si, Ping-Zhan; Choi, Chul-Jin; Park, Jihoon; Cho, Kyung Mox

    2018-05-01

    The effects of elemental doping of Si and Fe on the ɛ→τ phase transformation and the magnetic properties of MnAl were studied. The magnetic powders of Si- and Fe-doped MnAl were prepared by using induction melting followed by water-quenching, annealing, and salt-assisted ball-milling. The Fe-doped MnAl powders are mainly composed of the L10-structured τ-phase, while the Si-doped MnAl are composed of τ-phase and a small fraction of γ2- and β-phases. A unique thin leaves-like morphology with thickness of several tens of nanometers and diameter size up to 500 nm were observed in the Si-doped MnAl powders. The Fe-doped MnAl powders show irregular shape with much larger dimensions in the range from several to 10 μm. The morphology difference of the samples was ascribed to the variation of the mechanical properties affected by different doping elements. The phase transformation temperatures of the ɛ-phase of the samples were measured. The doping of Fe decreases the onset temperature of the massive phase transformation in MnAl, while the Si-doping increases the massive phase transformation temperature. Both Fe and Si increase the Curie temperature of MnAl. A substantially enhanced coercivity up to 0.45 T and 0.42 T were observed in the ball-milled MnAl powders doped with Si and Fe, respectively.

  14. Line profile analysis of ODS steels Fe20Cr5AlTiY milled powders at different Y2O3 concentrations

    Science.gov (United States)

    Afandi, A.; Nisa, R.; Thosin, K. A. Z.

    2017-04-01

    Mechanical properties of material are largely dictated by constituent microstructure parameters such as dislocation density, lattice microstrain, crystallite size and its distribution. To develop ultra-fine grain alloys such as Oxide Dispersion Strengthened (ODS) alloys, mechanical alloying is crucial step to introduce crystal defects, and refining the crystallite size. In this research the ODS sample powders were mechanically alloyed with different Y2O3 concentration respectively of 0.5, 1, 3, and 5 wt%. MA process was conducted with High Energy Milling (HEM) with the ball to powder ratio of 15:1. The vial and the ball were made of alumina, and the milling condition is set 200 r.p.m constant. The ODS powders were investigated by X-Ray Diffractions (XRD), Bragg-Brentano setup of SmartLab Rigaku with 40 KV, and 30 mA, step size using 0.02°, with scanning speed of 4°min-1. Line Profile Analysis (LPA) of classical Williamson-Hall was carried out, with the aim to investigate the different crystallite size, and microstrain due to the selection of the full wide at half maximum (FWHM) and integral breadth.

  15. Colloidal Precursors from 'Ball-Milling in Liquid Medium' Process for CuInSe2 Thin Film

    International Nuclear Information System (INIS)

    Chung, Jae Hoon; Kim, Seung Joo

    2010-01-01

    CIS thin film can be fabricated by using the precursor obtained through ball-milling the elemental reagents in liquid media. The amorphous colloidal precursor with good dispersity was prepared in the medium that contains strong base and polar solvent (2 M ethylenediamine in DMF solution as used in this study). The 'ball-milling in liquid medium' method requires only elemental sources as starting materials and a proper solution so that it can be employed without additional processes for separation and purification. As a simple and less-toxic preparative route, this method would be practically available to prepare CIS-related solar cells. CuInSe 2 (CIS) and related chalcopyrite compounds are very promising materials for thin film solar cells due to their favorable band gap, high optical absorption coefficient and long-term stability. CIS-based solar cells have shown the highest conversion efficiency reaching a value of 20%. However, the vacuum-based processes that are used to fabricate CIS thin-films have some drawbacks such as the complexity in process, high production cost and difficulty in scaling up. Recently, several research groups have proposed different non-vacuum deposition processes for CIS solar cell. For example, H. W. Hillhouse et al. prepared the CIS absorber layer by using 'nanocrystal ink method' in which a colloidal nanocrystal ink was obtained from reaction of CuCl, InCl 3 and Se in oleylamine. D. B. Mitzi et al. used a solution-based precursor that was prepared by dissolution of Cu 2 Se, In 2 Se 3 , Ga 2 Se 3 and Se in hydrazine to fabricate the Ga-containing absorber layer, Cu(In,Ga)Se 2

  16. Anisotropy of the critical current in MgB2 tapes made of high energy milled precursor powder

    DEFF Research Database (Denmark)

    Hässler, W.; Kovac, P.; Eisterer, M.

    2010-01-01

    For applications of MgB2 wires or tapes, high critical currents in high magnetic fields are essential. By using tapes in superconducting coils the anisotropic behaviour of the critical current, i.e. the dependence on the direction of the external field in relation to the tape surface, has to be t...

  17. Obtention of the TiFe compound by high-energy milling of Ti+Fe and TiH{sub 2}+Fe powder mixtures; Obtencao do composto TiFe a partir da moagem de alta energia de misturas Ti+Fe e TiH{sub 2}+Fe

    Energy Technology Data Exchange (ETDEWEB)

    Falcao, R.B.; Dammann, E.D.C.C.; Rocha, C.J.; Leal Neto, R.M., E-mail: railson.falcao@usp.b [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil). Centro de Ciencias e Tecnologia de Materiais. Lab. de Intermetalicos

    2010-07-01

    In this work TiFe compound was obtained by two process routes involving high-energy ball milling: mechanical alloying from Ti and Fe powders (route 1) and mechanical milling from TiH{sub 2} and Fe powders, both followed by an annealing heat treatment. Shaker and planetary ball mills were utilized for times varying from 1-25 hours. Milled and annealed powders were characterized by SEM and X-ray diffraction analyses. TiFe compound was formed in both routes. A strong powder adherence in the milling vial and balls occurred with route 1 in both mills. Powder adherence was significantly reduced by using TiH{sub 2} (route 2) mainly in the planetary mill, in spite of TiFe formation has only occurred after the annealing treatment. (author)

  18. Phase evolution during early stages of mechanical alloying of Cu–13 wt.% Al powder mixtures in a high-energy ball mill

    International Nuclear Information System (INIS)

    Dudina, Dina V.; Lomovsky, Oleg I.; Valeev, Konstantin R.; Tikhov, Serguey F.; Boldyreva, Natalya N.; Salanov, Aleksey N.; Cherepanova, Svetlana V.; Zaikovskii, Vladimir I.; Andreev, Andrey S.; Lapina, Olga B.; Sadykov, Vladislav A.

    2015-01-01

    Highlights: • Phase formation during early stages of Cu–Al mechanical alloying was studied. • The products of mechanical alloying are of highly non-equilibrium character. • X-ray amorphous phases are present in the products of mechanical alloying. • An Al-rich X-ray amorphous phase is distributed between the crystallites. - Abstract: We report the phase and microstructure evolution of the Cu–13 wt.% Al mixture during treatment in a high-energy planetary ball mill with a particular focus on the early stages of mechanical alloying. Several characterization techniques, including X-ray diffraction phase analysis, nuclear magnetic resonance spectroscopy, differential dissolution, thermal analysis, and electron microscopy/elemental analysis, have been combined to study the evolution of the phase composition of the mechanically alloyed powders and describe the microstructure of the multi-phase products of mechanical alloying at different length scales. The following reaction sequence has been confirmed: Cu + Al → CuAl 2 (+Cu) → Cu 9 Al 4 + (Cu) → Cu(Al). The phase evolution was accompanied by the microstructure changes, the layered structure of the powder agglomerates disappearing with milling time. This scheme is further complicated by the processes of copper oxidation, reduction of copper oxides by metallic aluminum, and by variation of the stoichiometry of Cu(Al) solid solutions with milling time. Substantial amounts of X-ray amorphous phases were detected as well. Differential dissolution technique has revealed that a high content of aluminum in the Cu(Al) solid solution-based powders is due to the presence of Al-rich phases distributed between the Cu(Al) crystallites

  19. Synthesis of Ti3AlC2 by spark plasma sintering of mechanically milled 3Ti/xAl/2C powder mixtures

    International Nuclear Information System (INIS)

    Yang Chen; Jin Songzhe; Liang Baoyan; Liu Guojun; Duan Lianfeng; Jia Shusheng

    2009-01-01

    Elemental powders of Ti, Al and C were mechanically milled as starting materials for the fabrication of ternary carbide Ti 3 AlC 2 by spark plasma sintering (SPS) technique. The effect of Al content in the starting materials on the Ti 3 AlC 2 synthesis was investigated. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were employed to determine the phase identification and observe the microstructure of the synthesized samples. With increasing proper Al content, it was found that the purity of Ti 3 AlC 2 increased and the sintering temperature reduced. The dense and high-purity Ti 3 AlC 2 could be successfully fabricated from 3Ti/1.2Al/2C powders at a lower sintering temperature of 1050 deg. C, holding for 10 min. In addition, the reaction path for the formation of Ti 3 AlC 2 in the present study was proposed

  20. Characterization of high-energy milled alumina powders Caracterização de pós de alumina submetidos a moagem de alta energia

    Directory of Open Access Journals (Sweden)

    Roberto Tomasi

    1998-10-01

    Full Text Available The utilization of reactive high-energy milling has been reported for the synthesis of ceramic powders namely, metal oxides, carbides, borides, nitrides or mixtures of ceramics or ceramic and metal compounds. In this work, high-energy milling was used for reduction of alumina powders to nanometric particle size. The ceramic characteristics of the powders were analyzed in terms of the behavior during deagglomeration, compaction curves, sintering and microstructure characterization. It was observed that the high energy milling has strong effect in producing agglomeration of the nanosized powders. This effect is explained by the high-energy impact of the balls, which may fracture particles or just cause the particles compacting. In this case, strong agglomerates are produced. As the powder surface area increases, stronger agglomerates are produced.Tem sido amplamente divulgada a utilização da moagem reativa de alta energia para a síntese de pós cerâmicos de óxidos de metais, carbetos, boretos, nitretos ou misturas de compostos cerâmicos ou compostos cerâmicos e metálicos. Neste trabalho, a moagem de alta energia (não reativa foi utilizada para a redução de pós de alumina para partículas de dimensões nanométricas. As características cerâmicas dos pós obtidos foram analisadas a partir de resultados de comportamento durante a desaglomeração, curvas de densificação, sinterização e caracterização de microestrutura. Observou-se que a moagem de alta energia tem forte efeito de aglomeração dos pós com partículas em dimensões nanométricas. Esse efeito é explicado pelo impacto de alta energia das bolas, os quais podem fraturar as partículas ou apenas causar a compactação das mesmas. Nesse último caso, que sempre ocorre, são formados aglomerados de alta resistência. O aumento da área superficial do pó produz aglomerados mais resistentes.

  1. The reduction of optimal heat treatment temperature and critical current density enhancement of ex situ processed MgB2 tapes using ball milled filling powder

    Science.gov (United States)

    Fujii, Hiroki; Iwanade, Akio; Kawada, Satoshi; Kitaguchi, Hitoshi

    2018-01-01

    The optimal heat treatment temperature (Topt) at which best performance in the critical current density (Jc) property at 4.2 K is obtained is influenced by the quality or reactivity of the filling powder in ex situ processed MgB2 tapes. Using a controlled fabrication process, the Topt decreases to 705-735 °C, which is lower than previously reported by more than 50 °C. The Topt decrease is effective to suppress both the decomposition of MgB2 and hence the formation of impurities such as MgB4, and the growth of crystallite size which decreases upper critical filed (Hc2). These bring about the Jc improvement and the Jc value at 4.2 K and 10 T reaches 250 A/mm2. The milling process also decreases the critical temperature (Tc) below 30 K. The milled powder is easily contaminated in air and thus, the Jc property of the contaminated tapes degrades severely. The contamination can raise the Topt by more than 50 °C, which is probably due to the increased sintering temperature required against contaminated surface layer around the grains acting as a barrier.

  2. Microstructural study of Ce1-xGdxO2-δ (x = 0.1 and 0.2) nano crystallized powders synthesized by the polymeric precursor method

    International Nuclear Information System (INIS)

    Cela, B.; Macedo, D.A.; Souza, G.L.; Paskocimas, C.A.; Martinelli, A.E.; Nascimento, R.M.

    2009-01-01

    Gadolinia-doped ceria powders (Ce 1-x Gd x O 2-δ ) were prepared with substitution of 10 and 20% of the dopant element by the polymeric precursor method. This method makes possible the attainment of homogeny powder in molecular level, ideal to application in Solid Oxide Fuel Cell (SOFC) component. In this work, the particulated materials were calcinated in a range from 500 °C to 900 °C and structurally characterized by X-Ray Diffraction (XRD). The sintering behaviors of the compact samples were determined by dilatometric analyses. The results showed the method efficiency to attain monophasic nanopowder with cubic crystalline structure starting at 700 °C. The crystallite average size and crystalline parameter were determined by the Rietveld refinement method. (author)

  3. Study of magnetic properties of nano-powders prepared by pyrite -> troilite transformation via high energy milling

    DEFF Research Database (Denmark)

    Balaz, P.; Alacova, A.; Godocikova, E.

    2004-01-01

    The preparation of nanocrystalline troilite by high-energy milling of FeS2 sulphide with elemental Fe acting as reducing element is reported. X-ray difractometry was used in order to determine the presence of different phases in investigated samples. This technique allowed us to identify the form......-->troilite transformation is almost finished already after 25 minutes of high-energy milling.......The preparation of nanocrystalline troilite by high-energy milling of FeS2 sulphide with elemental Fe acting as reducing element is reported. X-ray difractometry was used in order to determine the presence of different phases in investigated samples. This technique allowed us to identify...

  4. Microstructural analysis of sinterized aluminum powder obtained by the high energy milling of beverage cans; Analise microestrutural de po de aluminio sinterizado obtido pela moagem de alta energia de latas de bebidas

    Energy Technology Data Exchange (ETDEWEB)

    Souza, Jose Raelson Pereira de; Peres, Mauricio Mhirdaui, E-mail: mauricioperes@ct.ufrn.br [Universidade Federal do Rio Grande do Norte (UFRN), RN (Brazil)

    2016-07-01

    The objective is the study of the effect of high energy milling on the sintering of aluminum from beverage cans. The selected aluminum cans were cut and subjected to high energy milling under a common atmosphere (in the air). In milling, three grams of aluminum was used to maintain the ratio of 10/1 between the mass of the beads and the material. The milling time was varied in 1h, 1.5h and 2h, keeping the other variables constant. The particle size distribution was measured by laser granulometry, for further compaction and sintering at a temperature of 600 ° C for 2 h. The samples were characterized by scanning electron microscopy (SEM). The granulometric analysis of the powders found that higher milling times produced finer particles. Powders with granulometry of less than 45 μm were obtained at 1 h, 1.5 h and 2 h times. The times of 1.5h and 2h promoted finer particles with better distribution of size. The SEM analyzes showed little variation in the shape of the particles as a function of the variation of the grinding times, presenting irregularities in the platelet geometry. The sintering time and temperature were effective in the densification of the powder particles, which were influenced by the average particle size.

  5. Mechanical milling of a nano structured ductile iron powder under dry, wet and cryogenic atmospheres; Proceso de molturacion mecanica en medio seco, humedo y criogenico de polvo de hierro ductil nanoestructurado

    Energy Technology Data Exchange (ETDEWEB)

    Cinca, N.; Hurtado, E.; Cano, I. G.; Guilemany, J. M.

    2011-07-01

    The main objective of this study, is to obtain an effective particle and grain size reduction of a nano structured iron powder by mechanical milling under different milling media. One of the main challenges in this study is to work with this material of great ductility.The variables of the study to be optimized have been the following: speed of rotation, powder to ball ratio (PBR) and the percentage of control agent to induce an effective powder fracturing in front of cold welding. The powder has been characterized by a Laser Diffraction Particle Size Analyser, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) and, X-ray diffraction.Through the comparative study, it is found that operating under dry milling conditions: there is a more effective particle size reduction of 43 % and grain size reduction of 62 %. In wet conditions has been reduced the amount of oxide, as well as to obtain a more homogenous distribution of the resulting powder. The results under cryogenic media is presented as promising. (Author) 15 refs.

  6. Enhancement of Antioxidant Mechanisms and Reduction of Oxidative Stress in Chickens after the Administration of Drinking Water Enriched with Polyphenolic Powder from Olive Mill Waste Waters

    Directory of Open Access Journals (Sweden)

    Aliki Papadopoulou

    2017-01-01

    Full Text Available The aim of the study was to examine the effects of a polyphenolic powder from olive mill wastewater (OMWW administered through drinking water, on chickens’ redox status. Thus, 75 chickens were divided into three groups. Group A was given just drinking water, while groups B and C were given drinking water containing 20 and 50 μg/ml of polyphenols, respectively, for 45 days. The antioxidant effects of the polyphenolic powder were assessed by measuring oxidative stress biomarkers in blood after 25 and 45 days of treatment. These markers were total antioxidant capacity (TAC, protein carbonyls (CARB, thiobarbituric acid reactive species (TBARS and superoxide dismutase activity (SOD in plasma, and glutathione (GSH and catalase activity in erythrocytes. The results showed that CARB and TBARS were decreased significantly in groups B and C, and SOD decreased in group B compared to that in group A. TAC was increased significantly in group C and GSH was increased in group B, while catalase activity was increased in groups B and C compared to that in group A. In conclusion, this is the first study showing that supplementation of chickens with polyphenols from OMWW through drinking water enhanced their antioxidant mechanisms and reduced oxidative stress-induced damage.

  7. Enhancement of Antioxidant Mechanisms and Reduction of Oxidative Stress in Chickens after the Administration of Drinking Water Enriched with Polyphenolic Powder from Olive Mill Waste Waters.

    Science.gov (United States)

    Papadopoulou, Aliki; Petrotos, Konstantinos; Stagos, Dimitrios; Gerasopoulos, Konstantinos; Maimaris, Antonios; Makris, Haralampos; Kafantaris, Ioannis; Makri, Sotiria; Kerasioti, Efthalia; Halabalaki, Maria; Brieudes, Vincent; Ntasi, Georgia; Kokkas, Stylianos; Tzimas, Pavlos; Goulas, Panagiotis; Zakharenko, Alexander M; Golokhvast, Kirill S; Tsatsakis, Aristidis; Kouretas, Demetrios

    2017-01-01

    The aim of the study was to examine the effects of a polyphenolic powder from olive mill wastewater (OMWW) administered through drinking water, on chickens' redox status. Thus, 75 chickens were divided into three groups. Group A was given just drinking water, while groups B and C were given drinking water containing 20 and 50  μ g/ml of polyphenols, respectively, for 45 days. The antioxidant effects of the polyphenolic powder were assessed by measuring oxidative stress biomarkers in blood after 25 and 45 days of treatment. These markers were total antioxidant capacity (TAC), protein carbonyls (CARB), thiobarbituric acid reactive species (TBARS) and superoxide dismutase activity (SOD) in plasma, and glutathione (GSH) and catalase activity in erythrocytes. The results showed that CARB and TBARS were decreased significantly in groups B and C, and SOD decreased in group B compared to that in group A. TAC was increased significantly in group C and GSH was increased in group B, while catalase activity was increased in groups B and C compared to that in group A. In conclusion, this is the first study showing that supplementation of chickens with polyphenols from OMWW through drinking water enhanced their antioxidant mechanisms and reduced oxidative stress-induced damage.

  8. Obtaining beta phase in Ti through processing in high energy mill powders of Ti and Nb; Obtencao de fase beta no Ti atraves de processamento em moinho de alta energia de pos de Ti e Nb

    Energy Technology Data Exchange (ETDEWEB)

    Milanez, Mateus; Ferretto, Aline; Rocha, Marcio Roberto da; Arnt, Angela Coelho [Universidade do Extremo Sul Catarinense (UNESC), Criciuma, SC (Brazil). Departamento de Engenharia de Materiais; Milanez, Alexandre [Faculdade SATC (FASATC), Criciuma, SC (Brazil). Departamento de Engenharia Mecanica; Schaeffer, Lirio [Universidade Federal do Rio Grande do Sul (LdTM/UFRGS), RS (Brazil). Lab. de Transformacao Mecanica

    2014-07-01

    An orthopedic implant, ideal, must meet the requirements of biocompatibility, have good mechanical properties among others. Titanium and Niobium exhibit biocompatibility and the β-Ti phase relationships have the highest strength / weight among all titanium alloys, presenting lower values of elastic modulus. The alloy has mechanically produced specific microstructural characteristics and improved mechanical properties compared with conventional powder metallurgy. In this study, a titanium alloy with different additions of niobium was used. The metal powders were mixed via mechanical alloy in high energy mill (attritor). The powder samples were analyzed by X-ray diffraction (X-RD) and property held by adhesive wear testing with a Pin-on-Disk. The present study revealed that through the high-energy milling is possible the atomic interaction between Ti and Nb particles and the mechanical properties are affected by the concentration of Nb. (author)

  9. Normal and abnormal grain growth in fine-grained Nd-Fe-B sintered magnets prepared from He jet milled powders

    Energy Technology Data Exchange (ETDEWEB)

    Bittner, F., E-mail: f.bittner@ifw-dresden.de [IFW Dresden, Institute for Metallic Materials, PO Box 270116, 01171 Dresden (Germany); Technische Universität Dresden, Institute of Materials Science, 01062 Dresden (Germany); Woodcock, T.G. [IFW Dresden, Institute for Metallic Materials, PO Box 270116, 01171 Dresden (Germany); Schultz, L. [IFW Dresden, Institute for Metallic Materials, PO Box 270116, 01171 Dresden (Germany); Technische Universität Dresden, Institute of Materials Science, 01062 Dresden (Germany); Schwöbel, C. [Technische Universität Darmstadt, Materialwissenschaft, Alarich-Weiß-Str. 16, 64287 Darmstadt (Germany); Gutfleisch, O. [Technische Universität Darmstadt, Materialwissenschaft, Alarich-Weiß-Str. 16, 64287 Darmstadt (Germany); Fraunhofer ISC, Projektgruppe für Werkstoffkreisläufe und Ressourcenstrategie IWKS, Rodenbacher Chaussee 4, 63457 Hanau (Germany); Zickler, G.A.; Fidler, J. [Technische Universität Wien, Institute of Solid State Physics, Wiedner Hauptstr. 8-10, 1040 Wien (Austria); Üstüner, K.; Katter, M. [Vacuumschmelze GmbH & Co. KG, 63412 Hanau (Germany)

    2017-03-15

    Fine-grained, heavy rare earth free Nd-Fe-B sintered magnets were prepared from He jet milled powders with an average particle size of 1.5 µm by low temperature sintering at 920 °C or 980 °C. A coercivity of >1600 kA/m was achieved for an average grain size of 1.68 µm. Transmission electron microscopy showed that the distribution and composition of intergranular and grain boundary junction phases was similar to that in conventionally processed magnets. Microstructural analysis on different length scales revealed the occurrence of abnormal grain growth, which is unexpected for sintering temperatures below 1000 °C. A larger area fraction of abnormal grains was observed in the sample sintered at 920 °C compared to that sintered at 980 °C. Microtexture investigation showed a better crystallographic alignment of the abnormal grains compared to the fine-grained matrix, which is explained by a size dependent alignment of the powder particles during magnetic field alignment prior to sintering. Slightly larger particles in the initial powder show a better alignment and will act as nucleation sites for abnormal grain growth. Magneto-optical Kerr investigations confirmed the lower switching field of the abnormal grains compared to the fine-grained matrix. The demagnetisation curve of the sample sintered at 920 °C showed reduced rectangularity and this was attributed to a cooperative effect of the larger fraction of abnormal grains with low switching field and, as a minor effect, a reduced degree of crystallographic texture in this sample compared to the material sintered at 980 °C, which did not show the reduced rectangularity of the demagnetisation curve. - Highlights: • He Jet milling to reduce Nd-Fe-B grain size and to enhance coercivity. • Normal and abnormal grain growth observed for low temperature sintering. • Well oriented abnormal grown grains explained by size dependent field alignment. • Poor rectangularity is caused by low nucleation field of

  10. Normal and abnormal grain growth in fine-grained Nd-Fe-B sintered magnets prepared from He jet milled powders

    International Nuclear Information System (INIS)

    Bittner, F.; Woodcock, T.G.; Schultz, L.; Schwöbel, C.; Gutfleisch, O.; Zickler, G.A.; Fidler, J.; Üstüner, K.; Katter, M.

    2017-01-01

    Fine-grained, heavy rare earth free Nd-Fe-B sintered magnets were prepared from He jet milled powders with an average particle size of 1.5 µm by low temperature sintering at 920 °C or 980 °C. A coercivity of >1600 kA/m was achieved for an average grain size of 1.68 µm. Transmission electron microscopy showed that the distribution and composition of intergranular and grain boundary junction phases was similar to that in conventionally processed magnets. Microstructural analysis on different length scales revealed the occurrence of abnormal grain growth, which is unexpected for sintering temperatures below 1000 °C. A larger area fraction of abnormal grains was observed in the sample sintered at 920 °C compared to that sintered at 980 °C. Microtexture investigation showed a better crystallographic alignment of the abnormal grains compared to the fine-grained matrix, which is explained by a size dependent alignment of the powder particles during magnetic field alignment prior to sintering. Slightly larger particles in the initial powder show a better alignment and will act as nucleation sites for abnormal grain growth. Magneto-optical Kerr investigations confirmed the lower switching field of the abnormal grains compared to the fine-grained matrix. The demagnetisation curve of the sample sintered at 920 °C showed reduced rectangularity and this was attributed to a cooperative effect of the larger fraction of abnormal grains with low switching field and, as a minor effect, a reduced degree of crystallographic texture in this sample compared to the material sintered at 980 °C, which did not show the reduced rectangularity of the demagnetisation curve. - Highlights: • He Jet milling to reduce Nd-Fe-B grain size and to enhance coercivity. • Normal and abnormal grain growth observed for low temperature sintering. • Well oriented abnormal grown grains explained by size dependent field alignment. • Poor rectangularity is caused by low nucleation field of

  11. Liquid phase surface melting of AA8011 aluminum alloy by addition of Al/Al{sub 2}O{sub 3} nano-composite powders synthesized by high-energy milling

    Energy Technology Data Exchange (ETDEWEB)

    Sohi, M. Heydarzadeh [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran (Iran, Islamic Republic of); Hojjatzadeh, S.M.H., E-mail: Hojatzadeh@yahoo.com [Department of Welding, Science and Research Branch, Azad University, Tehran (Iran, Islamic Republic of); Moosavifar, Sh. S.; Heshmati-Manesh, S. [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran (Iran, Islamic Republic of)

    2014-09-15

    Highlights: • Aluminum matrix composite layers reinforced with alumina particles were fabricated. • Non milled powders caused porosity in the microstructures because of poor wettability. • The ball milling of powders was significantly improved the wettability of nano ceramic particles. • The micro hardness of the layers was approximately 3 times greater than that of the base metal. - Abstract: Poor wettability of particles is an obstacle in formation of sound composite layer via surface melting. Pre-coating of particles with metallic material by different techniques, such as ball milling may enhance the wettability of the particles with molten metal. In this study, composite surface layers containing Al{sub 2}O{sub 3} particles were fabricated on the surface of AA8011 aluminum substrates by tungsten inert gas (TIG) surface melting using preplaced layers of Al/Al{sub 2}O{sub 3} powder mixtures in two different forms: (1) a mixture of 40 wt% Al and 60 wt% of 50 nm Al{sub 2}O{sub 3} powders and (2) a mixture obtained by mechanical alloying of 40 wt% Al and 60 wt% of 60 μm Al{sub 2}O{sub 3} powders. Morphology evolution of powders during ball milling and the microstructure of the fabricated composite layers were studied through conventional characterization techniques, such as optical microscopy, scanning electron microscopy (SEM), and X-ray diffraction (XRD). Microhardness measurements were also performed across the alloyed zone. The results indicated that the layer fabricated by the second route showed a defect free structure with a more uniform distribution of Al{sub 2}O{sub 3} particles in comparison with the layer obtained by the first route. It was also noticed that the uniform dispersion of Al{sub 2}O{sub 3} particles in the fabricated layer increased the hardness to 133 HV which was over 3 times of that of the base metal.

  12. Effect of the calcining temperature on the porosity of the titanium dioxide powders obtained by Polymeric Precursor Method

    International Nuclear Information System (INIS)

    Silva, D.W.; Granado, S.R.; Ciola, R.A.; Cavalheiro, A.A.

    2011-01-01

    Ceramics materials obtained by Polymeric Precursor Method exhibit mechanisms of the pore formation and elimination dependents on the decomposition kinetics of the residual organic matter of the polyester. The mechanism of pore elimination seems to occur by disrupting of the wall among the pores because it leads to the consequent pore coalescence and increasing in pore volume, which posses higher pore diameters. In this case, it was observed that the porosity decreasing occurs by pore wall moving after that the residual organic matter is eliminated from the pore inside. The pore diameter associated to the highest volume desorption occurred for the material obtained after calcining at 450°C is approximately 1,7 nm, what seems to be related to the amorphous carbon accumulated inside the pores, once that the pore volume decreases more effectively for the material obtained by calcining at 550°C, making the maximum volume situates at 2,0 nm. (author)

  13. CH3 NH3 PbI3 and HC(NH2 )2 PbI3 Powders Synthesized from Low-Grade PbI2 : Single Precursor for High-Efficiency Perovskite Solar Cells.

    Science.gov (United States)

    Zhang, Yong; Kim, Seul-Gi; Lee, Do-Kyoung; Park, Nam-Gyu

    2018-05-09

    High-efficiency perovskite solar cells are generally fabricated by using highly pure (>99.99 %) PbI 2 mixed with an organic iodide in polar aprotic solvents. However, the use of such an expensive chemical may impede progress toward large-scale industrial applications. Here, we report on the synthesis of perovskite powders by using inexpensive low-grade (99 %) PbI 2 and on the photovoltaic performance of perovskite solar cells prepared from a powder-based single precursor. Pure APbI 3 [A=methylammonium (MA) or formamidinium (FA)] perovskite powders were synthesized by treating low-grade PbI 2 with MAI or FAI in acetonitrile at ambient temperature. The structural phase purity was confirmed by X-ray diffraction. The solar cell with a MAPbI 3 film prepared from the synthesized perovskite powder demonstrated a power conversion efficiency (PCE) of 17.14 %, which is higher than the PCE of MAPbI 3 films prepared by using both MAI and PbI 2 as precursors (PCE=13.09 % for 99 % pure PbI 2 and PCE=16.39 % for 99.9985 % pure PbI 2 ). The synthesized powder showed better absorption and photoluminescence, which were responsible for the better photovoltaic performance. For the FAPbI 3 powder, a solution with a yellow non-perovskite δ-FAPbI 3 powder synthesized at room temperature was found to lead to a black perovskite film, whereas a solution with the black perovskite α-FAPbI 3 powder synthesized at 150 °C was not transformed into a black perovskite film. The α↔δ transition between the powder and film was assumed to correlate with the difference in the iodoplumbates in the powder-dissolved solution. An average PCE of 17.21 % along with a smaller hysteresis [ΔPCE=PCE reverse -PCE forward )=1.53 %] was demonstrated from the perovskite solar cell prepared by using δ-FAPbI 3 powder; this PCE is higher than the average PCE of 17.05 % with a larger hysteresis (ΔPCE=2.71 %) for a device based on a conventional precursor solution dissolving MAI with high

  14. Thermal behavior and phase transformation of ZrO2–10%SiO2 precursor powder prepared by a co-precipitation route without adding stability agent

    International Nuclear Information System (INIS)

    Chu, Hsueh-Liang; Hwang, Weng-Sing; Wang, Cheng-Li; Wang, Moo-Chin; Lee, Kuen-Chan; Huang, Hong-Hsin; Lee, Huey-Er

    2014-01-01

    Highlights: • The precursor powders contained about 68.3 wt% ZrO 2 , which corresponds to ZrO 2 ·1/8 H 2 O. • The exothermic peak temperature of tetragonal ZrO 2 formation occurred at 1014 K. • The activation energy of ZrO 2 –10%SiO 2 precursors crystallization is 993.7 kJ/mol. • Only the tetragonal ZrO 2 formed when the precursor calcined at 1173–1373 K for 2 h. • As calcined at 1473 K for 2 h, tetragonal ZrO 2 fully converted to monoclinic ZrO 2 . - Abstract: Thermal behavior and phase transformation of ZrO 2 –10%SiO 2 precursor powder prepared by a co-precipitation route without adding stability agent has been studied using different thermal analysis/thermogravimetry (DTA/TG), X-ray diffraction (XRD), transmission electron microscopy (TEM), selected area electron diffraction (SAED), nano beam electron diffraction (NBED), high-resolution TEM (HRTEM) and energy-dispersive X-ray spectrometer (EDS). The TG results show that four weight loss regions were from 298 to 443 K, 443 to 743 K, 743 to 793 K and 793 to 1400 K. The DTA result shows that the ZrO 2 freeze-dried precursor powders crystallization at 1014 K. The activation energy of 993.7 kJ/mol was obtained for tetragonal ZrO 2 crystallization using a non-isothermal process. The XRD result shows that only a single phase of tetragonal ZrO 2 appears when the freeze-dried precursor powders after calcination between 1173 and 1373 K for 2 h. Moreover, when calcined at 1473 K for 2 h, the phase transformation from tetragonal ZrO 2 fully converted to monoclinic ZrO 2 occurred

  15. Growth kinetics of tetragonal and monoclinic ZrO{sub 2} crystallites in 3 mol% yttria partially stabilized ZrO{sub 2} (3Y-PSZ) precursor powder

    Energy Technology Data Exchange (ETDEWEB)

    Kuo, Chih-Wei [Department of Resources Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Lee, Kuen-Chan [Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 807, Taiwan (China); Yen, Feng-Lin, E-mail: flyen@kmu.edu.tw [Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 807, Taiwan (China); Shen, Yun-Hwei [Department of Resources Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Lee, Huey-Er [Department of Dentistry, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 807, Taiwan (China); Department of Dentistry, Kaohsiung Medical University, Chung Ho Memorial Hospital, 100 Tzyou 1st Road, Kaohsiung 807, Taiwan (China); Wen, Shaw-Bing [General Education Center, Meiho Institute of Technology, 23 Pingguang Road, Neipu, Pingtung 91202, Taiwan (China); Wang, Moo-Chin, E-mail: mcwang@kmu.edu.tw [Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 807, Taiwan (China); Stack, Margaret Mary [Department of Mechanical and Aerospace Engineering, University of Strathclyde, 75 Montrose Street, Glasgow (United Kingdom)

    2014-04-01

    Highlights: • The crystalline structures were composed of tetragonal and monoclinic ZrO{sub 2}. • Growth kinetics of t-ZrO{sub 2} in the 3Y-PSZ precursor powder is described as: D{sub te}{sup 2}=(4.57±0.55)t{sup 0.12±0.02}exp(-((24.79±0.38)×10{sup 3})/(RT) ). • Growth kinetics of m-ZrO{sub 2} in the 3Y-PSZ precursor powder is described as: D{sub m}{sup 2}=(4.40±1.63)t{sup 0.17±0.08}exp(-((66.47±3.97)×10{sup 3})/(RT) ). - Abstract: The growth kinetics of tetragonal and monoclinic ZrO{sub 2} crystallites in 3 mol% yttria partially stabilized ZrO{sub 2} (3Y-PSZ) precursor powder has been investigated using X-ray diffraction (XRD), Brunauer–Emmett–Teller (BET) specific surface area analysis, transmission electron microscopy (TEM) and high resolution TEM (HRTEM). After calcination of the 3Y-PSZ precursor powder between 773 and 1073 K for 2 h, the crystalline structures were composed of tetragonal and monoclinic ZrO{sub 2} as the primary and secondary phases, respectively. When the 3Y-PSZ precursor powder was calcined at 773 K for 2 h, the BET specific surface area was 97.13 m{sup 2}/g, which is equivalent to a particle size of 10.30 nm. The crystallite sizes determined via XRD and BET agreed well, indicating that the powder was virtually non-agglomerated. The growth kinetics of tetragonal and monoclinic ZrO{sub 2} crystallite isothermal growth in the 3Y-PSZ precursor powder are described by: D{sub te}{sup 2}=(4.57±0.55)t{sup 0.12±0.02}exp(-((24.79±0.38)×10{sup 3})/(RT) ) and D{sub m}{sup 2}=(4.40±1.63)t{sup 0.17±0.08}exp(-((66.47±3.97)×10{sup 3})/(RT) ), respectively, for 773K≤T≤1073K. D{sub te} and D{sub m} denote the crystallite size of tetragonal and monoclinic ZrO{sub 2} at time t and temperature T, respectively.

  16. Enhanced coagulation with powdered activated carbon or MIEX secondary treatment: a comparison of disinfection by-product formation and precursor removal.

    Science.gov (United States)

    Watson, Kalinda; Farré, Maria José; Knight, Nicole

    2015-01-01

    The removal of both organic and inorganic disinfection by-product (DBP) precursors prior to disinfection is important in mitigating DBP formation, with halide removal being particularly important in salinity-impacted water sources. A matrix of waters of variable alkalinity, halide concentration and dissolved organic carbon (DOC) concentration were treated with enhanced coagulation (EC) followed by anion exchange (MIEX resin) or powdered activated carbon (PAC) and the subsequent disinfection by-product formation potentials (DBP-FPs) assessed and compared to DBP-FPs for untreated samples. Halide and DOC removal were also monitored for both treatment processes. Bromide and iodide adsorption by MIEX treatment ranged from 0 to 53% and 4-78%, respectively. As expected, EC and PAC treatments did not remove halides. DOC removal by EC/PAC was 70 ± 10%, while EC/MIEX enabled a DOC removal of 66 ± 12%. Despite the halide removals achieved by MIEX, increases in brominated disinfection by-product (Br-DBP) formation were observed relative to untreated samples, when favourable Br:DOC ratios were created by the treatment. However, the increases in formation were less than what was observed for the EC/PAC treated waters, which caused large increases in Br-DBP formation when high Br-DBP-forming water quality conditions occurred. The formation potential of fully chlorinated DBPs decreased after treatment in all cases.

  17. From precursor powders to CsPbX3 perovskite nanowires. One-pot synthesis, growth mechanism, and oriented self-assembly

    International Nuclear Information System (INIS)

    Tong, Yu; Bohn, Bernhard J.; Urban, Alexander S.; Polavarapu, Lakshminarayana; Feldmann, Jochen; Bladt, Eva; Bals, Sara; Wang, Kun; Mueller-Buschbaum, Peter

    2017-01-01

    The colloidal synthesis and assembly of semiconductor nanowires continues to attract a great deal of interest. Herein, we describe the single-step ligand-mediated synthesis of single-crystalline CsPbBr 3 perovskite nanowires (NWs) directly from the precursor powders. Studies of the reaction process and the morphological evolution revealed that the initially formed CsPbBr 3 nanocubes are transformed into NWs through an oriented-attachment mechanism. The optical properties of the NWs can be tuned across the entire visible range by varying the halide (Cl, Br, and I) composition through subsequent halide ion exchange. Single-particle studies showed that these NWs exhibit strongly polarized emission with a polarization anisotropy of 0.36. More importantly, the NWs can self-assemble in a quasi-oriented fashion at an air/liquid interface. This process should also be easily applicable to perovskite nanocrystals of different morphologies for their integration into nanoscale optoelectronic devices. (copyright 2017 Wiley-VCH Verlag GmbH and Co. KGaA, Weinheim)

  18. From precursor powders to CsPbX{sub 3} perovskite nanowires. One-pot synthesis, growth mechanism, and oriented self-assembly

    Energy Technology Data Exchange (ETDEWEB)

    Tong, Yu; Bohn, Bernhard J.; Urban, Alexander S.; Polavarapu, Lakshminarayana; Feldmann, Jochen [Chair for Photonics and Optoelectronics, Department of Physics and Center for NanoScience (CeNS), Muenchen Univ. (Germany); Nanosystems Initiative Munich (NIM), Munich (Germany); Bladt, Eva; Bals, Sara [EMAT, University of Antwerp (Belgium); Wang, Kun; Mueller-Buschbaum, Peter [Department of Physics, Chair for Functional Materials, Technische Univ. Muenchen (Germany)

    2017-10-23

    The colloidal synthesis and assembly of semiconductor nanowires continues to attract a great deal of interest. Herein, we describe the single-step ligand-mediated synthesis of single-crystalline CsPbBr{sub 3} perovskite nanowires (NWs) directly from the precursor powders. Studies of the reaction process and the morphological evolution revealed that the initially formed CsPbBr{sub 3} nanocubes are transformed into NWs through an oriented-attachment mechanism. The optical properties of the NWs can be tuned across the entire visible range by varying the halide (Cl, Br, and I) composition through subsequent halide ion exchange. Single-particle studies showed that these NWs exhibit strongly polarized emission with a polarization anisotropy of 0.36. More importantly, the NWs can self-assemble in a quasi-oriented fashion at an air/liquid interface. This process should also be easily applicable to perovskite nanocrystals of different morphologies for their integration into nanoscale optoelectronic devices. (copyright 2017 Wiley-VCH Verlag GmbH and Co. KGaA, Weinheim)

  19. Structural and morphological characterization of TiO{sub 2}-ZrO{sub 2} powders obtained by the polymeric precursors method; Caracterizacao estrutural e morfologica de pos de TiO{sub 2}-ZrO{sub 2} obtidos pelo metodo dos precursores polimericos

    Energy Technology Data Exchange (ETDEWEB)

    Ribeiro, M.A.; Gama, L.; Bispo, A.; Neiva, L.S., E-mail: m_aparecidaribeiro@yahoo.com.b [Universidade Federal de Campina Grande (DEMa/UFCG), PB (Brazil). Dept. de Engenharia de Materiais; Bernardi, M.I.B. [Universidade de Sao Paulo (IFSC/USP), Sao Carlos, SP (Brazil). Inst. de Fisica; Kiminami, R.H.G.A. [Universidade Federal de Sao Carlos (DEMa/UFSCar), SP (Brazil). Dept. de Engenharia de Materiais

    2010-07-01

    This work aims to characterize the structure and morphology of TiO{sub 2}-ZrO{sub 2} powders obtained by polymeric precursor method. For this we studied the following compositions: 0.25, 0.5 and 0.75 moles of Zr and calcined at 800 deg C for one hour. The powders obtained were characterized by XRD, SEM and nitrogen adsorption (BET). The analysis of X-ray diffraction showed that the powders had a phase of TiO{sub 2} in the anatase form and a tetragonal phase of ZrO{sub 2}. The crystallite size was between 8, 13 and 11 nm respectively. The analysis of scanning electron microscopy showed the growth of ZrO{sub 2} nanoparticles and that these comprise spherical agglomerates of less than 100 nm. Particle size determined by the BET ranging 28.1-29.5 nm, showing thereby the character of nanosized powders. (author)

  20. The processing and characterization of animal-derived bone to yield materials with biomedical applications. Part II: milled bone powders, reprecipitated hydroxyapatite and the potential uses of these materials.

    Science.gov (United States)

    Johnson, G S; Mucalo, M R; Lorier, M A; Gieland, U; Mucha, H

    2000-11-01

    Further studies on the processing and use of animal-bone-derived calcium phosphate materials in biomedical applications are presented. Bone powders sourced either from the direct crushing and milling of bovine, ovine and cervine bone or after being subjected to defatting and acid digestion/NaOH reprecipitation and sodium hypochlorite hydrogen peroxide treatment of animal bones were characterized using Fourier transform infra-red (FTIR) spectroscopy, 13C solid state magic angle spinning (MAS) nuclear magnetic resonance (NMR) spectroscopy, atomic absorption (AA) and inductively coupled plasma (ICP) spectrometric techniques. Bone powders were trialled for their potential use as a substrate for phosphine coupling and enzyme immobilization as well as a feedstock powder for plasma spraying on titanium metal substrates. Results indicated that enzyme immobilization by phosphine coupling could be successfully achieved on milled cervine bone with the immobilized enzyme retaining some activity. It was found that the presence of impurities normally carried down with the processing of the bone materials (viz., fat and collagen) played an important role in influencing the adsorbency and reactivity of the powders. Plasma spraying studies using reprecipitated bovine-derived powders produced highly adherent coatings on titanium metal, the composition of which was mostly hydroxyapatite (Ca10(PO4)6(OH)2) with low levels of alpha-tricalcium phosphate (alpha-Ca3(PO4)2) and tetracalcium phosphate (Ca4P2O9) also detected. In general, animal derived calcium phosphate materials constitute a potentially cheaper source of calcium phosphate materials for biomedical applications and make use of a largely under-utilized resource from abattoir wastes. Copyright 2000 Kluwer Academic Publishers

  1. Thermal behavior and phase transformation of ZrO{sub 2}–10%SiO{sub 2} precursor powder prepared by a co-precipitation route without adding stability agent

    Energy Technology Data Exchange (ETDEWEB)

    Chu, Hsueh-Liang [Department of Materials Science and Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Hwang, Weng-Sing [Department of Materials Science and Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Institute of Nanotechnology and Microsystems Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Wang, Cheng-Li [Department of Materials Science and Engineering, National Cheng Kung University, 1 Ta-Hsueh Road, Tainan 70101, Taiwan (China); Wang, Moo-Chin, E-mail: mcwang@kmu.edu.tw [Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 80708, Taiwan (China); Lee, Kuen-Chan [Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 80708, Taiwan (China); Huang, Hong-Hsin [Department of Electrical Engineering, Cheng Shiu University, 840 Cheng Ching Road, Niaosong, Kaohsiung 83347, Taiwan (China); Lee, Huey-Er, E-mail: huerle@kmu.edu.tw [School of Dentistry, College of Dental Medicine, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 807, Taiwan (China); Department of Dentistry, Kaohsiung Medical University, 100 Tzyou 1st Road, Kaohsiung 807, Taiwan (China)

    2014-12-15

    Highlights: • The precursor powders contained about 68.3 wt% ZrO{sub 2}, which corresponds to ZrO{sub 2}·1/8 H{sub 2}O. • The exothermic peak temperature of tetragonal ZrO{sub 2} formation occurred at 1014 K. • The activation energy of ZrO{sub 2}–10%SiO{sub 2} precursors crystallization is 993.7 kJ/mol. • Only the tetragonal ZrO{sub 2} formed when the precursor calcined at 1173–1373 K for 2 h. • As calcined at 1473 K for 2 h, tetragonal ZrO{sub 2} fully converted to monoclinic ZrO{sub 2}. - Abstract: Thermal behavior and phase transformation of ZrO{sub 2}–10%SiO{sub 2} precursor powder prepared by a co-precipitation route without adding stability agent has been studied using different thermal analysis/thermogravimetry (DTA/TG), X-ray diffraction (XRD), transmission electron microscopy (TEM), selected area electron diffraction (SAED), nano beam electron diffraction (NBED), high-resolution TEM (HRTEM) and energy-dispersive X-ray spectrometer (EDS). The TG results show that four weight loss regions were from 298 to 443 K, 443 to 743 K, 743 to 793 K and 793 to 1400 K. The DTA result shows that the ZrO{sub 2} freeze-dried precursor powders crystallization at 1014 K. The activation energy of 993.7 kJ/mol was obtained for tetragonal ZrO{sub 2} crystallization using a non-isothermal process. The XRD result shows that only a single phase of tetragonal ZrO{sub 2} appears when the freeze-dried precursor powders after calcination between 1173 and 1373 K for 2 h. Moreover, when calcined at 1473 K for 2 h, the phase transformation from tetragonal ZrO{sub 2} fully converted to monoclinic ZrO{sub 2} occurred.

  2. XPS and SEM analysis of the surface of gas atomized powder precursor of ODS ferritic steels obtained through the STARS route

    Science.gov (United States)

    Gil, E.; Cortés, J.; Iturriza, I.; Ordás, N.

    2018-01-01

    An innovative powder metallurgy route to produce ODS FS, named STARS, has succeeded in atomizing steel powders containing the oxide formers (Y and Ti) and, hence, avoids the mechanical alloying (MA) step to dissolve Y in the matrix. A metastable oxide layer forms at the surface of atomized powders and dissociates during HIP consolidation at high temperatures, leading to precipitation of more stable Y-Ti-O nanoparticles.

  3. Influence of the control atmosphere and milling time on the morphology and microstructure of pure copper and copper-2.5 % lithium powders produced by mechanical alloying; Influencia de la atmosfera de control y tiempo de molienda sobre la morfologia y microestructura de polvos de cobre puro y cobre-2,5% litio producidos por aleado mecanio

    Energy Technology Data Exchange (ETDEWEB)

    Rojas, P. A.; Alvarez, M. P.; Penaloza, A.; Zuniga, A.; Ordonez, S.

    2009-07-01

    In the present work was investigated the effect of two milling parameters, atmosphere and milling time, on the morphology and microstructure of pure copper powder and a mixture of copper-2,5 wt. % lithium. The mechanical alloying was performed in a SPEX 8000D mill, using steel containers and balls. The two control atmospheres were argon and nitrogen and the milling time was varied from 3 up to 30 hours. The microstructural changes and the phases after milling were analyzed using scanning microscopy and X ray diffraction, whereas the amount of iron was measured by atomic absorption spectroscopy and the amount of oxygen by infrared spectroscopy. The results show the effect of the milling parameters studied on the microstructure as well as on the chemical composition of the samples. (Author) 22 refs.

  4. Mechanical alloying and reactive milling in a high energy planetary mill

    International Nuclear Information System (INIS)

    Jiang Xianjin; Trunov, Mikhaylo A.; Schoenitz, Mirko; Dave, Rajesh N.; Dreizin, Edward L.

    2009-01-01

    Powder refinement in a planetary mill (Retsch PM 400-MA) is investigated experimentally and analyzed using discrete element modeling (DEM). Refinement is defined as the average size of the individual components in a composite powder. The specific milling dose, defined as the product of charge ratio and milling time, is used as an experimental parameter tracking the progress of the material refinement. This parameter is determined experimentally for milling of boron and titanium powders, for which the time of initiation of a self-sustained reaction is measured under different milling conditions. It is assumed that the reaction becomes self-sustaining when the same powder refinement is achieved. The DEM calculations established that the milling balls primarily roll along the milling container's perimeter. The inverse of the rate of energy dissipation resulting from this rolling motion is used as the DEM analog of the specific milling dose. The results correlate well with experimental observations.

  5. Crystallization behavior of ZrO{sub 2}−3Y{sub 2}O{sub 3}−xSrO precursor powders synthesized by a coprecipitation process

    Energy Technology Data Exchange (ETDEWEB)

    Chu, Hsueh-Liang [Department of Materials Science and Engineering, National Cheng Kung University, 1 Ta- Hsueh Road, Tainan 70101, Taiwan (China); Hwang, Weng-Sing [Department of Materials Science and Engineering, National Cheng Kung University, 1 Ta- Hsueh Road, Tainan 70101, Taiwan (China); Institute of Nanotechnology and Microsystems Engineering, National Cheng Kung University, 1 Ta- Hsueh Road, Tainan 70101, Taiwan (China); Du, Je-Kang [Department of Dentistry, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 80708, Taiwan (China); Department of Dentistry, Kaohsiung Medical University, Chung Ho Memorial Hospital, 100 Tzyou 1st Road, Kaohsiung 80708, Taiwan (China); Chen, Ker-Kong, E-mail: enamel@kmu.edu.tw [Department of Dentistry, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 80708, Taiwan (China); Department of Dentistry, Kaohsiung Medical University, Chung Ho Memorial Hospital, 100 Tzyou 1st Road, Kaohsiung 80708, Taiwan (China); Wang, Moo-Chin, E-mail: mcwang@kmu.edu.tw [Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, 100 Shih-Chuan 1st Road, Kaohsiung 80708, Taiwan (China)

    2016-09-05

    Crystallization behaviors of ZrO{sub 2}−3Y{sub 2}O{sub 3}−xSrO precursor powders were studied with zirconium nitrate (Zr(NO{sub 3}){sub 4}·xH{sub 2}O), yttrium nitrate (Y(NO{sub 3}){sub 3}·6H{sub 2}O) and strontium nitrate (Sr(NO{sub 3}){sub 2}) constituting the initial materials. Differential thermal analysis (DTA), X-ray diffraction (XRD), transmission electron microscopy (TEM), selected area electron diffraction (SAED), nano beam electron diffraction (NBED) and high-resolution TEM (HRTEM) were utilized to characterize the crystallization behavior of ZrO{sub 2}−3Y{sub 2}O{sub 3}−xSrO precursor powders. The activation energies of tetragonal ZrO{sub 2} (t-ZrO{sub 2}) crystallization were 389.1, 327.6, and 315.1 kJ/mol with SrO content for 1, 2, and 3 mol%, respectively, obtained with a non-isothermal method. The growth morphology parameter and growth mechanism index were close to 2.0 and 1.0, respectively, showing that t-ZrO{sub 2} had a plate-like morphology. - Highlights: • The single phase of tetragonal ZrO{sub 2} formed when calcined at 923 K for 2 h. • ZrO{sub 2}−3Y{sub 2}O{sub 3}−2SrO precursor powders crystallization is at 765.6 K. • The activation energy of t-ZrO{sub 2} crystallization was 389.1 kJ/mol with 1 mol% SrO. • The growth morphology and index of crystallization were close to 2.0 and 1.0.

  6. Degradation of Highly Alloyed Metal Halide Perovskite Precursor Inks: Mechanism and Storage Solutions

    Energy Technology Data Exchange (ETDEWEB)

    Dou, Benjia [National Renewable Energy Laboratory (NREL), Golden, CO (United States); Wheeler, Lance M [National Renewable Energy Laboratory (NREL), Golden, CO (United States); Christians, Jeffrey A [National Renewable Energy Laboratory (NREL), Golden, CO (United States); Moore, David [National Renewable Energy Laboratory (NREL), Golden, CO (United States); Harvey, Steven P [National Renewable Energy Laboratory (NREL), Golden, CO (United States); Berry, Joseph J [National Renewable Energy Laboratory (NREL), Golden, CO (United States); Van Hest, Marinus F [National Renewable Energy Laboratory (NREL), Golden, CO (United States); Barnes, Frank S. [University of Colorado; Shaheen, Sean E. [University of Colorado

    2018-03-02

    Whereas the promise of metal halide perovskite (MHP) photovoltaics (PV) is that they can combine high efficiency with solution-processability, the chemistry occurring in precursor inks is largely unexplored. Herein, we investigate the degradation of MHP solutions based on the most widely used solvents, dimethylformamide (DMF) and dimethyl sulfoxide (DMSO). For the MHP inks studied, which contain formamidinium (FA+), methylammonium (MA+), cesium (Cs+), lead (Pb2+), bromide (Br-), and iodide (I-), dramatic compositional changes are observed following storage of the inks in nitrogen in the dark. We show that hydrolysis of DMF in the precursor solution forms dimethylammonium formate, which subsequently incorporates into the MHP film to compromise the ability of Cs+ and MA+ to stabilize FA+-based MHP. The changes in solution chemistry lead to a modification of the perovskite film stoichiometry, band gap, and structure. The solid precursor salts are stable when ball-milled into a powder, allowing for the storage of large quantities of stoichiometric precursor materials.

  7. Magnetoresistivity and microstructure of YBa2Cu3Oy prepared using planetary ball milling

    International Nuclear Information System (INIS)

    Hamrita, A.; Ben Azzouz, F.; Madani, A.; Ben Salem, M.

    2012-01-01

    Superconducting properties of YBa 2 Cu 3 O y prepared using planetary ball milling were studied. Y-deficient YBa 2 Cu 3 O y nanoparticles are embedded in the superconducting matrix. Ball milled sample exhibits a large magnetoresistivity in weak magnetic fields at 77 K. We have studied the microstructure and the magnetoresistivity of polycrystalline YBa 2 Cu 3 O y (YBCO or Y-123 for brevity) embedded with nanoparticles of Y-deficient YBCO, generated by the planetary ball milling technique. Bulk samples were synthesized from a precursor YBCO powder, which was prepared from commercial high purity Y 2 O 3 , Ba 2 CO 3 and CuO via a one-step annealing process in air at 950 °C. After planetary ball milling of the precursor, the powder was uniaxially pressed and subsequently annealed at 950 °C in air. Phase analysis by X-ray diffraction (XRD), granular structure examination by scanning electron microscopy (SEM), microstructure investigation by transmission electron microscopy (TEM) coupled with energy dispersive X-ray spectroscopy (EDXS) were carried out. TEM analyses show that nanoparticles of Y-deficient YBCO, generated by ball milling, are embedded in the superconducting matrix. Electrical resistance as a function of temperature, ρ(T), revealed that the zero resistance temperature, T co , is 84.5 and 90 K for the milled and unmilled samples respectively. The milled ceramics exhibit a large magnetoresistance in weak magnetic fields at liquid nitrogen temperature. This attractive effect is of high significance as it makes these materials promising candidates for practical application in magnetic field sensor devices.

  8. Characterization of tin selenides synthesized by high-energy milling

    Directory of Open Access Journals (Sweden)

    Marcela Achimovičová

    2011-12-01

    Full Text Available Tin selenides SnSeX (x=1,2 were synthesized from tin and selenium powder precursors by high-energy milling in the planetary ballmill Pulverisette 6 (Fritsch, Germany. The orthorhombic tin selenide SnSe and the hexagonal tin diselenide SnSe2 phases were formed after4 min and 5 min of milling, respectively. Specific surface area of both selenides increased with increasing time of mechanochemicalsynthesis. The particle size distribution analysis demonstrated that the synthesized products contain agglomerated selenide particlesconsisting of numerous idiomorphic tin selenide crystals, measuring from 2 to more than 100 nm in diameter, which were also documentedby TEM. UV-Vis spectrophotometry confirmed that tin selenide particles do not behave as quantum dots.

  9. Effect of the milling energy on the production and thermal stability of amorphous Mg50Ni50

    International Nuclear Information System (INIS)

    Guzman, D.; Ordonez, S.; Serafini, D.; Rojas, P.; Bustos, O.

    2009-01-01

    The effect of milling energy on the amorphisation process and subsequent thermal crystallization of Mg 50 Ni 50 was investigated. The amorphous Mg 50 Ni 50 was produced using a planetary mill (medium energy) with a ball to material weight ratio of 13:1, and a SPEX mill (high energy) with a ball to material weight ratio of 20:1. The results obtained by means of X-ray diffraction showed that it is possible to obtain an amorphous Mg 50 Ni 50 alloy, through both milling processes, starting of Ni powders and Mg turnings. However, the amorphisation process requires more time in the planetary mill (80-90 h) than in the SPEX mill (15-20 h), due to the difference in energy level and milling mechanism between these mills. The phase evolution during the amorphisation process is practically independent of the mill energy. In this way, it was observed that the mill conditions promoted an extensive refinement of the microstructure during the first hours of milling. The defects produced during this time led to the amorphisation of part of the system. This amorphous precursor suffers a mechanically induced crystallization into Mg 2 Ni, which is subsequently destabilized into amorphous Mg 50 Ni 50 . Based on the results obtained, it is proposed that the formation of amorphous precursor during mechanical milling of Mg and Ni is a characteristic of the Mg-Ni system, over a wide composition range, rather than of a particular composition. In relation to the thermal crystallization of the amorphous produced, the results of the differential thermal analysis applied to the amorphous samples showed that the formation enthalpy for both amorphous is the same, however, the amorphous produced in a planetary mill presented higher crystallization temperatures and apparent activation energies than the amorphous produced in a SPEX mill. The last behavior would be related with iron contamination coming from the erosion of the milling media. Finally, it is possible to conclude, that under the

  10. The effect of surfactant addition on high-energy milling upon the magnetic properties and microstructure of the Pr-Fe-B HDDR magnetic powders; Efeito da adicao de surfactantes nas propriedades e microestrutura de pos magneticos a base de Pr-Fe-B obtidos via HDDR e moagem de alta energia

    Energy Technology Data Exchange (ETDEWEB)

    Santos, P.B.; Silva, S.C.; Faria, R.N.; Takiishia, H., E-mail: pbsantos@ipen.b [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2010-07-01

    Nanomagnetic powders based on the composition Pr{sub 12}Fe{sub 65.9}Co{sub 16}B{sub 6}Nb{sub 0.1} have been obtained from using (a) the hydrogenation, disproportionation, desorption and recombination (HDDR) process; (b) by varying of milling time and (c) with the addition of an oleic acid as a surfactant. The latter has been used to enhance milling condition by preventing the agglomeration of particles and hence to improve the intrinsic coercivity of the material. High-energy mechanical milling has been used to yield magnetic nanoparticles. Powders were characterized magnetically using vibrating sample magnetometer (VSM) and microstructurally by Scanning Electron Microscopy (SEM), Field Emission Gun SEM (FEG-SEM) and X-ray diffraction. (author)

  11. Strain-enhanced sintering of iron powders

    Energy Technology Data Exchange (ETDEWEB)

    Amador, D.R.; Torralba, J.M. [Universidad Carlos III de Madrid, Departamento de Ciencias de Materiales e Ingenieria Metalurgica, Leganes, Madrid (Spain); Monge, M.A.; Pareja, R. [Universidad Carlos III de Madrid, Departamento de Fisica, Madrid (Spain)

    2005-02-01

    Sintering of ball-milled and un-milled Fe powders has been investigated using dilatometry, X-ray, density, and positron annihilation techniques. A considerable sintering enhancement is found in milled powders showing apparent activation energies that range between 0.44 and 0.80 eV/at. The positron annihilation results, combined with the evolution of the shrinkage rate with sintering temperature, indicate generation of lattice defects during the sintering process of milled and un-milled powders. The sintering enhancement is attributed to pipe diffusion along the core of moving dislocations in the presence of the vacancy excess produced by plastic deformation. Positron annihilation results do not reveal the presence of sintering-induced defects in un-milled powders sintered above 1200 K, the apparent activation energy being in good agreement with that for grain-boundary diffusion in {gamma}-Fe. (orig.)

  12. C, N co-doped TiO_2/TiC_0_._7N_0_._3 composite coatings prepared from TiC_0_._7N_0_._3 powder using ball milling followed by oxidation

    International Nuclear Information System (INIS)

    Hao, Liang; Wang, Zhenwei; Zheng, Yaoqing; Li, Qianqian; Guan, Sujun; Zhao, Qian; Cheng, Lijun; Lu, Yun; Liu, Jizi

    2017-01-01

    Highlights: • TiO_2/TiC_0_._7N_0_._3 coatings were prepared by ball milling followed by oxidation. • In situ co-doping of C and N with simultaneous TiO_2 formation was observed. • Improved photocatalytic activity under UV/visible light was noticed. • Synergism in co-doping and heterojunction formation promoted carrier separation. - Abstract: Ball milling followed by heat oxidation was used to prepared C, N co-doped TiO_2 coatings on the surfaces of Al_2O_3 balls from TiC_0_._7N_0_._3 powder. The as-prepared coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and ultraviolet-visible spectrophotometer (UV–vis). The results show that continuous TiC_0_._7N_0_._3 coatings were formed after ball milling. C, N co-doped TiO_2/TiC_0_._7N_0_._3 composite coatings were prepared after the direct oxidization of TiC_0_._7N_0_._3 coatings in the atmosphere. However, TiO_2 was hardly formed in the surface layer of TiC_0_._7N_0_._3 coatings within a depth less than 10 nm during the heat oxidation of TiC_0_._7N_0_._3 coatings in carbon powder. Meanwhile, the photocatalytic activity evaluation of these coatings was conducted under the irradiation of UV and visible light. All the coatings showed photocatalytic activity in the degradation of MB no matter under the irradiation of UV or visible light. The C, N co-doped TiO_2/TiC_0_._7N_0_._3 composite coatings showed the most excellent performance. The enhancement under visible light irradiation should attribute to the co-doping of carbon and nitrogen, which enhances the absorption of visible light. The improvement of photocatalytic activity under UV irradiation should attribute to the synergistic effect of C, N co-doping, the formation of rutile-anatase mixed phases and the TiO_2/TiC_0_._7N_0_._3 composite microstructure.

  13. Effect of the variation in the ambient moisture on the compaction behavior of powder undergoing roller-compaction and on the characteristics of tablets produced from the post-milled granules.

    Science.gov (United States)

    Gupta, Abhay; Peck, Garnet E; Miller, Ronald W; Morris, Kenneth R

    2005-10-01

    Effect of variation in the ambient moisture levels on the compaction behavior of a 10% acetaminophen (APAP) powder blend in microcrystalline cellulose (MCC) powder was studied by comparing the physical and mechanical properties of ribbons prepared by roller compaction with those of simulated ribbons, i.e., tablets prepared under uni-axial compression. Relative density, moisture content, tensile strength, and Young's modulus were used as key compact properties for comparison. Moisture was found to facilitate the particle rearrangement of both, the APAP and the MCC particles, as well as the deformation of the MCC particles. The tensile strength of the simulated ribbons also showed an increase with increasing moisture content. An interesting observation was that the tensile strength of the roller compacted samples first increased and then decreased with increasing moisture content. Variation in the ambient moisture during roller compaction was also found to influence the characteristics of tablets produced from the granules obtained post-milling the ribbons. A method to study this influence is also reported. Copyright (c) 2005 Wiley-Liss, Inc. and the American Pharmacists Association

  14. Effect of the calcining temperature on the porosity of the titanium dioxide powders obtained by Polymeric Precursor Method; Efeito da temperatura de calcinacao na porosidade de pos de dioxido de titanio obtidos pelo Metodo dos Precursores Polimericos

    Energy Technology Data Exchange (ETDEWEB)

    Silva, D.W.; Granado, S.R.; Ciola, R.A.; Cavalheiro, A.A., E-mail: douglas_levis@hotmail.com [Universidade Estadual de Mato Grosso do Sul (CPTREN/UEMS), Navirai, MS (Brazil). Centro de Pesquisas Tecnologicas em Recursos Naturais

    2011-07-01

    Ceramics materials obtained by Polymeric Precursor Method exhibit mechanisms of the pore formation and elimination dependents on the decomposition kinetics of the residual organic matter of the polyester. The mechanism of pore elimination seems to occur by disrupting of the wall among the pores because it leads to the consequent pore coalescence and increasing in pore volume, which posses higher pore diameters. In this case, it was observed that the porosity decreasing occurs by pore wall moving after that the residual organic matter is eliminated from the pore inside. The pore diameter associated to the highest volume desorption occurred for the material obtained after calcining at 450°C is approximately 1,7 nm, what seems to be related to the amorphous carbon accumulated inside the pores, once that the pore volume decreases more effectively for the material obtained by calcining at 550°C, making the maximum volume situates at 2,0 nm. (author)

  15. Sn powder as reducing agents and SnO2 precursors for the synthesis of SnO2-reduced graphene oxide hybrid nanoparticles.

    Science.gov (United States)

    Chen, Mingxi; Zhang, Congcong; Li, Lingzhi; Liu, Yu; Li, Xichuan; Xu, Xiaoyang; Xia, Fengling; Wang, Wei; Gao, Jianping

    2013-12-26

    A facile approach to prepare SnO2/rGO (reduced graphene oxide) hybrid nanoparticles by a direct redox reaction between graphene oxide (GO) and tin powder was developed. Since no acid was used, it is an environmentally friendly green method. The SnO2/rGO hybrid nanoparticles were characterized by ultraviolet-visible spectroscopy, Raman spectroscopy, thermogravimetric analysis, X-ray diffraction analysis, and X-ray photoelectron spectroscopy. The microstructure of the SnO2/rGO was observed with scanning electron microscopy and transmission electron microscopy. The tin powder efficiently reduced GO to rGO, and the Sn was transformed to SnO2 nanoparticles (∼45 nm) that were evenly distributed on the rGO sheets. The SnO2/rGO hybrid nanoparticles were then coated on an interdigital electrode to fabricate a humidity sensor, which have an especially good linear impedance response from 11% to 85% relative humidity.

  16. Study of the Adherence Mechanism Between the Metal and Inorganic Coating with Mill Addition of Li2Ni8O10 Nano Powder

    Institute of Scientific and Technical Information of China (English)

    QIAN Hui-chun; JIANG Wei-zhong

    2009-01-01

    The adherence strength between the metal and the inorganic coating can be greatly increased by mill addition of Li2Ni8O10,. The interface structure between metal and the inorganic coating with excellent adherence has been studied by investigating the chemical composition and the microstructure as well as elements valence bond on the interface with the help of scanning electron microscope (SEM), electron microprobe, and Auger electron spectroscope (AES). The results show that there is a non-stoichiometrical transitional layer on the interface between metal and the inorganic coating with excellent adherence, the adherence between metal and the non-stoichiometrical transitional layer is achieved by the metallic bond and the adherence between the non-stoichiometrical transitional layer and the inorganic coating is produced by ionic and covalent bond. The non-stoichiometrical transitional layer results in the strong adherence.

  17. Fabrication and Mechanical Properties of SiCw(p/SiC-Si Composites by Liquid Si Infiltration using Pyrolysed Rice Husks and SiC Powders as Precursors

    Directory of Open Access Journals (Sweden)

    Dan Zhu

    2014-03-01

    Full Text Available Dense silicon carbide (SiC matrix composites with SiC whiskers and particles as reinforcement were prepared by infiltrating molten Si at 1550 °C into porous preforms composed of pyrolysed rice husks (RHs and extra added SiC powder in different ratios. The Vickers hardness of the composites showed an increase from 18.6 to 21.3 GPa when the amount of SiC added in the preforms was 20% (w/w, and then decreased to 17.3 GPa with the increase of SiC added in the preforms up to 80% (w/w. The values of flexural strength of the composites initially decreased when 20% (w/w SiC was added in the preform and then increased to 587 MPa when the SiC concentration reached 80% (w/w. The refinement of SiC particle sizes and the improvement of the microstructure in particle distribution of the composites due to the addition of external SiC played an effective role in improving the mechanical properties of the composites.

  18. Structural and electrical properties of NASICON type solid electrolyte nanoscaled glass-ceramic powder by mechanical milling for thin film batteries.

    Science.gov (United States)

    Patil, Vaishali; Patil, Arun; Yoon, Seok-Jin; Choi, Ji-Won

    2013-05-01

    During last two decades, lithium-based glasses have been studied extensively as electrolytes for solid-state secondary batteries. For practical use, solid electrolyte must have high ionic conductivity as well as chemical, thermal and electrochemical stability. Recent progresses have focused on glass electrolytes due to advantages over crystalline solid. Glass electrolytes are generally classified into two types oxide glass and sulfide glass. Oxide glasses do not react with electrode materials and this chemical inertness is advantageous for cycle performances of battery. In this study, major effort has been focused on the improvement of the ion conductivity of nanosized LiAlTi(PO4)3 oxide electrolyte prepared by mechanical milling (MM) method. After heating at 1000 degrees C the material shows good crystallinity and ionic conductivity with low electronic conductivity. In LiTi2(PO4)3, Ti4+ ions are partially substituted by Al3+ ions by heat-treatment of Li20-Al2O3-TiO2-P2O5 glasses at 1000 degrees C for 10 h. The conductivity of this material is 1.09 x 10(-3) S/cm at room temp. The glass-ceramics show fast ion conduction and low E(a) value. It is suggested that high conductivity, easy fabrication and low cost make this glass-ceramics promising to be used as inorganic solid electrolyte for all-solid-state Li rechargeable batteries.

  19. Fe-FeS2 adsorbent prepared with iron powder and pyrite by facile ball milling and its application for arsenic removal.

    Science.gov (United States)

    Min, Xiaobo; Li, Yangwenjun; Ke, Yong; Shi, Meiqing; Chai, Liyuan; Xue, Ke

    2017-07-01

    Arsenic is one of the major pollutants and a worldwide concern because of its toxicity and chronic effects on human health. An adsorbent of Fe-FeS 2 mixture for effective arsenic removal was successfully prepared by mechanical ball milling. The products before and after arsenic adsorption were characterized with scanning electron microscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and X-ray photoelectron spectroscopy. The adsorbent shows high arsenic removal efficiency when molar ratio of iron to pyrite is 5:5. The experimental data of As(III) adsorption are fitted well with the Langmuir isotherm model with a maximal adsorption capacity of 101.123 mg/g. And As(V) data were described perfectly by the Freundlich model with a maximal adsorption capacity of 58.341 L/mg. As(III) is partial oxidized to As(V) during the adsorption process. High arsenic uptake capability and cost-effectiveness of waste make it potentially attractive for arsenic removal.

  20. Effect of process variables on synthesis of MgB2 by a high energy ball mill

    Directory of Open Access Journals (Sweden)

    Kurama Haldun

    2016-01-01

    Full Text Available The discovery of superconductivity of MgB2 in 2001, with a critical temperature of 39 K, offered the promise of important large-scale applications at around 20 K. Except than the other featured synthesis methods, mechanical activation performed by high energy ball mills, as bulk form synthesis or as a first step of wire and thin film productions, has considered as an effective alternative production route in recent years. The process of mechanical activation (MA starts with mixing the powders in the right proportion and loading the powder mixture into the mill with the grinding media. The milled powder is then consolidated into a bulk shape and heat-treated to obtain desired microstructure and properties. Thus, the important components of the MA process are the raw materials, mill type and process variables. During the MA process, heavy deformation of particles occure. This is manifested by the presence of a variety of crystal defects such as dislocations, vacancies, stacking faults and increased number of particle boundaries. The presence of this defect structure enhances the diffusivity of solute hence the critical currents and magnetic flux pinning ability of MgB2 are improved. The aim of the present study is to determine the effects of process variables such as ball-to-powder mass ratio, size of balls, milling time, annealing temperature and contribution of process control agent (toluene on the product size, morphology and conversion level of precursor powders to MgB2 after subsequent heat treatment. The morphological analyses of the samples were performed by a high vacuum electron microscope ZEISS SUPRA VP 50. The phase compositions of the samples were performed with an Rigaku-Rint 2200 diffractometer, with nickel filtered Cu Kα radiation and conversion level. The MgB2 phase wt % was calculated by the Rietveld refinement method. The obtained results were discussed according to the process variables to find out their affect on the structure

  1. Effect of process control agent on the structural and magnetic properties of nano/amorphous Fe0.7Nb0.1Zr0.1Ti0.1 powders prepared by high energy ball milling

    Science.gov (United States)

    Khazaei Feizabad, Mohammad Hossein; Sharafi, Shahriar; Khayati, Gholam Reza; Ranjbar, Mohammad

    2018-03-01

    In this study, amorphous Fe0.7Nb0.1Zr0.1Ti0.1 alloy without metalloids was produced by mechanical alloying of pure mixture elements. Miedema's semi-empirical model was employed to predict the possibility of amorphous phase formation in proposed alloying system. The effect of Hexane as process control agent (PCA) on the structural, magnetic, morphological and thermal properties of the products was investigated. The results showed that the presence of PCA was necessary for the formation of amorphous phase as well as improved its soft magnetic properties. The PCA addition causes an increase of the saturation magnetization (about 43%) and decrease of the coercivity (about 50%). Moreover, the sample milled without PCA, showed a wide particle size distribution as well as relatively spherical geometry. While, in the presence of PCA the powders were aspherical and Polygon. In addition, the crystallization and Curie temperatures were found to be around 800 °C and 650 °C, respectively which are relatively high values for these kinds of alloys.

  2. MILLING MECHANICS OF MATERIALS ROLLED IN THICK LAYER

    Directory of Open Access Journals (Sweden)

    E. B. Lojechnikov

    2006-01-01

    Full Text Available Powder rolling conditions are systematized with the purpose of their compacting and milling. The generalized  condition of solid and free-flowing bulk material deformation is proposed in the  paper. The analytical solution of a stressed state of powder being shaped mechanically that ensures milling of its particles has been obtained.

  3. Comminution of B4C powders with a high-energy mill operated in air in dry or wet conditions and its effect on their spark-plasma sinterability

    DEFF Research Database (Denmark)

    Ortiz, Angel L.; Sánchez-Bajo, Florentino; Leal, Victor Manuel Candelario

    2017-01-01

    to the nanoscale. While this is accompanied by oxidation and aggregation, these are not serious drawbacks. Wet shaker milling in methanol (i.e., conventional ball-milling) resulted only in a moderate B4C particle refinement with greater contamination by the milling tools, which limits its usefulness. It was also......-plasma sintering confirmed this recommendation, and also showed the usefulness of dry shaker milling to obtain refined B4C microstructures for structural applications....

  4. Wet milling versus co-precipitation in magnetite ferrofluid preparation

    Directory of Open Access Journals (Sweden)

    Almásy László

    2015-01-01

    Full Text Available Various uses of ferrofluids for technical applications continuously raise the interest in improvement and optimization of preparation methods. This paper deals with preparation of finely granulated magnetite particles coated with oleic acid in hydrocarbon suspensions following either chemical co-precipitation from iron salt precursors or wet milling of micron size magnetite powder with the goal to compare the benefits and disadvantages of each method. Microstructural measurements showed that both methods gave similar magnetite particle size of 10-15 nm. Higher saturation magnetization was achieved for the wet-milled magnetite suspension compared to relatively rapid co-precipitation synthesis. Different efficacies of ferrophase incorporation into kerosene could be related to the different mechanisms of oleic acid bonding to nanoparticle surface. The comparative data show that wet milling represents a practicable alternative to the traditional co-precipitation since despite of longer processing time, chemicals impact on environment can be avoided as well as the remnant water in the final product.

  5. Mechanical alloying of Hf and Fe powders

    International Nuclear Information System (INIS)

    Mendoza Zelis, L.; Crespo, E.; Creus, M.; Damonte, L.C.; Sanchez, F.H.; Punte, G.

    1994-01-01

    Pure crystalline Hf and Fe powders were mixed and milled under an argon atmosphere. The evolution of the system with milling time was followed with Moessbauer effect spectroscopy and X-ray diffraction. The results indicate that in the first stages an amorphous Fe-rich alloy was gradually formed together with a solid solution of Hf in Fe beyond the solubility limit. (orig.)

  6. Micro structrual characterization and analysis of ball milled silicon carbide

    Science.gov (United States)

    Madhusudan, B. M.; Raju, H. P.; Ghanaraja., S.

    2018-04-01

    Mechanical alloying has been one of the prominent methods of powder synthesis technique in solid state involving cyclic deformation, cold welding and fracturing of powder particles. Powder particles in this method are subjected to greater mechanical deformation due to the impact of ball-powder-ball and ball-powder-container collisions that occurs during mechanical alloying. Strain hardening and fracture of particles decreases the size of the particles and creates new surfaces. The objective of this Present work is to use ball milling of SiC powder for different duration of 5, 10, 15 and 20 hours by High energy planetary ball milling machine and to evaluate the effect of ball milling on SiC powder. Micro structural Studies using Scanning Electron Microscopy (SEM), X-ray Diffraction (XRD) and EDAX has been investigated.

  7. Solid-solid and gas-solid interactions induced during high-energy milling to produce PbTe nanopowders

    Energy Technology Data Exchange (ETDEWEB)

    Rojas-Chavez, H., E-mail: rojas_hugo@ittlahuac2.edu.mx [Instituto Tecnologico de Tlahuac - II (Mexico); Reyes-Carmona, F. [Facultad de Quimica - UNAM (Mexico); Garibay-Febles, V. [Instituto Mexicano del Petroleo, Laboratorio de Microscopia Electronica de Ultra Alta Resolucion (Mexico); Jaramillo-Vigueras, D. [Centro de Investigacion e Innovacion Tecnologica - IPN (Mexico)

    2013-05-15

    Transformations from precursors to nanoparticles by high-energy milling are promoted by two major driving forces, namely physical and/or chemical. While the former has been difficult to trace since stress, strain and recovery may occur almost simultaneously during milling, the latter has been sequentially followed as an evolution from precursors to intermediate phases and thereof to high purity nanocrystals. The specific objective of this work is to discern how solid-solid and partially solid-gas reactions manifest themselves correspondingly as a short-range diffusion through an interface or how vapor species, as a subliming phenomenon, grows as a different phase on an active local surface. These series of changes were traced by sub-cooling the as-milled powders extracted during a milling cycle. Through this experimental technique, samples were electron microscopically analyzed and where it was required, selected area electron diffraction images were obtained. High-resolution transmission electron microscopy results, unambiguously, confirm that nanocrystals in the last stage show a cubic morphology which average size distributions are around 17 nm.

  8. Crushing method for nuclear fuel powder

    International Nuclear Information System (INIS)

    Hasegawa, Shin-ichi; Tsuchiya, Haruo.

    1997-01-01

    A crushing medium is contained in mill pots disposed at the circumferential periphery of a main axis. The diameter of each mill pot is determined such that powdery nuclear fuels containing aggregated powders and ground and mixed powders do not reach criticality. A plurality of mill pots are revolved in the direction of the main axis while each pots rotating on its axis. Powdery nuclear fuels containing aggregated powders are conveyed to a supply portion of the moll pot, and an inert gas is supplied to the supply portion. The powdery nuclear fuels are supplied from the supply portion to the inside of the mill pots, and the powdery nuclear fuels containing aggregated powders are crushed by centrifugal force caused by the rotation and the revolving of the mill pots by means of the crushing medium. UO 2 powder in uranium oxide fuels can be crushed continuously. PuO 2 powder and UO 2 powder in MOX fuels can be crushed and mixed continuously. (I.N.)

  9. New technology for recycling materials from oily cold rolling mill sludge

    Institute of Scientific and Technical Information of China (English)

    Bo Liu; Shen-gen Zhang; Jian-jun Tian; De-an Pan; Ling Meng; Yang Liu

    2013-01-01

    Oily cold rolling mill (CRM) sludge is one of metallurgical industry solid wastes. The recycle of these wastes can not only protect the environment but also permit their reutilization. In this research, a new process of“hydrometallurgical treatment+hydrothermal synthesis”was investigated for the combined recovery of iron and organic materials from oily CRM sludge. Hydrometallurgical treatment, mainly including acid leaching, centrifugal separation, neutralization reaction, oxidizing, and preparation of hydrothermal reaction precursor, was first utilized for processing the sludge. Then, micaceous iron oxide (MIO) pigment powders were prepared through hydrothermal reaction of the obtained precursor in alkaline media. The separated organic materials can be used for fuel or chemical feedstock. The quality of the prepared MIO pigments is in accordance with the standards of MIO pigments for paints (ISO 10601-2007). This clean, eff ective, and economical technology off ers a new way to recycle oily CRM sludge.

  10. Influence of milling process on efavirenz solubility

    Directory of Open Access Journals (Sweden)

    Erizal Zaini

    2017-01-01

    Full Text Available Introduction: The aim of this study was to investigate the influence of the milling process on the solubility of efavirenz. Materials and Methods: Milling process was done using Nanomilling for 30, 60, and 180 min. Intact and milled efavirenz were characterized by powder X-ray diffraction, scanning electron microscopy (SEM, spectroscopy infrared (IR, differential scanning calorimetry (DSC, and solubility test. Results: The X-ray diffractogram showed a decline on peak intensity of milled efavirenz compared to intact efavirenz. The SEM graph depicted the change from crystalline to amorphous habit after milling process. The IR spectrum showed there was no difference between intact and milled efavirenz. Thermal analysis which performed by DSC showed a reduction on endothermic peak after milling process which related to decreasing of crystallinity. Solubility test of intact and milled efavirenz was conducted in distilled water free CO2with 0.25% sodium lauryl sulfate media and measured using high-performance liquid chromatography method with acetonitrile: distilled water (80:20 as mobile phases. The solubility was significantly increased (P < 0.05 after milling processes, which the intact efavirenz was 27.12 ± 2.05, while the milled efavirenz for 30, 60, and 180 min were 75.53 ± 1.59, 82.34 ± 1.23, and 104.75 ± 0.96 μg/mL, respectively. Conclusions: Based on the results, the solubility of efavirenz improved after milling process.

  11. Evaluating the Johanson theory for titanium powder

    CSIR Research Space (South Africa)

    Chikosha, S

    2015-05-01

    Full Text Available . In this study, the Johanson theory was used to determine the rolling parameters of titanium powder. Preliminary results of the nip angle, nip pressures and maximum horizontal pressures of the mill for the powder rolled on a 55mm diameter roll with roll gap sizes...

  12. Efeito do vapor d'água na síntese pelo método do precursor polimérico da alumina contendo aditivos Effect of water vapor on the synthesis by the polymeric precursor method of alumina doped powders

    Directory of Open Access Journals (Sweden)

    R. H. R. Castro

    2005-12-01

    Full Text Available A presença de H2O nos processos de síntese e transformação de fase da alumina tem usualmente função catalisadora, diminuindo as temperaturas dos processos e facilitando os possíveis rearranjos atômicos. Neste trabalho mostrou-se que o vapor de H2O durante a síntese pode não apenas acelerar os processos diminuindo as energias de ativação, mas também induzir diferentes formas de ação de aditivos. O estudo foi possível utilizando-se o método dos precursores poliméricos para a síntese dos pós, que permite um controle absoluto do teor de H2O na etapa de cristalização do material. Alumina contendo Mn ou Mg como aditivos foram sintetizadas na ausência de H2O e na presença de excesso controlado desta e fases diferentes para cada situação foram observadas. Uma explicação do fenômeno é descrita em função da dependência da cristalização da gama-Al2O3 na presença de H+ para compensação das vacâncias catiônicas.It is commonly accepted that the presence of H2O during the synthesis and phase transformation of alumina causes decreasing temperatures of these processes since it increases the atomic motilities. In addition to this general concept, in this work H2O vapor is also shown to play an important role on the influence of additives in alumina based systems. Alumina powders containing Mn or Mg were synthesized by the polymeric precursor method under H2O vapor or dry atmosphere during the crystallization stage. Each atmosphere promoted a different phase and an explanation for the phenomenon was given bases on the gamma-Al2O3 crystallization dependence on the H+ presence due to the required cationic vacancies compensations.

  13. Synthesis and characterization of superconducting YBCO powder

    International Nuclear Information System (INIS)

    Praveen, B.; Karki, T.; Krishnamoorthi, J.

    2008-01-01

    Full text: Superconducting yttrium barium copper oxide power has been synthesized through solid state sintering method - milling and sintering - using Y 2 O 3 , BaCo 3 and CuO powders. XRD result of the milled and sintered powder reveals that the powder that has formed contains YBa 2 Cu 3 O 6.5 superconducting phase. Results obtained by SEM/EDAX show the distribution of the different elements. Experiments carried out by intermediate firing and final annealing in oxygen controlled atmosphere show the diffusion of oxygen in preformed YBa 2 Cu 3 O 6.5 and their results are discussed

  14. A method of eliminating the surface defect in low-temperature oxidation powder added UO2 pellet

    International Nuclear Information System (INIS)

    Yoo, H. S.; Lee, S. J.; Kim, J. I.; Jeon, K. R.; Kim, J. W.

    2002-01-01

    A study on methods to eliminate surface defect shown in low-temperature oxidation powder added UO 2 pellet has been performed. Powders oxidized at 350 .deg. C for 4 hrs were prepared and mixed with UO 2 powder after crushing them. After being sintered, surfaces of the pellet were inspected both visually and optically. A large number of defects were observed on the surface of the specimens in which low-temperature oxidation powders were directly mixed or master mixed with UO 2 powder while both specimens produced from mixed powders including milled oxidation powders and powders that were milled totally after mixing had clean surfaces. However, optical examination showed considerably large defected pores in the milled oxidation powder added pellet and it was confirmed that the inner defects can be eliminated completely only when milling the entire mixture on UO 2 and low-temperature oxidation powder, but not by crushing only oxidation powder

  15. Improved hydrogen sorption kinetics in wet ball milled Mg hydrides

    Energy Technology Data Exchange (ETDEWEB)

    Meng, Li

    2011-05-04

    In this work, wet ball milling method is used in order to improve hydrogen sorption behaviour due to its improved microstructure of solid hydrogen materials. Compared to traditional ball milling method, wet ball milling has benefits on improvement of MgH{sub 2} microstructure and further influences on its hydrogen sorption behavior. With the help of solvent tetrahydrofuran (THF), wet ball milled MgH{sub 2} powder has much smaller particle size and its specific surface area is 7 times as large as that of dry ball milled MgH{sub 2} powder. Although after ball milling the grain size is decreased a lot compared to as-received MgH{sub 2} powder, the grain size of wet ball milled MgH{sub 2} powder is larger than that of dry ball milled MgH{sub 2} powder due to the lubricant effect of solvent THF during wet ball milling. The improved particle size and specific surface area of wet ball milled MgH{sub 2} powder is found to be determining its hydrogen sorption kinetics especially at relatively low temperatures. And it also shows good cycling sorption behavior, which decides on its industrial applicability. With three different catalysts MgH{sub 2} powder shows improved hydrogen sorption behavior as well as the cyclic sorption behavior. Among them, the Nb{sub 2}O{sub 5} catalyst is found to be the most effective one in this work. Compared to the wet ball milled MgH{sub 2} powder, the particle size and specific surface area of the MgH{sub 2} powder with catalysts are similar to the previous ones, while the grain size of the MgH{sub 2} with catalysts is much finer. In this case, two reasons for hydrogen sorption improvement are suggested: one is the reduction of the grain size. The other may be as pointed out in some literatures that formation of new oxidation could enhance the hydrogen sorption kinetics, which is also the reason why its hydrogen capacity is decreased compared to without catalysts. After further ball milling, the specific surface area of wet ball milled Mg

  16. Particle deformation during stirred media milling

    Science.gov (United States)

    Hamey, Rhye Garrett

    Production of high aspect ratio metal flakes is an important part of the paint and coating industry. The United States Army also uses high aspect ratio metal flakes of a specific dimension in obscurant clouds to attenuate infrared radiation. The most common method for their production is by milling a metal powder. Ductile metal particles are initially flattened in the process increasing the aspect ratio. As the process continues, coldwelding of metal flakes can take place increasing the particle size and decreasing the aspect ratio. Extended milling times may also result in fracture leading to a further decrease in the particle size and aspect ratio. Both the coldwelding of the particles and the breakage of the particles are ultimately detrimental to the materials performance. This study utilized characterization techniques, such as, light scattering and image analysis to determine the change in particle size as a function of milling time and parameters. This study proved that a fundamental relationship between the milling parameters and particle deformation could be established by using Hertz's theory to calculate the stress acting on the aluminum particles. The study also demonstrated a method by which milling efficiency could be calculated, based on the amount of energy required to cause particle deformation. The study found that the particle deformation process could be an energy efficient process at short milling times with milling efficiency as high as 80%. Finally, statistical design of experiment was used to obtain a model that related particle deformation to milling parameters, such as, rotation rate and milling media size.

  17. Analysis of crystallite size and microdeformation crystal lattice the tungsten carbide milling in mill high energy

    International Nuclear Information System (INIS)

    Silva, F.T. da; Nunes, M.A.M.; Souza, C.P. de; Gomes, U.U.

    2010-01-01

    The tungsten carbide (WC) has wide application due to its properties like high melting point, high hardness, wear resistance, oxidation resistance and good electrical conductivity. The microstructural characteristics of the starting powders influences the final properties of the carbide. In this context, the use of nanoparticle powders is an efficient way to improve the final properties of the WC. The high energy milling stands out from other processes to obtain nanometric powders due to constant microstructural changes caused by this process. Therefore, the objective is to undertake an analysis of microstructural characteristics on the crystallite size and microdeformations of the crystal lattice using the technique of X-ray diffraction (XRD) using the Rietveld refinement. The results show an efficiency of the milling process to reduce the crystallite size, leading to a significant deformation in the crystal lattice of WC from 5h milling. (author)

  18. Preparation and characterization of chrome doped sphene pigments prepared via precursor mechanochemical activation

    Energy Technology Data Exchange (ETDEWEB)

    Pantić, Jelena, E-mail: jelena.pantic@vinca.rs [Vinča Institute of Nuclear Sciences, University of Belgrade, P.O. Box 522, Belgrade (Serbia); Prekajski, Marija; Dramićanin, Miroslav; Abazović, Nadica [Vinča Institute of Nuclear Sciences, University of Belgrade, P.O. Box 522, Belgrade (Serbia); Vuković, Nikola [Faculty of Chemistry, University of Belgrade, 12-16 Studentski Trg, 11000 Belgrade (Serbia); Kremenović, Aleksandar [Faculty of Mining and Geology, University of Belgrade, Djušina 7, Belgrade (Serbia); Matović, Branko [Vinča Institute of Nuclear Sciences, University of Belgrade, P.O. Box 522, Belgrade (Serbia)

    2013-12-05

    Highlights: •Mechanical activation of precursors has been used for the preparation of Cr-doped sphene ceramic pigments (CaTi{sub 1−y}Cr{sub y}SiO{sub 5}). •The average particle size is around 1 μm, which is desirable for application. •The optimum pigment (best hue with lowest Cr content) is obtained with 0.1% Cr. •Both chromium ions (Cr{sup 4+} and Cr{sup 3+}), find itself within distorted octahedral coordination. -- Abstract: Mechanical activation of precursors has been used for the preparation of Cr-doped sphene ceramic pigments (CaTi{sub 1−y}Cr{sub y}SiO{sub 5}). Ceramic material has been prepared from a powder mixture of CaCO{sub 3}, TiO{sub 2}, SiO{sub 2} and Cr(NO{sub 3})⋅9H{sub 2}O using vibro-milling for homogenization and activation of precursors. The mechanochemical process initially yielded amorphous powders, which on further calcination, crystallized to yield Cr-doped sphene ceramic pigment. Phase evolution in CaTi{sub 1−y}Cr{sub y}SiO{sub 5} composition with thermal treatment was investigated by X-ray powder diffraction (XRPD). Texture properties and particle size distribution were analyzed by scanning electron microscopy (SEM) and laser diffraction, respectively. UV/Vis reflectance spectra are used to determinate the behavior of the chromium ion. The color efficiency of pigments was evaluated by colorimetric analysis (CIE L {sup *} a {sup *} b system). Photoluminescence measurements were also performed.

  19. Uranium milling costs

    International Nuclear Information System (INIS)

    Coleman, R.B.

    1980-01-01

    Basic process flowsheets are reviewed for conventional milling of US ores. Capital costs are presented for various mill capacities for one of the basic processes. Operating costs are shown for various mill capacities for all of the basic process flowsheets. The number of mills using, or planning to use, a particular process is reviewed. A summary of the estimated average milling costs for all operating US mills is shown

  20. A study of Al-Mo powder processing as a possible way to corrosion resistent aluminum-alloys

    Directory of Open Access Journals (Sweden)

    Wilson Corrêa Rodrigues

    2009-06-01

    Full Text Available Elementary Al and Mo powder mixtures have been processed by high energy ball milling up to milling times of 100 hours. The shift of the pitting potential and the X ray analysis of green milled samples showed that part of the Mo has formed a supersaturated solid solution of Mo in Al. Elementary Mo powder, however, was still present after 100 hours of milling. Sintering led to the formation of the intermetallic Al12Mo phase.

  1. Recoilless Factors in Nanostructured Iron-Based Powders

    International Nuclear Information System (INIS)

    Guerault, H.; Labaye, Y.; Greneche, J.-M.

    2001-01-01

    57 Fe Moessbauer spectrometry was carried out on high-energy ball-milled crystalline compounds in order to study the milling effect on the Lamb-Moessbauer factor f. A comparison between metallic (α-Fe) and ionic (r-FeF 3 ) milled powders is proposed, evidencing different milling mechanisms. In the case of the ionic system, a notable enhancement of the f factor at 77 K is observed by freezing the powder into a resin. This suggests that, in addition to nanostructured aggregated particles, the milling procedure favours the obtention of isolated nanoparticles, the sizes of which are smaller than the critical size for the observation of the Moessbauer effect. In return, in the case of the metallic system, the absorption gain due to the embedding is much smaller, probably due to a better re-agglomeration of the metallic particles during the milling process

  2. Spray drying of beryllium oxide powder

    International Nuclear Information System (INIS)

    Sepulveda, J.L.; Kahler, D.A.

    1991-01-01

    Forming of beryllia ceramics through dry pressing requires the agglomeration of the powder through spray drying. To produce high quality fired ceramics it is necessary to disperse/grind the primary powder prior to binder addition. Size reduction of the powder is accomplished using an aqueous system in Vibro-Energy mills (VEM) charged with beryllia media to minimize contamination. Two VEM mills of different size were used to characterize the grinding operation. Details of the grinding kinetics are described within the context of the Macroscopic Population Balance Model approach. Spray drying of the ceramic slurry was accomplished with both a centrifugal atomizer and a two fluid nozzle atomizer. Two different spray dryers were used. Important operating parameters affecting the size distribution of the spray dried powder are discussed

  3. Thermoset precursor

    International Nuclear Information System (INIS)

    Yamamoto, Y.

    1983-04-01

    This invention pertains to a distinctive thermoset precursor which is prepared by mixing a resin composition (A) which can be hardened by ionizing radiation, and a resin composition (B) which can be hardened by heat but cannot be hardened by, or is resistant to, ionizing radiation, and by coating or impregnating a molding or other substrate with a sheet or film of this mixture and irradiating this with an ionizing radiation. The principal components of composition (A) and (B) can be the following: (1) an acrylate or methacrylate and an epoxy resin and an epoxy resin hardener; (2) an unsaturated polyester resin and epoxy resin and an epoxy resin hardener; (3) a diacrylate or dimethacrylate or polyethylene glycol and an epoxy resin; (4) an epoxy acrylates or epoxy methacrylate obtained by the addition reaction of epoxy resin and acrylic or methacrylic acid

  4. Study on the characteristics and sinterability of DUPIC powder by using simulated fuel

    International Nuclear Information System (INIS)

    Lee, Jae-Won; Lee, Jung-Won; Kim, Jong-Ho; Yim, Sung-Paal; Lee, Young-Woo; Yang, Myung-Seung

    2002-01-01

    The sinterability of the OREOX (oxidation and reduction of oxide fuels) powder was investigated in terms of the number of the OREOX cycles and milling time using simulated spent fuel of an equivalent burnup of 35,000 MWD/MTU. Wet milled powder was prepared and sintered to compare the morphology and sinterability with the dry milled powder. Powders having a medium particle size of less than 1μm were obtained by dry milling of OREOX powders regardless of the number of cycles. The specific surface area of the simulated DUPIC powder was governed by the number of OREOX cycles rather than by milling time. The sound pellets with a sintered density of higher than 95% TD and average grain size of larger than 8μm were obtained with the dry milled powder after 1 cycle of OREOX treatment. The powders prepared by dry milling for a short time and wet milling for a long time after 3 cycles of OREOX treatment also produced pellets with a sintered density of higher than 95% TD and average grain size of larger than 8μm. (author)

  5. N-type nano-silicon powders with ultra-low electrical resistivity as anode materials in lithium ion batteries

    Science.gov (United States)

    Yue, Zhihao; Zhou, Lang; Jin, Chenxin; Xu, Guojun; Liu, Liekai; Tang, Hao; Li, Xiaomin; Sun, Fugen; Huang, Haibin; Yuan, Jiren

    2017-06-01

    N-type silicon wafers with electrical resistivity of 0.001 Ω cm were ball-milled to powders and part of them was further mechanically crushed by sand-milling to smaller particles of nano-size. Both the sand-milled and ball-milled silicon powders were, respectively, mixed with graphite powder (silicon:graphite = 5:95, weight ratio) as anode materials for lithium ion batteries. Electrochemical measurements, including cycle and rate tests, present that anode using sand-milled silicon powder performed much better. The first discharge capacity of sand-milled silicon anode is 549.7 mAh/g and it is still up to 420.4 mAh/g after 100 cycles. Besides, the D50 of sand-milled silicon powder shows ten times smaller in particle size than that of ball-milled silicon powder, and they are 276 nm and 2.6 μm, respectively. In addition, there exist some amorphous silicon components in the sand-milled silicon powder excepting the multi-crystalline silicon, which is very different from the ball-milled silicon powder made up of multi-crystalline silicon only.

  6. Effect of milling conditions on the properties of Cu-NbC alloys obtained by powder metallurgy; Efecto de las variables de molienda en las propiedades de aleaciones Cu-NbC obtenidas por pulvimetalurgia

    Energy Technology Data Exchange (ETDEWEB)

    Lopez, M.; Jimenez, J. A.; Ruano, O.; Benavente, R.

    2006-07-01

    Copper-base composite materials were obtained by reinforcing with homogeneous dispersions of 0.5 and 1% vol. of very fine NbC particles, through mechanical milling process in a planetary mill during 8 and 24 h at two different rotational speeds. The consolidation of the alloyed reinforced particles was achieved through a hot uniaxial pressing at 923K under 90 MPa during 2 h under a protective argon atmosphere. Factors to the suitable combination of electrical conductivity and mechanical properties attained are the hardness and good thermal stability of the niobium carbide which affords furthers refinement in the size of copper particles and the reinforcement of the alloy. A lower embrittlement and higher electrical conductivity of this alloys was observed, as a consequence of the smaller amount of impurities (Fe, Cr, C and O) incorporated during the lower-energy milling. Scanning and transmission electron microscopy and X-ray diffraction show and additional strengthening of the grain substructure by precipitation of nanometer-size impurities. (Author) 18 refs.

  7. Fuel powder production from ductile uranium alloys

    International Nuclear Information System (INIS)

    Clark, C.R.; Meyer, M.K.

    1998-01-01

    Metallic uranium alloys are candidate materials for use as the fuel phase in very-high-density LEU dispersion fuels. These ductile alloys cannot be converted to powder form by the processes routinely used for oxides or intermetallics. Three methods of powder production from uranium alloys have been investigated within the US-RERTR program. These processes are grinding, cryogenic milling, and hydride-dehydride. In addition, a gas atomization process was investigated using gold as a surrogate for uranium. (author)

  8. Preparation of iron sulphides by high energy ball milling

    DEFF Research Database (Denmark)

    Lin, R.; Jiang, Jianzhong; Larsen, R.K.

    1998-01-01

    The reaction of a powder mixture consisting of 50 a.% Fe and 50 a.% S during high energy ball milling has been studied by x-ray diffraction and Mossbauer spectroscopy. After around 19 h of milling FeS2 and FeS havebeen formed. By further milling the FeS compound becomes dominating and only Fe......S with an average crystallite size of about 10 nm was observed after milling times longer than 67 h. Mossbauer spectra obtained with applied fields show that the particles are antiferromagnetic or have a strongly canted spin structure....

  9. (YSZ) powders

    Indian Academy of Sciences (India)

    Unknown

    109–114. © Indian Academy of Sciences. 109 ... Materials Science Division, Bhabha Atomic Research Centre, Mumbai 400 085, India .... pensions of 900°C calcined YSZ powders. .... The sintered density data of the compacts (sintered at.

  10. Structure and magnetic properties of nanocrystalline Fe75Si25 powders prepared by mechanical alloying

    International Nuclear Information System (INIS)

    Kalita, M.P.C.; Perumal, A.; Srinivasan, A.

    2008-01-01

    Nanocrystalline Fe 75 Si 25 powders were prepared by mechanical alloying in a planetary ball mill. The evolution of the microstructure and magnetic properties during the milling process were studied by X-ray diffraction, scanning electron microscope and vibrating sample magnetometer measurements. The evolution of non-equilibrium solid solution Fe (Si) during milling was accompanied by refinement of crystallite size down to 10 nm and the introduction of high density of dislocations of the order of 10 17 m -2 . During the milling process, Fe sites get substituted by Si. This structural change and the resulting disorder are reflected in the lattice parameters and average magnetic moment of the powders milled for various time periods. A progressive increase of coercivity was also observed with increasing milling time. The increase of coercivity could be attributed to the introduction of dislocations and reduction of powder particle size as a function of milling time

  11. Fabrication mechanism of FeSe superconductors with high-energy ball milling aided sintering process

    International Nuclear Information System (INIS)

    Zhang, Shengnan; Liu, Jixing; Feng, Jianqing; Wang, Yao; Ma, Xiaobo; Li, Chengshan; Zhang, Pingxiang

    2015-01-01

    FeSe Superconducting bulks with high content of superconducting PbO-type β-FeSe phase were prepared with high-energy ball milling (HEBM) aided sintering process. During this process, precursor powders with certain Fe/Se ratio were ball milled first then sintered. The influences of HEBM process as well as initial Fe/Se ratio on the phase evolution process were systematically discussed. With HEBM process and proper initial Fe/Se ratio, the formation of non-superconducting hexagonal δ-FeSe phase were effectively avoided. FeSe bulk with the critical temperature of 9.0 K was obtained through a simple one-step sintering process with lower sintering temperature. Meanwhile, the phase evolution mechanism of the HEBM precursor powders during sintering was deduced based on both the thermodynamic analysis and step-by-step sintering results. The key function of the HEBM process was to provide a high uniformity of chemical composition distribution, thus to successfully avoide the formation of intermediate product during sintering, including FeSe 2 and Fe 7 Se 8 . Therefore, the fundamental principal for the synthesis of FeSe superconductors were concluded as: HEBM aided sintering process, with the sintering temperature of >635 °C and a slow cooling process. - Highlights: • A novel synthesis technique was developed for FeSe based superconductors. • FeSe bulks with high Tc and high β-FeSe phase content has been obtained. • Phase evolution process for the HEBM aided sintering process was proposed

  12. C, N co-doped TiO{sub 2}/TiC{sub 0.7}N{sub 0.3} composite coatings prepared from TiC{sub 0.7}N{sub 0.3} powder using ball milling followed by oxidation

    Energy Technology Data Exchange (ETDEWEB)

    Hao, Liang, E-mail: haoliang@tust.edu.cn [Tianjin Key Lab of Integrated Design and On-line Monitoring for Light Industry & Food Machinery and Equipment, Tianjin (China); College of Mechanical Engineering, Tianjin University of Science & Technology, No. 1038 Dagu Nanlu, Hexi District, Tianjin 300222 (China); Wang, Zhenwei, E-mail: 1004329228@qq.com [School of Naval Architecture and Ocean Engineering, Harbin Institute of Technology, Weihai, No. 2, Wenhua West Road, Weihai 264209 (China); Zheng, Yaoqing, E-mail: 13612177268@163.com [College of Mechanical Engineering, Tianjin University of Science & Technology, No. 1038 Dagu Nanlu, Hexi District, Tianjin 300222 (China); Li, Qianqian, E-mail: 1482471595@qq.com [College of Mechanical Engineering, Tianjin University of Science & Technology, No. 1038 Dagu Nanlu, Hexi District, Tianjin 300222 (China); Guan, Sujun, E-mail: sujunguan1221@gmail.com [College of Mechanical Engineering & Graduate School, Chiba University, 1-33, Yayoi-cho, Inage-ku, Chiba 263-8522 (Japan); Zhao, Qian, E-mail: zhaoqian@tust.edu.cn [Tianjin Key Lab of Integrated Design and On-line Monitoring for Light Industry & Food Machinery and Equipment, Tianjin (China); College of Mechanical Engineering, Tianjin University of Science & Technology, No. 1038 Dagu Nanlu, Hexi District, Tianjin 300222 (China); Cheng, Lijun, E-mail: chenglijun@tust.edu.cn [Tianjin Key Lab of Integrated Design and On-line Monitoring for Light Industry & Food Machinery and Equipment, Tianjin (China); College of Mechanical Engineering, Tianjin University of Science & Technology, No. 1038 Dagu Nanlu, Hexi District, Tianjin 300222 (China); Lu, Yun, E-mail: luyun@faculty.chiba-u.jp [College of Mechanical Engineering & Graduate School, Chiba University, 1-33, Yayoi-cho, Inage-ku, Chiba 263-8522 (Japan); Liu, Jizi, E-mail: jzliu@njust.edu.cn [Herbert Gleiter Institute of Nanoscience, Nanjing University of Science and Technology, No. 200, Xiaolingwei Street, Nanjing 210094 (China)

    2017-01-01

    Highlights: • TiO{sub 2}/TiC{sub 0.7}N{sub 0.3} coatings were prepared by ball milling followed by oxidation. • In situ co-doping of C and N with simultaneous TiO{sub 2} formation was observed. • Improved photocatalytic activity under UV/visible light was noticed. • Synergism in co-doping and heterojunction formation promoted carrier separation. - Abstract: Ball milling followed by heat oxidation was used to prepared C, N co-doped TiO{sub 2} coatings on the surfaces of Al{sub 2}O{sub 3} balls from TiC{sub 0.7}N{sub 0.3} powder. The as-prepared coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and ultraviolet-visible spectrophotometer (UV–vis). The results show that continuous TiC{sub 0.7}N{sub 0.3} coatings were formed after ball milling. C, N co-doped TiO{sub 2}/TiC{sub 0.7}N{sub 0.3} composite coatings were prepared after the direct oxidization of TiC{sub 0.7}N{sub 0.3} coatings in the atmosphere. However, TiO{sub 2} was hardly formed in the surface layer of TiC{sub 0.7}N{sub 0.3} coatings within a depth less than 10 nm during the heat oxidation of TiC{sub 0.7}N{sub 0.3} coatings in carbon powder. Meanwhile, the photocatalytic activity evaluation of these coatings was conducted under the irradiation of UV and visible light. All the coatings showed photocatalytic activity in the degradation of MB no matter under the irradiation of UV or visible light. The C, N co-doped TiO{sub 2}/TiC{sub 0.7}N{sub 0.3} composite coatings showed the most excellent performance. The enhancement under visible light irradiation should attribute to the co-doping of carbon and nitrogen, which enhances the absorption of visible light. The improvement of photocatalytic activity under UV irradiation should attribute to the synergistic effect of C, N co-doping, the formation of rutile-anatase mixed phases and the TiO{sub 2}/TiC{sub 0.7}N{sub 0.3} composite microstructure.

  13. Mechanical alloying and sitering of TI - 10WT.% MG powders

    CSIR Research Space (South Africa)

    Machio, Christopher N

    2009-06-01

    Full Text Available A Ti-10wt.%Mg powder alloy has been produced by mechanical alloying. Elemental powders of Ti and Mg were ball milled in a Zoz-Simoloyer CM01 for 16 and 20 hours under argon. Mechanical alloying was followed by XRD, SEM and particle size analysis...

  14. The influence of the milling environment on the sintered structure of a W-Cu composite

    International Nuclear Information System (INIS)

    Costa, F.A.; Gomes, U.U.; Acchar, W.; Ambrozio Filho, F.; Silva, A.G.P.; Lima, S.J.G.

    2009-01-01

    This work reports an investigation about the influence of the environment of milling on the characteristics of the powders and on the structure and density of sintered samples made of these powders. Mixtures of composition W-30wt%Cu were milled for 51 hours in a high energy planetary mill in dry and wet (cyclohexane) conditions. The milled powders have composite particles. The powders were pressed and sintered at 1050 deg, 1150 deg and 1200 deg C under flowing hydrogen. The isothermal times were 0 minutes for the first two temperatures and 60 minutes for the latter. The samples reached around 95% of relative density. The powders were characterized by means of XRD and SEM. The sintered samples were characterized by means of SEM, optical microscopy and density measurement. (author)

  15. Barium Ferrite Ball Milled in Vacuum

    International Nuclear Information System (INIS)

    Campbell, S.J.; Wu, E.; Kaczmarek, W.A.; Wang, G.

    1998-01-01

    The structural and magnetic behaviour of BaFe 12 O 19 subjected to milling in vacuum for 1000 h has been investigated by x-ray powder diffraction and Moessbauer effect spectroscopy techniques. Pronounced structural disorder is obtained along with partial decomposition of BaFe 12 O 19 to α-Fe 2 O 3 and evidence for superparamagnetic relaxation effects due to the fine particles produced on milling. Restoration of the fully crystallised BaFe 12 O 19 structure on annealing at 1000 deg. C is accompanied by a six fold enhancement in the magnetic coercivity. This behaviour is linked with the fine crystallites

  16. Effect of La{sub 0.8}Sr{sub 0.2}MnO{sub 3} powder addition in the precursor solution on the properties of cathode films deposited by spray pyrolysis

    Energy Technology Data Exchange (ETDEWEB)

    Silva, Caio Luis Santos; Rangel, Maria do Carmo, E-mail: clssilva@ufba.br, E-mail: mcarmov@ufba.br [Universidade Federal da Bahia (UFBA), Salvador, BA (Brazil). Grupo de Estudo em Cinetica e Catalise; Gama, Leonardo Marques; Paes Junior, Herval Ramos, E-mail: leonardo.m.gama@gmail.com, E-mail: herval@uenf.br [Universidade Estadual do Norte Fluminense Darcy Ribeiro (UENF), Campos dos Goytacazes, RJ (Brazil). Laboratorio de Materiais Avancados; Santos, Jacqueline Amanda Figueiredo dos; Domingues, Rosana Zacarias, E-mail: jac.amanda28@gmail.com, E-mail: rosanazd@ufmg.br [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte, MG (Brazil). Laboratorio de Materiais e Pilhas a Combustivel

    2017-01-15

    Films of lanthanum strontium manganite, LSM (La{sub 0.8}Sr{sub 0.2}MnO{sub 3}) were deposited on yttria stabilized zirconia (YSZ) substrates by different methods aiming to establish the most suitable route to prepare cathodes for solid oxide fuel cells (SOFC). Samples were obtained by using a solution of lanthanum, strontium and manganese nitrates or a dispersion of the LSM powder in this solution. Both commercial and synthesized LSM powders were used, the last one obtained by amorphous citrate method. The films were deposited by spray pyrolysis on YSZ substrates prepared by uniaxial and isostatic pressing. Samples were characterized by scanning electron microscopy, confocal laser scanning microscopy, X-ray diffraction and two-probe conductivity measurements. The area specific resistance and relaxation to cathodic activation were measured by electrochemical impedance spectroscopy. The substrate obtained by uniaxial pressing and the commercial LSM produced films with the highest amount of surface cracks. The film obtained from the suspension showed area specific resistance and activation energy lower than the other produced from the solution. For both samples, the cathodic activation process resulted in an initial reduction of the total resistance of around 20%, the sample produced from the suspension being more resistant to relaxation. Therefore, the LSM suspension is more suitable than the salts solution for preparing films by spray pyrolysis on YSZ substrates to obtain efficient cathodes for SOFC. (author)

  17. Synthesis of yttria powders by electrospray pyrolysis

    International Nuclear Information System (INIS)

    Rulison, A.J.; Flagan, R.C.

    1994-01-01

    Electrospray atomization of high-concentration (∼400 g/L) chemical precursor solutions was applied to the synthesis of yttria powders. Conditions were found which led to high-quality powders, composed of dense, spheroidal, submicrometer, and nanocrystalline oxide particles. The precursor solutions were hydrated yttrium nitrates dissolved in n-propyl alcohol at concentrations ranging from 44.1 to 455 g/L. Electrospray atomization produced submicrometer precursor droplets which were dispersed in air and carried through an electric furnace for thermal decomposition at 500 C for several seconds residence time. X-ray powder diffraction patterns indicated the expected cubic phase. Transmission electron micrographs showed that the particle structure varied with solution composition, ranging from hollow, inflated spheres for 6-hydrated nitrates to dense spheroids for 5-hydrated nitrates. The use of 6-hydrated nitrates in the solutions appeared to form particle surfaces which were impermeable to alcohol vapor evolved during thermal decomposition, leading to hollow, inflated spheres

  18. The magnetic properties of powdered and compacted microcrystalline permalloy

    International Nuclear Information System (INIS)

    Kollar, P.; Oleksakova, D.; Fuezer, J.; Kovac, J.; Roth, S.; Polanski, K.

    2007-01-01

    The aim of this work is to investigate the magnetic properties of powdered and compacted microcrystalline Ni-Fe (81 wt% of Ni) permalloy. It was found by investigating the influence of mechanical milling on the magnetic properties of powder samples prepared by milling of the ribbon that the alloy remains a solid solution with stable structure during the whole milling process. With decreasing particle size the rotation of magnetization vector gradually becomes dominant magnetization process and thus coercivity increases. After compaction of the powder by uniaxial hot pressing the magnetic contact between powder particles is recreated and for resulting bulk the displacement of the domain walls becomes dominant magnetization process with coercivity of 11 A/m (comparable with the coercivity of conventional permalloy)

  19. Powder diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Hart, M.

    1995-12-31

    the importance of x-ray powder diffraction as an analytical tool for phase identification of materials was first pointed out by Debye and Scherrer in Germany and, quite independently, by Hull in the US. Three distinct periods of evolution lead to ubiquitous application in many fields of science and technology. In the first period, until the mid-1940`s, applications were and developed covering broad categories of materials including inorganic materials, minerals, ceramics, metals, alloys, organic materials and polymers. During this formative period, the concept of quantitative phase analysis was demonstrated. In the second period there followed the blossoming of technology and commercial instruments became widely used. The history is well summarized by Parrish and by Langford and Loueer. By 1980 there were probably 10,000 powder diffractometers in routine use, making it the most widely used of all x-ray crystallographic instruments. In the third, present, period data bases became firmly established and sophisticated pattern fitting and recognition software made many aspects of powder diffraction analysis routine. High resolution, tunable powder diffractometers were developed at sources of synchrotron radiation. The tunability of the spectrum made it possible to exploit all the subtleties of x-ray spectroscopy in diffraction experiments.

  20. Powder diffraction

    International Nuclear Information System (INIS)

    Hart, M.

    1995-01-01

    The importance of x-ray powder diffraction as an analytical tool for phase identification of materials was first pointed out by Debye and Scherrer in Germany and, quite independently, by Hull in the US. Three distinct periods of evolution lead to ubiquitous application in many fields of science and technology. In the first period, until the mid-1940's, applications were and developed covering broad categories of materials including inorganic materials, minerals, ceramics, metals, alloys, organic materials and polymers. During this formative period, the concept of quantitative phase analysis was demonstrated. In the second period there followed the blossoming of technology and commercial instruments became widely used. The history is well summarized by Parrish and by Langford and Loueer. By 1980 there were probably 10,000 powder diffractometers in routine use, making it the most widely used of all x-ray crystallographic instruments. In the third, present, period data bases became firmly established and sophisticated pattern fitting and recognition software made many aspects of powder diffraction analysis routine. High resolution, tunable powder diffractometers were developed at sources of synchrotron radiation. The tunability of the spectrum made it possible to exploit all the subtleties of x-ray spectroscopy in diffraction experiments

  1. Powder diffractometry

    International Nuclear Information System (INIS)

    Doucet, J.

    1983-01-01

    The new possibilities openned by the synchrotron radiation in the powder diffractometry techniques are presented. This technique is described in a general manner and some aspects which can be developed with the use of the synchrotron radiation are analyzed. (L.C.) [pt

  2. Effect of zirconia content and powder processing mechanical properties of gelcasted ZTA composite

    International Nuclear Information System (INIS)

    Khoshkalam, M.; Faghihi-Sani, M.A.; Nojoomi, A.

    2013-01-01

    Addition of fine zirconia particles in the alumina matrix in order to produce ZTA composite is a well-known method for improving the mechanical properties of alumina ceramics such as flexural strength and fracture toughness. Increasing homogeneity and reducing alumina grain size are two key factors for achieving proper mechanical properties in this ceramic matrix composite. In this work two batches of ZTA powder precursor were prepared through mixing of alumina and zirconia by ball milling and in situ synthesis of ZTA composite via solution combustion method. The bending strength testing samples were fabricated through gel-casting process. The effects of different powder processing methods as well as zirconia contents on microstructural homogeneity and mechanical properties of ZTA composites were investigated. The samples produced by solution combustion synthesized powder yielded higher homogeneity, finer microstructure and higher flexural strength. Results showed an upswing in the fracture toughness for the synthesized samples even up to 20 vol% zirconia, while the mixed samples depicted optimum fracture toughness in 10 vol% zirconia content. (author)

  3. Effect of Initial ZrOCl₂ Concentration on the Homogeneous Precipitation of Nanoscale 3Y-TZP Powder.

    Science.gov (United States)

    Jeong, Hyeongdo; Lee, Jong Kook

    2018-09-01

    Nanoscale yttria-stabilized zirconia (Y-TZP) powder was synthesized by homogeneous precipitation via urea hydrolysis, and the influence of a dispersing agent and the initial ZrOCl2 concentration on the powder characteristics was investigated. A precipitated gel was obtained from the reaction of the precursor solution with zirconium oxychloride, yttrium chloride, and urea with heating at 110 °C for 5 h. The initial ZrOCl2 concentration was controlled from 0.25 to 1 M. To observe the effect of adding a dispersing agent on the agglomeration of primary particles, we used two starting compositions, one with and the other without a dispersing agent, ammonium polymethacrylate. Two crystalline powders were obtained after drying, calcination, and milling the gel, and we investigated the powder characteristics, such as particle agglomeration, the specific surface area, the microstructure, and phase composition. Two scales of agglomerates were observed in the particle size distribution, namely, 190 to 362 nm at the primary scale and 1.6-4.0 μm at the secondary scale. The amount of secondary agglomerate increased from 6 to 20 vol% with the increasing initial ZrOCl2 concentration. The size of both types of agglomerate and the amount of secondary agglomerates decreased due to the addition of the dispersing agent, especially the primary agglomerate size. The sintered density and microstructure of Y-TZP were affected by the agglomeration behavior, especially the amount of secondary agglomerates.

  4. Microstructural characteristics and mechanical properties of carbon nanotube reinforced aluminum alloy composites produced by ball milling

    International Nuclear Information System (INIS)

    Raviathul Basariya, M.; Srivastava, V.C.; Mukhopadhyay, N.K.

    2014-01-01

    Highlights: • 6082 Al alloy composite with 2 wt% multiwalled carbon nanotubes prepared by milling. • Effect of milling time on structure and property evolution has been studied. • The reinforced composite powders showed a drastic crystallite size refinement. • The presence of carbon nanotube led to a two fold increase in the hardness and modulus. • The composite powder showed good thermal stability studied by DTA. - Abstract: The influence of milling time on the structure, morphology and thermal stability of multi-walled carbon nanotubes (MWCNTs) reinforced EN AW6082 aluminum alloy powders has been studied. After structural and microstructural characterization of the mechanically milled powders micro- and nano-hardness of the composite powder particles were evaluated. The morphological and X-ray diffraction studies on the milled powders revealed that the carbon nanotubes (CNTs) were uniformly distributed and embedded within the aluminum matrix. No reaction products were detected even after long milling up to 50 h. Nanotubes became shorter in length as they fractured under the impact and shearing action during the milling process. A high hardness of about 436 ± 52 HV is achieved for the milled powders, due to the addition of MWCNTs, after milling for 50 h. The increased elastic modulus and nanohardness can be attributed to the finer grain size evolved during high energy ball milling and to the uniform distribution of hard CNTs in the Al-alloy matrix. The hardness values of the composite as well as the matrix alloy compares well with that predicted by the Hall–Petch relationship

  5. Biomass torrefaction mill

    Science.gov (United States)

    Sprouse, Kenneth M.

    2016-05-17

    A biomass torrefaction system includes a mill which receives a raw biomass feedstock and operates at temperatures above 400 F (204 C) to generate a dusty flue gas which contains a milled biomass product.

  6. Effect of milling on the magnetic properties of Al–Mn obtained by mechanical alloying

    International Nuclear Information System (INIS)

    Betancourt, Mirna; Silva, Pedro; Gonzalez, Gema

    2012-01-01

    Highlights: ► Al–42 at.% Mn transforms to α-Mn(Al) by mechanical milling after 5 h of milling. ► Transformation to nano β-Mn is reached after 50 h of milling with 6 nm grain size. ► Milling strongly affects magnetic behavior. - Abstract: Al–Mn powders were prepared to obtain the compound Mn 42 Al 58 by mechanical alloying. The powders were milled during different periods (1 h, 5 h, 11.5 h, 15 h, 20 h and 50 h) using a SPEX 8000 mixer mill in nitrogen atmosphere. The materials were characterized by X-ray diffraction (XRD) and magnetic properties at room temperature, using a vibrating sample magnetometer (VSM). XRD shows partial transformation to α-Mn after only 1 h of milling and a mixture of α-Mn and β-Mn after 11.5 h of milling and further milling resulted in transformation to β-Mn phase with a grain size of 6 nm after 50 h. The change in magnetic properties with milling time is quite dramatic, from a ferromagnetic behavior for α-Mn(Al) to paramagnetic after 11.5 h of milling and showing again ferromagnetic behavior, with a strong increase of magnetization values of 5.5 emu/g, after 50 h of milling with formation of β-Mn(Al).

  7. The influence of milling on the dissolution performance of simvastatin

    DEFF Research Database (Denmark)

    Zimper, Ulrike; Aaltonen, Jaakko; Krauel-Goellner, Karen

    2012-01-01

    properties such as solubility and dissolution rate and, therefore, process induced solid state modifications need to be monitored. The aim of this study was two-fold: firstly, to investigate the dissolution rates of milled and unmilled simvastatin; and secondly, to screen for the main milling factors......, as well as factor interactions in a dry ball milling process using simvastatin as model drug, and to optimize the milling procedure with regard to the opposing responses particle size and process induced disorder by application of a central composite face centered design. Particle size was assessed...... by scanning electron microscopy (SEM) and image analysis. Process induced disorder was determined by partial least squares (PLS) regression modeling of respective X-ray powder diffractograms (XRPD) and Raman spectra. Valid and significant quadratic models were built. The investigated milling factors were...

  8. Synthesis of ferrite nanoparticle by milling process for preparation of single domain magnet

    International Nuclear Information System (INIS)

    Suryadi; Hasbiyallah; Agus S W; Nurul TR; Budhy Kurniawan

    2009-01-01

    Study of ferrite nanoparticle synthesis for preparation of single domain magnet by milling of scrap magnet material have been done. Sample preparation were done using disk mill continued with high energy milling (HEM). Some powder were taken after 5, 10 dan 20 hours milling using HEM-E3D. The powder were then characterized using X-Ray Fluorescence (XRF), X-Ray Diffractometer (XRD) and Scanning Electron Microscope (SEM). XRF characterization result, confirmed by XRD analysis result, showed that the sample are of Strontium ferrite phase. Microstructure analysis result showed the occurrence of grain refining process of ferrite particle with increasing of milling time. Particle having size of nanometers successfully obtained, although in unhomogeneous distribution. Magnetic properties characterization result showed the increasing of hysteresis curve area of sample for longer milling time and sintering process. (author)

  9. Powder technology

    International Nuclear Information System (INIS)

    Agueda, Horacio

    1989-01-01

    Powder technology is experiencing nowadays a great development and has broad application in different fields: nuclear energy, medicine, new energy sources, industrial and home artifacts, etc. Ceramic materials are of daily use as tableware and also in the building industry (bricks, tiles, etc.). However, in machine construction its utilization is not so common. The same happens with metals: powder metallurgy is employed less than traditional metal forming techniques. Both cases deal with powder technology and the forming techniques as far as the final consolidation through sintering processes are very similar. There are many different methods and techniques in the forming stage: cold-pressing, slip casting, injection molding, extrusion molding, isostatic pressing, hot-pressing (which involves also the final consolidation step), etc. This variety allows to obtain almost any desired form no matter how complex it could be. Some applications are very specific as in the case of UO 2 pellets (used as nuclear fuels) but with the same technique and other materials, it is possible to manufacture a great number of different products. This work shows the characteristics and behaviour of two magnetic ceramic materials (ferrites) fabricated in the laboratory of the Applied Research Division of the Bariloche Atomic Center for different purposes. Other materials and products made with the same method are also mentioned. Likewise, densities and shrinkage obtained by different methods of forming (cold-pressing, injection molding, slip casting and extrusion molding) using high-purity alumina (99.5% Al 2 O 3 ). Finally, different applications of such methods are given. (Author) [es

  10. Effect of milling time on microstructure and properties of Nano-titanium polymer by high-energy ball milling

    Science.gov (United States)

    Wang, Bo; Wei, Shicheng; Wang, Yujiang; Liang, Yi; Guo, Lei; Xue, Junfeng; Pan, Fusheng; Tang, Aitao; Chen, Xianhua; Xu, Binshi

    2018-03-01

    Nano-titanium (Nano-Ti) was prepared by high-energy ball milling from pure Ti power and grinding agents (Epoxy resin) at room temperature. The effect of milling time on structure and properties of Nano-Ti polymer were investigated systematically. The results show that high-energy ball milling is an effective way to produce Nano-Ti polymer. The dispersion stability and compatibility between Ti power and grinding agents are improved by prolonging the milling time at a certain degree, that is to say, the optimization milling time is 240 min. The particle size of Ti powder and the diffraction peaks intensity of Ti decrease obviously as the milling time increases due to the compression stress, shear friction and other mechanical forces are formed during ball milling. FT-IR result displays that the wavenumber of all the bands move to lower wavenumber after ball milling, and the epoxy ring is open. The system internal energy rises owing to the broken epoxy group and much more Nano-Ti is formed to promote the grafting reaction between Nano-Ti and epoxy resin. The results from TEM and XPS also prove that. And the grafting ration is maximum as the milling time is 240 min, the mass loss ratio is 17.53%.

  11. ZnO nanoparticles obtained by ball milling technique: Structural, micro-structure, optical and photo-catalytic properties

    Energy Technology Data Exchange (ETDEWEB)

    Balamurugan, S., E-mail: scandium.chemistry@gmail.com; Joy, Josny; Godwin, M. Anto; Selvamani, S.; Raja, T. S. Gokul [Advanced Nanomaterials Research Laboratory, Department of Nanotechnology, Noorul Islam Centre for Higher Education, Thuckalay, Kumaracoil - 629 180 (India)

    2016-05-23

    The ZnO nanoparticles were obtained by ball milling of commercial grade ZnO powder at 250 rpm for 20 h and studied their structural, micro-structure, optical and photo-catalytic properties. Due to ball milling significant decrease in lattice parameters and average crystalline size is noticed for the as-milled ZnO nano powder. The HRSEM images of the as-milled powder consist of agglomerated fine spherical nanoparticles in the range of ~10-20 nm. The room temperature PL spectrum of as-milled ZnO nano powder excited under 320 nm reveals two emission bands at ~406 nm (violet emission) and ~639 nm (green emission). Interestingly about 98 % of photo degradation of methylene (MB) by the ZnO catalyst is achieved at 100 minutes of solar light irradiation.

  12. Studies on the structure of zirconium carbide powders subjected to vibration grinding

    International Nuclear Information System (INIS)

    Kravchik, A.E.; Neshpor, V.S.

    1976-01-01

    The present work is a study of zirconium carbide powders subjected to vibratory milling in various media. The powders were comminuted in air (dry milling), benzene, trichloroethylene, and distilled water. The milling time was 10-160 h. The chemical compositions, specific surfaces, and crystal lattice parameters of the powder in the initial condition and after milling for 100 h in the various media are given. Vibratory milling of zirconium carbide powder can be successfully performed in benzene. Comminution in benzene enables a large specific surface to be attained, with practically no chemical reaction between the medium and the milling products. In milling in trichloroethylene the latter decomposes, with the formation of hydrochloric acid which reacts with the milling products. In a study of the fine structure parameters of zirconium carbide in the , , and directions the smallest crystal lattice strains and block sizes were observed in the direction. This may be taken as evidence that under such disintegration conditions the (110) planes constitute cleavage planes. An evaluation of internal and surface energies established that the strained crystal lattice energy reaches values which must be allowed for in any subsequent uses of the powder

  13. Set up of Uranium-Molybdenum powder production (HMD process)

    International Nuclear Information System (INIS)

    Lopez, Marisol; Pasqualini, Enrique E.; Gonzalez, Alfredo G.

    2003-01-01

    Powder metallurgy offers different alternatives for the production of Uranium-Molybdenum (UMo) alloy powder in sizes smaller than 150 microns. This powder is intended to be used as a dispersion fuel in an aluminum matrix for research, testing and radioisotopes production reactors (MTR). A particular process of massive hydriding the UMo alloy in gamma phase has been developed. This work describes the final adjustments of process variables to obtain UMo powder by hydriding-milling-de hydriding (HMD) and its capability for industrial scaling up. (author)

  14. Synthesis of Ni-YSZ cermet for an electrode of high temperature electrolysis by high energy ball milling

    International Nuclear Information System (INIS)

    Hong, H.S.; Chae, U.S.; Park, K.M.; Choo, S.T.

    2005-01-01

    Ni/YSZ composites for a cathode that can be used in high temperature electrolysis were prepared by ball milling of Ni and YSZ powder. Ball milling was performed in a dry process and in ethanol. The microstructure and electrical conductivity of the composites were examined by XRD, SEM, TEM and a 4-point probe. XRD patterns for both the dry and wet ball-milled powders showed that the composites were composed of crystalline Ni and YSZ particles. The patterns did not change with increases in the milling time up to 48 h. Dry-milling slightly increased the average particle size compared to starting Ni particles, but little change in the particle size was observed with the increase in milling time. On the other hand, the wet-milling reduced the average size and the increasing milling time induced a further decrease in the particle size. After cold-pressing and annealing at 900 C for 2 h, the dry-milled powder exhibited high stability against Ni sintering so that the particle size changed little, but the particle size increased in the wet-milled powder. The electrical conductivity increased after sintering at 900 C. Particles from the dry and wet process became denser and contacted closer after sintering, providing better electron migration paths. (orig.)

  15. Ammonia synthesis over multi-promoted iron catalysts obtained by high-energy ball-milling

    DEFF Research Database (Denmark)

    Jacobsen, C.J.H.; Jiang, Jianzhong; Mørup, Steen

    1999-01-01

    The feasibility of producing ammonia synthesis catalysts from high-energy ball-milling of a simple mixture of the constituent oxides has been investigated. The effect of ball-milling the fused oxidic precursor of the industrial KM1 ammonia synthesis catalyst has also been studied. The results show...

  16. Characteristics of Cu–Al2O3 composites of various starting particle size obtained by high-energy milling

    Directory of Open Access Journals (Sweden)

    VIŠESLAVA RAJKOVIĆ

    2009-05-01

    Full Text Available The powder Cu– Al2O3 composites were produced by high-energy milling. Various combinations of particle size and mixtures and approximately constant amount of Al2O3 were used as the starting materials. These powders were separately milled in air for up to 20 h in a planetary ball mill. The copper matrix was reinforced by internal oxidation and mechanical alloying. During the milling, internal oxidation of pre-alloyed Cu-2 mass %-Al powder generated 3.7 mass % Al2O3 nano-sized particles finely dispersed in the copper matrix. The effect of different size of the starting copper and Al2O3 powder particles on the lattice parameter, lattice distortion and grain size, as well as on the size, morphology and microstructure of the Cu– Al2O3 composite powder particles was studied.

  17. Ionospheric earthquake precursors

    International Nuclear Information System (INIS)

    Bulachenko, A.L.; Oraevskij, V.N.; Pokhotelov, O.A.; Sorokin, V.N.; Strakhov, V.N.; Chmyrev, V.M.

    1996-01-01

    Results of experimental study on ionospheric earthquake precursors, program development on processes in the earthquake focus and physical mechanisms of formation of various type precursors are considered. Composition of experimental cosmic system for earthquake precursors monitoring is determined. 36 refs., 5 figs

  18. Uranium Mill Tailings Management

    International Nuclear Information System (INIS)

    Nelson, J.D.

    1982-01-01

    This book presents the papers given at the Fifth Symposium on Uranium Mill Tailings Management. Advances made with regard to uranium mill tailings management, environmental effects, regulations, and reclamation are reviewed. Topics considered include tailings management and design (e.g., the Uranium Mill Tailings Remedial Action Project, environmental standards for uranium mill tailings disposal), surface stabilization (e.g., the long-term stability of tailings, long-term rock durability), radiological aspects (e.g. the radioactive composition of airborne particulates), contaminant migration (e.g., chemical transport beneath a uranium mill tailings pile, the interaction of acidic leachate with soils), radon control and covers (e.g., radon emanation characteristics, designing surface covers for inactive uranium mill tailings), and seepage and liners (e.g., hydrologic observations, liner requirements)

  19. Effect of Milling Condition on the Microstructure and the Properties of Nano structured Copper Tungsten Carbide Composite

    International Nuclear Information System (INIS)

    Mahani Yusoff; Zuhailawati Hussain

    2011-01-01

    In this work, in-situ Cu-WC composite has been fabricated by high energy milling followed by sintering. Cu, W and C mixture were mechanically alloyed in a planetary ball mill for 40 h at various milling speeds. Cu-W-C composite powders were cold compacted and sintered in argon ambient. Milled powder and sintered Cu-W-C composite were characterized in terms of Xray diffraction (XRD), field emission scanning electron microscopy (FESEM) and its properties. The result showed that carbide phases are only detected after sintering process. Greater amount of grain refinement during milling generates very high internal strain which reduced Cu crystallite size. It was found that formation of metastable, W 2 C has taken place before the formation of WC. With the presence of WC, the composite become increasingly harden with the increased of milling speed. Increasing milling speed also found to lower the electrical conductivity. (author)

  20. FM Interviews: Stephanie Mills

    OpenAIRE

    Valauskas, Edward

    2002-01-01

    Stephanie Mills is an author, editor, lecturer and ecological activist who has concerned herself with the fate of the earth and humanity since 1969, when her commencement address at Mills College in Oakland, Calif., drew the attention of a nation. Her speech, which the New York Times called "perhaps the most anguished statement" of the year's crop of valedictory speeches, predicted a bleak future. According to Mills, humanity was destined for suicide, the result of overpopulation and overuse ...

  1. Effect of ball mill treatment on kinetics of amorphous Ni78Si10B12 alloy crystallization

    International Nuclear Information System (INIS)

    Tomilin, I.A.; Mochalova, T.Yu.; Kaloshkin, S.D.; Kostyukovich, T.G.; Lopatina, E.A.

    1993-01-01

    The effect of the parameters of Ni 78 Si 10 B 12 alloy amorphous strip milling in a ball planetary mill on the stability of powder amorphous state, crytallization kinetics and dispersity is studied by the methods of differential scanning microcaloremetry and X-ray diffraction analysis. Energy intensity of milling conditions is assessed. An increase of input energy results in a decrease of activation energy of powder crystallization. Strip milling parameters which enable to avaintain the amorphous state of the material are determined

  2. Synthesis and Characterization of Nanocrystalline Al-20 at. % Cu Powders Produced by Mechanical Alloying

    Directory of Open Access Journals (Sweden)

    Molka Ben Makhlouf

    2016-06-01

    Full Text Available Mechanical alloying is a powder processing technique used to process materials farther from equilibrium state. This technique is mainly used to process difficult-to-alloy materials in which the solid solubility is limited and to process materials where nonequilibrium phases cannot be produced at room temperature through conventional processing techniques. This work deals with the microstructural properties of the Al-20 at. % Cu alloy prepared by high-energy ball milling of elemental aluminum and copper powders. The ball milling of powders was carried out in a planetary mill in order to obtain a nanostructured Al-20 at. % Cu alloy. The obtained powders were characterized using scanning electron microscopy (SEM, differential scanning calorimetry (DSC and X-ray diffraction (XRD. The structural modifications at different stages of the ball milling are investigated with X-ray diffraction. Several microstructure parameters such as the crystallite sizes, microstrains and lattice parameters are determined.

  3. Obtainment of the alloy Cu13Al4Ni using processed by powder metallurgy

    International Nuclear Information System (INIS)

    Grossi, L.J.; Damasceno, N.; Muterlle, P.V.

    2016-01-01

    The powder metallurgy is a technique environmentally advantageous that allows the production of many pieces, with a good superficial finishing and dimensional tolerance. For the production of pieces using technique, basics steps are carried out, as the characterization of powders, the mixing and homogenization, compacting and sintering. In this context, this work has as objective the obtainment of the Cu13Al4Ni alloy via powder metallurgy. For this, was made a high energy milling for 2, 4 and 8 hours. Then, the milled powder was compacted and posteriorly, sintered in an oven with controlled atmosphere. It was observed that the milling time affects directly in sintering of the pieces. The best results obtained were for the samples that were milled for 4 hours. This samples have showed 21, 52% of porosity and 6,382 g/cm³ of the density of sintered. (author)

  4. Discrete element method based scale-up model for material synthesis using ball milling

    Science.gov (United States)

    Santhanam, Priya Radhi

    Mechanical milling is a widely used technique for powder processing in various areas. In this work, a scale-up model for describing this ball milling process is developed. The thesis is a combination of experimental and modeling efforts. Initially, Discrete Element Model (DEM) is used to describe energy transfer from milling tools to the milled powder for shaker, planetary, and attritor mills. The rolling and static friction coefficients are determined experimentally. Computations predict a quasisteady rate of energy dissipation, E d, for each experimental configuration. It is proposed that the milling dose defined as a product of Ed and milling time, t, divided by the mass of milled powder, mp characterizes the milling progress independently of the milling device or milling conditions used. Once the milling dose is determined for one experimental configuration, it can be used to predict the milling time required to prepare the same material in any milling configuration, for which Ed is calculated. The concept is validated experimentally for DEM describing planetary and shaker mills. For attritor, the predicted Ed includes substantial contribution from milling tool interaction events with abnormally high forces (>103 N). The energy in such events is likely dissipated to heat or plastically deform milling tools rather than refine material. Indeed, DEM predictions for the attritor correlate with experiments when such events are ignored in the analysis. With an objective of obtaining real-time indicators of milling progress, power, torque, and rotation speed of the impeller of an attritor mill are measured during preparation of metal matrix composite powders in the subsequent portion of this thesis. Two material systems are selected and comparisons made between in-situ parameters and experimental milling progress indicators. It is established that real-time measurements can certainly be used to describe milling progress. However, they need to be interpreted carefully

  5. The influence of powder particle size on properties of Cu-Al2O3 composites

    Directory of Open Access Journals (Sweden)

    Rajković V.

    2009-01-01

    Full Text Available Inert gas atomized prealloyed copper powder containing 2 wt.% Al (average particle size ≈ 30 μm and a mixture consisting of copper (average particle sizes ≈ 15 μm and 30 μm and 4 wt.% of commercial Al2O3 powder particles (average particle size ≈ 0.75 μm were milled separately in a high-energy planetary ball mill up to 20 h in air. Milling was performed in order to strengthen the copper matrix by grain size refinement and Al2O3 particles. Milling in air of prealloyed copper powder promoted formation of finely dispersed nano-sized Al2O3 particles by internal oxidation. On the other side, composite powders with commercial micro-sized Al2O3 particles were obtained by mechanical alloying. Following milling, powders were treated in hydrogen at 400 0C for 1h in order to eliminate copper oxides formed on their surface during milling. Hot-pressing (800 0C for 3 h in argon at pressure of 35 MPa was used for compaction of milled powders. Hot-pressed composite compacts processed from 5 and 20 h milled powders were additionally subjected to high temperature exposure (800°C for 1 and 5h in argon in order to examine their thermal stability. The results were discussed in terms of the effects of different size of starting powders, the grain size refinement and different size of Al2O3 particles on strengthening, thermal stability and electrical conductivity of copper-based composites.

  6. Grinding Si3N4 Powder In Si3N4 Equipment

    Science.gov (United States)

    Herbell, Thomas P.; Freedman, Marc R.; Kiser, James D.

    1989-01-01

    Three methods of grinding compared. Report based on study of grinding silicon nitride powder in preparation for sintering into solid ceramic material. Attrition, vibratory, and ball mills lined with reaction-bonded silicon nitride tested. Rates of reduction of particle sizes and changes in chemical compositions of powders measured so grinding efficiences and increases in impurity contents from wear of mills and media evaluated for each technique.

  7. A study on thermal and mechanical properties of mechanically milled HDPE and PP

    International Nuclear Information System (INIS)

    Can, S.; Tan, S.

    2003-01-01

    In this study, mechanical mixing of HDPE and PP was performed via ball milling. Prepared compositions were 75/25 , 50/50 , 25/75 w/w HDPE/PP. Milling time and ball to powder ratio (B/P) were kept constant and system was cooled by adding solid CO 2 to improve the milling efficiency. To compare these systems with traditional methods, mixtures were also melt mixed by Brabender Plasti-Corder. Both milled and melt mixed systems were examined with DSC for thermal properties and tensile testing for mechanical properties Results are discussed by comparing milled , melt mixed and as-received polymers. It is observed that, unlike ball milled systems' in melt mixed systems mechanical properties are composition dependent. In addition , ball milling results in amorphization of both polymers and very high amounts of PP (75wt %) creates very amorphous HDPE structure. (Original)

  8. Formation and characterization of solid-solution (V,W,Ti)CN composite powder

    CSIR Research Space (South Africa)

    Bolokang, Amogelang S

    2017-04-01

    Full Text Available We report on the synthesis of a mixture of vanadium (V), tungsten (W), titanium (Ti) and carbon (C) mixture using ball milling in argon atmosphere. Thermal analysis of the milled powder showed an exothermic reaction at approximately 700°C...

  9. Microstructural evolution of ferritic steel powder during mechanical alloying with iron oxide

    Energy Technology Data Exchange (ETDEWEB)

    Wen, Yuren; Liu, Yong; Liu, Donghua; Tang, Bei [Central South Univ., State Key Lab. of Powder Metallurgy, Changsha (China); Liu, C.T. [The Hong Kong Polytechnic Univ., Dept. of Mechanical Engineering, Hong Kong (China)

    2011-02-15

    Mechanical alloying of mixed powders is of great importance for preparing oxide dispersion strengthened ferritic steels. In this study, the microstructural evolution of ferritic steel powder mixed with TiH{sub x}, YH{sub 2} and Fe{sub 2}O{sub 3} in the process of mechanical alloying is systematically investigated by using X-ray diffraction analysis, scanning electron microscopy, transmission electron microscopy and microhardness tests. It is found that titanium, yttrium hydrides and iron oxide are completely dissolved during milling, and homogeneous element distribution can be achieved after milling for 12 h. The disintegration of the composite powder particles occurs at 24 h and reaches the balance of welding and fracturing after 36 h. The oxygen content increases sharply with the disintegration of powder particles due to the absorption of oxygen at the solid/gas interface from the milling atmosphere, which is the main source of extra oxygen in the milled powder. Grain refinement down to nanometer level occurs due to the severe plastic deformation of particles; however, the grain size does not change much with further disintegration of particles. The hardness increases with milling time and then becomes stable during further milling. The study indicates that the addition of iron oxide and hydrides may be more beneficial for the dispersion and homogenization of chemical compositions in the powder mixture, thus shortening the mechanical alloying process. (orig.)

  10. Development of equipment for fabricating DUPIC fuel powder

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Ki Ho; Yang, M. S.; Park, J. J.; Lee, J. W.; Kim, J. H.; Cho, K. H.; Lee, D. Y.; Lee, Y. S.; Na, S. H

    1999-06-01

    The powder fabrication processes, as the first stage of manufacturing DUPIC (Direct Use of PWR spent fuel In CANDU) fuel, consist of the slitting of spent PWR fuel rods, REOX (Oxidation and REduction of Oxide Fuels) processing to produce the powder feedstock, the milling of the produced powder, the granulation of the milled powder, and the mixing of the granulated powder with pressing lubricants. All these processes should be conducted by remote means in a hot-cell environment where the direct human access is limited to the strictest minimum due to the high radioactivity. This report describe the development of the equipment for fabricating DUPIC fuel powder. These equipment are Slitting Machine, Oxidation and Reduction (OREOX) Furnace, Mill, Roll Compactor, and Mixer. Remote design concept was applied to all the equipment for use in the M6 hot-cell of the IMEF. Mechanical design considerations and capabilities of the equipment for remote operation and maintenance are presented. First prototypes were developed and installed in the DUPIC full scale mock-up and tested using a master-slave manipulator. Redesign and reconstruction were made on each equipment based on mock-up test results. The remote technology acquired through this research was utilized in developing other equipment for DUPIC fuel fabrication, thereby improving safety and increasing productivity. This technology could also be extended to the area of remote handling equipment development for use in hazardous environments. (author). 14 refs., 9 tabs., 21 figs.

  11. Development of equipment for fabricating DUPIC fuel powder

    International Nuclear Information System (INIS)

    Kim, Ki Ho; Yang, M. S.; Park, J. J.; Lee, J. W.; Kim, J. H.; Cho, K. H.; Lee, D. Y.; Lee, Y. S.; Na, S. H.

    1999-06-01

    The powder fabrication processes, as the first stage of manufacturing DUPIC (Direct Use of PWR spent fuel In CANDU) fuel, consist of the slitting of spent PWR fuel rods, REOX (Oxidation and REduction of Oxide Fuels) processing to produce the powder feedstock, the milling of the produced powder, the granulation of the milled powder, and the mixing of the granulated powder with pressing lubricants. All these processes should be conducted by remote means in a hot-cell environment where the direct human access is limited to the strictest minimum due to the high radioactivity. This report describe the development of the equipment for fabricating DUPIC fuel powder. These equipment are Slitting Machine, Oxidation and Reduction (OREOX) Furnace, Mill, Roll Compactor, and Mixer. Remote design concept was applied to all the equipment for use in the M6 hot-cell of the IMEF. Mechanical design considerations and capabilities of the equipment for remote operation and maintenance are presented. First prototypes were developed and installed in the DUPIC full scale mock-up and tested using a master-slave manipulator. Redesign and reconstruction were made on each equipment based on mock-up test results. The remote technology acquired through this research was utilized in developing other equipment for DUPIC fuel fabrication, thereby improving safety and increasing productivity. This technology could also be extended to the area of remote handling equipment development for use in hazardous environments. (author). 14 refs., 9 tabs., 21 figs

  12. Transforming from paramagnetism to room temperature ferromagnetism in CuO by ball milling

    Directory of Open Access Journals (Sweden)

    Daqiang Gao

    2011-12-01

    Full Text Available In this work, we experimentally demonstrate that it is possible to induce ferromagnetism in CuO by ball milling without any ferromagnetic dopant. The magnetic measurements indicate that paramagnetic CuO is driven to the ferromagnetic state at room temperature by ball milling gradually. The saturation magnetization of the milled powders is found to increase with expanding the milling time and then decrease by annealing under atmosphere. The fitted X-ray photoelectron spectroscopy results indicate that the observed induction and weaken of the ferromagnetism shows close relationship with the valence charged oxygen vacancies (Cu1+-VO in CuO.

  13. Amorphous phase formation in intermetallic Mg2Ni alloy synthesized by ethanol wet milling

    International Nuclear Information System (INIS)

    Wang, H.-W.; Chyou, S.-D.; Wang, S.-H.; Yang, M.-W.; Hsu, C.-Y.; Tien, H.-C.; Huang, N.-N.

    2009-01-01

    The hydriding/dehydriding properties of an intermetallic Mg 2 Ni alloy synthesized by wet ball milling in ethanol have been investigated. The appearance of the particle surface after different milling methods is one obvious difference. The alloyed powders prepared by either dry milling or wet milling under ethanol were characterized for phase content by X-ray diffractometer (XRD). The results show that two broad diffuse peaks, which are an ionic-organic-Mg amorphous material, appear in addition to the nickel element peaks. This unexpected amorphous phase has the special hydrogen absorbing/desorbing features.

  14. Effect of composition and heat treatment on the phase formation of mechanically alloyed Cr-B and Mo-B powders

    International Nuclear Information System (INIS)

    Wu, H M; Hu, C J; Pai, K Y

    2009-01-01

    Blended elemental Cr-B and Mo-B powders in atomic ratio of 67:33, 50:50, and 20:80 were subjected to mechanical alloying up to 60 h and subsequent heat treatment to investigate effect of composition and heat treatment on the phase formation of Cr-B and Mo-B powders. It was studied by X-ray diffraction and differential thermal analysis. Mechanical alloying these powder mixtures for 60 h leads essentially to a amorphous structure except for the Mo 20 B 80 powder, which creates a partially amorphous MoB 4 structure. Annealing at lower temperatures relieves the strains cumulative in the milled powders and creates no new phase. The structures obtained after annealing the milled powders at higher temperature vary and depend on the overall composition of the powder mixtures. Annealing the milled Mo-B powders having greater Mo content ends up with a dissociation reaction at higher temperature.

  15. Fabrication of Fe1.1Se0.5Te0.5 bulk by a high energy ball milling technique

    Science.gov (United States)

    Liu, Jixing; Li, Chengshan; Zhang, Shengnan; Feng, Jianqing; Zhang, Pingxiang; Zhou, Lian

    2017-11-01

    Fe1.1Se0.5Te0.5 superconducting bulks were successfully synthesized by a high energy ball milling (HEBM) aided sintering technique. Two advantages of this new technique have been revealed compared with traditional solid state sintering method. One is greatly increased the density of sintered bulks. It is because the precursor powders with β-Fe(Se, Te) and δ-Fe(Se, Te) were obtained directly by the HEBM process and without formation of liquid Se (and Te), which could avoid the huge volume expansion. The other is the obvious decrease of sintering temperature and dwell time due to the effective shortened length of diffusion paths. The superconducting critical temperature Tc of 14.2 K in our sample is comparable with those in previous reports, and further optimization of chemical composition is on the way.

  16. Efek Waktu Wet Milling dan Suhu Annealing Terhadap Sifat Fisis, Mikrostruktur dan Magnet dari Flakes NdFeB

    OpenAIRE

    Sipahutar, Wahyu Solafide

    2015-01-01

    Had made research manufacture NdFeB magnets of flakes of wet milling process using a ball mill to the physic properties, microstructure, and magnetic properties with variations milling time is 16 hours, 24 hours, 48 hours, 72 hours. Powder result of mechanical milling using a ball mill and then analyzed the resulting particle size by using PSA and XRD. Then do the manufacture of test samples in the form of pellets by compaction process through print isotropy. Having obtained a sample of pelle...

  17. Characterization of structures and novel magnetic response of Fe87.5Si7Al5.5 alloy processed by ball milling

    International Nuclear Information System (INIS)

    Duan, Yuping; Gu, Shuchao; Zhang, Zhonglun; Wen, Ming

    2012-01-01

    Highlights: ► The water atomized Fe 87.5 Si 7 Al 5.5 (Wt.%) alloy was processed by ball-milling. ► The microstructure and magnetic properties of alloy changed following milling. ► The powders milled for 10 h have the largest M s and strongest reflection loss. ► The permeability of the powders milled for 2 h is the largest. ► The charge exchange between Fe and Si is discussed base on first-principles. - Abstract: The water atomized Fe 87.5 Si 7 Al 5.5 (Wt.%) alloy was processed by a high-energy planetary ball-milling. The characterization of morphology, microstructure, and electromagnetic properties were measured by scanning electron microscope (SEM), X-ray diffractometer, vibrating sample magnetometer (VSM), vector network analyzer and the first principle method. The analysis results showed that the powders shape became flaky from fusiform. The powders showed a reduction of the average grain size and the increase of the internal strain, and then presented an adverse variation trend after 55 h milling. The powders that milled 10 h had the largest saturation magnetization M S (131 emu/g). The value μ′ of the powders decreased with increasing milling time at relatively lower frequency (2–8 GHz), but opposite variation tendency happened at higher frequency (8–18 GHz). Also, only short time milling can enhance the value of μ″ in the test frequency. The powders after 10 h milling showed excellent microwave absorption (RL < −10 dB) at the frequency 9.0–15.6 GHz and the absorption peak shifted regularly to the high frequency as the increased milling time. Furthermore, the effect of charge exchange between the Fe and Si on the saturation magnetization in the ball-milling process was also investigated by using density functional theory (DFT) of first principle.

  18. Comparative Study by MS and XRD of Fe50Al50 Alloys Produced by Mechanical Alloying, Using Different Ball Mills

    International Nuclear Information System (INIS)

    Rojas Martinez, Y.; Perez Alcazar, G. A.; Bustos Rodriguez, H.; Oyola Lozano, D.

    2005-01-01

    In this work we report a comparative study of the magnetic and structural properties of Fe 50 Al 50 alloys produced by mechanical alloying using two different planetary ball mills with the same ball mass to powder mass relation. The Fe 50 Al 50 sample milled during 48 h using the Fritsch planetary ball mill pulverisette 5 and balls of 20 mm, presents only a bcc alloy phase with a majority of paramagnetic sites, whereas that sample milled during the same time using the Fritsch planetary ball mill pulverisette 7 with balls of 15 mm, presents a bcc alloy phase with paramagnetic site (doublet) and a majority of ferromagnetic sites which include pure Fe. However for 72 h of milling this sample presents a bcc paramagnetic phase, very similar to that prepared with the first system during 48 h. These results show that the conditions used in the first ball mill equipment make more efficient the milling process.

  19. Foundations of powder metallurgy

    International Nuclear Information System (INIS)

    Libenson, G.A.

    1987-01-01

    Consideration is being given to physicochemical foundations and technology of metal powders, moulding and sintering of bars, made of them or their mixtures with nonmetal powders. Data on he design of basic equipment used in the processes of powder metallurgy and its servicing are presented. General requirements of safety engineering when fabricating metal powders and products of them are mentioned

  20. Comparison of the mechanically alloyed (V,W)C and (V,W)C-co powders

    CSIR Research Space (South Africa)

    Bolokang, AS

    2008-01-01

    Full Text Available in XRD patterns because they were of extremely fine grain size.As a result of the loss ofVandWthrough oxidation, free carbonwas also found in the final powder. The lattice parameter of the (V,W)C powder increased with milling time up to a maximum...

  1. Fundamentals of powder metallurgy

    International Nuclear Information System (INIS)

    Khan, I.H.; Qureshi, K.A.; Minhas, J.I.

    1988-01-01

    This book is being presented to introduce the fundamentals of technology of powder metallurgy. An attempt has been made to present an overall view of powder metallurgy technology in the first chapter, whereas chapter 2 to 8 deal with the production of metal powders. The basic commercial methods of powder production are briefly described with illustrations. Chapter 9 to 12 describes briefly metal powder characteristics and principles of testing, mixing, blending, conditioning, compaction and sintering. (orig./A.B.)

  2. Soft wheat quality characteristics required for making baking powder biscuits

    Science.gov (United States)

    Fifteen soft wheat varieties were evaluated for their grain, milling, flour and dough mixing characteristics, as well as their solvent retention capacities (SRCs), pasting properties and suitability for making baking powder biscuits, to identify wheat quality characteristics required for making bisc...

  3. The Influence of Milling on the Dissolution Performance of Simvastatin

    Directory of Open Access Journals (Sweden)

    Thomas Rades

    2010-12-01

    Full Text Available Particle size reduction is a simple means to enhance the dissolution rate of poorly water soluble BCS-class II and IV drugs. However, the major drawback of this process is the possible introduction of process induced disorder. Drugs with different molecular arrangements may exhibit altered properties such as solubility and dissolution rate and, therefore, process induced solid state modifications need to be monitored. The aim of this study was two-fold: firstly, to investigate the dissolution rates of milled and unmilled simvastatin; and secondly, to screen for the main milling factors, as well as factor interactions in a dry ball milling process using simvastatin as model drug, and to optimize the milling procedure with regard to the opposing responses particle size and process induced disorder by application of a central composite face centered design. Particle size was assessed by scanning electron microscopy (SEM and image analysis. Process induced disorder was determined by partial least squares (PLS regression modeling of respective X-ray powder diffractograms (XRPD and Raman spectra. Valid and significant quadratic models were built. The investigated milling factors were milling frequency, milling time and ball quantity at a set drug load, out of which milling frequency was found to be the most important factor for particle size as well as process induced disorder. Milling frequency and milling time exhibited an interaction effect on the responses. The optimum milling settings using the maximum number of milling balls (60 balls with 4 mm diameter was determined to be at a milling frequency of 21 Hz and a milling time of 36 min with a resulting primary particle size of 1.4 μm and a process induced disorder of 6.1% (assessed by Raman spectroscopy and 8.4% (assessed by XRPD, at a set optimization limit of < 2 μm for particle size and < 10% for process induced disorder. This optimum was tested experimentally and the process induced disorder

  4. Preparation of tungsten-iron carbide by ball milling

    International Nuclear Information System (INIS)

    Wang, G.M.; Campbell, S.J.; Calka, A.; Kaczmarek, W.A.

    1996-01-01

    Several sets of elemental powder mixtures of Fe-W-C (W 46 Fe 46 C 8 , W 60 Fe 20 C 20 and W 34 Fe 33 C 33 ) were ball milled using Uni-Ball mill for periods of up to 550 h in vacuum with a ball - to - powder ratio of about 35:1. Depending on the milling time, the main component of the as-milled materials was found to be solid solutions of Fe-W-C or Fe-C. Ternary phase W 3 Fe 3 C was obtained on annealing the as-milled materials at about 700 deg C. This product was then found to transfer to (FeW) 6 C on heat treatment at about 800 deg C. The resultant products of the annealing processes were found to depend not only on the annealing temperature, but also the starting composition, especially the initial carbon concentration. Detailed information on the structural and phase evolution during thermal treatment as measured using x-ray diffraction, Moessbauer spectroscopy and thermal analysis is presented. Special interest is focused on the competition for formation in this system between the Fe-C, W-Fe and W-C phases

  5. Ball milling and annealing of Co-50 at% W Powders

    CSIR Research Space (South Africa)

    Bolokang, AS

    2013-04-01

    Full Text Available Broadening and height reduction of X-ray diffraction peaks were observed after cold-pressing of unmilled Co-W pow- der mixture. It seems the effect of cold pressing has slightly reduced the lattice parameter of W from 3.165 to 3.143 Å. Consequent...

  6. Process for producing ceramic nitrides anc carbonitrides and their precursors

    Science.gov (United States)

    Brown, G.M.; Maya, L.

    1987-02-25

    A process for preparing ceramic nitrides and carbon nitrides in the form of very pure, fine particulate powder. Appropriate precursors is prepared by reaching a transition metal alkylamide with ammonia to produce a mixture of metal amide and metal imide in the form of an easily pyrolyzable precipitate.

  7. Crystalline-to-amorphous phase transformation in mechanically alloyed Fe50W50 powders

    International Nuclear Information System (INIS)

    Sherif El-Eskandarany, M.S.; Sumiyama, K.; Suzuki, K.

    1997-01-01

    A mechanical alloying process via a ball milling technique has been applied for preparing amorphous Fe 50 W 50 alloy powders. The results have shown that during the first and second stages of milling (0 to 360 ks) W atoms emigrate to Fe lattices to form nanocrystalline b.c.c. Fe-W solid solution, with a grain size of about 7 nm in diameter. After 720 ks of the milling time, this solid solution was transformed to an amorphous Fe-W alloy coexisting with the residual fraction of the unprocessed W powders. During the last stage of milling (720 to 1,440 ks) all of this residual W powder reacts with the amorphous phase to form a homogeneous Fe 50 W 50 amorphous alloy. The crystallization temperature and the enthalpy change of crystallization of amorphous Fe 50 W 50 powders milled for 1,440 ks were measured to be 860 K and -9kJ/mol, respectively. The amorphous Fe 50 W 50 powder produced is almost paramagnetic at room temperature. The powder comprises homogeneous and smooth spheres with an average size of about 0.5 microm in diameter

  8. Low-temperature synthesis of MgB{sub 2} via powder metallurgy processing

    Energy Technology Data Exchange (ETDEWEB)

    Birol, Yucel [Dokuz Eylul University, Department of Metallurgical and Materials Engineering, Faculty of Engineering, Buca, Izmir (Turkey)

    2016-12-15

    Ball-milled Mg/B{sub 2}O{sub 3} powder blends reveal interpenetrating layers of deformed magnesium and boron oxide grains that are increasingly refined with increasing milling time. Boron oxide is reduced by Mg and MgO thus formed reacts with the remaining B{sub 2}O{sub 3} to produce Mg{sub 3}(BO{sub 3}){sub 2} during ball milling for 30 min. Both B{sub 2}O{sub 3} and Mg{sub 3}(BO{sub 3}){sub 2} react with Mg to produce MgB{sub 2} upon further ball milling. An annealing treatment can be employed when ball milling is performed for less than 1 h as thermal exposure of the ball-milled Mg/B{sub 2}O{sub 3} powder blends also leads to the formation of MgB{sub 2}. The above reactions take place between 500 and 700 C when the Mg/B{sub 2}O{sub 3} powder blend is ball milled for 30 min, and between 450 and 550 C, after ball milling for 1 h. This is a very attractive route owing to processing temperatures where the volatility of Mg is no longer a problem. (orig.)

  9. Spheroidization of molybdenum powder by radio frequency thermal plasma

    Science.gov (United States)

    Liu, Xiao-ping; Wang, Kuai-she; Hu, Ping; Chen, Qiang; Volinsky, Alex A.

    2015-11-01

    To control the morphology and particle size of dense spherical molybdenum powder prepared by radio frequency (RF) plasma from irregular molybdenum powder as a precursor, plasma process parameters were optimized in this paper. The effects of the carrier gas flow rate and molybdenum powder feeding rate on the shape and size of the final products were studied. The molybdenum powder morphology was examined using high-resolution scanning electron microscopy. The powder phases were analyzed by X-ray diffraction. The tap density and apparent density of the molybdenum powder were investigated using a Hall flow meter and a Scott volumeter. The optimal process parameters for the spherical molybdenum powder preparation are 50 g/min powder feeding rate and 0.6 m3/h carrier gas rate. In addition, pure spherical molybdenum powder can be obtained from irregular powder, and the tap density is enhanced after plasma processing. The average size is reduced from 72 to 62 µm, and the tap density is increased from 2.7 to 6.2 g/cm3. Therefore, RF plasma is a promising method for the preparation of high-density and high-purity spherical powders.

  10. Advanced powder metallurgy aluminum alloys via rapid solidification technology

    Science.gov (United States)

    Ray, R.

    1984-01-01

    Aluminum alloys containing 10 to 11.5 wt. pct. of iron and 1.5 to 3 wt. pct. of chromium using the technique of rapid solidification powder metallurgy were studied. Alloys were prepared as thin ribbons (.002 inch thick) rapidly solidified at uniform rate of 10(6) C/second by the melt spinning process. The melt spun ribbons were pulverized into powders (-60 to 400 mesh) by a rotating hammer mill. The powders were consolidated by hot extrusion at a high reduction ratio of 50:1. The powder extrusion temperature was varied to determine the range of desirable processing conditions necessary to yield useful properties. Powders and consolidated alloys were characterized by SEM and optical metallography. The consolidated alloys were evaluated for (1) thermal stability, (2) tensile properties in the range, room temperature to 450 F, and (3) notch toughness in the range, room temperature to 450 F.

  11. Simple process to fabricate nitride alloy powders

    International Nuclear Information System (INIS)

    Yang, Jae Ho; Kim, Dong-Joo; Kim, Keon Sik; Rhee, Young Woo; Oh, Jang-Soo; Kim, Jong Hun; Koo, Yang Hyun

    2013-01-01

    alloy powders were obtained. Two types of the simple thermal treatment procedures were tested to fabricate nitride powders. First, the procedure is a direct nitriding process in which the metal powders were annealed at 1000 deg. C under nitrogen gas and then further annealed at 1500 deg. C under hydrogen containing Ar gas atmosphere. It was revealed that the particles were fragmented to smaller particles during the annealing. The XRD results showed that the uranium metal converted to UN 2 phase during the annealing at 1000 deg. C and then decomposed to UN phase during the further annealing at 1500 deg. C. Observed fragmentation and cracking of particles were caused by sequential volume changes of expansion and contraction which were accompanied by the formation and decomposition of uranium nitrides. Although uranium nitride powders were successfully fabricated during the simple nitriding process, it seems that milling of the obtained powder might be necessary to fabricate sintered nitride fuel pellets. In order to fabricate finer nitride powders, a nitriding procedure has been modified. In the modified process, the particles were heat-treated at 250 deg. C in H 2 before nitriding. The addition of a hydriding step was effective in obtaining fine uranium nitride powder. In the case of U-10 wt% Zr-alloy, however, only a few large cracks were developed on the particle surface and the particle maintained its size. This result reveals that hydriding and nitriding kinetics or mechanisms of U-10 wt% Zr alloy are quite different from those of U metal

  12. Performance of Disk Mill Type Mechanical Grinder for Size Reducing Process of Robusta Roasted Beans

    Directory of Open Access Journals (Sweden)

    Sri Mulato

    2006-12-01

    Full Text Available One of improtant steps in secondary coffee processing that influence on final product quality such as consistency and uniformity is milling process. Usually, Indonesian smallholder used "lumpang" for milling coffee roasted beans to coffee powder product which caused the final product not uniformed and consistent, and low productivity. Milling process of coffee roasted beans can be done by disk mill type mechanical grinder which is used by smallholder for milling several cereals. Indonesian Coffee and Cocoa Research Institute have developed disk mill type grinding machine for milling coffee roasted beans. Objective of this research is to find performance of disk mill type grinding machine for size reducing process of Robusta roasted beans from several size dried beans and roasting level treatments. Robusta dried beans which are taken from dry processing method have 13—14% moisture content (wet basis, 680—685 kg/m3 density, and classified in 3 sizes level. The result showed that the disk mill type of grinding machine could be used for milling Robusta roasted beans. Machine hascapacity 31—54 kg/h on 5,310—5,610 rpm axle rotation and depend on roasting level. Other technical parameters were 91—98% process efficientcy, 19—31 ml/ kg fuel consumption, 0.3—1% slips, 50—55% particles had diameter less than 230 mesh and 38—44% particles had diameter bigger than 100 mesh, 32—38% lightness was increased, 0.6—12.6% density was decreased, and solubility of coffee powder between 28—30%. Cost milling process per kilogram of Robusta roasted beans which light roast on capacity 30 kg/hour was Rp362.9. Key words : Coffee roasted, Robusta, disk mill, mechanical grinder, size reduction.

  13. Waste glass as partial mineral precursor in alkali-activated slag/fly ash system

    NARCIS (Netherlands)

    Zhang, S.; Keulen, A.; Arbi, K.; Ye, G.

    2017-01-01

    The feasibility of a waste glass powder residue (GP) from glass recycling as partial mineral precursor to produce alkali-activated materials is investigated. GP served as powder coal fly ash (PCFA) replacement within a reference system composed of 50% PCFA and 50% ground granulated blast furnace

  14. Earthquakes: hydrogeochemical precursors

    Science.gov (United States)

    Ingebritsen, Steven E.; Manga, Michael

    2014-01-01

    Earthquake prediction is a long-sought goal. Changes in groundwater chemistry before earthquakes in Iceland highlight a potential hydrogeochemical precursor, but such signals must be evaluated in the context of long-term, multiparametric data sets.

  15. Ceria powders by homogeneous precipitation technique

    International Nuclear Information System (INIS)

    Ramanathan, S.; Roy, S.K.

    2003-01-01

    Formation of precursors for ceria by two homogeneous precipitation reactions - (cerium chloride + urea at 95 degC - called reaction A and cerium chloride + hexamethylenetetramine at 85 degC - called reaction B) - has been studied. The variation of size of the colloidal particles formed and the zeta potential of the suspensions with progress of reactions exhibited similar trends for both the precipitation processes. Particle size increased from 100 to 300 nm with increasing temperature and extent of reaction. The zeta potential was found to decrease with increasing extent of precipitation in the pH range of 5 to 7. Filtration and drying led to agglomeration of the fine particles in case of the precursor from reaction B. The as-formed precursors were crystalline - a basic carbonate in case of reaction A and hydrous oxide in case of reaction B. It was found that nano-crystalline ceria powders (average crystallite size -10 nm) formed above 400 degC from both these precursors. The agglomerate size (D50) of the precursors and ceria powders formed after calcination at 600 degC varied from 0.7 to 3 μm. Increasing calcination temperature up to 800 degC, increased the crystallite size (50 nm). The zeta potential variation with pH and concentration of an anionic dispersant (Calgon) for the ceria powders formed was studied to determine the ideal conditions for suspension stability. It was found to be maximum (i.e., the suspensions stable) in the pH range of 3 to 4 or Calgon concentration of 0.01 to 0.1 weight percent. (author)

  16. Milling condition effects on the Nd{sub 15} Fe{sub 77} B{sub 8} powder magnetic properties; Efeito das condicoes de moagem sobre as propriedades magneticas de po de Nd{sub 15} Fe{sub 77} B{sub 8}

    Energy Technology Data Exchange (ETDEWEB)

    Landgraf, Fernando J.G.; Missell, Frank P

    1993-12-31

    As a result of the first part of a study of the development of permanent magnets, an investigation of the effect of milling on the magnetic properties of the alloy Nd{sub 15} Fe{sub 77} B{sub 8} showed differences in efficiency between ball milling and vibration milling, as well as a dependence of the intrinsic coercive field on particle size. The maximum value of the coercive field was obtained for a particle size of 1.7 {mu}m in samples compacted without magnetic orientation. (author) 9 refs., 4 figs.

  17. Nanostructured hydroxyapatite powders produced by a flame-based technique

    Energy Technology Data Exchange (ETDEWEB)

    Trommer, R.M., E-mail: rafael_trommer@yahoo.com.br [Ceramic Materials Laboratory, av. Osvaldo Aranha 99/705, 90035190, Porto Alegre, RS (Brazil); Santos, L.A. [Biomaterials Laboratory, av. Bento Goncalves 9500, Campus do Vale Setor IV Predio 74 Sala 123, 91501970, Porto Alegre, RS (Brazil); Bergmann, C.P. [Ceramic Materials Laboratory, av. Osvaldo Aranha 99/705, 90035190, Porto Alegre, RS (Brazil)

    2009-08-01

    In this work we reported the production of hydroxyapatite (HA) powder, one of the most studied calcium phosphates in the bioceramics field, using a cost-effective apparatus, composed by three major components: the atomization device, the pilot and main flames and finally the powder collector system. Calcium acetate and ammonium phosphate, diluted in ethanol and water, were used as salts in the precursor solution. The Ca/P molar ratio in the precursor solution was 1.65, equivalent to biological hydroxyapatite. After its production and collection, HA powder was calcined at 600 deg. C for 2 h. X-ray diffraction analysis pointed to the formation of crystalline hydroxyapatite powders. Carbonate was identified in the powders by Fourier-transform infrared (FTIR) spectroscopy. Scanning electronic microscopy (SEM) showed that the powders were composed of spherical primary particles and secondary aggregates, with the morphology unchanged after calcination. By transmission electronic microscopy (TEM), it was observed that the crystallite size of the primary particles was 24.8 {+-} 5.8 nm, for the calcined powder. The specific surface area was 15.03 {+-} 6.4 and 26.50 {+-} 7.6 m{sup 2}/g, for the as-synthetized and calcined powder respectively.

  18. Phase Transitions in Mechanically Milled Mn-Al-C Permanent Magnets

    Directory of Open Access Journals (Sweden)

    Michael J. Lucis

    2014-04-01

    Full Text Available Mn-Al powders were prepared by rapid solidification followed by high-energy mechanical milling. The rapid solidification resulted in single-phase ε. The milling was performed in both the ε phase and the τ phase, with the τ-phase formation accomplished through a heat treatment at 500 °C for 10 min. For the ε-milled samples, the conversion of the ε to the τ phase was accomplished after milling via the same heat treatment. Mechanical milling induced a significant increase in coercivity in both cases, reaching 4.5 kOe and 4.1 kOe, respectively, followed by a decrease upon further milling. The increase in coercivity was the result of grain refinement induced by the high-energy mechanical milling. Additionally, in both cases a loss in magnetization was observed. Milling in the ε phase showed a smaller decrease in the magnetization due to a higher content of the τ phase. The loss in magnetization was attributed to a stress-induced transition to the equilibrium phases, as no site disorder or oxidation was observed. Surfactant-assisted milling in oleic acid also improved coercivity, but in this case values reached >4 kOe and remained stable at least through 32 h of milling.

  19. Investigation of the milling-induced thermal behavior of crystalline and amorphous griseofulvin.

    Science.gov (United States)

    Trasi, Niraj S; Boerrigter, Stephan X M; Byrn, Stephen Robert

    2010-07-01

    To gain a better understanding of the physical state and the unusual thermal behavior of milled griseofulvin. Griseofulvin crystals and amorphous melt quench samples were milled in a vibrating ball mill for different times and then analyzed using differential scanning calorimetry (DSC) and powder X-ray diffraction (PXRD). Modulated DSC (mDSC) and annealing studies were done for the milled amorphous samples to further probe the effects of milling. Milling of griseofulvin crystals results in decrease in crystallinity and amorphization of the compound. A double peak is seen for crystallization in the DSC, which is also seen for the milled melt quench sample. Both enthalpy and temperature of crystallization decrease for the milled melt quenched sample. Tg is visible under the first peak with the mDSC, and annealing shows that increasing milling time results in faster crystallization upon storage. Milling of griseofulvin results in the formation of an amorphous form and not a mesophase. It increases the amount of surface created and the overall energy of the amorphous griseofulvin, which leads to a decreased temperature of crystallization. The two exotherms in the DSC are due to some particles having nuclei on the surface.

  20. Effect of the milling conditions on the degree of amorphization of selenium by milling in a planetary ball mill

    International Nuclear Information System (INIS)

    Ksiazek, K; Wacke, S; Gorecki, T; Gorecki, Cz

    2007-01-01

    The effect of the milling parameters (rotation speed of the milling device and duration of milling) on the phase composition of the products of milling of fully crystalline selenium has been investigated. The milling was conducted using a planetary micromill and the phase composition of the milling products was determined by differential thermal analysis. It has been found that ball milling leads to the partial amorphization of the starting crystalline material. The content of amorphous phase in the milling products depends, in a rather complicated way, on the milling parameters. At the milling parameters adopted in the present study, the milling product was never fully amorphous. The complicated way the milling parameters affect the content of amorphous phase in the milling products is a result of competition of two processes: amorphization due to deformation and refinement of grains of milled material and crystallization of the already produced amorphous material at the cost of heat evolved in the milling vial during the milling process

  1. Changes in UO2 powder properties during processing via BNFL's binderless route

    International Nuclear Information System (INIS)

    Bromely, A.P.; Logsdon, R.; Roberts, V.A.

    1997-01-01

    The Short Binderless Route (SBR) has been developed for Mixed Oxide fuel production in BNFL's MOX Demonstration Facility (MDF) and the Sellafield MOX Plant (SMP). It is a compact process which enables good homogenisation of the Pu/U mixture and production of free flowing press feed materials. The equipment used to achieve this consists of an attritor mill to provide homogenization and a spheroidiser to provide press feed granules. As for other powder processes, the physical properties of the UO 2 powder can affect the different process stages and consequently a study of some of these effects has been carried out. The aim of the work were to gain a better understanding of the process, to consequently optimize press feed material quality and to also maintain powder hold-up levels in the equipment at a minimum. The paper considers the effects of milling processes on powder morphology and powder surface effects, on the granulation process and also on powder and granule bulk properties such as pour, tap and compaction densities. Results are discussed in terms of powder properties such as powder cohesivity, morphology and particle size. UO 2 powder derived from both the Integrated Dry Route (IDR) and the Ammonium Di-Uranate (ADU) Route are considered. Small (1 kg) scale work has been carried out which has been confirmed by larger (25 kg) scale trials. The work shows that IDR powder with differing morphologies and ADU powder can be successfully processed via the SBR route. (author). 4 figs, 4 tabs

  2. Aluminum powder metallurgy processing

    Energy Technology Data Exchange (ETDEWEB)

    Flumerfelt, J.F.

    1999-02-12

    The objective of this dissertation is to explore the hypothesis that there is a strong linkage between gas atomization processing conditions, as-atomized aluminum powder characteristics, and the consolidation methodology required to make components from aluminum powder. The hypothesis was tested with pure aluminum powders produced by commercial air atomization, commercial inert gas atomization, and gas atomization reaction synthesis (GARS). A comparison of the GARS aluminum powders with the commercial aluminum powders showed the former to exhibit superior powder characteristics. The powders were compared in terms of size and shape, bulk chemistry, surface oxide chemistry and structure, and oxide film thickness. Minimum explosive concentration measurements assessed the dependence of explosibility hazard on surface area, oxide film thickness, and gas atomization processing conditions. The GARS aluminum powders were exposed to different relative humidity levels, demonstrating the effect of atmospheric conditions on post-atomization processing conditions. The GARS aluminum powders were exposed to different relative humidity levels, demonstrating the effect of atmospheric conditions on post-atomization oxidation of aluminum powder. An Al-Ti-Y GARS alloy exposed in ambient air at different temperatures revealed the effect of reactive alloy elements on post-atomization powder oxidation. The pure aluminum powders were consolidated by two different routes, a conventional consolidation process for fabricating aerospace components with aluminum powder and a proposed alternative. The consolidation procedures were compared by evaluating the consolidated microstructures and the corresponding mechanical properties. A low temperature solid state sintering experiment demonstrated that tap densified GARS aluminum powders can form sintering necks between contacting powder particles, unlike the total resistance to sintering of commercial air atomization aluminum powder.

  3. Crystallite sizes of LiH before and after ball milling and thermal exposure

    International Nuclear Information System (INIS)

    Ortiz, Angel L.; Osborn, William; Markmaitree, Tippawan; Shaw, Leon L.

    2008-01-01

    The powder characteristics of lithium hydride (LiH) as a function of high-energy ball milling condition are systematically investigated via quantitative X-ray diffraction (XRD) analysis. The results obtained from the XRD analysis are compared with those attained from scanning electron microscopy (SEM), transmission electron microscopy (TEM), and specific surface area (SSA) analyses. The thermal stability of the ball-milled LiH is also investigated in order to provide physical insights into its cyclic stability in hydrogen sorption and desorption cycles. The results indicate that ball milling is effective in obtaining nano-crystalline LiH powder which is relatively stable with retention of nano-crystals after thermal exposure at 285 deg. C (equivalent to 0.58T m ) for 1 h. The good thermal stability observed is attributed to the presence of many pores in the agglomerates at the ball-milled condition. These pores effectively prevent crystal growth during the thermal exposure

  4. Preliminary study of sintering of metallic niobium processed for mechanical milling

    International Nuclear Information System (INIS)

    Tamura, H.M.; Vurobi Junior, S.; Cintho, O.M.; Sandim, H.R.Z.; Leite, G.S.

    2010-01-01

    In present study was preliminary study of mechanical milling influence on preparing of metallic niobium powder for sintering. Sample of metallic niobium in powder passing in sieve no. 635 mesh was processed by mechanical milling in SPEX mill for 8 hours using power grinding of 7:1 and a nitrogen atmosphere. The powder was annealed at different temperatures, 900 deg C, 1000 deg C, 1100 deg C and 1200 deg C for 1 hour in an atmosphere of hydrogen and argon to study their crystallization, which then were formed into blank for analysis of the curves compressibility. These samples were also subjected to x-ray diffraction in that their data were compared between the annealing temperatures. We also evaluate the compressibility curves of niobium samples with and without grinding these samples were subjected to x-ray diffraction and fluorescence. (author)

  5. Effect of milling on the damping behavior of nano-structured copper

    Energy Technology Data Exchange (ETDEWEB)

    Srikanth, Narasimalu; Thein, Maung Aye; Gupta, Manoj

    2004-02-05

    In the present study, elemental Cu powder was mechanically milled (MMed) for 10 h to reduce the grain (crystalline) size in the nano-range (<100 nm). The mechanically milled powder (10 h-MMed) and elemental powder without mechanical milling (MM) (0 h-MMed) was consolidated by die-cold compaction and were further hot extruded at different temperatures to maintain a crystallite size within the nano-range. Further, the specimen was tested by a novel free-free type suspended beam arrangement, coupled with circle-fit approach to determine damping characteristics. The characterization results help to understand the effect of the nano-size grains on the overall damping capacity of the bulk samples compared to a normal micro-crystalline sample. Results show that the damping capacity of the nano-grained material increases due to the presence of process induced microstructural changes similar to the damping behavior of a micro-grain sized specimen.

  6. Recycle of valuable products from oily cold rolling mill sludge

    Science.gov (United States)

    Liu, Bo; Zhang, Shen-gen; Tian, Jian-jun; Pan, De-an; Liu, Yang; Volinsky, Alex A.

    2013-10-01

    Oily cold rolling mill (CRM) sludge contains lots of iron and alloying elements along with plenty of hazardous organic components, which makes it as an attractive secondary source and an environmental contaminant at the same time. The compound methods of "vacuum distillation + oxidizing roasting" and "vacuum distillation + hydrogen reduction" were employed for the recycle of oily cold rolling mill sludge. First, the sludge was dynamically vacuum distilled in a rotating furnace at 50 r/min and 600°C for 3 h, which removed almost hazardous organic components, obtaining 89.2wt% ferrous resultant. Then, high purity ferric oxide powders (99.2wt%) and reduced iron powders (98.9wt%) were obtained when the distillation residues were oxidized and reduced, respectively. The distillation oil can be used for fuel or chemical feedstock, and the distillation gases can be collected and reused as a fuel.

  7. The preparation of UO2 powder: effect of ammonium uranate properties

    International Nuclear Information System (INIS)

    Woolfrey, J.L.

    1978-01-01

    Ammonium uranate (AU) powders were precipitated from a uranyl nitrate solution with gaseous ammonia. The decomposition of the powders in hydrogen was studied to determine those properties of AU which affect the decomposition reactions and influence the properties of the final UO 2 powder. The thermal decomposition was affected by the initial composition (ammonia and nitrate content) and the morphology of the AU powders. The amount of self-reduction increased with increasing combined ammonia content and decreased with increasing nitrate content. The specific surface area of the decomposed powder increased with increasing total ammonia content and initial surface area of the precursor AU powder. Thermal treatment of the decomposed powder can be used to modify such effects and, in commercial powder production, is used to control the properties of the final UO 2 powder. (Auth.)

  8. Effect of milling time on the structure, micro-hardness, and thermal behavior of amorphous/nanocrystalline TiNiCu shape memory alloys developed by mechanical alloying

    International Nuclear Information System (INIS)

    Alijani, Fatemeh; Amini, Rasool; Ghaffari, Mohammad; Alizadeh, Morteza; Okyay, Ali Kemal

    2014-01-01

    Highlights: • Potential to produce B1′ (thermal- and stress-induced) and B2 was established. • Martensitic transformation occurred without the formation of intermediate R-phase. • Formation of unwanted intermetallics during heating was hindered by milling. • During milling, microhardness was increased, then reduced, and afterward re-increased. • By milling evolution, thermal crystallization steps changed from 3 to 2. - Abstract: In the present paper, the effect of milling process on the chemical composition, structure, microhardness, and thermal behavior of Ti–41Ni–9Cu compounds developed by mechanical alloying was evaluated. The structural characteristic of the alloyed powders was evaluated by X-ray diffraction (XRD). The chemical composition homogeneity and the powder morphology and size were studied by scanning electron microscopy coupled with electron dispersive X-ray spectroscopy. Moreover, the Vickers micro-indentation hardness of the powders milled for different milling times was determined. Finally, the thermal behavior of the as-milled powders was studied by differential scanning calorimetery. According to the results, at the initial stages of milling (typically 0–12 h), the structure consisted of a Ni solid solution and amorphous phase, and by the milling evolution, nanocrystalline martensite (B19′) and austenite (B2) phases were initially formed from the initial materials and then from the amorphous phase. It was found that by the milling development, the composition uniformity is increased, the inter-layer thickness is reduced, and the powders microhardness is initially increased, then reduced, and afterward re-increased. It was also realized that the thermal behavior of the alloyed powders and the structure of heat treated samples is considerably affected by the milling time

  9. Uranium mill tailings

    International Nuclear Information System (INIS)

    McLaren, L.H.

    1982-11-01

    This bibliography contains information on uranium mill tailings included in the Department of Energy's Energy Data Base from January 1981 through October 1982. The abstracts are grouped by subject category as shown in the table of contents. Entries in the subject index also facilitate access by subject, e.g., Mill Tailings/Radiation Hazards. Within each category the arrangement is by report number for reports, followed by nonreports in reverse chronological order. These citations are to research reports, journal articles, books, patents, theses, and conference papers from worldwide sources. Five indexes, each preceded by a brief description, are provided: Corporate Author, Personal Author, Subject, Contract Number, and Report Number. (335 abstracts)

  10. Uranium mining and milling

    International Nuclear Information System (INIS)

    Floeter, W.

    1976-01-01

    In this report uranium mining and milling are reviewed. The fuel cycle, different types of uranium geological deposits, blending of ores, open cast and underground mining, the mining cost and radiation protection in mines are treated in the first part of this report. In the second part, the milling of uranium ores is treated, including process technology, acid and alkaline leaching, process design for physical and chemical treatment of the ores, and the cost. Each chapter is clarified by added figures, diagrams, tables, and flowsheets. (HK) [de

  11. Preparation and properties of Cobalt-based soft magnetic material prepared by novel powder metallurgy

    Energy Technology Data Exchange (ETDEWEB)

    Srivastava, Yogesh, E-mail: 123209001_yogesh@manit.ac.in; Srivastava, Sanjay

    2017-02-01

    The present work deals with the development of nanocrystalline 60Co–26Fe–14Al (wt%) soft magnetic materials via mechanical milling of elemental powders. The evolution of solid solution during milling proceeded with continuous decrease in atomic order and the crystallite size, and an introduction of internal strain and dislocations. The milling-induced lattice defects, crystallite size reduction, and atomic disorder exhibited a decrease in saturation magnetization, remanence magnetization, squareness ratio, and blocking temperature with increasing milling time. It has been demonstrated that, at subzero temperatures, the magnetization decreases with increasing temperature due to the development of an effective anisotropy caused by an evolution of canted spin structure owing to the introduction of lattice defects during milling. - Highlights: • Co-based HA have been fabricated by mechanical alloying. • The effect of milling time was investigated. • The saturation magnetization can be reached up to 140.79 emu/g.

  12. Spherical rhenium metal powder

    International Nuclear Information System (INIS)

    Leonhardt, T.; Moore, N.; Hamister, M.

    2001-01-01

    The development of a high-density, spherical rhenium powder (SReP) possessing excellent flow characteristics has enabled the use of advanced processing techniques for the manufacture of rhenium components. The techniques that were investigated were vacuum plasma spraying (VPS), direct-hot isostatic pressing (D-HIP), and various other traditional powder metallurgy processing methods of forming rhenium powder into near-net shaped components. The principal disadvantages of standard rhenium metal powder (RMP) for advanced consolidation applications include: poor flow characteristics; high oxygen content; and low and varying packing densities. SReP will lower costs, reduce processing times, and improve yields when manufacturing powder metallurgy rhenium components. The results of the powder characterization of spherical rhenium powder and the consolidation of the SReP are further discussed. (author)

  13. Effect of agglomerate strength on sintered density for yttria powders containing agglomerates of monosize spheres

    International Nuclear Information System (INIS)

    Ciftcioglu, M.; Akine, M.; Burkhart, L.

    1987-01-01

    The effect of agglomerate strength on sintered density was determined for several yttria powders made by intentionally agglomerating 0.1-μm, monodisperse yttriuim hydrocarbonate precursor spheres and calcining separate portions of the precursor at different temperatures to vary the strength of the intraaglomeate bonds. In this way, the effects of differences in particle morphology and other characteristics among the powders were minimized and the effect of agglomerate strength could be seen more clearly

  14. Barium strontium titanate powders prepared by spray pyrolysis

    International Nuclear Information System (INIS)

    Brankovic, G.; Brankovic, Z.; Goes, M.S.; Paiva-Santos, C.O.; Cilense, M.; Varela, J.A.; Longo, E.

    2005-01-01

    Ultasonic spray pyrolysis (SP) has been investigated for the production of the barium strontium titanate (BST) powders from the polymeric precursors. The processing parameters, such as flux of aerosol and temperature profile inside the furnace, were optimized to obtain single phase BST. The powders were characterized by the methods of X-ray diffraction analysis, SEM, EDS and TEM. The obtained powders were submicronic, consisting of spherical, polycrystalline particles, with internal nanocrystalline structure. Crystallite size of 10 nm, calculated using Rietveld refinement, is in a good agreement with results of HRTEM

  15. Microwave-assisted hydrothermal synthesis of lead zirconate fine powders

    Directory of Open Access Journals (Sweden)

    Apinpus Rujiwatra

    2011-01-01

    Full Text Available A rapid synthesis of lead zirconate fine powders by microwave-assisted hydrothermal technique is reported. The influences of type of lead precursor, concentration of potassium hydroxide mineraliser, applied microwave power and irradiation time are described. The synthesised powders were characterised by powder X-ray diffraction, field emission scanning electron microscopy, energy-dispersive X-ray spectroscopic microanalysis and light scattering technique. The merits of the microwave application in reducing reaction time and improving particle mono-dispersion and size uniformity as well as the drawbacks, viz. low purity of the desired phase and increasing demand of mineraliser, are discussed in relation to conventional heating method.

  16. Production of nanocrystalline metal powders via combustion reaction synthesis

    Science.gov (United States)

    Frye, John G.; Weil, Kenneth Scott; Lavender, Curt A.; Kim, Jin Yong

    2017-10-31

    Nanocrystalline metal powders comprising tungsten, molybdenum, rhenium and/or niobium can be synthesized using a combustion reaction. Methods for synthesizing the nanocrystalline metal powders are characterized by forming a combustion synthesis solution by dissolving in water an oxidizer, a fuel, and a base-soluble, ammonium precursor of tungsten, molybdenum, rhenium, or niobium in amounts that yield a stoichiometric burn when combusted. The combustion synthesis solution is then heated to a temperature sufficient to substantially remove water and to initiate a self-sustaining combustion reaction. The resulting powder can be subsequently reduced to metal form by heating in a reducing gas environment.

  17. Rapid formation of phase-clean 110 K (Bi-2223) powders derived via freeze-drying process

    Science.gov (United States)

    Balachandran, U.

    1996-06-04

    A process for the preparation of amorphous precursor powders for Pb-doped Bi{sub 2}Sr{sub 2} Ca{sub 2}Cu{sub 3}O{sub x} (2223) includes a freeze-drying process incorporating a splat-freezing step. The process generally includes splat freezing a nitrate solution of Bi, Pb, Sr, Ca, and Cu to form flakes of the solution without any phase separation; grinding the frozen flakes to form a powder; freeze-drying the frozen powder; heating the dried powder to form a dry green precursor powders; denitrating the green-powders; heating the denitrated powders to form phase-clean Bi-2223 powders. The grain boundaries of the 2223 grains appear to be clean, leading to good intergrain contact between 2223 grains. 11 figs.

  18. The structural changes of Y2O3 in ferritic ODS alloys during milling

    International Nuclear Information System (INIS)

    Hilger, I.; Tegel, M.; Gorley, M.J.; Grant, P.S.; Weißgärber, T.; Kieback, B.

    2014-01-01

    Oxide dispersion strengthened (ODS) ferritic steels are usually fabricated via mechanical alloying and subsequent consolidation via hot extrusion or hot isostatic pressing. During the individual process steps, a complex evolution of the nanoparticle structure is taking place. Powders with different Y 2 O 3 contents were milled and examined by means of X-ray diffraction (XRD) and atom probe tomography (APT). It has been observed that the Y 2 O 3 is fragmented and becomes partially amorphous upon milling due to the grain refinement of Y 2 O 3 during the milling process. There was no compelling evidence for Y 2 O 3 dissociation and dissolution into the steel matrix

  19. Aluminum-graphite composite produced by mechanical milling and hot extrusion

    International Nuclear Information System (INIS)

    Flores-Zamora, M.I.; Estrada-Guel, I.; Gonzalez-Hernandez, J.; Miki-Yoshida, M.; Martinez-Sanchez, R.

    2007-01-01

    Aluminum-graphite composites were produced by mechanical milling followed by hot extrusion. Graphite content was varied between 0 and 1 wt.%. Al-graphite mixtures were initially mixed in a shaker mill without ball, followed by mechanical milling in a High-energy simoloyer mill for 2 h under argon atmosphere. Milled powders were subsequently pressed at ∼950 MPa for 2 min, and next sintered under vacuum for 3 h at 823 K. Finally, sintered products were held for 0.5 h at 823 K and hot extruded using indirect extrusion. Tension and compression tests were carried out to determine the yield stress and maximum stress of the materials. We found that the mechanical resistance increased as the graphite content increased. Microstructural characterization was done by transmission electron microscopy. Al-O-C nanofibers and graphite nanoparticles were observed in extruded samples by transmission electron microscopy. These nanoparticles and nanofibers seemed to be responsible of the reinforcement phenomenon

  20. Reliable Mechanochemistry: Protocols for Reproducible Outcomes of Neat and Liquid Assisted Ball-mill Grinding Experiments.

    Science.gov (United States)

    Belenguer, Ana M; Lampronti, Giulio I; Sanders, Jeremy K M

    2018-01-23

    The equilibrium outcomes of ball mill grinding can dramatically change as a function of even tiny variations in the experimental conditions such as the presence of very small amounts of added solvent. To reproducibly and accurately capture this sensitivity, the experimentalist needs to carefully consider every single factor that can affect the ball mill grinding reaction under investigation, from ensuring the grinding jars are clean and dry before use, to accurately adding the stoichiometry of the starting materials, to validating that the delivery of solvent volume is accurate, to ensuring that the interaction between the solvent and the powder is well understood and, if necessary, a specific soaking time is added to the procedure. Preliminary kinetic studies are essential to determine the necessary milling time to achieve equilibrium. Only then can exquisite phase composition curves be obtained as a function of the solvent concentration under ball mill liquid assisted grinding (LAG). By using strict and careful procedures analogous to the ones here presented, such milling equilibrium curves can be obtained for virtually all milling systems. The system we use to demonstrate these procedures is a disulfide exchange reaction starting from the equimolar mixture of two homodimers to obtain at equilibrium quantitative heterodimer. The latter is formed by ball mill grinding as two different polymorphs, Form A and Form B. The ratio R = [Form B] / ([Form A] + [Form B]) at milling equilibrium depends on the nature and concentration of the solvent in the milling jar.

  1. Effect of Mechanical Activation on the In Situ Formation of TiB2 Particulates in the Powder Mixture of TiH2 and FeB

    Directory of Open Access Journals (Sweden)

    Huynh X.-K.

    2017-06-01

    Full Text Available The in situ formation of TiB2 particulates via an interface reaction between Ti and FeB powders was studied. The effects of mechanical activation by high-energy milling on the decomposition of TiH2 and the interface reactions between Ti and FeB powders to form TiB2 were investigated. Powder mixtures were fabricated using planetary ball-milling under various milling conditions. The specific ball-milling energy was calculated from the measured electrical power consumption during milling process. High specific milling energy (152.6 kJ/g resulted in a size reduction and homogeneous dispersion of constituent powders. This resulted in a decrease in the decomposition temperature of TiH2 and an increase in the formation reaction of TiB2 particulates in the Fe matrix, resulting in a homogeneous microstructure of nanoscale TiB2 evenly distributed within the Fe matrix. In contrast, the powder mixture milled with low specific milling energy (36.5 kJ/g showed an inhomogeneous microstructure composed of relatively large Fe-Fe2B particles surrounded by a thin layer of Fe-TiB2 within a finely dispersed Fe-TiB2 matrix region.

  2. Evaluation of End Mill Coatings

    Energy Technology Data Exchange (ETDEWEB)

    L. J. Lazarus; R. L. Hester,

    2005-08-01

    Milling tests were run on families of High Speed Steel (HSS) end mills to determine their lives while machining 304 Stainless Steel. The end mills tested were made from M7, M42 and T15-CPM High Speed Steels. The end mills were also evaluated with no coatings as well as with Titanium Nitride (TiN) and Titanium Carbo-Nitride (TiCN) coatings to determine which combination of HSS and coating provided the highest increase in end mill life while increasing the cost of the tool the least. We found end mill made from M42 gave us the largest increase in tool life with the least increase in cost. The results of this study will be used by Cutting Tool Engineering in determining which end mill descriptions will be dropped from our tool catalog.

  3. Synthesis of Amorphous Powders of Ni-Si and Co-Si Alloys by Mechanical Alloying

    Science.gov (United States)

    Omuro, Keisuke; Miura, Harumatsu

    1991-05-01

    Amorphous powders of the Ni-Si and Co-Si alloys are synthesized by mechanical alloying (MA) from crystalline elemental powders using a high energy ball mill. The alloying and amorphization process is examined by X-ray diffraction, differential scanning calorimetry (DSC), and scanning electron microscopy. For the Ni-Si alloy, it is confirmed that the crystallization temperature of the MA powder, measured by DSC, is in good agreement with that of the powder sample prepared by mechanical grinding from the cast alloy ingot products of the same composition.

  4. SAF line powder operations

    International Nuclear Information System (INIS)

    Frederickson, J.R.; Horgos, R.M.

    1983-10-01

    An automated nuclear fuel fabrication line is being designed for installation in the Fuels and Materials Examination Facility (FMEF) near Richland, Washington. The fabrication line will consist of seven major process systems: Receiving and Powder Preparation; Powder Conditioning; Pressing and Boat Loading; Debinding, Sintering, and Property Adjustment; Boat Transport; Pellet Inspection and Finishing; and Pin Operations. Fuel powder processing through pellet pressing will be discussed in this paper

  5. Two layer powder pressing

    International Nuclear Information System (INIS)

    Schreiner, H.

    1979-01-01

    First, significance and advantages of sintered materials consisting of two layers are pointed out. By means of the two layer powder pressing technique metal powders are formed resulting in compacts with high accuracy of shape and mass. Attributes of basic powders, different filling methods and pressing techniques are discussed. The described technique is supposed to find further applications in the field of two layer compacts in the near future

  6. Operation whey powder

    International Nuclear Information System (INIS)

    Brunner, E.

    1987-01-01

    The odyssey of the contaminated whey powder finally has come to an end, and the 5000 tonnes of whey now are designated for decontamination by means of an ion exchange technique. The article throws light upon the political and economic reasons that sent the whey powder off on a chaotic journey. It is worth mentioning in this context that the natural radioactivity of inorganic fertilizers is much higher than that of the whey powder in question. (HP) [de

  7. Effect of milling on DSC thermogram of excipient adipic acid.

    Science.gov (United States)

    Ng, Wai Kiong; Kwek, Jin Wang; Yuen, Aaron; Tan, Chin Lee; Tan, Reginald

    2010-03-01

    The purpose of this research was to investigate why and how mechanical milling results in an unexpected shift in differential scanning calorimetry (DSC) measured fusion enthalpy (Delta(fus)H) and melting point (T(m)) of adipic acid, a pharmaceutical excipient. Hyper differential scanning calorimetry (hyper-DSC) was used to characterize adipic acid before and after ball-milling. An experimental study was conducted to evaluate previous postulations such as electrostatic charging using the Faraday cage method, crystallinity loss using powder X-ray diffraction (PXRD), thermal annealing using DSC, impurities removal using thermal gravimetric analysis (TGA) and Karl Fischer titration. DSC thermograms showed that after milling, the values of Delta(fus)H and T(m) were increased by approximately 9% and 5 K, respectively. Previous suggestions of increased electrostatic attraction, change in particle size distribution, and thermal annealing during measurements did not explain the differences. Instead, theoretical analysis and experimental findings suggested that the residual solvent (water) plays a key role. Water entrapped as inclusions inside adipic acid during solution crystallization was partially evaporated by localized heating at the cleaved surfaces during milling. The correlation between the removal of water and melting properties measured was shown via drying and crystallization experiments. These findings show that milling can reduce residual solvent content and causes a shift in DSC results.

  8. Interaction in polysilazane/SiC powder systems

    Energy Technology Data Exchange (ETDEWEB)

    Boiteux, Y.P.

    1992-07-01

    Consolidation of ceramic precursor ceramic powder systems upon heating is investigated. A polysilazane (silicon nitride precursor) is chosen as ceramic precursor with a filler of a sub-micron SiC powder. A scheme to optimize the volume fraction of precursor is developed in order to maximize the density of the compacted samples in the green state. Different techniques are presented to improve the homogeneity of precursor distribution in the mixture. A microencapsulation technique is developed that leads to a uniform coating of precursor on individual SiC particles. Upon pyrolysis of systems with 20 wt% polysilazane, little shrinkage occurs. The SiC particles do not coarsen during the heat treatment. The precursor, upon pyrolysis, transforms into an amorphous ceramic phase that acts as a cement between SiC particles. This cement phase can remain amorphous up to 1500{degrees}C; and is best described as a siliconoxycarbide with or without traces of nitrogen. Elimination of nitrogen in the amorphous phase indicates that the filler material (SiC) has a strong influence on the pyrolysis behavior of the chosen polysilazane. The amorphous ceramic phase may crystallize between 1400 and 1500{degrees}C, and depending on the nature of the gas environment, the crystalline phases are SiC, Si or Si{sub 3}N{sub 4}. Mechanisms explaining the strength increase upon heat treatment are proposed. Redistribution of the precursor occurs by capillary forces or vapor phase diffusion and recondensation of volatile monomers. The confined pyrolysis of the precursor results in an increase of residual ceramic matter being decomposed inside the sample. Interfacial reaction between the native silica-rich surface layer on SiC particles and the precursor derived phase explains the high strength of the materials.

  9. Comparison of Two Powder Processing Techniques on the Properties of Cu-NbC Composites

    Directory of Open Access Journals (Sweden)

    B. D. Long

    2014-01-01

    Full Text Available An in situ Cu-NbC composite was successfully synthesized from Cu, Nb, and C powders using ball milling and high pressure torsion (HPT techniques. The novelty of the new approach, HPT, is the combination of high compaction pressure and large shear strain to simultaneously refine, synthesize, and consolidate composite powders at room temperature. The HPTed Cu-NbC composite was formed within a short duration of 20 min without Fe contamination from the HPT’s die. High porosity of 3–9%, Fe and niobium oxidations, from grinding media and ethanol during ball milling led to low electrical conductivity of the milled Cu-NbC composite. The electrical conductivity of the HPTed Cu-NbC composite showed a value 50% higher than that of milled Cu-NbC composite of the same composition.

  10. Pharmaceutical powder compaction technology

    National Research Council Canada - National Science Library

    Çelik, Metin

    2011-01-01

    ... through the compaction formulation process and application. Compaction of powder constituents both active ingredient and excipients is examined to ensure consistent and reproducible disintegration and dispersion profiles...

  11. Shear Roll Mill Reactivation

    Science.gov (United States)

    2012-09-13

    pneumatically operated paste dumper and belt conveyor system, the loss in weight feeder system, the hydraulically operated shear roll mill, the pellet...out feed belt conveyor , and the pack out system comprised of the metal detector, scale, and pack out empty and full drum roller conveyors . Page | 4...feed hopper and conveyor supplying the loss in weight feeder were turned on, and it was verified that these items functioned as designed . The

  12. Fabrication of spherical high-nitrogen stainless steel powder alloys by mechanical alloying and thermal plasma spheroidization

    Science.gov (United States)

    Razumov, Nikolay G.; Wang, Qing Sheng; Popovich, Anatoly A.; Shamshurin, Aleksey I.

    2018-04-01

    This paper describes the results of experimental studies on the treatment of Fe-23Cr-11Mn-1N high-nitrogen stainless steel powder alloys, synthesized by the mechanical alloying (MA) of elemental powders in the flow of a radio frequency thermal plasma. The as-milled powder with irregular particles were successfully converted into spherical high-nitrogen stainless steel powder alloy. Measurement of the residual nitrogen content in the obtained powder, shown that during the plasma spheroidization process, part of the nitrogen escapes from the alloy.

  13. Grain growth studies on nanocrystalline Ni powder

    International Nuclear Information System (INIS)

    Rane, G.K.; Welzel, U.; Mittemeijer, E.J.

    2012-01-01

    The microstructure of nanocrystalline Ni powder produced by ball-milling and its thermal stability were investigated by applying different methods of X-ray diffraction line-profile analysis: single-line analysis, whole powder-pattern modelling and the (modified) Warren–Averbach method were employed. The kinetics of grain growth were investigated by both ex-situ and in-situ X-ray diffraction measurements. With increasing milling time, the grain-size reduction is accompanied by a considerable narrowing of the size distribution and an increase in the microstrain. Upon annealing, initial, rapid grain growth occurs, accompanied by the (almost complete) annihilation of microstrain. For longer annealing times, the grain-growth kinetics depend on the initial microstructure: a smaller microstrain with a broad grain-size distribution leads to linear grain growth, followed by parabolic grain growth, whereas a larger microstrain with a narrow grain-size distribution leads to incessant linear grain growth. These effects have been shown to be incompatible with grain-boundary curvature driven growth. The observed kinetics are ascribed to the role of excess free volume at the grain boundaries of nanocrystalline material and the prevalence of an “abnormal grain-growth” mechanism.

  14. Mechanical alloying nanotechnology, materials science and powder metallurgy

    CERN Document Server

    El-Eskandarany, M Sherif

    2015-01-01

    This book is a detailed introduction to mechanical alloying, offering guidelines on the necessary equipment and facilities needed to carry out the process and giving a fundamental background to the reactions taking place. El-Eskandarany, a leading authority on mechanical alloying, discusses the mechanism of powder consolidations using different powder compaction processes. A new chapter will also be included on thermal, mechanically-induced and electrical discharge-assisted mechanical milling. Fully updated to cover recent developments in the field, this second edition also introduces new a

  15. Metal-Matrix Hardmetal/Cermet Reinforced Composite Powders for Thermal Spray

    Directory of Open Access Journals (Sweden)

    Dmitri GOLJANDIN

    2012-03-01

    Full Text Available Recycling of materials is becoming increasingly important as industry response to public demands, that resources must be preserved and environment protected. To produce materials competitive in cost with primary product, secondary producers have to pursue new technologies and other innovations. For these purposes different recycling technologies for composite materials (oxidation, milling, remelting etc are widely used. The current paper studies hardmetal/cermet powders produced by mechanical milling technology. The following composite materials were studied: Cr3C2-Ni cermets and WC-Co hardmetal. Different disintegrator milling systems for production of powders with determined size and shape were used. Chemical composition of produced powders was analysed.  To estimate the properties of recycled hardmetal/cermet powders, sieving analysis, laser granulometry and angularity study were conducted. To describe the angularity of milled powders, spike parameter–quadric fit (SPQ was used and experiments for determination of SPQ sensitivity and precision to characterize particles angularity were performed. Images used for calculating SPQ were taken by SEM processed with Omnimet Image Analyser 22. The graphs of grindability and angularity were composed. Composite powders based on Fe- and Ni-self-fluxing alloys for thermal spray (plasma and HVOF were produced. Technological properties of powders and properties of thermal sprayed coatings from studied powders were investigated. The properties of spray powders reinforced with recycled hardmetal and cermet particles as alternatives for cost-sensitive applications were demonstrated.DOI: http://dx.doi.org/10.5755/j01.ms.18.1.1348

  16. The Influence of Milling and Spark Plasma Sintering on the Microstructure and Properties of the Al7075 Alloy

    Science.gov (United States)

    Málek, Přemysl; Minárik, Peter; Novák, Pavel; Průša, Filip

    2018-01-01

    The compact samples of an Al7075 alloy were prepared by a combination of gas atomization, high energy milling, and spark plasma sintering. The predominantly cellular morphology observed in gas atomized powder particles was completely changed by mechanical milling. The continuous-like intermetallic phases present along intercellular boundaries were destroyed; nevertheless, a small amount of Mg(Zn,Cu,Al)2 phase was observed also in the milled powder. Milling resulted in a severe plastic deformation of the material and led to a reduction of grain size from several µm into the nanocrystalline region. The combination of these microstructural characteristics resulted in abnormally high microhardness values exceeding 300 HV. Consolidation through spark plasma sintering (SPS) resulted in bulk samples with negligible porosity. The heat exposition during SPS led to precipitation of intermetallic phases from the non-equilibrium microstructure of both gas atomized and milled powders. SPS of the milled powder resulted in a recrystallization of the severely deformed structure. An ultra-fine grained structure (grain size close to 500 nm) with grains divided primarily by high-angle boundaries was formed. A simultaneous release of stored deformation energy and an increase in the grain size caused a drop of microhardness to values close to 150 HV. This value was retained even after annealing at 425 °C. PMID:29614046

  17. Synthesis of the Mg2Ni alloy prepared by mechanical alloying using a high energy ball mill

    International Nuclear Information System (INIS)

    Iturbe G, J. L.; Lopez M, B. E.; Garcia N, M. R.

    2010-01-01

    Mg 2 Ni was synthesized by a solid state reaction from the constituent elemental powder mixtures via mechanical alloying. The mixture was ball milled for 10 h at room temperature in an argon atmosphere. The high energy ball mill used here was fabricated at ININ. A hardened steel vial and three steel balls of 12.7 mm in diameter were used for milling. The ball to powder weight ratio was 10:1. A small amount of powder was removed at regular intervals to monitor the structural changes. All the steps were performed in a little lucite glove box under argon gas, this glove box was also constructed in our Institute. The structural evolution during milling was characterized by X-ray diffraction and scanning electron microscopy techniques. The hydrogen reaction was carried out in a micro-reactor under controlled conditions of pressure and temperature. The hydrogen storage properties of mechanically milled powders were evaluated by using a thermogravimetric analysis system. Although homogeneous refining and alloying take place efficiently by repeated forging, the process time can be reduced to one fiftieth of the time necessary for conventional mechanical milling and attrition. (Author)

  18. Synthesis of the Mg{sub 2}Ni alloy prepared by mechanical alloying using a high energy ball mill

    Energy Technology Data Exchange (ETDEWEB)

    Iturbe G, J. L.; Lopez M, B. E. [ININ, Departamento de Quimica, Carretera Mexico-Toluca s/n, 52750 Ocoyoacac, Estado de Mexico (Mexico); Garcia N, M. R., E-mail: joseluis.iturbe@inin.gob.m [UNAM, Facultad de Estudios Superiores Zaragoza, Batalla 5 de Mayo s/n, Esq. Fuerte de Loreto, Col. Ejercito de Oriente, 09230 Mexico D. F. (Mexico)

    2010-07-01

    Mg{sub 2}Ni was synthesized by a solid state reaction from the constituent elemental powder mixtures via mechanical alloying. The mixture was ball milled for 10 h at room temperature in an argon atmosphere. The high energy ball mill used here was fabricated at ININ. A hardened steel vial and three steel balls of 12.7 mm in diameter were used for milling. The ball to powder weight ratio was 10:1. A small amount of powder was removed at regular intervals to monitor the structural changes. All the steps were performed in a little lucite glove box under argon gas, this glove box was also constructed in our Institute. The structural evolution during milling was characterized by X-ray diffraction and scanning electron microscopy techniques. The hydrogen reaction was carried out in a micro-reactor under controlled conditions of pressure and temperature. The hydrogen storage properties of mechanically milled powders were evaluated by using a thermogravimetric analysis system. Although homogeneous refining and alloying take place efficiently by repeated forging, the process time can be reduced to one fiftieth of the time necessary for conventional mechanical milling and attrition. (Author)

  19. The Influence of Milling and Spark Plasma Sintering on the Microstructure and Properties of the Al7075 Alloy

    Directory of Open Access Journals (Sweden)

    Orsolya Molnárová

    2018-04-01

    Full Text Available The compact samples of an Al7075 alloy were prepared by a combination of gas atomization, high energy milling, and spark plasma sintering. The predominantly cellular morphology observed in gas atomized powder particles was completely changed by mechanical milling. The continuous-like intermetallic phases present along intercellular boundaries were destroyed; nevertheless, a small amount of Mg(Zn,Cu,Al2 phase was observed also in the milled powder. Milling resulted in a severe plastic deformation of the material and led to a reduction of grain size from several µm into the nanocrystalline region. The combination of these microstructural characteristics resulted in abnormally high microhardness values exceeding 300 HV. Consolidation through spark plasma sintering (SPS resulted in bulk samples with negligible porosity. The heat exposition during SPS led to precipitation of intermetallic phases from the non-equilibrium microstructure of both gas atomized and milled powders. SPS of the milled powder resulted in a recrystallization of the severely deformed structure. An ultra-fine grained structure (grain size close to 500 nm with grains divided primarily by high-angle boundaries was formed. A simultaneous release of stored deformation energy and an increase in the grain size caused a drop of microhardness to values close to 150 HV. This value was retained even after annealing at 425 °C.

  20. Biaxially textured articles formed by powder metallurgy

    Science.gov (United States)

    Goyal, Amit; Williams, Robert K.; Kroeger, Donald M.

    2003-08-05

    A biaxially textured alloy article having a magnetism less than pure Ni includes a rolled and annealed compacted and sintered powder-metallurgy preform article, the preform article having been formed from a powder mixture selected from the group of ternary mixtures consisting of: Ni powder, Cu powder, and Al powder, Ni powder, Cr powder, and Al powder; Ni powder, W powder and Al powder; Ni powder, V powder, and Al powder; Ni powder, Mo powder, and Al powder; the article having a fine and homogeneous grain structure; and having a dominant cube oriented {100} orientation texture; and further having a Curie temperature less than that of pure Ni.

  1. Hollow crystalline straws of diclofenac for high-dose and carrier-free dry powder inhaler formulations.

    Science.gov (United States)

    Yazdi, Ashkan K; Smyth, Hugh D C

    2016-04-11

    To crystallize diclofenac (DF) from diclofenac sodium (DFNa), to micronize DF and DFNa, and to evaluate in vitro aerodynamic performance of the jet-milled formulations From the acidic titration of aqueous DFNa, DF crystals were formed and were identified using thermal analysis, spectroscopy, and X-ray powder diffraction. Following the micronization of the DF and DFNa powders, the recovered samples were imaged, and their particle size distributions were evaluated. Samples before and after jet millings were characterized, and in vitro aerodynamic performance testing was performed on the DF sample before jet milling and the DF and DFNa samples following jet milling. Hollow needles of DF were precipitated. With similar particle size distributions, the jet-milled DFNa sample from the collection bag, and the DF sample from the cyclone were used for further characterization. Despite different deposition patterns in the Next Generation Impactor, the DF hollow needles had a comparable respirable fraction percentage to the jet-milled DF and DFNa particles. However, the jet-milled DF formulation had the best in vitro aerodynamic performance. Hollow, crystalline needles of DF were formed and possessed promising aerosol performance in comparison with the jet-milled powders. Copyright © 2016 Elsevier B.V. All rights reserved.

  2. Synthesis and characterization of FePt nanoparticles by high energy ball milling with and without surfactant

    International Nuclear Information System (INIS)

    Velasco, V.; Martinez, A.; Recio, J.; Hernando, A.; Crespo, P.

    2012-01-01

    Highlights: ► Fe and Pt powders in the presence of surfactants don’t alloyed by HEBM technique. ► FePt alloys obtained by dry milling exhibit particle sizes of around 10 μm. ► FePt alloys obtained by dry milling exhibit soft magnetic behavior. ► A thermal treatment induces a phase transformation from FCC to FCT. - Abstract: FePt nanoparticles were prepared by high energy ball milling (HEBM) in two different ways. In the first one, elemental powders were mixed and milled whereas in the second one the milling was performed in the presence of oleyl amine and oleic acid as surfactants and hexane as a solvent. X-ray diffraction shows that when the milling is performed in dry conditions, Fe and Pt are alloyed after 5 h, whereas in the wet milling procedure alloying does not take place. In the first case, the diffraction pattern corresponds to the disordered FCC phase. This behavior is also corroborated by the evolution of the magnetic characteristics. In the case of the alloy obtained in dry conditions, the powder was heat treated in order to induce the transformation to the ordered phase. Coercivities of 2.5 kOe are obtained after 650 °C for 2 h.

  3. Synthesis and characterization of FePt nanoparticles by high energy ball milling with and without surfactant

    Energy Technology Data Exchange (ETDEWEB)

    Velasco, V., E-mail: vvjimeno@fis.ucm.es [Instituto de Magnetismo Aplicado, UCM-ADIF-CSIC, 28230 Las Rozas (Spain); Martinez, A.; Recio, J. [Instituto de Magnetismo Aplicado, UCM-ADIF-CSIC, 28230 Las Rozas (Spain); Hernando, A.; Crespo, P. [Instituto de Magnetismo Aplicado, UCM-ADIF-CSIC, 28230 Las Rozas (Spain); Dpto. de Fisica de Materiales, UCM, 28040 Madrid (Spain)

    2012-09-25

    Highlights: Black-Right-Pointing-Pointer Fe and Pt powders in the presence of surfactants don't alloyed by HEBM technique. Black-Right-Pointing-Pointer FePt alloys obtained by dry milling exhibit particle sizes of around 10 {mu}m. Black-Right-Pointing-Pointer FePt alloys obtained by dry milling exhibit soft magnetic behavior. Black-Right-Pointing-Pointer A thermal treatment induces a phase transformation from FCC to FCT. - Abstract: FePt nanoparticles were prepared by high energy ball milling (HEBM) in two different ways. In the first one, elemental powders were mixed and milled whereas in the second one the milling was performed in the presence of oleyl amine and oleic acid as surfactants and hexane as a solvent. X-ray diffraction shows that when the milling is performed in dry conditions, Fe and Pt are alloyed after 5 h, whereas in the wet milling procedure alloying does not take place. In the first case, the diffraction pattern corresponds to the disordered FCC phase. This behavior is also corroborated by the evolution of the magnetic characteristics. In the case of the alloy obtained in dry conditions, the powder was heat treated in order to induce the transformation to the ordered phase. Coercivities of 2.5 kOe are obtained after 650 Degree-Sign C for 2 h.

  4. Obtainment of the alloy Cu13Al4Ni using processed by powder metallurgy; Obtencao da liga Cu13Al4Ni via metalurgia do po

    Energy Technology Data Exchange (ETDEWEB)

    Grossi, L.J.; Damasceno, N.; Muterlle, P.V., E-mail: larajgrossi@yahoo.com.br [Universidade de Brasilia (UnB), Brasilia, DF (Brazil). Departamento de Engenharia Mecanica

    2016-07-01

    The powder metallurgy is a technique environmentally advantageous that allows the production of many pieces, with a good superficial finishing and dimensional tolerance. For the production of pieces using technique, basics steps are carried out, as the characterization of powders, the mixing and homogenization, compacting and sintering. In this context, this work has as objective the obtainment of the Cu13Al4Ni alloy via powder metallurgy. For this, was made a high energy milling for 2, 4 and 8 hours. Then, the milled powder was compacted and posteriorly, sintered in an oven with controlled atmosphere. It was observed that the milling time affects directly in sintering of the pieces. The best results obtained were for the samples that were milled for 4 hours. This samples have showed 21, 52% of porosity and 6,382 g/cm³ of the density of sintered. (author)

  5. Fabrication of Fe-Cr-Mo powder metallurgy steel via a mechanical-alloying process

    Science.gov (United States)

    Park, Jooyoung; Jeong, Gowoon; Kang, Singon; Lee, Seok-Jae; Choi, Hyunjoo

    2015-11-01

    In this study, we employed a mechanical-alloying process to manufacture low-alloy CrL and CrM steel powders that have similar specifications to their water-atomized counterparts. X-ray diffraction showed that Mo and Cr are alloyed in Fe after four cycles of planetary milling for 1 h at 150 RPM with 15-min pauses between the cycles (designated as P2C4 process). Furthermore, the measured powder size was found to be similar to that of the water-atomized counterparts according to both scanning electron microscope images and laser particle size analysis. The samples were sintered at 1120 °C, after which the P2C4-milled CrL showed similar hardness to that of water-atomized CrL, whereas the P2C4-milled CrM showed about 45% lower hardness than that of its water-atomized counterpart. Water-atomized CrM consists of a well-developed lathtype microstructure (bainite or martensite), while a higher fraction of polygonal ferrite is observed in P2C4-milled CrM. This phase difference causes the reduction of hardness in the P2C4-milled CrM, implying that the phase transformation behavior of specimens produced via powder metallurgy is influenced by the powder fabrication method.

  6. Structure investigations of ferromagnetic Co-Ni-Al alloys obtained by powder metallurgy.

    Science.gov (United States)

    Maziarz, W; Dutkiewicz, J; Lityńska-Dobrzyńska, L; Santamarta, R; Cesari, E

    2010-03-01

    Elemental powders of Co, Ni and Al in the proper amounts to obtain Co(35)Ni(40)Al(25) and Co(40)Ni(35)Al(25) nominal compositions were ball milled in a high-energy mill for 80 h. After 40 h of milling, the formation of a Co (Ni, Al) solid solution with f.c.c. structure was verified by a change of the original lattice parameter and crystallite size. Analytical transmission electron microscopy observations and X-ray diffraction measurements of the final Co (Ni, Al) solid solution showed that the crystallite size scattered from 4 to 8 nm and lattice parameter a = 0.36086 nm. The chemical EDS point analysis of the milled powder particles allowed the calculation of the e/a ratio and revealed a high degree of chemical homogeneity of the powders. Hot pressing in vacuum of the milled powders resulted in obtaining compacts with a density of about 70% of the theoretical one. An additional heat treatment increased the density and induced the martensitic transformation in a parent phase. Selected area diffraction patterns and dark field images obtained from the heat-treated sample revealed small grains around 300 nm in diameter consisting mainly of the ordered gamma phase (gamma'), often appearing as twins, and a small amount of the L1(0) ordered martensite.

  7. Structural evolution of Fe-50 at.% Al powders during mechanical alloying and subsequent annealing processes

    International Nuclear Information System (INIS)

    Haghighi, Sh. Ehtemam; Janghorban, K.; Izadi, S.

    2010-01-01

    Iron aluminides, despite having desirable properties like excellent corrosion resistance, present low room-temperature ductility and low strength at high temperatures. Mechanical alloying as a capable process to synthesize nanocrystalline materials is under consideration to modify these drawbacks. In this study, the microstructure of iron aluminide powders synthesized by mechanical alloying and subsequent annealing was investigated. Elemental Fe and Al powders with the same atomic percent were milled in a planetary ball mill for 15 min to 100 h. The powder milled for 80 h was annealed at temperatures of 300, 500 and 700 o C for 1 h. The alloyed powders were disordered Fe(Al) solid solutions which were transformed to FeAl intermetallic after annealing. The effect of the milling time and annealing treatment on structural parameters, such as crystallite size, lattice parameter and lattice strain was evaluated by X-ray diffraction. Typically, these values were 15 nm, 2.92 A and 3.1% for the disordered Fe(Al) solid solution milled for 80 h and were 38.5 nm, 2.896 A and 1.2% for the FeAl intermetallic annealed at 700 o C, respectively.

  8. Synthesis behavior of nanocrystalline Al-Al2O3 composite during low time mechanical milling process

    International Nuclear Information System (INIS)

    Alizadeh, Mostafa; Aliabadi, Morteza Mirzaei

    2011-01-01

    Research highlights: → In the low time milling the effect of Al 2 O 3 amount is investigated → Al 2 O 3 particles are distributed uniformly in the Al matrix → In the low time milling it is possible to produce nanostructured composite powder → Median size and bulk density measurements demonstrate reaching the steady state. - Abstract: In this work, four different volume fractions of Al 2 O 3 (10, 20, 30 and 40 vol.%) were mixed with the fine Al powder and the powder blends were milled for 5 h. Scanning electron microscopy analysis, particle size analysis and bulk density measurements were used to investigate the morphological changes and achieving the steady state conditions. The results showed that increasing the Al 2 O 3 content can provide the steady state particle size in 5 h milling process. It was found that increasing the volume fraction of Al 2 O 3 leads to increasing the uniformity of Al 2 O 3 . Standard deviations of microhardness measurements confirmed this result. The XRD pattern and XRF investigations depicted that increasing the Al 2 O 3 content causes an increase in the crystal defects, micro-strain and Fe contamination during 5 h milling process of nanocrystalline composite powders while the grain size is decreased. To investigate the effect of milling time, Al-30 vol.% Al 2 O 3 (which achieved steady state during 5 h milling process) was milled for 1-4 h. The results depicted that the milling time lower than 5 h, do not achieve to steady state conditions.

  9. PREPARATION OF TANTALUM CARBIDE FROM AN ORGANOMETALLIC PRECURSOR

    Directory of Open Access Journals (Sweden)

    C. P. SOUZA

    1999-03-01

    Full Text Available In this work we have synthesized an organometallic oxalic precursor from tantalum oxide. This oxide was solubilized by heating with potassium hydrogen sulfate. In order to precipitate Ta2O5.nH2O, the fused mass obtained was dissolved in a sulfuric acid solution and neutralized with ammonia. The hydrated tantalum oxide precipitated was dissolved in an equimolar solution of oxalic acid/ammonium oxalate. The synthesis and the characterization of the tantalum oxalic precursor are described. Pyrolysis of the complex in a mixture of hydrogen and methane at atmospheric pressure was studied. The gas-solid reaction made it possible to obtain tantalum carbide, TaC, in the powder form at 1000oC. The natural sintering of TaC powder in an inert atmosphere at 1400°C during 10 hours, under inert atmosphere made it possible to densify the carbide to 96% of the theoretical value.

  10. Sintered aluminium powders

    International Nuclear Information System (INIS)

    Stepanova, M.G.; Matveev, B.I.

    1974-01-01

    The mechanical and physical properties of aluminium powder alloys and the various methods employed to produce them are considered. Data are given on the hardening of the alloys SAP and SPAK-4, as well as the powder-alloy system Al-Cr-Zr. (L.M.)

  11. Method and apparatus for adding and mixing second cohesive powders in a fluidized bed blender

    International Nuclear Information System (INIS)

    Larson, R.I.; Brassfield, H.C.; Adomitis, J.T.

    1981-01-01

    Injection and uniform dispersion of a second cohesive powdered ingredient or ingredients having hydrophobic, hydrophilic or hydroscopic properties into a fluidized bed of UO 2 powder is effected by impinging the second ingredient against a deflection plate 21 mounted within the fluidized bed. The apparatus also includes an eductor, a pressurised vortex mill 11 and a pneumatic conveying system. Before entering the fluidized bed, the second ingredient is entrained in a gas and conveyed under pressure to the vortex mill 11 where the particles of the second ingredient are propelled radially outwardly through channels 28 and collide against tungsten carbide impact, blocks 32 causing comminution of the particles. (author)

  12. Synthesis of LiBOB Fine Powder to Increase Solubility

    Directory of Open Access Journals (Sweden)

    Etty Marti Wigayati

    2017-04-01

    Full Text Available Lithium bis (oxalate borate or LiBOB compound has captured interest of researchers, because it is potentially viable to be used as electrolyte salt in lithium-ion battery system. This compound is easy to synthesize and considered to be more environmentally friendly compared to conventional electrolyte salt because LiBOB does not contain halogen element. This research focused on the synthesis of LiBOB fine powder, which main purpose is improving LiBOB salt solubility in liquid electrolyte solution. This will aid the ion transfer between electrodes which in turn will increase the electrolyte performance. Solid state reaction was employed in this experiment. Synthesis of LiBOB compound was performed by reacting oxalic acid dihydrate, lithium hydroxide monohydrate, and boric acid. The resulting powder was then processed into fine powder using ball milling technique with varying milling time (0, 6, 10, and 13 hour. Microstructure of the sample was then analyzed to obtain information regarding phase formation, functional groups, grain surface morphology, surface area, pore volume, solubility, and ionic conductivity. The analysis shown that LiBOB and LiBOB hydrate phase was formed during the reaction, there was no changed in existing phase during milling process, crystallinity index was shifted to lower value but there was no difference in functional groups. Highest value in surface area was found to be 83.11 m2/g, with pore volume of 1.21311e+02 A at 10 hours milling. Smaller powder size resulted in higher solubility, unfortunately the ionic conductivity was found to be decreased.

  13. The EM Earthquake Precursor

    Science.gov (United States)

    Jones, K. B., II; Saxton, P. T.

    2013-12-01

    Many attempts have been made to determine a sound forecasting method regarding earthquakes and warn the public in turn. Presently, the animal kingdom leads the precursor list alluding to a transmission related source. By applying the animal-based model to an electromagnetic (EM) wave model, various hypotheses were formed, but the most interesting one required the use of a magnetometer with a differing design and geometry. To date, numerous, high-end magnetometers have been in use in close proximity to fault zones for potential earthquake forecasting; however, something is still amiss. The problem still resides with what exactly is forecastable and the investigating direction of EM. After the 1989 Loma Prieta Earthquake, American earthquake investigators predetermined magnetometer use and a minimum earthquake magnitude necessary for EM detection. This action was set in motion, due to the extensive damage incurred and public outrage concerning earthquake forecasting; however, the magnetometers employed, grounded or buried, are completely subject to static and electric fields and have yet to correlate to an identifiable precursor. Secondly, there is neither a networked array for finding any epicentral locations, nor have there been any attempts to find even one. This methodology needs dismissal, because it is overly complicated, subject to continuous change, and provides no response time. As for the minimum magnitude threshold, which was set at M5, this is simply higher than what modern technological advances have gained. Detection can now be achieved at approximately M1, which greatly improves forecasting chances. A propagating precursor has now been detected in both the field and laboratory. Field antenna testing conducted outside the NE Texas town of Timpson in February, 2013, detected three strong EM sources along with numerous weaker signals. The antenna had mobility, and observations were noted for recurrence, duration, and frequency response. Next, two

  14. Sinterability and microstructure evolution during sintering of ferrous powder mixtures

    Directory of Open Access Journals (Sweden)

    Kétner Bendo Demétrio

    2013-01-01

    Full Text Available The present work is focused on ferrous powder metallurgy and presents some results of a development of a suitable masteralloy for use as an additive to iron powder for the production of sintered steels. The masteralloy was produced by melting a powder mixture containing approximately Fe + 20% Ni + 20% Mn + 20% Si + 1% C (wt%, in order to obtain a cast billet that was converted into fine powder by crushing and milling. It was observed presence of SiC in the masteralloy after melting that is undesirable in the alloy. Si element should be introduced by using ferrosilicon. Sintered alloys with distinct contents of alloying elements were prepared by mixing the masteralloy powder to plain iron powder. Samples were produced by die compaction of the powder mixtures and sintering at 1200 °C in a differential dilatometer in order to record their linear dimensional behaviour during heating up and isothermal sintering, aiming at studying the sinterability of the compacts. Microstructure development during sintering was studied by SEM, XRD and microprobe analyses.

  15. 7 CFR 868.310 - Grades and grade requirements for the classes Long Grain Milled Rice, Medium Grain Milled Rice...

    Science.gov (United States)

    2010-01-01

    ... Grain Milled Rice, Medium Grain Milled Rice, Short Grain Milled Rice, and Mixed Milled Rice. (See also Â... Milled Rice Principles Governing Application of Standards § 868.310 Grades and grade requirements for the classes Long Grain Milled Rice, Medium Grain Milled Rice, Short Grain Milled Rice, and Mixed Milled Rice...

  16. Mechanochemical preparation of nanocrystalline TiO2 powders and their behavior at high temperatures

    International Nuclear Information System (INIS)

    Gajovic, A.; Furic, K.; Tomasic, N.; Popovic, S.; Skoko, Z.; Music, S.

    2005-01-01

    Nanocrystalline TiO 2 powders were prepared by high-energy ball-milling using zirconia vial and balls. The changes of microstructure caused by material processing were studied using Raman spectroscopy, X-ray powder diffraction (XRD), transmission electron microscopy (TEM) and selected area electron diffraction (SAED). The milling of the starting TiO 2 powder (anatase + rutile in traces) induced phase transitions to high-pressure polymorph, TiO 2 II, and rutile. We found that the phase transition to TiO 2 II was initiated at the surface of the small particles, while transition to rutile started in their center. Changes in crystallite size during milling process were obtained by the Scherrer method, while the particle size changes were monitored by TEM. The kinetics of phase changes, a decrease in crystallite/particle size, as well as zirconia contamination depended on the powder-to-ball weight ratio. The starting powder and some selected ball-milled samples were investigated in situ by Raman spectroscopy and XRD at high temperatures (up to 1300 deg. C) to examine their behavior during the sintering process. A difference in the results obtained by these two techniques was explained in frame of basic physical properties characterizing both methods. The morphology of the final sinters was monitored by scanning electron microscopy (SEM)

  17. Uranium-mill appraisal program

    International Nuclear Information System (INIS)

    Everett, R.J.; Cain, C.L.

    1982-08-01

    The results of special team appraisals at NRC-licensed uranium mills in the period May to November 1981 are reported. Since the Three Mile Island accident, NRC management has instituted a program of special team appraisals of radiation protection programs at certain NRC-licensed facilities. These appraisals were designed to identify weaknesses and strengths in NRC-licensed programs, including those areas not covered by explicit regulatory requirements. The regulatory requirements related to occupational radiation protection and environmental monitoring at uranium mills have been extensively upgraded in the past few years. In addition, there was some NRC staff concern with respect to the effectiveness of NRC licensing and inspection programs. In response to this concern and to changes in mill requirements, the NRC staff recommended that team appraisals be conducted at mills to determine the adequacy of mill programs, the effectiveness of the new requirements, and mill management implementation of programs and requirements. This report describes the appraisal scope and methodology as well as summary findings and conclusions. Significant weaknesses identified during the mill appraisals are discussed as well as recommendations for improvements in uranium mill programs and mill licensing and inspection

  18. Development of an alternative route for recycling AA2050 aluminum alloy by powder metallurgy

    International Nuclear Information System (INIS)

    Guido, V.; Oliveira, A.C. de; Travessa, D.N.; Cardoso, K.R.

    2014-01-01

    This paper presents an alternative solid state route to recycling AA2050 aeronautical aluminium alloy chips. The first stage in the recycling process, reported in this work, is the obtainment of the alloy powder by high energy ball milling to subsequent cold pressing and hot extrusion. The process started with the cleaning of chips with the aim of contaminant removing from machining process and transport, followed by the high energy ball milling to result in the AA2050 alloy powder. The powder obtained was characterized by laser size particle analysis, scanning electron microscopy (SEM), X-Ray diffraction (DRX) and inductively coupled plasma atomic emission spectroscopy (ICP-AES). The results show the feasibility of obtaining a powder having appropriate particle size and chemical composition in accordance with the specification for alloy. (author)

  19. Synthesis of boehmite by hydrothermal treatment used as inorganic binder for alumina powder

    International Nuclear Information System (INIS)

    Lima, M.B.; Tercini, M.B.; Yoshimura, H.N.

    2012-01-01

    Presently, due to the concerns with the environment, it has been developed studies to replace the organic binder by an inorganic binder for forming of ceramic powders, in order to avoiding the generation of polluting gases during sintering (firing). A potential alternative is the use of boehmite, produced by hydrothermal treatment on the surfaces of the alumina powder, previously ground in a ball mill using zirconia milling media to produce hydrated phases on alumina powder which are converted to boehmite. In the treated alumina powders, it was observed the formation of boehmite phase by X-ray diffraction analysis and Fourier transformed infrared (FTIR) spectroscopy, demonstrating the efficiency of boehmite formation during the hydrothermal treatment at 150°C for 3 hours.(author)

  20. Measurement of loose powder density

    International Nuclear Information System (INIS)

    Akhtar, S.; Ali, A.; Haider, A.; Farooque, M.

    2011-01-01

    Powder metallurgy is a conventional technique for making engineering articles from powders. Main objective is to produce final products with the highest possible uniform density, which depends on the initial loose powder characteristics. Producing, handling, characterizing and compacting materials in loose powder form are part of the manufacturing processes. Density of loose metallic or ceramic powder is an important parameter for die design. Loose powder density is required for calculating the exact mass of powder to fill the die cavity for producing intended green density of the powder compact. To fulfill this requirement of powder metallurgical processing, a loose powder density meter as per ASTM standards is designed and fabricated for measurement of density. The density of free flowing metallic powders can be determined using Hall flow meter funnel and density cup of 25 cm/sup 3/ volume. Density of metal powders like cobalt, manganese, spherical bronze and pure iron is measured and results are obtained with 99.9% accuracy. (author)

  1. Uranium mill tailings management

    International Nuclear Information System (INIS)

    1982-01-01

    Facilities for the disposal of uranium mill tailings will invariably be subjected to geomorphological and climatological influences in the long-term. Proceedings of a workshop discuss how the principles of geomorphology can be applied to the siting, design, construction, decommissioning and rehabilitation of disposal facilities in order to provide for long-term containment and stability of tailings. The characteristics of tailings and their behaviour after disposal influence the potential impacts which might occur in the long-term. Proceedings of another workshop examine the technologies for uranium ore processing and tailings conditioning with a view to identifying improvements that could be made in such characteristics

  2. Structural modifications of ultra-high molecular weight polyethylene (UHMWPE) processed in attritor type mill

    International Nuclear Information System (INIS)

    Gabriel, Melina C.; Carvalho, Benjamim de M.; Pinheiro, Luis A.; Cintho, Osvaldo M.; Capocchi, Jose D.T.; Kubaski, Evaldo T.

    2009-01-01

    Ultra-high molecular weight polyethylene (UHMWPE) is a polyethylene that has a high melt viscosity, hence its processing becomes very difficult. High-energy mechanical milling provides physical and chemical changes in polymers that have been studied recently. In order to study these changes in UHMWPE, powder of this polymer was mechanical milled in attritor type mill with a ball-to-powder weight ratio of 40:1 for 8 hours, varying the rotation speed: 200, 300, 400, 500 e 600 rpm. The polymer was characterized by scanning electron microscopy (SEM) and xray diffraction (XRD). From the XRD results it was noted that as the rotation speed increased the monoclinic phase also increased up to 500 rpm. For 600 rpm, the amount of monoclinic phase apparently decreased. At this rotation speed, the deformation rate probably increased the process temperature, allowing the monoclinic phase to return to its initial structural orthorhombic form. (author)

  3. Mechanochemical synthesis of nanostructured chemical hydrides in hydrogen alloying mills

    International Nuclear Information System (INIS)

    Wronski, Z.; Varin, R.A.; Chiu, C.; Czujko, T.; Calka, A.

    2007-01-01

    Mechanical alloying of magnesium metal powders with hydrogen in specialized hydrogen ball mills can be used as a direct route for mechanochemical synthesis of emerging chemical hydrides and hydride mixtures for advanced solid-state hydrogen storage. In the 2Mg-Fe system, we have successfully synthesized the ternary complex hydride Mg 2 FeH 6 in a mixture with nanometric Fe particles. The mixture of complex magnesium-iron hydride and nano-iron released 3-4 wt.%H 2 in a thermally programmed desorption experiment at the range 285-295 o C. Milling of the Mg-2Al powder mixture revealed a strong competition between formation of the Al(Mg) solid solution and the β-MgH 2 hydride. The former decomposes upon longer milling as the Mg atoms react with hydrogen to form the hydride phase, and drive the Al out of the solid solution. The mixture of magnesium dihydride and nano-aluminum released 2.1 wt.%H 2 in the temperature range 329-340 o C in the differential scanning calorimetry experiment. The formation of MgH 2 was suppressed in the Mg-B system; instead, a hydrogenated amorphous phase (Mg,B)H x , was formed in a mixture with nanometric MgB 2 . Annealing of the hydrogen-stabilized amorphous mixture produced crystalline MgB 2

  4. Improvement of deposition efficiency and control of hardness for cold-sprayed coatings using high carbon steel/mild steel mixture powder

    International Nuclear Information System (INIS)

    Ogawa, Kazuhiro; Amao, Satoshi; Yokoyama, Nobuyuki; Ootaki, Kousuke

    2011-01-01

    In this study, in order to make high carbon steel coating by cold spray technique, spray conditions such as carrier gas temperature and pressure etc. were investigated. And also, in order to improve deposition efficiency and control coating hardness of cold-sprayed high carbon steel, high carbon and mild steel mixed powder and its mechanical milled powder were developed and were optimized. By using the cold-spray technique, particle deposition of a high carbon steel was successful. Moreover, by applying mixed and mechanical milled powders, the porosity ratio was decreased and deposition efficiency was improved. Furthermore, using these powders, it is possible to control the hardness value. Especially, when using mechanical milled powder, it is very difficult to identify the interface between the coating and the substrate. The bonding between the coating and the substrate is thus considered to be excellent. (author)

  5. Dependence of hydrogen storage characteristics of mechanically milled carbon materials on their host structures

    International Nuclear Information System (INIS)

    Shindo, K.; Kondo, T.; Sakurai, Y.

    2004-01-01

    We investigated whether the hydrogen storage characteristics of carbon materials prepared by mechanical milling in an H 2 atmosphere were dependent on their host structures. We used natural graphite (NG) and activated carbon fibers (ACF) and compared them with activated carbon (AC) powders. The XRD patterns of NG and ACF milled for over 20 h and SEM images of these samples milled for 80 h were almost the same as those of AC. The hydrogen storage capacities of NG and ACF estimated by the inert gas fusion-thermal conductivity method increased with the mechanical milling time up to 10 h and showed little milling time dependence thereafter. The capacities of NG and ACF reached about 3.0 wt.% and were similar to that of AC. However, it should be noted that the hydrogen storage mechanism of NG and ACF mechanically milled in an H 2 atmosphere might be different because the changes in their specific surface areas with milling time were opposite. Thermal desorption mass spectroscopy (TDS) revealed that the desorption spectra of the hydrogen molecules (mass number=2) of NG and ACF milled for 10 h in the same way as AC contained two peaks at about 500 and 800 deg. C. The desorption activation energies of hydrogenated NG and ACF at these peaks calculated from a Kissinger plot were almost with the same as those of hydrogenated AC. This suggests that the state of the hydrogen trapped in the structural defects in NG introduced by the mechanical milling may be almost the same as that of AC. In addition, we assumed the possibility that the state of the hydrogen in ACF hydrogenated by mechanical milling could be almost the same as that in hydrogenated AC. We considered that the nanocarbon materials hydrogenated under our milling conditions had very similar physical shapes and hydrogen storage capacities, independent of their host structures

  6. Analysis of crystallite size and microdeformation crystal lattice the tungsten carbide milling in mill high energy; Analise do tamanho do cristalito e microdeformacao da rede cristalina do carbeto de tugstenio moidos em moinho de alta energia

    Energy Technology Data Exchange (ETDEWEB)

    Silva, F.T. da; Nunes, M.A.M. [Universidade Federal do Rio Grande do Norte (PPGCEM/UFRN), Natal (Brazil). Programa de Pos-Graduacao em Ciencia e Engenharia de Materiais; Oliveira, R.M.V. de; Silva, G.G. da [Instituto Federal do Rio Grande do Norte (IFRN), Natal (Brazil); Souza, C.P. de; Gomes, U.U. [Universidade Federal do Rio Grande do Norte (UFRN), Natal (Brazil)

    2010-07-01

    The tungsten carbide (WC) has wide application due to its properties like high melting point, high hardness, wear resistance, oxidation resistance and good electrical conductivity. The microstructural characteristics of the starting powders influences the final properties of the carbide. In this context, the use of nanoparticle powders is an efficient way to improve the final properties of the WC. The high energy milling stands out from other processes to obtain nanometric powders due to constant microstructural changes caused by this process. Therefore, the objective is to undertake an analysis of microstructural characteristics on the crystallite size and microdeformations of the crystal lattice using the technique of X-ray diffraction (XRD) using the Rietveld refinement. The results show an efficiency of the milling process to reduce the crystallite size, leading to a significant deformation in the crystal lattice of WC from 5h milling. (author)

  7. Spectroscopy Study of Synthetic Forsterite Obtained from Zeolite Precursors

    Directory of Open Access Journals (Sweden)

    Subotić, B.

    2008-02-01

    Full Text Available Important ceramics materials are prepared from aluminosilicate based precursors using novel methods, offering at the same time a better control over many important properties. Forsterite, due to its good refractoriness with melting point at 2163 K, excellent electrical insulation properties even at high temperatures, low dielectric permittivity, thermal expansion and chemical stability, is a material of interest to engineers and designers especially as an active medium for tuneable laser and is also a material of interest to SOFC (Solid oxide fuel cells manufacturers. The aim of this study is to investigate the synthesis of crystalline forsterite using different zeolite precursors previously activated by ball milling. Synthetic forsterite was synthesized from different zeolite precursors and MgO combining highenergy ball milling and thermal treatment of the mixture under determined conditions of time and temperature for each operation. In this research are studied the solid-state phase transformations taking place at temperatures below 1273 K. The obtained products were characterized using different spectroscopy techniques in comparison with surface analysis method and X-ray diffraction.

  8. Thermal conductivity of 238PuO2 powder, intermediates, and dense fuel forms

    International Nuclear Information System (INIS)

    Bickford, D.F.; Crain, B. Jr.

    1975-10-01

    The thermal conductivities of porous 238 PuO 2 powder (calcined oxalate), milled powder, and high-density granules were calculated from direct measurements of steady-state temperature profiles resulting from self-heating. Thermal conductivities varied with density, temperature, and gas content of the pores. Errors caused by thermocouple heat conduction were less than 5 percent when the dimensions of the thermal conductivity cell and the thermocouple were properly selected

  9. Processing equipment for grinding of building powders

    Science.gov (United States)

    Fediuk, R. S.; Ibragimov, R. A.; Lesovik, V. S.; Pak, A. A.; Krylov, V. V.; Poleschuk, M. M.; Stoyushko, N. Y.; Gladkova, N. A.

    2018-03-01

    In the article questions of mechanical grinding up to nanosize of building powder materials are considered. In the process of mechanoactivation of the composite binder, active molecules of cement minerals arise when molecular packets are destroyed in the areas of defects and loosening of the metastable phase during decompensation of intermolecular forces. The process is accompanied by a change in the kinetics of hardening Portland cement. Mechanical processes in the grinding of mineral materials cause, together with an increase in their surface energy, the growth of the isobaric potential of the powders and, accordingly, their chemical activity, which also contributes to high adhesion strength when they come into contact with binders. Thus, a set of measures for mechanical activation allows more fully use the mass of components of the filled cement systems and regulate their properties. At relatively low costs, it is possible to provide an impressive and, importantly, easily repeatable in production conditions result. It is revealed that the use of a vario-planetary mill allows to achieve the best results on grinding the powder building materials.

  10. Japan steel mill perspective

    Energy Technology Data Exchange (ETDEWEB)

    Murase, K. [Kobe Steel Ltd., Tokyo (Japan)

    2004-07-01

    The international and Japan's steel industry, the coking coal market, and Japan's expectations from Canada's coal industry are discussed. Japan's steel mills are operating at full capacity. Crude steel production for the first half of 2004 was 55.8 million tons. The steel mills are profitable, but costs are high, and there are difficulties with procuring raw materials. Japan is trying to enhance the quality of coke, in order to achieve higher productivity in the production of pig iron. Economic growth is rising disproportionately in the BRICs (Brazil, Russia, India, and China), with a large increase in coking coal demand from China. On the supply side, there are several projects underway in Australia and Canada to increase production. These include new developments by Elk Valley Coal Corporation, Grande Cache Coal, Western Canadian Coal, and Northern Energy and Mining in Canada. The Elga Mine in the far eastern part of Russia is under development. But the market is expected to remain tight for some time. Japan envisions Canadian coal producers will provide a stable coal supply, expansion of production and infrastructure capabilities, and stabilization of price. 16 slides/overheads are included.

  11. Influence of Chemical and Physical Properties of Activated Carbon Powders on Oxygen Reduction and Microbial Fuel Cell Performance

    KAUST Repository

    Watson, Valerie J.; Nieto Delgado, Cesar; Logan, Bruce E.

    2013-01-01

    Commercially available activated carbon (AC) powders made from different precursor materials (coal, peat, coconut shell, hardwood, and phenolic resin) were electrochemically evaluated as oxygen reduction catalysts and tested as cathode catalysts

  12. Sol-gel synthesis and densification of aluminoborosilicate powders. Part 1: Synthesis

    Science.gov (United States)

    Bull, Jeffrey; Selvaduray, Guna; Leiser, Daniel

    1992-01-01

    Aluminoborosilicate powders high in alumina content were synthesized by the sol-gel process utilizing various methods of preparation. Properties and microstructural effects related to these syntheses were examined. After heating to 600 C for 2 h in flowing air, the powders were amorphous with the metal oxides comprising 87 percent of the weight and uncombusted organics the remainder. DTA of dried powders revealed a T(sub g) at approximately 835 C and an exotherm near 900 C due to crystallization. Powders derived from aluminum secbutoxide consisted of particles with a mean diameter 5 microns less than those from aluminum isopropoxide. Powders synthesized with aluminum isopropoxide produced agglomerates comprised of rod shaped particulates while powders made with the secbutoxide precursor produced irregular glassy shards. Compacts formed from these powders required different loadings for equivalent densities according to the method of synthesis.

  13. Effect of heat treatment on Fe-B-Si-Nb alloy powder prepared by mechanical alloying

    Directory of Open Access Journals (Sweden)

    Rodrigo Estevam Coelho

    2005-06-01

    Full Text Available The effect of heat treatment on crystallization behavior of Fe73.5B15Si10Nb1.5 alloy powder prepared by mechanical alloying was studied. The powder samples were prepared by mechanical alloying (MA and for different milling times (1, 5, 25, 70 and 100 hours. Crystalline powders of iron, boron, silicon and niobium were sealed with tungsten carbide balls in a cylindrical vial under nitrogen atmosphere. The ball-to-powder weight ratio was 20 to 1. A Fritsch Pulverizette 5 planetary ball mill was used for MA the powders at room temperature and at 250 rpm. To study the microstructural evolution, a small amount of powder was collected after different milling times and examined by X-ray diffraction, using CuKalpha radiation (lambda = 0.15418 nm. The crystallization behavior was studied by differential thermal analysis, from 25 up to 1000 °C at a heating rate of 25 °C min-1.

  14. Bioassay for uranium mill tailings

    International Nuclear Information System (INIS)

    Tschaeche, A.N.

    1986-01-01

    Uranium mill tailings are composed of fine sand that contains, among other things, some uranium (U/sup 238/ primarily), and all of the uranium daughters starting with /sup 230/Th that are left behind after the usable uranium is removed in the milling process. Millions of pounds of tailings are and continue to be generated at uranium mills around the United States. Discrete uranium mill tailings piles exist near the mills. In addition, the tailings materials were used in communities situated near mill sites for such purposes as building materials, foundations for buildings, pipe runs, sand boxes, gardens, etc. The Uranium Mill Tailings Remedial Action Project (UMTRAP) is a U.S. Department of Energy Program designed with the intention of removing or stabilizing the mill tailings piles and the tailings used to communities so that individuals are not exposed above the EPA limits established for such tailings materials. This paper discusses the bioassay programs that are established for workers who remove tailings from the communities in which they are placed

  15. Indian Americans at Mille Lacs.

    Science.gov (United States)

    Holbert, Victoria L.; And Others

    The Training Center for Community Programs prepared a report on the Mille Lacs (Chippewa) Reservation in Minnesota. Data for the report were from 2 separate sources: a survey conducted by the Training Center with the assistance of the Mille Lacs community action program (1967) and an attitudinal survey conducted by Victoria Holbert during 1969.…

  16. Surface Area, and Oxidation Effects on Nitridation Kinetics of Silicon Powder Compacts

    Science.gov (United States)

    Bhatt, R. T.; Palczer, A. R.

    1998-01-01

    Commercially available silicon powders were wet-attrition-milled from 2 to 48 hr to achieve surface areas (SA's) ranging from 1.3 to 70 sq m/g. The surface area effects on the nitridation kinetics of silicon powder compacts were determined at 1250 or 1350 C for 4 hr. In addition, the influence of nitridation environment, and preoxidation on nitridation kinetics of a silicon powder of high surface area (approximately equals 63 sq m/g) was investigated. As the surface area increased, so did the percentage nitridation after 4 hr in N2 at 1250 or 1350 C. Silicon powders of high surface area (greater than 40 sq m/g) can be nitrided to greater than 70% at 1250 C in 4 hr. The nitridation kinetics of the high-surface-area powder compacts were significantly delayed by preoxidation treatment. Conversely, the nitridation environment had no significant influence on the nitridation kinetics of the same powder. Impurities present in the starting powder, and those accumulated during attrition milling, appeared to react with the silica layer on the surface of silicon particles to form a molten silicate layer, which provided a path for rapid diffusion of nitrogen and enhanced the nitridation kinetics of high surface area silicon powder.

  17. POWDER COAT APPLICATIONS

    Science.gov (United States)

    The report discusses an investigation of critical factors that affect the use of powder coatings on the environment, cost, quality, and production. The investigation involved a small business representative working with the National Defense Center for Environmental Excellence (ND...

  18. OIL SOLUTIONS POWDER

    Science.gov (United States)

    Technical product bulletin: aka OIL SOLUTIONS POWDER, SPILL GREEN LS, this miscellaneous oil spill control agent used in cleanups initially behaves like a synthetic sorbent, then as a solidifier as the molecular microencapsulating process occurs.

  19. Synthesis of nanostructured LiTi2(PO4)3 powder by a Pechini-type polymerizable complex method

    International Nuclear Information System (INIS)

    Mariappan, C.R.; Galven, C.; Crosnier-Lopez, M.-P.; Le Berre, F.; Bohnke, O.

    2006-01-01

    The nanostructured NASICON-type LiTi 2 (PO 4 ) 3 (LTP) material has been synthesized by Pechini-type polymerizable complex method. The use of water-soluble ammonium citratoperoxotitanate (IV) metal complex instead of alkoxides as precursor allows to prepare monophase material. Thermal analyses have been carried out on the powder precursor to check the weight loss and synthesis temperature. X-ray powder diffraction analysis (XRD) has been performed on the LTP powder obtained after heating the powder precursor over a temperature range from 550 to 1050 deg. C for 2 h. By varying the molar ratio of citric acid to metal ion (CA/Ti) and citric acid to ethylene glycol (CA/EG), the grain size of the LTP powder could be modified. The formation of small and well-crystalline grains, in the order of 50-125 nm in size, has been determined from the XRD patterns and confirmed by transmission electron microscopy

  20. Effect of processing of mechanical alloying and powder metallurgy on microstructure and properties of Cu-Al-Ni-Mn alloy

    International Nuclear Information System (INIS)

    Xiao Zhu; Li Zhou; Fang Mei; Xiong Shiyun; Sheng Xiaofei; Zhou Mengqi

    2008-01-01

    The fabrication conditions of Cu-Al-Ni-Mn alloy powder by mechanical alloying and powder metallurgy have been systematically studied. The mechanically alloyed powder (MAed powder) was fabricated at a speed between 100 rpm and 300 rpm for various milling times with and without process control agent (PCA). With an increasing of milling time, the size of crystallite grain decreases. Only the Cu diffraction pattern appear as the rotation speed is up to 300 rpm for 25 h. The elemental powders with PCA agglomerate slightly, but the degree of alloying is lower than that without PCA. The shape memory recovery of the quenched sample hot-extruded at extrusion rate of 50:1 is measured to be 100% recovered in 250 deg. C oil bath for 40 s after deformed to 4.0%. After aging at 120 deg. C for 10 days, the shape memory recovery of the alloy remains 98%

  1. Plasma sintering of ferritic steel reinforced with niobium carbide prepared by high energy milling

    International Nuclear Information System (INIS)

    Silva Junior, J.F. da; Almeida, E.O.; Gomes, U.U.; Alves Junior, C.; Messias, A.P.; Universidade Federal do Rio Grande do Norte

    2010-01-01

    Plasma is an ionized gas where ions are accelerated from anode to cathode surface, where the sample is placed. There are a lot of collisions on cathode surface by ions heating and sintering the sample. High energy milling (HEM) is often used to produce composite particles to be used on powder metallurgy. These particles can exhibit fine particles and high phase dispersion. This present work aim to study ferritic steels reinforced with 3%NbC prepared by HEM and sintered on plasma furnace. Ferritic steel and NbC powders were milled during 5 hours and characterized by SEM, XRD and laser scattering. Then, these composite powders were compacted in a cylindrical steel die and then sintered in a plasma furnace. Vickers microhardness tests and SEM and XRD analysis were performed on sintered samples. (author)

  2. Using of fluidized-bed jet mill to a super fine comminution of steel composite

    Directory of Open Access Journals (Sweden)

    D. Urbaniak

    2015-01-01

    Full Text Available In many industries the demand for very fine material increases. In the metallurgical industry, for example, there is increasing use of the production of high density metal elements with the use of metallurgical powder composites. The use of powder composites requires prior their grinding. Unfortunately, the very fine grinding is not an easy process. The using for this purpose fluidized-bed jet mill was proposed in the paper. The attempts of grinding of metallurgical powder were carried out in the fluidized-bed jet mill. After the experiment analyses of particle size distribution of grinding products were performed. The results are presented in graphs. Analyses of the obtained results concluded that the grinding of very fine metallurgical composite is possible and produces positive results.

  3. Effect of cryogenic milling on Al7075 prepared by spark plasma sintering method.

    Czech Academy of Sciences Publication Activity Database

    Lukáč, František; Chráska, Tomáš; Molnárová, O.; Málek, P.; Cinert, Jakub

    2017-01-01

    Roč. 32, S1 (2017), S221-S224 ISSN 0885-7156. [European Powder Diffraction Conference (EPDIC) /15./. Bari, 12.06.2016-15.06.2016] R&D Projects: GA ČR(CZ) GA15-15609S Institutional support: RVO:61389021 Keywords : Intermetallic precipitates * cryogenic milling * powder metallurgy * ultrafine-grained materials * Al7075 alloy Subject RIV: JG - Metallurgy OBOR OECD: Materials engineering Impact factor: 0.674, year: 2016 https://www.cambridge.org/core/journals/powder-diffraction/ article /effect-of-cryogenic-milling-on-al7075-prepared-by-spark-plasma-sintering-method/17E9F722BAFD428BA7310194FEE551C6

  4. Compact Process for the Preparation of Microfine Spherical High-Niobium-Containing TiAl Alloy Powders

    Science.gov (United States)

    Tong, J. B.; Lu, X.; Liu, C. C.; Wang, L. N.; Qu, X. H.

    2015-03-01

    High-Nb-containing TiAl alloys are a new generation of materials for high-temperature structural applications because of their superior high-temperature mechanical properties. The alloy powders can be widely used for additive manufacturing, thermal spraying, and powder metallurgy. Because of the difficulty of making microfine spherical alloy powders in quantity by conventional techniques, a compact method was proposed, which consisted of two-step ball milling of elemental powders and subsequent radio frequency (RF) argon plasma spheroidization. In comparison with conventional mechanical alloying techniques, the two-step milling process can be used to prepare alloy powders with uniform scale in a short milling time with no addition of process control agent. This makes the process effective and less contaminating. After RF argon plasma spheroidization, the powders produced exhibit good sphericity, and the number-average diameter is about 8.2 μm with a symmetric unimodal particle size distribution. The powders perform high composition homogeneity and contain predominately supersaturated α 2-Ti3Al phase. The oxygen and carbon contents of the spheroidized powder are 0.47% and 0.050%, respectively.

  5. Sol-gel preparation of lead magnesium niobate (PMN) powders and thin films

    Science.gov (United States)

    Boyle, T.J.

    1999-01-12

    A method of preparing a lead magnesium niobium oxide (PMN), Pb(Mg{sub 1/3}Nb{sub 2/3})O{sub 3}, precursor solution by a solvent method wherein a liquid solution of a lead-complex PMN precursor is combined with a liquid solution of a niobium-complex PMN precursor, the combined lead- and niobium-complex liquid solutions are reacted with a magnesium-alkyl solution, forming a PMN precursor solution and a lead-based precipitate, and the precipitate is separated from the reacted liquid PMN precursor solution to form a precipitate-free PMN precursor solution. This precursor solution can be processed to form both ferroelectric powders and thin films. 3 figs.

  6. Magnetically responsive enzyme powders

    Energy Technology Data Exchange (ETDEWEB)

    Pospiskova, Kristyna, E-mail: kristyna.pospiskova@upol.cz [Regional Centre of Advanced Technologies and Materials, Palacky University, Slechtitelu 11, 783 71 Olomouc (Czech Republic); Safarik, Ivo, E-mail: ivosaf@yahoo.com [Regional Centre of Advanced Technologies and Materials, Palacky University, Slechtitelu 11, 783 71 Olomouc (Czech Republic); Department of Nanobiotechnology, Institute of Nanobiology and Structural Biology of GCRC, Na Sadkach 7, 370 05 Ceske Budejovice (Czech Republic)

    2015-04-15

    Powdered enzymes were transformed into their insoluble magnetic derivatives retaining their catalytic activity. Enzyme powders (e.g., trypsin and lipase) were suspended in various liquid media not allowing their solubilization (e.g., saturated ammonium sulfate and highly concentrated polyethylene glycol solutions, ethanol, methanol, 2-propanol) and subsequently cross-linked with glutaraldehyde. Magnetic modification was successfully performed at low temperature in a freezer (−20 °C) using magnetic iron oxides nano- and microparticles prepared by microwave-assisted synthesis from ferrous sulfate. Magnetized cross-linked enzyme powders were stable at least for two months in water suspension without leakage of fixed magnetic particles. Operational stability of magnetically responsive enzymes during eight repeated reaction cycles was generally without loss of enzyme activity. Separation of magnetically modified cross-linked powdered enzymes from reaction mixtures was significantly simplified due to their magnetic properties. - Highlights: • Cross-linked enzyme powders were prepared in various liquid media. • Insoluble enzymes were magnetized using iron oxides particles. • Magnetic iron oxides particles were prepared by microwave-assisted synthesis. • Magnetic modification was performed under low (freezing) temperature. • Cross-linked powdered trypsin and lipase can be used repeatedly for reaction.

  7. Ductile zirconium powder by hydride-dehydride process

    Energy Technology Data Exchange (ETDEWEB)

    Krishnan, T S [BHABHA ATOMIC RESEARCH CENTRE, BOMBAY (INDIA); CHAUDHARY, S [NUCLEAR FUEL COMPLEX, HYDERABAD (INDIA)

    1976-09-01

    The preparation of ductile zirconium powder by the hydride-dehydride process has been described. In this process massive zirconium obtained from Kroll reduction of ZrCl/sub 4/ is first rendered brittle by hydrogenation and the hydride crushed and ground in a ball mill to the required particle size. Hydrogen is then hot vacuum extracted to yield the metal powder. The process has been successfully employed for the production of zirconium powders with low oxygen content and having hardness values in the range of 115-130 BHN, starting from a zirconium sponge of 100-120 BHN hardness. Influence of surface characteristics of the starting metal on its hydriding behaviour has been studied and the optimum hydriding-dehydriding conditions established.

  8. Yttrium orthoferrite powder obtained by the mechanochemical synthesis

    Directory of Open Access Journals (Sweden)

    Lazarević Zorica Ž.

    2017-01-01

    Full Text Available Yttrium orthoferrite (YFeO3 powder was prepared by a mechanochemical synthesis from a mixture of Y2O3 and α-Fe2O3 powders in a planetary ball mill for 2.5 h. The obtained YFeO3 powder sample was characterized by X-ray diffraction (XRD, Raman and infrared spectroscopy. The average crystallite size calculated by the Scherrer equation was 12 nm. The Mössbauer spectroscopy at room temperature confirms the superparamagnetic character of YFeO3 orthoferrite sample. [Project of the Serbian Ministry of Education, Science and Technological Development, Grant no. III 45003, Grant no. III 45015, Grant no. III 45018

  9. Characteristics of Inconel Powders for Powder-Bed Additive Manufacturing

    Directory of Open Access Journals (Sweden)

    Quy Bau Nguyen

    2017-10-01

    Full Text Available In this study, the flow characteristics and behaviors of virgin and recycled Inconel powder for powder-bed additive manufacturing (AM were studied using different powder characterization techniques. The results revealed that the particle size distribution (PSD for the selective laser melting (SLM process is typically in the range from 15 μm to 63 μm. The flow rate of virgin Inconel powder is around 28 s·(50 g−1. In addition, the packing density was found to be 60%. The rheological test results indicate that the virgin powder has reasonably good flowability compared with the recycled powder. The inter-relation between the powder characteristics is discussed herein. A propeller was successfully printed using the powder. The results suggest that Inconel powder is suitable for AM and can be a good reference for researchers who attempt to produce AM powders.

  10. Hydrophilic functionalized silicon nanoparticles produced by high energy ball milling

    Science.gov (United States)

    Hallmann, Steffen

    The mechanochemical synthesis of functionalized silicon nanoparticles using High Energy Ball Milling (HEBM) is described. This method facilitates the fragmentation of mono crystalline silicon into the nanometer regime and the simultaneous surface functionalization of the formed particles. The surface functionalization is induced by the reaction of an organic liquid, such as alkynes and alkenes with reactive silicon sites. This method can be applied to form water soluble silicon nanoparticles by lipid mediated micelle formation and the milling in organic liquids containing molecules with bi-functional groups, such as allyl alcohol. Furthermore, nanometer sized, chloroalkyl functionalized particles can be synthesized by milling the silicon precursor in the presence of an o-chloroalkyne with either alkenes or alkynes as coreactants. This process allows tuning of the concentration of the exposed, alkyl linked chloro groups, simply by varying the relative amounts of the coreactant. The silicon nanoparticles that are formed serve as the starting point for a wide variety of chemical reactions, which may be used to alter the surface properties of the functionalized nanoparticles. Finally, the use of functionalized silicon particles for the production of superhydrophobic films is described. Here HEBM proves to be an efficient method to produce functionalized silicon particles, which can be deposited to form a stable coating exhibiting superhydrophobic properties. The hydrophobicity of the silicon film can be tuned by the milling time and thus the resulting surface roughness of the films.

  11. Determination of milling parameters to obtain mechanosynthesized ZnFe2O4

    International Nuclear Information System (INIS)

    Jean, Malick; Nachbaur, Virginie

    2008-01-01

    In this work, the mechanosynthesis of zinc ferrite in WC vials is studied. Millings are performed under air, with a planetary ball-milling, starting from elemental oxides α-Fe 2 O 3 and ZnO. As-milled powders are structurally and magnetically characterized by X-ray diffraction and Moessbauer spectroscopy. Milling parameters as rotational speeds of main disc and vials are particularly discussed in terms of influence on the obtaining of a pure zinc ferrite phase. These parameters have a strong influence on injected power, on radial and tangential components of the impact force. Friction phenomenon, associated with injected power, have been found to be the governing parameters of the end product

  12. Quantification of process induced disorder in milled samples using different analytical techniques

    DEFF Research Database (Denmark)

    Zimper, Ulrike; Aaltonen, Jaakko; McGoverin, Cushla M.

    2012-01-01

    The aim of this study was to compare three different analytical methods to detect and quantify the amount of crystalline disorder/ amorphousness in two milled model drugs. X-ray powder diffraction (XRPD), differential scanning calorimetry (DSC) and Raman spectroscopy were used as analytical methods...... and indomethacin and simvastatin were chosen as the model compounds. These compounds partly converted from crystalline to disordered forms by milling. Partial least squares regression (PLS) was used to create calibration models for the XRPD and Raman data, which were subsequently used to quantify the milling......-induced crystalline disorder/ amorphousness under different process conditions. In the DSC measurements the change in heat capacity at the glass transition was used for quantification. Differently prepared amorphous indomethacin standards (prepared by either melt quench cooling or cryo milling) were compared...

  13. Effect of mechanical milling on barium titanate (BaTiO3) perovskite

    Science.gov (United States)

    Singh, Rajan Kumar; Sanodia, Sagar; Jain, Neha; Kumar, Ranveer

    2018-05-01

    Commercial Barium Titanate BaTiO3 (BT) is milled by planetary ball mill in acetone medium using stainless steel bowl & ball for different hours. BT is an important perovskite oxide with structure ABO3. BT has applications in electro-optic devices, energy storing devices such as photovoltaic cells, thermistors, multiceramic capacitors & DRAMs etc. BT is non-toxic & environment friendly ceramic with high dielectric and piezoelectric property so it can be used as the substitute of PZT & PbTiO3. Here, we have investigated the effect of milling time and temperature on particle size and phase transition of BT powder. We used use Raman spectroscopy for studying the spectra of BT; XRD is used for structural study. Intensity (height) of Raman spectra and XRD spectra continuously decrease with increasing the milling hours and width if these spectra increases which indicates, decrease in BT size.

  14. Identified EM Earthquake Precursors

    Science.gov (United States)

    Jones, Kenneth, II; Saxton, Patrick

    2014-05-01

    Many attempts have been made to determine a sound forecasting method regarding earthquakes and warn the public in turn. Presently, the animal kingdom leads the precursor list alluding to a transmission related source. By applying the animal-based model to an electromagnetic (EM) wave model, various hypotheses were formed, but the most interesting one required the use of a magnetometer with a differing design and geometry. To date, numerous, high-end magnetometers have been in use in close proximity to fault zones for potential earthquake forecasting; however, something is still amiss. The problem still resides with what exactly is forecastable and the investigating direction of EM. After a number of custom rock experiments, two hypotheses were formed which could answer the EM wave model. The first hypothesis concerned a sufficient and continuous electron movement either by surface or penetrative flow, and the second regarded a novel approach to radio transmission. Electron flow along fracture surfaces was determined to be inadequate in creating strong EM fields, because rock has a very high electrical resistance making it a high quality insulator. Penetrative flow could not be corroborated as well, because it was discovered that rock was absorbing and confining electrons to a very thin skin depth. Radio wave transmission and detection worked with every single test administered. This hypothesis was reviewed for propagating, long-wave generation with sufficient amplitude, and the capability of penetrating solid rock. Additionally, fracture spaces, either air or ion-filled, can facilitate this concept from great depths and allow for surficial detection. A few propagating precursor signals have been detected in the field occurring with associated phases using custom-built loop antennae. Field testing was conducted in Southern California from 2006-2011, and outside the NE Texas town of Timpson in February, 2013. The antennae have mobility and observations were noted for

  15. Study of the viability to obtain quasicrystal in the composition AlCuFe using high-energy milling, followed by pressing and sintering

    International Nuclear Information System (INIS)

    Coelho, Rodrigo Estevam; Cruz, Ramon Mateus Santos; Esteves, Paulo Jesus Costa; Viana, Silvana Garcia; Lima, Severino Jackson Guedes de

    2009-01-01

    This work was observed the phase formations of the mixture Al-Cu-Fe processed vial mechanical alloying, powders pressing at room temperature and subsequent heat treatment. The mixture of powders was made on the nominal composition Al 65 Cu 2 0Fe 15 . A mill of high energy of the horizontal atrittor type was used to process the powders mixtures, in fixed time of two hours of milling. After milling, the powders were pressing in a die closed, with a diameter of about 28mm. The samples were observed by optical microscopy and analyzed X-ray diffractometry. The results obtained in this study provide a basis for setting parameters may be used as a basis for future research and possible applications. (author)

  16. Biaxially textured articles formed by powder metallurgy

    Science.gov (United States)

    Goyal, Amit; Williams, Robert K.; Kroeger, Donald M.

    2003-07-29

    A biaxially textured alloy article having a magnetism less than pure Ni includes a rolled and annealed compacted and sintered powder-metallurgy preform article, the preform article having been formed from a powder mixture selected from the group of mixtures consisting of: at least 60 at % Ni powder and at least one of Cr powder, W powder, V powder, Mo powder, Cu powder, Al powder, Ce powder, YSZ powder, Y powder, Mg powder, and RE powder; the article having a fine and homogeneous grain structure; and having a dominant cube oriented {100} orientation texture; and further having a Curie temperature less than that of pure Ni.

  17. Nano powders, components and coatings by plasma technique

    Science.gov (United States)

    McKechnie, Timothy N. (Inventor); Antony, Leo V. M. (Inventor); O'Dell, Scott (Inventor); Power, Chris (Inventor); Tabor, Terry (Inventor)

    2009-01-01

    Ultra fine and nanometer powders and a method of producing same are provided, preferably refractory metal and ceramic nanopowders. When certain precursors are injected into the plasma flame in a reactor chamber, the materials are heated, melted and vaporized and the chemical reaction is induced in the vapor phase. The vapor phase is quenched rapidly to solid phase to yield the ultra pure, ultra fine and nano product. With this technique, powders have been made 20 nanometers in size in a system capable of a bulk production rate of more than 10 lbs/hr. The process is particularly applicable to tungsten, molybdenum, rhenium, tungsten carbide, molybdenum carbide and other related materials.

  18. Nano powders, components and coatings by plasma technique

    Science.gov (United States)

    McKechnie, Timothy N [Brownsboro, AL; Antony, Leo V. M. [Huntsville, AL; O'Dell, Scott [Arab, AL; Power, Chris [Guntersville, AL; Tabor, Terry [Huntsville, AL

    2009-11-10

    Ultra fine and nanometer powders and a method of producing same are provided, preferably refractory metal and ceramic nanopowders. When certain precursors are injected into the plasma flame in a reactor chamber, the materials are heated, melted and vaporized and the chemical reaction is induced in the vapor phase. The vapor phase is quenched rapidly to solid phase to yield the ultra pure, ultra fine and nano product. With this technique, powders have been made 20 nanometers in size in a system capable of a bulk production rate of more than 10 lbs/hr. The process is particularly applicable to tungsten, molybdenum, rhenium, tungsten carbide, molybdenum carbide and other related materials.

  19. Analysis of the production of U3O8 powder for low enrichment fuel plates

    International Nuclear Information System (INIS)

    Boero, N.L.; Celora, J.; Parodi, C.A.; Ponieman, G.; Kellner, M.; Marajofsky, A.

    1987-01-01

    Description is made of the processes used in the production of U 3 O 8 powder for low enrichment plates for fuel elements for Research Reactors. The analysis of the efficiency of each batch is foccused on the relationship between milling and sieving times and the morphology of the product in each production step. (Author)

  20. Effects of Temperature variations on the Super Fine Powderization of Korean Cultivated Wild Ginseng

    Directory of Open Access Journals (Sweden)

    Jin Ho Kim

    2006-12-01

    Full Text Available Objectives : The aim of this study was to find optimal conditions for producing red ginseng from cultivated wild ginseng using the Turbo Mill. Methods : Characteristics of powdered cultivated wild ginseng based on various temperature settings of the Turbo Mill were observed, and changes in the content was measured by HPLC for various ginsenosides. Results : 1. The diameter of cultivated wild ginseng powder ground by the Turbo Mill was around 10㎛. 2. As the temperature rose, presusre, Specific Mechanical Energy(SME, and density decreased, whileas Water Solubility Index(WSI increased. 3. As the temperature rose, super fine powder showed tendency to turn into dark brown. 4. Measuring content changes by HPLC, there was no detection of ginsenoside Rg3 and ginsenosideRg1, Rb1, and Rh2 concentrations decreased with increase in temperature. Conclusions : Super fine powder of cultivated wild ginseng produced by the Turbo Mill promotes easy absorption of effective ingredients by breaking the cell walls. Using this mechanism to produce red ginseng from cultivated wild ginseng, it yielded less than satisfactory results under the current experiment setup. Furtherresearches are needed to verify more suitable condition for the production of red ginseng.

  1. Structure and hardness of a hard metal alloy prepared with a WC powder synthesized at low temperature

    Energy Technology Data Exchange (ETDEWEB)

    Costa, F.A. da [Programa de Pos-Graduacao em Ciencia e Engenharia de Materiais, UFRN, Campus Universitario, 59072-970 Natal, RN (Brazil)], E-mail: francineac@yahoo.com; Medeiros, F.F.P. de [Programa de Pos-Graduacao em Ciencia e Engenharia de Materiais, UFRN, Campus Universitario, 59072-970 Natal, RN (Brazil); Silva, A.G.P. da [Laboratorio de Materiais Avancados, UENF, 28015-620 Campos de Goytacazes, RJ (Brazil); Gomes, U.U. [Departamento de Fisica Teorica e Experimental, UFRN, Campus Universitario, 59072-970 Natal, RN (Brazil); Filgueira, M. [Laboratorio de Materiais Avancados, UENF, 28015-620 Campos de Goytacazes, RJ (Brazil); Souza, C.P. de [Laboratorio de Termodinamica e Reatores, UFRN, Campus Universitario, 59072-970 Natal, RN (Brazil)

    2008-06-25

    The structure and hardness of a WC-10 wt% Co alloy prepared with an experimental WC powder are compared with those of another alloy of the same composition produced under the same conditions and prepared with a commercial WC powder. The experimental WC powder was synthesized by a gas-solid reaction between APT and methane at low temperature and the commercial WC powder was conventionally produced by a solid-solid reaction between tungsten and carbon black. WC-10 wt% Co alloys with the two powders were prepared under the same conditions of milling and sintering. The structure of the sample prepared with the experimental WC powder is homogeneous and coarse grained. The structure of the sample prepared with the commercial powder is heterogeneous. Furthermore the size and shape of the WC grains are significantly different.

  2. Powder metallurgical processing of magnetostrictive materials based on rare earth-iron intermetallic compounds

    International Nuclear Information System (INIS)

    Malekzadeh, M.

    1978-01-01

    Procedures are described for fabrication of high density rare earth-iron magnetostrictive compounds by powder metallurgical techniques. The fabrication involves a sequence of steps which includes preparing the pre-alloyed compounds, pulverizing them into a fine powder, compacting in suitable sizes and shapes, and sintering. Samples prepared by these procedures are carefully characterized by scanning electron microscopy, x-ray diffraction, dilatometry, and magnetic measurements. Process steps are found to exert important influences upon densities, microstructure and magnetic properties attained after densification. Investigations on a number of these process steps, including milling time and medium, sintering, and magnetic powder alignment are described

  3. Wear of micro end mills

    DEFF Research Database (Denmark)

    Bissacco, Giuliano; Hansen, Hans Nørgaard; De Chiffre, Leonardo

    2005-01-01

    This paper addresses the important issue of wear on micro end mills considering relevant metrological tools for its characterization and quantification. Investigation of wear on micro end mills is particularly difficult and no data are available in the literature. Small worn volumes cause large...... part. For this investigation 200 microns end mills are considered. Visual inspection of the micro tools requires high magnification and depth of focus. 3D reconstruction based on scanning electron microscope (SEM) images and stereo-pair technique is foreseen as a possible method for quantification...

  4. Dry grinding of talc in a stirred ball mill

    Directory of Open Access Journals (Sweden)

    Cayirli Serkan

    2016-01-01

    Full Text Available The aim of this work was to investigate micro fine size dry grindability of talc in a stirred ball mill. The effects of various parameters such as grinding time, stirrer speed, powder filling ratio and ball filling ratio were investigated. Alumina balls were used as grinding media. Experiments were carried out using the 24 full factorial design. The main and interaction effects were evaluated using the Yates method. Test results were evaluated on the basis of product size and surface area.

  5. Synthesis of nanosized powders of stabilized zirconia

    International Nuclear Information System (INIS)

    Takodoro, Sandra Kiyoko

    2000-01-01

    Zirconia solid solutions containing 3 mol % Yttria or 12 mol % ceria have been prepared by the coprecipitation technique followed by azeotropic distillation. The aim of this work is the synthesis of tetragonal zirconia polycrystals nanosized powders that sinter at comparatively lower temperatures attaining high densification, and without using any milling procedure. The main results show that: 1- the dopant cation has a strong influence on the crystallization behavior of the precipitates; 2- the used techniques allowed for obtaining high values of specific surface area (∼130 m 2 .g -1 ); 3- the optimization of the synthesis and processing parameters are responsible for obtaining high densification (≥97% of the theoretical value), at lower temperatures (∼1200 deg C) with average grain sizes lower than 500 nm; 4- impedance spectroscopy results show a strong correlation between the electrical resistivity and the microstructure of sintered ceramics.(author)

  6. Ultrafine hydrogen storage powders

    Science.gov (United States)

    Anderson, Iver E.; Ellis, Timothy W.; Pecharsky, Vitalij K.; Ting, Jason; Terpstra, Robert; Bowman, Robert C.; Witham, Charles K.; Fultz, Brent T.; Bugga, Ratnakumar V.

    2000-06-13

    A method of making hydrogen storage powder resistant to fracture in service involves forming a melt having the appropriate composition for the hydrogen storage material, such, for example, LaNi.sub.5 and other AB.sub.5 type materials and AB.sub.5+x materials, where x is from about -2.5 to about +2.5, including x=0, and the melt is gas atomized under conditions of melt temperature and atomizing gas pressure to form generally spherical powder particles. The hydrogen storage powder exhibits improved chemcial homogeneity as a result of rapid solidfication from the melt and small particle size that is more resistant to microcracking during hydrogen absorption/desorption cycling. A hydrogen storage component, such as an electrode for a battery or electrochemical fuel cell, made from the gas atomized hydrogen storage material is resistant to hydrogen degradation upon hydrogen absorption/desorption that occurs for example, during charging/discharging of a battery. Such hydrogen storage components can be made by consolidating and optionally sintering the gas atomized hydrogen storage powder or alternately by shaping the gas atomized powder and a suitable binder to a desired configuration in a mold or die.

  7. Microstructure and properties of copper composite containing in situ NbC reinforcement: Effects of milling speed

    International Nuclear Information System (INIS)

    Zuhailawati, Hussain; Salihin, Hassin Mohd; Mahani, Yusoff

    2010-01-01

    This paper presents a study on the effects of milling speed on the properties of in situ copper-based composite produced by mechanical alloying followed by cold pressing and sintering. A powdered mixture of copper, niobium and graphite with the composition of Cu-30%NbC was milled at various speeds (100, 200, 300 and 400 rpm). The NbC phase started to precipitate in the as-milled powder after 30 h milling at 400 rpm and the formation was completed after sintering at 950 o C. Enhancements of NbC phase formation with a reduction in Cu crystallite size were observed with the increase of milling speed. Density, hardness and electrical conductivity of the sintered composite were evaluated. An increase in milling speed resulted in an increase in sintered density and hardness but a reduction of electrical conductivity. The changes in the properties were correlated to the formation of NbC phase and refinement of copper and niobium carbide crystallite size since higher milling speed is associated with higher kinetic energy per hit.

  8. From chelating precursors to La0.05Sr0.95CoO3-y oxide

    International Nuclear Information System (INIS)

    Hong, L.; Guo, F.; Lin, J.

    1999-01-01

    Several La 0.05 Sr 0.95 CoO 3-y (LSCO-95) powders were synthesized by means of a chelated complex-based precursor approach, which involved pyrolysis of chelating precursors and subsequent calcination of the resulting oxides. This paper focuses on the coordination effects of the precursors on the formation of the crystalline phases of the LSCO-95 oxide, showing that when the precursor is composed of EDTA-metal complexes, the perovskite-type oxide LSCO-95, an electronic-ionic mixed conducting ceramic material, can be achieved. In contrast, those LSCO-95 powders obtained initially from the pyrolysis of the precursors containing other coordination ligands possess only the undesirable hexagonal structure

  9. Influences of precursor constitution and processing speed on microstructure and wear behavior during laser clad composite coatings on γ-TiAl intermetallic alloy

    International Nuclear Information System (INIS)

    Liu Xiubo; Yu Rongli

    2009-01-01

    The effects of constitution of precursor mixed powders and scan speed on microstructure and wear properties were designed and investigated during laser clad γ/Cr 7 C 3 /TiC composite coatings on γ-TiAl intermetallic alloy substrates with NiCr-Cr 3 C 2 precursor mixed powders. The results indicate that both the constitution of the precursor mixed powders and the beam scan rate have remarkable influence on microstructure and attendant hardness as well as wear resistance of the formed composite coatings. The wear mechanisms of the original TiAl alloy and laser clad composite coatings were investigated. The composite coating with an optimum compromise between constitution of NiCr-Cr 3 C 2 precursor mixed powders as well as being processed under moderate scan speed exhibits the best wear resistance under dry sliding wear test conditions

  10. Weighing fluidized powder

    International Nuclear Information System (INIS)

    Adomitis, J.T.; Larson, R.I.

    1980-01-01

    Fluidized powder is discharged from a fluidizing vessel into a container. Accurate metering is achieved by opening and closing the valve to discharge the powder in a series of short-duration periods until a predetermined weight is measured by a load cell. The duration of the discharge period may be increased in inverse proportion to the amount of powder in the vessel. Preferably the container is weighed between the discharge periods to prevent fluctuations resulting from dynamic effects. The gas discharged into the container causes the pressures in the vessel and container to equalize thereby decreasing the rate of discharge and increasing the accuracy of metering as the weight reaches the predetermined value. (author)

  11. Chemical Reduction Synthesis of Iron Aluminum Powders

    Science.gov (United States)

    Zurita-Méndez, N. N.; la Torre, G. Carbajal-De; Ballesteros-Almanza, L.; Villagómez-Galindo, M.; Sánchez-Castillo, A.; Espinosa-Medina, M. A.

    In this study, a chemical reduction synthesis method of iron aluminum (FeAl) nano-dimensional intermetallic powders is described. The process has two stages: a salt reduction and solvent evaporation by a heat treatment at 1100°C. The precursors of the synthesis are ferric chloride, aluminum foil chips, a mix of Toluene/THF in a 75/25 volume relationship, and concentrated hydrochloric acid as initiator of the reaction. The reaction time was 20 days, the product obtained was dried at 60 °C for 2 h and calcined at 400, 800, and 1100 °C for 4 h each. To characterize and confirm the obtained synthesis products, X-Ray Diffraction (XRD), and Scanning Electron Microscopy (SEM) techniques were used. The results of morphology and chemical characterization of nano-dimensional powders obtained showed a formation of agglomerated particles of a size range of approximately 150 nm to 1.0 μm. Composition of powders was identified as corundum (Al2O3), iron aluminide (FeAl3), and iron-aluminum oxides (Fe0. 53Al0. 47)2O3 phases. The oxide phases formation were associated with the reaction of atmospheric concentration-free oxygen during synthesis and sintering steps, reducing the concentration of the iron aluminum phase.

  12. Hexagonal ferrite powder synthesis using chemical coprecipitation

    International Nuclear Information System (INIS)

    Hsiang, H.-I; Yao, R.-Q.

    2007-01-01

    The formation mechanism of 3BaO.2CoO.12Fe 2 O 3 (Co 2 Z), 2BaO.2CoO.6Fe 2 O 3 (Co 2 Y) and BaO.6Fe 2 O 3 (BaM) powders were prepared using chemical coprecipitation methods in this study using X-ray diffraction (XRD), thermo-gravimetry (TG), differential thermal analysis (DTA) and Fourier transform infrared spectroscopy (FTIR). It was found that the BaM phase was formed directly through the reaction of the preceding ε-Fe 2 O 3 and amorphous BaCO 3 for BaM precursor. For the Co 2 Y precursor, the intermediate phase, BaM, was obtained through the reaction of the earlier formed BaFe 2 O 4 and α-Fe 2 O 3 . The Co 2 Y phase was obtained through a BaM and BaFe 2 O 4 reaction. However, for the Co 2 Z precursors, the BaM phase was obtained directly from the BaCO 3 and amorphous iron hydroxide reaction, with no α-Fe 2 O 3 and BaFe 2 O 4 formed as intermediates. Co 2 Z phase was obtained through the reaction of the two previous formed BaM and Co 2 Y phases

  13. Baking Powder Wars

    OpenAIRE

    Civitello, Linda

    2017-01-01

    How did a mid-nineteenth century American invention, baking powder, replace yeast as a leavening agent and create a culinary revolution as profound as the use of yeast thousands of years ago?The approach was two-pronged and gendered: business archives, U.S. government records and lawsuits revealed how baking powder was created, marketed, and regulated. Women’s diaries and cookbooks—personal, corporate, community, ethnic—from the eighteenth century to internet blogs showed the use women made o...

  14. Uranium mill tailings stabilization

    International Nuclear Information System (INIS)

    Hartley, J.N.; Koehmstedt, P.L.; Esterl, D.J.; Freeman, H.D.

    1980-02-01

    Uranium mill tailings pose a potential radiation health hazard to the public. Therefore, stabilization or disposal of these tailings in a safe and environmentally sound way is needed to minimize radon exhalation and other environmental hazards. One of the most promising concepts for stabilizing U tailings is the use of asphalt emulsion to contain radon and other hazardous materials within uranium tailings. This approach is being investigated at the Pacific Northwest Laboratory. Results of these studies indicate that a radon flux reduction of greater than 99% can be obtained using either a poured-on/sprayed-on seal (3.0 to 7.0 mm thick) or an admixture seal (2.5 to 12.7 cm thick) containing about 18 wt % residual asphalt. A field test was carried out in June 1979 at the Grand Junction tailings pile in order to demonstrate the sealing process. A reduction in radon flux ranging from 4.5 to greater than 99% (76% average) was achieved using a 15.2-cm (6-in.) admix seal with a sprayed-on top coat. A hydrostatic stabilizer was used to apply the admix. Following compaction, a spray coat seal was applied over the admix as the final step in construction of a radon seal. Overburden was applied to provide a protective soil layer over the seal. Included in part of the overburden was a herbicide to prevent root penetration

  15. Mechanically Induced Graphite-Nanodiamonds-Phase Transformations During High-Energy Ball Milling

    Science.gov (United States)

    El-Eskandarany, M. Sherif

    2017-05-01

    Due to their unusual mechanical, chemical, physical, optical, and biological properties, nearly spherical-like nanodiamonds have received much attention as desirable advanced nanomaterials for use in a wide spectrum of applications. Although, nanodiamonds can be successfully synthesized by several approaches, applications of high temperature and/or high pressure may restrict the real applications of such strategic nanomaterials. Distinct from the current preparation approaches used for nanodiamonds preparation, here we show a new process for preparing ultrafine nanodiamonds (3-5 nm) embedded in a homogeneous amorphous-carbon matrix. Our process started from high-energy ball milling of commercial graphite powders at ambient temperature under normal atmospheric helium gas pressure. The results have demonstrated graphite-single wall carbon nanotubes-amorphous-carbon-nanodiamonds phase transformations carried out through three subsequent stages of ball milling. Based on XRD and RAMAN analyses, the percentage of nanodiamond phase + C60 (crystalline phase) produced by ball milling was approximately 81%, while the amorphous phase amount was 19%. The pressure generated on the powder together the with temperature increase upon the ball-powder-ball collision is responsible for the phase transformations occurring in graphite powders.

  16. Niobium Carbide-Reinforced Al Matrix Composites Produced by High-Energy Ball Milling

    Science.gov (United States)

    Travessa, Dilermando Nagle; Silva, Marina Judice; Cardoso, Kátia Regina

    2017-06-01

    Aluminum and its alloys are key materials for the transportation industry as they contribute to the development of lightweight structures. The dispersion of hard ceramic particles in the Al soft matrix can lead to a substantial strengthening effect, resulting in composite materials exhibiting interesting mechanical properties and inspiring their technological use in sectors like the automotive and aerospace industries. Powder metallurgy techniques are attractive to design metal matrix composites, achieving a homogeneous distribution of the reinforcement into the metal matrix. In this work, pure aluminum has been reinforced with particles of niobium carbide (NbC), an extremely hard and stable refractory ceramic. Its use as a reinforcing phase in metal matrix composites has not been deeply explored. Composite powders produced after different milling times, with 10 and 20 vol pct of NbC were produced by high-energy ball milling and characterized by scanning electron microscopy and by X-ray diffraction to establish a relationship between the milling time and size, morphology, and distribution of the particles in the composite powder. Subsequently, an Al/10 pct NbC composite powder was hot extruded into cylindrical bars. The strength of the obtained composite bars is comparable to the commercial high-strength, aeronautical-grade aluminum alloys.

  17. Synthesis of ultrafine alumina powders using egg white as complexing medium

    International Nuclear Information System (INIS)

    Salem, R.E.P.; Guilherme, K. A.; Chinelatto, A.S.A.; Chinelatto, A.L.

    2011-01-01

    Synthesis of alumina powders through chemical methods has been attracting much attention of researchers in the past few years, due to the ability to produce powders in nanometric scale with high degree of purity. In this work, there were synthesized alumina powders through a chemical route, using egg white as a complexing medium and aluminium nitrate as the source of Al 3+ cations. Egg white contains ovalbumin, a protein which acts effectively on the isolation of aluminium cations during the mixing process, enabling the formation of ultrafine alumina powders in a relatively economic and environmentally friendly way. The powders obtained by calcinations of the precursor resin were characterized by X-ray diffraction, specific surface area measurements, infrared spectroscopy and scanning electron microscopy. It was observed that the egg white, present at the reaction medium, allowed obtaining transition alumina powders, with high degree of purity. (author)

  18. Scaling up the production capacity of U-Mo powder by HMD process

    International Nuclear Information System (INIS)

    Pasqualini, E.E.; Lopez, M.; Helzel Garcia, L.J.; Echenique, P.; Adelfang, P.

    2002-01-01

    The recent discovery that uranium alloys in metastable gamma phase can be hydrided at low temperatures and pressures have allowed developing the method of commuting bulk materials by milling the hydride to desired size and then dehydriding the powder. This process is called HMD (hydriding-milling-dehydriding) and needs an initial step of hydrogen incorporation to allow the alloy to be hydrided. This four step process has been conveniently set up for the production of U-7Mo powder for its use in nuclear fuels. Low equipment investment and low man power are needed for this achievement. The process is being analyzed in its scaling up for one kilogram batches and a 50 kilogram per year production capacity of U-Mo powder. (author)

  19. Fabrication of powder from ductile uranium alloys for use as nuclear dispersion

    International Nuclear Information System (INIS)

    Durazzo, M.; Leal Neto, R.M.; Rocha, C.J.; Urano de Carvalho, E.; Riella, H.G.

    2014-01-01

    This work forms part of the studies presently ongoing at IPEN investigating the feasibility of powdering ductile U-10wt%Mo alloy by hydriding-milling-de-hydriding of the gamma phase (HMD). Hydriding was conducted at room temperature in a Sievert apparatus following heat treatment activation. Hydrided pieces were fragile enough to be hand milled to the desired particle size range. Hydrogen was removed by heating the samples under high vacuum. X-ray diffraction analysis of the hydrided material showed an amorphous-like pattern that is completely reversed following de-hydriding. The hydrogen content of the hydrided samples corresponds to a trihydride, i.e. (U,Mo)H 3 . SEM analysis of HMD powder particles revealed equi-axial powder particles together with some plate-like particles. A hypothesis for the amorphous hydride phase formation is suggested. (authors)

  20. Characterization of ceramic powder compacts

    International Nuclear Information System (INIS)

    Yanai, K.; Ishimoto, S.; Kubo, T.; Ito, K.; Ishikawa, T.; Hayashi, H.

    1995-01-01

    UO 2 and Al 2 O 3 powder packing structures in cylindrical powder compacts are observed by scanning electron microscopy using polished cross sections of compacts fixed by low viscosity epoxy resin. Hard aggregates which are not destroyed during powder compaction are observed in some of the UO 2 powder compacts. A technique to measure local density in powder compacts is developed based on counting characteristic X-ray intensity by energy dispersive X-ray analysis (EDX). The local density of the corner portion of the powder compact fabricated by double-acting dry press is higher than that of the inner portion. ((orig.))

  1. ENTIRELY AQUEOUS SOLUTION-GEL ROUTE FOR THE PREPARATION OF ZIRCONIUM CARBIDE, HAFNIUM CARBIDE AND THEIR TERNARY CARBIDE POWDERS

    Directory of Open Access Journals (Sweden)

    Zhang Changrui

    2016-07-01

    Full Text Available An entirely aqueous solution-gel route has been developed for the synthesis of zirconium carbide, hafnium carbide and their ternary carbide powders. Zirconium oxychloride (ZrOCl₂.8H₂O, malic acid (MA and ethylene glycol (EG were dissolved in water to form the aqueous zirconium carbide precursor. Afterwards, this aqueous precursor was gelled and transformed into zirconium carbide at a relatively low temperature (1200 °C for achieving an intimate mixing of the intermediate products. Hafnium and the ternary carbide powders were also synthesized via the same aqueous route. All the zirconium, hafnium and ternary carbide powders exhibited a particle size of ∼100 nm.

  2. Evolution of Microstructure and Mechanical Properties of Oxide Dispersion Strengthened Steels Made from Water-Atomized Ferritic Powder

    Science.gov (United States)

    Arkhurst, Barton Mensah; Kim, Jeoung Han

    2018-05-01

    Nano-structured oxide dispersion strengthened (ODS) steels produced from a 410L stainless steel powder prepared by water-atomization was studied. The influences of Ti content and milling time on the microstructure and the mechanical properties were analysed. It was found that the ODS steels made from the Si bearing 410L powder contained Y-Ti-O, Y-Ti-Si-O, Y-Si-O, and TiO2 oxides. Most nanoparticles produced after 80 h of milling were aggregated nanoparticles; however, after 160 h of milling, most aggregated nanoparticles dissociated into smaller individual nanoparticles. Perfect mixing of Y and Ti was not achieved even after the longer milling time of 160 h; instead, the longer hours of milling rather resulted in Si incorporation into the Y-Ti-O rich nanoparticles and a change in the matrix morphology from an equiaxed microstructure to a tempered martensite-like microstructure. The overall micro-hardness of the ODS steel increased with the increase of milling time. After 80 and 160 h, the microhardnesses were over 400 HV, which primarily resulted from the finer dispersed nanoparticles and in part to the formation of martensitic phases. Tensile strength of the 410L ODS steels was comparable with that of ODS steel produced from gas-atomized powder.

  3. Magnetically responsive enzyme powders

    Czech Academy of Sciences Publication Activity Database

    Pospišková, K.; Šafařík, Ivo

    2015-01-01

    Roč. 380, APR 2015 (2015), s. 197-200 ISSN 0304-8853 R&D Projects: GA MŠk(CZ) LD13021 Institutional support: RVO:67179843 Keywords : enzyme powders * cross-linking * magnetic modification * magnetic separation * magnetic iron oxides particles * microwave-assisted synthesis Subject RIV: CE - Biochemistry Impact factor: 2.357, year: 2015

  4. Powder neutron diffractometers

    International Nuclear Information System (INIS)

    Adib, M.

    2002-01-01

    Basic properties and applications of powder neutron Diffractometers are described for optimum use of the continuous neutron beams. These instruments are equipped with position sensitive detectors, neutron guide tubes, and both high intensity and high resolution modes of operation are possible .The principles of both direct and Fourier reverse time-of-flight neutron Diffractometers are also given

  5. Low Temperature Powder Coating

    Science.gov (United States)

    2011-02-09

    of volatile organic compounds (VOCs) and hazardous air pollutants (HAPs) • Legacy primers contain hexavalent chrome • Conventional powder coatings...coatings both in laboratory and field service evaluations • LTCPC allows environmental cost reductions through VOC/HAP elimination and hexavalent ... chrome reduction. • The LTCPC process greatly shortens the coating operation (LTCPC cures much more rapidly then conventional wet coatings) resulting in

  6. Laser cladding with powder

    NARCIS (Netherlands)

    Schneider, M.F.; Schneider, Marcel Fredrik

    1998-01-01

    This thesis is directed to laser cladding with powder and a CO2 laser as heat source. The laser beam intensity profile turned out to be an important pa6 Summary rameter in laser cladding. A numerical model was developed that allows the prediction of the surface temperature distribution that is

  7. Dry sliding tribological behavior and mechanical properties of Al2024–5 wt.%B4C nanocomposite produced by mechanical milling and hot extrusion

    International Nuclear Information System (INIS)

    Abdollahi, Alireza; Alizadeh, Ali; Baharvandi, Hamid Reza

    2014-01-01

    Highlights: • Nanostructured Al2024 and Al2024–B 4 C nanocomposite prepared via mechanical milling. • The milled powders formed by hot pressing and then exposed to hot extrusion. • Tribological behavior and mechanical properties of samples were investigated. • Al2024–B 4 C nanocomposite showed a better wear resistance and mechanical properties. - Abstract: In this paper, tribological behavior and mechanical properties of nanostructured Al2024 alloy produced by mechanical milling and hot extrusion were investigated before and after adding B 4 C particles. Mechanical milling was used to synthesize the nanostructured Al2024 in attrition mill under argon atmosphere up to 50 h. A similar process was used to produce Al2024–5 wt.%B 4 C composite powder. The milled powders were formed by hot pressing and then were exposed to hot extrusion in 750 °C with extrusion ratio of 10:1. To study the microstructure of milled powders and hot extruded samples, optical microscopy, transmission electron microscopy and scanning electron microscopy (SEM) equipped with an energy dispersive X-ray spectrometer (EDS) were used. The mechanical properties of samples were also compared together using tension, compression and hardness tests. The wear properties of samples were studied using pin-on-disk apparatus under a 20 N load. The results show that mechanical milling decreases the size of aluminum matrix grains to less than 100 nm. The results of mechanical and wear tests also indicate that mechanical milling and adding B 4 C particles increase strength, hardness and wear resistance of Al2024 and decrease its ductility remarkably

  8. Effect of milling parameters on sinterability, mechanical and electrical properties of Cu-4 wt.% ZrO{sub 2} nanocomposite

    Energy Technology Data Exchange (ETDEWEB)

    Taha, Mohammed A., E-mail: mtahanrc@gmail.com [Solid-State Physics Department, National Research Centre, El-Buhooth St., 12622, Dokki, Cairo (Egypt); Nassar, Amira H. [Solid-State Physics Department, National Research Centre, El-Buhooth St., 12622, Dokki, Cairo (Egypt); Zawrah, M.F. [Ceramics Department, National Research Centre, El-Buhooth St., 12622, Dokki, Cairo (Egypt)

    2016-09-15

    Mechanical alloying was used to produce Cu matrix nanocomposite reinforced by 4 wt.% ZrO{sub 2} nanoparticles with different milling time up to 16 h and ball-to-powder ratios (BPRs) up to 40:1. The milled nanocomposite powders were investigated by X-ray diffraction (XRD) technique and transmission electron microscopy (TEM). To study the sinterability, the milled powders were cold pressed and sintered at 800 °C for 1 h in argon atmosphere. In order to investigate the relative density and microstructures of the sintered nanocomposites, scanning electron microscopy (SEM) as well as energy dispersive spectrometer (EDS) were employed. The electrical and mechanical properties of the sintered nanocomposites were also examined. The results revealed that a uniform distribution of ZrO{sub 2} reinforcement in Cu matrix was successfully obtained and the agglomeration, crystal and particle sizes were decreased after either milling times and/or BPRs. The results also pointed out that the relative density, microhardness, compressive strength and electrical conductivity of the sintered nanocomposite samples were increased with the increasing of milling time and/or BPRs while apparent porosity was decreased. The maximum values of microhardness, compressive strength and electrical conductivity were 872 MPa, 304 MPa and 45.9% IACS, respectively for the milled sample for 16 h and BRP 40:1. - Highlights: • Cu-4 wt.% ZrO{sub 2} nanoparticles with different parameter by mechanical alloying. • The increased milling times and/or BPRs led to a decrease in the particle size. • Microhardness is increased with increasing ball-to-powder weight ratios. • Compressive strength is increased with increasing milling time. • Electrical conductivity of the samples was increasing with increase milling time.

  9. Titanium Metal Powder Production by the Plasma Quench Process

    Energy Technology Data Exchange (ETDEWEB)

    R. A. Cordes; A. Donaldson

    2000-09-01

    The goals of this project included the scale-up of the titanium hydride production process to a production rate of 50 kg/hr at a purity level of 99+%. This goal was to be achieved by incrementally increasing the production capability of a series of reactor systems. This methodic approach was designed to allow Idaho Titanium Technologies to systematically address the engineering issues associated with plasma system performance, and powder collection system design and performance. With quality powder available, actual fabrication with the titanium hydride was to be pursued. Finally, with a successful titanium production system in place, the production of titanium aluminide was to be pursued by the simultaneously injection of titanium and aluminum precursors into the reactor system. Some significant accomplishments of the project are: A unique and revolutionary torch/reactor capable of withstanding temperatures up to 5000 C with high thermal efficiency has been operated. The dissociation of titanium tetrachloride into titanium powder and HC1 has been demonstrated, and a one-megawatt reactor potentially capable of producing 100 pounds per hour has been built, but not yet operated at the powder level. The removal of residual subchlorides and adsorbed HC1 and the sintering of powder to form solid bodies have been demonstrated. The production system has been operated at production rates up to 40 pounds per hour. Subsequent to the end of the project, Idaho Titanium Technologies demonstrated that titanium hydride powder can indeed be sintered into solid titanium metal at 1500 C without sintering aids.

  10. Fabrication of metal matrix composites by powder metallurgy: A review

    Science.gov (United States)

    Manohar, Guttikonda; Dey, Abhijit; Pandey, K. M.; Maity, S. R.

    2018-04-01

    Now a day's metal matrix components are used in may industries and it finds the applications in many fields so, to make it as better performable materials. So, the need to increase the mechanical properties of the composites is there. As seen from previous studies major problem faced by the MMC's are wetting, interface bonding between reinforcement and matrix material while they are prepared by conventional methods like stir casting, squeeze casting and other techniques which uses liquid molten metals. So many researchers adopt PM to eliminate these defects and to increase the mechanical properties of the composites. Powder metallurgy is one of the better ways to prepare composites and Nano composites. And the major problem faced by the conventional methods are uniform distribution of the reinforcement particles in the matrix alloy, many researchers tried to homogeneously dispersion of reinforcements in matrix but they find it difficult through conventional methods, among all they find ultrasonic dispersion is efficient. This review article is mainly concentrated on importance of powder metallurgy in homogeneous distribution of reinforcement in matrix by ball milling or mechanical milling and how powder metallurgy improves the mechanical properties of the composites.

  11. FePt magnetic particles prepared by surfactant-assisted ball milling

    Energy Technology Data Exchange (ETDEWEB)

    Velasco, V., E-mail: vvjimeno@fis.ucm.es [Instituto de Magnetismo Aplicado, UCM-ADIF-CSIC, P.O. Box 155, Las Rozas 28230 (Spain); Departamento de Física de Materiales, Universidad Complutense de Madrid, Madrid 28040 (Spain); Hernando, A.; Crespo, P. [Instituto de Magnetismo Aplicado, UCM-ADIF-CSIC, P.O. Box 155, Las Rozas 28230 (Spain); Departamento de Física de Materiales, Universidad Complutense de Madrid, Madrid 28040 (Spain)

    2013-10-15

    High-energy ball milling of Fe and Pt elemental powders has been carried out under dry and wet (in presence of solvent and surfactants) conditions. Dry milling leads to the formation of the disordered FCC-FePt alloy whereas by the wet milling procedure the main process is the decrease of Fe and Pt particle size, although some dissolution of Pt into Fe grains cannot be ruled out, and no hint of the formation of the FCC-FePt phase is observed even to milling times up to 20 h, as X-ray diffraction, electron microscopy and Mössbauer spectroscopy indicates. The as-milled particles were annealed at 600 °C for 2 h under Ar atmosphere. It is noticed that the disordered fcc-FePt phase observed in particles milled under dry conditions transform to ordered fct phase characterized by a hard magnetic behavior with a coercive field up to 10,000 Oe. However, those particles milled in the surfactant/solvent medium exhibit a soft magnetic behavior with a coercive field of 600 Oe. These results indicate that wet high-energy ball milling is not an adequate technique for obtaining single-phase FePt particles. - Highlights: • FePt particles have been obtained by high-energy ball milling. • In the presence of surfactants and solvents, almost no alloying process takes place. • After annealing, the coercive field of the FePt alloy particles increases from 150 Oe to 10,000 Oe.

  12. Preparation of glibenclamide nanocrystals by a simple laboratory scale ultra cryo-milling

    Energy Technology Data Exchange (ETDEWEB)

    Martena, Valentina; Censi, Roberta [University of Camerino, School of Pharmacy (Italy); Hoti, Ela; Malaj, Ledjan [University of Tirana, Department of Pharmacy (Albania); Martino, Piera Di, E-mail: piera.dimartino@unicam.it [University of Camerino, School of Pharmacy (Italy)

    2013-06-15

    The objective of this study is to evaluate the ability to reduce the particle size of glibenclamide (GBC) to the nanometric scale through a very simple and well-known laboratory scale method, the laboratory scale ultra cryo-milling. The effect of milling on GBC crystalline properties and dissolution behaviour was deliberately evaluated in the absence of any surfactants as stabilizers. The milling procedure consisted in adding particles to liquid nitrogen and milling them by hand in a mortar with a pestle for different time intervals (15, 30, 40 min). For comparison, the same milling procedure was also applied without liquid nitrogen. The particle size reduction was evaluated for the coarsest samples (>3 {mu}m) by measuring the particle Ferret's diameter through scanning electron microscopy, while for the smallest one (<3 {mu}m) by dynamic light scattering. A time grinding of 40 min in the presence of liquid nitrogen was revealed highly efficacious to obtain particles of nanodimensions, with a geometric mean particle size of 0.55 {+-} 0.23 {mu}m and more than the 80 % of particles lower than 1,000 nm. Interestingly, non-agglomerated particles were obtained. Differential scanning calorimetry and X-ray powder diffractometry allowed to assess that under mechanical treatment no polymorphic transitions were observed, while a decrease in crystallinity degree occurred depending on the milling procedure (presence or absence of liquid nitrogen) and the milling time (crystallinity decreases at increasing milling time from 15 to 40 min). A comparison of the intrinsic dissolution rate and the dissolution from particles revealed an interesting improvement of particle dissolution particularly for particles milled in the presence of liquid nitrogen due to an increase in particle surface area and concentration gradient, according to the Noyes-Whitney equation.

  13. Microstructural and electrical changes in nickel manganite powder induced by mechanical activation

    International Nuclear Information System (INIS)

    Savic, S.M.; Mancic, L.; Vojisavljevic, K.; Stojanovic, G.; Brankovic, Z.; Aleksic, O.S.; Brankovic, G.

    2011-01-01

    Highlights: → The influence of mechanical activation on microstructure evolution in the nickel manganite powder was investigated as well as electrical properties of the sintered samples. → Structural refinement obtained by Topas-Academic software based on Rietveld analysis showed that the milling process remarkably changed the powder morphology and microstructure. → SEM studies of sintered samples also revealed the strong influence of milling time on ceramics density (increases with milling time). → The electrical properties of ceramic samples are clearly conditioned by terms of synthesis, in our case the time of mechanical activation. → The highest density and higher values of dielectric constant were achieved at the sample activated for 45 min. -- Abstract: Nickel manganite powder synthesized by calcination of a stoichiometric mixture of manganese and nickel oxide was additionally mechanically activated in a high energy planetary ball mill for 5-60 min in order to obtain a pure NiMn 2 O 4 phase. The as-prepared powders were uniaxially pressed into disc shape pellets and then sintered for 60 min at 1200 o C. Changes in the particle morphology induced by mechanical activation were monitored using scanning electron microscopy, while changes in powder structural characteristics were followed using X-ray powder diffraction. The ac impedance spectroscopy was performed on sintered nickel manganite samples at 25 o C, 50 o C and 80 o C. It was shown that mechanical activation intensifies transport processes causing a decrease in the average crystallites size, while longer activation times can lead to the formation of aggregates, defects and increase of lattice microstrains. The observed changes in microstructures were correlated with measured electrical properties in order to define optimal processing conditions.

  14. Microstructural and electrical changes in nickel manganite powder induced by mechanical activation

    Energy Technology Data Exchange (ETDEWEB)

    Savic, S.M., E-mail: slavicas@cms.bg.ac.rs [Institute for Multidisciplinary Research-University of Belgrade, Kneza Viseslava 1a, 11030 Belgrade (Serbia); Mancic, L. [Institute of Technical Sciences SASA, Knez Mihailova 35/IV, 11000 Belgrade (Serbia); Vojisavljevic, K. [Institute for Multidisciplinary Research-University of Belgrade, Kneza Viseslava 1a, 11030 Belgrade (Serbia); Stojanovic, G. [Faculty of Technical Sciences University of Novi Sad, Trg Dositeja Obradovica 6, 21000 Novi Sad (Serbia); Brankovic, Z.; Aleksic, O.S.; Brankovic, G. [Institute for Multidisciplinary Research-University of Belgrade, Kneza Viseslava 1a, 11030 Belgrade (Serbia)

    2011-07-15

    Highlights: {yields} The influence of mechanical activation on microstructure evolution in the nickel manganite powder was investigated as well as electrical properties of the sintered samples. {yields} Structural refinement obtained by Topas-Academic software based on Rietveld analysis showed that the milling process remarkably changed the powder morphology and microstructure. {yields} SEM studies of sintered samples also revealed the strong influence of milling time on ceramics density (increases with milling time). {yields} The electrical properties of ceramic samples are clearly conditioned by terms of synthesis, in our case the time of mechanical activation. {yields} The highest density and higher values of dielectric constant were achieved at the sample activated for 45 min. -- Abstract: Nickel manganite powder synthesized by calcination of a stoichiometric mixture of manganese and nickel oxide was additionally mechanically activated in a high energy planetary ball mill for 5-60 min in order to obtain a pure NiMn{sub 2}O{sub 4} phase. The as-prepared powders were uniaxially pressed into disc shape pellets and then sintered for 60 min at 1200 {sup o}C. Changes in the particle morphology induced by mechanical activation were monitored using scanning electron microscopy, while changes in powder structural characteristics were followed using X-ray powder diffraction. The ac impedance spectroscopy was performed on sintered nickel manganite samples at 25 {sup o}C, 50 {sup o}C and 80 {sup o}C. It was shown that mechanical activation intensifies transport processes causing a decrease in the average crystallites size, while longer activation times can lead to the formation of aggregates, defects and increase of lattice microstrains. The observed changes in microstructures were correlated with measured electrical properties in order to define optimal processing conditions.

  15. Structure and soft magnetic properties of the bulk samples prepared by compaction of the mixtures of Co-based and Fe-based powders

    International Nuclear Information System (INIS)

    Fuezer, J.; Bednarcik, J.; Kollar, P.; Roth, S.

    2007-01-01

    Ball milling of CoFeZrB ribbons and subsequent compaction of the resulting powders were used to prepare bulk amorphous samples. Further, two sets of powder samples were prepared by cryomilling of FeCuNbMoSiB alloy in amorphous and nanocrystalline state. Amorphous and nanocrystalline FeCuNbMoSiB powders were blended with CoFeZrB powder at different concentrations. Such powder mixtures were consolidated and several bulk nanocomposites have been synthesized. An addition of nanocrystalline or amorphous FeCuNbMoSiB powder to amorphous CoFeZrB powder caused a decrease of the magnetostriction of the resultant bulk samples, while the coercivity shows an opposite behavior. Our results show that the powder consolidation by hot pressing is an alternative method for the preparation of bulk metallic glasses, which are difficult to prepare by casting methods

  16. EFFECT OF MILLING SOFTNESS ON BASIC TECHNOLOGICAL PARAMETERS OF WORT

    Directory of Open Access Journals (Sweden)

    Ján Mareček

    2011-02-01

    Full Text Available Crushing the malted grain in the process of milling enables extractive substances of malt to become available for water which accelerates dissolving and other chemical and physical processes during the time of mashing. The aim of this work was at the basis of performed analyses to evaluate to what extent the grist composition with regard to different proportion of meal fraction affects the amount of extract and other technological parameters of malt. Analyzed malt was made from four varieties of malting barley as are Nitran, Ebson, Malz and Xanadu coming from the harvest year 2009. Composition of malt grist in great extent influenced the entire process of mashing, lautering and the amount of extract. The highest values of extract were measured by all varieties at the variant III. with the highest content (50% of the softest fraction meal + powder meal. The difference between variant I. with 10% content of the softest fraction and variant III. with 50% content, was already 3%. The most significant increase of this parameter was found out by varieties Ebson and Malz. Mashing and lautering parameters have not been significantly influenced by the milling variants. More significant differences were found out with regard to wort turbidity. Only variety Malz showed out the turbidity up to 4 EBC units, measured by turbidity meter under the angle 90°. The highest turbidity was measured by variant I. with the lowest proportion of the fraction meal + powder meal.doi:10.5219/111

  17. Method to blend separator powders

    Science.gov (United States)

    Guidotti, Ronald A.; Andazola, Arthur H.; Reinhardt, Frederick W.

    2007-12-04

    A method for making a blended powder mixture, whereby two or more powders are mixed in a container with a liquid selected from nitrogen or short-chain alcohols, where at least one of the powders has an angle of repose greater than approximately 50 degrees. The method is useful in preparing blended powders of Li halides and MgO for use in the preparation of thermal battery separators.

  18. Einstein-Yang-Mills from pure Yang-Mills amplitudes

    Energy Technology Data Exchange (ETDEWEB)

    Nandan, Dhritiman; Plefka, Jan [Institut für Physik and IRIS Adlershof, Humboldt-Universität zu Berlin,Zum Großen Windkanal 6, D-12489 Berlin (Germany); Schlotterer, Oliver [Max-Planck-Institut für Gravitationsphysik, Albert-Einstein-Institut,Am Mühlenberg 1, D-14476 Potsdam (Germany); Wen, Congkao [I.N.F.N. Sezione di Roma Tor Vergata,Via della Ricerca Scientifica, 00133 Roma (Italy)

    2016-10-14

    We present new relations for scattering amplitudes of color ordered gluons and gravitons in Einstein-Yang-Mills theory. Tree-level amplitudes of arbitrary multiplicities and polarizations involving up to three gravitons and up to two color traces are reduced to partial amplitudes of pure Yang-Mills theory. In fact, the double-trace identities apply to Einstein-Yang-Mills extended by a dilaton and a B-field. Our results generalize recent work of Stieberger and Taylor for the single graviton case with a single color trace. As the derivation is made in the dimension-agnostic Cachazo-He-Yuan formalism, our results are valid for external bosons in any number of spacetime dimensions. Moreover, they generalize to the superamplitudes in theories with 16 supercharges.

  19. High anisotropic NdFeB submicro/nanoflakes prepared by surfactant-assisted ball milling at low temperature

    Science.gov (United States)

    An, Xiaoxin; Jin, Kunpeng; Abbas, Nadeem; Fang, Qiuli; Wang, Fang; Du, Juan; Xia, Weixing; Yan, Aru; Liu, J. Ping; Zhang, Jian

    2017-11-01

    Hard magnetic NdFeB submicro/nanoflakes were successfully prepared by surfactant-assisted ball milling at low temperature (SABMLT) by specially using 2-methyl pentane and trioctylamine (TOA) as solvent and surfactant, respectively. Influences of the amount of TOA and milling temperature on the crystal structure, morphology and magnetic performances of the as-prepared NdFeB powders were investigated systematically. There is significant difference on morphology between the NdFeB powders milled at room and low temperature. The NdFeB powders with flaky morphology could be obtained even with a small amount of TOA by SABMLT, which could not be achieved by surfactant-assisted ball milling at room temperature (SABMRT). The better crystallinity, better grain alignment, higher coercivity, larger saturation magnetization and remanence ratio were achieved in the samples prepared by SABMLT. Furthermore, the final NdFeB powders prepared by SABMLT possessed a lower amount of residual TOA than those prepared by SABMRT. It was demonstrated that SABMLT is a promising way to fabricate rare-earth-transition metal nanoflakes with high anisotropy for permanent magnetic materials. The effective method of preparing NdFeB flakes by lowering temperature will be also useful to fabricate flakes of other functional materials.

  20. Toward a theory of precursors

    International Nuclear Information System (INIS)

    Freivogel, Ben; Giddings, Steven B.; Lippert, Matthew

    2002-01-01

    To better understand the possible breakdown of locality in quantum gravitational systems, we pursue the identity of precursors in the context of the anti-de Sitter/conformal field theory correspondence. Holography implies a breakdown of standard bulk locality which we expect to occur only at extremely high energy. We consider precursors that encode bulk information causally disconnected from the boundary and whose measurement involves nonlocal bulk processes. We construct a toy model of holography which encapsulates the expected properties of precursors and compare it with previous such discussions. If these precursors can be identified in the gauge theory, they are almost certainly Wilson loops, perhaps with decorations, but the relevant information is encoded in the high-energy sector of the theory and should not be observable by low energy measurements. This would be in accord with the locality bound, which serves as a criterion for situations where breakdown of bulk locality is expected

  1. Moessbauer analysis of high-energy mechanical-milled sand fraction of a magnetic soil developing on basalt

    Energy Technology Data Exchange (ETDEWEB)

    Borges, Jose Flavio Marcelino; Hneda, Marlon Luiz; Brinatti, Andre Mauricio [State University of Ponta Grossa, Department of Physics (Brazil); Cunha, Joao Batista Marimon da [Federal University of Rio Grande do Sul, Institute of Physics (Brazil); Rosa, Jadir Aparecido [Polo Regional de Ponta Grossa, Agronomy Institute of Parana (Brazil); Fabris, Jose Domingos, E-mail: jdfabris@ufmg.br [Federal University of Jequitinhonha and Mucuri Valleys (UFVJM) (Brazil)

    2011-11-15

    A sample of the coarse sand fraction from the soil material of the A-horizon (0-0.2 m from the soil surface) of a dusky red magnetic Oxisol was submitted to high-energy mechanical milling for different times. This assay aimed mainly at (a) monitoring the individualization of strongly aggregated mineral particles, and (b) measuring the effect of the milling pressure on the mineralogy changes of the material. These data are also intended to experimentally subside any physical model describing the mechanical behavior of the superficial soil layer that is subjected to intensive machine management, in agriculture fields. Powder X-ray data reveal that some mineralogical phases, notably gibbsite, disappear soon after the first few hours milling. The 298 K-transmission Moessbauer spectrum for the non-milled sand sample shows a qualitatively typical pattern for the sand fraction of basalt derived soils, with magnetically ordered sextets, assignable mainly to hematite and maghemite, and an intense central (super)paramagnetic Fe{sup 3 + } doublet. For the milled samples, spectra revealed progressive spectral reduction of the magnetic hyperfine structure, with concomitant increase of relative subspectral areas due to (super)paramagnetic phases, as the milling time increased. This result is consistent with the reduction of measured saturation magnetization, from 4.96(8) J T{sup - 1} kg{sup - 1}, for the non-milled sample, to 3.26(7) J T{sup - 1} kg{sup - 1}, for the sample milled for 8 hours.

  2. Plasma technology for powder particles

    Energy Technology Data Exchange (ETDEWEB)

    Kranz, E. (Technische Hochschule, Ilmenau (German Democratic Republic))

    1983-03-01

    A survey is given of principles and applications of plasma spraying and of powder transformation and generation in plasma considering spheroidization, grain size transformation, powder particle formation, powder reduction, and melting within the power range of 10/sup 3/ to 10/sup 7/ W. The products are applied in many industrial fields such as nuclear engineering, hard metal production, metallurgy, catalysis, and semiconductor techniques.

  3. Current uranium mill licensing issues

    International Nuclear Information System (INIS)

    Scarano, R.A.

    1977-01-01

    The problems encountered to insure environmentally safe mining and milling of uranium ores are reviewed. Emphasis is placed on the management of tailings resulting from milling operations. It is pointed out that although the concentration of radioactivity in the tailings is relatively low, control measures are necessary because of the large quantities involved and because of the long half-life of the parent radionuclides present. The major concerns with mill tailings are radon release to the atmosphere and isolation of the tailings from the human environment. Since it is anticipated that the amount of tailings created by the year 2000 will be more than an order of magnitude greater than the quantities that have been generated during the past 30 years, it is recommended that all mill tailings storage areas be located remote from public contact and in areas such that disruption and dispersion by natural forces and seepage of toxic materials into ground water systems are reduced to the maximum extent achievable. Technical issues that receive attention during the NRC licensing process for uranium mills and the preparation of environmental impact statements are discussed briefly

  4. Colorado's prospectus on uranium milling

    International Nuclear Information System (INIS)

    Hazle, A.J.; Franz, G.A.; Gamewell, R.

    1982-01-01

    The first part of this paper will discuss Colorado's control of uranium mill tailings under Titles I and II of the Uranium Mill Tailings Radiation Control Act of 1978. Colorado has a legacy of nine inactive mill sites requiring reclamation under Title I, and two presently active plus a number of new mill proposals which must be regulated in accordance with Title II. Past failures in siting and control on the part of federal jurisdictions have left the state with a heavy legacy requiring extensive effort to address impacts to the state's environment and population. The second part of this paper will discuss the remedial action programme authorized under Public Law 92-314 for Mesa Country, where lack of federal control led to the dispersal of several hundred thousand tons of uranium mill tailings on thousands of properties, including hundreds of homes, schools and other structures. Successful completion of the State efforts under both programmes will depend on a high level of funding and on the maintenance of adequate regulatory standards. (author)

  5. Synthesis of Uranium nitride powders using metal uranium powders

    International Nuclear Information System (INIS)

    Yang, Jae Ho; Kim, Dong Joo; Oh, Jang Soo; Rhee, Young Woo; Kim, Jong Hun; Kim, Keon Sik

    2012-01-01

    Uranium nitride (UN) is a potential fuel material for advanced nuclear reactors because of their high fuel density, high thermal conductivity, high melting temperature, and considerable breeding capability in LWRs. Uranium nitride powders can be fabricated by a carbothermic reduction of the oxide powders, or the nitriding of metal uranium. The carbothermic reduction has an advantage in the production of fine powders. However it has many drawbacks such as an inevitable engagement of impurities, process burden, and difficulties in reusing of expensive N 15 gas. Manufacturing concerns issued in the carbothermic reduction process can be solved by changing the starting materials from oxide powder to metals. However, in nitriding process of metal, it is difficult to obtain fine nitride powders because metal uranium is usually fabricated in the form of bulk ingots. In this study, a simple reaction method was tested to fabricate uranium nitride powders directly from uranium metal powders. We fabricated uranium metal spherical powder and flake using a centrifugal atomization method. The nitride powders were obtained by thermal treating those metal particles under nitrogen containing gas. We investigated the phase and morphology evolutions of powders during the nitriding process. A phase analysis of nitride powders was also a part of the present work

  6. Investigation of planetary milling for nano-silicon carbide reinforced aluminium metal matrix composites

    Energy Technology Data Exchange (ETDEWEB)

    Kollo, Lauri, E-mail: lauri.kollo@staff.ttu.e [Laboratory of Advanced Materials Processing, EMPA, Feuerwerkerstrasse 39, 3602 Thun (Switzerland); Department of Materials Engineering, Tallinn University of Technology, Ehitajate tee 5, 19086 Tallinn (Estonia); Leparoux, Marc; Bradbury, Christopher R.; Jaeggi, Christian [Laboratory of Advanced Materials Processing, EMPA, Feuerwerkerstrasse 39, 3602 Thun (Switzerland); Carreno-Morelli, Efrain; Rodriguez-Arbaizar, Mikel [University of Applied Sciences of Western Switzerland, Design and Materials Unit, 1950 Sion (Switzerland)

    2010-01-21

    High-energy planetary milling was used for mixing aluminium powders with 1 vol.% of silicon carbide (SiC) nanoparticles. A number of milling parameters were modified for constituting the relationship between the energy input from the balls and the hardness of the bulk nanocomposite materials. It was shown that mixing characteristics and reaction kinetics with stearic acid as process control agent can be estimated by normalised input energy from the milling bodies. For this, the additional parameter characterising the vial filling was determined experimentally. Depending on the ball size, a local minimum in filling parameter was found, laying at 25 or 42% filling of the vial volume for the balls with diameter of 10 and 20 mm, respectively. These regions should be avoided to achieve the highest milling efficiency.After a hot compaction, fourfold difference of hardness for different milling conditions was detected. Therewith the hardness of the Al-1 vol.% nanoSiC composite could be increased from 47 HV{sub 0.5} of pure aluminium to 163 HV{sub 0.5} when milling at the highest input energy levels.

  7. Matrix model of the grinding process of cement clinker in the ball mill

    Science.gov (United States)

    Sharapov, Rashid R.

    2018-02-01

    In the article attention is paid to improving the efficiency of production of fine powders, in particular Portland cement clinker. The questions of Portland cement clinker grinding in closed circuit ball mills. Noted that the main task of modeling the grinding process is predicting the granulometric composition of the finished product taking into account constructive and technological parameters used ball mill and separator. It is shown that the most complete and informative characterization of the grinding process in a ball mill is a grinding matrix taking into account the transformation of grain composition inside the mill drum. Shows how the relative mass fraction of the particles of crushed material, get to corresponding fraction. Noted, that the actual task of reconstruction of the matrix of grinding on the experimental data obtained in the real operating installations. On the basis of experimental data obtained on industrial installations, using matrix method to determine the kinetics of the grinding process in closed circuit ball mills. The calculation method of the conversion of the grain composition of the crushed material along the mill drum developed. Taking into account the proposed approach can be optimized processing methods to improve the manufacturing process of Portland cement clinker.

  8. Polycrystalline Nd2Fe14B/α-Fe nanocomposite flakes with a sub-micro/nanometre thickness prepared by surfactant-assisted high-energy ball milling

    International Nuclear Information System (INIS)

    Tang, Xin; Chen, Xi; Chen, Renjie; Yan, Aru

    2015-01-01

    Highlights: • Nd 2 Fe 14 B/α-Fe flakes are formed by peeling along preferential planes. • (0 0 l) planes are found to be preferential cleavage planes. • Magnetic properties degrade with increasing ball milling time. • Anisotropic nanocomposite magnets are fabricated. - Abstract: A surfactant-assisted high-energy ball milling technique was employed to synthesize Nd 2 Fe 14 B/α-Fe nanoparticles and nanoflakes from melt-spun nanocrystalline powders. The microstructure evolution in ball milling process was investigated. In the beginning stage (0–4 h) of ball milling, raw powders were crushed into micrometre-sized particles. While flakes were mainly formed by reducing thickness of particles via peeling layer by layer along preferential planes in the late stage (8–16 h). The selected area electron diffraction and high-resolution transmission electron microscopy images show that preferential cleavage planes are basal planes. With ball milling proceeding, more and more defects were induced by ball milling. As a result, the coercivity and remanence decreased to 1.6 kOe and 3.2 kGs, respectively. After 16 h ball milling, the exchange decoupling occurred due to severe amorphorization. A weakly-textured nanocomposite magnet was fabricated after 12 h ball milling and the anisotropy in magnetic properties can be further improved by employing settling down process to select particle size and aligning particles in external field

  9. Effect of temperature, time, and milling process on yield, flavonoid, and total phenolic content of Zingiber officinale water extract

    Science.gov (United States)

    Andriyani, R.; Kosasih, W.; Ningrum, D. R.; Pudjiraharti, S.

    2017-03-01

    Several parameters such as temperature, time of extraction, and size of simplicia play significant role in medicinal herb extraction. This study aimed to investigate the effect of those parameters on yield extract, flavonoid, and total phenolic content in water extract of Zingiber officinale. The temperatures used were 50, 70 and 90°C and the extraction times were 30, 60 and 90 min. Z. officinale in the form of powder and chips were used to study the effect of milling treatment. The correlation among those variables was analysed using ANOVA two-way factors without replication. The result showed that time and temperature did not influence the yield of extract of Powder simplicia. However, time of extraction influenced the extract of simplicia treated without milling process. On the other hand, flavonoid and total phenolic content were not influenced by temperature, time, and milling treatment.

  10. Dispersing powders in liquids

    CERN Document Server

    Nelson, RD

    1988-01-01

    This book provides powder technologists with laboratory procedures for selecting dispersing agents and preparing stable dispersions that can then be used in particle size characterization instruments. Its broader goal is to introduce industrial chemists and engineers to the phenomena, terminology, physical principles, and chemical considerations involved in preparing and handling dispersions on a commercial scale. The book introduces novices to: - industrial problems due to improper degree of dispersion; - the nomenclature used in describing particles; - the basic physica

  11. The yang mills gravity dual

    International Nuclear Information System (INIS)

    Crooks, David E.; Evans, Nick

    2003-01-01

    We describe a ten dimensional supergravity geometry which is dual to a gauge theory that is non-supersymmetric Yang Mills in the infra-red but reverts to N=4 super Yang Mills in the ultra-violet. A brane probe of the geometry shows that the scalar potential of the gauge theory is stable. We discuss the infra-red behaviour of the solution. The geometry describes a Schroedinger equation potential that determines the glueball spectrum of the theory; there is a mass gap and a discrete spectrum. The glueball mass predictions match previous AdS/CFT Correspondence computations in the non-supersymmetric Yang Mills theory, and lattice data, at the 10% level. (author)

  12. Galilean Yang-Mills theory

    International Nuclear Information System (INIS)

    Bagchi, Arjun; Basu, Rudranil; Kakkar, Ashish; Mehra, Aditya

    2016-01-01

    We investigate the symmetry structure of the non-relativistic limit of Yang-Mills theories. Generalising previous results in the Galilean limit of electrodynamics, we discover that for Yang-Mills theories there are a variety of limits inside the Galilean regime. We first explicitly work with the SU(2) theory and then generalise to SU(N) for all N, systematising our notation and analysis. We discover that the whole family of limits lead to different sectors of Galilean Yang-Mills theories and the equations of motion in each sector exhibit hitherto undiscovered infinite dimensional symmetries, viz. infinite Galilean Conformal symmetries in D=4. These provide the first examples of interacting Galilean Conformal Field Theories (GCFTs) in D>2.

  13. Galilean Yang-Mills theory

    Energy Technology Data Exchange (ETDEWEB)

    Bagchi, Arjun [Center for Theoretical Physics, Massachusetts Institute of Technology,77 Massachusetts Avenue, Cambridge, MA 02139 (United States); Basu, Rudranil [Saha Institute of Nuclear Physics,Block AF, Sector 1, Bidhannagar, Kolkata 700068 (India); Kakkar, Ashish [Indian Institute of Science Education and Research,Dr Homi Bhabha Road, Pashan. Pune 411008 (India); Mehra, Aditya [Indian Institute of Science Education and Research,Dr Homi Bhabha Road, Pashan. Pune 411008 (India); Van Swinderen Institute for Particle Physics and Gravity, University of Groningen, Nijenborgh 4, 9747 AG Groningen (Netherlands)

    2016-04-11

    We investigate the symmetry structure of the non-relativistic limit of Yang-Mills theories. Generalising previous results in the Galilean limit of electrodynamics, we discover that for Yang-Mills theories there are a variety of limits inside the Galilean regime. We first explicitly work with the SU(2) theory and then generalise to SU(N) for all N, systematising our notation and analysis. We discover that the whole family of limits lead to different sectors of Galilean Yang-Mills theories and the equations of motion in each sector exhibit hitherto undiscovered infinite dimensional symmetries, viz. infinite Galilean Conformal symmetries in D=4. These provide the first examples of interacting Galilean Conformal Field Theories (GCFTs) in D>2.

  14. Container for nuclear fuel powders

    International Nuclear Information System (INIS)

    Etheredge, B.F.; Larson, R.I.

    1982-01-01

    A critically safe container is disclosed for the storage and rapid discharge of enriched nuclear fuel material in powder form is disclosed. The container has a hollow, slab-shaped container body that has one critically safe dimension. A powder inlet is provided on one side wall of the body adjacent to a corner thereof and a powder discharge port is provided at another corner of the body approximately diagonal the powder inlet. Gas plenum for moving the powder during discharge are located along the side walls of the container adjacent the discharge port

  15. Magnetic interactions in high-energy ball-milled NiZnFe2O4/SiO2 composites

    International Nuclear Information System (INIS)

    Pozo Lopez, G.; Silvetti, S.P.; Urreta, S.E.; Cabanillas, E.D.

    2007-01-01

    Composites Ni 0.5 Zn 0.5 Fe 2 O 4 /SiO 2 are obtained after high-energy ball milling precursor oxides, in stoichiometric proportions, for 200 h at room temperature and further isothermal annealing for 1 h at 1273 K, under air and argon atmosphere, respectively. After 200 h grinding, a complex microstructure develops with small hematite crystals mixed with SiO 2 and remanent NiO and ZnO particles, and very small NiZn ferrite clusters, reaching a mean size of ∼9 nm. The high temperature treatments remove the hematite grains from the powder and promote the growth of NiZn ferrite grains to reach mean sizes nearly ∼20 nm. For treatments in oxidizing atmospheres, the major phases are SiO 2 and NiZn ferrite, while for annealing in Ar a new phase appears, fayalite, which is paramagnetic at room temperature. The M-H loops are all well described by the sum of a ferromagnetic and a superparamagnetic-like contribution. The observed properties are interpreted considering the different magnetic phases obtained, their crystal sizes and their mutual interactions

  16. Preliminary study of sintering of metallic niobium processed for mechanical milling; Estudo preliminar da sinterizacao de niobio metalico processado por moagem de alta energia

    Energy Technology Data Exchange (ETDEWEB)

    Tamura, H.M.; Vurobi Junior, S.; Cintho, O.M., E-mail: lenatamura@interponta.com.b [Universidade Estadual de Ponta Grossa (UEPG), PR (Brazil); Sandim, H.R.Z.; Leite, G.S. [Universidade de Sao Paulo (EEL/USP), Lorena, SP (Brazil). Escola de Engenharia

    2010-07-01

    In present study was preliminary study of mechanical milling influence on preparing of metallic niobium powder for sintering. Sample of metallic niobium in powder passing in sieve no. 635 mesh was processed by mechanical milling in SPEX mill for 8 hours using power grinding of 7:1 and a nitrogen atmosphere. The powder was annealed at different temperatures, 900 deg C, 1000 deg C, 1100 deg C and 1200 deg C for 1 hour in an atmosphere of hydrogen and argon to study their crystallization, which then were formed into blank for analysis of the curves compressibility. These samples were also subjected to x-ray diffraction in that their data were compared between the annealing temperatures. We also evaluate the compressibility curves of niobium samples with and without grinding these samples were subjected to x-ray diffraction and fluorescence. (author)

  17. Ball mill tool for crushing coffee and cocoa beans base on fraction size sieving results

    Science.gov (United States)

    Haryanto, B.; Sirait, M.; Azalea, M.; Alvin; Cahyani, S. E.

    2018-02-01

    Crushing is one of the operation units that aimed to convert the size of solid material to be smoother particle’s size. The operation unit that can be used in this crushing is ball mill. The purpose of this study is to foresee the effect of raw material mass, grinding time, and the number of balls that are used in the ball mill tool related to the amount of raw material of coffee and cocoa beans. Solid material that has become smooth is then sieved with sieve mesh with size number: 50, 70, 100, and 140. It is in order to obtain the mass fraction that escaped from each sieve mesh. From the experiment, it can be concluded that mass percentage fraction of coffee powder is bigger than cocoa powder that escaped from the mesh. Hardness and humidity of coffee beans and cocoa beans have been the important factors that made coffee beans is easier to be crushed than cocoa beans.

  18. Microstructure and properties in Al-C-Cu system produced by mechanical milling

    International Nuclear Information System (INIS)

    Goytia-Reyes, R.; Gallegos-Orozco, V.; Flores-Zuniga, H.; Alvarado-Hernandez, F.; Huirache-Acuna, R.; Martinez-Sanchez, R.; Santos-Beltran, A.

    2009-01-01

    Different amounts of C and C-Cu mixtures were employed to produce Al-C and Al-C-Cu powder composites by mechanical milling. In order to determine the Cu effect, hardness tests were carried out in the as-milled samples and at different sintering temperatures. Also, X-ray analyses using Rietveld program, transmission electron microscopy and calorimetry were used for the microstructural characterization. In agreement with the results, the Cu powder acts as carrier in the incorporation of graphite into the Al matrix. Also, due to the presence of graphite particles together with Al 4 C 3 precipitation, hardness values remain stable even at elevated temperatures for these Al-based composites.

  19. Uranium mill tailings and radon

    International Nuclear Information System (INIS)

    Hanchey, L.A.

    1981-01-01

    The major health hazard from uranium mill tailings is presumed to be respiratory cancer resulting from the inhalation of radon daughter products. A review of studies on inhalation of radon and its daughters indicates that the hazard from the tailings is extremely small. If the assumptions used in the studies are correct, one or two people per year in the US may develop cancer as a result of radon exhaled from all the Uranium Mill Tailings Remedial Action Program sites. The remedial action should reduce the hazard from the tailings by a factor of about 100

  20. Soil Carbon 4 per mille

    Science.gov (United States)

    Minasny, Budiman; van Wesemael, Bas

    2017-04-01

    The '4 per mille Soils for Food Security and Climate' was launched at the COP21 aiming to increase global soil organic matter stocks by 4 per mille (or 0.4 %) per year as a compensation for the global emissions of greenhouse gases by anthropogenic sources. This paper surveyed the soil organic carbon (SOC) stock estimates and sequestration potentials from 20 regions in the world (New Zealand, Chile, South Africa, Australia, Tanzania, Indonesia, Kenya, Nigeria, India, China Taiwan, South Korea, China Mainland, United States of America, France, Canada, Belgium, England & Wales, Ireland, Scotland, and Russia) and asked whether the 4 per mille initiative is feasible. This study highlights region specific efforts and scopes for soil carbon sequestration. Reported soil C sequestration rates generally show that under best management practices, 4 per mille or even higher sequestration rates can be accomplished. High C sequestration rates (up to 10 per mille) can be achieved for soils with low initial SOC stock (topsoil less than 30 t C ha-1), and at the first twenty years after implementation of best management practices. In addition, areas that have reached equilibrium but not at their saturation level will not be able to further increase their sequestration. We found that most studies on SOC sequestration globally only consider topsoil (up to 0.3 m depth), as it is considered to be most affected by management techniques. The 4 per mille initiative was based on a blanket calculation of the whole global soil profile C stock, however the potential to increase SOC is mostly on managed agricultural lands. If we consider 4 per mille on global topsoil of agricultural land, SOC sequestration is about 3.6 Gt C per year, which effectively offset 40% of global anthropogenic greenhouse gas emissions. As a strategy for climate change mitigation, soil carbon sequestration buys time over the next ten to twenty years while other effective sequestration and low carbon technologies become

  1. Uranium mill tailings and radon

    Energy Technology Data Exchange (ETDEWEB)

    Hanchey, L A

    1981-04-01

    The major health hazard from uranium mill tailings is presumed to be respiratory cancer resulting from the inhalation of radon daughter products. A review of studies on inhalation of radon and its daughters indicates that the hazard from the tailings is extremely small. If the assumptions used in the studies are correct, one or two people per year in the United States may develop cancer as a result of radon exhaled from all the Uranium Mill Tailings Remedial Action program sites. The remedial action should reduce the hazard from the tailings by a factor of about 100.

  2. Uranium mill tailings and radon

    Energy Technology Data Exchange (ETDEWEB)

    Hanchey, L A

    1981-01-01

    The major health hazard from uranium mill tailings is presumed to be respiratory cancer resulting from the inhalation of radon daughter products. A review of studies on inhalation of radon and its daughters indicates that the hazard from the tailings is extremely small. If the assumptions used in the studies are correct, one or two people per year in the US may develop cancer as a result of radon exhaled from all the Uranium Mill Tailings Remedial Action Program sites. The remedial action should reduce the hazard from the tailings by a factor of about 100.

  3. Kinetics and formation mechanism of amorphous Fe52Nb48 alloy powder fabricated by mechanical alloying

    International Nuclear Information System (INIS)

    El-Eskandarany, S.

    1999-01-01

    A single phase amorphous Fe 52 Nb 48 alloy has been synthesized through a solid state interdiffusion of pure polycrystalline Fe and Nb powders at room temperature, using a high-energy ball-milling technique. The mechanisms of metallic glass formation and competing crystallization processes in the mechanically deformed composite powders have been investigated by means of X-ray diffraction, Moessbauer spectroscopy, differential thermal analysis, scanning electron microscopy and transmission electron microscopy. The numerous intimate layered composite particles of the diffusion couples that formed during the first and intermediate stages of milling time (0-56 ks), are intermixed to form amorphous phase(s) upon heating to about 625 K by so-called thermally assisted solid state amorphization, TASSA. The amorphization heat of formation for binary system via the TASSA, ΔH a , was measured directly as a function of the milling time. Comparable with the TASSA, homogeneous amorphous alloys were fabricated directly without heating the composite multilayered particles upon milling these particles for longer milling time (86 ks-144 ks). The amorphization reaction here is attributed to the mechanical driven solid state amorphization. This single amorphous phase transforms into an order phase (μ phase) upon heating at 1088 K (crystallization temperature, T x ) with enthalpy change of crystallization, ΔH x , of -8.3 kJmol -1 . (orig.)

  4. EFFECT OF CUP AND BALL TYPES ON MECHANO-CHEMICAL SYNTHES IS OF Al2O3–TiC NANOCOMPOSITE POWDER

    Directory of Open Access Journals (Sweden)

    M. Zakeri

    2012-07-01

    Full Text Available Al2O3–TiC nanocomposite powder was successfully synthesized by ball milling TiO2, Al and graphite powders. Effects of cup and ball type, milling time and annealing were investigated. XRD was used to characterize milled and annealed powders. The morphological and microstructural evolutions were studied by SEM and TEM. Results showed that the formation of this composite begins after 20 h and completes after 35 h of milling with stainless steel cup and balls. In contrast, there is no reaction during milling (up to 80 h with ZrO2 cup and balls. Fe and ZrO2 were the major impurities introduced during milling with stainless steel and ZrO2 cups, respectively. The Fe impurity was removed by leaching in 3HCl·HNO3 solution for 4 days. Mean grain size less than 7 nm was achieved at the end of milling. In spite of grain growth, this composite maintained its nanocrystalline nature after annealing at 1000°C.

  5. Hyperfine interactions and structural features of Fe–44Co–6Mo (wt.%) nanostructured powders

    International Nuclear Information System (INIS)

    Moumeni, Hayet; Nemamcha, Abderrafik; Alleg, Safia; Grenèche, Jean Marc

    2013-01-01

    Nanocrystalline Fe–44Co–6Mo (wt.%) powders have been prepared by high-energy ball milling from elemental Fe, Co and Mo pure powders in a P7 planetary ball mill. The obtained powders were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and Mössbauer spectrometry techniques. The influence of milling process and Mo substitution for Co in equiatomic FeCo have been examined in order to study structural evolution and formation mechanism of nanostructured Fe(CoMo) solid solution. XRD results show the formation of a BCC Fe(CoMo) solid solution (a = 0.2874 nm) where unmixed nanocrystalline Mo with a BCC structure is embedded. Disordered Fe(CoMo) solid solution is characterized by a broad hyperfine magnetic field distribution with two regions centered at B 1 = 35.0 T and B 2 = 30.7 T, respectively, attributed to disordered Fe(Co) solid solution and CoMo enriched environments. Prolonged milling and Mo addition cause the decrease of average hyperfine magnetic field while the average isomer shift remains nearly constant. - Highlights: ► BCC nanostructured Fe(CoMo) solid solution is prepared by milling of Fe, Co and Mo. ► Formation mechanism: Co diffusion into Fe lattice and Mo dissolution in Fe(Co). ► Crystallite size of Fe(CoMo) solid solution reaches 11 nm after 24 h of milling. ► Mössbauer analysis reveals 3 components: high field, enriched Co and low field

  6. Hyperfine interactions and structural features of Fe–44Co–6Mo (wt.%) nanostructured powders

    Energy Technology Data Exchange (ETDEWEB)

    Moumeni, Hayet, E-mail: hmoumeni@yahoo.fr [Laboratoire de Chimie Computationnelle et Nanostructures, Département des Sciences de la Matière, Faculté des Mathématiques et de l' Informatique et des Sciences de la Matière, Université 08 Mai 1945 - Guelma, B.P. 401, Guelma 24000 (Algeria); Nemamcha, Abderrafik [Laboratoire d' Analyses Industrielles et Génie des Matériaux, Faculté des Sciences et de la Technologie, Université 08 Mai 1945 - Guelma, B.P. 401, Guelma 24000 (Algeria); Alleg, Safia [Laboratoire de Magnétisme et de Spectroscopie des Solides, Département de Physique, Faculté des Sciences, Université de Annaba, B.P. 12, Annaba 23000 (Algeria); Grenèche, Jean Marc [Laboratoire de Physique de l' Etat Condensé, UMR CNRS 6087, Institut de Recherche en Ingénierie Moléculaire et Matériaux Fonctionnels IRIM2F, FR CNRS 2575, Université du Maine, 72085 Le Mans Cedex 9 (France)

    2013-02-15

    Nanocrystalline Fe–44Co–6Mo (wt.%) powders have been prepared by high-energy ball milling from elemental Fe, Co and Mo pure powders in a P7 planetary ball mill. The obtained powders were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and Mössbauer spectrometry techniques. The influence of milling process and Mo substitution for Co in equiatomic FeCo have been examined in order to study structural evolution and formation mechanism of nanostructured Fe(CoMo) solid solution. XRD results show the formation of a BCC Fe(CoMo) solid solution (a = 0.2874 nm) where unmixed nanocrystalline Mo with a BCC structure is embedded. Disordered Fe(CoMo) solid solution is characterized by a broad hyperfine magnetic field distribution with two regions centered at B{sub 1} = 35.0 T and B{sub 2} = 30.7 T, respectively, attributed to disordered Fe(Co) solid solution and CoMo enriched environments. Prolonged milling and Mo addition cause the decrease of average hyperfine magnetic field while the average isomer shift remains nearly constant. - Highlights: ► BCC nanostructured Fe(CoMo) solid solution is prepared by milling of Fe, Co and Mo. ► Formation mechanism: Co diffusion into Fe lattice and Mo dissolution in Fe(Co). ► Crystallite size of Fe(CoMo) solid solution reaches 11 nm after 24 h of milling. ► Mössbauer analysis reveals 3 components: high field, enriched Co and low field.

  7. Microstructural evolution of nanostructured Ti0.9Al0.1N prepared by reactive ball-milling

    International Nuclear Information System (INIS)

    Bhaskar, U.K.; Bid, S.; Pradhan, S.K.

    2011-01-01

    Research highlights: → Nanocrystalline stoichiometric Ti 0.9 Al 0.1 N powder has been prepared by ball-milling the 0.9 mol fraction of α-Ti (hcp) and 0.1 mol fraction of aluminum (fcc) powders under N 2 at room temperature. Initially, α-Ti phase partially transformed to the transient β-Ti phase and Ti 0.9 Al 0.1 N (fcc) phase is noticed to form after 3 h of milling. Nanocrystalline stoichiometric Ti 0.9 Al 0.1 N phase is formed after 7 h of milling. The main features which are observed in the present study are stated below: 1.During ball-milling of α-Ti, the α-Ti phase partially converted to transient cubic β-Ti phase within 1 h of milling. 2.Ti 0.9 Al 0.1 N (fcc) phase is noticed to form after 3 h of milling. Complete formation of Ti 0.9 Al 0.1 N (fcc) is obtained at 7 h of milling which is lesser than complete formation time (9 h) of TiN. Doping Al atoms accelerates the formation of (TiAl)N phase. 3.The particle size of Ti 0.9 Al 0.1 N decrease rapidly up to 3 h and then increase slightly due to agglomeration effect. 4.The particle size of Ti 0.9 Al 0.1 N estimated from X-ray is in good agreement with that measured from HRTEM. - Abstract: Nanocrystalline stoichiometric Ti 0.9 Al 0.1 N powder has been prepared by ball-milling the α-Ti (hcp) and aluminum (fcc) powders under N 2 at room temperature. Initially, α-Ti phase partially transformed to the transient cubic β-Ti phase and Ti 0.9 Al 0.1 N (fcc) phase is noticed to form after 3 h of milling. Nanocrystalline stoichiometric Ti 0.9 Al 0.1 N phase is formed after 7 h of milling. After 1 h of milling, all Al atoms are diffused into the α-Ti matrix. The transient β-Ti phase is noticed to form after 1 h of milling and disappears completely after 7 h of milling. Microstructure characterization of unmilled and ball-milled powders by analyzing XRD patterns employing the Rietveld structure refinement reveals the inclusion of Al and nitrogen atoms into the Ti lattice on the way to formation of Ti 0.9 Al 0.1 N

  8. EPA's role in uranium mining and milling

    International Nuclear Information System (INIS)

    Smith, P.B.

    1980-01-01

    EPA's role and actions in regulating uranium mining and milling are reviewed and updated. Special emphasis is given to EPA's current activities under the Uranium Mill Tailings Radiation Control Act of 1978

  9. Cold compaction behavior of nano-structured Nd–Fe–B alloy powders prepared by different processes

    International Nuclear Information System (INIS)

    Liu, Xiaoya; Hu, Lianxi; Wang, Erde

    2013-01-01

    Graphical abstract: Relative density enhancement and nanocrystallization of Nd 2 Fe 14 B phase are two major effective means to improve magnetic properties. Since the matrix Nd 2 Fe 14 B phase in the starting Nd–Fe–B alloy can be disproportionated into a nano-structured mixture of NdH 2.7 , Fe 2 B, and α-Fe phases during mechanical milling in hydrogen. It is thus important to study the densification behavior of nanocrystalline powders to evaluate and predict the cold compactibility of powders. By comparison with the as milled as well as melt-spun Nd 16 Fe 76 B 8 alloy powders, we find that the as-disproportionated Nd 16 Fe 76 B 8 alloy powder exhibits the best cold compactibility. As evident from the illustration presented below, compaction parameters (representing the powder compactibility) have been determined by fitting density–pressure data with double logarithm compaction equation. Densification mechanisms involved during cold compaction process are clarified in our work by referring to microstructure observation of samples prepared by various methods. As a result, highly densified green magnet compact can be obtained by cold pressing of as-disproportionated NdFeB alloy powders. Highlights: ► Nano-structured disproportionated Nd–Fe–B alloy powders by mechanical milling in hydrogen. ► Highly densified green magnet compact by cold pressing of as-disproportionated Nd–Fe–B alloy powders. ► Density–pressure data fitted well by an empirical powder compaction model. ► As-disproportionated powder showed better compactibility than as milled and melt-spun counterparts. ► The effects of physical properties on powder compactibility and densification mechanisms are clarified. - Abstract: The compaction behavior of nano-structured Nd 16 Fe 76 B 8 (atomic ratio) alloy powders, which were prepared by three different processing routes including melt spinning, mechanical milling in argon, and mechanically activated disproportionation by milling in

  10. Cold compaction behavior of nano-structured Nd-Fe-B alloy powders prepared by different processes

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Xiaoya [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China); Hu, Lianxi, E-mail: hulx@hit.edu.cn [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China); Wang, Erde [School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001 (China)

    2013-02-25

    Graphical abstract: Relative density enhancement and nanocrystallization of Nd{sub 2}Fe{sub 14}B phase are two major effective means to improve magnetic properties. Since the matrix Nd{sub 2}Fe{sub 14}B phase in the starting Nd-Fe-B alloy can be disproportionated into a nano-structured mixture of NdH{sub 2.7}, Fe{sub 2}B, and {alpha}-Fe phases during mechanical milling in hydrogen. It is thus important to study the densification behavior of nanocrystalline powders to evaluate and predict the cold compactibility of powders. By comparison with the as milled as well as melt-spun Nd{sub 16}Fe{sub 76}B{sub 8} alloy powders, we find that the as-disproportionated Nd{sub 16}Fe{sub 76}B{sub 8} alloy powder exhibits the best cold compactibility. As evident from the illustration presented below, compaction parameters (representing the powder compactibility) have been determined by fitting density-pressure data with double logarithm compaction equation. Densification mechanisms involved during cold compaction process are clarified in our work by referring to microstructure observation of samples prepared by various methods. As a result, highly densified green magnet compact can be obtained by cold pressing of as-disproportionated NdFeB alloy powders. Highlights: Black-Right-Pointing-Pointer Nano-structured disproportionated Nd-Fe-B alloy powders by mechanical milling in hydrogen. Black-Right-Pointing-Pointer Highly densified green magnet compact by cold pressing of as-disproportionated Nd-Fe-B alloy powders. Black-Right-Pointing-Pointer Density-pressure data fitted well by an empirical powder compaction model. Black-Right-Pointing-Pointer As-disproportionated powder showed better compactibility than as milled and melt-spun counterparts. Black-Right-Pointing-Pointer The effects of physical properties on powder compactibility and densification mechanisms are clarified. - Abstract: The compaction behavior of nano-structured Nd{sub 16}Fe{sub 76}B{sub 8} (atomic ratio) alloy

  11. Phase evolution in Al-Ni-(Ti, Nb, Zr) powder blends by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Samanta, A. [Department of Metallurgy and Materials Engineering, Bengal Engineering and Science University, Shibpur (India); Manna, I. [Metallurgical and Materials Engineering Department, I.I.T., Kharagpur 721302 (India); Chattopadhyay, P.P. [Department of Metallurgy and Materials Engineering, Bengal Engineering and Science University, Shibpur (India)], E-mail: c.partha@mailcity.com

    2007-08-25

    Mechanical alloying of Al-rich Al-Ni-ETM (ETM = Ti, Nb, Zr) elemental powder blends by planetary ball milling yielded amorphous and/or nanocrystalline products after ball milling for suitable duration. Powder samples collected at different stages of ball milling have been examined by X-ray diffraction, differential scanning caloremetry and high-resolution transmission electron microscopy to examine the solid-state phase evolution. Powder blends having nominal composition of Al{sub 80}Ni{sub 10}Ti{sub 10} and Al{sub 80}Ni{sub 10}Nb{sub 10} yielded predominantly amorphous products, while the other alloys formed composite microstructures comprising nanaocrystalline and amorphous solid solutions. The amorphous Al{sub 80}Ni{sub 10}Ti{sub 10} alloy was mixed with different amounts of Al powder, and subjected to warm rolling after consolidation within the Al-cans with or without intermediate annealing for 10 min at 500 K to obtain sheet of 2.5 mm thickness. Notable improvement in mechanical properties has been achieved for the composite sheets in comparison to the pure Al.

  12. Magneto-structural transformations in Ni{sub 50}Mn{sub 37.5}Sn{sub 12.5−x}In{sub x} Heusler powders

    Energy Technology Data Exchange (ETDEWEB)

    Maziarz, Wojciech; Wójcik, Anna; Czaja, Paweł [Instituite of Metallurgy and Materials Science, Polish Academy of Sciences, 25 Reymonta Str, 30-059 Kraków (Poland); Żywczak, Antoni [AGH University of Science and Technology, Academic Centre for Materials and Nanotechnology, Mickiewicza 30, 30-059 Kraków (Poland); Jan Dutkiewicz [Instituite of Metallurgy and Materials Science, Polish Academy of Sciences, 25 Reymonta Str, 30-059 Kraków (Poland); Hawełek, Łukasz [Institute of Non-Ferrous Metals, ul. Sowinskiego 5, 44-100 Gliwice (Poland); Cesari, Eduard [Department de Física, Universitat de les Illes Balears, Ctra. de Valldemossa, km 7.5, Palma de Mallorca E-07122 (Spain)

    2016-08-15

    The effect of ball milling and subsequently annealing of melt spun ribbons on magneto-structural transformations in Ni{sub 50}Mn{sub 37.5}Sn{sub 12.5−x}In{sub x} (x=0, 2, 4, 6) ribbons is presented. Short time vibration milling allows to obtain chemically homogenous powders of angular particle shapes and size within 10–50 μm. Milling does not change the characteristic temperatures of martensitic transformation in comparison to the melt spun ribbons. The effect of In substitution for Sn on martensitic transformation has a complex mechanism, associated with electron density change. Substitution of Sn by In in both milled and annealed powders leads to decrease of Curie temperature of austenite and increase of martensitic transformation temperature, stabilizing martensitic phase. The coexistence of magnetic transformation of austenite and martensitic transformation at low magnetic field was observed. The intermartensitic transformation of 4O martensite to L1{sub 0} martensite was observed during cooling at low magnetic field and this was confirmed by TEM microstructure observations. The annealing process of as-milled powders leads to the change of their martensitic structure due to relaxation of internal stresses associated with anisotropic columnar grain microstructure formed during melt spinning process. The level of stresses introduced during milling of ribbons has no significant influence on martensitic transformation. The annealing process of as milled powders leads to enhancement of their magnetic properties, decrease of Curie temperature of austenite, and marginal change of temperature of martenisitic transformation. - Highlights: • Vibration milling of ribbons allows to obtain angular powders of size 10–50 μm. • Vibration milling improves chemical homogeneity of alloys. • Indium addition changes the magneto-structural transformations in Ni–Mn–Sn–In alloys. • Complex character of magneto-structural transformations is visible. • Multistep

  13. Study of the sintering behavior of fine, ultrafine and nanocrystalline WC-CO mixtures obtained by high energy milling

    International Nuclear Information System (INIS)

    Salvador, M. D.; Bonache, V.; Amigo, V.; Busquets, D.

    2008-01-01

    In this work the sintering behaviour of fine, ultrafine and nanocrystalline WC-12Co mixtures obtained by high energy milling, as well commercial nano powders, have been studied, in order to evaluate the effect of the particle size and the powder processing, in the densification, microstructural development and mechanical properties of the final product. The consolidation of the mixtures has been made by uniaxial pressing and sintering in vacuum, and by hot isostatic pressing. The sintered materials have been evaluated by measures of density, hardness and indentation fracture toughness, and micro structurally characterized by optical microscopy and scanning and transmission electronic microscopy (SEM and TEM). The results show the improvements in resistant behaviour of the materials obtained from nanocrystalline powders, in spite of the grain growth experienced during the sintering. The best results were obtained for the milling nanocrystalline material, which presents values of hardness higher than 180 HV. (Author) 46 refs

  14. The effect of ZrO2 grinding media on the attrition milling of FeAl with Y2O3

    International Nuclear Information System (INIS)

    Gedevanishvili, S.; Deevi, S.C.

    2004-01-01

    Attrition milling of water and gas atomized FeAl was carried out with Y 2 O 3 , where ZrO 2 was used as a grinding media in place of stainless steel balls to avoid contamination with Cr and C. Consolidation of the milled powders produced complex FeAl phases containing Zr which doubled the hardness and significantly improved the creep resistance as compared to that of unmilled and consolidated FeAl

  15. Structural Relaxations and Thermodynamic Properties of Molecular Amorphous Solids by Mechanical Milling

    Science.gov (United States)

    Tsukushi, I.; Yamamuro, O.; Matsuo, T.

    The organic crystals of tri-O-methyl-β-cyclodextrin (TMCD) and its three clathrate compounds containing benzoic acid (BA), p-nitrobenzoic acid (NBA) and p-hydroxybenzoic acid (HBA), sucrose (SUC), salicin (SAL), phenolphthalein (PP), 1,3,5-tri-α-naphthylbenzene (TNB) were amorphized by milling with a vibrating mill for 2 ˜ 16 hours at room temperature. The amorphization was checked by differential scanning calorimetry (DSC) and X-ray powder diffraction. The heat capacities of crystals, liquid quenched glasses (LQG), and mechanically-milled amorphous solid (MMAS) of TMCD and TNB were measured with an adiabatic calorimeter in the temperature range between 12 and 375 K. For both compounds, the enthalpy relaxation of MMAS appeared in the wide temperature range below Tg and the released configurational enthalpy was much larger than that of LQG, indicating that MMAS is more disordered and strained than LQG.

  16. Transformation of Goethite to Hematite Nanocrystallines by High Energy Ball Milling

    Directory of Open Access Journals (Sweden)

    O. M. Lemine

    2014-01-01

    Full Text Available α-Fe2O3 nanocrystallines were prepared by direct transformation via high energy ball milling treatment for α-FeOOH powder. X-ray diffraction, Rietveld analysis, TEM, and vibrating sample magnetometer (VSM are used to characterize the samples obtained after several milling times. Phase identification using Rietveld analysis showed that the goethite is transformed to hematite nanocrystalline after 40 hours of milling. HRTEM confirm that the obtained phase is mostly a single-crystal structure. This result suggested that the mechanochemical reaction is an efficient way to prepare some iron oxides nanocrystallines from raw materials which are abundant in the nature. The mechanism of the formation of hematite is discussed in text.

  17. 75 FR 71463 - Woodland Mills Corporation Mill Spring, NC; Notice of Revised Determination on Reconsideration

    Science.gov (United States)

    2010-11-23

    ... DEPARTMENT OF LABOR Employment and Training Administration [TA-W-73,695] Woodland Mills Corporation Mill Spring, NC; Notice of Revised Determination on Reconsideration By application dated July 22... regarding the eligibility of workers and former workers of Woodland Mills Corporation, Mill Spring, North...

  18. Would John Stuart Mill have regulated pornography?

    OpenAIRE

    McGlynn, C.; Ward, I.

    2014-01-01

    John Stuart Mill dominates contemporary pornography debates where he is routinely invoked as an authoritative defence against regulation. This article, by contrast, argues that a broader understanding of Mill's ethical liberalism, his utilitarianism, and his feminism casts doubt over such an assumption. New insights into Mill's approach to sex, sexual activity, and the regulation of prostitution reveal an altogether more nuanced and activist approach. We conclude that John Stuart Mill would a...

  19. Thermal evolution of nitrate precursors for processing of lanthanide perovskites

    Directory of Open Access Journals (Sweden)

    Kozhukharov, V. S.

    1998-12-01

    Full Text Available Studies on thermal decomposition of ceramic powder with a general formula of (La1-x Ba x (Co0.8 Fe0.2O3 have been achieved. Precursors as nitrate solutions with additive of EDTA as complexion agent are used for powder processing. The black powders obtained are dried and their thermal evolution up to 1000ºC has been investigated by Differential Thermal Analysis. The powders was analyzed by EDX and ICP- AES, as well. It was established that the powder compositions are very close to the nominal one. The resulting DTA, TA, TG and DTG curves are analyzed as function of the composition and heating rate applied. At polythermal scanning regime three regions the powder thermal evolution are discussed. The correlation dependence has been examined for both Sr- and Ba- doped multicomponent lanthanide samples. The multicomponent nature of the samples have been shown on the base of the thermal treatment applied and XRD phase control carried out.

    Se han realizado estudios sobre la descomposición térmica de polvos cerámicos de fórmula general (La1-x Ba x (Co0.8 Fe0.2O3. Se utilizaron como precursores soluciones de nitratos con EDTA como agente acomplejante. La evolución térmica del polvo negro obtenido se estudió hasta la temperatura de 1000 ºC por medio de análisis térmico diferencial. Los polvos se analizaron así mismo por EDX e ICP-A ES. Se estableció que la composición de los polvos esta muy próxima a la composición nominal. Se distingue tres regímenes en la evolución térmica. Se examina la dependencia con el contenido en lantanidas multicomponentes de pulsos con Sr y Ba. La naturaleza multicomponente se ha mostrado sobre la base del tratamiento térmico empleado y el análisis de las fases cristalinas.

  20. Composition influence on positron annihilation parameters in ZnO-based nanocrystal semiconductor powders

    Energy Technology Data Exchange (ETDEWEB)

    Damonte, L.C.; Hernandez Fenollosa, M.A.; Donderis, V.; Mari, B. [Departamento de Fisica Aplicada, Universidad Politecnica de Valencia, Cami de Vera s/n, Valencia, 46071 (Spain)

    2007-07-01

    Zn{sub 1-x}Mg{sub x}O powders at various compositions were obtained by mechanical milling from the binary oxides. The progressive incorporation of Mg atoms into the ZnO lattice was monitored by X-ray diffraction (XRD). The evolution of annihilation parameters with milling time and composition were analyzed and related to the possible types of mechanical and substitutional induced defect present. It was concluded that the average lifetime constitute a useful parameter to sense the complete cation substitution in the wurtzite structure. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  1. Composition influence on positron annihilation parameters in ZnO-based nanocrystal semiconductor powders

    International Nuclear Information System (INIS)

    Damonte, L.C.; Hernandez Fenollosa, M.A.; Donderis, V.; Mari, B.

    2007-01-01

    Zn 1-x Mg x O powders at various compositions were obtained by mechanical milling from the binary oxides. The progressive incorporation of Mg atoms into the ZnO lattice was monitored by X-ray diffraction (XRD). The evolution of annihilation parameters with milling time and composition were analyzed and related to the possible types of mechanical and substitutional induced defect present. It was concluded that the average lifetime constitute a useful parameter to sense the complete cation substitution in the wurtzite structure. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  2. 77 FR 14837 - Bioassay at Uranium Mills

    Science.gov (United States)

    2012-03-13

    ... NUCLEAR REGULATORY COMMISSION [NRC-2012-0057] Bioassay at Uranium Mills AGENCY: Nuclear Regulatory..., ``Bioassay at Uranium Mills.'' This guide describes a bioassay program acceptable to the NRC staff for uranium mills and applicable portions of uranium conversion facilities where the possibility of exposure...

  3. Chevron's Panna Maria mill process description

    International Nuclear Information System (INIS)

    Anon.

    1979-01-01

    Key features of Chevron's Uranium Mill located near Panna Maria, Texas, are described. The mill is designed to process a nominal 2500 dry tons/day of uranium bearing ore containing 15% uncombined moisture. The following operations at the mill are highlighted: ore receiving, grinding, leaching, countercurrent decantation and tailings disposal, filtering, solvent extraction, solvent stripping, precipitation, drying, and packaging

  4. Ground beetle populations near a kraft mill

    Energy Technology Data Exchange (ETDEWEB)

    Freitag, R.; Hastings, L.; Mercer, W.R.; Smith, A.

    1973-02-01

    Twenty species of ground beetles (Family Carabidae) and one species of carrion beetle (Family Silphidae) were collected in six stations east of a kraft paper mill in Thunder Bay, Ontario, from May to August, 1971. The beetle population decreased markedly towards the mill. There was no apparent statistical difference in size variation of specimens near the mill and those further away.

  5. Raman spectroscopy fingerprint of stainless steel-MWCNTs nanocomposite processed by ball-milling

    Directory of Open Access Journals (Sweden)

    Marcos Allan Leite dos Reis

    2018-01-01

    Full Text Available Stainless steel 304L alloy powder and multiwalled carbon nanotubes were mixed by ball-milling under ambient atmosphere and in a broad range of milling times, which spans from 0 to 120 min. Here, we provided spectroscopic signatures for several distinct composites produced, to show that the Raman spectra present interesting splittings of the D-band feature into two main sub-bands, D-left and D-right, together with several other secondary features. The G-band feature also presents multiple splittings that are related to the outer and inner diameter distributions intrinsic to the multiwalled carbon nanotube samples. A discussion about the second order 2D-band (also known as G′-band is also provided. The results reveal that the multiple spectral features observed in the D-band are related to an increased chemical functionalization. A lower content of amorphous carbon at 60 and 90 min of milling time is verified and the G-band frequencies associated to the tubes in the outer diameters distribution is upshifted, which suggests that doping induced by strain is taking place in the milled samples. The results indicate that Raman spectroscopy can be a powerful tool for a fast and non-destructive characterization of carbon nanocomposites used in powder metallurgy manufacturing processes.

  6. Thermogravimetric and Differential Scanning Calorimetric Behavior of Ball-Milled Nuclear Graphite

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Eung Seon; Kim, Min Hwan; Kim, Yong Wan [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Park, Yi Hyun; Cho, Seung Yon [National Fusion Research Institute, Daejeon (Korea, Republic of)

    2013-10-15

    An examination was made to characterize the oxidation behavior of ball-milled nuclear graphite powder through a TG-DSC analysis. With the ball milling time, the BET surface area increased with the reduction of particle size, but decreased with the chemisorptions of O{sub 2} on the activated surface. The enhancement of the oxidation after the ball milling is attributed to both increases in the specific surface area and atomic scale defects in the graphite structure. In a high temperature gas-cooled reactor, nuclear graphite has been widely used as fuel elements, moderator or reflector blocks, and core support structures owing to its excellent moderating power, mechanical properties and machinability. For the same reason, it will be used in a helium cooled ceramic reflector test blanket module for the ITER. Each submodule has a seven-layer breeding zone, including three neutron multiplier layers packed with beryllium pebbles, three lithium ceramic pebbles packed tritium breeder layers, and a reflector layer packed with 1 mm diameter graphite pebbles to reduce the volume of beryllium. The abrasion of graphite structures owing to relative motion or thermal cycle during operation may produce graphite dust. It is expected that graphite dust will be more oxidative than bulk graphite, and thus the oxidation behavior of graphite dust must be examined to analyze the safety of the reactors during an air ingress accident. In this study, the thermal stability of ball-milled graphite powder was investigated using a simultaneous thermogravimeter-differential scanning calorimeter.

  7. Hydrogen storage in Mg-Ni-Fe compounds prepared by melt spinning and ball milling

    Energy Technology Data Exchange (ETDEWEB)

    Palade, P. [Settore Materiali, Dipartimento di Ingegneria Meccanica, Universita di Padova, via Marzolo 9, 35131 Padova (Italy); National Institute for Physics of Materials, Atomistilor 105 bis, P.O. Box MG-7, 077125 Bucharest-Magurele (Romania); Sartori, S. [Settore Materiali, Dipartimento di Ingegneria Meccanica, Universita di Padova, via Marzolo 9, 35131 Padova (Italy); Maddalena, A. [Settore Materiali, Dipartimento di Ingegneria Meccanica, Universita di Padova, via Marzolo 9, 35131 Padova (Italy); Principi, G. [Settore Materiali, Dipartimento di Ingegneria Meccanica, Universita di Padova, via Marzolo 9, 35131 Padova (Italy)]. E-mail: giovanni.principi@unipd.it; Lo Russo, S. [Dipartimento di Fisica, Universita di Padova, Via Marzolo 8, 35131 Padova (Italy); Lazarescu, M. [National Institute for Physics of Materials, Atomistilor 105 bis, P.O. Box MG-7, 077125 Bucharest-Magurele (Romania); Schinteie, G. [National Institute for Physics of Materials, Atomistilor 105 bis, P.O. Box MG-7, 077125 Bucharest-Magurele (Romania); Kuncser, V. [National Institute for Physics of Materials, Atomistilor 105 bis, P.O. Box MG-7, 077125 Bucharest-Magurele (Romania); Filoti, G. [National Institute for Physics of Materials, Atomistilor 105 bis, P.O. Box MG-7, 077125 Bucharest-Magurele (Romania)

    2006-05-18

    Magnesium-rich Mg-Ni-Fe intermetallic compounds have been prepared by two different routes: (a) short time ball milling of ribbons obtained by melt spinning; (b) long time ball milling of a mixture of MgH{sub 2}, Ni and Fe powders. The first type of samples displays an hydrogen desorption kinetics better than the second one. Pressure composition isotherm measurements exhibit for both type of samples two plateaux, the lower and wider corresponding to the MgH{sub 2} phase and the upper and shorter corresponding to the Mg{sub 2}NiH{sub 4} phase. The presence of the two types of hydrides is confirmed by X-ray diffraction analysis. Moessbauer spectroscopy shows that in melt spun and subsequently milled samples iron is mainly in a disordered structure and segregates after hydrogenation, while in directly milled powders remains mainly unalloyed. After multiple hydrogen absorption/desorption cycles the main part of iron is in metallic state in samples of both types, those of first type preserving better hydrogen desorption kinetics.

  8. A morphological evaluation of a duplex stainless steel processed by high energy Ball Mill

    International Nuclear Information System (INIS)

    Yonekubo, Ariane Emi; Cintho, Osvaldo Mitsuyuki; Aguiar, Denilson Jose Marcolino de; Capocchi, Jose Deodoro Trani

    2009-01-01

    The duplex stainless steels are formed by a ferrite and austenite mixture, giving them a combination of properties. Commercially, these steels are hot rolled, developing an anisotropic, alternated ferrite and austenite elongated lamellae microstructure. In this work, a duplex stainless steel was produced by the mixture of elementary powders with the composition Fe-19.5Cr-5Ni processed in an ATTRITOR ball mill during periods up to 15 hours. The powders obtained were compressed in specimens and were heat treated in the temperatures of 900, 1050 and 1200 °C during 1 hour and analysed by x ray diffraction, optic microscopy, scanning electron microscopy and energy dispersion spectroscopy. An optimized microstructure with ultrafine, equiaxial and regular duplex microstructure was obtained in the 15 hour milling and 1200 °C heat treatment. Afterwards, a commercially super duplex stainless steel UNS S32520 was aged at 800 °C aiming the precipitation of σ phase in order to reduce its toughness and then, milled in SPEX mill. The resulting microstructure was a very fine duplex type with irregular grain boundary morphology duo to the grain growth barrier promoted by the renascent σ phase particles during sintering process. (author)

  9. Raman spectroscopy fingerprint of stainless steel-MWCNTs nanocomposite processed by ball-milling

    Science.gov (United States)

    dos Reis, Marcos Allan Leite; Barbosa Neto, Newton Martins; de Sousa, Mário Edson Santos; Araujo, Paulo T.; Simões, Sónia; Vieira, Manuel F.; Viana, Filomena; Loayza, Cristhian R. L.; Borges, Diego J. A.; Cardoso, Danyella C. S.; Assunção, Paulo D. C.; Braga, Eduardo M.

    2018-01-01

    Stainless steel 304L alloy powder and multiwalled carbon nanotubes were mixed by ball-milling under ambient atmosphere and in a broad range of milling times, which spans from 0 to 120 min. Here, we provided spectroscopic signatures for several distinct composites produced, to show that the Raman spectra present interesting splittings of the D-band feature into two main sub-bands, D-left and D-right, together with several other secondary features. The G-band feature also presents multiple splittings that are related to the outer and inner diameter distributions intrinsic to the multiwalled carbon nanotube samples. A discussion about the second order 2D-band (also known as G'-band) is also provided. The results reveal that the multiple spectral features observed in the D-band are related to an increased chemical functionalization. A lower content of amorphous carbon at 60 and 90 min of milling time is verified and the G-band frequencies associated to the tubes in the outer diameters distribution is upshifted, which suggests that doping induced by strain is taking place in the milled samples. The results indicate that Raman spectroscopy can be a powerful tool for a fast and non-destructive characterization of carbon nanocomposites used in powder metallurgy manufacturing processes.

  10. Crystallite sizes of LiH before and after ball milling and thermal exposure

    Energy Technology Data Exchange (ETDEWEB)

    Ortiz, Angel L. [Departamento de Electronica e Ingenieria Electromecanica, Universidad de Extremadura, Badajoz (Spain); Osborn, William; Markmaitree, Tippawan [Department of Chemical, Materials and Biomolecular Engineering, University of Connecticut, 97 North Eagleville Road, U-3136 Storrs, CT 06269-3136 (United States); Shaw, Leon L. [Department of Chemical, Materials and Biomolecular Engineering, University of Connecticut, 97 North Eagleville Road, U-3136 Storrs, CT 06269-3136 (United States)], E-mail: leon.shaw@uconn.edu

    2008-04-24

    The powder characteristics of lithium hydride (LiH) as a function of high-energy ball milling condition are systematically investigated via quantitative X-ray diffraction (XRD) analysis. The results obtained from the XRD analysis are compared with those attained from scanning electron microscopy (SEM), transmission electron microscopy (TEM), and specific surface area (SSA) analyses. The thermal stability of the ball-milled LiH is also investigated in order to provide physical insights into its cyclic stability in hydrogen sorption and desorption cycles. The results indicate that ball milling is effective in obtaining nano-crystalline LiH powder which is relatively stable with retention of nano-crystals after thermal exposure at 285 deg. C (equivalent to 0.58T{sub m}) for 1 h. The good thermal stability observed is attributed to the presence of many pores in the agglomerates at the ball-milled condition. These pores effectively prevent crystal growth during the thermal exposure.

  11. The automatic lumber planing mill

    Science.gov (United States)

    Peter Koch

    1957-01-01

    It is probable that a truly automatic planning operation could be devised if some of the variables commonly present in the mill-run lumber were eliminated and the remaining variables kept under close control. This paper will deal with the more general situation faced by mostl umber manufacturing plants. In other words, it will be assumed that the incoming lumber has...

  12. Soil carbon 4 per mille

    NARCIS (Netherlands)

    Mulder, V.L.

    2017-01-01

    The ‘4 per mille Soils for Food Security and Climate’ was launched at the COP21 with an aspiration to increase global soil organic matter stocks by 4 per 1000 (or 0.4 %) per year as a compensation for the global emissions of greenhouse gases by anthropogenic sources. This paper surveyed the soil

  13. Massive Yang-Mills fields

    NARCIS (Netherlands)

    Veltman, M.J.G.; Reiff, J.

    1969-01-01

    Two problems are studied in the paper: (i) the relation between Lagrangian and Feynman rules if the Lagrangian contains derivative couplings and/or vector meson fields and (ii) the behaviour of certain two closed loop diagrams in the perturbation theory of Yang-Mills fields. With respect to ( i ) .

  14. Ultrafine yttria-stabilized zirconia powders prepared by pyrolysis of a metal-oxalate-cellulose complex

    Energy Technology Data Exchange (ETDEWEB)

    Solov`eva, L.V.; Bashmakov, I.A.; Kaputskii, F.N. [Research Institute of Physicochemical Problems, Minsk (Belarus)] [and others

    1995-12-01

    Preparation of high-purity submicron powders with uniform particles is a key stage in the fabrication of high-quality ceramics. For this purpose, chemical methods are commonly used. Recently, pyrolysis of salt-cellulose compositions has gained acceptance for the preparation of mixed oxide powders. This method ensures control of the morphology and particle size of the resultant powders. In this work, the authors present an environmentally safe method for preparing ZrO{sub 2}-based powders from metal-oxalate-cellulose complexes (MOCC) used as precursors instead of soluble metal salts physisorbed on the cellulose surface. The powders obtained by this method feature higher dispersity than their commercially available analogs.

  15. Influence of milling time on microstructure and magnetic properties of Fe{sub 80}P{sub 11}C{sub 9} alloy produced by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Taghvaei, A.H. [Department of Materials Science and Engineering, Shiraz University of Technology, Shiraz (Iran, Islamic Republic of); Ghajari, F., E-mail: fati.ghajari@gmail.com [Department of Materials Science and Engineering, Shiraz University, Shiraz (Iran, Islamic Republic of); Markó, D. [IFW Dresden, Institute for Complex Materials, Helmholtzstr. 20, 01069 Dresden (Germany); Prashanth, K.G. [IFW Dresden, Institute for Complex Materials, Helmholtzstr. 20, 01069 Dresden (Germany); Additive manufacturing Center, Sandvik AB, 81181 Sandviken (Sweden)

    2015-12-01

    Fe{sub 80}P{sub 11}C{sub 9} alloy with amorphous/nanocrytalline microstructure has been synthesized by mechanical alloying of the elemental powders. The microstructure, thermal behavior and morphology of the produced powders have been studied by X-ray diffraction (XRD), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM), respectively. The crystallite size, lattice strain and fraction of the amorphous phase have been calculated by Rietveld refinement method. The results indicate that the powders microstructure consists of α-Fe(P,C) nanocrystals with an average diameter of 9 nm±1 nm dispersed in the amorphous matrix after 90 h of milling. Moreover, the fraction of amorphous phase initially increases up to 90 h of milling and then decreases after 120 h of milling, as a result of mechanical crystallization and formation of Fe{sub 2}P phase. The magnetic measurements show that while the saturation magnetization decreases continuously with the milling time, the coercivity exhibits a complicated trend. The correlation between microstructural changes and magnetic properties has been discussed in detail. - Highlights: • Glass formation was investigated in Fe{sub 80}P{sub 11}C{sub 9} by mechanical alloying. • Structural parameters were calculated by Rietveld refinement method. • Milling first increased and then decreased the fraction of amorphous phase. • Magnetic properties were significantly changed upon milling.

  16. Performance enhancement of NdFeB nanoflakes prepared by surfactant-assisted ball milling at low temperature by using different surfactants

    Science.gov (United States)

    An, Xiaoxin; Jin, Kunpeng; Wang, Fang; Fang, Qiuli; Du, Juan; Xia, Weixing; Yan, Aru; Liu, J. Ping; Zhang, Jian

    2017-02-01

    Hard magnetic NdFeB submicron and nanoflakes were successfully prepared by surfactant-assisted ball milling at room temperature (SABMRT) and low temperature (SABMLT) by using oleic acid (OA), oleylamine (OLA) and trioctylamine (TOA) as surfactant, respectively. Among the surfactants used, OA and OLA have similar effects on the morphology of the NdFeB nanoflakes milled at both room and low temperature. In the case of TOA, irregular micron-sized particles and submirco/nanoflakes were obtained for the NdFeB powders prepared by SABMRT and SABMLT, respectively. Samples prepared by SABMLT show better crystallinity and better degree of grain alignment than that prepared by SABMRT with the same surfactant. Comparing with the samples milled at RT, higher coercivity and larger remanence ratio were achieved in the NdFeB samples prepared at LT. The amounts of residual surfactants in final NdFeB powders were also calculated, which reveals that the final NdFeB powders milled at LT possess lower amount of residual surfactants than those milled at RT. It was found that lowering milling temperature of SABM would be a promising way for fabricating permanent magnetic materials with better hard magnetic properties.

  17. Microstructural changes and effect of variation of lattice strain on positron annihilation lifetime parameters of zinc ferrite nanocomposites prepared by high enegy ball-milling

    Directory of Open Access Journals (Sweden)

    Abhijit Banerjee

    2012-12-01

    Full Text Available Zn-ferrite nanoparticles were synthesized at room temperature by mechanical alloying the stoichiometric (1:1 mol% mixture of ZnO and α-Fe2O3 powder under open air. Formation of both normal and inverse spinel ferrite phases was noticed after 30 minutes and 2.5 hours ball milling respectively and the content of inverse spinel phase increased with increasing milling time. The phase transformation kinetics towards formation of ferrite phases and microstructure characterization of ball milled ZnFe2O4 phases was primarily investigated by X-ray powder diffraction pattern analysis. The relative phase abundances of different phases, crystallite size, r.m.s. strain, lattice parameter change etc. were estimated from the Rietveld powder structure refinement analysis of XRD data. Positron annihilation lifetime spectra of all ball milled samples were deconvoluted with three lifetime parameters and their variation with milling time duration was explained with microstructural changes and formation of different phases with increase of milling time duration.

  18. Production of fine powder from silk by radiation

    International Nuclear Information System (INIS)

    Takeshita, Hidefumi; Yoshii, Fumio; Kume, Tamikazu

    2000-01-01

    Silk fine power was prepared directly from silk fiber irradiated with an accelerated electron beam(EB). Irradiated silk fiber was well pulverized only by physical crushing using ball mill without any chemical pretreatment. Raw and degummed silk fibers were irradiated at ambient temperature in the dose range of 250-1000 kGy. Although unirradiated silk fibers were not pulverized at all, irradiated fibers were easily pulverized and showed higher conversion from fiber to powder for higher doses. The presence of oxygen in the irradiation atmosphere enhanced pulverization of silk fiber. Raw silk fibers were less pulverized compared to degummed ones. The electron microscope observation showed that the minimum particle size of silk powder obtained from fiber irradiated by 1000 kGy in oxygen was less than 10 microns. It was found that fibroin powder obtained in this work dissolved remarkably into cold water, thought unirradiated fibroin fiber had little solubility even in hot water. A typical soluble fraction was about 60% for fibroin powder obtained from fiber irradiated by 1000 kGy in oxygen. (author)

  19. High yttria ferritic ODS steels through powder forging

    Science.gov (United States)

    Kumar, Deepak; Prakash, Ujjwal; Dabhade, Vikram V.; Laha, K.; Sakthivel, T.

    2017-05-01

    Oxide dispersion strengthened (ODS) steels are being developed for future nuclear reactors. ODS Fe-18%Cr-2%W-0.2%Ti steels with 0, 0.35, 0.5, 1 and 1.5% Y2O3 (all compositions in weight%) dispersion were fabricated by mechanical alloying of elemental powders. The powders were placed in a mild steel can and forged in a stream of hydrogen gas at 1473 K. The steels were forged again to final density. The strength of ODS steel increased with yttria content. Though this was accompanied by a decrease in tensile elongation, all the steels showed significant ductility. The ductility in high yttria alloys may be attributed to improved inter-particle bonding between milled powders due to reduction of surface oxides by hydrogen. This may permit development of ODS steels with yttria contents higher than the conventional limit of 0.5%. It is suggested that powder forging is a promising route to fabricate ODS steels with high yttria contents and improved ductility.

  20. Production of fine powder from silk by radiation

    Energy Technology Data Exchange (ETDEWEB)

    Takeshita, Hidefumi; Yoshii, Fumio; Kume, Tamikazu [Japan Atomic Energy Research Inst., Takasaki, Gunma (Japan). Takasaki Radiation Chemistry Research Establishment; Ishida, Kazunari; Kamiishi, Youichi [Textile Research Institute of Gunma, Kiryu, Gunma (Japan)

    2000-03-01

    Silk fine power was prepared directly from silk fiber irradiated with an accelerated electron beam(EB). Irradiated silk fiber was well pulverized only by physical crushing using ball mill without any chemical pretreatment. Raw and degummed silk fibers were irradiated at ambient temperature in the dose range of 250-1000 kGy. Although unirradiated silk fibers were not pulverized at all, irradiated fibers were easily pulverized and showed higher conversion from fiber to powder for higher doses. The presence of oxygen in the irradiation atmosphere enhanced pulverization of silk fiber. Raw silk fibers were less pulverized compared to degummed ones. The electron microscope observation showed that the minimum particle size of silk powder obtained from fiber irradiated by 1000 kGy in oxygen was less than 10 microns. It was found that fibroin powder obtained in this work dissolved remarkably into cold water, thought unirradiated fibroin fiber had little solubility even in hot water. A typical soluble fraction was about 60% for fibroin powder obtained from fiber irradiated by 1000 kGy in oxygen. (author)

  1. Elaboration of the hydroxyapatite with different precursors and application for the retention of the lead.

    Science.gov (United States)

    Meski, S; Ziani, S; Khireddine, H; Yataghane, F; Ferguene, N

    2011-01-01

    Carbonate hydroxyapatite (CHAP) was synthesized from different precursors; synthetic (CaCO3 and Ca(OH)2) and natural (egg shell before and after calcinations at 900 degrees C) under different conditions and characterized by using TG/DTG analysis, X-ray powder diffraction (XRD) method and Fourier transform infrared (FT-IR) spectroscopy techniques. The results of these analyses indicate that the four powders present the same structure of hydroxyapatite. Furthermore the four powders obtained were used for the retention of lead. The results obtained indicated that all powders present high adsorption capacity for lead, but from environmental and economic views, the hydroxyapatite synthesized from eggshell no calcined (HA2) is most advantageous. The influence of different sorption parameters, such as: initial metal concentration, equilibration time, solution pH and sorbent dosage was studied and discussed.

  2. Diffraction. Powder, amorphous, liquid

    International Nuclear Information System (INIS)

    Sosnowska, I.M.

    1999-01-01

    Neutron powder diffraction is a unique tool to observe all possible diffraction effects appearing in crystal. High-resolution neutron diffractometers have to be used in this study. Analysis of the magnetic structure of polycrystalline materials requires the use of high-resolution neutron diffraction in the range of large interplanar distances. As distinguished from the double axis diffractometers (DAS), which show high resolution only at small interplanar distances, TOF (time-of-flight) diffractometry offers the best resolution at large interplanar distances. (K.A.)

  3. LARC powder prepreg system

    Science.gov (United States)

    Baucom, Robert M.; Marchello, Joseph M.

    1990-01-01

    Thermoplastic prepregs of LARC-TPI have been produced in a fluidized bed unit on spread continuous fiber tows. The powders are melted on the fibers by radiant heating to adhere the polymer to the fiber. This process produces tow prepreg uniformly without imposing severe stress on the fibers or requiring long high temperature residence times for the polymer. Unit design theory and operating correlations have been developed to provide the basis for scale up to commercial operation. Special features of the operation are the pneumatic tow spreader, fluidized bed and resin feed systems.

  4. Y2O3-MgO Nano-Composite Synthesized by Plasma Spraying and Thermal Decomposition of Solution Precursors

    Science.gov (United States)

    Muoto, Chigozie Kenechukwu

    This research aims to identify the key feedstock characteristics and processing conditions to produce Y2O3-MgO composite coatings with high density and hardness using solution precursor plasma spray (SPPS) and suspension plasma spray (SPS) processes, and also, to explore the phenomena involved in the production of homogenized nano-composite powders of this material system by thermal decomposition of solution precursor mixtures. The material system would find potential application in the fabrication of components for optical applications such as transparent windows. It was shown that a lack of major endothermic events during precursor decomposition and the resultant formation of highly dense particles upon pyrolysis are critical precursor characteristics for the deposition of dense and hard Y2O3-MgO coatings by SPPS. Using these principles, a new Y2O3-MgO precursor solution was developed, which yielded a coating with Vickers hardness of 560 Hv. This was a considerable improvement over the hardness of the coatings obtained using conventional solution precursors, which was as low as 110 Hv. In the thermal decomposition synthesis process, binary solution precursor mixtures of: yttrium nitrate (Y[n]) or yttrium acetate (Y[a]), with magnesium nitrate (Mg[n]) or magnesium acetate (Mg[a]) were used in order to study the effects of precursor chemistry on the structural characteristics of the resultant Y2O3-MgO powders. The phase domains were coarse and distributed rather inhomogeneously in the materials obtained from the Y[n]Mg[n] and Y[a]Mg[a] mixtures; finer and more homogeneously-distributed phase domains were obtained for ceramics produced from the Y[a]Mg[n] and Y[n]Mg[a] mixtures. It was established that these phenomena were related to the thermal characteristics for the decomposition of the precursors and their effect on phase separation during oxide crystallization. Addition of ammonium acetate to the Y[n[Mg[n] mixture changed the endothermic process to exothermic

  5. Integration of micro milling highspeed spindle on a microEDM-milling machine set-up

    DEFF Research Database (Denmark)

    De Grave, Arnaud; Hansen, Hans Nørgaard; Andolfatto, Loic

    2009-01-01

    In order to cope with repositioning errors and to combine the fast removal rate of micro milling with the precision and small feature size achievable with micro EDM milling, a hybrid micro-milling and micro-EDM milling centre was built and tested. The aim was to build an affordable set-up, easy...... by micro milling. Examples of test parts are shown and used as an experimental validation....

  6. High yttria ferritic ODS steels through powder forging

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, Deepak [Department of Metallurgical and Materials Engineering, I.I.T-Roorkee, Uttarakhand 247667 (India); Prakash, Ujjwal, E-mail: ujwalfmt@iitr.ac.in [Department of Metallurgical and Materials Engineering, I.I.T-Roorkee, Uttarakhand 247667 (India); Dabhade, Vikram V. [Department of Metallurgical and Materials Engineering, I.I.T-Roorkee, Uttarakhand 247667 (India); Laha, K.; Sakthivel, T. [Mechanical Metallurgy Group, IGCAR, Kalpakkam, Tamilnadu 603102 (India)

    2017-05-15

    Oxide dispersion strengthened (ODS) steels are being developed for future nuclear reactors. ODS Fe-18%Cr-2%W-0.2%Ti steels with 0, 0.35, 0.5, 1 and 1.5% Y{sub 2}O{sub 3} (all compositions in weight%) dispersion were fabricated by mechanical alloying of elemental powders. The powders were placed in a mild steel can and forged in a stream of hydrogen gas at 1473 K. The steels were forged again to final density. The strength of ODS steel increased with yttria content. Though this was accompanied by a decrease in tensile elongation, all the steels showed significant ductility. The ductility in high yttria alloys may be attributed to improved inter-particle bonding between milled powders due to reduction of surface oxides by hydrogen. This may permit development of ODS steels with yttria contents higher than the conventional limit of 0.5%. It is suggested that powder forging is a promising route to fabricate ODS steels with high yttria contents and improved ductility. - Highlights: •ODS steels with yttria contents beyond the conventional limit of 0.5 wt% were fabricated by powder forging in a hydrogen atmosphere. •All the alloys exhibited significant ductility. •This may be attributed to improved inter-particle bonding due to reduction of surface oxides by hydrogen. •Strength in excess of 300 MPa was obtained at 973 K for 0.5%, 1% and 1.5% yttria ODS alloys. •Powder forging is a promising route to fabricate ODS steels and permits development of compositions with up to 1.5% yttria.

  7. Preparation of TiO2 Nanocrystallite Powders Coated with 9 mol% ZnO for Cosmetic Applications in Sunscreens

    Directory of Open Access Journals (Sweden)

    Moo-Chin Wang

    2012-02-01

    Full Text Available The preparation of TiO2 nanocrystallite powders coated with and without 9 mol% ZnO has been studied for cosmetic applications in sunscreens by a co-precipitation process using TiCl4 and Zn(NO32·6H2O as starting materials. XRD results show that the phases of anatase TiO2 and rutile TiO2 coexist for precursor powders without added ZnO (T-0Z and calcined at 523 to 973 K for 2 h. When the T-0Z precursor powders are calcined at 1273 K for 2 h, only the rutile TiO2 appears. In addition, when the TiO2 precursor powders contain 9 mol% ZnO (T-9Z are calcined at 873 to 973 K for 2 h, the crystallized samples are composed of the major phase of rutile TiO2 and the minor phases of anatase TiO2 and Zn2Ti3O8. The analyses of UV/VIS/NIR spectra reveal that the absorption of the T-9Z precursor powders after being calcined has a red-shift effect in the UV range with increasing calcination temperature. Therefore, the TiO2 nanocrystallite powders coated with 9 mol% ZnO can be used as the attenuate agent in the UV-A region for cosmetic applications in sunscreens.

  8. Infiltration Behavior Of Mechanical Alloyed 75 wt% Cu-25 wt% WC Powders Into Porous WC Compacts

    Directory of Open Access Journals (Sweden)

    Şelte A.

    2015-06-01

    Full Text Available In this work infiltration behavior of mechanical alloyed 75 wt% Cu – 25 wt% WC powders into porous WC compacts were studied. Owing to their ductile nature, initial Cu powders were directly added to mechanical alloying batch. On the other hand initial WC powders were high energy milled prior to mechanical alloying. Contact infiltration method was selected for densification and compacts prepared from processed powders were infiltrated into porous WC bodies. After infiltration, samples were characterized via X-Ray diffraction studies and microstructural evaluation of the samples was carried out via scanning electron microscopy observations. Based on the lack of solubility between WC and Cu it was possible to keep fine WC particles in Cu melt since solution reprecipitation controlled densification is hindered. Also microstructural characterizations via scanning electron microscopy confirmed that the transport of fine WC fraction from infiltrant to porous WC skeleton can be carried out via Cu melt flow during infiltration.

  9. Performance Characteristics of Waste Glass Powder Substituting Portland Cement in Mortar Mixtures

    Science.gov (United States)

    Kara, P.; Csetényi, L. J.; Borosnyói, A.

    2016-04-01

    In the present work, soda-lime glass cullet (flint, amber, green) and special glass cullet (soda-alkaline earth-silicate glass coming from low pressure mercury-discharge lamp cullet and incandescent light bulb borosilicate glass waste cullet) were ground into fine powders in a laboratory planetary ball mill for 30 minutes. CEM I 42.5N Portland cement was applied in mortar mixtures, substituted with waste glass powder at levels of 20% and 30%. Characterisation and testing of waste glass powders included fineness by laser diffraction particle size analysis, specific surface area by nitrogen adsorption technique, particle density by pycnometry and chemical analysis by X-ray fluorescence spectrophotometry. Compressive strength, early age shrinkage cracking and drying shrinkage tests, heat of hydration of mortars, temperature of hydration, X-ray diffraction analysis and volume stability tests were performed to observe the influence of waste glass powder substitution for Portland cement on physical and engineering properties of mortar mixtures.

  10. Low temperature fabrication of magnesium phosphate cement scaffolds by 3D powder printing.

    Science.gov (United States)

    Klammert, Uwe; Vorndran, Elke; Reuther, Tobias; Müller, Frank A; Zorn, Katharina; Gbureck, Uwe

    2010-11-01

    Synthetic bone replacement materials are of great interest because they offer certain advantages compared with organic bone grafts. Biodegradability and preoperative manufacturing of patient specific implants are further desirable features in various clinical situations. Both can be realised by 3D powder printing. In this study, we introduce powder-printed magnesium ammonium phosphate (struvite) structures, accompanied by a neutral setting reaction by printing farringtonite (Mg(3)(PO(4))(2)) powder with ammonium phosphate solution as binder. Suitable powders were obtained after sintering at 1100°C for 5 h following 20-40 min dry grinding in a ball mill. Depending on the post-treatment of the samples, compressive strengths were found to be in the range 2-7 MPa. Cytocompatibility was demonstrated in vitro using the human osteoblastic cell line MG63.

  11. The use of metal alkoxides in the preparation of ceramic powders

    International Nuclear Information System (INIS)

    Chetcuti, A.M.; Woolfrey, J.L.

    1982-01-01

    The production of fine, chemically homogeneous and highly reactive powder is particularly desirable where the synthesis and fabrication of multicomponent ceramic systems, such as SYNROC, are concerned. To produce good sinterable material, a preparation technique that allows intimate mixing of all reacting species is desirable. Traditional routes for preparing fine powders have involved ball-milling metal oxides and spray-drying or flash-drying the resulting oxide slurries. The hydrolysis of metal alkoxides has been investigated as a technique to produce fine powders. The preparation of SYNROC B powder from alkoxides involves hydrolysing a mixture of titanium and zirconium alkoxides. The precipitated product is then blended with Al 3 + , Ba 2 + and Ca 2 + nitrate solution

  12. Analysis of the cold compaction behaviour of TiH2-316L nanocomposite powder blend using compaction models

    CSIR Research Space (South Africa)

    Machio, Christopher N

    2015-07-01

    Full Text Available The paper captures the effect of structure and the applicability of compaction models using the cold compaction of a TiH2-SS316L composite powder prepared by high energy mechanical milling. The composite blend was cold pressed uniaxially...

  13. Effect of process control agent (PCA) on the characteristics of mechanically alloyed Ti-Mg powders [Journal article

    CSIR Research Space (South Africa)

    Machio, Christopher N

    2011-03-01

    Full Text Available This paper reports the results of a study to determine the effect of process control agent (PCA) on the characteristics of Ti-Mg powders during milling. It has been shown that a 2% increase in PCA content leads to up to a 40% increase in yield...

  14. Coercivities of hot-deformed magnets processed from amorphous and nanocrystalline precursors

    International Nuclear Information System (INIS)

    Tang, Xin; Sepehri-Amin, H.; Ohkubo, T.; Hioki, K.; Hattori, A.; Hono, K.

    2017-01-01

    Hot-deformed magnets have been processed from amorphous and nanocrystalline precursors and their hard magnetic properties and microstructures have been investigated in order to explore the optimum process route. The hot-deformed magnets processed from an amorphous precursor exhibited the coercivity of 1.40 T that is higher than that processed from nanocrystalline powder, ∼1.28 T. The average grain size was larger in the magnets processed from amorphous precursor. Detailed microstructure analyses by aberration corrected scanning transmission electron microscopy revealed that the Nd + Pr concentrations in the intergranular phases were higher in the hot-deformed magnet processed from the amorphous precursor, which is considered to lead to the enhanced coercivity due to a stronger pinning force against magnetic domain wall motion.

  15. Control of core structure in MgB{sub 2} wire through tailoring boron powder

    Energy Technology Data Exchange (ETDEWEB)

    Maeda, Minoru, E-mail: maeda.minoru70@nihon-u.ac.jp [Department of Physics, College of Science and Technology, Nihon University, 1-8-14 Kanda-Surugadai, Chiyoda-ku, Tokyo 101-8308 (Japan); Uchiyama, Daisuke [Department of Physics, College of Science and Technology, Nihon University, 1-8-14 Kanda-Surugadai, Chiyoda-ku, Tokyo 101-8308 (Japan); Hossain, Md Shahriar Al; Ma, Zongqing [Institute for Superconducting and Electronic Materials, University of Wollongong, North Wollongong, New South Wales 2500 (Australia); Shahabuddin, Mohammed [Department of Physics and Astronomy, College of Science, King Saud University, P.O. Box 2455, Riyadh 11451 (Saudi Arabia); Kim, Jung Ho, E-mail: jhk@uow.edu.au [Institute for Superconducting and Electronic Materials, University of Wollongong, North Wollongong, New South Wales 2500 (Australia)

    2015-07-05

    Highlights: • The typical void structure in the wire is obtained by using large-sized B powder. • In contrast, void alignment can be achieved by using fine B powder. • The sintering at lower temperatures improves the critical current density in fields. - Abstract: A common fabrication process for MgB{sub 2} wire, namely, the in situ powder-in-tube process, forms numerous voids within the wire core, and void formation cannot be completely avoided. The orientation is, however, known to be aligned more or less along the current-flow direction when ductile coarse magnesium powder is used as a precursor, and further tailoring approaches could open up the way to improving the transport critical current density. Herein, we have used boron powders with different particle sizes, in combination with the coarse magnesium powder, and evaluated their size effects on the phase composition, microstructure, and transport properties. A mixture of the coarse magnesium powder with large-sized boron powder in the wire core, after cold working and sintering, forms a granular morphology. In contrast, an aligned core appears during the reduction process for wire which is prepared by using fine boron powder. The sintering process, especially at a low temperature, where magnesium evaporation hardly occurs, yields an aligned structure, mainly consisting of MgB{sub 2} phase, along the wire direction. These findings demonstrate that the initial size of the starting materials is critical for the tailored structure.

  16. Solution precursor plasma deposition of nanostructured ZnO coatings

    International Nuclear Information System (INIS)

    Tummala, Raghavender; Guduru, Ramesh K.; Mohanty, Pravansu S.

    2011-01-01

    Highlights: → The solution precursor route employed is an inexpensive process with capability to produce large scale coatings at fast rates on mass scale production. → It is highly capable of developing tailorable nanostructures. → This technique can be employed to spray the coatings on any kind of substrates including polymers. → The ZnO coatings developed via solution precursor plasma spray process have good electrical conductivity and reflectivity properties in spite of possessing large amount of particulate boundaries, porosity and nanostructured grains. -- Abstract: Zinc oxide (ZnO) is a wide band gap semiconducting material that has various applications including optical, electronic, biomedical and corrosion protection. It is usually synthesized via processing routes, such as vapor deposition techniques, sol-gel, spray pyrolysis and thermal spray of pre-synthesized ZnO powders. Cheaper and faster synthesis techniques are of technological importance due to increased demand in alternative energy applications. Here, we report synthesis of nanostructured ZnO coatings directly from a solution precursor in a single step using plasma spray technique. Nanostructured ZnO coatings were deposited from the solution precursor prepared using zinc acetate and water/isopropanol. An axial liquid atomizer was employed in a DC plasma spray torch to create fine droplets of precursor for faster thermal treatment in the plasma plume to form ZnO. Microstructures of coatings revealed ultrafine particulate agglomerates. X-ray diffraction confirmed polycrystalline nature and hexagonal Wurtzite crystal structure of the coatings. Transmission electron microscopy studies showed fine grains in the range of 10-40 nm. Observed optical transmittance (∼65-80%) and reflectivity (∼65-70%) in the visible spectrum, and electrical resistivity (48.5-50.1 mΩ cm) of ZnO coatings are attributed to ultrafine particulate morphology of the coatings.

  17. Solution precursor plasma deposition of nanostructured ZnO coatings

    Energy Technology Data Exchange (ETDEWEB)

    Tummala, Raghavender [Department of Mechanical Engineering, University of Michigan - Dearborn, MI 48128 (United States); Guduru, Ramesh K., E-mail: rkguduru@umich.edu [Department of Mechanical Engineering, University of Michigan - Dearborn, MI 48128 (United States); Mohanty, Pravansu S. [Department of Mechanical Engineering, University of Michigan - Dearborn, MI 48128 (United States)

    2011-08-15

    Highlights: {yields} The solution precursor route employed is an inexpensive process with capability to produce large scale coatings at fast rates on mass scale production. {yields} It is highly capable of developing tailorable nanostructures. {yields} This technique can be employed to spray the coatings on any kind of substrates including polymers. {yields} The ZnO coatings developed via solution precursor plasma spray process have good electrical conductivity and reflectivity properties in spite of possessing large amount of particulate boundaries, porosity and nanostructured grains. -- Abstract: Zinc oxide (ZnO) is a wide band gap semiconducting material that has various applications including optical, electronic, biomedical and corrosion protection. It is usually synthesized via processing routes, such as vapor deposition techniques, sol-gel, spray pyrolysis and thermal spray of pre-synthesized ZnO powders. Cheaper and faster synthesis techniques are of technological importance due to increased demand in alternative energy applications. Here, we report synthesis of nanostructured ZnO coatings directly from a solution precursor in a single step using plasma spray technique. Nanostructured ZnO coatings were deposited from the solution precursor prepared using zinc acetate and water/isopropanol. An axial liquid atomizer was employed in a DC plasma spray torch to create fine droplets of precursor for faster thermal treatment in the plasma plume to form ZnO. Microstructures of coatings revealed ultrafine particulate agglomerates. X-ray diffraction confirmed polycrystalline nature and hexagonal Wurtzite crystal structure of the coatings. Transmission electron microscopy studies showed fine grains in the range of 10-40 nm. Observed optical transmittance ({approx}65-80%) and reflectivity ({approx}65-70%) in the visible spectrum, and electrical resistivity (48.5-50.1 m{Omega} cm) of ZnO coatings are attributed to ultrafine particulate morphology of the coatings.

  18. Yang-Mills gravity in biconformal space

    International Nuclear Information System (INIS)

    Anderson, Lara B; Wheeler, James T

    2007-01-01

    We write a gravity theory with Yang-Mills-type action using the biconformal gauging of the conformal group. We show that the resulting biconformal Yang-Mills gravity theories describe 4-dim, scale-invariant general relativity in the case of slowly changing fields. In addition, we systematically extend arbitrary 4-dim Yang-Mills theories to biconformal space, providing a new arena for studying flat-space Yang-Mills theories. By applying the biconformal extension to a 4-dim pure Yang-Mills theory with conformal symmetry, we establish a 1-1, onto mapping between a set of gravitational gauge theories and 4-dim, flat-space gauge theories

  19. Luminescence properties of YAG:Nd nano-sized ceramic powders ...

    Indian Academy of Sciences (India)

    Abstract. Nano-sized ceramic powders with weaker aggregation of Nd3+-doped yttrium aluminum garnet. (YAG:Nd3+) were synthesized via co-microemulsion and microwave heating. This method provides a limited small space in a micelle for the formation of nano-sized precursors. It also requires a very short heating time, ...

  20. High-efficient production of boron nitride nanosheets via an optimized ball milling process for lubrication in oil.

    Science.gov (United States)

    Deepika; Li, Lu Hua; Glushenkov, Alexey M; Hait, Samik K; Hodgson, Peter; Chen, Ying

    2014-12-03

    Although tailored wet ball milling can be an efficient method to produce a large quantity of two-dimensional nanomaterials, such as boron nitride (BN) nanosheets, milling parameters including milling speed, ball-to-powder ratio, milling ball size and milling agent, are important for optimization of exfoliation efficiency and production yield. In this report, we systematically investigate the effects of different milling parameters on the production of BN nanosheets with benzyl benzoate being used as the milling agent. It is found that small balls of 0.1-0.2 mm in diameter are much more effective in exfoliating BN particles to BN nanosheets. Under the optimum condition, the production yield can be as high as 13.8% and the BN nanosheets are 0.5-1.5 μm in diameter and a few nanometers thick and of relative high crystallinity and chemical purity. The lubrication properties of the BN nanosheets in base oil have also been studied. The tribological tests show that the BN nanosheets can greatly reduce the friction coefficient and wear scar diameter of the base oil.